  1. Cold laser machining of nickel-yttrium stabilised zirconia cermets: Composition dependence

    International Nuclear Information System (INIS)

    Sola, D.; Gurauskis, J.; Pena, J.I.; Orera, V.M.

    2009-01-01

    Cold laser micromachining efficiency in nickel-yttrium stabilised zirconia cermets was studied as a function of cermet composition. Nickel oxide-yttrium stabilised zirconia ceramic plates obtained via tape casting technique were machined using 8-25 ns pulses of a Nd: YAG laser at the fixed wavelength of 1.064 μm and a frequency of 1 kHz. The morphology of the holes, etched volume, drill diameter, shape and depth were evaluated as a function of the processing parameters such as pulse irradiance and of the initial composition. The laser drilling mechanism was evaluated in terms of laser-material interaction parameters such as beam absorptivity, material spallation and the impact on the overall process discussed. By varying the nickel oxide content of the composite the optical absorption (-value is greatly modified and significantly affected the drilling efficiency of the green state ceramic substrates and the morphology of the holes. Higher depth values and improved drilled volume upto 0.2 mm 3 per pulse were obtained for substrates with higher optical transparency (lower optical absorption value). In addition, a laser beam self-focussing effect is observed for the compositions with less nickel oxide content. Holes with average diameter from 60 μm to 110 μm and upto 1 mm in depth were drilled with a high rate of 40 ms per hole while the final microstructure of the cermet obtained by reduction of the nickel oxide-yttrium stabilised zirconia composites remained unchanged.

  2. Grain size stabilization of tetragonal phase of zirconia in sputtered Zr-O cermet films

    International Nuclear Information System (INIS)

    Hadavi, M. S.; Keshmiri, H.; Kompany, A.; Zhang, Q. C.

    2005-01-01

    In this research, thin films of Zr/ZrO 2 composites were deposited by reactive magnetron sputtering technique on Si and fused Silica substrates, and their structures were investigated by x-ray diffraction method. During the deposition of the cermet layers, a Zr metallic target was sputtered in a gas mixture of Ar and O 2 . By controlling of O 2 flow rate, the different metal volume fractions in the cermet layers were achieved. The optical response of the samples was studied using spectroscopy methods. Also the effect of vacuum annealing on the structures and the optical properties were studies. x-ray diffraction results indicated that the prepared samples were amorphous and vacuum annealing induced crystallization in the cermet films. This research also show that without doping, the tetragonal phase of Zirconia can be stabilized at a temperature lower than the normal transition temperature. This is g rain size stabilization a nd relates to the small size of the crystallizes. In order to study the electron diffraction in the selected area patterns, the samples were analysed by a high-resolution transmission microscope. The selected area patterns results showed that all of the as prepared samples were amorphous showing evidence of very small Zr crystallites immersed in a dielectric medium. The Sad results are in close agreement with those obtained by x-ray diffraction analysis

  3. Grain size stabilization of tetragonal phase of zirconia in sputtered Zr- O cermet films

    Directory of Open Access Journals (Sweden)

    M. S. Hadavi

    2005-06-01

    Full Text Available  In this research, thin films of Zr/ZrO2 composites were deposited by reactive magnetron sputtering technique on Si and fused Silica substrates, and their structures were investigated by XRD method. During the deposition of the cermet layers, a Zr metallic target was sputtered in a gas mixture of Ar and O2. By controlling of O2 flow rate, the different metal volume fractions in the cermet layers were achieved. The optical response of the samples was studied using spectroscopy methods. Also the effect of vacuum annealing on the structures and the optical properties were studied. XRD results indicated that the prepared samples were amorphous and vacuum annealing induced crystallization in the cermet films. This research also showed that without doping, the tetragonal phase of zirconia can be stabilized at a temperature lower than the normal transition temperature. This is “grain size stabilization” and relates to the small size of the crystallites. In order to study the electron diffraction in the selected area patterns (SAD, the samples were analyzed by a high-resolution transmission microscope. The SAD results showed that all of the as prepared samples were amorphous showing evidence of very small Zr crystallites immersed in a dielectric medium.The SAD results are in close agreement with those obtained by XRD analysis.

  4. Nickel/Yttria-stabilised zirconia cermet anodes for solid oxide fuel cells

    NARCIS (Netherlands)

    Primdahl, Søren

    1999-01-01

    This thesis deals with the porous Ni/yttria-stabilized zirconia (YSZ) cermet anode on a YSZ electrolyte for solid oxide fuel cells (SOFC). Such anodes are predominantly operated in moist hydrogen at 700°C to 1000°C, and the most important technological parameters are the polarization resistance and

  5. High temperature resistant cermet and ceramic compositions

    Science.gov (United States)

    Phillips, W. M. (Inventor)

    1978-01-01

    Cermet compositions having high temperature oxidation resistance, high hardness and high abrasion and wear resistance, and particularly adapted for production of high temperature resistant cermet insulator bodies are presented. The compositions are comprised of a sintered body of particles of a high temperature resistant metal or metal alloy, preferably molybdenum or tungsten particles, dispersed in and bonded to a solid solution formed of aluminum oxide and silicon nitride, and particularly a ternary solid solution formed of a mixture of aluminum oxide, silicon nitride and aluminum nitride. Also disclosed are novel ceramic compositions comprising a sintered solid solution of aluminum oxide, silicon nitride and aluminum nitride.

  6. High temperature oxidation resistant cermet compositions

    Science.gov (United States)

    Phillips, W. M. (Inventor)

    1976-01-01

    Cermet compositions are designed to provide high temperature resistant refractory coatings on stainless steel or molybdenum substrates. A ceramic mixture of chromium oxide and aluminum oxide form a coating of chromium oxide as an oxidation barrier around the metal particles, to provide oxidation resistance for the metal particles.

  7. [Comparative studies on fissure sealing: composite versus Cermet cement].

    Science.gov (United States)

    Hickel, R; Voss, A

    1989-06-01

    Fifty two molars sealed with either composite or Cermet cement were compared. The composite sealant was applied after enamel etching using a rubber dam. Before sealing with Cermet cement the enamel was only cleaned with pumice powder and sodium hypochlorie and the material was applied without enamel etching. After an average follow-up of 1.6 years composite sealants proved to be significantly more reliable. Cermet cement sealings showed defects more frequently.

  8. Influence of irradiation on electrical properties of cermet composition

    International Nuclear Information System (INIS)

    Iskhakov, V.M.; Avanesyan, R.R.; Daukeev, D.K.; Nedorezov, V.G.; Chormonov, N.T.; Chormonov, T.Kh.; Shevelev, G.A.

    1986-01-01

    Cermet composition radiation stability and also possibility of directed change of the composition properties during radiation treatment were studied. Investigations were carried out using cermet composition containing 40 mass % of conducting phase (RuO 2 +Nb 2 O 5 additions) and 60 mass % of alumoborosilicate glass. Composition and organic binder mixture was applied to a dielectric substrate with land by stenciling, then was calcinated in the travelling furnace at 850 deg C for 15 min

  9. Heterogeneous composite bodies with isolated lenticular shaped cermet regions

    Science.gov (United States)

    Sherman, Andrew J [Cirtland Hills, OH

    2009-12-22

    A heterogeneous body having ceramic rich cermet regions in a more ductile metal matrix. The heterogeneous bodies are formed by thermal spray operations on metal substrates. The thermal spray operations apply heat to a cermet powder and project it onto a solid substrate. The cermet powder is composed of complex composite particles in which a complex ceramic-metallic core particle is coated with a matrix precursor. The cermet regions are generally comprised of complex ceramic-metallic composites that correspond approximately to the core particles. The cermet regions are approximately lenticular shaped with an average width that is at least approximately twice the average thickness. The cermet regions are imbedded within the matrix phase and generally isolated from one another. They have obverse and reverse surfaces. The matrix phase is formed from the matrix precursor coating on the core particles. The amount of heat applied during the formation of the heterogeneous body is controlled so that the core particles soften but do not become so fluid that they disperse throughout the matrix phase. The force of the impact on the surface of the substrate tends to flatten them. The flattened cermet regions tend to be approximately aligned with one another in the body.

  10. Cermet anode compositions with high content alloy phase

    Science.gov (United States)

    Marschman, Steven C.; Davis, Norman C.

    1989-01-01

    Cermet electrode compositions comprising NiO-NiFe.sub.2 O.sub.4 -Cu-Ni, and methods for making, are disclosed. Addition of nickel metal prior to formation and densification of a base mixture into the cermet allows for an increase in the total amount of copper and nickel that can be contained in the NiO-NiFe.sub.2 O.sub.4 oxide system. Nickel is present in a base mixture weight concentration of from 0.1% to 10%. Copper is present in the alloy phase in a weight concentration of from 10% to 30% of the densified composition. Such cermet electrodes can be formed to have electrical conductivities well in excess of 100 ohm.sup.-1 cm.sup.-1. Other alloy and oxide system cermets having high content metal phases are also expected to be manufacturable in accordance with the invention.

  11. Toughening of Zirconia composites

    International Nuclear Information System (INIS)

    Burlingame, N.H.

    1980-06-01

    The addition of a ZrO 2 dispersion can significantly enhance the toughness of a ceramic matrix material. The toughness improvement is due to a stress reduction at the tip of a propagating crack which is the result of a preferential martensitic transformation of ZrO 2 particles in the stress field of the crack. From thermodynamic considerations and experimental observations the toughening effect is show to be strongly dependent on the ZrO 2 particle size. The effect of variations in temperature, composition and matrix materials are demonstrated, and analyzed in respect to the resultant deviations in the particle size toughening effect

  12. Osteoblastic cell response to spark plasma-sintered zirconia/titanium cermets.

    Science.gov (United States)

    Fernandez-Garcia, Elisa; Guillem-Marti, Jordi; Gutierrez-Gonzalez, Carlos F; Fernandez, Adolfo; Ginebra, Maria-Pau; Lopez-Esteban, Sonia

    2015-01-01

    Ceramic/metal composites, cermets, arise from the idea to combine the dissimilar properties in the pure materials. This work aims to study the biocompatibility of new micro-nanostructured 3 Y-TZP/Ti materials with 25, 50 and 75 vol.% Ti, which have been successfully obtained by spark slasma sintering technology, as well as to correlate their surface properties (roughness, wettability and chemical composition) with the osteoblastic cell response. All samples had isotropic and slightly waved microstructure, with sub-micrometric average roughness. Composites with 75 vol.% Ti had the highest surface hydrophilicity. Surface chemical composition of the cermets correlated well with the relative amounts used for their fabrication. A cell viability rate over 80% dismissed any cytotoxicity risk due to manufacturing. Cell adhesion and early differentiation were significantly enhanced on materials containing the nanostructured 3 Y-TZP phase. Proliferation and differentiation of SaOS-2 were significantly improved in their late-stage on the composite with 75 vol.% Ti that, from the osseointegration standpoint, is presented as an excellent biomaterial for bone replacement. Thus, spark plasma sintering is consolidated as a suitable technology for manufacturing nanostructured biomaterials with enhanced bioactivity. © The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

  13. Advanced CerMet ceramic composites for medical applications.

    Science.gov (United States)

    Dittmer, Robert; Schaefer, Christian M; Fischer, Jean-Francois; Hausch, Ulrich; Troetzschel, Jens; Specht, Heiko

    2017-11-01

    Implantable active devices such as pacemakers are facing rigorous requirements. Because they reside within the body for years, materials applied in this surrounding must exhibit biocompatibility and extraordinary reliability. They also have to provide a number of functional properties. In this work we present a method that enables the realization of a highly complex profile of properties by means of a dual composite approach. Using multilayer technology, an electrical conductor is embedded into a ceramic matrix, thus, creating conductive paths that are insulated from each other. In addition to this macroscopically hybrid architecture, this approach features a second composite aspect: the conductor is not composed of a single metallic phase, but is a ceramic-metal mixture. Owing to its interpenetrating microstructure, this CerMet allows for a strong and hermetic integration of the conductor into the ceramic matrix otherwise impossible due to mismatch in thermal expansion. In fact, the CerMet ceramic composite exhibits a higher strength than the pure ceramic as revealed by a three-point bending test study. At the same time, the CerMet offers high and virtually metal-like conductor properties, enabling a down-scaling of the conductive paths to 150µm diameter and smaller. Furthermore, the described composite is biocompatible, non-magnetic, and chemically inert, which is vital for the application in active, implantable, medical devices. Beside the general fabrication route, we present the microstructural, functional, and mechanical properties of this newly developed class of dual composites. Copyright © 2017 Elsevier Ltd. All rights reserved.

  14. Deposition, structure, and properties of cermet thin films composed of Ag and Y-stabilized zirconia

    International Nuclear Information System (INIS)

    Wang, L.S.; Barnett, S.A.

    1992-01-01

    This paper reports that Ag 1-x [(Y 2 O 3 ) 0.1 (ZrO 2 ) 0.9 ] x (YSZ) cermet thin films have been deposited by reactive magnetron cosputtering from Ag and Zr/Y targets in Ar-O 2 mixtures. The deposition conditions were such that the YSZ component in the films was fully oxidized. The film densities varied from ∼75% to >85% as the total pressure was decreased from 20 to 5 mTorr. Film resistivities ρ varied with Ag volume fraction f Ag from 5 x 10 -6 Ω-cm to >10 9 Ω-cm. For f Ag Ag . For f Ag > 0.4, ρ decreased more gradually with increasing f Ag . ρ in annealed films ranged from 4 x 10 -4 Ω-cm for f Ag = 0.4 to 5 x 10 -6 Ω-cm for pure Ag. Long term (>100 h) annealing at ≥700 degrees C resulted in a gradual increase in cermet resistivity due to Ag evaporation and Ag segregation to surface islands. Both decomposition mechanisms were effectively suppressed due to Ag evaporation and Ag segregation to surface islands. Both decomposition mechanisms were effectively suppressed at up to 750 degrees C by depositing a 1 μm thick porous perovskite cap layer on the cermet. Complex impedance spectroscopy measurements in air of cermet electrodes on YSZ electrolytes gave interfacial resistances that were a factor of ∼6 lower than those of pure AG electrodes, e.g., 1.4 Ω-cm 2 at 750 degrees C. Ag-YSZ cermets thus have potential as high-conductivity, low-overpotential air electrode materials for solid-oxide electrochemical devices operating at temperatures ≤750 degrees C

  15. Superconducting cermets

    International Nuclear Information System (INIS)

    Goyal, A.; Funkenbusch, P.D.; Chang, G.C.S.; Burns, S.J.

    1988-01-01

    Two distant classes of superconducting cermets can be distinguished, depending on whether or not a fully superconducting skeleton is established. Both types of cermets have been successfully fabricated using non-noble metals, with as high as 60wt% of the metal phase. The electrical, magnetic and mechanical behavior of these composites is discussed

  16. Iron-iron boride cermets - new P/M matrix composites

    International Nuclear Information System (INIS)

    Klimek, L.; Nowacki, J.

    1993-01-01

    Possibilities of producing Fe-Fe 2 B cermets as a result of sintering pure elements Fe and B in a vacuum have been analysed. Attempts of sintering in the solid phase and with the participation of the liquid phase - the Fe-Fe 2 B eutectic have been made. Various investigation of the cermets allowed determination of their structure as well as description of the kinetics of quantitative changes in phase proportions while sintering them. It has been found that its structure varies widely depending on sintering parameters and composition of the sinter. Measurements of Fe-Fe 2 B cermet hardness and wear during dry friction have shown distinct advantages of the cermets under investigation as constructional materials. (author). 10 refs, 6 figs

  17. Iron-iron boride cermets - new P/M matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Klimek, L.; Nowacki, J. [Politechnika Lodzka, Lodz (Poland)

    1993-12-31

    Possibilities of producing Fe-Fe{sub 2}B cermets as a result of sintering pure elements Fe and B in a vacuum have been analysed. Attempts of sintering in the solid phase and with the participation of the liquid phase - the Fe-Fe{sub 2}B eutectic have been made. Various investigation of the cermets allowed determination of their structure as well as description of the kinetics of quantitative changes in phase proportions while sintering them. It has been found that its structure varies widely depending on sintering parameters and composition of the sinter. Measurements of Fe-Fe{sub 2}B cermet hardness and wear during dry friction have shown distinct advantages of the cermets under investigation as constructional materials. (author). 10 refs, 6 figs.

  18. Shear bond strength of indirect composite material to monolithic zirconia.

    Science.gov (United States)

    Sari, Fatih; Secilmis, Asli; Simsek, Irfan; Ozsevik, Semih

    2016-08-01

    This study aimed to evaluate the effect of surface treatments on bond strength of indirect composite material (Tescera Indirect Composite System) to monolithic zirconia (inCoris TZI). Partially stabilized monolithic zirconia blocks were cut into with 2.0 mm thickness. Sintered zirconia specimens were divided into different surface treatment groups: no treatment (control), sandblasting, glaze layer & hydrofluoric acid application, and sandblasting + glaze layer & hydrofluoric acid application. The indirect composite material was applied to the surface of the monolithic zirconia specimens. Shear bond strength value of each specimen was evaluated after thermocycling. The fractured surface of each specimen was examined with a stereomicroscope and a scanning electron microscope to assess the failure types. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey LSD tests (α=.05). Bond strength was significantly lower in untreated specimens than in sandblasted specimens (Pcomposite material and monolithic zirconia.

  19. Reaction of yttria-stabilized zirconia with zirconium, silicon and Zircaloy-4 at high temperature: a compatibility study for cermet fuels

    International Nuclear Information System (INIS)

    Arima, T.; Tateyama, T.; Idemitsu, K.; Inagaki, Y.

    2003-01-01

    Compatibility studies for cermet (ceramic and metal) fuels have been completed for a temperature range of 1073-1423 K. A reaction between yttria-stabilized zirconia (YSZ), as a simulated fuel, and Zr, as a candidate for a metallic matrix, has been observed at temperatures ≥1273 K, which means the formation of a metallic reaction layer at the interface between YSZ and Zr and the occurrence of metallic phases inside the YSZ. Similar results were observed for the YSZ-Zry4 (cladding) system. On the other hand, the degree of reaction was relatively large for the YSZ-Si (metallic matrix) system, and Si diffused into the YSZ. However, the maximum fuel center-line temperature can be predicted to be less than ∼1273 K for cermet fuels. Therefore, compatibility between the ceramic fuel and the metallic matrix should be good under normal reactor operational conditions. Furthermore, since the temperature of the fuel-cladding gap is lower, the cermet fuel and the cladding material are compatible

  20. Cermet electrode

    Science.gov (United States)

    Maskalick, Nicholas J.

    1988-08-30

    Disclosed is a cermet electrode consisting of metal particles of nickel, cobalt, iron, or alloys or mixtures thereof immobilized by zirconia stabilized in cubic form which contains discrete deposits of about 0.1 to about 5% by weight of praseodymium, dysprosium, terbium, or a mixture thereof. The solid oxide electrode can be made by covering a substrate with particles of nickel, cobalt, iron, or mixtures thereof, growing a stabilized zirconia solid oxide skeleton around the particles thereby immobilizing them, contacting the skeleton with a compound of praseodymium, dysprosium, terbium, or a mixture thereof, and heating the skeleton to a temperature of at least 500.degree. C. The electrode can also be made by preparing a slurry of nickel, cobalt, iron, or mixture and a compound of praseodymium, dysprosium, terbium, or a mixture thereof, depositing the slurry on a substrate, heating the slurry to dryness, and growing a stabilized zirconia skeleton around the metal particles.

  1. Absence of Dopant Segregation to the Surface of Scandia and Yttria Co-Stabilized Zirconia

    DEFF Research Database (Denmark)

    Vels Hansen, Karin; Mogensen, Mogens Bjerg

    2012-01-01

    stabilized zirconia. The probable reason for this is that due to its size the Sc3+ ion fits better in the zirconia lattice than Y3+ does. The difference in surface composition may be the explanation for the observed increased tolerance toward sulfur of Ni-ScYSZ compared to Ni-YSZ cermets....

  2. Electrical characterization of zirconia-niobium and zirconia-titanium composites

    International Nuclear Information System (INIS)

    Reis, S.T. dos.

    1993-01-01

    Zirconia-niobium and zirconia-titanium composites were made by powder mixing, cold pressing, and vacuum sintering at 1600 0 C. The metallic particles were added in the proportion of 0-50% by volume. Electrical resistivity measurements were performed by the two probes and the four probes d.c. method as a function of metallic particle concentration. Electrical resistivity of these composites decreased sharply in the region of 30-40 vol% Nb or Ti, in agreement with the percolation theory. Tests in an induction furnace were performed to check the self-heating response of these composites. (author). 33 refs, 40 figs, 11 tabs

  3. Mechanical behavior of mullite-zirconia composites

    Directory of Open Access Journals (Sweden)

    Sahnoune F.

    2010-06-01

    Full Text Available In this work, mechanical properties of mullite–zirconia composites synthesised through reaction sintering of Algerian kaolin, α-Al2O3, and ZrO2 were characterized. Phases present and their transformations were characterized using x-ray diffraction. Hardness H and fracture toughness KIC were measured by Vickers indentation using a Zwick microhardness tester. The flexural strength was measured through three point bending test using an Instron Universal Testing Machine. It was found that the increase of ZrO2 content (from 0 to 32wt.% decreased the microhardness of the composites from 14 to 10.8 GPa. However, the increase of ZrO2 content (from 0 to 24wt.% increased the flexural strength of the composites from 142 to 390 MPa then decreased it with further increase of ZrO2 content. Also, the fracture toughness increased from 1.8 to 2.9 MPa.m1/2 with the increase of ZrO2 content from 0 to 32 wt.%; and the rate of the increase decreased at higher fractions of ZrO2 content. The average linear coefficient of thermal expansion (within the range 50 to 1450°C for samples containing 0 and 16 wt.% ZrO2 sintered at 1600°C for 2 hours was 4.7 x10-6 K-1 and 5.2 x 10-6 K-1 respectively.

  4. Electrical characterization of zirconia-niobium and zirconia-titanium composites; Caracterizacao eletrica dos compositos zirconia-niobio e zirconia-titanio

    Energy Technology Data Exchange (ETDEWEB)

    Reis, S.T. dos

    1994-12-31

    Zirconia-niobium and zirconia-titanium composites were made by powder mixing, cold pressing, and vacuum sintering at 1600{sup 0} C. The metallic particles were added in the proportion of 0-50% by volume. Electrical resistivity measurements were performed by the two probes and the four probes d.c. method as a function of metallic particle concentration. Electrical resistivity of these composites decreased sharply in the region of 30-40 vol% Nb or Ti, in agreement with the percolation theory. Tests in an induction furnace were performed to check the self-heating response of these composites. (author). 33 refs, 40 figs, 11 tabs.

  5. Preparation and Mechanical Properties of TiC-Fe Cermets and TiC-Fe/Fe Bilayer Composites

    Science.gov (United States)

    Zheng, Yong; Zhou, Yang; Li, Runfeng; Wang, Jiaqi; Chen, Lulu; Li, Shibo

    2017-10-01

    TiC-Fe cermets and TiC-Fe/Fe bilayer composites consisting of a pure Fe layer and a TiC-Fe cermets layer were fabricated by hot-pressing sintering. The pure Fe layer contributes to the toughness of composites, and the TiC-Fe cermets layer endows the composites with an improved tensile strength and hardness. The effect of TiC contents (30-60 vol.%) on the mechanical properties of TiC-Fe cermets and TiC-Fe/Fe bilayer composites was investigated. Among the TiC-Fe cermets, the 40 vol.% TiC-Fe cermets possessed the highest tensile strength of 581 MPa and Vickers hardness of 5.1 GPa. The maximum fracture toughness of 17.0 MPa m1/2 was achieved for the TiC-Fe cermets with 30 vol.% TiC. For the TiC-Fe/Fe bilayer composites, the 40 vol.% TiC-Fe/Fe bilayer composite owns the maximum tensile strength of 588 MPa, which is higher than that of 40 vol.% TiC-Fe cermets. In addition, the 33.5% increment of tensile strength of 30 vol.% TiC-Fe/Fe bilayer composite comparing with the 30 vol.% TiC-Fe cermets, which is attributed to the 30 vol.% TiC-Fe/Fe bilayer composite exhibited the largest interlaminar shear strength of 335 MPa. The bilayer composites are expected to be used as wear resistance components in some heavy wear conditions.

  6. Research of zirconia-based oxide spheres for CERMET fuel. Production through internal gelation process and the compatibility with Zr, Zircaloy-4 and Si

    International Nuclear Information System (INIS)

    Idemitsu, Kazuya; Inagaki, Yaohiro; Arima, Tatsumi

    2003-05-01

    Optimizing of sol-gel processes was carried out for manufacturing of ziroconium based oxide spheres used in CERMET fuels. In addition, compatibility of CERMET fuels was studied. The Zr 0.85-x Y 0.1 Er 0.05 Ce x O 2 (x=0.0-0.2) oxide spheres were made by preparation of suitable starting materials and the dropping method for an internal gelation process, and thorugh suitable drying, calcination and sintering processes. However, further studies were needed for optimizing the sintering condition. About the reaction of YSZ(yttria-stabilized zirconia) with Zr, Zry4 and Si, isothermal heating tests have been done at the temperature range from 800degC to 1150degC for a maximum of 112 days. Some reactions between YSZ and Zr were observed at temperatures ≥1000degC, which means the formation of a metallic reaction layer at the interface between them and the occurrence of meatallic phases inside the YSZ. Similar results were observed for the YSZ-Zry4 (cladding) system. The YSZ and Si were compatible below the temperature of 1000degC. However, above the temperatures, Si attacked YSZ so that the reaction layers formed on the YSZ side. (author)

  7. Sintering of Mo2FeB2 based cermet and its layered composites containing Sic fibers

    International Nuclear Information System (INIS)

    Rao, D.; Upadhyaya, G.S.

    2001-01-01

    In the present investigation Mo 2 FeB 2 based cermet (KH-C50) and its composites containing SiC fibers were sintered in two different atmospheres namely hydrogen and vacuum. It was observed that vacuum sintered samples have remarkably lower porosities than the hydrogen sintered ones. Two different sintering cycles were employed for each of the atmosphere and properties of the material were studied. Introduction of fibers in the composite imparts shrinkage anisotropy during sintering. Fiber containing cermets have rather poor densification and transverse rupture strength (TRS). TRS, macro and microhardness, and boride grain size measurements were also carried out for the cermets sintered in different atmospheres. (author)

  8. Zirconia based inert matrix fuel: fabrication concepts and feasibility studies

    International Nuclear Information System (INIS)

    Ingold, F.; Burghartz, M.; Ledergerber, G.

    1999-01-01

    The internal gelation process has traditionally been applied to fabricate standard fuel based on uranium, typically UO2 and MOX. To meet the recent aim to destroy plutonium in the most effective way, a uranium free fuel was evaluated. The fuel development programme at PSI has been redirected toward a fuel based on zirconium oxide or a mixture of zirconia and a conducting material to form ceramic/metal (CERMET) or ceramic/ceramic (CERCER) combinations. A feasibility study was carried out to demonstrate that microspheres based on zirconia and spinel can be fabricated with the required properties. The gelation parameters were investigated to optimise compositions of the starting solutions. Studies to fabricate a composite material (from zirconia and spinel) are ongoing. If the zirconia/spinel ratio is chosen appropriately, the low thermal conductivity of pure zirconia can be compensated by the higher thermal conductivity of spinel. Another solution to offset the low thermal conductivity of zirconia is the development of a CERMET, which consists of fine particles bearing plutonium in a cubic zirconia lattice dispersed in a metallic matrix. The fabrication of such a CERMET is also being studied. (author)

  9. Internal reforming characteristics of cermet supported solid oxide fuel cell using yttria stabilized zirconia fed with partially reformed methane

    Energy Technology Data Exchange (ETDEWEB)

    Momma, Akihiko; Takano, Kiyonami; Tanaka, Yohei; Negishi, Akira; Kato, Ken; Nozaki, Ken; Kato, Tohru [Energy Technology Research Institute, National Institute of Advanced Industrial Science and Technology, 1-1-1 Umezono Tsukuba Ibaraki, 305-8568 (Japan); Ichigi, Takenori; Matsuda, Kazuyuki; Ryu, Takashi [Application Development Project, Corporate R and D, NGK Insulators, Ltd., 2-56 Suda-cho Mizuho-ku Nagoya-shi Aichi, 467-8530 (Japan)

    2009-08-01

    In order to investigate the internal reforming characteristics in a cermet supported solid oxide fuel cell (SOFC) using YSZ as the electrolyte, the concentration profiles of the gaseous species along the gas flow direction in the anode were measured. Partially reformed methane using a pre-reformer kept at a constant temperature is supplied to the center of the cell which is operated with a seal-less structure at the gas outlet. The anode gas is sucked in via silica capillaries to the initially evacuated gas tanks. The process is simultaneously carried out using five sampling ports. The sampled gas is analyzed by a gas chromatograph. Most of the measurements are made at the cell temperature (T{sub cell}) of 750 C and at various temperatures of the pre-reformer (T{sub ref}) with various fuel utilizations (U{sub f}) of the cell. The composition of the fuel at the inlet of the anode was confirmed to be almost the same as that theoretically calculated assuming equilibrium at the temperature of the pre-reformer. The effect of internal reforming in the anode is clearly observed as a steady decrease in the methane concentration along the flow axis. The effect of the water-gas shift reaction is also observed as a decrease in the CO{sub 2} concentration and an increase of CO concentration around the gas inlet region, as the water-gas shift reaction inversely proceeds when T{sub cell} is higher than T{sub ref}. The diffusion of nitrogen from the seal-less outermost edge is observed, and the diffusion is confirmed to be more significant as U{sub f} decreases. The observations are compared with the results obtained by the SOFC supported by lanthanum gallate electrolyte. With respect to the internal reforming performance, the cell investigated here is found to be more effective when compared to the previously reported electrolyte supported cell. (author)

  10. Internal reforming characteristics of cermet supported solid oxide fuel cell using yttria stabilized zirconia fed with partially reformed methane

    Science.gov (United States)

    Momma, Akihiko; Takano, Kiyonami; Tanaka, Yohei; Negishi, Akira; Kato, Ken; Nozaki, Ken; Kato, Tohru; Ichigi, Takenori; Matsuda, Kazuyuki; Ryu, Takashi

    In order to investigate the internal reforming characteristics in a cermet supported solid oxide fuel cell (SOFC) using YSZ as the electrolyte, the concentration profiles of the gaseous species along the gas flow direction in the anode were measured. Partially reformed methane using a pre-reformer kept at a constant temperature is supplied to the center of the cell which is operated with a seal-less structure at the gas outlet. The anode gas is sucked in via silica capillaries to the initially evacuated gas tanks. The process is simultaneously carried out using five sampling ports. The sampled gas is analyzed by a gas chromatograph. Most of the measurements are made at the cell temperature (T cell) of 750 °C and at various temperatures of the pre-reformer (T ref) with various fuel utilizations (U f) of the cell. The composition of the fuel at the inlet of the anode was confirmed to be almost the same as that theoretically calculated assuming equilibrium at the temperature of the pre-reformer. The effect of internal reforming in the anode is clearly observed as a steady decrease in the methane concentration along the flow axis. The effect of the water-gas shift reaction is also observed as a decrease in the CO 2 concentration and an increase of CO concentration around the gas inlet region, as the water-gas shift reaction inversely proceeds when T cell is higher than T ref. The diffusion of nitrogen from the seal-less outermost edge is observed, and the diffusion is confirmed to be more significant as U f decreases. The observations are compared with the results obtained by the SOFC supported by lanthanum gallate electrolyte. With respect to the internal reforming performance, the cell investigated here is found to be more effective when compared to the previously reported electrolyte supported cell.

  11. Functionalization of sol-gel zirconia composites with europium complexes

    International Nuclear Information System (INIS)

    Danchova, Nina; Gutzov, Stoyan

    2014-01-01

    Different sol-gel strategies based on functionalization of ZrO 2 :Eu microparticles with 1,10-phenanthroline (phen) and incorporation of colloidal Eu(phen) 2 (NO 3 ) 3 into zirconia have been used to obtain hybrid sol-gel composites with controlled optical properties. The process leads to materials with quantum yields of about 48 % monitoring the 615 nm emission line at 350 nm excitation. Excitation/luminescence spectroscopy, diffuse reflectance spectroscopy and X-ray diffraction have been used to characterize the hybrid zirconia composites. (orig.)

  12. Synthesis of Ca,Y-zirconia/hydroxyapatite nanoparticles and composites

    Czech Academy of Sciences Publication Activity Database

    Částková, K.; Hadraba, Hynek; Matoušek, A.; Roupcová, P.; Chlup, Zdeněk; Novotná, L.; Cihlář, J.

    2016-01-01

    Roč. 36, č. 12 (2016), s. 2903-2912 ISSN 0955-2219 R&D Projects: GA ČR GA14-11234S; GA MŠk(CZ) LQ1601 Institutional support: RVO:68081723 Keywords : Zirconia * Hydroxyapatite * Composite * Bioactivity * Mechanical properties Subject RIV: JH - Ceramic s, Fire-Resistant Materials and Glass Impact factor: 3.411, year: 2016

  13. Phase composition of yttrium-doped zirconia ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Hennig, Christoph; Scheinost, Andreas C. [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Molecular Structures; Weiss, Stephan [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Surface Processes; Ikeda-Ohno, Atsushi [Helmholtz-Zentrum Dresden-Rossendorf e.V., Dresden (Germany). Chemistry of the F-Elements; Gumeniuk, R. [Technische Univ. Bergakademie Freiberg (Germany). Inst. fuer Experimentelle Physik

    2017-06-01

    Ceramic material might be an alternative to borosilicate glass for the immobilization of nuclear waste. The crystallinity of ceramic material increases the corrosion resistance over several magnitudes in relation to amorphous glasses. The stability of such ceramics depend on several parameters, among them the crystal phase composition. A reliable quantitative phase analysis is necessary to correlate the macroscopic material properties with structure parameters. We performed a feasibility study based on yttrium-doped zirconia ceramics as analogue for trivalent actinides to ascertain that the nanosized crystal phases in zirconia ceramics can be reliably determined.

  14. Metal-Matrix Hardmetal/Cermet Reinforced Composite Powders for Thermal Spray

    Directory of Open Access Journals (Sweden)

    Dmitri GOLJANDIN

    2012-03-01

    Full Text Available Recycling of materials is becoming increasingly important as industry response to public demands, that resources must be preserved and environment protected. To produce materials competitive in cost with primary product, secondary producers have to pursue new technologies and other innovations. For these purposes different recycling technologies for composite materials (oxidation, milling, remelting etc are widely used. The current paper studies hardmetal/cermet powders produced by mechanical milling technology. The following composite materials were studied: Cr3C2-Ni cermets and WC-Co hardmetal. Different disintegrator milling systems for production of powders with determined size and shape were used. Chemical composition of produced powders was analysed.  To estimate the properties of recycled hardmetal/cermet powders, sieving analysis, laser granulometry and angularity study were conducted. To describe the angularity of milled powders, spike parameter–quadric fit (SPQ was used and experiments for determination of SPQ sensitivity and precision to characterize particles angularity were performed. Images used for calculating SPQ were taken by SEM processed with Omnimet Image Analyser 22. The graphs of grindability and angularity were composed. Composite powders based on Fe- and Ni-self-fluxing alloys for thermal spray (plasma and HVOF were produced. Technological properties of powders and properties of thermal sprayed coatings from studied powders were investigated. The properties of spray powders reinforced with recycled hardmetal and cermet particles as alternatives for cost-sensitive applications were demonstrated.DOI: http://dx.doi.org/10.5755/j01.ms.18.1.1348

  15. Reduction Dynamics of Doped Ceria, Nickel Oxide, and Cermet Composites Probed Using In Situ Raman Spectroscopy.

    Science.gov (United States)

    Maher, Robert C; Shearing, Paul R; Brightman, Edward; Brett, Dan J L; Brandon, Nigel P; Cohen, Lesley F

    2016-01-01

    The redox properties of gadolinium doped ceria (CGO) and nickel oxide (NiO) composite cermets underpin the operation of solid oxide electrochemical cells. Although these systems have been widely studied, a full comprehension of the reaction dynamics at the interface of these materials is lacking. Here, in situ Raman spectroscopic monitoring of the redox cycle is used to investigate the interplay between the dynamic and competing processes of hydrogen spillover and water dissociation on the doped ceria surface. In order to elucidate these mechanisms, the redox process in pure CGO and NiO is studied when exposed to wet and dry hydrogen and is compared to the cermet behavior. In dry hydrogen, CGO reduces relatively rapidly via a series of intermediate phases, while NiO reduces via a single-step process. In wet reducing atmospheres, however, the oxidation state of pure CGO is initially stabilized due to the dissociation of water by reduced Ce(III) and subsequent incorporation of oxygen into the structure. In the reduction process involving the composite cermet, the close proximity of the NiO improves the efficiency and speed of the composite reduction process. Although NiO is already incorporated into working cells, these observations suggest direct routes to further improve cell performance.

  16. High temperature resistant cermet and ceramic compositions. [for thermal resistant insulators and refractory coatings

    Science.gov (United States)

    Phillips, W. M. (Inventor)

    1978-01-01

    High temperature oxidation resistance, high hardness and high abrasion and wear resistance are properties of cermet compositions particularly to provide high temperature resistant refractory coatings on metal substrates, for use as electrical insulation seals for thermionic converters. The compositions comprise a sintered body of particles of a high temperature resistant metal or metal alloy, preferably molybdenum or tungsten particles, dispersed in and bonded to a solid solution formed of aluminum oxide and silicon nitride, and particularly a ternary solid solution formed of a mixture of aluminum oxide, silicon nitride and aluminum nitride. Ceramic compositions comprising a sintered solid solution of aluminum oxide, silicon nitride and aluminum nitride are also described.

  17. Oxidation of mullite-zirconia-alumina-silicon carbide composites

    International Nuclear Information System (INIS)

    Baudin, C.; Moya, J.S.

    1990-01-01

    This paper reports the isothermal oxidation of mullite-alumina-zirconia-silicon carbide composites obtained by reaction sintering studied in the temperature interval 800 degrees to 1400 degrees C. The kinetics of the oxidation process was related to the viscosity of the surface glassy layer as well as to the crystallization of the surface film. The oxidation kinetics was halted to T ≤ 1300 degrees C, presumably because of crystallization

  18. Wear Resistant Thermal Sprayed Composite Coatings Based on Iron Self-Fluxing Alloy and Recycled Cermet Powders

    Directory of Open Access Journals (Sweden)

    Heikki SARJAS

    2012-03-01

    Full Text Available Thermal spray and WC-Co based coatings are widely used in areas subjected to abrasive wear. Commercial  cermet thermal spray powders for HVOF are relatively expensive. Therefore applying these powders in cost-sensitive areas like mining and agriculture are hindered. Nowadays, the use of cheap iron based self-fluxing alloy powders for thermal spray is limited. The aim of this research was to study properties of composite powders based on self-fluxing alloys and recycled cermets and to examine the properties of thermally sprayed (HVOF coatings from composite powders based on iron self-fluxing alloy and recycled cermet powders (Cr3C2-Ni and WC-Co. To estimate the properties of  recycled cermet powders, the sieving analysis, laser granulometry and morphology were conducted. For deposition of coatings High Velocity Oxy-Fuel spray was used. The structure and composition of powders and coatings were estimated by SEM and XRD methods. Abrasive wear performance of coatings was determined and compared with wear resistance of coatings from commercial powders. The wear resistance of thermal sprayed coatings from self-fluxing alloy and recycled cermet powders at abrasion is comparable with wear resistance of coatings from commercial expensive spray powders and may be an alternative in tribological applications in cost-sensitive areas.DOI: http://dx.doi.org/10.5755/j01.ms.18.1.1338

  19. On the processing, microstructure, mechanical and wear properties of cermet/stainless steel layer composites

    International Nuclear Information System (INIS)

    Farid, Akhtar; Guo Shiju

    2007-01-01

    This study deals with layer composites of carbide reinforcements and stainless steel prepared successfully by powder technology. The layer material consisted of two layers. The top layer consisted of reinforcements (TiC and NbC) and 465 stainless steel as the binder material for the carbides. The bottom layer was entirely of binder material (465 stainless steel). The microstructure of the composite was characterized by scanning electron microscopy. The microstructural study revealed that the top layer (TiC-NbC/465 stainless steel) showed the typical core-rim microstructure of conventional steel bonded cermets and the bottom layer showed the structure of sintered steel. An intermediate layer was found with a gradient microstructure, having a higher carbide content towards the cermet layer and lower carbide content towards the stainless steel layer. The bending strength of the layered material measured in the direction perpendicular to the layer alignment was remarkably high. The variation of strength as a function of the thickness of the bottom layer revealed that the character of the material changed from the cermet, to a layer composite and then towards metallic materials. The wear resistance of the top layer was studied against high speed steel. The wear mechanisms were discussed by means of microscopical observations on the worn surfaces. The wear was severe at higher wear loads and lower TiC content. Microploughing of the stainless steel matrix was found to be the dominant wear mechanism. Heavy microploughing and rapid removal of material from the wear surface was observed at high wear load. The fracture morphologies of the top, bottom and intermediate layers are reported

  20. Esterification of fatty acids using sulfated zirconia and composites activated carbon/sulfated zirconia catalysts

    International Nuclear Information System (INIS)

    Brum, Sarah S.; Santos, Valeria C. dos; Destro, Priscila; Guerreiro, Mario Cesar

    2011-01-01

    In this work sulfated zirconia (SZr) and activated carbon/SZr composites produced by impregnation method with or without heating treatment step (CABC/SZr-I and CABC/SZr-I SC) and by the method of synthesis of SZr on the carbon (CABC/SZr-S) was used as catalysts in the esterification reactions of fatty acids. The SZr presented very active, conversions higher than 90% were obtained after 2 h of reaction. The activity of the composite CABC/SZr-I20%SC was up to 92%, however, this was directly related to time and temperature reactions. CABC/SZr-I and CABC/SZr-S were less active in esterification reactions, what could be attributed to its low acidity. (author)

  1. Microstructure-electrical properties relation of zirconia based ceramic composites

    International Nuclear Information System (INIS)

    Fonseca, Fabio Coral

    2001-01-01

    The electrical properties of zirconia based ceramic composites were studied by impedance spectroscopy. Three materials were prepared with different relative compositions of the conducting and insulating phases: (ZrO 2 :8 mol% Y 2 ) 3 ) + MgO, (ZrO 2 :8 mol% Y 2 O 3 ) + Y 2 O 3 and ZrO 2 + 8 mol% Y 2 O 3 . All specimens were analyzed by X-ray diffraction and scanning electron microscopy for microstructural characterization and for correlation of microstructural aspects with electrical properties. For (ZrO 2 :8 mol% Y 2 O 3 ) + MgO the main results show that the dependence of the different (microstructural constituents) contributions to the electrical resistivity on the magnesia content follows two stages: one below and another above the solubility limit of magnesia in Yttria-stabilized zirconia. The same dependence is found for the lattice parameter determined by X-ray diffraction measurements. The impedance diagrams of the composites have been resolved allowing the identification of contributions due to the presence of each microstructural constituent in both stages. Magnesia as a second phase is found to inhibit grain growth in Yttria-stabilized zirconia and the solubility limit for magnesia in the zirconia matrix is around 10 mol%. For (ZrO 2 :8 mol% Y 2 O 3 ) + Y 2 O 3 the main results show that: Yttria is present as a second phase for 1350 deg C /0.1 h sintering; the addition of 2 mol% of Yttria does not modify significantly the electrical properties; the solubility limit for Yttria is around 2 mol% according to electrical measurements. Similarly to magnesia, Yttria inhibits grain growth on Yttria-stabilized zirconia. The general effective medium theory was used to analyze the percolation of the insulating phase; the percolation threshold is different if one considers separately the total, bulk and grain boundary contributions to the electrical conductivity: 32.0, 38.5 and 27.8 vol% for total, intra and intergranular contributions, respectively. The increase of

  2. Multidisciplinary Simulation of Graphite-Composite and Cermet Fuel Elements for NTP Point of Departure Designs

    Science.gov (United States)

    Stewart, Mark E.; Schnitzler, Bruce G.

    2015-01-01

    This paper compares the expected performance of two Nuclear Thermal Propulsion fuel types. High fidelity, fluid/thermal/structural + neutronic simulations help predict the performance of graphite-composite and cermet fuel types from point of departure engine designs from the Nuclear Thermal Propulsion project. Materials and nuclear reactivity issues are reviewed for each fuel type. Thermal/structural simulations predict thermal stresses in the fuel and thermal expansion mis-match stresses in the coatings. Fluid/thermal/structural/neutronic simulations provide predictions for full fuel elements. Although NTP engines will utilize many existing chemical engine components and technologies, nuclear fuel elements are a less developed engine component and introduce design uncertainty. Consequently, these fuel element simulations provide important insights into NTP engine performance.

  3. Dielectric properties of alumina/zirconia composites at millimeter wavelengths

    International Nuclear Information System (INIS)

    Molla, J.; Heidinger, R.; Ibarra, A.; Link, G.

    1994-01-01

    Alumina-zirconia composites with ZrO 2 contents up to 20% and negligible porosity were investigated at millimeter (mm) wavelengths to determine the changes appearing in the dielectric properties of pure alumina ceramics when unstabilized or partially stabilized ZrO 2 is added to improve the mechanical strength. It is demonstrated that it essential to distinguish between the contributions of the monoclinic and the tetragonal phase of zirconia (m-ZrO 2 , t-ZrO 2 ). Permittivity is raised with increasing content of either phases; the effective permittivity can be assessed by the rule of mixtures (Maxwell-Garnett formulation of the generalized Clasussius-Mossotti relation) using permittivity values of 10 for Al 2 O 3 , 14-21 for m-ZrO 2 and 40-45 for t-ZrO 2 . The permittivity data show only a small variation in the investigated range of 9-145 GHz. For the dielectric loss, there is evidence of a predominant contribution of m-ZrO 2 ; in addition, the marked increase in loss with frequency becomes sharper. The t-ZrO 2 , which is responsible for strengthening, does not show any significant influence on losses. It is therefore concluded, that ZrO 2 strengthening of alumina is feasible without affecting mm-wave losses at room temperature as long as the presence of m-ZrO 2 is avoided

  4. General review on cermets

    International Nuclear Information System (INIS)

    Nouvel, G.

    1975-01-01

    After an attempt to classify the basic constituents of cermets in function of their resistivity and microhardness, the history of ceramic-metal composites is reviewed. The two main methods of production, sintering and impregnation, are examined from the point of view of the problems posed and solutions required to obtain optimum mechanical properties (resistance to creep and thermal shock...). A summary table of the chief cermets and their applications is proposed with precise details in some particular cases [fr

  5. Shear bond strength between an indirect composite layering material and feldspathic porcelain-coated zirconia ceramics.

    Science.gov (United States)

    Fushiki, Ryosuke; Komine, Futoshi; Blatz, Markus B; Koizuka, Mai; Taguchi, Kohei; Matsumura, Hideo

    2012-10-01

    This study aims to evaluate the effect of both feldspathic porcelain coating of zirconia frameworks and priming agents on shear bond strength between an indirect composite material and zirconia frameworks. A total of 462 airborne-particle-abraded zirconia disks were divided into three groups: untreated disks (ZR-AB), airborne-particle-abraded zirconia disks coated with feldspathic porcelain, (ZR-PO-AB), and hydrofluoric acid-etched zirconia disks coated with feldspathic porcelain (ZR-PO-HF). Indirect composite (Estenia C&B) was bonded to zirconia specimens with no (CON) or one of four priming agents--Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB + activator), Estenia Opaque primer, or Porcelain Liner M Liquid B (PLB)--with or without an opaque material (Estenia C&B Opaque). All specimens were tested for shear bond strength before and after 20,000 thermocycles. The Steel-Dwass test and Mann-Whitney U test were used to compare shear bond strength. In ZR-AB specimens, the initial bond strength of the CPB and CPB + Activator groups was significantly higher as compared with the other three groups (P material, bond strength was significantly lower in ZR-AB specimens than in ZR-PO-AB and ZR-PO-HF specimens (P composite to zirconia independent of surface treatment. The use of a silane coupling agent and opaque material yields durable bond strength between the indirect composite and feldspathic-porcelain-coated zirconia. The results of the present study suggest that feldspathic porcelain coating of zirconia frameworks is an effective method to obtain clinically acceptable bond strengths of a layering indirect composite material to a zirconia framework.

  6. EFFECTIVE ELASTIC PROPERTIES OF ALUMINA-ZIRCONIA COMPOSITE CERAMICS - PART 4. TENSILE MODULUS OF POROUS ALUMINA AND ZIRCONIA

    Directory of Open Access Journals (Sweden)

    W. Pabst

    2004-12-01

    Full Text Available In this fourth paper of a series on the effective elastic properties of alumina-zirconia composite ceramics the influence of porosity on the effective tensile modulus of alumina and zirconia ceramics is discussed. The examples investigated are alumina and zirconia ceramics prepared from submicron powders by starch consolidation casting using two different types of starch, potato starch (median size D50 =47.2 µm and corn starch (median size D50 =13.7 µm. The dependence of effective tensile moduli E, on the porosity f, measured for porosities in the ranges of approx. 19-55 vol.% and 10-42 vol.% for alumina and zirconia, respectively, using a resonant frequency technique, was evaluated by fitting with various model relations, including newly developed ones. A detailed comparison of the fitting results suggests the superiority of the new relation E/E0 = (1 - f·(1 - f/fC, developed by the authors (with the tensile modulus of the dense ceramic material E0 and the critical porosity fC, over most other existing fit models. Only for special purposes and well-behaved data sets the recently proposed exponential relation E/E0 = exp [-Bf/(1 - f] and the well-known Phani-Niyogi relation E/E0 = (1 - f/fCN might be preferable.

  7. Shear bond strength of veneering porcelain to zirconia: Effect of surface treatment by CNC-milling and composite layer deposition on zirconia.

    Science.gov (United States)

    Santos, R L P; Silva, F S; Nascimento, R M; Souza, J C M; Motta, F V; Carvalho, O; Henriques, B

    2016-07-01

    The purpose of this study was to evaluate the shear bond strength of veneering feldspathic porcelain to zirconia substrates modified by CNC-milling process or by coating zirconia with a composite interlayer. Four types of zirconia-porcelain interface configurations were tested: RZ - porcelain bonded to rough zirconia substrate (n=16); PZ - porcelain bonded to zirconia substrate with surface holes (n=16); RZI - application of a composite interlayer between the veneering porcelain and the rough zirconia substrate (n=16); PZI - application of a composite interlayer between the porcelain and the zirconia substrate treated by CNC-milling (n=16). The composite interlayer was composed of zirconia particles reinforced porcelain (30%, vol%). The mechanical properties of the ceramic composite have been determined. The shear bond strength test was performed at 0.5mm/min using a universal testing machine. The interfaces of fractured and untested specimens were examined by FEG-SEM/EDS. Data was analyzed with Shapiro-Wilk test to test the assumption of normality. The one-way ANOVA followed by Tukey HSD multiple comparison test was used to compare shear bond strength results (α=0.05). The shear bond strength of PZ (100±15MPa) and RZI (96±11MPa) specimens were higher than that recorded for RZ (control group) specimens (89±15MPa), although not significantly (p>0.05). The highest shear bond strength values were recorded for PZI specimens (138±19MPa), yielding a significant improvement of 55% relative to RZ specimens (p<0.05). This study shows that it is possible to highly enhance the zirconia-porcelain bond strength - even by ~55% - by combining surface holes in zirconia frameworks and the application of a proper ceramic composite interlayer. Copyright © 2016 Elsevier Ltd. All rights reserved.

  8. Influence of the chemical composition and temperature in the mechanical behaviour of U3O8-Al cermets

    International Nuclear Information System (INIS)

    Ferreira, P.I.; Figueredo, A.M. de

    1982-01-01

    U 3 O 8 -Al nuclear cermets, with U 3 O 8 content varying from zero to 80 wt%, were prepared by rotary swaging of U 3 O 8 -Al compacts at 500 0 C. Specimens were fabricated from these materials and tensile tested at the temperatures 25 0 , 200 0 , 300 0 and 400 0 C at a strain rate of 4.3 x 10 - 5 s - 1 . The yield stress σ sub(E) and the ultimate tensile strength σ sub(R), were analysed as a function of the test temperature and cermet composition. The results show that the dependence of σ sub(E) and σ sub(R) on composition can be explained in terms of the variation of the minimum load bearing cross-sectional area of the aluminum matrix with U 3 O 8 concentration. The temperature dependence of σ sub(R) and σ sub(E) of the cermets was seen to be similar to the temperature dependence of these parameters of the aluminum matrix. (Author) [pt

  9. Zirconia-hydroxyapatite composite material with micro porous structure.

    Science.gov (United States)

    Matsumoto, Takuya Junior; An, Sang-Hyun; Ishimoto, Takuya; Nakano, Takayoshi; Matsumoto, Takuya; Imazato, Satoshi

    2011-11-01

    Titanium plates and apatite blocks are commonly used for restoring large osseous defects in dental and orthopedic surgery. However, several cases of allergies against titanium have been recently reported. Also, sintered apatite block does not possess sufficient mechanical strength. In this study, we attempted to fabricate a composite material that has mechanical properties similar to biocortical bone and high bioaffinity by compounding hydroxyapatite (HAp) with the base material zirconia (ZrO(2)), which possesses high mechanical properties and low toxicity toward living organisms. After mixing the raw material powders at several different ZrO(2)/HAp mixing ratios, the material was compressed in a metal mold (8 mm in diameter) at 5 MPa. Subsequently, it was sintered for 5 h at 1500°C to obtain the ZrO(2)/HAp composite. The mechanical property and biocompatibility of materials were investigated. Furthermore, osteoconductivity of materials was investigated by animal studies. A composite material with a minute porous structure was successfully created using ZrO(2)/HAp powders, having different particle sizes, as the starting material. The material also showed high protein adsorption and a favorable cellular affinity. When the mixing ratio was ZrO(2)/HAp=70/30, the strength was equal to cortical bone. Furthermore, in vivo experiments confirmed its high osteoconductivity. The composite material had strength similar to biocortical bones with high cell and tissue affinities by compounding ZrO(2) and HAp. The ZrO(2)/HAp composite material having micro porous structure would be a promising bone restorative material. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  10. Evaluation of porous gradient hydroxyapatite/zirconia composites for repair of lumbar vertebra defect in dogs.

    Science.gov (United States)

    Shao, Rong-Xue; Quan, Ren-Fu; Huang, Xiao-Long; Wang, Tuo; Xie, Shang-Ju; Gao, Huan-Huan; Wei, Xi-Cheng; Yang, Di-Sheng

    2016-04-01

    To evaluate the effects of porous gradient composites with hydroxyapatite/zirconia and autologous iliac in repair of lumbar vertebra body defects in dogs. (1) New porous gradient hydroxyapatite/zirconia composites were prepared using foam immersion, gradient compound and high temperature sintering; (2) A total of 18 adult beagle dogs, aged five to eight months and weighted 10-13 kg, were randomly assigned into two subgroups, which were implanted with new porous gradient hydroxyapatite/zirconia composites (subgroup A in 12) or autologous iliac bone (subgroup B in 6); (3) The post-operative data were analyzed and compared between the subgroups to repair the vertebral body defect by roentgenoscopy, morphology and biomechanics. The porosity of new porous gradient hydroxyapatite/zirconia composites is at 25 poles per inch, and the size of pores is at between 150 and 300 µm. The post-operative roentgenoscopy displayed that new-bone formation is increased gradually, and the interface between composites and host-bone becomes became blur, and the new-bone around the composites were integrated into host-bone at 24 weeks postoperatively in subgroup A. As to subgroup B, the resorption and restructure were found at six weeks after the surgery, and the graft-bone and host-bone have been integrated completely without obvious boundary at 24 weeks postoperatively. Histomorphologic study showed that the amount of bone within pores of the porous gradient hydroxyapatite/zirconia composites increased continuously with a prolonged implantation time, and that partial composites were degradated and replaced by new-bone trabeculae. There was no significant difference between subgroups (P > 0.05) in the ultimate compressive strengths. New porous gradient hydroxyapatite/zirconia composites can promote the repair of bony defect, and induce bone tissue to ingrow into the pores, which may be applied widely to the treatment of bony defect in the future. © The Author(s) 2016.

  11. Stereological observations of platelet-reinforced mullite- and zirconia-matrix composites

    International Nuclear Information System (INIS)

    Cherian, I.K.; Kriven, W.M.; Lehigh, M.D.; Nettleship, I.

    1996-01-01

    Recently, the effect of solid inclusions on the sintering of ceramic powders has been explained in terms of a back-stress that opposes densification. Several analyses have been proposed to describe this problem. However, little quantitative information exists concerning the effect of reinforcement on microstructural evolution. This study compares the microstructural development of zirconia and mullite matrices in the presence of alumina platelets. The effect of platelet loading on density is similar for both composites. Quantitative stereological examinations reveal that the average grain size and pore size are finer for the zirconia-matrix composite. The platelet loading does not have any noticeable effect on the average grain size of the matrix in either composite. However, the average pore size increases as the volume fraction of platelets increases for both materials. Contiguity measurements have detected some aggregation of platelets in the zirconia-matrix composite

  12. Effect of surface treatments on the bond strengths of facing composite resins to zirconia copings.

    Science.gov (United States)

    Tsumita, M; Kokubo, Y; Kano, T

    2012-09-01

    The present study evaluated and compared the bond strength between zirconia and facing composite resin using different surface conditioning methods before and after thermocycling. Four primers, three opaque resins, and two facing composite resins were used, and 10 surface treatment procedures were conducted. The bond strength was measured before and after 4,000 cycles of thermocycling. The mean values of each group were statistically analyzed using one-way analysis of variance (ANOVA). The bond strengths of facing composite resins to zirconia after various treatments varied depending on the primers, opaque resins, body resins, and thermocycling. The application of primers and opaque resins to the zirconia surface after sandblasting is expected to yield strong bond strength of the facing composite resin (Estenia CG&B) even after thermocycling.

  13. Mechanical and Thermal Properties of Epoxy Composites Containing Zirconia-Impregnated Halloysite Nanotubes with Different Loadings.

    Science.gov (United States)

    Kim, Suhyun; Kim, Moon Il; Shon, Minyoung; Seo, Bongkuk; Lim, Choongsun

    2018-09-01

    Epoxy resins are widely used in various industrial fields due to their low cost, good workability, heat resistance, and good mechanical strength. However, they suffer from brittleness, an issue that must be addressed for further applications. To solve this problem, additional fillers are needed to improve the mechanical and thermal properties of the resins; zirconia is one such filler. However, it has been reported that aggregation may occur in the epoxy composites as the amount of zirconia increases, preventing enhancement of the mechanical strength of the epoxy composites. Herein, to reduce the aggregation, zirconia was well dispersed on halloysite nanotubes (HNTs), which have high thermal and mechanical strength, by a conventional wet impregnation method. The HNTs were impregnated with zirconia at different loadings using zirconyl chloride octahydrate as a precursor. The mechanical and thermal strengths of the epoxy composites with these fillers were investigated. The zirconia-impregnated HNTs (Zr/HNT) were characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and tunneling electron microscopy (TEM). The hardening conditions of the epoxy composites were analyzed by differential scanning calorimetry (DSC). The thermal strength of the epoxy composites was studied by thermomechanical analysis (TMA) and micro-calorimetry and the mechanical strength of the epoxy composites (flexural strength and tensile strength) was studied by using a universal testing machine (UTM). The mechanical and thermal strengths of the epoxy composites with Zr/HNT were improved compared to those of the epoxy composite with HNT, and also increased as the zirconia loading on HNT increased.

  14. Ultrastructural Analysis and Long-term Evaluation of Composite-Zirconia Bond Strength.

    Science.gov (United States)

    Aboushelib, Moustafa N; Ragab, Hala; Arnaot, Mohamed

    2018-01-01

    To evaluate the influence of different aging techniques on zirconia-composite microtensile bond strength using different surface treatments over a 5-year follow-up period. Zirconia disks received three surface treatments: airborne-particle abrasion with 50-μm aluminum oxide particles, selective infiltration etching (SIE), or fusion sputtering (FS). The specimens were bonded to pre-aged composite disks using a composite cement containing phosphate monomers (Panavia F2.0). Bonded specimens were sectioned into microbars (1 x 1 x 6 mm) using a precision cutting machine, and all microbars received thermocycling (15,000 cycles between 5°C and 55°C). Initial microtensile bond strength was evaluated, and the test was repeated after storage in the following media for five years (artificial saliva, 20% ethanol, 5% NaOH, 4% acetic acid, and 5% phosphoric acid). The test was repeated every 12 months for 5 years. Scanning electron microscopic images were used to analyze the zirconia-composite interface. A repeated measures ANOVA and Bonferroni post-hoc tests were used to analyze the data (n = 20, α = 0.05). Significantly higher microtensile bond strength was observed for SIE compared to fusion sputtering and airborne particle abrasion. Five years of artificial aging resulted in significant reduction of zirconia-composite bond strength for all tested specimens. Zirconia-composite bond strength was more sensitive to storage in sodium hydroxide and phosphoric acid, while it was least affected when stored under saliva. These changes were related to the mechanism of ultra-structural interaction between surface treatment and adhesive, as deterioration of the hybrid layer (composite-infiltrated ceramic) was responsible for bond degeneration. Zirconia-composite bond strength was influenced by 5 years of artificial aging.

  15. Compressive fracture resistance of the marginal ridge in large Class II tunnels restored with cermet and composite resin.

    Science.gov (United States)

    Ehrnford, L E; Fransson, H

    1994-01-01

    Compressive fracture resistance of the marginal ridge was studied in large tunnel preparations, before and after restoration with cermet (Ketac Silver, ESPE), a universal hybrid composite (Superlux, DMG) and an experimental composite. Each group was represented by six tunnels in extracted upper premolars. The tunnels were prepared by the use of round burs up to size #6. Remaining ridge width was 1.5 mm and ridge height 1.7 mm in the contact area. The ridge was loaded to fracture by a rod placed perpendicular to the ridge. Generally this resulted in a shear fracture of the restoration. There was no significant reinforcement of the ridge by the cermet whereas the composites both reinforced by the same magnitude, averaging 62%. It was concluded that the ridge could be considered a "megafiller" where contact need to be preserved and contour protected against proximal and occlusal wear of the restoration. Clinically there would therefore be good reasons to save even ridge areas with very low inherent strength. Based on the present study composite resin might therefore be the filling material of choice for such tunnel preparations.

  16. Effect of zirconia content and powder processing mechanical properties of gelcasted ZTA composite

    International Nuclear Information System (INIS)

    Khoshkalam, M.; Faghihi-Sani, M.A.; Nojoomi, A.

    2013-01-01

    Addition of fine zirconia particles in the alumina matrix in order to produce ZTA composite is a well-known method for improving the mechanical properties of alumina ceramics such as flexural strength and fracture toughness. Increasing homogeneity and reducing alumina grain size are two key factors for achieving proper mechanical properties in this ceramic matrix composite. In this work two batches of ZTA powder precursor were prepared through mixing of alumina and zirconia by ball milling and in situ synthesis of ZTA composite via solution combustion method. The bending strength testing samples were fabricated through gel-casting process. The effects of different powder processing methods as well as zirconia contents on microstructural homogeneity and mechanical properties of ZTA composites were investigated. The samples produced by solution combustion synthesized powder yielded higher homogeneity, finer microstructure and higher flexural strength. Results showed an upswing in the fracture toughness for the synthesized samples even up to 20 vol% zirconia, while the mixed samples depicted optimum fracture toughness in 10 vol% zirconia content. (author)

  17. Shrinkage reduction of dental composites by addition of expandable zirconia filler

    DEFF Research Database (Denmark)

    Skovgaard, M.; Almdal, Kristoffer; Sørensen, Bent F.

    2011-01-01

    . The shrinkage of the composite was calculated from density measurements using Archimedes method. The rate of the phase transformation in resin was measured by determining the volume fraction of monoclinic zirconia (vm). The composite had a vm of 0.5 after 8 h of water storage. The overall shrinkage...

  18. Zirconia-mullite obtained from co-precipitated zirconia-mullite composite powders by SPS

    Energy Technology Data Exchange (ETDEWEB)

    Li, H.Z.; Li, Z.J.; Luo, X.D. [Univ. of Science and Technology Liaoning, Anshan (China). School of High Temperature Materials and Magnesium Resource Engineering; Gui, J.Y.; Xie, Z.P. [Tsinghua Univ., Beijing (China). School of Materials Science and Engineering

    2016-07-01

    The co-precipitation method is used to fabricate precursor powder. This powder is densified by means of the spark plasma sintering (SPS) technique at 1500 C with a holding time of 7 min to prepare zirconia-mullite samples. Their density measures up to 97 % of the theoretical density, and the sintered mullite compacts exhibit better strength properties (289 ± 12 MPa) and H{sub v} (9.99 GPa). The mode of fracture is changed with the addition of ZrO{sub 2} and extensive fine cleavages are observed on the grain surface. These cleavages join together to form steps, which can absorb more energy. The flexural strength of the samples is almost double that of pure mullite, which is related to the formation of cleavages.

  19. Study on Ablation Behavior of Phenolic Composites Prepared with Different Amounts of Zirconia and Asbestos Fiber

    Directory of Open Access Journals (Sweden)

    Mir Asad Mirzapour

    2012-12-01

    Full Text Available Ablative materials play a strategic role in aerospace industry. These materialsproduce a thermal protection system which protects the structure, theaerodynamic surfaces and the payload of vehicles and probes duringhypersonic flight through a planetary atmosphere. In this work, we investigated the effect of refractory zirconium oxide on mechanical, heat stability and ablation properties of asbestos/phenolic/zirconia composites. The asbestos/phenolic/zirconia composites were produced with different percentages of zirconia filler from 7 to 21% with average size of 7 μm and different number of layers of asbestos, say 3 to 6 layers. These ablative composites were made by an autoclave curing cycle process.The densities of the composites were in the range of 1.68 to 1.88 g/cm3. Ablation properties of composites were determined by oxy-acetylene torch environment and burn-through time, erosion rates and back surface temperature in the first required 20 seconds. Thermal stability of the produced materials was estimated by means of thermal gravimetric analysis, in both air and nitrogen which consisted of dynamic scans at a heating rate of 10°C/min from 30 to 1000°C with bulk samples of about 20±1 mg. The results showed that when the amount of zirconia was raised from 7% to 21%, the erosion rate and the back surface temperature of composites increased byabout 24% and 26% respectively, and the heat capacity of the composites increased by about 85%. Also, the result showed that when the thickness of composites of 4.2 mm was increased to 10.1mm the burn-through time raised by about 226% and erosion rate dropped by about 41%. These composites displayed the maximum flexural strength when the amount of zirconia was about 14%.

  20. Prognosis and comparison of performances of composite CERCER and CERMET fuels dedicated to transmutation of TRU in an EFIT ADS

    Science.gov (United States)

    Sobolev, V.; Uyttenhove, W.; Thetford, R.; Maschek, W.

    2011-07-01

    The neutronic and thermomechanical performances of two composite fuel systems: CERCER with (Pu,Np,Am,Cm)O 2-x fuel particles in ceramic MgO matrix and CERMET with metallic Mo matrix, selected for transmutation of minor actinides in the European Facility for Industrial Transmutation (EFIT), were analysed aiming at their optimisation. The ALEPH burnup code system, based on MNCPX and ORIGEN codes and JEFF3.1 nuclear data library, and the modern version of the fuel rod performance code TRAFIC were used for this analysis. Because experimental data on the properties of the mixed minor-actinide oxides are scarce, and the in-reactor behaviour of the T91 steel chosen as cladding, as well as of the corrosion protective layer, is still not well-known, a set of "best estimates" provided the properties used in the code. The obtained results indicate that both fuel candidates, CERCER and CERMET, can satisfy the fuel design and safety criteria of EFIT. The residence time for both types of fuel elements can reach about 5 years with the reactivity swing within ±1000 pcm, and about 22% of the loaded MA is transmuted during this period. However, the fuel centreline temperature in the hottest CERCER fuel rod is close to the temperature above which MgO matrix becomes chemically instable. Moreover, a weak PCMI can appear in about 3 years of operation. The CERMET fuel can provide larger safety margins: the fuel temperature is more than 1000 K below the permitted level of 2380 K and the pellet-cladding gap remains open until the end of operation.

  1. Long-term Bond Strength between Layering Indirect Composite Material and Zirconia Coated with Silicabased Ceramics.

    Science.gov (United States)

    Fushiki, Ryosuke; Komine, Futoshi; Honda, Junichi; Kamio, Shingo; Blatz, Markus B; Matsumura, Hideo

    2015-06-01

    This study evaluated the long-term shear bond strength between an indirect composite material and a zirconia framework coated with silica-based ceramics, taking the effect of different primers into account. A total of 165 airborne-particle abraded zirconia disks were subjected to one of three pretreatments: no pretreatment (ZR-AB), airborne-particle abrasion of zirconia coated with feldspathic porcelain (ZR-PO-AB), and 9.5% hydrofluoric acid etching of zirconia coated with feldspathic porcelain (ZR-PO-HF). An indirect composite material (Estenia C&B) was then bonded to the zirconia disks after they were treated with one of the following primers: Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB + Activator), Estenia Opaque Primer (EOP), Porcelain Liner M Liquid B (PLB), or no priming (CON, control group). Shear bond strength was tested after 100,000 thermocycles, and the data were analyzed using the Steel-Dwass U-test (α = 0.05). For ZR-PO-AB and ZR-PO-HF specimens, bond strength was highest in the CPB+Activator group (25.8 MPa and 22.4 MPa, respectively). Bond strengths were significantly lower for ZR-AB specimens in the CON and PLB groups and for ZR-PO-AB specimens in the CON, CPB, and EOP groups. Combined application of a hydrophobic phosphate monomer (MDP) and silane coupling agent enhanced the long-term bond strength of indirect composite material to a zirconia coated with silica-based ceramics.

  2. Production of mullite-zirconia ceramics composites by 'In situ' reaction

    International Nuclear Information System (INIS)

    Melo, F.C.L. de; Cairo, C.A.A.; Piorino Neto, F.; Devezas, T.C.

    1987-01-01

    Mullita-zirconia ceramic composites were produced by 'In situ' reaction of alumina and brazilian zircon. The ideal curve of thermal treatment (reaction + sinterization) was determined for the obtention of composites of maximum mechanical resistence. The retained fraction of tetragonal fase was evaluated by X-ray difraction and correlated with the values of mechanical resistence obtained by different treatment curves. The performance of the developed composites under corrosion and thermal shock was evaluated by glass casting. (Author) [pt

  3. Characterization of Mullite-Zirconia Composite Processed by Non-Transferred and Transferred Arc Plasma

    International Nuclear Information System (INIS)

    Yugeswaran, S.; Selvarajan, V.; Lusvarghi, L.; Tok, A. I. Y.; Krishna, D. Siva Rama

    2009-01-01

    The arc plasma melting technique is a simple method to synthesize high temperature reaction composites. In this study, mullite-zirconia composite was synthesized by transferred and non-transferred arc plasma melting, and the results were compared. A mixture of alumina and zircon powders with a mole ratio of 3: 2 were ball milled for four hours and melted for two minutes in the transferred and non-transferred mode of plasma arcs. Argon and air were used as plasma forming gases. The phase and microstructural formation of melted samples were investigated by X-ray diffraction (XRD) and scanning electron microscope (SEM). The microstructure of the composites was found to be affected by the mode of melting. In transferred arc melting, zirconia flowers with uniform lines along with mullite whiskers were obtained. In the case of non-transferred arc plasma melting, mullite whiskers along with star shape zirconia were formed. Differential thermal analysis (DTA) of the synthesized mullite-zirconia composites provided a deeper understanding of the mechanisms of mullite formation during the two different processes. (plasma technology)

  4. Alumina reinforced tetragonal zirconia (TZP) composites. Final technical report, July 1, 1993--December 31, 1996

    International Nuclear Information System (INIS)

    Shetty, D.K.

    1997-01-01

    This final technical report summarizes the significant research results obtained during the period July 1, 1993 through December 31, 1996 in the DOE-supported research project entitled, open-quotes Alumina Reinforced Tetragonal Zirconia (TZP) Compositesclose quotes. The objective of the research was to develop high-strength and high-toughness ceramic composites by combining mechanisms of platelet, whisker or fiber reinforcement with transformation toughening. The approach used included reinforcement of Celia- or yttria-partially-stabilized zirconia (Ce-TZP or Y-TZP) with particulates, platelets, or continuous filaments of alumina

  5. Thermo-mechanical properties of mullite/zirconia reinforced alumina ceramic composites

    International Nuclear Information System (INIS)

    Wahsh, M.M.S.; Khattab, R.M.; Awaad, M.

    2012-01-01

    Highlights: ► Alumina–mullite–zirconia ceramic composites were prepared from alumina and zircon. ► Constant amount of magnesia was added as a sintering aid. ► Mechanical properties were enhanced with increasing of zircon up to 30.52 mass%. ► All of ceramic composites were achieved excellent thermal shock resistance. -- Abstract: Alumina–mullite–zirconia ceramic composites were prepared by reaction bonding of alumina and zircon mixtures after firing at different temperatures 1300°, 1400° and 1500 °C. Constant amount of magnesia was added as a sintering aid. The technological parameters of the sintered ceramic composites, i.e. the mechanical properties and densification parameter as well as thermal shock resistance, have been investigated. The phase compositions and microstructure of the sintered ceramic composites were detected by using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Results indicated that alumina–mullite–zirconia ceramic composites fired at 1500 °C for 2 h were achieved a good densification parameters and mechanical properties as well as excellent thermal shock resistance. In addition, these ceramic composites were showed enhancement in Vickers’ microhardness and fracture toughness values.

  6. Cermet cements.

    Science.gov (United States)

    McLean, J W

    1990-01-01

    Cermet ionomer cements are sintered metal/glass powders, which can be made to react with poly(acids). These new cements are significantly more resistant to abrasion than regular glass ionomer cements and are widely accepted as core build-up materials and lining cements. They can strengthen teeth and provide the clinician with an opportunity to treat early dental caries.

  7. A short and long range study of mullite-zirconia-zircon composites

    Energy Technology Data Exchange (ETDEWEB)

    Rendtorff, Nicolas M.; Conconi, Maria S.; Aglietti, Esteban F. [Centro de Tecnologia de Recursos Minerales y Ceramica (CETMIC: CONICET-CIC) (Argentina); Chain, Cecilia Y.; Pasquevich, Alberto F. [Universidad Nacional de La Plata, Departamento de Fisica, IFLP, Facultad de Ciencias Exactas (Argentina); Rivas, Patricia C. [CONICET (Argentina); Martinez, Jorge A., E-mail: toto@fisica.unlp.edu.ar; Caracoche, Maria C. [Universidad Nacional de La Plata, Departamento de Fisica, IFLP, Facultad de Ciencias Exactas (Argentina)

    2010-06-15

    In the field of refractory materials, ceramics containing mullite-zirconia are the basis of those most used in the industry of glass and steel. It is known that the addition of zircon improves the behavior of the refractory used in service. Knowing that some mullite-zirconia composites properties as fracture strength and the elastic modulus E are associated with the material microstructure integrity, the eventual thermal decomposition of zircon into zirconia and silica could seriously alter the material elastic properties. In this paper the phase content of a series of mullite-zirconia-zircon (3Al{sub 2}O{sub 3}.2SiO{sub 2}-ZrO{sub 2}-ZrSiO{sub 4}) composites is determined at atomic level via perturbed angular correlations (PAC) and compared with that derived from the long range X-ray diffraction technique. PAC results on the as-prepared materials indicate that all nominal zircon is present and that it involves two types of nanoconfigurations, one of them describing aperiodic regions. The thermomechanical properties already reported for these materials could be related to the crystalline to aperiodic zircon concentrations ratio they exhibit.

  8. Electrodeposition of metals and metal/cermet composites in low gravity

    Science.gov (United States)

    Riley, Clyde; Coble, Dwain; Maybee, George

    1987-01-01

    Electrodeposition experiments were carried out on the bench and a KC-135 aircraft at 0.01 g in anticipation of microgravity flights on NASA's Space Transportation System Shuttle. Experimental results obtained by interferometry compare concentration gradients as a function of time in the vicinity of a reducing electrode (cathode) for Cu(+2) and Co(+2) electrodeposition cells. No difference was found between bench and 0.01 g produced gradients for a .1M CuSO4 cell, but a significant difference was noted between the gradients in a 1M CoSO4 cell even though the bench cells were operated in a nonconvecting shielded (cathode over anode) mode. The gradient for Co(+2) depletion produced at 0.01 g was greater and the entire layer was thicker than found on the bench. Neutral buoyancy/matched density codeposition experiments were performed on the bench in an attempt to physically duplicate the results of metal/cermet codepositions in microgravity. Polystyrene spheres with average diameter 11.8 microns and density approximately matching that of 1M CoSO4 were utilized to emulate nonsedimenting cermets in microgravity. The cells were operated in a shielded convectionless mode. Comparison with literature data on codeposition with stirred cells indicate significant improvement in volume percent neutral occluded in the depositing metal matrix. A multicell electrodeposition flight apparatus that has been designed, constructed and is undergoing testing is discussed.

  9. Rugometric and microtopographic non-invasive inspection in dental-resin composites and zirconia ceramics

    Science.gov (United States)

    Fernández-Oliveras, Alicia; Costa, Manuel F. M.; Pecho, Oscar E.; Rubiño, Manuel; Pérez, María. M.

    2013-11-01

    Surface properties are essential for a complete characterization of biomaterials. In restorative dentistry, the study of the surface properties of materials meant to replace dental tissues in an irreversibly diseased tooth is important to avoid harmful changes in future treatments. We have experimentally analyzed the surface characterization parameters of two different types of dental-resin composites and pre-sintered and sintered zirconia ceramics. We studied two shades of both composite types and two sintered zirconia ceramics: colored and uncolored. Moreover, a surface treatment was applied to one specimen of each dental-resin. All the samples were submitted to rugometric and microtopographic non-invasive inspection with the MICROTOP.06.MFC laser microtopographer in order to gather meaningful statistical parameters such as the average roughness (Ra), the root-mean-square deviation (Rq), the skewness (Rsk), and the kurtosis of the surface height distribution (Rku). For a comparison of the different biomaterials, the uncertainties associated to the surface parameters were also determined. With respect to Ra and Rq, significant differences between the composite shades were found. Among the dental resins, the nanocomposite presented the highest values and, for the zirconia ceramics, the pre-sintered sample registered the lowest ones. The composite performance may have been due to cluster-formation variations. Except for the composites with the surface treatment, the sample surfaces had approximately a normal distribution of heights. The surface treatment applied to the composites increased the average roughness and moved the height distribution farther away from the normal distribution. The zirconia-sintering process resulted in higher average roughness without affecting the height distribution.

  10. Microstructure and phase composition of sputter-deposited zirconia-yttria films

    International Nuclear Information System (INIS)

    Knoll, R.W.; Bradley, E.R.

    1983-11-01

    Thin ZrO 2 -Y 2 O 3 coatings ranging in composition from 3 to 15 mole % Y 2 O 3 were produced by rf sputter deposition. This composition range spanned the region on the equilibrium ZrO 2 -Y 2 O 3 phase diagram corresponding to partially stabilized zirconia (a mixture of tetragonal ZrO 2 and cubic solid solution). Microstructural characteristics and crystalline phase composition of as-deposited and heat treated films (1100 0 C and 1500 0 C) were determined by transmission electron microscopy (TEM) and by x-ray diffraction (XRD). Effects of substrate bias (0 approx. 250 volts), which induced ion bombardment of the film during growth, were also studied. The as-deposited ZrO 2 -Y 2 O 3 films were single phase over the composition range studied, and XRD data indicated considerable local atomic disorder in the lattice. Films produced at low bias contained intergranular voids, pronounced columnar growth, and porosity between columns. At high bias, the microstructure was denser, and films contained high compressive stress. After heat treatment, all deposits remained single phase, therefore a microstructure and precipitate distribution characteristic of toughened, partially stabilized zirconia appear to be difficult to achieve in vapor deposited zirconia coatings

  11. Zirconia toughened SiC whisker reinforced alumina composites small business innovation research

    Science.gov (United States)

    Loutfy, R. O.; Stuffle, K. L.; Withers, J. C.; Lee, C. T.

    1987-01-01

    The objective of this phase 1 project was to develop a ceramic composite with superior fracture toughness and high strength, based on combining two toughness inducing materials: zirconia for transformation toughening and SiC whiskers for reinforcement, in a controlled microstructure alumina matrix. The controlled matrix microstructure is obtained by controlling the nucleation frequency of the alumina gel with seeds (submicron alpha-alumina). The results demonstrate the technical feasibility of producing superior binary composites (Al2O3-ZrO2) and tertiary composites (Al2O3-ZrO2-SiC). Thirty-two composites were prepared, consolidated, and fracture toughness tested. Statistical analysis of the results showed that: (1) the SiC type is the key statistically significant factor for increased toughness; (2) sol-gel processing with a-alumina seed had a statistically significant effect on increasing toughness of the binary and tertiary composites compared to the corresponding mixed powder processing; and (3) ZrO2 content within the range investigated had a minor effect. Binary composites with an average critical fracture toughness of 6.6MPam sup 1/2, were obtained. Tertiary composites with critical fracture toughness in the range of 9.3 to 10.1 MPam sup 1/2 were obtained. Results indicate that these composites are superior to zirconia toughened alumina and SiC whisker reinforced alumina ceramic composites produced by conventional techniques with similar composition from published data.

  12. Superplastic flow of two-phase ceramics containing rigid inclusions-zirconia/mullite composites

    International Nuclear Information System (INIS)

    Yoon, C.K.; Chen, I.W.

    1990-01-01

    A continuum theory for non-newtonian flow of a two-phase composite containing rigid inclusions is presented. It predicts flow suppression by a factor of (1 - V) q , where V is the volume fraction of the rigid inclusion and q depends on the stress exponent and the inclusion shape. Stress concentrations in the rigid inclusion have also been evaluated. As the stress exponent increases, flow suppression is more pronounced even though stress concentration is less severe. To test this theory, superplastic flow of zirconia/mullite composites, in which zirconia is a soft, non-Newtonian super-plastic matrix and mullite is a rigid phase of various size, shape, and amount, is studied. The continuum theory is found to describe the two-phase superplastic flow reasonably well

  13. Hydroxyapatite/zirconia-microfibre composites with controlled microporosity and fracture properties prepared by electrophoretic deposition

    Czech Academy of Sciences Publication Activity Database

    Drdlík, D.; Sláma, M.; Hadraba, Hynek; Cihlář, J.

    2015-01-01

    Roč. 41, č. 9 (2015), s. 11202-11212 ISSN 0272-8842 R&D Projects: GA ČR(CZ) GAP108/11/1644; GA MŠk(CZ) ED1.1.00/02.0068 Institutional support: RVO:68081723 Keywords : hydroxyapatite * zirconia * composite * electrophoretic deposition * porosity Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 2.758, year: 2015

  14. Effect of composition on the degree of anisotropy of thermal expansion and electric resistance of cermet specimens of GeTe

    International Nuclear Information System (INIS)

    Barbakadze, K.G.; Vekua, T.S.; Ioseliani, M.I.; Kvitsiniya, K.M.

    1988-01-01

    A study was made on α temperature coefficient of thermal expansion and ρ specific electric resistance of cermet germanium telluride for alloys close to stoichiometric composition. It is shown that anisotropy of thermal expansion of cermet germanium telluride depends sufficiently on its composition. This dependence is clearly pronounced if tellurium content in alloys equals 50.4-51.2 at.%. The maximal anisotropy is observed in the alloy containing 50.8 at.% of tellurium. The temperature of extreme value of temperature coefficient of linear expansion decreases from 440 down to 373 deg.C for alloys with 49-50.8 at.% of tellurium, and grows from 373 up to 405 deg.C if tellurium content equals 50.8-52 at.%

  15. The effect of various primers on shear bond strength of zirconia ceramic and resin composite.

    Science.gov (United States)

    Sanohkan, Sasiwimol; Kukiattrakoon, Boonlert; Larpboonphol, Narongrit; Sae-Yib, Taewalit; Jampa, Thibet; Manoppan, Satawat

    2013-11-01

    To determine the in vitro shear bond strengths (SBS) of zirconia ceramic to resin composite after various primer treatments. Forty zirconia ceramic (Zeno, Wieland Dental) specimens (10 mm in diameter and 2 mm thick) were prepared, sandblasted with 50 μm alumina, and divided into four groups (n = 10). Three experimental groups were surface treated with three primers; CP (RelyX Ceramic Primer, 3M ESPE), AP (Alloy Primer, Kuraray Medical), and MP (Monobond Plus, Ivoclar Vivadent AG). One group was not treated and served as the control. All specimens were bonded to a resin composite (Filtek Supreme XT, 3M ESPE) cylinder with an adhesive system (Adper Scotchbond Multi-Purpose Plus Adhesive, 3M ESPE) and then stored in 100% humidity at 37°C for 24 h before SBS testing in a universal testing machine. Mean SBS (MPa) were analyzed with one-way analysis of variance (ANOVA) and the Tukey's Honestly Significant Difference (HSD) test (α = 0.05). Group AP yielded the highest mean and standard deviation (SD) value of SBS (16.8 ± 2.5 MPa) and Group C presented the lowest mean and SD value (15.4 ± 1.6 MPa). The SBS did not differ significantly among the groups (P = 0.079). Within the limitations of this study, the SBS values between zirconia ceramic to resin composite using various primers and untreated surface were not significantly different.

  16. Synthesis of mesh-shaped calcia partially stabilized zirconia using eggshell membrane template as filler composite

    Directory of Open Access Journals (Sweden)

    Gema Gempita

    2017-08-01

    Full Text Available This experiment was conducted experimentally to synthesize Calcia Partially Stabilized Zirconia (Ca-PSZ by sol-gel method using eggshell membrane template as a composite filler. The eggshell membrane was used to produce a mesh shaped structure, which hopefully can improve the mechanical properties of the composite. Ca-PSZ filler was synthesized from ZrOCl2 precursor and Ca(NO32 stabilizer with a 24 hours immersion time. Ca-PSZ of synthesis then mixed with the resin matrix to test its composite hardness. The EDS characterization results suggested that the sample contained elements of zirconia, calcium, and oxygen. Whereas, the XRD characterization identified that crystal structures that formed in the sample were nano scale tetragonal. Characterization of SEM showed Ca-PSZ with mesh structured. The average composite hardness value was 15.79 VHN. The composites with Ca-PSZ-synthesized filler could be prepared and its hardness value was higher than the composite with Ca-PSZ filler in spherical particles, but the hardness was still below the composite on the market.

  17. Solar Absorptance of Cermet Coatings Evaluated

    Science.gov (United States)

    Jaworske, Donald A.

    2004-01-01

    Cermet coatings, molecular mixtures of metal and ceramic, are being considered for the heat inlet surface of solar Stirling convertors. In this application, the key role of the cermet coating is to absorb as much of the incident solar energy as possible. To achieve this objective, the cermet coating has a high solar absorptance value. Cermet coatings are manufactured utilizing sputter deposition, and many different metal and ceramic combinations can be created. The ability to mix metal and ceramic at the atomic level offers the opportunity to tailor the composition, and hence, the optical properties of these coatings. The NASA Glenn Research Center has prepared and characterized a wide variety of cermet coatings utilizing different metals deposited in an aluminum oxide ceramic matrix. In addition, the atomic oxygen durability of these coatings has been evaluated.

  18. Preparation and characterization of porous alumina-zirconia composite ceramics

    Czech Academy of Sciences Publication Activity Database

    Pabst, W.; Gregorová, E.; Sedlářová, I.; Černý, Martin

    2011-01-01

    Roč. 31, č. 14 (2011), s. 2721-2731 ISSN 0955-2219. [International Conference on Ceramic Processing Science /11./. Zürich, 29.08.2010-01.09.2010] Institutional research plan: CEZ:AV0Z30460519 Keywords : sintering * slip casting * composites Subject RIV: JI - Composite Materials Impact factor: 2.353, year: 2011

  19. Grain size influence on residual stresses in alumina/zirconia composites

    International Nuclear Information System (INIS)

    Sergo, V.; Sbaizero, O.; Pezzotti, G.; Nishida, T.

    1998-01-01

    The grain size (GS) and volume fraction of alumina have been systematically varied in composites with a zirconia matrix and the corresponding residual stresses have been assessed by means of piezospectroscopy. The compressive stress in alumina depends on the volume fraction and it is well predicted by a stochastic model based on information theory. No dependence with GS has been detected, except at the highest volume content (20% vol. alumina). Conversely the stress distribution is independent from the volume fraction and depends on GS: intermediate values of GS exhibit the wider stress distribution. The tensile stress in zirconia shows no clear correlation with the volume fraction and increases with increasing zirconia GS. This latter behavior has been compared with a model based on diffusion relaxation of stresses. The model reproduces correctly the stress change due to different alumina contents, but it diverges from the experimental data at smaller GSs, overestimating the residual stress. It is suggested that grain boundary sliding may also contribute to the relaxation of stresses

  20. The influence of precipitation temperature on the properties of ceria–zirconia solid solution composites

    International Nuclear Information System (INIS)

    Cui, Yajuan; Fang, Ruimei; Shang, Hongyan; Shi, Zhonghua; Gong, Maochu; Chen, Yaoqiang

    2015-01-01

    Highlights: • The crystallite size of precipitate increases as the precipitation temperature rises. • The stack of large crystallite can form nanoparticles with big pore size. • Big pore sizes are advantageous to improve the thermal stability. • Phase segregation is restricted in CZ solid solution precipitated at 70 °C. • The reducibility and OSC of the solid solution precipitated at 70 °C are improved. - Abstract: The ceria–zirconia composites (CZ) with a Ce/Zr mass ratio of 1/1 were synthesized by a back-titration method, in which the influence of precipitation temperature on the properties of ceria–zirconia precipitates was investigated. The resulting precipitation and mixed oxides at different precipitation temperatures were then characterized by a range of techniques, including textural properties, X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS), H 2 -temperature programmed reduction (H 2 -TPR) as well as oxygen storage capacity (OSC) measurement. The results revealed that ceria–zirconia composites were formed as solid solution and such structure is favored of thermostability and texture properties. In particular, the composite CZ-70 synthesized at 70 °C exhibited prominent thermostability with a surface area of 32 m 2 /g as well as a pore volume of 0.15 cc/g after aging treatment at 1000 °C for 5 h. And this was found to be associated with the wider pore size distribution which maybe owed to the formation of large crystal at the primary stage of precipitation. Additionally, the composite CZ-70 showed excellent reduction property and OSC benefiting from stable texture and structure

  1. Synthesis and ceramic processing of zirconia alumina composites for application as solid oxide fuel cell electrolytes

    International Nuclear Information System (INIS)

    Garcia, Rafael Henrique Lazzari

    2007-01-01

    The global warmness and the necessity to obtain clean energy from alternative methods than petroleum raises the importance of developing cleaner and more efficient systems of energy generation, among then, the solid oxide fuel cell (SOFC). Cubic stabilized zirconia (CSZ) has been the most studied material as electrolyte in SOFC, due to its ionic conductivity and great stability at operation conditions. However, its low fracture toughness difficulties its application as a thin layer, what could lead to an improvement of cell efficiency. In this sense, the alumina addition in CSZ forms a composite, which can shift its mechanical properties, without compromising its electrical properties. In this work, coprecipitation synthesis route and ceramic processing of zirconia-alumina composites were studied, in order to establish optimum conditions to attain high density, homogeneous microstructure, and better mechanical properties than CSZ, without compromising ionic conductivity. For this purpose, composites containing up to 40 wt % of alumina, in a 9 mol % yttria-stabilized zirconia (9Y-CSZ) matrix were evaluated. In order to optimize the synthesis of the composites, a preliminary study of powder obtaining and processing were carried out, at compositions containing 20 wt % of alumina, in 9Y-CSZ. The ceramic powders were characterized by helium picnometry, X-ray diffraction, scanning electronic microscopy, transmission electronic microscopy, thermogravimetry, differential scanning calorimetry, granulometry by laser diffraction and gas adsorption (BET). The characterization of sinterized compacts were performed by X-ray diffraction, scanning electron microscopy, optical microscopy, density measurements, Vickers indentation and impedance spectroscopy. The obtained results show that the alumina addition, in the 9Y-CSZ matrix powders, raises the specific surface area, promotes deagglomeration of powders and elevates the oxides crystallization temperature, requiring higher

  2. Efficacy of ceramic repair material on the bond strength of composite resin to zirconia ceramic.

    Science.gov (United States)

    Kirmali, Omer; Kapdan, Alper; Harorli, Osman Tolga; Barutcugil, Cagatay; Ozarslan, Mehmet Mustafa

    2015-01-01

    The aim of this study was to evaluate the shear bond strength of composite resin in five different repair systems. Sixty specimens (7 mm in diameter and 3 mm in height) of zirconia ceramic were fabricated. All specimen surfaces were prepared with a 30 µm fine diamond rotary cutting instrument with water irrigation for 10 s and dried with oil-free air. Specimens were then randomly divided into six groups for the following different intra-oral repair systems (n = 10): Group 1, control group; Group 2, Cojet system (3M ESPE, Seefeld, Germany); Group 3, Cimara® System (Voco, Cuxhaven, Germany); Group 4, Z-Prime Plus System (Bisco Inc., Schaumburg, IL); Group 5, Clearfil™ System (Kuraray, Osaka, Japan); and Group 6, Z-Bond System (Danville, CA). After surface conditioning, a composite resin Grandio (Voco, Cuxhaven, Germany) was applied to the zirconia surface using a cylindrical mold (5 mm in diameter and 3 mm in length) and incrementally filled up, according to the manufacturer's instructions of each intra-oral system. Each specimen was subjected to a shear load at a crosshead speed of 1 mm/min until fracture. One-way analysis of variance (ANOVA) and Tukey post-hoc tests were used to analyze the bond strength values. There were significant differences between Groups 2-6 and Group 1. The highest bond strength values were obtained with Group 2 (17.26 ± 3.22) and Group 3 (17.31 ± 3.62), while the lowest values were observed with Group 1 (8.96 ± 1.62) and Group 6 (12.85 ± 3.95). All repair systems tested increased the bond strength values between zirconia and composite resin that used surface grinding with a diamond bur.

  3. Oxidation-resistant cermet

    Science.gov (United States)

    Phillips, W. M.

    1977-01-01

    Chromium metal alloys and chromium oxide ceramic are combined to produce cermets with oxidation-resistant properties. Application of cermets includes use in hot corrosive environments requiring strong resistive materials.

  4. Thermochemical stability of zirconia-titanium nitride as mixed ionic-electronic composites

    DEFF Research Database (Denmark)

    Silva, P. S. M.; Esposito, V.; Marani, D.

    2018-01-01

    Dense zirconia (8% molar yttria-stabilized ZrO2)-titanium nitride (TiN) composites are fabricated to obtain mixed ionic-electronic conducting ceramic systems with high degree of electronic and thermal conductivity. The composites are consolidated by spark plasma sintering (SPS), starting from pure...... the composites, high electrical conductivity is attained. Samples exhibit metallic behavior, showing an unexpected percolation of TiN in the YSZ matrix for volume fraction ≤ 25 wt% (27 vol%). Chemical degradation and electrical properties of the compounds were monitored under oxidative (air) and inert (Ar...... transport properties of the composite can be tuned by both the relative volume fraction of phases and controlled oxidative treatments. Adjusting such parameters different electric behaviors were observed ranging from predominant electronic conductors, to temperature-independent resistivity...

  5. Analysis of tribological behaviour of zirconia reinforced Al-SiC hybrid composites using statistical and artificial neural network technique

    Science.gov (United States)

    Arif, Sajjad; Tanwir Alam, Md; Ansari, Akhter H.; Bilal Naim Shaikh, Mohd; Arif Siddiqui, M.

    2018-05-01

    The tribological performance of aluminium hybrid composites reinforced with micro SiC (5 wt%) and nano zirconia (0, 3, 6 and 9 wt%) fabricated through powder metallurgy technique were investigated using statistical and artificial neural network (ANN) approach. The influence of zirconia reinforcement, sliding distance and applied load were analyzed with test based on full factorial design of experiments. Analysis of variance (ANOVA) was used to evaluate the percentage contribution of each process parameters on wear loss. ANOVA approach suggested that wear loss be mainly influenced by sliding distance followed by zirconia reinforcement and applied load. Further, a feed forward back propagation neural network was applied on input/output date for predicting and analyzing the wear behaviour of fabricated composite. A very close correlation between experimental and ANN output were achieved by implementing the model. Finally, ANN model was effectively used to find the influence of various control factors on wear behaviour of hybrid composites.

  6. Anisotropic ionic conductivity observed in superplastically deformed yttria-stabilized zirconia/alumina composite

    International Nuclear Information System (INIS)

    Drennan, J.; Swain, M.V.; Badwal, S.P.S.

    1989-01-01

    Ionic conductivity measurements on a yttria-stabilized tetragonal zirconia polycrystal/alumina composite subjected to superplastic deformation demonstrate anisotropic character. Parallel to the pressing direction, the grain-boundary resistance to oxygen ion mobility is 25% to 30% higher than that measured perpendicular to the pressing direction. The same directional dependency on the volume conductivity is observed but is less pronounced, showing approximately a 9% difference. Microstructural evidence reveals an agglomeration and elongation of alumina particles perpendicular to the pressing direction, and it is suggested that this phenomenon restricts the passage of ions parallel to the compression direction, giving rise to the anisotropic nature of the conductivity measurements

  7. Wear properties of alumina/zirconia composite ceramics for joint prostheses measured with an end-face apparatus.

    Science.gov (United States)

    Morita, Yusuke; Nakata, Kenichi; Kim, Yoon-Ho; Sekino, Tohru; Niihara, Koichi; Ikeuchi, Ken

    2004-01-01

    While only alumina is applied to all-ceramic joint prostheses at present, a stronger ceramic is required to prevent fracture and chipping due to impingement and stress concentration. Zirconia could be a potential substitute for alumina because it has high strength and fracture toughness. However, the wear of zirconia/zirconia combination is too high for clinical use. Although some investigations on composite ceramics revealed that mixing of different ceramics was able to improve the mechanical properties of ceramics, there are few reports about wear properties of composite ceramics for joint prosthesis. Since acetabular cup and femoral head of artificial hip joint are finished precisely, they indicate high geometric conformity. Therefore, wear test under flat contact was carried out with an end-face wear testing apparatus for four kinds of ceramics: alumina monolith, zirconia monolith, alumina-based composite ceramic, and zirconia based composite ceramic. Mean contact pressure was 10 MPa and sliding velocity was 40 mm/s. The wear test continued for 72 hours and total sliding distance was 10 km. After the test, the wear factor was calculated. Worn surfaces were observed with a scanning electron micrograph (SEM). The results of this wear test show that the wear factors of the both composite ceramics are similarly low and their mechanical properties are much better than those of the alumina monolith and the zirconia monolith. According to these results, it is predicted that joint prostheses of the composite ceramics are safer against break down and have longer lifetime compared with alumina/alumina joint prostheses.

  8. Demonstration of Subscale Cermet Fuel Specimen Fabrication Approach Using Spark Plasma Sintering and Diffusion Bonding

    Science.gov (United States)

    Barnes, Marvin W.; Tucker, Dennis S.; Benensky, Kelsa M.

    2018-01-01

    Nuclear thermal propulsion (NTP) has the potential to expand the limits of human space exploration by enabling crewed missions to Mars and beyond. The viability of NTP hinges on the development of a robust nuclear fuel material that can perform in the harsh operating environment (> or = 2500K, reactive hydrogen) of a nuclear thermal rocket (NTR) engine. Efforts are ongoing to develop fuel material and to assemble fuel elements that will be stable during the service life of an NTR. Ceramic-metal (cermet) fuels are being actively pursued by NASA Marshall Space Flight Center (MSFC) due to their demonstrated high-temperature stability and hydrogen compatibility. Building on past cermet fuel development research, experiments were conducted to investigate a modern fabrication approach for cermet fuel elements. The experiments used consolidated tungsten (W)-60vol%zirconia (ZrO2) compacts that were formed via spark plasma sintering (SPS). The consolidated compacts were stacked and diffusion bonded to assess the integrity of the bond lines and internal cooling channel cladding. The assessment included hot hydrogen testing of the manufactured surrogate fuel and pure W for 45 minutes at 2500 K in the compact fuel element environmental test (CFEET) system. Performance of bonded W-ZrO2 rods was compared to bonded pure W rods to access bond line integrity and composite stability. Bonded surrogate fuels retained structural integrity throughout testing and incurred minimal mass loss.

  9. Solid solution lithium alloy cermet anodes

    Science.gov (United States)

    Richardson, Thomas J.

    2013-07-09

    A metal-ceramic composite ("cermet") has been produced by a chemical reaction between a lithium compound and another metal. The cermet has advantageous physical properties, high surface area relative to lithium metal or its alloys, and is easily formed into a desired shape. An example is the formation of a lithium-magnesium nitride cermet by reaction of lithium nitride with magnesium. The reaction results in magnesium nitride grains coated with a layer of lithium. The nitride is inert when used in a battery. It supports the metal in a high surface area form, while stabilizing the electrode with respect to dendrite formation. By using an excess of magnesium metal in the reaction process, a cermet of magnesium nitride is produced, coated with a lithium-magnesium alloy of any desired composition. This alloy inhibits dendrite formation by causing lithium deposited on its surface to diffuse under a chemical potential into the bulk of the alloy.

  10. Towards long lasting zirconia-based composites for dental implants: Transformation induced plasticity and its consequence on ceramic reliability.

    Science.gov (United States)

    Reveron, Helen; Fornabaio, Marta; Palmero, Paola; Fürderer, Tobias; Adolfsson, Erik; Lughi, Vanni; Bonifacio, Alois; Sergo, Valter; Montanaro, Laura; Chevalier, Jérôme

    2017-01-15

    Zirconia-based composites were developed through an innovative processing route able to tune compositional and microstructural features very precisely. Fully-dense ceria-stabilized zirconia ceramics (84vol% Ce-TZP) containing equiaxed alumina (8vol%Al 2 O 3 ) and elongated strontium hexa-aluminate (8vol% SrAl 12 O 19 ) second phases were obtained by conventional sintering. This work deals with the effect of the zirconia stabilization degree (CeO 2 in the range 10.0-11.5mol%) on the transformability and mechanical properties of Ce-TZP-Al 2 O 3 -SrAl 12 O 19 materials. Vickers hardness, biaxial flexural strength and Single-edge V-notched beam tests revealed a strong influence of ceria content on the mechanical properties. Composites with 11.0mol% CeO 2 or above exhibited the classical behaviour of brittle ceramics, with no apparent plasticity and very low strain to failure. On the contrary, composites with 10.5mol% CeO 2 or less showed large transformation-induced plasticity and almost no dispersion in strength data. Materials with 10.5mol% of ceria showed the highest values in terms of biaxial bending strength (up to 1.1GPa) and fracture toughness (>10MPa√m). In these ceramics, as zirconia transformation precedes failure, the Weibull modulus was exceptionally high and reached a value of 60, which is in the range typically reported for metals. The results achieved demonstrate the high potential of using these new strong, tough and stable zirconia-based composites in structural biomedical applications. Yttria-stabilized (Y-TZP) zirconia ceramics are increasingly used for developing metal-free restorations and dental implants. Despite their success related to their excellent mechanical resistance, Y-TZP can undergo Low Temperature Degradation which could be responsible for restoration damage or even worst the failure of the implant. Current research is focusing on strategies to improve the LTD resistance of Y-TZP or to develop alternative composites with better

  11. Wear of human enamel opposing monolithic zirconia, glass ceramic, and composite resin: an in vitro study.

    Science.gov (United States)

    Sripetchdanond, Jeerapa; Leevailoj, Chalermpol

    2014-11-01

    Demand is increasing for ceramic and composite resin posterior restorations. However, ceramics are recognized for their high abrasiveness to opposing dental structure. The purpose of this study was to investigate the wear of enamel as opposed to dental ceramics and composite resin. Twenty-four test specimens (antagonists), 6 each of monolithic zirconia, glass ceramic, composite resin, and enamel, were prepared into cylindrical rods. Enamel specimens were prepared from 24 extracted human permanent molar teeth. Enamel specimens were abraded against each type of antagonist with a pin-on-disk wear tester under a constant load of 25 N at 20 rpm for 4800 cycles. The maximum depth of wear (Dmax), mean depth of wear (Da), and mean surface roughness (Ra) of the enamel specimens were measured with a profilometer. All data were statistically analyzed by 1-way ANOVA, followed by the Tukey test (α=.05). A paired t test was used to compare the Ra of enamel at baseline and after testing. The wear of both the enamel and antagonists was evaluated qualitatively with scanning electron microscopic images. No significant differences were found in enamel wear depth (Dmax, Da) between monolithic zirconia (2.17 ±0.80, 1.83 ±0.75 μm) and composite resin (1.70 ±0.92, 1.37 ±0.81 μm) or between glass ceramic (8.54 ±2.31, 7.32 ±2.06 μm) and enamel (10.72 ±6.31, 8.81 ±5.16 μm). Significant differences were found when the enamel wear depth caused by monolithic zirconia and composite resin was compared with that of glass ceramic and enamel (Pglass ceramic, and enamel (Pglass ceramic and enamel. All test materials except composite resin similarly increased the enamel surface roughness after wear testing. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  12. The effect of adding magnesium oxide on the mechanical properties of the tricalcium phosphate-zirconia composites

    Energy Technology Data Exchange (ETDEWEB)

    Sallemi, Imen, E-mail: imen.sallemi@hotmail.com; Bouaziz, Jamel; Ben Ayed, Foued

    2015-02-01

    The effect of magnesium oxide on the mechanical properties of the tricalcium phosphate – 50 wt.% zirconia composites was investigated during a sintering process between 1300 °C and 1400 °C. The characteristics of the samples before and after the sintering process were realized by using the differential thermal analysis, dilatometry, X-ray diffraction, the {sup 31}P magic angle scanning nuclear magnetic resonance, the scanning electron microscope and by considering such mechanical properties as the rupture strength and Vickers hardness. The mechanical performances of the tricalcium phosphate-50 wt.% zirconia composites increased with both the percentage of magnesium oxide and the sintering temperature. At 1400 °C, the mechanical properties of the composites sintered with 10 wt.% magnesium oxide reached their maximum value. Thus, Vickers hardness increased from 554 to 6350 MPa and the rupture strength of the corresponding composites varied from 5.2 to 25 MPa. The increase of the mechanical properties of the samples is due to the formation of both the tetragonal zirconia phase and the liquid phase which helps to fill the pores. The microstructure of needle form is most probably phosphate precipitates which are formed from this liquid phase. Furthermore, the presence of magnesium oxide in the composites prevented the inverse allotropic transformation of zirconia. - Highlights: • We measure the rupture strength and Vickers hardness of bioceramics. • We characterize the effect of MgO on the mechanical properties of the tricalcium phosphate – 50 wt% zirconia composites. • MgO increase the mechanical properties of the composites.

  13. Preparation and properties of yttria doped tetragonal zirconia polycrystal/Sr-doped barium hexaferrite ceramic composites

    International Nuclear Information System (INIS)

    Wang, Shanshan; Zhang, Chao; Guo, Ruisong; Liu, Lan; Yang, Yuexia; Li, Kehang

    2015-01-01

    Highlights: • The 3Y-TZP/Sr-doped barium ferrite composites were prepared. • The saturation magnetization was improved by 15% with Sr-doping. • The dispersion coefficient p could reflect the microscopic lattice variation. • The composite with x = 0.5 had the maximum fracture toughness of 8.3 MPa m 1/2 . - Abstract: The effects of substitution of Ba 2+ by Sr 2+ on the magnetic property of barium ferrite and addition barium ferrite secondary phase to the 3 mol% yttria-doped tetragonal zirconia polycrystal (3Y-TZP) matrix on the mechanical property of composites were investigated. The Sr-doped barium ferrite (Ba 1−x Sr x Fe 12 O 19 , x = 0, 0.25, 0.50 and 0.75) was synthesized by solid-state reaction in advance. Then 3Y-TZP/20 wt% Sr-doped barium ferrite composites were prepared by means of conventional ceramic method. It was found that a moderate amount of Sr added to barium ferrite could boost the saturation magnetization by 15% compared with the composites without Sr-doping. Besides, the composite with x = 0.50 possessed the best mechanical properties, such as 11.5 GPa for Vickers hardness and 8.3 MPa m 1/2 for fracture toughness, respectively. It was demonstrated that magnetic and mechanical properties of the composites could be harmonized by the incorporation of barium ferrite secondary phase

  14. Shear bond strengths of an indirect composite layering material to a tribochemically silica-coated zirconia framework material.

    Science.gov (United States)

    Iwasaki, Taro; Komine, Futoshi; Fushiki, Ryosuke; Kubochi, Kei; Shinohara, Mitsuyo; Matsumura, Hideo

    2016-01-01

    This study evaluated shear bond strengths of a layering indirect composite material to a zirconia framework material treated with tribochemical silica coating. Zirconia disks were divided into two groups: ZR-PRE (airborne-particle abrasion) and ZR-PLU (tribochemical silica coating). Indirect composite was bonded to zirconia treated with one of the following primers: Clearfil Ceramic Primer (CCP), Clearfil Mega Bond Primer with Clearfil Porcelain Bond Activator (MGP+Act), ESPE-Sil (SIL), Estenia Opaque Primer, MR. Bond, Super-Bond PZ Primer Liquid A with Liquid B (PZA+PZB), and Super-Bond PZ Primer Liquid B (PZB), or no treatment. Shear bond testing was performed at 0 and 20,000 thermocycles. Post-thermocycling shear bond strengths of ZR-PLU were higher than those of ZR-PRE in CCP, MGP+Act, SIL, PZA+PZB, and PZB groups. Application of silane yielded better durable bond strengths of a layering indirect composite material to a tribochemically silica-coated zirconia framework material.

  15. [Bonding of visible light cured composite resins to glass ionomer and Cermet cements].

    Science.gov (United States)

    Kakaboura, A; Vougiouklakis, G

    1990-04-01

    The "sandwich" technique involves combination of composite resins to etched glassionomer cements, is used today in restorative dentistry. The purpose of this study is to evaluate the bond strength between several composite resins and glass ionomer or cerment cements. Cylindrical specimens of the cements Ketac-Silver, Ionobond and GC-Lining Ce-ment were inserted in a mold and their flat free surfaces were etched for 30". Cylindrical plastic tubes were set upon each one of these surfaces and filled with the Composite resins Durafill, Brilliant Lux, Estilux posterior, Estilux posterior CVS and Herculite XR. Half of the specimens transferred in tap water for 24 hours and the others after thermocycling in the first month, kept for 4 months. Shear bond strengths were determined in Monsanto Testing Machine and some fractured surfaces were examined under SEM. The results of this investigation indicate that this technique produces bond strengths between composite resins and glassioners and the combination type of resin and type of cement, affects the values of the strength. Glass cermeet--small particle resin provides the most effective strength and glass ionomer--microfill resins the least. Storage time and thermocycling don't significantly effect the bond strength. SEM examination showed that all fracture failures were obtained in the cement while the opposite resin surfaces were covered with particles of the cements.

  16. In vitro comparison of fracture load of implant-supported, zirconia-based, porcelain- and composite-layered restorations after artificial aging.

    Science.gov (United States)

    Komine, Futoshi; Taguchi, Kohei; Fushiki, Ryosuke; Kamio, Shingo; Iwasaki, Taro; Matsumura, Hideo

    2014-01-01

    This study evaluated fracture load of single-tooth, implant-supported, zirconia-based, porcelain- and indirect composite-layered restorations after artificial aging. Forty-four zirconia-based molar restorations were fabricated on implant abutments and divided into four groups, namely, zirconia-based all-ceramic restorations (ZAC group) and three types of zirconia-based composite-layered restorations (ZIC-P, ZIC-E, and ZIC groups). Before layering an indirect composite material, the zirconia copings in the ZIC-P and ZIC-E groups were primed with Clearfil Photo Bond and Estenia Opaque Primer, respectively. All restorations were cemented on the abutments with glass-ionomer cement and then subjected to thermal cycling and cyclic loading. All specimens survived thermal cycling and cyclic loading. The fracture load of the ZIC-P group (2.72 kN) was not significantly different from that of the ZAC group (3.05 kN). The fracture load of the zirconia-based composite-layered restoration primed with Clearfil Photo Bond (ZIC-P) was comparable to that of the zirconia-based all-ceramic restoration (ZAC) after artificial aging.

  17. Effect of hot isostatic pressing temperature on the microstructural and mechanical properties in the mullite-zirconia composites

    International Nuclear Information System (INIS)

    Greca, M.C.G.; Melo, M. de F.

    1990-01-01

    This work studies the densification, the microstrutural evolution (porosity and zirconia grain size) and bending strength (σ f ) of the two mullite-zirconia composites with TiO 2 additions (0.25 and 1,0 mole%) submitted to different kind of hipping cycles at several temperatures. The results have been shown that: i) HIPing temperature seem to have no influence in densification and mechanical behaviour. ii) Total densification only appears in composition with more quantity of titania (1.0 mole%) which prove that titanium enhance the mass transfer by changes in grain boundary microchemistry. iii) Mechanical behaviour is correlated with densification and microstructural evolution for both composites and degradation is present at 1500 0 C and 1550 0 C which is related with particle coarsening. (author) [pt

  18. Microstructural stability of spark-plasma-sintered W f /W composite with zirconia interface coating under high-heat-flux hydrogen beam irradiation.

    Czech Academy of Sciences Publication Activity Database

    Avello de Lama, M.; Balden, M.; Greuner, H.; Höschen, T.; Matějíček, Jiří; You, J.H.

    2017-01-01

    Roč. 13, December (2017), s. 74-80 ISSN 2352-1791 R&D Projects: GA ČR GB14-36566G EU Projects: European Commission(XE) 633053 - EUROfusion Institutional support: RVO:61389021 Keywords : tungsten-fibre/tungsten composites * plasma-facing components * spark plasma sintering Subject RIV: JI - Composite Materials OBOR OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics https://www.sciencedirect.com/science/article/pii/S2352179117300273

  19. Aqueous degradation kinetics of pharmaceutical drug diclofenac by photo catalysis using nano structured titania–zirconia composite catalyst

    International Nuclear Information System (INIS)

    Das, L.; Barodia, S. K.; Sengupta, S.; Basu, J. K.

    2015-01-01

    Diclofenac is an anti-inflammatory pharmaceutical drug and its presence in a trace amount in waste water makes severe environmental pollution. The degradation of diclofenac was investigated by a photo catalytic process in presence of ultra violet irradiation at room temperature using titania and titania-zirconia nano composite catalysts in a batch reactor. The composite catalyst was prepared by sol-gel method and characterized by X-ray diffraction, transmission electron microscopy as well as BET surface area analyzer. The effect of various process parameters such as catalyst loading, initial concentration of diclofenac and p H of the experimental solution was observed on the degradation of diclofenac. The titania-zirconia nano composites exhibited reasonably higher photo catalytic activity than that of anatase form of titania without zirconia. The maximum removal of diclofenac of about 92.41% was achieved using Zr/Ti mass ratio of 11.8 wt% composite catalyst. A rate equation was proposed for the degradation of diclofenac using the composite catalyst. The values of rate constant (kc) and adsorption equilibrium constant (K1) were found to vary with the catalyst content in the reaction mixture.

  20. Cermet coatings for solar Stirling space power

    International Nuclear Information System (INIS)

    Jaworske, Donald A.; Raack, Taylor

    2004-01-01

    Cermet coatings, molecular mixtures of metal and ceramic, are being considered for the heat inlet surface of a solar Stirling space power convertor. The role of the cermet coating is to absorb as much of the incident solar energy as possible. The ability to mix metal and ceramic at the atomic level offers the opportunity to tailor the composition and the solar absorptance of these coatings. Several candidate cermet coatings were created and their solar absorptance was characterized as-manufactured and after exposure to elevated temperatures. Coating composition was purposely varied through the thickness of the coating. As a consequence of changing composition, islands of metal are thought to form in the ceramic matrix. Computer modeling indicated that diffusion of the metal atoms played an important role in island formation while the ceramic was important in locking the islands in place. Much of the solar spectrum is absorbed as it passes through this labyrinth

  1. Re-activation of degraded nickel cermet anodes - Nano-particle formation via reverse current pulses

    DEFF Research Database (Denmark)

    Hauch, Anne; Marchese, M.; Lanzini, A.

    2018-01-01

    The Ni/yttria-stabilized-zirconia (YSZ) cermet is the most commonly applied fuel electrode for solid oxide cells (SOCs). Loss of Ni/YSZ electrode activity is a key life-time limiting factor of the SOC. Developing means to mitigate this loss of performance or re-activate a fuel electrode is theref......The Ni/yttria-stabilized-zirconia (YSZ) cermet is the most commonly applied fuel electrode for solid oxide cells (SOCs). Loss of Ni/YSZ electrode activity is a key life-time limiting factor of the SOC. Developing means to mitigate this loss of performance or re-activate a fuel electrode...

  2. The influence of zirconia precursor/binding polymer mass ratio in the intermediate electrospun composite fibers on the phase transformation of final zirconia nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Rodaev, Vyacheslav V.; Zhigachev, Andrey O.; Korenkov, Viktor V.; Golovin, Yuri I. [Institute for Nanotechnology and Nanomaterials, Tambov State University, Internatsionalnaya Str. 33, 392000, Tambov (Russian Federation)

    2016-09-15

    Nanofibrous zirconia was fabricated by calcination of electrospun zirconium oxychloride/polyethylene oxide (PEO) composite fibers with different mass fraction of the components. ZrO{sub 2} nanofibers were characterized by scanning electron microscopy (SEM), nitrogen adsorption at 77 K, and X-ray diffractometry (XRD). It was revealed that increase in ZrOCl{sub 2}/PEO mass ratio above the threshold value significantly decreases tetragonal phase (t-ZrO{sub 2}) content and increases monoclinic phase (m-ZrO{sub 2}) content in final ceramic nanofibers. Distinct t-ZrO{sub 2} → m-ZrO{sub 2} transformation takes place when average ZrO{sub 2} grain size approaches to 30 nm. (copyright 2016 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  3. Effect of Mo2C content on the properties of TiC/TiB2 base cermets

    International Nuclear Information System (INIS)

    Takagi, Ken-ichi; Osada, Ken; Koike, Wataru; Fujima, Takuya

    2009-01-01

    The effects of Mo 2 C content on the microstructure and mechanical properties of TiC/TiB 2 base cermets were studied using the model cermets with the compositions of TiC/TiB 2 -(11-17)Mo 2 C-24Ni (mass%). TiC and TiB 2 ratio is set to molar ratio of 59:41 that is near quasi-eutectic composition. As a result, both transverse rupture strength and hardness of the cermets showed maxima for the cermet containing 13% Mo 2 C. The cermet achieved remarkable microstructural refinement and still maintained characteristic core-rim structure of the TiC base cermets. TiC/TiB 2 cermets, in addition to TiCN base cermets, are a good alternative material to cemented carbides.

  4. Microstructural characterization of a zirconia-toughened alumina fiber reinforced niobium aluminide composite

    International Nuclear Information System (INIS)

    Nourbakhsh, S.; Sahin, O.; Rhee, W.H.; Margolin, H.

    1992-01-01

    This paper reports on an NbAl 3 + Nb 2 Al composite reinforced with continuous zirconia-toughened alumina, PRD-166 fibers, that was produced by pressure casing and was examined by optical and transmission electron microscopy and energy dispersive spectroscopy. Exposure of the fiber to the molten metal resulted in ZrO 2 and Al; 2 O 3 grain growth, formation of a thin layer of an amorphous phase on the grain boundaries of Al 2 O 3 and transformation of ZrO 2 . Preferential Al 2 O 3 grain growth near the surface of the fiber led to the rejection of ZrO 2 from this region into the molten metal. In NbAl 3 slip occurred by the glide of a left-angle 110 right-angle superdislocations and to a lesser extent by the glide of a pair of left-angle 11 bar 1 right-angle + left-angle 3 bar 1 bar 1 right-angle dislocations on the (112) planes and a/2 left-angle 110 right-angle superpartial dislocations on the (001) plane. The operating slip system in Nb 2 Al was identified as {010 left-angle 100 right-angle. A left-angle 100 right-angle dislocations were dissociated into a/x left-angle 100 right-angle partial dislocations joined together by a stacking fault

  5. Atomic structure and composition of the yttria-stabilized zirconia (111) surface.

    Science.gov (United States)

    Vonk, Vedran; Khorshidi, Navid; Stierle, Andreas; Dosch, Helmut

    2013-06-01

    Anomalous and nonanomalous surface X-ray diffraction is used to investigate the atomic structure and composition of the yttria-stabilized zirconia (YSZ)(111) surface. By simulation it is shown that the method is sensitive to Y surface segregation, but that the data must contain high enough Fourier components in order to distinguish between different models describing Y/Zr disorder. Data were collected at room temperature after two different annealing procedures. First by applying oxidative conditions at 10 - 5  mbar O 2 and 700 K to the as-received samples, where we find that about 30% of the surface is covered by oxide islands, which are depleted in Y as compared with the bulk. After annealing in ultrahigh vacuum at 1270 K the island morphology of the surface remains unchanged but the islands and the first near surface layer get significantly enriched in Y. Furthermore, the observation of Zr and oxygen vacancies implies the formation of a porous surface region. Our findings have important implications for the use of YSZ as solid oxide fuel cell electrode material where yttrium atoms and zirconium vacancies can act as reactive centers, as well as for the use of YSZ as substrate material for thin film and nanoparticle growth where defects control the nucleation process.

  6. Fabrication and properties of yttria, ceria doped zirconia-aluminia ceramic composites

    International Nuclear Information System (INIS)

    Lyubushkin, R.A.; Ivanov, O.N.; Chuev, V.P.; Buzov, A.A.

    2011-01-01

    At present, zirconia-based ceramics are gaining popularity in dentistry, particularly in fixed prosthodontics. clinically, it is important that ceramic restorations reproduce the translucency and color of natural teeth. Zirconia based ceramics is a high performance material with excellent biocompatibility and mechanical properties, which suggest its suitability for posterior fixed partial dentures. Y 2 O 3 -stabilized tetragonal zirconia polycrystalline (YTZ/Al 2 O 3 ) and CeO 2 -stabilized tetragonal zirconia polycrystalline (CZA) ceramics with high-performance were prepared for dental application by use the wet chemical route, consolidated by cold isostatic pressing, and two-step sintering method. Physical and mechanical properties test results show that the bending strength, fracture toughness, and the density of full sintered ceramics suggest that the material is relatively suitable for dental restoration.

  7. Fabrication of hollow silica–zirconia composite spheres and their activity for hydrolytic dehydrogenation of ammonia borane

    Energy Technology Data Exchange (ETDEWEB)

    Umegaki, Tetsuo, E-mail: umegaki.tetsuo@nihon-u.ac.jp [Department of Materials and Applied Chemistry, College of Science and Engineering, Nihon University, 1-8-14, Kanda-Surugadai, Chiyoda-Ku, Tokyo 101-8308 (Japan); Hosoya, Tatsuya; Toyama, Naoki [Department of Materials and Applied Chemistry, College of Science and Engineering, Nihon University, 1-8-14, Kanda-Surugadai, Chiyoda-Ku, Tokyo 101-8308 (Japan); Xu, Qiang [National Institute of Advanced Industrial Science and Technology (AIST), 1-8-31 Midorigaoka, Ikeda, Osaka 563-8577 (Japan); Kojima, Yoshiyuki [Department of Materials and Applied Chemistry, College of Science and Engineering, Nihon University, 1-8-14, Kanda-Surugadai, Chiyoda-Ku, Tokyo 101-8308 (Japan)

    2014-09-01

    Highlights: • Hollow silica–zirconia composite spheres were fabricated on polystyrene templates by the sol–gel method. • We study the effect of preparation conditions on the activity for hydrolytic dehydrogenation of ammonia borane. • The activity of hollow silica–zirconia composite spheres depends on wall thickness. - Abstract: In this paper, we report fabrication of hollow silica–zirconia composite spheres by polystyrene (PS) template method and control of wall thickness of the hollow spheres in nanoscale. Both the hollow spheres before and after calcination were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), elemental analysis, and powder X-ray diffraction analysis (XRD). Morphology of the hollow spheres does not significantly change after calcination from the results of SEM and TEM images, while the amount of residual PS templates drastically decreases via the calcination procedure from the results of FTIR and elemental analysis. The sample after calcination mainly includes amorphous silica from the results of XRD, indicating that the hollow silica–zirconia composite spheres consist of amorphous phases and/or fine particles. Wall thicknesses of the samples after calcination are controlled by adjusting the amount of PS template suspension, and hollow silica–zirconia composite spheres with the wall thicknesses of 17.5, 15.0, 10.0, and 2.0 nm are obtained using the PS template suspension of 25.0, 33.5, 100.0, and 400.0 g, respectively. The activities of the hollow spheres for hydrolytic dehydrogenation of ammonia borane (NH{sub 3}BH{sub 3}) were compared. The evolutions of 2.0, 3.1, 5.0, and 8.0 mL hydrogen from aqueous NH{sub 3}BH{sub 3} solution were finished in about 4, 5, 3, and 7 min in the presence of the hollow spheres with wall thicknesses of 17.5, 15.0, 10.0, and 2.0 nm, respectively. The molar ratios of the hydrolytically generated hydrogen to

  8. Development and characterization of cermet forms for radioactive waste

    International Nuclear Information System (INIS)

    Aaron, W.S.; Quinby, T.C.; Kobisk, E.H.

    1979-01-01

    Cermets designed to isolate high-level wastes in a solid form are a composite consisting of various ceramic phase particles uniformly dispersed in and microencapsulated by an iron-nickel base alloy matrix. The metal matrix provides this waste form with many advantageous features including excellent thermal conductivity and mechanical strength. These cermets are formed by first dissolving the waste in molten urea, precipitating and calcining all the constituents, compacting the calcine, and sintering and reduction to form the final product. The exact formulation of cermets through additions to the waste is designed to fix most of the fission products in stable, leach resistant ceramic phases which are subsequently microencapsulated by an alloy matrix. The alloy matrix, which is derived primarily from the waste itself and includes the reducible fission and activation products from the waste, can be compositionally adjusted through additions to optimize its corrosion resistance under conditions existing in various disposal environments. The processes by which cermets are formed include several new and unique materials preparation options that are being developed to permit engineering scale-up and to be compatible with remote operations. Cermets formed by alternate processing methods are being characterized. Initially, cermet samples were prepared using a laboratory scale, batch process developed for the preparation of special ceramics having high compositional uniformity and excellent sinterability. The modification of this batch process to one suitable for scale-up and remote operation is the subject of this paper. Cermet characterization is also discussed

  9. Cermet fuel reactors

    International Nuclear Information System (INIS)

    Cowan, C.L.; Palmer, R.S.; Van Hoomissen, J.E.; Bhattacharyya, S.K.

    1987-01-01

    Cermet fueled nuclear reactors are attractive candidates for high performance space power systems. The cermet fuel consists of tungsten-urania hexagonal fuel blocks characterized by high strength at elevated temperatures, a high thermal conductivity and resultant high thermal shock resistance. The concept evolved in the 1960's with the objective of developing a reactor design which could be used for a wide range of mobile power generation systems including both Brayton and Rankine power conversion cycles. High temperature thermal cycling tests and in-reactor irradiation tests using cermet fuel were carried out by General Electric in the 1960's as part of the 710 Development Program and by Argonne National laboratory in a subsequent activity. Cermet fuel development programs are currently underway at Argonne National laboratory and Pacific Northwest Laboratory as part of the Multi-Megawatt Space Power Program. Key features of the cermet fueled reactor design are 1) the ability to achieve very high coolant exit temperatures, and 2) thermal shock resistance during rapid power changes, and 3) two barriers to fission product release - the cermet matrix and the fuel element cladding. Additionally, there is a potential for achieving a long operating life because of 1) the neutronic insensitivity of the fast-spectrum core to the buildup of fission products and 2) the utilization of a high strength refractory metal matrix and structural materials. These materials also provide resistance against compression forces that potentially might compact and/or reconfigure the core

  10. SiC fiber and yttria-stabilized zirconia composite thick thermal barrier coatings fabricated by plasma spray

    Science.gov (United States)

    Ma, Rongbin; Cheng, Xudong; Ye, Weiping

    2015-12-01

    Approximately 4 mm-thick SiC fiber/yttria-stabilized zirconia (YSZ) composite thermal barrier coatings (TBCs) were prepared by atmospheric plasma spray (APS). The composite coatings have a 'reinforced concrete frame structure', which can protect the coating from failure caused by increasing thickness of coating. The SiC fiber plays an important role in reducing the residual stress level of the composite coatings. The thermal conductivity (TC) value of the composite coatings is 0.632 W/m K, which is about 50% reduction compared to that of typical APS YSZ TBCs. And the composite coatings have higher fracture toughness and better thermal shock resistance than the YSZ TBCs.

  11. Effect of Different Surface Treatments on Repair Micro-shear Bond Strength of Silica- and Zirconia-filled Composite Resins

    Directory of Open Access Journals (Sweden)

    Mohammad Joulaei

    2012-11-01

    Full Text Available Background and aims. Effect of surface treatments on repair bond strength of aged composite resins might be different due to their dissimilar fillers. The aim was to evaluate the effect of different surface treatments on repair micro-shear bond strength (µSBS of silica- (Spectrum TPH and zirconia-filled (Filtek Z250 composite resins. Materials and methods. Twenty-seven composite resin blocks were made from each type of composite resin: Z250 and Spectrum TPH. After aging, blocks of each type were randomly divided into three groups according to surface treatments: alloy primer, silane, and only surface roughening. Subsequently, each group was further subdivided into 3 subgroups based on the adhesive system used: Single Bond, Clearfil SE Bond, and Margin Bond. Four composite resin columns were added on each block. After thermocycling, µSBStest were done at cross head speed of 0.5 mm/min. Data was analysed using multifactor ANOVA, one-way ANOVA and a post-hoc Bonferroni tests (α = 0.05. Results. Analysis of data showed that the effect of composite resin type was not significant (p > 0.05, but the effects of the type of surface treatment (p = 0.01 and the type of adhesive system (p = 0.01 were significant on repair µSBS. In addition, the cumulative effect of the composite type-surface treatment and the composite type with the type of adhesive system were not statistically significant (p > 0.05. However, the cumulative effects of the adhesive system-surface treatment (p = 0.03 and the composite type-the adhesive system-surface treatments (p = 0.002 were significant. Conclusion. Although repair µSBS values of both silica- and zirconia-filled composite resins were similar, use of different combinations of surface treatments and adhesive systems affected their repair µSBS differently.

  12. Effect of Different Surface Treatments on Repair Micro-shear Bond Strength of Silica- and Zirconia-filled Composite Resins

    Science.gov (United States)

    Joulaei, Mohammad; Bahari, Mahmoud; Ahmadi, Anahid; Savadi Oskoee, Siavash

    2012-01-01

    Background and aims Effect of surface treatments on repair bond strength of aged composite resins might be different due to their dissimilar fillers. The aim was to evaluate the effect of different surface treatments on repair micro-shear bond strength (µSBS) of silica- (Spectrum TPH) and zirconia-filled (Filtek Z250) composite resins. Materials and methods Twenty-seven composite resin blocks were made from each type of composite resin: Z250 and Spectrum TPH. After aging, blocks of each type were randomly divided into three groups according to surface treatments: alloy primer, silane, and only surface roughening. Subsequently, each group was further subdivided into 3 subgroups based on the adhesive system used: Single Bond, Clearfil SE Bond, and Margin Bond. Four composite resin columns were added on each block. After thermocycling, µSBStest were done at cross head speed of 0.5 mm/min. Data was analysed using multifactor ANOVA, one-way ANOVA and a post-hoc Bonferroni tests (α = 0.05). Results Analysis of data showed that the effect of composite resin type was not significant (p > 0.05), but the effects of the type of surface treatment (p = 0.01) and the type of adhesive system (p = 0.01) were significant on repair µSBS. In addition, the cumulative effect of the composite type-surface treatment and the composite type with the type of adhesive system were not statistically significant (p > 0.05). However, the cumulative effects of the adhesive system-surface treatment (p = 0.03) and the composite type-the adhesive system-surface treatments (p = 0.002) were significant. Conclusion Although repair µSBS values of both silica- and zirconia-filled composite resins were similar, use of different combinations of surface treatments and adhesive systems affected their repair µSBS differently. PMID:23277859

  13. The Chemical Composition and Structure of Supported Sulfated Zirconia with Regulated Size Nanoparticles

    International Nuclear Information System (INIS)

    Kanazhevskiy, V. V.; Shmachkova, V. P.; Kotsarenko, N. S.; Kochubey, D. I.; Vedrine, J. C.

    2007-01-01

    A set of model skeletal isomerization catalysts - sulfated zirconia nanoparticles of controlled thickness anchored on different supports - was prepared using colloidal solutions of Zr salt on titania as support. The nanoparticles of zirconia (1-5 nm) are epitaxially connected to the support surface, with S/Zr ratio equals to 1.3-1.5. It was shown by EXAFS that nanoparticles of non-stoichiometric zirconium sulfate Zr(SO4)1+x, where x<0.5, are formed on the support surface. Its structure looks like half-period shifted counterdirected chains built-up by zirconium atoms linked by triangle pyramids of sulfate groups. Considering catalytic data of skeletal n-butane isomerisation at 150 deg. C, one can suggest that these species behave as the active component of sulfated zirconia. They are formed in subsurface layers as zirconium hydroxide undergoes sulfation followed by thermal treatment

  14. Process for fabrication of cermets

    Science.gov (United States)

    Landingham, Richard L [Livermore, CA

    2011-02-01

    Cermet comprising ceramic and metal components and a molten metal infiltration method and process for fabrication thereof. The light weight cermets having improved porosity, strength, durability, toughness, elasticity fabricated from presintered ceramic powder infiltrated with a molten metal or metal alloy. Alumina titanium cermets biocompatible with the human body suitable for bone and joint replacements.

  15. Shear bond strength of a denture base acrylic resin and gingiva-colored indirect composite material to zirconia ceramics.

    Science.gov (United States)

    Kubochi, Kei; Komine, Futoshi; Fushiki, Ryosuke; Yagawa, Shogo; Mori, Serina; Matsumura, Hideo

    2017-04-01

    To evaluate the shear bond strengths of two gingiva-colored materials (an indirect composite material and a denture base acrylic resin) to zirconia ceramics and determine the effects of surface treatment with various priming agents. A gingiva-colored indirect composite material (CER) or denture base acrylic resin (PAL) was bonded to zirconia disks with unpriming (UP) or one of seven priming agents (n=11 each), namely, Alloy Primer (ALP), Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB+Act), Metal Link (MEL), Meta Fast Bonding Liner (MFB), MR. bond (MRB), and V-Primer (VPR). Shear bond strength was determined before and after 5000 thermocycles. The data were analyzed with the Kruskal-Wallis test and Steel-Dwass test. The mean pre-/post-thermalcycling bond strengths were 1.0-14.1MPa/0.1-12.1MPa for the CER specimen and 0.9-30.2MPa/0.1-11.1MPa for the PAL specimen. For the CER specimen, the ALP, CPB, and CPB+Act groups had significantly higher bond strengths among the eight groups, at both 0 and 5000 thermocycles. For the PAL specimen, shear bond strength was significantly lower after thermalcycling in all groups tested. After 5000 thermocycles, bond strengths were significantly higher in the CPB and CPB+Act groups than in the other groups. For the PAL specimens, bond strengths were significantly lower after thermalcycling in all groups tested. The MDP functional monomer improved bonding of a gingiva-colored indirect composite material and denture base acrylic resin to zirconia ceramics. Copyright © 2016 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

  16. The Chemical Composition and Structure of Supported Sulfated Zirconia with Regulated Size Nanoparticles

    Science.gov (United States)

    Kanazhevskiy, V. V.; Shmachkova, V. P.; Kotsarenko, N. S.; Kochubey, D. I.; Vedrine, J. C.

    2007-02-01

    A set of model skeletal isomerization catalysts — sulfated zirconia nanoparticles of controlled thickness anchored on different supports — was prepared using colloidal solutions of Zr salt on titania as support. The nanoparticles of zirconia (1-5 nm) are epitaxially connected to the support surface, with S/Zr ratio equals to 1.3-1.5. It was shown by EXAFS that nanoparticles of non-stoichiometric zirconium sulfate Zr(SO4)1+x, where xlayers as zirconium hydroxide undergoes sulfation followed by thermal treatment.

  17. Composite coating containing WC/12Co cermet and Fe-based metallic glass deposited by high-velocity oxygen fuel spraying

    International Nuclear Information System (INIS)

    Terajima, Takeshi; Takeuchi, Fumiya; Nakata, Kazuhiro; Adachi, Shinichiro; Nakashima, Koji; Igarashi, Takanori

    2010-01-01

    A composite coating containing WC/12Co cermet and Fe 43 Cr 16 Mo 16 C 15 B 10 metallic glass was successfully deposited onto type 304 stainless steel by high-velocity oxygen fuel (HVOF) spraying, and the microstructure and tribological properties were investigated. The microstructure of the coating was characterized by scanning electron microscopy/electron probe micro-analysis (SEM/EPMA) and X-ray diffractometry (XRD). The hardness, adhesion strength and tribological properties of the coating were tested with a Vickers hardness tester, tensile tester and reciprocating wear tester, respectively. The composite coating, in which flattened WC/12Co was embedded in amorphous Fe 43 Cr 16 Mo 16 C 15 B 10 layers, exhibited high hardness, good wear resistance and a low friction coefficient compared to the monolithic coating. The addition of 8% WC/12Co to the Fe 43 Cr 16 Mo 16 C 15 B 10 matrix increased the cross-sectional hardness from 660 to 870 HV and reduced the friction coefficient from 0.65 to 0.5. WC/12Co reinforcement plays an important role in improving the tribological properties of the Fe 43 Cr 16 Mo 16 C 15 B 10 coating.

  18. Design and Fabrication of Al2O3-(W, TiC-TiN-Mo-Ni Nano-composite Cermet Tool Materials with Graded Structures

    Directory of Open Access Journals (Sweden)

    NI Xiu-ying

    2018-02-01

    Full Text Available Based on the analysis on temperature and stress distributions, as well as fatigue crack propagation in cutting tools, a model for designing compositional distribution and microstructure with graded characteristics was proposed. The addition of ductile phase and the introduction of the graded structure are beneficial to slow down the fatigue crack propagation rate and improve tool life.Al2O3-(W,TiC-TiN-Mo-Ni nano-composite tool material with graded structures was fabricated via two stage hot pressing sintering process, and the microstructure and mechanical properties were studied. The results show that the surface hardness, fracture toughness of inner layer and bending strength of the cermet with sintered gradient structure reach 19.258GPa, 10.015MPa·m1/2 and 1017.475MPa,respectively.The performance requirements to cutting tools were met. The dimple cleavage and torn edge of the binding phase in the fracture surfaces can be beneficial to the improvement of the fracture toughness and bending strength,so the resistance to fatigue crack propagation of tools is improved.

  19. Phase characterization of precipitated zirconia

    International Nuclear Information System (INIS)

    Gutzov, S.; Ponahlo, J.; Lengauer, C.L.; Beran, A.

    1994-01-01

    The phase compositions of undoped and europium-doped zirconia samples, obtained by precipitation and thermal treatment from 350 to 1,000 C, have been investigated by powder X-ray diffractometry, infrared spectroscopy, and cathodoluminescence spectroscopy. The low-temperature stabilization of tetragonal zirconia is mainly controlled by the presence of anion additives, such as ammonium chloride. The influences of the crystallite size is less important. Cathodoluminescence spectra show a structural similarity between tetragonal and amorphous zirconia

  20. Mixed conductivity, structural and microstructural characterization of titania-doped yttria tetragonal zirconia polycrystalline/titania-doped yttria stabilized zirconia composite anode matrices

    International Nuclear Information System (INIS)

    Colomer, M.T.; Maczka, M.

    2011-01-01

    Taking advantage of the fact that TiO 2 additions to 8YSZ cause not only the formation of a titania-doped YSZ solid solution but also a titania-doped YTZP solid solution, composite materials based on both solutions were prepared by solid state reaction. In particular, additions of 15 mol% of TiO 2 give rise to composite materials constituted by 0.51 mol fraction titania-doped yttria tetragonal zirconia polycrystalline and 0.49 mol fraction titania-doped yttria stabilized zirconia (0.51TiYTZP/0.49TiYSZ). Furthermore, Y 2 (Ti 1-y Zr y ) 2 O 7 pyrochlore is present as an impurity phase with y close to 1, according to FT-Raman results. Lower and higher additions of titania than that of 15 mol%, i.e., x=0, 5, 10, 20, 25 and 30 mol% were considered to study the evolution of 8YSZ phase as a function of the TiO 2 content. Furthermore, zirconium titanate phase (ZrTiO 4 ) is detected when the titania content is equal or higher than 20 mol% and this phase admits Y 2 O 3 in solid solution according to FE-SEM-EDX. The 0.51TiYTZP/0.49TiYSZ duplex material was selected in this study to establish the mechanism of its electronic conduction under low oxygen partial pressures. In the pO 2 range from 0.21 to 10 -7.5 atm. the conductivity is predominantly ionic and constant over the range and its value is 0.01 S/cm. The ionic plus electronic conductivity is 0.02 S/cm at 1000 o C and 10 -12.3 atm. Furthermore, the onset of electronic conductivity under reducing conditions exhibits a -1/4 pO 2 dependence. Therefore, it is concluded that the n-type electronic conduction in the duplex material can be due to a small polaron-hopping between Ti 3+ and Ti 4+ . -- Graphical abstract: FE-SEM micrograph of a polished and thermal etched surface of a Ti-doped YTZP/Ti-doped YSZ composite material. Display Omitted Research highlights: → Ti-doped YTZP/Ti-doped YSZ composite materials are mixed conductors under low partial pressures. → From 5 mol% of TiO 2 , Y 2 (Ti 1-y ,Zr y ) 2 O 7 pyrochlore is

  1. Relationship between Magnetic and Mechanical Properties of Cermet Tools

    International Nuclear Information System (INIS)

    Ahn, Dong Gil; Lee, Jeong Hee

    2000-01-01

    The commercial cermet cutting tools consist of multi-carbide and a binder metal of iron group, such as cobalt and nickel which are ferromagnetic. In this paper, a new approach to evaluate the mechanical properties of TiCN based cermet by magnetic properties were studied in relation to binder content and sintering conditions. The experimental cermet was prepared using commercial composition with the other binder contents by PM process. It was found that the magnetic properties of the sintered cermets remarkably depended on the microstructure and the total carbon content. The magnetic saturation was proportional to increment of coercive force. At high carbon content in sintered cermet, the magnetic saturation was increased by decreasing the concentration of solutes such as W, Mo, Ti in Co-Ni binder. As the coercive force increases, the hardness usually increases. The strength and toughness of the cermet also increased with increasing the magnetic saturation. The measurement of magnetic properties made it possible to evaluate the mechanical properties in the cermet cutting tools

  2. Kinetic Studies For the Removal of UO22+ and Pb2+ Ions From Aqueous Solution Using Zirconia Composite Material

    International Nuclear Information System (INIS)

    Sharaf El-Deen, G.E.

    2008-01-01

    Zirconia composite material was chemically synthesized previously and prepared by applying the sol-gel polymeric route using MgO as a stabilizer. The prepared composite material was characterized using various techniques: x-ray fluorescence (XRF), scanning electron microscope (SEM), differential thermal analysis and thermogravimetric analysis (DTA-TG), x-ray diffraction (XRD) and surface area using the BET-method. The sorption removal of UO 2 2+ and Pb 2+ ions from aqueous waste solution by zirconia composite material using batch technique was investigated. The sorption was carried out as a function of ph, particle size, shaking time and temperature. In this work, a comparison of kinetic models applied to the sorption process of each ion was evaluated for the pseudo first-order, the pseudo second-order, intra particle diffusion and homogeneous particle diffusion kinetic models, respectively. The results showed that the homogeneous particle diffusion model (HPDM) best correlate the experimental rate data and the numerical values of the rate constants and particle diffusion coefficients were determined from the graphical representation of the proposed models. Activation energy (Ε a ) and thermodynamic parameters of free energy (δ G * ), enthalpy (δ H * ) and entropy (δ S * ) of activation were also computed from the linearized form of Arrhenius equation

  3. Cermet fuel reactors

    International Nuclear Information System (INIS)

    Cowan, C.L.; Palmer, R.S.; Van Hoomissen, J.E.; Bhattacharyya, S.K.; Barner, J.O.

    1987-09-01

    Cermet fueled nuclear reactors are attractive candidates for high performance space power systems. The cermet fuel consists of tungsten-urania hexagonal fuel blocks characterized by high strength at elevated temperatures, a high thermal conductivity and resultant high thermal shock resistance. Key features of the cermet fueled reactor design are (1) the ability to achieve very high coolant exit temperatures, and (2) thermal shock resistance during rapid power changes, and (3) two barriers to fission product release - the cermet matrix and the fuel element cladding. Additionally, thre is a potential for achieving a long operating life because of (1) the neutronic insensitivity of the fast-spectrum core to the buildup of fission products and (2) the utilization of a high strength refractory metal matrix and structural materials. These materials also provide resistance against compression forces that potentially might compact and/or reconfigure the core. In addition, the neutronic properties of the refractory materials assure that the reactor remains substantially subcritical under conditions of water immersion. It is concluded that cermet fueled reactors can be utilized to meet the power requirements for a broad range of advanced space applications. 4 refs., 4 figs., 3 tabs

  4. Hydroxyapatite and zirconia composites: Effect of MgO and MgF2 on the stability of phases and sinterability

    International Nuclear Information System (INIS)

    Evis, Zafer; Usta, Metin; Kutbay, Isil

    2008-01-01

    Composites of hydroxyapatite with cubic zirconia with MgO or MgF 2 were pressureless sintered at temperatures from 1000 to 1300 deg. C. The reactions and transformations of phases were monitored with X-ray diffraction. For the hydroxyapatite and zirconia composites with MgO, calcium diffused from hydroxyapatite into the zirconia, and hydroxyapatite decomposed to tri-calcium phosphate at sintering temperatures higher than 1000 deg. C. Above about 1200 deg. C, CaZrO 3 was formed. Composites containing the MgF 2 decomposed slower than the composites with MgO which was verified by the changes in the lattice volume of the hydroxyapatite left in the composites. Fluorine ions in MgF 2 diffused into hydroxyapatite which resulted in thermal stability at high sintering temperatures. Composites with MgF 2 had higher hardness than those with MgO. The lowest porosity was found in a composite initially containing 10 wt% cubic zirconia and 5 wt% MgF 2

  5. Degradation of conductivity and microstructure under thermal and current load in Ni-YSZ cermets for SOFC anodes

    DEFF Research Database (Denmark)

    Thydén, Karl Tor Sune; Barfod, Rasmus; Liu, Yi-Lin

    2006-01-01

    The degradation of electrical conductivity in porous nickel-yttria stabilized zirconia composite cermets in a H2/H2O atmosphere under high temperature treatments has been investigated. The parameters varied were: temperature, water partial pressure, and electrical current load. The microstructure...... fraction of percolated Ni was measured. Temperature proved to have the largest effect on the degradation. Samples tested at 1000°C, in contrast to 750°C, showed a severe decrease of conductivity and growth of Ni particles. Higher water partial pressure accelerated Ni particle growth at both temperatures......, but the loss of percolation and conductivity at 1000°C was less severe under high water partial pressure. A possible explanation for this behavior is discussed....

  6. The effect of partially stabilized zirconia on the biological properties of HA/HDPE composites in vitro.

    Science.gov (United States)

    Sadi, A Yari; Shokrgozar, M A; Homaeigohar, S Sh; Hosseinalipour, M; Khavandi, A; Javadpour, J

    2006-05-01

    The effect of partially stabilized zirconia (PSZ) on the biological properties of the hyroxyapatite - high density polyethylene (HA/HDPE) composites was studied by investigating the simultaneous effect of hydroxyapatite and PSZ volume fractions on the in vitro response of human osteoblast cells. The biocompatibility of composite samples with different volume fraction of HA and PSZ powders was assessed by proliferation, alkaline phosphatase (ALP) and cell attachment assays on the osteoblast cell line (G-292) in different time periods. The effect of composites on the behavior of G-292 cells was compared with those of HDPE and TPS (Tissue Culture Poly Styrene as negative control) samples. Results showed a higher proliferation rate of G-292 cells in the presence of composite samples as compared to the HDPE sample after 7 and 14 days of incubation period. ALP production rate in all composite samples was higher than HDPE and TPS samples. The number of adhered cells on the composite samples was higher than the number adhered on the HDPE and TPS samples after the above mentioned incubation periods. These findings indicates that the addition of PSZ does not have any adverse affect on the biocompatibility of HA/HDPE composites. In fact in some experiments PSZ added HA/HDPE composites performed better in proliferation, differentiation and attachment of osteoblastic cells.

  7. Cermets from molten metal infiltration processing

    Science.gov (United States)

    Landingham, Richard Lee

    2012-09-18

    New cermets with improved properties and applications are provided. These new cermets have lower density and/or higher hardness than B4C cermet. By incorporating other new ceramics into B4C powders or as a substitute for B4C, lower densities and/or higher hardness cermets result. The ceramic powders have much finer particle size than those previously used which significantly reduces grain size of the cermet microstructure and improves the cermet properties.

  8. Zirconia/Hydroxyapatite Composites Synthesized Via Sol-Gel: Influence of Hydroxyapatite Content and Heating on Their Biological Properties

    Science.gov (United States)

    Bollino, Flavia; Armenia, Emilia; Tranquillo, Elisabetta

    2017-01-01

    Zirconia (ZrO2) and zirconia-based glasses and ceramics are materials proposed for use in the dental and orthopedic fields. In this work, ZrO2 glass was modified by adding different amounts of bioactive and biocompatible hydroxyapatite (HAp). ZrO2/HAp composites were synthesized via the sol-gel method and heated to different temperatures to induce modifications of their chemical structure, as ascertained by Fourier transform infrared spectroscopy (FTIR) analysis. The aim was to investigate the effect of both HAp content and heating on the biological performances of ZrO2. The materials’ bioactivity was studied by soaking samples in a simulated body fluid (SBF). FTIR and scanning electron microscopy (SEM)) analyses carried out after exposure to SBF showed that all materials are bioactive, i.e., they are able to form a hydroxyapatite layer on their surface. Moreover, the samples were soaked in a solution containing bovine serum albumin (BSA). FTIR analysis proved that the synthesized materials are able to adsorb the blood protein, the first step of cell adhesion. WST-8 ([2-(2-methoxy-4-nitrophenyl)-3-(4-nitrophenyl)-5-(2,4-disulfophenyl)-2H-tetrazolium, monosodium salt]) assay showed that no cytotoxicity effects were induced by the materials’ extract. However, the results proved that bioactivity increases with both the HAp content and the temperature used for the thermal treatment, whereas biocompatibility increases with heating but is not affected by the HAp content. PMID:28773116

  9. Fabrication of High Temperature Cermet Materials for Nuclear Thermal Propulsion

    Science.gov (United States)

    Hickman, Robert; Panda, Binayak; Shah, Sandeep

    2005-01-01

    Processing techniques are being developed to fabricate refractory metal and ceramic cermet materials for Nuclear Thermal Propulsion (NTP). Significant advances have been made in the area of high-temperature cermet fuel processing since RoverNERVA. Cermet materials offer several advantages such as retention of fission products and fuels, thermal shock resistance, hydrogen compatibility, high conductivity, and high strength. Recent NASA h d e d research has demonstrated the net shape fabrication of W-Re-HfC and other refractory metal and ceramic components that are similar to UN/W-Re cermet fuels. This effort is focused on basic research and characterization to identify the most promising compositions and processing techniques. A particular emphasis is being placed on low cost processes to fabricate near net shape parts of practical size. Several processing methods including Vacuum Plasma Spray (VPS) and conventional PM processes are being evaluated to fabricate material property samples and components. Surrogate W-Re/ZrN cermet fuel materials are being used to develop processing techniques for both coated and uncoated ceramic particles. After process optimization, depleted uranium-based cermets will be fabricated and tested to evaluate mechanical, thermal, and hot H2 erosion properties. This paper provides details on the current results of the project.

  10. Preparation of a Composite of Sulfated Zirconia/Metal Organic Framework and its Application in Esterification Reaction

    Energy Technology Data Exchange (ETDEWEB)

    Park, Eun Young; Hasan, Zubair; Ahmed, Imteaz; Jhung, Sung Hwa [Kyungpook National Univ., Daegu (Korea, Republic of)

    2014-06-15

    A porous metal-organic framework (MOF), MIL-101, was synthesized in the presence of sulfated zirconia (SZ) to produce acidic SZ/MIL-101 composites for the first time. The composites were characterized with XRD, nitrogen adsorption, FT-IR, scanning electron microscope, chemical analysis and so on. The composites (SZ/MIL-101s) were successfully applied in a liquid-phase esterification for a high yield of ester. This catalytic result of SZ/MIL-101, compared with that of pure SZ or MIL-101 (showing a negligible yield of ester), suggests that the SZ in the composite is highly active in the acid catalysis probably because of the well-dispersed active species of SZ. Moreover, the esterification is catalyzed in heterogeneous mode as confirmed by negligible esterification after filtration of the catalyst. Finally, microwaves can be efficiently applied both in the synthesis of the composites and the esterification reaction to accelerate the two processes of synthesis and esterification by about 5 times.

  11. Preparation of a Composite of Sulfated Zirconia/Metal Organic Framework and its Application in Esterification Reaction

    International Nuclear Information System (INIS)

    Park, Eun Young; Hasan, Zubair; Ahmed, Imteaz; Jhung, Sung Hwa

    2014-01-01

    A porous metal-organic framework (MOF), MIL-101, was synthesized in the presence of sulfated zirconia (SZ) to produce acidic SZ/MIL-101 composites for the first time. The composites were characterized with XRD, nitrogen adsorption, FT-IR, scanning electron microscope, chemical analysis and so on. The composites (SZ/MIL-101s) were successfully applied in a liquid-phase esterification for a high yield of ester. This catalytic result of SZ/MIL-101, compared with that of pure SZ or MIL-101 (showing a negligible yield of ester), suggests that the SZ in the composite is highly active in the acid catalysis probably because of the well-dispersed active species of SZ. Moreover, the esterification is catalyzed in heterogeneous mode as confirmed by negligible esterification after filtration of the catalyst. Finally, microwaves can be efficiently applied both in the synthesis of the composites and the esterification reaction to accelerate the two processes of synthesis and esterification by about 5 times

  12. Thermal Shock Resistance of Stabilized Zirconia/Metal Coat on Polymer Matrix Composites by Thermal Spraying Process

    Science.gov (United States)

    Zhu, Ling; Huang, Wenzhi; Cheng, Haifeng; Cao, Xueqiang

    2014-12-01

    Stabilized zirconia/metal coating systems were deposited on the polymer matrix composites by a combined thermal spray process. Effects of the thicknesses of metal layers and ceramic layer on thermal shock resistance of the coating systems were investigated. According to the results of thermal shock lifetime, the coating system consisting of 20 μm Zn and 125 μm 8YSZ exhibited the best thermal shock resistance. Based on microstructure evolution, failure modes and failure mechanism of the coating systems were proposed. The main failure modes were the formation of vertical cracks and delamination in the outlayer of substrate, and the appearance of coating spallation. The residual stress, thermal stress and oxidation of substrate near the substrate/metal layer interface were responsible for coating failure, while the oxidation of substrate near the substrate/coating interface was the dominant one.

  13. Synthesis of nickel oxide - zirconia composites by coprecipitation route followed by hydrothermal treatment

    International Nuclear Information System (INIS)

    Yoshito, Walter Kenji; Ussui, Valter; Lazar, Dolores Ribeiro Ricci; Paschoal, Jose Octavio Armani

    2009-01-01

    Nickel oxide-yttria stabilized zirconia (NiO-YSZ) for use as solid oxide fuel cell anode were synthesized by coprecipitation to obtain amorphous zirconia and crystallized β-nickel gels of the corresponding metal hydroxides. Hydrothermal treatment at 200°C and 220 psi from 2 up to 16 hours, under stirring, was performed to produce nanocrystalline powder. The as-synthesized powders were uniaxially pressed and sintered in air. Powders were characterized by X-ray diffraction, laser scattering, scanning and transmission electron microscopy (SEM/TEM), gas adsorption technique (BET) and TGDTA thermal analysis. Ceramic samples were characterized by dilatometric analysis and density measurements by Archimedes method. The characteristics of hydrothermally synthesized powders and compacts were compared to those produced without temperature and pressure application. Crystalline powders were obtained after hydrothermal process, excluding the calcination step from this route. The specific surface area of powders decreases with increasing time of hydrothermal treatment while the agglomerate mean size is not affected by this parameter. (author)

  14. Preparation and characterization of TiO2 and Si-doped octacalcium phosphate composite coatings on zirconia ceramics (Y-TZP) for dental implant applications

    Science.gov (United States)

    Bao, Lei; Liu, Jingxiao; Shi, Fei; Jiang, Yanyan; Liu, Guishan

    2014-01-01

    In order to prevent the low temperature degradation and improve the bioactivity of zirconia ceramic implants, TiO2 and Si-doped octacalcium phosphate composite coating was prepared on zirconia substrate. The preventive effect on low temperature degradation and surface morphology of the TiO2 layer were studied. Meanwhile, the structure and property changes of the bioactive coating after doping Si were discussed. The results indicate that the dense TiO2 layer, in spite of some microcracks, inhibited the direct contact of the water vapor with the sample's surface and thus prevented the low temperature degradation of zirconia substrates. The acceleration aging test shows that the ratio of the monoclinic phase transition decreased from 10% for the original zirconia substrate to 4% for the TiO2-coated substrate. As to the Si-doped octacalcium phosphate coating prepared by biomimetic method, the main phase composition of the coating was octacalcium phosphate. The morphology of the coating was lamellar-like, and the surface was uniform and continuous with no cracks being observed. It is suggested that Si was added into the coating both through substituting for PO43- and doping as NaSiO3.

  15. Synthesis and ceramic processing of zirconia alumina composites for application as solid oxide fuel cell electrolytes; Sintese e processamento de compositos de zirconia-alumina para aplicacao como eletrolito em celulas a combustivel de oxido solido

    Energy Technology Data Exchange (ETDEWEB)

    Garcia, Rafael Henrique Lazzari

    2007-07-01

    The global warmness and the necessity to obtain clean energy from alternative methods than petroleum raises the importance of developing cleaner and more efficient systems of energy generation, among then, the solid oxide fuel cell (SOFC). Cubic stabilized zirconia (CSZ) has been the most studied material as electrolyte in SOFC, due to its ionic conductivity and great stability at operation conditions. However, its low fracture toughness difficulties its application as a thin layer, what could lead to an improvement of cell efficiency. In this sense, the alumina addition in CSZ forms a composite, which can shift its mechanical properties, without compromising its electrical properties. In this work, coprecipitation synthesis route and ceramic processing of zirconia-alumina composites were studied, in order to establish optimum conditions to attain high density, homogeneous microstructure, and better mechanical properties than CSZ, without compromising ionic conductivity. For this purpose, composites containing up to 40 wt % of alumina, in a 9 mol % yttria-stabilized zirconia (9Y-CSZ) matrix were evaluated. In order to optimize the synthesis of the composites, a preliminary study of powder obtaining and processing were carried out, at compositions containing 20 wt % of alumina, in 9Y-CSZ. The ceramic powders were characterized by helium picnometry, X-ray diffraction, scanning electronic microscopy, transmission electronic microscopy, thermogravimetry, differential scanning calorimetry, granulometry by laser diffraction and gas adsorption (BET). The characterization of sinterized compacts were performed by X-ray diffraction, scanning electron microscopy, optical microscopy, density measurements, Vickers indentation and impedance spectroscopy. The obtained results show that the alumina addition, in the 9Y-CSZ matrix powders, raises the specific surface area, promotes deagglomeration of powders and elevates the oxides crystallization temperature, requiring higher

  16. Zirconia - the cinderella transformation

    International Nuclear Information System (INIS)

    Hannink, R.H.J.

    1999-01-01

    Zirconia and its alloys have formed a turning point in mechanical property developments of engineering ceramics. This can be stated primarily because zirconia alloys were one of the first ceramic systems in which it was demonstrated that the mechanical properties could be tailored using careful control of composition, powder processing and thermal treatment. For the improved mechanical properties to be captured in zirconia-based or containing ceramics, control of the tetragonal to monoclinic transformation is required. Through microstructural control, zirconia-based ceramics can be tailored to form some of the strongest and toughest ceramics yet developed. By carefully controlling the use of various dopants (alloying additions), a variety of microstructures can be produced all of which may exhibit transformation toughening. While success in capturing the benefits of transformation toughening relies on adequate powder processing techniques, this review is restricted to outlining the phase control and behaviour that make zirconia and its alloys such a scientifically fascinating and rewarding system for study and a commercially appealing ceramic material

  17. The effect of explosive compacting on the properties of the 60% LaCr03-40% Cr cermet

    International Nuclear Information System (INIS)

    Atroshenko, E.S.; Barykin, B.M.; Ivanov, V.S.; Krasulin, Yu.L.; Spirodonov, E.G.

    1976-01-01

    A technique of explosive compacting of composite cermet materials (M + M0) has been used for producing large blanks with a density close to theoretical. A study has been made of the properties of an explosively compacted 60% LaCr0 3 -40% Cr cermet over a wide temperature range. Cermets compacted explosively are shown to have a number of advantages over ones prepared by conventional powder metallurgical techniques. (author)

  18. Study on the influences of reduction temperature on nickel-yttria-stabilized zirconia solid oxide fuel cell anode using nickel oxide-film electrode

    Science.gov (United States)

    Jiao, Zhenjun; Ueno, Ai; Suzuki, Yuji; Shikazono, Naoki

    2016-10-01

    In this study, the reduction processes of nickel oxide at different temperatures were investigated using nickel-film anode to study the influences of reduction temperature on the initial performances and stability of nickel-yttria-stabilized zirconia anode. Compared to conventional nickel-yttria-stabilized zirconia composite cermet anode, nickel-film anode has the advantage of direct observation at nickel-yttria-stabilized zirconia interface. The microstructural changes were characterized by scanning electron microscopy. The reduction process of nickel oxide is considered to be determined by the competition between the mechanisms of volume reduction in nickel oxide-nickel reaction and nickel sintering. Electrochemical impedance spectroscopy was applied to analyze the time variation of the nickel-film anode electrochemical characteristics. The anode performances and microstructural changes before and after 100 hours discharging and open circuit operations were analyzed. The degradation of nickel-film anode is considered to be determined by the co-effect between the nickel sintering and the change of nickel-yttria-stabilized zirconia interface bonding condition.

  19. Utilization of niobium pentoxide as additive for reducing the ''in situ'' reaction temperature of ceramic composites in the system mullite-zirconia

    International Nuclear Information System (INIS)

    Melo, F.C.L. de; Cairo, C.A.A.; Piorino Neto, F.; Cunha, P.A.; Devezas, T.C.

    1988-01-01

    Ceramics Composites of the system mullite-zirconia were produced trough reaction sintering, following the equation: 2ZrSiO 4 +3Al 2 O 3 +x(Al 2 O 3 +Nb 2 O 5 )--> 2ZrO 2 +Al 6 Si 2 O 13 +2xAlNbO 4 , with different x values (0.05,0.1 e 0.25), trying to investigate the role of niobia as sintering aid. Through x-ray diffraction was evaluated the fraction of zirconia tetragonal phase retained in the ceramic matrix, and the produced composites were caracterized as to the apparent porosity and density, sintering shrinkage and rupture strenght. The reaction sintering temperature was reduced from 1600 0 C (x=0) to 1400 0 C (with x=0.1). (author) [pt

  20. Effect of Alumina Addition to Zirconia Nano-composite on Low Temperature Degradation Process and Biaxial Strength

    Directory of Open Access Journals (Sweden)

    Moluk Aivazi

    2016-12-01

    Full Text Available Ceramic dental materials have been considered as alternatives to metals for dental implants application. In this respect, zirconia tetragonal stabilized with %3 yttrium, is of great importance among the ceramic materials for endosseous dental implant application. Because of its good mechanical properties and color similar to tooth. The aim and novelty of this study was to design and prepare Y-TZP nano-composite to reduce the degradation process at low temperature by alumina addition and maintaining submicron grain sized. Also, flexural strength of nano-composite samples was evaluated. Toward this purpose, alumina-Y-TZP nano-composites containing 0–30 vol% alumina (denoted as A-Y-TZP 0-30 were fabricated using α-alumina and Y-TZP nano-sized by sintering pressure less method. The synthesized samples were characterized using x-ray diffraction, field emission scanning electron microscopy equipped with energy dispersive x-ray spectroscopy techniques. Nano-composite samples with high density (≥96% and grain sized of ≤ 400 nm was obtained by sintering at 1270 °C for 170 min. After low temperature degradation test (LTD, A-Y-TZP20 and A-Y-TZP30 not showed monoclinic phase and the flexural strength in all of samples were higher than A-Y-TZP0. It was concluded that the grains were remained in submicron sized and A-Y-TZP20 and A-Y-TZP30 did not present biaxial strength reduction after LTD test.

  1. Fracture resistance of endodontically treated teeth restored with Zirconia filler containing composite core material and fiber posts.

    Science.gov (United States)

    Jeaidi, Zaid Al

    2016-01-01

    To assess the fracture resistance of endodontically treated teeth with a novel Zirconia (Zr) nano-particle filler containing bulk fill resin composite. Forty-five freshly extracted maxillary central incisors were endodontically treated using conventional step back preparation and warm lateral condensation filling. Post space preparation was performed using drills compatible for fiber posts (Rely X Fiber Post) on all teeth (n=45), and posts were cemented using self etch resin cement (Rely X Unicem). Samples were equally divided into three groups (n=15) based on the type of core materials, ZirconCore (ZC) MulticCore Flow (MC) and Luxacore Dual (LC). All specimens were mounted in acrylic resin and loads were applied (Universal testing machine) at 130° to the long axis of teeth, at a crosshead speed of 0.5 mm/min until failure. The loads and the site at which the failures occurred were recorded. Data obtained was tabulated and analyzed using a statistical program. The means and standard deviations were compared using ANOVA and Multiple comparisons test. The lowest and highest failure loads were shown by groups LC (18.741±3.02) and MC (25.16±3.30) respectively. Group LC (18.741±3.02) showed significantly lower failure loads compared to groups ZC (23.02±4.21) and MC (25.16±3.30) (pcomposite cores was comparable to teeth restored with conventional Zr free bulk fill composites. Zr filled bulk fill composites are recommended for restoration of endodontically treated teeth as they show comparable fracture resistance to conventional composite materials with less catastrophic failures.

  2. Preparation of one-step NiO/Ni-CGO composites using factorial design; Efeitos do processamento e do teor de formador de poros na microestrutura de cermets Ni-CGO

    Energy Technology Data Exchange (ETDEWEB)

    Araujo, A.J.M. de; Sousa, A R.O. de; Camposa, L.F.A.; Macedo, D.A. [Universidade Federal da Paraiba (UFPB), Joao Pessoa, PB (Brazil); Loureiro, F. J.A.; Fagg, D.P., E-mail: allanjp1993@hotmail.com [Universidade de Aveiro (Portugal)

    2016-07-01

    This work deals with the synthesis, processing and characterization of NiO/Ni- CGO composite materials as potential solid oxide fuel cell (SOFC) anodes. The particulate materials were obtained by a one-step synthesis method and characterized by thermal analysis (prior to calcination) and X-ray diffraction (calcined powder). The ceramic processing of samples containing from 30 to 70 wt.% NiO was carried out by factorial design. Besides the NiO content controlled during the chemical synthesis, the impacts of the pore-former content (citric acid, used in proportions of 0, 7.5 and 15 wt.%) and the sintering temperature (1300, 1350 and 1400 °C) were also investigated. The open porosity of NiO-CGO composites and reduced Ni-CGO cermets was modeled as a function of factors (NiO content, citric acid content and sintering temperature) and interaction of factors. (author)

  3. Durability of cermet ionomer cement conditioned in different media.

    Science.gov (United States)

    el-Din, I M

    1992-01-01

    The glass ionomer cement has exhibited significant adhesion to hard tooth structures, and good cariostatic properties. The sintering of the silver alloy powder and glass ionomer cement "cermet cement" has provided additional improvement in the physical properties of the restorative material. These were flexural resistance, wear resistance, increased radio-opacity, hardness and porosity. The improvement in the physical properties of the cermet glass cements has provided an extension in their clinical use as core build up, lining for inlays, amalgam and composite restoratives, fissure filling, restoration of primary teeth, class II tunnel preparation, treatment of root caries and repair of defective metal margins in crown and inlays.

  4. Dense cermets containing fine grained ceramics and their manufacture

    International Nuclear Information System (INIS)

    King, H.L.

    1986-01-01

    This patent describes a method of producing a ceramic-metal composite (cermet) containing boride-oxide ceramic having components of a first metal boride and a second metal oxide, which ceramic is in mixture in the cermet with elemental metal of the second metal, wherein the cermet is produced by sintering a reaction mixture of the first metal oxide, boron oxide and the elemental second metal. The improvement consists of: combining for the reaction mixture; A. (a) first metal oxide; (b) boron oxide; (c) ceramic component in very finely divided form; and (d) elemental second metal in very finely divided form and in an amount of at least a 100 percent molar excess beyond that amount stoichiometrically required to produce the second metal oxide during sintering; and B. sintering the reaction mixture in inert gas atmosphere

  5. Study of microstructure and mechanical properties of ceramics composites alumina-zirconia reinforced with yttria for inert coating of metal matrices used in the petroleum industry

    International Nuclear Information System (INIS)

    Pontual, J.O.; Silva, N.D.G.; Ferreira, R.A.S.; Yadava, Y.P.

    2014-01-01

    The storage and transportation of crude oil is complicated due to the hostile environment provided by this. Under these conditions, it is imperative to search for alternative solutions, using an inert coating to protect from corrosion caused by crude oil. In this work, alumina-zirconia ceramic composites with 5-20%w zirconia and 1 - 2%w yttria were produced through thermomechanical process. The structural and microstructural characterization of the sintered material was carried out by X-ray diffraction and scanning electron microscopy. Mechanical properties were analyzed by Vickers hardness tests. Currently, the pads are submerged in crude oil and after 30-60 days will be removed and sent for stability test.(author)

  6. Manufacture of annular cermet articles

    Science.gov (United States)

    Forsberg, Charles W.; Sikka, Vinod K.

    2004-11-02

    A method to produce annular-shaped, metal-clad cermet components directly produces the form and avoids multiple fabrication steps such as rolling and welding. The method includes the steps of: providing an annular hollow form with inner and outer side walls; filling the form with a particulate mixture of ceramic and metal; closing, evacuating, and hermetically sealing the form; heating the form to an appropriate temperature; and applying force to consolidate the particulate mixture into solid cermet.

  7. Plasma-sprayed tantalum/alumina cermets

    International Nuclear Information System (INIS)

    Kramer, C.M.

    1977-12-01

    Cermets of tantalum and alumina were fabricated by plasma spraying, with the amount of alumina varied from 0 to 65 percent (by volume). Each of four compositions was then measured for tensile strength, elastic modulus, and coefficient of thermal expansion. In general, strength and strain to failure decreased with increasing alumina content: 62 MPa for 100 percent Ta to 19 MPa for 35 v percent Ta. A maximum of 0.1 percent strain was observed for the sprayed 100 percent Ta specimens. The coefficient of thermal expansion measured for the pure Ta was 6.2 (10 -6 )/K

  8. Biocompatibility assessment of spark plasma-sintered alumina-titanium cermets.

    Science.gov (United States)

    Guzman, Rodrigo; Fernandez-García, Elisa; Gutierrez-Gonzalez, Carlos F; Fernandez, Adolfo; Lopez-Lacomba, Jose Luis; Lopez-Esteban, Sonia

    2016-01-01

    Alumina-titanium materials (cermets) of enhanced mechanical properties have been lately developed. In this work, physical properties such as electrical conductivity and the crystalline phases in the bulk material are evaluated. As these new cermets manufactured by spark plasma sintering may have potential application for hard tissue replacements, their biocompatibility needs to be evaluated. Thus, this research aims to study the cytocompatibility of a novel alumina-titanium (25 vol. % Ti) cermet compared to its pure counterpart, the spark plasma sintered alumina. The influence of the particular surface properties (chemical composition, roughness and wettability) on the pre-osteoblastic cell response is also analyzed. The material electrical resistance revealed that this cermet may be machined to any shape by electroerosion. The investigated specimens had a slightly undulated topography, with a roughness pattern that had similar morphology in all orientations (isotropic roughness) and a sub-micrometric average roughness. Differences in skewness that implied valley-like structures in the cermet and predominance of peaks in alumina were found. The cermet presented a higher surface hydrophilicity than alumina. Any cytotoxicity risk associated with the new materials or with the innovative manufacturing methodology was rejected. Proliferation and early-differentiation stages of osteoblasts were statistically improved on the composite. Thus, our results suggest that this new multifunctional cermet could improve current alumina-based biomedical devices for applications such as hip joint replacements. © The Author(s) 2015.

  9. Characteristics and fabrication of cermet spent nuclear fuel casks: ceramic particles embedded in steel

    Energy Technology Data Exchange (ETDEWEB)

    Forsberg, C.W.; Swaney, P.M.; Tiegs, T.N. [Oak Ridge National Lab., Oak Ridge, TN (United States)

    2004-07-01

    Cermets are being investigated as an advanced material of construction for casks that can be used for storage, transport, or disposal of spent nuclear fuel (SNF). Cermets, which consist of ceramic particles embedded in steel, are a method to incorporate brittle ceramics with highly desirable properties into a strong ductile metal matrix with a high thermal conductivity, thus combining the best properties of both materials. Traditional applications of cermets include tank armor, vault armor, drill bits, and nuclear test-reactor fuel. Cermets with different ceramics (DUO{sub 2}, Al{sub 2}O{sub 3}, Gd{sub 2}O{sub 3}, etc.) are being investigated for the manufacture of SNF casks. Cermet casks offer four potential benefits: greater capacity (more SNF assemblies) for the same gross weight cask, greater capacity (more SNF assemblies) for the same external dimensions, improved resistance to assault, and superior repository performance. These benefits are achieved by varying the composition, volume fraction, and particulate size of the ceramic particles in the cermet with position in the cask body. Addition of depleted uranium dioxide (DUO{sub 2}) to the cermet increases shielding density, improves shielding effectiveness, and increases cask capacity for a given cask weight or size. Addition of low-density aluminium oxide (Al{sub 2}O{sub 3}) to the outer top and bottom sections of the cermet cask, where the radiation levels are lower, can lower cask weight without compromising shielding. The use of Al2O3 and other oxides, in appropriate locations, can increase resistance to assault. Repository performance may be improved by compositional control of the cask body to (1) create a local geochemical environment that slows the long-term degradation of the SNF and (2) enables the use of DUO{sub 2} for longterm criticality control. While the benefits of using cermets follow directly from their known properties, the primary challenge is to develop low-cost methods to fabricate

  10. Characteristics and fabrication of cermet spent nuclear fuel casks: ceramic particles embedded in steel

    International Nuclear Information System (INIS)

    Forsberg, C.W.; Swaney, P.M.; Tiegs, T.N.

    2004-01-01

    Cermets are being investigated as an advanced material of construction for casks that can be used for storage, transport, or disposal of spent nuclear fuel (SNF). Cermets, which consist of ceramic particles embedded in steel, are a method to incorporate brittle ceramics with highly desirable properties into a strong ductile metal matrix with a high thermal conductivity, thus combining the best properties of both materials. Traditional applications of cermets include tank armor, vault armor, drill bits, and nuclear test-reactor fuel. Cermets with different ceramics (DUO 2 , Al 2 O 3 , Gd 2 O 3 , etc.) are being investigated for the manufacture of SNF casks. Cermet casks offer four potential benefits: greater capacity (more SNF assemblies) for the same gross weight cask, greater capacity (more SNF assemblies) for the same external dimensions, improved resistance to assault, and superior repository performance. These benefits are achieved by varying the composition, volume fraction, and particulate size of the ceramic particles in the cermet with position in the cask body. Addition of depleted uranium dioxide (DUO 2 ) to the cermet increases shielding density, improves shielding effectiveness, and increases cask capacity for a given cask weight or size. Addition of low-density aluminium oxide (Al 2 O 3 ) to the outer top and bottom sections of the cermet cask, where the radiation levels are lower, can lower cask weight without compromising shielding. The use of Al2O3 and other oxides, in appropriate locations, can increase resistance to assault. Repository performance may be improved by compositional control of the cask body to (1) create a local geochemical environment that slows the long-term degradation of the SNF and (2) enables the use of DUO 2 for longterm criticality control. While the benefits of using cermets follow directly from their known properties, the primary challenge is to develop low-cost methods to fabricate casks with variable cermet compositions

  11. Solid solution cermet: (Ti,Nb)(CN)-Ni cermet.

    Science.gov (United States)

    Kwon, Hanjung; Jung, Sun-A

    2014-11-01

    Solid solution powders without W, (Ti,Nb)(CN) powders with a B1 structure (NaCl like), were synthesized by high energy milling and carbothermal reduction in nitrogen. The range of molar ratios of Ti/Nb for forming complete (Ti,Nb)(CN) phase was broader than that of Ti/W for the (Ti,W)(CN) phase because carbide or carbonitride of Nb had a B1 crystal structure identical to Ti(CN) while WC had a hexagonal crystal structure. The results revealed that the hardness of (Ti,Nb)(CN)-Ni cermets was higher than that of (Ti,W)(CN)-Ni cermets. The lower density of the (Ti,Nb)(CN) powder contributed to the higher hardness compared to (Ti,W)(CN) because the volumetric ratio of (Ti,Nb)(CN) in the (Ti,Nb)(CN)-Ni cermets was higher than that of (Ti,Nb)(CN) in the (Ti,W)(CN)-Ni cermets at the same weight ratio of Ni. Additionally, it was assumed that intrinsic the properties of (Ti,Nb)(CN) could also be the cause for the high hardness of the (Ti,Nb)(CN)-Ni cermets.

  12. In vitro caries-inhibitory properties of a silver cermet.

    Science.gov (United States)

    Swift, E J

    1989-06-01

    Recurrent caries is one of the primary causes of failure of dental restorations. One method for reducing the frequency and severity of this problem is the use of fluoride-releasing restorative materials. The glass-ionomer cements are a type of fluoride-releasing material. They have been used extensively in recent years for a variety of clinical applications. However, in comparison with other restorative materials such as amalgam and composite resins, glass ionomers have relatively poor physical properties. Sintering of silver particles to glass-ionomer powder is a means of improving these physical properties. The sintered material is called a silver-glass ionomer or silver cermet. This study examined the in vitro caries-inhibitory potential of a silver cement by means of two methods. First, long-term fluoride release was measured. Second, an artificial caries system was used for evaluation of caries inhibition by cerment restorations in extracted teeth. In comparison with a standard glass-ionomer restorative material, fluoride release from the cermet material was significantly less throughout a 12-month period. The results from the artificial caries system indicated that this decreased fluoride release corresponded with a lesser degree of caries inhibition. Lesions around cermet restorations in both enamel and root surfaces were significantly more severe than those around conventional glass-ionomer restorations. However, in comparison with amalgam and composite resin restorations, the cermet did have some cariostatic activity.

  13. Investigation of a Cermet Gas-turbine-blade Material of Titanium Carbide Infiltrated with Hastalloy C

    Science.gov (United States)

    Hoffman, Charles A

    1955-01-01

    A cermet composition was investigated as a potential material for gas-turbine blades. Blades of HS-21 alloy were also operated in the engine simultaneously to provide a basis of comparison. The cermet blades survived as long as approximately 312-1/2 hours at about 1500 degrees F with an average midspan centrifugal stress of approximately 11,500 psi. The alloy blade midspan stress was about 15,300 psi. Because of extensive damage to both types of blade due to external causes, a reliable comparison of operating lives could not be made. The cermet blades tended to fail in the airfoil rather than in the base, although the base was the usual location of failure in a prior study of cold-pressed and sintered cermets of other compositions with the same blade shape.

  14. Direct metal brazing to cermet feedthroughs

    International Nuclear Information System (INIS)

    Hopper, A.C. Jr.

    1984-01-01

    An improved method for brazing metallic components to a cermet surface in an alumina substrate eliminates the prior art metallized layer over the cermet via and adjoining alumina surfaces. Instead, a nickel layer is applied over the cermet surface only and metallic components are brazed directly to this nickel coated cermet surface. As a result, heretofore unachievable tensile strength joints are produced. In addition, cermet vias with their brazed metal components can be spaced more closely in the alumina substrate because of the elimination of the prior art metallized alumina surfaces

  15. Effect of platelet orientation on the properties of alumina platelet zirconia matrix composites

    DEFF Research Database (Denmark)

    Toft Sørensen, O.; Li, W.-Y.

    1996-01-01

    Platelet alignment in Al2O3pl - TZ3YS composites formed by injection moulding, slip casting, and tape casting, has been examined. Mechanical properties have been determined in terms of flexural strength and fracture toughness, with respect to materials formed by different techniques, and to the p...... 220 and 300 degrees C, which is approximately in the same range as for the matrix....

  16. Compressive strength and magnetic properties of calcium silicate-zirconia-iron (III) oxide composite cements

    Science.gov (United States)

    Ridzwan, Hendrie Johann Muhamad; Shamsudin, Roslinda; Ismail, Hamisah; Yusof, Mohd Reusmaazran; Hamid, Muhammad Azmi Abdul; Awang, Rozidawati Binti

    2018-04-01

    In this study, ZrO2 microparticles and γ-Fe2O3 nanoparticles have been added into calcium silicate based cements. The purpose of this experiment was to investigate the compressive strength and magnetic properties of the prepared composite cement. Calcium silicate (CAS) powder was prepared by hydrothermal method. SiO2 and CaO obtained from rice husk ash and limestone respectively were autoclaved at 135 °C for 8 h and sintered at 950°C to obtain CAS powder. SiO2:CaO ratio was set at 45:55. CAS/ZrO2 sample were prepared with varying ZrO2 microparticles concentrations by 0-40 wt. %. Compressive strength value of CAS/ZrO2 cements range from 1.44 to 2.44 MPa. CAS/ZrO2/γ-Fe2O3 sample with 40 wt. % ZrO2 were prepared with varying γ-Fe2O3 nanoparticles concentrations (1-5 wt. %). The additions of γ-Fe2O3 nanoparticles showed up to twofold increase in the compressive strength of the cement. X-Ray diffraction (XRD) results confirm the formation of mixed phases in the produced composite cements. Vibrating sample magnetometer (VSM) analysis revealed that the ferromagnetic behaviour has been observed in CAS/ZrO2/γ-Fe2O3 composite cements.

  17. Nucleation and growth characteristics of cavities during the early stages of tensile creep deformation in a superplastic zirconia-20 wt% alumina composite

    International Nuclear Information System (INIS)

    Owen, D.M.; Chokshi, A.H.; Nutt, S.R.

    1997-01-01

    Constant-stress tensile creep experiments on a superplastic 3-mol%-yttria-stabilized tetragonal zirconia composite with 20 wt% alumina revealed that cavities nucleate relatively early during tensile deformation. The number of cavities nucleated increases with increasing imposed stress. The cavities nucleate at triple points associated largely with an alumina grain, and then grow rapidly in a cracklike manner to attain dimensions on the order of the grain facet size. It is suggested that coarser-grained superplastic ceramics exhibit lower ductility due to the ease in formation of such grain boundary facet-cracks and their interlinkage to form a macroscopic crack of critical dimensions

  18. Cermet materials prepared by combustion synthesis and metal infiltration

    Science.gov (United States)

    Holt, Joseph B.; Dunmead, Stephen D.; Halverson, Danny C.; Landingham, Richard L.

    1991-01-01

    Ceramic-metal composites (cermets) are made by a combination of self-propagating high temperature combustion synthesis and molten metal infiltration. Solid-gas, solid-solid and solid-liquid reactions of a powder compact produce a porous ceramic body which is infiltrated by molten metal to produce a composite body of higher density. AlN-Al and many other materials can be produced.

  19. The elastic modulus of alumina-zirconia composite using through transmission ultrasonics

    International Nuclear Information System (INIS)

    Tan, K.S.; Hing, P.

    1996-01-01

    The elastic modulus of unstabilized Al 2 O 3 -ZrO 2 composites is determined from ultrasonic velocities and density measurements. The dynamic elastic modulus and the density of the green unstabilized Al 2 O 3 -ZrO 2 follow the rule of mixture. However, the elastic modulus and density of the sintered Al 2 O 3 -ZrO 2 do not follow the rule of mixture. The elastic modulus and diametrical compressive fracture stress of the Al 2 O 3 can be enhanced by (1) a high green (before sintering) compacting pressure and (2) addition of about 3wt% unstabilized ZrO 2 at a sintering time of two hours at 1550 degC. The ZrO 2 is found to improve the bulk density of the composite by a reduction in the porosity. This improves the elastic modulus and the diametrical compressive fracture stress. The thermal expansion on cooling with > 25wt% ZrO 2 in the Al 2 O 3 matrix has also been established. (author)

  20. Saturation of cermets based on titanium carbide and diboride by metal melts

    International Nuclear Information System (INIS)

    Kitsaj, A.A.; Tsyganova, T.V.; Ordan'yan, S.S.

    1985-01-01

    Different sintered composites - TiC-Ni(Mo), TiC-Fe (Ni), TiB 2 -Fe (Mo) are studied for their interaction in contact with metal melts at the temperature of liquid phase existence in the cermet. Due to structural and physicochemical similarity of cermets the processes occuring with contact interaction are identical: additional quantity of liquid is imbibed into the cermet resulting in reconstruction of the solid phase frame and volumetric growth of the specimen. Elongation of the specimens permits concluding that the intensity of the solid phase (frame) reconstruction process in the cermet TiC-Fe (Ni) is lower than in TiC-Ni (Mo) and TiB 2 -Fe (Mo) systems. In the TiC-Fe (Ni) cermet it causes prevalence of the processes of diffusional levellng for compositions of the metal-binder and contacting metal over the process of laminar flow of the melt into the specimen. Choosing the composite components it is possible to control intensity of the cermet saturation by the additional quantity of the melt and distribution of the liquid phase in the article volume

  1. Effect of surface composition of yttrium-stabilized zirconia on partial oxidation of methane to synthesis gas.

    NARCIS (Netherlands)

    Zhu, J.J.; van Ommen, J.G.; Knoester, A.; Lefferts, Leonardus

    2005-01-01

    Catalytic partial oxidation of methane to synthesis gas (CPOM) over yttrium-stabilized zirconia (YSZ) was studied within a wide temperature window (500¿1100 °C). The catalysts were characterized by X-ray fluorescence (XRF) and low-energy ion scattering (LEIS). The influence of calcination

  2. Microcracking and mechanical properties of Hafnia-Zirconia toughened alumina composites

    International Nuclear Information System (INIS)

    Li, H.P.S.; Stevens, R.

    1995-01-01

    Despite the remarkably similar crystal structures and phase transformations of HfO 2 and ZrO 2 , the tetragonal to monoclinic transformation temperature for HfO 2 takes place six hundred degrees higher than that for ZrO 2 . This suggests the potential for HfO 2 as an engineering material for use at elevated temperatures (>700 C). Alloying HfO 2 with ZrO 2 has been suggested a feasible high-temperature toughening strategy for ZrO 2 -toughened ceramics. The role of ZrO 2 as a second phase toughening agent for ceramic composites has long been recognised and a considerable number of studies reported. In contrast, HfO 2 -toughened ceramics, have not been investigated in detail. This paper gives an account of composite ceramics consisting of an Al 2 O 3 matrix, mixed with unstabilised (Zr-Hf)O 2 inclusions containing volume fractions, of 0, 1, 5, 10, 15, and 25 vol. %, developed to investigate the effects of the second phase content on the microstructure and mechanical properties. A simple cubic packing model of microcracking, based on an ''end-point'' thermodynamic approach, is discussed with respect to microcrack extension for a critical volume fraction of second phase content. The results show an Al 2 O 3 matrix containing 5 vol. % of Hf 0.25 Zr 0.75 O 2 inclusions to give the optimum properties. Using the packing model, the critical volume fraction is predicted at 10 vol. %, which is in a good agreement with experimental results. (orig.)

  3. The Impact of Plasma Treatment of Cercon® Zirconia Ceramics on Adhesion to Resin Composite Cements and Surface Properties.

    Science.gov (United States)

    Tabari, Kasra; Hosseinpour, Sepanta; Mohammad-Rahimi, Hossein

    2017-01-01

    Introduction: In recent years, the use of ceramic base zirconia is considered in dentistry for all ceramic restorations because of its chemical stability, biocompatibility, and good compressive as well as flexural strength. However, due to its chemical stability, there is a challenge with dental bonding. Several studies have been done to improve zirconia bonding but they are not reliable. The purpose of this research is to study the effect of plasma treatment on bonding strength of zirconia. Methods: In this in vitro study, 180 zirconia discs' (thickness was 0.85-0.9 mm) surfaces were processed with plasma of oxygen, argon, air and oxygen-argon combination with 90-10 and 80-20 ratio (n=30 for each group) after being polished by sandblast. Surface modifications were assessed by measuring the contact angle, surface roughness, and topographical evaluations. Cylindrical Panavia f2 resin-cement and Diafill were used for microshear strength bond measurements. The data analysis was performed by SPSS 20.0 software and one-way analysis of variance (ANOVA) and Tukey test as the post hoc. Results: Plasma treatment in all groups significantly reduces contact angle compare with control ( P =0.001). Topographic evaluations revealed coarseness promotion occurred in all plasma treated groups which was significant when compared to control ( P <0.05), except argon plasma treated group that significantly decreased surface roughness ( P <0.05). In all treated groups, microshear bond strength increased, except oxygen treated plasma group which decreased this strength. Air and argon-oxygen combination (both groups) significantly increased microshear bond strength ( P <0.05). Conclusion: According to this research, plasmatic processing with dielectric barrier method in atmospheric pressure can increase zirconia bonding strength.

  4. Preparation of Calcined Zirconia-Carbon Composite from Metal Organic Frameworks and Its Application to Adsorption of Crystal Violet and Salicylic Acid

    Directory of Open Access Journals (Sweden)

    Zubair Hasan

    2016-03-01

    Full Text Available Zirconia-carbon (ZC composites were prepared via calcination of Zr-based metal organic frameworks, UiO-66 and amino-functionalized UiO-66, under N2 atmosphere. The prepared composites were characterized using a series of instrumental analyses. The surface area of the ZC composites increased with the increase of calcination temperature, with the formation of a graphite oxide phase observed at 900 °C. The composites were used for adsorptive removal of a dye (crystal violet, CV and a pharmaceutical and personal care product (salicylic acid, SA. The increase of the calcination temperature resulted in enhanced adsorption capability of the composites toward CV. The composite calcined at 900 °C exhibited a maximum uptake of 243 mg·g−1, which was much greater than that by a commercial activated carbon. The composite was also effective in SA adsorption (102 mg·g−1, and N-functionalization of the composite further enhanced its adsorption capability (109 mg·g−1. CV adsorption was weakly influenced by solution pH, but was more dependent on the surface area and pore volume of the ZC composite. Meanwhile, SA adsorption showed strong pH dependence, which implies an active role of electrostatic interactions in the adsorption process. Base-base repulsion and hydrogen bonding are also suggested to influence the adsorption of CV and SA, especially for the N-functionalized composite.

  5. The effect of Co particle structures on the mechanical properties and microstructure of TiCN-based cermets

    International Nuclear Information System (INIS)

    Deng, Y.; Jiang, X.Q.; Zhang, Y.H.; Chen, H.; Tu, M.J.; Deng, L.; Zou, J.P.

    2016-01-01

    Ti(C,N) based cermets are composite materials composed of a hard phase and a binder phase structure. Cubic-structured Co particles are the best choice for the binder phase of Ti(C,N) based cermets due to their excellent toughness performance. However, the application of β-Co particles in cermets has not been reported in the literature so far. In this pioneer study, ultrafine Ti(C,N) based cermet samples were prepared by separately using Co particles of different structures as the binder phase, and the effect of the Co particle structures on the mechanical properties and microstructure of the cermets were studied: First, the Empirical Electron Theory was used to calculate the difference in the interface density (∆ρ) for different crystals, and the interface combined strength between the hard phase of different structures containing Co particles were evaluated. Second, we systematically investigated the evolution of the microstructures of the two cermets during the sintering process, and evaluated the characteristics of the microstructure (which determines the properties of the cermets). Finally, the mechanical properties of the samples were tested, and the performances of the Co structures were evaluated. The results show that β-Co particles can optimize the cermet microstructure, which leads to excellent mechanical performance.

  6. The effect of Co particle structures on the mechanical properties and microstructure of TiCN-based cermets

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Y. [Chongqing University of Arts and Science, Chongqing 402160 (China); State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Jiang, X.Q. [Southwest University, Chongqing Academy Science and Technology, Chongqing 4100715 (China); Zhang, Y.H.; Chen, H.; Tu, M.J. [Chongqing University of Arts and Science, Chongqing 402160 (China); Deng, L., E-mail: dengying.163@163.com [Chengdu Chengliang Tool Group Co., Ltd., Chengdu 610056 (China); Zou, J.P., E-mail: 1042551842@qq.com [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China)

    2016-10-15

    Ti(C,N) based cermets are composite materials composed of a hard phase and a binder phase structure. Cubic-structured Co particles are the best choice for the binder phase of Ti(C,N) based cermets due to their excellent toughness performance. However, the application of β-Co particles in cermets has not been reported in the literature so far. In this pioneer study, ultrafine Ti(C,N) based cermet samples were prepared by separately using Co particles of different structures as the binder phase, and the effect of the Co particle structures on the mechanical properties and microstructure of the cermets were studied: First, the Empirical Electron Theory was used to calculate the difference in the interface density (∆ρ) for different crystals, and the interface combined strength between the hard phase of different structures containing Co particles were evaluated. Second, we systematically investigated the evolution of the microstructures of the two cermets during the sintering process, and evaluated the characteristics of the microstructure (which determines the properties of the cermets). Finally, the mechanical properties of the samples were tested, and the performances of the Co structures were evaluated. The results show that β-Co particles can optimize the cermet microstructure, which leads to excellent mechanical performance.

  7. Cermet crucible for metallurgical processing

    Science.gov (United States)

    Boring, Christopher P.

    1995-01-01

    A cermet crucible for metallurgically processing metals having high melting points comprising a body consisting essentially of a mixture of calcium oxide and erbium metal, the mixture comprising calcium oxide in a range between about 50 and 90% by weight and erbium metal in a range between about 10 and 50% by weight.

  8. A Comparison in Mechanical Properties of Cermets of Calcium Silicate with Ti-55Ni and Ti-6Al-4V Alloys for Hard Tissues Replacement

    Science.gov (United States)

    Pramanik, Sumit; Shirazi, Seyed Farid Seyed; Mehrali, Mehdi; Yau, Yat-Huang; Abu Osman, Noor Azuan

    2014-01-01

    This study investigated the impact of calcium silicate (CS) content on composition, compressive mechanical properties, and hardness of CS cermets with Ti-55Ni and Ti-6Al-4V alloys sintered at 1200°C. The powder metallurgy route was exploited to prepare the cermets. New phases of materials of Ni16Ti6Si7, CaTiO3, and Ni31Si12 appeared in cermet of Ti-55Ni with CS and in cermet of Ti-6Al-4V with CS, the new phases Ti5Si3, Ti2O, and CaTiO3, which were emerged during sintering at different CS content (wt%). The minimum shrinkage and density were observed in both groups of cermets for the 50 and 100 wt% CS content, respectively. The cermets with 40 wt% of CS had minimum compressive Young's modulus. The minimum of compressive strength and strain percentage at maximum load were revealed in cermets with 50 and 40 wt% of CS with Ti-55Ni and Ti-6Al-4V cermets, respectively. The cermets with 80 and 90 wt% of CS showed more plasticity than the pure CS. It concluded that the composition and mechanical properties of sintered cermets of Ti-55Ni and Ti-6Al-4V with CS significantly depend on the CS content in raw cermet materials. Thus, the different mechanical properties of the cermets can be used as potential materials for different hard tissues replacements. PMID:25538954

  9. A Comparison in Mechanical Properties of Cermets of Calcium Silicate with Ti-55Ni and Ti-6Al-4V Alloys for Hard Tissues Replacement

    Directory of Open Access Journals (Sweden)

    Azim Ataollahi Oshkour

    2014-01-01

    Full Text Available This study investigated the impact of calcium silicate (CS content on composition, compressive mechanical properties, and hardness of CS cermets with Ti-55Ni and Ti-6Al-4V alloys sintered at 1200°C. The powder metallurgy route was exploited to prepare the cermets. New phases of materials of Ni16Ti6Si7, CaTiO3, and Ni31Si12 appeared in cermet of Ti-55Ni with CS and in cermet of Ti-6Al-4V with CS, the new phases Ti5Si3, Ti2O, and CaTiO3, which were emerged during sintering at different CS content (wt%. The minimum shrinkage and density were observed in both groups of cermets for the 50 and 100 wt% CS content, respectively. The cermets with 40 wt% of CS had minimum compressive Young’s modulus. The minimum of compressive strength and strain percentage at maximum load were revealed in cermets with 50 and 40 wt% of CS with Ti-55Ni and Ti-6Al-4V cermets, respectively. The cermets with 80 and 90 wt% of CS showed more plasticity than the pure CS. It concluded that the composition and mechanical properties of sintered cermets of Ti-55Ni and Ti-6Al-4V with CS significantly depend on the CS content in raw cermet materials. Thus, the different mechanical properties of the cermets can be used as potential materials for different hard tissues replacements.

  10. Dynamic SEM wear studies of tungsten carbide cermets

    Science.gov (United States)

    Brainard, W. A.; Buckley, D. H.

    1975-01-01

    Dynamic friction and wear experiments were conducted in a scanning electron microscope. The wear behavior of pure tungsten carbide and composite with 6 and 15 weight percent cobalt binder was examined. Etching of the binder was done to selectively determine the role of the binder in the wear process. Dynamic experiments were conducted as the WC and bonded WC cermet surfaces were transversed by a 50 micron radiused diamond stylus. These studies show that the predominant wear process in WC is fracture initiated by plastic deformation. The wear of the etched cermets is similar to pure WC. The presence of the cobalt binder reduces both friction and wear. The cementing action of the cobalt reduces granular separation and promotes a dense polished layer because of its low shear strength film-forming properties. The wear debris generated from unetched surface is approximately the same composition as the bulk.

  11. Effect of adhesive luting on the fracture resistance of zirconia compared to that of composite resin and lithium disilicate glass ceramic

    Directory of Open Access Journals (Sweden)

    Myung-Jin Lim

    2017-02-01

    Full Text Available Objectives The purpose of this study was to evaluate the effect of adhesive luting on the fracture resistance of zirconia compared to that of a composite resin and a lithium disilicate glass ceramic. Materials and Methods The specimens (dimension: 2 mm × 2 mm × 25 mm of the composite resin, lithium disilicate glass ceramic, and yttria-stabilized tetragonal zirconia polycrystal (Y-TZP were prepared. These were then divided into nine groups: three non-luting groups, three non-adhesive luting groups, and three adhesive luting groups, for each restorative material. In the non-luting groups, specimens were placed on the bovine tooth without any luting agents. In the non-adhesive luting groups, only zinc phosphate cement was used for luting the specimen to the bovine tooth. In the adhesive luting groups, specimens were pretreated, and the adhesive luting procedure was performed using a self-adhesive resin cement. For all the groups, a flexural test was performed using universal testing machine, in which the fracture resistance was measured by recording the force at which the specimen was fractured. Results The fracture resistance after adhesive luting increased by approximately 29% in the case of the composite resin, 26% in the case of the lithium disilicate glass ceramic, and only 2% in the case of Y-TZP as compared to non-adhesive luting. Conclusions The fracture resistance of Y-TZP did not increased significantly after adhesive luting as compared to that of the composite resin and the lithium disilicate glass ceramic.

  12. Stochastic Computer Simulation of Cermet Coatings Formation

    OpenAIRE

    Solonenko, Oleg P.; Jordan, Vladimir I.; Blednov, Vitaly A.

    2015-01-01

    An approach to the modeling of the process of the formation of thermal coatings lamellar structure, including plasma coatings, at the spraying of cermet powders is proposed. The approach based on the theoretical fundamentals developed which could be used for rapid and sufficiently accurate prediction of thickness and diameter of cermet splats as well as temperature at interface “flattening quasi-liquid cermet particle-substrate” depending on the key physical parameters (KPPs): temperature, ve...

  13. Tunneling magnetoresistance in granular cermet films with particle size distribution

    International Nuclear Information System (INIS)

    Vovk, A.Ya.; Golub, V.O.; Malkinski, L.; Kravets, A.F.; Pogorily, A.M.; Shypil', O.V.

    2004-01-01

    The correlation between tunneling magnetoresistance (TMR) and field sensitivity (dMR/dH) for granular films (Co 50 Fe 50 ) x -(Al 2 O 3 ) 1-x was studied. The position of TMR maximum is shifted towards the lower x in the higher applied magnetic fields. Such a behavior was observed for metal granular nanocomposites but is first reported for granular cermets. However the highest dMR/dH was found for the compositions just below the percolation threshold

  14. Effects of Laser Power Level on Microstructural Properties and Phase Composition of Laser-Clad Fluorapatite/Zirconia Composite Coatings on Ti6Al4V Substrates

    Directory of Open Access Journals (Sweden)

    Chi-Sheng Chien

    2016-05-01

    Full Text Available Hydroxyapatite (HA is one of the most commonly used materials for the coating of bioceramic titanium (Ti alloys. However, HA has poor mechanical properties and a low bonding strength. Accordingly, the present study replaces HA with a composite coating material consisting of fluorapatite (FA and 20 wt % yttria (3 mol % stabilized zirconia (ZrO2, 3Y-TZP. The FA/ZrO2 coatings are deposited on Ti6Al4V substrates using a Nd:YAG laser cladding system with laser powers and travel speeds of 400 W/200 mm/min, 800 W/400 mm/min, and 1200 W/600 mm/min, respectively. The experimental results show that a significant inter-diffusion of the alloying elements occurs between the coating layer (CL and the transition layer (TL. Consequently, a strong metallurgical bond is formed between them. During the cladding process, the ZrO2 is completely decomposed, while the FA is partially decomposed. As a result, the CLs of all the specimens consist mainly of FA, Ca4(PO42O (TTCP, CaF2, CaZrO3, CaTiO3 and monoclinic phase ZrO2 (m-ZrO2, together with a small amount of θ-Al2O3. As the laser power is increased, CaO, CaCO3 and trace amounts of tetragonal phase ZrO2 (t-ZrO2 also appear. As the laser power increases from 400 to 800 W, the CL hardness also increases as a result of microstructural refinement and densification. However, at the highest laser power of 1200 W, the CL hardness reduces significantly due to the formation of large amounts of relatively soft CaO and CaCO3 phase.

  15. Effects of Laser Power Level on Microstructural Properties and Phase Composition of Laser-Clad Fluorapatite/Zirconia Composite Coatings on Ti6Al4V Substrates.

    Science.gov (United States)

    Chien, Chi-Sheng; Liu, Cheng-Wei; Kuo, Tsung-Yuan

    2016-05-17

    Hydroxyapatite (HA) is one of the most commonly used materials for the coating of bioceramic titanium (Ti) alloys. However, HA has poor mechanical properties and a low bonding strength. Accordingly, the present study replaces HA with a composite coating material consisting of fluorapatite (FA) and 20 wt % yttria (3 mol %) stabilized zirconia (ZrO₂, 3Y-TZP). The FA/ZrO₂ coatings are deposited on Ti6Al4V substrates using a Nd:YAG laser cladding system with laser powers and travel speeds of 400 W/200 mm/min, 800 W/400 mm/min, and 1200 W/600 mm/min, respectively. The experimental results show that a significant inter-diffusion of the alloying elements occurs between the coating layer (CL) and the transition layer (TL). Consequently, a strong metallurgical bond is formed between them. During the cladding process, the ZrO₂ is completely decomposed, while the FA is partially decomposed. As a result, the CLs of all the specimens consist mainly of FA, Ca₄(PO₄)₂O (TTCP), CaF₂, CaZrO₃, CaTiO₃ and monoclinic phase ZrO₂ (m-ZrO₂), together with a small amount of θ-Al₂O₃. As the laser power is increased, CaO, CaCO₃ and trace amounts of tetragonal phase ZrO₂ (t-ZrO₂) also appear. As the laser power increases from 400 to 800 W, the CL hardness also increases as a result of microstructural refinement and densification. However, at the highest laser power of 1200 W, the CL hardness reduces significantly due to the formation of large amounts of relatively soft CaO and CaCO₃ phase.

  16. Effects of Laser Power Level on Microstructural Properties and Phase Composition of Laser-Clad Fluorapatite/Zirconia Composite Coatings on Ti6Al4V Substrates

    Science.gov (United States)

    Chien, Chi-Sheng; Liu, Cheng-Wei; Kuo, Tsung-Yuan

    2016-01-01

    Hydroxyapatite (HA) is one of the most commonly used materials for the coating of bioceramic titanium (Ti) alloys. However, HA has poor mechanical properties and a low bonding strength. Accordingly, the present study replaces HA with a composite coating material consisting of fluorapatite (FA) and 20 wt % yttria (3 mol %) stabilized zirconia (ZrO2, 3Y-TZP). The FA/ZrO2 coatings are deposited on Ti6Al4V substrates using a Nd:YAG laser cladding system with laser powers and travel speeds of 400 W/200 mm/min, 800 W/400 mm/min, and 1200 W/600 mm/min, respectively. The experimental results show that a significant inter-diffusion of the alloying elements occurs between the coating layer (CL) and the transition layer (TL). Consequently, a strong metallurgical bond is formed between them. During the cladding process, the ZrO2 is completely decomposed, while the FA is partially decomposed. As a result, the CLs of all the specimens consist mainly of FA, Ca4(PO4)2O (TTCP), CaF2, CaZrO3, CaTiO3 and monoclinic phase ZrO2 (m-ZrO2), together with a small amount of θ-Al2O3. As the laser power is increased, CaO, CaCO3 and trace amounts of tetragonal phase ZrO2 (t-ZrO2) also appear. As the laser power increases from 400 to 800 W, the CL hardness also increases as a result of microstructural refinement and densification. However, at the highest laser power of 1200 W, the CL hardness reduces significantly due to the formation of large amounts of relatively soft CaO and CaCO3 phase. PMID:28773503

  17. Current Progress in Solution Precursor Plasma Spraying of Cermets: A Review

    Directory of Open Access Journals (Sweden)

    Romnick Unabia

    2018-06-01

    Full Text Available Ceramic and metal composites, known also as cermets, may considerably improve many material properties with regards to that of initial components. Hence, cermets are frequently applied in many technological fields. Among many processes which can be employed for cermet manufacturing, thermal spraying is one of the most frequently used. Conventional plasma spraying of powders is a popular and cost-effective manufacturing process. One of its most recent innovations, called solution precursor plasma spraying (SPPS, is an emerging coating deposition method which uses homogeneously mixed solution precursors as a feedstock. The technique enables a single-step deposition avoiding the powder preparation procedures. The nanostructured coatings developed by SPPS increasingly find a place in the field of surface engineering. The present review shows the recent progress in the fabrication of cermets using SPPS. The influence of starting solution precursors, such as their chemistry, concentration, and solvents used, to the micro-structural characteristics of cermet coatings is discussed. The effect of the operational plasma spray process parameters such as solution injection mode to the deposition process and coatings’ microstructure is also presented. Moreover, the advantages of the SPPS process and its drawbacks compared to the conventional powder plasma spraying process are discussed. Finally, some applications of SPPS cermet coatings are presented to understand the potential of the process.

  18. COMPORTAMENTO A CORROSIONE E TRIBOCORROSIONE DI RIVESTIMENTI CERMET E CERMET/ SUPERLATTICE

    OpenAIRE

    Monticelli, C.; Zucchi, F.

    2009-01-01

    È stato studiato il comportamento a corrosione e tribocorrosione di riporti cermet e cermet/superlattice,applicati su campioni di acciaio. I riporti cermet consistono in riporti termici HVOF a spessore,di tipo WC-12Co o Cr3C2-37WC-18Me. I doppi riporti cermet/superlattice sono ottenuti sovrapponendoai depositi cermet citati un superlattice a base di nitruri, in cui si alternano strati di CrN e di NbN. Unasoluzione al 3.5 % di NaCl costituisce l’ambiente aggressivo. Le condizioni di tribocorro...

  19. Influence of artificial aging on the shear bond strength of zirconia-composite interfaces after pretreatment with new 10-MDP adhesive systems

    Directory of Open Access Journals (Sweden)

    p.c pott

    2016-03-01

    Full Text Available Introduction: This in-vitro study investigates the bond strength of different zirconia composites  with three different modern adhesive systems after artificial aging using thermocycling and water storage. Methods: A total of 90 specimens of zirconia (InCoris, Sirona, Germany, Bernsheim were ground using a 165 µm grit rotating diamond disc. Thirty specimens were additionally treated with either Futurabond U “FBU” (VOCO GmbH, or Futurabond M+ “FBM” (VOCO GmbH or Futurabond M+ in combination with the DCA activator “FBMD” (VOCO GmbH. One of the three different types of composites – BifixSE “BS”, BifixQM “BQ” or GrandioSO “G” (VOCO GmbH – was bonded to the ten specimens of each group. All of the specimens underwent artificial aging using thermocycling between 5°C and 55°C for 5000 cycles followed by water storage for 100 days. Shear bond strength (SBS was determined in a universal testing machine. The type of failure was evaluated using fluorescence microscopy. The data were compared to existing data without artificial aging. Statistical analysis was performed with ANOVA and the Tukey test. Results: FBM and FBMD had higher SBS than FBU in combination with all tested composites, except BifixSE. In nearly all groups, artificial aging had no effect, with the exception of the combination of FBMD with BifixSE, in which there was a significant decrease in SBS after the aging process (p

  20. Synthesis and ceramic processing of alumina and zirconia based composites infiltrated with glass phase for dental applications

    International Nuclear Information System (INIS)

    Duarte, Daniel Gomes

    2009-01-01

    The interest for the use of ceramic materials for dental applications started due to the good aesthetic appearance promoted by the similarity to natural teeth. However, the fragility of traditional ceramics was a limitation for their use in stress conditions. The development of alumina and zirconia based materials, that associate aesthetic results, biocompatibility and good mechanical behaviour, makes possible the employment of ceramics for fabrication of dental restorations. The incorporation of vitreous phase in these ceramics is an alternative to minimize the ceramic retraction and to improve the adhesion to resin-based cements, necessary for the union of ceramic frameworks to the remaining dental structure. In the dentistry field, alumina and zirconia ceramic infiltrated with glassy phase are represented commercially by the In-Ceram systems. Considering that the improvement of powder's synthesis routes and of techniques of ceramic processing contributes for good performance of these materials, the goal of the present work is the study of processing conditions of alumina and/or 3 mol% yttria-stabilized zirconia ceramics infiltrated with aluminum borosilicate lanthanum glass. The powders, synthesized by hydroxide coprecipitation route, were pressed by uniaxial compaction and pre-sintered at temperature range between 950 and 1650 degree C in order to obtain porous ceramics bodies. Vitreous phase incorporation was performed by impregnation of aluminum borosilicate lanthanum powder, also prepared in this work, followed by heat treatment between 1200 and 1400 degree C .Ceramic powders were characterized by thermogravimetry, X-ray diffraction, scanning and transmission electron microscopy, gaseous adsorption (BET) and laser diffraction. Sinterability of alumina and /or stabilized zirconia green pellets was evaluated by dilatometry. Pre-sintered ceramics were characterized by apparent density measurements (Archimedes method), X-ray diffraction and scanning electron

  1. Thermal properties and thermal shock resistance of liquid phase sintered ZrC-Mo cermets

    International Nuclear Information System (INIS)

    Landwehr, Sean E.; Hilmas, Gregory E.; Fahrenholtz, William G.; Talmy, Inna G.; Wang Hsin

    2009-01-01

    The linear thermal expansion coefficient (CTE), heat capacity, and thermal conductivity, were investigated as a function of temperature for hot pressed ZrC and liquid phase sintered ZrC-Mo cermets. The ZrC and the ZrC-Mo cermets had the same CTE at 50 deg. C (∼5.1-5.5 ppm deg. C -1 ), but the CTE of ZrC increased to ∼12.2 ppm deg. C -1 at 1000 deg. C compared to ∼7.2-8.5 ppm deg. C -1 for the ZrC-Mo cermets. Heat capacity was calculated using a rule of mixtures and previously reported thermodynamic data. Thermal diffusivity was measured with a laser flash method and was, in turn, used to calculate thermal conductivity. Thermal conductivity increased linearly with increasing temperature for all compositions and was affected by solid solution formation and carbon deficiency of the carbide phases. Hot pressed ZrC had the highest thermal conductivity (∼30-37 W m -1 K -1 ). The nominally 20 and 30 vol% Mo compositions of the ZrC-Mo cermets had a lower thermal conductivity, but the thermal conductivity generally increased with increasing Mo content. Water quench thermal shock testing showed that ZrC-30 vol% Mo had a critical temperature difference of 350 deg. C, which was ∼120 deg. C higher than ZrC. This increase was due to the increased toughness of the cermet compared to ZrC.

  2. Cermet materials, self-cleaning cermet filters, apparatus and systems employing same

    Science.gov (United States)

    Kong, Peter C.

    2005-07-19

    A self-cleaning porous cermet material, filter and system utilizing the same may be used in filtering particulate and gaseous pollutants from internal combustion engines having intermetallic and ceramic phases. The porous cermet filter may be made from a transition metal aluminide phase and an alumina phase. Filler materials may be added to increase the porosity or tailor the catalytic properties of the cermet material. Additionally, the cermet material may be reinforced with fibers or screens. The porous filter may also be electrically conductive so that a current may be passed therethrough to heat the filter during use. Further, a heating element may be incorporated into the porous cermet filter during manufacture. This heating element can be coated with a ceramic material to electrically insulate the heating element. An external heating element may also be provided to heat the cermet filter during use.

  3. Study of microstructure and mechanical properties of ceramics composites alumina-zirconia reinforced with yttria for inert coating of metal matrices used in the petroleum industry; Estudo de microestrutura e propriedades mecanicas de compositos ceramicos alumina-zirconia reforcado com itria para revestimento inerte de matrizes metalicas usadas na industria petrolifera

    Energy Technology Data Exchange (ETDEWEB)

    Pontual, J.O.; Silva, N.D.G.; Ferreira, R.A.S.; Yadava, Y.P., E-mail: juliaopontual@hotmail.com, E-mail: yadava@ufpe.br [Universidade Federal de Pernambuco (UFPE), Recife, PE (Brazil). Departamento de Engenharia Mecanica

    2014-07-01

    The storage and transportation of crude oil is complicated due to the hostile environment provided by this. Under these conditions, it is imperative to search for alternative solutions, using an inert coating to protect from corrosion caused by crude oil. In this work, alumina-zirconia ceramic composites with 5-20%w zirconia and 1 - 2%w yttria were produced through thermomechanical process. The structural and microstructural characterization of the sintered material was carried out by X-ray diffraction and scanning electron microscopy. Mechanical properties were analyzed by Vickers hardness tests. Currently, the pads are submerged in crude oil and after 30-60 days will be removed and sent for stability test.(author)

  4. STABILISED ZIRCONIA

    Directory of Open Access Journals (Sweden)

    LUZ STELLA ARIAS-MAYA

    2014-01-01

    Full Text Available La densificación y la contracción de cerámicos u otros materiales en polvo pueden ser predichos de una manera sencilla usando la curva maestra de sinterizado. En este trabajo se han obtenido los datos de densificación requeridos para construir la curva maestra de sinterizado de zirconia en polvo estabilizada con 3-mol% itria. Se sinterizaron muestras compactadas en frío, así como películas gruesas hechas del mismo polvo y aplicadas a un sustrato rígido. Las pruebas de sinterizado libre y con restricción fueron realizadas aplicando tres velocidades de calentamiento, incluyendo o no una etapa isotérmica a la máxima temperatura de ~1450 °C. La contracción de las muestras se midió durante la densificación usando un dilatómetro de varilla de presión. También se usó un horno convencional, aplicando la misma curva de calentamiento para comparar resultados. El análisis microestructural fue logrado mediante microscopía de barrido electrónico, microscopía de barrido electrónico ambiental y microscopía óptica. Se obtuvo una concordancia aceptable entre muestras similares sinterizadas en el dilatómetro y en el horno convencional, indicando que los datos del dilatómetro pueden ser usados para ambos ambientes. Las muestras que se sinterizaron sin restricción alcanzaron menores densidades que las películas, probablemente debido a que sus densidades iniciales eran menores. Para las muestras libres de restricción, se obtuvo una curva maestra de sinterizado con una energía de activación de 550 kJ mol-1. Para las películas sinterizadas con restricción, algunos problemas asociados con el sustrato y con las incertidumbres de las mediciones impidieron la caracterización de la película, es decir, la obtención de una curva maestra de sinterizado con un solo valor de energía de activación.

  5. Cermet coatings for magnetic fusion reactors

    International Nuclear Information System (INIS)

    Smith, M.F.; Whitley, J.B.; McDonald, J.M.

    1984-01-01

    Cermet coatings consisting of SiC particles in an aluminum matrix were produced by a low pressure chamber plasma spray process. Properties of these coatings are being investigated to evaluate their suitability for use in the next generation of magnetic confinement fusion reactors. Although this preliminary study has focused primarily upon SiC-Al cermets, the deposition process can be adapted to other ceramic-metal combinations. Potential applications for cermet coatings in magnetic fusion devices are presented along with experimental results from thermal tests of candidate coatings. (Auth.)

  6. Cermets for high level waste containment

    International Nuclear Information System (INIS)

    Aaron, W.S.; Quinby, T.C.; Kobisk, E.H.

    1978-01-01

    Cermet materials are currently under investigation as an alternate for the primary containment of high level wastes. The cermet in this study is an iron--nickel base metal matrix containing uniformly dispersed, micron-size fission product oxides, aluminosilicates, and titanates. Cermets possess high thermal conductivity, and typical waste loading of 70 wt % with volume reduction factors of 2 to 200 and low processing volatility losses have been realized. Preliminary leach studies indicate a leach resistance comparable to other candidate waste forms; however, more quantitative data are required. Actual waste studies have begun on NFS Acid Thorex, SRP dried sludge and fresh, unneutralized SRP process wastes

  7. Cermet fuel behaviour and properties in ADS reactors

    International Nuclear Information System (INIS)

    Haas, D.; Fernandez, A.; Staicu, D.; Somers, J.; Maschek, W.; Chen, X.

    2007-01-01

    ).Irradiation programmes are in the final stage of preparation (and will start in 2007) to determine the in-reactor performance of the material. CERMET fuel pins are incorporated in two experiments: - Two pins will be loaded in the PHENIX reactor in Marcoule, within the FUTURIX FTA experiment [2]. These fuels have been fabricated at ITU in 2005-2006, according to the reference fabrication process in the Minor Actinide Laboratory, namely the infiltration of minor actinide solution in solid particles. These fuels have been fully characterised in terms of pellet structure, thermal properties, re-sintering behaviour, etc. The aim of the experiment is the investigation of the fuel behaviour under high fast neutron flux condition, and its comparison with other fuel types (CERCER, nitride and metallic).The completion of the irradiation is foreseen in 2009. - Two further CERMET fuel pins will be irradiated in the HFR reactor in Petten: the HELIOS experiment [3]. There the aim is the study of the gas (including Helium, produced by Am 2 41 transmutation chain) production and release, in comparison with Am targets supported in a pure zirconia matrix. The post-irradiation examinations to be performed after 10 irradiation cycles will be concluded in 2009. Safety studies for optimised EFIT core designs, developed within the AFTRA domain were performed. The safety coefficients and indicators were determined for each core, and various transients were investigated. For the new low power cores of EFIT with a power class of ∼ 400 MWth and a fuel power density of ∼ 250 MW/m 3 it can be demonstrated that the CERMET cores behave favourably and the design limits of the fuels are not violated [4]. Results indicate that the T 9 1 cladding used as clad more severely restricts possible design options. This report will present the status of the neutronic and safety studies for the EFIT core, the CERMET thermal properties determination results, as well as the final results of the fabrication, characterisation and

  8. Comparison of Ti(C,N)-based cermets processed by hot-pressing sintering and conventional pressureless sintering

    International Nuclear Information System (INIS)

    Xu, Qingzhong; Ai, Xing; Zhao, Jun; Qin, Weizhen; Wang, Yintao; Gong, Feng

    2015-01-01

    Highlights: • The HP sintered Ti(C,N)-based cermets exhibit high hardness with fine grain size. • The PLS sintered cermets possess high mechanical properties with low porosity. • The applied pressure can rearrange particles and contribute to grain refinement. • The heating rate can greatly affect the solid and liquid phase sintering of cermets. - Abstract: A suitable sintering method is important to obtain the Ti(C,N)-based cermets with superior properties. In this paper, Ti(C,N)-based cermets were fabricated by hot-pressing sintering (HP) and conventional pressureless sintering (PLS) technology, respectively, to investigate the influence of different sintering methods on the microstructure and mechanical properties of cermets materials. The microstructure, fracture morphology, indention cracks and phase composition were observed and detected using scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The transverse rupture strength (TRS), Vickers hardness (HV) and fracture toughness (K IC ) were also measured. The results reveal that all of the Ti(C,N)-based cermets exhibit core–rim microstructures with black cores, white cores and grey rims embedded into metal binder phases. The grain size of the samples fabricated by HP is much finer and the structure is more compact than those fabricated by PLS, while there exist pores in the HP sintered samples. The sintering process has no influence on the phase composition of cermets, but affects the phase content and crystallinity. The samples fabricated by PLS present higher transverse rupture strength, fracture toughness and density than samples fabricated by HP. However, the HP sintered samples possess a higher hardness

  9. Microstructural stability of spark-plasma-sintered Wf/W composite with zirconia interface coating under high-heat-flux hydrogen beam irradiation

    Directory of Open Access Journals (Sweden)

    M. Avello de Lama

    2017-12-01

    In this paper, the durability and chemical stability of Wf/W composite specimens under cyclic heat-flux loads up to 20 MW/m² (surface temperature: 1260 °C was investigated using hydrogen neutral beam. The bulk material was fabricated by means of spark-plasma-sintering (SPS method using fine tungsten powder and a stack of tungsten wire meshes as reinforcement where the surface of the wire was coated with zirconia thin film to produce an engineered interface. The impact of plasma beam irradiation on microstructure was examined for two kinds of specimens produced at different sintering temperatures, 1400 °C and 1700 °C. Results of microscopic (SEM and chemical (EDX analysis are presented comparing the microstructure and element distribution maps obtained before and after heat flux loading. Effects of different sintering temperatures on damage behaviour are discussed. The present composite materials are shown to be applicable as plasma-facing material for high-heat-flux components.

  10. Liquid phase sintered superconducting cermet

    International Nuclear Information System (INIS)

    Ray, S.P.

    1990-01-01

    This patent describes a method of making a superconducting cermet having superconducting properties with improved bulk density, low porosity and in situ stabilization. It comprises: forming a structure of a superconducting ceramic material having the formula RM 2 Cu 3 O (6.5 + x) wherein R is one or more rare earth elements capable of reacting to form a superconducting ceramic, M is one or more alkaline earth metal elements selected from barium and strontium capable of reacting to form a superconducting ceramic, x is greater than 0 and less than 0.5; and a precious metal compound in solid form selected from the class consisting of oxides, sulfides and halides of silver; and liquid phase sintering the mixture at a temperature wherein the precious metal of the precious metal compound is molten and below the melting point of the ceramic material. The liquid phase sintering is carried out for a time less than 36 hours but sufficient to improve the bulk density of the cermet

  11. New cermet coatings for mid-temperature applications for solar concentrated combine heat and power system

    OpenAIRE

    Wäckelgård, Ewa; Bartali, Ruben; Gerosa, Riccardo; Laidani, Nadhira; Mattsson, Andreas; Micheli, Victor; Rivolta, Barbara

    2014-01-01

    New cermet (ceramic-metal) composite coatings have been developed for solar absorbers in a solar concentrating system for combined heat and power operating in a mid-temperature range between 250 to 350 degrees C. The coatings were applied on stainless steel substrates. Two types of cermet with expected good duration properties were chosen: Nb-TiO2 and W-SiO2. The basic layer-structure concept consisted of four sub-layers, counted from the substrate: molybdenum infrared reflector, high metal c...

  12. Fabrication of cermet bearings for the control system of a high temperature lithium cooled nuclear reactor

    Science.gov (United States)

    Yacobucci, H. G.; Heestand, R. L.; Kizer, D. E.

    1973-01-01

    The techniques used to fabricate cermet bearings for the fueled control drums of a liquid metal cooled reference-design reactor concept are presented. The bearings were designed for operation in lithium for as long as 5 years at temperatures to 1205 C. Two sets of bearings were fabricated from a hafnium carbide - 8-wt. % molybdenum - 2-wt. % niobium carbide cermet, and two sets were fabricated from a hafnium nitride - 10-wt. % tungsten cermet. Procedures were developed for synthesizing the material in high purity inert-atmosphere glove boxes to minimize oxygen content in order to enhance corrosion resistance. Techniques were developed for pressing cylindrical billets to conserve materials and to reduce machining requirements. Finishing was accomplished by a combination of diamond grinding, electrodischarge machining, and diamond lapping. Samples were characterized in respect to composition, impurity level, lattice parameter, microstructure and density.

  13. Occlusal glass ionomer cermet, resin sandwich and amalgam restorations: a 2-year clinical study.

    Science.gov (United States)

    Lidums, A; Wilkie, R; Smales, R

    1993-08-01

    This study compared the clinical behavior of a glass ionomer silver cermet (Ketac-Silver), a posterior resin composite (Visio-Molar) used with the "sandwich" technique, and a high-copper amalgam (Dispersalloy) for restoring conventional Class I occlusal cavity preparations. Two dentists placed 116 restorations in the posterior permanent teeth of 35 adults treated at a dental hospital. Restorations were assessed at 6-month intervals over 2 years for bulk loss of material and occlusal wear, surface voids, roughness and cracking, surface and marginal staining, and marginal fracture. Losses of material and surface voids were obvious with the cermet material, with surface crazing or cracking being present in 33% of the restorations. The cermet cannot be recommended as a long-term permanent restorative material if the restorations are likely to be subjected to heavy occlusal stresses and abrasive wear.

  14. For cermet inert anode containing oxide and metal phases useful for the electrolytic production of metals

    Science.gov (United States)

    Ray, Siba P.; Liu, Xinghua; Weirauch, Douglas A.

    2002-01-01

    A cermet inert anode for the electrolytic production of metals such as aluminum is disclosed. The inert anode comprises a ceramic phase including an oxide of Ni, Fe and M, where M is at least one metal selected from Zn, Co, Al, Li, Cu, Ti, V, Cr, Zr, Nb, Ta, W, Mo, Hf and rare earths, preferably Zn and/or Co. Preferred ceramic compositions comprise Fe.sub.2 O.sub.3, NiO and ZnO or CoO. The cermet inert anode also comprises a metal phase such as Cu, Ag, Pd, Pt, Au, Rh, Ru, Ir and/or Os. A preferred metal phase comprises Cu and Ag. The cermet inert anodes may be used in electrolytic reduction cells for the production of commercial purity aluminum as well as other metals.

  15. Structure and strength of carbide-steel cermet and their changes during heat treatment

    International Nuclear Information System (INIS)

    Dariel, M.P.; Frage, N.R.; Kaputkina, L.M.; Kaputkin, D.M.; Sverdlova, N.R.

    2004-01-01

    Both homogeneous and 'graded' materials were produced by pressing and sintering of titanium carbide TiC x (0.7 x takes place during the joining. If the titanium carbide is carbon deficient that the carbon goes from the steel binder to TiC x , and this redistribution intensity with the x decreases. So-named graded cermets were produced on controlled distribution of TiC x with different x. An additional flow of carbon from C-rich to C-poor TiC x layers was obtained in these cermets. These changes both in the steel and TiC x compositions result in changes in such processes as austenitization, carbide dissolution and precipitation, and martensitic transformation. Both general strength of the material and the gradient of properties in graded cermets can be increased using kinetic factors of element redistribution and structure changes resulted from the heat treatment. (author)

  16. Working of Mo-TiC cermets for 'future nuclear systems'

    International Nuclear Information System (INIS)

    Allemand, Alexandre; Le Flem, Marion; Rousselet, Jerome

    2006-01-01

    The nuclear reactor cores (generation IV) will form an extremely severe environment (high temperature, severe and long irradiation...). These drastic criteria and the preoccupation to ensure a higher and higher safety level lead, beyond the preoccupations due to the feasibility of such reactors, to harsh choices in materials able to be used. Innovating materials such as Mo-TiC cermet are the subject of intense researches in the CEA. This study presents and compares two modes of Mo-TiC cermet working: the hot isostatic compression and the extrusion. Different compositions of Mo-TiC cermets are prepared by hot isostatic compression and extrusion, and then characterized in term of microstructural properties. At last, this study concludes to a very satisfying working by hot isostatic compression, nevertheless the extrusion has still to be improved. (O.M.)

  17. Surface properties of copper based cermet materials

    International Nuclear Information System (INIS)

    Voinea, M.; Vladuta, C.; Bogatu, C.; Duta, A.

    2008-01-01

    The paper presents the characterization of the surface properties of copper based cermets obtained by two different techniques: spray pyrolysis deposition (SPD) and electrodeposition. Copper acetate was used as precursor of Cu/CuO x cermet. The surface morphology was tailored by adding copolymers of maleic anhydride with controlled hydrophobia. The films morphology of Cu/CuO x was assessed using contact angle measurements and AFM analysis. The porous structures obtained via SPD lead to higher liquid adsorption rate than the electrodeposited films. A highly polar liquid - water is recommended as testing liquid in contact angle measurements, for estimating the porosity of copper based cermets, while glycerol can be used to distinguish among ionic and metal predominant structures. Thus, contact angle measurements can be used for a primary evaluation of the films morphology and, on the other hand, of the ratio between the cermet components

  18. Cermet Coatings for Solar Stirling Space Power

    Science.gov (United States)

    Jaworske, Donald A.; Raack, Taylor

    2004-01-01

    Cermet coatings, molecular mixtures of metal and ceramic are being considered for the heat inlet surface of a solar Stirling space power converter. This paper will discuss the solar absorption characteristics of as-deposited cermet coatings as well as the solar absorption characteristics of the coatings after heating. The role of diffusion and island formation, during the deposition process and during heating will also be discussed.

  19. Cermet fuels for space power systems

    International Nuclear Information System (INIS)

    Barner, J.O.; Coomes, E.P.; Williford, R.E.; Neimark, L.A.

    1986-01-01

    A refractory-metal matrix, UN-fueled cermet is a very promising fuel candidate for a wide range of multi-megawatt space reactor systems, e.g., steady-state, flexible duty-cycle, or bimodal, single- or two-phase liquid-metal cooled reactors, or thermionic reactors. Cermet fuel is especially promising for reactor designs that require operational strategies which incorporate rapid power changes because of its anticipated capability to withstand thermal shock

  20. Damage Maps of Veneered Zirconia under Simulated Mastication

    Science.gov (United States)

    Kim, Jae-Won; Kim, Joo-Hyung; Janal, Malvin N.; Zhang, Yu

    2016-01-01

    Zirconia based restorations often fracture from chipping and/or delamination of the porcelain veneers. We hypothesize that veneer chipping/delamination is a result of the propagation of near-contact induced partial cone cracks on the occlusal surface under mastication. Masticatory loading involves the opposing tooth sliding along the cuspal inner incline surface with an applied biting force. To test this hypothesis, flat porcelain veneered zirconia plates were cemented to dental composites and cyclically loaded (contact–slide–liftoff) at an inclination angle as a simplified model of zirconia based restorations under occlusion. In the light of in-situ observation of damage evolution in a transparent glass/zirconia/polycarbonate trilayer, postmortem damage evaluation of porcelain/zirconia/composite trilayers using a sectioning technique revealed that deep penetrating occlusal surface partial cone fracture is the predominant fracture mode of porcelain veneers. Clinical relevance is discussed. PMID:19029080

  1. Inverted amorphous silicon solar cell utilizing cermet layers

    Science.gov (United States)

    Hanak, Joseph J.

    1979-01-01

    An amorphous silicon solar cell incorporating a transparent high work function metal cermet incident to solar radiation and a thick film cermet contacting the amorphous silicon opposite to said incident surface.

  2. Deposition and characterization of plasma sprayed Ni-5A1/ magnesia stabilized zirconia based functionally graded thermal barrier coating

    International Nuclear Information System (INIS)

    Baig, M N; Khalid, F A

    2014-01-01

    Thermal barrier coatings (TBCs) are employed to protect hot section components in industrial and aerospace gas turbine engines. Conventional TBCs frequently fail due to high residual stresses and difference between coefficient of thermal expansion (CTE) of the substrate and coatings. Functionally graded thermal barrier coatings (FG-TBCs) with gradual variation in composition have been proposed to minimize the problem. In this work, a five layered functionally graded thermal barrier coating system was deposited by atmospheric plasma spray (APS) technique on Nimonic 90 substrates using Ni-5Al as bond coat (BC) and magnesia stabilized zirconia as top coat (TC). The coatings were characterized by SEM, EDS, XRD and optical profilometer. Microhardness and coefficient of thermal expansion of the five layers deposited as individual coatings were also measured. The deposited coating system was oxidized at 800°C. SEM analysis showed that five layers were successfully deposited by APS to produce a FG-TBC. The results also showed that roughness (Ra) of the individual layers decreased with an increase in TC content in the coatings. It was found that microhardness and CTE values gradually changed from bond coat to cermet layers to top coat. The oxidized coated sample revealed parabolic behavior and changes in the surface morphology and composition of coating

  3. Zirconia in biomedical applications.

    Science.gov (United States)

    Chen, Yen-Wei; Moussi, Joelle; Drury, Jeanie L; Wataha, John C

    2016-10-01

    The use of zirconia in medicine and dentistry has rapidly expanded over the past decade, driven by its advantageous physical, biological, esthetic, and corrosion properties. Zirconia orthopedic hip replacements have shown superior wear-resistance over other systems; however, risk of catastrophic fracture remains a concern. In dentistry, zirconia has been widely adopted for endosseous implants, implant abutments, and all-ceramic crowns. Because of an increasing demand for esthetically pleasing dental restorations, zirconia-based ceramic restorations have become one of the dominant restorative choices. Areas covered: This review provides an updated overview of the applications of zirconia in medicine and dentistry with a focus on dental applications. The MEDLINE electronic database (via PubMed) was searched, and relevant original and review articles from 2010 to 2016 were included. Expert commentary: Recent data suggest that zirconia performs favorably in both orthopedic and dental applications, but quality long-term clinical data remain scarce. Concerns about the effects of wear, crystalline degradation, crack propagation, and catastrophic fracture are still debated. The future of zirconia in biomedical applications will depend on the generation of these data to resolve concerns.

  4. High level waste fixation in cermet form

    International Nuclear Information System (INIS)

    Kobisk, E.H.; Aaron, W.S.; Quinby, T.C.; Ramey, D.W.

    1981-01-01

    Commercial and defense high level waste fixation in cermet form is being studied by personnel of the Isotopes Research Materials Laboratory, Solid State Division (ORNL). As a corollary to earlier research and development in forming high density ceramic and cermet rods, disks, and other shapes using separated isotopes, similar chemical and physical processing methods have been applied to synthetic and real waste fixation. Generally, experimental products resulting from this approach have shown physical and chemical characteristics which are deemed suitable for long-term storage, shipping, corrosive environments, high temperature environments, high waste loading, decay heat dissipation, and radiation damage. Although leach tests are not conclusive, what little comparative data are available show cermet to withstand hydrothermal conditions in water and brine solutions. The Soxhlet leach test, using radioactive cesium as a tracer, showed that leaching of cermet was about X100 less than that of 78 to 68 glass. Using essentially uncooled, untreated waste, cermet fixation was found to accommodate up to 75% waste loading and yet, because of its high thermal conductivity, a monolith of 0.6 m diameter and 3.3 m-length would have only a maximum centerline temperature of 29 K above the ambient value

  5. Fabrication and characterization of Cu/YSZ cermet high temperature electrolysis cathode material prepared by high-energy ball-milling method

    International Nuclear Information System (INIS)

    Lee, Sungkyu; Kim, Jong-Min; Hong, Hyun Seon; Woo, Sang-Kook

    2009-01-01

    Cu/YSZ cermet (40 and 60 vol.% Cu powder with balance YSZ) is a more economical cathode material than the conventional Ni/YSZ cermet for high temperature electrolysis (HTE) of water vapor and it was successfully fabricated by high-energy ball-milling of Cu and YSZ powders, pressing into pellets (o 13 mm x 2 mm) and subsequent sintering process at 700 deg. C under flowing 5%-H 2 /Ar gas. The Cu/YSZ composite material thus fabricated was characterized using various analytical tools such as XRD, SEM, and laser diffraction and scattering method. Electrical conductivity of sintered Cu/YSZ cermet pellets thus fabricated was measured by using 4-probe technique for comparison with that of conventional Ni/YSZ cermets. The effect of composite composition on the electrical conductivity was investigated and a marked increase in electrical conductivity for copper contents greater than 40 vol.% in the composite was explained by percolation threshold. Also, Cu/YSZ cermet was selected as a candidate for HTE cathode of self-supporting planar unit cell and its electrochemical performance was investigated, paving the way for preliminary correlation of high-energy ball-milling parameters with observed physical and electrochemical performance of Cu/YSZ cermets

  6. Densification of zirconia-hematite nanopowders

    NARCIS (Netherlands)

    Raming, T.P.; Winnubst, Aloysius J.A.; van Zyl, W.E.; Verweij, H.

    2003-01-01

    The densification of dual-phase yttria-doped tetragonal zirconia polycrystals (Y-TZP) and -Fe2O3 (hematite) composite powders is described. Different powder synthesis methods, different forms of dry compaction processes, and two sinter methods (pressureless sintering and sinterforging) were

  7. Thermionic emission of cermets made of refractory carbides

    International Nuclear Information System (INIS)

    Samsonow, G.W.; Bogomol, I.W.; Ochremtschuk, L.N.; Podtschernjajewa, I.A.; Fomenko, W.S.

    1975-01-01

    In order to improve the resistance to thermal variations of refractory carbides having good behavior for thermionic emission, they have been combined with transition metals d. Thermionic emission was studied with cermets in compact samples. Following systems were examined: TiC-Nb, TiC-Mo, TiC-W, ZrC-Nb, ZrC-Mo, ZrC-W, WC-Mo with compositions of: 75% M 1 C-25% M 2 , 50%M 1 C-50%M 2 , 25%M 1 C-75%M 2 . When following the variation of electron emission energy phi versus the composition, it appears that in the range of mixed crystals (M 1 M 2 )C, phi decreases and the resistance to thermal variations of these phases is higher than that of individual carbides. The study of obtained cermets shows that their resistance to thermal variations is largely superior to the one of starting carbides; TiC and ZrC carbides, combined with molybdenum and tungsten support the highest number of thermic cycles

  8. Cermets based on rhenium and rare earth element oxides

    International Nuclear Information System (INIS)

    Varfolomeev, M.B.; Velichko, A.V.; Zajtseva, L.L.; Shishkov, N.V.

    1977-01-01

    The reduction of perrhenates of rare earth elements and of yttrium by hydrogen and the subsequent sintering have yielded cermets based on rhenium and rare earth element oxides inherent in which are more disperse and homogeneous structures than those of the ''molecular'' rare earth element-Tc cermets. The dispersity of cermets increases in the rare earth elements series from La to Lu. The microhardness of the Re phase in cermets is 490 kgf/mm 2 ; the total microhardness of a cermet is substantially higher

  9. Microstructural development and mechanical properties of iron based cermets processed by pressureless and spark plasma sintering

    International Nuclear Information System (INIS)

    Alvaredo, P.; Gordo, E.; Van der Biest, O.; Vanmeensel, K.

    2012-01-01

    Highlights: ► Processing of Fe-based cermets by pressureless sintering and spark plasma sintering. ► Influence of carbon content on the sintering mechanism and hardness. ► The cermet phase diagram was calculated and permits to explain the microstructure. ► SPS provides ferritic matrix and different carbide distribution than CPS samples. ► Pressureless sintered samples contain retained austenite at room temperature. - Abstract: Iron-based cermets are an interesting class of metal-ceramic composites in which properties and the factors influencing them are to be explored. In this work the metal matrix contains Cr, W, Mo and V as alloying elements, and the hard phase is constituted by 50 vol% of titanium carbonitride (TiCN) particles. The work studies the influence of the C content and the processing method on the sinterability, microstructure and hardness of the developed cermet materials. For that purpose, cermet samples with different C content in the matrix (0 wt%, 0.25 wt%, 0.5 wt%, 1.0 wt%) were prepared by conventional pressureless sintering (CPS) and, in order to achieve finer microstructures and to reduce the sintering time, by spark plasma sintering (SPS). The density and hardness (HV30) of the processed materials was evaluated, while their phase composition and microstructure was characterised by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The equilibrium phase diagram of the composite material was calculated by ThermoCalc software in order to elucidate the influence of the carbon content on the obtained phases and developed microstructures.

  10. Cermet anode with continuously dispersed alloy phase and process for making

    Science.gov (United States)

    Marschman, Steven C.; Davis, Norman C.

    1989-01-01

    Cermet electrode compositions and methods for making are disclosed which comprise NiO--NiFe.sub.2 O.sub.4 --Cu--Ni. Addition of an effective amount of a metallic catalyst/reactant to a composition of a nickel/iron/oxide, NiO, copper, and nickel produces a stable electrode having significantly increased electrical conductivity. The metallic catalyst functions to disperse the copper and nickel as an alloy continuously throughout the oxide phase of the cermet to render the electrode compositon more highly electrically conductive than were the third metal not present in the base composition. The third metal is preferably added to the base composition as elemental metal and includes aluminum, magnesium, sodium and gallium. The elemental metal is converted to a metal oxide during the sintering process.

  11. Wear mechanisms of toughened zirconias

    International Nuclear Information System (INIS)

    Becker, P.C.; Libsch, T.A.; Rhee, S.K.

    1985-01-01

    The dry friction and wear behavior of toughened zirconias against hardened steel was studied using the falex ring and block technique. Three experimental ZrO 2 -Y 2 O 3 ceramics and two commerical ZrO 2 -MgO ceramics were investigated. Each ceramic was tested at 500 and 2000 rpm at normal loads in the range 2.3 to 40.8 kg. Significant trends in the friction and wear data were found correlating composition, test speeds, and loads. Microstructural examination of the ring, ceramic block, and wear debris has shown that the wear process is very complex and incorporates a number of mechanisms

  12. Effects of metal binder on the microstructure and mechanical properties of Ti(C,N)-based cermets

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Qingzhong; Ai, Xing, E-mail: aixingsdu@163.com; Zhao, Jun; Gong, Feng; Pang, Jiming; Wang, Yintao

    2015-09-25

    Highlights: • Ni–Co binder improves the solid solution reaction and the wetting of hard phases. • Cermets with 25 wt.% binder have evenly distributed grains with moderate rims. • Co/(Ni + Co) ratios influence the grain sizes and microstructure features of cermets. • The cermets with pure Co as binder exhibit optimal mechanical properties. - Abstract: To optimize the mechanical properties of Ti(C,N)-based cermets used as tool materials, the cermets with different Ni–Co binder contents and Co/(Ni + Co) weight ratios were prepared. The effects of metal binder content and Co/(Ni + Co) ratio on the microstructure and mechanical properties of Ti(C,N)-based cermets were investigated by scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and measuring the transverse rupture strength (TRS), Vickers hardness (HV) and fracture toughness (K{sub IC}). The experimental results reveal that increasing Ni–Co binder content can increase the thickness of rim phases by improving the solid solution reaction and the wetting of hard phases. The cermets with 25 wt.% binder addition present good comprehensive mechanical properties, which is attributed to the moderate rim phases and uniformly distributed Ti(C,N) grains. The Co/(Ni + Co) weight ratios in binder have a great influence on the grain sizes and microstructure features of Ti(C,N)-based cermets, in virtue of the synergic effects between the wettability of Co and the solubilizing capacity of Ni on hard phases. The cermets with pure Co as binder exhibit optimal mechanical properties with a TRS of 1767 ± 81 MPa, a hardness of 12.26 ± 0.10 GPa and a K{sub IC} of 8.40 ± 0.47 MPa m{sup 1/2}, which meet the requirements for tool materials. And the cermets with a Co/(Ni + Co) ratio of 0.2 have the second best mechanical properties with a TRS of 1848 ± 201 MPa, a hardness of 11.12 ± 0.40 GPa and a K{sub IC} of 9.43 ± 0.54 MPa m{sup 1/2}, in which the lower hardness can

  13. Effect of heating rate on the mechanical properties and microstructure of Ti(C,N)-based cermets

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Qingzhong; Ai, Xing, E-mail: aixingsdu@163.com; Zhao, Jun; Zhang, Hongshan; Qin, Wenzhen; Gong, Feng

    2015-03-25

    An appropriate heating rate in the sintering process is crucial to obtain the Ti(C,N)-based cermets with superior properties. In this paper, Ti(C,N)-based cermets were sintered to investigate the influence of heating rate on the mechanical properties and microstructure of the cermet materials. The transverse rupture strength (TRS), Vickers hardness (HV) and fracture toughness (K{sub IC}) were tested. The microstructure, indention crack, fracture morphology and phase composition of the cermets were also studied by scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results reveal that the heating rate has a great influence on the mechanical properties and microstructure of Ti(C,N)-based cermets. The cermets sintered at the heating rate of 3 °C/min between 1300 °C and 1430 °C have the optimum comprehensive mechanical properties with a transverse rupture strength of 1605±107 MPa, a hardness of 12.02±0.25 GPa and a fracture toughness of 10.73±0.40 MPa m{sup 1/2}. The heating rate can affect the reaction among the constituents of Ti(C,N)-based cermets and then influence the elements distribution in the core–rim microstructures and the lattice parameter of Ti(C,N) phase. When the heating rate is between 2 °C/min and 5 °C/min, the lower the heating rate is, the coarser the Ti(C,N) grains become. A higher heating rate is detrimental to the formation of core–rim microstructures, and a lower heating rate can result in grain coarsening and inhomogeneous microstructure. The observation of indention cracks and fracture surfaces show that the intergranular cracks and intergranular fractures mainly occur in the cermets with larger binder mean free path and medium grains. While the cleavage fractures appear more in the cermets with grain coarsening, and the transgranular fractures exist more in the cermets with non-fully developed fine grains.

  14. [Study of relationship between powder-size gradation and mechanical properties of Zirconia toughened glass infiltrated nanometer-ceramic composite powder].

    Science.gov (United States)

    Chai, Feng; Xu, Ling; Liao, Yun-mao; Chao, Yong-lie

    2003-07-01

    The fabrication of all-ceramic dental restorations is challenged by ceramics' relatively low flexural strength and intrinsic poor resistance to fracture. This paper aimed at investigating the relationships between powder-size gradation and mechanical properties of Zirconia toughened glass infiltrated nanometer-ceramic composite (Al(2)O(3)-nZrO(2)). Al(2)O(3)-nZrO(2) ceramics powder (W) was processed by combination methods of chemical co-precipitation and ball milling with addition of different powder-sized ZrO(2). Field-emission scanning electron microscopy was used to determine the particle size distribution and characterize the particle morphology of powders. The matrix compacts were made by slip-casting technique and sintered to 1,450 degrees C and flexural strength and the fracture toughness of them were measured. 1. The particle distribution of Al(2)O(3)-nZrO(2) ceramics powder ranges from 0.02 - 3.5 micro m and among them the superfine particles almost accounted for 20%. 2. The ceramic matrix samples with addition of nZrO(2) (W) showed much higher flexural strength (115.434 +/- 5.319) MPa and fracture toughness (2.04 +/- 0.10) MPa m(1/2) than those of pure Al(2)O(3) ceramics (62.763 +/- 7.220 MPa; 1.16 +/- 0.02 MPa m(1/2)). The particle size of additive ZrO(2) may impose influences on mechanical properties of Al(2)O(3)-nZrO(2) ceramics matrix. Good homogeneity and reasonable powder-size gradation of ceramic powder can improve the mechanical properties of material.

  15. Cermets and method for making same

    Science.gov (United States)

    Aaron, W. Scott; Kinser, Donald L.; Quinby, Thomas C.

    1983-01-01

    The present invention is directed to a method for making a wide variety of general-purpose cermets and for radioactive waste disposal from ceramic powders prepared from urea-dispersed solutions containing various metal values. The powders are formed into a compact and subjected to a rapid temperature increase in a reducing atmosphere. During this reduction, one or more of the more readily reducible oxides in the compact is reduced to a selected substoichiometric state at a temperature below the eutectic phase for that particular oxide or oxides and then raised to a temperature greater than the eutectic temperature to provide a liquid phase in the compact prior to the reduction of the liquid phase forming oxide to solid metal. This liquid phase forms at a temperature below the melting temperature of the metal and bonds together the remaining particulates in the cermet to form a solid polycrystalline cermet.

  16. Molybdenum-base cermet fuel development

    International Nuclear Information System (INIS)

    Gurwell, W.E.; Moss, R.W.; Pilger, J.P.; White, G.D.

    1987-07-01

    Development of a multimegawatt (MMW) space nuclear power system requires identification and resolution of several technical feasibility issues before selecting one or more promising system concepts. Demonstration of reactor fuel fabrication technology is required for cermet-fueled reactor concepts. MMW reactor fuel development activity at Pacific Northwest Laboratory (PNL) is focused on producing a molybdenum-matrix uranium-nitride (UN) fueled cermet. This cermet is to have a high matrix density (≥95%) for high strength and high thermal conductance coupled with a high particle (UN) porosity (∼25%) for retention of released fission gas at high burnup. Fabrication process development involves the use of porous TiN microspheres as surrogate fuel material until porous UN microspheres become available. Process development has been conducted in the areas of microsphere synthesis, particle sealing/coating, and high-energy-rate forming (HERF) and vacuum hot press consolidation techniques. This paper summarizes the status of these activities

  17. Experimental and numerical study of the high temperature mechanical behaviour of the MoTiC cermets

    International Nuclear Information System (INIS)

    Cedat, Denis

    2006-01-01

    In this work, in order to study the mechanical behaviour of Mo-TiC cermets, compression tests have been carried out on different compositions as well as on different temperatures on the composition (MoTiC 25at% ) which will be extruded. The main results show that: 1)the increase of the (TiC) ceramic rate in the cermet increases the rupture stress but decreases the rupture resistance of this material. Moreover, a transition of behaviour seems to be observed for a critical TiC rate (MoTiC 25at% ), this transition seems to be due to the percolation of the ceramic particles. 2)the behaviour of the MoTiC 25at% cermet is brittle at ambient temperature and begins to have a plastic deformation at 300 C. Thus, the rupture stress decreases proportionally to the increase of the temperature whereas the rupture deformation increases. (O.M.)

  18. Investigations on cermet electrodes for thermionic emitters

    International Nuclear Information System (INIS)

    Schmidt, D.; Nazare, S.

    1975-01-01

    Unstable Ba 2 CaWO 6 -W with their own supply of Ba, as well as stable UO 2 -Mo-emitter cermets that have to be operated with an external Ba-source, have been prepared by axial hot pressing. The relevant properties of these cermets such as electrical resistivity and thermal expansion are reported and compared with theoretical predictions. The electron emission of these materials is discussed on the basis of the surface films formed. It provides the basis for optimising the behavior of these materials

  19. High performance electrodes for reduced temperature solid oxide fuel cells with doped lanthanum gallate electrolyte. I. Ni-SDC cermet anode

    Science.gov (United States)

    Ohara, S.; Maric, R.; Zhang, X.; Mukai, K.; Fukui, T.; Yoshida, H.; Inagaki, T.; Miura, K.

    A Ni-samaria-doped ceria (SDC) cermet was selected as the anode material for reduced temperature (800°C) solid oxide fuel cells. The NiO-SDC composite powder, synthesized by spray pyrolysis, was employed as the starting anode powder in this study. The influence of Ni content in Ni-SDC cermets on the electrode performance was investigated in order to create the most suitable microstructures. It was found that anodic polarization was strongly influenced by the Ni content in Ni-SDC cermets. The best results were obtained for anode cermets with Ni content of around 50 vol.%; anodic polarization was about 30 mV at a current density of 300 mA/cm 2. This high performance seems to be attributable to the microstructure, in which Ni grains form a skeleton with well-connected SDC grains finely distributed over the Ni grains surfaces; such microstructure was also conducive to high stability of the anode.

  20. High performance electrodes for reduced temperature solide oxide fuel cells with doped lanthanum gallate electrolyte. Pt. 1. Ni-SDC cermet anode

    Energy Technology Data Exchange (ETDEWEB)

    Ohara, S.; Maric, R.; Zhang, X.; Mukai, K.; Fukui, T. [Japan Fine Ceramics Center, Nagoya (Japan); Yoshida, H.; Inagaki, T. [The Kansai Electroc Power Co. Inc., Hyogo (Japan); Miura, K. [Kanden Kakou Co. Ltd., Hyogo (Japan)

    2000-03-01

    A Ni-samaria-doped ceria (SDC) cermet was selected as the anode material for reduced temperature (800 C) solid oxide fuel cells. The NiO-SDC composite powder, synthesized by spray pyrolysis, was employed as the starting anode powder in this study. The influence of Ni content in Ni-SDC cermets on the electrode performance was investigated in order to create the most suitable microstructures. It was found that anodic polarization was strongly influenced by the Ni content in Ni-SDC cermets. The best results were obtained for anode cermets with Ni content of around 50 vol.%; anodic polarization was about 30 mV at a current density of 300 mA/cm{sup 2}. This high performance seems to be attributable to the microstructure, in which Ni grains form a skeleton with well-connected SDC grains finely distributed over the Ni grains surfaces; such microstructure was also conducive to high stability of the anode. (orig.)

  1. Mechanical Properties of Supports and Half‐Cells for Solid Oxide Electrolysis Influenced by Alumina‐Zirconia Composites

    DEFF Research Database (Denmark)

    Charlas, Benoit; Ni, De Wei; Frandsen, Henrik Lund

    2017-01-01

    In order to improve the durability and robustness of solid oxide electrolysis cells (SOEC) and stacks, it is necessary to improve the strength of its components. In cathode supported SOEC, the main structural component is the Ni(O)- YSZ support. But the strength of the half-cell or cell is also...... determined by the strength of other weaker components and by the residual stress state induced by the thermal expansion mismatch. In this study, the mechanical properties of Ni(O)-3YSZ supports with a reference composition and with substitution of 3YSZ by 20A3YSZ (3YSZ with 20 wt.% Al2O3) have been tested...... and compared. The initial interest of this substitution are a decrease of the coefficient of thermal expansion (CTE) mismatch within the half-cell and the fact that 20A3YSZ is stronger than 3YSZ. The influence of the process on the composition, strength, elastic properties and electrical conductivity...

  2. Ni-YSZ cermet substrate supported thin SDC and YSZ+SDC bi-layer SOFCs

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, X.; Robertson, M.; Deces-Petit, C.; Xie, Y.; Hui, R.; Yick, S.; Styles, E.; Roller, J.; Kesler, O.; Qu, W.; Jankovic, J.; Tang, Z.; Perednis, D.; Maric, R.; Ghosh, D. [National Research Council of Canada, Vancouver, BC (Canada). Inst. for Fuel Cell Innovation

    2005-07-01

    One of the disadvantages of a ceria-based electrolyte is that it becomes a mixed conductor at anode conditions, which causes cell voltage loss and fuel efficiency loss due to internal shorting. Chemical and mechanical stability is another concern for long-term service. To lower manufacturing costs, efforts have been made to bring proven semiconductor manufacturing technology to Solid Oxide Fuel Cells (SOFCs). This study employed Tape casting of cermet substrates, Screen-printing of functional layers and Co-firing of cell components (TSC) to fabricate nickel (Ni)-cermet supported cells with mainly ceria-based thin electrolytes. Ni-Yttria-Stabilized Zirconia (YSZ) cermet supported cell with Samaria Doped Ceria (SDC) single layer electrolytes and YSZ+SDC bi-layer electrolytes were successfully developed for low-temperature performance characterization. The elemental distribution at the cell interface was mapped and the electrochemical performance of the cells was recorded. Many high-Zr-content micro-islands were found on the thin SDC surface. The influence of co-firing temperature and thin-film preparation methods on the Zr-islands' appearance was also investigated. Using in-situ sintered cathodes, high performance of the SDC cells was obtained. It was concluded that the bi-layer cells did show higher Open Circuit Voltage (OCV) values, with 1180 mW/cm{sup 2} at 650 degrees C, as well as good performance at 700-800 degrees C, with near OCV value. However, their performance was much lower than those of the SDC cells at low operating temperature. Zr-micro-islands formation on the SDC electrolyte was observed and investigated. 6 refs., 5 tabs., 7 figs.

  3. Stochastic Computer Simulation of Cermet Coatings Formation

    Directory of Open Access Journals (Sweden)

    Oleg P. Solonenko

    2015-01-01

    Full Text Available An approach to the modeling of the process of the formation of thermal coatings lamellar structure, including plasma coatings, at the spraying of cermet powders is proposed. The approach based on the theoretical fundamentals developed which could be used for rapid and sufficiently accurate prediction of thickness and diameter of cermet splats as well as temperature at interface “flattening quasi-liquid cermet particle-substrate” depending on the key physical parameters (KPPs: temperature, velocity and size of particle, substrate temperature, and concentration of finely dispersed solid inclusions uniformly distributed in liquid metal binder. The results are presented, which concern the development of the computational algorithm and the program complex for modeling the process of laying the splats in the coating with regard to the topology of its surface, which varies dynamically at the spraying, as well as the formation of lamellar structure and porosity of the coating. The results of numerical experiments are presented through the example of thermal spraying the cermet TiC-30 vol.% NiCr powder, illustrating the performance of the developed computational technology.

  4. Nonlinear oxidation kinetics of nickel cermets

    International Nuclear Information System (INIS)

    Galinski, Henning; Bieberle-Huetter, Anja; Rupp, Jennifer L.M.; Gauckler, Ludwig J.

    2011-01-01

    The oxidation of a cermet of screen-printed nickel (Ni) and gadolinia-doped ceria (CGO) with an approximate median porosity of 50 vol.% has been studied via in situ X-ray diffraction and focused ion beam nanotomography in the temperature range 773-848 K. The oxidation kinetics of Ni to NiO is found to be highly nonlinear with an apparent activation energy of 2.8(2) eV in this temperature range. The nonlinear oxidation kinetics found is in good agreement with theoretical works on oxide growth driven by nonlinear inbuilt fields. Stress-induced Kirkendall void formation has been identified as the physical process that enhances the oxidation of Ni/CGO cermets. Compressive stresses within the Ni matrix result from the thermal expansion mismatch of Ni and CGO and cause plastic deformation as they exceed the yield stress of the Ni matrix. The pore size distribution of Kirkendall voids formed has been measured by FIB nanotomography and shows a significant temperature dependence. It is shown that even one cycle of reoxidation changes irreversibly the microstructure of the cermet which can be interpreted as the onset and main contribution to the mechanical degradation of the cermet.

  5. Multi-axial response of idealized cermets

    International Nuclear Information System (INIS)

    Pickering, E.G.; Bele, E.; Deshpande, V.S.

    2016-01-01

    The yield response of two idealized cermets comprising mono and bi-disperse steel spheres in a Sn/Pb solder matrix has been investigated for a range of axisymmetric stress states. Proportional stress path experiments are reported, from which are extracted the initial yield surfaces and their evolution with increasing plastic strain. The initial yield strength is nearly independent of the hydrostatic pressure but the strain hardening rate increases with stress triaxiality up to a critical value. For higher triaxialities, the responses are independent of hydrostatic pressure. Multi-axial measurements along with X-ray tomography were used to demonstrate that the deformation of these idealized cermets occurs by two competing mechanisms: (i) a granular flow mechanism that operates at low levels of triaxiality, where volumetric dilation occurs under compressive stress states, and (ii) a plastically incompressible mechanism that operates at high stress triaxialities. A phenomenological viscoplastic constitutive model that incorporates both deformation mechanisms is presented. While such multi-axial measurements are difficult for commercial cermets with yield strengths on the order of a few GPa, the form of their constitutive relation is expected to be similar to that of the idealized cermets presented here.

  6. Fractographic peculiarities of cermet tungsten fracture

    International Nuclear Information System (INIS)

    Stepanenko, V.A.; Babak, A.V.; Uskov, E.I.

    1982-01-01

    Effect of test temperature on fracture peculiarities of cermets tungsten with initial cellular structure of deformation is shown. Tungsten crack resistance increases at temperatures to Tsub(x) (ductile-brittle transition temperature) and decreases at temperatures above Tsub(x). The degree of ceramics tungsten plasticity realization depends on its crack resistance

  7. Electrochemical behaviour of Ni-BZO and Ni-BZY cermet anodes for Protonic Ceramic Fuel Cells (PCFCs) – A comparative study

    International Nuclear Information System (INIS)

    Nasani, Narendar; Ramasamy, Devaraj; Antunes, Isabel; Perez, Jose; Fagg, Duncan P.

    2015-01-01

    Highlights: • Cermet anodes Ni-BaZrO 3 (Ni-BZO) & Ni-BaZr 0.85 Y 0.15 O 3-δ (Ni-BZY) were synthesised • Resultant microstructure of both cermet anodes shown to be similar • Minimum Rp in Ni-BZY in 10%H 2 /N 2 with matrix phase of higher proton conductivity. • Strong links shown between R2 and proton conduction in cermet matrix phase. • Magnitude of R3 lower for Ni-BZO than for Ni-BZY under similar conditions. - Abstract: The matrix phase of protonic ceramic fuel cell (PCFC) cermet anodes potentially plays a vital role in hydrogen oxidation kinetics. The present work aims to investigate such involvement by selecting ceramic-oxide matrices with widely dissimilar levels of proton conduction. The materials chosen were that of the proton conducting phase BaZr 0.85 Y 0.15 O 3-δ and the nominal composition BaZrO 3 of negligible proton conduction. Cermet anodes Ni-BaZrO 3 and Ni-BaZr 0.85 Y 0.15 O 3-δ were synthesized by the acetate-H 2 O 2 combustion method for Ni contents of 40 vol%. The microstructure and electrochemical performance of the cermet anodes were investigated by scanning electron microscopy (SEM) and electrochemical impedance measurements (EIS) respectively. The polarisation behaviour of the two nickel cermet anodes was studied as a function of temperature, hydrogen partial pressure (pH 2 ) and water vapor partial pressure (pH 2 O). The results confirm that polarisation resistance is highly sensitive to the composition of the ceramic phase of the cermet anode and that the higher frequency electrode response exhibits strong links to levels of proton transport in the ceramic-oxide matrix

  8. Working of Mo-TiC cermets for 'future nuclear systems'; Mise en forme de cermets Mo-TiC pour les 'Systemes Nucleaires du futur'

    Energy Technology Data Exchange (ETDEWEB)

    Allemand, Alexandre [CEA-Saclay, DRT/LITEN/LTMEx, 91191 Gif-sur-Yvette (France); Le Flem, Marion [CEA-Saclay, DEN/DMN/SRMA, 91191 Gif-sur-Yvette (France); Rousselet, Jerome [UTT Troyes, 10010 Troyes (France)

    2006-07-01

    The nuclear reactor cores (generation IV) will form an extremely severe environment (high temperature, severe and long irradiation...). These drastic criteria and the preoccupation to ensure a higher and higher safety level lead, beyond the preoccupations due to the feasibility of such reactors, to harsh choices in materials able to be used. Innovating materials such as Mo-TiC cermet are the subject of intense researches in the CEA. This study presents and compares two modes of Mo-TiC cermet working: the hot isostatic compression and the extrusion. Different compositions of Mo-TiC cermets are prepared by hot isostatic compression and extrusion, and then characterized in term of microstructural properties. At last, this study concludes to a very satisfying working by hot isostatic compression, nevertheless the extrusion has still to be improved. (O.M.)

  9. Microstructure and properties of multiphase sintered cermets Fe-Fe2B

    International Nuclear Information System (INIS)

    Nowacki, J.; Klimek, L.

    1998-01-01

    The process of multiphase sintering of iron in the vacuum has been analysed. As a result of the process iron-iron boride cermets have been produced. Fe-Fe 2 B cermets were obtained as a result of sintering of the Fe and B pure elements in the vacuum. Attemps at sintering in the solid phase and with the participation of the liquid phase, the Fe-Fe 2 B eutectic, have been made. Metallographic qualitative and quantitative studies, X-ray structural qualitative and qauantitative analysis allowed to determine the structure of Fe 2 B cermets, as well as a description of the kinetics of quantitative changes in phase proportions in the course of sintering. It has been found that their structure varies widely depending on sintering parameters and the composition of the sinters. Measurements of the Fe-Fe 2 B cermets hardness and measurements on wear during dry friction by the pin-on-disc method have shown distinct advantages of the cermets as a modern constructional materials. The hardness of Fe-Fe 2 B cermets, depending on their chemical composition and sintering parameters, ranges widely from 150 to 1500 HV, and their resistance to wear is comparable to that of diffusively boronized steels. FeFe 2 B cermets are a composite material in which iron boride, Fe 2 B, with a hardness of about 1800 HV plays the role of the reinforcement,while iron-iron boride, Fe-Fe 2 B, with a hardness of about 500 HV plays the role of matrix. The eutectic in the spaces between iron boride grains is composed of boron solid solution plates in iron with a hardness of arround 250 HV, and iron boride, Fe 2 B, plates with a hardness of approximaly 1800 HV. The combination of such different materials, a hard reinforcement and a relatively plastic matrix produces favourable properties of the cermet thus produced high hardness (1500 HV) constant over whole cross section of the material, resistance of abrasive wear and acceptable ductility. The properties mentioned above, resulting from the cermet

  10. Characteristics of nanosized zirconia prepared by plasma and chemical technique

    International Nuclear Information System (INIS)

    Kuznetsova, L.; Grabis, J.; Heidemane, G.

    2003-01-01

    The studied preparation method of zirconia using the plasma technique, azeotropic distillation and glycine routes ensure obtaining of nano sized powders with close average particle size but different crystallite size and phase composition. The sinterability of nano sized zirconia particles prepared by plasma technique or wet-chemical methods is similar and depends on the green density of pressed powders, improvement of with can be achieved by using of granulated precursors. (authors)

  11. Methods of fabricating cermet materials and methods of utilizing same

    Science.gov (United States)

    Kong, Peter C.

    2006-04-04

    Methods of fabricating cermet materials and methods of utilizing the same such as in filtering particulate and gaseous pollutants from internal combustion engines having intermetallic and ceramic phases. The cermet material may be made from a transition metal aluminide phase and an aluminia phase. The mixture may be pressed to form a green compact body and then heated in a nitrogen-containing atmosphere so as to melt aluminum particles and form the cermet. Filler materials may be added to increase the porosity or tailor the catalytic properties of the cermet material. Additionally, the cermet material may be reinforced with fibers or screens. The cermet material may also be formed so as to pass an electrical current therethrough to heat the material during use.

  12. Methods of producing cermet materials and methods of utilizing same

    Science.gov (United States)

    Kong, Peter C [Idaho Falls, ID

    2008-12-30

    Methods of fabricating cermet materials and methods of utilizing the same such as in filtering particulate and gaseous pollutants from internal combustion engines having intermetallic and ceramic phases. The cermet material may be made from a transition metal aluminide phase and an alumina phase. The mixture may be pressed to form a green compact body and then heated in a nitrogen-containing atmosphere so as to melt aluminum particles and form the cermet. Filler materials may be added to increase the porosity or tailor the catalytic properties of the cermet material. Additionally, the cermet material may be reinforced with fibers or screens. The cermet material may also be formed so as to pass an electrical current therethrough to heat the material during use.

  13. Dynamic SEM wear studies of tungsten carbide cermets. [friction and wear experiments

    Science.gov (United States)

    Brainard, W. A.; Buckley, D. H.

    1975-01-01

    Dynamic friction and wear experiments were conducted in a scanning electron microscope. The wear behavior of pure tungsten carbide and composite with 6 and 15 weight percent cobalt binder was examined, and etching of the binder was done to selectively determine the role of the binder in the wear process. Dynamic experiments were conducted as the tungsten carbide (WC) and bonded WC cermet surfaces were transversed by a 50 micron radiused diamond stylus. These studies show that the predominant wear process in WC is fracture initiated by plastic deformation, and the wear of the etched cermets is similar to pure WC. The presence of the cobalt binder reduces both friction and wear. The cementing action of the cobalt reduces granular separation, and promotes a dense polished layer because of its low shear strength film-forming properties. The wear debris generated from unetched surface is approximately the same composition as the bulk.

  14. Development of Mo base alloys for conductive metal-alumina cermet applications

    International Nuclear Information System (INIS)

    Stephens, J.J.; Damkroger, B.K.; Monroe, S.L.

    1996-01-01

    A study of thermal expansion for binary Mo-V and ternary Mo-V-Fe/Mo-V-Co alloys has been conducted, with the aim of finding a composition which matches the CTE of 94% alumina ceramic. The overall goal was to identify an alloy which can be used in conductive 27 vol.% metal/73 vol.% alumina cermets. Besides thermal expansion properties, two additional requirements exist for this alloy: (1) compatibility with a hydrogen sinter fire atmosphere and (2) a single phase BCC microstructure. They have identified a ternary alloy with a nominal composition of Mo-22wt.% V-3Fe for use in cermet fabrication efforts. This paper summarizes thermal expansion properties of the various alloys studied, and compares the results with previous CTE data for Mo-V binary alloys

  15. Development of cermets for high-level radioactive waste fixation

    International Nuclear Information System (INIS)

    Aaron, W.S.; Quinby, T.C.; Kobisk, E.H.

    1979-01-01

    A method is currently under development for the solidification and fixation of commercial and defense high-level radioactive wastes in the form of ceramic particles encapsulated by metal, i.e., a cermet. The chemical and physical processing techniques which have been developed and the properties of the resulting cermet bodies are described in this paper. These cermets have the advantages of high thermal conductivity and low leach rates

  16. Zirconia toughened ceramics for heat engine applications

    International Nuclear Information System (INIS)

    Rossi, G.A.; Blum, J.B.; Manwiller, K.E.; Knapp, C.E.

    1986-01-01

    Three classes of zirconia toughened ceramics (ZTC) were studied, i.e. Mg-PSZ (MgO-partially stabilized zirconia), Y-TZP (Y/sub 2/O/sub 3/-tetragonal zirconia polycrystals) and ZTA (zirconia toughened alumina). The main objective was to improve the high temperature strength and toughness, which are not satisfactory in the ''state of the art'' ZTC materials. Powders prepared by melting/rapid solidification and by chemical routes were used. The green parts were made by both dry and wet shape forming methods. Fine grained Mg-PSZ ceramics with unique microstructures were produced using the rapidly solidified powders. The Y-TZP materials were improved mainly through microstructure control and by addition of alpha alumina as a dispersed phase. Preliminary results on ZTA ceramics made with the rapidly solidified powders were also obtained. It is concluded that the Al/sub 2/O/sub 3//Y-TZP composites offer a good chance of meeting the program objectives

  17. Class II glass ionomer cermet tunnel, resin sandwich and amalgam restorations over 2 years.

    Science.gov (United States)

    Wilkie, R; Lidums, A; Smales, R

    1993-08-01

    This study compared the clinical behavior of a glass ionomer (polyalkenoate) silver cermet, a posterior resin composite used with the "tunnel" technique, a posterior resin composite used with the "closed sandwich" technique, and a high-copper amalgam for restoring small, proximal surface carious lesions. Two dentists placed 86 restorations in the posterior permanent teeth of 26 adults treated at a dental hospital. Restorations were assessed at 6-month intervals over 2 years for gingivitis adjacent to them, the tightness of proximal contacts, occlusal wear, surface voids, roughness and cracking, surface and marginal staining, and marginal fracture. Small filling defects, surface voids and occlusal wear were obvious with the cermet material, with surface crazing and cracking present in 48% of the tunnel restorations. Two of the posterior resin composites, but none of the amalgam restorations, also failed. The cermet cannot be recommended as a long-term permanent restorative material in situations where it is likely to be subjected to heavy occlusal stresses and abrasive wear.

  18. Zirconia based dental ceramics: structure, mechanical properties, biocompatibility and applications.

    Science.gov (United States)

    Gautam, Chandkiram; Joyner, Jarin; Gautam, Amarendra; Rao, Jitendra; Vajtai, Robert

    2016-12-06

    Zirconia (ZrO 2 ) based dental ceramics have been considered to be advantageous materials with adequate mechanical properties for the manufacturing of medical devices. Due to its very high compression strength of 2000 MPa, ZrO 2 can resist differing mechanical environments. During the crack propagation on the application of stress on the surface of ZrO 2 , a crystalline modification diminishes the propagation of cracks. In addition, zirconia's biocompatibility has been studied in vivo, leading to the observation of no adverse response upon the insertion of ZrO 2 samples into the bone or muscle. In vitro experimentation has exhibited the absence of mutations and good viability of cells cultured on this material leading to the use of ZrO 2 in the manufacturing of hip head prostheses. The mechanical properties of zirconia fixed partial dentures (FPDs) have proven to be superior to other ceramic/composite restorations and hence leading to their significant applications in implant supported rehabilitations. Recent developments were focused on the synthesis of zirconia based dental materials. More recently, zirconia has been introduced in prosthetic dentistry for the fabrication of crowns and fixed partial dentures in combination with computer aided design/computer aided manufacturing (CAD/CAM) techniques. This systematic review covers the results of past as well as recent scientific studies on the properties of zirconia based ceramics such as their specific compositions, microstructures, mechanical strength, biocompatibility and other applications in dentistry.

  19. Powder metallurgy and fabricating processes of cermet and metmet fuel in Russia

    International Nuclear Information System (INIS)

    Vatulin, A.; Konovalov, I.; Savchenco, A.; Stetsky, Y.; Trifonov, Y.; Bochvar, A.A.

    2000-01-01

    Methods of powder metallurgy are widely used for manufacturing of various components of reactor core: beryllium reflectors, absorbers, parts of controlling and safety systems, fuel pellets for fuel elements of power reactors and etc. The new problems arising before atomic engineering associated with increasing requirements to safe operation of reactors, non-proliferation of the nuclear weapons and utilization of plutonium stockpile in the world, served as a push to development of new kinds of dispersion nuclear fuel CERMET, CERCER, METMET. The bases of fabricating processes of such compositions are the methods of powder metallurgy. In this report some results of research activities on the development of new kinds of CERMET and METMET fuel and fuel elements for different type reactors are presented. (author)

  20. Enhancing charge transfer kinetics by nanoscale catalytic cermet interlayer.

    Science.gov (United States)

    An, Jihwan; Kim, Young-Beom; Gür, Turgut M; Prinz, Fritz B

    2012-12-01

    Enhancing the density of catalytic sites is crucial for improving the performance of energy conversion devices. This work demonstrates the kinetic role of 2 nm thin YSZ/Pt cermet layers on enhancing the oxygen reduction kinetics for low temperature solid oxide fuel cells. Cermet layers were deposited between the porous Pt cathode and the dense YSZ electrolyte wafer using atomic layer deposition (ALD). Not only the catalytic role of the cermet layer itself but the mixing effect in the cermet was explored. For cells with unmixed and fully mixed cermet interlayers, the maximum power density was enhanced by a factor of 1.5 and 1.8 at 400 °C, and by 2.3 and 2.7 at 450 °C, respectively, when compared to control cells with no cermet interlayer. The observed enhancement in cell performance is believed to be due to the increased triple phase boundary (TPB) density in the cermet interlayer. We also believe that the sustained kinetics for the fully mixed cermet layer sample stems from better thermal stability of Pt islands separated by the ALD YSZ matrix, which helped to maintain the high-density TPBs even at elevated temperature.

  1. Cermet-fueled reactors for advanced space applications

    International Nuclear Information System (INIS)

    Cowan, C.L.; Palmer, R.S.; Taylor, I.N.; Vaidyanathan, S.; Bhattacharyya, S.K.; Barner, J.O.

    1987-12-01

    Cermet-fueled nuclear reactors are attractive candidates for high-performance advanced space power systems. The cermet consists of a hexagonal matrix of a refractory metal and a ceramic fuel, with multiple tubular flow channels. The high performance characteristics of the fuel matrix come from its high strength at elevated temperatures and its high thermal conductivity. The cermet fuel concept evolved in the 1960s with the objective of developing a reactor design that could be used for a wide range of mobile power generating sytems, including both Brayton and Rankine power conversion cycles. High temperature thermal cycling tests for the cermet fuel were carried out by General Electric as part of the 710 Project (General Electric 1966), and by Argonne National Laboratory in the Direct Nuclear Rocket Program (1965). Development programs for cermet fuel are currently under way at Argonne National Laboratory and Pacific Northwest Laboratory. The high temperature qualification tests from the 1960s have provided a base for the incorporation of cermet fuel in advanced space applications. The status of the cermet fuel development activities and descriptions of the key features of the cermet-fueled reactor design are summarized in this paper

  2. Fabrication and thermal conductivity of boron carbide/copper cermet

    International Nuclear Information System (INIS)

    Maruyama, Tadashi; Onose, Shoji

    1999-01-01

    Studies on fabrication and thermal conductivity of B 4 C/Cu cermet were made to obtain high performance neutron absorber materials for Liquid Metal-cooled Fast Breeder Reactor (LMFBR). A mixed powder of B 4 C and Cu was mechanically blended at high speed thereby a coating layer of Cu was formed on the surface of B 4 C powder. Then the B 4 C powder with Cu coating was hot pressed at temperatures from 950 to 1,050degC to form a B 4 C cermet. A high density B 4 C/Cu cermet with 70 vol% of B 4 C and relative density higher than 90% was successfully fabricated. In spite of the low volume fraction of Cu, the B 4 C/Cu cermet exhibited high thermal conductivity which originated from the existence of continuous metallic phase Cu in B 4 C/Cu cermet. (author)

  3. Bonding effectiveness to different chemically pre-treated dental zirconia.

    Science.gov (United States)

    Inokoshi, Masanao; Poitevin, André; De Munck, Jan; Minakuchi, Shunsuke; Van Meerbeek, Bart

    2014-09-01

    The objective of this study was to evaluate the effect of different chemical pre-treatments on the bond durability to dental zirconia. Fully sintered IPS e.max ZirCAD (Ivoclar Vivadent) blocks were subjected to tribochemical silica sandblasting (CoJet, 3M ESPE). The zirconia samples were additionally pre-treated using one of four zirconia primers/adhesives (Clearfil Ceramic Primer, Kuraray Noritake; Monobond Plus, Ivoclar Vivadent; Scotchbond Universal, 3M ESPE; Z-PRIME Plus, Bisco). Finally, two identically pre-treated zirconia blocks were bonded together using composite cement (RelyX Ultimate, 3M ESPE). The specimens were trimmed at the interface to a cylindrical hourglass and stored in distilled water (7 days, 37 °C), after which they were randomly tested as is or subjected to mechanical ageing involving cyclic tensile stress (10 N, 10 Hz, 10,000 cycles). Subsequently, the micro-tensile bond strength was determined, and SEM fractographic analysis performed. Weibull analysis revealed the highest Weibull scale and shape parameters for the 'Clearfil Ceramic Primer/mechanical ageing' combination. Chemical pre-treatment of CoJet (3M ESPE) sandblasted zirconia using Clearfil Ceramic Primer (Kuraray Noritake) and Monobond Plus (Ivoclar Vivadent) revealed a significantly higher bond strength than when Scotchbond Universal (3M ESPE) and Z-PRIME Plus (Bisco) were used. After ageing, Clearfil Ceramic Primer (Kuraray Noritake) revealed the most stable bond durability. Combined mechanical/chemical pre-treatment, the latter with either Clearfil Ceramic Primer (Kuraray Noritake) or Monobond Plus (Ivoclar Vivadent), resulted in the most durable bond to zirconia. As a standard procedure to durably bond zirconia to tooth tissue, the application of a combined 10-methacryloyloxydecyl dihydrogen phosphate/silane ceramic primer to zirconia is clinically highly recommended.

  4. Zirconia concentrate chlorination

    International Nuclear Information System (INIS)

    Costa, N.G.; Albuquerque Brocchi, E. de

    1990-01-01

    Chlorination experiments were conducted in order to study the kinetics of gasification of the zirconium oxide present in the zirconia concentrate. The variables studied are temperature (1173 to 1373 K), percentage of reducing agent (12 to 36%) and porosity (22 to 30%). The results indicated a greater influence of temperature and percentage of reducing agent as well as allowed the conclusion that a balance between the levels of these variables is an important factor in the appropriate chlorination conditions. (author)

  5. The Aqueous Electrochemical Response of TiC–Stainless Steel Cermets

    Directory of Open Access Journals (Sweden)

    Chukwuma Onuoha

    2018-05-01

    Full Text Available A family of TiC–stainless steel ceramic–metal composites, or cermets, has been developed in the present study, using steel grades of 304 L, 316 L, or 410 L as the binder phase. Melt infiltration was used to prepare the cermets, with the steel binder contents varying between 10–30 vol. %. The corrosion behaviour was evaluated using a range of electrochemical techniques in an aqueous solution containing 3.5 wt. % NaCl. The test methods included potentiodynamic, cyclic, and potentiostatic polarisation. The corroded samples were subsequently characterised using scanning electron microscopy (SEM and energy dispersive X-ray spectroscopy (EDS, while the post-corrosion solutions were analysed using inductively coupled plasma optical emission spectroscopy (ICP-OES to determine the residual ionic and particulate material removed from the cermets during electrochemical testing. It was demonstrated that the corrosion resistance was enhanced through decreasing the steel binder content, which arises due to the preferential dissolution of the binder phase, while the TiC ceramic remains largely unaffected. Increasing corrosion resistance was observed in the sequence TiC-304 L > TiC-316 L > TiC-410 L.

  6. Microstructure and thermal conductivity of Mo-TiC cermets processed by hot isostatic pressing

    International Nuclear Information System (INIS)

    Le Flem, Marion; Allemand, Alexandre; Urvoy, Stephane; Cedat, Denis; Rey, Colette

    2008-01-01

    In the scope of refractory material development for structural applications in the core of future nuclear reactors (gas fast reactors working between 500 o C and at least 800 o C in nominal conditions and up to 1650 o C in accidental scenarios), five Mo-TiC cermets, and single-phase TiC and Mo, were processed by hot isostatic pressing. Starting TiC volume contents were 0%, 12.5%, 25%, 37.5%, 50%, 75% and 100%. First, high dense specimens were characterized in terms of microstructure, composition and phase volume fractions. Cermets exhibited two phases in agreement with phase diagram previsions (Mo-TiC 1-2at.% and TiC-Mo 10-15at.% ), and a residual non-reacted TiC-rich phase (TiC-Mo 1at.% ). Second, heat capacity and thermal diffusivity were measured up to 1000 o C which allowed to evaluate the thermal conductivity of each cermet: this lays between TiC conductivity (12-18 W/m K) and Mo conductivity (95-125 W/m K), thermal properties continuously decreasing with starting TiC content. An analytical approach based on the volume fraction and properties of each constituent allowed to highlight the existence of thermal resistance at the interphases at low temperature

  7. Microstructure and properties of TiC-high manganese steel cermet prepared by different sintering processes

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Zhi; Lin, Tao, E-mail: lintao@ustb.edu.cn; He, Xinbo; Shao, Huiping; Zheng, Jianshu; Qu, Xuanhui

    2015-11-25

    In the paper, the TiC −50 wt.% high manganese steel cermet was made with different sintering processes including vacuum sintering, hot pressing, microwave sintering and spark plasma sintering (SPS). The microstructure, porosity and fracture morphology of the samples were analyzed with scanning electron microscopy (SEM). Phase analysis was carried out using X-ray diffraction (XRD). The density, hardness, transverse rupture strength (TRS) and wear resistance were investigated for the effect of the sintering processes. The results showed that the core–shell structure was not clearly observed for the TiC particles in microstructures and the high manganese steel matrix is BCC structure. Hot pressing, microwave sintering and SPS are useful processes for densification of the cermet. Nearly full density and higher hardness can be reached by these three processes at a lower sintering temperature and in a shorter sintering time. However, higher TRS can be reached by means of alloying completely in a longer sintering time, for example vacuum sintering. Pre-sintering in a long sintering time at a lower sintering temperature is also useful for improving the TRS. Finally, vacuum sintering is an effective process for producing this composite with the lowest cost in the mass production. - Highlights: • TiC-high manganese steel cermets were prepared by four sintering processes. • The core–shell structure was not clearly observed for the TiC particles in microstructures. • Th high manganese steel matrix is BCC structure instead of FCC structure. • Pre-sintering before microwave sintering is also useful for improving the TRS. • Vacuum sintering can be effective way for prepare this cermet in mass production.

  8. Submersion criticality safety of tungsten-rhenium urania cermet fuel for space propulsion and power applications

    Energy Technology Data Exchange (ETDEWEB)

    Craft, A.E., E-mail: aaron.craft@inl.gov [Center for Space Nuclear Research (CSNR), INL, Idaho Falls, ID (United States); O’Brien, R.C., E-mail: Robert.OBrien@inl.gov [Center for Space Nuclear Research (CSNR), INL, Idaho Falls, ID (United States); Howe, S.D., E-mail: Steven.Howe@inl.gov [Center for Space Nuclear Research (CSNR), INL, Idaho Falls, ID (United States); King, J.C., E-mail: kingjc@mines.edu [Nuclear Science and Engineering Program, Metallurgical and Materials Engineering Department, Colorado School of Mines, Golden, CO 80401 (United States)

    2014-07-01

    Highlights: • Criticality safety studies consider a generic space nuclear reactor in reentry scenarios. • Describes the submersion criticality behavior for a reactor fueled with a tungsten cermet fuel. • Study considers effects of varying fuel content, geometry, and other conditions. - Abstract: Nuclear thermal rockets are the preferred propulsion technology for a manned mission to Mars, and tungsten–uranium oxide cermet fuels could provide significant performance and cost advantages for nuclear thermal rockets. A nuclear reactor intended for use in space must remain subcritical before and during launch, and must remain subcritical in launch abort scenarios where the reactor falls back to Earth and becomes submerged in terrestrial materials (including seawater, wet sand, or dry sand). Submersion increases reflection of neutrons and also thermalizes the neutron spectrum, which typically increases the reactivity of the core. This effect is typically very significant for compact, fast-spectrum reactors. This paper provides a submersion criticality safety analysis for a representative tungsten/uranium oxide fueled reactor with a range of fuel compositions. Each submersion case considers both the rhenium content in the matrix alloy and the uranium oxide volume fraction in the cermet. The inclusion of rhenium significantly improves the submersion criticality safety of the reactor. While increased uranium oxide content increases the reactivity of the core, it does not significantly affect the submersion behavior of the reactor. There is no significant difference in submersion behavior between reactors with rhenium distributed within the cermet matrix and reactors with a rhenium clad in the coolant channels. The combination of the flooding of the coolant channels in submersion scenarios and the presence of a significant amount of spectral shift absorbers (i.e. high rhenium concentration) further decreases reactivity for short reactor cores compared to longer cores.

  9. Overlay metallic-cermet alloy coating systems

    International Nuclear Information System (INIS)

    Gedwill, M.A.; Glasgow, T.K.; Levine, S.R.

    1982-01-01

    A substrate, such as a turbine blade, vane, or the like, which is subjected to high temperature use is coated with a base coating of an oxide dispersed, metallic alloy (cermet). A top coating of an oxidation, hot corrosion, erosion resistant alloy of nickel, cobalt, or iron is then deposited on the base coating. A heat treatment is used to improve the bonding. The base coating serves as an inhibitor to interdiffusion between the protective top coating and the substrate. Otherwise, the protective top coating would rapidly interact detrimentally with the substrate and degrade by spalling of the protective oxides formed on the outer surface at elevated temperatures

  10. Overlay metallic-cermet alloy coating systems

    Science.gov (United States)

    Gedwill, M. A.; Levine, S. R.; Glasgow, T. K. (Inventor)

    1984-01-01

    A substrate, such as a turbine blade, vane, or the like, which is subjected to high temperature use is coated with a base coating of an oxide dispersed, metallic alloy (cermet). A top coating of an oxidation, hot corrosion, erosion resistant alloy of nickel, cobalt, or iron is then deposited on the base coating. A heat treatment is used to improve the bonding. The base coating serves as an inhibitor to interdiffusion between the protective top coating and the substrate. Otherwise, the protective top coating would rapidly interact detrimentally with the substrate and degrade by spalling of the protective oxides formed on the outer surface at elevated temperatures.

  11. Final report on cermet high-level waste forms

    International Nuclear Information System (INIS)

    Kobisk, E.H.; Quinby, T.C.; Aaron, W.S.

    1981-08-01

    Cermets are being developed as an alternate method for the fixation of defense and commercial high level radioactive waste in a terminal disposal form. Following initial feasibility assessments of this waste form, consisting of ceramic particles dispersed in an iron-nickel base alloy, significantly improved processing methods were developed. The characterization of cermets has continued through property determinations on samples prepared by various methods from a variety of simulated and actual high-level wastes. This report describes the status of development of the cermet waste form as it has evolved since 1977. 6 tables, 18 figures

  12. Optical and electrochromic properties of Sn:WO3 cermets

    International Nuclear Information System (INIS)

    Ashrit, P.V.; Bader, G.; Girouard, F.E.; Truong, V.V.

    1989-01-01

    This paper discusses optical and electrochromic properties of Sn:WO 3 cermets deposited by alternate layer thermal deposition. These cermets exhibit electrical and optical behavior in the as deposited state. The inclusion of Sn in the WO 3 matrix enhances the Electrical conductivity of the system and renders them fairly transparent in the visible region. The electrochromic behavior of such systems is studied under both proton and Li + ion injection. The good conductivity and good transmission combined with good electrochromic characteristics of these systems indicate the possibility of utilizing this type of cermet for the dual role of transparent conductor (TC) and electrochromic (EC) layer

  13. Studies on zirconia-mullite ceramic

    International Nuclear Information System (INIS)

    Virkar, Alka N.

    2014-01-01

    Zirconia Toughened Alumina (ZTA) ceramics with much improved Fracture Toughness and Strength have been used as a front material to fabricate composite Armour-Applications, Al 2 O 3 has very different fluxing ability with silica by sufficiently lowering the melting point. Addition of small amount of Fe 2 O 3 , TiO 2 , in an Al 2 O 3 -SiO 2 mixture enhances needle shaped Mullite crystal growth and also assist Liquid phase Sintering. In the present investigation, Zircon was used as a source of ZrO 2 and SiO 2 . Zircon (ZrSiO 4 ) has a low coefficient of Thermal Expansion and good Thermal Shock Resistance. Densification in terms of Relative Density and App. Porosity, Tetragonal ZrO 2 , phases, Thermal Expansion Coefficient, Hardness etc. were studied on Zirconia-Mullite system with and without additives. Z-M system with Y 2 O 3 additives show improved properties owing to the partial stabilization of Zirconia phase (PSZ). (author)

  14. Study of the effects of the interconnectivity of the metallic phase on the electrical and thermal behavior in alumina-ni and zirconia-ni interpenetrating phase composites (IPCs)

    International Nuclear Information System (INIS)

    Shahid, R.N.; Awais, H.B.; Mehmood, M.; Tariq, N.H.

    2007-01-01

    The addition of metallic inclusion in ceramic matrix can enhance the electrical and magnetic properties of the composite. Connectivity of conducting phase in an insulating matrix can be studied using electrical conductivity, thermal expansion, Hall Effect and by microscopic techniques. The wide range of application of such studies include, susceptor materials for induction heating, thin film resistors, gel formation permeability in porous structure and electromagnetic behavior of composites. The main phenomenon to be investigated is the insulating to conducting transition by the determination to of percolation range. This phenomenon depends on the concentration, shape, dimension and the crystallographic direction of the imbedded conducting particles. In this investigation variable concerning the percolation range of alumina- Ni and zirconia-Ni composites have been studied. The results provided the role of the size ratio of particles of matrix and the conducting phase, variation of resistance in terms of real part of impedance and thermal expansion on percolation effect. Scanning electron image have been used to study the percolation microscopically. (author)

  15. Fabrication and characterization of Cu/YSZ cermet high-temperature electrolysis cathode material prepared by high-energy ball-milling method

    International Nuclear Information System (INIS)

    Lee, Sungkyu; Kang, Kyoung-Hoon; Kim, Jong-Min; Hong, Hyun Seon; Yun, Yongseung; Woo, Sang-Kook

    2008-01-01

    Cu/YSZ composites (40 and 60 vol.% Cu powder with balance YSZ) was successfully fabricated by high-energy ball-milling of Cu and YSZ powders at 400 rpm for 24 h, pressing into pellets (O 13 mm x 2 mm) and subsequent sintering process at 900 deg. C under flowing 5%-H 2 /Ar gas for use as cermet cathode material of high-temperature electrolysis (HTE) of water vapor in a more economical way compared with conventional Ni/YSZ cermet cathode material. The Cu/YSZ composite powders thus synthesized and sintered were characterized using various analytical tools such as XRD, SEM, and laser diffraction and scattering method. Electrical conductivity of sintered Cu/YSZ cermet pellets thus fabricated was measured using 4-probe technique and compared with that of Ni/YSZ cermets. The effect of composites composition on the electrical conductivity was investigated and marked increase in electrical conductivity for copper contents greater than 40 vol.% in the composite was explained by percolation threshold

  16. Fabrication of cermet fuel for fast reactor

    International Nuclear Information System (INIS)

    Mishra, Sudhir; Kumar, Arun; Kutty, T.R.G.; Kamath, H.S.

    2011-01-01

    Mixed oxide (MOX) (U,Pu)O 2 , and metallic (U,Pu ,Zr) fuels are considered promising fuels for the fast reactor. The fuel cycle of MOX is well established. The advantages of the oxide fuel are its easy fabricability, good performance in the reactor and a well established reprocessing technology. However the problems lie in low thermal conductivity , low density of the fuel leading to low breeding ratio and consequently longer doubling time. The metallic fuel has the advantages of high thermal conductivity, higher metal density and higher coefficient of linear expansion. The higher coefficient of linear expansion is good from the safety consideration (negative reactivity factor). Because of higher metal density it offers highest breeding ratio and shortest doubling time. Metallic fuel disadvantages comprise large swelling at high burnup, fuel cladding interaction and lower margin between operating and melting temperature. The optimal solution may lie in cermet fuel (U, PuO 2 ), where PuO 2 is dispersed in U metal matrix and combines the favorable features of both the fuel types. The advantages of this fuel include high thermal conductivity, larger margin between melting and operating temperature, ability to retain fission product etc. The matrix being of high density metal the advantage of high breeding ratio is also maintained. In this report some results of fabrication of cermet pellet comprising of UO 2 /PuO 2 dispersed in U metal powder through classical powder metallurgy route and characterization are presented. (author)

  17. Zirconia based ceramics

    International Nuclear Information System (INIS)

    Bressiani, J.C.; Bressiani, A.H.A.

    1989-05-01

    Within the new generation of ceramic materials, zirconia continues to attract ever increasing attention of scients, technologists and users by virtue of its singular combination of properties and being able to perform thermo-mechanical, electroeletronic, chemico-biological functions. Nevertheless, in order to obtain these properties, a through understanding of the phase transformation mechanisms and microstructural changes is necessary. This paper discusses the main parameters that require control during fabrication of these materials to obtain desired properties for a specific application. (author) [pt

  18. Hydrothermal crystallization of zirconia and zirconia solid solutions

    International Nuclear Information System (INIS)

    Pyda, W.; Haberko, K.; Bucko, M.M.

    1991-01-01

    Zirconia as well as yttria-zirconia and calcia-zirconia solid-solution powders were crystallized under hydrothermal conditions from (co)precipitated hydroxides. The morphology of the power particles is strongly dependent on the crystallization conditions. The powders crystallized in a water solution of Na, K, and Li hydroxides show elongated particles of much larger sizes than those which result from the process carried out in pure water or a water solution of Na, K, or Li chlorides. The shapes of the latter particles are isometric. In this paper the growth mechanism of the elongated particles is suggested

  19. High-velocity-oxidation performance of metal-chromium-aluminum (MCrAl), cermet, and modified aluminide coatings on IN-100 and type VIA alloys at 1093 C

    Science.gov (United States)

    Deadmore, D. L.

    1974-01-01

    Cermet, MCrAl, and modified aluminide types of coatings applied to IN-100 and NASA-TRW-VIA alloy specimens were cyclically oxidation tested in a high velocity (Mach 1) gas flame at 1093 C. Several coating compositions of each type were evaluated for oxidation resistance. The modified aluminide coating, Pt-Al, applied to alloy 6A proved to be the best, providing oxidation protection to approximately 750 hours based on weight change measurements. The second best, a CoCrAlY coating applied to 6A, provided protection to 450 hours. The third best was a cermet + aluminide coating on 6A with a protection time to 385 hours.

  20. Corrosion resistant composite materials

    International Nuclear Information System (INIS)

    Ul'yanin, E.A.

    1986-01-01

    Foundations for corrosion-resistant composite materials design are considered with account of components compatibility. Fibrous and lamellar composites with metal matrix, dispersion-hardened steels and alloys, refractory metal carbides-, borides-, nitrides-, silicides-based composites are described. Cermet compositions and fields of their application, such as protective coatings for operation in agressive media at high temperatures, are presented

  1. Mechanical behaviour of U3O8-Al cermets

    International Nuclear Information System (INIS)

    Figueredo, A.M. de; Ferreira, I.

    1981-01-01

    Homogeneous, high density U 3 O 8 -Al cermets, containing between 5 W% and 55 Wt% of U 3 ω 8 were fabricated using hot swaging and powder metallurgy technics. Tensile tests were performed at room temperature on specimens obtained from the cermets fabricated. The results show that the ultimate tensile strength (UTS) and elongation to fracture decrease with increasing U 3 O 8 in the cermet. The UTS is shown to be proportional to the minimum matrix load bearing cross-sectional area. The main influence of an increase in the content of U 3 O 8 in the cermet appears to be the decrease in the minimum matrix, load bearing cross-section. (Author) [pt

  2. A cermet fuel reactor for nuclear thermal propulsion

    Science.gov (United States)

    Kruger, Gordon

    1991-01-01

    Work on the cermet fuel reactor done in the 1960's by General Electric (GE) and the Argonne National Laboratory (ANL) that had as its goal the development of systems that could be used for nuclear rocket propulsion as well as closed cycle propulsion system designs for ship propulsion, space nuclear propulsion, and other propulsion systems is reviewed. It is concluded that the work done in the 1960's has demonstrated that we can have excellent thermal and mechanical performance with cermet fuel. Thousands of hours of testing were performed on the cermet fuel at both GE and AGL, including very rapid transients and some radiation performance history. We conclude that there are no feasibility issues with cermet fuel. What is needed is reactivation of existing technology and qualification testing of a specific fuel form. We believe this can be done with a minimum development risk.

  3. A cermet fuel reactor for nuclear thermal propulsion

    International Nuclear Information System (INIS)

    Kruger, G.

    1991-01-01

    Work on the cermet fuel reactor done in the 1960's by General Electric (GE) and the Argonne National Laboratory (ANL) that had as its goal the development of systems that could be used for nuclear rocket propulsion as well as closed cycle propulsion system designs for ship propulsion, space nuclear propulsion, and other propulsion systems is reviewed. It is concluded that we can have excellent thermal and mechanical performance with cermet fuel. Thousands of hours of testing were performed on the cermet fuel at both GE and AGL, including very rapid transients and some radiation performance history. We conclude that there are no feasibility issues with cermet fuel. What is needed is reactivation of existing technology and qualification testing of a specific fuel form. We believe this can be done with a minimum development risk

  4. Cermet-fueled reactors for multimegawatt space power applications

    International Nuclear Information System (INIS)

    Cowan, C.L.; Armijo, J.S.; Kruger, G.B.; Palmer, R.S.; Van Hoomisson, J.E.

    1988-01-01

    The cermet-fueled reactor has evolved as a potential power source for a broad range of multimegawatt space applications. In particular, the fast spectrum reactor concept can be used to deliver 10s of megawatts of electric power for continuous, long term, unattended operation, and 100s of megawatts of electric power for times exceeding several hundred seconds. The system can also be utilized with either a gas coolant in a Brayton power conversion cycle, or a liquid metal coolant in a Rankine power conversion cycle. Extensive testing of the cermet fuel element has demonstrated that the fuel is capable of operating at very high temperatures under repeated thermal cycling conditions, including transient conditions which approach the multimegawatt burst power requirements. The cermet fuel test performance is reviewed and an advanced cermet-fueled multimegawatt nuclear reactor is described in this paper

  5. Treatment of root fracture with accompanying resorption using cermet cement.

    Science.gov (United States)

    Lui, J L

    1992-02-01

    A method of treating an apical root fracture with accompanying resorption at the junction of the fracture fragments using glass-cermet cement is described. Endodontically, the material had previously been used for repair of lateral resorptive root defects and retrograde root fillings. Complete bone regeneration was observed three years post-operatively following treatment of the root fracture in the conventional manner. The various advantages of glass-cermet cement as a root filling material used in the technique described are discussed.

  6. Corrosion stability of cermets on the base of titanium nitride

    International Nuclear Information System (INIS)

    Kajdash, O.N.; Marinich, M.A.; Kuzenkova, M.A.; Manzheleev, I.V.

    1991-01-01

    Corrosion resistance of titanium nitride and its cermets in 5% of HCl, 7% of HNO 3 , 10% of H 2 SO 4 is studied. It is established that alloys TiN-Ni-Mo alloyed with chromium (from 10 to 15%) possess the highest corrosion resistance. Cermet TiN-Cr has the higher stability than titanium nitride due to formation of binary nitride (Ti, Cr)N

  7. Electrical and thermal properties of niobium-base cermets

    International Nuclear Information System (INIS)

    Skidan, B.S.; Vlasov, A.S.; Alekseev, V.A.; Myl'nikova, T.S.; Ryzhkov, Yu.F.

    1979-01-01

    Behaviour of corundum-niobium cermets containing 16-70 vol.% metal was studied at low temperatures. It is found that the given materials are superconductors with Tsub(k) 6-7 K but their resistivity before their transfer into superconducting state is determined by the metal concentration and is found within 10 -2 -10 -4 Ohm. cm. The cermet heat conductivity is found to increase with the metal content

  8. Structure and friction properties of cermet and oxide explosion coatings

    International Nuclear Information System (INIS)

    RGrigorov, A.I.; Semenov, A.P.; Fed'ko, Yu.P.; Shtejn, L.M.

    1977-01-01

    Conditions have been specified for spraying explosion coatings of cermets over Kh18N10T stainless steel and an aluminum alloy. A mixture of WC and CO powders served as a material for spraying. The method of micro-X-ray spectrum analysis has been used to study the structure of the transition zone between the coating and the substrate and to establish the mechanism responsible for the formation of a cermet layer

  9. Development and application of high strength ternary boride base cermets

    International Nuclear Information System (INIS)

    Takagi, Ken-ichi

    2006-01-01

    Reaction boronizing sintering is a novel strategy to form a ternary boride coexisting with a metal matrix in a cermet during liquid phase sintering. This new sintering technique has successfully developed world first ternary boride base cermets with excellent mechanical properties such as Mo 2 FeB 2 , Mo 2 NiB 2 and WCoB base ones. In these cermets Mo 2 FeB 2 and Mo 2 NiB 2 base ones consist of a tetragonal M 3 B 2 (M: metal)-type complex boride as a hard phase and a transition metal base matrix. The cermets have already been applied to wear resistant applications such as injection molding machine parts, can making tools, and hot copper extruding dies, etc. This paper focuses on the characteristics, effects of the additional elements on the mechanical properties and structure, and practical applications of the ternary boride base cermets. - Graphical abstract: TRS and hardness of Ni-5B-51Mo-17.5Cr and Ni-5B-51Mo-12.5Cr-5V-xMn mass% cermets as functions of Mn content (Fig. 17)

  10. Wear resistance of TiB/sub 2/-Fe cermets

    International Nuclear Information System (INIS)

    Champagne, B.; Dallaire, S.

    1985-01-01

    A material which consists of TiB/sub 2/ dispersed in an iron matrix was synthesized by the exothermic reaction of ferrotitanium and boron. The as-reacted products were hot isostatically pressed to produce TiB/sub 2/-Fe cermets. The influence of HIP variables on the density and total fractional porosity of specimens is presented. Density above 95% is obtained by HIPping at temperatures below 1300 0 C. Increasing the temperature and the time of HIPping enhance the mechanical properties and wear resistance of TiB/sub 2/-Fe cermets by reducing their residual porosity. Relations obtained by regression analysis showed that the porosity strongly affects the properties of parts. Regression analysis point out that the wear loss of a 5% porosity TiB/sub 2/-Fe cermet is 270% higher than a dense HIPped cermet. Low stress and high stress abrasion resistance tests utilizing various abrasive media were carried out on dense HIPped cermets and results were compared with those obtained from WC-Co cermets and 1020 steel

  11. [Comparative investigation of compressive resistance of glass-cermet cements used as a core material in post-core systems].

    Science.gov (United States)

    Ersoy, E; Cetiner, S; Koçak, F

    1989-09-01

    In post-core applications, addition to the cast designs restorations that are performed on fabrication posts with restorative materials are being used. To improve the physical properties of glass-ionomer cements that are popular today, glass-cermet cements have been introduced and those materials have been proposed to be an alternative restorative material in post-core applications. In this study, the compressive resistance of Ketac-Silver as a core material was investigated comparatively with amalgam and composite resins.

  12. Theoretical studies of zirconia and defects in zirconia. Final report

    International Nuclear Information System (INIS)

    Jansen, H.J.F.

    1995-01-01

    Supported by this grant the author has performed total energy electronic structure calculations for cubic, tetragonal, and monoclinic zirconia. The results of these calculations agree with the observed ordering of structures in the phase diagram. He has developed model potentials based on the total energy results. Molecular dynamics calculations using these model potentials give a good description of the phase transitions in and the thermal properties of zirconia

  13. Microstructural evolution of nanograin nickel-zirconia cermet anode materials for solid oxide fuel cell applications

    International Nuclear Information System (INIS)

    Nayak, Bibhuti Bhusan

    2012-01-01

    The aim of the study is to study the structure, microstructure, porosity, thermal expansion, electrical conductivity and electrochemical behavior of the anode material thus synthesized in order to find its suitability for solid oxide fuel cell (SOFC) anode application

  14. Tetragonal zirconia quantum dots in silica matrix prepared by a modified sol-gel protocol

    Science.gov (United States)

    Verma, Surbhi; Rani, Saruchi; Kumar, Sushil

    2018-05-01

    Tetragonal zirconia quantum dots (t-ZrO2 QDs) in silica matrix with different compositions ( x)ZrO2-(100 - x)SiO2 were fabricated by a modified sol-gel protocol. Acetylacetone was added as a chelating agent to zirconium propoxide to avoid precipitation. The powders as well as thin films were given thermal treatment at 650, 875 and 1100 °C for 4 h. The silica matrix remained amorphous after thermal treatment and acted as an inert support for zirconia quantum dots. The tetragonal zirconia embedded in silica matrix transformed into monoclinic form due to thermal treatment ≥ 1100 °C. The stability of tetragonal phase of zirconia is found to enhance with increase in silica content. A homogenous dispersion of t-ZrO2 QDs in silica matrix was indicated by the mapping of Zr, Si and O elements obtained from scanning electron microscope with energy dispersive X-ray analyser. The transmission electron images confirmed the formation of tetragonal zirconia quantum dots embedded in silica. The optical band gap of zirconia QDs (3.65-5.58 eV) was found to increase with increase in zirconia content in silica. The red shift of PL emission has been exhibited with increase in zirconia content in silica.

  15. TiTaCN-Co cermets prepared by mechanochemical technique: microstructure and mechanical properties

    OpenAIRE

    Fides, Martin; Hvizdoš, P.; Balko, Ján; Chicardi, E.; Gotor, F.J.

    2016-01-01

    Microstructure and mechanical characterization of (Ti,Ta)(C,N)-Co based solid solution cermets prepared by two mechanochemical synthesis processes (one- and two-step milling) and a pressureless sintering in protective helium atmosphere. Materials with composition of TixTa1- xC0.5N0.5-20%Co with two different Ti/Ta ratios (x = 0.9 and x = 0.95) were developed to prepare four groups of experimental materials. Microstructures were observed using confocal microscopy and grain size was ev...

  16. Assessment of properties thermal sprayed coatings realised using cermet blend powder

    Directory of Open Access Journals (Sweden)

    J. Brezinová

    2014-10-01

    Full Text Available The article deals with the assessment of selected properties of plasma sprayed coatings based on ZrSiO4 doped with different volume fractions of metal dopant (Ni. Mixed powders are cermet blends. Aim of the work consists of verificating the possibility to replace the application of Ni interlayer by adding Ni directly to the ceramic powder and apply them together in a single technological operation. The coatings were studied from point of view of their structure, porosity, adhesion of the coatings in relation to the volume of dopant added and wear resistance. The best properties reached composite coating doped with 12 % Ni.

  17. Methods of three-dimensional electrophoretic deposition for ceramic and cermet applications and systems thereof

    Science.gov (United States)

    Rose, Klint Aaron; Kuntz, Joshua D.; Worsley, Marcus

    2016-09-27

    A ceramic, metal, or cermet according to one embodiment includes a first layer having a gradient in composition, microstructure and/or density in an x-y plane oriented parallel to a plane of deposition of the first layer. A ceramic according to another embodiment includes a plurality of layers comprising particles of a non-cubic material, wherein each layer is characterized by the particles of the non-cubic material being aligned in a common direction. Additional products and methods are also disclosed.

  18. Effects of core-to-dentin thickness ratio on the biaxial flexural strength, reliability, and fracture mode of bilayered materials of zirconia core (Y-TZP) and veneer indirect composite resins.

    Science.gov (United States)

    Su, Naichuan; Liao, Yunmao; Zhang, Hai; Yue, Li; Lu, Xiaowen; Shen, Jiefei; Wang, Hang

    2017-01-01

    Indirect composite resins (ICR) are promising alternatives as veneering materials for zirconia frameworks. The effects of core-to-dentin thickness ratio (C/Dtr) on the mechanical property of bilayered veneer ICR/yttria-tetragonal zirconia polycrystalline (Y-TZP) core disks have not been previously studied. The purpose of this in vitro study was to assess the effects of C/Dtr on the biaxial flexural strength, reliability, and fracture mode of bilayered veneer ICR/ Y-TZP core disks. A total of 180 bilayered 0.6-mm-thick composite resin disks in core material and C/Dtr of 2:1, 1:1, and 1:2 were tested with either core material placed up or placed down for piston-on-3-ball biaxial flexural strength. The mean biaxial flexural strength, Weibull modulus, and fracture mode were measured to evaluate the variation trend of the biaxial flexural strength, reliability, and fracture mode of the bilayered disks with various C/Dtr. One-way analysis of variance (ANOVA) and chi-square tests were used to evaluate the variation tendency of fracture mode with the C/Dtr or material placed down during testing (α=.05). Light microscopy was used to identify the fracture mode. The mean biaxial flexural strength and reliability improved with the increase in C/Dtr when specimens were tested with the core material either up and down, and depended on the materials that were placed down during testing. The rates of delamination, Hertzian cone cracks, subcritical radial cracks, and number of fracture fragments partially depended on the C/Dtr and the materials that were placed down during testing. The biaxial flexural strength, reliability, and fracture mode in bilayered structures of Y-TZP core and veneer ICR depend on both the C/Dtr and the material that was placed down during testing. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  19. Improved bonding strength of bioactive cermet Cold Gas Spray coatings.

    Science.gov (United States)

    Gardon, M; Concustell, A; Dosta, S; Cinca, N; Cano, I G; Guilemany, J M

    2014-12-01

    The fabrication of cermet biocompatible coatings by means Cold Gas Spray (CGS) provides prosthesis with outstanding mechanical properties and the required composition for enhancing the bioactivity of prosthetic materials. In this study, hydroxyapatite/Titanium coatings were deposited by means of CGS technology onto titanium alloy substrates with the aim of building-up well-bonded homogeneous coatings. Powders were blended in different percentages and sprayed; as long as the amount of hydroxyapatite in the feedstock increased, the quality of the coating was reduced. Besides, the relation between the particle size distribution of ceramic and metallic particles is of significant consideration. Plastic deformation of titanium particles at the impact eased the anchoring of hard hydroxyapatite particles present at the top surface of the coating, which assures the looked-for interaction with the cells. Coatings were immersed in Hank's solution for 1, 4 and 7 days; bonding strength value was above 60 MPa even after 7 days, which enhances common results of HAp coatings obtained by conventional thermal spray technologies. Copyright © 2014 Elsevier B.V. All rights reserved.

  20. Teknologi Pembuatan Cermet Du0¬2 - Steel Untuk Wadah Limbah Bahan Bakar Bekas Pwr

    OpenAIRE

    Alimah, Siti; Budiarto, Budiarto

    2005-01-01

    DUO­2-STEEL CERMET MANUFACTURING TECHNOLOGY FOR PWR Spent Nuclear Fuel (SNF) CASKS. Assessment of DU02 - Steel cermet manufacturing technology for PWR SNF casks has been done. DU02 - Steel cermet consisting of DU02 particulates and other particulates, embedded in a steel matrix. Cermet SNF casks have the potential for superior performance compared with casks constructed of other materials. The addition of DU02 ceramic particulates can increase SNF cask capacity, improve of repository performa...

  1. Cutting performance of TiCN–HSS cermet in dry machining

    OpenAIRE

    Canteli Fernández, José Antonio; Cantero Guisández, José Luis; Marín, N.C.; Gómez, B.; Gordo Odériz, Elena; Miguélez, Henar

    2010-01-01

    This work is focused on the cutting performance of a new cermet based on high-speed steel (HSS) matrix with hard phase TiCN. The processing route to manufacture the cermet M2+ 50 vol.% TiCN is described. Orthogonal cutting tests, carried out in a lathe showed the ability of the new cermet to achieve turning operations, showing reasonably wear resistance performing dry cutting operations. Tool life was significantly increased, when the cermet was compared with the reference materia...

  2. NiO-YSZ cermets supported low temperature solid oxide fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xinge; Robertson, Mark; Deces-Petit, Cyrille; Xie, Yongsong; Hui, Rob; Yick, Sing; Styles, Edward; Roller, Justin; Kesler, Olivera; Maric, Radenka; Ghosh, Dave [Institute for Fuel Cell Innovation, National Research Council Canada, 3250 East Mall, Vancouver, BC (Canada V6T 1W5)

    2006-10-20

    Solid oxide fuel cells with thin electrolyte of two types, Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9} (SDC) (15{mu}m) single-layer and 8mol% Yttria stabilized zirconia (YSZ) (5{mu}m)+SDC (15{mu}m) bi-layer on NiO-YSZ cermet substrates were fabricated by screen printing and co-firing. A Sm{sub 0.5}Sr{sub 0.5}CoO{sub 3} cathode was printed, and in situ sintered during a cell performance test. The SDC single-layer electrolyte cell showed high electrochemical performance at low temperature, with a 1180mWcm{sup -2} peak power density at 650{sup o}C. The YSZ+SDC bi-layer electrolyte cell generated 340mWcm{sup -2} peak power density at 650{sup o}C, and showed good performance at 700-800{sup o}C, with an open circuit voltage close to theoretical value. Many high Zr-content micro-islands were found on the SDC electrolyte surface prior to the cathode preparation. The influence of co-firing temperature and thin film preparation methods on the Zr-islands' appearance was investigated. (author)

  3. Re-activation of degraded nickel cermet anodes - Nano-particle formation via reverse current pulses

    Science.gov (United States)

    Hauch, A.; Marchese, M.; Lanzini, A.; Graves, C.

    2018-02-01

    The Ni/yttria-stabilized-zirconia (YSZ) cermet is the most commonly applied fuel electrode for solid oxide cells (SOCs). Loss of Ni/YSZ electrode activity is a key life-time limiting factor of the SOC. Developing means to mitigate this loss of performance or re-activate a fuel electrode is therefore important. In this work, we report a series of five tests on state-of-the-art Ni/YSZ-YSZ-CGObarrier-LSC/CGO cells. All cells were deliberately degraded via gas stream impurities in CO2/CO or harsh steam electrolysis operation. The cells were re-activated via a variety of reverse current treatments (RCTs). Via electrochemical impedance spectroscopy, we found that the Ni/YSZ electrode performance could be recovered via RCT, but not via constant fuel cell operation. For optimized RCT, we obtained a lower Ni/YSZ electrode resistance than the initial resistance. E.g. at 700 °C we measured fuel electrode resistance of 180 mΩ cm2, 390 mΩ cm2, and 159 mΩ cm2 before degradation, after degradation and after re-activation via RCT, respectively. Post-test SEM revealed that the RCT led to formation of nano-particles in the fuel electrode. Besides the remarkable improvement, the results also showed that RCTs can weaken Ni/YSZ interfaces and the electrode/electrolyte interface. This indicates that finding an optimum RCT profile is crucial for achieving maximum benefit.

  4. Microstructure and temperature coefficient of resistance of thin cermet resistor films deposited from CrSi2-Cr-SiC targets by S-gun magnetron

    International Nuclear Information System (INIS)

    Felmetsger, Valery V.

    2010-01-01

    Technological solutions for producing nanoscale cermet resistor films with sheet resistances above 1000 Ω/□ and low temperature coefficients of resistance (TCR) have been investigated. 2-40 nm thick cermet films were sputter deposited from CrSi 2 -Cr-SiC targets by a dual cathode dc S-gun magnetron. In addition to studying film resistance versus temperature, the nanofilm structural features and composition were analyzed using scanning electron microscopy, atomic force microscopy, high-resolution transmission electron microscopy, energy-dispersive x-ray spectroscopy, and electron energy loss spectroscopy. This study has revealed that all cermet resistor films deposited at ambient and elevated temperatures were amorphous. The atomic ratio of Si to Cr in these films was about 2 to 1. The film TCR displayed a significant increase when the deposited film thickness was reduced below 2.5 nm. An optimized sputter process consisting of wafer degassing, cermet film deposition at elevated temperature with rf substrate bias, and a double annealing in vacuum, consisting of in situ annealing following the film sputtering and an additional annealing following the exposure of the wafers to air, has been found to be very effective for the film thermal stabilization and for fine tuning the film TCR. Cermet films with thicknesses in the range of 2.5-4 nm deposited using this technique had sheet resistances ranging from 1800 to 1200 Ω/□ and TCR values from -50 ppm/ deg. C to near zero, respectively. A possible mechanism responsible for the high efficiency of annealing the cermet films in vacuum (after preliminary exposure to air), resulting in resistance stabilization and TCR reduction, is also discussed.

  5. Novel boride base cermets with very high strength

    International Nuclear Information System (INIS)

    Ken-ichi Takagi; Mari Yonetsu; Yuji Yamasaki

    2001-01-01

    Mo 2 NiB 2 boride base cermets consist of a Mo 2 NiB 2 type complex boride as a hard phase and a Ni base binder. The addition of Cr and V to the cermets changed the boride structure from orthorhombic to tetragonal and resulted in the improvement of mechanical properties and microstructural refinement. The tetragonal Mo 2 NiB 2 was formed through the orthorhombic Mo 2 NiB 2 by the solid state reaction during sintering and not formed directly from the raw material powders. Ni-4.5B-46.9Mo-12.5V-xMn (wt.%) model cermets with five levels of Mn content from 0 to 10 wt.% were prepared to investigate the effects of Mn on the mechanical properties and microstructure Of Mo 2 NiB 2 base cermets. The transverse rupture strength (TRS) of the cermets depended strongly on the microstructure, which varied significantly with Mn content. The maximum TRS obtained at 2.5 wt.%Mn were 3.5 Gpa with hardness of 87 R A . (author)

  6. Plasmachemical synthesis of nanopowders of yttria and zirconia from dispersed water-salt-organic mixtures

    Science.gov (United States)

    Novoselov, Ivan; Karengin, Alexander; Shamanin, Igor; Alyukov, Evgeny; Gusev, Alexander

    2018-03-01

    Article represents results on theoretical and experimental research of yttria and zirconia plasmachemical synthesis in air plasma from water-salt-organic mixtures "yttrium nitrate-water-acetone" and "zirconyl nitrate-water-acetone". On the basis of thermotechnical calculations the influence of organic component on lower heat value and adiabatic combustion temperature of water-salt-organic mixtures as well as compositions of mixtures providing their energy-efficient plasma treatment were determined. The calculations found the influence of mass fraction and temperature of air plasma supporting gas on the composition of plasma treatment products. It was determined the conditions providing yttria and zirconia plasmachemical synthesis in air plasma. During experiments it was b eing carried out the plasmachemical synthesis of yttria and zirconia powders in air plasma flow from water -salt-organic mixtures. Analysis of the results for obtained powders (scanning electron microscopy, X-ray diffraction analysis, BET analysis) confirm nanostructure of yttria and zirconia.

  7. Cermet sintering on the oase of molybdenum, nickel, aluminium oxide in dry and wet hydrogen medium

    International Nuclear Information System (INIS)

    Fedotov, A.V.; Lutskaya, E.Eh.

    1985-01-01

    Cermet sintering on the base of molybdenum, nickel and aluminium oxide in dry and wer hydrogen medium is studied. It is stated that presence of water vapours permits to decrease sintering temperature of molybdenum containing cermets and to prepare dense nickeliferous cermets. Cermet density can he rather high at final stages of sintering that is probably conditioned by decrease of growth rate of corundum crystals. Pressing pressure activates cermet siptering at intermediate stages and it is low effective at finite stages of condensation. Constancy of relative reduction of void volume is preserved only at final stages of sintering

  8. Boron-carbide-aluminum and boron-carbide-reactive metal cermets. [B/sub 4/C-Al

    Science.gov (United States)

    Halverson, D.C.; Pyzik, A.J.; Aksay, I.A.

    1985-05-06

    Hard, tough, lighweight boron-carbide-reactive metal composites, particularly boron-carbide-aluminum composites, are produced. These composites have compositions with a plurality of phases. A method is provided, including the steps of wetting and reacting the starting materials, by which the microstructures in the resulting composites can be controllably selected. Starting compositions, reaction temperatures, reaction times, and reaction atmospheres are parameters for controlling the process and resulting compositions. The ceramic phases are homogeneously distributed in the metal phases and adhesive forces at ceramic-metal interfaces are maximized. An initial consolidated step is used to achieve fully dense composites. Microstructures of boron-carbide-aluminum cermets have been produced with modules of rupture exceeding 110 ksi and fracture toughness exceeding 12 ksi..sqrt..in. These composites and methods can be used to form a variety of structural elements.

  9. The development of Zirconia and Copper toughened Alumina ceramic insert

    Science.gov (United States)

    Amalina Sabuan, Nur; Zolkafli, Nurfatini; Mebrahitom, A.; Azhari, Azmir; Mamat, Othman

    2018-04-01

    Ceramic cutting tools have been utilized in industry for over a century for its productivity and efficiency in machine tools and cutting tool material. However, due to the brittleness property the application has been limited. In order to manufacture high strength ceramic cutting tools, there is a need for suitable reinforcement to improve its toughness. In this case, copper (Cu) and zirconia (ZrO2) powders were added to investigate the hardness and physical properties of the developed composite insert. A uniaxial pre-forming process of the mix powder was done prior to densification by sintering at 1000 and 1300°C. The effect of the composition of the reinforcement on the hardness, density, shrinkage and microstructure of the inserts was investigated. It was found that an optimum density of 3.26 % and hardness 1385HV was obtained for composite of 10wt % zirconia and 10wt% copper at temperature 1000 °C.

  10. Martensitic transformation in zirconia

    International Nuclear Information System (INIS)

    Deville, Sylvain; Guenin, Gerard; Chevalier, Jerome

    2004-01-01

    We investigate by atomic force microscopy (AFM) the surface relief resulting from martensitic tetragonal to monoclinic phase transformation induced by low temperature autoclave aging in ceria-stabilized zirconia. AFM appears as a very powerful tool to investigate martensite relief quantitatively and with a great precision. The crystallographic phenomenological theory is used to predict the expected relief induced by the transformation, for the particular case of lattice correspondence ABC1, where tetragonal c axis becomes the monoclinic c axis. A model for variants spatial arrangement for this lattice correspondence is proposed and validated by the experimental observations. An excellent agreement is found between the quantitative calculations outputs and the experimental measurements at nanometer scale yielded by AFM. All the observed features are explained fully quantitatively by the calculations, with discrepancies between calculations and quantitative experimental measurements within the measurements and calculations precision range. In particular, the crystallographic orientation of the transformed grains is determined from the local characteristics of transformation induced relief. It is finally demonstrated that the strain energy is the controlling factor of the surface transformation induced by low temperature autoclave treatments in this material

  11. Molybdenum-UO2 cermet irradiation at 1145 K.

    Science.gov (United States)

    Mcdonald, G.

    1971-01-01

    Two molybdenum-uranium dioxide cermet fuel pins with molybdenum clad were fission-heated in a forced-convection helium coolant for sufficient time to achieve 5.3% burnup. The cermet core contained 20 wt % of 93.2% enriched uranium dioxide. The results were as follows: there was no visible change in the appearance of the molybdenum clad during irradiation; the maximum increase in diameter of the fuel pins was 0.8%; there was no migration of uranium dioxide along grain boundaries and no evident interaction between molybdenum and uranium dioxide; and, finally, approximately 12% of the fission gas formed was released from the cermet core into the gas plenum.

  12. Zirconia implants and peek restorations for the replacement of upper molars

    Directory of Open Access Journals (Sweden)

    José María Parmigiani-Izquierdo

    2017-02-01

    Full Text Available Abstract Background One of the disadvantages of the zirconia implants is the lack of elasticity, which is increased with the use of ceramic or zirconia crowns. The consequences that could result from this lack of elasticity have led to the search for new materials with improved mechanical properties. Case presentation A patient who is a 45-year-old woman, non-smoker and has no medical record of interest with a longitudinal fracture in the palatal root of molar tooth 1.7 and absence of tooth 1.6 was selected in order to receive a zirconia implant with a PEEK-based restoration and a composite coating. The following case report describes and analyses treatment with zirconia implants in molars following a flapless surgical technique. Zirconia implants are an alternative to titanium implants in patients with allergies or who are sensitive to metal alloys. However, one of the disadvantages that they have is their lack of elasticity, which increases with the use of ceramic or zirconia crowns. The consequences that can arise from this lack of elasticity have led to the search for new materials with better mechanical properties to cushion occlusal loads. PEEK-based restoration in implant prosthetics can compensate these occlusal forces, facilitating cushioning while chewing. Conclusion This procedure provides excellent elasticity and resembles natural tooth structure. This clinical case suggests that PEEK restorations can be used in zirconia implants in dentistry.

  13. Mixed zirconia calcium phosphate coatings for dental implants: Tailoring coating stability and bioactivity potential

    International Nuclear Information System (INIS)

    Pardun, Karoline; Treccani, Laura; Volkmann, Eike; Streckbein, Philipp; Heiss, Christian; Destri, Giovanni Li; Marletta, Giovanni; Rezwan, Kurosch

    2015-01-01

    Enhanced coating stability and adhesion are essential for long-term success of orthopedic and dental implants. In this study, the effect of coating composition on mechanical, physico-chemical and biological properties of coated zirconia specimens is investigated. Zirconia discs and dental screw implants are coated using the wet powder spraying (WPS) technique. The coatings are obtained by mixing yttria-stabilized zirconia (TZ) and hydroxyapatite (HA) in various ratios while a pure HA coating served as reference material. Scanning electron microscopy (SEM) and optical profilometer analysis confirm a similar coating morphology and roughness for all studied coatings, whereas the coating stability can be tailored with composition and is probed by insertion and dissections experiments in bovine bone with coated zirconia screw implants. An increasing content of calcium phosphate (CP) resulted in a decrease of mechanical and chemical stability, while the bioactivity increased in simulated body fluid (SBF). In vitro experiments with human osteoblast cells (HOB) revealed that the cells grew well on all samples but are affected by dissolution behavior of the studied coatings. This work demonstrates the overall good mechanical strength, the excellent interfacial bonding and the bioactivity potential of coatings with higher TZ contents, which provide a highly interesting coating for dental implants. - Highlights: • Different ratios of zirconia (TZ) and calcium phosphate (CP) were deposited on zirconia substrates. • Enhancement of TZ content in mixed coatings increased coating stability. • Enhancement of CP content in mixed coatings increased bioactivity. • All tested coating compositions were non-toxic

  14. Mixed zirconia calcium phosphate coatings for dental implants: Tailoring coating stability and bioactivity potential

    Energy Technology Data Exchange (ETDEWEB)

    Pardun, Karoline [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Treccani, Laura, E-mail: treccani@uni-bremen.de [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Volkmann, Eike [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Streckbein, Philipp [University Hospital, Justus-Liebig-University Giessen, Department of Cranio-Maxillo-Facial Surgery, Klinikstrasse 33, 35385 Giessen (Germany); Heiss, Christian [University Hospital of Giessen-Marburg, Department of Trauma Surgery, Rudolf-Buchheim-Strasse 7, 35385 Giessen, Germany, (Germany); Laboratory of Experimental Surgery, Kerkraderstrasse 9, 35392 Giessen (Germany); Destri, Giovanni Li; Marletta, Giovanni [Laboratory for Molecular Surfaces and Nanotechnology (LAMSUN), Department of Chemistry, University of Catania and CSGI, Viale A. Doria 6, 95125 Catania (Italy); Rezwan, Kurosch [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany)

    2015-03-01

    Enhanced coating stability and adhesion are essential for long-term success of orthopedic and dental implants. In this study, the effect of coating composition on mechanical, physico-chemical and biological properties of coated zirconia specimens is investigated. Zirconia discs and dental screw implants are coated using the wet powder spraying (WPS) technique. The coatings are obtained by mixing yttria-stabilized zirconia (TZ) and hydroxyapatite (HA) in various ratios while a pure HA coating served as reference material. Scanning electron microscopy (SEM) and optical profilometer analysis confirm a similar coating morphology and roughness for all studied coatings, whereas the coating stability can be tailored with composition and is probed by insertion and dissections experiments in bovine bone with coated zirconia screw implants. An increasing content of calcium phosphate (CP) resulted in a decrease of mechanical and chemical stability, while the bioactivity increased in simulated body fluid (SBF). In vitro experiments with human osteoblast cells (HOB) revealed that the cells grew well on all samples but are affected by dissolution behavior of the studied coatings. This work demonstrates the overall good mechanical strength, the excellent interfacial bonding and the bioactivity potential of coatings with higher TZ contents, which provide a highly interesting coating for dental implants. - Highlights: • Different ratios of zirconia (TZ) and calcium phosphate (CP) were deposited on zirconia substrates. • Enhancement of TZ content in mixed coatings increased coating stability. • Enhancement of CP content in mixed coatings increased bioactivity. • All tested coating compositions were non-toxic.

  15. Class II glass ionomer/silver cermet restorations and their effect on interproximal growth of mutans streptococci.

    Science.gov (United States)

    Berg, J H; Farrell, J E; Brown, L R

    1990-02-01

    The release of fluoride from glass ionomer materials is one of the most important features of this newly implemented material, and the remineralization effects of this phenomenon have been documented (Hicks and Silverstone 1986). This paper examines the effects of glass ionomer/silver cermet restorations on the plaque levels of interproximal mutans streptococci. Fifteen patients with Class II lesions in primary molars were selected for study. Interproximal plaque samples were obtained from each of the lesion sites and from one caries-free site approximal to a primary molar. One lesion was restored with composite resin to serve as a treated control to the glass ionomer/silver cermet (Ketac Silver, ESPE/Premier Sales Corp., Norristown, Pennsylvania) test site. A sound (unaltered) interproximal site served as the untreated control site. Plaque samples were collected before and at one week, one month, and three months post-treatment. Samples were serially diluted to enable colony counts of mutans streptococci. One week post-treatment counts showed that the glass ionomer/silver cermet restorations significantly reduced (P less than 0.05) the approximal plaque levels of mutans streptococci. Conversely, the untreated and treated control sites did not exhibit reductions in approximal plaque levels of mutans streptococci. These results indicate that glass ionomer restorations may be inhibitory to the growth of mutans streptococci in dental plaque approximal to this restorative material in the primary dentition.

  16. Effect of carbon content on the microstructure and mechanical properties of superfine Ti(C, N)-based cermets

    International Nuclear Information System (INIS)

    Liu Ning; Liu Xuesong; Zhang Xiaobo; Zhu Longwei

    2008-01-01

    As a new kind of tool materials which appeared in the seventies last century, the Ti (C, N)-based cermets have been widely used in recent years due to many of its good properties. The microstructure of Ti(C, N)-based cermets with various carbon content were studied using scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). Vickers hardness and transverse rupture strength (TRS) were also measured. An increased carbon content resulted in the finer grain size, decreased solution strength of tungsten and molybdenum in the binder phase, and a higher volume fraction of heavy (Ti, Mo, W)(C,N) cores. If the addition of carbon content is too little or too much, the phase composition of material will deviate from the normal dual phase section and lead to the formation of the third phase: η-phase if the carbon content is too low or dissociative carbon if the carbon content is too high. And the formation of the third phase will remarkably deteriorate the mechanical properties of cermets

  17. Glass ceramic toughened with tetragonal zirconia

    Science.gov (United States)

    Keefer, Keith D.; Michalske, Terry A.

    1986-01-01

    A phase transformation-toughened glass ceramic and a process for making it are disclosed. A mixture of particulate network-forming oxide, network-modifying oxide, and zirconium oxide is heated to yield a homogeneous melt, and this melt is then heat-treated to precipitate an appreciable quantity of tetragonal zirconia, which is retained at ambient temperature to form a phase transformation-toughened glass ceramic. Nucleating agents and stabilizing agents may be added to the mixture to facilitate processing and improve the ceramic's properties. Preferably, the mixture is first melted at a temperature from 1200.degree. to 1700.degree. C. and is then heat-treated at a temperature within the range of 800.degree. to 1200.degree. C. in order to precipitate tetragonal ZrO.sub.2. The composition, as well as the length and temperature of the heat-treatment, must be carefully controlled to prevent solution of the precipitated tetragonal zirconia and subsequent conversion to the monoclinic phase.

  18. Preparation of refractory cermet structures for lithium compatibility testing

    Science.gov (United States)

    Heestand, R. L.; Jones, R. A.; Wright, T. R.; Kizer, D. E.

    1973-01-01

    High-purity nitride and carbide cermets were synthesized for compatability testing in liquid lithium. A process was developed for the preparation of high-purity hafnium nitride powder, which was subsequently blended with tungsten powder or tantalum nitride and tungsten powders and fabricated into 3 in diameter billets by uniaxial hot pressing. Specimens were then cut from the billets for compatability testing. Similar processing techniques were applied to produce hafnium carbide and zirconium carbide cermets for use in the testing program. All billets produced were characterized with respect to chemistry, structure, density, and strength properties.

  19. Cermet high level waste forms: a pregress report

    International Nuclear Information System (INIS)

    Aaron, W.S.; Quinby, T.C.; Kobisk, E.H.

    1978-06-01

    The fixation of high level radioactive waste from both commercial and DOE defense sources as cermets is currently under study. This waste form consists of a continuous iron-nickel base metal matrix containing small particles of fission product oxides. Preliminary evaluations of cermets fabricated from a variety of simulated wastes indicate they possess properties providing advantages over other waste forms presently being considered, namely thermal conductivity, waste loading levels, and leach resistance. This report describes the progress of this effort, to date, since its initiation in 1977

  20. Improved corrosion resistant and mechanical behavior of distinct composite coatings (silica/titania/zirconia on Ti–6Al–4V deposited by EPD

    Directory of Open Access Journals (Sweden)

    M. Chellappa

    2017-09-01

    Full Text Available Synthesized composite powders (ZrO2/TiO2, SiO2/TiO2, and SiO2/ZrO2 were successfully deposited on Ti–6Al–4V by electrophoretic deposition method (EPD to improve its electrochemical characteristics for better biomedical applications. In the present investigation, the three composite powders were prepared by sol–gel synthesis and its phase purity was analyzed by Powder X-ray diffraction (XRD method. Further, the performance of the deposited coatings was assessed by scanning electron microscopy (SEM coupled with energy dispersive X-ray analysis (EDAX, scratch resistance test. The electrochemical properties of the composite coatings were analyzed by Potentiodynamic (Tafel polarization and electrochemical impedance spectroscopy (EIS studies. From the results, we observed that the corrosion resistance behavior of the different composite coated metallic substrate exhibited divergent corrosion resistance nature than blank Ti–6Al–4V. Of all these coatings on Ti–6Al–4V, the composite made up of, ZrO2/TiO2 has pronounced corrosion resistance behavior in Ringer’s solution when compared to others. This behavior is due to the presence of strong adherent coating owing to the existence of uniform deposition on Ti–6Al–4V.

  1. Effect of coping thickness and background type on the masking ability of a zirconia ceramic.

    Science.gov (United States)

    Tabatabaian, Farhad; Taghizade, Fateme; Namdari, Mahshid

    2018-01-01

    The masking ability of zirconia ceramics as copings is unclear. The purpose of this in vitro study was to evaluate the effect of coping thickness and background type on the masking ability of a zirconia ceramic and to determine zirconia coping thickness cut offs for masking the backgrounds investigated. Thirty zirconia disks in 3 thickness groups of 0.4, 0.6, and 0.8 mm were placed on 9 backgrounds to measure CIELab color attributes using a spectrophotometer. The backgrounds included A1, A2, and A3.5 shade composite resin, A3 shade zirconia, nickel-chromium alloy, nonprecious gold-colored alloy, amalgam, black, and white. ΔE values were measured to determine color differences between the specimens on the A2 shade composite resin background and the same specimens on the other backgrounds. The color change (ΔE) values were compared with threshold values for acceptability (ΔE=5.5) and perceptibility (ΔE=2.6). Repeated measures ANOVA, the Bonferroni test, and 1-sample t tests were used to analyze data (α=.05). Mean ΔE values ranged between 1.44 and 7.88. The zirconia coping thickness, the background type, and their interaction affected the CIELab and ΔE values (Pmasking, the minimum thickness of a zirconia coping should be 0.4 mm for A1 and A3.5 shade composite resin, A3 shade zirconia, and nonprecious gold-colored alloy, 0.6 mm for amalgam, and 0.8 mm for nickel-chromium alloy. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  2. Model-supported interpretation of the electrochemical characteristics of solid oxide fuel cells with Ni/YSZ cermet anodes; Modellgestuetzte Interpretation der elektrochemischen Charakteristik von Festoxid-Brennstoffzellen mit Ni/YSZ-Cermetanoden

    Energy Technology Data Exchange (ETDEWEB)

    Gewies, Stefan

    2009-01-29

    This work presents the development, validation and application of a multiscale model for the detailed description of a solid oxide fuel cell (SOFC) with a Ni/YSZ (nickel/yttria-stabilized zirconia) cermet anode. The aim of the study is the identification of the physico-chemical loss processes, as seen in impedance spectra and polarization curves. The model consists of an elementary kinetic description of the electrochemistry including the development of an electrical double layer at the electrode/electrolyte interface of the cermet anode, a homogenized description of charge and gas-phase transport in the electrodes as well as a macroscopic description of convective and diffusive mass transport in the gas phase above the electrodes. For the rst time this study allows for a complete description of the impedance spectra of a diffusively fuel-supplied cermet anode. By comparing simulations with experiments on symmetrical cells (University of Karlsruhe) three dominant loss processes could be identified. The model was extended to account for the description of segmented SOFCs. In correspondence with experimental data (German Aerospace Center) the simulations show strong gradients in current densities and gas concentrations. (orig.)

  3. Induction Heating Model of Cermet Fuel Element Environmental Test (CFEET)

    Science.gov (United States)

    Gomez, Carlos F.; Bradley, D. E.; Cavender, D. P.; Mireles, O. R.; Hickman, R. R.; Trent, D.; Stewart, E.

    2013-01-01

    Deep space missions with large payloads require high specific impulse and relatively high thrust to achieve mission goals in reasonable time frames. Nuclear Thermal Rockets (NTR) are capable of producing a high specific impulse by employing heat produced by a fission reactor to heat and therefore accelerate hydrogen through a rocket nozzle providing thrust. Fuel element temperatures are very high (up to 3000 K) and hydrogen is highly reactive with most materials at high temperatures. Data covering the effects of high-temperature hydrogen exposure on fuel elements are limited. The primary concern is the mechanical failure of fuel elements due to large thermal gradients; therefore, high-melting-point ceramics-metallic matrix composites (cermets) are one of the fuels under consideration as part of the Nuclear Cryogenic Propulsion Stage (NCPS) Advance Exploration System (AES) technology project at the Marshall Space Flight Center. The purpose of testing and analytical modeling is to determine their ability to survive and maintain thermal performance in a prototypical NTR reactor environment of exposure to hydrogen at very high temperatures and obtain data to assess the properties of the non-nuclear support materials. The fission process and the resulting heating performance are well known and do not require that active fissile material to be integrated in this testing. A small-scale test bed; Compact Fuel Element Environmental Tester (CFEET), designed to heat fuel element samples via induction heating and expose samples to hydrogen is being developed at MSFC to assist in optimal material and manufacturing process selection without utilizing fissile material. This paper details the analytical approach to help design and optimize the test bed using COMSOL Multiphysics for predicting thermal gradients induced by electromagnetic heating (Induction heating) and Thermal Desktop for radiation calculations.

  4. Cold spraying of aluminum bronze on profiled submillimeter cermet structures formed by laser cladding

    Science.gov (United States)

    Ryashin, N. S.; Malikov, A. G.; Shikalov, V. S.; Gulyaev, I. P.; Kuchumov, B. M.; Klinkov, S. V.; Kosarev, V. F.; Orishich, A. M.

    2017-10-01

    The paper presents results of the cold spraying of aluminum bronze coatings on substrates profiled with WC/Ni tracks obtained by laser cladding. Reinforcing cermet frames shaped as grids with varied mesh sizes were clad on stainless steel substrates using a CO2 laser machine "Siberia" (ITAM SB RAS, Russia). As a result, surfaces/substrates with heterogeneous shape, composition, and mechanical properties were obtained. Aluminum bronze coatings were deposited from 5lF-NS powder (Oerlikon Metco, Switzerland) on those substrates using cold spraying equipment (ITAM SB RAS). Data of profiling, microstructure diagnostics, EDS analysis, and mechanical tests of obtained composites is reported. Surface relief of the sprayed coatings dependence on substrate structure has been demonstrated.

  5. Microstructural stability of spark-plasma-sintered Wf/W composite with zirconia interface coating under high-heat-flux hydrogen beam irradiation

    OpenAIRE

    M. Avello de Lama; M. Balden; H. Greuner; T. Höschen; J. Matejicek; J.H. You

    2017-01-01

    Tungsten is considered as the most suitable material for the plasma-facing armour of future fusion reactors. However, in spite of many advantageous properties, pure tungsten has a major drawback, namely, brittleness at lower temperatures and embrittlement by neutron irradiation. Tungsten fibre-reinforced tungsten (Wf/W) composites are thought to be a promising candidate material for armour owing to the pseudo-toughness effect which is based on controlled cracking of coated interfaces. In this...

  6. Long term stability of yttria-stabilized zirconia waste forms. Stability for secular change of partitioned TRU waste composition by disintegration

    International Nuclear Information System (INIS)

    Kuramoto, Ken-ichi; Banba, Tsunetaka; Mitamura, Hisayoshi; Sakai, Etsuro; Uno, Masayoshi; Kinoshita, H.; Yamanaka, Shinsuke

    1999-01-01

    In this study, the stability of YSZ waste forms for secular change of partitioned TRU waste composition by disintegration, one of important terms in long-term stability, is the special concern. Designed amount of waste and YSZ powder were mixed and sintered. These TRU waste forms were submitted to tests of phase stability, chemical durability, mechanical property and compactness. The results were compared with those of another YSZ waste forms, non-radioactive Ce and/or Nd doped YSZ samples, and glass and Synroc waste forms. Experimental results show following: (1) Phase stability of (Np+Am)-, (Np+U)-, and (Np+U+Bi)-doped YSZ waste forms could be maintained of that of the initial Np+Am-doped YSZ waste form permanently even when the composition of partitioned TRU waste were changed by disintegration. (2) Secular change also accelerated volume increase of YSZ waste forms as well as alpha-decay damage. (3) Hv, E and K IC of (Np+U)- and (Np+U+Bi)-doped YSZ waste forms were independent of the secular change of the partitioned TRU waste composition by disintegration. (4) Mechanical properties of YSZ waste forms were more than those of a glass and Synroc waste forms. (5) Compactness of YSZ waste forms was good as waste forms for the partitioned TRU wastes. (J.P.N.)

  7. Zirconia toughened mica glass ceramics for dental restorations.

    Science.gov (United States)

    Gali, Sivaranjani; K, Ravikumar; Murthy, B V S; Basu, Bikramjit

    2018-03-01

    The objective of the present study is to understand the role of yttria stabilized zirconia (YSZ) in achieving the desired spectrum of clinically relevant mechanical properties (hardness, elastic modulus, fracture toughness and brittleness index) and chemical solubility of mica glass ceramics. The glass-zirconia mixtures with varying amounts of YSZ (0, 5, 10, 15 and 20wt.%) were ball milled, compacted and sintered to obtain pellets of glass ceramic-YSZ composites. Phase analysis was carried out using X-ray diffraction and microstructural characterization with SEM revealed the crystal morphology of the composites. Mechanical properties such as Vickers hardness, elastic modulus, indentation fracture toughness and chemical solubility were assessed. Phase analysis of sintered pellets of glass ceramic-YSZ composites revealed the characteristic peaks of fluorophlogopite (FPP) and tetragonal zirconia. Microstructural investigation showed plate and lath-like interlocking mica crystals with embedded zirconia. Vickers hardness of 9.2GPa, elastic modulus of 125GPa, indentation toughness of 3.6MPa·m 1/2 , and chemical solubility of 30μg/cm 2 (well below the permissible limit) were recorded with mica glass ceramics containing 20wt.% YSZ. An increase in hardness and toughness of the glass ceramic-YSZ composites with no compromise on their brittleness index and chemical solubility has been observed. Such spectrum of properties can be utilised for developing a machinable ceramic for low stress bearing inlays, onlays and veneers. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  8. Improvement of the steel quality through zirconia base ceramic filter

    International Nuclear Information System (INIS)

    Santos, Benedito M.; Foschini, Cesar R.; Santos, Ieda M.G.; Pinheiro, Adriano S.; Paskocimas, Carlos A.; Leite, Edson R.; Longo, Elson

    1997-01-01

    At the end of production, the steel presents inclusions own to the making process. Ceramics filters, with controlled porosity, are being produced to eliminate the impurities, so as to increase the good quality steel production. This work studies the optimization of the zirconia filters composition and production for siderurgical processes application. The study was done through the granulometric control, using BET, XRD and Hg Porosimetry. (author)

  9. Sm{sub 0.5}Sr{sub 0.5}CoO{sub 3}+Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9} composite cathode for cermet supported thin Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9} electrolyte SOFC operating below 600{sup o}C

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xinge; Robertson, Mark; Yick, Sing; Deces-Petit, Cyrille; Styles, Edward; Qu, Wei; Xie, Yongsong; Hui, Rob; Roller, Justin; Kesler, Olivera; Maric, Radenka; Ghosh, Dave [Institute for Fuel Cell Innovation, National Research Council Canada, 3250 East Mall, Vancouver, BC (Canada V6T 1W5)

    2006-10-06

    The cathode is a key component in low temperature solid oxide fuel cells. In this study, composite cathode, 75wt.% Sm{sub 0.5}Sr{sub 0.5}CoO{sub 3} (SSC)+25wt.% Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9} (SDC), was applied on the cermet supported thin SDC electrolyte cell which was fabricated by tape casting, screen-printing, and co-firing. Single cells with the composite cathodes sintered at different temperatures were tested from 400 to 650{sup o}C. The best cell performance, 0.75Wcm{sup -2} peak power operating at 600{sup o}C, was obtained from the 1050{sup o}C sintered cathode. The measured thin SDC electrolyte resistance R{sub s} was 0.128{omega}cm{sup 2} and total electrode polarization R{sub p}(a+c) was only 0.102{omega}cm{sup 2} at 600{sup o}C. (author)

  10. Structure And Properties Of PVD Coatings Deposited On Cermets

    Directory of Open Access Journals (Sweden)

    Żukowska L.

    2015-06-01

    Full Text Available The main aim of the research is the investigation of the structure and properties of single-layer and gradient coatings of the type (Ti,AlN and Ti(C,N deposited by physical vapour deposition technology (PVD on the cermets substrate.

  11. The compaction and sintering of UO_2-Zr cermet pellets

    International Nuclear Information System (INIS)

    Tri Yulianto; Meniek Rachmawati; Etty Mutiara

    2013-01-01

    An innovative fuel pellet of UO_2-Zr cermet has been developed to improve thermal conductivity of UO_2 pellet by adding small amount Zr metal in to UO_2 matrix below 10 % weight. Zirconium powder will serve for the creation of bridges or web structure during compaction and will effectively reduce contact between of UO_2 particles. Based on the theory of phase equilibrium of metals-metal oxides-ceramic, this fabrication technique may produce UO_2 pellets containing continuous metal channel on the grain boundary of UO_2 through sintering in a reduction atmosphere. The fabrication was done by varying process parameters of mixing and compaction. Characterisation of UO_2-Zr cermet pellet involved visual test, dimensional and density measurement, and ceramography test. This advanced cermet fabrication technology may address common issue with cermet fuels such as microstructure with continuous metal channel structure in the UO_2 matrix, which is more effectively than the commonly accepted microstructure involving fraction of UO_2 pellet by standard fabrication route. (author)

  12. Aspects of fretting wear of sprayed cermet coatings

    International Nuclear Information System (INIS)

    Chivers, T.C.

    1985-01-01

    Two experimental fretting programmes which investigated aspects of fretting wear of sprayed cermet coatings are reviewed. These programmes were conducted in support of components used in the advanced gas-cooled reactor. It is speculated that the results from these programmes are compatible with a simple two-stage wear model. This model assumes that an initial wear process occurs which is dominated by an interlocking and removal of asperities. Such a phase will be dependent on the superficial contact areas and possibly the interfacial load, but the latter aspect is not considered. This initial wear is of very short duration and is followed by a mild, oxidative, wear mode. Coatings data are also compared with those for structural steels. In short-term low temperature tests it appears that structural steels have comparable performance with the cermet coatings but it is argued that this is an artefact of the wear process. However, at high temperatures (600 0 C) wear of stainless steel could not be determined, the specimens showing a net weight gain. It is concluded that for in-reactor fretting applications cermet coatings will have advantages over structural steels at low temperatures. Even in high temperature regions some operation at low temperatures is experienced and consequently cermet coatings may be useful here also. (orig.)

  13. CERMET fuel behavior and properties in ADS reactors

    International Nuclear Information System (INIS)

    Haas, D.; Fernandez, A.; Staicu, D.; Somers, J.; Maschek, W.; Liu, P.; Chen, X.

    2008-01-01

    Within the EUROTRANS Integrated Project, Forschungszentrum Karlsruhe (FZK) and the Institute for Transuranium Elements (ITU) are joining their efforts to study the behavior of Mo-based CERMET non-uranium fuel for the ADS. Contributions include core safety calculations, and fuel property measurements and irradiation experiments. Safety studies for optimized EFIT core designs have concluded that, for the new low power cores of EFIT with a power class of ∼400 MWth and a fuel power density of ∼250 MW/m 3 , the CERMET-loaded cores behave favorably and the design limits of the fuels were not violated. Mo-based CERMET fuel pellets and pins loaded with Pu and Am were fabricated for irradiation programmes which will start by mid-2007 in PHENIX (France) and HFR-Petten (The Netherlands). The thermal diffusivity and specific heat of the CERMET fuels (loaded with Pu and Am) were the main properties measured, and the thermal conductivity was deduced. The results were used to prepare the safety report for the irradiation experiments

  14. Thermal Cycling of Uranium Dioxide - Tungsten Cermet Fuel Specimens

    Energy Technology Data Exchange (ETDEWEB)

    Gripshover, P.J.; Peterson, J.H.

    1969-12-08

    In phase I tungsten clad cermet fuel specimens were thermal cycled, to study the effects of fuel loading, fuel particle size, stablized fuel, duplex coatings, and fabrication techniques on dimensional stability during thermal cycling. In phase II the best combination of the factors studies in phase I were combined in one specimen for evaluation.

  15. Effects of surface treatment on bond strength between dental resin agent and zirconia ceramic

    Energy Technology Data Exchange (ETDEWEB)

    Moradabadi, Ashkan [Department of Electrochemistry, Universität Ulm, Ulm (Germany); Roudsari, Sareh Esmaeily Sabet [Department of Optoelectonics, Universität Ulm, Ulm (Germany); Yekta, Bijan Eftekhari [School of Materials Engineering, Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Rahbar, Nima, E-mail: nrahbar@wpi.edu [Department of Civil and Environmental Engineering, Worcester Polytechnic Institute, Worcester, MA 01609 (United States)

    2014-01-01

    This paper presents the results of an experimental study to understand the dominant mechanism in bond strength between dental resin agent and zirconia ceramic by investigating the effects of different surface treatments. Effects of two major mechanisms of chemical and micromechanical adhesion were evaluated on bond strength of zirconia to luting agent. Specimens of yttrium-oxide-partially-stabilized zirconia blocks were fabricated. Seven groups of specimens with different surface treatment were prepared. 1) zirconia specimens after airborne particle abrasion (SZ), 2) zirconia specimens after etching (ZH), 3) zirconia specimens after airborne particle abrasion and simultaneous etching (HSZ), 4) zirconia specimens coated with a layer of a Fluorapatite-Leucite glaze (GZ), 5) GZ specimens with additional acid etching (HGZ), 6) zirconia specimens coated with a layer of salt glaze (SGZ) and 7) SGZ specimens after etching with 2% HCl (HSGZ). Composite cylinders were bonded to airborne-particle-abraded surfaces of ZirkonZahn specimens with Panavia F2 resin luting agent. Failure modes were examined under 30 × magnification and the effect of surface treatments was analyzed by scanning electron microscopy (SEM) and atomic force microscopy (AFM). SZ and HSZ groups had the highest and GZ and SGZ groups had the lowest mean shear bond strengths among all groups. Mean shear bond strengths were significantly decreased by applying a glaze layer on zirconia surfaces in GZ and SGZ groups. However, bond strengths were improved after etching process. Airborne particle abrasion resulted in higher shear bond strengths compared to etching treatment. Modes of failure varied among different groups. Finally, it is concluded that micromechanical adhesion was a more effective mechanism than chemical adhesion and airborne particle abrasion significantly increased mean shear bond strengths compared with another surface treatments. - Highlights: • Understanding the dominant mechanism of bonding

  16. Design and safety studies on the European Facility for Industrial Transmutation (EFIT) with CERMET fuel

    International Nuclear Information System (INIS)

    Chen, X.N.; Rineiski, A.; Liu, P.; Matzerath Boccaccini, C.; Flad, M.; Gabrielli, F.; Maschek, W.; Morita, K.

    2008-01-01

    European R and D for ADS design and fuel development is driven in the 6 th FP of the EU by the EUROTRANS Programme [1]. In EUROTRANS two ADS design routes are followed, the XT-ADS and the EFIT. The XT-ADS is designed to provide the experimental demonstration of transmutation in an Accelerator Driven System. The EFIT development, the European Facility for Industrial Transmutation, aims at a generic conceptual design of a full transmuter. A key issue of the R and D work is the choice of an adequate fuel to be used in an Accelerator Driven Transmuter (ADT) like EFIT. Various fuel forms have been assessed. CERCER and CERMET fuels, specifically with the matrices MgO and Mo, have finally been selected and are now under closer investigation. Within EUROTRANS, a special domain named 'AFTRA', is responsible to more deeply assess the behavior of these dedicated fuels and to provide the fuel data base for the core design of the EFIT. The EFIT concept has to be optimized towards: a good transmutation efficiency, high burnup, low reactivity swing, low power peaking, adequate subcriticality, reasonable beam requirements and a high safety level. The final recommendation on fuels by AFTRA gave a ranking of these fuels based on the mentioned criteria. The composite CERMET fuel (Pu 0.5 ,Am 0.5 )O 2-x - Mo (with the isotope 92 Mo comprising 93% of the molybdenum) has been recommended as the primary candidate for the EFIT. This CERMET fuel fulfils adopted criteria for fabrication and reprocessing, and provides excellent safety margins. Disadvantages include the cost for enrichment of 92 Mo and a lower specific transmutation rate of minor actinides, because of the higher neutron absorption cross-section of the matrix. The composite CERCER fuel (Pu 0.4 ,Am 0.6 )O 2-x - MgO has therefore been recommended as a backup solution as it might offer a higher consumption rate of minor actinides, and can be manufactured for a lower unit cost. This paper is in fact a sequel to our last paper [2

  17. Ionoluminscence of partially-stabilized zirconia for thermal barrier coatings

    International Nuclear Information System (INIS)

    Rebollo, N.R.; Ruvalcaba-Sil, J.L.; Miranda, J.

    2007-01-01

    Ionoluminescence is explored as an alternative technique to study the high temperature phase stability of zirconia-based oxides. The evolution of an initially metastable single tetragonal phase towards de-stabilization is investigated for three single-doped zirconia compositions with Y, Yb and Gd. The differences in de-stabilization paths are identified using X-ray diffraction and ionoluminescence; elemental analysis is also performed using particle-induced X-ray emission. X-ray diffraction studies reveal a different scenario for each of the compositions selected; the differences are strongly influenced by the thermodynamic driving forces associated to the fluorite-to-tetragonal displacive transformation. Ionoluminescence studies indicate a significant increment on the signal intensity for de-stabilized samples, relative to previous annealing stages. There are also more subtle differences in the luminescent response from the samples at intermediate annealing stages also related to phase changes. This study provides a basis to characterize phase evolution in single-doped zirconia compositions for thermal insulation applications using luminescence

  18. Effect of accelerated aging on translucency of monolithic zirconia

    Directory of Open Access Journals (Sweden)

    O. Abdelbary

    2016-12-01

    Conclusion: Thickness of zirconia has significant effect on translucency. Aging has significant effect on thinner sections of zirconia. More research is required on zirconia towards making the material more translucent for its potential use as esthetic monolithic restoration.

  19. Nanooxide/Polymer Composites with Silica@PDMS and Ceria-Zirconia-Silica@PDMS: Textural, Morphological, and Hydrophilic/Hydrophobic Features.

    Science.gov (United States)

    Sulym, Iryna; Goncharuk, Olena; Sternik, Dariusz; Terpilowski, Konrad; Derylo-Marczewska, Anna; Borysenko, Mykola V; Gun'ko, Vladimir M

    2017-12-01

    SiO 2 @PDMS and CeO 2 -ZrO 2 -SiO 2 @PDMS nanocomposites were prepared and studied using nitrogen adsorption-desorption, Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), measurements of advancing and receding contact angles with water, and microcalorimetry. The pore size distributions indicate that the textural characteristics change after oxide modification by poly(dimethylsiloxane) (PDMS). Composites are characterized by mainly mesoporosity and macroporosity of aggregates of oxide nanoparticles or oxide@PDMS nanoparticles and their agglomerates. The FT-IR spectra show that PDMS molecules cover well the oxide surface, since the intensity of the band of free silanols at 3748 cm -1 decreases with increasing PDMS concentration and it is absent in the IR spectrum at C PDMS  ≥ 20 wt% that occurs due to the hydrogen bonding of the PDMS molecules to the surface hydroxyls. SEM images reveal that the inter-particle voids are gradually filled and aggregates are re-arranged and increase from 20 to 200 nm in size with the increasing polymer concentration. The highest hydrophobicity (contact angle θ = 140° at C PDMS  = 20-40 wt%) is obtained for the CeO 2 -ZrO 2 -SiO 2 @PDMS nanocomposites. The heat of composite immersion in water shows a tendency to decrease with increasing PDMS concentration.

  20. Microstructure and properties of multiphase sintered cermets Fe-Fe{sub 2}B; Mikrostruktura i wlasnosci spiekanych reakcyjnie cermetali Fe-Fe{sub 2}B

    Energy Technology Data Exchange (ETDEWEB)

    Nowacki, J. [Wydzial Inzynierii Materialowej, Politechnika Szczecinska, Szczecin (Poland); Klimek, L. [Instytut Inzynierii Materialowej i Technik Bezwiorowych, Politechnika Lodzka, Lodz (Poland)

    1998-12-31

    The process of multiphase sintering of iron in the vacuum has been analysed. As a result of the process iron-iron boride cermets have been produced. Fe-Fe{sub 2}B cermets were obtained as a result of sintering of the Fe and B pure elements in the vacuum. Attemps at sintering in the solid phase and with the participation of the liquid phase, the Fe-Fe{sub 2}B eutectic, have been made. Metallographic qualitative and quantitative studies, X-ray structural qualitative and qauantitative analysis allowed to determine the structure of Fe{sub 2}B cermets, as well as a description of the kinetics of quantitative changes in phase proportions in the course of sintering. It has been found that their structure varies widely depending on sintering parameters and the composition of the sinters. Measurements of the Fe-Fe{sub 2}B cermets hardness and measurements on wear during dry friction by the pin-on-disc method have shown distinct advantages of the cermets as a modern constructional materials. The hardness of Fe-Fe{sub 2}B cermets, depending on their chemical composition and sintering parameters, ranges widely from 150 to 1500 HV, and their resistance to wear is comparable to that of diffusively boronized steels. FeFe{sub 2}B cermets are a composite material in which iron boride, Fe{sub 2}B, with a hardness of about 1800 HV plays the role of the reinforcement,while iron-iron boride, Fe-Fe{sub 2}B, with a hardness of about 500 HV plays the role of matrix. The eutectic in the spaces between iron boride grains is composed of boron solid solution plates in iron with a hardness of arround 250 HV, and iron boride, Fe{sub 2}B, plates with a hardness of approximaly 1800 HV. The combination of such different materials, a hard reinforcement and a relatively plastic matrix produces favourable properties of the cermet thus produced high hardness (1500 HV) constant over whole cross section of the material, resistance of abrasive wear and acceptable ductility. The properties mentioned above

  1. Uranium-Based Cermet Alloys; Cermets a base d'uranium; Metallokeramicheskie splavy na osnove urana; Cermets a base de uranio

    Energy Technology Data Exchange (ETDEWEB)

    Ivanov, V. E.; Zelenskij, V. F.; Voloshchuk, A. I.; Grishok, V. N. [Fiziko-Tekhnicheskij Institut an USSR, Khar' kov, SSSR (Russian Federation)

    1963-11-15

    The paper describes certain features of dispersion-hardened uranium-based cermets. As possible hardening materials, consideration was given to UO{sub 2}, UC, Al{sub 2}O{sub 3}, MgO and UBe{sub 13}. Data were obtained on the behaviour of uranium alloys containing the above-mentioned admixtures during creep tests, short-term strength tests and cyclic thermal treatment. The corrosion resistance o f UBe{sub 13}-based uranium alloys was also studied. )author) [French] Les auteurs decrivent certaines proprietes de cermets a base d'uranium, dont la resistance a ete accrue a l'aide de particules dispersees. Les materiaux utilises a cette fin sont notamment: UO{sub 2}, UC, Al{sub 2}O{sub 3}, MgO et UBe{sub 13}. Les auteurs indiquent les donnees obtenues sur le comportement des cermets a l'uranium; durant les essais de fluage, les essais de resistance a court terme et le traitement thermique cyclique, en mentionnant les substances ajoutees. Ils etudient enfin la resistance a la corrosion des cermets d'uranium et UBe{sub 13}. (author) [Spanish] Los autores describen algunas propiedades de los cermets a base de uranio, reforzados por particulas de diversos compuestos en dispersion. En calidad de posibles materiales de refuerzo, ensayaron el UO{sub 2}, el UC, el Al{sub 2}O{sub 3}, el MgO y el UBe{sub 13}. Obtuvieron datos sobre el comportamiento de esas aleaciones en ensayos de fluencia, ensayoe rapidos de resistencia y tratamiento termico ciclico. Por ultimo, estudiaron la resistencia a la corrosion de las aleaciones de uranio a base de UBe{sub 13}. (author) [Russian] Daetsya opisanie nekotorykh svojstv metallokeramicheskikh splavov urana, uprochnennykh dispersionnymi chastitsami. V kachestve vozmozhnykh uprochnyayushchikh materialov izuchalis' UO{sub 2}, UC, Al{sub 2}O{sub 3} , MgO i UBe{sub 13}. Polucheny dannye o povedenii splavov urana s ukazannymi primesyami pri kripovykh ispytaniyakh, pri kratkovremennykh prochnostnykh ispytaniyakh i pri tsiklicheskoj termoobrabotke

  2. Grinding mechanism of zirconia toughened alumina

    International Nuclear Information System (INIS)

    Tsukuda, A.; Kondo, Y.; Yokota, K.

    1998-01-01

    In the grinding process, physical properties of ceramics affect both grinding mechanism and quality of ground surface. In this study we focused on fracture toughness of ceramics and the effect on grinding. A grinding test was carried out by single point grinding for ten different zirconia toughened alumina ceramics with different monoclinic zirconia contents. Effects of zirconia contents on the grinding mechanism and crack initiation were discussed. Copyright (1998) AD-TECH - International Foundation for the Advancement of Technology Ltd

  3. Basic research on cermet nuclear fuel

    Energy Technology Data Exchange (ETDEWEB)

    Ohashi, Hiroshi; Sto, Seichi [Hokkaido Univ., Sapporo (Japan). Faculty of Engineering; Takano, Masahide; Minato, Kazuo; Fukuda, Kosaku

    1998-01-01

    Production of cermet nuclear fuel having fine uranium dioxide (UO{sub 2}) particles dispersed in matrix metal requires basic property data on the compatibility of matrix metal with fission product compounds. It is thermodynamically suggested that, as burnup increases, cesium in oxide fuel reacts with the fuel, other fission products or cladding pipe and produces cesium uranates, cesium molybdate, or cesium chromate in stainless steel cladding pipe. Attempt was made to measure the thermal expansion coefficient and thermal conductivity of cesium uranates (Cs{sub 2}UO{sub 4} and Cs{sub 2}U{sub 2}O{sub 7}), cesium molybdate (Cs{sub 2}MoO{sub 4}) and cesium chromate (Cs{sub 2}CrO{sub 4}). Thermal expansion was measured by X-ray diffraction and determined by Cohen`s method. Thermal conductivity was obtained by measuring thermal diffusion by laser flash method. The thermal expansion of Cs{sub 2}UO{sub 4} and Cs{sub 2}U{sub 2}O{sub 7} is as low as 1.2% for the former and 1.0% for the latter, up to 1000K. The thermal expansion of Cs{sub 2}MoO{sub 4} is as high as that of Cs{sub 2}CrO{sub 4}, 2.1% for the former and 2.5% for the latter at temperatures from room temperature to 873K. Average thermal expansion in this temperature range is 4.4 x 10{sup -5} K{sup -1} for Cs{sub 2}MoO{sub 4} and 4.2 x 10{sup -5} K{sup -1}. The thermal expansion of Cs{sub 2}CrO{sub 4} is four times higher than that of UO{sub 2} and five times higher than that of Cr{sub 2}O{sub 3}. The thermal conductivity of Cs{sub 2}UO{sub 4} is nearly equal to that of Cs{sub 2}U{sub 2}O{sub 7} in absolute value and temperature dependency. Cs{sub 2}U{sub 2}O{sub 7}, having different thermal conductivity between {alpha} and {beta} phases, shows higher conductivity with {beta} than with {alpha}, about 1/4 of that of UO{sub 2} at 1000K. The thermal conductivity of Cs{sub 2}CrO{sub 4} is nearly equal to that of Cs{sub 2}MoO{sub 4} in absolute value and temperature dependency. (N.H.)

  4. In-Situ Optical Studies of Oxidation/Reduction Kinetics on SOFC Cermet Anodes

    Science.gov (United States)

    2010-12-28

    DATES COVERED (From - To) 1/29/10-9/30/10 4. TITLE AND SUBTITLE In situ optical studies of oxidation/reduction kinetics on SOFC cermet anodes 5a...0572 In-situ Optical Studies of Oxidation/Reduction Kinetics on SOFC Cermet Anodes Department of Chemistry and Biochemistry Montana State University...of Research In-situ Optical Studies of Oxidation/Reduction Kinetics on SOFC Cermet Anodes Principal Investigator Robert Walker Organization

  5. Glass-ionomer-silver-cermet interim Class I restorations for permanent teeth.

    Science.gov (United States)

    Croll, T P; Killian, C M

    1992-11-01

    Glass-ionomer-silver-cermet cement has proved to be a worthy alternative to silver amalgam for restoring certain Class I lesions in primary teeth. Such restorations are now known to last up to 8 years without need for repair or replacement. Cermet cement has also been used for interim restoration of permanent teeth in special cases, with ideal results. The procedure for placing a glass-ionomer-silver-cermet cement Class I restoration is described.

  6. Results of experimental investigations for substantiation of WWER cermet fuel pin performance

    International Nuclear Information System (INIS)

    Popov, V.V.; Karpin, A.D.; Isupov, I.A.; Rumyantsev, V.N.; Troyanov, V.M.; Subonyaev, V.N.; Melnichenko, N.A.

    1997-01-01

    The out-of-pile experiment results on interaction of the cladding and matrix materials and uranium dioxide at cermet fuel temperature for normal operating conditions of the WWER-440 reactor are analyzed. Cermet fuel element behaviour under the maximum designed damage of the WWER-440 reactor is considered. In the AM reactor loop a fission product output from the unsealed cermet fuel elements have been studied. (author). 6 figs, 3 tabs

  7. Cermet based solar selective absorbers : further selectivity improvement and developing new fabrication technique

    OpenAIRE

    Nejati, Mohammadreza

    2008-01-01

    Spectral selectivity of cermet based selective absorbers were increased by inducing surface roughness on the surface of the cermet layer using a roughening technique (deposition on hot substrates) or by micro-structuring the metallic substrates before deposition of the absorber coating using laser and imprint structuring techniques. Cu-Al2O3 cermet absorbers with very rough surfaces and excellent selectivity were obtained by employing a roughness template layer under the infrared reflective l...

  8. The design of cermet fuel phase fraction and fuel particle diameter

    International Nuclear Information System (INIS)

    Tian Sheng.

    1986-01-01

    UO 2 -Zr-2 is an ideal cermet fuel. As an exemplification with this fuel, this paper emphatically elucidates the irradiation theory of cermet fuel and its application in the design of cermet fuel phase fraction and of fuel particle diameter. From the point of view of the irradiation theory and the consideration for sandwich rolling, the suitable volume fraction of UO 2 phase of 25% and diameter of UO 2 particle of 100 +- 15 μm are selected

  9. Light modulation in phase change disordered metamaterial - A smart cermet concept

    OpenAIRE

    Kumar , Sunil; Maury , Francis; Bahlawane , Naoufal

    2017-01-01

    International audience; Cermet coatings are popular solar selective absorbers as they allow capturing most of the solar energywhile minimising radiative losses. Embedded metallic nanoparticles in dielectric matrices promotemultiple internal reflection of light and provide an overall low emissivity. VO2 in the metamaterial stateis regarded in this study as a responsive mixed phase comprising metallic rutile VO2 inclusions insemiconducting monoclinic VO2 phase mimicking cermet. The smart cermet...

  10. Dilemmas in zirconia bonding: A review

    Directory of Open Access Journals (Sweden)

    Obradović-Đuričić Kosovka

    2013-01-01

    Full Text Available This article presents a literature review on the resin bond to zirconia ceramic. Modern esthetic dentistry has highly recognized zirconia, among other ceramic materials. Biocompatibility of zirconia, chemical and dimensional stability, excellent mechanical properties, all together could guarantee optimal therapeutical results in complex prosthodontic reconstruction. On the other hand, low thermal degradation, aging of zirconia as well as problematic bonding of zirconia framework to dental luting cements and tooth structures, opened the room for discussion concerning their clinical durability. The well known methods of mechanical and chemical bonding used on glass-ceramics are not applicable for use with zirconia. Therefore, under critical clinical situations, selection of the bonding mechanism should be focused on two important points: high initial bond strength value and long term bond strength between zirconia-resin interface. Also, this paper emphases the use of phosphate monomer luting cements on freshly air-abraded zirconia as the simplest and most effective way for zirconia cementation procedure today.

  11. Duo_2-Steel cermet manufacturing technology for PWR Spent Nuclear Fuel (SNF) casks

    International Nuclear Information System (INIS)

    Siti Alimah; Budiarto

    2005-01-01

    Assessment of DUO_2-Steel cermet manufacturing technology for PWR SNF casks has been done. DUO_2-Steel cermet consisting of DUO_2 particulates and other particulates, embedded in a steel matrix. Cermet SNF casks have the potential for superior performance compared with casks constructed of other materials. The addition of DUO_2 ceramic particulates can increase SNF cask capacity, improve of repository performance and disposal of excess depleted uranium as potential waste. Two sets of cermet manufacturing technologies are casting and powder metallurgy. Three casting methods are infusion casting, traditional casting and centrifugal casting. While for powder metallurgy methods there are traditional method and new method. DUO_2-Steel cermet have traditionally been produced by powder metallurgy methods. The production of a cask, however, presents special requirements: the manufacture of an annular object with weights up to 100 tons, and methods are being not to manufacture a cermet of this size and geometry. A new powder metallurgy method, is a method for manufacturing cermet for PWR SNF cask. This powder metallurgy techniques have potentials low costs and provides greater freedom In the design of the cermet cask by allowing variable cermet properties. (author)

  12. Influence of starting precursors and synthesis methods on the physiochemical properties of zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Gaydhankar, T.R., E-mail: tr.gaydhankar@ncl.res.in [Catalysis Division, National Chemical Laboratory, Pune 411008 (India); Jha, R.K. [Catalysis Division, National Chemical Laboratory, Pune 411008 (India); Nikalje, M.D. [Department of Chemistry, University of Pune, Pune 411 007 (India); Waghmare, K.J. [Catalysis Division, National Chemical Laboratory, Pune 411008 (India)

    2014-07-01

    Graphical abstract: Crystallite size of tetragonal phase of the zirconia samples prepared using different synthesis parameters and precursors as a function of calcination temperature. Surface area values of the zirconia samples calcined at 500 and 700 °C are in given brackets. - Highlights: • Zirconia prepared with modified sol–gel method is less stable compared with zirconia prepared by precipitation method. • Optimized synthesis conditions shifted the glow exotherm to higher temperature range indicating better thermal stability. • Tetragonal-zirconia could be synthesized in cost-effective manner using zirconium oxy-nitrate. • In our studies no co-relation between the surface area and crystallite size was observed. - Abstract: Under identical and judiciously pre-optimized synthesis conditions, the influence of different combinations of zirconium sources and/or post treatment conditions on structural properties, thermal stability, phase composition and morphology of zirconia has been investigated. High surface area tetragonal zirconia could be synthesized in a cost-effective manner from 1 M solution of zirconium oxy-nitrate at pH 11 using aqueous ammonia solution as a precipitant when calcined at 400 °C for 3 h. Irrespective of the preparation method, pH and starting precursor, zirconia samples prepared without digestion contained dominant monoclinic phase with some traces of tetragonal phase when calcined at 700 °C. Even though there is linear decrease in surface area with increase in the crystallite size for each sample as a function of calcination temperature, no co-relation between the surface area and crystallite size could be achieved. SEM images show agglomerated and irregular shape particles between 10 to 20 μm.

  13. Influence of heat treatment on the high temperature oxidation mechanisms of an Fe-TiCN cermet

    OpenAIRE

    Alvaredo Olmos, Paula; Abajo Clemente, Carolina; Tsipas, Sophia Alexandra; Gordo Odériz, Elena

    2014-01-01

    In this study, the oxidation behaviour of an iron matrix cermet containing 50 % vol. Ti(C,N) was investigated before and after heat treatment by oxidation tests performed in static air at temperatures between 500 °C and 1000 °C. The oxidation mechanism for this type of composite materials was established and it was found that the heat treated material presents lower mass gain than the as-sintered material at the early stages of the oxidation, due to the volatilization of oxides. The oxidation...

  14. HIGH TEMPERATURE EROSION WEAR OF CERMET PARTICLES REINFORCED SELF-FLUXING ALLOY MATRIX HVOF SPRAYED COATINGS

    Directory of Open Access Journals (Sweden)

    Andrei Surzhenkov

    2015-09-01

    Full Text Available In the present paper, the resistance of high velocity oxy-fuel (HVOF sprayed TiC-NiMo and Cr3C2-Ni cermet particles reinforced NiCrSiB self-fluxing alloy matrix coatings to high temperature erosion wear is studied. Microstructure of the coatings was examined by SEM, phase composition was determined by XRD. A four-channel centrifugal particle accelerator was applied to study the high temperature erosion wear of the coatings. The impact angles were 30 and 90 degrees, initial particle velocity was 50 m/s, temperature of the test - 650 degrees. Volume wear of the coatings was calculated and compared to the respective values of the reference materials. Wear mechanisms were studied by SEM.DOI: http://dx.doi.org/10.5755/j01.ms.21.3.7617

  15. Synthesis and characterization of nanocrystalline Ni-YSZ cermet anode for SOFC

    International Nuclear Information System (INIS)

    Priyatham, T.; Bauri, Ranjit

    2010-01-01

    Ni-YSZ cermet anode has been synthesized in one step using a simple and cost effective combustion synthesis process. The processed powder of NiO-YSZ is found to be nanocrystalline with crystallite sizes of 29 and 22 nm for NiO and YSZ respectively by X-ray diffraction and transmission electron microscopy analysis. X-ray diffraction analysis also shows that the precursor salts are converted to highly crystalline phases of NiO and YSZ (8 mol% Y 2 O 3 ) without any intermediate calcination step and no undesirable phases are present. Comparison with the X-ray diffraction pattern of a commercial YSZ sample shows that the process is also effective in maintaining a close compositional control. The microstructure of the sintered and reduced sample shows a well defined network of pores which is necessary for the effective functioning of the anode. The electrical conductivity as a function of temperature shows metallic behavior.

  16. Superplasticity and joining of zirconia-based ceramics

    International Nuclear Information System (INIS)

    Dominguez-Rodriguez, A.; Gutierrez-Mora, F.; Jimenez-Melendo, M.; Chaim, R.; Routbort, J. L.

    1999-01-01

    Steady-state creep and joining of alumina/zirconia composites containing alumina volume fractions of 20, 60, and 85% have been investigated between 1,250 and 1,350 C. Superplasticity of these compounds is controlled by grain-boundary sliding and the creep rate is a function of alumina volume fraction, not grain size. Using the principles of superplasticity, pieces of the composite have been joined by applying the stress required to achieve 5 to 10% strain to form a strong interface at temperatures as low as 1,200 C

  17. Superplasticity and joining of zirconia-based ceramics

    International Nuclear Information System (INIS)

    Gutierrez-Mora, F.; Dominguez-Rodriguez, A.; Jimenez-Melendo, M.; Chaim, R.; Ravi, G.B.; Routbort, J.L.

    2000-01-01

    Steady-state creep and joining of alumina/zirconia composites containing alumina volume fractions of 20, 60 and 85% have been investigated between 1,250 and 1,350 C. Superplasticity of these compounds is controlled by grain-boundary sliding and the creep rate is a function of alumina volume fraction, not grain size. Using the principles of superplasticity, pieces of the composite have been joined by applying the stress required to achieve 5 to 10% strain to form a strong interface at temperatures as low as 1,200 C

  18. Advanced propulsion engine assessment based on a cermet reactor

    Science.gov (United States)

    Parsley, Randy C.

    1993-01-01

    A preferred Pratt & Whitney conceptual Nuclear Thermal Rocket Engine (NTRE) has been designed based on the fundamental NASA priorities of safety, reliability, cost, and performance. The basic philosophy underlying the design of the XNR2000 is the utilization of the most reliable form of ultrahigh temperature nuclear fuel and development of a core configuration which is optimized for uniform power distribution, operational flexibility, power maneuverability, weight, and robustness. The P&W NTRE system employs a fast spectrum, cermet fueled reactor configured in an expander cycle to ensure maximum operational safety. The cermet fuel form provides retention of fuel and fission products as well as high strength. A high level of confidence is provided by benchmark analysis and independent evaluations.

  19. High pressure gas-filled cermet spark gaps

    International Nuclear Information System (INIS)

    Avilov, Eh.A.; Yur'ev, A.L.

    2000-01-01

    The results of modernization of the R-48 and R-49 spark gaps making it possible to improve their electrical characteristics are presented. The design is described and characteristics of gas-filled cermet spark gaps are presented. By the voltage rise time of 5-6 μs in the Marx generator scheme they provide for the pulse break-through voltage of 120 and 150 kV. By the voltage rise time of 0.5-1 μs the break-through voltage of these spark gaps may be increased up to 130 and 220 kV. The proper commutation time is equal to ≤ 0.5 ns. Practical recommendations relative to designing cermet spark gaps are given [ru

  20. Sintering of cermets on the base of corundum and molybdenum

    International Nuclear Information System (INIS)

    Fedotov, A.V.

    1987-01-01

    Liquid-phase sintering of cermets has been studied to develop rational technology allowing to produce a dense material at lower temperatures. Molybdenum of the MPCh mark with the specific surface ranged from 1900 to 4000 cm 2 /g and the corundum powder of the VK-94-1 mark with the specific surface of 6000 cm 2 /g containing upto 10% of the glass-phase have been used as initial materials. It is shown that application of the VK-94-1 ceramics powder for molybdenum content cermets allows to decrease the temperature of dense material production (∼ upto 100 deg C). To produce dense materials, it is necessary to restrict the initial porosity of compaction and to correspond it to the sintering conditions. The increase of molybdenum dispersion allows to produce material with the more homogeneous structure, higher density and strength. Molybdenum presence decreases recrystallization of corundum crystals and causes structure production resistant to high-temperature heating

  1. Electrochemical corrosion of cermet coatings in artificial marine water

    International Nuclear Information System (INIS)

    Cabot, P.L.; Fernandez, J.; Guilemany, J.M.

    1998-01-01

    The electrochemical corrosion of different WC+12Co coatings sprayed on 34CrMo4 (UNS-G41350) steel by the high velocity oxygen fuel technique has been studied by corrosion potential and impedance measurements considering previous SEM observations and EDX microanalysis. The experiments were conducted in artificial marine water at 20 C and the impedance spectra were obtained at the corresponding corrosion potentials for the substrate, coating and substrate-coating systems. The impedance diagrams indicated that the electrochemical corrosion of the steel-coating systems is controlled by oxygen diffusion through a porous film of corrosion products, as in the case of the shot-blasted steel. In contrast, the corrosion of the coating appeared to be controlled by diffusion of oxygen through the electrolyte. The impedance diagrams obtained for the steel-coating systems depended on the porosities of the cermet coatings, thus being an useful procedure to characterize metals coated by cermets. (orig.)

  2. Remote micro-encapsulation of curium-gold cermets

    International Nuclear Information System (INIS)

    Coops, M.S.; Voegele, A.L.; Hayes, W.N.; Sisson, D.H.

    1980-01-01

    A technique is described for fabricating minature, high-density capsules of curium-244 oxide contained in three concentric jackets of metallic gold (or silver), with the outer surface being free of alpha contamination. The completed capsules are right circular cylinders 0.2500-inch diameter and 0.125-inch tall, with each level of containment soldered (or brazed) closed. A typical capsule would contain approx. 70 mg of 244 Cm (5.7 Ci) mixed with 120 mg of gold powder in the form of a cermet wafer clad in three concentric, 0.010-inch thick, liquid tight jackets. This method of fabrication eliminates voids between the jackets and produces a minimum size, maximum density capsule. Cermet densities of 11.5 g/cc were obtained, with an overall density of 17.3 g/cc for the finished capsule

  3. Synthesis of Ceria Zirconia Oxides using Solvothermal Treatment

    Directory of Open Access Journals (Sweden)

    Machmudah Siti

    2018-01-01

    Full Text Available Ceria oxide (CeO2 is widely used as catalyst with high oxygen storage capacity at low temperature. The addition of zirconia oxide (ZrO2 to CeO2 can enhance oxygen storage capacity as well as thermal stability. In this work, ceria zirconia oxides has been synthesized via a low temperature solvothermal treatment in order to produce ceria zirconia oxides composite with high oxygen storage capacity as electrolyte of solid oxide fuel cells (SOFC. Under solvothermal conditions, solvent may control the direction of crystal growth, morphology, particle size and size distribution, because of the controllability of thermodynamics and transport properties by pressure and temperature. Water, mixed of water and ethanol (70/30 vol/vol, and mixed of water and ethylene glycol (70/30 vol/vol were used as solvent, while Ce(NO33 and ZrO(NO32 with 0.06 M concentration were used as precursor. The experiments were conducted at temperature of 150 °C and pressure for 2 h in a Teflon-lined autoclave of 100 mL volume. The synthesized products were dried at 60 °C for 6 and 12 h and then calcined at 900 °C for 6 h. The particle products were characterized using SEM, XRD, TG/DTA, and Potentiostat. The results showed that the morphology of particles formed were affected by the solvent. Solid plate shaped particles were produced in water, and tend to be pore with the addition of ethylene glycol. The addition of ethanol decreased the size of particles with sphere shaped. The XRD pattern indicated that ceria-zirconia oxides particles are uniformly distributed in the structure to form a homogeneous solid solution. Based on the electrochemical analysis, ceria zirconia oxides produced via solvothermal synthesis had high conductivity ion of 0.5594 S/cm, which is higher than minimum conductivity ion requirement of 0.01 S/cm for SOFC electrolyte. It indicated that ceria zirconia oxides produced via solvothermal synthesis is suitable for SOFC electrolyte.

  4. A fast spectrum dual path flow cermet reactor

    International Nuclear Information System (INIS)

    Anghaie, S.; Feller, G.J.; Peery, S.D.; Parsley, R.C.

    1993-01-01

    A cermet fueled, dual path fast reactor for space nuclear propulsion applications is conceptually designed. The reactor utilizes an outer annulus core and an inner cylindrical core with radial and axial reflector. The dual path flow minimizes the impact of power peaking near the radial reflector. Basic neutronics and core design aspects of the reactor are discussed. The dual path reactor is integrated into a 25000 lbf thrust nuclear rocket

  5. A Science-Based Understanding of Cermet Processing

    Energy Technology Data Exchange (ETDEWEB)

    Cesarano, III, Joseph [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Roach, Robert Allen [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Kilgo, Alice C. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Susan, Donald Francis [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Van Ornum, David J. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Stuecker, John N. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Shollenberger, Kimberly A. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2006-04-01

    This report is a summary of the work completed in FY01 for science-based characterization of the processes used to fabricate 1) cermet vias in source feedthrus using slurry and paste-filling techniques and 2) cermet powder for dry pressing. Common defects found in cermet vias were characterized based on the ability of subsequent processing techniques (isopressing and firing) to remove the defects. Non-aqueous spray drying and mist granulation techniques were explored as alternative methods of creating CND50, the powder commonly used for dry pressed parts. Compaction and flow characteristics of these techniques were analyzed and compared to standard dry-ball-milled CND50. Due to processing changes, changes in microstructure can occur. A microstructure characterization technique was developed to numerically describe cermet microstructure. Machining and electrical properties of dry pressed parts were also analyzed and related to microstructure using this analytical technique.3 Executive SummaryThis report outlines accomplishments in the science-based understanding of cermet processing up to fiscal year 2002 for Sandia National Laboratories. The three main areas of work are centered on 1) increasing production yields of slurry-filled cermets, 2) evaluating the viability of high-solids-loading pastes for the same cermet components, and 3) optimizing cermet powder used in pressing processes (CND50). An additional development that was created as a result of the effort to fully understand the impacts of alternative processing techniques is the use of analytical methods to relate microstructure to physical properties. Recommendations are suggested at the end of this report. Summaries of these four efforts are as follows:1.Increase Production Yields of Slurry-Filled Cermet Vias Finalized slurry filling criteria were determined based on three designs of experiments where the following factors were analyzed: vacuum time, solids loading, pressure drop across the filter paper

  6. Characteristics of porous zirconia coated with hydroxyapatite

    Indian Academy of Sciences (India)

    However, porous hydroxyapatite bodies are mechanically weak and brittle, which makes shaping and implantation difficult. One way to solve this problem is to introduce a strong porous network onto which hydroxyapatite coating is applied. In this study, porous zirconia and alumina-added zirconia ceramics were prepared ...

  7. Surface degradation of nanocrystalline zirconia dental implants

    NARCIS (Netherlands)

    Ocelík, Václav; Schepke, Ulf; Rasoul, Hamid Haji; Cune, Marco S.; De Hosson, Jeff Th M.

    2017-01-01

    Yttria-stabilized zirconia prepared by hot isostatic pressing represents attractive material for biomedical applications. In this work the degradation of yttria-stabilized zirconia dental implants abutments due to the tetragonal to monoclinic phase transformation after one year of clinical use was

  8. Evolution of the nickel/zirconia interface

    International Nuclear Information System (INIS)

    Shinde, S.L.; Olson, D.A.; De Jonghe, L.C.; Miller, R.A.

    1986-01-01

    The changes taking place at the nickel zirconia interface during oxidation in air at 900 0 C were studied using analytical electron microscopy (AEM). The nickel oxide layer growing at the interface and the stabilizers used in zirconia interact, giving different interface morphologies

  9. Detection and classification of gaseous sulfur compounds by solid electrolyte cyclic voltammetry of cermet sensor array.

    Science.gov (United States)

    Kramer, Kirsten E; Rose-Pehrsson, Susan L; Hammond, Mark H; Tillett, Duane; Streckert, Holger H

    2007-02-12

    Electrochemical sensors composed of a ceramic-metallic (cermet) solid electrolyte are used for the detection of gaseous sulfur compounds SO(2), H(2)S, and CS(2) in a study involving 11 toxic industrial chemical (TIC) compounds. The study examines a sensor array containing four cermet sensors varying in electrode-electrolyte composition, designed to offer selectivity for multiple compounds. The sensors are driven by cyclic voltammetry to produce a current-voltage profile for each analyte. Raw voltammograms are processed by background subtraction of clean air, and the four sensor signals are concatenated to form one vector of points. The high-resolution signal is compressed by wavelet transformation and a probabilistic neural network is used for classification. In this study, training data from one sensor array was used to formulate models which were validated with data from a second sensor array. Of the 11 gases studied, 3 that contained sulfur produced the strongest responses and were successfully analyzed when the remaining compounds were treated as interferents. Analytes were measured from 10 to 200% of their threshold-limited value (TLV) according to the 8-h time weighted average (TWA) exposure limits defined by the National Institute of Occupational Safety and Health (NIOSH). True positive classification rates of 93.3, 96.7, and 76.7% for SO(2), H(2)S, and CS(2), respectively, were achieved for prediction of one sensor unit when a second sensor was used for modeling. True positive rates of 83.3, 90.0, and 90.0% for SO(2), H(2)S, and CS(2), respectively, were achieved for the second sensor unit when the first sensor unit was used for modeling. Most of the misclassifications were for low concentration levels (such 10-25% TLV) in which case the compound was classified as clean air. Between the two sensors, the false positive rates were 2.2% or lower for the three sulfur compounds, 0.9% or lower for the interferents (eight remaining analytes), and 5.8% or lower for

  10. Detection and classification of gaseous sulfur compounds by solid electrolyte cyclic voltammetry of cermet sensor array

    International Nuclear Information System (INIS)

    Kramer, Kirsten E.; Rose-Pehrsson, Susan L.; Hammond, Mark H.; Tillett, Duane; Streckert, Holger H.

    2007-01-01

    Electrochemical sensors composed of a ceramic-metallic (cermet) solid electrolyte are used for the detection of gaseous sulfur compounds SO 2 , H 2 S, and CS 2 in a study involving 11 toxic industrial chemical (TIC) compounds. The study examines a sensor array containing four cermet sensors varying in electrode-electrolyte composition, designed to offer selectivity for multiple compounds. The sensors are driven by cyclic voltammetry to produce a current-voltage profile for each analyte. Raw voltammograms are processed by background subtraction of clean air, and the four sensor signals are concatenated to form one vector of points. The high-resolution signal is compressed by wavelet transformation and a probabilistic neural network is used for classification. In this study, training data from one sensor array was used to formulate models which were validated with data from a second sensor array. Of the 11 gases studied, 3 that contained sulfur produced the strongest responses and were successfully analyzed when the remaining compounds were treated as interferents. Analytes were measured from 10 to 200% of their threshold-limited value (TLV) according to the 8-h time weighted average (TWA) exposure limits defined by the National Institute of Occupational Safety and Health (NIOSH). True positive classification rates of 93.3, 96.7, and 76.7% for SO 2 , H 2 S, and CS 2 , respectively, were achieved for prediction of one sensor unit when a second sensor was used for modeling. True positive rates of 83.3, 90.0, and 90.0% for SO 2 , H 2 S, and CS 2 , respectively, were achieved for the second sensor unit when the first sensor unit was used for modeling. Most of the misclassifications were for low concentration levels (such 10-25% TLV) in which case the compound was classified as clean air. Between the two sensors, the false positive rates were 2.2% or lower for the three sulfur compounds, 0.9% or lower for the interferents (eight remaining analytes), and 5.8% or lower for

  11. Assessment of polyphase sintered iron-cobalt-iron boride cermets

    International Nuclear Information System (INIS)

    Nowacki, J.; Pieczonka, T.

    2004-01-01

    Sintering of iron, cobalt and boron powders has been analysed. As a result iron-iron boride, Fe-Fe 2 B and iron/cobalt boride with a slight admixture of molybdenum, Fe - Co - (FeMoCo) 2 B cermets have been produced. Iron was introduced to the mixture as the Astalloy Mo Hoeganaes grade powder. Elemental amorphous boron powder was used, and formation of borides occurred both during heating and isothermal sintering periods causing dimensional changes of the sintered body. Dilatometry was chosen to control basic phenomena taking place during multiphase sintering of investigated systems. The microstructure and phase constituents of sintered compacts were controlled as well. The cermets produced were substituted to: metallographic tests, X-ray analysis, measurements of hardness and of microhardness, and of wear in the process of sliding dry friction. Cermets are made up of two phases; hard grains of iron - cobalt boride, (FeCo) 2 B (1800 HV) constituting the reinforcement and a relatively soft and plastic eutectic mixture Fe 2 B - Co (400-500 HV) constituting the matrix. (author)

  12. Cermet Ni-ZrO2 by mechanical alloying

    International Nuclear Information System (INIS)

    Leite, Douglas Will

    2010-01-01

    The ZrO 2 and metallic Ni Cermet obtained by Mechanical Alloying - MA is studied in the present work with the objective to prepare solid oxide fuel cells anodes (SOFC). Metallic Ni is added under three different concentrations: 30, 40 and 50% volume. The millings were conducted in SPEX vibratory mill where the influence of milling time, process control additives efficiency, type and geometry of milling vessels were studied. The study of the influence of these variables was made under particle size analysis, surface area determination and resulting material morphology. The use of teflon vessel causes contamination by carbon. On the other side, steel vessel increases the contamination by metallic impurities. The several geometries projected and analyzed for the vessels showed that vessels with larger bottom radius (R.15) showed the best results. After conformation and sintering at 1300 degree C in argon atmosphere the samples reached densities between 60 and 80% of the theoretical density. Microstructures observed by scanning electron microscopy reveal good homogeneity in the Cermet phases distribution. The mechanical alloying technique was considered a good option to obtain Ni- ZrO 2 Cermet. (author)

  13. The radiation response of mesoporous nanocrystalline zirconia thin films

    Energy Technology Data Exchange (ETDEWEB)

    Manzini, Ayelén M.; Alurralde, Martin A. [Comisión Nacional de Energía Atómica, Centro Atómico Constituyentes, Av. General Paz 1499, 1650 San Martin, Provincia de Buenos Aires (Argentina); Giménez, Gustavo [Instituto Nacional de Tecnología Industrial - CMNB, Av. General Paz 5445, 1650 San Martín, Provincia de Buenos Aires (Argentina); Luca, Vittorio, E-mail: vluca@cnea.gov.ar [Comisión Nacional de Energía Atómica, Centro Atómico Constituyentes, Av. General Paz 1499, 1650 San Martin, Provincia de Buenos Aires (Argentina)

    2016-12-15

    The next generation of nuclear systems will require materials capable of withstanding hostile chemical, physical and radiation environments over long time-frames. Aside from its chemical and physical stability, crystalline zirconia is one of the most radiation tolerant materials known. Here we report the first ever study of the radiation response of nanocrystalline and mesoporous zirconia and Ce{sup 3+}-stabilized nanocrystalline zirconia (Ce{sub 0.1}Zr{sub 0.9}O{sub 2}) thin films supported on silicon wafers. Zirconia films prepared using the block copolymer Brij-58 as the template had a thickness of around 60–80 nm. In the absence of a stabilizing trivalent cation they consisted of monoclinic and tetragonal zirconia nanocrystals with diameters in the range 8–10 nm. Films stabilized with Ce{sup 3+} contained only the tetragonal phase. The thin films were irradiated with iodine ions of energies of 70 MeV and 132 keV at low fluences (10{sup 13} - 10{sup 14} cm{sup −2}) corresponding to doses of 0.002 and 1.73 dpa respectively, and at 180 keV and high fluences (2 × 10{sup 16} cm{sup −2}) corresponding to 82.4 dpa. The influence of heavy ion irradiation on the nanocrystalline structure was monitored through Rietveld analysis of grazing incidence X-ray diffraction (GIXRD) patterns recorded at angles close to the critical angle to ensure minimum contribution to the diffraction pattern from the substrate. Irradiation of the mesoporous nanocrystalline zirconia thin films with 70 MeV iodine ions, for which electronic energy loss is dominant, resulted in slight changes in phase composition and virtually no change in crystallographic parameters as determined by Rietveld analysis. Iodine ion bombardment in the nuclear energy loss regime (132–180 keV) at low fluences did not provoke significant changes in phase composition or crystallographic parameters. However, at 180 keV and high fluences the monoclinic phase was totally eliminated from the GIXRD

  14. Sulfur tolerant composite cermet electrodes for solid oxide electrochemical cells

    Science.gov (United States)

    Isenberg, Arnold O.

    1987-01-01

    An electrochemical apparatus is made containing an exterior electrode bonded to the exterior of a tubular, solid, oxygen ion conducting electrolyte where the electrolyte is also in contact with an interior electrode, said exterior electrode comprising particles of an electronic conductor contacting the electrolyte, where a ceramic metal oxide coating partially surrounds the particles and is bonded to the electrolyte, and where a coating of an ionic-electronic conductive material is attached to the ceramic metal oxide coating and to the exposed portions of the particles.

  15. Use of cermet thin film resistors with nitride passivated metal insulator field effect transistor

    Science.gov (United States)

    Brown, G. A.; Harrap, V.

    1971-01-01

    Film deposition of cermet resistors on same chip with metal nitride oxide silicon field effect transistors permits protection of contamination sensitive active devices from contaminants produced in cermet deposition and definition processes. Additional advantages include lower cost, greater reliability, and space savings.

  16. A thermionic energy converter with a molybdenum-alumina cermet emitter

    NARCIS (Netherlands)

    Gubbels, G.H.M.; Wolff, L.R.; Metselaar, R.

    1990-01-01

    A study is made of the properties of cermets as electrode materials for thermionic energy converters. For thermodynamic reasons it is expected that all cermets composed of pure Mo and refractory oxides have the same bare work function. From data on the work function of Mo in an oxygen atmosphere

  17. 3D-WOVEN FIBER-REINFORCED COMPOSITE FOR CAD/CAM DENTAL APPLICATION.

    Science.gov (United States)

    Petersen, Richard; Liu, Perng-Ru

    2016-05-01

    Three-dimensional (3D)-woven noncrimp fiber-reinforced composite (FRC) was tested for mechanical properties in the two principal directions of the main XY plane and compared to different Computer-Aided-Design/Computer-Aided-Machining (CAD/CAM) Dental Materials. The Dental Materials included ceramic with Vitablock Mark II®, ProCAD®, InCeram® Spinel, InCeram® Alumina and InCeram® Zirconia in addition to a resin-based 3M Corp. Paradigm® particulate-filled composite. Alternate material controls included Coors 300 Alumina Ceramic and a tungsten carbide 22% cobalt cermet. The 3D-woven FRC was vacuum assisted resin transfer molding processed as a one-depth-thickness ~19-mm preform with a vinyl-ester resin and cut into blocks similar to the commercial CAD/CAM Dental Materials. Mechanical test samples prepared for a flexural three-point span length of 10.0 mm were sectioned for minimum-depth cuts to compare machinability and fracture resistance between groups. 3D-woven FRC improved mechanical properties with significant statistical differences over all CAD/CAM Dental Materials and Coors Alumina Ceramic for flexural strength (p<0.001), resilience (p<0.05), work of fracture (p<0.001), strain energy release (p<0.05), critical stress intensity factor (p<0.001) and strain (p<0.001).

  18. Micro-scale mechanical characterization of Inconel cermet coatings deposited by laser cladding

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Ch.; Verdi, D.; Garrido, M.A.; Ruiz-Hervias, J.

    2016-07-01

    In this study, an Inconel 625-Cr3C2 cermet coating was deposited on a steel alloy by laser cladding. The elastic and plastic mechanical properties of the cermet matrix were studied by the depth sensing indentation (DSI) in the micro scale. These results were compared with those obtained from an Inconel 600 bulk specimen. The values of Young's modulus and hardness of cermet matrix were higher than those of an Inconel 600 bulk specimen. Meanwhile, the indentation stress–strain curve of the cermet matrix showed a strain hardening value which was more than twice the one obtained for the Inconel 600 bulk. Additionally, the mechanical properties of unmelted Cr3C2 ceramic particles, embedded in the cermet matrix were also evaluated by DSI using a spherical indenter. (Author)

  19. Micro-scale mechanical characterization of Inconel cermet coatings deposited by laser cladding

    Directory of Open Access Journals (Sweden)

    Chao Chang

    2016-07-01

    Full Text Available In this study, an Inconel 625-Cr3C2 cermet coating was deposited on a steel alloy by laser cladding. The elastic and plastic mechanical properties of the cermet matrix were studied by the depth sensing indentation (DSI in the micro scale. These results were compared with those obtained from an Inconel 600 bulk specimen. The values of Young's modulus and hardness of cermet matrix were higher than those of an Inconel 600 bulk specimen. Meanwhile, the indentation stress–strain curve of the cermet matrix showed a strain hardening value which was more than twice the one obtained for the Inconel 600 bulk. Additionally, the mechanical properties of unmelted Cr3C2 ceramic particles, embedded in the cermet matrix were also evaluated by DSI using a spherical indenter.

  20. Development of UO2/PuO2 dispersed in uranium matrix CERMET fuel system for fast reactors

    International Nuclear Information System (INIS)

    Sinha, V.P.; Hegde, P.V.; Prasad, G.J.; Pal, S.; Mishra, G.P.

    2012-01-01

    CERMET fuel with either PuO 2 or enriched UO 2 dispersed in uranium metal matrix has a strong potential of becoming a fuel for the liquid metal cooled fast breeder reactors (LMR’s). In fact it may act as a bridge between the advantages and disadvantages associated with the two extremes of fuel systems (i.e. ceramic fuel and metallic fuel) for fast reactors. At Bhabha Atomic Research Centre (BARC), R and D efforts are on to develop this CERMET fuel by powder metallurgy route. This paper describes the development of flow sheet for preparation of UO 2 dispersed in uranium metal matrix pellets for three different compositions i.e. U–20 wt%UO 2 , U–25 wt%UO 2 and U–30 wt%UO 2 . It was found that the sintered pellets were having excellent integrity and their linear mass was higher than that of carbide fuel pellets used in Fast Breeder Test Reactor programme (FBTR) in India. The pellets were characterized by X-ray diffraction (XRD) technique for phase analysis and lattice parameter determination. The optical microstructures were developed and reported for all the three different U–UO 2 compositions.

  1. Development of UO2/PuO2 dispersed in uranium matrix CERMET fuel system for fast reactors

    Science.gov (United States)

    Sinha, V. P.; Hegde, P. V.; Prasad, G. J.; Pal, S.; Mishra, G. P.

    2012-08-01

    CERMET fuel with either PuO2 or enriched UO2 dispersed in uranium metal matrix has a strong potential of becoming a fuel for the liquid metal cooled fast breeder reactors (LMR's). In fact it may act as a bridge between the advantages and disadvantages associated with the two extremes of fuel systems (i.e. ceramic fuel and metallic fuel) for fast reactors. At Bhabha Atomic Research Centre (BARC), R & D efforts are on to develop this CERMET fuel by powder metallurgy route. This paper describes the development of flow sheet for preparation of UO2 dispersed in uranium metal matrix pellets for three different compositions i.e. U-20 wt%UO2, U-25 wt%UO2 and U-30 wt%UO2. It was found that the sintered pellets were having excellent integrity and their linear mass was higher than that of carbide fuel pellets used in Fast Breeder Test Reactor programme (FBTR) in India. The pellets were characterized by X-ray diffraction (XRD) technique for phase analysis and lattice parameter determination. The optical microstructures were developed and reported for all the three different U-UO2 compositions.

  2. Controlled atmosphere for fabrication of cermet electrodes

    Science.gov (United States)

    Ray, Siba P.; Woods, Robert W.

    1998-01-01

    A process for making an inert electrode composite wherein a metal oxide and a metal are reacted in a gaseous atmosphere at an elevated temperature of at least about 750.degree. C. The metal oxide is at least one of the nickel, iron, tin, zinc and zirconium oxides and the metal is copper, silver, a mixture of copper and silver or a copper-silver alloy. The gaseous atmosphere has an oxygen content that is controlled at about 5-3000 ppm in order to obtain a desired composition in the resulting composite.

  3. Fracture Strength of Aged Monolithic and Bilayer Zirconia-Based Crowns

    Directory of Open Access Journals (Sweden)

    Deborah Pacheco Lameira

    2015-01-01

    Full Text Available The purpose of this study was to evaluate the effect of design and surface finishing on fracture strength of yttria-tetragonal zirconia polycrystal (Y-TZP crowns in monolithic (1.5 mm thickness and bilayer (0.8 mm zirconia coping and 0.7 mm porcelain veneer configuration after artificial aging. Bovine incisors received crown preparation and Y-TZP crowns were manufactured using CAD/CAM technique, according to the following groups (n=10: Polished monolithic zirconia crowns (PM; Glazed monolithic zirconia crowns (GM; Bi-layer crowns (BL. Crowns were cemented with resin cement, submitted to artificial aging in a chewing simulator (2.5 million cycles/80 N/artificial saliva/37°C, and tested for fracture strength. Two remaining crowns referring to PM and GM groups were submitted to a chemical composition analysis to measure the level of yttrium after aging. One-way ANOVA and Tukey’s test (P=.05 indicated that monolithic zirconia crowns presented similar fracture strength (PM=3476.2 N ± 791.7; GM=3561.5 N ± 991.6, which was higher than bilayer crowns (2060.4 N ± 810.6. There was no difference in the yttrium content among the three surfaces evaluated in the monolithic crowns. Thus, monolithic zirconia crowns present higher fracture strength than bilayer veneered zirconia after artificial aging and surface finishing does not affect their fracture strength.

  4. Thermal barrier coating by electron beam-physical vapor deposition of zirconia co-doped with yttria and niobia

    Directory of Open Access Journals (Sweden)

    Daniel Soares de Almeida

    2010-08-01

    Full Text Available The most usual ceramic material for coating turbine blades is yttria doped zirconia. Addition of niobia, as a co-dopant in the Y2O3-ZrO2 system, can reduce the thermal conductivity and improve mechanical properties of the coating. The purpose of this work was to evaluate the influence of the addition of niobia on the microstructure and thermal properties of the ceramic coatings. SEM on coatings fractured cross-section shows a columnar structure and the results of XRD show only zirconia tetragonal phase in the ceramic coating for the chemical composition range studied. As the difference NbO2,5-YO1,5 mol percent increases, the tetragonality increases. A significant reduction of the thermal conductivity, measured by laser flash technique in the zirconia coating co-doped with yttria and niobia when compared with zirconia-yttria coating was observed.

  5. Improvement of mechanical properties of zirconia-toughened alumina by sinter forging

    NARCIS (Netherlands)

    He, Y.; Winnubst, Aloysius J.A.; Verweij, H.; Burggraaf, Anthonie; Burggraaf, A.J.

    1994-01-01

    ZTA powder with a composition of 85 wt% alumina/15 wt% zirconia was prepared by a gel precipitation method. Sinter forging was performed with this powder to enhance the mechanical properties of ZTA materials. The influence of processing flaws on mechanical properties of sinter forged materials and

  6. Modern trends in engineering ceramics: review of transformation toughening in zirconia based ceramics

    International Nuclear Information System (INIS)

    Khan, A.A.

    1998-01-01

    The investigation of zirconia has continued to attract the interest of ever increasing number of scientists and solid evidence of commercial applications for the engineering ceramic is now available. To use zirconia to its full potential, the properties of the oxide have been modified extensively by the addition of cubic stabilizing oxides. These can be added in amounts sufficient to form a partially stabilized zirconia (PSZ) or to form a fully stabilized zirconia, which has a cubic structure at room temperature. The addition of varying amounts of cubic oxides, particularly MgO, CaO, Y sub 2 O sub 3, has allowed the development of novel and innovative ceramic materials. In this article an overview of the recent advances in zirconia based engineering materials is presented. It is shown that intelligent control of the composition and microstructure can lead the the production of extremely though ceramic materials, a property which is generally thought to be the major weak point of ceramics vis a vis other class of materials. (author)

  7. Effects of framework design and layering material on fracture strength of implant-supported zirconia-based molar crowns.

    Science.gov (United States)

    Kamio, Shingo; Komine, Futoshi; Taguchi, Kohei; Iwasaki, Taro; Blatz, Markus B; Matsumura, Hideo

    2015-12-01

    To evaluate the effects of framework design and layering material on the fracture strength of implant-supported zirconia-based molar crowns. Sixty-six titanium abutments (GingiHue Post) were tightened onto dental implants (Implant Lab Analog). These abutment-implant complexes were randomly divided into three groups (n = 22) according to the design of the zirconia framework (Katana), namely, uniform-thickness (UNI), anatomic (ANA), and supported anatomic (SUP) designs. The specimens in each design group were further divided into two subgroups (n = 11): zirconia-based all-ceramic restorations (ZAC group) and zirconia-based restorations with an indirect composite material (Estenia C&B) layered onto the zirconia framework (ZIC group). All crowns were cemented on implant abutments, after which the specimens were tested for fracture resistance. The data were analyzed with the Kruskal-Wallis test and the Mann-Whitney U-test with the Bonferroni correction (α = 0.05). The following mean fracture strength values (kN) were obtained in UNI design, ANA design, and SUP design, respectively: Group ZAC, 3.78, 6.01, 6.50 and Group ZIC, 3.15, 5.65, 5.83. In both the ZAC and ZIC groups, fracture strength was significantly lower for the UNI design than the other two framework designs (P = 0.001). Fracture strength did not significantly differ (P > 0.420) between identical framework designs in the ZAC and ZIC groups. A framework design with standardized layer thickness and adequate support of veneer by zirconia frameworks, as in the ANA and SUP designs, increases fracture resistance in implant-supported zirconia-based restorations under conditions of chewing attrition. Indirect composite material and porcelain perform similarly as layering materials on zirconia frameworks. © 2014 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

  8. Effect of the shades of background substructures on the overall color of zirconia-based all-ceramic crowns

    Science.gov (United States)

    Tulapornchai, Chantana; Mamani, Jatuphol; Kamchatphai, Wannaporn; Thongpun, Noparat

    2013-01-01

    PURPOSE The objective of this study was to determine the effect of the color of a background substructure on the overall color of a zirconia-based all-ceramic crown. MATERIALS AND METHODS Twenty one posterior zirconia crowns were made for twenty subjects. Seven premolar crowns and six molar crowns were cemented onto abutments with metal post and core in the first and second group. In the third group, eight molar crowns were cemented onto abutments with a prefabricated post and composite core build-up. The color measurements of all-ceramic crowns were made before try-in, before and after cementation. A repeated measure ANOVA was used for a statistical analysis of a color change of all-ceramic crowns at α=.05. Twenty four zirconia specimens, with different core thicknesses (0.4-1 mm) were also prepared to obtain the contrast ratio of zirconia materials after veneering. RESULTS L*, a*, and b* values of all-ceramic crowns cemented either on a metal cast post and core or on a prefabricated post did not show significant changes (P>.05). However, the slight color changes of zirconia crowns were detected and represented by ΔE*ab values, ranging from 1.2 to 3.1. The contrast ratios of zirconia specimens were 0.92-0.95 after veneering. CONCLUSION No significant differences were observed between the L*, a*, and b* values of zirconia crowns cemented either on a metal cast post and core or a prefabricated post and composite core. However, the color of a background substructure could affect the overall color of posterior zirconia restorations with clinically recommended core thickness according to ΔE*ab values. PMID:24049574

  9. Microscopic mechanism of stability in yttria-doped zirconia

    CERN Document Server

    Ostanin, S A

    2001-01-01

    The relaxed configurations of yttria-stabilized zirconia (YSZ) between 3 and 10 mol. % Y sub 2 O sub 3 were modeled within the pseudopotential technique. The vibration mode corresponding to the soft phonon in pure c-ZrO sub 2 has been calculated for each Y sub 2 O sub 3 composition. These anharmonic vibrations, associated with stabilization of YSZ, have been investigated within the self-consistent phonon approximation that makes obtainable the fine structure in spectral density. In studying the phonon dynamics, it is proposed to use the displacement probability density which can quantify very accurately the transition temperature needed to stabilize the YSZ cubic phase

  10. Microstructure and durability of zirconia thermal barrier coatings

    International Nuclear Information System (INIS)

    Suhr, D.S.; Mitchell, T.E.; Keller, R.J.

    1983-01-01

    Various combinations of plasma-sprayed bond coatings and zirconia ceramic coatings on a nickel-based superalloy substrate were tested by static thermal exposure at 1200 0 C and cyclic thermal exposure to 1000 0 C. The bond coats were based on Ni-Cr-Al alloys with additions of rare earth elements and Si. The ceramic coats were various ZrO 2 -Y 2 O 3 compositions, of which the optimum was found to be ZrO 2 -8.9 wt% Y 2 O 3 . Microstructural analysis showed that resistance to cracking during thermal exposure is strongly related to deleterious phase changes

  11. Effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations: in vitro study of color masking ability.

    Science.gov (United States)

    Oh, Seon-Hee; Kim, Seok-Gyu

    2015-10-01

    The aim of the study was to evaluate the effect of abutment shade, ceramic thickness, and coping type on the final shade of zirconia all-ceramic restorations. Three different types of disk-shaped zirconia coping specimens (Lava, Cercon, Zirkonzahn: ø10 mm × 0.4 mm) were fabricated and veneered with IPS e.max Press Ceram (shade A2), for total thicknesses of 1 and 1.5 mm. A total of sixty zirconia restoration specimens were divided into six groups based on their coping types and thicknesses. The abutment specimens (ø10 mm × 7 mm) were prepared with gold alloy, base metal (nickel-chromium) alloy, and four different shades (A1, A2, A3, A4) of composite resins. The average L*, a*, b* values of the zirconia specimens on the six abutment specimens were measured with a dental colorimeter, and the statistical significance in the effects of three variables was analyzed by using repeated measures analysis of variance (α=.05).The average shade difference (ΔE) values of the zirconia specimens between the A2 composite resin abutment and other abutments were also evaluated. The effects of zirconia specimen thickness (Pabutment shade (Pabutments was higher (close to the acceptability threshold of 5.5 ΔE) than th ose between the A2 composite resin and other abutments. This in-vitro study demonstrated that abutment shade, ceramic thickness, and coping type affected the resulting shade of zirconia restorations.

  12. The promise and challenges of cermet fueled nuclear thermal propulsion reactors

    International Nuclear Information System (INIS)

    Brengle, R.G.; Harty, R.B.; Bhattacharyya, S.K.

    1993-06-01

    The use of cermet fuels in nuclear thermal propulsion systems was examined and the characteristics of systems using these fuel forms is discussed in terms of current mission and safety requirements. For use at high temperatures cermet fueled reactors utilize ceramic fuels with refractory metals as the matrix material. Cermet fueled reactors tend to be heavy when compared to concepts that utilize graphite as the fuel matrix because of the high density of the refractory metal matrix which makes up 20-40 percent of the total volume. On the positive side the metal matrix is strong and more resistant to loads from either the launch or flow induced vibration. The compatibility of the tungsten cermet with hydrogen is excellent and lifetimes of several hours is certainly achievable. Probably the biggest drawback to cermet nuclear thermal propulsion concepts is that the amount of actual data to support the theoretical conclusions is small. In fact there is no data under representative conditions of temperature, propellant and flux for the required fuel burnup. Although cermet systems appear to be attractive, the lack of fuel data at representative conditions does not allow reliable comparisons of cermet systems to systems where fuel data is available. 10 refs

  13. Tungstophosphoric acid supported onto hydrous zirconia ...

    Indian Academy of Sciences (India)

    Unknown

    Hydrous zirconia; heteropolyacid; morphology; particle size; acidity. 1. Introduction. Catalysis by .... chemisorbed on the sample in every pulse was detected by a thermal ..... qualitative organic analysis (New York: Longman), Ch. 3,. 4th ed.

  14. [Cermet cements for milk tooth fillings. Preliminary results].

    Science.gov (United States)

    Hickel, R; Petschelt, A; Voss, A

    1989-06-01

    106 Ketac-Silver fillings in deciduous molars were reevaluated after 1 to 3.3 years, i.e. 25 month on the average. About 90% of 50 occlusal fillings and about 84% of 56 multisurface restorations were unchanged. Without claiming statistical evidence for their conclusiveness, we consider these results as an indication that cermet cements are a useful alternative to amalgam fillings in deciduous teeth, particularly since the life of these fillings is limited to the time until the milk tooth is physiologically lost.

  15. Coating with overlay metallic-cermet alloy systems

    Science.gov (United States)

    Gedwill, M. A.; Levine, S. R.; Glasgow, T. K. (Inventor)

    1984-01-01

    A base layer of an oxide dispersed, metallic alloy (cermet) is arc plasma sprayed onto a substrate, such as a turbine blade, vane, or the like, which is subjected to high temperature use. A top layer of an oxidation, hot corrosion, erosion resistant alloy of nickel, cobalt, or iron is then arc plasma sprayed onto the base layer. A heat treatment is used to improve the bonding. The base layer serves as an inhibitor to interdiffusion between the protective top layer and the substrate. Otherwise, the 10 protective top layer would rapidly interact detrimentally with the substrate and degrade by spalling of the protective oxides formed on the outer surface at elevated temperatures.

  16. Electrochemical reduction of CerMet fuels for transmutation using surrogate CeO2-Mo pellets

    Science.gov (United States)

    Claux, B.; Souček, P.; Malmbeck, R.; Rodrigues, A.; Glatz, J.-P.

    2017-08-01

    One of the concepts chosen for the transmutation of minor actinides in Accelerator Driven Systems or fast reactors proposes the use of fuels and targets containing minor actinides oxides embedded in an inert matrix either composed of molybdenum metal (CerMet fuel) or of ceramic magnesium oxide (CerCer fuel). Since the sufficient transmutation cannot be achieved in a single step, it requires multi-recycling of the fuel including recovery of the not transmuted minor actinides. In the present work, a pyrochemical process for treatment of Mo metal inert matrix based CerMet fuels is studied, particularly the electroreduction in molten chloride salt as a head-end step required prior the main separation process. At the initial stage, different inactive pellets simulating the fuel containing CeO2 as minor actinide surrogates were examined. The main studied parameters of the process efficiency were the porosity and composition of the pellets and the process parameters as current density and passed charge. The results indicated the feasibility of the process, gave insight into its limiting parameters and defined the parameters for the future experiment on minor actinide containing material.

  17. Fluency over the monoclinic zirconia indentation

    International Nuclear Information System (INIS)

    Pereira, A.S.; Jornada, J.A.H. da

    1992-01-01

    It was investigated the environment and the time dependence of the Vickers microhardness of monoclinic zirconia single-crystals. The samples were kept at room temperature and the identifications were performed for different environments (air, toluene and water). An indentation creep process was observed for the samples indented is moist media, indicating for a water activated plastic relaxation mechanism. The possible influence of such effect in the fatigue and phase transformations mechanisms of zirconia based ceramics is discussed. (author)

  18. Precipitation in partially stabilized zirconia

    International Nuclear Information System (INIS)

    Bansal, G.K.

    1975-01-01

    Transmission electron microscopy was used to study the substructure of partially stabilized ZrO 2 (PSZ) samples, i.e., 2-phase systems containing both cubic and monoclinic modifications of zirconia, after various heat treatments. Monoclinic ZrO 2 exists as (1) isolated grains within the polycrystalline aggregate (a grain- boundary phase) and (2) small plate-like particles within cubic grains. These intragranular precipitates are believed to contribute to the useful properties of PSZ via a form of precipitation hardening. These precipitates initially form as tetragonal ZrO 2 , with a habit plane parallel to the brace 100 brace matrix planes. The orientation relations between the tetragonal precipitates and the cubic matrix are brace 100 brace/sub matrix/ 2 parallel brace 100 brace /sub precipitate/ or (001)/sub precipitate/ and broken bracket 100 broken bracket/sub matrix/ 2 parallel broken bracket 100 broken bracket/sub precipitate/ or [001]/sub precipitate/. (U.S.)

  19. Surface treatment of zirconia ceramics

    International Nuclear Information System (INIS)

    1980-01-01

    A method of chemically micropitting and/or microcratering at least a portion of a smooth surface of an impervious zirconia-base ceramic is described, comprising (a) contacting the smooth surface with a liquid leachant selected from concentrated sulphuric acid, ammonium bisulphate, alkali metal bisulphates and mixtures thereof at a temperature of at least 250 0 C for a period of time sufficient to effect micropitting and/or microcratering generally uniformly distributed throughout the microstructure of the resultant leached surface; (b) removing the leached surface from contact with the leachant; (c) contacting the leached surface with hydrochloric acid to effect removal from the leached surface of a residue thereon comprising sulphate of metal elements including zirconium in the ceramic; (d) removing the leached surface from contact with the hydrochloric acid; and (e) rinsing the leached surface with water to effect removal of acid residue from that surface. (author)

  20. An overview of monolithic zirconia in dentistry

    Directory of Open Access Journals (Sweden)

    Özlem Malkondu

    2016-07-01

    Full Text Available Zirconia restorations have been used successfully for years in dentistry owing to their biocompatibility and good mechanical properties. Because of their lack of translucency, zirconia cores are generally veneered with porcelain, which makes restorations weaker due to failure of the adhesion between the two materials. In recent years, all-ceramic zirconia restorations have been introduced in the dental sector with the intent to solve this problem. Besides the elimination of chipping, the reduced occlusal space requirement seems to be a clear advantage of monolithic zirconia restorations. However, scientific evidence is needed to recommend this relatively new application for clinical use. This mini-review discusses the current scientific literature on monolithic zirconia restorations. The results of in vitro studies suggested that monolithic zirconia may be the best choice for posterior fixed partial dentures in the presence of high occlusal loads and minimal occlusal restoration space. The results should be supported with much more in vitro and particularly in vivo studies to obtain a final conclusion.

  1. A Historical Review of Cermet Fuel Development and the Engine Performance Implications

    Science.gov (United States)

    Stewart, Mark E.

    2015-01-01

    To better understand Cermet engine performance, examined historical material development reports two issues: High vaporization rate of UO2, High temperature chemical stability of UO2. Cladding and chemical stabilizers each result in large, order of magnitude improvements in high temperature performance. Few samples were tested above 2770 K. Results above 2770 K are ambiguous. Contemporary testing may clarify performance. Cermet sample testing during the NERVA Rover era. Important properties, melting temperature, vaporization rate, strength, Brittle-to-Ductile Transition, cermet sample test results, engine performance, location, peak temperature.

  2. Micro-scale mechanical characterization of Inconel cermet coatings deposited by laser cladding

    OpenAIRE

    Chao Chang; Davide Verdi; Miguel Angel Garrido; Jesus Ruiz-Hervias

    2016-01-01

    In this study, an Inconel 625-Cr3C2 cermet coating was deposited on a steel alloy by laser cladding. The elastic and plastic mechanical properties of the cermet matrix were studied by the depth sensing indentation (DSI) in the micro scale. These results were compared with those obtained from an Inconel 600 bulk specimen. The values of Young's modulus and hardness of cermet matrix were higher than those of an Inconel 600 bulk specimen. Meanwhile, the indentation stress–strain curve of the cerm...

  3. Study of Some Innovant Reactors without on- Site Refueling with Triso and Cermet Fuel

    OpenAIRE

    A.Chetaine; A. Benchrif; H. Amsil; V. Kuznetsov; Y. Shimazu

    2012-01-01

    The evaluation of unit cell neutronic parameters and lifetime for some innovant reactors without on sit-refuling will be held in this work. the behavior of some small and medium reactors without on site refueling with triso and cermet fuel. For the FBNR long life except we propose to change the enrichment of the Cermet MFE to 9%. For the AFPR reactor we can see that the use of the Cermet MFE can extend the life of this reactor but to maintain the same life period for AFPR...

  4. Cermet fuel for fast reactor – Fabrication and characterization

    Energy Technology Data Exchange (ETDEWEB)

    Mishra, Sudhir, E-mail: sudhir@barc.gov.in [Radiometallurgy Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400 085 (India); Kutty, P.S.; Kutty, T.R.G. [Radiometallurgy Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400 085 (India); Das, Shantanu [Uranium Extraction Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400 085 (India); Dey, G.K. [Materials Science Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400 085 (India); Kumar, Arun [Radiometallurgy Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400 085 (India)

    2013-11-15

    (U, Pu)O{sub 2} ceramic fuel is the well-established fuel for the fast reactors and (U, Pu, Zr) metallic fuel is the future fuel. Both the fuels have their own merits and demerits. Optimal solution may lie in opting for a fuel which combines the favorable features of both fuel systems. The choice may be the use of cermet fuel which can be either (U, PuO{sub 2}) or (Enriched U, UO{sub 2}). In the present study, attempt has been made to fabricate (Natural U, UO{sub 2}) cermet fuel by powder metallurgy route. Characterization of the fuel has been carried out using dilatometer, differential thermal analyzer, X-ray diffractometer, and Scanning Electron Microscope. The results show a high solidus temperature, high thermal expansion, presence of porosities, etc. in the fuel. The thermal conductivity of the fuel has also been measured. X-ray diffraction study on the fuel compact reveals presence of α U and UO{sub 2} phases in the matrix of the fuel.

  5. Bond strength of resin cement to CO2 and Er:YAG laser-treated zirconia ceramic

    Directory of Open Access Journals (Sweden)

    Shahin Kasraei

    2014-11-01

    Full Text Available Objectives It is difficult to achieve adhesion between resin cement and zirconia ceramics using routine surface preparation methods. The aim of this study was to evaluate the effects of CO2 and Er:YAG laser treatment on the bond strength of resin cement to zirconia ceramics. Materials and Methods In this in-vitro study 45 zirconia disks (6 mm in diameter and 2 mm in thickness were assigned to 3 groups (n = 15. In control group (CNT no laser treatment was used. In groups COL and EYL, CO2 and Er:YAG lasers were used for pretreatment of zirconia surface, respectively. Composite resin disks were cemented on zirconia disk using dual-curing resin cement. Shear bond strength tests were performed at a crosshead speed of 0.5 mm/min after 24 hr distilled water storage. Data were analyzed by one-way ANOVA and post hoc Tukey's HSD tests. Results The means and standard deviations of shear bond strength values in the EYL, COL and CNT groups were 8.65 ± 1.75, 12.12 ± 3.02, and 5.97 ± 1.14 MPa, respectively. Data showed that application of CO2 and Er:YAG lasers resulted in a significant higher shear bond strength of resin cement to zirconia ceramics (p < 0.0001. The highest bond strength was recorded in the COL group (p < 0.0001. In the CNT group all the failures were adhesive. However, in the laser groups, 80% of the failures were of the adhesive type. Conclusions Pretreatment of zirconia ceramic via CO2 and Er:YAG laser improves the bond strength of resin cement to zirconia ceramic, with higher bond strength values in the CO2 laser treated samples.

  6. Analysis of factors affecting failure of glass cermet tunnel restorations in a multi-center study.

    Science.gov (United States)

    Pilebro, C E; van Dijken, J W

    2001-06-01

    The aim of this study was to analyze factors influencing the failures of tunnel restorations performed with a glass cermet cement (Ketac Silver). Caries activity, lesion size, tunnel cavity opening size, partial or total tunnel, composite lamination or operating time showed no significant correlation to failure rate. Twelve dentists in eight clinics clinically experienced and familiar with the tunnel technique placed 374 restorations. The occlusal sections of fifty percent of the restorations were laminated with hybrid resin composite. The results of the yearly clinical and radiographic evaluations over the course of 3 years were correlated to factors that could influence the failure rate using logistic regression analysis. At the 3-year recall a cumulative number of 305 restorations were available. The cumulative replacement rate was 20%. The main reasons for replacement were marginal ridge fracture (14%) and dentin caries (3%). Another 7% of the restorations which had not been replaced were classified as failures because of untreated dentin caries. The only significant variable observed was the individual failure rate of the participating dentists varying between 9 and 50% (p=0.013).

  7. The Effect of Zirconia in Hydroxyapatite on Staphylococcus epidermidis Growth

    Directory of Open Access Journals (Sweden)

    Widowati Siswomihardjo

    2012-01-01

    . Conclusion. The addition of zirconia into hydroxyapatite affected the growth of S. epidermidis. Hydroxyapatite with 20% zirconia proved to be an effective concentration to inhibit the growth of S. epidermidis colony.

  8. Microstructural characterization of cermet-steel interface in rock drilling tool

    International Nuclear Information System (INIS)

    Ybarra, L.A.C.; Molisani, A.L.; Yoshimura, H.N.

    2010-01-01

    Rock drilling tools basically present a WC cermet bonded to a steel shank. The interface cermet-steel plays fundamental role during drilling operation, since the fracture of this interface is the main failure mode of the tools. In this work, the microstructure of this interface in crown samples (type A), prepared in an industrial like process, was evaluated. In this process, a WC-containing powder was infiltrated with a copper alloy at 1100 deg C in a graphite mold previously mounted with a 1020 steel tube. The powder was characterized by XRD analysis and the cross-section microstructure of cermet-steel was analyzed using SEM-EDS. It was observed that Ni and small amount of Cu from cermet matrix diffused into the superficial region of the steel, and the Cu alloy dissolved and penetrated along the steel grain boundaries, resulting in good metallurgical bonding of the interface.(author)

  9. Experimental Evaluation of Cermet Turbine Stator Blades for Use at Elevated Gas Temperatures

    Science.gov (United States)

    Chiarito, Patrick T.; Johnston, James R.

    1959-01-01

    The suitability of cermets for turbine stator blades of a modified turbojet engine was determined at an average turbine-inlet-gas temperature of 2000 F. Such an increase in temperature would yield a premium in thrust from a service engine. Because the cermet blades require no cooling, all the available compressor bleed air could be used to cool a turbine made from conventional ductile alloys. Cermet blades were first run in 100-hour endurance tests at normal gas temperatures in order to evaluate two methods for mounting them. The elevated gas-temperature test was then run using the method of support considered best for high-temperature operation. After 52 hours at 2000 F, one of the group of four cermet blades fractured probably because of end loads resulting from thermal distortion of the spacer band of the nozzle diaphragm. Improved design of a service engine would preclude this cause of premature failure.

  10. The Influence of Sintering Temperature of Reactive Sintered (Ti, MoC-Ni Cermets

    Directory of Open Access Journals (Sweden)

    Marek Jõeleht

    2015-09-01

    Full Text Available Titanium-molybdenum carbide nickel cermets ((Ti, MoC-Ni were produced using high energy milling and reactive sintering process. Compared to conventional TiC-NiMo cermet sintering the parameters for reactive sintered cermets vary since additional processes are present such as carbide synthesis. Therefore, it is essential to acquire information about the suitable sintering regime for reactive sintered cermets. One of the key parameters is the final sintering temperature when the liquid binder Ni forms the final matrix and vacancies inside the material are removed. The influence of the final sintering temperature is analyzed by scanning electron microscopy. Mechanical properties of the material are characterized by transverse rupture strength, hardness and fracture toughness.DOI: http://dx.doi.org/10.5755/j01.ms.21.3.7179

  11. Computer simulation of the optical properties of high-temperature cermet solar selective coatings

    Energy Technology Data Exchange (ETDEWEB)

    Nejati, M. Reza [K.N. Toosi Univ. of Technology, Dept. of Mechanical Engineering, Tehran (Iran); Fathollahi, V.; Asadi, M. Khalaji [AEOI, Center for Renewable Energy Research and Applications (CRERA), Tehran (Iran)

    2005-02-01

    A computer simulation is developed to calculate the solar absorptance and thermal emittance of various configurations of cermet solar selective coatings. Special attention has been paid to those material combinations, which are commonly used in high-temperature solar thermal applications. Moreover, other material combinations such as two-, three- and four-cermet-layer structures as solar selective coatings have been theoretically analyzed by computer simulation using three distinct physical models of Ping Sheng, Maxwell-Garnett and Bruggeman. The novel case of two-cermet-layer structure with different cermet components has also been investigated. The results were optimized by allowing the program to manipulate the metal volume fraction and thickness of each layer and the results compared to choose the best possible configuration. The calculated results are within the range of 0.91-0.97 for solar absorptance and 0.02-0.07 for thermal emittance at room temperature. (Author)

  12. Properties of U sub 3 O sub 8 -aluminum cermet fuel

    Energy Technology Data Exchange (ETDEWEB)

    Peacock, H.B.

    1989-10-01

    Nuclear fuel elements containing U{sub 3}O{sub 8} dispersed in an aluminum matrix have been used in research and test reactors for about 30 years. These elements, sometimes called cermet fuel, are made by powder metallurgical methods (PM) and can accommodate up to approximately 50 wt % uranium in the core section of extruded tubes. Cermet fuel elements have been fabricated and irradiated at the Savannah River Site (SRS). Irradiation behavior is excellent. Extruded tubes with up to 50 wt % uranium have been successfully irradiated to fission densities of about 2 {times} 10{sup 21} fissions per cc of core. Physical, mechanical, and chemical properties of cermet fuels are assembled into a reference document. Results will be used by Argonne National Laboratory to design cermet fuel elements for possible use in the New Production Reactor at SRS. 57 refs., 33 figs., 12 tabs.

  13. Cermet based metamaterials for multi band absorbers over NIR to LWIR frequencies

    International Nuclear Information System (INIS)

    Pradhan, Jitendra K; Behera, Gangadhar; Anantha Ramakrishna, S; Agarwal, Amit K; Ghosh, Amitava

    2017-01-01

    Cermets or ceramic-metals are known for their use in solar thermal technologies for their absorption across the solar band. Use of cermet layers in a metamaterial perfect absorber allows for flexible control of infra-red absorption over the short wave infra-red, to long wave infra-red bands, while keeping the visible/near infra-red absorption properties constant. We design multilayered metamaterials consisting of a conducting ground plane, a low metal volume fraction cermet/ZnS as dielectric spacer layers, and a top structured layer of an array of circular discs of metal/high volume metal fraction cermet that give rise to specified absorption bands in the near-infra-red (NIR) frequencies, as well as any specified band at SWIR–LWIR frequencies. Thus, a complete decoupling of the absorption at optical/NIR frequencies and the infra-red absorption behaviour of a structured metamaterial is demonstrated. (paper)

  14. Reverse martensitic transformation in alumina-15 vol% zirconia nanostructured powder synthesized by high energy ball milling

    Energy Technology Data Exchange (ETDEWEB)

    Maneshian, M.H. [Department of Materials Science and Engineering, Sharif University of Technology, Azadi Avenue, P.O. Box 11365-9466, Tehran (Iran, Islamic Republic of)], E-mail: mh_maneshian@yahoo.com; Banerjee, M.K. [National Institute of Foundry and Forge Technology, Hatia, Ranchi 834003 (India)

    2008-07-14

    In the present work, three alumina-15 vol% zirconia composites with Y{sub 2}O{sub 3}, MgO as dopants and without oxide as dopant have been investigated. High energy ball milling (HEBM) provides the positive thermodynamic driving force for monoclinic to tetragonal transformation and it reduces starting temperature for the reverse martensitic transformation, meanwhile mobility of zirconium cations and oxygen anions are enhanced in zirconia by HEBM. The general, albeit heuristic, reasoning is corroborated by nanocrystallity, particle size and also the retained monoclinic seem to play an important role. After 10 h HEBM, approximately 28% zirconia tetragonal phase is achieved. Non-stoichiometric tetragonal zirconia phase; Zr{sub 0.95}O{sub 2} is seen to have been achieved by high energy ball milling (HEBM). The structural and compositional evolutions during HEBM have been investigated using X-ray diffraction method (XRD) and scanning electron microscopy (SEM). High resolution transmission electron microscope (TEM) is also used for further understanding about the phenomenological changes taking place during high energy ball milling.

  15. Initial Bacterial Adhesion on Different Yttria-Stabilized Tetragonal Zirconia Implant Surfaces in Vitro

    Directory of Open Access Journals (Sweden)

    Lamprini Karygianni

    2013-12-01

    Full Text Available Bacterial adhesion to implant biomaterials constitutes a virulence factor leading to biofilm formation, infection and treatment failure. The aim of this study was to examine the initial bacterial adhesion on different implant materials in vitro. Four implant biomaterials were incubated with Enterococcus faecalis, Staphylococcus aureus and Candida albicans for 2 h: 3 mol % yttria-stabilized tetragonal zirconia polycrystal surface (B1a, B1a with zirconium oxide (ZrO2 coating (B2a, B1a with zirconia-based composite coating (B1b and B1a with zirconia-based composite and ZrO2 coatings (B2b. Bovine enamel slabs (BES served as control. The adherent microorganisms were quantified and visualized using scanning electron microscopy (SEM; DAPI and live/dead staining. The lowest bacterial count of E. faecalis was detected on BES and the highest on B1a. The fewest vital C. albicans strains (42.22% were detected on B2a surfaces, while most E. faecalis and S. aureus strains (approximately 80% were vital overall. Compared to BES; coated and uncoated zirconia substrata exhibited no anti-adhesive properties. Further improvement of the material surface characteristics is essential.

  16. Numerical Simulation of Brazing TiC Cermet to Iron with TiZrNiCu Filler Metal

    Institute of Scientific and Technical Information of China (English)

    Lixia ZHANG; Jicai FENG

    2004-01-01

    The maximum thermal stress and stress concentration zones of iron/TiC cermet joint during cooling were studied in this paper. The results showed that the shear stress on iron/TiC cermet joint concentrates on the interface tip and the maximum shear stress appears on the left tip of iron/TiZrNiCu interlace. Positive tensile stress on TiC cermet undersurface concentrates on both sides of TiC cermet and its value decreases during cooling. Negative tensile stress on TiC cermet undersurface concentrates on the center of TiC cermet and its value increases during cooling. Brazing temperature has little effect on the development and maximum thermal stress.

  17. Fabrication of porous zirconia using filter paper template

    International Nuclear Information System (INIS)

    Deng Yuhua; Wei Pan

    2005-01-01

    In this work, porous zirconia ceramic was synthesized using filter papers as a template. Special attention is paid to whether the structural of the filter paper can be transferred to the zirconia structure. Microstructure of so synthesized porous zirconia was observed with SEM and the phase was determined by XRD. The surface area and the pore were investigated with an automatic volumetric sorption analyzer. It has been found that the morphology of the template transmit to the porous zirconia quite well. (orig.)

  18. The preparation of titanium-vanadium carbide/nickel cermets. Technical report

    International Nuclear Information System (INIS)

    Precht, W.; Sprissler, B.

    1976-01-01

    Titanium/vanadium alloy carbide rods were prepared by a zone melting procedure. Wetting studies were carried out using sections of the fused rods and candidate matrix material. It was established that nickel exhibits excellent wetting of (Ti, V) C, and accordingly cermet blends were prepared and liquid phase sintered. Processing parameters are discussed as well as their effect on the final microstructure. Alternate methods for cermet preparation are offered which use as received titanium carbide and vanadium carbide powders

  19. Magnetic properties of a cermet on the base of Al2O3

    International Nuclear Information System (INIS)

    Tien, C.; Charnaya, E.V.; Gropyanov, V.M.; Mikhailova, I.S.; Wur, C.S.; Abramovich, A.A.

    2000-01-01

    The zero-field-cooled and field-cooled magnetizations, magnetization versus field, and remanent magnetization were measured for a cermet on the base of Al 2 O 3 using a SQUID magnetometer in the temperature range of 2-360 K. It was shown that magnetic properties of the cermet are determined by independent ferromagnetic, paramagnetic and spin-glass contributions. The spin-glass behavior was studied

  20. Processing and microstructural characterization of B4C-Al cermets

    International Nuclear Information System (INIS)

    Halverson, D.C.; Pyzik, A.J.; Aksay, I.A.

    1985-01-01

    Reaction thermodynamics and wetting studies were employed to evaluate boron carbide-aluminum cermets. Wetting phonomenon and interfacial reactions are characterized using ''macroscale'' and ''microscale'' techniques. Macroscale evaluation involved aluminium sessile drop studies on boron carbide substrates. Microscale evaluation involved the fabrication of actural cermet microstructures and their characterization through sem, x-ray diffraction, metallography, and electron microprobe. Contact-angle measurements and interfacial-reaction products are reported

  1. Microstructure analysis and wear behavior of titanium cermet femoral head with hard TiC layer.

    Science.gov (United States)

    Luo, Yong; Ge, Shirong; Liu, Hongtao; Jin, Zhongmin

    2009-12-11

    Titanium cermet was successfully synthesized and formed a thin gradient titanium carbide coating on the surface of Ti6Al4V alloy by using a novel sequential carburization under high temperature, while the titanium cermet femoral head was produced. The titanium cermet phase and surface topography were characterized with X-ray diffraction (XRD) and backscattered electron imaging (BSE). And then the wear behavior of titanium cermet femoral head was investigated by using CUMT II artificial joint hip simulator. The surface characterization indicates that carbon effectively diffused into the titanium alloys and formed a hard TiC layer on the Ti6Al4V alloys surface with a micro-porous structure. The artificial hip joint experimental results show that titanium cermet femoral head could not only improve the wear resistance of artificial femoral head, but also decrease the wear of UHMWPE joint cup. In addition, the carburized titanium alloy femoral head could effectively control the UHMWPE debris distribution, and increase the size of UHMWPE debris. All of the results suggest that titanium cermet is a prospective femoral head material in artificial joint.

  2. High temperature oxidation resistance of (Ti,Ta)(C,N)-based cermets

    International Nuclear Information System (INIS)

    Chicardi, E.; Córdoba, J.M.; Gotor, F.J.

    2016-01-01

    Highlights: • Cermets based on (Ti,Ta)(C,N) were oxidized in air between 800 and 1100 °C for 48 h. • The substitution of Ti by Ta resulted in a high resistance to oxidation. • A protective layer of cobalt titanates at the surface of cermets was observed. • A rutile phase in which some Ti"4"+ are replaced by Ta"5"+ was detected. • This replacement decelerated the oxygen diffusion into the cermets. - Abstract: Cermets based on titanium–tantalum carbonitride were oxidized in static air between 800 °C and 1100 °C for 48 h. The thermogravimetric and microstructural study showed an outstanding reduction in the oxidation of more than 90% when the Ta content was increased. In cermets with low Ta content, the formation of a thin CoO/Co_3O_4 outer layer tends to disappear by reacting with the underlying rutile phase, which emerges at the surface. However, in cermets with higher Ta content, the formation of an external titanate layer, observed even at a low temperature, appears to prevent the oxygen diffusion and the oxidation progression.

  3. Study of behavior of cermet fuel elements on IGR reactor under RIA type accident condition

    International Nuclear Information System (INIS)

    Vasil'ev, Yu.S.; Vurim, A.D.; Koltyshev, S.M.; Pakhnits, V.A.; Tukhvatulin, Sh.T.; Popov, V.V.; Ryzhkov, A.N.

    1996-01-01

    In 1993 December in IGR reactor of Inst. of Atomic Energy of National Nuclear Center of Republic of Kazakstan the second batch of in-pile testing of perspective cermet fuel elements under the condition, simulating RIA type accident was conducted. In the second batch of testing during eight start-ups 10 cermet fuel elements were examined. Among which 8 of monolith type and 2 fuel elements with false jacket beside cladding (FJF), as well as, 6 standard fuel elements of WWER-1000 type reactor with dioxide fuel were tested. 2 fuel elements - cermet and standard were placed into capsule filled with water. To measure energy release for the each start-up two fission monitor and inside core control gauge were placed. In all the start-ups operation mode of IGR was neutron pulse. Power of fuel element kept changing from 151 to 336 k W; energy release was 38-93 kJ/gr m 235 U; maximum temperature of cermet fuel was 1943-2173 K, of dioxide fuel - 1923-2843 K. The testing has demonstrated that operability of cermet fuel elements under reactivity accident condition with pulse width of 0,2 s is, at least, not less that operability of dioxide fuel elements, through advantages of cermet fuel under these conditions are revealed to the least extent

  4. Interfaces study of all-polysaccharide composite films

    Czech Academy of Sciences Publication Activity Database

    Šimkovic, I.; Kelnar, Ivan; Mendichi, R.; Tracz, A.; Filip, J.; Bertók, T.; Kasák, P.

    2018-01-01

    Roč. 72, č. 3 (2018), s. 711-718 ISSN 0366-6352 Institutional support: RVO:61389013 Keywords : all-polysaccharide composites * elemental analysis * film properties study Subject RIV: JI - Composite Materials OBOR OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics Impact factor: 1.258, year: 2016

  5. Translucent zirconia in the ceramic scenario for monolithic restorations: A flexural strength and translucency comparison test.

    Science.gov (United States)

    Carrabba, Michele; Keeling, Andrew J; Aziz, Aziz; Vichi, Alessandro; Fabian Fonzar, Riccardo; Wood, David; Ferrari, Marco

    2017-05-01

    To compare three different compositions of Yttria-Tetragonal Zirconia Polycrystal (Y-TZP) ceramic and a lithium disilicate ceramic in terms of flexural strength and translucency. Three zirconia materials of different composition and translucency, Aadva ST [ST], Aadva EI [EI] and Aadva NT [NT](GC Tech, Leuven, Belgium) were cut with a slow speed diamond saw into beams and tabs in order to obtain, after sintering, dimensions of 1.2×4.0×15.0mm and 15.0×15.0×1.0mm respectively. Blocks of IPS e.max CAD LT were cut and crystallized in the same shapes and dimensions and used as a reference group [LD]. Beams (n=15) were tested in a universal testing machine for three-point bending strength. Critical fracture load was recorded in N, flexural strength (σ in MPa), Weibull modulus (m) and Weibull characteristic strength (σ 0 in MPa) were then calculated. Tabs (n=10) were measured with a spectrophotometer equipped with an integrating sphere. Contrast Ratios were calculated as CR=Yb/Yw. SEM of thermally etched samples coupled with lineal line analysis (n=6) was used to measure the tested zirconia grain size. Data were statistically analyzed. Differences in translucency, flexural strength and grain size were found to be statistically significant. CR increased and flexural strength decreased in the following order ST(σ 1215±190MPa, CR 0.74±0.01)>EI(σ 983±182MPa, CR 0.69±0.01)>NT(σ 539±66MPa, CR 0.65±0.01)>LD (σ 377±39Mpa, CR 0.56±0.02). The average grain size was different for the three zirconia samples with NT(558±38nm)>ST(445±34nm)>EI(284±11nm). The zirconia composition heavily influenced both the flexural strength and the translucency. Different percentages of Yittria and Alumina result in new materials with intermediate properties in between the conventional zirconia and lithium disilicate. Clinical indications for Zirconia Aadva NT should be limited up to three-unit span bridges. Copyright © 2017 Elsevier Ltd. All rights reserved.

  6. Effect of an experimental zirconia-silica coating technique on micro tensile bond strength of zirconia in different priming conditions

    NARCIS (Netherlands)

    Chen, C.; Kleverlaan, C.J.; Feilzer, A.J.

    2012-01-01

    Objectives This study aimed to evaluate the adhesive properties of a MDP-containing resin cement to a colored zirconia ceramic, using an experimental zirconia-silica coating technique with different priming conditions. Methods 18 zirconia ceramic discs (Cercon base colored) were divided into two

  7. Lateral-access Class II restoration using resin-modified glass-ionomer or silver-cermet cement.

    Science.gov (United States)

    Croll, T P

    1995-02-01

    Direct-access preparation of a carious proximal surface is perhaps the most conservative approach to restoration. Physical properties and handling characteristics of silver amalgam and of resin composite and lack of fluoride ion release make these materials unsuitable for direct buccal- or lingual-access proximal restoration. Insufficient strengths and radiolucency of self-hardening glass-ionomer cements preclude their use for Class II restorations. However, glass-ionomer silver-cermet cement and some resin-modified glass-ionomer materials are proving useful for non-stress-bearing Class II restorations and may have applications in preventive dentistry. This article describes lateral-access Class II restoration with modified glass-ionomer cements. Emphasis is placed on careful handling of materials, maintenance of an ideal operative field, and conservation of tooth structure.

  8. Anelasticity and strength in zirconia ceramics

    International Nuclear Information System (INIS)

    Matsuzawa, M.; Horibe, S.; Sakai, J.

    2005-01-01

    Non-elastic strain behavior was investigated for several different zirconia ceramics and a possible mechanism for anelasticity was discussed. Anelastic strain was detected in zirconia ceramics irrespective of the crystallographic phase and its productivity depended on the particular kind of dopant additive. It was found that the anelastic properties could be significantly influenced by the level of oxygen vacancy in the matrix, and that the anelastic strain might be produced by a light shift of ionic species. In order to investigate the effect of anelasticity on mechanical properties on zirconia ceramics, the tensile strength was investigated for a wide range of strain rates. The obviously unique strain rate dependence was observed only in the materials having anelastic properties. It was assumed that anelasticity could be efficient at improving the tensile strength. (orig.)

  9. Microstructural evolution of alumina-zirconia nanocomposites

    International Nuclear Information System (INIS)

    Ojaimi, C.L.; Chinelatto, A.S.A.; Chinelatto, A.L.; Pallone, E.M.J.A.

    2012-01-01

    Ceramic materials have limited use due to their brittleness. The inclusion of nanosized particles in a ceramic matrix, which are called nanocomposites, and ceramic processing control by controlling the grain size and densification can aid in obtaining ceramic products of greater strength and toughness. Studies showed that the zirconia nano inclusions in the matrix of alumina favors an increase in mechanical properties by inhibiting the grain growth of the matrix and not by the mechanism of the transformation toughening phase of zirconia. In this work, the microstructural evolution of alumina nanocomposites containing 15% by volume of nanometric zirconia was studied. From the results it was possible to understand the sintering process of these nanocomposites. (author)

  10. X-ray photoelectron spectroscopy study of the metal/cermet interface

    International Nuclear Information System (INIS)

    Lu Hua; Shen Dianhong; Xue Qikun

    2001-01-01

    Interfacial reactions between aluminium and polycrystalline cermet TiC 0.6 were investigated using x-ray photo-electron spectroscopy, Auger electron spectroscopy and x-ray diffraction. It was found that titanium exists in two chemical states. The carbide and oxide of titanium can be detected simultaneously, and the atomic ratio of Ti:C:O is 5:3:2. This suggests that TiC 0.6 is a Ti-oxycarbide or oxygenated Tic composite: Ti 5 C 3 O 2 (TiO 2 + 4TiC 0.75 ). When Al is deposited in vacuum on the Ti-oxycarbide surface, the active Al atoms react chemically only with TiO 2 at room temperature, but not with TiC 0.75 in Ti-oxycarbide. The reaction products are Al 2 O 3 and the intermetallic compound Al 3 Ti. Annealing the Al/TiC 0.6 interface at 750 degree C, Al reacts also with TiC 0.75 to form a brittle Al 4 C 3 phase

  11. Basic properties of a zirconia based fuel material for LWRs

    International Nuclear Information System (INIS)

    Degueldre, C.; Paratte, J.M.

    1997-01-01

    The properties of zirconia cubic solid solutions doped with yttria, erbia and ceria or thoria are investigated with emphasis on the potential use of this material as inert matrix fuel for plutonium incineration in a light water reactor (LWR). The material is selected on the basis of its neutronic properties. Zr and Y are not neutron absorbers. Among the rare earth elements, Er was identified as a suitable burnable poison. The high density cubic solid solution is stable for a rather large range of compositions and from room temperature up to about 3000 K. Samples irradiated under low and high energy Xe ion irradiation up to a fluence of 1.8.10 16 Xe.cm -2 were investigated by transmission electron microscopy. Low energy (60 keV) Xe ions did not produce amorphization. From the observed bubble formation, swelling values during irradiation at room temperature or at high temperature (925 K) were estimated to be 0.1-0.72% by volume. Furthermore, no amorphization was obtained by Xe irradiation under extreme conditions such as high energy (1.5 MeV) Xe ion irradiation and low temperature (20 K). This confirms the robustness of this material and argues in favour of the selection of a zirconia based material as an advanced nuclear fuel for plutonium incineration. (author) 5 figs., 1 tab., 17 refs

  12. Mechanical and magnetic properties of semi-Heusler/light-metal composites consolidated by spark plasma sintering

    Czech Academy of Sciences Publication Activity Database

    Koller, M.; Chráska, Tomáš; Cinert, Jakub; Heczko, Oleg; Kopeček, Jaromír; Landa, Michal; Mušálek, Radek; Rameš, Michal; Seiner, Hanuš; Stráský, J.; Janeček, M.

    2017-01-01

    Roč. 126, July (2017), s. 351-357 ISSN 0264-1275 R&D Projects: GA ČR GB14-36566G Institutional support: RVO:61389021 ; RVO:68378271 ; RVO:61388998 Keywords : Metal–metal composites * Spark plasma sintering * Light metals * Ferromagnetic alloys * Mechanical properties Subject RIV: JI - Composite Materials; JI - Composite Materials (FZU-D); JI - Composite Materials (UT-L) OBOR OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics (FZU-D); Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics (UT-L) Impact factor: 4.364, year: 2016 https://www.sciencedirect.com/science/ article /pii/S0264127517303842?via%3Dih

  13. High performance W-AIN cermet solar coatings designed by modelling calculations and deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Qi-Chu Zhang [The University of Sydney (Australia). School of Physics; Shen, Y.G. [City University of Hong Kong (Hong Kong). Department of Manufacturing Engineering and Engineering Management

    2004-01-25

    High solar performance W-AIN cermet solar coatings were designed using a numerical computer model and deposited experimentally. In the numerical calculations aluminium oxynitride (AlON) was used as ceramic component. The dielectric functions and then complex refractive index of W-AlON cermet materials were calculated using the Sheng's approximation. The layer thickness and W metal volume fraction were optimised to achieve maximum photo-thermal conversion efficiency for W-AlON cermet solar coatings on an Al reflector with a surface AlON ceramic anti-reflection layer. Optimisation calculations show that the W-AlON cermet solar coatings with two and three cermet layers have nearly identical solar absorptance, emittance and photo-thermal conversion efficiency that are much better than those for films with one cermet layer. The optimised calculated AlON/W-AlON/Al solar coating film with two cermet layers has a high solar absorptance of 0.953 and a low hemispherical emittance of 0.051 at 80{sup o}C for a concentration factor of 2. The AlN/W-AlN/Al solar selective coatings with two cermet layers were deposited using two metal target direct current magnetron sputtering technology. During the deposition of W-AlN cermet layer, both Al and W targets were run simultaneously in a gas mixture of argon and nitrogen. By substrate rotation a multi-sub-layer system consisting of alternating AlN ceramic and W metallic sub-layers was deposited that can be considered as a macro-homogeneous W-AlN cermet layer. A solar absorptance of 0.955 and nearly normal emittance of 0.056 at 80{sup o}C have been achieved for deposited W-AlN cermet solar coatings. (author)

  14. High performance W-AlN cermet solar coatings designed by modelling calculations and deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Qi-Chu [School of Physics, The University of Sydney, Sydney, NSW 2006 (Australia); Shen, Y.G. [Department of Manufacturing Engineering and Engineering Management, City University of Hong Kong (Hong Kong)

    2004-01-25

    High solar performance W-AlN cermet solar coatings were designed using a numerical computer model and deposited experimentally. In the numerical calculations aluminium oxynitride (AlON) was used as ceramic component. The dielectric function and then complex refractive index of W-AlON cermet materials were calculated using the Sheng's approximation. The layer thickness and W metal volume fraction were optimised to achieve maximum photo-thermal conversion efficiency for W-AlON cermet solar coatings on an Al reflector with a surface AlON ceramic anti-reflection layer. Optimisation calculations show that the W-AlON cermet solar coatings with two and three cermet layers have nearly identical solar absorptance, emittance and photo-thermal conversion efficiency that are much better than those for films with one cermet layer. The optimised calculated AlON/W-AlON/Al solar coating film with two cermet layers has a high solar absorptance of 0.953 and a low hemispherical emittance of 0.051 at 80C for a concentration factor of 2. The AlN/W-AlN/Al solar selective coatings with two cermet layers were deposited using two metal target direct current magnetron sputtering technology. During the deposition of W-AlN cermet layer, both Al and W targets were run simultaneously in a gas mixture of argon and nitrogen. By substrate rotation a multi-sub-layer system consisting of alternating AlN ceramic and W metallic sub-layers was deposited that can be considered as a macro-homogeneous W-AlN cermet layer. A solar absorptance of 0.955 and nearly normal emittance of 0.056 at 80C have been achieved for deposited W-AlN cermet solar coatings.

  15. Increase in the thermal strength of the binder phase of Cermets; Steigerung der Warmfestigkeit der Bindephase von Cermets

    Energy Technology Data Exchange (ETDEWEB)

    Grewe, H. [Krupp-Entwicklungszentrum, Bereich Werkstofftechnik, Essen (Germany); Kolaska, H. [Entwicklung Hartstoffe, Krupp Widia GmbH, Essen (Germany)

    1995-05-01

    According to recent investigations, hard metals with a good profile of characteristics can be produced from tungsten carbide with appropriate sintering conditions and with optimized alloying ratios in the Fe-Co-Ni system. The Co binder phase is substituted by a Fe-Co-Ni binder phase, by Co-Ni or Fe-Ni, or by alloys of the Nimonic type. The following analyses were carried out for the sintered HIP state, the quenched state, and the state of maximum magnetic and mechanical hardening: Light microscopy, measurement of the mechanical and technical characteristics, analysis of oxidation characteristics, hot hardness and edge-holding property, investigation of precipitation and hardening processes in the binder phase by a metallurgical analysis, and attempts to describe the kinetics of hardening. (orig./MM) [Deutsch] Neuere Untersuchungsergebnisse ergeben Hinweise, wonach unter Einhaltung bestimmter Sinterbedingungen und nach Optimierung der Legierungsverhaeltnisse im Dreistoffsystem Eisen-Cobalt-Nickel gute Aussichten fuer die Herstellung von Hartmetallen auf Wolframcarbid-Basis mit einem guenstigen Eigenschaftsprofil bestehen. Die uebliche Cobalt-Bindephase wird dabei durch eine Fe-Co-Ni-Bindephase, durch Co-Ni oder Fe-Ni oder durch Legierungen vom Nimonic-Typ substituiert. Aufbauend auf diesen Kenntnissen wurde eine konzeptionelle Modifizierung der Bindephase von Cermets vorgenommen, die auf einer Co-Ni-Legierung basiert und durch die Ausscheidung von intermetallischen Phasen mit moeglichst einfacher Struktur aushaertet. Dabei eilt die magnetische Aushaertung der mechanischen Aushaertung des Cermet-Versuchswerkstoffs voraus. Fuer den Sinter-HIP-Zustand, fuer den Abschreckzustand sowie fuer den Zustand der maximalen magnetischen und der maximalen mechanischen Aushaertung wurden folgende Untersuchungen durchgefuehrt: Lichtmikroskopie Messung der mechanisch-technologischen Eigenschaften, Beurteilung von Oxidationsverhalten, Warmhaerte und Schneidhaltigkeit, Untersuchung

  16. Mesoporous yttria-zirconia and metal-yttria-zirconia solid solutions for fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Mamak, M.; Coombs, N.; Ozin, G. [Toronto Univ., ON (Canada). Dept. of Chemistry

    2000-02-03

    A new class of binary mesoporous yttria-zirconia (YZ) and ternary mesoporous metal-YZ materials (M = electroactive Ni/Pt) is presented here that displays the highest surface area of any known form of yttria-stabilized zirconia. These mesoporous materials form as solid solutions and retain their structural integrity to 800 C, which bodes well for their possible utilization in fuel cells. (orig.)

  17. Using glass-graded zirconia to increase delamination growth resistance in porcelain/zirconia dental structures.

    Science.gov (United States)

    Chai, Herzl; Mieleszko, Adam J; Chu, Stephen J; Zhang, Yu

    2018-01-01

    Porcelain fused to zirconia (PFZ) restorations are widely used in prosthetic dentistry. However, their tendency to delaminate along the P/Z interface remains a practical problem so that assessing and improving the interfacial strength are important design aspects. This work examines the effect of modifying the zirconia veneering surface with an in-house felspathic glass on the interfacial fracture resistance of fused P/Z. Three material systems are studied: porcelain fused to zirconia (control) and porcelain fused to glass-graded zirconia with and without the presence of a glass interlayer. The specimens were loaded in a four-point-bend fixture with the porcelain veneer in tension. The evolution of damage is followed with the aid of a video camera. The interfacial fracture energy G C was determined with the aid of a FEA, taking into account the stress shielding effects due to the presence of adjacent channel cracks. Similarly to a previous study on PFZ specimens, the fracture sequence consisted of unstable growth of channel cracks in the veneer followed by stable cracking along the P/Z interface. However, the value of GC for the graded zirconia was approximately 3 times that of the control zirconia, which is due to the good adhesion between porcelain and the glass network structure on the zirconia surface. Combined with its improved bonding to resin-based cements, increased resistance to surface damage and good esthetic quality, graded zirconia emerges as a viable material concept for dental restorations. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  18. Wear Micro-Mechanisms of Composite WC-Co/Cr - NiCrFeBSiC Coatings. Part I: Dry Sliding

    Directory of Open Access Journals (Sweden)

    D. Kekes

    2014-12-01

    Full Text Available The influence of the cermet fraction in cermet/ metal composite coatings developed by High-Velocity Oxyfuel Flame (HVOF spraying on their tribological behaviour was studied. Five series of coatings, each one containing different proportion of cermet-metal components, prepared by premixing commercially available feedstocks of NiCrFeBSiC metallic and WC-Co/Cr cermet powders were deposited on AISI 304 stainless steel substrate. The microstructure of as-sprayed coatings was characterized by partial decomposition of the WC particles, lamellar morphology and micro-porosity among the solidified splats. Tribological behavior was studied under sliding friction conditions using a Si3N4 ball as counterbody and the friction coefficient and volume loss were determined as a function of the cermet fraction. Microscopic examinations of the wear tracks and relevant cross sections identified the wear mechanisms involved. Coatings containing only the metallic phase were worn out through a combination of ploughing, micro-cracking and splat exfoliation, whilst those containing only the cermet phase primarily by micro-cracking at the individual splat scale. The wear mechanisms of the composite coatings were strongly affected by their randomly stratified structure. In-depth cracks almost perpendicular to the coating/ substrate interface occurring at the wear track boundaries resulted in cermet trans-splat fracture.

  19. Zirconia-based colors for ceramic glazes

    International Nuclear Information System (INIS)

    Eppler, R.A.

    1977-01-01

    The history of color development for use in ceramic glazes is outlined. The most significant modern development is based on zirconia and zircon. These materials have gained increasing acceptance in the industry since their introduction in the late 1950's and early 1960's, due to their superior stability during firing of the glaze

  20. Peculiarities of structural transformations in zirconia nanocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Vasilevskaya, A., E-mail: a.k.vasilevskaya@gmail.com [Technical University, Saint-Petersburg State Institute of Technology (Russian Federation); Almjasheva, O. V. [Saint-Petersburg Electrotechnical University “LETI” (Russian Federation); Gusarov, V. V. [Ioffe Physical-Technical Institute of the Russian Academy of Sciences (Russian Federation)

    2016-07-15

    The transitions of metastable tetragonal phase as well as high-temperature tetragonal phase into the low-temperature monoclinic phase upon heating and cooling were thoroughly studied in zirconia nanoparticles. High-temperature X-ray diffraction, thermal analysis and Raman spectroscopy were used to provide the systematic approach to the investigation of zirconia nanoparticles thermal behavior. A phase transformation sequence in the ZrO{sub 2}–H{sub 2}O system was determined, and the mechanisms of tetragonal-to-monoclinic transition upon heating and cooling were suggested. Here, the phenomenon was found and described, which was determined as “self-powdering” of nanoparticles occurring during structural transition. This phenomenon was observed by in situ investigation of the evolution of crystalline nanoparticles from amorphous zirconium hydroxide during thermal treatment in air. The tetragonal-to-monoclinic phase transition, induced by cooling from the temperature of equilibrium of tetragonal zirconia (i.e., above 1170 °C), is accompanied by a significant crystallite size decrease (with corresponding 3–4 times decrease of crystallite volume). The experimental results facilitate applications of zirconia nanoparticles to obtain high-performance nanopowders for nanoceramics.

  1. Yield stress of alumina-zirconia suspensions

    International Nuclear Information System (INIS)

    Ramakrishnan, V.; Pradip; Malghan, S.G.

    1996-01-01

    The yield stress of concentrated suspensions of alumina, zirconia, and mixed alumina-zirconia powders was measured by the vane technique as a function of solids loading, relative amounts of alumina and zirconia, and pH. At the isoelectric point (IEP), the yield stress varied as the fourth power of the solids loading. The relative ratio of alumina and zirconia particles was important in determining the yield stress of the suspension at the IEP. The yield stress of single and mixed suspensions showed a marked variation with pH. The maximum value occurred at or near the IEP of the suspension. The effect of electrical double-layer forces on the yield stress can be described on the basis of the Derjaguin-Landau-Verwey-Overbeek (DLVO) theory. A normalized yield stress--that is, the ratio of the yield stress at a given pH to the yield stress at the IEP predicted by this model--showed good correlation with experimental data

  2. Yttria-stabilized zirconia as membrane material for electrolytic deoxidation of CaO-CaCl{sub 2} melts

    Energy Technology Data Exchange (ETDEWEB)

    Martin, A.; Poignet, J. C.; Fouletier, J. [Univ Grenoble, LEPMI, CNRS, INPG, UJF, F-38402 St Martin Dheres (France); Allibert, M. [LPSC, F-38026 Grenoble 1 (France); Lambertin, D. [SPDE, CEA Marcoule, F-30207 Bagnols Sur Ceze (France); Bourges, G. [SRPU, CEA Valduc, F-21120 Is Sur Tille (France)

    2010-07-01

    This article is devoted to the study of the stability of an yttria-stabilized zirconia membrane used in the electrolysis of molten CaCl{sub 2}-CaO mixtures at 850 degrees C. Intentiostatic and potentiostatic electrolysis were carried for periods ranging from 10 to 20 h. Post-mortem composition profiles across the zirconia membrane were determined using Raman spectroscopy and microprobe analysis. The membrane degradation was analyzed in terms of synergetic parameters, i. e., chemical, electrochemical, and thermomechanical effects. (authors)

  3. Cermets Ni-GDC para su uso como ánodos en IT-SOFC basadas en electrolitos GDC

    Directory of Open Access Journals (Sweden)

    Gil, V.

    2008-08-01

    Full Text Available The purpose of this work is to investigate the possible solid state reactions between the NiO-Ce0.9Gd0.1O1.95 (NiO-GDC composites with 50% wt NiO, and cermets Ni- Ce0.9Gd0.1O1.95 (Ni-GDC with 39 vol. % of Ni, and electrolyte solid solutions based on Ce0.9Gd0.1O1.95 (GDC employing the X-ray diffraction technique. At the same time the thermochemical and thermomechanical compatibility between these materials was established. Results obtained from SEM and EDAX analysis showed that the electrolyte based on ceria (GDC and the anode based on nickel-ceria cermet (Ni-GDC present good adhesion and well defined interfaces. No reactive phases and other type of defects were detected. This study showed that both materials, Ni-GDC and GDC are thermochemical and thermomechanically compatible.

    El objetivo de este trabajo es estudiar en un amplio rango de temperaturas (1000-1450ºC y mediante difracción de rayos-X (DRX las posibles reacciones en estado sólido que pueden tener lugar en las regiones interfaciales de sistemas constituidos por composites NiO-Ce0.9Gd0.1O1.95 (NiO-GDC con un 50% en peso de NiO, y de Cermets Ni-Ce0.9Gd0.1O1.95 (Ni-GDC con un 39% en volumen Ni, y electrolitos basados en soluciones sólidas Ce0.9Gd0.1O1.95 (GDC. Y así mismo, estudiar la compatibilidad termoquímica y termomecánica entre los distintos materiales cerámicos que constituyen los sistemas electrolito/ánodo. Se confirma mediante MEB y análisis EDAX que los sistemas cosinterizados entre 1350 y 1400ºC durante 2h y constituidos por un electrolito basado en ceria (GDC y un ánodo basado en un cermet níquel-ceria (Ni-GDC, presentan una buena adherencia entre capas, sin la formación de defectos y sin la presencia de interdifusión de especies a lo

  4. Effect of graphite content on magnetic and mechanical properties of TiC-TiN-Mo-Ni cermets

    Science.gov (United States)

    Zhang, Man; Yang, Qingqing; Xiong, Weihao; Huang, Bin; Ruan, Linji; Mao, Qiao; Li, Shengtao

    2018-04-01

    TiC-10TiN-6Mo-xGr-yNi (mol%, Gr represents graphite, x = 0, 2, 4, 6, 8, and y = 15, 30) cermets were prepared by powder metallurgy method, in order to inverstigate the effect of Gr content on magnetic and mechanical properties of TiC-TiN-Mo-Ni cermets. Room-temperature (RT) saturation magnetization (Ms) and remanence (Mr) of cermets increased with increasing x. This was mainly attributed to that the total content of non-ferromagnetic carbonitride-forming elements Ti and Mo in Ni-based binder phase decreased with increasing x. At the same x, cermets for y = 15 had lower RT Ms and Mr than those for y = 30. Cermets containing more than 2 mol% Gr became ferromagnetic at RT. Bending strength of cermets first increased and then decreased with increasing x. It reached the maximum at x = 2, mainly due to high total content of solutes Ti and Mo in Ni-based binder phase, and moderate thickness of outer rim of Ti(C,N) ceramic grains. Hardness of cermets was not significantly affected by x, mainly due to the combined action of the decrease of the total content of Ti and Mo in binder phase and the increase of the volume fraction of ceramic grains. At the same x, cermets for y = 15 had lower bending strength and higher hardness than those for y = 30.

  5. Influence of WC addition on the microstructure and mechanical properties of NbC-Co cermets

    International Nuclear Information System (INIS)

    Huang, S.G.; Li, L.; Van der Biest, O.; Vleugels, J.

    2007-01-01

    NbC-24.5 wt.% Co cermets with up to 30 wt.% WC were obtained by solid state hot pressing at 1300 o C under a pressure of 45 MPa for 10 min and pressureless liquid phase sintering at 1360 o C for 60 min. The effect of WC addition on the microstructure and mechanical properties of NbC-Co based cermets was investigated. The hot pressed cermets exhibited interconnected and irregular niobium carbide (NbC) or (Nb,W)C grains, whereas the shape of the NbC grains changed from faceted with rounded corners to spherical, as the WC content increased in the pressureless sintered cermets. The undissolved WC increased with increasing WC addition. A clear core/rim structure was observed in the hot pressed cermets with 10-30 wt.% WC additions, whereas this structure was gradually eliminated when pressureless sintering. The hardness remains nearly constant whereas the fracture toughness slightly increases with increasing WC addition. The dissolution of WC in the Co binder and NbC grains, as well as the formation of a solid solution (Nb,W)C phase were supported by thermodynamic calculations

  6. Oxygen potential of a prototypic Mo-cermet fuel containing plutonium oxide

    Energy Technology Data Exchange (ETDEWEB)

    Miwa, Shuhei, E-mail: miwa.shuhei@jaea.go.jp [Japan Atomic Energy Agency, 4002 Narita-cho, Oarai-machi, Higashiibaraki-gun, Ibaraki, 311-1393 (Japan); Osaka, Masahiko [Japan Atomic Energy Agency, 4002 Narita-cho, Oarai-machi, Higashiibaraki-gun, Ibaraki, 311-1393 (Japan); Nozaki, Takahiro; Arima, Tatsumi; Idemitsu, Kazuya [Kyushu University, 744 Motooka Nishi-ku, Fukuoka, 819-0395 (Japan)

    2015-10-15

    Oxygen potential of a prototypic Mo-cermet fuel containing 50 vol.% PuO{sub 2−x} were investigated by the thermogravimetric analysis in the temperature range from 1273 K to 1473 K. It was shown that the oxygen potential and oxidation rate of the Mo-cermet were the same as those of pure PuO{sub 2−x} below the oxygen potential of Mo/MoO{sub 2} oxidation reaction. The same features of the Mo-cermet sample containing 50 vol.% PuO{sub 2−x} with those of pure PuO{sub 2−x} were discussed in terms of the microstructure. - Highlights: • Oxygen potential of Mo-cermet fuel was investigated by thermogravimetric analysis. • It was the same as that of pure PuO{sub 2−x} below the oxygen potential for Mo/MoO{sub 2}. • Gradual oxidation of Mo matrix occurred only above the oxygen potential for Mo/MoO{sub 2}. • Mo matrix and PuO{sub 2−x} in Mo-cermet fuel can thus be thermochemically individual.

  7. Strength and fracture mechanism of iron reinforced tricalcium phosphate cermet fabricated by spark plasma sintering.

    Science.gov (United States)

    Tkachenko, Serhii; Horynová, Miroslava; Casas-Luna, Mariano; Diaz-de-la-Torre, Sebastian; Dvořák, Karel; Celko, Ladislav; Kaiser, Jozef; Montufar, Edgar B

    2018-05-01

    The present work studies the microstructure and mechanical performance of tricalcium phosphate (TCP) based cermet toughened by iron particles. A novelty arises by the employment of spark plasma sintering for fabrication of the cermet. Results showed partial transformation of initial alpha TCP matrix to beta phase and the absence of oxidation of iron particles, as well as a lack of chemical reaction between TCP and iron components during sintering. The values of compressive and tensile strength of TCP/Fe cermet were 3.2 and 2.5 times, respectively, greater than those of monolithic TCP. Fracture analysis revealed the simultaneous action of crack-bridging and crack-deflection microstructural toughening mechanisms under compression. In contrast, under tension the reinforcing mechanism was only crack-bridging, being the reason for smaller increment of strength. Elastic properties of the cermet better matched values reported for human cortical bone. Thereby the new TCP/Fe cermet has potential for eventual use as a material for bone fractures fixation under load-bearing conditions. Copyright © 2018 Elsevier Ltd. All rights reserved.

  8. Oxygen potential of a prototypic Mo-cermet fuel containing plutonium oxide

    International Nuclear Information System (INIS)

    Miwa, Shuhei; Osaka, Masahiko; Nozaki, Takahiro; Arima, Tatsumi; Idemitsu, Kazuya

    2015-01-01

    Oxygen potential of a prototypic Mo-cermet fuel containing 50 vol.% PuO_2_−_x were investigated by the thermogravimetric analysis in the temperature range from 1273 K to 1473 K. It was shown that the oxygen potential and oxidation rate of the Mo-cermet were the same as those of pure PuO_2_−_x below the oxygen potential of Mo/MoO_2 oxidation reaction. The same features of the Mo-cermet sample containing 50 vol.% PuO_2_−_x with those of pure PuO_2_−_x were discussed in terms of the microstructure. - Highlights: • Oxygen potential of Mo-cermet fuel was investigated by thermogravimetric analysis. • It was the same as that of pure PuO_2_−_x below the oxygen potential for Mo/MoO_2. • Gradual oxidation of Mo matrix occurred only above the oxygen potential for Mo/MoO_2. • Mo matrix and PuO_2_−_x in Mo-cermet fuel can thus be thermochemically individual.

  9. Physical properties and microstructure of Ti(CN)-based cermets with different WC particle size

    International Nuclear Information System (INIS)

    Deng, Ying; Deng, Ling; Xiong, Xiang; Ye, J.W.; Li, P.P.

    2014-01-01

    Ti(CN)-based cermets with different WC particle sizes from 0.2 to 4 μm were prepared at 1450 °C with 2 MPa Air pressure. The microstructure of cermets was investigated by scanning electron microscope (SEM), X-ray diffraction (XRD), Transmission electron microscope (TEM). The results showed that all the cermets with different WC particle sizes have a typical “core–rim” structure. With the increase of WC powder sizes, the frequency and portion of Ti(C 0.7 N 0.3 ) cores and rim are somewhat decreased while the portion of white core is increased, due to the relative dissolution rate decreasing. In addition, the fracture mode of Ti(C,N) based cermets is a mixture of trans-granular (primary) and inter-granular (subordinate) fracture. The TRS (about 1850 MPa) of the cermets fluctuate slightly with the WC particle sizes from 0.2 to 1.0 μm, but decrease evidently with WC particle sizes up to 2 μm

  10. CURING EFFICIENCY OF DUAL-CURE RESIN CEMENT UNDER ZIRCONIA WITH TWO DIFFERENT LIGHT CURING UNITS

    Directory of Open Access Journals (Sweden)

    Pınar GÜLTEKİN

    2015-04-01

    Full Text Available Purpose: Adequate polymerization is a crucial factor in obtaining optimal physical properties and a satisfying clinical performance from composite resin materials. The aim of this study was to evaluate the polymerization efficiency of dual-cure resin cement cured with two different light curing units under zirconia structures having differing thicknesses. Materials and Methods: 4 zirconia discs framework in 4 mm diameter and in 0.5 mm, 1 mm and 1.5 mm thickness were prepared using computer-aided design system. One of the 0.5 mm-thick substructures was left as mono-layered whereas others were layered with feldspathic porcelain of same thickness and ceramic samples with 4 different thicknesses (0.5, 1, 1.5 and 2.0 mm were prepared. For each group (n=12 resin cement was light cured in polytetrafluoroethylene molds using Light Emitting Diode (LED or Quartz-Tungsten Halogen (QHT light curing units under each of 4 zirconia based discs (n=96. The values of depth of cure (in mm and the Vickers Hardness Number values (VHN were evaluated for each specimen. Results: The use of LED curing unit produced a greater depth of cure compared to QTH under ceramic discs with 0.5 and 1 mm thickness (p<0.05.At 100μm and 300 μm depth, the LED unit produced significantly greater VHN values compared to the QTH unit (p<0.05. At 500 μm depth, the difference between the VHN values of LED and QTH groups were not statistically significant. Conclusion: Light curing may not result in adequate resin cement polymerization under thick zirconia structures. LED light sources should be preferred over QTH for curing dual-cure resin cements, especially for those under thicker zirconia restorations.

  11. High-Temperature Tolerance in Multi-Scale Cermet Solar-Selective Absorbing Coatings Prepared by Laser Cladding.

    Science.gov (United States)

    Pang, Xuming; Wei, Qian; Zhou, Jianxin; Ma, Huiyang

    2018-06-19

    In order to achieve cermet-based solar absorber coatings with long-term thermal stability at high temperatures, a novel single-layer, multi-scale TiC-Ni/Mo cermet coating was first prepared using laser cladding technology in atmosphere. The results show that the optical properties of the cermet coatings using laser cladding were much better than the preplaced coating. In addition, the thermal stability of the optical properties for the laser cladding coating were excellent after annealing at 650 °C for 200 h. The solar absorptance and thermal emittance of multi-scale cermet coating were 85% and 4.7% at 650 °C. The results show that multi-scale cermet materials are more suitable for solar-selective absorbing coating. In addition, laser cladding is a new technology that can be used for the preparation of spectrally-selective coatings.

  12. High-Temperature Tolerance in Multi-Scale Cermet Solar-Selective Absorbing Coatings Prepared by Laser Cladding

    Directory of Open Access Journals (Sweden)

    Xuming Pang

    2018-06-01

    Full Text Available In order to achieve cermet-based solar absorber coatings with long-term thermal stability at high temperatures, a novel single-layer, multi-scale TiC-Ni/Mo cermet coating was first prepared using laser cladding technology in atmosphere. The results show that the optical properties of the cermet coatings using laser cladding were much better than the preplaced coating. In addition, the thermal stability of the optical properties for the laser cladding coating were excellent after annealing at 650 °C for 200 h. The solar absorptance and thermal emittance of multi-scale cermet coating were 85% and 4.7% at 650 °C. The results show that multi-scale cermet materials are more suitable for solar-selective absorbing coating. In addition, laser cladding is a new technology that can be used for the preparation of spectrally-selective coatings.

  13. Literature review of thermal and radiation performance parameters for high-temperature, uranium dioxide fueled cermet materials

    International Nuclear Information System (INIS)

    Haertling, C.; Hanrahan, R.J.

    2007-01-01

    High-temperature fissile-fueled cermet literature was reviewed. Data are presented primarily for the W-UO 2 as this was the system most frequently studied; other reviewed systems include cermets with Mo, Re, or alloys as a matrix. Failure mechanisms for the cermets are typically degradation of mechanical integrity and loss of fuel. Mechanical failure can occur through stresses produced from dissimilar expansion coefficients, voids created from diffusion of dissimilar materials or formation of metal hydride and subsequent volume expansion. Fuel loss failure can occur by high temperature surface vaporization or by vaporization after loss of mechanical integrity. Techniques found to aid in retaining fuel include the use of coatings around UO 2 fuel particles, use of oxide stabilizers in the UO 2 , minimizing grain sizes in the metal matrix, minimizing impurities, controlling the cermet sintering atmosphere, and cladding around the cermet

  14. Comparative studies of CERCER and CERMET fuels for EFIT from the viewpoint of core performance and safety

    International Nuclear Information System (INIS)

    Chen, X.N.; Rineiski, A.; Maschek, W.; Liu, P.; Boccaccini, C.M.; Sobolev, V.; Delage, F.; Rimpault, G.

    2011-01-01

    The European Facility for Industrial Transmutation (EFIT) has been developed within the 6. EU Framework by the EUROTRANS Program, aiming at a generic conceptual design of an accelerator driven transmuter. This paper deals with assessments of EFIT cores with CERCER and CERMET fuels from the viewpoint of core performance and safety. The conclusive remarks can be drawn as follows. Because of its much better thermal conductivity, the CERMET core can be designed by using thicker pins, so that it has the same or even better transmutation performance compared to the CERCER core. Both CERCER and CERMET fuels fulfill safety requirements. Moreover the CERMET fuel has higher fuel safety margins than the CERCER one. Preliminary analyses show that the CERMET total core power can be further increased by 50% at least without exceeding fuel and clad temperature limits. (authors)

  15. Chemical treatment and biomimetic coating evaluating in zirconia-alumina ceramics; Avaliacao de tratamentos quimicos e recobrimento biomimetico em ceramicas de alumina-zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Aguiar, Amanda Abati

    2007-07-01

    Ceramic materials, as alumina and zirconia have been explored along the years as biomaterials application. The bio inert nature has been stimulating the development of new alternatives, as chemical treatments to improve the biological application of these ceramics. The biomimetic process of bio inert ceramics for coating apatite is based on soaking the implant in a simulated body fluid, SBF, with ion concentrations nearly equal to those of human blood plasma. The bioactivity of the material is related with the formation of a layer constituted of hydroxyapatite low crystalline, similar to the biological apatite. The biocompatibility associated to the structural properties of the alumina and zirconia has been stimulating the clinical use of these materials, mainly in areas of larger mechanical requests, places not recommended for bioactive hydroxyapatite, for instance. In this work samples of alumina, zirconia doped with Yttria (3% mol) and composites of alumina and zirconia doped with Yttria (3% mol) were prepared by co-precipitation method, calcinate, sintered, chemically treated with solutions of acid phosphoric and sodium hydroxide and them immersed in 1.0 M and 1.5 M SBF. The calcinate powders were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), gas adsorption (BET) and laser diffraction. The XRD results indicate that the samples are low crystalline. It was observed for BET that the samples present high specific surface area. The results of laser diffraction and SEM showed that the powders are agglomerates. The sintered samples were analyzed by XRD, SEM and X-ray fluorescence (XRF). The phases quantified by Rietveld method were: cubic, tetragonal and monoclinic of the zirconia, besides the phase alpha of the alumina. The chemical treatment with phosphoric acid didn't present a tendency of larger apatite formation in relation to the samples no chemically treated. The treatment with sodium hydroxide provoked accentuated transformation

  16. Graphene nanosheet-induced toughening of yttria-stabilized zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Su, Jianan; Chen, Yao; Huang, Qiqi [Soochow University, School of Mechanical and Electric Engineering, Collaborative Innovation Center of Suzhou Nano Science and Technology, Suzhou (China)

    2017-01-15

    Graphene nanosheet (GNS)-reinforced yttria-stabilized tetragonal zirconia polycrystals (TZP) were synthesized using spark plasma sintering (SPS), and the influences of the added GNSs on microstructure evolution and the microscopic mechanical properties of the sintered composites were investigated. Raman spectroscopy and microstructure observation corroborated that these added GNSs, which can survive the harsh SPS processing condition, homogeneously distribute in the matrix of all composites to hinder significantly the grain growth. In comparison with the monolithic TZP, the indentation fracture toughness of a GNS/TZP composite reaches maximum value and increases by up to ∝36% (from ∝4.1 to ∝5.6 MPa m{sup 0.5}) even at 0.5% weight fraction, GNS pullout, crack bridging, crack deflection, and crack branching are responsible for the increased fracture toughness. The computed energy dissipation by GNS pullout decreases with increasing the number of graphene layers due to weak bonding between them, and therefore, graphene agglomeration would impair toughening effect. Moreover, scratch studies suggest that GNS/TZP composites exhibit improved scratch resistance due to the fact that GNSs are promising reinforcing and lubricating nanofillers in ceramic composites. (orig.)

  17. Properties and clinical application of zirconia bioceramics in medicine

    Directory of Open Access Journals (Sweden)

    Čedomir Oblak

    2014-01-01

    Full Text Available Background: A group of inorganic non-metal biomaterials, that are commonly used in clinical medicine to replace or repair tissues, can be classified as a bioceramics. This group includes bioactive glasses, glass-ceramics, hydroxy-apatite and some other calcium phosphates. In addition, some bio-inert engineering ceramics materials have become increasingly utilised, aluminum oxide, zirconium oxide and their composites being the most popular. With the developement of yttria stabilized tetragonal zirconium oxide ceramics (Y-TZP medical community received a high strength biomaterial that is currently a material of choice for the manufacturing of medical devices. Y-TZP ceramics is becoming also increasingly used in dental medicine, where frameworks are manufactured by the use of computer-assisted technology.Conclusions: The article describes the basic properties of zirconia oxide ceramics important for the use in clinical medicine; high strength and fracture toughness, biocompatibility and negligible radiation. The ageing issue of this particular material, which is attributable to the thermo-dynamical instability of tetragonal zirconium oxide in hydrothermal conditions, is also discussed. When exposed to an aqueous environment over long periods of time, the surface of the Y-TZP ceramic will start transforming spontaneously into the monoclinic structure. The mechanism leading to the t-m transformation is temperature-dependent and is accompanied by extensive micro-cracking, which ultimately leads to strength degradation. The degradation might influence the clinical success rate of medical devices and therefore Y-TZP femoral heads are no longer made of pure zirconium oxide. Composites of zirconium and aluminium oxides are used instead, that are currently the strongest ceramic materials used in clinical medicine. In this work the clinical application of zirconia oxide ceramics in dental medicine is also presented. Conventional porcelain fused to metal

  18. THE EFFECT OFCARBON NANOTUBES ON THE SINTERING BEHAVIOR OF ZIRCONIA BASED MATERIALS

    OpenAIRE

    A. M. Zahedi; H. R. Rezaie; J. Javadpour

    2015-01-01

    Different volume fractions (1.3, 2.6, and 7.6 Vol.%) of carbon nanotubes (CNTs) were dispersed within 8Y-TZP nanopowders. Mixed powder specimens were subsequently processed by spark plasma sintering (SPS) and effects of CNTs on the sintering process of 8Y-TZP/CNT composites was studied. Maintenance of CNTs through the SPS process was confirmed using TEM and Raman Spectroscopy. Studies on the sintering profile of zirconia-CNT composites (Z-xC composites) could, to some extent, clarify the effe...

  19. Densification behavior of aluminum alloy powder mixed with zirconia powder inclusion under cold compaction

    International Nuclear Information System (INIS)

    Ryu, Hyun Seok; Lee, Sung Chul; Kim, Ki Tae

    2002-01-01

    Densification behavior of composite powders was investigated during cold compaction. Experimental data were obtained for aluminum alloy powder mixed with zirconia powder inclusion under triaxial compression. The cap model with constraint factors was implemented into a finite element program(ABAQUS) to simulate compaction responses of composite powders during cold compaction. Finite element results were compared with experimental data for densification behavior of composite powders under cold isostatic pressing and die compaction. The agreements between experimental data and finite element calculations from the cap model with constraint factors were good

  20. Investigation of phase stability in the scandia-zirconia

    International Nuclear Information System (INIS)

    Grosso, Robson Lopes

    2016-01-01

    In this work, the phase stability of scandia-zirconia (ScSZ) system was investigated by the thermodynamic study of nanoparticles, within the range of 0 to 20 mol% Sc 2 O 3 , and by codoping of ZrO 2 -10 mol% Sc 2 O 3 (10ScSZ) with Dy 2 O 3 and Nb 2 O 5 . The phase stability of ScSZ was evaluated based on thermodynamic data collected by water adsorption microcalorimetry and high temperature oxide melt solution. Nanostructured zirconia-scandia solid solutions were synthesized by coprecipitation method. Thermodynamic data were determined for ScSZ polymorph (monoclinic, tetragonal, cubic, rhombohedral β and γ) found by X-ray diffraction. This systemic work resulted in an unprecedented phase diagram at the nanoscale of particle size-composition. The effects of additives on 10ScSZ were investigated aiming to stabilize the cubic (c) structure at room temperature and to suppress the characteristic cubic-rhombohedral β phase transformation. Compositions were prepared by coprecipitation and solid state reaction. Materials were sintered by conventional and spark plasma sintering. Full stabilization of the cubic phase was attained by 1 mol% Dy 2 O 3 and 0.5 mol% Nb 2 O 5 additions. The smallest Nb 2 O 5 content required for cubic phase stabilization was attributed to liquid phase formation during sintering and to small ionic radius of Nb 5+ . Results of high temperature X-ray diffraction and thermal analysis show suppression of the c-β transformation. Samples containing 0.5 mol% Nb 2 O 5 show total ionic conductivity similar to 10ScSZ without additives within a broad temperature range with high stability during 170 h at 600 °C. (author)

  1. Effect of Mo and C additions on magnetic properties of TiC–TiN–Ni cermets

    International Nuclear Information System (INIS)

    Zhang, Man; Yang, Qingqing; Xiong, Weihao; Zheng, Liyun; Huang, Bin; Chen, Shan; Yao, Zhenhua

    2015-01-01

    The effect of 2–8 mol.% Mo and 4 mol.% C additions on magnetic properties of TiC–10TiN–30Ni (mol.%) cermet was investigated. Saturation magnetization M_s, remanence M_r and Curie temperature T_c of as-sintered cermets (1420 °C, 1 h) decreased with increasing Mo. This was mainly attributed to that the total content of non-magnetic alloying elements Mo and Ti in Ni-based binder phase increased with increasing Mo in cermets, leading to the weakening of magnetic exchange interaction among Ni atoms in binder phase. The further addition of 4 mol.% C inversely increased M_s, M_r and T_c of cermets, which was mainly attributed to that it decreased the total content of Mo and Ti in binder phase, leading to the strengthening of magnetic exchange interaction among Ni atoms in binder phase. T_c of cermets without C addition was about 250 K at 6 mol.% Mo and 115 K at 8 mol.% Mo, respectively, and that of cermets with 4 mol.% C addition was about 194 K at 8 mol.% Mo. - Highlights: • M_s, M_r and T_c of TiC–10TiN–30Ni–xMo cermets decreased with the increase of Mo content, x. • Further addition of 4 mol.% C inversely increased M_s, M_r and T_c of cermets at the same Mo content. • T_c of cermets without C addition was about 250 K at x = 6 and 115 K at x = 8, respectively. • T_c of cermets with 4 mol.% C addition was about 194 K at x = 8.

  2. Effect of Mo and C additions on magnetic properties of TiC–TiN–Ni cermets

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Man [State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Yang, Qingqing, E-mail: yqqah@sina.com [State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Xiong, Weihao [State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Zheng, Liyun [School of Equipment Manufacture, Hebei University of Engineering, Handan 056038 (China); Huang, Bin; Chen, Shan; Yao, Zhenhua [State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 (China)

    2015-11-25

    The effect of 2–8 mol.% Mo and 4 mol.% C additions on magnetic properties of TiC–10TiN–30Ni (mol.%) cermet was investigated. Saturation magnetization M{sub s}, remanence M{sub r} and Curie temperature T{sub c} of as-sintered cermets (1420 °C, 1 h) decreased with increasing Mo. This was mainly attributed to that the total content of non-magnetic alloying elements Mo and Ti in Ni-based binder phase increased with increasing Mo in cermets, leading to the weakening of magnetic exchange interaction among Ni atoms in binder phase. The further addition of 4 mol.% C inversely increased M{sub s}, M{sub r} and T{sub c} of cermets, which was mainly attributed to that it decreased the total content of Mo and Ti in binder phase, leading to the strengthening of magnetic exchange interaction among Ni atoms in binder phase. T{sub c} of cermets without C addition was about 250 K at 6 mol.% Mo and 115 K at 8 mol.% Mo, respectively, and that of cermets with 4 mol.% C addition was about 194 K at 8 mol.% Mo. - Highlights: • M{sub s}, M{sub r} and T{sub c} of TiC–10TiN–30Ni–xMo cermets decreased with the increase of Mo content, x. • Further addition of 4 mol.% C inversely increased M{sub s}, M{sub r} and T{sub c} of cermets at the same Mo content. • T{sub c} of cermets without C addition was about 250 K at x = 6 and 115 K at x = 8, respectively. • T{sub c} of cermets with 4 mol.% C addition was about 194 K at x = 8.

  3. Composite films prepared from agricultural by-products

    Czech Academy of Sciences Publication Activity Database

    Šimkovic, I.; Kelnar, Ivan; Mendichi, R.; Bertok, T.; Filip, J.

    2017-01-01

    Roč. 156, 20 January (2017), s. 77-85 ISSN 0144-8617 Institutional support: RVO:61389013 Keywords : sugar beet residue * bagasse * holocellulose Subject RIV: JI - Composite Materials OBOR OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics Impact factor: 4.811, year: 2016

  4. Sealing ability of cermet ionomer cement as a retrograde filling material.

    Science.gov (United States)

    Aktener, B O; Pehlivan, Y

    1993-03-01

    An in vitro dye leakage study was performed to compare the sealing ability of high copper amalgam with cavity varnish and cermet ionomer cement with and without varnish when used as retrofilling materials. The root canals of 54 maxillary anterior teeth were instrumented and obturated with gutta-percha and sealer. The apical 3 mm of the roots were resected and apical class I cavity preparations were made. The roots were then randomly divided into three groups and retrofilled with one of the experimental materials. After 72 h of immersion in India ink, the roots were cleared and evaluated for leakage with a stereomicroscope. Statistical analysis indicated that the cermet ionomer cement with varnish group had significantly less leakage than the amalgam group (P cermet ionomer cement without varnish group (P 0.05).

  5. High-performance circular sawing of AISI 1045 steel with cermet and tungsten carbide inserts

    International Nuclear Information System (INIS)

    Abrao, A. M.; Rubio, J. C. Campos; Moreira, C.; Faria, P. E.

    2014-01-01

    This work investigated the influence of cutting speed and feed rate on cutting forces, surface roughness, and slot width circular sawing of AISI 1045 steel. The effects of tool material (cermet and tungsten carbide) and geometry (chip breaker flute and pre-cutting/postcutting teeth) were also investigated. Thrust and radial forces generally tended to decrease as the cutting speed increased and tended to increase with the feed rate. The lowest values of thrust and radial forces were obtained using a tungsten carbide saw ground with precutting and post-cutting teeth. With regard to the quality of the machined wall, the lowest surface roughness was obtained by applying the highest cutting speed and lowest feed rate and employing a cermet brazed saw. Under this condition, roughness values comparable to face turning and parting off operations were obtained. The cermet brazed saw was responsible for producing the narrowest slot widths.

  6. Processing microstructure property correlation of porous Ni-YSZ cermets anode for SOFC application

    International Nuclear Information System (INIS)

    Pratihar, Swadesh K.; Dassharma, A.; Maiti, H.S.

    2005-01-01

    The present paper investigates microstructural properties and electrical conductivity of cermets prepared by a solid-state technique, a liquid-dispersion technique and a novel electroless coating technique. The Ni-YSZ processed through different techniques shows varying temperature-conductivity behaviour. The cermets synthesised by electroless coating were found to be electronically conducting with 20 vol% nickel, which is substantially lower than that normally reported. The conductivity of Ni-YSZ cermets was found highest for the samples prepared by an electroless coating technique and lowest for the samples prepared by a solid-state technique, the samples prepared from liquid-dispersion show an intermediate value for a constant nickel content. The variation in electrical conductivity has been well explained from the microstructure of the samples

  7. Characterization of porous texture of cermet electrode for steam electrolysis at intermediate temperature

    International Nuclear Information System (INIS)

    Deslouis, C.; Keddam, M.; Rahmouni, K.; Takenouti, H.; Grasset, F.; Lacroix, O.; Sala, B.

    2011-01-01

    Electrodes designed for PCEC (Proton Conducting Electrolyzing Cell) should ensure both electron and proton conductions and also allowed the supply or the draining of gaseous phase such as steam, hydrogen and oxygen. Porous cermet electrodes fulfil these requirements: percolated metallic phase for electron conduction, ceramic for proton conduction, and pores for transport of reactant and products in gas phase. The electrochemical reactions will take place at boundaries of these three phases, commonly named triple points. Therefore, the cermet electrode has to possess a sufficient open porosity and the expanded metallic surface area exposed to pores as large as possible. In this work, the pore texture of cermet electrodes was characterized by means of Electrochemical Impedance Spectroscopy in aprotic liquid medium. The parameter regression calculation based on de Levie's transmission-line model allowed us to determine the pore texture characterized by expanded surface area, number, mean radius of pores, and open porosity.

  8. Investigation of phase stability in the scandia-zirconia; Investigacao da estabilidade de fases da zirconia-escandia

    Energy Technology Data Exchange (ETDEWEB)

    Grosso, Robson Lopes

    2016-11-01

    In this work, the phase stability of scandia-zirconia (ScSZ) system was investigated by the thermodynamic study of nanoparticles, within the range of 0 to 20 mol% Sc{sub 2}O{sub 3}, and by codoping of ZrO{sub 2}-10 mol% Sc{sub 2}O{sub 3} (10ScSZ) with Dy{sub 2}O{sub 3} and Nb{sub 2}O{sub 5}. The phase stability of ScSZ was evaluated based on thermodynamic data collected by water adsorption microcalorimetry and high temperature oxide melt solution. Nanostructured zirconia-scandia solid solutions were synthesized by coprecipitation method. Thermodynamic data were determined for ScSZ polymorph (monoclinic, tetragonal, cubic, rhombohedral β and γ) found by X-ray diffraction. This systemic work resulted in an unprecedented phase diagram at the nanoscale of particle size-composition. The effects of additives on 10ScSZ were investigated aiming to stabilize the cubic (c) structure at room temperature and to suppress the characteristic cubic-rhombohedral β phase transformation. Compositions were prepared by coprecipitation and solid state reaction. Materials were sintered by conventional and spark plasma sintering. Full stabilization of the cubic phase was attained by 1 mol% Dy{sub 2}O{sub 3} and 0.5 mol% Nb{sub 2}O{sub 5} additions. The smallest Nb{sub 2}O{sub 5} content required for cubic phase stabilization was attributed to liquid phase formation during sintering and to small ionic radius of Nb{sup 5+}. Results of high temperature X-ray diffraction and thermal analysis show suppression of the c-β transformation. Samples containing 0.5 mol% Nb{sub 2}O{sub 5} show total ionic conductivity similar to 10ScSZ without additives within a broad temperature range with high stability during 170 h at 600 °C. (author)

  9. Low Cost Nuclear Thermal Rocket Cermet Fuel Element Environment Testing

    Science.gov (United States)

    Bradley, David E.; Mireles, Omar R.; Hickman, Robert R.

    2011-01-01

    Deep space missions with large payloads require high specific impulse (Isp) and relatively high thrust in order to achieve mission goals in reasonable time frames. Conventional, storable propellants produce average Isp. Nuclear thermal rockets (NTR) capable of high Isp thrust have been proposed. NTR employs heat produced by fission reaction to heat and therefore accelerate hydrogen which is then forced through a rocket nozzle providing thrust. Fuel element temperatures are very high (up to 3000K) and hydrogen is highly reactive with most materials at high temperatures. Data covering the effects of high temperature hydrogen exposure on fuel elements is limited. The primary concern is the mechanical failure of fuel elements which employ high-melting-point metals, ceramics or a combination (cermet) as a structural matrix into which the nuclear fuel is distributed. It is not necessary to include fissile material in test samples intended to explore high temperature hydrogen exposure of the structural support matrices. A small-scale test bed designed to heat fuel element samples via non-contact RF heating and expose samples to hydrogen is being developed to assist in optimal material and manufacturing process selection without employing fissile material. This paper details the test bed design and results of testing conducted to date.

  10. Toughening effect of multi-walled boron nitride nanotubes and their influence on the sintering behaviour of 3Y-TZP zirconia ceramics

    Czech Academy of Sciences Publication Activity Database

    Tatarko, Peter; Grasso, S.; Chlup, Zdeněk; Porwal, H.; Kasiarova, M.; Dlouhý, Ivo; Reece, M.J.

    2014-01-01

    Roč. 34, č. 7 (2014), s. 1829-1843 ISSN 0955-2219 EU Projects: European Commission(XE) 264526 - GLACERCO Institutional support: RVO:68081723 Keywords : Zirconia * Boron nitride nanotubes * Composite * Spark plasma sintering * Toughening mechanism Subject RIV: JI - Composite Materials Impact factor: 2.947, year: 2014

  11. Combustion synthesis of TiB2-based cermets: modeling and experimental results

    International Nuclear Information System (INIS)

    Martinez Pacheco, M.; Bouma, R.H.B.; Katgerman, L.

    2008-01-01

    TiB 2 -based cermets are prepared by combustion synthesis followed by a pressing stage in a granulate medium. Products obtained by combustion synthesis are characterized by a large remaining porosity (typically 50%). To produce dense cermets, a subsequent densification step is performed after the combustion process and when the reacted material is still hot. To design the process, numerical simulations are carried out and compared to experimental results. In addition, physical and electrical properties of the products related to electrical contact applications are evaluated. (orig.)

  12. Cermet reinforcement of a weakened endodontically treated root: a case report.

    Science.gov (United States)

    Lui, J L

    1992-08-01

    Many clinical applications have been recommended for glass-cermet cement because of its improved properties compared to the original glass-ionomer cements. It has also been accepted as a dentinal substitute that can strengthen teeth. In this paper, an additional clinical application for glass-cermet cement, the reinforcement of weakened endodontically treated roots, is suggested. This technique is in keeping with the trends of tooth conservation and the use of an adhesive restorative material in the restoration of severely damaged teeth by a conservative approach.

  13. Corrosion characteristics of several thermal spray cermet-coating/alloy systems

    International Nuclear Information System (INIS)

    Ashary, A.A.; Tucker, R.C. Jr.

    1991-01-01

    The corrosion characteristics of a thermal spray multiphase cermet coating can be quite complex. Factors such as porosity and galvanic effects between different phases in the coating and the substrate, as well as the inherent general and localized corrosion resistance of each phase, can play an important role. The present paper describes the corrosion of several cermet-coating/alloy systems as studied by a potentiodynamic cyclic polarization technique. The corrosion of these coating systems was found to be most often dominated by corrosion of the metallic phases in the coating or of the substrate alloy. (orig.)

  14. The role of powder preparation method in enhancing fracture toughness of zirconia ceramics with low alumina amount

    International Nuclear Information System (INIS)

    Danilenko, I.; Konstantinova, T.; Volkova, G.; Burkhovetski, V.; Glazunova, V.

    2015-01-01

    In most cases zirconia-alumina composites for scientific investigations and industry are prepared by means of mechanical mixing of powders, compaction and sintering. In our opinion, this is one of the reasons for the low values for fracture toughness of the sintered materials. In this study, we investigated the effect of nanopowder synthesis methods on the structure and mechanical properties of 3Y-TZP/alumina ceramic composites and determined the mechanisms involved in composite toughening. We show that the addition of a small amount of alumina (1 - 2 wt%) to zirconia ceramics has the potential to increase the fracture toughness of zirconia ceramics. The starting powders were obtained by means of co-precipitation and ball milling. It turned out that at equal density, bending strength and hardness values, the fracture toughness in ceramic composites sintered from co-precipitated nanopowders is higher in comparison with fracture toughness values in matrix material and traditional 3Y-TZP/alumina composites. We believed that the role of the crack deflection process in ceramic composites sintered from co-precipitated nanopowders increased significantly. This can be conditioned by means of a series of processes for composite structure formation during precipitation, crystallization, and sintering of nanopowders.

  15. The role of powder preparation method in enhancing fracture toughness of zirconia ceramics with low alumina amount

    Energy Technology Data Exchange (ETDEWEB)

    Danilenko, I.; Konstantinova, T.; Volkova, G.; Burkhovetski, V.; Glazunova, V. [NAS of Ukraine, Donetsk (Ukraine). Donetsk Inst. for Physics and Engineering

    2015-07-01

    In most cases zirconia-alumina composites for scientific investigations and industry are prepared by means of mechanical mixing of powders, compaction and sintering. In our opinion, this is one of the reasons for the low values for fracture toughness of the sintered materials. In this study, we investigated the effect of nanopowder synthesis methods on the structure and mechanical properties of 3Y-TZP/alumina ceramic composites and determined the mechanisms involved in composite toughening. We show that the addition of a small amount of alumina (1 - 2 wt%) to zirconia ceramics has the potential to increase the fracture toughness of zirconia ceramics. The starting powders were obtained by means of co-precipitation and ball milling. It turned out that at equal density, bending strength and hardness values, the fracture toughness in ceramic composites sintered from co-precipitated nanopowders is higher in comparison with fracture toughness values in matrix material and traditional 3Y-TZP/alumina composites. We believed that the role of the crack deflection process in ceramic composites sintered from co-precipitated nanopowders increased significantly. This can be conditioned by means of a series of processes for composite structure formation during precipitation, crystallization, and sintering of nanopowders.

  16. Interaction of oxygen with zirconia surface

    International Nuclear Information System (INIS)

    Ivankiv, L.I.; Ketsman, I.V.

    1999-01-01

    The influence of surface heat treatment, electron (50-800) eV irradiation and UV (180-300) nM illumination of adsorption system on the state of oxygen adsorbed on zirconia surface have been investigated. On the basis of experimental results obtained by investigation of photon emission accompanying oxygen adsorption (AL) and TPD data existence of adsorption sites on the surface is suggested on which irreversible dissociative adsorption of oxygen occurs. These very sites are associated with emission processes Conclusion is made that the only type of adsorption sites connected with anion vacancy is present on zirconia surface and this is its charge state that determines the state of adsorbed oxygen. One of the important mechanisms by which the electron and UV photon excitation affects the adsorption interaction is the change of the charge state of the adsorption site

  17. Synthesis of nanosized powders of stabilized zirconia

    International Nuclear Information System (INIS)

    Takodoro, Sandra Kiyoko

    2000-01-01

    Zirconia solid solutions containing 3 mol % Yttria or 12 mol % ceria have been prepared by the coprecipitation technique followed by azeotropic distillation. The aim of this work is the synthesis of tetragonal zirconia polycrystals nanosized powders that sinter at comparatively lower temperatures attaining high densification, and without using any milling procedure. The main results show that: 1- the dopant cation has a strong influence on the crystallization behavior of the precipitates; 2- the used techniques allowed for obtaining high values of specific surface area (∼130 m 2 .g -1 ); 3- the optimization of the synthesis and processing parameters are responsible for obtaining high densification (≥97% of the theoretical value), at lower temperatures (∼1200 deg C) with average grain sizes lower than 500 nm; 4- impedance spectroscopy results show a strong correlation between the electrical resistivity and the microstructure of sintered ceramics.(author)

  18. Characterization of the alumina-zirconia ceramic system by ultrasonic velocity measurements

    International Nuclear Information System (INIS)

    Carreon, Hector; Ruiz, Alberto; Medina, Ariosto; Barrera, Gerardo; Zarate, Juan

    2009-01-01

    In this work an alumina-zirconia ceramic composites have been prepared with α-Al 2 O 3 contents from 10 to 95 wt.%. The alumina-zirconia ceramic system was characterized by means of precise ultrasonic velocity measurements. In order to find out the factors affecting the variation in wave velocity, the ceramic composite have been examined by X-ray diffraction (XRD) and (SEM) scanning electron microscopy. It was found that the ultrasonic velocity measurements changed considerably with respect to the ceramic composite composition. In particular, we studied the behavior of the physical material property hardness, an important parameter of the ceramic composite mechanical properties, with respect to the variation in the longitudinal and shear wave velocities. Shear wave velocities exhibited a stronger interaction with microstructural and sub-structural features as compared to that of longitudinal waves. In particular, this phenomena was observed for the highest α-Al 2 O 3 content composite. Interestingly, an excellent correlation between ultrasonic velocity measurements and ceramic composite hardness was observed.

  19. Optimization of the conditions for producing zirconia by the precipitation of basic zirconium sulfate

    International Nuclear Information System (INIS)

    Ricci, D.R.; Paschoal, J.O.A.

    1988-01-01

    The process of precipitation of the basic sulfate from zirconium oxychlorides solutions has been optimized in order to obtain zirconia of high purity as well as suitable for ceramic processing. The main parameters of this study were obtained from the determination of the pH and of the concentration of the initial oxychloride solution, of the sulfate/zirconium molar ratio and of the reaction temperature. The following experimental procedure has been carried out: a) reaction of each precipitate with ammonium hydroxide followed by drying at 150 0 -C / 5 h and calcination at 1000 0 C / 1 h, yielding the final product (zirconia) b) product characterization by means of spectrographic, X - ray fluorescence and diffractometry analyses, determination of grain size distribution and of apparent density, and morphology study by scanning electron microscopy. The yielding of the overall reaction has been determined by chemical analysis and the composition of the basic zirconium sulfate by thermogravimetric analyses. (author) [pt

  20. Toughness determination of zirconia toughened alumina ceramics from growth of indentation-induced cracks

    International Nuclear Information System (INIS)

    Basu, D.; Sarkar, B.K.

    1996-01-01

    Short surface cracks were generated by Vickers indentation on the polished surface of alumina and different zirconia toughened alumina (ZTA) specimens, and their morphology was studied by serial sectioning. These cracks were grown in three-point bend tests under stepwise loading, and variation of toughness with crack extension was plotted to graphically separate the contributions from residual stress intensity and applied stress intensity factors. The plateau toughness determined from the intercept height of the crack extension plots exhibited an upward trend with zirconia content up to 15 vol% ZrO 2 addition in the composition, which was proportional to the fraction of transformable tetragonal grains contributing to transformation toughening. copyright 1996 Materials Research Society

  1. Processing-structure-property relationships in electron beam physical vapor deposited yttria stabilized zirconia coatings

    International Nuclear Information System (INIS)

    Rao, D. Srinivasa; Valleti, Krishna; Joshi, S. V.; Janardhan, G. Ranga

    2011-01-01

    The physical and mechanical properties of yttria stabilized zirconia (YSZ) coatings deposited by the electron beam physical vapor deposition technique have been investigated by varying the key process variables such as vapor incidence angle and sample rotation speed. The tetragonal zirconia coatings formed under varying process conditions employed were found to have widely different surface and cross-sectional morphologies. The porosity, phase composition, planar orientation, hardness, adhesion, and surface residual stresses in the coated specimens were comprehensively evaluated to develop a correlation with the process variables. Under transverse scratch test conditions, the YSZ coatings exhibited two different crack formation modes, depending on the magnitude of residual stress. The influence of processing conditions on the coating deposition rate, column orientation angle, and adhesion strength has been established. Key relationships between porosity, hardness, and adhesion are also presented.

  2. Evaluation of technological properties of alumina refractory systems-zirconia and zirconia-silica-alumina

    International Nuclear Information System (INIS)

    Marinho, A.R.O.; Carvalho, T.U.S.; Fagury Neto, E.; Rabelo, A.A.

    2014-01-01

    Alumina-zirconia refractories are noted for being products of excellent cost-effective, however, zirconia may limit its use due to decreasing resistance to thermal shock. This study aims to evaluate these refractories with the addition of microsilica, which can greatly improve their properties. Were used the following starting materials: calcined alumina, zirconia (stabilized and monoclinic) in amounts of 2%, 4% and 6% by weight, plus microsilica (5%w.). The powders were milled together with binder and lubricant for conformation bodies by uniaxial pressing. The samples were dried, calcined and sintered at 1400 °C/2h were characterized using the methods of Archimedes, and scanning electron microscopy (SEM), chemical analysis using energy dispersive X-ray (EDS), and mechanical flexural strength tests at room temperature. Formulations with the presence of microsilica showed satisfactory results and optimized properties. (author)

  3. Microstructural evolution of alumina-zirconia nanocomposites; Evolucao microestrutural de nanocompositos alumina-zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Ojaimi, C.L.; Chinelatto, A.S.A.; Chinelatto, A.L. [Universidade Estadual de Ponta Grossa (UEPG), PR (Brazil); Pallone, E.M.J.A., E-mail: christianelago@yahoo.com.br [Universidade de Sao Paulo (USP), Pirassununga, Sao Paulo, SP (Brazil). Faculdade de Zootecnia e Engenharia de Alimentos

    2012-07-01

    Ceramic materials have limited use due to their brittleness. The inclusion of nanosized particles in a ceramic matrix, which are called nanocomposites, and ceramic processing control by controlling the grain size and densification can aid in obtaining ceramic products of greater strength and toughness. Studies showed that the zirconia nano inclusions in the matrix of alumina favors an increase in mechanical properties by inhibiting the grain growth of the matrix and not by the mechanism of the transformation toughening phase of zirconia. In this work, the microstructural evolution of alumina nanocomposites containing 15% by volume of nanometric zirconia was studied. From the results it was possible to understand the sintering process of these nanocomposites. (author)

  4. Electrical properties and conduction mechanisms of Ru-based thick-film (cermet) resistors

    International Nuclear Information System (INIS)

    Pike, G.E.; Seager, C.H.

    1977-01-01

    This paper presents an experimental study of the electrical conduction mechanisms in thick-film (cermet) resistor. The resistors were made from one custom and three commercially formulated inks with sheet resistivities ranging from 10 2 to 10 6 Ω/D 7 Alembertian in decade increments. Their microstructure and composition have been examined using optical and scanning electron microscopy, electron microprobe analysis, x-ray diffraction, and various chemical analyses. This portion of our study shows that the resistors are heterogeneous mixtures of metallic metal oxide particles (approx.4 x 10 -5 cm in diameter) and a lead silicate glass. The metal oxide particles are ruthenium containing pyrochlores, and are joined to form a continuous three-dimensional network of chain segments. The principal experimental work reported here is an extensive study of the electrical transport properties of the resistors. The temperature dependence of conductance has been measured from 1.2 to 400 K, and two features common to all resistors are found. There is a pronounced decrease in conductance at low temperatures and a shallow maximum at several hundred Kelvin. Within the same range of temperatures the reversible conductance as a function of electric field from 0 to 28 kV/cm has been studied. The resistors are non-Ohmic at all temperatures, but particularly at cryogenic temperatures for low fields. At higher fields the conductance shows a linear variation with electric field. The thick-film resistors are found to have a small dielectric constant and a (nearly) frequency-independent conductance from dc to 50 MHz. The magnetoresistance to 100 kG, the Hall mobility, and the Seebeck coefficient of most of the resistors have been measured and discovered to be quite small. Many of the electrical transport properties have also been determined for the metal oxide particles which were extracted from the fired resistors

  5. Niobia and tantala codoped orthorhombic zirconia ceramics

    International Nuclear Information System (INIS)

    Hoeftberger, M.; Gritzner, G.

    1995-01-01

    During recent studies it was found that codoping of zirconia with niobia and tantala yielded very corrosion resistant, orthorhombic zirconia ceramics. The powders for those novel ceramics were made via the sol-gel technique by hydrolysis of the respective metal propoxides; a method which required dry-box techniques during the preparation of the alkoxides. In these studies the authors investigated the fabrication of precursor material from aqueous solutions. The preparation of aqueous solutions of salts of zirconium, niobium and tantalum is hampered by rapid hydrolysis. Premature hydrolysis of the chlorides and oxichlorides of niobium, tantalum and zirconium can be, however, prevented in aqueous solutions of oxalic acid. Thus the authors investigated the coprecipitation of hydroxides as precursors by reacting oxalic acid solutions of the respective cations with aqueous ammonia. In addition they studied the effects of calcination and of hydrothermal conversion of the hydroxides to oxides on the powder characteristics and on the mechanical properties of the niobia and tantala codoped zirconia ceramics

  6. Stabilized zirconia with cerium and neodymium addition

    International Nuclear Information System (INIS)

    Andrade, I.M. de; Pessoa, R.C.; Nasar, M.C.; Nasar, R.S.; Rodriques, M.K.C.; Oliveira, J.F.

    2006-01-01

    Zr 0,9 Ce 0,05 Nd 0,05 O 1,975 system was synthesized with the use of the Pechini method. The polymeric resin was calcined at 350 deg C/3 h and analysed by FTIR that show bands relative to organic. Radicals esther type. The TGA curve indicated the polymeric decomposition occurring from 30 deg C to 740 deg C. DTA analysis show a exothermic peak in 100 deg C due to loss of water of material. From 500 deg C to 800 deg C was observed a intense peak due to polymer decomposition and the zirconia crystallization. The calcined powder from 350 deg C/3 h e 30 min to 900 deg/3 h were analysed by XRD that show the crystalline phase formation with the increase of temperature. The X-ray diffraction pattern show the presence of two phases, such as tetragonal and cubic of zirconia demonstrating that neodymium and cerium additions led to zirconia stabilization. (author)

  7. Characterization of Cr-O cermet solar selective coatings deposited by using direct-current magnetron sputtering technology

    International Nuclear Information System (INIS)

    Lee, Kil Dong

    2006-01-01

    Cr-O (Cr-CrO) cermet solar selective coatings with a double cermet layer film structure were prepared by using a special direct-current (dc) magnetron sputtering technology. The typical film structure from the surface to the bottom substrate was an Al 2 O 3 anti-reflection layer on a double Cr-O cermet layer on an Al metal infrared reflection layer. The deposited Cr-O cermet solar selective coating had an absorptance of α = 0.93 - 0.95 and an emittance of ε = 0.09 - 0.10(100 .deg. C). The absorption layers of the Cr-O cermet coatings deposited on glass and silicon substrates were identified as being amorphous by using X-ray diffraction (XRD). Atomic force microscopy (AFM) showed that Cr-O cermet layers were very smooth and that their grain sizes were very small. The result of thermal stability test showed that the Cr-O cermet solar selective coating was stable for use at temperatures of under 400 .deg. C.

  8. Investigation on microstructure and mechanical properties of Mo2FeB2 based cermets with and without PVA

    Science.gov (United States)

    Shen, Yupeng; Huang, Zhifu; Jian, Yongxin; Yang, Ming; Li, Kemin

    2018-03-01

    Mo2FeB2 based cermets with and without PVA have been investigated by x-ray diffractometry (XRD), x-ray photoelectron spectroscope (XPS) and scanning electron microscopy (SEM). The density and transverse rupture strength (TRS) of green compact, relative density, hardness (HRA), fracture toughness (KIC) and TRS of Mo2FeB2 based cermets were also measured. The results indicate that, compared with the Mo2FeB2 based cermets without PVA, the density of green compact with PVA can be improved slightly at the same pressure. However, the much higher TRS is obtained for the green compact without PVA. Meanwhile, Mo2FeB2 particles exhibit the finer and less congruity feature for Mo2FeB2 based cermets without PVA. In addition, the higher relative density, hardness, fracture toughness and TRS can be acquired for the cermets without PVA. Obviously, considering the mechanical properties and preparation period of Mo2FeB2 based cermets, no adding PVA is the optimized process of powder molding in the manufacture of Mo2FeB2 based cermets.

  9. Critical tuning of magnetron sputtering process parameters for optimized solar selective absorption of NiCrO{sub x} cermet coatings on aluminium substrate

    Energy Technology Data Exchange (ETDEWEB)

    Gaouyat, Lucie, E-mail: lucie.gaouyat@fundp.ac.be [Solid State Physics Laboratory, Research Center in Physics of Matter and Radiation (PMR), Facultés Universitaires Notre-Dame de la Paix (FUNDP), 61 rue de Bruxelles, B-5000 Namur (Belgium); Mirabella, Frédéric [CRM Group – AC and CS, 57b boulevard de Colonster, B-4000 Liège (Belgium); Deparis, Olivier [Solid State Physics Laboratory, Research Center in Physics of Matter and Radiation (PMR), Facultés Universitaires Notre-Dame de la Paix (FUNDP), 61 rue de Bruxelles, B-5000 Namur (Belgium)

    2013-04-15

    NiCrO{sub x} ceramic–metal composites (i.e. cermets) exhibit not only oxidation and moisture resistances, which are very important for industrial applications, but also remarkable solar selective absorption properties. In order to reach the best optical performances with only one coating layer, tuning of the magnetron sputtering process parameters (O{sub 2} flow rate, pressure and deposition time) was performed systematically. The process window turned out to be very narrow implying a critical tuning of the parameters. The optimal operating point was determined for a single layer coating of NiCrO{sub x} on an aluminium substrate, leading to a spectrally integrated solar absorption as high as 78%. Among various material properties, the focus was put on the optical reflectance of the coating/substrate system, which was measured by UV–vis–NIR spectrophotometry. Using complex refractive index data from the literature, the theoretical reflectance spectra were calculated and found to be in good agreement with the measurements. Chemical analysis combined with scanning electronic and atomic force microscopies suggested a cermet structure consisting of metallic Ni particles and a compound matrix made of a mixture of chromium oxide, nickel oxide and nickel hydroxide.

  10. Comparison of shear test methods for evaluating the bond strength of resin cement to zirconia ceramic.

    Science.gov (United States)

    Kim, Jae-Hoon; Chae, Soyeon; Lee, Yunhee; Han, Geum-Jun; Cho, Byeong-Hoon

    2014-11-01

    This study compared the sensitivity of three shear test methods for measuring the shear bond strength (SBS) of resin cement to zirconia ceramic and evaluated the effects of surface treatment methods on the bonding. Polished zirconia ceramic (Cercon base, DeguDent) discs were randomly divided into four surface treatment groups: no treatment (C), airborne-particle abrasion (A), conditioning with Alloy primer (Kuraray Medical Co.) (P) and conditioning with Alloy primer after airborne-particle abrasion (AP). The bond strengths of the resin cement (Multilink N, Ivoclar Vivadent) to the zirconia specimens of each surface treatment group were determined by three SBS test methods: the conventional SBS test with direct filling of the mold (Ø 4 mm × 3 mm) with resin cement (Method 1), the conventional SBS test with cementation of composite cylinders (Ø 4 mm × 3 mm) using resin cement (Method 2) and the microshear bond strength (μSBS) test with cementation of composite cylinders (Ø 0.8 mm × 1 mm) using resin cement (Method 3). Both the test method and the surface treatment significantly influenced the SBS values. In Method 3, as the SBS values increased, the coefficients of variation decreased and the Weibull parameters increased. The AP groups showed the highest SBS in all of the test methods. Only in Method 3 did the P group show a higher SBS than the A group. The μSBS test was more sensitive to differentiating the effects of surface treatment methods than the conventional SBS tests. Primer conditioning was a stronger contributing factor for the resin bond to zirconia ceramic than was airborne-particle abrasion.

  11. Synthesis, by alkaline fusion of zirconia from zirconite: characterization and preparation of lead zirconate-titanate

    International Nuclear Information System (INIS)

    Zaghete, M.A.

    1985-01-01

    Zirconium oxide was prepared from zirconite by alkaline fusion. The purity of zirconia was determined by atomic absorption spectroscopy and was found to be 99,94 wt%. In order to prepare en unglomerated and dry hidrous zirconia powder it was used alcohol and acetone for washing and gel suspension; control of the drying rate; and control of the atmosphere and temperature of the oven. The physical characteristics of the hidrous zirconia powder were determined after calcining in several conditions. The zirconia obtained by calcining at 800 0 C during 5 hours (13,9m 2 /g) was used with titanium oxide (7,6m 2 /g and lead oxide (0,6m 2 /g) to prepare a lead zirconate-titanate (PZT) with composition Pb(Zr 0,5 Ti 0,5 O 3 . Two different procedures were used to obtain high densits PZT pellets: in the first procedure the misture of the oxide powder with above composition were reacted at 850 0 C for 4 hours. Then the powder was pressed and sintered at 1200 0 C during 4 and 6 hours; in the second procedure the mixture of unreacted oxide were pressed in pellets and then reacted at 850 0 C during 4 hours and sintered at 1200 0 C during 4 and 6 hours. The apparent density of the sintered pellets were determined By mercury displacement and ranged from 7,25 to 7,39 g/cm 3 for the compacts obtained by the second procedure and from 8,08 to 8,10g/cm 3 for the compacts obtained by the first procedure. The microstructure observed by scanning electron microscopy showed that sintered compact obtained by the first procedure has a more homogeneous size distribution when compared with samples obtained be the second procedure. (author) [pt

  12. Interaction on boundary of current-conducting and glass-forming phases in cermet films under annealing

    International Nuclear Information System (INIS)

    Shulishova, O.I.; Zyrin, A.V.; Ismalgaliev, R.K.; Izmajlov, Sh.Z.; Kovylyaev, V.V.; Shevchuk, N.V.; Shcherbak, I.A.

    1990-01-01

    The electron-probe microanalysis permits investigating the interaction on the boundary of current-conducting and glass-binding phases in cermet films without noble metals on the base of ruthenium oxide. The performed studies along with experiments on model microsections subject to annealing in different media have shown the differences in the process of formation of structure and properties of cermet resistive elements as well as a significance of the oxidation process of current-conducting phase in formation of high working characteristics of cermet resistors on the base of hexaborides of the rare-earth elements

  13. Effect of artificial aging and surface treatment on bond strengths to dental zirconia.

    Science.gov (United States)

    Perdigão, J; Fernandes, S D; Pinto, A M; Oliveira, F A

    2013-01-01

    The objective of this project was to study the influence of artificial aging and surface treatment on the microtensile bond strengths (μTBS) between zirconia and a phosphate monomer-based self-adhesive cement. Thirty zirconia disks (IPS e.max ZirCAD, Ivoclar Vivadent) were randomly assigned to two aging regimens: AR, used as received, which served as a control, and AG, artificial aging to simulate low-temperature degradation. Subsequently, the disks of each aging regimen were assigned to three surface treatments: NT, no surface treatment; CO, surface silicatization with CoJet sand (3M ESPE); and ZP, zirconia surface treated with Z-Prime Plus (Bisco Inc). Thirty discs were made of Filtek Z250 (3M ESPE) composite resin and luted to the zirconia discs using RelyX Unicem (3M ESPE). The specimens were sectioned with a diamond blade in X and Y directions to obtain bonded beams with a cross-section of 1.0 ± 0.2 mm. The beams were tested in tensile mode in a universal testing machine at a speed of 0.5 mm/min to measure μTBS. Selected beams were selected for fractographic analysis under the SEM. Statistical analysis was carried out with two-way analysis of variance and Dunnett T3 post hoc test at a significance level of 95%. The mean μTBS for the three AR subgroups (AR-NT, AR-CO, and AR-ZP) were significantly higher than those of the corresponding AG groups (p<0.0001). Both AR-CO and AR-ZP resulted in statistically significant higher mean bond strengths than the group AR-NT (p<0.006 and p<0.0001, respectively). Both AG-CO and AG-ZP resulted in statistically significant higher mean bond strengths than the group AG-NT (both at p<0.0001). Overall, AG decreased mean μTBS. Under the SEM, mixed failures showed residual cement attached to the zirconia side of the beams. CO resulted in a characteristic roughness of the zirconia surface. AR-ZP was the only group for which the amount of residual cement occupied at least 50% of the interface in mixed failures.

  14. Chemical treatment and biomimetic coating evaluating in zirconia-alumina ceramics

    International Nuclear Information System (INIS)

    Aguiar, Amanda Abati

    2007-01-01

    Ceramic materials, as alumina and zirconia have been explored along the years as biomaterials application. The bio inert nature has been stimulating the development of new alternatives, as chemical treatments to improve the biological application of these ceramics. The biomimetic process of bio inert ceramics for coating apatite is based on soaking the implant in a simulated body fluid, SBF, with ion concentrations nearly equal to those of human blood plasma. The bioactivity of the material is related with the formation of a layer constituted of hydroxyapatite low crystalline, similar to the biological apatite. The biocompatibility associated to the structural properties of the alumina and zirconia has been stimulating the clinical use of these materials, mainly in areas of larger mechanical requests, places not recommended for bioactive hydroxyapatite, for instance. In this work samples of alumina, zirconia doped with Yttria (3% mol) and composites of alumina and zirconia doped with Yttria (3% mol) were prepared by co-precipitation method, calcinate, sintered, chemically treated with solutions of acid phosphoric and sodium hydroxide and them immersed in 1.0 M and 1.5 M SBF. The calcinate powders were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), gas adsorption (BET) and laser diffraction. The XRD results indicate that the samples are low crystalline. It was observed for BET that the samples present high specific surface area. The results of laser diffraction and SEM showed that the powders are agglomerates. The sintered samples were analyzed by XRD, SEM and X-ray fluorescence (XRF). The phases quantified by Rietveld method were: cubic, tetragonal and monoclinic of the zirconia, besides the phase alpha of the alumina. The chemical treatment with phosphoric acid didn't present a tendency of larger apatite formation in relation to the samples no chemically treated. The treatment with sodium hydroxide provoked accentuated transformation of

  15. Characterization of Nanometric-Sized Carbides Formed During Tempering of Carbide-Steel Cermets

    Directory of Open Access Journals (Sweden)

    Matus K.

    2016-06-01

    Full Text Available The aim of this article of this paper is to present issues related to characterization of nanometric-sized carbides, nitrides and/or carbonitrides formed during tempering of carbide-steel cermets. Closer examination of those materials is important because of hardness growth of carbide-steel cermet after tempering. The results obtained during research show that the upswing of hardness is significantly higher than for high-speed steels. Another interesting fact is the displacement of secondary hardness effect observed for this material to a higher tempering temperature range. Determined influence of the atmosphere in the sintering process on precipitations formed during tempering of carbide-steel cermets. So far examination of carbidesteel cermet produced by powder injection moulding was carried out mainly in the scanning electron microscope. A proper description of nanosized particles is both important and difficult as achievements of nanoscience and nanotechnology confirm the significant influence of nanocrystalline particles on material properties even if its mass fraction is undetectable by standard methods. The following research studies have been carried out using transmission electron microscopy, mainly selected area electron diffraction and energy dispersive spectroscopy. The obtained results and computer simulations comparison were made.

  16. Plasma spraying of zirconium carbide – hafnium carbide – tungsten cermets

    Czech Academy of Sciences Publication Activity Database

    Brožek, Vlastimil; Ctibor, Pavel; Cheong, D.-I.; Yang, S.-H.

    2009-01-01

    Roč. 9, č. 1 (2009), s. 49-64 ISSN 1335-8987 Institutional research plan: CEZ:AV0Z20430508 Keywords : Plasma spraying * cermet coatings * microhardness * zirconium carbide * hafnium carbide * tungsten * water stabilized plasma Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass

  17. PLASMA SPRAYING OF REFRACTORY CERMETS BY THE WATER-STABILIZED SPRAY (WSP®) SYSTEM

    Czech Academy of Sciences Publication Activity Database

    Ctibor, Pavel; Brožek, V.; Cheong, D.-I.; Chráska, Pavel

    2009-01-01

    Roč. 54, č. 3 (2009), s. 241-253 ISSN 0001-7043 Institutional research plan: CEZ:AV0Z20430508 Keywords : Plasma spraying * cermet coatings * microhardness * zirconium carbide * tungsten Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass

  18. Effect of surface treatment on flexural strength of zirconia bars

    NARCIS (Netherlands)

    Aboushelib, M.N.; Wang, H.

    2010-01-01

    Statement of problem Clinical and laboratory processing techniques induce damage to the surface of zirconia frameworks, which significantly lessens their strength. Purpose The purpose of this study was to investigate the influence of 3 surface restoration methods on the flexural strength of zirconia

  19. Sulfated zirconia modified SBA-15 catalysts for cellobiose hydrolysis

    NARCIS (Netherlands)

    Degirmenci, V.; Uner, D.; Cinlar, B.; Shanks, B.H.; Yilmaz, A.; Santen, van R.A.; Hensen, E.J.M.

    2011-01-01

    Zirconia modified SBA-15 becomes a very active catalyst for the selective hydrolysis of cellobiose to glucose after sulfation. Spectroscopic investigations indicate the presence of Brønsted acid sites with similar properties to those present in conventional sulfated zirconia. Indications are found

  20. Osseointegration of a Zirconia Implant : A Histologic Assessment

    NARCIS (Netherlands)

    Schepke, Ulf; Meijer, Gert J; Meijer, Henny Ja; Walboomers, X Frank; Cune, Marco

    2017-01-01

    PURPOSE: The aim of this study was to describe the histologic and histomorphometric features of a retrieved, functional endosseous zirconia implant in a human subject. MATERIALS AND METHODS: A maxillary zirconia implant (ZV3) placed in a 52-year-old man was retrieved after 2 years of uncompromised

  1. Production of zirconia - hydroxyapatite (Z Ha) by using the co-precipitation method and studies of densification

    International Nuclear Information System (INIS)

    Silva, Viviane V.; Domingues, Rosana Z.

    1997-01-01

    Hydroxyapatite (Ha) is one of the materials most bio compatible with human bones and teeth, but its mechanical properties, especially toughness, are insufficient for hard tissue. Recent studies demonstrated that ceramics can be toughened by zirconium particles disperse in them, due to transformation, microcracking, and/or crack diffraction toughening mechanisms. The objective of this study is to characterize zirconia-toughened hydroxy apatite powders prepared by precipitation method by XRD, IR spectroscopy, TEM, TAG, DTA and BET analysis. The density of their ceramics was determined by mercury picnometry method. It was discussed the influence of addition of zirconium in different compositions and phases (Zr O 2 or Zr(OH) 4 ), compacting pressure and sintering temperature on zirconia - hydroxyapatite composites (ZHA). The results show that there is not any kind of reaction or chemical interaction between both phases of the composite materials. (author)

  2. Internal Nano Voids in Yttria-Stabilised Zirconia (YSZ Powder

    Directory of Open Access Journals (Sweden)

    Chen Barad

    2017-12-01

    Full Text Available Porous yttria-stabilised zirconia ceramics have been gaining popularity throughout the years in various fields, such as energy, environment, medicine, etc. Although yttria-stabilised zirconia is a well-studied material, voided yttria-stabilised zirconia powder particles have not been demonstrated yet, and might play an important role in future technology developments. A sol-gel synthesis accompanied by a freeze-drying process is currently being proposed as a method of obtaining sponge-like nano morphology of embedded faceted voids inside yttria-stabilised zirconia particles. The results rely on a freeze-drying stage as an effective and simple method for generating nano-voided yttria-stabilised zirconia particles without the use of template-assisted additives.

  3. Resource recovery of WC-Co cermet using hydrothermal oxidation technique

    International Nuclear Information System (INIS)

    Gao Ningfeng; Inagaki, F.; Sasai, R.; Itoh, H.; Watari, K.

    2005-01-01

    WC-Co cermet is widely used in industrial applications such as cutting tools, dies, wear parts and so on. It is of great importance to establish the recycling process for the precious metal resources contained in WC-Co cermet, because all these metals used in Japan are imported. In this paper we reported a hydrothermal oxidation technique using nitric acid for the reclamation of WC and Co. The WC-Co cermet specimens with various WC particle sizes and Co contents were hydrothermally treated in HNO 3 aqueous solutions at temperatures of 110-200 C for durations of 6-240 h. The Co was preferentially leached out into the acidic solution, while the WC was oxidized to insoluble WO 3 hydrate which was subsequently separated by filtration. The hydrothermal treatment parameters such as solvent concentrations, treatment temperatures, holding time were optimized in respect to different kinds of WC-Co cermets. A hydrothermal oxidation treatment in 3M HNO 3 aqueous solution at 150 C for 24 h was capable of fully disintegrating the cermet chip composed of coarse WC grains of 1-5 μm in size with 20 wt% of Co as binder. While the more oxidation resistant specimen composed of fine WC grains of 0.5-1.0 μm in size with 13 wt% of Co, was completely disintegrated by a treatment in 7 M HNO 3 aqueous solution at 170 C for 24 h. The filtered solid residues were composed of fine WO 3 .0.33H 2 O powder and a small amount of WO 3 . The recovered WO 3 .0.33H 2 O powder can be easily returned to the industrial process for the synthesis of WC powder so that the overall recycling cost can be possibly lowered. (orig.)

  4. Neutronic calculations of AFPR-100 reactor based on Spherical Cermet Fuel particles

    International Nuclear Information System (INIS)

    Benchrif, A.; Chetaine, A.; Amsil, H.

    2013-01-01

    Highlights: • AFPR-100 reactor considered as a small nuclear reactor without on-site refueling originally based on TRISO micro-fuel element. • The AFPR-100 reactor was re-designed using the new Spherical Cermet fuel element. • The adoption of the Cermet fuel instead of TRISO fuel reduces the core lifetime operation by 3.1 equivalent full power years. • We discussed the new micro-fuel element candidate for small and medium sized reactors. - Abstract: The Atoms For Peace Reactor (AFPR-100), as a 100 MW(e) without the need of on-site refueling, was originally based on UO2 TRISO fuel coated particles embedded in a carbon matrix directly cooled by light water. AFPR-100 is considered as a small nuclear reactor without open-vessel refueling which is proposed by Pacific Northwest National Laboratory (PNNL). An account of significant irradiation swelling in the silicon carbide fission product barrier coating layer of TRISO fuel element, a Spherical Cermet Fuel element has been proposed. Indeed, the new fuel concept, which was developed by PNNL, consists of changing the pyro-carbon and ceramic coatings that are incompatible with low temperature by Zirconium. The latter was chosen to avoid any potential Wigner energy effect issues in the TRISO fuel element. Actually, the purpose of this study is to assess the goal of AFPR-100 concept using the Cermet fuel; undeniably, the fuel core lifetime prediction may be extended for reasonably long period without on-site refueling. In fact, we investigated some neutronic parameters of reactor core by the calculation code SRAC95. The results suggest that the core fuel lifetime beyond 12 equivalent full power years (EFPYs) is possible. Hence, the adoption of Cermet fuel concept shows a core lifetime decrease of about 3.1 EFPY

  5. Irradiation behaviour of UO2/Mo porous cermets for thermionic converters

    International Nuclear Information System (INIS)

    Stora, J.P.; Kauffmann, Y.

    1975-01-01

    Two types of UO 2 Mo porous cernets have been fabricated and irradiated in a Cythere irradiation device. The first cermet is constituted by little bits of dense fuel in which the two constituants are finely dispersed. The whole open porosity is located between the granules. This type of cermet is called breche (33.4vol%UO 2 , 51vol%Mo, 14.8vol%porosity). At the end of the irradiation the burn up was 19000MWd/t(U) and neither swelling of the cermet nor deformation of the can were noted. On the contrary, a shrinkage of the emitter was observed attributed to a fuel densification under irradiation. The second type of cermet is called macrogranule (36vol%UO 2 , 49vol%Mo 15vol%porosity). UO 2 granules of 0.07cm mean diameter are dispersed in the molybdenum matrix. The porosity is regularly distributed all around the UO 2 kernels. The post irradiation metrology shows that the emitter is fairly stable. Only a slight ovalisation of about 0.5% was noted, but the granules of UO 2 were redistributed inside the molybdenum matrix, overlapping the metallic cavity by a condensation-evaporation process. The matrix has crept into the central void and consequently the volume has grown and the whole porosity has increased from about 15% to about 23%. This creeping is due to the fission gas pressure in the molybdenum cavities after 3000 hours of irradiation. In conclusion two types of cermets have shown good behaviour under irradiation and should allow lifetimes of several thousand hours of operation for thermionic fuel elements [fr

  6. Cermet Fuel Element (FE) on the basis of micro fuel - FE prototype for future power engineering

    International Nuclear Information System (INIS)

    Fedik, I.; Deniskin, V.; Nalivaev, V.; Gavrilin, S.

    2006-01-01

    The FE with ceramic fuel and cladding of E110 alloy under average burnup depth of 43-45MW day/kg U with providing of 3 and 4 year operation periods are used successfully in WWER. The program had been developed for improving of the fuel cycles economical indexes and for further increasing the WWER operational characteristics. In this program the reactor safety increasing has been foreseen and also the coefficient of capacity using (KIUM) at the expense of the average implement of 55-60 MW day/kg U has been achieved. The program foresees also the integration of 5-6 year fuel cycle and other developments. It is planning to solve the pointed problems with help of traditional technical solution, directed to the improving of FE with ceramic fuel. In the present paper the design-engineering and experimental development results have been presented for creation of cermet FE on the basis of micro-fuel with matrix structure (in the further -the cermet FE) for WWER. The works have been carried out over period of the last 10 years in SRI SIA 'Luch' jointly with OKB 'Gidropress', VSRINM Bochvar name, RNTs 'Kurchatovsky institute', FEI and other. During the cermet FE introduction on the basis micro fuel at the NPP, external FE construction constant is kept. That allows installation of the new active zones without any sufficient changing of reactor installations constructions. Using of cermet FE in a new generation of WWER will allow to realize its quality in large volume, in particular, to create the first hermetic contour, to simplify and to reduce the price of safety systems, automatic adjustment, radiation protection, heat transfer purity, etc. The using of cermet FE, for example, in WWER may attach to the installation the exceeded operational properties of safety in different operation conditions, manoeuvrability, vibration strength, FA life time and FE geometrical stability

  7. Effect of hydrothermal treatment on light transmission of translucent zirconias.

    Science.gov (United States)

    Putra, Armand; Chung, Kwok-Hung; Flinn, Brian D; Kuykendall, Tuesday; Zheng, Cheng; Harada, Kosuke; Raigrodski, Ariel J

    2017-09-01

    Studies of the light transmission of translucent zirconias after hydrothermal treatment are limited. The purpose of this in vitro study was to evaluate the effect of hydrothermal treatment on the light transmission of translucent zirconias for monolithic restorations. Four commercially available zirconia products, BruxZir Anterior Solid Zirconia (BruxAnt, BA), Lava Plus High Translucency (LPHT), Katana Zirconia Super Translucent (KST), and Katana Zirconia Ultra Translucent (KUT) were assessed and 1 type of lithium disilicate, e.max Press LT (LDLT) was used as a control. Plate specimens, 20×20×1 mm (n=80) for the translucency assessment were sectioned from postsintered zirconia bulk materials and ground with a #400-grit diamond wheel and coolant. The specimens were placed under hydrothermal conditions of 134°C at 0.2 MPa (n=5 per group at 0, 5, 50, and 100 hours). Percentage of total transmittance of light (T t %) of each specimen was measured using a spectrophotometer with an integrating sphere. X-ray diffraction analyses were used to measure tetragonal-monoclinic phase transformation. Surfaces were examined by scanning electron microscopy and energy dispersive spectrometry. Data were analyzed using 2-way ANOVA followed by the Tukey test (α=.05). The T t % ranged from 6.5% to 28.3%. Group LDLT obtained significantly higher transmittance than other tested groups, whereas groups KST and KUT had significantly higher T t % than groups BA and LPHT (Phydrothermal treatment for all tested translucent zirconias and a lithium disilicate glass-ceramic control. Hydrothermal treatment had minimal effects on the translucency of translucent zirconias. The tetragonal-monoclinic phase transformation rate of translucent zirconias was found to be low, except in group LPHT. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  8. Influence of Zirconia on Hydroxyapatite Coating on Ti-Alloy by Laser Cladding

    Institute of Scientific and Technical Information of China (English)

    杜海燕; 霍伟荣; 高海; 王丽娟; 邱世鹏; 刘家臣

    2003-01-01

    Coating titanium alloy with the bioceramic material hydroxyapatite(HAP) has been used to improve the poor osteoinductive properties of pure titanium alloy. But in clinical applications, the mechanical failure of HAP-coated titanium alloy implant suffered at the interface of the HAP coatings and titanium alloy substrate will be a potential weakness in prosthesis. Yttria-stablized zirconia (YSZ) is expected to enhance the mechanical properties of the HAP coating and reduce the coefficient of thermal expansion difference between the coated layer and the substrate. These may reinforce the bonding strength between the coatings and the substrate. In this paper, HAP/YSZ composite coatings were cladded by laser. The effects of zirconia on the microstructure, mechanical properties and formation of tricalcium phosphate (TCP, Ca3(PO4)2) of the HAP/YSZ composite coatings were evaluated. XRD, SEM and TEM were used to investigate the phase composition, microstructure and morphology of the coatings. The experimental results showed that adding YSZ in coatings was favorable to the composition and stability of HAP, and to the improvement of the adhesion strength, microhardness and microtoughness. A well uniform, crack-free coating of HAP/YSZ composites was formed on Ti-alloy substrate by laser cladding.

  9. The development of fabrication techniques for europia/iron cermet tips for coarse-control arms in DIDO and PLUTO

    International Nuclear Information System (INIS)

    Moore, D.A.; Tarrant, E.A.

    1980-11-01

    The applicability of cermet-fabrication techniques to the production of europia/iron cermets for use as coarse-control arm tips in the materials test reactors DIDO and PLUTO has been investigated. Spheroids of europia were prepared by a dry agglomeration process. These were sintered, dispersed in iron powder and pressed into plates; the plates were then sintered to densify the iron matrix. These stages were optimised to produce a strong cermet with a europia density of >= 2.75 g/cm 3 . The uniformity of distribution of the absorber particles was confirmed by radiography, and adequate neutron-absorption worth by measurements carried out in the GLEEP reactor. An outline flow sheet has been prepared for the manufacture of europia/iron cermet plates suitable for use in the tips of DIDO and PLUTO coarse-control arms. (author)

  10. Temperature dependence of bending strength for plasma sprayed zirconia coating; Plasuma yosha zirconia himaku no magetsuyosa no ondo izonsei

    Energy Technology Data Exchange (ETDEWEB)

    Arai, M.; Sakuma, T. [Central Research Inst. of Electric Power Industry, Tokyo (Japan)] Mizutani, T. [Tokyo Inst. of Tech. (Japan)] Kishimoto, K. [Tokyo Inst. of Tech. (Japan). Faculty of Engineering] Saito, M. [Toshiba Corp. (Japan). Heavy Apparatus Engineering Lab.

    1998-02-01

    Plasma sprayed zirconia applying to the thermal barrier coating in gas turbine has been developing for protecting the hot parts such as blades and nozzles from high-temperature enviroments. In this paper, four point bending tests under various temperature conditions are conducted on plasma sprayed zirconia and its mechanical properties are examined. Results show that the bending strength at room temperature for plasma sprayed zirconia is much lower than that of sintered zirconia and is decreased with the increase in temperature. However, Weibull modulus at each temperature is relatively large and the dispersion of bending strength is very small in comparison with that of sintered zirconia. It is also clarified by the SEM observations of fracture surface that many defects such as debonding and microcrack are responsible for the lower bending strength. 9 refs., 8 figs., 1 tab.

  11. Magnesium Cermets and Magnesium-Beryllium Alloys; Cermets au magnesium et au magnesium-beryllium; Metallokeramicheskie magnievye i magnievo-berillievye splavy; Cermets de magnesio y aleaciones de magnesio y berillio

    Energy Technology Data Exchange (ETDEWEB)

    Ivanov, V. E.; Zelenskij, V. F.; Fajfer, S. I.; Zhdanov, S. M.; Maksimenko, V. I.; Savchenko, V. I. [Fiziko-Tekhnicheskij Institut an USSR, Khar' kov, SSSR (Russian Federation)

    1963-11-15

    The paper describes some results of work on the development of magnesium-magnesium oxide cermets and of super heat-resistant magnesiumberyllium alloys produced by powder metallurgical methods. The introduction of even a minute quantity of finely dispersed magnesium oxide into magnesium results in a strengthening of the material, the degree of which increases with increased magnesium oxide concentration, although variation of this concentration within the limits of 0.3 to 5 wt.% has a comparatively slight effect on the corresponding variation in the short-term strength over the whole range of temperatures investigated. At 20{sup o}C, in the case of the cermets, {sigma}{sub {beta}} = 28 to 31 kg/mm{sup 2} and {delta} = 3 .5 to 4.5%; at 500{sup o}C {sigma}{sub {beta}} = 2.6 to 3.2 kg/mm{sup 2} and {delta} =30 to 40%. The positive effect of the finely dispersed oxide phase is particularly evident in protracted tests. For magnesium cermets, {sigma} (300)/100 = 2.2 kg/mm{sup 2}. Characteristic of the mixtures is the high thermal stability of the strength properties, linked chiefly with the thermodynamic stability of the strength-giving oxide phase in the metal matrix. The use of powder metallurgical methods has yielded super heat-resistant magnesium-beryllium alloys containing heightened concentrations of beryllium (PMB alloys). In their strength characteristics PMB alloys are close to Mg-MgO cermets, but the magnesium-beryllium alloys have a degree and duration of resistance to high temperature oxidation which exceeds the corresponding qualities of the magnesium alloys at present known. Thus, in air of 580{sup o}C, PMB alloys with 2 to 5% beryllium maintain a high resistance to oxidation for a period of over 12000 to 14000 h. This long-term heat resistance is chiefly a result of the amount of beryllium in the alloy, and increases with increasing beryllium content. PMB alloys are also marked by high resistance to short bursts of overheating. Magnesium cermets and

  12. Studies of alumina additions in zirconia - magnesia

    International Nuclear Information System (INIS)

    Muccillo, R.

    1987-01-01

    Ionic conductivity measurements have been carried out in the 500 0 C - 1000 0 C temperature range in Mg - PSZ (Partially Stabilized Zirconia) with 0.5 to 10 mol % alumina additions. All specimens were prepared by pressing followed by pre - and sintering at 1000 0 C/2h and1450 0 C/4h, respectively. Thermal histerysis of the ionic conductivity have been detected, probably due to phase changes in the Mg-PSZ samples. The results show that alumina additions up to 2.1% enhances densification with no major variations in electrical resistivity values. (Author) [pt

  13. Analytical determination of thermal conductivity of W-UO2 and W-UN CERMET nuclear fuels

    Science.gov (United States)

    Webb, Jonathan A.; Charit, Indrajit

    2012-08-01

    The thermal conductivity of tungsten based CERMET fuels containing UO2 and UN fuel particles are determined as a function of particle geometry, stabilizer fraction and fuel-volume fraction, by using a combination of an analytical approach and experimental data collected from literature. Thermal conductivity is estimated using the Bruggeman-Fricke model. This study demonstrates that thermal conductivities of various CERMET fuels can be analytically predicted to values that are very close to the experimentally determined ones.

  14. Comparison of Amount of Primary Tooth Reduction Required for Anterior and Posterior Zirconia and Stainless Steel Crowns.

    Science.gov (United States)

    Clark, Larkin; Wells, Martha H; Harris, Edward F; Lou, Jennifer

    2016-01-01

    To determine if aggressiveness of primary tooth preparation varied among different brands of zirconia and stainless steel (SSC) crowns. One hundred primary typodont teeth were divided into five groups (10 posterior and 10 anterior) and assigned to: Cheng Crowns (CC); EZ Pedo (EZP); Kinder Krowns (KKZ); NuSmile (NSZ); and SSC. Teeth were prepared, and assigned crowns were fitted. Teeth were weighed prior to and after preparation. Weight changes served as a surrogate measure of tooth reduction. Analysis of variance showed a significant difference in tooth reduction among brand/type for both the anterior and posterior. Tukey's honest significant difference test (HSD), when applied to anterior data, revealed that SSCs required significantly less tooth removal compared to the composite of the four zirconia brands, which showed no significant difference among them. Tukey's HSD test, applied to posterior data, revealed that CC required significantly greater removal of crown structure, while EZP, KKZ, and NSZ were statistically equivalent, and SSCs required significantly less removal. Zirconia crowns required more tooth reduction than stainless steel crowns for primary anterior and posterior teeth. Tooth reduction for anterior zirconia crowns was equivalent among brands. For posterior teeth, reduction for three brands (EZ Pedo, Kinder Krowns, NuSmile) did not differ, while Cheng Crowns required more reduction.

  15. Effect of Carbon Content on the Microstructure and Mechanical Properties of NbC-Ni Based Cermets

    Directory of Open Access Journals (Sweden)

    Shuigen Huang

    2018-03-01

    Full Text Available The aim of this work was to correlate the overall carbon content in NbC-Ni, NbC-Ni-VC and NbC-Ni-Mo starting powders with the resulting microstructure, hardness, and fracture toughness of Ni-bonded NbC cermets. A series of NbC-Ni, NbC-Ni-VC and NbC-Ni-Mo cermets with different carbon content were prepared by conventional liquid phase sintering for 1 h at 1420 °C in vacuum. Microstructural analysis of the fully densified cermets was performed by electron probe microanalysis (EPMA to assess the effect of carbon and VC or Mo additions on the NbC grain growth and morphology. A decreased carbon content in the starting powder mixtures resulted in increased dissolution of Nb, V, and Mo in the Ni binder and a decreased C/Nb ratio in the NbC based carbide phase. The Vickers hardness (HV30 and Palmqvist indentation toughness were found to decrease significantly with an increasing carbon content in the Mo-free cermets, whereas an antagonistic correlation between hardness and toughness was obtained as a function of the Mo-content in Mo-modified NbC cermets. To obtain optimized mechanical properties, methods to control the total carbon content of NbC-Ni mixtures were proposed and the prepared cermets were investigated in detail.

  16. Zr-ZrO sub 2 cermet solar coatings designed by modelling calculations and deposited by dc magnetron sputtering

    CERN Document Server

    Zhang Qi Chu; Lee, K D; Shen, Y G

    2003-01-01

    High solar performance Zr-ZrO sub 2 cermet solar coatings were designed using a numerical computer model and deposited experimentally. The layer thickness and Zr metal volume fraction for the Zr-ZrO sub 2 cermet solar selective coatings on a Zr or Al reflector with a surface ZrO sub 2 or Al sub 2 O sub 3 anti-reflection layer were optimized to achieve maximum photo-thermal conversion efficiency at 80 deg. C under concentration factors of 1-20 using the downhill simplex method in multi-dimensions in the numerical calculation. The dielectric function and the complex refractive index of Zr-ZrO sub 2 cermet materials were calculated using Sheng's approximation. Optimization calculations show that Al sub 2 O sub 3 /Zr-ZrO sub 2 /Al solar coatings with two cermet layers and three cermet layers have nearly identical solar absorptance, emittance and photo-thermal conversion efficiency that are much better than those for films with one cermet layer. The optimized Al sub 2 O sub 3 /Zr-ZrO sub 2 /Al solar coating film w...

  17. Effect of TaC addition on the microstructures and mechanical properties of Ti(C, N)-based cermets

    International Nuclear Information System (INIS)

    Wu, Peng; Zheng, Yong; Zhao, Yongle; Yu, Haizhou

    2010-01-01

    The microstructures of the prepared Ti(C, N)-based cermets with various TaC additions were studied using X-ray diffractometry (XRD) and scanning electron microscopy (SEM). Mechanical properties such as transverse rupture strength (TRS), fracture toughness (K 1C ) and hardness (HRA) were also measured. The results showed that the grain size of the cermets decreased with increasing TaC addition, but too high TaC addition resulted in agglomeration of the grains. An increasing TaC addition increased the dissolution of tungsten, titanium, molybdenum and tantalum in the binder phase. The hardness of the cermets decreased slightly with increasing TaC addition. The transverse rupture strength was the highest for the cermets with 5 wt.% TaC addition, which was characterized by fine grains, homogeneous microstructure and the moderate thickness of rim phase in the binder. The fracture toughness of the cermets with TaC addition from 0 to 5 wt.% decreased obviously, which resulting from decreased grain size. The further decreasing of fracture toughness for the cermets with 7 wt.% TaC addition was due to increased porosity and interfacial tensile stress.

  18. Densification of zirconia films by coevaporation with silica

    International Nuclear Information System (INIS)

    Feldman, A.; Farabaugh, E.N.

    1985-04-01

    Optical films of zirconia have been receiving considerable attention because of their potential use as the high-index layer in multilayer optical coatings for the ultraviolet portion of the spectrum. Several problems are associated with electron-beam deposited zirconia films, including index instability and index inhomogeneity. The index instability is caused by the adsorption and the desorption of water in the porous columnar structure of the zirconia films. Index inhomogeneity is due to the inhomogeneous structure in the films. Recent work has shown that the first several tens of nanometers of a film possess a cubic structure, whereas the outmost layers possess a monoclinic structure. One approach for producing bulk-like zirzonia films that is receiving considerable attention at present is ion-assisted electron-beam deposition. This is because the method has successfully produced zirconia films having bulk-like densities and refractive indices that show insignificant sensitivity to water adsorption. In this paper a similar effect is demonstrated when mixed zirconia:silica films are produced by coevaporation from independent electron-beam sources, and, in particular, it is shown that the admixture of a small amount of silica with the zirconia produces a film possessing a higher refractive index than a pure zirconia film

  19. J-integral evaluation of nanoclay-modified HDPE/PA6 microfibrillar composites

    Czech Academy of Sciences Publication Activity Database

    Kelnar, Ivan; Hodan, Jiří; Kaprálková, Ludmila; Kratochvíl, Jaroslav; Hromádková, Jiřina; Kotek, Jiří

    2017-01-01

    Roč. 58, April (2017), s. 54-59 ISSN 0142-9418 R&D Projects: GA ČR(CZ) GA13-15255S Institutional support: RVO:61389013 Keywords : nanocomposite * blend * melt drawing Subject RIV: JI - Composite Materials OBOR OECD: Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics Impact factor: 2.464, year: 2016

  20. Method of making a cermet fuel electrode containing an inert additive

    Science.gov (United States)

    Jensen, Russel R.

    1992-01-01

    An electrode is attached to a solid electrolyte material by: (1) mixing a metallic nickel component and 1 wt% to 10 wt% of yttria stabilized zirconia having particle diameters up to 3 micrometers with an organic binder solution to form a slurry, (2) applying the slurry to a solid zirconia electrolyte material, (3) heating the slurry to drive off the organic binder and form a porous layer of metallic nickel substantially surrounded and separated by the zirconia particles, and (4) electro-chemical vapor depositing a skeletal structure between and around the metallic nickel and the zirconia particles where the metallic nickel components do not substantially sinter to each other, yet the layer remains porous.