  1. High trapped fields in bulk YBCO superconductors

    Science.gov (United States)

    Fuchs, Günter; Gruss, Stefan; Krabbes, Gernot; Schätzle, Peter; Verges, Peter; Müller, Karl-Hartmut; Fink, Jörg; Schultz, Ludwig

    The trapped field properties of bulk melt-textured YBCO material were investigated at different temperatures. In the temperature range of liquid nitrogen, maximum trapped fields of 1.1 T were found at 77 K by doping of YBCO with small amounts of zinc. The improved pinning of zinc-doped YBa2Cu3O7-x (YBCO) results in a pronounced peak effect in the field dependence of the critical current density. the trapped field at lower temperatures increases due to the increasing critical current density, however, at temperatures around 50 K cracking of the material is observed which is exposed to considerably tensile stresses due to Lorentz forces. Very high trapped fields up to 14.4 T were achieved at 22.5 K for a YBCO disk pair by the addition of silver improving the tensile strength of YBCO and by using a bandage made of a steel tube. The steel tube produces a compressive stress on YBCO after cooling down from 300 K to the measuring temperature, which is due to the higher coeeficient of thermal expansion of steel compared with that of YBCO in the a,b plane. The application of superconducting permanent magnets with trapped fields of 10 T and more in superconducting bearings would allow to obtain very high levitation pressures up to 2500 N/cm2 which is two orders of magnitude higher than the levitation pressure achievable in superconducting bearings with conventional permanent magnets. The most important problem for the application of superconducting permanent magnets is the magnetizing procedure of the YBCO material. Results of magnetizing YBCO disks by using of pulsed magnetic fields will be presented.

  2. Contamination of YBCO bulk superconductors by samarium and ytterbium

    Czech Academy of Sciences Publication Activity Database

    Volochová, D.; Jurek, Karel; Radušovská, M.; Piovarči, S.; Antal, V.; Kováč, J.; Jirsa, Miloš; Diko, P.

    2014-01-01

    Roč. 496, JAN (2014), s. 14-17 ISSN 0921-4534 Institutional support: RVO:68378271 Keywords : YBCO bulk superconductors * critical temperature * critical current density * peak effect Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.942, year: 2014

  3. A small Maglev car model using YBCO bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Yang, W M [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Zhou, L [Northwest Institute for Nonferrous Metal Research, PO Box 51, Xi' an, Shaanxi 710016 (China); Yong, Feng [Northwest Institute for Nonferrous Metal Research, PO Box 51, Xi' an, Shaanxi 710016 (China); Zhang, P X [Northwest Institute for Nonferrous Metal Research, PO Box 51, Xi' an, Shaanxi 710016 (China); Chao, X X [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Bian, X B [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Zhu, S H [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Wu, X L [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Liu, P [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China)

    2006-07-15

    Models of two small Maglev cars have been made. The track was paved with NdFeB magnets. The arrangement of the magnets made it easy to get a uniform magnetic field distribution along the length of the track and a magnetic field gradient in the lateral direction. When the car with YBCO bulk superconductors was field cooled to LN{sub 2} temperature at a certain distance above the track, the car could be automatically levitated over the track and moved along the track without any obvious friction. The model can be used to demonstrate the Meissner effect and a fast transportation system to students and adults.

  4. A small Maglev car model using YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Yang, W M; Zhou, L; Yong, Feng; Zhang, P X; Chao, X X; Bian, X B; Zhu, S H; Wu, X L; Liu, P

    2006-01-01

    Models of two small Maglev cars have been made. The track was paved with NdFeB magnets. The arrangement of the magnets made it easy to get a uniform magnetic field distribution along the length of the track and a magnetic field gradient in the lateral direction. When the car with YBCO bulk superconductors was field cooled to LN 2 temperature at a certain distance above the track, the car could be automatically levitated over the track and moved along the track without any obvious friction. The model can be used to demonstrate the Meissner effect and a fast transportation system to students and adults

  5. Acoustic emission behavior under bending deformation of YBCO bulk superconductor

    International Nuclear Information System (INIS)

    Yoneda, K.; Ye, J.; Tomita, M.

    2005-01-01

    Bending tests were conducted on U-notched specimens cut from a YBCO bulk superconductor. Acoustic emission (AE) signals obtained under loading parallel or perpendicular to the c-axis were analyzed to investigate the correlation between crack growth behavior and the AE signals. As a result of analyzing log-log plots of strength (σ B ) versus total AE energy (ΣE AE ), a linear relationship was found between ΣE AE and σ B n . Cracks could be broadly divided into two types based on the value of n as an index of crack growth behavior. One type consisted of microcracks originating from cleavage planes and gas holes; these crack propagated parallel to the c-axis and had an n index value of approximately 0.7. The other type was a main crack that originated from the U-notch and had an n index value of approximately 6.5. A sample (A) loaded parallel to the c-axis showed mean bending strength of 74.8MPa. Cracks displaying two different growth patterns of n=0.7 and 6.5 were presented in this sample. Microcracks parallel to the c-axis occurred in the vicinity of 5-10MPa. This sample was characterized by mixed crack growth of a main crack and microcracks. A sample (B) loaded perpendicular to the c-axis displayed mean bending strength of 43MPa. A main crack occurred in the vicinity of 20MPa and displayed a single growth pattern of n=6.5. By analyzing AE signals in this way in the process of conducting a strength evaluation, it was possible to evaluate the failure process of the bulk superconductor in relation to the strength level induced by the applied load

  6. Oxygenation and cracking in melt-textured YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Kracunovska, S; Diko, P; Litzkendorf, D; Habisreuther, T; Bierlich, J; Gawalek, W

    2005-01-01

    Microstructural changes during the oxygenation of YBCO bulks were studied. It was shown that a lower temperature of oxygenation leads to the formation of a denser structure of a/b- and c-macrocracks and causes faster and more homogeneous oxygenation of the sample. The opening of created macrocracks is the way in which the macroscopic stresses induced by macroscopic 211 particle concentration inhomogeneity are released. This is very important, because it prevents the formation of fatal c-macrocracks, which divide the sample into more domains, during cooling from oxygenation temperature or during sample performance. Oxygenation with a multistage programme causes the oxygen concentration difference between the oxygenated layer and the tetragonal matrix to be smaller, and consequently fewer macrocracks are formed. This leads to the prolongation of oxygenation times for full oxygenation and to the insufficient release of macroscopic stresses. 211 low concentration regions and pores also enhance the oxygenation rate of YBCO bulks

  7. New method for introducing nanometer flux pinning centers into single domain YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Yang, W.M.; Wang, Miao

    2013-01-01

    Highlights: • Single domain YBCO bulks with Bi 2 O 3 additions fabricated by TSIG process. • Nanoscale Y 2 Ba 4 CuBiOx(YBi2411) particles introduced by Bi 2 O 3 additions. • The YBi2411 particles are about 150 nm, can act as effective flux pinning centers. • The optimal addition of Bi 2 O 3 is 0.7wt% to achieve higher levitation force. • The result is helpful to improve the quality of REBCO bulk superconductors. -- Abstract: Single domain YBCO superconductors with different additions of Bi 2 O 3 have been fabricated by top seeded infiltration and growth process (TSIG). The effect of Bi 2 O 3 additions on the growth morphology, microstructure and levitation force of the YBCO bulk superconductor has been investigated. The results indicate that single domain YBCO superconductors can be fabricated with the additions of Bi 2 O 3 less than 2 wt%; Bi 2 O 3 can be reacted with Y 2 BaCuO 5 and liquid phase and finally form Y 2 Ba 4 CuBiO x (YBi2411) nanoscale particles; the size of the YBi2411 particles is about 100 nm, which can act as effective flux pinning centers. It is also found that the levitation force of single domain YBCO bulks is increasing from 13 N to 34 N and decreasing to 11 N with the increasing of Bi 2 O 3 addition from 0.1 wt% to 0.7 wt% and 2 wt%. This result is helpful for us to improve the physical properties of REBCO bulk superconductors

  8. Magnetic levitation and its application for education devices based on YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Yang, W.M.; Chao, X.X.; Guo, F.X.; Li, J.W.; Chen, S.L.

    2013-01-01

    Highlights: • A small superconducting maglev propeller system has been designed and constructed based on YBCO bulk superconductors. • Several small maglev vehicle models have been designed and constructed based on YBCO bulk superconductors. • The models can be used as experimental or demonstration devices for the magnetic levitation applications. -- Abstract: A small superconducting maglev propeller system, a small spacecraft model suspending and moving around a terrestrial globe, several small maglev vehicle models and a magnetic circuit converter have been designed and constructed. The track was paved by NdFeB magnets, the arrangement of the magnets made us easy to get a uniform distribution of magnetic field along the length direction of the track and a high magnetic field gradient in the lateral direction. When the YBCO bulks mounted inside the vehicle models or spacecraft model was field cooled to LN 2 temperature at a certain distance away from the track, they could be automatically floating over and moving along the track without any obvious friction. The models can be used as experimental or demonstration devices for the magnetic levitation applications

  9. Magnetic levitation and its application for education devices based on YBCO bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Yang, W.M., E-mail: yangwm@snnu.edu.cn; Chao, X.X.; Guo, F.X.; Li, J.W.; Chen, S.L.

    2013-10-15

    Highlights: • A small superconducting maglev propeller system has been designed and constructed based on YBCO bulk superconductors. • Several small maglev vehicle models have been designed and constructed based on YBCO bulk superconductors. • The models can be used as experimental or demonstration devices for the magnetic levitation applications. -- Abstract: A small superconducting maglev propeller system, a small spacecraft model suspending and moving around a terrestrial globe, several small maglev vehicle models and a magnetic circuit converter have been designed and constructed. The track was paved by NdFeB magnets, the arrangement of the magnets made us easy to get a uniform distribution of magnetic field along the length direction of the track and a high magnetic field gradient in the lateral direction. When the YBCO bulks mounted inside the vehicle models or spacecraft model was field cooled to LN{sub 2} temperature at a certain distance away from the track, they could be automatically floating over and moving along the track without any obvious friction. The models can be used as experimental or demonstration devices for the magnetic levitation applications.

  10. Single domain YBCO/Ag bulk superconductors fabricated by seeded infiltration and growth

    International Nuclear Information System (INIS)

    Iida, K; Babu, N H; Shi, Y; Cardwell, D A; Miyazaki, T; Murakami, M; Sakai, N

    2008-01-01

    We have applied the seeded infiltration and growth (IG) technique to the processing of samples containing Ag in an attempt to fabricate Ag-doped Y-Ba-Cu-O (YBCO) bulk superconductors with enhanced mechanical properties. The IG technique has been used successfully to grow bulk Ag-doped YBCO superconductors of up to 25 mm in diameter in the form of single grains. The distribution of Ag in the parent Y-123 matrix fabricated by the IG technique is observed to be at least as uniform as that in samples grown by conventional top seeded melt growth (TSMG). Fine Y-211 particles were observed to be embedded within the Y-123 matrix for the IG processed samples, leading to a high critical current density, J c , of over 70 kA/cm 2 at 77.3 K in self-field. The distribution of Y-211 in the IG sample microstructure, however, is inhomogeneous, which leads to a variation in the spatial distribution of J c throughout the bulk matrix. A maximum-trapped field of around 0.43 T at 1.2 mm above the sample surface (i.e. including 0.7 mm for the sensor mould thickness) is observed at liquid nitrogen temperature, despite the relatively small grain size of the sample (20 mm diameter x 7 mm thickness)

  11. AC susceptibility response of bulk YBCO superconductors in the presence of a temperature gradient

    International Nuclear Information System (INIS)

    Bodi, A.C.; Kirschner, I.

    1997-01-01

    Low-frequency AC susceptibility measurements on ceramic YBCO superconductors carried out at the presence of a quasi-one-dimensional temperature gradient are compared with those made without the temperature gradient. The values of the different characteristic temperatures measured on samples without and with a temperature gradient are identical but in the second case its characteristic temperature is a medium value. When the temperature gradient is constant on the sample the arithmetic medium value of the local temperatures is the effective characteristic temperature different phenomena. (orig.)

  12. The effect of magnet size on the levitation force and attractive force of single-domain YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Yang, W M; Chao, X X; Bian, X B; Liu, P; Feng, Y; Zhang, P X; Zhou, L

    2003-01-01

    The levitation forces between a single-domain YBCO bulk and several magnets of different sizes have been measured at 77 K to investigate the effect of the magnet size on the levitation force. It is found that the levitation force reaches a largest (peak) value when the size of the magnet approaches that of the superconductor when the other conditions are fixed. The absolute maximum attractive force (in the field-cooled state) increases with the increasing of the magnet size, and is saturated when the magnet size approaches that of the superconductor. The maximum attractive force in the field-cooled (FC) state is much higher than that of the maximum attractive force in the zero field-cooled (ZFC) state. The results indicate that the effects of magnetic field distribution on the levitation force have to be considered during the designing and manufacturing of superconducting devices

  13. The effect of Sm addition on the microstructure and superconducting properties of YBCO bulk superconductors

    Czech Academy of Sciences Publication Activity Database

    Volochová, D.; Diko, P.; Piovarči, S.; Antal, V.; Kováč, J.; Jirsa, Miloš

    2017-01-01

    Roč. 131, č. 4 (2017), s. 1009-1011 ISSN 0587-4246 Institutional support: RVO:68378271 Keywords : YBaCuO * bulk superconductors * paramagnetic ions * microstructure * vortex pinning Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 0.469, year: 2016

  14. Magnetic levitation and its application for education devices based on YBCO bulk superconductors

    Science.gov (United States)

    Yang, W. M.; Chao, X. X.; Guo, F. X.; Li, J. W.; Chen, S. L.

    2013-10-01

    A small superconducting maglev propeller system, a small spacecraft model suspending and moving around a terrestrial globe, several small maglev vehicle models and a magnetic circuit converter have been designed and constructed. The track was paved by NdFeB magnets, the arrangement of the magnets made us easy to get a uniform distribution of magnetic field along the length direction of the track and a high magnetic field gradient in the lateral direction. When the YBCO bulks mounted inside the vehicle models or spacecraft model was field cooled to LN2 temperature at a certain distance away from the track, they could be automatically floating over and moving along the track without any obvious friction. The models can be used as experimental or demonstration devices for the magnetic levitation applications.

  15. Development of superconductor bulk for superconductor bearing

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Chan Joong; Jun, Byung Hyuk; Park, Soon Dong (and others)

    2008-08-15

    Current carrying capacity is one of the most important issues in the consideration of superconductor bulk materials for engineering applications. There are numerous applications of Y-Ba-Cu-O (YBCO) bulk superconductors e.g. magnetic levitation train, flywheel energy storage system, levitation transportation, lunar telescope, centrifugal device, magnetic shielding materials, bulk magnets etc. Accordingly, to obtain YBCO materials in the form of large, single crystals without weak-link problem is necessary. A top seeded melt growth (TSMG) process was used to fabricate single crystal YBCO bulk superconductors. The seeded and infiltration growth (IG) technique was also very promising method for the synthesis of large, single-grain YBCO bulk superconductors with good superconducting properties. 5 wt.% Ag doped Y211 green compacts were sintered at 900 .deg. C {approx} 1200 .deg.C and then a single crystal YBCO was fabricated by an infiltration method. A refinement and uniform distribution of the Y211 particles in the Y123 matrix were achieved by sintering the Ag-doped samples. This enhancement of the critical current density was ascribable to a fine dispersion of the Y211 particles, a low porosity and the presence of Ag particles. In addition, we have designed and manufactured large YBCO single domain with levitation force of 10-13 kg/cm{sup 2} using TSMG processing technique.

  16. Dynamic characteristics and finite element analysis of a magnetic levitation system using a YBCO bulk superconductor

    International Nuclear Information System (INIS)

    Ueda, H; Ishiyama, A

    2004-01-01

    We have been developing a magnetic levitating device with two-dimensional movement, namely a 'levitating X-Y transporter'. For the real design of a levitating X-Y transporter, it is necessary to clarify the levitation characteristics, such as the lift, the levitation height and the stability against mechanical disturbances. Furthermore various kinds of force may be applied to the levitating part and cause mechanical oscillation. Therefore the characteristics of oscillation are also important factors in the dynamic stability of such a levitation system. In this paper, we examine experimentally the lift and the restoring force and develop a new simulation code based on the three-dimensional hybrid finite and boundary element method to analyse the dynamic electromagnetic behaviour of the HTS bulk. We have investigated a suitable permanent-magnet arrangement to enhance the levitation characteristics through experiment and numerical simulation. We can then determine the suitable conditions for stable levitation from those results

  17. Influence of Sm2O3 microalloying and Yb contamination on Y211 particles coarsening and superconducting properties of IG YBCO bulk superconductors

    Science.gov (United States)

    Vojtkova, L.; Diko, P.; Kovac, J.; Vojtko, M.

    2018-06-01

    Single grain YBa2Cu3O7‑x (YBCO or Y123) bulk superconductors were produced by an infiltration growth process. The solid phase precursor was prepared by solid state synthesis from Y2O3 + BaCuO2 powders. The influence of the addition of Sm2O3 and YB contamination from the substrate on the microstructure and superconducting properties was analyzed. The dependences of Yb concentration on the distance from the bottom of the samples measured by energy dispersive spectroscopy microanalysis used in conjunction with scanning electron microscopy confirmed the contamination of the samples during the melting stage of the sample preparation. It is shown that the addition of Sm in low concentration and its combination with Yb from the substrate modify the coarsening of the Y211 particles as well as lead to the appearance of a secondary peak effect in the field dependences of the critical current density.

  18. Control of Y-211 content in bulk YBCO superconductors fabricated by a buffer-aided, top seeded infiltration and growth melt process

    International Nuclear Information System (INIS)

    Namburi, Devendra K; Shi, Yunhua; Palmer, Kysen G; Dennis, Anthony R; Durrell, John H; Cardwell, David A

    2016-01-01

    Bulk (RE)–Ba–Cu–O ((RE)BCO, where RE stands for rare-earth), single grain superconductors can trap magnetic fields of several tesla at low temperatures and therefore can function potentially as high field magnets. Although top seeded melt growth (TSMG) is an established process for fabricating relatively high quality single grains of (RE)BCO for high field applications, this technique suffers from inherent problems such as sample shrinkage, a large intrinsic porosity and the presence of (RE) 2 BaCuO 5 (RE-211)-free regions in the single grain microstructure. Seeded infiltration and growth (SIG), therefore, has emerged as a practical alternative to TSMG that overcomes many of these problems. Until now, however, the superconducting properties of bulk materials processed by SIG have been inferior to those fabricated using the TSMG technique. In this study, we identify that the inferior properties of SIG processed bulk superconductors are related to the presence of a relatively large Y-211 content (∼41.8%) in the single grain microstructure. Controlling the RE-211 content in SIG bulk samples is particularly challenging because it is difficult to regulate the entry of the liquid phase into the solid RE-211 preform during the infiltration process. In an attempt to solve this issue, we have investigated the effect of careful control of both the infiltration temperature and the quantity of liquid phase powder present in the sample preforms prior to processing. We conclude that careful control of the infiltration temperature is the most promising of these two process variables. Using this knowledge, we have fabricated successfully a YBCO bulk single grain using the SIG process of diameter 25 mm that exhibits a trapped field of 0.69 T at 77 K, which is the largest value reported to date for a sample fabricated by the SIG technique. (paper)

  19. The influence of slow cooling on Y211 size and content in single-grain YBCO bulk superconductor through the infiltration-growth process

    Energy Technology Data Exchange (ETDEWEB)

    Ouerghi, A [Systems and Applied Mechanics Laboratory LASMAP, Polytechnic School of Tunisia, Rue El Kawarezmi La Marsa 743, Université de Carthage Tunis (Tunisia); Moutalbi, N., E-mail: nahed.moutalbi@yahoo.fr [Systems and Applied Mechanics Laboratory LASMAP, Polytechnic School of Tunisia, Rue El Kawarezmi La Marsa 743, Université de Carthage Tunis (Tunisia); Noudem, J.G. [CRISMAT-ENSICAEN (UMR-CNRS 6508), Université de Caen-Basse-Normandie, F-14050 Caen (France); LUSAC, Université de Caen-Basse-Normandie F-50130 Cherbourg-Octeville (France); M' chirgui, A. [Systems and Applied Mechanics Laboratory LASMAP, Polytechnic School of Tunisia, Rue El Kawarezmi La Marsa 743, Université de Carthage Tunis (Tunisia)

    2017-03-15

    Highlights: • YBCO bulk superconductors are produced by optimized Seeded Infiltration and Growth process. • The slow cooling time, in a fixed slow cooling temperature window, affects considerably the surface morphology and the bulk’s microstructure. • The Y211 particle’s size and content depend on the slow cooling time and its distribution behavior changes from one position to another. • There is an optimum slow cooling time, estimated to 88h, over which the shrinkage for both the liquid phase and the Y211 pellet is maximal, without any improvement of the crystal grain growth. • The magnetic trapped flux distribution for a given sample brings out the single grain characteristic. - Abstract: Highly textured YBa{sub 2}Cu{sub 3}O{sub 7-δ} (Y123) superconductors were produced using modified Textured Top Seeded Infiltration Growth (TSIG) process. The liquid source is made of only Y123 powder whereas the solid source is composed of Y{sub 2}BaCuO{sub 5} (Y211) powder. We aim to control the amount of liquid that infiltrates the solid pellet, which in turn controls the final amount of Y{sub 2}BaCuO{sub 5} particles in Y123 matrix. The effect of the slow cooling kinetics on sample morphology, on grain growth and on final microstructure was too investigated. It is shown that appropriate slow cooling time may also contribute to the control of the amount of Y211 inclusions in the final structure of Y123 bulk. We report herein the Y211 particle size and density distribution in the whole Y123 matrix. The present work proves that finest Y211 particles locate under the seed and that their size and density increase with distance from the seed.

  20. Recent results in characterization of melt-grown and quench-melt- grown YBCO superconductors

    International Nuclear Information System (INIS)

    Balachandran, U.; Poeppel, R.B.; Gangopadhyay, A.K.

    1992-02-01

    From the standpoint of applications, melt-grown (MG) and quench-melt-grown (QMG) bulk YBCO superconductors are of considerable interest. In this paper, we studied the intragranular critical current density (J c ), the apparent pinning potential (U o ), and the irreversibility temperature (T irr ) of MG and QMG samples and compared the results to those for conventionally sintered YBCO. A systematic increase in U o and a slower drop in J c with temperature indicate a systematic improvement in flux-pinning properties in progressing from the sintered YBCO to QMG and MG samples. Weaker pinning is observed in the QMG YBCO than in the MG samples

  1. Large area bulk superconductors

    Science.gov (United States)

    Miller, Dean J.; Field, Michael B.

    2002-01-01

    A bulk superconductor having a thickness of not less than about 100 microns is carried by a polycrystalline textured substrate having misorientation angles at the surface thereof not greater than about 15.degree.; the bulk superconductor may have a thickness of not less than about 100 microns and a surface area of not less than about 50 cm.sup.2. The textured substrate may have a thickness not less than about 10 microns and misorientation angles at the surface thereof not greater than about 15.degree.. Also disclosed is a process of manufacturing the bulk superconductor and the polycrystalline biaxially textured substrate material.

  2. Static Test for a Gravitational Force Coupled to Type 2 YBCO Superconductors

    Science.gov (United States)

    Li, Ning; Noever, David; Robertson, Tony; Koczor, Ron; Brantley, Whitt

    1997-01-01

    As a Bose condensate, superconductors provide novel conditions for revisiting previously proposed couplings between electromagnetism and gravity. Strong variations in Cooper pair density, large conductivity and low magnetic permeability define superconductive and degenerate condensates without the traditional density limits imposed by the Fermi energy (approx. 10(exp -6) g cc. Recent experiments have reported anomalous weight loss for a test mass suspended above a rotating type II, YBCO superconductor, with the percentage change (0.05 - 2.1 %) independent of the test mass' chemical composition and diamagnetic properties. A variation of 5 parts per 10' was reported above a stationary (non-rotating) superconductor. In experiments using a sensitive gravimeter, bulk YBCO superconductors were stably levitated in a DC magnetic field. Changes in acceleration were measured to be less than 2 parts in 108 of the normal gravitational acceleration. This result puts new limits on the strength and range of the proposed coupling between static superconductors and gravity.

  3. Bulk Superconductors in Mobile Application

    Science.gov (United States)

    Werfel, F. N.; Delor, U. Floegel-; Rothfeld, R.; Riedel, T.; Wippich, D.; Goebel, B.; Schirrmeister, P.

    We investigate and review concepts of multi - seeded REBCO bulk superconductors in mobile application. ATZ's compact HTS bulk magnets can trap routinely 1 T@77 K. Except of magnetization, flux creep and hysteresis, industrial - like properties as compactness, power density, and robustness are of major device interest if mobility and light-weight construction is in focus. For mobile application in levitated trains or demonstrator magnets we examine the performance of on-board cryogenics either by LN2 or cryo-cooler application. The mechanical, electric and thermodynamical requirements of compact vacuum cryostats for Maglev train operation were studied systematically. More than 30 units are manufactured and tested. The attractive load to weight ratio is more than 10 and favours group module device constructions up to 5 t load on permanent magnet (PM) track. A transportable and compact YBCO bulk magnet cooled with in-situ 4 Watt Stirling cryo-cooler for 50 - 80 K operation is investigated. Low cooling power and effective HTS cold mass drives the system construction to a minimum - thermal loss and light-weight design.

  4. Thermally actuated magnetization flux pump in single-grain YBCO bulk

    Energy Technology Data Exchange (ETDEWEB)

    Yan Yu; Li Quan; Coombs, T A, E-mail: yy300@cam.ac.u, E-mail: ql229@cam.ac.u, E-mail: tac1000@cam.ac.u [EPEC Superconductivity Group, Electrical Engineering Department, Cambridge University, 9 J J Thomson Avenue, Cambridge CB3 0FA (United Kingdom)

    2009-10-15

    Recent progress in material processing has proved that high temperature superconductors (HTS) have a great potential to trap large magnetic fields at cryogenic temperatures. For example, HTS are widely used in MRI scanners and in magnetic bearings. However, using traditional ways to magnetize, the YBCO will always need the applied field to be as high as the expected field on the superconductor or much higher than it, leading to a much higher cost than that of using permanent magnets. In this paper, we find a method of YBCO magnetization in liquid nitrogen that only requires the applied field to be at the level of a permanent magnet. Moreover, rather than applying a pulsed high current field on the YBCO, we use a thermally actuated material (gadolinium) as an intermedia and create a travelling magnetic field through it by changing the partial temperature so that the partial permeability is changed to build up the magnetization of the YBCO gradually after multiple pumps. The gadolinium bulk is located between the YBCO and the permanent magnet and is heated and cooled repeatedly from the outer surface to generate a travelling thermal wave inwards. In the subsequent experiment, an obvious accumulation of the flux density is detected on the surface of the YBCO bulk.

  5. Thermally actuated magnetization flux pump in single-grain YBCO bulk

    International Nuclear Information System (INIS)

    Yan Yu; Li Quan; Coombs, T A

    2009-01-01

    Recent progress in material processing has proved that high temperature superconductors (HTS) have a great potential to trap large magnetic fields at cryogenic temperatures. For example, HTS are widely used in MRI scanners and in magnetic bearings. However, using traditional ways to magnetize, the YBCO will always need the applied field to be as high as the expected field on the superconductor or much higher than it, leading to a much higher cost than that of using permanent magnets. In this paper, we find a method of YBCO magnetization in liquid nitrogen that only requires the applied field to be at the level of a permanent magnet. Moreover, rather than applying a pulsed high current field on the YBCO, we use a thermally actuated material (gadolinium) as an intermedia and create a travelling magnetic field through it by changing the partial temperature so that the partial permeability is changed to build up the magnetization of the YBCO gradually after multiple pumps. The gadolinium bulk is located between the YBCO and the permanent magnet and is heated and cooled repeatedly from the outer surface to generate a travelling thermal wave inwards. In the subsequent experiment, an obvious accumulation of the flux density is detected on the surface of the YBCO bulk.

  6. High temperature superconductor bulk materials. Fundamentals - processing - properties control - application aspects

    International Nuclear Information System (INIS)

    Krabbes, G.; Fuchs, G.; Canders, W.R.; May, H.; Palka, R.

    2006-01-01

    This book presents all the features of bulk high temperature superconducting materials. Starting from physical and chemical fundamentals, the authors move on to portray methods and problems of materials processing, thoroughly working out the characteristic properties of bulk superconductors in contrast to long conductors and films. The authors provide a wide range of specific materials characteristics with respect to the latest developments and future applications guiding from fundamentals to practical engineering examples. This book contains the following chapters: 1. Fundamentals 2. Growth and melt processing of YBCO 3. Pinning-relevant defects in bulk YBCO 4. Properties of bulk YBCO 5. Trapped fields 6. Improved YBCO based bulk superconductors and functional elements 7. Alternative systems 8. Peak effect 9. Very high trapped fields in YBCO permanent magnets 10. Engineering aspects: Field distribution in bulk HTSC 11. Inherently stable superconducting magnetic bearings 12. Application of bulk HTSCs in electromagnetic energy converters 13. Applications in magnet technologies and power supplies

  7. Mechanical and Magnetic Properties of YBCO Superconductor with Bi/CNT Composite and Resin/CNT Impregnation

    International Nuclear Information System (INIS)

    Oh, W. S.; Jang, G. E.; Han, Y. H.; Sung, T. H.

    2007-01-01

    Bi/CNT composite and resin/CNT were chosen to improve the mechanical properties of YBa 2 Cu 3 O 7 (YBCO) superconductor. In order to elucidate the effects of Bi/CNT composite and resin/CNT in YBCO superconductors, melt texture superconductor were impregnated by mixed compound of Bi and CNT into the artificial holes parallel to the c-axis, which were drilled on the YBCO superconductor. Various amount of Bi/CNT and resin/CNT were impregnated to YBCO superconductor with different holes diameters. Typical artificial holes diameters were 0.5, 0.7, and 1.0 mm respectively. Result of three-point bending test measurement, the bending strength with resin/CNT impregnation was improved up to 59.64 MPa as compared with 50.79 MPa of resin/CNT free bulk. Resin/CNT impregnation has been found to be one of the effective ways in improving the mechanical properties of bulk superconductor.

  8. Multiseeding with (100)/(100) Grain Junctions in Top Seeded Melt Growth Processed YBCO Superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Kim, C.J.; Gee, Y.A.; Hong, G.W. [Korea Atomic Energy Research Institute, Taejon (Korea); Kim, H.J.; Joo, J.H. [Sungkyunkwan University, Suwon (Korea); Han, S.C.; Han, Y.H.; Sung, T.H.; Kim, S.J. [Korea Electric Power Research Institute, Taejon (Korea)

    2000-06-01

    Multiseeding with (100)/(100) grain junctions of top-seeded melt growth (TSMG) processed YBCO superconductors was studied. Multiple seeding shortened the processing time for the fabrication of TSMG-processed YBCO superconductors. The relationship among the number of seeds, the levitation forces and the trapped magnetic fields of the TSMG-processed YBCO samples is reported. The characteristic of the (100)/(100) grain junction is discussed in terms of a wetting angle of a melt. (author). 25 refs., 7 figs.

  9. Surface flux density distribution characteristics of bulk high-Tc superconductor in external magnetic field

    International Nuclear Information System (INIS)

    Torii, S.; Yuasa, K.

    2004-01-01

    Various magnetic levitation systems using oxide superconductors are developed as strong pinning forces are obtained in melt-processed bulk. However, the trapped flux of superconductor is moved by flux creep and fluctuating magnetic field. Therefore, to examine the internal condition of superconductor, the authors measure the dynamic surface flux density distribution of YBCO bulk. Flux density measurement system has a structure with the air-core coil and the Hall sensors. Ten Hall sensors are arranged in series. The YBCO bulk, which has 25 mm diameter and 13 mm thickness, is field cooled by liquid nitrogen. After that, magnetic field is changed by the air-core coil. This paper describes about the measured results of flux density distribution of YBCO bulk in the various frequencies of air-core coils currents

  10. Surface flux density distribution characteristics of bulk high- Tc superconductor in external magnetic field

    Science.gov (United States)

    Torii, S.; Yuasa, K.

    2004-10-01

    Various magnetic levitation systems using oxide superconductors are developed as strong pinning forces are obtained in melt-processed bulk. However, the trapped flux of superconductor is moved by flux creep and fluctuating magnetic field. Therefore, to examine the internal condition of superconductor, the authors measure the dynamic surface flux density distribution of YBCO bulk. Flux density measurement system has a structure with the air-core coil and the Hall sensors. Ten Hall sensors are arranged in series. The YBCO bulk, which has 25 mm diameter and 13 mm thickness, is field cooled by liquid nitrogen. After that, magnetic field is changed by the air-core coil. This paper describes about the measured results of flux density distribution of YBCO bulk in the various frequencies of air-core coils currents.

  11. Modelling of bulk superconductor magnetization

    International Nuclear Information System (INIS)

    Ainslie, M D; Fujishiro, H

    2015-01-01

    This paper presents a topical review of the current state of the art in modelling the magnetization of bulk superconductors, including both (RE)BCO (where RE = rare earth or Y) and MgB 2 materials. Such modelling is a powerful tool to understand the physical mechanisms of their magnetization, to assist in interpretation of experimental results, and to predict the performance of practical bulk superconductor-based devices, which is particularly important as many superconducting applications head towards the commercialization stage of their development in the coming years. In addition to the analytical and numerical techniques currently used by researchers for modelling such materials, the commonly used practical techniques to magnetize bulk superconductors are summarized with a particular focus on pulsed field magnetization (PFM), which is promising as a compact, mobile and relatively inexpensive magnetizing technique. A number of numerical models developed to analyse the issues related to PFM and optimise the technique are described in detail, including understanding the dynamics of the magnetic flux penetration and the influence of material inhomogeneities, thermal properties, pulse duration, magnitude and shape, and the shape of the magnetization coil(s). The effect of externally applied magnetic fields in different configurations on the attenuation of the trapped field is also discussed. A number of novel and hybrid bulk superconductor structures are described, including improved thermal conductivity structures and ferromagnet–superconductor structures, which have been designed to overcome some of the issues related to bulk superconductors and their magnetization and enhance the intrinsic properties of bulk superconductors acting as trapped field magnets. Finally, the use of hollow bulk cylinders/tubes for shielding is analysed. (topical review)

  12. Zone refining of sintered, microwave-derived YBCO superconductors

    International Nuclear Information System (INIS)

    Warrier, K.G.K.; Varma, H.K.; Mani, T.V.; Damodaran, A.D.; Balachandran, U.

    1993-07-01

    Post-sintering treatments such as zone melting under thermal gradient has been conducted on sintered YBCO tape cast films. YBCO precursor powder was derived through decomposition of a mixture of nitrates of cations in a microwave oven for ∼4 min. The resulting powder was characterized and made into thin sheets by tape casting and then sintered at 945 C for 5 h. The sintered tapes were subjected to repeated zone refining operations at relatively high speeds of ∼30 mm/h. A microstructure having uniformly oriented grains in the a-b plane throughout the bulk of the sample was obtained by three repeated zone refining operations. Details of precursor preparation, microwave processing and its advantages, zone refining conditions, and microstructural features are presented in this paper

  13. The fabrication of YBCO superconductor polycrystalline powder by CCSO

    International Nuclear Information System (INIS)

    Martirosyan, K S; Luss, D; Galstyan, E; Xue, Y Y

    2008-01-01

    We present a novel, cost-effective and simple method to produce polycrystalline superconductor YBa 2 Cu 3 O 7-δ (YBCO) powder by a self-sustaining one-step process called carbon combustion synthesis of oxides (CCSO). In this process the exothermic oxidation of carbon nanoparticles generates a thermal wave that propagates at a velocity of about 1 mm s -1 through the solid yttrium, barium, and copper precursors, converting them rapidly (in the order of seconds) to polycrystalline YBCO. The carbon is not incorporated in the product and is emitted as carbon dioxide (CO 2 ) from the sample, generating a highly porous (∼70%) and friable product. Most of the grains have a plate-like shape, are well connected, and have a size of between 1 and 3 μm. The concentration of the residual carbon was less than 0.06 wt%. The magnetization of as-synthesized samples (without external post-annealing in oxygen), as determined by a SQUID magnetometer, showed an onset of the superconducting (SC) transition at ∼91 K, with a 44% shielding fraction of the -1/(4π) value

  14. Bulk YBCO seeded with 45°–45° bridge-seeds of different lengths

    International Nuclear Information System (INIS)

    Shi, Y-H; Durrell, J H; Dennis, A R; Cardwell, D A

    2013-01-01

    Single grain, (RE)BCO (rare earth–barium–copper oxide) bulk superconductors in large or complicated geometries are required for a variety of potential applications, such as in motors and generators and magnetic shielding devices. As a result, top, multi-seeded, melt growth has been investigated over the past 15 years in an attempt to enlarge the size of (RE)BCO single grains specifically for such applications. Of these multi-seeding techniques, so-called bridge-seeding provides the best alignment of two seeds in a single grain growth process. Here we report, for the first time, the successful growth of YBCO (yttrium–barium–copper oxide) using a special, 45°–45°, arrangement of bridge-seeds. The superconducting properties, including trapped field, of the multi-seeded YBCO grains have been measured for different bridge lengths of the 45°–45° bridge-seeds. The boundaries at the impinging growth front and the growth features of the top, multi-seeded surface and cross-section of the multi-seeded, samples have been analysed using optical microscopy. The results suggest that an impurity-free boundary between the two seeds of each leg of the bridge-seed can form when 45°–45° bridge-seeds are used to enlarge the size of YBCO grains. (paper)

  15. Progress in melt-texturing of YBCO superconductors

    International Nuclear Information System (INIS)

    Salama, K.; Lee, D.F.; Selvamanickam, V.

    1993-01-01

    Since the discovery of high temperature superconductors (HTS), tremendous efforts have been expanded toward the improvement of these materials. Due to the weak-link problem associated with grain boundaries, sintered bulk HTS possess a transport critical current density (J c ) on the order of 10 2 -10 3 A/cm 2 at 77 K. While these sintered superconductors may be utilized in low current applications, novel processing methods have to be developed to obtain HTS that can sustain high currents. Melt-texturing of HTS was found to result in a high degree of grain orientation, and is presently the most prominent processing method used to manufacture bulk YBa 2 Cu 3 O x (123) with superior transport and magnetic properties. In this review paper, various melt-texturing methods will be discussed, and the variation in J c with processing will be presented. (orig.)

  16. Preliminary experiments of a tubular linear actuator in the vertical direction using YBCO bulk

    Energy Technology Data Exchange (ETDEWEB)

    Sugawara, A; Ueda, H; Ishiyama, A [Department of Electrical Engineering and Bioscience, Waseda University, 3-4-1 Ohkubo, Shinjuku-ku, Tokyo 169-8555 (Japan)

    2004-05-01

    We have been developing a new type of active-maglev system composed of field-cooled disc-shaped YBCO bulk and multiple ring-shaped electromagnets, which are vertically piled up. One of the useful features of the active-maglev system is that the levitation height is adjustable by varying the operating current through an electromagnet. Maximum levitation height in stable levitation, however, is restricted by the magnetic field distribution produced by the electromagnet. To enhance the levitation height, we have fabricated and tested an active-maglev system with multiple ring-shaped electromagnets instead of using a larger single electromagnet. Up to now, we have reported the experimental results in a model active-maglev system composed of five electromagnets and showed that the levitation height, as well as stability, can be remarkably improved by adjusting the operating current of each electromagnet individually. In this study, we constructed a model system operated as a tubular linear synchronous actuator in the vertical direction in expectation of it being applied in factory automation upgrading. The primary consists of six ring-shaped copper-winding coils without iron core and is supplied with three-phase sinusoidal excitation. A disc-shaped YBCO bulk, which was magnetized by a field-cooling process, was adopted as a secondary (mover). We carried out preliminary experiments to confirm the feasibility of synchronous operation and also numerically investigated the electromagnetic phenomenon within the bulk superconductor by a developed computer program based on the finite element method.

  17. Preliminary experiments of a tubular linear actuator in the vertical direction using YBCO bulk

    International Nuclear Information System (INIS)

    Sugawara, A; Ueda, H; Ishiyama, A

    2004-01-01

    We have been developing a new type of active-maglev system composed of field-cooled disc-shaped YBCO bulk and multiple ring-shaped electromagnets, which are vertically piled up. One of the useful features of the active-maglev system is that the levitation height is adjustable by varying the operating current through an electromagnet. Maximum levitation height in stable levitation, however, is restricted by the magnetic field distribution produced by the electromagnet. To enhance the levitation height, we have fabricated and tested an active-maglev system with multiple ring-shaped electromagnets instead of using a larger single electromagnet. Up to now, we have reported the experimental results in a model active-maglev system composed of five electromagnets and showed that the levitation height, as well as stability, can be remarkably improved by adjusting the operating current of each electromagnet individually. In this study, we constructed a model system operated as a tubular linear synchronous actuator in the vertical direction in expectation of it being applied in factory automation upgrading. The primary consists of six ring-shaped copper-winding coils without iron core and is supplied with three-phase sinusoidal excitation. A disc-shaped YBCO bulk, which was magnetized by a field-cooling process, was adopted as a secondary (mover). We carried out preliminary experiments to confirm the feasibility of synchronous operation and also numerically investigated the electromagnetic phenomenon within the bulk superconductor by a developed computer program based on the finite element method

  18. Surface flux density distribution characteristics of bulk high-T{sub c} superconductor in external magnetic field

    Energy Technology Data Exchange (ETDEWEB)

    Torii, S.; Yuasa, K

    2004-10-01

    Various magnetic levitation systems using oxide superconductors are developed as strong pinning forces are obtained in melt-processed bulk. However, the trapped flux of superconductor is moved by flux creep and fluctuating magnetic field. Therefore, to examine the internal condition of superconductor, the authors measure the dynamic surface flux density distribution of YBCO bulk. Flux density measurement system has a structure with the air-core coil and the Hall sensors. Ten Hall sensors are arranged in series. The YBCO bulk, which has 25 mm diameter and 13 mm thickness, is field cooled by liquid nitrogen. After that, magnetic field is changed by the air-core coil. This paper describes about the measured results of flux density distribution of YBCO bulk in the various frequencies of air-core coils currents.

  19. Critical Current Properties in Longitudinal Magnetic Field of YBCO Superconductor with APC

    Science.gov (United States)

    Kido, R.; Kiuchi, M.; Otabe, E. S.; Matsushita, T.; Jha, A. K.; Matsumoto, K.

    The critical current density (Jc) properties of the Artificial Pinning Center (APC) introduced YBa2Cu3O7 (YBCO) films in the longitudinal magnetic field were measured. Y2O3 or Y2BaCuO5 (Y211) was introduced as APCs to YBCO, and YBCO films with APC were fabricated on SrTiO3 single crystal substrate. The sizes of Y2O3 and Y211 were 5-10 nm and 10-20 nm, respectively. As a result, Jc enhancement in the longitudinal magnetic field was observed in Y2O3 introduced YBCO films. However, it was not observed in Y211 introduced YBCO films. Therefore, it was considered that Jc properties in the longitudinal magnetic field were affected by introducing of small size APC, and it was necessary that APC does not disturb the current pathway in the superconductor.

  20. The homogeneity of levitation force in single domain YBCO bulk

    International Nuclear Information System (INIS)

    Zhou Keran; Xu Kexi; Wu Xingda; Pan Pengjun

    2007-01-01

    The pellet homogeneity of levitation force versus the position in comparison to the seed or to the top surface has been studied in the entire volume of a single domain YBa 2 Cu 3 O 7-δ bulk sample processed by the top-seeded melt texturing growth (TSMTG). It is found that the levitation forces increase and peak at a depth of 3 mm from the top of the sample at liquid nitrogen temperature. In other words, the second disk has the largest levitation force density. The phenomenon can be interpreted by the interaction between the microcracks or pores produced by crystal growth and the oxygenation. We propose a model in which Y211 particles distribution leading to microcracks and pores reduces the effective induced shielding current loops (ISCL) and increases the perimeters of ISCL. This corresponds to a decrease in the grain size and results in greatly reduced levitation forces of the bottom of the bulk. From the research, we know that the density of the YBCO bulk is also an important parameter for the levitation properties. The result is very attractive and useful for the fundamental studies and fabrication of TSMTG YBa 2 Cu 3 O 7-δ bulk

  1. The homogeneity of levitation force in single domain YBCO bulk

    Science.gov (United States)

    Zhou, Keran; Xu, Ke-Xi; Wu, Xing-da; Pan, Peng-jun

    2007-11-01

    The pellet homogeneity of levitation force versus the position in comparison to the seed or to the top surface has been studied in the entire volume of a single domain YBa 2Cu 3O 7-δ bulk sample processed by the top-seeded melt texturing growth (TSMTG). It is found that the levitation forces increase and peak at a depth of 3 mm from the top of the sample at liquid nitrogen temperature. In other words, the second disk has the largest levitation force density. The phenomenon can be interpreted by the interaction between the microcracks or pores produced by crystal growth and the oxygenation. We propose a model in which Y211 particles distribution leading to microcracks and pores reduces the effective induced shielding current loops (ISCL) and increases the perimeters of ISCL. This corresponds to a decrease in the grain size and results in greatly reduced levitation forces of the bottom of the bulk. From the research, we know that the density of the YBCO bulk is also an important parameter for the levitation properties. The result is very attractive and useful for the fundamental studies and fabrication of TSMTG YBa 2Cu 3O 7-δ bulk.

  2. Technique of Critical Current Density Measurement of Bulk Superconductor with Linear Extrapolation Method

    International Nuclear Information System (INIS)

    Adi, Wisnu Ari; Sukirman, Engkir; Winatapura, Didin S.

    2000-01-01

    Technique of critical current density measurement (Jc) of HTc bulk ceramic superconductor has been performed by using linear extrapolation with four-point probes method. The measurement of critical current density HTc bulk ceramic superconductor usually causes damage in contact resistance. In order to decrease this damage factor, we introduce extrapolation method. The extrapolating data show that the critical current density Jc for YBCO (123) and BSCCO (2212) at 77 K are 10,85(6) Amp.cm - 2 and 14,46(6) Amp.cm - 2, respectively. This technique is easier, simpler, and the use of the current flow is low, so it will not damage the contact resistance of the sample. We expect that the method can give a better solution for bulk superconductor application. Key words. : superconductor, critical temperature, and critical current density

  3. Force measurements for levitated bulk superconductors

    International Nuclear Information System (INIS)

    Tachi, Y.; Sawa, K.; Iwasa, Y.; Nagashima, K.; Otani, T.; Miyamoto, T.; Tomita, M.; Murakami, M.

    2000-01-01

    We have developed a force measurement system which enables us to directly measure the levitation force of levitated bulk superconductors. Experimental data of the levitation forces were compared with the results of numerical simulation based on the levitation model that we deduced in our previous paper. They were in fairly good agreement, which confirms that our levitation model can be applied to the force analyses for levitated bulk superconductors. (author)

  4. Force measurements for levitated bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Tachi, Y. [Department of Electrical Engineering, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama (Japan); ISTEC, Superconductivity Research Laboratory, 1-16-25 Shibaura, Minato-ku, Tokyo (Japan). E-mail: tachi at istec.or.jp; Uemura, N. [Department of Electrical Engineering, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama (Japan); ISTEC, Superconductivity Research Laboratory, 1-16-25 Shibaura, Minato-ku, Tokyo (Japan); Sawa, K. [Department of Electrical Engineering, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama (Japan); Iwasa, Y. [Francis Bitter Magnet Laboratory, Massachusetts Institute of Technology, Cambridge, MA (United States); Nagashima, K. [Railway Technical Research Institute, Hikari-cho, Kokubunji-shi, Tokyo (Japan); Otani, T.; Miyamoto, T.; Tomita, M.; Murakami, M. [ISTEC, Superconductivity Research Laboratory, 1-16-25 Shibaura, Minato-ku, Tokyo (Japan)

    2000-06-01

    We have developed a force measurement system which enables us to directly measure the levitation force of levitated bulk superconductors. Experimental data of the levitation forces were compared with the results of numerical simulation based on the levitation model that we deduced in our previous paper. They were in fairly good agreement, which confirms that our levitation model can be applied to the force analyses for levitated bulk superconductors. (author)

  5. Development of YBCO Superconductor for Electric Systems: Cooperative Research and Development Final Report, CRADA Number CRD-04-150

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharya, R.

    2013-03-01

    The proposed project will be collaborative in exploration of high temperature superconductor oxide films between SuperPower, Inc. and the National Renewable Energy Laboratory. This CRADA will attempt to develop YBCO based high temperature oxide technology.

  6. The magnetoresistance of YBCO/BZO composite superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Malik, Bilal A. [Department of Physics, University of Kashmir, Srinagar- 190006 (India); Asokan, K. [Materials Science Division, Inter University Accelerator Centre, New Delhi -110067 (India); Ganesan, V; Singh, Durgesh [UGC-DAE Consortium for Scientific Research, Khandwa Road, Indore (MP) 452 001 (India); Malik, Manzoor A., E-mail: mmalik@kashmiruniversity.ac.in [Department of Physics, University of Kashmir, Srinagar- 190006 (India)

    2016-12-15

    Highlights: • Limited addition of BZO in YBCO shows low resistive tailing behavior. • Limited addition of BZO in YBCO increases the activation energy of flux lines. • Vortex glass transition temperature increases with the limited addition of BZO. • Significant enhancement of H{sub C2}(0) is observed up to 4% BZO addition. - Abstract: We study the effect of addition of BaZrO{sub 3} (BZO) on normal and superconducting state of YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO). We find that in general both room temperature and residual resistivity increase with the addition of BZO except at low concentration of BZO. The temperature dependence of resistivity in presence of magnetic field also shows less resistivity broadening in composites containing low concentration of BZO below transition temperature (T{sub C}). The zero temperature upper critical field (H{sub c2}(0)), estimated by using Werthamer, Helfand and Hohenberg theory and Ginzburg Landau theory, shows an increase by the finite addition of BZO in YBCO. Further, the activation energy (U{sub 0}) determined from Arrhenius plots and vortex glass transition temperature (T{sub g}) also increase with the limited addition of BZO. Such an enhancement in H{sub c2}(0), U{sub o} and T{sub g} has been attributed to the increase in grain connectivity of YBCO . We conclude that the limited addition of BZO in YBCO significantly improves its superconducting performance in magnetic environment.

  7. Preparation of Superconductor YBCO-123/Ag Composite Through Urea Molten Salt

    International Nuclear Information System (INIS)

    Yustinus, P.; Indra-Gunawan; Wuryanto

    1996-01-01

    Superconductor YBCO-123/Ag composite has been prepared through Urea molten salt by mixing salt nitrate of Yttrium, Barium, Copper and Silver. The weight of Silver content varied from 0 % - 50 %. After pyrolysis process the powder was subjected to calcination at 300, 500 and 700 o C subsequently for 1 hour. The calcined powders was pelletized into a disk of 1.0 cm in diameter and thickness of 2-3 mm. Sintering of pellet samples was done at 900 o C for 16 hours. Meissner effect on all samples displayed superconductivity phenomena. Samples were examined by XRD, SEM, measurement of critical temperature by using susceptibility magnet vs temperature, and critical current density measurement by using four point probe. Based on orthorhombic structure of YBCO-123 the result of the lattice crystal calculation were is a = 3.8167 - 3.8241 A o ; b = 3.8561 - 3.8895 A o and c = 11.6518 - 11.7104 A o , this showed that silver did not influence the structure of YBCO. Superconductor YBCO-123/Ag composite was prepared. This was proved by critical current density. Jc data which showed increased with increasing of silver content and the highest result was 9.71 x 10 5 Amp/m 2

  8. FLUX PINNING EFFECTS IN Ag-DOPED YBCO (123 SUPERCONDUCTOR

    Directory of Open Access Journals (Sweden)

    Madelen Pérez

    2010-07-01

    Full Text Available Polycrystalline samples of Ag+-doped YBCO (123 (YBa2 (Cu1-xAgx3O7-δwith 0≤x≤0.3 were produced by solid state reaction method. The Ag- doped YBCO samples showed higher critical current densities (Jc with a Jc maximum for samples doped with x=0.05. This behavior can be assigned to an increase of pinning forces. The irreversibility temperature (Tirr, also increased in doped samples as a function of Ag content, with the highest temperature for the sample doped with x=0.05, wich correlates well with the observed Jc increasing. However, samples doped with x>0.05 displayed a decreasing of electrical properties (less Tirr, less Jc, etc. atributed to an excess of Ag in the grain boundaries which, reduces the grain sizes and increases the number of weak- links.

  9. Levitation performance of YBCO bulk in different applied magnetic fields

    International Nuclear Information System (INIS)

    Liu, W.; Wang, S.Y.; Jing, H.; Zheng, J.; Jiang, M.; Wang, J.S.

    2008-01-01

    The maglev performance of bulk high-T c superconductor (HTS) is investigated above three different types of permanent magnet guideways (PMGs). The main difference among these PMGs is the method used to concentrate the magnetic flux. The experimental results indicate that the levitation force depends only in part on the peak value of the magnetic field. The variation of the vertical component of the magnetic field (B z ), and the structure of the magnetic field are also responsible for the levitation force. These results imply that the permanent magnet with high coercive force is better at concentrating flux th an iron. The conclusions contribute in a very helpful way to the design and optimization of PMGs for HTS maglev systems

  10. Levitation performance of YBCO bulk in different applied magnetic fields

    Energy Technology Data Exchange (ETDEWEB)

    Liu, W. [Applied Superconductivity Laboratory, Southwest Jiaotong University, Chengdu 610031 (China)], E-mail: asclab@asclab.cn; Wang, S.Y.; Jing, H.; Zheng, J.; Jiang, M.; Wang, J.S. [Applied Superconductivity Laboratory, Southwest Jiaotong University, Chengdu 610031 (China)

    2008-07-01

    The maglev performance of bulk high-T{sub c} superconductor (HTS) is investigated above three different types of permanent magnet guideways (PMGs). The main difference among these PMGs is the method used to concentrate the magnetic flux. The experimental results indicate that the levitation force depends only in part on the peak value of the magnetic field. The variation of the vertical component of the magnetic field (B{sub z}), and the structure of the magnetic field are also responsible for the levitation force. These results imply that the permanent magnet with high coercive force is better at concentrating flux th an iron. The conclusions contribute in a very helpful way to the design and optimization of PMGs for HTS maglev systems.

  11. Improving superconducting properties of YBCO high temperature superconductor by Graphene Oxide doping

    Energy Technology Data Exchange (ETDEWEB)

    Dadras, S., E-mail: dadras@alzahra.ac.ir; Dehghani, S.; Davoudiniya, M.; Falahati, S.

    2017-06-01

    In this research, we report the synthesis and characterization of YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) high temperature superconductor prepared by sol-gel method and doped with Graphene Oxide (GO) in different weight percentages, 0, 0.1, 0.7 and 1 % wt. The x-ray diffraction (XRD) analysis confirms the formation of orthorhombic phase of superconductivity for all the prepared samples. We found that GO doping reduces the crystalline size of the samples. We evaluated the effects of GO doping on the normal state resistivity (ρ), superconducting transition temperature (T{sub c}) and critical current density (J{sub c}). The results show that the GO doping has a positive effect on these properties. Also, the highest J{sub c} is obtained for the 0.7 %wt GO doped YBCO compound that its critical current density is about 15 times more than the J{sub c} of pure one in 0.4 T magnetic field. The scanning electron microscope (SEM) analysis shows that there are better connections between the grains of GO doped samples. - Highlights: • Graphene Oxide doping increased the YBCO critical current density. • Graphene Oxide creates a better connection between the YBCO grains. • The normal resistivity of samples were decreased by GO doping to YBCO compounds. • Graphene Oxide doping has a positive effect on the critical transition temperature.

  12. Nonequilibrium states of high tc YBCO superconductors under tunnel injection of quasiparticles

    International Nuclear Information System (INIS)

    Iguchi, I.; Wang, Q.; Lee, K.; Yoshida, K.

    1995-01-01

    The nonequilibrium states of high Tc superconductors are investigated by means of tunnel injection of quasiparticles using Pb(or Au)/MgO/YBCO tunnel junctions. The effective critical-current reduction due to tunnel injection is observed, whose behaviour is different from simple heating. The observed results suggest that the resultant nonequilibrium states may also differ from those described by conventional nonequilibrium models

  13. Raman spectra, microstructure and superconducting properties of Sb(III)-YBCO composite superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Elsabawy, Khaled M. [Chemistry Department, Faculty of Science, Tanta University, Tanta (Egypt)]. E-mail: ksabawy@yahoo.com

    2005-11-15

    The pure YBCO (YBa{sub 2}Cu{sub 3}O{sub 7}) and its variant antimony containing composites with general formula; Y{sub 1+x}Sb {sub x}Ba{sub 2}Cu{sub 3}O {sub z}, where x = 0.1, 0.2, 0.4 and 0.6 mol%, respectively, were prepared by the solid-state reaction route. X-ray measurements indicated that Sb{sup 3+} ions have a negligible effect on the main crystalline structure and substitutes Y-sites successfully in lattice structure of 123-YBCO at low concentrations of doping (x = 0.1 {sup {yields}} 0.2). From SE-microscopy mapping and EDX elemental analysis, Sb{sup 3+} was detected qualitatively with good approximation to the actual molar ratio but not observed at 123-YBCO grain boundaries which confirm that antimony (III) has diffused regularly into material bulk of superconducting 123-YBCO-phase at low concentrations. Additions of Sb(III) affected sharply on the main vibrating modes of YBCO regime particularly, on the apical oxygen (O{sub 4}) vibrational mode A {sub 1g}. Magnetic susceptibility measurements proved that antimony oxide additions have slight effect on the transport properties of YBCO-composites regime.

  14. Surface flux density distribution characteristics of bulk high-T c superconductor in external magnetic field

    International Nuclear Information System (INIS)

    Nishikawa, H.; Torii, S.; Yuasa, K.

    2005-01-01

    This paper describes the measured results of the two-dimensional flux density distribution of a YBCO bulk under applied AC magnetic fields with various frequency. Melt-processed oxide superconductors have been developed in order to obtain strong pinning forces. Various electric mechanical systems or magnetic levitation systems use those superconductors. The major problem is that cracks occur because the bulk superconductors are brittle. The bulk may break in magnetizing process after cracks make superconducting state instable. The trapped flux density and the permanent current characteristics of bulk superconductors have been analyzed, so as to examine the magnetizing processes or superconducting states of the bulk. In those studies, the two-dimensional surface flux density distributions of the bulk in static fields are discussed. On the other hand, the distributions in dynamic fields are little discussed. We attempted to examine the states of the bulk in the dynamic fields, and made a unique experimental device which has movable sensors synchronized with AC applied fields. As a result, the two-dimensional distributions in the dynamic fields are acquired by recombining the one-dimensional distributions. The dynamic states of the flux of the bulk and the influences of directions of cracks are observed from the distributions. In addition, a new method for measuring two-dimensional flux density distribution under dynamic magnetic fields is suggested

  15. Development of fabrication technique of bulk high superconductor

    International Nuclear Information System (INIS)

    Hong, Gye Won; Kim, Chang Joong; Kim, Ki Baik; Lee, Ho Jin; Lee, Hee Gyoun; Kwon, Sun Chil.

    1997-05-01

    In order to realize the commercial application of HTSC materials, it is necessary to develop the fabrication process of high Tc oxide superconductor materials with desired shape and for practical application and high critical current density as well as good mechanical strength which critical current density as well as good mechanical strength which can withstand high lorenz force generated at high magnetic field. Much studies have been concentrated to develop the fabrication technique for high critical current density but still there are a lot of gap which should be overcome for large scale application of HTSC materials at liquid nitrogen temperature. Recently some new fabrication techniques have been developed for YBCO bulk superconductor with high mechanical strength and critical current density. In this project, plastic extrusion and melt process techniques were studied. The components materials for the current lead and the flywheel application were fabricated and their characteristics were investigated from the view point of microstructure and phase formation during heat treatment process. (author). 64 refs., 59 figs

  16. Interaction of ultra soft magnetic materials with the high-T{sub c} superconductor YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Stahl, Claudia; Treiber, Sebastian; Schuetz, Gisela [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Walker, Patrick [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Albrecht, Joachim [Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2013-07-01

    We have grown bilayers of optimally doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) and ferromagnetic CoFeB on single-crystalline substrates by pulsed laser deposition and sputtering. These heterostructures are typically composed of about 100 nm YBCO and several 10 nm of CoFeB. Regarding the superconductor, the properties of the YBCO film change as a consequence of the vicinity of the ferromagnet. In detail we investigated the critical current density as a function of temperature, applied field and time as well as the transition temperature by SQUID magnetization measurements and quantitative magneto-optical measurements. The amorphous material CoFeB exhibits an in plane anisotropy and a very low coercivity. From magneto-optical images we find that the flux line lattice of the superconductor is mapped into the magnet and still visible as significant magnetic out-of-plane contrast at room temperature. We discuss this phenomenon as a new route to high-resolution mapping of the flux line distribution on a nanometer scale.

  17. Role of oxygen partial pressure in microstructural development and properties of YBCO superconductors

    International Nuclear Information System (INIS)

    Singh, J.P.; Guttschow, R.; Dusek, J.T.; Poeppel, R.B.

    1991-01-01

    Results are presented for the effect of oxygen partial pressure (pO 2 ) on the sintered density and microstructure of YBCO superconductors. Extruded YBCO wires were sintered at 910C at different values of pO 2 . Generally, the density increased with decreasing pO 2 , and a density of 91% was achieved at pO 2 = 0.01 atm. Wires sintered at pO 2 = 0.01 atm had a fine microstructure with an average grain size of ∼3 μm and an average strength of 191 MPa. The high strength is due to the small grain size, which causes a decrease in residual tensile stress because of grain anisotropy

  18. Levitation force of melt-textured YBCO superconductors under non-quasi-static situation

    Science.gov (United States)

    Zhao, Z. M.; Xu, J. M.; Yuan, X. Y.; Zhang, C. P.

    2018-06-01

    The superconducting levitation force of a simple superconductor-magnet system under non-quasi-static situation is investigated experimentally. Two yttrium barium copper oxide (YBCO) samples with different performances are chosen from two small batches of samples prepared by the top-seeded melt-textured growth process. The residual carbon content of the precursor powders of the two batches is different due to different heat treatment processes. During the experimental process for measuring the levitation force, the value of the relative speed between the YBCO sample and the permanent magnet is higher than that in conventional studies. The variation characteristics of the superconducting levitation force are analyzed and a crossing phenomenon in the force-displacement hysteresis curves is observed. The results indicate that the superconducting levitation force is different due to the different residual carbon contents. As residual carbon contents reduce, the crossing phenomenon is more obvious accordingly.

  19. Applications of YBCO melt textured bulks in Maglev technology

    International Nuclear Information System (INIS)

    Zhao, Y.; Wang, J.S.; Wang, S.Y.; Ren, Z.Y.; Song, H.H.; Wang, X.R.; Cheng, C.H.

    2004-01-01

    In this paper we report the present status and progress of HTS Maglev project undertaken at the Southwest Jiaotong University. The efforts and results towards solving the material-related issues in HTS Maglev system are emphasized, including the levitation and guidance forces, the magnetic and thermal stabilities related to the ac loss of YBCO superconducting material during a high speed movement, and the low stiffness of HTS Maglev system

  20. Superconductors, analysis and applications, with special reference to the utilisation of bulk (Re)BCO materials

    Energy Technology Data Exchange (ETDEWEB)

    Coombs, T.A., E-mail: tac1000@cam.ac.u [University of Cambridge, Department of Engineering, Trumpington Street, Cambridge CB2 1PZ (United Kingdom)

    2010-11-01

    The Electrical Power and Energy Conversion (EPEC) superconductivity group at Cambridge University has been working on the application of superconductivity to large scale devices. This work is taking place over a range of areas which cover FCLs, motors and generators, SMES, accelerator magnets and MRI. The research is underpinned by advanced modelling techniques using both pure Critical State models and E-J models to analyse the behaviour of the superconductors. As part of the device design we are concentrating on the analysis of AC losses in complicated geometries such as are found in motor windings and the magnetisation of bulk superconductors to enable their full potential to be realised. We are interested in the full range of high-temperature superconductors and have measured and predicted the performance of YBCO, MgB{sub 2} and BSCCO at a range of temperatures and in wire, tape and bulk forms. This paper concentrates on recent work which includes: modelling of coils using formulations based on H and A. A critical state model for the analysis of coils in SMES; crossed field effects in bulk superconductors; a magnetic model together with experimental results which explain and describe the method of flux pumping whereby a bulk superconductor can be magnetised to a high flux density using a repeatedly applied field of low flux density and finally a new configuration for MRI magnets

  1. Development of a 20kA current feedthrough using YBCO bulk conductors

    International Nuclear Information System (INIS)

    Maehata, Keisuke; Ishibashi, Kenji; Shintomi, Takakazu; Iwamoto, Akifumi; Maekawa, Ryuji; Mito, Toshiyuki

    2004-01-01

    In the phase II experiment of the Large Helical Device (LHD) of the National Institute for Fusion Science (NIFS), it is planned to operate the helical coils at 1.8 K by employing pressurized superfluid cooling to raise the magnetic field to 4 T with 17.3 kA. It is important to develop a 20kA-class current feedthrough into the 1.8 K region, but it must have a high current capacity and low heat leakage in the maximum magnetic leakage field of 1 T. Rectangle-shaped YBCO bulk conductors measuring 20 mm wide, 140 mm long and 10 mm thick were manufactured from square-pillar-shaped YBCO bulk materials for a 20 kA current. To check the quality of the bulk conductors, internal defects or cracks were detected by carrying out a precise survey of trapped magnetic flux. An assembled 20 kA current feedthrough was mounted in the λ-plate of a pressurized superfluid cooling cryostat. Experiments of current feeding into the 1.8 K region were carried out by operating the 20 kA current feedthrough. In the experiments, the transport current was kept at 20 kA for longer than 1,200 s. During the 20 kA operation, the current transport section of the YBCO bulk conductors remained in the superconducting state and the voltage drop between the YBCO bulk conductors and the copper electrode was observed to be constant. A contact resistance and the Joule heat generation in the joint region between the YBCO bulk conductors and the copper electrode were obtained as 1.45 nΩ and 0.72 W, respectively in the 20 kA operation. We have demonstrated the feasibility of using a 20 kA current feedthrough for the phase II experiment of the LHD. (author)

  2. Influence of grain boundary connectivity on the trapped magnetic flux of multi-seeded bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Z., E-mail: zgdeng@gmail.com [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology, Tokyo 135-8533 (Japan); Miki, M.; Felder, B.; Tsuzuki, K.; Shinohara, N.; Hara, S.; Uetake, T.; Izumi, M. [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology, Tokyo 135-8533 (Japan)

    2011-09-15

    Four different performance multi-seeded YBCO bulks as representatives. A coupling ratio to reflect the coupling quality of GBs inside multi-seeded bulks. An averaged trapped magnetic flux density parameter was introduced. The top-seeded melt-growth process with multi-seeding technique provides a promising way to fabricate large-sized bulk superconductors in an economical way. To understand the essential characteristics of the multi-seeded bulks, the paper reports the influence of the grain boundary (GB) coupling or connectivity on the total trapped magnetic flux. The coupling ratio, the lowest trapped flux density in the GB area to the averaged top value of the two neighboring peak trapped fields, is introduced to reflect the coupling quality of GBs inside a multi-seeded bulk. By the trapped flux density measurement of four different performance multi-seeded YBCO bulk samples as representatives, it was found that the GB coupling plays an important role for the improvement of the total trapped magnetic flux; moreover, somewhat more significant than the widely used parameter of the peak trapped fields to evaluate the physical performance of bulk samples. This characteristic is different with the case of the well-grown single-grain bulks.

  3. Effect of Au nano-particles doping on polycrystalline YBCO high temperature superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Dadras, Sedigheh, E-mail: dadras@alzahra.ac.ir; Gharehgazloo, Zahra

    2016-07-01

    In this research, we prepared different Au nanoparticles (0.1–2 wt%) doped YBCO high temperature superconductor samples by sol-gel method. To characterize the samples, we used X-Ray diffraction (XRD) and scanning electron microscope (SEM) analysis. Results show the formation of orthorhombic phase of superconductivity for all prepared samples. We observed that by adding Au nanoparticles, the grains' size of the samples reduces from 76 nm to 47 nm as well. The critical current density (J{sub c}) and transition temperature (T{sub c}) were determined using current versus voltage (I–V) and resistivity versus temperature (ρ-T) measurements, respectively. We found that by increasing Au nanoparticles in the compound, in comparison to the pure YBCO sample, the transition temperature, pinning energy and critical current density will increase. Also, the highest J{sub c} is for 1 wt% Au doped YBCO compound that its critical current density is about 8 times more than the J{sub c} of pure one in 0.7 T magnetic field.

  4. Growth and characterization of bulk superconductor material

    CERN Document Server

    Chen, Dapeng; Maljuk, Andrey; Zhou, Fang

    2016-01-01

    This book focuses on recently developed crystal growth techniques to grow large and high quality superconducting single crystals. The techniques applied are traveling solvent floating zone (TSFZ) with infrared image furnace, Bridgeman, solution/flux and top seeded solution growth (TSSG) methods. The materials range from cuprates, cobaltates to pnictides including La2CuO4-based (LCO), YBa2Cu3O7-d (YBCO), Bi2Sr2Can−1CunO2n+4+δ (n=1,2,3) (BSCCO) to NaxCoO2. The modified Bridgman “cold finger” method is devoted to the pnictide system with the best quality (transition width DTc~0.5 K) with highest Tc~38.5 K of Ba0.68K0.32Fe2A2. The book presents various iron-based superconductors with different structures, such as 1111, 122, 111, 11 and 42622,10-3-8. Detailed single crystal growth methods (fluxes, Bridgman, floating zone), the associated procedures and their impact to crystal size and quality are presented. The book also describes the influence of doping on the structure and the electric, magnetic, and supe...

  5. Gap-related trapped magnetic flux dependence between single and combined bulk superconductors

    International Nuclear Information System (INIS)

    Deng, Z.; Miki, M.; Felder, B.; Tsuzuki, K.; Shinohara, N.; Uetake, T.; Izumi, M.

    2011-01-01

    Highlights: → Rectangular YBCO bulks to realize a compact combination. → The gap effect was added to consider in the trapped flux density mapping. → The trapped-flux dependence between single and combined bulks is gap related. → It is possible to estimate the total magnetic flux of bulk combinations. - Abstract: Aiming at examining the trapped-flux dependence between single and combined bulk superconductors for field-pole applications, three rectangular Y 1.65 Ba 2 Cu 3 O 7-x (YBCO) bulks with a possibly compact combination were employed to investigate the trapped-flux characteristics of single and combined bulks with a field-cooling magnetization (FCM) method. A gap-related dependence was found between them. At lower gaps of 1 mm and 5 mm, the peak trapped fields and total magnetic flux of combined bulks are both smaller than the additive values of each single bulk, which can be ascribed to the demagnetization influences of the field around the bulk generated by the adjacent ones. While, at larger gaps like 10 mm, the situation becomes reversed. The combined bulks can attain bigger peak trapped fields as well as total magnetic flux, which indicates that the magnetic field by the bulk combination can reach higher gaps, thanks to the bigger magnetic energy compared with the single bulk. The presented results show that, on one hand, it is possible to estimate the total trapped magnetic flux of combined bulks by an approximate additive method of each single bulk while considering a demagnetization factor; on the other hand, it also means that the performance of combined bulks will be superior to the addition of each single bulk at larger gaps, thus preferable for large-scaled magnet applications.

  6. Gap-related trapped magnetic flux dependence between single and combined bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Z., E-mail: zgdeng@gmail.co [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology, Tokyo 135-8533 (Japan); Miki, M.; Felder, B.; Tsuzuki, K.; Shinohara, N.; Uetake, T.; Izumi, M. [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology, Tokyo 135-8533 (Japan)

    2011-05-15

    Highlights: {yields} Rectangular YBCO bulks to realize a compact combination. {yields} The gap effect was added to consider in the trapped flux density mapping. {yields} The trapped-flux dependence between single and combined bulks is gap related. {yields} It is possible to estimate the total magnetic flux of bulk combinations. - Abstract: Aiming at examining the trapped-flux dependence between single and combined bulk superconductors for field-pole applications, three rectangular Y{sub 1.65}Ba{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) bulks with a possibly compact combination were employed to investigate the trapped-flux characteristics of single and combined bulks with a field-cooling magnetization (FCM) method. A gap-related dependence was found between them. At lower gaps of 1 mm and 5 mm, the peak trapped fields and total magnetic flux of combined bulks are both smaller than the additive values of each single bulk, which can be ascribed to the demagnetization influences of the field around the bulk generated by the adjacent ones. While, at larger gaps like 10 mm, the situation becomes reversed. The combined bulks can attain bigger peak trapped fields as well as total magnetic flux, which indicates that the magnetic field by the bulk combination can reach higher gaps, thanks to the bigger magnetic energy compared with the single bulk. The presented results show that, on one hand, it is possible to estimate the total trapped magnetic flux of combined bulks by an approximate additive method of each single bulk while considering a demagnetization factor; on the other hand, it also means that the performance of combined bulks will be superior to the addition of each single bulk at larger gaps, thus preferable for large-scaled magnet applications.

  7. Gap-related trapped magnetic flux dependence between single and combined bulk superconductors

    Science.gov (United States)

    Deng, Z.; Miki, M.; Felder, B.; Tsuzuki, K.; Shinohara, N.; Uetake, T.; Izumi, M.

    2011-05-01

    Aiming at examining the trapped-flux dependence between single and combined bulk superconductors for field-pole applications, three rectangular Y 1.65Ba 2Cu 3O 7-x (YBCO) bulks with a possibly compact combination were employed to investigate the trapped-flux characteristics of single and combined bulks with a field-cooling magnetization (FCM) method. A gap-related dependence was found between them. At lower gaps of 1 mm and 5 mm, the peak trapped fields and total magnetic flux of combined bulks are both smaller than the additive values of each single bulk, which can be ascribed to the demagnetization influences of the field around the bulk generated by the adjacent ones. While, at larger gaps like 10 mm, the situation becomes reversed. The combined bulks can attain bigger peak trapped fields as well as total magnetic flux, which indicates that the magnetic field by the bulk combination can reach higher gaps, thanks to the bigger magnetic energy compared with the single bulk. The presented results show that, on one hand, it is possible to estimate the total trapped magnetic flux of combined bulks by an approximate additive method of each single bulk while considering a demagnetization factor; on the other hand, it also means that the performance of combined bulks will be superior to the addition of each single bulk at larger gaps, thus preferable for large-scaled magnet applications.

  8. Fiber Bragg grating based spatially resolved characterization of flux-pinning induced strain of rectangular-shaped bulk YBCO samples

    International Nuclear Information System (INIS)

    Latka, Ines; Habisreuther, Tobias; Litzkendorf, Doris

    2011-01-01

    Highlights: → Fiber Bragg gratings (FBG) act as strain sensors, also at cryogenic temperatures. → FBGs are not sensitive to magnetic fields. → Local, shape dependent magnetostriction was detected on rectangular samples. → Magnetostrictive effects of the top surface and in a gap between two samples are different. - Abstract: We report on measurements of the spatially resolved characterization of flux-pinning induced strain of rectangular-shaped bulk YBCO samples. The spatially resolved strain measurements are accomplished by the use 2 fiber Bragg grating arrays, which are with an included angle of 45 o fixed to the surface. In this paper first attempts to confirm the shape distortions caused by the flux-pinning induced strain as predicted in will be presented. Two sample setups, a single bulk and a 'mirror' arrangement, will be compared. This mirror setup represents a model configuration for a measurement inside the superconductor, where demagnetization effects can be neglected and the magnetic field merely has a z-component.

  9. Study of microstructure and electrical properties of bulk YBCO prepared by melt textured growth technique

    International Nuclear Information System (INIS)

    Gonal, M. R.; Krishnan, Madangopal; Tewari, R.; Tyagi, A. K.; Gyore, A.; Vajda, I.

    2015-01-01

    Bulk YBCO components were prepared using Melt Texture Growth (MTG) technique. Components were fabricated using MTG by addition of Y 2 BaCuO 5 (Y211) and Ag to YBCO, which leads to improved grain size without affecting superconducting properties. Green compacts prepared by cold isostatic pressing were pre-sintered at 930°C before subjecting melt texturing. Cooling rates lower than 1 °C.h −1 was used, in between (peritectic) temperature of about 995 and 1025°C, to obtain large grained components. Microstructure studies in details were carried out by Scanning Electron Microscope (SEM), Electron Probe Micro Analysis (EPMA), Orientation Imaging Microscope (OIM) and TEM correlated with electrical properties like Critical current density (J c )

  10. Mechanical reliability of bulk high Tc superconductors

    International Nuclear Information System (INIS)

    Freiman, S.W.

    1990-01-01

    Most prospective applications for high T c superconductors in bulk form, e.g. magnets, motors, will require appreciable mechanical strength. Work at NIST [National Institute of Standards and Technology] has begun to address issues related to mechanical reliability. For example, recent studies on Ba-Y-Cu-O have shown that the intrinsic crack growth resistance, K IC , of crystals of this material is even smaller than was first reported, less than that of window glass, and is sensitive to moisture. Processing conditions, particularly sintering and annealing atmosphere, have been shown to have a major influence on microstructure and internal stresses in the material. Large internal stresses result from the tetragonal to orthorhombic phase transformation as well as the thermal expansion anisotropy in the grains of the ceramic. Because stress relief is absent, microcracks form which have a profound influence on strength

  11. SmBa2NbO6 Nanopowders, an Effective Percolation Network Medium for YBCO Superconductors

    Directory of Open Access Journals (Sweden)

    S. Vidya

    2013-01-01

    Full Text Available The percolation behavior of superconductor-insulator composite, YBa2Cu3O7–δ, and nano SmBa2NbO2 synthesized by modified combustion technique was studied. Particle size of nano SmBa2NBO6 was determined using transmission electron microscopy. The chemical nonreactivity of nano SmBa2NbO6 with YBCO is evident from the X-Ray diffraction study which makes it a suitable nanoceramic substrate material for high temperature superconducting films. A systematic increase in the sintered density, approaching the optimum value of the insulating nanophase is clearly observed, as the vol.% of YBCO in the composite decreases. SEM micrograph showed uniform distribution of nanopowder among the large clusters of YBCO. The obtained percolation threshold is ~26 vol% of YBCO in the composite. All the composites below the threshold value showed TC(0~92 K even though the room resistivity increases with increase in vol.% of nano SmBa2NbO6. The values of critical exponents obtained matches well with the theoretically expected ones for an ideal superconductor-insulator system.

  12. Study of dependence upon the magnetic field and transport current of the magnetoresistive effect in YBCO-based bulk composites

    International Nuclear Information System (INIS)

    Balaev, D A; Prus, A G; Shaykhutdinov, K A; Gokhfeld, D M; Petrov, M I

    2007-01-01

    The magnetoresistive properties of bulk YBCO + CuO and YBCO+BaPb 0.75 Sn 0.25 O 3 composites for different orientations of external magnetic field H and macroscopic transport current j have been measured. These composites exhibit large magnetoresistance in weak magnetic fields ( 2 θ. This fact suggests that the flux flow in the intergrain boundaries is responsible for the large magnetoresistive effect observed in the composites

  13. Development of a generic seed crystal for the fabrication of large grain (RE)-Ba-Cu-O bulk superconductors

    International Nuclear Information System (INIS)

    Shi, Y; Babu, N Hari; Cardwell, D A

    2005-01-01

    The critical current density, J c , irreversibility field, B irr , and magnetic field trapping ability of (LRE)-Ba-Cu-O bulk superconductors, where LRE is a light rare earth element such as Nd, Sm, Eu and Gd, are generally superior to those of the more common melt-processed Y-Ba-Cu-O (YBCO). The lack of availability of a suitable seed crystal to grow large, single grain (LRE)-Ba-Cu-O superconductors with controlled orientation, however, has hindered severely the development of these materials for engineering applications over the past ten years. In this communication we report for the first time the development of a generic seed crystal that can be used to fabricate any rare earth (RE) based (RE)-Ba-Cu-O ((RE)BCO) superconductor in the form of a large single grain with controlled orientation. The new seed crystal will potentially enable large grain (LRE)-Ba-Cu-O bulk superconductors to be fabricated routinely, as is the case for YBCO. This will enable the field trapping and current-carrying characteristics of these materials to be explored in more detail than has been possible to date. (rapid communication)

  14. Fault current limiter using bulk oxides superconductors

    International Nuclear Information System (INIS)

    Belmont, O.; Ferracci, P.; Porcar, L.; Barbut, J.M.; Tixador, P.; Noudem, J.G.; Bourgault, D.; Tournier, R.

    1998-01-01

    We study the limitation possibilities of bulk Bi high T c materials. For this we test these materials with AC or DC currents above their critical currents. We study particularly the evolution of the voltage with time or with current. The material, the value of the current and the time duration play important parts. For sintered Bi samples the voltage depends only on the current even for values much larger than the critical current. With textured samples the V(I) curves shows an hysteretic behaviour due to a warming up. The textured materials are more interesting than sintered ones in terms of required volume for the current limitation. In both cases the superconductors are in a dissipative state but not in the normal state. This state is nevertheless reached if the dissipated energy inside the sample is sufficient. We have tried to apply a magnetic field on the samples in order to trigger a more effective limitation. The voltage increases but with a limited effect for currents much higher (3-4 times) than the critical zero field current. We think that the dissipative state is due mainly to the grain boundaries which become resistive above the critical current. (orig.)

  15. Development of application technique of bulk high-Tc superconductor

    International Nuclear Information System (INIS)

    Hong, Kye Won; Kim, Chan Joong; Kim, Kee Baek; Kwon, Sun Chil; Won, Dong Yun; Lee, Hoh Jin; Lee, Heui Kyoon; Jang, Kun Ik; Yang, Suk Woo

    1995-03-01

    YBCO-Ag composite superconductors were prepared by extrusion using inorganic binder materials. In the case of the undoped 1-2-3 sample with a dia. of 2.5 mm, critical current density (Jc) was 150 A/cm 2 and current density (Ic) was 10 amps. In the case of the sample with a die. of 4.5 mm, meanwhile, Jc and Ic were 50 A/cm 2 and 32 amps, respectively. Influence of BaCeO 3 addition on magnetization characteristics of melt-textured Y-Ba-Cu-O superconductor was investigated. The variation of magnetization behavior due to the addition of BaCeO 3 is discussed on the basis of the related microstructures. 37 figs, 1 tab, 56 refs. (Author)

  16. Levitation and guidance force relaxations of the single-seeded and multi-seeded YBCO superconductors

    Science.gov (United States)

    Abdioglu, M.; Ozturk, K.; Kabaer, M.; Ekici, M.

    2018-01-01

    The stable levitation and guidance forces at higher force levels are important parameters for technological applicability of high temperature superconductors (HTSs) in Maglev and Flywheel energy storage systems. In this study, we have investigated the levitation and guidance force relaxation of both the single-seeded and multi-seeded YBCOs for different (HTS)-permanent magnetic guideway (PMG) arrangements in different cooling heights (CH). The measured saturated force values of Halbach PMG arrangements are bigger than the maximum force values of other PMGs. It is determined that the normalized magnetic levitation force (MLF) and normalized guidance force (GF) relaxation rate values decrease while the relaxation rates increase with increasing magnetic pole number and the effective external magnetic field area for both the single-seeded and multi-seeded YBCO. Also it can be said that the force stability at the higher force value of Halbach PMG arrangement indicates that the relaxation quality of Halbach PMG is better than that of the others. Additionally, it can be said that both the MLF and GF relaxation qualities of the multi-seeded YBCOs are better than that of the single-seeded ones. This magnetic force and relaxation results of the single-seeded and multi-seeded YBCOs are useful to optimize the loading capacity and lateral reliability of HTS Maglev and similar magnetic bearing systems.

  17. Grain alignment in bulk YBa2Cu3Ox superconductor by a low temperature phase transformation method

    International Nuclear Information System (INIS)

    Selvamanickam, V.; Goyal, A.; Kroeger, D.M.

    1994-01-01

    A quench and directional phase transformation process has been developed to achieve grain alignment in bulk YBa 2 Cu 3 O x superconductors at temperatures about 100 degree C below the peritectic temperature. Isothermal phase transformation of quenched precursors at 890 degree C for 3 min is found to result in the formation of more than 75% of YBa 2 Cu 3 O x phase without any formation of Y 2 BaCuO 5 . Phase transformation at higher temperatures leads to rapid formation of Y 2 BaCuO 5 in addition to YBa 2 Cu 3 O x . A well-aligned microstructure is achieved by directional phase transformation of the quenched compacts as a rate of 10 mm/h. The magnetic field dependence of the critical current density at 77 K of the directionally phase transformed material compares well with that of melt-textured YBCO and is superior to that of magnetically aligned and sintered YBCO

  18. Influence of grain boundary connectivity on the trapped magnetic flux of multi-seeded bulk superconductors

    Science.gov (United States)

    Deng, Z.; Miki, M.; Felder, B.; Tsuzuki, K.; Shinohara, N.; Hara, S.; Uetake, T.; Izumi, M.

    2011-09-01

    The top-seeded melt-growth process with multi-seeding technique provides a promising way to fabricate large-sized bulk superconductors in an economical way. To understand the essential characteristics of the multi-seeded bulks, the paper reports the influence of the grain boundary (GB) coupling or connectivity on the total trapped magnetic flux. The coupling ratio, the lowest trapped flux density in the GB area to the averaged top value of the two neighboring peak trapped fields, is introduced to reflect the coupling quality of GBs inside a multi-seeded bulk. By the trapped flux density measurement of four different performance multi-seeded YBCO bulk samples as representatives, it was found that the GB coupling plays an important role for the improvement of the total trapped magnetic flux; moreover, somewhat more significant than the widely used parameter of the peak trapped fields to evaluate the physical performance of bulk samples. This characteristic is different with the case of the well-grown single-grain bulks.

  19. Influence of Heat Treatments on Electrical Properties and Microstructure of 10 % Mass Fraction of Sucrose YBCO Superconductor

    International Nuclear Information System (INIS)

    Khalida Salleh; Fariesha, F.; Azhan, H.; Yusainee, S.Y.

    2013-01-01

    The influence of different heat treatments on the superconducting properties of 10 % mass fraction of sucrose structure YBCO superconductor was investigated. X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) equipment were used to determine the phase of superconductor and structural studies respectively at 10 % mass fraction of sucrose. The samples were prepared via solid state (SSM) and co-precipitation (CPM) reaction methods and underwent sintering and heat treatment process at 900, 930 and 960 degree Celsius respectively with mixing of C 12 H 22 O 11 sucrose during pelletization. The T C,on decreases with respect to higher heat treatment temperature. The suppression of both T C,on and T C,off indicates the destruction of superconductivity trends. The best T C,off were achieved in pure SSM and CPM samples sintered at 950 degree Celsius for 5 hours with T C,off 86 K and 91 K respectively. Comparing with pure YBCO, the 10 % mass fraction of sucrose YBCO exhibited higher critical current, I C by two times. It indicates the effect of high surface area in porous structure. The XRD results confirmed that all the samples remain in single phase, which indicates no effect of sucrose in the porous structures sample and maintaining in orthorhombic structure. Higher heat treatment at 960 degree Celsius resulted in destruction on its superconductivity behavior due to the partial melt phase on its microstructure, especially in CPM. This is due to the smaller grain size of samples which trapped more heat and causing partial melting to occur rapidly. It can be deduced that, annealing temperatures at 900 and 930 degree Celsius are the best optimum heat treatments for CPM and SSM porous superconductor, respectively. (author)

  20. Measurement of the magnetic field inside the holes of a drilled bulk high-Tc superconductor

    Science.gov (United States)

    Lousberg, Gregory P.; Fagnard, Jean-François; Noudem, Jacques G.; Ausloos, Marcel; Vanderheyden, Benoit; Vanderbemden, Philippe

    2009-04-01

    We use macroscopic holes drilled in a bulk YBCO superconductor to probe its magnetic properties in the volume of the sample. The sample is subjected to an AC magnetic flux with a density ranging from 30 to 130 mT and the flux in the superconductor is probed by miniature coils inserted in the holes. In a given hole, three different penetration regimes can be observed: (i) the shielded regime, where no magnetic flux threads the hole; (ii) the gradual penetration regime, where the waveform of the magnetic field has a clipped sine shape whose fundamental component scales with the applied field; and (iii) the flux concentration regime, where the waveform of the magnetic field is nearly a sine wave, with an amplitude exceeding that of the applied field by up to a factor of two. The distribution of the penetration regimes in the holes is compared with that of the magnetic flux density at the top and bottom surfaces of the sample, and is interpreted with the help of optical polarized light micrographs of these surfaces. We show that the measurement of the magnetic field inside the holes can be used as a local characterization of the bulk magnetic properties of the sample.

  1. Superconducting-electromagnetic hybrid bearing using YBCO bulk blocks for passive axial levitation

    Science.gov (United States)

    Nicolsky, R.; de Andrade, R., Jr.; Ripper, A.; David, D. F. B.; Santisteban, J. A.; Stephan, R. M.; Gawalek, W.; Habisreuther, T.; Strasser, T.

    2000-06-01

    A superconducting/electromagnetic hybrid bearing has been designed using active radial electromagnetic positioning and a superconducting passive axial levitator. This bearing has been tested for an induction machine with a vertical shaft. The prototype was conceived as a four-pole, two-phase induction machine using specially designed stator windings for delivering torque and radial positioning simultaneously. The radial bearing uses four eddy-current sensors, displaced 90° from each other, for measuring the shaft position and a PID control system for feeding back the currents. The stator windings have been adapted from the ones of a standard induction motor. The superconducting axial bearing has been assembled with commercial NdFeB permanent magnets and a set of seven top-seeded-melt-textured YBCO large-grain cylindrical blocks. The bearing set-up was previously simulated by a finite element method for different permanent magnet-superconductor block configurations. The stiffness of the superconducting axial bearing has been investigated by measuring by a dynamic method the vertical and transversal elastic constants for different field cooling processes. The resulting elastic constants show a linear dependence on the air gap, i.e. the clearance between the permanent magnet assembly and the set of superconducting large-grain blocks, which is dependent on cooling distance.

  2. Temperature measurement of RE123 bulk superconductors on magnetizing process

    International Nuclear Information System (INIS)

    Yokoyama, K.; Kaneyama, M.; Oka, T.; Fujishiro, H.; Noto, K.

    2004-01-01

    We study on the magnetization behavior of to magnetize RE123 bulk superconductors to apply it as strong magnets. Through magnetizing process, the temperature of bulk superconductors is raised by pinning loss caused by the magnetic fluxes motion (e.g. flux jump of flux flow), and the trapped field is decreased. This paper presents the measurement of temperature changes of Sm123 bulk superconductors during the exciting process by iteratively magnetizing pulsed-field operation with reducing amplitudes (IMRA) method. Five thermocouples are put on the surface of Sm123 bulk superconductor of 46 mm in diameter. The temperatures at the center, on the growth sector boundary (GSB) line and in the sector region surrounded by GSB's line (inter-GSB region) are monitored. The temperature at a cold stage is also measured. A Hall sensor is attached near the center thermocouple to measure the trapped field. After a bulk superconductor is cooled by the GM type refrigerator until 40 K, iterative pulsed-fields of 2.32-5.42 T are applied by a magnetizing coil. When high magnetic field of 5.42 T is applied, a temperature of bulk superconductor reaches to 72.4 K and the magnetic field distribution has C form with which a part of circle is dented, and then, a trapped field is 2.28 T. When a lower magnetic field of 4.64 T is applied, a maximum temperature is 68.3 K and a trapped field is raised to 2.70 T, and moreover, the distribution becomes round shape like field-cooling method (FC). We showed clearly that heat generation by pinning loss was related to the mechanism of magnetic field capture

  3. Application of textured YBCO bulks with artificial holes for superconducting magnetic bearing

    International Nuclear Information System (INIS)

    Dias, D H N; Sotelo, G G; Moysés, L A; Telles, L G T; Bernstein, P; Aburas, M; Noudem, J G; Kenfaui, D; Chaud, X

    2015-01-01

    The levitation force between a superconductor and a permanent magnet has been investigated for the development of superconducting magnetic bearings (SMBs). Depending on the proposed application, the SMBs can be arranged with two kinds of symmetries: rotational or linear. The SMBs present passive operation, low level of noise and no friction, but they need a cooling system for their operation. Nowadays the cooling problem may be easily solved by the use of a commercial cryocooler. The levitation force of SMBs is directly related to the quality of the superconductor material (which depends on its critical current density) and the permanent magnet arrangement. Also, research about the YBa 2 Cu 3 O x (Y123) bulk materials has shown that artificial holes enhance the superconducting properties, in particular the magnetic trapped field. In this context, this work proposes the investigation of the levitation force of a bulk Y123 sample with multiple holes and the comparison of its performances with those of conventional plain Y123 superconductors. (paper)

  4. Analysis of YBCO high temperature superconductor doped with silver nanoparticles and carbon nanotubes using Williamson-Hall and size-strain plot

    Science.gov (United States)

    Dadras, Sedigheh; Davoudiniya, Masoumeh

    2018-05-01

    This paper sets out to investigate and compare the effects of Ag nanoparticles and carbon nanotubes (CNTs) doping on the mechanical properties of Y1Ba2Cu3O7-δ (YBCO) high temperature superconductor. For this purpose, the pure and doped YBCO samples were synthesized by sol-gel method. The microstructural analysis of the samples is performed using X-ray diffraction (XRD). The crystalline size, lattice strain and stress of the pure and doped YBCO samples were estimated by modified forms of Williamson-Hall analysis (W-H), namely, uniform deformation model (UDM), uniform deformation stress model (UDSM) and the size-strain plot method (SSP). These results show that the crystalline size, lattice strain and stress of the YBCO samples declined by Ag nanoparticles and CNTs doping.

  5. Induction linear accelerators with high-Tc bulk superconductor lenses

    International Nuclear Information System (INIS)

    Matsuzawa, Hidenori; Wada, Haruhisa; Mori, Satoshi; Yamamoto, Tadashi

    1991-01-01

    Solenoidal coils in a one-stage induction accelerator were replaced by a high-T c bulk superconductor lens (Supertron). The accelerator postaccelerated injected electron beams to ∼ 400 keV, ∼ 0.35 kA, and ∼ 10 ns of duration time. (author)

  6. Microstructure and associated properties of YBa2Cu3Ox superconductors prepared by melt-processing techniques

    International Nuclear Information System (INIS)

    Balachandran, U.; Zhong, W.; Youngdahl, C.A.; Poeppel, R.B.

    1993-03-01

    From the standpoint of applications, melt-processed bulk YBa 2 Cu 3 O x (YBCO) superconductors are of considerable interest. We have studied the microstructure and levitation force of melt-processed YBCO, YBCO plus Y 2 BaCuO 5 , and YBCO plus Pt samples. Large single crystalline samples, grown using a seeding technique, were also studied. The levitation force is highest in melt-processed samples made by the seeding technique. 6 figs, 24 refs

  7. Engineered flux-pinning centers in BSCCO TBCCO and YBCO superconductors

    Science.gov (United States)

    Goretta, K.C.; Lanagan, M.T.; Miller, D.J.; Sengupta, S.; Parker, J.C.; Hu, J.; Balachandran, U.; Siegel, R.W.; Shi, D.

    1999-07-27

    A method of preparing a high temperature superconductor is disclosed. A method of preparing a superconductor includes providing a powdered high temperature superconductor and a nanophase material. These components are combined to form a solid compacted mass with the material disposed in the polycrystalline high temperature superconductor. This combined mixture is rapidly heated, forming a dispersion of nanophase size particles without a eutectic reaction. These nanophase particles can have a flat plate or columnar type morphology. 4 figs.

  8. Modelling and comparison of trapped fields in (RE)BCO bulk superconductors for activation using pulsed field magnetization

    Science.gov (United States)

    Ainslie, M. D.; Fujishiro, H.; Ujiie, T.; Zou, J.; Dennis, A. R.; Shi, Y.-H.; Cardwell, D. A.

    2014-06-01

    The ability to generate a permanent, stable magnetic field unsupported by an electromotive force is fundamental to a variety of engineering applications. Bulk high temperature superconducting (HTS) materials can trap magnetic fields of magnitude over ten times higher than the maximum field produced by conventional magnets, which is limited practically to rather less than 2 T. In this paper, two large c-axis oriented, single-grain YBCO and GdBCO bulk superconductors are magnetized by the pulsed field magnetization (PFM) technique at temperatures of 40 and 65 K and the characteristics of the resulting trapped field profile are investigated with a view of magnetizing such samples as trapped field magnets (TFMs) in situ inside a trapped flux-type superconducting electric machine. A comparison is made between the temperatures at which the pulsed magnetic field is applied and the results have strong implications for the optimum operating temperature for TFMs in trapped flux-type superconducting electric machines. The effects of inhomogeneities, which occur during the growth process of single-grain bulk superconductors, on the trapped field and maximum temperature rise in the sample are modelled numerically using a 3D finite-element model based on the H-formulation and implemented in Comsol Multiphysics 4.3a. The results agree qualitatively with the observed experimental results, in that inhomogeneities act to distort the trapped field profile and reduce the magnitude of the trapped field due to localized heating within the sample and preferential movement and pinning of flux lines around the growth section regions (GSRs) and growth sector boundaries (GSBs), respectively. The modelling framework will allow further investigation of various inhomogeneities that arise during the processing of (RE)BCO bulk superconductors, including inhomogeneous Jc distributions and the presence of current-limiting grain boundaries and cracks, and it can be used to assist optimization of

  9. Flux-pinning-induced stress and magnetostriction in bulk superconductors

    International Nuclear Information System (INIS)

    Johansen, Tom H.

    2000-01-01

    The development of bulk high-temperature superconductors (HTSs) and their applications has today come to a point where the mechanical response to high magnetic fields may be more important than their critical-current density and large-grain property. Reviewed in this article are the recent studies of the magneto-elastic effects which are caused by flux pinning in the superconductors. This includes the work on the giant irreversible magnetostriction and internal stress, which often cause fatal cracking of the HTS bulks as they become magnetized. The cracking is a problem that today accompanies the quest for the highest trapped field values, and the latest development in this area is also presented. While the first part is an overview of experimental efforts, the second summarizes the work done to model the pinning-induced stress and strain under various magnetic and geometrical conditions. (author)

  10. High output power reluctance electric motors with bulk high-temperature superconductor elements

    Energy Technology Data Exchange (ETDEWEB)

    Kovalev, L.K. [Moscow State Aviation Institute (Technical University) (MAI), Moscow (Russian Federation)]. E-mail: kovalev@mail.sitek.net; Ilushin, K.V.; Penkin, V.T. [Moscow State Aviation Institute (Technical University) (MAI), Moscow (RU)] [and others

    2002-05-01

    We present new types of electric machines with the rotors containing bulk high-temperature superconductor (HTS)-YBCO and Bi-Ag-elements. We discuss different schematics of hysteresis, reluctance, 'trapped field' and composed synchronous HTS machines. The two-dimensional mathematical models describing the processes in such types of HTS machines were developed on the basis of the theoretical analysis of the electrodynamic and hysteresis processes in the single-domain and polycrystal YBCO ceramic samples and plate shape Bi-Ag elements. We give the test results of the series of hysteresis, reluctance, 'trapped field' and composed with permanent magnets HTS motors with an output power rating of 0.1-18 kW and current frequencies 50 Hz and 400 Hz. These results show that in the media of liquid nitrogen the specific output power per one unit weight of the HTS motor is four to seven times better than for conventional electric machines. A comparison of the theoretical and experimental characteristics of the developed HTS motors show that they are in good agreement. We discuss the test results for a liquid nitrogen cryogenic pump system with a hysteresis 500 W HTS motor. We describe several designs of new HTS motors operating in the media of liquid nitrogen with an output power 125 kW (and more) and a power factor of more than 0.8. We discuss future applications of new types of HTS motors for aerospace technology, on-land industry and transport systems. (author)

  11. Study by Hall probe mapping of the trapped flux modification produced by local heating in YBCO HTS bulks for different surface/volume ratios

    International Nuclear Information System (INIS)

    Laurent, Ph; Mathieu, J-P; Mattivi, B; Fagnard, J-F; Meslin, S; Noudem, J G; Ausloos, M; Cloots, R; Vanderbemden, Ph

    2005-01-01

    The aim of this report is to compare the trapped field distribution under a local heating created at the sample edge for different sample morphologies. Hall probe mappings of the magnetic induction trapped in YBCO bulk samples maintained out of thermal equilibrium were performed on YBCO bulk single domains, YBCO single domains with regularly spaced hole arrays, and YBCO superconducting foams. The capability of heat draining was quantified by two criteria: the average induction decay and the size of the thermally affected zone caused by a local heating of the sample. Among the three investigated sample shapes, the drilled single domain displays a trapped induction which is weakly affected by the local heating while displaying a high trapped field. Finally, a simple numerical modelling of the heat flux spreading into a drilled sample is used to suggest some design rules about the hole configuration and their size

  12. Permanent magnet with MgB{sub 2} bulk superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Yamamoto, Akiyasu, E-mail: yamamoto@appchem.t.u-tokyo.ac.jp [The University of Tokyo, 7-3-1 Hongo, Bunkyo, Tokyo 113-8656 (Japan); JST-PRESTO, 4-1-8 Honcho, Kawaguchi, Saitama 332-0012 (Japan); Ishihara, Atsushi; Tomita, Masaru [Railway Technical Research Institute, 2-8-38 Hikari, Kokubunji, Tokyo 185-8540 (Japan); Kishio, Kohji [The University of Tokyo, 7-3-1 Hongo, Bunkyo, Tokyo 113-8656 (Japan)

    2014-07-21

    Superconductors with persistent zero-resistance currents serve as permanent magnets for high-field applications requiring a strong and stable magnetic field, such as magnetic resonance imaging. The recent global helium shortage has quickened research into high-temperature superconductors (HTSs)—materials that can be used without conventional liquid-helium cooling to 4.2 K. Herein, we demonstrate that 40-K-class metallic HTS magnesium diboride (MgB{sub 2}) makes an excellent permanent bulk magnet, maintaining 3 T at 20 K for 1 week with an extremely high stability (<0.1 ppm/h). The magnetic field trapped in this magnet is uniformly distributed, as for single-crystalline neodymium-iron-boron. Magnetic hysteresis loop of the MgB{sub 2} permanent bulk magnet was determined. Because MgB{sub 2} is a simple-binary-line compound that does not contain rare-earth metals, polycrystalline bulk material can be industrially fabricated at low cost and with high yield to serve as strong magnets that are compatible with conventional compact cryocoolers, making MgB{sub 2} bulks promising for the next generation of Tesla-class permanent-magnet applications.

  13. Processing of bulk Bi-2223 high-temperature superconductor

    Directory of Open Access Journals (Sweden)

    Alexander Polasek

    2005-12-01

    Full Text Available The Bi2Sr2Ca2Cu3 O10+x (Bi-2223 is one of the main high temperature superconductors for applications. One of these applications is the Superconductor Fault Current Limiter (SCFCL, which is a very promising high temperature superconducting device. SCFCL's can be improved by using bulk superconductors with high critical currents, which requires a sufficiently dense and textured material. In the present work, a process for improving the microstructure of Bi-2223 bulk samples is investigated. Pressed precursor blocks are processed by sintering with a further partial melting step, in order to enhance the Bi-2223 grain texture and to healing cracks induced by pressing. In order to improve the microstructure, the precursor is mixed with silver powder before pressing. Samples with and without silver powder have been studied, with the aim of investigating the influence of silver on the microstructure evolution. The phase contents and the microstructure obtained have been analyzed through XRD and SEM/EDS. The electromagnetic characterization has been performed by Magnetic Susceptibility Analysis. We present and discuss the process and the properties of the superconducting blocks. High fractions of textured Bi-2223 grains have been obtained.

  14. Possible charge analogues of spin transfer torques in bulk superconductors

    Science.gov (United States)

    Garate, Ion

    2014-03-01

    Spin transfer torques (STT) occur when electric currents travel through inhomogeneously magnetized systems and are important for the motion of magnetic textures such as domain walls. Since superconductors are easy-plane ferromagnets in particle-hole (charge) space, it is natural to ask whether any charge duals of STT phenomena exist therein. We find that the superconducting analogue of the adiabatic STT vanishes in a bulk superconductor with a momentum-independent order parameter, while the superconducting counterpart of the nonadiabatic STT does not vanish. This nonvanishing superconducting torque is induced by heat (rather than charge) currents and acts on the charge (rather than spin) degree of freedom. It can become significant in the vicinity of the superconducting transition temperature, where it generates a net quasiparticle charge and alters the dispersion and linewidth of low-frequency collective modes. This work has been financially supported by Canada's NSERC.

  15. Monte Carlo simulation study of the positron contribution to displacements per atom production in YBCO superconductors

    International Nuclear Information System (INIS)

    Pinera, I.; Cruz, C.M.; Abreu, Y.; Leyva, A.

    2008-01-01

    The contribution from positrons to the displacements per atom (dpa) distribution induced by the gamma irradiation on YBCO superconducting slabs is presented. The procedure implemented previously by the authors was adapted to take into account the contribution from positrons to dpa induced by the gamma radiation. The results show that, when positrons are considered in the atom displacement process, the total dpa almost doubles at 10 MeV of incident gamma radiation. At that energy positrons contribute 7% more to the total dpa than electrons, although electrons maintain having the highest contribution up to about 8 MeV.

  16. Direct images and unconventional dynamics of vortices in the high-Tc superconductors YBCO (123) and BSCCO (2212)

    International Nuclear Information System (INIS)

    Gammel, P.L.; Bishop, D.; Murray, C.; Huse, D.

    1991-01-01

    Static imaging has been used to complement transport I-V measurements in inferring the phase diagram and structure of the mixed state of the high T c superconductors YBCO(123) and BSCCO (2212). High resolution Bitter patterns reveal the static structure of the flux lattice in the low field mixed state of BSCCO (2212). For B parallel c, the in-plane effective mass anisotropy is found to distort the lattice. Rotation of the field away from the c axis results in the appearance of a unique structure: a striking array of vortex chains. At low fields, the pattern is otherwise amorphous. Increasing the field above ∼ 20G results in an abrupt transition into an hexatic phase. At high fields, I-V curves with picovolt resolution imply critical behavior within the mixed state, consistent in both 123 and 2212 with a three-dimensional vortex glass transition well below T c . In 2212, a field and temperature dependent crossover in the effective dimensionality of the vortex lattice is also found

  17. The effect of nano-size ZrO2 powder addition on the microstructure and superconducting properties of single-domain Y-Ba-Cu-O bulk superconductors

    International Nuclear Information System (INIS)

    Iida, K; Babu, N H; Reddy, E S; Shi, Y-H; Cardwell, D A

    2005-01-01

    The effect of nano-size ZrO 2 powder addition on the microstructure and superconducting properties of Y-Ba-Cu-O single grain bulk superconductors has been investigated. Significant pushing phenomena of Y 2 BaCuO 5 (Y-211) particles, particularly in the c growth sector, were observed even with a small amount of ZrO 2 added to the precursor powder. An increase in Y-211 particle pushing was observed with increasing ZrO 2 content, leading to an inhomogeneous bulk microstructure. In addition, a growth cycle consisting of a Y-211 free layer-porous narrow layer-Y-211 high concentration layer was observed for samples prepared with 0.25 wt% ZrO 2 in both the a and c growth sectors. The extent of the growth of single grain Y-Ba-Cu-O (YBCO) decreased with increasing ZrO 2 content due to increased pushing of Y-211 particles towards molten liquid. The superconducting transition temperature, T c , of the ZrO 2 containing YBCO samples was sharp but depressed slightly (by up to 1 K) compared with an undoped YBCO grain, indicating a relative insensitivity of T c to ZrO 2 content. Finally, the sensitivity of critical current density, J c , to applied magnetic field in large grain bulk YBCO containing ZrO 2 was observed to depend critically on position due to the inhomogeneous sample microstructure

  18. Oxygen plasma effects on zero resistance behavior of Yb,Er-doped YBCO (123) based superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Schaefer, Helmut; Rathmann, Dirk [Department of Physics, Biophysics, and Photosynthesis, Freie Universitaet Berlin (Germany); Banko, Franziska; Steinhart, Martin [Physical Chemistry, Institute of Chemistry of New Materials, University of Osnabrueck (Germany); Nordmann, Joerg; Voss, Benjamin [Inorganic Chemistry, Institute of Chemistry of New Materials, University of Osnabrueck (Germany); Walder, Lorenz [Organic Chemistry, Molecular Electrochemistry, Institute of Chemistry of New Materials, University of Osnabrueck (Germany)

    2014-08-15

    Rare-earth doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} samples were synthesized starting from the corresponding oxides Y{sub 2}O{sub 3}, Yb{sub 2}O{sub 3}, Er{sub 2}O{sub 3}, CuO as well as Ba(OH){sub 2} by heating to 950 C under air. The doping concentrations were adjusted to 15 % Yb, 7 % Er and 20 % Yb, 15 % Er, respectively, with respect to the yttrium content. The orthogonal phased (123) YBCO ceramics were exposed to an oxygen plasma for 140 and 380 min. Zero resistance temperature (T{sub c,0}) was determined by measuring the resistivity-temperature dependence using a classical four point measurement approach. Under optimal conditions with respect to the material composition and the oxygen treatment an unusual high zero resistance temperature of 97.5 K (T{sub c,onset} ∼ 101 K) was achieved. This represents an increase of T{sub c,0} by 7.5 K. The oxygen treatment could not be monitored by IR spectroscopy, X-ray fluorescence spectroscopy, and X-ray powder diffraction. The results showed good reproducibility. (Copyright copyright 2014 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  19. Mechanical properties of Nd-Ba-Cu-O bulk superconductors

    International Nuclear Information System (INIS)

    Matsui, Motohide; Sakai, Naomichi; Murakami, Masato; Osamura, Kozo

    2003-01-01

    We investigated the effects of Nd422 and Ag particles on the mechanical properties in Nd-Ba-Cu-O bulk superconductors. Both Nd422 and Ag particles were effective in decreasing the amount of microcracks running along the c direction. In the case of Nd422, however, excessive Nd422 addition enhanced the crack propagation, resulting in the degradation of mechanical strength. In the case of Ag addition, the beneficial effect of its ductile mechanical property was not observed. This was due to a relatively large size of Ag particles and low interfacial strength between Ag and Nd123 matrix. It was remarkable that the Weibull coefficient of the sample with Ag 2 O addition exceeded 13, which is reliable enough for practical engineering applications

  20. Effects of the Seed Distance on the Characteristics of the (100)/(100) Junctions of Top-Seeded Melt Growth Processed YBCO Superconductors Using Two Seeds

    Energy Technology Data Exchange (ETDEWEB)

    Kim, C.J.; Gee, Y.A.; Hong, G.Y. [Korea Atomic Energy Research Institute, Taejon (Korea); Kim, H.J.; Joo, J.H. [Sungkyunkwan University, Suwon (Korea); Han, S.C.; Han, Y.H.; Sung, T.H.; Kim, S.J. [Korea Electric Power Research Institute, Taejon (Korea)

    1999-06-01

    The effects of the distance (d) between two Sm{sub 1.8}Ba{sub 2.4}Cu{sub 3.4}Ox seeds on the characteristics of the (100)/(100) junctions of top-seeded melt growth processed YBCO superconductors were investigated. The trapped magnetic field at the grain junction and the levitation force of the top surface decreased with increasing d value. The degradation of the properties is attributed to the presence of the residual melt-forming phases (CuO and BaCUO{sub 2}) at the grain junction, whose amount depends on the d value. (author). 18 refs., 10 figs.

  1. Relationship of the Levitation Force Between Single and Multiple YBCO Bulks Above a Permanent Magnet Guideway Operating Dive-Lift Movement with Different Angles

    Science.gov (United States)

    Zeng, R.; Wang, S. Y.; Liao, X. L.; Deng, Z. G.; Wang, J. S.

    2013-04-01

    In practical applications, the acceleration and deceleration motions inevitably happen in the operation of high temperature superconducting (HTS) maglev trains. For further research of the maglev properties of YBaCuO bulk above a permanent magnet guideway (PMG), by moving a fixed vertical distance, this paper studies the relationship of the levitation force between single and multiple YBCO bulks above a PMG operating dive-lift movement with different angles. Experimental results show that the maximal levitation force increment of two bulks than one bulk is smaller than the maximal levitation force increment of three bulks than two bulks. With the degree decreasing, the maximal levitation force increment of three bulks is bigger than the maximal levitation force increment of two bulks and one bulk, and the hysteresis loop of the levitation force of the three-bulk arrangement is getting smaller.

  2. Improvement of the mechanical properties of bulk superconductors; Jushiganshin niyoru baruku chodendotai no kikaitekitokusei no kaizen

    Energy Technology Data Exchange (ETDEWEB)

    Tomita, M; Murakami, M [Superconductivity Research Laboratory, Tokyo (Japan)

    1999-11-25

    Large single-grain bulk rare earth element (RE)-Ba-Cu-O superconductors can trip large fields exceeding several teslas and thus can function as very strong quasi-permanent magnets. However, the maximum trapped field is essentially limited by the mechanical strength of the bulk superconductors. The stress produced by refrigeration sometimes causes cracking. A large electromagnetic force also acts on superconductors when they trap large magnetic fields, and this occasionally leads to device failure. We have recently found that epoxy resin can penetrate into bulk superconductors under certain conditions. Microstructural observation revealed that microcracks as well as porosities can be impregnated with epoxy resin, which greatly improves the mechanical properties of bulk RE-Ba-Cu-O and thus results in the improvement of field trapping capability. (author)

  3. Remagnetization of bulk high-temperature superconductors subjected to crossed and rotating magnetic fields

    Energy Technology Data Exchange (ETDEWEB)

    Vanderbemden, P [SUPRATECS and Department of Electrical Engineering and Computer Science B28, Sart-Tilman, B-4000 Liege (Belgium); Hong, Z [Centre for Advanced Photonics and Electronics, Engineering Department, University of Cambridge, 9 JJ Thomson Avenue, Cambridge CB3 0FA (United Kingdom); Coombs, T A [Centre for Advanced Photonics and Electronics, Engineering Department, University of Cambridge, 9 JJ Thomson Avenue, Cambridge CB3 0FA (United Kingdom); Ausloos, M [SUPRATECS and Department of Physics B5, Sart-Tilman, B-4000 Liege (Belgium); Babu, N Hari [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Cardwell, D A [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Campbell, A M [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom)

    2007-09-15

    Bulk melt-processed Y-Ba-Cu-O (YBCO) has significant potential for a variety of high-field permanent-magnet-like applications, such as the rotor of a brushless motor. When used in rotating devices of this kind, however, the YBCO can be subjected to both transient and alternating magnetic fields that are not parallel to the direction of magnetization and which have a detrimental effect on the trapped field. These effects may lead to long-term decay of the magnetization of the bulk sample. In the present work, we analyze both experimentally and numerically the remagnetization process of a melt-processed YBCO single domain that has been partially demagnetized by a magnetic field applied orthogonal to the initial direction of trapped flux. Magnetic torque measurements are used as a tool to probe changes in the remanent magnetization during various sequences of applied field. The application of a small magnetic field between the transverse cycles parallel to the direction of original magnetization results in partial remagnetization of the sample. Rotating the applied field, however, is found to be much more efficient at remagnetizing the bulk material than applying a magnetizing field pulse of the same amplitude. The principal features of the experimental data can be reproduced qualitatively using a two-dimensional finite-element numerical model based on an E-J power law. Finally, the remagnetization process is shown to result from the complex modification of current distribution within the cross-section of the bulk sample.

  4. Remagnetization of bulk high-temperature superconductors subjected to crossed and rotating magnetic fields

    International Nuclear Information System (INIS)

    Vanderbemden, P; Hong, Z; Coombs, T A; Ausloos, M; Babu, N Hari; Cardwell, D A; Campbell, A M

    2007-01-01

    Bulk melt-processed Y-Ba-Cu-O (YBCO) has significant potential for a variety of high-field permanent-magnet-like applications, such as the rotor of a brushless motor. When used in rotating devices of this kind, however, the YBCO can be subjected to both transient and alternating magnetic fields that are not parallel to the direction of magnetization and which have a detrimental effect on the trapped field. These effects may lead to long-term decay of the magnetization of the bulk sample. In the present work, we analyze both experimentally and numerically the remagnetization process of a melt-processed YBCO single domain that has been partially demagnetized by a magnetic field applied orthogonal to the initial direction of trapped flux. Magnetic torque measurements are used as a tool to probe changes in the remanent magnetization during various sequences of applied field. The application of a small magnetic field between the transverse cycles parallel to the direction of original magnetization results in partial remagnetization of the sample. Rotating the applied field, however, is found to be much more efficient at remagnetizing the bulk material than applying a magnetizing field pulse of the same amplitude. The principal features of the experimental data can be reproduced qualitatively using a two-dimensional finite-element numerical model based on an E-J power law. Finally, the remagnetization process is shown to result from the complex modification of current distribution within the cross-section of the bulk sample

  5. YBCO bulk material processed in an oxygen controlled melt-growth process

    International Nuclear Information System (INIS)

    Giovannelli, F.; Monot-Laffez, I.

    2002-01-01

    YBCO pellets have been submitted to the top-seeding melt-textured growth process under a reduced oxygen atmosphere (1% O 2 in Ar). Ce and (Ce, Sn) doping have been investigated. In the Ce-doped sample, a fishtail has been observed when the thermal cycle maximal temperature of 1020 deg. C is used. However, the microstructure exhibits large Y211 particles under these processing conditions. When the maximal temperature is 1000 deg. C, the size of Y211 decreases and the critical current density (J c ) is enhanced. The effect observed under a field is a shoulder in the J c curve. The same effect is observed in the (Ce, Sn)-doped sample. The Ce-doped and (Ce, Sn)-doped samples exhibit J c under a self-field of 90 000 A cm -2 and 84 000 A cm -2 , respectively. Moreover, when the pre-sintering step is suppressed, the values of J c are improved and the samples present a J c of 100 000 A cm -2 under a self-field. (author)

  6. Proposal of Magnetic Circuit using Magnetic Shielding with Bulk-Type High Tc Superconductors

    Science.gov (United States)

    Fukuoka, Katsuhiro; Hashimoto, Mitsuo; Tomita, Masaru; Murakami, Masato

    Recently, bulk-type high Tc superconductors having a characteristic of critical current density over 104 A/cm2 in liquid nitrogen temperature (77K) on 1T, can be produced. They are promising for many practical applications such as a magnetic bearing, a magnetic levitation, a flywheel, a magnetic shielding and others. In this research, we propose a magnetic circuit that is able to use for the magnetic shield of plural superconductors as an application of bulk-type high Tc superconductors. It is a closed magnetic circuit by means of a toroidal core. Characteristics of the magnetic circuit surrounded with superconductors are evaluated and the possibility is examined. As the magnetic circuit of the ferrite core is surrounded with superconductors, the magnetic flux is shielded even if it leaked from the ferrite core.

  7. A novel HTS magnetometer, exploiting the low jc of bulk YBCO

    International Nuclear Information System (INIS)

    Gallop, J.C.; Lilleyman, S.; Langham, C.D.; Radcliffe, W.J.; Stewart, M.

    1989-01-01

    The authors report here a novel of magnetometer which is based on the low critical magnetic field H/sub cl/ of sintered samples of the high temperature ceramic superconductor YBa/sub 2/Cu/sub 3/O/sub y/. By driving a sample of the superconductor around a magnetization hysteresis loop, at a frequency of --100 kHz, and detecting the induced voltage in a coil coupled to the sample, at the second harmonic of the drive frequency, the authors find that this voltage is linearly dependent on the aplied d.c. magnetic field in which the sample is situated. They present a model which explains the operation of this magnetometer. This device, while not as sensitive as a SQUID, has the advantage of a wider dynamic range and direct measurement of flux density, unlike a SQUID which is only capable of sensing flux density changes. When operated at 77K the prototype magnetometer has already demonstrated a sensitivity at least 10 times better than that of a commercial fluxgate magnetometer. The system also appears to provide a simple method for investigation of flux flow in these materials

  8. Surface barrier and bulk pinning in MgB$_2$ superconductor

    OpenAIRE

    Pissas, M.; Moraitakis, E.; Stamopoulos, D.; Papavassiliou, G.; Psycharis, V.; Koutandos, S.

    2001-01-01

    We present a modified method of preparation of the new superconductor MgB$_2$. The polycrystalline samples were characterized using x-ray and magnetic measurements. The surface barriers control the isothermal magnetization loops in powder samples. In bulk as prepared samples we always observed symmetric magnetization loops indicative of the presence of a bulk pinning mechanism. Magnetic relaxation measurements in the bulk sample reveal a crossover of surface barrier to bulk pinning.

  9. Magnetic Signals of High-Temperature Superconductor Bulk During the Levitation Force Measurement Process

    Science.gov (United States)

    Huang, Huan; Zheng, Jun; Qian, Nan; Che, Tong; Zheng, Botian; Jin, Liwei; Deng, Zigang

    2017-05-01

    In order to study the commonly neglected magnetic field information in the course of levitation force measurement process in a superconducting maglev system, a multipoint magnetic field measurement platform was employed to acquire magnetic signals of a bulk high-Tc superconductor on both the top and the bottom surface. Working conditions including field cooling (FC) and zero field cooling were investigated for these vertical down and up motions above a permanent magnet guideway performed on a HTS maglev measurement system. We have discussed the magnetic flux variation process based on the Bean model. A magnetic hysteresis effect similar to the levitation force hysteresis loop of the bulk superconductor was displayed and analyzed in this paper. What is more valuable, there exists some available magnetic flux on the top surface of the bulk superconductor, and the proportion is as high as 62.42% in the FC condition, which provides an experimental hint to design the superconductor bulk and the applied field for practical use in a more efficient way. In particular, this work reveals real-time magnetic flux variation of the bulk superconductor in the levitation application, which is the other important information in contrast to the macroscopic levitation and guidance force investigations in previous studies, and it enriches the existing research methods. The results are significant for understanding the magnetic characteristic of superconductors, and they can contribute to optimize the present HTS maglev system design.

  10. Microstructure and superconducting properties of YBCO bulk superconductors with RE substitutions

    Czech Academy of Sciences Publication Activity Database

    Volochová, D.; Antal, V.; Piovarči, S.; Kováč, J.; Jirsa, Miloš; Noudem, J.; Diko, P.

    2016-01-01

    Roč. 26, č. 3 (2016), s. 1-4, č. článku 7200604. ISSN 1051-8223 Institutional support: RVO:68378271 Keywords : yttrium barium copper oxide * critical current density (superconductivity) * powders * magnetic fields * microstructure * temperature measurement Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.092, year: 2015

  11. Recent progress in material technology on RE-Ba-Cu-O bulk superconductors

    International Nuclear Information System (INIS)

    Teshima, Hidekazu; Morita, Mitsuru

    2011-01-01

    The current status of large-grained RE-Ba-Cu-O (RE: Y or rare earth elements) bulk superconductors with excellent superconducting properties is described. Gd-Ba-Cu-O bulk superconductors can trap a very high magnetic field even if they are melt-processed in air. Although the electromagnetic force caused by the trapped field is larger for a larger sample and may break the sample, a large sample of Gd-Ba-Cu-O 46 mm in diameter has the potential of trapped magnetic fields greater than 10 T at around 40 K. In addition, single-grained bulk superconductors as large as 150 mm can be obtained using the RE compositional gradient method. Dy-Ba-Cu-O is an ideal material for current leads because it has low thermal conductivity and high critical current density at 77 K in high magnetic fields. Eu-Ba-Cu-O has low magnetic permeability, and is therefore suitable for bulk NMR applications. Progress in machining technology has made possible various bulk superconductors with complicated shapes such as coils, leading to small and strong electromagnets by stacking several coil-shaped bulk superconductors together. (author)

  12. Bulk superconductivity in Type II superconductors near the second critical field

    DEFF Research Database (Denmark)

    Fournais, Søren; Helffer, Bernard

    2010-01-01

    We consider superconductors of Type II near the transition from the ‘bulk superconducting’ to the ‘surface superconducting’ state. We prove a new L∞ estimate on the order parameter in the bulk, i.e. away from the boundary. This solves an open problem posed by Aftalion and Serfaty [AS]....

  13. Estudio de la evolución y técnica de regulación de la corriente persistente en anillos superconductores de YBCO

    Directory of Open Access Journals (Sweden)

    Quelle, I.

    2008-04-01

    Full Text Available In this work, a study of the relation between the density of trapped vortices and the current evolution and a technique for controlling the current from its critical value in YBCO rings, are performed. To generate the persistent current in the rings, an inducting technique called field cooling is used. Combining the field cooling technique with magnetic fields in opposite direction to the inducting one, the density of trapped vortices decreases and the current decay also decreases. Then, a part of the sample is heated to decrease the current to the desired value, which is checked using a Hall sensor.

    En este trabajo se realiza un estudio de la evolución de corriente en función de la densidad de vórtices atrapados y se presenta una técnica para regular la corriente partiendo del valor crítico, en anillos superconductores de YBCO. Para generar una corriente persistente en los anillos se utiliza un método de tipo inductivo, denominado field cooling, que combinado con campos magnéticos en sentido contrario al inductor permite disminuir la densidad de vórtices atrapados y se logra también disminuir el decaimiento de corriente. Una vez que se ha inducido la corriente crítica en los anillos una zona muy localizada de éstos se calienta hasta que el superconductor alcanza el valor deseado de corriente, lo cual se comprueba mediante la medida de campo magnético con una sonda Hall.

  14. Project of RE123 bulk superconductors fabrication in a microgravity environment; Bishojuryokuka chodensotai seizo purojekuto

    Energy Technology Data Exchange (ETDEWEB)

    Sakai, N; Murakami, M [International Superconductivity Technology Center, Tokyo (Japan); Shisa, A [Ishikawajima-Harima Heavy Industries Co., Ltd., Toky o(Japan); Hirata, H [Institute for Unmanned Space Experiment Free Flyer, Tokyo (Japan)

    1999-11-25

    Large single-grain bulk rare earth element (RE)-Ba-Cu-O superconductors can be used for various applications such magnetic bearings, load trapped field magnets. The magnetic field generated by bulk RE-Ba-Cu-O superconductors is proportional to its radius, however, the growth of a large single-grain bulk with good quality is difficult due to contamination from the substrate or the crucible and also due to liquid loss. Such problems can be solved by growing RE-Cu-O bulk in a microgravity environment, where the bulk can be supported by a seed crystal alone during crystal growth. Such experiments will be conducted in the Unmanned Space Experiment Recovery System (USERS) project. In this paper, the experiment plan and the present status of the system development are reported. (author)

  15. Flux Trapping Properties of Bulk HIGH-TC Superconductors in Static Field-Cooling Magnetization

    Science.gov (United States)

    Deng, Z.; Tsuzuki, K.; Miki, M.; Felder, B.; Hara, S.; Izumi, M.

    2013-06-01

    The trapping process and saturation effect of trapped magnetic flux of bulk high-temperature superconductors by static field-cooling magnetization (FCM) are reported in the paper. With a cryogenic Bell Hall sensor attached on the center of the bulk surface, the synchronous magnetic signals were recorded during the whole magnetization process. It enables us to know the flux trapping behavior since the removal of the excitation field, as well as the subsequent flux relaxation phenomenon and the flux dissipation in the quench process of the bulk sample. With the help of flux mapping techniques, the relationship between the trapped flux and the applied field was further investigated; the saturation effect of trapped flux was discussed by comparing the peak trapped field and total magnetic flux of the bulk sample. These studies are useful to understand the basic flux trapping properties of bulk superconductors.

  16. Development of high temperature superconductors having high critical current density

    International Nuclear Information System (INIS)

    Hong, Gye Wong; Kim, C. J.; Lee, H.G.; Kwon, S. C.; Lee, H. J.; Kim, K. B.; Park, J. Y.; Jung, C. H.

    2000-08-01

    Fabrication of high T c superconductors and its applications for electric power device were carried out for developing superconductor application technologies. High quality YBCO superconductors was fabricated by melt texture growth, top-seeded melt growth process and multi-seeded melt growth process and the properties was compared. The critical current density of the melt processed YBCO superconductors was about few 10,000 A/cm 2 and the levitation force was 50 N. The processing time needed for the growth of the 123 single grain was greatly reduced by applying multi-seeding without no significant degradation of the levitation force. The multi-seeded melt growth process was confirmed as a time-saving and cost-effective method for the fabrication of bulk superconductors with controlled crystallographic orientation

  17. Development of high temperature superconductors having high critical current density

    Energy Technology Data Exchange (ETDEWEB)

    Hong, Gye Wong; Kim, C. J.; Lee, H.G.; Kwon, S. C.; Lee, H. J.; Kim, K. B.; Park, J. Y.; Jung, C. H

    2000-08-01

    Fabrication of high T{sub c} superconductors and its applications for electric power device were carried out for developing superconductor application technologies. High quality YBCO superconductors was fabricated by melt texture growth, top-seeded melt growth process and multi-seeded melt growth process and the properties was compared. The critical current density of the melt processed YBCO superconductors was about few 10,000 A/cm{sup 2} and the levitation force was 50 N. The processing time needed for the growth of the 123 single grain was greatly reduced by applying multi-seeding without no significant degradation of the levitation force. The multi-seeded melt growth process was confirmed as a time-saving and cost-effective method for the fabrication of bulk superconductors with controlled crystallographic orientation.

  18. Granular Superconductors and Gravity

    Science.gov (United States)

    Noever, David; Koczor, Ron

    1999-01-01

    As a Bose condensate, superconductors provide novel conditions for revisiting previously proposed couplings between electromagnetism and gravity. Strong variations in Cooper pair density, large conductivity and low magnetic permeability define superconductive and degenerate condensates without the traditional density limits imposed by the Fermi energy (approx. 10(exp -6) g cu cm). Recent experiments have reported anomalous weight loss for a test mass suspended above a rotating Type II, YBCO superconductor, with a relatively high percentage change (0.05-2.1%) independent of the test mass' chemical composition and diamagnetic properties. A variation of 5 parts per 104 was reported above a stationary (non-rotating) superconductor. In experiments using a sensitive gravimeter, bulk YBCO superconductors were stably levitated in a DC magnetic field and exposed without levitation to low-field strength AC magnetic fields. Changes in observed gravity signals were measured to be less than 2 parts in 108 of the normal gravitational acceleration. Given the high sensitivity of the test, future work will examine variants on the basic magnetic behavior of granular superconductors, with particular focus on quantifying their proposed importance to gravity.

  19. Concepts for using trapped-flux bulk high-temperature superconductor in motors and generators

    International Nuclear Information System (INIS)

    Hull, John R; Strasik, Michael

    2010-01-01

    We review previous concepts for using bulk high-temperature superconductors (HTSs) in motors and generators and discuss methods for using trapped-flux (TF) HTSs in motors and generators that have been recently investigated in our laboratory. We examine the expected performance of a brushless motor/generator that uses TF bulk HTSs to provide magnetomotive force, where the stator windings are used to create the TF. A key feature is the use of dysprosium for the stator and rotor cores.

  20. Clean bulk YBaCuO superconductors doped by paramagnetic ions of Sm and Yb

    Czech Academy of Sciences Publication Activity Database

    Jirsa, Miloš; Volochová, D.; Kováč, J.; Diko, P.

    2017-01-01

    Roč. 131, č. 4 (2017), s. 1027-1029 ISSN 0587-4246 Institutional support: RVO:68378271 Keywords : YBaCuO * bulk superconductors * paramagnetic ions * microstructure * vortex pinning Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 0.469, year: 2016

  1. Bulk viscosity of spin-one color superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Sa' d, Basil A.

    2009-08-27

    The bulk viscosity of several quark matter phases is calculated. It is found that the effect of color superconductivity is not trivial, it may suppress, or enhance the bulk viscosity depending on the critical temperature and the temperature at which the bulk viscosity is calculated. Also, is it found that the effect of neutrino-emitting Urca processes cannot be neglected in the consideration of the bulk viscosity of strange quark matter. The results for the bulk viscosity of strange quark matter are used to calculate the r-mode instability window of quark stars with several possible phases. It is shown that each possible phase has a different structure for the r-mode instability window. (orig.)

  2. Bulk viscosity of spin-one color superconductors

    International Nuclear Information System (INIS)

    Sa'd, Basil A.

    2009-01-01

    The bulk viscosity of several quark matter phases is calculated. It is found that the effect of color superconductivity is not trivial, it may suppress, or enhance the bulk viscosity depending on the critical temperature and the temperature at which the bulk viscosity is calculated. Also, is it found that the effect of neutrino-emitting Urca processes cannot be neglected in the consideration of the bulk viscosity of strange quark matter. The results for the bulk viscosity of strange quark matter are used to calculate the r-mode instability window of quark stars with several possible phases. It is shown that each possible phase has a different structure for the r-mode instability window. (orig.)

  3. A superconducting conveyer system using multiple bulk Y-Ba-Cu-O superconductors and permanent magnets

    Science.gov (United States)

    Kinoshita, T.; Koshizuka, N.; Nagashima, K.; Murakami, M.

    Developments of non-contact superconducting devices like superconducting magnetic levitation transfer and superconducting flywheel energy storage system have been performed based on the interactions between bulk Y-Ba-Cu-O superconductors and permanent magnets, in that the superconductors can stably be levitated without any active control. The performances of noncontact superconducting devices are dependent on the interaction forces like attractive forces and stiffness. In the present study, we constructed a non-contact conveyer for which the guide rails were prepared by attaching many Fe-Nd-B magnets onto an iron base plate. Along the translational direction, all the magnets were arranged as to face the same pole, and furthermore their inter-distance was made as small as possible. The guide rail has three magnet rows, for which the magnets were glued on the iron plate such that adjacent magnet rows have opposite poles like NSN. At the center row, the magnetic field at zero gap reached 0.61T, while the field strengths of two rows on the side edges were only 0.48T due to magnetic interactions among permanent magnets. We then prepared a cryogenic box made with FRP that can store several bulk Y-Ba-Cu-O superconductors 25 mm in diameter cooled by liquid nitrogen. It was found that the levitation forces and stiffness increased with increasing the number of bulk superconductors installed in the box, although the levitation force per unit bulk were almost the same. We also confirmed that these forces are dependent on the configuration of bulk superconductors.

  4. Transport current anisotropy in oriented grained bulk YBa2Cu3O(x) superconductor

    International Nuclear Information System (INIS)

    Selvamanickam, V.; Salama, K.

    1990-01-01

    The anisotropy in transport current density has been studied on bulk YBa2Cu3O(x) superconductor. The transport current density measurements were performed on oriented grained YBa2Cu3O(x) superconductor with the current aligned at different angles to the a-b plane. The angular dependence of Jc shows a rapid drop when the transport current is misaligned from the a-b plane at small angles and then a slow decrease at higher angles. An anisotropy ratio of about 25 is observed at 77 K and zero field between the Jc along a-b plane and that perpendicular to the plane. 15 refs

  5. Transport current anisotropy in oriented grained bulk YBa2Cu3Ox superconductor

    International Nuclear Information System (INIS)

    Selvamanickam, V.; Salama, K.

    1990-01-01

    The anisotropy in transport current density has been studied on bulk YBa 2 Cu 3 O x superconductor. The transport current density measurements were performed on oriented grained YBa 2 Cu 3 O x superconductor with the current aligned at different angles to the a endash b plane. The angular dependence of J c shows a rapid drop when the transport current is misaligned from the a endash b plane at small angles and then a slow decrease at higher angles. An anisotropy ratio of about 25 is observed at 77 K and zero field between the J c along a endash b plane and that perpendicular to the plane

  6. The effect of growth temperature on the irreversibility line of MPMG YBCO bulk with Y2O3 layer

    Science.gov (United States)

    Kurnaz, Sedat; Çakır, Bakiye; Aydıner, Alev

    2017-07-01

    In this study, three kinds of YBCO samples which are named Y1040, Y1050 and Y1060 were fabricated by Melt-Powder-Melt-Growth (MPMG) method without a seed crystal. Samples seem to be single crystal. The compacted powders were located on a crucible with a buffer layer of Y2O3 to avoid liquid to spread on the furnace plate and also to support crystal growth. YBCO samples were investigated by magnetoresistivity (ρ-T) and magnetization (M-T) measurements in dc magnetic fields (parallel to c-axis) up to 5 T. Irreversibility fields (Hirr) and upper critical fields (Hc2) were obtained using 10% and 90% criteria of the normal state resistivity value from ρ-T curves. M-T measurements were carried out using the zero field cooling (ZFC) and field cooling (FC) processes to get irreversible temperature (Tirr). Fitting of the irreversibility line results to giant flux creep and vortex glass models were discussed. The results were found to be consistent with the results of the samples fabricated using a seed crystal. At the fabrication of MPMG YBCO, optimized temperature for crystal growth was determined to be around 1050-1060 °C.

  7. Transport properties of high-temperature superconductors: Surface vs bulk effect

    International Nuclear Information System (INIS)

    Burlachkov, L.; Koshelev, A.E.; Vinokur, V.M.

    1996-01-01

    We investigate surface-related transport properties of high-temperature superconductors. We find the mean vortex velocity under applied transport current determined by the activation energies for vortex penetration and exit through the Bean-Livingston barrier. We determine the current distribution between the surfaces of superconductor and the field and current dependencies of the transport activation energies. For a three-dimensional superconductor the transport activation energy, U s 3D , is found to decrease with the external field, H, and transport current, J, as U s 3D ∝H -1/2 and U s 3D ∝J -1/2 , respectively. In the quasi-two-dimensional compounds, U s 2D decays logarithmically with field and current. The interplay between the surface and the bulk contributions to the transport properties, such as current-voltage characteristics, is discussed. copyright 1996 The American Physical Society

  8. Improvement of critical currents in Bi-2223 bulk superconductors

    International Nuclear Information System (INIS)

    Eujen, R.; Brauer, D.J.; Huedepohl, J.

    1991-01-01

    Potential applications of the high-Tc superconductors for energy transport or high-field magnets require high critical current densities. A limiting factor in polycrystalline oxidic materials is the quality of the grain boundaries. Weak links have been made responsible for the steep decrease in the critical current density j c upon application of even weak magnetic fields of YBa CuO whereas flux creep seems to dominate the obtainable j c values for the Bi-Sr-Ca-Cu-O system (BSCCO) at 77 K. In the lead containing material (BPSCCO) the formation of a porous microstructure is enhanced by the platelike shape of the crystals. Special techniques such as powder-in-tube, hot isostatic pressing, zone melting or application of fluxes have been used in order to improve the grain contacts. A positive influence of fluxes on j c , e.g. by addition of Ca 2 CuO 3 or Ag 2 O, has been reported. In this study we have investigated the influence of various compositions and conditions on the formation of the BSCCO-2223 phase (T c ca. 107 K), the critical current density j c , and the magnet field dependence of the a.c. susceptibility. (orig.)

  9. An overview of rotating machine systems with high-temperature bulk superconductors

    Science.gov (United States)

    Zhou, Difan; Izumi, Mitsuru; Miki, Motohiro; Felder, Brice; Ida, Tetsuya; Kitano, Masahiro

    2012-10-01

    The paper contains a review of recent advancements in rotating machines with bulk high-temperature superconductors (HTS). The high critical current density of bulk HTS enables us to design rotating machines with a compact configuration in a practical scheme. The development of an axial-gap-type trapped flux synchronous rotating machine together with the systematic research works at the Tokyo University of Marine Science and Technology since 2001 are briefly introduced. Developments in bulk HTS rotating machines in other research groups are also summarized. The key issues of bulk HTS machines, including material progress of bulk HTS, in situ magnetization, and cooling together with AC loss at low-temperature operation are discussed.

  10. Granularity effect on microwave surface resistance in high-Tc YBa2Cu3O7-x bulk and thin film superconductor

    International Nuclear Information System (INIS)

    Swarup, Ram; Gupta, A.K.

    2001-01-01

    We report the effect of variation of Josephson coupling strength in YBa 2 Cu 3 O 7-x (YBCO) superconductor due to grain enlargement, grain orientation and magnetic field on microwave surface resistance (R s ). The coupling strength in the bulk samples has been increased by increasing the sample density from 4.4 to 5.3 g/cm 3 , whereas in thin films, the same could be increased by increasing the c-axis orientation of the grains. The value of R s (10 GHz, 65 K) in bulk samples has been found to decrease from 52 to 4 mΩ with the increase of the coupling strength from 0.06 to 0.43 and in thin films from 930 to 600 μΩ with increase of the coupling strength from 0.92 to 2.43. The effect of grain decoupling on microwave surface resistance was studied under dc and microwave magnetic fields. The surface resistance increases gradually with the application of dc and microwave magnetic fields due to grain decoupling and finally gets saturated beyond a certain critical field. (author)

  11. Interior seeding for the fabrication of single-grain REBCO bulk superconductors

    International Nuclear Information System (INIS)

    Kim, C-J; Park, S-D; Jun, B-H; Park, H-W

    2016-01-01

    This study presents a new seeding technique, named ‘interior seeding’ which allows the growth of a single REBCO (RE: rare-earth elements) grain in the interior of REBCO compacts. The key techniques of interior seeding are to provide appropriate open space for seeds in the interior of REBCO powder compacts to supply air or oxygen to the seeds, and to minimize the contact area between the seeds and liquid. The advantages of interior seeding are as follows: (1) simultaneous growth from the seed to the top and bottom of the REBCO compacts is possible, (2) fractions of the a-b growth sector and the a-c growth sector on the top surface can be controlled and (3) the top surfaces of the single-grain REBCO bulk superconductors are free from samarium or neodymium contamination from the used seeds. The very large single-grain Y 1.5 Ba 2 Cu 3 O 7−y (Y1.5) bulk superconductors (42 mm) were successfully fabricated using a melt growth (MG) process combined with interior seeding. Also, large-grain Y1.5 bulk superconductors (41 mm) with 〈110〉/〈110〉 and 〈100〉/〈100〉 grain junctions were fabricated using multiple interior seeding. In this paper, the detailed process of interior seeding, the development of top surface patterns and the properties of single-grain Y123 bulk superconductors fabricated using interior seeding were reported. (paper)

  12. Maximum repulsed magnetization of a bulk superconductor with low pulsed field

    International Nuclear Information System (INIS)

    Tsuchimoto, M.; Kamijo, H.; Fujimoto, H.

    2005-01-01

    Pulsed field magnetization of a bulk high-T c superconductor (HTS) is important technique especially for practical applications of a bulk superconducting magnet. Full magnetization is not obtained for low pulsed field and trapped field is decreased by reversed current in the HTS. The trapped field distribution by repulsed magnetization was previously reported in experiments with temperature control. In this study, repulsed magnetization technique with the low pulsed field is numerically analyzed under assumption of variable shielding current by the temperature control. The shielding current densities are discussed to obtain maximum trapped field by two times of low pulsed field magnetizations

  13. Melt-growth bulk superconductors and application to an axial-gap-type rotating machine

    International Nuclear Information System (INIS)

    Zhang, Yufeng; Zhou, Difan; Ida, Tetsuya; Miki, Motohiro; Izumi, Mitsuru

    2016-01-01

    The present manuscript addresses key issues in the course of our study of materials processing of bulk high-temperature superconductors, trapped flux and its application to a prototype axial-gap-type rotating machine. The TUMSAT group has conducted a series of studies since 2003 on the growth of GdBa 2 Cu 3 O 7−δ bulk material and its application in a compact low-speed high-torque rotating machine. In the stage of material growth, gaining the advantage of a large motive torque density requires large integrated flux in the motor/generators. A large grain surface might be required with sophisticated techniques for the melt-growth texture in the bulk with optimal flux pinning. In the second stage, the in situ magnetization procedure for bulk superconductors in the applied machine is a crucial part of the technology. Pulsed current excitation by using an armature copper winding has magnetized field pole bulks on the rotor. The axial-gap flux synchronous machine studied in the past decade is a condensed technology and indicates that further scientific development is required for a future compact machine to be superior to conventional ones in accordance with the cryogenic periphery and flux stabilization. (paper)

  14. Pulsed-Field Magnetization Properties of Bulk Superconductors by Employment of Vortex-Type Coils

    Science.gov (United States)

    Deng, Z.; Shinohara, N.; Miki, M.; Felder, B.; Tsuzuki, K.; Watasaki, M.; Kawabe, S.; Taguchi, R.; Izumi, M.

    Vortex-type magnetizing coils are gaining more and more attention to activate bulk superconductors in pulsed-field magnetization (PFM) studies, compared with solenoid-type ones. Following existing reports, we present experimental results of the different penetration patterns of magnetic flux between the two kinds of coils. It was found that the magnetic flux will primarily penetrate inside the bulk from the upper and lower surfaces by using vortex coils, rather than from the periphery in the case of solenoid coils. Moreover, the bulk submitted to a small pulsed-field excitation exhibits a similar field profile as the excitation field (convex or concave shape); a phenomenon named field memory effect. The use of vortex- or solenoid-type coils in PFM will pose an influence on the initial flux penetration patterns during the flux trapping processes, but both coils can finally excite the best conical trapped field shape of the bulk.

  15. Measurement of electromagnetic force between multiple bulk superconductors; Fukusu no barukutai chodendotai to eikyujishakukairo niokeru denjiryoku sokutei

    Energy Technology Data Exchange (ETDEWEB)

    Otani, T.; Murakami, M. [Superconductivity Research Laboratory, Tokyo (Japan); Nagashima, K. [Railway Technical Research Institute, Tokyo (Japan); Murayama, M. [Shikoku Ekectric Power Co., Inc., Kagawa (Japan)

    1999-11-25

    The electromagnetic force (EMF) that is exhibited by the interaction between bulk superconductors and permanent magnets is used for magnetic levitation devices. To facilitate such applications, it is necessary to enhance the EMF. We measured the EMF for Y-Ba-Cu-O superconductors with different shapes and dimensions by varying the structure of disk magnets such as their thickness and the number of poles. The EMF is strongly dependent on the magnet structure as long as permanent magnets and good quality bulk superconductors are used. Thus, for the design of practical devices, it is important to optimize the magnet structure. (author)

  16. Numerical analysis of thermally actuated magnets for magnetization of superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Li Quan; Yan Yu; Rawlings, Colin; Coombs, Tim, E-mail: ql229@cam.ac.u [EPEC Superconductivity Group, Engineering Department, University of Cambridge, Trumpington Street. Cambridge, CB2 1PZ (United Kingdom)

    2010-06-01

    Superconductors, such as YBCO bulks, have extremely high potential magnetic flux densities, comparing to rare earth magnets. Therefore, the magnetization of superconductors has attracted broad attention and contribution from both academic research and industry. In this paper, a novel technique is proposed to magnetize superconductors. Unusually, instead of using high magnetic fields and pulses, repeatedly magnetic waves with strength of as low as rare earth magnets are applied. These magnetic waves, generated by thermally controlling a Gadolinium (Gd) bulk with a rare earth magnet underneath, travel over the flat surface of a YBCO bulk and get trapped little by little. Thus, a very small magnetic field can be used to build up a very large magnetic field. In this paper, the modelling results of thermally actuated magnetic waves are presented showing how to transfer sequentially applied thermal pulses into magnetic waves. The experiment results of the magnetization of YBCO bulk are also presented to demonstrate how superconductors are progressively magnetized by small magnetic field

  17. Numerical analysis of thermally actuated magnets for magnetization of superconductors

    International Nuclear Information System (INIS)

    Li Quan; Yan Yu; Rawlings, Colin; Coombs, Tim

    2010-01-01

    Superconductors, such as YBCO bulks, have extremely high potential magnetic flux densities, comparing to rare earth magnets. Therefore, the magnetization of superconductors has attracted broad attention and contribution from both academic research and industry. In this paper, a novel technique is proposed to magnetize superconductors. Unusually, instead of using high magnetic fields and pulses, repeatedly magnetic waves with strength of as low as rare earth magnets are applied. These magnetic waves, generated by thermally controlling a Gadolinium (Gd) bulk with a rare earth magnet underneath, travel over the flat surface of a YBCO bulk and get trapped little by little. Thus, a very small magnetic field can be used to build up a very large magnetic field. In this paper, the modelling results of thermally actuated magnetic waves are presented showing how to transfer sequentially applied thermal pulses into magnetic waves. The experiment results of the magnetization of YBCO bulk are also presented to demonstrate how superconductors are progressively magnetized by small magnetic field

  18. Maglev performance of a double-layer bulk high temperature superconductor above a permanent magnet guideway

    International Nuclear Information System (INIS)

    Deng, Z; Wang, J; Zheng, J; Lin, Q; Zhang, Y; Wang, S

    2009-01-01

    In order to improve the performance of the present high temperature superconducting (HTS) maglev vehicle system, the maglev performance of single- and double-layer bulk high temperature superconductors (HTSC) was investigated above a permanent magnet guideway (PMG). It is found that the maglev performance of a double-layer bulk HTSC is not a simple addition of each layer's levitation and guidance force. Moreover, the applied magnetic field at the position of the upper layer bulk HTSC is not completely shielded by the lower layer bulk HTSC either. 53.5% of the levitation force and 27.5% of the guidance force of the upper layer bulk HTSC are excited in the double-layer bulk HTSC arrangement in the applied field-cooling condition and working gap, bringing a corresponding improvement of 16.9% and 8.8% to the conventional single-layer bulk HTSC. The present research implies that the cost performance of upper layer bulk HTSC is a little low for the whole HTS maglev system.

  19. Maglev performance of a double-layer bulk high temperature superconductor above a permanent magnet guideway

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Z; Wang, J; Zheng, J; Lin, Q; Zhang, Y; Wang, S [Applied Superconductivity Laboratory, Southwest Jiaotong University, Chengdu, 610031 (China)], E-mail: asclab@asclab.cn

    2009-05-15

    In order to improve the performance of the present high temperature superconducting (HTS) maglev vehicle system, the maglev performance of single- and double-layer bulk high temperature superconductors (HTSC) was investigated above a permanent magnet guideway (PMG). It is found that the maglev performance of a double-layer bulk HTSC is not a simple addition of each layer's levitation and guidance force. Moreover, the applied magnetic field at the position of the upper layer bulk HTSC is not completely shielded by the lower layer bulk HTSC either. 53.5% of the levitation force and 27.5% of the guidance force of the upper layer bulk HTSC are excited in the double-layer bulk HTSC arrangement in the applied field-cooling condition and working gap, bringing a corresponding improvement of 16.9% and 8.8% to the conventional single-layer bulk HTSC. The present research implies that the cost performance of upper layer bulk HTSC is a little low for the whole HTS maglev system.

  20. High current density in bulk YBa2Cu3O/sub x/ superconductor

    International Nuclear Information System (INIS)

    Salama, K.; Selvamanickam, V.; Gao, L.; Sun, K.

    1989-01-01

    A liquid phase processing method for the fabrication of bulk YBa 2 Cu 3 O/sub x/ superconductors with large current carrying capacity has been developed. Slow cooling through the peritectic transformation (1030--980 degree C) has been shown to control the microstructure of these superconductors. A cooling rate of 1 degree C/h in this temperature range has yielded a microstructure with long plate type, thick grains oriented over a wide area. Current density up to 18 500 A/cm 2 has been obtained by continuous direct current measurements and in excess of 62 000 A/cm 2 with pulse current of 10 ms duration and 75 000 A/cm 2 using 1 ms pulse. The strong magnetic field dependence observed in sintered bulk 1-2-3 superconductors is also minimized to a large extent where a current density in excess of 37 000 A/cm 2 is obtained in a field of 6000 G

  1. Doping-Induced Isotopic Mg11B2 Bulk Superconductor for Fusion Application

    Directory of Open Access Journals (Sweden)

    Qi Cai

    2017-03-01

    Full Text Available Superconducting wires are widely used for fabricating magnetic coils in fusion reactors. Superconducting magnet system represents a key determinant of the thermal efficiency and the construction/operating costs of such a reactor. In consideration of the stability of 11B against fast neutron irradiation and its lower induced radioactivation properties, MgB2 superconductor with 11B serving as the boron source is an alternative candidate for use in fusion reactors with a severe high neutron flux environment. In the present work, the glycine-doped Mg11B2 bulk superconductor was synthesized from isotopic 11B powder to enhance the high field properties. The critical current density was enhanced (103 A·cm−2 at 20 K and 5 T over the entire field in contrast with the sample prepared from natural boron.

  2. Enhancement of magnetic coupling between permanent magnets and bulk superconductors through iron embedding

    International Nuclear Information System (INIS)

    Seki, H.; Kurabayashi, H.; Suzuki, A.; Ikeda, M.; Akiyama, S.; Murakami, M.

    2009-01-01

    Magnetic torque can be transferred without contact through the coupling of permanent magnets (PM) and bulk superconductors (BSC). For this purpose, permanent magnets should have multiple pole configuration like NSNS. The magnitude of the transferable torque depends on the field strength and the gap between PM and BSC. It was found that the torque decays quickly with the gap. In order to enhance the strength of transferable magnetic torque, we prepared bulk Y-Ba-Cu-O superconductors for which Fe bars are embedded. Holes about 1 mm in diameter were mechanically drilled into bulk Y-Ba-Cu-O, and Fe bars about 0.9 mm in diameter were inserted followed by impregnation of Bi-Pb-Sn alloys with low melting points. The composite of Y-Ba-Cu-O and Fe bars attract magnetic fields generated from permanent magnet before cooling, and thereby magnetic coupling will be improved. We have found that the magnetic torque force can be greatly enhanced through iron embedding.

  3. Evaluation of mechanical properties of Dy123 bulk superconductors by 3-point bending tests

    International Nuclear Information System (INIS)

    Katagiri, K.; Hatakeyama, Y.; Sato, T.; Kasaba, K.; Shoji, Y.; Murakami, A.; Teshima, H.; Hirano, H.

    2006-01-01

    In order to evaluate the mechanical properties, such as Young's modulus and strength, of Dy123 bulk superconductors and those with 10 wt.% Ag 2 O, we performed 3-point bending tests at room (RT) and liquid nitrogen temperatures (LNT) using specimens cut from the bulks. The Young's modulus and the bending strength increased with decrease in temperature. In the tests loading in the direction of c-axis and ones perpendicular to it, Young's moduli were almost comparable at both RT and LNT. Although the strengths for both orientations were also comparable at LNT, those at RT were different. Young's moduli loaded in the direction of c-axis for Ag 2 O added bulk specimens, 127 GPa in average at RT, were almost comparable to those without Ag 2 O, and 134 GPa at LNT, were slightly lower than those without Ag 2 O. On the other hand, the strengths at both RT and LNT were enhanced by 20% by the Ag addition. The mechanical properties of Dy123 bulks without Ag 2 O were compared with those of Y123 bulks obtained previously. The Young's modulus for loading in the direction of c-axis was slightly lower, and the strength was comparable to those in Y123 bulks, respectively

  4. Magnetic torque transferring study for bulk High-Tc superconductors and permanent magnets

    International Nuclear Information System (INIS)

    Wongsatanawarid, A; Suzuki, A; Seki, H; Murakami, M

    2009-01-01

    The torque transferring mechanism taking place in a superconducting mixer design has been studied. Several coupling magnetic arrangements were investigated for more details in the engineering design. A bulk superconductor sample was used to study the torque forces for various cooling gaps, and the twist angle dependence was also monitored for the rotational stiffness in stability. The experimental data with four permanent magnet configurations have been studied in the present work. The maximum torque forces are summarized for usage of engineering design with various gaps. The torque/gap characteristics for four configurations were also measured for the optimisation of the torque at a designed operating gap.

  5. Levitation properties of superconducting magnetic bearings using superconducting coils and bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Arai, Yuuki; Seino, Hiroshi; Nagashima, Ken [Railway Technical Research Institute, 2-8-38 Hikari-cho, Kokubunji-shi, Tokyo 185-8540 (Japan)

    2010-11-15

    We have been developing a flywheel energy storage system (FESS) with 36 MJ energy capacity for a railway system with superconducting magnetic bearings (SMBs). We prepared two kinds of models using superconducting coils and bulk superconductors (SCs). One model demonstrated SMB load capacity of 20 kN and the other model proved non-contact stable levitation and non-contact rotation with SMBs. Combining these results, the feasibility of a 36 MJ energy capacity FESS with SMBs completely inside a cryostat has been confirmed. In this paper, we report the levitation properties of SMBs in these models.

  6. On the pinning performance analysis in bulk RE-123 twin-free superconductors

    Czech Academy of Sciences Publication Activity Database

    Jirsa, Miloš; Petrenko, Pavlo; Yao, X.; Muralidhar, M.

    463-465, - (2007), s. 353-356 ISSN 0921-4534. [International Symposium on Superconductivity /19./. Nagoya, 01.10.2006-03.10.2006] R&D Projects: GA MŠk 1P05ME728 Grant - others:MOST(CN) 2006CB601003; SSTC(CN) 055207077 Institutional research plan: CEZ:AV0Z10100520 Keywords : Penk effect * bulk RE-123 superconductors * pinning force scaling * pinning classification Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.079, year: 2007

  7. Levitation properties of superconducting magnetic bearings using superconducting coils and bulk superconductors

    International Nuclear Information System (INIS)

    Arai, Yuuki; Seino, Hiroshi; Nagashima, Ken

    2010-01-01

    We have been developing a flywheel energy storage system (FESS) with 36 MJ energy capacity for a railway system with superconducting magnetic bearings (SMBs). We prepared two kinds of models using superconducting coils and bulk superconductors (SCs). One model demonstrated SMB load capacity of 20 kN and the other model proved non-contact stable levitation and non-contact rotation with SMBs. Combining these results, the feasibility of a 36 MJ energy capacity FESS with SMBs completely inside a cryostat has been confirmed. In this paper, we report the levitation properties of SMBs in these models.

  8. Strongly enhanced irreversibility fields and Bose-glass behaviour in bulk YBCO with discontinuous columnar irradiation defects

    International Nuclear Information System (INIS)

    Fuchs, G; Nenkov, K; Krabbes, G; Weinstein, R; Gandini, A; Sawh, R; Mayes, B; Parks, D

    2007-01-01

    Flux pinning properties and irreversibility fields B irr (T) of melt-textured YBCO with discontinuous or multiple-in-line-damage (MILD) columnar defects produced by irradiation with high-energy U 238 ions were studied at a constant matching field of B φ = 10 T and for several energy losses between S e = 1.67 and 2.4 keV A -1 . With increasing S e and increasing length of the MILD pins, the critical current density j c (H,T) strongly increases and B irr (T) for fields along the c axis progressively shifts upwards reaching 9 T at 77 K. For S e = 2.4 keV A -1 , a pronounced kink is observed in B irr (T) at 8 T which is a strong indication of Bose-glass behaviour. The j c (H) dependence of this sample shows a peak at a low applied field B p . This peak effect is explained by the entanglement of vortices. It is argued that for MILD pins single vortices interact simultaneously with many short columnar defects in neighbouring ion trails resulting in an automatic splay in the vortex orientation. The observed decrease of B p with increasing temperature is estimated taking the increasing thermal fluctuations into account

  9. Orientation and thickness dependence of magnetic levitation force and trapped magnetic field of single grain YBa{sub 2}Cu{sub 3}O{sub 7-y} bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Jung, Y.; Go, S. J.; Joo, H. T. [Korea Science Academy of Korea Advanced Institute of Science and Technology, Pusan (Korea, Republic of); Lee, Y. J.; Park, S. D.; Jun, B. H.; KIm, C. J. [Neutron Utilization Technology Division, Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2017-03-15

    The effects of the crystallographic orientation and sample thickness on the magnetic levitation forces (F) and trapped magnetic field (B) of single grain YBCO bulk superconductors were examined. Single grain YBCO samples with a (001), (110) or (100) surface were used as the test samples. The samples used for the force-distance (F-d) measurement were cooled at 77 K without a magnetic field (zero field cooling, ZFC), whereas the samples used for the B measurement were cooled under the external magnetic field of a Nd-B-Fe permanent magnet (field cooling, FC). It was found that F and B of the (001) surface were higher than those of the (110) or (100) surface, which is attributed to the higher critical current density (J{sub c}) of the (001) surface. For the (001) samples with t=5–18 mm, the maximum magnetic levitation forces (F{sub max}s) of the ZFC samples were larger than 40 N. About 80% of the applied magnetic field was trapped in the FC samples. However, the F and B decreased rapidly as t decreased below 5 mm. There exists a critical sample thickness (t=5 mm for the experimental condition of this study) for maintaining the large levitation/trapping properties, which is dependent on the material properties and magnitude of the external magnetic fields.

  10. Development of superconducting magnetic bearing using superconducting coil and bulk superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Seino, H; Nagashima, K; Arai, Y [Railway Technical Research Institute, Hikari-cho 2-8-38, Kokubunji-shi, Tokyo (Japan)], E-mail: seino@rtri.or.jp

    2008-02-01

    The authors conducted a study on superconducting magnetic bearing, which consists of superconducting rotor and stator to apply the flywheel energy-storage system for railways. In this study, high temperature bulk superconductor (HTS bulk) was combined with superconducting coils to increase the load capacity of the bearing. In the first step of the study, the thrust rolling bearing was selected for application by using liquid nitrogen cooled HTS bulk. 60mm-diameter HTS bulks and superconducting coil which generated a high gradient of magnetic field by cusp field were adopted as a rotor and a stator for superconducting magnetic bearing, respectively. The results of the static load test and the rotation test, creep of the electromagnetic forces caused by static flux penetration and AC loss due to eccentric rotation were decreased to the level without any problems in substantial use by using two HTS bulks. In the result of verification of static load capacity, levitation force (thrust load) of 8900N or more was supportable, and stable static load capacity was obtainable when weight of 460kg was levitated.

  11. Development of superconducting magnetic bearing using superconducting coil and bulk superconductor

    International Nuclear Information System (INIS)

    Seino, H; Nagashima, K; Arai, Y

    2008-01-01

    The authors conducted a study on superconducting magnetic bearing, which consists of superconducting rotor and stator to apply the flywheel energy-storage system for railways. In this study, high temperature bulk superconductor (HTS bulk) was combined with superconducting coils to increase the load capacity of the bearing. In the first step of the study, the thrust rolling bearing was selected for application by using liquid nitrogen cooled HTS bulk. 60mm-diameter HTS bulks and superconducting coil which generated a high gradient of magnetic field by cusp field were adopted as a rotor and a stator for superconducting magnetic bearing, respectively. The results of the static load test and the rotation test, creep of the electromagnetic forces caused by static flux penetration and AC loss due to eccentric rotation were decreased to the level without any problems in substantial use by using two HTS bulks. In the result of verification of static load capacity, levitation force (thrust load) of 8900N or more was supportable, and stable static load capacity was obtainable when weight of 460kg was levitated

  12. Feasibility of introducing ferromagnetic materials to onboard bulk high-Tc superconductors to enhance the performance of present maglev systems

    Science.gov (United States)

    Deng, Zigang; Wang, Jiasu; Zheng, Jun; Zhang, Ya; Wang, Suyu

    2013-02-01

    Performance improvement is a long-term research task for the promotion of practical application of promising high-temperature superconducting (HTS) magnetic levitation (maglev) vehicle technologies. We studied the feasibility to enhance the performance of present HTS Maglev systems by introducing ferromagnetic materials to onboard bulk superconductors. The principle here is to make use of the high magnetic permeability of ferromagnetic materials to alter the flux distribution of the permanent magnet guideway for the enhancement of magnetic field density at the position of the bulk superconductors. Ferromagnetic iron plates were added to the upper surface of bulk superconductors and their geometric and positioning effects on the maglev performance were investigated experimentally. Results show that the guidance performance (stability) was enhanced greatly for a particular setup when compared to the present maglev system which is helpful in the application where large guidance forces are needed such as maglev tracks with high degrees of curves.

  13. Comparison of simulation and experiment on levitation force between GdBCO bulk superconductor and superconducting magnet

    Energy Technology Data Exchange (ETDEWEB)

    Araki, S., E-mail: satoshi@sum.sd.keio.ac.j [Department of System Design Engineering, Faculty of Science and Technology, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama 223-8522 (Japan); Nagashima, K.; Seino, H. [Railway Technical Research Institute, 2-8-38 Hikari-cho, Kokubunji, Tokyo 185-8540 (Japan); Murakami, T.; Sawa, K. [Department of System Design Engineering, Faculty of Science and Technology, Keio University, 3-14-1 Hiyoshi, Kohoku-ku, Yokohama 223-8522 (Japan)

    2009-10-15

    High temperature bulk superconductors have significant potential for various engineering applications such as a flywheel energy storage system. This system is expected to decrease the energy loss by using bulk superconductors for the bearing. Recently, the authors have developed a new superconducting magnet to realize large levitation force. In this system, the axial component of magnetic field is canceled each other but the radial component of magnetic field expects to be enhanced. Thus, it was expected that the large levitation force can be realized and its time relaxation will be decreased. And in the previous paper, the levitation force and its time relaxation were measured under the various conditions by using this new magnet. But it is difficult to consider what phenomenon has happened in the bulk from only experimental results. In addition the quantitative evaluation cannot be done only by the experimental results, for example, the influence of the magnetic field penetration and magnetic distribution around a bulk superconductor on the maximum force and so on. Thus, in this paper, the authors simulated the levitation force of bulk superconductor by using ELF/MAGIC, which is a three-dimensional electromagnetic analytical software. In the simulation the bulk was considered as a rigid body and the simulation was executed under the same conditions and model with the experiment. The distribution of magnetic field and the levitation force were obtained and discussed.

  14. Comparison of simulation and experiment on levitation force between GdBCO bulk superconductor and superconducting magnet

    International Nuclear Information System (INIS)

    Araki, S.; Nagashima, K.; Seino, H.; Murakami, T.; Sawa, K.

    2009-01-01

    High temperature bulk superconductors have significant potential for various engineering applications such as a flywheel energy storage system. This system is expected to decrease the energy loss by using bulk superconductors for the bearing. Recently, the authors have developed a new superconducting magnet to realize large levitation force. In this system, the axial component of magnetic field is canceled each other but the radial component of magnetic field expects to be enhanced. Thus, it was expected that the large levitation force can be realized and its time relaxation will be decreased. And in the previous paper, the levitation force and its time relaxation were measured under the various conditions by using this new magnet. But it is difficult to consider what phenomenon has happened in the bulk from only experimental results. In addition the quantitative evaluation cannot be done only by the experimental results, for example, the influence of the magnetic field penetration and magnetic distribution around a bulk superconductor on the maximum force and so on. Thus, in this paper, the authors simulated the levitation force of bulk superconductor by using ELF/MAGIC, which is a three-dimensional electromagnetic analytical software. In the simulation the bulk was considered as a rigid body and the simulation was executed under the same conditions and model with the experiment. The distribution of magnetic field and the levitation force were obtained and discussed.

  15. Trapped field recovery of bulk superconductor magnets by static field magnetization

    Science.gov (United States)

    Deng, Z.; Tsuzuki, K.; Miki, M.; Felder, B.; Hara, S.; Izumi, M.

    2011-11-01

    Thanks to the trapped field of bulk high-temperature superconductors, they can be used as field-pole magnets in the high temperature superconducting (HTS) rotating machines. For example, an output power of 10 kW at 720 rpm was realized by an average trapped field of 0.56 T of eight melt-textured GdBa2Cu3Oy (Gd-123) bulks at liquid nitrogen temperature in TUMSAT in 2004. Similarly to the HTS machines involving 1G or 2G wires, the trapped field of the bulk is possibly sensitive and even can be attenuated by the AC component field during the operation. Hence, it is necessary to recover the trapped field once being decreased to some extent in the practical application. From this point, we have investigated the trapped field recovery of HTS bulk magnets by static field magnetization in the paper. A series of different initial trapped fields after zero-field-cooling or field-cooling magnetization are used to simulate the attenuated trapped field. By comparing the trapped field peak and its distribution, the trapped field was found to be able to recover by the static field magnetization method with a stronger excitation field and the initial trapped flux inside the bulk also has an influence on the recovery process. The optimum recovery field was found to be about 2.5 times the saturated trapped field of the bulk at liquid nitrogen temperature, by which the bulk can regain the former best trapped field performance.

  16. Modification of the trapped field in bulk high-temperature superconductors as a result of the drilling of a pattern of artificial columnar holes

    International Nuclear Information System (INIS)

    Lousberg, Gregory P; Vanderbemden, Ph; Vanderheyden, B; Fagnard, J-F; Ausloos, M

    2010-01-01

    The trapped magnetic field is examined in bulk high-temperature superconductors that are artificially drilled along their c-axis. The influence of the hole pattern on the magnetization is studied and compared by means of numerical models and Hall probe mapping techniques. To this aim, we consider two bulk YBCO samples with a rectangular cross-section that are drilled each by six holes arranged either on a rectangular lattice (sample I) or on a centered rectangular lattice (sample II). For the numerical analysis, three different models are considered for calculating the trapped flux: (i), a two-dimensional (2D) Bean model neglecting demagnetizing effects and flux creep, (ii), a 2D finite-element model neglecting demagnetizing effects but incorporating magnetic relaxation in the form of an E - J power law, and, (iii), a 3D finite element analysis that takes into account both the finite height of the sample and flux creep effects. For the experimental analysis, the trapped magnetic flux density is measured above the sample surface by Hall probe mapping performed before and after the drilling process. The maximum trapped flux density in the drilled samples is found to be smaller than that in the plain samples. The smallest magnetization drop is found for sample II, with the centered rectangular lattice. This result is confirmed by the numerical models. In each sample, the relative drops that are calculated independently with the three different models are in good agreement. As observed experimentally, the magnetization drop calculated in the sample II is the smallest one and its relative value is comparable to the measured one. By contrast, the measured magnetization drop in sample (1) is much larger than that predicted by the simulations, most likely because of a change of the microstructure during the drilling process.

  17. Trapped field recovery of bulk superconductor magnets by static field magnetization

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Z., E-mail: zigang@kaiyodai.ac.jp [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology, Tokyo 135-8533 (Japan); Tsuzuki, K.; Miki, M.; Felder, B.; Hara, S.; Izumi, M. [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology, Tokyo 135-8533 (Japan)

    2011-11-15

    A series of initial trapped fields after ZFC or FC magnetization are used to simulate the attenuated trapped field. It is possible and easy to recover the lost trapped field and regain the best trapped field performance as before. In the re-magnetization process, the initial magnetic flux inside the bulk magnets will help to recover the trapped field. The optimum recovery field is recommended to be 2.5 times the saturation field of the bulk at LN2 temperature. Thanks to the trapped field of bulk high-temperature superconductors, they can be used as field-pole magnets in the high temperature superconducting (HTS) rotating machines. For example, an output power of 10 kW at 720 rpm was realized by an average trapped field of 0.56 T of eight melt-textured GdBa{sub 2}Cu{sub 3}O{sub y} (Gd-123) bulks at liquid nitrogen temperature in TUMSAT in 2004. Similarly to the HTS machines involving 1G or 2G wires, the trapped field of the bulk is possibly sensitive and even can be attenuated by the AC component field during the operation. Hence, it is necessary to recover the trapped field once being decreased to some extent in the practical application. From this point, we have investigated the trapped field recovery of HTS bulk magnets by static field magnetization in the paper. A series of different initial trapped fields after zero-field-cooling or field-cooling magnetization are used to simulate the attenuated trapped field. By comparing the trapped field peak and its distribution, the trapped field was found to be able to recover by the static field magnetization method with a stronger excitation field and the initial trapped flux inside the bulk also has an influence on the recovery process. The optimum recovery field was found to be about 2.5 times the saturated trapped field of the bulk at liquid nitrogen temperature, by which the bulk can regain the former best trapped field performance.

  18. Anisotropy and intergrain current density in oriented grained bulk YBa2Cu3Ox superconductor

    International Nuclear Information System (INIS)

    Selvamanickam, V.; Salama, K.

    1990-01-01

    The intergrain transport current density and its anisotropy have been studied in oriented grained bulk YBa 2 Cu 3 O x superconductors fabricated by the liquid phase processing method. Current density measurements were performed on oriented grained samples with the transport current aligned at different angles to the a-b plane. In these measurements, the transport current passed through several oriented grain boundaries. The results indicate that the critical current density drops rapidly when the transport current flows at small angles to the a-b plane and then decreases slowly at larger angles. At 77 K and zero magnetic field, an anisotropy ratio of about 25 is observed between J c along a-b plane and that perpendicular to the plane. Further, the critical current density in these samples is found to depend weakly on magnetic field even though the current crosses grain boundaries. These results support the notion that grain boundaries of these superconductors are different in nature from those of solid-state sintered samples.

  19. Alternating-current transport losses of melt-cast processed Bi-2212 bulk superconductor bars

    International Nuclear Information System (INIS)

    Tsukamoto, T; Inada, R; Inagaki, N; Andoh, H; Sugiura, T; Oota, A

    2003-01-01

    Using a melt-casting method, we have fabricated two pieces of Bi-2212 bulk superconductor bar with square and rectangular cross-sections, and we have investigated the alternating-current (ac) transport self-field losses at 77 K. Despite the main contribution of hysteresis loss of the superconductor, there is some difference in the loss behaviour between these two samples. To elucidate the origin, we make numerical calculations on the ac transport self-field losses as a function of current amplitude I 0 below the critical current I c . At a fixed I 0 , the calculated values using the uniform J c distribution and the actual cross-sectional geometry are much higher than the experimental data for the sample with a square cross-section 7.5 x 7.5 mm 2 , while there is good agreement between the calculation and the experiment for the sample with a rectangular cross-section 4.5 x 13.6 mm 2 . The discrepancy appearing in the sample with a square cross-section is ascribed to the actual J c distribution, which is confirmed by critical current measurements when scraping off the sample. The local J c value decreases significantly in going from the surface to the interior of the sample. This suppresses the extension of the flux-penetration region to the interior under ac current transmission and lowers the loss generation compared with the calculated results obtained by the uniform J c distribution

  20. Upper critical and irreversibility fields in Ni- and Co-doped pnictide bulk superconductors

    Science.gov (United States)

    Nikolo, Martin; Singleton, John; Solenov, Dmitry; Jiang, Jianyi; Weiss, Jeremy; Hellstrom, Eric

    2018-05-01

    A comprehensive study of upper critical and irreversibility magnetic fields in Ba(Fe0.95Ni0.05)2As2 (large grain and small grain samples), Ba(Fe0.94Ni0.06)2As2, Ba(Fe0.92Co0.08)2As2, and Ba(Fe0.92Co0.09)2As2 polycrystalline bulk pnictide superconductors was made in pulsed fields of up to 65 T. The full magnetic field-temperature (H-T) phase diagrams, starting at 1.5 K, were measured. The higher temperature, upper critical field Hc2 data are well described by the one-band Werthamer, Helfand, and Hohenberg (WHH) model. At low temperatures, the experimental data depart from the fitted WHH curves, suggesting an emergence of a new phase that could be attributed to the Fulde-Ferrell-Larkin-Ovchinnikov (FFLO) state. The large values of the Maki fitting parameter α indicate that the Zeeman pair breaking dominates over the orbital pair breaking and spin-paramagnetic pair-breaking effect is significant in these materials. Possible multi-band structure of these materials is lumped into effective parameters of the single-band model. Table of measured physical parameters allows us to compare these pnictide superconductors for different Co- and Ni- doping levels and granularity.

  1. Superconductor bearings, flywheels and transportation

    International Nuclear Information System (INIS)

    Werfel, F N; Floegel-Delor, U; Rothfeld, R; Riedel, T; Goebel, B; Wippich, D; Schirrmeister, P

    2012-01-01

    This paper describes the present status of high temperature superconductors (HTS) and of bulk superconducting magnet devices, their use in bearings, in flywheel energy storage systems (FESS) and linear transport magnetic levitation (Maglev) systems. We report and review the concepts of multi-seeded REBCO bulk superconductor fabrication. The multi-grain bulks increase the averaged trapped magnetic flux density up to 40% compared to single-grain assembly in large-scale applications. HTS magnetic bearings with permanent magnet (PM) excitation were studied and scaled up to maximum forces of 10 kN axially and 4.5 kN radially. We examine the technology of the high-gradient magnetic bearing concept and verify it experimentally. A large HTS bearing is tested for stabilizing a 600 kg rotor of a 5 kWh/250 kW flywheel system. The flywheel rotor tests show the requirement for additional damping. Our compact flywheel system is compared with similar HTS–FESS projects. A small-scale compact YBCO bearing with in situ Stirling cryocooler is constructed and investigated for mobile applications. Next we show a successfully developed modular linear Maglev system for magnetic train operation. Each module levitates 0.25t at 10 mm distance during one-day operation without refilling LN 2 . More than 30 vacuum cryostats containing multi-seeded YBCO blocks are fabricated and are tested now in Germany, China and Brazil.

  2. Flux motion in Y-Ba-Cu-O bulk superconductors during pulse field magnetization

    International Nuclear Information System (INIS)

    Yoshizawa, K; Nariki, S; Sakai, N; Murakami, M; Hirabayasi, I; Takizawa, T

    2004-01-01

    We have studied the relationship between the magnetization and temperature change in Y-Ba-Cu-O bulk superconductor during pulse field magnetization (PFM). The flux motion was monitored using both Hall sensors and pick-up coils that are placed on a surface of a Y-Ba-Cu-O disc having dimensions of 15 mm in diameter and 0.95 mm in thickness. The peak value of the field was varied from 0.2 to 0.8 T. The effect of the static bias field was also studied in the range of 0-3 T. The temperature of the sample surface was measured using a resistance temperature sensor. The temperature increased with the magnitude of the applied pulsed magnetic field, and the amount of temperature rise decreased with increasing static bias field

  3. Coasting characteristic of the flywheel system under anisotropy effect of bulk high temperature superconductors

    Science.gov (United States)

    Wu, J. F.; Li, Y.

    2014-10-01

    High-temperature superconductors (HTSCs) array with aligned growth section boundary (GSB) pattern (AGSBP) exhibits larger levitation force and suppression of levitation force decay above a permanent magnet guideway (PMG) compared with misaligned GSB pattern (MGSBP) has been studied in maglev train application (Zheng et al., 2013). This result maybe helpful and support a new way for the HTS bearing design for flywheel systems. So, in this paper, we further examine this growth anisotropy effect on the maglev performance of flywheel system. Levitation force and coasting time were investigated from the point-view of HTS flywheel applications. The GS/GSB alignment of AGSBP bulk HTSCs produces larger levitation force than that of MGSBP, but the coasting time is shorter than that of MGSBP, that is to say, the electric magnetic drag force with AGSBP is larger than that of MGSBP. This result may also exist in the maglev guideline when the maglev train stops freely.

  4. High temperature superconducting YBCO microwave filters

    Science.gov (United States)

    Aghabagheri, S.; Rasti, M.; Mohammadizadeh, M. R.; Kameli, P.; Salamati, H.; Mohammadpour-Aghdam, K.; Faraji-Dana, R.

    2018-06-01

    Epitaxial thin films of YBCO high temperature superconductor are widely used in telecommunication technology such as microwave filter, antenna, coupler and etc., due to their lower surface resistance and lower microwave loss than their normal conductor counterparts. Thin films of YBCO were fabricated by PLD technique on LAO substrate. Transition temperature and width were 88 K and 3 K, respectively. A filter pattern was designed and implemented by wet photolithography method on the films. Characterization of the filter at 77 K has been compared with the simulation results and the results for a made gold filter. Both YBCO and gold filters show high microwave loss. For YBCO filter, the reason may be due to the improper contacts on the feedlines and for gold filter, low thickness of the gold film has caused the loss increased.

  5. Crack propagation and acoustic emission behavior of silver-added Dy123 bulk superconductor

    International Nuclear Information System (INIS)

    Yoneda, K.; Ye, J.

    2006-01-01

    The relationship between the crack propagation process and acoustic emission (AE) signals was investigated in 3-point bending tests in which stress loading was applied parallel to the c-axis of U-notched specimens cut from Dy123 bulk superconductors with and without the addition of silver (Ag). The average bending stress of the specimens containing 10 mass% of Ag was approximately 20% higher than that of the specimens without the addition of Ag; the total AE energy of the former specimens was approximately fourfold greater than that of the latter specimens. However, cracks initiated in all of the specimens at a bending stress level of around 25 MPa, regardless of the presence or absence of Ag. An analysis of the amplitude distribution revealed that the failure mode was matrix failure in both types of specimens. Cracks in the low-strength specimens without Ag propagated between gas holes or along cleavage planes, and the AE event count and total AE energy were low. By contrast, the high-strength Ag-added specimens had fewer gas holes and cleavage cracks on account of their improved microstructure. In these samples, crack propagation orthogonal to the cleavage planes caused Ag particles to separate from the matrix and induced cleavage cracks. The addition of Ag presumably had the effect of inhibiting crack propagation, with the result that the AE event count and AE energy increased. The results of this study indicate that failure phenomena can be interpreted by evaluating the amplitude distribution, AE event count and total AE energy. This suggests that the AE method is also applicable to evaluations of bulk superconductors

  6. Improving magnetic properties of MgB{sub 2} bulk superconductors by synthetic engine oil treatment

    Energy Technology Data Exchange (ETDEWEB)

    Taylan Koparan, E., E-mail: etaylan20@gmail.com [Department of Science Education, Eregli Faculty of Education, Bulent Ecevit University, TR-67300, Zonguldak (Turkey); Savaskan, B. [Energy Systems Engineering, Faculty of Technology, Karadeniz Technical University, 61830, Of, Trabzon (Turkey); Yanmaz, E. [Department of Mechatronics, Faculty of Engineering and Architecture, İstanbul Gelişim University, İstanbul (Turkey)

    2016-08-15

    Highlights: • The effects of synthetic engine oil treatment on magnetic properties of bulk MgB{sub 2} superconductors has been first time investigated and reported. • Synthetic engine oil used as a product which is cheap and a rich carbon source obviously has improved the superconducting magnetic properties of MgB{sub 2}. • The critical current density of all of MgB{sub 2} samples immersed at different standby time in engine oil in whole field range has been better than that of the pure MgB{sub 2} sample. • The MgB{sub 2} sample immersed at 300 min standby time in synthetic engine oil has the best performance compared to other samples. - Abstract: The present study focuses on the effects of standby time of the MgB{sub 2} samples immersed in synthetic engine oil on the critical current density ( J{sub c}(H)), magnetic field dependence of the pinning force density f{sub p}(b) and T{sub c} performances of MgB{sub 2} bulk superconductors. Synthetic engine oil was used as a product which is cheap and a rich carbon source. Manufactured MgB{sub 2} pellet samples were immersed at different standby time of 30 min, 120 min, 300 min and 1440 min in synthetic engine oil after the first heating process. Finally, MgB{sub 2} samples immersed in synthetic engine oil were sintered at 1000 °C and kept for 15 min in Ar atmosphere. The critical current density of all of MgB{sub 2} samples immersed at different standby time in engine oil in whole field range was better than that of the pure MgB{sub 2} sample because of the number of the pinning centers. The MgB{sub 2} sample immersed at 300 min standby time in synthetic engine oil has the best performance compared to other samples. The J{sub c} value for the pure sample is 2.0 × 10{sup 3} A/cm{sup 2}, whereas for the MgB{sub 2} sample immersed at 300 min standby time in engine oil the J{sub c} is enhanced to 4.8 × 10{sup 3} A/cm{sup 2} at 5 K and 3 T. The superconducting transition temperature (T{sub c}) did not change

  7. Improving magnetic properties of MgB_2 bulk superconductors by synthetic engine oil treatment

    International Nuclear Information System (INIS)

    Taylan Koparan, E.; Savaskan, B.; Yanmaz, E.

    2016-01-01

    Highlights: • The effects of synthetic engine oil treatment on magnetic properties of bulk MgB_2 superconductors has been first time investigated and reported. • Synthetic engine oil used as a product which is cheap and a rich carbon source obviously has improved the superconducting magnetic properties of MgB_2. • The critical current density of all of MgB_2 samples immersed at different standby time in engine oil in whole field range has been better than that of the pure MgB_2 sample. • The MgB_2 sample immersed at 300 min standby time in synthetic engine oil has the best performance compared to other samples. - Abstract: The present study focuses on the effects of standby time of the MgB_2 samples immersed in synthetic engine oil on the critical current density ( J_c(H)), magnetic field dependence of the pinning force density f_p(b) and T_c performances of MgB_2 bulk superconductors. Synthetic engine oil was used as a product which is cheap and a rich carbon source. Manufactured MgB_2 pellet samples were immersed at different standby time of 30 min, 120 min, 300 min and 1440 min in synthetic engine oil after the first heating process. Finally, MgB_2 samples immersed in synthetic engine oil were sintered at 1000 °C and kept for 15 min in Ar atmosphere. The critical current density of all of MgB_2 samples immersed at different standby time in engine oil in whole field range was better than that of the pure MgB_2 sample because of the number of the pinning centers. The MgB_2 sample immersed at 300 min standby time in synthetic engine oil has the best performance compared to other samples. The J_c value for the pure sample is 2.0 × 10"3 A/cm"2, whereas for the MgB_2 sample immersed at 300 min standby time in engine oil the J_c is enhanced to 4.8 × 10"3 A/cm"2 at 5 K and 3 T. The superconducting transition temperature (T_c) did not change with the increasing standby time of the samples in synthetic engine oil at all. The best diamagnetic property was

  8. Superconductors

    International Nuclear Information System (INIS)

    1988-01-01

    The chapter 6.3 p. 143 to 153 of this book deals with superconductors 19 items are briefly presented with address of manufacturer or laboratory to contact, mainly in the USA or Japan. In particular magnets, films, high temperature superconductors and various applications are presented [fr

  9. Heat conduction and thermal stabilization in YBCO tape

    Indian Academy of Sciences (India)

    Yttrium barium copper oxide (YBCO) based 2G/3G tech- nical superconductors ... off-normal scenarios, these superconductors do exceed in an irreversible fashion .... ler G 2007 Factory testing of a 36·5 MW high temperature superconducting ...

  10. Feasibility of introducing ferromagnetic materials to onboard bulk high-Tc superconductors to enhance the performance of present maglev systems

    International Nuclear Information System (INIS)

    Deng, Zigang; Wang, Jiasu; Zheng, Jun; Zhang, Ya; Wang, Suyu

    2013-01-01

    Highlights: ► Ferromagnetic materials guide the flux distribution of the PMG to bulk positions. ► With ferromagnetic materials, guidance performance can be enhanced greatly. ► A new HTS Maglev system with onboard ferromagnetic materials is designed. ► The design can meet large guidance force requirements for practical applications. -- Abstract: Performance improvement is a long-term research task for the promotion of practical application of promising high-temperature superconducting (HTS) magnetic levitation (maglev) vehicle technologies. We studied the feasibility to enhance the performance of present HTS Maglev systems by introducing ferromagnetic materials to onboard bulk superconductors. The principle here is to make use of the high magnetic permeability of ferromagnetic materials to alter the flux distribution of the permanent magnet guideway for the enhancement of magnetic field density at the position of the bulk superconductors. Ferromagnetic iron plates were added to the upper surface of bulk superconductors and their geometric and positioning effects on the maglev performance were investigated experimentally. Results show that the guidance performance (stability) was enhanced greatly for a particular setup when compared to the present maglev system which is helpful in the application where large guidance forces are needed such as maglev tracks with high degrees of curves

  11. Superconductors

    CERN Document Server

    Narlikar, A V

    2014-01-01

    Superconductors is neither about basic aspects of superconductivity nor about its applications, but its mainstay is superconducting materials. Unusual and unconventional features of a large variety of novel superconductors are presented and their technological potential as practical superconductors assessed. The book begins with an introduction to basic aspects of superconductivity. The presentation is readily accessible to readers from a diverse range of scientific and technical disciplines, such as metallurgy, materials science, materials engineering, electronic and device engineering, and chemistry. The derivation of mathematical formulas and equations has been kept to a minimum and, wherever necessary, short appendices with essential mathematics have been added at the end of the text. The book is not meant to serve as an encyclopaedia, describing each and every superconductor that exists, but focuses on important milestones in their exciting development.

  12. Growth anisotropy effect of bulk high temperature superconductors on the levitation performance in the applied magnetic field

    Science.gov (United States)

    Zheng, J.; Liao, X. L.; Jing, H. L.; Deng, Z. G.; Yen, F.; Wang, S. Y.; Wang, J. S.

    2013-10-01

    Growth anisotropies of bulk high temperature superconductors (HTSCs) fabricated by a top-seeded melt texture growth process, that is, different pinning effect in the growth sectors (GSs) and growth sector boundaries (GSBs), possess effect on the macro flux trapping and levitation performance of bulk HTSCs. Previous work (Physics Procedia, 36 (2012) 1043) has found that the bulk HTSC array with aligned GSB pattern (AGSBP) exhibits better capability for levitation and suppression of levitation force decay above a permanent magnet guideway (PMG) compared with misaligned GSB pattern (MGSBP). In this paper, we further examine this growth anisotropy effect on the maglev performance of a double-layer bulk HTSC. In contrast to reported trapped flux cases (Supercond. Sci. Technol. 19 (2006) S466), the two superposed bulk HTSCs with same AGSBP with PMG are found to show better maglev performance. These series of results are helpful and support a new way for the performance optimization of present HTS maglev systems.

  13. Effects of seed geometry on the crystal growth and the magnetic properties of single grain REBCO bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Hwi Joo; Lee, Hee Gyoun [Korea Polytechnic University, Siheung (Korea, Republic of); Park, Soon Dong; Jun, Bung Hyack; Kim, Chan Joong [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2017-09-15

    This study presents that the orientation and the geometry of seed affect on the growth behavior of melt processed single grain REBCO bulk superconductor and its magnetic properties. The effects of seed geometry have been investigated for thin 30mm x 30mm rectangular powder compacts. Single grain REBCO bulk superconductors have been grown successfully by a top seed melt growth method for 8-mm thick vertical thin REBCO slab. Asymmetric structures have been developed at the front surface and at the rear surface of the specimen. Higher magnetic properties have been obtained for the specimen that c-axis is normal to the specimen surface. The relationships between microstructure, grain growth and magnetic properties have been discussed.

  14. Improvement of the field-trapping capabilities of bulk Nd Ba Cu O superconductors using Ba Cu O substrates

    Science.gov (United States)

    Matsui, Motohide; Nariki, Shinya; Sakai, Naomichi; Iwafuchi, Kengo; Murakami, Masato

    2006-07-01

    We used Ba-Cu-O substrates to fabricate bulk Nd-Ba-Cu-O superconductors using a top-seeded melt-growth method. There were several advantages for the use of Ba-Cu-O substrate compared to conventional substrate materials such as MgO, ZrO2, Al2O3, RE123 and RE211 (RE = rare earth). The Ba-Cu-O did not react with the precursor and minimized liquid loss. Accordingly, the introduction of large-sized cracks was suppressed. We also found that Tc values were high at the bottom regions, which was ascribed to the beneficial effect of Ba-Cu-O in suppressing Nd/Ba substitution. As a result, we obtained bulk Nd-Ba-Cu-O superconductors that exhibited fairly good field-trapping capabilities, even at the bottom surfaces.

  15. Flux pinning characteristics of YBCO coated conductor

    International Nuclear Information System (INIS)

    Matsushita, T.; Watanabe, T.; Fukumoto, Y.; Yamauchi, K.; Kiuchi, M.; Otabe, E.S.; Kiss, T.; Watanabe, T.; Miyata, S.; Ibi, A.; Muroga, T.; Yamada, Y.; Shiohara, Y.

    2005-01-01

    Flux pinning properties of PLD-processed YBCO coated conductors deposited on IBAD substrate are investigated. The thickness of YBCO layer is changed in the range of 0.27-1.0 μm. The thickness dependence of critical current density, n-value and irreversibility field are measured in a wide range of magnetic field. The results are compared with the theoretical flux creep-flow model. It is found that these pinning properties are strongly influenced by the thickness as well as the pinning strength. Optimum condition for high field application of this superconductor is discussed

  16. Coasting characteristic of the flywheel system under anisotropy effect of bulk high temperature superconductors

    International Nuclear Information System (INIS)

    Wu, J.F.; Li, Y.

    2014-01-01

    Highlights: • Coasting time was investigated from the point-view of HTS flywheel applications. • The coasting time of aligned growth section boundary pattern (AGSBP) is shorter than that of MGSBP. • The electric magnetic drag force with AGSBP is larger than that of MGSBP. • This result may also exist in the maglev guideline when the maglev train stops freely. - Abstract: High-temperature superconductors (HTSCs) array with aligned growth section boundary (GSB) pattern (AGSBP) exhibits larger levitation force and suppression of levitation force decay above a permanent magnet guideway (PMG) compared with misaligned GSB pattern (MGSBP) has been studied in maglev train application (Zheng et al., 2013). This result maybe helpful and support a new way for the HTS bearing design for flywheel systems. So, in this paper, we further examine this growth anisotropy effect on the maglev performance of flywheel system. Levitation force and coasting time were investigated from the point-view of HTS flywheel applications. The GS/GSB alignment of AGSBP bulk HTSCs produces larger levitation force than that of MGSBP, but the coasting time is shorter than that of MGSBP, that is to say, the electric magnetic drag force with AGSBP is larger than that of MGSBP. This result may also exist in the maglev guideline when the maglev train stops freely

  17. Effects of seed orientation on the growth behavior of single grain REBCO bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Hee Gyoun [Korea Polytechnic University, Siheung (Korea, Republic of)

    2017-06-15

    This study presents a simple method to control the seed orientation which leads to the various growth characteristics of a single grain REBCO (RE: rare-earth elements) bulk superconductors. Seed orientation was varied systematically from c-axis to a-axis with every 30 degree rotation around b-axis. Orientations of a REBCO single grain was successfully controlled by placing the seed with various angles on the prismatic indent prepared on the surface of REBCO powder compacts. Growth pattern was changed from cubic to rectangular when the seed orientation normal to compact surface was varied from c-axis to a-axis. Macroscopic shape change has been explained by the variation of the wetting angle of un-reacted melt depending on the interface energy between YBa2Cu3O7-y (Y123) grain and melt. Higher magnetic levitation force was obtained for the specimen prepared using tilted seed with an angle of 30 degree rotation around b-axis.

  18. Coasting characteristic of the flywheel system under anisotropy effect of bulk high temperature superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Wu, J.F., E-mail: wujf@ciomp.ac.cn; Li, Y.

    2014-10-15

    Highlights: • Coasting time was investigated from the point-view of HTS flywheel applications. • The coasting time of aligned growth section boundary pattern (AGSBP) is shorter than that of MGSBP. • The electric magnetic drag force with AGSBP is larger than that of MGSBP. • This result may also exist in the maglev guideline when the maglev train stops freely. - Abstract: High-temperature superconductors (HTSCs) array with aligned growth section boundary (GSB) pattern (AGSBP) exhibits larger levitation force and suppression of levitation force decay above a permanent magnet guideway (PMG) compared with misaligned GSB pattern (MGSBP) has been studied in maglev train application (Zheng et al., 2013). This result maybe helpful and support a new way for the HTS bearing design for flywheel systems. So, in this paper, we further examine this growth anisotropy effect on the maglev performance of flywheel system. Levitation force and coasting time were investigated from the point-view of HTS flywheel applications. The GS/GSB alignment of AGSBP bulk HTSCs produces larger levitation force than that of MGSBP, but the coasting time is shorter than that of MGSBP, that is to say, the electric magnetic drag force with AGSBP is larger than that of MGSBP. This result may also exist in the maglev guideline when the maglev train stops freely.

  19. Fabrication and characterizations of the BSCCO-2212/SrSO4 bulk superconductors

    International Nuclear Information System (INIS)

    Kim, Kyu Tae; Jang, Seok Hern; Park, Eui Cheol; Hwang, Sumin; Joo, Jin Hoo; Hong, Gye Won; Kim, Chan Joong; Kim, Hye Rim; Hyun, Ok Bae

    2006-01-01

    We fabricated Bi-2212/SrSO 4 bulk superconductors by the casting process and evaluated the effects of the powder mixing method and annealing temperature on the texture, microstructure, and critical current. In the process, the Bi-2212 powders were mixed with SrSO 4 by hand-mixing(HM) and planetary ball milling(PBM) method and then the powder mixtures were melted at 1100 - 1200 degrees C, solidified, and annealed. We observed that the rod made by the PBM had a more homogeneous microstructure and smaller SrSO 4 and second phases than that of the rod made by the HM, resulting in increased I c . The I c of the rod also depended on the annealing temperature and the highest I c was obtained to be 200 A when prepared by HM at 1200 degrees C and annealed at 810 degrees C which is probably due to the moderate density and 2212 texture and the smaller and less second phase compared to that at higher temperature. The possible causes of the variations of I c with the powder mixing method and annealing temperature were related to the microstructural evolution based on the SEM, EPMA, and DTA analyses.

  20. Effect of silver addition on the mechanical and field trapping properties of Gd-Ba-Cu-O bulk superconductors

    CERN Document Server

    Nariki, S; Matsui, M; Murakami, M

    2002-01-01

    The effect of Ag addition on the microstructure and the mechanical and field trapping properties of Gd-Ba-Cu-O bulk superconductor has been investigated. The single grain Gd-Ba-Cu-O bulk superconductors 32 mm in diameter were fabricated with 0-30 mass%Ag/sub 2/O additions by the melt growth method under controlled oxygen partial pressure of 1.0%. From microscopic observations, it was found that the macro- cracks in the a-b plane decreased with Ag addition. The three-point bending test showed that the average strength of Ag-free bulk was 69 MPa at room temperature, while the strength was dramatically improved to 110-115 MPa with 10-30 mass%Ag/sub 2/O additions. The trapped magnetic field of Ag-free bulk sample was 1.3 T at 77 K. The trapped field of bulk Gd-Ba-Cu-O samples with 10-20 mass%Ag/sub 2/O exhibited high values of 1.8-2.0 T at 77 K. However, the trapped field of the sample with 30 mass%Ag/sub 2/O addition was lowered to 1.1 T with decreasing the critical current density. The trapped field of Ag- adde...

  1. Nano-engineered pinning centres in YBCO superconducting films

    Energy Technology Data Exchange (ETDEWEB)

    Crisan, A., E-mail: adrian.crisan@infim.ro [National Institute for Materials Physics Bucharest, 105 bis Atomistilor Str., 077125 Magurele (Romania); School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Dang, V.S. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Nano and Energy Center, VNU Hanoi University of Science, 334 Nguyen Trai, Thanh Xuan, Hanoi (Viet Nam); Mikheenko, P. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Department of Physics, University of Oslo, P.O. Box 1048 Blindern, N-0316 Oslo (Norway)

    2017-02-15

    Highlights: • Power applications of YBCO films/coated conductors in technological relevant magnetic fields requires nano-engineered pinning centre. • Three approaches have been proposed: substrate decoration, quasi-multilayers, and targets with secondary phase nano-inclusions. • Combination of all three approaches greatly increased critical current in YBCO films. • Bulk pinning force, pinning potential, and critical current density are estimated and discussed in relation with the type and strength of pinning centres related to the defects evidenced by Transmission Electron Microscopy. - Abstract: For practical applications of superconducting materials in applied magnetic fields, artificial pinning centres in addition to natural ones are required to oppose the Lorentz force. These pinning centres are actually various types of defects in the superconductor matrix. The pinning centres can be categorised on their dimension (volume, surface or point) and on their character (normal cores or Δκ cores). Different samples have been produced by Pulsed Laser Deposition, with various thicknesses, temperatures and nanostructured additions to the superconducting matrix. They have been characterized by SQUID Magnetic Properties Measurement System and Physical Properties Measurement System, as well as by Transmission Electron Microscopy (TEM). Correlations between pinning architecture, TEM images, and critical currents at various fields and field orientations will be shown for a large number of YBa{sub 2}Cu{sub 3}O{sub x} films with various types and architectures of artificial pinning centres.

  2. Growth anisotropy effect of bulk high temperature superconductors on the levitation performance in the applied magnetic field

    International Nuclear Information System (INIS)

    Zheng, J.; Liao, X.L.; Jing, H.L.; Deng, Z.G.; Yen, F.; Wang, S.Y.; Wang, J.S.

    2013-01-01

    Highlights: • The single-layer bulk HTSC with AGSBP obtains better levitation performance than that of MGSBP. • The double-layer bulk with AGSBP obtains better levitation performance than that of MGSBP too. • The double-layer bulk finding is contrast to MGSBP if pursuing high trapped field. • The optimization is highlighted by simple and easy operation, thus economical in the practice. -- Abstract: Growth anisotropies of bulk high temperature superconductors (HTSCs) fabricated by a top-seeded melt texture growth process, that is, different pinning effect in the growth sectors (GSs) and growth sector boundaries (GSBs), possess effect on the macro flux trapping and levitation performance of bulk HTSCs. Previous work (Physics Procedia, 36 (2012) 1043) has found that the bulk HTSC array with aligned GSB pattern (AGSBP) exhibits better capability for levitation and suppression of levitation force decay above a permanent magnet guideway (PMG) compared with misaligned GSB pattern (MGSBP). In this paper, we further examine this growth anisotropy effect on the maglev performance of a double-layer bulk HTSC. In contrast to reported trapped flux cases (Supercond. Sci. Technol. 19 (2006) S466), the two superposed bulk HTSCs with same AGSBP with PMG are found to show better maglev performance. These series of results are helpful and support a new way for the performance optimization of present HTS maglev systems

  3. Growth anisotropy effect of bulk high temperature superconductors on the levitation performance in the applied magnetic field

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, J., E-mail: jzheng@swjtu.edu.cn; Liao, X.L.; Jing, H.L.; Deng, Z.G.; Yen, F.; Wang, S.Y.; Wang, J.S.

    2013-10-15

    Highlights: • The single-layer bulk HTSC with AGSBP obtains better levitation performance than that of MGSBP. • The double-layer bulk with AGSBP obtains better levitation performance than that of MGSBP too. • The double-layer bulk finding is contrast to MGSBP if pursuing high trapped field. • The optimization is highlighted by simple and easy operation, thus economical in the practice. -- Abstract: Growth anisotropies of bulk high temperature superconductors (HTSCs) fabricated by a top-seeded melt texture growth process, that is, different pinning effect in the growth sectors (GSs) and growth sector boundaries (GSBs), possess effect on the macro flux trapping and levitation performance of bulk HTSCs. Previous work (Physics Procedia, 36 (2012) 1043) has found that the bulk HTSC array with aligned GSB pattern (AGSBP) exhibits better capability for levitation and suppression of levitation force decay above a permanent magnet guideway (PMG) compared with misaligned GSB pattern (MGSBP). In this paper, we further examine this growth anisotropy effect on the maglev performance of a double-layer bulk HTSC. In contrast to reported trapped flux cases (Supercond. Sci. Technol. 19 (2006) S466), the two superposed bulk HTSCs with same AGSBP with PMG are found to show better maglev performance. These series of results are helpful and support a new way for the performance optimization of present HTS maglev systems.

  4. Influence of crossed fields in structures combining large grain, bulk (RE)BCO superconductors and soft ferromagnetic discs

    International Nuclear Information System (INIS)

    Philippe, M P; Fagnard, J F; Wéra, L; Vanderheyden, B; Vanderbemden, P; Morita, M; Nariki, S; Teshima, H; Caps, H

    2016-01-01

    Bulk (RE)BCO superconductors are able to trap record magnetic fields and can be used as powerful permanent magnets in various engineering applications such as rotating machines and magnetic bearings. When such superconducting (SC) “trapped field magnets” are combined to a ferromagnetic (FM) disc, the total magnetic moment is increased with respect to that of the superconductor alone. In the present work, we study experimentally the magnetic behaviour of such hybrid FM/SC structures when they are subjected to cycles of applied field that are orthogonal to their permanent magnetization, i.e. a “crossed-field” configuration. Experimental results show that the usual “crossed-field demagnetization” caused by the cycles of transverse field is strongly reduced in the presence of the ferromagnet. (paper)

  5. Materials process and applications of single grain (RE)-Ba-Cu-O bulk high-temperature superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Li Beizhan; Zhou Difan; Xu Kun; Hara, Shogo; Tsuzuki, Keita; Miki, Motohiro; Felder, Brice; Deng Zigang [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology (TUMSAT), 2-1-6, Etchu-jima, Koto-ku, Tokyo 135-8533 (Japan); Izumi, Mitsuru, E-mail: izumi@kaiyodai.ac.jp [Laboratory of Applied Physics, Department of Marine Electronics and Mechanical Engineering, Tokyo University of Marine Science and Technology (TUMSAT), 2-1-6, Etchu-jima, Koto-ku, Tokyo 135-8533 (Japan)

    2012-11-20

    This paper reviews recent advances in the melt process of (RE)-Ba-Cu-O [(RE)BCO, where RE represents a rare earth element] single grain high-temperature superconductors (HTSs), bulks and its applications. The efforts on the improvement of the magnetic flux pinning with employing the top-seeded melt-growth process technique and using a seeded infiltration and growth process are discussed. Which including various chemical doping strategies and controlled pushing effect based on the peritectic reaction of (RE)BCO. The typical experiment results, such as the largest single domain bulk, the clear TEM observations and the significant critical current density, are summarized together with the magnetization techniques. Finally, we highlight the recent prominent progress of HTS bulk applications, including Maglev, flywheel, power device, magnetic drug delivery system and magnetic resonance devices.

  6. Materials process and applications of single grain (RE)-Ba-Cu-O bulk high-temperature superconductors

    Science.gov (United States)

    Li, Beizhan; Zhou, Difan; Xu, Kun; Hara, Shogo; Tsuzuki, Keita; Miki, Motohiro; Felder, Brice; Deng, Zigang; Izumi, Mitsuru

    2012-11-01

    This paper reviews recent advances in the melt process of (RE)-Ba-Cu-O [(RE)BCO, where RE represents a rare earth element] single grain high-temperature superconductors (HTSs), bulks and its applications. The efforts on the improvement of the magnetic flux pinning with employing the top-seeded melt-growth process technique and using a seeded infiltration and growth process are discussed. Which including various chemical doping strategies and controlled pushing effect based on the peritectic reaction of (RE)BCO. The typical experiment results, such as the largest single domain bulk, the clear TEM observations and the significant critical current density, are summarized together with the magnetization techniques. Finally, we highlight the recent prominent progress of HTS bulk applications, including Maglev, flywheel, power device, magnetic drug delivery system and magnetic resonance devices.

  7. Melt-processed LRE-Ba-Cu-O superconductors and prospects for their applications

    International Nuclear Information System (INIS)

    Yoo, S.I.; Fujimoto, H.; Sakai, N.; Murakami, M.

    1997-01-01

    We have recently found that control of the oxygen partial pressure (PO 2 ) during melt processing, named the oxygen-controlled melt-growth (OCMG) process, is critical for obtaining a high superconducting transition temperature (T c ) in the light rare earth (LRE)-Ba-Cu-O (LREBCO) superconductors particularly for Nd, Sm and Eu. Further, compared to a good melt-processed Y-Ba-Cu-O (YBCO) bulk superconductor, LREBCO bulks exhibit larger critical current density (J c ) in high magnetic field and a much improved irreversibility field (H irr ) at 77 K, implying that more effective flux pinning can be realized in a commercially feasible way. In this paper, properties and characteristic flux pinning of OCMG-processed LREBCO (LRE: Nd,Sm,Eu) superconductors are described on the basis of our study during the last several years. We also present the prospects for bulk-type applications, such as the magnetic bearings, flywheels and magnetically levitated (MAGLEV) trains. (orig.)

  8. Superconductors

    International Nuclear Information System (INIS)

    Ekin, J.W.

    1983-01-01

    This chapter attempts to provide an introductory guide to interpreting handbook data on practical, high-current, superconducting materials, principally for magnet applications. An overview is given of the properties and operational limits of superconductive materials, as well as techniques used to fabricate practical superconducting wires. Topics considered include critical temperature, critical magnetic field, Type I and Type II superconductors, upper critical field values for practical materials, the temperature dependence of critical field and upper critical field, critical current, critical current density values for practical materials, the measurement of critical current, composite fabrication, stability, ac losses, eddy current loss, hysteretic loss, mechanical properties, critical current degradation, and superconducting materals selection and composite design

  9. Materials processing, pulsed field magnetization and field-pole application to propulsion motors on Gd123 bulk superconductors

    International Nuclear Information System (INIS)

    Izumi, M; Xu, C; Xu, Y; Morita, E; Kimura, Y; Hu, A; Ichihara, M; Murakami, M; Sakai, N; Hirabayashi, I; Sugimoto, H; Miki, M

    2008-01-01

    Gd123 bulk superconductor is one of the promising magnet materials. We studied the materials processing to grow high performance magnet with a doping of nano-sized metal oxides such as ZrO 2 as a candidature of pinning centre. The enhancement of the critical current density was obtained. Growth of nano-sized particles of Gd211 in addition to BaZrO 3 were observed by TEM. The formation of nano-sized particles appears a key to improve the integrated flux trapped inside the bulks and the TEM reveals an intriguing effect of the addition to the microstructure of bulk materials. Magnetization process is crucial especially for an extended machinery. Pulsed field magnetization was applied to the field-pole bulk on the rotor disk of the tested synchronous motor. The trapped flux density of 1.3 T for Gd123 bulk sample and of 60 mm diameter was reached in the limited dimension of the tested motor by a step cooling method down to 38 K with a closed-cycle condensed neon. The pulsed magnetic field was applied with a new type of split-armature coil. A large bulk of 140 mm diameter has also shown a potential flux trapping superior to other smaller specimens. The bulk magnet provides a strong magnetic field around the bulk body itself with high current density relative to a coil winding. A comparative drawing of a 'torque density' of a variety of motors which is defined as the torque divided by the volume of the motor indicates a potential advantage of bulk motor as a super permanent magnet motor

  10. Thickness dependence of the levitation performance of double-layer high-temperature superconductor bulks above a magnetic rail

    International Nuclear Information System (INIS)

    Sun, R.X.; Zheng, J.; Liao, X.L.; Che, T.; Gou, Y.F.; He, D.B.; Deng, Z.G.

    2014-01-01

    Highlights: • Thickness optimization of double-layer bulk HTSC arrangement is studied. • The new bulk HTSC arrangement makes better use of the flux distribution of the magnetic rails. • Levitation performance can be enhanced with the optimization. • The optimization can meet large levitation force requirements for HTS Maglev system. - Abstract: A double-layer high-temperature superconductor (HTSC) arrangement was proposed and proved to be able to bring improvements to both levitation force and guidance force compared with present single-layer HTSC arrangement. To fully exploit the applied magnetic field by a magnetic rail, the thickness dependence of a double-layer HTSC arrangement on the levitation performance was further investigated in the paper. In this study, the lower-layer bulk was polished step by step to different thicknesses, and the upper-layer bulk with constant thickness was directly superimposed on the lower-layer one. The levitation force and the force relaxation of the double-layer HTSC arrangement were measured above a Halbach magnetic rail. Experimental result shows that a bigger levitation force and a less levitation force decay could be achieved by optimizing the thickness of the lower-layer bulk HTSC. This thickness optimization method could be applied together with former reported double-layer HTSC arrangement method with aligned growth sector boundaries pattern. This series of study on the optimized combination method do bring a significant improvement on the levitation performance of present HTS maglev systems

  11. Thickness dependence of the levitation performance of double-layer high-temperature superconductor bulks above a magnetic rail

    Energy Technology Data Exchange (ETDEWEB)

    Sun, R.X.; Zheng, J.; Liao, X.L.; Che, T.; Gou, Y.F.; He, D.B.; Deng, Z.G., E-mail: zgdeng@gmail.com

    2014-10-15

    Highlights: • Thickness optimization of double-layer bulk HTSC arrangement is studied. • The new bulk HTSC arrangement makes better use of the flux distribution of the magnetic rails. • Levitation performance can be enhanced with the optimization. • The optimization can meet large levitation force requirements for HTS Maglev system. - Abstract: A double-layer high-temperature superconductor (HTSC) arrangement was proposed and proved to be able to bring improvements to both levitation force and guidance force compared with present single-layer HTSC arrangement. To fully exploit the applied magnetic field by a magnetic rail, the thickness dependence of a double-layer HTSC arrangement on the levitation performance was further investigated in the paper. In this study, the lower-layer bulk was polished step by step to different thicknesses, and the upper-layer bulk with constant thickness was directly superimposed on the lower-layer one. The levitation force and the force relaxation of the double-layer HTSC arrangement were measured above a Halbach magnetic rail. Experimental result shows that a bigger levitation force and a less levitation force decay could be achieved by optimizing the thickness of the lower-layer bulk HTSC. This thickness optimization method could be applied together with former reported double-layer HTSC arrangement method with aligned growth sector boundaries pattern. This series of study on the optimized combination method do bring a significant improvement on the levitation performance of present HTS maglev systems.

  12. Growth rate of YBCO-Ag superconducting single grains

    Science.gov (United States)

    Congreve, J. V. J.; Shi, Y. H.; Dennis, A. R.; Durrell, J. H.; Cardwell, D. A.

    2017-12-01

    The large scale use of (RE)Ba2Cu3O7 bulk superconductors, where RE=Y, Gd, Sm, is, in part, limited by the relatively poor mechanical properties of these inherently brittle ceramic materials. It is reported that alloying of (RE)Ba2Cu3O7 with silver enables a significant improvement in the mechanical strength of bulk, single grain samples without any detrimental effect on their superconducting properties. However, due to the complexity and number of inter-related variables involved in the top seeded melt growth (TSMG) process, the growth of large single grains is difficult and the addition of silver makes it even more difficult to achieve successful growth reliably. The key processing variables in the TSMG process include the times and temperatures of the stages within the heating profile, which can be derived from the growth rate during the growth process. To date, the growth rate of the YBa2Cu3O7-Ag system has not been reported in detail and it is this lacuna that we have sought to address. In this work we measure the growth rate of the YBCO-Ag system using a method based on continuous cooling and isothermal holding (CCIH). We have determined the growth rate by measuring the side length of the crystallised region for a number of samples for specified isothermal hold temperatures and periods. This has enabled the growth rate to be modelled and from this an optimized heating profile for the successful growth of YBCO-Ag single grains to be derived.

  13. Superconductors

    International Nuclear Information System (INIS)

    Newkirk, L.R.; Valencia, F.A.

    1977-01-01

    The structural quality of niobium germanide as a high-transition-temperature superconducting material is substantially improved by the presence of about 5 at. percent oxygen. Niobium germanide having this oxygen content may readily be prepared as a bulk coating bonded to a metallic substrate by chemical vapor deposition techniques. 2 figures, 1 table

  14. Superconductors

    Science.gov (United States)

    Newkirk, Lawrence R.; Valencia, Flavio A.

    1977-02-01

    The structural quality of niobium germanide as a high-transition-temperature superconducting material is substantially improved by the presence of about 5 at. % oxygen. Niobium germanide having this oxygen content may readily be prepared as a bulk coating bonded to a metallic substrate by chemical vapor deposition techniques.

  15. Atomic site tunneling spectroscopy on high-Tc superconductors

    International Nuclear Information System (INIS)

    Hasegawa, T.; Nantoh, M.; Takagi, A.; Yamaguchi, W.; Ogino, M.; Kawasaki, M.

    1994-01-01

    Superconducting gap structures of Bi 2 Sr 2 CaCu 2 O y (BSCCO) and YBa 2 Cu 3 O y (YBCO) have been probed by scanning tunneling microscopy (STM) at cryogenic temperatures. The tunneling conductance curves observed on bulk single crystals of BSCCO and epitaxial thin films of YBCO revealed clear obershooting peaks and flat bottom regions around V=0 with quite low zero-bias conductances of ∝1%. Since the electron tunneling process in STM is essentially incoherent, the present observation is favored by the s-wave pairing mechanism. However, the conductance curves were found to be substantially smeared in comparison with the conventional spectra predicted in the BCS (isotropic s-wave) superconductors, suggesting gap anisotropy. (orig.)

  16. The effect of processing parameters during heat treatment of bulk high-T(sub c) superconductors

    Science.gov (United States)

    Cha, Y. S.; Dorris, S. E.; Hull, J. R.; Poeppel, R. B.

    1991-04-01

    Plastic extrusion is a promising method for producing the long lengths of high-Tc superconductor that will be necessary to meet many potential applications. A crucial phase of the extrusion method is removal of organic constituents. Incomplete removal can leave residual carbon at grain boundaries, which can adversely affect the superconducting properties, whereas excessively rapid removal of the organics can cause the extruded superconductor to disintegrate completely. In this paper, we analyze the effects of the following aspects of organics removal, as they apply to the firing of extruded YBa2Cu3O(x) coils: (1) total pressure in the furnace, (2) oxygen flow, (3) heat conduction, and (4) diffusion of volatile components during removal of organics.

  17. Levitation force and magnetization in bulk and thin film high Tc superconductors

    International Nuclear Information System (INIS)

    Riise, A.B

    1998-04-01

    The authors present high-resolution measurements of the repulsive vertical force and its associated stiffness between a Nd-B-Fe magnet and a YBa 2 Cu 3 O 7-δ superconductor in cylindrical geometry. The results are compared with theoretical predictions. The calculations are based on a model in which the superconductor is assumed to be either a sintered granular material or consisting of grains embedded in a nonactive matrix so that only intragranular currents are important. The critical state model is applied to each grain individually and closed form expressions for both vertical force F z and stiffness are obtained in a configuration with cylindrical symmetry. The model explains all features of the experimental results in a consistent way. A good quantitative agreement has been obtained using only three adjustable parameters. Several central aspects of the phenomenon of magnetic levitation with high-T c superconductors are presented. High-resolution measurements are made of the repulsive vertical force and its associated stiffness as well as the horizontal stabilizing force and the stiffness governing lateral vibrations. The results obtained at 77 K using a granular YBa 2 Cu 3 O 7-δ sample and Nd-Fe-B magnet in a rectangular levitation configuration are compared with theoretical predictions. The calculations, which are based on the critical state model with the assumption that it applies to the grins individually, give closed-form expressions for all the measured quantities. It is concluded that the present model explains all features of the observations in a consistent way. Using only three adjustable parameters a good agreement exists also at a quantitative level. Experimental studies and theoretical modelling of the levitation force on a permanent magnet placed above a superconducting thin film are offered. It is shown that measurements of the levitation force is a simple and precise method to determine the critical current density in thin films

  18. Levitation force and magnetization in bulk and thin film high T{sub c} superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Riise, A.B

    1998-04-01

    The authors present high-resolution measurements of the repulsive vertical force and its associated stiffness between a Nd-B-Fe magnet and a YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} superconductor in cylindrical geometry. The results are compared with theoretical predictions. The calculations are based on a model in which the superconductor is assumed to be either a sintered granular material or consisting of grains embedded in a nonactive matrix so that only intragranular currents are important. The critical state model is applied to each grain individually and closed form expressions for both vertical force F{sub z} and stiffness are obtained in a configuration with cylindrical symmetry. The model explains all features of the experimental results in a consistent way. A good quantitative agreement has been obtained using only three adjustable parameters. Several central aspects of the phenomenon of magnetic levitation with high-T{sub c} superconductors are presented. High-resolution measurements are made of the repulsive vertical force and its associated stiffness as well as the horizontal stabilizing force and the stiffness governing lateral vibrations. The results obtained at 77 K using a granular YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} sample and Nd-Fe-B magnet in a rectangular levitation configuration are compared with theoretical predictions. The calculations, which are based on the critical state model with the assumption that it applies to the grins individually, give closed-form expressions for all the measured quantities. It is concluded that the present model explains all features of the observations in a consistent way. Using only three adjustable parameters a good agreement exists also at a quantitative level. Experimental studies and theoretical modelling of the levitation force on a permanent magnet placed above a superconducting thin film are offered. It is shown that measurements of the levitation force is a simple and precise method to determine the

  19. The enhancement of critical current density on the bulk of BPSCCO-system superconductor with silver additions

    International Nuclear Information System (INIS)

    Engkir Sukirman; Wisnu Ari Adi; Puji Sulisworo dan W Prasuad

    1999-01-01

    The influence of silver additions on the critical current density (Jc) of BPSCCO-bulk superconductor was investigated, with the aim of getting an increase of its Jc and trying to find out a correlation of Jc and structures of BPSCCO-silver composites. The BPSCCO-system superconductors with nominal composition Bi 1.84 Pb 0.34 Sr 2.00 Ca 2.03 Cu 3.06 O x (2223-phase) were synthesized by using solid state reaction method. The silver added was in the powder-AgO form varied from 0 to 30 wt % AgO. The critical current density, crystal structure, and micro-structure of BPSCCO-silver composites were characterized by means of four-point probe, x-ray diffractometer, and scanning electron microscope that is equipped with a link system energy dispersive spectrometer. It was found that silver additions to BPSCCO cause a reasonable improvement in Jc from 120 to 215 A/cm 2 , and a slight increase in Tc from 92 to 108 K, and lattice parameters of the 2223-phase from a 3.811(3) to 3.820(2) A, and from c = 37.08(3) to 37.15(2) A, with the optimum value occurs at 20 wt % AgO. The AgO powders added to the BPSCCO specimens were converted to Ag 2 O and metallic Ag during the annealing process at 827degC for 96 h in air. The addition of AgO to BPSCCO system does not necessarily lead to decomposition of the 2223-phase. The AgO reacts with and suppresses the 2201-phase. (author)

  20. Present Status and Future Prospects in Bulk Processing of HIGH-Tc Superconductors

    Science.gov (United States)

    Jin, S.; Chu, C. W.

    The following sections are included: * INTRODUCTION * HIGH SUPERCONDUCTING TRANSITION TEMPERATURE * HIGH CRITICAL CURRENT DENSITY * Grain Boundary Weak Links * Nature of Weak Links * Possible Processing Approaches for Weak Link Problem * Processing Techniques for Texture Formation * Flux Creep in HTSC * Desirable Pinning Defects * Processing for Flux Pinning Enhancement * PROSPECTS FOR BULK APPLICATIONS * Magnetic Field Gener * Energy Storage * Magnetic Shielding * Other Applications * CONCLUDING REMARKS * ACKNOWLEDGMENT * REFERENCES

  1. Temperature dependence of the mechanical properties of melt-processed Dy-Ba-Cu-O bulk superconductors evaluated by three point bending tests

    International Nuclear Information System (INIS)

    Katagiri, K; Nyilas, A; Sato, T; Hatakeyama, Y; Hokari, T; Teshima, H; Iwamoto, A; Mito, T

    2006-01-01

    Dy-Ba-Cu-O bulk superconductor has an excellent capability of trapping magnetic flux and lower heat conductivity at cryogenic temperatures as compared with Y-Ba-Cu-O bulk superconductor. The Young's modulus and the bending strength in the range from room temperature to 7 K were measured by the three-point bending tests using specimens cut from a melt-processed Dy-Ba-Cu-O bulk superconductor. They were tested in a helium gas flow type cryostat at Forschungszentrum Karlsruhe and in a liquid nitrogen bath at Iwate University. The Young's modulus was calculated by either the slope of stress-strain curve or that of the load-deflection curve of the specimen. Although the bending strength measured in the two institutes coincided well, there was a significant discrepancy in the Young's modulus. The Young's modulus and bending strength increased with decrease of temperature down to 7 K. The amount of increase in the Young's modulus and the bending strength were about 32% and 36% of those at room temperature, respectively. The scatter of data for each run was significant and did not depend on temperature. The temperature dependence of the Young's modulus coincided with that in Y-Ba-Cu-O obtained by ultrasonic velocity. The temperature dependence of the Young's modulus and the bending strength was discussed from the view point of interatomic distance of the bulk crystal

  2. Feasibility of introducing ferromagnetic materials to onboard bulk high-T{sub c} superconductors to enhance the performance of present maglev systems

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Zigang, E-mail: zgdeng@gmail.com [Applied Superconductivity Laboratory (ASCLab), Southwest Jiaotong University (SWJTU), Chengdu, Sichuan 610031 (China); State Key Laboratory of Traction Power (TPL), Southwest Jiaotong University (SWJTU), Chengdu, Sichuan 610031 (China); Wang, Jiasu [Applied Superconductivity Laboratory (ASCLab), Southwest Jiaotong University (SWJTU), Chengdu, Sichuan 610031 (China); Zheng, Jun; Zhang, Ya [Applied Superconductivity Laboratory (ASCLab), Southwest Jiaotong University (SWJTU), Chengdu, Sichuan 610031 (China); State Key Laboratory of Traction Power (TPL), Southwest Jiaotong University (SWJTU), Chengdu, Sichuan 610031 (China); Wang, Suyu [Applied Superconductivity Laboratory (ASCLab), Southwest Jiaotong University (SWJTU), Chengdu, Sichuan 610031 (China)

    2013-02-14

    Highlights: ► Ferromagnetic materials guide the flux distribution of the PMG to bulk positions. ► With ferromagnetic materials, guidance performance can be enhanced greatly. ► A new HTS Maglev system with onboard ferromagnetic materials is designed. ► The design can meet large guidance force requirements for practical applications. -- Abstract: Performance improvement is a long-term research task for the promotion of practical application of promising high-temperature superconducting (HTS) magnetic levitation (maglev) vehicle technologies. We studied the feasibility to enhance the performance of present HTS Maglev systems by introducing ferromagnetic materials to onboard bulk superconductors. The principle here is to make use of the high magnetic permeability of ferromagnetic materials to alter the flux distribution of the permanent magnet guideway for the enhancement of magnetic field density at the position of the bulk superconductors. Ferromagnetic iron plates were added to the upper surface of bulk superconductors and their geometric and positioning effects on the maglev performance were investigated experimentally. Results show that the guidance performance (stability) was enhanced greatly for a particular setup when compared to the present maglev system which is helpful in the application where large guidance forces are needed such as maglev tracks with high degrees of curves.

  3. Influence of soft ferromagnetic sections on the magnetic flux density profile of a large grain, bulk Y–Ba–Cu–O superconductor

    International Nuclear Information System (INIS)

    Philippe, M P; Wéra, L; Fagnard, J-F; Vanderheyden, B; Vanderbemden, P; Ainslie, M D; Dennis, A R; Shi, Y-H; Cardwell, D A

    2015-01-01

    Bulk, high temperature superconductors have significant potential for use as powerful permanent magnets in a variety of practical applications due to their ability to trap record magnetic fields. In this paper, soft ferromagnetic sections are combined with a bulk, large grain Y–Ba–Cu–O high temperature superconductor to form superconductor/ferromagnet hybrid structures. We study how the ferromagnetic sections influence the shape of the profile of the trapped magnetic induction at the surface of each structure and report the surface magnetic flux density measured by Hall probe mapping. These configurations have been modelled using a 2D axisymmetric finite element method based on the H-formulation and the results show excellent qualitative and quantitative agreement with the experimental measurements. The model has also been used to study the magnetic flux distribution and predict the behaviour for other constitutive laws and geometries. The results show that the ferromagnetic material acts as a magnetic shield, but the flux density and its gradient are enhanced on the face opposite to the ferromagnet. The thickness and saturation magnetization of the ferromagnetic material are important and a characteristic ferromagnet thickness d* is derived: below d*, saturation of the ferromagnet occurs, and above d*, a weak thickness-dependence is observed. The influence of the ferromagnet is observed even if its saturation magnetization is lower than the trapped flux density of the superconductor. Conversely, thin ferromagnetic discs can be driven to full saturation even though the outer magnetic field is much smaller than their saturation magnetization. (paper)

  4. Enhancement of mechanical properties of 123 superconductors

    Science.gov (United States)

    Balachandran, U.

    1995-04-25

    A composition and method are disclosed of preparing YBa{sub 2}Cu{sub 3}O{sub 7{minus}x} superconductor. Addition of tin oxide containing compounds to YBCO superconductors results in substantial improvement of fracture toughness and other mechanical properties without affect on T{sub c}. About 5-20% additions give rise to substantially improved mechanical properties.

  5. Enhancement of mechanical properties of 123 superconductors

    Science.gov (United States)

    Balachandran, Uthamalingam

    1995-01-01

    A composition and method of preparing YBa.sub.2 Cu.sub.3 O.sub.7-x superconductor. Addition of tin oxide containing compounds to YBCO superconductors results in substantial improvement of fracture toughness and other mechanical properties without affect on T.sub.c. About 5-20% additions give rise to substantially improved mechanical properties.

  6. Characteristic of the flux pinning at intergrain boundaries in bulk Bi-Pb-Sr-Ca-Cu-O superconductors

    International Nuclear Information System (INIS)

    Wang Yugui; Yang Yu; Xiong Xiaozhong; Yuan Songliu; Wang Shunxi

    1991-02-01

    The magnetization measurement shows that there are two kinds of different intergrain boundaries in the sintered Bi 1.8 Pb 0.34 Sr 1.86 Ca 2 Cu 3 O y superconductors. One has nearly no pinning force for flux line, the other can trap some flux line in the low field range where a pinning current may be sustained. When the applied field is removed, most of the remanent magnetization comes from the intergrain boundaries. The area of hysteresis loop at low field and the remanent magnetization for the cold-pressed bulk samples are significantly increased. Cold pressing results in aligning the grain orientation and raising the packing density, both of which enhanced intergrain coupling. The J c value of 1040 A/cm 2 at H = 0 and 150 A/cm 2 at H = 1 k Oe are obtained. The flux creep along the intergrain boundaries and the pinning potential energy U 0 for the coldpressed samples are also discussed

  7. Influence of lateral displacement on the levitation performance of a magnetized bulk high-Tc superconductor magnet

    International Nuclear Information System (INIS)

    Liu, W.; Wang, J.S.; Ma, G.T.; Zheng, J.; Tuo, X.G.; Li, L.L.; Ye, C.Q.; Liao, X.L.; Wang, S.Y.

    2012-01-01

    Compared with the permanent magnet, the magnetized bulk high-T c superconductor magnet (MBSCM) can trap higher magnetic field due to its strong flux pinning ability, so it is a good candidate to improve the levitation performance of high-T c superconductive (HTS) maglev system. The trapped magnetic flux of a MBSCM is sustained by the inductive superconducting current produced by the magnetizing process and is susceptible to the current intensity as well as configuration. In the HTS maglev system, the lateral displacement is an important process to change the superconducting current within a MBSCM and then affects its levitation performance, which is essential for the traffic ability in curve-way, the loading capacity of lateral impact and so on. The research about influence of lateral displacement on the levitation performance of MBSCM is necessary when MBSCM is applied on the HTS maglev vehicle. The experimental investigations about the influence of lateral displacement on the levitation performance of a MBSCM with different trapped fluxes and applied fields are processed in this article. The analyses and conclusions of this article are useful for the practical application of MBSCM in HTS maglev system.

  8. Influence of lateral displacement on the levitation performance of a magnetized bulk high-T{sub c} superconductor magnet

    Energy Technology Data Exchange (ETDEWEB)

    Liu, W., E-mail: tonny-violet@163.com [College of Nuclear Technology and Automation Engineering, Chengdu University of Technology, Chengdu 610059 (China) and Applied Superconductivity Laboratory, Southwest Jiaotong University, Chengdu 610031 (China); Wang, J.S.; Ma, G.T.; Zheng, J. [Applied Superconductivity Laboratory, Southwest Jiaotong University, Chengdu 610031 (China); State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu 610031 (China); National Laboratory of Rail Transit, Chengdu, 610031 (China); Tuo, X.G.; Li, L.L. [College of Nuclear Technology and Automation Engineering, Chengdu University of Technology, Chengdu 610059 (China); Ye, C.Q.; Liao, X.L. [Applied Superconductivity Laboratory, Southwest Jiaotong University, Chengdu 610031 (China); National Laboratory of Rail Transit, Chengdu, 610031 (China); Wang, S.Y. [Applied Superconductivity Laboratory, Southwest Jiaotong University, Chengdu 610031 (China); State Key Laboratory of Traction Power, Southwest Jiaotong University, Chengdu 610031 (China); National Laboratory of Rail Transit, Chengdu, 610031 (China)

    2012-03-15

    Compared with the permanent magnet, the magnetized bulk high-T{sub c} superconductor magnet (MBSCM) can trap higher magnetic field due to its strong flux pinning ability, so it is a good candidate to improve the levitation performance of high-T{sub c} superconductive (HTS) maglev system. The trapped magnetic flux of a MBSCM is sustained by the inductive superconducting current produced by the magnetizing process and is susceptible to the current intensity as well as configuration. In the HTS maglev system, the lateral displacement is an important process to change the superconducting current within a MBSCM and then affects its levitation performance, which is essential for the traffic ability in curve-way, the loading capacity of lateral impact and so on. The research about influence of lateral displacement on the levitation performance of MBSCM is necessary when MBSCM is applied on the HTS maglev vehicle. The experimental investigations about the influence of lateral displacement on the levitation performance of a MBSCM with different trapped fluxes and applied fields are processed in this article. The analyses and conclusions of this article are useful for the practical application of MBSCM in HTS maglev system.

  9. Enhancement of critical currents in bulk and Ag-sheathed Bi(Pb)-2223 superconductors

    International Nuclear Information System (INIS)

    Brauer, D.J.; Eujen, R.; Hudepohl, J.

    1991-01-01

    This paper reports on the superconducting properties of the Bi(Pb)-2223 phase that have been optimized. Prolonged annealing of coarse powder raised j c in bulk samples to as high as 1100 Acm -2 at 77 K. the temperature dependence was studied between 96 and 4.2 K whereby j c rose gradually from 120 to 2100 Acm -2 . T c dropped from 107 K to 64 K in magnetic fields up to 4 T but decreased by only 1 K/T in higher fields. A tape prepared by rolling and subsequent annealing of Ag tubes containing Bi(Pb)-2223 powder exhibited a j c of 1700 Acm -2 at 77 K and 11000 Acm -2 at 4.2 K. The latter j c dropped to 3000 Acm -2 in a magnetic field of 0.25 t, but it was still 1200 Acm -2 in a 10 T field. A tape fabricated by pressing a drawn and annealed wire proved to be less sensitive to low magnetic fields

  10. Superconductor-ferromagnet-superconductor nanojunctions from perovskite materials

    International Nuclear Information System (INIS)

    Štrbík, V.; Beňačka, Š.; Gaži, Š.; Španková, M.; Šmatko, V.; Knoška, J.; Gál, N.; Chromik, Š.; Sojková, M.; Pisarčík, M.

    2017-01-01

    Highlights: • Superconductor-ferromagnet-superconductor nanojunction. • Nanojunctions prepared by Ga"3"+ focused ion beam patterning. • Indication of triplet Cooper pair component in junction superconducting current. • Qualitative agreement with theoretical model. - Abstract: The lateral superconductor-ferromagnet–superconductor (SFS) nanojunctions based on high critical temperature superconductor YBa_2Cu_3O_x (YBCO) and half-metallic ferromagnet La_0_._6_7Sr_0_._3_3MnO_3 (LSMO) thin films were prepared to investigate a possible presence of long range triplet component (LRTC) of Cooper pairs in the LSMO. We applied Ga"3"+ focused ion beam patterning to create YBCO/LSMO/YBCO lateral type nanojunctions with LSMO length as small as 40 nm. The resistivity vs. temperature, critical current density vs. temperature and resistance vs. magnetic field dependence were studied to recognize the LRTC of Cooper pairs in the LSMO. A non-monotonic temperature dependence of junction critical current density and a decrease of the SFS nanojunction resistance in increased magnetic field were observed. Only weak manifestations of LRTC and some qualitative agreement with theory were found out in SFS nanojunctions realized from the perovskite materials. The presence of equal-spin triplet component of Cooper pairs in half-metallic LSMO ferromagnet is not such apparent as in SFS junctions prepared from low temperature superconductors NbTiN and half-metallic ferromagnet CrO_2.

  11. Superconductor-ferromagnet-superconductor nanojunctions from perovskite materials

    Energy Technology Data Exchange (ETDEWEB)

    Štrbík, V., E-mail: vladimir.strbik@savba.sk [Institute of Electrical Engineering, SAS, Dúbravská Cesta 9, Bratislava (Slovakia); Beňačka, Š.; Gaži, Š.; Španková, M.; Šmatko, V. [Institute of Electrical Engineering, SAS, Dúbravská Cesta 9, Bratislava (Slovakia); Knoška, J. [Center for Free-Electron Laser Science, DESY, Notkestraße 85, 22607, Hamburg (Germany); Department of Physics, University of Hamburg, Luruper Chaussee 149, 22607, Hamburg (Germany); Gál, N.; Chromik, Š.; Sojková, M.; Pisarčík, M. [Institute of Electrical Engineering, SAS, Dúbravská Cesta 9, Bratislava (Slovakia)

    2017-02-15

    Highlights: • Superconductor-ferromagnet-superconductor nanojunction. • Nanojunctions prepared by Ga{sup 3+} focused ion beam patterning. • Indication of triplet Cooper pair component in junction superconducting current. • Qualitative agreement with theoretical model. - Abstract: The lateral superconductor-ferromagnet–superconductor (SFS) nanojunctions based on high critical temperature superconductor YBa{sub 2}Cu{sub 3}O{sub x} (YBCO) and half-metallic ferromagnet La{sub 0.67}Sr{sub 0.33}MnO{sub 3} (LSMO) thin films were prepared to investigate a possible presence of long range triplet component (LRTC) of Cooper pairs in the LSMO. We applied Ga{sup 3+} focused ion beam patterning to create YBCO/LSMO/YBCO lateral type nanojunctions with LSMO length as small as 40 nm. The resistivity vs. temperature, critical current density vs. temperature and resistance vs. magnetic field dependence were studied to recognize the LRTC of Cooper pairs in the LSMO. A non-monotonic temperature dependence of junction critical current density and a decrease of the SFS nanojunction resistance in increased magnetic field were observed. Only weak manifestations of LRTC and some qualitative agreement with theory were found out in SFS nanojunctions realized from the perovskite materials. The presence of equal-spin triplet component of Cooper pairs in half-metallic LSMO ferromagnet is not such apparent as in SFS junctions prepared from low temperature superconductors NbTiN and half-metallic ferromagnet CrO{sub 2}.

  12. Cryogenic milling for the fabrication of high J{sub c} MgB{sub 2} bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Kim, D. N.; Kang, M. O.; Park, H. W. [Korea University of Technology and Education, Cheonan (Korea, Republic of); Jun, B. H.; Kim, C. J. [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2017-06-15

    Cryogenic milling which is a combined process of low-temperature treatment and mechanical milling was applied to fabricate high critical current density (J{sub c}) MgB{sub 2} bulk superconductors. Liquid nitrogen was used as a coolant, and no solvent or lubricant was used. Spherical Mg (6-12 μm, 99.9 % purity) and plate-like B powder (⁓ 1 μm, 97 % purity) were milled simultaneously for various time periods (0, 2, 4, 6 h) at a rotating speed of 500 rpm using ZrO{sub 2} balls. The (Mg{sup +2B}) powders milled were pressed into pellets and heat-treated at 700°C for 1 h in flowing argon. The use of cryomilled powders as raw materials promoted the formation reaction of superconducting MgB{sub 2}, reduced the grain size of MgB{sub 2}, and suppressed the formation of impurity MgO. The superconducting critical temperature (T{sub c}) of MgB{sub 2} was not influenced as the milling time (t) increased up to 6 h. Meanwhile, the critical current density (J{sub c}) of MgB{sub 2} increased significantly when t increased to 4 h. When t increased further to 6 h, however, Jc decreased. The J{sub c} enhancement of MgB{sub 2} by cryogenic milling is attributed to the formation of the fine grain MgB{sub 2} and a suppression of the MgO formation.

  13. DC magnetization of random Y1Ba2Cu3O8-δ/Ag bulk composites

    International Nuclear Information System (INIS)

    Ash, C.L.; Harris, D.C.; Calabrese, J.J.; Garland, J.C.

    1994-01-01

    It is commonly believed that high-field magnetization measurements of superconducting/normal metal bulk composites probe only the intragranular nature of the superconducting constituent. According to this view, the measured magnetic moment divided by the volume of superconducting material should be independent of the volume fraction of superconductor. We have tested this hypothesis by measuring the dc magnetization at 10K in magnetic fields to 5T of a series of YBCO/Ag bulk composites with 0 ≤ p ≤ 1.0, where p is the volume fraction of superconductor. We find that the magnetization hysteresis curves for p ≥ 0.70 are nearly identical, while those for the p < 0.70 samples fall inside the p ≥ 0.70 curves. Two possible interpretations are (i) that variations in Ag content alters the superconducting properties of individual YBCO grains, and (ii) that the p-dependent variations in the YBCO clusters affects the demagnetization factor for samples with p < 0.70. (orig.)

  14. Controlled levitation of Y-Ba-Cu-O bulk superconductors and energy minimum analysis; Y-Ba-Cu-O baruku chodendotai no fujo to enerugi kaiseki

    Energy Technology Data Exchange (ETDEWEB)

    Magashima, K. [Railway Technical Research Institute, Tokyo (Japan); Iwasa, Y. [Francis Bitter Magnet Laboratory, Canbridge (United States); Sawa, K. [keio University, Tokyo (Japan); Murakami, M. [Superconductivity research Laboratory, Tokyo (Japan)

    1999-11-25

    The levitation of bulk Y-Ba-Cu-O superconductors can be controlled using a Bi-Sr-Ca-Cu-O (Bi2223) superconducting electromagnet. It was found that stable levitation without tilting could be obtained only when the sample trapped a certain amount of fields, the minimum of which depended on the external field and sample dimensions. We employed a novel analysis method for levitation based on the total energy balance, which is much simpler than the force method and could be applied to understanding general levitation behavior. Numerical analyses thus developed showed that stable levitation of superconductors with large dimensions cen only be achieved when the induced currents can flow with three-dimensional freedom. (author)

  15. An efficient and economical way to enhance the performance of present HTS Maglev systems by utilizing the anisotropy property of bulk superconductors

    International Nuclear Information System (INIS)

    Deng Zigang; Wang Jiasu; Zheng Jun; Zhang Ya; Wang Suyu

    2013-01-01

    We report a simple, efficient and economical way to enhance the levitation or guidance performance of present high-temperature superconducting (HTS) Maglev systems by exploring the anisotropic properties of the critical current density in the a–b plane and along the c-axis of bulk superconductors. In the method, the bulk laying mode with different c-axis directions is designed to match with the magnetic field configuration of the applied permanent magnet guideway (PMG). Experimental results indicate that more than a factor of two improvement in the levitation force or guidance force is achieved when changing the laying mode of bulk superconductors from the traditional fashion of keeping the c-axis vertical to the PMG surface to the studied one of keeping the c-axis parallel to the PMG surface, at the maximum horizontal and vertical magnetic field positions of the PMG, respectively. These phenomena resulted from the physical nature of the generated levitation force and guidance force (electromagnetic forces) and the fact that there are different critical current densities in the a–b plane and along the c axis. Based on the experimental results, new HTS Maglev systems can be designed to meet the requirements of practical heavy-load or curved-route applications. (paper)

  16. An efficient and economical way to enhance the performance of present HTS Maglev systems by utilizing the anisotropy property of bulk superconductors

    Science.gov (United States)

    Deng, Zigang; Wang, Jiasu; Zheng, Jun; Zhang, Ya; Wang, Suyu

    2013-02-01

    We report a simple, efficient and economical way to enhance the levitation or guidance performance of present high-temperature superconducting (HTS) Maglev systems by exploring the anisotropic properties of the critical current density in the a-b plane and along the c-axis of bulk superconductors. In the method, the bulk laying mode with different c-axis directions is designed to match with the magnetic field configuration of the applied permanent magnet guideway (PMG). Experimental results indicate that more than a factor of two improvement in the levitation force or guidance force is achieved when changing the laying mode of bulk superconductors from the traditional fashion of keeping the c-axis vertical to the PMG surface to the studied one of keeping the c-axis parallel to the PMG surface, at the maximum horizontal and vertical magnetic field positions of the PMG, respectively. These phenomena resulted from the physical nature of the generated levitation force and guidance force (electromagnetic forces) and the fact that there are different critical current densities in the a-b plane and along the c axis. Based on the experimental results, new HTS Maglev systems can be designed to meet the requirements of practical heavy-load or curved-route applications.

  17. Effects of artificial holes in very large single-grain Y_1_._5Ba_2Cu_3O_7_-_y bulk superconductors

    International Nuclear Information System (INIS)

    Park, S. D.; Jun, B. H.; Kim, C. J.; Park, H. W.

    2017-01-01

    The effects of artificial holes on the trapped magnetic fields and magnetic levitation forces of very large single-grain Y_1_._5Ba_2Cu_3O_7_-_y (Y1.5) bulk superconductors were studied. Artificial holes were made for Y1.5 powder compacts by die pressing using cylindrical dies with a diameter of 30 mm or 40 m, or rectangular dies with a side length of 50 mm. The single grain Y1.5 bulk superconductors (25 mm, 33 mm in diameter and 42 mm in side length) with artificial holes were fabricated using a top-seeded melt growth (TSMG) process for the die-pressed Y1.5 powder compacts. The magnetic levitation forces at 77 K of the 25 mm single grain Y1.5 samples with one (diameters of 4.2 mm) or six artificial holes (diameters of 2.5 mm) were 10-17% higher than that of the Y1.5 sample without artificial holes. The trapped magnetic fields at 77 K of the Y1.5 samples with artificial holes were also 9.6-18% higher than that of the Y1.5 sample without artificial holes. The 33 mm and 42 mm single grain Y1.5 samples with artificial holes (2.5 mm and 4.2 mm in diameter) also showed trapped magnetic fields 10-13% higher than that of the Y1.5 samples without artificial holes in spite of the reduced superconducting volume fraction due to the presence of artificial holes. The property enhancement in the large single grain Y1.5 bulk superconductors appears to be attributed to the formation of the pore-free regions near the artificial holes and the homogeneous oxygen distribution in the large Y123 grains

  18. Magnetic characterisation of large grain, bulk Y–Ba–Cu–O superconductor–soft ferromagnetic alloy hybrid structures

    International Nuclear Information System (INIS)

    Philippe, M.P.; Fagnard, J.-F.; Kirsch, S.; Xu, Z.; Dennis, A.R.; Shi, Y.-H.; Cardwell, D.A.; Vanderheyden, B.; Vanderbemden, P.

    2014-01-01

    Highlights: • Large grain, bulk YBaCuO superconductor (SC) combined with ferromagnetic elements. • The flux lines curve outwards through the ferromagnet in the remanent state. • The trapped field in the SC is enhanced by the presence of the ferromagnet. • The effects of the SC and the ferromagnet add when the ferromagnet is saturated. - Abstract: Large grain, bulk Y–Ba–Cu–O (YBCO) high temperature superconductors (HTS) have significant potential for use in a variety of practical applications that incorporate powerful quasi-permanent magnets. In the present work, we investigate how the trapped field of such magnets can be improved by combining bulk YBCO with a soft FeNi, ferromagnetic alloy. This involves machining the alloy into components of various shapes, such as cylinders and rings, which are attached subsequently to the top surface of a solid, bulk HTS cylinder. The effect of these modifications on the magnetic hysteresis curve and trapped field of the bulk superconductor at 77 K are then studied using pick-up coil and Hall probe measurements. The experimental data are compared to finite element modelling of the magnetic flux distribution using Campbell’s algorithm. Initially we establish the validity of the technique involving pick-up coils wrapped around the bulk superconductor to obtain its magnetic hysteresis curve in a non-destructive way and highlight the difference between the measured signal and the true magnetization of the sample. We then consider the properties of hybrid ferromagnet/superconductor (F/S) structures. Hall probe measurements, together with the results of the model, establish that flux lines curve outwards through the ferromagnet, which acts, effectively, like a magnetic short circuit. Magnetic hysteresis curves show that the effects of the superconductor and the ferromagnet simply add when the ferromagnet is saturated fully by the applied field. The trapped field of the hybrid structure is always larger than that of the

  19. Maximum permissible voltage of YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Wen, J.; Lin, B.; Sheng, J.; Xu, J.; Jin, Z. [Department of Electrical Engineering, Shanghai Jiao Tong University, Shanghai (China); Hong, Z., E-mail: zhiyong.hong@sjtu.edu.cn [Department of Electrical Engineering, Shanghai Jiao Tong University, Shanghai (China); Wang, D.; Zhou, H.; Shen, X.; Shen, C. [Qingpu Power Supply Company, State Grid Shanghai Municipal Electric Power Company, Shanghai (China)

    2014-06-15

    Highlights: • We examine three kinds of tapes’ maximum permissible voltage. • We examine the relationship between quenching duration and maximum permissible voltage. • Continuous I{sub c} degradations under repetitive quenching where tapes reaching maximum permissible voltage. • The relationship between maximum permissible voltage and resistance, temperature. - Abstract: Superconducting fault current limiter (SFCL) could reduce short circuit currents in electrical power system. One of the most important thing in developing SFCL is to find out the maximum permissible voltage of each limiting element. The maximum permissible voltage is defined as the maximum voltage per unit length at which the YBCO coated conductors (CC) do not suffer from critical current (I{sub c}) degradation or burnout. In this research, the time of quenching process is changed and voltage is raised until the I{sub c} degradation or burnout happens. YBCO coated conductors test in the experiment are from American superconductor (AMSC) and Shanghai Jiao Tong University (SJTU). Along with the quenching duration increasing, the maximum permissible voltage of CC decreases. When quenching duration is 100 ms, the maximum permissible of SJTU CC, 12 mm AMSC CC and 4 mm AMSC CC are 0.72 V/cm, 0.52 V/cm and 1.2 V/cm respectively. Based on the results of samples, the whole length of CCs used in the design of a SFCL can be determined.

  20. Synthesis and Characterization of Nano Scale YBCO

    International Nuclear Information System (INIS)

    Sukirman, E.; Wisnu AA; Yustinus P; Sahidin W, D.; Rina M, Th.

    2009-01-01

    Synthesis and characterization of the nano scale YBCO superconductor have been performed. The nano scale superconductor was synthesized from YBCO system (YBa 2 Cu 3 O 7-X ). Raw materials, namely Y 2 O 3 , BaCO 3 , and Cu°, were balanced and mixed with ethanol using magnetic steering as a churn in a beaker glass. Then, the precursor was calcined at T k = 900°C for 5 hours and repeated it until three times. The resulting precursor was ground by using High Energy Milling (HEM) for t = 0, 30, 50, 70, and 90 hour and hereinafter precursors are successively referred as YKM-00, YKM-30, YKM-50, YKM-70, and YKM-90. The resulting powders phase were characterized by means of x-ray diffraction technique using the Rietveld analysis method. Precursor of YKM-90 was pressed into pellets, and then sintered at various temperatures and periods. The sample phase was then characterized by using the Rietveld analysis method based on the x-ray diffraction data. The crystallites size were calculated using Scherrer formula. Results of analysis indicate that by minimizing crystallites size, period of sinter can be shortened from 10 to 1 hour, resulting crystallite size of D = 925 Å, critical current density of J c = 4 A / cm 2 , and can be grown of about 15 weight % of 211-phase in a matrix of 123-phase. The decrease of crystallite size will generate a change in physical properties dramatically, if the crystallite size of the material, D is smaller or equal to the coherence length of 10 Å. (author)

  1. Vortex pinning landscape in MOD-TFA YBCO nanostroctured films

    Science.gov (United States)

    Gutierrez, J.; Puig, T.; Pomar, A.; Obradors, X.

    2008-03-01

    A methodology of general validity to study vortex pinning in YBCO based on Jc transport measurements is described. It permits to identify, separate and quantify three basic vortex pinning contributions associated to anisotropic-strong, isotropic-strong and isotropic-weak pinning centers. Thereof, the corresponding vortex pinning phase diagrams are built up. This methodology is applied to the new solution-derived YBCO nanostructured films, including controlled interfacial pinning by the growth of nanostructured templates by means of self-assembled processes [1] and YBCO-BaZrO3 nanocomposites prepared by modified solution precursors. The application of the methodology and comparison with a standard solution-derived YBCO film [2], enables us to identify the nature and the effect of the additional pinning centers induced. The nanostructured templates films show c-axis pinning strongly increased, controlling most of the pinning phase diagram. On the other hand, the nanocomposites have achieved so far, the highest pinning properties in HTc-superconductors [3], being the isotropic-strong defects contribution the origin of their unique properties. [1] M. Gibert et al, Adv. Mat. vol 19, p. 3937 (2007) [2] Puig.T et al, SuST EUCAS 2007 (to be published) [3] J. Gutierrez et al, Nat. Mat. vol. 6, p. 367 (2007) * Work supported by HIPERCHEM, NANOARTIS and MAT2005-02047

  2. Correlating properties and microstructure of YBCO thin films by magnetic X-ray microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Ruoss, Stephen; Stahl, Claudia; Weigand, Markus; Schuetz, Gisela [Max-Planck-Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Zahn, Patrick; Bayer, Jonas [Max-Planck-Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Research Institute for Innovative Surfaces, FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Albrecht, Joachim [Research Institute for Innovative Surfaces, FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2016-07-01

    The magnetic flux distribution in high-temperature superconductors namely YBCO has been observed using a novel high-resolution technique based on the X-ray magnetic circular dichroism (XMCD). Therefore, a CoFeB layer is deposited on the superconductor which exhibits a strong XMCD-effect. X-ray absorption measurements with circular polarized radiation allows the analysis of the magnetic flux distribution in the superconductor via the soft-magnetic sensor layer [3,4]. In the total electron yield (TEY) mode of the scanning X-ray microscope (SXM) the surface structure and the magnetic domains can be imaged at the same time. Having obtained such high resolution images, the correlation of magnetic flux penetration and defect structure of YBCO thin films can be analyzed. The measurements have been performed at the scanning X-ray microscope MAXYMUS at Bessy II, HZB Berlin.

  3. Fast neutron induced flux pinning in Tl-based high-Tc single crystals and thin films, highly textured tapes and melt-textured bulk 123-superconductors

    International Nuclear Information System (INIS)

    Brandstaetter, G.; Samadi Hosseinalli, G.; Kern, C.; Sauerzopf, F.M.; Schulz, G.W.; Straif, W.; Yang, X.; Weber, H.W.; Hu, Q.Y.

    1999-01-01

    Various compounds (TI-2223, TI-1223, TI-2212) as well as material forms (single crystals, thin films, ceramics, tapes) of TI-based high temperature superconductors were investigated by magnetic and transport techniques. TI-2223 has a very 'low lying' irreversibility line (H parallel e) and negligible critical current densities J c at 77 K. However, the irreversibility line shifts to higher fields and temperatures and J c is strongly enhanced, even at 77 K, after fast neutron irradiation. In contrast, the related TI-1223 compound has a much steeper irreversibility line (H parallel c) similar to that of Y-123. J c is significant up to 77 K, even in the unirradiated state, and can be largely improved by neutron irradiation. Transport measurements made on TI-1223 tapes still show much lower critical current densities. TI-2212 and Tl-2223 thin films have J c 's at 77 K, which are comparable to those of TI-1223 single crystals. Transport measurements on highly textured Bi-2223 tapes as well as flux profile measurements on Nd-123 bulk superconductors confirm the beneficial effects of neutron induced defects (collision cascades) for flux pinning. (author)

  4. Some experimental and theoretical aspects of the surface impedance in bulk high-temperature superconductors at 10 GHz

    Energy Technology Data Exchange (ETDEWEB)

    Deville, A.; Fawaz, H.; Gaillard, B. (Lab. d' Electronique des Milieux Condenses, Univ. de Provence, Centre Saint-Jerome, 13 - Marseille (France)); Noel, H.; Potel, M. (Lab. de Chimie Minerale, Univ. de Rennes, 35 (France)); Monnereau, O. (Lab. de Chimie des Materiaux, Univ. de Provence, Centre Saint-Charles, 13 - Marseille (France))

    1992-07-15

    After a presentation of the theoretical framework, and a short review of existing r.f. results in high-temperature superconductors, we present our own 10 GHz measurements on YBa[sub 2]Cu[sub 3]O[sub 7] single crystals and sintered samples. We use an electron spin resonance (ESR) heterodyne spectrometer and measurements of the reflection coefficient and resonant frequency of a cavity to get information not only on the surface resistance, R[sub S], as generally done, but also on the surface reactance, X[sub S]. The theoretical analysis of the frequency shift is made by adapting Slater's perturbation method to the present problem. In order to explain both the R[sub s] and X[sub S] results, and previous ESR observations, while keeping theoretical simplicity, we are led to suggest that in the normal state these materials show an unconventional skin effect, where the phenomenon is governed not by the d.c. conductivity, but by an effective (lower) conductivity, the other characteristics being unchanged. We briefly discuss the superconductor results and the validity of the two-fluid model. (orig.).

  5. Fault current limitation with HTc superconductors; Limitation de courant a partir de materiaux supraconducteurs HTc

    Energy Technology Data Exchange (ETDEWEB)

    Buzon, D.

    2002-09-15

    This report deals with the possibility of using high critical temperature (HTc) superconductors for current limitation. The transition from a superconductive to a high dissipative state could be used to limit inrush currents. This application of superconductivity is very attractive because it's an innovative device for electrical networks without any conventional equivalence at high voltage. This device would allow to improve the density of connections and the continuity of the electrical distribution. This study can be divided into two fields. The aim of the first one is to analyse the behaviour of different HTc superconductors for current limitation. We carried out experimental measurements to characterise those conductors during a nominal AC rating (measurements of losses) and during a fault setting. Particularly, a description of the transition in bulk textured YBCO samples near Tc was made of inhomogeneous transition of the device and to estimate its losses. Finally, a 1 kV / 100 A demonstrator made of 43 meanders of textured YBCO was tested at 90,5 K. Thermal gradients seem to be responsible of the altering of some of the samples. The other part of this study concerns the dynamic of the transition. Near Tc, our experiments showed that the transition is more homogeneous. Experimental measurements also showed the influence of thermal exchanges with the cryogenic surrounding on the transition. This point can be justified if the dissipated energy is locally concentrated. (author)

  6. Fault current limitation with HTc superconductors; Limitation de courant a partir de materiaux supraconducteurs HTc

    Energy Technology Data Exchange (ETDEWEB)

    Buzon, D

    2002-09-15

    This report deals with the possibility of using high critical temperature (HTc) superconductors for current limitation. The transition from a superconductive to a high dissipative state could be used to limit inrush currents. This application of superconductivity is very attractive because it's an innovative device for electrical networks without any conventional equivalence at high voltage. This device would allow to improve the density of connections and the continuity of the electrical distribution. This study can be divided into two fields. The aim of the first one is to analyse the behaviour of different HTc superconductors for current limitation. We carried out experimental measurements to characterise those conductors during a nominal AC rating (measurements of losses) and during a fault setting. Particularly, a description of the transition in bulk textured YBCO samples near Tc was made of inhomogeneous transition of the device and to estimate its losses. Finally, a 1 kV / 100 A demonstrator made of 43 meanders of textured YBCO was tested at 90,5 K. Thermal gradients seem to be responsible of the altering of some of the samples. The other part of this study concerns the dynamic of the transition. Near Tc, our experiments showed that the transition is more homogeneous. Experimental measurements also showed the influence of thermal exchanges with the cryogenic surrounding on the transition. This point can be justified if the dissipated energy is locally concentrated. (author)

  7. Structure and properties of YBa2Cu3O7-δ superconductor doped with bulk cadmium oxide

    Directory of Open Access Journals (Sweden)

    A Echresh

    2010-09-01

    Full Text Available In this paper, the Y1-xCdxBa2Cu3O7-δ superconductor with x=0, 0.05, 0.1, 0.15, 0.2, 0.3, 0.4, 0.5 are prepared using the solid state method and the structure, electrical resistance, critical current density and critical temperature of it, have been studied. The results show that these doping do not affect so much on the structure and lattice parameters. The electrical resistance of samples increased with doping. A little amount of doping cadmium improve critical current density such that the sample x=0.1 has a maximum critical current density among the samples. The critical temperature with doping cadmium up to x=0.2 has little fluctuation and its variation can be ignored, but by increasing up to x=0.5 the critical temperature decreases gradually.

  8. AFM studies on heavy ion irradiated YBCO single crystals

    International Nuclear Information System (INIS)

    Lakhani, Archana; Marhas, M.K.; Saravanan, P.; Ganesan, V.; Srinivasan, R.; Kanjilal, D.; Mehta, G.K.; Elizabeth, Suja; Bhat, H.L.

    2000-01-01

    Atomic Force Microscopy (AFM) is extensively used to characterise the surface morphology of high energy ion irradiated single crystals of high temperature superconductor - YBCO. Our earlier systematic studies on thin films of YBCO under high energy and heavy ion irradiation shows clear evidence of ion induced sputtering or erosion, even though the effect is more on the grain boundaries. These earlier results were supported by electrical resistance measurements. In order to understand more clearly, the nature of surface modification at these high energies, AFM studies were carried out on single crystals of YBCO. Single crystals were chosen in order to see the effect on crystallites alone without interference from grain boundaries. 200 MeV gold ions were used for investigation using the facilities available at Nuclear Science Centre, New Delhi. The type of ion and the range of energies were chosen to meet the threshold for electronically mediated defect production. The results are in conformity with our earlier studies and will be described in detail in the context of electronic energy loss mediated sputtering or erosion. (author)

  9. Studies of proximity-effect and tunneling in YBCO/metal layered films

    Energy Technology Data Exchange (ETDEWEB)

    Greene, L.H.; Barner, J.B.; Feldmann, W.L.; Farrow, L.A.; Miceli, P.F.; Ramesh, R.; Wilkens, B.J.; Bagley, B.G.; Tarascon, J.M.; Wernick, J.H. (Bellcore, Red Bank, NJ (USA)); Giroud, M. (CRTBT-CNRS, Grenoble (France)); Rowell, J.M. (Conductus, Sunnyvale, CA (USA))

    1989-12-01

    The short coherence length of the high-Tc superconductors, coupled with their tendency to form non-superconducting surface layers, accounts for the difficulty in achieving good tunnel junctions. A proximity layer of a longer coherence length normal metal (N) is expected to ''draw out'' Cooper pairs. Our goal is to fabricate reproducible, planar tunnel junctions of SNIS layered structures for proximity tunneling spectroscopy. Such structures of YBCO/N/I/Pb and SNS structures of YBCO/N/Pb indicate that the normal metal produces a low resistance contact to the YBCO surface with a supercurrent observed in the SNS. The insulating barrier in the SNIS is reproducible, insulating and continuous: A sharp Pb gap and phonons from the counter-electrode are routinely observed. (orig.).

  10. Studies of proximity-effect and tunneling in YBCO/metal layered films

    International Nuclear Information System (INIS)

    Greene, L.H.; Barner, J.B.; Feldmann, W.L.; Farrow, L.A.; Miceli, P.F.; Ramesh, R.; Wilkens, B.J.; Bagley, B.G.; Tarascon, J.M.; Wernick, J.H.; Giroud, M.; Rowell, J.M.

    1989-01-01

    The short coherence length of the high-T c superconductors, coupled with their tendency to form non-superconducting surface layers, accounts for the difficulty in achieving good tunnel junctions. A proximity layer of a longer coherence length normal metal (N) is expected to draw out Cooper pairs. The authors' goal is to fabricate reproducible, planar tunnel junctions of SNIS layered structures for proximity tunneling spectroscopy. They discuss how such structures of YBCO/N/I/Pb and SNS structures of YBCO/N/Pb indicate that the normal metal produces a low resistance contact to the YBCO surface with a supercurrent observed in the SNS. The insulating barrier in the SNIS is reproducible, insulating and continuous: A sharp Pb gap and phonons from the counter-electrode are routinely observed

  11. Applications of high-Tc-superconductors to power engineering. Manufacture of YBCO plate-type conductors and construction of a HTS current limiter model up to 1 MVA nominal power. Final report

    International Nuclear Information System (INIS)

    Utz, B.; Schmidt, W.; Schilling, W.; Fischperer, I.; Kraemer, H.P.; Wacker, B.; Gromoll, B.; Neumueller, H.W.; Arndt, A.; Karras, B.; Krueger, U.; Pyritz, U.; Schiewe, H.; Schiller, H.P.; Volkmar, R.R.; Hering, U.; Roessler, R.; Freyhardt, H.C.; Sievers, S.; Hoffmann, J.; Dzich, J.; Kinder, H.; Hoffmann, C.; Lindmayer, M.; Grundmann, J.; Woerdenweber, R.; Hollmann, E.; Kutzner, R.; Klein, W.; Bunte, S.; Kuhn, M.

    2002-06-01

    In terms of materials, the main focus of the work was on the manufacture of large-area YBCO plate-type conductors with homogeneous properties and maximum current densities of j c >1 MA/cm 2 . j c values of better than 3 MA/cm 2 were achieved reproducibly on sapphire substrates of 100 mm diameter and 10 x 20 cm 2 in size with a homogeneity of 10%; on polycrystalline substrates of 10 x 20 cm 2 in size, homogeneous j c values of up to 2 MA/cm 2 were also successfully demonstrated. Of the total of four methods of coating available at the start of the project, thermal co-evaporation (TCE) proved best for YBCO thin films and the IBAD method best for quasi single-crystal buffer films. The latter are necessary to achieve high j c on polycrystalline substrates such as ZrO 2 (Y), glass and Al 2 O 3 . Polycrystalline substrates are essential in order to make the HTS current limiter as a future product commercially feasible. The favoured solutions ZrO 2 (Y) and glass have not come up to expectations, because present investigations into quench propagation are showing that, with this approach, the high values of power density required for the switching process (1600 VA/cm 2 ) cannot be achieved. Towards the end of the project, polycrystalline Al 2 O 3 began to be seen as a successful alternative; the work is being pursued further within the context of a follow-on project. The coating processes were stabilized successfully and, when combined with strict quality control, allowed the yield of tested, ready-to-use plate-type conductors to be improved to 85%. This success was an essential prerequisite for the building of a 3-phase, 1.2 MVA model (7.2 kV) comprising a total of sixty-three 100 mm plate-type conductors. At the Berlin factory the model has been successfully tested up to a prospective short-circuit current of 5 kV. This has demonstrated the basic suitability of HTS thin-film technology for use in current limiters. So far the model has been switched a total of 43 times

  12. Influence of radius of cylinder HTS bulk on guidance force in a maglev vehicle system

    International Nuclear Information System (INIS)

    Longcai, Zhang

    2014-01-01

    Highlights: • The guidance force was decayed by the application of the AC external magnetic field. • The guidance force was higher for the bulk with bigger radius. • The guidance force decay rates of the bulks were approximately equal despite of the different radius in the maglev vehicle system. - Abstract: Bulk superconductors had great potential for various engineering applications, especially in a high-temperature superconducting (HTS) maglev vehicle system. In such a system, the HTS bulks were always exposed to AC external magnetic field, which was generated by the inhomogeneous surface magnetic field of the NdFeB guideway. In our previous work, it was observed that the guidance force of the YBCO bulk over the NdFeB guideway used in the HTS maglev vehicle system was decayed by the application of the AC external magnetic field. In this paper, we investigated the influence of the radius of the cylinder HTS bulk exposed to an AC magnetic field perturbation on the guidance force in the maglev vehicle system. From the results, it was found that the guidance force was stronger for the bulk with bigger radius and the guidance force decay rates of the bulks were approximately equal despite of the different radius in the maglev vehicle system. Therefore, in order to obtain higher guidance force in the maglev vehicle system, we could use the cylinder HTS bulks with the bigger radius

  13. Influence of radius of cylinder HTS bulk on guidance force in a maglev vehicle system

    Energy Technology Data Exchange (ETDEWEB)

    Longcai, Zhang, E-mail: zhlcai2000@163.com

    2014-07-15

    Highlights: • The guidance force was decayed by the application of the AC external magnetic field. • The guidance force was higher for the bulk with bigger radius. • The guidance force decay rates of the bulks were approximately equal despite of the different radius in the maglev vehicle system. - Abstract: Bulk superconductors had great potential for various engineering applications, especially in a high-temperature superconducting (HTS) maglev vehicle system. In such a system, the HTS bulks were always exposed to AC external magnetic field, which was generated by the inhomogeneous surface magnetic field of the NdFeB guideway. In our previous work, it was observed that the guidance force of the YBCO bulk over the NdFeB guideway used in the HTS maglev vehicle system was decayed by the application of the AC external magnetic field. In this paper, we investigated the influence of the radius of the cylinder HTS bulk exposed to an AC magnetic field perturbation on the guidance force in the maglev vehicle system. From the results, it was found that the guidance force was stronger for the bulk with bigger radius and the guidance force decay rates of the bulks were approximately equal despite of the different radius in the maglev vehicle system. Therefore, in order to obtain higher guidance force in the maglev vehicle system, we could use the cylinder HTS bulks with the bigger radius.

  14. Process parameters, orientation, and functional properties of melt-processed bulk Y-Ba-Cu-O superconductors

    International Nuclear Information System (INIS)

    Zakharchenko, I.V.; Terryll, K.M.; Rao, K.V.; Balachandran, U.

    1995-03-01

    This study compared the microstructure, texturing, and functional properties (critical currents) of YBa 2 Cu 3 O 7-x -based bulk pellets that were prepared by the quench-melt-growth-process (QMGP), melt-textured growth (MTG), and conventional solid-state reaction (SSR) approaches. Using two X-ray diffraction (XRD) methods, θ-2θ, and rocking curves, the authors found that the individual grains of two melt-processed pellets exhibited remarkable preferred orientational alignment (best rocking curve width = 3.2 degree). However, the direction of the preferred orientation among the grains was random. Among the three types of bulk materials studied, the QMGP sample was found to have the best J c values, ∼ 4,500 A/cm 2 at 77 K in a field of 2 kG, as determined from SQUID magnetic data

  15. Development of YBCO tape conductor fabrication technology

    Energy Technology Data Exchange (ETDEWEB)

    Hong, G W; Kim, C J; Lee, H G. and others

    2001-08-01

    Superconductor when fabricated into wire shape is applied for developing electric power transmission cable, transformer, generator and SMES. Such superconducting power devices are capable of maximizing the efficiency of electricity and are anticipated to contribute for solving the energy problem of humankind. Furthermore the high temperature oxide superconductor developed in late 1980s is superconducting above boiling temperature of liquid nitrogen temperature has strong potential to realize superconducting power device and a lot of researches are being done in this field. Superconducting wire is the most important core material for developing superconducting power device and thermo-mechanical powder in tube process was developed to fabricated Ag/Bi-2223 conductor in long length having high critical current carrying capacity. Several companies fabricate and sell Ag/Bi-2223 superconducting wire longer than km length and used for developed electrical power device. But because of its inherent property of sharp decrease in current carrying capacity when applying high magnetic field, the application of Bi-2223 sire is limited as low as 20 K when the power device is in operating under high magnetic field. The YBCO tape conductor has the advantages of maintaining high critical current applying high magnetic field and can be used to most of the power device without special limitation. The metal substrate having good crystallographic texture and deposition technique which can deposit the good quality superconducting thin film continuously in large area are need to fabricate coated conductor, and this technique can be applied to develop the superconducting current limiter or magnetic field shielding device. A superconducting wire for using in high magnetic field is play a critical role in developing maglev, MRI, SMES, transformer, generator and motor and the continuous film deposition technique can be applied in other industry very much.

  16. Plasma-enhanced chemical vapor deposition for YBCO film fabrication of superconducting fault-current limiter

    Energy Technology Data Exchange (ETDEWEB)

    Jun, Byung Hyuk; Kim, Chan Joong

    2006-05-15

    Since the high-temperature superconductor of oxide type was founded, many researches and efforts have been performed for finding its application field. The YBCO superconducting film fabricated on economic metal substrate with uniform critical current density is considered as superconducting fault-current limiter (SFCL). There are physical and chemical processes to fabricate superconductor film, and it is understood that the chemical methods are more economic to deposit large area. Among them, chemical vapor deposition (CVD) is a promising deposition method in obtaining film uniformity. To solve the problems due to the high deposition temperature of thermal CVD, plasma-enhanced chemical vapor deposition (PECVD) is suggested. This report describes the principle and fabrication trend of SFCL, example of YBCO film deposition by PECVD method, and principle of plasma deposition.

  17. Fiber optic quench detection via optimized Rayleigh Scattering in high-field YBCO accelerator magnets

    Energy Technology Data Exchange (ETDEWEB)

    Flanagan, Gene [North Carolina State Univ., Raleigh, NC (United States)

    2016-02-17

    Yttrium barium copper oxide (YBCO) coated conductors are known for their ability to operate in the superconducting state at relatively high temperatures, even above the boiling point of liquid nitrogen (77 K). When these same conductors are operated at lower temperatures, they are able to operate in much higher magnetic fields than traditional superconductors like NiTi or Nb3Sn. Thus, YBCO superconducting magnets are one of the primary options for generating the high magnetic fields needed for future high energy physics devices. Due to slow quench propagation, quench detection remains one of the primary limitations to YBCO magnets. Fiber optic sensing, based upon Rayleigh scattering, has the potential for spatial resolution approaching the wavelength of light, or very fast temporal resolution at low spatial resolution, and a continuum of combinations in between. This project has studied, theoretically and experimentally, YBCO magnets and Rayleigh scattering quench detection systems to demonstrate feasibility of the systems for YBCO quench protection systems. Under this grant an experimentally validated 3D quench propagation model was used to accurately define the acceptable range of spatial and temporal resolutions for effective quench detection in YBCO magnets and to evaluate present-day and potentially improved YBCO conductors. The data volume and speed requirements for quench detection via Rayleigh scattering required the development of a high performance fiber optic based quench detection/data acquisition system and its integration with an existing voltage tap/thermo-couple based system. In this project, optical fibers are tightly co-wound into YBCO magnet coils, with the fiber on top of the conductor as turn-to-turn insulation. Local changes in the temperature or strain of the conductor are sensed by the optical fiber, which is in close thermal and mechanical contact with the conductor. Intrinsic imperfections in the fiber reflect Rayleigh

  18. Recent development in crystal growth of large-diameter Y-QMG (reg sign) bulk superconductors; Y kei ogata QMG (reg sign) baruku koonchodendotai no kaihatsu jokyo

    Energy Technology Data Exchange (ETDEWEB)

    Fujimoto, T.; Morita, M. [Nippon Steel Corporation, Tokyo (Japan); Masahashi, N. [Tohoku University, Miyagi (Japan). Institute for Materials Research

    1999-11-25

    The current status of large-diameter Y-Ba-Cu-O OMG(reg sign) bulk superconductors is described. 75 mm-diameter QMG(reg sign) samples with fairly concentric trapped-magnetic-flux-density distributions have been successfully grown. In addition, a record-high value of the magnetic levitation force, 171 kgf, measured at 77 K using a 90 mm-diameter Nd-Fe-B magnet has been obtained for a 100 mm-diameter sample. The crystal orientation of subgrains in the sample was determined using Electron Back-Scattering Diffraction as well as using a conventional optical apparatus including a He-Ne-laser. For the sample grown under normal process conditions, the maximum value of the [001]-axis misorientation angles at the subgrain-boundaries we obtained in the c-substructure region is 2.9 degree. However, in the a/b-substructure regions, the misorientation angles are larger, and the maximum value obtained is 6.6 degree, exceeding the critical angle at which a significant reduction of the critical current density occurs in Y123 thin films due to the weak-link problem. (author)

  19. Effects of Bi-2212 addition on the levitation force properties of bulk MgB2 superconductors

    International Nuclear Information System (INIS)

    Taylan Koparan, E.; Savaskan, B.; Guner, S.B.; Celik, S.

    2016-01-01

    We present a detailed investigation of the effects of Bi 2 Sr 2 Ca 1 Cu 2 O 8+κ (Bi-2212) adding on the levitation force and magnetic properties of bulk MgB 2 obtained by hot press method. The amount of Bi-2212 was varied between 0 and 10 wt% (0, 2, 4, 6, 10 wt%) of the total MgB 2 . Moreover, we present MgB 2 bulk samples fabricated by using different production methods including hot pressing method to our knowledge. All samples were prepared by using elemental magnesium (Mg) powder, amorphous nano-boron (B) powder and Bi-2212 powder which are produced by hot press method. As a result of hot press process, compact pellet samples were manufactured. The vertical and lateral levitation force measurements were executed at the temperatures of 20, 24 and 28 K under zero-field-cooled (ZFC) and field-cooled (FC) regimes for samples with various adding levels. At 24 K and 28 K under ZFC regime, the 2 wt% Bi-2212 added sample exhibits a higher vertical levitation force than the pure sample. Bi-2212 added MgB 2 samples compared to the pure sample have lower attractive force values in FC regime. The magnetic field dependence of the critical current density J c was calculated from the M-H loops for Bi-2212 added MgB 2 samples. The 2 wt% Bi-2212 added sample has the best levitation and critical current density performance compared to other samples. The critical temperature (T c ) has slightly dropped from 37.8 K for the pure MgB 2 sample to 36.7 K for the 10 wt% of Bi-2212 added sample. The transition temperature slightly decreases when Bi-2212 adding level is increased. (orig.)

  20. Influence of radius of cylinder HTS bulk on guidance force in a maglev vehicle system

    Science.gov (United States)

    Longcai, Zhang

    2014-07-01

    Bulk superconductors had great potential for various engineering applications, especially in a high-temperature superconducting (HTS) maglev vehicle system. In such a system, the HTS bulks were always exposed to AC external magnetic field, which was generated by the inhomogeneous surface magnetic field of the NdFeB guideway. In our previous work, it was observed that the guidance force of the YBCO bulk over the NdFeB guideway used in the HTS maglev vehicle system was decayed by the application of the AC external magnetic field. In this paper, we investigated the influence of the radius of the cylinder HTS bulk exposed to an AC magnetic field perturbation on the guidance force in the maglev vehicle system. From the results, it was found that the guidance force was stronger for the bulk with bigger radius and the guidance force decay rates of the bulks were approximately equal despite of the different radius in the maglev vehicle system. Therefore, in order to obtain higher guidance force in the maglev vehicle system, we could use the cylinder HTS bulks with the bigger radius.

  1. Co-current Doping Effect of Nanoscale Carbon and Aluminum Nitride on Critical Current Density and Flux Pinning Properties of Bulk MgB2 Superconductors

    Science.gov (United States)

    Tripathi, D.; Dey, T. K.

    2018-05-01

    The effect of nanoscale aluminum nitride (n-AlN) and carbon (n-C) co-doping on superconducting properties of polycrystalline bulk MgB2 superconductor has been investigated. Polycrystalline pellets of MgB2, MgB2 + 0.5 wt% AlN (nano), MgB_{1.99}C_{0.01} and MgB_{1.99}C_{0.01} + 0.5 wt% AlN (nano) have been synthesized by a solid reaction process under inert atmosphere. The transition temperature (TC) estimated from resistivity measurement indicates only a small decrease for C (nano) and co-doped MgB2 samples. The magnetic field response of investigated samples has been measured at 4, 10, and 20 K in the field range ± 6 T. MgB2 pellets co-doped with 0.5 wt% n-AlN and 1 wt% n-C display appreciable enhancement in critical current density (J_C) of MgB2 in both low (≥ 3 times), as well as, high-field region (≥ 15 times). J_C versus H behavior of both pristine and doped MgB2 pellets is well explained in the light of the collective pinning model. Further, the normalized pinning force density f_p(= F_p/F_{pmax}) displays a fair correspondence with the scaling procedure proposed by Eisterer et al. Moreover, the scaled data of the pinning force density (i.e., f_p{-}h data) of the investigated pellets at different temperature are well interpreted by a modified Dew-Hughes expression reported by Sandu and Chee.

  2. Effect of argon addition into oxygen atmosphere on YBCO thin films deposition

    International Nuclear Information System (INIS)

    Mozhaev, P. B.; Borisenko, I. V.; Ovsyannikov, G. A.; Kuehle, A.; Bindslev-Hansen, J.; Johannes, L.; Skov, J. L.

    2002-01-01

    Multicomponent nature of the YBa 2 Cu 3 O x (YBCO) high-temperature superconductor makes difficult fabrication of smooth thin films: every local deviation from stoichiometry can result in seeding of a non-superconducting oxide particle. High density of such particles on typical YBCO thin film surface, however, presumes overall non-stoichiometry of the film. Such an effect can result from (i) non-uniform material transport from target to substrate, and (ii) re-evaporation or re-sputtering from the growing film surface. The first reason is more usual for laser ablation deposition technique, the second is typical for long sputtering deposition processes. Substitution of oxygen with argon in the deposition atmosphere improves surface quality of YBCO thin films deposited both by laser ablation and DC-sputtering at high pressure techniques. In the first case, the ablated species are scattered different ways in the oxygen atmosphere. Addition of argon decreases the inelastic scattering of barium; the proper part of Ar in the deposition atmosphere makes scattering and, hence, transport of all atoms uniform. The YBCO films deposited by DC-sputtering at high pressure technique are Ba-deficient also, but the reason is re-sputtering of Ba from the growing film as a result of negative oxygen ions bombardment. Such bombardment can lead also to chemical interaction of the deposited material with the substrate, as in the case of deposition of YBCO thin film on the CeO 2 buffer layer on sapphire. Substitution of oxygen with argon not only suppresses ion bombardment of the film, but also increases discharge stability due to presence of positive Ar + ions. The limiting factor of argon substitution is sufficient oxygenation of the growing oxide film. When oxygen partial pressure is too small, the superconducting quality of the YBCO thin film decreases and such a decrease cannot be overcome by prolonged oxygenation after deposition. (Authors)

  3. Solderability study of RABiTS-based YBCO coated conductors

    International Nuclear Information System (INIS)

    Zhang Yifei; Duckworth, Robert C.; Ha, Tam T.; Gouge, Michael J.

    2011-01-01

    Study examines the implication of solder and flux selection in YBCO splice joints. Focus is on commercially available RABiTS-based YBCO coated conductors. Solderability varied with solder and flux for three different stabilizations tested. Resistivity of stabilizer was dominant factor in splice joint resistance. Solder materials affected splice joint resistance when solderability was poor. The solderability of commercially available YBa 2 Cu 3 O 7-x (YBCO) coated conductors that were made from Rolling Assisted Biaxially Textured Substrates (RABiTS)-based templates was studied. The coated conductors, also known as second-generation (2G) high temperature superconductor (HTS) wires (in the geometry of flat tapes about 4 mm wide), were laminated with copper, brass, or stainless steel strips as stabilizers. To understand the factors that influence their solderability, surface profilometry and scanning electron microscopy were used to characterize the wire surfaces. The solderability of three solders, 52In48Sn, 67Bi33In, and 100In (wt.%), was evaluated using a standard test (IPC/ECA J-STD-002) and with two different commercial fluxes. It was found that the solderability varied with the solder and flux but the three different wires showed similar solderability for a fixed combination of solder and flux. Solder joints of the 2G wires were fabricated using the tools and the procedures recommended by the HTS wire manufacturer. The solder joints were made in a lap-joint geometry and with the superconducting sides of the two wires face-to-face. The electrical resistances of the solder joints were measured at 77 K, and the results were analyzed to qualify the soldering materials and evaluate the soldering process. It was concluded that although the selection of soldering materials affected the resistance of a solder joint, the resistivity of the stabilizer was the dominant factor.

  4. Magnetic-field dependence of electrothermal conductivity in YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Marino, A.; Uribe, R. [Universidad del Tolima, Ibague (Colombia); Grupo de Superconductividad y Nuevos Materiales, Universidad Nacional de Colombia, Bogota (Colombia)

    2008-11-15

    Experimental measurements of the electrothermal conductivity (P) near T{sub c}, as a function of external magnetic field were carried out in undoped YBCO (123) superconducting samples. The electrothermal conductivity which relates electrical and thermal currents, depends on the applied magnetic field in high T{sub c} materials, contrary to conventional low T{sub c} superconductors where P is nearly independent of the magnetic field. The experimental P(B,T) data determined from resistivity and thermopower measurements were analyzed in terms of theoretical models and showed a behavior consistent with an order-parameter symmetry (OPS) of d{sub x{sup 2}-y{sup 2}}-wave type. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  5. Passivation of Flexible YBCO Superconducting Current Lead With Amorphous SiO2 Layer

    Science.gov (United States)

    Johannes, Daniel; Webber, Robert

    2013-01-01

    Adiabatic demagnetization refrigerators (ADR) are operated in space to cool detectors of cosmic radiation to a few 10s of mK. A key element of the ADR is a superconducting magnet operating at about 0.3 K that is continually energized and de-energized in synchronism with a thermal switch, such that a piece of paramagnetic salt is alternately warm in a high magnetic field and cold in zero magnetic field. This causes the salt pill or refrigerant to cool, and it is able to suck heat from an object, e.g., the sensor, to be cooled. Current has to be fed into and out of the magnets from a dissipative power supply at the ambient temperature of the spacecraft. The current leads that link the magnets to the power supply inevitably conduct a significant amount of heat into the colder regions of the supporting cryostat, resulting in the need for larger, heavier, and more powerful supporting refrigerators. The aim of this project was to design and construct high-temperature superconductor (HTS) leads from YBCO (yttrium barium copper oxide) composite conductors to reduce the heat load significantly in the temperature regime below the critical temperature of YBCO. The magnet lead does not have to support current in the event that the YBCO ceases to be superconducting. Cus - tomarily, a normal metal conductor in parallel with the YBCO is a necessary part of the lead structure to allow for this upset condition; however, for this application, the normal metal can be dispensed with. Amorphous silicon dioxide is deposited directly onto the surface of YBCO, which resides on a flexible substrate. The silicon dioxide protects the YBCO from chemically reacting with atmospheric water and carbon dioxide, thus preserving the superconducting properties of the YBCO. The customary protective coating for flexible YBCO conductors is silver or a silver/gold alloy, which conducts heat many orders of magnitude better than SiO2 and so limits the use of such a composite conductor for passing current

  6. Effects of artificial holes in very large single-grain Y{sub 1.5}Ba{sub 2}Cu{sub 3}O{sub 7-y} bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Park, S. D.; Jun, B. H.; Kim, C. J. [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Park, H. W. [Korea University of Technology and Education, Cheonan (Korea, Republic of)

    2017-09-15

    The effects of artificial holes on the trapped magnetic fields and magnetic levitation forces of very large single-grain Y{sub 1.5}Ba{sub 2}Cu{sub 3}O{sub 7-y} (Y1.5) bulk superconductors were studied. Artificial holes were made for Y1.5 powder compacts by die pressing using cylindrical dies with a diameter of 30 mm or 40 m, or rectangular dies with a side length of 50 mm. The single grain Y1.5 bulk superconductors (25 mm, 33 mm in diameter and 42 mm in side length) with artificial holes were fabricated using a top-seeded melt growth (TSMG) process for the die-pressed Y1.5 powder compacts. The magnetic levitation forces at 77 K of the 25 mm single grain Y1.5 samples with one (diameters of 4.2 mm) or six artificial holes (diameters of 2.5 mm) were 10-17% higher than that of the Y1.5 sample without artificial holes. The trapped magnetic fields at 77 K of the Y1.5 samples with artificial holes were also 9.6-18% higher than that of the Y1.5 sample without artificial holes. The 33 mm and 42 mm single grain Y1.5 samples with artificial holes (2.5 mm and 4.2 mm in diameter) also showed trapped magnetic fields 10-13% higher than that of the Y1.5 samples without artificial holes in spite of the reduced superconducting volume fraction due to the presence of artificial holes. The property enhancement in the large single grain Y1.5 bulk superconductors appears to be attributed to the formation of the pore-free regions near the artificial holes and the homogeneous oxygen distribution in the large Y123 grains.

  7. Numerical simulation and analysis of single grain YBCO processed from graded precursor powders

    OpenAIRE

    Zou, J; Ainslie, Mark Douglas; Hu, D; Zhai, W; Kumar, N Devendra; Durrell, John Hay; Shi, Yunhua; Cardwell, David Anthony

    2015-01-01

    Large single-grain bulk high-temperature superconducting materials can trap high magnetic fields in comparison with conventional permanent magnets, making them ideal candidates to develop more compact and efficient devices, such as actuators, magnetic levitation systems, flywheel energy storage systems and electric machines. However, macro-segregation of Y-211 inclusions in melt processed Y–Ba–Cu–O (YBCO) limits the macroscopic critical current density Jc of such bulk supercond...

  8. Ag induced suppression of irradiation response in YBCO/Ag composite thin films

    International Nuclear Information System (INIS)

    Behera, D.; Mohanty, T.; Mohanta, D.; Patnaik, K.; Mishra, N.C.; Senapati, L.; Kanjilal, D.; Mehta, G.K.; Pinto, R.

    1999-01-01

    Practical application of cuprate superconductors in radiation environment demands that these systems remain insensitive to the irradiation induced defects. The cuprate superconductors however are many orders of magnitude more sensitive than the conventional low T c superconductors. To suppress the irradiation sensitivity of cuprates we consider a crystal engineering approach where metal ions as Ag is made to occupy inter and intra-granular sites of YBa 2 Cu 3 O 7 thin films. We show that superconducting and normal state properties of YBCO/Ag composite thin films prepared by laser ablation remain unchanged under 140 MeV Si ion irradiation up to fluence of 8 x 10 14 ions/cm 2 . The inter- and intra-granular occupancy of Ag is shown to induce microstructural modifications and rigidity to the CuO chains respectively which in turn lead to the radiation insensitivity of the composite films. (author)

  9. Flux Pinning and AC Loss in Second Generation High Temperature Superconductor Wires

    Energy Technology Data Exchange (ETDEWEB)

    Paranthaman, Mariappan Parans [ORNL; Selvamanickam, V. [SuperPower Incorporated, Schenectady, New York

    2007-01-01

    Major advances have been made in the last 18 years in high-temperature superconductor (HTS) reserach and development, resulting in increased use of HTS materials in commerical and pre-commercial electric-power applications. This new and important book addresses the issues related to flux pinning, AC losses and thick YBCO film growth. Written by top most scientists in the world, it presents the current status and issues related to YBCO coated conductors and the need for further fundamental materials science work in YBCO coated conductor. It will be a useful handbook for years to come.

  10. Critical current in nonhomogeneous YBCO coated conductors

    International Nuclear Information System (INIS)

    Rostila, L; Mikkonen, R; Lehtonen, J

    2008-01-01

    The critical current of an YBCO tape is determined by the magnetic field inside the YBCO layer and the quality of YBCO material. In thick YBCO layers the average critical current density is reduced by the self-field and decreased material quality. In this paper the combined influence of the material nonhomogeneities and self-field on the critical current of YBCO tapes is scrutinised. First, the zero field critical current density was assumed to decrease along the YBCO thickness. Secondly, the possible defects created in the cutting of YBCO tapes were modelled as a function of lowered critical current density near the tape edges. In both cases the critical current was computed numerically with integral element method. The results suggest that the variation of zero field critical current density, J c0 , along the tape thickness does not effect on the critical current if the mean value of J c0 is kept constant. However, if J c0 is varied along the tape width the critical current can change due to the variated self-field. The computations can be used to determine when it is possible to evaluate the average zero field critical current density from a voltage-current measurement with an appropriate accuracy

  11. Calibration of Hall sensor array for critical current measurement of YBCO tape with ferromagnetic substrate

    International Nuclear Information System (INIS)

    Zhu, Yunpeng; Wang, Gang; Liu, Liyuan; Yang, Xinsheng; Zhao, Yong

    2015-01-01

    Abstract : HAS (Hall sensor array) is a powerful tool to detect the uniformity of HTS (high temperature superconductor) tape through mapping the distribution of remanent or shielding field along the surface of the tape. However, measurement of HTS tape with ferromagnetic parts by HSA is still an issue because the ferromagnetic substrate has influence on the magnetic field around the HTS layer. In this work, a continuous HSA system has been designed to measure the critical current of the YBCO tape with ferromagnetic substrate. The relationship between the remanent field and critical current was calibrated by the finite element method. The result showed that the HSA is an effective method for evaluating the critical current of the HTS tape with ferromagnetic substrate. - Highlight: • A continuous Hall sensor array system has been designed. • The inhomogeneity of YBCO tape with ferromagnetic substrate can be detected by HAS. • Finite element method is an effective method for calibrating the remanent field.

  12. Calibration of Hall sensor array for critical current measurement of YBCO tape with ferromagnetic substrate

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Yunpeng; Wang, Gang; Liu, Liyuan [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Yang, Xinsheng, E-mail: xsyang@swjtu.edu.cn [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Zhao, Yong [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney 2052, NSW (Australia)

    2015-12-15

    Abstract : HAS (Hall sensor array) is a powerful tool to detect the uniformity of HTS (high temperature superconductor) tape through mapping the distribution of remanent or shielding field along the surface of the tape. However, measurement of HTS tape with ferromagnetic parts by HSA is still an issue because the ferromagnetic substrate has influence on the magnetic field around the HTS layer. In this work, a continuous HSA system has been designed to measure the critical current of the YBCO tape with ferromagnetic substrate. The relationship between the remanent field and critical current was calibrated by the finite element method. The result showed that the HSA is an effective method for evaluating the critical current of the HTS tape with ferromagnetic substrate. - Highlight: • A continuous Hall sensor array system has been designed. • The inhomogeneity of YBCO tape with ferromagnetic substrate can be detected by HAS. • Finite element method is an effective method for calibrating the remanent field.

  13. First steps towards cube textured nickel profile wires for YBCO-coated conductors

    International Nuclear Information System (INIS)

    Eickemeyer, J.; Gueth, A.; Freudenberger, J.; Holzapfel, B.; Schultz, L.

    2011-01-01

    The cube texture as a typical sheet texture can also be formed by cold drawing and recrystallization in profile wires. Cube textured Ni profile wires containing up to 96.2% cube oriented grains in the central region were obtained. Forthcoming investigations are promising to get a textured substrate wire for YBCO-coated conductors. Cube textured nickel alloy tapes prepared by cold rolling and annealing (RABiTS method) represent a standard metallic substrate for superconductor coatings of the YBa 2 Cu 3 O 7-δ (YBCO) type. These tapes have a width to thickness ratio of about 30-100. However, a value of close to one is optimal concerning low energetic losses under alternating current applications. First experiments on micro-alloyed nickel prove that the cube texture as a typical sheet texture can also be formed in profile wires with a rectangular cross-section after cold drawing and recrystallization treatment.

  14. Phase dynamics of low critical current density YBCO Josephson junctions

    Energy Technology Data Exchange (ETDEWEB)

    Massarotti, D., E-mail: dmassarotti@na.infn.it [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, Via Cinthia, 80126 Napoli (Italy); CNR-SPIN UOS Napoli, Complesso Universitario di Monte Sant’Angelo, Via Cinthia, 80126 Napoli (Italy); Stornaiuolo, D. [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, Via Cinthia, 80126 Napoli (Italy); Rotoli, G. [Dipartimento di Ingegneria Industriale e dell’Informazione, Seconda Università di Napoli, Via Roma 29, 81031 Aversa (CE) (Italy); Carillo, F. [Nest, Scuola Normale Superiore, Piazza San Silvestro 12, 56126 Pisa (Italy); Galletti, L. [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, Via Cinthia, 80126 Napoli (Italy); CNR-SPIN UOS Napoli, Complesso Universitario di Monte Sant’Angelo, Via Cinthia, 80126 Napoli (Italy); Longobardi, L. [Dipartimento di Ingegneria Industriale e dell’Informazione, Seconda Università di Napoli, Via Roma 29, 81031 Aversa (CE) (Italy); American Physical Society, 1 Research Road, Ridge, NY 11961 (United States); Beltram, F. [Nest, Scuola Normale Superiore, Piazza San Silvestro 12, 56126 Pisa (Italy); Tafuri, F. [CNR-SPIN UOS Napoli, Complesso Universitario di Monte Sant’Angelo, Via Cinthia, 80126 Napoli (Italy); Dipartimento di Ingegneria Industriale e dell’Informazione, Seconda Università di Napoli, Via Roma 29, 81031 Aversa (CE) (Italy)

    2014-08-15

    Highlights: • We study the phase dynamics of YBaCuO Josephson junctions using various tools. • We derive information on the dissipation in a wide range of transport parameters. • Dissipation in such devices can be described by a frequency dependent damping model. • The use of different substrates allows us to tune the shell circuit. - Abstract: High critical temperature superconductors (HTS) based devices can have impact in the study of the phase dynamics of Josephson junctions (JJs) thanks to the wide range of junction parameters they offer and to their unconventional properties. Measurements of current–voltage characteristics and of switching current distributions constitute a direct way to classify different regimes of the phase dynamics and of the transport, also in nontrivial case of the moderately damped regime (MDR). MDR is going to be more and more common in JJs with advances in nanopatterning superconductors and synthesizing novel hybrid systems. Distinctive signatures of macroscopic quantum tunneling and of thermal activation in presence of different tunable levels of dissipation have been detected in YBCO grain boundary JJs. Experimental data are supported by Monte Carlo simulations of the phase dynamics, in a wide range of temperatures and dissipation levels. This allows us to quantify dissipation in the MDR and partially reconstruct a phase diagram as guideline for a wide range of moderately damped systems.

  15. Pinning Mechanisms in YBCO Tapes

    CERN Document Server

    Spera, Marcello; Ballarino, Amalia

    2015-01-01

    In this thesis work, a study on flux pinning mechanisms of commercial YBCO tapes is presented. This study has been performed via critical current characterization using transport (via direct I-V curves) and magnetization (via a Vibrating Sample Magnetometer) measurements. The latter ones turned out to be better concerning the comprehension of the pinning landscape of the provided samples, as a wider range of magnetic fields and temperatures is available for those measurements in the setup I used. The comparison of the experimental data with existing theoretical models allowed me to draw a picture of the pinning mechanisms underlying in each sample, and they turned out to be quite different one another. Moreover, for high-performance research tapes, another interesting feature has been found: the counterplay between the self-field critical current and the in-field one. Very well engineered artificial pinning structures limit the self-field critical current density due to the hi...

  16. Intermodulation distortion and surface resistance in impurity-doped YBCO and MgB{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Agassi, Y.D. [Naval Surface Warfare Center, Carderock Division, Bethesda, MD 20817 (United States); Oates, D.E., E-mail: oates@ll.mit.edu [MIT-Lincoln Laboratory, Lexington, MA 02420 (United States)

    2014-11-15

    Highlights: • Calculations of impurity-doping effects on surface resistance and intermodulation distortion. • The calculations are compared with previously published measurements in YBCO and MgB{sub 2}. • Excellent agreement between calculations and experiments are shown. • The effects of the symmetry of the energy gap are presented and discussed. - Abstract: Calculations of the microwave intermodulation distortion (IMD) and surface resistance of impurity-doped YBCO, MgB{sub 2} and Nb are presented. These are qualitatively distinct superconductors due to their energy-gap symmetries, d-wave (ℓ = 2), i-wave (ℓ = 6) and s-wave (ℓ = 0), respectively. The calculations are compared with previously published IMD and surface-resistance measurements of impurity-doped YBCO and Nb. The agreement between the data and fitted calculations is excellent in all cases. In the absence of IMD and surface-resistance measurements for doped MgB{sub 2}, we present representative predictions. The calculations are based on a Green’s-function approach that yields analytical expressions for the penetration depth and the nonlinear kernel in the constitutive relation. This penetration-depth expression reproduces the measured T{sup 2} low-temperature variation for doped superconductors and the surface-resistance reduction over that of the pure material. Regarding the IMD in superconductors with a nodal energy gap, the effect of doping is to enhance its magnitude and suppress its low-temperature 1/T{sup 2} divergence predicted by the nonlinear Meissner effect.

  17. Flux cutting in superconductors

    International Nuclear Information System (INIS)

    Campbell, A M

    2011-01-01

    This paper describes experiments and theories of flux cutting in superconductors. The use of the flux line picture in free space is discussed. In superconductors cutting can either be by means of flux at an angle to other layers of flux, as in longitudinal current experiments, or due to shearing of the vortex lattice as in grain boundaries in YBCO. Experiments on longitudinal currents can be interpreted in terms of flux rings penetrating axial lines. More physical models of flux cutting are discussed but all predict much larger flux cutting forces than are observed. Also, cutting is occurring at angles between vortices of about one millidegree which is hard to explain. The double critical state model and its developments are discussed in relation to experiments on crossed and rotating fields. A new experiment suggested by Clem gives more direct information. It shows that an elliptical yield surface of the critical state works well, but none of the theoretical proposals for determining the direction of E are universally applicable. It appears that, as soon as any flux flow takes place, cutting also occurs. The conclusion is that new theories are required. (perspective)

  18. Vortex cutting in superconductors

    Science.gov (United States)

    Vlasko-Vlasov, Vitalii K.; Koshelev, Alexei E.; Glatz, Andreas; Welp, Ulrich; Kwok, Wai-K.

    2015-03-01

    Unlike illusive magnetic field lines in vacuum, magnetic vortices in superconductors are real physical strings, which interact with the sample surface, crystal structure defects, and with each other. We address the complex and poorly understood process of vortex cutting via a comprehensive set of magneto-optic experiments which allow us to visualize vortex patterns at magnetization of a nearly twin-free YBCO crystal by crossing magnetic fields of different orientations. We observe a pronounced anisotropy in the flux dynamics under crossing fields and the filamentation of induced supercurrents associated with the staircase vortex structure expected in layered cuprates, flux cutting effects, and angular vortex instabilities predicted for anisotropic superconductors. At some field angles, we find formation of the vortex domains following a type-I phase transition in the vortex state accompanied by an abrupt change in the vortex orientation. To clarify the vortex cutting scenario we performed time-dependent Ginzburg-Landau simulations, which confirmed formation of sharp vortex fronts observed in the experiment and revealed a left-handed helical instability responsible for the rotation of vortices. This work was supported by the U.S. Department of Energy, Office of Science, Materials Sciences and Engineering Division.

  19. Measurement of oxygen disorder and nano-twin microstructure associated with columnar defects in YBCO

    International Nuclear Information System (INIS)

    Yan, Y.

    1998-01-01

    Studies of defects generated by high energy (>1 GeV) heavy ion irradiation in high-Tc superconductors have been performed by transmission electron microscopy (TEM). Our study shows that high dose irradiation leads to the formation of nano-twins, by which the columnar defects are connected. An analysis of the local Fourier components of the image intensity in [001] lattice images indicates that these new ''twin'' boundaries are much more diffuse than pre-existing twin boundaries in YBCO. The mechanism of the formation of nano-twin boundaries on {110} planes and their possible relation to superconducting properties are discussed

  20. Topological surface states in nodal superconductors.

    Science.gov (United States)

    Schnyder, Andreas P; Brydon, Philip M R

    2015-06-24

    Topological superconductors have become a subject of intense research due to their potential use for technical applications in device fabrication and quantum information. Besides fully gapped superconductors, unconventional superconductors with point or line nodes in their order parameter can also exhibit nontrivial topological characteristics. This article reviews recent progress in the theoretical understanding of nodal topological superconductors, with a focus on Weyl and noncentrosymmetric superconductors and their protected surface states. Using selected examples, we review the bulk topological properties of these systems, study different types of topological surface states, and examine their unusual properties. Furthermore, we survey some candidate materials for topological superconductivity and discuss different experimental signatures of topological surface states.

  1. Macroscopic theory of superconductors

    International Nuclear Information System (INIS)

    Carr, W.J. Jr.

    1981-01-01

    A macroscopic theory for bulk superconductors is developed in the framework of the theory for other magnetic materials, where ''magnetization'' current is separated from ''free'' current on the basis of scale. This contrasts with the usual separation into equilibrium and nonequilibrium currents. In the present approach magnetization, on a large macroscopic scale, results from the vortex current, while the Meissner current and other surface currents are surface contributions to the Maxwell j. The results are important for the development of thermodynamics in type-II superconductors. The advantage of the description developed here is that magnetization becomes a local concept and its associated magnetic field can be given physical meaning

  2. Microstructure and property correlations in high-temperature superconductors

    Science.gov (United States)

    Kalyanaraman, Ramakrishnan

    1998-11-01

    The work in this dissertation is intended at developing high quality device gradefilms of the high temperature (high-Tsbc) superconductor, Yttrium Barium Copper Oxide (YBCO), on MgO(001) substrates. Three approaches have been used to achieve the above goal, (i) The use of a SrTiOsb3 buffer layer, (ii) The use of Ag to enhance the growth of YBCO films and (iii) Investigation of the atomic structure-property correlations of low-angle grain boundaries in these films. Thin film heterostructures of YBCO/MgO and YBCO/SrTiOsb3/MgO were fabricated by pulsed laser deposition (PLD), using a 248 nm KrF excimer laser. Analysis of the structure and measurement of superconducting properties of the films were carried out to optimize the suitable conditions under each approach. The key findings were, (i) Single crystal-like SrTiOsb3 buffer layers can be grown and they give the highest JsbcYBCO films, (ii) An in-depth study of the role of Ag showed that it enhanced film growth of YBCO thereby improving its quality, and (iii) Low-angle boundaries in YBCO/MgO occur with two probable habit planes and the Jsbcs across them differ slightly. A systematic investigation of the crystalline quality of the SrTiOsb3 films deposited by PLD was performed as a function of oxygen partial pressure (pOsb2) and substrate temperature (Tsbc). The highest quality films were grown in the pOsb2 range of 0.1-1 mTorr at 750sp°C. The films had as-deposited x-ray diffraction rocking curve (omega) values of {˜}0.70sp° and Rutherford backscattering channeling yields (chisbmin) of 5% as compared to omega˜1.40sp° and chisbmin˜14% for the film deposited in 100 mTorr of pOsb2. The x-ray phi-scans showed epitaxial cube-on-cube alignment of the SrTiOsb3 films on MgO(001) substrates. Thermal annealing of the SrTiOsb3 films further improved the quality, and the 1 mTorr films gave omega{˜}0.13sp° and chisbmin˜2.0%. Transmission electron microscopy investigations (TEM) of these films showed that the defects in

  3. A novel heat engine for magnetizing superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Coombs, T A; Hong, Z; Zhu, X [Cambridge University Engineering Department, Trumpington Street, CB2 1PZ (United Kingdom); Krabbes, G [IFW Dresden, Helmholtzstrasse 20, 01069 Dresden (Germany)

    2008-03-01

    The potential of bulk melt-processed YBCO single domains to trap significant magnetic fields (Tomita and Murakami 2003 Nature 421 517-20; Fuchs et al 2000 Appl. Phys. Lett. 76 2107-9) at cryogenic temperatures makes them particularly attractive for a variety of engineering applications including superconducting magnets, magnetic bearings and motors (Coombs et al 1999 IEEE Trans. Appl. Supercond. 9 968-71; Coombs et al 2005 IEEE Trans. Appl. Supercond. 15 2312-5). It has already been shown that large fields can be obtained in single domain samples at 77 K. A range of possible applications exist in the design of high power density electric motors (Jiang et al 2006 Supercond. Sci. Technol. 19 1164-8). Before such devices can be created a major problem needs to be overcome. Even though all of these devices use a superconductor in the role of a permanent magnet and even though the superconductor can trap potentially huge magnetic fields (greater than 10 T) the problem is how to induce the magnetic fields. There are four possible known methods: (1) cooling in field; (2) zero field cooling, followed by slowly applied field; (3) pulse magnetization; (4) flux pumping. Any of these methods could be used to magnetize the superconductor and this may be done either in situ or ex situ. Ideally the superconductors are magnetized in situ. There are several reasons for this: first, if the superconductors should become demagnetized through (i) flux creep, (ii) repeatedly applied perpendicular fields (Vanderbemden et al 2007 Phys. Rev. B 75 (17)) or (iii) by loss of cooling then they may be re-magnetized without the need to disassemble the machine; secondly, there are difficulties with handling very strongly magnetized material at cryogenic temperatures when assembling the machine; thirdly, ex situ methods would require the machine to be assembled both cold and pre-magnetized and would offer significant design difficulties. Until room temperature superconductors can be prepared, the

  4. A novel heat engine for magnetizing superconductors

    International Nuclear Information System (INIS)

    Coombs, T A; Hong, Z; Zhu, X; Krabbes, G

    2008-01-01

    The potential of bulk melt-processed YBCO single domains to trap significant magnetic fields (Tomita and Murakami 2003 Nature 421 517-20; Fuchs et al 2000 Appl. Phys. Lett. 76 2107-9) at cryogenic temperatures makes them particularly attractive for a variety of engineering applications including superconducting magnets, magnetic bearings and motors (Coombs et al 1999 IEEE Trans. Appl. Supercond. 9 968-71; Coombs et al 2005 IEEE Trans. Appl. Supercond. 15 2312-5). It has already been shown that large fields can be obtained in single domain samples at 77 K. A range of possible applications exist in the design of high power density electric motors (Jiang et al 2006 Supercond. Sci. Technol. 19 1164-8). Before such devices can be created a major problem needs to be overcome. Even though all of these devices use a superconductor in the role of a permanent magnet and even though the superconductor can trap potentially huge magnetic fields (greater than 10 T) the problem is how to induce the magnetic fields. There are four possible known methods: (1) cooling in field; (2) zero field cooling, followed by slowly applied field; (3) pulse magnetization; (4) flux pumping. Any of these methods could be used to magnetize the superconductor and this may be done either in situ or ex situ. Ideally the superconductors are magnetized in situ. There are several reasons for this: first, if the superconductors should become demagnetized through (i) flux creep, (ii) repeatedly applied perpendicular fields (Vanderbemden et al 2007 Phys. Rev. B 75 (17)) or (iii) by loss of cooling then they may be re-magnetized without the need to disassemble the machine; secondly, there are difficulties with handling very strongly magnetized material at cryogenic temperatures when assembling the machine; thirdly, ex situ methods would require the machine to be assembled both cold and pre-magnetized and would offer significant design difficulties. Until room temperature superconductors can be prepared, the

  5. The superconductor

    International Nuclear Information System (INIS)

    Lad, J.K.

    1979-01-01

    Techniques for fabrication of a few important superconductors like Nb, Ti and Nb 3 Sn are described. Copper or bronze or both can be used as a matrix in the superconductor. Current densities obtained for different ratios of copper to superconductor are studied. The specifications of multi-filament Nb 3 Sn superconductors are given. The relative merits of the two superconductors are discussed. The temperature range obtained is approximately 3 0 K and a magnetic field of 9T(tesla) can be achieved. (A.K.)

  6. A novel method of flat YBCO rings development for shield-type superconducting fault current limiters fabrication

    International Nuclear Information System (INIS)

    Hekmati, Arsalan; Hosseini, Mehdi; Vakilian, Mehdi; Fardmanesh, Mehdi

    2012-01-01

    A method has been proposed for flat YBCO ring Fabrication. A prototype SFCL with proposed design has been fabricated using the rings. J c characteristics of the rings are measured using an innovative method. The application of flat superconductor rings has been investigated in the structure of inductive shield-type high temperature superconducting fault current limiters, HT c -SFCL. A laboratory scale inductive shield-type HT c -SFCL has been designed and fabricated using flat superconductor rings. The fabrication process has been fully presented. YBCO powder has been used for the fabrication of superconductor rings. This fabrication process, being quite innovative, is introduced completely. The method of the trapped field measurement has been used for the critical current density measurement of the fabricated superconductor rings. The device with nominal current of 2 A was tested in a 30 V circuit. The SFCL successfully limited the fault currents of up to 10 times the nominal current to an approximately fixed value of 3 A. The voltage-current characteristic of the fabricated prototype has also been obtained and has shown compatibility with the fault current limitation results.

  7. Thermodynamical fluctuations and critical behavior in weakly disordered YBCO thin and ultra-thin films

    International Nuclear Information System (INIS)

    Lesueur, J.; Aprili, M.; Degoy, S.; Chambonnet, D.; Keller, D.

    1996-01-01

    The specific role of disorder in the transport properties of YBCO has been investigated, using both light-ion irradiation of thin films to finely tune the amount of atomic disorder, and ultra-thin films grown to study possible dimensional effects. For weak disorder, the samples display a resistive transition typical of the mean-field paraconductive regime of a homogeneous media, well described by the Lawrence and Doniach model for layered superconductors. As the disorder increases, two effects take place. First, the c-axis coherence length becomes shorter, leading to a more anisotropic material, as shown by the excess conductivity above T c . Second, an incipient granularity is revealed, leading to a less sharper transition, which is analyzed within the random 3D XY critical model for the paracoherence transition. Two main results are derived: an experimental test of the Ginzburg criteria for the paracoherence transition, and a new fluctuation regime in nanometric grain size superconductors

  8. Microstructure of Josephson junctions: Effect on supercurrent transport in YBCO grain boundary and barrier layer junctions

    International Nuclear Information System (INIS)

    Merkle, K.L.; Huang, Y.

    1998-01-01

    The electric transport of high-temperature superconductors, such as YBa 2 Cu 3 O 7-x (YBCO), can be strongly restricted by the presence of high-angle grain boundaries (GB). This weak-link behavior is governed by the macroscopic GB geometry and the microscopic grain boundary structure and composition at the atomic level. Whereas grain boundaries present a considerable impediment to high current applications of high T c materials, there is considerable commercial interest in exploiting the weak-link-nature of grain boundaries for the design of microelectronic devices, such as superconducting quantum interference devices (SQUIDs). The Josephson junctions which form the basis of this technology can also be formed by introducing artificial barriers into the superconductor. The authors have examined both types of Josephson junctions by EM techniques in an effort to understand the connection between microstructure/chemistry and electrical transport properties. This knowledge is a valuable resource for the design and production of improved devices

  9. Influence of the size of Gd211 starting powder on the critical current density of Gd-Ba-Cu-O bulk superconductor

    International Nuclear Information System (INIS)

    Nariki, S.; Seo, S.J.; Sakai, N.; Murakami, M.

    2000-01-01

    The relationship between the particle size of Gd211 powder in the precursor and the particle size of Gd211 inclusions in Gd-Ba-Cu-O bulk has been investigated. Gd211 starting powders with various diameters were prepared by the calcination of Gd 2 O 3 , BaO 2 and CuO powders at different temperatures between 800 and 1000 deg. C. The particle size of Gd211 in the melt-grown bulk was proportional to the particle size of the initial Gd211 powder. In conclusion, the employment of fine Gd211 powder led to a size reduction of 211 particles in the bulk, while largely enhancing the J c values in low magnetic fields. A large Gd-Ba-Cu-O/Ag bulk sample, 32 mm in diameter, could also be fabricated by the hot-seeding method. The maximum trapped field value revealed 1.5 T at 77 K. (author)

  10. Ferromagnet / superconductor oxide superlattices

    Science.gov (United States)

    Santamaria, Jacobo

    2006-03-01

    The growth of heterostructures combining oxide materials is a new strategy to design novel artificial multifunctional materials with interesting behaviors ruled by the interface. With the (re)discovery of colossal magnetoresistance (CMR) materials, there has been renewed interest in heterostructures involving oxide superconductors and CMR ferromagnets where ferromagnetism (F) and superconductivity (S) compete within nanometric distances from the interface. In F/S/F structures involving oxides, interfaces are especially complex and various factors like interface disorder and roughness, epitaxial strain, polarity mismatch etc., are responsible for depressed magnetic and superconducting properties at the interface over nanometer length scales. In this talk I will focus in F/S/F structures made of YBa2Cu3O7 (YBCO) and La0.7Ca0.3MnO3 (LCMO). The high degree of spin polarization of the LCMO conduction band, together with the d-wave superconductivity of the YBCO make this F/S system an adequate candidate for the search of novel spin dependent effects in transport. We show that superconductivity at the interface is depressed by various factors like charge transfer, spin injection or ferromagnetic superconducting proximity effect. I will present experiments to examine the characteristic distances of the various mechanisms of superconductivity depression. In particular, I will discuss that the critical temperature of the superconductor depends on the relative orientation of the magnetization of the F layers, giving rise to a new giant magnetoresistance effect which might be of interest for spintronic applications. Work done in collaboration with V. Peña^1, Z. Sefrioui^1, J. Garcia-Barriocanal^1, C. Visani^1, D. Arias^1, C. Leon^1 , N. Nemes^2, M. Garcia Hernandez^2, S. G. E. te Velthuis^3, A. Hoffmann^3, M. Varela^4, S. J. Pennycook^4. Work supported by MCYT MAT 2005-06024, CAM GR- MAT-0771/2004, UCM PR3/04-12399 Work at Argonne supported by the Department of Energy, Basic

  11. Organic superconductors

    International Nuclear Information System (INIS)

    Bulaevskij, L.N.; Shchegolev, I.F.

    1986-01-01

    Main achievements in creating new organic conducting materials - synthetic metals and superconductors, are considered. The processes of superconductivity occurrence in organic materials are discussed. It is shown that conjugated bonds between C and H atoms in organic molecules play an important role in this case. At present ''crystal direction'' in organic superconductor synthesis is mainly developed. Later on, organic superconductor crystals are supposed to be introduced into usual polymers, e.g. polyethylene

  12. High temperature superconductors for fusion magnets -influence of neutron irradiation

    International Nuclear Information System (INIS)

    Chudy, M.; Eisterer, M.; Weber, H. W.

    2010-01-01

    In this work authors present the results of study of influence of neutron irradiation of high temperature superconductors for fusion magnets. High temperature superconductors (type of YBCO (Yttrium-Barium-Copper-Oxygen)) are strong candidates to be applied in the next step of fusion devices. Defects induced by fast neutrons are effective pinning centres, which can significantly improve critical current densities and reduce J c anisotropy. Due to induced lattice disorder, T c is reduced. Requirements for ITER (DEMO) are partially achieved at 64 K.

  13. Critical state of anisotropic hard superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Romero-Salazar, C; Perez-RodrIguez, F [Instituto de FIsica, Universidad Autonoma de Puebla, Apdo Post J-48, Puebla, Pue 72570 (Mexico)

    2003-11-01

    The magnetic response of anisotropic irreversible type-II superconductors is investigated theoretically. Using an elliptic vertical law for the electric field E as a function of the current density J, we have reproduced available experimental magnetization curves of YBCO samples with the c axis lying in the sample plane. Specifically, we could reproduce quantitatively and interpret correctly the appearance of additional extrema and segments with relatively small slopes of the virgin magnetization curves when the direction of the applied magnetic field differs from the principal axes. The notable deformation of magnetization curves in a tilted magnetic field is connected to the strong coupling between the components of the magnetic induction.

  14. Transport AC losses in YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Majoros, M [Ohio State University, Columbus, OH 43210 (United States); Ye, L [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Velichko, A V [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Coombs, T A [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Sumption, M D [Ohio State University, Columbus, OH 43210 (United States); Collings, E W [Ohio State University, Columbus, OH 43210 (United States)

    2007-09-15

    Transport AC loss measurements have been made on YBCO-coated conductors prepared on two different substrate templates-RABiTS (rolling-assisted biaxially textured substrate) and IBAD (ion-beam-assisted deposition). RABiTS samples show higher losses compared with the theoretical values obtained from the critical state model, with constant critical current density, at currents lower than the critical current. An origin of this extra AC loss was demonstrated experimentally by comparison of the AC loss of two samples with different I-V curves. Despite a difference in I-V curves and in the critical currents, their measured losses, as well as the normalized losses, were practically the same. However, the functional dependence of the losses was affected by the ferromagnetic substrate. An influence of the presence of a ferromagnetic substrate on transport AC losses in YBCO film was calculated numerically by the finite element method. The presence of a ferromagnetic substrate increases transport AC losses in YBCO films depending on its relative magnetic permeability. The two loss contributions-transport AC loss in YBCO films and ferromagnetic loss in the substrate-cannot be considered as mutually independent.

  15. AFM plough YBCO micro bridges: substrate effects

    CSIR Research Space (South Africa)

    Elkaseh, A

    2009-04-01

    Full Text Available AFM nanolithography was used as a novel cutting technique to define micro-size YBCO superconducting constrictions. Researchers studied the substrate effects on MgO and STO substrates and showed that the observed Shapiro steps from the bridges on STO...

  16. Memory effect in the high-temperature superconducting bulks

    International Nuclear Information System (INIS)

    Zhang, Xing-Yi; Zhou, Jun; Zhou, You-He

    2013-01-01

    Highlights: •Effects of temperature cycles on levitation force relaxation are investigated. •Memory effect of the YBCO bulks is observed in experiments. •With an increase of temperature, memory of the superconductor is gradually lost. -- Abstract: We present an experimental investigation of the relaxation of vertical force components in a high-temperature superconducting levitation system with different temperature cycle processes. For a selected ambient temperature (T 1 ) of the system, the experimental results show that the relaxations of the levitation forces are strongly dependent on the initial temperature. When the sample was submitted to temperature jumps around T 1 , the sample temperature was regulated at T 2 , and there were two cases of the experiments, ΔT = T 2 − T 1 0 (positive temperature cycle). It was found that in the case of negative temperature cycle, the superconducting samples have memory effect. And for the positive temperature cycle, with the experimental temperature increase, the memory effect of samples is gradually losing. Additionally, with the increase of temperature, the influences of the negative and positive temperature cycle on the levitation force relaxation are unsymmetrical. All the results are interpreted by using the characteristics of the free energy ‘ground’ plot of the Spin-glasses qualitatively

  17. Current induced magnetic flux response in frustrated three-band superconductors as a bulk probe of broken time reversal symmetry (BTRS) ground states

    Energy Technology Data Exchange (ETDEWEB)

    Yerin, Yuriy; Omelyanchouk, Alexander [Verkin Inst. for Low Temperature Physics and Engineering. 61103 Kharkiv (Ukraine); Drechsler, Stefan-Ludwig; Brink, Jeroen van den; Efremov, Dmitriy [Inst. for Theorretical Solid State Physics at the Leibniz Inst. for Solid State an Materials Research, IFW-Dresden, D-01171 Dresden (Germany)

    2016-07-01

    Within the Ginzburg-Landau formalism we provide a classification of all possible ground states (GS) of a three-band superconductor (3BSC) where either frustrated states with BTRS or a single non-BTRS GS with unconventional/conventional s-wave symmetry, respectively, exist. The necessary condition for a BTRS GS in general cannot be reduced to a ''-''sign of the product of all interband couplings (IBC) valid in the case of 3 equivalent bands with repulsive equal IBC, only. It corresponds to a maximal IBC frustration. We show that with increasing diversity of the parameter space this frustration is reduced and the regions of possible BTRS GS start to shrink. We track possible evolutions of a BTRS GS of a 3BSC based doubly-connected system in an external magnetic field. Depending on its parameters, a magnetic flux can induce various current density leaps, connected with adiabatic or non-adiabatic transitions from BTRS to non-BTRS states and vice versa. The current induced magnetic flux response of samples with a doubly-connected geometry e.g. as a thin tube provides a suitable experimental tool for the detection of BTRS GS.

  18. Evaluation of magnetic loss in a YBa sub 2 Cu sub 3 O sub x superconductor

    CERN Document Server

    Konishi, H; Futamura, M

    2003-01-01

    We measured the magnetic force between a YBa sub 2 Cu sub 3 O sub x (YBCO) superconductor and a Nd-Fe-B magnet while reciprocating the superconductor under the magnet. The magnetic force showed a hysteretic characteristic against the displacement of the superconductor. Magnetic loss calculated from the hysteresis curve decreased as the drive frequency increased. A mechanical model was used to analyze the characteristics of the magnetic loss. By adding the contribution of viscous force and repined flux lines to the mechanical model, we obtained good agreement between the analytical and experimental results. (author)

  19. Method for fabrication of high temperature superconductors

    Science.gov (United States)

    Balachandran, Uthamalingam [Hinsdale, IL; Ma, Beihai [Naperville, IL; Miller, Dean [Darien, IL

    2009-07-14

    A layered article of manufacture and a method of manufacturing same is disclosed. A substrate has a biaxially textured MgO crystalline layer having the c-axes thereof inclined with respect to the plane of the substrate deposited thereon. A layer of one or more of YSZ or Y.sub.2O.sub.3 and then a layer of CeO.sub.2 is deposited on the MgO. A crystalline superconductor layer with the c-axes thereof normal to the plane of the substrate is deposited on the CeO.sub.2 layer. Deposition of the MgO layer on the substrate is by the inclined substrate deposition method developed at Argonne National Laboratory. Preferably, the MgO has the c-axes thereof inclined with respect to the normal to the substrate in the range of from about 10.degree. to about 40.degree. and YBCO superconductors are used.

  20. Fabrication and characterization of hybrid Nb-YBCO dc SQUIDs

    International Nuclear Information System (INIS)

    Frack, E.K.; Drake, R.E.; Patt, R.; Radparvar, M.

    1991-01-01

    This paper reports on the fabrication of hybrid low T c /high T c dc SQUIDs of two flavors. The first kind utilizes niobium tunnel junctions and a YBCO film strip as the most inductive portion of the SQUID loop. This configuration allows a direct measurement of the inductance of the YBCO microstrip from which the effective penetration depth can be calculated. The successful fabrication of these SQUIDs has required 1. superconducting Nb-to-YBCO contacts, 2. deposition and patterning of an SiO 2 insulation layer over YBCO, and 3. selective patterning of niobium and SiO 2 relative to YBCO. All these process steps are pertinent to the eventual use of YBCO thin films in electronic devices

  1. Development of Bulk Bi2+xSr3-yCa yCu 2O8+delta Superconductors by Partial-Melting Route for Fault Current Limiters Application

    Directory of Open Access Journals (Sweden)

    Bojan A. Marinkovic

    2002-06-01

    Full Text Available The production of bulk Bi2+xSr3-yCa yCu 2O8+delta (Bi-2212 superconductors for fault current limiter application was developed via a partial-melting route. Aiming high Ic (critical current, which is the essential superconducting characteristic for application of this material in the construction of Fault Current Limiters (FCL, the produced blocks have predominance of Bi-2212 phase (83 wt%, which characterizes with high values of zero and onset transport critical temperature of 92K and 97.5K, respectively. A relatively low transition width, deltaT, from the superconducting to the normal state of 5.5K, revealed a good intergrain connectivity. Consequently, current measurements on the blocks of Bi-2212 show promising Ic values of 230A and 850A for direct and alternate current, respectively. It is expected that further increases in the Ic values will depend on the elimination of an observed amorphous phase and further reduction of amount and grain sizes of secondary phases, still present in the blocks obtained by the proposed partial-melting route. This may be achieved by a further optimization of the partial-melting processing parameters.

  2. Microwave absorption in YBCO/PrBCO superlattices

    International Nuclear Information System (INIS)

    Carlos, W.E.; Kaplan, R.; Lowndes, D.H.; Norton, D.P.

    1992-01-01

    In this paper, non-resonant microwave absorption is employed to probe YBCO/PrBCO superlattices and compare the response to that of a YBCO film. Near the transition temperatures, the response of the superlattice samples and the YBCO film have similar amplitudes and orientation dependencies. At lower temperatures, the response of the superlattices is much stronger than that of the YBCO film and, while both responses are hysteretic at low temperatures, the widths of the hysteresis have opposite orientation dependencies, which the authors attribute to the role of the PrBCO layers

  3. Positron annihilation studies in Hf doped YBCO

    International Nuclear Information System (INIS)

    Gopalan, P.; Priya, E.R.; Premila, M.; Sundar, C.S.; Gopinathan, K.P.

    1992-01-01

    The variation of positron lifetime and oxygen stoichiometry as a function of quench temperature has been measured in undoped and 0.5at%, 0.75at%, and 1.0 at% Hf doped YBCO. In both the undoped and Hf doped samples, the lifetime decreases and the oxygen content increases as the quench temperature is lowered from 900degC to 300degC. The lifetime in the tetragonal phase (900degC) decreases with the increase in Hf content, whereas in the orthorhombic phase (450degC) it increases. The difference in lifetime between the tetragonal and orthorhombic phases decreases with the increase in the Hf content. These trends are discussed in terms of the influence of Hf doping on the oxygen content and the positron density distribution in YBCO

  4. Characteristics of a Bulk High-Critical Temperature Superconductor Fabricated by the Shock Compaction Method: Possible Use as a Highly Sensitive Magnetic Sensor

    International Nuclear Information System (INIS)

    Fujita, H; Maeji, Y; Yamagata, K; Itoh, M; Kezuka, H; Kikuchi, M; Atou, T; Kawasaki, M; Fukuoka, K

    2006-01-01

    A magnetic sensor, constructed of bulk Bi-Pb-Sr-Ca-Cu-O (BPSCCO), was fabricated by use of the shock compaction method, employing a propellant gun-system, and then sintered under through use of an electronic furnace. The specimen as a magnetic sensor was maintained in the superconducting state at 77.4 K, under a current density J of approximately 40 A/cm 2 in the absence of an excitation magnetic field B ex . The superconducting state was then broken and the specimen exposed to a B ex value of 40x10 -4 T. That is, the resistance R meas of the specimen occurred when exposed to 40x10 -4 T under a constant J of 40 A/cm 2 . The magnetic sensitivity S of the specimen was approximately 13 %/(10 -4 T) over the range of measurement of the magnetic field B meas from 0 to ±5x10 -4 T, under a constant 40x10 -4 T for the value of B ex , being approximately 13 times greater than that of a giant magnetoresistance (GMR) sensor. It was, consequently, determined that it was possible to apply the bulk BPSCCO specimen as a highly sensitive magnetic sensor

  5. Characteristics of a Bulk High-Critical Temperature Superconductor Fabricated by the Shock Compaction Method: Possible Use as a Highly Sensitive Magnetic Sensor

    Energy Technology Data Exchange (ETDEWEB)

    Fujita, H [Interdisci. Grad. School of Sci. and Engi., Grad. School of Kinki University, Higashi-Osaka, Osaka 577-8502 (Japan); Maeji, Y [Interdisci. Grad. School of Sci. and Engi., Grad. School of Kinki University, Higashi-Osaka, Osaka 577-8502 (Japan); Yamagata, K [Relia. Eval. Technol. Center, Nitto Denko Corp., Onomichi, Hiroshima 722-0212 (Japan); Itoh, M [Interdisci. Grad. School of Sci. and Engi., Grad. School of Kinki University, Higashi-Osaka, Osaka 577-8502 (Japan); Kezuka, H [Faculty of Bionics, Tokyo University of Technol., Hachioji, Tokyo 192-0982 (Japan); Kikuchi, M [Kansen Fukushi Research Center, Tohoku Fukushi University Sendai, Miyagi 989-3201 (Japan); Atou, T [Insti. for Mate. Research, Tohoku University Sendai, Miyagi 980-8577 (Japan); Kawasaki, M [Insti. for Mate. Research, Tohoku University Sendai, Miyagi 980-8577 (Japan); Fukuoka, K [Insti. for Mate. Research, Tohoku University Sendai, Miyagi 980-8577 (Japan)

    2006-06-01

    A magnetic sensor, constructed of bulk Bi-Pb-Sr-Ca-Cu-O (BPSCCO), was fabricated by use of the shock compaction method, employing a propellant gun-system, and then sintered under through use of an electronic furnace. The specimen as a magnetic sensor was maintained in the superconducting state at 77.4 K, under a current density J of approximately 40 A/cm{sup 2} in the absence of an excitation magnetic field B{sub ex}. The superconducting state was then broken and the specimen exposed to a B{sub ex} value of 40x10{sup -4} T. That is, the resistance R{sub meas} of the specimen occurred when exposed to 40x10{sup -4} T under a constant J of 40 A/cm{sup 2}. The magnetic sensitivity S of the specimen was approximately 13 %/(10{sup -4} T) over the range of measurement of the magnetic field B{sub meas} from 0 to {+-}5x10{sup -4} T, under a constant 40x10{sup -4} T for the value of B{sub ex}, being approximately 13 times greater than that of a giant magnetoresistance (GMR) sensor. It was, consequently, determined that it was possible to apply the bulk BPSCCO specimen as a highly sensitive magnetic sensor.

  6. A study for designing YBCO power transformer

    International Nuclear Information System (INIS)

    Hayashi, H.; Okamoto, H.; Harimoto, T.; Imayoshi, T.; Tomioka, A.; Bouno, T.; Konno, M.; Iwakuma, M.

    2007-01-01

    It is highly expected that superconducting transformers, which are characterized by incombustibility, light weight, and compactness, will be used practically for equipment in substations and office buildings sited in urban areas. In recent years, remarkable improvements in the performance of YBaCuO (YBCO) tape wire have been seen. This kind of tape wire has the property that its critical current is large in a highly magnetic field; and, its use is expected to reduce AC loss by applying slit processing on the tape wire, contributing to future cost reductions. In addition, the development of efficient, economical cryogenic units is also expected. The authors have developed a conceptual design for a 66 kV/20 MVA power transformer using YBCO tape wires, or an YBCO power transformer. As a result, we were able to identify the transformer's optimal system structure including coil winding comprised of coils and tape wires; and, we confirmed that the devised transformer can made to be both compact and highly efficient

  7. Briefing on superconductor developments

    International Nuclear Information System (INIS)

    Larbalestier, D.

    1987-01-01

    In this paper, the author covers the technology of the new oxide superconductors and how they might relate to the existing superconductors. He discusses old-fashioned superconductors; the material science of superconductors; the new oxide superconductors; and the future of oxide superconductors. 13 figures, 1 table

  8. Oxide superconductors

    International Nuclear Information System (INIS)

    Cava, R.J.

    2000-01-01

    This article briefly reviews ceramic superconductors from historical and materials perspectives. It describes the factors that distinguish high-temperature cuprate superconductors from most electronic ceramics and places them in the context of other families of superconducting materials. Finally, it describes some of the scientific issues presently being actively pursued in the search for the mechanism for high-temperature superconductivity and the directions of research into new superconducting ceramics in recent years

  9. Remarkable weakness against cleavage stress for YBCO-coated conductors and its effect on the YBCO coil performance

    International Nuclear Information System (INIS)

    Yanagisawa, Y.; Nakagome, H.; Takematsu, T.; Takao, T.; Sato, N.; Takahashi, M.; Maeda, H.

    2011-01-01

    Cleavage strength for YBCO-coated conductor is extremely low, typically 0.5 MPa. The remarkable weakness is due to cracks on the slit edge of the conductor. The cleavage stress appears on YBCO double pancake coils impregnated with epoxy. The cleavage stress should be avoided in the coil winding. Cleavage strength for an YBCO-coated conductor at 77 K was investigated with a model experiment. The nominal cleavage strength for an YBCO-coated conductor is extremely low, typically 0.5 MPa. This low nominal cleavage strength is due to stress concentration on a small part of the YBCO-coated conductor in cleavage fracture. Debonding by the cleavage stress occurs at the interface between the buffer layer and the Hastelloy substrate. The nominal cleavage strength for a slit edge of the conductor is 2.5-times lower than that for the original edge of the conductor; cracks and micro-peel existing over the slit edge reduce the cleavage strength for the slit edge. Cleavage stress and peel stress should be avoided in coil winding, as they easily delaminate the YBCO-coated conductor, resulting in substantial degradation of coil performance. These problems are especially important for epoxy impregnated YBCO-coated conductor coils. It appears that effect of cleavage stress and peel stress are mostly negligible for paraffin impregnated YBCO-coated conductor coils or dry wound YBCO-coated conductor coils.

  10. Iron-YBCO heterostructures and their application for trapped field superconducting motor

    Energy Technology Data Exchange (ETDEWEB)

    Granados, X [Institut de Ciencia de Materials de Barcelona, ICMAB-CSIC, Campus U.A. Barcelona, 08193 Bellaterra (Spain); Bartolome, E [Institut de Ciencia de Materials de Barcelona, ICMAB-CSIC, Campus U.A. Barcelona, 08193 Bellaterra (Spain); Obradors, X [Institut de Ciencia de Materials de Barcelona, ICMAB-CSIC, Campus U.A. Barcelona, 08193 Bellaterra (Spain); Tornes, M [ETSE-UAB, Barcelona (Spain); Rodrigues, L [UNL, Lisbon (Portugal); Gawalek, W [IPHT, Jena (Germany); McCulloch, M [Department Engineering Science, University of Oxford, Oxford (United Kingdom); Hughes, D Dew [Department Engineering Science, University of Oxford, Oxford (United Kingdom); Campbell, A [IRC-UCAM, Cambridge (United Kingdom); Coombs, T [IRC-UCAM, Cambridge (United Kingdom); Ausloos, M [SUPRATEC, Liege (Belgium); Cloots, R [SUPRATEC, Liege (Belgium)

    2006-06-01

    In this work we report on the magnetic behavior of the heterostructures formed by bulk based YBCO rings and ferromagnetic yoke. The magnetization cycle has been performed by an In-Field Hall Mapping technique. A video-like recording of the magnetization process makes it possible to obtain the magnetization of selected areas. The current flowing through the superconducting rings can be deduced from the magnetic field maps. The displacement of the peak of magnetization due to the flux reversal produced by the magnetization of the yoke is also considered. These hybrid heterostructures formed by ferromagnetic and superconducting material have been applied in the construction of the rotor for a brushless AC motor. The design and construction of this machine was carried out within the framework of the TMR Network SUPERMACHINES. The rotor has been designed in a quadrupolar configuration by cutting large YBCO 'window frames' from seeded melt-textured single domain YBCO pellets. This rotor has been coupled to a conventional stator of copper coils wound on an iron armature. The stator can be excited both in bipolar or quadrupolar mode. We report on the behaviour of the motor after a field cooling process when excited in quadrupolar mode.

  11. Iron-YBCO heterostructures and their application for trapped field superconducting motor

    International Nuclear Information System (INIS)

    Granados, X; Bartolome, E; Obradors, X; Tornes, M; Rodrigues, L; Gawalek, W; McCulloch, M; Hughes, D Dew; Campbell, A; Coombs, T; Ausloos, M; Cloots, R

    2006-01-01

    In this work we report on the magnetic behavior of the heterostructures formed by bulk based YBCO rings and ferromagnetic yoke. The magnetization cycle has been performed by an In-Field Hall Mapping technique. A video-like recording of the magnetization process makes it possible to obtain the magnetization of selected areas. The current flowing through the superconducting rings can be deduced from the magnetic field maps. The displacement of the peak of magnetization due to the flux reversal produced by the magnetization of the yoke is also considered. These hybrid heterostructures formed by ferromagnetic and superconducting material have been applied in the construction of the rotor for a brushless AC motor. The design and construction of this machine was carried out within the framework of the TMR Network SUPERMACHINES. The rotor has been designed in a quadrupolar configuration by cutting large YBCO 'window frames' from seeded melt-textured single domain YBCO pellets. This rotor has been coupled to a conventional stator of copper coils wound on an iron armature. The stator can be excited both in bipolar or quadrupolar mode. We report on the behaviour of the motor after a field cooling process when excited in quadrupolar mode

  12. Chemical characterization of melt-textured YBCO produced by hybrid powder metallurgy

    International Nuclear Information System (INIS)

    To, P.-C.; Meen, James K.

    2008-01-01

    Monolithic YBCO samples were made by traditional top-seeded melt-texturing processes from cold-milled mixtures of Y123 (YBa 2 Cu 3 O 7-δ ) and elemental Y. The bulk composition does not lie on the Y211 (Y 2 BaCuO 5 )-Y123 join so, formation of Y123 from liquid and Y211 is not an essentially isothermal process on cooling. The reaction liquid + Y211 = Y123 is a ternary reaction and occurs over several tens of degrees. The Y123 thus produced has a range in compositions - particularly in Cu:(Y + Ba) - which may reflect crystallization over the thermal interval. The liquid migrates to an invariant point at which CuO also crystallizes with complete loss of liquid. The presence of trains of CuO grains in the YBCO indicates the locations of the last liquids to be preserved in the sample. These trains are dominantly in an annulus 1-3 mm from the edge of the 20-mm diameter sample. Mapping the compositional variation in Y123 may allow mapping the path of crystallization of these monolithic YBCO samples

  13. Chemical characterization of melt-textured YBCO produced by hybrid powder metallurgy

    Energy Technology Data Exchange (ETDEWEB)

    To, P.-C. [Texas Center for Superconductivity and Department of Chemistry, University of Houston, 4800 Calhoun Street, Houston, TX 77035 (United States); Meen, James K. [Texas Center for Superconductivity and Department of Chemistry, University of Houston, 4800 Calhoun Street, Houston, TX 77035 (United States)], E-mail: jmeen@uh.edu

    2008-06-15

    Monolithic YBCO samples were made by traditional top-seeded melt-texturing processes from cold-milled mixtures of Y123 (YBa{sub 2}Cu{sub 3}O{sub 7-{delta}}) and elemental Y. The bulk composition does not lie on the Y211 (Y{sub 2}BaCuO{sub 5})-Y123 join so, formation of Y123 from liquid and Y211 is not an essentially isothermal process on cooling. The reaction liquid + Y211 = Y123 is a ternary reaction and occurs over several tens of degrees. The Y123 thus produced has a range in compositions - particularly in Cu:(Y + Ba) - which may reflect crystallization over the thermal interval. The liquid migrates to an invariant point at which CuO also crystallizes with complete loss of liquid. The presence of trains of CuO grains in the YBCO indicates the locations of the last liquids to be preserved in the sample. These trains are dominantly in an annulus 1-3 mm from the edge of the 20-mm diameter sample. Mapping the compositional variation in Y123 may allow mapping the path of crystallization of these monolithic YBCO samples.

  14. What can Andreev bound states tell us about superconductors?

    Science.gov (United States)

    Millo, Oded; Koren, Gad

    2018-08-06

    Zero-energy Andreev bound states, which manifest themselves in the tunnelling spectra as zero-bias conductance peaks (ZBCPs), are abundant at interfaces between superconductors and other materials and on the nodal surface of high-temperature superconductors. In this review, we focus on the information such excitations can provide on the properties of superconductor systems. First, a general introduction to the physics of Andreev bound states in superconductor/normal metal interfaces is given with a particular emphasis on why they appear at zero energy in d -wave superconductors. Then, specific spectroscopic tunnelling studies of thin films, bilayers and junctions are described, focusing on the corresponding ZBCP features. Scanning tunnelling spectroscopy (STS) studies show that the ZBCPs on the c -axis YBa 2 Cu 3 O 7- δ (YBCO) films are correlated with the surface morphology and appear only in proximity to (110) facets. STS on c -axis La 1.88 Sr 0.12 CuO 4 (LSCO) films exhibiting the 1/8 anomaly shows spatially modulated peaks near zero bias associated with the anti-phase ordering of the d -wave order parameter predicted at this doping level. ZBCPs were also found in micrometre-size edge junctions of YBCO/SrRuO 3 /YBCO, where SrRuO 3 is ferromagnetic. Here, the results are consistent with a crossed Andreev reflection effect (CARE) at the narrow domain walls of the SrRuO 3 ZBCPs measured in STS studies of manganite/cuprate bilayers could not be attributed to CARE because the manganite's domain wall is much larger than the coherence length in YBCO, and instead are attributed to proximity-induced triplet-pairing superconductivity with non-conventional symmetry. And finally, ZBCPs found in junctions of non-intentionally doped topological insulator films of Bi 2 Se 3 and the s -wave superconductor NbN are attributed to proximity-induced p x  + ip y triplet order parameter in the topological material.This article is part of the theme issue 'Andreev bound states'.

  15. Influence of pH during modified sol-gel process to synthesized pure phased YBCO

    International Nuclear Information System (INIS)

    Barekat Rezaee, S.; Daadmehr, V.; Saeb, F.; Falahati, S.

    2007-01-01

    Full text: Among numerous studies of high-Tc superconductor compound, the YBCO system is the most studied system. During 3 last decades synthesized of high quality pure homogeneous powder were done. One of these methods was modified citrate gel that was widely used to obtain nanosized single phase YBCO. One of the most important factors to yield pure product is adjustment of the pH during the gelation. Then in this work, we adjusted different pH for gelatin and compare phase purity and elemental composition by using XRD and EDS. To synthesize the YBCO, we used Nitrate of metal (Y, Ba, Cu) as precursor. stoichiometric (1:2:3) amount of metal nitrate were solved in distilled water and mixed with constant stirring, (for each equivalent gram of metal nitrate add one equivalent gram of citric acid) and stirred up to have unclear light blue solution and the ethylendiamine was added drop wise to adjust pH from 4.56 to 7.45. Then the solution was heated up 80 C to achieve viscous gel. The color changed from dark blue to purple according to pH. The gel was heated on furnace up to 520 C and kept for 2 hours. During heating the gel swell and filled the baker then special attention is needed to use over sized baker. Obtained powder was calcined for 22h at 900 C to yield homogeneous pure phase and then pellets with 1 sm diameter in 10 ton pressure were produced and sintered for 19 h at 930 C and annealed to room temperature in oxygen. Resistivity measurement using standard four probe technique exhibit Tc (zero) from 90 K to 94 K. The samples were discussed by XRD, SEM and EDS. (authors)

  16. Preparation of PZT thin films on YBCO electrodes by KrF excimer laser ablation technique

    International Nuclear Information System (INIS)

    Kurogi, H.; Yamagata, Y.; Ebihara, K.

    1998-01-01

    Pb(Zr X Ti 1-X )O 3 (PZT) films have excellent ferroelectric, optical, piezoelectric, and pyroelectric properties. We prepared PZT thin films by the excimer laser ablation technique. A pulsed KrF excimer laser (Lambda Physik LPX305icc, pulse duration of 25 ns, λ=248 nm, 850 mJ Max.) was used to ablate the bulk targets. We investigated the influence of bottom electrode materials on the characteristics of the PZT thin films prepared on Pt and YBCO underlayers. The X-ray diffraction (XRD) patterns showed that the PZT films prepared with a laser fluence of 2 Jcm -2 on YBCO/MgO(100) substrate at a wide temperature range of 550-680 C have a perovskite (001) structure. At the same laser fluence, the PZT films prepared on Pt/MgO(100) substrate have a perovskite (001) structure only at 650 C. The polarization-electric field (P-E) characteristics and fatigue properties of PZT thin films were measured by the Sawyer-Tower circuit. The remnant polarization and coercive field have been found to be P r =15 μC cm -2 , 30 μC cm -2 and E c =200 kV cm -1 , 100 kV cm -1 for Au/PZT/Pt/MgO and Au/PZT/YBCO/MgO correspondingly. The remnant polarization of Au/PZT/YBCO/MgO thin film was reduced to one-half after about 10 8 cycles of switching. (orig.)

  17. Preparation of PZT thin films on YBCO electrodes by KrF excimer laser ablation technique

    Energy Technology Data Exchange (ETDEWEB)

    Kurogi, H; Yamagata, Y; Ebihara, K [Kumamoto Univ. (Japan). Dept. of Electr. Eng. and Comput. Sci.; Inoue, N [Kyushu Electric Power Co., Inc., Suizenji, 1-6-36, Kumamoto 862 (Japan)

    1998-03-01

    Pb(Zr{sub X}Ti{sub 1-X})O{sub 3} (PZT) films have excellent ferroelectric, optical, piezoelectric, and pyroelectric properties. We prepared PZT thin films by the excimer laser ablation technique. A pulsed KrF excimer laser (Lambda Physik LPX305icc, pulse duration of 25 ns, {lambda}=248 nm, 850 mJ Max.) was used to ablate the bulk targets. We investigated the influence of bottom electrode materials on the characteristics of the PZT thin films prepared on Pt and YBCO underlayers. The X-ray diffraction (XRD) patterns showed that the PZT films prepared with a laser fluence of 2 Jcm{sup -2} on YBCO/MgO(100) substrate at a wide temperature range of 550-680 C have a perovskite (001) structure. At the same laser fluence, the PZT films prepared on Pt/MgO(100) substrate have a perovskite (001) structure only at 650 C. The polarization-electric field (P-E) characteristics and fatigue properties of PZT thin films were measured by the Sawyer-Tower circuit. The remnant polarization and coercive field have been found to be P{sub r}=15 {mu}C cm{sup -2}, 30 {mu}C cm{sup -2} and E{sub c}=200 kV cm{sup -1}, 100 kV cm{sup -1} for Au/PZT/Pt/MgO and Au/PZT/YBCO/MgO correspondingly. The remnant polarization of Au/PZT/YBCO/MgO thin film was reduced to one-half after about 10{sup 8} cycles of switching. (orig.) 7 refs.

  18. Advanced technologies related to a high temperature superconductor for small laboratory experiments

    International Nuclear Information System (INIS)

    Ogawa, Yuichi; Mito, Toshiyuki; Yanagi, Nagato

    2006-01-01

    Advanced technologies related to a high temperature superconductor materials and small refrigerator are reviewed. Mini-RT/RT-1 is designed and constructed as a plasma examination device. The element technology of low temperature apparatus, the results of performance tests and application examples are explained. The superconductors such as Bi 2 Sr 2 CaCu 2 O 8 (Bi-2212) for the low temperature phase, Bi 2 Sr 2 Ca 2 Cu 3 O 10 (Bi-2223) for the high temperature phase, and YBa 2 Cu 3 O y (YBCO or Y123) are described. Advanced 4K-Giford-Mcmahon (GM) refrigerator on the market put superconductor coil made of low temperature superconductor metals to practical use and extends its application field. Small laboratory is able to experiment on the high temperature superconductor materials. (S.Y.)

  19. Pinning potentials of the vortex lattice in YBCO crystals in the peak effect region

    International Nuclear Information System (INIS)

    Pasquini, G.; Bekeris, V.

    2004-01-01

    Memory effects in the dynamic response of the vortex lattice (VL) in type II superconductors and its relationship with the controversial peak effect, have attracted great interest for a long time. In the last years, these features have been observed in YBCO single crystals, with the DC magnetic field tilted away from the twin planes and were related with robust dynamical states characterized by different degrees of mobility. Recently, we reported that the previous dynamical history of the VL can modify not only its dynamic response, but can even modify its static properties as well. In the present work, we try to understand the nature of the peak effect in YBCO crystals by sensing the effective AC penetration depth in the linear Campbell regime. We report history dependent effective pinning potential well curvatures and study the stability of the different static configurations. Interestingly, we observe that the more pinned VL configuration is not the more stable. Results agree with a dynamic scenario undergoing the Peak Effect

  20. Second Generation HTs Wire Based on RABiTS Substrates and MOD YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Schoop, U. [American Superconductor Corporation, Westborough, MA; Rupich, Marty [American Superconductor Corporation, Westborough, MA; Thieme, C. L. H. [American Superconductor Corporation, Westborough, MA; Verebelyi, D. T. [American Superconductor Corporation, Westborough, MA; Zhang, W. [American Superconductor Corporation, Westborough, MA; Li, Xiaoping [American Superconductor Corporation, Westborough, MA; Kodenkandath, Thomas [American Superconductor Corporation, Westborough, MA; Nguyen, N. [American Superconductor Corporation, Westborough, MA; Siegal, E. E. [American Superconductor Corporation, Westborough, MA; Civale, L. [Los Alamos National Laboratory (LANL); Holesinger, T. G. [Los Alamos National Laboratory (LANL); Maiorov, B. [Los Alamos National Laboratory (LANL); Goyal, Amit [ORNL; Paranthaman, Mariappan Parans [ORNL

    2005-01-01

    The performance of Second Generation (2G) high temperature superconducting wire manufactured by continuous reel-to-reel processes is nearing the 300 A/cm-width (77 K, self field) performance threshold for commercial power cable applications. The 2G manufacturing approach under development at American Superconductor is based on the combination of the RABiTS substrate-buffer technology with metal organic deposition (MOD) of the YBCO layer. The capability of this process has been demonstrated in multiple 10 meter lengths with critical currents exceeding 250 A/cm-width with high uniformity and reproducibility. Critical currents of 380 A/cm-width have been achieved in short length samples prepared by the same basic process. The incorporation of nanoparticles ('nanodots') into the YBCO layer using the MOD process has resulted in a 2-fold improvement in the critical current at 65 K in a 3 T field. The research and development focus at ASMC is now directed toward the economical scale-up of the RABiTS/MOD process, optimization of the conductor properties for targeted applications and the use of 2G wire in initial demonstration applications.

  1. Estimation of magnetic relaxation property for CVD processed YBCO-coated conductors

    International Nuclear Information System (INIS)

    Takahashi, Y.; Kiuchi, M.; Otabe, E.S.; Matsushita, T.; Shikimachi, K.; Watanabe, T.; Kashima, N.; Nagaya, S.

    2010-01-01

    Ion Beam Assist Deposition/Chemical Vapor Deposition(IBAD/CVD)-processed YBCO-coated conductors with high critical current density J c at high magnetic fields are expected to be applied to superconducting equipments such as superconducting magnetic energy storage (SMES). For application to superconducting magnet in SMES one of the most important properties for superconductors is the relaxation property of superconducting current. In this paper, the relaxation property is investigated for IBAD/CVD-processed YBCO-coated conductors of the superconducting layer in the range of 0.18-0.90 μm. This property can be quantitatively characterized by the apparent pinning potential, U 0 *. It is found that U 0 * takes a smaller value due to the two-dimensional pinning mechanism at high magnetic fields for conductor with thinner superconducting layer. Although U 0 * decreases with increasing thickness at low magnetic fields at 20 K, it increases at high magnetic fields. The results are theoretically explained by the model of the flux creep and flow based on the dimensionality of flux pinning. Scaling analysis is examined for the dependence of U 0 * on the magnetic field, temperature and the layer thickness.

  2. Inkjet printing of multifilamentary YBCO for low AC loss coated conductors

    International Nuclear Information System (INIS)

    Hopkins, S C; Joseph, D; Mitchell-Williams, T B; Glowacki, B A; Calleja, A; Vlad, V R; Vilardell, M; Ricart, S; Granados, X; Puig, T; Obradors, X; Usoskin, A; Falter, M; Bäcker, M

    2014-01-01

    Considerable progress has been made with the development of REBCO coated conductors in recent years, and high performance conductors are available commercially. For many applications, however, the cost remains prohibitive, and AC losses discourage their selection for higher frequency applications. Chemical solution deposition (CSD) methods are attractive for low-cost, scalable preparation of buffer and superconductor layers, and in many respects inkjet printing is the method of choice, permitting non-contact deposition with minimal materials wastage and excellent control of coating thickness. Highly textured coatings of YBCO and Gd-doped CeO 2 have previously been reported on buffered metal substrates. Inkjet printing also introduces the possibility of patterning - directly depositing two and three dimensional structures without subtractive processing - offering a low-cost route to coated conductors with reduced AC losses. In this contribution, the inkjet deposition of superconducting YBCO tracks is reported on industrially relevant buffered metal substrates both by direct printing and an inverse patterning approach. In the latter approach, ceria tracks were printed reported, which are a candidate both for resistive filament spacers and buffer layers. TFA-based precursor solutions have been printed on SS/ABAD-YSZ/CeO 2 and Ni-W/LZO/CeO 2 RABiTS substrates, and the resulting multifilamentary samples characterised by microscopy and scanning Hall probe measurements. The prospects for future inkjet-printed low AC loss coated conductors are discussed, including control of interfilamentary resistivity and bridging, transposed filamentary structures and stabilisation material.

  3. Formation and physical properties of YBCO thick films grown by using the electrophoretic deposition method

    CERN Document Server

    Kim, U J; Kim, Y C; Han, S K; Kang, K Y

    1999-01-01

    Thick films of the YBa sub 2 Cu sub 3 O subgamma sub - subdelta (YBCO) superconductor were prepared by using the electrophoretic deposition technique and a flexible wire as the substrate. The transition temperature of the wires was 91 K, the intragranular magnetic critical current density J sub c sub g sup m sup a sup g was about 10 sup 5 A/cm sup 2 at 77 K in a weak field, and the transport J sub c sup t sup r sup a sup n sup s was about 365 A/cm sup 2 at 77 K. We calculated the intergranular magnetic critical current J sub c sub J sup m sup a sup g and the activation energy from the AC-susceptibility measurements, and their values were about 444 A/cm sup 2 at 77 K and 2.02 eV, respectively.

  4. Flux pinning in MOD YBCO films by chemical doping

    International Nuclear Information System (INIS)

    Zhou, Y X; Ghalsasi, S; Rusakova, I; Salama, K

    2007-01-01

    A novel nanomaterial synthesis technique has been developed to introduce 0D (particles), 1D (columnar defects) and 3D (domains) nanoscale pinning centres in MOD Y 1 Ba 2 Cu 3 O 7 (YBCO) coated conductors. We have succeeded in introducing nanoscale Y enriched particles, nanoscale 90 0 rotated Y 1/3 Sm 2/3 Ba 2 Cu 3 O 7 domains and nanoscale Zr enriched columnar defects into YBCO layers by different chemical doping. The pinning force density in Y 2 O 3 -doped YBCO film is found to be larger than that of pure YBCO film at all fields. Also it was found that YBCO films with Sm substituting for Y have yielded improved critical current density characteristics over a wide range of magnetic fields. Maximum pinning force densities exceeding 7 and 8 GN m -3 are obtained in 5% BZO-doped and Sm substituted YBCO films, respectively. Additionally, TEM studies revealed nanoscale Zr enriched columnar defects distributing in the matrix of the c-oriented YBCO film throughout the whole cross section. This indicates that chemical doping is a promising fabrication technique to create specific pinning landscapes in YBCO coated conductors

  5. Conceptual design of a forced-flow-cooled 20-kA current lead using Ag-alloy-sheathed Bi-2223 high-temperature superconductors

    International Nuclear Information System (INIS)

    Heller, R.

    1994-11-01

    The use of high-temperature superconductors in current leads to reduce refrigeration power has been investigated by many groups in the past. Most used YBCO and Bi-2212 bulk superconductors, although their critical current density is not very high. In this paper, BI-2223 HTSC tapes sheathed with Ag alloys are used in the design of a 20-kA current lead because of their higher critical current in medium magnetic fields. The lead current of 20 kA is related to the coil current of the planned stellarator WENDELSTEIN 7-X. Forced-now helium cooling has been used in the design, allowing position-independent and well-controlled operation. The design characteristics of the lead are presented and 4-K helium cooling of the whole lead, as well as 60-K helium cooling of the copper part of the lead, is discussed. The power consumption at zero current, and the lead's behaviour in case of loss of coolant flow, are given, The results of the design allow extrapolation to current leads of the 50-kA range

  6. Comparative study on the critical current performance of Bi-2223/Ag and YBCO wires in low magnetic fields at liquid nitrogen temperature

    International Nuclear Information System (INIS)

    Feng, F.; Qu, T.-M.; Gu, C.; Xin, Y.; Gong, W.-Z.; Wu, W.; Han, Z.

    2011-01-01

    Highlights: → The I c values of Bi-2223/Ag and YBCO wires in low fields at 77 K were compared. → The performance of Bi-2223/Ag in low parallel fields was better than that of YBCO. → The phenomenon mentioned above can be verified by the published literature datum. → A new aspect was brought to understand the transport properties of HTS wires. - Abstract: A comparative study on the critical current performance of Bi-2223/Ag and YBCO coated conductor wires in low magnetic fields at liquid nitrogen temperature was carried out in this work. Five commercial high temperature superconductor wires from different manufacturers were collected. Their critical currents were measured in magnetic fields, ranging from 0 to 0.4 T. On contrary to the common conception, the Bi-2223/Ag samples had better performance than YBCO coated conductor samples in the magnetic fields parallel to the wide surface of superconducting wires within the experimental scope. We also found similar results by collecting the concerned datum from the published literatures to confirm our measurement results. At the present stage, this fact made that the Bi-2223/Ag wires might be the preferred choice for the applications with mainly low parallel fields involved, unless other considerations were prioritized.

  7. Electron beam induced oxygen in YBa2Cu3O7-x superconductors

    International Nuclear Information System (INIS)

    Basu, S.N.; Roy, T.; Mitchell, T.E.; Nastasi, M.

    1989-01-01

    Thin foils of bulk YBa 2 Cu 3 O 7-x (YBCO) superconductors were subjected to electron irradiation in a Transmission Electron Microscope (TEM). The resulting disordering of the oxygen atoms and vacancies in the Cu-O planes was monitored by measuring the splitting of the (110) diffraction spots in the [001] diffraction pattern. Samples were irradiated at 83K with 100, 150, 200 and 300kV electrons. The 100kV electrons did not cause any disordering, even after prolonged irradiation. The results of the higher energy irradiations showed an excellent fit to a disordering model, indicating a lack of radiation assisted ordering at 83K. This was further confirmed by the insensitivity of the disordering to the dose rate of 300kV electrons at 83K. However, at 300K, an increase in the dose rate of 300kV electrons increased the disordering rate, indicating that radiation assisted reordering was occurring at that temperature. 7 refs., 4 figs

  8. Electron beam induced oxygen disordering in YBa2Cu3O7-x superconductors

    International Nuclear Information System (INIS)

    Basu, S.N.; Roy, T.; Mitchell, T.E.; Nastasi, M.

    1990-01-01

    Thin foils of bulk YBa 2 Cu 3 O 7-x (YBCO) superconductors were subjected to electron irradiation in a transmission electron microscope (TEM). The resulting disordering of the oxygen atoms and vacancies in the Cu-O planes was monitored by measuring the splitting of the (110) diffraction spots in the [001] diffraction pattern. Samples were irradiated at 83 K with 100, 150, 200 and 300 kV electrons. The 100 kV electrons did not cause any disordering, even after prolonged irradiation. The results of the higher energy irradiations showed an excellent fit to a disordering model, indicating a lack of radiation assisted reordering at 83 K. This was further confirmed by the insensitivity of the disordering to the dose rate of 300 kV electrons at 83 K. However, at 300 K, an increase in the dose rate of 300 kV electrons increased the disordering rate, indicating that radiation assisted reordering was occurring at that temperature

  9. Ceramic superconductors II

    International Nuclear Information System (INIS)

    Yan, M.F.

    1988-01-01

    This volume compiles papers on ceramic superconductors. Topics include: structural patterns in High-Tc superconductors, phase equilibria of barium oxide superconductors, localized electrons in tetragonal YBa/sub 2/Cu/sub 3/O/sub 7-δ/, lattice and defect structure and properties of rare earth/alkaline earth-copper-oxide superconductors, alternate candidates for High-Tc superconductors, perovskite-structure superconductors; superconductive thin film fabrication, and superconductor/polymer composites

  10. Topological surface states in nodal superconductors

    International Nuclear Information System (INIS)

    Schnyder, Andreas P; Brydon, Philip M R

    2015-01-01

    Topological superconductors have become a subject of intense research due to their potential use for technical applications in device fabrication and quantum information. Besides fully gapped superconductors, unconventional superconductors with point or line nodes in their order parameter can also exhibit nontrivial topological characteristics. This article reviews recent progress in the theoretical understanding of nodal topological superconductors, with a focus on Weyl and noncentrosymmetric superconductors and their protected surface states. Using selected examples, we review the bulk topological properties of these systems, study different types of topological surface states, and examine their unusual properties. Furthermore, we survey some candidate materials for topological superconductivity and discuss different experimental signatures of topological surface states. (topical review)

  11. Shot noise in YBCO bicrystal Josephson junctions

    DEFF Research Database (Denmark)

    Constantinian, K.Y.; Ovsyannikov, G.A.; Borisenko, I.V.

    2003-01-01

    We measured spectral noise density in YBCO symmetric bicrystal Josephson junctions on sapphire substrates at bias voltages up to 100 mV and T 4.2 K. Normal state resistance of the Josephson junctions, R-N = 20-90 Omega and ICRN up to 2.2 mV have been observed in the experimental samples. Noise...... may explain the experimentally measured linewidth broadening of Josephson oscillations at mm and submm wave frequencies in high-Tc superconducting junctions. Experimental results are discussed in terms of bound states existing at surfaces of d-wave superconducting electrodes....

  12. Current transfer between superconductor and normal layer in coated conductors

    International Nuclear Information System (INIS)

    Takacs, S

    2007-01-01

    The current transfer between superconducting stripes coated with normal layer is examined in detail. It is shown that, in present YBCO coated conductors with striations, a considerable amount of the current flowing in the normal layer is not transferred into the superconducting stripes. This effect also influences the eddy currents and the coupling currents between the stripes. The effective resistance for the coupling currents is calculated. The maximum allowable twist length of such a striated structure is given, which ensures lower losses than in the corresponding normal conductor of the same volume as the total YBCO cable (including substrate, buffer layer, superconductor and normal coating). In addition, a new simple method for determining the transfer resistance between superconducting and normal parts is proposed

  13. Making superconductors

    International Nuclear Information System (INIS)

    McDonald, W.K.

    1981-01-01

    A method is described of producing composite rod or wire of increased strength and fineness wherein the composite is formed by reducing a lamina of two metals which have been rolled to form a cylindrical billet in which one of the metals is in expanded form. The composite produced can be encased in copper and fabricated to produce a superconductor. Alloys contemplated for producing superconductors are Nb 3 Sn, Nb 3 Ga, Nb 3 Ge, Nb 3 Si, Nb-Ti, V 3 Ga, V 3 Si, V 3 Sn, V 3 Al, and V 3 Ge laminated on bronze, Al, Cu, Ta, or combinations thereof. (author)

  14. Growth techniques for monolithic YBCO solenoidal magnets

    International Nuclear Information System (INIS)

    Scruggs, S.J.; Putman, P.T.; Fang, H.; Alessandrini, M.; Salama, K.

    2006-01-01

    The possibility of growing large single domain YBCO solenoids by the use of a large seed has been investigated. There are two known methods for producing a similar solenoid. This first is a conventional top seeded melt growth process followed by a post processing machining step to create the bore. The second involves using multiple seeds spaced around the magnet bore. The appeal of the new technique lies in decreasing processing time compared to the single seed technique, while avoiding alignment problems found in the multiple seeding technique. By avoiding these problems, larger diameter monoliths can be produced. Large diameter monoliths are beneficial because the maximum magnetic field produced by a trapped field magnet is proportional to the radius of the sample. Furthermore, the availability of trapped field magnets with large diameter could enable their use in applications that traditionally have been considered to require wound electromagnets, such as beam bending magnets for particle accelerators or electric propulsion. A comparison of YBCO solenoids grown by the use of a large seed and grown by the use of two small seeds simulating multiple seeding is made. Trapped field measurements as well as microstructure evaluation were used in characterization of each solenoid. Results indicate that high quality growth occurs only in the vicinity of the seeds for the multiple seeded sample, while the sample with the large seeded exhibited high quality growth throughout the entire sample

  15. Growth techniques for monolithic YBCO solenoidal magnets

    Energy Technology Data Exchange (ETDEWEB)

    Scruggs, S.J. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States)]. E-mail: Sscruggs2@uh.edu; Putman, P.T. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Fang, H. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Alessandrini, M. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Salama, K. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States)

    2006-10-01

    The possibility of growing large single domain YBCO solenoids by the use of a large seed has been investigated. There are two known methods for producing a similar solenoid. This first is a conventional top seeded melt growth process followed by a post processing machining step to create the bore. The second involves using multiple seeds spaced around the magnet bore. The appeal of the new technique lies in decreasing processing time compared to the single seed technique, while avoiding alignment problems found in the multiple seeding technique. By avoiding these problems, larger diameter monoliths can be produced. Large diameter monoliths are beneficial because the maximum magnetic field produced by a trapped field magnet is proportional to the radius of the sample. Furthermore, the availability of trapped field magnets with large diameter could enable their use in applications that traditionally have been considered to require wound electromagnets, such as beam bending magnets for particle accelerators or electric propulsion. A comparison of YBCO solenoids grown by the use of a large seed and grown by the use of two small seeds simulating multiple seeding is made. Trapped field measurements as well as microstructure evaluation were used in characterization of each solenoid. Results indicate that high quality growth occurs only in the vicinity of the seeds for the multiple seeded sample, while the sample with the large seeded exhibited high quality growth throughout the entire sample.

  16. Inhomogeneous superconductors

    International Nuclear Information System (INIS)

    Tinkham, M.

    1978-01-01

    The coherence length xi and penetration depth lambda set the characteristic length scales in superconductors, typically 100 to 5,000 A. A lattice of flux lines, each carrying a single quantum, can penetrate type II superconductors, i.e., those for which kappa identical with lambda/xi > 1/√2. Inhomogeneities on the scale of the flux lattice spacing are required to pin the lattice to prevent dissipative flux motion. Recent work using voids as pinning centers has demonstrated this principle, but practical materials rely on cold-work, inclusions of second phases, etc., to provide the inhomogeneity. For stability against thermal fluctuations, the superconductor should have the form of many filaments of diameter 10 to 100 μm imbedded in a highly conductive normal metal matrix. Such wire is made by drawing down billets of copper containing rods of the superconductor. An alternative approach is the metallurgical one of Tsuei, which leads to thousands of superconducting filamentary segments in a copper matrix. The superconducting proximity effect causes the whole material to superconduct at low current densities. At high current densities, the range of the proximity effect is reduced so that the effective superconducting volume fraction falls below the percolation threshold, and a finite resistance arises from the copper matrix. But, because of the extremely elongated filaments, this resistance is orders of magnitude lower than that of the normal wire, and low enough to permit the possibility of technical applications

  17. Simulation of ion-beam induced defects in cuprate superconductors

    International Nuclear Information System (INIS)

    Dineva, M.; Marksteiner, M.; Lang, W.

    2005-01-01

    Full text: Heavy-ion irradiation of cuprate superconductors is well known to produce columnar defect tracks along which magnetic vortices can be pinned. Hence, this effect has a large potential for practical applications and can enhance the critical current of the high-temperature superconducting materials. On the other hand, little work has been devoted to light-ion irradiation of the new superconductors. Our previous experimental results have indicated a systematic change of electric transport properties when irradiating YBa 2 Cu 3 O 7 (YBCO) with 75 KEXV He + ions. The purpose of the present study is the investigation of the ion-target interactions with computer simulation programs based on the binary collision approximation. The program package SRIM (Stopping and Range of Ions in Matter) is widely used to simulate the impact of energetic ions (10 eV to 2 GeV) on a solid target using a quantum mechanical treatment of ion-atom collisions under the assumption of an unstructured target material. A similar program, MARLOWE, includes the exact crystalline structure of the target and, thus, is able to calculate ion channeling effects and angle dependences. Detailed results of the penetration range of ions into YBCO, scattering cascades, creation of vacancies and interstitials, are reported for various kinds of ions. One of the central results is that light ions with energy of about 80 KEXV can penetrate through thin films of the cuprate superconductors and create point defects, mainly by oxygen displacement. (author)

  18. Magnetic properties of high temperature superconductors and their interaction with high energy permanent magnets

    International Nuclear Information System (INIS)

    Agarwala, A.K.

    1990-01-01

    Magnetic properties of sintered samples of YBCO ceramic superconductors at various temperatures were measured using a vibrating sample magnetometer (VSM). Also, measurements of forces experienced by a well characterized rare earth-transition metal (RE-TM) permanent magnet (PM) interacting with the superconducting YBCO sample cooled in liquid nitrogen, were performed. Based upon the observed hysteretic magnetization properties of these high temperature superconductors (HTS), the HTS-PM interaction force at liquid nitrogen temperature was calculated from first principle, and finally correlated to the force measurement results. With this analysis, magnetic forces between the same HTS and PM system including the levitation as well as suspension effects at liquid-helium temperature are predicted

  19. Development of superconductor application technology

    Energy Technology Data Exchange (ETDEWEB)

    Hong, G W; Kim, C J; Lee, H G; Lee, H J; Kim, K B; Won, D Y; Jang, K I; Kwon, S C; Kim, W J; Ji, Y A; Yang, S W; Kim, W K; Park, S D; Lee, M H; Lee, D M; Park, H W; Yu, J K; Lee, I S; Kim, J J; Choi, H S; Chu, Y; Kim, Y S; Kim, D H

    1997-09-01

    Fabrication of high Tc bulk superconductor and its application, fabrication of superconducting wire for electric power device and analysis for cryogenic system were carried out for developing superconductor application technologies for electric power system. High quality YBaCuO bulk superconductor was fabricated by controlling initial powder preparation process and prototype flywheel energy storage device was designed basically. The superconducting levitation force measuring device was made to examine the property of prepared superconductor specimen. Systematic studies onthe method of starting powder preparation, mechanical fabrication process, heat treatment condition and analysis of plastic deformation were carried out to increase the stability and reproducibility of superconducting wire. A starting power with good reactivity and fine particle size was obtained by mechanical grinding, control of phase assemblage, and emulsion drying method. Ag/BSCCO tape with good cross sectional shape and Jc of 20,000 A/cm{sup 2} was fabricated by applying CIP packing procedure. Multifilamentary wire with Jc of 10,000 A/cm{sup 2} was fabricated by rolling method using square billet as starting shape. The joining of the multifilamentary wire was done by etching and pressing process and showed 50% of joining efficiency. Analysis on the heat loss in cryostat for high Tc superconducting device was carried out for optimum design of the future cryogenic system. (author). 66 refs., 104 figs.

  20. Development of superconductor application technology

    International Nuclear Information System (INIS)

    Hong, G. W.; Kim, C. J.; Lee, H. G.; Lee, H. J.; Kim, K. B.; Won, D. Y.; Jang, K. I.; Kwon, S. C.; Kim, W. J.; Ji, Y. A.; Yang, S. W.; Kim, W. K.; Park, S. D.; Lee, M. H.; Lee, D. M.; Park, H. W.; Yu, J. K.; Lee, I. S.; Kim, J. J.; Choi, H. S.; Chu, Y.; Kim, Y. S.; Kim, D. H.

    1997-09-01

    Fabrication of high Tc bulk superconductor and its application, fabrication of superconducting wire for electric power device and analysis for cryogenic system were carried out for developing superconductor application technologies for electric power system. High quality YBaCuO bulk superconductor was fabricated by controlling initial powder preparation process and prototype flywheel energy storage device was designed basically. The superconducting levitation force measuring device was made to examine the property of prepared superconductor specimen. Systematic studies onthe method of starting powder preparation, mechanical fabrication process, heat treatment condition and analysis of plastic deformation were carried out to increase the stability and reproducibility of superconducting wire. A starting power with good reactivity and fine particle size was obtained by mechanical grinding, control of phase assemblage, and emulsion drying method. Ag/BSCCO tape with good cross sectional shape and Jc of 20,000 A/cm 2 was fabricated by applying CIP packing procedure. Multifilamentary wire with Jc of 10,000 A/cm 2 was fabricated by rolling method using square billet as starting shape. The joining of the multifilamentary wire was done by etching and pressing process and showed 50% of joining efficiency. Analysis on the heat loss in cryostat for high Tc superconducting device was carried out for optimum design of the future cryogenic system. (author). 66 refs., 104 figs

  1. Optimal design of superconducting fault detector for superconductor triggered fault current limiters

    International Nuclear Information System (INIS)

    Yim, S.-W.; Kim, H.-R.; Hyun, O.-B.; Sim, J.; Park, K.B.; Lee, B.W.

    2008-01-01

    We have designed and tested a superconducting fault detector (SFD) for a 22.9 kV superconductor triggered fault current limiters (STFCLs) using Au/YBCO thin films. The SFD is to detect a fault and commutate the current from the primary path to the secondary path of the STFCL. First, quench characteristics of the Au/YBCO thin films were investigated for various faults having different fault duration. The rated voltage of the Au/YBCO thin films was determined from the results, considering the stability of the Au/YBCO elements. Second, the recovery time to superconductivity after quench was measured in each fault case. In addition, the dependence of the recovery characteristics on numbers and dimension of Au/YBCO elements were investigated. Based on the results, a SFD was designed, fabricated and tested. The SFD successfully detected a fault current and carried out the line commutation. Its recovery time was confirmed to be less than 0.5 s, satisfying the reclosing scheme in the Korea Electric Power Corporation (KEPCO)'s power grid

  2. Field mapping measurements to determine spatial and field dependence of critical current density in YBCO tapes

    International Nuclear Information System (INIS)

    Leclerc, J.; Berger, K.; Douine, B.; Lévêque, J.

    2013-01-01

    Highlights: • A method for characterizing superconducting tapes from field mapping is presented. • A new and efficient field mapping apparatus has been setup. • This method allows the spatial characterization of superconducting tapes. • The critical current density is obtained as a function of the flux density. • This method has been experimentally tested on an YBCO tape. -- Abstract: In this paper a measurement method that allows the determination of the critical current density of superconducting tape from field mapping measurements is presented. This contact-free method allows obtaining characteristics of the superconductor as a function of the position and of the applied flux density. With some modifications, this technique can be used for reel-to-reel measurements. The determination of the critical current density is based on an inverse calculation. This involves calculating the current distribution in the tape from magnetic measurements. An YBaCuO tape has been characterized at 77 K. A defect in this superconductor has been identified. Various tests were carried out to check the efficiency of the method. The inverse calculation was tested theoretically and experimentally. Comparison with a transport current measurement was also performed

  3. Chapter 27. Superconductors

    International Nuclear Information System (INIS)

    Vavra, O.

    2007-01-01

    In this chapter author deals with superconductors and superconductivity. Different chemical materials used as high-temperature superconductors are presented. Some applications of superconductivity are presented.

  4. Influence of superconductor film composition on adhesion strength of coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Kesgin, Ibrahim; Khatri, Narayan; Liu, Yuhao; Delgado, Louis; Galstyan, Eduard; Selvamanickam, Venkat

    2015-11-20

    The effect of high temperature superconductor (HTS) film composition on the adhesion strength of rare- earth barium copper oxide coated conductors (CCs) has been studied. It has been found that the mechanical integrity of the superconductor layer is very susceptible to the defects especially those along the ab plane, probably due to the weak interfaces between the defects and the matrix. Gd and Y in the standard composition were substituted with Sm and the number of in-plane defects was drastically reduced. Consequently, a four-fold increase in adhesion or peeling strength in Sm-based CCs was achieved compared to the standard GdYBCO samples.

  5. Influence of superconductor film composition on adhesion strength of coated conductors

    International Nuclear Information System (INIS)

    Kesgin, Ibrahim; Khatri, Narayan; Liu, Yuhao; Delgado, Louis; Galstyan, Eduard; Selvamanickam, Venkat

    2016-01-01

    The effect of high temperature superconductor (HTS) film composition on the adhesion strength of rare-earth barium copper oxide coated conductors (CCs) has been studied. It has been found that the mechanical integrity of the superconductor layer is very susceptible to the defects especially those along the ab plane, probably due to the weak interfaces between the defects and the matrix. Gd and Y in the standard composition were substituted with Sm and the number of in-plane defects was drastically reduced. Consequently, a four-fold increase in adhesion or peeling strength in Sm-based CCs was achieved compared to the standard GdYBCO samples. (paper)

  6. YBCO coated conductors by reactive thermal co-evaporation

    Energy Technology Data Exchange (ETDEWEB)

    Schmatz, U.; Hoffmann, Ch.; Bauer, M.; Metzger, R.; Berberich, P.; Kinder, H. [Technische Univ. Muenchen, Garching (Germany). Physik-Department

    2001-12-01

    Coated tape conductors of YBCO require a deposition process allowing to obtain a high volume growth rate in order to produce long lengths of tape in a reasonable amount of time. We present our tape coating system where 15 parallel loops of travelling tape of 1 cm width can be coated simultaneously by reactive thermal co-evaporation. For high critical current densities, in-plane alignment of the YBCO film is necessary. Inclined substrate deposition (ISD) is a technique that allows to deposit in-plane oriented buffer layers suitable for YBCO growth at high deposition rates. We present results obtained for YBCO films grown on MgO-ISD buffer layers deposited by e-gun evaporation onto metallic tape substrates. (orig.)

  7. Ternary superconductors

    International Nuclear Information System (INIS)

    Giorgi, A.L.

    1987-01-01

    Ternary superconductors constitute a class of superconducting compounds with exceptional properties such as high transition temperatures (≅ 15.2 K), extremely high critical fields (H c2 >60 Tesla), and the coexistence of superconductivity and long-range magnetic order. This has generated great interest in the scientific community and resulted in a large number of experimental and theoretical investigations in which many new ternary compounds have been discovered. A review of some of the properties of these ternary compounds is presented with particular emphasis on the ternary molybdenum chalcogenides and the ternary rare earth transition metal tetraborides. The effect of partial substitution of a second metal atom to form pseudoternary compounds is examined as well as some of the proposed correlations between the superconducting transition temperature and the structural and electronic properties of the ternary superconductors

  8. Superconductor Dynamics

    Energy Technology Data Exchange (ETDEWEB)

    Gömöry, F [Bratislava, Inst. Elect. Eng. (Slovakia)

    2014-07-01

    Superconductors used in magnet technology could carry extreme currents because of their ability to keep the magnetic flux motionless. The dynamics of the magnetic flux interaction with superconductors is controlled by this property. The cases of electrical transport in a round wire and the magnetization of wires of various shapes (circular, elliptical, plate) in an external magnetic field are analysed. Resistance to the magnetic field penetration means that the field produced by the superconducting magnet is no longer proportional to the supplied current. It also leads to a dissipation of electromagnetic energy. In conductors with unequal transverse dimensions, such as flat cables, the orientation with respect to the magnetic field plays an essential role. A reduction of magnetization currents can be achieved by splitting the core of a superconducting wire into fine filaments; however, new kinds of electrical currents that couple the filaments consequently appear. Basic formulas allowing qualitative analyses of various flux dynamic cases are presented.

  9. Chiral superconductors.

    Science.gov (United States)

    Kallin, Catherine; Berlinsky, John

    2016-05-01

    Chiral superconductivity is a striking quantum phenomenon in which an unconventional superconductor spontaneously develops an angular momentum and lowers its free energy by eliminating nodes in the gap. It is a topologically non-trivial state and, as such, exhibits distinctive topological modes at surfaces and defects. In this paper we discuss the current theory and experimental results on chiral superconductors, focusing on two of the best-studied systems, Sr2RuO4, which is thought to be a chiral triplet p-wave superconductor, and UPt3, which has two low-temperature superconducting phases (in zero magnetic field), the lower of which is believed to be chiral triplet f-wave. Other systems that may exhibit chiral superconductivity are also discussed. Key signatures of chiral superconductivity are surface currents and chiral Majorana modes, Majorana states in vortex cores, and the possibility of half-flux quantum vortices in the case of triplet pairing. Experimental evidence for chiral superconductivity from μSR, NMR, strain, polar Kerr effect and Josephson tunneling experiments are discussed.

  10. Microwave dynamics of YBCO bi-epitaxial Josephson structures

    DEFF Research Database (Denmark)

    Constantinian, K. Y.; Ovsyannikov, G. A.; Mashtakov, A. D.

    1996-01-01

    The processes of interaction of microwaves (frequency View the MathML source) with a single high-Tc superconducting YBa2Cu3Ox (YBCO) bi-epitaxial grain-boundary junction and with an array of two junctions connected in series, have been investigated experimentally at temperatures T = 4.2− 77 K......, as well as the subharmonic detector response at weak magnetic fields φ microwave field induced frequency synchronization of two series connected bi-epitaxial YBCO junctions....

  11. The effect of silver nanoparticle size on Jc of YBa2Cu3O7-x superconductor

    International Nuclear Information System (INIS)

    Farbod, M.; Batvandi, M.; Shoushtari, M. Z.

    2007-01-01

    Full text: Critical current density Jc is one of the most important superconducting parameters which is crucial in superconductor's applications. Introducing silver into the superconductors as intergrain filler has been a routine way to increase the Jc. In this work, YBa 2 Cu 3 O 7-x (YBCO), was doped by silver nanoparticles and their effect was studied on Jc as the flux pinning centers. Silver nanoparticles with sizes ranging from 30 to 1000 nm have been prepared using the reduction of silver in ethanol. The stoichiometric amounts of initial material of YBCO superconductor were added to the solution. After evaporation of ethanol, the obtained powder was used to fabricate YBCO samples. The total weight ratio of silver nanoparticles to superconductor was 1:100. The samples were characterized using SEM, EDX and XRD measurements. Jc was measured by a standard four probe technique. The results show by increasing silver nanoparticle size up to 700 nm, Jc increases then decreases by further increase in silver particle size. (authors)

  12. Processing and characterization of ceramic superconductor/polymer composites

    International Nuclear Information System (INIS)

    Kander, R.G.; Namboodri, S.L.

    1993-01-01

    One way to more easily process a brittle high-temperature ceramic superconductor into a useful structure is to combine it with a polymer to form a composite material. Processing of polymer-based composites into complex shapes is well established and relatively easy when compared with traditional ceramic processing unit operations. In addition, incorporating a ceramic superconductor into a polymer matrix can improve mechanical performance as compared with a monolithic ceramic. Finally, because ceramic superconductors are susceptible to attack by moisture, a polymer-based composite structure can also provide protection from deleterious environmental effects. This paper focuses on the processing and subsequent characterization of ceramic superconductor/polymer composites designed primarily for electromagnetic shielding and diamagnetic applications. YBa 2 Cu 3 O 7-x [YBCO] ceramic superconductor is combined with poly(methyl methacrylate) [PMMA] to form novel composite structures. Composite structures have been molded with both a discontinuous superconducting phase (i.e., ceramic particulate reinforced polymers) and with a continuous superconducting phase (i.e., polymer infiltrated porous ceramics). Characterization of these composite structures includes the determination of diamagnetic strength, electromagnetic shielding effectiveness, mechanical performance, and environmental resistance. The goal of this program is to produce a composite structure with increased mechanical integrity and environmental resistance at liquid nitrogen temperatures without compromising the electromagnetic shielding and diamagnetic properties of the superconducting phase. Composites structures of this type are potentially useful in numerous magnetic applications including electromagnetic shielding, magnetic sensors, energy storage, magnetic levitation, and motor windings

  13. New Phases of YBaCuGeO Superconductors Identified from X-ray Diffraction and Infra-red Absorption Measurements

    Science.gov (United States)

    Abo-Arais, Ahmed; Dawoud, Mohamad Ahmad Taher

    2005-01-01

    X-ray powder diffraction patterns and infra-red absorption spectra have been evaluated and analysed for the Y1 Ba2 Cu3 O7-d - Gex compound samples prepared by the solid state reaction with x values ranging from 0.0 to 1.13. All samples show bulk superconductivity above liquid nitrogen temperature using the levitation test (Meissner effect). Samples with Ge content up to x = 0.2 have offset Tc between 83K and 92K while the sample with x = 1.13 shows semiconducting behavior above 100K. As a result of the solid state interaction between YBCO and Ge, new phases are observed and determined, mainly three phases are concluded from X-ray powder diffraction analysis: (i) Ba2GeO4 (ii) Y2BaCuO5 (iii) BaCO3. The unit cell parameters a, b and c of the orthorhombic superconducting phase are calculated for all the prepared samples. The anisotropy factor is evaluated and related to the new structural phases in YBCO-Ge composite system. The I-R absorption spectra for the samples with orthorhombic symmetry have been determined. The phonon modes between ~ 400 cm-1 and 630 cm-1 are attributed to the Cu - O octahedron and pyramid vibrations for the CuO2 -planes and CuO-chains, while the peaks in the range from ~ 700 cm-1 to ~ 860 cm-1 may be due to defects such as the new phase Ba2GeO4 and the green phase Y2BaCuO5. The obtained results are discussed according to the superconductor - semi-conductor composite model and with the phonon-mediated charge transfer between CuO2 -planes and CuO- chains through apex oxygen (BaO).

  14. Oxygen desorption from YBa2Cu3O(7-x) and Bi2CaSr2Cu2O(8 + delta) superconductors

    Science.gov (United States)

    Mesarwi, A.; Levenson, L. L.; Ignatiev, A.

    1991-01-01

    Oxygen desorption experiments from YBa2Cu3O(7-x) (YBCO) and Bi2CaSr2Cu2O(8 + delta) (BSCCO) superconductors were carried out using a quadrupole mass spectrometer for monitoring the desorbing species and X-ray photoemission spectroscopy for surface characterization. Molecular oxygen was found to desorb from both superconductors following photoirradiation with ultraviolet/optical radiation and subsequent heating at over 150 C. Both YBCO and BSCCO were found to have similar oxygen desorption rates and similar activation energies. The desorption data as well as the X-ray photoemission data indicate that the oxygen desorption is not intrinsic to the superconductors but rather due to molecular oxygen entrapped in the material.

  15. Theory of disordered superconductors

    International Nuclear Information System (INIS)

    Wysokinski, K.I.

    1991-01-01

    The influence of disorder on the superconducting transition temperature is discussed. The main steps on the way to complete theory of disordered superconductors follows the steps in the authors' understanding of disorder and its effect on the quasiparticles in metals. Loosely speaking one can distinguish three such steps. First is the study of weakly disordered systems and this resulted in famous, celebrated Anderson theorem. The second step is ultimately connected with the coherent potential approximation as a method to study the spectrum and transport in concentrated alloys. The discovery of the role of usually neglected interferences between scattered waves in disordered conductors leading to decrease in mobility and increase of the mutual interactions between quantum particles, known as localization and interaction effects has given the new impetus to the theory of superconductivity. This is third step to be discussed in this lecture. The authors limit themselves to homogeneous bulk superconductors. In this paper some experiments on thin films as well as on copper oxides related to the presented theory are briefly mentioned

  16. Dynamics of vortices in planar and tubular microstructured superconductors

    International Nuclear Information System (INIS)

    Fomin, V. M.

    2011-01-01

    Full text: Nucleation and denucleation of vortices as well as their guided motion between antidots are key issues to design methods for controlling the vortex manipulation in micro patterned thin films and self-assembled micro tubes. The vortex dynamics in micro structured superconductors is modelled using an adaptive numerical approach on the basis of the time dependent Ginzburg-Landau equations. Evolution of the order parameter and the current density is analyzed for superconducting YBCO films with different patterns of antidots. The resulting picture of the accumulated vortex trajectories clearly reveals a guided motion between the antidots. Dynamics of correlated vortices in superconductor tubes in a magnetic field, which is perpendicular to their axes, is governed by the curvature. I acknowledge fruitful collaboration with R. Woerdenweber and O. G. Schmidt. (author)

  17. Textured YBCO films grown on wires: application to superconducting cables

    International Nuclear Information System (INIS)

    Dechoux, N; Jiménez, C; Chaudouët, P; Rapenne, L; Sarigiannidou, E; Robaut, F; Petit, S; Garaudée, S; Porcar, L; Soubeyroux, J L; Odier, P; Bruzek, C E; Decroux, M

    2012-01-01

    Efforts to fabricate superconducting wires made of YBa 2 Cu 3 O 7 (YBCO) on La 2 Zr 2 O 7 (LZO) buffered and biaxially textured Ni-5 at.%W (NiW) are described. Wires were manually shaped from LZO buffered NiW tapes. Different diameters were produced: 1.5, 2 and 3 mm. The wires were further covered with YBCO grown by metal organic chemical vapor deposition (MOCVD). We developed an original device in which the round substrate undergoes an alternated rotation of 180° around its axis in addition to a reel-to-reel translation. This new approach allows covering the whole circumference of the wire with a YBCO layer. This was confirmed by energy dispersive x-ray spectroscopy (EDX) analysis coupled to a scanning electron microscope (SEM). For all wire diameters, the YBCO layer thickness varied from 300 to 450 nm, and the cationic composition was respected. Electron backscattering diffraction (EBSD) measurements were performed directly on an as-deposited wire without surface preparation allowing the investigation of the crystalline quality of the film surface. Combining EBSD with XRD results we show that YBCO grows epitaxially on the LZO buffered NiW wires. For the first time, superconductive behaviors have been detected on round substrates in both the rolling and circular direction. J c reached 0.3 MA cm −2 as measured at 77 K by transport and third-harmonic detection. Those preliminary results confirm the effectiveness of the MOCVD for complex geometries, especially for YBCO deposition on small diameter wires. This approach opens huge perspectives for the elaboration of a new generation of YBCO-based round conductors. (paper)

  18. Localized superconductors

    International Nuclear Information System (INIS)

    Ma, M.; Lee, P.A.

    1985-01-01

    We study the effects of Anderson localization on superconductivity by using a Bardeen-Cooper-Schrieffer (BCS)-type trial wave function which pairs electrons in exact time-reversed eigenstates of the single-particle Hamiltonian. Within this approximation, and neglecting localization effects on the effective Coulomb repulsion and the electron-phonon coupling, we find that superconductivity persists below the mobility edge. In fact, Anderson's theorem is valid in the localized phase as long as rhoΔ 0 L/sup d/ > 1 (rho is the density of states averaged over +- Δ 0 of the Fermi energy, Δ 0 the BCS gap parameter, and L the localization length). Hence the gap order parameter Δ(r) remains uniform in space at the BCS value Δ 0 . The superfluid density and response to electromagnetic perturbations, however, show marked differences from the ''dirty superconductor'' regime. For rhoΔ 0 L/sup d/ < 1, Δ(r) fluctuates spatially and eventually drops to zero. In the limit when states are site localized, the system crosses over into the ''Anderson negative-U glass.'' Considerations beyond the trial wave-function approximation will speed up the destruction of superconductivity. The superconductor formed from localized states has the property that its quasiparticle excitations are also localized. Such excitations can be probed by observing the normal current in a tunneling junction

  19. Mode I type delamination fracture toughness of YBCO coated conductor with additional Cu layer

    International Nuclear Information System (INIS)

    Miyazato, T.; Hojo, M.; Sugano, M.; Adachi, T.; Inoue, Y.; Shikimachi, K.; Hirano, N.; Nagaya, S.

    2011-01-01

    A fracture toughness test method was developed for a YBCO coated conductor with an additional Cu layer. Mode I type tests were carried out using double cantilever beam (DCB) specimens. Delamination propagated into the YBCO layer, and sometimes reached the Ag/YBCO interface. The fracture toughness for YBCO was about 10 J/m 2 . That for Ag/YBCO interface was about 100 J/m 2 . Although interlaminar fracture at a YBa 2 Cu 3 O 7-δ (YBCO)/CeO 2 interface was reported for YBCO coated conductors, this has not yet been investigated by a fracture mechanical approach. In the present study, we developed a mode I type fracture toughness test method for a YBCO coated conductor with an additional Cu layer using double cantilever beam (DCB) specimens. Fracture mechanism was investigated by microscopic observation by a scanning electron microscope (SEM), together with composition analysis by an energy dispersive X-ray spectroscope (EDS). A pre-crack introduced at the YBCO/CeO 2 interface deviated from the interface, and propagated into the YBCO layer, and sometimes reached the Ag/YBCO interface. The fracture toughness, G R , for YBCO and the Ag/YBCO interface was evaluated to be 7-10 J/m 2 and 80-120 J/m 2 , respectively. The complex stress intensity factor ratio, K 2 /K 1 , at YBCO/CeO 2 interface was evaluated to be -0.19, and this ratio controlled the formation of microcracks in the YBCO layer. The main crack propagated into the YBCO layer accompanied with the formation of microcracks.

  20. Investigation of the properties of carbon-base nanostructures doped YBa{sub 2}Cu{sub 3}O{sub 7−δ} high temperature superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Dadras, Sedigheh, E-mail: dadras@alzahra.ac.ir; Ghavamipour, Mahshid

    2016-03-01

    In this research, we have investigated the effects of three samples of carbon-base nanostructures (carbon nanoparticles, carbon nanotubes and silicon carbide nanoparticles) doping on the properties of Y{sub 1}Ba{sub 2}Cu{sub 3}O{sub 7−δ} (YBCO) high temperature superconductor. The pure and doped YBCO samples were synthesized by sol–gel method and characterized by resistivity versus temperature (ρ–T), current versus voltage (I–V), through X-ray diffraction (XRD) and scanning electron microscope (SEM) analysis. The results confirmed that for all the samples, the orthorhombic phase of YBCO compound is formed. We found that the pinning energy and critical current density of samples increase by adding carbon nanostructures to YBCO compound. Also critical temperature is improved by adding carbon nanotubes to YBCO compound, while it does not change much for carbon and silicon carbide nanoparticles doped compounds. Furthermore, the samples were characterized by UV–vis spectroscopy in 300 K and the band gap of the samples was determined. We found that the carbon nanotubes doping decreases YBCO band gap in normal state from 1.90 eV to 1.68 eV, while carbon and SiC nanoparticles doping increases it to 2.20 and 3.37 eV respectively.

  1. Investigation of the properties of carbon-base nanostructures doped YBa_2Cu_3O_7_−_δ high temperature superconductor

    International Nuclear Information System (INIS)

    Dadras, Sedigheh; Ghavamipour, Mahshid

    2016-01-01

    In this research, we have investigated the effects of three samples of carbon-base nanostructures (carbon nanoparticles, carbon nanotubes and silicon carbide nanoparticles) doping on the properties of Y_1Ba_2Cu_3O_7_−_δ (YBCO) high temperature superconductor. The pure and doped YBCO samples were synthesized by sol–gel method and characterized by resistivity versus temperature (ρ–T), current versus voltage (I–V), through X-ray diffraction (XRD) and scanning electron microscope (SEM) analysis. The results confirmed that for all the samples, the orthorhombic phase of YBCO compound is formed. We found that the pinning energy and critical current density of samples increase by adding carbon nanostructures to YBCO compound. Also critical temperature is improved by adding carbon nanotubes to YBCO compound, while it does not change much for carbon and silicon carbide nanoparticles doped compounds. Furthermore, the samples were characterized by UV–vis spectroscopy in 300 K and the band gap of the samples was determined. We found that the carbon nanotubes doping decreases YBCO band gap in normal state from 1.90 eV to 1.68 eV, while carbon and SiC nanoparticles doping increases it to 2.20 and 3.37 eV respectively.

  2. Self-doping processes between planes and chains in the metal-to-superconductor transition of YBa2Cu3O6.9.

    Science.gov (United States)

    Magnuson, M; Schmitt, T; Strocov, V N; Schlappa, J; Kalabukhov, A S; Duda, L-C

    2014-11-12

    The interplay between the quasi 1-dimensional CuO-chains and the 2-dimensional CuO2 planes of YBa(2)Cu(3)O(6+x) (YBCO) has been in focus for a long time. Although the CuO-chains are known to be important as charge reservoirs that enable superconductivity for a range of oxygen doping levels in YBCO, the understanding of the dynamics of its temperature-driven metal-superconductor transition (MST) remains a challenge. We present a combined study using x-ray absorption spectroscopy and resonant inelastic x-ray scattering (RIXS) revealing how a reconstruction of the apical O(4)-derived interplanar orbitals during the MST of optimally doped YBCO leads to substantial hole-transfer from the chains into the planes, i.e. self-doping. Our ionic model calculations show that localized divalent charge-transfer configurations are expected to be abundant in the chains of YBCO. While these indeed appear in the RIXS spectra from YBCO in the normal, metallic, state, they are largely suppressed in the superconducting state and, instead, signatures of Cu trivalent charge-transfer configurations in the planes become enhanced. In the quest for understanding the fundamental mechanism for high-Tc-superconductivity (HTSC) in perovskite cuprate materials, the observation of such an interplanar self-doping process in YBCO opens a unique novel channel for studying the dynamics of HTSC.

  3. Low ac loss geometries in YBCO coated conductors

    International Nuclear Information System (INIS)

    Duckworth, R.C.; List, F.A.; Paranthaman, M.P.; Rupich, M.W.; Zhang, W.; Xie, Y.Y.; Selvamanickam, V.

    2007-01-01

    Reduction of ac losses in applied ac fields can be accomplished through either the creation of filaments and bridging in YBCO coated conductors or by an assembly of narrow width YBCO tapes. The ac losses for each of these geometries were measured at 77 K in perpendicular ac fields up to 100 mT. Despite physical isolation of the filaments, coupling losses were still present in the samples when compared to the expected hysteretic loss. In addition to filamentary conductors the assembly of stacked YBCO conductor provides an alternative method of ac loss reduction. When compared to a 4-mm wide YBCO coated conductor with a critical current of 60 A, the ac loss in a stack of 2-mm wide YBCO coated conductors with a similar total critical current was reduced. While the reduction in ac loss in a 2-mm wide stack coincided with the reduction in the engineering current density of the conductor, further reduction of ac loss was obtained through the splicing of the 2-mm wide tapes with low resistance solders

  4. Low ac loss geometries in YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Duckworth, R.C. [Oak Ridge National Laboratory, One Bethel Valley Road, P.O. Box 2008, MS-6305, Oak Ridge, TN 37831-6305 (United States)], E-mail: duckworthrc@ornl.gov; List, F.A.; Paranthaman, M.P. [Oak Ridge National Laboratory, One Bethel Valley Road, P.O. Box 2008, MS-6305, Oak Ridge, TN 37831-6305 (United States); Rupich, M.W.; Zhang, W. [American Superconductor, Two Technology Drive, Westborough, MA 01581 (United States); Xie, Y.Y.; Selvamanickam, V. [SuperPower, 450 Duane Ave, Schenectady, NY 12304 (United States)

    2007-10-01

    Reduction of ac losses in applied ac fields can be accomplished through either the creation of filaments and bridging in YBCO coated conductors or by an assembly of narrow width YBCO tapes. The ac losses for each of these geometries were measured at 77 K in perpendicular ac fields up to 100 mT. Despite physical isolation of the filaments, coupling losses were still present in the samples when compared to the expected hysteretic loss. In addition to filamentary conductors the assembly of stacked YBCO conductor provides an alternative method of ac loss reduction. When compared to a 4-mm wide YBCO coated conductor with a critical current of 60 A, the ac loss in a stack of 2-mm wide YBCO coated conductors with a similar total critical current was reduced. While the reduction in ac loss in a 2-mm wide stack coincided with the reduction in the engineering current density of the conductor, further reduction of ac loss was obtained through the splicing of the 2-mm wide tapes with low resistance solders.

  5. YBCO SQUIDs with unconventional current phase relation

    International Nuclear Information System (INIS)

    Bauch, T.; Johansson, J.; Cedergren, K.; Lindstroem, T.; Lombardi, F.

    2007-01-01

    We have studied the dynamics of YBa 2 Cu 3 O 7-δ (YBCO) dc sperconducting quantum interference devices (SQUIDs) characterized by an unconventional Josephson current phase relation (CPR). We have focused on SQUID configurations with Josephson junctions where the lobe of the order parameter in one electrode is facing a node in the other electrode. This order parameter arrangement should enhance the appearance of a sin(2φ) term in the CPR. The response of the critical current of the dc SQUID, under the effect of an external magnetic field, has been measured in temperature, down to 20 mK. Our experimental data have been compared with numerical simulations of the SQUIDs dynamics by considering a CPR of a single junction of the form I(φ) = I I sin(φ) - I II sin(2φ) where I I and I II are, respectively, the first and second harmonic component. In our devices the values of the sin(2φ) term are such that the fundamental state of the SQUID is naturally double degenerate. This is of great relevance for applications of d-wave SQUIDs in quantum information processing

  6. Magnetic levitation systems using a high-Tc superconducting bulk magnet

    Energy Technology Data Exchange (ETDEWEB)

    Ohsaki, Hiroyuki [Dept. of Electrical Engineering, Univ. of Tokyo (Japan); Kitahara, Hirotaka [Dept. of Electrical Engineering, Univ. of Tokyo (Japan); Masada, Eisuke [Dept. of Electrical Engineering, Univ. of Tokyo (Japan)

    1996-12-31

    Recent development of high-performance high-Tc bulk superconductors is making their application for electromagnetic force use feasible. We have studied electromagnetic levitation systems using high-Tc bulk superconducting material. In this paper, after an overview of superconducting magnetic levitation systems, with an emphasis on high-Tc bulk superconductor applications, experimental results of a high-Tc bulk EMS levitation and FEM analysis results of magnetic gradient levitation using bulk superconductor are described. Problems to be solved for their application are also discussed. (orig.)

  7. Method for preparation of textured YBa.sub.2 Cu.sub.3 O.sub.x superconductor

    Science.gov (United States)

    Selvamanickam, Venkat; Goyal, Amit; Kroeger, Donald M.

    1998-01-01

    The present invention relate to textured YBa.sub.2 Cu.sub.3 O.sub.x (Y-123) superconductors and a process of preparing them by directional recrystallization of compacts fabricated from quenched YBCO powders at temperatures about 100.degree. C. below the peritectic temperature to provide a superconductor where more than 75% of the YBa.sub.2 Cu.sub.3 O.sub.x phase is obtained without any Y.sub.2 BaCuO.sub.5 .

  8. Fabrication and characterization of melt-processed YBCO

    International Nuclear Information System (INIS)

    Sengupta, S.; Corpus, J.; Gaines, J.R. Jr.; Todt, V.R.; Zhang, X.F.; Miller, D.J.; Varanasi, C.; McGinn, P.J.

    1996-01-01

    Large domain YBCO are fabricated by using a melt processing technique for magnetic levitation applications. A Nd 1+x Ba 2-x Cu 3 O y seed is used to initiate grain growth and to control the orientation of YBCO grains. Samples as large as 2 inch have been fabricated by utilizing this method. Microstructural studies reveals two distinct regions in these levitators due to different growth mechanism along a/b and c axis. Some initial results on the mass production of these levitators are also reported

  9. High temperature superconductor based on thin strata reactively sputtered on metal targets. Final report

    International Nuclear Information System (INIS)

    Francke, C.; Meyer, B.; Wunderlich, R.; Mueller, J.

    1996-01-01

    SNS - Josephson contacts stable for a long period and dc SQUIDS working at 77 K were produced from the high temperature superconductor YBa 2 Cu 3 O 7-δ , where silver was used as the normal conductor. On MgO stages etched with ion beams, a defined section of the YBCO stratum can be produced and therefore a desired spacing can be set beteen the two YBCO electrodes. Structuring of the silver layer increases the normal conductive resistance of the Josephson contacts of the SQUIDs and therefore also the flux/voltage modulation stroke by up to 2 orders of mangitude. The dc SQUIDS in the so-called Ketchen design with 700 x 700 μm 2 square washers alone have a field sensitivity around 25 nT/Φ 0 . A multi-strata technology was developed from YBCO/STO/YBCO layer packages, which makes it possible to produce superconducting coils with corssovers and through contacts, which show critical currents of over 10 mA at 77 K. Using this multi-strata technology, flux transformers on 10 x 10 mm 2 STO substrates and on 20 x 20 mm 2 STO substrates were produced. Coupled to dc SQUIDs inductively in 'flip-chip' technique, such flux transformers supply a field sensitivity which is several times better than that of a flex transformer with a 10 x 10 mm 2 substrate. Field sensitivities around 0.2 nT/Φ 0 can be achieved. (orig./MM) [de

  10. High-resolution dichroic imaging of magnetic flux distributions in superconductors with scanning x-ray microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Ruoss, Stephen; Stahl, Claudia; Weigand, Markus; Schuetz, Gisela [Max-Planck-Institut fuer Intelligente Systeme, Stuttgart (Germany); Albrecht, Joachim [Research Institute for Innovative Surfaces, FINO, Aalen University (Germany)

    2015-07-01

    The penetration of magnetic flux into the high-temperature superconductor YBCO has been observed using a new high-resolution technique based on X-ray magnetic circular dichroism (XMCD). Superconductors coated with thin soft magnetic layers of CoFeB are observed in a scanning x-ray microscope providing cooling of the sample down to 83 K under the influence of external magnetic fields. Resulting electrical currents create an inhomogeneous magnetic field distribution above the superconductor which leads to a local reorientation of the ferromagnetic layer. X-ray absorption measurements with circular polarized radiation allows the analysis of the magnetic flux distribution in the superconductor via the ferromagnetic layer. In this work we present first images taken at 83K with high spatial resolution in the nanoscale.

  11. Studies on ceramic superconductors

    International Nuclear Information System (INIS)

    Chaklader, A.C.D.; Roemer, G.; Hardy, W.N.; Brewer, J.H.; Carolan, J.F.; Parsons, R.R.

    1987-01-01

    The superconducting properties of both bulk specimens and sputtered thin films of the YBa 2 Cu 3 O x compound have been studied. The bulk specimens were fabricated by cold pressing and sintering, and also by hot-pressing (subsequent reheating). The dc resistivity measurements showed a sharp drop in the temperature range 92-87K in this material. Muon spin relaxation (μSR) measurements of sintered discs in 3.4 kOe revealed the formation of a mixed state with an effective magnetic penetration depth λ ∼ 1365 angstrom at 6K, implying an effective charge carrier density of 6 x 10 21 cm -3 . The temperature dependence λ(T) is that of an ordinary s-wave superconductor. The resistivity of the thin film prepared from the compound by dc planar magnetron sputtering, showed a sharp drop to a very low value near 80K. The compound YBa 2 Cu 3 O x loses its superconducting properties, when either hot-pressed (in air) or oxidized at 500 degree C in high O 2 pressure, but this property can be restored when reheated in one atmosphere of O 2 above 900 degree C

  12. AC over-current test results of YBCO conductor for YBCO power transformer with fault current limiting function

    International Nuclear Information System (INIS)

    Tomioka, A.; Otonari, T.; Ogata, T.; Iwakuma, M.; Okamoto, H.; Hayashi, H.; Iijima, Y.; Saito, T.; Gosho, Y.; Tanabe, K.; Izumi, T.; Shiohara, Y.

    2011-01-01

    The single-layer coils with a diameter of 250 mm and 12 turns were manufactured with YBCO tapes with a CuNi- or Cu-Tape. The AC over-current tests were carried out in subcooled liquid nitrogen at 66 K and 74 K to develop power transformers with current limiting function. The AC over-current was two to seven times larger than the I c of conductor and it was reduced to the same level of I c . The I c of model coils did not degrade. The test results showed the possibility of YBCO superconducting transformers with current limiting function. We are developing elemental technology for 66 kV/6.9 kV 20 MVA-class YBCO power transformer. The YBCO transformer is considered to have a possibility to stabilize the power system by improving function of fault current limiting. Current limiting behavior functions over critical current flows. There is a possibility that superconducting characteristic may be damaged due to increase in temperature of YBCO tapes. Therefore, we have taken a measure to combine YBCO tape with CuNi tape or Cu Tape. We manufactured model coils using these conductors and conducted the AC over-current tests. The test current was two to seven times larger than the I c of conductor and it was damped with time from its maximum value according to the generation of conductor resistance. We verified the effectiveness of current limiting characteristics. In these tests, the I c of model coil did not degrade. We consider this conductor to be able to withstand AC over-current with the function of current limiting.

  13. Strong Flux Pinning of Nano-Sized Ysz Particles in Ybco Films Prepared by Mod Method

    Science.gov (United States)

    Ye, S.; Suo, H. L.; Liu, M.; Tang, X.; Wu, Z. P.; Zhao, Y.; Zhou, M. L.

    The YBCO films with doped YSZ nanoparticles have been prepared successfully by metal organic doepositon method using trifluoroacetates (TFA-MOD) through dissolving Zr organic salt into the YBCO precursor solution. The doped films have well in-plane and out-plane textures detected by both XRD Φ-scan and ω-scan. The YSZ nanoparticles with the size of about 5 ~ 15 nm were observed on the surface of the YBCO films using both FE-SEM and TEM. By comparing the superconducting properties, it was found that the doped YBCO films had lower Tc than that of undoped YBCO films. However, as increasing the applied magnetic field, Jc of the doped YBCO films were much better than that of undoped one. The Jc was as higher as 2.5 times than that of undoped YBCO film at 77 K and 1 T applied field.

  14. Phase transitions and transport in anisotropic superconductors with large thermal fluctuations

    International Nuclear Information System (INIS)

    Fisher, D.S.

    1991-01-01

    Fluctuation effects in conventional superconductors such as broadening of phase transitions and flux creep tend to be very small primarily because of the large coherence lengths. Thus mean field theory, with only small fluctuation corrections, usually provides an adequate description of these systems. Regimes in which fluctuation effects cause qualitatively different physics are very difficult to study as they typically occur in very small regions of the phase diagram or, in transport, require measuring extremely small voltages. In striking contrast, in the high temperature cuprate superconductors a combination of factors - short coherence lengths, anisotropy and higher temperatures - make fluctuation effects many orders of magnitude larger. The current understanding of transport and phase transitions in the cuprate superconductors-particularly YBCO and BSCCO-is reviewed. New results are presented on the two-dimensional regimes and 2D-3D crossover in the strongly anisotropic case of BSCCO. The emphasis is on pinning and vortex glass behavior

  15. Magneto-optical Kerr-effect at low temperatures. Investigation of superconductor/ferromagnet heterostructures

    Energy Technology Data Exchange (ETDEWEB)

    Zahn, Patrick; Bayer, Jonas [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Institute for Innovative Surfaces FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Stahl, Claudia; Ruoss, Stephen; Graefe, Joachim; Schuetz, Gisela [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Albrecht, Joachim [Institute for Innovative Surfaces FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2016-07-01

    With XMCD microscopy it is possible to visualize the critical current density of the superconductor YBCO with high spatial resolution. Therefore, soft magnetic CoFeB is introduced as sensor layer. The magnetic stray fields of the supercurrents lead to a local reorientation of the magnetic moments in the ferromagnet, which are then imaged via X-ray microscopy. These experiments have to be carried out at the scanning X-ray microscope MAXYMUS at the synchrotron Bessy II in Berlin. For that purpose pre-characterization of the sensor is highly desirable: Magnetic interactions between the superconductor and the ferromagnetic sensor layer have been investigated at low temperatures using Kerr-effect measurements. Therefore hysteresis loops are obtained by a sophisticated magnet and field ramping setup within the NanoMOKE3 system. The results are used to optimize the ferromagnetic sensor layer for XMCD microscopy of superconductors.

  16. Passivation of high temperature superconductors

    Science.gov (United States)

    Vasquez, Richard P. (Inventor)

    1991-01-01

    The surface of high temperature superconductors such as YBa2Cu3O(7-x) are passivated by reacting the native Y, Ba and Cu metal ions with an anion such as sulfate or oxalate to form a surface film that is impervious to water and has a solubility in water of no more than 10(exp -3) M. The passivating treatment is preferably conducted by immersing the surface in dilute aqueous acid solution since more soluble species dissolve into the solution. The treatment does not degrade the superconducting properties of the bulk material.

  17. Fabrication and properties of sub-micrometric YBCO biepitaxial junctions

    Energy Technology Data Exchange (ETDEWEB)

    Stornaiuolo, D; Born, D; Barone, A [CNR-INFM Coherentia, Napoli (Italy); Cedergren, K; Bauch, T; Lombardi, F [MC2 Chalmers University of Technology, Goteborg (Sweden); Rotoli, G [CNISM and Universita dell' Aquila (Italy); Tafuri, F, E-mail: stornaiuolo@na.infh.i [Seconda Universita degli Studi di Napoli, Aversa (Italy)

    2009-03-01

    We report on the fabrication procedure and the transport properties of submicron grain boundary biepitaxial YBCO Josephson junctions. These first results are very encouraging and justify further expectations on improved performances for such types of devices. A reduced and more controlled faceting along the grain boundary interface, for instance, will better preserve intrinsic d-wave effects, and favour the study of fluxons dynamics.

  18. A Thermally Actuated Flux Pump for Energizing YBCO Pucks

    Science.gov (United States)

    2016-05-01

    a Hall sensor with an advertised active area of approximately 1.016 mm diameter supplied by Lakeshore was positioned in the centre of the YBCO as...top and the coldhead (green) along the bottom. The brown colour is the light green of the coldhead and the orange of the dysprosium centre

  19. Preparation of YBCO superconducting films by spray pyrolysis method

    International Nuclear Information System (INIS)

    Mora Alonso, M.; Leyva Fabelo, A.; Rubio Frias, E.; Pupo Gonzalez, I.; Lopez Sanchez, D.

    1994-01-01

    The methodology for the preparation of YBCO superconducting films on Zr 2O (Y) substrates by spray pyrolysis method is reported. The transition temperature of these films is superior than the boiling temperature of liquid 2N . Other critical parameters are similar to those reported by other authors using the same technique

  20. Processing Y- and Bi-based superconductors

    International Nuclear Information System (INIS)

    Balachandran, U.; Dos Santos, D.I.; von Stumberg, A.W.; Graham, S.W.; Singh, J.P.; Youngdahl, C.A.; Goretta, K.C.; Shi, D.; Poeppel, R.B.

    1989-01-01

    This paper reports on bulk specimens of YBa 2 Cu 3 O x and Bi 2 Sr 2 CaCu 2 O y formed and then processed by sintering in the solid state, in the presence of a liquid phase, or by sinter forging. Both Y- and Bi-based superconductors are difficult to densify by solid-state sintering but easy to densify in the presence of a liquid phase. Effects of sintering conditions on superconducting properties are, however, different between the two materials. These differences will be discussed. Attempts to texture microstructures and increase J c by sinter-forging techniques have been successful for Y-based superconductors, but unsuccessful for Bi-based superconductors

  1. Powder processing of high Tc oxide superconductors and their properties

    International Nuclear Information System (INIS)

    Vajpei, A.C.; Upadhyaya, G.S.

    1992-01-01

    Powder processing of ceramics is an established technology and in the area of high T c superconductors, its importance is felt even more significantly. The present monograph is an attempt in this direction to explore the perspectives and practice of powder processing routes towards control and optimization of the microstructure and pertinent properties of high T c oxide superconductors. The monograph consists of 6 chapters. After a very brief introduction (Chapter 1), Chapter 2 describes various classes of high T c oxide superconductors and their phase equilibria. Chapter 3 highlights the preparation of oxide superconductor powders through various routes and details their subtle distinctions. Chapter 4 briefly covers characterisation of the oxide superconductors, laying emphasis on the process-analysis and microstructure. Chapter 5 describes in detail various fabrication techniques for bulk superconductors through the powder routes. The last Chapter (Chapter 6) describing properties of bulk oxide superconductors, discusses the role of subtituents, compositional variations and processing methods on such properties. References are given at the end of each chapter. (orig.)

  2. Study of the glass formation of high temperature superconductors

    Science.gov (United States)

    Ethridge, Edwin C.; Kaukler, William F.; Rolin, Terry

    1992-01-01

    A number of compositions of ceramic oxide high T(sub c) superconductors were elevated for their glass formation ability by means of rapid thermal analysis during quenching, optical, and electron microscopy of the quenched samples, and with subsequent DSC measurements. Correlations between experimental measurements and the methodical composition changes identified the formulations of superconductors that can easily form glass. The superconducting material was first formed as a glass; then, with subsequent devitrification, it was formed into a bulk crystalline superconductor by a series of processing methods.

  3. Holographic superconductor in the analytic hairy black hole

    International Nuclear Information System (INIS)

    Myung, Yun Soo; Park, Chanyong

    2011-01-01

    We study the charged black hole of hyperbolic horizon with scalar hair (charged Martinez-Troncoso-Zanelli: CMTZ black hole) as a model of analytic hairy black hole for holographic superconductor. For this purpose, we investigate the second order phase transition between CMTZ and hyperbolic Reissner-Nordstroem-AdS (HRNAdS) black holes. However, this transition unlikely occurs. As an analytic treatment for holographic superconductor, we develop superconductor in the bulk and superfluidity on the boundary using the CMTZ black hole below the critical temperature. The presence of charge destroys the condensates around the zero temperature, which is in accord with the thermodynamic analysis of the CMTZ black hole.

  4. Macroturbulence in superconductors

    International Nuclear Information System (INIS)

    Vlasko-Vlasov, V.K.; Nikitenko, V.I.; Polyanskii, A.A.

    1994-07-01

    Direct magneto-optic observation of coupling of the Abrikosov vortices into macroscopic drops of increased flux density at remagnetization of the YBCO single crystal is presented. Appearance of these flux structures correspond to strong perturbations of the current trajectories and transition fro laminar to turbulent current flow

  5. Doped Tl-1212 and Tl-1223 superconductors

    International Nuclear Information System (INIS)

    Eder, M.H.

    2001-09-01

    This work describes the preparation and characterization of thallium-lead-strontium-barium-calcium-(uranium)-copperoxide (Tl-1212, Tl-1223) high-temperature superconductors. The precursors were prepared via nitrate method. After calcination the oxidic powders were mixed with stoichiometric amounts of an Tl 2 O 3 , PbO, Er 2 O 3 and Gd 2 O 3 by milling and afterwards uniaxial compressed. Sintering was carried out in silver foils. X-ray diffractometry and high-resolution microscopy in combination with scanning electron microscopy (including EDAX) were used to study the influence of varying thallium/lead-, strontium/barium-, calcium/rare earth element ratios and the effect of uranium on the phase composition and microstructure of bulk superconductors. Furthermore the influence of the composition on the electrical and magnetical properties was studied. On phase pure Tl-1212 and Tl-1223 superconductors NMR-measurements were done. Small amounts of gadolinium and erbium instead of calcium and excess-uranium have a positive impact on the electrical and magnetical properties of the Tl-1223 superconductors. Higher amounts of these doping elements favor the Tl-1212 phase. Tl-1212 superconductors with varying thallium/lead- strontium/barium- and calcium/gadolinium ratios were prepared phasepure in wide range of doping. Transition temperatures up to 96 K were achieved. It was shown that lead has an oxidation number of +4 and thallium of +3. (author)

  6. Detection of second harmonic of phase dependence of superconducting current in Nb/Au/YBCO heterojunctions

    CERN Document Server

    Komissinskij, F V; Ilichev, E V; Ivanov, Z G

    2001-01-01

    The results of the experimental study on the current phase dependence (CPD) of the heterotransitions, consisting of the niobium and the YBa sub 2 Cu sub 3 O sub x (YBCO) film with an additional interlayer from gold (Nb/Au/YBCO) are presented. The CPD measurement is carried out through the radiofrequency superconducting quantum interferometer. The CPD second harmonic is determined in the Nb/Au/YBCO heterotransitions. Possible causes of its appearance are discussed within the frames of the d +- s combined symmetry of the YBCO order parameter. One of the causes of the CPD second harmonic appearance is the twinning of the YBCO films (001). The second cause of existing the anomalously high critical current consists in the availability of the Nb/Au boundary with the transparence of approx 10 sup - sup 1 in the Nb/Au/YBCO

  7. Bulk Kosterlitz-Thouless Type Molecular Superconductor β″-(BEDT-TTF)2[(H2O)(NH4)2Cr(C2O4)3]·18-crown-6.

    Science.gov (United States)

    Martin, Lee; Lopez, Jordan R; Akutsu, Hiroki; Nakazawa, Yasuhiro; Imajo, Shusaku

    2017-11-20

    A new molecular superconductor, β″-(BEDT-TTF) 2 [(H 2 O)(NH 4 ) 2 Cr(C 2 O 4 ) 3 ]·18-crown-6, has been synthesized from the organic donor molecule BEDT-TTF with the anion Cr(C 2 O 4 ) 3 3- . The crystal structure consists of conducting organic layers of BEDT-TTF molecules which adopt the β″ packing motif (layer A), layers of NH 4 + and Λ-Cr(C 2 O 4 ) 3 3- (layer B), layers of (H 2 O)(NH 4 )18-crown-6 (layer C), and layers of NH 4 + and Δ-Cr(C 2 O 4 ) 3 3- (layer D) which produce a superstructure with a repeating pattern of ABCDABCDA. As a result of this packing arrangement, this is the 2D superconductor with the widest gap between conducting layers where only a single donor packing motif is present (β″). Superconducting critical temperatures at ambient pressure observed by electrical transport and magnetic measurements are 4.0-4.9 and 2.5 K, respectively. The strong 2D nature of this system, the broad transition to T zero at 1.8K, and the transition of α of V ∝ I α from 1 to 3 on I-V curves strongly suggest that the superconducting transition is very close to a Kosterlitz-Thouless transition. The magnetic field dependence of the superconducting critical temperature parallel to the conducting plane gives an upper critical field μ 0 H c2∥ > 8 T, which is over the calculated Pauli-Clogston limit for this material.

  8. Property and microstructural nonuniformity in the yttrium-barium-copper-oxide superconductor determined from electrical, magnetic, and ultrasonic measurements

    International Nuclear Information System (INIS)

    Roth, D.J.

    1991-01-01

    This dissertation is presented in two major chapters. In the first chapter, the use of ultrasonic velocity for estimating pore fraction in YBCO and other polycrystalline materials is reviewed, modeled, and statistically analyzed. This chapter provides the basis for using ultrasonic velocity to interrogate microstructure. In the second chapter, (1) the effect of pore fraction (0.10-0.25) on superconductor properties of YBCO samples is characterized, (2) spatial (within-sample) variations in microstructure and superconductor properties are investigated and (3) the effect of oxygen content on elastic behavior is examined. Experimental methods used included a.c. susceptibility, electrical, and ultrasonic-velocity measurements. Superconductor properties measured included transition temperature, magnetic transition width, transport and magnetic critical current density, magnetic shielding, a.c. loss, and sharpness of the voltage-current characteristic. Superconductor properties including within-sample uniformity were generally poorest for samples containing the lowest (0.10) pore fraction. Ultrasonic velocity was linearly related to pore fraction thereby allowing sample classification. Changes in superconducting behavior were observed consistent with changes in oxygen content

  9. Large-scale HTS bulks for magnetic application

    International Nuclear Information System (INIS)

    Werfel, Frank N.; Floegel-Delor, Uta; Riedel, Thomas; Goebel, Bernd; Rothfeld, Rolf; Schirrmeister, Peter; Wippich, Dieter

    2013-01-01

    Highlights: ► ATZ Company has constructed about 130 HTS magnet systems. ► Multi-seeded YBCO bulks joint the way for large-scale application. ► Levitation platforms demonstrate “superconductivity” to a great public audience (100 years anniversary). ► HTS magnetic bearings show forces up to 1 t. ► Modular HTS maglev vacuum cryostats are tested for train demonstrators in Brazil, China and Germany. -- Abstract: ATZ Company has constructed about 130 HTS magnet systems using high-Tc bulk magnets. A key feature in scaling-up is the fabrication of YBCO melts textured multi-seeded large bulks with three to eight seeds. Except of levitation, magnetization, trapped field and hysteresis, we review system engineering parameters of HTS magnetic linear and rotational bearings like compactness, cryogenics, power density, efficiency and robust construction. We examine mobile compact YBCO bulk magnet platforms cooled with LN 2 and Stirling cryo-cooler for demonstrator use. Compact cryostats for Maglev train operation contain 24 pieces of 3-seed bulks and can levitate 2500–3000 N at 10 mm above a permanent magnet (PM) track. The effective magnetic distance of the thermally insulated bulks is 2 mm only; the stored 2.5 l LN 2 allows more than 24 h operation without refilling. 34 HTS Maglev vacuum cryostats are manufactured tested and operate in Germany, China and Brazil. The magnetic levitation load to weight ratio is more than 15, and by group assembling the HTS cryostats under vehicles up to 5 t total loads levitated above a magnetic track is achieved

  10. Large-scale HTS bulks for magnetic application

    Energy Technology Data Exchange (ETDEWEB)

    Werfel, Frank N., E-mail: werfel@t-online.de [Adelwitz Technologiezentrum GmbH (ATZ), Rittergut Adelwitz 16, 04886 Arzberg-Adelwitz (Germany); Floegel-Delor, Uta; Riedel, Thomas; Goebel, Bernd; Rothfeld, Rolf; Schirrmeister, Peter; Wippich, Dieter [Adelwitz Technologiezentrum GmbH (ATZ), Rittergut Adelwitz 16, 04886 Arzberg-Adelwitz (Germany)

    2013-01-15

    Highlights: ► ATZ Company has constructed about 130 HTS magnet systems. ► Multi-seeded YBCO bulks joint the way for large-scale application. ► Levitation platforms demonstrate “superconductivity” to a great public audience (100 years anniversary). ► HTS magnetic bearings show forces up to 1 t. ► Modular HTS maglev vacuum cryostats are tested for train demonstrators in Brazil, China and Germany. -- Abstract: ATZ Company has constructed about 130 HTS magnet systems using high-Tc bulk magnets. A key feature in scaling-up is the fabrication of YBCO melts textured multi-seeded large bulks with three to eight seeds. Except of levitation, magnetization, trapped field and hysteresis, we review system engineering parameters of HTS magnetic linear and rotational bearings like compactness, cryogenics, power density, efficiency and robust construction. We examine mobile compact YBCO bulk magnet platforms cooled with LN{sub 2} and Stirling cryo-cooler for demonstrator use. Compact cryostats for Maglev train operation contain 24 pieces of 3-seed bulks and can levitate 2500–3000 N at 10 mm above a permanent magnet (PM) track. The effective magnetic distance of the thermally insulated bulks is 2 mm only; the stored 2.5 l LN{sub 2} allows more than 24 h operation without refilling. 34 HTS Maglev vacuum cryostats are manufactured tested and operate in Germany, China and Brazil. The magnetic levitation load to weight ratio is more than 15, and by group assembling the HTS cryostats under vehicles up to 5 t total loads levitated above a magnetic track is achieved.

  11. Study of the inhomogeneity of critical current under in-situ tensile stress for YBCO tape

    Science.gov (United States)

    Zhu, Y. P.; Chen, W.; Zhang, H. Y.; Liu, L. Y.; Pan, X. F.; Yang, X. S.; Zhao, Y.

    2018-07-01

    A Hall sensor system was used to measure the local critical current of YBCO tape with high spatial resolution under in-situ tensile stress. The hot spot generation and minimum quench energy of YBCO tape, which depended on the local critical current, was calculated through the thermoelectric coupling model. With the increase in tensile stress, the cracks which have different dimensions and critical current degradation arose more frequently and lowered the thermal stability of the YBCO tape.

  12. Flux pinning characteristics of Sn-doped YBCO film by the MOD process

    International Nuclear Information System (INIS)

    Choi, S.M.; Shin, G.M.; Yoo, S.I.

    2013-01-01

    Highlights: ► The pinning effects of undoped and Sn-doped YBCO films by MOD were characterized. ► Sn-containing nanoparticles were trapped in Sn-doped YBCO films by MOD. ► Sn-containing nanoparticles were identified as the YBa 2 SnO 5.5 (YBSO) phase by TEM. ► The YBSO nanoparticles are responsible for improved flux pinning effect. ► We report the orientation relationship between YBSO nanoparticles and YBCO matrix. -- Abstract: Compared with the undoped YBa 2 Cu 3 O 7−δ (YBCO) film, 10 mol% Sn-doped YBCO film exhibited significantly enhanced critical current densities (J c ) in magnetic fields up to 5 T at 65 and 77 K for H//c, indicating that the Sn-doped YBCO film possesses more effective flux pinning centers. Both samples were grown on the SrTiO 3 (STO) (1 0 0) single crystal substrates by the metal-organic deposition (MOD) process. Larger J c (77 K, 1 T) values of Sn-doped YBCO film are observed over a wide field-orientation angle (θ) except the field-orientations close to the ab-plane of YBCO (85° c values for 85° 2 SnO 5.5 (YBSO) phase by STEM (scanning transmission electron microscopy)-EDS (energy dispersive X-ray spectroscopy) analysis. Further analyses by HR-TEM (high resolution-transmission electron microscopy) revealed that YBSO nanoparticles completely surrounded by the YBCO matrix had random orientation with YBCO while those located at the interface of YBCO/STO substrate had epitaxial relationship with YBCO

  13. Bulk electronic structures of n-type superconductor Nd1.85Ce0.15CuO4 probed by high energy angle-resolved photoemission spectroscopy

    International Nuclear Information System (INIS)

    Tsunekawa, M.; Sekiyama, A.; Kasai, S.; Yamasaki, A.; Fujiwara, H.; Sing, M.; Shigemoto, A.; Imada, S.; Onose, Y.; Tokura, Y.; Muro, T.; Suga, S.

    2005-01-01

    We report on a high-energy angle-resolved photoemission (ARPES) study of the n-type high-T C cuprate, Nd 1.85 Ce 0.15 CuO 4 (NCCO). Our bulk sensitive results suggest a hole-like Fermi surface as seen by the so far reported low-energy ARPES studies. The soft X-ray Cu 2p core-level photoemission spectra show clear polar-angle dependence, suggesting the difference in electron states between the bulk and surface

  14. Anomalous Josephson Effect between Even-and Odd-Frequency Superconductors

    NARCIS (Netherlands)

    Tanaka, Yukio; Golubov, Alexandre Avraamovitch; Kashiwaya, Satoshi; Ueda, Masahito

    2007-01-01

    We demonstrate that, contrary to standard wisdom, the lowest-order Josephson coupling is possible between odd- and even-frequency superconductors. The origin of this effect is the induced odd- (even-)frequency pairing component at the interface of bulk even- (odd-)frequency superconductors. The

  15. Pinning characteristics in chemically modified (Nd, Eu, Gd)-Ba-Cu-O superconductors

    Czech Academy of Sciences Publication Activity Database

    Muralidhar, M.; Sakai, N.; Nishiyama, M.; Jirsa, Miloš; Machi, T.; Murakami, M.

    2003-01-01

    Roč. 82, č. 6 (2003), s. 943-945 ISSN 0003-6951 R&D Projects: GA AV ČR IAA1010919 Institutional research plan: CEZ:AV0Z1010914 Keywords : melt-textured superconductors * pinning defects * irreversibility field * bulk superconductors * ternary systems * twin structure Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 4.049, year: 2003

  16. Estudio de la susceptibilidad magnética AC en el superconductor YBCO

    OpenAIRE

    Blandón Pedraza, Adriana Lizeth

    2014-01-01

    En este trabajo se fabricaron muestras volumétricas de YBa2Cu3O7−d , variando la presión de compactación de 191,03 MPa a 445,74 MPa, la temperatura en el ciclo térmico de sinterizado de 700 °C a 900 °C y el porcentaje de plata del 0% al 20%, con el propósito de mejorar la conexión entre granos y consecuentemente la densidad de corriente crítica intergranular. Las muestras fueron caracterizadas por difracción de rayos X, microscopia electrónica de barrido, efecto Meissner y mediciones de susce...

  17. Effects of magnetizing on flux pinning force for sintered YBCO superconductor

    International Nuclear Information System (INIS)

    Ding, S.Y.; Yan, J.L.; Yu, Z.; Shi, K.X.; Tong, H.W.; Qiu, L.

    1989-01-01

    It is shown that magnitude and course of magnetizing field influence magnetization and transport current. Effective flux pinning force density with two types is extracted by an iterative procedure based on the critical state equation. One of the types is attributed to the weak links and the other is considered to be resulted from the intragrain flux pinning centers

  18. Fine uniform filament superconductors

    Science.gov (United States)

    Riley, Jr., Gilbert N.; Li, Qi; Roberts, Peter R.; Antaya, Peter D.; Seuntjens, Jeffrey M.; Hancock, Steven; DeMoranville, Kenneth L.; Christopherson, Craig J.; Garrant, Jennifer H.; Craven, Christopher A.

    2002-01-01

    A multifilamentary superconductor composite having a high fill factor is formed from a plurality of stacked monofilament precursor elements, each of which includes a low density superconductor precursor monofilament. The precursor elements all have substantially the same dimensions and characteristics, and are stacked in a rectilinear configuration and consolidated to provide a multifilamentary precursor composite. The composite is thereafter thermomechanically processed to provide a superconductor composite in which each monofilament is less than about 50 microns thick.

  19. Development of an YBCO coil with SSTC conductors for high field application

    Science.gov (United States)

    Shi, Y.; Liu, H. J.; Liu, F.; Tan, Y. F.; Jin, H.; Yu, M.; Lei, L.; Guo, L.; Hong, Z. Y.

    2018-07-01

    With the continuous reduction of the production costs and improvement of the transport performance, YBCO coated conductor is the most promising candidate for the high field magnet application due to its high irreversibility field and strong mechanical properties. Presently a stable production capacity of the YBCO conductors has been achieved by Shanghai Superconducting Technology Co., Ltd (SSTC) in China. Therefore, the demand in high field application with YBCO conductors is growing in China. This paper describes the design, fabrication and preliminary experiment of a solenoid coil with YBCO conductors supplied by SSTC to validate the possibility of high field application. Four same double pancakes were manufactured and assembled for the YBCO coil where the outer diameter and height was 54.3 and 48 mm respectively to match the dimensional limitation of the 14 T background magnets. The critical current (Ic) of YBCO conductors was obtained by measuring as a function of the applied field perpendicular to the YBCO conductor surface which provides the necessary input parameters for preliminary performance evaluation of the coil. Finally the preliminary test and discussion at 77 and 4.2 K were carried out. The consistency of four double pancakes Ic was achieved. The measured results indicate that the fabrication technology of HTS coil is reliable which gives the conference for the in-field test in high field application. This YBCO coil is the first demonstration of the SSTC YBCO coated conductors.

  20. Control of Flux Pinning in MOD YBCO Coated Conductor

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, W. [American Superconductor Corporation, Westborough, MA; Huang, Y. [American Superconductor Corporation, Westborough, MA; Li, X. [American Superconductor Corporation, Westborough, MA; Kodenkandath, Thomas [American Superconductor Corporation, Westborough, MA; Rupich, Marty [American Superconductor Corporation, Westborough, MA; Schoop, U. [American Superconductor Corporation, Westborough, MA; Verebelyi, D. T. [American Superconductor Corporation, Westborough, MA; Thieme, C. L. H. [American Superconductor Corporation, Westborough, MA; Siegal, E. E. [American Superconductor Corporation, Westborough, MA; Holesinger, T. G. [Los Alamos National Laboratory (LANL); Maiorov, B. [Los Alamos National Laboratory (LANL); Miller, D. J. [Argonne National Laboratory (ANL); Maroni, V. A. [Argonne National Laboratory (ANL); Goyal, Amit [ORNL; Specht, Eliot D [ORNL; Paranthaman, Mariappan Parans [ORNL

    2007-01-01

    Two different types of defect structures have been identified to be responsible for the enhanced pinning in metal organic deposited YBCO films. Rare earth additions result in the formation of nanodots in the YBCO matrix, which form uncorrelated pinning centers, increasing pinning in all magnetic field orientations. 124-type intergrowths, which form as laminar structures parallel to the ab-plane, are responsible for the large current enhancement when the magnetic field is oriented in the ab-plane. TEM studies showed that the intergrowths emanate from cuprous containing secondary phase particles, whose density is partially controlled by the rare earth doping level. Critical process parameters have been identified to control this phase formation, and therefore, control the f 24 intergrowth formation. This work has shown that through process control and proper conductor design, either by adjusting the composition or by multiple coatings of different functional layers, the desired angular dependence can be achieved.

  1. Control of flux pinning in MOD YBCO coated conductor.

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, W.; Huang, Y.; Li, X.; Kodenkandath, T.; Rupich, M. W.; Schoop, U.; Verebelyi, D. T.; Thieme, C. L. H.; Siegal, E.; Holesinger, T. G.; Maiorov, B.; Civale, L.; Miller, D. J.; Maroni, V. A.; Li, J.; Martin, P. M.; Specht, E. D.; Goyal, A.; Paranthaman, M. P.; American Superconductor Corp.; LANL; ORNL

    2007-06-01

    NTwo different types of defect structures have been identified to be responsible for the enhanced pinning in metal organic deposited YBCO films. Rare earth additions result in the formation of nanodots in the YBCO matrix, which form uncorrelated pinning centers, increasing pinning in all magnetic field orientations. 124-type intergrowths, which form as laminar structures parallel to the ab-plane, are responsible for the large current enhancement when the magnetic field is oriented in the ab-plane. TEM studies showed that the intergrowths emanate from cuprous containing secondary phase particles, whose density is partially controlled by the rare earth doping level. Critical process parameters have been identified to control this phase formation, and therefore, control the f 24 intergrowth formation. This work has shown that through process control and proper conductor design, either by adjusting the composition or by multiple coatings of different functional layers, the desired angular dependence can be achieved.

  2. Thermoelectric power of the Ni and Cd substituted YBCO system

    International Nuclear Information System (INIS)

    Mukherjee, C.D.; Ranganathan, R.; Raychaudhuri, A.K.; Chatterjee, N.

    1989-01-01

    The thermoelectric power behaviour in the range between 250 K and the superconducting transition temperature T c of YBa 2 Cu 3-x A x O 7-y (where A = Ni or Cd and x = 0.2 and 0.4) samples has been examined. The normalized resistance and thermopower of substituted samples as functions of temperature are plotted and discussed. It was concluded that nickel has a slight positive role in causing overall thermopower generation in the YBCO system

  3. Memory effects and peak effect in type II superconductors

    International Nuclear Information System (INIS)

    Pasquini, G.; Luna, D.; Eismann, B.; Bettachini, V.; Bekeris, V.

    2007-01-01

    A large amount of experimental and theoretical work has been devoted to understand memory effects (ME) in the solid vortex lattice (VL) but has remained, however, controversial until now. In the vicinity of the anomaly known as the peak effect (PE) both the VL mobility and the measured critical current density are found to be dependent of the dynamical history of the sample, in both low T c (LTS) and high T c (HTS) superconductors. Experiments in YBa 2 Cu 3 O 7 (YBCO) crystals have shown that the mobility of the VL increases after assisting the system with a symmetric AC field (or current) of moderated amplitude. On the other hand, after an asymmetric AC field assists vortices, the VL becomes less mobile. These features indicate that ME in these samples cannot be ascribed to an equilibration process, but probably are related to the organization of the lattice after nearest neighbor re-accommodation or induced plastic VL deformation. Recently, we have shown evidence that in YBCO the PE is a dynamic anomaly observed in the non-linear response, and is absent in the Labusch constant derived from the linear Campbell regime. However, this behavior seems not to be extensive to other systems as the traditional LTS NbSe 2 . In this work, the AC response in the PE region of NbSe 2 and YBCO samples are presented and compared. Very salient differences both in the linear and non-linear response as well as in the ME characteristics indicate that a different physics governs the PE phenomena in each case

  4. Towards Faster FEM Simulation of Thin Film Superconductors: A Multiscale Approach

    DEFF Research Database (Denmark)

    Rodriguez Zermeno, Victor Manuel; Mijatovic, Nenad; Træholt, Chresten

    2011-01-01

    This work presents a method to simulate the electromagnetic properties of superconductors with high aspect ratio such as the commercially available second generation superconducting YBCO tapes. The method is based on a multiscale representation for both thickness and width of the superconducting...... at considerable lower computational time. Several test cases were simulated including transport current, externally applied magnetic field and a combination of both. The results are in good agreement with recently published numerical simulations. The computational time to solve the present multiscale approach...

  5. A neutron depolarization study of magnetic inhomogeneities in weak-link superconductors

    International Nuclear Information System (INIS)

    Zhuchenko, N.K.; Yagud, R.Z.

    1993-01-01

    Neutron depolarization measurements in the mixed state of both high-T c and low-T c weak-link superconductors have been carried out. Samples of YBCO, BSCCO, SnMo 6 S 8 and 0.5 Nb-0.5 Ti of different magnetic prehistory were analyzed at temperatures T 4.2 K under applied magnetic fields II <= 16.5 kOe. We ascribe the appearance of magnetic inhomogeneities and their hysteresis behaviour to the interaction between dipole magnetic fields (diamagnetic and paramagnetic ones) and applied magnetic fields

  6. Observation of Sinusoidal Voltage Behaviour in Silver Doped YBCO

    Science.gov (United States)

    Altinkok, Atilgan; Olutas, Murat; Kilic, Kivilcim; Kilic, Atilla

    The influence of bi-directional square wave (BSW) current was investigated on the evolution of the V - t curves at different periods (P) , temperatures and external magnetic fields. It was observed that slow transport relaxation measurements result in regular sinusoidal voltage oscillations which were discussed mainly in terms of the dynamic competition between pinning and depinning.The symmetry in the voltage oscillations was attributed to the elastic coupling between the flux lines and the pinning centers along grain boundaries and partly inside the grains. This case was also correlated to the equality between flux entry and exit along the YBCO/Ag sample during regular oscillations. It was shown that the voltage oscillations can be described well by an empirical expression V (t) sin(wt + φ) . We found that the phase angle φgenerally takes different values for the repetitive oscillations. Fast Fourier Transform analysis of the V - t oscillations showed that the oscillation period is comparable to that (PI) of the BSW current. This finding suggests a physical mechanism associated with charge density waves (CDWs), and, indeed, the weakly pinned flux line system in YBCO/Ag resembles the general behavior of CDWs. At certain values of PI, amplitude of BSW current, H and T, the YBCO/Ag sample behaves like a double-integrator, since it converts the BSW current to sinusoidal voltage oscillations in time.

  7. Simulation of YBCO Tape and Coils in HTS Maglev System

    Directory of Open Access Journals (Sweden)

    Song Mengxiao

    2017-01-01

    Full Text Available In the process of running high temperature superconducting maglev train, the AC(Alternating Current loss of superconducting coil is directly related to its safe operation and operating cost. In this paper, the simulation model was built based on the finite element software COMSOL Multiphysics, and mainly simulated and calculated the AC losses of YBCO(Yttrium Barium Copper Oxide tape and coils. In this model, as the solving object, the singular and infinite long YBCO tape and coils model was solved with H-formulation and the nonlinear characteristic (E-J constitutive law and anisotrophy (B-J characteristic were taken into consideration as the theoretical foundation. Then on the basis of the model under maglev suspension system, AC losses under different amplitude and frequence AC currents were calculated. The results shows that under different frequencies and dynamic components, the local maximum AC loss of YBCO tape and coils occurs when the steady-state DC(Direct Current current is 30A. Then comparing with old maglev suspension system, the new system can greatly reduce the energy consumption and the material cost.

  8. Irreversible properties of YBCO coated conductors

    International Nuclear Information System (INIS)

    Vostner, A.

    2001-02-01

    Over the past few years substantial efforts were made to optimize the fabrication techniques of various high temperature superconductors for commercial applications. In addition to Bi-2223 tapes, Y-123 coated conductors have the potential for large-scale production and are considered as the second generation of superconducting 'wires' for high current applications. This work reports on magnetic and transport current investigations of Y-123 thick films deposited on either single crystalline substrates by liquid phase epitaxy (LPE) or on metallic substrates by pulsed laser deposition (PLD). At the beginning, a short introduction of the general idea of a coated conductor and of the different production techniques is presented, followed by a description of the different experimental set-ups and the evaluation methods. The main part starts with the results obtained from SQUID magnetometry and ac-susceptibility measurements including the transition temperatures T c , the field dependence of the magnetic critical current densities and the irreversibility lines. In addition, some issues concerning the granular structure and the inter- and intragranular current distribution of the superconducting films are discussed. The investigations by transport currents are focused on the behavior of the application relevant irreversible parameters. These are the angular and the field dependence of the critical transport current densities at 77 and 60 K, as well as the temperature dependence of the irreversibility fields up to 6 T. To gain more insight into the defect structure of the films, neutron irradiation studies were performed on some samples. The introduction of these artificial pinning centers causes large enhancements of the magnetic J c in LPE specimens for the field parallel to the c-axis (H//c) at higher temperatures and magnetic fields. The granular structure of the samples does not change up to the highest neutron fluences. However, the enhancements of the transport J c

  9. Large-scale HTS bulks for magnetic application

    Science.gov (United States)

    Werfel, Frank N.; Floegel-Delor, Uta; Riedel, Thomas; Goebel, Bernd; Rothfeld, Rolf; Schirrmeister, Peter; Wippich, Dieter

    2013-01-01

    ATZ Company has constructed about 130 HTS magnet systems using high-Tc bulk magnets. A key feature in scaling-up is the fabrication of YBCO melts textured multi-seeded large bulks with three to eight seeds. Except of levitation, magnetization, trapped field and hysteresis, we review system engineering parameters of HTS magnetic linear and rotational bearings like compactness, cryogenics, power density, efficiency and robust construction. We examine mobile compact YBCO bulk magnet platforms cooled with LN2 and Stirling cryo-cooler for demonstrator use. Compact cryostats for Maglev train operation contain 24 pieces of 3-seed bulks and can levitate 2500-3000 N at 10 mm above a permanent magnet (PM) track. The effective magnetic distance of the thermally insulated bulks is 2 mm only; the stored 2.5 l LN2 allows more than 24 h operation without refilling. 34 HTS Maglev vacuum cryostats are manufactured tested and operate in Germany, China and Brazil. The magnetic levitation load to weight ratio is more than 15, and by group assembling the HTS cryostats under vehicles up to 5 t total loads levitated above a magnetic track is achieved.

  10. AC loss in YBCO coated conductors at high dB/dt measured using a spinning magnet calorimeter (stator testbed environment)

    Science.gov (United States)

    Murphy, J. P.; Gheorghiu, N. N.; Bullard, T.; Haugan, T.; Sumption, M. D.; Majoros, M.; Collings, E. W.

    2017-09-01

    A new facility for the measurement of AC loss in superconductors at high dB/dt has been developed. The test device has a spinning rotor consisting of permanent magnets arranged in a Halbach array; the sample, positioned outside of this, is exposed to a time varying AC field with a peak radial field of 0.566 T. At a rotor speed of 3600 RPM the frequency of the AC field is 240 Hz, the radial dB/dt is 543 T/s and the tangential dB/dt is 249 T/s. Loss is measured using nitrogen boiloff from a double wall calorimeter feeding a gas flow meter. The system is calibrated using power from a known resistor. YBCO tape losses were measured in the new device and compared to the results from a solenoidal magnet AC loss system measurement of the same samples (in this latter case measurements were limited to a field of amplitude 0.1 T and a dB/dt of 100 T/s). Solenoidal magnet system AC loss measurements taken on a YBCO sample agreed with the Brandt loss expression associated with a 0-0.1 T Ic of 128 A. Subsequently, losses for two more YBCO tapes nominally identical to the first were individually measured in this spinning magnet calorimeter (SMC) machine with a Bmax of 0.566 T and dB/dt of up to 272 T/s. The losses, compared to a simplified version of the Brandt expression, were consistent with the average Ic expected for the tape in the 0-0.5 T range at 77 K. The eddy current contribution was consistent with a 77 K residual resistance ratio, RR, of 4.0. The SMC results for these samples agreed to within 5%. Good agreement was also obtained between the results of the SMC AC loss measurement and the solenoidal magnet AC loss measurement on the same samples.

  11. Fermi-surface reconstruction by stripe order in cuprate superconductors

    Science.gov (United States)

    Laliberté, Francis

    2012-02-01

    The origin of pairing in a superconductor resides in the underlying normal state. In the cuprate high-temperature superconductor YBCO, application of a magnetic field to suppress superconductivity reveals a ground state that appears to break the translational symmetry of the lattice, pointing to some density-wave order [1,2,3]. In another cuprate, Eu-LSCO, the onset of stripe order - a modulation of spin and charge densities - at low temperature is well established [4]. By a comparative study of thermoelectric transport in the cuprates YBCO and Eu-LSCO, we show that the two materials exhibit a very similar process of Fermi-surface reconstruction as a function of temperature and doping [5,6]. This strongly suggests that Fermi-surface reconstruction is caused by stripe order in both cases, compelling evidence that stripe order is a generic tendency of hole-doped cuprates.[4pt] Work done in collaboration with J. Chang, N. Doiron-Leyraud, E. Hassinger, R. Daou, D. LeBoeuf, M. Rondeau, B. J. Ramshaw, R. Liang, D. A. Bonn, W. N. Hardy, S. Pyon, T. Takayama, H. Takagi, I. Sheikin, L. Malone, C. Proust, K. Behnia and L. Taillefer.[4pt] [1] N. Doiron-Leyraud et al., Nature 447, 565 (2007).[0pt] [2] D. LeBoeuf et al., Nature 450, 533 (2007).[0pt] [3] D. LeBoeuf et al., Phys. Rev. B 83, 054506 (2011).[0pt] [4] J. Fink et al., Phys. Rev. B 83, 092503 (2011).[0pt] [5] J. Chang et al., Phys. Rev. Lett. 104, 057005 (2010).[0pt] [6] F. Lalibert'e et al., Nat. Commun. 2, 432 (2011).

  12. Superconductors with excess quasiparticles

    International Nuclear Information System (INIS)

    Elesin, V.F.; Kopaev, Y.V.

    1981-01-01

    This review presents a systematic kinetic theory of nonequilibrium phenomena in superconductors with excess quasiparticles created by electromagnetic or tunnel injection. The energy distributions of excess quasiparticles and of nonequilibrium phonons, dependence of the order parameter on the power and frequency (or intensity) of the electromagnetic field, magnetic properties of nonequilibrium superconductors, I-V curves of superconductor-insulator-superconductor junctions, and other properties are described in detail. The stability of superconducting states far from thermodynamic equilibrium is investigated and it is shown that characteristic instabilities leading to the formation of nonuniform states of a new type or phase transitions of the first kind are inherent to superconductors with excess quasiparticles. The results are compared with experimental data

  13. An improved FEM model for computing transport AC loss in coils made of RABiTS YBCO coated conductors for electric machines

    International Nuclear Information System (INIS)

    Ainslie, Mark D; Yuan Weijia; Flack, Timothy J; Coombs, Timothy A; Rodriguez-Zermeno, Victor M; Hong Zhiyong

    2011-01-01

    AC loss can be a significant problem for any applications that utilize or produce an AC current or magnetic field, such as an electric machine. The authors investigate the electromagnetic properties of high temperature superconductors with a particular focus on the AC loss in superconducting coils made from YBCO coated conductors for use in an all-superconducting electric machine. This paper presents an improved 2D finite element model for the cross-section of such coils, based on the H formulation. The model is used to calculate the transport AC loss of a racetrack-shaped coil using constant and magnetic field-dependent critical current densities, and the inclusion and exclusion of a magnetic substrate, as found in RABiTS (rolling-assisted biaxially textured substrate) YBCO coated conductors. The coil model is based on the superconducting stator coils used in the University of Cambridge EPEC Superconductivity Group's all-superconducting permanent magnet synchronous motor design. To validate the modeling results, the transport AC loss of a stator coil is measured using an electrical method based on inductive compensation by means of a variable mutual inductance. Finally, the implications of the findings on the performance of the motor are discussed.

  14. An improved FEM model for computing transport AC loss in coils made of RABiTS YBCO coated conductors for electric machines

    Energy Technology Data Exchange (ETDEWEB)

    Ainslie, Mark D; Yuan Weijia; Flack, Timothy J; Coombs, Timothy A [Department of Engineering, University of Cambridge, 9 J J Thomson Avenue, Cambridge CB3 0FA (United Kingdom); Rodriguez-Zermeno, Victor M [Department of Mathematics, Technical University of Denmark, Kongens Lyngby 2800 (Denmark); Hong Zhiyong, E-mail: mda36@cam.ac.uk [School of Electronic, Information and Electrical Engineering, Shanghai Jiao Tong University, Shanghai (China)

    2011-04-15

    AC loss can be a significant problem for any applications that utilize or produce an AC current or magnetic field, such as an electric machine. The authors investigate the electromagnetic properties of high temperature superconductors with a particular focus on the AC loss in superconducting coils made from YBCO coated conductors for use in an all-superconducting electric machine. This paper presents an improved 2D finite element model for the cross-section of such coils, based on the H formulation. The model is used to calculate the transport AC loss of a racetrack-shaped coil using constant and magnetic field-dependent critical current densities, and the inclusion and exclusion of a magnetic substrate, as found in RABiTS (rolling-assisted biaxially textured substrate) YBCO coated conductors. The coil model is based on the superconducting stator coils used in the University of Cambridge EPEC Superconductivity Group's all-superconducting permanent magnet synchronous motor design. To validate the modeling results, the transport AC loss of a stator coil is measured using an electrical method based on inductive compensation by means of a variable mutual inductance. Finally, the implications of the findings on the performance of the motor are discussed.

  15. Protection of the 6 T YBCO insert in the 13 T Nb$_{3}$Sn Fresca II dipole

    CERN Document Server

    Stenvall, A.; Fazilleau, Ph.; Devaux, M.; Durante, M.; Lecrevisse, T.; Rey, J. -M.; Fleiter, J.; Sorbi, M.; Volpini, G.; Tixador, P.

    2013-01-01

    In the EuCARD project, we aim to construct a dipole magnet in YBCO producing 6 T in the background field of a 13 T Nb$_{3}$Sn dipole FRESCA II. This paper reviews the quench analysis and protection of the YBCO coil. In addition, a recommendation for the protection system of the YBCO coil is presented.

  16. Fabrication of high temperature superconductors

    Science.gov (United States)

    Balachandran, Uthamalingam; Dorris, Stephen E.; Ma, Beihai; Li, Meiya

    2003-06-17

    A method of forming a biaxially aligned superconductor on a non-biaxially aligned substrate substantially chemically inert to the biaxially aligned superconductor comprising is disclosed. A non-biaxially aligned substrate chemically inert to the superconductor is provided and a biaxially aligned superconductor material is deposited directly on the non-biaxially aligned substrate. A method forming a plume of superconductor material and contacting the plume and the non-biaxially aligned substrate at an angle greater than 0.degree. and less than 90.degree. to deposit a biaxially aligned superconductor on the non-biaxially aligned substrate is also disclosed. Various superconductors and substrates are illustrated.

  17. Pre-fabricated nanorods in RE–Ba–Cu–O superconductors

    International Nuclear Information System (INIS)

    Khatri, N D; Majkic, G; Shi, T; Selvamanickam, V; Chen, Y

    2013-01-01

    Pre-fabrication of metallic nanorods on biaxially textured templates has been explored in this study to introduce flux pinning centers in RE–Ba–Cu–O (REBCO, RE =rare earth) based superconductors. Pt nanorods were deposited by an electron beam assisted deposition method on LaMnO 3 -capped biaxially textured IBAD-(ion beam assisted deposition) substrates. Well-controlled nanorods with varying diameter (50–120 nm), length (up to 1 μm), orientation and unit cell size were grown over an area of 120–150 μm 2 . The nanorod-decorated samples were then deposited with Gd–Y–Ba–Cu–O ((Gd, Y)BCO) by metal organic chemical vapor deposition (MOCVD). The Pt nanorods remain in their positions during MOCVD and become embedded in the (Gd, Y)BCO matrix, although they suffer creep-induced shape deformation due to exposure to elevated temperature. Higher unit cell size, longer nanorods, and nanorods oriented at an angle to the substrate normal adversely affect the epitaxy of the (Gd, Y)BCO film due to formation of a-axis grains. The observed current-carrying capacity of the Pt nanorod sample is lower than its corresponding reference sample without any nanorods and processed under identical conditions, but it decreases at a slower rate with increasing magnetic field. Potential routes to improve the performance while retaining the desirable characteristics of controlled nanorod direction and density are discussed. (paper)

  18. Microstructure and critical current density in high-Tc metal oxide superconductors

    International Nuclear Information System (INIS)

    Johnson, S.M.; Gusman, M.I.

    1992-03-01

    Superconductor powders in the U-Ba-Cu-O (YBCO) and Bi-Pb-Sr-Ca-Cu-O (BSCCO) systems were synthesized by freeze-drying. Powders were characterized, and processed into samples for evaluation of superconducting behavior. Freeze-drying is attractive because the powders have high purity, are homogeneous, have a small size and are active. YBCO powders can be sintered to high density at 890 degrees C. Many compositions, processing approaches and heat treatments were explored in an effort to understand relations between microstructure and critical density, and to improve the critical current density. Powders were also formed into sputtering targets for coating preparation at Stanford University. The highest critical current density achieved with the YBCO powders was ∼15,000 A/cm 2 at 4.2K and 0.5T using powders treated to prevent carbon contamination. The BSCCO materials with the highest critical current density, ∼30,000 A/cm 2 at the same conditions were formed by heat treating melted and quenched samples. All critical current density measurements were made by Stanford University, a subcontractor to this effort. Stanford University also prepared coatings by off-axis magnetron sputtering

  19. Advanced magneto-optical Kerr effect measurements of superconductors at low temperatures

    Directory of Open Access Journals (Sweden)

    Claudia Stahl

    2017-10-01

    Full Text Available Magneto-optical Kerr-effect (MOKE measurements of superconducting films with soft-magnetic coatings are performed at low temperatures using a laser-based MOKE set-up. An elaborate measurement scheme with internal reference allows the quantitative comparison of the temperature dependent Kerr-amplitude with the magnetic field generated by supercurrents. For this purpose, an amorphous CoFeB thin film exhibiting a large Kerr-signal is deposited directly on top of the YBCO superconductor acting as field sensing layer. It is shown that the resulting magnetic hysteresis loops of the soft-magnetic film can be used to reconstruct the electric properties of the superconductor.

  20. Deformation of high-temperature superconductors

    International Nuclear Information System (INIS)

    Goretta, K.C.; Routbort, J.L.; Miller, D.J.; Chen, N.; Dominguez-Rodriguez, A.; Jimenez-Melendo, M.; De Arellano-Lopez, A.R.

    1994-08-01

    Of the many families of high-temperature superconductors, only the properties of those discovered prior to 1989 - Y-Ba-Cu-O, Tl-Ba(Sr)-Ca-Cu-O, and Bi(Pb)-Sr-Ca-Cu-O - have been studied extensively. Deformation tests have been performed on YBa 2 Cu 3 O x (Y-123), YBa 2 Cu 4 O x (Y-124), TlBa 2 Ca 2 Cu 3 O x (Bi-2223). The tests have revealed that plasticity is generally limited in these compounds and that the rate-controlling diffusional kinetics for creep are very slow. Nevertheless, hot forming has proved to be quite successful for fabrication of bulk high-temperature superconductors, so long as deformation rates are low or large hydrostatic stresses are applied. Steady-state creep data have proved to be useful in designing optimal heat treatments for superconductors and in support of more-fundamental diffusion experiments. The high-temperature superconductors are highly complex oxides, and it is a challenge to understand their deformation responses. In this paper, results of interest and operant creep mechanisms will be reviewed

  1. Deposition studies and coordinated characterization of MOCVD YBCO films on IBAD-MgO templates

    International Nuclear Information System (INIS)

    Aytug, T; Paranthaman, M; Heatherly, L; Zuev, Y; Zhang, Y; Kim, K; Goyal, A; Maroni, V A; Chen, Y; Selvamanickam, V

    2009-01-01

    A recently installed research-scale metal-organic chemical vapor deposition (MOCVD) system at Oak Ridge National Laboratory, provided by SuperPower, Inc., has been used to investigate processing variables for MOCVD YBCO precursors and trends in the resulting properties. Systematic studies of YBCO film growth on LaMnO 3 /IBAD-MgO templates were carried out by optimizing deposition temperature and oxygen flow rate. Microstructural and superconducting properties of the YBCO films were analyzed by x-ray diffraction, scanning electron microscopy and transport measurements. The identification of intermediate phases formed during the YBCO precursor transformation was investigated by coordinated reel-to-reel Raman microprobe analysis. With this combination of various characterization techniques, an improved understanding of the growth characteristics of MOCVD YBCO films was established. Finally, critical current densities greater than 2 MA cm -2 for film thicknesses of 0.8 μm were demonstrated.

  2. Deposition studies and coordinated characterization of MOCVD YBCO films on IBAD-MgO templates

    Energy Technology Data Exchange (ETDEWEB)

    Aytug, T; Paranthaman, M [Oak Ridge National Laboratory, Chemical Sciences Division, Oak Ridge, TN 37831 (United States); Heatherly, L; Zuev, Y; Zhang, Y; Kim, K; Goyal, A [Oak Ridge National Laboratory, Materials Science and Technology Division, Oak Ridge, TN 37831 (United States); Maroni, V A [Argonne National Laboratory, Chemical Sciences and Engineering Division, Argonne, IL 60439 (United States); Chen, Y; Selvamanickam, V [SuperPower, Incorporated, 450 Duane Avenue, Schenectady, NY 12304 (United States)], E-mail: aytugt@ornl.gov

    2009-01-15

    A recently installed research-scale metal-organic chemical vapor deposition (MOCVD) system at Oak Ridge National Laboratory, provided by SuperPower, Inc., has been used to investigate processing variables for MOCVD YBCO precursors and trends in the resulting properties. Systematic studies of YBCO film growth on LaMnO{sub 3}/IBAD-MgO templates were carried out by optimizing deposition temperature and oxygen flow rate. Microstructural and superconducting properties of the YBCO films were analyzed by x-ray diffraction, scanning electron microscopy and transport measurements. The identification of intermediate phases formed during the YBCO precursor transformation was investigated by coordinated reel-to-reel Raman microprobe analysis. With this combination of various characterization techniques, an improved understanding of the growth characteristics of MOCVD YBCO films was established. Finally, critical current densities greater than 2 MA cm{sup -2} for film thicknesses of 0.8 {mu}m were demonstrated.

  3. Preparation and structural properties of YBCO films grown on GaN/c-sapphire hexagonal substrate

    Energy Technology Data Exchange (ETDEWEB)

    Chromik, S., E-mail: stefan.chromik@savba.sk [Institute of Electrical Engineering, SAS, Dubravska cesta 9, 84104 Bratislava (Slovakia); Gierlowski, P. [Institute of Physics, Polish Academy of Sciences, Al. Lotnikow 32/46, 02-668 Warsaw (Poland); Spankova, M.; Dobrocka, E.; Vavra, I.; Strbik, V.; Lalinsky, T.; Sojkova, M. [Institute of Electrical Engineering, SAS, Dubravska cesta 9, 84104 Bratislava (Slovakia); Liday, J.; Vogrincic, P. [Department of Microelectronics, Slovak Technical University, Ilkovicova 3, 81219 Bratislava (Slovakia); Espinos, J.P. [Instituto de Ciencia de Materiales de Sevilla, Avda Americo Vespucio 49, 41092 Sevilla (Spain)

    2010-07-01

    Epitaxial YBCO thin films have been grown on hexagonal GaN/c-sapphire substrates using DC magnetron sputtering and pulsed laser deposition. An MgO buffer layer has been inserted between the substrate and the YBCO film as a diffusion barrier. X-ray diffraction analysis indicates a c-axis oriented growth of the YBCO films. {Phi}-scan shows surprisingly twelve maxima. Transmission electron microscopy analyses confirm an epitaxial growth of the YBCO blocks with a superposition of three a-b YBCO planes rotated by 120 deg. to each other. Auger electron spectroscopy and X-ray photoelectron spectroscopy reveal no surface contamination with Ga even if a maximum substrate temperature of 700 deg. C is applied.

  4. Characterization and properties of batch-processed melt-textured YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Kaiser, A.W.; Adam, M.; Bornemann, H.J. [INFP, Forschungszentrum Karlsruhe GmbH, PO Box 3640, 76021 Karlsruhe (Germany)

    1998-01-01

    High-temperature superconductor bulk parts are batch processed using a semi-automated processing technique based on the melt-texturation process. Levitation properties under static and dynamic load levels were analysed using a test bench with a three-dimensional force sensor unit. Measurements of levitation force give no detailed suggestions on texture, secondary domains or cracks. Therefore other measurements to control homogeneity of the bulk were performed. Texture on full-size pellets (FWHM < 5 deg., {delta}{sub {chi}} < 3 deg.) was verified by elastic neutron scattering. To study the influence of local texture on properties a pellet was divided into nine segments. Preliminary results indicate that a correlation between neutron data and levitation force needs further investigations. Flux maps of samples magnetized by permanent magnets or by a pulsed magnetization unit were used to verify the homogeneity and domain structure of the material and to evaluate macroscopic critical currents. (author)

  5. Atomic hydrogen effects on high-Tc superconductors

    International Nuclear Information System (INIS)

    Frantskevich, N.V.; Ulyashin, A.G.; Alifanov, A.V.; Stepanenko, A.V.; Fedotova, V.V.

    1999-01-01

    The atomic hydrogen effects on the properties of bulk high-temperature superconductors were investigated. It is shown that the insertion of the atomic hydrogen into the bulk of these materials from a DC plasma leads to the increase of the critical current density J c for YBaCuO(123) as well as for BiSrCaCuO(2223) high-temperature superconductors. It is found that the hydrogenation of the He implanted samples with following annealing leads to the optically detected blistering on the surface. It means that the textured thin subsurface layers of high-temperature superconductors can be formed by this method. The improvement of superconductivity by atomic hydrogen can be explained by the passivation of dangling bonds and defects on grain boundaries of these materials

  6. Effective Ginzburg–Landau free energy functional for multi-band isotropic superconductors

    International Nuclear Information System (INIS)

    Grigorishin, Konstantin V.

    2016-01-01

    Highlights: • The intergradient coupling of order parameters in a two-band superconductor plays important role and cannot be neglected. • A two-band superconductor must be characterized with a single coherence length and a single Ginzburg–Landau parameter. • Type-1.5 superconductors are impossible. • The free energy functional for a multi-band superconductor can be reduced to the effective single-band Ginzburg–Landau functional. - Abstract: It has been shown that interband mixing of gradients of two order parameters (drag effect) in an isotropic bulk two-band superconductor plays important role – such a quantity of the intergradients coupling exists that the two-band superconductor is characterized with a single coherence length and a single Ginzburg–Landau (GL) parameter. Other quantities or neglecting of the drag effect lead to existence of two coherence lengths and dynamical instability due to violation of the phase relations between the order parameters. Thus so-called type-1.5 superconductors are impossible. An approximate method for solving of set of GL equations for a multi-band superconductor has been developed: using the result about the drag effect it has been shown that the free-energy functional for a multi-band superconductor can be reduced to the GL functional for an effective single-band superconductor.

  7. Electronic structure and superconductivity of FeSe-related superconductors.

    Science.gov (United States)

    Liu, Xu; Zhao, Lin; He, Shaolong; He, Junfeng; Liu, Defa; Mou, Daixiang; Shen, Bing; Hu, Yong; Huang, Jianwei; Zhou, X J

    2015-05-13

    FeSe superconductors and their related systems have attracted much attention in the study of iron-based superconductors owing to their simple crystal structure and peculiar electronic and physical properties. The bulk FeSe superconductor has a superconducting transition temperature (Tc) of ~8 K and it can be dramatically enhanced to 37 K at high pressure. On the other hand, its cousin system, FeTe, possesses a unique antiferromagnetic ground state but is non-superconducting. Substitution of Se with Te in the FeSe superconductor results in an enhancement of Tc up to 14.5 K and superconductivity can persist over a large composition range in the Fe(Se,Te) system. Intercalation of the FeSe superconductor leads to the discovery of the AxFe2-ySe2 (A = K, Cs and Tl) system that exhibits a Tc higher than 30 K and a unique electronic structure of the superconducting phase. A recent report of possible high temperature superconductivity in single-layer FeSe/SrTiO3 films with a Tc above 65 K has generated much excitement in the community. This pioneering work opens a door for interface superconductivity to explore for high Tc superconductors. The distinct electronic structure and superconducting gap, layer-dependent behavior and insulator-superconductor transition of the FeSe/SrTiO3 films provide critical information in understanding the superconductivity mechanism of iron-based superconductors. In this paper, we present a brief review of the investigation of the electronic structure and superconductivity of the FeSe superconductor and related systems, with a particular focus on the FeSe films.

  8. Neutron-diffraction investigations of flux-lines in superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Forgan, E M [Birmingham Univ. (United Kingdom); Lee, S L [Saint Andrews Univ. (United Kingdom); McKPaul, D [Warwick Univ., Coventry (United Kingdom); Mook, H A [Oak Ridge National Lab., TN (United States); Cubitt, R [Institut Max von Laue - Paul Langevin (ILL), 38 - Grenoble (France)

    1997-04-01

    SANS has proved an extremely useful tool for investigating flux-line structures within the bulk of superconductors. With high-T{sub c} materials, the scattered intensities are weak, but careful measurements are giving important new information about flux lattices, flux pinning and flux-lattice melting. (author). 10 refs.

  9. Friction in levitated superconductors

    International Nuclear Information System (INIS)

    Brandt, E.H.

    1988-01-01

    A type I superconductor levitated above a magnet of low symmetry has a unique equilibrium position about which it may oscillate freely. In contrast, a type II superconductor has a continuous range of stable equilibrium positions and orientations where it floats rigidly without swinging or orbiting as if it were stuck in sand. A strong internal friction conspicuously indicates the existence and unpinning of flux lines in oxide superconductors levitated above liquid nitrogen. It is shown how these effects follow from the hysteretic magnetization curves and how the energy is dissipated

  10. Preparing superconducting nanopowder based YBCO/Ag tapes

    DEFF Research Database (Denmark)

    Paturi, P.; Raittila, J.; Grivel, J.C.

    2002-01-01

    YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also...... carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved....

  11. Magnetic response of superconducting mesoscopic-size YBCO powder

    Energy Technology Data Exchange (ETDEWEB)

    Deimling, C.V. [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos, SP (Brazil)], E-mail: cesard@df.ufscar.br; Motta, M.; Lisboa-Filho, P.N. [Laboratorio de Materiais Supercondutores, Departamento de Fisica, Universidade Estadual Paulista, Bauru, SP Brazil (Brazil); Ortiz, W.A. [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos, SP (Brazil)

    2008-07-15

    In this work it is reported the magnetic behavior of submicron and mesoscopic-size superconducting YBCO powders, prepared by a modified polymeric precursors method. The grain size and microstructure were analyzed using scanning electron microscopy (SEM). Measurements of magnetization and AC-susceptibility as a function of temperature were performed with a quantum design SQUID magnetometer. Our results indicated significant differences on the magnetic propreties, in connection with the calcination temperature and the pressure used to pelletize the samples. This contribution is part of an effort to study vortex dynamics and magnetic properties of submicron and mesoscopic-size superconducting samples.

  12. Harmonic response of coupled and uncoupled granular YBCO

    International Nuclear Information System (INIS)

    Torralba, Maria Veronica S; Sarmago, Roland V

    2004-01-01

    The harmonic responses of granular YBCO were obtained via mutual inductance measurements. Two samples, one with and another without intergranular coupling, were investigated in terms of the harmonic components of magnetization at various field amplitudes and frequencies. By comparing the behaviour of the features in the harmonics to that of the peaks in the fundamental response, we explicitly identified which features in the harmonics originate from intragranular harmonic generation and which arise due to a contribution of intergranular coupling. Harmonic responses were obtained despite the absence of vortices and even harmonics were detected in a purely AC magnetic field

  13. Reply to the ''Comment on 'Observation of trapped O2 in high-Tc metal oxide superconductors' ''

    International Nuclear Information System (INIS)

    Chen, C.H.; Phillips, R.C.; Payne, M.G.

    1990-01-01

    Desorption of O 2 in certain high-T c superconductors was observed from scraping the surfaces of superconductors by Rosenberg and Wen. Their conclusion agrees with the results from the observation of O 2 trapping by a laser ablation of superconductors. However, the local heating due to the scraping process can possibly raise the local surface temperature significantly higher than the temperature of the bulk

  14. Static Properties of Superconductor Journal Bearing Substator for Superconductor Flywheel Energy Storage System

    International Nuclear Information System (INIS)

    Park, B. J.; Jung, S. Y.; Lee, J. P.; Park, B. C.; Jeong, N. H.; Sung, T. H.; Han, Y. H.

    2008-01-01

    A Superconductor Flywheel Energy Storage System(SFES) mainly consists of a pair of non-contacting High Temperature Superconductor(HTS) bearings that provide very low frictional losses, a composite flywheel with high energy storage density. The HTS bearings, which offer dynamic stability without active control, are the key technology that distinguishes the SFES from other flywheel energy storage devices, and great effort is being put into developing this technology. The Superconductor Journal Bearing(SJB) mainly consists of HTS bulks and a stator, which holds the HTS bulks and also acts as a cold head. Static properties of HTS bearings provide data to solve problems which may occur easily in a running system. Since stiffness to counter vibration is the main parameter in designing an HTS bearing system, we investigate SJB magnetic force through static properties between the Permanent Magnet(PM) and HTS. We measure stiffness in static condition and the results are used to determine the optimal number of HTS bulks for a 100kWh SFES.

  15. Bi axially textured YBCO coated tape prepared using dynamic magnetic grain alignment

    International Nuclear Information System (INIS)

    Genoud, Jean-Yves; Quinton, William

    1999-01-01

    A new magnetic grain alignment technique has been applied to produce bi axially aligned YBCO coated tapes. A bi axially aligned dispersion of orthorhombic Y 2 Ba 4 Cu 7 O 15 (Y-247) powder was settled on un textured silver substrates. The Y-247 tapes were then melt processed to achieve high critical current YBa 2 Cu 3 O 7 (Y-123) tapes with CuO as a secondary phase. The biaxial alignment is preserved after the densification process and a clear enhancement of J c relative to identically prepared un textured or uniaxially textured samples is obtained. Critical current densities of up to 5000 A cm -2 at 77 K in self-field and 1500 A cm -2 in 0.5 T magnetic field at 65 K were obtained in films from 20 to 40 μm thick. Problems were experienced in achieving fully densified thick films while retaining biaxial texture. The initial grain size distribution was found to have a major influence on the final microstructure. Provided significant improvements in J c can be obtained this method offers an alternative to coated tape processes based on epitaxial growth which has the advantage that it does not require textured substrates. The biaxial alignment technique described here intrinsically acts on the bulk material rather than at surfaces. This offers the possibility of texturing without thickness limitations. (author)

  16. Fabrication of single-grain GdBa 2 Cu 3 O 7− bulk ...

    Indian Academy of Sciences (India)

    Research Articles Volume 74 Issue 5 May 2010 pp 827-832 ... Superconductors; top seeded infiltration and growth process; GdBa2 ... The morphology, microstructure and levitation force of the bulk GdBCO have also been investigated.

  17. Critical current enhancement in high Tc superconductors

    International Nuclear Information System (INIS)

    Jin, S.; Graebner, J.E.; Tiefel, T.H.

    1990-01-01

    Progress toward major technological applications of the bulk, high T c superconductors has been hindered by two major barriers, i.e., the Josephson weak-links at grain boundaries and the lack of sufficient intragrain flux pinning. It has been demonstrated that the weak link problem can be overcome by extreme alignment of grains such as in melt-textured-growth (MTG) materials. Modified or improved processing by various laboratories has produced further increased critical currents. However, the insufficient flux pinning seems to limit the critical current density in high fields to about 10 4 --10 5 A/cm 2 at 77K, which is not satisfactory for many applications. In this paper, processing, microstructure, and critical current behavior of the MTG type superconductors are described, and various processing possibilities for flux pinning enhancement are discussed

  18. Kohn anomalies in superconductors

    International Nuclear Information System (INIS)

    Flatte, M.E.

    1994-01-01

    The detailed behavior of phonon dispersion curves near momenta which span the electronic Fermi sea in a superconductor is presented. An anomaly, similar to the metallic Kohn anomaly, exists in a superconductor's dispersion curves when the frequency of the photon spanning the Fermi sea exceeds twice the superconducting energy gap. This anomaly occurs at approximately the same momentum but is stronger than the normal-state Kohn anomaly. It also survives at finite temperature, unlike the metallic anomaly. Determination of Fermi-surface diameters from the location of these anomalies, therefore, may be more successful in the superconducting phase than in the normal state. However, the superconductor's anomaly fades rapidly with increased phonon frequency and becomes unobservable when the phonon frequency greatly exceeds the gap. This constraint makes these anomalies useful only in high-temperature superconductors such as La 1.85 Sr 0.15 CuO 4

  19. Topological superconductors: a review.

    Science.gov (United States)

    Sato, Masatoshi; Ando, Yoichi

    2017-07-01

    This review elaborates pedagogically on the fundamental concept, basic theory, expected properties, and materials realizations of topological superconductors. The relation between topological superconductivity and Majorana fermions are explained, and the difference between dispersive Majorana fermions and a localized Majorana zero mode is emphasized. A variety of routes to topological superconductivity are explained with an emphasis on the roles of spin-orbit coupling. Present experimental situations and possible signatures of topological superconductivity are summarized with an emphasis on intrinsic topological superconductors.

  20. Room temperature superconductors

    International Nuclear Information System (INIS)

    Sleight, A.W.

    1995-01-01

    If the Holy Grail of room temperature superconductivity could be achieved, the impact on could be enormous. However, a useful room temperature superconductor for most applications must possess a T c somewhat above room temperature and must be capable of sustaining superconductivity in the presence of magnetic fields while carrying a significant current load. The authors will return to the subject of just what characteristics one might seek for a compound to be a room temperature superconductor. 30 refs., 3 figs., 1 tab

  1. The new Fe-based superconductors

    International Nuclear Information System (INIS)

    Mao, Zhiqiang

    2011-01-01

    The discovery of unconventional superconductivity in doped iron pnictides has ushered in a new era of high temperature superconductivity. The superconductivity of these materials occurs in close proximity to magnetic instability; superconductivity is achieved by suppressing a long-range antiferromagnetic (AFM) order through charge carrier doping or pressure. In this talk, I will first give a brief overview of the phase diagrams of iron-based superconductors, and then talk about our recent research on iron chalcogenide Fe 1+y (Te 1-x Se x ) superconductors, which is structurally the simplest of the Fe-based superconductors. Although the Fermi surface of iron chalcogenides is similar to iron pnictides, the parent compound Fe 1+y Te exhibits AFM order with in-plane magnetic wave-vector (π, 0). This contrasts the pnictide parent compounds where the magnetic order has an in-plane magnetic wave-vector (π, π) that connects hole and electron parts of the Fermi surface. Despite these differences, both the pnictide and chalcogenide Fe-superconductors exhibit superconducting spin resonances around (π, π), suggesting a common symmetry for their superconducting order parameter. A central question in this burgeoning field is therefore how (π, π) superconductivity can emerge from a (π, 0) magnetic instability. I will address this issue in my talk. I will show the phase diagram of electronic and magnetic properties we recently established for this system and discuss the relationship between magnetic coupling and electronic properties. Our results reveal that the magnetic soft mode evolving from the (π, 0)-type magnetic long-range order is associated with weak charge carrier localization. Bulk superconductivity occurs only as magnetic correlations near (π, 0) are strongly suppressed and the magnetic mode at (π, π) becomes dominant; this suggests a common magnetic origin for superconductivity in iron chalcogenide and pnictide superconductors. (author)

  2. Continuous lengths of oxide superconductors

    Science.gov (United States)

    Kroeger, Donald M.; List, III, Frederick A.

    2000-01-01

    A layered oxide superconductor prepared by depositing a superconductor precursor powder on a continuous length of a first substrate ribbon. A continuous length of a second substrate ribbon is overlaid on the first substrate ribbon. Sufficient pressure is applied to form a bound layered superconductor precursor powder between the first substrate ribbon and the second substrate ribbon. The layered superconductor precursor is then heat treated to establish the oxide superconducting phase. The layered oxide superconductor has a smooth interface between the substrate and the oxide superconductor.

  3. Low ac loss geometries in YBCO coated conductors and impact on conductor stability

    Energy Technology Data Exchange (ETDEWEB)

    Duckworth, Robert C [ORNL; List III, Frederick Alyious [ORNL; Paranthaman, Mariappan Parans [ORNL; Rupich, M. W. [American Superconductor Corporation, Westborough, MA; Zhang, W. [American Superconductor Corporation, Westborough, MA; Xie, Y. Y. [SuperPower Incorporated, Schenectady, New York; Selvamanickam, V. [SuperPower Incorporated, Schenectady, New York

    2007-01-01

    Reduction of ac losses in applied ac fields can be accomplished through either the creation of filaments and bridging in YBCO coated conductors or an assembly of narrow width YBCO tapes. The ac losses for each of these geometries were measured at 77 K in perpendicular ac fields up to 100 mT. While ac loss reduction was achieved with YBCO filaments created through laser scribing and inkjet deposition, the assembly of stacked YBCO conductor provides an alternative method of ac loss reduction. When compared to a 4-mm wide YBCO coated conductor with a critical current of 60 A, the ac loss in a stack of 2-mm wide YBCO coated conductors with a similar total critical current was reduced. While the reduction in ac loss in a 2-mm wide stack coincided with the reduction in the engineering current density of the conductor, further reduction of ac loss was obtained through the splicing of the 2-mm wide tapes with low resistance solders. To better determine the practicality of these methods from a stability point of view, a numerical analysis was carried out to determine the influence of bridging and splicing on stability of a YBCO coated conductor for both liquid nitrogen-cooled and conduction cooled geometries.

  4. Superconducting fault current limiter using high-resistive YBCO tapes

    Energy Technology Data Exchange (ETDEWEB)

    Yazawa, T. [Power and Industrial System R and D Center, Toshiba Corporation, 2-4 Suehiro, Tsurumi, Yokohama 230-0045 (Japan)], E-mail: takashi.yazawa@toshiba.co.jp; Koyanagi, K.; Takahashi, M.; Ono, M.; Toba, K.; Takigami, H.; Urata, M. [Power and Industrial System R and D Center, Toshiba Corporation, 2-4 Suehiro, Tsurumi, Yokohama 230-0045 (Japan); Iijima, Y.; Saito, T. [Fujikura Ltd., 1-5-1 Kiba, Koto, Tokyo 135-0042 (Japan); Ameniya, N. [Yokohama National University, 79-1 Tokiwadai, Hodogaya, Yokohama 240-8501 (Japan); Shiohara, Y. [Superconductivity Research Laboratory, ISTEC, 1-10-13 Shinonome, Koto, Tokyo 135-0062 (Japan)

    2008-09-15

    One of the programs in the Ministry of Economy and Trade and Industry (METI) project regarding R and D on YBCO conductor is to evaluate the applicability of the developed conductor toward several applications. This paper focuses on a fault current limiter (FCL) as one of the expected power applications. YBCO tape conductors with ion beam assisted deposition (IBAD) substrate are used in this work. In order to obtain high resistance of the conductor, which is preferable to an FCL, the thickness of the protecting layer made of silver was decreased as possible. Then high-resistive metal stabilizing layer is attached on the silver layer to improve stability. Obtaining the relevant current limiting performance on short sample experiments, model coils were developed to aim the 6.6 kV-class FCL. Short circuit experiments were implemented with a short circuit generator. The coil successfully restricted the short circuit current over 17 kA to about 700 A by the applied voltage of 3.8 kV, which is nominal phase-to-ground voltage. The experimental results show good agreement with computer analyses and show promising toward the application.

  5. Dynamics of vortex matter in YBCO sub-micron bridges

    Energy Technology Data Exchange (ETDEWEB)

    Papari, G., E-mail: papari@fisica.unina.it [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, I-80126 Napoli (Italy); Carillo, F. [NEST, CNR-NANO and Scuola Normale Superiore, Piazza San Silvestro 12, 56127 Pisa (Italy); Stornaiuolo, D.; Massarotti, D. [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, I-80126 Napoli (Italy); CNR-SPIN UOS Napoli, Complesso Universitario di Monte SantAngelo, via Cinthia, 80126 Napoli (Italy); Longobardi, L. [American Physical Society, 1 Research Road, Ridge, NY 11961 (United States); Beltram, F. [NEST, CNR-NANO and Scuola Normale Superiore, Piazza San Silvestro 12, 56127 Pisa (Italy); Tafuri, F. [CNR-SPIN UOS Napoli, Complesso Universitario di Monte SantAngelo, via Cinthia, 80126 Napoli (Italy); Dipartimento di Ingegneria Industriale e dell' informazione, Seconda Universit‘a di Napoli, via Roma 29, 81031 Aversa (CE) (Italy)

    2014-11-15

    Highlights: • Superconducting properties of YBCO nanowires in the width range ξYBCO nanowires displaying robust superconductivity at widths w as low as 160 nm. We can modify the process in order to maintain a Au protective layer. This allows us to scale our nanowires even further to widths as low as 50 nm. We have studied how the presence of vortices and the occurrence of phase slips affect the transport properties of nanowires in the width range ξ

  6. Low temperature X-ray imaging of magnetic flux patterns in high temperature superconductors

    Science.gov (United States)

    Stahl, Claudia; Ruoß, Stephen; Weigand, Markus; Bechtel, Michael; Schütz, Gisela; Albrecht, Joachim

    2015-05-01

    We present X-ray magnetic circular dichroism (XMCD) microscopy results obtained at liquid nitrogen temperatures on the high-Tc superconductor YBCO (YBa2Cu3O7-δ). The magnetic flux distribution arising from electric currents in the superconductor is detected and visualized using soft-magnetic Co40Fe40B20 (CoFeB) as sensor layer and XMCD as contrast mechanism. It has been shown that the XMCD contrast in the sensor layer directly corresponds to magnetic flux distribution of the superconductor and hence can be used to image magnetic structures in superconductors [Stahl et al., Phys. Rev. B 90, 104515 (2014)]. The existing scanning UHV X-ray microscopy setup MAXYMUS at the synchrotron BESSY II in Berlin has been upgraded for that purpose: we use a nitrogen based MMR Micro Miniature Joule-Thompson Cryostat with temperature range from 75 K to 580 K. The capability of the method is demonstrated on two different superconducting samples, an optimally doped thin film and a melt-textured block.

  7. Correlations Between Magnetic Flux and Levitation Force of HTS Bulk Above a Permanent Magnet Guideway

    Science.gov (United States)

    Huang, Huan; Zheng, Jun; Zheng, Botian; Qian, Nan; Li, Haitao; Li, Jipeng; Deng, Zigang

    2017-10-01

    In order to clarify the correlations between magnetic flux and levitation force of the high-temperature superconducting (HTS) bulk, we measured the magnetic flux density on bottom and top surfaces of a bulk superconductor while vertically moving above a permanent magnet guideway (PMG). The levitation force of the bulk superconductor was measured simultaneously. In this study, the HTS bulk was moved down and up for three times between field-cooling position and working position above the PMG, followed by a relaxation measurement of 300 s at the minimum height position. During the whole processes, the magnetic flux density and levitation force of the bulk superconductor were recorded and collected by a multipoint magnetic field measurement platform and a self-developed maglev measurement system, respectively. The magnetic flux density on the bottom surface reflected the induced field in the superconductor bulk, while on the top, it reveals the penetrated magnetic flux. The results show that the magnetic flux density and levitation force of the bulk superconductor are in direct correlation from the viewpoint of inner supercurrent. In general, this work is instructive for understanding the connection of the magnetic flux density, the inner current density and the levitation behavior of HTS bulk employed in a maglev system. Meanwhile, this magnetic flux density measurement method has enriched present experimental evaluation methods of maglev system.

  8. High temperature superconductor accelerator magnets

    NARCIS (Netherlands)

    van Nugteren, J.

    2016-01-01

    For future particle accelerators bending dipoles are considered with magnetic fields exceeding 20T. This can only be achieved using high temperature superconductors (HTS). These exhibit different properties from classical low temperature superconductors and still require significant research and

  9. Stress analysis in high-temperature superconductors under pulsed field magnetization

    Science.gov (United States)

    Wu, Haowei; Yong, Huadong; Zhou, Youhe

    2018-04-01

    Bulk high-temperature superconductors (HTSs) have a high critical current density and can trap a large magnetic field. When bulk superconductors are magnetized by the pulsed field magnetization (PFM) technique, they are also subjected to a large electromagnetic stress, and the resulting thermal stress may cause cracking of the superconductor due to the brittle nature of the sample. In this paper, based on the H-formulation and the law of heat transfer, we can obtain the distributions of electromagnetic field and temperature, which are in qualitative agreement with experiment. After that, based on the dynamic equilibrium equations, the mechanical response of the bulk superconductor is determined. During the PFM process, the change in temperature has a dramatic effect on the radial and hoop stresses, and the maximum radial and hoop stress are 24.2 {{MPa}} and 22.6 {{MPa}}, respectively. The mechanical responses of a superconductor for different cases are also studied, such as the peak value of the applied field and the size of bulk superconductors. Finally, the stresses are also presented for different magnetization methods.

  10. Entanglement entropy and complexity for one-dimensional holographic superconductors

    Science.gov (United States)

    Kord Zangeneh, Mahdi; Ong, Yen Chin; Wang, Bin

    2017-08-01

    Holographic superconductor is an important arena for holography, as it allows concrete calculations to further understand the dictionary between bulk physics and boundary physics. An important quantity of recent interest is the holographic complexity. Conflicting claims had been made in the literature concerning the behavior of holographic complexity during phase transition. We clarify this issue by performing a numerical study on one-dimensional holographic superconductor. Our investigation shows that holographic complexity does not behave in the same way as holographic entanglement entropy. Nevertheless, the universal terms of both quantities are finite and reflect the phase transition at the same critical temperature.

  11. Ivar Giaever, Tunneling, and Superconductors

    Science.gov (United States)

    dropdown arrow Site Map A-Z Index Menu Synopsis Ivar Giaever, Tunneling, and Superconductors Resources with in Superconductors Measured by Electron Tunneling; Physical Review Letters, Vol. 5 Issue 4: 147 - 148 ; August 15, 1960 Electron Tunneling Between Two Superconductors; Physical Review Letters, Vol. 5 Issue 10

  12. Microgravity Processing of Oxide Superconductors

    Science.gov (United States)

    Olive, James R.; Hofmeister, William H.; Bayuzick, Robert J.; Vlasse, Marcus

    1999-01-01

    Considerable effort has been concentrated on the synthesis and characterization of high T(sub c) oxide superconducting materials. The YBaCuO system has received the most intense study, as this material has shown promise for the application of both thin film and bulk materials. There are many problems with the application of bulk materials- weak links, poor connectivity, small coherence length, oxygen content and control, environmental reactivity, phase stability, incongruent melting behavior, grain boundary contamination, brittle mechanical behavior, and flux creep. The extent to which these problems are intrinsic or associated with processing is the subject of controversy. This study seeks to understand solidification processing of these materials, and to use this knowledge for alternative processing strategies, which, at the very least, will improve the understanding of bulk material properties and deficiencies. In general, the phase diagram studies of the YBaCuO system have concentrated on solid state reactions and on the Y2BaCuO(x) + liquid yields YBa2Cu3O(7-delta) peritectic reaction. Little information is available on the complete melting relations, undercooling, and solidification behavior of these materials. In addition, rare earth substitutions such as Nd and Gd affect the liquidus and phase relations. These materials have promising applications, but lack of information on the high temperature phase relations has hampered research. In general, the understanding of undercooling and solidification of high temperature oxide systems lags behind the science of these phenomena in metallic systems. Therefore, this research investigates the fundamental melting relations, undercooling, and solidification behavior of oxide superconductors with an emphasis on improving ground based synthesis of these materials.

  13. Chemical solution deposition of YBCO thin film by different polymer additives

    International Nuclear Information System (INIS)

    Wang, W.T.; Li, G.; Pu, M.H.; Sun, R.P.; Zhou, H.M.; Zhang, Y.; Zhang, H.; Yang, Y.; Cheng, C.H.; Zhao, Y.

    2008-01-01

    A polymer-assisted chemical solution deposition approach has been proposed for the preparation of YBCO thin film. Different additives like PVB (polyvinyl butyral), PEG (polyethylene glycol) and PVP (polyvinylpyrrolidone) have been used to adjust the final viscosity of the precursor solution and thus the film formation. In this fluorine-free approach, YBCO has been deposited on single crystal substrates with metal acetates being starting materials. Biaxially textured YBCO thin films have been obtained. However, different additives lead to different microstructure. Dense, smooth and crack-free YBCO film prepared with PVB as additive yields sharp superconducting transition around T c = 90 K as well as high J c (0 T, 77 K) over 3 MA/cm 2

  14. Chemical solution deposition of YBCO thin film by different polymer additives

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T.; Li, G.; Pu, M.H.; Sun, R.P.; Zhou, H.M.; Zhang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Yang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)], E-mail: yzhao@swjtu.edu.cn

    2008-09-15

    A polymer-assisted chemical solution deposition approach has been proposed for the preparation of YBCO thin film. Different additives like PVB (polyvinyl butyral), PEG (polyethylene glycol) and PVP (polyvinylpyrrolidone) have been used to adjust the final viscosity of the precursor solution and thus the film formation. In this fluorine-free approach, YBCO has been deposited on single crystal substrates with metal acetates being starting materials. Biaxially textured YBCO thin films have been obtained. However, different additives lead to different microstructure. Dense, smooth and crack-free YBCO film prepared with PVB as additive yields sharp superconducting transition around T{sub c} = 90 K as well as high J{sub c} (0 T, 77 K) over 3 MA/cm{sup 2}.

  15. Growth and BZO-doping of the nanostructured YBCO thin films on buffered metal substrates

    DEFF Research Database (Denmark)

    Huhtinen, H.; Irjala, M.; Paturi, P.

    2010-01-01

    The growth of the nanostructured YBa2Cu3O6+x (YBCO) films is investigated for the first time on biaxially textured NiW substrates used in coated conductor technology. The optimization process of superconducting layers is made in wide magnetic field and temperature range in order to understand...... the vortex pinning structure and mechanism in our films prepared from nanostructured material. Structural analysis shows that growth mechanism in YBCO films grown on NiW is completely different when compared to YBCO on STO. Films on NiW are much rougher, there is huge in-plane variation of YBCO crystals...... and moreover out-of-plane long range lattice ordering is greatly reduced. Magnetic measurements demonstrate that jc in films grown on NiW is higher in high magnetic fields and low temperatures. This effect is connected to the amount of pinning centres observed in films on metal substrates which are effective...

  16. YBCO/manganite layered structures on NdGaO{sub 3} substrates

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Blagoev, B [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Donchev, T [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Miteva, S [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Mozhaev, P B [Institute of Physics and Technology RAS, Nakhimovsky ave. 36, 117218 Moscow (Russian Federation); Mozhaeva, J E [Institute of Physics and Technology RAS, Nakhimovsky ave. 36, 117218 Moscow (Russian Federation); Ovsyannikov, G A [Institute of Radio Engineering and Electronics RAS, Mokhovaya st.11, 103907 Moscow (Russian Federation); Kotelyanskii, I M [Institute of Radio Engineering and Electronics RAS, Mokhovaya st.11, 103907 Moscow (Russian Federation); Jacobsen, C [Technical University of Denmark, Building 307-309, DK-2800, Kgs.Lyngby, Denmark (Denmark)

    2006-06-01

    Results of deposition of YBa{sub 2}Cu{sub 3}O{sub 7-x}/CeO{sub 2}/(La{sub 0.7}Ca{sub 0.3}MnO{sub 3} or La{sub 0.7}Sr{sub 0.3}MnO{sub 3}) structures on the standard oriented and tilted ( 8{sup 0}) NdGaO{sub 3} substrates and results of investigation of electrical parameters of YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) films in such structures are presented. The YBCO component of the structure exhibits lower value of the critical parameters in comparison with those of single YBCO films. The contribution of the magnetic layer to the microwave losses of the YBCO film in the layered structure is evaluated.

  17. YBCO/manganite layered structures on NdGaO3 substrates

    International Nuclear Information System (INIS)

    Nurgaliev, T; Blagoev, B; Donchev, T; Miteva, S; Mozhaev, P B; Mozhaeva, J E; Ovsyannikov, G A; Kotelyanskii, I M; Jacobsen, C

    2006-01-01

    Results of deposition of YBa 2 Cu 3 O 7-x /CeO 2 /(La 0.7 Ca 0.3 MnO 3 or La 0.7 Sr 0.3 MnO 3 ) structures on the standard oriented and tilted ( 8 0 ) NdGaO 3 substrates and results of investigation of electrical parameters of YBa 2 Cu 3 O 7-x (YBCO) films in such structures are presented. The YBCO component of the structure exhibits lower value of the critical parameters in comparison with those of single YBCO films. The contribution of the magnetic layer to the microwave losses of the YBCO film in the layered structure is evaluated

  18. High quality uniform YBCO film growth by the metalorganic deposition using trifluoroacetates

    Energy Technology Data Exchange (ETDEWEB)

    Wang, S.S., E-mail: wangssh@tsinghua.edu.cn [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Beihang University), Ministry of Education, Beijing 100191 (China); Beijing Dingchen Superconducting Technology Co., Ltd., Beijing 100084 (China); Zhang, Z.L. [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Beihang University), Ministry of Education, Beijing 100191 (China); Wang, L. [Applied superconductivity research center, Department of Physics, Tsinghua University, Beijing 100084 (China); Gao, L.K.; Liu, J. [Beijing Dingchen Superconducting Technology Co., Ltd., Beijing 100084 (China)

    2017-03-15

    Highlights: • High quality double-sided YBCO films are fabricated on LaAlO3 substrates by TFA-MOD method with diameters up to 2 in. • Large area YBCO films were very uniform in microstructure and thickness distribution, an average inductive Jc in excess of 6 MA/cm{sup 2} and low R{sub s} (10 GHz) of 0.3 mΩ at 77 K were obtained. • It will greatly promoted the research and applications of large-area YBCO films by chemical solution method. - Abstract: A need exists for the large-area superconducting YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) films with high critical current density for microwave communication and/or electric power applications. Trifluoroacetic metalorganic (TFA-MOD) method is a promising low cost technique for large-scale production of YBCO films, because it does not need high vacuum device and is easily applicable to substrates of various shape and size. In this paper, double-sided YBCO films with maximum 2 in diameter were prepared on LaAlO{sub 3} substrates by TFA-MOD method. Inductive critical current densitiy J{sub c}, microwave surface resistance R{sub s}, as well as the microstructure were characterized. A newly homemade furnace system was used to epitaxially grown YBCO films, which can improve the uniformity of YBCO film significantly by gas supply and temperature distribution proper design. Results showed that the large area YBCO films were very uniform in microstructure and thickness distribution, an average inductive J{sub c} in excess of 6 MA/cm{sup 2} with uniform distribution, and low R{sub s} (10 GHz) below 0.3 mΩ at 77 K were obtained. Andthe film filter may be prepared to work at temperatures lower than 74 K. These results are very close to the highest value of YBCO films made by conventional vacuum method, so we show a very promising route for large-scale production of high quality large-area YBCO superconducting films at a lower cost.

  19. BaF2 POST-DEPOSITION REACTION PROCESS FOR THICK YBCO FILMS

    International Nuclear Information System (INIS)

    SUENAGA, M.; SOLOVYOV, V.F.; WU, L.; WIESMANN, H.J.; ZHU, Y.

    2001-01-01

    The basic processes of the so-called BaF 2 process for the formation of YBa 2 Cu 3 O 7 , YBCO, films as well as its advantages over the in situ formation processes are discussed in the previous chapter. The process and the properties of YBCO films by this process were also nicely described in earlier articles by R. Feenstra, (et al.) Here, we will discuss two pertinent subjects related to fabrication of technologically viable YBCO conductors using this process. These are (1) the growth of thick (>> 1 microm) c-axis-oriented YBCO films and (2) their growth rates. Before the detail discussions of these subjects are given, we first briefly discuss what geometrical structure a YBCO-coated conductor should be. Then, we will provide examples of simple arguments for how thick the YBCO films and how fast their growth rates need to be. Then, the discussions in the following two sections are devoted to: (1) the present understanding of the nucleation and the growth process for YBCO, and why it is so difficult to grow thick c-axis-oriented films (> 3 microm), and (2) our present understanding of the YBCO growth-limiting mechanism and methods to increase the growth rates. The values of critical-current densities J c in these films are of primary importance for the applications,. and the above two subjects are intimately related to the control of J c of the films. In general, the lower the temperatures of the YBCO formation are the higher the values of J c of the films. Thus, the present discussion is limited to those films which are reacted at ∼735 C. This is the lowest temperature at which c-axis-oriented YBCO films (1-3 microm thick) are comfortably grown. It is also well known that the non-c-axis oriented YBCO platelets are extremely detrimental to the values of J c such that their effects on J c dwarf essentially all of other microstructural effects which control J c . Hence, the discussion given below is mainly focused on how to avoid the growth of these crystallites

  20. Measurement of noise in YBCO bi-crystal junctions

    International Nuclear Information System (INIS)

    Kuznik, J.; Hao, L.; Macfarlane, J.C.; Pegrum, C.M.; Fischer, G.M.; Mygind, J.; Pedersen, N.F.; Beck, A.; Gross, R.

    1993-01-01

    This paper describes collaborative work between three institutions as part of an ESPRIT programme to fabricate and characterise grain-boundary junctions. Bi-crystal junctions were fabricated at Tuebingen on SrTiO 3 substrates with a 24 misorientation angle and a-b tilt. 200nm of c-axis YBCO was sputter-deposited using a hollow-cathode magnetron, and the films patterned with optical lithography and Ar ion beam etching (3). For test purposes junctions with a range of sizes were made, with widths between 4 and 20μm. These have been characterised for noise properties at 0.3 - 1kHz and 60kHz at Strathclyde, and at 70GHz at Lyngby. (orig.)

  1. Variation of Quench Propagation Velocities in YBCO Cables

    CERN Document Server

    Härö, E.; Stenvall, A.; 10.1007/s10948-015-2976-y

    2015-01-01

    changes during the quench. Due to the large temperature margin between the operation and the current sharing temperatures, the normal zone does not propagate with the temperature front. This means that the temperature will rise in a considerably larger volume when compared to the quenched volume. Thus, the evolution of the temperature distribution below current sharing temperature Tcs after the quench onset affects the normal zone propagation velocity in HTS more than in LTS coils. This can be seen as an acceleration of the quench propagation velocities while the quench evolves when margin to Tcs is high. In this paper we scrutinize quench propagation in a stack of YBCO cables with an in-house finite element method software which solves the heat diffusion equation. We compute the longitudinal and transverse normal zone propagation velocities at various distances from the hot spot to demonstrate the distance-variation...

  2. Trapped magnetic field of a superconducting bulk magnet in high- Tc RE-Ba-Cu-O

    International Nuclear Information System (INIS)

    Fujimoto, Hiroyuki; Yoo, Sang Im; Higuchi, Takamitsu; Nakamura, Yuichi; Kamijo, Hiroki; Nagashima, Ken; Murakami, Masato

    1999-01-01

    Superconducting magnets made of high-T c superconductors are promising for industrial applications. It is well known that REBa 2 Cu 3 O 7-x and LRE (light rare-earth) Ba 2 Cu 3 O 7-x superconductors prepared by melt processes have a high critical current density, J c , at 77 K and high magnetic fields. Therefore, the materials are very prospective for high magnetic field application as a superconducting permanent/bulk magnet with liquid-nitrogen refrigeration. LREBaCuO bulks, compared with REBaCuO bulks, exhibit a larger J c in high magnetic fields and a much improved irreversibility field, H irr , at 77 K. In this study, we discuss the possibility and trapped field properties of a superconducting bulk magnet, as well as the melt processing for bulk superconductors and their characteristic superconducting properties. One of the applications is a superconducting magnet for the future magnetically levitated (Maglev) train

  3. Growth of YBCO superconducting thin films on CaF sub 2 buffered silicon

    CERN Document Server

    Bhagwat, S S; Patil, J M; Shirodkar, V S

    2000-01-01

    CaF sub 2 films were grown on silicon using the neutral cluster beam deposition technique. These films were highly crystalline and c-axis oriented. Superconducting YBCO thin films were grown on the Ca F sub 2 buffered silicon using the laser ablation technique. These films showed T sub c (onset) at 90 K and Tc(zero) at 86 K. X-ray diffraction analysis showed that the YBCO films were also oriented along the c-axis.

  4. Magnetron sputtering of Fe-oxides on the top of HTS YBCO films

    International Nuclear Information System (INIS)

    Nurgaliev, T.; Blagoev, B.; Buchkov, K.; Mateev, E.; Gajda, G.; Nedkov, I.; Kovacheva, D.; Slavov, L.; Starbova, I.; Starbov, N.; Nankovski, M.

    2017-01-01

    The possibilities for preparation of bilayers containing magnetic Fe-oxide (Fe-O) and high temperature superconducting (HTS) YBa 2 Cu 3 O 7−x (YBCO) thin films were investigated. For this purpose, Fe-O films were deposited using reactive magnetron sputtering at comparatively low temperatures T≤250 °C onto dielectric (for example, LaAlO 3 (LAO)) substrates, covered with a HTS YBCO film. The sputtering of the Fe-O layer at such conditions did not lead to a crucial damage of the critical temperature T C of the YBCO film, but could affect the width of the superconducting transition. A decrease of the critical temperature of the (Fe-O)/YBCO/LAO bilayer kept at ambient conditions was observed, possibly due to the negative effects of the water vapour on the sample characteristics. The double peak structure of the imaginary component of the response signal to the AC harmonic magnetic field, observed in such a (Fe-O)/YBCO/LAO sample, was ascribed from two possible views: as a consequence of morphology determined inter- and intra-granular contributions and/or as transitions from dominant irreversible processes as Bean-Livingston barrier to vortex state chains formation. - Highlights: • Iron-oxide (Fe-O) film sputtered on the top of superconducting HTS YBCO film at not very high temperatures. • No crucially damaged superconducting properties of YBCO film during Fe-O sputtering process. • A negative effect of the ambient conditions on the critical temperature of the obtained samples. • A double peak structure of the response signal to the AC harmonic magnetic field in a (Fe-O)/YBCO/LAO is observed.

  5. Magnetron sputtering of Fe-oxides on the top of HTS YBCO films

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Blagoev, B. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Buchkov, K. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Mateev, E. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Gajda, G. [Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Nedkov, I. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Kovacheva, D. [Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev Street, bl. 10, 1113 Sofia (Bulgaria); Slavov, L. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Starbova, I.; Starbov, N. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Nankovski, M. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Sofia university “St. Kliment Ohridski”, Faculty of Physics, 5 James Bourchier Blvd., 1164 Sofia (Bulgaria)

    2017-05-01

    The possibilities for preparation of bilayers containing magnetic Fe-oxide (Fe-O) and high temperature superconducting (HTS) YBa{sub 2}Cu{sub 3}O{sub 7−x} (YBCO) thin films were investigated. For this purpose, Fe-O films were deposited using reactive magnetron sputtering at comparatively low temperatures T≤250 °C onto dielectric (for example, LaAlO{sub 3} (LAO)) substrates, covered with a HTS YBCO film. The sputtering of the Fe-O layer at such conditions did not lead to a crucial damage of the critical temperature T{sub C} of the YBCO film, but could affect the width of the superconducting transition. A decrease of the critical temperature of the (Fe-O)/YBCO/LAO bilayer kept at ambient conditions was observed, possibly due to the negative effects of the water vapour on the sample characteristics. The double peak structure of the imaginary component of the response signal to the AC harmonic magnetic field, observed in such a (Fe-O)/YBCO/LAO sample, was ascribed from two possible views: as a consequence of morphology determined inter- and intra-granular contributions and/or as transitions from dominant irreversible processes as Bean-Livingston barrier to vortex state chains formation. - Highlights: • Iron-oxide (Fe-O) film sputtered on the top of superconducting HTS YBCO film at not very high temperatures. • No crucially damaged superconducting properties of YBCO film during Fe-O sputtering process. • A negative effect of the ambient conditions on the critical temperature of the obtained samples. • A double peak structure of the response signal to the AC harmonic magnetic field in a (Fe-O)/YBCO/LAO is observed.

  6. Photothermal measurements of superconductors

    International Nuclear Information System (INIS)

    Kino, G.S.; Wu, X.D.; Kapitulnik, A.; Fishman, I.

    1993-01-01

    The authors have developed a new photothermal technique to investigate electronic phase transitions of high temperature superconductors. The phase shift of the thermal wave yields the anisotropic thermal diffusivity coefficient of the sample. The amplitude of the photothermal signal is sensitive to electronic phase transitions of the second kind. The technique is completely noncontacting and nondestructive, and is well suited to measure small and fragile single-crystal high-T c superconductors. The measurements give good agreement with fluctuation theory near the transition temperature. They have studied diffusion in, and superconducting fluctuations of, single crystals of YBa 2 Cu 3 O 7-δ and Bi 2 Sr 2 CaCu 2 O 8 . Both systems show fluctuation effects beyond Gaussian fluctuations. While YBa 2 Cu 3 O 7-δ behaves as a three-dimensional anisotropic superconductor, results on Bi 2 Sr 2 CaCu 2 O 8 indicate strong two-dimensional effects

  7. Development of 1 m HTS conductor using YBCO on textured metal substrate

    International Nuclear Information System (INIS)

    Yagi, M.; Sakamoto, H.; Mukoyama, S.; Yamamoto, K.; Amemiya, N.; Nagaya, S.; Kashima, N.; Shiohara, Y.

    2009-01-01

    We fabricated 1 m high temperature superconducting conductor (HTS conductor) using YBa 2 Cu 3 O 7-x coated conductors (YBCO tapes) on textured metal substrates, which are expected to be lower in cost than YBCO tapes using ion-beam assisted deposition. Those substrate and intermediate layers were manufactured by Furukawa Electric, and YBCO and a protective layer were applied to the intermediate layer by Chubu Electric Power. Before fabricating the conductor, a 0.1 mm thick copper tape was soldered to the YBCO tape, and 10 mm wide YBCO tape was divided into three strips by a YAG laser. To have sufficient current capacity for 1 kA, a two-layer conductor was fabricated, and its critical current (I c ) was 1976 A, but the magnetic properties of the textured metal substrates affected the increase in AC loss. In a low current region, the AC loss in this conductor was much higher than the Norris strip model, but approached the Norris strip model in the high current region because the magnetization was almost saturated. Low AC loss of 0.144 W/m at 1 kA rms was achieved even though the conductor had a small outer diameter of 20 mm and was composed of YBCO tapes with magnetic substrates.

  8. Enhanced flux-pinning in fluorine-free MOD YBCO films by chemical doping

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T.; Pu, M.H.; Yang, Y. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Cheng, C.H. [Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y., E-mail: yzhao@swjtu.edu.c [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)

    2010-11-01

    YBCO films without and with dilute cobalt and zinc doping were prepared on (0 0 l) LaAlO{sub 3} substrate by non-fluorine metal organic deposition method. Effects of dilute cobalt and zinc doping on biaxial texture, microstructure and flux-pinning properties of YBCO films were investigated. The surface density and smoothness of the doped YBCO films have been distinctly improved compared with that of the pure film. Dilute cobalt- and zinc-doped YBCO films exhibit significantly enhanced J{sub c} values in the magnetic field. The best result is achieved in the cobalt-doped YBCO film. At 77 K, J{sub c} values of cobalt-doped film are 1.7 and 5.4 times higher than that of pure film in 0.5 T and 1.5 T, respectively. These results strongly suggest that dilute cobalt and zinc doping is a promising way to increase the current carrying capability of YBCO films.

  9. Enhancement of flux pinning of TFA-MOD YBCO thin films by embedded nanoscale Y2O3

    International Nuclear Information System (INIS)

    Cui, X M; Tao, B W; Tian, Z; Xiong, J; Zhang, X F; Li, Y R

    2006-01-01

    YBCO films with different levels of excess yttrium were prepared on single-crystal LaAlO 3 with metal-organic deposition using trifluoroacetates (TFA-MOD). X-ray diffraction and transmission electron microscope measurements revealed excess yttrium in YBCO in the form of nanoscale Y 2 O 3 with (400) preferred orientation. The field dependence of J c demonstrated that YBCO films with Y 2 O 3 doping had enhanced J c in comparison with stoichiometric YBCO films in the magnetic fields. We think the reason for this is that the Y 2 O 3 nanoparticles act as pinning centres. YBCO films with 60% yttrium excess display 43% increased J c compared to stoichiometric YBCO films at a magnetic field of 1 T

  10. Hysteretic Vortex-Matching Effects in High-Tc Superconductors with Nanoscale Periodic Pinning Landscapes Fabricated by He Ion-Beam Projection

    Science.gov (United States)

    Zechner, G.; Jausner, F.; Haag, L. T.; Lang, W.; Dosmailov, M.; Bodea, M. A.; Pedarnig, J. D.

    2017-07-01

    Square arrays of submicrometer columnar defects in thin YBa2 Cu3 O7 -δ (YBCO) films with spacings down to 300 nm are fabricated by a He ion-beam projection technique. Pronounced peaks in the critical current and corresponding minima in the resistance demonstrate the commensurate arrangement of flux quanta with the artificial pinning landscape, despite the strong intrinsic pinning in epitaxial YBCO films. While these vortex-matching signatures are exactly at the predicted values in field-cooled experiments, they are displaced in zero-field-cooled, magnetic-field-ramped experiments, conserving the equidistance of the matching peaks and minima. These observations reveal an unconventional critical state in a cuprate superconductor with an artificial, periodic pinning array. The long-term stability of such out-of-equilibrium vortex arrangements paves the way for electronic applications employing fluxons.

  11. An unconventional colour superconductor

    International Nuclear Information System (INIS)

    Huang Mei

    2007-01-01

    Superfluidity, or superconductivity with mismatched Fermi momenta, appears in many systems such as charge-neutral dense quark matter, asymmetric nuclear matter, and in imbalanced cold atomic gases. The mismatch plays the role of breaking the Cooper pairing, and the pair-breaking state cannot be properly described in the framework of standard BCS theory. I give a brief review on recent theoretical developments in understanding unconventional colour superconductivity, including a gapless colour superconductor, chromomagnetic instabilities and the Higgs instability in the gapless phase. I also introduce a possible new framework for describing an unconventional colour superconductor

  12. The Born-Mayer-Huggins potential in high temperature superconductors

    Science.gov (United States)

    Singh, Hempal; Singh, Anu; Indu, B. D.

    2016-07-01

    The Born-Mayer-Huggins potential which has been found the best suitable potential to study the YBa2Cu3O7-δ type high temperature superconductors is revisited in a new framework. A deeper insight in it reveals that the Born-Mayer parameters for different interactions in high temperature superconductor are not simple quantities but several thermodynamic and spatial functions enter the problem. Based on the new theory, the expressions for pressure, bulk modulus and Born-Mayer parameters have been derived and it is established that these quantities depend upon Gruneisen parameter which is the measure of the strength of anharmonic effects in high temperature superconductors. This theory has been applied to a specific model YBa2Cu3O7-δ crystal for the purpose of numerical estimates to justify the new results.

  13. Calculation and analysis of thermodynamic relations for superconductors

    International Nuclear Information System (INIS)

    Nazarenko, A.B.

    1989-01-01

    The absorption coefficients of high-frequency and low-frequency sound have been calculated on the basis of the Ginzburg-Landau theory. This sound is a wave of periodic adiabatic bulk compressions and rarefactions of the frequency ω in an isotropic superconductor near the transition temperature. Thermodynamic relations have been obtained for abrupt changes in the physical quantities produced as a result of a transition from the normal state to the superconducting state. These relations are similar to the Ehrenfest relations. The above--mentioned thermodynamic quantities are compared with the published experimental results on YBa 2 Cu 3 O 7-δ . The experiments on the absorption of ultrasound in recently discovered superconductors mainformation on the phase transition type and thermodynamic relations for these superconductors, in particular, the T c -vs-dp curve. Similar calculations have been carried out for 2 He-transition experiments with ferromagnetic materials. The order parameter in the thermodynamic potential was assumed to be isotropic

  14. Quantum information aspects on bulk and nano interacting Fermi system: A spin-space density matrix approach

    Energy Technology Data Exchange (ETDEWEB)

    Afzali, R., E-mail: afzali@kntu.ac.ir [Department of Physics, K. N. Toosi University of Technology, Tehran, 15418 (Iran, Islamic Republic of); Ebrahimian, N., E-mail: n.ebrahimian@shahed.ac.ir [Department of Physics, Faculty of Basic Sciences, Shahed University, Tehran, 18155-159 (Iran, Islamic Republic of); Eghbalifar, B., E-mail: b.eghbali2011@yahoo.com [Department of Agricultural Management, Marvdasht Branch, Azad University, Marvdasht (Iran, Islamic Republic of)

    2016-10-07

    Highlights: • In contrast to a s-wave superconductor, the quantum correlation of the d-wave superconductor is sensitive to the change of the gap magnitude. • Quantum discord of the d-wave superconductor oscillates. • Quantum discord becomes zero at a characteristic length of the d-wave superconductor. • Quantum correlation strongly depends on the length of grain. Length of the superconductor lower, the quantum correlation length higher. • Quantum tripartite entanglement for a nano-scale d-wave superconductor is better than for a bulk d-wave superconductor. - Abstract: By approximating the energy gap, entering nano-size effect via gap fluctuation and calculating the Green's functions and the space-spin density matrix, the dependence of quantum correlation (entanglement, discord and tripartite entanglement) on the relative distance of two electron spins forming Cooper pairs, the energy gap and the length of bulk and nano interacting Fermi system (a nodal d-wave superconductor) is determined. In contrast to a s-wave superconductor, quantum correlation of the system is sensitive to the change of the gap magnitude and strongly depends on the length of the grain. Also, quantum discord oscillates. Furthermore, the entanglement length and the correlation length are investigated. Discord becomes zero at a characteristic length of the d-wave superconductor.

  15. Strain analysis of I-c(epsilon) characteristic of YBCO coated conductor measured by a Walters spring

    OpenAIRE

    Sugano, M; Choi, S; Miyazoe, A; Miyamatsu, K; Ando, T; Itoh, K; Kiyoshi, T; Wada, H; Selvamanickam, V

    2008-01-01

    lc-strain characteristic of YBCO coated conductor was measured using a Walters spring (WASP). In this technique, additional bending and thermal strains induced to the YBCO layer should be considered. In order to produce different initial bending strain to the YBCO layer, the conductor was wound around the springs with different diameters and in the different bending directions. The clear evidence was obtained that -strain curves using a WASP strongly depend on the initial bending strain state...

  16. Quality of YBCO thin films grown on LAO substrates exposed to the film deposition - film removal processes

    Energy Technology Data Exchange (ETDEWEB)

    Blagoev, B; Nurgaliev, T [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee, 1784 Sofia (Bulgaria); Mozhaev, P B [Institute of Physics and Technology, Russian Academy of Sciences, 117218 Moscow (Russian Federation); Sardela, M; Donchev, T [Materials Research Laboratory, University of Illinois, 104 South Goodwin Ave., Urbana, IL 61801 (United States)], E-mail: blago_sb@yahoo.com

    2008-05-01

    The characteristics are investigated of high temperature superconducting YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) films grown on LaAlO{sub 3} (LAO) substrates being exposed a different number of times to YBCO film deposition and acid-solution-based cleaning procedures. Possible mechanisms of degradation of the substrate surface quality reflecting on the growing YBCO film parameters are discussed and analyzed.

  17. Topological insulators/superconductors: Potential future electronic materials

    International Nuclear Information System (INIS)

    Hor, Y. S.

    2014-01-01

    A new material called topological insulator has been discovered and becomes one of the fastest growing field in condensed matter physics. Topological insulator is a new quantum phase of matter which has Dirac-like conductivity on its surface, but bulk insulator through its interior. It is considered a challenging problem for the surface transport measurements because of dominant internal conductance due to imperfections of the existing crystals of topological insulators. By a proper method, the internal bulk conduction can be suppressed in a topological insulator, and permit the detection of the surface currents which is necessary for future fault-tolerant quantum computing applications. Doped topological insulators have depicted a large variety of bulk physical properties ranging from magnetic to superconducting behaviors. By chemical doping, a TI can change into a bulk superconductor. Nb x Bi 2 Se 3 is shown to be a superconductor with T c ∼ 3.2 K, which could be a potential candidate for a topological superconductor

  18. Properties of amorphous and microcrystalline superconductors

    International Nuclear Information System (INIS)

    Johnson, W.L.; Poon, S.J.

    1975-01-01

    Results of x-ray diffraction, electrical resistivity, critical field(H/sub c2/) and transport measurements are presented and discussed for bulk amorphous and microcrystalline transition metal alloys (Au--La, Nb--Rh, Nb--Ni--Rh, and Pd--Zr) obtained by liquid quenching. The transition temperature of the alloys is in the range 1.5 to 4.7 0 K. The J/sub c/--H/sub c2/--T/sub c/ relations are rather simple for this class of material and are compared with the theories of type II superconductors. The high resistance of bulk metallic glass to radiation damage might render them suitable for magnetic field applications in high radiation environments

  19. Submillimeter residual losses in high-Tc superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Miller, David [Univ. of California, Berkeley, CA (United States)

    1993-09-01

    Bolometry was used obtain accurate submillimeter residual loss data for epitaxial films of YBa2Cu3O7 (YBCO), Tl2Ca2Ba2Cu3O10, Tl2CaBa2Cu2O8 (TCBCO), and Ba0.6K0.4BiO3 (BKBO). We were able to fit the absorptivity measured for Nb films to an Eliashberg strong coupling calculation; excellent agreement resulted between parameters from best fits and measured Residual Resistivity Ratio. Microwave surface resistance measurements made on the same YBCO and TCBCO films are in excellent agreement with submillimeter measurements. Absorptivities for all YBCO films studied are qualitatively similar, increasing smoothly with frequency, with no gap-like features below the well known absorption edge at 450 cm-1. Losses in YBCO films were fit to a weakly coupled grain model for the a-b plane conductivity. Strong phonon structure was observed in TCBCO films between 60 and 700 cm-1 (2 THz and 23 THz); these losses could not be fitted to the simple weakly coupled grain model, in contrast to the case for other high-Tc superconductors where phonon structure observed in ceramics are is absent in epitaxial oriented films and crystals because of electronic screening due to high conductivity of a-b planes. Absorptivity data for the BKBO films all show a strong absorption onset near the BCS tunneling gap of 3.5 kBTc. Comparison with strong coupling Eliashberg predictions and of a Kramers-Kronig analysis indicate that the absorption onset is consistent with a superconducting energy gap. Effects of magnetic field on residual losses in YBCO films show a resonant absorption feature in vicinity of predicted

  20. Glass formability of high T(sub c) Bi-Sr-Ca-Cu-O superconductors

    Science.gov (United States)

    Kaukler, William F.

    1992-01-01

    A number of compositions of ceramic oxide high T(sub c) superconductors were evaluated for their glass formation ability by means of rapid thermal analysis during quenching, optical and electron microscopy of the quenched samples, and with subsequent DSC measurements. Correlations between experimental measurements and the methodical composition changes identified the formulations of superconductors that can easily form glass. The superconducting material was first formed as a glass, then with subsequent devitrification it was formed into bulk crystalline superconductor by a series of processing methods.

  1. Open questions in the magnetic behaviour of high-temperature superconductors

    International Nuclear Information System (INIS)

    Cohen, L.F.; Jensen, Henrik Jeldtoft

    1997-01-01

    A principally experimental review of vortex behaviour in high-temperature superconductors is presented. The reader is first introduced to the basic concepts needed to understand the magnetic properties of type II superconductors. The concepts of vortex melting, the vortex glass, vortex creep, etc are also discussed briefly. The bulk part of the review relates the theoretical predictions proposed for the vortex system in high temperature superconductors to experimental findings. The review ends with an attempt to direct the reader to those areas which still require further clarification. (author)

  2. Classical spins in superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Shiba, H [Tokyo Univ.; Maki, K

    1968-08-01

    It is shown that there exists a localized excited state in the energy gap in a superconductor with a classical spin. At finite concentration localized excited states around classical spins form an impurity band. The process of growth of the impurity band and its effects on observable quantities are investigated.

  3. Superconductors and medical imaging

    International Nuclear Information System (INIS)

    Aubert, Guy

    2011-01-01

    After difficult beginnings in the 1970's, magnetic resonance imaging (MRI) has evolved to become nowadays the jewel in the crown of medical technology. Superconductors have been a key factor for the extraordinary expansion of MRI which in turn represents about 75 % of their total market. After recalling some basic principles, this article traces their common history and refers to future developments. (author)

  4. Irradiation damage in superconductors

    International Nuclear Information System (INIS)

    Quere, Y.

    1989-01-01

    Most superconductors are quite sensitive to irradiation defects. Critical temperatures may be depressed, critical currents may be increased, by irradiation, but other behaviours may be encountered. In compounds, the sublattice in which defects are created is of significant importance. 24 refs

  5. Single Crystal Synthesis and STM Studies of High Temperature Superconductors

    Science.gov (United States)

    Barrientos, Alfonso

    1997-01-01

    This is a final report for the work initiated in September of 1994 under the grant NAG8-1085 - NASA/OMU, on the fabrication of bulk and single crystal synthesis, specific heat measuring and STM studies of high temperature superconductors. Efforts were made to fabricate bulk and single crystals of mercury based superconducting material. A systematic thermal analysis on the precursors for the corresponding oxides and carbonates were carried out to synthesized bulk samples. Bulk material was used as seed in an attempt to grow single crystals by a two-step self flux process. On the other hand bulk samples were characterized by x-ray diffraction, electrical resistivity and magnetic susceptibility, We studied the specific heat behavior in the range from 80 to 300 K. Some preliminary attempts were made to study the atomic morphology of our samples. As part of our efforts we built an ac susceptibility apparatus for measuring the transition temperature of our sintered samples.

  6. Three-dimensional Majorana fermions in chiral superconductors.

    Science.gov (United States)

    Kozii, Vladyslav; Venderbos, Jörn W F; Fu, Liang

    2016-12-01

    Using a systematic symmetry and topology analysis, we establish that three-dimensional chiral superconductors with strong spin-orbit coupling and odd-parity pairing generically host low-energy nodal quasiparticles that are spin-nondegenerate and realize Majorana fermions in three dimensions. By examining all types of chiral Cooper pairs with total angular momentum J formed by Bloch electrons with angular momentum j in crystals, we obtain a comprehensive classification of gapless Majorana quasiparticles in terms of energy-momentum relation and location on the Fermi surface. We show that the existence of bulk Majorana fermions in the vicinity of spin-selective point nodes is rooted in the nonunitary nature of chiral pairing in spin-orbit-coupled superconductors. We address experimental signatures of Majorana fermions and find that the nuclear magnetic resonance spin relaxation rate is significantly suppressed for nuclear spins polarized along the nodal direction as a consequence of the spin-selective Majorana nature of nodal quasiparticles. Furthermore, Majorana nodes in the bulk have nontrivial topology and imply the presence of Majorana bound states on the surface, which form arcs in momentum space. We conclude by proposing the heavy fermion superconductor PrOs 4 Sb 12 and related materials as promising candidates for nonunitary chiral superconductors hosting three-dimensional Majorana fermions.

  7. Advanced nuclear materials development -Development of superconductor application technology-

    International Nuclear Information System (INIS)

    Hong, Kye Won; Lee, Heui Kyoon; Lee, Hoh Jin; Kim, Chan Joong; Jang, Kun Ik; Kim, Kee Baek; Kwon, Sun Chil; Park, Hae Woong; Yoo, Jae Keun; Kim, Jong Jin; Jang, Joong Chul; Yang, Suk Woo

    1995-07-01

    Fabrication of high Tc bulk superconductor and its application, fabrication of superconducting wire for electric power device and analysis for cryogenic system were carried out for developing superconductor application technologies for electric power system. High quality YBaCuO bulk superconductor was fabricated by controlling initial powder preparation process and prototype fly wheel energy storage device was designed basically. The superconducting levitation force measuring device was made to examine the property of prepared superconductor specimen. Systematic studies on the method of starting powder preparation, mechanical fabrication process, heat treatment condition and analysis of plastic deformation were carried out to increase the stability and reproducibility of superconducting wire. A starting powder with good reactivity and fine particle size was obtained by emulsion drying method. Ag/BSCCO tape with good cross sectional shape and Tc of 16,000 A/cm 2 was fabricated by applying CIP packing procedure. Multifilamentary wire with the Jc of approx. 10000 A/cm 2 was fabricated by rolling method using square billet as starting shape. The joining of the multifilament wire was done by etching and pressing process and showed 50% of joining efficiency. Analysis on the heat loss in cryostat for high Tc superconducting device was carried out for optimum design of the future cryogenic system. 126 figs, 14 tabs, 214 refs. (Author)

  8. Advanced nuclear materials development -Development of superconductor application technology-

    Energy Technology Data Exchange (ETDEWEB)

    Hong, Kye Won; Lee, Heui Kyoon; Lee, Hoh Jin; Kim, Chan Joong; Jang, Kun Ik; Kim, Kee Baek; Kwon, Sun Chil; Park, Hae Woong; Yoo, Jae Keun; Kim, Jong Jin; Jang, Joong Chul; Yang, Suk Woo [Korea Atomic Energy Research Institute, Taejon (Korea, Republic of)

    1995-07-01

    Fabrication of high Tc bulk superconductor and its application, fabrication of superconducting wire for electric power device and analysis for cryogenic system were carried out for developing superconductor application technologies for electric power system. High quality YBaCuO bulk superconductor was fabricated by controlling initial powder preparation process and prototype fly wheel energy storage device was designed basically. The superconducting levitation force measuring device was made to examine the property of prepared superconductor specimen. Systematic studies on the method of starting powder preparation, mechanical fabrication process, heat treatment condition and analysis of plastic deformation were carried out to increase the stability and reproducibility of superconducting wire. A starting powder with good reactivity and fine particle size was obtained by emulsion drying method. Ag/BSCCO tape with good cross sectional shape and Tc of 16,000 A/cm{sup 2} was fabricated by applying CIP packing procedure. Multifilamentary wire with the Jc of approx. 10000 A/cm{sup 2} was fabricated by rolling method using square billet as starting shape. The joining of the multifilament wire was done by etching and pressing process and showed 50% of joining efficiency. Analysis on the heat loss in cryostat for high Tc superconducting device was carried out for optimum design of the future cryogenic system. 126 figs, 14 tabs, 214 refs. (Author).

  9. 5 MJ flywheel based on bulk HTS magnetic suspension

    Science.gov (United States)

    Poltavets, V.; Kovalev, K.; Ilyasov, R.; Glazunov, A.; Maevsky, V.; Verzbitsky, L.; Akhmadyshev, V.; Shikov, A.

    2014-05-01

    Nowadays the flywheel energy storage systems (FES) are developed intensively as uninterruptible power supply (UPS) devices for on-land and transport (especially airborne) applications worldwide. This work is devoted to the FES with magnetic suspension on the base of bulk HTS YBCO elements and permanent magnets. The developed FES is intended to be used as UPS in Russian atomic industry in case of an emergency. For the successful design of the FES the following questions should be solved: design of the motor/generator, design of the rotor (flywheel), design of the bearing system, design of the control system and system of power load matching, design of the cooling system. The developed small-scale FES with the stored energy 0.5 MJ was used to solve these basic questions. The elaborated FES consists of the synchronous electric machine with permanent magnets, the solid flywheel with axial magnetic suspension on the base of YBCO bulks and permanent magnets, the system of control and power load matching, and the system of liquid nitrogen cooling. The results of theoretical modeling of different schematics of magnetic suspension and experimental investigations of the constructed FES are presented. The design of the future full-scale FES with the stored energy ~5 MJ and output power up to 100 kW is described. The test results of the flywheel rotor and HTS magnetic suspension of 5 MJ FES are presented. This work is done under support of Rosatom within the frames of Russian Project "Superconducting Industry"

  10. To Crack or Not to Crack: Strain in High Temperature Superconductors

    International Nuclear Information System (INIS)

    Godeke, Arno

    2007-01-01

    Round wire Bi 2212 is emerging as a viable successor of Nb3Sn in High Energy Physics and Nuclear Magnetic Resonance, to generate magnetic fields that surpass the intrinsic limitations of Nb3Sn. Rather bold claims are made on achievable magnetic fields in applications using Bi 2212, due to the materials' estimated critical magnetic field of 100 Tor higher. High transport currents in high magnetic fields, however, lead to large stress on, and resulting large strain in the superconductor. The effect of strain on the critical properties of Bi-2212 is far from understood, and strain is, as with Nb3Sn, often treated as a secondary parameter in the design of superconducting magnets. Reversibility of the strain induced change of the critical surface of Nb3Sn, points to an electronic origin of the observed strain dependence. Record breaking high field magnets are enabled by virtue of such reversible behavior. Strain effects on the critical surface of Bi-2212, in contrast, are mainly irreversible and suggest a non-electronic origin of the observed strain dependence, which appears to be dominated by the formation of cracks in the superconductor volumes. A review is presented of available results on the effects of strain on the critical surface of Bi-2212, Bi-2223 and YBCO. It is shown how a generic behavior emerges for the (axial) strain dependence of the critical current density, and how the irreversible reduction of the critical current density is dominated by strain induced crack formation in the superconductor. From this generic model it becomes clear that magnets using high temperature superconductors will be strain limited far before the intrinsic magnetic field limitations will be approached, or possibly even before the magnetic field limitation of Nb3Sn can be surpassed. On a positive note, in a very promising recent result from NIST on the axial strain dependence of the critical current density in extremely well aligned YBCO, reversible behavior was observed. This

  11. Seven harmonic susceptibility in oxygen and hydrogen loading of sintered YBCO by μs pulsed electrolysis in an aqueous solution at room temperature

    International Nuclear Information System (INIS)

    Tripodi, P.; Di Gioacchino, D.; Celani, F.

    1996-09-01

    The complex AC susceptibility of high T c superconducting materials has been described in terms of the first seven harmonic component of Fourier series. Has been measured the χ' n and χ n (n=1,7) of sintered YBa 2 Cu 3 O 7-x (YBCO) bulk oxygen and hydrogen loaded samples versus amplitude and frequency of AC magnetic field at fixed temperature. The sample have been loaded by μs current pulses electrolysis in an aqueous solution (0.3N LiOH+H 2 O) at room temperature. In addition to the simplicity of the experimental setup, this procedure allows to obtain extremely high equivalent hydrogen/oxygen gas pressure on the surface of the electrodes. The YBCO electrode is polarized by short pulse width (0.5-10 μs) and high power (120 W) peaks with a variable repetition rate (0.1-10000 Hz). The pulses are obtained by an home.made pulse generator. The difference in the behavior of the susceptibilities harmonic component between the deficiency and oxygen or hydrogen loaded samples give us the possibility to connect the susceptibilities with variations of the flux pinning in respect to normal losses in the superconducting materials. The loading can be a good probe to have information on the mechanism of the processes that sustain the critical current density Jc in this situation these affects appear strongly dependent on the loading conditions. By comparison of this measurements has been observed drastic change in behavior of susceptibility

  12. The effects of carbon nano filaments (CNT and CNF) doping on high temperature superconductors Y-123

    International Nuclear Information System (INIS)

    Dadras, S.; Daadmehr, V.

    2007-01-01

    carbon content increasing. Also increasing of carbon in samples over 0.06 wt%, decreases Tc and less than 0.06wt% carbon content has no effect on Tc . According to our experiments, we obtained changes in critical temperature Tc, by changing CNT doping in Y-123 samples (0.1- 1 wt%), with optimum in 0.3 wt%. Increasing CNT over that amount decreases Tc. In addition, we prepared samples with different carbon percentage (0.05-1 wt%), and found that superconductivity disappears in materials containing more than 0.5 wt% carbon. Carbon increasing in Y-123 samples decreases the critical current density (JC). In this experience, JC in embedded CNT-Y-123 samples was increasing in compare to pure ones. Carbon nano tubes with proper geometry (diameter and its length) could connect the grains of YBCO causing to increase JC. The CNT's are expected to act as efficient pinning centers in HTSC materials. In summary, we have prepared high-quality bulk samples of both pure and CNF-Y-123. The samples have a sharp superconducting transition from 90 up to 94 K, depending on different weight of CNF doping, which have had optimum TC in 0.3 wt%. Besides, increasing amount of CNT doping increases the critical current density JC. (authors)

  13. Improved magnetic-field homogeneity of NMR HTS bulk magnet using a new stacking structure and insertion of an HTS film cylinder into a bulk bore

    International Nuclear Information System (INIS)

    Itoh, Yoshitaka; Yanagi, Yousuke; Nakamura, Takashi

    2017-01-01

    A new type of superconducting bulk magnet for compact nuclear magnetic resonance (NMR) devices with high magnetic-field homogeneity has been developed by inserting an HTS film cylinder into a bulk superconductor bore. Annular 60 mmϕ Eu-Ba-Cu-O bulk superconductors with a larger inner diameter (ID) of 36 mm were sandwiched between bulk superconductors with a smaller ID of 28 mm, and the total height of the bulk superconductor set was made to be 120 mm. The inner height of central wide bore space was optimized by magnetic-field simulation so that the influence of the bulk superconductor's paramagnetic moment on applied field homogeneity was minimized during the magnetization process. An HTS film cylinder, in which Gd-Ba-Cu-O tapes were wound helically in three layers around a copper cylinder, was inserted into the bulk bore in order to compensate for the inhomogeneous field trapped by the bulk superconductor. The superconducting bulk magnet composed of the above bulk superconductor set and the film cylinder were cooled by a GM pulse tube refrigerator and magnetized at 4.747 T using the field cooling (FC) method and a conventional superconducting coil magnet adjusted to below 0.5 ppm in magnetic-field homogeneity. The NMR measurement was conducted for an H_2O sample with a diameter of 6.9 mm and a length of 10 mm by setting the sample in the center of the 20 mm ID room-temperature bore of the bulk magnet. The magnetic-field homogeneity derived from the full width at half maximum (FWHM) of the "1H spectrum of H_2O was 0.45 ppm. We confirmed that the HTS film inner cylinder was effective in maintaining the homogeneity of the magnetic field applied in the magnetization process, and as a result, a magnetic field with a homogeneity of less than 1 ppm can be generated in the bore of the bulk magnet without using shim coils. (author)

  14. The fluctuation Hall conductivity and the Hall angle in type-II superconductor under magnetic field

    Energy Technology Data Exchange (ETDEWEB)

    Tinh, Bui Duc, E-mail: tinhbd@hnue.edu.vn [Institute of Research and Development, Duy Tan University, K7/25 Quang Trung, Danang (Viet Nam); Department of Physics, Hanoi National University of Education, 136 Xuan Thuy, Cau Giay, Hanoi (Viet Nam); Hoc, Nguyen Quang; Thu, Le Minh [Department of Physics, Hanoi National University of Education, 136 Xuan Thuy, Cau Giay, Hanoi (Viet Nam)

    2016-02-15

    Highlights: • The time-dependent Ginzburg–Landau was used to calculate fluctuation Hall conductivity and Hall angle in type-II superconductor in 2D and 3D. • We obtain analytical expressions for the fluctuation Hall conductivity and the Hall angle summing all Landau levels without need to cutoff higher Landau levels to treat arbitrary magnetic field. • The results were compared to the experimental data on YBCO. - Abstract: The fluctuation Hall conductivity and the Hall angle, describing the Hall effect, are calculated for arbitrary value of the imaginary part of the relaxation time in the frame of the time-dependent Ginzburg–Landau theory in type II-superconductor with thermal noise describing strong thermal fluctuations. The self-consistent Gaussian approximation is used to treat the nonlinear interaction term in dynamics. We obtain analytical expressions for the fluctuation Hall conductivity and the Hall angle summing all Landau levels without need to cutoff higher Landau levels to treat arbitrary magnetic field. The results are compared with experimental data on high-T{sub c} superconductor.

  15. Iron pnictide superconductors

    International Nuclear Information System (INIS)

    Tegel, Marcus Christian

    2011-01-01

    The scope of this dissertation therefore has not only been the synthesis of various new superconducting and non-superconducting iron pnictides of several structural families but also their in-depth crystallographic and physical characterisation. In Chapters 3 - 6, the family of the ZrCuSiAs-type (1111) compounds is subject of discussion. The solid solution series La(Co x Fe 1-x )PO is analysed regarding magnetic and superconducting properties and the new compounds EuMnPF and REZnPO, as well as the new superconductor parent compound SrFeAsF are presented. Chapters 7 - 9 are dedicated to the new iron arsenide superconductors of the ThCr 2 Si 2 -type (122 family). Therein, also the discovery of the first superconductor in this structural family, Ba 0.6 K 0.4 Fe 2 As 2 , is unveiled. A detailed examination of the complete solid solution series (Ba 1-x K x )Fe 2 As 2 is presented. Moreover, the crystallographic phase transitions of the closely related compounds SrFe 2 As 2 and EuFe 2 As 2 are characterised and the superconductors Sr 1-x K x Fe 2 As 2 and Ca 1-x Na x Fe 2 As 2 are examined for magnetic and phononic excitations. In Chapter 10, the redetermined crystal structure of the superconductor Fe(Se 1-x Te x ) (11-type) is presented from a chemist's point of view. Chapters 11 - 14 look into the superconducting and non-superconducting iron arsenides of more complex structural families (32522-type and 21311-type). Therein, crystallographic and magnetic details of Sr 3 Sc 2 O 5 Fe 2 As 2 are presented and Ba 2 ScO 3 FeAs and Sr 2 CrO 3 FeAs, the first two members of the new 21311-type are portrayed. Sr 2 CrO 3 FeAs is looked at in close detail with various methods, so e.g. the spin structure of the magnetically ordered compound is solved and a possible reason for the absence of superconductivity in this compound is given. Finally, the superconductor Sr 2 VO 3 FeAs is scrutinised and necessary prerequisites for superconductivity in this compound are suggested. (orig.)

  16. "Fluctuoscopy" of Superconductors

    Science.gov (United States)

    Varlamov, A. A.

    Study of fluctuation phenomena in superconductors (SCs) is the subject of great fundamental and practical importance. Understanding of their physics allowed to clear up the fundamental properties of SC state. Being predicted in 1968, one of the fluctuation effects, namely paraconductivity, was experimentally observed almost simultaneously. Since this time, fluctuations became a noticeable part of research in the field of superconductivity, and a variety of fluctuation effects have been discovered. The new wave of interest to fluctuations (FL) in superconductors was generated by the discovery of cuprate oxide superconductors (high-temperature superconductors, HTS), where, due to extremely short coherence length and low effective dimensionality of the electron system, superconductive fluctuations manifest themselves in a wide range of temperatures. Moreover, anomalous properties of the normal state of HTS were attributed by many theorists to strong FL in these systems. Being studied in the framework of the phenomenological Ginzburg-Landau theory and, more extensively, in diagrammatic microscopic approach, SC FLs side by side with other quantum corrections (weak localization, etc.) became a new tool for investigation and characterization of such new systems as HTS, disordered electron systems, granular metals, Josephson structures, artificial super-lattices, etc. The characteristic feature of SC FL is their strong dependence on temperature and magnetic fields in the vicinity of phase transition. This allows one to definitely separate the fluctuation effects from other contributions and to use them as the source of information about the microscopic parameters of a material. By their origin, SC FLs are very sensitive to relaxation processes, which break phase coherence. This allows using them for versatile characterization of SC. Today, one can speak about the " fluctuoscopy" of superconductive systems. In review, we present the qualitative picture both of thermodynamic

  17. Measuring condensate fraction in superconductors

    International Nuclear Information System (INIS)

    Chakravarty, Sudip; Kee, Hae-Young

    2000-01-01

    An analysis of off-diagonal long-range order in superconductors shows that the spin-spin correlation function is significantly influenced by the order if the order parameter is anisotropic on a microscopic scale. Thus, magnetic neutron scattering can provide a direct measurement of the condensate fraction of a superconductor. It is also argued that recent measurements in high-temperature superconductors come very close to achieving this goal. (c) 2000 The American Physical Society

  18. Processing of Mixed Oxide Superconductors

    Science.gov (United States)

    1990-07-01

    rapid changes world wide a major research centre on high Tc superconductors was awarded to Cambridge which involved moving the work and people to a...reports and paper is in the appendices. Separation Ceramic superconductors tend to be mixtures of phases, especially when first discovered. It would...properties of the superconducting state will in principle allow superconducting material to be levitated from the non superconductor and several designs

  19. Superconductor stability 90: A review

    International Nuclear Information System (INIS)

    Dresner, L.

    1990-01-01

    This paper reviews some recent developments in the field of stability of superconductors. The main topics dealt with are hydrodynamic phenomena in cable-in-conduit superconductors, namely, multiple stability, quench pressure, thermal expulsion, and thermal hydraulic quenchback, traveling normal zones in large, composite conductors, such as those intended for SMES, and the stability of vapor-cooled leads made of high-temperature superconductors. 31 refs., 5 figs

  20. Research on active magnetic levitation of multiple high-T{sub c} superconductors; Fukusu no baruku chodendotai wo mochiita akuteibu jikifujo ni kansuru kenkyu

    Energy Technology Data Exchange (ETDEWEB)

    Nishi, K.; Tachi, K.; Sawa, K. [Keio University, Tokyo (Japan); Iwasa, K. [Francis Bitter Magnet Laboratory, Cambridge (United States); Nagashima, K.; Fujimoto, H. [Railway Technical Research Institute, Tokyo (Japan); Miyamoto, T.; Tomita, M.; Murakami, M. [Superconducting Research Laboratory, Tokyo (Japan)

    1999-11-25

    This paper describes a new [electromaglev] system, in which multiple Y-Ba-Cu-O bulk superconductors are levitated on a DC magnet. In this system, we have succeeded in controlling the levitation height and force like the case of a single bulk system. We also simulated the total levitation force for multiple bulks, which were in good agreement with the experimental results. (author)

  1. High Temperature Superconductor Resonator Detectors

    Data.gov (United States)

    National Aeronautics and Space Administration — High Temperature Superconductor (HTS) infrared detectors were studied for years but never matured sufficiently for infusion into instruments. Several recent...

  2. Critical current survival in the YBCO superconducting layer of a delaminated coated conductor

    Science.gov (United States)

    Feng, Feng; Fu, Qishu; Qu, Timing; Mu, Hui; Gu, Chen; Yue, Yubin; Wang, Linli; Yang, Zhirong; Han, Zhenghe; Feng, Pingfa

    2018-04-01

    A high-temperature superconducting coated conductor can be practically applied in electric equipment due to its favorable mechanical properties and critical current (I c) performance. However, the coated conductor can easily delaminate because of its poor stress tolerance along the thickness direction. It would be interesting to investigate whether the I c of the delaminated YBa2Cu3O7-δ (YBCO) layer can be preserved. In this study, coated conductor samples manufactured through the metal organic deposition route were delaminated by liquid nitrogen immersion. Delaminated samples, including the YBCO layer and silver stabilizer, were obtained. Delamination occurred inside the YBCO layer and near the YBCO-CeO2 interface, as suggested by the results of scanning electron microscopy (SEM) and x-ray diffraction. A scanning Hall probe system was employed to measure the I c distribution of the original sample and the delaminated sample. It was found that approximately 50% of the I c can be preserved after delamination, which was verified by I c measurements using the four-probe method. Dense and crack-free morphologies of the delaminated surfaces were observed by SEM, which accounts for the I c survival of the delaminated YBCO layer. The potential application of the delaminated sample in superconducting joints was discussed based on the oxygen diffusion estimation.

  3. Investigation of DC current injection effect on the microwave characteristics of HTS YBCO microstrip resonators

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T., E-mail: timur@ie.bas.bg [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Blagoev, B.; Mateev, E.; Neshkov, L. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Strbik, V. [Institute of Electrical Engineering, Slovak Academy of Sciences, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Uspenskaya, L. [Institute of Solid State Physics, Russian Academy of Sciences, 142432 Chernogolovka, Moscow (Russian Federation); Nedkov, I. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Chromik, Š. [Institute of Electrical Engineering, Slovak Academy of Sciences, Dúbravská cesta 9, 841 04 Bratislava (Slovakia)

    2014-03-15

    Highlights: • Current (spin) injection effect in LSMO/YBCO was studied by impedance measurements. • Complex impedance of YBCO increases at current injection from LSMO to YBCO at 77 K. • This increase is due to an increase of the quasiparticle conductivity of YBCO. • Injection does not significantly affect the relaxation time of the quasiparticles. - Abstract: The DC current injection effect from a ferromagnetic (FM) La{sub 0.7}Sr{sub 0.3}MnO{sub 3} (LSMO) to a high temperature superconducting (HTS) Y{sub 1}Ba{sub 2}Cu{sub 3}O{sub 7−x} (YBCO) thin film was investigated by the microwave surface impedance measurements in a FM/HTS structure, formed as a microstrip resonator for improving the sensitivity of the experiments. The quality factor and the resonance frequency of this structure were found to strongly depend on the current strength, injected from the LSMO electrode into the HTS microstrip electrode. The magnetic penetration depth and the quasiparticle conductivity of the HTS component were determined to increase under DC current injection process, which in all probability stimulated breaking of Cooper pairs and led to a decrease of the superfluid concentration and an increase of the normal fluid concentration without significantly affecting the relaxation time of the quasiparticles.

  4. Resistive switching phenomenon and hole wind effect in YBCO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Truchly, Martin; Plecenik, Tomas [Department of Experimental Physics, Comenius University, Bratislava (Slovakia); Zhitlukhina, Elena [Donetsk Institute for Physics and Engineering, Kyiv (Ukraine)

    2016-07-01

    We present an overview of our experimental and theoretical activities aimed to clarify the mechanism of resistive memory effects in YBCO thin layers. The phenomenon was studied by scanning spreading resistance microscopy (SSRM) and scanning tunneling microscopy (STM) techniques. The most striking feature uncovered (in contrast to previous experiments on planar bilayers with YBCO films) was the opposite voltage-bias polarity of the switching effect in all SSRM and a number of STM measurements. Observed hysteresis in current-voltage characteristics is interpreted as a movement of oxygen vacancies in the vicinity of the tip-YBCO contact. Since the charge distribution in YBCO samples is expected to be strongly inhomogeneous, the balance between the direct electrostatic force on activated oxygen ions and that caused by momentum exchange with the current carriers (holes) hitting them determines direction in which the oxygen vacancies are moving. We propose a minimalist model with the only fitting parameter that accounts for the resistance hysteresis phenomenon in the YBCO films studied.

  5. Coaxial magnetic brakes using single-domain YBCO

    International Nuclear Information System (INIS)

    Putman, P.T.; Salama, K.

    2008-01-01

    In coaxial magnetic brakes, the changing field produced by movement of a solenoidal magnet induces a current in the wall of a conductive tube. The interaction of the field and current leads to a repulsive force that slows the motion of the magnet. For brake applications that require high force density, melt-textured YBCO is a clear choice of material for the magnet because it can carry high currents at a given field and temperature, and is inherently capable of operating in persistent current mode. We present calculations of the performance of this type of brake as a function of magnet current density for catch tubes composed of aluminum and titanium. These results are validated with low speed (20 m/s) tests. Calculations indicate that melt-textured magnets can decelerate projectiles with a mass of 1 kg from 2000 m/s to rest in distances on the order of 10 m. This suggests that this type of brake is suitable for use in hypervelocity experiments, which sometimes requires nondestructive deceleration of projectiles for diagnostic purposes

  6. In-plane optical response in underdoped YBCO

    Science.gov (United States)

    Kakeshita, Teruhisa; Masui, Takahiko; Tajima, Setsuko

    2005-03-01

    The recent STM experiments demonstrated that the electronic state in CuO2 plane is inhomogeneous [1], which becomes conspicuous in the underdoped regime. In such an inhomogeneous state, it is not obvious whether a superfluid density is correctly estimated by a conventional way. We investigated the in-plane optical response for underdoped YBCO crystal to discuss the relation between inhomogeneity and superfluid density in the pseudo-gapped state. The a-axis optical spectrum shows a larger residual conductivity than that for the optimum doping. The superfluid density estimated from our optical spectrum at the lowest temperature is substantially smaller than that determined by μSR. We discuss this strongly suppressed superfluid density and the large residual conductivity in terms of the inhomogeneity in real- and k-space. This work was supported by the New Energy and Industrial Technology Development Organization(NEDO) through ISTEC as the Collaborative Research and Development of Fundamental Technologies for Superconductivity Applications. [1]K.M.Lang et al., Nature 415, 412 (2002). *present address: Dept. of Physics, Osaka University, Machikaneyama 1-1, Toyonaka, Osaka 560-0043, Japan

  7. Structure and oxygen incorporation in low pressure sputtered YBCO films

    International Nuclear Information System (INIS)

    Chaudhary, S.; Pandya, D. K.; Kashyap, S. C.

    2002-01-01

    Thin films of YBa 2 Cu 3 O 7- δ (YBCO) have been successfully grown by reactive RF-magnetron sputtering technique at low pressure. The oxygen partial pressure of 0.95 mTorr, a total pressure (argon and oxygen) of 1.9 mTorr, and a substrate temperature of 775 grad C resulted in good quality films with T C (R=0) = 85.3 K and J Cmag (4.2 K) ≅ 2x10 7 A/cm 2 . The incorporation of oxygen in the as-grown films has been controlled by using different ambient - oxygen, air or argon during in-situ cooling. The superconducting behaviour of the films was studied using resistance-temperature and low field ac-susceptibility measurements and correlated with their structure. All the films exhibited metallic conduction in the normal state. The oxygen- and air- cooled films were superconducting, possessing the usual orthorhombic structure. The argon-cooled films were non-superconducting possessing the tetragonal structure, thus implying that the structure of the film during deposition is tetragonal which transforms to either of the oxygen rich orthorhombic-I or -II phases depending upon the oxygen/air ambient. The 'δ' values of 0.14, 0.32 and 0.70 and higher 'c'-parameters of 1.1785, 1.180 and 1.183 nm have been obtained for oxygen, air and argon cooled films respectively. (Authors)

  8. A neutron depolarization study of magnetic inhomogeneities in weak-link superconductors. Issledovanie magnitnykh neodnorodnostej v sverkhprovodnikakh so slabymi svyazyami metodom depolyarizatsii nejtronov

    Energy Technology Data Exchange (ETDEWEB)

    Zhuchenko, N K; Yagud, R Z [AN SSSR, Leningrad (Russian Federation). Inst. Yadernoj Fiziki

    1993-09-01

    Neutron depolarization measurements in the mixed state of both high-T[sub c] and low-T[sub c] weak-link superconductors have been carried out. Samples of YBCO, BSCCO, SnMo[sub 6]S[sub 8] and 0.5 Nb-0.5 Ti of different magnetic prehistory were analyzed at temperatures T 4.2 K under applied magnetic fields II <= 16.5 kOe. We ascribe the appearance of magnetic inhomogeneities and their hysteresis behaviour to the interaction between dipole magnetic fields (diamagnetic and paramagnetic ones) and applied magnetic fields.

  9. Neutron Depolarization in Superconductors

    Science.gov (United States)

    Zhuchenko, N. K.

    1995-04-01

    The dependences of neutron depolarization on applied magnetic field are deduced along the magnetization hysteresis loop in terms of the Bean model of the critical state. The depolarization in uniaxial superconductors with the reversible magnetization, including uniaxial magnetic superconductors, is also considered. A strong depolarization is expected if the neutrons travel along the vortex lines. On calcule la dépendance en champ magnétique de la dépolarisation des neutrons le long du cycle d'hystérésis en termes du modèle critique de Bean. On considère aussi la dépolarisation dans les supraconducteurs uniaxiaux en fonction de l'aimantation réversible, y compris pour les supraconducteurs magnétiques. On attend une forte dépolarisation si les neutrons se propagent le long des vortex.

  10. Vortices and nanostructured superconductors

    CERN Document Server

    2017-01-01

    This book provides expert coverage of modern and novel aspects of the study of vortex matter, dynamics, and pinning in nanostructured and multi-component superconductors. Vortex matter in superconducting materials is a field of enormous beauty and intellectual challenge, which began with the theoretical prediction of vortices by A. Abrikosov (Nobel Laureate). Vortices, vortex dynamics, and pinning are key features in many of today’s human endeavors: from the huge superconducting accelerating magnets and detectors at the Large Hadron Collider at CERN, which opened new windows of knowledge on the universe, to the tiny superconducting transceivers using Rapid Single Flux Quanta, which have opened a revolutionary means of communication. In recent years, two new features have added to the intrinsic beauty and complexity of the subject: nanostructured/nanoengineered superconductors, and the discovery of a range of new materials showing multi-component (multi-gap) superconductivity. In this book, leading researche...

  11. Intermediate Phase Study on YBCO Films Coated by Precursor Solutions With F/Ba Atomic Ratio of 2

    DEFF Research Database (Denmark)

    Wu, W.; Feng, F.; Zhao, Y.

    2016-01-01

    In the chemical solution deposition process of YBCO superconducting films, fluorine is widely regarded to be of significant importance in avoiding the formation of BaCO3, which hinders the growth of high-quality YBCO films. On the other hand, great efforts have been made to decrease the fluorine......) could be routinely obtained on lanthanum aluminate single-crystal substrates....

  12. Radiation behavior of superconductors

    International Nuclear Information System (INIS)

    Scanlan, R.M.; Raymond, E.L.

    1979-01-01

    High energy neutron irradiations have been performed on Nb 3 Sn superconductors to assess their behavior in a fusion reactor environment. Irradiations were performed at 4.2 K and property measurements were made without warming the samples. The critical current I/sub c/ increased with irradiation to a level about 50% above the unirradiated value at the highest fluences reached in our experiments. These results are compared with the results of other low temperature irradiations of Nb 3 Sn

  13. Strongly disordered superconductors

    International Nuclear Information System (INIS)

    Muttalib, K.A.

    1982-01-01

    We examine some universal effects of strong non-magnetic disorder on the electron-phonon and electron-electron interactions in a superconductor. In particular we explicitly take into account the effect of slow diffusion of electrons in a disordered medium by working in an exact impurity eigenstate representation. We find that the normal diffusion of electrons characterized by a constant diffusion coefficient does not lead to any significant correction to the electron-phonon or the effective electron-electron interactions in a superconductor. We then consider sufficiently strong disorder where Anderson localization of electrons becomes important and determine the effect of localization on the electron-electron interactions. We find that due to localization, the diffusion of electrons becomes anomalous in the sense that the diffusion coefficient becomes scale dependent. This results in an increase in the effective electron-electron interaction with increasing disorder. We propose that this provides a natural explanation for the unusual sensitivity of the transition temperature T/sub c/ of the high T/sub c/ superconductors (T/sub c/ > 10 0 K) to damage effects

  14. Field dependence of the current density of superconductors at high temperatures

    International Nuclear Information System (INIS)

    Hiergeist, R.; Hergt, R.; Erb, A.; Kummeth, P.; Winzer, K.

    1993-01-01

    An essential drawback of the high-T c superconductors (HTS) with respect to technical applications at liquid nitrogen temperature is the large degradation of their pinning properties in magnetic fields. For the field dependence of the volume pinning force often a high field tail due to thermally activated flux flow is observed. An exponential decay of the irreversible magnetization with increasing field was reported in the case of sintered material (YBCO) for the intergranular part of the magnetization while a power law decay was found for the intragranular part. Song et al. observed an exponential field dependence of the critical current density for proton-irradiated material which before irradiation showed a power law decay. Gladun et al. found an exponential decay for BSCCO-2223 tapes. The high field behaviour of BSCCO was shown to be governed by thermally activated flux creep with a logarithmic pinning barrier, which may result in an exponential decrease of the current with the external magnetic field, as argued recently by Ries et al. We will show in the present paper that the different HTS substance classes (YBCO, BSCCO, TBCCO) behave qualitatively in a similar way. (orig.)

  15. Vortex transport entropy in the H-T diagram of high T{sub c} superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Bridoux, G; Nieva, G; Cruz, F de la, E-mail: gbridoux@yahoo.com.a [Centro Atomico Bariloche and Instituto Balseiro, Comision Nacional de Energia Atomica, Av. E. Bustillo 9500, R84002AGP S. C. de Bariloche (Argentina)

    2009-05-01

    The combination of Nernst effect and electrical resistivity measurements allows to extract the transport entropy carried by moving vortices. In high T{sub c} superconductors, the vortex-like fluctuations close and above T{sub c} can be detected with these tools if local phase coherence is still present. In this work we study the vortex transport entropy in the two milestone high T{sub c}, YBa{sub 2}Cu{sub 3}O{sub 7-d}elta (YBCO) and Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8+d}elta (BSCCO). While below T{sub c} the YBCO entropy displays a mean field like behavior, close and above T{sub c} the entropy reveals typical features of strong superconducting fluctuations. The lower dimensionality in BSCCO enhances the strength of superconducting fluctuations in a wider region of the H - Tdiagram and a mean field treatment can not be applied. In this region the vortex transport entropy remains unaffected by the presence of correlated defects.

  16. Influence of stabilizer thickness on over-current test of YBCO-coated conductors

    International Nuclear Information System (INIS)

    Kwon, N Y; Kim, H S; Kim, K L; Lee, H G; Yim, S W; Kim, H-R; Hyun, O-B; Kim, H M

    2009-01-01

    The increased use of distributed power generation has led to increasingly high fault current levels. A superconducting fault current limiter (SFCL) is a potential solution to prevent the problem of short-circuit currents. YBCO-coated conductors (CCs) are one of the most promising superconducting materials for SFCLs. Most YBCO CCs have stabilizers, which play a significant role in limiting the fault current in the SFCL. Therefore, the selection of the appropriate material and the thickness of the stabilizer of the CC used for the SFCL may affect its quench/recovery characteristics. In this paper, the quench/recovery characteristics of YBCO CC tapes having stabilizers with various thicknesses were investigated. The quench/recovery test results showed that, as the thickness of the stabilizer decreased, both the final approach temperature and the recovery time decreased.

  17. An all-field-range description of the critical current density in superconducting YBCO films

    International Nuclear Information System (INIS)

    Golovchanskiy, I A; Pan, A V; Shcherbakova, O V; Fedoseev, S A; Dou, S X

    2011-01-01

    A new critical current density (J c ) model for high-quality YBCO (YBa 2 Cu 3 O 7 ) thin films has been proposed, combining thermally activated flux creep with a vortex pinning potential for columnar defects. The pinning for thermally activated vortices has been described as strong pinning on chains of individual edge dislocations that form low-angle domain boundaries in high-quality YBCO thin films. The model yields an adequate description of the J c behaviour over the whole applied field range, as verified by direct measurements of J c in YBCO thin films grown by pulsed-laser deposition. It also indicates that the effective pinning landscape changes under the influence of the external conditions. Remarkably, the pinning potential obtained from the model is consistent with the values obtained for columnar defects, which confirms the validity of the overall approach.

  18. The effect of a thin silver layer on the critical current of epitaxial YBCO films

    International Nuclear Information System (INIS)

    Polturak, E.; Koren, G.; Cohen, D.; Cohen, D.; Snapiro, I.

    1992-01-01

    We compare measurements of the critical current density of an epitaxial YBCO film with that of an identical film overlaid by a thin silver layer. We find that the presence of the silver lowers Tc of the film by about 1.5 K, which is two orders of magnitude larger than predicted by the theory of the proximity effect for our experimental conditions. In addition, J c of the Ag/YBCO film near Tc is also significantly lower than that of the bare YBCO film. We propose two alternate interpretations of this effect, one in terms of destabilization of the flux distribution in the film and the other making use of the effect of the silver on the Bean-Livingston surface barrier for the initial penetration of flux. The latter seems the more plausible explanation of our results. (orig.)

  19. Mechanical characterization of YBCO thin films using nanoindentation and finite element method

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Weixing [The Ministry of Education of China (China). Key Lab. of Mechanics on Environment and Disaster in Western China; Lanzhou Univ. (China). College of Civil Engineering and Mechanics

    2017-09-15

    The mechanical properties of YBCO thin film deposited on SrTiO{sub 3} (100) substrates by magnetron sputtering were determined using Berkovich nanoindentation and scanning electron microscopy. Hardness and elastic modulus were determined via the Oliver-Pharr method from indentation load-depth curves. The hardness values of the YBCO thin film show depth dependence, i. e., indentation size effect, which arose from the surface roughness as detected by scanning electron microscopy. Multiple pop-in events were observed on the loading curves, however, no obvious pop-out takes place during the elastic recovery. In addition, an effective analytical method accommodating the indenter imperfection was proposed and validated against experimental data in terms of elastic modulus, yield stress and friction angle using the Drucker-Prager yield criterion for the YBCO thin film.

  20. Finite-element analysis and comparison of the AC loss performance of BSCCO and YBCO conductors

    International Nuclear Information System (INIS)

    Stavrev, Svetlomir; Grilli, Francesco; Dutoit, Bertrand; Ashworth, Stephen

    2006-01-01

    The AC loss performance of two BSCCO and two YBCO conductors of different geometry, characterized by the same self-field critical current of 150 A, is analysed and compared quantitatively. The comparison is made using the finite-element method with a nonlinear B-dependent E-J relation. A new shell-region model is utilised for the simulations of thin YBCO strips. Different AC working conditions are simulated: self-field, applied external field, and combined transport current and external perpendicular field application. Magnetic field and current density profiles are investigated in order to illustrate the reasons for the loss difference in the conductors. Depending on the application, the advantages of using BSCCO or YBCO conductors with specific geometry are outlined