  1. Optical properties of zinc lead tellurite glasses

    Directory of Open Access Journals (Sweden)

    Salah Hassan Alazoumi

    2018-06-01

    Full Text Available Tellurite glass systems in the form of [ZnO]x [(TeO20.7-(PbO0.3]1-x with x = 0.15, 0.17, 0.20, 0.22 and 0.25 mol% were prepared using the melt quenching technique. XRD of the prepared samples have been measured for all samples. Both FTIR (280–4000 cm−1 and UV-Vis (200–800 nm spectra have been measured. Optical band gap and refractive index were calculated for every glass sample. Density of glass, molar volume and oxygen packing density (OPD were obtained. Values of the direct, indirect band gap ranged were found in the range 3.41–3.94 eV and 2.40–2.63 eV with increasing of ZnO concentration. Refractive index 2.58 and dielectric constant 6.66 were heigh at 17 ZnO mol% concentration. Molar polarizability, metallization criterion, polaron radius have been calculated for every glass composition. Keywords: Tellurite, Glass, Optical band gap, Refractive index

  2. Optical properties of zinc lead tellurite glasses

    Science.gov (United States)

    Alazoumi, Salah Hassan; Aziz, Sidek Abdul; El-Mallawany, R.; Aliyu, Umar Sa'ad; Kamari, Halimah Mohamed; Zaid, Mohd Hafiz Mohd Mohd; Matori, Khamirul Amin; Ushah, Abdulbaset

    2018-06-01

    Tellurite glass systems in the form of [ZnO]x [(TeO2)0.7-(PbO)0.3]1-x with x = 0.15, 0.17, 0.20, 0.22 and 0.25 mol% were prepared using the melt quenching technique. XRD of the prepared samples have been measured for all samples. Both FTIR (280-4000 cm-1) and UV-Vis (200-800 nm) spectra have been measured. Optical band gap and refractive index were calculated for every glass sample. Density of glass, molar volume and oxygen packing density (OPD) were obtained. Values of the direct, indirect band gap ranged were found in the range 3.41-3.94 eV and 2.40-2.63 eV with increasing of ZnO concentration. Refractive index 2.58 and dielectric constant 6.66 were heigh at 17 ZnO mol% concentration. Molar polarizability, metallization criterion, polaron radius have been calculated for every glass composition.

  3. Optical, physical and structural studies of boro-zinc tellurite glasses

    International Nuclear Information System (INIS)

    Gayathri Pavani, P.; Sadhana, K.; Chandra Mouli, V.

    2011-01-01

    To investigate the modification effect of the modifier ZnO on boro-tellurite glass, a series of glasses with compositions 50B 2 O 3 -(50-x)ZnO-xTeO 2 have been prepared by conventional melt quenching technique. Amorphous nature of the samples was confirmed through X-ray diffraction technique. Optical absorption and IR structural studies are carried out on the glass system. The optical absorption studies revealed that the cutoff wavelength increases while optical band gap (E opt ) and Urbach energy decreases with an increase of ZnO content. Refractive index evaluated from E opt was found to increase with an increase of ZnO content. The compositional dependence of different physical parameters such as density, molar volume, oxygen packing density, optical basicity, have been analyzed and discussed. The IR studies showed that the structure of glass consists of TeO 4 , TeO 3 /TeO 3+1 , BO 3 , BO 4 and ZnO 4 units. -- Research highlights: → Novel boro-zinc tellurite ternary glasses that can compete with boro-tellurite and zinc tellurite glasses are successfully prepared. → Boro-zinc tellurite ternary glasses are of higher refractive index compared with zinc tellurite glasses. → Optical, physical and structural properties of the novel ternary glass system are explained.→ At 30 mol% of ZnO, TeO 4 is replaced by ZnO 4 indicating the presence of ZnO 4 network.

  4. Optical Properties of Erbium Zinc Tellurite Glass System

    Directory of Open Access Journals (Sweden)

    Sidek Hj. Abdul Aziz

    2015-01-01

    Full Text Available Er3+-doped tellurite glasses with molar compositions of xEr2O3-20ZnO-(80-xTeO2 (x=0, 1, 2, 3, and 4 mole% (EZT have been successfully synthesized by the melt-quenching method. Density and molar volume have been measured. UV-VIS absorption spectra in the wavelength range of 400–800 nm at room temperature has been measured. The band gap for every composition has been calculated. Photoluminescence spectroscopy in the wavelength range of 400–650 nm and at room temperature has been evaluated.

  5. Spectroscopic investigation of zinc tellurite glasses doped with Yb3 + and Er3 + ions

    Science.gov (United States)

    Bilir, Gökhan; Kaya, Ayfer; Cinkaya, Hatun; Eryürek, Gönül

    2016-08-01

    This paper presents a detailed spectroscopic investigation of zinc tellurite glasses with the compositions (0.80 - x - y) TeO2 + (0.20) ZnO + xEr2O3 + yYb2O3 (x = 0, y = 0; x = 0.004, y = 0; x = 0, y = 0.05 and x = 0.004, y = 0.05 per moles). The samples were synthesized by the conventional melt quenching method. The optical absorption and emission measurements were conducted at room temperature to determine the spectral properties of lanthanides doped zinc tellurite glasses and, to study the energy transfer processes between dopant lanthanide ions. The band gap energies for both direct and indirect possible transitions and the Urbach energies were measured from the absorption spectra. The absorption spectra of the samples were analyzed by using the Judd-Ofelt approach. The effect of the ytterbium ions on the emission properties of erbium ions was investigated and the energy transfer processes between dopant ions were studied by measuring the up-conversion emission properties of the materials. The color quality parameters of obtained visible up-conversion emission were also determined as well as possibility of using the Er3 + glasses as erbium doped fiber amplifiers at 1.55 μm in infrared emission region.

  6. Spectroscopic investigation of zinc tellurite glasses doped with Yb(3+) and Er(3+) ions.

    Science.gov (United States)

    Bilir, Gökhan; Kaya, Ayfer; Cinkaya, Hatun; Eryürek, Gönül

    2016-08-05

    This paper presents a detailed spectroscopic investigation of zinc tellurite glasses with the compositions (0.80-x-y) TeO2+(0.20) ZnO+xEr2O3+yYb2O3 (x=0, y=0; x=0.004, y=0; x=0, y=0.05 and x=0.004, y=0.05 per moles). The samples were synthesized by the conventional melt quenching method. The optical absorption and emission measurements were conducted at room temperature to determine the spectral properties of lanthanides doped zinc tellurite glasses and, to study the energy transfer processes between dopant lanthanide ions. The band gap energies for both direct and indirect possible transitions and the Urbach energies were measured from the absorption spectra. The absorption spectra of the samples were analyzed by using the Judd-Ofelt approach. The effect of the ytterbium ions on the emission properties of erbium ions was investigated and the energy transfer processes between dopant ions were studied by measuring the up-conversion emission properties of the materials. The color quality parameters of obtained visible up-conversion emission were also determined as well as possibility of using the Er(3+) glasses as erbium doped fiber amplifiers at 1.55μm in infrared emission region. Copyright © 2016 Elsevier B.V. All rights reserved.

  7. Synthesis and characterization of barium fluoride substituted zinc tellurite glasses

    Science.gov (United States)

    Aishwarya, K.; Vinitha, G.; Varma, G. Sreevidya; Asokan, S.; Manikandan, N.

    2017-12-01

    Glasses in the TeO2-ZnO-BaF2 system were prepared by standard melt quenching technique and were characterized for their thermal, optical and structural properties. Samples were found to show good thermal stability with values ranging above 100 °C for all the compositions. Optical bandgap and refractive index values were calculated from linear optical measurements using UV-Vis spectroscopy. Infrared spectra showed the presence of hydroxyl groups in the glasses indicating that the effect of fluorine was negligible in removing the hydroxyl impurities for the experimental conditions and compositions used. Raman measurements showed the modification occurring in the glass network due to addition of barium fluoride in terms of increase in the formation of non-bridging oxygen atoms compared to strong Te-O-Te linkages in the glass matrix.

  8. Thermal and structural properties of zinc modified tellurite based glasses

    Energy Technology Data Exchange (ETDEWEB)

    Kundu, R. S., E-mail: rskundu2007@gmail.com; Dhankhar, Sunil; Dult, Meenakshi [Department of Applied Physics, G.J.University of Science & Technology,Hisar-125001, Haryana (India); Punia, R. [Department of Physics, Indira Gandhi University, Meerpur-123401, Rewari, Haryana (India); Kishore, N. [Department of Physics, Central University of Haryana, Mahendergarh-123029, Haryana (India)

    2016-05-23

    Glass system 60 TeO{sub 2} – 10 B{sub 2}O{sub 3}-(30-x) Bi{sub 2}O{sub 3}-x ZnO with mole fraction x = 10, 15, 20, 25 and 30 were synthesized by conventional melt quenching technique under controlled atmospheric conditions. The glass transition temperature (T{sub g}) has been determined using differential scanning Calorimetry (DSC) and its value is observed to increase with increase in ZnO content. This increase may be due to the increase in the concentration of the bridging oxygen (BO) atoms. IR and Raman spectra of the present glass system indicate that ZnO acts as network modifier and exists in ZnO{sub 4} units. TeO{sub 2} exists as TeO{sub 3}, TeO{sub 4}, and TeO{sub 3+1} structural units. Bismuth plays the role of network modifier with BiO{sub 6} octahedral structural units whereas B{sub 2}O{sub 3} exists in the form of BO{sub 3} trigonal and BO{sub 4} tetrahedral structural units.

  9. Thermal and structural properties of zinc modified tellurite based glasses

    Science.gov (United States)

    Kundu, R. S.; Dhankhar, Sunil; Punia, R.; Dult, Meenakshi; Kishore, N.

    2016-05-01

    Glass system 60 TeO2 - 10 B2O3-(30-x) Bi2O3-x ZnO with mole fraction x = 10, 15, 20, 25 and 30 were synthesized by conventional melt quenching technique under controlled atmospheric conditions. The glass transition temperature (Tg) has been determined using differential scanning Calorimetry (DSC) and its value is observed to increase with increase in ZnO content. This increase may be due to the increase in the concentration of the bridging oxygen (BO) atoms. IR and Raman spectra of the present glass system indicate that ZnO acts as network modifier and exists in ZnO4 units. TeO2 exists as TeO3, TeO4, and TeO3+1 structural units. Bismuth plays the role of network modifier with BiO6 octahedral structural units whereas B2O3 exists in the form of BO3 trigonal and BO4 tetrahedral structural units.

  10. Role of lithium ions on the physical, structural and optical properties of zinc boro tellurite glasses

    Science.gov (United States)

    Rani, S.; Ahlawat, N.; Parmar, R.; Dhankhar, S.; Kundu, R. S.

    2018-01-01

    Lithium zinc boro tellurite glasses with compositions xLi2O-(100-x) [0.25ZnO-0.15B2O3-0.60TeO2] [where x = 0, 5, 10, 15 and 20 mol%] have been prepared by melt-quench technique. The amorphous nature of the prepared system is ascertained by X-ray diffraction. The density and molar volume are found to decrease with the increase in concentration of Li2O. The differential scanning calorimetry is used to calculate the glass transition temperature (Tg) and the observed values are found to be decreased. The IR and Raman spectra indicate that Li2O acts as a network modifier in the glass matrix. In the present system, tellurium exists as TeO4 and TeO3, B2O3 in the form of BO4 and BO3 and zinc oxide exists as ZnO4 structural units. The values of the optical band gap are estimated from the fitting of Mott and Davis's and model. A better convergence is achieved between experimental observed spectra of absorption coefficient and hydrogenic excitonic model. The optical band gap energy increases, whereas refractive index and molar refractivity follow the reverse trend with Li2O. The range of metallization criterion suggests that these glasses may be a potential candidate for nonlinear optical materials.

  11. Improved ionic conductivity of lithium-zinc-tellurite glass-ceramic electrolytes

    Directory of Open Access Journals (Sweden)

    W. Widanarto

    Full Text Available An enhancement in the secondary battery safety demands the optimum synthesis of glass-ceramics electrolytes with modified ionic conductivity. To achieve improved ionic conductivity and safer operation of the battery, we synthesized Li2O included zinc-tellurite glass-ceramics based electrolytes of chemical composition (85-xTeO2·xLi2O·15ZnO, where x = 0, 5, 10, 15 mol%. Samples were prepared using the melt quenching method at 800 °C followed by thermal annealing at 320 °C for 3 h and characterized. The effects of varying temperature, alternating current (AC frequency and Li2O concentration on the structure and ionic conductivity of such glass-ceramics were determined. The SEM images of the annealed glass-ceramic electrolytes displayed rough surface with a uniform distribution of nucleated crystal flakes with sizes less than 1 μm. X-ray diffraction analysis confirmed the well crystalline nature of achieved electrolytes. Incorporation of Li2O in the electrolytes was found to generate some new crystalline phases including hexagonal Li6(TeO6, monoclinic Zn2Te3O8 and monoclinic Li2Te2O5. The estimated crystallite size of the electrolyte was ranged from ≈40 to 80 nm. AC impedance measurement revealed that the variation in the temperatures, Li2O contents, and high AC frequencies have a significant influence on the ionic conductivity of the electrolytes. Furthermore, electrolyte doped with 15 mol% of Li2O exhibited the optimum performance with an ionic conductivity ≈2.4 × 10−7 S cm−1 at the frequency of 54 Hz and in the temperature range of 323–473 K. This enhancement in the conductivity was attributed to the sizable alteration in the ions vibration and ruptures of covalent bonds in the electrolytes network structures. Keywords: Zinc-tellurite, Glass-ceramics, X-ray diffraction, Ionic conductivity, Lithium oxide

  12. Synthesis and different optical properties of Gd2O3 doped sodium zinc tellurite glasses

    Science.gov (United States)

    Samanta, Buddhadev; Dutta, Dibakar; Ghosh, Subhankar

    2017-06-01

    A series of Gd2O3 doped sodium zinc tellurite [xGd2O3-(0.8-x) TeO2-0.1Na2O-0.1ZnO] glasses are prepared by the conventional melt quenching method and their optical properties have been studied. UV-vis spectrophotometric studies within the wavelength range from 230 nm-800 nm are carried out in the integrating sphere mode to study the effect of Gd2O3 doping on the optical band gap (Eg), refractive index (n), dielectric constant (εr) and susceptibility (χ). Other physical properties like molar volume, molar refraction, polarizability, metallization criterion, number density of rare-earth ions (N), polaron radius (rp), inter ionic distance (ri), molar cation polarizability (∑αi), number of oxide ions in chemical composition (NO2-), optical band gap based electronic oxide ion polarizability (αO2-) and optical basicity (Λ) of glass samples have been studied on the basis of UV-vis spectra and density profile of the different glasses.

  13. Concentration dependent luminescence quenching of Er{sup 3+}-doped zinc boro-tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Said Mahraz, Zahra Ashur; Sahar, M.R., E-mail: mrahim057@gmail.com; Ghoshal, S.K.; Reza Dousti, M.

    2013-12-15

    Understanding the mechanism of luminescence quenching in rare earth doped tellurite glass is an important issue. The Er{sup 3+}-doped boro-tellurite glasses with compositions 30B{sub 2}O{sub 3}+10ZnO+(60−x)TeO{sub 2}+xEr{sub 2}O{sub 3} (where x=0, 0.5, 1, 1.5 and 2 mol%) were prepared by melt quenching method. Structural and optical properties of the proposed glasses were characterized using XRD, FTIR, density, UV–vis-IR absorption and PL spectroscopy. The amorphous nature of these glasses was confirmed by XRD technique. The IR-spectrum reveals five absorption bands assigned to different B–O and Te–O vibrational groups. UV–vis-IR absorption spectrum exhibits seven absorption bands at 6553, 10,244, 12,547, 15,360, 19,230, 20,661 and 22,522 cm{sup −1} corresponding to {sup 4}I{sub 13/2}, {sup 4}I{sub 11/2}, {sup 4}I{sub 9/2}, {sup 4}F{sub 9/2}, {sup 2}H{sub 11/2}, {sup 4}F{sub 7/2} and {sup 4}F{sub 3/2} excited states of Er{sup 3+} ion respectively. The optical band gap energy (E{sub opt}) corresponding to the direct and indirect allowed transitions decreased, while the Urbach energy and cut-off wavelengths are increased by the introduction of Er{sup 3+} ions. The refractive index, density and phonon cut-off edge of the samples are increased and the molar volume decreased with the further addition of dopants. The Judd–Ofelt parameter (Ω{sub 2}) decreased from 5.73 to 3.13×10{sup −20} cm{sup 2} with the increase of erbium ions concentration from 0.5 to 2 mol%. The PL spectra show green emissions for the transition from {sup 2}H{sub 11/2} and {sup 4}S{sub 3/2} excited states to {sup 4}I{sub 15/2} ground state, which show strong quenching due to the addition of Er{sup 3+} ions. -- Highlights: • Er{sup 3+}-doped zinc boro-tellurite glass has been synthesized by melt quench method. • Spectroscopic properties dependent concentration is analyzed by different techniques. • Judd–Ofelt intensity parameter (Ω{sub 2}) decreased by increase in erbium

  14. Improved ionic conductivity of lithium-zinc-tellurite glass-ceramic electrolytes

    Science.gov (United States)

    Widanarto, W.; Ramdhan, A. M.; Ghoshal, S. K.; Effendi, M.; Cahyanto, W. T.; Warsito

    An enhancement in the secondary battery safety demands the optimum synthesis of glass-ceramics electrolytes with modified ionic conductivity. To achieve improved ionic conductivity and safer operation of the battery, we synthesized Li2O included zinc-tellurite glass-ceramics based electrolytes of chemical composition (85-x)TeO2·xLi2O·15ZnO, where x = 0, 5, 10, 15 mol%. Samples were prepared using the melt quenching method at 800 °C followed by thermal annealing at 320 °C for 3 h and characterized. The effects of varying temperature, alternating current (AC) frequency and Li2O concentration on the structure and ionic conductivity of such glass-ceramics were determined. The SEM images of the annealed glass-ceramic electrolytes displayed rough surface with a uniform distribution of nucleated crystal flakes with sizes less than 1 μm. X-ray diffraction analysis confirmed the well crystalline nature of achieved electrolytes. Incorporation of Li2O in the electrolytes was found to generate some new crystalline phases including hexagonal Li6(TeO6), monoclinic Zn2Te3O8 and monoclinic Li2Te2O5. The estimated crystallite size of the electrolyte was ranged from ≈40 to 80 nm. AC impedance measurement revealed that the variation in the temperatures, Li2O contents, and high AC frequencies have a significant influence on the ionic conductivity of the electrolytes. Furthermore, electrolyte doped with 15 mol% of Li2O exhibited the optimum performance with an ionic conductivity ≈2.4 × 10-7 S cm-1 at the frequency of 54 Hz and in the temperature range of 323-473 K. This enhancement in the conductivity was attributed to the sizable alteration in the ions vibration and ruptures of covalent bonds in the electrolytes network structures.

  15. Structure of zinc and niobium tellurite glasses by neutron and x-ray diffraction

    International Nuclear Information System (INIS)

    Hoppe, U; Yousef, E; Ruessel, C; Neuefeind, J; Hannon, A C

    2004-01-01

    Neutron and x-ray diffraction experiments of high resolving power with neutrons from a spallation source and high-energy photons from a synchrotron have been performed on compositional series of binary Zn, Nb and on mixed Zn/Nb tellurite glasses. The Te-O, Zn-O and Nb-O coordination numbers are determined by Gaussian fitting of the first-neighbour peaks in the neutron and x-ray data simultaneously. The transition of TeO 4 to TeO 3 units with increasing fraction of a second component is indicated by decreasing total Te-O coordination numbers. This transition appears different for glasses with ZnO or Nb 2 O 5 additions. Details of the Te-O peaks suggest there are two species of Te-O bonds with lengths of ∼ 0.19 and ∼ 0.21 nm. The change of their fractions shows excellent agreement with the existence of TeO 4 trigonal bipyramids and TeO 3 trigonal pyramids. All oxygen atoms from ZnO and Nb 2 O 5 are used for rupture of Te-O-Te bridges, which is accompanied with a change of nearly all participating TeO 4 to TeO 3 groups. The tendency for a TeO 4 → TeO 3 change decreases for glasses of higher second component content which is accompanied by the occurrence of TeO 4 groups with non-bridging oxygens. The Nb tellurite glasses show transition to network-forming behaviour with the formation of Nb-O-Nb bridges. The fractions of TeO 3 units of ternary Zn/Nb tellurite glasses agree with an additivity behaviour of the modifying effects of ZnO and Nb 2 O 5 additions

  16. Structure of zinc and niobium tellurite glasses by neutron and x-ray diffraction

    Science.gov (United States)

    Hoppe, U.; Yousef, E.; Rüssel, C.; Neuefeind, J.; Hannon, A. C.

    2004-03-01

    Neutron and x-ray diffraction experiments of high resolving power with neutrons from a spallation source and high-energy photons from a synchrotron have been performed on compositional series of binary Zn, Nb and on mixed Zn/Nb tellurite glasses. The Te-O, Zn-O and Nb-O coordination numbers are determined by Gaussian fitting of the first-neighbour peaks in the neutron and x-ray data simultaneously. The transition of TeO4 to TeO3 units with increasing fraction of a second component is indicated by decreasing total Te-O coordination numbers. This transition appears different for glasses with ZnO or Nb2O5 additions. Details of the Te-O peaks suggest there are two species of Te-O bonds with lengths of {\\sim }0.19 and {\\sim }0.21 nm. The change of their fractions shows excellent agreement with the existence of TeO4 trigonal bipyramids and TeO3 trigonal pyramids. All oxygen atoms from ZnO and Nb2O5 are used for rupture of Te-O-Te bridges, which is accompanied with a change of nearly all participating TeO4 to TeO3 groups. The tendency for a {\\mathrm {TeO}}_{4} \\to {\\mathrm {TeO}}_{3} change decreases for glasses of higher second component content which is accompanied by the occurrence of TeO4 groups with non-bridging oxygens. The Nb tellurite glasses show transition to network-forming behaviour with the formation of Nb-O-Nb bridges. The fractions of TeO3 units of ternary Zn/Nb tellurite glasses agree with an additivity behaviour of the modifying effects of ZnO and Nb2O5 additions. Some of these results have already been presented in thesis work: Yousef E 2003 A study of some physical properties of tellurite glass (Al-Azhar University, Assiut Egypt).

  17. Effect of AlF3 on the Density and Elastic Properties of Zinc Tellurite Glass Systems

    Science.gov (United States)

    Sidek, Haji Abdul Aziz; Rosmawati, Shaharuddin; Halimah, Mohamed Kamari; Matori, Khamirul Amin; Talib, Zainal Abidin

    2012-01-01

    This paper presents the results of the physical and elastic properties of the ternary zinc oxyfluoro tellurite glass system. Systematic series of glasses (AlF3)x(ZnO)y(TeO2)z with x = 0–19, y = 0–20 and z = 80, 85, 90 mol% were synthesized by the conventional rapid melt quenching technique. The composition dependence of the physical, mainly density and molar volume, and elastic properties is discussed in term of the AlF3 modifiers addition that are expected to produce quite substantial changes in their physical properties. The absence of any crystalline peaks in the X-ray diffraction (XRD) patterns of the present glass samples indicates the amorphous nature. The addition of AlF3 lowered the values of the densities in ternary oxyfluorotellurite glass systems. The longitudinal and transverse ultrasonic waves propagated in each glass sample were measured using a MBS8020 ultrasonic data acquisition system. All the velocity data were taken at 5 MHz frequency and room temperature. The longitudinal modulus (L), shear modulus (G), Young’s modulus (E), bulk modulus (K) and Poisson’s ratio (σ) are obtained from both velocities data and their respective density. Experimental data shows the density and elastic moduli of each AlF3-ZnO-TeO2 series are found strongly depend upon the glass composition. The addition of AlF3 modifiers into the zinc tellurite causes substantial changes in their density, molar volume as well as their elastic properties.

  18. Prominent spectral features of Sm3+ ion in disordered zinc tellurite glass

    Directory of Open Access Journals (Sweden)

    Y.A. Tanko

    Full Text Available Trivalent rare earth doped glasses with modified spectroscopic features are essential for solid state lasers and diverse photonic applications. Glass composition optimisation may fulfil such demand. Stimulating the spectral properties of samarium (Sm3+ ions in tellurite glass host with desired enhancement is the key issue. Glasses with composition (80 − xTeO2–20ZnO–(xSm2O3, where 0 ⩽ x ⩽ 1.5 mol% are prepared using melt quenching method. The role of varying Sm3+ contents to improving the absorption and emission properties of the prepared glasses are determined. XRD pattern verifies amorphous nature of synthesised glasses. FTIR spectroscopy has been used to observe the structural modification of (TeO4 trigonal bipyramid structural units. DTA traces display prominent transition peaks for glass transition, crystallisation and melting temperature. Samples are discerned to be stable with desired Hruby parameter and superior glass forming ability. The UV–Vis–NIR absorption spectra reveals nine peaks centred at 470, 548, 947, 1085, 1238, 1385, 1492, 1550 and 1589 nm. These bands arise due to 6H5/2 → 4I11/2, 4G5/2, 6F11/2, 6F9/2, 6F7/2, 6F5/2, 6F3/2, 6H15/2 and 6F1/2 transitions, respectively. The direct, indirect band gap and Urbach energy calculated from the absorption edge of UV–Vis–NIR spectra are found to appear within (2.75–3.18 eV, (3.22–3.40 eV, and (0.20–0.31 eV, respectively. The observed increase in refractive index from 2.45 to 2.47 is ascribed to the generation of non-bridging oxygen atoms via the conversion of TeO4 into TeO3 units. Conversely the decrease in refractive index to 2.39 is attributed to the lower ionic radii (1.079 Å of Sm3+. PL spectra under the excitation of 452 nm display four emission bands centred at 563, 600, 644 and 705 nm corresponding to 4G5/2 → 6H5/2, 6H7/2, 6H9/2 and 6H11/2 transitions of samarium ions. Excellent features of the results nominate these compositions

  19. Spectroscopic study of Pr3+ ions doped Zinc Lead Tungsten Tellurite glasses for visible photonic device applications

    Science.gov (United States)

    Sharma, Ritu; Rao, A. S.; Deopa, Nisha; Venkateswarlu, M.; Jayasimhadri, M.; Haranath, D.; Prakash, G. Vijaya

    2018-04-01

    Zinc Lead Tungsten Tellurite (ZnPbWTe) glasses doped with different Pr3+ ion concentrations having the composition 5ZnO + 15PbO + 20WO3 + (60-x)TeO2 + xPr6O11 (where x = 0.5, 1, 1.5, 2.0 and 2.5 mol%) were prepared by using sudden quenching technique and characterized to understand their visible emission characteristic features using spectroscopic techniques such as absorption, excitation and emission. The Judd-Ofelt (J-O) theory has been applied to the absorption spectral features with an aim to evaluate various radiative properties for the prominent fluorescent levels of Pr3+ions in the as-prepared glasses. The emission spectra recorded for the as-prepared glasses under 468 nm excitation show three prominent emission transitions 3P0→3H6, 3P0→3F2 and 3P1→3F4, of which 3P0→3F2 observed in visible red region (648 nm), is relatively more intense. The intensity of 3P0→3F2 emission transition in the titled glasses increases up to 1mol% of Pr3+ ions and beyond concentration quenching is observed. Branching ratios (βR) and emission cross-sections (σse) were estimated for 3P0→3F2 transition to understand the luminescence efficiency in visible red region (648 nm). The CIE chromaticity coordinates were also evaluated in order to understand the suitability of these glasses for visible red luminescence devices. From the emission cross-sections, quantum efficiency and CIE coordinates, it was concluded that 1mol% of Pr3+ ions in ZnPbWTe glasses are quite suitable for preparing visible reddish orange luminescent devices.

  20. Electrical conductivity and modulus formulation in zinc modified bismuth boro-tellurite glasses

    Science.gov (United States)

    Dhankhar, Sunil; Kundu, R. S.; Dult, Meenakshi; Murugavel, S.; Punia, R.; Kishore, N.

    2016-09-01

    The ac conductivity of zinc modified tellurium based quaternary glasses having composition 60 TeO2-10 B2O3-(30 - x) Bi2O3-x ZnO; x = 10, 15, 20, 25 and 30 has been investigated in the frequency range 10-1-105 Hz and in temperature range 483-593 K. Frequency and temperature dependent ac conductivity found to obey Jonscher power law modified by Almond-West. DC conductivity, crossover frequency and frequency exponent have been estimated from the fitting of the experimental data of conductivity with Jonscher power law modified by Almond-West. The ac conductivity and its frequency exponent have been analyzed by various theoretical models. In presently studied glasses ac conduction takes place via tunneling of overlapping large polaron tunneling. Activation energy is found to be increased with increase in zinc content and dc conduction takes place via variable range hopping proposed by Mott with some modification suggested by Punia et al. The value of the stretched exponent ( β) obtained by fitting of M^' ' }} reveals the presence of non-Debye type relaxation. Scaling spectra of ac conductivity and electric modulus collapse into a single master curve for all compositions and temperatures, reveals the presence of composition and temperature independent conduction and relaxation process in these glasses. Activation energy of conduction ( W) and electric modulus ( E R ) are nearly equal, indicating that polaron have to overcome the same energy barrier during conduction as well as relaxation processes.

  1. Zinc chloride modified electronic transport and relaxation studies in barium-tellurite glasses

    Science.gov (United States)

    Dhankhar, Sunil; Kundu, R. S.; Rani, Sunita; Sharma, Preeti; Murugavel, S.; Punia, Rajesh; Kishore, N.

    2017-09-01

    The ac conductivity of halide based tellurium glasses having composition 70 TeO2-(30-x) BaO-x ZnCl2; x = 5, 10, 15, 20 and 25 has been investigated in the frequency range 10-1 Hz to 105Hz and in the temperature range 453 K to 553 K. The frequency and temperature dependent ac conductivity show mixed behaviour with increase in halide content and found to obey Jonscher's universal power law. The values of dc conductivity, crossover frequency and frequency exponent have been estimated from the fitting of experimental data of ac conductivity with Jonscher's universal power law. For determining the conduction mechanism in studied glass system, frequency exponent has been analyzed by various theoretical models. In presently studied glasses, the ac conduction takes place via overlapping large polaron tunneling (OLPT). The values of activation energy for dc conduction (W) and the one associated with relaxation process ( E R) are found to increase with increase in x up to glass sample with x = 15 and thereafter it decrease with increase in zinc chloride content. DC conduction takes place via variable range hopping (VRH) as proposed by Mott with some modification suggested by Punia et al. The value of real part of modulus ( M') is observed to decrease with increase in temperature. The value of stretched exponent (β) obtained from fitting of M'' reveals the presence of non-Debye type of relaxation in presently studied glass samples. Scaling spectra of ac conductivity and values of electric modulus ( M' and M'') collapse into a single master curve for all the compositions and temperatures. The values of relaxation energy ( E R) for all the studied glass compositions are almost equal to W, suggesting that polarons have to overcome same barrier while relaxing and conducting. The conduction and relaxation processes in the studied glass samples are composition and temperature independent. [Figure not available: see fulltext.

  2. Electronic transport and relaxation studies in bismuth modified zinc boro-tellurite glasses

    Science.gov (United States)

    Dhankhar, Sunil; Kundu, R. S.; Parmar, R.; Murugavel, S.; Punia, R.; Kishore, N.

    2015-10-01

    The ac conductivity of tellurium based quaternary glasses having composition 60 TeO2 - 10 ZnO - (30 - x) B2O3 - xBi2O3; x = 0, 5, 10, 15 and 20 has been investigated in the frequency range 10-1 Hz to 105 Hz and in the temperature range 483 K-593 K. The frequency and temperature dependent ac conductivity increase with increase in bismuth content and found to obey Jonscher's universal power law. The dc conductivity, crossover frequency and frequency exponent have been estimated from the fitting of the experimental data of conductivity with Jonscher's universal power law. In the studied glasses the ac conduction may be described by overlapping of large polaron tunneling model. The activation energy is found to be decrease with increase in bismuth content and variable range hopping (VRH) proposed by Mott with some modification suggested by Punia et al. is more or less suitable to explain dc conduction. The value of the stretched exponent (β) obtained by fitting of M″ reveals the presence of non-Debye type of relaxation in the presently studied glass samples. Scaling spectra of electric modulus (M‧ and M″) collapse into a single master curve for all the compositions and temperatures. The values of activation energy of electric modulus (ER) and conduction (W) are nearly equal for all the studied glasses, indicating that the polaron have to overcome the same energy barrier during conduction as well as relaxation processes. The conduction and relaxation process in the presently studied glass samples are composition and temperature independent.

  3. Effect of lithium addition on thermal and optical properties of zinc-tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Mohamed, E.A., E-mail: emanattamohammed@yahoo.com [Department of Physics, Faculty of Science (Girl' s Branch), Al Azhar University, Nasr City, Cairo (Egypt); Ahmad, F. [Department of Physics, Faculty of Science (Girl' s Branch), Al Azhar University, Nasr City, Cairo (Egypt); Aly, K.A. [Physics Department, Faculty of Science, Al-Azhar University, P.O 71452, Assiut (Egypt); Physics Department, Faculty of Science and Arts, King Abdulaziz University (KAU), Khulais (Saudi Arabia)

    2012-10-15

    Highlights: Black-Right-Pointing-Pointer (80-x)TeO{sub 2}-x Li{sub 2}O-20ZnO) (0 Less-Than-Or-Slanted-Equal-To x Less-Than-Or-Slanted-Equal-To 10) glasses were prepared by melt quenching method. Black-Right-Pointing-Pointer FTIR results revealed that the glassy matrix is composed of TeO{sub 3}, TeO{sub 4} and ZnO{sub 4} units. Black-Right-Pointing-Pointer Some physical properties as a function of Li{sub 2}O content have been evaluated. - Abstract: Glasses with the composition, (80-x)TeO{sub 2}-xLi{sub 2}O-20ZnO with x = 0, 5 and 10 (in mol%), were prepared by conventional melt quenching method. Properties such as density, molar volume, glass transition activation energy, crystallization activation energy and thermal stability as a function of Li{sub 2}O content are reported. FTIR results revealed that the glassy matrix is composed of TeO{sub 3}, TeO{sub 3+1}, TeO{sub 4} units and ZnO{sub 4} structural units. The optical transmission studies revealed that the {lambda}{sub cutoff} wavelength and optical band gap energy (E{sub opt}) decreases with the addition and increase of Li{sub 2}O content while Urbach energy (E{sub 0}) and refractive index increases.

  4. Triple modifier effect on physical, optical and structural properties of boro tellurite zinc lithium glasses

    Science.gov (United States)

    Naresh, P.; Srinivasu, D.; Narsimlu, N.; Ch. Srinivas, Kavitha, B.; Deshpandhe, Uday; Kumar, K. Siva

    2018-05-01

    To investigate physical, optical and structural properties of glass samples of the Quaternary system (60-x)B2O3-xTeO2-10ZnO-30Li2O with x=0,5,10,15, and 20 mol% were prepared by conventional melt quenching technique. XRD confirmed the amorphous nature of all samples. Physical parameters like density, molar volume, Oxygen packing density and etc. calculated. Density of glass samples increased with the increase of TeO2 concentration due to the replacement of lighter B2O3 with heavier TeO2. Optical properties has studied with the help of UV-Visible spectra. Cut off wavelength is increases whereas Eopt and Urbache energies is decreased except intermediate mole fraction of TeO2 at which the triple modifier effect can be observed. Fourier Transform Infrared spectroscopy reveals that the network consists of TeO3 and TeO6 structural units along with BO3 and BO4 units.

  5. Spectroscopic properties of Er3+/Yb3+ Co-doped zinc boro-tellurite glasses for 1.5 xB5m broadband optical amplifiers

    Science.gov (United States)

    Suthanthirakumar, P.; Karthikeyan, P.; Vijayakumar, R.; Marimuthu, K.

    2015-06-01

    A new series of Er3+/Yb3+ co-doped Zinc boro-tellurite glasses with the chemical composition (40-x-y)B2O3+ 25TeO2+20ZnO+15BaO+xYb2O3+yEr2O3 (where x = 0.1, 0.5, 1 and 3; y =1 in wt %) were prepared by melt quenching technique and their spectroscopic behavior were studied through UV-Vis-NIR absorption and NIR luminescence measurements. The bonding parameters (β ¯ and δ) and Judd-Ofelt (JO) intensity parameters Ωλ (λ=2, 4 and 6) have been calculated from the band positions of the absorption spectra. A broad near-infrared emission band at 1540 nm with a full width at half maximum around 80 nm was observed from the NIR luminescence spectra by monitoring an excitation at 980 nm. The absorption cross-section and emission cross-section for the4I13/2→4I15/2 transition of the Er3+ ions were also determined using McCumber theory and the results were discussed and reported.

  6. Erbium concentration dependent absorbance in tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Sazali, E. S., E-mail: mdsupar@utm; Rohani, M. S., E-mail: mdsupar@utm; Sahar, M. R., E-mail: mdsupar@utm; Arifin, R., E-mail: mdsupar@utm; Ghoshal, S. K., E-mail: mdsupar@utm; Hamzah, K., E-mail: mdsupar@utm [Advanced Optical Material Research Group, Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, 81310, Skudai, Johor Bahru, Johor (Malaysia)

    2014-09-25

    Enhancing the optical absorption cross-section in topically important rare earth doped tellurite glasses is challenging for photonic devices. Controlled synthesis and detailed characterizations of the optical properties of these glasses are important for the optimization. The influence of varying concentration of Er{sup 3+} ions on the absorbance characteristics of lead tellurite glasses synthesized via melt-quenching technique are investigated. The UV-Vis absorption spectra exhibits six prominent peaks centered at 490, 526, 652, 800, 982 and 1520 nm ascribed to the transitions in erbium ion from the ground state to the excited states {sup 4}F{sub 7/2}, {sup 2}H{sub 11/2}, {sup 4}F{sub 9/2}, {sup 4}I{sub 9/2}, {sup 2}H{sub 11/2} and {sup 4}I{sub 13/2}, respectively. The results are analyzed by means of optical band gap E{sub g} and Urbach energy E{sub u}. The values of the energy band gap are found decreased from 2.82 to 2.51 eV and the Urbach energy increased from 0.15 to 0.24 eV with the increase of the Er{sub 2}O{sub 3} concentration from 0 to 1.5 mol%. The excellent absorbance of the prepared tellurite glasses makes them suitable for fabricating solid state lasers.

  7. Technological advances in tellurite glasses properties, processing, and applications

    CERN Document Server

    Manzani, Danilo

    2017-01-01

    This book is the first to provide a comprehensive introduction to the synthesis, optical properties, and photonics applications of tellurite glasses. The book begins with an overview of tellurite glasses, followed by expert chapters on synthesis, properties, and state-of-the-art applications ranging from laser glass, optical fibers, and optical communications through color tuning, plasmonics, supercontinuum generation, and other photonic devices. The book provides in-depth information on the the structural, linear, and non-linear optical properties of tellurite glasses and their implications for device development. Real-world examples give the reader valuable insight into the applications of tellurite glass. A detailed discussion of glass production methods, including raw materials and melting and refining oxide- and fluoro-tellurite glasses, is also included. The book features an extensive reference list for further reading. This highly readable and didactic text draws on chemical composition, glass science,...

  8. Viscosity properties of tellurite-based glasses

    International Nuclear Information System (INIS)

    Tincher, B.; Massera, J.; Petit, L.; Richardson, K.

    2010-01-01

    The viscosity behavior of glasses with the composition (90-x)TeO 2 -10Bi 2 O 3 -xZnO with x = 15, 17.5, and 20 (TBZ glasses) and 80TeO 2 -(20-y)Na 2 O-yZnO system with y = 0, 5, and 10 (TNZ glasses) have been measured as a function of temperature using a beam-bending (BBV) and a parallel-plate (PPV) viscometer. The structure of the glass' network has been characterized using Raman spectroscopy and has been related to the viscosity temperature behavior and the fragility parameter (m) of the glasses. As the concentration of ZnO in the TBZ system (x) increases, the fragility parameter of the glass increases, whereas it decreases with an increase of the ZnO concentration (y) in the TNZ system. In both glasses, these variations in m have been related to the partial depolymerization of the tellurite network associated with the level of modifier content. The depolymerization of the tellurite network is believed to be the result of a reduction in the number of [TeO 4 ] units and the formation of [TeO 3 ] and [TeO 3+1 ] units that occurs with a change in TeO 2 content in the TBZ system and modifier content in the TNZ system.

  9. Optical Properties of Bismuth Tellurite Based Glass

    Directory of Open Access Journals (Sweden)

    Hooi Ming Oo

    2012-04-01

    Full Text Available A series of binary tellurite based glasses (Bi2O3x (TeO2100−x was prepared by melt quenching method. The density, molar volume and refractive index increase when bismuth ions Bi3+ increase, this is due to the increased polarization of the ions Bi3+ and the enhanced formation of non-bridging oxygen (NBO. The Fourier transform infrared spectroscopy (FTIR results show the bonding of the glass sample and the optical band gap, Eopt decreases while the refractive index increases when the ion Bi3+ content increases.

  10. Optical Properties of Bismuth Tellurite Based Glass

    Science.gov (United States)

    Oo, Hooi Ming; Mohamed-Kamari, Halimah; Wan-Yusoff, Wan Mohd Daud

    2012-01-01

    A series of binary tellurite based glasses (Bi2O3)x (TeO2)100−x was prepared by melt quenching method. The density, molar volume and refractive index increase when bismuth ions Bi3+ increase, this is due to the increased polarization of the ions Bi3+ and the enhanced formation of non-bridging oxygen (NBO). The Fourier transform infrared spectroscopy (FTIR) results show the bonding of the glass sample and the optical band gap, Eopt decreases while the refractive index increases when the ion Bi3+ content increases. PMID:22605999

  11. Studies on boro cadmium tellurite glasses

    Science.gov (United States)

    Gayathri Pavani, P.; Suresh, S.; Chandra Mouli, V.

    2011-11-01

    To investigate the modification effect of the modifier CdO on boro tellurite glass, a series of glasses with compositions (50 - x) CdO- xTeO 2-50B 2O 3 have been prepared by conventional melt quenching technique. Optical absorption, IR and Raman structural studies are carried out on the glass system. The optical absorption studies revealed that the cutoff wave length and refractive index increase while optical band gap ( Eopt) and Urbach energy decreases with increase of CdO content. The IR and Raman studies revealed that structure of glass network consists of [TeO 3]/[TeO 3+1], [TeO 4], [BO 3], [BO 4] and [Cd-Te] linkages .The compositional dependence of different physical parameters such as density, molar volume, oxygen packing density, optical basicity, have been analyzed and discussed.

  12. Bismuth modified physical, structural and optical properties of mid-IR transparent zinc boro-tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Kundu, R.S.; Dhankhar, Sunil; Punia, R., E-mail: rajeshpoonia13@gmail.com; Nanda, Kirti; Kishore, N.

    2014-02-25

    Highlights: • Novel materials transmitting in mid-infrared spectral region. • Studied glasses may be good candidates for military and non-linear applications. • Hydrogenic excitonic model is applicable. • Transformation of TeO{sub 4} structural units into TeO{sub 3} units with increase in bismuth content. • B{sub 2}O{sub 3} exists in the both BO{sub 3} trigonal and BO{sub 4} tetrahedral structural units. -- Abstract: Tellurium oxide based quaternary glasses in the system TeO{sub 2}⋅B{sub 2}O{sub 3}⋅Bi{sub 2}O{sub 3}⋅ZnO have been prepared by melt quenching technique. Amorphous nature of the samples has been ascertained by X-ray Diffractogram. The values of density and molar volume increase with increase in Bi{sub 2}O{sub 3} content. Theoretical calculations of crystalline volume (V{sub c}) have also been made. The glass transition temperature (T{sub g}) has been determined using differential scanning calorimetry (DSC) and its value is observed to decrease with increase in Bi{sub 2}O{sub 3} content. IR and Raman spectra of the present glass system indicate that ZnO acts as network modifier and exists in ZnO{sub 4} units. TeO{sub 2} exists as TeO{sub 3}, TeO{sub 4}, and TeO{sub 6} structural units and the number of TeO{sub 4} groups decreases with increase in bismuth content except for the glass sample with x = 5, which shows maximum number of TeO{sub 4} structural units among all other studied glass samples and transformation of some of TeO{sub 4} structural units into TeO{sub 3} structural units is observed with increase in bismuth content. Bismuth plays the role of network modifier with BiO{sub 6} octahedral structural units for glass samples with x = 5, 10, and 15, whereas, exists in network forming BiO{sub 3} pyramidal structural units for glass sample with x = 20. B{sub 2}O{sub 3} exists in the form of BO{sub 3} trigonal and BO{sub 4} tetrahedral structural units. The transmittance of the present glasses is observed to be very high (up to 95

  13. Effect of ZnO on the Thermal Properties of Tellurite Glass

    Directory of Open Access Journals (Sweden)

    H. A. A. Sidek

    2013-01-01

    Full Text Available Systematic series of binary zinc tellurite glasses in the form (ZnOx(TeO2 (where x=0 to 0.4 with an interval of 0.05 mole fraction have been successfully prepared via conventional melt cast-quenching technique. Their density was determined by Archimedes method with acetone as buoyant liquid. The thermal expansion coefficient of each zinc tellurite glasses was measured using L75D1250 dilatometer, while their glass transition temperature (Tg was determined by the SETARAM Labsys DTA/6 differential thermogravimetric analysis at a heating rate of 20 K min−1. The acoustic Debye temperature and the softening temperature (Ts were estimated based on the longitudinal (VL and shear ultrasonic (Vs wave velocities propagated in each glass sample. For ultrasonic velocity measurement of the glass sample, MATEC MBS 8000 Ultrasonic Data Acquisition System was used. All measurements were taken at 10 MHz frequency and at room temperature. All the thermal properties of such binary tellurite glasses were measured as a function of ZnO composition. The composition dependence was discussed in terms of ZnO modifiers that were expected to change the thermal properties of tellurite glasses. Experimental results show their density, and the thermal expansion coefficient increases as more ZnO content is added to the tellurite glass network, while their glass transition, Debye temperature, and the softening temperature decrease due to a change in the coordination number (CN of the network forming atoms and the destruction of the network structure brought about by the formation of some nonbridging oxygen (NBO atoms.

  14. Glass Transition Temperature- and Specific Volume- Composition Models for Tellurite Glasses

    Energy Technology Data Exchange (ETDEWEB)

    Riley, Brian J. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States); Vienna, John D. [Pacific Northwest National Lab. (PNNL), Richland, WA (United States)

    2017-09-01

    This report provides models for predicting composition-properties for tellurite glasses, namely specific gravity and glass transition temperature. Included are the partial specific coefficients for each model, the component validity ranges, and model fit parameters.

  15. Magnetically sensitive nanodiamond-doped tellurite glass fibers.

    Science.gov (United States)

    Ruan, Yinlan; Simpson, David A; Jeske, Jan; Ebendorff-Heidepriem, Heike; Lau, Desmond W M; Ji, Hong; Johnson, Brett C; Ohshima, Takeshi; Afshar V, Shahraam; Hollenberg, Lloyd; Greentree, Andrew D; Monro, Tanya M; Gibson, Brant C

    2018-01-19

    Traditional optical fibers are insensitive to magnetic fields, however many applications would benefit from fiber-based magnetometry devices. In this work, we demonstrate a magnetically sensitive optical fiber by doping nanodiamonds containing nitrogen vacancy centers into tellurite glass fibers. The fabrication process provides a robust and isolated sensing platform as the magnetic sensors are fixed in the tellurite glass matrix. Using optically detected magnetic resonance from the doped nanodiamonds, we demonstrate detection of local magnetic fields via side excitation and longitudinal collection. This is a first step towards intrinsically magneto-sensitive fiber devices with future applications in medical magneto-endoscopy and remote mineral exploration sensing.

  16. Structural and thermal properties of vanadium tellurite glasses

    Science.gov (United States)

    Kaur, Rajinder; Kaur, Ramandeep; Khanna, Atul; González, Fernando

    2018-04-01

    V2O5-TeO2 glasses containing 10 to 50 mol% V2O5 were prepared by melt quenching and characterized by X-ray diffraction (XRD), density, Differential Scanning Calorimetry (DSC) and Raman studies.XRD confirmed the amorphous nature of vanadium tellurite samples. The density of the glasses decreases and the molar volume increases on increasing the concentration of V2O5. The thermal properties, such as glass transition temperature Tg, crystallization temperature Tc, and the melting temperature Tm were measured. Tg decreases from a value of 288°C to 232°C. The changes in Tg were correlated with the number of bonds per unit volume, and the average stretching force constant. Raman spectra were used to elucidate the short-range structure of vanadium tellurite glasses.

  17. Study of optical properties of Erbium doped Tellurite glass-polymer composite

    Energy Technology Data Exchange (ETDEWEB)

    Sushama, D., E-mail: sushasukumar@gmail.com [Research Awardee, LAMP, Dept. of Physics, Nit, Calicut, India and Dept. of Physics, M.S.M. College, Kayamkulam, Kerala (India)

    2014-10-15

    Chalcogenide glasses have wide applications in optical device technology. But it has some disadvantages like thermal instability. Among them Tellurite glasses exhibits high thermal Stability. Doping of rare earth elements into the Tellurite glasses improve its optical properties. To improve its mechanical properties composites of this Tellurite glasses with polymer are prepared. Bulk samples of Er{sub 2}O{sub 3} doped TeO{sub 2}‐WO{sub 3}‐La{sub 2}O{sub 3} Tellurite glasses are prepared from high purity oxide mixtures, melting in an alumina crucible in air atmosphere. Composites of this Tellurite glasses with polymer are prepared by powder mixing method and the thin films of these composites are prepared using polymer press. Variations in band gap of these composites are studied from the UV/Vis/NIR absorption.

  18. Study of optical properties of Erbium doped Tellurite glass-polymer composite

    International Nuclear Information System (INIS)

    Sushama, D.

    2014-01-01

    Chalcogenide glasses have wide applications in optical device technology. But it has some disadvantages like thermal instability. Among them Tellurite glasses exhibits high thermal Stability. Doping of rare earth elements into the Tellurite glasses improve its optical properties. To improve its mechanical properties composites of this Tellurite glasses with polymer are prepared. Bulk samples of Er 2 O 3 doped TeO 2 ‐WO 3 ‐La 2 O 3 Tellurite glasses are prepared from high purity oxide mixtures, melting in an alumina crucible in air atmosphere. Composites of this Tellurite glasses with polymer are prepared by powder mixing method and the thin films of these composites are prepared using polymer press. Variations in band gap of these composites are studied from the UV/Vis/NIR absorption

  19. Study of optical properties of Erbium doped Tellurite glass-polymer composite

    Science.gov (United States)

    Sushama, D.

    2014-10-01

    Chalcogenide glasses have wide applications in optical device technology. But it has some disadvantages like thermal instability. Among them Tellurite glasses exhibits high thermal Stability. Doping of rare earth elements into the Tellurite glasses improve its optical properties. To improve its mechanical properties composites of this Tellurite glasses with polymer are prepared. Bulk samples of Er2O3 doped TeO2-WO3-La2O3 Tellurite glasses are prepared from high purity oxide mixtures, melting in an alumina crucible in air atmosphere. Composites of this Tellurite glasses with polymer are prepared by powder mixing method and the thin films of these composites are prepared using polymer press. Variations in band gap of these composites are studied from the UV/Vis/NIR absorption.

  20. Optical and spectroscopic properties of Eu-doped tellurite glasses and glass ceramics

    International Nuclear Information System (INIS)

    Stambouli, W.; Elhouichet, H.; Gelloz, B.; Férid, M.

    2013-01-01

    Tellurite glasses doped with trivalent europium were prepared by the conventional melt quenching technique, in the chemical composition of (85−x) TeO 2 +5La 2 O 3 +10TiO 2 +xEu 2 O 3 by varying the concentration of the rare-earth ion in the order 0.5, 1 and 1.5 mol%. Using Judd–Ofelt analysis, we calculated intensity parameters (Ω 2 and Ω 4 ), spontaneous emission probabilities, the radiative lifetime, luminescence branching factors, the quantum yield of luminescence, and the stimulated emission cross-sections for 5 D 0 → 7 F 2 transition. The change in optical properties with the variation of Eu 3+ ion concentration have been discussed and compared with other glasses. The luminescence intensity ratio, quantum efficiency and emission cross-section values support that the TeEu1.5 tellurite glass is a suitable candidate for red laser source applications. Optical properties for Eu 3+ doped tellurite glass, heated for different temperature, were investigated. Crystalline phases for α-TeO 2 , γ-TeO 2 and TiTe 3 O 8 system were determined by the XRD method. The effect of heat treatment on luminescence properties in the tellurite glass was discussed. By using Eu 3+ as a probe, the local structure of rare-earth ion in tellurite glass, vitro-ceramic and ceramic glass has been investigated. The evaluated J–O intensity parameters have been used to calculate different radiative and laser characteristic parameters of the 5 D 0 excited level. The large magnitudes of stimulated emission cross-section (σ e ), branching ratio (β) and Gain bandwidth (σ e ×Δλ eff ) obtained for 5 D 0 → 7 F 2 (613 nm) transition for ceramic glass indicate that the present glass ceramic is promising host material for Eu 3+ doped fiber amplifiers. The measured lifetime of 5 D 0 excited state increases with increase of the heat treatment which further indicate that some Eu 3+ ions were successfully embedded in the crystal phase and prove the low phonon energy environment of Eu 3+ ions

  1. Raman band intensities of tellurite glasses.

    Science.gov (United States)

    Plotnichenko, V G; Sokolov, V O; Koltashev, V V; Dianov, E M; Grishin, I A; Churbanov, M F

    2005-05-15

    Raman spectra of TeO2-based glasses doped with WO3, ZnO, GeO2, TiO2, MoO3, and Sb2O3 are measured. The intensity of bands in the Raman spectra of MoO3-TeO2 and MoO3-WO3-TeO2 glasses is shown to be 80-95 times higher than that for silica glass. It is shown that these glasses can be considered as one of the most promising materials for Raman fiber amplifiers.

  2. Influence of tellurite on lifetime for samarium doped lanthanum lead borate glass

    Science.gov (United States)

    Madhu, A.; Eraiah, B.

    2018-04-01

    Samarium substituted tellurium lanthanum lead borate glass is prepared using melt quenching technique. Luminescence spectra have been recorded upon excitation with 402 nm various transitions from 4G5/2 level, for samarium doped tellurite glasses are studied and also lifetime for all the samples exhibit single exponential behaviour of decay curve. Luminescence spectra of present glasses show quenching effect due to cross-relation channels of samarium ions. The lifetime of glass samples decrease as the tellurite concentration is decreased. So, it evidences that to attain longer lifetime for lasing material one can tune the host by selecting concentration of tellurite.

  3. Fragility–structure–conductivity relations in vanadium tellurite glass

    DEFF Research Database (Denmark)

    Kjeldsen, Jonas; Yue, Yuanzheng; Rodrigues, Ana Candida Martins

    the ability to intercalate lithium-ions, it is a candidate as cathode material. Here, we investigate the correlation between liquid fragility, structure and electronic conductivity in a series of vanadium-tellurite glasses with varying vanadium concentration. We measure dynamic and thermodynamic fragility...... the number of bonding and non-bonding oxygen atoms per network former, while we use IS and ESR to determine the electronic conductivity and the valence states of the system. We correlate the changes in local atomic structures as determined by NMR to the observed changes in macroscopic properties. Since...

  4. Optical studies on Eu3+ doped boro-tellurite glasses

    Science.gov (United States)

    Maheshvaran, K.; Marimuthu, K.

    2012-06-01

    Eu3+ doped boro-tellurite glasses with the chemical composition (39-x)B2O3+30TeO2+15MgO+15K2O +xEu2O3 (where x = 0.01, 0.1, 1, 2 and 3 wt%) have been prepared by following conventional melt quenching technique. Spectroscopic properties of the Eu3+ doped boro-tellurite glasses have been studied by recording the optical absorption and luminescence measurements. Through the optical absorption spectra, bonding parameters (β¯, δ) have been calculated to identify the ionic/covalent nature of the glasses. Judd-Ofelt (JO) analysis have been carried out using the luminescence spectra. The JO parameters (Ωλ = 2, 4 and 6) were used to calculate the radiative properties for the 5D0 → 7FJ (J = 1, 2, 3 and 4) emission transitions of the Eu3+ ions. The change in optical properties with the variation of Eu3+ ion concentration have been studied and discussed with similar studies.

  5. Spectroscopic studies of silver boro tellurite glasses

    Science.gov (United States)

    Kumar, E. Ramesh; Kumari, K. Rajani; Rao, B. Appa; Bhikshamaiah, G.

    2014-04-01

    The FTIR absorption and Raman scattering studies were used to obtain the structural information of AgI-Ag2O-[(1-x)B2O3-xTeO2] (x=0 to 1 mol% in steps of 0.2) glasses. The glassy nature of the compounds has been confirmed by X-ray diffraction. FTIR and Raman spectra were recorded for all samples at room temperature. FTIR spectra which provides the information about the change in bond structure of the glasses. Raman spectra provide the effect of TeO2 on SBT glass system is that as increasing the concentration of TeO2 the band intensity at 707 cm-1 increase.

  6. Spectroscopic studies of silver boro tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, E. Ramesh, E-mail: apparao.bojja@gmail.com; Kumari, K. Rajani, E-mail: apparao.bojja@gmail.com; Rao, B. Appa, E-mail: apparao.bojja@gmail.com; Bhikshamaiah, G., E-mail: apparao.bojja@gmail.com [Department of Physics, Osmania University, Hyderabad-500007 (India)

    2014-04-24

    The FTIR absorption and Raman scattering studies were used to obtain the structural information of AgI−Ag{sub 2}O−[(1−x)B{sub 2}O{sub 3}−xTeO{sub 2}] (x=0 to 1 mol% in steps of 0.2) glasses. The glassy nature of the compounds has been confirmed by X-ray diffraction. FTIR and Raman spectra were recorded for all samples at room temperature. FTIR spectra which provides the information about the change in bond structure of the glasses. Raman spectra provide the effect of TeO{sub 2} on SBT glass system is that as increasing the concentration of TeO{sub 2} the band intensity at 707 cm{sup −1} increase.

  7. Immobilization of Technetium Waste from Pyro-processing Using Tellurite Glasses

    Energy Technology Data Exchange (ETDEWEB)

    Heo, Jong; Pyo, Jae-Young; Lee, Cheong-Won [POSTECH, Pohang (Korea, Republic of); Yang, Jae-Hwan; Park, Hwan-Seo [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2016-10-15

    Vitrification of Tc wastes has been challenging because of the low solubility in the silicate glass and high volatility in the melting process. In previous studies, the measured solubility of Tc and Re was ⁓ 3000 ppm at 1000 .deg. C in low activity waste (LAW) glass. And retention of Tc has been reported within 12 - 77% during the borosilicate vitrification process. Tellurite glasses have been studied for halide waste immobilization due to low melting temperatures (Tm= 600-800 .deg. C) and flexibility of network with foreign ions. Tellurite glasses offered higher halide retention than borosilicate glasses. The structure of pure tellurite (TeO{sub 2}) consists of TeO{sub 4} trigonal bipyramids (tbp), but TeO{sub 4} units are converted to TeO{sub 3} trigonal pyramids (tp) having non-bridging oxygen (NBO) as the modifiers added. Objectives of this study are to investigate the tellurite glasses for Tc immobilization using Re as a surrogate. Retention and waste loading of Re were analyzed during the vitrification process of tellurite glass. We investigated local structures of Re ions in glasses by Raman and X-ray absorption spectroscopies. The tellurite glass was investigated to immobilize the Ca(TcO{sub 4}){sub 2}, surrogated by Ca(ReO{sub 4}){sub 2}. The average of Re retention in tellurite glass was 86%. The 7-day PCT results were satisfied with U.S requirement up to 9 mass% of Ca(ReO{sub 4}){sub 2} content. Re in the tellurite glass exists +7 oxidation state and was coordinated with 4 oxygen.

  8. Immobilization and bonding scheme of radioactive iodine-129 in silver tellurite glass

    Science.gov (United States)

    Lee, Cheong Won; Pyo, Jae-Young; Park, Hwan-Seo; Yang, Jae Hwan; Heo, Jong

    2017-08-01

    Silver tellurite glasses with melting temperatures disposal site. Iodine waste loading in glasses was as high as 12.64 wt% of all metallic elements and 11.21 wt% including oxygen. Normalized elemental releases obtained from the product consistency test were well below US regulation of 2 g/m2. Iodines are surrounded by four Ag+ ions forming [Ag4I]3+ units that are further connected to tellurite network through bonds with non-bridging oxygens.

  9. Structural and optical study of tellurite-barium glasses

    Science.gov (United States)

    Grelowska, I.; Reben, M.; Burtan, B.; Sitarz, M.; Cisowski, J.; Yousef, El Sayed; Knapik, A.; Dudek, M.

    2016-12-01

    The goal of this work was to determine the effect of barium oxide on the structural, thermal and optical properties of the TeO2-BaO-Na2O (TBN) and TeO2-BaO-WO3 (TBW) glass systems. Raman spectra allow relating the glass structure and vibration properties (i.e. vibrational frequencies and Raman intensities) with the glass composition. Raman spectra show the presence of TeO4 and TeO3+1/TeO3 units that conform with the glass matrix. Differential thermal analysis DTA, XRD measurements have been considered in term of BaO addition. The spectral dependence of ellipsometric angles of the tellurite-barium glass has been studied. The optical measurements were conducted on Woollam M2000 spectroscopic ellipsometer in spectral range of 190-1700 nm. The reflectance and transmittance measurements have been done on spectrophotometer Perkin Elmer, Lambda 900 in the range of 200-2500 nm (UV-VIS-NIR). From the transmittance spectrum, the energy gap was determined.

  10. The effect of excitation intensity variation and silver nanoparticle codoping on nonlinear optical properties of mixed tellurite and zinc oxide glass doped with Nd2O3 studied through ultrafast z-scan spectroscopy

    Science.gov (United States)

    Moreira, L.; Falci, R. F.; Darabian, H.; Anjos, V.; Bell, M. J. V.; Kassab, L. R. P.; Bordon, C. D. S.; Doualan, J. L.; Camy, P.; Moncorgé, R.

    2018-05-01

    The research on Nd3+ doped new solid-state laser hosts with specific thermo-mechanical and optical properties is very active. Nd3+ doped tellurite glasses are suitable for these applications. They have high linear and nonlinear refraction index, wide transmittance range. The TeO2-ZnO (TZO) glass considered in the present work combines all those features and the nonlinear optical properties can be used for the development of Kerr-lens mode-locked sub picosecond lasers. Recently the laser performance of Nd3+ doped TZO glass and was reported and laser slope efficiency of 21% was observed. We investigate how the intensity variation and the silver nanoparticles codoping affects the nonlinear optical properties of Nd3+ doped TZO glasses. Intensity dependent nonlinear refraction indices coefficients at 750, 800 and 850 nm were observed. The nonlinear optical features were obtained through ultrafast single beam z-scan technique with excitations at 750, 800 and 850 nm and are up to two orders of magnitude higher than those reported in the literature.

  11. Optical spectroscopy of rare earth-doped oxyfluoro-tellurite glasses ...

    Indian Academy of Sciences (India)

    2017-08-16

    Aug 16, 2017 ... glass matrix with different RE ions for optical properties is of importance. ... Figure 1. XRD pattern of the tellurite glasses studied. Table 1. Composition and glass transition ... convoluted using Gaussian line shape. Parameters like .... On the other hand, in Er3+ ion, the ground state 4I15/2 itself has manifold.

  12. Band gap and polarizability of boro-tellurite glass: Influence of erbium ions

    Science.gov (United States)

    Said Mahraz, Zahra Ashur; Sahar, M. R.; Ghoshal, S. K.

    2014-08-01

    Understanding the influence of rare earth ions in improving the structural and optical properties of inorganic glasses are the key issues. Er3+-doped zinc boro-tellurite glasses with composition 30B2O3-10ZnO-(60-x) TeO2-xEr2O3 are prepared (x = 0, 0.5, 1, 1.5 and 2 mol%) using melt quenching technique. The physical and optical characterizations are measured by density and UV-Vis-IR absorption spectroscopy. The color of the glass changed from light yellow to deep pink due to the introduction of Er3+ ions. The maximum density is found to be ∼4.73 g cm-3 for 1 mol% of Er3+ doping. The variations in the polarizability (6.7-6.8 cm3) and the molar volume (27.987-28.827 cm3 mol-1) with dopant concentration are ascribed to the formation of non-bridging oxygen. This observation is consistent with the alteration of number of bonds per unit volume. The direct and indirect optical band gaps are increased while the phonon cut-off wavelength and Urbach energy decreased with the increase of erbium content. A high density and wide transparency range in VIS-IR area are achieved. Our results on high refractive index (∼2.416) and polarizability suggest that these glasses are potential for photonics, solid state lasers and communications devices.

  13. Faraday rotation influence factors in tellurite-based glass and fibers

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Qiuling; Wang, Qingwei [Henan University of Technology, School of Materials Science and Engineering, Zhengzhou, Henan (China); Wang, Hui; Chen, Qiuping [Politecnico di Torino, Department of Applied Science and Technology, Turin (Italy)

    2015-09-15

    The Faraday rotation influence factors in tellurite-based glass and fibers were studied by experiments and simulations. TeO{sub 2}-ZnO-Na{sub 2}O-BaO glass family was fabricated and characterized in terms of the thermal and magneto-optical properties. Two core-cladding pairs for two fibers were selected from fabricated glasses. The Verdet constants of the glasses and fibers were measured at different wavelengths using a homemade optical bench, and the Verdet constant of fiber was close to that of the bulk glass. The influence from external factors (wavelength, laser power and magnetic field) and internal factors (thermal expansion coefficient difference, refractive index and Verdet constant of core and cladding) on Faraday rotation in fibers was investigated and discussed, and the purpose of this study is to improve the Faraday rotation in tellurite fibers for MO device applications both from internal material property match and external parameter configuration in measurement. (orig.)

  14. Faraday rotation influence factors in tellurite-based glass and fibers

    International Nuclear Information System (INIS)

    Chen, Qiuling; Wang, Qingwei; Wang, Hui; Chen, Qiuping

    2015-01-01

    The Faraday rotation influence factors in tellurite-based glass and fibers were studied by experiments and simulations. TeO 2 -ZnO-Na 2 O-BaO glass family was fabricated and characterized in terms of the thermal and magneto-optical properties. Two core-cladding pairs for two fibers were selected from fabricated glasses. The Verdet constants of the glasses and fibers were measured at different wavelengths using a homemade optical bench, and the Verdet constant of fiber was close to that of the bulk glass. The influence from external factors (wavelength, laser power and magnetic field) and internal factors (thermal expansion coefficient difference, refractive index and Verdet constant of core and cladding) on Faraday rotation in fibers was investigated and discussed, and the purpose of this study is to improve the Faraday rotation in tellurite fibers for MO device applications both from internal material property match and external parameter configuration in measurement. (orig.)

  15. Solid State Field-Assisted Diffusion of Copper in Multi-Component Tellurite Glass

    Czech Academy of Sciences Publication Activity Database

    Stepanov, B.; Ren, J.; Wágner, T.; Lorinčík, Jan; Frumar, M.; Churbanov, M.; Chigirinsky, Y.

    2011-01-01

    Roč. 94, č. 7 (2011), 1986-1988 ISSN 0002-7820 Institutional research plan: CEZ:AV0Z20670512 Keywords : Solid state diffusion * Secondary Ion Mass Spectrometry * Tellurite glass Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering Impact factor: 2.272, year: 2011

  16. Solid state field-assisted diffusion of silver in multi-component tellurite glasses

    Czech Academy of Sciences Publication Activity Database

    Stepanov, B.; Ren, J.; Wágner, T.; Lorinčík, Jan; Frumar, M.; Churbanov, M.; Chigirinsky, Y.

    2011-01-01

    Roč. 357, č. 15 (2011), 3022-3026 ISSN 0022-3093 Institutional research plan: CEZ:AV0Z20670512 Keywords : Solid state diffusion * Secondary Ion Mass Spectrometry * Tellurite glass Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering Impact factor: 1.537, year: 2011

  17. Comparative investigation on the spectroscopic properties of Pr3+-doped boro-phosphate, boro-germo-silicate and tellurite glasses

    Science.gov (United States)

    Zhang, Liaolin; Dong, Guoping; Peng, Mingying; Qiu, Jianrong

    We report on the spectroscopic properties of Pr3+-doped boro-phosphate, boro-germo-silicate and tellurite glasses. The stimulated absorption and emission cross sections were estimated. Only one emission at 596 nm and 605 nm is observed in Pr3+-doped boro-phosphate and boro-germo-silicate glasses, respectively, while three emissions at 605 nm, 612 nm and 645 nm are observed in Pr3+-doped tellurite glass when excited at 467 nm. The fluorescence lifetime at 600 nm in Pr3+-doped boro-phosphate, boro-germo-silicate and tellurite glasses is 137 μs, 73 μs and 51 μs, respectively. The emissions from Pr3+-doped boro-phosphate, boro-germo-silicate and tellurite glasses show different decay behaviors and can be well explained by multiphonon relaxation theory.

  18. Assessment of lead tellurite glass for immobilizing electrochemical salt wastes from used nuclear fuel reprocessing

    Energy Technology Data Exchange (ETDEWEB)

    Riley, Brian J.; Kroll, Jared O.; Peterson, Jacob A.; Pierce, David A.; Ebert, William L.; Williams, Benjamin D.; Snyder, Michelle M. V.; Frank, Steven M.; George, Jaime L.; Kruska, Karen

    2017-11-01

    This paper provides an overview of research evaluating the use of lead tellurite glass as a waste form for salt wastes from electrochemical reprocessing of used nuclear fuel. The efficacy of using lead tellurite glass to immobilize three different salt compositions was evaluated: a LiCl-Li2O oxide reduction salt containing fission products from oxide fuel, a LiCl-KCl eutectic salt containing fission products from metallic fuel, and SrCl2. Physical and chemical properties of glasses made with these salts were characterized with X-ray diffraction, bulk density measurements, differential thermal analysis, chemical durability tests, scanning and transmission electron microscopies, and energy-dispersive X-ray spectroscopy. These glasses were found to accommodate high salt concentrations and have high densities, but further development is needed to improve chemical durability. (C) 2017 Published by Elsevier B.V.

  19. The electronic and optical properties of germanium tellurite glasses containing various transition metal oxides

    International Nuclear Information System (INIS)

    Khan, M.N.

    1988-01-01

    Various transition metal oxides, such as TiO 2 , V 2 O 5 , NiO, CuO, and ZnO are added to germanium-tellurite glass and measurements are reported of the electrical conductivity, density, optical absorption, infra-red absorption spectra, and electron spin resonance. It is found that the d.c. conductivity of glasses containing the same amount of V 2 O 5 is higher than that of germanium tellurite glasses containing a similar amount of other transition metal oxides, and is due to hopping between localized states. The optical absorption measurements show that the fundamental absorption edge is a function of glass composition and the optical absorption is due to forbidden indirect transitions. From the infra-red absorption spectra, it is found that the addition of transition metal oxides does not introduce any new absorption band in the infra-red spectrum of germanium tellurite glasses. A small shift of existing absorptions toward higher wave number is observed. The ESR measurements revealed that some transition metal ions are diamagnetic while others are paramagnetic in the glass network. (author)

  20. Critical V2O5/TeO2 Ratio Inducing Abrupt Property Changes in Vanadium Tellurite Glasses.

    Science.gov (United States)

    Kjeldsen, Jonas; Rodrigues, Ana C M; Mossin, Susanne; Yue, Yuanzheng

    2014-12-26

    Transition metal containing glasses have unique electrical properties and are therefore often used for electrochemical applications, such as in batteries. Among oxide glasses, vanadium tellurite glasses exhibit the highest electronic conductivity and thus the high potential for applications. In this work, we investigate how the dynamic and physical properties vary with composition in the vanadium tellurite system. The results show that there exists a critical V(2)O(5) concentration of 45 mol %, above which the local structure is subjected to a drastic change with increasing V(2)O(5), leading to abrupt changes in both hardness and liquid fragility. Electronic conductivity does not follow the expected correlation to the valence state of the vanadium as predicted by the Mott-Austin equation but shows a linear correlation to the mean distance between vanadium ions. These findings could contribute to designing optimum vanadium tellurite compositions for electrochemical devices. The work gives insight into the mechanism of electron conduction in the vanadium tellurite systems.

  1. Elemental redistribution behavior in tellurite glass induced by high repetition rate femtosecond laser irradiation

    International Nuclear Information System (INIS)

    Teng, Yu; Zhou, Jiajia; Khisro, Said Nasir; Zhou, Shifeng; Qiu, Jianrong

    2014-01-01

    Highlights: • Abnormal elements redistribution behavior was observed in tellurite glass. • The refractive index and Raman intensity distribution changed significantly. • The relative glass composition remained unchanged while the glass density changed. • First time report on the abnormal element redistribution behavior in glass. • The glass network structure determines the elemental redistribution behavior. - Abstract: The success in the fabrication of micro-structures in glassy materials using femtosecond laser irradiation has proved its potential applications in the construction of three-dimensional micro-optical components or devices. In this paper, we report the elemental redistribution behavior in tellurite glass after the irradiation of high repetition rate femtosecond laser pulses. The relative glass composition remained unchanged while the glass density changed significantly, which is quite different from previously reported results about the high repetition rate femtosecond laser induced elemental redistribution in silicate glasses. The involved mechanism is discussed with the conclusion that the glass network structure plays the key role to determine the elemental redistribution. This observation not only helps to understand the interaction process of femtosecond laser with glassy materials, but also has potential applications in the fabrication of micro-optical devices

  2. Enhancing the Electronic Conductivity of Vanadium-tellurite Glasses by Tuning the Redox State

    DEFF Research Database (Denmark)

    Kjeldsen, Jonas; Yue, Yuanzheng

    Transition metal oxides are used in a variety of electronic purposes, e.g., vanadium tellurite as cathode material in high-power demanding batteries. By tuning the redox state of vanadium, it is possible to achieve a lower internal resistance within the entire battery unit, thus a higher capacity....... In this work we vary the redox state of a given vanadium tellurite system by performing post heat-treatment in controlled atmosphere. This process is in theory not limited only to varying electronic conductivity, but also varying the glass structure, and hence, changing properties of the glasses, e.g, thermal...... and mechanical properties. Finally we give insight into the relation between the redox state and electronic conductivity....

  3. Critical V2O5/TeO2 ratio inducing abrupt property changes in vanadium tellurite glasses

    DEFF Research Database (Denmark)

    Kjeldsen, Jonas; Rodrigues, Ana C. M.; Mossin, Susanne

    2014-01-01

    Transition metal containing glasses have unique electrical properties and are therefore often used for electrochemical applications, such as in batteries. Among oxide glasses, vanadium tellurite glasses exhibit the highest electronic conductivity and thus the high potential for applications. In t...

  4. Up-conversion luminescence and local heating in Er{sup 3+} doped tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Dwivedi, Y.; Rai, S.B. [Banaras Hindu University, Laser and Spectroscopy Laboratory, Physics Department, Varanasi, UP (India)

    2012-10-15

    The present article discusses the up-conversion and thermometric properties of Er doped tellurite glass on excitation with 976 nm laser radiation. Temperature has been measured using fluorescence intensity ratio variation, in 528/548 and 801/828 nm, with temperature. Temperature at laser focus spot has been estimated by comparing the intensity ratios at different laser powers with the intensity ratio at different temperatures when sample was heated externally. (orig.)

  5. Structural investigation and simulation of acoustic properties of some tellurite glasses using artificial intelligence technique

    International Nuclear Information System (INIS)

    Gaafar, M.S.; Abdeen, Mostafa A.M.; Marzouk, S.Y.

    2011-01-01

    Research highlights: → Simulation the acoustic properties of some tellurite glasses using one of the artificial intelligence techniques (artificial neural network). → The glass network is strengthened by enhancing the linkage of Te-O chains. The tellurite network will also come to homogenization, because of uniform distribution of Nb 5+ ions among the Te-O chains, though some of the tellurium-oxide polyhedra still link each other in edge sharing. → Excellent agreements between the measured values and the predicted values were obtained for over 50 different tellurite glass compositions. → The model we designed gives a better agreement as compared with Makishima and Machenzie model. - Abstract: The developments in the field of industry raise the need for simulating the acoustic properties of glass materials before melting raw material oxides. In this paper, we are trying to simulate the acoustic properties of some tellurite glasses using one of the artificial intelligence techniques (artificial neural network). The artificial neural network (ANN) technique is introduced in the current study to simulate and predict important parameters such as density, longitudinal and shear ultrasonic velocities and elastic moduli (longitudinal and shear moduli). The ANN results were found to be in successful good agreement with those experimentally measured parameters. Then the presented ANN model is used to predict the acoustic properties of some new tellurite glasses. For this purpose, four glass systems xNb 2 O 5 -(1 - x)TeO 2 , 0.1PbO-xNb 2 O 5 -(0.9 - x)TeO 2 , 0.2PbO-xNb 2 O 5 -(0.8 - x)TeO 2 and 0.05Bi 2 O 3 -xNb 2 O 5 -(0.95 - x)TeO 2 were prepared using melt quenching technique. The results of ultrasonic velocities and elastic moduli showed that the addition of Nb 2 O 5 as a network modifier provides oxygen ions to change [TeO 4 ] tbps into [TeO 3 ] tps.

  6. Structural investigation and simulation of acoustic properties of some tellurite glasses using artificial intelligence technique

    Energy Technology Data Exchange (ETDEWEB)

    Gaafar, M.S., E-mail: mohamed_s_gaafar@hotmail.com [Ultrasonic Department, National Institute for Standards, Giza (Egypt); Physics Department, Faculty of Science, Majmaah University, Zulfi (Saudi Arabia); Abdeen, Mostafa A.M., E-mail: mostafa_a_m_abdeen@hotmail.com [Dept. of Eng. Math. and Physics, Faculty of Eng., Cairo University, Giza (Egypt); Marzouk, S.Y., E-mail: samir_marzouk2001@yahoo.com [Arab Academy of Science and Technology, Al-Horria, Heliopolis, Cairo (Egypt)

    2011-02-24

    Research highlights: > Simulation the acoustic properties of some tellurite glasses using one of the artificial intelligence techniques (artificial neural network). > The glass network is strengthened by enhancing the linkage of Te-O chains. The tellurite network will also come to homogenization, because of uniform distribution of Nb{sup 5+} ions among the Te-O chains, though some of the tellurium-oxide polyhedra still link each other in edge sharing. > Excellent agreements between the measured values and the predicted values were obtained for over 50 different tellurite glass compositions. > The model we designed gives a better agreement as compared with Makishima and Machenzie model. - Abstract: The developments in the field of industry raise the need for simulating the acoustic properties of glass materials before melting raw material oxides. In this paper, we are trying to simulate the acoustic properties of some tellurite glasses using one of the artificial intelligence techniques (artificial neural network). The artificial neural network (ANN) technique is introduced in the current study to simulate and predict important parameters such as density, longitudinal and shear ultrasonic velocities and elastic moduli (longitudinal and shear moduli). The ANN results were found to be in successful good agreement with those experimentally measured parameters. Then the presented ANN model is used to predict the acoustic properties of some new tellurite glasses. For this purpose, four glass systems xNb{sub 2}O{sub 5}-(1 - x)TeO{sub 2}, 0.1PbO-xNb{sub 2}O{sub 5}-(0.9 - x)TeO{sub 2}, 0.2PbO-xNb{sub 2}O{sub 5}-(0.8 - x)TeO{sub 2} and 0.05Bi{sub 2}O{sub 3}-xNb{sub 2}O{sub 5}-(0.95 - x)TeO{sub 2} were prepared using melt quenching technique. The results of ultrasonic velocities and elastic moduli showed that the addition of Nb{sub 2}O{sub 5} as a network modifier provides oxygen ions to change [TeO{sub 4}] tbps into [TeO{sub 3}] tps.

  7. Spectroscopic properties and thermal stability of Er3+-doped tungsten-tellurite glass for waveguide amplifier application

    International Nuclear Information System (INIS)

    Zhao Shilong; Wang Xiuli; Fang Dawei; Xu Shiqing; Hu Lili

    2006-01-01

    Tungsten-tellurite glass with molar composition of 60TeO 2 -30WO 3 -10Na 2 O has been investigated for developing planar broadband waveguide amplifier application. Spectroscopic properties and thermal stability of Er 3+ -doped tungsten-tellurite glass have been discussed. The results show that the introduction of WO 3 increases significantly the glass transition temperature and the maximum phonon energy. Er 3+ -doped tungsten-tellurite glass exhibits high glass transition temperature (377 deg. C), large emission cross-section (0.91 x 10 -20 cm 2 ) at 1532 nm and broad full width at half maximum (FWHM), which make it preferable for broadband Er 3+ -doped waveguide amplifier application

  8. Energy transfer induced Eu{sup 3+} photoluminescence enhancement in tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Stambouli, W. [Laboratoire des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Elhouichet, H., E-mail: habib.elhouichet@fst.rnu.tn [Laboratoire des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Departement de Physique, Faculte des Sciences de Tunis, Universite de Tunis-ElManar ElManar 2092, Tunis (Tunisia); Gelloz, B. [Graduate School of Engineering, Tokyo University of Agriculture and Technology, 2-24-16 Nakacho, Koganei, 184-8588 Tokyo (Japan); Ferid, M. [Laboratoire des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Koshida, N. [Graduate School of Engineering, Tokyo University of Agriculture and Technology, 2-24-16 Nakacho, Koganei, 184-8588 Tokyo (Japan)

    2012-01-15

    In this work, structural, thermal and optical properties of Eu{sup 3+} doped TeO{sub 2}-La{sub 2}O{sub 3}-TiO{sub 2} glass were investigated. The differential scanning calorimetry (DSC) measurements reveal an important stability factor {Delta}T=143.52 K, which indicates the good thermal and mechanical stabilities of tellurite glass. From the absorption spectrum, the optical band gap was found to be direct with E{sub g}=3.23 eV. The temperature dependences of photoluminescence (PL) properties of Eu-doped and Eu-Tb codoped tellurite glass are investigated. As the temperature increases from 7 to 300 K, both the PL intensity and the PL lifetime relative to the {sup 5}D{sub 2}{yields}{sup 7}F{sub 0} are nearly constant below 230 K and then an enhancement takes place. This anomalous feature is attributed to the thermally activated carrier transfer process from charged intrinsic defects states to Eu{sup 3+} energy levels. By co-doping tellurite glasses with Eu and Tb, a strong Eu{sup 3+} PL enhancement is shown due to excitation transfer from Tb{sup 3+} and intrinsic defects to Eu ions. - Highlights: > TeO{sub 2}-La{sub 2}O{sub 3}-TiO{sub 2} glass doped Eu{sup 3+} with good thermal stability elaborated. > PL evolution of Eu{sup 3+} with temperature shows a non-conventional behavior. > Thermally activated carrier transfer from intrinsic defects states to Eu{sup 3+} shown. > Strong Eu{sup 3+} PL enhancement is shown in Eu-Tb codoped glass.

  9. The structural studies of vanadium substituted lithium-bismuth-boro-tellurite glass

    Science.gov (United States)

    Madhu, A.; Eraiah, B.

    2018-05-01

    The structural studies of vanadium substituted lithium-bismuth-boro-tellurite glass is successfully prepared and certain analysis like XRD,FTIR,DTA/TGA with density, molar volume are done. The amorphous phase has been identified based on X-ray diffraction analysis. The vanadium oxide plays the role as a glass-modifier and influences on BO3 ↔ BO4 conversion. The observed nonlinear variation in Tg with vanadium oxide increase, it reflects structural changes. The nonlinear variation of density and molar volume can be attributed to vanadium oxide incorporation have increased the number of Non-bridging oxygen (NBO'S).

  10. Luminescence studies on Dy3+ doped calcium boro-tellurite glasses for White light applications

    Science.gov (United States)

    Karthikeyan, P.; Vijayakumar, R.; Marimuthu, K.

    2017-09-01

    A new series of Dy3+ doped calcium boro-tellurite glasses have been prepared by melt quenching technique and their spectroscopic properties were studied through FTIR, absorption luminescence and lifetime spectral measurements. FTIR studies have been made to explore the presence of various stretching and bending vibrations of different borate and tellurite groups in the prepared glasses. The bonding parameter values were estimated from the absorption band positions using Nephelauxetic ratios to examine the nature of the metal-ligand bond. The optical band gap and Urbach energy (ΔE) values were obtained from the absorption spectra to explore the electronic band structure of the studied glasses. Judd-Ofelt (JO) theory have been used to determine the JO intensity parameters (Ω2, Ω4, Ω6) following the least square fitting procedure between the experimental and calculated oscillator strength values. The luminescence spectra of the Dy3+ doped calcium boro-tellurite glasses exhibit two intense emission bands corresponding to the 4F9/2→6H15/2 and 4F9/2→6H13/2 transitions. Further, they exhibit less intense emission band due to the 4F9/2→6H11/2 transition. Luminescence spectra were characterized through CIE 1931 chromaticity diagram to obtain the dominant emission color of the prepared glasses. The JO intensity parameters and refractive index values have been used to calculate the radiative parameters such as transition probabilities (AR), branching ratios (βR) and stimulated emission cross-section (σPE) values for the observed transitions in the luminescence spectra. The decay curves of all the studied glasses found to exhibit non-exponential behavior and further to understand the energy transfer process takes place between the Dy3+ ions, the decay curves were fitted to the Inokuti-Hirayama (IH) model. The structural and optical properties of the Dy3+ doped calcium boro-tellurite glasses have been studied as a function of different metal cations (Zn, Cd, Pb and

  11. Absorption and emission analysis of RE3+(Sm3+ and Dy3+): lithium boro tellurite glasses.

    Science.gov (United States)

    Sooraj Hussain, N; Hungerford, G; El-Mallawany, R; Gomes, M J M; Lopes, M A; Ali, Nasar; Santos, J D; Buddhudu, S

    2009-06-01

    This paper reports on the development and spectral analysis of Sm3+ (1.0%) and Dy3+ (1.0%) doped lithium-boro-tellurite glasses. A bright orange (4G5/2-->6H7/2) along with a red (4G5/2-->6H9/2) and a yellow (4G5/2-->6H5/2) emission transition have been measured from Sm3+ doped lithium-boro-tellurite glass. Both blue (4F9/2-->6H15/2) and yellow (4F9/2-->6H13/2) emission bands have been obtained from Dy3+ glass. From the measured decay profiles, the lifetimes of the emissions of the Sm3+ glass (4G5/2-->6H5/2, 7/2, 9/2 and 11/2) at an excitation of 401 nm have been found to be in the range 0.47-0.81 ms, and with respect to the Dy3+ emissions (4F9/2-->6H15/2 and 13/2), with excitation at 450 nm, are measured to be in the range of 0.302-0.307 ms. Stimulated emission cross-sections (sigmapE) of the measured emission transitions have also been computed and the values are in the range of (0.38-1.20) x 10(-20) cm2 for Sm3+ and for Dy3+ doped lithium-boro-tellurite glass the values are (0.66-1.39) x 10(-20) cm2.

  12. Effect of B2O3 on luminescence of erbium doped tellurite glasses.

    Science.gov (United States)

    Shen, Xiang; Nie, Qiuhua; Xu, Tiefeng; Dai, Shixun; Wang, Xunsi

    2007-02-01

    The B2O3 was introduced into the Er3+ doped TeO2-ZnO-Na2O glass to increase the phonon energy of the host. The effect of B2O3 on the non-radiative rate of the 4I11/2-->4I13/2 transition of Er3+, the lifetime of the 4I11/2 and 4I13/2 levels, the green and red upconversion emissions intensity, and the 4I13/2-->4I15/2 emission intensity was discussed. The results show that the phonon energy of boro-tellurite glass is close to that of germanate glass and is quite smaller than that of borate glass. The lifetime of 4I11/2 level and the upconversion emissions decrease with increasing B2O3 concentration. The higher OH group concentration presented in the boro-tellurite glass may shorten the lifetime of 4I13/2 level and also reduce the quantum efficiency of 4I13/2-->4I15/2 emission. The future dehydrating procedures are suggested to enhance the efficiency of amplification at 1.5 microm band.

  13. Spectroscopy of Yb-doped tungsten-tellurite glass and assessment of its lasing properties

    Science.gov (United States)

    Merzliakov, M. A.; Kouhar, V. V.; Malashkevich, G. E.; Pestryakov, E. V.

    2018-01-01

    Glasses of the TeO2-WO3-Yb2O3 system are synthesized for wide range of Yb3+ concentrations of up to 6.0 × 1021 ions/cm3. The spectral-luminescent properties of lightly doped samples are investigated at room temperature and at the boiling point of liquid nitrogen. The energies of the Stark levels of the ground and excited states of Yb3+ ions incorporated into tungsten-tellurite glass are determined by analyzing the low-temperature spectra. The absorption, emission, and gain cross section spectra are obtained. The excess of the measured fluorescence decay time over the radiative lifetime ∼0.3 ms derived from the absorption spectra is attributed to the reabsorption effect in bulk samples. Measurements of lightly doped glass powder in the immersion liquid are made to reduce the effect of reabsorption. The fluorescence decay time of the powder is very close to the calculated radiative lifetime. Compared with phosphate, silicate, and other Yb3+-doped glasses, the tungsten-tellurite glass has a promising potential as a gain medium for lasers and amplifiers.

  14. Natural Fe3O4 nanoparticles embedded zinc–tellurite glasses: Polarizability and optical properties

    International Nuclear Information System (INIS)

    Widanarto, W.; Sahar, M.R.; Ghoshal, S.K.; Arifin, R.; Rohani, M.S.; Hamzah, K.; Jandra, M.

    2013-01-01

    Modifying the optical behavior of zinc–tellurite glass by embedding magnetic nanoparticles has implication in nanophotonics. A series of zinc–tellurite glasses containing natural Fe 3 O 4 nanoparticles with composition (80 − x)TeO 2 ·xFe 3 O 4 ·20ZnO (0 ≤ x ≤ 2) in mol% are synthesized by melt quenching method and their optical properties are investigated using FTIR and UV–vis–NIR spectroscopies. Lorentz–Lorenz relations are exploited to determine the refractive index, molar refraction and electronic polarizability. The sharp absorption peaks of FTIR spectra show a shift from 667 cm −1 to 671 cm −1 in the presence of nanoparticles that increase the non-bridging oxygen, confirmed by the intensity change of the TeO 3 peak at 752 cm −1 . A new peak around 461 cm −1 is also observed which is attributed to the band characteristic of covalent Fe–O linkages. A decrease in the Urbach energy as much as 0.122 eV and the optical energy band gap with the increase of Fe 3 O 4 concentration (0.5–1.0 mol%) is evidenced. Electronic polarizability of the glasses increases with increasing Fe 3 O 4 nanoparticles concentration up to 1 mol%. Interestingly, the polarizability tends to decrease with the further increase of Fe 3 O 4 concentration at 2 mol%. The role of magnetic nanoparticles in influencing the structural and optical behavior are examined and understood. - Highlights: ► Incorporation of natural Fe 3 O 4 nanoparticles into the zinc–tellurite glass. ► Influence of magnetic nanoparticles in modifying structure and optical properties. ► Enhancement of refraction index and change in electronic polarizability

  15. Electronic Conductivity of Vanadium-Tellurite Glass-Ceramics

    DEFF Research Database (Denmark)

    Kjeldsen, Jonas; Yue, Yuanzheng; Bragatto, Caio B.

    2013-01-01

    In this paper, we investigate the electronic conductivity of 2TeO2-V2O5 glass-ceramics with crystallinity ranging from 0 to 100 wt.%, i.e., from entirely amorphous to completely crystalline. The glass is prepared by the melt quenching technique, and the crystal is prepared by subsequent heat...... spectroscopy. We find similar activation energies for both glass and crystal, implying that they have similar conduction mechanisms, i.e., thermally activated hopping. The electronic conductivity of 2TeO2-V2O5 glass is about one order of magnitude higher than that of the corresponding crystal......, and a percolation phenomenon occurs at a glass fraction of 61 wt.%, increasing from a lower conductivity in the crystal to a higher conductivity in the glass. We explain the behavior of electronic conduction in the 2TeO2-V2O5 glass-ceramics by considering constriction effects between particles as well...

  16. Short-range structure and thermal properties of barium tellurite glasses

    Science.gov (United States)

    Kaur, Amarjot; Khanna, Atul; Gonzàlez, Fernando

    2017-05-01

    BaO-TeO2 glasses containing 10 to 20 BaO mol% were prepared and characterized by X-ray diffraction, density measurements, differential scanning calorimetry and Raman spectroscopy. Glass density decreases with increase in BaO concentration from 10 to 20 mol%, due to replacement of heavier TeO2 by lighter BaO, however glass transition temperature (Tg) increases significantly from a value of 318°C to 327°C due to increase in average single bond enthalpy of the tellurite network. Raman studies found that glass short-range structure consists of TeO4 and TeO3 structural units and BaO modifies the network by producing the structural transformation: TeO4→ TeO3.

  17. Effect of heat treatment on the structural and optical properties of tellurite glasses doped erbium

    Energy Technology Data Exchange (ETDEWEB)

    Jlassi, I., E-mail: ifa.jlassi@fst.rnu.tn [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95 Hammam-Lif 2050 (Tunisia); Elhouichet, H. [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95 Hammam-Lif 2050 (Tunisia); Departement de Physique, Faculte des Sciences de Tunis, Campus ElManar 2092 (Tunisia); Hraiech, S.; Ferid, M. [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95 Hammam-Lif 2050 (Tunisia)

    2012-03-15

    The 75TeO{sub 2}-20ZnO-4Na{sub 2}CO{sub 3}-1Er{sub 2}O{sub 3} (in molar ratio) glass system was prepared by the conventional melt-quenching method. As such, the samples prepared were investigated by differential scanning calorimetry (DSC), X-ray diffractrometry (XRD), Raman spectroscopy and infrared luminescence. DSC analyses were carried out on our glass at different heating rates between 5 and 20 Degree-Sign C/min. The result of the annealing temperature on the spectroscopic properties of Er{sup 3+} in tellurite glasses was discussed. The activation energy, for surface crystallization, was determined graphically from a Kissinger-type plot and had a value about 897.2 kJ/mol. Crystalline phases for both {alpha}-TeO{sub 2}, {gamma}-TeO{sub 2} and Zn{sub 2}Te{sub 3}O{sub 8} system were determined by the XRD method and were confirmed by Raman spectroscopy characterizations after heat treatment. The effect of heat treatment on absorption spectra and luminescence properties in the tellurite glass was also investigated. With heat treatment, the ultraviolet absorption edge presented a redshift. As a result, the Judd-Ofelt (J-O) intensity parameters ({Omega}{sub 2}, {Omega}{sub 4}, {Omega}{sub 6}) were determined. The spontaneous emission probabilities of some relevant transitions, the branching ratio and the radiative lifetimes of several excited states of Er{sup 3+} were predicted using intensity J-O parameters. The near infrared emission that corresponds to Er{sup 3+}: {sup 4}I{sub 13/2}{yields}{sup 4}I{sub 15/2} can be significantly enhanced after heat treatment. Notably, it is found that the luminescence lifetime in the present system is much longer than that in most other glasses and glass ceramics. A comparative study on luminescence performance suggests that the obtained glass ceramic is a promising material for Er{sup 3+} doped fiber amplifiers. - Highlights: Black-Right-Pointing-Pointer Tellurite glasses were prepared by conventional melt-quenching method. Black

  18. Optical properties of samarium doped zinc–tellurite glasses

    Indian Academy of Sciences (India)

    Unknown

    Optical absorption spectra of these glasses were recorded in the range 300–700 nm at room ... cause of their potential as hosts of rare earth elements for ... nature of these glasses was examined by X-ray diffraction ... absorption coefficient).

  19. The influence of ytterbium doping on the optical properties of tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Jaglarz, Janusz; Burtan, Bozena [Institute of Physics, Cracow University of Technology, ul. Podchorazych 1, 30-084 Cracow (Poland); Reben, Manuela; Wasylak, Jan [Faculty of Materials Science and Ceramics, AGH - University of Science and Technology, al. Mickiewicza 30, 30-059 Cracow (Poland); Cisowski, Jan [Institute of Physics, Cracow University of Technology, ul. Podchorazych 1, 30-084 Cracow (Poland); Centre of Polymer and Carbon Materials, Polish Academy of Sciences, ul. M. Curie-Sklodowskiej 34, 41-819 Zabrze (Poland); Jarzabek, Bozena [Centre of Polymer and Carbon Materials, Polish Academy of Sciences, ul. M. Curie-Sklodowskiej 34, 41-819 Zabrze (Poland)

    2011-09-15

    The goal of this work was to investigate the influence of rare earth ion Yb{sup 3+} doping on the thermal and optical properties of tellurite glass (TG) of the TeO{sub 2}-ZnO-PbO-La{sub 2}O{sub 3} system. The reflectance, transmittance and ellipsometric measurements have been done. Decreasing of the refractive index of TG with the Yb{sup 3+} ion doping has been concluded. For determination of the refractive index variation in the bulk, the small angle light scatter (SALS) measurements have been carried out. (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  20. Dy{sup 3+} ions as optical probes for studying structure of boro-tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Tuyen, Vu Phi, E-mail: vptuyen@gust-edu.vast.vn [Duytan University, K7/25 Quang Trung, Da Nang (Viet Nam); Graduate University of Science and Technology – VAST, 18 Hoang Quoc Viet, Hanoi (Viet Nam); Sengthong, Bounyavong; Quang, Vu Xuan [Duytan University, K7/25 Quang Trung, Da Nang (Viet Nam); Van Do, Phan [Thuyloi University, 175 Tay Son, Dong Da, Hanoi (Viet Nam); Van Tuyen, Ho; Xuan Hung, Le [Duytan University, K7/25 Quang Trung, Da Nang (Viet Nam); Thanh, Nguyen Trong [Institute of Materials Science – VAST, 18 Hoang Quoc Viet, Hanoi (Viet Nam); Nogami, Masayuki [Duytan University, K7/25 Quang Trung, Da Nang (Viet Nam); Toyota Physical and Chemical research Institute (Japan); Hayakawa, Tomokatsu [Nagoya Institute of Technology, Gokisocho Showaku, 466-8555 Nagoya, Aichiken (Japan); Huy, Bui The, E-mail: buithehuy.nt@gmail.com [Duytan University, K7/25 Quang Trung, Da Nang (Viet Nam); Department of Chemistry, Changwon National University, Changwon 641-773 (Korea, Republic of)

    2016-10-15

    Dy{sup 3+}-doped glasses with various compositions (35+x)B{sub 2}O{sub 3}+ (45−x)TeO{sub 2}+9.5ZnO+10Na{sub 2}O+0.5Dy{sub 2}O{sub 3} (x=0; 10 and 20) were prepared by a melt–quenching technique. The Dy{sup 3+} ions are used as an optical probe, of which the Judd–Ofelt parameters, the phonon-side band, and the Raman spectra were quantitatively estimated to search the change of glass structure (the change of the ratio of [BO{sub 4}] to [BO{sub 3}] units, formation of the non-bridging oxygens (NBO{sup −}), the change of [TeO{sub 3}] to [TeO{sub 4}] units) as a function of the B{sub 2}O{sub 3} content. The Ω{sub 2} and Ω{sub 6} values of Dy{sup 3+}-doped boro-tellurite samples are larger than that of Dy{sup 3+}-doped borate or tellurite sample. The CIE chromaticity color coordinates were calculated for the luminescence spectra of Dy{sup 3+} ions of the glasses with the different compositions and they were all located in the vicinity of white light center of the color coordination diagram.

  1. Structural studies on iron-tellurite glasses prepared by sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Rada, S., E-mail: Simona.Rada@phys.utcluj.r [Department of Physics, Technical University of Cluj-Napoca, Bibliotecii, No. 10, 400020 Cluj-Napoca (Romania); Dehelean, A. [Department of Physics, Technical University of Cluj-Napoca, Bibliotecii, No. 10, 400020 Cluj-Napoca (Romania); Nat. Inst. for R and D of Isotopic and Molec. Technologies, Cluj-Napoca (Romania); Stan, M. [Nat. Inst. for R and D of Isotopic and Molec. Technologies, Cluj-Napoca (Romania); Chelcea, R. [Department of Physics, Technical University of Cluj-Napoca, Bibliotecii, No. 10, 400020 Cluj-Napoca (Romania); Nat. Inst. for R and D of Isotopic and Molec. Technologies, Cluj-Napoca (Romania); Culea, E. [Department of Physics, Technical University of Cluj-Napoca, Bibliotecii, No. 10, 400020 Cluj-Napoca (Romania)

    2011-01-05

    Research highlights: {yields} Iron-tellurite glasses obtained using the sol-gel synthesis. - Abstract: In this study, we report structural properties of the iron-tellurite glasses obtained using the sol-gel synthesis. The samples were characterized by X-ray diffraction, FTIR, UV-vis and EPR spectroscopy. Our results indicate dominant presence of iron ions in the trivalent state and the existence some Fe{sup 2+} ions. The analysis of the IR spectra indicates a gradual transformation of iron ions from tetrahedral into octahedral sites when the concentration of Fe(NO{sub 3}){sub 3} is increased beyond 0.64 mol%. EPR studies show that the increase of Fe(NO{sub 3}){sub 3} content in the host matrix induces the growth of the number of effective g values. This can be explained considering that the orbitals of O{sup 2-} ion with a large spin-orbit interaction constant will interact with the 3d orbital of Fe{sup 3+} ion bonded to this O{sup 2-} ion, thus leading to appearance of an orbital angular momentum which contributes to the magnetic moment of Fe{sup 3+} ion. A strong dipolar interaction, which is more predominant in a glass with higher content of Fe(NO{sub 3}){sub 3}, causing a localized magnetic field along the site of the Fe{sup 3+} ions and the increase the effective g values.

  2. Thermal and optical properties of Tm3+ doped tellurite glasses.

    Science.gov (United States)

    Ozen, G; Demirata, B; Oveçoğlu, M L; Genç, A

    2001-02-01

    Ultraviolet, visible (UV/VIS) and differential thermal analysis (DTA) measurements were carried out in order to investigate the optical and thermal properties of various 0.5 mol.% Tm2O3 containing (1 - x)TeO2 + xLiCl glasses in molar ratio. The samples were prepared by fusing the mixture of their respective reagent grade powders in a platinum cricuble at 750 degrees C for 30 min. DTA curves taken in the 23-600 degrees C temperature range with a heating rate of 10 degrees C/min reveal a change in the value of the glass transition temperature, Tg, while melting was not observed for the glasses containing LiCl content less than 50 mol.%. These glasses were found to be moisture-resistant. However, the glasses with LiCl content higher than 50 mol.%, in which a melting peak was observed at Tc = 401 degrees C, were moisture-sensitive. Absorption measurements in the UV/VIS region of the glasses without Tm2O3 content show that the Urbach cutoff occurs at about 320 nm and, is relatively independent of the LiCl content. Six absorption bands were observed in the Tm2O3 doped glasses corresponding to the absorption of the 1G4, 3F2, 3F3 and 3F4, 3H5 and 3H4 levels from the 3H6 ground level of Tm3+ ions. The spectra also show that the integrated absorption cross-section of each band depends on the glass composition. Judd-Ofelt theory was used to determine the Judd-Ofelt parameters as well as the radiative transition probabilities for the metastable levels of Tm3+ ions in (0.3)LiCl + (0.7) TeO2: 0.01 Tm2O3 glass which is moisture-resistant.

  3. Effect of co-doping Tm3+ ions on the emission properties of Dy3+ ions in tellurite glasses

    International Nuclear Information System (INIS)

    Sasikala, T.; Rama Moorthy, L.; Mohan Babu, A.; Srinivasa Rao, T.

    2013-01-01

    The present work reports the absorption, photoluminescence and decay properties of singly doped Dy 3+ and co-doped Dy 3+ /Tm 3+ ions in TeO 2 +ZnO+K 2 O+CaO (TZKC) glasses prepared by the melt quenching technique. The glassy nature of the host glass has been confirmed by X-ray diffraction analysis and the primary vibrational modes were determined from the Raman spectrum. Judd–Ofelt (JO) analysis has been used to calculate the radiative transition rates, branching ratios and radiative lifetime of the emitting 4 F 9/2 state. The effect of co-doping of different concentrations of Tm 3+ ions on the emission properties of Dy 3+ ions has been investigated. The decay profiles of the 4 F 9/2 level were fitted to double exponential as well as Inokuti–Hirayama (IH) model to determine the energy transfer rates between Dy 3+ and Tm 3+ ions. The energy transfer rates found to increase with the increase of Tm 3+ ions concentration. The chromaticity coordinates and color purity of the emitted light for all glasses were determined. - Graphical abstract: The graphical abstract shows the emission spectra of Dy 3+ , Tm 3+ and Dy 3+ /Tm 3+ co-doped TZKC glasses recorded by exciting at 355 nm wavelength. - Highlights: • Zinc tellurite glasses doped with Dy 3+ , Tm 3+ and Dy 3+ /Tm 3+ ions were prepared. • XRD, DTA and Raman spectral measurements were recorded to know the nature of host. • Energy transfer occurs from Dy 3+ ions to Tm 3+ ions. • The color purity of the emitted light was determined

  4. Preparation and characterization of boro-tellurite glasses

    Science.gov (United States)

    Kaur, Nirmal; Khanna, Atul; Krishna, P. S. R.

    2014-04-01

    Glass samples of the system: xB2O3-(100-x) TeO2; x= 15, 20, 25 and 30 mol% were prepared by melt quenching and characterized by X-ray diffraction, density measurements, Differential Scanning Calorimetry and FTIR spectroscopy. XRD confirmed the amorphous structure of all samples. Density of glasses decreased with increase in B2O3 concentration due to the replacement of heavier TeO2 with lighter B2O3 whereas the glass transition temperature increased from 339°C to 366°C; the later effect was due to increase in the concentration of stronger B-O bonds in the glass network. FTIR studies found that BO4 units convert into BO3 with the addition of B2O3.

  5. Preparation and characterization of boro-tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Nirmal, E-mail: akphysics@yahoo.com; Khanna, Atul, E-mail: akphysics@yahoo.com [Glass Physics and Sensors Laboratory, Department of Physics, Guru Nanak Dev University, Amritsar-143005, Punjab (India); Krishna, P. S. R. [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai-400085, Maharashtra (India)

    2014-04-24

    Glass samples of the system: xB{sub 2}O{sub 3}−(100−x) TeO{sub 2}; x= 15, 20, 25 and 30 mol% were prepared by melt quenching and characterized by X-ray diffraction, density measurements, Differential Scanning Calorimetry and FTIR spectroscopy. XRD confirmed the amorphous structure of all samples. Density of glasses decreased with increase in B{sub 2}O{sub 3} concentration due to the replacement of heavier TeO{sub 2} with lighter B{sub 2}O{sub 3} whereas the glass transition temperature increased from 339°C to 366°C; the later effect was due to increase in the concentration of stronger B-O bonds in the glass network. FTIR studies found that BO{sub 4} units convert into BO{sub 3} with the addition of B{sub 2}O{sub 3}.

  6. Optical properties of lead–tellurite glasses doped with samarium ...

    Indian Academy of Sciences (India)

    Administrator

    392. Table 1. Density, molar volume, optical energy bandgap, refractive index, molar refraction and polarizability of oxide ion for. Sm2O3–PbO–TeO2 glasses. Glass composition (mol%). Energy. Molar. Polarizability. Density Molar volume bandgap. Refractive refraction. (αe). Sm2O3. PbO. TeO2. (ρ) (g/cm. 3. ) (Vm) (cm. –3. ).

  7. Luminescent properties of Ln3+ doped tellurite glasses containing AlF3

    Science.gov (United States)

    Walas, Michalina; Pastwa, Agata; Lewandowski, Tomasz; Synak, Anna; Gryczyński, Ignacy; Sadowski, Wojciech; Kościelska, Barbara

    2016-09-01

    The low-phonon energy tellurite glasses TeO2-BaO-Bi2O3 and TeO2-BaO-Bi2O3-AlF3 triply doped with Eu3+, Tb3+, Tm3+ ions in two different molar ratios were synthesized using melt-quenching technique. Their structure and luminescence properties were widely investigated by X-ray Diffraction (XRD), Differential Scanning Calorimetry (DSC), Fourier Transform Infrared Spectroscopy (FTIR) and Photoluminescence Spectroscopy (PL). The luminescence spectra of Eu3+, Tb3+, Tm3+ co-doped glasses show apart of the bands corresponding to the 4f-4f transitions of lanthanide ions also band corresponding to glass matrix. AlF3 doping increases emission intensity, although to improve overall emission color further studies on molar composition of samples and the molar ratio of the components should be carried out.

  8. Assessment of lead tellurite glass for immobilizing electrochemical salt wastes from used nuclear fuel reprocessing

    Energy Technology Data Exchange (ETDEWEB)

    Riley, Brian J.; Kroll, Jared O.; Peterson, Jacob A.; Pierce, David A.; Ebert, William L.; Williams, Benjamin D.; Snyder, Michelle M. V.; Frank, Steven M.; George, Jaime L.; Kruska, Karen

    2017-11-01

    This paper provides an overview of research evaluating the use of tellurite glass as a waste form for salt wastes from electrochemical processing. The capacities to immobilize different salts were evaluated including: a LiCl-Li2O oxide reduction salt (for oxide fuel) containing fission products, a LiCl-KCl eutectic salt (for metallic fuel) containing fission products, and SrCl2. Physical and chemical properties of the glasses were characterized by using X-ray diffraction, bulk density measurements, chemical durability tests, scanning electron microscopy, and energy dispersive X-ray emission spectroscopy. These glasses were found to accommodate high concentrations of halide salts and have high densities. However, improvements are needed to meet chemical durability requirements.

  9. Comparative Spectroscopic Investigation of Tm3+:Tellurite Glasses for 2-μm Lasing Applications

    Directory of Open Access Journals (Sweden)

    Huseyin Cankaya

    2018-02-01

    Full Text Available We performed a comparative spectroscopic analysis on three novel Tm3+:tellurite-based glasses with the following compositions Tm2O3:TeO2-ZnO (TeZnTm, Tm2O3:TeO2-Nb2O5 (TeNbTm, and Tm3+:TeO2-K2O-Nb2O5 (TeNbKTm, primarily for 2-μm laser applications. Tellurite glasses were prepared at different doping concentrations in order to investigate the effect of Tm3+ ion concentration as well as host composition on the stimulated emission cross sections and the luminescence quantum efficiencies. By performing Judd–Ofelt analysis, we determined the average radiative lifetimes of the 3H4 level to be 2.55 ± 0.07 ms, 2.76 ± 0.03 ms and 2.57 ± 0.20 ms for the TeZnTm, TeNbTm and TeNbKTm samples, respectively. We clearly observed the effect of the cross-relaxation, which becomes significant at higher Tm2O3 concentrations, leading to the quenching of 1460-nm emission and enhancement of 1860-nm emission. Furthermore, with increasing Tm2O3 concentrations, we observed a decrease in the fluorescence lifetimes as a result of the onset of non-radiative decay. For the 3H4 level, the highest obtained quantum efficiency was 32% for the samples with the lowest Tm2O3 ion concentration. For the 1860-nm emission band, the average emission cross section was determined to measure around 6.33 ± 0.34 × 10−21 cm2, revealing the potential of thulium-doped tellurite gain media for 2-μm laser applications in bulk and fiber configurations.

  10. Study of boro-tellurite glasses doped with neodymium oxide

    Science.gov (United States)

    Sanjay, Kishore, N.; Sheoran, M. S.; Devi, S.

    2018-05-01

    Borotellurite glasses doped with Nd2O3 [xB2O3(95-x)TeO25Nd2O3] have been prepared by the standard melt-quenching technique. Amorphous nature of the present system was estimated by XRD patterns. The thermal parameters like glass transition temperature (Tg), crystallization (Tc) and melting (Tm) temperatures have been estimated from differential scanning calorimetry (DSC) traces. Density and molar volume have been determined. It was found that Tg is increased due to increasing number of Te-O bonds were replaced by a number of stronger B-O bonds whereas density was decreased with an increase in B2O3 content is due to the higher degree of cross-bonding between the Boron and non-bridging oxygen ions resulting in a strengthening of glass network.

  11. Structural and spectroscopic studies on Er{sup 3+} doped boro-tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Selvaraju, K. [Department of Physics, Gandhigram Rural University, Gandhigram - 624 302 (India); Marimuthu, K., E-mail: mari_ram2000@yahoo.com [Department of Physics, Gandhigram Rural University, Gandhigram - 624 302 (India)

    2012-04-01

    Er{sup 3+} doped boro-tellurite glasses with the chemical composition (69-x)B{sub 2}O{sub 3}-xTeO{sub 2}-15MgO-15K{sub 2}O-1Er{sub 2}O{sub 3} (where x=0, 10, 20, 30 and 40 wt%) have been prepared and their structural and spectroscopic behavior were studied and reported. The varying tellurium dioxide content in the host matrix that results, changes in structural and spectroscopic behavior around Er{sup 3+} ions are explored through XRD, FTIR, UV-VIS-NIR and luminescence measurements. The XRD pattern confirms the amorphous nature of the prepared glasses and the FTIR spectra explore the fundamental groups and the local structural units in the prepared boro-tellurite glasses. The bonding parameters ({beta}{sup Macron} and {delta}) have been calculated from the observed band positions of the absorption spectra to claim the ionic/covalent nature of the prepared glasses. The Judd-Ofelt (JO) intensity parameters {Omega}{sub {lambda}} ({lambda}=2, 4 and 6) were determined through experimental and calculated oscillator strengths obtained from the absorption spectra and their results are studied and compared with reported literature. The variation in the JO parameters {Omega}{sub {lambda}} ({lambda}=2, 4 and 6) with the change in chemical composition have been discussed in detail. The JO parameters have also been used to derive the important radiative properties like transition probability (A), branching ratio ({beta}{sub R}) and peak stimulated emission cross-section ({sigma}{sub P}{sup E}) for the excited state transitions {sup 2}H{sub 9/2}{yields}{sup 4}I{sub 15/2} and {sup 2}H{sub 11/2} and {sup 4}S3{sub /2}{yields}{sup 4}I{sub 15/2} of the Er{sup 3+} ions and the results were studied and reported. Using Davis and Mott theory, optical band gap energy (E{sub opt}) values for the direct and indirect allowed transitions have been calculated and discussed along with the Urbach energy values for the prepared Er{sup 3+} doped boro-tellurite glasses in the present study. The

  12. Structural and spectroscopic studies on Er3+ doped boro-tellurite glasses

    Science.gov (United States)

    Selvaraju, K.; Marimuthu, K.

    2012-04-01

    Er3+ doped boro-tellurite glasses with the chemical composition (69-x)B2O3-xTeO2-15MgO-15K2O-1Er2O3 (where x=0, 10, 20, 30 and 40 wt%) have been prepared and their structural and spectroscopic behavior were studied and reported. The varying tellurium dioxide content in the host matrix that results, changes in structural and spectroscopic behavior around Er3+ ions are explored through XRD, FTIR, UV-VIS-NIR and luminescence measurements. The XRD pattern confirms the amorphous nature of the prepared glasses and the FTIR spectra explore the fundamental groups and the local structural units in the prepared boro-tellurite glasses. The bonding parameters (βbar and δ) have been calculated from the observed band positions of the absorption spectra to claim the ionic/covalent nature of the prepared glasses. The Judd-Ofelt (JO) intensity parameters Ωλ (λ=2, 4 and 6) were determined through experimental and calculated oscillator strengths obtained from the absorption spectra and their results are studied and compared with reported literature. The variation in the JO parameters Ωλ (λ=2, 4 and 6) with the change in chemical composition have been discussed in detail. The JO parameters have also been used to derive the important radiative properties like transition probability (A), branching ratio (βR) and peak stimulated emission cross-section (σPE) for the excited state transitions 2H9/2→4I15/2 and 2H11/2 and 4S3/2→4I15/2 of the Er3+ ions and the results were studied and reported. Using Davis and Mott theory, optical band gap energy (Eopt) values for the direct and indirect allowed transitions have been calculated and discussed along with the Urbach energy values for the prepared Er3+ doped boro-tellurite glasses in the present study. The optical properties of the prepared glasses with the change in tellurium dioxide have been studied and compared with similar results.

  13. Low-frequency Raman scattering in alkali tellurite glasses

    Indian Academy of Sciences (India)

    Wintec

    utilization of these glasses for non-linear optical materials. (Shioya et al 1995) and ... laser–vertical analysis of scattered light) and depolarized (VH: vertical polarization .... data as described in the text and (b) exponent of power law vs. 1/ R. 2.

  14. Structural, thermal and optical absorption features of heavy metal oxides doped tellurite rich glasses

    Directory of Open Access Journals (Sweden)

    Kawa M. Kaky

    Full Text Available In order to improve tellurite glass stability to be applicable for optical fiber amplifier applications, glasses with the composition of (70 − xTeO2. (10ZnO. (10WO3. (5Na2O. (5TiO2. (xBi2O3 (x = 1, 2, 3, 4, and 5 mol% have been produced and characterized using the related methods. Structural properties were investigated using X-ray diffraction (XRD which confirms the non-crystalline structure and scanning electron microscopy (SEM micrographs also confirm the XRD results. The energy dispersive X-ray (EDX analysis profiles show that all the mentioned elements are present in the prepared glasses. Following the IR spectra, all the tellurium bonds such as stretching vibrations of TeO4 tbp and TeO3/TeO3+1 unit are revealed. Raman spectra confirm the presence of different functional groups, actually, it shows bands mainly in four spectral regions: R1 (65–150 cm−1, R2 (280–550 cm−1, R3 (880–950 cm−1 and R4 (916–926 cm−1 and the identified bands are assigned to respective molecular groups. The thermal study was carried out using Differential scanning calorimetry (DSC which indicates good thermal stability of the synthesized glasses with increasing Bi concentration. From the optical absorption spectra, we evaluated cut-off edge wavelengths and found increasing cutoff wavelength with an increase in Bi2O3 concentration. In the UV–Visible region, optical band gap energy and allowed transitions were investigated using three methods; direct, indirect, and absorption spectrum fitting (ASF, and band gaps from indirect and ASF were matched. Keywords: Tellurite glasses, XRD, FT-IR, Raman, TGA/DSC

  15. Comparative investigation on the spectroscopic properties of Pr³⁺-doped boro-phosphate, boro-germo-silicate and tellurite glasses.

    Science.gov (United States)

    Zhang, Liaolin; Dong, Guoping; Peng, Mingying; Qiu, Jianrong

    2012-07-01

    We report on the spectroscopic properties of Pr(3+)-doped boro-phosphate, boro-germo-silicate and tellurite glasses. The stimulated absorption and emission cross sections were estimated. Only one emission at 596 nm and 605 nm is observed in Pr(3+)-doped boro-phosphate and boro-germo-silicate glasses, respectively, while three emissions at 605 nm, 612 nm and 645 nm are observed in Pr(3+)-doped tellurite glass when excited at 467 nm. The fluorescence lifetime at 600 nm in Pr(3+)-doped boro-phosphate, boro-germo-silicate and tellurite glasses is 137 μs, 73 μs and 51 μs, respectively. The emissions from Pr(3+)-doped boro-phosphate, boro-germo-silicate and tellurite glasses show different decay behaviors and can be well explained by multiphonon relaxation theory. Copyright © 2012 Elsevier B.V. All rights reserved.

  16. Electrical properties of praseodymium oxide doped Boro-Tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Jagadeesha Gowda, G.V. [Dept. of Physics, Sapthagiri College of Engineering, Bengaluru,India.Email:jagadeeshphy@rediffmail.com (India); Devaraja, C. [Dept.of Physics, Nagarjuna college of engineering and Technology, Bengaluru. India Email: deva.drr@rediffmail.com (India); Eraiah, B. [Dept.of Physics, Bangalore University, Bengaluru,India.Email:eraiah@rediffmail.com (India)

    2016-05-06

    Glasses of the composition xPr{sub 6}O{sub 11}- (35-x)TeO{sub 2}-65B{sub 2}O{sub 3} (x=0, 0.1 to 0.5 mol %) have been prepared using the melt quenching method. The ac and dc conductivity of glass have been measured over a wide range of frequencies and temperatures. Experimental results indicate that the ac conductivity depend on temperature, frequency and Praseodymium content. The conductivity as a function of frequency exhibited two components: dc conductivity (σ{sub dc}), and ac conductivity (σ{sub ac}). The activation energies are estimated and found to be decreases with composition. The impedance plot at each temperature appeared as a semicircle passes through the origin.

  17. Electrical properties of praseodymium oxide doped Boro-Tellurite glasses

    Science.gov (United States)

    Jagadeesha Gowda G., V.; Devaraja, C.; Eraiah, B.

    2016-05-01

    Glasses of the composition xPr6O11- (35-x)TeO2-65B2O3 (x=0, 0.1 to 0.5 mol %) have been prepared using the melt quenching method. The ac and dc conductivity of glass have been measured over a wide range of frequencies and temperatures. Experimental results indicate that the ac conductivity depend on temperature, frequency and Praseodymium content. The conductivity as a function of frequency exhibited two components: dc conductivity (σdc), and ac conductivity (σac). The activation energies are estimated and found to be decreases with composition. The impedance plot at each temperature appeared as a semicircle passes through the origin.

  18. Plasmon-Assisted Efficiency Enhancement of Eu3+-Doped Tellurite Glass-Covered Solar Cells

    Science.gov (United States)

    Lima, Bismarck C.; Gómez-Malagón, L. A.; Gomes, A. S. L.; Garcia, J. A. M.; Kassab, L. R. P.

    2017-12-01

    Rare-earth-doped tellurite glass containing metallic nanoparticles can be exploited to manage the solar spectrum in order to increase solar cell efficiency. It is therefore possible to modify the incident solar spectrum profile to the spectrum that optimizes the solar cell recombination process by covering the solar cell with plasmonic luminescent downshifting layers. With this approach, the losses due to thermalization are minimized and the efficiency is increased. Due to the down-conversion process that couples the plasmon resonance of the metallic nanoparticles and the rare-earth electronic energy levels, it is possible to convert photons from the ultraviolet region to the visible and near-band-gap region of the semiconductor. It is demonstrated here that plasmon-assisted efficiency enhancements of 14.0% and 34.5% can be obtained for commercial Si and GaP solar cells, respectively, covered with Eu3+-doped TeO2-ZnO glass containing silver nanoparticles.

  19. Study of absorption and IR-emission of Er3+, Dy3+, Tm3+ doped high-purity tellurite glasses

    Science.gov (United States)

    Motorin, S. E.; Dorofeev, V. V.; Galagan, B. I.; Sverchkov, S. E.; Koltashev, V. V.; Denker, B. I.

    2018-04-01

    A study of high-purity TeO2-ZnO based tellurite glasses doped with Er3+, Dy3+ or Tm3+ that could be used as laser media in the 2-3 μm spectral range is presented. The glasses are prepared by melting the oxides mixture inside a silica glass reactor in an atmosphere of purified oxygen. The low level of hydroxyl groups absorption allowed to measure correctly the luminescence decay characteristics of the dopants. The rare-earth ions absorption bands, the luminescence spectra and kinetic characteristics of emission from the levels 4I11/2, 4I13/2 of Er3+, 6H13/2 of Dy3+ and 3H4, 3H5, 3F4 of Tm3+ ions are investigated. The results confirm the high potential of tellurite glasses as an active media for bulk, planar waveguide and fiber lasers.

  20. Evaluation of shielding parameters for heavy metal fluoride based tellurite-rich glasses for gamma ray shielding applications

    International Nuclear Information System (INIS)

    Sayyed, M.I.; Lakshminarayana, G.; Kityk, I.V.; Mahdi, M.A.

    2017-01-01

    In this work, we have evaluated the γ-ray shielding parameters such as mass attenuation coefficient (μ/ρ), effective atomic number (Z eff ), half value layer (HVL), mean free path (MFP) and exposure buildup factors (EBF) for heavy metal fluoride (PbF 2 ) based tellurite-rich glasses. In addition, neutron total macroscopic cross sections (∑ R ) for these glasses were also calculated. The maximum value for µ/ρ, Z eff and ∑ R was found for heavy metal (Bi 2 O 3 ) oxide introduced glass. The results of the selected glasses have been compared, in terms of MFP with different glass systems. The shielding effectiveness of the selected glasses is found comparable or better than of common ones, which indicates that these glasses with suitable oxides could be developed for gamma ray shielding applications. - Highlights: • μ/ρ, Z eff , HVL and MFP for PbF 2 based tellurite-rich glasses have been calculated. • µ/ρ and Z eff depend on the photon energy and chemical composition of the glasses. • EBF values of these glasses have been calculated using G-P fitting method. • The maximum value for µ/ρ and Z eff was found for Bi 2 O 3 oxide introduced glass. • New types of non-traditional radiation shielding glasses are demonstrated.

  1. Enhanced luminescence from silver nanoparticles integrated Er{sup 3+}-doped boro-tellurite glasses: Impact of annealing temperature

    Energy Technology Data Exchange (ETDEWEB)

    Said Mahraz, Zahra Ashur; Sahar, M.R., E-mail: mrahim057@gmail.com; Ghoshal, S.K.

    2015-11-15

    Considerable enhancement of rare earth ions luminescence intensity stimulated via metal nanoparticles (NPs) inclusion inside inorganic glass matrix opened a new avenue to achieving efficient lasing glass media. Tuning the localised surface plasmon resonance (LSPR) band of noble metal NPs through their precise size manipulation is demonstrated to be the key for such accomplishment. We report the influences of annealing (heat treatment) temperature (AT) on the down-conversion luminescence features of erbium (Er{sup 3+}) doped zinc-boro-tellurite (ZBT) glasses containing silver NPs. The AT dependent (between 390 and 450 °C) variations in refractive index and density are ascribed to the generation of non-bridging oxygen (NBO) ions. X-ray diffraction pattern confirmed the amorphous nature of the melt-quenched synthesized glass samples. TEM micrograph revealed the nucleation of Ag NPs inside the glass matrix having average diameter between 8.4 (un-annealed sample) to 11.8 nm (annealed). The UV–Vis spectra exhibited seven absorption bands corresponding to {sup 4}f–{sup 4}f transitions of Er{sup 3+} ions. Annealed samples displayed a red shift of SPR bands positioned at 550 and 580 nm. Judd–Ofelt theory is used to evaluate the intensity parameters for radiative transitions within 4f{sup n} configuration of Er{sup 3+} ion. Annealing up to 410 °C is found to stimulate the plasmonic effect through the enlargement of NPs. Consequently, the PL intensity is enhanced by a factor of 3.23 ({sup 2}H{sub 11/2} → {sup 4}I{sub 15/2}), 4.10 ({sup 4}S{sub 3/2} → {sup 4}I{sub 15/2}), and 3.79 ({sup 4}F{sub 9/2} → {sup 4}I{sub 15/2}). This achieved excellent down-conversion luminescence efficiency of proposed glasses shows their potential implementation in photonic devices and solid state lasers. - Highlights: • The changes in the physical properties are ascribed to the generation of NBO. • TEM images confirmed the presence of Ag NPs in the glass matrix. • The achieved

  2. Evolution of ferroelectric SrBi2Nb2O9 phase embedded in tellurite glass

    Science.gov (United States)

    Mohamed, E. A.

    2017-12-01

    Glasses with the composition, [(100-x)TeO2- x(SrO-Bi2O3-Nb2O5)] with x = 20, 30 and 40 (in mol %) were prepared. The X-ray diffraction (XRD) pattern and differential thermal analysis (DTA) for the as-prepared samples confirmed the amorphous and glassy characteristics, respectively. The SrBi2Nb2O9 phase in tellurite glass for HT773 sample at x = 40 mol % is formed and confirmed by the Rietveld refinement. DTA curves for all glass samples exhibit two endothermic dips while the two broad exothermic peaks at lower x reduced to one at higher x. Infrared (IR) results revealed that the glassy matrix are composed of TeO3, TeO3+1, TeO4, BiO6 and NbO6 structural units. The changes in the density (ρ), molar volume (Vm), oxygen molar volume (V0) and oxygen packing fraction (OPD) have correlated with structural changes in the glass network. The optical studies show an absorption bands below the absorption edge in the glass samples.

  3. Spectral properties of Er3+/Yb3+ codoped tungsten-tellurite glasses.

    Science.gov (United States)

    Shen, Xiang; Nie, QiuHua; Xu, TieFeng; Gao, Yuan

    2005-07-01

    The spectral properties of Er3+/Yb3+ codoped tungsten-tellurite (WT) glasses have been investigated. The measured absorption spectra are analyzed by Judd-Ofelt theory. The compositional change of intensity parameter omega2 is attributed to the change in the covalency between the Er3+ and oxygen ions, the asymmetry in the local structures around the Er3+ ions can be neglected. The lifetimes of 4I(13/2) level of Er3+ in WT glasses are measured and comparable with other TeO2-based glasses. The stimulated emission cross-section is calculated based on McCumber theory. The fluorescence full width at half maximum (FWHM) and the emission cross-section (sigma(peak)) of the 4I(13/2) --> 4I(15/2) transition of Er3+ in different glass hosts have been compared. The suitability of such WT glasses as host materials for 1.5 microm broadband amplification is discussed.

  4. Spectroscopic studies of Dy3 + ion doped tellurite glasses for solid state lasers and white LEDs

    Science.gov (United States)

    Himamaheswara Rao, V.; Syam Prasad, P.; Mohan Babu, M.; Venkateswara Rao, P.; Satyanarayana, T.; Luís F., Santos; Veeraiah, N.

    2018-01-01

    Rare earth ion Dy3 +-doped tellurite glasses were synthesised in the system of (75-x)TeO2-15Sb2O3-10WO3-xDy2O3 (TSWD glasses). XRD and FTIR characterizations were used to find the crystalline and structural properties. The intensities of the electronic transitions and the ligand environment around the Dy3 + ion were determined using the Judd-Ofelt (J-O) theory on the absorption spectra of the glasses. The measured luminescence spectra exhibit intense emissions at 574 and 484 nm along with less intense emissions around 662 and 751 nm. Various radiative properties of the 4F9/2 excited level of Dy3 + ion were calculated for the glasses. Decay profiles were measured to find the life times and quantum efficiencies. Yellow to blue intensity ratio (Y/B), CIE chromaticity coordinates and correlated color temperature (CCT) values are calculated using the emission spectra to evaluate the emitted light. The obtained results suggest the utility of the glasses for potential yellow laser and white LED's applications.

  5. Investigations on luminescence behavior of Er3+/Yb3+ co-doped boro-tellurite glasses

    Science.gov (United States)

    Maheshvaran, K.; Arunkumar, S.; Venkata Krishnaiah, K.; Marimuthu, K.

    2015-01-01

    Er3+/Yb3+ co-doped boro-tellurite glasses with the chemical composition 30TeO2+(24 - x)B2O3 + 15SrO + 10BaO + 10Li2O + 10LiF + 1Er2O3 + xYb2O3 (where x = 0, 0.1, 0.5, 1 and 2 in wt%) have been prepared and their luminescence behavior were studied and reported. Absorption spectral measurements have been used to derive the Judd-Ofelt (JO) intensity parameters from the experimental and calculated oscillator strength values following the JO theory. The various lasing parameters such as stimulated emission cross-section (σEp), experimental and calculated branching ratios (βR) and radiative lifetime (τcal) for the 2H9/2 → 4I15/2, 4S3/2 → 4I15/2 and 4I13/2 → 4I15/2 emission transitions were determined using the JO intensity parameters. The absorption and emission cross-section values for the 4I13/2 → 4I15/2 emission band have been calculated using McCumbar theory and the Gain cross-section for the 4I13/2 → 4I15/2 emission transition also obtained. The upconversion emission mechanism have been studied through various energy transfer processes and the intensity of the upconversion emission transitions are found to increase with the increase in Yb3+ ion concentration. The luminescence decay curves corresponding to the 4I13/2 → 4I15/2 transition of the Er3+/Yb3+ co-doped boro-tellurite glasses under 980 nm excitation wavelength have also been studied and reported in the present work.

  6. Nd3+-doped lanthanum lead boro-tellurite glass for lasing and amplification applications

    Science.gov (United States)

    Madhu, A.; Eraiah, B.; Manasa, P.; Srinatha, N.

    2018-01-01

    Nd3+-doped lanthanum lead boro-tellurite glass samples were prepared by conventional melt quenching method and their structural, thermal, fluorescence, and decay times of the glasses were investigated. Prepared glass samples exhibits amorphous nature and shows good thermal stability in the temperature range of 100-800 °C. Judd-Ofelt (JO) analysis was carried out and the intensity parameters (Ωλ = 2, 4, 6) also spontaneous radiative probability and stimulated-.emission cross-sections were estimated. The magnitude of Ωλ confirms the covalency nature. The near infrared emission spectra were measured by 808 nm excitation in which the emission intensity is found to be high at 1060 nm for the 4F3/2 → 4F11/2 transition. The stimulated cross section, effective band width and branching ratios are found to be 8.910 × 10-20 cm2, 21.57 nm and 53.72 % respectively, for 4F3/2 → 4F11/2 transition. The derived gain bandwidth, figure of merit, threshold and saturation intensity found to be comparable to some of the glass systems. Furthermore, the time decay rate found to decrease from 100 μs to 27 μs when the concentration increased from 0.1 to 3.0 mol% of Nd3+ ions and also all follow the single exponential behaviour which is attributed to the self quenching effect due to the cross-relaxation channels.

  7. Thermal, structural and spectroscopic investigations on Eu{sup 3+} doped boro-tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Selvaraju, K. [Department of Physics, Gandhigram Rural University, Gandhigram 624 302 (India); Marimuthu, K., E-mail: mari_ram2000@yahoo.com [Department of Physics, Gandhigram Rural University, Gandhigram 624 302 (India); Seshagiri, T.K.; Godbole, S.V. [Radiochemistry Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400 085 (India)

    2011-12-15

    Highlights: Black-Right-Pointing-Pointer Fundamental O-H, (BO{sub 3}){sup -} vibrations and B-O-B linkages in borate network explored. Black-Right-Pointing-Pointer The covalent nature of the Eu{sup 3+} ions with surrounding ligands have been confirmed. Black-Right-Pointing-Pointer B3TMK glass is found to be the best optical candidate for laser working at 612 nm. - Abstract: Eu{sup 3+} doped boro-tellurite glasses with the chemical composition (69 - x)B{sub 2}O{sub 3}-xTeO{sub 2}-15Mg{sub 2}O-15K{sub 2}O-1Eu{sub 2}O{sub 3} (where x = 0, 10, 20, 30 and 40 wt%) have been synthesized and its thermal, structural and spectroscopic behavior were studied and reported. The thermal behavior of the Eu{sup 3+} doped boro-tellurite glasses were explored through DTA thermograms. The presence of varying tellurium dioxide results in structural and spectroscopic changes around Eu{sup 3+} ions and are explored through XRD, FTIR, UV-vis, Luminescence and lifetime measurements. The XRD pattern confirms the amorphous nature and the FTIR spectra reveal the formation of the local structural units BO{sub 3} and BO{sub 4} in the prepared glasses. The bonding parameters (-bar {beta} and {delta}) have been calculated based on the observed band positions of the absorption spectra. The Judd-Ofelt (JO) parameters were determined from the absorption and luminescence spectra and the results are presented. The variation in the JO intensity parameters {Omega}{sub {lambda}} ({lambda} = 2, 4 and 6) and the hypersensitive band positions with the change in chemical composition have been discussed in detail. The JO parameters have been used to derive important radiative properties like transition probabilities (A), branching ratios ({beta}{sub R}) and peak stimulated emission cross section ({sigma}E/P) for the {sup 5}D{sub 0} {yields} {sup 7}F{sub J} (J = 1, 2, 3 and 4) transitions of the Eu{sup 3+} ions. The varying optical properties of the prepared glasses with the change in tellurium dioxide have

  8. Energy transfer and infrared-to-visible upconversion luminescence of Er3+/Yb3+-codoped halide modified tellurite glasses

    International Nuclear Information System (INIS)

    Zhang, Q.Y.; Feng, Z.M.; Yang, Z.M.; Jiang, Z.H.

    2006-01-01

    We report on the energy transfer and frequency upconversion spectroscopic properties of Er 3+ -doped and Er 3+ /Yb 3+ -codoped TeO 2 -ZnO-Na 2 O-PbCl 2 halide modified tellurite glasses upon excitation with 808 and 978 nm laser diode. Three intense emissions centered at around 529, 546 and 657 nm, alongwith a very weak blue emission at 410 nm have clearly been observed for the Er 3+ /Yb 3+ -codoped halide modified tellurite glasses upon excitation at 978 nm and the involved mechanisms are explained. The quadratic dependence of fluorescence on excitation laser power confirms the fact that the two-photon contribute to the infrared to green-red upconversion emissions. And the blue upconversion at 410 nm involved a sequential three-photon absorption process

  9. Investigations on structural and optical behavior of Er3+ doped lead boro-tellurite glasses

    Science.gov (United States)

    Karthikeyan, P.; Suthanthirakumar, P.; Vijayakumar, R.; Marimuthu, K.

    2015-06-01

    Er3+ doped lead boro-tellurite glasses with the chemical composition (30-x)B2O3+30TeO2+23MgO+17PbF2+xEr2O3 (where x=0.05, 0.25, 0.5, and 1 in wt%) were synthesized by melt quenching technique. The structural and optical behaviors have been investigated through FTIR, absorption and emission spectral analysis. The UV-vis- NIR absorption spectra were used to calculate the bonding parameters (β ¯, δ), Judd-Ofelt intensity parameters (Ωλ, λ = 2, 4 and 6), Optical band gap and Urbach's energy of the prepared glasses. The radiative properties such as transition probability (AR), stimulated emission cross-section (σPE ), branching ratios (βR) were calculated from the luminescence spectra. The optical properties of the prepared glasses with varying Er3+ ion concentration have been studied and reported in the present work.

  10. Optical properties of Dy3+ doped bismuth boro-tellurite glasses for WLED applications

    Science.gov (United States)

    Karthikeyan, P.; Marimuthu, K.

    2016-05-01

    The Dy3+ doped bismuth boro-tellurite glasses with the chemical composition (79.5-x) B2O3+xTeO2+10Bi2O3+10PbF2+0.5Dy2O3 (where x = 10, 20, 30 and 40 in wt%) have been prepared by melt quenching technique. The optical properties of the prepared glasses have been studied through absorption and emission spectral measurements. The bonding parameters, optical band gap energy, Urbach's energy and Judd-Ofelt (JO) intensity parameters (Ωλ, λ = 2, 4 and 6) were calculated from the absorption spectra. The radiative properties like transition probability (A), stimulated emission cross-section (σPE) and branching ratios (βR) were calculated from the emission spectra using JO theory. The strong emissions in the visible region, large stimulated emission cross-section and higher branching ratio values observed for the title glasses are found to be suitable for lasers and WLED applications.

  11. Lanthanum lead boro-tellurite glasses doped with samarium trioxide for luminescent devices application

    Science.gov (United States)

    Madhu, A.; Eraiah, B.

    2018-04-01

    Boro-tellurite based glasses (10La2O3-(20-x) TeO2-30PbO-40B2O3-xSm2O3) (x = 0, 0.5, 1.0 and 2.0 mol %) doped with different concentrations of Sm3+ ions has been investigated. The optical properties have been studied through spectroscopic measurements such as absorption and luminescence. Absorption spectra reveals nine peaks due to 6H5/2→6P3/2, 4I3/2+4F5/2+4I11/2, 6F11/2, 6F9/2, 6F7/2, 6F5/2, 6F3/2, 6H15/2, and 6H13/2 transitions. Luminescence spectra under the excitation of 403 nm display four emission bands due to 4G5/2→6H5/2, 6H7/2, 6H9/2 and 6H11/2 transitions of Sm3+ ions. Among them 6H7/2 bright orange -red is more intense which proves that the present glasses are potential candidates for luminescent device applications in visible range as well as optical fibre communication since its refractive index is 1.65 high compared to other glasses.

  12. Annealing time dependent up-conversion luminescence enhancement in magnesium–tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Amjad, Raja J., E-mail: rajajunaid25@gmail.com [Advanced Optical Material Research Group, Faculty of Science, Universiti Teknologi Malaysia, Skudai, Johor bahru 81310 (Malaysia); Centre for Solid State Physics, University of the Punjab, QAC, Lahore 54590 (Pakistan); Sahar, M.R.; Ghoshal, S.K.; Dousti, M.R. [Advanced Optical Material Research Group, Faculty of Science, Universiti Teknologi Malaysia, Skudai, Johor bahru 81310 (Malaysia); Riaz, S. [Centre for Solid State Physics, University of the Punjab, QAC, Lahore 54590 (Pakistan); Samavati, A.R.; Arifin, R. [Advanced Optical Material Research Group, Faculty of Science, Universiti Teknologi Malaysia, Skudai, Johor bahru 81310 (Malaysia); Naseem, S. [Centre for Solid State Physics, University of the Punjab, QAC, Lahore 54590 (Pakistan)

    2013-04-15

    Silver nanoparticles (NPs) embedded Er{sup 3+} ions doped magnesium–tellurite glasses are prepared using melt quenching technique. Heat treatment with different time intervals above the glass transition temperature is applied in order to reduce the silver ions (Ag{sup +}) to silver NPs (Ag{sup o}). The transmission electron microscopy (TEM), differential thermal analyses (DTA), UV–vis-NIR absorption spectroscopy and photoluminescence (PL) spectroscopy are used to examine annealing time dependent structural and optical properties. The characteristics temperatures such as glass transition temperature (T{sub g}), crystallization temperature (T{sub c}) and melting temperature (T{sub m}) obtained from DTA for an as prepared sample are 322 °C, 450 °C and 580 °C, respectively. TEM image clearly shows the homogeneous distribution of silver NPs with an average diameter ∼12 nm. The observed localized surface plasmon resonance (LSPR) band is evidenced at 534 nm. Furthermore, the infrared to visible frequency up-conversion (UC) emission under 786 nm excitation exhibits three emission bands centered at 532 nm, 554 nm and 634 nm corresponding to {sup 2}H{sub 11/2}→{sup 4}I{sub 15/2}, {sup 4}S{sub 3/2}→{sup 4}I{sub 15/2} and {sup 4}F{sub 9/2}→{sup 4}I{sub 15/2} transitions of Er{sup 3+}, respectively. Intensity of all the bands is found to enhance by increasing the annealing time up to 24 h. However, further increase in the annealing time duration (∼40 h) reduces the intensity. Enhancement in the luminescence intensity is understood in terms of the local field effect of the silver NPs whereas the quenching is attributed to the energy transfer from Er{sup 3+} ions to silver NPs. -- Highlights: ► Er{sup 3+}-doped silver NPs embedded magnesium–tellurite glasses are prepared. ► TEM confirms the successful precipitation of spherical NPs by heat treatment (HT). ► Luminescence is enhanced due to the growth of NPs after HT up to 24 h. ► With HT>24 h (40 h

  13. Evaluation of shielding parameters for heavy metal fluoride based tellurite-rich glasses for gamma ray shielding applications

    Science.gov (United States)

    Sayyed, M. I.; Lakshminarayana, G.; Kityk, I. V.; Mahdi, M. A.

    2017-10-01

    In this work, we have evaluated the γ-ray shielding parameters such as mass attenuation coefficient (μ/ρ), effective atomic number (Zeff), half value layer (HVL), mean free path (MFP) and exposure buildup factors (EBF) for heavy metal fluoride (PbF2) based tellurite-rich glasses. In addition, neutron total macroscopic cross sections (∑R) for these glasses were also calculated. The maximum value for μ/ρ, Zeff and ∑R was found for heavy metal (Bi2O3) oxide introduced glass. The results of the selected glasses have been compared, in terms of MFP with different glass systems. The shielding effectiveness of the selected glasses is found comparable or better than of common ones, which indicates that these glasses with suitable oxides could be developed for gamma ray shielding applications.

  14. Structural and optical studies on Eu3+ doped boro-tellurite glasses

    Science.gov (United States)

    Maheshvaran, K.; Veeran, P. K.; Marimuthu, K.

    2013-03-01

    Eu3+ doped boro-tellurite glasses (69 - x)B2O3 + xTeO2 + 15Na2CO3 + 15NaF + 1Eu2O3 (where x = 0, 10, 20, 30 and 40 wt%) have been prepared and their structural and optical properties were studied through XRD, FTIR, absorption, luminescence and decay time measurements. The FTIR spectra reveal the presence of B-O-B bond bending vibrations and Te-O-Te or O-Te-O linkage bending vibrations in the prepared glasses. The absorption spectral measurements were used to calculate the bonding parameters (β¯, δ). The direct, indirect allowed band gap (Eopt), band tail parameter (B) and Urbach energy (ΔE) values of the prepared glasses have also been determined from the absorption spectral measurements. The phonon sideband is observed from the excitation spectra on the higher energy side of the 7F0 → 5D2 transition. The phonon energy (hω) and the electron-phonon coupling constant (g) were also derived from the phonon sideband spectra. Through the luminescence spectra, Judd-Ofelt (JO) intensity parameters (Ωλ, λ = 2, 4 and 6) and the luminescence intensity ratio (R) have been determined. The JO parameters have also been used to calculate the radiative properties like transition probability (A), stimulated emission cross-section (σPE), radiative lifetime (τrad), and branching ratios (βR) for the 5D0 → 7FJ (J = 0, 1, 2, 3 and 4) emission transitions of the Eu3+ ions. The experimental lifetime of the 5D0 level is found to be single exponential for all the prepared glasses. The obtained results were discussed and reported in the present work.

  15. Structural, thermal and optical absorption features of heavy metal oxides doped tellurite rich glasses

    Science.gov (United States)

    Kaky, Kawa M.; Lakshminarayana, G.; Baki, S. O.; Kityk, I. V.; Taufiq-Yap, Y. H.; Mahdi, M. A.

    In order to improve tellurite glass stability to be applicable for optical fiber amplifier applications, glasses with the composition of (70 - x)TeO2. (10)ZnO. (10)WO3. (5)Na2O. (5)TiO2. (x)Bi2O3 (x = 1, 2, 3, 4, and 5 mol%) have been produced and characterized using the related methods. Structural properties were investigated using X-ray diffraction (XRD) which confirms the non-crystalline structure and scanning electron microscopy (SEM) micrographs also confirm the XRD results. The energy dispersive X-ray (EDX) analysis profiles show that all the mentioned elements are present in the prepared glasses. Following the IR spectra, all the tellurium bonds such as stretching vibrations of TeO4 tbp and TeO3/TeO3+1 unit are revealed. Raman spectra confirm the presence of different functional groups, actually, it shows bands mainly in four spectral regions: R1 (65-150) cm-1, R2 (280-550) cm-1, R3 (880-950) cm-1 and R4 (916-926) cm-1 and the identified bands are assigned to respective molecular groups. The thermal study was carried out using Differential scanning calorimetry (DSC) which indicates good thermal stability of the synthesized glasses with increasing Bi concentration. From the optical absorption spectra, we evaluated cut-off edge wavelengths and found increasing cutoff wavelength with an increase in Bi2O3 concentration. In the UV-Visible region, optical band gap energy and allowed transitions were investigated using three methods; direct, indirect, and absorption spectrum fitting (ASF), and band gaps from indirect and ASF were matched.

  16. Raman scattering boson peak and differential scanning calorimetry studies of the glass transition in tellurium-zinc oxide glasses.

    Science.gov (United States)

    Stavrou, E; Tsiantos, C; Tsopouridou, R D; Kripotou, S; Kontos, A G; Raptis, C; Capoen, B; Bouazaoui, M; Turrell, S; Khatir, S

    2010-05-19

    Raman scattering and differential scanning calorimetry (DSC) measurements have been carried out on four mixed tellurium-zinc oxide (TeO(2))(1 - x)(ZnO)(x) (x = 0.1, 0.2, 0.3, 0.4) glasses under variable temperature, with particular attention being given to the respective glass transition region. From the DSC measurements, the glass transition temperature T(g) has been determined for each glass, showing a monotonous decrease of T(g) with increasing ZnO content. The Raman study is focused on the low-frequency band of the glasses, the so-called boson peak (BP), whose frequency undergoes an abrupt decrease at a temperature T(d) very close to the respective T(g) values obtained by DSC. These results show that the BP is highly sensitive to dynamical effects over the glass transition and provides a means for an equally reliable (to DSC) determination of T(g) in tellurite glasses and other network glasses. The discontinuous temperature dependence of the BP frequency at the glass transition, along with the absence of such a behaviour by the high-frequency Raman bands (due to local atomic vibrations), indicates that marked changes of the medium range order (MRO) occur at T(g) and confirms the correlation between the BP and the MRO of glasses.

  17. Raman scattering boson peak and differential scanning calorimetry studies of the glass transition in tellurium-zinc oxide glasses

    International Nuclear Information System (INIS)

    Stavrou, E; Tsiantos, C; Tsopouridou, R D; Kripotou, S; Kontos, A G; Raptis, C; Capoen, B; Bouazaoui, M; Turrell, S; Khatir, S

    2010-01-01

    Raman scattering and differential scanning calorimetry (DSC) measurements have been carried out on four mixed tellurium-zinc oxide (TeO 2 ) 1-x (ZnO) x (x = 0.1, 0.2, 0.3, 0.4) glasses under variable temperature, with particular attention being given to the respective glass transition region. From the DSC measurements, the glass transition temperature T g has been determined for each glass, showing a monotonous decrease of T g with increasing ZnO content. The Raman study is focused on the low-frequency band of the glasses, the so-called boson peak (BP), whose frequency undergoes an abrupt decrease at a temperature T d very close to the respective T g values obtained by DSC. These results show that the BP is highly sensitive to dynamical effects over the glass transition and provides a means for an equally reliable (to DSC) determination of T g in tellurite glasses and other network glasses. The discontinuous temperature dependence of the BP frequency at the glass transition, along with the absence of such a behaviour by the high-frequency Raman bands (due to local atomic vibrations), indicates that marked changes of the medium range order (MRO) occur at T g and confirms the correlation between the BP and the MRO of glasses.

  18. Tailored white light emission in Eu3+/Dy3+ doped tellurite glass phosphors containing Al3+ ions

    Science.gov (United States)

    Walas, Michalina; Piotrowski, Patryk; Lewandowski, Tomasz; Synak, Anna; Łapiński, Marcin; Sadowski, Wojciech; Kościelska, Barbara

    2018-05-01

    Tellurite glass systems modified by addition of aluminum fluoride AlF3 have been successfully synthesized as host matrices for optically active rare earth ions RE3+ (RE3+ = Eu3+, Dy3+). Samples with different Eu3+ to Dy3+ molar ratio have been studied in order to determine possibility of white light emission via UV excitation. Structural investigations confirmed amorphous character of materials whereas spectroscopic studies brought more insight into glass network's nature. FTIR results shown presence of two features related to tellurite glass matrix (in 490-935 cm-1 spectral region) and another one (940-1250 cm-1) due to aluminum addition. Especially, Al-O and Te-O-Al bonds of AlO4 tetrahedrons have been found. AlO4 units are considered as glass formers that improve network's strength and thermal resistivity against devitrification. Based on XPS studies of Al3+ photoelectron band the existence of Al-O and also Al-F bonds have been examined. Moreover, signals originating from Eu3+ and Dy3+ have been found confirming their valence state. Luminescence results revealed possibility of simultaneous UV excitation of Eu3+ and Dy3+ ions. Excitation with λexc = 390 and 393 nm resulted in white light generation starting from warm white to neutral and cool white depending on Eu3+ concentration and used excitation wavelength. Additionally, increase of decay lifetime of Eu3+ induced by Al3+ presence have been revealed based on luminescence decay analysis. Thus, tellurite glass systems modified by AlF3 and doped with Eu3+/Dy3+ may be considered as promising candidates for white light emitting sources.

  19. Effect of concentration on the photoluminescence properties of Sm3+ and Dy3+: cadmium lithium boro tellurite glasses.

    Science.gov (United States)

    Raju, K Vemasevana; Sailaja, S; Reddy, M Bhushana; Giridhar, P; Raju, C Nageswara; Reddy, B Sudhakar

    2012-02-01

    Rare-earth (Sm3+ or Dy3+) ions doped cadmium lithium boro tellurite glasses have been prepared by melt quenching method for their spectral studies. From X-ray diffraction (XRD) patterns the glass amorphous nature has been confirmed. Vis-NIR absorption, excitation and emission spectra of these glasses have been analyzed systematically and also rare earth ion concentration is optimised Sm3+: CLiBT glasses have shown strong orange-reddish emission at 598 nm (4G5/2-->6H7/2) with an excitation wavelength lambda(exci) = 401 nm and Dy3+: CLiBT glasses have shown strong yellow emission at 574 nm (6F9/2-->6H13/2) with lambda(exci) = 451 nm.

  20. Structural and optical investigations on Dy{sup 3+} doped boro-tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Maheshvaran, K. [Department of Physics, Gandhigram Rural University, Gandhigram 624 302 (India); Marimuthu, K., E-mail: mari_ram2000@yahoo.com [Department of Physics, Gandhigram Rural University, Gandhigram 624 302 (India)

    2011-07-07

    Highlights: > The structural and optical properties have been studied through XRD, FTIR, absorption, luminescence and decay time measurements. > The prepared glasses posses ionic nature and the ionic nature gradually increases when the tellurium di-oxide content increases in the host matrix. > The radiative properties such as radiative transition probability (A), radiative lifetime ({tau}{sub rad}), stimulated emission cross section ({sigma}{sub P}{sup E}) and branching ratios ({beta}{sub R}) are calculated for the {sup 4}F{sub 9/2} {yields} {sup 6}H{sub 15/2}, {sup 6}H{sub 13/2} and {sup 6}H{sub 11/2} transitions. > The decay curve of the {sup 4}F{sub 9/2} level of Dy{sup 3+}:BXTD glasses is well fitted for single exponential. > The stimulated emission cross section for the Dy{sup 3+}:B3TD glass possess higher value and therefore it is suggested for suitable laser applications. - Abstract: Dy{sup 3+} doped boro-tellurite glasses were prepared by following melt quenching technique with the chemical composition (69 - x)H{sub 3}BO{sub 3} + xTeO{sub 2} + 15Mg{sub 2}CO{sub 3} + 15K{sub 2}CO{sub 3} + 1Dy{sub 2}O{sub 3} (where x = 0, 10, 20, 30 and 40 wt%) by varying the tellurium dioxide content. The structural and optical properties have been studied through XRD, FTIR, absorption, luminescence and decay time measurements. The XRD pattern has been used to confirm the amorphous nature of the prepared glasses. The FTIR spectra reveals the presence of B-O vibrations and Te-O stretching modes of TeO{sub 3} and TeO{sub 6} units in the prepared glasses. The UV-vis-NIR absorption spectra were used to calculate the oscillator strength, bonding parameters ({beta}-bar and {delta}) and Judd-Ofelt intensity parameters ({Omega}{sub {lambda},} {lambda} = 2, 4 and 6). The radiative transition probability (A), stimulated emission cross section ({sigma}{sub P}{sup E}) and the experimental, calculated branching ratios ({beta}{sub R}) have been calculated from the luminescence spectra

  1. Optical properties of gold nanoparticle embedded Er{sup 3+} doped lead–tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Sazali, E.S.; Sahar, M.R., E-mail: mrahim057@gmail.com; Ghoshal, S.K.; Arifin, R.; Rohani, M.S.; Awang, A.

    2014-09-01

    Highlights: • Er{sup 3+} doped lead–tellurite glass with and without GNPs has been synthesized. • The existence of Au NPs with average diameter of 6.09 nm dispersed in glass matrix. • Plasmonic effect from Au NPs exert prominent enhancement in UC. - Abstract: Enhanced optical properties of rare earth doped glasses for sundry applications are current challenges in materials science and technology. Series of gold nanoparticles (GNPs) embedded Er{sup 3+} doped TeO{sub 2}–PbO–PbO{sub 2} glasses are synthesized and the influences of GNPs on the optical behaviors are examined. XRD spectra confirm the amorphous nature of all the glass samples. TEM images display the existence of a broad distribution of spherical crystalline GNPs with average diameter ∼6.09 nm. UV–Vis–NIR spectra reveal seven absorption bands centered at 490, 526, 551, 652, 800, 982 and 1520 nm due to the absorptions from the ground state to different excited states. Two surface plasmon resonance bands of gold (Au{sup 0}) are evidenced at 556 and 585 nm. The sizable decrease in the optical band gap (2.82–1.09 eV) with the increase of GNPs concentration from 0.025 to 0.1 mol% is attributed to the generation of higher NPs nucleation sites. The intensity parameters related to the radiative transitions within 4f{sup n} configuration of Er{sup 3+} ion are determined and analyzed using Judd–Ofelt (J–O) theory. The room temperature up-conversion emission spectra under 779 nm excitations shows three peaks centered at 520, 550 and 660 nm corresponding to the transitions from {sup 2}H{sub 11/2}, {sup 4}S{sub 3/2} and {sup 4}F{sub 9/2} excited states to {sup 4}I{sub 15/2} ground state. Significant enhancement in the luminescence intensity is primarily ascribed to surface plasmon resonance mediated strong local field effect of GNPs in the proximity Er{sup 3+} ion and radiative energy transfer. The maximum enhancement are evident for green and red bands at 0.05 mol% of Au. The stimulated

  2. Infrequent blue and green emission transitions from Eu3+ in heavy metal tellurite glasses with low phonon energy

    International Nuclear Information System (INIS)

    Lin, H.; Tanabe, S.; Lin, L.; Yang, D.L.; Liu, K.; Wong, W.H.; Yu, J.Y.; Pun, E.Y.B.

    2006-01-01

    Eu 3+ doped alkali-barium-bismuth-tellurite (Eu 3+ :LKBBT) glasses were prepared by conventional melt quenching. Twelve emission bands including infrequent blue and green bands are observed and they almost cover whole visible spectral region under violet light radiation. The blue and green emissions of Eu 3+ rarely appeared in oxide glasses before, but they have been clearly recorded in Eu 3+ :LKBBT glasses even in the case of high concentration doping of Eu 3+ . The analysis based on spontaneous-radiative rate, energy gap and Raman scattering reveals that the obtaining of the abundant multichannel emissions of Eu 3+ is due to the higher refractive index and the lower phonon energy in LKBBT glass system

  3. Watt-level ~2 μm laser output in Tm3+-doped tungsten tellurite glass double-cladding fiber.

    Science.gov (United States)

    Li, Kefeng; Zhang, Guang; Hu, Lili

    2010-12-15

    We report, for the first time to the best of our knowledge, a watt level cw fiber laser at ~2 μm from a piece of 40-cm-long newly developed highly thulium-doped (3.76 × 10(20) ions/cm(3)) tungsten tellurite glass double cladding fiber pumped by a commercial 800 nm laser diode. The maximum output power of the fiber laser reaches 1.12 W. The slope efficiency and the optical-optical efficiency with respect to the absorbed pump are 20% and 16%, respectively. The lasing threshold is 1.46 W, and the lasing wavelength is centered at 1937 nm.

  4. Eigenstates and radiative transition probabilities for Tm3+(4f12) in phosphate and tellurite glasses

    International Nuclear Information System (INIS)

    Spector, N.; Reisfeld, R.; Boehm, L.

    1977-01-01

    Electronic wavefunctions of Tm 3+ in intermediate coupling were obtained and used to calculate the Usup((lambda)) matrix elements between all possible states of the 4f 12 configuration. The Judd-Ofelt intensity parameters Ωsub(lambda) obtained for Tm 3+ in phosphate and tellurite glasses were used in conjunction with the Usup((lambda))'s to calculate the forced electric dipole line strengths. The total electric and magnetic radiative transition probabilities are calculated. The entire theoretical spectrum involving the ground and excited levels (from 129 nm to 16447 nm) is given. (Auth.)

  5. Photoluminescence study of Sm{sup 3+}–Yb{sup 3+}co-doped tellurite glass embedding silver nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Reza Dousti, M., E-mail: mrdousti@ifsc.usp.br [Laboratório de Espectroscopia de Materiais Funcionais (LEMAF), Instituto de Fisica de São Carlos, Universidade de São Paulo, Av. Trabalhador So-carlense 400, São Carlos, SP 13566-590 (Brazil); Department of Physics, Tehran-North Branch, Islamic Azad University Tehran (Iran, Islamic Republic of); Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Skudai 81310, Johor (Malaysia); Amjad, R.J. [Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Skudai 81310, Johor (Malaysia); Department of Physics, COMSATS Institute of Information Technology, Lahore 54000 (Pakistan); Hosseinian S, R.; Salehi, M.; Sahar, M.R. [Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Skudai 81310, Johor (Malaysia)

    2015-03-15

    We report on the upconversion emission of Sm{sup 3+} ions doped tellurite glass in the presence of Yb{sup 3+} ions and silver nanoparticles. The enhancement of infrared-to-visible upconversion emissions is achieved under 980 nm excitation wavelength and attributed to the high absorption cross section of Yb{sup 3+} ions and an efficient energy transfer to Sm{sup 3+} ions. Further enhancements are attributed to the plasmonic effect via metallic nanoparticles resulting in the large localized field around rare earth ions. However, under excitation at 406 nm, the addition of Yb{sup 3+} content and heat-treated silver nanoparticles quench the luminescence of Sm{sup 3+} ions likely due to quantum cutting and plasmonic diluent effects, respectively. - Highlights: • Sm{sup 3+} tellurite glasses co-doped with Yb{sup 3+} ions and tri-doped with Yb{sup 3+}:Ag NPs were prepared. • In first step, Yb{sup 3+} ions enhanced the upconversion emissions of Sm{sup 3+} doped samples. • In second step, Ag NPs further enhanced the upconversion emissions in tri-doped glasses. • Finally, the quench in luminescence under 406 nm excitation is observed and discussed.

  6. Spectroscopic Studies of the Behavior of Eu3+ on the Luminescence of Cadmium Tellurite Glasses

    Directory of Open Access Journals (Sweden)

    I. V. García-Amaya

    2015-01-01

    Full Text Available The effect of europium doping on the photoluminescence of ZnO-CdO-TeO2 glasses is analyzed. TeO2-based glasses are of high interest as hosts for laser glasses. The Eu-doped oxide glasses were prepared by the conventional melt-quenching method. Five different concentrations of europium nitrate hexahydrate that varied from 0.3 to 1.5 mol% were used. SEM observations revealed the formation of zinc aluminate spinel and disperse droplets of liquid-liquid phase separation in the glasses. X-Ray diffraction reveals the amorphous structure of the fabricated glasses. FT-IR and Raman spectra show the presence of TeO4 and TeO3+1/TeO3 units that conform with the glass matrix. Raman spectra evidenced a band located at 1556 cm−1 that can be related to interstitial molecular oxygen in the glass matrix. Photoluminescence of the glasses showed light emission due to the following europiumtransitions from its D52, D51, and D50 levels to its F7J manifolds: D52→F70 (468 nm, D52→F72 (490 nm, D52→F73 (511 nm, D51→F71 (536 nm, D51→F72 (554 nm, D50→F70 (579.5 nm, D50→F71 (592 nm, D50→F72 (613 nm, D50→F73 (652 nm, and D50→F74 (490 nm. The estimated decay time, τ, was 0.4 ms for all the glasses.

  7. Silver nanoparticles enhanced 1.53 µm band fluorescence of Er{sup 3+}/Yb{sup 3+} codoped tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Qi, Yawei; Zhou, Yaxun, E-mail: zhouyaxun@nbu.edu.cn; Wu, Libo; Yang, Fengjing; Peng, Shengxi; Zheng, Shichao; Yin, Dandan

    2014-09-15

    The silver nanoparticles (NPs) was introduced into the Er{sup 3+}/Yb{sup 3+} codoped tellurite glasses with composition of TeO{sub 2}–ZnO to improve the 1.53 µm band fluorescence of Er{sup 3+} and the thermal stability of glass host. The UV–Vis–NIR absorption spectra, 1.53 µm band fluorescence spectra and fluorescence decaying curves, the differential scanning calorimeter (DSC) curves, X-ray diffraction (XRD) patterns and transmission electron microscopy (TEM) images of glass samples were characterized to investigate the effect of silver NPs on the fluorescence properties of Er{sup 3+}, thermal stability and structure behavior of glass host. It is shown that the Er{sup 3+}/Yb{sup 3+} codoped tellurite glass emits intense 1.53 µm band fluorescence with peak wavelength located at about 1532 nm under the 980 nm excitation. The introduction of silver NPs further improves the fluorescence intensity of Er{sup 3+} which is attributed to the enhanced local electric field effect induced by localized surface Plasmon resonance (LSPR) of silver NPs and the possible energy transfer from silver NPs to Er{sup 3+}. An improvement by about 62% of 1.5{sup 3} µm band fluorescence intensity was found in the studied Er{sup 3+}/Yb{sup 3+} codoped tellurite glass containing 0.5 mol% amount of AgNO{sub 3}. In addition, the thermal stability of glass host increases with the introduction of silver NPs while the glass structure maintains the amorphous nature. The present results indicate that the prepared Er{sup 3+}/Yb{sup 3+} codoped tellurite glass with an appropriate amount of silver NPs has good prospect as a gain medium applied for 1.53 µm band broad and high-gain erbium-doped fiber amplifiers (EDFAs). - Highlights: • Tellurite glass with Er{sup 3+}/Yb{sup 3+} and silver NPs was prepared by melt-quenching method. • Silver NPs with average size of 12 nm and Plasmon band at 560 nm was observed. • Addition of silver NPs increased the thermal stability of tellurite glass.

  8. Judd-Ofelt analysis and photoluminescence properties of RE3+ (RE = Er & Nd): Cadmium lithium boro tellurite glasses

    Science.gov (United States)

    Raju, K. Vemasevana; Raju, C. Nageswara; Sailaja, S.; Reddy, B. Sudhakar

    2013-01-01

    Rare earth (Er3+ and Nd3+) ions doped cadmium lithium boro tellurite (CLiBT) glasses were prepared by melt quenching method. The vis-NIR absorption spectra of these glasses have been analyzed systematically. Judd-Ofelt intensity parameters Ωλ (λ = 2, 4, 6) have been evaluated and used to compute the radiative properties of emission transitions of Er3+ and Nd3+: CLiBT glasses. From the NIR emission spectra of Er3+: CLiBT glasses a broad emission band centered at 1538 nm (4I13/2 → 4I15/2) is observed and from Nd3+: CLiBT glasses, three NIR emission bands at 898 nm (4F3/2 → 4I9/2), 1070 nm (4F3/2 → 4I11/2) and 1338 nm (4F3/2 → 4I13/2) are observed with an excitation wavelength λexci = 514.5 nm (Ar+ Laser). The FWHM and stimulated emission cross-section values are calculated for Er3+ and Nd3+: CLiBT glasses. FWHM × σeP values are also calculated for Er3+: CLiBT glasses.

  9. Variation of energy absorption and exposure buildup factors with incident photon energy and penetration depth for boro-tellurite (B2O3-TeO2) glasses

    Science.gov (United States)

    Sayyed, M. I.; Elhouichet, H.

    2017-01-01

    The gamma ray energy absorption (EABF) and exposure buildup factors (EBF) of (100-x)TeO2-xB2O3 glass systems (where x=5, 10, 15, 20, 22.5 and 25 mol%) have been calculated in the energy region 0.015-15 MeV up to a penetration depth of 40 mfp (mean free path). The five parameters (G-P) fitting method has been used to estimate both EABF and EBF values. Variations of EABF and EBF with incident photon energy and penetration depth have been studied. It was found that EABF and EBF values were higher in the intermediate energy region, for all the glass systems. Furthermore, boro-tellurite glass with 5 mol% B2O3, was found to present the lowest EABF and EBF values, hence it is superior gamma-ray shielding material. The results indicate that the boro-tellurite glasses can be used as radiation shielding materials.

  10. Natural Fe{sub 3}O{sub 4} nanoparticles embedded zinc–tellurite glasses: Polarizability and optical properties

    Energy Technology Data Exchange (ETDEWEB)

    Widanarto, W. [Physics Study Program, Jenderal Soedirman University, Jl. Dr. Soeparno 61, Purwokerto 53123 (Indonesia); Sahar, M.R., E-mail: rahimsahar@utm.my [Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Johor Bahru, Skudai 81310 (Malaysia); Ghoshal, S.K.; Arifin, R.; Rohani, M.S.; Hamzah, K. [Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Johor Bahru, Skudai 81310 (Malaysia); Jandra, M. [FTI, University Teknologi Malaysia, Johor Bahru, Skudai 81310 (Malaysia)

    2013-02-15

    Modifying the optical behavior of zinc–tellurite glass by embedding magnetic nanoparticles has implication in nanophotonics. A series of zinc–tellurite glasses containing natural Fe{sub 3}O{sub 4} nanoparticles with composition (80 − x)TeO{sub 2}·xFe{sub 3}O{sub 4}·20ZnO (0 ≤ x ≤ 2) in mol% are synthesized by melt quenching method and their optical properties are investigated using FTIR and UV–vis–NIR spectroscopies. Lorentz–Lorenz relations are exploited to determine the refractive index, molar refraction and electronic polarizability. The sharp absorption peaks of FTIR spectra show a shift from 667 cm{sup −1} to 671 cm{sup −1} in the presence of nanoparticles that increase the non-bridging oxygen, confirmed by the intensity change of the TeO{sub 3} peak at 752 cm{sup −1}. A new peak around 461 cm{sup −1} is also observed which is attributed to the band characteristic of covalent Fe–O linkages. A decrease in the Urbach energy as much as 0.122 eV and the optical energy band gap with the increase of Fe{sub 3}O{sub 4} concentration (0.5–1.0 mol%) is evidenced. Electronic polarizability of the glasses increases with increasing Fe{sub 3}O{sub 4} nanoparticles concentration up to 1 mol%. Interestingly, the polarizability tends to decrease with the further increase of Fe{sub 3}O{sub 4} concentration at 2 mol%. The role of magnetic nanoparticles in influencing the structural and optical behavior are examined and understood. - Highlights: ► Incorporation of natural Fe{sub 3}O{sub 4} nanoparticles into the zinc–tellurite glass. ► Influence of magnetic nanoparticles in modifying structure and optical properties. ► Enhancement of refraction index and change in electronic polarizability.

  11. Structural characterization of ZnCl{sub 2} modified tellurite based glasses

    Energy Technology Data Exchange (ETDEWEB)

    Dhankhar, Sunil, E-mail: dhankhar.sunil@gmail.com; Kundu, R. S.; Sunita [Guru Jambheshwar University of Science and Technology, Hisar (Haryana) – 125001 (India); Punia, R. [Indira Gandhi University, Meerpur, Rewari (Haryana) -123401 (India); Parmar, R. [Maharishi Dayanand University, Rohtak (Haryana)-124001 (India); Sanjay [Rawal Institute of Engineering and Technology, Faridabad (Haryana)-121004 (India); Kishore, N. [Central University of Haryana, Mahendergarh (Haryana)-123029 (India)

    2016-05-06

    Glass composition 70 TeO{sub 2}-(30-x) BaO – x ZnCl{sub 2}; x = 5, 10, 15, 20 and 25 have been prepared by rapid melt quenching technique under controlled atmospheric conditions. Amorphous nature of the samples was confirmed by x-ray diffractogram. The glass transition temperature (T{sub g}) has been determined using differential scanning calorimetry (DSC) and its value is observed to decrease with increase in ZnCl{sub 2} content. The peaks in the Raman and FTIR spectra have been estimated by deconvolutation of the spectra and each of deconvoluted spectra exhibits several peaks. IR and Raman spectra of the present glass system indicate that TeO{sub 2} exists as TeO{sub 3} trigonal pyramidal (tp), TeO{sub 4} trigonal bipyramidal (tbp) and TeO{sub 6} polyhedra structural units. With increase in zinc halide content, transformation of some of TeO{sub 4} structural units into TeO{sub 3} structural units is observed Increase in TeO{sub 3} structural units shows that non-bridging oxygen contribution increases which confirms the decrease in glass transition temperature.

  12. Structural characterization of ZnCl2 modified tellurite based glasses

    Science.gov (United States)

    Dhankhar, Sunil; Kundu, R. S.; Punia, R.; Sunita, Parmar, R.; Sanjay, Kishore, N.

    2016-05-01

    Glass composition 70 TeO2-(30-x) BaO - x ZnCl2; x = 5, 10, 15, 20 and 25 have been prepared by rapid melt quenching technique under controlled atmospheric conditions. Amorphous nature of the samples was confirmed by x-ray diffractogram. The glass transition temperature (Tg) has been determined using differential scanning calorimetry (DSC) and its value is observed to decrease with increase in ZnCl2 content. The peaks in the Raman and FTIR spectra have been estimated by deconvolutation of the spectra and each of deconvoluted spectra exhibits several peaks. IR and Raman spectra of the present glass system indicate that TeO2 exists as TeO3 trigonal pyramidal (tp), TeO4 trigonal bipyramidal (tbp) and TeO6 polyhedra structural units. With increase in zinc halide content, transformation of some of TeO4 structural units into TeO3 structural units is observed Increase in TeO3 structural units shows that non-bridging oxygen contribution increases which confirms the decrease in glass transition temperature.

  13. Structural characterization of tellurite glasses doped with transition metal oxides using Raman spectra and ab initio calculations.

    Science.gov (United States)

    Mohamed, Tarek A; Shaltout, I; Al Yahyaei, K M

    2006-05-01

    Systems of iron tellurite glasses were prepared by melt quenching with compositions of [85%TeO2+5%Fe2O3+10%TMO], where transition metal oxides (TMO) are TiO2, V2O5, MnO, CoO, NiO and CuO. Furthermore, the main structural units of these samples have been characterized by means of Raman spectra (150-1200 cm(-1)) as well as wavenumber predictions by means of Gaussian 98 ab initio calculations for the proposed site symmetries of TeO4(4-) triagonal bipyramid (C2v) and Te2O7(6-) bridged tetrahedra (Cs and C1). Aided by normal coordinate analysis, calculated vibrational frequencies, Raman scattering activities, force constants in internal coordinates and potential energy distributions (PEDs), revised vibrational assignments for the fundamental modes have been proposed. The main structural features are correlated to the dominant units of triagonal bipyramid (tbp) or bridged tetrahedral (TeO3+1 binds to TeO3 through TeOTe bridge; corner sharing). Moreover, the Raman spectra of the investigated tellurites reflect a structural change from tbp (coordination number is four) to triagonal pyramidal (coordination number is three).

  14. Optical analysis of RE(3+) (RE = Pr(3) (+) , Er(3) (+) and Nd(3) (+) ):cadmium lead boro tellurite glasses.

    Science.gov (United States)

    Giridhar, P; Bhushana Reddy, M; Neelima, G; Ramanaiah, R; Nagamuni Reddy, K; Sahadeva Reddy, V; Sudhakar Reddy, B

    2016-09-01

    This article reports on the optical characterization of Pr(3) (+) -, Er(3) (+) - and Nd(3) (+) -doped cadmium lead boro tellurite (CLBT) glasses prepared using the melt quenching method. The visible-near infrared (Vis-NIR) absorption spectra of these glasses were analyzed systematically. On measuring the NIR emission spectra of Er(3) (+) :CLBT glasses, a broad emission band centered at 1536 nm ((4) I13 /2  → (4) I15 /2 ) was observed, as were three NIR emission bands at 900 nm ((4) F3 /2  → (4) I9 /2 ), 1069 nm ((4) F3 /2  → (4) I11 /2 ) and 1338 nm ((4) F3 /2  → (4) I13 /2 ) from Nd(3) (+) :CLBT glasses and an NIR emission band at 1334 nm ((1) G4  → (3) H5 ) from Pr(3) (+) :CLBT glasses at an excitation wavelength (λex ) of 514.5 nm (Ar(+) laser). Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

  15. A 125Te and 23Na NMR investigation of the structure and crystallisation of sodium tellurite glasses.

    Science.gov (United States)

    Holland, D; Bailey, J; Ward, G; Turner, B; Tierney, P; Dupree, R

    2005-01-01

    125Te static nuclear magnetic resonance (NMR) and 23Na and 125Te magic angle spinning (MAS) NMR have been used, in conjunction with X-ray diffraction, to examine the structure and crystallisation behaviour of glasses of composition xNa2O.(1-x)TeO2 (0.075 x 0.4). The MAS NMR 23Na spectra from the glasses are broad and featureless but shift by approximately +5 ppm with increased x, i.e. as the system becomes more ionic. The static 125Te NMR spectra show an increase in axial symmetry with increasing x, indicating a shift from predominantly [TeO4] to [TeO3] structural units. The 23Na and 125Te spectra from the crystallised samples have been fitted to obtain information on the sites in the metastable crystal phases, which are the first to form on heating and which are therefore more closely related to the glass structure than thermodynamically stable crystal phases. New sodium tellurite phases are reported, including a sodium stabilised, face centred cubic phase related to delta-TeO2; a metastable form of Na2Te4O9 containing 3 sodium and 4 tellurium sites; and a metastable form of Na2Te2O5 containing 2 sodium sites. There is evidence of oxidation of TeIV to TeVI occurring in glasses with high values of x and, at x=0.40 and 0.50 (outside the glass forming range), some sodium metatellurate (Na2TeO4) is formed at the same time as sodium metatellurite (Na2TeO3). The 125Te shift is very sensitive to environment within the sodium tellurite system, covering more than 320 ppm, with anisotropies varying from 640 to 1540 ppm. The lack of features in the 125Te spectra of the glass phases, combined with the large shift range and high but variable anisotropy, means than it is not possible to obtain a unique fit to any presumed species present. Furthermore, the chemical shift anisotropy parameters for three of the four Te sites in the Na2Te4O9 phase are found to lie outside the range used for previous simulations of glass spectra.

  16. The effect of La2O3 in Tm3+-doped germanate-tellurite glasses for ~2 μm emission

    Science.gov (United States)

    Peng, Ya-Pei; Yuan, Xinqiang; Zhang, Junjie; Zhang, Long

    2014-01-01

    A germanate-tellurite glass (GeO2-TeO2-K2O-Nb2O5-La2O3) with thulium doping has been investigated for application as a laser material around 2.0 μm regions. Under the 808 nm laser diode pumped, intense 1.8 μm emission is obtained. Based on the absorption spectra, radiative properties are predicted using Judd-Ofelt theory. The maximum value of emission cross-section of Tm3+ around 1.8 μm can reach 1.46 × 10−20 cm2, which indicated that the germanate-tellurite glass may provide high gain as a good medium for efficient 1.8 μm laser system. PMID:24918516

  17. The effect of La2O3 in Tm3+-doped germanate-tellurite glasses for ~2 μm emission

    Science.gov (United States)

    Peng, Ya-Pei; Yuan, Xinqiang; Zhang, Junjie; Zhang, Long

    2014-06-01

    A germanate-tellurite glass (GeO2-TeO2-K2O-Nb2O5-La2O3) with thulium doping has been investigated for application as a laser material around 2.0 μm regions. Under the 808 nm laser diode pumped, intense 1.8 μm emission is obtained. Based on the absorption spectra, radiative properties are predicted using Judd-Ofelt theory. The maximum value of emission cross-section of Tm3+ around 1.8 μm can reach 1.46 × 10-20 cm2, which indicated that the germanate-tellurite glass may provide high gain as a good medium for efficient 1.8 μm laser system.

  18. The effect of La2O3 in Tm3+-doped germanate-tellurite glasses for ~2 μm emission

    OpenAIRE

    Peng, Ya-Pei; Yuan, Xinqiang; Zhang, Junjie; Zhang, Long

    2014-01-01

    A germanate-tellurite glass (GeO2-TeO2-K2O-Nb2O5-La2O3) with thulium doping has been investigated for application as a laser material around 2.0 μm regions. Under the 808 nm laser diode pumped, intense 1.8 μm emission is obtained. Based on the absorption spectra, radiative properties are predicted using Judd-Ofelt theory. The maximum value of emission cross-section of Tm3+ around 1.8 μm can reach 1.46 × 10−20 cm2, which indicated that the germanate-tellurite glass may provide high gain as a g...

  19. Optical properties of single doped Cr3+ and co-doped Cr3+-Nd3+ aluminum tantalum tellurite glasses

    International Nuclear Information System (INIS)

    Rodriguez-Mendoza, U.R.; Speghini, A.; Jaque, D.; Zambelli, M.; Bettinelli, M.

    2004-01-01

    The optical properties for single doped Cr 3+ and co-doped Cr 3+ -Nd 3+ aluminum tantalum tellurite glasses have been studied as a function of temperature. For the single doped glass, the existence of two bands in the emission spectra at low temperature indicates the presence of two different sites for the Cr 3+ ions, labelled as usual as low- and high-field sites. The broad band centred in the Near Infrared region, corresponds to low-field sites transition 4 T 2 → 4 A 2 , and the narrow band centred at approximately 715 nm to the high-field sites transition 2 E→ 4 A 2 . The emission intensity for both high- and low-field sites shows a strong decrease with increasing temperature, with the emission for the former sites vanishing at RT. In both cases the quenching observed with the increase of temperature can be ascribed to the presence of non-radiative relaxation mechanisms. Experimental observations for the co-doped glass show that both radiative and non-radiative energy transfer processes from Cr 3+ to Nd 3+ are present

  20. Effect of silver nanoparticles on the 1.53 μm fluorescence in Er3+/Yb3+ codoped tellurite glasses

    Science.gov (United States)

    Wu, Libo; Zhou, Yaxun; Zhou, Zizhong; Cheng, Pan; Huang, Bo; Yang, Fengjing; Li, Jun

    2016-07-01

    Improving the spectroscopic properties of rare earth (RE) doped glass materials is a challenging task. In the present work the metallic silver nanoparticles (Ag NPs) were embedded into Er3+/Yb3+ codoped tellurite glasses with composition TeO2-Bi2O3-TiO2, prepared using melt-quenching and subsequent heat-treated techniques, and the improved effect of Ag NPs on the 1.53 μm band fluorescence of Er3+ ions was investigated. About 24 h heat-treatment of Er3+/Yb3+ codoped tellurite glass containing 1 mol % amount of AgNO3 at the temperature 370 °C yielded the well-dispersed and near-spherical Ag NPs with ∼11.4 nm average diameter as evidenced by transmission electron microscopy (TEM) image. The intense 1.53 μm band fluorescence was observed in the prepared Er3+/Yb3+ codoped tellurite glasses under the excitation of 980 nm and was further improved with the presence of Ag NPs in the glass matrix, which is attributed to the enhanced local electric field around doped RE ions induced by Ag NPs and the possible energy transfer from Ag NPs to Er3+ ions. The enhanced local electric field was well demonstrated by comparing the variation of emission spectra of hypersensitive probe Eu3+ ions in tellurite glasses with and without Ag NPs. From the Judd-Ofelt analysis, it was also found that the value of Ω6 intensity parameter increased slightly with the increase of Ag NPs concentration in a certain range, also confirming the possibility of realizing strong fluorescence emission. In addition, the amorphous structural nature was demonstrated by the measured X-ray diffraction (XRD) patterns with no sharp diffraction peak. The enhanced 1.53 μm band fluorescence indicates that the Er3+/Yb3+ codoped tellurite glass with an appropriate amount of Ag NPs is a promising candidate for the development of Er3+-doped fiber amplifiers (EDFAs) applied in the WDM systems.

  1. On observation of the downconversion mechanism in Er{sup 3+}/Yb{sup 3+} co-doped tellurite glass using thermal and optical parameters

    Energy Technology Data Exchange (ETDEWEB)

    Figueiredo, M.S.; Santos, F.A. [Universidade Federal da Grande Dourados, Faculdade de Ciências Exatas e Tecnologias, Dourados, MS (Brazil); Yukimitu, K.; Moraes, J.C.S. [Universidade Estadual Paulista, UNESP, Departamento de Física e Química, Av. Brasil, 56, 15385-000 Ilha Solteira, SP (Brazil); Nunes, L.A.O. [Instituto de Física de São Carlos, Universidade de São Paulo, CP 369, 13560-970 São Carlos, SP (Brazil); Andrade, L.H.C. [Grupo de Espectroscopia Óptica e Fototérmica, Universidade Estadual de Mato Grosso do Sul, Cidade Universitária de Dourados, CP 351, Dourados, MS (Brazil); Lima, S.M., E-mail: smlima@uems.br [Grupo de Espectroscopia Óptica e Fototérmica, Universidade Estadual de Mato Grosso do Sul, Cidade Universitária de Dourados, CP 351, Dourados, MS (Brazil)

    2015-01-15

    In this work we report the observed downconversion (DC) mechanism in Er{sup 3+}/Yb{sup 3+}-codoped tellurite glasses (in mol%, 80TeO{sub 2}–10Li{sub 2}O–10TiO{sub 2}). The samples were synthesized by the conventional melt-quenching method and then studied using optical spectroscopy and thermal lens spectroscopy (TLS). These characterizations enabled investigation of the radiative and nonradiative processes involved in energy transfer from erbium to ytterbium. The visible Er{sup 3+} fluorescence intensities decreased as a function of the Yb{sup 3+} concentration, and there was a corresponding increase in the ytterbium emission at around 980 nm. Simultaneously, there was a reduction in the heat-generated due nonradiative decays (∼21%) when ytterbium was added. This temperature change was measured by TLS measurements and the results corroborate with the indicated by spectroscopic interpretation. - Highlights: • Energy transfer from erbium to ytterbium in tellurite glass. • ∼56% of cross-relaxation efficiency from Er{sup 3+} to Yb{sup 3+}. • Downconversion effect in tellurite glasses. • Downconversion effect observation by thermal lens spectroscopy.

  2. Structural, optical absorption and photoluminescence spectral studies of Sm3+ ions in Alkaline-Earth Boro Tellurite glasses

    Science.gov (United States)

    Siva Rama Krishna Reddy, K.; Swapna, K.; Mahamuda, Sk.; Venkateswarlu, M.; Srinivas Prasad, M. V. V. K.; Rao, A. S.; Prakash, G. Vijaya

    2018-05-01

    Sm3+ ions doped Alkaline-Earth Boro Tellurite (AEBT) glasses were prepared by using conventional melt quenching technique and characterized using the spectroscopic techniques such as FT-IR, optical absorption, emission and decay spectral measurements to understand their utility in optoelectronic devices. From absorption spectra, the bonding parameters, nephelauxetic ratios were determined to know the nature of bonding between Sm3+ ions and its surrounding ligands. From the measured oscillator strengths, the Judd-Ofelt (J-O) intensity parameters were evaluated and in turn used to estimate various radiative parameters for the fluorescent levels of Sm3+ ions in AEBT glasses. The PL spectra of Sm3+ ions exhibit three emission bands corresponding to the transitions 4G5/2 → 6H5/2, 6H7/2 and 6H9/2 in the visible region for which the emission cross-sections and branching ratios were evaluated. The decay spectral profiles measured for 4G5/2 → 6H7/2 transition showed single exponential for lower concentration and non-exponential for higher concentration of doped rare earth ion in the as prepared glasses. Conversion of decay spectral profiles from single to non-exponential have been analyzed using Inokuti-Hirayama (I-H) model to understand the energy transfer mechanism involved in the decay process. CIE Chromaticity coordinates were measured using emission spectral data to identify the exact region of emission from the as-prepared glasses. From the evaluated radiative parameters, emission cross-sections and quantum efficiencies, it was observed that AEBT glass with 1 mol% of Sm3+ ions is more suitable for designing optoelectronic devices.

  3. Enhanced green and red upconversion emissions in Er3+-doped boro-tellurite glass containing gold nanoparticles

    Science.gov (United States)

    Dousti, M. Reza; Amjad, Raja J.; Mahraz, Zahra Ashur S.

    2015-01-01

    Increasing the cross-section of upconversion emissions from the rare earth ions doped materials is a challenging issue. In this work, we report on the enhancement of the up-converted emissions of Er3+-doped boro-tellurite glasses containing gold nanoparticles which have been prepared by a conventional melt-quench technique. Seven absorption bands and three emission lines are observed using the UV-Vis-IR and photoluminescence spectroscopic techniques, respectively. Red emission is enhanced up to 30 times in a sample having 1 wt% of Au nanoparticles. The presence of the gold nanoparticles with average size of ∼5.74 nm is confirmed by transmission electron microscopy and corresponding surface plasmon band is observed at 630 nm in a singly-doped Au-nanoparticles embedded glass sample. A model to determine the enhancement factor of the emissions is suggested which could not describe the phenomenon for high concentrations of nanoparticles. Enhancement is attributed to the increased local field around the metal, and the results are discussed in details.

  4. Optical characterization of Eu3+ and Tb3+ ions doped cadmium lithium alumino fluoro boro tellurite glasses.

    Science.gov (United States)

    Raju, K Vemasevana; Sailaja, S; Raju, C Nageswara; Reddy, B Sudhakar

    2011-06-01

    This article reports on the development and spectral results of Eu(3+) and Tb(3+) ions doped cadmium lithium alumino fluoro boro tellurite (CLiAFBT) glasses in the following composition. 40TeO2-30B2O3-10CdO-10Li2O-10AlF3 (Hostglass) (40-x)TeO2-30B2O3-10CdO-10Li2O-10AlF3-xEu2O3 (40-x)TeO2-30B2O3-10CdO-10Li2O-10AlF3-xTb4O7 where x=0.25, 0.50, 0.75, 1.0, 1.25 mol%. Glass amorphous nature and thermal properties have been studied using the XRD and DSC profiles. From the emission spectra of Eu(3+):glasses, five emission transitions have been observed at 578 nm, 592 nm, 612 nm, 653 nm, 701 nm and are assigned to the transitions (5)D(0)→(7)F(0), (7)F(1,)(7)F(2), (7)F(3) and (7)F(4), respectively, with λ(exci)=392 nm ((7)F(0)→(5)L(6)). In case of Tb(3+):glasses, four emission transitions ((5)D(4)→(7)F(6,)(7)F(5), (7)F(4) and (7)F(3)) are observed at 488 nm, 543 nm, 584 nm and 614 nm, respectively, with λ(exci)=376 nm. Decay curves and energy level diagrams have been plotted to evaluate the life times and to analyze the emission mechanism. Copyright © 2011 Elsevier B.V. All rights reserved.

  5. Gold nanoparticles assisted surface enhanced Raman scattering and luminescence of Er{sup 3+} doped zinc–sodium tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Ghoshal, S.K.; Awang, Asmahani, E-mail: asmahani_awang@yahoo.com; Sahar, M.R.; Arifin, R.

    2015-03-15

    Significant enhancements in Er{sup 3+} luminescence and Raman intensity mediated via surface plasmon resonance (SPR) of gold (Au) nanoparticles (NPs) embedded zinc–sodium tellurite glass are reported. The observed modifications in the physical and spectroscopic properties are ascribed to the alterations in the glass network. XRD pattern confirms the amorphous nature of prepared glass sample. UV–vis-NIR spectra reveal seven absorption bands. Surface plasmon band is evidenced around 626–630 nm. TEM images manifest the growth of non-spherical Au NPs with average diameter between ∼7.2 nm and 8.6 nm. The visible up-conversion (UC) emission for all samples under 779 nm excitation exhibits three bands centered at 503 nm (green), 546 (green) and 637 nm (red) ascribed to {sup 2}H{sub 11/2}→{sup 4}I{sub 15/2}, {sup 4}S{sub 3/2}→{sup 4}I{sub 15/2} and {sup 4}F{sub 9/2}→{sup 4}I{sub 15/2} transitions. Glass sample with 0.4 mol% Au displaying the highest luminescence intensity with enhancement factor of 3.85 and 3.56 for green bands, and 7.61 for the red band is ascribed to the NPs local field enhancement and energy transfer between rare earth (RE) ions and NPs. FTIR spectra show the vibration of ZnO{sub 4} bonds, Te-O bond in TeO{sub 3} (tp) and TeO{sub 4} (tbp) units and the hydroxyl groups. Raman spectra demonstrate the presence of Er-O and Zn-O bond, anti-symmetric vibrations of Te-O-Te bonds and stretching modes of non-bonded oxygen exists in TeO{sub 3} and TeO{sub 3+1} unit. The amplifications in Raman signals by a factor of 1.62, 1.58, 1.64, 1.68 and 1.69 corresponding to the peak centered at 262 cm{sup −1}, 382 cm{sup −1}, 521 cm{sup −1}, 670 cm{sup −1} and 725 cm{sup −1} are attributed to the contribution of a surface plasmon generating a strong, localized and secondary field. We assert that our glass compositions offer favorable potential to develop solid state lasers and other versatile nanophotonic devices. - Highlights: • Gold

  6. Benefits and drawbacks of zinc in glass ionomer bone cements

    Energy Technology Data Exchange (ETDEWEB)

    Brauer, Delia S; Hill, Robert G [Unit of Dental Physical Sciences, Barts and The London School of Medicine and Dentistry, Queen Mary University of London, Mile End Road, London E1 4NS (United Kingdom); Gentleman, Eileen; Stevens, Molly M [Department of Materials, Imperial College London, Exhibition Road, London SW7 2AZ (United Kingdom); Farrar, David F, E-mail: d.brauer@qmul.ac.uk [Smith and Nephew Research Centre, York Science Park, Heslington YO10 5DF (United Kingdom)

    2011-08-15

    Glass polyalkenoate (ionomer) cements (GPCs) based on poly(acrylic acid) and fluoro-alumino-silicate glasses are successfully used in a variety of orthopaedic and dental applications; however, they release small amounts of aluminium, which is a neurotoxin and inhibits bone mineralization in vivo. Therefore there has been significant interest in developing aluminium-free glasses containing zinc for forming GPCs because zinc can play a similar structural role in the glass, allowing for glass degradation and subsequent cement setting, and is reported to have beneficial effects on bone formation. We created zinc-containing GPCs and characterized their mechanical properties and biocompatibility. Zinc-containing cements showed adhesion to bone close to 1 MPa, which was significantly greater than that of zinc-free cements (<0.05 MPa) and other currently approved biological adhesives. However, zinc-containing cements produced significantly lower metabolic activity in mouse osteoblasts exposed to cell culture medium conditioned with the cements than controls. Results show that although low levels of zinc may be beneficial to cells, zinc concentrations of 400 {mu}M Zn{sup 2+} or more resulted in cell death. In summary, we demonstrate that while zinc-containing GPCs possess excellent mechanical properties, they fail basic biocompatibility tests, produce an acute cytotoxic response in vitro, which may preclude their use in vivo.

  7. Silver nanoparticles enhanced luminescence properties of Er³⁺ doped tellurite glasses: Effect of heat treatment

    Energy Technology Data Exchange (ETDEWEB)

    Fares, Hssen; Férid, Mokhtar [Laboratoire de Physico-Chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, B.P. 95 Hammam-Lif, 2050 (Tunisia); Elhouichet, Habib, E-mail: habib.elhouichet@fst.rnu.tn [Laboratoire de Physico-Chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, B.P. 95 Hammam-Lif, 2050 (Tunisia); Department of Physics, Sciences Faculty of Tunis, University Tunis ElManar 2092 (Tunisia); Gelloz, Bernard [Graduate School of Engineering, Nagoya University, 2-24-16 Furo-cho, Chikusa-ku, Nagoya, Aichi 464-8603 (Japan)

    2014-09-28

    Tellurite glasses doped Er³⁺ ions and containing Silver nanoparticles (Ag NPs) are prepared using melt quenching technique. The nucleation and growth of Ag NPs were controlled by a thermal annealing process. The X-ray diffraction pattern shows no sharp peak indicating an amorphous nature of the glasses. The presence of Ag NPs is confirmed from transmission electron microscopy micrograph. Absorption spectra show typical surface plasmon resonance (SPR) band of Ag NPs within the 510–550 nm range in addition to the distinctive absorption peaks of Er³⁺ ions. The Judd-Ofelt (J-O) intensity parameters, oscillator strengths, spontaneous transition probabilities, branching ratios, and radiative lifetimes were successfully calculated based on the experimental absorption spectrum and the J-O theory. It was found that the presence of silver NPs nucleated and grown during the heat annealing process improves both of the photoluminescence (PL) intensity and the PL lifetime relative to the ⁴I13/2 → ⁴I15/2 transition. Optimum PL enhancement was obtained after 10 h of heat-treatment. Such enhancements are mainly attributed to the strong local electric field induced by SPR of silver NPs and also to energy transfer from the surface of silver NPs to Er³⁺ ions, whereas the quenching is ascribed to the energy transfer from Er³⁺ ions to silver NPs. Using the Mc Cumber method, absorption cross-section, calculated emission cross-section, and gain cross-section for the ⁴I13/2 → ⁴I15/2 transition were determined and compared for the doped and co-doped glasses. The present results indicate that the glass heat-treated for 10 h has good prospect as a gain medium applied for 1.53 μm band broad and high-gain erbium-doped fiber amplifiers.

  8. Enhanced 1.32 μm fluorescence and broadband amplifying for O-band optical amplifier in Nd3+-doped tellurite glass

    Science.gov (United States)

    Zhou, Zi-zhong; Zhou, Ming-han; Su, Xiu-e.; Cheng, Pan; Zhou, Ya-xun

    2017-01-01

    WO3 oxides with relatively high phonon energy and different concentrations were introduced into the Nd3+-doped tellurite-based glasses of TeO2-ZnO-Na2O to improve the 1.32 μm band fluorescence emission. The absorption spectra, Raman spectra, 1.32 μm band fluorescence spectra and differential scanning calorimeter (DSC) curves were measured, together with the Judd-Ofelt intensity parameters, stimulated emission and gain parameters were calculated to evaluate the effects of WO3 amount on the glass structure and spectroscopic properties of 1.32 μm band fluorescence. It is shown that the introduction of an appropriate amount of WO3 oxide can effectively improve the 1.32 μm band fluorescence intensity through the enhanced multi-phonon relaxation (MPR) processes between the excited levels of Nd3+. The results indicate that the prepared Nd3+-doped tellurite glass with an appropriate amount of WO3 oxide is a potential gain medium applied for the O-band broad and high-gain fiber amplifier.

  9. Yb3+ sensitized Tm3+ upconversion in tellurite lead oxide glass.

    Science.gov (United States)

    Mohanty, Deepak Kumar; Rai, Vineet Kumar; Dwivedi, Y

    2012-04-01

    Triply ionized thulium/thulium--ytterbium doped/codoped TeO2-Pb3O4 (TPO) glasses have been fabricated by classical quenching method. The upconversion emission spectra in the Tm3+/Tm3+-Yb3+ doped/codoped glasses upon excitation with a diode laser lasing at ∼980 nm has been studied. Effect of the addition of the Yb3+ on the upconversion emission intensity in the visible and near infrared regions of the Tm3+ doped in TPO glass has been studied and the processes involved explored. Copyright © 2011 Elsevier B.V. All rights reserved.

  10. Effect of γ-ray irradiation on optical properties of erbium doped bismuth-tellurite glasses

    Science.gov (United States)

    Keshavamurthy, K.; Eraiah, B.

    2018-05-01

    Heavy metal oxide contained glasses are very promising candidates in shielding and photonic materials. In this paper, we studied the effect of γ-ray irradiation on optical properties of Er2O3-Bi2O3-TeO2 glasses through UV-Visible spectrophotometer. After γ-ray exposure, the optical band gap decreases and Urbach energy increases, which is due to creation of defects within the glass network as a result increases the number of non-bridging oxygens.

  11. Short-range structure and thermal properties of lead tellurite glasses

    Science.gov (United States)

    Hirdesh, Kaur, Amarjot; Khanna, Atul; Gonzàlez, Fernando

    2017-05-01

    PbO-TeO2 glasses having composition: xPbO-(100 - x)TeO2 (x = 10, 15 and 20 mol%) were prepared by melt quenching and characterized by X-ray diffraction, density measurements, differential scanning calorimetry and Raman spectroscopy. Glass density increases from 5.89 to 6.22 g cm-3 with increase in PbO concentration from 10 to 20 mol%, due to the replacement of TeO2 by heavier PbO. DSC studies found that glass transition temperature (Tg) decreases from a value of 295°C to 281°C. Raman studies found that glass short-range structure consists of TeO4 and TeO3 structural units and that PbO modifies the network by the structural transformation: TeO4 to TeO3.

  12. Physical, structural and optical characterizations of borate modified bismuth-silicate-tellurite glasses

    Science.gov (United States)

    Berwal, Neelam; Kundu, R. S.; Nanda, Kirti; Punia, R.; Kishore, N.

    2015-10-01

    Quaternary bismuthate glasses with compositions xB2O3-(80 - x) Bi2O3-15SiO2-5TeO2 have been prepared by melt-quench technique. X-ray diffraction studies were performed to ascertain the amorphous nature of samples. The density, molar volume and crystalline volume decrease with increase in B2O3 content whereas the glass transition temperature shows the reverse trend. The Raman and FTIR spectra of the studied glasses indicate that B2O3 has been found to exist in the form of BO3 trigonal and BO4 tetrahedral structural units and vibrations corresponding to these structural units increase with increase in B2O3 content. SiO2 is present in the form of SiO4 tetrahedral structural units and TeO2 in the form of TeO3 structural units. Bismuth plays the role of network modifier [BiO6 octahedra] as well as network former [BiO3 pyramids] for all the glass compositions. The optical band gap energy has been calculated from the fitting of both Mott and Davis's model and Hydrogenic excitonic model with the experimentally observed absorption spectra. A good fitting of experimental data with HEM indicates the excitonic formation in the studies glass system. The values of optical band gap energy show nonlinear behavior due to the structural changes that take place in the present glass samples. The Urbach energy calculated using Urbach empirical formula for studied glass samples suggest the possibility of reduction in defect concentrations. The metallization criterion of the presently studied samples suggests that the prepared glasses may be potential candidates for nonlinear optical applications.

  13. Near infrared and upconversion luminescence behaviour of Er3+/Yb3+ codoped boro-tellurite glasses

    Science.gov (United States)

    Maheshvaran, K.; Arunkumar, S.; Vijayakumar, R.; Marimuthu, K.

    2014-04-01

    The broadband NIR and upconversion luminescence behavior in a new series of Er3+/Yb3+ codoped TeO2-B2O3-SrO-BaO-Li2O-LiF glasses have been studied exciting at a wavelength of 980 nm using semiconductor laser. A broadband emission is observed from 1450 to 1650 nm with a full width at half maximum (FWHM) around 165 nm in 0.5wt% Yb3+ ion content E0.5YLTB glass. The radiative parameters such as transition probability (A), stimulated emission cross-section (σE), experimental and calculated branching ratios (βR), optical gain width (σp×FWHM) and radiative lifetime (τcal) have been calculated for the 4I13/2→4I15/2 NIR emission. Upconversion luminescence spectra of the prepared glasses have been studied and the ESA & ET processes have also been discussed and reported.

  14. Radiative transition, local field enhancement and energy transfer microcosmic mechanism of tellurite glasses containing Er3+, Yb3+ ions and Ag nanoparticles

    International Nuclear Information System (INIS)

    Zhang, Wenjun; Lin, Jian; Cheng, Mingzhao; Zhang, Shuo; Jia, Yujie; Zhao, Junhong

    2015-01-01

    Er 3+ -doped, Er 3+ /Yb 3+ co-doped tellurite glass with and without Ag NPs were synthesized by melt-quenching method. The high resolution transmission electron microscopy (HR-TEM) and selected area electron diffractions (SAED) manifest growth of Ag NPs. The UV–vis–NIR absorption spectroscopy and fluorescence spectroscopy were measured. The optical band gap and multiphonon relaxation rate constants were calculated. The electronic band structure and local density of state (DOS) of Ag NPs are calculated. The fluorescence emission and enhancement mechanism including localized surface plasmon resonance (LSPR) and energy transfer (ET) microcosmic mechanism were discussed. The electric field distributions of Ag NPs are emulated by FDTD solutions software. Local field enhancement (LFE) induced by LSPR and lightning rod effect was found to be responsible for the fluorescence enhancement while energy transfer from Ag NPs to rare-earth was considered ignorable in the samples without photoluminescent emission. - Highlights: • Tellurite glasses containing Er 3+ , Yb 3+ and Ag NPs are prepared. • Judd–Ofelt and multiphonon relaxation are calculated. • The electronic band structures of Ag NPs are calculated. • The energy transfer mechanism is discussed. • The plasmon resonance effect of Ag NPs is discussed

  15. Correlation between physical properties and ultrasonic relaxation parameters in transition metal tellurite glasses

    Science.gov (United States)

    Abd El-Moneim, A.

    2003-07-01

    The correlation between activation energy of ultrasonic relaxation process through the temperature range from 140 to 300 K and some physical properties has been investigated in pure TeO 2 and transition metal TeO 2-V 2O 5 and TeO 2-MoO 3 glasses according to Bridge and Patel's theory. The oxygen density (loss centers), number of two-well systems, hopping distance and mechanical relaxation time have been calculated in these glasses from the data of density, bulk modulus and stretching force constant of the glass. It has been found that the acoustic activation energy increased linearly with both the oxygen density and the number of two-well systems. The correlation between the acoustic activation energy and bulk modulus was achieved through the stretching force constant of the network and other structural parameters. Moreover, the experimental values of activation energy (V) agree well with those calculated from an empirical equation presented in this study in the form V=2.9×10 -7 F( F/ K) 3.37, where F is the stretching force constant of the glass and K is the experimental bulk modulus.

  16. Mixed conductivity studies in silver oxide based barium vanado-tellurite glasses

    International Nuclear Information System (INIS)

    Pant, Meenakshi; Kanchan, D.K.; Sharma, Poonam; Jayswal, Manish S.

    2008-01-01

    The dc conductivity and frequency dependent ac conductivity of the quaternary glass system x(BaO:1.5 Ag 2 O)-(95 - x)V 2 O 5 -5TeO 2 , are reported in the frequency range 1 Hz to 32 MHz in the temperature range from room temperature to 433 K. The dc conductivity measured in high temperature range increased with transition metal oxide content while the activation range decreased. The conductivity arises mainly from polaron hopping between V 4+ and V 5+ ions. High temperature conductivity data satisfy Mott's small polaron hopping model. It is found that a mechanism of non-adiabatic hopping is the most appropriate conduction model for these glasses. A power law behavior σ(ω) = σ dc + Aω n (with 0 < n < 1) is well exhibited by the ac conductivity data of the glasses. The activation energy calculated from both the relaxation time and dc conductivity is found to be nearly same in both the cases. A scaling of the conductivity spectra with respect to temperature and composition is attempted and it is observed that the relaxation dynamics of charge carriers in the present glasses is independent of temperature and composition

  17. Femtosecond laser writing of waveguides in zinc phosphate glasses [Invited

    NARCIS (Netherlands)

    Fletcher, L.B.; Witcher, J.J.; Troy, N.; Reis, S.T.; Brow, R.K.; Martinez Vazquez, R.; Osellame, R.; Krol, D.M.

    2011-01-01

    We have studied the relationship between the initial glass composition and the structural changes associated with laser-induced refractive index modification in a series of Er-Yb doped and undoped zinc phosphate glasses. White light microscopy and waveguide experiments are used together with Raman

  18. Benefits and drawbacks of zinc in glass ionomer bone cements

    International Nuclear Information System (INIS)

    Brauer, Delia S; Hill, Robert G; Gentleman, Eileen; Stevens, Molly M; Farrar, David F

    2011-01-01

    Glass polyalkenoate (ionomer) cements (GPCs) based on poly(acrylic acid) and fluoro-alumino-silicate glasses are successfully used in a variety of orthopaedic and dental applications; however, they release small amounts of aluminium, which is a neurotoxin and inhibits bone mineralization in vivo. Therefore there has been significant interest in developing aluminium-free glasses containing zinc for forming GPCs because zinc can play a similar structural role in the glass, allowing for glass degradation and subsequent cement setting, and is reported to have beneficial effects on bone formation. We created zinc-containing GPCs and characterized their mechanical properties and biocompatibility. Zinc-containing cements showed adhesion to bone close to 1 MPa, which was significantly greater than that of zinc-free cements ( 2+ or more resulted in cell death. In summary, we demonstrate that while zinc-containing GPCs possess excellent mechanical properties, they fail basic biocompatibility tests, produce an acute cytotoxic response in vitro, which may preclude their use in vivo.

  19. Tm3+/Yb3+ co-doped tellurite glass with silver nanoparticles for 1.85 μm band laser material

    Science.gov (United States)

    Huang, Bo; Zhou, Yaxun; Cheng, Pan; Zhou, Zizhong; Li, Jun; Jin, Wei

    2016-10-01

    Tm3+/Yb3+ co-doped tellurite glasses with different silver nanoparticles (Ag NPs) concentrations were prepared using the conventional melt-quenching technique and characterized by the UV/Vis/NIR absorption spectra, 1.85 μm band fluorescence emission spectra, transmission electron microscopy (TEM) images, differential scanning calorimeter (DSC) curves and X-ray diffraction (XRD) patterns to investigate the effects of Ag NPs on the 1.85 μm band spectroscopic properties of Tm3+ ions, thermal stability and structural nature of glass hosts. Under the excitation of 980 nm laser diode (LD), the 1.85 μm band fluorescence emission of Tm3+ ions enhances significantly in the presence of Ag NPs with average diameter of ∼8 nm and local surface Plasmon resonance (LSPR) band of ∼590 nm, which is mainly attributed to the increased local electric field induced by Ag NPs at the proximity of doped rare-earth ions on the basis of energy transfer from Yb3+ to Tm3+ ions. An improvement by about 110% of fluorescence intensity is observed in the Tm3+/Yb3+ co-doped tellurite glass containing 0.5 mol% amount of AgNO3 while the prepared glass samples possess good thermal stability and amorphous structural nature. Meanwhile, the Judd-Ofelt intensity parameters Ωt (t = 2,4,6), spontaneous radiative transition probabilities, fluorescence branching ratios and radiative lifetimes of relevant excited levels of Tm3+ ions were determined based on the Judd-Ofelt theory to reveal the enhanced effects of Ag NPs on the 1.85 μm band spectroscopic properties, and the energy transfer micro-parameters and phonon contribution ratios were calculated based on the non-resonant energy transfer theory to elucidate the energy transfer mechanism between Yb3+ and Tm3+ ions. The present results indicate that the prepared Tm3+/Yb3+ co-doped tellurite glass with an appropriate amount of Ag NPs is a promising lasing media applied for 1.85 μm band solid-state lasers and amplifiers.

  20. Study of upconversion fluorescence property of novel Er3+/Yb3+ co-doped tellurite glasses.

    Science.gov (United States)

    Xu, Tie-Feng; Li, Guang-Po; Nie, Qiu-Hua; Shen, Xiang

    2006-06-01

    Er3+/Yb3+ co-doped TeO2-B2O3-Nb2O5-ZnO (TBN) glasses were prepared. The absorption spectra and upconversion luminescence spectra of TBN glasses were measured and analyzed. The upconversion emission bands centered at 530, 546 and 658 nm were observed under the excitation at 975 nm, corresponding to the transitions of 2H11/2-->4I15/2, 4S3/2-->4I15/2 and 4F9/2-->4I15/2 respectively. The ratio of red emission to green emission increases with an increasing of Yb3+ ions concentration. According to the quadratic dependence on excitation power, the possible upconversion mechanisms and processes were discussed.

  1. Ion dynamics in AgI doped silver selenium-tellurite mixed former glasses

    Science.gov (United States)

    Palui, A.; Ghosh, A.

    2017-03-01

    The ionic conductivity and the conductivity spectra of the glass compositions xAgI-(1-x)[yAg2O-(1-y)(0.5SeO2-0.5TeO2)] have been studied at different temperatures The activation energy for the dc conduction has been analyzed using the Anderson-Stuart model, and a correlation between the dc conductivity and the doorway radius has been obtained. We have analyzed the conductivity spectra using the random free-energy barrier model, taking into account the contribution of electrode polarization. It is observed that the Barton-Nakajima-Namikawa relation between the conductivity and the relaxation time is valid for these glasses. The time-temperature superposition principle has been verified using the scaling of the conductivity spectra in the framework of the random barrier model. The charge carrier density, obtained from the Nernst-Einstein relation, is found to be almost independent of temperature, but dependent weakly on composition. We have also studied the influence of the modification of the network structure of these glasses on ion migration and correlated the conductivity with the relative strength of the structural units.

  2. Judd-Ofelt analysis and improvement of thermal and optical properties of tellurite glasses by adding P{sub 2}O{sub 5}

    Energy Technology Data Exchange (ETDEWEB)

    Jlassi, I. [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Elhouichet, H., E-mail: habib.elhouichet@fst.rnu.t [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Departement de Physique, Faculte des Sciences de Tunis, Campus ElManar 2092 (Tunisia); Ferid, M. [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Barthou, C. [Institut des Nanosciences de Paris, Universite P. et M. Curie, Centre Nationale de la Recherche Scientifique, UMR-7588, Campus Boucicaut, 140 rue de Lourmel, 75015 Paris (France)

    2010-12-15

    Er{sup 3+} and Er{sup 3+}/Yb{sup 3+} co-doped tellurite glasses, suitable for developing optical fiber laser and amplifier, have been elaborated from the conventional melt-quenching method. Results of differential scanning calorimetry (DSC) measurements indicate a good thermal stability of tellurite glasses. The DSC measurements show an improvement of thermal stability of glass hosts after adding P{sub 2}O{sub 5}. Absorption spectrum from near infrared to visible was obtained and the Judd-Ofelt (J-O) intensity parameters ({Omega}{sub 2}, {Omega}{sub 4}, and {Omega}{sub 6}) were determined. Spontaneous emission probabilities of some relevant transitions, branching ratio, and radiative lifetimes of several excited states of Er{sup 3+} have been predicted using intensity J-O parameters. Absorption cross-section and calculated emission cross-section, using the McCumber method, for the {sup 4}I{sub 13/2{yields}}{sup 4}I{sub 15/2} transition, were determined and compared for the doped and co-doped glasses. Energy transfer (ET) and effect of changing concentration of P{sub 2}O{sub 5} and Yb{sup 3+} ions on spectroscopic properties were investigated. It was found that the addition of P{sub 2}O{sub 5} can increase the symmetry of the Er{sup 3+} ion. As a consequence, PL lifetime becomes more longer. The spectroscopic properties and the efficient infrared luminescence indicate that Er{sup 3+} doped TeO{sub 2}-ZnO-Na{sub 2}O-Er{sub 2}O{sub 3}(TZNE) is a promising laser and amplifier materials and may be a potentially useful material for developing upconversion fiber optical devices.

  3. Short-range structure of barium tellurite glasses and its correlation with stress-optic response

    Science.gov (United States)

    Kaur, Amarjot; Khanna, Atul; Fábián, Margit

    2018-06-01

    The atomic parameters of metal ion-oxygen speciation such as bond-lengths and nearest neighbor distances for Ba-O, Te-O and O-O pairs, co-ordination numbers and bond angle distributions for O-Ba-O, O-Te-O and O-O-O linkages are determined by neutron diffraction and Reverse Monte Carlo simulations on the series of xBaO-(100-x)TeO2 glasses containing 10, 15 and 20 mol% BaO. The glass network depolymerizes and the average Te-O co-ordination number decreases from 3.60 ± 0.02 to 3.48 ± 0.02 with increase in BaO concentration. Te-O bond lengths are in the range: 1.97 ± 0.01–1.92 ± 0.01 Å. Ba2+ is mostly in octahedral coordination and the Ba-O bond lengths are in the range: 2.73 ± 0.01 to 2.76 ± 0.03 Å. Te-O co-ordination number is also determined by Raman spectroscopy and it shows good agreement with the neutron data. The short-range structural properties i.e. metal ion coordination number (Nc) and bond lengths (d) were correlated with the stress-optic response. The bonding characteristic, Br values were determined from the structural data of xBaO-(100-x)TeO2 glasses and were used to predict the stress-induced birefringence properties.

  4. Up-conversion luminescence of Er3+/Yb3+/Nd3+-codoped tellurite glasses

    International Nuclear Information System (INIS)

    Lu Longjun; Nie Qiuhua; Xu Tiefeng; Dai Shixun; Shen Xiang; Zhang Xianghua

    2007-01-01

    Up-conversion luminescence and energy transfer (ET) processes in Nd 3+ -Yb 3+ -Er 3+ triply doped TeO 2 -ZnO-Na 2 O glasses have been studied under 800 nm excitation. Intense green up-conversion emissions around 549 nm, which can be attributed to the Er 3+ : 4 S 3/2 →4 I 15/2 transition, are observed in triply doped samples. In contrast, the green emissions are hardly observed in Er 3+ singly doped and Er 3+ -Yb 3+ codoped samples under the same condition. Up-conversion luminescence intensity exhibits dependence of Yb 2 O 3 -concentration and Nd 2 O 3 -concentration. Up-conversion mechanism in the triply doped glasses under 800 nm pump is discussed by analyzing the ET among Nd 3+ , Yb 3+ and Er 3+ . And a possible up-conversion mechanism based on sequential ET from Nd 3+ to Er 3+ through Yb 3+ is proposed for green and red up-conversion emission processes

  5. Crystallisation behavior and electronic conductivity of vanadium tellurite glass-ceramics

    DEFF Research Database (Denmark)

    Kjeldsen, Jonas; Yue, Yuanzheng; Rodrigues, A.C.M.

    2012-01-01

    is synthesized via the melt quenching technique, and crystalline 2TeO2-V2O5 is obtained by further heat-treatment of the quenched glass. Both states are confirmed by x-ray diffraction, scanning electron microscopy and differential scanning calorimetry. The redox state of vanadium is controlled via the melting...... and the ability to intercalate lithium-ions, it is a candidate for usage as cathode material. In the present work, we optimize the electronic conductivity of the congruent 2TeO2-V2O5 composition by tuning both the redox state of the vanadium and the overall degree of crystallinity. Amorphous 2TeO2-V2O5...

  6. Femtosecond laser-written double line waveguides in germanate and tellurite glasses

    Science.gov (United States)

    S. da Silva, Diego; Wetter, Niklaus U.; de Rossi, Wagner; Samad, Ricardo E.; Kassab, Luciana R. P.

    2018-02-01

    The authors report the fabrication and characterization of passive waveguides in GeO2-PbO and TeO2-ZnO glasses written with a femtosecond laser delivering pulses with 3μJ, 30μJ and 80fs at 4kHz repetition rate. Permanent refractive index change at the focus of the laser beam was obtained and waveguides were formed by two closely spaced laser written lines, where the light guiding occurs between them. The refractive index change at 632 nm is around 10-4 . The value of the propagation losses was around 2.0 dB/cm. The output mode profiles indicate multimodal guiding behavior. Raman measurements show structural modification of the glassy network. The results show that these materials are potential candidates for passive waveguides applications as low-loss optical components.

  7. Effect of PbO on optical properties of tellurite glass

    Science.gov (United States)

    Elazoumi, S. H.; Sidek, H. A. A.; Rammah, Y. S.; El-Mallawany, R.; Halimah, M. K.; Matori, K. A.; Zaid, M. H. M.

    2018-03-01

    Binary (1 - x)(TeO2) - x(PbO), x = 0, 0.10, 0.15, 0.20, 0.25, 0.30 mol% glass system was fabricated using melt quenching method. X-ray diffraction (XRD) technique was employed to confirm the amorphous nature. The microanalysis of the major components was performed using energy dispersive EDX and X-ray spectrometry. Both the molar volume and the density were measured. FTIR and UV spectra were recorded at 400-4000 cm-1 and 220-800 nm, respectively. The optical band gap (Eopt), Urbach's energy (Eu), index of refraction (n) were calculated using absorption spectrum fitting (ASF) and derivation of absorption spectrum fitting (DASF) methods. Molar refraction Rm and molecular polarizability αm have been calculated according to (ASF) method.

  8. Frequency upconversion in Er3+ doped tungsten tellurite glass containing Ag nanoparticles

    Science.gov (United States)

    Mahajan, S. K.; Parashar, J.

    2018-05-01

    The frequency upconversion emission in Er3+ doped TeO2-WO3-Li2O containing Ag nanoparticle (TWLEOAG) glasses at 980nm excitation is reported. The absorption spectra reveal not only the peaks due to Er3+ ions, but also the surface plasmon resonance band of silver NPs located around 525nm and 650 nm. The spherical AgNPs with average size ˜38 nm in the glassy matrix is evidenced from the TEM measurement. Under 980nm laser excitation upconversion emission spectra show two major emission at 550nm and 638nm originating from 4S3/2 and 4F9/2 energy levels of the Er3+ ions, respectively was observed. Upconversion emission enhancement factor 7 fold has been measured for sample heat treated during 40h. However for 18h heat treated TWLEOAG sample under 980 nm flash lamp excitation produced Intense green compare to red emission. Since the 980nm frequency is far from the AgNPs surface plasmon resonance frequency, visible emission ehancement is attributed to local field increase in proximity of the Ag NPs and not energy tranfer from NPs to emitters. Possible energy transfer upconversion mechanism has been also discussed.

  9. Elaboration and optimization of tellurite-based materials for raman gain application

    Science.gov (United States)

    Guery, Guillaume

    Tellurite-based oxide glasses have been investigated as promising materials for Raman gain applications, due to their good linear and nonlinear optical properties and their wide transparency windows in the near- and midwave infrared spectral region. Furthermore, their interesting thermal properties, i.e. low glass transition temperature and ability to be drawn into optical fibers, make tellurite-based glasses excellent candidates for optical fiber amplifiers. The estimation of the strength and spectral distribution of Raman gain in materials is commonly approximated from the spontaneous Raman scattering cross-section measurement. For development of tellurite-based glasses as Raman amplifiers, understanding the relationship between glass structure, vibrational response, and nonlinear optical properties (NLO) represents a key point. This dissertation provides an answer to the fundamental question of the PhD study: "What is the impact of the glass structure on Raman gain properties of tellurite glasses?" This dissertation summarizes findings on different tellurite-based glass families: the TeO2-TaO5/2-ZnO, TeO2-BiO 3/2-ZnO and TeO2-NbO5/2 glass networks. The influence of glass modifiers has been shown on the glass' properties. Introduction of tantalum oxide or zinc oxide has been shown to increase the glass' stability against crystallization, quantified by DeltaT, where DeltaT = Tx -Tg. Added to the variation of the glass viscosity, this attribute is critical in fabricating optical fibers and for the use of these materials in fiber-based Raman gain applications. The role of ZnO in the tellurite network and the mechanism for structural modification has been determined. This addition results in not only the largest DeltaT reported for these highly nonlinear glasses to date, but coincides with a commensurate decrease of the refractive index. A hydroxyl purification has been developed that when employed, resulted in high purity preform materials exhibiting a limited

  10. Crystal growth in zinc borosilicate glasses

    Science.gov (United States)

    Kullberg, Ana T. G.; Lopes, Andreia A. S.; Veiga, João P. B.; Monteiro, Regina C. C.

    2017-01-01

    Glass samples with a molar composition (64+x)ZnO-(16-x)B2O3-20SiO2, where x=0 or 1, were successfully synthesized using a melt-quenching technique. Based on differential thermal analysis data, the produced glass samples were submitted to controlled heat-treatments at selected temperatures (610, 615 and 620 °C) during various times ranging from 8 to 30 h. The crystallization of willemite (Zn2SiO4) within the glass matrix was confirmed by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM). Under specific heat-treatment conditions, transparent nanocomposite glass-ceramics were obtained, as confirmed by UV-vis spectroscopy. The influence of temperature, holding time and glass composition on crystal growth was investigated. The mean crystallite size was determined by image analysis on SEM micrographs. The results indicated an increase on the crystallite size and density with time and temperature. The change of crystallite size with time for the heat-treatments at 615 and 620 °C depended on the glass composition. Under fixed heat-treatment conditions, the crystallite density was comparatively higher for the glass composition with higher ZnO content.

  11. WO.sub.3./sub.-doped zinc borophosphate glasses

    Czech Academy of Sciences Publication Activity Database

    Šubčík, J.; Koudelka, L.; Mošner, P.; Gregora, Ivan; Montagne, L.; Revel, B.

    2009-01-01

    Roč. 50, č. 4 (2009), 243-248 ISSN 1753-3562 R&D Projects: GA AV ČR KAN301370701 Institutional research plan: CEZ:AV0Z10100520 Keywords : tungstate zinc borophosphate glasses * Raman spectroscopy * temperature * NMR Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.553, year: 2009

  12. Enhanced 2.7 μm emission from Er3+ doped oxyfluoride tellurite glasses for a diode-pump mid-infrared laser

    Directory of Open Access Journals (Sweden)

    F. F. Zhang

    2014-04-01

    Full Text Available The influence of fluoride and shielding gas (O2 or Ar on the physical and spectroscopic properties of Er3+ doped TeO2-ZnO-ZnF2 glass system is investigated. The larger electronegativity of F than O accounts for the gradual decrease of refractive index, density, and J-O parameters with increasing ZnF2. An analysis on Fourier transform infrared transmission spectra reveals that the absorption coefficient of OH− around 3 μm as low as 0.247 cm−1 can be achieved when 30 mol% ZnF2 containing sample is treated with Ar gas during glass melting process. The reduction of OH− groups combined with the low multiphonon relaxation rate (207 s−1 contributes to the enhanced emissions at 1.5 and 2.7 μm, along with prolonged lifetimes of 4I11/2 and 4I13/2 levels. A high branching ratio (17.95% corresponding to the Er3+: 4I11/2 → 4I13/2 transition, the large absorption and emission cross section (0.44 × 10−20 cm2 and 0.45 × 10−20 cm2, and good gain cross section demonstrate that oxyfluoride tellurite glass could be a promising material for a diode-pump 2.7 μm fiber laser.

  13. Effect of natural Fe{sub 3}O{sub 4} nanoparticles on structural and optical properties of Er{sup 3+} doped tellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Widanarto, W. [Physics Study Program, Jenderal Soedirman University, Jl. dr. Soeparno 61 Purwokerto 53123 (Indonesia); Sahar, M.R., E-mail: m-rahim@dfiz2.fs.utm.my [Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Johor Bahru, Skudai 81310 (Malaysia); Ghoshal, S.K.; Arifin, R.; Rohani, M.S.; Hamzah, K. [Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Johor Bahru, Skudai 81310 (Malaysia)

    2013-01-15

    Control doping of magnetic nanoparticles and its influence on optical and structural properties of tellurite glass is important from device perspectives. Natural Fe{sub 3}O{sub 4} nanoparticles obtained by extracting and ball milling iron sand, are incorporated in the Er{sup 3+} doped tellurite glasses having composition (80-x)TeO{sub 2}{center_dot}xFe{sub 3}O{sub 4}{center_dot}18ZnO{center_dot}1Li{sub 2}O{center_dot}1Er{sub 2}O{sub 3} (0{<=}x{<=}1.5) in mol% by melt quenching method at 850 Degree-Sign C. X-Ray diffraction spectra confirms the presence of iron nanoparticles with estimated sizes 18-70 nm and an amorphous structure of the samples. Thermal and optical characterizations are made using diffential thermal analysis, ultraviolet-visible and photoluminescence spectrocopies. It is found that the presence of nanoparticles changes color and thermal stability of the glasses, which is proved by increasing thermal stability factor from 118 to 132 Degree-Sign C. Absorption spectra consist of six peaks corresponding to different transition from ground state to the excited states in which the quench of the peak associated with {sup 4}F{sub 1/2} is attributed to the effect nanoparticles. Moreover, the shift in the absorption edge from {approx}400 to {approx}500 nm indicates a significant decrease of the optical energy band gap for both direct and indirect allowed transitions and a decrease in the Urbach energy as much as 0.116 eV is observed. The room temperature down-conversion luminescence spectra obtained under 500 nm excitation exhibit two strong peaks related to excited states {sup 4}S{sub 3/2} and {sup 4}F{sub 9/2} of Er{sup 3+} ions in the absence of nanoparticles. Furthermore, embedding nanoparticles into the glass not only make the peaks weaker but the second peak completely disappears. Interestingly, the emission bands of the Er{sup 3+} ion are quenched as concentration of the magnetic nanoparticles is increased.

  14. Al2O3 influence on structural, elastic, thermal properties of Yb(3+) doped Ba-La-tellurite glass: evidence of reduction in self-radiation trapping at 1μm emission.

    Science.gov (United States)

    Balaji, S; Biswas, K; Sontakke, A D; Gupta, G; Ghosh, D; Annapurna, K

    2014-12-10

    Ba-La-tellurite glasses doped with Yb(3+) ions have been prepared through melt quenching technique by modifying their composition with the inclusion of varied concentration of Al2O3 to elucidate its effects on glass structural, elastic, thermal properties and Yb(3+) ion NIR luminescence performance. The FTIR spectral analysis indicates Al2O3 addition is promoting the conversion of BOs from NBOs which have been generated during the process of depolymerisation of main glass forming TeO4 units. The elastic properties of the glass revealed an improved rigidity of the glass network on addition of Al2O3. In concurrence to this, differential thermal analysis showed an increase in glass transition temperature with improved thermal stability factor. Also, Yb(3+) fluorescence dynamics demonstrated that, Al2O3 inclusion helps in restraining the detrimental radiation trapping of ∼1μm emission. Copyright © 2014 Elsevier B.V. All rights reserved.

  15. The superspin glass transition in zinc ferrite nanoparticles

    Czech Academy of Sciences Publication Activity Database

    Kaman, Ondřej; Kořínková, T.; Jirák, T.; Maryško, Miroslav; Veverka, Miroslav

    2015-01-01

    Roč. 117, č. 17 (2015), "17C706-1"-"17C706-4" ISSN 0021-8979 R&D Projects: GA ČR(CZ) GAP108/11/0807; GA ČR GAP204/10/0035 Institutional support: RVO:68378271 Keywords : superspin glass * zinc ferrite * doped magnetite * magnetic nanoparticles * thermal decomposition Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.101, year: 2015

  16. Preparation and optical properties of TeO2-BaO-ZnO-ZnF2 fluoro-tellurite glass for mid-infrared fiber Raman laser applications

    Science.gov (United States)

    Li, Jie; Xiao, Xusheng; Gu, Shaoxuan; Xu, Yantao; Zhou, Zhiguang; Guo, Haitao

    2017-04-01

    A serial of novel fluoro-tellurite glasses with compositions of 60TeO2-20BaO-(20-x)ZnO-xZnF2 (x = 0, 2, 4, 5 and 6 mol%) were prepared. The compositional dependences of glass structural evaluation, Raman gain coefficient, UV-Vis transmission spectrum, IR transmission spectrum, linear refractive index and third-order nonlinearity were analyzed. The results showed that the addition of 6 mol% ZnF2 can further improve the Raman gain coefficient to as well as 52 × 10-11 cm/W and effectively decrease around 73% and 57% absorption coefficients respectively caused by free Osbnd H groups (@3.3 μm) and hydrogen-bonded Osbnd H groups (@4.5 μm) in glass. Addition of ZnF2 does not change the UV-Vis absorption edge, optical band gap energy and infrared region cut-off edge almost, while the linear refraction index and ultrafast third-nonlinearity show unmonotonic changes. These novel fluoro-tellurite glasses may be suitable candidates for using in mid-infrared Raman fiber laser and/or amplifier.

  17. Effect of Concurrent ZnO Addition and AlF3 Reduction on the Elastic Properties of Tellurite Based Glass System

    Directory of Open Access Journals (Sweden)

    Haji Abdul Aziz Sidek

    2014-01-01

    Full Text Available New ternary zinc oxyfluorotellurite (ZOFT with the composition (ZnOx-(AlF3y-(TeO2z, where 5≤x<35; 5≤y≤25; 60≤z≤70, has been successfully prepared by the conventional rapid melt quenching technique. Density, molar volume, and glass transition temperature have been assessed for each ZOFT glass sample. The longitudinal and transverse ultrasonic waves propagated in each glass sample were measured using a MBS8020 ultrasonic data acquisition system at 5 MHz frequency and room temperature. The longitudinal modulus (L, shear modulus (G, Young’s modulus (E, bulk modulus (K, and Poisson’s ratio (σ are assessed from both velocity data and their respective density. The compositional dependence of the ultrasonic velocities and related parameters are discussed to understand the rigidity and compactness of the glass system studied.

  18. Effect of ZnO and PbO/ZnO on structural and thermal properties of tellurite glasses

    International Nuclear Information System (INIS)

    Ramamoorthy, Raj Kumar; Bhatnagar, Anil K

    2015-01-01

    Highlights: • Structural units/linkages variation of TeO 2 -ZnO and TeO 2 -ZnO-PbO glasses was studied. • Structural arrangements of TeO 2 -ZnO glasses are rich in Te-O-Te network. • A mixture of Te-O-Te and Te-O-Pb networks is identified in TeO 2 -ZnO-PbO glasses. • Changes in thermal parameters T g and T o are correlated with the structural variations. • 15PbO and 20PbO samples of TeO 2 -ZnO-PbO glasses show large thermal stability. - Abstract: Two series of glasses, (100 − x)TeO 2 -xZnO (x = 20, 25, 30, 35) and 70TeO 2 -(30 − y)ZnO-yPbO (y = 5, 10, 15, 20), referred as TZ and TZP, respectively, were prepared by a melt quenching technique and characterized by X-ray diffraction (XRD), density, refractive index, Raman scattering and differential scanning calorimetry (DSC) to observe the changes in their properties as a function of ZnO and PbO/ZnO. Variations in individual structural units/linkages in these glasses are derived from the de-convoluted Raman spectra. The glass transition (T g ) and onset of crystallization (T o ) temperatures are determined from DSC isothermal scans. It is observed that the thermal stability (ΔT = T o − T g ) decreases for TZ glasses with increase in x, while it increases for TZP glasses with increase in y. Changes in thermal parameters of these glasses are correlated with the structural variation as a function of ZnO and PbO/ZnO ratio to determine the effect of substitution/addition of metal oxide, ZnO and PbO, to TeO 2 and TeO 2 -ZnO glasses

  19. Microwave and conventional preparation of Zinc borate glass: Eu3+ ion as luminescent probe

    International Nuclear Information System (INIS)

    Mandal, Ashis K.; Balaji, S.; Sen, Ranjan

    2014-01-01

    Highlights: • IR transparent Zinc borate glass is prepared using microwave heating. • Glass transition temperature of microwave melted glass is found higher than that of glass prepared in conventional melting. • Low OH concentration in glass can be prepared in microwave heating. • We report higher reduction of Eu 3+ to Eu 2+ in microwave processing of Zinc borate glass. - Abstract: Transparent Zinc borate glass is melted using microwave energy as an alternative heating route to conventional resistive heating. A comparative study of the properties of the glasses prepared by both the methods is conducted by adopting X-ray diffraction (XRD), Differential scanning calorimetry (DSC), UV–VIS–NIR spectroscopy, Fourier transform infrared (FTIR) spectroscopy, Refractive Indices (RI). Amorphous nature of samples is confirmed by X-ray diffraction study. Glass transition temperature (T g ) of microwave melted glass is found ∼7–9 °C higher than that of glass prepared in conventional melting. OH content is found less than 250 ppm in microwave melted glass whereas it is above 330 ppm in conventional melted glasses. Photoluminescence study of Eu 2 O 3 doped glass prepared in microwave heating indicates higher reduction of Eu 3+ → Eu 2+ than the glass melted in conventional route. Thus, microwave processing can be an alternative energy efficient, time saving, environmental friendly glass preparation method

  20. Thermal stability and Judd-Ofelt analysis of optical properties of Sm3+-doped sodium tellurite glasses

    Science.gov (United States)

    Mawlud, Saman Q.; Ameena, Mudhafar M.; Sahar, Md. Rahim; Mahraz, Zahra A. Said; Ahmed, Kasim Fawzy

    2017-09-01

    Series of glasses based on (70-x) TeO2 - 20Na2O - xSm2O3 (x=0, 0.3, 0.6, 1, 1.2, 1.5 mol%) have been prepared using melt-quenching technique. The nature of the glass has been confirmed using X-ray diffraction; it is found that the glass samples are amorphous in nature. The thermal stability of the glass has been determined by means of Differential Thermal Analysis (DTA). From the DTA curve, the glass transition temperature (Tg), crystallization temperature (Tc) and melting temperature (Tm) have been identified and thermal stability is also calculated. The absorption properties of these samples are obtained by using UV-Visible-NIR spectrometer, the recorded absorption spectra exhibit nine absorption transition bands peaks corresponding to the transitions from ground level 6H5/2→6P3/2, 4I11/2, 6F11/2, 6F9/2, 6F7/2, 6F5/2, 6F3/2, 6H15/2 and 6F1/2. The emission characteristic of this glass is characterized using Photoluminescence (PL) spectroscopy at excited wavelength 404 nm, the emission spectra consisted of four emission bands at 561.95 nm, 598.69 nm, 643.77 nm and 704.56 nm which were assigned as a transition 4G5/2→6H5/2, 6H7/2, 6H9/2 and 6H11/2 respectively. From f-f intensity model the experimental oscillator strengths, fexp and theoretical oscillator strength fcal were calculated. Using Judd-Ofelt theory and fit process of least square, the phenomenological intensity parameters Ωλ (λ=2,4,6) were obtained, In order to evaluate potential applications of Sm3+ ions in telluride glasses, the spectroscopic parameters: transition probability AR, branching ratio Br, radiative life time τr, emission pick cross section σλ for each band were calculated. The comparative studies with other Sm3+ doped different glasses showed that present glasses could be a potential candidate for lasers.

  1. Single- and double energy N{sup +} ion irradiated planar optical waveguides in Er: Tungsten–tellurite oxide glass and sillenite type Bismuth Germanate crystals working up to telecommunications wavelengths

    Energy Technology Data Exchange (ETDEWEB)

    Bányász, I., E-mail: banyasz@sunserv.kfki.hu [Department of Crystal Physics, Wigner Research Centre for Physics, Hungarian Academy of Sciences, P.O. Box 49, H-1525 Budapest (Hungary); Zolnai, Z.; Fried, M.; Lohner, T. [Research Institute for Technical Physics and Materials Science, Research Centre for Natural Sciences, Hungarian Academy of Sciences, P.O. Box 49, H-1525 Budapest (Hungary); Berneschi, S.; Righini, G.C. [MDF-Lab, “Nello Carrara” Institute of Applied Physics, IFAC-CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino (Italy); “Enrico Fermi” Center for Study and Research, Piazza del Viminale 2, 00184 Roma (Italy); Pelli, S.; Nunzi-Conti, G. [MDF-Lab, “Nello Carrara” Institute of Applied Physics, IFAC-CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino (Italy)

    2013-07-15

    Ion implantation proved to be a universal technique for producing waveguides in most optical materials. Tellurite glasses are good hosts of rare-earth elements for the development of fibre and integrated optical amplifiers and lasers covering all the main telecommunication bands. Er{sup 3+}-doped tellurite glasses are good candidates for the fabrication of broadband amplifiers in wavelength division multiplexing around 1.55 μm, as they exhibit large stimulated cross sections and broad emission bandwidth. Fabrication of channel waveguides in such a material via N{sup +} ion implantation was reported recently. Sillenite type Bismuth Germanate (BGO) crystals are good nonlinear optical materials. Parameters of waveguide fabrication in both materials via implantation of MeV-energy N{sup +} ions were optimized. First single-energy implantations at 3.5 MeV at various fluences were applied. Waveguide operation up to 1.5 μm was observed in both materials. Then double-energy implantations at a fixed upper energy of 3.5 MeV and lower energies between 2.5 and 3.1 MeV were performed to suppress leaky modes by increasing barrier width. Improvement of waveguide characteristics was found by m-line spectroscopy and spectroscopic ellipsometry.

  2. Red, green, blue and white light upconversion emission in Yb3+/Tm3+/Ho3+ co-doped tellurite glasses

    International Nuclear Information System (INIS)

    Desirena, H; De la Rosa, E; Meza, O; Salas, P

    2011-01-01

    Several Yb 3+ /Tm 3+ /Ho 3+ co-doped transparent TeO 2 -ZnO-Na 2 O-Yb 2 O 3 -Ho 2 O 3 -Tm 2 O 3 glasses were prepared and luminescence properties were characterized. Simultaneous red, green and blue (RGB) emission were obtained after excitation at 970 nm. Colour emission was tuned from multicolour to white light with colour coordinate (0.32, 0.33) matching very well with the white reference (0.33, 0.33). Changes in colour emission were obtained by varying the intensity ratios between RGB bands that are strongly concentration dependent because of the interaction of co-dopants. The colour tunability, high quality of white light and high intensity of the emitted signal make these transparent glasses excellent candidates for applications in solid-state lighting.

  3. Near infrared and upconversion luminescence behaviour of Er{sup 3+}/Yb{sup 3+} codoped boro-tellurite glasses

    Energy Technology Data Exchange (ETDEWEB)

    Maheshvaran, K. [Department of Physics, Gandhigram Rural Institute - Deemed University, Gandhigram - 624302, India and Department of Physics, K.S. Rangasamy College of Technology, Trichengode - 637215 (India); Arunkumar, S., E-mail: mari-ram2000@yahoo.com; Vijayakumar, R., E-mail: mari-ram2000@yahoo.com; Marimuthu, K., E-mail: mari-ram2000@yahoo.com [Department of Physics, Gandhigram Rural Institute − Deemed University, Gandhigram - 624302 (India)

    2014-04-24

    The broadband NIR and upconversion luminescence behavior in a new series of Er{sup 3+}/Yb{sup 3+} codoped TeO{sub 2}-B{sub 2}O{sub 3}-SrO-BaO-Li{sub 2}O-LiF glasses have been studied exciting at a wavelength of 980 nm using semiconductor laser. A broadband emission is observed from 1450 to 1650 nm with a full width at half maximum (FWHM) around 165 nm in 0.5wt% Yb{sup 3+} ion content E0.5YLTB glass. The radiative parameters such as transition probability (A), stimulated emission cross-section (σ{sup E}), experimental and calculated branching ratios (β{sub R}), optical gain width (σ{sub p}×FWHM) and radiative lifetime (τ{sub cal}) have been calculated for the {sup 4}I{sub 13/2}→{sup 4}I{sub 15/2} NIR emission. Upconversion luminescence spectra of the prepared glasses have been studied and the ESA and ET processes have also been discussed and reported.

  4. Structural, thermal, and optical properties of Er3+/Yb3+ co-doped oxyhalide tellurite glasses, glass-ceramics and ceramics

    International Nuclear Information System (INIS)

    Joshi, C.; Rai, R.N.; Rai, S.B.

    2012-01-01

    Glass-ceramics and ceramics containing nano-crystals of different phases doped with Er 3+ /Yb 3+ ions have been successfully prepared by heat treatment of the precursor oxyhalide glasses synthesized by the melt-quench method. X-ray diffraction patterns and transmission electron microscopy (TEM) images verify the precipitation of nano-crystals. Emission of Er 3+ enhances several times when Yb 3+ ion is added with the matrix. The Stark splitting and the intensity of different emission bands increase to a great extent when we approach to ceramics from glasses via glass-ceramics. The intensity of the blue and green emission bands increases much faster than the red and NIR emission bands. Intense upconversion emission observed by the naked eye has been quantified in terms of standard chromaticity diagram (CIE). Power dependence study shows that the upconversion of NIR radiation to visible radiation takes place mainly via photon avalanche (PA) process.

  5. Tellurite Composite Microstructured Optical Fibers with Tailored Chromatic Dispersion for Nonlinear Applications

    Science.gov (United States)

    Duan, Zhongchao; Liao, Meisong; Yan, Xin; Kito, Chihiro; Suzuki, Takenobu; Ohishi, Yasutake

    2011-07-01

    We report the fabrication of tellurite composite microstructured optical fibers (CMOFs) which consist of a TeO2-Li2O-WO3-MoO3-Nb2O5 (TLWMN) tellurite glass core and TeO2-ZnO-Na2O-La2O3 (TZNL) tellurite glass cladding. Flattened chromatic dispersion and tunable zero dispersion wavelength (ZDW) were realized in the small core diameter (˜1.5 µm) fiber with six surrounding air holes. The optical loss was measured to be about 4.0 dB/m in the spectral range of 1510-1640 nm. Supercontinuum (SC) generation was demonstrated by a femtosecond laser pumping at 1.55 µm. The threshold pump power for this novel tellurite CMOF was the lowest among tellurite microstructured optical fibers (MOFs).

  6. The structural analysis of zinc borate glass by laboratory EXAFS and X-ray diffraction measurements

    International Nuclear Information System (INIS)

    Kajinami, Akihiko; Harada, Yasushi; Inoue, Shinsuke; Deki, Shigehito; Umesaki, Norimasa

    1999-01-01

    The structure of zinc borate glass has been investigated by laboratory EXAFS and X-ray diffraction measurement as preliminary investigations for the detailed study in SPring-8. The zinc borate glass was prepared in the range from 40 to 65 mol% of zinc oxide content. The X-ray diffraction was measured by horizontal θ-θ goniometer with 60 kV and 300 mA output of Mo target. The EXAFS of zinc borate glass was measured by laboratory EXAFS system with 20 kV, 100 mA output of Mo target for the K absorption edge of zinc atom. From the X-ray diffraction and the EXAFS measurements, it is found that the zinc ion is surrounded by four oxygen atoms and formed a tetrahedral structure whose (Zn-O) distance is about 2 A and that the structure is unchanged with the zinc oxide content. The diffraction data show that the neighboring structure of boron atom transforms from BO 4 tetrahedra to BO 3 tetragonal planar structure with increasing of the zinc oxide content. (author)

  7. Structural characterization of hog iron oxide content glasses obtained from zinc hydrometallurgy wastes

    International Nuclear Information System (INIS)

    Romero, M.; Rincon, J.M.; Musik, S.; Kozhujharov, W.

    1997-01-01

    It has been carried out the structural characterization of high oxide content glasses obtained by melting of a goethite industrial waste from the zinc hydrometallurgy with other raw materials as dolomite and glass cullet. The structural characterization has been carried out by X-ray Diffraction (XRD), X-Ray Diffraction by Amorphous Dispersion (RDF) and Mossbauer spectroscopy. It has been determined the interatomic distance, the oxidation state and the coordination of iron atoms in these glasses. (Author) 16 refs

  8. Magnetic properties of bioactive glass-ceramics containing nanocrystalline zinc ferrite

    International Nuclear Information System (INIS)

    Singh, Rajendra Kumar; Srinivasan, A.

    2011-01-01

    Glass-ceramics with finely dispersed zinc ferrite (ZnFe 2 O 4 ) nanocrystallites were obtained by heat treatment of x(ZnO,Fe 2 O 3 )(65-x)SiO 2 20(CaO,P 2 O 5 )15Na 2 O (6≤x≤21 mole%) glasses. X-ray diffraction patterns of the glass-ceramic samples revealed the presence of calcium sodium phosphate [NaCaPO 4 ] and zinc ferrite [ZnFe 2 O 4 ] as major crystalline phases. Zinc ferrite present in nanocrystalline form contributes to the magnetic properties of the glass-ceramic samples. Magnetic hysteresis cycles of the glass-ceramic samples were obtained with applied magnetic field sweeps of ±20 kOe and ±500 Oe, in order to evaluate the potential of these glass-ceramics for hyperthermia treatment of cancer. The evolution of magnetic properties in these samples, viz., from a partially paramagnetic to fully ferrimagnetic nature has been explored using magnetometry and X-ray diffraction studies. - Research highlights: → The glass-ceramics contain bone mineral and magnetic phases. → Calcium sodium phosphate and zinc ferrite nanocrystallites have been identified in all the sample. → With an increase in ZnO and Fe2O3 content, magnetic property of samples evolved from partially paramagnetic to fully ferrimagnetic nature. → Large magnetic hysteresis loops have been obtained for samples with high ZnO+Fe2O3 content.

  9. The peculiarity of the formation of zinc films on a glass substrate

    Energy Technology Data Exchange (ETDEWEB)

    Tomaev, V. V., E-mail: tvaza@mail.ru [Saint Petersburg State University, 198504, Russia, Saint-Petersburg, Petrodvorets, Universitetskii pr. 26 (Russian Federation); Saint Petersburg Mining University, Russia, 199106, St. Petersburg, V.O., 21-st line, 2 (Russian Federation); Polishchuk, V. A., E-mail: vpvova2010@yandex.ru [St. Petersburg University of Information Technologies, Mechanics, and Optics, 197101, Russia, St. Petersburg, Kronverksky Pr., 49 (Russian Federation); Borisov, E. N., E-mail: enbor@bk.ru [Saint Petersburg State University, 198504, Russia, Saint-Petersburg, Petrodvorets, Universitetskii pr. 26 (Russian Federation)

    2016-06-17

    Thin Nanocrystalline films of the zinc have been fabricated by thermal spraying on the glass substrate. Morphologies and structure of the films had been investigated by the methods X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). It is found that the surface of the films has a different types of the nanocrystals zinc. Were detected intergrowths of two or more the nanocrystals, hexagonal shape. Using the theory of homogeneous and heterogeneous nucleation of a new phase, had been evaluated the geometrical and thermodynamic parameters nanocrystals zinc.

  10. Mechanical Coating of Zinc Particles with Bi2O3-Li2O-ZnO Glasses as Anode Material for Rechargeable Zinc-Based Batteries

    Directory of Open Access Journals (Sweden)

    Tobias Michlik

    2018-02-01

    Full Text Available The electrochemical performance of zinc particles with 250 μm and 30 μm diameters, coated with Bi2O3-Li2O-ZnO glass is investigated and compared with noncoated zinc particles. Galvanostatic investigations were conducted in the form of complete discharge and charging cycles in electrolyte excess. Coated 30 μm zinc particles provide the best rechargeability after complete discharge. The coatings reached an average charge capacity over 20 cycles of 113 mAh/g compared to the known zero rechargeability of uncoated zinc particles. Proposed reasons for the prolonged cycle life are effective immobilization of discharge products in the glass layer and the formation of percolating metallic bismuth and zinc phases, forming a conductive network through the glass matrix. The coating itself is carried out by mechanical ball milling. Different coating parameters and the resulting coating quality as well as their influence on the passivation and on the rechargeability of zinc–glass composites is investigated. Optimized coating qualities with respect to adhesion, homogeneity and compactness of the glass layer are achieved at defined preparation conditions, providing a glass coating content of almost 5 wt % for 250 μm zinc particles and almost 11 wt % for 30 μm zinc particles.

  11. Infrared spectra of zinc doped lead borate glasses

    Indian Academy of Sciences (India)

    Unknown

    size, smaller heat of fusion and valence (= 3) of B. In ... of amorphous materials, we have used it to determine the structure ... 1073 K. The homogenized molten glass was cast in two ... ing the glass, all the samples were immediately transferred.

  12. Viscosity and Softening Behavior of Alkali Zinc Sulfophosphate Glasses

    DEFF Research Database (Denmark)

    Da, Ning; Krolikowski, Sebastian; Nielsen, Karsten Hansgaard

    2010-01-01

    We report on the softening properties and viscosity of glasses from the system ZnO-Na2O-SO3-P2O5 for low-temperature sealing applications. Up to a ratio of network-forming ions PO(4)3-:SO(4)2- of about 2:1, a gradual substitution of P2O5 by SO3 results in decreasing glass transition and softening...

  13. Spectroscopic studies of copper doped alkaline earth lead zinc phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Sastry, S. Sreehari, E-mail: sreeharisastry@yahoo.com [Department of Physics, Acharya Nagarjuna University, Nagarjunanagar 522510 (India); Rao, B. Rupa Venkateswara [Department of Physics, Acharya Nagarjuna University, Nagarjunanagar 522510 (India); Department of Physics, V.R. Siddhartha Engineering College, Vijayawada 52007 (India)

    2014-02-01

    In this paper spectroscopic investigation of Cu{sup 2+} doped alkaline earth lead zinc phosphate glasses was done through the spectroscopic techniques like X-ray diffraction, Ultra Violet (UV) absorption Spectroscopy, Electron Paramagnetic Resonance (EPR – X band), Fourier Transform Infra Red (FTIR) and Raman Spectroscopy. Alkaline earth lead zinc phosphate glasses containing 0.1% copper oxide (CuO) were prepared by the melt quenching technique. Spectroscopic studies indicated that there is a greater possibility for the copper ions to exist in Cu{sup 2+} state in these glasses. The optical absorption spectra indicated that the absorption peak of Cu{sup 2+} is a function of composition. The maxima absorption peak was reported at 862 nm for strontium lead zinc phosphate glass. Bonding parameters were calculated for the optical and EPR data. All these spectral results indicated clearly that there are certain structural changes in the present glass system with different alkaline earth contents. The IR and Raman spectra noticed the breaking of the P–O–P bonds and creating more number of new P–O–Cu bonds.

  14. Spectroscopic studies of copper doped alkaline earth lead zinc phosphate glasses

    International Nuclear Information System (INIS)

    Sastry, S. Sreehari; Rao, B. Rupa Venkateswara

    2014-01-01

    In this paper spectroscopic investigation of Cu 2+ doped alkaline earth lead zinc phosphate glasses was done through the spectroscopic techniques like X-ray diffraction, Ultra Violet (UV) absorption Spectroscopy, Electron Paramagnetic Resonance (EPR – X band), Fourier Transform Infra Red (FTIR) and Raman Spectroscopy. Alkaline earth lead zinc phosphate glasses containing 0.1% copper oxide (CuO) were prepared by the melt quenching technique. Spectroscopic studies indicated that there is a greater possibility for the copper ions to exist in Cu 2+ state in these glasses. The optical absorption spectra indicated that the absorption peak of Cu 2+ is a function of composition. The maxima absorption peak was reported at 862 nm for strontium lead zinc phosphate glass. Bonding parameters were calculated for the optical and EPR data. All these spectral results indicated clearly that there are certain structural changes in the present glass system with different alkaline earth contents. The IR and Raman spectra noticed the breaking of the P–O–P bonds and creating more number of new P–O–Cu bonds

  15. Optical Characterization of Zinc Modified Bismuth Silicate Glasses

    Directory of Open Access Journals (Sweden)

    Rajesh Parmar

    2015-01-01

    Full Text Available The optical characterization of glass samples in the system 40SiO2 · xZnO · (60-xBi2O3 with x=0, 5, 10, 15, 20, 25, 30, 35, and 40 prepared by conventional melt-quench technique has been carried out in the light of Hydrogenic Excitonic Model (HEM. The absorption coefficient spectra show good agreement with theoretical HEM for the present glass system and the values of different parameters like Eg, R, Γ1, Γc, and Co have been estimated from fitting of this model. The values of energy band gap estimated from fitting of HEM with experimental data are in good agreement with those obtained from Tauc’s plot for direct transitions. The band gap energy is found to increase with increase of ZnO content. The decrease in values of Urbach energy with increase in ZnO content indicates a decrease in defect concentration in the glass matrix on addition of ZnO content. Optical constants n and k obey k-k consistency and the dielectric response of the studied glass system is similar to that obtained for Classical Electron Theory of Dielectric Materials. The calculated values of the metallization criterion (M show that the synthesized glasses may be good candidates for new nonlinear optical materials.

  16. Raman and DSC studies of fragility in tellurium-zinc oxide glass formers

    International Nuclear Information System (INIS)

    Stavrou, Elissaios; Kripotou, Sotiria; Raptis, Constantine; Turrell, Sylvia; Syassen, Karl

    2011-01-01

    Raman scattering and differential scanning calorimetry (DSC) measurements have been carried out in four mixed (TeO 2 ) 1-x (ZnO) x (x = 0.1, 0.2, 0.3, 0.4) glasses at high temperatures (Raman and DSC through the glass transition) and high pressures (Raman) with the aim of determining the fragility of these glass forming oxides. Four different criteria, corresponding to four parameters, were applied to assess the fragility of the glasses. From the DSC studies, we have obtained the fragility parameter m which corresponds to the slopes of Arrhenius (lnQ vs. 1/T g , were Q is the heating rate) plots, and the glass transition width ΔT g . Also, from the low-frequency Raman scattering, and in particular the boson peak intensity of the glasses at T g , we have estimated the fragility ratio r R (T g ) = I min /I max whose value serves as another (empirical) fragility criterion. Finally, from high pressure Raman measurements on the glasses, we have estimated the Grueneisen parameter γ T for each glass, which constitutes the fourth fragility parameter adopted in this work. Considering the four parameters ΔT g , m, r (T g ) and γ T and the generally accepted (empirical) fragility criteria, we conclude that the mixed tellurium-zinc oxides constitute strong-to-intermediate glass formers (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  17. Optical basicity and electronic polarizability of zinc borotellurite glass doped La3+ ions

    Directory of Open Access Journals (Sweden)

    M.K. Halimah

    Full Text Available Zinc borotellurite glasses doped with lanthanum oxide were successfully prepared through melt-quenching technique. The amorphous nature of the glass system was validated by the presence of a broad hump in the XRD result. The refractive index of the prepared glass samples was calculated by using the equation proposed by Dimitrov and Sakka. The theoretical value of molar refraction, electronic polarizability, oxide ion polarizability and metallization criterion were calculated by using Lorentz-Lorenz equation. Meanwhile, expression proposed by Duffy and Ingram for the theoretical value of optical basicity of multi-component glasses were applied to obtain energy band gap based optical basicity and refractive index based optical basicity. The optical basicity of prepared glasses decreased with the increasing concentration of lanthanum oxide. Metallization criterion on the basis of refractive index showed an increasing trend while energy band gap based metallization criterion showed a decreasing trend. The small metallization criterion values of the glass samples represent that the width of the conduction band becomes larger which increase the tendency for metallization of the glasses. The results obtained indicates that the fabricated glasses have high potential to be applied on optical limiting devices in photonic field. Keywords: Borotellurite glasses, Refractive index, Electronic polarizability, Oxide ion polarizability, Optical basicity, Metallization criterion

  18. Red light emission from europium doped zinc sodium bismuth borate glasses

    Science.gov (United States)

    Hegde, Vinod; Viswanath, C. S. Dwaraka; Upadhyaya, Vyasa; Mahato, K. K.; Kamath, Sudha D.

    2017-12-01

    Zinc sodium bismuth borate (ZNBB) glasses doped with different concentrations of europium were prepared by conventional melt quenching method and characterized through the measurements of density, refractive index, X-ray diffraction (XRD), Fourier Transform Infrared (FTIR) spectra, optical absorption, luminescence and radiative lifetimes. FTIR spectra showed seven characteristic peaks of bismuth and borate functional groups in the range of 400-1600 cm-1. The optical band gap and bonding parameters have been calculated from absorption spectra. Photoluminescence spectra recorded in the visible region with 394 nm excitation are used to calculate the Judd-Ofelt (JO) intensity parameters (Ω2 and Ω4). The JO intensity parameters have been used to calculate the radiative parameters such as branching ratio (β), stimulated emission cross-section (σse), transition probability (A) for the fluorescent level of 5D0→7F2. Decay rates through single exponential are used to calculate the lifetime (τm) of the meta-stable state 5D0 of (Eu3+ ion) these glasses. The radiative parameters measured for all these glasses show 0.7 mol% europium doped zinc sodium bismuth borate glass 5D0→7F2 transition has the potential for red laser applications. The quality of the colour emitted by the present glasses are estimated quantitatively by CIE chromaticity coordinates, which confirms the suitability of these glasses as a red emitting material for field emission technologies and LEDs.

  19. Propriedades estruturais e térmicas de vidros teluretos 20Li2O-80TeO2 Structural and thermal properties of tellurite 20Li2O-80TeO2 glasses

    Directory of Open Access Journals (Sweden)

    E. Idalgo

    2007-09-01

    Full Text Available O presente trabalho reporta estudos sobre a cristalização em vidros teluretos 20Li2O-80TeO2 induzida a partir de tratamentos térmicos realizados sobre vidros com tamanho de partículas entre 38 µm e 75 µm. Estes estudos foram conduzidos em duas matrizes vítreas tratadas e não tratadas termicamente para aliviar as tensões após o quenching, utilizando-se de forma combinada às técnicas de difração de raios X, calorimetria diferencial de varredura e espectroscopia no infravermelho. Os resultados revelaram a presença de três fases cristalinas distintas durante o processo de cristalização e apontaram para uma hierarquia tal que as fases alfa-TeO2 e gama-TeO2 cristalizam-se antecipadamente à fase Li2Te2O5 no vidro 20Li2O-80TeO2 sujeito a tensões mecânicas induzidas durante a síntese. No vidro 20Li2O-80TeO2, livre de tensões mecânicas, não foi possível discriminar esta hierarquia de cristalização.This work report crystallization studies on tellurite 20Li2O-80TeO2 glasses induced from heat thermal annealing on glasses with particle size between 38 µm and 75 µm. These studies were conducted on two glass matrix heat thermal annealed and non-annealed to remove the stress after the quenching, by using the X-Ray diffraction analysis, Fourier transform infrared spectroscopy and differential scanning calorimetry techniques. The results shown the presence of three distinct crystalline alpha-TeO2, gamma-TeO2 and Li2Te2O5 phases during the crystallization process, suggesting a crystallization hierarchy on the glass matrix under stress, since the gamma-TeO2 and alpha-TeO2 phases crystallization occurs before the Li2Te2O5 phase. On the glass stress free, this crystallization hierarchy was not clearly determined.

  20. Experimental and theoretical approach on the optical properties of zinc borotellurite glass doped with dysprosium oxide

    Science.gov (United States)

    Halimah, M. K.; Ami Hazlin, M. N.; Muhammad, F. D.

    2018-04-01

    A series of glass samples with chemical formula {[(TeO2)0.7(B2O3)0.3]0.7(ZnO)0.3}1 - x(Dy2O3)x where x = 0.01, 0.02, 0.03, 0.04 and 0.05 M fraction were synthesized through conventional melt-quenching method. The most common way to fabricate a glass material is by fusion of two or more component oxides followed by their quenching. This technique is known as melt-quenching technique. Kaur et al. (2016) [1] highlighted that the melt-quenching method able to enhance the mechanical properties like hardness and flexural strength of the material. The nature of the glass systems is proven to be amorphous based on the XRD pattern. The FTIR spectra of the glass systems confirm the existence of five bands which are assigned for the BO4, BO3, TeO4 and TeO3 vibrational groups. The density of the glass systems is increased with the addition of Dy2O3 while the molar volume is found to be inversely proportional to the density of the proposed glass. The optical properties of the glasses are determined through the absorption spectra obtained from the UV-VIS spectrophotometer. From the absorption spectra, the indirect and direct optical band gaps and the Urbach energy are found to be inversely proportional to each other. As the molar fraction of the Dy2O3 increased, the optical band gaps are observed to increase as opposed to the Urbach energy. For this glass system, the values of refractive index, electronic polarizability, oxide ion polarizability and the optical basicity are found to decrease as the addition of the dysprosium oxide is increased. From the emission spectra, two intense blue and yellow emission bands are observed, which correspond to the 4F9/2 → 6H15/2 and 4F9/2 → 6H13/2 transitions of Dy3 + ions respectively. The CIE chromaticity coordinates of the zinc borotellurite glass systems are found to be located in the white light region. Generation of white light The generation of the white light can be achieved by using two emission bands which comprise of the yellow

  1. Zinc

    Science.gov (United States)

    ... Consumer Datos en español Health Professional Other Resources Zinc Fact Sheet for Consumers Have a question? Ask ... find out more about zinc? Disclaimer What is zinc and what does it do? Zinc is a ...

  2. Effect of incorporation of zinc oxide nanoparticles on mechanical properties of conventional glass ionomer cements.

    Science.gov (United States)

    Panahandeh, Narges; Torabzadeh, Hassan; Aghaee, Mohammadamin; Hasani, Elham; Safa, Saeed

    2018-01-01

    The aim of this study is to investigate the physical properties of conventional and resin-modified glass ionomer cements (GICs) compared to GICs supplemented with zinc oxide (ZnO) nanofiller particles at 5% (w/w). In this in vitro study, ZnO nanoparticles of different morphologies (nanospherical, nanorod, and nanoflower) were incorporated to glass ionomer powder. The samples were subjected to the flexural strength ( n = 20) and surface hardness test ( n = 12) using a universal testing machine and a Vickers hardness machine, respectively. Surface analysis and crystal structure of samples were performed with scanning electron microscope and X-radiation diffraction, respectively. The data were analyzed using one-way ANOVA, Shapiro-Wilk, and Tukey's tests ( P glass ionomer containing nanoparticles was not significantly different from the control group ( P > 0.05). The surface hardness of the glass ionomer containing nanospherical or nanoflower ZnO was significantly lower than the control group ( P glass ionomer containing nanorod ZnO was not significantly different from the control group ( P = 0.868). Incorporation of nanospherical and nanoflower ZnO to glass ionomer decreased their surface hardness, without any changes on their flexural strength. Incorporation of nanorod ZnO particles caused no effect on the mechanical properties.

  3. Gamma radiation shielding and optical properties measurements of zinc bismuth borate glasses

    International Nuclear Information System (INIS)

    Yasaka, P.; Pattanaboonmee, N.; Kim, H.J.; Limkitjaroenporn, P.; Kaewkhao, J.

    2014-01-01

    Highlights: • 10ZnO:xBi 2 O 3 :(90−x)B 2 O 3 , (ZBB) glasses were prepared. • Radiation shielding and optical properties were investigated. • Higher 25 mol% of Bi 2 O 3 show better shielding property compared with concretes. • ZBB glasses can develop as a Pb-free radiation shielding material. - Abstract: In this work, the zinc bismuth borate (ZBB) glasses of the composition 10ZnO:xBi 2 O 3 :(90−x)B 2 O 3 (where x = 15, 20, 25 and 30 mol%) were prepared by the melt quenching technique. Their radiation shielding and optical properties were investigated and compared with theoretical calculations. The mass attenuation coefficients of ZBB glasses have been measured at different energies obtained from a Compton scattering technique. The results show a decrease of the mass attenuation coefficient, effective atomic number and effective electron density values with increasing of gamma-ray energies; and good agreements between experimental and theoretical values. The glass samples with Bi 2 O 3 concentrations higher than 25 mol% (25 and 30 mol%) were observed with lower mean free path (MFP) values than all the standard shielding concretes studied. These results are indications that the ZBB glasses in the present study may be developed as a lead-free radiation shielding material in the investigated energy range

  4. Concentration effect on the spectroscopic behavior of Tb3+ ions in zinc phosphate glasses

    International Nuclear Information System (INIS)

    Kesavulu, C.R.; Almeida Silva, Anielle Christine; Dousti, M.R.; Dantas, Noelio Oliveira; Camargo, A.S.S. de; Catunda, Tomaz

    2015-01-01

    Zinc phosphate glasses (PZABPTb) in the compositional system: P 2 O 5 –ZnO–Al 2 O 3 –BaO–PbO doped with variable Tb 3+ concentrations (1–5 wt% Tb 2 O 3 ) were prepared and characterized through absorption, excitation, emission and intensity decay rate measurements. The Judd–Ofelt model has been adopted to evaluate the radiative properties of the 5 D 4 → 7 F 6–3 emission transitions. The effect of Tb 3+ ion concentration on the emissions from the 5 D 3,4 excited levels is discussed in detail. Analysis of the intensity decay curves corresponding to blue and green emissions from levels 5 D 3 and 5 D 4 , respectively, allowed determination of effective lifetimes, which confirmed the Tb 3+ ion concentration quenching of the blue emission in these glasses. The decay curves for the 5 D 3 level are found to be non-exponential in nature for all the studied concentrations due to ion–ion energy transfer through cross-relaxation. In an attempt to identify the origin of the energy transfer mechanism, the decay curves were well fitted to the Inokuti–Hirayama model for S=6, which indicates that the energy transfer process is of dipole–dipole type. The optical band gap energy (E opt ) has been evaluated taking into account the ultraviolet edge of absorption spectra. - Highlights: • Tb 3+ -doped zinc phosphate glasses have been prepared by melt quenching technique. • Spectroscopic parameters were evaluated using the Judd–Ofelt theory. • Effects of Tb 3+ concentration on luminescence of the glasses were studied. • Strong intense laser transition for Tb 3+ ion in PZABPTb glasses is 5 D 4 → 7 F 5 (0.54 μm). • PZABPTb glasses could be used in the development of green color display devices and solid state visible lasers

  5. In vitro study of nano-sized zinc doped bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Goh, Yi-Fan; Alshemary, Ammar Z.; Akram, Muhammad [Department of Chemistry, Faculty of Science, Universiti Teknologi Malaysia, 81310 UTM skudai, Johor Darul Ta' zim (Malaysia); Abdul Kadir, Mohammed Rafiq [Medical Implant Technology Group, Faculty of Biomedical Engineering and Health Science, Universiti Teknologi Malaysia, 81310 UTMJohor Bahru (Malaysia); Hussain, Rafaqat, E-mail: rafaqat@kimia.fs.utm.my [IbnuSina Institute for Fundamental Science Studies, Universiti Teknologi Malaysia, 81310 UTM Johor Bahru, Johor DarulTa' zim (Malaysia)

    2013-01-15

    Surface reactivity in physiological fluid has been linked to bioactivity of a material. Past research has shown that bioactive glass containing zinc has the potential in bone regeneration field due to its enhanced bioactivity. However, results from literature are always contradictory. Therefore, in this study, surface reactivity of bioactive glass containing zinc was evaluated through the study of morphology and composition of apatite layer formed after immersion in simulated body fluid (SBF). Nano-sized bioactive glass with 5 and 10 mol% zinc were synthesized through quick alkali sol-gel method. The synthesized Zn-bioglass was characterized using field emission scanning electron microscope (FESEM), energy dispersive X-ray spectrometer (EDX), X-ray diffractometer (XRD) and Fourier transform infrared spectrometer (FTIR). Samples after SBF immersion were characterized using scanning electron microscope (SEM) and EDX. Morphological study through SEM showed the formation of spherical apatite particles with Ca/P ratio closer to 1.67 on the surface of 5 mol% Zn-bioglass. Whereas, the 10 mol% Zn-bioglass samples induced the formation of flake-like structure of calcite in addition to the spherical apatite particles with much higher Ca/P ratio. Our results suggest that the higher Zn content increases the bioactivity through the formation of bone-bonding calcite as well as the spherical apatite particles. -- Highlights: Black-Right-Pointing-Pointer Nano-sized bioactive glasses were synthesized through quick alkali sol-gel method. Black-Right-Pointing-Pointer 5 and 10 mol% Zn-bioglass induced the formation of spherical particles in SBF test. Black-Right-Pointing-Pointer 10 mol% Zn-bioglass also induced the formation of flake-like structure. Black-Right-Pointing-Pointer The flake-like structure is calcium carbonate; spherical particles are apatite. Black-Right-Pointing-Pointer High Zn contents negatively influence the chemical composition of the apatite layer.

  6. Preparation of Ho3+/Tm3+ Co-doped Lanthanum Tungsten Germanium Tellurite Glass Fiber and Its Laser Performance for 2.0 μm

    Science.gov (United States)

    Zhou, Dechun; Bai, Xuemei; Zhou, Hang

    2017-03-01

    Ho3+/Tm3+ co-doped 50TeO2-25GeO2-3WO3-5La2O3-3Nb2O5-5Li2O-9BaF2 glass fiber is prepared with the rod-tube drawing method of 15 μm core diameter and 125 μm inner cladding diameter applied in the 2.0 μm-infrared laser. The 2.0 μm luminescence properties of the core glass are researched and the fluorescence intensity variation for different Tm3+ doping concentration is systematically analyzed. The results show that the 2.0 μm luminescence of Ho3+ is greatly influenced by the doping concentration ratio of Ho3+ to Tm3+ and that the maximum fluorescence intensity of the core glass can be obtained and its emission cross section can reach 0.933 × 10-21 cm2 when the sensitized proportion of holmium to thulium is 0.3 to 0.7 (mol%). Simultaneously, the maximum phonon energy of the core glass sample is 753 cm-1, which is significantly lower than that of silicate, gallate and germanate glass and the smaller matrix phonon energy can be conductive to the increase 2.0 μm-band emission intensity. The continuous laser with the maximum laser output power of 0.993 W and 2051 nm -wavelength of 31.9%-slope efficiency is output within the 0.5 m glass fiber and the experiment adopts 1560 nm erbium-doped fiber laser(EDFL) as the pump source and the self-built all-fiber laser. Therefore, the glass fiber has excellent laser characteristics and it is suitable for the 2.0 μm-band laser.

  7. Structural and luminescence properties of Mn2+ ions doped calcium zinc borophosphate glasses

    International Nuclear Information System (INIS)

    Wan, Ming Hua; Wong, Poh Sum; Hussin, Rosli; Lintang, Hendrik O.; Endud, Salasiah

    2014-01-01

    Highlights: • FT-IR revealed that the network structures are from borate and phosphate network. • The PL spectrum exhibits a green emission band at 582 nm ( 4 T 1g → 6 A 1g ). • As the concentration of Mn 2+ ions is increased, the emission band had been red shifted. • These glasses are found to have potential applications as luminescent optical materials. - Abstract: Calcium zinc borophosphate glasses (CaZnBP) doped with various concentrations of Mn 2+ ions and borate and phosphate as variable were prepared using conventional melt quenching technique. The structure of obtained glasses were examined by means of use: X-ray diffraction (XRD) and fourier transform infrared (FT-IR). XRD analysis confirmed amorphous nature of glass samples. The FT-IR spectra reveals the presence of both borate and phosphate vibrational modes in the prepared glasses. The doping of Mn 2+ ions (2–10 mol%) shows no significant changes in the main IR vibrational bands. Optical properties were studied by measuring the near infrared photoluminescence (PL) spectra. CaZnBP glasses exhibited intense green emission peak (582 nm) (tetrahedral symmetry), which is assigned to a transition from the upper 4 T 1g → 6 A 1g ground state of Mn 2+ ions. As the concentration of Mn 2+ ions increases, the emission band increases from 582 nm to 650 nm and exhibited a red light emission (octahedral symmetry). The decay curves of 4 T 1g level were examined for all concentrations and the measured lifetimes are found to depend strongly on Mn 2+ concentrations. From the emission characteristic parameters of 6 A 1g (S) level, it shows that the CaZnBP glasses could have potential applications as luminescent optical materials, visible lasers and fluorescent display devices

  8. Fabrication of optical fiber of zinc tin borophosphate glass with zero photoelastic constant

    Science.gov (United States)

    Saitoh, Akira; Oba, Yuya; Takebe, Hiromichi

    2015-10-01

    An optical fiber made of zinc tin boro-phosphate glass having a zero photoelastic constant, good water durability, and excluding hazardous elements was drawn from a prepared preform for use in a fiber-type current sensor device. The proposed cladding compositions enable single-mode propagation for a wavelength of 1550 nm, which is estimated from the difference in the refractive index between the core and cladding compositions. The drawing conditions should be controlled since the multiple-component glass is very sensitive to changes in viscosity and crystal precipitation during the heat-treated stretching of the preform. The temperature dependence of viscosity in the core and cladding reveals the feasibility of drawing.

  9. Structural study and DC conductivity of vanadyl doped zinc lithium borate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Seema [Physics Department, Deenbandhu Chhotu Ram University of Science & Technology, Murthal-131039 (India); Physics Department, Baba Mast Nath University, Asthal Bohr, Rohtak-124001 (India); Khasa, S., E-mail: skhasa@rediff.com; Dahiya, M. S.; Yadav, Arti [Physics Department, Deenbandhu Chhotu Ram University of Science & Technology, Murthal-131039 (India); Agarwal, A. [Applied Physics Department, Guru Jambheshwar University of Science & Technology, Hisar-125001 (India); Dahiya, S. [Physics Department, Baba Mast Nath University, Asthal Bohr, Rohtak-124001 (India)

    2015-06-24

    Glasses with composition xZnO⋅(30 − x)⋅Li{sub 2}O⋅70B{sub 2}O{sub 3} containing 2 mol% of V{sub 2}O{sub 5} (x = 0, 2, 5, 7 and 10) were prepared by standard melt-quench technique. The amorphous nature of the glass samples was confirmed by using x-ray diffraction. The structural changes in these glasses have been investigated by employing IR spectroscopy in the mid-IR range. The infrared spectroscopic analysis confirms the presence of both triangular and tetraheldral coordinated boron units and absence of boroxol ring. It also shows that metal-oxide vibrations are present which are due to the bonding of lithium and zinc ions with oxygen. The dc conductivity was measured in the temperature range 353-523 K. The dc conductivity results show that conductivity decreases and activation energy increases when Li{sub 2}O is replaced by ZnO, keeping the concentration of B{sub 2}O{sub 3} constant. Decrease in conductivity and increase in activation energy shows that addition of ZnO to the glass matrix shows a “blocking effect” on the overall mobility of alkali ions, but at higher concentration the hopping effect was also observed.

  10. Effect of Erbium Nanoparticles on Optical Properties of Zinc Borotellurite Glass System

    Directory of Open Access Journals (Sweden)

    Azlan Muhammad Noorazlan

    2013-01-01

    Full Text Available Erbium nanoparticles (NPs doped zinc borotellurite glasses have been prepared by conventional melt-quenching technique with the chemical composition {[(TeO20.70(B2O30.30]1-x(ZnOx}1-y(Er3O2y (where y=0.005,0.01,0.02,0.03,0.04,0.05. The structural properties of the prepared glasses were determined via X-ray diffraction (XRD analysis and FTIR analysis. It was confirmed that the prepared glasses are amorphous. The bonding parameters of the glasses were analyzed by using FTIR analysis and were confirmed to be ionic in nature. The refractive index increases as the content of erbium NPs increases. The optical absorption spectra revealed that fundamental absorption edge shifts to longer wavelength as the content of erbium NPs increases. The value of band gap had been calculated and shown to be decreased with an increase content of erbium NPs. The Urbach energy was shown to be linearly increased with an increase content of erbium NPs oxides.

  11. Optical properties of zinc borotellurite glass doped with trivalent dysprosium ion

    Science.gov (United States)

    Ami Hazlin, M. N.; Halimah, M. K.; Muhammad, F. D.; Faznny, M. F.

    2017-04-01

    The zinc borotellurite doped with dysprosium oxide glass samples with chemical formula {[(TeO2) 0 . 7(B2O3) 0 . 3 ] 0 . 7(ZnO) 0 . 3 } 1 - x(Dy2O3)x (where x=0.01, 0.02, 0.03, 0.04 and 0.05 M fraction) were prepared by using conventional melt quenching technique. The structural and optical properties of the proposed glass systems were characterized by using X-ray diffraction (XRD) spectroscopy, Fourier Transform Infrared (FTIR) spectroscopy, and UV-VIS spectroscopy. The amorphous nature of the glass systems is confirmed by using XRD technique. The infrared spectra of the glass systems indicate three obvious absorption bands which are assigned to BO3 and TeO4 vibrational groups. Based on the absorption spectra obtained, the direct and indirect optical band gaps, as well as the Urbach energy were calculated. It is observed that both the direct and indirect optical band gaps increase with the concentration of Dy3+ ions. On the other hand, the Urbach energy is observed to decrease as the concentration of Dy3+ ions increases.

  12. Ho3+-Yb3+ codoped tellurite based glasses in visible lasers and optical devices: Judd-Ofelt analysis and frequency upconversion

    Science.gov (United States)

    Azam, Mohd; Rai, Vineet Kumar

    2017-04-01

    The optical absorption and frequency upconversion emission in the Ho3+/Yb3+ codoped TeO2-ZnO (TZ), TeO2-ZnO-WO3 (TZW) and TeO2-ZnO-WO3-TiO2 (TZWTi) glasses prepared by melting and quenching method has been studied. Judd-Ofelt theory has been used to calculate the Judd-Ofelt intensity parameters (Ω2, Ω4 and Ω6), transition probabilities, radiative lifetimes, absorption cross sections and the branching ratios. Upconversion (UC) emission bands centered at ∼ 549 nm, ∼658 nm and ∼754 nm are observed upon 980 nm excitation. On codoping with the Yb3+ ions at 3.0 mol% the upconversion emission intensity enhancement of about ∼57 times, ∼342 times and ∼480 times for the green band whereas for the red band arising from the Ho3+ ions it is about ∼71 times, ∼438 times and ∼707 times respectively have been observed. The enhancement observed in the UC emission intensity is explained on the basis of efficient energy transfer from Yb3+ to Ho3+, larger absorption cross section, larger oscillator strengths and increase in the local field corrections factor. The spectroscopic quality factor Ω4/Ω6 has been calculated to get the information about the developed materials for laser applications. The upconversion emission cross section determined on the basis of Judd-Ofelt analysis is found to be maximum for Ho-Yb-TZWTi glass. The nephelauxetic ratio, bonding and covalency parameters have been calculated to know the nature of bonding between the rare earth ions and neighbouring oxygen atoms. The high color purity 83.8% has been reported in the codoped glasses at ∼81.2 W/cm2 pump power density.

  13. Concentration effect on the spectroscopic behavior of Tb{sup 3+} ions in zinc phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Kesavulu, C.R., E-mail: crkesavulu2005@gmail.com [Instituto de Fisica de São Carlos, Universidade de São Paulo, Avenida Trabalhador Sãocarlense 400, São Carlos, SP (Brazil); Almeida Silva, Anielle Christine [Laboratorio de Novos Materials Isolantes e Semicondutores (LNMIS), Instituto de Física, Universidade Federal de Uberândia, MG (Brazil); Dousti, M.R. [Instituto de Fisica de São Carlos, Universidade de São Paulo, Avenida Trabalhador Sãocarlense 400, São Carlos, SP (Brazil); Dantas, Noelio Oliveira [Laboratorio de Novos Materials Isolantes e Semicondutores (LNMIS), Instituto de Física, Universidade Federal de Uberândia, MG (Brazil); Camargo, A.S.S. de; Catunda, Tomaz [Instituto de Fisica de São Carlos, Universidade de São Paulo, Avenida Trabalhador Sãocarlense 400, São Carlos, SP (Brazil)

    2015-09-15

    Zinc phosphate glasses (PZABPTb) in the compositional system: P{sub 2}O{sub 5}–ZnO–Al{sub 2}O{sub 3}–BaO–PbO doped with variable Tb{sup 3+} concentrations (1–5 wt% Tb{sub 2}O{sub 3}) were prepared and characterized through absorption, excitation, emission and intensity decay rate measurements. The Judd–Ofelt model has been adopted to evaluate the radiative properties of the {sup 5}D{sub 4}→{sup 7}F{sub 6–3} emission transitions. The effect of Tb{sup 3+} ion concentration on the emissions from the {sup 5}D{sub 3,4} excited levels is discussed in detail. Analysis of the intensity decay curves corresponding to blue and green emissions from levels {sup 5}D{sub 3} and {sup 5}D{sub 4}, respectively, allowed determination of effective lifetimes, which confirmed the Tb{sup 3+} ion concentration quenching of the blue emission in these glasses. The decay curves for the {sup 5}D{sub 3} level are found to be non-exponential in nature for all the studied concentrations due to ion–ion energy transfer through cross-relaxation. In an attempt to identify the origin of the energy transfer mechanism, the decay curves were well fitted to the Inokuti–Hirayama model for S=6, which indicates that the energy transfer process is of dipole–dipole type. The optical band gap energy (E{sub opt}) has been evaluated taking into account the ultraviolet edge of absorption spectra. - Highlights: • Tb{sup 3+}-doped zinc phosphate glasses have been prepared by melt quenching technique. • Spectroscopic parameters were evaluated using the Judd–Ofelt theory. • Effects of Tb{sup 3+} concentration on luminescence of the glasses were studied. • Strong intense laser transition for Tb{sup 3+} ion in PZABPTb glasses is {sup 5}D{sub 4}→{sup 7}F{sub 5} (0.54 μm). • PZABPTb glasses could be used in the development of green color display devices and solid state visible lasers.

  14. Influence of silver and copper doping on luminescent properties of zinc-phosphate glasses after x-ray irradiation

    Science.gov (United States)

    Murashov, Alexander A.; Sidorov, Alexander I.; Shakhverdov, Teimur A.; Stolyarchuk, Maxim V.

    2017-11-01

    It is shown, experimentally, that in silver- and copper-containing zinc-phosphate glasses, metal molecular clusters are formed during the glass synthesis. X-ray irradiation of these glasses led to the considerable increase of its luminescence in visible spectral range. This effect is caused by the transformation of the charged metal molecular clusters into the neutral state. Luminescence and excitation spectra of the glass, doped with silver and copper simultaneously, change significantly in comparison with the spectra of glasses doped with one metal. The reason for this can be the formation of hybrid AgnCum molecular clusters. The computer simulation of the structure and optical properties of such clusters by the time-dependent density functional theory method is presented. It is shown that the optimal luminescent material for photonics application, in comparison with other studied materials, is glass, containing hybrid molecular clusters.

  15. Thermo-physical and structural studies of sodium zinc borovanadate glasses in the region of high concentration of modifier oxides

    Energy Technology Data Exchange (ETDEWEB)

    Chethana, B.K. [Solid State and Structural Chemistry Unit, Indian Institute of Science, Bangalore 560 012 (India); Reddy, C. Narayana [Maharani' s Science College for Women, Bangalore 560 001 (India); Rao, K.J., E-mail: kalyajrao@yahoo.co.in [Solid State and Structural Chemistry Unit, Indian Institute of Science, Bangalore 560 012 (India)

    2012-07-15

    Highlights: ► Highly modified sodium zinc borovanadate glasses. ► Structural model for borovanadate glasses. ► Network forming tendency of ZnO in borovanadate glasses. ► Fragility can be limited to NBO concentration in borovanadate glasses. -- Abstract: This paper reports investigation of Na{sub 2}O and ZnO modified borovanadate glasses in the highly modified regime of compositions. These glasses have been prepared by microwave route. Ultraviolet (UV) and visible, infrared (IR), Magic Angle Spinning Nuclear Magnetic Resonance (MAS NMR) and Electron Paramagnetic Resonance (EPR) spectroscopies have been used to characterize the speciation in the glasses. Together with the variation of properties such as molar volume and glass transition temperatures, spectroscopic data indicate that at high levels of modification, ZnO tends to behave like network former. It is proposed that the observed variation of all the properties can be reasonably well understood with a structural model. The model considers that the modification and speciation in glasses are strongly determined by the hierarchy of group electronegativities. Further, it is proposed that the width of the transitions of glasses obtained under same condition reflects the fragility of the glasses. An empirical expression has been suggested to quantify fragility on the basis of width of the transition regions.

  16. Role of glass structure in defining the chemical dissolution behavior, bioactivity and antioxidant properties of zinc and strontium co-doped alkali-free phosphosilicate glasses.

    Science.gov (United States)

    Kapoor, Saurabh; Goel, Ashutosh; Tilocca, Antonio; Dhuna, Vikram; Bhatia, Gaurav; Dhuna, Kshitija; Ferreira, José M F

    2014-07-01

    We investigated the structure-property relationships in a series of alkali-free phosphosilicate glass compositions co-doped with Zn(2+) and Sr(2+). The emphasis was laid on understanding the structural role of Sr(2+) and Zn(2+) co-doping on the chemical dissolution behavior of glasses and its impact on their in vitro bioactivity. The structure of glasses was studied using molecular dynamics simulations in combination with solid state nuclear magnetic resonance spectroscopy. The relevant structural properties are then linked to the observed degradation behavior, in vitro bioactivity, osteoblast proliferation and oxidative stress levels. The apatite-forming ability of glasses has been investigated by X-ray diffraction, infrared spectroscopy and scanning electron microscopy-energy-dispersive spectroscopy after immersion of glass powders/bulk in simulated body fluid (SBF) for time durations varying between 1h and 14 days, while their chemical degradation has been studied in Tris-HCl in accordance with ISO 10993-14. All the glasses exhibit hydroxyapatite formation on their surface within 1-3h of their immersion in SBF. The cellular responses were observed in vitro on bulk glass samples using human osteosarcoma MG63 cell line. The dose-dependent cytoprotective effect of glasses with respect to the concentration of zinc and strontium released from the glasses is also discussed. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  17. Structural and luminescence properties of Mn{sup 2+} ions doped calcium zinc borophosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Wan, Ming Hua, E-mail: wanminghua819@gmail.com [Phosphor Research Group, Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Skudai 81310, Johor (Malaysia); Wong, Poh Sum, E-mail: pohsumwong@gmail.com [Phosphor Research Group, Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Skudai 81310, Johor (Malaysia); Hussin, Rosli, E-mail: roslihussin@utm.my [Phosphor Research Group, Department of Physics, Faculty of Science, Universiti Teknologi Malaysia, Skudai 81310, Johor (Malaysia); Lintang, Hendrik O., E-mail: hendrik@ibnusina.utm.my [Catalytic Science and Technology (CST) Research Group, Ibnu Sina Institute for Fundamental Science Studies, Universiti Teknologi Malaysia, Skudai 81310, Johor (Malaysia); Endud, Salasiah, E-mail: salasiah@kimia.fs.utm.my [Department of Chemistry, Faculty of Science, Universiti Teknologi Malaysia, 81310 UTM Johor Bahru, Johor (Malaysia)

    2014-05-15

    Highlights: • FT-IR revealed that the network structures are from borate and phosphate network. • The PL spectrum exhibits a green emission band at 582 nm ({sup 4}T{sub 1g} → {sup 6}A{sub 1g}). • As the concentration of Mn{sup 2+} ions is increased, the emission band had been red shifted. • These glasses are found to have potential applications as luminescent optical materials. - Abstract: Calcium zinc borophosphate glasses (CaZnBP) doped with various concentrations of Mn{sup 2+} ions and borate and phosphate as variable were prepared using conventional melt quenching technique. The structure of obtained glasses were examined by means of use: X-ray diffraction (XRD) and fourier transform infrared (FT-IR). XRD analysis confirmed amorphous nature of glass samples. The FT-IR spectra reveals the presence of both borate and phosphate vibrational modes in the prepared glasses. The doping of Mn{sup 2+} ions (2–10 mol%) shows no significant changes in the main IR vibrational bands. Optical properties were studied by measuring the near infrared photoluminescence (PL) spectra. CaZnBP glasses exhibited intense green emission peak (582 nm) (tetrahedral symmetry), which is assigned to a transition from the upper {sup 4}T{sub 1g} → {sup 6}A{sub 1g} ground state of Mn{sup 2+} ions. As the concentration of Mn{sup 2+} ions increases, the emission band increases from 582 nm to 650 nm and exhibited a red light emission (octahedral symmetry). The decay curves of {sup 4}T{sub 1g} level were examined for all concentrations and the measured lifetimes are found to depend strongly on Mn{sup 2+} concentrations. From the emission characteristic parameters of {sup 6}A{sub 1g} (S) level, it shows that the CaZnBP glasses could have potential applications as luminescent optical materials, visible lasers and fluorescent display devices.

  18. Zinc

    Science.gov (United States)

    ... Some early research suggests that zinc supplementation increases sperm count, testosterone levels, and pregnancy rates in infertile men with low testosterone levels. Other research suggests that taking zinc can improve sperm shape in men with moderate enlargement of a ...

  19. Linear Optical Properties of Zinc Borotellurite Glass Doped with Lanthanum Oxide Nanoparticles for Optoelectronic and Photonic Application

    Directory of Open Access Journals (Sweden)

    Faznny Mohd Fudzi

    2017-01-01

    Full Text Available Enhancing the optical properties of glasses for the sake of optical application in various fields is an ongoing challenge in materials science and technology. Thus, the optical properties of zinc borotellurite glass doped with lanthanum oxide nanoparticles (La2O3 NPs with the chemical composition of {[(TeO20.7(B2O30.3]0.7(ZnO0.3}1−x (La2O3 NPsx, where x = 0.01, 0.02, 0.03, 0.04, and 0.05 molar fraction, have been investigated. Characterization techniques such as x-ray diffraction, Fourier Transform Infrared Spectroscopy, and Ultraviolet-Visible Spectroscopy are employed to yield the structural properties and optical parameter of the glass. The amorphous nature of the fabricated glasses is confirmed with the presence of a broad hump via XRD diffraction pattern. The decreasing amount of high polarizable nonbridging oxygen as the concentration of La2O3 NPs increases has contributed to the increasing trend of energy band gap in the range of 2.70 to 3.52 eV and decreasing value of refractive index between 2.34 and 2.48. The fabricated glasses that have a higher refractive index than the widely used fiber material, pure silica glass, indicate that zinc borotellurite glass doped with lanthanum nanoparticles is a promising material to be applied as optical fibers.

  20. Measurements of defect structures by positron annihilation lifetime spectroscopy of the tellurite glass TeO2-P2O5-ZnO-LiNbO3 doped with ions of rare earth elements: Er3+, Nd3+ and Gd3+

    Science.gov (United States)

    Golis, E.; Yousef, El. S.; Reben, M.; Kotynia, K.; Filipecki, J.

    2015-12-01

    The objective of the study was the structural analysis of the TeO2-P2O5-ZnO-LiNbO3 tellurite glasses doped with ions of the rare-earth elements: Er3+, Nd3+ and Gd3+ based on the PALS (Positron Annihilation Lifetime Spectroscopy) method of measuring positron lifetimes. Values of positron lifetimes and the corresponding intensities may be connected with the sizes and number of structural defects, such as vacancies, mono-vacancies, dislocations or pores, the sizes of which range from a few angstroms to a few dozen nanometres. Experimental positron lifetime spectrum revealed existence of two positron lifetime components τ1 and τ2. Their interpretation was based on two-state positron trapping model where the physical parameters are the annihilation velocity and positron trapping rate.

  1. Optical spectroscopy and luminescence properties of Ho3+ doped zinc fluorophosphate (ZFP) glasses for green luminescent device applications

    Science.gov (United States)

    Reddy Prasad, V.; Damodaraiah, S.; Ratnakaram, Y. C.

    2018-04-01

    Ho3+ doped zinc fluorophosphate (ZFP) glasses with molar chemical compositions, (60-x) NH4H2PO4+20ZnO+10BaF2+10NaF+xHo2O3 (where x = 0.1, 0.3, 0.5, 1.0 and 1.5 mol%) were prepared by melt quenching technique. These glasses were characterized through physical, structural, optical, excitation, luminescence and decay curve analysis. From the absorption spectra, spectral intensities (fexp and fcal), Judd-Ofelt intensity parameters (Ω2, Ω4 and Ω6), radiative transition probabilities (AT), radiative lifetimes (τR) and branching ratios (βR) were evaluated for all Ho3+ doped ZFP glass matrices. From the photoluminescence spectra, peak stimulated emission cross-sections (σP) were calculated for all Ho3+ doped ZFP glasses. The Ho3+ doped ZFP glasses show strong green emission at 545 nm and red emission at 656 nm under excitation, 450 nm. The measured lifetimes (τmeas) of (5S2)5F4 level of Ho3+ doped ZFP glasses were obtained from decay profiles. The CIE color coordinates of Ho3+ doped ZFP glasses were calculated from emission spectra and 1.0 mol% of Ho3+ doped ZFP glass matrix gives green emission. Hence, these results confirm that the Ho3+ doped ZFP glasses could be considered as a promising candidate for visible green laser applications.

  2. Spectroscopic attributes of Sm3+ doped magnesium zinc sulfophosphate glass: Effects of silver nanoparticles inclusion

    Science.gov (United States)

    Ahmadi, F.; Hussin, R.; Ghoshal, S. K.

    2017-11-01

    We report the modified optical properties of Sm3+ doped magnesium zinc sulfophosphate glass system with silver nanoparticles (Ag NPs) inclusion. Three glass samples were prepared using melt quenching method and characterized. TEM images revealed the nucleation of Ag NPs with average diameter ≈12.50 nm. The UV-Vis-NIR spectra showed thirteen absorption bands. The surface plasmon resonance (SPR) band of Ag NPs was manifested at 446 nm. FTIR spectra disclosed the bonding vibrations for P-O bonds, P-O-P linkages, and PO2 units. Ag NPs concentration dependent bonding parameters and Judd-Ofelt (JO) intensity parameters were calculated. The JO parameter Ω2 was reduced with the increase of Ag NPs contents, indicating the ionicity and symmetry enhancement between Sm3+ ions with their surrounding ligands. The emission spectra of all samples under the excitation wavelength of 402 nm exhibited four significant peaks centered at 562, 599, 644 and 702 nm which are allocated to 4G5/2 →6H5/2, 6H7/2, 6H9/2 and 6H11/2 transitions, respectively. Inclusion of Ag NPs was discerned to augment the luminescence intensity by a factor of two, which was majorly ascribed to the local field effect of Ag NPs and subsequent energy transfer from the NPs to Sm3+ ions.

  3. Luminescence properties of Dy3+ doped lithium zinc borosilicate glasses for photonic applications

    Directory of Open Access Journals (Sweden)

    N. Jaidass

    2018-03-01

    Full Text Available Different concentrations of Dy3+ ions doped lithium zinc borosilicate glasses of chemical composition (30-x B2O3 - 25 SiO2 -10 Al2O3 -30 LiF - 5 ZnO - x Dy2O3 (x = 0, 0.1, 0.5, 1.0 and 2.0 mol% were prepared by the melt quenching technique. The prepared glasses were investigated through X-ray diffraction, optical absorption, photoluminescence and decay measurements. Intensities of absorption bands expressed in terms of oscillator strengths (f were used to determine the Judd-Ofelt (J-O intensity parameters Ωλ (λ = 2, 4 and 6. The evaluated J-O parameters were used to determine the radiative parameters such as transition probabilities (AR, total transition probability rate (AT, radiative lifetime (τR and branching ratios (βR for the excited 4F9/2 level of Dy3+ ions. The chromaticity coordinates determined from the emission spectra were found to be located in the white light region of CIE chromaticity diagram. Keywords: Condensed matter physics, Engineering, Materials science

  4. A comparative study of the experimental and the theoretical elastic data of Tm{sup 3+} doped zinc borotellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Hasnimulyati, L. [Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400, UPM, Serdang, Selangor (Malaysia); Halimah, M.K., E-mail: halimahmk@upm.edu.my [Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400, UPM, Serdang, Selangor (Malaysia); Zakaria, A.; Halim, S.A. [Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400, UPM, Serdang, Selangor (Malaysia); Ishak, M. [Technical Support Division, Malaysian Institute for Nuclear Technology Research (MINT), Bangi, 43000 Kajang (Malaysia)

    2017-05-01

    A series of glass samples with composition {[(TeO_2)_0_._7(B_2O_3)_0_._3]_0_._7[ZnO]_0_._3}{sub 1-x}{Tm_2O_3}{sub x} was prepared by using the melt-quenching technique. Then, the samples were characterized by using the densimeter, FTIR and ultrasound technique. The variations of density, molar volume, ultrasonic velocity, elastic moduli, and Poisson’s ratio were discussed and correlated with the composition of the glass samples and the FTIR spectra. It was found that the addition of thulium caused bridging and non-bridging oxygen to be formed at the same time due to the different effect that occur to tellurite and borate network as thulium is added. As thulium is varied from 1 until 3 mol%, bridging oxygens had been found to occur at a high rate and caused the ultrasonic velocity to increase. Nonetheless, when thulium oxide exceeded 3 mol%, non-bridging oxygens formed at a high rate. As a result, ultrasonic velocity was reduced. Furthermore, the values of elastic moduli (including bulk, shear, Young’s modulus, and Poisson’s ratio) were compared with the data that were calculated theoretically by using bulk compression, Makishima-Mackenzie, and Rocherulle models. - Highlights: • Bridging and non-bridging oxygen produced concurrently with the addition of Tm{sub 2}O{sub 3}. • All elastic moduli are increase with the increment of thulium oxide. • The three theoretical models are found invalid to be used in this study.

  5. Retentive [correction of Preventive] efficacy of glass ionomer, zinc phosphate and zinc polycarboxylate luting cements in preformed stainless steel crowns: a comparative clinical study.

    Science.gov (United States)

    Khinda, V I S; Grewal, N

    2002-06-01

    This study was undertaken to assess the efficacy of three luting cements, namely, glass ionomer, zinc phosphate and zinc polycarboxylate in retainng the preformed stainless steel crowns in-vivo. Twenty subjects, with an indication for restoration of three primary molars with stainless steel crowns, were selected. Sixty teeth were taken up for the study, and twenty crowns were cemented with each of the three luting cements. After an eight month follow up the crowns were assessed for their presence/ absence or "rocking". Statistical analysis was done using Chi-square test. The results have shown no significant difference in retentivity of stainless steel crowns with the use of either of the three luting agents.

  6. Electronic polarizability, optical basicity and interaction parameter for Nd2O3 doped lithium-zinc-phosphate glasses

    Science.gov (United States)

    Algradee, M. A.; Sultan, M.; Samir, O. M.; Alwany, A. Elwhab B.

    2017-08-01

    The Nd3+-doped lithium-zinc-phosphate glasses were prepared by means of conventional melt quenching method. X-ray diffraction results confirmed the glassy nature of the studied glasses. The physical parameters such as the density, molar volume, ion concentration, polaron radius, inter-ionic distance, field strength and oxygen packing density were calculated using different formulae. The transmittance and reflectance spectra of glasses were recorded in the wavelength range 190-1200 nm. The values of optical band gap and Urbach energy were determined based on Mott-Davis model. The refractive indices for the studied glasses were evaluated from optical band gap values using different methods. The average electronic polarizability of the oxide ions, optical basicity and an interaction parameter were investigated from the calculated values of the refractive index and the optical band gap for the studied glasses. The variations in the different physical and optical properties of glasses with Nd2O3 content were discussed in terms of different parameters such as non-bridging oxygen and different concentrations of Nd cation in glass system.

  7. Novel adaptations to zinc-silicate glass polyalkenoate cements: the unexpected influences of germanium based glasses on handling characteristics and mechanical properties.

    Science.gov (United States)

    Dickey, B T; Kehoe, S; Boyd, D

    2013-07-01

    Aluminum-free glass polyalkenoate cements (GPC) have been hindered for use as injectable bone cements by their inability to balance handling characteristics with mechanical integrity. Currently, zinc-based, aluminum-free GPCs demonstrate compression strengths in excess of 60MPa, but set in c. 1-2 min. Previous efforts to extend the setting reaction have remained clinically insufficient and are typically accompanied by a significant drop in strength. This work synthesized novel glasses based on a zinc silicate composition with the inclusion of GeO2, ZrO2, and Na2O, and evaluated the setting reaction and mechanical properties of the resultant GPCs. Germanium based GPCs were found to have working times between 5 and 10 min, setting times between 14 and 36 min, and compression strengths in excess of 30 MPa for the first 30 days. The results of this investigation have shown that the inclusion of GeO2, ZrO2, and Na2O into the glass network have produced, for the first time, an aluminum-free GPC that is clinically viable as injectable bone cements with regards to handling characteristics and mechanical properties. Crown Copyright © 2013. Published by Elsevier Ltd. All rights reserved.

  8. Proteomic differences between tellurite-sensitive and tellurite-resistant E.coli.

    Directory of Open Access Journals (Sweden)

    Jana Aradská

    Full Text Available Tellurite containing compounds are in use for industrial processes and increasing delivery into the environment generates specific pollution that may well result in contamination and subsequent potential adverse effects on public health. It was the aim of the current study to reveal mechanism of toxicity in tellurite-sensitive and tellurite-resistant E. coli at the protein level. In this work an approach using gel-based mass spectrometrical analysis to identify a differential protein profile related to tellurite toxicity was used and the mechanism of ter operon-mediated tellurite resistance was addressed. E. coli BL21 was genetically manipulated for tellurite-resistance by the introduction of the resistance-conferring ter genes on the pLK18 plasmid. Potassium tellurite was added to cultures in order to obtain a final 3.9 micromolar concentration. Proteins from tellurite-sensitive and tellurite-resistant E. coli were run on 2-D gel electrophoresis, spots of interest were picked, in-gel digested and subsequently analysed by nano-LC-MS/MS (ion trap. In addition, Western blotting and measurement of enzymatic activity were performed to verify the expression of certain candidate proteins. Following exposure to tellurite, in contrast to tellurite-resistant bacteria, sensitive cells exhibited increased levels of antioxidant enzymes superoxide dismutases, catalase and oxidoreductase YqhD. Cysteine desulfurase, known to be related to tellurite toxicity as well as proteins involved in protein folding: GroEL, DnaK and EF-Tu were upregulated in sensitive cells. In resistant bacteria, several isoforms of four essential Ter proteins were observed and following tellurite treatment the abovementioned protein levels did not show any significant proteome changes as compared to the sensitive control. The absence of general defense mechanisms against tellurite toxicity in resistant bacteria thus provides further evidence that the four proteins of the ter operon

  9. Preliminary investigation of novel bone graft substitutes based on strontium-calcium-zinc-silicate glasses.

    Science.gov (United States)

    Boyd, D; Carroll, G; Towler, M R; Freeman, C; Farthing, P; Brook, I M

    2009-01-01

    Bone graft procedures typically require surgeons to harvest bone from a second site on a given patient (Autograft) before repairing a bone defect. However, this results in increased surgical time, excessive blood loss and a significant increase in pain. In this context a synthetic bone graft with excellent histocompatibility, built in antibacterial efficacy and the ability to regenerate healthy tissue in place of diseased tissue would be a significant step forward relative to current state of the art philosophies. We developed a range of calcium-strontium-zinc-silicate glass based bone grafts and characterised their structure and physical properties, then evaluated their in vitro cytotoxicity and in vivo biocompatibility using standardised models from the literature. A graft (designated BT109) of composition 0.28SrO/0.32ZnO/0.40 SiO(2) (mol fraction) was the best performing formulation in vitro shown to induce extremely mild cytopathic effects (cell viability up to 95%) in comparison with the commercially available bone graft Novabone (cell viability of up to 72%). Supplementary to this, the grafts were examined using the standard rat femur healing model on healthy Wister rats. All grafts were shown to be equally well tolerated in bone tissue and new bone was seen in close apposition to implanted particles with no evidence of an inflammatory response within bone. Complimentary to this BT109 was implanted into the femurs of ovariectomized rats to monitor the response of osteoporotic tissue to the bone grafts. The results from this experiment indicate that the novel grafts perform equally well in osteoporotic tissue as in healthy tissue, which is encouraging given that bone response to implants is usually diminished in ovariectomized rats. In conclusion these materials exhibit significant potential as synthetic bone grafts to warrant further investigation and optimisation.

  10. Ac-conductivity and dielectric response of new zinc-phosphate glass/metal composites

    Energy Technology Data Exchange (ETDEWEB)

    Maaroufi, A., E-mail: maaroufi@fsr.ac.ma [University of Mohammed V, Laboratory of Composite Materials, Polymers and Environment, Department of Chemistry, Faculty of Sciences, P.B. 1014, Rabat-Agdal (Morocco); Oabi, O. [University of Mohammed V, Laboratory of Composite Materials, Polymers and Environment, Department of Chemistry, Faculty of Sciences, P.B. 1014, Rabat-Agdal (Morocco); Lucas, B. [XLIM UMR 7252 – Université de Limoges/CNRS, 123 avenue Albert Thomas, 87060 Limoges Cedex (France)

    2016-07-01

    The ac-conductivity and dielectric response of new composites based on zinc-phosphate glass with composition 45 mol%ZnO–55 mol%P{sub 2}O{sub 5}, filled with metallic powder of nickel (ZP/Ni) were investigated by impedance spectroscopy in the frequency range from 100 Hz to 1 MHz at room temperature. A high percolating jump of seven times has been observed in the conductivity behavior from low volume fraction of filler to the higher fractions, indicating an insulator – semiconductor phase transition. The measured conductivity at higher filler volume fraction is about 10{sup −1} S/cm and is frequency independent, while, the obtained conductivity for low filler volume fraction is around 10{sup −8} S/cm and is frequency dependent. Moreover, the elaborated composites are characterized by high dielectric constants in the range of 10{sup 5} for conductive composites at low frequencies (100 Hz). In addition, the distribution of the relaxation processes was also evaluated. The Debye, Cole-Cole, Davidson–Cole and Havriliak–Negami models in electric modulus formalism were used to model the observed relaxation phenomena in ZP/Ni composites. The observed relaxation phenomena are fairly simulated by Davidson–Cole model, and an account of the interpretation of results is given. - Highlights: • Composites of ZnO-P{sub 2}O{sub 5}/metal were investigated by impedance spectroscopy. • Original ac-conductivity behavior was discovered in ZnO-P{sub 2}O{sub 5}/metal composites. • High dielectric constant is measured in ZnO-P{sub 2}O{sub 5}/metal composites. • Dielectric constant as filler function is well interpreted with percolation theory. • Observed relaxation processes are well described using electric modulus formalism.

  11. Effect of MnO2 doped on physical, structure and optical properties of zinc silicate glasses from waste rice husk ash

    Directory of Open Access Journals (Sweden)

    Ali Jabbar Abed Al-Nidawi

    Full Text Available In this study, an investigation was conducted to explore and synthesize silicate (SiO2 glass from waste rice husk ash (RHA. MnO2 doped zinc silicate glasses with chemical formula [(ZnO55 + (WRHA45]100-X[MnO2]X, (where X = 0, 1, 3 and 5 wt% was prepared by conventional melt quenching technique. The glass samples were characterized using energy dispersive X-ray fluorescence (EDXRF, X-ray diffraction (XRD, field emission scanning electron microscopy (FESEM, Fourier transform infrared (FTIR spectroscopy, and ultraviolet–visible (UV–Vis spectroscopy. The results revealed that by increasing the concentration of MnO2, the color of glass samples changed from colorless to brown and the density of glass increased. XRD results showed that a broad halo peak which centered on the low angle (2θ = 30° indicated the amorphous nature of the glass. FTIR results showed basic structural units of Si-O-Si in non-bridging oxygen, Si-O and Mn-O in the glass network. FESEM result showed a decreasing porosity with an increasing MnO2 content, which was attributed to the Mn ions resort to occupy interstitial sites inside the pores of glass. Besides, the absorption intensity of glass increased and the band gap value decreased with increasing the MnO2 percentage. In this synthesized glass system of MnO2 doped zinc silicate glasses using RHA as a source of silica, the MnO2 affect most of the properties of the glass system under investigation. Keywords: Rice husk, Manganese dioxide, Glass, Zinc silicate, Sintering, Optical properties

  12. Structural and luminescence studies of Ho{sup 3+}-doped zinc-aluminium-sodium-phosphate (ZANP) glasses

    Energy Technology Data Exchange (ETDEWEB)

    Brahmachary, K.; Rajesh, D.; Ratnakaram, Y. C., E-mail: ratnakaramsvu@gmail.com [Department of Physics, Sri Venkateswara University, Tirupati-517502 (India)

    2015-06-24

    Trivalent holmium doped zinc-aluminium-sodium-phosphate (ZANP) glasses were prepared by conventional melt-quenching technique and characterized for their structural and luminescence properties. The amorphous nature, elemental analysis and thermal stability of the glasses were studied by using X-ray diffraction, energy dispersive spectrum and differential scanning calorimetry analysis, respectively. The absorption and fluorescence spectra have been recorded at room temperature. Based on the absorption spectra, the Judd-Ofelt parameters and radiative parameters such as spontaneous transition probabilities (A{sub R}), branching ratios (β{sub R}), radiative lifetimes (τ{sub R}) were calculated and discussed. From the emission spectra emission peak positions (λ{sub P}), effective bandwidths (Δλ{sub eff}) and stimulated emission cross-sections (σ{sub P}) were calculated for the observed emission transitions,{sup 5}S{sub 2} ({sup 5}F{sub 4}→{sup 5}I{sub 8}) and {sup 5}F{sub 5}→{sup 5}I{sub 8} in all the glass samples. The stimulated emission cross-section is higher for ZANPHo10 glass matrix and so it may be useful for laser excitation.

  13. Investigation of Er doped zinc borate glasses by low-temperature photoluminescence

    Czech Academy of Sciences Publication Activity Database

    Kostka, Petr; Kabalci, I.; Tay, T.; Gladkov, Petar; Zavadil, Jiří

    2017-01-01

    Roč. 192, DEC 2017 (2017), s. 1104-1109 ISSN 0022-2313 Institutional support: RVO:67985891 ; RVO:67985882 Keywords : borate glasses * rare-earth ions * stark levels * photoluminiscence Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass; JH - Ceramics, Fire-Resistant Materials and Glass (URE-Y) OBOR OECD: Ceramics; Ceramics (URE-Y) Impact factor: 2.686, year: 2016

  14. Optical aging observation in suspended core tellurite microstructured fibers under atmospheric conditions

    Science.gov (United States)

    Strutynski, C.; Mouawad, O.; Picot-Clémente, J.; Froidevaux, P.; Désévédavy, F.; Gadret, G.; Jules, J.-C.; Kibler, B.; Smektala, F.

    2017-11-01

    Tellurite glasses are good candidates for the development of broadband supercontinuum (SC) laser sources in the 1-5 μm range. At the moment, beside very few exceptions, SC generation in TeO2-based microstructured optical fibers (MOFs) is limited to 3 μm in the mid-infrared (MIR). We present here an observation of an optical aging occurring in six-hole suspended-core tellurite MOFs. When exposed to atmospheric conditions, such fibers show an alteration of their transmission between 3 and 4 μm. This aging phenomenon leads to the growth of strong additional losses in this wavelengths range over time. Impact of the transmission degradation on spectral broadening is studied through numerical simulations of SC generation.

  15. Structure and properties of MoO.sub.3./sub.-containing zinc borophosphate glasses

    Czech Academy of Sciences Publication Activity Database

    Šubčík, J.; Koudelka, L.; Mošner, P.; Montagne, L.; Revel, B.; Gregora, Ivan

    2009-01-01

    Roč. 355, 16-17 (2009), 970-975 ISSN 0022-3093 R&D Projects: GA AV ČR KAN301370701 Institutional research plan: CEZ:AV0Z10100520 Keywords : glass formation * glass es * phosphates * structure Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.252, year: 2009

  16. Thermal, structural and magnetic properties of some zinc phosphate glasses doped with manganese ions

    International Nuclear Information System (INIS)

    Pascuta, Petru; Bosca, Maria; Borodi, Gheorghe; Culea, Eugen

    2011-01-01

    Research highlights: → MnO) x .(P 2 O 5 ) 40 .(ZnO) 60-x glasses (0 ≤ x ≤ 20 mol%) were prepared by the melt-quenching technique. → The DTA data indicate a good thermal stability of the studied glasses. → EPR spectra shows isolated Mn 2+ ions in octahedral symmetric sites or to associated ones when the Mn 2+ ions are involved in dipole-dipole and/or superexchange interactions. → The magnetic susceptibility data revealed superexchange magnetic interactions involving manganese ions, antiferromagnetically coupled for the sample containing 20 mol% MnO. - Abstract: (MnO) x .(P 2 O 5 ) 40 .(ZnO) 60-x glasses containing different concentrations of MnO ranging from 0 to 20 mol% were prepared by the melt-quenching technique. The samples had a fixed P 2 O 5 content of 40 mol% and the MnO:ZnO ratio was varied. The thermal, structural and magnetic properties of these glasses were investigated by means of differential thermal analysis (DTA), electron paramagnetic resonance (EPR) and magnetic susceptibility measurements. Compositional dependence of the glass transition (T g ), crystallization (T p ) and melting temperatures were determined by DTA investigations. From the dependence of the T g on the heating rate (a), the activation energy of the glass transition (E g ) was calculated. The fragility index (F) for the studied glasses was determined to see whether these materials are obtained from kinetically strong-glass-forming (KS) or kinetically fragile-glass forming (KF) liquids. The EPR spectra of the studied glasses revealed absorptions centered at g ∼ 2.0, 3.3 and 4.3. The compositional variations of the intensity and line width of these absorption lines was interpreted in terms of the variation in the concentration of the Mn 2+ and Mn 3+ ions in the glass and the interaction between the manganese ions. EPR and magnetic susceptibility data reveal that both Mn 2+ and Mn 3+ ions are present in the studied glasses, their relative concentration being dependent on

  17. Effect of MnO2 doped on physical, structure and optical properties of zinc silicate glasses from waste rice husk ash

    Science.gov (United States)

    Al-Nidawi, Ali Jabbar Abed; Matori, Khamirul Amin; Zakaria, Azmi; Mohd Zaid, Mohd Hafiz

    In this study, an investigation was conducted to explore and synthesize silicate (SiO2) glass from waste rice husk ash (RHA). MnO2 doped zinc silicate glasses with chemical formula [(ZnO)55 + (WRHA)45]100-X[MnO2]X, (where X = 0, 1, 3 and 5 wt%) was prepared by conventional melt quenching technique. The glass samples were characterized using energy dispersive X-ray fluorescence (EDXRF), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), Fourier transform infrared (FTIR) spectroscopy, and ultraviolet-visible (UV-Vis) spectroscopy. The results revealed that by increasing the concentration of MnO2, the color of glass samples changed from colorless to brown and the density of glass increased. XRD results showed that a broad halo peak which centered on the low angle (2θ = 30°) indicated the amorphous nature of the glass. FTIR results showed basic structural units of Si-O-Si in non-bridging oxygen, Si-O and Mn-O in the glass network. FESEM result showed a decreasing porosity with an increasing MnO2 content, which was attributed to the Mn ions resort to occupy interstitial sites inside the pores of glass. Besides, the absorption intensity of glass increased and the band gap value decreased with increasing the MnO2 percentage. In this synthesized glass system of MnO2 doped zinc silicate glasses using RHA as a source of silica, the MnO2 affect most of the properties of the glass system under investigation.

  18. EPR Study of Vanadium Ion in Zinc-Boro-Vanadate Glasses

    International Nuclear Information System (INIS)

    Renuka, C.; Gowda, V. C. Veeranna; Chakradhar, R. P. S.; Reddy, C. Narayana

    2011-01-01

    This paper describes EPR studies on x V 2 O 5 -(40-x)ZnO-60B 2 O 3 (where x 5, 10, 15 and 20 mol %) glass system. These studies indicate a strong compositional dependent trend and existence of characteristic boro-vanadate groups in these glasses. The EPR spectra show a distinct hyperfine structure of 51 V. Spectral analysis shows that the vanadium is present in the glass as vanadyl ion [VO] 2+ at tetragonally distorted octahedral site. The decrease of A || and A perpendicular with increase of V 2 O 5 concentration suggests an increase in the covalence between the central atom and the surrounding oxygen ligands.

  19. Effect of F- ions on physical and spectroscopic properties of Yb3+-doped TeO2-based glasses

    International Nuclear Information System (INIS)

    Wang Guonian; Dai Shixun; Zhang Junjie; Xu Shiqing; Hu Lili; Jiang Zhonghong

    2005-01-01

    The effects of F - ions on physical and spectroscopic properties of the Yb 3+ in tellurite glass system are investigated. The results show that the glass system takes on good thermal stability with the content of ZnF 2 lower than 15 mol%, both the emission cross-section and the fluorescence lifetime of Yb 3+ ions increase evidently which indicate that such oxyfluoride tellurite glass system is a promising laser host matrix for high power generation. FT-IR spectra were used to analyze the effect of F- ions on the structure of tellurite glasses and OH - groups in this glass system. Analysis demonstrates that addition of fluoride decreases the symmetry of the structure of tellurite glasses which increases the emission cross-section and removes the OH - groups, and which improves the measured fluorescence lifetime of Yb 3+ ions

  20. Microstructure and spectroscopic investigations of calcium zinc bismuth phosphate glass ceramics doped with manganese ions

    Science.gov (United States)

    Suneel Kumar, A.; Sambasiva Rao, M. V.; Chinna Ram, G.; Krishna Rao, D.

    2018-01-01

    Multi-component 10CaF2-20ZnO-(15 - x)Bi2O3-55P2O5:xMnO (0 ≤ x ≤ 2.5) glass ceramics were synthesised by melt quenching technique and heat treatment. The prepared glass ceramics were characterised by XRD, DTA, EDS and SEM. Spectroscopic studies such as optical absorption, EPR, FTIR and Raman were also carried out on these glass ceramics. The XRD and SEM studies have indicated that ceramic samples contain well defined and randomly distributed grains of different crystalline phases. The observed increase of enthalpy from DTA patterns up to 1 mol% of MnO indicates that the crystallisation starts initially from the surface of the material then gradually it is extended to the volume of the material and this influence is meagre at higher concentrations of MnO. The absorption spectra of manganese doped glass ceramics have exhibited two types of conventional bands; one due to Mn2+ ions and other due to Mn3+ ions. The EPR spectra of MnO doped glass ceramics showed a resonance signal around g2 = 2.023 with a six line hyperfine structure and another signal at about g1 = 4.314. The relative intensity and half-width of these two signals are observed to increase with the increase in the concentration of manganese ions up to 1 mol% beyond this concentration it is found to decrease. Such observation indicates the conversion of part of Mn2+ ions into Mn3+ ions in the glass ceramic matrix. The observed increase in the intensity of symmetrical structural units at the expense of asymmetrical structural units from the FTIR and Raman spectra at higher concentration of MnO indicating that Mn2+ ions occupy the network forming positions in the glass ceramic structure.

  1. Calcium and Zinc Containing Bactericidal Glass Coatings for Biomedical Metallic Substrates

    Directory of Open Access Journals (Sweden)

    Leticia Esteban-Tejeda

    2014-07-01

    Full Text Available The present work presents new bactericidal coatings, based on two families of non-toxic, antimicrobial glasses belonging to B2O3–SiO2–Na2O–ZnO and SiO2–Na2O–Al2O3–CaO–B2O3 systems. Free of cracking, single layer direct coatings on different biomedical metallic substrates (titanium alloy, Nb, Ta, and stainless steel have been developed. Thermal expansion mismatch was adjusted by changing glass composition of the glass type, as well as the firing atmosphere (air or Ar according to the biomedical metallic substrates. Formation of bubbles in some of the glassy coatings has been rationalized considering the reactions that take place at the different metal/coating interfaces. All the obtained coatings were proven to be strongly antibacterial versus Escherichia coli (>4 log.

  2. Disordered Zinc in Zn4Sb3 with Phonon-Glass and Electron-Crystal Thermoelectric Properties

    Science.gov (United States)

    Snyder, G. Jeffrey; Christensen, Mogens; Nishibori, Eiji; Caillat, Thierry; Brummerstedt Iversen, Bo

    2004-01-01

    By converting waste heat into electricity, thermoelectric generators could be an important part of the solution to today's energy challenges. The compound Zn4Sb3 is one of the most efficient thermoelectric materials known. Its high efficiency results from an extraordinarily low thermal conductivity in conjunction with the electronic structure of a heavily doped semiconductor. Previous structural studies have been unable to explain this unusual combination of properties. Here, we show through a comprehensive structural analysis using single-crystal X-ray and powder-synchrotron-radiation diffraction methods, that both the electronic and thermal properties of Zn4Sb3 can be understood in terms of unique structural features that have been previously overlooked. The identification of Sb3- ions and Sb-2(4-) dimers reveals that Zn4Sb3 is a valence semiconductor with the ideal stoichiometry Zn13Sb10. In addition, the structure contains significant disorder, with zinc atoms distributed over multiple positions. The discovery of glass-like interstitial sites uncovers a highly effective mechanism for reducing thermal conductivity. Thus Zn4Sb3 is in many ways an ideal 'phonon glass, electron crystal' thermoelectric material.

  3. Lessons from a “Failed” Experiment: Zinc Silicates with Complex Morphology by Reaction of Zinc Acetate, the Ionic Liquid Precursor (ILP Tetrabutylammonium Hydroxide (TBAH, and Glass

    Directory of Open Access Journals (Sweden)

    Andreas Taubert

    2008-08-01

    Full Text Available At elevated temperatures, the ionic liquid precursor (ILP tetrabutylammonium hydroxide reacts with zinc acetate and the glass wall of the reaction vessel. While the reaction of OH- with the glass wall is not surprising as such and could be considered a failed experiment, the resulting materials are interesting for a variety of applications. If done on purpose and under controlled conditions, the reaction with the glass wall results in uniform, well-defined hemimorphite Zn4Si2O7(OH2·nH2O and willemite Zn2SiO4 microcrystals and films. Their morphology can be adjusted by variation of the reaction time and reaction temperature. The hemimorphite can be transformed to Zn2SiO4 via calcination. The process is therefore a viable approach for the fabrication of porous films on glass surfaces with potential applications as catalyst support, among others.

  4. Structural and optical properties of Eu3+ activated low cost zinc soda lime silica glasses

    Directory of Open Access Journals (Sweden)

    Nur Alia Sheh Omar

    Full Text Available A low cost method was employed to synthesize ZnO-SLS:xEu3+ phosphors using recyclable bottle glass as silica source. The structural and optical properties of ZnO-SLS:xEu3+ (x = 0, 1, 2, 3, 4 and 5 wt.% glasses were determined using X-ray diffraction (XRD, Fourier transform infrared reflectance (FTIR, UV-visible (Uv-Vis and photoluminescence (PL spectroscopy. Structural investigation using XRD measurement had broadened the halo peak with the doping of dopants. FTIR spectra showed the glass system consists of –OH and SiO4 bands. Meanwhile, the optical measurement using UV-Vis absorption has been induced a blue shift of the electronic absorption edge. The emission peak intensity of ZnO-SLS:xEu3+ phosphors was enhanced with the progression of doping concentration and thus, revealed their potential as red emitting phosphors under 400 nm excitation. Keywords: Eu3+ doped ZnO-SLS glasses, Solid state method, Optical band gap, Photoluminescence

  5. Photoluminescence study of Er-doped zinc-sodium-antimonite glasses

    Czech Academy of Sciences Publication Activity Database

    Zavadil, Jiří; Ivanova, Z. G.; Kostka, Petr; Hamzaoui, M.; Soltani, M.

    2014-01-01

    Roč. 611, 25 October (2014), s. 111-116 ISSN 0925-8388 R&D Projects: GA ČR GAP106/12/2384; GA MŠk(CZ) 7AMB14SK009 Institutional support: RVO:67985882 ; RVO:67985891 Keywords : Erbium * Photoluminescence * Antimonite glasses Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering; BM - Solid Matter Physics ; Magnetism (USMH-B) Impact factor: 2.999, year: 2014

  6. Influence of samarium ions (Sm3+) on the optical properties of lithium zinc phosphate glasses

    Science.gov (United States)

    Shwetha, M.; Eraiah, B.

    2018-05-01

    New glass samples with composition xSm2O3-(15-x) Li2O-45ZnO-40P2O5, where x= 0, 0.1, 0.3 and 0.5 mol % are prepared by conventional melt-quenching method. X-ray Diffraction measurements were performed to confirm their amorphous nature. Densities of these glasses were measured by Archimedes method. Optical properties were studied using optical absorption spectra which was recorded at room temperature in the UV-Vis region. Electronic transitions specific to the rare earth ion were observed from the UV-Visible spectroscopy. Optical direct band gap and indirect band gap energies were measured and their values were found to be between 4.23-4.74 eV and 3.02-3.67 eV, respectively. Refractive index has been measured with respect to different concentrations of Sm2O3. Polaron radius, inter-nuclear distance, field strength, dielectric constant and polarizability of oxide ions have been calculated. Fluorescence spectroscopy measurements have been performed by excitation in the UV-Visible range, which resulted in the significant fluorescence peaks. The luminescence color of the glass system has been characterized using Commission International de l'Eclairage de France 1931 chromaticity diagram.

  7. Advances in Mid-IR Fiber Lasers: Tellurite, Fluoride and Chalcogenide

    Directory of Open Access Journals (Sweden)

    Mario Christian Falconi

    2017-06-01

    Full Text Available A review on the recent progress in modeling and fabrication of medium infrared (Mid-IR fiber lasers is reported. The main objective is to illustrate some recent examples of continuous wave optical sources at wavelengths longer than those commonly employed in telecom applications and allowing high beam quality. A small number of Mid-IR lasers, among the large variety of schemes, glasses, dopants and pumping schemes reported in literature, is selected on the basis of their slope efficiency and threshold pump power. In particular, tellurite, fluoride and chalcogenide fiber lasers are considered. More details are given with reference to the novel pumping schemes.

  8. [Raman spectroscopic study of binary PbO-TeO2 glasses].

    Science.gov (United States)

    Huang, Li; You, Jing-Lin; Chen, Hui; Jiang, Guo-Chang

    2008-07-01

    Raman spectra of lead tellurite glasses and their melts were measured. Results show that four coordinate tellurite units convert into three coordinate units with increasing the concentration of PbO, and the number of non-bridging oxygen bonds (NBO) increases accordingly in this system. Three spectral peaks in the high frequency range were assigned to stretching vibration of bridging oxygen in four coordinate tellurite units (Q(b)), stretching vibration of non-bridging oxygen in four coordinate tellurite units (Q(nb)) and in three coordinate tellurite units (T(nb)). The relative density of four coordinate structure units decreases and the three coordinate tellurite units considerably exist in tellurite glasses when the concentration of PbO > 50%. Besides, the Raman frequencies of the three species' peaks become blue-shifted because of the temperature induced crystallization at high temperature, and the peak intensities increase and the peaks sharpen. The peaks merge together and become much broader while the glass is heated above the melting point because of multiple microstructure units coexisting.

  9. A comparative study of retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements with stainless steel crowns - an in vitro study.

    Science.gov (United States)

    Raghunath Reddy, M H; Subba Reddy, V V; Basappa, N

    2010-01-01

    An in vitro study was conducted to compare the retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements using Instron universal testing machine. Thirty preformed and pretrimmed stainless steel crowns were used for cementation on 30 extracted human primary molars which were divided into three groups of 10 teeth in each group. Then the teeth were stored in artificial saliva and incubated at 37°C for 24 h. A load was applied on to the crown and was gradually increased till the crown showed dislodgement, and then the readings were recorded using Instron recorder and analyzed for statistical significance. The surface area of crown was measured by graphical method. The retentive strength was expressed in terms of kg/cm 2 , which was calculated by the equation load divided by area. Retentive strengths of zinc phosphate (ranged from a minimum of 16.93 to amaximum of 28.13 kg/cm 2 with mean of 21.28 kg/cm 2 ) and glass ionomer cement (minimum of 13.69 - 28.15 kg/cm 2 with mean of 20.69 kg/cm 2 ) were greater than that of polycarboxylate cement (minimum of 13.26 - 22.69 kg/cm 2 with mean of 16.79 kg/cm 2 ). Negligible difference (0.59 kg/cm 2 ) of retentive strength was observed between zinc phosphate (21.28 kg/cm 2 ) and glass ionomer cements (20.69 kg/cm 2 ). Glass ionomer cements can be recommended for cementation of stainless steel crowns because of its advantages and the retentive strength was almost similar to that of zinc phosphate cement.

  10. A comparative study of retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements with stainless steel crowns - An in vitro study

    Directory of Open Access Journals (Sweden)

    Raghunath Reddy M

    2010-01-01

    Full Text Available An in vitro study was conducted to compare the retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements using Instron universal testing machine. Thirty preformed and pretrimmed stainless steel crowns were used for cementation on 30 extracted human primary molars which were divided into three groups of 10 teeth in each group. Then the teeth were stored in artificial saliva and incubated at 37°C for 24 h. A load was applied on to the crown and was gradually increased till the crown showed dislodgement, and then the readings were recorded using Instron recorder and analyzed for statistical significance. The surface area of crown was measured by graphical method. The retentive strength was expressed in terms of kg/cm 2 , which was calculated by the equation load divided by area. Retentive strengths of zinc phosphate (ranged from a minimum of 16.93 to amaximum of 28.13 kg/cm 2 with mean of 21.28 kg/cm 2 and glass ionomer cement (minimum of 13.69 - 28.15 kg/cm 2 with mean of 20.69 kg/cm 2 were greater than that of polycarboxylate cement (minimum of 13.26 - 22.69 kg/cm 2 with mean of 16.79 kg/cm 2 . Negligible difference (0.59 kg/cm 2 of retentive strength was observed between zinc phosphate (21.28 kg/cm 2 and glass ionomer cements (20.69 kg/cm 2 . Glass ionomer cements can be recommended for cementation of stainless steel crowns because of its advantages and the retentive strength was almost similar to that of zinc phosphate cement.

  11. Electronic polarizability, optical basicity and interaction parameter for Nd{sub 2}O{sub 3} doped lithium-zinc-phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Algradee, M.A.; Sultan, M.; Samir, O.M.; Alwany, A.E.B. [Ibb University, Department of Physics, Faculty of Science, Ibb (Yemen)

    2017-08-15

    The Nd{sup 3+}-doped lithium-zinc-phosphate glasses were prepared by means of conventional melt quenching method. X-ray diffraction results confirmed the glassy nature of the studied glasses. The physical parameters such as the density, molar volume, ion concentration, polaron radius, inter-ionic distance, field strength and oxygen packing density were calculated using different formulae. The transmittance and reflectance spectra of glasses were recorded in the wavelength range 190-1200 nm. The values of optical band gap and Urbach energy were determined based on Mott-Davis model. The refractive indices for the studied glasses were evaluated from optical band gap values using different methods. The average electronic polarizability of the oxide ions, optical basicity and an interaction parameter were investigated from the calculated values of the refractive index and the optical band gap for the studied glasses. The variations in the different physical and optical properties of glasses with Nd{sub 2}O{sub 3} content were discussed in terms of different parameters such as non-bridging oxygen and different concentrations of Nd cation in glass system. (orig.)

  12. Glasses

    DEFF Research Database (Denmark)

    Dyre, Jeppe

    2004-01-01

    The temperature dependence of the viscosity of most glassforming liquids is known to depart significantly from the classical Arrhenius behaviour of simple fluids. The discovery of an unexpected correlation between the extent of this departure and the Poisson ratio of the resulting glass could lead...... to new understanding of glass ageing and viscous liquid dynamics....

  13. A comparative study of retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements with stainless steel crowns--an in vitro study.

    Science.gov (United States)

    Reddy, R; Basappa, N; Reddy, V V

    1998-03-01

    This study was conducted on 30 extracted human primary molars to assess the retentive strengths of zinc phosphate, polycarboxylate and glass ionomer cements. The teeth were embedded in resin blocks and were randomly divided into 3 groups of 10 each. The occlusal surfaces of all teeth were reduced uniformly by 1.0 to 1.5 mm. All mesial, distal undercuts were removed and sharp angles rounded. This was followed by cementing pretrimmed and precontoured stainless steel crowns on each tooth with hand pressure and storing in artificial saliva at 37 degrees C for 24 hours. Retentive strength was tested using Instron Universal Testing Machine. The load was applied starting from a zero reading and gradually increased until the cemented stainless steel crowns showed signs of movement and then the readings were recorded. It was found that retentive strengths of zinc phosphate and glass ionomer cements were statistically better (P cement. Negligible difference (0. 59 kg/cm2) was however observed between zinc phosphate and glass ionomer cements.

  14. Effect of annealing on refractive indices of radio-frequency magnetron sputtered waveguiding zinc oxide films on glass

    International Nuclear Information System (INIS)

    Mehan, Navina; Gupta, Vinay; Sreenivas, Kondepudy; Mansingh, Abhai

    2004-01-01

    The effects of annealing and gas composition on the refractive indices of zinc oxide films were studied in light of the structural properties. ZnO films (1 μm) were deposited by rf magnetron sputtering in different oxygen:argon mixtures on glass and annealed at 380 deg. C in air, at different times. Waveguide modes were excited in the films by prism coupling using a He-Ne laser. The estimated values of the extraordinary and ordinary refractive indices of the films, which were close to the corresponding bulk values (n e =2.006, n o =1.990), initially decreased with annealing time and later increased before becoming constant with further annealing. The variation in refractive indices was explained on the basis of contribution from both packing density p and lattice constant c of the films. The initial decrease in refractive indices was attributed to the observed lattice contraction, and the latter increase was explained in terms of the increase in packing density (p) of the films on annealing. A relation is proposed to estimate the refractive indices of films, which have the lattice constant c different from the bulk value

  15. Theoretical Studies of the Spin Hamiltonian Parameters and Local Distortions for Cu2+ in Alkaline Earth Lead Zinc Phosphate Glasses

    Science.gov (United States)

    Wang, Bo-Kun; Wu, Shao-Yi; Yuan, Zi-Yi; Liu, Zi-Xuan; Jiang, Shi-Xin; Liu, Zheng; Yao, Zi-Jian; Teng, Bao-Hua; Wu, Ming-He

    2016-08-01

    The spin Hamiltonian parameters and local structures are theoretically studied for Cu2+-doped alkaline earth lead zinc phosphate (RPPZ, R=Mg, Ca, Sr, and Ba) glasses based on the high-order perturbation calculations for a tetragonally elongated octahedral 3d9 cluster. The relative elongation ratios are found to be ρ≈3.2%, 4.4%, 4.6%, and 3.3% for R=Mg, Ca, Sr, and Ba, respectively, because of the Jahn-Teller effect. The whole decreasing crystal-field strength Dq and orbital reduction factor k from Mg to Sr are ascribed to the weakening electrostatic coulombic interactions and the increasing probability of productivity of nonbridge oxygen (and hence increasing Cu2+-O2- electron cloud admixtures) under PbO addition, respectively, with increasing alkali earth ionic radius. The anomalies (the largest Dq and the next highest k among the systems) for R=Ba are attributed to the cross linkage of this large cation in the network. The overall increasing order (Mg≤Bacontaining copper dopants.

  16. Expression of Aeromonas caviae ST pyruvate dehydrogenase complex components mediate tellurite resistance in Escherichia coli

    International Nuclear Information System (INIS)

    Castro, Miguel E.; Molina, Roberto C.; Diaz, Waldo A.; Pradenas, Gonzalo A.; Vasquez, Claudio C.

    2009-01-01

    Potassium tellurite (K 2 TeO 3 ) is harmful to most organisms and specific mechanisms explaining its toxicity are not well known to date. We previously reported that the lpdA gene product of the tellurite-resistant environmental isolate Aeromonas caviae ST is involved in the reduction of tellurite to elemental tellurium. In this work, we show that expression of A. caviae ST aceE, aceF, and lpdA genes, encoding pyruvate dehydrogenase, dihydrolipoamide transacetylase, and dihydrolipoamide dehydrogenase, respectively, results in tellurite resistance and decreased levels of tellurite-induced superoxide in Escherichia coli. In addition to oxidative damage resulting from tellurite exposure, a metabolic disorder would be simultaneously established in which the pyruvate dehydrogenase complex would represent an intracellular tellurite target. These results allow us to widen our vision regarding the molecular mechanisms involved in bacterial tellurite resistance by correlating tellurite toxicity and key enzymes of aerobic metabolism.

  17. Study on the water durability of zinc boro-phosphate glasses doped with MgO, Fe2O3, and TiO2

    Science.gov (United States)

    Hwang, Moon Kyung; Ryu, Bong Ki

    2016-07-01

    The water durability of zinc boro-phosphate (PZB) glasses with the composition 60P2O5-20ZnO-20B2O3- xMeO ( x = 0, 2, 4, 6 and MeO = MgO, Fe2O3, or TiO2) (mol%) was measured, and PZB glass was studied in terms of its thermal properties, density, and FTIR characteristics. The surface conditions and corrosion byproducts were analyzed using scanning electron microscopy. When MgO, Fe2O3, and TiO2 were doped into the PZB glass, Q2 was decreased and Q1 was increased in the phosphate structure, while the number of BO4 structures increased with increasing MeO content. The density of the PZB glass was increased by the addition of Fe2O3 and TiO2, while the glass transition temperature ( T g ) and dilatometric softening temperature ( T d ) were increased when additional MgO, Fe2O3, and TiO2 were added. From the weight loss analysis (95 ◦ C, 96 h), TiO2 doped glass showed the lowest weight loss (1.70 × 10 -3 g/cm2) while MgO doped glass showed the highest value (2.44 × 10 -3 g/cm2), compared with PZB glass (3.07 × 10 -3 g/cm2). These results were discussed in terms of the Me n+ ions in the glass structure, and their different coordination numbers and bonding strengths.

  18. Tellurite composite microstructured optical fibers with ultra-flattened and zero dispersion

    Science.gov (United States)

    Duan, Zhongchao; Liao, Meisong; Tomas, Kohoutek; Tong, Hoangtuan; Asano, Koji; Suzuki, Takenobu; Ohishi, Yasutake

    2012-04-01

    We report the fabrication of tellurite composite microstructured optical fiber (CMOF) with ultra-flattened zero dispersion (+/-3 ps/nm/Km) over 200nm band. To obtain this dispersion profile together with high nonlinearity, one ring of air holes and two layers of glass cladding are employed in the tellurite CMOF. The core of fiber is made of TeO2-Li2O-WO3 -MoO3-Nb2O5 (TLWMN) tellurite glass which possesses high linear and nonlinear refractive indices. The refractive index (n) at 1544nm and nonlinear refractive index (n2) of TLWMN glass is 2.08 and 3.78×10-11 esu, respectively. TeO2-ZnO-Na2O-La2O3 (TZNL) glass with n of 1.96 at 1544 nm and TeO2-ZnO-Li2O-Na2O-P2O5 (TZLNP) glass with low refractive index n of 1.63 at 1544 nm are used as the first cladding and the second cladding, respectively. Six small air holes are located between the core and the first glass cladding. Such kind of fiber with ~1.7 μm core and ~0.6 μm air holes are fabricated by a rod-in-tube method. The chromatic dispersion of the fiber is calculated by the fully vectorial finite difference method (FV-FDM) and becomes (+/-3 ps/nm/Km) in the wide range from 1.53 μm to 1.72 μm. And the nonlinear coefficient of present fiber is about 3.47 m-1W-1 which is much higher than that of silica MOFs. Furthermore, broad and flattened supercontinuum generation is demonstrated in 30-cm-long fiber with femtosecond laser pumping at 1557 nm. This kind of fiber has promising potential in nonlinear applications owing to the high nonlinearity and flattened dispersion profile.

  19. An evaluation of the processing conditions, structure, and properties (biaxial flexural strength and antibacterial efficacy) of sintered strontium-zinc-silicate glass ceramics.

    Science.gov (United States)

    Looney, Mark; Shea, Helen O'; Gunn, Lynda; Crowley, Dolores; Boyd, Daniel

    2013-05-01

    The use of artificial bone grafts has increased in order to satisfy a growing demand for bone replacement materials. Initial mechanical stability of synthetic bone grafts is very advantageous for certain clinical applications. Coupled with the advantage of mechanical strength, a material with inherent antibacterial properties would be very beneficial. A series of strontium-doped zinc silicate (Ca-Sr-Na-Zn-Si) glass ceramics have been characterized in terms of their crystalline structure, biaxial flexural strength and antibacterial efficacy based on the identification of optimum sintering conditions. All three glass ceramics, namely, BT110, BT111, and BT112 were found to be fully crystalline, with BT111 and BT112 comprising of biocompatible crystalline phases. The biaxial flexural strengths of the three glass ceramics ranged from 70 to 149 MPa and were shown to be superior to those of clinically established ceramics in dry conditions and following incubation in simulated physiological conditions. The bacteriostatic effect for each glass ceramic was also established, where BT112 showed an inhibitory effect against three of the most common bacteria found at implantation sites, namely, Enterococcus faecalis, methicillin-resistant Staphylococcus aureus (MRSA), and Pseudomonas aeruginosa. The results of the evaluation suggest that the materials studied offer advantages over current clinical materials and indicate the potential suitability of the glass ceramics as therapeutic bone grafts.

  20. Lithium-aluminum-zinc phosphate glasses activated with Tb3+ and Tb3+/Eu3+ for green laser medium, reddish-orange and white phosphor applications

    Science.gov (United States)

    Francisco-Rodriguez, H. I.; Lira, A.; Soriano-Romero, O.; Meza-Rocha, A. N.; Bordignon, S.; Speghini, A.; Lozada-Morales, R.; Caldiño, U.

    2018-05-01

    A spectroscopic analysis of Tb3+ and Tb3+/Eu3+ doped lithium-aluminum-zinc phosphate glasses is performed through their absorbance and photoluminescence spectra, and decay time profiles. Laser parameter values (stimulated emission cross section, effective bandwidth, gain bandwidth and optical gain) were obtained for the terbium 5D4 → 7F5 green emission from the Tb3+ singly-doped glass (LAZT) excited at 350 nm to judge the suitability of the glass phosphor for fiber lasers. A quantum yield of (47.68 ± 0.49)% was measured for the 5D4 level luminescence. Upon 350 nm excitation the LAZT glass phosphor emits green light with a color purity of 65.6% and chromaticity coordinates (0.285, 0.585) very close to those (0.29, 0.60) of European Broadcasting Union illuminant green. The Tb3+/Eu3+codoped glass emission color can be tuned from reddish-orange of 1865 K upon 318 nm excitation to warm white of 3599 K and neutral white of 4049 K upon 359 and 340 nm excitations, respectively. Upon Tb3+ excitation at 340 nm Eu3+ is sensitized by Tb3+ through a non-radiative energy transfer with an efficiency of 0.23-0.26. An electric dipole-dipole interaction might be the dominant mechanism in the Tb3+ to Eu3+ energy transfer taking place into Tb3+ - Eu3+ clusters.

  1. Optical properties and energy transfer behavior from Tb{sup 3+} to Mn{sup 2+} ions in co-doped zinc strontium phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Liang Xiaoluan [Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237 (China); Xing Zhongwen [Department of Materials Science and Engineering, Nanjing University, Nanjing 210093 (China); Liu Yinyao; Xu Weina; Yang Yunxia [Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237 (China); Chen Guorong, E-mail: grchen@ecust.edu.cn [Key Laboratory for Ultrafine Materials of Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237 (China)

    2011-10-17

    Highlights: {yields} We choose Tb{sup 3+} as the sensitizer to enhance the emission of Mn{sup 2+} ions in ZSP glasses. {yields} We make a serious of characterization on the optical properties of the glasses. {yields} Tb{sup 3+} can transfer its energy to the neighbor Mn{sup 2+} during excitation process. {yields} The energy transfer mechanism is dipolar-quadrupole interaction in phosphate glasses. {yields} Meanwhile, this process is taken by two modes: cross-relaxation and resonant transfer. - Abstract: In this paper, we report optical properties and energy transfer behavior between Tb and Mn in zinc strontium phosphate glasses. Electron Paramagnetic Resonance spectra indicate a stronger hyperfine interaction of Mn{sup 2+}-Mn{sup 2+} pairs with higher MnO concentrations. The co-existence of Tb{sup 3+} and Mn{sup 2+} ions in glasses is clearly evident in the transmittance spectra. Emission spectra show an obvious energy transfer from Tb{sup 3+} to Mn{sup 2+} ions in glasses. Based on Dexter's energy transfer formula and Reisfeld's approximation, the energy transfer mechanism was postulated to proceed via a dipolar-quadrupole interaction. The energy transfer carries out with resonant and cross-relaxation transfer modes with the understanding of Tb{sup 3+} and Mn{sup 2+} energy level diagrams. The decreasing in mean-duration time ({tau}{sub mean}) of Tb{sup 3+} ions obtained from the decay curves make a further evidence of energy transfer from Tb{sup 3+} to Mn{sup 2+} ions in glasses.

  2. Optical spectroscopy of lanthanide ions in ZnO-TeO2 glasses.

    Science.gov (United States)

    Rolli, R; Wachtler, K; Wachtler, M; Bettinelli, M; Speghini, A; Ajò, D

    2001-09-01

    Zinc tellurite glasses of compositions 19ZnO-80TeO2-1Ln2O3 with Ln = Eu, Er, Nd and Tm were prepared by melt quenching. The absorption spectra were measured and from the experimental oscillator strengths of the f-->f transitions the Judd-Ofelt parameters ohm(lambda) were obtained. The values of the ohm(lambda) parameters are in the range usually observed for oxide glasses. For Nd3+ and Er3+, luminescence spectra in the near infrared were measured and the stimulated emission cross sections sigma(p) were evaluated for some laser transitions. The high values of sigma(p), especially for Nd3+, make them possible candidates for optical applications. Fluorescence line narrowing (FLN) spectra of the Eu3+ doped glass were measured at 20 K, and the energies of the Stark components of the 7F1 and 7F2 states were obtained. A crystal field analysis was carried out assuming a C2v site symmetry. The behaviour of the crystal field ratios B22/B20 and B44/B40 agrees reasonably well with the values calculated using the geometric model proposed by Brecher and Riseberg. The crystal field strength at the Eu3+ sites appears to be very low compared to other oxide glasses.

  3. Dielectric properties of the ternary TeO2/Nb2O5/ZnO glasses

    International Nuclear Information System (INIS)

    Ahmad, Mohamad M.; Yousef, El Sayed; Moustafa, El Sayed

    2006-01-01

    Glasses of the system TeO 2 /Nb 2 O 5 /ZnO containing different concentration of ZnO (ranging from 5 to 20 mol%) were prepared. The dielectric properties over wide ranges of frequencies and temperatures were investigated as a function of ZnO content by impedance spectroscopy measurements. The impedance spectra of the present glasses were modeled by appropriate equivalent circuit. The dielectric constant has a value of 66 for the 85TeO 2 /10Nb 2 O 5 /5ZnO glass, which is three times larger than that of pure TeO 2 glass and other binary, e.g. TeO 2 /ZnCl 2 , tellurite glassy systems. The results have been analyzed in light of varying NbO 6 octahedra and NbO 4 tetrahedra of niobium oxide as zinc oxide varies from 5 to 20 mol%. The relaxation properties of the investigated glasses are presented in the electric modulus formalism, where the relaxation time and the respective activation energy are determined

  4. Elastic properties and structural studies on some zinc-borate glasses derived from ultrasonic, FT-IR and X-ray techniques

    International Nuclear Information System (INIS)

    Gaafar, M.S.; El-Aal, N.S. Abd; Gerges, O.W.; El-Amir, G.

    2009-01-01

    Glasses in the system (1 - x) [29Na 2 O- 4Al 2 O 3 - 67B 2 O 3 ]- xZnO (0 ≤ x ≤ 35 mol%), have been prepared by the melt quenching technique. Elastic properties, X-ray and FT-IR spectroscopic studies have been employed to study the role of ZnO on the structure of the investigated glass system. Elastic properties and Debye temperature have been investigated using sound wave velocity measurements at 4 MHz at room temperature. The results showed that the density increases and the molar volume decreases while both sound velocities and the determined glass transition temperatures decrease with increase in x. X-ray and infrared spectra of the glasses reveal that the borate network consists of diborate units and is affected by the increase in the concentration of ZnO content. These results are interpreted in terms of the decrease in the N 4 values (fraction of tetrahedral coordinated boron atoms), and substitution of longer bond lengths of Zn-O in place of shorter B-O bond. The results indicate that Zinc ions have been substituted for boron ions as tetrahedral network former ions. The elastic moduli are observed to increase with the increase of ZnO content.

  5. Sol-gel synthesis and in vitro bioactivity of copper and zinc-doped silicate bioactive glasses and glass-ceramics.

    Science.gov (United States)

    Bejarano, Julian; Caviedes, Pablo; Palza, Humberto

    2015-03-11

    Metal doping of bioactive glasses based on ternary 60SiO2-36CaO-4P2O5 (58S) and quaternary 60SiO2-25CaO-11Na2O-4P2O5 (NaBG) mol% compositions synthesized using a sol-gel process was analyzed. In particular, the effect of incorporating 1, 5 and 10 mol% of CuO and ZnO (replacing equivalent quantities of CaO) on the texture, in vitro bioactivity, and cytocompatibility of these materials was evaluated. Our results showed that the addition of metal ions can modulate the textural property of the matrix and its crystal structure. Regarding the bioactivity, after soaking in simulated body fluid (SBF) undoped 58S and NaBG glasses developed an apatite surface layer that was reduced in the doped glasses depending on the type of metal and its concentration with Zn displaying the largest inhibitions. Both the ion release from samples and the ion adsorption from the medium depended on the type of matrix with 58S glasses showing the highest values. Pure NaBG glass was more cytocompatible to osteoblast-like cells (SaOS-2) than pure 58S glass as tested by 3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide (MTT) assay. The incorporation of metal ions decreased the cytocompatibility of the glasses depending on their concentration and on the glass matrix doped. Our results show that by changing the glass composition and by adding Cu or Zn, bioactive materials with different textures, bioactivity and cytocompatibility can be synthesized.

  6. Catalases are NAD(PH-dependent tellurite reductases.

    Directory of Open Access Journals (Sweden)

    Iván L Calderón

    2006-12-01

    Full Text Available Reactive oxygen species damage intracellular targets and are implicated in cancer, genetic disease, mutagenesis, and aging. Catalases are among the key enzymatic defenses against one of the most physiologically abundant reactive oxygen species, hydrogen peroxide. The well-studied, heme-dependent catalases accelerate the rate of the dismutation of peroxide to molecular oxygen and water with near kinetic perfection. Many catalases also bind the cofactors NADPH and NADH tenaciously, but, surprisingly, NAD(PH is not required for their dismutase activity. Although NAD(PH protects bovine catalase against oxidative damage by its peroxide substrate, the catalytic role of the nicotinamide cofactor in the function of this enzyme has remained a biochemical mystery to date. Anions formed by heavy metal oxides are among the most highly reactive, natural oxidizing agents. Here, we show that a natural isolate of Staphylococcus epidermidis resistant to tellurite detoxifies this anion thanks to a novel activity of its catalase, and that a subset of both bacterial and mammalian catalases carry out the NAD(PH-dependent reduction of soluble tellurite ion (TeO(3(2- to the less toxic, insoluble metal, tellurium (Te(o, in vitro. An Escherichia coli mutant defective in the KatG catalase/peroxidase is sensitive to tellurite, and expression of the S. epidermidis catalase gene in a heterologous E. coli host confers increased resistance to tellurite as well as to hydrogen peroxide in vivo, arguing that S. epidermidis catalase provides a physiological line of defense against both of these strong oxidizing agents. Kinetic studies reveal that bovine catalase reduces tellurite with a low Michaelis-Menten constant, a result suggesting that tellurite is among the natural substrates of this enzyme. The reduction of tellurite by bovine catalase occurs at the expense of producing the highly reactive superoxide radical.

  7. Acoustic relaxation of some lead niobium tellurite glasses

    Indian Academy of Sciences (India)

    This dependence was analysed in terms of the loss of standard linear solid type, with low dispersion and a .... of other components such as alkali and alkali earth elements. Moreover, the ... The variations of ultrasonic attenuation coefficient for.

  8. Li ion conductivities in boro-tellurite glasses

    Indian Academy of Sciences (India)

    Unknown

    nature of the added alkali-salt, changes in bonding features and also the equilibrium of ... (to remove water from LiBO2⋅2H2O) for 2 h. The mixture was then ..... particularly at higher temperatures. β and s do not bear out the relation β = 1-s.

  9. All-solid tellurite optical fiber with transversely disordered refractive index profile and its optical image transport performance

    Science.gov (United States)

    Tong, Hoang Tuan; Kuroyanagi, Shunei; Suzuki, Takenobu; Ohishi, Yasutake

    2018-02-01

    All-solid tellurite-glass optical rod and fiber with transversely-disordered refractive index profile were successfully fabricated to study the transport of infrared images by using transverse localization of light. The fabrication was carried out by using stack-and-draw and rod-in-tube techniques. The fabricated tellurite optical rod and fiber were composed of high-index and low-index units which were arranged randomly in the transverse plane but were invariant in the longitudinal direction. The diameter of each unit was approximately 1.0 μm. The high-index and low-index materials were TeO2-Li2O-WO3-MoO3-Nb2O5 (TLWMN) glass and TeO2-ZnO-Na2O-La2O3 (TZNL) glass, respectively. At 1550 nm, their refractive index difference Δn is 0.096. To investigate the optical image transport capability, A CW laser light at 1550 nm was used as an input probe beam and the 1951 U.S. Air Force test target was installed in front of 10-cm-long segments of the fabricated rod and fiber in the experimental setup. The output signal was recorded by a beam profiler. As a result, clear transported images of numbers and lines on the test target were obtained.

  10. Orange and reddish-orange light emitting phosphors: Sm{sup 3+} and Sm{sup 3+}/Eu{sup 3+} doped zinc phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Meza-Rocha, A.N., E-mail: ameza@fis.cinvestav.mx [Departamento de Física, Universidad Autónoma Metropolitana-Iztapalapa, P.O. Box 55-534, 09340 México D.F., México (Mexico); Speghini, A. [Dipartimento di Biotecnologie, Universita di Verona and INSTM, UdR Verona, Strada Le Grazie 15, I-37314 Verona (Italy); IFAC CNR, Nello Carrara Institute of Applied Physics, MDF Lab, I-50019 Sesto Fiorentino, FI (Italy); Bettinelli, M. [Dipartimento di Biotecnologie, Universita di Verona and INSTM, UdR Verona, Strada Le Grazie 15, I-37314 Verona (Italy); Caldiño, U. [Departamento de Física, Universidad Autónoma Metropolitana-Iztapalapa, P.O. Box 55-534, 09340 México D.F., México (Mexico)

    2015-11-15

    A spectroscopy study of Sm{sup 3+} and Sm{sup 3+}/Eu{sup 3+} doped zinc phosphate glasses is performed through photoluminescence spectra and decay time profile measurements. Under Sm{sup 3+} excitation at 344 nm, the Sm{sup 3+} singly doped glass shows an orange global emission with x=0.579 and y=0.414 CIE1931 chromaticity coordinates, whereas the Sm{sup 3+}/Eu{sup 3+} co-doped sample exhibits orange overall emissions (x=0.581 and y=0.398, and x=0.595 and y=0.387) and reddish-orange overall emission (x=0.634 and y=0.355) upon excitations at 344, 360 and 393 nm, respectively. Such luminescence from the co-doped sample is originated by the simultaneous emission of Sm{sup 3+} and Eu{sup 3+}. Under Sm{sup 3+} excitation at 344 and 360 nm, the Eu{sup 3+} emission is sensitized and enhanced by Sm{sup 3+} through a non-radiative energy transfer process. The non-radiative nature was inferred from the shortening of the Sm{sup 3+} lifetime observed in the Sm{sup 3+}/Eu{sup 3+} co-doped sample. An analysis of the Sm{sup 3+} emission decay time profiles using the Inokuti–Hirayama model suggests that an electric quadrupole–quadrupole interaction into Sm–Eu clusters might dominate the energy transfer process, with an efficiency of 0.17. - Highlights: • Zinc phosphate glasses are optically activated with Sm{sup 3+}/Eu{sup 3+} (ZPOSmEu). • Non-radiative energy transfer Sm{sup 3+}→Eu{sup 3+} takes place in ZPOSmEu. • ZPOSmEu overall emission can be modulated with the excitation wavelength. • ZPOSmEu might be useful as orange/reddish-orange phosphor for UV-white LEDs.

  11. Fabrication and characterization of an all-solid tellurite-phosphate photonic bandgap fiber.

    Science.gov (United States)

    Cheng, Tonglei; Sakai, Yukiko; Suzuki, Takenobu; Ohishi, Yasutake

    2015-05-01

    We present an all-solid tellurite-phosphate photonic bandgap fiber (PBGF) with two layers of high-index rods (TeO2-Li2O-WO3-MoO3-Nb2O5, TLWMN) in the cladding (TeO2-ZnO-Li2O-K2O-Al2O3-P2O5, TZLKAP). TLWMN and TZLKAP glasses have good compatibility for fabricating the all-solid PBGF. Photonic bandgap (PBG) properties are calculated by the plane wave expansion method (PWM), and the results agree well with the measured transmission spectrum. Furthermore, the modal field patterns are measured at ∼1300 and 1520 nm, respectively. The light is confined to the core at ∼1300  nm and lost in the cladding at ∼1520  nm, which match well with the calculated modal field intensities.

  12. Raman spectra of TeO2-PbCl2 glasses

    Czech Academy of Sciences Publication Activity Database

    Ležal, Dimitrij; Bludská, Jana; Horák, J.; Sklenář, A.; Karamazov, S.; Vlček, M.

    2002-01-01

    Roč. 43, č. 6 (2002), s. 296-299 ISSN 0031-9090 Institutional research plan: CEZ:AV0Z4032918 Keywords : tellurite glasses * TeO2glass * model Subject RIV: CA - Inorganic Chemistry Impact factor: 0.691, year: 2002

  13. Thermal analyses, spectral characterization and structural interpretation of Nd3+/Er3+ ions co-doped TeO2-ZnCl2 glasses system

    Science.gov (United States)

    Ahmed, Kasim F.; Ibrahim, Saeed O.; Sahar, Md. R.; Mawlud, Saman Q.; Khizir, Hersh A.

    2017-09-01

    The Nd3+/Er3+ ions co-doped in the system of zinc-tellurite with the composition of (70-2x)TeO2-30ZnCl2-xNd2O3-xEr2O3 concentration from 1.0 to 3.0 mol% (x=1, 2 and 3) glasses were prepared by using conventional melt-quenching technique. The amorphous nature of the glass been confirmed by using X-RAY Diffraction Spectroscopy. Thermal characteristic were determined using a DTA. The obtained results discussed in terms of the glass structure. The glass structure studied by means of FTIR. Seven significant vibrational peaks around 471, 687, 742, 768, 1632, 2833 and 3378 cm-1 which correspond to the structural bonding of the glass are observed in a range of 400-4000cm-1. The peaks observed are consistent with the stretching and bending vibrations of the Te-O, TeO4 trigonal bipyramids, TeO3 trigonal pyramids, Te-O-Te and OH linkages respectively.

  14. Characterization and spectroscopic studies of multi-component calcium zinc bismuth phosphate glass ceramics doped with iron ions

    Science.gov (United States)

    Kumar, A. Suneel; Narendrudu, T.; Suresh, S.; Ram, G. Chinna; Rao, M. V. Sambasiva; Tirupataiah, Ch.; Rao, D. Krishna

    2018-04-01

    Glass ceramics with the composition 10CaF2-20ZnO-(15-x)Bi2O3-55P2O5:x Fe2O3(0≤x≤2.5) were synthesized by melt-quenching technique and heat treatment. These glass ceramics were characterized by XRD and SEM. Spectroscopic studies such as optical absorption, EPR were also carried out on these glass ceramics. From the absorption spectra the observed bands around 438 and 660nm are the octahedral transitions of Fe3+ (d5) ions and another band at about 536 nm is the tetrahedral transition of Fe3+ (d5) ions. The absorption spectrum also consist of a band around 991 nm and is attributed to the octahedral transition of Fe2+ ions. The EPR spectra of the prepared glass ceramics have exhibited two resonance signals one at g1=4.32 and another signal at g2=2.008. The observed decrease in band gap energy up to 2 mol% Fe2O3 doped glass ceramics is an evidence for the change of environment around iron ions and ligands from more covalent to less covalent (ionic) and induces higher concentration of NBOs which causes the depolymerization of the glass ceramic network.

  15. Thermal, structural and spectroscopic properties of Pr3+-doped lead zinc borate glasses modified by alkali metal ions

    Directory of Open Access Journals (Sweden)

    M.V. Sasi kumar

    2017-07-01

    Full Text Available This paper offers a study on Pr3+-doped alkali and mixed-alkali borate glasses prepared by the melt quenching technique and characterized by thermal, structural and spectroscopic studies. The amorphous nature of the glassy systems was identified based on X-ray diffraction. The thermal behaviour of glasses was studied using differential thermal analysis (DTA. The functional groups contained in the glasses were identified by Fourier transform infrared spectroscopy (FTIR. Spectral intensities were evaluated from the absorption spectra and used for calculating J–O intensity parameters, Ωλ (λ = 2, 4 and 6. Further, these parameters were used for calculating different radiative properties. The best radiative state was identified as the laser transition state among the various states. Emission analysis was performed for this state by calculating the branching ratios and stimulated emission cross sections (σp for all the prepared glasses. These studies suggest that borate glasses are useful for visible fluorescence.

  16. Effects of titanium nanoparticles on self-cleaning and structural features of zinc-magnesium-phosphate glass

    International Nuclear Information System (INIS)

    Ismail, S.F.; Sahar, M.R.; Ghoshal, S.K.

    2016-01-01

    Graphical abstract: Water contact angle for sample S2, S3, S4 and S5. The water contact angle increased with increased the titanium NPs content (mol%). - Highlights: • ZnO–MgO–P_2O_5 embedded TiO_2 NPs prepared by conventional melt-quenching method. • The amorphous nature is confirmed by X-ray diffraction spectroscopy. • The structural characteristics of glasses is investigated using FTIR and Raman. • Wettability of the glasses surface by water contact angle. - Abstract: The loss of glass transparency on surface pollutants contamination unless inhibited not only causes vision obscurity but also responsible for major aesthetic damages of cultural heritage. It is due to the sticking of fine dirt particles on wetting layers, a complex process with several possible ramifications still to be clarified. We report the influence of titanium dioxide or titania (TiO_2) nanoparticles (NPs) on the structural and self-cleaning properties of zinc–magnesium–phosphate glasses. Following melt-quenching method glass samples of optimized composition (42 − x)P_2O_5–8MgO–50ZnO–xTiO_2 with x = 0, 1, 2, 3 and 4 mol% are prepared. XRD patterns verified their amorphous nature and TEM images revealed the nucleation of TiO_2 NPs of average diameter ≈4.05 ± 0.01 nm. Fourier transform infrared (FTIR) spectra displayed four absorption band centred at 1618–3438 cm"−"1, 902– 931 cm"−"1, 757–762 cm"−"1 and 531–560 cm"−"1. Raman spectra exhibited four peaks each accompanied by a blue-shift. Water contact angle is found to increase with the increase of titanium NPs concentration into the amorphous matrix. This knowledge can be used to set up strategies and selective treatments to preventing glass transparency loss via the modification of self-cleaning attributes.

  17. In Vitro Comparison of Zinc Phosphate and Glass Ionomers Ability to Inhibit Decalcification under and Adjacent to Orthodontic Bands.

    Science.gov (United States)

    1985-08-01

    confer the ability to leach fluoride ions into the surrounding tooth enamel . Kidd 3 7 using an artifical caries tec- hnique with a diffusion controlled...5 - Enamel Changes Scoring System- 1. NONE: No color change evident 2. MILD: Slight change in enamel color 3.MODERATE: Definate whitening of enamel ...to adhere to stainless steel and to tooth enamel with a chemical bond 51 . Zinc phosphate, on the other hand, does not chemically adhere to enamel or

  18. Theoretical studies of the spin Hamiltonian parameters and local distortions for Cu{sup 2+} in alkaline earth lead zinc phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Bo-Kun; Yuan, Zi-Yi; Liu, Zi-Xuan; Jiang, Shi-Xin; Liu, Zheng; Yao, Zi-Jian [University of Electronic Science and Technology of China, Chengdu (China). School of Yingcai Honors; Wu, Shao-Yi; Teng, Bao-Hua; Wu, Ming-He [University of Electronic Science and Technology of China, Chengdu (China). Dept. of Applied Physics

    2016-11-01

    The spin Hamiltonian parameters and local structures are theoretically studied for Cu{sup 2+}-doped alkaline earth lead zinc phosphate (RPPZ, R=Mg, Ca, Sr, and Ba) glasses based on the high-order perturbation calculations for a tetragonally elongated octahedral 3d{sup 9} cluster. The relative elongation ratios are found to be ρ ∼ 3.2%, 4.4%, 4.6%, and 3.3% for R=Mg, Ca, Sr, and Ba, respectively, because of the Jahn-Teller effect. The whole decreasing crystal-field strength Dq and orbital reduction factor k from Mg to Sr are ascribed to the weakening electrostatic coulombic interactions and the increasing probability of productivity of nonbridge oxygen (and hence increasing Cu{sup 2+}-O{sup 2-} electron cloud admixtures) under PbO addition, respectively, with increasing alkali earth ionic radius. The anomalies (the largest Dq and the next highest k among the systems) for R=Ba are attributed to the cross linkage of this large cation in the network. The overall increasing order (Mg≤Baglasses containing copper dopants.

  19. Comparative studies on antisickling properties of thiocyanate, tellurite and hydroxyurea

    International Nuclear Information System (INIS)

    Oyewole, O.I.; Maloma, S.O.; Adebayo, J.O.

    2008-01-01

    Thiocyanate, hydroxyurea and tellurite are among chemical agents being used as antisickling drugs and currently receiving attention for research. The antisickling properties of these drugs was investigated and compared in this study. Human sickle blood was incubated with the drugs in vitro at concentrations related to the dose used by patients in vivo. Haemoglobin function and specific aspects of the sickling process were then measured by employing standard methods used in screening potential antisickling agents. All the drugs significantly inhibited (P<0.05) sickling of deoxygenated sickle blood and formation of irreversibly sickled cell in a dose and time-dependent manner. Thiocyanate, hydroxyurea and tellurite inhibited sickling optimally at 20 mM, 40 mM and 50 microM respectively. Thiocyanate and hydroxyurea prolonged sickle red blood cell life span as indicated in the significant decrease in haemolysis and osmotic fragility while tellurite increased these blood parameters. The three drugs also caused significant prolongation of delay time of haemoglobin S (HbS) polymerization while thiocyanate and hydroxyurea significantly increased (P<0.05) both solubility ratio and oxygen affinity of HbS. Results obtained in this study suggest that the three drugs have remarkable antisickling potential in vitro with thiocyanate being the most efficient followed by tellurite. (author)

  20. New greenish-yellow and yellowish-green emitting glass phosphors: Tb{sup 3+}/Eu{sup 3+} and Ce{sup 3+}/Tb{sup 3+}/Eu{sup 3+} in zinc phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Caldino, U., E-mail: cald@xanum.uam.mx [Departamento de Fisica, Universidad Autonoma Metropolitana-Iztapalapa, P.O. Box 55-534, 09340 Mexico D.F. (Mexico); Alvarez, E. [Departamento de Fisica, Universidad de Sonora (UNISON), Boulevard Luis Encinas y Rosales s/n, Hermosillo, Sonora 83000, Mexico (Mexico); Speghini, A. [Dipartimento di Biotecnologie, Universita di Verona, and INSTM, UdR Verona, Strada Le Grazie 15, I-37314 Verona (Italy); IFAC CNR, Nello Carrara Institute of Applied Physics, MDF Lab, I-50019 Sesto Fiorentino, FI (Italy); Bettinelli, M. [Dipartimento di Biotecnologie, Universita di Verona, and INSTM, UdR Verona, Strada Le Grazie 15, I-37314 Verona (Italy)

    2013-03-15

    A spectroscopic investigation of zinc phosphate glasses activated with Eu{sup 3+}, Tb{sup 3+}/Eu{sup 3+} and Ce{sup 3+}/Tb{sup 3+}/Eu{sup 3+} ions is performed through photoluminescence spectra and decay time measurements. Greenish-yellow light emission, with x=0.42 and y=0.50 CIE1931 chromaticity coordinates, is obtained in the 5.0% Tb(PO{sub 3}){sub 3}-2.0% Eu(PO{sub 3}){sub 3} codoped zinc phosphate glass upon Tb{sup 3+} excitation at 340 nm. Such greenish-yellow luminescence is generated mainly by the {sup 5}D{sub 4}{yields}{sup 7}F{sub 6,5} and {sup 5}D{sub 0}{yields}{sup 7}F{sub 1,2} emissions of Tb{sup 3+} and Eu{sup 3+}, respectively, europium being sensitized by terbium through a non-radiative energy transfer. By codoping with 0.1 Ce(PO{sub 3}){sub 3} in addition to Tb{sup 3+}/Eu{sup 3+} yellowish-green light emission with CIE1931 chromaticity coordinates, x=0.33 and y=0.48, is achieved through non-radiative energy transfer from Ce{sup 3+} to Tb{sup 3+} and from Ce{sup 3+} via Tb{sup 3+} to Eu{sup 3+} upon 280 nm excitation (peak emission wavelength of AlGaN-based LEDs). - Highlights: Black-Right-Pointing-Pointer Zn(PO{sub 3}){sub 2} glasses are optically activated with Tb{sup 3+}/Eu{sup 3+} (ZPO5Tb2Eu) and Ce{sup 3+}/Eu{sup 3+}/Tb{sup 3+} (ZPOCe5Tb2Eu). Black-Right-Pointing-Pointer Non-radiative energy transfer Tb{sup 3+}{yields}Eu{sup 3+} takes place in ZPO5Tb2Eu. Black-Right-Pointing-Pointer Greenish-yellow light is generated by ZPO5Tb2Eu pumped with 340 nm-UV light. Black-Right-Pointing-Pointer Non-radiative energy transfer Ce{sup 3+}{yields}Tb{sup 3+} and Ce{sup 3+}{yields}Eu{sup 3+} via Tb{sup 3+} takes place in ZPOCe5Tb2Eu. Black-Right-Pointing-Pointer Yellowish-green light is generated by ZPOCe5Tb2Eu pumped with 280 nm-UV light (AlGaN-LEDs).

  1. Raman, photoluminescence and EPR spectroscopic characterization of europium(III) oxide–lead dioxide–tellurite glassy network

    Energy Technology Data Exchange (ETDEWEB)

    Dehelean, A. [National Research and Development Institute for Isotopic and Molecular Technologies, Cluj-Napoca (Romania); Rada, S. [Technical University of Cluj-Napoca (Romania); Popa, A.; Suciu, R.C. [National Research and Development Institute for Isotopic and Molecular Technologies, Cluj-Napoca (Romania); Culea, E., E-mail: eugen.culea@phys.utcluj.ro [Technical University of Cluj-Napoca (Romania)

    2016-09-15

    Raman, photoluminescence and EPR spectroscopies were used to characterize some xEu{sub 2}O{sub 3}·(100−x)[4TeO{sub 2}·PbO{sub 2}] glasses with x=0–50 mol% obtained by melt quenching technique. Raman spectra of these glasses were interpreted in terms of vibration modes of deformed Te–O–Te linkages due to the intercalation of [PbO{sub n}] and [EuO{sub n}] entities produced by addition of Eu{sub 2}O{sub 3} to the host lead–tellurite glass. Photoluminescence spectra of xEu{sub 2}O{sub 3}·(100−x)[4TeO{sub 2}·PbO{sub 2}] glasses reveal the presence of Pb{sup 2+}, Eu{sup 2+} and Eu{sup 3+} ions. EPR data confirm the presence of Eu{sup 2+} ions in the europium–lead–tellurite glassy network and offer information about the compositional evolution of the Eu{sup 2+} ions local environment and Eu{sup 3+}↔Eu{sup 2+} redox process. PL and EPR data show that the decrease of the Eu{sup 2+} ions luminescence intensity for the x≥40 mol% Eu{sub 2}O{sub 3} region is not due to the clusterization of europium ions but is due the decrease of the amount of Eu{sup 2+} ions as result of changes in the Eu{sup 3+}→Eu{sup 2+} redox equilibrium.

  2. Effects of titanium nanoparticles on self-cleaning and structural features of zinc-magnesium-phosphate glass

    Energy Technology Data Exchange (ETDEWEB)

    Ismail, S.F.; Sahar, M.R., E-mail: mrahim057@gmail.com; Ghoshal, S.K.

    2016-02-15

    Graphical abstract: Water contact angle for sample S2, S3, S4 and S5. The water contact angle increased with increased the titanium NPs content (mol%). - Highlights: • ZnO–MgO–P{sub 2}O{sub 5} embedded TiO{sub 2} NPs prepared by conventional melt-quenching method. • The amorphous nature is confirmed by X-ray diffraction spectroscopy. • The structural characteristics of glasses is investigated using FTIR and Raman. • Wettability of the glasses surface by water contact angle. - Abstract: The loss of glass transparency on surface pollutants contamination unless inhibited not only causes vision obscurity but also responsible for major aesthetic damages of cultural heritage. It is due to the sticking of fine dirt particles on wetting layers, a complex process with several possible ramifications still to be clarified. We report the influence of titanium dioxide or titania (TiO{sub 2}) nanoparticles (NPs) on the structural and self-cleaning properties of zinc–magnesium–phosphate glasses. Following melt-quenching method glass samples of optimized composition (42 − x)P{sub 2}O{sub 5}–8MgO–50ZnO–xTiO{sub 2} with x = 0, 1, 2, 3 and 4 mol% are prepared. XRD patterns verified their amorphous nature and TEM images revealed the nucleation of TiO{sub 2} NPs of average diameter ≈4.05 ± 0.01 nm. Fourier transform infrared (FTIR) spectra displayed four absorption band centred at 1618–3438 cm{sup −1}, 902– 931 cm{sup −1}, 757–762 cm{sup −1} and 531–560 cm{sup −1}. Raman spectra exhibited four peaks each accompanied by a blue-shift. Water contact angle is found to increase with the increase of titanium NPs concentration into the amorphous matrix. This knowledge can be used to set up strategies and selective treatments to preventing glass transparency loss via the modification of self-cleaning attributes.

  3. Thermal, optical and structural properties of glasses within the TeO{sub 2}-TiO{sub 2}-ZnO system

    Energy Technology Data Exchange (ETDEWEB)

    Ghribi, N. [CNRS-Université de Limoges, Science des Procédés Céramiques et de Traitements de Surface, UMR7315 CNRS, Centre Européen de la Céramique, 12 rue Atlantis, 87068 Limoges Cedex (France); Sciences des Matériaux et de l’Environnement Laboratory, Sfax University, Route de Soukra km 4, 3038 Sfax (Tunisia); Dutreilh-Colas, M.; Duclère, J.-R. [CNRS-Université de Limoges, Science des Procédés Céramiques et de Traitements de Surface, UMR7315 CNRS, Centre Européen de la Céramique, 12 rue Atlantis, 87068 Limoges Cedex (France); Hayakawa, T. [Field of Advanced Energy Conversion, Department of Frontier Materials, Nagoya Institute of Technology, Gokiso, Showa, Nagoya 466-8555 (Japan); Carreaud, J. [CNRS-Université de Limoges, Science des Procédés Céramiques et de Traitements de Surface, UMR7315 CNRS, Centre Européen de la Céramique, 12 rue Atlantis, 87068 Limoges Cedex (France); Karray, R.; Kabadou, A. [Sciences des Matériaux et de l’Environnement Laboratory, Sfax University, Route de Soukra km 4, 3038 Sfax (Tunisia); and others

    2015-02-15

    Highlights: • This paper reports on original results on new tellurium oxide-based glasses which are actually very promising glasses in the field of nonlinear optics. • We present for the first time the determination of a new glassy system and the structure of the glasses has been investigated using Raman spectroscopy which is actually the most adapted method in laboratory to study the local structure of tellurite glasses, a detail linear and non-linear optical study is also presented. - Abstract: A glass-forming domain was evidenced and studied within the TeO{sub 2}-TiO{sub 2}-ZnO system. Density, glass transition temperature (T{sub g}) and onset crystallization temperature (T{sub 0}) were measured and interpreted as a function of the zinc oxide mole fraction for relevant glasses. It was concluded that the zinc oxide favors the thermal stability of glasses. On the other hand, the impact of TiO{sub 2} addition is even more pronounced on the enhancement of the thermal stability. The optical transmission was recorded for series of glasses in the UV-Visible-NIR range. Refractive index and optical band gap were extracted from these measurements and studied as a function of the ZnO content. Linear refractive indices and optical band gap were found to decrease and increase respectively, with increasing ZnO content. The third-order non-linear susceptibility Re (χ{sup 3}), measured for two series of glasses (TiO{sub 2} content was fixed either to 5 or 10 mol%), was found to progressively decrease when the ZnO concentration increases. The impact of ZnO modifier on the glass structure was discussed based on Raman spectroscopy data. We evidenced that TiO{sub 2} does not change drastically the glass network, whereas ZnO leads in a first step to the breaking of the Te-O-Te bridges, inducing network depolymerization. A further addition in ZnO leads to the formation of new Te-O-Zn and Zn-O-Zn linkages.

  4. Structural and optical studies of Er3+-doped alkali/alkaline oxide containing zinc boro-aluminosilicate glasses for 1.5 μm optical amplifier applications

    Science.gov (United States)

    Kaky, Kawa M.; Lakshminarayana, G.; Baki, S. O.; Lira, A.; Caldiño, U.; Meza-Rocha, A. N.; Falcony, C.; Kityk, I. V.; Taufiq-Yap, Y. H.; Halimah, M. K.; Mahdi, M. A.

    2017-07-01

    In the present work, we report on the optical spectral properties of Er3+-doped zinc boro-aluminosilicate glasses with an addition of 10 mol % alkali/alkaline modifier regarding the fabrication of new optical materials for optical amplifiers. A total of 10 glasses were prepared using melt-quenching technique with the compositions (40-x)B2O3 - 10SiO2 - 10Al2O3 - 30ZnO - 10Li2O - xEr2O3 and (40-x)B2O3 - 10SiO2 - 10Al2O3 - 30ZnO - 10MgO - xEr2O3 (x = 0.1, 0.25, 0.5, 1.0, and 2.0 mol %). We confirm the amorphous-like structure for all the prepared glasses using X-ray diffraction (XRD). To study the functional groups of the glass composition after the melt-quenching process, Raman spectroscopy was used, and various structural units such as triangular and tetrahedral-borates (BO3 and BO4) have been identified. All the samples were characterized using optical absorption for UV, visible and NIR regions. Judd-Ofelt (JO) intensity parameters (Ωλ, λ = 2, 4 and 6) were calculated from the optical absorption spectra of two glasses LiEr 2.0 and MgEr 2.0 (doped with 2 mol % of Er3+). JO parameters for LiEr 2.0 and MgEr 2.0 glasses follow the trend as Ω6>Ω2>Ω4. Using Judd-Ofelt intensity parameters, we obtained radiative probability A (S-1), branching ratios (β), radiative decay lifetimes τrad (μs) of emissions from excited Er+3 ions in LiEr 2.0 and MgEr 2.0 to all lower levels. Quantum efficiency (η) of 4I13/2 and 4S3/2 levels for LiEr 2.0 and MgEr 2.0 with and without 4D7/2 level was calculated using the radiative decay lifetimes τrad. (μs) and measured lifetimes τexp. (μs). We measured the visible photoluminescence under 377 nm excitation for both LiEr and MgEr glass series within the region 390-580 nm. Three bands were observed in the visible region at 407 nm, 530 nm, and 554 nm, as a result of 2H9/2 → 4I15/2, 2H11/2 → 4I15/2 and 4S3/2 → 4I15/2 transitions, respectively. Decay lifetimes for emissions at 407 nm, 530 nm, and 554 nm were measured and they show

  5. Enhanced green upconversion by controlled ceramization of Er3+–Yb3+ co-doped sodium niobium tellurite glass–ceramics for low temperature sensors

    International Nuclear Information System (INIS)

    Suresh Kumar, J.; Pavani, K.; Graça, M.P.F.; Soares, M.J.

    2014-01-01

    Highlights: • Upconversion luminescence improved in glass–ceramics compared to host glass. • Judd–Ofelt and radiative parameters calculated. • NIR decay curve results concur the results of improved luminescence. • Temperature dependent upconversion support the use of materials for sensors. - Abstract: Tellurite based glasses are well-known for their upconversion properties besides having a disadvantage of low mechanical strength dragging them away from practical applications. The present work deals with preparation of sodium niobium tellurite (SNT) glasses using melt quenching method, in which small quantities of boron and silicon in the form of oxides are added to improve their mechanical properties. Controlled heat treatment is performed to ceramize the prepared glasses based on the thermal data given by DTA. XRD and SEM profiles of the glass–ceramics which confirmed the formation of crystalline monoclinic Sodium Tellurium Niobium Oxide (Na 1.4 Nb 3 Te 4.9 O 18 ) phase (JCPDS card No. 04–011-7556). Upconversion measurements in the visible region were made for the prepared Er 3+ –Yb 3+ co-doped glasses and glass–ceramics with 980 nm laser excitation varying the laser power and concentration of Er 3+ ions. Results showed that the upconversion luminescence intensity was enhanced by ten times in SNT glass–ceramics compared to that in the SNT glasses. Decay curves give evidence of high performance of glass–ceramics compared to glasses due to ceramization and structural changes. Temperature dependent visible upconversion was performed to test the ability of efficient SNT glass–ceramic at low temperatures and variation of upconversion intensities was studied

  6. Role of Tellurite Resistance Operon in Filamentous Growth of Yersinia pestis in Macrophages.

    Science.gov (United States)

    Ponnusamy, Duraisamy; Clinkenbeard, Kenneth D

    2015-01-01

    Yersinia pestis initiates infection by parasitism of host macrophages. In response to macrophage infections, intracellular Y. pestis can assume a filamentous cellular morphology which may mediate resistance to host cell innate immune responses. We previously observed the expression of Y. pestis tellurite resistance proteins TerD and TerE from the terZABCDE operon during macrophage infections. Others have observed a filamentous response associated with expression of tellurite resistance operon in Escherichia coli exposed to tellurite. Therefore, in this study we examine the potential role of Y. pestis tellurite resistance operon in filamentous cellular morphology during macrophage infections. In vitro treatment of Y. pestis culture with sodium tellurite (Na2TeO3) caused the bacterial cells to assume a filamentous phenotype similar to the filamentous phenotype observed during macrophage infections. A deletion mutant for genes terZAB abolished the filamentous morphologic response to tellurite exposure or intracellular parasitism, but without affecting tellurite resistance. However, a terZABCDE deletion mutant abolished both filamentous morphologic response and tellurite resistance. Complementation of the terZABCDE deletion mutant with terCDE, but not terZAB, partially restored tellurite resistance. When the terZABCDE deletion mutant was complemented with terZAB or terCDE, Y. pestis exhibited filamentous morphology during macrophage infections as well as while these complemented genes were being expressed under an in vitro condition. Further in E. coli, expression of Y. pestis terZAB, but not terCDE, conferred a filamentous phenotype. These findings support the role of Y. pestis terZAB mediation of the filamentous response phenotype; whereas, terCDE confers tellurite resistance. Although the beneficial role of filamentous morphological responses by Y. pestis during macrophage infections is yet to be fully defined, it may be a bacterial adaptive strategy to macrophage

  7. Study of gamma radiation shielding properties of ZnO-TeO_2 glasses

    International Nuclear Information System (INIS)

    Issa, Shama A.M.; Sayyed, M.I.; Kurudirek, Murat

    2017-01-01

    Mass attenuation coefficient (μm), half value layer (HVL) and mean free path (MFP) for xZnO-(100-x)TeO_2, where x=10, 15, 20, 25, 30, 35 and 40 mol%, have been measured for 0.662, 1.173 and 1.33 MeV photons emitted from "1"3"7Cs and "6"0Co using a 3 x 3 inch NaI (Tl) detector. Some relevant parameters such as effective atomic numbers (Z_e_f_f) and electron densities (Nel) of glass samples have been also calculated in the photon energy range of 0.015-15 MeV. Moreover, gamma-ray energy absorption buildup factor (EABF) and exposure buildup factor (EBF) were estimated using a five-parameter Geometric Progression (GP) fitting approximation, for penetration depths up to 40 MFP and in the energy range 0.015-15 MeV. The measured mass attenuation coefficients were found to agree satisfactorily with the theoretical values obtained through WinXcom. Effective atomic numbers (Z_e_f_f) and electron densities (N_e_l) were found to be the highest for 40ZnO-60TeO_2 glass in the energy range 0.04-0.2 MeV. The 10ZnO-90TeO_2 glass sample has lower values of gamma-ray EBFs in the intermediate energy region. The reported new data on radiation shielding characteristics of zinc tellurite glasses should be beneficial from the point of proper gamma shield designs when intended to be used as radiation shields. (author)

  8. Down-shifting by energy transfer in Tb{sup 3+}/Dy{sup 3+} co-doped zinc phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Caldiño, U., E-mail: cald@xanum.uam.mx [Departamento de Física, Universidad Autónoma Metropolitana-Iztapalapa, P.O. Box 55-534, México, D.F. 09340 (Mexico); Muñoz H, G.; Camarillo, I. [Departamento de Física, Universidad Autónoma Metropolitana-Iztapalapa, P.O. Box 55-534, México, D.F. 09340 (Mexico); Speghini, A. [Dipartimento di Biotecnologie, Università di Verona, and INSTM, UdR Verona, Strada Le Grazie 15, I-37314 Verona (Italy); IFAC CNR, Nello Carrara Institute of Applied Physics, MDF Lab, I-50019 Sesto Fiorentino, FI (Italy); Bettinelli, M. [Dipartimento di Biotecnologie, Università di Verona, and INSTM, UdR Verona, Strada Le Grazie 15, I-37314 Verona (Italy)

    2015-05-15

    An optical spectroscopy investigation of zinc phosphate glasses activated with Tb{sup 3+}/Dy{sup 3+} ions is carried out through photoluminescence spectra and decay time measurements. The emission color can be adjusted from yellow–green light, with CIE1931 chromaticity coordinates (0.36,0.44), toward the white light region (0.35,0.39) by decreasing the Tb{sup 3+} content from 1.0 to 0.1 mol% of Tb(PO{sub 3}){sub 3} upon Dy{sup 3+} excitation at 423 nm. Such visible region luminescence is generated by {sup 5}D{sub 4}→{sup 7}F{sub 5} and {sup 5}D{sub 4}→{sup 7}F{sub 3} emissions of Tb{sup 3+} in addition to {sup 4}I{sub 15/2}→{sup 6}H{sub 15/2}, {sup 4}F{sub 9/2}→{sup 6}H{sub 15/2}, {sup 4}F{sub 9/2}→{sup 6}H{sub 13/2} and {sup 4}F{sub 9/2}→{sup 6}H{sub 11/2} emissions of Dy{sup 3+}, so that Tb{sup 3+} emission is sensitized by Dy{sup 3+} through a non-radiative resonant energy transfer. A dominant {sup 5}D{sub 4}→{sup 7}F{sub 5} green emission is observed in detriment of the {sup 5}D{sub 3}→{sup 7}F{sub J} blue emissions upon 282 nm excitation, as well as an extended excitation range (280–500 nm), due to multiple Dy{sup 3+} and Tb{sup 3+} transitions, which might contribute to enhance the spectral response of solar photovoltaic cells by down-shifting of the incident solar spectrum. - Highlights: • Zn(PO{sub 3}){sub 2} glasses are optically activated with Tb{sup 3+}/Dy{sup 3+} (ZPTbDy). • Non-radiative resonant energy transfer takes place between Tb{sup 3+} and Dy{sup 3+}. • Luminescence can be adjusted from yellow–green light toward the white light region. • ZPTbDy phosphor exhibits spectroscopic properties for photovoltaic applications.

  9. Tailoring Nd3+ emission spectrum by a neodymium-doped tellurite all-solid photonic bandgap fiber

    Science.gov (United States)

    Tong, Hoang Tuan; Demichi, Daisuke; Suzuki, Takenobu; Ohishi, Yasutake

    2018-02-01

    A tellurite all-solid photonic bandgap fiber (ASPBF) whose cladding consists of 60 high-index rods arranged periodically around a central core was successfully fabricated. The diameter of high-index rod was about 5.0 μm and the distance between the center of two adjacent high-index rods was approximately 8.0 μm. The high-index rod was made of the TeO2-Li2O-WO3-MoO3-Nb2O5 (TLWMN) glass, the cladding was made of the TeO2-ZnO-Na2O-La2O3 (TZNL) glass as the background glass material and the central core was made of TZNL glass doped with 0.5 wt% of Nd2O3. A supercontinuum light from 0.6 to 2.4 μm was coupled into the core of fiber which is 2.2 cm long to measure its transmission spectrum. High transmission bands were obtained in the vicinity of 0.75 and 1.3 μm but the transmission was suppressed in the wavelength range from 1.0 to 1.06 μm. When a titanium∶Sapphire laser source at 0.75 μm was used, the emission spectrum was obtained with two peaks at 1.06 and 1.33 μm which are attributed to the 4F3/2->4I11/2 and 4F3/2->4I13/2 transitions of Nd3+ ion, respectively. The intensities of those emission peaks were compared with those obtained from a bulk glass having the same doping concentration of Nd3+. The results showed that by using tellurite ASPBF, the intensity of the 1.06-μm emission was suppressed by one-twelfth but the intensity of the 1.33-μm emission was maintained. This feature is very advantageous to filter out the 1.06-μm emission of Nd3+ ion in order to realize practical amplifier devices at 1.3 μm.

  10. Investigation of radiation shielding properties for MeO-PbCl2-TeO2 (MeO = Bi2O3, MoO3, Sb2O3, WO3, ZnO) glasses

    Czech Academy of Sciences Publication Activity Database

    Sayyed, M.I.; Celikbilek Ersundu, M.; Ersundu, A.E.; Lakshminarayana, G.; Kostka, Petr

    2018-01-01

    Roč. 144, March 2018 (2018), s. 419-425 ISSN 0969-806X Institutional support: RVO:67985891 Keywords : tellurite glasses * XCOM * radiation shielding * mass attenuation coefficient * exposure buildup factor Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.315, year: 2016

  11. Midinfrared optical rogue waves in soft glass photonic crystal fiber

    DEFF Research Database (Denmark)

    Buccoliero, Daniel; Steffensen, Henrik; Ebendorff-Heidepriem, Heike

    2011-01-01

    We investigate numerically the formation of extreme events or rogue waves in soft glass tellurite fibers and demonstrate that optical loss drastically diminishes shot-to-shot fluctuations characteristic of picosecond pumped supercontinuum (SC). When loss is neglected these fluctuations include...... distributions. Our results thus implicitly show that rogue waves will not occur in any SC spectrum that is limited by loss, such as commercial silica fiber based SC sources. © 2011 Optical Society of America....

  12. Mass spectrometric study of vaporization of cesium tellurate and tellurite

    International Nuclear Information System (INIS)

    Semenov, G.A.; Fokina, L.A.; Mouldagalieva, R.A.

    1994-01-01

    The process of vaporization of cesium tellurate and tellurite was studied by the Knudsen effusion method with a mass spectrometric analysis of the vapor composition. The thermal dissociation of Cs 2 TeO 4 to Cs 2 TeO 3 and the congruent vaporization of Cs 2 TeO 3 were established. Thermodynamic functions for gaseous Cs 2 TeO 3 have been calculated. The standard enthalpy of sublimation Δ s H (298.15)=268.1±13.0 kJ mol -1 was determined by the 2nd and 3rd laws of thermodynamics. The enthalpy of formation Δ f H (298.15)=-725.1±13.0 kJ mol -1 for gaseous Cs 2 TeO 3 and the enthalpy of atomization Δ at H (298.15)=1841.3±15.0 kJ mol -1 have been computed. ((orig.))

  13. Physical and structural properties of Sm3+ ions doped heavy metal oxide containing lanthanum-boro-telluirte glass

    Science.gov (United States)

    Madhu, A.; Eraiah, B.

    2018-05-01

    The structural studies of Tellurium oxide substituted by samarium oxide in lathanum-lead-boro-tellurite glass are successfully prepared with physical and optical parameters are determined. Due to the effect of increased number of non-bridging oxygen's in the glass samples few physical parameters are observed to be decreased. For the better structural analysis FTIR was carried out and transformation of BO3 → BO4 is observed. Most effective absorption coefficient OH- group was attained in the present work.

  14. Enhanced green upconversion by controlled ceramization of Er{sup 3+}–Yb{sup 3+} co-doped sodium niobium tellurite glass–ceramics for low temperature sensors

    Energy Technology Data Exchange (ETDEWEB)

    Suresh Kumar, J., E-mail: suresh@ua.pt; Pavani, K.; Graça, M.P.F.; Soares, M.J.

    2014-12-25

    Highlights: • Upconversion luminescence improved in glass–ceramics compared to host glass. • Judd–Ofelt and radiative parameters calculated. • NIR decay curve results concur the results of improved luminescence. • Temperature dependent upconversion support the use of materials for sensors. - Abstract: Tellurite based glasses are well-known for their upconversion properties besides having a disadvantage of low mechanical strength dragging them away from practical applications. The present work deals with preparation of sodium niobium tellurite (SNT) glasses using melt quenching method, in which small quantities of boron and silicon in the form of oxides are added to improve their mechanical properties. Controlled heat treatment is performed to ceramize the prepared glasses based on the thermal data given by DTA. XRD and SEM profiles of the glass–ceramics which confirmed the formation of crystalline monoclinic Sodium Tellurium Niobium Oxide (Na{sub 1.4}Nb{sub 3}Te{sub 4.9}O{sub 18}) phase (JCPDS card No. 04–011-7556). Upconversion measurements in the visible region were made for the prepared Er{sup 3+}–Yb{sup 3+} co-doped glasses and glass–ceramics with 980 nm laser excitation varying the laser power and concentration of Er{sup 3+} ions. Results showed that the upconversion luminescence intensity was enhanced by ten times in SNT glass–ceramics compared to that in the SNT glasses. Decay curves give evidence of high performance of glass–ceramics compared to glasses due to ceramization and structural changes. Temperature dependent visible upconversion was performed to test the ability of efficient SNT glass–ceramic at low temperatures and variation of upconversion intensities was studied.

  15. Glucose-6-phosphate dehydrogenase protects Escherichia coli from tellurite-mediated oxidative stress.

    Directory of Open Access Journals (Sweden)

    Juan M Sandoval

    Full Text Available The tellurium oxyanion tellurite induces oxidative stress in most microorganisms. In Escherichia coli, tellurite exposure results in high levels of oxidized proteins and membrane lipid peroxides, inactivation of oxidation-sensitive enzymes and reduced glutathione content. In this work, we show that tellurite-exposed E. coli exhibits transcriptional activation of the zwf gene, encoding glucose 6-phosphate dehydrogenase (G6PDH, which in turn results in augmented synthesis of reduced nicotinamide adenine dinucleotide phosphate (NADPH. Increased zwf transcription under tellurite stress results mainly from reactive oxygen species (ROS generation and not from a depletion of cellular glutathione. In addition, the observed increase of G6PDH activity was paralleled by accumulation of glucose-6-phosphate (G6P, suggesting a metabolic flux shift toward the pentose phosphate shunt. Upon zwf overexpression, bacterial cells also show increased levels of antioxidant molecules (NADPH, GSH, better-protected oxidation-sensitive enzymes and decreased amounts of oxidized proteins and membrane lipids. These results suggest that by increasing NADPH content, G6PDH plays an important role in E. coli survival under tellurite stress.

  16. Mixed mobile ion effect in fluorozincate glasses

    International Nuclear Information System (INIS)

    Ghosh, S; Ghosh, A

    2005-01-01

    The mixed mobile ion effect has been investigated for the first time in zinc fluoride glasses where in addition to alkali cations fluorine anions also participate in the diffusion process, unlike mixed alkali oxide glasses. The minimum in the conductivity, conductivity relaxation frequency, crossover frequency and decoupling index indicates the existence of the mixed mobile ion effect in these fluoride glasses. It has been observed that the non-exponential parameter and the frequency exponent are independent of temperature. It has been established that alkali ions and fluorine anions exhibit lower dimensionality of the conduction pathways in mixed alkali zinc fluoride glasses than that in the single alkali lithium based zinc fluoride glasses while they are migrating. From the scaling of the conductivity spectra, it has been established that the relaxation dynamics in mixed alkali zinc fluoride glasses is independent of temperature and composition

  17. Thermal characteristics, Raman spectra, optical and structural properties of TiO2-Bi2O3-B2O3-TeO2 glasses

    Science.gov (United States)

    Gupta, Nupur; Khanna, Atul; Gonzàlez, Fernando; Iordanova, Reni

    2017-05-01

    Tellurite and borotellurite glasses containing Bi2O3 and TiO2 were prepared and structure-property correlations were carried out by density measurements, X-ray Diffraction (XRD), Differential Scanning Calorimetry (DSC), Raman and UV-visible spectroscopy. Titanium tellurite glasses require high melt-cooling rates and were fabricated by splat quenching. On adding B2O3, the glass forming ability (GFA) enhances, and glasses could be synthesized at lower quenching rates. The density of glasses shows a direct correlation with molecular mass of the constituents. UV-visible studies were used to determine the optical band gap and refractive index. Raman studies found that the co-ordination number of tellurium ions with oxygen (NTe-O) decreases with the increase in B2O3 as well as Bi2O3 content while, TiO2 produce only a small decrease in NTe-O, which explains the lower GFA of titanium tellurite glasses that do not contain Bi2O3 and B2O3. DSC studies show that the glass transition temperature (Tg) increases with B2O3 and TiO2 concentrations and that Tg correlates well with bond enthalpy of the metal oxides.

  18. Polarographic behaviour and determination of selenite and tellurite in simple solutions or in a binary mixture

    International Nuclear Information System (INIS)

    Hassan, A.

    1991-01-01

    The polarographic behaviour of simple solutions of selenite and tellurite in 1 M ammonium salts of formate, acetate, tartrate, oxalate, and benzoate solutions in absence and in presence of Triton X-100 as a maximum suppressor and a temperature of 25 O C has been investigated. Schemes for the mechanism of reductions occuring at the DME have been deduced. A method for analytical determination of selenite and tellurite in simple solutions as well as in a binary mixture in the presence of 4-14 . 10 -3 % Triton X-100 is reported. (author)

  19. Atom-Photon Coupling from Nitrogen-vacancy Centres Embedded in Tellurite Microspheres

    Science.gov (United States)

    Ruan, Yinlan; Gibson, Brant C.; Lau, Desmond W. M.; Greentree, Andrew D.; Ji, Hong; Ebendorff-Heidepriem, Heike; Johnson, Brett C.; Ohshima, Takeshi; Monro, Tanya M.

    2015-06-01

    We have developed a technique for creating high quality tellurite microspheres with embedded nanodiamonds (NDs) containing nitrogen-vacancy (NV) centres. This hybrid method allows fluorescence of the NVs in the NDs to be directly, rather than evanescently, coupled to the whispering gallery modes of the tellurite microspheres at room temperature. As a demonstration of its sensing potential, shifting of the resonance peaks is also demonstrated by coating a sphere surface with a liquid layer. This new approach is a robust way of creating cavities for use in quantum and sensing applications.

  20. Extremely radioresistant microbe Deinococcus radiodurans does not survive tellurite-mediated oxidative stress: revelation of molecular basis

    International Nuclear Information System (INIS)

    Apte, Shree Kumar; Narasimha, Anaganti; Basu, Bhakti

    2014-01-01

    Deinococcus radiodurans exhibits extraordinary resistance to gamma radiation as well as oxidative stress. Comparison of tellurite stress with gamma irradiation, both of which impart severe oxidative stress, revealed that tellurite induced less ROS and caused less oxidative damage to proteins, but was much more lethal to D. radiodurans than gamma irradiation. The proteomic changes induced by tellurite exposure were mapped by two dimensional protein electrophoresis followed by mass spectrometry. Seventy proteins belonging to major functional categories of oxidative stress alleviation, protein translation/folding and metabolism were identified. Tellurite responsive proteome dynamics displayed (i) up-regulation of proteins involved in tellurite stress resistance and oxidative stress alleviation, dehydrogenases involved in generation of reducing potential, and chaperones (such DnaK), and (ii) down regulation of key glycolysis and TCA cycle enzymes, proteins involved in protein translation/folding and energy production. Tellurite stress also resulted in nearly 50% loss in the cellular reducing potential within 1h of exposure while gamma irradiation had no such effect. The findings provide a better insight into the mechanism of tellurite toxicity, beyond metal mediated oxidative stress, in this extremophile. (author)

  1. Comparisons of plutonium, thorium, and cerium tellurite sulfates.

    Science.gov (United States)

    Lin, Jian; Cross, Justin N; Diwu, Juan; Meredith, Nathan A; Albrecht-Schmitt, Thomas E

    2013-04-15

    The hydrothermal reaction of PuCl3 or CeCl3 with TeO2 in the presence of sulfuric acid under the comparable conditions results in the crystallization of Pu(TeO3)(SO4) or Ce2(Te2O5)(SO4)2, respectively. Pu(TeO3)(SO4) and its isotypic compound Th(TeO3)(SO4) are characterized by a neutral layer structure with no interlamellar charge-balancing ions. However, Ce2(Te2O5)(SO4)2 possesses a completely different dense three-dimensional framework. Bond valence calculation and UV-vis-NIR spectra indicate that the Ce compound is trivalent whereas the Pu and Th compounds are tetravalent leading to the formation of significantly different compounds. Pu(TeO3)(SO4), Th(TeO3)(SO4), and Ce2(Te2O5)(SO4)2 represent the first plutonium/thorium/cerium tellurite sulfate compounds. Our study strongly suggests that the chemistries of Pu and Ce are not the same, and this is another example of the failure of Ce as a surrogate.

  2. Accelerated bone ingrowth by local delivery of Zinc from bioactive ...

    African Journals Online (AJOL)

    2015-10-19

    Oct 19, 2015 ... Aims: This study aims to evaluate in vivo the performance therapy of zinc-doped bioactive glass (BG-Zn) and ... Keywords: zinc metallic ion; bioactive glass; osteoporosis; trabecular bone architecture; mechanical property; oxidative stress ..... Ducheyne P, Qiu Q. Bioactive ceramics: the effect of surface.

  3. Fabrication of optical channel waveguides in crystals and glasses using macro- and micro ion beams

    Czech Academy of Sciences Publication Activity Database

    Banyasz, I.; Rajta, I.; Nagy, G. U. L.; Zolnai, Z.; Havránek, Vladimír; Veres, M.; Berneschi, S.; Nunzi-Conti, G.; Righini, G. C.

    2014-01-01

    Roč. 331, JUL (2014), s. 157-162 ISSN 0168-583X R&D Projects: GA MŠk(XE) LM2011019 Institutional support: RVO:61389005 Keywords : channel optical waveguides * ion beam irradiation * focussed ion beam * Er-doped tungsten-tellurite glass * Bismuth germanate * Micro Raman spectroscopy Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 1.124, year: 2014

  4. Calculation and analysis of vibrational spectra of PbCl(2)-Sb(2)O(3)-TeO(2) glass from first principles

    Czech Academy of Sciences Publication Activity Database

    Macháček, J.; Kostka, Petr; Liška, M.; Zavadil, Jiří; Gedeon, O.

    2011-01-01

    Roč. 357, č. 14 (2011), s. 2562-2570 ISSN 0022-3093 R&D Projects: GA ČR GA104/08/0734; GA MPO 2A-1TP1/063 Institutional research plan: CEZ:AV0Z40320502; CEZ:AV0Z20670512 Keywords : vibrational spectrum * tellurite glass * ab initio molecular simulation Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.537, year: 2011

  5. Solid state field-assisted diffusion silver diffusion in (TeO2)0.6(WO3)0.25(La2O3)0.05(Na2O)0.1 glass

    Czech Academy of Sciences Publication Activity Database

    Stepanov, B.; Wágner, T.; Lorinčík, Jan; Frumar, M.; Churbanov, M.; Chigirinsky, Y.

    2012-01-01

    Roč. 48, č. 6 (2012), s. 642-647 ISSN 0020-1685 Institutional support: RVO:67985882 Keywords : Tellurite glass * Solid state diffusion * Secondary Ion Mass Spectrometry Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering Impact factor: 0.376, year: 2012

  6. Structure and optical properties of TeO2 center dot PbCl2 center dot PbF2 glasses doped with Pr and Er, prepared in Au or Pt crucibles

    Czech Academy of Sciences Publication Activity Database

    Trnovcová, V.; Kubliha, M.; Labas, V.; Kadleciková, M.; Pedlíková, Jitka; Greguš, J.; Slabeyclus, J.

    2012-01-01

    Roč. 14, 1-2 (2012), s. 77-83 ISSN 1454-4164 Institutional research plan: CEZ:AV0Z40320502 Keywords : Tellurite/lead chloride/lead fluoride glasses * Optical absorption * Photoluminescence Subject RIV: CA - Inorganic Chemistry Impact factor: 0.516, year: 2012

  7. Electrical and dielectric properties of doped TeO2 center dot PbCl2 center dot PbF2 glasses, prepared in Au or Pt crucibles

    Czech Academy of Sciences Publication Activity Database

    Kubliha, M.; Trnovcová, V.; Labas, V.; Psota, J.; Pedlíková, Jitka; Podolinčiaková, J.

    2011-01-01

    Roč. 13, 11-12 (2011), s. 1493-1497 ISSN 1454-4164 Institutional research plan: CEZ:AV0Z40320502 Keywords : tellurite/lead chloride/lead fluoride glasses * electrical conductivity * TSDC * permittivity Subject RIV: CA - Inorganic Chemistry Impact factor: 0.457, year: 2011

  8. Electrical and optical properties of zinc oxide: thin films

    International Nuclear Information System (INIS)

    Zuhairusnizam Md Darus; Abdul Jalil Yeop Majlis; Anis Faridah Md Nor; Burhanuddin Kamaluddin

    1992-01-01

    Zinc oxide films have been prepared by high temperature oxidation of thermally evaporated zinc films on glass substrates. The resulting films are characterized using X-ray diffraction, optical absorption and electrical conductivity measurements. These zinc oxide films are very transparent and photoconductive

  9. Isolation and initial characterization of the tellurite reducing moderately halophilic bacterium, Salinicoccus sp. strain QW6.

    Science.gov (United States)

    Amoozegar, Mohammad Ali; Ashengroph, Morahem; Malekzadeh, Feridon; Reza Razavi, Mohamad; Naddaf, Saied; Kabiri, Mahboubeh

    2008-01-01

    Among the 49 strains of moderately halophilic bacteria isolated from the salty environments of Iran, a Gram-positive coccus designated as strain QW6 showed high capacity in the removal of toxic oxyanions of tellurium in a wide range of culture medium factors including pH (5.5-10.5), temperature (25-45 degrees C), various salts including NaCl, KCl, and Na(2)SO(4) (0.5-4 M), selenooxyanions (2-10 mM), and at different concentrations of potassium tellurite (0.5-1 mM) under aerobic condition. Phenotypic characterization and phylogenetic analyses based on 16S rDNA sequence comparisons indicated that this strain was a member of the genus Salinicoccus. The maximum tellurite removal was exhibited in 1.5M NaCl at 35 degrees C, while the activity reduced by 53% and 47% at 25 and 45 degrees C, respectively. The optimum pH for removal activity was shown to be 7.5, with 90% and 83% reduced removal capacities at the two extreme values of 5.5 and 10, respectively. The impact of different concentrations of selenooxyanions (2-10 mM) on tellurite removal by strain QW6 was evaluated. The ability of strain QW6 in the removal of tellurite in the presence of 6mM selenite increased by 25%. The concentration of toxic potassium tellurite in the supernatant of the bacterial culture medium decreased by 99% (from 0.5 to 0.005 mM) after 6 days and the color of the medium changed to black due to the formation of less toxic elemental tellurium.

  10. Lasing transition at 1.06 μm emission in Nd3+ -doped borate-based tellurium calcium zinc niobium oxide glasses for high-power solid-state lasers.

    Science.gov (United States)

    Ravi, O; Prasad, K; Jain, Rajiv; Venkataswamy, M; Chaurasia, Shivanand; Deva Prasad Raju, B

    2017-08-01

    The spectroscopic properties of Tellurium Calcium Zinc Niobium oxide Borate (TCZNB) glasses of composition (in mol%) 10TeO 2  + 15CaO + 5ZnO + 10 Nb 2 O 5  + (60 - x)B 2 O 3  + Nd 2 O 3 (x = 0.1, 0.5, 1.0 or 1.5 mol%) have been investigated experimentally. The three phenomenological intensity parameters Ω 2 , Ω 4, Ω 6 have been calculated using the Judd-Ofelt theory and in turn radiative properties such as radiative transition probabilities, emission cross-sections, branching ratios and radiative lifetimes have been estimated. The trend found in the JO intensity parameter is Ω 2  > Ω 6  > Ω 4 If Ω 6  > Ω 4 , the glass system is favourable for the laser emission 4 F 3 /2  →  4 I 11 /2 in the infrared (IR) wavelength. The experimental values of branching ratio of 4 F 3 /2  →  4 I 11 /2 transition indicate favourable lasing action with low threshold power. The evaluated total radiative transition probabilities (A T ), stimulated emission cross-section (σ e ) and gain bandwidth parameters (σ e  × Δλ p ) were compared with earlier reports. An energy level analysis has been carried out considering the experimental energy positions of the absorption and emission bands. Copyright © 2016 John Wiley & Sons, Ltd.

  11. Structure and properties of TeO2-WO3 system glasses

    International Nuclear Information System (INIS)

    Kolobkov, V.P.; Ovcharenko, N.V.; Morozova, I.N.; Chebotarev, S.A.; Chikovskij, A.N.; Arkatova, T.G.

    1987-01-01

    Study of TeO 2 -WO 3 system is of interest for production of high-refractive-glasses with comparatively low crystallizability. Results of investigating some properties and structural features of this system glasses are presented. Composition and properties of studied glasses are presented. The properties were studied using the following techniques: the density was measured by hydrostatic weighing in toluene; thermal expansion coefficient was measured in quartz dilatometer DKV-5A; dilatometric temperature of glass softening (T g ) was defined as an intersection point of linear and curved parts of the plot of thermal expansion coefficient; refractive index (RI) - by immersion method; dielectric properties are measured. Consideration of vibronic spectra permits to conclude that in tungsten-tellurium glasses rare earth activator ions are arranged near tellurite and tungstate groupings proportional to glass-forming component content

  12. Effect of co-doping of sodium on the thermoluminescence dosimetry properties of copper-doped zinc lithium borate glass system

    International Nuclear Information System (INIS)

    Saidu, A.; Wagiran, H.; Saeed, M.A.; Alajerami, Y.S.M.; Kadir, A.B.A.

    2016-01-01

    The effect of sodium as a co-dopant on the thermoluminescence (TL) properties of copper-doped zinc lithium borate (ZLB: Cu) subjected to Co-60 gamma radiation is reported in this study. TL intensity is enhanced with the introduction of sodium in ZLB: Cu. The obtained glow curve is simple with a single peak. The annealing procedure and the best heating rate for the proposed thermoluminescent dosimeter (TLD) are established, and the phosphor is reusable. The TL response within the dose range of 0.5–1000 Gy is investigated. The results show that the thermal fading behaviour is improved significantly. - Highlights: • Dosimetry properties of an improved TL dosimeter. • The dosimeter is made of lithium borate, modified with ZnO, doped with CuO and co-doped with Na 2 O. • With addition of Na to Cu in the ZLB host, TL yield and sensitivity has significantly enhanced. • The fading behaviour has also been minimized significantly. • The new material is also characterized with the linear dose response, and good reproducibility behaviour.

  13. Structural and thermal properties of tellurite 20Li2O-80TeO2 glasses

    OpenAIRE

    Idalgo, E. [UNESP; Araújo, E. B. [UNESP

    2007-01-01

    O presente trabalho reporta estudos sobre a cristalização em vidros teluretos 20Li2O-80TeO2 induzida a partir de tratamentos térmicos realizados sobre vidros com tamanho de partículas entre 38 µm e 75 µm. Estes estudos foram conduzidos em duas matrizes vítreas tratadas e não tratadas termicamente para aliviar as tensões após o quenching, utilizando-se de forma combinada às técnicas de difração de raios X, calorimetria diferencial de varredura e espectroscopia no infravermelho. Os resultados r...

  14. Phosphate glasses, containing nitrogen

    International Nuclear Information System (INIS)

    Lisitsyna, E.A.; Khalilev, V.D.; Koryavin, A.A.; Goncharova, L.N.

    1987-01-01

    Possibilities of nitrogen-containing glass synthesis by the introduction into the charge of ammonium salts, as well as aluminium nitride, are studied. Zinc alumoyttrium phosphate glass (mol. %) Zn(PO 3 ) 2 - 4O, Al(PO 3 ) 3 - 3O, Y(PO 3 ) 3 -3O is suggested as a matrix. It is shown that the effect of amide and imide groups on the properties of the glass is less noticeable than the effect of nitride groups. Direct introduction of nitride constituent was realized using AlN, but aluminium introduction was taken into account so that the oxide was subtracted. The attempt to introduce more than 2.5 mass % of nitrogen into initial matrix by aluminium nitride has failed due to repeated restoration of glass with amorphous phosphorus isolation

  15. Soliton self-frequency shift controlled by a weak seed laser in tellurite photonic crystal fibers.

    Science.gov (United States)

    Liu, Lai; Meng, Xiangwei; Yin, Feixiang; Liao, Meisong; Zhao, Dan; Qin, Guanshi; Ohishi, Yasutake; Qin, Weiping

    2013-08-01

    We report the first demonstration of soliton self-frequency shift (SSFS) controlled by a weak continuous-wave (CW) laser, from a tellurite photonic crystal fiber pumped by a 1560 nm femtosecond fiber laser. The control of SSFS is performed by the cross-gain modulation of the 1560 nm femtosecond laser. By varying the input power of the weak CW laser (1560 nm) from 0 to 1.17 mW, the soliton generated in the tellurite photonic crystal fiber blue shifts from 1935 to 1591 nm. The dependence of the soliton wavelength on the operation wavelength of the weak CW laser is also measured. The results show the CW laser with a wavelength tunable range of 1530-1592 nm can be used to control the SSFS generation.

  16. Fabrication of optical channel waveguides in crystals and glasses using macro- and micro ion beams

    Energy Technology Data Exchange (ETDEWEB)

    Bányász, I., E-mail: banyasz@sunserv.kfki.hu [Wigner Research Centre for Physics, Hungarian Academy of Sciences, P.O. Box 49, H-1525 Budapest (Hungary); Rajta, I.; Nagy, G.U.L. [MTA Atomki, Institute for Nuclear Research, Hungarian Academy of Sciences, P.O. Box 51, H-4001 Debrecen (Hungary); Zolnai, Z. [Research Institute for Technical Physics and Materials Science, Research Centre for Natural Sciences, Hungarian Academy of Sciences, P.O. Box 49, H-1525 Budapest (Hungary); Havranek, V. [Nuclear Physics Institute AV CR, Řež near Prague 250 68 (Czech Republic); Pelli, S. [MDF-Lab, “Nello Carrara” Institute of Applied Physics, IFAC-CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino, FI (Italy); “Enrico Fermi” Center for Study and Research, Piazza del Viminale 2, 00184 Roma (Italy); Veres, M. [Wigner Research Centre for Physics, Hungarian Academy of Sciences, P.O. Box 49, H-1525 Budapest (Hungary); Berneschi, S.; Nunzi-Conti, G. [MDF-Lab, “Nello Carrara” Institute of Applied Physics, IFAC-CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino, FI (Italy); Righini, G.C. [“Enrico Fermi” Center for Study and Research, Piazza del Viminale 2, 00184 Roma (Italy)

    2014-07-15

    Active and passive optical waveguides are fundamental elements in modern telecommunications systems. A great number of optical crystals and glasses were identified and are used as good optoelectronic materials. However, fabrication of waveguides in some of those materials remains still a challenging task due to their susceptibility to mechanical or chemical damages during processing. Researches were initiated on ion beam fabrication of optical waveguides in tellurite glasses. Channel waveguides were written in Er:TeO{sub 2}–WO{sub 3} glass through a special silicon mask using 1.5 MeV N{sup +} irradiation. This method was improved by increasing N{sup +} energy to 3.5 MeV to achieve confinement at the 1550 nm wavelength, too. An alternative method, direct writing of the channel waveguides in the tellurite glass using focussed beams of 6–11 MeV C{sup 3+} and C{sup 5+} and 5 MeV N{sup 3+}, has also been developed. Channel waveguides were fabricated in undoped eulytine-(Bi{sub 4}Ge{sub 3}O{sub 12}) and sillenite type (Bi{sub 12}GeO{sub 20}) bismuth germanate crystals using both a special silicon mask and a thick SU8 photoresist mask and 3.5 MeV N{sup +} irradiation. The waveguides were studied by phase contrast and interference microscopy and micro Raman spectroscopy. Guiding properties were checked by the end fire method.

  17. In vitro activity of zinc oxide-eugenol and glass ionomer cements on Candida albicans Atividade in vitro dos cimentos de óxido de zinco e eugenol e ionômero de vidro sobre Candida albicans

    Directory of Open Access Journals (Sweden)

    Anna Carolina Aguiar Cassanho

    2005-06-01

    Full Text Available The aim of this study was to evaluate in vitro the antimicrobial activity of glass ionomer (GIC and zinc oxide-eugenol (ZOE cements against Candida albicans. Standardized GIC and ZOE specimens were maintained in contact with C. albicans suspension (1 ´ 10(6 cells/ml at 37°C for 24 h, 48 h or 7 days. A control group without any testing cement was included. After the incubation period, aliquots of 0.1 ml were plated on Sabouraud's agar, and then the number of colonies was counted. The results were expressed as values of logarithms of colony-forming units per milliliter (log CFU/mL and were analyzed statistically by Kruskal-Wallis ANOVA. After 48 h of incubation, the ZOE group presented no growth of C. albicans. GIC and control groups presented similar mean values at all tested periods. According to the results obtained, it could be concluded that, under the experimental conditions, ZOE cement was more effective in vitro against C. albicans than GIC.O objetivo deste estudo foi avaliar in vitro a atividade antimicrobiana dos cimentos de ionômero de vidro (CIV e óxido de zinco e eugenol (OZE sobre Candida albicans. Corpos-de-prova padronizados de CIV e OZE foram mantidos em contato com suspensão (1 ´ 10(6 células/ml de C. albicans a 37°C por 24 horas, 48 horas ou 7 dias. Um grupo controle sem nenhum cimento teste foi incluído. Após o período de incubação, alíquotas de 0,1 ml foram semeadas em ágar Sabouraud e o número de colônias foi contado. Os resultados foram expressos em logaritmos de valores de unidades formadoras de colônias por ml (log UFC/mL e analisados estatisticamente pelo teste ANOVA Kruskal-Wallis. Após 48 horas de incubação, o grupo OZE não apresentou crescimento de C. albicans. Os grupos CIV e controle apresentaram médias similares em todos os períodos testados. De acordo com os resultados obtidos, pode ser concluído que, sob as condições experimentais testadas, o cimento OZE apresentou-se mais efetivo in

  18. Selenite and tellurite form mixed seleno- and tellurotrisulfides with CstR from Staphylococcus aureus.

    Science.gov (United States)

    Luebke, Justin L; Arnold, Randy J; Giedroc, David P

    2013-04-01

    Staphylococcus aureus CstR (CsoR-like sulfur transferase repressor) is a member of the CsoR family of transition metal sensing metalloregulatory proteins. Unlike CsoR, CstR does not form a stable complex with transition metals but instead reacts with sulfite to form a mixture of di- and trisulfide species, CstR2(RS-SR') and CstR2(RS-S-SR')n)n=1 or 2, respectively. Here, we investigate if CstR performs similar chemistry with related chalcogen oxyanions selenite and tellurite. In this work we show by high resolution tandem mass spectrometry that CstR is readily modified by selenite (SeO3(2-)) or tellurite (TeO3(2-)) to form a mixture of intersubunit disulfides and selenotrisulfides or tellurotrisulfides, respectively, between Cys31 and Cys60'. Analogous studies with S. aureus CsoR reveals no reaction with selenite and minimal reaction with tellurite. All cross-linked forms of CstR exhibit reduced DNA binding affinity. We show that Cys31 initiates the reaction with sulfite through the formation of S-sulfocysteine (RS-SO3(2-)) and Cys60 is required to fully derivatize CstR to CstR2(RS-SR') and CstR2(RS-S-SR'). The modification of Cys31 also drives an allosteric switch that negatively regulates DNA binding while derivatization of Cys60 alone has no effect on DNA binding. These results highlight the differences between CstRs and CsoRs in chemical reactivity and metal ion selectivity and establish Cys31 as the functionally important cysteine residue in CstRs.

  19. Selenite and tellurite form mixed seleno- and tellurotrisulfides with CstR from Staphylococcus aureus

    OpenAIRE

    Luebke, Justin L.; Arnold, Randy J.; Giedroc, David P.

    2013-01-01

    Staphylococcus aureus CstR (CsoR-like sulfur transferase repressor) is a member of the CsoR family of transition metal sensing metalloregulatory proteins. Unlike CsoR, CstR does not form a stable complex with transition metals but instead reacts with sulfite to form a mixture of di- and trisulfide species, CstR2(RS-SR′) and CstR2(RS-S-SR′)n, n = 1 or 2, respectively. Here, we investigate if CstR performs similar chemistry with related chalcogen oxyanions selenite and tellurite. In this work w...

  20. All-optical control of group velocity dispersion in tellurite photonic crystal fibers.

    Science.gov (United States)

    Liu, Lai; Tian, Qijun; Liao, Meisong; Zhao, Dan; Qin, Guanshi; Ohishi, Yasutake; Qin, Weiping

    2012-12-15

    We demonstrate all-optical control of group velocity dispersion (GVD) via optical Kerr effect in highly nonlinear tellurite photonic crystal fibers. The redshift of the zero-dispersion wavelength is over 307 nm, measured by soliton self-frequency shift cancellation, when the pump peak power of a 1.56 μm femtosecond fiber laser is increased to 11.6 kW. The all-optical control of GVD not only offers a new platform for constructing all-optical-control photonic devices but also promises a new class of experiments in nonlinear fiber optics and light-matter interactions.

  1. Symptomatic zinc deficiency in experimental zinc deprivation.

    OpenAIRE

    Taylor, C M; Goode, H F; Aggett, P J; Bremner, I; Walker, B E; Kelleher, J

    1992-01-01

    An evaluation of indices of poor zinc status was undertaken in five male subjects in whom dietary zinc intake was reduced from 85 mumol d-1 in an initial phase of the study to 14 mumol d-1. One of the subjects developed features consistent with zinc deficiency after receiving the low zinc diet for 12 days. These features included retroauricular acneform macullo-papular lesions on the face, neck, and shoulders and reductions in plasma zinc, red blood cell zinc, neutrophil zinc and plasma alkal...

  2. Glass sealing

    Energy Technology Data Exchange (ETDEWEB)

    Brow, R.K.; Kovacic, L.; Chambers, R.S. [Sandia National Labs., Albuquerque, NM (United States)

    1996-04-01

    Hernetic glass sealing technologies developed for weapons component applications can be utilized for the design and manufacture of fuel cells. Design and processing of of a seal are optimized through an integrated approach based on glass composition research, finite element analysis, and sealing process definition. Glass sealing procedures are selected to accommodate the limits imposed by glass composition and predicted calculations.

  3. Electrochromic Glasses.

    Science.gov (United States)

    1980-07-31

    this glass and that dipole-dipole correlations contribute to the "ferroelectric-like" character of this amorphous system. The TeO2 -W03 glasses can only...shows the dielectric constant and Fig. I(b) glass from pure TeO2 ot pure WO. In addition, glass the tan 8 of the WO glass as a function of temperature... glasses containing WO, in various glass forming nitworks of LifO-B1O0, Na:O-BzO,, and TeO2 were prepared from reagent grade oxides at 800 C - 9SO C in

  4. Flavoprotein-mediated tellurite reduction: structural basis and applications to the synthesis of tellurium-containing nanostructures

    Directory of Open Access Journals (Sweden)

    Mauricio Arenas-Salinas

    2016-07-01

    Full Text Available The tellurium oxyanion tellurite (TeO32- is extremely harmful for most organisms. It has been suggested that a potential bacterial tellurite resistance mechanism would consist of an enzymatic, NAD(PH-dependent, reduction to the less toxic form elemental tellurium (Te0. To date, a number of enzymes such as catalase, type II NADH dehydrogenase and terminal oxidases from the electron transport chain, nitrate reductases, and dihydrolipoamide dehydrogenase (E3, among others, have been shown to display tellurite-reducing activity. This activity is generically referred to as tellurite reductase (TR. Bioinformatic data resting on some of the abovementioned enzymes enabled the identification of common structures involved in tellurite reduction including vicinal catalytic cysteine residues and the FAD/NAD(P+-binding domain, which is characteristic of some flavoproteins. Along this line, thioredoxin reductase (TrxB, alkyl hydroperoxide reductase (AhpF, glutathione reductase (GorA, mercuric reductase (MerA, NADH: flavorubredoxin reductase (NorW, dihydrolipoamide dehydrogenase, and the putative oxidoreductase YkgC from Escherichia coli or environmental bacteria were purified and assessed for TR activity. All of them displayed in vitro TR activity at the expense of NADH or NADPH oxidation. In general, optimal reducing conditions occurred around pH 9-10 and 37 °C.Enzymes exhibiting strong TR activity produced Te-containing nanostructures (TeNS. While GorA and AhpF generated TeNS of 75 nm average diameter, E3 and YkgC produced larger structures (> 100 nm. Electron-dense structures were observed in cells over-expressing genes encoding TrxB, GorA and YkgC.

  5. Determination of Abundance of Tellurite-Resistant Bacteria and the Ability of Remove of them from Qom Province Industrial Wastewater, Qom, Iran

    Directory of Open Access Journals (Sweden)

    Mahboubeh Soleimani Sasani

    2013-02-01

    Full Text Available Background and Objectives: Accumulation of toxic oxyanion of potassium tellurite, which has increased in the environment due to industrial activities, can cause complications in human, such as skin irritation, dermatitis, anorexia, tremor, nausea, vomiting, nervous system stimulation, convulsion, and respiratory arrest. The purpose of this research was to isolate tellurite-resistant bacteria, determine the minimum inhibitory concentration (MIC, and evaluate bioreduction of tellurite in strains.Methods: MIC was measured by agar dilution method in 84 resistant strains isolated from wastewater. QWTm6 strain with tolerance of tellurite concentration of 6684μg/ml was selected as superior strain. Toleration of this level of tellurite has not been reported yet. Results: According to biochemical, phenotypic, and physiological characteristics, QWTm6 was initially classified into Staphylococcus genus. Using the spectrophotometric technique and DDTC reagent (A340nm & sodium diethyldithiocarbamate trihydrate, maximum elimination was seen in 0.4mM concentration of potassium tellurite in 24 hours. The strain showed high ability in the elimination of toxic oxyanion of potassium tellurite under a wide range of factors such as pH=(5-11, temperature (15-50◦C, blender speed (50, 100, 150, and 200rpm, various oxyanion concentrations (0.04-1mM, and different percentages of NaCl (0-20%. This strain was also resistant to penicillin, cefixime, tetracycline, chloramphenicol, streptomycin, neomycin, erythromycin, gentamicin, kanamycin, norfloxacin, and ciprofloxacin.Conclusion: The results of this study showed that QWTm6 could be introduced in the international societies as an acceptable candidate for bioremediation, because of its high ability in removal and reduction of potassium tellurite.

  6. Production and characterization of femtosecond laser-written double line waveguides in heavy metal oxide glasses

    Science.gov (United States)

    da Silva, Diego Silvério; Wetter, Niklaus Ursus; de Rossi, Wagner; Kassab, Luciana Reyes Pires; Samad, Ricardo Elgul

    2018-01-01

    We report the fabrication and characterization of double line waveguides directly written in tellurite and germanate glasses using a femtosecond laser delivering 30 μJ, 80 fs pulses at 4 kHz repetition rate. The double line waveguides produced presented internal losses inferior to 2.0 dB/cm. The output mode profile and the M2 measurements indicate multimodal guiding behavior. A better beam quality for the GeO2 - PbO waveguide was observed when compared with TeO2 - ZnO glass. Raman spectroscopy of the waveguides showed structural modification of the glassy network and indicates that a negative refractive index modification occurs at the focus of the laser beam, therefore allowing for light guiding in between two closely spaced laser written lines. The refractive index change at 632 nm is around 10-4, and the structural changes in the laser focal region of the writing, evaluated by Raman spectroscopy, corroborated our findings that these materials are potential candidates for optical waveguides and passive components. To the best of our knowledge, the two double line configuration demonstrated in the present work was not reported before for germanate or tellurite glasses.

  7. Synthesis, structural, thermal and optical properties of TeO2-Bi2O3-GeO2-Li2O glasses

    Science.gov (United States)

    Dimowa, Louiza; Piroeva, Iskra; Atanasova-Vladimirova, S.; Petrova, Nadia; Ganev, Valentin; Titorenkova, Rositsa; Yankov, Georgi; Petrov, Todor; Shivachev, Boris L.

    2016-10-01

    In this study, synthesis and characterization of novel quaternary tellurite glass system TeO2-Bi2O3-GeO2-Li2O is presented. The compositions include TeO2 and GeO2 as glass formers while different proportion of Bi2O3 and Li2O act as network modifiers. Differential thermal analysis, X-ray diffraction, scanning electron microscopy energy dispersive X-ray spectroscopy, laser ablation inductively coupled plasma mass spectrometry, UV-Vis and Raman spectroscopy are applied to study the structural, thermal and optical properties of the studied glasses. Obtained glasses possess a relatively low glass transition temperature (around 300 °C) if compared to other tellurite glasses, show good thermal transparency in the visible and near infra-red (from 2.4 to 0.4 μm) and can double the frequency of laser light from its original wavelength of 1064 nm to its second-harmonic at 532 nm (i.e. second harmonic generation).

  8. Resolved discrepancies between visible spontaneous Raman cross-section and direct near-infrared Raman gain measurements in TeO2-based glasses.

    Science.gov (United States)

    Rivero, Clara; Stegeman, Robert; Couzi, Michel; Talaga, David; Cardinal, Thierry; Richardson, Kathleen; Stegeman, George

    2005-06-13

    Disagreements on the Raman gain response of different tellurite-based glasses, measured at different wavelengths, have been recently reported in the literature. In order to resolve this controversy, a multi-wavelength Raman cross-section experiment was conducted on two different TeO2-based glass samples. The estimated Raman gain response of the material shows good agreement with the directly-measured Raman gain data at 1064 nm, after correction for the dispersion and wavelength-dependence of the Raman gain process.

  9. Structure of TeO2 - LiNbO3 glasses

    Science.gov (United States)

    Shinde, A. B.; Krishna, P. S. R.; Rao, Rekha

    2017-05-01

    Tellurite based lithium niobate glasses with composition (100-x)TeO2-xLiNbO3 (x=0.1,0.2 & 0.3) were prepared by conventional melt quenching method. The microscopic structural investigation of these glasses is carried out by means of neutron diffraction and Raman scattering measurements. It is found that the basic structural units in these glasses are TeO4 trigonal bipyramids(TBP), TeO3 trigonal pyramids(TP) and NbO6 Octahedra depending on the composition. It is evident from Raman studies that TBPs decreases, TPs increases and NbO6 Octahedra increases with increasing x. From Neutron diffraction studies it is found that network is comprised of TBPs and TPs along with TeO3+1 structural units. Distorted NbO6 octahedral units are present and also increase with the increase in x.

  10. Glass consistency and glass performance

    International Nuclear Information System (INIS)

    Plodinec, M.J.; Ramsey, W.G.

    1994-01-01

    Glass produced by the Defense Waste Processing Facility (DWPF) will have to consistently be more durable than a benchmark glass (evaluated using a short-term leach test), with high confidence. The DWPF has developed a Glass Product Control Program to comply with this specification. However, it is not clear what relevance product consistency has on long-term glass performance. In this report, the authors show that DWPF glass, produced in compliance with this specification, can be expected to effectively limit the release of soluble radionuclides to natural environments. However, the release of insoluble radionuclides to the environment will be limited by their solubility, and not glass durability

  11. Zinc Signals and Immunity.

    Science.gov (United States)

    Maywald, Martina; Wessels, Inga; Rink, Lothar

    2017-10-24

    Zinc homeostasis is crucial for an adequate function of the immune system. Zinc deficiency as well as zinc excess result in severe disturbances in immune cell numbers and activities, which can result in increased susceptibility to infections and development of especially inflammatory diseases. This review focuses on the role of zinc in regulating intracellular signaling pathways in innate as well as adaptive immune cells. Main underlying molecular mechanisms and targets affected by altered zinc homeostasis, including kinases, caspases, phosphatases, and phosphodiesterases, will be highlighted in this article. In addition, the interplay of zinc homeostasis and the redox metabolism in affecting intracellular signaling will be emphasized. Key signaling pathways will be described in detail for the different cell types of the immune system. In this, effects of fast zinc flux, taking place within a few seconds to minutes will be distinguish from slower types of zinc signals, also designated as "zinc waves", and late homeostatic zinc signals regarding prolonged changes in intracellular zinc.

  12. Colloidal glasses

    Indian Academy of Sciences (India)

    First page Back Continue Last page Overview Graphics. Colloidal glasses. Glassy state is attained when system fails to reach equilibrium due to crowding of constituent particles. In molecular glasses, glassy state is reached by rapidly lowering the temperature. In colloidal glasses, glassy state is reached by increasing the ...

  13. Silicate glasses

    International Nuclear Information System (INIS)

    Lutze, W.

    1988-01-01

    Vitrification of liquid high-level radioactive wastes has received the greatest attention, world-wide, compared to any other HLW solidification process. The waste form is a borosilicate-based glass. The production of phosphate-based glass has been abandoned in the western world. Only in the Soviet Union are phosphate-based glasses still being developed. Vitrification techniques, equipment and processes and their remote operation have been developed and studied for almost thirty years and have reached a high degree of technical maturity. Industrial demonstration of the vitrification process has been in progress since 1978. This chapter is a survey of world-wide research and development efforts in nuclear waste glasses and its production technology. The principal glasses considered are silicate glasses which contain boron, i.e., borosilicate glasses

  14. Correlation between the structural relaxation and the functionality of optically functional glasses; Kokinosei glass ni okeru kozo kanwa to kinosei no sokan

    Energy Technology Data Exchange (ETDEWEB)

    Nishida, T [Kyushu University, Fukuoka (Japan). Faculty of Engineering

    1994-12-15

    A discussion was given to elucidate the correlation between the crystallization of infrared ray permeating glass and the infrared ray permeability. The elucidation used infrared ray permeation spectrum, infrared ray absorption spectrum, and the Mosbauer effect. Reduction in permeability due to heat treatment of aluminate glass was discussed from the crystallization mechanism. Ultrafine crystals of mayenite phase having a composition ratio of CaO/Al2O3 = 1.7 diffuse and grow from the glass surface into interior as a result of heat treatment. The crystal growth is triggered by severance of Al-O tetrahedron. Gallate glass has CaGa2O4 and small amount of CaFe2O4 phase deposited when it is heat-treated in the vicinity of Tg. Although the infrared ray permeability decreases in association with the crystallization, the decrease is limited to crystallization on the glass surface, hence the permeability will not fall to zero. Laser irradiation on the gallate glass causes crystallization, resulting in reduced infrared ray permeability. Semi-stable Ca3Ga4O7 phase remains, however, because the heat energy amount is not large. Tellurite glass has {alpha}-TeO2 and a small amount of telluric acid iron deposit when heat-treated. 29 refs., 10 figs.

  15. Production of zinc pellets

    Science.gov (United States)

    Cooper, J.F.

    1996-11-26

    Uniform zinc pellets are formed for use in batteries having a stationary or moving slurry zinc particle electrode. The process involves the cathodic deposition of zinc in a finely divided morphology from battery reaction product onto a non-adhering electrode substrate. The mossy zinc is removed from the electrode substrate by the action of gravity, entrainment in a flowing electrolyte, or by mechanical action. The finely divided zinc particles are collected and pressed into pellets by a mechanical device such as an extruder, a roller and chopper, or a punch and die. The pure zinc pellets are returned to the zinc battery in a pumped slurry and have uniform size, density and reactivity. Applications include zinc-air fuel batteries, zinc-ferricyanide storage batteries, and zinc-nickel-oxide secondary batteries. 6 figs.

  16. Comparative analyses reveal different consequences of two oxidative stress inducers, gamma irradiation and potassium tellurite, in the extremophile Deinococcus radiodurans

    International Nuclear Information System (INIS)

    Narasimha, Anaganti; Basu, Bhakti; Apte, Shree Kumar

    2014-01-01

    Proteomic and mass spectrometric analyses revealed differential responses of D. radiodurans to two oxidative stressors. While both elicited oxidative stress alleviation response, major divergence was observed at the level of DNA repair, metabolic pathways and protein homeostasis. Response to gamma irradiation was focused on DNA repair and ROS scavenging but supported metabolism as well as protein homeostasis. Tellurite, induced oxidative stress alleviation but decreased reducing affected and adversely affected metabolism and protein homeostasis

  17. Genomic Variability of O Islands Encoding Tellurite Resistance in Enterohemorrhagic Escherichia coli O157:H7 Isolates

    OpenAIRE

    Taylor, Diane E.; Rooker, Michelle; Keelan, Monika; Ng, Lai-King; Martin, Irene; Perna, Nicole T.; Burland, N. T. Valerie; Blattner, Fredrick R.

    2002-01-01

    Strains of Escherichia coli causing enterohemorrhagic colitis belonging to the O157:H7 lineage are reported to be highly related. Fifteen strains of E. coli O157:H7 and 1 strain of E. coli O46:H− (nonflagellated) were examined for the presence of potassium tellurite resistance (Ter). Ter genes comprising terABCDEF were shown previously to be part of a pathogenicity island also containing integrase, phage, and urease genes. PCR analysis, both conventional and light cycler based, demonstrated t...

  18. Magnetic properties of glasses from geothite industrial wastes recycling (FeOOH)

    International Nuclear Information System (INIS)

    Romero, M.; Rincon, J.M.; Esparza, M.; Gonzalez-Oliver, C.

    1997-01-01

    It has been carried out the magnetic properties determination for high iron oxide content glasses series obtained from a geothite red mud waste from the zinc hydrometallurgy and dolomite and glass cullet as main raw materials. It has been determined the magnetic susceptibility and magnetization values for the glasses here investigated. The results suggest that the magnetic behaviour are depending on the glass chemical composition, so that glasses can be differently classified like ferrimagnetic, ferromagnetic, superparamagnetic and paramagnetic. (Author) 6 refs

  19. Solitonic supercontinuum of femtosecond mid-IR pulses in W-type index tellurite fibers with two zero dispersion wavelengths

    Directory of Open Access Journals (Sweden)

    S. Kedenburg

    2016-11-01

    Full Text Available We present a detailed experimental parameter study on mid-IR supercontinuum generation in W-type index tellurite fibers, which reveals how the core diameter, pump wavelength, fiber length, and pump power dramatically influence the spectral broadening. As pump source, we use femtosecond mid-IR pulses from a post-amplified optical parametric oscillator tunable between 1.7 μm and 4.1 μm at 43 MHz repetition rate. We are able to generate red-shifted dispersive waves up to a wavelength of 5.1 μm by pumping a tellurite fiber in the anomalous dispersion regime between its two zero dispersion wavelengths. Distinctive soliton dynamics can be identified as the main broadening mechanism resulting in a maximum spectral width of over 2000 nm with output powers of up to 160 mW. We experimentally demonstrated that efficient spectral broadening with considerably improved power proportion in the important first atmospheric transmission window between 3 and 5 μm can be achieved in robust W-type tellurite fibers pumped at long wavelengths by ultra-fast lasers.

  20. Aeration Controls the Reduction and Methylation of Tellurium by the Aerobic, Tellurite-Resistant Marine Yeast Rhodotorula mucilaginosa▿

    Science.gov (United States)

    Ollivier, Patrick R. L.; Bahrou, Andrew S.; Church, Thomas M.; Hanson, Thomas E.

    2011-01-01

    We previously described a marine, tellurite-resistant strain of the yeast Rhodotorula mucilaginosa that both precipitates intracellular Te(0) and volatilizes methylated Te compounds when grown in the presence of the oxyanion tellurite. The uses of microbes as a “green” route for the production of Te(0)-containing nanostructures and for the remediation of Te-oxyanion wastes have great potential, and so a more thorough understanding of this process is required. Here, Te precipitation and volatilization catalyzed by R. mucilaginosa were examined in continuously aerated and sealed (low oxygen concentration) batch cultures. Continuous aeration was found to strongly promote Te volatilization while inhibiting Te(0) precipitation. This differs from the results in sealed batch cultures, for which tellurite reduction to Te(0) was found to be very efficient. We show also that volatile Te species may be degraded rapidly in medium and converted to the particulate form by biological activity. Further experiments revealed that Te(0) precipitates produced by R. mucilaginosa can be further transformed to volatile and dissolved Te species. However, it was not clearly determined whether Te(0) is a required intermediate for Te volatilization. Based on these results, we conclude that low oxygen concentrations will be the most efficient for production of Te(0) nanoparticles while limiting the production of toxic volatile Te species, although the production of these compounds may never be completely eliminated. PMID:21602387

  1. Dietary phytate, zinc and hidden zinc deficiency.

    Science.gov (United States)

    Sandstead, Harold H; Freeland-Graves, Jeanne H

    2014-10-01

    Epidemiological data suggest at least one in five humans are at risk of zinc deficiency. This is in large part because the phytate in cereals and legumes has not been removed during food preparation. Phytate, a potent indigestible ligand for zinc prevents it's absorption. Without knowledge of the frequency of consumption of foods rich in phytate, and foods rich in bioavailable zinc, the recognition of zinc deficiency early in the illness may be difficult. Plasma zinc is insensitive to early zinc deficiency. Serum ferritin concentration≤20μg/L is a potential indirect biomarker. Early effects of zinc deficiency are chemical, functional and may be "hidden". The clinical problem is illustrated by 2 studies that involved US Mexican-American children, and US premenopausal women. The children were consuming home diets that included traditional foods high in phytate. The premenopausal women were not eating red meat on a regular basis, and their consumption of phytate was mainly from bran breakfast cereals. In both studies the presence of zinc deficiency was proven by functional responses to controlled zinc treatment. In the children lean-mass, reasoning, and immunity were significantly affected. In the women memory, reasoning, and eye-hand coordination were significantly affected. A screening self-administered food frequency questionnaire for office might help caregiver's identify patients at risk of zinc deficiency. Copyright © 2014 Elsevier GmbH. All rights reserved.

  2. Recycle Glass in Foam Glass Production

    DEFF Research Database (Denmark)

    Petersen, Rasmus Rosenlund; König, Jakob; Yue, Yuanzheng

    The foam glass industry turn recycle glass into heat insulating building materials. The foaming process is relative insensitive to impurities in the recycle glass. It is therefore considered to play an important role in future glass recycling. We show and discuss trends of use of recycled glasses...... in foam glass industry and the supply sources and capacity of recycle glass....

  3. Relative leach behavior of waste glasses and naturally occurring glasses

    International Nuclear Information System (INIS)

    Adams, P.B.

    1979-01-01

    Simulated nuclear waste glasses of the sodium-borosilicate type with a low waste loading and of the zinc-borosilicate type with a high waste loading have been compared with obsidians. The resuls indicate that the waste glasses would corrode in normal natural environments at a rate of about 0.1 μm per year at 30 0 C and about 5 μm per year at 90 0 C, compared with obsidians which seem to corrode at, or less than, about 0.01 μm per year at 30 0 C and less than 1 μm per year at 90 0 C. Activation energies for reactions of the two waste glasses with pure water are about 20 kcal/g-mol. 3 figures, 7 tables

  4. BWR zinc addition Sourcebook

    International Nuclear Information System (INIS)

    Garcia, Susan E.; Giannelli, Joseph F.; Jarvis, Alfred J.

    2014-01-01

    Boiling Water Reactors (BWRs) have been injecting zinc into the primary coolant via the reactor feedwater system for over 25 years for the purpose of controlling primary system radiation fields. The BWR zinc injection process has evolved since the initial application at the Hope Creek Nuclear Station in 1986. Key transitions were from the original natural zinc oxide (NZO) to depleted zinc oxide (DZO), and from active zinc injection of a powdered zinc oxide slurry (pumped systems) to passive injection systems (zinc pellet beds). Zinc addition has continued through various chemistry regimes changes, from normal water chemistry (NWC) to hydrogen water chemistry (HWC) and HWC with noble metals (NobleChem™) for mitigation of intergranular stress corrosion cracking (IGSCC) of reactor internals and primary system piping. While past reports published by the Electric Power Research Institute (EPRI) document specific industry experience related to these topics, the Zinc Sourcebook was prepared to consolidate all of the experience gained over the past 25 years. The Zinc Sourcebook will benefit experienced BWR Chemistry, Operations, Radiation Protection and Engineering personnel as well as new people entering the nuclear power industry. While all North American BWRs implement feedwater zinc injection, a number of other BWRs do not inject zinc. This Sourcebook will also be a valuable resource to plants considering the benefits of zinc addition process implementation, and to gain insights on industry experience related to zinc process control and best practices. This paper presents some of the highlights from the Sourcebook. (author)

  5. Method of capturing or trapping zinc using zinc getter materials

    Science.gov (United States)

    Hunyadi Murph, Simona E.; Korinko, Paul S.

    2017-07-11

    A method of trapping or capturing zinc is disclosed. In particular, the method comprises a step of contacting a zinc vapor with a zinc getter material. The zinc getter material comprises nanoparticles and a metal substrate.

  6. Glasses obtained from industrial wastes

    International Nuclear Information System (INIS)

    Bortoluzzi, D.; Oliveira Fillho, J.; Uggioni, E.; Bernardin, A.M.

    2009-01-01

    This paper deals with the study of the vitrification mechanism as an inertization method for industrial wastes contaminated with heavy metals. Ashes from coal (thermoelectric), wastes from mining (fluorite and feldspar) and plating residue were used to compose vitreous systems planed by mixture design. The chemical composition of the wastes was determined by XRF and the formulations were melted at 1450 deg C for 2h using 10%wt of CaCO 3 (fluxing agent). The glasses were poured into a mold and annealed (600 deg C). The characteristic temperatures were determined by thermal analysis (DTA, air, 20 deg C/min) and the mechanical behavior by Vickers microhardness. As a result, the melting temperature is strongly dependent on silica content of each glass, and the fluorite residue, being composed mainly by silica, strongly affects Tm. The microhardness of all glasses is mainly affected by the plating residue due to the high iron and zinc content of this waste. (author)

  7. BNFL Report Glass Formers Characterization

    Energy Technology Data Exchange (ETDEWEB)

    Schumacher, R.F.

    2000-07-27

    The objective of this task was to obtain powder property data on candidate glass former materials, sufficient to guide conceptual design and estimate the cost of glass former handling facilities as requested under Part B1 of BNFL Technical and Development Support. Twenty-nine glass forming materials were selected and obtained from vendors for the characterization of their physical properties, durability in caustic solution, and powder flow characteristics. A glass former was selected based on the characterization for each of the ten oxide classes required for Envelope A, B, and C mixtures. Three blends (A, B, and C) were prepared based on formulations provided by Vitreous State Laboratory and evaluated with the same methods employed for the glass formers. The properties obtained are presented in a series of attached Tables. It was determined that five of the ten glass formers, (kyanite, iron oxide, titania, zircon, and zinc oxide) have the potential to cause some level of solids f low problems. The problems might include arching or ratholing in the silo/hopper. In addition, all of the blends may require consideration for their handling.

  8. BNFL Report Glass Formers Characterization

    Energy Technology Data Exchange (ETDEWEB)

    Schumacher, R.F.

    2000-07-27

    The objective of this task was to obtain powder property data on candidate glass former materials, sufficient to guide conceptual design and estimate the cost of glass former handling facilities as requested under Part B1 of BNFL Technical and Development Support. Twenty-nine glass forming materials were selected and obtained from vendors for the characterization of their physical properties, durability in caustic solution, and powder flow characteristics. A glass former was selected based on the characterization for each of the ten oxide classes required for Envelope A, B, and C mixtures. Three blends (A, B, and C) were prepared based on formulations provided by Vitreous State Laboratory and evaluated with the same methods employed for the glass formers. The properties obtained are presented in a series of attached Tables. It was determined that five of the ten glass formers, (kyanite, iron oxide, titania, zircon, and zinc oxide) have the potential to cause some level of solids f low problems. In addition, all of the blends may require consideration for their handling. A number of engineering considerations and recommendations were prepared based on the experimental findings, experience, and other process considerations. Recommendations for future testing are included. In conjunction with future work, it is recommended that a professional consultant be engaged to guide and assist with testing and design input.

  9. BNFL Report Glass Formers Characterization

    International Nuclear Information System (INIS)

    Schumacher, R.F.

    2000-01-01

    The objective of this task was to obtain powder property data on candidate glass former materials, sufficient to guide conceptual design and estimate the cost of glass former handling facilities as requested under Part B1 of BNFL Technical and Development Support. Twenty-nine glass forming materials were selected and obtained from vendors for the characterization of their physical properties, durability in caustic solution, and powder flow characteristics. A glass former was selected based on the characterization for each of the ten oxide classes required for Envelope A, B, and C mixtures. Three blends (A, B, and C) were prepared based on formulations provided by Vitreous State Laboratory and evaluated with the same methods employed for the glass formers. The properties obtained are presented in a series of attached Tables. It was determined that five of the ten glass formers, (kyanite, iron oxide, titania, zircon, and zinc oxide) have the potential to cause some level of solids f low problems. In addition, all of the blends may require consideration for their handling. A number of engineering considerations and recommendations were prepared based on the experimental findings, experience, and other process considerations. Recommendations for future testing are included. In conjunction with future work, it is recommended that a professional consultant be engaged to guide and assist with testing and design input

  10. BNFL Report Glass Formers Characterization

    International Nuclear Information System (INIS)

    Schumacher, R.F.

    2000-01-01

    The objective of this task was to obtain powder property data on candidate glass former materials, sufficient to guide conceptual design and estimate the cost of glass former handling facilities as requested under Part B1 of BNFL Technical and Development Support. Twenty-nine glass forming materials were selected and obtained from vendors for the characterization of their physical properties, durability in caustic solution, and powder flow characteristics. A glass former was selected based on the characterization for each of the ten oxide classes required for Envelope A, B, and C mixtures. Three blends (A, B, and C) were prepared based on formulations provided by Vitreous State Laboratory and evaluated with the same methods employed for the glass formers. The properties obtained are presented in a series of attached Tables. It was determined that five of the ten glass formers, (kyanite, iron oxide, titania, zircon, and zinc oxide) have the potential to cause some level of solids f low problems. The problems might include arching or ratholing in the silo/hopper. In addition, all of the blends may require consideration for their handling

  11. Cosmos & Glass

    DEFF Research Database (Denmark)

    Beim, Anne

    1996-01-01

    The article unfolds the architectural visions of glass by Bruno Taut. It refers to inspirations by Paul Sheerbart and litterature and the Crystal Chain, also it analyses the tectonic univers that can be found in the glass pavillion for the Werkbund exposition in Cologne....

  12. Glass Glimpsed

    DEFF Research Database (Denmark)

    Lock, Charles

    2015-01-01

    Glass in poetry as it reflects the viewer and as its power of reflection are both reduced and enhanced by technology.......Glass in poetry as it reflects the viewer and as its power of reflection are both reduced and enhanced by technology....

  13. Zinc at glutamatergic synapses.

    Science.gov (United States)

    Paoletti, P; Vergnano, A M; Barbour, B; Casado, M

    2009-01-12

    It has long been known that the mammalian forebrain contains a subset of glutamatergic neurons that sequester zinc in their synaptic vesicles. This zinc may be released into the synaptic cleft upon neuronal activity. Extracellular zinc has the potential to interact with and modulate many different synaptic targets, including glutamate receptors and transporters. Among these targets, NMDA receptors appear particularly interesting because certain NMDA receptor subtypes (those containing the NR2A subunit) contain allosteric sites exquisitely sensitive to extracellular zinc. The existence of these high-affinity zinc binding sites raises the possibility that zinc may act both in a phasic and tonic mode. Changes in zinc concentration and subcellular zinc distribution have also been described in several pathological conditions linked to glutamatergic transmission dysfunctions. However, despite intense investigation, the functional significance of vesicular zinc remains largely a mystery. In this review, we present the anatomy and the physiology of the glutamatergic zinc-containing synapse. Particular emphasis is put on the molecular and cellular mechanisms underlying the putative roles of zinc as a messenger involved in excitatory synaptic transmission and plasticity. We also highlight the many controversial issues and unanswered questions. Finally, we present and compare two widely used zinc chelators, CaEDTA and tricine, and show why tricine should be preferred to CaEDTA when studying fast transient zinc elevations as may occur during synaptic activity.

  14. A short review on the pulsed laser deposition of Er3+ ion doped oxide glass thin films for integrated optics

    International Nuclear Information System (INIS)

    Irannejad, M.; Zhao, Z.; Jose, G.; Steenson, D.P.; Jha, A.

    2010-01-01

    Short pulsed (ns) excimer laser was employed as a technique for the deposition of more than 2 μm thick glassy films from phosphorous pentoxide and tungsten lanthanum modified tellurite bulk glasses. High quality glass thin films with measured propagation loss less than 0.15, 0.71 and 2.3 dB.cm -1 were obtained after optimization of deposition parameters for silica, siloxane and semiconductor substrates. The optical, spectroscopic and microstructural properties of deposited thin films were compared with bulk glass materials for demonstrating the differences in the properties, which must be optimized for device engineering. Channel waveguides were fabricated after using reactive ion etching technique, up to 2 μm thickness by using CHF 3 and Ar gas mixture

  15. Raman spectrum, quantum mechanical calculations and vibrational assignments of (95% alpha-TeO2/5% Sm2O3) glass.

    Science.gov (United States)

    Shaltout, I; Mohamed, Tarek A

    2007-06-01

    Chozen system of tellurite glasses doped with rare earth oxides (95% alpha-TeO(2)+5% Sm2O3) was prepared by melt quenching. Consequently, the Raman spectrum (150-1250 cm(-1)) of the modified tellurite have been recorded. As a continuation to our normal coordinate analysis, force constants and quantum mechanical (QM) calculations for tbp TeO4(4-) (triagonal bipyramid, C(2v)) and TeO(3+1); Te2O7(6-) (bridged tetrahedral), we have carried out ab initio frequency calculations for tpy TeO3(2-) (triagonal pyramidal, C(3v) and C(s)) and tp TeO3(2-) (triagonal planar, D(3h)) ions. The quantum mechanical calculations at the levels of RHF, B3LYP and MP2 allow confident vibrational assignments and structural identification in the binary oxide glass (95% alpha-TeO2 +5% Sm2O3). The dominant three-dimensional network structures in the modified glass are triagonal pyramidal TeO3 with minor features of short range distorted tbp TeO4 and bridged tetrahedral unit of TeO(3+1), leading to a structure of infinite chain. Therefore, alpha-TeO2/Sm2O3 (95/5%) glass experience structural changes from TeO4 (tbp); Te2O7 (TeO(3+1))-->TeO3 (tpy).

  16. Spin glasses

    CERN Document Server

    Bovier, Anton

    2007-01-01

    Spin glass theory is going through a stunning period of progress while finding exciting new applications in areas beyond theoretical physics, in particular in combinatorics and computer science. This collection of state-of-the-art review papers written by leading experts in the field covers the topic from a wide variety of angles. The topics covered are mean field spin glasses, including a pedagogical account of Talagrand's proof of the Parisi solution, short range spin glasses, emphasizing the open problem of the relevance of the mean-field theory for lattice models, and the dynamics of spin glasses, in particular the problem of ageing in mean field models. The book will serve as a concise introduction to the state of the art of spin glass theory, usefull to both graduate students and young researchers, as well as to anyone curious to know what is going on in this exciting area of mathematical physics.

  17. Multisample conversion of water to hydrogen by zinc for stable isotope determination

    Science.gov (United States)

    Kendall, C.; Coplen, T.B.

    1985-01-01

    Two techniques for the conversion of water to hydrogen for stable isotope ratio determination have been developed that are especially suited for automated multisample analysis. Both procedures involve reaction of zinc shot with a water sample at 450 ??C. in one method designed for water samples in bottles, the water is put in capillaries and is reduced by zinc in reaction vessels; overall savings in sample preparation labor of 75% have been realized over the standard uranium reduction technique. The second technique is for waters evolved under vacuum and is a sealed-tube method employing 9 mm o.d. quartz tubing. Problems inherent with zinc reduction include surface inhomogeneity of the zinc and exchange of hydrogen both with the zinc and with the glass walls of the vessels. For best results, water/zinc and water/glass surface area ratios of vessels should be kept as large as possible.

  18. Tellurite and Tellurate Reduction by the Aerobic Anoxygenic Phototroph Erythromonas ursincola, Strain KR99 Is Carried out by a Novel Membrane Associated Enzyme

    Directory of Open Access Journals (Sweden)

    Chris Maltman

    2017-04-01

    Full Text Available Erythromonas ursincola, strain KR99 isolated from a freshwater thermal spring of Kamchatka Island in Russia, resists and reduces very high levels of toxic tellurite under aerobic conditions. Reduction is carried out by a constitutively expressed membrane associated enzyme, which was purified and characterized. The tellurite reductase has a molecular weight of 117 kDa, and is comprised of two subunits (62 and 55 kDa in a 1:1 ratio. Optimal activity occurs at pH 7.0 and 28 °C. Tellurite reduction has a Vmax of 5.15 µmol/min/mg protein and a Km of 3.36 mM. The enzyme can also reduce tellurate with a Vmax and Km of 1.08 µmol/min/mg protein and 1.44 mM, respectively. This is the first purified membrane associated Te oxyanion reductase.

  19. Infrared Spectroscopy and Raman Scattering Studies on the Structure of Ag2O. B2O3. TeO2 Glass

    International Nuclear Information System (INIS)

    Thazin Myint; Soe Soe Thin; Pho Kaung; Sein Htoon

    2006-06-01

    Infrared spectroscopy investigation of silver - borate - tellurite glasses in the system 0.4 Ag2 O. 0.6 (x B2 O2. (1-x) TeO2) for various of x (0 < x < 1) has been performed in order to understand the glass modifying properties of the TeO2. In pure crystalline TeO2 spectra observed absorption bands at 780 cm-1 and 660 cm-1 have been ascribed to the stretching vibration of TeO bonds in the TeO4 units. In the glass 0.4 Ag2 O. 0.6 (x B2 O3. (1-x) TeO2) the bands at 700 cm-1 and 694 cm-1 are assigned to the symmetric breathing vibration of the boroxol group and the pentaborate one. The glasses show bands at 630 cm-1 which corresponds to the vibrations due to TeO4 units

  20. Zinc oxide overdose

    Science.gov (United States)

    Zinc oxide is an ingredient in many products. Some of these are certain creams and ointments used ... prevent or treat minor skin burns and irritation. Zinc oxide overdose occurs when someone eats one of ...

  1. Zinc and gastrointestinal disease

    Institute of Scientific and Technical Information of China (English)

    Sonja; Skrovanek; Katherine; DiGuilio; Robert; Bailey; William; Huntington; Ryan; Urbas; Barani; Mayilvaganan; Giancarlo; Mercogliano; James; M; Mullin

    2014-01-01

    This review is a current summary of the role that both zinc deficiency and zinc supplementation can play in the etiology and therapy of a wide range of gastrointestinal diseases. The recent literature describing zinc action on gastrointestinal epithelial tight junctions and epithelial barrier function is described. Zinc enhancement of gastrointestinal epithelial barrier function may figure prominently in its potential therapeutic action in several gastrointestinal diseases.

  2. investigation of the effect of zinc oxide-modified gum arabic on polar ...

    African Journals Online (AJOL)

    BARTH EKWUEME

    Gum Arabic solution, a water-based adhesive, was modified with zinc oxide filler and the formulation was applied on wood, ceramic, glass and textile substrates. A strip of paper was used as a common adherent to all the substrates. Zinc oxide increased the viscosity of 30wt% gum Arabic solution and increased bond ...

  3. Investigation of the effect of zinc oxide-modified gum Arabic on polar ...

    African Journals Online (AJOL)

    Gum Arabic solution, a water-based adhesive, was modified with zinc oxide filler and the formulation was applied on wood, ceramic, glass and textile substrates. A strip of paper was used as a common adherent to all the substrates. Zinc oxide increased the viscosity of 30wt% gum Arabic solution and increased bond ...

  4. GLASS BOX

    National Research Council Canada - National Science Library

    Curtis, Laura

    2008-01-01

    The goals of this effort were to develop Glass Box capabilities to allow for the capturing of analyst activities and the associated data resources, track and log the results of automated processing...

  5. YCu(TeO32(NO3(H2O3: a novel layered tellurite

    Directory of Open Access Journals (Sweden)

    Stuart J. Mills

    2016-08-01

    Full Text Available A new hydrated yttrium copper tellurite nitrate, yttrium(III copper(II bis[trioxidotellurate(IV] nitrate trihydrate, has been synthesized hydrothermally in a Teflon-lined autoclave and structurally determined using synchrotron radiation. The new phase is the first example containing yttrium, copper and tellurium in one structure. Its crystal structure is unique, with relatively strongly bound layers extending parallel to (020, defined by YO8, CuO4 and TeO3 polyhedra, while the NO3− anions and one third of the water molecules lie between those layers. The structural unit consists of [Cu2(TeO34]4− loop-branched chains of {Cu...Te...Cu...Te} squares running parallel to [001], which are linked further into layers only through Y(O,H2O8 polyhedra. Weak `secondary' Te bonds and O—H...O hydrogen-bonding interactions, involving water molecules and layer O atoms, link the layers and interlayer species. IR spectroscopic data are also presented.

  6. Tellurites of hexavalent uranium: first observation of polymerized (UO{sub 4}){sup 2-} tetraoxido cores

    Energy Technology Data Exchange (ETDEWEB)

    Zadoya, Anastasiya I.; Siidra, Oleg I.; Nazarchuk, Evgeny V.; Bocharov, Sergey N. [Department of Crystallography, St. Petersburg State University (Russian Federation); Bubnova, Rimma S. [Department of Crystallography, St. Petersburg State University (Russian Federation); Institute of Silicate Chemistry, Russian Academy of Sciences, St. Petersburg (Russian Federation)

    2016-09-15

    Two novel Ca{sub 2}(UO{sub 3})(TeO{sub 3}){sub 2} (1) and K{sub 2}(UO{sub 2}){sub 2}O{sub 2}(TeO{sub 3}) (2) uranyl tellurites were obtained from telluric acid, used as a starting reagent for both compounds. In 1, the tetraoxido core is coordinated by TeO{sub 3} groups and UO{sub 4} squares polymerize into [UO{sub 3}] chains. The tetraoxido core coordination modes in compound 1 are unique. New layered {sub ∞}{sup 2}[(UO{sub 2}){sub 2}(TeO{sub 3})O{sub 2}]{sup 2-} topology is observed for 2. Both of the compounds were studied by the means of high-temperature X-ray diffraction. The thermal decomposition of 1 and 2 is different and leads to formation of uranate compounds. (copyright 2016 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  7. Self-Q-switching behavior of erbium-doped tellurite microstructured fiber lasers

    International Nuclear Information System (INIS)

    Jia, Zhi-Xu; Yao, Chuan-Fei; Kang, Zhe; Qin, Guan-Shi; Qin, Wei-Ping; Ohishi, Yasutake

    2014-01-01

    We reported self-Q-switching behavior of erbium-doped tellurite microstructured fiber (EDTMF) lasers and further demonstrated a self-Q-switched EDTMF laser with a high repetition rate of more than 1 MHz. A 14 cm EDTMF was used as the gain medium. Upon a pump power of ∼705 mW at 1480 nm, output pulses with a lasing wavelength of ∼1558 nm, a repetition rate of ∼1.14 MHz, and a pulse width of ∼282 ns were generated from the fiber by employing a linear cavity. The maximum output power was ∼316 mW and the slope efficiency was about 72.6% before the saturation of the laser power. Moreover, the influence of the fiber length on laser performances was investigated. The results showed that self-Q-switching behavior in our experiments was caused by the re-absorption originated from the ineffectively pumped part of the active fiber.

  8. Zinc in human serum

    International Nuclear Information System (INIS)

    Kiilerich, S.

    1987-01-01

    The zinc ion is essential for the living organism. Many pathological conditions have been described as a consequence of zinc deficiency. As zinc constitutes less than 0.01 per cent of the body weight, it conventionally belongs to the group of trace elements. The method of atomic absorption spectrophotometry is used to measure the concentration of zinc in serum and urine from healthy persons. The assumptions of the method is discussed. The importance of proteinbinding, diet and the diurnal variation of serum zinc concentration is presented. Serum versus plasma zinc concentration is discussed. Reference serum zinc values from 104 normal subjects are given. Zinc in serum is almost entirely bound to proteins. A preliminary model for the estimation of the distribution of zinc between serum albumin and α 2 -macroglobulin is set up. This estimate has been examined by an ultracentrufugation method. The binding of zinc to a α 2 -macroglobulin in normal persons is appoximately 7 per cent, in patients with cirrhosis of the liver of alcoholic origin approximately 6 per cent, in patients with insulin dependent diabetes mellitus approximately 5 per cent, and in patients with chronic renal failure approximately 2 per cent. It is concluded, therefore, that for clinical purposes it is sufficient to use the concentration of total serum zinc corrected for the concentration of serum albumin. (author)

  9. Tellurite-, tellurate-, and selenite-based anaerobic respiration by strain CM-3 isolated from gold mine tailings.

    Science.gov (United States)

    Maltman, Chris; Piercey-Normore, Michele D; Yurkov, Vladimir

    2015-09-01

    The newly discovered strain CM-3, a Gram-negative, rod-shaped bacterium from gold mine tailings of the Central Mine in Nopiming Provincial Park, Canada, is capable of dissimilatory anaerobic reduction of tellurite, tellurate, and selenite. CM-3 possesses very high level resistance to these oxides, both aerobically and anaerobically. During aerobic growth, tellurite and tellurate resistance was up to 1500 and 1000 µg/ml, respectively. In the presence of selenite, growth occurred at the highest concentration tested, 7000 µg/ml. Under anaerobic conditions, resistance was decreased to 800 µg/ml for the Te oxides; however, much like under aerobic conditions, growth with selenite still took place at 7000 µg/ml. In the absence of oxygen, CM-3 couples oxide reduction to an increase in biomass. Following an initial drop in viable cells, due to switching from aerobic to anaerobic conditions, there was an increase in CFU/ml greater than one order of magnitude in the presence of tellurite (6.6 × 10(3)-8.6 × 10(4) CFU/ml), tellurate (4.6 × 10(3)-1.4 × 10(5) CFU/ml), and selenite (2.7 × 10(5)-5.6 × 10(6) CFU/ml). A control culture without metalloid oxides showed a steady decrease in CFU/ml with no recovery. ATP production was also increased in the presence of each oxide, further indicating anaerobic respiration. Partial 16S rRNA gene sequencing revealed a 99.0 % similarity of CM-3 to Pseudomonas reactans.

  10. Effect of Ga2O3 on the spectroscopic properties of erbium-doped boro-bismuth glasses.

    Science.gov (United States)

    Ling, Zhou; Ya-Xun, Zhou; Shi-Xun, Dai; Tie-Feng, Xu; Qiu-Hua, Nie; Xiang, Shen

    2007-11-01

    The spectroscopic properties and thermal stability of Er3+-doped Bi2O3-B2O3-Ga2O3 glasses are investigated experimentally. The effect of Ga2O3 content on absorption spectra, the Judd-Ofelt parameters Omega t (t=2, 4, 6), fluorescence spectra and the lifetimes of Er3+:4I 13/2 level are also investigated, and the stimulated emission cross-section is calculated from McCumber theory. With the increasing of Ga2O3 content in the glass composition, the Omega t (t=2, 4, 6) parameters, fluorescence full width at half maximum (FWHM) and the 4I 13/2 lifetimes of Er3+ first increase, reach its maximum at Ga2O3=8 mol.%, and then decrease. The results show that Er3+-doped 50Bi2O3-42B2O3-8Ga2O3 glass has the broadest FWHM (81nm) and large stimulated emission cross-section (1.03 x1 0(-20)cm2) in these glass samples. Compared with other glass hosts, the gain bandwidth properties of Er+3-doped Bi2O3-B2O3-Ga2O3 glass is better than tellurite, silicate, phosphate and germante glasses. In addition, the lifetime of 4I 13/2 level of Er(3+) in bismuth-based glass, compared with those in other glasses, is relative low due to the high-phonon energy of the B-O bond, the large refractive index of the host and the existence of OH* in the glass. At the same time, the glass thermal stability is improved in which the substitution of Ga2O3 for B2O3 strengthens the network structure. The suitability of bismuth-based glass as a host for a Er3+-doped broadband amplifier and its advantages over other glass hosts are also discussed.

  11. Application of zinc oxide quantum dots in food safety

    Science.gov (United States)

    Zinc oxide quantum dots (ZnO QDs) are nanoparticles of purified powdered ZnO. The ZnO QDs were directly added into liquid foods or coated on the surface of glass jars using polylactic acid (PLA) as a carrier. The antimicrobial activities of ZnO QDs against Listeria monocytogenes, Salmonella Enteriti...

  12. Optical, electrical and solid state properties of nano crystalline zinc ...

    African Journals Online (AJOL)

    Semiconducting Zinc Sulphide (ZnS) thin films were deposited on glass substrate using relatively simple Chemical Bath Deposition (CBD) technique. Nano crystalline ZnS thin films were fabricated in the study. Optical characterization of the films showed that the materials are transparent to visible light, opaque to ultraviolet ...

  13. Effects of Deposition Potentialon the Optical Properties of Zinc ...

    African Journals Online (AJOL)

    Thin films of Zinc Sulphide (ZnS) were grown on glass substrate by electrodeposition technique. The optical characterization of the grown films (ZnS) was done by using a Janway 6405 UV-VIS spectrophotometer in the range of 300-900nm using a step size of 20. The effect of deposition potential variationon the films optical ...

  14. The effects of Nd2O3 concentration in the laser emission of TeO2-ZnO glasses

    Science.gov (United States)

    Moreira, L. M.; Anjos, V.; Bell, M. J. V.; Ramos, C. A. R.; Kassab, L. R. P.; Doualan, D. J. L.; Camy, P.; Moncorgé, R.

    2016-08-01

    The present work reports the modification introduced by different Nd2O3 concentration on optical properties and the laser operation of Nd3+ doped (TeO2-ZnO) bulk tellurite glass. The spectroscopic data are analyzed within the Judd Ofelt formalism framework and the results are compared to the fluorescence lifetime and emission measurements to derive values for the quantum efficiency and the stimulated emission cross section of the considered 4F3/2 → 4I11/2 infrared laser transition around 1062.5 nm. Continuous-wave laser action is achieved with this bulk tellurite glass by pumping the sample inside a standard plan-concave mirror laser cavity with different output couplers. It is possible to observe coherent emission only for the lower concentration (0.5%(wt.) of Nd2 O3). Also laser action could only be observed for this sample with threshold pump power of 73 mW associated with a laser slope efficiency of 8% for an output coupler transmission of 4% indicating that TeO2-ZnO are potential materials for laser action. The results presented in this work together with those previously reported with higher concentration (1.0% (wt) of Nd2O3) determine the adequate Nd2O3 concentration for laser action and guide the correct experimental procedure for TeO2-ZnO glasses preparation.

  15. Cation coordination in oxychloride glasses

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, J A [Energy Technology Division, Argonne National Laboratory, Argonne, IL (United States); Holland, D [Physics Department, Warwick University, Coventry (United Kingdom); Bland, J [Physics Department, University of Liverpool, PO Box 147, Liverpool (United Kingdom); Johnson, C E [Physics Department, Northern Illinois University, DeKalb, IL (United States); Thomas, M F [Physics Department, University of Liverpool, PO Box 147, Liverpool (United Kingdom)

    2003-02-19

    Glasses containing mixtures of cations and anions of nominal compositions [Sb{sub 2}O{sub 3}]{sub x} - [ZnCl{sub 2}]{sub 1-x} where x = 0.25, 0.50, 0.75, and 1.00, have been studied by means of neutron diffraction and Raman and Moessbauer spectroscopy. There is preferential bonding within the system with the absence of Sb-Cl bonds. Antimony is found to be threefold coordinated to oxygen, and zinc fourfold coordinated. The main contributing species are of the form [Sb(OSb){sub 2}(OZn)] and [Zn(ClZn){sub 2}(OSb){sub 2}].

  16. Cation coordination in oxychloride glasses

    International Nuclear Information System (INIS)

    Johnson, J A; Holland, D; Bland, J; Johnson, C E; Thomas, M F

    2003-01-01

    Glasses containing mixtures of cations and anions of nominal compositions [Sb 2 O 3 ] x - [ZnCl 2 ] 1-x where x = 0.25, 0.50, 0.75, and 1.00, have been studied by means of neutron diffraction and Raman and Moessbauer spectroscopy. There is preferential bonding within the system with the absence of Sb-Cl bonds. Antimony is found to be threefold coordinated to oxygen, and zinc fourfold coordinated. The main contributing species are of the form [Sb(OSb) 2 (OZn)] and [Zn(ClZn) 2 (OSb) 2

  17. Glass compositions

    Energy Technology Data Exchange (ETDEWEB)

    France, P W

    1985-05-30

    A fluoride glass for use in the production of optical fibres has an enhanced D/H ratio, preferably such that OD:OH is at least 9:1. In the example, such a glass is prepared by treating with D/sub 2/O a melt comprising 51.53 mole per cent ZrF/sub 4/, 20.47 mole per cent BaF/sub 2/, 5.27 mole per cent LaF/sub 3/, 3.24 mole per cent AlF/sub 3/, and 19.49 mole per cent LiF.

  18. Characteristics of indium zinc oxide films deposited using the facing targets sputtering method for OLEDs applications

    International Nuclear Information System (INIS)

    Rim, Y.S.; Kim, H.J.; Kim, K.H.

    2010-01-01

    The amorphous indium zinc oxide (IZO) thin films were deposited on polyethersulfone (PES) and glass substrates using the facing targets sputtering (FTS) system. The electrical, optical and structural properties of the IZO thin films deposited as functions of sputtering parameters on the glass and PES substrates. An optimal IZO deposition condition is fabricated for organic light-emitting device (OLED) based on glass and PES. The amorphous IZO anode-based OLEDs show superior current density and luminance characteristics.

  19. Continuous reduction of tellurite to recoverable tellurium nanoparticles using an upflow anaerobic sludge bed (UASB) reactor.

    Science.gov (United States)

    Ramos-Ruiz, Adriana; Sesma-Martin, Juan; Sierra-Alvarez, Reyes; Field, Jim A

    2017-01-01

    According to the U.S. Department of Energy and the European Union, tellurium is a critical element needed for energy and defense technology. Thus methods are needed to recover tellurium from waste streams. The objectives of this study was to determine the feasibility of utilizing upflow anaerobic sludge bed (UASB) reactors to convert toxic tellurite (Te IV ) oxyanions to non-toxic insoluble elemental tellurium (Te 0 ) nanoparticles (NP) that are amendable to separation from aqueous effluents. The reactors were supplied with ethanol as the electron donating substrate to promote the biological reduction of Te IV . One reactor was additionally amended with the redox mediating flavonoid compound, riboflavin (RF), with the goal of enhancing the bioreduction of Te IV . Its performance was compared to a control reactor lacking RF. The continuous formation of Te 0 NPs using the UASB reactors was found to be feasible and remarkably improved by the addition of RF. The presence of this flavonoid was previously shown to enhance the conversion rate of Te IV by approximately 11-fold. In this study, we demonstrated that this was associated with the added benefit of reducing the toxic impact of Te IV towards the methanogenic consortium in the UASB and thus enabled a 4.7-fold higher conversion rate of the chemical oxygen demand. Taken as a whole, this work demonstrates the potential of a methanogenic granular sludge to be applied as a bioreactor technology producing recoverable Te 0 NPs in a continuous fashion. Copyright © 2016 Elsevier Ltd. All rights reserved.

  20. Simple one-pot aqueous synthesis of CdHgTe nanocrystals using sodium tellurite as the Te source

    International Nuclear Information System (INIS)

    Shen, Zhitao; Luo, Chunhua; Huang, Rong; Wang, Yiting; Peng, Hui; Travas-sejdic, Jadranka

    2014-01-01

    In this work, we systematically investigated the one-pot aqueous synthesis conditions of CdHgTe nanocrystals (NCs) using sodium tellurite (Na 2 TeO 3 ) as the Te source, and found that the added content of Hg 2+ and the initial pH value of reaction solutions significantly affected the photoluminescence quantum yield (PL QY) of alloyed CdHgTe NCs. When the concentration of Cd was 1.0 mmol L −1 , the mole ratio of Cd/Te/Hg/MPA was 1:0.5:0.05:2.4, and the initial pH value of the reaction solution was about 8.78, the PL QY of as-prepared CdHgTe NCs was up to 45%. Characterization by HRTEM and XRD confirmed the crystalline nature of CdHgTe NCs. Compared to other synthetic approaches of CdHgTe NCs, our experimental results indicate that Na 2 TeO 3 could be an attractive alternative Te source to directly synthesize CdHgTe NCs in aqueous media. - Highlights: • A one-pot method was developed for the synthesis of highly luminescent CdHgTe nanocrystals (NCs). • Sodium tellurite was used as the Te source. • The quantum yield reached up to 45%. • The experimental conditions were optimized and the prepared CdHgTe NCs were characterized

  1. Large optical second-order nonlinearity of poled WO3-TeO2 glass.

    Science.gov (United States)

    Tanaka, K; Narazaki, A; Hirao, K

    2000-02-15

    Second-harmonic generation, one of the second-order nonlinear optical properties of thermally and electrically poled WO>(3)-TeO>(2) glasses, has been examined. We poled glass samples with two thicknesses (0.60 and 0.86 mm) at various temperatures to explore the effects of external electric field strength and poling temperature on second-order nonlinearity. The dependence of second-harmonic intensity on the poling temperature is maximum at a specific poling temperature. A second-order nonlinear susceptibility of 2.1 pm/V was attained for the 0.60-mm-thick glass poled at 250 degrees C. This value is fairly large compared with those for poled silica and tellurite glasses reported thus far. We speculate that the large third-order nonlinear susceptibility of WO>(3)- TeO>(2) glasses gives rise to the large second-order nonlinearity by means of a X((2)) = 3X((3)) E(dc) process.

  2. Chelators for investigating zinc metalloneurochemistry

    OpenAIRE

    Radford, Robert John; Lippard, Stephen J.

    2013-01-01

    The physiology and pathology of mobile zinc signaling has become an important topic in metalloneurochemistry. To study the action of mobile zinc effectively, specialized tools are required that probe the temporal and positional changes of zinc ions within live tissue and cells. In the present article we describe the design and implementation of selective zinc chelators as antagonists to interrogate the function of mobile zinc, with an emphasis on the pools of vesicular zinc in the terminals o...

  3. Zinc triggers microglial activation.

    Science.gov (United States)

    Kauppinen, Tiina M; Higashi, Youichirou; Suh, Sang Won; Escartin, Carole; Nagasawa, Kazuki; Swanson, Raymond A

    2008-05-28

    Microglia are resident immune cells of the CNS. When stimulated by infection, tissue injury, or other signals, microglia assume an activated, "ameboid" morphology and release matrix metalloproteinases, reactive oxygen species, and other proinflammatory factors. This innate immune response augments host defenses, but it can also contribute to neuronal death. Zinc is released by neurons under several conditions in which microglial activation occurs, and zinc chelators can reduce neuronal death in animal models of cerebral ischemia and neurodegenerative disorders. Here, we show that zinc directly triggers microglial activation. Microglia transfected with a nuclear factor-kappaB (NF-kappaB) reporter gene showed a severalfold increase in NF-kappaB activity in response to 30 microm zinc. Cultured mouse microglia exposed to 15-30 microm zinc increased nitric oxide production, increased F4/80 expression, altered cytokine expression, and assumed the activated morphology. Zinc-induced microglial activation was blocked by inhibiting NADPH oxidase, poly(ADP-ribose) polymerase-1 (PARP-1), or NF-kappaB activation. Zinc injected directly into mouse brain induced microglial activation in wild-type mice, but not in mice genetically lacking PARP-1 or NADPH oxidase activity. Endogenous zinc release, induced by cerebral ischemia-reperfusion, likewise induced a robust microglial reaction, and this reaction was suppressed by the zinc chelator CaEDTA. Together, these results suggest that extracellular zinc triggers microglial activation through the sequential activation of NADPH oxidase, PARP-1, and NF-kappaB. These findings identify a novel trigger for microglial activation and a previously unrecognized mechanism by which zinc may contribute to neurological disorders.

  4. Synthesis of zinc sulfide by chemical vapor deposition using an organometallic precursor: Di-tertiary-butyl-disulfide

    International Nuclear Information System (INIS)

    Vasekar, Parag; Dhakal, Tara; Ganta, Lakshmikanth; Vanhart, Daniel; Desu, Seshu

    2012-01-01

    Zinc sulfide has gained popularity in the last few years as a cadmium-free heterojunction partner for thin film solar cells and is seen as a good replacement for cadmium sulfide due to better blue photon response and non-toxicity. In this work, zinc sulfide films are prepared using an organic sulfur source. We report a simple and repeatable process for development of zinc sulfide using a cost-effective and less hazardous organic sulfur source. The development of zinc sulfide has been studied on zinc oxide-coated glass where the zinc oxide is converted into zinc sulfide. Zinc oxide grown by atomic layer deposition as well as commercially available zinc oxide-coated glass was used. The zinc sulfide synthesis has been studied and the films are characterized using scanning electron microscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and a UV–VIS spectrophotometer. XRD, XPS and optical characterization confirm the zinc sulfide phase formation. - Highlights: ► Synthesis of ZnS using a less-hazardous precursor, di-tertiary-butyl-disulfide. ► ZnS process optimized for two types of ZnO films. ► Preliminary results for a solar cell show an efficiency of 1.09%.

  5. Glass: Rotary Electric Glass Furnace

    Energy Technology Data Exchange (ETDEWEB)

    Recca, L.

    1999-01-29

    Compared to conventional gas-fired furnaces, the new rotary electric furnace will increase energy efficiency while significantly reducing air emissions, product turnaround time, and labor costs. As this informative new fact sheet explains, the thousand different types of glass optical blanks produced for the photonics industry are used for lasers, telescopes, cameras, lights, and many other products.

  6. Spectroscopic investigation of Er{sup 3+} in fluorotellurite glasses for 2.7 μm luminescence

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Feng; Bi, Zhuanfang; Chen, Jiayang; Huang, Anping [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Ministry of Education), School of Physics and Nuclear Energy Engineering, Beihang University, Beijing, 100191 (China); Zhu, Yongchang [China Building Materials Academy, Beijing, 100024 (China); Chen, Baojie [Department of Electronic Engineering, City University of Hong Kong, Kowloon, Hong Kong (China); Xiao, Zhisong, E-mail: zsxiao@buaa.edu.cn [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Ministry of Education), School of Physics and Nuclear Energy Engineering, Beihang University, Beijing, 100191 (China)

    2015-11-15

    Er{sup 3+} doped fluorotellurite glass (TeO{sub 2}–BaF{sub 2}–NaF) with different Er{sup 3+} concentrations were prepared, glass thermal stability and structure were investigated by differential scanning calorimetry (DSC) test and Raman spectrum, respectively. 2.7 μm light emission was observed under 980 nm excitation in these fluorotellurite glasses. The 2.7 μm emission properties were investigated through the measured absorption and emission spectra. The spontaneous transition probability (A), branching ratio (β), emission and absorption cross sections were calculated and the values were relatively larger than some reported values, which indicated that this kind of fluorotellurite glass has potential application as host material for 2.7 μm lasers. - Highlights: • High T{sub g} (375 °C) provides good thermal stability to resist thermal damage. • The introduction of F{sup −} decreases the connectivity of the tellurite former network. • Er{sup 3+} doped TBN glasses have been investigated using Judd–Ofelt (JO) theory. • TBN glasses possess high stimulated emission cross section σ{sub e} for 2.7 μm emission.

  7. Nitrate glass

    International Nuclear Information System (INIS)

    Kirilenko, I.A.; Vinogradov, E.E.

    1977-01-01

    Experimental evidence on behaviour of nitrate glasses is reviewed in terms of relationships between the presence of water in vitrescent nitrate systems and the properties of the systems. The glasses considered belong to systems of Mg(NO 3 ) 2 - Nd(NO 3 ) 3 ; Hg(NO 3 ) 2 -Nd(NO 3 ) 3 ; NaNO 3 -Mg(NO 3 ) 2 -Nd(NO 3 ) 3 ; M-Zn(NO 3 ) 3 , where M is a mixture of 20% mass NaNO 3 and 80% mass Mg(NO 3 ) 2 , and Zn is a rare earth ion. Nitrate glass is shown to be a product of dehydration. Vitrification may be regarded as a resusl of formation of molecular complexes in the chain due to hydrogen bonds of two types, i.e. water-water, or water-nicrate group. Chain formation, along with low melting points of the nitrates, hinder crystallization of nitrate melts. Provided there is enough water, this results in vitrification

  8. Zinc phosphate conversion coatings

    Science.gov (United States)

    Sugama, Toshifumi

    1997-01-01

    Zinc phosphate conversion coatings for producing metals which exhibit enhanced corrosion prevention characteristics are prepared by the addition of a transition-metal-compound promoter comprising a manganese, iron, cobalt, nickel, or copper compound and an electrolyte such as polyacrylic acid, polymethacrylic acid, polyitaconic acid and poly-L-glutamic acid to a phosphating solution. These coatings are further improved by the incorporation of Fe ions. Thermal treatment of zinc phosphate coatings to generate .alpha.-phase anhydrous zinc phosphate improves the corrosion prevention qualities of the resulting coated metal.

  9. Er{sup 3+}-doped fluorotellurite thin film glasses with improved photoluminescence emission at 1.53 µm

    Energy Technology Data Exchange (ETDEWEB)

    Morea, R. [Laser Processing Group, Instituto de Optica, CSIC, Serrano 121, 28006 Madrid (Spain); Miguel, A. [Departamento de Física Aplicada I, Escuela Superior de Ingeniería, Universidad del País Vasco UPV/EHU, Alda. Urquijo s/n, 48013 Bilbao (Spain); Fernandez, T.T. [Laser Processing Group, Instituto de Optica, CSIC, Serrano 121, 28006 Madrid (Spain); Maté, B. [Instituto de Estructura de la Materia, CSIC, Serrano 121, 28006 Madrid (Spain); Ferrer, F.J. [Centro Nacional de Aceleradores, Univ. Sevilla-CSIC, Av. Thomas A. Edison 7, 41092 Sevilla (Spain); Maffiotte, C. [CIEMAT, Departamento de Tecnología, Av. Complutense 40, 28040 Madrid (Spain); Fernandez, J.; Balda, R. [Departamento de Física Aplicada I, Escuela Superior de Ingeniería, Universidad del País Vasco UPV/EHU, Alda. Urquijo s/n, 48013 Bilbao (Spain); Materials Physics Center CSIC-UPV/EHU and Donostia International Physics Center, 20018 San Sebastian (Spain); Gonzalo, J., E-mail: j.gonzalo@csic.es [Laser Processing Group, Instituto de Optica, CSIC, Serrano 121, 28006 Madrid (Spain)

    2016-02-15

    Transparent oxyfluoride tellurite thin film glasses have been produced at room temperature by pulsed laser deposition in O{sub 2} atmosphere from an Er-doped TeO{sub 2}–ZnO–ZnF{sub 2} bulk glass. Thin film glasses present high refractive index (n≥1.95) and good transparency (T≥80%) in the visible (λ>400 nm) and near infrared range. However, their photoluminescence (PL) performance at 1.5 μm is poor. Thermal annealing at moderate temperatures (T≤315 °C), well below glass crystallization, increases the PL intensity by more than one order of magnitude as well as the PL lifetime up to τ≈3.3 ms. Film glasses present a larger fraction of TeO{sub 3} trigonal pyramids than the bulk glass and a very large OH{sup −} content. The structure and composition of film glasses do not change upon annealing and thus the activation of the PL response is related to the improvement of the surface morphology and the significant decrease of their OH{sup −} content. - Highlights: • Transparent Er-doped fluorotellurite films are produced by pulsed laser deposition. • Post-deposition thermal treatments are required to activate Er{sup 3+} photoluminescence. • {sup 4}I{sub 13/2}→{sup 4}I{sub 15/2} emission spectrum is similar for bulk and annealed film glasses. • {sup 4}I{sub 13/2} level fluorescence decay is shorter in annealed films than in bulk glasses. • Photoluminescence response relates to hydroxyl groups concentration in film glasses.

  10. Leaky mode suppression in planar optical waveguides written in Er:TeO{sub 2}–WO{sub 3} glass and CaF{sub 2} crystal via double energy implantation with MeV N{sup +} ions

    Energy Technology Data Exchange (ETDEWEB)

    Bányász, I., E-mail: banyasz@sunserv.kfki.hu [Department of Crystal Physics, Wigner Research Centre for Physics, Hungarian Academy of Sciences, P.O.B. 49, H-1525 Budapest (Hungary); Zolnai, Z.; Fried, M. [Research Institute for Technical Physics and Materials Science, Research Centre for Natural Sciences, Hungarian Academy of Sciences, P.O.B. 49, Budapest H-1525 (Hungary); Berneschi, S. [MDF-Lab, “Nello Carrara” Institute of Applied Physics, IFAC-CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino (Italy); “Enrico Fermi” Center for Study and Research, Piazza del Viminale 2, 00184 Roma (Italy); Pelli, S.; Nunzi-Conti, G. [MDF-Lab, “Nello Carrara” Institute of Applied Physics, IFAC-CNR, Via Madonna del Piano 10, 50019 Sesto Fiorentino (Italy)

    2014-05-01

    Ion implantation proved to be an universal technique for producing waveguides in most optical materials. Tellurite glasses are good hosts of rare-earth elements for the development of fibre and integrated optical amplifiers and lasers covering all the main telecommunication bands. Er{sup 3+}-doped tellurite glasses are good candidates for the fabrication of broadband amplifiers in wavelength division multiplexing around 1.55 μm, as they exhibit large stimulated cross sections and broad emission bandwidth. Calcium fluoride is an excellent optical material, due to its perfect optical characteristics from UV wavelengths up to near IR. It has become a promising laser host material (doped with rare earth elements). Ion implantation was also applied to optical waveguide fabrication in CaF{sub 2} and other halide crystals. In the present work first single-energy implantations at 3.5 MeV at various fluences were applied. Waveguide operation up to 1.5 μm was observed in Er:Te glass, and up to 980 nm in CaF{sub 2}. Then double-energy implantations at a fixed upper energy of 3.5 MeV and lower energies between 2.5 and 3.2 MeV were performed to suppress leaky modes by increasing barrier width.

  11. Zinc fingers, zinc clusters, and zinc twists in DNA-binding protein domains

    International Nuclear Information System (INIS)

    Vallee, B.L.; Auld, D.S.; Coleman, J.E.

    1991-01-01

    The authors recognize three distinct motifs of DNA-binding zinc proteins: (i) zinc fingers, (ii) zinc clusters, and (iii) zinc twists. Until very recently, x-ray crystallographic or NMR three-dimensional structure analyses of DNA-binding zinc proteins have not been available to serve as standards of reference for the zinc binding sites of these families of proteins. Those of the DNA-binding domains of the fungal transcription factor GAL4 and the rat glucocorticoid receptor are the first to have been determined. Both proteins contain two zinc binding sites, and in both, cysteine residues are the sole zinc ligands. In GAL4, two zinc atoms are bound to six cysteine residues which form a zinc cluster akin to that of metallothionein; the distance between the two zinc atoms of GAL4 is ∼3.5 angstrom. In the glucocorticoid receptor, each zinc atom is bound to four cysteine residues; the interatomic zinc-zinc distance is ∼13 angstrom, and in this instance, a zinc twist is represented by a helical DNA recognition site located between the two zinc atoms. Zinc clusters and zinc twists are here recognized as two distinctive motifs in DNA-binding proteins containing multiple zinc atoms. For native zinc fingers, structural data do not exist as yet; consequently, the interatomic distances between zinc atoms are not known. As further structural data become available, the structural and functional significance of these different motifs in their binding to DNA and other proteins participating in the transmission of the genetic message will become apparent

  12. Zinc in diet

    Science.gov (United States)

    ... Effects Symptoms of zinc deficiency include: Frequent infections Hypogonadism in males Loss of hair Poor appetite Problems with the ... any medical emergency or for the diagnosis or treatment of any medical condition. A licensed physician should ...

  13. Optical properties and crystallization kinetics of (TeO{sub 2})(ZnO)(TiO{sub 2}) glasses

    Energy Technology Data Exchange (ETDEWEB)

    Kabalci, Idris [Department of Physics Education, Education Faculty, Harran University, Sanliurfa (Turkey); Koerpe, Nese Oeztuerk [Department of Materials Science, Eskisehir, Osmangazi University, Eskisehir (Turkey); Duran, Tugba; Oezdemir, Mustafa [Department of Physics, Science and Arts Faculty, Marmara University, Istanbul (Turkey)

    2011-09-15

    Ternary tellurite based glasses in the (TeO{sub 2})(ZnO)(TiO{sub 2}) system were prepared and its optical properties and crystallization kinetics investigated by using UV-VIS spectrophotometer and differential thermal analyzer (DTA). All the glasses were transparent from visible to near infrared region for different ZnO glass compositions (x=0.05, 0.10, 0.20, and 0.30 mol). In the experiment, optical band gap and Urbach energies were estimated from the optical absorption spectra between 400 and 800 nm wavelength region. The observed results confirm that the addition of ZnO glass composition from 0.05 to 0.30 mol increases the optical band gap energy from 2.94 to 3.0 eV. In addition, glass transition (T{sub g}), crystallization (T{sub p}) and melting temperature (T{sub m}) were determined by using the DTA plots. Finally, DTA results obtained with a heating rate of 20 C/min show that the peak crystallization temperature increases from 463 to 533 C as the ZnO content increases from 0.05 to 0.30 mol (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  14. Optical Properties of Ternary TeO2-B2O3-ZnO Glass System

    Energy Technology Data Exchange (ETDEWEB)

    Ayuni, J N; Halimah, M K; Talib, Z A; Sidek, H A A; Daud, W M; Zaidan, A W; Khamirul, A M, E-mail: nfarhanayuni@gmail.com, E-mail: halimah@science.upm.edu.my [Department of Physics, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia)

    2011-02-15

    A series of ternary tellurite based glasses [(TeO2)70 (B203)30]100-x [ZnO]x glasses with different compositions of ZnO (x= 5 to 30 wt.% in steps of 5 wt.%) have been synthesized by melt quenching method. The role of ZnO to the glasses structure was studied by IR spectroscopy. FTIR spectra revealed broad, weak and strong absorption bands in the investigated range of wavenumber from 280-4000 cm-1 which associated with their corresponding bond modes of vibration and the glass structure. The indirect optical band gap and the direct optical band gap are in the range 2.08-3.12 and 1.54-2.36 eV, respectively. A decrease in the values of energy band gap Eg may come down to the reason that the non-bridging oxygen ion content increases with increasing ZnO content and shifting the band edge to lower energies. The optical band gap and Urbach energies were calculated from the absorption spectra measured between 190 and 900 nm at room temperature. The refractive index, n of the glasses change from 1.84-2.00 while the molar refractivities decrease from 13.06 to 12.00 with the increase of ZnO in mol%.

  15. Optical properties of ternary TeO2-B2O3-ZnO Glass system

    International Nuclear Information System (INIS)

    Nurfarhana Ayuni Joha; Halimah, M.K.; Talib, Z.A.; Sidek, H.A.A.; Daud, W.M.; Zaidan, A.W.; Khamirul, A.M.

    2009-01-01

    Full text: A series of ternary tellurite based glasses [ (TeO 2 ) 70 (B 2 0 3 ) 30 ] 100-x [ZnO] x glasses with different compositions of ZnO (x= 5 to 30 wt.% in steps of 5 wt.%) have been synthesized by melt quenching method. The role of ZnO to the glasses structure was studied by IR spectroscopy. FTIR spectra revealed broad, weak and strong absorption bands in the investigated range of wavenumber from 280 - 4000 cm -1 which associated with their corresponding bond modes of vibration and the glass structure. The indirect optical band gap and the direct optical band gap are in the range 2.08-3.12 and 1.54-2.36 eV, respectively. An increase in the values of energy band gap E g may come down to the reason that the non-bridging oxygen ion content decreases with increasing ZnO content and shifting the band edge to higher energies. The optical band gap and Urbach energies were calculated from the absorption spectra measured between 190 and 900 nm at room temperature. The refractive index, n of the glasses change from 1.84 - 2.00 while the molar refractivities decrease from 13.06 to 12.00 with the increase of ZnO in mol %. (author)

  16. Optical Properties of Ternary TeO2-B2O3-ZnO Glass System

    International Nuclear Information System (INIS)

    Ayuni, J N; Halimah, M K; Talib, Z A; Sidek, H A A; Daud, W M; Zaidan, A W; Khamirul, A M

    2011-01-01

    A series of ternary tellurite based glasses [(TeO2)70 (B203)30]100-x [ZnO]x glasses with different compositions of ZnO (x= 5 to 30 wt.% in steps of 5 wt.%) have been synthesized by melt quenching method. The role of ZnO to the glasses structure was studied by IR spectroscopy. FTIR spectra revealed broad, weak and strong absorption bands in the investigated range of wavenumber from 280-4000 cm-1 which associated with their corresponding bond modes of vibration and the glass structure. The indirect optical band gap and the direct optical band gap are in the range 2.08-3.12 and 1.54-2.36 eV, respectively. A decrease in the values of energy band gap Eg may come down to the reason that the non-bridging oxygen ion content increases with increasing ZnO content and shifting the band edge to lower energies. The optical band gap and Urbach energies were calculated from the absorption spectra measured between 190 and 900 nm at room temperature. The refractive index, n of the glasses change from 1.84-2.00 while the molar refractivities decrease from 13.06 to 12.00 with the increase of ZnO in mol%.

  17. The bioavailability of four zinc oxide sources and zinc sulphate in broiler chickens

    OpenAIRE

    Veldkamp, T.; Diepen, van, J.T.M.; Bikker, P.

    2014-01-01

    Zinc is an essential trace element for all farm animal species. It is commonly included in animal diets as zinc oxide, zinc sulphate or organically bound zinc. Umicore Zinc Chemicals developed zinc oxide products with different mean particle sizes. Umicore Zinc Chemicals requested Wageningen UR Livestock Research to determine the bioavailability of four zinc oxide sources and zinc sulphate in broiler chickens. A precise estimate of the bioavailability of zinc sources is required both for fulf...

  18. Red luminescence from Eu3+-doped TeO2-WO3-GeO2 glasses for solid state lasers

    Science.gov (United States)

    Subrahmanyam, Tallam; Gopal, Kotalo Rama; Suvarna, Reniguntla Padma; Jamalaiah, Bungala Chinna

    2018-05-01

    Eu3+-doped oxyfluoro tellurite (TWGEu) glasses were prepared by conventional melt quenching method. The optical band gap energy and covalence between Eu3+ and O2-/F- ions were determined from optical absorption spectra. Using the 5D0 → 7F1,2,4 emission transitions, the Ω2 and Ω4 intensity parameters were determined. These intensity parameters were used to evaluate the radiative parameters such as emission probability rate (AR), luminescence branching ratio (βR) and radiative life time (τR) of 5D0 → 7FJ transitions. The laser characteristic parameters such as stimulated emission cross-section, gain bandwidth and quantum efficiency were determined. The luminescence decay profiles of 5D0 emission level were well fitted to single exponential function for all the concentrations. The experimental results show that the 0.5 mol% of Eu3+-doped TWGEu glass could be the best choice to design red laser sources.

  19. CRYSTALLIZATION IN MULTICOMPONENT GLASSES

    Energy Technology Data Exchange (ETDEWEB)

    KRUGER AA; HRMA PR

    2009-10-08

    In glass processing situations involving glass crystallization, various crystalline forms nucleate, grow, and dissolve, typically in a nonuniform temperature field of molten glass subjected to convection. Nuclear waste glasses are remarkable examples of multicomponent vitrified mixtures involving partial crystallization. In the glass melter, crystals form and dissolve during batch-to-glass conversion, melter processing, and product cooling. Crystals often agglomerate and sink, and they may settle at the melter bottom. Within the body of cooling glass, multiple phases crystallize in a non-uniform time-dependent temperature field. Self-organizing periodic distribution (the Liesegnang effect) is common. Various crystallization phenomena that occur in glass making are reviewed.

  20. Crystallization In Multicomponent Glasses

    International Nuclear Information System (INIS)

    Kruger, A.A.; Hrma, P.R.

    2009-01-01

    In glass processing situations involving glass crystallization, various crystalline forms nucleate, grow, and dissolve, typically in a nonuniform temperature field of molten glass subjected to convection. Nuclear waste glasses are remarkable examples of multicomponent vitrified mixtures involving partial crystallization. In the glass melter, crystals form and dissolve during batch-to-glass conversion, melter processing, and product cooling. Crystals often agglomerate and sink, and they may settle at the melter bottom. Within the body of cooling glass, multiple phases crystallize in a non-uniform time-dependent temperature field. Self-organizing periodic distribution (the Liesegnang effect) is common. Various crystallization phenomena that occur in glass making are reviewed.

  1. Recycling of Glass

    DEFF Research Database (Denmark)

    Christensen, Thomas Højlund; Damgaard, Anders

    2011-01-01

    Glass is used for many purposes, but in the waste system glass is predominantly found in terms of beverage and food containers with a relatively short lifetime before ending up in the waste. Furthermore there is a large amount of flat glass used in building materials which also ends up in the waste...... system; this glass though has a long lifetime before ending up in the waste. Altogether these product types add up to 82% of the production of the European glass industry (IPCC, 2001). Recycling of glass in terms of cleaning and refilling of bottles as well as the use of broken glass in the production...... of new glass containers is well established in the glass industry. This chapter describes briefly howglass is produced and howwaste glass is recycled in the industry. Quality requirements and use of recycled products are discussed, as are the resource and environmental issues of glass recycling....

  2. Relationship between maternal serum zinc, cord blood zinc and ...

    African Journals Online (AJOL)

    Background: Adequate in utero supply of zinc is essential for optimal fetal growth because of the role of zinc in cellular division, growth and differentiation. Low maternal serum zinc has been reported to be associated with low birth weight and the later is associated with increased morbidity and mortality in newborns.

  3. The study and microstructure analysis of zinc and zinc oxide

    Czech Academy of Sciences Publication Activity Database

    Luptáková, Natália; Pešlová, F.; Kliber, J.

    2015-01-01

    Roč. 54, č. 1 (2015), s. 43-46 ISSN 0543-5846 Grant - others:KEGA(SK) KEGA 007 TnUAD-4/2013 Institutional support: RVO:68081723 Keywords : zinc * production of zinc oxide * microstructure * chemical composition * zinc slag Subject RIV: JG - Metal lurgy Impact factor: 0.959, year: 2014

  4. Structural and luminescence behavior of Er(3+) ions doped Barium tellurofluoroborate glasses.

    Science.gov (United States)

    Annapoorani, K; Maheshvaran, K; Arunkumar, S; Suriya Murthy, N; Marimuthu, K

    2015-01-25

    Er(3+) doped Barium tellurofluoroborate glasses (BTFBxE) with the chemical composition (30-x)TeO2+30B2O3+20BaO+20BaF+xEr2O3 (where x=0.01, 0.05, 0.1, 0.5, 1.0 and 2.0 in wt%) were prepared following the melt quenching technique. The different vibrational modes of borates and tellurites in the prepared glasses were explored through FTIR and Raman spectra. The optical absorption spectra have been used to determine the ionic/covalent nature of the metal-ligand bond in the prepared glasses with the help of Nephelauxetic ratio (β) and bonding parameter (δ) studies. The optical band gap of direct and indirect allowed transitions were determined from Tauc's plot and the variations of band gap energy with structural arrangements were discussed. The Urbach energy values were determined and the relatively lower values of the Urbach's energy reveal the minimal degree of disorderness in the prepared glasses. The oscillator strengths (fexp and fcal) and Judd-Ofelt (JO) intensity parameters (Ω2, Ω4 and Ω6) were calculated with the application of JO theory and the trends of the JO intensity parameters are found to be Ω2>Ω6>Ω4 for all the prepared glasses with a minimum variation in Ω2 intensity parameter values. A bright green emission was observed from the (2)H11/2+(4)S3/2→ (4)I15/2 transition and the radiative properties such as transition probability (A), stimulated emission cross-section (σP(E)), branching ratio (βr) and radiative lifetime (τ) were calculated using the JO parameters. The suitability of the prepared glasses for the fabrication of photonic devices were also discussed and reported in the present work. Copyright © 2014 Elsevier B.V. All rights reserved.

  5. Spectroscopic investigations on Pr3+ ions doped lead telluro-borate glasses for photonic applications

    Science.gov (United States)

    Suthanthirakumar, P.; Mariyappan, M.; Marimuthu, K.

    2018-04-01

    A new series of Lead telluro-borate glasses doped with different concentrations of Pr3+ ions (xPLTB) were prepared by melt quenching technique and their structural and spectroscopic properties were investigated by recording XRD, FTIR, optical absorption and luminescence spectral measurements. XRD measurements confirm the amorphous nature and the FTIR spectra reveal the presence of different vibrational modes of borate and tellurite networks in the prepared glasses. The bonding parameter values (δ) obtained from the absorption band positions indicates that the bonding between Pr3+ ions and their surrounding ligands is of ionic in nature. The optical band gap (Eopt) corresponding to the direct and indirect allowed transitions were determined with the framework of tauc's plot. From the luminescence spectra, important radiative parameters such as stimulated emission cross-section (σPE) , branching ratios (βR) and radiative lifetime (τR) were calculated for the dominant emission transition 3P0→3H4 (blue) in order to suggest the suitability of the studied glasses for suitable photonic applications.

  6. Intense green emission from Tb3+- doped Teo2-Wo3-Geo2 glasses

    Science.gov (United States)

    Subrahmanyam, Tallam; Gopal, Kotalo Rama; Suvarna, Reniguntla Padma; Jamalaiah, Bungala Chinna

    2018-04-01

    Tb3+ -doped oxyfluoro tellurite (TWGTb) glasses were prepared by conventional melt quenching technique. The Judd-Ofelt theory has been applied to evaluate the Ωλ (λ=2,4,6) intensity parameters. The TWGTb glasses exhibit 5D3 → 7F5-3 and 5D4 → 7F6-0 transitions when excited at 316 nm wavelength. The variation of intensity of 5D4 → 7F5 (Green) and 5D3 → 7F4 (Blue) transitions and the green to blue (IG/IB) intensity ratios were studied as a function of Tb3+ ions concentration. The laser characteristic parameters such as effective bandwidth (Δλeff), stimulated emission cross-section (σe), gain bandwidth (σe×Δλeff) and optical gain (σe×τR) were determined using the emission spectra and radiative parameters. The luminescence decay profiles exhibit single-exponential nature for all the samples. Based on the experimental results we suggest that the 1.0 mol% of Tb3+-doped TWGTb glass could be the suitable laser host materials to emit intense green luminescence at 545 nm.

  7. Zinc biofortification of cereals

    DEFF Research Database (Denmark)

    Palmgren, Michael; Clemens, Stephan; Williams, Lorraine E.

    2008-01-01

    The goal of biofortification is to develop plants that have an increased content of bioavailable nutrients in their edible parts. Cereals serve as the main staple food for a large proportion of the world population but have the shortcoming, from a nutrition perspective, of being low in zinc...... and other essential nutrients. Major bottlenecks in plant biofortification appear to be the root-shoot barrier and - in cereals - the process of grain filling. New findings demonstrate that the root-shoot distribution of zinc is controlled mainly by heavy metal transporting P1B-ATPases and the metal...... tolerance protein (MTP) family. A greater understanding of zinc transport is important to improve crop quality and also to help alleviate accumulation of any toxic metals....

  8. Electrical properties of V205-ZnO-TeO2 glasses. V205-ZnO-TeO2 kei garasu no denki dendo

    Energy Technology Data Exchange (ETDEWEB)

    Mori, H; Igarashi, J; Sakata, H [Tokai Univ., Tokyo (Japan). Faculty of Engineering

    1993-12-01

    It is known that glasses contained Transition Metal Oxide (TMO) such as V2O5 show a semi-conductivity, those conductive mechanism has been understood according to the Small Polaron Hopping (SPH) theory developed by Mott and Austin. Authors investigated the glass formation regions, de-conductivity([sigma]) and the conductive mechanism for V2O5-Bi2O3-TeO2 glasses as a tellurite glass containing the TMO. It was clarified that the adiabatic SPH and the non-adiabatic SPH are satisfied for the glasses with V2O5>50 mol% and V2O5<50 mol%, respectively. In this study, the electrical properties of V2O5-ZnO-TeO2 glasses were investigated, and the SPH conductions were considered from the standpoints of the polaron band width J, carrier mobility [mu], carrier density Nc. The conductive mechanism and dependence of V2O5 density on Seebeck coefficients Q were clarified in which a formation region of V2O5 is from 30 to 60 mol%. 40 refs., 9 figs., 2 tabs.

  9. Spin glasses

    International Nuclear Information System (INIS)

    Mookerjee, Abhijit

    1976-01-01

    ''Spin glasses'', are entire class of magnetic alloys of moderate dilution, in which the magnetic atoms are far enough apart to be unlike the pure metal, but close enough so that the indirect exchange energy between them (mediated by the s-d interaction between local moments and conduction electrons) dominates all other energies. Characteristic critical phenomena displayed such as freezing of spin orientation at 'Tsub(c)' and spreading of magnetic ordering, are pointed out. Anomalous behaviour, associated with these critical phenomena, as reflected in : (i) Moessbauer spectroscopy giving hyperfine splitting at Tsub(c), (ii) maxima in susceptibility and remanent magnetism, (iii) thermopower maxima and change in slope, (iv) Characteristic cusp in susceptibility and its removal by very small magnetic fields, and (v) conductivity-resistivity measurements, are discussed. Theoretical developments aimed at explaining these phenomena, in particular, the ideas from percolation and localisation theories, and the approach based on the gellations of polymers, are discussed. Finally, a new approach based on renormalisation group in disordered systems is also briefly mentioned. (K.B.)

  10. Photovoltaic cells employing zinc phosphide

    Science.gov (United States)

    Barnett, Allen M.; Catalano, Anthony W.; Dalal, Vikram L.; Masi, James V.; Meakin, John D.; Hall, Robert B.

    1984-01-01

    A photovoltaic cell having a zinc phosphide absorber. The zinc phosphide can be a single or multiple crystal slice or a thin polycrystalline film. The cell can be a Schottky barrier, heterojunction or homojunction device. Methods for synthesizing and crystallizing zinc phosphide are disclosed as well as a method for forming thin films.

  11. Environmental risk limits for zinc

    NARCIS (Netherlands)

    Bodar CWM; SEC

    2007-01-01

    Environmental Riks Limits (ERLs) were derived for zinc. ERLs serve as advisory values to set environmental quality standards in the Netherlands. The ERLs for zinc closely follow the outcomes of earlier discussions on zinc within the Water Framework Directive and EC Regulation 793/93. The ERLs

  12. Environmental risk limits for zinc

    NARCIS (Netherlands)

    Bodar CWM; SEC

    2007-01-01

    Environmental Riks Limits (ERLs) were derived for zinc. ERLs serve as advisory values to set environmental quality standards in the Netherlands. The ERLs for zinc closely follow the outcomes of earlier discussions on zinc within the Water Framework Directive and EC Regulation 793/93. The ERLs refer

  13. The bioavailability of four zinc oxide sources and zinc sulphate in broiler chickens

    NARCIS (Netherlands)

    Veldkamp, T.; Diepen, van J.T.M.; Bikker, P.

    2014-01-01

    Zinc is an essential trace element for all farm animal species. It is commonly included in animal diets as zinc oxide, zinc sulphate or organically bound zinc. Umicore Zinc Chemicals developed zinc oxide products with different mean particle sizes. Umicore Zinc Chemicals requested Wageningen UR

  14. Influence of iron ions on the structural properties of some inorganic glasses

    International Nuclear Information System (INIS)

    Music, S.; Gotic, M.; Popovic, S.; Grzeta, B.

    1987-01-01

    The effects of iron on the structural properties of Zn-borosilicate glass and Pb-metaphosphate glass were studied using x-ray diffraction, 57 Fe Moessbauer spectroscopy and IR spectroscopy. At high concentration of iron the crystallization of zinc ferrite in the glass matrix takes place. X-ray diffraction and 57 Fe Moessbauer spectroscopy showed that the amount of zinc ferrite in Zn-borosilicate glass decreases. In Pb-metaphosphate glass doped with high concentration of α-Fe 2 O 3 , the crystallization of Fe 3 (PO 4 ) 2 is pronounced. The assignments of IR band positions and the corresponding interpretation are given. The importance of this study for the technology of vitrification of high-level radioactive wastes is emphasized. (author) 31 refs.; 6 figs,.; 6 tabs

  15. Alkali-free bioactive glasses for bone regeneration =

    Science.gov (United States)

    Kapoor, Saurabh

    Bioactive glasses and glass-ceramics are a class of third generation biomaterials which elicit a special response on their surface when in contact with biological fluids, leading to strong bonding to living tissues. The purpose of the present study was to develop diopside based alkali-free bioactive glasses in order to achieve good sintering behaviour, high bioactivity, and a dissolution/ degradation rates compatible with the target applications in bone regeneration and tissue engineering. Another aim was to understand the structure-property relationships in the investigated bioactive glasses. In this quest, various glass compositions within the Diopside (CaMgSi2O6) - Fluorapatite (Ca5(PO4)3F) - Tricalcium phosphate (3CaO•P2O5) system have been investigated. All the glasses were prepared by melt-quenching technique and characterized by a wide array of complementary characterization techniques. The glass-ceramics were produced by sintering of glass powders compacts followed by a suitable heat treatment to promote the nucleation and crystallization phenomena. Furthermore, selected parent glass compositions were doped with several functional ions and an attempt to understand their effects on the glass structure, sintering ability and on the in vitro bio-degradation and biomineralization behaviours of the glasses was made. The effects of the same variables on the devitrification (nucleation and crystallization) behaviour of glasses to form bioactive glass-ceramics were also investigated. Some of the glasses exhibited high bio-mineralization rates, expressed by the formation of a surface hydroxyapatite layer within 1-12 h of immersion in a simulated body fluid (SBF) solution. All the glasses showed relatively lower degradation rates in comparison to that of 45S5 Bioglass. Some of the glasses showed very good in vitro behaviour and the glasses co-doped with zinc and strontium showed an in vitro dose dependent behaviour. The as-designed bioactive glasses and glass

  16. Genomic Variability of O Islands Encoding Tellurite Resistance in Enterohemorrhagic Escherichia coli O157:H7 Isolates

    Science.gov (United States)

    Taylor, Diane E.; Rooker, Michelle; Keelan, Monika; Ng, Lai-King; Martin, Irene; Perna, Nicole T.; Burland, N. T. Valerie; Blattner, Fredrick R.

    2002-01-01

    Strains of Escherichia coli causing enterohemorrhagic colitis belonging to the O157:H7 lineage are reported to be highly related. Fifteen strains of E. coli O157:H7 and 1 strain of E. coli O46:H− (nonflagellated) were examined for the presence of potassium tellurite resistance (Ter). Ter genes comprising terABCDEF were shown previously to be part of a pathogenicity island also containing integrase, phage, and urease genes. PCR analysis, both conventional and light cycler based, demonstrated that about one-half of the Ter E. coli O157:H7 strains (6 of 15), including the Sakai strain, which has been sequenced, carried a single copy of the Ter genes. Five of the strains, including EDL933, which has also been sequenced, contained two copies. Three other O157:H7 strains and the O46:H− strain did not contain the Ter genes. In strains containing two copies, the Ter genes were associated with the serW and serX tRNA genes. Five O157:H7 strains resembled the O157 Sakai strain whose sequence contained one copy, close to serX, whereas in one isolate the single copy was associated with serW. There was no correlation between Ter and the ability to produce Shiga toxin ST1 or ST2. The Ter MIC for most strains, containing either one or two copies, was 1,024 μg/ml, although for a few the MIC was intermediate, 64 to 128 μg/ml, which could be increased to 512 μg/ml by pregrowth of strains in subinhibitory concentrations of potassium tellurite. Reverse transcriptase PCR analysis confirmed that in most strains Ter was constitutive but that in the rest it was inducible and involved induction of terB and terC genes. Only the terB, -C, -D, and -E genes are required for Ter. The considerable degree of homology between the ter genes on IncH12 plasmid R478, which originated in Serratia marcescens, and pTE53, from an E. coli clinical isolate, suggests that the pathogenicity island was acquired from a plasmid. This work demonstrates diversity among E. coli O157:H7 isolates, at least as

  17. Conductivity studies of lithium zinc silicate glasses with varying ...

    Indian Academy of Sciences (India)

    WINTEC

    Values of activation energy derived from σd.c., ωh and τ are almost equal within the ... materials can be changed by varying the proportion of the .... The solid line is a guide to the eye. ... does not show a maximum as d.c. conductivity drops to a.

  18. Zinc in multiple sclerosis

    DEFF Research Database (Denmark)

    Bredholt, Mikkel; Fredriksen, Jette Lautrup

    2016-01-01

    In the last 35 years, zinc (Zn) has been examined for its potential role in the disease multiple sclerosis (MS). This review gives an overview of the possible role of Zn in the pathogenesis of MS as well as a meta-analysis of studies having measured Zn in serum or plasma in patients with MS...

  19. Zinc bioavailability in the chick

    International Nuclear Information System (INIS)

    Hempe, J.M.

    1987-01-01

    Methods for assessing zinc bioavailability were evaluated in the chick. A low-zinc chick diet was developed using rehydrated, spray-dried egg white autoclaved at 121 C for 30 min as the primary protein source. The relative bioavailability of zinc from soy flour and beef was determined by whole-body retention of extrinsic 65 Zn, and in slope ratio assays for growth rate and tissue zinc. Compared to zinc carbonate added to an egg white-based diet, all methods gave similar estimates of approximately 100% zinc bioavailability for beef but estimates for soy flour varied widely. The slope ratio assay for growth rate gave the best estimate of zinc bioavailability for soy flour. True absorption, as measured by percent isotope retention from extrinsically labeled soy flour, was 47%

  20. XPS and ion beam scattering studies of leaching in simulated waste glass containing uranium

    International Nuclear Information System (INIS)

    Karim, D.P.; Pronko, P.P.; Marcuso, T.L.M.; Lam, D.J.; Paulikas, A.P.

    1980-01-01

    Glass samples (consisting of 2 mole % UO 3 dissolved in a number of complex borosilicate simulated waste glasses including Battelle 76-68) were leached for varying times in distilled water at 75 0 C. The glass surfaces were examined before and after leaching using x-ray photoemission spectroscopy and back-scattered ion beam profiling. Leached samples showed enhanced surface layer concentrations of several elements including uranium, titanium, zinc, iron and rare earths. An experiment involving the leaching of two glasses in the same vessel showed that the uranium surface enhancement is probably not due to redeposition from solution

  1. Reactive ion etching of tellurite and chalcogenide waveguides using hydrogen, methane, and argon

    International Nuclear Information System (INIS)

    Vu, K. T.; Madden, S. J.

    2011-01-01

    The authors report in detail on the reactive plasma etching properties of tellurium and demonstrate a high quality etching process using hydrogen, methane, and argon. Very low loss planar ridge waveguides are demonstrated. Optical losses in tellurium dioxide waveguides below 0.1 dB/cm in most of the near infrared region of the electromagnetic spectrum and at 1550 nm have been achieved--the lowest ever reported by more than an order of magnitude and clearly suitable for planar integrated devices. The etch process is also shown to be suitable for chalcogenide glasses which may be of importance in applications such as phase change memory devices and nonlinear integrated optics.

  2. C-di-GMP regulates Pseudomonas aeruginosa stress response to tellurite during both planktonic and biofilm modes of growth

    DEFF Research Database (Denmark)

    Chua, Song Lin; Sivakumar, Krishnakumar; Rybtke, Morten Levin

    2015-01-01

    tellurite (TeO3(2-)) exposure induced the intracellular content of the secondary messenger cyclic di-GMP (c-di-GMP) of Pseudomonas aeruginosa. Two diguanylate cyclases (DGCs), SadC and SiaD, were responsible for the increased intracellular content of c-di-GMP. Enhanced c-di-GMP levels by TeO3(2-) further...... increased P. aeruginosa biofilm formation and resistance to TeO3(2-). P. aeruginosa ΔsadCΔsiaD and PAO1/p(lac)-yhjH mutants with low intracellular c-di-GMP content were more sensitive to TeO3(2-) exposure and had low relative fitness compared to the wild-type PAO1 planktonic and biofilm cultures exposed...... to TeO3(2-). Our study provided evidence that c-di-GMP level can play an important role in mediating stress response in microbial communities during both planktonic and biofilm modes of growth....

  3. lead glass brick

    CERN Multimedia

    When you look through the glass at a picture behind, the picture appears raised up because light is slowed down in the dense glass. It is this density (4.06 gcm-3) that makes lead glass attractive to physicists. The refractive index of the glass is 1.708 at 400nm (violet light), meaning that light travels in the glass at about 58% its normal speed. At CERN, the OPAL detector uses some 12000 blocks of glass like this to measure particle energies.

  4. Analysis of the luminescent spectra of Eu{sup 3+} in glasses

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Sha; Wei, Xiantao; Chen, Zhejia; Chen, Yonghu, E-mail: yhuchen@ustc.edu.cn; Yin, Min

    2013-11-15

    The spectroscopy properties of lanthanide ions in glasses differ remarkably from crystal and powder samples due to superposition of transitions from many ions with different local environments. Eu{sup 3+} ions were doped in lead–borosilicate and boro–tellurite glass samples to probe the structural information and to reveal their effects on the luminescent properties of lanthanide ions. Three emission peaks were observed for {sup 5}D{sub 0}→{sup 7}F{sub 0} transition, with peak energies linearly dependent on the excitation wavelengths, and correlation between the intensity ratio of {sup 5}D{sub 0}→{sup 7}F{sub 0} versus {sup 5}D{sub 0}→{sup 7}F{sub 2} and the width of {sup 7}F{sub 1} was observed. The former indicates that there are three subsets of Eu{sup 3+} sites in the samples, with {sup 7}F{sub 0} being pushed downwards by {sup 7}F{sub J} (J=2, 4, and 6) by crystal-field J-mixing, and the latter can be quantitatively modeled by the adaptation of the theoretical model of Wen et al. [Phys. Chem. Chem. Phys. 12, 9933 (2010)] to account for the corrections due to the inhomogeneous broadening of {sup 7}F{sub J} (J=0, and1) crystal-field levels. The methods explored here can be applied to study other glass hosts for luminescent materials. -- Highlights: • The quantitative analysis of Eu{sup 3+5}D{sub 0}→{sup 7}F{sub 0} emission spectra in glasses. • Improved data fitting with the modified CF splitting width calculation method. • Demonstration of the generality of the spectral analysis method in two glasses.

  5. Solubility effects in waste-glass/demineralized-water systems

    International Nuclear Information System (INIS)

    Fullam, H.T.

    1981-06-01

    Aqueous systems involving demineralized water and four glass compositions (including standins for actinides and fission products) at temperatures of up to 150 0 C were studied. Two methods were used to measure the solubility of glass components in demineralized water. One method involved approaching equilibrium from subsaturation, while the second method involved approaching equilibrium from supersaturation. The aqueous solutions were analyzed by induction-coupled plasma spectrometry (ICP). Uranium was determined using a Scintrex U-A3 uranium analyzer and zinc and cesium were determined by atomic absorption. The system that results when a waste glass is contacted with demineralized water is a complex one. The two methods used to determine the solubility limits gave very different results, with the supersaturation method yielding much higher solution concentrations than the subsaturation method for most of the elements present in the waste glasses. The results show that it is impossible to assign solubility limits to the various glass components without thoroughly describing the glass-water systems. This includes not only defining the glass type and solution temperature, but also the glass surface area-to-water volume ratio (S/V) of the system and the complete thermal history of the system. 21 figures, 22 tables

  6. Optoelectronic properties of expanding thermal plasma deposited textured zinc oxide : effect of aluminum doping

    NARCIS (Netherlands)

    Groenen, R.; Kieft, E.R.; Linden, J.L.; Sanden, van de M.C.M.

    2006-01-01

    Aluminum-doped zinc oxide films exhibiting a rough surface morphol. are deposited on glass substrates utilizing expanding thermal plasma. Spectroscopic ellipsometry is used to evaluate optical and electronic film properties. The presence of aluminum donors in doped films is confirmed by a shift in

  7. Effect of Thermal Cycling on Zinc Antimonide Thin Film Thermoelectric Characteristics

    DEFF Research Database (Denmark)

    Mirhosseini, M.; Rezania, A.; Rosendahl, L.

    2017-01-01

    In this study, performance and stability of zinc antimonide thin film thermoelectric sample is analyzed under transient thermal conditions. The thermoelectric materials are deposited on glass based substrate where the heat flow is parallel with the thermoelectric element length. The specimen...

  8. Autometallographic silver enhancement of zinc sulfide crystals created in cryostat sections from human brain biopsies

    DEFF Research Database (Denmark)

    Danscher, G; Juhl, S; Stoltenberg, M

    1997-01-01

    samples containing zinc-enriched (ZEN) cells, are frozen in liquid nitrogen or by CO2 gas immediately after removal. The tissue blocks are cut in a cryostat and the sections placed on glass slides. The slides are transferred to an H2S exposure chamber placed in a -15 C freezer. After 1-24 hr of gas...

  9. Zinc oxide films prepared by spray pyrolysis

    Directory of Open Access Journals (Sweden)

    Maciąg Andrzej

    2017-01-01

    Full Text Available In this work we developed and tested spray pyrolysis system for layers deposition. In the system we have used ultrasonic apparatus (nebulizator as a sprayer. A zinc nitrate aqueous solution has been used as a precursor solution. The idea of the method is the decomposition of nitrate on a hot substrate according to the reaction Zn(NO32 → ZnO +2 NO2 +1/2O2. The layers were grown on glass, (001Si and KCl substrates at the temperatures 300 – 500°C. The thickness of the obtained layers was in the range 50 – 500 nm, depending on the growth time and rate. The influence of substrate temperature on the morphology of the layers has been studied by SEM method. The energy gap of the layers was found to be the range of 3.26-3.3 eV from their absorption spectra.

  10. Interaction Between Yeasts and Zinc

    Science.gov (United States)

    Nicola, Raffaele De; Walker, Graeme

    Zinc is an essential trace element in biological systems. For example, it acts as a cellular membrane stabiliser, plays a critical role in gene expression and genome modification and activates nearly 300 enzymes, including alcohol dehydrogenase. The present chapter will be focused on the influence of zinc on cell physiology of industrial yeast strains of Saccharomyces cerevisiae, with special regard to the uptake and subsequent utilisation of this metal. Zinc uptake by yeast is metabolism-dependent, with most of the available zinc translocated very quickly into the vacuole. At cell division, zinc is distributed from mother to daughter cells and this effectively lowers the individual cellular zinc concentration, which may become zinc depleted at the onset of the fermentation. Zinc influences yeast fermentative performance and examples will be provided relating to brewing and wine fermentations. Industrial yeasts are subjected to several stresses that may impair fermentation performance. Such stresses may also impact on yeast cell zinc homeostasis. This chapter will discuss the practical implications for the correct management of zinc bioavailability for yeast-based biotechnologies aimed at improving yeast growth, viability, fermentation performance and resistance to environmental stresses

  11. Optical properties of Sm3+ -doped TeO2sbnd WO3sbnd GeO2 glasses for solid state lasers

    Science.gov (United States)

    Subrahmanyam, T.; Gopal, K. Rama; Suvarna, R. Padma; Jamalaiah, B. Chinna; Rao, Ch Srinivasa

    2018-03-01

    Sm3+ -doped oxyfluoride tellurite-tungsten (TWGSm) glasses were prepared by conventional melt quenching method. The optical properties were investigated through photoluminescence excitation, emission and luminescence decay analysis. The optical band gap energy was determined as ∼3.425 eV for 1.0 mol% of Sm3+ -doped TWGSm glass. Upon 404 nm excitation, the TWGSm glasses emit luminescence through 4G5/2 → 6H5/2 (563 nm), 4G5/2 → 6H7/2 (600 nm), 4G5/2 → 6H9/2 (645 nm) and 4G5/2 → 6H11/2 (705 nm) transitions. The Judd-Ofelt analysis was performed using absorption spectrum and obtained radiative parameters were used to estimate the laser characteristics of present glasses. The concentration of Sm3+ has been optimized as 1.0 mol% for efficient luminescence. The luminescence decay of 4G5/2 emission level was studied by monitoring the emission and excitation wavelengths at 600 and 404 nm, respectively. The experimental lifetime of 4G5/2 level was decrease with increase of Sm3+ concentration. The 1.0 mol% of Sm3+ -doped TWGSm glass could be the best choice for solid state visible lasers to emit orange luminescence.

  12. Does the oral zinc tolerance test measure zinc absorption

    Energy Technology Data Exchange (ETDEWEB)

    Valberg, L.S.; Flanagan, P.R.; Brennan, J.; Chamberlain, M.J.

    1985-01-01

    Increases in plasma zinc concentration were compared with radiozinc absorption after oral test doses. Ten healthy, fasting subjects were each given 385 mumol zinc chloride (25 mg Zn) labelled with 0.5 muCi /sup 65/ZnCl/sub 2/ and a non-absorbed marker, /sup 51/CrCl/sub 3/, dissolved in 100 ml of water; another 10 persons were given 354 mumol zinc chloride and 125 g of minced turkey containing 31 mumol zinc also labelled with /sup 65/Zn and /sup 51/Cr. Measurements were made of plasma zinc concentration at hourly intervals for 5 hours, radiozinc absorption by stool counting of unabsorbed radioactivity 12-36 hours later, and radiozinc retention by whole body counting at 7 days. The mean percentage of radiozinc absorbed and retained in the body from the two test meals was found to be identical (42%). In contrast the increased area under the plasma zinc curve up to 5 hours after the turkey meal, 28 +/- 9 mumol/L (mean +/- SD) was significantly less than that for zinc chloride alone, 47 +/- 15 mumol/L, p less than 0.005. Despite this difference, a good correlation was found between the area under the plasma zinc curve and /sup 65/Zn absorption in individual subjects after each meal. The discrepancy between the results of zinc absorption derived from the plasma zinc curve and /sup 65/Zn absorption for the liquid and solid test meals was most likely explained by binding of zinc to food and delayed gastric emptying of the solid meal. With a test meal of turkey meat at least this dampened the plasma appearance of zinc but did not affect its overall absorption.

  13. Does the oral zinc tolerance test measure zinc absorption

    International Nuclear Information System (INIS)

    Valberg, L.S.; Flanagan, P.R.; Brennan, J.; Chamberlain, M.J.

    1985-01-01

    Increases in plasma zinc concentration were compared with radiozinc absorption after oral test doses. Ten healthy, fasting subjects were each given 385 mumol zinc chloride (25 mg Zn) labelled with 0.5 muCi 65 ZnCl 2 and a non-absorbed marker, 51 CrCl 3 , dissolved in 100 ml of water; another 10 persons were given 354 mumol zinc chloride and 125 g of minced turkey containing 31 mumol zinc also labelled with 65 Zn and 51 Cr. Measurements were made of plasma zinc concentration at hourly intervals for 5 hours, radiozinc absorption by stool counting of unabsorbed radioactivity 12-36 hours later, and radiozinc retention by whole body counting at 7 days. The mean percentage of radiozinc absorbed and retained in the body from the two test meals was found to be identical (42%). In contrast the increased area under the plasma zinc curve up to 5 hours after the turkey meal, 28 +/- 9 mumol/L (mean +/- SD) was significantly less than that for zinc chloride alone, 47 +/- 15 mumol/L, p less than 0.005. Despite this difference, a good correlation was found between the area under the plasma zinc curve and 65 Zn absorption in individual subjects after each meal. The discrepancy between the results of zinc absorption derived from the plasma zinc curve and 65 Zn absorption for the liquid and solid test meals was most likely explained by binding of zinc to food and delayed gastric emptying of the solid meal. With a test meal of turkey meat at least this dampened the plasma appearance of zinc but did not affect its overall absorption

  14. Glass and nuclear wastes

    International Nuclear Information System (INIS)

    Sombret, C.

    1982-10-01

    Glass shows interesting technical and economical properties for long term storage of solidified radioactive wastes by vitrification or embedding. Glass composition, vitrification processes, stability under irradiation, thermal stability and aqueous corrosion are studied [fr

  15. Microstructuring of glasses

    CERN Document Server

    Hülsenberg, Dagmar; Bismarck, Alexander

    2008-01-01

    As microstructured glass becomes increasingly important for microsystems technology, the main application fields include micro-fluidic systems, micro-analysis systems, sensors, micro-actuators and implants. And, because glass has quite distinct properties from silicon, PMMA and metals, applications exist where only glass devices meet the requirements. The main advantages of glass derive from its amorphous nature, the precondition for its - theoretically - direction-independent geometric structurability. Microstructuring of Glasses deals with the amorphous state, various glass compositions and their properties, the interactions between glasses and the electromagnetic waves used to modify it. Also treated in detail are methods for influencing the geometrical microstructure of glasses by mechanical, chemical, thermal, optical, and electrical treatment, and the methods and equipment required to produce actual microdevices.

  16. Piezoelectric Zinc Oxide Based MEMS Acoustic Sensor

    Directory of Open Access Journals (Sweden)

    Aarti Arora

    2008-04-01

    Full Text Available An acoustic sensors exhibiting good sensitivity was fabricated using MEMS technology having piezoelectric zinc oxide as a dielectric between two plates of capacitor. Thin film zinc oxide has structural, piezoelectric and optical properties for surface acoustic wave (SAW and bulk acoustic wave (BAW devices. Oxygen effficient films are transparent and insulating having wide applications for sensors and transducers. A rf sputtered piezoelectric ZnO layer transforms the mechanical deflection of a thin etched silicon diaphragm into a piezoelectric charge. For 25-micron thin diaphragm Si was etched in tetramethylammonium hydroxide solution using bulk micromachining. This was followed by deposition of sandwiched structure composed of bottom aluminum electrode, sputtered 3 micron ZnO film and top aluminum electrode. A glass having 1 mm diameter hole was bonded on backside of device to compensate sound pressure in side the cavity. The measured value of central capacitance and dissipation factor of the fabricated MEMS acoustic sensor was found to be 82.4pF and 0.115 respectively, where as the value of ~176 pF was obtained for the rim capacitance with a dissipation factor of 0.138. The response of the acoustic sensors was reproducible for the devices prepared under similar processing conditions under different batches. The acoustic sensor was found to be working from 30Hz to 8KHz with a sensitivity of 139µV/Pa under varying acoustic pressure.

  17. Electrical mobility of silver ion in Ag2O-B2O3-P2O5-TeO2 glasses.

    Science.gov (United States)

    Sklepić, Kristina; Vorokhta, Maryna; Mošner, Petr; Koudelka, Ladislav; Moguš-Milanković, Andrea

    2014-10-16

    The effect of adding TeO(2) into (100 - x)[0.5Ag(2)O - 0.1B(2)O(3) - 0.4P(2)O(5)] - xTeO(2), with 0-80 mol % TeO(2) glass, on the structural changes and electrical properties has been investigated. DSC and thermodilatomery were used to study their thermal behavior, structure was studied by Raman spectroscopy, and electrical properties have been studied by impedance spectroscopy over a wide temperature and frequency range. The introduction of TeO(2) as a third glass former to the glass network causes the structural transformation from TeO(3) (tp) to TeO(4) (tbp) which contributes to the changes in conductivity. The glasses with low TeO(2) content show only a slow decrease in dc conductivity with addition of TeO(2) due to the increase of the number of nonbridging oxygens, which increases the mobility of Ag(+) ions. The steep decrease in conductivity for glasses containing more than 40 mol % TeO(2) is a result of decrease of the Ag(2)O content and stronger cross-linkage in glass network through the formation of more Te-(eq)O(ax)-Te bonds in TeO(4) tbp units. The glasses obey ac conductivity scaling with respect to temperature, implying that the dynamic process is not temperature dependent. On the other hand, the scaling of the spectra for different glass compositions showed the deviations from the Summerfield scaling because of the local structural disorder which occurs as a result of the structural modifications in the tellurite glass network.

  18. Measurement of optical glasses

    International Nuclear Information System (INIS)

    Nicolau-Rebigan, S.

    1978-11-01

    The possibilities of measurement of the optical glasses parameters needed in building optical devices especially in lasers devices are presented. In the first chapter the general features of the main optical glasses as well as the modalities of obtaining them are given. Chapter two defines the optical glass parameters, and the third chapter describes the measuring methods of the optical glass parameters. Finally, the conclusions which point out the utilization of this paper are presented. (author)

  19. Photovoltaic Properties of Co-doped ZnO Thin Film on Glass Substrate

    International Nuclear Information System (INIS)

    Sabia Aye; Zin Ma Ma; May Nwe Oo; Than Than Win; Yin Maung Maung; Ko Ko Kyaw Soe

    2011-12-01

    Cobalt (Co) 0.4 mol doped zinc oxide (ZnO) fine powder was prepared by solid state mixed oxide route. Phase formation and crystal structure of Co-doped ZnO (CZO) powder were examined by X-ray diffraction (XRD). Scanning Electron Microscopy (SEM) was used to observe the micro structure of Co doped ZnO powder. Energy Dispersive X-ray Fluorescent (EDXRF) technique gave the elemental content of cobalt and zinc. Co-doped ZnO film was formed on glass substrate by spin coating technique. Photovoltaic properties of CZO/glass cell were measured.

  20. Mechanically reinforced glass beams

    DEFF Research Database (Denmark)

    Nielsen, Jens Henrik; Olesen, John Forbes

    2007-01-01

    laminated float glass beam is constructed and tested in four-point bending. The beam consist of 4 layers of glass laminated together with a slack steel band glued onto the bottom face of the beam. The glass parts of the tested beams are \\SI{1700}{mm} long and \\SI{100}{mm} high, and the total width of one...

  1. Structural and luminescence studies of Eu3+: TeO2sbnd B2O3sbnd AOsbnd AF2 (A = Pb, Ba, Zn, Cd, Sr) glasses

    Science.gov (United States)

    Selvi, S.; Marimuthu, K.; Muralidharan, G.

    2017-09-01

    Eu3+ doped oxyfluoro boro-tellurite (TBXFE) with molar composition 29 TeO2sbnd 30B2O3sbnd 20AOsbnd 20AF2sbnd 1Eu2O3 (where A = Pb, Ba, Zn, Cd, Sr) glasses were prepared and investigated by XRD, FTIR, UV-Vis-NIR, luminescence and decay measurements. XRD patterns confirm the glassy nature of the prepared glasses. The influence of metal ions on the structure of boro-tellurite glasses were investigated through FTIR spectra. The intra band (4f-4f) transitions of Eu3+ ions are discussed through UV-Vis-NIR absorption spectra. The covalent nature around the Eu3+ ions with ligands are discussed using the bonding parameter (δ) and nephelauxetic ratio (β). The fundamental absorption edge, direct, indirect band gap, Urbach energy and band tailing parameters are reported. A bright red emission at 616 nm corresponding to the 5D0 → 7F2 transition of Eu3+ ions could be observed in the title glasses. Judd-Ofelt parameters were estimated from the emission spectra of Eu3+ ions. The dependence of these parameters on the composition of the glass is discussed. Judd-Ofelt parameters were used to derive the radiative parameters such as transition probabilities (A, s-1), branching ratios (βR), radiative lifetime (τrad) and stimulated emission cross-section (σPE) for the 5D0 → 7FJ (J = 0, 1, 2, 3 and 4) transitions. The luminescence intensity ratio (LIR) of 5D0 → 7F2/5D0 → 7F1 transitions was estimated to analyze the local site symmetry around the Eu3+ ions in the present glasses. The chromaticity coordinates and colour purity were calculated from the emission spectra and analyzed with Commission International de I'Eclairage (CIE) 1931 diagram. The experimental lifetime of 5D0 level could be fitted to a single exponential indicating the absence of energy transfer between the Eu3+ ions in the present glasses.

  2. Caracterización estructural de vidrios con altos contenidos de óxidos de hierro obtenidos a partir de un residuo de la hidrometalurgia del zinc

    OpenAIRE

    Romero, M.; Rincón, J. María; Mûsik, S.; Kozhukharov, W.

    1997-01-01

    It has been carried out the structural characterization of high oxide content glasses obtained by melting of a goethite industrial waste from the zinc hydrometallurgy with other raw materials as dolomite and glass cullet. The structural characterization has been carried out by X-Ray Diffraction (XRD), X-Ray Diffraction by Amorphous Dispersion (RDF) and Mossbauer spectroscopy. It has been determined the interatomic distance, the oxidation state and the coordination of iron atoms in these glass...

  3. Effect of TeO2 on the elastic moduli of sodium borate glasses

    International Nuclear Information System (INIS)

    Saddeek, Y.B.; Abd El Latif, Lamia

    2004-01-01

    Sodium borate glass containing tellurite as Te x Na 2-2x B 4-4x O 7-5x with x=0, 0.05, 0.15, 0.25 and 0.35 have been prepared by rapid quenching. Ultrasonic velocity (both longitudinal and shear) measurements have been made using a transducer operated at the fundamental frequency of 4 MHz at room temperature. The density was measured by the conventional Archimedes method. The elastic moduli, the Debye temperature, Poisson's ratio, and the parameters derived from the Makishima-Mackenzie model and the bond compression model have been obtained as a function of TeO 2 content. The monotonic decrease in the velocities and the elastic moduli, and the increase in the ring diameter and the ratio K bc /K e as a function of TeO 2 modifier content reveals the loose packing structure, which is attributed to the increase in the molar volume and the reduction in the vibrations of the borate lattice. The observed results confirm that the addition of TeO 2 changes the rigid character of Na 2 B 4 O 7 to a matrix of ionic behaviour bonds (NBOs). This is due to the creation of more and more discontinuities and defects in the glasses, thus breaking down the borax structure

  4. Chloroquine is a zinc ionophore.

    Directory of Open Access Journals (Sweden)

    Jing Xue

    Full Text Available Chloroquine is an established antimalarial agent that has been recently tested in clinical trials for its anticancer activity. The favorable effect of chloroquine appears to be due to its ability to sensitize cancerous cells to chemotherapy, radiation therapy, and induce apoptosis. The present study investigated the interaction of zinc ions with chloroquine in a human ovarian cancer cell line (A2780. Chloroquine enhanced zinc uptake by A2780 cells in a concentration-dependent manner, as assayed using a fluorescent zinc probe. This enhancement was attenuated by TPEN, a high affinity metal-binding compound, indicating the specificity of the zinc uptake. Furthermore, addition of copper or iron ions had no effect on chloroquine-induced zinc uptake. Fluorescent microscopic examination of intracellular zinc distribution demonstrated that free zinc ions are more concentrated in the lysosomes after addition of chloroquine, which is consistent with previous reports showing that chloroquine inhibits lysosome function. The combination of chloroquine with zinc enhanced chloroquine's cytotoxicity and induced apoptosis in A2780 cells. Thus chloroquine is a zinc ionophore, a property that may contribute to chloroquine's anticancer activity.

  5. Innovative uses for zinc in dermatology.

    Science.gov (United States)

    Bae, Yoon Soo; Hill, Nikki D; Bibi, Yuval; Dreiher, Jacob; Cohen, Arnon D

    2010-07-01

    Severe zinc deficiency states, such as acrodermatitis enteropathica, are associated with a variety of skin manifestations, such as perioral, acral, and perineal dermatitis. These syndromes can be reversed with systemic zinc repletion. In addition to skin pathologies that are clearly zinc-dependent, many dermatologic conditions (eg, dandruff, acne, and diaper rash) have been associated and treated with zinc. Success rates for treatment with zinc vary greatly depending on the disease, mode of administration, and precise zinc preparation used. With the exception of systemic zinc deficiency states, there is little evidence that convincingly demonstrates the efficacy of zinc as a reliable first-line treatment for most dermatologic conditions. However, zinc may be considered as an adjunctive treatment modality. Further research is needed to establish the indications for zinc treatment in dermatology, optimal mode of zinc delivery, and best type of zinc compound to be used. Copyright 2010 Elsevier Inc. All rights reserved.

  6. Fluoride glass fiber optics

    CERN Document Server

    Aggarwal, Ishwar D

    1991-01-01

    Fluoride Glass Fiber Optics reviews the fundamental aspects of fluoride glasses. This book is divided into nine chapters. Chapter 1 discusses the wide range of fluoride glasses with an emphasis on fluorozirconate-based compositions. The structure of simple fluoride systems, such as BaF2 binary glass is elaborated in Chapter 2. The third chapter covers the intrinsic transparency of fluoride glasses from the UV to the IR, with particular emphasis on the multiphonon edge and electronic edge. The next three chapters are devoted to ultra-low loss optical fibers, reviewing methods for purifying and

  7. Multiple Glass Ceilings

    OpenAIRE

    Russo, Giovanni; Hassink, Wolter

    2011-01-01

    Both vertical (between job levels) and horizontal (within job levels) mobility can be sources of wage growth. We find that the glass ceiling operates at both margins. The unexplained part of the wage gap grows across job levels (glass ceiling at the vertical margin) and across the deciles of the intra-job-level wage distribution (glass ceiling at the horizontal margin). This implies that women face many glass ceilings, one for each job level above the second, and that the glass ceiling is a p...

  8. Homogeneity of Inorganic Glasses

    DEFF Research Database (Denmark)

    Jensen, Martin; Zhang, L.; Keding, Ralf

    2011-01-01

    Homogeneity of glasses is a key factor determining their physical and chemical properties and overall quality. However, quantification of the homogeneity of a variety of glasses is still a challenge for glass scientists and technologists. Here, we show a simple approach by which the homogeneity...... of different glass products can be quantified and ranked. This approach is based on determination of both the optical intensity and dimension of the striations in glasses. These two characteristic values areobtained using the image processing method established recently. The logarithmic ratio between...

  9. Reactive radio frequency sputtering deposition and characterization of zinc nitride and oxynitride thin films

    International Nuclear Information System (INIS)

    Jiang, Nanke; Georgiev, Daniel G.; Wen, Ting; Jayatissa, Ahalapitiya H.

    2012-01-01

    Zinc nitride films were deposited on glass or silicon substrates by reactive magnetron radio frequency sputtering of zinc in either N 2 –Ar or N 2 –Ar–O 2 ambient. The effects of varying the nitrogen contents and the substrate temperature were investigated. X-ray diffraction data showed that the as-deposited films contain the zinc nitride cubic crystalline phase with a preferred orientation, and Raman scattering measurements revealed Zn-N related modes. According to energy-dispersive X-ray spectroscopy analysis, the as-deposited films were nitrogen-rich and contained only a small fraction of oxygen. Hall-effect measurements showed that p-type zinc nitride with carrier concentration of ∼ 10 19 cm −3 , mobility of ∼ 10 1 cm 2 /Vs, resistivity of ∼ 10 −2 Ω ∗ cm, was obtained. The photon energy dependence of optical transmittance suggested that the material has an indirect bandgap.

  10. Selective masking and demasking for the stepwise complexometric determination of aluminium, lead and zinc from the same solution

    OpenAIRE

    Kayal, Nijhuma; Singh, Nahar

    2008-01-01

    Abstract Background A complexometric method based on selective masking and de-masking has been developed for the rapid determination of aluminium, lead and zinc from the same solution in glass and glass frit samples. The determination is carried out using potassium cyanide to mask zinc, and excess disodium salt of EDTA to mask lead and aluminium. The excess EDTA was titrated with standard Mn(II)SO4 solution using Erichrome Black-T as the indicator. Subsequently selective de-masking agents – t...

  11. Leaching of glass

    International Nuclear Information System (INIS)

    Hench, L.L.

    1977-01-01

    Understanding surface compositional profiles of glasses over a range of 0-2000 A with a variety of analytical instruments shows that five general types of glass surfaces exist. The surface character of a glass article depends upon bulk composition and environmental history during which surface dealkalization, film formation, and network dissolution can occur. Environmental-surface interactions generally result in complex compositional profiles of all the constituents in a glass. Durable glasses almost always develop a stable surface film which has a higher concentration of network formers than the bulk composition. Compositional effects that are used to improve glass durability usually improve the stability of the surface films. Durability tests or service conditions that lead to film destruction are especially severe for the most silicate glasses. 43 references

  12. Evaluation of TeO2 content on the optical and spectroscopic properties of Yb3 +-doped calcium borotellurite glasses

    Science.gov (United States)

    Lima, A. M. O.; Gomes, J. F.; Hegeto, F. L.; Medina, A. N.; Steimacher, A.; Barboza, M. J.

    2018-03-01

    This paper reports the synthesis and the characterization of Yb3 +-doped calcium borotellurite (CaBTeX) glasses with composition 10CaF2-(29.5 - 0.4x)CaO-(60 - 0.6x)B2O3-xTeO2-0.5Yb2O3 (x = 10, 16, 22, 31 and 54 mol%). The results of XRD confirm the amorphous character of all the samples. The density, molar volume, refractive index and electronic polarizability values show an increase with TeO2 content. Otherwise, the optical band gap energy shows a decrease with the increase of TeO2 content. The replacement of CaO and B2O3 by TeO2 changes the glass structure, which decreases the excited Yb3 +/cm3 and, consequently, the luminescence intensity. The temperature dependence of luminescence was studied for all the samples up to 420 K. The fluorescence lifetime does not change significantly due to TeO2 addition. In addition, absorption and emission cross section were calculated and present high values as compared to other tellurite and phosphate glasses.

  13. Protein-protein association and cellular localization of four essential gene products encoded by tellurite resistance-conferring cluster "ter" from pathogenic Escherichia coli.

    Science.gov (United States)

    Valkovicova, Lenka; Vavrova, Silvia Minarikova; Mravec, Jozef; Grones, Jozef; Turna, Jan

    2013-12-01

    Gene cluster "ter" conferring high tellurite resistance has been identified in various pathogenic bacteria including Escherichia coli O157:H7. However, the precise mechanism as well as the molecular function of the respective gene products is unclear. Here we describe protein-protein association and localization analyses of four essential Ter proteins encoded by minimal resistance-conferring fragment (terBCDE) by means of recombinant expression. By using a two-plasmid complementation system we show that the overproduced single Ter proteins are not able to mediate tellurite resistance, but all Ter members play an irreplaceable role within the cluster. We identified several types of homotypic and heterotypic protein-protein associations among the Ter proteins by in vitro and in vivo pull-down assays and determined their cellular localization by cytosol/membrane fractionation. Our results strongly suggest that Ter proteins function involves their mutual association, which probably happens at the interface of the inner plasma membrane and the cytosol.

  14. Transformation of zinc hydroxide chloride monohydrate to crystalline zinc oxide.

    Science.gov (United States)

    Moezzi, Amir; Cortie, Michael; McDonagh, Andrew

    2016-04-25

    Thermal decomposition of layered zinc hydroxide double salts provides an interesting alternative synthesis for particles of zinc oxide. Here, we examine the sequence of changes occurring as zinc hydroxide chloride monohydrate (Zn5(OH)8Cl2·H2O) is converted to crystalline ZnO by thermal decomposition. The specific surface area of the resultant ZnO measured by BET was 1.3 m(2) g(-1). A complicating and important factor in this process is that the thermal decomposition of zinc hydroxide chloride is also accompanied by the formation of volatile zinc-containing species under certain conditions. We show that this volatile compound is anhydrous ZnCl2 and its formation is moisture dependent. Therefore, control of atmospheric moisture is an important consideration that affects the overall efficiency of ZnO production by this process.

  15. Uptake and partitioning of zinc in Lemnaceae.

    Science.gov (United States)

    Lahive, Elma; O'Callaghan, Michael J A; Jansen, Marcel A K; O'Halloran, John

    2011-11-01

    Macrophytes provide food and shelter for aquatic invertebrates and fish, while also acting as reservoirs for nutrients and trace elements. Zinc accumulation has been reported for various Lemnaceae species. However, comparative accumulation across species and the link between zinc accumulation and toxicity are poorly understood. Morphological distribution and cellular storage, in either bound or soluble form, are important for zinc tolerance. This study shows differences in the uptake and accumulation of zinc by three duckweed species. Landoltia punctata and Lemna minor generally accumulated more zinc than Lemna gibba. L. minor, but not L. gibba or L. punctata, accumulated greater concentrations of zinc in roots compared to fronds when exposed to high levels of zinc. The proportion of zinc stored in the bound form relative to the soluble-form was higher in L. minor. L. punctata accumulated greater concentrations of zinc in fronds compared to roots and increased the proportion of zinc it stored in the soluble form, when exposed to high zinc levels. L. gibba is the only species that significantly accumulated zinc at low concentrations, and was zinc-sensitive. Overall, internal zinc concentrations showed no consistent correlation with toxic effect. We conclude that relationships between zinc toxicity and uptake and accumulation are species specific reflecting, among others, zinc distribution and storage. Differences in zinc distribution and storage are also likely to have implications for zinc bioavailability and trophic mobility.

  16. Inhibitory zinc-enriched terminals in mouse spinal cord

    DEFF Research Database (Denmark)

    Danscher, G; Jo, S M; Varea, E

    2001-01-01

    The ultrastructural localization of zinc transporter-3, glutamate decarboxylase and zinc ions in zinc-enriched terminals in the mouse spinal cord was studied by zinc transporter-3 and glutamate decarboxylase immunohistochemistry and zinc selenium autometallography, respectively.The distribution...

  17. Zinc: an essential oligoelement

    OpenAIRE

    Rubio, C.; González Weller, D.; Martín-Izquierdo, R. E.; Revert, C.; Rodríguez, I.; Hardisson, A.

    2007-01-01

    En este artículo se hace una revisión exhaustiva del zinc, elemento metálico esencial para el funcionamiento del organismo. Repasamos y reflejamos aspectos relacionados con la farmacocinética, con las fuentes dietéticas más importantes, así como las IDR (Ingestas Dietéticas Recomendadas) del mismo. También se hace mención a los signos y síntomas relacionados tanto con una ingesta deficiente, como con posibles efectos tóxicos, derivados de ingestas excesivas.This article comprehensively review...

  18. Cadmium and zinc

    International Nuclear Information System (INIS)

    Safaya, N.M.; McLean, J.E.; Halverson, G.A.

    1987-01-01

    Cadmium and zinc are naturally occurring trace metals that are often considered together because of their close geochemical association and similarities in chemical reactivity. The loss of two electrons from an atom of Cd or Zn imparts to each an electron configuration with completely filled d orbitals; this results in a highly stable 2/sup +/ oxidation state. But Cd and Zn differ greatly in their significance to biological systems. Whereas Zn is an essential nutrient for plants, animals, and humans, Cd is best known for its toxicity to plants and as a causative agent of several disease syndromes in animals and humans

  19. Study of broadband near-infrared emission in Tm3+-Er3+ codoped TeO2-WO3-PbO glasses.

    Science.gov (United States)

    Balda, R; Fernández, J; Fernández-Navarro, J M

    2009-05-25

    In this work, we report the near-infrared emission properties of Tm(3+)-Er(3+) codoped tellurite TeO(2)-WO(3)-PbO glasses under 794 nm excitation. A broad emission from 1350 to 1750 nm corresponding to the Tm(3+) and Er(3+) emissions is observed. The full width at half-maximum of this broadband increases with increasing [Tm]/[Er] concentration ratio up to a value of ~ 160 nm. The energy transfer between Tm(3+) and Er(3+) ions is evidenced by both the temporal behavior of the near-infrared luminescence and the effect of Tm3+ codoping on the visible upconversion of Er(3+) ions.

  20. Crystallization and chemical durability of glasses in the system Bi2O3-SiO2

    International Nuclear Information System (INIS)

    Fredericci, C.

    2011-01-01

    The crystallization of the Bi 2 O 3 -SiO 2 -TiO 2 -Al 2 O 3 -Na 2 O-K 2 O and Bi 2 O 3 -SiO 2 -ZnO-Al 2 O 3 -B 2 O 3 -Na 2 O glasses was studied using glass samples prepared by traditional melt-quench method. Differential thermal analysis (DTA) curves suggested that surface crystallization played a major role in the crystallization of the glass samples. X-ray diffraction (XRD) analysis revealed the crystallization of bismuth silicate for both glasses and bismuth silicate and zinc silicate for the glass containing ZnO. Through scanning electron microscopy (MEV) and energy dispersive spectroscopy (EDS), it was possible to observe that the crystals of zinc silicate (Zn 2 SiO 4 ) were readily attacked by hot 0,1 N sulfuric acid, whereas bismuth silicate crystals were more resistant to acidic attack etching. (author)

  1. Zinc in Infection and Inflammation

    Directory of Open Access Journals (Sweden)

    Nour Zahi Gammoh

    2017-06-01

    Full Text Available Micronutrient homeostasis is a key factor in maintaining a healthy immune system. Zinc is an essential micronutrient that is involved in the regulation of the innate and adaptive immune responses. The main cause of zinc deficiency is malnutrition. Zinc deficiency leads to cell-mediated immune dysfunctions among other manifestations. Consequently, such dysfunctions lead to a worse outcome in the response towards bacterial infection and sepsis. For instance, zinc is an essential component of the pathogen-eliminating signal transduction pathways leading to neutrophil extracellular traps (NET formation, as well as inducing cell-mediated immunity over humoral immunity by regulating specific factors of differentiation. Additionally, zinc deficiency plays a role in inflammation, mainly elevating inflammatory response as well as damage to host tissue. Zinc is involved in the modulation of the proinflammatory response by targeting Nuclear Factor Kappa B (NF-κB, a transcription factor that is the master regulator of proinflammatory responses. It is also involved in controlling oxidative stress and regulating inflammatory cytokines. Zinc plays an intricate function during an immune response and its homeostasis is critical for sustaining proper immune function. This review will summarize the latest findings concerning the role of this micronutrient during the course of infections and inflammatory response and how the immune system modulates zinc depending on different stimuli.

  2. Zinc in Infection and Inflammation.

    Science.gov (United States)

    Gammoh, Nour Zahi; Rink, Lothar

    2017-06-17

    Micronutrient homeostasis is a key factor in maintaining a healthy immune system. Zinc is an essential micronutrient that is involved in the regulation of the innate and adaptive immune responses. The main cause of zinc deficiency is malnutrition. Zinc deficiency leads to cell-mediated immune dysfunctions among other manifestations. Consequently, such dysfunctions lead to a worse outcome in the response towards bacterial infection and sepsis. For instance, zinc is an essential component of the pathogen-eliminating signal transduction pathways leading to neutrophil extracellular traps (NET) formation, as well as inducing cell-mediated immunity over humoral immunity by regulating specific factors of differentiation. Additionally, zinc deficiency plays a role in inflammation, mainly elevating inflammatory response as well as damage to host tissue. Zinc is involved in the modulation of the proinflammatory response by targeting Nuclear Factor Kappa B (NF-κB), a transcription factor that is the master regulator of proinflammatory responses. It is also involved in controlling oxidative stress and regulating inflammatory cytokines. Zinc plays an intricate function during an immune response and its homeostasis is critical for sustaining proper immune function. This review will summarize the latest findings concerning the role of this micronutrient during the course of infections and inflammatory response and how the immune system modulates zinc depending on different stimuli.

  3. Zinc as a Gatekeeper of Immune Function

    Directory of Open Access Journals (Sweden)

    Inga Wessels

    2017-11-01

    Full Text Available After the discovery of zinc deficiency in the 1960s, it soon became clear that zinc is essential for the function of the immune system. Zinc ions are involved in regulating intracellular signaling pathways in innate and adaptive immune cells. Zinc homeostasis is largely controlled via the expression and action of zinc “importers” (ZIP 1–14, zinc “exporters” (ZnT 1–10, and zinc-binding proteins. Anti-inflammatory and anti-oxidant properties of zinc have long been documented, however, underlying mechanisms are still not entirely clear. Here, we report molecular mechanisms underlying the development of a pro-inflammatory phenotype during zinc deficiency. Furthermore, we describe links between altered zinc homeostasis and disease development. Consequently, the benefits of zinc supplementation for a malfunctioning immune system become clear. This article will focus on underlying mechanisms responsible for the regulation of cellular signaling by alterations in zinc homeostasis. Effects of fast zinc flux, intermediate “zinc waves”, and late homeostatic zinc signals will be discriminated. Description of zinc homeostasis-related effects on the activation of key signaling molecules, as well as on epigenetic modifications, are included to emphasize the role of zinc as a gatekeeper of immune function.

  4. Electrical conduction of glasses in the system Fe2O3-Sb2O3-TeO2; Fe2O3-Sb2O3-TeO2 kei garasu no denki dendo

    Energy Technology Data Exchange (ETDEWEB)

    Qiu, Honghua; Mori, H; Sakata, H; Hirayama, T [Tokai Univ., Tokyo (Japan). Faculty of Engineering

    1995-01-01

    In this study, taking into consideration that TeO2 is a component of the glass network and Sb2O3 shows the redox effect in the glasses reducing its possibility of transformation of Sb{sup 3+} to Sb{sup 5+} as well as glass basicity, highly conductive tellurite based glasses have been prepared by the press-quenching method selecting the Fe2O3-Sb2O3-TeO2 system, and the electroconductive mechanism of the glasses has been examined by measuring its D.C. conductivity {sigma}. Part of the obtained information is as follows; the glass formation range of the Fe2O3-Sb2O3-TeO2 system has been 0 {le} Fe2O3 {le} 15mol%, 0 {le} Sb2O3 {le} 18mol% and 78 {le} TeO2 {le} 100mol% and about 15mol% of the additional amount of Fe2O3 has been the limit of glass formation. As the amount of Fe2O3 has increased, C{sub Fe} has also increased and with this, the linear electroconductivity of the glasses has increased from 1.86 {times} 10{sup -7}S{center_dot}cm{sup -1} to 1.62 {times} 10{sup -6}S{center_dot}cm{sup -1} and the glasses have been confirmed as the n-type semiconductor. The factor determining {sigma} of the glasses has been C{sub Fe} which has increased as the amount of Fe2O3 has increased. 34 refs., 8 figs., 2 tabs.

  5. Fractography of glass

    CERN Document Server

    Tressler, Richard

    1994-01-01

    As the first major reference on glass fractography, contributors to this volume offer a comprehensive account of the fracture of glass as well as various fracture surface topography Contributors discuss optical fibers, glass containers, and flatglass fractography In addition, papers explore fracture origins; the growth of the original flaws of defects; and macroscopic fracture patterns from which fracture patterns evolve This volume is complete with photographs and schematics

  6. Diamond turning of glass

    Energy Technology Data Exchange (ETDEWEB)

    Blackley, W.S.; Scattergood, R.O.

    1988-12-01

    A new research initiative will be undertaken to investigate the critical cutting depth concepts for single point diamond turning of brittle, amorphous materials. Inorganic glasses and a brittle, thermoset polymer (organic glass) are the principal candidate materials. Interrupted cutting tests similar to those done in earlier research are Ge and Si crystals will be made to obtain critical depth values as a function of machining parameters. The results will provide systematic data with which to assess machining performance on glasses and amorphous materials

  7. Glass to contain wastes

    International Nuclear Information System (INIS)

    Moncouyoux, M.; Jacquet-Francillon, M.

    1994-01-01

    Here are the tables and figures presented during the conference on the glass to confine high level radioactive wastes: definition, fabrication, storage and disposal. The composition of glasses are detailed, their properties and the vitrification proceeding. The behaviour of these glasses in front of water, irradiation and heat are shown. The characteristics of parcels are given according to the radiation protection rule, ALARA principle, the concept of multi-barriers and the geological stability

  8. Glass microspheres for brachytherapy

    International Nuclear Information System (INIS)

    Prado, Miguel O.; Prastalo, Simon; Blaumann, Herman; Longhino, Juan M.; Repetto Llamazares, A.H.V.

    2007-01-01

    We developed the capacity to produce glass microspheres containing in their structure one or more radioactive isotopes useful for brachytherapy. We studied the various facts related with their production: (Rare earth) alumino silicate glass making, glass characterization, microspheres production, nuclear activation through (n,γ) nuclear reactions, mechanical characterization before and after irradiation. Corrosion tests in simulated human plasma and mechanical properties characterization were done before and after irradiation. (author) [es

  9. Silicate glasses. Chapter 1

    International Nuclear Information System (INIS)

    Lutze, W.

    1988-01-01

    This chapter is a survey of world-wide research and development efforts in nuclear waste glasses and its production technology. The principal glasses considered are silicate glasses which contain boron, i.e. borosilicate glass. A historical overview of waste form development programs in nine countries is followed by a summary of the design criteria for borosilicate glass compositions glass compositions. In the sections on glass properties the waste form is characterized in terms of potential alterations under the influence of heat, thermal gradients, radiation, aqueous solutions and combinations thereof. The topics are phase transformations, mechanical properties, radiation effects and chemical durability. The results from studies of volcanic glasses, as natural analogues for borosilicate nuclear waste glasses in order to verify predictions obtained from short-term tests in the laboratory, have been compiled in a special section on natural analogues. A special section on advanced vitrification techniques summarizes the various actual and potential processing schemes and describes the facilities. The literature has been considered until 1985. (author). 430 refs.; 68 figs.; 29 tabs

  10. Glass and vitrification

    International Nuclear Information System (INIS)

    Barton, J.L.; Vacher, R.; Moncouyoux, J.P.; Vernaz, E.

    1997-01-01

    Most glasses used as materials are oxides glasses that are produced by a quick quench of a liquid. Glasses are characterized by the absence of periodicity in the atomic arrangements, they do not have symmetries and do not present order over a long distance. This series of 4 short articles present: 1) the properties of glass and its industrial story, 2) the glass structure, 3) a forty years long story of glass as dies used to confine wastes and 4) the methodology used to study the behaviour of glass over very long periods of time. This methodology is based on 5 steps: 1) define and specify the material to study (the prediction of long term alteration of a material is nonsense unless you know well its initial properties), 2) identify all the alteration processes that are likely to happen, determine their kinetics and the influence of environmental parameters, 3) develop mathematical models in order to simulate long-term behaviour of glasses, 4) determine the release rates of the radionuclides confined in the glass, and 5) validate data and models, it is not possible to expect a complete validation of a model that will be extrapolated over tens of thousands of years, nevertheless some ways of validation can lead to a satisfactory level of confidence taking into account reasonable uncertainties. (A.C.)

  11. Cathodic hydrogen charging of zinc

    International Nuclear Information System (INIS)

    Panagopoulos, C.N.; Georgiou, E.P.; Chaliampalias, D.

    2014-01-01

    Highlights: •Incorporation of hydrogen into zinc and formation of zinc hydrides. •Investigation of surface residual stresses due to hydrogen diffusion. •Effect of hydrogen diffusion and hydride formation on mechanical properties of Zn. •Hydrogen embrittlement phenomena in zinc. -- Abstract: The effect of cathodic hydrogen charging on the structural and mechanical characteristics of zinc was investigated. Hardening of the surface layers of zinc, due to hydrogen incorporation and possible formation of ZnH 2 , was observed. In addition, the residual stresses brought about by the incorporation of hydrogen atoms into the metallic matrix, were calculated by analyzing the obtained X-ray diffraction patterns. Tensile testing of the as-received and hydrogen charged specimens revealed that the ductility of zinc decreased significantly with increasing hydrogen charging time, for a constant value of charging current density, and with increasing charging current density, for a constant value of charging time. However, the ultimate tensile strength of this material was slightly affected by the hydrogen charging procedure. The cathodically charged zinc exhibited brittle transgranular fracture at the surface layers and ductile intergranular fracture at the deeper layers of the material

  12. Electrodeposition of zinc--nickel alloys coatings

    Energy Technology Data Exchange (ETDEWEB)

    Dini, J W; Johnson, H R

    1977-10-01

    One possible substitute for cadmium in some applications is a zinc--nickel alloy deposit. Previous work by others showed that electrodeposited zinc--nickel coatings containing about 85 percent zinc and 15 percent nickel provided noticeably better corrosion resistance than pure zinc. Present work which supports this finding also shows that the corrosion resistance of the alloy deposit compares favorably with cadmium.

  13. Characterization of glass and glass ceramic nuclear waste forms

    International Nuclear Information System (INIS)

    Lutze, W.; Borchardt, J.; De, A.K.

    1979-01-01

    Characteristics of solidified nuclear waste forms, glass and glass ceramic compositions and the properties (composition, thermal stability, crystallization, phase behavior, chemical stability, mechanical stability, and radiation effects) of glasses and glass ceramics are discussed. The preparation of glass ceramics may be an optional step for proposed vitrification plants if tailored glasses are used. Glass ceramics exhibit some improved properties with respect to glasses. The overall leach resistance is similar to that of glasses. An increased leach resistance may become effective for single radionuclides being hosted in highly insoluble crystal phases mainly when higher melting temperatures are applicable in order to get more leach resistant residual glass phases. The development of glass ceramic is going on. The technological feasibility is still to be demonstrated. The potential gain of stability when using glass ceramics qualifies the material as an alternative nuclear waste form

  14. Aluminum-doped zinc oxide films as transparent conductive electrode for organic light-emitting devices

    International Nuclear Information System (INIS)

    Jiang, X.; Wong, F.L.; Fung, M.K.; Lee, S.T.

    2003-01-01

    Highly transparent conductive, aluminum-doped zinc oxide (ZnO:Al) films were deposited on glass substrates by midfrequency magnetron sputtering of metallic aluminum-doped zinc target. ZnO:Al films with surface work functions between 3.7 and 4.4 eV were obtained by varying the sputtering conditions. Organic light-emitting diodes (OLEDs) were fabricated on these ZnO:Al films. A current efficiency of higher than 3.7 cd/A, was achieved. For comparison, 3.9 cd/A was achieved by the reference OLEDs fabricated on commercial indium-tin-oxide substrates

  15. Zinc and cadmium monosalicylates

    International Nuclear Information System (INIS)

    Kharitonov, Yu.Ya.; Tujebakhova, Z.K.

    1984-01-01

    Zinc and cadmium monosalicylates of the composition MSal, where M-Zn or Cd, Sal - twice deprotonated residue of salicylic acid O-HOC 6 H 4 COOH (H 2 Sal), are singled out and characterized. When studying thermograms, thermogravigrams, IR absorption spectra, roentgenograms of cadmium salicylate compounds (Cd(OC 6 H 4 COO) and products of their thepmal transformations, the processes of thermal decomposition of the compounds have been characterized. The process of cadmium monosalicylate decomposition takes place in one stage. Complete loss of salicylate acido group occurs in the range of 320-460 deg. At this decomposition stage cadmium oxide is formed. A supposition is made that cadmium complex has tetrahedral configuration, at that, each salicylate group plays the role of tetradentate-bridge ligand. The compound evidently has a polymer structure

  16. New insight into nanoparticle precipitation by electron beams in borosilicate glasses

    Science.gov (United States)

    Sabri, M. M.; Möbus, G.

    2017-06-01

    Nanoprecipitation in different oxide glasses by means of electron irradiation in transmission electron microscopy (TEM) has been compared in this study. Upon irradiation, groups or patterns of nanoparticles with various morphologies and sizes were formed in borosilicate glasses, loaded with zinc, copper, and silver. The study successfully includes loading ranges for the target metal from doping level (1%) over medium level (20%) to majority phase (60%). It is found that particle patterning resolution is affected by parallel processes of amorphous phase separation, glass ablation, and delocalised precipitation. In addition, via an in-situ study, it is confirmed that by heating alone without irradiation, no precipitate nanoparticles form.

  17. Compositional dependence thermal and optical properties of a novel germanate glass

    International Nuclear Information System (INIS)

    El-Rabaie, S.; Taha, T.A.; Higazy, A.A.

    2014-01-01

    A series of zinc lithium germanate glasses of the composition (45−x)Li 2 O–xZnO–55GeO 2 have been synthesized via melt quenching technique. Dependencies of their thermal and optical properties on composition were investigated. It is found that the gradual replacement of Li 2 O by ZnO, decreases the glass transition temperature from 430 to 280 °C and increases the thermal stability (ΔT) of the studied glasses. The optical band gap E opt also decreases from 2.31 to 1.40 eV with increasing the mole content of ZnO

  18. New insight into nanoparticle precipitation by electron beams in borosilicate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Sabri, M.M.; Moebus, G. [University of Sheffield, Department of Materials Science and Engineering (United Kingdom)

    2017-06-15

    Nanoprecipitation in different oxide glasses by means of electron irradiation in transmission electron microscopy (TEM) has been compared in this study. Upon irradiation, groups or patterns of nanoparticles with various morphologies and sizes were formed in borosilicate glasses, loaded with zinc, copper, and silver. The study successfully includes loading ranges for the target metal from doping level (1%) over medium level (20%) to majority phase (60%). It is found that particle patterning resolution is affected by parallel processes of amorphous phase separation, glass ablation, and delocalised precipitation. In addition, via an in-situ study, it is confirmed that by heating alone without irradiation, no precipitate nanoparticles form. (orig.)

  19. Relaxations in spin glasses: Similarities and differences from ordinary glasses

    International Nuclear Information System (INIS)

    Ngai, K.L.; Rajagopal, A.K.; Huang, C.Y.

    1984-01-01

    Relaxation phenomena have become a major concern in the physics of spin glasses. There are certain resemblances of these relaxation properties to those of ordinary glasses. In this work, we compare the relaxation properties of spin glasses near the freezing temperature with those of glasses near the glass transition temperature. There are similarities between the two types of glasses. Moreover, the relaxation properties of many glasses and spin glasses are in conformity with two coupled ''universality'' relations predicted by a recent model of relaxations in condensed matter

  20. Evaluation of Structural Cellular Glass

    Science.gov (United States)

    Adams, M. A.; Zwissler, J. G.

    1984-01-01

    Preliminary design information presented. First report discusses state of structural-cellular-glass programs as of June 1979. Second report gives further details of program to develop improved cellular glasses and to characterize properties of glasses and commercially available materials.

  1. Electric glass capturing markets

    Energy Technology Data Exchange (ETDEWEB)

    Wikman, K.; Wikstroem, T.

    1996-11-01

    Electric glass has found its place on the construction market. In public buildings, electrically heatable windows are becoming the leading option for large glass walls. Studies on detached houses, both new and renovated, show that floor heating combined with electrically heatable windowpanes is the best choice with respect to resident`s comfort. (orig.)

  2. Radioresistance of inorganic glasses

    International Nuclear Information System (INIS)

    Vorob'ev, A.A.; Zavadovskaya, E.K.; Fedorov, B.V.; Starodubtsev, V.A.

    1977-01-01

    Regularities are considered in the variation of properties of glass due to irradiations. On the basis of previous theoretical statements and experimental investigations, it is inferred that the irradiation resistance of glasses of the same type, synthesis conditions, content of impurities and amount of imperfections, is a function of the ''element-oxygen'' bond energy. The irradiation resistance depends on the number and the nature of glass structure imperfections. The averaged level of bonding forces is indicative of the glass formation temperature; the imperfections in glasses are formed in structure elements whose amount predominates as compared to the others. Electric charges which accumulate on the crack surface tend to increase its size, thus lessening even further the electric strength of the dielectric. The greater the irradiation time, the greater the number of irradiation imperfections causing a drop in the electric strength of glass. When choosing a glass for service in a radiation field, it is necessary to select those of a highest temperature of glass formation and with a least amount of imperfections

  3. Nucleation in ZBLAN glasses

    NARCIS (Netherlands)

    de Leede, G.L.A.; Waal, de H.

    1989-01-01

    Nucleation rates were detd. in a ZrF4-BaF2-NaF-LaF3-AlF3 glass (ZBLAN) using an optical method. The results were compared with a similar glass having a slightly different compn. The difference in the nucleation rate is explained by classical nucleation theory using calcd. free-energy differences

  4. Maternal Zinc Intakes and Homeostatic Adjustments during Pregnancy and Lactation

    OpenAIRE

    Donangelo, Carmen Marino; King, Janet C.

    2012-01-01

    Zinc plays critical roles during embryogenesis, fetal growth, and milk secretion, which increase the zinc need for pregnancy and lactation. Increased needs can be met by increasing the dietary zinc intake, along with making homeostatic adjustments in zinc utilization. Potential homeostatic adjustments include changes in circulating zinc, increased zinc absorption, decreased zinc losses, and changes in whole body zinc kinetics. Although severe zinc deficiency during pregnancy has devastating e...

  5. DSC, Raman and impedance spectroscopy studies on the xB2O3 - (90 - x)TeO2 - 10TiO2 (where x = 0 to 50 mol%) glass system

    Science.gov (United States)

    Sripada, Suresh; Rani, D. Esther Kalpana; Upender, G.; Pavani, P. Gayathri

    2013-03-01

    Titanium boro tellurite glasses in the xB2O3 -(90- x) TeO2 - 10TiO2 (where x = 0 to 50 mol%) system were prepared by using the conventional melt-quenching technique. Glass transition temperatures were measured with differential scanning calorimetry (DSC) and found to be in the range of 300-370 °C. The Raman spectra showed a cleavage of the continuous TeO4 (tbp) network by breaking of the Te-O-Te linkages. The relative transition of TeO4 - groups to TeO3 - groups is accompanied by a change in the oxygen coordination of the boron from 3 to 4 (BO3 - to BO4 -). The impedance plots Z″( ω) versus Z'( ω) for all the glass samples were recorded and found to exhibit a single circle. The AC conductivity of all glass samples was studied in the frequency range from 100 Hz to 1 MHz and in the temperature range from room temperature (RT) to 375 °C. The AC conductivity decreased by about one order in magnitude with increasing B2O3 content. The conductivity was found to be on the order of 10-4.5 to 10-6 (Ωcm)-1 at 375 °C and 1 MHz for 10 mol% and 50 mol% B2O3 contents, respectively. The relaxation behavior in these glass samples is discussed based on the complex modulus and impedance data.

  6. Selective masking and demasking for the stepwise complexometric determination of aluminium, lead and zinc from the same solution

    Directory of Open Access Journals (Sweden)

    Singh Nahar

    2008-03-01

    Full Text Available Abstract Background A complexometric method based on selective masking and de-masking has been developed for the rapid determination of aluminium, lead and zinc from the same solution in glass and glass frit samples. The determination is carried out using potassium cyanide to mask zinc, and excess disodium salt of EDTA to mask lead and aluminium. The excess EDTA was titrated with standard Mn(IISO4 solution using Erichrome Black-T as the indicator. Subsequently selective de-masking agents – triethanolamine, 2,3-dimercaptopropanol and a formaldehyde/acetone mixture – were used to determine quantities of aluminium, lead and zinc in a stepwise and selective manner. Results The accuracy of the method was established by analysing glass certified reference material NBS 1412. The standard deviation of the measurements, calculated by analysing five replicates of each sample, was found to be less than 1.5% for the method proposed. Conclusion The novelty of the method lies in its simplicity and accuracy afforded by there not being a need for a prior separation or instrumentation. The proposed method was found to be highly selective for the precise determination of aluminum, zinc and lead in the routine analysis of glass batch and allied materials.

  7. Mechanical relaxation in glasses

    International Nuclear Information System (INIS)

    Hiki, Y.

    2004-01-01

    The basic properties of glasses and the characteristics of mechanical relaxation in glasses were briefly reviewed, and then our studies concerned were presented. Experimental methods adopted were viscosity, internal friction, ultrasonic attenuation, and Brillouin scattering measurements. The specimens used were several kinds of inorganic, organic, and metallic glasses. The measurements were mainly carried out from the room temperature up to the glass transition temperature, and the relaxation time was determined as a function of temperature. The 'double relaxation' composed of two Arrhenius-type relaxations was observed in many materials. In both relaxations, the 'compensation effect' showing a correlation of the pre-exponential factor and the activation energy was observed. These results were explained by considering the 'complex relaxation' due to cooperative motions of atoms or group of atoms. Values of activation energy near the glass transition determined by the various experimental methods were compared with each other

  8. Polymorphism in glasses

    International Nuclear Information System (INIS)

    Landa, L.M.; Nikolaeva, I.N.

    1979-01-01

    To defect phase interfaces and spasmodic properties change, the inhomogeneity and the second radiation effects in quartz glass, metamict phase and intermediate states have been investigated. When irradiating with fast neutrons the transformation of quartz glass - metamict phase occurs completely. The transformation is completed at 2x10 20 part./cm 2 dose. Thermal treatment not only increases the number of inhomogeneities but also results in increasing quartz glass density. Annealing transforms the metamict phase into common quartz glass at 1400 K. The fact, that thermal treatment results in the complete transformation of metamict phase into quartz glass, and the inverse transformation occurs only partially, is quite regular, as the metamict phase has a lesser entropy and is a more ordered state. It is shown that different amorphous phases of a chemical composition have different structures and properties, that there are interfaces between them, and the transformation from one state to another in microvolumes is realized spasmodically and requires expenditure of energy

  9. Luminescence and energy transfer studies on Sm3+/Tb3+codoped telluroborate glasses for WLED applications

    Science.gov (United States)

    Uma, V.; Vijayakumar, M.; Marimuthu, K.; Muralidharan, G.

    2018-01-01

    A new series of Sm3+/Tb3+ codoped telluroborate glasses have been prepared by conventional melt quenching technique with the chemical composition (40-x-y)B2O3+15TeO2+15Li2O+15LiF+15NaF+xTb2O3+ySm2O3 (where x = 0, 0.5; y = 0, 0.05, 0.1, 0.25, 0.5, 1 and 2 wt%). The structural and optical behaviour of the prepared glasses were investigated through Fourier transform infrared spectroscopy (FTIR), optical absorption, photoluminescence and lifetime measurements. The fundamental vibrational units of the borate and tellurite network have been identified through FTIR spectra. Nephelauxetic ratio (βbar) and bonding parameter (δ) values indicate that the Smsbnd O bonds are ionic in nature. The characteristic emissions of terbium (543 nm, green) and samarium (645 nm, orange-red) were observed while exciting the Tb3+ ions. Higher magnitude of asymmetric intensity ratio (AIR) values confirms the higher asymmetry around the Sm3+ ion site. Decay profiles of Tb3+ ions (5D4 state) and Sm3+ ions (4G9/2 state) exhibit double exponential nature. The nature of interaction between the donor (Tb3+) and acceptor (Sm3+) has been analyzed through Inokuti-Hirayama (IH) model. Energy transfer from Tb3+ to Sm3+ ions is dominated by dipole-dipole type interaction. TBLT0.5S glass possess the better colour coordinates (0.41, 0.45) and colour correlated temperature (CCT) value (3524 K) and the same is suggested for eye safe warm white light emitting applications.

  10. Effect of zinc from zinc sulfate on trace mineral concentrations of milk ...

    African Journals Online (AJOL)

    PRECIOUS

    2009-11-16

    Nov 16, 2009 ... It suggests that supplementation of ewes diet with zinc sulfate could be an effective way to increase zinc ... alkaline phosphates activity. Zinc supplements were .... Similar results have been reported previously when dairy cows.

  11. Studies on nanocrystalline zinc coating

    Indian Academy of Sciences (India)

    Wintec

    The particles size was also characterized by TEM analysis. Keywords. Electrochemical ... netic materials for magnetic recording, and electrocatalyst for hydrogen .... polarization behaviour was studied in the test electrolyte for zinc deposit of ...

  12. Glass leaching performance

    International Nuclear Information System (INIS)

    Chick, L.A.; Turcotte, R.P.

    1983-05-01

    Current understanding of the leaching performance of high-level nuclear waste (HLW) glass is summarized. The empirical model of waste glass leaching behavior developed shows that at high water flow rates the glass leach rate is kinetically limited to a maximum value. At intermediate water flow rates, leaching is limited by the solution concentration of silica and decreases with decreasing water flow rates. Release of soluble elements is controlled by silica dissolution because silica forms the binding network of the glass. At low water flow rates, mass loss rates reach values controlled by formation rates of alteration minerals, or by diffusion of dissolution products through essentially stagnant water. The parameters reviewed with respect to their quantifiable influence on leaching behavior include temperature, pH, leachant composition, glass composition, thermal history, and radiation. Of these, temperature is most important since the rate of mass loss approximately doubles with each 10 0 C increase in dilute solutions. The pH has small effects within the 4 to 10 range. The chemical composition of the leachant is most important with regard to its influence on alteration product formation. Glass composition exhibits the largest effects at high flow rates where improved glasses leach from ten to thirty times slower than glass 76 to 68. The effects of the thermal history (devitrification) of the glass are not likely to be significant. Radiation effects are important primarily in that radiolysis can potentially drive pH values to less than 4. Radiation damage to the glass causes insignificant changes in leaching performance

  13. Enhancement of 800 nm upconversion emission in a thulium doped tellurite microstructured fiber pumped by a 1560 nm femtosecond fiber laser

    Energy Technology Data Exchange (ETDEWEB)

    Jia, Zhixu; Zheng, Kezhi [State Key Laboratory of Optical Fiber and Cable Manufacture Technology, Yangtze Optical Fiber and Cable Joint Stock Limited Company, Wuhan 430073 (China); State Key Laboratory on Integrated Optoelectronics, College of Electronic Science and Engineering, Jilin University, Changchun 130012 (China); Yao, Chuanfei; Wang, Shunbin; Qin, Guanshi, E-mail: qings@jlu.edu.cn; Qin, Weiping, E-mail: wpqin@jlu.edu.cn [State Key Laboratory on Integrated Optoelectronics, College of Electronic Science and Engineering, Jilin University, Changchun 130012 (China); Xiong, Liangming; Luo, Jie; Lv, Dajuan [State Key Laboratory of Optical Fiber and Cable Manufacture Technology, Yangtze Optical Fiber and Cable Joint Stock Limited Company, Wuhan 430073 (China); Ohishi, Yasutake [Research Center for Advanced Photon Technology, Toyota Technological Institute, 2-12-1 Hisakata, Tempaku, Nagoya 468–8511 (Japan)

    2016-04-28

    We report enhanced upconversion (UC) fluorescence in Tm{sup 3+} doped tellurite microstructured fibers (TDTMFs) fabricated by using a rod-in-tube method. Under the pumping of a 1560 nm femtosecond fiber laser, ultrabroadband supercontinuum light expanding from ∼1050 to ∼2700 nm was generated in a 4 cm long TDTMF. Simultaneously, intense 800 nm UC emission from the {sup 3}H{sub 4} → {sup 3}H{sub 6} transition of Tm{sup 3+} was observed in the same TDTMF. Compared to that pumped by a 1560 nm continuous wave fiber laser, the UC emission intensity was enhanced by ∼4.1 times. The enhancement was due to the spectral broadening in the TDTMF under the pumping of the 1560 nm femtosecond fiber laser.

  14. Organically pillared layered zinc hydroxides

    International Nuclear Information System (INIS)

    Kongshaug, K.O.; Fjellvaag, Helmer

    2004-01-01

    The two organically pillared layered zinc hydroxides [Zn 2 (OH) 2 (ndc)], CPO-6, and [Zn 3 (OH) 4 (bpdc)], CPO-7, were obtained in hydrothermal reactions between 2,6-naphthalenedicarboxylic acid (ndc) and zinc nitrate (CPO-6) and 4,4'biphenyldicarboxylate (bpdc) and zinc nitrate (CPO-7), respectively. In CPO-6, the tetrahedral zinc atoms are connected by two μ 2 -OH groups and two carboxylate oxygen atoms, forming infinite layers extending parallel to the bc-plane. These layers are pillared by ndc to form a three-dimensional structure. In CPO-7, the zinc hydroxide layers are containing four-, five- and six coordinated zinc atoms, and the layers are built like stairways running along the [001] direction. Each step is composed of three infinite chains running in the [010] direction. Both crystal structures were solved from conventional single crystal data. Crystal data for CPO-6: Monoclinic space group P2 1 /c (No. 14), a=11.9703(7), b=7.8154(5), c=6.2428(4) A, β=90.816(2) deg., V=583.97(6) A 3 and Z=4. Crystal data for CPO-7: Monoclinic space group C2/c (No. 15), a=35.220(4), b=6.2658(8), c=14.8888(17) A, β=112.580(4) deg., V=3033.8(6) A 3 and Z=8. The compounds were further characterized by thermogravimetric- and chemical analysis

  15. Evaluation of the gamma radiation shielding parameters of bismuth modified quaternary glass system

    Science.gov (United States)

    Kaur, Parminder; Singh, K. J.; Thakur, Sonika

    2018-05-01

    Glasses modified with heavy metal oxides (HMO) are an interesting area of research in the field of gamma-ray shielding. Bismuth modified lithium-zinc-borate glasses have been studied whereby bismuth oxide is added from 0 to 50 mol%. The gamma ray shielding properties of the glasses were evaluated at photon energy 662 keV with the help of XMuDat computer program by using the Hubbell and Seltzer database. Various gamma ray shielding parameters such as attenuation coefficient, shield thickness in terms of half and tenth value layer, effective atomic number have been studied in this work. A useful comparison of this glass system has been made with standard radiation shielding concretes viz. ordinary, barite and iron concrete. The glass samples containing 20 to 50 mol% bismuth oxide have shown better gamma ray shielding properties and hence have the potential to become good radiation absorbers.

  16. Effect of ZnO on phase emergence, microstructure and surface modifications of calcium phosphosilicate glass/glass-ceramics having iron oxide

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, K.; Dixit, A.; Bhattacharya, S.; Jagannath [Technical Physics and Prototype Engineering Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India); Deo, M.N. [High Pressure Physics Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India); Kothiyal, G.P., E-mail: gpkoth@barc.gov.in [Technical Physics and Prototype Engineering Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India)

    2010-03-01

    The effect of ZnO on phase emergence and microstructure properties of glass and glass-ceramics with composition 25SiO{sub 2}-50CaO-15P{sub 2}O{sub 5}-(10 - x)Fe{sub 2}O{sub 3}-xZnO (where x = 0, 2, 5, 7 mol%) has been studied. They have been characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Surface modifications of these glass-ceramics in simulated body fluid have been studied using Fourier transform infrared reflection spectroscopy (FTIR), XPS and SEM. Results have shown a decrease in the fraction of non-bridging oxygen with increase in zinc oxide content. Emergence of crystalline phases in glass-ceramics at different heat treatment temperatures was studied using XRD. When glass is heat treated at 800 deg. C calcium phosphate, hematite and magnetite are developed as major phases in the glass-ceramics samples with ZnO up to 5 mol%. In addition to these, calcium silicate (Ca{sub 3}Si{sub 2}O{sub 7}) phase is also observed when glass is heat treated at 1000 deg. C. The microstructure of the glass-ceramics heat treated at 800 deg. C exhibits the formation of nano-size (40-50 nm) grains. On heat treatment at 1000 deg. C crystallites grow to above 50 nm size and more than one phase are observed in the microstructure. The formation of thin flake-like structure with coarse particles is observed at high zinc oxide concentration (x = 7 mol%). In vitro studies have shown the surface modifications and formation of Ca-P-rich layer on the glass-ceramics when immersed in simulated body fluids (SBF) for different durations. The bioactive response was found to depend on ZnO content.

  17. Effect of ZnO on phase emergence, microstructure and surface modifications of calcium phosphosilicate glass/glass-ceramics having iron oxide

    International Nuclear Information System (INIS)

    Sharma, K.; Dixit, A.; Bhattacharya, S.; Jagannath; Deo, M.N.; Kothiyal, G.P.

    2010-01-01

    The effect of ZnO on phase emergence and microstructure properties of glass and glass-ceramics with composition 25SiO 2 -50CaO-15P 2 O 5 -(10 - x)Fe 2 O 3 -xZnO (where x = 0, 2, 5, 7 mol%) has been studied. They have been characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Surface modifications of these glass-ceramics in simulated body fluid have been studied using Fourier transform infrared reflection spectroscopy (FTIR), XPS and SEM. Results have shown a decrease in the fraction of non-bridging oxygen with increase in zinc oxide content. Emergence of crystalline phases in glass-ceramics at different heat treatment temperatures was studied using XRD. When glass is heat treated at 800 deg. C calcium phosphate, hematite and magnetite are developed as major phases in the glass-ceramics samples with ZnO up to 5 mol%. In addition to these, calcium silicate (Ca 3 Si 2 O 7 ) phase is also observed when glass is heat treated at 1000 deg. C. The microstructure of the glass-ceramics heat treated at 800 deg. C exhibits the formation of nano-size (40-50 nm) grains. On heat treatment at 1000 deg. C crystallites grow to above 50 nm size and more than one phase are observed in the microstructure. The formation of thin flake-like structure with coarse particles is observed at high zinc oxide concentration (x = 7 mol%). In vitro studies have shown the surface modifications and formation of Ca-P-rich layer on the glass-ceramics when immersed in simulated body fluids (SBF) for different durations. The bioactive response was found to depend on ZnO content.

  18. Effect of zinc sources on yield and utilization of zinc in rice-wheat sequence

    International Nuclear Information System (INIS)

    Deb, D.L.

    1990-01-01

    A field experiment was conducted on an inceptisol of Delhi to evaluate three sources of zinc, namely, zinc sulphate, zincated urea and zinc oxide on yield and utilization of zinc in rice-wheat sequence. Results indicated that, amongst the three zinc sources, zinc sulphate and zincated urea gave the best performance in increasing the grain yield of rice whereas zinc oxide depressed the grain yield of wheat significantly when compared to other treatments. The highest Zn derived from fertilizer and its utilization was obtained with zinc sulphate for both rice and wheat crops. (author). 9 refs., 4 tabs

  19. Influence of the Hydrothermal Method Growth Parameters on the Zinc Oxide Nanowires Deposited on Several Substrates

    Directory of Open Access Journals (Sweden)

    Concepción Mejía-García

    2014-01-01

    Full Text Available We report the synthesis of ZnO nanowires grown on several substrates (PET, glass, and Si using a two-step process: (a preparation of the seed layer on the substrate by spin coating, from solutions of zinc acetate dihydrate and 1-propanol, and (b growth of the ZnO nanostructures by dipping the substrate in an equimolar solution of zinc nitrate hexahydrate and hexamethylenetetramine. Subsequently, films were thermally treated with a commercial microwave oven (350 and 700 W for 5, 20, and 35 min. The ZnO nanowires obtained were characterized structurally, morphologically, and optically using XRD, SEM, and UV-VIS transmission, respectively. XRD patterns spectra revealed the presence of Zn(OH2 on the films grown on glass and Si substrates. A preferential orientation along c-axis directions for films grown on PET substrate was observed. An analysis by SEM revealed that the growth of the ZnO nanowires on PET and glass is better than the growth on Si when the same growth parameters are used. On glass substrates, ZnO nanowires less than 50 nm in diameter and between 200 nm and 1200 nm in length were obtained. The ZnO nanowires band gap energy for the films grown on PET and glass was obtained from optical transmission spectra.

  20. Thermal Conductivity of Foam Glass

    DEFF Research Database (Denmark)

    Petersen, Rasmus Rosenlund; König, Jakob; Yue, Yuanzheng

    Due to the increased focus on energy savings and waste recycling foam glass materials have gained increased attention. The production process of foam glass is a potential low-cost recycle option for challenging waste, e.g. CRT glass and industrial waste (fly ash and slags). Foam glass is used...... as thermal insulating material in building and chemical industry. The large volume of gas (porosity 90 – 95%) is the main reason of the low thermal conductivity of the foam glass. If gases with lower thermal conductivity compared to air are entrapped in the glass melt, the derived foam glass will contain...... only closed pores and its overall thermal conductivity will be much lower than that of the foam glass with open pores. In this work we have prepared foam glass using different types of recycled glasses and different kinds of foaming agents. This enabled the formation of foam glasses having gas cells...