  1. Study on the influences of reduction temperature on nickel-yttria-stabilized zirconia solid oxide fuel cell anode using nickel oxide-film electrode

    Science.gov (United States)

    Jiao, Zhenjun; Ueno, Ai; Suzuki, Yuji; Shikazono, Naoki

    2016-10-01

    In this study, the reduction processes of nickel oxide at different temperatures were investigated using nickel-film anode to study the influences of reduction temperature on the initial performances and stability of nickel-yttria-stabilized zirconia anode. Compared to conventional nickel-yttria-stabilized zirconia composite cermet anode, nickel-film anode has the advantage of direct observation at nickel-yttria-stabilized zirconia interface. The microstructural changes were characterized by scanning electron microscopy. The reduction process of nickel oxide is considered to be determined by the competition between the mechanisms of volume reduction in nickel oxide-nickel reaction and nickel sintering. Electrochemical impedance spectroscopy was applied to analyze the time variation of the nickel-film anode electrochemical characteristics. The anode performances and microstructural changes before and after 100 hours discharging and open circuit operations were analyzed. The degradation of nickel-film anode is considered to be determined by the co-effect between the nickel sintering and the change of nickel-yttria-stabilized zirconia interface bonding condition.

  2. Preparation and characterization of epitaxially grown unsupported yttria-stabilized zirconia (YSZ) thin films

    Energy Technology Data Exchange (ETDEWEB)

    Götsch, Thomas; Mayr, Lukas [Institute of Physical Chemistry, Universität Innsbruck, A-6020 Innsbruck (Austria); Stöger-Pollach, Michael [University Service Center for Transmission Electron Microscopy (USTEM), Vienna University of Technology, A-1040 Vienna (Austria); Klötzer, Bernhard [Institute of Physical Chemistry, Universität Innsbruck, A-6020 Innsbruck (Austria); Penner, Simon, E-mail: simon.penner@uibk.ac.at [Institute of Physical Chemistry, Universität Innsbruck, A-6020 Innsbruck (Austria)

    2015-03-15

    Highlights: • Preparation of unsupported yttrium-stabilized zirconia films. • Control of ordering and epitaxy by temperature of deposition template. • Adjustment of film defectivity by deposition and post-oxidation temperature. • Reproducibility of target stoichiometry in the deposited films. • Lateral and vertical chemical homogeneity. - Abstract: Epitaxially grown, chemically homogeneous yttria-stabilized zirconia thin films (“YSZ”, 8 mol% Y{sub 2}O{sub 3}) are prepared by direct-current sputtering onto a single-crystalline NaCl(0 0 1) template at substrate temperatures ≥493 K, resulting in unsupported YSZ films after floating off NaCl in water. A combined methodological approach by dedicated (surface science) analytical characterization tools (transmission electron microscopy and diffraction, atomic force microscopy, angle-resolved X-ray photoelectron spectroscopy) reveals that the film grows mainly in a [0 0 1] zone axis and no Y-enrichment in surface or bulk regions takes place. In fact, the Y-content of the sputter target is preserved in the thin films. Analysis of the plasmon region in EEL spectra indicates a defective nature of the as-deposited films, which can be suppressed by post-deposition oxidation at 1073 K. This, however, induces considerable sintering, as deduced from surface morphology measurements by AFM. In due course, the so-prepared unsupported YSZ films might act as well-defined model systems also for technological applications.

  3. Rapid, cool sintering of wet processed yttria-stabilized zirconia ceramic electrolyte thin films

    OpenAIRE

    Park, Jun-Sik; Kim, Dug-Joong; Chung, Wan-Ho; Lim, Yonghyun; Kim, Hak-Sung; Kim, Young-Beom

    2017-01-01

    Here we report a photonic annealing process for yttria-stabilized zirconia films, which are one of the most well-known solid-state electrolytes for solid oxide fuel cells (SOFCs). Precursor films were coated using a wet-chemical method with a simple metal-organic precursor solution and directly annealed at standard pressure and temperature by two cycles of xenon flash lamp irradiation. The residual organics were almost completely decomposed in the first pre-annealing step, and the fluorite cr...

  4. The radiation response of mesoporous nanocrystalline zirconia thin films

    Energy Technology Data Exchange (ETDEWEB)

    Manzini, Ayelén M.; Alurralde, Martin A. [Comisión Nacional de Energía Atómica, Centro Atómico Constituyentes, Av. General Paz 1499, 1650 San Martin, Provincia de Buenos Aires (Argentina); Giménez, Gustavo [Instituto Nacional de Tecnología Industrial - CMNB, Av. General Paz 5445, 1650 San Martín, Provincia de Buenos Aires (Argentina); Luca, Vittorio, E-mail: vluca@cnea.gov.ar [Comisión Nacional de Energía Atómica, Centro Atómico Constituyentes, Av. General Paz 1499, 1650 San Martin, Provincia de Buenos Aires (Argentina)

    2016-12-15

    The next generation of nuclear systems will require materials capable of withstanding hostile chemical, physical and radiation environments over long time-frames. Aside from its chemical and physical stability, crystalline zirconia is one of the most radiation tolerant materials known. Here we report the first ever study of the radiation response of nanocrystalline and mesoporous zirconia and Ce{sup 3+}-stabilized nanocrystalline zirconia (Ce{sub 0.1}Zr{sub 0.9}O{sub 2}) thin films supported on silicon wafers. Zirconia films prepared using the block copolymer Brij-58 as the template had a thickness of around 60–80 nm. In the absence of a stabilizing trivalent cation they consisted of monoclinic and tetragonal zirconia nanocrystals with diameters in the range 8–10 nm. Films stabilized with Ce{sup 3+} contained only the tetragonal phase. The thin films were irradiated with iodine ions of energies of 70 MeV and 132 keV at low fluences (10{sup 13} - 10{sup 14} cm{sup −2}) corresponding to doses of 0.002 and 1.73 dpa respectively, and at 180 keV and high fluences (2 × 10{sup 16} cm{sup −2}) corresponding to 82.4 dpa. The influence of heavy ion irradiation on the nanocrystalline structure was monitored through Rietveld analysis of grazing incidence X-ray diffraction (GIXRD) patterns recorded at angles close to the critical angle to ensure minimum contribution to the diffraction pattern from the substrate. Irradiation of the mesoporous nanocrystalline zirconia thin films with 70 MeV iodine ions, for which electronic energy loss is dominant, resulted in slight changes in phase composition and virtually no change in crystallographic parameters as determined by Rietveld analysis. Iodine ion bombardment in the nuclear energy loss regime (132–180 keV) at low fluences did not provoke significant changes in phase composition or crystallographic parameters. However, at 180 keV and high fluences the monoclinic phase was totally eliminated from the GIXRD

  5. Fabrication of Yttria stabilized zirconia thin films on poroussubstrates for fuel cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Leming, Andres [Univ. of California, Berkeley, CA (United States)

    2003-06-16

    A process for the deposition of yttria stabilized zirconia (YSZ) films, on porous substrates, has been developed. These films have possible applications as electrolyte membranes in fuel cells. The films were deposited from colloidal suspensions through the vacuum infiltration technique. Films were deposited on both fully sintered and partially sintered substrates. A critical cracking thickness for the films was identified and strategies are presented to overcome this barrier. Green film density was also examined, and a method for improving green density by changing suspension pH and surfactant was developed. A dependence of film density on film thickness was observed, and materials interactions are suggested as a possible cause. Non-shorted YSZ films were obtained on co-fired substrates, and a cathode supported solid oxide fuel cell was constructed and characterized.

  6. Microstructure of thin film platinum electrodes on yttrium stabilized zirconia prepared by sputter deposition

    Energy Technology Data Exchange (ETDEWEB)

    Toghan, Arafat, E-mail: arafat.toghan@pci.uni-hannover.de [Institute of Physical Chemistry and Electrochemistry, Leibniz University of Hannover, Callinstrasse 3-3a, D-30167 Hannover (Germany); Khodari, M. [Chemistry Department, Faculty of Science, South Valley University, Qena, 83523 (Egypt); Steinbach, F.; Imbihl, R. [Institute of Physical Chemistry and Electrochemistry, Leibniz University of Hannover, Callinstrasse 3-3a, D-30167 Hannover (Germany)

    2011-09-01

    (111) oriented thin film Pt electrodes were prepared on single crystals of yttrium-stabilized zirconia (YSZ) by sputter deposition of platinum. The electrodes were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), X-ray diffraction (XRD), energy-dispersive X-ray analysis (EDX), atomic force microscopy (AFM) and by profilometry. SEM images of the as-sputtered platinum film show a compact amorphous Pt film covering uniformly the substrate. Upon annealing at 1123 K, gaps and pores at the interface develop leading to a partial dewetting of the Pt film. Increasing the annealing temperature to 1373 K transforms the polycrystalline Pt film into single crystalline grains exhibiting a (111) orientation towards the substrate.

  7. The fictional transition of the preferential orientation of yttria-stabilized zirconia thin films

    International Nuclear Information System (INIS)

    Lamas, J.S.; Leroy, W.P.; Depla, D.

    2012-01-01

    The fundamental study of the microstructural and textural evolution of yttria-stabilized zirconia (YSZ) thin films is of great importance given that the crystallographic properties are intimately related to their extrinsic or functional properties. In order to study these properties, YSZ thin films were obtained using dual magnetron sputtering. The results of a polar plot graph, based on X-ray diffraction (XRD) data, seem to indicate a transition from [200] out-of-plane preferential orientation to [111], indicating a dependence on composition and yttrium target–substrate (Y T–S) distance at low pressure. However, no transition is identified at high pressure, showing only [111] out-of-plane orientation, independent of composition and Y T–S distance. Scanning electron microscopy (SEM) indicates a tilt in the columnar structure of the film but no other microstructural change is in evidence, possibly related to the growth transition from [200] to [111]. Pole figures were used to clarify the texture transition in the YSZ thin films. These results indicate that there is indeed no transition in the preferential orientation of the films from [200] to [111] but a tilt of the [200] orientation towards the zirconium source. Detailed study using pole figures and SEM, clearly indicated that no growth zone transition was present and the effect is caused by geometrical configuration, contradicting expectations from standard θ/2θ XRD measurements. - Highlights: ► Study of the preferential orientation of Yttria-stabilized zirconia thin films ► Comparison of the preferential orientation at two different chamber pressures ► Correlation with the energy per adparticle and the extended structure zone model ► Use of pole figures analyses to clarify the change in the preferential orientation

  8. The fictional transition of the preferential orientation of yttria-stabilized zirconia thin films

    Energy Technology Data Exchange (ETDEWEB)

    Lamas, J.S., E-mail: Jerika.Lamas@UGent.be; Leroy, W.P.; Depla, D.

    2012-12-15

    The fundamental study of the microstructural and textural evolution of yttria-stabilized zirconia (YSZ) thin films is of great importance given that the crystallographic properties are intimately related to their extrinsic or functional properties. In order to study these properties, YSZ thin films were obtained using dual magnetron sputtering. The results of a polar plot graph, based on X-ray diffraction (XRD) data, seem to indicate a transition from [200] out-of-plane preferential orientation to [111], indicating a dependence on composition and yttrium target-substrate (Y T-S) distance at low pressure. However, no transition is identified at high pressure, showing only [111] out-of-plane orientation, independent of composition and Y T-S distance. Scanning electron microscopy (SEM) indicates a tilt in the columnar structure of the film but no other microstructural change is in evidence, possibly related to the growth transition from [200] to [111]. Pole figures were used to clarify the texture transition in the YSZ thin films. These results indicate that there is indeed no transition in the preferential orientation of the films from [200] to [111] but a tilt of the [200] orientation towards the zirconium source. Detailed study using pole figures and SEM, clearly indicated that no growth zone transition was present and the effect is caused by geometrical configuration, contradicting expectations from standard {theta}/2{theta} XRD measurements. - Highlights: Black-Right-Pointing-Pointer Study of the preferential orientation of Yttria-stabilized zirconia thin films Black-Right-Pointing-Pointer Comparison of the preferential orientation at two different chamber pressures Black-Right-Pointing-Pointer Correlation with the energy per adparticle and the extended structure zone model Black-Right-Pointing-Pointer Use of pole figures analyses to clarify the change in the preferential orientation.

  9. Characterization of cubic yttria-stabilized zirconia obtained by spray pyrolysis

    International Nuclear Information System (INIS)

    Halmenschlager, Cibele M.; Nunes, Marilia; Vieira, Ramaugusto; Bergmann, Carlos Perez; Falcade, Tiago; Malfatti, Celia de Fraga

    2009-01-01

    Yttria-stabilized-zirconia (YSZ) has been the object of many studies as a SOFC electrolyte. The aim of this work is to produce, by spray pyrolysis process, thin and dense films of YSZ. A disk of steel 316L, previously heated, was used as substrate. The film was obtained with zirconium acetylacetonate (Zr(C 6 H 7 O 2 ) 4 ) and yttrium chloride (YCl 3.6 H 2 O), dissolved in a mixture of ethanol + butyl carbitol with volume ratio (1:1). ZrO 2 amorphous films were deposited in the substrate heated at many temperatures. After thermal treatment at 700 deg C the films were changed into cubic yttria-stabilized-zirconia structure. The thin films obtained were characterized by thermal analysis, scanning electron microscopy, transmission electron microscopy, X-ray diffraction and micro-Raman spectroscopy. (author)

  10. Room temperature growth of biaxially aligned yttria-stabilized zirconia films on glass substrates by pulsed-laser deposition

    CERN Document Server

    Li Peng; Mazumder, J

    2003-01-01

    Room temperature deposition of biaxially textured yttria-stabilized zirconia (YSZ) films on amorphous glass substrates was successfully achieved by conventional pulsed-laser deposition. The influence of the surrounding gases, their pressure and the deposition time on the structure of the films was studied. A columnar growth process was revealed based on the experimental results. The grown biaxial texture appears as a kind of substrate independence, which makes it possible to fabricate in-plane aligned YSZ films on various substrates.

  11. Synthesis, microstructural, optical and mechanical properties of yttria stabilized zirconia thin films

    International Nuclear Information System (INIS)

    Amézaga-Madrid, P.; Hurtado-Macías, A.; Antúnez-Flores, W.; Estrada-Ortiz, F.; Pizá-Ruiz, P.; Miki-Yoshida, M.

    2012-01-01

    Highlights: ► Thin films of YSZ obtained by AACVD have high quality. ► They are uniform, very transparent, and have high hardness. ► Optical characterization were performed in detail, optical constants and band gap energy were determined as a function of dopant content. - Abstract: Thin films of yttria-stabilized zirconia (YSZ) exhibit exceptional properties, such as high thermal, chemical and mechanical stability. Here, we report the synthesis of YSZ thin films by aerosol assisted chemical vapour deposition onto borosilicate glass and fused silica substrates. Optimum deposition temperature was 673 ± 5 K. In addition, different Y content was tried to analyse its influence in the microstructure and properties of the films. The films were uniform, transparent and non-light scattering. Surface morphology and cross sectional microstructure were studied by field emission scanning electron microscopy. The microstructure of the films was characterized by grazing incidence X-ray diffraction. Crystallite size and lattice parameter were obtained. Optical properties were analysed from reflectance and transmittance spectra; from these measurements, optical constants and band gap were obtained. Quantum confinement effect, due to the small grain size of the films, was evident in the high band gap energy obtained. Nanoindentation tests were realized at room temperature employing the continuous stiffness measurement method, to determine the hardness and elastic modulus as a function of Y content.

  12. Obtention of zirconia films stabilized with Yttria via pyrolysis spray: study of the solvent influence; Obtencao de filmes de zirconia estabilizada com itria via spray pirolise: estudo da influencia do solvente

    Energy Technology Data Exchange (ETDEWEB)

    Halmenschlager, Cibele Melo; Vieira, Ramaugusto da Porciuncula; Takimi, Antonio Shigueaki; Bergmann, Carlos Perez; Silva, Aline Lima da; Malfatti, Celia de Fraga [Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS (Brazil). Programa de Pos-Graduacao em Engenharia de Minas, Metalurgica e de Materiais (PPGEM). Lab. de Materiais Ceramicos (LACER)]. E-mail: cibelemh@yahoo.com.br

    2008-07-01

    Yttria-stabilized-zirconia (YSZ) has been object of many studies, due to its great chemical stability and excellent ionic conduction in high temperature. This material has been studies with an intention of to be used with electrolyte of oxide solid fuel cells, which work in high temperature. The aim of the present work was to evaluate the influence of the solvent on the elaboration of crystalline films of YSZ via spray pyrolysis. The film was prepared by spray pyrolysis with zirconium acetylacetonate (Zr(C{sub 6}H{sub 7}O{sub 2}){sub 4}) and yttrium chloride (YCl{sub 3}.6H{sub 2}O), dissolved in different solvents: ethanol (C{sub 2}H{sub 6}O), ethanol (C{sub 2}H{sub 6}O) + propyleneglycol (C{sub 3}H{sub 8}O{sub 2}) with volume ratio (1:1) and ethanol (C{sub 2}H{sub 6}O) + diethylene glycol butyl ether (C{sub 8}H{sub 18}O{sub 3}) with volume ratio of 1:1. A disk of steel 316L was used as substrate. The amorphous film was deposited in the substrate heated at 280 deg C {+-} 50 deg C. After deposition from thermal treatment at 700 deg C the amorphous film was changed into Yttria-stabilized-zirconia film. The thermal behavior of the films has been studied by both (DTA/TGA) thermogravimetric and mass spectroscopy analyses. The morphology and crystalline phase of the films was investigated by scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. The YSZ film obtained after heat treatment was dense and crystalline, however, the analyses indicate a significant influence of the solvent and of the substrate temperature during the deposition process on the film morphology.(author)

  13. Microstructure and phase composition of sputter-deposited zirconia-yttria films

    International Nuclear Information System (INIS)

    Knoll, R.W.; Bradley, E.R.

    1983-11-01

    Thin ZrO 2 -Y 2 O 3 coatings ranging in composition from 3 to 15 mole % Y 2 O 3 were produced by rf sputter deposition. This composition range spanned the region on the equilibrium ZrO 2 -Y 2 O 3 phase diagram corresponding to partially stabilized zirconia (a mixture of tetragonal ZrO 2 and cubic solid solution). Microstructural characteristics and crystalline phase composition of as-deposited and heat treated films (1100 0 C and 1500 0 C) were determined by transmission electron microscopy (TEM) and by x-ray diffraction (XRD). Effects of substrate bias (0 approx. 250 volts), which induced ion bombardment of the film during growth, were also studied. The as-deposited ZrO 2 -Y 2 O 3 films were single phase over the composition range studied, and XRD data indicated considerable local atomic disorder in the lattice. Films produced at low bias contained intergranular voids, pronounced columnar growth, and porosity between columns. At high bias, the microstructure was denser, and films contained high compressive stress. After heat treatment, all deposits remained single phase, therefore a microstructure and precipitate distribution characteristic of toughened, partially stabilized zirconia appear to be difficult to achieve in vapor deposited zirconia coatings

  14. Preparation and antibacterial properties of hybrid-zirconia films with silver nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Azocar, Ignacio, E-mail: manuel.azocar@usach.cl [Departamento de Quimica de los Materiales, Facultad de Quimica y Biologia, Universidad de Santiago de Chile, USACH, Avenida Bernardo O' Higgins 3363, Casilla 40, Correo 33, Santiago (Chile); Vargas, Esteban [Facultad de Ingenieria, Departamento de Metalurgia, Universidad de Santiago de Chile, USACH (Chile); Duran, Nicole [Departamento de Quimica de los Materiales, Facultad de Quimica y Biologia, Universidad de Santiago de Chile, USACH, Avenida Bernardo O' Higgins 3363, Casilla 40, Correo 33, Santiago (Chile); Arrieta, Abel [Departamento de Biologia, Facultad de Quimica y Biologia, Universidad de Santiago de Chile, USACH (Chile); Gonzalez, Evelyn [Departamento de Quimica de los Materiales, Facultad de Quimica y Biologia, Universidad de Santiago de Chile, USACH, Avenida Bernardo O' Higgins 3363, Casilla 40, Correo 33, Santiago (Chile); Facultad de Ingenieria, Departamento de Metalurgia, Universidad de Santiago de Chile, USACH (Chile); Departamento de Biologia, Facultad de Quimica y Biologia, Universidad de Santiago de Chile, USACH (Chile); Departamento de Quimica Farmacologica y Toxicologica, Facultad de Ciencias Quimicas, Universidad de Chile, Sergio Livingstone Polhammer 1007, Santiago (Chile); and others

    2012-11-15

    The antimicrobial effect of incorporating silver nanoparticles (AgNps) into zirconia matrix-polyether glycol was studied. AgNps of 4-6 nm in size were synthesized using the inverse micelles method, and different doses of metallic nanoparticles were incorporated into zirconia-polyether glycol mixtures during the ageing procedure. Atomic force microscopy (AFM) of the modified hybrid film showed a homogenous distribution of 20-80 nm diameter AgNps, indicating agglomeration of these structures during film modification; such agglomerations were greater when increasing the dosage of the colloidal system. The AgNps-hybrid films showed higher antimicrobial activity against Gram-positive bacteria than for Gram-negative bacteria. Hybrid films prepared with dioctyl sodium sulfosuccinate (AOT) stabilized AgNps presented enhanced antibacterial activity compared to that obtained through the addition of a high AgNO{sub 3} concentration (0.3 wt%). -- Graphical abstract: Atomic Force Micrographs, top and cross section view, showing silver nanoparticles embedded in a zirconia-polyether glycol hybrid film. Highlights: Black-Right-Pointing-Pointer Antibacterial activity of films (zirconia-polyether glycol) modified with silver nanoparticles. Black-Right-Pointing-Pointer Biofilm formation is prevented. Black-Right-Pointing-Pointer High sensibility against gram positive bacteria.

  15. Rapid, cool sintering of wet processed yttria-stabilized zirconia ceramic electrolyte thin films.

    Science.gov (United States)

    Park, Jun-Sik; Kim, Dug-Joong; Chung, Wan-Ho; Lim, Yonghyun; Kim, Hak-Sung; Kim, Young-Beom

    2017-09-29

    Here we report a photonic annealing process for yttria-stabilized zirconia films, which are one of the most well-known solid-state electrolytes for solid oxide fuel cells (SOFCs). Precursor films were coated using a wet-chemical method with a simple metal-organic precursor solution and directly annealed at standard pressure and temperature by two cycles of xenon flash lamp irradiation. The residual organics were almost completely decomposed in the first pre-annealing step, and the fluorite crystalline phases and good ionic conductivity were developed during the second annealing step. These films showed properties comparable to those of thermally annealed films. This process is much faster than conventional annealing processes (e.g. halogen furnaces); a few seconds compared to tens of hours, respectively. The significance of this work includes the treatment of solid-state electrolyte oxides for SOFCs and the demonstration of the feasibility of other oxide components for solid-state energy devices.

  16. Synthesis and characterization of Yttria-stabilized-zirconia by spray pyrolysis

    International Nuclear Information System (INIS)

    Melo Halmenschlager, Cibele; Vieira, Ramaugusto; Shigueaki Takimi, Antonio; Lima da Silva, Aline; De Fraga Malfatti, Celia; Perez Bergmann, Carlos

    2003-01-01

    Yttria-stabilized-zirconia (YSZ) has been object of many studies due to its great chemical stability and excellent ionic conduction in high temperature. One of the applications of YSZ films is the use as electrolyte in solid oxide fuel cells (SOFC). The great challenge of the SOFC is the development of a intermediary temperature solid oxide fuel cell (ITSOFC) to work in a temperature around 700 o C with the same efficiency of high temperature SOFC, with this aim fuel cells utilizing thin electrolyte films ha been developed. Traditional techniques of thin films deposition as Combustion Vapour Deposition (CVD) and Sputtering are very expensive, the reagents must be very pure and it is necessary to use a system of vacuum. Spray pyrolysis is a good alternative to deposit dense films with thickness between 0,1 and 10 . This technique has a lot of advantages front to classic methods of deposition because of the simplicity of the process and the equipment, low cost, and minimal waste production. In this process, when the parameters are very well controlled, it is possible to obtain oxide films with high quality. In the present work, amorphous films consisted of a layer of 8 mol% Yttria-stabilized zirconia were produced by spray pyrolysis and heat treated to obtain crystalline films. The film was prepared with zirconium acetylacetonate (Zr(C 6 H 7 O 2 ) 4 ) and yttrium chloride (YCl 3 .6H 2 O), dissolved in ethanol (C 2 H 6 O) and diethylene glycol butyl ether (C 8 H 18 O 3 ) mixed in the volume ratio of 1:1, and a disk of steel 316L was used as substrate. The amorphous film was deposited in the substrate heat until 280 o C ± 50 o C and after deposition from thermal treatment at 700 o C, the amorphous film was changed into Yttria-stabilized-zirconia crystalline film. The precursor solution was characterized for the Differential Thermal Analysis (DTA). The morphology and crystallinity of the films was investigated by scanning electron microscopy (SEM) and X-ray diffraction

  17. Normal spectral emittance of Inconel 718 aeronautical alloy coated with yttria stabilized zirconia films

    Energy Technology Data Exchange (ETDEWEB)

    Gonzalez-Fernandez, L. [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain); Industria de Turbo Propulsores, S.A., Planta de Zamudio, Edificio 300, 48170 Zamudio, Bizkaia (Spain); Campo, L. del [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain); Perez-Saez, R.B., E-mail: raul.perez@ehu.es [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain); Tello, M.J. [Departamento de Fisica de la Materia Condensada, Facultad de Ciencia y Tecnologia, Universidad del Pais Vasco, Barrio Sarriena s/n, 48940 Leioa, Bizkaia (Spain)

    2012-02-05

    Highlights: Black-Right-Pointing-Pointer Emittance of Inconel 718 coated with plasma sprayed yttria stabilized zirconia. Black-Right-Pointing-Pointer The coating is opaque for {lambda} > 9 {mu}m and semi-transparent for {lambda} < 9 {mu}m. Black-Right-Pointing-Pointer In the semi-transparent region the emittance decreases with coating thickness. Black-Right-Pointing-Pointer 300 {mu}m thick coatings are still semi-transparent. Black-Right-Pointing-Pointer In the opaque region the surface roughness determines the emittance level. - Abstract: Knowledge of the radiative behaviour of the yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) is needed to perform radiative heat transfer calculations in industrial applications. In this paper, normal spectral emittance experimental data of atmospheric plasma sprayed (PS) YSZ films layered on Inconel 718 substrates are shown. The spectral emittance was measured between 2.5 and 22 {mu}m on samples with film thicknesses ranging from 20 to 280 {mu}m. The samples were heated in a controlled environment, and the emittance was measured for several temperatures between 330 and 730 Degree-Sign C. The dependence of the spectral emittance with film thickness, surface roughness and temperature has been studied and compared with the available results for YSZ TBCs obtained by electron-beam physical vapour deposition. The PS-TBC samples show a Christiansen point at {lambda} = 12.8 {mu}m. The films are semi-transparent for {lambda} < 9 {mu}m, and opaque for {lambda} > 9 {mu}m. In the semi-transparent region, the contribution of the radiation emitted by the Inconel 718 substrate to the global emittance of the samples is analysed. In addition, the influence of the roughness in the emittance values in the opaque spectral region is discussed. Finally, the total normal emittance is obtained as a function of the TBC thickness.

  18. Densification of zirconia films by coevaporation with silica

    International Nuclear Information System (INIS)

    Feldman, A.; Farabaugh, E.N.

    1985-04-01

    Optical films of zirconia have been receiving considerable attention because of their potential use as the high-index layer in multilayer optical coatings for the ultraviolet portion of the spectrum. Several problems are associated with electron-beam deposited zirconia films, including index instability and index inhomogeneity. The index instability is caused by the adsorption and the desorption of water in the porous columnar structure of the zirconia films. Index inhomogeneity is due to the inhomogeneous structure in the films. Recent work has shown that the first several tens of nanometers of a film possess a cubic structure, whereas the outmost layers possess a monoclinic structure. One approach for producing bulk-like zirzonia films that is receiving considerable attention at present is ion-assisted electron-beam deposition. This is because the method has successfully produced zirconia films having bulk-like densities and refractive indices that show insignificant sensitivity to water adsorption. In this paper a similar effect is demonstrated when mixed zirconia:silica films are produced by coevaporation from independent electron-beam sources, and, in particular, it is shown that the admixture of a small amount of silica with the zirconia produces a film possessing a higher refractive index than a pure zirconia film

  19. Anatase thin film with diverse epitaxial relationship grown on yttrium stabilized zirconia substrate by chemical vapor deposition

    International Nuclear Information System (INIS)

    Miyagi, Takahira; Ogawa, Tomoyuki; Kamei, Masayuki; Wada, Yoshiki; Mitsuhashi, Takefumi; Yamazaki, Atsushi

    2003-01-01

    An anatase epitaxial thin film with diverse epitaxial relationship, YSZ (001) // anatase (001), YSZ (010) // anatase (110), was grown on a single crystalline yttrium stabilized zirconia (YSZ) (001) substrate by metal organic chemical vapor deposition (MOCVD). The full width at half maximum (FWHM) of the (004) reflection of this anatase epitaxial film was 0.4deg, and the photoluminescence of this anatase epitaxial film showed visible emission with broad spectral width and large Stokes shift at room temperature. These results indicate that this anatase epitaxial film possessed almost equal crystalline quality compared with that grown under identical growth conditions on single crystalline SrTiO 3 substrate. (author)

  20. Yttria and ceria doped zirconia thin films grown by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Saporiti, F.; Juarez, R. E., E-mail: cididi@fi.uba.ar [Grupo de Materiales Avanzados, Facultad de Ingenieria, Universidad de Buenos Aires (Argentina); Audebert, F. [Consejo Nacional de Investigaciones Cientificas y Tecnicas (CONICET) (Argentina); Boudard, M. [Laboratoire des Materiaux et du Genie Physique (CNRS), Grenoble (France)

    2013-11-01

    The Yttria stabilized Zirconia (YSZ) is a standard electrolyte for solid oxide fuel cells (SOFCs), which are potential candidates for next generation portable and mobile power sources. YSZ electrolyte thin films having a cubic single phase allow reducing the SOFC operating temperature without diminishing the electrochemical power density. Films of 8 mol% Yttria stabilized Zirconia (8YSZ) and films with addition of 4 weight% Ceria (8YSZ + 4CeO{sub 2}) were grown by pulsed laser deposition (PLD) technique using 8YSZ and 8YSZ + 4CeO{sub 2} targets and a Nd-YAG laser (355 nm). Films have been deposited on Soda-Calcia-Silica glass and Si(100) substrates at room temperature. The morphology and structural characteristics of the samples have been studied by means of X-ray diffraction and scanning electron microscopy. Films of a cubic-YSZ single phase with thickness in the range of 1-3 Micro-Sign m were grown on different substrates (author)

  1. Ultra-thin zirconia films on Zr-alloys

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Joong Il Jake; Mayr-Schmoelzer, Wernfried; Mittendorfer, Florian; Redinger, Josef; Diebold, Ulrike; Schmid, Michael [Institute of Applied Physics, Vienna University of Technology (Austria); Li, Hao; Rupprechter, Guenther [Institute of Materials Chemistry, Vienna University of Technology (Austria)

    2014-07-01

    Zirconia ultra-thin films have been prepared by oxidation of Pt{sub 3}Zr(0001) and showed a structure equivalent to (111) of cubic zirconia. Following previous work, we have prepared ultra-thin zirconia by oxidation of a different alloy, Pd{sub 3}Zr(0001), which resulted in a similar structure with a slightly different lattice parameter, 351.2 ±0.4 pm. Unlike the oxide on Pt{sub 3}Zr, where Zr of the oxide binds to Pt in the substrate, here the oxide binds to substrate Zr via oxygen. This causes stronger distortion of the oxide structure, i.e. a stronger buckling of Zr in the oxide. After additional oxidation of ZrO{sub 2}/Pt{sub 3}Zr, a different ultra-thin zirconia phase is observed. A preliminary structure model for this film is based on (113)-oriented cubic zirconia. 3D oxide clusters are also present after growing ultra-thin zirconia films. They occur at the step edges, and the density is higher on Pd{sub 3}Zr. These clusters also appear on terraces after additional oxidation. XPS reveals different core level shifts of the oxide films, bulk, and oxide clusters.

  2. Artificial in-plane ordering of textured YBa2Cu3O(7-x) films deposited on polycrystalline yttria-stabilized zirconia substrates

    Science.gov (United States)

    Harshavardhan, K. S.; Rajeswari, M.; Hwang, D. M.; Chen, C. Y.; Sands, T. D.; Venkatesan, T.; Tkaczyk, J. E.; Lay, K. W.; Safari, A.; Johnson, L.

    1992-12-01

    Anisotropic surface texturing of the polycrystalline yttria-stabilized zirconia substrates, prior to YBa2Cu3O(7-x) film deposition, is shown to promote in-plane (basal plane) ordering of the film growth in addition to the c-axis texturing. The Jc's of the films in the weak-link-dominated low-field regime are enhanced considerably, and this result is attributed to the reduction of weak links resulting from a reduction in the number of in-plane large-angle grain boundaries.

  3. Processing and characterization of yttrium-stabilized zirconia thin films on polyimide from aqueous polymeric precursors

    International Nuclear Information System (INIS)

    Gorman, B.P.; Anderson, H.U.

    2004-01-01

    Low-temperature deposition of dense, nanocrystalline yttrium-stabilized zirconia (YSZ) thin films on polyimide (PI) substrates is illustrated using an aqueous polymeric precursor spin-coating technique. The polymeric precursor uses low-cost materials, is water-soluble and the viscosity and cation concentrations can be easily adjusted in order to vary the film thickness from 0.02 to 0.3 μm. Due to the use of water as the solvent in the YSZ precursor and the hydrophobic nature of the PI surface, surface modification processes were utilized in order to improve the wetting characteristics. Surface modification of PI substrates using wet chemical and oxygen plasma techniques led to a decrease in the precursor contact angle, and ultimately allowed for uniform film formation on both bulk and thin film PI substrates. Scanning electron microscopy, transmission electron microscopy and UV/Vis absorption illustrate that near full-density nanocrystalline thin films of YSZ can be produced at temperatures as low as 350 deg. C. Thermogravimetric analyses illustrate that the PI substrate does not undergo any weight loss up to these temperatures

  4. Are zirconia corrosion films a form of partially stabilised zirconia (PSZ)?

    International Nuclear Information System (INIS)

    Cox, B.

    1987-03-01

    The problem of understanding the development of porosity in a zirconium oxide film still under biaxial compression is discussed. The oxide film is compared with partially stabilised zirconia (PSZ) where stress induced transformation of tetragonal zirconia has been observed to lead to microcracking of the structure. The similarities between PSZ and the thermal oxide films formed on zirconium alloys are enumerated, and an hypothesis is proposed that can both explain the penetration of pores or microcracks in oxides on Zircaloy-2 to a point very close to the oxide/metal interface, and explain the observation that such a phenomenon does not occur in oxide films on Zr-2.5%Nb. This hypothesis could be tested by laser Raman spectroscopy on oxide films during growth at elevated temperatures. 87 refs

  5. Thickness determination of large-area films of yttria-stabilized zirconia produced by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Pryds, N. [Materials Research Department, Riso National Laboratory, DK-4000 Roskilde (Denmark)]. E-mail: nini.pryds@risoe.dk; Toftmann, B. [Department of Optics and Plasma Research, Riso National Laboratory, DK-4000 Roskilde (Denmark); Bilde-Sorensen, J.B. [Materials Research Department, Riso National Laboratory, DK-4000 Roskilde (Denmark); Schou, J. [Department of Optics and Plasma Research, Riso National Laboratory, DK-4000 Roskilde (Denmark); Linderoth, S. [Materials Research Department, Riso National Laboratory, DK-4000 Roskilde (Denmark)

    2006-04-30

    Films of yttria-stabilized zirconia (YSZ) on a polished silicon substrate of diameter up to 125 mm have been produced in a large-area pulsed laser deposition (PLD) setup under typical PLD conditions. The film thickness over the full film area has been determined by energy-dispersive X-ray spectrometry in a scanning electron microscope (SEM) with use of a method similar to one described by Bishop and Poole. The attenuation of the electron-induced X-rays from the Si wafer by the film was monitored at a number of points along a diameter and the thickness was determined by Monte Carlo simulations of the attenuation for various values of film thickness with the program CASINO. These results have been compared with direct measurements in the SEM of the film thickness on a cross-section on one of the wafers. The results of these measurements demonstrate the ability of this technique to accurately determine the thickness of a large film, i.e. up to diameters of 125 mm, in a relatively short time, without destroying the substrate, without the need of a standard sample and without the need of a flat substrate. We have also demonstrated that by controlling the deposition parameters large-area YSZ films with uniform thickness can be produced.

  6. Thickness determination of large-area films of yttria-stabilized zirconia produced by pulsed laser deposition

    International Nuclear Information System (INIS)

    Pryds, N.; Toftmann, B.; Bilde-Sorensen, J.B.; Schou, J.; Linderoth, S.

    2006-01-01

    Films of yttria-stabilized zirconia (YSZ) on a polished silicon substrate of diameter up to 125 mm have been produced in a large-area pulsed laser deposition (PLD) setup under typical PLD conditions. The film thickness over the full film area has been determined by energy-dispersive X-ray spectrometry in a scanning electron microscope (SEM) with use of a method similar to one described by Bishop and Poole. The attenuation of the electron-induced X-rays from the Si wafer by the film was monitored at a number of points along a diameter and the thickness was determined by Monte Carlo simulations of the attenuation for various values of film thickness with the program CASINO. These results have been compared with direct measurements in the SEM of the film thickness on a cross-section on one of the wafers. The results of these measurements demonstrate the ability of this technique to accurately determine the thickness of a large film, i.e. up to diameters of 125 mm, in a relatively short time, without destroying the substrate, without the need of a standard sample and without the need of a flat substrate. We have also demonstrated that by controlling the deposition parameters large-area YSZ films with uniform thickness can be produced

  7. Low-Temperature Superionic Conductivity in Strained Yttria-Stabilized Zirconia

    DEFF Research Database (Denmark)

    Sillassen, Michael; Eklund, Per; Pryds, Nini

    2010-01-01

    Very high lateral ionic conductivities in epitaxial cubic yttria-stabilized zirconia (YSZ) synthesized on single-crystal SrTiO3 and MgO substrates by reactive direct current magnetron sputtering are reported. Superionic conductivities (i.e., ionic conductivities of the order 1 -1cm-1) are observed...... at 500 °C for 58-nm-thick films on MgO. The results indicate a superposition of two parallel contributions - one due to bulk conductivity and one attributable to conduction along the film-substrate interface. Interfacial effects dominate the conductivity at low temperatures (...

  8. Ionic conductivity and thermal stability of magnetron-sputtered nanocrystalline yttria-stabilized zirconia

    DEFF Research Database (Denmark)

    Sillassen, M.; Eklund, P.; Sridharan, M.

    2009-01-01

    Thermally stable, stoichiometric, cubic yttria-stabilized zirconia (YSZ) thin-film electrolytes have been synthesized by reactive pulsed dc magnetron sputtering from a Zr–Y (80/20 at. %) alloy target. Films deposited at floating potential had a texture. Single-line profile analysis of the 111 x.......5% at bias voltages of −175 and −200 V with additional incorporation of argon. The films were thermally stable; very limited grain coarsening was observed up to an annealing temperature of 800 °C. Temperature-dependent impedance spectroscopy analysis of the YSZ films with Ag electrodes showed that the in......-plane ionic conductivity was within one order of magnitude higher in films deposited with substrate bias corresponding to a decrease in grain size compared to films deposited at floating potential. This suggests that there is a significant contribution to the ionic conductivity from grain boundaries...

  9. Oblique ion texturing of yttria-stabilized zirconia: The {211} structure

    International Nuclear Information System (INIS)

    Berdahl, Paul; Reade, Ronald P.; Liu, Jinping; Russo, Richard E.; Fritzemeier, Les; Buczek, David; Schoop, Urs

    2002-01-01

    Amorphous (Zr,Y)O x films were synthesized by reactive magnetron sputtering and subsequently crystallized by oblique ion bombardment. Crystalline texture nucleated by the ion beam was replicated by solid-phase epitaxial growth throughout the formerly amorphous yttria-stabilized zirconia (YSZ) film. The resulting YSZ films have (211) orientation normal to the substrate with in-plane directions (111), parallel, and (110), transverse, to the azimuth of the ion beam. We hypothesize that the texture mechanism involves ion-induced film compression and shear. The results, taken together with prior work, show that oblique ion texturing of amorphous films is a general phenomenon that can be used to fabricate substrates with more than one type of crystallographic orientation

  10. Dominant pinning mechanisms in YBa2Cu3O7-x films on single and polycrystalline yttria stabilized zirconia substrates

    Science.gov (United States)

    Harshavardhan, K. S.; Rajeswari, M.; Hwang, D. M.; Chen, C. Y.; Sands, T.; Venkatesan, T.; Tkaczyk, J. E.; Lay, K. W.; Safari, A.

    1992-04-01

    Critical-current densities have been measured in YBa2Cu3O7-x films deposited on (100) yttria stabilized zirconia (YSZ) and polycrystalline YSZ substrates as a function of temperature (4.5-88 K), magnetic field (0-1 T) and orientation relative to the applied field. The results indicate that in films on polycrystalline substrates, surface and interface pinning play a dominant role at high temperatures. In films on (100) YSZ, pinning is mainly due to intrinsic layer pinning as well as extrinsic pinning associated with the interaction of the fluxoids with point defects and low energy planar (2D) boundaries. The differences are attributed to the intrinsic rigidity of single fluxoids which is reduced in films on polycrystalline substrates thereby weakening the intrinsic layer pinning.

  11. Characterization of single crystal uranium-oxide thin films grown via reactive-gas magnetron sputtering on yttria-stabilized zirconia and sapphire

    Energy Technology Data Exchange (ETDEWEB)

    Strehle, Melissa M.; Heuser, Brent J., E-mail: bheuser@illinois.edu; Elbakhshwan, Mohamed S.; Han Xiaochun; Gennardo, David J.; Pappas, Harrison K.; Ju, Hyunsu

    2012-06-30

    The microstructure and valence states of three single crystal thin film systems, UO{sub 2} on (11{sup Macron }02) r-plane sapphire, UO{sub 2} on (001) yttria-stabilized zirconia, and U{sub 3}O{sub 8} on (11{sup Macron }02) r-plane sapphire, grown via reactive-gas magnetron sputtering are analyzed primarily with X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and ultraviolet photoelectron spectroscopy (UPS). XRD analysis indicates the growth of single crystal domains with varying degrees of mosaicity. XPS and UPS analyses yield U-4f, U-5f, O-1s, and O-2p electron binding energies consistent with reported bulk values. A change from p-type to n-type semiconductor behavior induced by preferential sputtering of oxygen during depth profile analysis was observed with both XPS and UPS. Trivalent cation impurities (Nd and Al) in UO{sub 2} lower the Fermi level, shifting the XPS spectral weight. This observation is consistent with hole-doping of a Mott-Hubbard insulator. The uranium oxide-(11{sup Macron }02) sapphire system is unstable with respect to Al interdiffusion across the film-substrate interface at elevated temperature. - Highlights: Black-Right-Pointing-Pointer Single crystal uranium-oxides grown on sapphire and yttria-stabilized zirconia. Black-Right-Pointing-Pointer Anion and cation valence states studied by photoelectron emission spectroscopy. Black-Right-Pointing-Pointer Trivalent Nd and Al impurities lower the Fermi level. Black-Right-Pointing-Pointer Uranium-oxide films on sapphire found to be unstable with respect to Al interdiffusion.

  12. Grain size stabilization of tetragonal phase of zirconia in sputtered Zr-O cermet films

    International Nuclear Information System (INIS)

    Hadavi, M. S.; Keshmiri, H.; Kompany, A.; Zhang, Q. C.

    2005-01-01

    In this research, thin films of Zr/ZrO 2 composites were deposited by reactive magnetron sputtering technique on Si and fused Silica substrates, and their structures were investigated by x-ray diffraction method. During the deposition of the cermet layers, a Zr metallic target was sputtered in a gas mixture of Ar and O 2 . By controlling of O 2 flow rate, the different metal volume fractions in the cermet layers were achieved. The optical response of the samples was studied using spectroscopy methods. Also the effect of vacuum annealing on the structures and the optical properties were studies. x-ray diffraction results indicated that the prepared samples were amorphous and vacuum annealing induced crystallization in the cermet films. This research also show that without doping, the tetragonal phase of Zirconia can be stabilized at a temperature lower than the normal transition temperature. This is g rain size stabilization a nd relates to the small size of the crystallizes. In order to study the electron diffraction in the selected area patterns, the samples were analysed by a high-resolution transmission microscope. The selected area patterns results showed that all of the as prepared samples were amorphous showing evidence of very small Zr crystallites immersed in a dielectric medium. The Sad results are in close agreement with those obtained by x-ray diffraction analysis

  13. Phase stability in yttria-stabilized zirconia from first principles

    Energy Technology Data Exchange (ETDEWEB)

    Carbogno, Christian; Scheffler, Matthias [Materials Department, University of California, Santa Barbara, CA (United States); Fritz-Haber-Institut der Max-Planck-Gesellschaft, Berlin (Germany); Levi, Carlos G.; Van de Walle, Chris G. [Materials Department, University of California, Santa Barbara, CA (United States)

    2012-07-01

    Zirconia based ceramics are of pivotal importance for a variety of industrial technologies, e.g., for thermal barrier coatings in gas and airplane turbines. Naturally, the stability of such coatings at elevated temperatures plays a critical role in these applications. It is well known that an aliovalent doping of tetragonal ZrO{sub 2} with yttria, which induces oxygen vacancies due to charge conservation, increases its thermodynamic stability. However, the atomistic mechanisms that determine the phase stability of such yttria-stabilized Zirconia (YSZ) coatings are not yet fully understood. In this work, we use density functional theory calculations to assess the electronic structure of the different YSZ polymorphs at various levels of doping. With the help of population analysis schemes, we are able to unravel the intrinsic mechanisms that govern the interaction in YSZ and that can so explain the relative stabilities of the various polymorphs. We critically compare our results to experimental measurements and discuss the implications of our findings with respect to other oxides.

  14. Zirconia thin film preparation by wet chemical methods at low temperature

    NARCIS (Netherlands)

    Popovici, M.; Graaf, de J.; Verschuuren, M.A.; Graat, P.C.J.; Verheijen, M.A.

    2010-01-01

    In this study the preparation of zirconia thin films with a high refractive index at low temperature is aimed for. Two non-hydrolytic type approaches of wet chemical synthesis are presented. Both by sol–gel and colloid chemistry, highly transmissive, smooth thin films of zirconia cubic and/or

  15. Crystal structures of sol-gel deposited zirconia thin films

    International Nuclear Information System (INIS)

    Bell, J.M.; Cheary, R.W.; Rice, M.; Ben-Nissan, B.; Cocking, J.L.; Johnstone, G.R.

    1992-01-01

    The authors reports on the crystal structure of zirconia thin films by high temperature x-ray diffraction. The films were deposited by sol-gel processing onto polished stainless steel substrates, and dried at 200 deg C. X-ray diffraction at temperatures between 400 deg C and 800 deg C was carried out using an APEX diffractometer with a position sensitive detector. Previous results indicated that there was a transformation between the tetragonal phase and the monoclinic phase at approximately 770 deg C. Two experiments have been carried out: temperature runs, where the structure evolution is studied as a function of temperature; and time evolution of the structure at fixed temperatures. The results for both experiments, including structural analysis of the different phases found in the thin zirconia films and an analysis of the kinetics of the phase transformation(s) from the time evolution work are presented. This will include a comparison with theories of nucleation and crystallisation in single element films. Impurity phases introduced by interaction of the zirconia with the substrate have been observed, and the effect of increasing annealing time on the substrate-film interaction will also be discussed. 17 refs., 1 tab., 3 figs

  16. Fracture toughness improvements of dental ceramic through use of yttria-stabilized zirconia (YSZ) thin-film coatings.

    Science.gov (United States)

    Chan, Ryan N; Stoner, Brian R; Thompson, Jeffrey Y; Scattergood, Ronald O; Piascik, Jeffrey R

    2013-08-01

    The aim of this study was to evaluate strengthening mechanisms of yttria-stabilized zirconia (YSZ) thin film coatings as a viable method for improving fracture toughness of all-ceramic dental restorations. Bars (2mm×2mm×15mm, n=12) were cut from porcelain (ProCAD, Ivoclar-Vivadent) blocks and wet-polished through 1200-grit using SiC abrasive. A Vickers indenter was used to induce flaws with controlled size and geometry. Depositions were performed via radio frequency magnetron sputtering (5mT, 25°C, 30:1 Ar/O2 gas ratio) with varying powers of substrate bias. Film and flaw properties were characterized by optical microscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD). Flexural strength was determined by three-point bending. Fracture toughness values were calculated from flaw size and fracture strength. Data show improvements in fracture strength of up to 57% over unmodified specimens. XRD analysis shows that films deposited with higher substrate bias displayed a high %monoclinic volume fraction (19%) compared to non-biased deposited films (87%), and resulted in increased film stresses and modified YSZ microstructures. SEM analysis shows critical flaw sizes of 67±1μm leading to fracture toughness improvements of 55% over unmodified specimens. Data support surface modification of dental ceramics with YSZ thin film coatings to improve fracture toughness. Increase in construct strength was attributed to increase in compressive film stresses and modified YSZ thin film microstructures. It is believed that this surface modification may lead to significant improvements and overall reliability of all-ceramic dental restorations. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  17. Stabilization of metastable tetragonal zirconia nanocrystallites by surface modification

    DEFF Research Database (Denmark)

    Nielsen, Mette Skovgaard; Almdal, Kristoffer; Lelieveld, A. van

    2011-01-01

    Metastable tetragonal zirconia nanocrystallites were studied in humid air and in water at room temperature (RT). A stabilizing effect of different surfactants on the tetragonal phase was observed. Furthermore, the phase stability of silanized metastable tetragonal zirconia nanocrystallites was te...... exposure to humidity. Only silanes and phosphate esters of these were able to stabilize the tetragonal phase in water. Even as small amounts of silanes as 0.25 silane molecule per nm2 are able to stabilize the tetragonal phase in water at RT. Aminopropyl trimethoxy silane and γ...

  18. Characterization of the yttria-stabilized zirconia thin film electrophoretic deposited on La0.8Sr0.2MnO3 substrate

    International Nuclear Information System (INIS)

    Yang, Koho; Shen, Jung-Hsiung; Yang, Kai-Yun; Hung, I-Ming; Fung, Kuan-Zong; Wang, Moo-Chin

    2007-01-01

    The yttria-stabilized zirconia (YSZ) thin films electrophoretic deposited on the La 0.8 Sr 0.2 MnO 3 (LSM) substrate have been characterized by using zeta potential analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The La 2 Zr 2 O 7 (LZ) formed at the interface between the YSZ thin film and LSM substrate, after sintered at 1400 o C for 52 h, are identified by XRD. The zeta potential of the YSZ particles in pure ethanol-acetone is about 7.8 mV, but when the I 2 concentration is greater than 0.6 g/1, the zeta potential attains a constant value, 46 mV. The relation between deposit weight of the YSZ films and the applied voltage shows a non-linear behavior. Thickness of the YSZ thin film deposited on the LSM substrate by electrophoretic deposition is controlled by a diffusion process. A larger LZ with the thickness of 200 nm is formed at the interface between the YSZ film and the LSM substrate

  19. Grain size stabilization of tetragonal phase of zirconia in sputtered Zr- O cermet films

    Directory of Open Access Journals (Sweden)

    M. S. Hadavi

    2005-06-01

    Full Text Available  In this research, thin films of Zr/ZrO2 composites were deposited by reactive magnetron sputtering technique on Si and fused Silica substrates, and their structures were investigated by XRD method. During the deposition of the cermet layers, a Zr metallic target was sputtered in a gas mixture of Ar and O2. By controlling of O2 flow rate, the different metal volume fractions in the cermet layers were achieved. The optical response of the samples was studied using spectroscopy methods. Also the effect of vacuum annealing on the structures and the optical properties were studied. XRD results indicated that the prepared samples were amorphous and vacuum annealing induced crystallization in the cermet films. This research also showed that without doping, the tetragonal phase of zirconia can be stabilized at a temperature lower than the normal transition temperature. This is “grain size stabilization” and relates to the small size of the crystallites. In order to study the electron diffraction in the selected area patterns (SAD, the samples were analyzed by a high-resolution transmission microscope. The SAD results showed that all of the as prepared samples were amorphous showing evidence of very small Zr crystallites immersed in a dielectric medium.The SAD results are in close agreement with those obtained by XRD analysis.

  20. Ionoluminscence of partially-stabilized zirconia for thermal barrier coatings

    International Nuclear Information System (INIS)

    Rebollo, N.R.; Ruvalcaba-Sil, J.L.; Miranda, J.

    2007-01-01

    Ionoluminescence is explored as an alternative technique to study the high temperature phase stability of zirconia-based oxides. The evolution of an initially metastable single tetragonal phase towards de-stabilization is investigated for three single-doped zirconia compositions with Y, Yb and Gd. The differences in de-stabilization paths are identified using X-ray diffraction and ionoluminescence; elemental analysis is also performed using particle-induced X-ray emission. X-ray diffraction studies reveal a different scenario for each of the compositions selected; the differences are strongly influenced by the thermodynamic driving forces associated to the fluorite-to-tetragonal displacive transformation. Ionoluminescence studies indicate a significant increment on the signal intensity for de-stabilized samples, relative to previous annealing stages. There are also more subtle differences in the luminescent response from the samples at intermediate annealing stages also related to phase changes. This study provides a basis to characterize phase evolution in single-doped zirconia compositions for thermal insulation applications using luminescence

  1. Preparation of epitaxial YBa2Cu3O7-y films on CeO2-buffered yttria-stabilized zirconia substrates by fluorine-free metalorganic deposition

    International Nuclear Information System (INIS)

    Tsukada, Kenichi; Yamaguchi, Iwao; Sohma, Mitsugu; Kondo, Wakichi; Kamiya, Kunio; Kumagai, Toshiya; Manabe, Takaaki

    2007-01-01

    Epitaxial YBa 2 Cu 3 O 7-y (YBCO) films of 120-550 nm thickness have been prepared by fluorine-free metalorganic deposition using a metal acetylacetonate-based coating solution on yttria-stabilized zirconia (YSZ) substrates with an evaporated CeO 2 buffer layer. The YBCO films were highly (0 0 1)-oriented by X-ray diffraction θ-2θ scanning and φ scanning. The YBCO films 120-400 nm in thickness demonstrated high critical current densities (J c ) with an average in excess of 3 MA/cm 2 at 77 K using an inductive method. In particular, a 210-nm-thick film showed a J c of 4.5 MA/cm 2 . These excellent properties are attributed to the high crystallinity, small in-plane fluctuation due to high epitaxy and to the microstructure free from grain boundaries in the YBCO films. Further increase of film thickness increased the fraction of irregularities, i.e., precipitates and micropores, in the film surfaces, resulting in lower J c values

  2. Structural and optical properties of zirconia thin films deposited by reactive high-power impulse magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Xiaoli; Jin, Jie [Tianjin University, School of Electronic Information Engineering, Tianjin (China); Cheng, Jui-Ching, E-mail: juiching@ntut.edu.tw [Chang-Gung University, Department of Electronics, Taoyuan, Taiwan (China); Lee, Jyh-Wei [Ming Chi University of Technology, College of Materials Engineering, New Taipei City, Taiwan (China); Wu, Kuo-Hong [Chang-Gung University, Department of Electronics, Taoyuan, Taiwan (China); Lin, Kuo-Cheng; Tsai, Jung-Ruey [Asia University, Department of Photonics and Communication Engineering, Taichung, Taiwan (China); Liu, Kou-Chen, E-mail: jacobliu@mail.cgu.edu.tw [Chang-Gung University, Department of Electronics, Taoyuan, Taiwan (China)

    2014-11-03

    Zirconia films are deposited by reactive high power impulse magnetron sputtering (HiPIMS) technology on glass and indium-tin-oxide (ITO)/glass substrates. Preparation, microstructure and optical characteristics of the films have been studied. During deposition, the influence of the target power and duty cycle on the peak current–voltage and power density has been observed in oxide mode. Transparent thin films under different oxygen proportions are obtained on the two substrates. Atomic force microscopy measurements showed that the surface roughness of the films was lower by reactive HiPIMS than DC sputtering for all oxygen contents. The transmission and reflectance properties of differently grown zirconia films were also investigated using an ultraviolet–visible spectrophotometer. The optical transmittance of films grown on glass substrates by HiPIMS reached maximum values above 90%, which exceeded that by DC sputtering. The band edge near 5.86 eV shifted to a lower wavelength for zirconia films prepared with oxygen flow rates lower than 4.5 sccm. For the films prepared on ITO/glass substrates, the transmittance and the band gap of zirconia films were limited by ITO films; a maximum average transmittance of 84% was obtained at 4.5 sccm O{sub 2} and the energy band gap was in the range of 3.7–3.8 eV for oxygen flow rates ranging from 3.5 to 5.0 sccm. Finally, the electrical properties of zirconia films have also been discussed. - Highlights: • Zirconia films are deposited by reactive high power impulse magnetron sputtering. • Low roughness films are obtained. • Films show a high transmittance (> 90%). • Films prepared on glass have a band gap of 5.9 eV.

  3. Stability of yttria-stabilized zirconia during pyroprocessing tests

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Eun-Young, E-mail: eychoi@kaeri.re.kr; Lee, Jeong; Lee, Sung-Jai; Kim, Sung-Wook; Jeon, Sang-Chae; Cho, Soo Haeng; Oh, Seung Chul; Jeon, Min Ku; Lee, Sang Kwon; Kang, Hyun Woo; Hur, Jin-Mok

    2016-07-15

    In this study, the feasibility of yttria-stabilized zirconia (YSZ) was investigated for use as a ceramic material, which can be commonly used for both electrolytic reduction and electrorefining. First, the stability of YSZ in salts for electrolytic reduction and electrorefining was examined. Then, its stability was demonstrated by a series of pyroprocessing tests, such as electrolytic reduction, LiCl distillation, electrorefining, and LiCl−KCl distillation, using a single stainless steel wire mesh basket containing fuel and YSZ. A single basket was used by its transportation from one test to subsequent tests without the requirements for unloading.

  4. Effect of SiO2 addition in the zirconia stabilization

    International Nuclear Information System (INIS)

    Pessoa, R.C.; Lima, U.R.; Nasar, M.C.; Nasar, R.S.; Yoshida, I.V.P.; Acchar, W.

    2006-01-01

    The aims of this work was investigated the zirconia stabilization with a mixture of resins based on silico nas promoting the Zr O 2 /Si O 2 formation. The powder was heated and characterized by TGA, DTA, FTIR, XRD and SEM/EDS. The results indicated the tetragonal and cubic phase formation stabilized at 1000 deg C/2 h. The increase of calcing temperature promoted decrease of stabilization. The amorphous silica calcined at 1000 deg C induced defects into the zirconia structure and favour the formation of more stable phases. The decrease of stabilization at high temperatures are related to growth of crystallite above of critical value. (author)

  5. Surface modification of yttria stabilized zirconia by ion implantation

    International Nuclear Information System (INIS)

    Scholten, D.

    1987-01-01

    The results of investigations of surface modification by ion implantation in zirconia are described. As dopant material, iron was investigated thoroughly. The depth distribution of implanted ions depends on implantation parameters and the dopant-matrix system. The investigations of thermal stability of some implanted iron profiles by RBS and AES are described. Special interest lies in the thermal stability under working conditions of the zirconia material (400-1000 0 C). Radiation damage introduced in the implanted layer was investigated using transmission electron microscopy on polycrystalline material and channeling experiments on a single crystal implanted with iron. 179 refs.; 87 figs.; 20 tabs

  6. Preparation and antibacterial properties of hybrid-zirconia films with silver nanoparticles

    International Nuclear Information System (INIS)

    Azócar, Ignacio; Vargas, Esteban; Duran, Nicole; Arrieta, Abel; González, Evelyn

    2012-01-01

    The antimicrobial effect of incorporating silver nanoparticles (AgNps) into zirconia matrix–polyether glycol was studied. AgNps of 4–6 nm in size were synthesized using the inverse micelles method, and different doses of metallic nanoparticles were incorporated into zirconia–polyether glycol mixtures during the ageing procedure. Atomic force microscopy (AFM) of the modified hybrid film showed a homogenous distribution of 20–80 nm diameter AgNps, indicating agglomeration of these structures during film modification; such agglomerations were greater when increasing the dosage of the colloidal system. The AgNps-hybrid films showed higher antimicrobial activity against Gram-positive bacteria than for Gram-negative bacteria. Hybrid films prepared with dioctyl sodium sulfosuccinate (AOT) stabilized AgNps presented enhanced antibacterial activity compared to that obtained through the addition of a high AgNO 3 concentration (0.3 wt%). -- Graphical abstract: Atomic Force Micrographs, top and cross section view, showing silver nanoparticles embedded in a zirconia–polyether glycol hybrid film. Highlights: ► Antibacterial activity of films (zirconia–polyether glycol) modified with silver nanoparticles. ► Biofilm formation is prevented. ► High sensibility against gram positive bacteria.

  7. Characterization of plasma sprayed NiCrAlY-Yttria stabilized zirconia coatings

    International Nuclear Information System (INIS)

    Bhave, V.S.; Rakhasia, R.H.; Tripathy, P.K.; Hubli, R.C.; Sengupta, P.; Bhanumurthy; Satpute, R.U.; Sreekumar, K.P.; Thiyagarajan, T.K.; Padmanabhan, P.V.A.

    2004-01-01

    Plasma sprayed coatings of yttria stabilized zirconia are used in many advanced technologies for thermal and chemical barrier applications. Development and characterization of NiCrAlY-yttria stabilized zirconia duplex coatings on Inconel substrates is reported in this paper. Plasma spraying was carried out using the 40 kW atmospheric plasma spray facility at the Laser and Plasma Technology Division, BARC. A bond coat of NiCrAlY was deposited on Inconel substrates and yttria stabilized zirconia (YSZ) was deposited over the bond coat. The coatings have been characterized by x-ray diffraction and EPMA. It is observed that the coating characteristics are affected by the input power to the torch. (author)

  8. Controlling Microstructure of Yttria-Stabilized Zirconia Prepared from Suspensions and Solutions by Plasma Spraying with High Feed Rates.

    Czech Academy of Sciences Publication Activity Database

    Mušálek, Radek; Medřický, Jan; Tesař, Tomáš; Kotlan, Jiří; Pala, Zdeněk; Lukáč, František; Illková, Ksenia; Hlína, Michal; Chráska, Tomáš; Sokołowski, P.; Curry, N.

    2017-01-01

    Roč. 26, č. 8 (2017), s. 1787-1803 ISSN 1059-9630 R&D Projects: GA ČR GA15-12145S Institutional support: RVO:61389021 Keywords : hybrid plasma torch * microstructure * solution * precursor spraying * suspension spraying * thermal barrier * coatings (TBCs) * water-stabilized plasma * yttria-stabilized zirconia (YSZ) Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films Impact factor: 1.488, year: 2016 https://link.springer.com/ article /10.1007/s11666-017-0622-x

  9. Synthesis of zirconia sol stabilized by trivalent cations (yttrium and neodymium or americium): a precursor for Am-bearing cubic stabilized zirconia.

    Science.gov (United States)

    Lemonnier, Stephane; Grandjean, Stephane; Robisson, Anne-Charlotte; Jolivet, Jean-Pierre

    2010-03-07

    Recent concepts for nuclear fuel and targets for transmuting long-lived radionuclides (minor actinides) and for the development of innovative Gen-IV nuclear fuel cycles imply fabricating host phases for actinide or mixed actinide compounds. Cubic stabilized zirconia (Zr, Y, Am)O(2-x) is one of the mixed phases tested in transmutation experiments. Wet chemical routes as an alternative to the powder metallurgy are being investigated to obtain the required phases while minimizing the handling of contaminating radioactive powder. Hydrolysis of zirconium, neodymium (a typical surrogate for americium) and yttrium in aqueous media in the presence of acetylacetone was firstly investigated. Progressive hydrolysis of zirconium acetylacetonate and sorption of trivalent cations and acacH on the zirconia particles led to a stable dispersion of nanoparticles (5-7 nm) in the 6-7 pH range. This sol gels with time or with temperature. The application to americium-containing solutions was then successfully tested: a stable sol was synthesized, characterized and used to prepare cubic stabilized zirconia (Zr, Y, Am)O(2-x).

  10. Investigation of the evaporation process conditions on the optical constants of zirconia films

    International Nuclear Information System (INIS)

    Dobrowolski, J.A.; Grant, P.D.; Simpson, R.; Waldorf, A.

    1989-01-01

    Deposition parameters required for producing zirconia films for use in optical multilayer systems by electron-beam gun evaporation of zirconia and zirconium starting materials were investigated. The optical constants were determined as a function of distance, partial pressure of oxygen, and angle of incidence. The direct and reactive evaporation processes yielded ZrO 2 films with refractive indices of 2.08 and 2.14, respectively, for vapor incident on the substrate at normal incidence

  11. Novel transparent ternary nanocomposite films of trialkoxysilane-capped poly(methyl methacrylate)/zirconia/titania with incorporating networks

    International Nuclear Information System (INIS)

    Wang Yuan; Zhang Dengsong; Shi Liyi; Li Li; Zhang Jianping

    2008-01-01

    Novel ternary nanocomposite trialkoxysilane-capped poly(methyl methacrylate)/zirconia/titania optical films were successfully prepared through a nonaqueous in situ sol-gel method. The acrylic monomers used were methyl methacrylate (MMA) and 3-(trimethoxysilyl)propyl methacrylate (MSMA). PMMA/ZrO 2 -TiO 2 incorporating networks formed from alcoholysis of poly(MMA-co-MSMA), zirconium n-butoxide and titanium isoproproxide. The structure, morphology and property of the obtained nanocomposite films were investigated by X-ray photoelectron spectra, Fourier transform infrared spectroscopy, field emission scanning electron microscopy, scanning probe microscopy, thermogravimetric analyses, UV-vis spectrum and spectro-ellipsometer. The nanoparticle size, roughness, thermal stability, UV-shielding property, and refractive index of nanocomposite films increase with the increasing of inorganic contents. The formation mechanism and reason of such improvements were examined and interpreted in a theoretical model. The nanocomposite films possess interesting properties in thermal stability and optical response due to the uniform incorporating networks between organic polymer chains and inorganic clusters

  12. Novel transparent ternary nanocomposite films of trialkoxysilane-capped poly(methyl methacrylate)/zirconia/titania with incorporating networks

    Energy Technology Data Exchange (ETDEWEB)

    Wang Yuan [Research Center of Nano Science and Technology, Department of Chemistry, Shanghai University, Shanghai 200444 (China); Zhang Dengsong [Research Center of Nano Science and Technology, Department of Chemistry, Shanghai University, Shanghai 200444 (China)], E-mail: dszhang@shu.edu.cn; Shi Liyi [Research Center of Nano Science and Technology, Department of Chemistry, Shanghai University, Shanghai 200444 (China)], E-mail: sly0726@163.com; Li Li; Zhang Jianping [Research Center of Nano Science and Technology, Department of Chemistry, Shanghai University, Shanghai 200444 (China)

    2008-08-15

    Novel ternary nanocomposite trialkoxysilane-capped poly(methyl methacrylate)/zirconia/titania optical films were successfully prepared through a nonaqueous in situ sol-gel method. The acrylic monomers used were methyl methacrylate (MMA) and 3-(trimethoxysilyl)propyl methacrylate (MSMA). PMMA/ZrO{sub 2}-TiO{sub 2} incorporating networks formed from alcoholysis of poly(MMA-co-MSMA), zirconium n-butoxide and titanium isoproproxide. The structure, morphology and property of the obtained nanocomposite films were investigated by X-ray photoelectron spectra, Fourier transform infrared spectroscopy, field emission scanning electron microscopy, scanning probe microscopy, thermogravimetric analyses, UV-vis spectrum and spectro-ellipsometer. The nanoparticle size, roughness, thermal stability, UV-shielding property, and refractive index of nanocomposite films increase with the increasing of inorganic contents. The formation mechanism and reason of such improvements were examined and interpreted in a theoretical model. The nanocomposite films possess interesting properties in thermal stability and optical response due to the uniform incorporating networks between organic polymer chains and inorganic clusters.

  13. Hardness Enhancement of STS304 Deposited with Yttria Stabilized Zirconia by Aerosol Deposition Method

    Energy Technology Data Exchange (ETDEWEB)

    Lim, Il-Ho; Park, Chun-Kil; Kim, Hyung Sun; Jeong, Dea-Yong [Inha University, Incheon (Korea, Republic of); Lee, Yong-Seok [Sodoyeon Co., Yeoju (Korea, Republic of); Kong, Young-Min [University of Ulsan, Ulsan (Korea, Republic of); Kang, Kweon Ho [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2016-03-15

    To improve the surface hardness of the STS304, Yttria stabilized zirconia (YSZ) films with nano-sized grain were deposited by an aerosol-deposition (AD) method. Coating layers showed dense structure and had -5µm thickness. When 3 mol% YSZ powders with tetragonal phase were deposited on STS304 substrate, tetragonal structure was transformed to cubic structure due to the high impact energy during the AD process. At the same time, strong impact by YSZ particles allowed the austenite phase in STS304 to be transformed into martensite phase. Surface hardness measured with nano indentor showed that YSZ coated film had 11.5 GPa, which is larger value than 7 GPa of STS304.

  14. Stabilized zirconia with cerium and neodymium addition

    International Nuclear Information System (INIS)

    Andrade, I.M. de; Pessoa, R.C.; Nasar, M.C.; Nasar, R.S.; Rodriques, M.K.C.; Oliveira, J.F.

    2006-01-01

    Zr 0,9 Ce 0,05 Nd 0,05 O 1,975 system was synthesized with the use of the Pechini method. The polymeric resin was calcined at 350 deg C/3 h and analysed by FTIR that show bands relative to organic. Radicals esther type. The TGA curve indicated the polymeric decomposition occurring from 30 deg C to 740 deg C. DTA analysis show a exothermic peak in 100 deg C due to loss of water of material. From 500 deg C to 800 deg C was observed a intense peak due to polymer decomposition and the zirconia crystallization. The calcined powder from 350 deg C/3 h e 30 min to 900 deg/3 h were analysed by XRD that show the crystalline phase formation with the increase of temperature. The X-ray diffraction pattern show the presence of two phases, such as tetragonal and cubic of zirconia demonstrating that neodymium and cerium additions led to zirconia stabilization. (author)

  15. Structure and chemistry of epitaxial ceria thin films on yttria-stabilized zirconia substrates, studied by high resolution electron microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Sinclair, Robert, E-mail: bobsinc@stanford.edu [Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305 (United States); Lee, Sang Chul, E-mail: sclee99@stanford.edu [Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305 (United States); Shi, Yezhou; Chueh, William C. [Department of Materials Science and Engineering, Stanford University, Stanford, CA 94305 (United States); Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory, Menlo Park, CA 94025 (United States); Stanford Institute for Materials and Energy Sciences, SLAC National Accelerator Laboratory, Menlo Park, CA 94025 (United States)

    2017-05-15

    We have applied aberration-corrected transmission electron microscopy (TEM) imaging and electron energy loss spectroscopy (EELS) to study the structure and chemistry of epitaxial ceria thin films, grown by pulsed laser deposition onto (001) yttria-stabilized zirconia (YSZ) substrates. There are few observable defects apart from the expected mismatch interfacial dislocations and so the films would be expected to have good potential for applications. Under high electron beam dose rate (above about 6000 e{sup -}/Å{sup 2}s) domains of an ordered structure appear and these are interpreted as being created by oxygen vacancy ordering. The ordered structure does not appear at lower lose rates (ca. 2600 e{sup -}/Å{sup 2}s) and can be removed by imaging under 1 mbar oxygen gas in an environmental TEM. EELS confirms that there is both oxygen deficiency and the associated increase in Ce{sup 3+} versus Ce{sup 4+} cations in the ordered domains. In situ high resolution TEM recordings show the formation of the ordered domains as well as atomic migration along the ceria thin film (001) surface. - Highlights: • The local structure and chemistry of ceria can be studied by TEM combined with EELS. • At lower electron, there are no observable changes in the ceria thin films. • At higher dose rates, an ordered phase is created due to oxygen vacancy ordering. • In situ HRTEM shows the oxygen vacancy ordering and the movement of surface atoms.

  16. Characterization of the yttria-stabilized zirconia thin film electrophoretic deposited on La{sub 0.8}Sr{sub 0.2}MnO{sub 3} substrate

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Koho [Department of Mold and Die Engineering, National Kaohsiung University of Applied Sciences, 415 Chien-Kung Rode, Kaohsiung 80782, Taiwan (China); Shen, Jung-Hsiung [Department of Mold and Die Engineering, National Kaohsiung University of Applied Sciences, 415 Chien-Kung Rode, Kaohsiung 80782, Taiwan (China); Yang, Kai-Yun [Department of Materials Science and Engineering, National Chen Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Hung, I-Ming [Department of Materials Science and Engineering, National Chen Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Department of Chemical Engineering and Materials Science, Yuan Ze University, 135 Yuan-Tung Road, Chungli, Taoyunn 320, Taiwan (China); Fung, Kuan-Zong [Department of Materials Science and Engineering, National Chen Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Wang, Moo-Chin [Faculty of Fragrance and Cosmetics, Kaohsiung Medical University, 100 Shi-Chuan 1st Road, Kaohsiung 807, Taiwan (China)]. E-mail: mcwang@kmu.edu.tw

    2007-06-14

    The yttria-stabilized zirconia (YSZ) thin films electrophoretic deposited on the La{sub 0.8}Sr{sub 0.2}MnO{sub 3} (LSM) substrate have been characterized by using zeta potential analysis, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The La{sub 2}Zr{sub 2}O{sub 7} (LZ) formed at the interface between the YSZ thin film and LSM substrate, after sintered at 1400 {sup o}C for 52 h, are identified by XRD. The zeta potential of the YSZ particles in pure ethanol-acetone is about 7.8 mV, but when the I{sub 2} concentration is greater than 0.6 g/1, the zeta potential attains a constant value, 46 mV. The relation between deposit weight of the YSZ films and the applied voltage shows a non-linear behavior. Thickness of the YSZ thin film deposited on the LSM substrate by electrophoretic deposition is controlled by a diffusion process. A larger LZ with the thickness of 200 nm is formed at the interface between the YSZ film and the LSM substrate.

  17. Kinetics of hydrothermally induced transformation of yttria partially stabilized zirconia

    International Nuclear Information System (INIS)

    Payyapilly, J.J.; Butt, D.P.

    2007-01-01

    Yttria-stabilized zirconia undergoes tetragonal to monoclinic phase transformation under hydrothermal conditions in the temperature range of 150-350 deg. C. Phase transformation accompanied by volume change in bulk yttria partially stabilized zirconia (YPSZ) leads to micro-cracking, loss of mechanical integrity and ultimately disintegration. The mechanical properties of the bulk YPSZ material deteriorate with the amount of the phase transformation and in some cases catastrophic failure are observed. The phase transformation is analyzed using macroscopic and microscopic techniques. X-ray diffraction data is used to quantify the phase transformation in bulk material. Kinetics of the phase transformation is studied at various temperatures

  18. Dense zig-zag microstructures in YSZ thin films by pulsed laser deposition

    Science.gov (United States)

    Stender, Dieter; Schäuble, Nina; Weidenkaff, Anke; Montagne, Alex; Ghisleni, Rudy; Michler, Johann; Schneider, Christof W.; Wokaun, Alexander; Lippert, Thomas

    2015-01-01

    The very brittle oxygen ion conductor yttria stabilized zirconia (YSZ) is a typical solid electrolyte for miniaturized thin film fuel cells. In order to decrease the fuel cell operating temperature, the thickness of yttria stabilized zirconia thin films is reduced. Often, these thin membranes suffer from mechanical failure and gas permeability. To improve these mechanical issues, a glancing angle deposition approach is used to grow yttria stabilized zirconia thin films with tilted columnar structures. Changes of the material flux direction during the deposition result in a dense, zigzag-like structure with columnar crystallites. This structure reduces the elastic modulus of these membranes as compared to columnar yttria stabilized zirconia thin films as monitored by nano-indentation which makes them more adaptable to applied stress.

  19. Dense zig-zag microstructures in YSZ thin films by pulsed laser deposition

    Directory of Open Access Journals (Sweden)

    Dieter Stender

    2015-01-01

    Full Text Available The very brittle oxygen ion conductor yttria stabilized zirconia (YSZ is a typical solid electrolyte for miniaturized thin film fuel cells. In order to decrease the fuel cell operating temperature, the thickness of yttria stabilized zirconia thin films is reduced. Often, these thin membranes suffer from mechanical failure and gas permeability. To improve these mechanical issues, a glancing angle deposition approach is used to grow yttria stabilized zirconia thin films with tilted columnar structures. Changes of the material flux direction during the deposition result in a dense, zigzag-like structure with columnar crystallites. This structure reduces the elastic modulus of these membranes as compared to columnar yttria stabilized zirconia thin films as monitored by nano-indentation which makes them more adaptable to applied stress.

  20. HRTEM investigation of phase stability in alumina–zirconia ...

    Indian Academy of Sciences (India)

    tries, at high temperatures, the small diffusion lengths involved can influence the phase stability. The present work ... a function of nanocrystalline size has been shown by Shukla ... and zirconia on a Si(100) single crystal substrate with differ-.

  1. Mixed zirconia calcium phosphate coatings for dental implants: Tailoring coating stability and bioactivity potential

    International Nuclear Information System (INIS)

    Pardun, Karoline; Treccani, Laura; Volkmann, Eike; Streckbein, Philipp; Heiss, Christian; Destri, Giovanni Li; Marletta, Giovanni; Rezwan, Kurosch

    2015-01-01

    Enhanced coating stability and adhesion are essential for long-term success of orthopedic and dental implants. In this study, the effect of coating composition on mechanical, physico-chemical and biological properties of coated zirconia specimens is investigated. Zirconia discs and dental screw implants are coated using the wet powder spraying (WPS) technique. The coatings are obtained by mixing yttria-stabilized zirconia (TZ) and hydroxyapatite (HA) in various ratios while a pure HA coating served as reference material. Scanning electron microscopy (SEM) and optical profilometer analysis confirm a similar coating morphology and roughness for all studied coatings, whereas the coating stability can be tailored with composition and is probed by insertion and dissections experiments in bovine bone with coated zirconia screw implants. An increasing content of calcium phosphate (CP) resulted in a decrease of mechanical and chemical stability, while the bioactivity increased in simulated body fluid (SBF). In vitro experiments with human osteoblast cells (HOB) revealed that the cells grew well on all samples but are affected by dissolution behavior of the studied coatings. This work demonstrates the overall good mechanical strength, the excellent interfacial bonding and the bioactivity potential of coatings with higher TZ contents, which provide a highly interesting coating for dental implants. - Highlights: • Different ratios of zirconia (TZ) and calcium phosphate (CP) were deposited on zirconia substrates. • Enhancement of TZ content in mixed coatings increased coating stability. • Enhancement of CP content in mixed coatings increased bioactivity. • All tested coating compositions were non-toxic

  2. Mixed zirconia calcium phosphate coatings for dental implants: Tailoring coating stability and bioactivity potential

    Energy Technology Data Exchange (ETDEWEB)

    Pardun, Karoline [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Treccani, Laura, E-mail: treccani@uni-bremen.de [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Volkmann, Eike [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Streckbein, Philipp [University Hospital, Justus-Liebig-University Giessen, Department of Cranio-Maxillo-Facial Surgery, Klinikstrasse 33, 35385 Giessen (Germany); Heiss, Christian [University Hospital of Giessen-Marburg, Department of Trauma Surgery, Rudolf-Buchheim-Strasse 7, 35385 Giessen, Germany, (Germany); Laboratory of Experimental Surgery, Kerkraderstrasse 9, 35392 Giessen (Germany); Destri, Giovanni Li; Marletta, Giovanni [Laboratory for Molecular Surfaces and Nanotechnology (LAMSUN), Department of Chemistry, University of Catania and CSGI, Viale A. Doria 6, 95125 Catania (Italy); Rezwan, Kurosch [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany)

    2015-03-01

    Enhanced coating stability and adhesion are essential for long-term success of orthopedic and dental implants. In this study, the effect of coating composition on mechanical, physico-chemical and biological properties of coated zirconia specimens is investigated. Zirconia discs and dental screw implants are coated using the wet powder spraying (WPS) technique. The coatings are obtained by mixing yttria-stabilized zirconia (TZ) and hydroxyapatite (HA) in various ratios while a pure HA coating served as reference material. Scanning electron microscopy (SEM) and optical profilometer analysis confirm a similar coating morphology and roughness for all studied coatings, whereas the coating stability can be tailored with composition and is probed by insertion and dissections experiments in bovine bone with coated zirconia screw implants. An increasing content of calcium phosphate (CP) resulted in a decrease of mechanical and chemical stability, while the bioactivity increased in simulated body fluid (SBF). In vitro experiments with human osteoblast cells (HOB) revealed that the cells grew well on all samples but are affected by dissolution behavior of the studied coatings. This work demonstrates the overall good mechanical strength, the excellent interfacial bonding and the bioactivity potential of coatings with higher TZ contents, which provide a highly interesting coating for dental implants. - Highlights: • Different ratios of zirconia (TZ) and calcium phosphate (CP) were deposited on zirconia substrates. • Enhancement of TZ content in mixed coatings increased coating stability. • Enhancement of CP content in mixed coatings increased bioactivity. • All tested coating compositions were non-toxic.

  3. Cluster-assembled cubic zirconia films with tunable and stable nanoscale morphology against thermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Borghi, F.; Lenardi, C.; Podestà, A.; Milani, P., E-mail: pmilani@mi.infn.it [CIMAINA and Dipartimento di Fisica, Università degli Studi di Milano, via Celoria 16, 20133 Milano (Italy); Sogne, E. [CIMAINA and Dipartimento di Fisica, Università degli Studi di Milano, via Celoria 16, 20133 Milano (Italy); European School of Molecular Medicine (SEMM), IFOM-IEO, Milano (Italy); Merlini, M. [Dipartimento di Scienze della Terra “Ardito Desio”, Università degli Studi di Milano, via Mangiagalli 32, 20133 Milano (Italy); Ducati, C. [Department of Materials Science and Metallurgy, University of Cambridge, 27 Charles Babbage Road, Cambridge CB3 0FS (United Kingdom)

    2016-08-07

    Nanostructured zirconium dioxide (zirconia) films are very promising for catalysis and biotechnological applications: a precise control of the interfacial properties of the material at different length scales and, in particular, at the nanoscale, is therefore necessary. Here, we present the characterization of cluster-assembled zirconia films produced by supersonic cluster beam deposition possessing cubic structure at room temperature and controlled nanoscale morphology. We characterized the effect of thermal annealing in reducing and oxidizing conditions on the crystalline structure, grain dimensions, and topography. We highlight the mechanisms of film growth and phase transitions, which determine the observed interfacial morphological properties and their resilience against thermal treatments.

  4. Cluster-assembled cubic zirconia films with tunable and stable nanoscale morphology against thermal annealing

    International Nuclear Information System (INIS)

    Borghi, F.; Lenardi, C.; Podestà, A.; Milani, P.; Sogne, E.; Merlini, M.; Ducati, C.

    2016-01-01

    Nanostructured zirconium dioxide (zirconia) films are very promising for catalysis and biotechnological applications: a precise control of the interfacial properties of the material at different length scales and, in particular, at the nanoscale, is therefore necessary. Here, we present the characterization of cluster-assembled zirconia films produced by supersonic cluster beam deposition possessing cubic structure at room temperature and controlled nanoscale morphology. We characterized the effect of thermal annealing in reducing and oxidizing conditions on the crystalline structure, grain dimensions, and topography. We highlight the mechanisms of film growth and phase transitions, which determine the observed interfacial morphological properties and their resilience against thermal treatments.

  5. Cluster-assembled cubic zirconia films with tunable and stable nanoscale morphology against thermal annealing

    KAUST Repository

    Borghi, F.

    2016-08-05

    Nanostructured zirconium dioxide (zirconia) films are very promising for catalysis and biotechnological applications: a precise control of the interfacial properties of the material at different length scales and, in particular, at the nanoscale, is therefore necessary. Here, we present the characterization of cluster-assembled zirconia films produced by supersonic cluster beam deposition possessing cubic structure at room temperature and controlled nanoscale morphology. We characterized the effect of thermal annealing in reducing and oxidizing conditions on the crystalline structure, grain dimensions, and topography. We highlight the mechanisms of film growth and phase transitions, which determine the observed interfacial morphological properties and their resilience against thermal treatments. Published by AIP Publishing.

  6. Cluster-assembled cubic zirconia films with tunable and stable nanoscale morphology against thermal annealing

    KAUST Repository

    Borghi, F.; Sogne, Elisa; Lenardi, C.; Podestà , A.; Merlini, M.; Ducati, C.; Milani, P.

    2016-01-01

    Nanostructured zirconium dioxide (zirconia) films are very promising for catalysis and biotechnological applications: a precise control of the interfacial properties of the material at different length scales and, in particular, at the nanoscale, is therefore necessary. Here, we present the characterization of cluster-assembled zirconia films produced by supersonic cluster beam deposition possessing cubic structure at room temperature and controlled nanoscale morphology. We characterized the effect of thermal annealing in reducing and oxidizing conditions on the crystalline structure, grain dimensions, and topography. We highlight the mechanisms of film growth and phase transitions, which determine the observed interfacial morphological properties and their resilience against thermal treatments. Published by AIP Publishing.

  7. Electrochemical behaviour of ceramic yttria stabilized zirconia on carbon steel synthesized via sol-gel process

    International Nuclear Information System (INIS)

    Crespo, M.A. Dominguez; Murillo, A. Garcia; Torres-Huerta, A.M.; Yanez-Zamora, C.; Carrillo-Romo, F. de J

    2009-01-01

    Chromate conversion coatings have been widely applied for the corrosion of different metallic substrates. However, the waste containing Cr 6+ has many limitations due to the environmental consideration and health hazards. An interesting alternative seems to be the deposition on metallic surface of thin layers of yttria or zirconia or both by the sol-gel process. In this study, Ytttria and Yttria stabilized zirconia (YSZ, 8% Y 2 O 3 ) thin films were used for coating commercial carbon steel substrates by sol-gel method and the dip-coating process. The evolution of organic compounds up to crystallization process as a function of heat treatments was study by FT-IR spectroscopy. The structure and morphology of the coatings were analysed using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The anticorrosion performance of the coatings has been evaluated by using electrochemical techniques in an aggressive media (3.5 wt.% NaCl). The corrosion behaviour of sol-gel method was compared with traditional chromate conversion coatings. Differences in the electrochemical behaviour of YSZ coatings are related to the development of microcracks during the sintering process and to the presence of organic compounds during growth film. Electrochemical results showed that sol-gel YSZ and Y 2 O 3 coatings can act as protective barriers against wet corrosion; however yttria films displayed low adhesion to substrate. The corrosion parameters provide an explanation of the role of each film and show a considerable increase in the corrosion resistance for coated samples in comparison to the bare steel samples.

  8. Electrochemical behaviour of ceramic yttria stabilized zirconia on carbon steel synthesized via sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Crespo, M.A. Dominguez, E-mail: mdominguezc@ipn.m [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada, Unidad Altamira (CICATA-IPN) km 14.5 Carr. Tampico-Puerto Industrial, C.P. 89600, Altamira, Tamaulipas (Mexico); Murillo, A. Garcia; Torres-Huerta, A.M. [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada, Unidad Altamira (CICATA-IPN) km 14.5 Carr. Tampico-Puerto Industrial, C.P. 89600, Altamira, Tamaulipas (Mexico); Yanez-Zamora, C. [Estudiante del postgrado en Tecnologia Avanzada del CICATA-IPN, Unidad Altamira, km 14.5, Carr. Tampico-Puerto Industrial. C.P. 89600, Altamira, Tamaulipas (Mexico); Carrillo-Romo, F. de J [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada, Unidad Altamira (CICATA-IPN) km 14.5 Carr. Tampico-Puerto Industrial, C.P. 89600, Altamira, Tamaulipas (Mexico)

    2009-08-26

    Chromate conversion coatings have been widely applied for the corrosion of different metallic substrates. However, the waste containing Cr{sup 6+} has many limitations due to the environmental consideration and health hazards. An interesting alternative seems to be the deposition on metallic surface of thin layers of yttria or zirconia or both by the sol-gel process. In this study, Ytttria and Yttria stabilized zirconia (YSZ, 8% Y{sub 2}O{sub 3}) thin films were used for coating commercial carbon steel substrates by sol-gel method and the dip-coating process. The evolution of organic compounds up to crystallization process as a function of heat treatments was study by FT-IR spectroscopy. The structure and morphology of the coatings were analysed using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The anticorrosion performance of the coatings has been evaluated by using electrochemical techniques in an aggressive media (3.5 wt.% NaCl). The corrosion behaviour of sol-gel method was compared with traditional chromate conversion coatings. Differences in the electrochemical behaviour of YSZ coatings are related to the development of microcracks during the sintering process and to the presence of organic compounds during growth film. Electrochemical results showed that sol-gel YSZ and Y{sub 2}O{sub 3} coatings can act as protective barriers against wet corrosion; however yttria films displayed low adhesion to substrate. The corrosion parameters provide an explanation of the role of each film and show a considerable increase in the corrosion resistance for coated samples in comparison to the bare steel samples.

  9. Methods for improving mechanical properties of partially stabilized zirconia and the resulting product

    International Nuclear Information System (INIS)

    Aronov, V.A.

    1987-01-01

    A method for improving mechanical surface properties of a rigid body comprising partially stabilized zirconia as a constituent is described comprising the following steps: (i) providing a rigid body having an exposed surface and an interior volume; (ii) subjecting the exposed surface region of partially stabilized zirconia to external heating to heat the exposed surface region to 1100 0 C-1600 0 C without heating the interior volume above 500 0 C-800 0 C; and (iii) cooling the rigid body to a temperature of less than 500 0 C to cause a portion of the exposed surface region to transform from the tetragonal lattice modification to the monoclinic lattice modification, thereby creating a compressive stress field in the exposed surface region and improving the mechanical surface properties of the exposed surface region. In a ceramic body comprising a first exposed region of a partially stabilized zirconia, and a second region of a partially stabilized zirconia at an interior portion of the ceramic body, the improvement is described comprising the ceramic body having in the first, exposed region a greater percentage of the monoclinic lattice modification than in the second region; having in the first, exposed region 5 percent to 100 percent in the monoclinic lattice modification; and having a molded surface finish in the first, exposed region; the first, exposed region being subjected to a compressive field resulting from the greater percentage of the monoclinic lattice modification

  10. Characterization on the electrophoretic deposition of the 8 mol% yttria-stabilized zirconia nanocrystallites prepared by a sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Y.-H. [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Kuo, C.-W. [Department of Resources Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Shih, C.-J. [Faculty of Fragrance and Cosmetics, Kaohsiung Medical University, 100 Shi-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Hung, I-M. [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Fung, K.-Z. [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Wen, S.-B. [Department of Resources Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Wang, M.-C. [Faculty of Fragrance and Cosmetics, Kaohsiung Medical University, 100 Shi-Chuan 1st Road, Kaohsiung 807, Taiwan (China)]. E-mail: cjshih@kmu.edu.tw

    2007-02-15

    An 8 mol% yttria-stabilized zirconia (8YSZ) films are electrophoretically deposited on the La{sub 0.8}Sr{sub 0.2}MnO{sub 3} substrate using 8YSZ nanocrystallites prepared by a sol-gel process. Effects of liquid suspension on the particle zeta potential and degree of agglomeration at different pH values are investigated. When the pH value deviates from the point of zero charge (PZC), the adsorption of protons on particle surfaces cause higher zeta potential and well-dispersed suspension. The optimal values of the iodine concentration, applied voltage and deposition time for the electrophoretic deposition of 8YSZ films are also found.

  11. Microscopic mechanism of stability in yttria-doped zirconia

    CERN Document Server

    Ostanin, S A

    2001-01-01

    The relaxed configurations of yttria-stabilized zirconia (YSZ) between 3 and 10 mol. % Y sub 2 O sub 3 were modeled within the pseudopotential technique. The vibration mode corresponding to the soft phonon in pure c-ZrO sub 2 has been calculated for each Y sub 2 O sub 3 composition. These anharmonic vibrations, associated with stabilization of YSZ, have been investigated within the self-consistent phonon approximation that makes obtainable the fine structure in spectral density. In studying the phonon dynamics, it is proposed to use the displacement probability density which can quantify very accurately the transition temperature needed to stabilize the YSZ cubic phase

  12. Absence of Dopant Segregation to the Surface of Scandia and Yttria Co-Stabilized Zirconia

    DEFF Research Database (Denmark)

    Vels Hansen, Karin; Mogensen, Mogens Bjerg

    2012-01-01

    stabilized zirconia. The probable reason for this is that due to its size the Sc3+ ion fits better in the zirconia lattice than Y3+ does. The difference in surface composition may be the explanation for the observed increased tolerance toward sulfur of Ni-ScYSZ compared to Ni-YSZ cermets....

  13. Investigation of phase stability in the scandia-zirconia

    International Nuclear Information System (INIS)

    Grosso, Robson Lopes

    2016-01-01

    In this work, the phase stability of scandia-zirconia (ScSZ) system was investigated by the thermodynamic study of nanoparticles, within the range of 0 to 20 mol% Sc 2 O 3 , and by codoping of ZrO 2 -10 mol% Sc 2 O 3 (10ScSZ) with Dy 2 O 3 and Nb 2 O 5 . The phase stability of ScSZ was evaluated based on thermodynamic data collected by water adsorption microcalorimetry and high temperature oxide melt solution. Nanostructured zirconia-scandia solid solutions were synthesized by coprecipitation method. Thermodynamic data were determined for ScSZ polymorph (monoclinic, tetragonal, cubic, rhombohedral β and γ) found by X-ray diffraction. This systemic work resulted in an unprecedented phase diagram at the nanoscale of particle size-composition. The effects of additives on 10ScSZ were investigated aiming to stabilize the cubic (c) structure at room temperature and to suppress the characteristic cubic-rhombohedral β phase transformation. Compositions were prepared by coprecipitation and solid state reaction. Materials were sintered by conventional and spark plasma sintering. Full stabilization of the cubic phase was attained by 1 mol% Dy 2 O 3 and 0.5 mol% Nb 2 O 5 additions. The smallest Nb 2 O 5 content required for cubic phase stabilization was attributed to liquid phase formation during sintering and to small ionic radius of Nb 5+ . Results of high temperature X-ray diffraction and thermal analysis show suppression of the c-β transformation. Samples containing 0.5 mol% Nb 2 O 5 show total ionic conductivity similar to 10ScSZ without additives within a broad temperature range with high stability during 170 h at 600 °C. (author)

  14. Experimental R-curve behavior in partially stabilized zirconia using moiracute e interferometry

    International Nuclear Information System (INIS)

    Perry, K.E.; Okada, H.; Atluri, S.N.

    1993-01-01

    Moiracute e interferometry is employed to study toughening in partially stabilized zirconia (PSZ). Energy to fracture as a function of crack growth curves (R-curves) is derived from mode I compliance calculations and from near tip fitting of the moiracute e fringes. The effect of the tetragonal to monoclinic phase transformation in the zirconia is found by comparing the bulk compliance R-curves to the locally derived moiracute e R-curve. Localized strain field plots are produced from the moiracute e data for the PSZ zirconia. The observed transformation zone height compares favorably with that predicted by Okada et al. in a companion paper, as does the qualitative nature of the R-curve with predictions by Stump and Budiansky

  15. Zirconia nano-colloids transfer from continuous hydrothermal synthesis to inkjet printing

    DEFF Research Database (Denmark)

    Rosa, Massimo; Gooden, P. N.; Butterworth, S.

    2017-01-01

    Water dispersions of nanometric yttria stabilized zirconia (YSZ) particles synthesized by Continuous Hydrothermal Synthesis are transferred into nano-inks for thin film deposition. YSZ nanoparticles are synthesized in supercritical conditions resulting in highly dispersed crystals of 10 nm in size...

  16. Growth and micro structural studies on Yittria Stabilized Zirconia (YSZ) and Strontium Titanate (STO) buffer layers

    Energy Technology Data Exchange (ETDEWEB)

    Srinivas, S.; Bhatnagar, A.K. [Univ. of Hyderabad (India); Pinto, R. [Solid State Electronics Group, Bombay (India)] [and others

    1994-12-31

    Microstructure of Yittria Stabilized Zirconia (YSZ) and Strontium Titanate (STO) of radio frequency magnetron sputtered buffer layers was studied at various sputtering conditions on Si<100>, Sapphire and LaAlO{sub 3} <100> substrates. The effect of substrate temperatures upto 800 C and sputtering gas pressures in the range of 50 mTorr. of growth conditions was studied. The buffer layers of YSZ and STO showed a strong tendency for columnar structure with variation growth conditions. The buffer layers of YSZ and STO showed orientation. The tendency for columnar growth was observed above 15 mTorr sputtering gas pressure and at high substrate temperatures. Post annealing of these films in oxygen atmosphere reduced the oxygen deficiency and strain generated during growth of the films. Strong c-axis oriented superconducting YBa{sub 2}Cu{sub 9}O{sub 7-x} (YBCO) thin films were obtained on these buffer layers using pulsed laser ablation technique. YBCO films deposited on multilayers of YSZ and STO were shown to have better superconducting properties.

  17. Effect of performance of Zr-Y alloy target on thin film deposition technology

    International Nuclear Information System (INIS)

    Pan Qianfu; Liu Chaohong; Jiang Mingzhong; Yin Changgeng

    2011-01-01

    Yttria-stabilized zirconia (YSZ) films are synthesized on corrosion resistant plates by pulsed bias arc ion plating. The arc starting performance and the stability of thin film deposition is explored by improving the uniformity and compactibility of Zr-Y alloy target. The property of Zr-Y alloy target and depositional thin films were measured with the optical microscope, scanning electron microscope, X-ray diffractometer. The result shows that the target with hot rolling and annealing has a good arc starting performance and stability of thin film deposition, and the depositional thin films made of Yttria and amorphous zirconia are homogeneous and compact. (authors)

  18. Suspension chemistry and electrophoretic deposition of zirconia electrolyte on conducting and non-conducting substrates

    International Nuclear Information System (INIS)

    Das, Debasish; Basu, Rajendra N.

    2013-01-01

    Graphical abstract: - Highlights: • Stable suspension of yttria stabilized zirconia (YSZ) obtained in isopropanol medium. • Suspension chemistry and process parameters for electrophoretic deposition optimized. • Deposited film quality changed with iodine and water (dispersants) concentration. • Dense YSZ film (∼5 μm) fabricated onto non-conducting porous NiO-YSZ anode substrate. - Abstract: Suspensions of 8 mol% yttria stabilized zirconia (YSZ) particulates in isopropanol medium are prepared using acetylacetone, iodine and water as dispersants. The effect of dispersants concentration on suspension stability, particle size distribution, electrical conductivity and pH of the suspensions are studied in detail to optimize the suspension chemistry. Electrophoretic deposition (EPD) has been conducted to produce thin and dense YSZ electrolyte films. Deposition kinetics have been studied in depth and good quality films on conducting substrate are obtained at an applied voltage of 15 V for 3 min. YSZ films are also fabricated on non-conducting NiO-YSZ anode substrate using a steel plate on the reverse side of the substrate. Upon co-firing at 1400 °C for 6 h a dense YSZ film of thickness ∼5 μm is obtained. Such a half cell (anode + electrolyte) can be used to fabricate a solid oxide fuel cell on applying a suitable cathode layer

  19. Microstructure and thermal stability of Fe, Ti and Ag implanted Yttria-stabilized zirconia

    NARCIS (Netherlands)

    van Hassel, B.A.; van Hassel, B.A.; Burggraaf, Anthonie; Burggraaf, A.J.

    1991-01-01

    Yttria-stabilized zirconia (YSZ) was implanted with 15 keV Fe or Ti ions up to a dose of 8×1016 at cm−2. The resulting “dopant” concentrations exceeded the concentrations corresponding to the equilibrium solid solubility of Fe2O3 or TiO2 in YSZ. During oxidation in air at 400° C, the Fe and Ti

  20. Ceramics in engines - Long term stability of transformation toughened zirconia

    International Nuclear Information System (INIS)

    Marmach, M.; Swain, M.V.

    1985-01-01

    The long term thermal stability of two types of magnesia partially stabilized zirconia at temperatures below 1000 0 C has been determined. The effect on mechanical properties and phase stability of isothermal heating at 800 0 C and 900 0 C for up to 2000 hours, and with thermal cycling for a similar period between R.T. and 800 0 C in air, was measured. it was found that peak-aged (MS) type Mg-PSZ was much more stable than the thermal shock resistant (TS) type in both tests and showed minimal degradation

  1. Correlation between Thermal Treatment and Phase Transformation in Nanocrystalline Stabilized Zirconia

    Directory of Open Access Journals (Sweden)

    Tajudeen Oladele AHMED

    2013-06-01

    Full Text Available Stabilized zirconia produced via wet chemistry has chemically higher uniformity and purity. However, the grain size, particle shape, agglomerate size and specific surface area can be modified within certain degree by controlling the precipitation and sintering conditions. Generally, any physical or chemical difference between phases or effect occurring on the appearance or disappearance of a phase can be determined via thermal analysis and X-ray Diffractometry coupled with electron microscopy. In the last few decades, these materials have received tremendous attention globally in the field of defect solid-state devices. However, the challenge in this field of research has been to study thermal behaviour of these electrolytes during phase transformations and develop improved electrolytes with low activation temperature in the range of 600°C-800°C. In this paper, we report the wet chemistry of bismuth oxide stabilized zirconia having high experimental yield and low transformation temperature. Thus, the phase transformation from amorphous Zirconia to monoclinic is reported to begin above 600oC to an optimum temperature of 700oC. After calcination at 800oC for 4h, the powder have narrow particle size distribution in the range of 63-101µm. The average crystallite sizes of the synthesized powders range from 8-33nm.

  2. Color stability of CAD/CAM Zirconia ceramics following exposure to acidic and staining drinks.

    Science.gov (United States)

    Colombo, Marco; Cavallo, Marco; Miegge, Matteo; Dagna, Alberto; Beltrami, Riccardo; Chiesa, Marco; Poggio, Claudio

    2017-11-01

    The aim of this in vitro study was to evaluate the color stability of CAD/CAM Zirconia ceramics following exposure to acidic drink (Coca Cola) and after exposure to staining solution (coffee). All the samples were immersed in different staining solutions over a 28-day test period. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. Shapiro Wilk test and Kruskal-Wallis ANOVA were applied to assess significant differences among restorative materials. Paired t-test was applied to test which CIE L*a*b* parameters significantly changed after immersion in staining solutions. One week immersion in acidic drink did not cause a perceivable discoloration for all restorative materials (ΔE < 3.3). Subsequent immersion in coffee affected color stability of all Zirconia samples, even if Kruskal-Wallis ANOVA found significant differences among the various restorative materials. The ∆Es of CAD/CAM Zirconia ceramics after immersion in coffee varied among the products, but color integrity is not affected by contact with acidic drinks. Key words: CAD/CAM restorative materials, CIE Lab, Zirconia ceramics.

  3. Stability of zirconia sol in the presence of various inorganic electrolytes

    Directory of Open Access Journals (Sweden)

    Marković Jelena P.

    2013-01-01

    Full Text Available Zirconia sol was prepared from zirconium oxychloride solutions by forced hydrolysis at 102ºC. The prepared sol consisted of almost spherical, monoclinic, hydrated zirconia particles 61 nm in diameter. The stability of zirconia sol in the presence of various inorganic electrolytes (LiCl, NaCl, KCl, CsCl, KBr, KI, KNO3, and K2SO4 was studied by potentiometric titration method. Dependence of the critical concentration of coagulation (CCC on the dispersion pH was determined for all studied electrolytes. The critical coagulation concentration values, for all investigated electrolytes, are lower at higher pH. These values for all 1:1 electrolytes are equal in the range of experimental error. For a given pH value, CCCs of K2SO4 are 3-4 orders of magnitude lower than the corresponding values for 1:1 electrolytes. [Projekat Ministarstva nauke republike Srbije, br. III 45012

  4. Chemical vapor deposition of yttria stabilized zirconia in porous substrates

    International Nuclear Information System (INIS)

    Carolan, M.F.; Michaels, J.N.

    1987-01-01

    Electrochemical vapor deposition (EVD) of yttria stabilized zirconia (YSZ) is the preferred route to the production of thin films of YSZ on porous substrates. This process has been used in the construction of both fuel cells and steam electrolyzers. A critical aspect of the EVD process is an initial chemical vapor deposition phase in which the pores of a porous substrate are plugged by YSZ. In this process, water vapor and a mixture of gaseous zirconium chloride and yttrium chloride diffuse into the porous substrate from opposite sides and react to form YSZ and HCl ga. During the second stage of the process a continuous dense film of electrolyte is formed by a tarnishing-type process. Experimentally it is observed that the pores plug within a few pore diameters of the metal chloride face of the substrate. A kinetic rate expression that is first order in metal chloride but zero order in water is best able to explain this phenomenon. With this rate expression, the pores always plug near the metal chloride face. The model predicts less pore narrowing to occur as the ratio of the reaction rate to the diffusion rate of the metal chloride is increased. A kinetic rate expression that is first order in both water and metal chloride predicts that the pores plug much deeper in the substrate

  5. Investigation of phase stability in the scandia-zirconia; Investigacao da estabilidade de fases da zirconia-escandia

    Energy Technology Data Exchange (ETDEWEB)

    Grosso, Robson Lopes

    2016-11-01

    In this work, the phase stability of scandia-zirconia (ScSZ) system was investigated by the thermodynamic study of nanoparticles, within the range of 0 to 20 mol% Sc{sub 2}O{sub 3}, and by codoping of ZrO{sub 2}-10 mol% Sc{sub 2}O{sub 3} (10ScSZ) with Dy{sub 2}O{sub 3} and Nb{sub 2}O{sub 5}. The phase stability of ScSZ was evaluated based on thermodynamic data collected by water adsorption microcalorimetry and high temperature oxide melt solution. Nanostructured zirconia-scandia solid solutions were synthesized by coprecipitation method. Thermodynamic data were determined for ScSZ polymorph (monoclinic, tetragonal, cubic, rhombohedral β and γ) found by X-ray diffraction. This systemic work resulted in an unprecedented phase diagram at the nanoscale of particle size-composition. The effects of additives on 10ScSZ were investigated aiming to stabilize the cubic (c) structure at room temperature and to suppress the characteristic cubic-rhombohedral β phase transformation. Compositions were prepared by coprecipitation and solid state reaction. Materials were sintered by conventional and spark plasma sintering. Full stabilization of the cubic phase was attained by 1 mol% Dy{sub 2}O{sub 3} and 0.5 mol% Nb{sub 2}O{sub 5} additions. The smallest Nb{sub 2}O{sub 5} content required for cubic phase stabilization was attributed to liquid phase formation during sintering and to small ionic radius of Nb{sup 5+}. Results of high temperature X-ray diffraction and thermal analysis show suppression of the c-β transformation. Samples containing 0.5 mol% Nb{sub 2}O{sub 5} show total ionic conductivity similar to 10ScSZ without additives within a broad temperature range with high stability during 170 h at 600 °C. (author)

  6. Nature and strength of defect interactions in cubic stabilized zirconia

    International Nuclear Information System (INIS)

    Bogicevic, A.; Wolverton, C.

    2003-01-01

    The intrinsic ordering tendencies that limit ionic conduction in doped zirconia electrolytes are fully elucidated using first-principles calculations. A detailed analysis of nearly 300 yttria- and scandia-stabilized cubic-zirconia-ordered vacancy compounds reveals a delicate balance between competing elastic and electrostatic interactions. These results explain several outstanding experimental observations and provide substantial insight needed for improving ionic conduction and enabling low-temperature operation of zirconia-based electrolytes. We show that the surprising vacancy ordering in dilute solid solutions is a consequence of repulsive electrostatic and attractive elastic interactions that balance at third-neighbor vacancy separations. In contrast, repulsive elastic vacancy-dopant interactions prevail over electrostatic attraction at all probed defect separations in YSZ and lead to very weak ordering preferences in ScSZ. The total electronic contribution to the defect interactions is shown to be strongly dominated by simple point-charge electrostatics, leaving speciation of defect ordering for a given class of aliovalent dopants to the elastic term. Thus, ion size becomes a critical parameter in controlling the ionic conductivity of doped oxide electrolytes

  7. Surface modification of yttria stabilized zirconia via polydopamine inspired coating for hydroxyapatite biomineralization

    Energy Technology Data Exchange (ETDEWEB)

    Zain, Norhidayu Muhamad [Medical Devices and Technology Group, Faculty of Biosciences and Medical Engineering, Universiti Teknologi Malaysia, 81310 UTM Johor Bahru, Johor (Malaysia); Hussain, Rafaqat [Ibnu Sina Institute for Fundamental Science Studies, Universiti Teknologi Malaysia, 81310 UTM Johor Bahru, Johor (Malaysia); Kadir, Mohammed Rafiq Abdul, E-mail: rafiq@biomedical.utm.my [Medical Devices and Technology Group, Faculty of Biosciences and Medical Engineering, Universiti Teknologi Malaysia, 81310 UTM Johor Bahru, Johor (Malaysia)

    2014-12-15

    Highlights: • Synthesis of functionalized yttria stabilized zirconia using polydopamine. • Improved hydrophilicity of the grafted samples with low contact angle of 44.0 ± 2.3. • Apatite layer with Ca/P ratio of 1.78 formed on the surface of the grafted samples. • Atomic percentage of Ca 2p increased by 2-fold at coating temperature of 37 °C. - Abstract: Yttria stabilized zirconia (YSZ) has been widely used as biomedical implant due to its high strength and enhanced toughening characteristics. However, YSZ is a bioinert material which constrains the formation of chemical bonds with bone tissue following implantation. Inspired by the property of mussels, the surface of YSZ ceramics was functionalized by quinone-rich polydopamine to facilitate the biomineralization of hydroxyapatite. YSZ discs were first immersed in 2 mg/mL of stirred or unstirred dopamine solution at either 25 or 37 °C. The samples were then incubated in 1.5 simulated body fluid (SBF) for 7d. The effect of coating temperature for stirred and unstirred dopamine solutions during substrate grafting was investigated on the basis of chemical compositions, wettability and biomineralization of hydroxyapatite on the YSZ functionalized surface. The results revealed that the YSZ substrate grafted at 37 °C in stirred solution of dopamine possessed significantly improved hydrophilicity (water contact angle of 44.0 ± 2.3) and apatite-mineralization ability (apatite ratio of 1.78). In summary, the coating temperature and stirring condition during grafting procedure affected the chemical compositions of the films and thus influenced the formation of apatite layer on the substrate during the biomineralization process.

  8. Surface modification of yttria stabilized zirconia via polydopamine inspired coating for hydroxyapatite biomineralization

    International Nuclear Information System (INIS)

    Zain, Norhidayu Muhamad; Hussain, Rafaqat; Kadir, Mohammed Rafiq Abdul

    2014-01-01

    Highlights: • Synthesis of functionalized yttria stabilized zirconia using polydopamine. • Improved hydrophilicity of the grafted samples with low contact angle of 44.0 ± 2.3. • Apatite layer with Ca/P ratio of 1.78 formed on the surface of the grafted samples. • Atomic percentage of Ca 2p increased by 2-fold at coating temperature of 37 °C. - Abstract: Yttria stabilized zirconia (YSZ) has been widely used as biomedical implant due to its high strength and enhanced toughening characteristics. However, YSZ is a bioinert material which constrains the formation of chemical bonds with bone tissue following implantation. Inspired by the property of mussels, the surface of YSZ ceramics was functionalized by quinone-rich polydopamine to facilitate the biomineralization of hydroxyapatite. YSZ discs were first immersed in 2 mg/mL of stirred or unstirred dopamine solution at either 25 or 37 °C. The samples were then incubated in 1.5 simulated body fluid (SBF) for 7d. The effect of coating temperature for stirred and unstirred dopamine solutions during substrate grafting was investigated on the basis of chemical compositions, wettability and biomineralization of hydroxyapatite on the YSZ functionalized surface. The results revealed that the YSZ substrate grafted at 37 °C in stirred solution of dopamine possessed significantly improved hydrophilicity (water contact angle of 44.0 ± 2.3) and apatite-mineralization ability (apatite ratio of 1.78). In summary, the coating temperature and stirring condition during grafting procedure affected the chemical compositions of the films and thus influenced the formation of apatite layer on the substrate during the biomineralization process

  9. Color stability of CAD/CAM Zirconia ceramics following exposure to acidic and staining drinks

    Science.gov (United States)

    Colombo, Marco; Cavallo, Marco; Miegge, Matteo; Dagna, Alberto; Beltrami, Riccardo; Chiesa, Marco

    2017-01-01

    Background The aim of this in vitro study was to evaluate the color stability of CAD/CAM Zirconia ceramics following exposure to acidic drink (Coca Cola) and after exposure to staining solution (coffee). Material and Methods All the samples were immersed in different staining solutions over a 28-day test period. A colorimetric evaluation according to the CIE L*a*b* system was performed by a blind trained operator at 7, 14, 21, 28 days of the staining process. Shapiro Wilk test and Kruskal-Wallis ANOVA were applied to assess significant differences among restorative materials. Paired t-test was applied to test which CIE L*a*b* parameters significantly changed after immersion in staining solutions. Results One week immersion in acidic drink did not cause a perceivable discoloration for all restorative materials (ΔE < 3.3). Subsequent immersion in coffee affected color stability of all Zirconia samples, even if Kruskal-Wallis ANOVA found significant differences among the various restorative materials. Conclusions The ∆Es of CAD/CAM Zirconia ceramics after immersion in coffee varied among the products, but color integrity is not affected by contact with acidic drinks. Key words:CAD/CAM restorative materials, CIE Lab, Zirconia ceramics. PMID:29302281

  10. Influence of nature of the substrate in the deposition of yttria-stabilized zirconia by spray pyrolysis

    International Nuclear Information System (INIS)

    Halmenschlager, C.M.; Malfatti, C.F.; Bergmann, C.P.; Neagu, R.

    2012-01-01

    Spray pyrolysis technique consist in spraying a precursor solution on a heated substrate. In the last few decades this process has attracted much attention because of its versatility. Controlling the parameters is possible to produce dense or porous film. Spray pyrolysis has been applied to obtain several materials such as electrodes or electrolytes for SOFC, semiconductors, materials for solar cells and so on. However, some behaviors such as Leidenfrost effect have been poorly considered and it may affect the coating quality. This work aims to evaluate the influence of the substrate and how Leidenfrost effect affects the coating by spray pyrolysis. To achieve this goal yttria-stabilized zirconia solutions made with different solvents were deposited on different substrates at different temperatures. These coatings were characterized by X-ray diffraction and scanning electron microscopy. The results show that there is a limit temperature which is related to properties of the solvent and the surface of the substrates where films are continuous. (author)

  11. Epitaxial growth of In-rich InGaN on yttria-stabilized zirconia and its application to metal–insulator–semiconductor field-effect transistors

    Energy Technology Data Exchange (ETDEWEB)

    Kobayashi, Atsushi; Lye, Khe Shin; Ueno, Kohei [Institute of Industrial Science, The University of Tokyo, Tokyo 153-8505 (Japan); Ohta, Jitsuo [Institute of Industrial Science, The University of Tokyo, Tokyo 153-8505 (Japan); PRESTO, Japan Science and Technology Agency, Saitama 332-0012 (Japan); Fujioka, Hiroshi, E-mail: hfujioka@iis.u-tokyo.ac.jp [Institute of Industrial Science, The University of Tokyo, Tokyo 153-8505 (Japan); ACCEL, Japan Science and Technology Agency, Tokyo 102-0076 (Japan)

    2016-08-28

    We grew In-rich In{sub x}Ga{sub 1-x}N films on yttria-stabilized zirconia (YSZ) substrates at low temperatures by pulsed sputtering deposition. It was found that single-crystal In{sub x}Ga{sub 1-x}N (0.63 ≤ x ≤ 0.82) films can be prepared without significant compositional fluctuations at growth temperatures below 500 °C. It was also found that the electrical properties of InGaN are strongly dependent on In composition, growth temperature, and film polarity. N-channel operation of the metal–insulator–semiconductor field-effect transistor (MISFET) with an ultrathin InGaN channel on the YSZ substrates was successfully demonstrated. These results indicate that an InGaN-based MISFET is a promising device for next-generation high-speed electronics.

  12. Yttria-stabilized zirconia as membrane material for electrolytic deoxidation of CaO-CaCl{sub 2} melts

    Energy Technology Data Exchange (ETDEWEB)

    Martin, A.; Poignet, J. C.; Fouletier, J. [Univ Grenoble, LEPMI, CNRS, INPG, UJF, F-38402 St Martin Dheres (France); Allibert, M. [LPSC, F-38026 Grenoble 1 (France); Lambertin, D. [SPDE, CEA Marcoule, F-30207 Bagnols Sur Ceze (France); Bourges, G. [SRPU, CEA Valduc, F-21120 Is Sur Tille (France)

    2010-07-01

    This article is devoted to the study of the stability of an yttria-stabilized zirconia membrane used in the electrolysis of molten CaCl{sub 2}-CaO mixtures at 850 degrees C. Intentiostatic and potentiostatic electrolysis were carried for periods ranging from 10 to 20 h. Post-mortem composition profiles across the zirconia membrane were determined using Raman spectroscopy and microprobe analysis. The membrane degradation was analyzed in terms of synergetic parameters, i. e., chemical, electrochemical, and thermomechanical effects. (authors)

  13. Precipitation in partially stabilized zirconia

    International Nuclear Information System (INIS)

    Bansal, G.K.

    1975-01-01

    Transmission electron microscopy was used to study the substructure of partially stabilized ZrO 2 (PSZ) samples, i.e., 2-phase systems containing both cubic and monoclinic modifications of zirconia, after various heat treatments. Monoclinic ZrO 2 exists as (1) isolated grains within the polycrystalline aggregate (a grain- boundary phase) and (2) small plate-like particles within cubic grains. These intragranular precipitates are believed to contribute to the useful properties of PSZ via a form of precipitation hardening. These precipitates initially form as tetragonal ZrO 2 , with a habit plane parallel to the brace 100 brace matrix planes. The orientation relations between the tetragonal precipitates and the cubic matrix are brace 100 brace/sub matrix/ 2 parallel brace 100 brace /sub precipitate/ or (001)/sub precipitate/ and broken bracket 100 broken bracket/sub matrix/ 2 parallel broken bracket 100 broken bracket/sub precipitate/ or [001]/sub precipitate/. (U.S.)

  14. Initial Bacterial Adhesion on Different Yttria-Stabilized Tetragonal Zirconia Implant Surfaces in Vitro

    Directory of Open Access Journals (Sweden)

    Lamprini Karygianni

    2013-12-01

    Full Text Available Bacterial adhesion to implant biomaterials constitutes a virulence factor leading to biofilm formation, infection and treatment failure. The aim of this study was to examine the initial bacterial adhesion on different implant materials in vitro. Four implant biomaterials were incubated with Enterococcus faecalis, Staphylococcus aureus and Candida albicans for 2 h: 3 mol % yttria-stabilized tetragonal zirconia polycrystal surface (B1a, B1a with zirconium oxide (ZrO2 coating (B2a, B1a with zirconia-based composite coating (B1b and B1a with zirconia-based composite and ZrO2 coatings (B2b. Bovine enamel slabs (BES served as control. The adherent microorganisms were quantified and visualized using scanning electron microscopy (SEM; DAPI and live/dead staining. The lowest bacterial count of E. faecalis was detected on BES and the highest on B1a. The fewest vital C. albicans strains (42.22% were detected on B2a surfaces, while most E. faecalis and S. aureus strains (approximately 80% were vital overall. Compared to BES; coated and uncoated zirconia substrata exhibited no anti-adhesive properties. Further improvement of the material surface characteristics is essential.

  15. Effect of dysprosia doping on structural and electrical property of stabilized zirconia for intermediate- temperature SOFCs

    International Nuclear Information System (INIS)

    Pastor, M.; Maiti, S.; Pandey, A.; Biswas, K.; Manna, I.

    2011-01-01

    Present work deals with structural, micro-structural and electrical properties of dysprosia stabilized zirconia electrolyte, which have been evaluated by means of X-ray diffraction (XRD) and scanning (SEM), and complex impedance analysis respectively. The amount of dysprosia was varied from 2 to 12 mol% in zirconia. The addition of dysprosia (8-12 mol%) stabilized the cubic zirconia phase, which was analyzed from XRD analysis. SEM micrographs clearly showed the improvement in sinterability with increase in dysprosia concentration up to 6 mol% disprosia. Complex impedance analysis was performed in the temperature range from 250 to 600 deg. C. The results indicated a gradual decrease in impedance of both bulk and grain boundary and increase in conductivity with dysprosia doping up to 6 mol% and thereafter showing a reverse trend. The activation energies for oxygen ion migration were also found to decrease with increase in dysprosia doping which was in the range of 0.99 - 1.28 eV. The average thermal expansion coefficient increases linearly.

  16. Thermal stability and phase transformation in fully indium oxide (InO{sub 1.5}) stabilized zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Piva, R.H., E-mail: honorato.piva@ua.pt; Piva, D.H.; Morelli, M.R.

    2017-01-15

    Indium oxide (InO{sub 1.5}) stabilized zirconia (InSZ) is an attractive material as electrolyte, or electrode, in solid oxide fuel cells (SOFCs), and as corrosion resistant top coat in thermal barrier coatings. However, little is known about the phase stability of cubic InSZ at temperatures that simulate the conditions in an operating SOFC or turbine. This article provides an investigation of the phase stability and phase transformations in cubic InSZ after heat treatments at 800, 1000, and 1200 °C for periods up to 2000 h. The results revealed that cubic InSZ is not stable during annealing at 1000 and 1200 °C, owing to a fast destabilization of the initial cubic phase to tetragonal, and eventually to monoclinic (c → t → m). The c → t → m transition in InSZ is intimately associated with the indium volatilization. On the other hand, cubic InSZ remained stable for 2000 h at 800 °C, although the partial formation of the tetragonal phase was observed along with a 0.25% contraction in the unit cell volume of the cubic phase, caused by short-range ordering. These results demonstrate that technological applications of cubic InSZ are restricted to temperatures at which the volatilization of the InO{sub 1.5} stabilizer does not occur. - Highlights: •Phase stability of fully InO{sub 1.5} stabilized zirconia (cubic InSZ) was evaluated. •Cubic InSZ is instable at temperatures ≥ 1000 °C, owing to the cubic-to-tetragonal-to-monoclinic destabilization. •Cubic InSZ undergoes the cubic-to-tetragonal transformation at ~ 800 °C. •Owing to the low phase stability, applications of cubic InSZ in TBCs or SOFCs are restricted.

  17. Implant stability and marginal bone level of microgrooved zirconia dental implants: A 3-month experimental study on dogs

    Directory of Open Access Journals (Sweden)

    Delgado-Ruíz Rafael Arcesio

    2014-01-01

    Full Text Available Background/Aim. The modification of implant surfaces could affect mechanical implant stability as well as dynamics and quality of peri-implant bone healing. The aim of this 3-month experimental study in dogs was to investigate implant stability, marginal bone levels and bone tissue response to zirconia dental implants with two laser-micro-grooved intraosseous surfaces in comparison with nongrooved sandblasted zirconia and sandblasted, high-temperature etched titanium implants. Methods. Implant surface characterization was performed using optical interferometric profilometry and energy dispersive X-ray spectroscopy. A total of 96 implants (4 mm in diameter and 10 mm in length were inserted randomly in both sides of the lower jaw of 12 Fox Hound dogs divided into groups of 24 each: the control (titanium, the group A (sandblasted zirconia, the group B (sandblasted zirconia plus microgrooved neck and the group C (sandblasted zirconia plus all microgrooved. All the implants were immediately loaded. Insertion torque, periotest values, radiographic crestal bone level and removal torque were recorded during the 3-month follow-up. Qualitative scanning electon micro-scope (SEM analysis of the bone-implant interfaces of each group was performed. Results. Insertion torque values were higher in the group C and control implants (p the control > the group B > the group A (p the control > the group B > the group A (p < 0.05. SEM showed that implant surfaces of the groups B and C had an extra bone growth inside the microgrooves that corresponded to the shape and direction of the microgrooves. Conclusion. The addition of micro-grooves to the entire intraosseous surface of zirconia dental implants enhances primary and secondary implant stability, promotes bone tissue ingrowth and preserves crestal bone levels.

  18. Zirconia thin films from aqueous precursors: Processing, microstructural development, and epitaxial growth

    International Nuclear Information System (INIS)

    Miller, K.T.

    1991-01-01

    Thin films of ZrO 2 (Y 2 O 3 ) were prepared from aqueous salt precursors by spin coating. Films were pyrolyzed to produce porous polycrystalline thin films of 5-10 nm grain size. Subsequent microstructural development depends greatly upon the nature of the substrate. Upon randomly oriented sapphire, the films initially sintered to full density; further heat treatment and grain growth causes these films to break into interconnected islands and finally isolated particles. Thermodynamic calculations predict that breakup is energetically favorable when the grain-size film-thickness ratio exceeds a critical value. Upon basal-plane-oriented sapphire, grain growth and breakup prefer the (100) oriented grains, presumably because this orientation is a special interface of low energy. The isolated, oriented grains produced by film breakup act as seeds for the growth of newly deposited material. Upon (100) cubic zirconia, true epitaxial films develop. Epitaxial growth was observed for lattice mismatches up to 1.59%. Growth proceeds from a fine epitaxial layer which is produced during the initial stages of heat treatment, consuming the porous polycrystalline material and producing a dense epitaxial thin film whose misfit is accommodated by a combination of film strain and misfit dislocations

  19. Surface degradation of nanocrystalline zirconia dental implants

    NARCIS (Netherlands)

    Ocelík, Václav; Schepke, Ulf; Rasoul, Hamid Haji; Cune, Marco S.; De Hosson, Jeff Th M.

    2017-01-01

    Yttria-stabilized zirconia prepared by hot isostatic pressing represents attractive material for biomedical applications. In this work the degradation of yttria-stabilized zirconia dental implants abutments due to the tetragonal to monoclinic phase transformation after one year of clinical use was

  20. Tetragonal zirconia quantum dots in silica matrix prepared by a modified sol-gel protocol

    Science.gov (United States)

    Verma, Surbhi; Rani, Saruchi; Kumar, Sushil

    2018-05-01

    Tetragonal zirconia quantum dots (t-ZrO2 QDs) in silica matrix with different compositions ( x)ZrO2-(100 - x)SiO2 were fabricated by a modified sol-gel protocol. Acetylacetone was added as a chelating agent to zirconium propoxide to avoid precipitation. The powders as well as thin films were given thermal treatment at 650, 875 and 1100 °C for 4 h. The silica matrix remained amorphous after thermal treatment and acted as an inert support for zirconia quantum dots. The tetragonal zirconia embedded in silica matrix transformed into monoclinic form due to thermal treatment ≥ 1100 °C. The stability of tetragonal phase of zirconia is found to enhance with increase in silica content. A homogenous dispersion of t-ZrO2 QDs in silica matrix was indicated by the mapping of Zr, Si and O elements obtained from scanning electron microscope with energy dispersive X-ray analyser. The transmission electron images confirmed the formation of tetragonal zirconia quantum dots embedded in silica. The optical band gap of zirconia QDs (3.65-5.58 eV) was found to increase with increase in zirconia content in silica. The red shift of PL emission has been exhibited with increase in zirconia content in silica.

  1. Yttria-Ceria stabilized tetragonal zirconia polycrystals: Sintering, grain growth and grain boundary segregation

    NARCIS (Netherlands)

    Boutz, M.M.R.; Boutz, M.M.R.; Winnubst, Aloysius J.A.; Burggraaf, Anthonie; Burggraaf, A.J.

    1994-01-01

    An analysis is presented of grain growth and densification of yttria-ceria stabilized tetragonal zirconia polycrystals (Y, Ce-TZPs) using both isothermal and non-isothermal techniques. The characteristics of Y, Ce-TZPs are compared to those of Y-TZP and Ce-TZP and the effect of increasing ceria

  2. Role of yttria-stabilized zirconia produced by ion-beam-assisted deposition on the properties of RuO2 on SiO2/Si

    International Nuclear Information System (INIS)

    Jia, Q.X.; Arendt, P.; Groves, J.R.; Fan, Y.; Roper, J.M.; Foltyn, S.R.

    1998-01-01

    Highly conductive biaxially textured RuO 2 thin films were deposited on technically important SiO 2 /Si substrates by pulsed laser deposition, where yttria-stabilized zirconia (YSZ) produced by ion-beam-assisted-deposition (IBAD) was used as a template to enhance the biaxial texture of RuO 2 on SiO 2 /Si. The biaxially oriented RuO 2 had a room-temperature resistivity of 37 μΩ-cm and residual resistivity ratio above 2. We then deposited Ba 0.5 Sr 0.5 TiO 3 thin films on RuO 2 /IBAD-YSZ/SiO 2 /Si. The Ba 0.5 Sr 0.5 TiO 3 had a pure (111) orientation normal to the substrate surface and a dielectric constant above 360 at 100 kHz. copyright 1998 Materials Research Society

  3. Electrophoretic deposition of thin film zirconia electrolyte on non-conducting NiO-YSZ substrate

    International Nuclear Information System (INIS)

    Das, Debasish; Basu, Rajendra N.

    2014-01-01

    Eight (8) mol% yttria stabilized zirconia (YSZ), an electrolyte material for solid oxide fuel cell (SOFC), has been deposited onto porous non-conducting NiO-YSZ substrate using electrophoretic deposition technique (EPD) from a stable non-aqueous suspension of YSZ. Normally, EPD cannot be performed on a non-conducting substrate, but, in this present study, YSZ particulate film has been successfully deposited on a non-conducting NiO-YSZ substrate following two different EPD approaches:(a) using a conducting metallic plate on the reverse side of the porous NiO-YSZ anode substrate and (b) using a conducting polymer coated NiO-YSZ substrate. The deposited films are then formed dense coatings of 5-15 μm after sintering at 1400℃ for 6 h in air. Surface and cross-sectional morphologies of green and sintered films deposited by different EPD approaches are investigated using SEM. La 0.65 Sr 0.3 MnO 3 (LSM), a cathode for SOFC, is then screen-printed onto the electrolyte layer of such sintered half cells (anode+electrolyte) prepared by both the above approaches to construct SOFC single cells. A maximum output power density of 0.37 W.cm -2 is obtained using single cells prepared by conducting metallic plate assisted EPD compared to that of 0.73 W.cm -2 for polymer coated at 800℃ using H 2 as fuel and O 2 as oxidant. (author)

  4. Phase characterization of precipitated zirconia

    International Nuclear Information System (INIS)

    Gutzov, S.; Ponahlo, J.; Lengauer, C.L.; Beran, A.

    1994-01-01

    The phase compositions of undoped and europium-doped zirconia samples, obtained by precipitation and thermal treatment from 350 to 1,000 C, have been investigated by powder X-ray diffractometry, infrared spectroscopy, and cathodoluminescence spectroscopy. The low-temperature stabilization of tetragonal zirconia is mainly controlled by the presence of anion additives, such as ammonium chloride. The influences of the crystallite size is less important. Cathodoluminescence spectra show a structural similarity between tetragonal and amorphous zirconia

  5. Atomic structure and composition of the yttria-stabilized zirconia (111) surface.

    Science.gov (United States)

    Vonk, Vedran; Khorshidi, Navid; Stierle, Andreas; Dosch, Helmut

    2013-06-01

    Anomalous and nonanomalous surface X-ray diffraction is used to investigate the atomic structure and composition of the yttria-stabilized zirconia (YSZ)(111) surface. By simulation it is shown that the method is sensitive to Y surface segregation, but that the data must contain high enough Fourier components in order to distinguish between different models describing Y/Zr disorder. Data were collected at room temperature after two different annealing procedures. First by applying oxidative conditions at 10 - 5  mbar O 2 and 700 K to the as-received samples, where we find that about 30% of the surface is covered by oxide islands, which are depleted in Y as compared with the bulk. After annealing in ultrahigh vacuum at 1270 K the island morphology of the surface remains unchanged but the islands and the first near surface layer get significantly enriched in Y. Furthermore, the observation of Zr and oxygen vacancies implies the formation of a porous surface region. Our findings have important implications for the use of YSZ as solid oxide fuel cell electrode material where yttrium atoms and zirconium vacancies can act as reactive centers, as well as for the use of YSZ as substrate material for thin film and nanoparticle growth where defects control the nucleation process.

  6. Effect of crystal structure on optical properties of sol–gel derived zirconia thin films

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Xiaodong, E-mail: xiaodong_wang@tongji.edu.cn [Pohl Institute of Solid State Physics, Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology, Tongji University, Shanghai 200092 (China); Wu, Guangming; Zhou, Bin [Pohl Institute of Solid State Physics, Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology, Tongji University, Shanghai 200092 (China); Shen, Jun, E-mail: shenjun67@tongji.edu.cn [Pohl Institute of Solid State Physics, Shanghai Key Laboratory of Special Artificial Microstructure Materials and Technology, Tongji University, Shanghai 200092 (China)

    2013-04-15

    Highlights: ► ZrO{sub 2} films were deposited by sol–gel method. ► Crystal structures of the films were tuned by different thermal annealing methods. ► The refractive indices vary with the crystal structures of the films. ► Lattice-mismatch was found to reduce the refractive index of ZrO{sub 2} films. -- Abstract: The optical properties of sol–gel derived zirconia thin films and their relation to the crystal structure are studied in this paper. ZrO{sub 2} films were deposited on quartz glass and silicon wafer substrates by sol–gel method with conventional furnace annealing (CFA) and rapid thermal annealing (RTA). Crystal structures of the films were analyzed by X-ray diffraction (XRD) and Raman spectroscopy, while refractive indices of the films were determined from the reflectance and transmittance spectra. The refractive indices vary with the function of crystal structure and density of the films, which depends on annealing temperature and annealing technique. Lattice-mismatch between monoclinic phase and tetragonal phase was found to reduce the refractive index of ZrO{sub 2} films.

  7. Mesoporous yttria-zirconia and metal-yttria-zirconia solid solutions for fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Mamak, M.; Coombs, N.; Ozin, G. [Toronto Univ., ON (Canada). Dept. of Chemistry

    2000-02-03

    A new class of binary mesoporous yttria-zirconia (YZ) and ternary mesoporous metal-YZ materials (M = electroactive Ni/Pt) is presented here that displays the highest surface area of any known form of yttria-stabilized zirconia. These mesoporous materials form as solid solutions and retain their structural integrity to 800 C, which bodes well for their possible utilization in fuel cells. (orig.)

  8. Leveling and thixotropic characteristics of concentrated zirconia inks for screen-printing

    DEFF Research Database (Denmark)

    Phair, John; Lundberg, Mats; Kaiser, Andreas

    2009-01-01

    of ethyl cellulose (binder) content upon the thixotropic and leveling characteristics of zirconia inks. While the yield stress (τ 0), extent of recovery R(%), and rate of recovery (K) increase with increasing binder content, so did the surface roughness and thickness of the screen-printed films. Increasing...... the binder content not only increases the network strength of the thick films but also leads to increased leveling time. As a result, rheological modifiers are proposed to be necessary to improve the leveling characteristics of zirconia inks without losing the green strength of the thick films......Screen-printing is a cost-effective method for the mass manufacture of zirconia-based solid oxide fuel cells (SOFCs) and oxygen separation membranes. The present work outlines an investigation into the leveling, thixotropic, and screen-printing characteristics of concentrated zirconia inks...

  9. Stability of cubic zirconia in a granitic system under high pressure and temperature

    International Nuclear Information System (INIS)

    Gibb, F. G. F.; Burakov, B. E.; Taylor, K. J.; Domracheva, Y.

    2008-01-01

    Cubic zirconia is a well known, highly durable material with potential uses as an actinide host phase in ceramic waste forms and inert matrix fuels and in containers for very deep borehole disposal of some highly radioactive wastes. To investigate the behaviour of this material under the conditions of possible use, a cube of ∼2.5 mm edge was made from a single crystal of Yttria stabilized cubic zirconia doped with 0.3 wt.% CeO 2 . The cube was enclosed in powdered granite within a gold capsule and a small amount of H 2 O added before sealing. The sealed capsule was held for 4 months in a cold-seal pressure vessel at a temperature of 780 deg. C and a pressure 150 MPa, simulating both the conditions of a deep borehole disposal involving partial melting of the host rock and the conditions under which the actinide waste form might be encapsulated in granite prior to disposal. At the end of the experiment the quenched, largely glassy, sample was cut into thin slices and studied by optical microscopy, EMPA, SEM and cathodoluminescence methods. The results show that no corrosion of the zirconia crystal or reaction with the granite melt occurred and that no detectable diffusion of elements, including Ce, in or out of the zirconia took place on the timescale of the experiment. Consequently, it appears that cubic zirconia could perform most satisfactorily as both an actinide host waste form for encapsulation in solid granite for very deep disposal and as a container material for deep borehole disposal of highly radioactive wastes (HLW), including spent fuel. (authors)

  10. Dilemmas in zirconia bonding: A review

    Directory of Open Access Journals (Sweden)

    Obradović-Đuričić Kosovka

    2013-01-01

    Full Text Available This article presents a literature review on the resin bond to zirconia ceramic. Modern esthetic dentistry has highly recognized zirconia, among other ceramic materials. Biocompatibility of zirconia, chemical and dimensional stability, excellent mechanical properties, all together could guarantee optimal therapeutical results in complex prosthodontic reconstruction. On the other hand, low thermal degradation, aging of zirconia as well as problematic bonding of zirconia framework to dental luting cements and tooth structures, opened the room for discussion concerning their clinical durability. The well known methods of mechanical and chemical bonding used on glass-ceramics are not applicable for use with zirconia. Therefore, under critical clinical situations, selection of the bonding mechanism should be focused on two important points: high initial bond strength value and long term bond strength between zirconia-resin interface. Also, this paper emphases the use of phosphate monomer luting cements on freshly air-abraded zirconia as the simplest and most effective way for zirconia cementation procedure today.

  11. Sintering of a freeze-dried 10 mol% Y2O3-stabilized zirconia

    International Nuclear Information System (INIS)

    Rakotoson, A.; Paulus, M.

    1983-01-01

    After presenting the results of freeze drying a sulfate solution, the authors describe a preparation process in which the freeze-drying technique by addition of a suspension of stabilized zirconia in the liquid solution before freeze-drying. This process breaks the polymeric chains, increases the green density of the compact, and decreases the sintering temperature. The mechanisms involved are discussed

  12. Reaction scheme of partial oxidation of methane to synthesis gas over yttrium-stabilized zirconia

    NARCIS (Netherlands)

    Zhu, J.J.; van Ommen, J.G.; Lefferts, Leonardus

    2004-01-01

    The partial oxidation of methane to synthesis gas over yttrium-stabilized zirconia (YSZ) was studied with in situ FTIR and both steady-state and transient experiments. The four major products, CO, H2, CO2, and H2O, are primary products of CPOM over YSZ. Besides these major products and traces of

  13. In situ ion-beam analysis and modification of sol-gel zirconia thin films

    International Nuclear Information System (INIS)

    Levine, T.E.; Mayer, J.W.

    1995-01-01

    We report the investigation of ion-beam-induced densification of sol-gel zirconia thin films via in situ ion backscattering spectrometry. We have irradiated three regions of a sample with neon, argon, and krypton ions. For each ion species, a series of irradiation and analysis steps were performed using an interconnected 3 MV tandem accelerator. The technique offers the advantages of minimizing the variation of experimental parameters and sequentially monitoring the densification phenomenon with increasing ion dose

  14. Evolution of the nickel/zirconia interface

    International Nuclear Information System (INIS)

    Shinde, S.L.; Olson, D.A.; De Jonghe, L.C.; Miller, R.A.

    1986-01-01

    The changes taking place at the nickel zirconia interface during oxidation in air at 900 0 C were studied using analytical electron microscopy (AEM). The nickel oxide layer growing at the interface and the stabilizers used in zirconia interact, giving different interface morphologies

  15. HIGHLY REFRACTORY CRUCIBLES OF STABILIZED ZIRCONIA FOR INDUCTION MELTING OF THE PLATINUM GROUP METALS, FABRICATED BY VIBROCASTING

    OpenAIRE

    V. V. Primachenko; V. V. Martynenko; I. G. Szulik; I. A. Kushchenko

    2012-01-01

    As the result of the studies at PJSC « UKRNIIO them. A.S.Berezhnogo» the technology and commercial production of crucibles from stabilized zirconia for the smelting of platinum group metals are develop

  16. Enhanced ionic transport in fine-grained scandia-stabilized zirconia ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Abdala, Paula M.; Lamas, Diego G. [CINSO (Centro de Investigaciones en Solidos), CONICET-CITEFA, J.B. de La Salle 4397 (B1603ALO) Villa Martelli, Pcia. de Buenos Aires (Argentina); Custo, Graciela S. [Gerencia de Area Seguridad Nuclear y Ambiente, Gerencia Quimica, Departamento Quimica Analitica, Centro Atomico Constituyentes, Comision Nacional de Energia Atomica, Av. Constituyentes 1499 (B1650KNA) San Martin, Pcia. de Buenos Aires (Argentina)

    2010-06-01

    In this work, the transport properties of fine-grained scandia-stabilized zirconia ceramics with low Si content have been investigated. These materials were prepared from ZrO{sub 2}-6 mol% Sc{sub 2}O{sub 3} nanopowders synthesized by a nitrate-lysine gel-combustion route. High relative densities and excellent electrical properties were obtained, even for sintering temperatures as low as 1350 C. Our electrochemical impedance spectroscopy study showed that both the volume fraction of grain boundaries and the specific grain-boundary conductivity are significantly enhanced with decreasing grain size, resulting in a higher total ionic conductivity. (author)

  17. Structure and mechanical properties of silica doped zirconia thin films

    Energy Technology Data Exchange (ETDEWEB)

    Uhlmann, Ina, E-mail: uhlmann@ceramics.tu-darmstadt.de [Institute of Materials Science, Technische Universität Darmstadt, 64287 Darmstadt (Germany); Hawelka, Dominik [Fraunhofer Institute for Laser Technology ILT, 52074 Aachen (Germany); Hildebrandt, Erwin [Institute of Materials Science, Technische Universität Darmstadt, 64287 Darmstadt (Germany); Pradella, Jens [Merck KGaA Darmstadt, 64293 Darmstadt (Germany); Rödel, Jürgen [Institute of Materials Science, Technische Universität Darmstadt, 64287 Darmstadt (Germany)

    2013-01-01

    Sol–gel based wear resistant coatings are presented as an alternative to existing vapor deposition coatings. The films consist of zirconia which has been doped with 8 wt.% silica. Crack-free single as well as multilayer coatings with thicknesses of 80 and 150 nm, respectively, could be produced after sintering at 1000 °C. The evolution of layer thickness, optical, chemical and mechanical properties during film annealing was investigated by ellipsometry, scanning electron microscopy, thermal gravimetric analysis, Fourier transform infrared spectroscopy, X-ray diffraction, nanoindentation and micro-abrasion. Micro-abrasion has been established as an easy and powerful tool to achieve first comparative abrasion data which could be correlated to hardness, Young's modulus and structure of the films. Above 600 °C a tetragonal, oxide coating with a Young's modulus ranging from 80 to 90 GPa, a hardness from 7 to 8 GPa and an increased abrasion resistance was obtained. The film density reached 4.64 g/cm{sup 3} with the mean refractive index n{sub 550} {sub nm} lying between 1.88 and 1.93. - Highlights: ► Sol–gel zirconia–8 wt.% silica coatings with hardness up to 8 GPa achieved ► Layer thickness as compared by ellipsometry and scanning electron microscopy ► Crack-free multilayer coatings produced up to 150 nm.

  18. Influence of additives on phase stabilization of scandia-doped zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Muccillo, Eliana Navarro dos Santos; Grosso, Robson Lopes; Reis, Shirley Leite dos; Muccillo, Reginaldo, E-mail: enavarro@usp.br, E-mail: roblopeg@usp.br, E-mail: shirley.reis@usp.br, E-mail: muccillo@usp.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2017-04-15

    The effects of small additions of tin, zinc, calcium and boron oxides on phase composition and electrical conductivity of zirconia-10 mol% scandia were investigated. Compounds containing 1 mol% zinc, tin and calcium oxides and 1, 3 and 5 wt.% boron oxide were prepared by solid state reaction and characterized by X-ray diffraction, density measurements, scanning electron microscopy and impedance spectroscopy. Full stabilization of the cubic structure at room temperature was obtained with additions of 1 mol% calcium oxide and 2 wt.% boron oxide. Partially stabilized compounds exhibit herringbone structure, characteristic of the β- rhombohedric phase. Specimens with calcium as additive show total conductivity of 23.8 mS.cm{sup -1} at 750 deg C with activation energy of 1.13 eV. Liquid phase sintering by boron oxide addition is effective to enhance the densification of the solid electrolyte. (author)

  19. Synthesis of Mesoporous Nanocrystalline Zirconia by Surfactant-Assisted Hydrothermal Approach.

    Science.gov (United States)

    Nath, Soumav; Biswas, Ashik; Kour, Prachi P; Sarma, Loka S; Sur, Ujjal Kumar; Ankamwar, Balaprasad G

    2018-08-01

    In this paper, we have reported the chemical synthesis of thermally stable mesoporous nanocrystalline zirconia with high surface area using a surfactant-assisted hydrothermal approach. We have employed different type of surfactants such as CTAB, SDS and Triton X-100 in our synthesis. The synthesized nanocrystalline zirconia multistructures exhibit various morphologies such as rod, mortar-pestle with different particle sizes. We have characterized the zirconia multistructures by X-ray diffraction study, Field emission scanning electron microscopy, Attenuated total refection infrared spectroscopy, UV-Vis spectroscopy and photoluminescence spectroscopy. The thermal stability of as synthesized zirconia multistructures was studied by thermo gravimetric analysis, which shows the high thermal stability of nanocrystalline zirconia around 900 °C temperature.

  20. HIGHLY REFRACTORY CRUCIBLES OF STABILIZED ZIRCONIA FOR INDUCTION MELTING OF THE PLATINUM GROUP METALS, FABRICATED BY VIBROCASTING

    Directory of Open Access Journals (Sweden)

    V. V. Primachenko

    2012-01-01

    Full Text Available As the result of the studies at PJSC « UKRNIIO them. A.S.Berezhnogo» the technology and commercial production of crucibles from stabilized zirconia for the smelting of platinum group metals are develop

  1. Two R curves for partially stabilized zirconia

    International Nuclear Information System (INIS)

    Rose, L.R.F.; Swain, M.V.

    1986-01-01

    The enhanced fracture toughness due to stress-induced transformation can be explained from two view points: (1) the increase can be attributed to the need to supply a work of transformation, or (2) the transformation can be considered to result in internal stresses which oppose crack opening. Experimental results for magnesia-partially-stabilized zirconia are presented for the two experimental measures of toughness corresponding to these two viewpoints, namely (1) the specific work of fracture, R, and (2) the nominal stress intensity factor, K/sup R/. It is observed that these two measures are not equivalent during the initial stage of R-curve behavior, prior to reaching steady-state cracking. The theoretical reason for this difference is discussed. In particular, it is noted that the usual definition for the crack extension force does not correspond to the experimentally measured work of fracture in the presence of stress-induced (or pre-existing) sources of internal stress

  2. Yttria-doped zirconia as solid electrolyte for fuel-cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Butz, Benjamin

    2009-11-27

    7.3-10 mol% yttria-doped zirconia (YDZ) was studied with emphasis on its long-term stability as solid electrolyte. The decomposition of common 8.5YDZ (950 C) was detected by analytical TEM. As second issue, the microstructural and chemical properties of nanocrystalline 7.3YDZ thin films were investigated. Metastable t''-YDZ was found to precipitate in nanoscaled regions in YDZ up to 10 mol% yttria. Furthermore, a revised boundary of the c+t phase field, in which YDZ decomposes, is presented. (orig.)

  3. Yttria-doped zirconia as solid electrolyte for fuel-cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Butz, Benjamin

    2009-11-27

    7.3-10 mol% yttria-doped zirconia (YDZ) was studied with emphasis on its long-term stability as solid electrolyte. The decomposition of common 8.5YDZ (950 C) was detected by analytical TEM. As second issue, the microstructural and chemical properties of nanocrystalline 7.3YDZ thin films were investigated. Metastable t''-YDZ was found to precipitate in nanoscaled regions in YDZ up to 10 mol% yttria. Furthermore, a revised boundary of the c+t phase field, in which YDZ decomposes, is presented. (orig.)

  4. Effect of surface composition of yttrium-stabilized zirconia on partial oxidation of methane to synthesis gas.

    NARCIS (Netherlands)

    Zhu, J.J.; van Ommen, J.G.; Knoester, A.; Lefferts, Leonardus

    2005-01-01

    Catalytic partial oxidation of methane to synthesis gas (CPOM) over yttrium-stabilized zirconia (YSZ) was studied within a wide temperature window (500¿1100 °C). The catalysts were characterized by X-ray fluorescence (XRF) and low-energy ion scattering (LEIS). The influence of calcination

  5. Effects of accelerated degradation on metal supported thin film-based solid oxide fuel cell

    DEFF Research Database (Denmark)

    Reolon, R. P.; Sanna, S.; Xu, Yu

    2018-01-01

    A thin film-based solid oxide fuel cell is deposited on a Ni-based metal porous support by pulsed laser deposition with a multi-scale-graded microstructure design. The fuel cell, around 1 μm in thickness, is composed of a stabilized-zirconia/doped-ceria bi-layered dense electrolyte and nanostruct......A thin film-based solid oxide fuel cell is deposited on a Ni-based metal porous support by pulsed laser deposition with a multi-scale-graded microstructure design. The fuel cell, around 1 μm in thickness, is composed of a stabilized-zirconia/doped-ceria bi-layered dense electrolyte......, electrochemical performances are steady, indicating the stability of the cell. Under electrical load, a progressive degradation is activated. Post-test analysis reveals both mechanical and chemical degradation of the cell. Cracks and delamination of the thin films promote a significant nickel diffusion and new...

  6. Synthesis, microstructure and mechanical properties of ceria stabilized tetragonal zirconia prepared by spray drying technique

    International Nuclear Information System (INIS)

    Sharma, S.C.; Gokhale, N.M.; Dayal, Rajiv; Lazl, Ramji

    2002-01-01

    Ceria stabilized zirconia powders with ceria concentration varying from 6 to 16 mol% were synthesized using spray drying technique. Powders were characterized for their particle size distribution and specific surface area. The dense sintered ceramics fabricated using these powders were characterized for their microstructure, crystallite size and phase composition. The flexural strength, fracture toughness and micro-hardness of sintered ceramics were measured. High fracture toughness and flexural strength were obtained for sintered bodies with 12 mol% of CeO 2 . Flexural strength and fracture toughness were dependent on CeO 2 concentration, crystallite size and phase composition of sintered bodies. Correlation of data has indicated that the transformable tetragonal phase is the key factor in controlling the fracture toughness and strength of ceramics. It has been demonstrated that the synthesis method is effective to prepare nanocrystalline tetragonal ceria stabilized zirconia powders with improved mechanical properties. Ce-ZrO 2 with 20 wt% alumina was also prepared with flexural strength, 1200 MPa and fracture toughness 9.2 MPa√m. (author)

  7. Synthesis of mesh-shaped calcia partially stabilized zirconia using eggshell membrane template as filler composite

    Directory of Open Access Journals (Sweden)

    Gema Gempita

    2017-08-01

    Full Text Available This experiment was conducted experimentally to synthesize Calcia Partially Stabilized Zirconia (Ca-PSZ by sol-gel method using eggshell membrane template as a composite filler. The eggshell membrane was used to produce a mesh shaped structure, which hopefully can improve the mechanical properties of the composite. Ca-PSZ filler was synthesized from ZrOCl2 precursor and Ca(NO32 stabilizer with a 24 hours immersion time. Ca-PSZ of synthesis then mixed with the resin matrix to test its composite hardness. The EDS characterization results suggested that the sample contained elements of zirconia, calcium, and oxygen. Whereas, the XRD characterization identified that crystal structures that formed in the sample were nano scale tetragonal. Characterization of SEM showed Ca-PSZ with mesh structured. The average composite hardness value was 15.79 VHN. The composites with Ca-PSZ-synthesized filler could be prepared and its hardness value was higher than the composite with Ca-PSZ filler in spherical particles, but the hardness was still below the composite on the market.

  8. Hydroxyapatite and zirconia composites: Effect of MgO and MgF2 on the stability of phases and sinterability

    International Nuclear Information System (INIS)

    Evis, Zafer; Usta, Metin; Kutbay, Isil

    2008-01-01

    Composites of hydroxyapatite with cubic zirconia with MgO or MgF 2 were pressureless sintered at temperatures from 1000 to 1300 deg. C. The reactions and transformations of phases were monitored with X-ray diffraction. For the hydroxyapatite and zirconia composites with MgO, calcium diffused from hydroxyapatite into the zirconia, and hydroxyapatite decomposed to tri-calcium phosphate at sintering temperatures higher than 1000 deg. C. Above about 1200 deg. C, CaZrO 3 was formed. Composites containing the MgF 2 decomposed slower than the composites with MgO which was verified by the changes in the lattice volume of the hydroxyapatite left in the composites. Fluorine ions in MgF 2 diffused into hydroxyapatite which resulted in thermal stability at high sintering temperatures. Composites with MgF 2 had higher hardness than those with MgO. The lowest porosity was found in a composite initially containing 10 wt% cubic zirconia and 5 wt% MgF 2

  9. Sintered stabilized zirconia microstructure and conductivity

    International Nuclear Information System (INIS)

    Bernard, Herve.

    1981-04-01

    The elaboration of a stabilized zirconia powder which sinters at 1300 0 C and the influence of the sintered polycristal microstructure on its ionic conductivity have been studied. Among three investigated powder preparation processes, coprecipitation in an ammoniacal solution was chosen. After sintering at 1300 0 C, the pellet density was higher than 93% of the theoretical density. It even approached up to 98% TD with addition of less than 0,5 mole % Al 2 O 3 to the initial powder. The overall electrolyte conductivity and the inter and intragranular contributions have been determined by complex impedance spectroscopy. ZrO 2 -Y 2 O 3 solid solution conductivity was scarcely improved by Y 2 O 3 exchange with Yb 2 O 3 or Gd 2 O 3 . This conductivity greatly increases with grain size, its improvement with decreasing porosity, which has been quantified, is less sensible. Moreover, two original properties were noticed: small amounts of Al 2 O 3 and quenching greatly enhanced the overall conductivity. At temperatures below 500 0 C, grain boundaries only insured a partial migration of conductive ions. A parallel type electrical equivalent circuit suited well with this blocking effect [fr

  10. Theoretical Investigation on Structural and Electronic Properties of InN Growth on Ce-Stabilized Zirconia (111 Substrates

    Directory of Open Access Journals (Sweden)

    Yao Guo

    2016-01-01

    Full Text Available The structural and electronic properties of InN on Ce-stabilized zirconia (CeSZ (111 substrates are investigated using first-principles calculations based on density functional theory with GGA + U method. Surface energy calculations indicate that the structure of Ce-segregated surface is more energetically stable than that of Ce-segregation-free surface. Adsorption energies of indium and nitrogen atoms on both Ce-segregated and Ce-segregation-free CeSZ (111 surfaces at the initial growth stage have been studied. The results suggest that the first layer of InN films consists of a nitrogen layer, which leads to epitaxial relationships between InN (0001 // CeSZ (111 and InN [112¯0] // CeSZ [11¯0]. In addition, density of states (DOS analysis revealed that the hybridization effect plays a crucial role in determining the interface structure for the growth of InN on CeSZ (111 surfaces. Furthermore, adsorption energies of indium atoms on the nitrogen layer have also been evaluated in order to investigate the lattice polarity determination for InN films. It was found that an indium atom preferentially adsorbs at the center of three nitrogen atoms stacked on the CeSZ substrate, which results in the formation of In-polarity InN.

  11. Mn-stabilized zirconia: From imitation diamonds to a new potential High-T-C ferromagnetic spintronics

    Czech Academy of Sciences Publication Activity Database

    Ostanin, S.; Ernst, A.; Sandratskii, L. M.; Bruno, P.; Dane, M.; Hughes, I.D.; Staunton, J.B.; Hergert, W.; Mertig, I.; Kudrnovský, Josef

    2007-01-01

    Roč. 98, č. 1 (2007), 016101/1-016101/4 ISSN 0031-9007 R&D Projects: GA MŠk OC 150; GA AV ČR IAA100100616 Institutional research plan: CEZ:AV0Z10100520 Keywords : Mn-stabilized zirconia * ab initio electronic structure calculations Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 6.944, year: 2007

  12. Processing-structure-property relationships in electron beam physical vapor deposited yttria stabilized zirconia coatings

    International Nuclear Information System (INIS)

    Rao, D. Srinivasa; Valleti, Krishna; Joshi, S. V.; Janardhan, G. Ranga

    2011-01-01

    The physical and mechanical properties of yttria stabilized zirconia (YSZ) coatings deposited by the electron beam physical vapor deposition technique have been investigated by varying the key process variables such as vapor incidence angle and sample rotation speed. The tetragonal zirconia coatings formed under varying process conditions employed were found to have widely different surface and cross-sectional morphologies. The porosity, phase composition, planar orientation, hardness, adhesion, and surface residual stresses in the coated specimens were comprehensively evaluated to develop a correlation with the process variables. Under transverse scratch test conditions, the YSZ coatings exhibited two different crack formation modes, depending on the magnitude of residual stress. The influence of processing conditions on the coating deposition rate, column orientation angle, and adhesion strength has been established. Key relationships between porosity, hardness, and adhesion are also presented.

  13. Microstructural development in physical vapour-deposited partially stabilized zirconia thermal barrier coatings

    Energy Technology Data Exchange (ETDEWEB)

    Sohn, Y. H. (Center for Intelligent Processing of Materials, Worcester Polytechnic Institute, 100 Institute Road, Worcester, MA 01609-2280 (United States)); Biederman, R.R. (Center for Intelligent Processing of Materials, Worcester Polytechnic Institute, 100 Institute Road, Worcester, MA 01609-2280 (United States)); Sisson, R.D. Jr. (Center for Intelligent Processing of Materials, Worcester Polytechnic Institute, 100 Institute Road, Worcester, MA 01609-2280 (United States))

    1994-10-01

    The effects of processing parameters of physical vapour deposition on the microstructure of partially stabilized zirconia (PSZ) thermal barrier coatings have been experimentally investigated. Emphasis has been placed on the crystallographic texture of the PSZ coatings and the microstructure of the top surface of the PSZ coatings as well as the metal-ceramic interface. The variations in the deposition chamber temperature, substrate thickness, substrate rotation and vapour incidence angle resulted in the observation of significant differences in the crystallographic texture and microstructure of the PSZ coatings. ((orig.))

  14. Oxygen diffusion in nanocrystalline yttria-stabilized zirconia: the effect of grain boundaries.

    Science.gov (United States)

    De Souza, Roger A; Pietrowski, Martha J; Anselmi-Tamburini, Umberto; Kim, Sangtae; Munir, Zuhair A; Martin, Manfred

    2008-04-21

    The transport of oxygen in dense samples of yttria-stabilized zirconia (YSZ), of average grain size d approximately 50 nm, has been studied by means of 18O/16O exchange annealing and secondary ion mass spectrometry (SIMS). Oxygen diffusion coefficients (D*) and oxygen surface exchange coefficients (k*) were measured for temperatures 673

  15. Strontium zirconate as silicon and aluminum scavenger in yttria stabilized zirconia

    DEFF Research Database (Denmark)

    Andersen, Thomas; Hansen, Karin Vels; Chorkendorff, Ib

    2011-01-01

    Here we report on strontium zirconate as a getter for silicon dioxide and aluminum oxide in yttria stabilized zirconia (YSZ) single crystals for cleaning purposes. YSZ single crystals were covered with strontium zirconate powder and heat treated at 1450°C in water vapor. After treatment the YSZ...... by transmission electron microscopy (TEM) the interface region between bump and YSZ single crystal bulk was examined. EDS showed a homogeneous distribution of silicon and aluminum through the cross section of a bump. The results suggest strontium zirconate as a good getter for silicon and aluminum from bulk...

  16. Shape memory lifetime of CeO2-stabilized tetragonal zirconia polycrystals

    International Nuclear Information System (INIS)

    Zhe Xiaoli; Li Bo; Meng Man

    1993-01-01

    Lifetime of shape memory effect (SME) of CeO 2 -stabilized tetragonal zirconia polycrystals was studied by means of both tests of constraint stress and constraint strain mode during reverse martensite transformation. Up to 8th cycling of SME, the shape of sample entirely recovered except microcracks in the constraint stress mode and the accumulated strain reached 4.6% in the constraint strain mode. It was found that the yield stress decreased, however, the reverse transformation temperature of stress-induced martensite increased with times of the cycling. The reason of these phenomena are discussed in terms of microcracking and strain energy relaxation

  17. Surface modification of yttria stabilized zirconia via polydopamine inspired coating for hydroxyapatite biomineralization

    Science.gov (United States)

    Zain, Norhidayu Muhamad; Hussain, Rafaqat; Kadir, Mohammed Rafiq Abdul

    2014-12-01

    Yttria stabilized zirconia (YSZ) has been widely used as biomedical implant due to its high strength and enhanced toughening characteristics. However, YSZ is a bioinert material which constrains the formation of chemical bonds with bone tissue following implantation. Inspired by the property of mussels, the surface of YSZ ceramics was functionalized by quinone-rich polydopamine to facilitate the biomineralization of hydroxyapatite. YSZ discs were first immersed in 2 mg/mL of stirred or unstirred dopamine solution at either 25 or 37 °C. The samples were then incubated in 1.5 simulated body fluid (SBF) for 7d. The effect of coating temperature for stirred and unstirred dopamine solutions during substrate grafting was investigated on the basis of chemical compositions, wettability and biomineralization of hydroxyapatite on the YSZ functionalized surface. The results revealed that the YSZ substrate grafted at 37 °C in stirred solution of dopamine possessed significantly improved hydrophilicity (water contact angle of 44.0 ± 2.3) and apatite-mineralization ability (apatite ratio of 1.78). In summary, the coating temperature and stirring condition during grafting procedure affected the chemical compositions of the films and thus influenced the formation of apatite layer on the substrate during the biomineralization process.

  18. Effects of focused ion beam milling on electron backscatter diffraction patterns in strontium titanate and stabilized zirconia

    DEFF Research Database (Denmark)

    Saowadee, Nath; Agersted, Karsten; Bowen, Jacob R.

    2012-01-01

    This study investigates the effect of focused ion beam (FIB) current and accelerating voltage on electron backscatter diffraction pattern quality of yttria‐stabilized zirconia (YSZ) and Nb‐doped strontium titanate (STN) to optimize data quality and acquisition time for 3D‐EBSD experiments by FIB...

  19. Low Friction in CuO-Doped Yttria-Stabilized Tetragonal Zirconia Ceramics: A Complementary Macro- and Nanotribology Study

    NARCIS (Netherlands)

    Tocha, E.; Pasaribu, H.R.; Schipper, Dirk J.; Schönherr, Holger; Vancso, Gyula J.

    2008-01-01

    The tribological behavior of CuO-doped yttria-stabilized tetragonal zirconia (3Y-TZP) ceramics in the absence of additional lubricants was characterized by macroscale pin-on-disk measurements and nanoscale atomic force microscopy (AFM) for a broad range of velocities. The previously observed low

  20. CHARACTERIZATION OF YTTRIA AND MAGNESIA PARTIALLY STABILIZED ZIRCONIA BIOCOMPATIBLE COATINGS DEPOSITED BY PLASMA SPRAYING

    Directory of Open Access Journals (Sweden)

    Roşu R. A.

    2013-09-01

    Full Text Available Zirconia (ZrO2 is a biocompatible ceramic material which is successfully used in medicine to cover the metallic implants by various methods. In order to avoid the inconvenients related to structural changes which may appear because of the temperature treatment while depositing the zirconia layer over the metallic implant, certain oxides are added, the most used being Y2O3, MgO and CaO. This paper presents the experimental results regarding the deposition of yttria (Y2O3 and magnesia (MgO partially stabilized zirconia layers onto titanium alloy substrate by plasma spraying method. X ray diffraction investigations carried out both on the initial powders and the coatings evidenced the fact that during the thermal spraying process the structure has not been significantly modified, consisting primarily of zirconium oxide with tetragonal structure. Electronic microscopy analyses show that the coatings are dense, uniform and cracks-free. Adherence tests performed on samples whose thickness ranges between 160 and 220 μm showed that the highest value (23.5 MPa was obtained for the coating of ZrO2 - 8 wt. % Y2O3 with 160 μm thickness. The roughness values present an increasing tendency with increasing the coatings thickness.

  1. Evaluation of technological properties of alumina refractory systems-zirconia and zirconia-silica-alumina; Avaliacao das propriedades tecnologicas de refratarios dos sistemas alumina-zirconia e alumina-zirconia-silica

    Energy Technology Data Exchange (ETDEWEB)

    Marinho, A.R.O.; Carvalho, T.U.S.; Fagury Neto, E.; Rabelo, A.A., E-mail: adriano@unifesspa.edu.br [Universidade Federal do Sul e Sudeste do Para (UFSSPA), Maraba, PA (Brazil)

    2014-07-01

    Alumina-zirconia refractories are noted for being products of excellent cost-effective, however, zirconia may limit its use due to decreasing resistance to thermal shock. This study aims to evaluate these refractories with the addition of microsilica, which can greatly improve their properties. Were used the following starting materials: calcined alumina, zirconia (stabilized and monoclinic) in amounts of 2%, 4% and 6% by weight, plus microsilica (5%w.). The powders were milled together with binder and lubricant for conformation bodies by uniaxial pressing. The samples were dried, calcined and sintered at 1400 °C/2h were characterized using the methods of Archimedes, and scanning electron microscopy (SEM), chemical analysis using energy dispersive X-ray (EDS), and mechanical flexural strength tests at room temperature. Formulations with the presence of microsilica showed satisfactory results and optimized properties. (author)

  2. Defect ordering in aliovalently doped cubic zirconia from first principles

    International Nuclear Information System (INIS)

    Bogicevic, A.; Wolverton, C.; Crosbie, G.M.; Stechel, E.B.

    2001-01-01

    Defect ordering in aliovalently doped cubic-stabilized zirconia is studied using gradient corrected density-functional calculations. Intra- and intersublattice ordering interactions are investigated for both cation (Zr and dopant ions) and anion (oxygen ions and vacancies) species. For yttria-stabilized zirconia, the crystal structure of the experimentally identified, ordered compound δ-Zr 3 Y 4 O 12 is established, and we predict metastable zirconia-rich ordered phases. Anion vacancies repel each other at short separations, but show an energetic tendency to align as third-nearest neighbors along directions. Calculations with divalent (Be, Mg, Ca, Sr, Ba) and trivalent (Y, Sc, B, Al, Ga, In) oxides show that anion vacancies prefer to be close to the smaller of the cations (Zr or dopant ion). When the dopant cation is close in size to Zr, the vacancies show no particular preference, and are thus less prone to be bound preferentially to any particular cation type when the vacancies traverse such oxides. This ordering tendency offers insight into the observed high conductivity of Y 2 O 3 - and Sc 2 O 3 -stabilized zirconia, as well as recent results using, e.g., lanthanide oxides. The calculations point to In 2 O 3 as a particularly promising stabilizer for high ionic conductivity. Thus we are able to directly link (thermodynamic) defect ordering to (kinetic) ionic conductivity in cubic-stabilized zirconia using first-principles atomistic calculations

  3. Positron annihilation study of yttria-stabilized zirconia nanopowders containing Cr2O3 additive

    International Nuclear Information System (INIS)

    Prochazka, I; Cizek, J; Melikhova, O; Kuriplach, J; Konstantinova, T E; Danilenko, I A

    2011-01-01

    Yttria-stabilized zirconia compacted nanopowders, doped with trivalent chromium oxide, were studied by means of high-resolution positron lifetime and coincidence Doppler broadening techniques. The observed data suggest that positrons annihilate mainly in vacancylike defects at grain boundaries or in larger open volumes most likely located at triple points. The results also show that an addition of Cr 2 O 3 leads to a decrease in grain size.

  4. Trial production and characterisation of fully calcia-stabilised zirconia

    International Nuclear Information System (INIS)

    George, A.M.; Karkhanavala, M.D.

    1980-01-01

    A process for manufacture of stabilized zirconia powder has been developed. The process is quite versatile since stabilization is achieved at relatively low temperatures (950deg - 1000deg C) and can be used for manufacture of either fully or partially calcia-stabilized zirconia. A 100 Kg trial batch of fully stabilized zirconia powder was produced accordingly at the Indian Rare Earths Ltd. plant and its characteristics were evaluated by XRD, microscopy, surface area and density measurements. The powder on firing at 1400deg C showed considerable volume shrinkage, as expected. On manually compacting with a phosphatic binder and firing for 8-10 hrs at 1300deg-1400deg C sintered shapes having bulk densities around 80-85% T.D. are easily obtained. Details of the measurements and the prospective industrial applications of the material are discussed. (auth.)

  5. Thin film battery/fuel cell power generating system. Final report, Task E-4, April 1976-April 1978

    Energy Technology Data Exchange (ETDEWEB)

    Feduska, W.

    1978-03-31

    A two-year researth program to design and demonstrate the technical feasibility of a high-temperature solid-electrolyte fuel cell is described in detail. A rare-earth chromite, in particular, La /sub 95/Mg /sub 05/Cr /sub 75/Al /sub 25/0/sub 3/ was identified, synthesized by RF-sputtering tested for resistivity, thermal expansion and inertness in contact with yttria-stabilized zirconia, and was found promising as a candidate interconnection material. Films of these interconnection materials have been successfully deposited onto stabilized zirconia tubes by electrochemical vapor deposition (EVD) and the technique has been used to fabricate such films in building fuel cell stacks. Tin-doped indium oxide and antimony-doped tin oxide air electrode current collector materials have been successfully (CVD) chemically vapor deposited, as thin films, onto zirconia tubes. Fabrication procedures for the preparation of thin films of the nickel-cermet fuel electrode and yttria-stabilized zirconia solid electrolyte have been re-verified and improved for use in preparing unit cells and cell stacks on the program. An in-house extrusion technology for porous calcia-stabilized zirconia tubes has been developed and has been used to provide suitable support tubes for component combination samples, unit cell and cell stack sample preparation. Test concepts for component combinations and for unit cells and cell stacks have been evolved, particularly, the crossed electrode technique, and test equipment has been designed, built and used to evaluate fuel cell components and their interfaces. A five-cell fuel cell stack has been fabricated and operated for 700 hours at 200 mA/cm/sup 2/ at 950 to 980/sup 0/C and was subjected to three temperature cycles during the testing. Three series connected cells of this five cell stack met the 80% voltage efficiency final target objective of the program (less than 10% voltage degradation in 700 hours - with only 300 hours required.)

  6. Highly oriented as-deposited superconducting laser ablated thin films of Y1Ba2Cu3O/sub 7-//sub δ/ on SrTiO3, zirconia, and Si substrates

    International Nuclear Information System (INIS)

    Koren, G.; Polturak, E.; Fisher, B.; Cohen, D.; Kimel, G.

    1988-01-01

    KrF excimer laser ablation of an Y 1 Ba 2 Cu 3 O/sub 7-//sub δ/ pellet in 0.1--0.2 Torr of O 2 ambient was used to deposit thin superconducting films onto SrTiO 3 , yttria-stabilized zirconia (YSZ), and silicon substrates at 600--700 0 C. The as-deposited 1-μm-thick films at 650--700 0 C substrate temperature were superconducting, without further high-temperature annealing. All films had a similar T/sub c/ onset of ∼92 K but different zero-resistance T/sub c/ of 90, 85, and 70 K for the films on SrTiO 3 , YSZ, and Si substrates, respectively. Angular x-ray diffraction analysis showed that all the films were highly oriented with the c axis perpendicular to their surface. Critical current densities at 77 K were about 40 000 and 10 000 A/cm 2 for the films on SrTiO 3 and YSZ, respectively. Smooth surface morphology was observed in all films, with occasional defects and cracks in the films on YSZ, which seems to explain the lower critical current in these films

  7. Effects of the presence of heavy rare earths on the stabilization of the zirconia ceramics - Yttria; Efeito da presenca de terras raras pesadas na estabilizacao das fases de ceramicas de zirconia - itria

    Energy Technology Data Exchange (ETDEWEB)

    Lazar, D.R.R.; Fancio, E.; Menezes, C.A.B.; Ussui, V.; Bressiani, A.H.A.; Lima, N.B.; Paschoal, J.O.A. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)], e-mail: drlazar@net.ipen.br

    2000-07-01

    The use of Yttria concentrates has been proposed to substitute the high purity Yttria in the zirconia stabilization. The elements terbium, dysprosium, holmium, erbium and ytterbium, classified as heavy rare earths, are the main impurities in these concentrates, due to their presence in yttrium ores. Besides that, the chemical similarities of these elements need the utilization of complex purification techniques. Considering the importance of the employed dopant on zirconia crystallization, this work shows the quantitative phases analysis of powders and ceramics of stabilized zirconia doped with 3 and 9 mol % of high purity Yttria and with a 85 wt % Yttria concentrate. This determination was performed using the Rietveld refinement of the X-ray diffraction data. The powders were synthesized by the hydroxides coprecipitation route, which includes treatments with ethanol and butanol, drying, calcination at 800 deg C for 1 hour and milling in a ball mill and in an attrition mill. The ceramics pellets were pressed uniaxially and sintered at 1550 deg C for 1 hour. The powders and sintered pellets were also characterized by X-ray fluorescence analysis, laser diffraction, gas adsorption (B.E.T.), scanning electron microscopy and determination of apparent density by the Archimedes method. The results showed the same stabilization behavior when it was employed high purity Yttria and a concentrate of this oxide. It was also observed the predominating formation of tetragonal and cubic phases when the dopant concentration is 3 and 9 mol %, respectively. (author)

  8. Using Dark Field X-Ray Microscopy To Study In-Operando Yttria Stabilized Zirconia Electrolyte Supported Solid Oxide Cell

    DEFF Research Database (Denmark)

    Sierra, J. X.; Poulsen, H. F.; Jørgensen, P. S.

    Dark Field X-Ray Microscopy is a promising technique to study the structure of materials in nanometer length scale. In combination with x-ray diffraction technique, the microstructure evolution of Yttria Stabilized Zirconia electrolyte based solid oxide cell was studied running at extreme operating...

  9. Tetragonal BiFeO3 on yttria-stabilized zirconia

    International Nuclear Information System (INIS)

    Liu, Heng-Jui; Du, Yu-Hao; Gao, Peng; Ikuhara, Yuichi; Huang, Yen-Chin; Chen, Yi-Chun; Chen, Hsiao-Wen; Liu, Hsiang-Lin; He, Qing; Chu, Ying-Hao

    2015-01-01

    High structural susceptibility of multiferroic BiFeO 3 (BFO) makes it a potential replacement of current Pb-based piezoelectrics. In this study, a tetragonal phase is identified based on a combination of x-ray diffraction, scanning transmission electronic microscopy, x-ray absorption spectroscopy, and Raman spectroscopy when BFO is grown on yttria-stabilized zirconia (YSZ) substrates. To distinguish the discrepancy between this tetragonal phase and common cases of monoclinic BFO, piezoelectric force microscopy images and optical property are also performed. It shows a lower electrostatic energy of ferroelectric domains and a large reduction of band gap for BFO grown on YSZ substrate comparing to the well-known one grown on LaAlO 3 substrate. Our findings in this work can provide more insights to understand the structural diversity of multiferroic BFO system for further applications

  10. Enhancement of ionic conductivity in stabilized zirconia ceramics under millimeter-wave irradiation heating

    International Nuclear Information System (INIS)

    Kishimoto, Akira; Ayano, Keiko; Hayashi, Hidetaka

    2011-01-01

    Ionic conductivity in yttria-stabilized zirconia ceramics under millimeter-wave irradiation heating was compared with that obtained using conventional heating. The former was found to result in higher conductivity than the latter. Enhancement of the ionic conductivity and the reduction in activation energy seemed to depend on self-heating resulting from the millimeter-wave irradiation. Millimeter-wave irradiation heating restricted the degradation in conductivity accompanying over-substitution, suggesting the optimum structure that provided the maximum conductivity could be different between the two heating methods.

  11. EPR study of electron traps in x-ray-irradiated yttria-stabilized zirconia

    International Nuclear Information System (INIS)

    Azzoni, C.B.; Paleari, A.

    1989-01-01

    Single crystals of yttria-stabilized zirconia (12 mol % of Y 2 O 3 ) have been x-ray irradiated at room temperature. The electron paramagnetic resonance spectrum of the filled electron traps is analyzed in terms of a single oxygen vacancy type of defect with its symmetry axis along the left-angle 111 right-angle direction. The angular dependence of the linewidth and the asymmetry of the line shape are attributed to the disordered rearrangements of the anion sublattice surrounding the oxygen vacancy. This affects the local crystal fields and the directions of the symmetry axis of the defects

  12. EPR study of electron traps in x-ray-irradiated yttria-stabilized zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Azzoni, C.B.; Paleari, A. (Dipartimento di Fisica, Alessandro Volta dell' Universita di Pavia, via Bassi 6, 27100 Pavia, Italy (IT))

    1989-10-01

    Single crystals of yttria-stabilized zirconia (12 mol % of Y{sub 2}O{sub 3}) have been x-ray irradiated at room temperature. The electron paramagnetic resonance spectrum of the filled electron traps is analyzed in terms of a single oxygen vacancy type of defect with its symmetry axis along the {l angle}111{r angle} direction. The angular dependence of the linewidth and the asymmetry of the line shape are attributed to the disordered rearrangements of the anion sublattice surrounding the oxygen vacancy. This affects the local crystal fields and the directions of the symmetry axis of the defects.

  13. Study of the cubic - to - monoclinic transformation in magnesia partially stabilized zirconia

    International Nuclear Information System (INIS)

    Muccillo, R.

    1988-01-01

    The transformation of the cubic phase to the stable monoclinic phase in ZrO 2 : 3%MgO quenched from 1450 0 C to RT has been studied by X-ray diffractometry in order to explain the thermal hysteresis in the electrical conductivity. The monoclinic-to-cubic ratio has been measured for samples annealed in the 500 0 C-1000 0 C temperature range. The results show that the decrease in the cubic phase content is the main responsible for the thermal hysteresis in the electrical conductivity of the magnesia partially stabilized zirconia solid electrolytes. (author) [pt

  14. Zirconia stabilization and its retention at room temperature in the ZrO sub(2). TiO sub(2) system. Estabilizacao de zirconia e sua retencao a temperatura ambiente no sistema ZrO sub(2). TiO sub(2)

    Energy Technology Data Exchange (ETDEWEB)

    Pandolfelli, V C; Rodrigues, J A [Sao Carlos Univ., SP (Brazil). Dept. de Engenharia de Materiais; Longo, E [Sao Carlos Univ., SP (Brazil). Dept. de Quimica; Stevens, R [Leeds Univ. (UK)

    1990-01-01

    Based on the results obtained in the ZrO sub(2).MO sub(x) systems, the stabilization aspects of tetragonal zirconia is discussed in an integrated way, in order to differentiate among the thermodynamical, the kinetic and stress fields effects of the dopant ion on the stabilization. In the ZrO2.TiO2 system, when in solid solution, TiO additions act to suppress the ZrO2 densification, leading to grain growth when attempts are made to attain higher densities. Such effect is believed to be the main factor preventing retention of tetragonal zirconia at room temperature in this system. (author).

  15. Analysis of the zirconia structure by `ab initio` and Rietveld methods; Analise da estrutura da zirconia por metodos `Ab initio` e de Rietveld

    Energy Technology Data Exchange (ETDEWEB)

    Bechepeche, A.P.; Nasar, R.S.; Longo, E. [Sao Carlos Univ., SP (Brazil). Dept. de Quimica; Treu Junior, O.; Varela, J.A. [UNESP, Araraquara, SP (Brazil). Inst. de Quimica

    1995-12-31

    The zirconia was doped with 0,113 mol of Mg O e 0,005 mol of Ti O{sub 2}, and it was calcined in 1550{sup d}eg C and it was analyzed by XRD. The results shows that pure zirconia contains 96,19% of monoclinic phase and 3,18% of cubic. However, the doping magnesia stabilizes the zirconia in 17,24 of monoclinic; 29,63 of tetragonal and 53,13% of cubic phase. The addition of titanium in zirconia gives 25,85% of tetragonal phase and 37,66% of cubic, and this shows the no stabilizing action of this transition metal. By the other side, the results with ab-initio calculating shows the same tendency resulting in the next values of total energy: pure zirconia - monoclinic -11.316,86ua; tetragonal -8742,09 ua and cubic -8742,80 ua and Zr O{sub 2} Ti O{sub 2} system - monoclinic -9463,02 ua, tetragonal -9459,39 ua and cubic -9459,97 ua (author) 3 figs., 2 tabs.

  16. Long-term stability and properties of zirconia ceramics for heavy duty diesel engine components

    Science.gov (United States)

    Larsen, D. C.; Adams, J. W.

    1985-01-01

    Physical, mechanical, and thermal properties of commercially available transformation-toughened zirconia are measured. Behavior is related to the material microstructure and phase assemblage. The stability of the materials is assessed after long-term exposure appropriate for diesel engine application. Properties measured included flexure strength, elastic modulus, fracture toughness, creep, thermal shock, thermal expansion, internal friction, and thermal diffusivity. Stability is assessed by measuring the residual property after 1000 hr/1000C static exposure. Additionally static fatigue and thermal fatigue testing is performed. Both yttria-stabilized and magnesia-stabilized materials are compared and contrasted. The major limitations of these materials are short term loss of properties with increasing temperature as the metastable tetragonal phase becomes more stable. Fine grain yttria-stabilized material (TZP) is higher strength and has a more stable microstructure with respect to overaging phenomena. The long-term limitation of Y-TZP is excessive creep deformation. Magnesia-stabilized PSZ has relatively poor stability at elevated temperature. Overaging, decomposition, and/or destabilization effects are observed. The major limitation of Mg-PSZ is controlling unwanted phase changes at elevated temperature.

  17. Impact of impurity content on the sintering resistance and phase stability of dysprosia- and yttria-stabilized zirconia thermal barrier coatings

    Czech Academy of Sciences Publication Activity Database

    Curry, N.; Janikowski, W.; Pala, Zdeněk; Vilémová, Monika; Markocsan, N.

    2014-01-01

    Roč. 23, 1-2 (2014), s. 160-169 ISSN 1059-9630. [International Thermal Spray Conference (ITSC2013). Busan, 13.05.2013-15.05.2013] Institutional support: RVO:61389021 Keywords : atmospheric plasma spray (APS) * thermal and phase stability of coatings * thermal barrier coatings (TBCs) * thermal conductivity * zirconia Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.344, year: 2014 http://link.springer.com/article/10.1007%2Fs11666-013-0014-9/fulltext.html

  18. Structural evolution of plasma-sprayed nanoscale 3 mol% and 5 mol% yttria-stabilized zirconia coatings during sintering

    Science.gov (United States)

    Zhao, Yan; Gao, Yang

    2017-12-01

    The microstructure of plasma-sprayed nanostructured yttria-stabilized zirconia (YSZ) coatings may change during high-temperature exposure, which would influence the coating performance and service lifetime. In this study, the phase structure and the microstructural evolution of 3YSZ (zirconia-3 mol% yttria) and 5YSZ (zirconia-5 mol% yttria) nanostructured coatings were investigated by means of sintering at 1400 °C for 50-100 h. The microhardness, elastic moduli, and thermal shock cycles of the 3YSZ and 5YSZ nanostructured coatings were also investigated. The results showed that the redistribution of yttrium ions at 1400 °C caused the continuous increase of monoclinic-phase zirconia, but no obvious inter-splat cracking formed at the cross-sections, even after 100 h. Large voids appeared around the nanoporous zone because of the sintering of nanoscale granules upon high-temperature exposure. The microhardness and elastic moduli of the nanostructured coatings first increased and then decreased with increasing sintering times. The growth rate of the nanograins in the 3YSZ coating was lower than that in 5YSZ, which slowed the changes in 3YSZ coating porosity during sintering. Although the 3YSZ coating was prone to monoclinic phase transition, the experimental results showed that the thermal shock resistance of the 3YSZ coating was better than that of the 5YSZ coating.

  19. Evaluation of technological properties of alumina refractory systems-zirconia and zirconia-silica-alumina

    International Nuclear Information System (INIS)

    Marinho, A.R.O.; Carvalho, T.U.S.; Fagury Neto, E.; Rabelo, A.A.

    2014-01-01

    Alumina-zirconia refractories are noted for being products of excellent cost-effective, however, zirconia may limit its use due to decreasing resistance to thermal shock. This study aims to evaluate these refractories with the addition of microsilica, which can greatly improve their properties. Were used the following starting materials: calcined alumina, zirconia (stabilized and monoclinic) in amounts of 2%, 4% and 6% by weight, plus microsilica (5%w.). The powders were milled together with binder and lubricant for conformation bodies by uniaxial pressing. The samples were dried, calcined and sintered at 1400 °C/2h were characterized using the methods of Archimedes, and scanning electron microscopy (SEM), chemical analysis using energy dispersive X-ray (EDS), and mechanical flexural strength tests at room temperature. Formulations with the presence of microsilica showed satisfactory results and optimized properties. (author)

  20. Synthesis of nanosized powders of stabilized zirconia

    International Nuclear Information System (INIS)

    Takodoro, Sandra Kiyoko

    2000-01-01

    Zirconia solid solutions containing 3 mol % Yttria or 12 mol % ceria have been prepared by the coprecipitation technique followed by azeotropic distillation. The aim of this work is the synthesis of tetragonal zirconia polycrystals nanosized powders that sinter at comparatively lower temperatures attaining high densification, and without using any milling procedure. The main results show that: 1- the dopant cation has a strong influence on the crystallization behavior of the precipitates; 2- the used techniques allowed for obtaining high values of specific surface area (∼130 m 2 .g -1 ); 3- the optimization of the synthesis and processing parameters are responsible for obtaining high densification (≥97% of the theoretical value), at lower temperatures (∼1200 deg C) with average grain sizes lower than 500 nm; 4- impedance spectroscopy results show a strong correlation between the electrical resistivity and the microstructure of sintered ceramics.(author)

  1. Formation of metastable tetragonal zirconia nanoparticles: Competitive influence of the dopants and surface state

    Energy Technology Data Exchange (ETDEWEB)

    Gorban, Oksana, E-mail: matscidep@aim.com [Donetsk Institute for Physics and Engineering named after A.A. Galkin of the NAS of Ukraine, Nauki av. 46, Kyiv 03680 (Ukraine); Synyakina, Susanna; Volkova, Galina; Gorban, Sergey; Konstantiova, Tetyana [Donetsk Institute for Physics and Engineering named after A.A. Galkin of the NAS of Ukraine, Nauki av. 46, Kyiv 03680 (Ukraine); Lyubchik, Svetlana, E-mail: s_lyubchik@yahoo.com [REQUIMTE, Universida de Nova de Lisboa, 2829-516 Caparica (Portugal)

    2015-12-15

    The effect of the surface modification of the nanoparticles of amorphous and crystalline partially stabilized zirconia by fluoride ions on stability of the metastable tetragonal phase was investigated. Based on the DSC, titrimetry and FTIR spectroscopy data it was proven that surface modification of the xerogel resulted from an exchange of the fluoride ions with the basic OH groups. The effect of the powder pre-calcination temperature before modification on the formation of metastable tetragonal phase in partially stabilized zirconia was investigated. It was shown that the main factor of tetragonal zirconia stabilization is the state of nanoparticles surface at pre-crystallization temperatures.

  2. Granular nanocrystalline zirconia electrolyte layers deposited on porous SOFC cathode substrates

    International Nuclear Information System (INIS)

    Seydel, Johannes; Becker, Michael; Ivers-Tiffee, Ellen; Hahn, Horst

    2009-01-01

    Thin granular yttria-stabilized zirconia (YSZ) electrolyte layers were prepared by chemical vapor synthesis and deposition (CVD/CVS) on a porous substoichiometric lanthanum-strontium-manganite (ULSM) solid oxide fuel cell cathode substrate. The substrate porosity was optimized with a screen printed fine porous buffer layer. Structural analysis by scanning electron microscopy showed a homogeneous, granular nanocrystalline layer with a microstructure that was controlled via reactor settings. The CVD/CVS gas-phase process enabled the deposition of crack-free granular YSZ films on porous ULSM substrates. The electrolyte layers characterized with impedance spectroscopy exhibited enhanced grain boundary conductivity.

  3. Stability of prototype two-piece zirconia and titanium implants after artificial aging: an in vitro pilot study.

    Science.gov (United States)

    Kohal, Ralf-Joachim; Finke, Hans Christian; Klaus, Gerold

    2009-12-01

    270 and 393 N (mean: 325.1 N), for group 2 between 235 and 321 N (mean: 281.8 N), and between 474 and 765 N (mean: 595.2 N) for the titanium group. The failure mode during the fracture testing in the zirconia implant groups was a fracture of the implant head and a bending/fracture of the abutment screw in the titanium group. Within the limits of this pilot investigation, the biomechanical stability of all tested prototype implant groups seems to be - compared with the possibly exerted occlusal forces - borderline for clinical use. A high number of failures occurred already during the artificial loading in the titanium group at the abutment screw level. The zirconia implant groups showed irreparable implant head fractures at relatively low fracture loads. Therefore, the clinical use of the presented prototype implants has to be questioned.

  4. Microstructural stability of spark-plasma-sintered Wf/W composite with zirconia interface coating under high-heat-flux hydrogen beam irradiation

    Directory of Open Access Journals (Sweden)

    M. Avello de Lama

    2017-12-01

    In this paper, the durability and chemical stability of Wf/W composite specimens under cyclic heat-flux loads up to 20 MW/m² (surface temperature: 1260 °C was investigated using hydrogen neutral beam. The bulk material was fabricated by means of spark-plasma-sintering (SPS method using fine tungsten powder and a stack of tungsten wire meshes as reinforcement where the surface of the wire was coated with zirconia thin film to produce an engineered interface. The impact of plasma beam irradiation on microstructure was examined for two kinds of specimens produced at different sintering temperatures, 1400 °C and 1700 °C. Results of microscopic (SEM and chemical (EDX analysis are presented comparing the microstructure and element distribution maps obtained before and after heat flux loading. Effects of different sintering temperatures on damage behaviour are discussed. The present composite materials are shown to be applicable as plasma-facing material for high-heat-flux components.

  5. Synthesis and characterization of scandia ceria stabilized zirconia powders prepared by polymeric precursor method for integration into anode-supported solid oxide fuel cells

    Science.gov (United States)

    Tu, Hengyong; Liu, Xin; Yu, Qingchun

    2011-03-01

    Scandia ceria stabilized zirconia (10Sc1CeSZ) powders are synthesized by polymeric precursor method for use as the electrolyte of anode-supported solid oxide fuel cell (SOFC). The synthesized powders are characterized in terms of crystalline structure, particle shape and size distribution by X-ray diffraction (XRD), transmission electron microscopy (TEM) and photon correlation spectroscopy (PCS). 10Sc1CeSZ electrolyte films are deposited on green anode substrate by screen-printing method. Effects of 10Sc1CeSZ powder characteristics on sintered films are investigated regarding the integration process for application as the electrolytes in anode-supported SOFCs. It is found that the 10Sc1CeSZ films made from nano-sized powders with average size of 655 nm are very porous with many open pores. In comparison, the 10Sc1CeSZ films made from micron-sized powders with average size of 2.5 μm, which are obtained by calcination of nano-sized powders at higher temperatures, are much denser with a few closed pinholes. The cell performances are 911 mW cm-2 at the current density of 1.25 A cm-2 and 800 °C by application of Ce0.8Gd0.2O2 (CGO) barrier layer and La0.6Sr0.4CoO3 (LSC) cathode.

  6. Synthesis, processing and characterization of the solid oxide half-cells cathode/electrolyte of strontium-doped lanthanum manganite/Yttria-stabilized zirconia

    International Nuclear Information System (INIS)

    Chiba, Rubens

    2010-01-01

    The ceramic films of strontium-doped lanthanum manganite (LSM) and strontium doped lanthanum manganite/Yttria-stabilized zirconia (LSM/YSZ) are used as cathodes of the high temperature solid oxide fuel cells (HTSOFC). These porous ceramic films had been deposited on the YSZ dense ceramic substrate, used as electrolyte, structural component of the module, thus conferring a configuration of half-cell called auto-support. The study of the half-cell it is basic, therefore in the interface cathode/electrolyte occurs the oxygen reduction reaction, consequently influencing in the performance of the HTSOFC. In this direction, the present work contributes for the processing of thin films, using the wet powder spraying technique, adopted for the conformation of the ceramic films for allowing the attainment of porous layers with thicknesses varied in the order of micrometers. The LSM powders were synthesized by the citrate technique and the LSM/YSZ powders synthesized by the solid mixture technique. In the stage of formation were prepared organic suspensions of LSM and LSM/YSZ fed by gravity in a manual aerograph. For the formation of the YSZ substrate was used a hydraulic uniaxial press. The attainment of solid oxide half-cells cathode/electrolyte was possible of crystalline structures hexagonal for phase LSM and cubic for phase YSZ. The half-cells micrographs show that the YSZ substrate is dense, enough to be used as solid electrolyte, and the LSM and LSM/YSZ films are presented porous with approximately 30 μm of thickness and good adherence between the cathodes and the electrolyte. The presence of composite cathode between the LSM cathode and YSZ substrate, presented an increase in the electrochemical performance in the oxygen reduction reaction. (author)

  7. Anisotropic ionic conductivity observed in superplastically deformed yttria-stabilized zirconia/alumina composite

    International Nuclear Information System (INIS)

    Drennan, J.; Swain, M.V.; Badwal, S.P.S.

    1989-01-01

    Ionic conductivity measurements on a yttria-stabilized tetragonal zirconia polycrystal/alumina composite subjected to superplastic deformation demonstrate anisotropic character. Parallel to the pressing direction, the grain-boundary resistance to oxygen ion mobility is 25% to 30% higher than that measured perpendicular to the pressing direction. The same directional dependency on the volume conductivity is observed but is less pronounced, showing approximately a 9% difference. Microstructural evidence reveals an agglomeration and elongation of alumina particles perpendicular to the pressing direction, and it is suggested that this phenomenon restricts the passage of ions parallel to the compression direction, giving rise to the anisotropic nature of the conductivity measurements

  8. Analysis of the zirconia structure by 'ab initio' and Rietveld methods

    International Nuclear Information System (INIS)

    Bechepeche, A.P.; Nasar, R.S.; Longo, E.; Treu Junior, O.; Varela, J.A.

    1995-01-01

    The zirconia was doped with 0,113 mol of Mg O e 0,005 mol of Ti O 2 , and it was calcined in 1550 d eg C and it was analyzed by XRD. The results shows that pure zirconia contains 96,19% of monoclinic phase and 3,18% of cubic. However, the doping magnesia stabilizes the zirconia in 17,24 of monoclinic; 29,63 of tetragonal and 53,13% of cubic phase. The addition of titanium in zirconia gives 25,85% of tetragonal phase and 37,66% of cubic, and this shows the no stabilizing action of this transition metal. By the other side, the results with ab-initio calculating shows the same tendency resulting in the next values of total energy: pure zirconia - monoclinic -11.316,86ua; tetragonal -8742,09 ua and cubic -8742,80 ua and Zr O 2 Ti O 2 system - monoclinic -9463,02 ua, tetragonal -9459,39 ua and cubic -9459,97 ua (author)

  9. Deformation bands in ceria-stabilized tetragonal zirconia/alumina. 2: Stress-induced aging at room temperature

    International Nuclear Information System (INIS)

    Sergo, V.; Clarke, D.R.

    1995-01-01

    A stress-induced aging phenomenon is observed to occur at room temperature in deformation bands introduced into a 8.5 mol% ceria-stabilized tetragonal zirconia/alumina (Ce-TZP/Al 2 O 3 ) composite by flexural loading. The aging occurs with time after unloading and in laboratory air. Over a period of 100 days, the concentration of monoclinic zirconia within a deformation band increases and, in addition, the wedge-shaped deformation band grows with time. Accompanying these two changes are an increase in the tensile stress in the remaining tetragonal zirconia within the deformation band and a consequential increase in the overall compressive stress within the band. The average value of the monoclinic concentration within the deformation band is found to increase parabolically with time, suggesting the mechanism responsible for the observed aging is diffusion limited. Away from the deformation bands, no aging is observed to occur, suggesting aging is stress dependent. Although a water-vapor-mediated mechanism cannot be ruled out, it is proposed that the observed aging is in fact due to a tensile stress assisted chemical reduction of Ce 4+ to Ce 3+ whose rate is controlled by the indiffusion of oxygen vacancies driven by the tensile stress gradient. It is further proposed that the deformation band grows with time the region ahead of the band is under tension a subject to an enhanced rate of reduction

  10. Fabrication and properties of yttria, ceria doped zirconia-aluminia ceramic composites

    International Nuclear Information System (INIS)

    Lyubushkin, R.A.; Ivanov, O.N.; Chuev, V.P.; Buzov, A.A.

    2011-01-01

    At present, zirconia-based ceramics are gaining popularity in dentistry, particularly in fixed prosthodontics. clinically, it is important that ceramic restorations reproduce the translucency and color of natural teeth. Zirconia based ceramics is a high performance material with excellent biocompatibility and mechanical properties, which suggest its suitability for posterior fixed partial dentures. Y 2 O 3 -stabilized tetragonal zirconia polycrystalline (YTZ/Al 2 O 3 ) and CeO 2 -stabilized tetragonal zirconia polycrystalline (CZA) ceramics with high-performance were prepared for dental application by use the wet chemical route, consolidated by cold isostatic pressing, and two-step sintering method. Physical and mechanical properties test results show that the bending strength, fracture toughness, and the density of full sintered ceramics suggest that the material is relatively suitable for dental restoration.

  11. Thermochemical stability of zirconia-titanium nitride as mixed ionic-electronic composites

    DEFF Research Database (Denmark)

    Silva, P. S. M.; Esposito, V.; Marani, D.

    2018-01-01

    Dense zirconia (8% molar yttria-stabilized ZrO2)-titanium nitride (TiN) composites are fabricated to obtain mixed ionic-electronic conducting ceramic systems with high degree of electronic and thermal conductivity. The composites are consolidated by spark plasma sintering (SPS), starting from pure...... the composites, high electrical conductivity is attained. Samples exhibit metallic behavior, showing an unexpected percolation of TiN in the YSZ matrix for volume fraction ≤ 25 wt% (27 vol%). Chemical degradation and electrical properties of the compounds were monitored under oxidative (air) and inert (Ar...... transport properties of the composite can be tuned by both the relative volume fraction of phases and controlled oxidative treatments. Adjusting such parameters different electric behaviors were observed ranging from predominant electronic conductors, to temperature-independent resistivity...

  12. Thickness dependence of light transmittance, translucency and opalescence of a ceria-stabilized zirconia/alumina nanocomposite for dental applications.

    Science.gov (United States)

    Shiraishi, Takanobu; Watanabe, Ikuya

    2016-05-01

    This study was conducted to investigate thickness dependence of light transmittance, translucency and opalescence of a commercially available fully-sintered ceria-stabilized zirconia/alumina nanocomposite for dental all-ceramic restorations. Three disk samples of 16 mm in diameter and thickness ranging from 0.2 to 0.6 mm with 0.1 mm increment each were cut from a fully-sintered rod-shaped Ce-TZP/alumina nanocomposite (NANOZR, Panasonic Healthcare, Japan) and polished flat by using diamond slurry. Spectral light transmittance data under the CIE standard illuminant D65 were recorded at 10nm intervals from 360 to 740 nm using a computer-controlled spectrophotometer. Average transmittance, translucency and opalescence parameters were determined as a function of sample thickness. Optical properties of a fully-sintered yttria-stabilized tetragonal zirconia polycrystals (Cercon(®) base, DeguDent GmbH, Germany) were also investigated as a reference. Two-way ANOVA was performed to determine the significant differences in various optical parameters among types of ceramic and thicknesses at α=0.05. Results of the two-way ANOVA showed that the average transmittance, translucency and opalescence parameters of both ceramic materials were significantly influenced by the type of ceramic and thickness (popalescence parameters exceeding 20 CIE units when the sample thickness was nearly 0.3 mm. The prominent characteristics of high opalescence and low transmittance of light in the NANOZR was considered to be caused by its specific very fine interpenetrated intragranular microstructure and by a large difference of refractive indices of Ce-TZP and alumina components. High opalescence and low transmittance of light of the ceria-stabilized zirconia/alumina nanocomposite (NANOZR) are attractive properties for use as a substructure in fabricating porcelain-veneering-type esthetic all-ceramic restorations. Copyright © 2016 Academy of Dental Materials. Published by Elsevier Ltd. All

  13. Tetragonal BiFeO{sub 3} on yttria-stabilized zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Heng-Jui [Department of Materials Science Engineering, National Chiao Tung University, Hsinchu 30010, Taiwan (China); Department of Physics, National Taiwan Normal University, Taipei 11677, Taiwan (China); Du, Yu-Hao [Department of Materials Science Engineering, National Chiao Tung University, Hsinchu 30010, Taiwan (China); Gao, Peng; Ikuhara, Yuichi [Institute of Engineering Innovation, The University of Tokyo, Tokyo 113-8656 (Japan); Huang, Yen-Chin; Chen, Yi-Chun [Department of Physics, National Cheng Kung University, Tainan 70101, Taiwan (China); Chen, Hsiao-Wen; Liu, Hsiang-Lin [Department of Physics, National Taiwan Normal University, Taipei 11677, Taiwan (China); He, Qing [Department of Physics, Durham University, Durham DH1 3LE (United Kingdom); Chu, Ying-Hao, E-mail: yhc@nctu.edu.tw [Department of Materials Science Engineering, National Chiao Tung University, Hsinchu 30010, Taiwan (China); Institute of Physics, Academia Sinica, Taipei 11529, Taiwan (China)

    2015-11-01

    High structural susceptibility of multiferroic BiFeO{sub 3} (BFO) makes it a potential replacement of current Pb-based piezoelectrics. In this study, a tetragonal phase is identified based on a combination of x-ray diffraction, scanning transmission electronic microscopy, x-ray absorption spectroscopy, and Raman spectroscopy when BFO is grown on yttria-stabilized zirconia (YSZ) substrates. To distinguish the discrepancy between this tetragonal phase and common cases of monoclinic BFO, piezoelectric force microscopy images and optical property are also performed. It shows a lower electrostatic energy of ferroelectric domains and a large reduction of band gap for BFO grown on YSZ substrate comparing to the well-known one grown on LaAlO{sub 3} substrate. Our findings in this work can provide more insights to understand the structural diversity of multiferroic BFO system for further applications.

  14. Gel combustion synthesis of yttria stabilized zirconia

    International Nuclear Information System (INIS)

    Vijay, Soja K.; Chandramouli, V.; Anthonysamy, S.

    2013-01-01

    Nano - crystalline 8 mol% yttria stabilized zirconia (YSZ) powders were synthesized by gel combustion technique employing both microwave heating as well as conventional heating method. Three different fuels - citric acid, urea and glycine were used for the synthesis with fuel to oxidant ratio as 1:1. The effect of fuel on the crystal structure, particle size, specific surface area, morphology and sintering density was studied. X-ray powder diffraction (XRD), BET gas adsorption technique, dynamic light scattering, transmission and scanning electron microscopy (TEM and SEM) and micro-Raman spectroscopy were used to characterize the powders. The results obtained for powders obtained using both methods - microwave assisted and hotplate - were compared. The specific surface area of powders in all cases are comparable except in the case of urea as fuel where microwave assisted synthesis yielded powders with lower surface area. The particle size distribution of all samples obtained using microwave method was unimodal, whereas the particle size distribution of samples prepared using hot plate method using urea fuel showed bimodal distribution. The compacts obtained using powders with citric acid and glycine as fuel showed more than 94% theoretical density, whereas the samples obtained using urea showed density below 90% of theoretical density. (author)

  15. Modern trends in engineering ceramics: review of transformation toughening in zirconia based ceramics

    International Nuclear Information System (INIS)

    Khan, A.A.

    1998-01-01

    The investigation of zirconia has continued to attract the interest of ever increasing number of scientists and solid evidence of commercial applications for the engineering ceramic is now available. To use zirconia to its full potential, the properties of the oxide have been modified extensively by the addition of cubic stabilizing oxides. These can be added in amounts sufficient to form a partially stabilized zirconia (PSZ) or to form a fully stabilized zirconia, which has a cubic structure at room temperature. The addition of varying amounts of cubic oxides, particularly MgO, CaO, Y sub 2 O sub 3, has allowed the development of novel and innovative ceramic materials. In this article an overview of the recent advances in zirconia based engineering materials is presented. It is shown that intelligent control of the composition and microstructure can lead the the production of extremely though ceramic materials, a property which is generally thought to be the major weak point of ceramics vis a vis other class of materials. (author)

  16. Study on nano-structured hydroxyapatite/zirconia stabilized yttria on healing of articular cartilage defect in rabbit

    Directory of Open Access Journals (Sweden)

    Amir Sotoudeh

    2013-05-01

    Full Text Available PURPOSE: Articular Cartilage has limited potential for self-repair and tissue engineering approaches attempt to repair articular cartilage by scaffolds. We hypothesized that the combined hydroxyapatite and zirconia stabilized yttria would enhance the quality of cartilage healing. METHODS: In ten New Zealand white rabbits bilateral full-thickness osteochondral defect, 4 mm in diameter and 3 mm depth, was created on the articular cartilage of the patellar groove of the distal femur. In group I the scaffold was implanted into the right stifle and the same defect was created in the left stifle without any transplant (group II. Specimens were harvested at 12 weeks after implantation, examined histologically for morphologic features, and stained immunohistochemically for type-II collagen. RESULTS: In group I the defect was filled with a white translucent cartilage tissue In contrast, the defects in the group II remained almost empty. In the group I, the defects were mostly filled with hyaline-like cartilage evidenced but defects in group II were filled with fibrous tissue with surface irregularities. Positive immunohistochemical staining of type-II collagen was observed in group I and it was absent in the control group. CONCLUSION: The hydroxyapatite/yttria stabilized zirconia scaffold would be an effective scaffold for cartilage tissue engineering.

  17. Influence of potassium on the competition between methane and ethane in steam reforming over Pt supported on yttrium-stabilized zirconia.

    NARCIS (Netherlands)

    Graf, P.O.; Mojet, Barbara; Lefferts, Leonardus

    2008-01-01

    effect of addition of potassium to Pt supported on yttrium-stabilized zirconia (PtYSZ) catalyst for steam reforming of methane, ethane and methane/ethane mixtures was explored. Addition of potassium has a positive effect on preferential steam reforming of methane in mixtures of methane and ethane

  18. Graphene nanosheet-induced toughening of yttria-stabilized zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Su, Jianan; Chen, Yao; Huang, Qiqi [Soochow University, School of Mechanical and Electric Engineering, Collaborative Innovation Center of Suzhou Nano Science and Technology, Suzhou (China)

    2017-01-15

    Graphene nanosheet (GNS)-reinforced yttria-stabilized tetragonal zirconia polycrystals (TZP) were synthesized using spark plasma sintering (SPS), and the influences of the added GNSs on microstructure evolution and the microscopic mechanical properties of the sintered composites were investigated. Raman spectroscopy and microstructure observation corroborated that these added GNSs, which can survive the harsh SPS processing condition, homogeneously distribute in the matrix of all composites to hinder significantly the grain growth. In comparison with the monolithic TZP, the indentation fracture toughness of a GNS/TZP composite reaches maximum value and increases by up to ∝36% (from ∝4.1 to ∝5.6 MPa m{sup 0.5}) even at 0.5% weight fraction, GNS pullout, crack bridging, crack deflection, and crack branching are responsible for the increased fracture toughness. The computed energy dissipation by GNS pullout decreases with increasing the number of graphene layers due to weak bonding between them, and therefore, graphene agglomeration would impair toughening effect. Moreover, scratch studies suggest that GNS/TZP composites exhibit improved scratch resistance due to the fact that GNSs are promising reinforcing and lubricating nanofillers in ceramic composites. (orig.)

  19. Influence of diesel engine combustion on the rupture strength of partially stabilized zirconia

    International Nuclear Information System (INIS)

    Brinkman, C.R.; Begun, G.M.; Cavin, O.B.; Foster, B.E.; Graves, R.L.; Kahl, W.K.; Liu, K.C.; Simpson, W.A.

    1989-01-01

    Results are reported for tests on partially stabilized zirconia (PSZ-TS and MS grade) bars exposed in the combustion chambers of two operating single-cylinder 0.825-L diesel engines. Specifics of test conditions and procedures are presented. Subsequent to exposure, the bars were subjected to four-point bending and the rupture strengths determined. The TS grade showed a decrease in average strength of 32%, while the strength of the MS grade decreased by about 9% in comparison to average behavior of unaged material. Results of X-ray diffraction analysis, Raman spectroscopy, isothermal aging studies, and ceramographic characterization are given to define reasons for material degradation

  20. Microscopic observation of laser glazed yttria-stabilized zirconia coatings

    Science.gov (United States)

    Morks, M. F.; Berndt, C. C.; Durandet, Y.; Brandt, M.; Wang, J.

    2010-08-01

    Thermal barrier coatings (TBCs) are frequently used as insulation system for hot components in gas-turbine, combustors and power plant industries. The corrosive gases which come from combustion of low grade fuels can penetrate into the TBCs and reach the metallic components and bond coat and cause hot corrosion and erosion damage. Glazing the top coat by laser beam is advanced approach to seal TBCs surface. The laser beam has the advantage of forming a dense thin layer composed of micrograins. Plasma-sprayed yttria-stabilized zirconia (YSZ) coating was glazed with Nd-YAG laser at different operating conditions. The surface morphologies, before and after laser treatment, were investigated by scanning electron microscopy. Laser beam assisted the densification of the surface by remelting a thin layer of the exposed surface. The laser glazing converted the rough surface of TBCs into smooth micron-size grains with size of 2-9 μm and narrow grain boundaries. The glazed surfaces showed higher Vickers hardness compared to as-sprayed coatings. The results revealed that the hardness increases as the grain size decreases.

  1. Zirconia powders production by precipitation: state-of-art review; Producao de pos de zirconia por precipitacao - revisao do estado da arte

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Ana Paula Almeida de; Torem, Mauricio Leonardo [Pontificia Univ. Catolica do Rio de Janeiro, RJ (Brazil). Dept. de Ciencia dos Materiais e Metalurgia

    1994-12-31

    The important role played by zirconia in advanced ceramics can be attributed to its excellent wear and corrosion resistance and refractory character. The polymorphic nature of zirconia made the controlled addition of stabilizing oxides or the constraining effect of a dense ceramics matrix necessary to maintain high parameters had a significant influence on powder properties and on compacted powder behaviour in sintering. Particle shape and size, purity and crystalline structure were specially influenced by precipitation parameters. Therefore, this work presented a review of the state of the art in zirconia powder production and in the recent research on precipitation of that powder. (author) 15 refs., 5 figs., 2 tabs.

  2. Zirconia toughened ceramics for heat engine applications

    International Nuclear Information System (INIS)

    Rossi, G.A.; Blum, J.B.; Manwiller, K.E.; Knapp, C.E.

    1986-01-01

    Three classes of zirconia toughened ceramics (ZTC) were studied, i.e. Mg-PSZ (MgO-partially stabilized zirconia), Y-TZP (Y/sub 2/O/sub 3/-tetragonal zirconia polycrystals) and ZTA (zirconia toughened alumina). The main objective was to improve the high temperature strength and toughness, which are not satisfactory in the ''state of the art'' ZTC materials. Powders prepared by melting/rapid solidification and by chemical routes were used. The green parts were made by both dry and wet shape forming methods. Fine grained Mg-PSZ ceramics with unique microstructures were produced using the rapidly solidified powders. The Y-TZP materials were improved mainly through microstructure control and by addition of alpha alumina as a dispersed phase. Preliminary results on ZTA ceramics made with the rapidly solidified powders were also obtained. It is concluded that the Al/sub 2/O/sub 3//Y-TZP composites offer a good chance of meeting the program objectives

  3. Synthesis and characterization of Yttria-stabilized zirconia (YSZ) thin films using spray pyrolysis technique

    International Nuclear Information System (INIS)

    Jamale, A.P.; Chourasiya, M.G.; Chavan, A.U.; Patil, S.P.; Jadhav, L.D.

    2009-01-01

    Micro solid oxide fuel cells (SOFC) are of great potential, which require components in film form. We are reporting the spray pyrolysis of 8YSZ films as solid electrolyte for micro-SOFC. The process parameters of the technique were optimized to get stoichiometric films of YSZ. The micro-structural and electrical properties of the films were studied. The elemental analysis of the film showed the desired composition in the film. The conductivity of the film was 0.05 S/cm at 500 deg C with activation energy of 0.90eV. (author)

  4. Studies on zirconia-mullite ceramic

    International Nuclear Information System (INIS)

    Virkar, Alka N.

    2014-01-01

    Zirconia Toughened Alumina (ZTA) ceramics with much improved Fracture Toughness and Strength have been used as a front material to fabricate composite Armour-Applications, Al 2 O 3 has very different fluxing ability with silica by sufficiently lowering the melting point. Addition of small amount of Fe 2 O 3 , TiO 2 , in an Al 2 O 3 -SiO 2 mixture enhances needle shaped Mullite crystal growth and also assist Liquid phase Sintering. In the present investigation, Zircon was used as a source of ZrO 2 and SiO 2 . Zircon (ZrSiO 4 ) has a low coefficient of Thermal Expansion and good Thermal Shock Resistance. Densification in terms of Relative Density and App. Porosity, Tetragonal ZrO 2 , phases, Thermal Expansion Coefficient, Hardness etc. were studied on Zirconia-Mullite system with and without additives. Z-M system with Y 2 O 3 additives show improved properties owing to the partial stabilization of Zirconia phase (PSZ). (author)

  5. Effect of boron oxide on the cubic-to-monoclinic phase transition in yttria-stabilized zirconia

    International Nuclear Information System (INIS)

    Florio, D.Z. de; Muccillo, R.

    2004-01-01

    Specimens of yttria fully stabilized zirconia with different amounts of boron oxide have been studied by X-ray diffraction at room temperature and at higher temperatures up to 1250 deg. C. A boron oxide-assisted cubic-to-monoclinic phase transformation was determined in the temperature range 800-1250 deg. C. In situ high temperature X-ray diffraction experiments gave evidences of the dependence of the phase transformation on the heating rate. The possibility of tuning the cubic-monoclinic phase ratio by suitable addition of boron oxide before pressing and sintering is proposed

  6. Partially stabilized zirconia (PSZ) - what's in it for chemical engineers?

    International Nuclear Information System (INIS)

    Michelmore, A.G.

    1988-01-01

    Partial Stabilized Zirconia (PSZ) is a non-brittle ceramic material with virtually the same modulus of elasticity, Poisson's ratio, tensile strength, and co-efficient of thermal expansion as steel, coupled with low thermal conductivity, low electrical conductivity, high hardness, non-magnetic properties and high corrosion resistance. Uses are in a wide variety of applications such as automotive, computer, hot copper extrusion dies, delicate laboratory equipment, mining spigots and injection moulding gates for plastic. Applications previously thought to be impossible for ceramics such as in high thermal and/or mechanical shock situations are now possible with benefits such as longer life, reduced maintenance costs, less downtime, lower stock inventory and improved productivity. Examples given here include downhole pump check valves in the oil and gas industry, dry bearings in the mining industry and plungers for pumping tomato paste in the food processing industry. A brief comparison is made of other PSZs and Nilcra PSZ. 1 fig

  7. Zirconia powders production by precipitation: state-of-art review

    International Nuclear Information System (INIS)

    Oliveira, Ana Paula Almeida de; Torem, Mauricio Leonardo

    1994-01-01

    The important role played by zirconia in advanced ceramics can be attributed to its excellent wear and corrosion resistance and refractory character. The polymorphic nature of zirconia made the controlled addition of stabilizing oxides or the constraining effect of a dense ceramics matrix necessary to maintain high parameters had a significant influence on powder properties and on compacted powder behaviour in sintering. Particle shape and size, purity and crystalline structure were specially influenced by precipitation parameters. Therefore, this work presented a review of the state of the art in zirconia powder production and in the recent research on precipitation of that powder. (author)

  8. Study of crystallite size of yttria-stabilized zirconia powders by Rietveld method

    International Nuclear Information System (INIS)

    Leite, Wellington Claiton; Brinatti, Andre Mauricio; Ribeiro, Mauricio Aparecido; Andrade, Andre Vitor Chaves de; Chinelatto, Adriana Scoton Antonio; Chinelatto, Adilson Luiz

    2009-01-01

    The yttria-stabilized zirconia (YSZ) is used in a great variety of applications, for example, electrolytes of solid oxide fuel cells and oxygen sensors. In the study of YSZ, the particle size powders and sintering processes are important to define the final properties of the zirconia products. The objectives of this work were to determine the phases and the crystalline size using X-Ray Diffraction (XRD) data and the Rietveld Method (RM) of the YSZ powders obtained by chemical synthesis based on the Pechini method. It was used ZrOCl 2.8 H 2 O and Y(NO 3 ) 3.5 H 2 O as precursors reagents. After calcination at 550 deg C during 24 hours, the powder was analyzed by XRD and scanning electronic microscopy (SEM). From XRD and using Rietveld method were verified that there is only cubic phase with lattice parameter a = 5.1307(1) Å and the space group Fm3m. Due to substitution of the Zr atoms in the Y atoms sites, there were vacancies in 17.72 % of O atoms sites. However, the percentage of substitution of Zr atoms in Y atoms sites in the structure not was determinate because the curves of atomic scattering of them are very similar. Using Scherrer equation and considering anisotropy effect, the average crystalline size was determinate: 10,43 nm (c axis) and 10,39 (b axis). This spherical symmetry also observed for SEM. (author)

  9. Hot Corrosion of Yttrium Stabilized Zirconia Coatings Deposited by Air Plasma Spray on a Nickel-Based Superalloy

    Science.gov (United States)

    Vallejo, N. Diaz; Sanchez, O.; Caicedo, J. C.; Aperador, W.; Zambrano, G.

    In this research, the electrochemical impedance spectroscopy (EIS) and Tafel analysis were utilized to study the hot corrosion performance at 700∘C of air plasma-sprayed (APS) yttria-stabilized zirconia (YSZ) coatings with a NiCrAlY bond coat grown by high velocity oxygen fuel spraying (HVOF), deposited on an INCONEL 625 substrate, in contact with corrosive solids salts as vanadium pentoxide V2O5 and sodium sulfate Na2SO4. The EIS data were interpreted based on proposed equivalent electrical circuits using a suitable fitting procedure performed with Echem AnalystTM Software. Phase transformations and microstructural development were examined using X-ray diffraction (XRD), with Rietveld refinement for quantitative phase analysis, scanning electron microscopy (SEM) was used to determinate the coating morphology and corrosion products. The XRD analysis indicated that the reaction between sodium vanadate (NaVO3) and yttrium oxide (Y2O3) produces yttrium vanadate (YVO4) and leads to the transformation from tetragonal to monoclinic zirconia phase.

  10. Electrical conductivity of zirconia and yttrium-doped zirconia from Indonesian local zircon as prospective material for fuel cells

    International Nuclear Information System (INIS)

    Apriany, Karima; Permadani, Ita; Rahmawati, Fitria; Syarif, Dani G.; Soepriyanto, Syoni

    2016-01-01

    In this research, zirconium dioxide, ZrO 2 , was synthesized from high-grade zircon sand that was founded from Bangka Island, Sumatra, Indonesia. The zircon sand is a side product of Tin mining plant industry. The synthesis was conducted by caustic fusion method with considering definite stoichiometric mole at every reaction step. Yttrium has been doped into the prepared zirconia by solid state reaction. The prepared materials were then being analyzed by X-ray diffraction equipped with Le Bail refinement to study its crystal structure and cell parameters. Electrical conductivity was studied through impedance measurement at a frequency range of 20 Hz- 5 MHz. Morphological analysis was conducted through Scanning Electron Microscopy (SEM) equipped with Energy Dispersive X-ray (EDX) for elemental analysis. The results show that the prepared yttrium stabilized zirconia, YSZ, was crystallized in the cubic structure with a space group of P42/NMC. The sintered zirconia and yttrium stabilized zirconia at 8 mol% of yttrium ions (8YSZ) show dense surface morphology with a grain size less than 10 pm. Elemental analysis on the sintered zirconia and 8YSZ show that sintering at 1500°C could eliminate the impurities, and the purity became 81.30%. Impedance analysis shows that ZrO 2 provide grain and grain boundary conductivity meanwhile 8YSZ only provide grain mechanism. The yttrium doping enhanced the conductivity up to 1.5 orders. The ionic conductivity of the prepared 8YSZ is categorized as a good material with conductivity reach 7.01 x10 -3 at 700 °C. The ionic conductivities are still lower than commercial 8YSZ at various temperature. It indicates that purity of raw material might significantly contribute to the electrical conductivity. (paper)

  11. Magnetoresistance and Microstructure of Magnetite Nanocrystals Dispersed in Indium−Tin Oxide Thin Films

    OpenAIRE

    Okada, Koichi; Kohiki, Shigemi; Mitome, Masanori; Tanaka, Hidekazu; Arai, Masao; Mito, Masaki; Deguchi, Hiroyuki

    2009-01-01

    Epitaxial indium−tin oxide (ITO) thin films were fabricated on a yttria-stabilized zirconia (YSZ) substrate by pulsed-laser deposition using magnetite (Fe3O4) nanoparticle dispersed ITO powders as a target. Magnetoresistance of the film at a field of 1 T was 39% at 45 K, and it stayed at 3% above 225 K. The film demonstrated cooling hysteresis in the temperature dependence of direct-current magnetization. Transmission electron microscopy revealed that phase-separated Fe3O4 nanocrystals with w...

  12. Eco friendly nitration of toluene using modified zirconia

    Directory of Open Access Journals (Sweden)

    K.R. Sunaja Devi

    2013-03-01

    Full Text Available Nitration of toluene has been studied in the liquid phase over a series of modified zirconia catalysts.  Zirconia, zirconia- ceria (Zr0.98Ce0.02O2, sulfated zirconia and sulfated zirconia- ceria were synthesised by co precipitation method and were characterised by X-ray diffraction, BET surface area, Infra red spectroscopy analysis (FTIR, Thermogravimetric analysis (TGA, Scanning Electron Microscopy (SEM and Energy Dispersive X ray analysis (EDAX. The acidity of the prepared catalysts was determined by FTIR pyridine adsorption study. X-ray diffraction studies reveal that the catalysts prepared mainly consist of tetragonal phase with the crystallite size in the nano range and the tetragonal phase of zirconia is stabilized by the addition of ceria. The modified zirconia samples have higher surface area and exhibits uniform pore size distribution aggregated by zirconia nanoparticles. The onset of sulfate decomposition was observed around 723 K for sulfated samples. The catalytic performance was determined for the liquid phase nitration of toluene to ortho-, meta- and para- nitro toluene. The effect of reaction temperature, concentration of nitric acid, catalyst reusability and reaction time was also investigated. © 2013 BCREC UNDIP. All rights reservedReceived: 20th November 2012; Revised: 8th December 2012; Accepted: 7th January 2013[How to Cite: K. R. S. Devi, S. Jayashree, (2013. Eco friendly nitration of toluene using modified zirconia. Bulletin of Chemical Reaction Engineering & Catalysis, 7 (3: 205-214. (doi:10.9767/bcrec.7.3.4154.205-214][Permalink/DOI: http://dx.doi.org/10.9767/bcrec.7.3.4154.205-214 ] View in  |

  13. Effect of nanoparticles generation method on ionic conductivity in Yttria stabilized zirconia

    International Nuclear Information System (INIS)

    Khare, J.; Joshi, M.P.; Kukreja, L.M.; Satapathy, S.

    2013-01-01

    Yttria stabilized zirconia nanoparticles were generated in pulsed and CW mode of laser operation using CO 2 laser based laser vaporization method. Impedance spectroscopic measurements were carried out in frequency range of 100 Hz - 1 MHz at various temperatures ranging from room temperature to 500 C. The deconvolution of grain and grain boundary contribution were obtained from impedance spectra by an equivalent circuit analysis. Grain and grain boundary ionic conductivity of pellet made from nanoparticles generated in pulsed mode was two orders of magnitude large in comparison to pellets made from nanoparticles generated in CW mode of laser operation. The difference in ionic conductivities of pellets made from nanoparticles generated in pulsed mode and CW mode were explained on the basis of defect associations in nanoparticles produced during nanoparticles generation. (author)

  14. Stabilized chromium oxide film

    Science.gov (United States)

    Garwin, Edward L.; Nyaiesh, Ali R.

    1988-01-01

    Stabilized air-oxidized chromium films deposited on high-power klystron ceramic windows and sleeves having a thickness between 20 and 150.ANG. are useful in lowering secondary electron emission yield and in avoiding multipactoring and window failure due to overheating. The ceramic substrate for the film is chosen from alumina, sapphire or beryllium oxide.

  15. Phase composition of yttrium-doped zirconia ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Hennig, Christoph; Scheinost, Andreas C. [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Molecular Structures; Weiss, Stephan [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Surface Processes; Ikeda-Ohno, Atsushi [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Chemistry of the F-Elements; Gumeniuk, R. [Technische Univ. Bergakademie Freiberg (Germany). Inst. fuer Experimentelle Physik

    2017-06-01

    Ceramic material might be an alternative to borosilicate glass for the immobilization of nuclear waste. The crystallinity of ceramic material increases the corrosion resistance over several magnitudes in relation to amorphous glasses. The stability of such ceramics depend on several parameters, among them the crystal phase composition. A reliable quantitative phase analysis is necessary to correlate the macroscopic material properties with structure parameters. We performed a feasibility study based on yttrium-doped zirconia ceramics as analogue for trivalent actinides to ascertain that the nanosized crystal phases in zirconia ceramics can be reliably determined.

  16. Shear bond strength of indirect composite material to monolithic zirconia.

    Science.gov (United States)

    Sari, Fatih; Secilmis, Asli; Simsek, Irfan; Ozsevik, Semih

    2016-08-01

    This study aimed to evaluate the effect of surface treatments on bond strength of indirect composite material (Tescera Indirect Composite System) to monolithic zirconia (inCoris TZI). Partially stabilized monolithic zirconia blocks were cut into with 2.0 mm thickness. Sintered zirconia specimens were divided into different surface treatment groups: no treatment (control), sandblasting, glaze layer & hydrofluoric acid application, and sandblasting + glaze layer & hydrofluoric acid application. The indirect composite material was applied to the surface of the monolithic zirconia specimens. Shear bond strength value of each specimen was evaluated after thermocycling. The fractured surface of each specimen was examined with a stereomicroscope and a scanning electron microscope to assess the failure types. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey LSD tests (α=.05). Bond strength was significantly lower in untreated specimens than in sandblasted specimens (Pcomposite material and monolithic zirconia.

  17. Deposition of yttria stabilized zirconia layer for solid oxide fuel cell by chemical vapor infiltration

    International Nuclear Information System (INIS)

    John, John T.; Dubey, Vivekanand; Kain, Vivekanand; Dey, Gautham Kumar; Prakash, Deep

    2011-01-01

    Free energy associated with a chemical reaction can be converted into electricity, if we can split the reaction into an anodic reaction and a cathodic reaction and carry out the reactions in an electrochemical cell using electrodes that will catalyze the reactions. We also have to use a suitable electrolyte, that serves to isolate the chemical species in the two compartments from getting mixed directly but allow an ion produced in one of the reactions to proceed to the other side and complete the reaction. For this reason cracks and porosity are not tolerated in the electrolyte. First generation solid oxide fuel cell (SOFC) uses yttria stabilized zirconia (YSZ) as the electrolyte. In spite of the fact that several solid electrolytes with higher conductivities at lower temperature are being investigated and developed, 8 mol% yttria stabilized zirconia (8YSZ) is considered to be the most favored electrolyte for the SOFC today. The electrolyte should be present as a thin, impervious layer of uniform thickness with good adherence, chemical and mechanical stability, in between the porous cathode and anode. Efforts to produce the 8YSZ coatings on porous lanthanum strontium manganite tubes by electrochemical vapor deposition (ECVD) have met with unexpected difficulties such as impurity pick up and chemical and mechanical instability of the LSM tubes in the ECVD environment. It was also difficult to keep the chemical composition of the YSZ coating at exactly 8 mol% Yttria in zirconia and to control the coating thickness in tight control. These problems were overcome by a two step deposition process where a YSZ layer of required thickness was produced by electrophoretic coating from an acetyl acetone bath at a voltage of 30-300V DC and sintered at 1300 deg C. The resulting porous YSZ layer was made impervious by chemical vapor infiltration (CVI) by the reaction between a mixture of vapors of YCl 3 and ZrCl 4 and steam at 1300 deg C as in the case of ECVD for a short

  18. Defect structure of yttria-stabilized zirconia and its influence on the ionic conductivity at elevated temperatures

    DEFF Research Database (Denmark)

    Goff, J.P.; Hayes, W.; Hull, S.

    1999-01-01

    The defect structure of cubic fluorite structured yttria-stabilized zirconia (ZrO2)(1-x)(Y2O3)(x) has been investigated over the composition range 0.100(3)less than or equal to x less than or equal to 0.241 (10) and temperatures T(K) up to 2780(10) K, using single-crystal specimens. Analysis of n......, we propose that the anomalous decrease in the ionic conductivity with increasing x is a consequence of the decreasing mobility of the isolated defects, possibly due to blockage by the increasing number of static aggregates....

  19. Comparison of mechanical and biological properties of zirconia and titanium alloy orthodontic micro-implants.

    Science.gov (United States)

    Choi, Hae Won; Park, Young Seok; Chung, Shin Hye; Jung, Min Ho; Moon, Won; Rhee, Sang Hoon

    2017-07-01

    The aim of this study was to compare the initial stability as insertion and removal torque and the clinical applicability of novel orthodontic zirconia micro-implants made using a powder injection molding (PIM) technique with those parameters in conventional titanium micro-implants. Sixty zirconia and 60 titanium micro-implants of similar design (diameter, 1.6 mm; length, 8.0 mm) were inserted perpendicularly in solid polyurethane foam with varying densities of 20 pounds per cubic foot (pcf), 30 pcf, and 40 pcf. Primary stability was measured as maximum insertion torque (MIT) and maximum removal torque (MRT). To investigate clinical applicability, compressive and tensile forces were recorded at 0.01, 0.02, and 0.03 mm displacement of the implants at angles of 0°, 10°, 20°, 30°, and 40°. The biocompatibility of zirconia micro-implants was assessed via an experimental animal study. There were no statistically significant differences between zirconia micro-implants and titanium alloy implants with regard to MIT, MRT, or the amount of movement in the angulated lateral displacement test. As angulation increased, the mean compressive and tensile forces required to displace both types of micro-implants increased substantially at all distances. The average bone-to-implant contact ratio of prototype zirconia micro-implants was 56.88 ± 6.72%. Zirconia micro-implants showed initial stability and clinical applicability for diverse orthodontic treatments comparable to that of titanium micro-implants under compressive and tensile forces.

  20. Optical properties and light irradiance of monolithic zirconia at variable thicknesses.

    Science.gov (United States)

    Sulaiman, Taiseer A; Abdulmajeed, Aous A; Donovan, Terrence E; Ritter, André V; Vallittu, Pekka K; Närhi, Timo O; Lassila, Lippo V

    2015-10-01

    The aims of this study were to: (1) estimate the effect of polishing on the surface gloss of monolithic zirconia, (2) measure and compare the translucency of monolithic zirconia at variable thicknesses, and (3) determine the effect of zirconia thickness on irradiance and total irradiant energy. Four monolithic partially stabilized zirconia (PSZ) brands; Prettau® (PRT, Zirkonzahn), Bruxzir® (BRX, Glidewell), Zenostar® (ZEN, Wieland), Katana® (KAT, Noritake), and one fully stabilized zirconia (FSZ); Prettau Anterior® (PRTA, Zirkonzahn) were used to fabricate specimens (n=5/subgroup) with different thicknesses (0.5, 0.7, 1.0, 1.2, 1.5, and 2.0mm). Zirconia core material ICE® Zircon (ICE, Zirkonzahn) was used as a control. Surface gloss and translucency were evaluated using a reflection spectrophotometer. Irradiance and total irradiant energy transmitted through each specimen was quantified using MARC® Resin Calibrator. All specimens were then subjected to a standardized polishing method and the surface gloss, translucency, irradiance, and total irradiant energy measurements were repeated. Statistical analysis was performed using two-way ANOVA and post-hoc Tukey's tests (pgloss was significantly affected by polishing (p<0.05), regardless of brand and thickness. Translucency values ranged from 5.65 to 20.40 before polishing and 5.10 to 19.95 after polishing. The ranking from least to highest translucent (after polish) was: BRX=ICE=PRTzirconia and the amount was brand dependent (p<0.05). Brand selection, thickness, and polishing of monolithic zirconia can affect the ultimate clinical outcome of the optical properties of zirconia restorations. FSZ is relatively more polishable and translucent than PSZ. Copyright © 2015 Academy of Dental Materials

  1. Formulation of nano-ceramic filters used in separation of heavy metals . Part II: Zirconia ceramic filters

    International Nuclear Information System (INIS)

    Khalil, T.; Labib, Sh.; Abou EI-Nour, F.H.; Abdel-Kbalik, M.

    2007-01-01

    Zirconia ceramic filters are prepared using polymeric sol-gel process. An optimization of synthesis parameters was studied to give cracked free coated nano porous film with high performance quality. Zirconia ceramic filters are characterized to select tbe optimized conditions that give tbe suitable zirconia filter used in heavy metal separation. The ceramic filters were characterized using BET method for surface measurements, mercury porosimeter for pore size distribution analysis and coating thickness measurements, SEM for microstructural studies and atomic absorption spectrophotometer (AAS) for metal analysis. The results indicated that zirconia ceramic filters. show high separation performance for cadmium, cupper, iron, manganese and lead

  2. Effect of autoclave induced low-temperature degradation on the adhesion energy between yttria-stabilized zirconia veneered with porcelain.

    Science.gov (United States)

    Li, Kai Chun; Waddell, J Neil; Prior, David J; Ting, Stephanie; Girvan, Liz; van Vuuren, Ludwig Jansen; Swain, Michael V

    2013-11-01

    To investigate the effect of autoclave induced low-temperature degradation on the adhesion energy between yttria-stabilized zirconia veneered with porcelain. The strain energy release rate using a four-point bending stable fracture test was evaluated for two different porcelains [leucite containing (VM9) and glass (Zirox) porcelain] veneered to zirconia. Prior to veneering the zirconia had been subjected to 0 (control), 1, 5, 10 and 20 autoclave cycles. The specimens were manufactured to a total bi-layer dimension of 30 mm × 8 mm × 3 mm. Subsequent scanning electron microscopy/energy dispersive spectrometry, electron backscatter diffraction and X-ray diffraction analysis were performed to identify the phase transformation and fracture behavior. The strain energy release rate for debonding of the VM9 specimens were significantly higher (pautoclave cycles lowered the strain energy release rate significantly (pautoclave cycles between 5 and 20. The monoclinic phase reverted back to tetragonal phase after undergoing conventional porcelain firing cycles. EBSD data showed significant changes of the grain size distribution between the control and autoclaved specimen (cycle 20). Increasing autoclave cycles only significantly decreased the adhesion of the VM9 layered specimens. In addition, a conventional porcelain firing schedule completely reverted the monoclinic phase back to tetragonal. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  3. Polymer Thin Film Stabilization.

    Science.gov (United States)

    Costa, A. C.; Oslanec, R.; Composto, R. J.; Vlcek, P.

    1998-03-01

    We study the dewetting dynamics of thin polystyrene (PS) films deposited on silicon oxide surfaces using optical (OM) and atomic force (AFM) microscopes. Quantitative analysis of the hole diameter as a function of annealing time at 175^oC shows that blending poly(styrene-block-methyl-methacrylate) (PS-b-PMMA) with PS acts to dramatically slow down the dewetting rate and even stops holes growth before they impinge. AFM studies show that the hole floor is smooth for a pure PS film but contains residual polymer for the blend. At 5% vol., a PS-b-PMMA with high molar mass and low PMMA is a more effective stabilizing agent than a low molar mass/high PMMA additive. The optimum copolymer concentration is 3% vol. beyond which film stability doesn't improve. Although dewetting is slowed down relative to pure PS, PS/PS-b-PMMA bilayers dewet at a faster rate than blends having the same overall additive concentration.

  4. Synthesis, mechanical properties and bioactivity of nanostructured zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Sarkar, Debasish, E-mail: dsarkar@nitrkl.ac.in; Swain, Sanjaya Kumar; Adhikari, Sangeeta; Reddy, B. Sambi; Maiti, Himadri Sekhar, E-mail: hsmaiti2009@gmail.com

    2013-08-01

    Yttria stabilized zirconia 3Y – TZP nanopowders (10–30 nm) are prepared through direct precursor calcination of mixed zirconium oxychloride and yttrium nitrate solutions at 600 °C for 2 h. Cuboid(50 × 25 × 20 mm{sup 3}) zirconia blanks are fabricated through centrifuge casting and followed by sintering at 1350 °C for 2 h. Sintered zirconia blanks exhibit 24% volume shrinkage and 98% relative density with average grain size of 250 nm. Vickers hardness and indented fracture toughness of sintered blanks are measured as 13.5 GPa and 3.5 MPa.m{sup 1/2}, respectively. Bioactivity of nanostructured zirconia originates after four weeks incubation in simulated body fluid solution. An optimum time is required for the deposition of hydroxyapatite nanoparticles on stress-induced nucleation site of nanostructured zirconia. - Highlights: • A new technique has been proposed to prepare 10–30 nm 3Y – TZP nanopowders. • Cuboid zirconia blanks are fabricated through centrifuge casting. • Average grain size varies from 100 to 400 nm after sintering at 1350 °C for 2 h. • Hardness and fracture toughness are found as 13.5 GPa and 3.5 MPa.m{sup 1/2}, respectively. • Nanoscale hydroxyapatite deposits on stress-induced nucleation site of ZrO{sub 2} after optimum time.

  5. Accelerated ceria–zirconia solubilization by cationic diffusion inversion at low oxygen activity

    DEFF Research Database (Denmark)

    Esposito, Vincenzo; Ni, De Wei; Marani, Debora

    2016-01-01

    Fast elemental diffusion at the Gd-doped ceria/Y-stabilized zirconia interface occurs under reducing conditions at low oxygen activity (pO2 < 10−12 atm) and high temperature (1400 °C). This effect leads to formation of thick ceria–zirconia solid solution reaction layers in the micro-range vs. thi...

  6. Atomistic modeling of La3+ doping segregation effect on nanocrystalline yttria-stabilized zirconia.

    Science.gov (United States)

    Zhang, Shenli; Sha, Haoyan; Castro, Ricardo H R; Faller, Roland

    2018-05-16

    The effect of La3+ doping on the structure and ionic conductivity change in nanocrystalline yttria-stabilized zirconia (YSZ) was studied using a combination of Monte Carlo and molecular dynamics simulations. The simulation revealed the segregation of La3+ at eight tilt grain boundary (GB) structures and predicted an average grain boundary (GB) energy decrease of 0.25 J m-2, which is close to the experimental values reported in the literature. Cation stabilization was found to be the main reason for the GB energy decrease, and energy fluctuations near the grain boundary are smoothed out with La3+ segregation. Both dynamic and energetic analysis on the Σ13(510)/[001] GB structure revealed La3+ doping hinders O2- diffusion in the GB region, where the diffusion coefficient monotonically decreases with increasing La3+ doping concentration. The effect was attributed to the increase in the site-dependent migration barriers for O2- hopping caused by segregated La3+, which also leads to anisotropic diffusion at the GB.

  7. [In vitro evaluation of low-temperature aging effects of Y2O3 stabilized tetragonal zirconia polycrystals dental ceramics].

    Science.gov (United States)

    Yi, Yuan-fu; Liu, Hong-chen; Wang, Chen; Tian, Jie-mo; Wen, Ning

    2008-03-01

    To investigate the influence of in vitro low-temperature degradation (LTD) treatment on the structural stability of 5 kinds of Y2O3 stabilized tetragonal zirconia polycrystals (Y-TZP) dental ceramics. TZ-3YS powder was compacted at 200 MPa using cold isostatic pressure and pre-sintered at 1050 degrees C for 2 h forming presintered blocks. Specimens were sectioned into 15 mm x 15 mm x 1.5 mm slices from blocks of TZ-3YS, Vita In-Ceram YZ, Ivoclar, Cercon Smart, and Kavo Y-TZP presintered blocks, 18 slices for each brand, and then densely sintered. Specimens were divided into 6 groups and subjected to an accelerated aging test carried out in an autoclave in steam at 134 degrees C, 0.2 MPa, for 0, 1, 2, 3, 4, and 5 h. X-ray diffraction (XRD) was used to identify crystal phases and relative content of monoclinic phase was calculated. Specimens for three-point bending test were fabricated using TZ-3YS ceramics according to the ISO 6872 standard and bending strength was tested before and after aging. The polished and aging specimens of TZ-3YS and Cercon Smart zirconia ceramics were observed by atomic force microscopy (AFM) to evaluate surface microstructure. Tetragonal-to-monoclinic phase transformation was detected for specimens of TZ-3YS, Vita In-Ceram YZ, Ivoclar, and Kavo zirconia ceramics except for Cercon Smart ceramics after aging, and the relative content of monoclinic phase was increasing with the prolonged aging time. TZ-3YS was the most affected material, Kavo took the second, and Vita and Ivoclar were similar. Aging had no significant negative effects on flexural strength of TZ-3YS with average bending strength being over 1100 MPa. The nucleation and growth of monoclinic phase were detected by AFM in surface of Cercon Smart zirconia in which monoclinic phase was not detected by XRD. The results suggest that LTD of dental Y-TZP is time dependent, but the aging test does not reduce the flexural strength of TZ-3YS. The long-term clinical serviceability of dental

  8. The role of target-to-substrate distance on the DC magnetron sputtered zirconia thin films' bioactivity

    Energy Technology Data Exchange (ETDEWEB)

    Thaveedeetrakul, Arisara [Department of Chemical Engineering, King Mongkut' s University of Technology Thonburi, Bangkok (Thailand); Witit-anun, Nirun [Department of Physics, Burapha University, Chon Buri (Thailand); Thailand Center of Excellence in Physics, CHE, Ministry of Education, Bangkok (Thailand); Boonamnuayvitaya, Virote, E-mail: virote.boo@kmutt.ac.th [Department of Chemical Engineering, King Mongkut' s University of Technology Thonburi, Bangkok (Thailand)

    2012-01-15

    Zirconium dioxide thin films were deposited on 316L-stainless steel type substrates using DC unbalanced magnetron sputtering. The process parameter of this work was the target-to-substrate distance (d{sub t-s}), which was varied from 60 to 120 mm. The crystal structure and surface topography of zirconium dioxide thin films were characterized by X-ray diffraction (XRD) and atomic force microscopy (AFM). The results demonstrate that all of the ZrO{sub 2} thin films are composed monoclinic phase. The film sputtered at short d{sub t-s} (60 mm) shows a rather heterogeneous, uneven surface. The grain size, roughness, and thickness of thin films were decreased by increasing d{sub t-s}. The bioactivity was assessed by investigating the formation of hydroxyapatite (Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2}) on the thin film surface soaked in simulated body fluids (SBF) for 7 days. XRD and scanning electron microscopy (SEM) were used to verify the formation of apatite layers on the samples. Bone-like apatites were formed on the surface of the ZrO{sub 2} thin film in SBF immersion experiments. A nanocrystalline hydroxyapatite (HA) with a particle size of 2-4 {mu}m was deposited. Higher crystallinity of HA on the surface was observed when the distance d{sub t-s} increased to more than 80 mm. Therefore, it seems that a d{sub t-s} greater than 80 mm is an important sputtering condition for inducing HA on the zirconia film.

  9. Structural investigations of zirconia powders obtained by hf-plasmochemical denitration

    International Nuclear Information System (INIS)

    Dedov, N.V.; Ivanov, Yu.F.; Dorda, F.A.; Paul', A.V.; Zav'yalov, A.V.; Koneva, N.A.; Korobtsev, V.P.; Kutyavin, E.M.; Mazin, V.I.; Matyukha, V.A.

    1992-01-01

    Results are presented of structural and physicochemical investigations of unstabilized and stabilized (using yttria, magnesia, calcium oxide and alumina) zirconia, obtained from nitrate solutions on pilot HF-plasmochemical equipment with an electric rating of 63 kW. The phase composition of the ultradispersed powder is shown. Morphological and grain-size analyses were carried out on the EM-125K electron diffraction microscope. specimens were prepared by applying powder to a carbon film obtained in a VUP-4 vacuum cell. The phase composition was studied by x-ray analysis on the DRON-3 diffractometer. These studies established that the main morphological constituents of the ZrO 2 powder are polycrystalline hollow spheres and fragments of films. The average sizes (diameter) of the spheres in 0.77 μ (mean square deviation σ n = 0.57μ) and for the grains in them 31 nm (σ n = 9.5 nm). There exists a certain correlation between the dimensions of the polycrystalline spheres and their grain structure - the coarser the powders, the larger the grains observed

  10. Influence of starting precursors and synthesis methods on the physiochemical properties of zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Gaydhankar, T.R., E-mail: tr.gaydhankar@ncl.res.in [Catalysis Division, National Chemical Laboratory, Pune 411008 (India); Jha, R.K. [Catalysis Division, National Chemical Laboratory, Pune 411008 (India); Nikalje, M.D. [Department of Chemistry, University of Pune, Pune 411 007 (India); Waghmare, K.J. [Catalysis Division, National Chemical Laboratory, Pune 411008 (India)

    2014-07-01

    Graphical abstract: Crystallite size of tetragonal phase of the zirconia samples prepared using different synthesis parameters and precursors as a function of calcination temperature. Surface area values of the zirconia samples calcined at 500 and 700 °C are in given brackets. - Highlights: • Zirconia prepared with modified sol–gel method is less stable compared with zirconia prepared by precipitation method. • Optimized synthesis conditions shifted the glow exotherm to higher temperature range indicating better thermal stability. • Tetragonal-zirconia could be synthesized in cost-effective manner using zirconium oxy-nitrate. • In our studies no co-relation between the surface area and crystallite size was observed. - Abstract: Under identical and judiciously pre-optimized synthesis conditions, the influence of different combinations of zirconium sources and/or post treatment conditions on structural properties, thermal stability, phase composition and morphology of zirconia has been investigated. High surface area tetragonal zirconia could be synthesized in a cost-effective manner from 1 M solution of zirconium oxy-nitrate at pH 11 using aqueous ammonia solution as a precipitant when calcined at 400 °C for 3 h. Irrespective of the preparation method, pH and starting precursor, zirconia samples prepared without digestion contained dominant monoclinic phase with some traces of tetragonal phase when calcined at 700 °C. Even though there is linear decrease in surface area with increase in the crystallite size for each sample as a function of calcination temperature, no co-relation between the surface area and crystallite size could be achieved. SEM images show agglomerated and irregular shape particles between 10 to 20 μm.

  11. Spatially resolved Raman spectroscopy study of transformed zones in magnesia-partially-stabilized zirconia

    International Nuclear Information System (INIS)

    Davskardt, R.H.; Veirs, D.K.; Ritchie, R.O.

    1989-01-01

    Raman vibrational spectroscopy provides an effective phase characterization technique in materials systems containing particle dispersions of the tetragonal and monoclinic polymorphs of zirconia, each of which yields a unique Raman spectrum. An investigation is reported to assess a novel, spatially resolved Raman spectroscopy system in the study of transformed zones surrounding cracks in partially stabilized MgO-ZrO 2 (PSZ). The experimental arrangement uses an imaging (two-dimensional) photomultiplier tube to produce a one-dimensional Raman profile of phase compositions along a slitlike laser beam without translation of either the sample or the laser beam and without scanning the spectrometer. Results from phase characterization studies of the size, frontal morphology, and extent of transformation of transformation zones surrounding cracks produced under monotonic and cyclic loading conditions are presented

  12. The effect of Al intermediate layer on thermal resistance of EB-PVD yttria-stabilized zirconia coatings on titanium substrate

    Science.gov (United States)

    Panin, Alexey; Panin, Victor; Kazachenok, Marina; Shugurov, Artur; Sinyakova, Elena; Martynov, Sergey; Rusyaev, Andrey; Kasterov, Artur

    2017-12-01

    The yttria-stabilized zirconia coatings sprayed on titanium substrates by the electron beam physical vapor deposition were subjected to thermal annealing in air at 1000°C for 1, 30 and 60 min. The delamination and fracture of the coatings are studied by the scanning electron microscopy and X-ray diffraction. It is shown that a magnetron sputtered Al interlayer between the coating and the substrate considerably improves the thermal resistance of ceramic coatings.

  13. Microstructure-electrical properties relation of zirconia based ceramic composites

    International Nuclear Information System (INIS)

    Fonseca, Fabio Coral

    2001-01-01

    The electrical properties of zirconia based ceramic composites were studied by impedance spectroscopy. Three materials were prepared with different relative compositions of the conducting and insulating phases: (ZrO 2 :8 mol% Y 2 ) 3 ) + MgO, (ZrO 2 :8 mol% Y 2 O 3 ) + Y 2 O 3 and ZrO 2 + 8 mol% Y 2 O 3 . All specimens were analyzed by X-ray diffraction and scanning electron microscopy for microstructural characterization and for correlation of microstructural aspects with electrical properties. For (ZrO 2 :8 mol% Y 2 O 3 ) + MgO the main results show that the dependence of the different (microstructural constituents) contributions to the electrical resistivity on the magnesia content follows two stages: one below and another above the solubility limit of magnesia in Yttria-stabilized zirconia. The same dependence is found for the lattice parameter determined by X-ray diffraction measurements. The impedance diagrams of the composites have been resolved allowing the identification of contributions due to the presence of each microstructural constituent in both stages. Magnesia as a second phase is found to inhibit grain growth in Yttria-stabilized zirconia and the solubility limit for magnesia in the zirconia matrix is around 10 mol%. For (ZrO 2 :8 mol% Y 2 O 3 ) + Y 2 O 3 the main results show that: Yttria is present as a second phase for 1350 deg C /0.1 h sintering; the addition of 2 mol% of Yttria does not modify significantly the electrical properties; the solubility limit for Yttria is around 2 mol% according to electrical measurements. Similarly to magnesia, Yttria inhibits grain growth on Yttria-stabilized zirconia. The general effective medium theory was used to analyze the percolation of the insulating phase; the percolation threshold is different if one considers separately the total, bulk and grain boundary contributions to the electrical conductivity: 32.0, 38.5 and 27.8 vol% for total, intra and intergranular contributions, respectively. The increase of

  14. Thermo-stimulated luminescence of ion-irradiated yttria-stabilized zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Costantini, Jean-Marc [CEA, DMN, SRMA, 91191 Gif-sur Yvette Cedex (France); Beuneu, Francois [LSI, CEA-CNRS-Ecole Polytechnique, 91128 Palaiseau Cedex (France); Fasoli, Mauro; Galli, Anna; Vedda, Anna; Martini, Marco, E-mail: jean-marc.costantini@cea.fr [CNR-IFN (Italy)

    2011-03-23

    Yttria-stabilized zirconia (ZrO{sub 2}:Y{sup 3+}) single crystals (with 9.5 mol% Y{sub 2}O{sub 3}) were irradiated with ions (from 1 MeV He to 2.6 GeV U). Electron paramagnetic resonance (EPR) data show that two kinds of colour centres (F{sup +}-type and T centres) are produced. Thermo-stimulated luminescence (TSL) data exhibit a quite strong peak at {approx} 500-550 K in the glow curves of all irradiated samples regardless of the ion species and energy. Moreover, the 3D-TSL measurements reveal that this peak is correlated with a light emission at a wavelength of {approx} 620 nm (i.e. photon energy {approx} 2 eV). The TSL peak maximum temperatures are consistent with characteristic temperatures of about 500 K of annealing stages of colour centres. However, the trap-depth energies (ranging between 0.7 and 1.4 eV) deduced from the initial rise of partially cleaned TSL peaks, or from a rough approximation using Urbach's formula, are rather larger than the activation energies for defect recovery, ranging between 0.3 and 0.7 eV, as deduced from the EPR data. The processes involved in TSL are discussed in relation to available photoluminescence and defect energy-level data.

  15. Suspensions Plasma Spraying of Ceramics with Hybrid Water-Stabilized Plasma Technology

    Czech Academy of Sciences Publication Activity Database

    Mušálek, Radek; Medřický, Jan; Tesař, T.; Kotlan, Jiří; Pala, Zdeněk; Lukáč, František; Chráska, Tomáš; Curry, N.

    2017-01-01

    Roč. 26, 1-2 (2017), s. 37-46 ISSN 1059-9630. [ISTC 2016: International Thermal Spray Conference. Shanghai, 10.05.2016-12.05.2016] R&D Projects: GA ČR GA15-12145S Institutional support: RVO:61389021 Keywords : alumina * ceramics * dense * hybrid plasma torch * suspension plasma spraying * water-stabilized plasma * yttria-stabilized zirconia (YSZ) Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films Impact factor: 1.488, year: 2016 http://link.springer.com/article/10.1007/s11666-016-0493-6

  16. Catalytic Activity Enhancement for Oxygen Reduction on Epitaxial Perovskite Thin Films for Solid-Oxide Fuel Cells

    KAUST Repository

    la O', Gerardo Jose; Ahn, Sung-Jin; Crumlin, Ethan; Orikasa, Yuki; Biegalski, Michael D.; Christen, Hans M.; Shao-Horn, Yang

    2010-01-01

    Figure Presented The active ingredient: La0.8Sr 0.2CoO3-δ (LSC) epitaxial thin films are prepared on (001 )-oriented yttria-stabilized zirconia (YSZ) single crystals with a gadolinium-doped ceria (GDC) buffer layer (see picture). The LSC epitaxial films exhibit better oxygen reduction kinetics than bulk LSC. The enhanced activity is attributed in part to higher oxygen nonstoichiometry. © 2010 Wiley-VCH Verlag GmbH & Co. KCaA, Weinheim.

  17. Catalytic Activity Enhancement for Oxygen Reduction on Epitaxial Perovskite Thin Films for Solid-Oxide Fuel Cells

    KAUST Repository

    la O', Gerardo Jose

    2010-06-22

    Figure Presented The active ingredient: La0.8Sr 0.2CoO3-δ (LSC) epitaxial thin films are prepared on (001 )-oriented yttria-stabilized zirconia (YSZ) single crystals with a gadolinium-doped ceria (GDC) buffer layer (see picture). The LSC epitaxial films exhibit better oxygen reduction kinetics than bulk LSC. The enhanced activity is attributed in part to higher oxygen nonstoichiometry. © 2010 Wiley-VCH Verlag GmbH & Co. KCaA, Weinheim.

  18. Hydrogen oxidation mechanisms on Ni/yttria stabilized zirconia anodes: Separation of reaction pathways by geometry variation of pattern electrodes

    Science.gov (United States)

    Doppler, M. C.; Fleig, J.; Bram, M.; Opitz, A. K.

    2018-03-01

    Nickel/yttria stabilized zirconia (YSZ) electrodes are affecting the overall performance of solid oxide fuel cells (SOFCs) in general and strongly contribute to the cell resistance in case of novel metal supported SOFCs in particular. The electrochemical fuel conversion mechanisms in these electrodes are, however, still only partly understood. In this study, micro-structured Ni thin film electrodes on YSZ with 15 different geometries are utilized to investigate reaction pathways for the hydrogen electro-oxidation at Ni/YSZ anodes. From electrodes with constant area but varying triple phase boundary (TPB) length a contribution to the electro-catalytic activity is found that does not depend on the TPB length. This additional activity could clearly be attributed to a yet unknown reaction pathway scaling with the electrode area. It is shown that this area related pathway has significantly different electrochemical behavior compared to the TPB pathway regarding its thermal activation, sulfur poisoning behavior, and H2/H2O partial pressure dependence. Moreover, possible reaction mechanisms of this reaction pathway are discussed, identifying either a pathway based on hydrogen diffusion through Ni with water release at the TPB or a path with oxygen diffusion through Ni to be a very likely explanation for the experimental results.

  19. Fabricating Pinhole-Free YSZ Sub-Microthin Films by Magnetron Sputtering for Micro-SOFCs

    Directory of Open Access Journals (Sweden)

    T. Hill

    2011-01-01

    Full Text Available Submicron thin yttria stabilized zirconia (YSZ films were prepared on a variety of substrates with different surface morphologies by magnetron sputtering followed by thermal oxidation. Pinholes were observed in the films deposited on nanoporous alumina substrates. Initial dense Y/Zr films developed nanocracks after thermal oxidation on smooth Si wafer substrates. At optimal sputtering and oxidation conditions, smooth and crack/pore-free films were achieved on Si wafer substrates. The thin YSZ films exhibited fully ionic conduction with ionic conductivities, and activation energy corroborated well with the values from commercial YSZ plates. The thin YSZ films can be utilized in Solid Oxide Fuel Cells (SOFCs for intermediate temperature operations.

  20. Corrosion resistance of ZrTi alloys with hydroxyapatite-zirconia-silver layer in simulated physiological solution containing proteins for biomaterial applications

    Energy Technology Data Exchange (ETDEWEB)

    Mareci, D., E-mail: danmareci@yahoo.com [Technical University “Gheorghe Asachi” of Iasi, Faculty of Chemical Engineering and Environmental Protection, D. Mangeron, Iasi, 700050 (Romania); Trincă, L.C. [“Ion Ionescu de la Brad” University of Agricultural Science and Veterinary Medicine, Faculty of Horticulture, Science Department, 3, Mihail Sadoveanu Alley, Iaşi, 700490 (Romania); Căilean, D. [Technical University “Gheorghe Asachi” of Iasi, Faculty of Chemical Engineering and Environmental Protection, D. Mangeron, Iasi, 700050 (Romania); Souto, R.M., E-mail: rsouto@ull.es [Department of Chemistry, Universidad de La Laguna, E-38200 La Laguna (Tenerife, Canary Islands) (Spain); Institute of Material Science and Nanotechnology, Universidad de La Laguna, E-38200 La Laguna (Tenerife, Canary Islands) (Spain)

    2016-12-15

    Highlights: • Hydroxyapatite-zirconia coated ZrTi alloys were characterized for biocompatibility. • Silver nanoparticles added for antimicrobial activity. • Electrochemical behaviour consistent with surface layer of duplex structure. • Porous coating forms on passivating oxide layer. • HA-ZrO{sub 2}-Ag coated Zr45Ti exhibits high potential for implant application. - Abstract: The degradation characteristics of hydroxyapatite-zirconia-silver films (HA-ZrO{sub 2}-Ag) coatings on three ZrTi alloys were investigated in Ringer’s solution containing 10% human albumin protein at 37 °C. Samples were immersed for 7 days while monitored by electrochemical impedance spectroscopy (EIS) and linear potentiodynamic polarization (LPP). The electrochemical analysis in combination with surface analytical characterization by scanning electron microscopy (SEM/EDX) reveals the stability and corrosion resistance of the HA-ZrO{sub 2}-Ag coated ZrTi alloys. The characteristic feature that describes the electrochemical behaviour of the coated alloys is the coexistence of large areas of the coating presenting pores in which the ZrTi alloy substrate is exposed to the simulated physiological environment. The EIS interpretation of results was thus performed using a two-layer model of the surface film. The blocking effect in the presence the human albumin protein produces an enhancement of the corrosion resistance. The results disclose that the Zr45Ti alloy is a promising material for biomedical devices, since electrochemical stability is directly associated to biocompatibility.

  1. Superconducting films of YBaCuO

    International Nuclear Information System (INIS)

    Coelho, A.L.

    1991-01-01

    Thick films of YBa 2 Cu 3 O 7 - x have been prepared on alumina and YSZ (Yttria-stabilized zirconia) substrates by the screen printing technique. Several experimental conditions have been studied, for instance: sintering time, temperature, thickness and atmosphere annealed. The resulting films have been characterized by X-ray diffraction, AC electrical resistance, AC susceptibility and scanning electron microscopy. The surface and cross-section have been observed with an optical microscope. The X-ray diffraction patterns have been compared with a typical pattern and that has indicated the good quality of the samples. AC resistance and its temperature dependence have been measured in the standard four-probe configuration. Films thickness has been estimated in the scanning electron microscope. This technique has been suitable for production of high T c superconducting films being a simple and inexpensive method. (author)

  2. Zirconia-based colors for ceramic glazes

    International Nuclear Information System (INIS)

    Eppler, R.A.

    1977-01-01

    The history of color development for use in ceramic glazes is outlined. The most significant modern development is based on zirconia and zircon. These materials have gained increasing acceptance in the industry since their introduction in the late 1950's and early 1960's, due to their superior stability during firing of the glaze

  3. Application of the electrophoretic deposition technique for obtaining Yttria-stabilized zirconia tubes; Aplicacao da tecnica de deposicao eletroforetica para a obtencao de tubos ceramicos de zirconia-itria

    Energy Technology Data Exchange (ETDEWEB)

    Caproni, E.; Muccillo, R., E-mail: ecaproni@gmail.com, E-mail: muccillo@usp.br [Centro de Ciencia e Tecnologia de Materiais, Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2012-01-15

    The electrophoretic deposition (EPD) is recognized as the most versatile technique for processing particulate materials, due to low cost, deposition in minutes and forming of pieces with complex geometry shapes. In this work an experimental setup for the simultaneous conformation of 16 ceramic tubes by EPD was built. Bimodal submicron Yttria-stabilized zirconia particles were deposited into graphite electrodes, after suitably adjusting the rheological characteristics of the suspension in isopropanol. After graphite burning and YSZ sintering at 1500 deg C, the ceramic tubes were characterized by X-ray diffraction, scanning probe microscope, impedance spectroscopy and electrical response as a function of oxygen content. Small dense one end-closed ceramic tubes, fully stabilized in the cubic phase, were successfully obtained by the EPD technique, showing the ability of that technique for processing large quantities of tubular solid electrolytes with electrical response to different amounts of oxygen according to the Nernst law (author)

  4. Bond strength and Raman analysis of the zirconia-feldspathic porcelain interface.

    Science.gov (United States)

    Ramos, Carla Müller; Cesar, Paulo Francisco; Lia Mondelli, Rafael Francisco; Tabata, Americo Sheitiro; de Souza Santos, Juliete; Sanches Borges, Ana Flávia

    2014-10-01

    Zirconia has the best mechanical properties of the available ceramic systems. However, the stability of the zirconia-feldspathic porcelain interface may be jeopardized by the presence of the chipping and debonding of the feldspathic porcelain. The purpose of this study is to evaluate the shear bond strength of 3 cold isostatic pressed zirconia materials and a feldspathic veneer by analyzing their interface with micro-Raman spectroscopy. The test groups were experimental zirconia, Zirkonzahn zirconia, and Schuetz zirconia. Blocks of partially sintered zirconia were cut into disks (n=20) and then veneered with a feldspathic porcelain. Half of the specimens from each group (n=10) were incubated in 37°C water for 24 hours, and the other half were thermocycled. All the specimens were then subjected to shear testing. The fractured areas were analyzed with optical stereomicroscopy and classified as adhesive, cohesive, or an adhesive-cohesive failure. Spectral patterns were examined to detect bands related to the zirconia and feldspathic porcelain phases. The shear strength data were submitted to 2-way ANOVA. No significant differences in shear bond strength were observed among the 3 groups, regardless of whether or not the specimens were thermocycled. Adhesive failures were the most prevalent types of failure (70%). Raman spectra were clearly distinguished for all the materials, which showed the presence of tetragonal and monoclinic phases. The controlled production of the experimental zirconia did not influence the results of the bond strength. Raman analysis suggested a process of interdiffusion by the presence of peaks associated with the zirconia and feldspathic ceramics. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  5. SiC fiber and yttria-stabilized zirconia composite thick thermal barrier coatings fabricated by plasma spray

    Science.gov (United States)

    Ma, Rongbin; Cheng, Xudong; Ye, Weiping

    2015-12-01

    Approximately 4 mm-thick SiC fiber/yttria-stabilized zirconia (YSZ) composite thermal barrier coatings (TBCs) were prepared by atmospheric plasma spray (APS). The composite coatings have a 'reinforced concrete frame structure', which can protect the coating from failure caused by increasing thickness of coating. The SiC fiber plays an important role in reducing the residual stress level of the composite coatings. The thermal conductivity (TC) value of the composite coatings is 0.632 W/m K, which is about 50% reduction compared to that of typical APS YSZ TBCs. And the composite coatings have higher fracture toughness and better thermal shock resistance than the YSZ TBCs.

  6. Polarity control and growth mode of InN on yttria-stabilized zirconia (111) surfaces

    International Nuclear Information System (INIS)

    Kobayashi, Atsushi; Okubo, Kana; Ohta, Jitsuo; Oshima, Masaharu; Fujioka, Hiroshi

    2012-01-01

    We have found that polarity of epitaxial InN layers has been controlled by choice of a capping material during high-temperature annealing of yttria-stabilized zirconia (YSZ) (111) substrates in air. Angle-resolved X-ray photoelectron spectroscopy has revealed that the amount of segregation of Y atoms to the YSZ surface depended on the capping material of the substrates. In-polar and N-polar InN have been reproducibly grown on Y-segregated and Y-segregation-free YSZ surfaces, respectively. We have also found that the growth of the first monolayer (ML) of N-polar InN proceeds in a step-flow mode which then switches to layer-by-layer mode after the coverage by 1-ML-thick InN. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  7. Effects of artificial aging conditions on yttria-stabilized zirconia implant abutments.

    Science.gov (United States)

    Basílio, Mariana de Almeida; Cardoso, Kátia Vieira; Antonio, Selma Gutierrez; Rizkalla, Amin Sami; Santos Junior, Gildo Coelho; Arioli Filho, João Neudenir

    2016-08-01

    Most ceramic abutments are fabricated from yttria-stabilized tetragonal zirconia (Y-TZP). However, Y-TZP undergoes hydrothermal degradation, a process that is not well understood. The purpose of this in vitro study was to assess the effects of artificial aging conditions on the fracture load, phase stability, and surface microstructure of a Y-TZP abutment. Thirty-two prefabricated Y-TZP abutments were screwed and tightened down to external hexagon implants and divided into 4 groups (n = 8): C, control; MC, mechanical cycling (1×10(6) cycles; 10 Hz); AUT, autoclaving (134°C; 5 hours; 0.2 MPa); and TC, thermal cycling (10(4) cycles; 5°/55°C). A single-load-to-fracture test was performed at a crosshead speed of 0.5 mm/min to assess the assembly's resistance to fracture (ISO Norm 14801). X-ray diffraction (XRD) analysis was applied to observe and quantify the tetragonal-monoclinic (t-m) phase transformation. Representative abutments were examined with high-resolution scanning electron microscopy (SEM) to observe the surface characteristics of the abutments. Load-to-fracture test results (N) were compared by ANOVA and Tukey test (α=.05). XRD measurements revealed the monoclinic phase in some abutments after each aging condition. All the aging conditions reduced the fracture load significantly (Paging conditions. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  8. Y-Ba-Cu-O superconducting thin films by simultaneous or sequential evaporation

    International Nuclear Information System (INIS)

    Mogro-Campero, A.; Hunt, B.D.; Turner, L.G.; Burrell, M.C.; Balz, W.E.

    1988-01-01

    Superconducting thin films of Y-Ba-Cu-O near the 1:2:3 stoichiometry were produced by simultaneous (coevaporation) and sequential (multilayer) evaporation in the same evaporator. The best film obtained on yttria-stabilized zirconia (YSZ) had a superconducting onset temperature of 104 K, a midpoint T/sub c/ of 92 K, and zero resistance at T≤74 K. Stoichiometry was deduced by inductively coupled plasma emission spectroscopy, and elemental depth profiles were obtained by x-ray photoelectron spectroscopy. Film stoichiometry changes only near the film/substrate boundary for films on YSZ. Films on Si/SiO 2 were not superconducting; depth profiling shows severe changes of film composition with depth. A major theme of this work is process reproducibility, which was found to be poor for coevaporation but improved considerably for sequential evaporation

  9. Microbial adhesion on novel yttria-stabilized tetragonal zirconia (Y-TZP) implant surfaces with nitrogen-doped hydrogenated amorphous carbon (a-C:H:N) coatings.

    Science.gov (United States)

    Schienle, Stefanie; Al-Ahmad, Ali; Kohal, Ralf Joachim; Bernsmann, Falk; Adolfsson, Erik; Montanaro, Laura; Palmero, Paola; Fürderer, Tobias; Chevalier, Jérôme; Hellwig, Elmar; Karygianni, Lamprini

    2016-09-01

    Biomaterial surfaces are at high risk for initial microbial colonization, persistence, and concomitant infection. The rationale of this study was to assess the initial adhesion on novel implant surfaces of Enterococcus faecalis, Staphylococcus aureus, Escherichia coli, Pseudomonas aeruginosa, and Candida albicans upon incubation. The tested samples were 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) samples with nitrogen-doped hydrogenated amorphous carbon (a-C:H:N) coating (A) and 3Y-TZP samples coated with ceria-stabilized zirconia-based (Ce-TZP) composite and a-C:H:N (B). Uncoated 3Y-TZP samples (C) and bovine enamel slabs (BES) served as controls. Once the surface was characterized, the adherent microorganisms were quantified by estimating the colony-forming units (CFUs). Microbial vitality was assessed by live/dead staining, and microbial-biomaterial surface topography was visualized by scanning electron microscopy (SEM). Overall, A and B presented the lowest CFU values for all microorganisms, while C sheltered significantly less E. faecalis, P. aeruginosa, and C. albicans than BES. Compared to the controls, B demonstrated the lowest vitality values for E. coli (54.12 %) and C. albicans (67.99 %). Interestingly, A (29.24 %) exhibited higher eradication rates for S. aureus than B (13.95 %). Within the limitations of this study, a-C:H:N-coated 3Y-TZP surfaces tended to harbor less initially adherent microorganisms and selectively interfered with their vitality. This could enable further investigation of the new multi-functional zirconia surfaces to confirm their favorable antimicrobial properties in vivo.

  10. Pulsed laser deposition of YBCO films on ISD MgO buffered metal tapes

    CERN Document Server

    Ma, B; Koritala, R E; Fisher, B L; Markowitz, A R; Erck, R A; Baurceanu, R; Dorris, S E; Miller, D J; Balachandran, U

    2003-01-01

    Biaxially textured magnesium oxide (MgO) films deposited by inclined-substrate deposition (ISD) are desirable for rapid production of high-quality template layers for YBCO-coated conductors. High-quality YBCO films were grown on ISD MgO buffered metallic substrates by pulsed laser deposition (PLD). Columnar grains with a roof-tile surface structure were observed in the ISD MgO films. X-ray pole figure analysis revealed that the (002) planes of the ISD MgO films are tilted at an angle from the substrate normal. A small full-width at half maximum (FWHM) of approx 9deg was observed in the phi-scan for ISD MgO films deposited at an inclination angle of 55deg . In-plane texture in the ISD MgO films developed in the first approx 0.5 mu m from the substrate surface, and then stabilized with further increases in film thickness. Yttria-stabilized zirconia and ceria buffer layers were deposited on the ISD MgO grown on metallic substrates prior to the deposition of YBCO by PLD. YBCO films with the c-axis parallel to the...

  11. Effect of metal chloride solutions on coloration and biaxial flexural strength of yttria-stabilized zirconia

    Science.gov (United States)

    Oh, Gye-Jeong; Lee, Kwangmin; Lee, Doh-Jae; Lim, Hyun-Pil; Yun, Kwi-Dug; Ban, Jae-Sam; Lee, Kyung-Ku; Fisher, John G.; Park, Sang-Won

    2012-10-01

    The effect of three kinds of transition metal dopants on the color and biaxial flexural strength of zirconia ceramics for dental applications was evaluated. Presintered zirconia discs were colored through immersion in aqueous chromium, molybdenum and vanadium chloride solutions and then sintered at 1450 °C. The color of the doped specimens was measured using a digital spectrophotometer. For biaxial flexural strength measurements, specimens infiltrated with 0.3 wt% of each aqueous chloride solution were used. Uncolored discs were used as a control. Zirconia specimens infiltrated with chromium, molybdenum and vanadium chloride solutions were dark brown, light yellow and dark yellow, respectively. CIE L*, a*, and b* values of all the chromium-doped specimens and the specimens infiltrated with 0.1 wt% molybdenum chloride solution were in the range of values for natural teeth. The biaxial flexural strengths of the three kinds of metal chloride groups were similar to the uncolored group. These results suggest that chromium and molybdenum dopants can be used as colorants to fabricate tooth colored zirconia ceramic restorations.

  12. Hydrothermal crystallization of zirconia and zirconia solid solutions

    International Nuclear Information System (INIS)

    Pyda, W.; Haberko, K.; Bucko, M.M.

    1991-01-01

    Zirconia as well as yttria-zirconia and calcia-zirconia solid-solution powders were crystallized under hydrothermal conditions from (co)precipitated hydroxides. The morphology of the power particles is strongly dependent on the crystallization conditions. The powders crystallized in a water solution of Na, K, and Li hydroxides show elongated particles of much larger sizes than those which result from the process carried out in pure water or a water solution of Na, K, or Li chlorides. The shapes of the latter particles are isometric. In this paper the growth mechanism of the elongated particles is suggested

  13. Long-time aging in 3 mol.% yttria-stabilized tetragonal zirconia polycrystals at human body temperature.

    Science.gov (United States)

    Keuper, Melanie; Berthold, Christoph; Nickel, Klaus Georg

    2014-02-01

    We present new findings on the low-temperature degradation of yttria-stabilized zirconia at 37°C over several years and at high and low partial pressures of water. With the aid of focused ion beam cross-section confirmation studies we are able to show an extensive linear, continuous degradation without retardation, even at low temperatures and low water pressures. The characteristic layer growth and its inferred rate constant imply a lifetime of tens of years under simple tension and open the possibility of studying the longevity of these ceramics more rigorously. In addition, we show reproducibility complications of accelerated aging tests by the use of different autoclaves and possible implications for standardized procedures. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  14. Comparison of non-invasive tear film stability measurement techniques.

    Science.gov (United States)

    Wang, Michael Tm; Murphy, Paul J; Blades, Kenneth J; Craig, Jennifer P

    2018-01-01

    Measurement of tear film stability is commonly used to give an indication of tear film quality but a number of non-invasive techniques exists within the clinical setting. This study sought to compare three non-invasive tear film stability measurement techniques: instrument-mounted wide-field white light clinical interferometry, instrument-mounted keratoscopy and hand-held keratoscopy. Twenty-two subjects were recruited in a prospective, randomised, masked, cross-over study. Tear film break-up or thinning time was measured non-invasively by independent experienced examiners, with each of the three devices, in a randomised order, within an hour. Significant correlation was observed between instrument-mounted interferometric and keratoscopic measurements (p 0.05). Tear film stability values obtained from the hand-held device were significantly shorter and demonstrated narrower spread than the other two instruments (all p 0.05). Good clinical agreement exists between the instrument-mounted interferometric and keratoscopic measurements but not between the hand-held device and either of the instrument-mounted techniques. The results highlight the importance of specifying the instrument employed to record non-invasive tear film stability. © 2017 Optometry Australia.

  15. Exponential temperature dependence of the critical transport current in Y-Ba-Cu-O thin films

    International Nuclear Information System (INIS)

    Yom, S.S.; Hahn, T.S.; Kim, Y.H.; Chu, H.; Choi, S.S.

    1989-01-01

    We have measured the critical currents in rf-sputtered YBa 2 Cu 3 O/sub 7-x/ thin films deposited on polycrystalline yttria-stabilized zirconia substrates as a function of temperature down to 10 K. The dependence of the granular films at low temperature indicated exponential behavior which is similar to the superconductor-normal metal-superconductor (S-N-S) type tunneling junctions. For the films with a grain size of approximately 1 μm, we observed two exponential decay constants, which suggest that Josephson junctions limiting the transport critical current are possible both at the grain boundaries and at twin boundaries

  16. Chemical stability of soda-alumina-zirconia-silica glasses to Na, Na2S4, and S

    International Nuclear Information System (INIS)

    Bloom, S.I.; Bradley, J.; Nelson, P.A.; Roche, M.F.

    1985-01-01

    Twenty-two glasses with a broad range of compositions, spanning the quaternary soda-alumina-zirconia-silica system, have been prepared to allow characterization of the various properties of the system. The glasses were characterized by their resistivities, energies of activation for conduction, and glass transition temperatures. The glasses were screened for compositions of especially high chemical stability of static corrosion tests in Na, S, and Na 2 S 4 for 1000h at 400 0 C. Among the glasses tested, the high soda glasses showed the smallest weight change after exposure to the three media. The weight change observed was comparable to that seen in the Dow borate glass and beta'' alumina

  17. Tribological and wear behavior of yttria stabilized zirconia thermal barrier coatings on mild steel

    International Nuclear Information System (INIS)

    Farooq, M.; Pervez, A.

    2012-01-01

    The perfection of the temperature confrontation of the engine essentials can be obtained by claim of a single ceramic thermal barrier coating (TBC) or several composite layers. Engine elements protected by TBC can work safely in elevated temperature range above 1000 degree C. Continuous endeavor to increase thermal resistance of engine the elements requires, apart from laboratory investigations, also numerical study of the different engine parts. The high temperatures and stress concentrations can act as the local sources of damage initiation and defects propagation in the form of cracks. The current study focuses the development of Yttria stabilized zirconia thermal barrier coating by Thermal spray technique. Mild steel was used as a substrate and the coating was then characterized for tribological analysis followed by the optical analysis of wear tracks and found the TBC behavior more promising then steel. (author)

  18. Study of tape casting of Yttria stabilized zirconia for apply in solid oxide fuel cell

    International Nuclear Information System (INIS)

    Santana, Leonardo de Paulo

    2008-01-01

    The hydrogen economy has been risen as new option for supply the growing global demand for energy. A fuel cell is an electrochemical device able to use hydrogen as a energy source. Carbon dioxide (CO 2 ) emission is very low so it is ecologically friendly, once energy is produced by a reaction of hydrogen and oxygen. The production of energy from hydrogen fuelled devices can be done even in small unities and in a distributed way. It can bring energy for isolated communities, where traditional energy distribution systems can not be reached. A fuel cell is composed essentially of 3 components: anode, cathode and the electrolyte. In present days, there are many materials proposed for use as electrolyte in fuel cells. Among then, Yttria stabilized zirconia (YSZ) is the most studied and effectively used in solid oxide fuel cell. Tape casting technology is a cheap, simple and efficient way to cast ceramics slurries in laminates thick enough to be used as components for fuel cells. Considering theses aspects, in this work, ceramic thin film forming was studied using tape casting technology with raw materials prepared from Brazilian zircon ores. It is described in literature that ceramic slurries are generally made from powders with low surface area (often between 0,5 to 10m 2 /g), and the powders used in this study had larger surface area (often between 40 to 80m 2 /g). The use of zeta potential is indicated to study the stability of a suspension of ceramic powders. However, for suspensions with large concentration of solid, it is also necessary to determine the flow curve, because in these conditions, the double electric layer formed during the stabilization of suspensions can be compressed. In the rheological properties study, calcined ceramic powders were classified using a set of ABNT series screens and separated and retained by the de mesh 60 screen. Flow curve of suspension was determined in aqueous suspensions of these powders. For tape casting processing, a binder

  19. Towards long lasting zirconia-based composites for dental implants: Transformation induced plasticity and its consequence on ceramic reliability.

    Science.gov (United States)

    Reveron, Helen; Fornabaio, Marta; Palmero, Paola; Fürderer, Tobias; Adolfsson, Erik; Lughi, Vanni; Bonifacio, Alois; Sergo, Valter; Montanaro, Laura; Chevalier, Jérôme

    2017-01-15

    Zirconia-based composites were developed through an innovative processing route able to tune compositional and microstructural features very precisely. Fully-dense ceria-stabilized zirconia ceramics (84vol% Ce-TZP) containing equiaxed alumina (8vol%Al 2 O 3 ) and elongated strontium hexa-aluminate (8vol% SrAl 12 O 19 ) second phases were obtained by conventional sintering. This work deals with the effect of the zirconia stabilization degree (CeO 2 in the range 10.0-11.5mol%) on the transformability and mechanical properties of Ce-TZP-Al 2 O 3 -SrAl 12 O 19 materials. Vickers hardness, biaxial flexural strength and Single-edge V-notched beam tests revealed a strong influence of ceria content on the mechanical properties. Composites with 11.0mol% CeO 2 or above exhibited the classical behaviour of brittle ceramics, with no apparent plasticity and very low strain to failure. On the contrary, composites with 10.5mol% CeO 2 or less showed large transformation-induced plasticity and almost no dispersion in strength data. Materials with 10.5mol% of ceria showed the highest values in terms of biaxial bending strength (up to 1.1GPa) and fracture toughness (>10MPa√m). In these ceramics, as zirconia transformation precedes failure, the Weibull modulus was exceptionally high and reached a value of 60, which is in the range typically reported for metals. The results achieved demonstrate the high potential of using these new strong, tough and stable zirconia-based composites in structural biomedical applications. Yttria-stabilized (Y-TZP) zirconia ceramics are increasingly used for developing metal-free restorations and dental implants. Despite their success related to their excellent mechanical resistance, Y-TZP can undergo Low Temperature Degradation which could be responsible for restoration damage or even worst the failure of the implant. Current research is focusing on strategies to improve the LTD resistance of Y-TZP or to develop alternative composites with better

  20. Very low pressure plasma sprayed yttria-stabilized zirconia coating using a low-energy plasma gun

    International Nuclear Information System (INIS)

    Zhu, Lin; Zhang, Nannan; Bolot, Rodolphe; Planche, Marie-Pierre; Liao, Hanlin; Coddet, Christian

    2011-01-01

    In the present study, a more economical low-energy plasma source was used to perform a very low pressure plasma-spray (VLPPS) process. The plasma-jet properties were analyzed by means of optical emission spectroscopy (OES). Moreover, yttria-stabilized zirconia coating (YSZ) was elaborated by a F100 low-power plasma gun under working pressure of 1 mbar, and the substrate specimens were partially shadowed by a baffle-plate during plasma spraying for obtaining different coating microstructures. Based on the SEM observation, a column-like grain coating was deposited by pure vapor deposition at the shadowed region, whereas, in the unshadowed region, the coating exhibited a binary microstructure which was formed by a mixed deposition of melted particles and evaporated particles. The mechanical properties of the coating were also well under investigation. (orig.)

  1. Zirconia in biomedical applications.

    Science.gov (United States)

    Chen, Yen-Wei; Moussi, Joelle; Drury, Jeanie L; Wataha, John C

    2016-10-01

    The use of zirconia in medicine and dentistry has rapidly expanded over the past decade, driven by its advantageous physical, biological, esthetic, and corrosion properties. Zirconia orthopedic hip replacements have shown superior wear-resistance over other systems; however, risk of catastrophic fracture remains a concern. In dentistry, zirconia has been widely adopted for endosseous implants, implant abutments, and all-ceramic crowns. Because of an increasing demand for esthetically pleasing dental restorations, zirconia-based ceramic restorations have become one of the dominant restorative choices. Areas covered: This review provides an updated overview of the applications of zirconia in medicine and dentistry with a focus on dental applications. The MEDLINE electronic database (via PubMed) was searched, and relevant original and review articles from 2010 to 2016 were included. Expert commentary: Recent data suggest that zirconia performs favorably in both orthopedic and dental applications, but quality long-term clinical data remain scarce. Concerns about the effects of wear, crystalline degradation, crack propagation, and catastrophic fracture are still debated. The future of zirconia in biomedical applications will depend on the generation of these data to resolve concerns.

  2. Formation of (111) orientation-controlled ferroelectric orthorhombic HfO{sub 2} thin films from solid phase via annealing

    Energy Technology Data Exchange (ETDEWEB)

    Mimura, Takanori; Katayama, Kiliha [Department of Innovative and Engineered Materials, Tokyo Institute of Technology, Yokohama 226-8502 (Japan); Shimizu, Takao [Materials Research Center for Element Strategy, Tokyo Institute of Technology, Yokohama 226-8503 (Japan); Uchida, Hiroshi [Department of Materials and Life Sciences, Sophia University, Tokyo 102-8554 (Japan); Kiguchi, Takanori; Akama, Akihiro; Konno, Toyohiko J. [Institute for Materials Research, Tohoku University, Sendai 980-8577 (Japan); Sakata, Osami [Synchrotron X-ray Station at SPring-8 and Synchrotron X-ray Group, National Institute for Materials Science, Sayo, Hyogo 679-5148 (Japan); Funakubo, Hiroshi, E-mail: funakubo.h.aa@m.titech.ac.jp [Department of Innovative and Engineered Materials, Tokyo Institute of Technology, Yokohama 226-8502 (Japan); Materials Research Center for Element Strategy, Tokyo Institute of Technology, Yokohama 226-8503 (Japan); School of Materials and Chemical Technology, Tokyo Institute of Technology, Yokohama 226-8502 (Japan)

    2016-08-01

    0.07YO{sub 1.5}-0.93HfO{sub 2} (YHO7) films were prepared on various substrates by pulse laser deposition at room temperature and subsequent heat treatment to enable a solid phase reaction. (111)-oriented 10 wt. % Sn-doped In{sub 2}O{sub 3}(ITO)//(111) yttria-stabilized zirconia, (111)Pt/TiO{sub x}/SiO{sub 2}/(001)Si substrates, and (111)ITO/(111)Pt/TiO{sub x}/SiO{sub 2}/(001)Si substrates were employed for film growth. In this study, X-ray diffraction measurements including θ–2θ measurements, reciprocal space mappings, and pole figure measurements were used to study the films. The film on (111)ITO//(111)yttria-stabilized zirconia was an (111)-orientated epitaxial film with ferroelectric orthorhombic phase; the film on (111)ITO/(111)Pt/TiO{sub x}/SiO{sub 2}/(001)Si was an (111)-oriented uniaxial textured film with ferroelectric orthorhombic phase; and no preferred orientation was observed for the film on the (111)Pt/TiO{sub x}/SiO{sub 2}/(001)Si substrate, which does not contain ITO. Polarization–hysteresis measurements confirmed that the films on ITO covered substrates had saturated ferroelectric hysteresis loops. A remanent polarization (P{sub r}) of 9.6 and 10.8 μC/cm{sup 2} and coercive fields (E{sub c}) of 1.9 and 2.0 MV/cm were obtained for the (111)-oriented epitaxial and uniaxial textured YHO7 films, respectively. These results demonstrate that the (111)-oriented ITO bottom electrodes play a key role in controlling the orientation and ferroelectricity of the phase formation of the solid films deposited at room temperature.

  3. Oxidation of mullite-zirconia-alumina-silicon carbide composites

    International Nuclear Information System (INIS)

    Baudin, C.; Moya, J.S.

    1990-01-01

    This paper reports the isothermal oxidation of mullite-alumina-zirconia-silicon carbide composites obtained by reaction sintering studied in the temperature interval 800 degrees to 1400 degrees C. The kinetics of the oxidation process was related to the viscosity of the surface glassy layer as well as to the crystallization of the surface film. The oxidation kinetics was halted to T ≤ 1300 degrees C, presumably because of crystallization

  4. Stability of Polymer Ultrathin Films (Top-Down Approach.

    Science.gov (United States)

    Bal, Jayanta Kumar; Beuvier, Thomas; Unni, Aparna Beena; Chavez Panduro, Elvia Anabela; Vignaud, Guillaume; Delorme, Nicolas; Chebil, Mohamed Souheib; Grohens, Yves; Gibaud, Alain

    2015-08-25

    In polymer physics, the dewetting of spin-coated polystyrene ultrathin films on silicon remains mysterious. By adopting a simple top-down method based on good solvent rinsing, we are able to prepare flat polystyrene films with a controlled thickness ranging from 1.3 to 7.0 nm. Their stability was scrutinized after a classical annealing procedure above the glass transition temperature. Films were found to be stable on oxide-free silicon irrespective of film thickness, while they were unstable (2.9 nm) on 2 nm oxide-covered silicon substrates. The Lifshitz-van der Waals intermolecular theory that predicts the domains of stability as a function of the film thickness and of the substrate nature is now fully reconciled with our experimental observations. We surmise that this reconciliation is due to the good solvent rinsing procedure that removes the residual stress and/or the density variation of the polystyrene films inhibiting thermodynamically the dewetting on oxide-free silicon.

  5. Assessment of the primary stability of root analog zirconia implants designed using cone beam computed tomography software by means of the Periotest® device: An ex vivo study. A preliminary report.

    Science.gov (United States)

    Matys, Jacek; Świder, Katarzyna; Flieger, Rafał; Dominiak, Marzena

    2017-08-01

    The implant primary stability is a fundamental prerequisite for a success of osseointegration process which determines the prosthetic reconstruction time. The aim of the present study was to assess the quality and precision of modern conical bone computer tomography (CBCT) software in preparing root analog zirconia implants (RAZIs) by measuring its primary stability by means of the Periotest device. Thirteen pig jaws with proper erupted first premolar (P1) teeth were used in the study. The CBCT examination was conducted in the area of the P1 tooth in each mandible. The 3-dimensional (3D) view of each tooth was designed from CBCT scan. The created 3D images were used to prepare root analog zirconia implants milled from a medical-grade zirconia block by means of laboratory milling. The RAZIs and titanium implants were placed into an alveolar socket after the tooth had been removed. The primary stability of the teeth before their extraction (G1), RAZIs (G2) and titanium implants (G3) were checked by Periotest devices. The mean results in PTV were: 15.9, 3.35, 12.7 for G1, G2 and G3 group, respectively. RAZIs during immediate loading achieved a significantly higher primary stability (lower Periotest value) as compared to the teeth and implants. The modern CBCT device allows us to design a precise image of an extracted tooth for the purpose of manufacturing a root analog implant. The additional feature of the surgical protocol using RAZI is the possibility of avoiding the augmentation procedure, which reduces the whole cost of the treatment.

  6. Design and Fabrication of Porous Yttria-Stabilized Zirconia Ceramics for Hot Gas Filtration Applications

    Science.gov (United States)

    Shahini, Shayan

    Hot gas filtration has received growing attention in a variety of applications over the past few years. Yttria-stabilized zirconia (YSZ) is a promising candidate for such an application. In this study, we fabricated disk-type porous YSZ filters using the pore forming procedure, in which poly methyl methacrylate (PMMA) was used as the pore-forming agent. After fabricating the pellets, we characterized them to determine their potential for application as gas filters. We investigated the effect of sintering temperature, polymer particle size, and polymer-to-ceramic ratio on the porosity, pore size, gas permeability, and Vickers hardness of the sintered pellets. Furthermore, we designed two sets of experiments to investigate the robustness of the fabricated pellets--i.e., cyclic heating/cooling and high temperature exposure. This study ushers in a robust technique to fabricate such porous ceramics, which have the potential to be utilized in hot gas filtration.

  7. Band structure of TiO sub 2 -doped yttria-stabilized zirconia probed by soft-x-ray spectroscopy

    CERN Document Server

    Higuchi, T; Kobayashi, K; Yamaguchi, S; Fukushima, A; Shin, S

    2003-01-01

    The electronic structure of TiO sub 2 -doped yttria-stabilized zirconia (YSZ) has been studied by soft-X-ray emission spectroscopy (SXES) and X-ray absorption spectroscopy (XAS). The valence band is mainly composed of the O 2p state. The O 1s XAS spectrum exhibits the existence of the Ti 3d unoccupied state under the Zr 4d conduction band. The intensity of the Ti 3d unoccupied state increases with increasing TiO sub 2 concentration. The energy separation between the top of the valence band and the bottom of the Ti 3d unoccupied state is in accord with the energy gap, as expected from dc-polarization and total conductivity measurements. (author)

  8. Si-based thin film coating on Y-TZP: Influence of deposition parameters on adhesion of resin cement

    Energy Technology Data Exchange (ETDEWEB)

    Queiroz, José Renato Cavalcanti, E-mail: joserenatocq@hotmail.com [Potiguar University, Department of Biotechnology, Natal (Brazil); Nogueira Junior, Lafayette [São Paulo State University, Department of Prosthodontics and Dental Materials, São José dos Campos (Brazil); Massi, Marcos [Federal University of São Paulo, Institute of Science and Technology, São José dos Campos (Brazil); Silva, Alecssandro de Moura; Bottino, Marco Antonio [São Paulo State University, Department of Prosthodontics and Dental Materials, São José dos Campos (Brazil); Sobrinho, Argemiro Soares da Silva [Technological Institute of Aeronautics, Department of Physics, São José dos Campos (Brazil); Özcan, Mutlu [University of Zurich, Dental Materials Unit, Center for Dental and Oral Medicine, Clinic for Fixed and Removable Prosthodontics and Dental Materials Science, Zurich (Switzerland)

    2013-10-01

    This study evaluated the influence of deposition parameters for Si-based thin films using magnetron sputtering for coating zirconia and subsequent adhesion of resin cement. Zirconia ceramic blocks were randomly divided into 8 groups and specimens were either ground finished and polished or conditioned using air-abrasion with alumina particles coated with silica. In the remaining groups, the polished specimens were coated with Si-based film coating with argon/oxygen magnetron discharge at 8:1 or 20:1 flux. In one group, Si-based film coating was performed on air-abraded surfaces. After application of bonding agent, resin cement was bonded. Profilometry, goniometry, Energy Dispersive X-ray Spectroscopy and Rutherford Backscattering Spectroscopy analysis were performed on the conditioned zirconia surfaces. Adhesion of resin cement to zirconia was tested using shear bond test and debonded surfaces were examined using Scanning Electron Microscopy. Si-based film coating applied on air-abraded rough zirconia surfaces increased the adhesion of the resin cement (22.78 ± 5.2 MPa) compared to those of other methods (0–14.62 MPa) (p = 0.05). Mixed type of failures were more frequent in Si film coated groups on either polished or air-abraded groups. Si-based thin films increased wettability compared to the control group but did not change the roughness, considering the parameters evaluated. Deposition parameters of Si-based thin film and after application of air-abrasion influenced the initial adhesion of resin cement to zirconia.

  9. Si-based thin film coating on Y-TZP: Influence of deposition parameters on adhesion of resin cement

    International Nuclear Information System (INIS)

    Queiroz, José Renato Cavalcanti; Nogueira Junior, Lafayette; Massi, Marcos; Silva, Alecssandro de Moura; Bottino, Marco Antonio; Sobrinho, Argemiro Soares da Silva; Özcan, Mutlu

    2013-01-01

    This study evaluated the influence of deposition parameters for Si-based thin films using magnetron sputtering for coating zirconia and subsequent adhesion of resin cement. Zirconia ceramic blocks were randomly divided into 8 groups and specimens were either ground finished and polished or conditioned using air-abrasion with alumina particles coated with silica. In the remaining groups, the polished specimens were coated with Si-based film coating with argon/oxygen magnetron discharge at 8:1 or 20:1 flux. In one group, Si-based film coating was performed on air-abraded surfaces. After application of bonding agent, resin cement was bonded. Profilometry, goniometry, Energy Dispersive X-ray Spectroscopy and Rutherford Backscattering Spectroscopy analysis were performed on the conditioned zirconia surfaces. Adhesion of resin cement to zirconia was tested using shear bond test and debonded surfaces were examined using Scanning Electron Microscopy. Si-based film coating applied on air-abraded rough zirconia surfaces increased the adhesion of the resin cement (22.78 ± 5.2 MPa) compared to those of other methods (0–14.62 MPa) (p = 0.05). Mixed type of failures were more frequent in Si film coated groups on either polished or air-abraded groups. Si-based thin films increased wettability compared to the control group but did not change the roughness, considering the parameters evaluated. Deposition parameters of Si-based thin film and after application of air-abrasion influenced the initial adhesion of resin cement to zirconia.

  10. Thickness determination of large-area films of yttria-stabilized zirconia produced by pulsed laser deposition

    DEFF Research Database (Denmark)

    Pryds, N.; Christensen, Bo Toftmann; Bilde-Sørensen, Jørgen

    2006-01-01

    of the attenuation for various values of film thickness with the program CASINO. These results have been compared with direct measurements in the SEM of the film thickness on a cross-section on one of the wafers. The results of these measurements demonstrate the ability of this technique to accurately determine...

  11. Low-temperature technique for thick film resist stabilization and curing

    Science.gov (United States)

    Minter, Jason P.; Wong, Selmer S.; Marlowe, Trey; Ross, Matthew F.; Narcy, Mark E.; Livesay, William R.

    1999-06-01

    For a range of thick film photoresist applications, including MeV ion implant processing, thin film head manufacturing, and microelectromechanical systems processing, there is a need for a low-temperature method for resist stabilization and curing. Traditional methods of stabilizing or curing resist films have relied on thermal cycling, which may not be desirable due to device temperature limitations or thermally-induced distortion of the resist features.

  12. Investigation of temperature stability of ITO films characteristics

    Directory of Open Access Journals (Sweden)

    Troyan Pavel

    2018-01-01

    Full Text Available The paper represents research of thermal stability of optical and electro-physical parameters of ITO films deposited using various techniques. Variation of optical and electro-physical parameters was recorded using spectroscopy, and Hall’s and four-probe measurements. The best thermal stability was demonstrated by ITO films deposited by metal target sputtering In(90%/Sn(10% in mixture of gases O2 (25% + Ar (75% with further annealing in air atmosphere. This enables to apply this technique for production of thin film transparent resistive elements capable to heat the translucent structures up to 100°C without deterioration of their parameters.

  13. Structure of yttria stabilized zirconia beads produced by gel supported precipitation

    International Nuclear Information System (INIS)

    Walter, M.; Somers, J.; Fernandez, A.; Specht, Eliot D.; Hunn, John D.; Boulet, P.; Denecke, M. A.; Gobel, C.

    2007-01-01

    Yttria stabilized zirconia (YSZ) is one of the inert matrix candidates selected for investigation as host matrix for minor actinide (MA) transmutation. The structural properties of (Zr0.84, Y0.16)O1.92 beads prepared by a sol-gel method for MA infiltration, are characterized as calcined (850 C) and sintered (1,600 C) beads. The calcined YSZ beads are fine-grained and homogenous over the entire sphere and are surrounded by a uniform outer layer of approximately 30 (micro)m thickness. After sintering at 1,600 C, the beads are compacted to 51% of their initial volume and exhibit a granular structure. The thermal expansion is nearly linear for the calcined material, but shows a parabolic behavior for the sintered (1,400 C) beads. In addition, the thermal expansion of calcined material is 20-25% less than after sintering. During heating up to 1,400 C, two processes can be distinguished. The first occurs between 900 and 1,000 C and is related to an increase in unit cell order. The second process involves grain-growth of the less crystalline calcined material between 1,100 and 1,300 C. These results have implications for preparation of YSZ and its use as an inert MA transmutation matrix

  14. Evaluation of the tear film stability after laser in situ keratomileusis using the tear film stability analysis system.

    Science.gov (United States)

    Goto, Tomoko; Zheng, Xiaodong; Klyce, Stephen D; Kataoka, Hisashi; Uno, Toshihiko; Yamaguchi, Masahiko; Karon, Mike; Hirano, Sumie; Okamoto, Shigeki; Ohashi, Yuichi

    2004-01-01

    To evaluate the tear film stability of patients before and after laser in situ keratomileusis (LASIK) using the tear film stability analysis system (TSAS). Prospective observational case series. New videokeratography software for a topographic modeling system (TMS-2N) was developed that can automatically capture consecutive corneal surface images every second for 10 seconds. Thirty-four subjects (64 eyes) who underwent myopia LASIK were enrolled in this study. All subjects were examined with the new system before LASIK and at 1 week, 1 month, 3 months, and 6 months after the surgery. Corneal topographs were analyzed for tear breakup time (TMS breakup time) and breakup area (TMS breakup area). Based on pre-LASIK TSAS analysis, subjects were separated into normal and abnormal TSAS value groups. The criteria for the normal group were either TMS breakup time more than 5 seconds or TMS breakup area less than 0.2. The percentage of the occurrence of superficial punctuate keratitis was compared between the two groups with regard to subject's dry eye signs and symptoms. Tear film stability decreased significantly during the early period after LASIK, as indexed by decreased TMS breakup time and increased TMS breakup area. Tear film instability resolved at 6 months after surgery. Before LASIK, 22 subjects (43 eyes) had normal TSAS evaluation and 12 subjects (21 eyes) were abnormal. After LASIK, among normal TSAS value eyes, 8 of 43 (18.6%) eyes developed superficial punctuate keratitis. In sharp contrast, 14 of 21 (66.7%) eyes in the abnormal group displayed superficial punctuate keratitis, correlating well with the patients' dry eye symptoms. The difference in the presence of superficial punctuate keratitis after LASIK between normal and abnormal TSAS value groups was statistically significant (P <.001). Subjects with abnormal TSAS evaluation also displayed resistance to dry eye treatment and had extended period of recovery. Tear film stability analysis can be a useful

  15. Determination of optical properties in nanostructured thin films using the Swanepoel method

    International Nuclear Information System (INIS)

    Sanchez-Gonzalez, J.; Diaz-Parralejo, A.; Ortiz, A.L.; Guiberteau, F.

    2006-01-01

    We present the methodological framework of the Swanepoel method for the spectrophotometric determination of optical properties in thin films using transmittance data. As an illustrative case study, we determined the refractive index, thickness, absorption index, and extinction coefficient of a nanostructured 3 mol% Y 2 O 3 -doped ZrO 2 (yttria stabilized zirconia, 3YSZ) thin film prepared by the sol-gel method and deposited by dipping onto a soda-lime glass substrate. In addition, using the absorption index obtained with the Swanepoel method, we calculated the optical band gap of the film. The refractive index was found to increase, then decrease, and finally stabilize with increasing wavelength of the radiation, while the absorption index and extinction coefficient decreased monotonically to zero. These trends are explained in terms of the location of the absorption bands. We also deduced that this 3YSZ thin film has a direct optical band gap of 4.6 eV. All these results compared well with those given in the literature for similar thin films. This suggests that the Swanepoel method has an important role to play in the optical characterization of ceramic thin films

  16. Determination of optical properties in nanostructured thin films using the Swanepoel method

    Energy Technology Data Exchange (ETDEWEB)

    Sanchez-Gonzalez, J. [Departamento de Electronica e Ingenieria Electromecanica, Escuela de Ingenierias Industriales, Universidad de Extremadura, Badajoz 06071 (Spain); Diaz-Parralejo, A. [Departamento de Electronica e Ingenieria Electromecanica, Escuela de Ingenierias Industriales, Universidad de Extremadura, Badajoz 06071 (Spain); Ortiz, A.L. [Departamento de Electronica e Ingenieria Electromecanica, Escuela de Ingenierias Industriales, Universidad de Extremadura, Badajoz 06071 (Spain)]. E-mail: alortiz@unex.es; Guiberteau, F. [Departamento de Electronica e Ingenieria Electromecanica, Escuela de Ingenierias Industriales, Universidad de Extremadura, Badajoz 06071 (Spain)

    2006-06-30

    We present the methodological framework of the Swanepoel method for the spectrophotometric determination of optical properties in thin films using transmittance data. As an illustrative case study, we determined the refractive index, thickness, absorption index, and extinction coefficient of a nanostructured 3 mol% Y{sub 2}O{sub 3}-doped ZrO{sub 2} (yttria stabilized zirconia, 3YSZ) thin film prepared by the sol-gel method and deposited by dipping onto a soda-lime glass substrate. In addition, using the absorption index obtained with the Swanepoel method, we calculated the optical band gap of the film. The refractive index was found to increase, then decrease, and finally stabilize with increasing wavelength of the radiation, while the absorption index and extinction coefficient decreased monotonically to zero. These trends are explained in terms of the location of the absorption bands. We also deduced that this 3YSZ thin film has a direct optical band gap of 4.6 eV. All these results compared well with those given in the literature for similar thin films. This suggests that the Swanepoel method has an important role to play in the optical characterization of ceramic thin films.

  17. Stability of sputter deposited ZnO:Cr films against acids

    International Nuclear Information System (INIS)

    Shinoda, Makoto; Nishide, Toshikazu; Sawada, Yutaka; Hosaka, Masato; Matsumoto, Toshihiko.

    1993-01-01

    ZnO:Cr films were deposited on water-cooled soda-lime glass substrates at room temperature in an Ar atmosphere by rf magnetron sputtering of a ZnO target on which Cr chips were placed. The films exhibited extraordinary stability against acids such as HCl or HNO 3 , and also high resistivities similar to those of ZnO films. The addition of Cr suppressed the growth of ZnO grains which resulted in the formation of a dense film with a smooth surface. The stability and high resistivity displayed by the ZnO:Cr films can be attributed to the formation of a chromium-oxide-rich grain boundary. (author)

  18. Glass ceramic toughened with tetragonal zirconia

    Science.gov (United States)

    Keefer, Keith D.; Michalske, Terry A.

    1986-01-01

    A phase transformation-toughened glass ceramic and a process for making it are disclosed. A mixture of particulate network-forming oxide, network-modifying oxide, and zirconium oxide is heated to yield a homogeneous melt, and this melt is then heat-treated to precipitate an appreciable quantity of tetragonal zirconia, which is retained at ambient temperature to form a phase transformation-toughened glass ceramic. Nucleating agents and stabilizing agents may be added to the mixture to facilitate processing and improve the ceramic's properties. Preferably, the mixture is first melted at a temperature from 1200.degree. to 1700.degree. C. and is then heat-treated at a temperature within the range of 800.degree. to 1200.degree. C. in order to precipitate tetragonal ZrO.sub.2. The composition, as well as the length and temperature of the heat-treatment, must be carefully controlled to prevent solution of the precipitated tetragonal zirconia and subsequent conversion to the monoclinic phase.

  19. Stabilization of thin liquid films by repulsive van der waals force

    KAUST Repository

    Li, Erqiang

    2014-05-13

    Using high-speed video recording of bubble rise experiments, we study the stability of thin liquid films trapped between a rising bubble and a surfactant-free liquid-liquid meniscus interface. Using different combinations of nonpolar oils and water that are all immiscible, we investigate the extent to which film stability can be predicted by attractive and repulsive van der Waals (vdW) interactions that are indicated by the relative magnitude of the refractive indices of the liquid combinations, for example, water (refractive index, n = 1.33), perfluorohexane (n = 1.23), and tetradecane (n = 1.43). We show that, when the film-forming phase was oil (perfluorohexane or tetradecane), the stability of the film could always be predicted from the sign of the vdW interaction, with a repulsive vdW force resulting in a stable film and an attractive vdW force resulting in film rupture. However, if aqueous electrolyte is the film-forming bulk phase between the rising air bubble and the upper oil phase, the film always ruptured, even when a repulsive vdW interaction was predicted. We interpret these results as supporting the hypothesis that a short-ranged hydrophobic attraction determines the stability of the thin water film formed between an air phase and a nonpolar oil phase. © 2014 American Chemical Society.

  20. Synthesis of Ceria Zirconia Oxides using Solvothermal Treatment

    Directory of Open Access Journals (Sweden)

    Machmudah Siti

    2018-01-01

    Full Text Available Ceria oxide (CeO2 is widely used as catalyst with high oxygen storage capacity at low temperature. The addition of zirconia oxide (ZrO2 to CeO2 can enhance oxygen storage capacity as well as thermal stability. In this work, ceria zirconia oxides has been synthesized via a low temperature solvothermal treatment in order to produce ceria zirconia oxides composite with high oxygen storage capacity as electrolyte of solid oxide fuel cells (SOFC. Under solvothermal conditions, solvent may control the direction of crystal growth, morphology, particle size and size distribution, because of the controllability of thermodynamics and transport properties by pressure and temperature. Water, mixed of water and ethanol (70/30 vol/vol, and mixed of water and ethylene glycol (70/30 vol/vol were used as solvent, while Ce(NO33 and ZrO(NO32 with 0.06 M concentration were used as precursor. The experiments were conducted at temperature of 150 °C and pressure for 2 h in a Teflon-lined autoclave of 100 mL volume. The synthesized products were dried at 60 °C for 6 and 12 h and then calcined at 900 °C for 6 h. The particle products were characterized using SEM, XRD, TG/DTA, and Potentiostat. The results showed that the morphology of particles formed were affected by the solvent. Solid plate shaped particles were produced in water, and tend to be pore with the addition of ethylene glycol. The addition of ethanol decreased the size of particles with sphere shaped. The XRD pattern indicated that ceria-zirconia oxides particles are uniformly distributed in the structure to form a homogeneous solid solution. Based on the electrochemical analysis, ceria zirconia oxides produced via solvothermal synthesis had high conductivity ion of 0.5594 S/cm, which is higher than minimum conductivity ion requirement of 0.01 S/cm for SOFC electrolyte. It indicated that ceria zirconia oxides produced via solvothermal synthesis is suitable for SOFC electrolyte.

  1. Ion-exchange behaviour of hydrous zirconia in mixed solvents: capacity and kinetics of exchange

    International Nuclear Information System (INIS)

    Misak, N.Z.; Ghoneimy, H.F.

    1982-01-01

    The capacity of the Li + form of hydrous zirconia for Na + and Cs + increases in the presence of methanol. This may be due to the greater stability of Li + in methanol/water than in pure water and to dehydration of Na + and Cs + and their stronger interaction with the exchange sites, which may facilitate their replacing Li + . The ion-exchange capacity of zirconia for NO 3 - , Cl - and Br - is almost the same in aqueous solution and is not affected by addition of up to 90% (v/v) methanol, which probably shows that these anions are electrostatically bound in zirconia without specific interactions. The internal diffusion coefficients of the Na + /H + and Cl - /OH - systems decrease in the presence of alcohol: the decrease is highest with methanol and similar for ethanol and propan-2-ol. This is discussed in the light of ion solvation and alcohol penetration inside zirconia. (author)

  2. Deposition, structure, and properties of cermet thin films composed of Ag and Y-stabilized zirconia

    International Nuclear Information System (INIS)

    Wang, L.S.; Barnett, S.A.

    1992-01-01

    This paper reports that Ag 1-x [(Y 2 O 3 ) 0.1 (ZrO 2 ) 0.9 ] x (YSZ) cermet thin films have been deposited by reactive magnetron cosputtering from Ag and Zr/Y targets in Ar-O 2 mixtures. The deposition conditions were such that the YSZ component in the films was fully oxidized. The film densities varied from ∼75% to >85% as the total pressure was decreased from 20 to 5 mTorr. Film resistivities ρ varied with Ag volume fraction f Ag from 5 x 10 -6 Ω-cm to >10 9 Ω-cm. For f Ag Ag . For f Ag > 0.4, ρ decreased more gradually with increasing f Ag . ρ in annealed films ranged from 4 x 10 -4 Ω-cm for f Ag = 0.4 to 5 x 10 -6 Ω-cm for pure Ag. Long term (>100 h) annealing at ≥700 degrees C resulted in a gradual increase in cermet resistivity due to Ag evaporation and Ag segregation to surface islands. Both decomposition mechanisms were effectively suppressed due to Ag evaporation and Ag segregation to surface islands. Both decomposition mechanisms were effectively suppressed at up to 750 degrees C by depositing a 1 μm thick porous perovskite cap layer on the cermet. Complex impedance spectroscopy measurements in air of cermet electrodes on YSZ electrolytes gave interfacial resistances that were a factor of ∼6 lower than those of pure AG electrodes, e.g., 1.4 Ω-cm 2 at 750 degrees C. Ag-YSZ cermets thus have potential as high-conductivity, low-overpotential air electrode materials for solid-oxide electrochemical devices operating at temperatures ≤750 degrees C

  3. Chemically stabilized epitaxial wurtzite-BN thin film

    Science.gov (United States)

    Vishal, Badri; Singh, Rajendra; Chaturvedi, Abhishek; Sharma, Ankit; Sreedhara, M. B.; Sahu, Rajib; Bhat, Usha; Ramamurty, Upadrasta; Datta, Ranjan

    2018-03-01

    We report on the chemically stabilized epitaxial w-BN thin film grown on c-plane sapphire by pulsed laser deposition under slow kinetic condition. Traces of no other allotropes such as cubic (c) or hexagonal (h) BN phases are present. Sapphire substrate plays a significant role in stabilizing the metastable w-BN from h-BN target under unusual PLD growth condition involving low temperature and pressure and is explained based on density functional theory calculation. The hardness and the elastic modulus of the w-BN film are 37 & 339 GPa, respectively measured by indentation along direction. The results are extremely promising in advancing the microelectronic and mechanical tooling industry.

  4. Zirconia toughened mica glass ceramics for dental restorations.

    Science.gov (United States)

    Gali, Sivaranjani; K, Ravikumar; Murthy, B V S; Basu, Bikramjit

    2018-03-01

    The objective of the present study is to understand the role of yttria stabilized zirconia (YSZ) in achieving the desired spectrum of clinically relevant mechanical properties (hardness, elastic modulus, fracture toughness and brittleness index) and chemical solubility of mica glass ceramics. The glass-zirconia mixtures with varying amounts of YSZ (0, 5, 10, 15 and 20wt.%) were ball milled, compacted and sintered to obtain pellets of glass ceramic-YSZ composites. Phase analysis was carried out using X-ray diffraction and microstructural characterization with SEM revealed the crystal morphology of the composites. Mechanical properties such as Vickers hardness, elastic modulus, indentation fracture toughness and chemical solubility were assessed. Phase analysis of sintered pellets of glass ceramic-YSZ composites revealed the characteristic peaks of fluorophlogopite (FPP) and tetragonal zirconia. Microstructural investigation showed plate and lath-like interlocking mica crystals with embedded zirconia. Vickers hardness of 9.2GPa, elastic modulus of 125GPa, indentation toughness of 3.6MPa·m 1/2 , and chemical solubility of 30μg/cm 2 (well below the permissible limit) were recorded with mica glass ceramics containing 20wt.% YSZ. An increase in hardness and toughness of the glass ceramic-YSZ composites with no compromise on their brittleness index and chemical solubility has been observed. Such spectrum of properties can be utilised for developing a machinable ceramic for low stress bearing inlays, onlays and veneers. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  5. Electroactive mesoporous yttria stabilized zirconia containing platinum or nickel oxide nanoclusters: a new class of solid oxide fuel cell electrode materials

    Energy Technology Data Exchange (ETDEWEB)

    Mamak, M.; Coombs, N.; Ozin, G.A. [Toronto Univ., ON (Canada). Dept. of Chemistry

    2001-02-01

    The electroactivity of surfactant-templated mesoporous yttria stabilized zirconia, containing nanoclusters of platinum or nickel oxide, is explored by alternating current (AC) complex impedance spectroscopy. The observed oxygen ion and mixed oxygen ion-electron charge-transport behavior for these materials, compared to the sintered-densified non-porous crystalline versions, is ascribed to the unique integration of mesoporosity and nanocrystallinity within the binary and ternary solid solution microstructure. These attributes inspire interest in this new class of materials as candidates for the development of improved performance solid oxide fuel cell electrodes. (orig.)

  6. Zirconia - the cinderella transformation

    International Nuclear Information System (INIS)

    Hannink, R.H.J.

    1999-01-01

    Zirconia and its alloys have formed a turning point in mechanical property developments of engineering ceramics. This can be stated primarily because zirconia alloys were one of the first ceramic systems in which it was demonstrated that the mechanical properties could be tailored using careful control of composition, powder processing and thermal treatment. For the improved mechanical properties to be captured in zirconia-based or containing ceramics, control of the tetragonal to monoclinic transformation is required. Through microstructural control, zirconia-based ceramics can be tailored to form some of the strongest and toughest ceramics yet developed. By carefully controlling the use of various dopants (alloying additions), a variety of microstructures can be produced all of which may exhibit transformation toughening. While success in capturing the benefits of transformation toughening relies on adequate powder processing techniques, this review is restricted to outlining the phase control and behaviour that make zirconia and its alloys such a scientifically fascinating and rewarding system for study and a commercially appealing ceramic material

  7. Kinetic Monte Carlo Simulation of Oxygen and Cation Diffusion in Yttria-Stabilized Zirconia

    Science.gov (United States)

    Good, Brian

    2011-01-01

    Yttria-stabilized zirconia (YSZ) is of interest to the aerospace community, notably for its application as a thermal barrier coating for turbine engine components. In such an application, diffusion of both oxygen ions and cations is of concern. Oxygen diffusion can lead to deterioration of a coated part, and often necessitates an environmental barrier coating. Cation diffusion in YSZ is much slower than oxygen diffusion. However, such diffusion is a mechanism by which creep takes place, potentially affecting the mechanical integrity and phase stability of the coating. In other applications, the high oxygen diffusivity of YSZ is useful, and makes the material of interest for use as a solid-state electrolyte in fuel cells. The kinetic Monte Carlo (kMC) method offers a number of advantages compared with the more widely known molecular dynamics simulation method. In particular, kMC is much more efficient for the study of processes, such as diffusion, that involve infrequent events. We describe the results of kinetic Monte Carlo computer simulations of oxygen and cation diffusion in YSZ. Using diffusive energy barriers from ab initio calculations and from the literature, we present results on the temperature dependence of oxygen and cation diffusivity, and on the dependence of the diffusivities on yttria concentration and oxygen sublattice vacancy concentration. We also present results of the effect on diffusivity of oxygen vacancies in the vicinity of the barrier cations that determine the oxygen diffusion energy barriers.

  8. Effect of coarse grinding, overglazing, and 2 polishing systems on the flexural strength, surface roughness, and phase transformation of yttrium-stabilized tetragonal zirconia.

    Science.gov (United States)

    Mohammadi-Bassir, Mahshid; Babasafari, Mansoure; Rezvani, Mohammad Bagher; Jamshidian, Mahdieh

    2017-11-01

    Limited information is available for the best polishing systems and methods to obtain minimally abrasive monolithic zirconia surfaces after contouring and occlusal adjustment. The purpose of this in vitro study was to evaluate the effect of grinding and polishing procedures on the flexural strength, quality and quantity of surface roughness, topography, and phase transformation of a zirconia-based ceramic system. Fifty bar-shaped yttrium-stabilized zirconium oxide specimens (20×4×2 mm) were cut from presintered zirconia blanks. The specimens were wet-polished and divided into 5 groups (n=10): standard polishing without any surface treatment (group SP); grinding with a diamond rotary instrument (group Gr); grinding with a diamond rotary instrument (DRI) and over-glazing (group Gl); grinding with a DRI and polishing with an intraoral zirconia polishing kit in a 2-step procedure (group BP); and grinding with a DRI and polishing with an intraoral polishing kit (group MP). The Ra and Rz surface roughness values (μm) were measured with a profilometer. One specimen of each group was subjected to x-ray diffraction (XRD) to estimate the monoclinic phase and evaluated using scanning electron microscopy (SEM) for surface topography. The 3-point flexural strength of the bars was measured in a universal testing machine at a crosshead speed of 0.5 mm/min. The mean flexural strength (MPa) and surface roughness values were calculated, and the results were analyzed using 1-way ANOVA and Tukey honest significant difference tests (α=.05). Statistically significant differences were noted among the experimental groups for Ra, Rz (Pgrinding that were smoothened by glazing and polishing. Roughness increased significantly after grinding, but polishing and glazing similarly diminished it. Glazing after grinding significantly decreased the flexural strength values, but polishing did not. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier

  9. Thermal properties and stabilities of polymer thin films

    International Nuclear Information System (INIS)

    Kanaya, Toshiji; Kawashima, Kazuko; Inoue, Rintaro; Miyazaki, Tsukasa

    2009-01-01

    Recent extensive studies have revealed that polymer thin films showed very interesting but unusual thermal properties and stabilities. In the article we show that X-ray reflectivity and neutron reflectivity are very powerful tools to study the anomalous properties of polymer thin films. (author)

  10. Electrical characterization of zirconia-niobium and zirconia-titanium composites; Caracterizacao eletrica dos compositos zirconia-niobio e zirconia-titanio

    Energy Technology Data Exchange (ETDEWEB)

    Reis, S.T. dos

    1994-12-31

    Zirconia-niobium and zirconia-titanium composites were made by powder mixing, cold pressing, and vacuum sintering at 1600{sup 0} C. The metallic particles were added in the proportion of 0-50% by volume. Electrical resistivity measurements were performed by the two probes and the four probes d.c. method as a function of metallic particle concentration. Electrical resistivity of these composites decreased sharply in the region of 30-40 vol% Nb or Ti, in agreement with the percolation theory. Tests in an induction furnace were performed to check the self-heating response of these composites. (author). 33 refs, 40 figs, 11 tabs.

  11. Using glass-graded zirconia to increase delamination growth resistance in porcelain/zirconia dental structures.

    Science.gov (United States)

    Chai, Herzl; Mieleszko, Adam J; Chu, Stephen J; Zhang, Yu

    2018-01-01

    Porcelain fused to zirconia (PFZ) restorations are widely used in prosthetic dentistry. However, their tendency to delaminate along the P/Z interface remains a practical problem so that assessing and improving the interfacial strength are important design aspects. This work examines the effect of modifying the zirconia veneering surface with an in-house felspathic glass on the interfacial fracture resistance of fused P/Z. Three material systems are studied: porcelain fused to zirconia (control) and porcelain fused to glass-graded zirconia with and without the presence of a glass interlayer. The specimens were loaded in a four-point-bend fixture with the porcelain veneer in tension. The evolution of damage is followed with the aid of a video camera. The interfacial fracture energy G C was determined with the aid of a FEA, taking into account the stress shielding effects due to the presence of adjacent channel cracks. Similarly to a previous study on PFZ specimens, the fracture sequence consisted of unstable growth of channel cracks in the veneer followed by stable cracking along the P/Z interface. However, the value of GC for the graded zirconia was approximately 3 times that of the control zirconia, which is due to the good adhesion between porcelain and the glass network structure on the zirconia surface. Combined with its improved bonding to resin-based cements, increased resistance to surface damage and good esthetic quality, graded zirconia emerges as a viable material concept for dental restorations. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  12. Effects of annealing on the microstructure of yttria-stabilised zirconia thin films deposited by laser ablation

    International Nuclear Information System (INIS)

    Mengucci, P.; Barucca, G.; Caricato, A.P.; Di Cristoforo, A.; Leggieri, G.; Luches, A.; Majnia, G.

    2005-01-01

    In this paper the microstructural characterisation of yttria-stabilised zirconia (YSZ) thin films deposited by laser ablation is reported for the as-deposited sample as well as for samples submitted to thermal treatments in different atmospheres (vacuum, N 2 and O 2 ) at a moderate temperature (500 deg. C). Results obtained by different characterisation techniques such as grazing incidence X-ray diffraction, X-ray reflectivity and transmission electron microscopy evidenced the formation of the cubic YSZ phase after the annealing treatments. On the contrary, the as-deposited sample is amorphous with nanocrystals of the cubic YSZ phase dispersed inside. It also exhibits a difference between the density of the surface region and the region of the interface with the substrate. This latter effect has been attributed to the loss of oxygen atoms during the deposition. The annealing treatments are able to recover the density unhomogeneity present inside the as-deposited sample, the degree of recovering depends on the ambient atmosphere

  13. Growth of highly oriented La{sub 0.84}Sr{sub 0.16}MnO{sub 3} perovskite films

    Energy Technology Data Exchange (ETDEWEB)

    Chung, B.W.; Brosha, E.L.; Garzon, F.H.; Raistrick, I.D.; Houlton, R.J.; Hawley, M.E. [Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States)

    1995-10-01

    We have grown thin films of La{sub 0.84}Sr{sub 0.16}MnO{sub 3} on SrTiO{sub 3} (100), MgO (100), CeO{sub 2} (100)/Al{sub 2}O{sub 3}, and (100) oriented yttria-stabilized zirconia (YSZ) substrates by using a 90{degree} off-axis RF magnetron sputtering deposition. X-ray diffraction analysis and ion beam channeling experiments reveal that the deposited films grow epitaxially on SrTiO{sub 3}, biaxially textured on MgO, and highly textured on YSZ. Scanning tunneling microscopy reveals that the thin films possess extremely smooth surfaces. {copyright} 1995 Materials Research Society

  14. Influence of solvent on the morphology and microstructure of YSZ films obtained by spray pyrolysis technique

    International Nuclear Information System (INIS)

    Falcade, T.; Oliveira, G.B.; Mueller, I.L.; Malfatti, C.F.

    2010-01-01

    This work aims to investigate the influence of solvent used for the deposition of thin films of yttria stabilized zirconia (YSZ) on porous substrate. The films were obtained directly on the porous LSM substrate by spray pyrolysis technique, which consists of spraying a precursor solution containing salts of zirconium (Zr (C 6 H 7 O 2 ) 4) and yttrium (YCl 3 .6H 2 O), dissolved in specific solvents, on the heated substrate. The use of solvents with different boiling points and viscosity aims the optimization of experimental operating parameters to obtain homogeneous and dense films suitable for application as electrolyte in fuel cells, solid oxide (SOFC). The films were characterized by scanning electron microscopy, infrared spectroscopy and X-ray diffraction. (author)

  15. Convective transport and stability in films of binary mixtures

    OpenAIRE

    Madruga Sánchez, Santiago; Bribesh, Fathi; Uwe, Thiele

    2011-01-01

    Thin polymer films are increasingly used in advanced technological applications. The use of these films as coatings is often limited by their lack of stability due to their wettability properties on the substrates

  16. Preparation of stabilized zirconia (Zr O2) with Yttria (Y2 O3) by simultaneous precipitation

    International Nuclear Information System (INIS)

    Campos, M. de.

    1993-01-01

    The preparation of cubic or tetragonal partially stabilized zirconia with Yttria by simultaneous precipitation was studied. The metals Zr and Y, in nitric acid and hydrogen peroxide medium, were precipitated with ammonia solution. The variables studied were: the pH of the aqueous medium (8, 9 e 10) and yttrium molar concentration (2, 3 and 5 mol %) in the final product. The resulting oxide samples were divided and calcined at 500, 700 and 900 0 C, separately. After that, all samples were sintered at 1500 0 C for one hour. For physico-chemical characterization were used techniques such as: ICP-AES, XRF, XRD, SEM etc. The results have showed that using this approach predominant cubic and/or tetragonal phases can be reached with theoretical density over 92% and grain size lower than 1 μm. (author)

  17. Thermal Shock Resistance of Stabilized Zirconia/Metal Coat on Polymer Matrix Composites by Thermal Spraying Process

    Science.gov (United States)

    Zhu, Ling; Huang, Wenzhi; Cheng, Haifeng; Cao, Xueqiang

    2014-12-01

    Stabilized zirconia/metal coating systems were deposited on the polymer matrix composites by a combined thermal spray process. Effects of the thicknesses of metal layers and ceramic layer on thermal shock resistance of the coating systems were investigated. According to the results of thermal shock lifetime, the coating system consisting of 20 μm Zn and 125 μm 8YSZ exhibited the best thermal shock resistance. Based on microstructure evolution, failure modes and failure mechanism of the coating systems were proposed. The main failure modes were the formation of vertical cracks and delamination in the outlayer of substrate, and the appearance of coating spallation. The residual stress, thermal stress and oxidation of substrate near the substrate/metal layer interface were responsible for coating failure, while the oxidation of substrate near the substrate/coating interface was the dominant one.

  18. Protection of yttria-stabilized zirconia for dental applications by oxidic PVD coating.

    Science.gov (United States)

    Hübsch, C; Dellinger, P; Maier, H J; Stemme, F; Bruns, M; Stiesch, M; Borchers, L

    2015-01-01

    In this study, the application of transparent physical vapor deposition (PVD) coatings on zirconia ceramics was examined as an approach to retard the low-temperature degradation of zirconia for dental applications. Transparent monolayers of titanium oxide (TixOy) and multilayers consisting of titanium oxide-alumina-titanium oxide (TixOy-AlxOy-TixOy) were deposited onto standardized discs of 3Y-TZP using magnetron sputtering. Using X-ray photospectroscopy and time-of-flight secondary-ion mass spectrometry, the compositions of the coatings were verified, and an approximate thickness of 50 nm for each type of coating was ascertained. After aging the coated and uncoated samples in water vapor at 134°C and 3 bar for 4, 8, 16, 32, 64 and 128 h, the monoclinic phase content was determined using X-ray diffraction, and its impact on mechanical properties was assessed in biaxial flexural strength tests. In addition, the depth of the transformation zone was measured from scanning electron microscopy images of the fracture surfaces of hydrothermally aged samples. The results revealed that the tetragonal-to-monoclinic phase transformation of the zirconia ceramic was retarded by the application of PVD coatings. During the first stages of aging, the coated samples exhibited a significantly lower monoclinic phase content than the uncoated samples and, after 128 h of aging, showed a transformation zone which was only ∼12-15 μm thick compared to ∼30 μm in the control group. Biaxial flexural strength decreased by ∼10% during aging and was not influenced by the application of a PVD coating. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  19. Optical characterization of Pr3+-doped yttria-stabilized zirconia single crystals

    International Nuclear Information System (INIS)

    Savoini, B.; Munoz Santiuste, J.E.; Gonzalez, R.

    1997-01-01

    The optical absorption and fluorescence of Pr 3+ ions in yttria-stabilized zirconia single crystals are investigated. Fluorescence emissions from the 1 D 2 level are clearly dominant and low intensity emission lines from the 3 P 0 and 1 G 4 states are also observed. Analysis with the Judd-Ofelt theory of the absorption intensities has been made assuming that only ∼40% of the praseodymium ions contribute to the optical absorption bands. Quantum efficiency values of η( 3 P 0 )∼0.2 and η( 1 D 2 )∼ 1 are obtained at room temperature. 1 D 2 fluorescence quenching has been observed in heavily-doped samples due to cross relaxation processes among neighboring Pr 3+ ions. Analysis using the Inokuti-Hirayama model shows that electric dipole-dipole interactions are mainly responsible for the quenching effect. Pr 3+ ions are present in seven and sixfold configurations with a statistical distribution. The energy position of the 4f5d configuration is very different for each center. The fluorescence dynamics is explained by a mechanism involving thermally assisted population of the 3 P 1,2 + 1 I 6 upper levels and fast relaxation to the 1 D 2 level via states of the excited 4f5d configuration. copyright 1997 The American Physical Society

  20. Effect of various intermediate ceramic layers on the interfacial stability of zirconia core and veneering ceramics.

    Science.gov (United States)

    Yoon, Hyung-In; Yeo, In-Sung; Yi, Yang-Jin; Kim, Sung-Hun; Lee, Jai-Bong; Han, Jung-Suk

    2015-01-01

    The purposes of this study were to evaluate the effects of intermediate ceramics on the adhesion between the zirconia core and veneer ceramics. The polished surfaces of fully sintered Y-TZP blocks received three different treatments: (1) connector (C), (2) liner (L) or (3) wash layer (W). All the treated zirconia blocks were veneered with either (a) fluorapatite glass-ceramic (E) or (b) feldspathic porcelain (V) and divided into four groups (CE, CV, LE and WV). For the control group, the testing surfaces of metal blocks were veneered with feldspathic porcelain (VM). A half of the samples in each group (n = 21) were exposed to thermocycling, while the other half of the specimens were stored at room temperature under dry conditions. All specimens were subjected to the shear test and the failed surfaces were microscopically examined. The elemental distribution at the zirconia core/veneer interface was analyzed. The specimens in Groups CE and CV exhibited significantly greater mean bond strength values than those in Groups LE and WV, respectively (p ceramic substances into the zirconia surface. A glass-ceramic based connector is significantly more favorable to core/veneer adhesion than the other intermediate ceramics evaluated in the study. However, thermal cycling affected the bond strength at the core/veneer interface differently according to the intermediate ceramics.

  1. Sulfation of ceria-zirconia model automotive emissions control catalysts

    Science.gov (United States)

    Nelson, Alan Edwin

    Cerium-zirconium mixed metal oxides are used in automotive emissions control catalysts to regulate the partial pressure of oxygen near the catalyst surface. The near surface oxygen partial pressure is regulated through transfer of atomic oxygen from the ceria-zirconia solid matrix to the platinum group metals to form metal oxides capable of oxidizing carbon monoxide and unburned hydrocarbons. Although the addition of zirconium in the cubic lattice of ceria increases the oxygen storage capacity and thermal stability of the ceria matrix, the cerium-zirconium oxide system remains particularly susceptible to deactivation from sulfur compounds. While the overall effect of sulfur on these systems is understood (partially irreversible deactivation), the fundamental and molecular interaction of sulfur with ceria-zirconia remains a challenging problem. Ceria-zirconia metal oxide solid solutions have been prepared through co-precipitation with nitrate precursors. The prepared powders were calcined and subsequently formed into planer wafers and characterized for chemical and physical attributes. The prepared samples were subsequently exposed to a sulfur dioxide based environment and characterized with spectroscopic techniques to characterize the extent of sulfation and the nature of surface sulfur species. The extent of sulfation of the model ceria-zirconia systems was characterized with Auger electron spectroscopy (AES) prior to and after treatment in a microreactor. Strong dependencies were observed between the atomic ratio of ceria to zirconia and the extent of sulfation. In addition, the partial pressure of sulfur dioxide during treatments also correlated to the extent of sulfation, while temperature only slightly effected the extent of sulfation. The AES data suggests the gas phase sulfur dioxide preferentially chemisorbs on surface ceria atoms and the extent of sulfation is heavily dependent on sulfur dioxide concentrations and only slightly dependent on catalyst

  2. Evaluation of biological activities of nanocrystalline zirconia synthesis via combustion method

    International Nuclear Information System (INIS)

    Thakare, V.G.; Omanwar, S.K.; Bhatkar, V.B.; Wadegaokar, P.A.

    2016-01-01

    The objective of the following study was synthesis of nanocrystalline zirconia by modified solution combustion synthesis method and evaluation of its structural and biological properties. The sample was characterized by powder X-ray diffraction (XRD), Field Emission Scanning Electron Microscopy (FESEM) and evaluated for cytotoxicity study using 3T3 mouse fibroblast cells, the antibacterial property are investigated by spread plate method against E. coli bacterial pathogen and studied for degradation using phosphate buffered saline (PBS) solution. The XRD pattern shows that the monoclinic phase of nanocrystalline zirconia was obtained. The FESEM images showed that the prepared sample consists of particles in the range of 45 nm and homogenous particle size distribution. The sample of zirconia has excellent tissue biocompatibility and does not show any toxicity towards normal 3T3 mouse fibroblast cells. It also inhibited the bacterial growth. The sample shows stability at physiological condition and does not show degradation. (author)

  3. Attachment and growth behaviour of human gingival fibroblasts on titanium and zirconia ceramic surfaces

    International Nuclear Information System (INIS)

    Pae, Ahran; Kim, Hyeong-Seob; Woo, Yi-Hyung; Lee, Heesu; Kwon, Yong-Dae

    2009-01-01

    The attachment, growth behaviour and the genetic effect of human gingival fibroblasts (HGF) cultured on titanium and different zirconia surfaces were investigated. HGF cells were cultured on (1) titanium discs with a machined surface, (2) yttrium-stabilized tetragonal zirconia polycrystals (Y-TZP) with a smooth surface and (3) Y-TZP with 100 μm grooves. The cell proliferation activity was evaluated through a MTT assay at 24 h and 48 h, and the cell morphology was examined by SEM. The mRNA expression of integrin-β1, type I and III collagen, laminin and fibronectin in HGF were evaluated by RT-PCR after 24 h. From the MTT assay, the mean optical density values for the titanium and grooved zirconia surfaces after 48 h of HGF adhesion were greater than the values obtained for the smooth zirconia surfaces. SEM images showed that more cells were attached to the grooves, and the cells appeared to follow the direction of the grooves. The results of RT-PCR suggest that all groups showed comparable fibroblast-specific gene expression. A zirconia ceramic surface with grooves showed biological responses that were comparable to those obtained with HGF on a titanium surface.

  4. Sol-gel dip coating of yttria-stabilized tetragonal zirconia dental ceramic by aluminosilicate nanocomposite as a novel technique to improve the bonding of veneering porcelain.

    Science.gov (United States)

    Madani, Azamsadat; Nakhaei, Mohammadreza; Karami, Parisa; Rajabzadeh, Ghadir; Salehi, Sahar; Bagheri, Hossein

    2016-01-01

    The aim of this in vitro study was to evaluate the effect of silica and aluminosilicate nanocomposite coating of zirconia-based dental ceramic by a sol-gel dip-coating technique on the bond strength of veneering porcelain to the yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) in vitro. Thirty Y-TZP blocks (10 mm ×10 mm ×3 mm) were prepared and were assigned to four experimental groups (n=10/group): C, without any further surface treatment as the control group; S, sandblasted using 110 μm alumina powder; Si, silica sol dip coating + calcination; and Si/Al, aluminosilicate sol dip coating + calcination. After preparing Y-TZP samples, a 3 mm thick layer of the recommended porcelain was fired on the coated Y-TZP surface. Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray analysis were used to characterize the coating and the nature of the bonding between the coating and zirconia. To examine the zirconia-porcelain bond strength, a microtensile bond strength (μTBS) approach was chosen. FT-IR study showed the formation of silica and aluminosilicate materials. XRD pattern showed the formation of new phases consisting of Si, Al, and Zr in coated samples. SEM showed the formation of a uniform coating on Y-TZP samples. Maximum μTBS values were obtained in aluminosilicate samples, which were significantly increased compared to control and sandblasted groups (P=0.013 and Pcoating can be considered as a convenient, less expensive reliable method for improving the bond strength between dental Y-TZP ceramics and veneering porcelain.

  5. Effects of surface treatment on bond strength between dental resin agent and zirconia ceramic

    Energy Technology Data Exchange (ETDEWEB)

    Moradabadi, Ashkan [Department of Electrochemistry, Universität Ulm, Ulm (Germany); Roudsari, Sareh Esmaeily Sabet [Department of Optoelectonics, Universität Ulm, Ulm (Germany); Yekta, Bijan Eftekhari [School of Materials Engineering, Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Rahbar, Nima, E-mail: nrahbar@wpi.edu [Department of Civil and Environmental Engineering, Worcester Polytechnic Institute, Worcester, MA 01609 (United States)

    2014-01-01

    This paper presents the results of an experimental study to understand the dominant mechanism in bond strength between dental resin agent and zirconia ceramic by investigating the effects of different surface treatments. Effects of two major mechanisms of chemical and micromechanical adhesion were evaluated on bond strength of zirconia to luting agent. Specimens of yttrium-oxide-partially-stabilized zirconia blocks were fabricated. Seven groups of specimens with different surface treatment were prepared. 1) zirconia specimens after airborne particle abrasion (SZ), 2) zirconia specimens after etching (ZH), 3) zirconia specimens after airborne particle abrasion and simultaneous etching (HSZ), 4) zirconia specimens coated with a layer of a Fluorapatite-Leucite glaze (GZ), 5) GZ specimens with additional acid etching (HGZ), 6) zirconia specimens coated with a layer of salt glaze (SGZ) and 7) SGZ specimens after etching with 2% HCl (HSGZ). Composite cylinders were bonded to airborne-particle-abraded surfaces of ZirkonZahn specimens with Panavia F2 resin luting agent. Failure modes were examined under 30 × magnification and the effect of surface treatments was analyzed by scanning electron microscopy (SEM) and atomic force microscopy (AFM). SZ and HSZ groups had the highest and GZ and SGZ groups had the lowest mean shear bond strengths among all groups. Mean shear bond strengths were significantly decreased by applying a glaze layer on zirconia surfaces in GZ and SGZ groups. However, bond strengths were improved after etching process. Airborne particle abrasion resulted in higher shear bond strengths compared to etching treatment. Modes of failure varied among different groups. Finally, it is concluded that micromechanical adhesion was a more effective mechanism than chemical adhesion and airborne particle abrasion significantly increased mean shear bond strengths compared with another surface treatments. - Highlights: • Understanding the dominant mechanism of bonding

  6. Linear stability of liquid films with phase change at the interface

    International Nuclear Information System (INIS)

    Spindler, Bertrand

    1980-01-01

    The objective of this research thesis is to study the linear stability of the flow of a liquid film on an inclined plane with a heat flow on the wall and an interfacial phase change, and to highlight the influence of the phase change on the flow stability. In order to do so, the author first proposed a rational simplification of equations by studying the order of magnitude of different terms, and based on some simple hypotheses regarding flow physics. Two stability studies are then addressed, one regarding a flow with a pre-existing film, and the other regarding the flow of a condensation film. In both cases, it is assumed that there is no imposed heat flow, but that the driving effect of vapour by the liquid film is taken into account [fr

  7. Color center annealing and ageing in electron and ion-irradiated yttria-stabilized zirconia

    International Nuclear Information System (INIS)

    Costantini, Jean-Marc; Beuneu, Francois

    2005-01-01

    We have used X-band electron paramagnetic resonance (EPR) measurements at room-temperature (RT) to study the thermal annealing and RT ageing of color centers induced in yttria-stabilized zirconia (YSZ), i.e. ZrO 2 :Y with 9.5 mol% Y 2 O 3 , by swift electron and ion-irradiations. YSZ single crystals with the orientation were irradiated with 2.5 MeV electrons, and implanted with 100 MeV 13 C ions. Electron and ion beams produce the same two color centers, namely an F + -type center (singly ionized oxygen vacancy) and the so-called T-center (Zr 3+ in a trigonal oxygen local environment) which is also produced by X-ray irradiations. Isochronal annealing was performed in air up to 973 K. For both electron and ion irradiations, the defect densities are plotted versus temperature or time at various fluences. The influence of a thermal treatment at 1373 K of the YSZ single crystals under vacuum prior to the irradiations was also investigated. In these reduced samples, color centers are found to be more stable than in as-received samples. Two kinds of recovery processes are observed depending on fluence and heat treatment

  8. Preparation of mesoporous zirconia microspheres as inert matrix

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Ting [State Key Laboratory of New Ceramics and Fine Processing, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing, 100084 (China); Wang, Chen; Lv, Jinlong [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing, 100084 (China); Liang, Tongxiang, E-mail: txliang@tsinghua.edu.cn [State Key Laboratory of New Ceramics and Fine Processing, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing, 100084 (China)

    2016-12-01

    Mesoporous zirconia microspheres, with a diameter of 900 μm, were prepared as an inert accelerator driven system (ADS) transmutation element matrix by the sol-gel method. The purpose of mesopores is to improve the adsorption capacity of inert matrix fuel (IMF) for minor actinides. The study indicated that the mesoporous zirconia performance was improved after the microspheres were hydrothermally treated at 150 °C, the specific surface area increased from 28.29 m{sup 2}/g to 61.28 m{sup 2}/g, and hydrothermal treatment avoided the cracking of the microspheres. Pre-decomposition of the organics during the hydrothermal process stabilized the mesoporous structure. The average pore diameter of mesoporous microsphere was 14.3 nm. - Highlights: • Mesoporous zirconia microspheres with a diameter of 900 μm were prepared as ADS transmutation element inert matrix. • The mesoporous performance was improved after the microspheres were hydrothermally treated at 150 °C. • The specific surface area increased from 28.29 m{sup 2}/g to 61.28 m{sup 2}/g. • The hydrothermal treatment could avoid the cracking of the microspheres. • The specific surface area of mesoporous microsphere was 61.28 m{sup 2}/g and the average pore diameter was 14.3 nm.

  9. Stability of tetraphenyl butadiene thin films in liquid xenon

    International Nuclear Information System (INIS)

    Sanguino, P.; Balau, F.; Botelho do Rego, A.M.; Pereira, A.; Chepel, V.

    2016-01-01

    Tetraphenyl butadiene (TPB) is widely used in particle detectors as a wavelength shifter. In this work we studied the stability of TPB thin films when immersed in liquid xenon (LXe). The thin films were deposited on glass and quartz substrates by thermal evaporation. Morphological and chemical surface properties were monitored before and after immersion into LXe by scanning electron microscopy and X-ray photoelectron spectroscopy. No appreciable changes have been detected with these two methods. Grain size and surface chemical composition were found to be identical before and after submersion into LXe. However, the film thickness, measured via optical transmission in the ultraviolet–visible wavelength regions, decreased by 1.6 μg/cm 2 (24%) after immersion in LXe during 20 h. These results suggest the necessity of using a protective thin film over the Tetraphenyl butadiene when used as a wavelength shifter in LXe particle detectors. - Highlights: • Stability of tetraphenyl butadiene (TPB) thin films immersed in liquid xenon (LXe). • Thermally evaporated TPB thin films were immersed in LXe for 20 h. • Film morphology and chemical surface properties remained unchanged. • Surface density of the films decreased by 1.6 μg/cm 2 (24%) after immersion in LXe. • For using in LXe particle detectors, TPB films should be protected with a coating.

  10. High stability mechanisms of quinary indium gallium zinc aluminum oxide multicomponent oxide films and thin film transistors

    International Nuclear Information System (INIS)

    Lee, Ching-Ting; Lin, Yung-Hao; Lin, Jhong-Ham

    2015-01-01

    Quinary indium gallium zinc aluminum oxide (IGZAO) multicomponent oxide films were deposited using indium gallium zinc oxide (IGZO) target and Al target by radio frequency magnetron cosputtering system. An extra carrier transport pathway could be provided by the 3 s orbitals of Al cations to improve the electrical properties of the IGZO films, and the oxygen instability could be stabilized by the strong Al-O bonds in the IGZAO films. The electron concentration change and the electron mobility change of the IGZAO films for aging time of 10 days under an air environment at 40 °C and 75% humidity were 20.1% and 2.4%, respectively. The experimental results verified the performance stability of the IGZAO films. Compared with the thin film transistors (TFTs) using conventional IGZO channel layer, in conducting the stability of TFTs with IGZAO channel layer, the transconductance g m change, threshold voltage V T change, and the subthreshold swing S value change under the same aging condition were improved to 7.9%, 10.5%, and 14.8%, respectively. Furthermore, the stable performances of the IGZAO TFTs were also verified by the positive gate bias stress. In this research, the quinary IGZAO multicomponent oxide films and that applied in TFTs were the first studied in the literature

  11. High stability mechanisms of quinary indium gallium zinc aluminum oxide multicomponent oxide films and thin film transistors

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Ching-Ting, E-mail: ctlee@ee.ncku.edu.tw; Lin, Yung-Hao; Lin, Jhong-Ham [Institute of Microelectronics, Department of Electrical Engineering, Research Center for Energy Technology and Strategy (RCETS), National Cheng Kung University, Tainan, Taiwan (China)

    2015-01-28

    Quinary indium gallium zinc aluminum oxide (IGZAO) multicomponent oxide films were deposited using indium gallium zinc oxide (IGZO) target and Al target by radio frequency magnetron cosputtering system. An extra carrier transport pathway could be provided by the 3 s orbitals of Al cations to improve the electrical properties of the IGZO films, and the oxygen instability could be stabilized by the strong Al-O bonds in the IGZAO films. The electron concentration change and the electron mobility change of the IGZAO films for aging time of 10 days under an air environment at 40 °C and 75% humidity were 20.1% and 2.4%, respectively. The experimental results verified the performance stability of the IGZAO films. Compared with the thin film transistors (TFTs) using conventional IGZO channel layer, in conducting the stability of TFTs with IGZAO channel layer, the transconductance g{sub m} change, threshold voltage V{sub T} change, and the subthreshold swing S value change under the same aging condition were improved to 7.9%, 10.5%, and 14.8%, respectively. Furthermore, the stable performances of the IGZAO TFTs were also verified by the positive gate bias stress. In this research, the quinary IGZAO multicomponent oxide films and that applied in TFTs were the first studied in the literature.

  12. Theoretical studies of zirconia and defects in zirconia. Final report

    International Nuclear Information System (INIS)

    Jansen, H.J.F.

    1995-01-01

    Supported by this grant the author has performed total energy electronic structure calculations for cubic, tetragonal, and monoclinic zirconia. The results of these calculations agree with the observed ordering of structures in the phase diagram. He has developed model potentials based on the total energy results. Molecular dynamics calculations using these model potentials give a good description of the phase transitions in and the thermal properties of zirconia

  13. Enhanced stability of solid oxide fuel cells by employing a modified cathode-interlayer interface with a dense La0.6Sr0.4Co0.2Fe0.8O3-δ thin film

    Science.gov (United States)

    De Vero, Jeffrey C.; Develos-Bagarinao, Katherine; Kishimoto, Haruo; Ishiyama, Tomohiro; Yamaji, Katsuhiko; Horita, Teruhisa; Yokokawa, Harumi

    2018-02-01

    In La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) cathode/Gd-doped ceria (GDC)/yttria-stabilized zirconia (YSZ)-electrolyte based solid oxide fuel cells (SOFCs), one of the key issues affecting performance and long-term stability is the apparent deactivation of LSCF cathode by the presence of secondary phases such as SrZrO3 at the interfaces. Herein, we report that by modifying the cathode-interlayer interface with a dense LSCF thin film, the severe cation interdiffusion is suppressed especially the fast gas or surface diffusion of Sr into adjacent GDC-interlayer/YSZ-electrolyte resulting in the significant reduction of SrZrO3 formation at the interfaces improving cell stability. In order to understand the present results, the interface chemistry is carefully considered and discussed. The results show that modification of cathode-interlayer interfaces is an important strategy for improving the lifetime of SOFCs.

  14. Stability of Tl-Ba-Ca-Cu-O Superconducting Thin Films

    Energy Technology Data Exchange (ETDEWEB)

    Siegal, M.P.; Overmyer, D.L.; Venturini, E.L.; Padilla, R.R.; Provencio, P.N.

    1999-08-23

    We report the stability of TlBa{sub 2}CaCu{sub 2}O{sub 7} (Tl-1212) and Tl{sub 2}Ba{sub 2}CaCu{sub 2}O{sub 8} (T1-2212) thin films and by inference, the stability of TlBa{sub 2}Ca{sub 2}Cu{sub 3}O{sub 9} (Tl-1223) and Tl{sub 2}Ba{sub 2}Ca{sub 2}Cu{sub 3}O{sub 10} (Tl-2223) thin films, under a variety of conditions. In general, we observe that the stability behavior of the single Tl-O layer materials (Tl-1212 and Tl-1223)are similar and the double Tl-O layer materials (Tl-2212 and Tl-2223) are similar. All films are stable with repeated thermal cycling to cryogenic temperatures. Films are also stable in acetone and methanol. Moisture degrades film quality rapidly, especially in the form of vapor. Tl-1212 is more sensitive to vapor than Tl-2212. These materials are stable to high temperatures in either N{sub 2}, similar to vacuum for the cuprates, and O{sub 2} ambients. While total degradation of properties (superconducting and structural) occur at the same temperatures for all phases, 600 C in N{sub 2} and 700 C in O{sub 2}, the onset of degradation occurs at somewhat lower temperatures for Tl-1212 than for Tl-2212 films. In all cases, sample degradation is associated with Tl depletion from the films.

  15. Nickel/Yttria-stabilised zirconia cermet anodes for solid oxide fuel cells

    NARCIS (Netherlands)

    Primdahl, Søren

    1999-01-01

    This thesis deals with the porous Ni/yttria-stabilized zirconia (YSZ) cermet anode on a YSZ electrolyte for solid oxide fuel cells (SOFC). Such anodes are predominantly operated in moist hydrogen at 700°C to 1000°C, and the most important technological parameters are the polarization resistance and

  16. Amperometric sensing of NADH and ethanol using a hybrid film electrode modified with electrochemically fabricated zirconia nanotubes and poly (acid fuchsin)

    International Nuclear Information System (INIS)

    Liu, X.; Li, B.; Zhan, G.; Liu, C.; Li, C.; Ma, M.

    2012-01-01

    We report on a glassy carbon electrode (GCE) modified with a film of chitosin containing acid fuchsin (AF) adsorbed onto zirconia nanotubes. The mixture was polymerized by cyclic voltammetric scannings in the potential range from - 0. 8 V to +1. 3 V in buffer solution to produce a hybrid film electrode (nano-ZrO 2 /PAF/GCE). The morphology of the hybrid film electrode surface was characterized by scanning electron microscopy. Its electrochemical properties were studied via electrochemical impedance spectroscopy. The electrochemical response of nicotinamide adenine dinucleotide (NADH) was investigated by differential pulse voltammetry and amperometry. The results indicated that the nano-ZrO 2 /PAF/GCE possesses well synergistic catalytic activity towards NADH. Compared to an unmodified GCE, the oxidation overpotential is negatively shifted by 224 mV, and the oxidation current is significantly increased. Under optimal conditions, the amperometric response is linearly proportional to the concentration of NADH in the 1. 0 - 100. 0 μM concentration range. Ethanol also can be determined by amperometry if alcohol dehydrogenase and NADH are added to the sample. Two linear relationships between current and alcohol concentration were obtained. They cover the range from 0. 03 to 1. 0 mM, and from 1. 0 to 12. 0 mM. (author)

  17. International Conference on the Science and Technology of Zirconia (ZrO2IV) (4th) Held in Anaheim, California on Nov 1-3, 1989

    Science.gov (United States)

    1990-02-01

    niobia-zirconia powder from freshly precipitated hydrous zirconia and niobium- Different ceria stabilized TZP ceram- ammonium oxalate . Zirconia powders...is mol% Nb205 showed single orthorhombic phase an acid soluble Zr-Y-REE-Nb-Ta-sili- while this phase always coexisted with mono- cate occurring in a...C :1RCONIA, Chen-Feng Kao and Tsu-Meng BY HYDROTHERMAL PRECIPITATION METHOD, S. P Fueng, Dept of Chemical Engineering, Somiya*, Nishi-Tokyo Univ

  18. Sol-gel derived bioactive coating on zirconia: Effect on flexural strength and cell proliferation.

    Science.gov (United States)

    Shahramian, Khalil; Leminen, Heidi; Meretoja, Ville; Linderbäck, Paula; Kangasniemi, Ilkka; Lassila, Lippo; Abdulmajeed, Aous; Närhi, Timo

    2017-11-01

    The purpose of this study was to evaluate the effect of sol-gel derived bioactive coatings on the biaxial flexural strength and fibroblast proliferation of zirconia, aimed to be used as an implant abutment material. Yttrium stabilized zirconia disc-shaped specimens were cut, ground, sintered, and finally cleansed ultrasonically in each of acetone and ethanol for 5 minutes. Three experimental groups (n = 15) were fabricated, zirconia with sol-gel derived titania (TiO 2 ) coating, zirconia with sol-gel derived zirconia (ZrO 2 ) coating, and non-coated zirconia as a control. The surfaces of the specimens were analyzed through images taken using a scanning electron microscope (SEM), and a non-contact tapping mode atomic force microscope (AFM) was used to record the surface topography and roughness of the coated specimens. Biaxial flexural strength values were determined using the piston-on-three ball technique. Human gingival fibroblast proliferation on the surface of the specimens was evaluated using AlamarBlue assay™. Data were analyzed using a one-way analysis of variance (ANOVA) followed by Tukey's post-hoc test. Additionally, the biaxial flexural strength data was also statistically analyzed with the Weibull distribution. The biaxial flexural strength of zirconia specimens was unaffected (p > 0.05). Weibull modulus of TiO 2 coated and ZrO 2 coated groups (5.7 and 5.4, respectively) were lower than the control (8.0). Specimens coated with ZrO 2 showed significantly lower fibroblast proliferation compared to other groups (p sol-gel derived coatings have no influence on the flexural strength of zirconia. ZrO 2 coated specimens showed significantly lower cell proliferation after 12 days than TiO 2 coated or non-coated control. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 2401-2407, 2017. © 2016 Wiley Periodicals, Inc.

  19. Laser surface modification of Yttria Stabilized Zirconia (YSZ) thermal barrier coating on AISI H13 tool steel substrate

    Science.gov (United States)

    Reza, M. S.; Aqida, S. N.; Ismail, I.

    2018-03-01

    This paper presents laser surface modification of plasma sprayed yttria stabilized zirconia (YSZ) coating to seal porosity defect. Laser surface modification on plasma sprayed YSZ was conducted using 300W JK300HPS Nd: YAG laser at different operating parameters. Parameters varied were laser power and pulse frequency with constant residence time. The coating thickness was measured using IM7000 inverted optical microscope and surface roughness was analysed using two-dimensional Mitutoyo Surface Roughness Tester. Surface roughness of laser surface modification of YSZ H-13 tool steel decreased significantly with increasing laser power and decreasing pulse frequency. The re-melted YSZ coating showed higher hardness properties compared to as-sprayed coating surface. These findings were significant to enhance thermal barrier coating surface integrity for dies in semi-solid processing.

  20. Nucleation and strain-stabilization during organic semiconductor thin film deposition.

    Science.gov (United States)

    Li, Yang; Wan, Jing; Smilgies, Detlef-M; Bouffard, Nicole; Sun, Richard; Headrick, Randall L

    2016-09-07

    The nucleation mechanisms during solution deposition of organic semiconductor thin films determine the grain morphology and may influence the crystalline packing in some cases. Here, in-situ optical spectromicroscopy in reflection mode is used to study the growth mechanisms and thermal stability of 6,13-bis(trisopropylsilylethynyl)-pentacene thin films. The results show that the films form in a supersaturated state before transforming to a solid film. Molecular aggregates corresponding to subcritical nuclei in the crystallization process are inferred from optical spectroscopy measurements of the supersaturated region. Strain-free solid films exhibit a temperature-dependent blue shift of optical absorption peaks due to a continuous thermally driven change of the crystalline packing. As crystalline films are cooled to ambient temperature they become strained although cracking of thicker films is observed, which allows the strain to partially relax. Below a critical thickness, cracking is not observed and grazing incidence X-ray diffraction measurements confirm that the thinnest films are constrained to the lattice constants corresponding to the temperature at which they were deposited. Optical spectroscopy results show that the transition temperature between Form I (room temperature phase) and Form II (high temperature phase) depends on the film thickness, and that Form I can also be strain-stabilized up to 135 °C.

  1. Indium and gallium diffusion through zirconia in the TiN/ZrO{sub 2}/InGaAs stack

    Energy Technology Data Exchange (ETDEWEB)

    Ceballos-Sanchez, O. [CINVESTAV-Unidad Queretaro, Queretaro, Qro. 76230 (Mexico); Univ. Grenoble Alpes, F-38000 Grenoble, France and CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Martinez, E.; Guedj, C.; Veillerot, M. [Univ. Grenoble Alpes, F-38000 Grenoble, France and CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Herrera-Gomez, A. [CINVESTAV-Unidad Queretaro, Queretaro, Qro. 76230 (Mexico)

    2015-06-01

    Angle-resolved X-ray Photoelectron Spectroscopy (ARXPS) was applied to the TiN/ZrO{sub 2}/InGaAs stack to assess its thermal stability. Through a robust ARXPS analysis, it was possible to observe subtle effects such as the thermally induced diffusion of substrate atomic species (In and Ga) through the dielectric layer. The detailed characterization of the film structure allowed for assessing the depth profiles of the diffused atomic species by means of the scenarios-method. Since the quantification for the amount of diffused material was done at different temperatures, it was possible to obtain an approximate value of the activation energy for the diffusion of indium through zirconia. The result is very similar to the previously reported values for indium diffusion through alumina and through hafnia.

  2. Microstructural evolution of alumina-zirconia nanocomposites; Evolucao microestrutural de nanocompositos alumina-zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Ojaimi, C.L.; Chinelatto, A.S.A.; Chinelatto, A.L. [Universidade Estadual de Ponta Grossa (UEPG), PR (Brazil); Pallone, E.M.J.A., E-mail: christianelago@yahoo.com.br [Universidade de Sao Paulo (USP), Pirassununga, Sao Paulo, SP (Brazil). Faculdade de Zootecnia e Engenharia de Alimentos

    2012-07-01

    Ceramic materials have limited use due to their brittleness. The inclusion of nanosized particles in a ceramic matrix, which are called nanocomposites, and ceramic processing control by controlling the grain size and densification can aid in obtaining ceramic products of greater strength and toughness. Studies showed that the zirconia nano inclusions in the matrix of alumina favors an increase in mechanical properties by inhibiting the grain growth of the matrix and not by the mechanism of the transformation toughening phase of zirconia. In this work, the microstructural evolution of alumina nanocomposites containing 15% by volume of nanometric zirconia was studied. From the results it was possible to understand the sintering process of these nanocomposites. (author)

  3. Diblock Copolymer/Layered Silicate Nanocomposite Thin Film Stability

    Science.gov (United States)

    Limary, Ratchana; Green, Peter

    2000-03-01

    The stability of thin film symmetric diblock copolymers blended with layered silicate nanocomposites were examined using a combination of optical microscopy, atomic force microscopy (AFM), and X-ray diffraction (XRD). Two cases were examined PS-b-PMMA (polystyrene-b-polymethylacrylate) blended with montmorillonite stoichiometrically loaded with alkyl ammonium ions, OLS(S), and PS-b-PMMA blended with montmorillonite loaded with excess alkyl ammonium ions, OLS(E). XRD spectra show an increase in the gallery spacing of the OLSs, indicating that the copolymer chains have intercalated the layered silicates. AFM images reveal a distinct difference between the two nanocomposite thin films: regions in the vicinity of OLS(S) aggregates were depleted of material, while in the vicinity of OLS(E) aggregates, dewetting of the substrate occurred. We show that the stability of the copolymer/OLS nanocomposite films is determined by the enthalpic driving force associated with intercalation of the copolymer chains into the galleries of the modified OLS layers and by the substrate/organic modifier interactions.

  4. Significance of internal stresses for the martensitic transformation in yttria-stabilized tetragonal zirconia polycrystals during degradation

    International Nuclear Information System (INIS)

    Schmauder, S.; Schubert, H.

    1986-01-01

    Various aspects of the tetragonal (t) to monoclinic (m) transformation during degradation have been studied experimentally and theoretically in yttria-stabilized tetragonal zirconia polycrystals (Y-TZP), i.e., polycrystalline t-ZrO/sub 2/ containing Y/sub 2/O/sub 3/ in solution. Transmission electron microscopy (TEM) revealed that protruding grains at the surface of Y-TZP specimens do not transform under corrosive conditions (250 0 C, humid atmosphere) even after n annealing time of 168 h.) Eigenstresses due to anistropic thermal expansion in and around protruding and bulk grains have been calculated for Y-TZP containing 2 and 3 mol% Y/sub 2/O/sub 3/. The prominent role of these stresses on subsequent transformation nucleation during degradation is shown to agree qualitatively with an established free energy concept. The lack of complete transformation of m-ZrO/sub 2/ is attributed to characteristics of the nucleation - and growth- controlled transformation process

  5. Stability of thin liquid films containing surface active particles

    Science.gov (United States)

    Umashankar, Hariharan; Kalpathy, Sreeram; Dixit, Harish

    2017-11-01

    The stability and dynamics of thin liquid films(industrial settings like coating and printing processes and extraction of oil from porous rocks. In this study a hydrodynamic model is introduced to capture the long term evolution of a Newtonian liquid film containing insoluble surfaceactive particles.We consider here the possibility of four distinct interaction regimes based on the surface rheological effects of the particles, such that either, both or neither of Marangoni and surface viscosity effects would be present at the leading order in the governing equations. The liquid film is bounded by a rigid impermeable solid below and covered by passive air phase above.A standard linear stability analysis and nonlinear simulations are performed on the set of highly coupled partial differential evolution equations. Linear stability analysis gives insights on whether a particular imposed perturbationwavenumber will grow or decay in time and also evaluating the fastest growing wavenumber. Parametric studies for all four regimes provides a strong confirmation that surface viscosity and Marangoni effects are indeed rupture delaying effects.

  6. Tear film stability analysis system: introducing a new application for videokeratography.

    Science.gov (United States)

    Goto, Tomoko; Zheng, Xiaodong; Okamoto, Shigeki; Ohashi, Yuichi

    2004-11-01

    To review our previous studies regarding the development of a tear stability analysis system (TSAS) using videokeratography and the clinical application of TSAS for evaluation of tear film stability in patients subject to laser in situ keratomileusis (LASIK). New software, namely TSAS, was developed for the videokeratography system TMS-2N (topographic modeling system). TSAS automatically captures consecutive corneal surface images every second for 10 seconds. Corneal topographs were analyzed for tear breakup time (TMS-BUT) and tear breakup area (TMS-BUA, the ratio of breakup area to entire color-code area). First, we recruited volunteers to test the sensitivity and specificity of this new system in comparison with the routine method for tear stability analysis, tear film breakup time evaluation by slit-lamp microscope (SLE-BUT), with fluorescence staining. Second, we investigated the practicability of TSAS in dynamic evaluation of tear film stability before and after LASIK. TMS-BUT had a positive correlation with SLE-BUT, whereas TMS-BUA showed a negative correlation. Although they showed similar rates of specificity as SLE-BUT, the sensitivity rates of TMS-BUT and TMS-BUA were 97.5% and 95%, respectively, significantly higher than that of SLE-BUT (75%). The study on patients subject to LASIK showed that tear film stability significantly decreased during the early time period following LASIK and resolved at 6 months after surgery. Eyes that had abnormal TSAS evaluation tended to have higher risk of developing superficial punctuate keratitis and dry eye symptoms after LASIK, and their responses to treatment were slow. TSAS is a noninvasive and objective method with higher sensitivity for tear film stability analysis than SLE-BUT.

  7. Investigation of the oxygen exchange mechanism on Pt|yttria stabilized zirconia at intermediate temperatures: Surface path versus bulk path

    International Nuclear Information System (INIS)

    Opitz, Alexander K.; Lutz, Alexander; Kubicek, Markus; Kubel, Frank; Hutter, Herbert; Fleig, Juergen

    2011-01-01

    Highlights: → Oxygen exchange kinetics of Pt on YSZ investigated by means of Pt model electrodes. → Two different geometry dependencies of the polarization resistance identified. → At higher temperatures the oxygen exchange reaction proceeds via a Pt surface path. → At lower temperatures a bulk path through the Pt thin film electrode is discussed. - Abstract: The oxygen exchange kinetics of platinum on yttria-stabilized zirconia (YSZ) was investigated by means of geometrically well-defined Pt microelectrodes. By variation of electrode size and temperature it was possible to separate two temperature regimes with different geometry dependencies of the polarization resistance. At higher temperatures (550-700 deg. C) an elementary step located close to the three phase boundary (TPB) with an activation energy of ∼1.6 eV was identified as rate limiting. At lower temperatures (300-400 deg. C) the rate limiting elementary step is related to the electrode area and exhibited a very low activation energy in the order of 0.2 eV. From these observations two parallel pathways for electrochemical oxygen exchange are concluded. The nature of these two elementary steps is discussed in terms of equivalent circuits. Two combinations of parallel rate limiting reaction steps are found to explain the observed geometry dependencies: (i) Diffusion through an impurity phase at the TPB in parallel to diffusion of oxygen through platinum - most likely along Pt grain boundaries - as area-related process. (ii) Co-limitation of oxygen diffusion along the Pt|YSZ interface and charge transfer at the interface with a short decay length of the corresponding transmission line (as TPB-related process) in parallel to oxygen diffusion through platinum.

  8. Positron annihilation investigation and nuclear reaction analysis of helium and oxygen-implanted zirconia

    International Nuclear Information System (INIS)

    Grynszpan, R.I.; Saude, S.; Anwand, W.; Brauer, G.

    2005-01-01

    Since irradiation affects in-service properties of zirconia, we investigated the fluence dependence on production and thermal stability of defects induced by helium and oxygen-ion implantation in single crystals of yttria-fully-stabilized zirconia. In either case, depth profiling by slow positron implantation spectroscopy (SPIS) detects a distribution of vacancy-type defects peaking at 60% of the projected ion range R p . Owing to the saturation of positron-trapping occurring for low fluences, which depends on the ion mass, we could estimate a critical size of clusters ranging from 0.4 to 1.6 nm. The lack of SPIS-evidence of an open-volume excess at R p is explained by the presence of over-pressurized gas bubbles. This assumption is confirmed by Nuclear Reaction Analysis of 3 He concentration profiles, which shows that helium remains partly trapped at R p , even after annealing above 400 o C

  9. A Controlled Study on the Correlation between Tear Film Volume and Tear Film Stability in Diabetic Patients.

    Science.gov (United States)

    Eissa, Iman M; Khalil, Noha M; El-Gendy, Heba A

    2016-01-01

    Purpose. To assess the tear film quantity and correlate it with the quality and stability of the tear film in diabetics and compare them to age matched controls. Introduction. Diabetes affects tear film parameters in multiple ways. Poor metabolic control and neuropathy are postulated factors. To further understand how diabetes affects tear film parameters this study was conducted. Subjects and Methods. Tear meniscus height was measured by anterior segment OCT, along with tear thinning time, a subtype of noninvasive tear break-up time, and blinking rate per minute which were all recorded for 22 diabetic patients. Correlations between these tear film parameters were studied and then compared to 16 age matched controls. Results. A statistically significant difference was found in blinking rate between the diabetic and the control group (P = 0.002), with higher blinking rate among diabetics. All tear film parameters were negatively correlated with duration of diabetes. A positive correlation was found between tear film volume and stability. Conclusion. Diabetes affects the tear film in various ways. Diabetics should be examined for dry eye signs even in absence of symptoms which may be masked by associated neuropathy. Duration of diabetes has an impact on tear film status.

  10. Fracture of Reduced-Diameter Zirconia Dental Implants Following Repeated Insertion.

    Science.gov (United States)

    Karl, Matthias; Scherg, Stefan; Grobecker-Karl, Tanja

    Achievement of high insertion torque values indicating good primary stability is a goal during dental implant placement. The objective of this study was to evaluate whether or not two-piece implants made from zirconia ceramic may be damaged as a result of torque application. A total of 10 two-piece zirconia implants were repeatedly inserted into polyurethane foam material with increasing density and decreasing osteotomy size. The insertion torque applied was measured, and implants were checked for fractures by applying the fluorescent penetrant method. Weibull probability of failure was calculated based on the recorded insertion torque values. Catastrophic failures could be seen in five of the implants from two different batches at insertion torques ranging from 46.0 to 70.5 Ncm, while the remaining implants (all belonging to one batch) survived. Weibull probability of failure seems to be low at the manufacturer-recommended maximum insertion torque of 35 Ncm. Chipping fractures at the thread tips as well as tool marks were the only otherwise observed irregularities. While high insertion torques may be desirable for immediate loading protocols, zirconia implants may fracture when manufacturer-recommended insertion torques are exceeded. Evaluating bone quality prior to implant insertion may be useful.

  11. The synthesis and certification of zirconia certified reference materials (CRM) as a processed result of zircon sand

    International Nuclear Information System (INIS)

    Samin; Supriyanto C; Sajima

    2016-01-01

    In order to support the pilot plant of zirconia production at PSTA-BATAN, synthesis and certification of zirconia certified reference materials (CRM) is absolutely needed. The synthesis and certification of zirconia CRM has been carried out from the row material of zirconium oxide chloride as a processed result of Kalimantan zircon sand. Zirconium oxide chloride dissolved in distilled water (1:10), added by ammonia at pH 10, it was formed a zirconium hydroxide precipitate. Zirconium hydroxide was heated at 110 °C and calcination at a temperature of 900 °C in order to obtain zirconia. Zirconia was dried at 110 °C, crushed and sieved to obtain a grain size of 200 mesh qualify. Zirconia powder was homogenized and then treated by homogenation test, stabilization test, characterization test and water content test. In the evaluation of the test data showed that candidate of CRM zirconia were homogeneous, stable, contain the monoklin of baddeleyite minerals and the water content obtained was less than 1%. It was concluded that zirconia powder are already physical qualified as CRM. Certificate of test results on parameters of zirconia CRM from 7 accredited laboratories using statistical methods obtained 9 oxides were ZrO_2 : (95.422 ± 0.027)%; HfO_2: (1.443 ± 0.004)%; SiO_2 : (0.535 ± 0.002)%; Al_2O_3 : (0.362 ± 0.012)%; Fe_2O_3 : (0.028 ± 0.003)%; TiO_2: (0.026 ± 0.001) %; Na_2O: (0.262 ± 0.026)%; Nd_2O_3 : (0.0367 ± 0.007)%; CeO_2: (0.131 ± 0.013)%. This certification was traceable to BCS-CRM No. 358 zirconia from BAS-France. (author)

  12. Alumina reinforced tetragonal zirconia (TZP) composites. Final technical report, July 1, 1993--December 31, 1996

    International Nuclear Information System (INIS)

    Shetty, D.K.

    1997-01-01

    This final technical report summarizes the significant research results obtained during the period July 1, 1993 through December 31, 1996 in the DOE-supported research project entitled, open-quotes Alumina Reinforced Tetragonal Zirconia (TZP) Compositesclose quotes. The objective of the research was to develop high-strength and high-toughness ceramic composites by combining mechanisms of platelet, whisker or fiber reinforcement with transformation toughening. The approach used included reinforcement of Celia- or yttria-partially-stabilized zirconia (Ce-TZP or Y-TZP) with particulates, platelets, or continuous filaments of alumina

  13. Characterization of Lanthanum Ferric Cobaltite doped with Strontium (LSCF) films deposited by spray-pyrolysis for application as cathode in PaCOS-TI; Caracterizacao de filmes de CFLE depositados por spray-pirolise para utilizacao como catodo em PaCOS-TI

    Energy Technology Data Exchange (ETDEWEB)

    Almeida, L.S.; Guimaraes, V.F.; Paes Junior, H.R. [Universidade Estadual do Norte Fluminense Darcy Ribeiro (UENF), Campos dos Goytacazes, RJ (Brazil). Lab. de Materiais Avancados], Emails: laryssadsa@yahoo.com.br, valtencyguimaraes@yahoo.com.br, herval@uenf.br

    2010-07-01

    The lanthanum ferric cobaltite doped with strontium (LSCF) is a ceramic material with the perovskite structure that stands out in the field of research for its use as cathode in solid oxide fuel cells at intermediate temperatures (IT-SOFC). The films were synthesized by spray-pyrolysis technique on 8% mol Yttria stabilized zirconia (YSZ) substrates. It was studied the influence of heat treatment temperatures (600-1000 deg C) on the properties of the films under the conditions of treatment during four hours. Samples were tested electrically by measuring the variation of electrical conductivity with temperature, structurally by X-ray diffraction (XRD) and morphologically by scanning electron microscopy (SEM). The films heat treated at 700 deg C for 4 hours showed better performance for application as cathode. (author)

  14. Effect of Co3O4 addition on densification of 8 mil% Yttria stabilized zirconia

    International Nuclear Information System (INIS)

    Grilo, J.P.F.; Neto, P.P.B.; Souza, G.L.; Macedo, D.A.; Paskocimas, C.A.; Nascimento, R.M.

    2012-01-01

    8 mol% Yttria stabilized zirconia (8YSZ) is the most common material used as electrolyte in solid oxide fuel cells (SOFC). In recent years, many research efforts have been focused on trying to reduce its sintering temperature with a view of the possibility of co-sintering of the anode/electrolyte interface. In this context, the use of sintering aids is a major technological routes used to enhance the densification of YSZ. In this work, Co 3 O 4 powders obtained by the Pechini method were used as sintering aids for 8YSZ. The effect of the addition of Co 3 O 4' (between 0.075 and 1 wt.%) in the densification of 8YSZ was investigated by X-ray diffraction, electron microscopy and density measurements. The results indicated that the optimum temperature sintering decreases with increasing content of Co 3 O 4 . The best content of the sintering aid was 0.25 wt.%, for this content was obtained value of relative density above 90% after sintering at temperatures as low as 1350 deg C. (author)

  15. Structural and Chemical Analysis of the Zirconia-Veneering Ceramic Interface.

    Science.gov (United States)

    Inokoshi, M; Yoshihara, K; Nagaoka, N; Nakanishi, M; De Munck, J; Minakuchi, S; Vanmeensel, K; Zhang, F; Yoshida, Y; Vleugels, J; Naert, I; Van Meerbeek, B

    2016-01-01

    The interfacial interaction of veneering ceramic with zirconia is still not fully understood. This study aimed to characterize morphologically and chemically the zirconia-veneering ceramic interface. Three zirconia-veneering conditions were investigated: 1) zirconia-veneering ceramic fired on sandblasted zirconia, 2) zirconia-veneering ceramic on as-sintered zirconia, and 3) alumina-veneering ceramic (lower coefficient of thermal expansion [CTE]) on as-sintered zirconia. Polished cross-sectioned ceramic-veneered zirconia specimens were examined using field emission gun scanning electron microscopy (Feg-SEM). In addition, argon-ion thinned zirconia-veneering ceramic interface cross sections were examined using scanning transmission electron microscopy (STEM)-energy dispersive X-ray spectrometry (EDS) at high resolution. Finally, the zirconia-veneering ceramic interface was quantitatively analyzed for tetragonal-to-monoclinic phase transformation and residual stress using micro-Raman spectroscopy (µRaman). Feg-SEM revealed tight interfaces for all 3 veneering conditions. High-resolution transmission electron microscopy (HRTEM) disclosed an approximately 1.0-µm transformed zone at sandblasted zirconia, in which distinct zirconia grains were no longer observable. Straight grain boundaries and angular grain corners were detected up to the interface of zirconia- and alumina-veneering ceramic with as-sintered zirconia. EDS mapping disclosed within the zirconia-veneering ceramic a few nanometers thick calcium/aluminum-rich layer, touching the as-sintered zirconia base, with an equally thick silicon-rich/aluminum-poor layer on top. µRaman revealed t-ZrO2-to-m-ZrO2 phase transformation and residual compressive stress at the sandblasted zirconia surface. The difference in CTE between zirconia- and the alumina-veneering ceramic resulted in residual tensile stress within the zirconia immediately adjacent to its interface with the veneering ceramic. The rather minor chemical

  16. Computational study of structures of yttria-stabilised zirconia/strontium titanate multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Cheah, Wei Li; Finnis, Mike [Imperial College London (United Kingdom)

    2012-07-01

    Growing interest in the field of functional oxide multilayered nano-heterostructures may be attributed to their unusual interfacial properties that are not yet fully understood. For instance, the nature of the unexpectedly high conductivity reported in a trilayer of 1-nm thick epitaxial yttria-stabilised zirconia (YSZ) film sandwiched between strontium titanate (STO) layers still remains controversial. In an effort to investigate the source of conductivity in this system, we first establish an unexpected YSZ lattice within such hetero-system using a combination of techniques - a genetic algorithm in which the interatomic forces are described by classical pair potentials, and a pseudo-potential-based DFT method as implemented in the plane-wave code CASTEP. We find this structure to be more stable than an anatase zirconia epitaxial lattice on STO which has been previously found as the most stable structure if yttrium dopants were not incorporated within the zirconia layer. Analysis of charge density of this new structure reveals not localised vacancies, but several small pockets of low charge densities for each expected vacancy. We examine the mobility of oxide ions in the hetero-system using classical molecular dynamics simulation and attempt to relate the results to experimental conductivity values.

  17. YSZ thin films deposited on NiO-CSZ anodes by pulsed injection MOCVD for intermediate temperature-SOFC applications

    International Nuclear Information System (INIS)

    Garcia, G.; Pardo, J.A.; Santiso, J.; Merino, R.I.; Orera, V.M.; Larrea, A.; Pena, J.I.; Laguna-Bercero, M.A.; Figueras, A.

    2004-01-01

    Yttria-stabilized zirconia (YSZ) films are prepared on NiO-CaSZ by PIMOCVD (pulsed injection metal organic chemical vapor deposition). High quality, 5 to 10 μm thick, totally dense YSZ layers are prepared by controlling the oxygen partial pressure during the deposition. YSZ solid electrolyte deposition onto Ni-YSZ eutectic substrate is found to be a promising combination with regard to intermediate-temperature solid-oxide fuel cell applications. (Abstract Copyright [2004], Wiley Periodicals, Inc.)

  18. Stability and modification of passive films of new PUREX-materials

    International Nuclear Information System (INIS)

    Schultze, J.W.; Siemensmeyer, B.; Patzelt, T.

    1991-10-01

    The valve metals Ti, Zr and others and their alloys can be used in nitric acid solutions of the Purex process. They are protected by passive films which are stable at least at low temperatures and concentrations. Electrochemical investigations and corrosion tests are applied to check improvements of the materials. Niobium can be used to substitute the very expensive tantalum. Electrochemical and analytical investigations show the formation of the corrosion stable oxide film. Special problems are treated, such as the stability of welded joints or the influence of radioactive irradiation. α-radiation and hot atoms are simulated by ion implantation, β- and γ-radiation are simulated by laser light. In both types of experiments no decrease of stability is indicated. The alloy Ti5Ta is more stable than Ti, but it is not as good as Ta. Other alloys of Ti were investigated, but they are not suitable for the Purex process. New protection layers are tested. With respect to their preparation as well as their corrosion stability, ANOF-films are promising, but TiN-films are not stable enough. (orig.) With 71 refs., 7 tabs., 71 figs [de

  19. Investigating On Colour Stability Conditions Of Postirradiation Radiochromic Film Dosimeter

    International Nuclear Information System (INIS)

    Nguyen Nguyet Dieu; Doan Binh; Pham Thu Hong; Cao Van Chung; Nguyen Thanh Duoc

    2011-01-01

    B3 dosimeter is a thin film with average thickness of 0.0194 mm, which is supplied by the Gex company, the United States. This dosimeter was influenced by many factors: light, temperature, humidity during and after irradiation process. In fact, B3 film dosimeters will be stable under certain conditions such as tightly sealed packs, controlled irradiation and stored temperature after irradiated. Therefore, investigation of the stability effect of postirradiated B3 film dosimeters on the heating temperature, heating time and storing time is carried out before the absorbed dose is read and followed standard reading procedures. When exposed to ionizing radiation, the dosimeters change from colorless to colour. The absorbed doses are read on a Genesys 20 spectrophotometer at a wavelength of 544 nm. Absorbed dose range is investigated from 0.55 to 80 kGy. Experimental results were indicated that colour stability of the postirradiated dosimeters at a temperature of 65 ± 3 o C for 30 minutes and keeping them in desiccator for 5 minutes before read out. Under these conditions, colour stability of B3 film dosimeter has maintained for 3 months. (author)

  20. Electrical characterization of zirconia-niobium and zirconia-titanium composites

    International Nuclear Information System (INIS)

    Reis, S.T. dos.

    1993-01-01

    Zirconia-niobium and zirconia-titanium composites were made by powder mixing, cold pressing, and vacuum sintering at 1600 0 C. The metallic particles were added in the proportion of 0-50% by volume. Electrical resistivity measurements were performed by the two probes and the four probes d.c. method as a function of metallic particle concentration. Electrical resistivity of these composites decreased sharply in the region of 30-40 vol% Nb or Ti, in agreement with the percolation theory. Tests in an induction furnace were performed to check the self-heating response of these composites. (author). 33 refs, 40 figs, 11 tabs

  1. High Stability Performance of Quinary Indium Gallium Zinc Aluminum Oxide Films and Thin-Film Transistors Deposited Using Vapor Cooling Condensation Method

    Science.gov (United States)

    Lin, Yung-Hao; Lee, Ching-Ting

    2017-08-01

    High-quality indium gallium zinc aluminum oxide (IGZAO) thin films with various Al contents have been deposited using the vapor cooling condensation method. The electron mobility of the IGZAO films was improved by 89.4% on adding Al cation to IGZO film. The change in the electron concentration and mobility of the IGZAO films was 7.3% and 7.0%, respectively, when the temperature was changed from 300 K to 225 K. These experimental results confirm the high performance and stability of the IGZAO films. The performance stability mechanisms of IGZAO thin-film transistors (TFTs) were investigated in comparison with IGZO TFTs.

  2. Effects of NiO addition on the densification, microstructure and electrical conductivity of Yttria fully-stabilized zirconia

    International Nuclear Information System (INIS)

    Batista, Rafael Morgado

    2010-01-01

    The effects produced by NiO addition to yttria fully-stabilized zirconia were systematically investigated. Commercial zirconia-8 mol% yttria, nickel acetate, nitrate, trihydroxycarbonate and nickel oxide were used as starting materials. The NiO content varied from 0.5 to 5 mol%, and the compositions were prepared by mechanically mixing the starting materials in the stoichiometric proportions. Densification studies carried out by density and dilatometry measurements revealed that the maximum shrinkage (∼16-∼20%) depends on the type of nickel precursor. In the second sintering stage the linear shrinkage increased with increasing NiO content (precursor: nickel trihydroxy-carbonate). In the first sintering stage, the activation energy for grain boundary diffusion changed according to the additive precursor, being lower for the oxide and higher for the trihydroxy-carbonate. In the second stage, when the major part of porosity is eliminated, the maximum shrinkage rate temperatures were found to be independent on the precursor except when nickel acetate is used. The solubility limit at 1350 degree C is 1.48% as determined by X-ray diffraction. Above the solubility limit the excess NiO is retained as a second randomly distributed phase. The main effect of the additive in the ceramic microstructure is to increase the average grain size. The electrical measurements showed that the additive did not produce any significant effect in the grain conductivity irrespective of the sintering time, except when the precursor material was nickel oxide. In this case, the grain conductivity increased with increasing sintering time. This effect is attributed to the crystallite size of the nickel oxide precursor, which is higher than that of 8YSZ, slowing down the formation of solid solution. However, the grain conductivity of samples prepared with nickel trihydroxy-carbonate precursor is slightly lower than those of other samples. The samples sintered for 15 h exhibited an additional

  3. Film packed lithium-ion battery with polymer stabilizer

    International Nuclear Information System (INIS)

    Satoh, Masaharu; Nakahara, Kentaro

    2004-01-01

    The 1600 mAh class of film packed lithium-ion battery has been fabricated with the polymer stabilizer. The adhesive polymer covered with fluorinated polymer beads enables to penetrate into the prismatically wounded jerry-roll layers and connects the electrode layers and separator film. The battery demonstrates the improved properties after repeating the charge and discharge processes and should be useful for the various electronics equipment such as notebook type computer

  4. 3D-printing zirconia implants; a dream or a reality? An in-vitro study evaluating the dimensional accuracy, surface topography and mechanical properties of printed zirconia implant and discs.

    Science.gov (United States)

    Osman, Reham B; van der Veen, Albert J; Huiberts, Dennis; Wismeijer, Daniel; Alharbi, Nawal

    2017-11-01

    The aim of this study was to evaluate the dimensional accuracy, surface topography of a custom designed, 3D-printed zirconia dental implant and the mechanical properties of printed zirconia discs. A custom designed implant was 3D-printed in zirconia using digital light processing technique (DLP). The dimensional accuracy was assessed using the digital-subtraction technique. The mechanical properties were evaluated using biaxial flexure strength test. Three different build angles were adopted to print the specimens for the mechanical test; 0°(Vertical), 45° (Oblique) and 90°(Horizontal) angles. The surface topography, crystallographic phase structure and surface roughness were evaluated using scanning electron microscopy analysis (SEM), X-ray diffractometer and confocal microscopy respectively. The printed implant was dimensionally accurate with a root mean square (RMSE) value of 0.1mm. The Weibull analysis revealed a statistically significant higher characteristic strength (1006.6MPa) of 0° printed specimens compared to the other two groups and no significant difference between 45° (892.2MPa) and 90° (866.7MPa) build angles. SEM analysis revealed cracks, micro-porosities and interconnected pores ranging in size from 196nm to 3.3µm. The mean Ra (arithmetic mean roughness) value of 1.59µm (±0.41) and Rq (root mean squared roughness) value of 1.94µm (±0.47) was found. A crystallographic phase of primarily tetragonal zirconia typical of sintered Yttria tetragonal stabilized zirconia (Y-TZP) was detected. DLP prove to be efficient for printing customized zirconia dental implants with sufficient dimensional accuracy. The mechanical properties showed flexure strength close to those of conventionally produced ceramics. Optimization of the 3D-printing process parameters is still needed to improve the microstructure of the printed objects. Copyright © 2017 Elsevier Ltd. All rights reserved.

  5. CAD/CAM Zirconia vs. slip-cast glass-infiltrated Alumina/Zirconia all-ceramic crowns: 2-year results of a randomized controlled clinical trial

    Directory of Open Access Journals (Sweden)

    Murat Cavit Çehreli

    2009-02-01

    Full Text Available The aim of this randomized controlled clinical trial was to compare the early clinical outcome of slip-cast glass-infiltrated Alumina/Zirconia and CAD/CAM Zirconia all-ceramic crowns. A total of 30 InCeram® Zirconia and Cercon® Zirconia crowns were fabricated and cemented with a glass ionomer cement in 20 patients. At baseline, 6-month, 1-year, and 2-year recall appointments, Californian Dental Association (CDA quality evaluation system was used to evaluate the prosthetic replacements, and plaque and gingival index scores were used to explore the periodontal outcome of the treatments. No clinical sign of marginal discoloration, persistent pain and secondary caries was detected in any of the restorations. All InCeram® Zirconia crowns survived during the 2-year period, although one nonvital tooth experienced root fracture coupled with the fracture of the veneering porcelain of the restoration. One Cercon® Zirconia restoration fractured and was replaced. According to the CDA criteria, marginal integrity was rated excellent for InCeram® Zirconia (73% and Cercon® Zirconia (80% restorations, respectively. Slight color mismatch rate was higher for InCeram® Zirconia restorations (66% than Cercon® Zirconia (26% restorations. Plaque and gingival index scores were mostly zero and almost constant over time. Time-dependent changes in plaque and gingival index scores within and between groups were statistically similar (p>0.05. This clinical study demonstrates that single-tooth InCeram® Zirconia and Cercon® Zirconia crowns have comparable early clinical outcome, both seem as acceptable treatment modalities, and most importantly, all-ceramic alumina crowns strengthened by 25% zirconia can sufficiently withstand functional load in the posterior zone.

  6. Effect of an experimental zirconia-silica coating technique on micro tensile bond strength of zirconia in different priming conditions

    NARCIS (Netherlands)

    Chen, C.; Kleverlaan, C.J.; Feilzer, A.J.

    2012-01-01

    Objectives This study aimed to evaluate the adhesive properties of a MDP-containing resin cement to a colored zirconia ceramic, using an experimental zirconia-silica coating technique with different priming conditions. Methods 18 zirconia ceramic discs (Cercon base colored) were divided into two

  7. The Structure and Stability of Molybdenum Ditelluride Thin Films

    Directory of Open Access Journals (Sweden)

    Zhouling Wang

    2014-01-01

    Full Text Available Molybdenum-tellurium alloy thin films were fabricated by electron beam evaporation and the films were annealed in different conditions in N2 ambient. The hexagonal molybdenum ditelluride thin films with well crystallization annealed at 470°C or higher were obtained by solid state reactions. Thermal stability measurements indicate the formation of MoTe2 took place at about 350°C, and a subtle weight-loss was in the range between 30°C and 500°C. The evolution of the chemistry for Mo-Te thin films was performed to investigate the growth of the MoTe2 thin films free of any secondary phase. And the effect of other postdeposition treatments on the film characteristics was also investigated.

  8. A Controlled Study on the Correlation between Tear Film Volume and Tear Film Stability in Diabetic Patients

    Directory of Open Access Journals (Sweden)

    Iman M. Eissa

    2016-01-01

    Full Text Available Purpose. To assess the tear film quantity and correlate it with the quality and stability of the tear film in diabetics and compare them to age matched controls. Introduction. Diabetes affects tear film parameters in multiple ways. Poor metabolic control and neuropathy are postulated factors. To further understand how diabetes affects tear film parameters this study was conducted. Subjects and Methods. Tear meniscus height was measured by anterior segment OCT, along with tear thinning time, a subtype of noninvasive tear break-up time, and blinking rate per minute which were all recorded for 22 diabetic patients. Correlations between these tear film parameters were studied and then compared to 16 age matched controls. Results. A statistically significant difference was found in blinking rate between the diabetic and the control group (P=0.002, with higher blinking rate among diabetics. All tear film parameters were negatively correlated with duration of diabetes. A positive correlation was found between tear film volume and stability. Conclusion. Diabetes affects the tear film in various ways. Diabetics should be examined for dry eye signs even in absence of symptoms which may be masked by associated neuropathy. Duration of diabetes has an impact on tear film status.

  9. Effect of Graphene-EC on Ag NW-Based Transparent Film Heaters: Optimizing the Stability and Heat Dispersion of Films.

    Science.gov (United States)

    Cao, Minghui; Wang, Minqiang; Li, Le; Qiu, Hengwei; Yang, Zhi

    2018-01-10

    To optimize the performance of silver nanowire (Ag NW) film heaters and explore the effect of graphene on a film, we introduced poly(3,4-ethylenedioxythiophene):poly(4-styrenesulfonate) (PEDOT:PSS) and graphene modified with ethyl cellulose (graphene-EC) into the film. The high-quality and well-dispersed graphene-EC was synthesized from graphene obtained by electrochemical exfoliation as a precursor. The transparent film heaters were fabricated via spin-coating. With the assistance of graphene-EC, the stability of film heaters was greatly improved, and the conductivity was optimized by adjusting the Ag NW concentration. The film heaters exhibited a fast and accurate response to voltage, accompanied by excellent environmental endurance, and there was no significant performance degradation after being operated for a long period of time. These results indicate that graphene-EC plays a crucial role in optimizing film stability and heat dispersion in the film. The Ag NW/PEDOT:PSS-doped graphene-EC film heaters show a great potential in low-cost indium-tin-oxide-free flexible transparent electrodes, heating systems, and transparent film heaters.

  10. An overview of monolithic zirconia in dentistry

    Directory of Open Access Journals (Sweden)

    Özlem Malkondu

    2016-07-01

    Full Text Available Zirconia restorations have been used successfully for years in dentistry owing to their biocompatibility and good mechanical properties. Because of their lack of translucency, zirconia cores are generally veneered with porcelain, which makes restorations weaker due to failure of the adhesion between the two materials. In recent years, all-ceramic zirconia restorations have been introduced in the dental sector with the intent to solve this problem. Besides the elimination of chipping, the reduced occlusal space requirement seems to be a clear advantage of monolithic zirconia restorations. However, scientific evidence is needed to recommend this relatively new application for clinical use. This mini-review discusses the current scientific literature on monolithic zirconia restorations. The results of in vitro studies suggested that monolithic zirconia may be the best choice for posterior fixed partial dentures in the presence of high occlusal loads and minimal occlusal restoration space. The results should be supported with much more in vitro and particularly in vivo studies to obtain a final conclusion.

  11. Adherent zirconia films by reactive ion implantation

    International Nuclear Information System (INIS)

    Bunker, S.N.; Armini, A.J.

    1993-01-01

    Conventional methods of forming ceramic coatings on metal substrates, such as CVD or plasma spray, typically retain a sharp interface and may have adhesion problems. In order to produce a completely mixed interface for better adhesion, a method using reactive ion implantation was used which can grow a thick stoichiometric film of an oxide ceramic starting from inside the substrate. Zirconium oxide ceramic films have been produced by this technique using a high-energy zirconium ion beam in an oxygen gas ambient. Compositional data are shown based on Auger electron spectroscopy of the film. Tribological properties of the layer were determined from wear and friction measurements using a pin-on-disk test apparatus. The adhesion was measured both by a scratch technique as well as by thermal shock. Results show an extremely adherent ZrO 2 film with good tribological properties

  12. Film packed lithium-ion battery with polymer stabilizer

    Energy Technology Data Exchange (ETDEWEB)

    Satoh, Masaharu; Nakahara, Kentaro [NEC Corp., Environment and Material Research Labs., Kawasaki, Kanagawa (Japan)

    2004-11-30

    The 1600 mAh class of film packed lithium-ion battery has been fabricated with the polymer stabilizer. The adhesive polymer covered with fluorinated polymer beads enables to penetrate into the prismatically wound jerry-roll layers and connects the electrode layers and separator film. The battery demonstrates the improved properties after repeating the charge and discharge processes and should be useful for the various electronic equipment such as notebook type computers. (Author)

  13. Thermal propagation and stability in superconducting films

    International Nuclear Information System (INIS)

    Gray, K.E.; Kampwirth, R.T.; Zasadzinski, J.F.; Ducharme, S.P.

    1983-01-01

    Thermal propagation and stable hot spots (normal domains) are studied in various high Tsub(c) superconducting films (Nb 3 Sn, Nb, NbN and Nb 3 Ge). A new energy balance is shown to give reasonable quantitative agreement of the dependence of the propagation velocity on the length of short normal domains. The steady state (zero velocity) measurements indicate the existence of two distinct situations for films on high thermal conductivity (sapphire) substrates. For low power per unit area the film and substrate have the same temperature, and the thermal properties of the substrate dominate. However, for higher power densities in short hot spots, the coupling is relatively weak and the thermal properties of the film alone are important. Here a connection is made between the critical current stability of superconducting films and a critical hot spot size for thermal propagation. As a result efficient heat removal is shown to dominate the stabilisation of superconducting films. The strong and weak coupling situations also lead to modifications of the models for propagation velocities on sapphire substrates. Self-healing of hot spots and other phenomena in superconducting film are explained. The potential use of the thermal propagation model in applications of superconductors, especially switches is discussed. (author)

  14. Study on Ablation Behavior of Phenolic Composites Prepared with Different Amounts of Zirconia and Asbestos Fiber

    Directory of Open Access Journals (Sweden)

    Mir Asad Mirzapour

    2012-12-01

    Full Text Available Ablative materials play a strategic role in aerospace industry. These materialsproduce a thermal protection system which protects the structure, theaerodynamic surfaces and the payload of vehicles and probes duringhypersonic flight through a planetary atmosphere. In this work, we investigated the effect of refractory zirconium oxide on mechanical, heat stability and ablation properties of asbestos/phenolic/zirconia composites. The asbestos/phenolic/zirconia composites were produced with different percentages of zirconia filler from 7 to 21% with average size of 7 μm and different number of layers of asbestos, say 3 to 6 layers. These ablative composites were made by an autoclave curing cycle process.The densities of the composites were in the range of 1.68 to 1.88 g/cm3. Ablation properties of composites were determined by oxy-acetylene torch environment and burn-through time, erosion rates and back surface temperature in the first required 20 seconds. Thermal stability of the produced materials was estimated by means of thermal gravimetric analysis, in both air and nitrogen which consisted of dynamic scans at a heating rate of 10°C/min from 30 to 1000°C with bulk samples of about 20±1 mg. The results showed that when the amount of zirconia was raised from 7% to 21%, the erosion rate and the back surface temperature of composites increased byabout 24% and 26% respectively, and the heat capacity of the composites increased by about 85%. Also, the result showed that when the thickness of composites of 4.2 mm was increased to 10.1mm the burn-through time raised by about 226% and erosion rate dropped by about 41%. These composites displayed the maximum flexural strength when the amount of zirconia was about 14%.

  15. Structure, electrical characteristics, and high-temperature stability of aerosol jet printed silver nanoparticle films

    Energy Technology Data Exchange (ETDEWEB)

    Rahman, Md Taibur; McCloy, John; Panat, Rahul, E-mail: rahul.panat@wsu.edu, E-mail: rvchintalapalle@utep.edu [School of Mechanical and Materials Engineering, Washington State University, Pullman, Washington 99163 (United States); Ramana, C. V., E-mail: rahul.panat@wsu.edu, E-mail: rvchintalapalle@utep.edu [Department of Mechanical Engineering, University of Texas at El Paso, El Paso, Texas 79968 (United States)

    2016-08-21

    Printed electronics has emerged as a versatile eco-friendly fabrication technique to create sintered nanoparticle (NP) films on arbitrary surfaces with an excellent control over the film microstructure. While applicability of such films for high-temperature applications is not explored previously, herein we report the high-temperature electrical stability of silver (Ag) metal NP films fabricated using an Aerosol Jet based printing technique and demonstrate that this behavior is dictated by changes in the film microstructure. In-situ high temperature (24–500 °C) impedance spectroscopy measurements show that the real part of the impedance increases with increasing temperature up to 150 °C, at which point a decreasing trend prevails until 300 °C, followed again by an increase in impedance. The electrical behavior is correlated with the in-situ grain growth of the Ag NP films, as observed afterwards by scanning electron microscopy and X-ray diffraction (XRD), and could be tailored by controlling the initial microstructure through sintering conditions. Using combined diffraction and spectroscopic analytical methods, it is demonstrated the Aerosol Jet printed Ag NP films exhibit enhanced thermal stability and oxidation resistance. In addition to establishing the conditions for stability of Ag NP films, the results provide a fundamental understanding of the effect of grain growth and reduction in grain boundary area on the electrical stability of sintered NP films.

  16. Structure, electrical characteristics, and high-temperature stability of aerosol jet printed silver nanoparticle films

    International Nuclear Information System (INIS)

    Rahman, Md Taibur; McCloy, John; Panat, Rahul; Ramana, C. V.

    2016-01-01

    Printed electronics has emerged as a versatile eco-friendly fabrication technique to create sintered nanoparticle (NP) films on arbitrary surfaces with an excellent control over the film microstructure. While applicability of such films for high-temperature applications is not explored previously, herein we report the high-temperature electrical stability of silver (Ag) metal NP films fabricated using an Aerosol Jet based printing technique and demonstrate that this behavior is dictated by changes in the film microstructure. In-situ high temperature (24–500 °C) impedance spectroscopy measurements show that the real part of the impedance increases with increasing temperature up to 150 °C, at which point a decreasing trend prevails until 300 °C, followed again by an increase in impedance. The electrical behavior is correlated with the in-situ grain growth of the Ag NP films, as observed afterwards by scanning electron microscopy and X-ray diffraction (XRD), and could be tailored by controlling the initial microstructure through sintering conditions. Using combined diffraction and spectroscopic analytical methods, it is demonstrated the Aerosol Jet printed Ag NP films exhibit enhanced thermal stability and oxidation resistance. In addition to establishing the conditions for stability of Ag NP films, the results provide a fundamental understanding of the effect of grain growth and reduction in grain boundary area on the electrical stability of sintered NP films.

  17. Structure, electrical characteristics, and high-temperature stability of aerosol jet printed silver nanoparticle films

    Science.gov (United States)

    Rahman, Md Taibur; McCloy, John; Ramana, C. V.; Panat, Rahul

    2016-08-01

    Printed electronics has emerged as a versatile eco-friendly fabrication technique to create sintered nanoparticle (NP) films on arbitrary surfaces with an excellent control over the film microstructure. While applicability of such films for high-temperature applications is not explored previously, herein we report the high-temperature electrical stability of silver (Ag) metal NP films fabricated using an Aerosol Jet based printing technique and demonstrate that this behavior is dictated by changes in the film microstructure. In-situ high temperature (24-500 °C) impedance spectroscopy measurements show that the real part of the impedance increases with increasing temperature up to 150 °C, at which point a decreasing trend prevails until 300 °C, followed again by an increase in impedance. The electrical behavior is correlated with the in-situ grain growth of the Ag NP films, as observed afterwards by scanning electron microscopy and X-ray diffraction (XRD), and could be tailored by controlling the initial microstructure through sintering conditions. Using combined diffraction and spectroscopic analytical methods, it is demonstrated the Aerosol Jet printed Ag NP films exhibit enhanced thermal stability and oxidation resistance. In addition to establishing the conditions for stability of Ag NP films, the results provide a fundamental understanding of the effect of grain growth and reduction in grain boundary area on the electrical stability of sintered NP films.

  18. Mixed conductivity, structural and microstructural characterization of titania-doped yttria tetragonal zirconia polycrystalline/titania-doped yttria stabilized zirconia composite anode matrices

    International Nuclear Information System (INIS)

    Colomer, M.T.; Maczka, M.

    2011-01-01

    Taking advantage of the fact that TiO 2 additions to 8YSZ cause not only the formation of a titania-doped YSZ solid solution but also a titania-doped YTZP solid solution, composite materials based on both solutions were prepared by solid state reaction. In particular, additions of 15 mol% of TiO 2 give rise to composite materials constituted by 0.51 mol fraction titania-doped yttria tetragonal zirconia polycrystalline and 0.49 mol fraction titania-doped yttria stabilized zirconia (0.51TiYTZP/0.49TiYSZ). Furthermore, Y 2 (Ti 1-y Zr y ) 2 O 7 pyrochlore is present as an impurity phase with y close to 1, according to FT-Raman results. Lower and higher additions of titania than that of 15 mol%, i.e., x=0, 5, 10, 20, 25 and 30 mol% were considered to study the evolution of 8YSZ phase as a function of the TiO 2 content. Furthermore, zirconium titanate phase (ZrTiO 4 ) is detected when the titania content is equal or higher than 20 mol% and this phase admits Y 2 O 3 in solid solution according to FE-SEM-EDX. The 0.51TiYTZP/0.49TiYSZ duplex material was selected in this study to establish the mechanism of its electronic conduction under low oxygen partial pressures. In the pO 2 range from 0.21 to 10 -7.5 atm. the conductivity is predominantly ionic and constant over the range and its value is 0.01 S/cm. The ionic plus electronic conductivity is 0.02 S/cm at 1000 o C and 10 -12.3 atm. Furthermore, the onset of electronic conductivity under reducing conditions exhibits a -1/4 pO 2 dependence. Therefore, it is concluded that the n-type electronic conduction in the duplex material can be due to a small polaron-hopping between Ti 3+ and Ti 4+ . -- Graphical abstract: FE-SEM micrograph of a polished and thermal etched surface of a Ti-doped YTZP/Ti-doped YSZ composite material. Display Omitted Research highlights: → Ti-doped YTZP/Ti-doped YSZ composite materials are mixed conductors under low partial pressures. → From 5 mol% of TiO 2 , Y 2 (Ti 1-y ,Zr y ) 2 O 7 pyrochlore is

  19. Development of a novel zirconia dental post resistant to hydrothermal degradation

    International Nuclear Information System (INIS)

    Camposilvan, E; Marro, F G; Mestra, A; Anglada, M J

    2012-01-01

    Tetragonal Zirconia Polycrystals stabilized with 3% mol. content of yttria (3Y-TZP) has excellent properties in terms of strength and fracture toughness. These properties are mostly imputable to the transformation toughening mechanism, by which the doped metastable tetragonal phase of zirconia transforms to monoclinic under applied stress ahead of a crack. This phenomenon is accompanied by a volume expansion of 5%, and increases the resistance to crack growth, thus leading to higher toughness and strength. An important drawback of this material is represented by the Low Temperature Degradation (LTD or aging), which consists in the progressive tetragonal-to-monoclinic phase transformation by the influence of water. This work focuses on the improvement of 3Y-TZP aging behavior in order to develop a novel dental post, by means of the addition of ceria from the surface. This was achieved through the impregnation of the pre-sintered samples with a solution containing Cerium, followed by sintering. Various pre-sintering temperatures were studied in terms of microstructure, mechanical properties and aging resistance. The novel zirconia dental posts developed in this work are much more resistant to LTD as compared to the base material with no loss in mechanical properties.

  20. Langmuir-Blodgett films of alkane chalcogenice (S, Se, Te) stabilized gold nanoparticles

    DEFF Research Database (Denmark)

    Brust, M.; Stuhr-Hansen, N.; Norgaard, K.

    2001-01-01

    Gold nanoparticles stabilized by alkanethiolates, alkaneselenides, and alkanetellurides have been prepared by analogous methods. Chloroform solutions of thiolate and selenide stabilized particles were spread and evaporated on the water/air interface where the particles formed well-defined Langmuir...... films. The films were transferred to solid supports of freshly cleaved mica and were studied by atomic force microscopy (AFM). The particles were found to have an average core diameter of 2 nm. The stability of the particles under ambient conditions increased in the order Te

  1. Bulk and Interface Thermodynamics of Calcia-, and Yttria-doped Zirconia Ceramics: Nanograined Phase Stability

    Science.gov (United States)

    Drazin, John Walter

    while simultaneously collecting the energetic contribution of the adsorbing water vapor. With this data and apparatus, I have derived a 2nd order differential equation that relates the surface energy to the measured quantities such that I collected surfaces energies for over 35 specimens in the calcia-zirconia and yttria-zirconia systems for the first time. From the results, it was found that the monoclinic polymorph had the largest surface energy in the range of 1.9 - 2.1 ( J/m2) while the tetragonal surface energies were roughly 1.4 - 1.6 (J/m2), the cubic surface energies were roughly 0.8 - 1.0 (J/m2), and the amorphous surface energies were the smallest at roughly 0.7 - 0.8 (J/m 2). With the measured surface energy data, collected for the first time, we can create a nano-grain phase diagram similar to a bulk phase diagram that shows the stable polymorph as a function of dopant concentration and grain size using the bulk enthalpy data collected from high temperature oxide melt drop solution calorimetry. The phase diagrams show that pure zirconia will transform into tetragonal and cubic polymorphs from the monoclinic one at 7 and 5 nm respectively which confirms the experimental observations. The results are powerful predictive tools successfully applied in the nCZ and nYZ systems to a high degree of accuracy and adds a new development to conventional bulk phase diagrams. These diagrams should be the basis for nanotechnological efforts in nCZ and nYZ based systems, and suggest similar efforts are needed in other nano systems to pursue an in depth understanding and optimization of nanomaterials. After working on the theoretical aspects of phase stability, the focus of the research will shift to producing dense samples to measure observable quantities such as oxygen conduction and mechanical hardness. However, producing said samples with the nanocrystalline grain sizes has also been challenging as conventional sintering requires high temperatures which, as a consequence

  2. Development of novel zein-sodium caseinate nanoparticle (ZP)-stabilized emulsion films for improved water barrier properties via emulsion/solvent evaporation.

    Science.gov (United States)

    Wang, Li-Juan; Yin, Ye-Chong; Yin, Shou-Wei; Yang, Xiao-Quan; Shi, Wei-Jian; Tang, Chuan-He; Wang, Jin-Mei

    2013-11-20

    This work attempted to develop novel high barrier zein/SC nanoparticle (ZP)-stabilized emulsion films through microfluidic emulsification (ZPE films) or in combination with solvent (ethyl acetate) evaporation techniques (ZPE-EA films). Some physical properties, including tensile and optical properties, water vapor permeability (WVP), and surface hydrophobicity, as well as the microstructure of ZP-stabilized emulsion films were evaluated and compared with SC emulsion (SCE) films. The emulsion/solvent evaporation approach reduced lipid droplets of ZP-stabilized emulsions, and lipid droplets of ZP-stabilized emulsions were similar to or slightly lower than that of SC emulsions. However, ZP- and SC-stabilized emulsion films exhibited a completely different microstructure, nanoscalar lipid droplets were homogeneously distributed in the ZPE film matrix and interpenetrating protein-oil complex networks occurred within ZPE-EA films, whereas SCE films presented a heterogeneous microstructure. The different stabilization mechanisms against creaming or coalescence during film formation accounted for the preceding discrepancy of the microstructures between ZP-and SC-stabilized emulsion films. Interestingly, ZP-stabilized emulsion films exhibited a better water barrier efficiency, and the WVP values were only 40-50% of SCE films. A schematic representation for the formation of ZP-stabilized emulsion films was proposed to relate the physical performance of the films with their microstructure and to elucidate the possible forming mechanism of the films.

  3. [Influence of compaction pressure and pre-sintering temperature on the machinability of zirconia ceramic].

    Science.gov (United States)

    Huang, Huil; Li, Jing; Zhang, Fuqiang; Sun, Jing; Gao, Lian

    2011-10-01

    In order to make certain the compaction pressure as well as pre-sintering temperature on the machinability of the zirconia ceramic. 3 mol nano-size 3 mol yttria partially stabilized zirconia (3Y-TZP) powder were compacted at different isostatic pressure and sintered at different temperature. The cylindrical surface was traversed using a hard metal tool. Surface and edge quality were checked visually using light stereo microscopy. Pre-sintering temperature had the obviously influence on the machinability of 3Y-TZP. The cutting surface was smooth, and the integrality of edge was better when the pre-sintering temperature was chosen between 800 degrees C to 900 degrees C. Compaction pressure showed only a weak influence on machinability of 3Y-TZP blanks, but the higher compaction pressure result in the poor surface quality. The best machinability of pre-sintered zirconia body was found for 800-900 degrees C pre-sintering temperature, and 200-300 MPa compaction pressure.

  4. Grinding mechanism of zirconia toughened alumina

    International Nuclear Information System (INIS)

    Tsukuda, A.; Kondo, Y.; Yokota, K.

    1998-01-01

    In the grinding process, physical properties of ceramics affect both grinding mechanism and quality of ground surface. In this study we focused on fracture toughness of ceramics and the effect on grinding. A grinding test was carried out by single point grinding for ten different zirconia toughened alumina ceramics with different monoclinic zirconia contents. Effects of zirconia contents on the grinding mechanism and crack initiation were discussed. Copyright (1998) AD-TECH - International Foundation for the Advancement of Technology Ltd

  5. Effect of impregnation of La0.85Sr0.15MnO3/Yttria Stabilized Zirconia Solid Oxide Fuel Cell cathodes with La0.85Sr0.15MnO3 or Al2O3 nano-particles

    DEFF Research Database (Denmark)

    Kammer Hansen, Kent; Wandel, Marie; Liu, Yi-Lin

    2010-01-01

    Strontium substituted lanthanum manganite and yttria stabilized zirconia solid oxide fuel cell composite electrodes were impregnated with nano-particles of strontium substituted lanthanum manganite or alumina. A clear positive effect was observed on low performing electrodes and on good performing...

  6. Influence of surface treatment of yttria-stabilized tetragonal zirconia polycrystal with hot isostatic pressing on cyclic fatigue strength.

    Science.gov (United States)

    Iijima, Toshihiko; Homma, Shinya; Sekine, Hideshi; Sasaki, Hodaka; Yajima, Yasutomo; Yoshinari, Masao

    2013-01-01

    Hot isostatic pressing processed yttria-stabilized tetragonal zirconia polycrystal (HIP Y-TZP) has the potential for application to implants due to its high mechanical performance. The aim of this study was to investigate the influence of surface treatment of HIP Y-TZP on cyclic fatigue strength. HIP Y-TZP specimens were subjected to different surface treatments. Biaxial flexural strength was determined by both static and cyclic fatigue testing. In the cyclic fatigue test, the load was applied at a frequency of 10 Hz for 10(6) cycles in distilled water at 37°C. The surface morphology, roughness, and crystal phase of the surfaces were also evaluated. The cyclic fatigue strength (888 MPa) of HIP Y-TZP with sandblasting and acid-etching was more than twice that of Y-TZP as specified in ISO 13356 for surgical implants (320 MPa), indicating the clinical potential of this material.

  7. Evaluation of tensile strength and fracture toughness of yttria-stabilized zirconia polycrystals with fracture surface analysis

    International Nuclear Information System (INIS)

    Oishi, Manabu; Matsuda, Yukihisa; Noguchi, Kenichi; Masaki, Takaki

    1995-01-01

    The tensile strength of yttria-stabilized tetragonal zirconia polycrystals (Y-TZPs) was measured and the fracture surfaces were analyzed with the scanning electron microscope and X-ray microanalyzer. The fracture origins of the pressureless-sintered samples were voids or inclusions such as Al 2 O 3 , Al 2 O 3 with SiO 2 , and cubic-ZrO 2 , while the fracture origins of the hot isostatically pressed samples were inclusions; no voids were detected at fracture origins. The higher strengths of the hot isostatically pressed samples versus those of the pressureless-sintered samples were consistent with the change in fracture origins. The fracture toughness of the samples calculate from the tensile strength and analysis of the fracture origins was 3.4 to 3.7 MPa ·√m. These values are lower than those measured with the SEPB method. These discrepancies might be caused by the difference in the state of the fracture origin and its neighborhood, such as the size of the fracture origin and interaction between two surfaces in the precrack

  8. High temperature superconducting films by rf magnetron sputtering

    International Nuclear Information System (INIS)

    Kadin, A.M.; Ballentine, P.H.

    1989-01-01

    The authors have produced sputtered films of Y-Ba-Cu-O and Bi-Sr-Ca-Cu-O by rf magnetron sputtering from an oxide target consisting of loose reacted powder. The use of a large 8-inch stoichiometric target in the magnetron mode permits films located above the central region to be free of negative-ion resputtering effects, and hence yields reproducible, uniform stoichiometric compositions for a wide range of substrate temperatures. Superconducting YBCO films have been obtained either by sputtering at low temperatures followed by an 850 0 C oxygen anneal, or alternatively by depositing onto substrates heated to ∼600 - 650 0 C and cooling in oxygen. Films prepared by the former method on cubic zirconia substrate consist of randomly oriented crystallites with zero resistance above 83 K. Those deposited on zirconia at medium temperatures without the high-temperature anneal contain smooth partially oriented crystallites, with a slightly depressed T/sub c/ ∼75K. Finally, superconducting films have been deposited on MgO using a BiSrCaCu/sub 2/O/sub x/ powder target

  9. Thermal stability of pulsed laser deposited iridium oxide thin films at low oxygen atmosphere

    Science.gov (United States)

    Gong, Yansheng; Wang, Chuanbin; Shen, Qiang; Zhang, Lianmeng

    2013-11-01

    Iridium oxide (IrO2) thin films have been regarded as a leading candidate for bottom electrode and diffusion barrier of ferroelectric capacitors, some process related issues need to be considered before integrating ferroelectric capacitors into memory cells. This paper presents the thermal stability of pulsed laser deposited IrO2 thin films at low oxygen atmosphere. Emphasis was given on the effect of post-deposition annealing temperature at different oxygen pressure (PO2) on the crystal structure, surface morphology, electrical resistivity, carrier concentration and mobility of IrO2 thin films. The results showed that the thermal stability of IrO2 thin films was strongly dependent on the oxygen pressure and annealing temperature. IrO2 thin films can stably exist below 923 K at PO2 = 1 Pa, which had a higher stability than the previous reported results. The surface morphology of IrO2 thin films depended on PO2 and annealing temperature, showing a flat and uniform surface for the annealed films. Electrical properties were found to be sensitive to both the annealing temperature and oxygen pressure. The room-temperature resistivity of IrO2 thin films with a value of 49-58 μΩ cm increased with annealing temperature at PO2 = 1 Pa. The thermal stability of IrO2 thin films as a function of oxygen pressure and annealing temperature was almost consistent with thermodynamic calculation.

  10. Conformation of LSM/YSZ and LSM ceramic films obtained by the citrate and solid mixture techniques; Conformacao de filmes ceramicos de LSM e LSM/YSZ obtidos pelas tecnicas citratos e mistura de solidos

    Energy Technology Data Exchange (ETDEWEB)

    Chiba, R.; Vargas, R.A.; Andreoli, M.; Seo, E.S.M., E-mail: rchiba@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (CCTM/IPEN/CNEN-SP), Sao Paulo, SP (Brazil). Centro de Ciencia e Tecnologia de Materiais. Lab. de SOFC - Insumos e Componentes

    2009-07-01

    In this work, the ceramic films of LSM/YSZ (strontium-doped lanthanum manganite/Yttria-stabilized zirconia) and LSM used as cathodes of the solid oxide fuel cells (SOFC) are conformed by the wet powder spraying technique. The composite LSM/YSZ was obtained by the solid mixture technique and LSM by the citrate technique. For the formation of the LSM/YSZ and LSM ceramic films was necessary the preparation of dispersed ceramic suspensions for the deposition in YSZ substrate, used as electrolyte of the CaCOS. These powders were conformed using an aerograph for the deposition of the LSM/YSZ and LSM thin films of approximately 40 microns. The half-cells had been characterized by X-ray diffractometry (XRD), identifying the phases hexagonal (LSM) and cubica (YSZ). And electronic scanning electron microscopy (SEM) was used to evaluate the adherence and porosity of the ceramic films according to the characteristics of the cathode. (author)

  11. Porous La0.6Sr0.4CoO3-δ thin film cathodes for large area micro solid oxide fuel cell power generators

    DEFF Research Database (Denmark)

    Garbayo, A.; Esposito, Vincenzo; Sanna, Simone

    2014-01-01

    Porous La0.6Sr0.4CoO3-δ thin films were fabricated by pulsed laser deposition for being used as a cathode for micro solid oxide fuel cell applications as MEMS power generators. Symmetrical La0.6Sr0.4CoO3-δ/ yttria-stabilized zirconia/La0.6Sr0.4CoO3-δ free-standing membranes were fabricated using ...

  12. Morphology and thermal stability of Ti-doped copper nitride films

    International Nuclear Information System (INIS)

    Fan Xiaoyan; Wu Zhiguo; Li Huajun; Geng Baisong; Li Chun; Yan Pengxun

    2007-01-01

    A weakly Ti-doped copper nitride (Cu 3 N) film was prepared by cylindrical magnetron sputtering. The XPS results indicate that Ti atoms do not substitute for the Cu atoms but probably locate at the grain boundaries. The columnar grains size is about half of that of the undoped Cu 3 N film and the surface is smoother. For weakly Ti-doped Cu 3 N films, a dense layer appears on top of the columnar crystals. The RMS of the Cu film formed by annealing of the weakly Ti-doped Cu 3 N film is more than twice larger than that of the film before annealing. Compared with the undoped Cu 3 N film, it possesses fine thermal stability both in vacuum and in atmosphere

  13. Novel Cranial Implants of Yttria-Stabilized Zirconia as Acoustic Windows for Ultrasonic Brain Therapy.

    Science.gov (United States)

    Gutierrez, Mario I; Penilla, Elias H; Leija, Lorenzo; Vera, Arturo; Garay, Javier E; Aguilar, Guillermo

    2017-11-01

    Therapeutic ultrasound can induce changes in tissues by means of thermal and nonthermal effects. It is proposed for treatment of some brain pathologies such as Alzheimer's, Parkinson's, Huntington's diseases, and cancer. However, cranium highly absorbs ultrasound reducing transmission efficiency. There are clinical applications of transcranial focused ultrasound and implantable ultrasound transducers proposed to address this problem. In this paper, biocompatible materials are proposed for replacing part of the cranium (cranial implants) based on low porosity polycrystalline 8 mol% yttria-stabilized-zirconia (8YSZ) ceramics as acoustic windows for brain therapy. In order to assess the viability of 8YSZ implants to effectively transmit ultrasound, various 8YSZ ceramics with different porosity are tested; their acoustic properties are measured; and the results are validated using finite element models simulating wave propagation to brain tissue through 8YSZ windows. The ultrasound attenuation is found to be linearly dependent on ceramics' porosity. Results for the nearly pore-free case indicate that 8YSZ is highly effective in transmitting ultrasound, with overall maximum transmission efficiency of ≈81%, compared to near total absorption of cranial bone. These results suggest that 8YSZ polycrystals could be suitable acoustic windows for ultrasound brain therapy at 1 MHz. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  14. Synthesis and ceramic processing of zirconia alumina composites for application as solid oxide fuel cell electrolytes; Sintese e processamento de compositos de zirconia-alumina para aplicacao como eletrolito em celulas a combustivel de oxido solido

    Energy Technology Data Exchange (ETDEWEB)

    Garcia, Rafael Henrique Lazzari

    2007-07-01

    The global warmness and the necessity to obtain clean energy from alternative methods than petroleum raises the importance of developing cleaner and more efficient systems of energy generation, among then, the solid oxide fuel cell (SOFC). Cubic stabilized zirconia (CSZ) has been the most studied material as electrolyte in SOFC, due to its ionic conductivity and great stability at operation conditions. However, its low fracture toughness difficulties its application as a thin layer, what could lead to an improvement of cell efficiency. In this sense, the alumina addition in CSZ forms a composite, which can shift its mechanical properties, without compromising its electrical properties. In this work, coprecipitation synthesis route and ceramic processing of zirconia-alumina composites were studied, in order to establish optimum conditions to attain high density, homogeneous microstructure, and better mechanical properties than CSZ, without compromising ionic conductivity. For this purpose, composites containing up to 40 wt % of alumina, in a 9 mol % yttria-stabilized zirconia (9Y-CSZ) matrix were evaluated. In order to optimize the synthesis of the composites, a preliminary study of powder obtaining and processing were carried out, at compositions containing 20 wt % of alumina, in 9Y-CSZ. The ceramic powders were characterized by helium picnometry, X-ray diffraction, scanning electronic microscopy, transmission electronic microscopy, thermogravimetry, differential scanning calorimetry, granulometry by laser diffraction and gas adsorption (BET). The characterization of sinterized compacts were performed by X-ray diffraction, scanning electron microscopy, optical microscopy, density measurements, Vickers indentation and impedance spectroscopy. The obtained results show that the alumina addition, in the 9Y-CSZ matrix powders, raises the specific surface area, promotes deagglomeration of powders and elevates the oxides crystallization temperature, requiring higher

  15. Contrasting the beam interaction characteristics of selected lasers with a partially stabilized zirconia bio-ceramic

    International Nuclear Information System (INIS)

    Lawrence, J.

    2002-01-01

    Differences in the beam interaction characteristics of a CO 2 laser, a Nd:YAG laser, a high power diode laser (HPDL) and an excimer laser with a partially stabilized zirconia bio-ceramic have been studied. A derivative of Beer-Lambert's law was applied and the laser beam absorption lengths of the four lasers were calculated as 33.55x10 -3 cm for the CO 2 laser, 18.22x10 -3 cm for the Nd : YAG laser, 17.17x10 -3 cm for the HPDL and 8.41x10 -6 cm for the excimer laser. It was determined graphically that the fluence threshold values at which significant material removal was effected by the CO 2 laser, the Nd:YAG laser, the HPDL and the excimer laser were 52 J cm -2 , 97 J cm -2 , 115 J cm -2 and 0.48 J cm -2 , respectively. The thermal loading value for the CO 2 laser, the Nd : YAG laser, the HPDL and the excimer laser were calculated as being 1.55 kJ cm -3 , 5.32 kJ cm 3 , 6.69 kJ cm -3 and 57.04 kJ cm -3 , respectively. (author)

  16. In-plane aligned YBCO film on textured YSZ buffer layer deposited on NiCr alloy tape by laser ablation with only O+ ion beam assistance

    International Nuclear Information System (INIS)

    Xin Tang Huang

    2000-01-01

    High critical current density and in-plane aligned YBa 2 Cu 3 O 7-x (YBCO) film on a textured yttria-stabilized zirconia (YSZ) buffer layer deposited on NiCr alloy (Hastelloy c-275) tape by laser ablation with only O + ion beam assistance was fabricated. The values of the x-ray phi-scan full width at half-maximum (FWHM) for YSZ(202) and YBCO(103) are 18 deg. and 11 deg., respectively. The critical current density of YBCO film is 7.9 x 105 A cm -2 at liquid nitrogen temperature and zero field, and its critical temperature is 90 K. (author)

  17. Microstructure and surface morphology of YSZ thin films deposited by e-beam technique

    International Nuclear Information System (INIS)

    Laukaitis, G.; Dudonis, J.; Milcius, D.

    2008-01-01

    In present study yttrium-stabilized zirconia (YSZ) thin films were deposited on optical quartz (amorphous SiO 2 ), porous Ni-YSZ and crystalline Alloy 600 (Fe-Ni-Cr) substrates using e-beam deposition technique and controlling technological parameters: substrate temperature and electron gun power which influence thin-film deposition mechanism. X-ray diffraction, scanning electron microscopy (SEM), and atomic force microscopy (AFM) were used to investigate how thin-film structure and surface morphology depend on these parameters. It was found that the crystallite size, roughness and growth mechanism of YSZ thin films are influenced by electron gun power. To clarify the experimental results, YSZ thin-film formation as well evolution of surface roughness at its initial growing stages were analyzed. The evolution of surface roughness could be explained by the processes of surface mobility of adatoms and coalescence of islands. The analysis of these experimental results explain that surface roughness dependence on substrate temperature and electron gun power non-monotonous which could result from diffusivity of adatoms and the amount of atomic clusters in the gas stream of evaporated material

  18. Stability and instability of axisymmetric droplets in thermocapillary-driven thin films

    Science.gov (United States)

    Nicolaou, Zachary G.

    2018-03-01

    The stability of compactly supported, axisymmetric droplet states is considered for driven thin viscous films evolving on two-dimensional surfaces. Stability is assessed using Lyapunov energy methods afforded by the Cahn-Hilliard variational form of the governing equation. For general driving forces, a criterion on the gradient of profiles at the boundary of their support (their contact slope) is shown to be a necessary condition for stability. Additional necessary and sufficient conditions for stability are established for a specific driving force corresponding to a thermocapillary-driven film. It is found that only droplets of sufficiently short height that satisfy the contact slope criterion are stable. This destabilization of droplets with increasing height is characterized as a saddle-node bifurcation between a branch of tall, unstable droplets and a branch of short, stable droplets.

  19. Temperature dependence of bending strength for plasma sprayed zirconia coating; Plasuma yosha zirconia himaku no magetsuyosa no ondo izonsei

    Energy Technology Data Exchange (ETDEWEB)

    Arai, M.; Sakuma, T. [Central Research Inst. of Electric Power Industry, Tokyo (Japan)] Mizutani, T. [Tokyo Inst. of Tech. (Japan)] Kishimoto, K. [Tokyo Inst. of Tech. (Japan). Faculty of Engineering] Saito, M. [Toshiba Corp. (Japan). Heavy Apparatus Engineering Lab.

    1998-02-01

    Plasma sprayed zirconia applying to the thermal barrier coating in gas turbine has been developing for protecting the hot parts such as blades and nozzles from high-temperature enviroments. In this paper, four point bending tests under various temperature conditions are conducted on plasma sprayed zirconia and its mechanical properties are examined. Results show that the bending strength at room temperature for plasma sprayed zirconia is much lower than that of sintered zirconia and is decreased with the increase in temperature. However, Weibull modulus at each temperature is relatively large and the dispersion of bending strength is very small in comparison with that of sintered zirconia. It is also clarified by the SEM observations of fracture surface that many defects such as debonding and microcrack are responsible for the lower bending strength. 9 refs., 8 figs., 1 tab.

  20. Orientation control and domain structure analysis of {100}-oriented epitaxial ferroelectric orthorhombic HfO{sub 2}-based thin films

    Energy Technology Data Exchange (ETDEWEB)

    Katayama, Kiliha [Department of Innovative and Engineered Materials, Tokyo Institute of Technology, 4259 Nagatsuta, Midori-ku, Yokohama 226-8502 (Japan); Shimizu, Takao [Materials Research Center for Element Strategy, Tokyo Institute of Technology, 4259 Nagatsuta, Midori-ku, Yokohama 226-8503 (Japan); Sakata, Osami [Synchrotron X-ray Station at SPring-8, National Institute for Materials Science (NIMS), 1-1-1 Kouto, Sayo-cho, Sayo-gun, Hyogo 679-5148 (Japan); Shiraishi, Takahisa; Nakamura, Shogo; Kiguchi, Takanori; Akama, Akihiro; Konno, Toyohiko J. [Institute for Materials Research, Tohoku University, 2-1-1 Katahira, Aoba-ku, Sendai 980-8577 (Japan); Uchida, Hiroshi [Department of Materials and Life Sciences, Sophia University, Chiyoda, Tokyo 102-8554 (Japan); Funakubo, Hiroshi, E-mail: funakubo.h.aa@m.titech.ac.jp [Department of Innovative and Engineered Materials, Tokyo Institute of Technology, 4259 Nagatsuta, Midori-ku, Yokohama 226-8502 (Japan); Materials Research Center for Element Strategy, Tokyo Institute of Technology, 4259 Nagatsuta, Midori-ku, Yokohama 226-8503 (Japan)

    2016-04-07

    Orientation control of {100}-oriented epitaxial orthorhombic 0.07YO{sub 1.5}-0.93HfO{sub 2} films grown by pulsed laser deposition was investigated. To achieve in-plane lattice matching, indium tin oxide (ITO) and yttria-stabilized zirconia (YSZ) were selected as underlying layers. We obtained (100)- and (001)/(010)-oriented films on ITO and YSZ, respectively. Ferroelastic domain formation was confirmed for both films by X-ray diffraction using the superlattice diffraction that appeared only for the orthorhombic symmetry. The formation of ferroelastic domains is believed to be induced by the tetragonal–orthorhombic phase transition upon cooling the films after deposition. The present results demonstrate that the orientation of HfO{sub 2}-based ferroelectric films can be controlled in the same manner as that of ferroelectric films composed of conventional perovskite-type material such as Pb(Zr, Ti)O{sub 3} and BiFeO{sub 3}.

  1. Studies of alumina additions in zirconia - magnesia

    International Nuclear Information System (INIS)

    Muccillo, R.

    1987-01-01

    Ionic conductivity measurements have been carried out in the 500 0 C - 1000 0 C temperature range in Mg - PSZ (Partially Stabilized Zirconia) with 0.5 to 10 mol % alumina additions. All specimens were prepared by pressing followed by pre - and sintering at 1000 0 C/2h and1450 0 C/4h, respectively. Thermal histerysis of the ionic conductivity have been detected, probably due to phase changes in the Mg-PSZ samples. The results show that alumina additions up to 2.1% enhances densification with no major variations in electrical resistivity values. (Author) [pt

  2. Collagen films with stabilized liquid crystalline phases and concerns on osteoblast behaviors

    Energy Technology Data Exchange (ETDEWEB)

    Tang, Minjian; Ding, Shan; Min, Xiang; Jiao, Yanpeng, E-mail: tjiaoyp@jnu.edu.cn; Li, Lihua; Li, Hong; Zhou, Changren, E-mail: tcrz9@jnu.edu.cn

    2016-01-01

    To duplicate collagen's in vivo liquid crystalline (LC) phase and investigate the relationship between the morphology of LC collagen and osteoblast behavior, a self-assembly method was introduced for preparing collagen films with a stabilized LC phase. The LC texture and topological structure of the films before and after stabilization were observed with polarizing optical microscopy, scanning electron microscopy (SEM), and atomic force microscopy (AFM). The relationship between the collagen films and osteoblast behavior was studied with the 3-(4,5)-dimethylthiahiazo(-z-y1)-3,5-di-phenytetrazoliumromide method, proliferation index detection, alkaline phosphatase measurements, osteocalcin assay, inverted microscopy, SEM observation, AFM observation, and cytoskeleton fluorescence staining. The results showed that the LC collagen film had continuously twisting orientations in the cholesteric phase with a typical series of arced patterns. The collagen fibers assembled in a well-organized orientation in the LC film. Compared to the non-LC film, the LC collagen film can promote cell proliferation, and increase ALP and osteocalcin expression, revealing a contact guide effect on osteoblasts. - Highlights: • Collagen film with liquid crystalline (LC) phase was observed by POM, SEM and AFM. • The effect of LC collagen film on osteoblasts behaviors was studied in detail. • LC collagen film promoted osteoblast proliferation and osteogenesis activity.

  3. Shear bond strength of veneering porcelain to zirconia: Effect of surface treatment by CNC-milling and composite layer deposition on zirconia.

    Science.gov (United States)

    Santos, R L P; Silva, F S; Nascimento, R M; Souza, J C M; Motta, F V; Carvalho, O; Henriques, B

    2016-07-01

    The purpose of this study was to evaluate the shear bond strength of veneering feldspathic porcelain to zirconia substrates modified by CNC-milling process or by coating zirconia with a composite interlayer. Four types of zirconia-porcelain interface configurations were tested: RZ - porcelain bonded to rough zirconia substrate (n=16); PZ - porcelain bonded to zirconia substrate with surface holes (n=16); RZI - application of a composite interlayer between the veneering porcelain and the rough zirconia substrate (n=16); PZI - application of a composite interlayer between the porcelain and the zirconia substrate treated by CNC-milling (n=16). The composite interlayer was composed of zirconia particles reinforced porcelain (30%, vol%). The mechanical properties of the ceramic composite have been determined. The shear bond strength test was performed at 0.5mm/min using a universal testing machine. The interfaces of fractured and untested specimens were examined by FEG-SEM/EDS. Data was analyzed with Shapiro-Wilk test to test the assumption of normality. The one-way ANOVA followed by Tukey HSD multiple comparison test was used to compare shear bond strength results (α=0.05). The shear bond strength of PZ (100±15MPa) and RZI (96±11MPa) specimens were higher than that recorded for RZ (control group) specimens (89±15MPa), although not significantly (p>0.05). The highest shear bond strength values were recorded for PZI specimens (138±19MPa), yielding a significant improvement of 55% relative to RZ specimens (p<0.05). This study shows that it is possible to highly enhance the zirconia-porcelain bond strength - even by ~55% - by combining surface holes in zirconia frameworks and the application of a proper ceramic composite interlayer. Copyright © 2016 Elsevier Ltd. All rights reserved.

  4. Properties of zirconium ceramics and film stabilized by yttrium

    International Nuclear Information System (INIS)

    Korobova, N.

    2004-01-01

    Full text: Unstable zirconium dioxide phase transformation can be eliminated by stabilization of the cubic phase with an addition of a selected alkaline earth or rare-earth oxide. Stabilized ZrO 2 has been widely utilized in various high-temperature refractory applications. These stabilized ZrO 2 -base solid solutions also possess rather unique electrical properties, and as a result have considerable potential as solid electrolytes in galvanic and fuel cells and, possibly, as heating elements in high-temperature furnaces. The complex study of synthesis processes, structure and properties of metal alkoxide organic sols have been developed. These have allowed to create main principles of their formation and to show the practical realization of obtained theoretical and experimental results. The correlation between hydrolysis conditions of (Zr+Y) metal alkoxide sols and synthesis of stable colloid multi-component systems has been established. Systematic research of zirconium and yttrium bi-alkoxide electrophoretic deposition was conducted for the first time. The formation mechanism of electrophoretic deposits has been offered and general scientific principles of the electrophoretic process have been formulated. The model of gel deposits structure was proposed. It has enabled to analyze the main (for example, cluster) effects, which have been exhibited in technological procedure for thin film preparation. The structure investigation of stabilized zirconium dioxide thin films and ceramics has been studied. The researches were based on the comparative analysis of the initial gel microstructure and dried gel by the various drying methods. The new approach for drying of gel electrophoretic deposits was formulated theoretically and experimentally has been proved. The modeling of the aggregate kinetics as a type of 'cluster-cluster' has been proposed like a qualitative description of the process. The data of fractal dimensions of aggregates which have been formed at the

  5. Real-time kinetic modeling of YSZ thin film roughness deposited by e-beam evaporation technique

    International Nuclear Information System (INIS)

    Galdikas, A.; Cerapaite-Trusinskiene, R.; Laukaitis, G.; Dudonis, J.

    2008-01-01

    In the present study, the process of yttrium-stabilized zirconia (YSZ) thin films deposition on optical quartz (SiO 2 ) substrates using e-beam deposition technique controlling electron gun power is analyzed. It was found that electron gun power influences the non-monotonous kinetics of YSZ film surface roughness. The evolution of YSZ thin film surface roughness was analyzed by a kinetic model. The model is based on the rate equations and includes processes of surface diffusion of the adatoms and the clusters, nucleation, growth and coalescence of islands in the case of thin film growth in Volmer-Weber mode. The analysis of the experimental results done by modeling explains non-monotonous kinetics and dependence of the surface roughness on the electron gun power. A good quantitative agreement with experimental results is obtained taking into account the initial roughness of the substrate surface and the amount of the clusters in the flux of evaporated material.

  6. Stability of J-aggregated species in an indocarbocyanine dye in Langmuir–Blodgett Films

    Energy Technology Data Exchange (ETDEWEB)

    Debnath, Pintu [Thin film and Nanoscience Laboratory, Department of Physics, Tripura University, Suryamaninagar 799022, Tripura (India); Chakraborty, Santanu [Department of Physics, NIT Agartala, Jiraniya 799046, Tripura (India); Deb, Subrata [Department of Physics, Women' s College, Agartala 799001, Tripura (India); Nath, Jayasree [Department of Chemistry, Tripura University, Suryamaninagar 799022, Tripura (India); Dey, Bapi; Bhattacharjee, D. [Thin film and Nanoscience Laboratory, Department of Physics, Tripura University, Suryamaninagar 799022, Tripura (India); Hussain, Syed Arshad, E-mail: sa_h153@hotmail.com [Thin film and Nanoscience Laboratory, Department of Physics, Tripura University, Suryamaninagar 799022, Tripura (India)

    2016-11-15

    Here, the stability behaviour of J-aggregate of an indocarbocyanine dye 1,1′-Dioctadecyl-3,3,3′,3′-Tetramethylindocarbocynine perchlorate (DiI) in fatty acid mixed (X{sub DiI}=0.4) Langmuir–Blodgett (LB) films under different condition was reported. Surface pressure–area per molecule (π–A) isotherm measurement suggest that the molecular interaction between the constituent molecules changes with subphase temperature. UV–vis absorption and fluorescence spectroscopy and Atomic Force Microscopy (AFM) were used to study the stability behaviour. It has been observed that prominent J-aggregate of DiI occurred in the mixed films at subphase temperature 15 °C. With the passage of time as well as post heat treatment DiI J-aggregate decayed to excimer in both mono- and multilayer LB films. Total transition from J-aggregate to excimer occurred in monolayer films, whereas, the transition was partial in multilayer films. The stability of DiI J-aggregate in monolayer films was increased by two ways – (i) depositing the DiI-SA mixed LB films at higher surface pressure, (ii) exposing the films at 50 °C for 5 min. It has been observed that after heat treatment the DiI J-aggregate remained almost stable even after 200 days. AFM investigations gave the compelling visual evidences of the same.

  7. Novel carboxymethyl cellulose-polyvinyl alcohol blend films stabilized by Pickering emulsion incorporation method.

    Science.gov (United States)

    Fasihi, Hadi; Fazilati, Mohammad; Hashemi, Mahdi; Noshirvani, Nooshin

    2017-07-01

    The aim of this study was to investigate the possibility of increasing the antimicrobial and antioxidant properties of biodegradable active films stabilized via Pickering emulsions. The blend films were prepared from carboxymethyl cellulose (CMC) and polyvinyl alcohol (PVA), emulsified with oleic acid (OL) and incorporated with rosemary essential oil (REO). Formation of Pickering emulsion was confirmed by scanning electron microscopy (SEM), optical microscopy, mean droplet size and emulsion stability. Morphological, optical, physical, mechanical, thermal, antifungal and antioxidant properties of the films incorporated with different concentrations of REO (0.5, 1.5 and 3%) were determined. The results showed an increase in UV absorbance and elongation at break but, a decrease in tensile strength and thermal stability of the films. Interestingly, films containing REO exhibited considerable antioxidant and antimicrobial properties. In vitro microbial tests exhibited 100% fungal inhibition against Penicillium digitatum in the films containing 3% REO. In addition, no fungal growth were observed after 60days of storage at 25°C in bread slices were stored with active films incorporated with 3% REO, could attributed to the slow and regular release of REO caused by Pickering emulsions. The results of this study suggest that Pickering emulsion is a very promising method, which significantly affects antioxidant and antimicrobial activities of the films. Copyright © 2017 Elsevier Ltd. All rights reserved.

  8. Fabrication of porous zirconia using filter paper template

    International Nuclear Information System (INIS)

    Deng Yuhua; Wei Pan

    2005-01-01

    In this work, porous zirconia ceramic was synthesized using filter papers as a template. Special attention is paid to whether the structural of the filter paper can be transferred to the zirconia structure. Microstructure of so synthesized porous zirconia was observed with SEM and the phase was determined by XRD. The surface area and the pore were investigated with an automatic volumetric sorption analyzer. It has been found that the morphology of the template transmit to the porous zirconia quite well. (orig.)

  9. Penetration and characteristics of an intergranular-liquid phase during sintering of CaSi2O5-dropped 8 mol%-yttria-stabilized zirconia estimation by impedance spectroscopy

    International Nuclear Information System (INIS)

    Jung, Young-Soo; Choi, Jung-Hae; Lee, Jong-Heun

    2004-01-01

    The grain-boundary resistivity of CaSi 2 O 5 -dropped 8 mol%-yttria-stabilized zirconia (8YSZ) was determined by impedance spectroscopy using sub-millimeter-scale electrodes. During sintering, a liquid that formed at the top surface of the specimen penetrated into the 8YSZ and induced enhanced grain growth near the surface region. The grain-boundary resistivity of the specimen surface was observed to be 150 times higher than that of the interior. The deterioration of the grain-boundary conductivity was explained in terms of the presence of an intergranular siliceous phase

  10. Novel polypyrrole films with excellent crystallinity and good thermal stability

    International Nuclear Information System (INIS)

    Jeeju, Pullarkat P.; Varma, Sreekanth J.; Francis Xavier, Puthampadath A.; Sajimol, Augustine M.; Jayalekshmi, Sankaran

    2012-01-01

    Polypyrrole has drawn a lot of interest due to its high thermal and environmental stability in addition to high electrical conductivity. The present work highlights the enhanced crystallinity of polypyrrole films prepared from the redoped sample solution. Initially hydrochloric acid doped polypyrrole was prepared by chemical oxidative polymerization of pyrrole using ammonium peroxidisulphate as oxidant. The doped polypyrrole was dedoped using ammonia solution and then redoped with camphor sulphonic acid. Films were coated on ultrasonically cleaned glass substrates from the redoped sample solution in meta-cresol. The enhanced crystallinity of the polypyrrole films has been established from X-ray diffraction (XRD) studies. The room temperature electrical conductivity of the redoped polypyrrole film is about 30 times higher than that of the hydrochloric acid doped pellet sample. The results of Raman spectroscopy, Differential scanning calorimetry (DSC) and Thermogravimetric analysis (TGA) of the samples support the enhancement in crystallinity. Percentage crystallinity of the samples is estimated from XRD and DSC data. The present work is significant, since crystallinity of films is an important parameter for selecting polymers for specific applications. - Highlights: ► Polypyrrole films redoped with CSA have been prepared from meta-cresol solution. ► The solution casted films exhibit semi-crystallinity and good thermal stability. ► Percentage crystallinity estimated using XRD and DSC analysis is about 65%. ► Raman studies support the enhancement in crystallinity based on XRD and DSC data. ► The conductivity of the film is 30 times higher than that of HCl doped sample.

  11. Novel polypyrrole films with excellent crystallinity and good thermal stability

    Energy Technology Data Exchange (ETDEWEB)

    Jeeju, Pullarkat P., E-mail: jeejupp@gmail.com [Division for Research in Advanced Materials, Department of Physics, Cochin University of Science and Technology, Cochin-22, Kerala (India); Varma, Sreekanth J.; Francis Xavier, Puthampadath A.; Sajimol, Augustine M. [Division for Research in Advanced Materials, Department of Physics, Cochin University of Science and Technology, Cochin-22, Kerala (India); Jayalekshmi, Sankaran, E-mail: jayalekshmi@cusat.ac.in [Division for Research in Advanced Materials, Department of Physics, Cochin University of Science and Technology, Cochin-22, Kerala (India)

    2012-06-15

    Polypyrrole has drawn a lot of interest due to its high thermal and environmental stability in addition to high electrical conductivity. The present work highlights the enhanced crystallinity of polypyrrole films prepared from the redoped sample solution. Initially hydrochloric acid doped polypyrrole was prepared by chemical oxidative polymerization of pyrrole using ammonium peroxidisulphate as oxidant. The doped polypyrrole was dedoped using ammonia solution and then redoped with camphor sulphonic acid. Films were coated on ultrasonically cleaned glass substrates from the redoped sample solution in meta-cresol. The enhanced crystallinity of the polypyrrole films has been established from X-ray diffraction (XRD) studies. The room temperature electrical conductivity of the redoped polypyrrole film is about 30 times higher than that of the hydrochloric acid doped pellet sample. The results of Raman spectroscopy, Differential scanning calorimetry (DSC) and Thermogravimetric analysis (TGA) of the samples support the enhancement in crystallinity. Percentage crystallinity of the samples is estimated from XRD and DSC data. The present work is significant, since crystallinity of films is an important parameter for selecting polymers for specific applications. - Highlights: Black-Right-Pointing-Pointer Polypyrrole films redoped with CSA have been prepared from meta-cresol solution. Black-Right-Pointing-Pointer The solution casted films exhibit semi-crystallinity and good thermal stability. Black-Right-Pointing-Pointer Percentage crystallinity estimated using XRD and DSC analysis is about 65%. Black-Right-Pointing-Pointer Raman studies support the enhancement in crystallinity based on XRD and DSC data. Black-Right-Pointing-Pointer The conductivity of the film is 30 times higher than that of HCl doped sample.

  12. Shear Bond Strengths between Three Different Yttria-Stabilized Zirconia Dental Materials and Veneering Ceramic and Their Susceptibility to Autoclave Induced Low-Temperature Degradation

    Directory of Open Access Journals (Sweden)

    Manoti Sehgal

    2016-01-01

    Full Text Available A study was undertaken to evaluate the effect of artificial aging through steam and thermal treatment as influencing the shear bond strength between three different commercially available zirconia core materials, namely, Upcera, Ziecon, and Cercon, layered with VITA VM9 veneering ceramic using Universal Testing Machine. The mode of failure between zirconia and ceramic was further analyzed as adhesive, cohesive, or mixed using stereomicroscope. X-ray diffraction and SEM (scanning electron microscope analysis were done to estimate the phase transformation (m-phase fraction and surface grain size of zirconia particles, respectively. The purpose of this study was to simulate the clinical environment by artificial aging through steam and thermal treatment so as the clinical function and nature of the bond between zirconia and veneering material as in a clinical trial of 15 years could be evaluated.

  13. The Impact of Plasma Treatment of Cercon® Zirconia Ceramics on Adhesion to Resin Composite Cements and Surface Properties.

    Science.gov (United States)

    Tabari, Kasra; Hosseinpour, Sepanta; Mohammad-Rahimi, Hossein

    2017-01-01

    Introduction: In recent years, the use of ceramic base zirconia is considered in dentistry for all ceramic restorations because of its chemical stability, biocompatibility, and good compressive as well as flexural strength. However, due to its chemical stability, there is a challenge with dental bonding. Several studies have been done to improve zirconia bonding but they are not reliable. The purpose of this research is to study the effect of plasma treatment on bonding strength of zirconia. Methods: In this in vitro study, 180 zirconia discs' (thickness was 0.85-0.9 mm) surfaces were processed with plasma of oxygen, argon, air and oxygen-argon combination with 90-10 and 80-20 ratio (n=30 for each group) after being polished by sandblast. Surface modifications were assessed by measuring the contact angle, surface roughness, and topographical evaluations. Cylindrical Panavia f2 resin-cement and Diafill were used for microshear strength bond measurements. The data analysis was performed by SPSS 20.0 software and one-way analysis of variance (ANOVA) and Tukey test as the post hoc. Results: Plasma treatment in all groups significantly reduces contact angle compare with control ( P =0.001). Topographic evaluations revealed coarseness promotion occurred in all plasma treated groups which was significant when compared to control ( P <0.05), except argon plasma treated group that significantly decreased surface roughness ( P <0.05). In all treated groups, microshear bond strength increased, except oxygen treated plasma group which decreased this strength. Air and argon-oxygen combination (both groups) significantly increased microshear bond strength ( P <0.05). Conclusion: According to this research, plasmatic processing with dielectric barrier method in atmospheric pressure can increase zirconia bonding strength.

  14. Synthesis and ceramic processing of zirconia alumina composites for application as solid oxide fuel cell electrolytes

    International Nuclear Information System (INIS)

    Garcia, Rafael Henrique Lazzari

    2007-01-01

    The global warmness and the necessity to obtain clean energy from alternative methods than petroleum raises the importance of developing cleaner and more efficient systems of energy generation, among then, the solid oxide fuel cell (SOFC). Cubic stabilized zirconia (CSZ) has been the most studied material as electrolyte in SOFC, due to its ionic conductivity and great stability at operation conditions. However, its low fracture toughness difficulties its application as a thin layer, what could lead to an improvement of cell efficiency. In this sense, the alumina addition in CSZ forms a composite, which can shift its mechanical properties, without compromising its electrical properties. In this work, coprecipitation synthesis route and ceramic processing of zirconia-alumina composites were studied, in order to establish optimum conditions to attain high density, homogeneous microstructure, and better mechanical properties than CSZ, without compromising ionic conductivity. For this purpose, composites containing up to 40 wt % of alumina, in a 9 mol % yttria-stabilized zirconia (9Y-CSZ) matrix were evaluated. In order to optimize the synthesis of the composites, a preliminary study of powder obtaining and processing were carried out, at compositions containing 20 wt % of alumina, in 9Y-CSZ. The ceramic powders were characterized by helium picnometry, X-ray diffraction, scanning electronic microscopy, transmission electronic microscopy, thermogravimetry, differential scanning calorimetry, granulometry by laser diffraction and gas adsorption (BET). The characterization of sinterized compacts were performed by X-ray diffraction, scanning electron microscopy, optical microscopy, density measurements, Vickers indentation and impedance spectroscopy. The obtained results show that the alumina addition, in the 9Y-CSZ matrix powders, raises the specific surface area, promotes deagglomeration of powders and elevates the oxides crystallization temperature, requiring higher

  15. Synthesis, characterization and thermal stability of solid solutions Zr (Y, Fe, MoO2

    Directory of Open Access Journals (Sweden)

    Felipe Legorreta-García

    2015-05-01

    Full Text Available The synthesis of Fe3+, Mo4+ and Y3+ fully stabilized zirconia by the nitrate/urea combustion route and thermal stability in air was investigated. The solid solution obtained was characterized by X ray diffraction (XRD, scanning electron microscopy (SEM and used the BET method for determining specific surface. The ceramic powders obtained were calcined at 1473 K in air atmosphere in order to determine their thermal stability. The scanning electron microscopy (SEM results showed a homogeneous grain surface, measuring several tens of micrometers across. The crystallographic study revealed that by this method it was successfully achieved zirconia doped with Fe3+, Mo4+ and Y3+ ions in the zirconia tetragonal monophase, even after calcinations.

  16. Effect of Three Different Core Materials on Masking Ability of a Zirconia Ceramic

    Directory of Open Access Journals (Sweden)

    Farhad Tabatabaian

    2016-12-01

    Full Text Available Objectives: Masking ability of a restorative material plays a role in hiding colored substructures; however, the masking ability of zirconia ceramic (ZRC has not yet been clearly understood in zirconia-based restorations. This study evaluated the effect of three different core materials on masking ability of a ZRC.Materials and Methods: Ten zirconia disc samples, 0.5mm in thickness and 10mm in diameter, were fabricated. A white (W substrate (control and three substrates of nickel-chromium alloy (NCA, non-precious gold alloy (NPGA, and ZRC were prepared. The zirconia discs were placed on the four types of substrates for spectrophotometry. The L*, a*, and b* values of the specimens were measured by a spectrophotometer and color change (ΔE values were calculated to determine color differences between the test and control groups and were then compared with the perceptual threshold. Randomized block ANOVA and Bonferroni test analyzed the data. A significance level of 0.05 was considered.Results: The mean and standard deviation values of ΔE for NCA, NPGA, and ZRC groups were 10.26±2.43, 9.45±1.74, and 6.70±1.91 units, respectively. Significant differences were found in the ΔE values between ZRC and the other two experimental groups (NCA and NPGA; P<0.0001 and P=0.001, respectively. The ΔE values for the groups were more than the predetermined perceptual threshold.Conclusions: Within the limitations of this study, it was concluded that the tested ZRC could not well mask the examined core materials.Keywords: Color; Spectrophotometry; Visual Perception; Yttria Stabilized Tetragonal Zirconia

  17. Thermal stability of diamond-like carbon–MoS{sub 2} thin films in different environments

    Energy Technology Data Exchange (ETDEWEB)

    Niakan, H., E-mail: hamid.niakan@usask.ca [Department of Mechanical Engineering, University of Saskatchewan, 57 Campus Drive, Saskatoon, SK S7N 5A9 (Canada); Zhang, C. [Department of Mechanical Engineering, University of Saskatchewan, 57 Campus Drive, Saskatoon, SK S7N 5A9 (Canada); Hu, Y. [Canadian Light Source, 101 Perimeter Road, Saskatoon, SK S7N 0X4 (Canada); Szpunar, J.A.; Yang, Q. [Department of Mechanical Engineering, University of Saskatchewan, 57 Campus Drive, Saskatoon, SK S7N 5A9 (Canada)

    2014-07-01

    Diamond-like carbon (DLC) based coatings are ideal for low friction and wear resistant applications. For those tribological applications, the coatings may expose to high temperature environments. Therefore, the thermal stability of the coating is very important for its long-term performance. In this work, DLC–MoS{sub 2} composite thin films were synthesized using biased target ion beam deposition technique in which MoS{sub 2} was produced by sputtering a MoS{sub 2} target using Ar ion beams while DLC was deposited by an ion source with CH{sub 4} gas as carbon source. DLC films without MoS{sub 2} deposited under similar conditions were used as reference samples. After the deposition, DLC and DLC–MoS{sub 2} thin films were heat-treated in ambient air and low pressure environments at different temperatures ranging from 100 to 600 °C for 2 h. The effect of annealing on the structure, mechanical and tribological properties of the resulting films were studied by means of Raman spectroscopy, X-ray absorption near edge structure, scanning electron microscopy, nanoindentation, and ball-on-disk testing. The results showed that the structure, hardness, Young's modulus, friction coefficient and wear coefficient of the DLC films were stable up to 200 °C annealing in air and 300 °C in low pressure. At higher temperature, the annealing led to the transformation of sp{sup 3} to sp{sup 2}, which degraded the mechanical and tribological properties of the thin films. Comparing with the DLC films, the DLC–MoS{sub 2} thin films showed a slower rate of graphitization and higher structure stability throughout the range of annealing temperatures, indicating a relatively higher thermal stability. - Highlights: • Thermal stability of diamond-like carbon (DLC) and DLC–MoS{sub 2} films were evaluated. • DLC–MoS{sub 2} films can be synthesized by biased target ion beam deposition technique. • Comparing with DLC films, the DLC–MoS{sub 2} thin films showed higher

  18. Epitaxial YBa2Cu3O7 films on rolled-textured metals for high temperature superconducting applications

    International Nuclear Information System (INIS)

    Norton, D.P.; Park, C.; Prouteau, C.

    1998-04-01

    The epitaxial growth of high temperature superconducting (HTS) films on rolled-textured metal represents a viable approach for long-length superconducting tapes. Epitaxial, 0.5 microm thick YBa 2 Cu 3 O 7 (YBCO) films with critical current densities, J c , greater than 1 MA/cm 2 have been realized on rolled-textured (001) Ni tapes with yttria-stabilized zirconia (YSZ)/CeO 2 oxide buffer layers. This paper describes the synthesis using pulsed-laser deposition (PLD) of epitaxial oxide buffer layers on biaxially-textured metal that comprise the so-called rolling-assisted biaxially-textured substrates (RABiTs trademark). The properties of the buffer and YBa 2 Cu 3 O 7 films on rolled-textured Ni are discussed, with emphasis given to the crystallographic and microstructural properties that determine the superconducting properties of these multilayer structures

  19. Development of high temperature and pressure zirconia-based pH sensors

    International Nuclear Information System (INIS)

    Danielson, M.J.; Koski, O.H.; Myers, J.

    1985-01-01

    Yttria-stabilized zirconia pH sensors are suitable for use from 100-300 0 C. A new Pt internal half cell is discussed which results in a considerable simplification in their calibration. A degradation process takes place after prolonged exposure to 300 0 C conditions and is manifested by a loss of full Nerstian response at temperature ≤ 200 0 C. A hypothesis for the degradation process is discussed

  20. The film thickness dependent thermal stability of Al{sub 2}O{sub 3}:Ag thin films as high-temperature solar selective absorbers

    Energy Technology Data Exchange (ETDEWEB)

    Xiao Xiudi; Xu Gang, E-mail: xiudixiao@163.com; Xiong Bin; Chen Deming; Miao Lei [Chinese Academy of Sciences, Key Laboratory of Renewable Energy and Gas Hydrates, Guangzhou Institute of Energy Conversion (China)

    2012-03-15

    The monolayer Al{sub 2}O{sub 3}:Ag thin films were prepared by magnetron sputtering. The microstructure and optical properties of thin film after annealing at 700 Degree-Sign C in air were characterized by transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and spectrophotometer. It revealed that the particle shape, size, and distribution across the film were greatly changed before and after annealing. The surface plasmon resonance absorption and thermal stability of the film were found to be strongly dependent on the film thickness, which was believed to be associated with the evolution process of particle diffusion, agglomeration, and evaporation during annealing at high temperature. When the film thickness was smaller than 90 nm, the film SPR absorption can be attenuated until extinct with increasing annealing time due to the evaporation of Ag particles. While the film thickness was larger than 120 nm, the absorption can keep constant even after annealing for 64 h due to the agglomeration of Ag particles. On the base of film thickness results, the multilayer Al{sub 2}O{sub 3}:Ag solar selective thin films were prepared and the thermal stability test illustrated that the solar selectivity of multilayer films with absorbing layer thickness larger than 120 nm did not degrade after annealing at 500 Degree-Sign C for 70 h in air. It can be concluded that film thickness is an important factor to control the thermal stability of Al{sub 2}O{sub 3}:Ag thin films as high-temperature solar selective absorbers.

  1. Thermal stability of ultrasoft Fe-Zr-N films

    NARCIS (Netherlands)

    Chechenin, NG; van Veen, A; Schut, H; Chezan, AR; Boerma, D; Vystavel, T; De Hosson, JTM

    2003-01-01

    The thermal stability of nanocrystalline ultrasoft magnetic (Fe98Zr2)(1-x)N-x films with x = 0.10-0.25 was studied using thermal desorption spectrometry, positron beam analysis and high resolution transmission electron microscopy. The results demonstrate that grain growth during the heat treatment

  2. Optical stability under photo-irradiation of urushi films by ion implantation

    Energy Technology Data Exchange (ETDEWEB)

    Awazu, Kaoru; Funada, Yoshinori; Kasamori, Masato; Sakamoto, Makoto; Ichikawa, Tachio [Industrial Research Inst. of Ishikawa, Kanazawa (Japan)

    1995-06-01

    Nitrogen ions, argon ions and others were implanted in urushi-coated surfaces by using a simplified ion implantation apparatus, and the optical stability test was carried out by a sunshine weather meter. The rate of remaining luster on urushi-coated surfaces accompanying ultraviolet irradiation showed respective peculiar behavior according to the kinds of the implanted ions, the time of implantation, transparent and black urushi films, and the use of brightener or not. In electron beam irradiation, change hardly occurred. In urushi-coated products, the luster and the properties are maintained for long period, therefore recently, urushi coating has become to be applied to road sign panels and notice boards in addition to lacquer wares and applied fine art products, and the improvement of the optical stability of urushi films has become the subject. In this study, the experimental methods on urushi coating, ion implantation, the optical stability test and measuring method are explained. The changes of urushi film luster, transmittance, haze, lightness, and chromaticity by nitrogen ion implantation are reported. (K.I.).

  3. Optical stability under photo-irradiation of urushi films by ion implantation

    International Nuclear Information System (INIS)

    Awazu, Kaoru; Funada, Yoshinori; Kasamori, Masato; Sakamoto, Makoto; Ichikawa, Tachio

    1995-01-01

    Nitrogen ions, argon ions and others were implanted in urushi-coated surfaces by using a simplified ion implantation apparatus, and the optical stability test was carried out by a sunshine weather meter. The rate of remaining luster on urushi-coated surfaces accompanying ultraviolet irradiation showed respective peculiar behavior according to the kinds of the implanted ions, the time of implantation, transparent and black urushi films, and the use of brightener or not. In electron beam irradiation, change hardly occurred. In urushi-coated products, the luster and the properties are maintained for long period, therefore recently, urushi coating has become to be applied to road sign panels and notice boards in addition to lacquer wares and applied fine art products, and the improvement of the optical stability of urushi films has become the subject. In this study, the experimental methods on urushi coating, ion implantation, the optical stability test and measuring method are explained. The changes of urushi film luster, transmittance, haze, lightness, and chromaticity by nitrogen ion implantation are reported. (K.I.)

  4. Effect of accelerated aging on translucency of monolithic zirconia

    Directory of Open Access Journals (Sweden)

    O. Abdelbary

    2016-12-01

    Conclusion: Thickness of zirconia has significant effect on translucency. Aging has significant effect on thinner sections of zirconia. More research is required on zirconia towards making the material more translucent for its potential use as esthetic monolithic restoration.

  5. Transmutation of americium and curium incorporated in zirconia-based host materials

    International Nuclear Information System (INIS)

    Raison, P.E.

    2001-01-01

    Presented are studies involving the incorporation of americium and curium in zirconia-based materials. First explored was the pseudo ternary system AmO 2 -ZrO 2 -Y 2 O 3 . It was determined that selected Y-CSZ materials can incorporate significant quantities of americium oxide and remain cubic single-phase. The cell parameters of these fluorite-type products were established to be linear with the AmO 2 content. The Cm 2 O 3 -ZrO 2 system was also investigated. It was found that at 25 mol% of CmO 1.5 , the Cm(III) stabilized zirconia in its cubic form (a = 5.21 ±0.01 Angstrom). At higher and lower concentrations, diphasic materials were encountered. At 50 mol% of CmO 1.5 , a pyrochlore oxide - Cm 2 Zr 2 O 7 - is formed (a = 10.63 ±0.02 Angstrom). (author)

  6. Zirconia dispersion as a toughening agent in alumina - Influence of the cerium oxide

    International Nuclear Information System (INIS)

    Gritti, Olivier

    1987-01-01

    The improvement of mechanical properties of alumina can be obtained by fine dispersion of zirconia particles. The addition of cerium oxide as a stabilizer of the tetragonal phase has been examined. Different powder preparations, based on impregnation of the alumina powder by zirconium and cerium precursor salts, have been studied. Parameters, such as properties of alumina powder and cerium oxide content, for the production of reactive powders have been determined by two laboratory processes. The sintering of these powders in air at 1600 deg. C has resulted in dense materials with homogeneous microstructure. The mechanical properties, in particular the biaxial flexure strength and the toughness, have been determined in the temperature range 20 deg. C-900 deg. C. A reinforcement of about 80 pc in comparison with alumina is achieved. The optimal composition is (Al 2 O 3 ) 0.8 (ZrO 2 ) 0.18 (CeO 2 ) 0.02 . In the other hand, powder preparation by spray drying has been chosen for an approach to a larger scale process. The sintered ceramics made with these powders present a double microstructure which does not affect the mechanical properties. The presence of cerium oxide produces the following improvements: - increased mobility of the intergranular zirconia inclusions which results in a faster densification; - stabilization of a tetragonal phase without prohibiting the stress induced transformation; - increase of the critical sizes of the tetragonal → monoclinic transformation; - a large decrease in the transformation kinetic in water at 300 deg. C in comparison with that observed for alumina-zirconia doped with yttrium oxide. (author) [fr

  7. Evaporation of Particle-Stabilized Emulsion Sunscreen Films.

    Science.gov (United States)

    Binks, Bernard P; Fletcher, Paul D I; Johnson, Andrew J; Marinopoulos, Ioannis; Crowther, Jonathan M; Thompson, Michael A

    2016-08-24

    We recently showed (Binks et al., ACS Appl. Mater. Interfaces, 2016, DOI: 10.1021/acsami.6b02696) how evaporation of sunscreen films consisting of solutions of molecular UV filters leads to loss of UV light absorption and derived sun protection factor (SPF). In the present work, we investigate evaporation-induced effects for sunscreen films consisting of particle-stabilized emulsions containing a dissolved UV filter. The emulsions contained either droplets of propylene glycol (PG) in squalane (SQ), droplets of SQ in PG or droplets of decane in PG. In these different emulsion types, the SQ is involatile and shows no evaporation, the PG is volatile and evaporates relatively slowly, whereas the decane is relatively very volatile and evaporates quickly. We have measured the film mass and area, optical micrographs of the film structure, and the UV absorbance spectra during evaporation. For emulsion films containing the involatile SQ, evaporation of the PG causes collapse of the emulsion structure with some loss of specular UV absorbance due to light scattering. However, for these emulsions with droplets much larger than the wavelength of light, the light is scattered only at small forward angles so does not contribute to the diffuse absorbance and the film SPF. The UV filter remains soluble throughout the evaporation and thus the UV absorption by the filter and the SPF remain approximately constant. Both PG-in-SQ and SQ-in-PG films behave similarly and do not show area shrinkage by dewetting. In contrast, the decane-in-PG film shows rapid evaporative loss of the decane, followed by slower loss of the PG resulting in precipitation of the UV filter and film area shrinkage by dewetting which cause the UV absorbance and derived SPF to decrease. Measured UV spectra during evaporation are in reasonable agreement with spectra calculated using models discussed here.

  8. Yield stress of alumina-zirconia suspensions

    International Nuclear Information System (INIS)

    Ramakrishnan, V.; Pradip; Malghan, S.G.

    1996-01-01

    The yield stress of concentrated suspensions of alumina, zirconia, and mixed alumina-zirconia powders was measured by the vane technique as a function of solids loading, relative amounts of alumina and zirconia, and pH. At the isoelectric point (IEP), the yield stress varied as the fourth power of the solids loading. The relative ratio of alumina and zirconia particles was important in determining the yield stress of the suspension at the IEP. The yield stress of single and mixed suspensions showed a marked variation with pH. The maximum value occurred at or near the IEP of the suspension. The effect of electrical double-layer forces on the yield stress can be described on the basis of the Derjaguin-Landau-Verwey-Overbeek (DLVO) theory. A normalized yield stress--that is, the ratio of the yield stress at a given pH to the yield stress at the IEP predicted by this model--showed good correlation with experimental data

  9. Synthesis, characterization and thermal stability of solid solutions Zr (Y, Fe, Mo)O {sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Legorreta-Garcia, F.; Esperanza Hernandez-Cruz, L.; Villanueva-Ibanez, M.; Flores-Gonzalez, M. A.

    2015-10-01

    The synthesis of Fe{sup 3}+, Mo{sup 4+} and Y{sup 3+} fully stabilized zirconia by the nitrate/urea combustion route and thermal stability in air was investigated. The solid solution obtained was characterized by X ray diffraction (XRD), scanning electron microscopy (SEM) and used the BET method for determining specific surface. The ceramic powders obtained were calcined at 1473 K in air atmosphere in order to determine their thermal stability. The scanning electron microscopy (SEM) results showed a homogeneous grain surface, measuring several tens of micrometers across. The crystallographic study revealed that by this method it was successfully achieved zirconia doped with Fe{sup 3+}, Mo{sup 4+} and Y{sup 3+} ions in the zirconia tetragonal monophase, even after calcinations. (Author)

  10. Temperature-dependent thermal conductivity of flexible yttria-stabilized zirconia substrate via 3ω technique

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Shivkant; Yarali, Milad; Mavrokefalos, Anastassios [Department of Mechanical Engineering, University of Houston, Houston, TX (United States); Shervin, Shahab [Materials Science and Engineering Program, University of Houston, Houston, TX (United States); Venkateswaran, Venkat; Olenick, Kathy; Olenick, John A. [ENrG Inc., Buffalo, NY (United States); Ryou, Jae-Hyun [Department of Mechanical Engineering, University of Houston, Houston, TX (United States); Materials Science and Engineering Program, University of Houston, Houston, TX (United States); Texas Center for Superconductivity, University of Houston (TcSUH), Houston, TX (United States)

    2017-10-15

    Thermal management in flexible electronic has proven to be challenging thereby limiting the development of flexible devices with high power densities. To truly enable the technological implementation of such devices, it is imperative to develop highly thermally conducting flexible substrates that are fully compatible with large-scale fabrication. Here, we present the thermal conductivity of state-of-the-art flexible yttria-stabilized zirconia (YSZ) substrates measured using the 3ω technique, which is already commercially manufactured via roll-to-roll technique. We observe that increasing the grain size increases the thermal conductivity of the flexible 3 mol.% YSZ, while the flexibility and transparency of the sample are hardly affected by the grain size enlargement. We exhibit thermal conductivity values of up to 4.16 Wm{sup -1}K {sup -1} that is at least 4 times higher than state-of-the-art polymeric flexible substrates. Phonon-hopping model (PHM) for granular material was used to fit the measured thermal conductivity and accurately define the thermal transport mechanism. Our results show that through grain size optimization, YSZ flexible substrates can be realized as flexible substrates, that pave new avenues for future novel application in flexible electronics through the utilization of both their ceramic structural flexibility and high heat dissipating capability. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  11. Effectiveness of screw surface coating on the stability of zirconia abutments after cyclic loading.

    Science.gov (United States)

    Basílio, Mariana de Almeida; Butignon, Luis Eduardo; Arioli Filho, João Neudenir

    2012-01-01

    Different surface treatments have been developed in attempts to prevent the loosening of abutment screws. The aim of the current study was to compare the effectiveness of titanium alloy screws with tungsten-doped diamond-like carbon (W-DLC) coating and uncoated screws in providing stability to zirconia (ZrO2) ceramic abutments after cyclic loading. Twenty prefabricated ZrO2 ceramic abutments on their respective external-hex implants were divided into two groups of equal size according to the type of screw used: uncoated titanium alloy screw (Ti) or titanium alloy screw with W-DLC coating (W-DLC/Ti). The removal torque value (preload) of the abutment screw was measured before and after loading. Cyclic loading between 11 and 211 N was applied at an angle of 30 degrees to the long axis of the implants at a frequency of 15 Hz. A target of 0.5 X 106 cycles was defined. Group means were calculated and compared using analysis of variance and the F test (α = .05). Before cyclic loading, the preload for Ti screws was significantly higher than that for W-DLC/Ti screws (P = .021). After cyclic loading, there was no significant difference between them (P = .499). Under the studied conditions, it can be concluded that, after cyclic loading, both abutment screws presented a significant reduction in the mean retained preload and similar effectiveness in maintaining preload.

  12. Damage Maps of Veneered Zirconia under Simulated Mastication

    Science.gov (United States)

    Kim, Jae-Won; Kim, Joo-Hyung; Janal, Malvin N.; Zhang, Yu

    2016-01-01

    Zirconia based restorations often fracture from chipping and/or delamination of the porcelain veneers. We hypothesize that veneer chipping/delamination is a result of the propagation of near-contact induced partial cone cracks on the occlusal surface under mastication. Masticatory loading involves the opposing tooth sliding along the cuspal inner incline surface with an applied biting force. To test this hypothesis, flat porcelain veneered zirconia plates were cemented to dental composites and cyclically loaded (contact–slide–liftoff) at an inclination angle as a simplified model of zirconia based restorations under occlusion. In the light of in-situ observation of damage evolution in a transparent glass/zirconia/polycarbonate trilayer, postmortem damage evaluation of porcelain/zirconia/composite trilayers using a sectioning technique revealed that deep penetrating occlusal surface partial cone fracture is the predominant fracture mode of porcelain veneers. Clinical relevance is discussed. PMID:19029080

  13. Using high thermal stability flexible thin film thermoelectric generator at moderate temperature

    Science.gov (United States)

    Zheng, Zhuang-Hao; Luo, Jing-Ting; Chen, Tian-Bao; Zhang, Xiang-Hua; Liang, Guang-Xing; Fan, Ping

    2018-04-01

    Flexible thin film thermoelectric devices are extensively used in the microscale industry for powering wearable electronics. In this study, comprehensive optimization was conducted in materials and connection design for fabricating a high thermal stability flexible thin film thermoelectric generator. First, the thin films in the generator, including the electrodes, were prepared by magnetron sputtering deposition. The "NiCu-Cu-NiCu" multilayer electrode structure was applied to ensure the thermal stability of the device used at moderate temperature in an air atmosphere. A design with metal layer bonding and series accordant connection was then employed. The maximum efficiency of a single PN thermocouple generator is >11%, and the output power loss of the generator is <10% after integration.

  14. Synthesis of Yttria-stabilized zirconia nanoparticles by decomposition of metal nitrates coated on carbon powder

    International Nuclear Information System (INIS)

    Jiang, S.; Stangle, G.C.; Amarakoon, V.R.; Schulze, W.A.

    1996-01-01

    Weakly agglomerated nanoparticles of yttria-stabilized zirconia (YSZ) were synthesized by a novel process which involved the decomposition of metal nitrates that had been coated on ultrafine carbon black powder, after which the carbon black was gasified. The use of ultrafine, high-surface-area carbon black powder apparently allowed the nanocrystalline oxide particles to form and remain separate from each other, after which the carbon black was gasified at a somewhat higher temperature. As a result, the degree of agglomeration was shown to be relatively low. The average crystallite size and the specific surface area of the as-synthesized YSZ nanoparticles were 5∼6 nm and 130 m 2 /g, respectively, for powder synthesized at 650 degree C. The as-synthesized YSZ nanoparticles had a light brown color and were translucent, which differs distinctly from conventional YSZ particles which are typically white and opaque. The mechanism of the synthesis process was investigated, and indicated that the gasification temperature had a direct effect on the crystallite size of the as-synthesized YSZ nanoparticles. High-density and ultrafine-grained YSZ ceramic articles were prepared by fast-firing, using a dwell temperature of 1250 degree C and a dwell time of two minutes or less. copyright 1996 Materials Research Society

  15. The thermal stability of the carbon-palladium films for hydrogen sensor applications

    Science.gov (United States)

    Rymarczyk, Joanna; Czerwosz, ElŻbieta; Diduszko, Ryszard; Kozłowski, Mirosław

    2017-08-01

    The thermal stability of two types of C-Pd films prepared in PVD process were studied. These films are composed of Pd nanograins embedded in a multiphase carbonaceous matrix. These films were distinguished by Pd content. These films were annealed in a range of temperatures 50÷1000°C. The structural, topographical and molecular changes were studied by scanning electron microscopy (SEM), infrared spectroscopy (FTIR) and X-ray diffraction (XRD) methods. The results show that investigated films are thermally stable up to 200°C.

  16. Internal Nano Voids in Yttria-Stabilised Zirconia (YSZ Powder

    Directory of Open Access Journals (Sweden)

    Chen Barad

    2017-12-01

    Full Text Available Porous yttria-stabilised zirconia ceramics have been gaining popularity throughout the years in various fields, such as energy, environment, medicine, etc. Although yttria-stabilised zirconia is a well-studied material, voided yttria-stabilised zirconia powder particles have not been demonstrated yet, and might play an important role in future technology developments. A sol-gel synthesis accompanied by a freeze-drying process is currently being proposed as a method of obtaining sponge-like nano morphology of embedded faceted voids inside yttria-stabilised zirconia particles. The results rely on a freeze-drying stage as an effective and simple method for generating nano-voided yttria-stabilised zirconia particles without the use of template-assisted additives.

  17. Nanostructured thin film La{sub 0.6}Sr{sub 0.4}CoO{sub 3-δ} synthesized via salt-assisted spray pyrolysis for micro-SOFC application

    Energy Technology Data Exchange (ETDEWEB)

    Benel, Cahit; Darbandi, Azad J. [Institute for Nanotechnology, Karlsruhe Institute of Technology (Germany); Joint Research Laboratory Nanomaterials/Technische Universitaet Darmstadt and Karlsruhe Institute of Technology (Germany); Center for Functional Nanostructures, Karlsruhe Institute of Technology (Germany); Evans, Anna; Toelke, Rene [Nonmetallic Inorganic Materials, Department of Materials, ETH Zurich (Switzerland); Hahn, Horst [Institute for Nanotechnology, Karlsruhe Institute of Technology (Germany); Joint Research Laboratory Nanomaterials/Technische Universitaet Darmstadt and Karlsruhe Institute of Technology (Germany)

    2012-07-01

    Micro-solid oxide fuel cells (micro-SOFCs) are anticipated for battery replacement due to their increased energy capacity for applications such as portable electronic devices, mobile phones and laptops. In this work, nanocrystalline La{sub 0.6}Sr{sub 0.4}CoO{sub 3-δ} (LSC) powder with ultrafine microstructure and high specific surface area was synthesized via salt-assisted spray pyrolysis method. XRD results show the formation of a nanocrystalline single phase perovskite structure. Agglomerate-free LSC nanoparticles were stabilized in water-based dispersion without the need of ultrasonic energy application. Nanoparticulate cathode thin films of LSC with thickness between 150 and 500 nm were prepared via single step spin coating on yttria stabilized zirconia (YSZ) substrates. Gadolinium doped ceria (GDC) film was applied to YSZ substrate to avoid the chemical reaction between cathode and electrolyte. The performance of the thin film cathodes was evaluated by high temperature impedance spectroscopy on symmetrical samples.

  18. Role of temperature and energy density in the pulsed laser deposition of zirconium oxide thin film

    International Nuclear Information System (INIS)

    Mittra, Joy; Abraham, G.J.; Viswanadham, C.S.; Kulkarni, U.D.; Dey, G.K.

    2011-01-01

    Present work brings out the effects of energy density and substrate temperature on pulsed laser deposition of zirconium oxide thin film on Zr-base alloy substrates. The ablation of sintered zirconia has been carried out using a KrF excimer laser having 30 ns pulse width and 600 mJ energy at source at 10 Hz repetition rate. To comprehend effects of these parameters on the synthesized thin film, pure zirconia substrate has been ablated at two different energy densities, 2 J.cm -2 and 5 J.cm -2 , keeping the substrate at 300 K, 573 K and 873 K, respectively. After visual observation, deposited thin films have been examined using Raman Spectroscopy (RS) and X-ray Photo-electron Spectroscopy (XPS). It has been found that the oxide deposited at 300 K temperature does not show good adherence with the substrate and deteriorates further with the reduction in energy density of the incident laser. The oxide films, deposited at 573 K and 873 K, have been found to be adherent with the substrate and appear lustrous black. These indicate that the threshold for adherence of the zirconia film on the Zr-base alloy substrate lies in between 300 K and 573 K. Analysis of Raman spectra has indicated that thin films of zirconia, deposited using pulsed laser, on the Zr-base metallic substrate are initially in amorphous state. Experimental evidence has indicated a strong link among the degree of crystallinity of the deposited oxide film, the substrate temperature and the energy density. It also has shown that the crystallization of the oxide film is dependent on the substrate temperature and the duration of holding at high temperature. The O:Zr ratios of the films, analyzed from the XPS data, have been found to be close to but less than 2. This appears to explain the reason for the transformation of amorphous oxide into monoclinic and tetragonal phases, below 573 K, and not into cubic phase, which is reported to be more oxygen deficient. (author)

  19. Hydrodynamic stability of thermoviscous liquid film inside a rotating horizontal cylinder: Heating and cooling effects

    Science.gov (United States)

    Kumawat, Tara Chand; Tiwari, Naveen

    2018-03-01

    Steady two-dimensional solutions and their stability analysis are presented for thin film of a thermoviscous liquid flowing inside a cylinder rotating about its horizontal axis. The inner surface of the cylinder is either uniformly hotter or colder than the enveloping air. The mass, momentum, and energy equations are simplified using thin-film approximation. The analytically obtained film thickness evolution equation consists of various dimensionless parameters such as gravitational number, Bond number, Biot number, thermoviscosity number, and Marangoni number. The viscosity of the liquid is considered as an exponential function of temperature. The viscosity increases (decreases) within the film thickness away from the inner surface of the cylinder when the surface is uniformly hotter (colder) than the atmosphere. For hotter (colder) surface, the film thickness on the rising side decreases (increases) when convective heat transfer at the free surface is increased. The surface tension gradient at the free surface generates Marangoni stress that has a destabilizing (stabilizing) effect on the thin film flow in the case of a hotter (colder) cylinder. The thermoviscosity number stabilizes (destabilizes) the flow on a heating (cooling) surface and this effect increases with an increase in the heat transfer at the free surface. For a hotter surface and in the presence of Marangoni stress, the convective heat transfer at the interface has the destabilizing effect for small values of the Biot number and assumes a stabilizing role for larger values. Non-linear simulations show consistency with the linear stability analysis.

  20. Monoclinic phase transformation and mechanical durability of zirconia ceramic after fatigue and autoclave aging.

    Science.gov (United States)

    Mota, Yasmine A; Cotes, Caroline; Carvalho, Rodrigo F; Machado, João P B; Leite, Fabíola P P; Souza, Rodrigo O A; Özcan, Mutlu

    2017-10-01

    This study evaluated the influence of two aging procedures on the biaxial flexural strength of yttria-stabilized tetragonal zirconia ceramics. Disc-shaped zirconia specimens and (ZE: E.max ZirCAD, Ivoclar; ZT: Zirkon Translucent, Zirkonzahn) (N = 80) (∅:12 mm; thickness:1.2 mm, ISO 6872) were prepared and randomly divided into four groups (n = 10 per group) according to the aging procedures: C: Control, no aging; M: mechanical cycling (2 × 10 6 cycles/3.8 Hz/200 N); AUT: Aging in autoclave at 134°C, 2 bar for 24 h; AUT + M: Autoclave aging followed by mechanical cycling. After aging, the transformed monoclinic zirconia (%) were evaluated using X-ray diffraction and surface roughness was measured using atomic force microscopy. The average grain size was measured by scanning electron microscopy and the specimens were submitted to biaxial flexural strength testing (1 mm/min, 1000 kgf in water). Data (MPa) were statistically analyzed using 2-way analysis of variance and Tukey's test (α = 0.05). Aging procedures significantly affected (p = 0.000) the flexural strength data but the effect of zirconia type was not significant (p = 0.657). AUT ZT (936.4 ± 120.9 b ) and AUT + M ZE (867.2 ± 49.3 b ) groups presented significantly higher values (p autoclave aging alone or with mechanical aging increased the flexure strength but also induced higher transformation from tetragonal to monoclinic phase in both zirconia materials tested. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 1972-1977, 2017. © 2016 Wiley Periodicals, Inc.

  1. Tribological properties of coating films for core structure of HTGR

    International Nuclear Information System (INIS)

    Ozawa, Kenji; Kikuchi, Akiyoshi; Kawakami, Haruo

    1985-01-01

    The tribological properties of the various coating films used for the in-core structures of a high temperature gas-cooled experimental reactor were examined. When the explosion sprayed films of chrome carbide were applied for preventing galling in core restraining mechanism, the hardness of substrate materials exerted influence on the strength of the coating films. Also the effect of the surface roughness of the plasma sprayed films of zirconia on the sliding characteristics of the zirconia films and PGX graphite used for support plates was clarified. The coefficient of friction and the dependence of the amount of wear on surface pressure of these materials were examined. These results have been effectively utilized for the design of the test bodies of HENDEL-T2. In helium atmosphere, oxide film is hard to be formed on metal surface, especially on the contact surface of metals exposed to high temperature, there is the possibility to cause adhesion due to mutual diffusion and galling in sliding. As the means to prevent those, ceramic coating has been attempted. Sliding test, high pressure joining test, thermal cycle test and corrosion test in helium were carried out to evaluate the properties. (Koko, I.)

  2. Orthodontic bracket bonding to glazed full-contour zirconia

    Directory of Open Access Journals (Sweden)

    Ji-Young Kwak

    2016-05-01

    Full Text Available Objectives This study evaluated the effects of different surface conditioning methods on the bond strength of orthodontic brackets to glazed full-zirconia surfaces. Materials and Methods Glazed zirconia (except for the control, Zirkonzahn Prettau disc surfaces were pre-treated: PO (control, polishing; BR, bur roughening; PP, cleaning with a prophy cup and pumice; HF, hydrofluoric acid etching; AA, air abrasion with aluminum oxide; CJ, CoJet-Sand. The surfaces were examined using profilometry, scanning electron microscopy, and electron dispersive spectroscopy. A zirconia primer (Z-Prime Plus, Z or a silane primer (Monobond-S, S was then applied to the surfaces, yielding 7 groups (PO-Z, BR-Z, PP-S, HF-S, AA-S, AA-Z, and CJ-S. Metal bracket-bonded specimens were stored in water for 24 hr at 37℃, and thermocycled for 1,000 cycles. Their bond strengths were measured using the wire loop method (n = 10. Results Except for BR, the surface pre-treatments failed to expose the zirconia substructure. A significant difference in bond strengths was found between AA-Z (4.60 ± 1.08 MPa and all other groups (13.38 ± 2.57 - 15.78 ± 2.39 MPa, p < 0.05. For AA-Z, most of the adhesive remained on the bracket. Conclusions For bracket bonding to glazed zirconia, a simple application of silane to the cleaned surface is recommended. A zirconia primer should be used only when the zirconia substructure is definitely exposed.

  3. Natural radioactivity in zirconia-based dental ceramics

    International Nuclear Information System (INIS)

    Giussani, Augusto; Gerstmann, Udo; La Porta, Caterina; Cantone, Marie C.; Veronese, Ivan

    2008-01-01

    Zirconia-based ceramics are being increasingly used in dental prosthetics in substitution of metal cores, which are known to induce local toxic reactions and delayed allergic responses in the oral tissues. Some concerns have been however raised about the use of zirconia, since it is known that unpurified zirconia materials may contain non negligible levels of natural radionuclides of the U/Th series. Combined measurements of alpha and gamma spectrometry as well as beta dosimetry were conducted on zirconia samples used for dental applications. Samples were available in form of powder and/or solid blocks. The results showed that the beta dose rate in zirconia ceramics was on average only slightly higher than the levels measured in natural teeth, and generally lower than the values measured in feldspatic and glass ceramics. These materials are indeed known to deliver a beta dose significantly higher than that measured from natural teeth, due to the relatively high levels of 40 K (between 2 and 3 kBq·kg -1 ). The content of radionuclides of the U/Th series in the zirconia sample was estimated to be lower than 15 Bq·kg -1 , i.e. doubtlessly below the exclusion level of 1 kBq·kg -1 recommended by IAEA in the Safety Standard Series. Beta dosimetry measurements, however, gave indications of possible inhomogeneous clusters of radioactivity, which might give rise to local doses above the background. (author)

  4. Transmutation of americium and curium incorporated in zirconia-based host materials

    Energy Technology Data Exchange (ETDEWEB)

    Raison, P.E. [CEA Cadarache, 13 - Saint-Paul-lez-Durance (France). Dept. d' Etudes des Combustibles; Haire, R.G. [Oak Ridge National Lab., TN (United States)

    2001-07-01

    Presented are studies involving the incorporation of americium and curium in zirconia-based materials. First explored was the pseudo ternary system AmO{sub 2}-ZrO{sub 2}-Y{sub 2}O{sub 3}. It was determined that selected Y-CSZ materials can incorporate significant quantities of americium oxide and remain cubic single-phase. The cell parameters of these fluorite-type products were established to be linear with the AmO{sub 2} content. The Cm{sub 2}O{sub 3}-ZrO{sub 2} system was also investigated. It was found that at 25 mol% of CmO{sub 1.5}, the Cm(III) stabilized zirconia in its cubic form (a = 5.21 {+-}0.01 Angstrom). At higher and lower concentrations, diphasic materials were encountered. At 50 mol% of CmO{sub 1.5}, a pyrochlore oxide - Cm{sub 2}Zr{sub 2}O{sub 7} - is formed (a = 10.63 {+-}0.02 Angstrom). (author)

  5. Controlling plasmonic properties of epitaxial thin films of indium tin oxide in the near-infrared region

    Science.gov (United States)

    Kamakura, R.; Fujita, K.; Murai, S.; Tanaka, K.

    2015-06-01

    Epitaxial thin films of indium tin oxide (ITO) were grown on yttria-stabilized zirconia single-crystal substrates by using a pulsed laser deposition to examine their plasmonic properties. The dielectric function of ITO was characterized by spectroscopic ellipsometry. Through the concentration of SnO2 in the target, the carrier concentration in the films was modified, which directly leads to the tuning of the dielectric function in the near-infrared region. Variable-angle reflectance spectroscopy in the Kretschmann geometry shows the dip in the reflection spectrum of p-polarized light corresponding to the excitation of surface plasmon polaritions (SPPs) in the near-infrared region. The excitation wavelength of the SPPs was shifted with changing the dielectric functions of ITO, which is reproduced by the calculation using transfer matrix method.

  6. Microstructural evolution of alumina-zirconia nanocomposites

    International Nuclear Information System (INIS)

    Ojaimi, C.L.; Chinelatto, A.S.A.; Chinelatto, A.L.; Pallone, E.M.J.A.

    2012-01-01

    Ceramic materials have limited use due to their brittleness. The inclusion of nanosized particles in a ceramic matrix, which are called nanocomposites, and ceramic processing control by controlling the grain size and densification can aid in obtaining ceramic products of greater strength and toughness. Studies showed that the zirconia nano inclusions in the matrix of alumina favors an increase in mechanical properties by inhibiting the grain growth of the matrix and not by the mechanism of the transformation toughening phase of zirconia. In this work, the microstructural evolution of alumina nanocomposites containing 15% by volume of nanometric zirconia was studied. From the results it was possible to understand the sintering process of these nanocomposites. (author)

  7. Asymmetric diffusion of Zr, Sc and Ce, Gd at the interface between zirconia electrolyte and ceria interlayer for solid oxide fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Liang, Bo, E-mail: Liangbo@gdut.edu.cn; Tao, Tao; Zhang, Silong; Huang, Yongan; Cai, Zhihong; Lu, Shenguo, E-mail: sglu@gdut.edu.cn

    2016-09-15

    The microstructures of cathode interlayer and elemental diffusion behaviors across the interfacial region (electrolyte/interlayer) have been characterized using high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD) and scanning TEM combined with energy dispersive X-ray spectroscopy (STEM-EDS). A densified film about 100 nm is locally formed at the interface of electrolyte/interlayer as the interlayer using dip-coating method and being sintered at 1200 °C. It is observed that the compositional distribution curves across the interface are asymmetric. More amount of the Zr, Sc component is detected in gadolinium-doped ceria (GDC) than that of the Ce, Gd component is detected in scandia-stabilized-zirconia (SSZ). XRD and EDS results show that the densified layer might consist of (Zr, Ce)O{sub 2}-based solid solution. The high open circuit voltage of the cell is related to the dense structure of electrolyte, while the increased activation energy in overpotential resistance is attributed to the porous structure of interlayer as well as the high resistance phases locally formed at its interface. - Highlights: • The (Ce−Zr)O{sub 2} based solid solution was locally formed at 1200 °C. • More Zr, Sc elements were detected in GDC than Ce, Gd elements in SSZ. • Zirconia nanodomain was embedded in GDC beside grain boundary. • High OCVs were achieved due to the highly dense electrolyte layer.

  8. Impact of gastric acidic challenge on surface topography and optical properties of monolithic zirconia.

    Science.gov (United States)

    Sulaiman, Taiseer A; Abdulmajeed, Aous A; Shahramian, Khalil; Hupa, Leena; Donovan, Terrence E; Vallittu, Pekka; Närhi, Timo O

    2015-12-01

    To evaluate the surface topography and optical properties of monolithic zirconia after immersion in simulated gastric acid. Four partially stabilized (PSZ) and one fully stabilized (FSZ) zirconia materials were selected for the study: Prettau (PRT, Zirkonzahn), Zenostar (ZEN, Ivoclar), Bruxzir (BRX, Glidewell), Katana (KAT, Noritake) and FSZ Prettau Anterior (PRTA, Zirkonzahn). IPS e.max (Ivoclar) was used as a control. The specimens (10×10×1.2mm, n=5 per material) were cut, sintered, polished and cleaned before immersed in 5ml of simulated gastric acid solution (Hydrochloric acid (HCl) 0.06M, 0.113% solution in deionized distal water, pH 1.2) for 96h in a 37°C incubator. Specimens were weighed and examined for morphological changes under scanning electron microscope (SEM) coupled with energy dispersive X-ray spectroscopy (EDX). Surface roughness was evaluated by a confocal microscope. Surface gloss and translucency parameter (TP) values were determined by a reflection spectrophotometer before and after acid immersion. The data was analyzed by one-way ANOVA followed by Tukey's HSD post hoc test (pgloss of ZEN, PRTA and IPS e.max increased (p<0.05). Monolithic zirconia materials show some surface alterations in an acidic environment with minimum effect on their optical properties. Whether a smoother surface is in fact a sign of true corrosion resistance or is purely the result of an evenly progressive corrosive process is yet to be confirmed by further research. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  9. Stability, bistability and instability of amorphous ZrO2 resistive memory devices

    International Nuclear Information System (INIS)

    Parreira, P; Paterson, G W; McVitie, S; MacLaren, D A

    2016-01-01

    Amorphous zirconium oxide thin films deposited at room temperature, sandwiched between Pt and Ti electrodes, show resistive bipolar resistive switching with good overall performance figures (retention, ON/OFF ratio and durability). A variability observed during electrical characterisation is consistent with the coexistence of two different resistive switching mechanisms within the ZrO 2 layer. Electron energy loss spectroscopy is used to map chemical variations across the device on the nanoscale. Partial oxidation of the Ti electrode creates an ohmic contact with zirconia and injects positively charged oxygen vacancies into the zirconia layer that are then responsible for resistive switching at the Pt / zirconia interface. (paper)

  10. Thermal stability of tungsten sub-nitride thin film prepared by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, X.X. [School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050 (China); State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China); Wu, Y.Z., E-mail: youzhiwu@163.com [School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050 (China); Mu, B. [College of Petrochemical Technology, Lanzhou University of Technology, Lanzhou, 730050 (China); Qiao, L. [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China); Li, W.X.; Li, J.J. [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); Wang, P., E-mail: pengwang@licp.cas.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China)

    2017-03-15

    Tungsten sub-nitride thin films deposited on silicon samples by reactive magnetron sputtering were used as a model system to study the phase stability and microstructural evolution during thermal treatments. XRD, SEM&FIB, XPS, RBS and TDS were applied to investigate the stability of tungsten nitride films after heating up to 1473 K in vacuum. At the given experimental parameters a 920 nm thick crystalline film with a tungsten and nitrogen stoichiometry of 2:1 were achieved. The results showed that no phase and microstructure change occurred due to W{sub 2}N film annealing in vacuum up to 973 K. Heating up to 1073 K led to a partial decomposition of the W{sub 2}N phase and the formation of a W enrichment layer at the surface. Increasing the annealing time at the same temperature, the further decomposition of the W{sub 2}N phase was negligible. The complete decomposition of W{sub 2}N film happened as the temperature reached up to 1473 K.

  11. Effect of spherical porosity on co-fired dense/porous zirconia bi-layers cambering

    DEFF Research Database (Denmark)

    Teocoli, Francesca; Marani, Debora; Kiebach, Wolff-Ragnar

    2018-01-01

    analyze the model case of dense taped of 8 mol% Y2O3-stabilized ZrO2 laminated on ca. 400 μ thick 3 mol% Y2O3 doped zirconia porous tapes, with homogenous spherical porosity of 13 vol%, 46 vol%, and 54 vol%. Sintering stress during densification is evaluated from the shrinkage rates and viscoelastic...

  12. In situ growth and characterization of La{sub 0.8}Sr{sub 0.2}CoO{sub 3} perovskite mixed conductor films

    Energy Technology Data Exchange (ETDEWEB)

    Brosha, E.L.; Chung, B.W.; Garzon, F.H.; Raistrick, I.D.; Houlton, R.J.; Hawley, M.E. [Los Alamos National Lab., NM (United States)

    1995-05-01

    The authors have grown thin films of La{sub 0.8}Sr{sub 0.2}CoO{sub 3} on SrTiO{sub 3} [100], MgO [100], yttrium-stabilized zirconia YSZ [100], and CeO{sub 2} [100]/Al{sub 2}O{sub 3} substrates by using a 90{degree} off-axis RF magnetron sputtering deposition. X-ray diffraction analysis reveals that, depending on substrate, the deposited films grew either epitaxially or highly textured. Scanning tunneling microscopy reveals that the thin films grow with a smooth surface and with different growth mechanisms according to substrate. For La{sub 0.8}Sr{sub 0.2}CoO{sub 3} thin films grown on MgO [100], the low values of the channeling minimum yield from Rutherford backscattering spectroscopy indicated excellent epitaxy with the substrate. Thin films of perovskite materials are among the major focal research areas for optical, sensor, electronic, and superconducting applications.

  13. Surface roughness and hardness of yttria stabilized zirconia (Y-TZP after 10 years of simulated brushing

    Directory of Open Access Journals (Sweden)

    Lucas Miguel Candido

    Full Text Available Introduction: The Y-TZP zirconia used for prosthetic infrastructure, in some clinical situations, can be exposed to the oral environment. In these situations, a polished surface without changes is extremely important. Objective: The aim of this study was to evaluate the mean roughness (Ra and Vickers hardness of Y-TZP zirconia (Lava™ after simulating ten years of brushing. Material and method: Thirty-six Y-TZP bar-shaped specimens (20mm X 4mm X 1.2mm were divided into three groups: storage in distilled water (DW, n=12, control; brushing with distilled water (BDW, n=12 and brushing with distilled water and fluoride toothpaste (BFT, n=12. Brushing was performed using a brushing machine with a soft-bristled toothbrush, simulating 10 years of brushing (878.400 cycles, 100gf. The mean roughness (Ra in μm and Vickers hardness (VHN of all specimens were measured twice: before and after the experimental treatment, in profilometer and microhardness tester (500gf, 30 seconds, respectively. Data were analyzed using the two-way ANOVA test (α = 0.05. Result: The interaction between groups was not significant for roughness (p = 0.701 nor for hardness (p = 0.928. The final averages for Ra (μm were equal to: DW - 0.63; BDW - 0.64; and, BFT - 0.68. The final averages for Vickers hardness (VHN were: DW - 1301.16; BDW - 1316.60; and, BFT - 1299.58. Conclusion: It was concluded that the brushing with distilled or fluoridated toothpaste was not able to change the roughness and hardness of Y-TZP zirconia used in this study.

  14. Performance evaluation of solid oxide fuel cells with thin film electrolyte fabricated by binder-assisted slurry casting

    Energy Technology Data Exchange (ETDEWEB)

    Guo, W.M.; Liu, X.M.; Li, L.J. [Department of Biological and Chemical Engineering, Guangxi University of Technology, Liuzhou 545006 (China); Xiao, Y.F. [Department of Stomatology, Liuzhou Maternity and Child Health Hospital, Liuzhou 545001 (China); Chen, Y. [School of Yingdong Life Science, Shaoguan University, Shaoguan 512005 (China)

    2011-10-15

    A gas-tight yttria-stabilized zirconia (YSZ) electrolyte film was fabricated on porous NiO-YSZ anode substrates by a binder-assisted slurry casting technique. The scanning electron microscope (SEM) results showed that the YSZ film was relatively dense with a thickness of 10 {mu}m. La{sub 0.8}Sr{sub 0.2}MnO{sub 3} (LSM)-YSZ was applied to cathode using a screen-print technique and the single fuel cells were tested in a temperature range from 600 to 800 C. An open circuit voltage (OCV) of over 1.0 V was observed. The maximum power densities at 600, 700, and 800 C were 0.13, 0.44, and 1.1 W cm{sup -2}, respectively. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  15. Effects of different lasers and particle abrasion on surface characteristics of zirconia ceramics.

    Directory of Open Access Journals (Sweden)

    Sakineh Arami

    2014-04-01

    Full Text Available The aim of this study was to assess the surface of yttrium-stabilized tetragonal zirconia (Y-TZP after surface treatment with lasers and airborne-particle abrasion.First, 77 samples of presintered zirconia blocks measuring 10 × 10 × 2 mm were made, sintered and polished. Then, they were randomly divided into 11 groups (n=7 and received surface treatments namely, Er:YAG laser irradiation with output power of 1.5, 2 and 2.5 W, Nd:YAG laser with output power of 1.5, 2 and 2.5 W, CO2 laser with output power of 3, 4 and 5 W, AL2O3 airborne-particle abrasion (50μ and no treatment (controls. Following treatment, the parameters of surface roughness such as Ra, Rku and Rsk were evaluated using a digital profilometer and surface examination was done by SEM.According to ANOVA and Tukey's test, the mean surface roughness (Ra after Nd:YAG laser irradiation at 2 and 2.5 W was significantly higher than other groups. Roughness increased with increasing output power of Nd:YAG and CO2 lasers. Treated surfaces by Er:YAG laser and air abrasion showed similar surface roughness. SEM micrographs showed small microcracks in specimens irradiated with Nd:YAG and CO2 lasers.Nd:YAG laser created a rough surface on the zirconia ceramic with many microcracks; therefore, its use is not recommended. Air abrasion method can be used with Er:YAG laser irradiation for the treatment of zirconia ceramic.

  16. An eigenstrain approach to predict phase transformation and self-accommodation in partially stabilized zirconia

    International Nuclear Information System (INIS)

    Hensl, Th.; Mühlich, U.; Budnitzki, M.; Kuna, M.

    2015-01-01

    Highlights: • Analytical model to predict phase transformation in PSZ is developed. • Analytical model to predict number of twins in monoclinic inclusions in PSZ. • Models consider inclusions size, shape, temperature, remote loading and surface energy. - Abstract: This work focuses on micromechanical modeling of the tetragonal to monoclinic phase transformation (t–m transformation) in partially stabilized zirconia (PSZ). Tetragonal particles dispersed in a cubic matrix may transform into the monoclinic phase under sufficiently high mechanical loading or if the material is cooled down below a critical temperature. This phase transformation is supposed to be responsible for the so called transformation toughening effect of PSZ. The transformation is usually accompanied by a self-accommodation process, which reduces the occurring eigenstresses in the surrounding matrix. The influences of particle size and geometry, chemical driving force, temperature, surface energy and remote loading on the t–m transformation are estimated by a thermostatic approach. We assume, that transformations occur, once the Gibbs free energy of the transformed equilibrium state is lower than that of the untransformed reference state. To obtain an analytical solution, the microstructure is modeled as an inclusion of rectangular cross section, restrained by an infinite elastic matrix, under plane strain conditions. The developed model for phase transformation captures the well-known size and temperature dependencies. Furthermore, it indicates a significant influence of the particle geometry, that large aspect ratios of the inclusion’s cross section lower the trigger stress for phase transformation

  17. Raman spectroscopic characterization of ZrO2 and yttrium stabilized zirconias

    DEFF Research Database (Denmark)

    Kjerulf-Jensen, N.; Berg, Rolf W.; Poulsen, Finn Willy

    1996-01-01

    Current literature on the analysis of vibrational spectra of monoclinic, tetragonal and cubic zirconias is reviewed. The selection rules based on simple factor group analysis are not obeyed for the structurally disordered tetragonal and cubic materials. The interpretation is thus not straight...... in clear single crystals and may tentatively be assigned to rare earth impurities (e.g. Er, Tb, Ho, Eu), although other causes are possible. Upon cooling to liquid temperature these bands grow in intensity, ruling out their assignment as vibrational over- or combination tones. The low frequency modes...

  18. Comparison of bond strengths of ceramic brackets bonded to zirconia surfaces using different zirconia primers and a universal adhesive.

    Science.gov (United States)

    Lee, Ji-Yeon; Ahn, Jaechan; An, Sang In; Park, Jeong-Won

    2018-02-01

    The aim of this study is to compare the shear bond strengths of ceramic brackets bonded to zirconia surfaces using different zirconia primers and universal adhesive. Fifty zirconia blocks (15 × 15 × 10 mm, Zpex, Tosoh Corporation) were polished with 1,000 grit sand paper and air-abraded with 50 µm Al 2 O 3 for 10 seconds (40 psi). They were divided into 5 groups: control (CO), Metal/Zirconia primer (MZ, Ivoclar Vivadent), Z-PRIME Plus (ZP, Bisco), Zirconia Liner (ZL, Sun Medical), and Scotchbond Universal adhesive (SU, 3M ESPE). Transbond XT Primer (used for CO, MZ, ZP, and ZL) and Transbond XT Paste was used for bracket bonding (Gemini clear ceramic brackets, 3M Unitek). After 24 hours at 37°C storage, specimens underwent 2,000 thermocycles, and then, shear bond strengths were measured (1 mm/min). An adhesive remnant index (ARI) score was calculated. The data were analyzed using one-way analysis of variance and the Bonferroni test ( p = 0.05). Surface treatment with primers resulted in increased shear bond strength. The SU group showed the highest shear bond strength followed by the ZP, ZL, MZ, and CO groups, in that order. The median ARI scores were as follows: CO = 0, MZ = 0, ZP = 0, ZL = 0, and SU = 3 ( p < 0.05). Within this experiment, zirconia primer can increase the shear bond strength of bracket bonding. The highest shear bond strength is observed in SU group, even when no primer is used.

  19. Straight-chain halocarbon forming fluids for TRISO fuel kernel production – Tests with yttria-stabilized zirconia microspheres

    Energy Technology Data Exchange (ETDEWEB)

    Baker, M.P. [Nuclear Science and Engineering Program, Metallurgical and Materials Engineering Department, Colorado School of Mines, 1500 Illinois St., Golden, CO 80401 (United States); King, J.C., E-mail: kingjc@mines.edu [Nuclear Science and Engineering Program, Metallurgical and Materials Engineering Department, Colorado School of Mines, 1500 Illinois St., Golden, CO 80401 (United States); Gorman, B.P. [Metallurgical and Materials Engineering Department, Colorado Center for Advanced Ceramics, Colorado School of Mines, 1500 Illinois St., Golden, CO 80401 (United States); Braley, J.C. [Nuclear Science and Engineering Program, Chemistry and Geochemistry Department, Colorado School of Mines, 1500 Illinois St., Golden, CO 80401 (United States)

    2015-03-15

    Highlights: • YSZ TRISO kernels formed in three alternative, non-hazardous forming fluids. • Kernels characterized for size, shape, pore/grain size, density, and composition. • Bromotetradecane is suitable for further investigation with uranium-based precursor. - Abstract: Current methods of TRISO fuel kernel production in the United States use a sol–gel process with trichloroethylene (TCE) as the forming fluid. After contact with radioactive materials, the spent TCE becomes a mixed hazardous waste, and high costs are associated with its recycling or disposal. Reducing or eliminating this mixed waste stream would not only benefit the environment, but would also enhance the economics of kernel production. Previous research yielded three candidates for testing as alternatives to TCE: 1-bromotetradecane, 1-chlorooctadecane, and 1-iodododecane. This study considers the production of yttria-stabilized zirconia (YSZ) kernels in silicone oil and the three chosen alternative formation fluids, with subsequent characterization of the produced kernels and used forming fluid. Kernels formed in silicone oil and bromotetradecane were comparable to those produced by previous kernel production efforts, while those produced in chlorooctadecane and iodododecane experienced gelation issues leading to poor kernel formation and geometry.

  20. Perovskite Oxide Thin Film Growth, Characterization, and Stability

    Science.gov (United States)

    Izumi, Andrew

    Studies into a class of materials known as complex oxides have evoked a great deal of interest due to their unique magnetic, ferroelectric, and superconducting properties. In particular, materials with the ABO3 perovskite structure have highly tunable properties because of the high stability of the structure, which allows for large scale doping and strain. This also allows for a large selection of A and B cations and valences, which can further modify the material's electronic structure. Additionally, deposition of these materials as thin films and superlattices through techniques such as pulsed laser deposition (PLD) results in novel properties due to the reduced dimensionality of the material. The novel properties of perovskite oxide heterostructures can be traced to a several sources, including chemical intermixing, strain and defect formation, and electronic reconstruction. The correlations between microstructure and physical properties must be investigated by examining the physical and electronic structure of perovskites in order to understand this class of materials. Some perovskites can undergo phase changes due to temperature, electrical fields, and magnetic fields. In this work we investigated Nd0.5Sr 0.5MnO3 (NSMO), which undergoes a first order magnetic and electronic transition at T=158K in bulk form. Above this temperature NSMO is a ferromagnetic metal, but transitions into an antiferromagnetic insulator as the temperature is decreased. This rapid transition has interesting potential in memory devices. However, when NSMO is deposited on (001)-oriented SrTiO 3 (STO) or (001)-oriented (LaAlO3)0.3-(Sr 2AlTaO6)0.7 (LSAT) substrates, this transition is lost. It has been reported in the literature that depositing NSMO on (110)-oriented STO allows for the transition to reemerge due to the partial epitaxial growth, where the NSMO film is strained along the [001] surface axis and partially relaxed along the [11¯0] surface axis. This allows the NSMO film enough

  1. Effect of hydrothermal treatment on light transmission of translucent zirconias.

    Science.gov (United States)

    Putra, Armand; Chung, Kwok-Hung; Flinn, Brian D; Kuykendall, Tuesday; Zheng, Cheng; Harada, Kosuke; Raigrodski, Ariel J

    2017-09-01

    Studies of the light transmission of translucent zirconias after hydrothermal treatment are limited. The purpose of this in vitro study was to evaluate the effect of hydrothermal treatment on the light transmission of translucent zirconias for monolithic restorations. Four commercially available zirconia products, BruxZir Anterior Solid Zirconia (BruxAnt, BA), Lava Plus High Translucency (LPHT), Katana Zirconia Super Translucent (KST), and Katana Zirconia Ultra Translucent (KUT) were assessed and 1 type of lithium disilicate, e.max Press LT (LDLT) was used as a control. Plate specimens, 20×20×1 mm (n=80) for the translucency assessment were sectioned from postsintered zirconia bulk materials and ground with a #400-grit diamond wheel and coolant. The specimens were placed under hydrothermal conditions of 134°C at 0.2 MPa (n=5 per group at 0, 5, 50, and 100 hours). Percentage of total transmittance of light (T t %) of each specimen was measured using a spectrophotometer with an integrating sphere. X-ray diffraction analyses were used to measure tetragonal-monoclinic phase transformation. Surfaces were examined by scanning electron microscopy and energy dispersive spectrometry. Data were analyzed using 2-way ANOVA followed by the Tukey test (α=.05). The T t % ranged from 6.5% to 28.3%. Group LDLT obtained significantly higher transmittance than other tested groups, whereas groups KST and KUT had significantly higher T t % than groups BA and LPHT (Phydrothermal treatment for all tested translucent zirconias and a lithium disilicate glass-ceramic control. Hydrothermal treatment had minimal effects on the translucency of translucent zirconias. The tetragonal-monoclinic phase transformation rate of translucent zirconias was found to be low, except in group LPHT. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  2. Sol–gel zirconia nanopowders with α-cyclodextrin as organic additive

    International Nuclear Information System (INIS)

    Răileanu, M.; Todan, L.; Crişan, D.; Drăgan, N.; Crişan, M.; Stan, C.; Andronescu, C.; Voicescu, M.; Vasile, B.S.; Ianculescu, A.

    2012-01-01

    Highlights: ► The sol–gel synthesis of a zirconia powder has been performed, in the presence of α-cyclodextrin as organic additive. ► A crystalline powder consisting from a mixture of monoclinic and tetragonal zirconia phases has resulted after the thermal treatment. ► The organic additive acted the role of metal oxides used as doppants for zirconia powders, avoiding phase transformations. ► The α-cyclodextrin made particles to assume spherical shape and reach fairly uniform size and prevented their agglomeration. ► The organic additive led to a certain porous morphology of the zirconia particles that is pores embedded within grains. - Abstract: Nanomaterials present unique structural and physicochemical properties due to their ultra fine size of particles that make them very useful in many domains. The most spectacular applications of nanosized zirconia include ceramics, piezoelectrics, refractories, pigments, solid electrolytes, oxygen sensors, catalysts, ultrafiltration membranes, and chromatography packing materials. Nanostructured zirconia powders can be prepared using various methods, such as sol–gel process, coprecipitation, hydrothermal synthesis, and reverse micelle method. The aim of the present work was to prepare zirconia nanopowders through the sol–gel method, using α-cyclodextrin as organic additive and to establish its influence on the structural and textural properties of the obtained product. A white, amorphous ZrO 2 powder containing α-cyclodextrin was prepared, which became a crystalline, stable one, after removing the organic matter by thermal treatment. The resulted nanocrystalline powder contains both monoclinic and tetragonal zirconia phases and is very stable. It presents a relatively reduced tendency of agglomeration of particles and contains closed pores which are embedded in the zirconia matrix. The zirconia powders were characterized using the following methods: thermal analysis, IR spectroscopy, UV–vis spectroscopy

  3. Study of the creep of lime-stabilised zirconia

    International Nuclear Information System (INIS)

    Saint-Jacques, Robert G.

    1971-09-01

    This research thesis reports the study of creep of stabilised zirconia containing between 13 and 20 per cent of lime, at temperatures between 1.200 and 1.400 C, and under compression stresses between 500 and 4.000 pounds by square inch. Specimens are polycrystalline with an average grain diameter between 7 and 29 microns. The author notably shows that the creep rate of lime-stabilised zirconia is directly proportional to the applied stress, and that the creep apparent activation energy is close to activation energy of volume self-diffusion of calcium and zirconium in lime-stabilised zirconia. Results of creep tests show that, in the studied conditions, the creep rate is directly proportional to the inverse of the grain average diameter, and this is in compliance with the Gifkins and Snowden theory of creep by sliding at grain boundaries. The author also shows that the creep rate of the lime stabilised zirconia varies with lime content, and reaches a maximum when zirconia contains about 15 per cent of lime. Lower creep rates obtained for higher and lower lime contents are explained [fr

  4. Effects of oxidation potential and retention time on electrochromic stability of poly (3-hexyl thiophene) films

    Science.gov (United States)

    Kim, Tae-Ho; Hyun Song, Seok; Kim, Hyo-Jae; Oh, Seong-Hyeon; Han, Song-Yi; Kim, Goung; Nah, Yoon-Chae

    2018-06-01

    Herein, we report the effects of applied voltage on the electrochromic (EC) stability of poly(3-hexylthiophene) (P3HT) films during EC reactions. The transmittance difference and cycling stability of these films were monitored to optimize the oxidation voltage, and their chemical compositions were analyzed by X-ray photoelectron spectroscopy after long-term electrochemical cycling. High oxidation voltages increased the color contrast of P3HT films but decreased their cycling stability due to facilitating chemical degradation. Furthermore, at an optimized oxidation voltage, the retention time during potential pulsing was adjusted utilizing the optical memory of P3HT, revealing that the decreased voltage application time reduced power consumption by 9.6% and enhanced EC stability without loss of color contrast.

  5. Characteristics of porous zirconia coated with hydroxyapatite

    Indian Academy of Sciences (India)

    However, porous hydroxyapatite bodies are mechanically weak and brittle, which makes shaping and implantation difficult. One way to solve this problem is to introduce a strong porous network onto which hydroxyapatite coating is applied. In this study, porous zirconia and alumina-added zirconia ceramics were prepared ...

  6. Foam-film-stabilized liquid bridge networks in evaporative lithography and wet granular matter

    KAUST Repository

    Vakarelski, Ivan Uriev

    2013-04-23

    Evaporative lithography using latex particle templates is a novel approach for the self-assembly of suspension-dispersed nanoparticles into ordered microwire networks. The phenomenon that drives the self-assembly process is the propagation of a network of interconnected liquid bridges between the template particles and the underlying substrate. With the aid of video microscopy, we demonstrate that these liquid bridges are in fact the border zone between the underlying substrate and foam films vertical to the substrate, which are formed during the evaporation of the liquid from the suspension. The stability of the foam films and thus the liquid bridge network stability are due to the presence of a small amount of surfactant in the evaporating solution. We show that the same type of foam-film-stabilized liquid bridge network can also propagate in 3D clusters of spherical particles, which has important implications for the understanding of wet granular matter. © 2013 American Chemical Society.

  7. Hot corrosion behavior of plasma-sprayed partially stabilized zirconia coatings in a lithium molten salt

    International Nuclear Information System (INIS)

    Cho, Soo Haeng; Hong, Sun Seok; Kang, Dae Seong; Park, Byung Heong; Hur, Jin Mok; Lee, Han Soo

    2008-01-01

    The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is too corrosive for typical structural materials. It is essential to choose the optimum material for the process equipment handling molten salt. IN713LC is one of the candidate materials proposed for application in electrolytic reduction process. In this study, Yttria-Stabilized Zirconia (YSZ) top coat was applied to a surface of IN713LC with an aluminized metallic bond coat by an optimized plasma spray process, and were investigated the corrosion behavior at 675 .deg. C for 216 hours in the molten salt LiCl-Li 2 O under an oxidizing atmosphere. The as-coated and tested specimens were examined by OM, SEM/EDS and XRD, respectively. The bare superalloy reveals obvious weight loss, and the corrosion layer formed on the surface of the bare superalloy was spalled due to the rapid scale growth and thermal stress. The top coatings showed a much better hot-corrosion resistance in the presence of LiCl-Li 2 O molten salt when compared to those of the uncoated superalloy and the aluminized bond coatings. These coatings have been found to be beneficial for increasing to the hot-corrosion resistance of the structural materials for handling high temperature lithium molten salts

  8. The Influence of Heat Treatments on the Porosity of Suspension Plasma-Sprayed Yttria-Stabilized Zirconia Coatings

    Science.gov (United States)

    Ekberg, Johanna; Ganvir, Ashish; Klement, Uta; Creci, Simone; Nordstierna, Lars

    2018-02-01

    Suspension plasma-sprayed coatings are produced using fine-grained feedstock. This allows to control the porosity and to achieve low thermal conductivity which makes the coatings attractive as topcoats in thermal barrier coatings (TBCs). Used in gas turbine applications, TBCs are exposed to high temperature exhaust gases which lead to microstructure alterations. In order to obtain coatings with optimized thermomechanical properties, microstructure alterations like closing of pores and opening of cracks have to be taken into account. Hence, in this study, TBC topcoats consisting of 4 mol.% yttria-stabilized zirconia were heat-treated in air at 1150 °C and thereafter the coating porosity was investigated using image analysis (IA) and nuclear magnetic resonance (NMR) cryoporometry. Both IA and NMR cryoporometry showed that the porosity changed as a result of the heat treatment for all investigated coatings. In fact, both techniques showed that the fine porosity decreased as a result of the heat treatment, while IA also showed an increase in the coarse porosity. When studying the coatings using scanning electron microscopy, it was noticed that finer pores and cracks disappeared and larger pores grew slightly and achieved a more distinct shape as the material seemed to become more compact.

  9. On the interfacial fracture of porcelain/zirconia and graded zirconia dental structures.

    Science.gov (United States)

    Chai, Herzl; Lee, James J-W; Mieleszko, Adam J; Chu, Stephen J; Zhang, Yu

    2014-08-01

    Porcelain fused to zirconia (PFZ) restorations are widely used in prosthetic dentistry. However, their susceptibility to fracture remains a practical problem. The failure of PFZ prostheses often involves crack initiation and growth in the porcelain, which may be followed by fracture along the porcelain/zirconia (P/Z) interface. In this work, we characterized the process of fracture in two PFZ systems, as well as a newly developed graded glass-zirconia structure with emphases placed on resistance to interfacial cracking. Thin porcelain layers were fused onto Y-TZP plates with or without the presence of a glass binder. The specimens were loaded in a four-point-bending fixture with the thin porcelain veneer in tension, simulating the lower portion of the connectors and marginal areas of a fixed dental prosthesis (FDP) during occlusal loading. The evolution of damage was observed by a video camera. The fracture was characterized by unstable growth of cracks perpendicular to the P/Z interface (channel cracks) in the porcelain layer, which was followed by stable cracking along the P/Z interface. The interfacial fracture energy GC was determined by a finite-element analysis taking into account stress-shielding effects due to the presence of adjacent channel cracks. The resulting GC was considerably less than commonly reported values for similar systems. Fracture in the graded Y-TZP samples occurred via a single channel crack at a much greater stress than for PFZ. No delamination between the residual glass layer and graded zirconia occurred in any of the tests. Combined with its enhanced resistance to edge chipping and good esthetic quality, graded Y-TZP emerges as a viable material concept for dental restorations. Copyright © 2014 Acta Materialia Inc. All rights reserved.

  10. Zirconia based inert matrix fuel: fabrication concepts and feasibility studies

    International Nuclear Information System (INIS)

    Ingold, F.; Burghartz, M.; Ledergerber, G.

    1999-01-01

    The internal gelation process has traditionally been applied to fabricate standard fuel based on uranium, typically UO2 and MOX. To meet the recent aim to destroy plutonium in the most effective way, a uranium free fuel was evaluated. The fuel development programme at PSI has been redirected toward a fuel based on zirconium oxide or a mixture of zirconia and a conducting material to form ceramic/metal (CERMET) or ceramic/ceramic (CERCER) combinations. A feasibility study was carried out to demonstrate that microspheres based on zirconia and spinel can be fabricated with the required properties. The gelation parameters were investigated to optimise compositions of the starting solutions. Studies to fabricate a composite material (from zirconia and spinel) are ongoing. If the zirconia/spinel ratio is chosen appropriately, the low thermal conductivity of pure zirconia can be compensated by the higher thermal conductivity of spinel. Another solution to offset the low thermal conductivity of zirconia is the development of a CERMET, which consists of fine particles bearing plutonium in a cubic zirconia lattice dispersed in a metallic matrix. The fabrication of such a CERMET is also being studied. (author)

  11. SEM evaluation of human gingival fibroblasts growth onto CAD/CAM zirconia and veneering ceramic for zirconia

    Science.gov (United States)

    Zizzari, Vincenzo; Borelli, Bruna; De Colli, Marianna; Tumedei, Margherita; Di Iorio, Donato; Zara, Susi; Sorrentino, Roberto; Cataldi, Amelia; Gherlone, Enrico Felice; Zarone, Fernando; Tetè, Stefano

    2013-01-01

    Summary Aim To evaluate the growth of Human Gingival Fibroblasts (HGFs) cultured onto sample discs of CAD/CAM zirconia and veneering ceramic for zirconia by means of Scanning Electron Microscope (SEM) analysis at different experimental times. Methods A total of 26 experimental discs, divided into 2 groups, were used: Group A) CAD/CAM zirconia (3Y-TZP) discs (n=13); Group B) veneering ceramic for zirconia discs (n=13). HGFs were obtained from human gingival biopsies, isolated and placed in culture plates. Subsequently, cells were seeded on experimental discs at 7,5×103/cm2 concentration and cultured for a total of 7 days. Discs were processed for SEM observation at 3h, 24h, 72h and 7 days. Results In Group A, after 3h, HGFs were adherent to the surface and showed a flattened profile. The disc surface covered by HGFs resulted to be wider in Group A than in Group B samples. At SEM observation, after 24h and 72h, differences in cell attachment were slightly noticeable between the groups, with an evident flattening of HGFs on both surfaces. All differences between Group A and group B became less significant after 7 days of culture in vitro. Conclusions SEM analysis of HGFs showed differences in terms of cell adhesion and proliferation, especially in the early hours of culture. Results showed a better adhesion and cell growth in Group A than in Group B, especially up to 72h in vitro. Differences decreased after 7 days, probably because of the rougher surface of CAD/CAM zirconia, promoting better cell adhesion, compared to the smoother surface of veneering ceramic. PMID:24611089

  12. Reaction of yttria-stabilized zirconia with zirconium, silicon and Zircaloy-4 at high temperature: a compatibility study for cermet fuels

    International Nuclear Information System (INIS)

    Arima, T.; Tateyama, T.; Idemitsu, K.; Inagaki, Y.

    2003-01-01

    Compatibility studies for cermet (ceramic and metal) fuels have been completed for a temperature range of 1073-1423 K. A reaction between yttria-stabilized zirconia (YSZ), as a simulated fuel, and Zr, as a candidate for a metallic matrix, has been observed at temperatures ≥1273 K, which means the formation of a metallic reaction layer at the interface between YSZ and Zr and the occurrence of metallic phases inside the YSZ. Similar results were observed for the YSZ-Zry4 (cladding) system. On the other hand, the degree of reaction was relatively large for the YSZ-Si (metallic matrix) system, and Si diffused into the YSZ. However, the maximum fuel center-line temperature can be predicted to be less than ∼1273 K for cermet fuels. Therefore, compatibility between the ceramic fuel and the metallic matrix should be good under normal reactor operational conditions. Furthermore, since the temperature of the fuel-cladding gap is lower, the cermet fuel and the cladding material are compatible

  13. Structure, stability and electrochromic properties of polyaniline film covalently bonded to indium tin oxide substrate

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Wenzhi, E-mail: zhangwz@xatu.edu.cn [Key Laboratory for Photoelectric Functional Materials and Devices of Shaanxi Province, School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710021 (China); Ju, Wenxing; Wu, Xinming; Wang, Yan; Wang, Qiguan; Zhou, Hongwei; Wang, Sumin [Key Laboratory for Photoelectric Functional Materials and Devices of Shaanxi Province, School of Materials and Chemical Engineering, Xi’an Technological University, Xi’an 710021 (China); Hu, Chenglong [Key Laboratory of Optoelectronic Chemical Materials and Devices of Ministry of Education, School of Chemistry and Environmental Engineering, Jianghan University, Wuhan 430056 (China)

    2016-03-30

    Graphical abstract: A chemical bonding approach was proposed to prepare the PANI film covalently bonded to ITO substrate and the film exhibited high electrochemical activities and stability compared with that obtained by conventional film-forming approach. - Highlights: • The PANI film covalently bonded to ITO substrate was prepared using ABPA as modifier. • The oxidative potentials of the obtained PANI film were decreased. • The obtained PANI film exhibits high electrochemical activities and stability. - Abstract: Indium tin oxide (ITO) substrate was modified with 4-aminobenzylphosphonic acid (ABPA), and then the polyaniline (PANI) film covalently bonded to ITO substrate was prepared by the chemical oxidation polymerization. X-ray photoelectron spectroscopy (XPS), attenuated total reflection infrared (ATR-IR) spectroscopy, and atomic force microscopy (AFM) measurements demonstrated that chemical binding was formed between PANI and ABPA-modified ITO surface, and the maximum thickness of PANI layer is about 30 nm. The adhesive strength of PANI film on ITO substrate was tested by sonication. It was found that the film formed on the modified ITO exhibited a much better stability than that on bare one. Cyclic voltammetry (CV) and UV–vis spectroscopy measurements indicated that the oxidative potentials of PANI film on ABPA-modified ITO substrate were decreased and the film exhibited high electrochemical activities. Moreover, the optical contrast increased from 0.58 for PANI film (without ultrasound) to 1.06 for PANI film (after ultrasound for 60 min), which had an over 83% enhancement. The coloration time was 20.8 s, while the bleaching time was 19.5 s. The increase of electrochromic switching time was due to the lower ion diffusion coefficient of the large cation of (C{sub 4}H{sub 9}){sub 4}N{sup +} under the positive and negative potentials as comparison with the small Li{sup +} ion.

  14. Effects of stabilizer ratio on photoluminescence properties of sol-gel ZnO nano-structured thin films

    International Nuclear Information System (INIS)

    Boudjouan, F.; Chelouche, A.; Touam, T.; Djouadi, D.; Khodja, S.; Tazerout, M.; Ouerdane, Y.; Hadjoub, Z.

    2015-01-01

    Nanostructured ZnO thin films with different molar ratios of MEA to zinc acetate (0.5, 1.0, 1.5 and 2.0) have been deposited on glass substrates by a sol–gel dip coating technique. X-ray diffraction, Scanning Electron Microscopy, UV–visible spectrophotometry and photoluminescence spectroscopy have been employed to investigate the effect of MEA stabilizer ratio on structural, morphological, absorbance and emission properties of the ZnO thin films. Diffraction patterns have shown that all the films are polycrystalline and exhibit a wurtzite hexagonal structure. The c axis orientation has been enhanced with increasing stabilizer ratio. SEM micrographs have revealed that the morphology of the ZnO films depend on stabilizer ratio. The UV–visible absorption spectra have demonstrated that the optical absorption is affected by stabilizer ratio. The photoluminescence spectra have indicated one ultraviolet and two visible emission bands (green and red), while band intensities are found to be dependent on stabilizer ratio. ZnO thin films deposited at MEA ratio of 1.0 show the highest UV emission while the minimum UV emission intensity is observed in thin films deposited at ratio of 0.5 and the maximum green has been recorded for films deposited at MEA ratio of 2.0. - Highlight: • c axis orientation increases with increasing MEA ratio. • The increase of MEA ration from 0.5 to 1.0 enhances greatly the UV emission. • The larger I UV /I visible is obtained for the MEA to Zn ratio of 1:1. • The MEA ratio of 0.5 favors the formation of large density of V zn . • The MEA ratio of 2.0 increases the V o density

  15. Anelasticity and strength in zirconia ceramics

    International Nuclear Information System (INIS)

    Matsuzawa, M.; Horibe, S.; Sakai, J.

    2005-01-01

    Non-elastic strain behavior was investigated for several different zirconia ceramics and a possible mechanism for anelasticity was discussed. Anelastic strain was detected in zirconia ceramics irrespective of the crystallographic phase and its productivity depended on the particular kind of dopant additive. It was found that the anelastic properties could be significantly influenced by the level of oxygen vacancy in the matrix, and that the anelastic strain might be produced by a light shift of ionic species. In order to investigate the effect of anelasticity on mechanical properties on zirconia ceramics, the tensile strength was investigated for a wide range of strain rates. The obviously unique strain rate dependence was observed only in the materials having anelastic properties. It was assumed that anelasticity could be efficient at improving the tensile strength. (orig.)

  16. The flow and hydrodynamic stability of a liquid film on a rotating disc

    International Nuclear Information System (INIS)

    Kim, Tae-Sung; Kim, Moon-Uhn

    2009-01-01

    The flow of a liquid film on a rotating disc is investigated in the case where a liquid is supplied at a constant flow rate. We propose thin film equations by the integral method with a simple approach to satisfy the boundary conditions on a disc and a free surface, and the results are compared with those of the Navier-Stokes equations. The radial film velocity is assumed to be a quartic profile in our analysis, whereas it was assumed to be a quadratic one, neglecting the inertia force so that the boundary conditions were not completely satisfied, in the analysis of Sisoev et al (2003 J. Fluid Mech. 229 531-54). The basic flow and its stability are analyzed using the thin film equations even in the region where the inertia force is not negligible. A local stability analysis of the flow is conducted using the linearized disturbance equations and correctly predicts Needham's simple instability criterion. The present thin film equations give a good approximation of the Navier-Stokes equations.

  17. Effects of H-implantation energy on the optical stability of implanted usher films under photo-irradiation

    International Nuclear Information System (INIS)

    Awazu, K.; Yasui, H.; Kasamori, M.; Ichikawa, T.; Funada, Y.; Iwaki, M.

    1999-01-01

    A study has been made on the improvement of the optical stability of urushi films under optical irradiation using ion implantation. Ion implantation of hydrogen ions in urushi films was performed with a dose of 10 15 ions/cm 2 at ion energies ranging from 0.2 to 150 keV at room temperature. The photo-irradiation onto the urushi films was carried out at irradiation energies ranging from 40 to 400 MJ/m 2 . H-implantation onto urushi films is useful for improving the optical stability under photo-irradiation when the implantation energy is larger than 60 keV

  18. Metastable Electrical Characteristics of Polycrystalline Thin-Film Photovoltaic Modules upon Exposure and Stabilization: Preprint

    Energy Technology Data Exchange (ETDEWEB)

    Deline, C. A.; del Cueto, J. A.; Albin, D. S.; Rummel, S. R.

    2011-09-01

    The significant features of a series of stabilization experiments conducted at the National Renewable Energy Laboratory (NREL) between May 2009 and the present are reported. These experiments evaluated a procedure to stabilize the measured performance of thin-film polycrystalline cadmium telluride (CdTe) and copper indium gallium diselenide (CIGS) thin-film photovoltaic (PV) modules. The current-voltage (I-V) characteristics of CdTe and CIGS thin-film PV devices and modules exhibit transitory changes in electrical performance after thermal exposure in the dark and/or bias and light exposures. We present the results of our case studies of module performance versus exposure: light-soaked at 65 degrees C; exposed in the dark under forward bias at 65 degrees C; and, finally, longer-term outdoor exposure. We find that stabilization can be achieved to varying degrees using either light-soaking or dark bias methods and that the existing IEC 61646 light-soaking interval may be appropriate for CdTe and CIGS modules with one caveat: it is likely that at least three exposure intervals are required for stabilization.

  19. Development of mesoporosity in scandia-stabilized zirconia: particle size, solvent, and calcination effects.

    Science.gov (United States)

    Cahill, James T; Ruppert, Jesse N; Wallis, Bryce; Liu, Yanming; Graeve, Olivia A

    2014-05-20

    We present the mechanisms of formation of mesoporous scandia-stabilized zirconia using a surfactant-assisted process and the effects of solvent and thermal treatments on the resulting particle size of the powders. We determined that cleaning the powders with water resulted in better formation of a mesoporous structure because higher amounts of surfactant were preserved on the powders after washing. Nonetheless, this resulted in agglomerate sizes that were larger. The water-washed powders had particle sizes of >5 μm in the as-synthesized state. Calcination at 450 and 600 °C reduced the particle size to ∼1-2 and 0.5 μm, respectively. Cleaning with ethanol resulted in a mesoporous morphology that was less well-defined compared to the water-washed powders, but the agglomerate size was smaller and had an average size of ∼250 nm that did not vary with calcination temperature. Our analysis showed that surfactant-assisted formation of mesoporous structures can be a compromise between achieving a stable mesoporous architecture and material purity. We contend that removal of the surfactant in many mesoporous materials presented in the literature is not completely achieved, and the presence of these organics has to be considered during subsequent processing of the powders and/or for their use in industrial applications. The issue of material purity in mesoporous materials is one that has not been fully explored. In addition, knowledge of the particle (agglomerate) size is essential for powder handling during a variety of manufacturing techniques. Thus, the use of dynamic light scattering or any other technique that can elucidate particle size is essential if a full characterization of the powders is needed for achieving postprocessing effectiveness.

  20. Bonding effectiveness to different chemically pre-treated dental zirconia.

    Science.gov (United States)

    Inokoshi, Masanao; Poitevin, André; De Munck, Jan; Minakuchi, Shunsuke; Van Meerbeek, Bart

    2014-09-01

    The objective of this study was to evaluate the effect of different chemical pre-treatments on the bond durability to dental zirconia. Fully sintered IPS e.max ZirCAD (Ivoclar Vivadent) blocks were subjected to tribochemical silica sandblasting (CoJet, 3M ESPE). The zirconia samples were additionally pre-treated using one of four zirconia primers/adhesives (Clearfil Ceramic Primer, Kuraray Noritake; Monobond Plus, Ivoclar Vivadent; Scotchbond Universal, 3M ESPE; Z-PRIME Plus, Bisco). Finally, two identically pre-treated zirconia blocks were bonded together using composite cement (RelyX Ultimate, 3M ESPE). The specimens were trimmed at the interface to a cylindrical hourglass and stored in distilled water (7 days, 37 °C), after which they were randomly tested as is or subjected to mechanical ageing involving cyclic tensile stress (10 N, 10 Hz, 10,000 cycles). Subsequently, the micro-tensile bond strength was determined, and SEM fractographic analysis performed. Weibull analysis revealed the highest Weibull scale and shape parameters for the 'Clearfil Ceramic Primer/mechanical ageing' combination. Chemical pre-treatment of CoJet (3M ESPE) sandblasted zirconia using Clearfil Ceramic Primer (Kuraray Noritake) and Monobond Plus (Ivoclar Vivadent) revealed a significantly higher bond strength than when Scotchbond Universal (3M ESPE) and Z-PRIME Plus (Bisco) were used. After ageing, Clearfil Ceramic Primer (Kuraray Noritake) revealed the most stable bond durability. Combined mechanical/chemical pre-treatment, the latter with either Clearfil Ceramic Primer (Kuraray Noritake) or Monobond Plus (Ivoclar Vivadent), resulted in the most durable bond to zirconia. As a standard procedure to durably bond zirconia to tooth tissue, the application of a combined 10-methacryloyloxydecyl dihydrogen phosphate/silane ceramic primer to zirconia is clinically highly recommended.

  1. Comparative evaluation of shear bond strength of zirconia restorations cleansed various cleansing protocols bonded with two different resin cements: An In vitro study

    Directory of Open Access Journals (Sweden)

    Sriram Sankar

    2017-01-01

    Full Text Available Context: Yttria partially stabilized tetragonal zirconia polycrystalline restorations have gained widespread use because of its enhanced strength and esthetics. During the try-in process, zirconia is likely to be contaminated with saliva. This contamination leads to a clear weakening of the bond between restorative material and cement. For this reason, zirconia surface should be cleaned before cementation. Hence, the purpose of this study is to compare the shear bond strength of zirconia restorations cleansed with various surface cleansing protocols bonded with two different resin cements. Materials and Methods: Eighty samples of zirconia discs were prepared in the dimensions 2.5 mm diameter and 4.5 mm thickness. They were divided into two groups of each forty samples based on luting cement used. Each group was further subdivided into four subgroups of each (n = 10: Group 1: uncontaminated zirconia blocks, Group 2: saliva-contaminated zirconia blocks and cleaned only with distilled water, Group 3: saliva-contaminated zirconia blocks treated with Ivoclean, and Group 4: saliva-contaminated zirconia blocks were air abraded. Eighty human maxillary premolars were then sectioned to expose dentin and were mounted on an acrylic block. A jig was fabricated to bond zirconia with the tooth using two self-adhesive resin cements. The samples were subjected to shear bond strength testing. The data were analyzed using one-way analysis of variance and Tukey's honest significance difference test with a level of significance set at p < 0.05. Results: The mean shear bond strength values of Group 1 and 2 - subgroup B are 10.3 ± 0.4 and 9.80 ± 0.7 (saliva-contaminated zirconia, cleansed with distilled water only, respectively, were lowest among all test subgroups and were significantly less than mean values of subgroup C, Group 1 - 20.45 ± 0.6 and Group 2 - 20.75 ± 0.4 (Ivoclean group and subgroup D, Group 1 - 20.90 ± 0.3 and Group 2 - 20.60 ± 0.5 (air

  2. Application of sol gel spin coated yttria-stabilized zirconia layers for the improvement of solid oxide fuel cell electrolytes produced by atmospheric plasma spraying

    Energy Technology Data Exchange (ETDEWEB)

    Rose, Lars [University of British Columbia, Department of Materials Engineering, 309-6350 Stores Road, Vancouver, British Columbia, V6T 1Z4 (Canada); National Research Council, Institute for Fuel Cell Innovation, 4250 Wesbrook Mall, Vancouver, British Columbia, V6T 1W5 (Canada); Kesler, Olivera [National Research Council, Institute for Fuel Cell Innovation, 4250 Wesbrook Mall, Vancouver, British Columbia, V6T 1W5 (Canada); University of British Columbia, Department of Mechanical Engineering, 2054-6250 Applied Science Lane, Vancouver, British Columbia, V6T 1Z4 (Canada); Tang, Zhaolin; Burgess, Alan [Northwest Mettech Corp., 467 Mountain Hwy, North Vancouver, British Columbia, V7J 2L3 (Canada)

    2007-05-15

    Due to its high thermal stability and purely oxide ionic conductivity, yttria-stabilized zirconia (YSZ) is the most commonly used electrolyte material for solid oxide fuel cells (SOFCs). Standard electrolyte fabrication techniques for planar SOFCs involve wet ceramic techniques such as tape-casting or screen printing, requiring sintering steps at temperatures above 1300 C. Plasma spraying (PS) may provide a more rapid and cost efficient method to produce SOFCs without sintering. High-temperature sintering requires long processing times and can lead to oxidation of metal alloys used as mechanical supports, or to detrimental interreactions between the electrolyte and adjacent electrode layers. This study investigates the use of spin coated sol gel derived YSZ precursor solutions to fill the pores present in plasma sprayed YSZ layers, and to enhance the surface area for reaction at the electrolyte-cathode interface, without the use of high-temperature firing steps. The effects of different plasma conditions and sol concentrations and solid loadings on the gas permeability and fuel cell performance have been investigated. (author)

  3. Properties, ageing behavior and stability of bipolar films containing nano-layers of allylamine and acrylic acid plasma polymers

    Science.gov (United States)

    Aziz, Gaelle; Asadian, Mahtab; Declercq, Heidi; Morent, Rino; De Geyter, Nathalie

    2018-06-01

    In this work, a dielectric barrier discharge (DBD) has been used for the deposition of bipolar films containing alternating nano-layers of plasma polymerized allylamine (PPAam) and acrylic acid (PPAac). Various films were obtained by varying the single-layer thickness of each plasma polymer while maintaining a constant total film thickness and two kinds of films were fabricated via different depositing sequences (PPAam/Aac and PPAac/Aam). Films properties, ageing in air and stability in water over a 7 days period were investigated. Results showed that, COO- and NH3+ polar entities, generated from the interaction of PPAam and PPAac, are present in the bipolar films. Concerning the films stability, the different reaction mechanisms involved in the formation of each kind of films resulted in a higher amount of polar groups in the PPAam/Aac films; this conferred these films a higher stability than PPAac/Aam. Concerning the films ageing behavior, all prepared samples underwent some kind of ageing which was found to be dependent on the deposition sequence. Results also showed that bipolar coatings exhibited better cell-material interactions compared to PPAam and PPAac films; with a better cell viability observed on PPAam/Aac coatings after 1 and 7 days culture.

  4. Translucency of Zirconia Ceramics before and after Artificial Aging.

    Science.gov (United States)

    Walczak, Katarzyna; Meißner, Heike; Range, Ursula; Sakkas, Andreas; Boening, Klaus; Wieckiewicz, Mieszko; Konstantinidis, Ioannis

    2018-03-11

    The aging of zirconia ceramics (Y-TZP) is associated with tetragonal to monoclinic phase transformation. This change in microstructure may affect the optical properties of the ceramic. This study examines the effect of aging on the translucency of different zirconia materials. 120 disc-shaped specimens were fabricated from four zirconia materials: Cercon ht white, BruxZir Solid Zirconia, Zenostar T0, Lava Plus (n = 30 per group). Accelerated aging was performed in a steam autoclave (134°C, 0.2 MPa, 5 hours). CIELab coordinates (L*, a*, b*) and luminous reflectance (Y) were measured with a spectrophotometer before and after aging. Contrast ratio (CR) and translucency parameter (TP) were calculated from the L*, a*, b*, and Y tristimulus values. The general linear model (Bonferroni adjusted) was used to compare both parameters before and after aging, as well as between the different zirconia materials (p ≤ 0.05). CR and TP differed significantly before and after aging in all groups tested. Before aging, Zenostar T showed the highest and Lava Plus showed the lowest translucency. After aging, Cercon ht and Zenostar T showed the highest and BruxZir and Lava Plus the lowest translucency. Aging reduced the translucency in all specimens tested. Furthermore, translucency differed between the zirconia brands tested. Nevertheless, the differences were below the detectability threshold of the human eye. The aging process can influence the translucency and thus the esthetic outcome of zirconia restorations; however, the changes in translucency were minimal and probably undetectable by the human eye. © 2018 by the American College of Prosthodontists.

  5. Film Grain-Size Related Long-Term Stability of Inverted Perovskite Solar Cells.

    Science.gov (United States)

    Chiang, Chien-Hung; Wu, Chun-Guey

    2016-09-22

    The power conversion efficiency (PCE) of the perovskite solar cell is high enough to be commercially viable. The next important issue is the stability of the device. This article discusses the effect of the perovskite grain-size on the long-term stability of inverted perovskite solar cells. Perovskite films composed of various sizes of grains were prepared by controlling the solvent annealing time. The grain-size related stability of the inverted cells was investigated both in ambient atmosphere at relative humidity of approximately 30-40 % and in a nitrogen filled glove box (H 2 Operovskite film having the grain size larger than 1 μm (D-10) decreases less than 10 % with storage in a glove box and less than 15 % when it was stored under an ambient atmosphere for 30 days. However, the cell using the perovskite film composed of small (∼100 nm) perovskite grains (D-0) exhibits complete loss of PCE after storage under the ambient atmosphere for only 15 days and a PCE loss of up to 70 % with storage in the glove box for 30 days. These results suggest that, even under H 2 O-free conditions, the chemical- and thermal-induced production of pin holes at the grain boundaries of the perovskite film could be the reason for long-term instability of inverted perovskite solar cells. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  6. EFFECTIVE ELASTIC PROPERTIES OF ALUMINA-ZIRCONIA COMPOSITE CERAMICS - PART 4. TENSILE MODULUS OF POROUS ALUMINA AND ZIRCONIA

    Directory of Open Access Journals (Sweden)

    W. Pabst

    2004-12-01

    Full Text Available In this fourth paper of a series on the effective elastic properties of alumina-zirconia composite ceramics the influence of porosity on the effective tensile modulus of alumina and zirconia ceramics is discussed. The examples investigated are alumina and zirconia ceramics prepared from submicron powders by starch consolidation casting using two different types of starch, potato starch (median size D50 =47.2 µm and corn starch (median size D50 =13.7 µm. The dependence of effective tensile moduli E, on the porosity f, measured for porosities in the ranges of approx. 19-55 vol.% and 10-42 vol.% for alumina and zirconia, respectively, using a resonant frequency technique, was evaluated by fitting with various model relations, including newly developed ones. A detailed comparison of the fitting results suggests the superiority of the new relation E/E0 = (1 - f·(1 - f/fC, developed by the authors (with the tensile modulus of the dense ceramic material E0 and the critical porosity fC, over most other existing fit models. Only for special purposes and well-behaved data sets the recently proposed exponential relation E/E0 = exp [-Bf/(1 - f] and the well-known Phani-Niyogi relation E/E0 = (1 - f/fCN might be preferable.

  7. Incorporation of TiO2 nanotubes in a polycrystalline zirconia: Synthesis of nanotubes, surface characterization, and bond strength.

    Science.gov (United States)

    Dos Santos, Angélica Feltrin; Sandes de Lucena, Fernanda; Sanches Borges, Ana Flávia; Lisboa-Filho, Paulo Noronha; Furuse, Adilson Yoshio

    2018-04-05

    Despite numerous advantages such as high strength, the bond of yttria-stabilized zirconia polycrystal (Y-TZP) to tooth structure requires improvement. The purpose of this in vitro study was to evaluate the incorporation of TiO 2 nanotubes into zirconia surfaces and the bond strength of resin cement to the modified ceramic. TiO 2 nanotubes were produced by alkaline synthesis, mixed with isopropyl alcohol (50 wt%) and applied on presintered zirconia disks. The ceramics were sintered, and the surfaces were characterized by confocal laser microscopy, scanning electron microscopy (SEM), and energy-dispersive x-ray spectroscopy (EDS) analysis. For bond strength, the following 6 groups (n=16) were evaluated: without TiO 2 and Single Bond Universal; with TiO 2 nanotubes and Single Bond Universal; without TiO 2 nanotubes and Z-prime; with TiO 2 nanotubes and Z-prime; without TiO 2 and Signum Zirconia Bond; with TiO 2 and Signum Zirconia Bond. After sintering, resin cement cylinders, diameter of 1.40 mm and 1 mm in height, were prepared and polymerized for 20 seconds. Specimens were stored in water at 37°C for 30 days and submitted to a shear test. Data were analyzed by 2-way ANOVA and Tukey honest significant difference (α=.05) tests. EDS analysis confirmed that nanoagglomerates were composed of TiO 2 . The shear bond strength showed statistically significant differences among bonding agents (P<.001). No significant differences were found with the application of nanotubes, regardless of the group analyzed (P=.682). The interaction among the bonding agent factors and addition of nanotubes was significant (P=.025). Nanotubes can be incorporated into zirconia surfaces. However, this incorporation did not improve bond strength. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  8. Phase coexistence in thin liquid films stabilized by colloidal particles: equilibrium and non-equilibrium properties

    International Nuclear Information System (INIS)

    Blawzdziewicz, J.; Wajnryb, E.

    2005-01-01

    Phase equilibria between regions of different thickness in thin liquid films stabilized by colloidal particles are investigated using a quasi-two-dimensional thermodynamic formalism. Appropriate equilibrium conditions for the film tension, normal pressure, and chemical potential of the particles in the film are formulated, and it is shown that the relaxation of these parameters occurs consecutively on three distinct time scales. Film stratification is described quantitatively for a hard-sphere suspension using a Monte-Carlo method to evaluate thermodynamic equations of state. Coexisting phases are determined for systems in constrained- and full-equilibrium states that correspond to different stages of film relaxation. We also evaluated the effective viscosity coefficients for two-dimensional compressional and shear flows of a film and the self and collective mobility coefficients of the stabilizing particles. The hydrodynamic calculations were performed using a multiple-reflection representation of Stokes flow between two free surfaces. In this approach, the particle-laden film is equivalent to a periodic system of spheres with a unit cell that is much smaller in the transverse direction than in the lateral direction. (author)

  9. Modulation of human dermal microvascular endothelial cell and human gingival fibroblast behavior by micropatterned silica coating surfaces for zirconia dental implant applications

    International Nuclear Information System (INIS)

    Laranjeira, Marta S; Carvalho, Ângela; Ferraz, Maria Pia; Monteiro, Fernando Jorge; Pelaez-Vargas, Alejandro; Hansford, Derek; Coimbra, Susana; Costa, Elísio; Santos-Silva, Alice; Fernandes, Maria Helena

    2014-01-01

    Dental ceramic implants have shown superior esthetic behavior and the absence of induced allergic disorders when compared to titanium implants. Zirconia may become a potential candidate to be used as an alternative to titanium dental implants if surface modifications are introduced. In this work, bioactive micropatterned silica coatings were produced on zirconia substrates, using a combined methodology of sol–gel processing and soft lithography. The aim of the work was to compare the in vitro behavior of human gingival fibroblasts (HGFs) and human dermal microvascular endothelial cells (HDMECs) on three types of silica-coated zirconia surfaces: flat and micropatterned (with pillars and with parallel grooves). Our results showed that cells had a higher metabolic activity (HGF, HDMEC) and increased gene expression levels of fibroblast-specific protein-1 (FSP-1) and collagen type I (COL I) on surfaces with pillars. Nevertheless, parallel grooved surfaces were able to guide cell growth. Even capillary tube-like networks of HDMEC were oriented according to the surface geometry. Zirconia and silica with different topographies have shown to be blood compatible and silica coating reduced bacteria adhesion. All together, the results indicated that microstructured bioactive coating seems to be an efficient strategy to improve soft tissue integration on zirconia implants, protecting implants from peri-implant inflammation and improving long-term implant stabilization. This new approach of micropatterned silica coating on zirconia substrates can generate promising novel dental implants, with surfaces that provide physical cues to guide cells and enhance their behavior. (paper)

  10. Microstructure and transport current characterization of YBa2Cu3O7-x thick films prepared by modified solid-liquid melt growth and powder melt process routes

    International Nuclear Information System (INIS)

    Langhorn, J.; McGinn, P.J.

    1999-01-01

    From the characterization of superconducting YBa 2 Cu 3 O 7-x (YBCO) thick films processed by melt texturing on yttria-stabilized zirconia substrates from YBCO precursors it is clear that the properties are highly dependent on the precursor powder. Increased YBCO grain sizes have been induced in thick films processed from by modified solid-liquid melt growth (SLMG) and powder melt (PMP) processes with respect to those processed from pre-reacted YBCO materials. The SLMG and PMP routes utilize precursors consisting of BaCuO 2 -CuO flux material mixed with Y 2 O 3 and Y 2 BaCuO 5 respectively. Cross-sectional analysis of films textured by these routes shows a decreased Y 2 BaCuO 5 size and an increased homogeneity within the matrix with respect to films processed from YBCO powder. Such microstructural improvements lead to an improvement of both the flux pinning and current-carrying characteristics of the processed YBCO films. (author)

  11. Corrosion behavior of zirconia in acidulated phosphate fluoride

    Directory of Open Access Journals (Sweden)

    Anie Thomas

    2016-02-01

    Full Text Available ABSTRACT Objective The corrosion behavior of zirconia in acidulated phosphate fluoride (APF representing acidic environments and fluoride treatments was studied. Material and Methods Zirconia rods were immersed in 1.23% and 0.123% APF solutions and maintained at 37°C for determined periods of time. Surfaces of all specimens were imaged using digital microscopy and scanning electron microscopy (SEM. Sample mass and dimensions were measured for mass loss determination. Samples were characterized by powder X-ray diffraction (XRD to detect changes in crystallinity. A biosensor based on electrochemical impedance spectroscopy (EIS was used to detect ion dissolution of material into the immersion media. Results Digital microscopy revealed diminishing luster of the materials and SEM showed increased superficial corrosion of zirconia submerged in 1.23% APF. Although no structural change was found, the absorption of salts (sodium phosphate onto the surface of the materials bathed in 0.123% APF was significant. EIS indicated a greater change of impedance for the immersion solutions with increasing bathing time. Conclusion Immersion of zirconia in APF solutions showed deterioration limited to the surface, not extending to the bulk of the material. Inferences on zirconia performance in acidic oral environment can be elucidated from the study.

  12. Synthesis of nickel oxide - zirconia composites by coprecipitation route followed by hydrothermal treatment

    International Nuclear Information System (INIS)

    Yoshito, Walter Kenji; Ussui, Valter; Lazar, Dolores Ribeiro Ricci; Paschoal, Jose Octavio Armani

    2009-01-01

    Nickel oxide-yttria stabilized zirconia (NiO-YSZ) for use as solid oxide fuel cell anode were synthesized by coprecipitation to obtain amorphous zirconia and crystallized β-nickel gels of the corresponding metal hydroxides. Hydrothermal treatment at 200°C and 220 psi from 2 up to 16 hours, under stirring, was performed to produce nanocrystalline powder. The as-synthesized powders were uniaxially pressed and sintered in air. Powders were characterized by X-ray diffraction, laser scattering, scanning and transmission electron microscopy (SEM/TEM), gas adsorption technique (BET) and TGDTA thermal analysis. Ceramic samples were characterized by dilatometric analysis and density measurements by Archimedes method. The characteristics of hydrothermally synthesized powders and compacts were compared to those produced without temperature and pressure application. Crystalline powders were obtained after hydrothermal process, excluding the calcination step from this route. The specific surface area of powders decreases with increasing time of hydrothermal treatment while the agglomerate mean size is not affected by this parameter. (author)

  13. Fluency over the monoclinic zirconia indentation

    International Nuclear Information System (INIS)

    Pereira, A.S.; Jornada, J.A.H. da

    1992-01-01

    It was investigated the environment and the time dependence of the Vickers microhardness of monoclinic zirconia single-crystals. The samples were kept at room temperature and the identifications were performed for different environments (air, toluene and water). An indentation creep process was observed for the samples indented is moist media, indicating for a water activated plastic relaxation mechanism. The possible influence of such effect in the fatigue and phase transformations mechanisms of zirconia based ceramics is discussed. (author)

  14. Photocatalytic activity and stability of TiO{sub 2} and WO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Carcel, Radu Adrian; Andronic, Luminita, E-mail: andronic-luminita@unitbv.ro; Duta, Anca, E-mail: a.duta@unitbv.ro

    2012-08-15

    Photocatalysis represents a viable option for complete degrading the dye molecules resulted in the textile industry, up to products that do not represent environmental threats. The photocatalytic degradation of methyl orange has been investigated using TiO{sub 2}, WO{sub 3} and mixed thin films. The photodegradation efficiency is examined in correlation with the experimental parameters (irradiation time, H{sub 2}O{sub 2} addition and stability), along with the morphology and crystallinity data. The H{sub 2}O{sub 2} addition increases the photodegradation efficiency by providing additional hydroxyl groups and further reducing the recombination of the electron-hole pairs by reacting with the electrons at the catalyst interface. To test the stability of the photocatalytic films in long time running processes, batch series of experiments were conducted using contact periods up to 9 days. The results show that the thin films maintained their photocatalytic properties confirming their stability and viability for up-scaling. Highlights: Black-Right-Pointing-Pointer TiO{sub 2}, WO{sub 3} and mixed thin films Black-Right-Pointing-Pointer We tested the photocatalytic activity and photocatalyst stability over a period up to 9 days of continuous irradiation. Black-Right-Pointing-Pointer The influence of medium pH and oxidizing agent (H{sub 2}O{sub 2}) was analyzed.

  15. Physical stability and moisture sorption of aqueous chitosan-amylose starch films plasticized with polyols

    DEFF Research Database (Denmark)

    Cervera, Mirna Fernández; Karjalainen, Milja; Airaksinen, Sari

    2004-01-01

    The short-term stability and the water sorption of films prepared from binary mixtures of chitosan and native amylose maize starch (Hylon VII) were evaluated using free films. The aqueous polymer solutions of the free films contained 2% (w/w) film formers, glycerol, or erythritol as a plasticizer...... in the crystallinity of the films are evident within a 3-month period of storage, and the changes in the solid state are dependent on the plasticizer and storage conditions. When stored at ambient conditions for 3 months, the aqueous chitosan-amylose starch films plasticized with erythritol exhibited a partly...

  16. Lifetime estimation of zirconia ceramics by linear ageing kinetics

    International Nuclear Information System (INIS)

    Zhang, Fei; Inokoshi, Masanao; Vanmeensel, Kim; Van Meerbeek, Bart; Naert, Ignace; Vleugels, Jef

    2015-01-01

    Up to now, the ageing kinetics of zirconia ceramics were mainly derived from the sigmoidal evolution of the surface phase transformation as a function of time, as quantified by means of X-ray diffraction (XRD). However, the transformation propagation into the material should be better to monitor the ageing kinetics. In this work, μ-Raman spectroscopy was used to quantitatively measure the transformation profiles in depth as a function of ageing time at 160 °C, 140 °C, 134 °C and 110 °C. A linear relationship between the transformed depth and the ageing time was observed for all investigated yttria stabilized tetragonal zirconia polycrystals (3Y-TZP). Furthermore, the μ-Raman investigation of residual stresses in the subsurface of aged 3Y-TZPs showed that the highest tensile stress was located just ahead of the transformation front, indicating the key responsibility of stress accumulation for transformation front propagating into the material. Moreover, the linear kinetics of the transformation propagation were more accurate to calculate the apparent activation energy of the ageing process and allowed a more straightforward estimation of the lifetime of 3Y-TZP at body temperature, as compared to the conventional ageing kinetic parameters obtained from the surface transformation analysis by XRD

  17. Nano-structured yttria-stabilized zirconia coating by electrophoretic deposition

    Energy Technology Data Exchange (ETDEWEB)

    Maleki-Ghaleh, H., E-mail: H_Maleki@sut.ac.ir [Faculty of Materials Engineering, Sahand University of Technology, Tabriz (Iran, Islamic Republic of); Rekabeslami, M. [Faculty of Mechanical Engineering, Materials Science and Engineering Division, K. N. Toosi University of Technology, Tehran (Iran, Islamic Republic of); Shakeri, M.S. [Materials and Energy Research Center, Karaj (Iran, Islamic Republic of); Siadati, M.H. [Faculty of Mechanical Engineering, Materials Science and Engineering Division, K. N. Toosi University of Technology, Tehran (Iran, Islamic Republic of); Javidi, M. [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz (Iran, Islamic Republic of); Talebian, S.H. [Faculty of Petroleum Engineering, Universiti Technologi Petronas, Perak (Malaysia); Aghajani, H. [Department of Materials Engineering, University of Tabriz, Tabriz (Iran, Islamic Republic of)

    2013-09-01

    The most important role of thermal barrier coatings is to reduce the temperature of the substrate in high temperature applications. Nanoparticle zirconia might be a suitable choice for improving the efficiency of thermal barrier coatings. Nanostructured coatings have lower thermal conduction, higher thermal expansion and lower dimensional variations at higher temperatures in comparison with the microstructured coatings. Electrophoretic deposition has been preferred for thermal barrier coatings due to its simplicity, controllability and low cost. In the present study, three different suspensions of ZrO{sub 2}–8 wt%Y{sub 2}O{sub 3} (40 nm) made with ethanol, acetone and acetyl acetone were used. Electrophoretic deposition was conducted at a fixed voltage of 60 V for 120 s on aluminized Inconel 738-LC, and then heat treated at 1100{sup o}C for 4 h in air atmosphere. The coating morphology and elemental distribution were studied using scanning electron microscopy. It was observed that suspension media have an important effect on the quality of the final product. Acetyl acetone showed better dispersion of particles than the other two media. Consequently, deposition from acetyl acetone resulted in uniform and crack-free layers while those from ethanol and acetone were completely non-uniform due to agglomeration and low viscosity, respectively.

  18. Evaluation of participants' perception and taste thresholds with a zirconia palatal plate.

    Science.gov (United States)

    Wada, Takeshi; Takano, Tomofumi; Tasaka, Akinori; Ueda, Takayuki; Sakurai, Kaoru

    2016-10-01

    Zirconia and cobalt-chromium can withstand a similar degree of loading. Therefore, using a zirconia base for removable dentures could allow the thickness of the palatal area to be reduced similarly to metal base dentures. We hypothesized that zirconia palatal plate for removable dentures provides a high level of participants' perception without influencing taste thresholds. The purpose of this study was to evaluate the participants' perception and taste thresholds of zirconia palatal plate. Palatal plates fabricated using acrylic resin, zirconia, and cobalt-chromium alloy were inserted into healthy individuals. Taste thresholds were investigated using the whole-mouth gustatory test, and participants' perception was evaluated using the 100-mm visual analog scale to assess the ease of pronunciation, ease of swallowing, sensation of temperature, metallic taste, sensation of foreign body, subjective sensory about weight, adhesiveness of chewing gum, and general satisfaction. For the taste thresholds, no significant differences were noted in sweet, salty, sour, bitter, or umami tastes among participants wearing no plate, or the resin, zirconia, and metal plates. Speech was easier and foreign body sensation was lower with the zirconia plate than with the resin plate. Evaluation of the adhesiveness of chewing gum showed that chewing gum does not readily adhere to the zirconia plate in comparison with the metal plate. The comprehensive participants' perception of the zirconia plate was evaluated as being superior to the resin plate. A zirconia palatal plate provides a high level of participants' perception without influencing taste thresholds. Copyright © 2016 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

  19. The effect of partially stabilized zirconia on the biological properties of HA/HDPE composites in vitro.

    Science.gov (United States)

    Sadi, A Yari; Shokrgozar, M A; Homaeigohar, S Sh; Hosseinalipour, M; Khavandi, A; Javadpour, J

    2006-05-01

    The effect of partially stabilized zirconia (PSZ) on the biological properties of the hyroxyapatite - high density polyethylene (HA/HDPE) composites was studied by investigating the simultaneous effect of hydroxyapatite and PSZ volume fractions on the in vitro response of human osteoblast cells. The biocompatibility of composite samples with different volume fraction of HA and PSZ powders was assessed by proliferation, alkaline phosphatase (ALP) and cell attachment assays on the osteoblast cell line (G-292) in different time periods. The effect of composites on the behavior of G-292 cells was compared with those of HDPE and TPS (Tissue Culture Poly Styrene as negative control) samples. Results showed a higher proliferation rate of G-292 cells in the presence of composite samples as compared to the HDPE sample after 7 and 14 days of incubation period. ALP production rate in all composite samples was higher than HDPE and TPS samples. The number of adhered cells on the composite samples was higher than the number adhered on the HDPE and TPS samples after the above mentioned incubation periods. These findings indicates that the addition of PSZ does not have any adverse affect on the biocompatibility of HA/HDPE composites. In fact in some experiments PSZ added HA/HDPE composites performed better in proliferation, differentiation and attachment of osteoblastic cells.

  20. EXAFS study of the stability of amorphous TbFe thin films

    International Nuclear Information System (INIS)

    Samant, M.G.; Marinero, E.E.; Robinson, C.; Cargill, G.S.

    1989-01-01

    This paper discusses the measurement of the local atomic structure of Fe in Au doped Tb-Fe thin film alloys by the use of EXAFS. The as deposited sample shows structural features which are essentially identical to those of the undoped films. Au additions stabilizes the amorphous structure against recrystallization, however, the loss of magnetic anisotropy under thermal annealing is not reduced. This demonstrates that magnetic relaxation in these alloys does not involve crystallization of the amorphous structure

  1. Dehydration and crystallization kinetics of zirconia-yttria gels

    International Nuclear Information System (INIS)

    Ramanathan, S.; Muraleedharan, R.V.; Roy, S.K.; Nayar, P.K.K.

    1995-01-01

    Zirconia and zirconia-yttria gels containing 4 and 8 mol% yttria were obtained by coprecipitation and drying at 373 K. The dehydration and crystallization behavior of the dried gels was studied by DSC, TG, and XRD. The gels undergo elimination of water over a wide temperature range of 373--673 K. The peak temperature of the endotherm corresponding to dehydration and the kinetic constants for the process were not influenced by the yttria content of the gel. The enthalpy of dehydration observed was in good agreement with the heat of vaporization data. The dehydration was followed by a sharp exothermic crystallization process. The peak temperature of the exotherm and the activation energy of the process increased with an increase in yttria content, while the enthalpy of crystallization showed a decrease. The ''glow effect'' reduced with increasing yttria content. Pure zirconia crystallizes in the tetragonal form while the zirconia containing 4 and 8 mol% yttria appears to crystallize in the cubic form

  2. Peculiarities of structural transformations in zirconia nanocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Vasilevskaya, A., E-mail: a.k.vasilevskaya@gmail.com [Technical University, Saint-Petersburg State Institute of Technology (Russian Federation); Almjasheva, O. V. [Saint-Petersburg Electrotechnical University “LETI” (Russian Federation); Gusarov, V. V. [Ioffe Physical-Technical Institute of the Russian Academy of Sciences (Russian Federation)

    2016-07-15

    The transitions of metastable tetragonal phase as well as high-temperature tetragonal phase into the low-temperature monoclinic phase upon heating and cooling were thoroughly studied in zirconia nanoparticles. High-temperature X-ray diffraction, thermal analysis and Raman spectroscopy were used to provide the systematic approach to the investigation of zirconia nanoparticles thermal behavior. A phase transformation sequence in the ZrO{sub 2}–H{sub 2}O system was determined, and the mechanisms of tetragonal-to-monoclinic transition upon heating and cooling were suggested. Here, the phenomenon was found and described, which was determined as “self-powdering” of nanoparticles occurring during structural transition. This phenomenon was observed by in situ investigation of the evolution of crystalline nanoparticles from amorphous zirconium hydroxide during thermal treatment in air. The tetragonal-to-monoclinic phase transition, induced by cooling from the temperature of equilibrium of tetragonal zirconia (i.e., above 1170 °C), is accompanied by a significant crystallite size decrease (with corresponding 3–4 times decrease of crystallite volume). The experimental results facilitate applications of zirconia nanoparticles to obtain high-performance nanopowders for nanoceramics.

  3. Osseointegration of a Zirconia Implant : A Histologic Assessment

    NARCIS (Netherlands)

    Schepke, Ulf; Meijer, Gert J; Meijer, Henny Ja; Walboomers, X Frank; Cune, Marco

    2017-01-01

    PURPOSE: The aim of this study was to describe the histologic and histomorphometric features of a retrieved, functional endosseous zirconia implant in a human subject. MATERIALS AND METHODS: A maxillary zirconia implant (ZV3) placed in a 52-year-old man was retrieved after 2 years of uncompromised

  4. Fracture Strength of Aged Monolithic and Bilayer Zirconia-Based Crowns

    Directory of Open Access Journals (Sweden)

    Deborah Pacheco Lameira

    2015-01-01

    Full Text Available The purpose of this study was to evaluate the effect of design and surface finishing on fracture strength of yttria-tetragonal zirconia polycrystal (Y-TZP crowns in monolithic (1.5 mm thickness and bilayer (0.8 mm zirconia coping and 0.7 mm porcelain veneer configuration after artificial aging. Bovine incisors received crown preparation and Y-TZP crowns were manufactured using CAD/CAM technique, according to the following groups (n=10: Polished monolithic zirconia crowns (PM; Glazed monolithic zirconia crowns (GM; Bi-layer crowns (BL. Crowns were cemented with resin cement, submitted to artificial aging in a chewing simulator (2.5 million cycles/80 N/artificial saliva/37°C, and tested for fracture strength. Two remaining crowns referring to PM and GM groups were submitted to a chemical composition analysis to measure the level of yttrium after aging. One-way ANOVA and Tukey’s test (P=.05 indicated that monolithic zirconia crowns presented similar fracture strength (PM=3476.2 N ± 791.7; GM=3561.5 N ± 991.6, which was higher than bilayer crowns (2060.4 N ± 810.6. There was no difference in the yttrium content among the three surfaces evaluated in the monolithic crowns. Thus, monolithic zirconia crowns present higher fracture strength than bilayer veneered zirconia after artificial aging and surface finishing does not affect their fracture strength.

  5. Improved damp heat stability of Ga-Doped ZnO thin film by pretreatment of the polyethylene terephthalate substrate

    Science.gov (United States)

    Kim, B. B.; Seo, S. G.; Lim, Y. S.; Choi, H.-S.; Seo, W.-S.; Park, H.-H.

    2013-09-01

    A study on the damp heat stability of transparent conducting ZnO thin film grown on a polyethylene terephthalate substrate (PET) is reported. By thermal annealing of the PET substrate at 100°C with Ar flow in a vacuum chamber prior to the sputtering growth of Ga-doped ZnO (GZO) thin film, significantly enhanced damp heat stability was achieved at 60°C with a 90% relative humidity. Electrical and structural characterizations of the GZO thin films were carried out and the effects of the pretreatment on the improved damp heat stability are discussed.

  6. Stabilization of thin liquid films by repulsive van der waals force

    KAUST Repository

    Li, Erqiang; Vakarelski, Ivan Uriev; Chan, Derek Y C; Thoroddsen, Sigurdur T

    2014-01-01

    Using high-speed video recording of bubble rise experiments, we study the stability of thin liquid films trapped between a rising bubble and a surfactant-free liquid-liquid meniscus interface. Using different combinations of nonpolar oils and water

  7. Enhancement of Moisture Protective Properties and Stability of Pectin through Formation of a Composite Film: Effects of Shellac and Plasticizer.

    Science.gov (United States)

    Luangtana-Anan, Manee; Soradech, Sitthiphong; Saengsod, Suthep; Nunthanid, Jurairat; Limmatvapirat, Sontaya

    2017-12-01

    The aim of this investigation was to develop the high moisture protective ability and stable pectin through the design of composite films based on varying shellac concentrations. A film casting method was applied to prepare a free film. The moisture protective properties and mechanical properties were investigated. The findings was the composite films exhibited the reductions in the hydrophilicity, water vapor permeability, and the moisture content compared with pectin films. The single and composite films were then study for their stability at 40 °C and 75% RH for 90 d. Among the concentrations of shellac, 50% (w/w) could improve stability in terms of moisture protection after 90 d of storage, whereas lower concentrations of shellac (10% to 40%) could not achieve this. However, the higher shellac content also contributed to weaker mechanical properties. The mechanical improvement and stability of composite films with the incorporation of plasticizers were further investigated. Polyethylene glycol 400 and diethyl phthalate at a concentration of 10% were used. The results indicated that both plasticizers could enhance the mechanical characteristics and had a slight effect on moisture protection. The stability of pectin in terms of moisture protective properties could, therefore, be modified through the fabrication of composite films with hydrophobic polymers, that is, shellac and the addition of proper plasticizers to enhance mechanical properties, which could offer wide applications for edible film in food, agro, and pharmaceutical industries. The composite film with 50% shellac could improve moisture protective properties of pectin film. Adding a plasticizer could build up the higher mechanical characteristics of composite film. Stability of pectin could be modified by fabrication of composite films with proper content of shellac and plasticizer. © 2017 Institute of Food Technologists®.

  8. Tribological properties of toughened zirconia-based ceramics

    International Nuclear Information System (INIS)

    Stachowiak, G.W.; Stachowiak, G.B.

    1991-01-01

    The physical and mechanical properties of toughened zirconia ceramics are briefly characterized and described with a special emphasis on their tribological behaviour. The wear and friction properties of PSZ and TZP ceramics at room and elevated temperatures are described. The influence of the environment on the tribological characteristics of zirconia ceramics is discussed. Both lubricated and unlubricated conditions for ceramic/ceramic and metal/ceramic sliding contacts are analysed. One of the main, and as yet unresolved problems, lubrication of ceramic at elevated temperatures and/or space environment, is addressed and the possible solutions to the problem are suggested. The critical needs in the research and development area of improving the tribological properties of zirconia ceramics are defined and its future market potentials stated. 30 refs., 2 tabs., 4 figs

  9. YBa2Cu3O(7-x) based superconducting thin films by multitarget sputtering

    International Nuclear Information System (INIS)

    Bouteloup, E.; Mercey, B.; Poullain, G.; Brousse, T.; Murray, H.; Raveau, B.

    1990-01-01

    This paper reports a new technique to prepare superconducting YBa 2 Cu 3 O (7-x) thin films. The multitarget sputtering apparatus described below allows the simultaneous and reproducible production of numerous films with a metallic composition close to Y 17% Ba 33% Cu 50% . Superconducting films (R = 0) at 80 K have been produced on polycrystalline zirconia substrates after a high temperature annealing [fr

  10. The high temperature mechanical characteristics of superplastic 3 mol% yttria stabilized zirconia

    International Nuclear Information System (INIS)

    Owen, D.M.; Chokshi, A.H.

    1998-01-01

    A detailed study was undertaken to characterize the deformation behavior of a superplastic 3 mol% yttria-stabilized tetragonal zirconia (3YTZ) over a wide range of strain rates, temperatures and grain sizes. The experimental data were analyzed in terms of the following equation for high temperature deformation: SR ∝ FS n d -p exp(-Q/RT), where SR is the strain rate, FS is the flow stress, d is the grain size, Q is the activation energy, R is the gas constant, T is the absolute temperature, and n and p are constants termed the stress exponent and the inverse grain size exponent, respectively. The experimental data over a wide range of stresses revealed a transition in stress exponent. Deformation in the low and high stress regions was associated with n about 3 and p about 1, and n about 2 and p about 3, respectively. The transition stress between the two regions decreased with increasing grain size. The activation energy was similar for both regions with a value of about 550 kJ/mol. Microstructural measurements revealed that grains remained essentially equiaxed after the accumulation of large strains, and very limited concurrent grain growths occurred in most experiments. Assessment of possible rate controlling creep mechanisms and comparison with previous studied indicate that in the n=2 region, deformation occurs by a grain boundary sliding process whose rate is independent of impurity content. Deformation in the n=3 region is controlled by an interface reaction that is highly sensitive to impurity content. It is concluded that an increase in impurity content increases yttrium segregation to grain boundaries, which enhances the rate of the interface reaction, thereby decreasing the apparent transition stress between the n=2 and n=3 regions. This unified approach incorporating two sequential mechanisms can rationalize many of the apparently dissimilar results that have been reported previously for deformation of 3YTZ

  11. Survival of anterior cantilevered all-ceramic resin-bonded fixed dental prostheses made from zirconia ceramic.

    Science.gov (United States)

    Sasse, Martin; Kern, Matthias

    2014-06-01

    This study evaluated the clinical outcome of all-ceramic resin-bonded fixed dental prostheses (RBFDPs) with a cantilevered single-retainer design made from zirconia ceramic. Forty-two anterior RBFDPs with a cantilevered single-retainer design were made from yttrium oxide-stabilized zirconium oxide ceramic. RBFDPs were inserted using Panavia 21 TC as luting agent after air-abrasion of the ceramic bonding surface. During a mean observation time of 61.8 months two debondings occurred. Both RBFDPs were rebonded using Panavia 21 TC and are still in function. A caries lesion was detected at one abutment tooth during recall and was treated with a composite filling. Therefore, the overall six-year failure-free rate according to Kaplan-Meier was 91.1%. If only debonding was defined as failure the survival rate increased to 95.2%. Since all RBFDPs are still in function the overall survival rate was 100% after six years. Cantilevered zirconia ceramic RBFDPs showed promising results within the observation period. Single-retainer resin-bonded fixed dental prostheses made from zirconia ceramic show very good mid-term clinical survival rates. They should therefore be considered as a viable treatment alternative for the replacement of single missing anterior teeth especially as compared to an implant therapy. Copyright © 2014 Elsevier Ltd. All rights reserved.

  12. Selective hydrogen detection at high temperature by using yttria-stabilized zirconia-based sensor with coupled metal-oxide-based sensing electrodes

    International Nuclear Information System (INIS)

    Yamaguchi, Mami; Anggraini, Sri Ayu; Fujio, Yuki; Breedon, Michael; Plashnitsa, Vladimir V.; Miura, Norio

    2012-01-01

    A selective and sensitive hydrogen (H 2 ) sensor capable of working at a high operating temperature was developed by using a pair of metal-oxide-based SEs formed on a yttria-stabilized zirconia (YSZ) tube, operating as a mixed-potential type sensor. The utilization of SnO 2 (+30 wt.% YSZ) electrode together with NiO-TiO 2 electrode configured as a combined-type sensor, successfully diminished the response of the examined interfering gases (especially propene), while maintaining high response toward H 2 at an operating temperature of 600 °C under humid operating conditions. The developed sensor exhibited quick response to 100 ppm H 2 , as the 90% response time was observed to be 9 s. The sensing performance of the combined-type sensor was barely affected by changes in water vapor concentration within the range of 1–4 vol.%, suggesting the resilience of the sensor to function in realistic working conditions. This sensor exhibited a linear relationship between sensitivity and H 2 concentration on a logarithmic scale.

  13. A study of the bending resistance of implant-supported reinforced alumina and machined zirconia abutments and copies.

    Science.gov (United States)

    Sundh, Anders; Sjögren, Göran

    2008-05-01

    The purpose of the present study was to evaluate the bending resistance of implant-supported CAD/CAM-processed restorations made out of zirconia or manually shaped made out of reinforced alumina. Units of abutments and copies made of (i) a prefabricated hot isostatic pressed (HIPed) yttrium oxide partially-stabilized zirconia (Y-TZP) (Denzir), (ii) a prefabricated densely-sintered magnesia partially stabilized zirconia (Mg-PSZ) (Denzir-M) or, copies made of (iii) a prefabricated partially-sintered, porous reinforced alumina ceramic (RN synOcta-In-Ceram) were subjected to static loading perpendicularly at the long axis. The abutments were attached to either stainless steel analogs or titanium implant fixtures. The Y-TZP and Mg-PSZ copies were bonded onto the ceramic abutments with a dual-cured resin composite (Rely-X Unicem). Units of titanium abutment attached to a titanium implant fixtures were used as reference. The units comprising Denzir abutments as delivered (pstainless steel analogs exhibited significantly higher bending resistance than the control. The heat-treated Denzir copies bonded to the heat-treated Denzir M abutments attached to titanium implant fixtures and the In-Ceram specimens attached to stainless steel analogs showed significantly (pstainless steel analogs. No statistically significant (p>0.05) differences were seen among the other groups studied. All the ceramic abutments and copies exhibited values that were equal or superior to that of the control and exceeded the reported value, up to 300 N, for maximum incisal bite forces. To assess the clinical behavior long-term clinical studies should be conducted.

  14. Twenty-nine-month follow-up of a paediatric zirconia dental crown.

    Science.gov (United States)

    Lopez Cazaux, Serena; Hyon, Isabelle; Prud'homme, Tony; Dajean Trutaud, Sylvie

    2017-06-14

    The aim of this paper is to present the long-term follow-up of one paediatric zirconia crown on a deciduous molar. Preformed crowns are part of the armamentarium in paediatric dentistry. In recent years, aesthetic alternatives to preformed metal crowns have been developed, first preveneered crowns and then zirconia crowns. This paper describes the restoration of a primary molar with a zirconia crown (EZ-Pedo, Loomis, California, USA) in an 8-year-old boy. In this clinical case, the protocol for the implementation and maintenance of zirconia crowns is detailed. The patient was followed up for 29 months until the natural exfoliation of his primary molar. The adaptation of the zirconia crown, the gingival health and the wear on the opposing tooth were considered. In this case, the paediatric zirconia crown allowed sustainable functional restoration while restoring a natural appearance of the tooth. © BMJ Publishing Group Ltd (unless otherwise stated in the text of the article) 2017. All rights reserved. No commercial use is permitted unless otherwise expressly granted.

  15. The effects of radiant cooling versus convective cooling on human eye tear film stability and blinking rate

    DEFF Research Database (Denmark)

    Nygaard, Linette; Uth, Simon C.; Bolashikov, Zhecho Dimitrov

    2014-01-01

    The effect of indoor temperature, radiant and convective cooling on tear film stability and eye blink frequency was examined. 24 human subjects were exposed to the non-uniform environment generated by localised chilled beam and a chilled ceiling combined with overhead mixing ventilation. The subj......The effect of indoor temperature, radiant and convective cooling on tear film stability and eye blink frequency was examined. 24 human subjects were exposed to the non-uniform environment generated by localised chilled beam and a chilled ceiling combined with overhead mixing ventilation....... The subjects participated in four two-hour experiments. The room air temperature was kept at 26 °C or 28 °C. Tear film samples were collected after 30 min of acclimatisation and at the end of the exposures. Eye blinking frequency was analysed for the first and last 15 min of each exposure. The tear film...... stability decreased as the temperature increased. The highest number of subjects with unchanged or improved tear film quality was observed with the localised chilled beam at 26 °C. A trend was found between subjects who reported eye irritation and had a bad tear film quality....

  16. Synthesis and ceramic processing of alumina and zirconia based composites infiltrated with glass phase for dental applications

    International Nuclear Information System (INIS)

    Duarte, Daniel Gomes

    2009-01-01

    The interest for the use of ceramic materials for dental applications started due to the good aesthetic appearance promoted by the similarity to natural teeth. However, the fragility of traditional ceramics was a limitation for their use in stress conditions. The development of alumina and zirconia based materials, that associate aesthetic results, biocompatibility and good mechanical behaviour, makes possible the employment of ceramics for fabrication of dental restorations. The incorporation of vitreous phase in these ceramics is an alternative to minimize the ceramic retraction and to improve the adhesion to resin-based cements, necessary for the union of ceramic frameworks to the remaining dental structure. In the dentistry field, alumina and zirconia ceramic infiltrated with glassy phase are represented commercially by the In-Ceram systems. Considering that the improvement of powder's synthesis routes and of techniques of ceramic processing contributes for good performance of these materials, the goal of the present work is the study of processing conditions of alumina and/or 3 mol% yttria-stabilized zirconia ceramics infiltrated with aluminum borosilicate lanthanum glass. The powders, synthesized by hydroxide coprecipitation route, were pressed by uniaxial compaction and pre-sintered at temperature range between 950 and 1650 degree C in order to obtain porous ceramics bodies. Vitreous phase incorporation was performed by impregnation of aluminum borosilicate lanthanum powder, also prepared in this work, followed by heat treatment between 1200 and 1400 degree C .Ceramic powders were characterized by thermogravimetry, X-ray diffraction, scanning and transmission electron microscopy, gaseous adsorption (BET) and laser diffraction. Sinterability of alumina and /or stabilized zirconia green pellets was evaluated by dilatometry. Pre-sintered ceramics were characterized by apparent density measurements (Archimedes method), X-ray diffraction and scanning electron

  17. Surface roughness of zirconia for full-contour crowns after clinically simulated grinding and polishing.

    Science.gov (United States)

    Hmaidouch, Rim; Müller, Wolf-Dieter; Lauer, Hans-Christoph; Weigl, Paul

    2014-12-01

    The aim of this study was to evaluate the effect of controlled intraoral grinding and polishing on the roughness of full-contour zirconia compared to classical veneered zirconia. Thirty bar-shaped zirconia specimens were fabricated and divided into two groups (n=15). Fifteen specimens (group 1) were glazed and 15 specimens (group 2) were veneered with feldspathic ceramic and then glazed. Prior to grinding, maximum roughness depth (Rmax) values were measured using a profilometer, 5 times per specimen. Simulated clinical grinding and polishing were performed on the specimens under water coolant for 15 s and 2 N pressure. For grinding, NTI diamonds burs with grain sizes of 20 µm, 10 µm, and 7.5 µm were used sequentially. The ground surfaces were polished using NTI kits with coarse, medium and fine polishers. After each step, Rmax values were determined. Differences between groups were examined using one-way analysis of variance (ANOVA). The roughness of group 1 was significantly lower than that of group 2. The roughness increased significantly after coarse grinding in both groups. The results after glazing were similar to those obtained after fine grinding for non-veneered zirconia. However, fine-ground veneered zirconia had significantly higher roughness than venerred, glazed zirconia. No significant difference was found between fine-polished and glazed zirconia, but after the fine polishing of veneered zirconia, the roughness was significantly higher than after glazing. It can be concluded that for full-contour zirconia, fewer defects and lower roughness values resulted after grinding and polishing compared to veneered zirconia. After polishing zirconia, lower roughness values were achieved compared to glazing; more interesting was that the grinding of glazed zirconia using the NTI three-step system could deliver smooth surfaces comparable to untreated glazed zirconia surfaces.

  18. Short range investigation of sub-micron zirconia particles

    Energy Technology Data Exchange (ETDEWEB)

    Caracoche, M C; Martinez, J A [Departamento de Fisica, IFLP, Facultad de Ciencias Exactas, CICPBA, Universidad Nacional de La Plata (Argentina); Rivas, P C [IFLP-CONICET, Facultad de Ciencias Agrarias y Forestales, Universidad Nacional de La Plata (Argentina); Bondioli, F; Cannillo, V [Dipartimento di Ingegniria dei Materiali e dell' Ambiente, Facolta di Ingegneria, Universita di Modena e Reggio Emilia (Italy); Ferrari, A M, E-mail: cristina@fisica.unlp.edu.a [Dipartimento di Scienza a Metodi dell' Ingegneria, Universita di Modena e Reggio Emilia (Italy)

    2009-05-01

    The Perturbed Angular Correlations technique was used to determine the configurations around Zirconium ions and their thermal behavior in non-aggregated sub-micron zirconia spherical particles. Three residues containing- Zr surroundings were determined for the non-crystalline starting particles, which were identified under the assumption of a certain chemical reactions sequence during synthesis. While the one made up mainly by hydroxyl groups was common to both samples, the two involving mainly organic residues were particle size dependent. Upon crystallization, both samples stabilized in the t'- and t- tetragonal forms and the Xc-cubic form but their amounts and temperatures of appearance were different. On heating, the structure of the smaller particles became gradually monoclinic achieving total degradation upon the subsequent cooling to RT.

  19. Sulfated zirconia modified SBA-15 catalysts for cellobiose hydrolysis

    NARCIS (Netherlands)

    Degirmenci, V.; Uner, D.; Cinlar, B.; Shanks, B.H.; Yilmaz, A.; Santen, van R.A.; Hensen, E.J.M.

    2011-01-01

    Zirconia modified SBA-15 becomes a very active catalyst for the selective hydrolysis of cellobiose to glucose after sulfation. Spectroscopic investigations indicate the presence of Brønsted acid sites with similar properties to those present in conventional sulfated zirconia. Indications are found

  20. Stabilization of polar Mn3O4(001) film on Ag(001): Interplay between kinetic and structural stability

    Science.gov (United States)

    Kundu, Asish K.; Barman, Sukanta; Menon, Krishnakumar S. R.

    2017-10-01

    Stabilization processes of polar surfaces are often very complex and interesting. Understanding of these processes is crucial as it ultimately determines the properties of the film. Here, by the combined study of Low Energy Electron Diffraction (LEED), X-ray Photoelectron Spectroscopy (XPS) and Ultraviolet Photoemission Spectroscopy (UPS) techniques we show that, although there can be many processes involved in the stabilization of the polar surfaces, in case of Mn3O4(001)/Ag(001), it goes through different reconstructions of the Mn2O4 terminated surface which is in good agreements with the theoretical predictions. The complex surface phase diagram has been probed by LEED as a function of film thickness, oxygen partial pressure and substrate temperature during growth, while their chemical compositions have been probed by XPS. Below a critical film thickness of ∼ 1 unit cell height (8 sublayers or 3 ML) of Mn3O4 and oxygen partial pressure range of 2 × 10-8 mbar oxygen partial pressure (> 5 × 10-7 mbar) and higher temperature UHV annealing. The origin of these stripes has been explained with the help of UPS results.

  1. Effect of environmental dust particles on laser textured yttria-stabilized zirconia surface in humid air ambient

    Science.gov (United States)

    Yilbas, B. S.; Ali, H.; Al-Sharafi, A.; Al-Sulaiman, F.; Karatas, C.

    2018-05-01

    Zirconium nitride is used as a selective surface for concentrated solar heating applications and one of the methods to form a zirconium nitride is texturing of zirconia surface by a high intensity laser beam under high pressure nitrogen gas environment. Laser texturing also provides hydrophobic surface characteristics via forming micro/nano pillars at the surface; however, environmental dust settlement on textured surface influences the surface characteristics significantly. In the present study, laser texturing of zirconia surface and effects of the dust particles on the textured surface in a humid air ambient are investigated. Analytical tools are used to assess the morphological changes on the laser textured surface prior and after the dust settlement in the humid air ambient. It is found that laser textured surface has hydrophobic characteristics. The mud formed during condensate of water on the dust particles alters the characteristics of the laser textured surface. The tangential force required to remove the dry mud from the textured surface remains high; in which case, the dried liquid solution at the mud-textured surface interface is responsible for the strong adhesion of the dry mud on the textured surface. The textured surface becomes hydrophilic after the dry mud was removed from the surface by a desalinated water jet.

  2. Stability of amorphous Ge-As(Sb)-Se films to high-energy electron irradiation

    International Nuclear Information System (INIS)

    Savchenko, N.D.

    1999-01-01

    The results of the investigation of high-energy electron (6.5 MeV) irradiation effect on structure, optical, electrical and mechanical properties for thin films obtained by thermal evaporation of Ge-As-Se and Ge-Sb-Se glasses have been presented. The electron-induced changes in film properties versus average coordination number and relative free volume for bulk glasses have been discussed. It has been found that the higher radiation stability is characteristic to the films deposited from the glasses with the lower relative free volume

  3. Charging kinetics in virgin and 1 MeV-electron irradiated yttria-stabilized zirconia in the 300-1000 K range

    International Nuclear Information System (INIS)

    Thome, T.; Braga, D.; Blaise, G.; Cousty, J.; Pham Van, L.; Costantini, J.M.

    2006-01-01

    A study performed with a dedicated scanning electron microscope (SEM) on the surface electrical properties of (1 0 0)-oriented yttria-stabilized zirconia (YSZ) single crystals irradiated with 1 MeV electrons is presented. When compared with virgin YSZ, the 1 MeV-irradiated YSZ shows a decrease of the intrinsic total electron emission coefficient σ 0 and an increase of the time constant τ associated with the charging kinetics of the material at room temperature. These measurements performed with the SEM beam at 10 keV indicate that the defects induced by the 1 MeV-electron irradiation generate a positive electric field of the order of 0.5 x 10 6 V/m at a depth of about 1 μm that prevents electrons to escape. When the SEM beam with a 1.1 keV energy is used, a smaller field (∼0.5 x 10 3 V/m) is detected closer to the surface (∼20 nm). The fading of these fields during the thermal annealing in the 400-1000 K temperature range provides information on the nature of defects induced by the 1 MeV-electron irradiation

  4. Sequential Ar-O2 sputtering of Y2O3, BaF2, and CuO targets for preparation of Y-Ba-Cu-O superconducting films without wet-O2 annealing

    International Nuclear Information System (INIS)

    Bhushan, M.; Strauss, A.J.; Finn, M.C.

    1989-01-01

    Superconducting Y-Ba-Cu-O (YBCO) films have been prepared by ex situ O 2 annealing of multilayer films deposited on yttria-stabilized zirconia substrates by sequential rf diode sputtering of Y 2 O 3 , BaF 2 , and CuO targets, all of which are chemically stable. If sputtering is performed in an Ar ambient, the as-deposited films contain sufficient F to require its removal by annealing in wet O 2 at about 800 degree C or above before the superconducting YBCO phase can be formed by annealing in dry O 2 . However, sputtering in an Ar-O 2 ambient greatly reduces the F content, making it possible to obtain the superconducting phase by annealing in dry O 2 only. If the ambient contains about 20% O 2 , films with T c (R=0)>85 K can be prepared without wet-O 2 annealing. The Ar-O 2 process therefore has the potential for in situ preparation of superconducting YBCO films

  5. The Effect of Zirconia in Hydroxyapatite on Staphylococcus epidermidis Growth

    Directory of Open Access Journals (Sweden)

    Widowati Siswomihardjo

    2012-01-01

    . Conclusion. The addition of zirconia into hydroxyapatite affected the growth of S. epidermidis. Hydroxyapatite with 20% zirconia proved to be an effective concentration to inhibit the growth of S. epidermidis colony.

  6. Optical properties of pre-colored dental monolithic zirconia ceramics.

    Science.gov (United States)

    Kim, Hee-Kyung; Kim, Sung-Hun

    2016-12-01

    The purposes of this study were to evaluate the optical properties of recently marketed pre-colored monolithic zirconia ceramics and to compare with those of veneered zirconia and lithium disilicate glass ceramics. Various shades of pre-colored monolithic zirconia, veneered zirconia, and lithium disilicate glass ceramic specimens were tested (17.0×17.0×1.5mm, n=5). CIELab color coordinates were obtained against white, black, and grey backgrounds with a spectrophotometer. Color differences of the specimen pairs were calculated by using the CIEDE2000 (ΔE 00 ) formula. The translucency parameter (TP) was derived from ΔE 00 of the specimen against a white and a black background. X-ray diffraction was used to determine the crystalline phases of monolithic zirconia specimens. Data were analyzed with 1-way ANOVA, Scheffé post hoc, and Pearson correlation testing (α=0.05). For different shades of the same ceramic brand, there were significant differences in L * , a * , b * , and TP values in most ceramic brands. With the same nominal shade (A2), statistically significant differences were observed in L * , a * , b * , and TP values among different ceramic brands and systems (Pceramics of the corresponding nominal shades ranged beyond the acceptability threshold. Due to the high L * values and low a * and b * values, pre-colored monolithic zirconia ceramics can be used with additional staining to match neighboring restorations or natural teeth. Due to their high value and low chroma, unacceptable color mismatch with adjacent ceramic restorations might be expected. Copyright © 2016 Elsevier Ltd. All rights reserved.

  7. Stability of Tl-Ba-Ca-Cu-O superconducting thin films

    International Nuclear Information System (INIS)

    Siegal, M. P.; Overmyer, D. L.; Venturini, E. L.; Padilla, R. R.; Provencio, P. N.

    1999-01-01

    We report the stability of TlBa 2 CaCu 2 O 7 and Tl 2 Ba 2 CaCu 2 O 8 on LaAlO 3 (100) epitaxial thin films, under a variety of conditions. All films are stable in acetone and methanol and with repeated thermal cycling to cryogenic temperatures. Moisture, especially vapor, degrades film quality rapidly. These materials are stable to high temperatures in either N 2 or O 2 ambients. While total degradation, resulting from Tl depletion, occurs at the same temperatures for both phases, 600 degree sign C in N 2 and 700 degree sign C in O 2 , the onset of degradation occurs at somewhat lower temperatures for TlBa 2 CaCu 2 O 7 than for Tl 2 Ba 2 CaCu 2 O 8 . (c) 1999 Materials Research Society

  8. Zirconia UV-curable colloids for additive manufacturing via hybrid inkjet printing-stereolithography

    DEFF Research Database (Denmark)

    Rosa, Massimo; Barou, C.; Esposito, Vincenzo

    2018-01-01

    Currently, additive manufacturing of ceramics by stereolithography (SLA) is limited to single materials and by a poor thickness resolution that strongly depends on the ceramic particles-UV light interaction. Combining selective laser curing with inkjet printing represents a novel strategy...... to overcome these constrains. Nonetheless, this approach requires UV-curable inks that allow hardening of the printed material and sintering to high density. In this work, we report how to design an ink for inkjet printing of yttria stabilized zirconia (YSZ) which can be impressed by addition of UV...

  9. Improved thermal stability of polylactic acid (PLA) composite film via PLA-β-cyclodextrin-inclusion complex systems.

    Science.gov (United States)

    Byun, Youngjae; Rodriguez, Katia; Han, Jung H; Kim, Young Teck

    2015-11-01

    The effects of the incorporation of PLA-β-cyclodextrin-inclusion complex (IC) and β-cyclodextrin (β-CD) on biopolyester PLA films were investigated. Thermal stability, surface morphology, barrier, and mechanical properties of the films were measured at varying IC (1, 3, 5, and 7%) and β-CD (1 and 5%) concentrations. The PLA-IC-composite films (IC-PLA-CFs) showed uniform morphological structure, while samples containing β-CD (β-CD-PLA-CFs) showed high agglomeration of β-CD due to poor interfacial interaction between β-CD and PLA moieties. According to the thermal property analysis, the 5% IC-PLA-CFs showed 6.6 times lower dimensional changes (6.5%) at the temperature range of 20-80°C than that of pure PLA film (43.0%). The increase of IC or β-CD content in the PLA-composite films shifted the glass transition and crystallization temperature to higher temperature regions. The crystallinity of both composite films improved by increasing IC or β-CD content. Both composite films had higher oxygen and water vapor permeability as IC or β-CD content increased in comparison to pure PLA film. All the composite films had less flexibility and lower tensile strength than the pure PLA film. In conclusion, this study shows that the IC technique is valuable to improve the thermal expansion stability of PLA-based films. Published by Elsevier B.V.

  10. Synthesis and catalytic activity of polysaccharide templated nanocrystalline sulfated zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Sherly, K. B.; Rakesh, K. [Mahatma Gandhi University Regional Research Center in Chemistry, Department of Chemistry, Mar Athanasius College, Kothamangalam-686666, Kerala (India)

    2014-01-28

    Nanoscaled materials are of great interest due to their unique enhanced optical, electrical and magnetic properties. Sulfate-promoted zirconia has been shown to exhibit super acidic behavior and high activity for acid catalyzed reactions. Nanocrystalline zirconia was prepared in the presence of polysaccharide template by interaction between ZrOCl{sub 2}⋅8H{sub 2}O and chitosan template. The interaction was carried out in aqueous phase, followed by the removal of templates by calcination at optimum temperature and sulfation. The structural and textural features were charac