  1. Development of Underwater Laser Cladding and Underwater Laser Seal Welding Techniques for Reactor Components

    Science.gov (United States)

    Hino, Takehisa; Tamura, Masataka; Tanaka, Yoshimi; Kouno, Wataru; Makino, Yoshinobu; Kawano, Shohei; Matsunaga, Keiji

    Stress corrosion cracking (SCC) has been reported at the aged components in many nuclear power plants. Toshiba has been developing the underwater laser welding. This welding technique can be conducted without draining the water in the reactor vessel. It is beneficial for workers not to exposure the radiation. The welding speed can be attaining twice as fast as that of Gas Tungsten Arc Welding (GTAW). The susceptibility of SCC can also be lower than the Alloy 600 base metal.

  2. Development of End Plug Welding Technique for SFR Fuel Rod Fabrication

    Directory of Open Access Journals (Sweden)

    Jung Won Lee

    2016-01-01

    Full Text Available In Korea, R&D on a sodium-cooled fast reactor (SFR was begun in 1997, as one of the national long-term nuclear R&D programs. As one fuel option for a prototype SFR, a metallic fuel, U-Zr alloy fuel, was selected and is currently being developed. For the fabrication of SFR metallic fuel rods, the end plug welding is a crucial process. The sealing of the end plug to the cladding tube should be hermetically perfect to prevent a leakage of fission gases and to maintain a good reactor performance. In this study, the welding technique, welding equipment, welding conditions, and parameters were developed for the end plug welding of SFR metallic fuel rods. A gas tungsten arc welding (GTAW technique was adopted and the welding joint design was developed. In addition, the optimal welding conditions and parameters were established. Based on the establishment of the welding conditions, the GTAW technique was qualified for the end plug welding of SFR metallic fuel rods.

  3. Development of laser welding techniques for vanadium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Strain, R.V.; Leong, K.H.; Smith, D.L. [Argonne National Laboratory, IL (United States)

    1996-10-01

    Laser welding is potentially advantageous because of its flexibility and the reduced amount of material affected by the weld. Bead-on-plate and butt welds were previously performed to depths of about 4 mm with a 6-kW CO{sub 2} laser on V-4%Cr-4%Ti and V-5%Cr-5%Ti alloys. These welds were made at a speed of 0.042 m/s using argon purging at a flow rate of 2.8 m{sup 3}/s. The purge was distributed with a diffuser nozzle aimed just behind the laser beam during the welding operation. The fusion zones of welds made under these conditions consisted of very fine, needle-shaped grains and were also harder than the bulk metal (230-270 dph, compared to {approx}180 dph for the bulk metal). A limited number of impact tests showed that the as-welded ductile-brittle transition temperatures (DBTT) was above room temperature, but heat treatment at 1000{degrees}C for 1 h in vacuum reduced the DBTT to <{minus}25{degrees}C. Activities during this reporting period focused on improvements in the purging system and determination of the effect of welding speed on welds. A 2-kW continuous YAG laser at Lumonics Corp. in Livonia, MI, was used to make 34 test welds for this study.

  4. Development of laser welding techniques for vanadium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Strain, R.V.; Leong, K.H.; Smith, D.L.

    1996-04-01

    Laser welding is potentially advantageous because of its flexibility and the reduced amount of material affected by the weld. Lasers do not require a vacuum (as do electron beam welders) and the welds they produce high depth-to-width ratios. Scoping with a small pulsed 50 J YAG laser indicated that lasers could produce successful welds in vanadium alloy (V-5%Cr-5%Ti) sheet (1 mm thick) when the fusion zone was isolated from air. The pulsed laser required an isolating chamber filled with inert gas to produce welds that did not contain cracks and showed only minor hardness increases. Following the initial scoping tests, a series of tests were preformed with a 6 kW continuous CO{sub 2} laser. Successful bead-on-plate welds were made on V-4%Cr-4%Ti and V-5%Cr-5%Ti alloys to depths of about 4 mm with this laser.

  5. Mechanical Behaviour Investigation Of Aluminium Alloy Tailor Welded Blank Developed By Using Friction Stir Welding Technique

    Science.gov (United States)

    Dwi Anggono, Agus; Sugito, Bibit; Hariyanto, Agus; Subroto; Sarjito

    2017-10-01

    The objective on the research was to investigate the mechanical properties and microstructure of tailor welded blank (TWB) made from AA6061-T6 and AA1100 using friction stir welding (FSW) process. Due to the dissimilar mechanical properties of the two aluminium alloys, microhardness test was conducted to measure the hardness distribution across the weld nugget. The mixing of two distinct materials was influenced by tool rotation speed. Therefore, microstructure analysis was carried out to investigate the grain size and shape. The grain size of AA6061-T6 has increased in the heat affected zone (HAZ) while for AA1100 has decreased. In the weld nugget, it has found a hook defects in the dissimilar aluminium joining. By using monotonic tensile load, the different weld line direction was observed with the expansion in tool rotation. The joints failure were consistently on the area of AA1100 series. Furthermore, two specimens were investigated, one through the dissimilar aluminium and the other through similiar material. Inspection of the weld nugget hardness was shown that nonhomogen material intermixing during the stiring process as confirmed by microhardness measurement.

  6. SHADOW: a new welding technique

    Science.gov (United States)

    Kramer, Thorsten; Olowinsky, Alexander M.; Durand, Friedrich

    2002-06-01

    The new welding technique 'SHADOW ' is introduced. SHADOW means the use of a single pulse to generate a quasi continuous weld of several millimeters in length. HET processing time is defined by the pulse duration of the pulsed laser. At present, a state-of-the-art laser is capable of a maximum pulse duration of 20 ms. The variation of the laser power depend on time is a vital capability of the pulsed laser to adapt the energy deposition into the workpiece. Laser beam welds of several watch components were successfully performed. Similar metals like crowns and axes made out of stainless steel have been welded using pulsed laser radiation. Applying a series of about 130 single pulses for the crown-axis combination the total energy accumulates to 19.5 J. The use of the SHADOW welding technique reduces the energy to 2.5 J. While welding dissimilar metals like stainless steel and bras, the SHADOW welding reduces drastically the contamination as well as the distortion. Laser beam welding of copper has a low process reliability due to the high reflection and the high thermal conductivity. SHADOW welds of 3.6 mm length were performed on 250 micrometers thick copper plates with very high reproducibility. As a result, a pilot plant for laser beam welding of copper plates has been set up. The work to be presented has partly been funded by the European Commission in a project under the contract BRPR-CT-0634.

  7. Residual stress characterization of welds and post-weld processes using x-ray diffraction techniques

    Science.gov (United States)

    Brauss, Michael E.; Pineault, James A.; Eckersley, John S.

    1998-03-01

    This paper illustrates the importance of residual stress characterization in welds and post weld processes. The failure to characterize residual stresses created during welding and/or post weld processes can lead to unexpected occurrences of stress corrosion cracking, distortion, fatigue cracking as well as instances of over design or over processing. The development of automated residual stress mapping and the availability of portable and fast equipment have now made the characterization of residual stresses using x-ray diffraction practical for process control and optimization. The paper presents examples where x-ray diffraction residual stress characterization techniques were applied on various kinds of welds including arc welds, TIG welds, resistance welds, laser welds and electron beam welds. The nondestructive nature of the x-ray diffraction technique has made the residual stress characterization of welds a useful tool for process optimization and failure analysis, particularly since components can be measured before and after welding and post welding processes. Some examples presented show the residual stresses before and after the application of post weld processes such as shot peening, grinding and heat treatment.

  8. Aluminum alloy weldability. Identification of weld solidification cracking mechanisms through novel experimental technique and model development

    Energy Technology Data Exchange (ETDEWEB)

    Coniglio, Nicolas

    2008-07-01

    The objective of the present thesis is to make advancements in understanding solidification crack formation in aluminum welds, by investigating in particular the aluminum 6060/4043 system. Alloy 6060 is typical of a family of Al-Mg-Si extrusion alloys, which are considered weldable only when using an appropriate filler alloy such as 4043 (Al-5Si). The effect of 4043 filler dilution (i.e. weld metal silicon content) on cracking sensitivity and solidification path of Alloy 6060 welds are investigated. Afterwards, cracking models are developed to propose mechanisms for solidification crack initiation and growth. Cracking Sensitivity. Building upon the concept that silicon improves weldability and that weldability can be defined by a critical strain rate, strain rate-composition combinations required for solidification crack formation in the Al- 6060/4043 system were determined using the newly developed Controlled Tensile Weldability (CTW) test utilizing local strain extensometer measurements. Results, presented in a critical strain rate - dilution map, show a crack - no crack boundary which reveals that higher local strain rates require higher 4043 filler dilution to avoid solidification cracking when arc welding Alloy 6060. Using the established crack - no crack boundary as a line of reference, additional parameters were examined and their influence on cracking characterized. These parameter influences have included studies of weld travel speed, weld pool contaminants (Fe, O, and H), and grain refiner additions (TiAl{sub 3} + Boron). Each parameter has been independently varied and its effect on cracking susceptibility quantified in terms of strain rate - composition combinations. Solidification Path. Solidification path of the Al-6060/4043 system was characterized using thermal analysis and phase identification. Increasing 4043 filler dilution from 0 to 16% in Alloy 6060 arc welds resulted in little effect on thermal arrests and microstructure, no effect on

  9. Development of the manufacture and process for DUPIC fuel elements; development of the quality evaluation techniques for end cap welds of DUPIC fuel elements

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Sang Tae; Choi, Myong Seon; Yang, Hyun Tae; Kim, Dong Gyun; Park, Jin Seok; Kim, Jin Ho [Yeungnam University, Kyongsan (Korea)

    2002-04-01

    The objective of this research is to set up the quality evaluation techniques for end cap welds of DUPIC fuel element. High temperature corrosion test and the SCC test for Zircaloy-4 were performed, and also the possibility of the ultrasonic test technique was verified for the quality evaluation and control of the laser welds in the DUPIC fuel rod end cap. From the evaluation of corrosion properties with measuring the weight gain and observing oxide film of the specimen that had been in the circumstance of steam(400 .deg. C, 1,500 psi) by max. 70 days later, the weight gain of the welded specimens was larger than original tube and the weight increasing rate increased with the exposed days. For the Development of techniques for ultrasonic test, semi-auto ultrasonic test system has been made based on immersion pulse-echo technique using spherically concentrated ultrasonic beam. Subsequently, developed ultrasonic test technique is quite sensible to shape of welds in the inside and outside of tube as well as crack, undercut and expulsion, and also this ultrasonic test, together with metallurgical fracture test, has good reliance as enough to be used for control method of welding process. 43 refs., 47 figs., 8 tabs. (Author)

  10. ITER lip seal welding and cutting developments

    Energy Technology Data Exchange (ETDEWEB)

    Levesy, B.; Cordier, J.J.; Jokinen, T. [ITER Organization, Route de Vinon sur Verdon, 13115 Saint Paul Lez Durance (France); Kujanpää, V.; Karhu, M. [VTT Technical Research Centre of Finland (Finland); Le Barbier, R. [ITER Organization, Route de Vinon sur Verdon, 13115 Saint Paul Lez Durance (France); Määttä, T. [VTT Technical Research Centre of Finland (Finland); Martins, J.P.; Utin, Y. [ITER Organization, Route de Vinon sur Verdon, 13115 Saint Paul Lez Durance (France)

    2015-10-15

    Highlights: • Different TIG and Laser welding techniques are tested. • Twin spot laser welding techniques is the best. • Limited heat input gives a stable weld pool in all positions. • Penetrations is achieved. • Lip seal welding and cutting with a robotic arm is successfully performed on a representative mock-up. - Abstract: The welded lip seals form part of the torus primary vacuum boundary in between the port plugs and the vacuum vessel, and are classified as Protection Important Component. In order to refurbish the port plugs or the in-vessel components, port plugs have to be removed from the machine. The lip seal design must enable up to ten opening of the vacuum vessel during the life time operation of the ITER machine. Therefore proven, remote reliable cutting and re-welding are essential, as these operations need to be performed in the port cells in a nuclear environment, where human presence will be restricted. Moreover, the combination of size of the components to be welded (∼10 m long vacuum compatible thin welds) and the congested environment close to the core of the machine constraint the type and size of tools to be used. This paper describes the lip seal cutting and welding development programme performed at the VTT Technical Research Centre, Finland. Potential cutting and welding techniques are analyzed and compared. The development of the cutting, TIG and laser welding techniques on samples are presented. Effects of lip seal misalignments and optimization of the 2 welding processes are discussed. Finally, the manufacturing and test of the two 1.2 m × 1 m representative mock-ups are presented. The set-up and use of a robotic arm for the mock-up cutting and welding operations are also described.

  11. Secondary ledeburite formation during various welding techniques

    Directory of Open Access Journals (Sweden)

    Tonkovič M.P.

    2015-01-01

    Full Text Available The occurrence and formation sequence of secondary ledeburite in the heat affected zone of chromium ledeburitic tool steel W.Nr. 1.2379 (OCR12 VM after welding with SAW, TIG, microplasma and laser welding techniques is presented in this paper. Special attention was paid on the behaviour of carbides. The occurrence of secondary ledeburite is a result of local enrichment of the austenite matrix with alloying elements, due to partial or complete dissolution of primary/eutectic carbides. The results show that the largest amount of secondary ledeburite is formed during submerged arc welding, followed by TIG and microplasma welding technique. Welding by laser technique, with appropriate technological parameters, could prevent secondary ledeburite formation.

  12. Review of techniques for on-line monitoring and inspection of laser welding

    Science.gov (United States)

    Shao, J.; Yan, Y.

    2005-01-01

    Laser welding has been applied to various industries, in particular, automotive, aerospace and microelectronics. However, traditional off-line testing of the welds is costly and inefficient. Therefore, on-line inspection systems with low cost have being developed to increase productivity and maintain high welding quality. This paper presents the applications of acoustic, optical, visual, thermal and ultrasonic techniques and latest development of laser welding monitoring. The advantages and limitations of these techniques are also discussed.

  13. Solar array welding developement

    Science.gov (United States)

    Elms, R. V., Jr.

    1974-01-01

    The present work describes parallel gap welding as used for joining solar cells to the cell interconnect system. Sample preparation, weldable cell parameter evaluation, bond scheduling, bond strength evaluation, and bonding and thermal shock tests are described. A range of weld schedule parameters - voltage, time, and force - can be identified for various cell/interconnect designs that will provide adequate bond strengths and acceptably small electrical degradation. Automation of solar array welding operations to a significant degree has been achieved in Europe and will be receiving increased attention in the U.S. to reduce solar array fabrication costs.

  14. Weld procedure development with OSLW - optimization software for laser welding

    Energy Technology Data Exchange (ETDEWEB)

    Fuerschbach, P.W.; Eisler, G.R. [Sandia National Labs., Albuquerque, NM (United States); Steele, R.J. [Naval Air Warfare Center, China Lake, CA (United States)

    1998-06-01

    Weld procedure development can require extensive experimentation, in-depth process knowledge, and is further complicated by the fact that there are often multiple sets of parameters that will meet the weld requirements. Choosing among these multiple weld procedures can be hastened with computer models that find parameters to meet selected weld dimensional requirements while simultaneously optimizing important figures of merit. Software is described that performs this task for CO{sub 2} laser beam welding. The models are based on dimensionless parameter correlations that are derived from solutions to the moving heat source equations. The use of both handbook and empirically verified thermophysical property values allows OSLW to be extended to many different materials. Graphics displays show the resulting solution on contour plots that can be used to further probe the model. The important figures of merit for laser beam welding are energy transfer efficiency and melting efficiency. The application enables the user to input desired weld shape dimensions, select the material to be welded, and to constrain the search problem to meet the application requirements. Successful testing of the software at a laser welding fabricator has validated this tool for weld procedure development.

  15. An Intelligent System for Analyzing Welding Defects using Image Retrieval Techniques

    OpenAIRE

    Pein, Raoul Pascal; Lu, Joan; Stav, John Birger; Xu, Qiang; Uran, Miro; Mráz, Luboš

    2009-01-01

    The development of new approaches in image processing and retrieval provides several opportunities in supporting in different\\ud domains. The group of welding engineers frequently needs to conduct visual inspections to assess the quality of welding products.\\ud It is investigated, if this process can be supported by different kinds of software. Techniques from a generic CBIR system have\\ud been successfully used to cluster welding photographs according to the severeness of visual faults. Simi...

  16. The use of welding techniques in protection of welding structures against corrosion

    Directory of Open Access Journals (Sweden)

    J.St. Kowalski

    2010-07-01

    Full Text Available The paper presents possibilities of using welding techniques as a means of protection from corrosion of materials for welding structuresoperating in power engineering industry, chemical industry and shipbuilding. Based on the example of an LNG installation, the potentials of weld overlaying in anti-corrosive protection of parts operating in LNG installations have been described. The weld overlaying technique enables building up of protective coatings, which not only protect material from corrosion resulting from the flow of more or less aggressive medium (e.g. water, exhaust gas but also increase the performance life of thus “coated” elements due to the improved abrasion wear resistance of weld overlays. The weld overlaying process is equally well suitable in building of new structures as in the repair of damaged or worn out elements of water or power feeding installations.

  17. Complete Report on the Development of Welding Parameters for Irradiated Materials

    Energy Technology Data Exchange (ETDEWEB)

    Frederick, Greg [Electric Power Research Inst. (EPRI), Knoxville, TN (United States); Sutton, Benjamin J. [Electric Power Research Inst. (EPRI), Knoxville, TN (United States); Tatman, Jonathan K. [Electric Power Research Inst. (EPRI), Knoxville, TN (United States); Vance, Mark Christopher [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Clark, Scarlett R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Feng, Zhili [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Miller, Roger G. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Chen, Jian [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Tang, Wei [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Gibson, Brian T. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-11-01

    The advanced welding facility at the Radiochemical Engineering Development Center of Oak Ridge National Laboratory, which was conceived to enable research and development of weld repair techniques for nuclear power plant life extension, is now operational. The development of the facility and its advanced welding capabilities, along with the model materials for initial welding trials, were funded jointly by the U.S. Department of Energy, Office of Nuclear Energy, Light Water Reactor Sustainability Program, the Electric Power Research Institute, Long Term Operations Program and the Welding and Repair Technology Center, with additional support from Oak Ridge National Laboratory. Welding of irradiated materials was initiated on November 17, 2017, which marked a significant step in the development of the facility and the beginning of extensive welding research and development campaigns on irradiated materials that will eventually produce validated techniques and guidelines for weld repair activities carried out to extend the operational lifetimes of nuclear power plants beyond 60 years. This report summarizes the final steps that were required to complete weld process development, initial irradiated materials welding activities, near-term plans for irradiated materials welding, and plans for post-weld analyses that will be carried out to assess the ability of the advanced welding processes to make repairs on irradiated materials.

  18. Improved electron-beam welding technique

    Science.gov (United States)

    Schumacher, B.

    1970-01-01

    Electron-beam generator produces high quality welds without vaporization by relying on the mobility and hydrodynamic properties of the material in its liquid phase. The power density of the beam is relative to the speed of the workpiece, producing an inclined weld-front.

  19. New technique of skin embedded wire double-sided laser beam welding

    Science.gov (United States)

    Han, Bing; Tao, Wang; Chen, Yanbin

    2017-06-01

    In the aircraft industry, double-sided laser beam welding is an approved method for producing skin-stringer T-joints on aircraft fuselage panels. As for the welding of new generation aluminum-lithium alloys, however, this technique is limited because of high hot cracking susceptibility and strengthening elements' uneven distributions within weld. In the present study, a new technique of skin embedded wire double-sided laser beam welding (LBW) has been developed to fabricate T-joints consisting of 2.0 mm thick 2060-T8/2099-T83 aluminum-lithium alloys using eutectic alloy AA4047 filler wire. Necessary dimension parameters of the novel groove were reasonably designed for achieving crack-free welds. Comparisons were made between the new technique welded T-joint and conventional T-joint mainly on microstructure, hot crack, elements distribution features and mechanical properties within weld. Excellent crack-free microstructure, uniform distribution of silicon and superior tensile properties within weld were found in the new skin embedded wire double-sided LBW T-joints.

  20. CLOSURE WELD DEVELOPMENT FOR 3013 OUTER CONTAINERS

    Energy Technology Data Exchange (ETDEWEB)

    Daugherty, W.; Howard, S.; Peterson, K.; Stokes, M.

    2009-11-10

    Excess plutonium materials in the DOE complex are packaged and stored in accordance with DOE-STD-3013. This standard specifies requirements for the stabilization of such materials and subsequent packaging in dual nested seal-welded containers. Austenitic stainless steels have been selected for container fabrication. The inner 3013 container provides contamination control while the outer 3013 container is the primary containment vessel and is the focus of this paper. Each packaging site chose a process for seal welding the outer 3013 containers in accordance with its needs and expertise. The two processes chosen for weld closure were laser beam welding (LBW) and gas tungsten arc welding (GTAW). Following development efforts, each system was qualified in accordance with DOE-STD-3013 prior to production use. The 3013 outer container closure weld joint was designed to accommodate the characteristics of a laser weld. This aspect of the joint design necessitated some innovative process and equipment considerations in the application of the GTAW process. Details of the weld requirements and the development processes are presented and several potential enhancements for the GTAW system are described.

  1. Lasers in car body construction - substitution of conventional welding techniques or supplement

    Energy Technology Data Exchange (ETDEWEB)

    Imhoff, R.; Behler, K.; Beyer, E.

    1988-09-01

    In car body construction, laser beam welding competes with resistance spot welding and with projection welding. There are problems concerning the short bridging distance of the laser beam welding, but there are also some advantages, i.e.: lower weight; higher strength and stiffness of the car body; high welding speed (5 to 10 m/min); triple-pass welding; welding at a present depth for attaching reinforcing elements on the inside of visible car parts for the purpose of vibration and noise damping; good process control characteristics. In the long run, laser beam welding is expected to replace conventional welding techniques in car body construction.

  2. Electron Beam Welding: study of process capability and limitations towards development of nuclear components

    Science.gov (United States)

    Vadolia, Gautam R.; Premjit Singh, K.

    2017-04-01

    Electron Beam Welding (EBW) technology is an established and widely adopted technique in nuclear research and development area. Electron beam welding was thought of as a candidate process for ITER Vacuum Vessel Fabrication. Dhruva Reactor at BARC, Mumbai and Niobium superconducting accelerator cavity at BARC has adopted the EB welding technique as a fabrication route. Study of process capability and limitations based on available literature is consolidated in this short review paper.

  3. Laser welding and syncristallization techniques comparison: "Ex vivo" study.

    Science.gov (United States)

    Fornaini, Carlo; Meleti, Marco; Vescovi, Paolo; Merigo, Elisabetta; Rocca, Jean-Paul

    2013-12-30

    Stabilization of implant abutments through electric impulses at high voltage for a very short time (electrowelding) was developed in the Eighties. In 2009, the same procedure was performed through the use of laser (laser welding) The aim of this study is to compare electrowelding and laser welding for intra-oral implant abutments stabilization on "ex vivo models" (pig jaws). Six bars were welded with two different devices (Nd:YAG laser and Electrowelder) to eighteen titanium implant abutment inserted in three pig jaws. During the welding process, thermal increase was recorded, through the use of k-thermocouples, in the bone close to the implants. The strength of the welded joints was evaluated by a traction test after the removal of the implants. For temperature measurements a descriptive analysis and for traction test "values unpaired t test with Welch's correction" were performed: the significance level was set at Pwelding gives a lower thermal increase than Electrowelding at the bone close to implants (Mean: 1.97 and 5.27); the strength of laser welded joints was higher than that of Electrowelding even if nor statistically significant. (Mean: 184.75 and 168.29) CONCLUSION: Electrowelding seems to have no advantages, in term of thermal elevation and strength, while laser welding may be employed to connect titanium implants for immediate load without risks of thermal damage at surrounding tissues.

  4. Laser welding and syncristallization techniques comparison: in vitro study.

    Science.gov (United States)

    Fornaini, C; Merigo, E; Vescovi, P; Meleti, M; Nammour, S

    2012-01-01

    Background. Laser welding was first reported in 1967 and for many years it has been used in dental laboratories with several advantages versus the conventional technique. Authors described, in previous works, the possibility of using also chair-side Nd : YAG laser device (Fotona Fidelis III, λ = 1064 nm) for welding metallic parts of prosthetic appliances directly in the dental office, extra- and also intra-orally. Syncristallisation is a soldering technique based on the creation of an electric arc between two electrodes and used to connect implants to bars intra-orally. Aim. The aim of this study was to compare two different laser welding devices with a soldering machine, all of these used in prosthetic dentistry. Material and Methods. In-lab Nd : YAG laser welding (group A = 12 samples), chair-side Nd : YAG laser welding (group B = 12 samples), and electrowelder (group C = 12 samples) were used. The tests were performed on 36 CrCoMo plates and the analysis consisted in evaluation, by microscopic observation, of the number of fissures in welded areas of groups A and B and in measurement of the welding strength in all the groups. The results were statistically analysed by means of one-way ANOVA and Tukey-Kramer multiple comparison tests. Results. The means and standard deviations for the number of fissures in welded areas were 8.12 ± 2.59 for group A and 5.20 ± 1.38 for group B. The difference was statistical significant (P = 0.0023 at the level 95%). On the other hand, the means and standard deviations for the traction tests were 1185.50 ± 288.56 N for group A, 896.41 ± 120.84 N for group B, and 283.58 ± 84.98 N for group C. The difference was statistical significant (P = 0.01 at the level 95%). Conclusion. The joint obtained by welding devices had a significant higher strength compared with that obtained by the electrowelder, and the comparison between the two laser devices used demonstrated that the chair-side Nd : YAG, even giving

  5. Laser Welding and Syncristallization Techniques Comparison: In Vitro Study

    Directory of Open Access Journals (Sweden)

    C. Fornaini

    2012-01-01

    Full Text Available Background. Laser welding was first reported in 1967 and for many years it has been used in dental laboratories with several advantages versus the conventional technique. Authors described, in previous works, the possibility of using also chair-side Nd : YAG laser device (Fotona Fidelis III, =1064 nm for welding metallic parts of prosthetic appliances directly in the dental office, extra- and also intra-orally. Syncristallisation is a soldering technique based on the creation of an electric arc between two electrodes and used to connect implants to bars intra-orally. Aim. The aim of this study was to compare two different laser welding devices with a soldering machine, all of these used in prosthetic dentistry. Material and Methods. In-lab Nd : YAG laser welding (group A = 12 samples, chair-side Nd : YAG laser welding (group B = 12 samples, and electrowelder (group C = 12 samples were used. The tests were performed on 36 CrCoMo plates and the analysis consisted in evaluation, by microscopic observation, of the number of fissures in welded areas of groups A and B and in measurement of the welding strength in all the groups. The results were statistically analysed by means of one-way ANOVA and Tukey-Kramer multiple comparison tests. Results. The means and standard deviations for the number of fissures in welded areas were 8.12±2.59 for group A and 5.20±1.38 for group B. The difference was statistical significant (=0.0023 at the level 95%. On the other hand, the means and standard deviations for the traction tests were 1185.50±288.56 N for group A, 896.41±120.84 N for group B, and 283.58±84.98 N for group C. The difference was statistical significant (=0.01 at the level 95%. Conclusion. The joint obtained by welding devices had a significant higher strength compared with that obtained by the electrowelder, and the comparison between the two laser devices used demonstrated that the chair-side Nd : YAG, even giving a

  6. The influence of the weld toe grinding and wig remelting weld toe rehabilitation techniques, on variable stresses, in case of cross fillet welds, reinforced with additional welding rows

    Directory of Open Access Journals (Sweden)

    Babis Claudiu

    2017-01-01

    Full Text Available Variable stresses where the load value varies between a maximum and a minimum value, or varies the position in time, cause after accumulating a large number of load cycles in those structures, the emergence of drug fatigue. Fatigue is characterized by failure on values of the applied stress from the load cycles, below the material flow, values which in case of static stress would not have caused problems. Knowing that the variable stressed structures are sensitive to stress concentrators, the paper aims to highlight the influence of two techniques to reduce stress concentrator weld toe grinding and WIG remelting weld toe, on the behavior of variable tensile test of cross corner welded specimens, reinforced with additional welding rows.

  7. Welding processes handbook

    CERN Document Server

    Weman, Klas

    2011-01-01

    Offers an introduction to the range of available welding technologies. This title includes chapters on individual techniques that cover principles, equipment, consumables and key quality issues. It includes material on such topics as the basics of electricity in welding, arc physics, and distortion, and the weldability of particular metals.$bThe first edition of Welding processes handbook established itself as a standard introduction and guide to the main welding technologies and their applications. This new edition has been substantially revised and extended to reflect the latest developments. After an initial introduction, the book first reviews gas welding before discussing the fundamentals of arc welding, including arc physics and power sources. It then discusses the range of arc welding techniques including TIG, plasma, MIG/MAG, MMA and submerged arc welding. Further chapters cover a range of other important welding technologies such as resistance and laser welding, as well as the use of welding techniqu...

  8. Characterisation of submerged arc welding process using infrared imaging technique

    CSIR Research Space (South Africa)

    Zondi, MC

    2017-09-01

    Full Text Available Infrared (IR) thermography is a technique used to measure temperature distribution of heat generation in manufacturing processes such as welding. IR thermography is a non-destructive and non-contact method, which makes it favoured for the arc...

  9. Numerical simulation of electron beam welding and instrumental technique

    Energy Technology Data Exchange (ETDEWEB)

    Carin, M.; Rogeon, P.; Carron, D.; Le Masson, P.; Couedel, D. [Universite de Bretagne Sud, Centre de Recherche, Lab. d' Etudes Thermiques Energetique et Environnement, 56 - Lorient (France)

    2004-07-01

    In the present work, thermal cycles measured with thermocouples embedded in specimens are employed to validate a numerical thermo-metallurgical model of an Electron Beam welding process. The implemented instrumentation techniques aim at reducing the perturbations induced by the sensors in place. The numerical model is based on the definition of a heat source term linked to the keyhole geometry predicted by a model of pressure balance using the FEMLAB code. The heat source term is used by the thermo-metallurgical simulation carried out with the finite element code SYSWELD. Kinetics parameters are extracted from dilatometric experiments achieved in welding austenitization conditions at constant cooling rates. (authors)

  10. Advanced Welding Concepts

    Science.gov (United States)

    Ding, Robert J.

    2010-01-01

    Four advanced welding techniques and their use in NASA are briefly reviewed in this poster presentation. The welding techniques reviewed are: Solid State Welding, Friction Stir Welding (FSW), Thermal Stir Welding (TSW) and Ultrasonic Stir Welding.

  11. Tailored Welding Technique for High Strength Al-Cu Alloy for Higher Mechanical Properties

    Science.gov (United States)

    Biradar, N. S.; Raman, R.

    AA2014 aluminum alloy, with 4.5% Cu as major alloying element, offers highest strength and hardness values in T6 temper and finds extensive use in aircraft primary structures. However, this alloy is difficult to weld by fusion welding because the dendritic structure formed can affect weld properties seriously. Among the welding processes, AC-TIG technique is largely used for welding. As welded yield strength was in the range of 190-195 MPa, using conventional TIG technique. Welding metallurgy of AA2014 was critically reviewed and factors responsible for lower properties were identified. Square-wave AC TIG with Transverse mechanical arc oscillation (TMAO) was postulated to improve the weld strength. A systematic experimentation using 4 mm thick plates produced YS in the range of 230-240 MPa, has been achieved. Through characterization including optical and SEM/EDX was conducted to validate the metallurgical phenomena attributable to improvement in weld properties.

  12. Welding.

    Science.gov (United States)

    South Carolina State Dept. of Education, Columbia. Office of Vocational Education.

    This curriculum guide is designed for use by South Carolina vocational education teachers as a continuing set of lesson plans for a two-year course on welding. Covered in the individual sections of the guide are the following topics: an orientation to welding, oxyacetylene welding, advanced oxyacetylene welding, shielded metal arc welding, TIG…

  13. Trends in Development of Weld Overlaying During The 21ST Century

    Directory of Open Access Journals (Sweden)

    Nikolov Mitko

    2014-08-01

    Full Text Available The present article discusses the trends in the development of welding and weld overlaying on the threshold of the new millennium and during it. It presents the trends in the production of welding materials for welding and weld overlaying in industrially developed and developing countries. The structure of welding methods is also shown, giving priority to its development until 2020.

  14. Development of Technology and Equipment of the Automated Laser Welding for Manufacturing Heat Exchanger Details of Marine Engines

    Directory of Open Access Journals (Sweden)

    Shelyagin, V.D.

    2014-09-01

    Full Text Available Based on the developed automated laser welding technology for flat tubes of copper-nickel alloys laser welding complex technological equipment, which can be applied on the enterprises of machine building, aerospace, shipbuilding and automobile industries, was designed and created. To control the integrity of welded flat tubes a technique, which consists in testing sample pressure and finding defective sections by laser interferometry in the automated mode, was developed. Specialized welding head was designed and manufactured for the industrial use of the developed laser welding technology.

  15. Development of field welding technology for rails; Tetsudo rail no genchi yoyu yosetsu gijutsu no kaihatsu

    Energy Technology Data Exchange (ETDEWEB)

    Okumura, M.; Karimine, K.; Uchino, K.; Yurioka, N. [Nippon Steel Corp., Tokyo (Japan)

    1995-02-28

    A new element technology is outlined which is for welding regular rails in the field and making a long rail. A new EAW (Enclosed Arc Welding) has been developed for the purpose of improving vibration and noise due to the local abrasion of the existing EAW and improving the deterioration of resistibility against rolling fatigue breakage and the generation of transverse fissure due to the high temperature liquefaction crack. It has been verified that a highly carbonized metal improves the local abrasion and the generation of crack. Problems were brought up, in the case of welding rails by thermit welding (TW) utilizing the reaction of Al powder and brown iron oxide, such that strength was rather small against the bending fatigue of a joint and that the soundness of internal property of a welded part was likely to fluctuate. A test was carried out concerning the latter problem, and it was revealed that the temperature to pour molten steel dropped, whether the Al compound was insufficient or excessive, possibly causing reaction defects. As a technology to replace EAW and TW techniques, an automatic welding was developed which combinedly used narrow groove electro-slag welding and gas sealed arc welding. Further, as an after-treatment of this technology, a method was developed to remove a weld overlay. 19 refs., 16 figs., 6 tabs.

  16. Optimization of process parameters during vibratory welding technique using Taguchi's analysis

    Directory of Open Access Journals (Sweden)

    Pravin Kumar Singh

    2016-09-01

    Full Text Available With an aim to improve the mechanical properties of a weld joint, a new concept of vibratory setup has been designed which is capable to stir the molten weld pool before it solidifies during shielded metal arc welding (SMAW operation. Mechanical vibration having resonance frequency of 300 Hz and amplitude of 0.5 mm was transferred to the molten weld pool of 6 mm thick mild steel butt-welded joints during the welding operation. The experimental work was conducted at various ranges of frequencies, welding current and welding speed. Taguchi's analysis technique has been applied to optimize the process parameters; the response values for analysis are yield strength and micro-hardness. The test results showed that with the application of the vibratory treatment the values of hardness and tensile properties increased. The auxiliary vibrations induced into the weld pool resulted in increased micro-hardness of the weld metal which indicates the orientation of the crystal and refinement of grains took place. This study shows that vibration applied into the weld pool can be successfully improved the mechanical properties of welded joints. Thus this research attempt provided an alternative welding technique for grain refinement of weldments.

  17. Development of Alternative Technology to PWHT in Site Welding

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Ho Jin; Lee, B. S.; Jang, J. S.; Kim, K. H.; Park, S. D.; Yoon, J. H.; Kim, M. C.; Kim, K. B.; Sung, K. W

    2007-04-15

    ASME Section IX added requirements for qualification when using temper bead welding in the 2004 edition. The temper bead welding techniques which can satisfy the requirements of the Code are needed to use them in the site repair welding. The optimized welding parameters can be obtained when controlling the process to supercritically-reheat and to subcritically-reheat the coarse grain region sequently. The microstructures of SCFGCG obtained from the Gleegle simulated specimens and those of post weld heat treated coarse grain region are compared. The obtained both microstructures showed almost similar patterns. mid bead deposition technique Suggested in this study has a technical concept that the mid beads are deposited between the deposited initial beads repeatedly in a bead layer, which gives a lot of reheating effects on brittle microstructure in HAZ. This newly suggested technique is considered to have more effective tempering effect than the conventional temper bead technique which has concept to deposit one type of beads in a bead layer. The suggested modeling in this study can simulate well the SMAW process. Hence this modeling was used in analyzing the more complicated welding process of multi-layer welding. The modeling was used to analyze the tempering effect on the microstructures of HAZ by considering the patterns of overlapping of the reheating regions under the consequently deposited beads. When considering the crack path in the ever-matched weld metal condition, the interface may have a resistance against the crack propagation. A182 filler and A625 filler were used to make the weld specimens which have different weld metal conditions. The crack directed toward the under-matched weld metal may propagate across the fusion line easier than that of the even-matched weld metal condition.

  18. Plasma spectroscopy analysis technique based on optimization algorithms and spectral synthesis for arc-welding quality assurance.

    Science.gov (United States)

    Mirapeix, J; Cobo, A; González, D A; López-Higuera, J M

    2007-02-19

    A new plasma spectroscopy analysis technique based on the generation of synthetic spectra by means of optimization processes is presented in this paper. The technique has been developed for its application in arc-welding quality assurance. The new approach has been checked through several experimental tests, yielding results in reasonably good agreement with the ones offered by the traditional spectroscopic analysis technique.

  19. Thermal Stir Welding Development at Marshall Space Flight Center

    Science.gov (United States)

    Ding, Robert J.

    2008-01-01

    Solid state welding processes have become the focus of welding process development at NASA's Marshall Space Flight Center. Unlike fusion weld processes such as tungsten inert gas (TIG), variable polarity plasma arc (VPPA), electron beam (EB), etc., solid state welding processes do not melt the material during welding. The resultant microstructure can be characterized as a dynamically recrystallized morphology much different than the casted, dentritic structure typical of fusion weld processes. The primary benefits of solid state processes over fusion weld processes include superior mechanic properties and the elimination of thermal distortion and residual stresses. These solid state processes attributes have profoundly influenced the direction of advanced welding research and development within the NASA agency. Thermal Stir Welding (TSW) is a new solid state welding process being developed at the Marshall Space Flight Center. Unlike friction stir welding, the heating, stirring and forging elements of the weld process can be decoupled for independent control. An induction coil induces energy into a workpiece to attain a desired plastic temperature. An independently controlled stir rod, captured within non-rotating containment plates, then stirs the plasticized material followed by forging plates/rollers that work the stirred weld joint. The independent control (decoupling) of heating, stirring and forging allows, theoretically, for the precision control of microstructure morphology. The TSW process is being used to evaluate the solid state joining of Haynes 230 for ARES J-2X applications. It is also being developed for 500-in (12.5 mm) thick commercially pure grade 2 titanium for navy applications. Other interests include Inconel 718 and stainless steel. This presentation will provide metallurgical and mechanical property data for these high melting temperature alloys.

  20. Modelling of damage development and ductile failure in welded joints

    DEFF Research Database (Denmark)

    Nielsen, Kim Lau

    conducted ([P1], [P2], [P7]-[P9]). The focus in the thesis is on FS-welded 2xxx and 6xxx series of aluminum alloys, which are attractive, for example, to the aerospace industry, since the 2024 aluminum in particular, is typically classified as un-weldable by conventional fusion welding techniques. Secondly...

  1. GMAW (Gas Metal Arc Welding) process development for girth welding of high strength pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Rajan, Vaidyanath; Daniel, Joe; Quintana, Marie [The Lincoln Electric Company, Cleveland, OH (United States); Chen, Yaoshan [Center for Reliable Energy Systems (CRES), Dublin, OH (United States); Souza, Antonio [Lincoln Electric do Brasil, Guarulhos, SP (Brazil)

    2009-07-01

    This paper highlights some of the results and findings from the first phase of a consolidated program co-funded by US Department of Transportation Pipeline and Hazardous Materials Safety Administration (PHMSA) and Pipeline Research Council Inc (PRCI) to develop pipe weld assessment and qualification methods and optimize X 100 pipe welding technologies. One objective of the program is to establish the range of viable welding options for X 100 line pipe, and define the essential variables to provide welding process control for reliable and consistent mechanical performance of the weldments. In this first phase, a series of narrow gap girth welds were made with pulsed gas metal arc welding (GMAW), instrumented with thermocouples in the heat affected zone (HAZ) and weld metal to obtain the associated thermal profiles, and instrumented to measure true energy input as opposed to conventional heat input. Results reveal that true heat input is 16%-22% higher than conventional heat input. The thermal profile measurements correlate very well with thermal model predictions using true energy input data, which indicates the viability of treating the latter as an essential variable. Ongoing microstructural and mechanical testing work will enable validation of an integrated thermal-microstructural model being developed for these applications. Outputs from this model will be used to correlate essential welding process variables with weld microstructure and hardness. This will ultimately enable development of a list of essential variables and the ranges needed to ensure mechanical properties are achieved in practice, recommendations for controlling and monitoring these essential variables and test methods suitable for classification of welding consumables. (author)

  2. Fiber laser welding of dual-phase galvanized sheet steel (DP590): traditional analysis and new quality assessment techniques

    Science.gov (United States)

    Miller, Stephanie; Pfeif, Erik; Kazakov, Andrei; Baumann, Esther; Dowell, Marla

    2016-03-01

    Laser welding has many advantages over traditional joining methods, yet remains underutilized. NIST has undertaken an ambitious initiative to improve predictions of weldability, reliability, and performance of laser welds. This study investigates butt welding of galvanized and ungalvanized dual-phase automotive sheet steels (DP 590) using a 10 kW commercial fiber laser system. Parameter development work, hardness profiles, microstructural characterization, and optical profilometry results are presented. Sound welding was accomplished in a laser power range of 2.0 kW to 4.5 kW and travel speed of 2000 mm/min to 5000 mm/min. Vickers hardness ranged from approximately 2 GPa to 4 GPa across the welds, with limited evidence of heat affected zone softening. Decreased hardness across the heat affected zone directly correlated to the appearance of ferrite. A technique was developed to non-destructively evaluate weld quality based on geometrical criteria. Weld face profilometry data were compared between light optical, metallographic sample, and frequency-modulated continuous-wave laser detection and ranging (FMCW LADAR) methods.

  3. Peculiarities and future development of space welding

    Science.gov (United States)

    Shulym, V. F.; Lapchinskii, V. F.; Nikitskii, V. P.; Demidov, D. L.; Neznamova, L. O.

    The paper deals with the peculiar features of space as a medium in which welding operations are performed. Studies of different methods of welding carried out both in the plane-laboratory and in space are briefly described, and the comparative characteristics of the most promising methods of welding for space conditions are given. The selection of electron beam as a basic method for space is supported. The paper considers the main welding processes performed in space with the help of an electron beam, such as heating, brazing, welding, cutting and coating.

  4. Welding Course Curriculum.

    Science.gov (United States)

    Genits, Joseph C.

    This guide is intended for use in helping students gain a fundamental background on the major aspects of the welding trade. The course emphasis is on mastery of the manipulative skills necessary to develop successful welding techniques and on acquisition of an understanding of the specialized tools and equipment used in welding. The first part…

  5. Electron beam weld development on a Filter Pack Assembly

    Science.gov (United States)

    Dereskiewicz, J. P.

    1994-06-01

    A continuous electron beam welding procedure was developed to replace the manual gas tungsten arc welding procedure on the Filter Pack Assembly. A statistical study was used to evaluate the feasibility of electron beam welding 6061-T6 aluminum covers to A356 cast weldments throughout the joint tolerance range specified on product drawings. Peak temperature exposures were not high enough to degrade the heat sensitive electrical components inside the cast weldment. Actual weldments with alodine coating on the weld joint area were successfully cleaned using a nonmetallic fiberglass brush cleaning method.

  6. EB-welding of the copper canister for the nuclear waste disposal. Final report of the development programme 1994-1997

    Energy Technology Data Exchange (ETDEWEB)

    Aalto, H. [Outokumpu Oy Poricopper, Pori (Finland)

    1998-10-01

    During 1994-1997 Posiva Oy and Outokumpu Poricopper Oy had a joint project Development of EB-welding method for massive copper canister manufacturing. The project was part of the national technology program `Weld 2000` and it was supported financially by Technology Development Centre (TEKES). The spent fuel from Finnish nuclear reactors is planned to be encapsulated in thick-walled copper canisters and placed deep into the bedrock. The thick copper layer of the canister provides a long time corrosion resistance and prevents deposited nuclear fuel from contact with water. The quality requirements of the copper components are high because of the designed long lifetime of the canister. The EB-welding technology has proved to be applicable method for the production of the copper canisters and the EB-welding technique is needed at least when the lids of the copper canister will be closed. There are a number of parameters in EB-welding which affect weldability. However, the effect of the welding parameters and their optimization has not been extensively studied in welding of thick copper sections using conventional high vacuum EB-welding. One aim of this development work was to extensively study effect of welding parameters on weld quality. The final objective was to minimise welding defects in the main weld and optimize slope out procedure in thick copper EB-welding. Welding of 50 mm thick copper sections was optimized using vertical and horizontal EB-welding techniques. As a result two full scale copper lids were welded to a short cylinder successfully. The resulting weld quality with optimised welding parameters was reasonable good. The optimised welding parameters for horizontal and vertical beam can be applied to the longitudinal body welds of the canister. The optimal slope out procedure for the lid closure needs some additional development work. In addition of extensive EB-welding program ultrasonic inspection and creep strength of the weld were studied. According

  7. Multi Objective Optimization of Flux Cored Arc Weld Parameters Using Hybrid Grey - Fuzzy Technique

    Directory of Open Access Journals (Sweden)

    M Satheesh

    2014-06-01

    Full Text Available In the present work, an attempt has been made to use the grey-based fuzzy logic method to solve correlated multiple response optimization problems in the field of flux cored arc welding. This approach converts the complex multiple objectives into a single grey-fuzzy reasoning grade. Based on the grey-fuzzy reasoning grade, optimum parameters are identified. The significant contributions of parameters are estimated using analysis of variance (ANOVA. This evaluation procedure can be used in intelligent decision making for a welding operator. The proposed and developed method has good accuracy and competency. The proposed technique provides manufacturers who develop intelligent manufacturing systems a method to facilitate the achievement of the highest level of automation.

  8. A Review of Dissimilar Welding Techniques for Magnesium Alloys to Aluminum Alloys

    Directory of Open Access Journals (Sweden)

    Liming Liu

    2014-05-01

    Full Text Available Welding of dissimilar magnesium alloys and aluminum alloys is an important issue because of their increasing applications in industries. In this document, the research and progress of a variety of welding techniques for joining dissimilar Mg alloys and Al alloys are reviewed from different perspectives. Welding of dissimilar Mg and Al is challenging due to the formation of brittle intermetallic compound (IMC such as Mg17Al12 and Mg2Al3. In order to increase the joint strength, three main research approaches were used to eliminate or reduce the Mg-Al intermetallic reaction layer. First, solid state welding techniques which have a low welding temperature were used to reduce the IMCs. Second, IMC variety and distribution were controlled to avoid the degradation of the joining strength in fusion welding. Third, techniques which have relatively controllable reaction time and energy were used to eliminate the IMCs. Some important processing parameters and their effects on weld quality are discussed, and the microstructure and metallurgical reaction are described. Mechanical properties of welds such as hardness, tensile, shear and fatigue strength are discussed. The aim of the report is to review the recent progress in the welding of dissimilar Mg and Al to provide a basis for follow-up research.

  9. A Review of Dissimilar Welding Techniques for Magnesium Alloys to Aluminum Alloys

    Science.gov (United States)

    Liu, Liming; Ren, Daxin; Liu, Fei

    2014-01-01

    Welding of dissimilar magnesium alloys and aluminum alloys is an important issue because of their increasing applications in industries. In this document, the research and progress of a variety of welding techniques for joining dissimilar Mg alloys and Al alloys are reviewed from different perspectives. Welding of dissimilar Mg and Al is challenging due to the formation of brittle intermetallic compound (IMC) such as Mg17Al12 and Mg2Al3. In order to increase the joint strength, three main research approaches were used to eliminate or reduce the Mg-Al intermetallic reaction layer. First, solid state welding techniques which have a low welding temperature were used to reduce the IMCs. Second, IMC variety and distribution were controlled to avoid the degradation of the joining strength in fusion welding. Third, techniques which have relatively controllable reaction time and energy were used to eliminate the IMCs. Some important processing parameters and their effects on weld quality are discussed, and the microstructure and metallurgical reaction are described. Mechanical properties of welds such as hardness, tensile, shear and fatigue strength are discussed. The aim of the report is to review the recent progress in the welding of dissimilar Mg and Al to provide a basis for follow-up research. PMID:28788646

  10. Development of Welding Fumes Health Index (WFHI) for Welding Workplace's Safety and Health Assessment.

    Science.gov (United States)

    Hariri, Azian; Paiman, Nuur Azreen; Leman, Abdul Mutalib; Md Yusof, Mohammad Zainal

    2014-08-01

    This study aimed to develop an index that can rank welding workplace that associate well with possible health risk of welders. Welding Fumes Health Index (WFHI) were developed based on data from case studies conducted in Plant 1 and Plant 2. Personal sampling of welding fumes to assess the concentration of metal constituents along with series of lung function tests was conducted. Fifteen metal constituents were investigated in each case study. Index values were derived from aggregation analysis of metal constituent concentration while significant lung functions were recognized through statistical analysis in each plant. The results showed none of the metal constituent concentration was exceeding the permissible exposure limit (PEL) for all plants. However, statistical analysis showed significant mean differences of lung functions between welders and non-welders. The index was then applied to one of the welding industry (Plant 3) for verification purpose. The developed index showed its promising ability to rank welding workplace, according to the multiple constituent concentrations of welding fumes that associates well with lung functions of the investigated welders. There was possibility that some of the metal constituents were below the detection limit leading to '0' value of sub index, thus the multiplicative form of aggregation model was not suitable for analysis. On the other hand, maximum or minimum operator forms suffer from compensation issues and were not considered in this study.

  11. Advanced examination techniques applied to the qualification of critical welds for the ITER correction coils

    Energy Technology Data Exchange (ETDEWEB)

    Sgobba, Stefano, E-mail: Stefano.Sgobba@cern.ch [CERN, CH-1211 Genève (Switzerland); Langeslag, Stefanie Agnes Elisabeth [CERN, CH-1211 Genève (Switzerland); Libeyre, Paul [ITER Organization, Route de Vinon-sur-Verdon, CS 90 046, 13067 St. Paul Lez Durance Cedex (France); Marcinek, Dawid Jaroslaw [Tadeusz Kościuszko Cracow University of Technology, 31-155 Kraków (Poland); Piguiet, Aline [CERN, CH-1211 Genève (Switzerland); Cécillon, Alexandre [RX Solutions, ZAC Altaïs, Chavanod (France)

    2015-10-15

    Highlights: • X-ray computed tomography (CT) was successfully applied to inspect the full weld volume of critical qualification welds for the ITER correction coils. • These welds featuring a complex geometry are virtually uninspectable with sufficient resolution by conventional Non-Destructive Examination (NDE) techniques. • The applied advanced examinations allowed an exhaustive identification of weld imperfections and a thorough understanding of their nature, position and size. • A substantial progress in weld quality could be achieved during the weld qualification phases. - Abstract: The ITER correction coils (CCs) consist of three sets of six coils located in between the toroidal (TF) and poloidal field (PF) magnets. The CCs rely on a Cable-in-Conduit Conductor (CICC), whose supercritical cooling at 4.5 K is provided by helium inlets and outlets. The assembly of the nozzles to the stainless steel conductor conduit includes fillet welds requiring full penetration through the thickness of the nozzle. Static and cyclic stresses have to be sustained by the inlet welds during operation. The entire volume of helium inlet and outlet welds, that are submitted to the most stringent quality levels of imperfections according to standards in force, is virtually uninspectable with sufficient resolution by conventional or computed radiography or by Ultrasonic Testing. On the other hand, X-ray computed tomography (CT) was successfully applied to inspect the full weld volume of several dozens of helium inlet qualification samples. The extensive use of CT techniques allowed a significant progress in the weld quality of the CC inlets. CT is also a promising technique for inspection of qualification welds of helium inlets of the TF magnets, by far more complex to examine due to their larger dimensions.

  12. Analysis on Development of Transverse - Sectioned Weld Zone using FEM Verified with Multipulsed Resistance Seam Welding

    Directory of Open Access Journals (Sweden)

    N Muhammad

    2013-12-01

    Full Text Available This paper details an investigation, through an experimental study, of the development of weld nuggets and a heat-affected zone (HAZ in resistance seam welding(RSEW using a numerical simulation approach. SYSWELD software for the simulation of heat treatment, welding, and welding assembly was utilized for the simulation process. The integrated Spot Weld Advisor (SWA in SYSWELD was applied to simulate the RSEW model using a two-dimensional axis-symmetric FE model with customized electrode meshing. The thermal-mechanical-electrical characteristic and contact condition were taken into account throughout this study. The developed model comprised a transverse cross section for welding two layers of low carbon steel with a thickness of 1 mm. For the experimental verification, three-pulsed RSEW with two different current stages was carried out. It was discovered that this program code, Spotweld Advisor, when used with the meshing method, was capable of offering results that were in agreement with physical experiments.

  13. Laser penetration spike welding : A microlaser welding technique enabling novel product designs and constructions

    NARCIS (Netherlands)

    Dijken, D.K; Hoving, W.; de Hosson, J.T.M.

    A novel method for laser penetration microspot welding of sheet metal is presented. With this so called "laser spike-welding," large gap tolerances are allowed. Depending on the ratio of laser spot radius to top plate thickness, gaps of 100% of the top layer thickness and more can be bridged. With

  14. Joining of beryllium by braze welding technique: preliminary results

    Energy Technology Data Exchange (ETDEWEB)

    Banaim, P.; Abramov, E. [Ben-Gurion Univ. of the Negev, Beersheba (Israel); Zalkind, S.; Eden, S.

    1998-01-01

    Within the framework of some applications, there is a need to join beryllium parts to each other. Gas Tungsten Arc Braze Welds were made in beryllium using 0.3 mm commercially Aluminum (1100) shim preplaced at the joint. The welds exhibited a tendency to form microcracks in the Fusion Zone and Heat Affected Zone. All the microcracks were backfilled with Aluminum. (author)

  15. Welding of Mo-Based Alloy Using Electron Beam and Laser-GTAW Hybrid Welding Techniques

    Science.gov (United States)

    Chatterjee, Anjan; Kumar, Santosh; Tewari, Raghvendra; Dey, Gautam Kumar

    2016-03-01

    In the current study, welding of TZM (molybdenum-based alloy) plates in square-butt configuration was carried out using electron beam and laser-GTAW hybrid power sources. Microstructures of weld joint containing three zones—parent metal, heat-affected zone, and fusion zone—were clearly identified when examined through optical and scanning electron microscopy. The weld joints were found to be sound with very wide fusion and heat-affected zones. The microstructure of the fusion zone was coarse-grained. as-solidified microstructure, while the microstructure of heat-affected zone was the recrystallized microstructure with reduction in grain size as distance from the fusion line increased. Microhardness profile using Vickers hardness tester was obtained across the weld region, and the tensile properties of the weld joints were evaluated by performing room temperature tensile test and fracture was examined using scanning electron microscope. Joint coefficient of the weld joints were ~40 to 45 pct of that of the parent metals with nonmeasurable tensile ductility with predominantly transgranular mode of fracture indicating weakness along the grain boundary. Detailed orientation imaging and transmission electron microscopy were carried out to understand the most dominating factor in introducing weld joint brittleness.

  16. Characterization of 2.25Cr1Mo welded ferritic steel plate by using diffractometric and ultrasonic techniques

    Energy Technology Data Exchange (ETDEWEB)

    Cernuschi, F.; Ghia, S. [Ente Nazionale per l`Energia Elettrica, Milan (Italy); Albertini, G.; Ceretti, M.; Rustichelli, F. [Ancona Univ. (Italy). Ist. di Fisica Medica; Castelnuovo, A.; Depero, L. [Univ. degli studi, Brescia.Fac. di ingegneria, dip. di ingegneria meccanica (Italy); Giamboni, S.; Gori, M. [Centro Elettrotecnico Sperimentale Italiano (CESI), Milan (Italy)

    1995-12-01

    Four different techniques (X-ray and neutron diffraction, ultrasonic birefringence and incremental hole drilling method) were applied for evaluating residual stress in a butt-welded ferritic steel palte. Measurements were carried out both before and after welding. Effects of post-welding heat treatment is also considered. A comparison between results obtained by using four different techniques is done.

  17. INVESTIGATION OF SINGLE-PASS/DOUBLE-PASS TECHNIQUES ON FRICTION STIR WELDING OF ALUMINIUM

    Directory of Open Access Journals (Sweden)

    N.A.A. Sathari

    2014-12-01

    Full Text Available The aim of this research is to study the effects of single-pass/ double-pass techniques on friction stir welding of aluminium. Two pieces of AA1100 with a thickness of 6.0 mm were friction stir welded using a CNC milling machine at rotational speeds of 1400 rpm, 1600 rpm and 1800 rpm respectively for single-pass and double-pass. Microstructure observations of the welded area were studied using an optical microscope. The specimens were tested by using a tensile test and Vickers hardness test to evaluate their mechanical properties. The results indicated that, at low rotational speed, defects such as ‘surface lack of fill’ and tunnels in the welded area contributed to a decrease in mechanical properties. Welded specimens using double-pass techniques show increasing values of tensile strength and hardness. From this investigation it is found that the best parameters of FSW welded aluminium AA1100 plate were those using double-pass techniques that produce mechanically sound joints with a hardness of 56.38 HV and 108 MPa strength at 1800 rpm compared to the single-pass technique. Friction stir welding, single-pass/ double-pass techniques, AA1100, microstructure, mechanical properties.

  18. A non-conventional technique for evaluating welded joints based on the electrical conductivity

    Energy Technology Data Exchange (ETDEWEB)

    Santos, T.G.; Sorger, G., E-mail: telmo.santos@fct.unl.pt, E-mail: lgs18243@campus.fct.unl.pt [Universidade Nova de Lisboa, UNIDEMI, Departamento de Engenharia Mecanica e Industrial, Faculdade de Ciencias e Tecnologia, Caparica (Portugal); Vilaca, P., E-mail: pedro.vilaca@aalto.fi [Aalto Univ., Dept. of Engineering Design and Production, School of Engineering, Aalto (Finland); Miranda, R., E-mail: rmiranda@fct.unl.pt [Universidade Nova de Lisboa, UNIDEMI, Departamento de Engenharia Mecanica e Industrial, Faculdade de Ciencias e Tecnologia, Caparica (Portugal)

    2015-01-15

    Recent studies showed that electrical conductivity is a valuable technique to identify the different zones of solid-state welded joints with a good correlation with the microstructure and hardness. This is a relevant result since this technique is fast and, in some cases, non destructive, The concept was applied to other welding processes such as the ones involving fusion to a wide range of materials, For this, a comprehensive study was performed using friction stir welding, tungsten inert gas (TlG) and gas metal arc (MAG) welding processes in either bead on plate or butt joints in: carbon steel, magnesium and titanium, Eddy current nondestructive testing (NDT) was used to measure the electrical conductivity at different depths in transverse sections of the processed materials. The profiles were compared to the hardness profiles in the same sections. As a result, a correlation was observed in most materials welded by solid state and by fusion processes. The variation of the electrical conductivity closely follows that measured in the hardness. Another interesting conclusion is that, even for fusion welding of carbon steels, the technique has potential to complement the hardness measurements and microstructural observations, allowing the identification of the distinct zones of welds in materials commonly used in industry. (author)

  19. Development of a suitable weld geometry for pressure resistance welding of the leader test assembly (LTA's) 16NGF fuel assembly fuel rod at Angra-1 Nuclear Power Plant

    Energy Technology Data Exchange (ETDEWEB)

    Junqueira, Fabio da Silva; Silva, Josue Ribeiro, E-mail: fabiojunqueira@inb.gov.br, E-mail: josueribeiro@inb.gov.br [Industrias Nucleares do Brasil (GEPRDN/INB), Rio de Janeiro, RJ (Brazil). Gerencia do Produto

    2013-07-01

    The purpose of this work is to develop suitable weld geometry for pressure resistance welding of the zircaloy-4 end plug to the special zirconium alloy cladding tube, Ø 9,14mm, for demonstration at Angra-1 Nuclear Plant. Weld geometry development was carried out in two steps: at the first one, the influence caused by the variation of the welding process key parameters, the axial compression strength of the end plug against the cladding tube, projection of the cladding tube into the welding chamber and the welding current have been evaluated; at the second step, the influence of the variation of end-plug weld geometry area was checked. For the combination of welding parameters, the technique of factorial design was used. Results from mechanical and metallographic tests have indicated a strong and direct influence of weld geometry dimensional variation on the weld mechanical resistance, and a modest influence in relation to the range of key parameters used to carry out tests. (author)

  20. Weld procedure produces quality welds for thick sections of Hastelloy-X

    Science.gov (United States)

    Flens, F. J.; Fletcher, C. W.; Glasier, L. F., Jr.

    1967-01-01

    Welding program produces premium quality, multipass welds in heavy tube sections of Hastelloy-X. It develops semiautomatic tungsten/inert gas procedures, weld wire procurement specifications material weld properties, welder-operator training, and nondestructive testing inspection techniques and procedures.

  1. Welding.

    Science.gov (United States)

    Cowan, Earl; And Others

    The curriculum guide for welding instruction contains 16 units presented in six sections. Each unit is divided into the following areas, each of which is color coded: terminal objectives, specific objectives, suggested activities, and instructional materials; information sheet; transparency masters; assignment sheet; test; and test answers. The…

  2. Ultrapulse welding: A new joining technique. [for automotive industry

    Science.gov (United States)

    Anderson, D. G.

    1972-01-01

    The ultrapulse process is a resistance welding process that utilizes unidirectional current of high magnitude for a very short time with a precisely controlled dynamic force pulse. Peak currents of up to 220,000 amperes for two to ten milliseconds are used with synchronized force pulses of up to nine thousand pounds. The welding current passing through the relatively high resistance of the interface between the parts that are being joined results in highly localized heating. Described is the UPW process as it applies to the automotive industry.

  3. Cleaning Effect of Interlayer Metal on the Joining Surface during Braze Pressure Welding

    National Research Council Canada - National Science Library

    INAGAKI, Yohei; SUZUMURA, Akio; IKESHOJI, Toshi-Taka; YAMAZAKI, Takahisa

    2005-01-01

    Braze Pressure Welding (BPW) with high frequency induction heating is a newly developed pressure welding technique using interlayer metals for welding the general steel pipes for pipe arrangement in buildings...

  4. Laser welding and syncristallization techniques comparison: “Ex vivo” study

    Science.gov (United States)

    Meleti, Marco; Vescovi, Paolo; Merigo, Elisabetta; Rocca, Jean-Paul

    2013-01-01

    Background and aims: Stabilization of implant abutments through electric impulses at high voltage for a very short time (electrowelding) was developed in the Eighties. In 2009, the same procedure was performed through the use of laser (laser welding) The aim of this study is to compare electrowelding and laser welding for intra-oral implant abutments stabilization on “ex vivo models” (pig jaws). Materials and methods: Six bars were welded with two different devices (Nd:YAG laser and Electrowelder) to eighteen titanium implant abutment inserted in three pig jaws. During the welding process, thermal increase was recorded, through the use of k-thermocouples, in the bone close to the implants. The strength of the welded joints was evaluated by a traction test after the removal of the implants. For temperature measurements a descriptive analysis and for traction test “values unpaired t test with Welch's correction” were performed: the significance level was set at Pwelding gives a lower thermal increase than Electrowelding at the bone close to implants (Mean: 1.97 and 5.27); the strength of laser welded joints was higher than that of Electrowelding even if nor statistically significant. (Mean: 184.75 and 168.29) Conclusion: Electrowelding seems to have no advantages, in term of thermal elevation and strength, while laser welding may be employed to connect titanium implants for immediate load without risks of thermal damage at surrounding tissues. PMID:24511205

  5. Weld Development for Aluminum Fission Chamber

    Energy Technology Data Exchange (ETDEWEB)

    Cross, Carl Edward [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Martinez, Jesse Norris [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2017-05-16

    The Sigma welding team was approached to help fabricate a small fission chamber (roughly ½ inch dia. x ½ inch tall cylinder). These chambers are used as radiation sensors that contain small traces of radionuclides (Cf 252, U 235, and U 238) that serve to ionize gas atoms in addition to external radiation. When a voltage is applied within the chamber, the resulting ion flow can be calibrated and monitored. Aluminum has the advantage of not forming radioactive compounds when exposed to high external radiation (except from minor Na alloy content). Since aluminum has not been used before in this application, this presented an unexplored challenge.

  6. An Evaluation of Welding Processes to Reduce Hexavalent Chromium Exposures and Reduce Costs by Using Better Welding Techniques

    OpenAIRE

    Keane, Michael J

    2014-01-01

    A group of stainless steel arc welding processes was compared for emission rates of fume and hexavalent chromium, and costs per meter length of weld. The objective was to identify those with minimal emissions and also compare relative labor and consumables costs. The selection included flux-cored arc welding (FCAW), shielded-metal arc welding (SMAW), and multiple gas metal arc welding (GMAW) processes. Using a conical chamber, fumes were collected, and fume generation rates and hexavalent chr...

  7. Optical design and development of a fiber coupled high-power diode laser system for laser transmission welding of plastics

    Science.gov (United States)

    Rodríguez-Vidal, Eva; Quintana, Iban; Etxarri, Jon; Azkorbebeitia, Urko; Otaduy, Deitze; González, Francisco; Moreno, Fernando

    2012-12-01

    Laser transmission welding (LTW) of thermoplastics is a direct bonding technique already used in different industrial applications sectors such as automobiles, microfluidics, electronics, and biomedicine. LTW evolves localized heating at the interface of two pieces of plastic to be joined. One of the plastic pieces needs to be optically transparent to the laser radiation whereas the other part has to be absorbent, being that the radiation produced by high power diode lasers is a good alternative for this process. As consequence, a tailored laser system has been designed and developed to obtain high quality weld seams with weld widths between 0.7 and 1.4 mm. The developed laser system consists of two diode laser bars (50 W per bar) coupled into an optical fiber using a nonimaging solution: equalization of the beam parameter product (BPP) in the slow and fast axes by a pair of step-mirrors. The power scaling was carried out by means of a multiplexing polarization technique. The analysis of energy balance and beam quality was performed considering ray tracing simulation (ZEMAX) and experimental validation. The welding experiments were conducted on acrylonitrile/butadiene/styrene (ABS), a thermoplastic frequently used in automotive, electronics and aircraft applications, doped with two different concentrations of carbon nanotubes (0.01% and 0.05% CNTs). Quality of the weld seams on ABS was analyzed in terms of the process parameters (welding speed, laser power and clamping pressure) by visual and optical microscope inspections. Mechanical properties of weld seams were analyzed by mechanical shear tests. High quality weld seams were produced in ABS, revealing the potential of the laser developed in this work for a wide range of plastic welding applications.

  8. Immediate loading of zygomatic implants using the intraoral welding technique: a 12-month case series.

    Science.gov (United States)

    Degidi, Marco; Nardi, Diego; Piattelli, Adriano; Malevez, Chantal

    2012-10-01

    The aim of this prospective study was to evaluate the concept of intraoral welding as a suitable technique for fabricating a fixed restoration for the edentulous maxilla the day of surgery using standard and zygomatic implants. Ten consecutive patients (four men, six women; mean age, 62.3 ± 11.6 years) were involved in this study, each of whom had an edentulous atrophic maxilla and received two standard and two zygomatic implants. All implants were loaded immediately with a fixed prosthesis supported by an intraorally welded titanium framework. Definitive abutments were connected to the implants, and a titanium bar was welded to them using an intraoral welding unit. This framework was used to support the definitive prosthesis, which was fitted the day of implant placement. Patients were checked for swelling, pain, and framework stability at 1, 3, 6, and 12 months. A total of 20 immediately loaded standard and 20 zygomatic implants were used. The cases included in this study achieved a 100% prosthetic success rate at the 12-month follow-up. No fracture or radiographically detectable alteration of the welded frameworks was noticed. It is possible to successfully rehabilitate the edentulous atrophic maxilla with a permanently fixed prosthesis supported by an intraorally welded titanium framework attached to standard and zygomatic implants the day of surgery.

  9. Impact of different welding techniques on biological effect markers in exhaled breath condensate of 58 mild steel welders.

    Science.gov (United States)

    Hoffmeyer, Frank; Raulf-Heimsoth, Monika; Lehnert, Martin; Kendzia, Benjamin; Bernard, Sabine; Berresheim, Hans; Düser, Maria; Henry, Jana; Weiss, Tobias; Koch, Holger M; Pesch, Beate; Brüning, Thomas

    2012-01-01

    Total mass and composition of welding fumes are predominantly dependent on the welding technique and welding wire applied. The objective of this study was to investigate the impact of welding techniques on biological effect markers in exhaled breath condensate (EBC) of 58 healthy welders. The welding techniques applied were gas metal arc welding with solid wire (GMAW) (n=29) or flux cored wire (FCAW) (n=29). Welding fume particles were collected with personal samplers in the breathing zone inside the helmets. Levels of leukotriene B(4) (LTB(4)), prostaglandin E(2) (PGE(2)), and 8-isoprostane (8-iso-PGF(2α)) were measured with immunoassay kits and the EBC pH was measured after deaeration. Significantly higher 8-iso-PGF(2α) concentrations and a less acid pH were detected in EBC of welders using the FCAW than in EBC of welders using the GMAW technique. The lowest LTB(4) concentrations were measured in nonsmoking welders applying a solid wire. No significant influences were found in EBC concentrations of PGE(2) based upon smoking status or type of welding technique. This study suggests an enhanced irritative effect in the lower airways of mild steel welders due to the application of FCAW compared to GMAW, most likely associated with a higher emission of welding fumes.

  10. Welding Curriculum.

    Science.gov (United States)

    Alaska State Dept. of Education, Juneau. Div. of Adult and Vocational Education.

    This competency-based curriculum guide is a handbook for the development of welding trade programs. Based on a survey of Alaskan welding employers, it includes all competencies a student should acquire in such a welding program. The handbook stresses the importance of understanding the principles associated with the various elements of welding.…

  11. Challenges to Resistance Welding

    DEFF Research Database (Denmark)

    Song, Quanfeng

    This report originates from the compulsory defense during my Ph.D. study at the Technical University of Denmark. Resistance welding is an old and well-proven technology. Yet the emergence of more and more new materials, new designs, invention off new joining techniques, and more stringent...... requirement in quality have imposed challenges to the resistance welding. More some research and development have to be done to adapt the old technology to the manufacturing industry of the 21st century. In the 1st part of the report, the challenging factors to the resistance welding are reviewed. Numerical...... simulation of resistance welding has been under development for many years. Yet it is no easy to make simulation results reliable and accurate because of the complexity of resistance welding process. In the 2nd part of the report numerical modeling of resistance welding is reviewed, some critical factors...

  12. Fibre Laser Welding of HY-80 Steel: Procedure Development and Testing

    Science.gov (United States)

    2010-09-01

    fusion zone, but also weld procedural developments required to minimize porosity. Future plans: Tungsten inert gas ( TIG ) weld repaired threads are...Canada Fibre Laser Welding of HY-80 Steel Proceedure Development and Testing Christopher Bayley DLP Neil Aucoin DLP Xinjin Cao NRC IAR AMTC Technical...Memorandum DRDC Atlantic TM 2009-187 September 2010 This page intentionally left blank. Fibre Laser Welding of HY-80 Steel Procedure

  13. Development of sensor augmented robotic weld systems for aerospace propulsion system fabrication

    Science.gov (United States)

    Jones, C. S.; Gangl, K. J.

    1986-01-01

    In order to meet stringent performance goals for power and reuseability, the Space Shuttle Main Engine was designed with many complex, difficult welded joints that provide maximum strength and minimum weight. To this end, the SSME requires 370 meters of welded joints. Automation of some welds has improved welding productivity significantly over manual welding. Application has previously been limited by accessibility constraints, requirements for complex process control, low production volumes, high part variability, and stringent quality requirements. Development of robots for welding in this application requires that a unique set of constraints be addressed. This paper shows how robotic welding can enhance production of aerospace components by addressing their specific requirements. A development program at the Marshall Space Flight Center combining industrial robots with state-of-the-art sensor systems and computer simulation is providing technology for the automation of welds in Space Shuttle Main Engine production.

  14. Optimization of Thermal Aspects of Friction Stir Welding – Initial Studies Using a Space Mapping Technique

    DEFF Research Database (Denmark)

    Larsen, Anders Astrup; Bendsøe, Martin P.; Schmidt, Henrik Nikolaj Blicher

    2007-01-01

    The aim of this paper is to optimize a thermal model of a friction stir welding process. The optimization is performed using a space mapping technique in which an analytical model is used along with the FEM model to be optimized. The results are compared to traditional gradient based optimization...

  15. Welding arc plasma physics

    Science.gov (United States)

    Cain, Bruce L.

    1990-01-01

    The problems of weld quality control and weld process dependability continue to be relevant issues in modern metal welding technology. These become especially important for NASA missions which may require the assembly or repair of larger orbiting platforms using automatic welding techniques. To extend present welding technologies for such applications, NASA/MSFC's Materials and Processes Lab is developing physical models of the arc welding process with the goal of providing both a basis for improved design of weld control systems, and a better understanding of how arc welding variables influence final weld properties. The physics of the plasma arc discharge is reasonably well established in terms of transport processes occurring in the arc column itself, although recourse to sophisticated numerical treatments is normally required to obtain quantitative results. Unfortunately the rigor of these numerical computations often obscures the physics of the underlying model due to its inherent complexity. In contrast, this work has focused on a relatively simple physical model of the arc discharge to describe the gross features observed in welding arcs. Emphasis was placed of deriving analytic expressions for the voltage along the arc axis as a function of known or measurable arc parameters. The model retains the essential physics for a straight polarity, diffusion dominated free burning arc in argon, with major simplifications of collisionless sheaths and simple energy balances at the electrodes.

  16. The Use of CDM Analysis Techniques in High Temperature Creep Failure of Welded Structures

    Science.gov (United States)

    Hayhurst, David R.; Wong, Man Tak; Vakili-Tahami, Farid

    Techniques are reviewed for the calibration of constitutive relationships for the different phases of the weld. It is shown how the calibration is carried out using property ratios, and a knowledge of the constitutive equations of the parent material. The results of CDM analyses, obtained using the two-dimensional solver Damage XX, are reviewed for: a butt-welded pipe at 565°C and, a welded cylinder-sphere pipe intersection at 590°C. Results are then presented of a three-dimensional CDM solution for a three-degree slice of the welded cylinder-sphere pipe intersection, and shown to be in close agreement with the two-dimensional, Damage XX, solution. Then the paper examines damage growth at a constant temperature of 590°C in a ferritic steel butt-welded pipe subjected to a combined constant internal pressure of 4MPa and a constant global bending moment of 49kNm. The CDM results for a three-dimensional analysis are compared with qualitative experimental results, and good correlation is indicated.

  17. Instant loading with intraoral welding technique and PRAMA implants: a new prosthetic approach.

    Science.gov (United States)

    Celletti, R; Fanali, S; Laici, C U; Santori, C; Pignatelli, P; Sinjari, B

    2017-01-01

    When splinting multiple implants passive fit of the framework should be achieved to avoid excessive force distribution on the implants. Recently, a protocol was suggested for immediate loading of multiple implants by welding a titanium bar to implant abutments directly in the oral cavity so as to create a customized, precise and passive metal-reinforced provisional restoration. The intraoral welding technique subsequently proves to be a successful option in the full-arch immediate restorations of the mandible and maxilla. The aim of this article is to present a case report in which a new prosthetic approach, using trans-mucosal implants, is described. Dental implants are instantly loaded with a provisional prosthesis supported by an intraoral welded titanium framework to obtain a precise passive fit of the immediate loaded prosthesis.

  18. Laser weld process monitoring and control using chromatic filtering of thermal radiation from a weld pool

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Cheol Jung; Kim, Min Suk; Baik, Sung Hoon; Chung, Chin Man

    2000-06-01

    The application of high power Nd: YAG lasers for precision welding in industry has been growing quite fast these days in diverse areas such as the automobile, the electronics and the aerospace industries. These diverse applications also require the new developments for the precise control and the reliable process monitoring. Due to the hostile environment in laser welding, a remote monitoring is required. The present development relates in general to weld process monitoring techniques, and more particularly to improved methods and apparatus for real-time monitoring of thermal radiation of a weld pool to monitor a size variation and a focus shift of the weld pool for weld process control, utilizing the chromatic aberration of focusing lens or lenses. The monitoring technique of the size variation and the focus shift of a weld pool is developed by using the chromatic filtering of the thermal radiation from a weld pool. The monitoring of weld pool size variation can also be used to monitor the weld depth in a laser welding. Furthermore, the monitoring of the size variation of a weld pool is independent of the focus shift of a weld pool and the monitoring of the focus shift of a weld pool is independent of the size variation of a weld pool.

  19. Linear friction welding for constructing and repairing rail for high speed and intercity passenger service rail : final report.

    Science.gov (United States)

    2016-08-01

    This project developed a solid-state welding process based on linear friction welding (LFW) technology. While resistance flash welding or : thermite techniques are tried and true methods for joining rails and performing partial rail replacement repai...

  20. Development of underwater laser cutting technique for steel and ...

    Indian Academy of Sciences (India)

    Abstract. In nuclear field, underwater cutting and welding technique is required for post-irradiation examination, maintenance, decommissioning and to reduce storage space of irradiated materials like used zircaloy pressure tubes etc., of nuclear power plants. We have developed underwater cutting technique for 4.2 mm ...

  1. Robotic and automatic welding development at the Marshall Space Flight Center

    Science.gov (United States)

    Jones, C. S.; Jackson, M. E.; Flanigan, L. A.

    1988-01-01

    Welding automation is the key to two major development programs to improve quality and reduce the cost of manufacturing space hardware currently undertaken by the Materials and Processes Laboratory of the NASA Marshall Space Flight Center. Variable polarity plasma arc welding has demonstrated its effectiveness on class 1 aluminum welding in external tank production. More than three miles of welds were completed without an internal defect. Much of this success can be credited to automation developments which stabilize the process. Robotic manipulation technology is under development for automation of welds on the Space Shuttle's main engines utilizing pathfinder systems in development of tooling and sensors for the production applications. The overall approach to welding automation development undertaken is outlined. Advanced sensors and control systems methodologies are described that combine to make aerospace quality welds with a minimum of dependence on operator skill.

  2. Ultrasonic Phased Array Technique for Accurate Flaw Sizing in Dissimilar Metal Welds

    Energy Technology Data Exchange (ETDEWEB)

    Jonathan D Buttram

    2005-03-11

    Described is a manual,portable non-destructive technique to determine the through wall height of cracks present in dissimilar metal welds used in the primary coolling systems of pressure water and boiler light water reactors. Current manual methods found in industry have proven not to exhibit the sizing accuracy required by ASME inspection requirement. The technique described demonstrated an accuracy approximately three times that required to ASME Section XI, Appendix 8 qualification.

  3. [Spectra and thermal analysis of the arc in activating flux plasma arc welding].

    Science.gov (United States)

    Chai, Guo-Ming; Zhu, Yi-Feng

    2010-04-01

    In activating flux plasma arc welding the welding arc was analyzed by spectra analysis technique, and the welding arc temperature field was measured by the infrared sensing and computer image technique. The distribution models of welding arc heat flow density of activating flux PAW welding were developed. The composition of welding arc affected by activated flux was studied, and the welding arc temperature field was studied. The results show that the spectral lines of argon atom and ionized argon atom of primary ionization are the main spectra lines of the conventional plasma welding arc. The spectra lines of weld metal are inappreciable in the spectra lines of the conventional plasma welding arc. The gas particle is the main in the conventional plasma welding arc. The conventional plasma welding arc is gas welding arc. The spectra lines of argon atom and ionized argon atom of primary ionization are intensified in the activating flux plasma welding arc, and the spectra lines of Ti, Cr and Fe elements are found in the activating flux plasma welding arc. The welding arc temperature distribution in activating flux plasma arc welding is compact, the outline of the welding arc temperature field is narrow, the range of the welding arc temperature distribution is concentrated, the welding arc radial temperature gradient is large, and the welding arc radial temperature gradient shows normal Gauss distribution.

  4. New Tendencies in Development of Carbonaceous Additives for Welding Fluxes

    Science.gov (United States)

    Kozyrev, N. A.; Kryukov, R. E.; Kozyreva, O. A.

    2015-09-01

    The paper provides results of comparative analysis of the effect of carbonaceous components introduced into welding fluxes on molten metal - slag interaction. Thermodynamical calculations of dehydrogenization are presented for submerged arc welding. A positive influence of carbonaceous additives on gas content and mechanical properties of welds is demonstrated. Carbon and fluorine containing additives are emphasized to be promising for automatic submerged arc welding.

  5. Resistance welding

    DEFF Research Database (Denmark)

    Bay, Niels; Zhang, Wenqi; Rasmussen, Mogens H.

    2003-01-01

    Resistance welding comprises not only the well known spot welding process but also more complex projection welding operations, where excessive plastic deformation of the weld point may occur. This enables the production of complex geometries and material combinations, which are often not possible...... to weld by traditional spot welding operations. Such joining processes are, however, not simple to develop due to the large number of parameters involved. Development has traditionally been carried out by large experimental investigations, but the development of a numerical programme system has changed...

  6. Development of an encapsulation method using plasma arc welding to produce iodine-125 seeds for brachytherapy

    Energy Technology Data Exchange (ETDEWEB)

    Feher, Anselmo; Calvo, Wilson A.P.; Rostelato, Maria E.C.M.; Zeituni, Carlos A.; Somessari, Samir L.; Costa, Osvaldo L.; Moura, Joao A.; Moura, Eduardo S.; Souza, Carla D.; Rela, Paulo R., E-mail: afeher@ipen.b, E-mail: wapcalvo@ipen.b, E-mail: elisaros@ipen.b, E-mail: somessar@ipen.b, E-mail: olcosta@ipen.b, E-mail: esmoura@ipen.b, E-mail: cdsouza@ipen.b, E-mail: prela@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2011-07-01

    The prostate cancer, which is the second cause of death by cancer in men, overcome only by lung cancer is public health problem in Brazil. Brachytherapy is among the possible available treatments for prostate cancer, in which small seeds containing Iodine-125 radioisotope are implanted into the prostate gland. The seed consists of a titanium sealed capsule with 0.8 mm external diameter and 4.5 mm length, containing a central silver wire with adsorbed Iodine-125. The Plasma Arc Welding (PAW) is one of the viable techniques for sealing process. The equipment used in this technique is less costly than in other processes, such as, Laser Beam Welding (LBW). The main purpose of this work was the development of an encapsulation method using PAW. The development of this work has presented the following phases: cutting and cleaning titanium tube, determination of the welding parameters, development of a titanium tube holding device for PAW, sealed sources validation according to ISO 2919 - Sealed Radioactive Sources - General Requirements and Classification, and metallographic assays. The developed procedure to seal Iodine-125 seeds using PAW has shown high efficiency, satisfying all the established requirements of ISO 2919. The results obtained in this work will give the possibility to establish a routine production process according to the orientations presented in resolution RDC 17 - Good Manufacturing Practices to Medical Products defined by the ANVISA - National Agency of Sanitary Surveillance. (author)

  7. Synthetic Aperture Focusing Technique for the Ultrasonic Evaluation of Friction Stir Welds

    Science.gov (United States)

    Lévesque, D.; Dubourg, L.; Mandache, C.; Kruger, S. E.; Lord, M.; Merati, A.; Jahazi, M.; Monchalin, J.-P.

    2008-02-01

    An ultrasonic technique using numerical focusing and processing is presented in this paper for the detection of different types of flaws in friction stir welds (FSW). The data is acquired using immersion ultrasonic technique or laser ultrasonics, while the Synthetic Aperture Focusing Technique (SAFT) is used for numerical focusing. Measurements on the top and far sides of the weld for both lap and butt joints of thin aluminum sheets are investigated. Discontinuities such as wormholes, hooking, lack of penetration and voids are found to be easily detected. The limit of detectability and a comparison with mechanical properties are discussed. Also, the detection of joint line remnants or kissing bonds due to entrapped oxide layers seems possible in lap joint structures using high frequency laser-ultrasonics.

  8. A study of processes for welding pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Weston, J. (ed.)

    1991-07-01

    A review was made of exisiting and potential processes for welding pipelines: fusion welding (arc, electron beam, laser, thermit) and forge welding (friction, flash, magnetically impelled arc butt, upset butt, explosive, shielded active gas, gas pressure). Consideration of J-lay operations gave indications that were reflections of the status of the processes in terms of normal land and offshore S-lay operation: forge welding processes, although having promise require considerable development; fusion welding processes offer several possibilities (mechanized GMA welding likely to be used in 1991-2); laser welding requires development in all pipeline areas: a production machine for electron beam welding will involve high costs. Nondestructive testing techniques are also reviewed. Demand for faster quality assessment is being addressed by speeding radiographic film processing and through the development of real time radiography and automatic ultrasonic testing. Conclusions on most likely future process developments are: SMAW with cellulosic electrodes is best for tie-ins, short pip runs; SMAW continues to be important for small-diameter lines, although mechanized GMA could be used, along with mechanical joining, MIAB, radial fraction, and flash butt; mechanized GMA welding is likely to predominate for large diameter lines and probably will be used for the first J-lay line (other techniques could be used too); and welding of piping for station facilities involves both shop welding of sub-assemblies and on-site welding of pipe and sub-assemblies to each other (site welding uses both SMAW and GMAW). Figs, tabs.

  9. Advanced examination techniques applied to the qualification of critical welds for the ITER correction coils

    CERN Document Server

    Sgobba, Stefano; Libeyre, Paul; Marcinek, Dawid Jaroslaw; Piguiet, Aline; Cécillon, Alexandre

    2015-01-01

    The ITER correction coils (CCs) consist of three sets of six coils located in between the toroidal (TF) and poloidal field (PF) magnets. The CCs rely on a Cable-in-Conduit Conductor (CICC), whose supercritical cooling at 4.5 K is provided by helium inlets and outlets. The assembly of the nozzles to the stainless steel conductor conduit includes fillet welds requiring full penetration through the thickness of the nozzle. Static and cyclic stresses have to be sustained by the inlet welds during operation. The entire volume of helium inlet and outlet welds, that are submitted to the most stringent quality levels of imperfections according to standards in force, is virtually uninspectable with sufficient resolution by conventional or computed radiography or by Ultrasonic Testing. On the other hand, X-ray computed tomography (CT) was successfully applied to inspect the full weld volume of several dozens of helium inlet qualification samples. The extensive use of CT techniques allowed a significant progress in the ...

  10. Comparison of the Thermal Welding Technique and Cold Dissection for Pediatric Tonsillectomy

    OpenAIRE

    Yaşar, Hüsamettin; Özkul, Haluk; Verim, Ayşegül

    2014-01-01

    Objectives: To compare the thermal welding technique (TWT) with cold dissection (CD) for pediatric tonsillectomy. Patients and Methods: Fifty consecutive children with chronic tonsillitis and/or upper airway obstruction were alternately assigned to the TWT or CD group. Age, gender, operation time, intraoperative hemostasis method, early postoperative pain, time to regain normal diet, and extent of healing of the tonsillar fossa on the tenth postoperative day were evaluated. Re...

  11. In-Situ Nondestructive Examination of Weld Penetration

    National Research Council Canada - National Science Library

    Chin, Bryan

    1998-01-01

    The objective of this program is to develop infrared sensing techniques to monitor and control welding penetration in gas tungsten arc and submerged arc welding processes used by the US Navy in the construction of ships...

  12. An evaluation of welding processes to reduce hexavalent chromium exposures and reduce costs by using better welding techniques.

    Science.gov (United States)

    Keane, Michael J

    2014-01-01

    A group of stainless steel arc welding processes was compared for emission rates of fume and hexavalent chromium, and costs per meter length of weld. The objective was to identify those with minimal emissions and also compare relative labor and consumables costs. The selection included flux-cored arc welding (FCAW), shielded-metal arc welding (SMAW), and multiple gas metal arc welding (GMAW) processes. Using a conical chamber, fumes were collected, and fume generation rates and hexavalent chromium (Cr(6+)) were measured. GMAW processes used were short-circuit (SC) and pulsed-spray modes. Flux-cored welding used gas shielding. Costs were estimated per meter of a 6.3-mm thick horizontal butt weld. Emission rates of Cr(6+) were lowest for GMAW processes and highest for SMAW; several GMAW processes had less than 2% of the SMAW generation rate. Labor and consumable costs for the processes studied were again highest for SMAW, with those of several GMAW types about half that cost. The results show that use of any of the GMAW processes (and flux-cored welding) could substantially reduce fume and Cr(6+) emissions, and greatly reduce costs relative to SMAW.

  13. Laser welded steel sandwich panel bridge deck development : finite element analysis and stake weld strength tests.

    Science.gov (United States)

    2009-09-01

    This report summarizes the analysis of laser welded steel sandwich panels for use in bridge structures and : static testing of laser stake welded lap shear coupons. Steel sandwich panels consist of two face sheets : connected by a relatively low-dens...

  14. Development of Heat-Affected Zone Hardness Limits for In-Service Welding

    Science.gov (United States)

    2009-09-29

    Welding onto in-service pipelines is frequently required to facilitate a repair or to install a branch connection using the "hot tapping" technique. Welds made in-service cool at an accelerated rate as the result of the ability of the flowing content...

  15. Robot welding process control development task

    Science.gov (United States)

    Romine, Peter L.

    1992-01-01

    The completion of, and improvements made to, the software developed during 1990 for program maintenance on the PC and HEURIKON and transfer to the CYRO, and integration of the Rocketdyne vision software with the CYRO is documented. The new programs were used successfully by NASA, Rocketdyne, and UAH technicians and engineers to create, modify, upload, download, and control CYRO NC programs.

  16. Development of Appropriate Spot Welding Practice for Advanced High Strength Steels (TRP 0114)

    Energy Technology Data Exchange (ETDEWEB)

    Brian Girvin; Warren Peterson; Jerry Gould

    2004-09-17

    This program evaluated the effects of common manufacturing variables on spike-tempering effectiveness. The investigation used design-of-experiment (DOE) techniques, and examined both dual-phase and martensitic grades of high-strength steels (HSS). The specific grades chosen for this project were: Dual-phase (DP) 600, galvannealed (GA), 1.55 mm (DP) 600; Dual-phase (DP) 980 (uncoated), 1.55 mm (DP) 980; and Martensitic (M) 1300, 1.55 mm (M) 1300. Common manufacturing conditions of interest included tempering practice (quench and temper time), button size, simulated part fitup (sheet angular misalignment and fitup), and electrode wear (increased electrode face diameter). All of these conditions were evaluated against mechanical performance (static and dynamic tensile shear). Weld hardness data was also used to examine correlations between mechanical performance and the degree of tempering. Mechanical performance data was used to develop empirical models. The models were used to examine the robustness of weld strength and toughness to the selected processing conditions. This was done using standard EWI techniques. Graphical representations of robustness were then coupled with metallographic data to relate mechanical properties to the effectiveness of spike tempering. Mechanical properties for all three materials were relatively robust to variation in tempering. Major deviations in mechanical properties were caused by degradation of the weld itself. This was supported by a lack of correlation between hardness data and mechanical results. Small button sizes and large electrode face diameters (worn electrodes) produced large reductions in both static and dynamic strength levels when compared to standard production setups. Dynamic strength was further degraded by edge-located welds.

  17. First industrial application of the auto-adaptative MAG STT welding technique with laser joint tracking; Premiere application industrielle du soudage MAG STT avec suivi de joint auto-adaptatif au laser

    Energy Technology Data Exchange (ETDEWEB)

    Tran Tien, Th. [Institut de Soudure, 93 - Villepinte (France)

    2007-05-15

    The Welding Institute has participated to the plan of construction of the Large Hadron Collider. The hoops of the dipolar magnets are composed of two half cylinders 15 m in length in 10 mm 316LN austenitic stainless steel and are assembled around the magnet in a horizontal-vertical position. The Welding Institute has developed a software for carrying out the auto-adaptative welding technique with laser joint tracking, in using the MAG STT (Surface Tension Transfer) process. The modelling of the welding laws and the strategy of filling the joints in multi-paths absorb the physical tolerances of the preparation (clearance, poor alignment, root..) in dynamic welding condition too. (O.M.)

  18. Development of Process Maps in Two-Wire Tandem Submerged Arc Welding Process of HSLA Steel

    Science.gov (United States)

    Kiran, D. V.; Alam, S. A.; De, A.

    2013-04-01

    Appropriate selection of welding conditions to guarantee requisite weld joint mechanical properties is ever difficult because of their complex interactions. An approach is presented here to identify suitable welding conditions in typical two-wire tandem submerged arc welding (SAW-T) that involves many welding variables. First, an objective function is defined, which depicts the squared error between the mechanical properties of weld joint and of base material. A set of artificial neural network (ANN)-based models are developed next to estimate the weld joint properties as function of welding conditions using experimentally measured results. The neural network model-based predictions are used next to create a set of process map contours that depict the minimum achievable values of the objective function and the corresponding welding conditions. In typical SAW-T of HSLA steel, welding speed from 9.0 to 11.5 mm/s, leading wire current from 530 to 580 A, and trailing wire negative current from 680 to 910 A are found to be the most optimal.

  19. Microstructural developments and mechanical properties of friction stir welding of AZ91D magnesium alloy plates

    Directory of Open Access Journals (Sweden)

    Nagabhushan Kumar Kadigithala

    2017-06-01

    Full Text Available Friction stir welding (FSW is an efficient technique which can be used particularly for magnesium and aluminum alloys that are difficult to fusion weld. In this work AZ91D Mg alloy plates 3mm thick were friction stir welded at different process variables such as rotational speed and welding speed. The range of rotational speeds varied from 1025 to 1525 rpm, and the welding speed varied from 25 to 75 mm/min. Good quality welds were obtained under 1025 rpm of rotational speed with the welding speeds range from 25 to 75 mm/min. The microstructure of the AZ91D alloy consists of primary α-phase, eutectic α-phase and eutectic β (Mg17Al12 phase in the received condition (gravity die cast. The original dendrite grain structure completely disappeared and was transformed to fine equiaxed grains in stir zone (SZ. It was observed that there was a slight increase in hardness in SZ, because of fine recrystallized grain structure. The transverse tensile test results of weld specimens indicated constant strength irrespective of traveling speed. Fractrographic analysis of the friction stir welded specimens showed the brittle failure.

  20. Performance Improvement of Friction Stir Welds by Better Surface Finish

    Science.gov (United States)

    Russell, Sam; Nettles, Mindy

    2015-01-01

    The as-welded friction stir weld has a cross section that may act as a stress concentrator. The geometry associated with the stress concentration may reduce the weld strength and it makes the weld challenging to inspect with ultrasound. In some cases, the geometry leads to false positive nondestructive evaluation (NDE) indications and, in many cases, it requires manual blending to facilitate the inspection. This study will measure the stress concentration effect and develop an improved phased array ultrasound testing (PAUT) technique for friction stir welding. Post-welding, the friction stir weld (FSW) tool would be fitted with an end mill that would machine the weld smooth, trimmed shaved. This would eliminate the need for manual weld preparation for ultrasonic inspections. Manual surface preparation is a hand operation that varies widely depending on the person preparing the welds. Shaving is a process that can be automated and tightly controlled.

  1. The effect of reconditioning techniques by welding on the quality of deposits on crankshafts, case study SMAW

    Science.gov (United States)

    Chivu, O. R.; Cicic, D. T.; Rontescu, C.; Vasile, I. M.; Petriceanu, C.

    2015-11-01

    Currently, we are searching for a range of solutions for repairing the crankshafts that had snapped during operation. The paper deals with the extension of the two methods for reconditioning by welding in the energy industry in the field of repairing the crankshafts in the automotive industry. The results obtained through the application of methods for reconditioning Weld Toe Tempering Technique and filling layers of sidings, which was used as a welding procedure SMAW. Qualitative and quantitative comparisons between the results of the two methods based on the criterion of rigidity are carried out.

  2. The role of welding techniques in the biomechanical behavior of implant-supported prostheses.

    Science.gov (United States)

    Rodrigues, Sabrina Alessandra; Presotto, Anna Gabriella Camacho; Barão, Valentim Adelino Ricardo; Consani, Rafael Leonardo Xediek; Nóbilo, Mauro Antônio Arruda; Mesquita, Marcelo Ferraz

    2017-09-01

    This in vitro study investigated the role of welding techniques of implant-supported prostheses in the 2D and 3D marginal misfits of prosthetic frameworks, strain induced on the mini abutment, and detorque of prosthetic screws. The correlations between the analyzed variables were also investigated. Frameworks were cast in commercially pure titanium (cp-Ti). A marginal misfit of 200μm was simulated in the working models (control group) (n=20). The 2D marginal misfit was analyzed according to the single-screw test protocol using a precision optical microscope. The 3D marginal misfit was performed by X-ray microtomography. Strain gauge analysis was performed to investigate the strain induced on the mini abutment. A digital torque meter was used for analysis of the detorque and the mean value was calculated for each framework. Afterwards, the frameworks were divided into two experimental groups (n=10): Laser (L) and TIG (T). The welding techniques were performed according to the following parameters: L (390V/9ms); T (36A/60ms). The L and T groups were reevaluated according to the marginal misfit, strain, and detorque. The results were submitted to one-way ANOVA followed by Tukey's HSD test and Person correlation analysis (α=0.05). Welding techniques statistically reduced the 2D and 3D marginal misfits of prosthetic frameworks (p0.05). Positive correlations were observed between 2D and 3D marginal misfit reading methods (r=0.943, pwelding techniques improved the biomechanical behavior of the implant-supported system. TIG can be an acceptable and affordable technique to reduce the misfit of 3-unit Ti frameworks. Copyright © 2017 Elsevier B.V. All rights reserved.

  3. Development of stress corrosion cracking resistant welds of 321 stainless steel by simple surface engineering

    Science.gov (United States)

    Mankari, Kamal; Acharyya, Swati Ghosh

    2017-12-01

    We hereby report a simple surface engineering technique to make AISI grade 321 stainless steel (SS) welds resistant to stress corrosion cracking (SCC) in chloride environment. Heat exchanger tubes of AISI 321 SS, welded either by (a) laser beam welding (LBW) or by (b) metal inert gas welding (MIG) were used for the study. The welds had high magnitude of tensile residual stresses and had undergone SCC in chloride environment while in service. The welds were characterized using field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD). Subsequently, the welded surfaces were subjected to buffing operation followed by determination of residual stress distribution and surface roughness by XRD and surface profilometer measurements respectively. The susceptibility of the welds to SCC was tested in buffed and un-buffed condition as per ASTM G-36 in boiling MgCl2 for 5 h and 10 h, followed by microstructural characterization by using optical microscope and FESEM. The results showed that the buffed surfaces (both welds and base material) were resistant to SCC even after 10 h of exposure to boiling MgCl2 whereas the un-buffed surfaces underwent severe SCC for the same exposure time. Buffing imparted high magnitude of compressive stresses on the surface of stainless steel together with reduction in its surface roughness and reduction in plastic strain on the surface which made the welded surface, resistant to chloride assisted SCC. Buffing being a very simple, portable and economic technique can be easily adapted by the designers as the last step of component fabrication to make 321 stainless steel welds resistant to chloride assisted SCC.

  4. Technique for the residual life assessment of high temperature components based on creep-rupture testing on welded miniature specimens

    Energy Technology Data Exchange (ETDEWEB)

    Garzillo, A.; Guardamagna, C.; Moscotti, L.; Ranzani, L. [Ente Nazionale per l`Energia Elettrica, Milan (Italy)

    1995-06-01

    Following the present trend in the development of advanced methodologies for residual life assessment of high temperature components operating in power plants, particularly in non destructive methods, a testing technique has been set up at ENEL-CRAM based on creep-rupture testa in an argon on welded miniature specimens. Five experimental systems for creep-rupture tests in an argon atmosphere have been set up which include high accuracy systems, vacuum chambers and exrwnsometer devices. With the aim of establishing and validating the suitability of the experimental methodology, creep-rupture and interrupted creep testing programmes have been performed on miniature specimens (2 mm diameter and 10 mm gauge lenght). On the basis of experience gathered by various European research laboratories, a miniature specimen construction procedure has been developed using a laser welding technique for joining threaded heads to sample material. Low alloy ferritic steels, such as virgin 2.25CrlMo, 0.5Cr 0.5Mo 0.25V, and IN 738 superalloy miniature specimens have been investigated and the results, compared with those from standard specimens, show a regular trend in deformation vs time. Additional efforts to provide guidelines for material sampling from each plant component will be required in order to reduce uncertainties in residual life prediction.

  5. Performance improvement and development of design and manufacturing technology of KAERI type laser welding tool

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Ki Soo; Kim, Heung Cheol; Im Wan Seong [Chungnam National University, Taejon(Korea)

    1998-04-01

    Laser welding technology for repair of steam generator in nuclear power plants is an important research issue for the development of nuclear industry. In order to make credible laser repair welding inside steam generator pipe, it is necessary to device a welding tool which will succeed in accurate laser welding. There have been accomplished drawing including assembly drawing, isometric perspective drawing, dimension of parts, machining accuracy, materials, and machining methods of 3/4 inch laser welding tool to repair steam generator pipe, and also manufacture specification mentioning methods, machining process, test standard, and test methods. The design drawing and manufacture specification will contribute to producing laser welding tool. (author). 6 refs., 5 figs.

  6. Optimization of Welding Parameters of Submerged Arc Welding Using Analytic Hierarchy Process (AHP) Based on Taguchi Technique

    Science.gov (United States)

    Sarkar, A.; Roy, J.; Majumder, A.; Saha, S. C.

    2014-04-01

    The present paper reports a new procedure using an analytic hierarchy process (AHP) based Taguchi method for the selection of the best welding parameters to fabricate submerged arc welding of plain carbon steel. Selection of best welding parameters is an unstructured decision problem involving process parameters for multiple weldments. In the present investigation, three process parameter variables i.e. wire feed rate (Wf), stick out (So) and traverse speed (Ts) and the three response parameters i.e. penetration, bead width and bead reinforcement have been considered. The objective of the present work is thus to improve the quality of the welded elements by using AHP analysis based Taguchi method. Taguchi L16 orthogonal array is used to perform with less number of experimental runs. Taguchi approach is insufficient to solve a multi response optimization problem. In order to overcome this limitation, a multi criteria decision making method, AHP is applied in the present study. The optimal condition to have a quality weld (i.e. bead geometry) is found at 210 mm/min of wire feed rate, 15 mm of stick out and 0.75 m/min of traverse speed and also observed that the effect of wire feed rate on the overall bead geometry properties is more significant than other welding parameters. Finally, a confirmatory test has been carried out to verify the optimal setting so obtained.

  7. Development of remote pipe welding tool for divertor cassettes in JT-60SA

    Energy Technology Data Exchange (ETDEWEB)

    Hayashi, Takao, E-mail: hayashi.takao@jaea.go.jp [Fusion Research and Development Directorate, Japan Atomic Energy Agency, Naka (Japan); Sakurai, Shinji; Sakasai, Akira; Shibanuma, Kiyoshi [Fusion Research and Development Directorate, Japan Atomic Energy Agency, Naka (Japan); Kono, Wataru; Ohnawa, Toshio; Matsukage, Takeshi [Toshiba Corporation, Yokohama, Kanagawa (Japan)

    2015-12-15

    Highlights: • Remote pipe welding tool accessing from inside of the pipe has been newly developed. • Cooling pipe with a jut on the edge expands the acceptable welding gap up to 0.5 mm. • Positioning accuracy of the laser beam is realized to be less than ±0.1 mm. • We have achieved robust welding for an angular misalignment of 0.5°. - Abstract: Remote pipe welding tool accessing from inside of the pipe has been newly developed for JT-60SA. Remote handling (RH) system is necessary for the maintenance and repair of the divertor cassette in JT-60SA. Because the space around the cooling pipe connected with the divertor cassette is very limited, the cooling pipe is to be remotely cut and welded from inside for the maintenance. A laser welding method was employed to perform circumferential welding by rotating the focusing mirror inside the pipe. However, the grooves of connection pipes are not precisely aligned for welding. The most critical issue is therefore to develop a reliable welding tool for pipe connection without a defect such as undercut weld due to a gap caused by angular and axial misalignments of grooves. In addition, an angular misalignment between two pipes due to inclination of pipe has to be taken into account for the positioning of the laser beam during welding. In this paper, the followings are proposed to solve the above issues: (1) Cooling pipe connected with the divertor is machined to have a jut on the edge so as to expand the acceptable welding gap up to 0.5 mm by filling the gap with welded jut. (2) Positioning accuracy of the laser beam for reliable welding is realized to be less than ±0.1 mm along the circumferential target for welding by a position control mechanism provided in the tool even in the case of up to angular misalignment of 0.5° between connection pipes. Based on the above proposals, we have achieved robust welding for a large gap up to 0.5 mm as well as the maximum angular misalignment of 0.5° between connection pipes

  8. Development of precision numerical controlled high vacuum electron beam welding machine

    CERN Document Server

    Li Shao Lin

    2002-01-01

    The structure, main technical parameters and characteristics of the precision numerical controlled high vacuum electron beam welding machine are introduced. The design principle, some features and solutions to some key technique problems of this new type machine are described

  9. The development of a quality prediction system for aluminum laser welding to measure plasma intensity using photodiodes

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Ji Young [Technical Research Center, Hyundai Steel Company, Dangjin (Korea, Republic of); Sohn, Yong Ho [Dept. of Materials Science and Engineering, University of Central Florida, Orlando (United States); Park, Young Whan; Kwak, Jae Seob [Dept. of Mechanical Engineering, Pukyong National University, Busan (Korea, Republic of)

    2016-10-15

    Lightweight metals have been used to manufacture the body panels of cars to reduce the weight of car bodies. Typically, aluminum sheets are welded together, with a focus on weld quality assurance. A weld quality prediction system for the laser welding of aluminum was developed in this research to maximize welding production. The behavior of the plasma was also analyzed, dependent on various welding conditions. The light intensity of the plasma was altered with heat input and wire feed rate conditions, and the strength of the weld and sensor signals correlated closely for this heat input condition. Using these characteristics, a new algorithm and program were developed to evaluate the weld quality. The design involves a combinatory algorithm using a neural network model for the prediction of tensile strength from measured signals and a fuzzy multi-feature pattern recognition algorithm for the weld quality classification to improve predictability of the system.

  10. An accurate method for determining residual stresses with magnetic non-destructive techniques in welded ferromagnetic steels

    Science.gov (United States)

    Vourna, P.

    2016-03-01

    The scope of the present research work was to investigate the proper selection criteria for developing a suitable methodology for the accurate determination of residual stresses existing in welded parts. Magnetic non-destructive testing took place by the use of two magnetic non-destructive techniques: by the measurement of the magnetic Barkhausen noise and by the evaluation of the magnetic hysteresis loop parameters. The spatial distribution of residual stresses in welded metal parts by both non-destructive magnetic methods and two diffraction methods was determined. The conduction of magnetic measurements required an initial calibration of ferromagnetic steels. Based on the examined volume of the sample, all methods used were divided into two large categories: the first one was related to the determination of surface residual stress, whereas the second one was related to bulk residual stress determination. The first category included the magnetic Barkhausen noise and the X-ray diffraction measurements, while the second one included the magnetic permeability and the neutron diffraction data. The residual stresses determined by the magnetic techniques were in a good agreement with the diffraction ones.

  11. effect of post-weld heat treatment on the microstructure

    African Journals Online (AJOL)

    user

    among others are shielded metal arc welding, submerge arc welding, gas metal arc welding, plasma arc welding, gas ... welding (SMAW) technique is preferable to the other techniques ..... studies''International Journal of Innovative Research.

  12. An Investigation of the Perception of Professional Development among Mississippi's Secondary Welding Teachers

    Science.gov (United States)

    Ferguson, Douglas Forrest

    2012-01-01

    This research study originated as a result of a paucity of information available regarding how secondary welding teachers in Mississippi perceive the value of professional development they have received within the previous two years. The purpose of this study was to examine the perceptions of Mississippi's secondary welding teachers regarding how…

  13. Creep damage development in welded X20 and P91

    Energy Technology Data Exchange (ETDEWEB)

    Brett, Steve; Holmstrom, Stefan; Hald, John; Borg, Ulrik; Aakjaer Jensen, Soeren; Vulpen, Rijk Van; Degnan, Craig; Vinter Dahl, Kristian; Vilhelmsen, Tommy

    2011-03-15

    The Martensitic steel X20CrMoV121 (hereinafter called X20) and the modified 9Cr1Mo steel (hereinafter called P91) have been used for a number of years in high temperature applications since they posses superior creep strength compared to low alloyed steels. Due to the simple fact that very few failures were observed, almost no knowledge as to the evolution of creep damage in welds were available despite long operation times exceeding well over 100.000 hours. It has been suggested that X20 will develop creep damage in a different manner compared to low alloyed steel, i.e damage initiation should be slow followed by accelerated growth. The research work presented in this report included systematic investigations of the first components of X20, which has developed creep during long-term operation. All of the investigated components showed creep damage evolution similar to low alloy steels

  14. Braze welding of cobalt with a silver–copper filler

    Directory of Open Access Journals (Sweden)

    Everett M. Criss

    2015-01-01

    Full Text Available A new method of joining cobalt by braze-welding it with a silver–copper filler was developed in order to better understand the residual stresses in beryllium–aluminum/silicon weldments which are problematic to investigate because of the high toxicity of Be. The base and filler metals of this new welding system were selected to replicate the physical properties, crystal structures, and chemical behavior of the Be–AlSi welds. Welding parameters of this surrogate Co–AgCu system were determined by experimentation combining 4-point bending tests and microscopy. Final welds are 5 pass manual TIG (tungsten inert gas, with He top gas and Ar back gas. Control of the welding process produces welds with full penetration melting of the cobalt base. Microscopy indicates that cracking is minimal, and not through thickness, whereas 4-point bending shows failure is not by base-filler delamination. These welds improve upon the original Be–AlSi welds, which do not possess full penetration, and have considerable porosity. We propose that utilization of our welding methods will increase the strength of the Be–AlSi weldments. The specialized welding techniques developed for this study may be applicable not only for the parent Be–AlSi welds, but to braze welds and welds utilizing brittle materials in general. This concept of surrogacy may prove useful in the study of many different types of exotic welds.

  15. Fatigue limits of titanium-bar joints made with the laser and the electric resistance welding techniques: microstructural characterization and hardness properties.

    Science.gov (United States)

    Degidi, Marco; Nardi, Diego; Morri, Alessandro; Sighinolfi, Gianluca; Tebbel, Florian; Marchetti, Claudio

    2017-09-01

    Fatigue behavior of the titanium bars is of utmost importance for the safe and reliable operation of dental implants and prosthetic constructions based on these implants. To date, however, only few data are available on the fatigue strength of dental prostheses made with electric resistance welding and laser welding techniques. This in-vitro study highlighted that although the joints made with the laser welding approach are credited of a superior tensile strength, joints made with electric resistance welding exhibited double the minimum fatigue strength with respect to the joints made with laser welding (120 vs 60 N).

  16. Development of the new physical method for real time spot weld quality evaluation using ultrasound

    Science.gov (United States)

    Chertov, Andriy M.

    Since the invention of resistance spot welding, the manufacturers have been concerned about the quality assurance of the joints. One of the most promising directions in quality inspection is the real time ultrasonic nondestructive evaluation. In such a system, the acoustic signals are sent through the spot weld during welding and then analyzed to characterize the quality of the joint. Many research groups are currently working to develop a reliable inspection method. In this dissertation the new physical method of resistance spot weld quality monitoring is presented. It differs from all other ultrasonic methods by the physical principles of inspection. The multilayered structure of the spot weld with varying physical properties is investigated with short pulses of longitudinal ultrasonic waves. Unlike other methods, the developed technology works in reflection mode. The waves bring back the information which, after careful analysis, can be used to evaluate the weld quality. The complex structure of the weldment modifies the waves in different ways which, makes it hard to accurately measure the physical properties of the weldment. The frequency-dependent attenuation of the sound, diffraction, and beam divergence - all contribute to the signal distraction. These factors are fully studied, and ways to minimize them are presented. After application of pattern recognition routines, the weld characteristics are submitted to fuzzy logic algorithm, and the weld is characterized. The current level of the system development allowed the installation of two prototype machines at one assembly plant. The technology is now under thorough evaluation for robustness and accuracy in an industrial environment.

  17. Optimization of process parameters during vibratory welding technique using Taguchi's analysis

    OpenAIRE

    Singh, Pravin Kumar; Patel, D.; Prasad,S.B.

    2016-01-01

    With an aim to improve the mechanical properties of a weld joint, a new concept of vibratory setup has been designed which is capable to stir the molten weld pool before it solidifies during shielded metal arc welding (SMAW) operation. Mechanical vibration having resonance frequency of 300 Hz and amplitude of 0.5 mm was transferred to the molten weld pool of 6 mm thick mild steel butt-welded joints during the welding operation. The experimental work was conducted at various ranges of frequenc...

  18. A review of micro/nano welding and its future developments.

    Science.gov (United States)

    Guo, Kelvii W

    2009-01-01

    A review is given about the current state-of-the-art surrounding micro/nano scale welding/joining used in miniaturization or microsystems. Except for reviewing the applications of micro/nano welding/joining in various fields, such as microelectromechanical system (MEMS), micro total-analysis systems (microTAS), carbon nanotubes (CNTs) etc., the optimal equipments for micro/nano welding/joining, its corresponding future applications and research directions are discussed. Moreover, an extensive part of the paper is devoted to the introduction of new techniques, micro/nano laser and electron beam welding/joining. In turn, it is anticipated these techniques will be used in future micro/nano welding/joining applications. Meanwhile, because even smallest particles of dust can influence the results, more considerations are given to machine improvements that are required for its corresponding nano welding/joining. It will be one challenge for R&D efforts to combine the progress in micro/nano scales with that in miniaturization. This review provides a timely explanation of the literature surrounding the factors required for successful micro and nano welding/joining.

  19. High quality joining techniques: in-process assurance (IPA) welding system

    Energy Technology Data Exchange (ETDEWEB)

    Kaihara, Shoichiro [Ishikawajima-Harima Heavy Industries Co. Ltd., Tokyo (Japan)

    1996-08-01

    On July 1, 1995, the Product Liability Law was enforced, and in industrial world, further reliability has been demanded. Recently, accompanying the progress of electronics, the proportion taken by automatic welders and robots increased in welding. By memorizing proper welding conditions, the welding from initial to final passes can be done fully automatically. Also feedback mechanism was equipped to mechanized welders, and the in-process control has become to be feasible. The way of thinking on confirming in process welding quality in arc welding is explained. IPA welding system utilizes the multi-media collecting images and sound, samples the change of welding conditions and the state of arc on a same screen, and monitors the deviation from the range of proper welding conditions. At the time of abnormality, inspector or a computer carries out image diagnosis and welding control, and the system indicates the soundness of welded parts. The basic concept and the flow chart of this system are shown. The experiment of applying the system to arc welding is reported. The correlation of welding phenomena and welding conditions is examined. (K.I.)

  20. Microstructure development of welding joints in high Cr ferritic steels

    Energy Technology Data Exchange (ETDEWEB)

    Kubushiro, Keiji; Takahashi, Satoshi; Morishima, Keiko [IHI Corporation (Japan). Research Lab.

    2010-07-01

    Creep failure in high Cr ferritic steels welding joints are Type IV failure. Type IV-failure was ruptured in fine grained region of heat affected zone, microstructure and phase transformation process at welding in fine grained region were very important to clarify. Microstructure difference of heat affected zone was investigated in Gr.91, Gr.92, Gr.122 welding joint. The fraction of 60 degree block boundary, packet boundary, random boundary (including prior gamma boundary) length was compared in three ferritic steels by EBSP(Electron Backscatter Diffraction Pattern) analysis. HAZ was almost fully martensite phase in Gr.122 weld joint. On the other hand, HAZ in Gr.91 welding joint were some equiaxial grain and martensite structure. (orig.)

  1. [New welding processes and health effects of welding].

    Science.gov (United States)

    La Vecchia, G Marina; Maestrelli, Piero

    2011-01-01

    This paper describes some of the recent developments in the control technology to enhance capability of Pulse Gas Metal Arc Welding. Friction Stir Welding (FSW) processing has been also considered. FSW is a new solid-state joining technique. Heat generated by friction at the rotating tool softens the material being welded. FSW can be considered a green and energy-efficient technique without deleterious fumes, gas, radiation, and noise. Application of new welding processes is limited and studies on health effects in exposed workers are lacking. Acute and chronic health effects of conventional welding have been described. Metal fume fever and cross-shift decline of lung function are the main acute respiratory effects. Skin and eyes may be affected by heat, electricity and UV radiations. Chronic effects on respiratory system include chronic bronchitis, a benign pneumoconiosis (siderosis), asthma, and a possible increase in the incidence of lung cancer. Pulmonary infections are increased in terms of severity, duration, and frequency among welders.

  2. Investigate The Effect Of Welding Parameters On Mechanical Properties During The Welding Of Al-6061 Alloy

    Directory of Open Access Journals (Sweden)

    Rajendra Prasad

    2017-10-01

    Full Text Available Friction welding is a solid state welding technique which is being used in recent times to weld similar as well as dissimilar metals for getting defect free weld. Many combinations like low carbon to stainless steel austenitic to ferrite stainless steel aluminium to copper and titanium to aluminium or steel have been tried out by various solid state welding processes with quite good results. In the present work the 3 level full factorial design has been employed to investigate the effect of welding parameters on tensile strength toughness and heat generation during the welding of Al-6061 alloy. Mathematical relationships between friction welding parameters and mechanical properties like heat generation tensile strength and toughness have also been developed. An attempt has also been made to examine the fracture surfaces of test specimens using SEM. It has been found that welding speed is the most significant parameter thats affect the heat generation tensile strength and toughness. it has been found that tensile strength and toughness during welding increases with increased in welding speed while tensile strength and toughness initially increased as the welding time increases after that it decreased with increase in welding time. The difference in weight of alloying elements can be clearly seen by analyzing spectrum of elements.

  3. Fuzzy Logic-Based Techniques for Modeling the Correlation between the Weld Bead Dimension and the Process Parameters in MIG Welding

    Directory of Open Access Journals (Sweden)

    Y. Surender

    2013-01-01

    Full Text Available Fuzzy logic-based techniques have been developed to model input-output relationships of metal inert gas (MIG welding process. Both conventional and hierarchical fuzzy logic controllers (FLCs of Mamdani type have been developed, and their performances are compared. The conventional FLC suffers from the curse of dimensionality for handling a large number of variables, and a hierarchical FLC was proposed earlier to tackle this problem. However, in that study, both the structure and knowledge base of the FLC were not optimized simultaneously, which has been attempted here. Simultaneous optimization of the structure and knowledge base is a difficult task, and to solve it, a genetic algorithm (GA will have to deal with the strings having varied lengths. A new scheme has been proposed here to tackle the problem related to crossover of two parents with unequal lengths. It is interesting to observe that the conventional FLC yields the best accuracy in predictions, whereas the hierarchical FLC can be computationally faster than others but at the cost of accuracy. Moreover, there is no improvement of interpretability by introducing a hierarchical fuzzy system. Thus, there exists a trade-off between the accuracy obtained in predictions and computational complexity of various FLCs.

  4. Advanced Welding Applications

    Science.gov (United States)

    Ding, Robert J.

    2010-01-01

    Some of the applications of advanced welding techniques are shown in this poster presentation. Included are brief explanations of the use on the Ares I and Ares V launch vehicle and on the Space Shuttle Launch vehicle. Also included are microstructural views from four advanced welding techniques: Variable Polarity Plasma Arc (VPPA) weld (fusion), self-reacting friction stir welding (SR-FSW), conventional FSW, and Tube Socket Weld (TSW) on aluminum.

  5. Study of Mechanical Properties and Characterization of Pipe Steel welded by Hybrid (Friction Stir Weld + Root Arc Weld) Approach

    Energy Technology Data Exchange (ETDEWEB)

    Lim, Yong Chae [ORNL; Sanderson, Samuel [MegaStir Technologies LLC; Mahoney, Murray [Consultant; Wasson, Andrew J [ExxonMobil, Upstream Research Company (URC); Fairchild, Doug P [ExxonMobil, Upstream Research Company (URC); Wang, Yanli [ORNL; Feng, Zhili [ORNL

    2015-01-01

    Friction stir welding (FSW) has recently attracted attention as an alternative construction process for gas/oil transportation applications due to advantages compared to fusion welding techniques. A significant advantage is the ability of FSW to weld the entire or nearly the entire wall thickness in a single pass, while fusion welding requires multiple passes. However, when FSW is applied to a pipe or tube geometry, an internal back support anvil is required to resist the plunging forces exerted during FSW. Unfortunately, it may not be convenient or economical to use internal backing support due to limited access for some applications. To overcome this issue, ExxonMobil recently developed a new concept, combining root arc welding and FSW. That is, a root arc weld is made prior to FSW that supports the normal loads associated with FSW. In the present work, mechanical properties of a FSW + root arc welded pipe steel are reported including microstructure and microhardness.

  6. Applying a nonlinear, pitch-catch, ultrasonic technique for the detection of kissing bonds in friction stir welds.

    Science.gov (United States)

    Delrue, Steven; Tabatabaeipour, Morteza; Hettler, Jan; Van Den Abeele, Koen

    2016-05-01

    Friction stir welding (FSW) is a promising technology for the joining of aluminum alloys and other metallic admixtures that are hard to weld by conventional fusion welding. Although FSW generally provides better fatigue properties than traditional fusion welding methods, fatigue properties are still significantly lower than for the base material. Apart from voids, kissing bonds for instance, in the form of closed cracks propagating along the interface of the stirred and heat affected zone, are inherent features of the weld and can be considered as one of the main causes of a reduced fatigue life of FSW in comparison to the base material. The main problem with kissing bond defects in FSW, is that they currently are very difficult to detect using existing NDT methods. Besides, in most cases, the defects are not directly accessible from the exposed surface. Therefore, new techniques capable of detecting small kissing bond flaws need to be introduced. In the present paper, a novel and practical approach is introduced based on a nonlinear, single-sided, ultrasonic technique. The proposed inspection technique uses two single element transducers, with the first transducer transmitting an ultrasonic signal that focuses the ultrasonic waves at the bottom side of the sample where cracks are most likely to occur. The large amount of energy at the focus activates the kissing bond, resulting in the generation of nonlinear features in the wave propagation. These nonlinear features are then captured by the second transducer operating in pitch-catch mode, and are analyzed, using pulse inversion, to reveal the presence of a defect. The performance of the proposed nonlinear, pitch-catch technique, is first illustrated using a numerical study of an aluminum sample containing simple, vertically oriented, incipient cracks. Later, the proposed technique is also applied experimentally on a real-life friction stir welded butt joint containing a kissing bond flaw. Copyright © 2016

  7. Study of a fiber laser assisted friction stir welding process

    Science.gov (United States)

    Casalino, G.; Campanelli, S.; Ludovico, A. D.; Contuzzi, N.; Angelastro, A.

    2012-03-01

    Friction stir welding is a relatively new joining technique. This technique, which is considered a derivative of the more common friction welding method, was developed mainly for aluminum and its alloys. In recent years, this method has been used to join various other alloys. FSW has many advantages, including the following: the welding procedure is relatively simple with no consumables or filler metal; joint edge preparation is not needed; oxide removal prior to welding is unnecessary; high joint strength has been achieved in aluminum and magnesium alloys; FSW can be used with alloys that cannot be fusion welded due to crack sensitivity. The drawbacks of FSW include the need for powerful fixtures to clamp the workpiece to the welding table, the high force needed to move the welding tool forward, the relatively high wear rate of the welding tool, and weld speeds in FSW are slower, which can lead to longer process times. To overcome these drawbacks, a fiber laser-assisted friction stir welding system was designed (FLAFSW). The system combined a conventional commercial friction machine and a fiber pumped laser system. The scope is to investigate the influence of the laser assistance on the weld quality. A number of different aluminum plates, which are still mentioned to be difficult to be joint as intermetallic phases appear during melting welding techniques, were used. The evaluation of quality was performed through analysis of appearance, mechanical and microstructure characterization of the weld.

  8. Development of pipe welding, cutting and inspection tools for the ITER blanket

    Energy Technology Data Exchange (ETDEWEB)

    Oka, Kiyoshi; Ito, Akira; Taguchi, Kou; Takiguchi, Yuji; Takahashi, Hiroyuki; Tada, Eisuke [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

    1999-07-01

    In D-T burning reactors such as International Thermonuclear Experimental Reactor (ITER), an internal access welding/cutting of blanket cooling pipe with bend sections is inevitably required because of spatial constraint due to nuclear shield and available port opening space. For this purpose, internal access pipe welding/cutting/inspection tools for manifolds and branch pipes are being developed according to the agreement of the ITER R and D task (T329). A design concept of welding/cutting processing head with a flexible optical fiber has been developed and the basic feasibility studies on welding, cutting and rewelding are performed using stainless steel plate (SS316L). In the same way, a design concept of inspection head with a non-destructive inspection probe (including a leak-testing probe) has been developed and the basic characteristic tests are performed using welded stainless steel pipes. In this report, the details of welding/cutting/inspection heads for manifolds and branch pipes are described, together with the basic experiment results relating to the welding/cutting and inspection. In addition, details of a composite type optical fiber, which can transmit both the high-power YAG laser and visible rays, is described. (author)

  9. Advanced characterization techniques in understanding the roles of nickel in enhancing strength and toughness of submerged arc welding high strength low alloy steel multiple pass welds in the as-welded condition

    Science.gov (United States)

    Sham, Kin-Ling

    Striving for higher strength along with higher toughness is a constant goal in material properties. Even though nickel is known as an effective alloying element in improving the resistance of a steel to impact fracture, it is not fully understood how nickel enhances toughness. It was the goal of this work to assist and further the understanding of how nickel enhanced toughness and maintained strength in particular for high strength low alloy (HSLA) steel submerged arc welding multiple pass welds in the as-welded condition. Using advanced analytical techniques such as electron backscatter diffraction, x-ray diffraction, electron microprobe, differential scanning calorimetry, and thermodynamic modeling software, the effect of nickel was studied with nickel varying from one to five wt. pct. in increments of one wt. pct. in a specific HSLA steel submerged arc welding multiple pass weldment. The test matrix of five different nickel compositions in the as-welded and stress-relieved condition was to meet the targeted mechanical properties with a yield strength greater than or equal to 85 ksi, a ultimate tensile strength greater than or equal to 105 ksi, and a nil ductility temperature less than or equal to -140 degrees F. Mechanical testing demonstrated that nickel content of three wt. pct and greater in the as-welded condition fulfilled the targeted mechanical properties. Therefore, one, three, and five wt. pct. nickel in the as-welded condition was further studied to determine the effect of nickel on primary solidification mode, nickel solute segregation, dendrite thickness, phase transformation temperatures, effective ferrite grain size, dislocation density and strain, grain misorientation distribution, and precipitates. From one to five wt. pct nickel content in the as-welded condition, the primary solidification was shown to change from primary delta-ferrite to primary austenite. The nickel partitioning coefficient increased and dendrite/cellular thickness was

  10. Monitoring and Control of the Hybrid Laser-Gas Metal-Arc Welding Process

    Energy Technology Data Exchange (ETDEWEB)

    Kunerth, D. C.; McJunkin, T. R.; Nichol, C. I.; Clark, D.; Todorov, E.; Couch, R. D.; Yu, F.

    2013-07-01

    Methods are currently being developed towards a more robust system real time feedback in the high throughput process combining laser welding with gas metal arc welding. A combination of ultrasonic, eddy current, electronic monitoring, and visual techniques are being applied to the welding process. Initial simulation and bench top evaluation of proposed real time techniques on weld samples are presented along with the concepts to apply the techniques concurrently to the weld process. Consideration for the eventual code acceptance of the methods and system are also being researched as a component of this project. The goal is to detect defects or precursors to defects and correct when possible during the weld process.

  11. Friction stir scribe welding technique for dissimilar joining of aluminium and galvanised steel

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Tianhao [Center for Friction Stir Processing, Department of Materials Science and Engineering, University of North Texas, Denton, TX, USA; Sidhar, Harpreet [Center for Friction Stir Processing, Department of Materials Science and Engineering, University of North Texas, Denton, TX, USA; Mishra, Rajiv S. [Center for Friction Stir Processing, Department of Materials Science and Engineering, University of North Texas, Denton, TX, USA; Hovanski, Yuri [Pacific Northwest National Laboratory, Energy Materials and Manufacturing, Richland, WA, USA; Upadhyay, Piyush [Pacific Northwest National Laboratory, Energy Materials and Manufacturing, Richland, WA, USA; Carlson, Blair [General Motors Technical Center, Warren, MI, USA

    2017-10-04

    Friction stir scribe technology, a derivative of friction stir welding, was applied for the dissimilar lap welding of an aluminum alloy and galvanized mild steel sheets. During the process, the rotating tool with a cobalt steel scribe first penetrated the top material — aluminum — and then the scribe cut the bottom material — steel. The steel was displaced into the upper material to produce a characteristic hook feature. Lap welds were shear tested, and their fracture paths were studied. Welding parameters affected the welding features including hook height, which turned out to be highly related to fracture position. Therefore, in this paper, the relationships among welding parameters, hook height, joint strength and fracture position are presented. In addition, influence of zinc coating on joint strength was also studied. Keywords: friction stir scribe technology; dissimilar material welding; zinc coating; hook height; joint strength; fracture position

  12. Modal testing and finite element model updating of laser spot welds

    Science.gov (United States)

    Abu Husain, N.; Haddad Khodaparast, H.; Snaylam, A.; James, S.; Sharp, M.; Dearden, G.; Ouyang, H.

    2009-08-01

    Spot welds are used extensively in automotive engineering. One of the latest manufacturing techniques for producing spot welds is Laser Welding. Finite element (FE) modelling of laser welds for dynamic analysis is a research issue because of the complexity and uncertainty of the welds and thus formed structures. In this work, FE model of the welds is developed by employing CWELD element in NASTRAN and its feasibility for representing laser spot welds is investigated. The FE model is updated based on the measured modal data of hat-plate structures and cast as a structural minimisation problem by the application of NASTRAN codes.

  13. Development and actual application of new welding process for weld-type piston crown in LMC diesel engine

    Energy Technology Data Exchange (ETDEWEB)

    Hatano, H.; Shimizu, H.; Fujiwara, F.; Tokuoka, T.; Nishimoto, T.; Fujita, R.; Matsui, S.; Nakayama, S.

    1985-04-01

    In the improved LMC diesel engines for saving fuel oil, the piston crown becomes more rigid. Unibody casting cannot achieve sufficiently high quality for piston crowns, in the smoothness of the inner surface of the cooling hole, for example. A welded piston crown would solve this problem, in which various pieces could be machined smoothly and then welded together. Joint locations are selected to satisfy welding and design requirements. Welding sequence and welding restraint are analysed using the finite element method. Because pistons can be welded from outside only, narrow gap TIG welding is applied to obtain a smooth bead. Then, narrow gap MAG welding is applied to reduce welding time. TIG-MAG combined welding equipment including welding torchs manipulator, positioner and controller is designed, fabricated, and assembled. Utilizing this equipment, experiments such as welding condition test, restraint crack test, joint property test, operation tests, and mock-up tests are carried out. Then, the products are welded and welds are inspected by an optical fiber for the appearance of the bead and also by ultrasonic and magnetic tests for defects.

  14. An Approach to Maximize Weld Penetration During TIG Welding of P91 Steel Plates by Utilizing Image Processing and Taguchi Orthogonal Array

    Science.gov (United States)

    Singh, Akhilesh Kumar; Debnath, Tapas; Dey, Vidyut; Rai, Ram Naresh

    2017-10-01

    P-91 is modified 9Cr-1Mo steel. Fabricated structures and components of P-91 has a lot of application in power and chemical industry owing to its excellent properties like high temperature stress corrosion resistance, less susceptibility to thermal fatigue at high operating temperatures. The weld quality and surface finish of fabricated structure of P91 is very good when welded by Tungsten Inert Gas welding (TIG). However, the process has its limitation regarding weld penetration. The success of a welding process lies in fabricating with such a combination of parameters that gives maximum weld penetration and minimum weld width. To carry out an investigation on the effect of the autogenous TIG welding parameters on weld penetration and weld width, bead-on-plate welds were carried on P91 plates of thickness 6 mm in accordance to a Taguchi L9 design. Welding current, welding speed and gas flow rate were the three control variables in the investigation. After autogenous (TIG) welding, the dimension of the weld width, weld penetration and weld area were successfully measured by an image analysis technique developed for the study. The maximum error for the measured dimensions of the weld width, penetration and area with the developed image analysis technique was only 2 % compared to the measurements of Leica-Q-Win-V3 software installed in optical microscope. The measurements with the developed software, unlike the measurements under a microscope, required least human intervention. An Analysis of Variance (ANOVA) confirms the significance of the selected parameters. Thereafter, Taguchi's method was successfully used to trade-off between maximum penetration and minimum weld width while keeping the weld area at a minimum.

  15. Optimization of vibratory welding process parameters using response surface methodology

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Pravin Kumar; Kumar, S. Deepak; Patel, D.; Prasad, S. B. [National Institute of Technology Jamshedpur, Jharkhand (India)

    2017-05-15

    The current investigation was carried out to study the effect of vibratory welding technique on mechanical properties of 6 mm thick butt welded mild steel plates. A new concept of vibratory welding technique has been designed and developed which is capable to transfer vibrations, having resonance frequency of 300 Hz, into the molten weld pool before it solidifies during the Shielded metal arc welding (SMAW) process. The important process parameters of vibratory welding technique namely welding current, welding speed and frequency of the vibrations induced in molten weld pool were optimized using Taguchi’s analysis and Response surface methodology (RSM). The effect of process parameters on tensile strength and hardness were evaluated using optimization techniques. Applying RSM, the effect of vibratory welding parameters on tensile strength and hardness were obtained through two separate regression equations. Results showed that, the most influencing factor for the desired tensile strength and hardness is frequency at its resonance value, i.e. 300 Hz. The micro-hardness and microstructures of the vibratory welded joints were studied in detail and compared with those of conventional SMAW joints. Comparatively, uniform and fine grain structure has been found in vibratory welded joints.

  16. Robust Optimization of Thermal Aspects of Friction Stir Welding Using Manifold Mapping Techniques

    DEFF Research Database (Denmark)

    Larsen, Anders Astrup; Lahaye, Domenico; Schmidt, Henrik Nikolaj Blicher

    2008-01-01

    The aim of this paper is to optimize a friction stir welding process taking robustness into account. The optimization problems are formulated with the goal of obtaining desired mean responses while reducing the variance of the response. We restrict ourselves to a thermal model of the process...... and use the manifold mapping technique to solve the optimization problems using a fast analytical coarse and an expensive accurate fine model. The statistics of the response are calculated using Taylor expansions and are compared to Monte Carlo simulations. The results show that the use of manifold...... mapping reduces the number of fine model evaluations required and that the Taylor expansion approach gives good results when compared to Monte Carlo simulations....

  17. Friction Pull Plug Welding in Aluminum Alloys

    Science.gov (United States)

    Brooke, Shane A.; Bradford, Vann

    2012-01-01

    NASA's Marshall Space Flight Center (MSFC) has recently invested much time and effort into the process development of Friction Pull Plug Welding (FPPW). FPPW, is a welding process similar to Friction Push Plug Welding in that, there is a small rotating part (plug) being spun and simultaneously pulled (forged) into a larger part. These two processes differ, in that push plug welding requires an internal reaction support, while pull plug welding reacts to the load externally. FPPW was originally conceived as a post proof repair technique for the Space Shuttle fs External Tank. FPPW was easily selected as the primary weld process used to close out the termination hole on the Constellation Program's ARES I Upper Stage circumferential Self-Reacting Friction Stir Welds (SR-FSW). The versatility of FPPW allows it to also be used as a repair technique for both SR-FSW and Conventional Friction Stir Welds. To date, all MSFC led development has been concentrated on aluminum alloys (2195, 2219, and 2014). Much work has been done to fully understand and characterize the process's limitations. A heavy emphasis has been spent on plug design, to match the various weldland thicknesses and alloy combinations. This presentation will summarize these development efforts including weld parameter development, process control, parameter sensitivity studies, plug repair techniques, material properties including tensile, fracture and failure analysis.

  18. Microstructure Characterization and Hardness Evaluation of Alloy 52 Welded Stainless Steel 316 Subjected to Ultrasonic Nanocyrtal Surface Modification Technique

    Energy Technology Data Exchange (ETDEWEB)

    Kim, H. D.; Amanov, A.; Pyun, Y. S. [Sun Moon Univ., Asan (Korea, Republic of); Kim, Y. S.; Choi, Y. S. [Andong National Univ., Andong (Korea, Republic of)

    2015-10-15

    In this study, an ultrasonic nanocrystal surface modification (UNSM) technique was applied to dissimilar weld point between STS316L and Alloy 52. This UNSM technique is a patented technology, which can be described as a type of ultrasonic cold-forging technology. It has been demonstrated that the UNSM technique is a simple method to produce a nanocrystalline surface layer at the top surface of metallic materials. Microstructure and hardness of STS316L and Alloy 52 are investigated before and after UNSM treatment. It is expected according to the previous study that the UNSM technique is able to release the residual stress which delays PWSCC. In this study, microstructural characterization and hardness evaluation of STS316L and welded Alloy 52 subjected to UNSM technique were investigated.

  19. Residual stress in a laser welded EUROFER blanket module assembly using non-destructive neutron diffraction techniques

    Energy Technology Data Exchange (ETDEWEB)

    Hughes, D.J., E-mail: d.hughes@warwick.ac.uk [WMG, University of Warwick, Coventry CV4 7AL (United Kingdom); Koukovini-Platia, E. [CERN, CH-1211 Geneva 23 (Switzerland); Heeley, E.L. [Department of Physical Sciences, Open University, Walton Hall, Milton Keynes MK7 6AA (United Kingdom)

    2014-02-15

    Highlights: • Residual stresses were determined in a welded EUROFER blanket assembly with integrated cooling channels. • Good agreement was seen between experimentally determined and predicted stresses. • We show that microstructure changes that occur in EUROFER steels during welding must be considered for residual stress determination. • An experimental route is proposed for validation of predicted stresses in reactor components using non-destructive diffraction techniques. - Abstract: Whilst the structural integrity and lifetime considerations in welded joints for blanket modules can be predicted using finite element software, it is essential to prove the validity of these simulations. This paper provides detailed analysis for the first time, of the residual stress state in a laser-welded sample with integral cooling channels. State-of-the-art non-destructive neutron diffraction was employed to determine the triaxial stress state and to understand microstructural changes around the heat affected zone. Synchrotron X-ray diffraction was used to probe the variation of strain-free lattice reference parameter around the weld zone allowing correction of the neutron measurements. This paper details an important experimental route to validation of predicted stresses in complex safety-critical reactor components for future applications.

  20. WELDING METHOD

    Science.gov (United States)

    Cornell, A.A.; Dunbar, J.V.; Ruffner, J.H.

    1959-09-29

    A semi-automatic method is described for the weld joining of pipes and fittings which utilizes the inert gasshielded consumable electrode electric arc welding technique, comprising laying down the root pass at a first peripheral velocity and thereafter laying down the filler passes over the root pass necessary to complete the weld by revolving the pipes and fittings at a second peripheral velocity different from the first peripheral velocity, maintaining the welding head in a fixed position as to the specific direction of revolution, while the longitudinal axis of the welding head is disposed angularly in the direction of revolution at amounts between twenty minutas and about four degrees from the first position.

  1. The Welding Institute has developed the strategy of the LHC magnets welding; L' institut de soudure a developpe la strategie de soudage des aimants du LHC

    Energy Technology Data Exchange (ETDEWEB)

    Champigny, F

    2008-11-15

    The Welding Institute has participated to the realization of the Large Hadron Collider (LHC) in the framework of two expert missions, the first one in research and development and the other one in inspection. (O.M.)

  2. Development of an Automatic Beam Focal Detection System for Electron Beam Welding

    OpenAIRE

    Seigo, Hiramoto; Megumi, OHMINE; Masahiko, SAKAMOTO; Manufacturing Development Laboratory, Mitsubishi Electric Corporation

    1992-01-01

    In electron beam welding, it is very important to set the beam's focal position on a workpiece properly. However, it is very difficult to position one accurately in the case of workpieces having complex joint geometry. A new beam focal detection system has been developed as part of an intelligent wedling system for electron bearn welding. When electrons are irradiated on a workpiece, backscattered electrons, thermoelectrons, secondary electrons, ions or X-rays are emitted from the workpiece. ...

  3. Development of laser materials processing and laser metrology techniques

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Cheol Jung; Chung, Chin Man; Kim, Jeong Mook; Kim, Min Suk; Kim, Kwang Suk; Baik, Sung Hoon; Kim, Seong Ouk; Park, Seung Kyu

    1997-09-01

    The applications of remote laser materials processing and metrology have been investigated in nuclear industry from the beginning of laser invention because they can reduce the risks of workers in the hostile environment by remote operation. The objective of this project is the development of laser material processing and metrology techniques for repairing and inspection to improve the safety of nuclear power plants. As to repairing, we developed our own laser sleeve welding head and innovative optical laser weld monitoring techniques to control the sleeve welding process. Furthermore, we designedand fabricated a 800 W Nd:YAG and a 150 W Excimer laser systems for high power laser materials processing in nuclear industry such as cladding and decontamination. As to inspection, we developed an ESPI and a laser triangulation 3-D profile measurement system for defect detection which can complement ECT and UT inspections. We also developed a scanning laser vibrometer for remote vibration measurement of large structures and tested its performance. (author). 58 refs., 16 tabs., 137 figs.

  4. Computer-assisted surgery and intraoral welding technique for immediate implant-supported rehabilitation of the edentulous maxilla: case report and technical description.

    Science.gov (United States)

    Albiero, Alberto Maria; Benato, Renato

    2016-09-01

    Complications are frequently reported when combining computer assisted flapless surgery with an immediate loaded prefabricated prosthesis. The authors have combined computer-assisted surgery with the intraoral welding technique to obtain a precise passive fit of the immediate loading prosthesis. An edentulous maxilla was rehabilitated with four computer assisted implants welded together intraorally and immediately loaded with a provisional restoration. A perfect passive fit of the metal framework was obtained that enabled proper osseointegration of implants. Computer assisted preoperative planning has been shown to be effective in reducing the intraoperative time of the intraoral welding technique. No complications were observed at 1 year follow-up. This guided-welded approach is useful to achieve a passive fit of the provisional prosthesis on the inserted implants the same day as the surgery, reducing intraoperative time with respect to the traditional intraoral welding technique. Copyright © 2015 John Wiley & Sons, Ltd. Copyright © 2015 John Wiley & Sons, Ltd.

  5. Solid State Welding Development at Marshall Space Flight Center

    Science.gov (United States)

    Ding, Robert J.; Walker, Bryant

    2012-01-01

    What is TSW and USW? TSW is a solid state weld process consisting of an induction coil heating source, a stir rod, and non-rotating containment plates Independent heating, stirring and forging controls Decouples the heating, stirring and forging process elements of FSW. USW is a solid state weld process consisting of an induction coil heating source, a stir rod, and a non-rotating containment plate; Ultrasonic energy integrated into non-rotating containment plate and stir rod; Independent heating, stirring and forging controls; Decouples the heating, stirring and forging process elements of FSW.

  6. Wear behavior of the surface alloyed AISI 1020 steel with Fe-Nb-B by TIG welding technique

    Energy Technology Data Exchange (ETDEWEB)

    Kilinc, B., E-mail: bkilinc@sakarya.edu.tr; Durmaz, M.; Abakay, E. [Department of Metallurgical and Materials Engineering, Institute of Arts and Sciences, SakaryaUniversity, Esentepe Campus, 54187Sakarya (Turkey); Sen, U.; Sen, S. [Department of Metallurgical and Materials Engineering, Engineering Faculty, Sakarya University, Esentepe Campus, 54187 Sakarya (Turkey)

    2015-03-30

    Weld overlay coatings also known as hardfacing is a method which involves melting of the alloys and solidification for applied coatings. Recently hardfacing by welding has become a commonly used technique for improvement of material performance in extreme (high temperature, impact/abrasion, erosion, etc.) conditions.In the present study, the coatings were produced from a mixture of ferrous niobium, ferrous boron and iron powders in the ranges of -45µm particle size with different ratio. Fe{sub 12}Nb{sub 5}B{sub 3} and Fe{sub 2}NbBalloys were coated on the AISI 1020 steel surface by TIG welding. The phases formed in the coated layer are Fe{sub 2}B, NbB{sub 2}, NbFeB and Fe0,2 Nb{sub 0,8} phases. The hardness of the presence phases are changing between 1689±85 HV{sub 0.01}, and 181±7 HV{sub 0.1}. Microstructural examinations were realized by optical and scanning electron microscopy. The wear and friction behaviors of Fe{sub 12}Nb{sub 5}B{sub 3} and Fe2NbB realized on the AISI 1020 steel were investigated by the technique of TIG welding by using ball-on-disk arrangement against alumina ball.

  7. Wear behavior of the surface alloyed AISI 1020 steel with Fe-Nb-B by TIG welding technique

    Science.gov (United States)

    Kilinc, B.; Durmaz, M.; Abakay, E.; Sen, U.; Sen, S.

    2015-03-01

    Weld overlay coatings also known as hardfacing is a method which involves melting of the alloys and solidification for applied coatings. Recently hardfacing by welding has become a commonly used technique for improvement of material performance in extreme (high temperature, impact/abrasion, erosion, etc.) conditions.In the present study, the coatings were produced from a mixture of ferrous niobium, ferrous boron and iron powders in the ranges of -45µm particle size with different ratio. Fe12Nb5B3 and Fe2NbBalloys were coated on the AISI 1020 steel surface by TIG welding. The phases formed in the coated layer are Fe2B, NbB2, NbFeB and Fe0,2 Nb0,8 phases. The hardness of the presence phases are changing between 1689±85 HV0.01, and 181±7 HV0.1. Microstructural examinations were realized by optical and scanning electron microscopy. The wear and friction behaviors of Fe12Nb5B3 and Fe2NbB realized on the AISI 1020 steel were investigated by the technique of TIG welding by using ball-on-disk arrangement against alumina ball.

  8. Sensor development and integration for robotized laser welding

    NARCIS (Netherlands)

    Iakovou, D.

    2009-01-01

    Laser welding requires fast and accurate positioning of the laser beam over the seam trajectory. The task of accurate positioning of the laser tools is performed by robotic systems. It is therefore necessary to teach the robot the path it has to follow. Seam teaching is implemented in several ways:

  9. Development of laser beam welding transverse-varestraint test for assessment of solidification cracking susceptibility in laser welds

    Science.gov (United States)

    Chun, Eun-Joon; Baba, Hayato; Nishimoto, Kazutoshi; Saida, Kazuyoshi

    2015-05-01

    In order to quantitatively evaluate the solidification cracking susceptibility in laser welds of type 310S stainless steel, a transverse-Varestraint testing system using a laser beam welding apparatus was newly constructed. The timing-synchronization between the laser oscillator, welding robot and hydraulic pressure devices was established by employing high-speed camera observations together with electrical signal control among the three components. Moreover, the yoke-drop time measured by the camera was used to prevent underestimation of the crack length. The laser beam melt-run welding used a variable welding speed from 10.0 to 40.0 mm/s, while the gas tungsten arc welding varied the welding speed from 1.67 to 5.00 mm/s. As the welding speed increased from 1.67 to 40.0mm/s, the solidification brittle temperature range of type 310S stainless steel welds was reduced from 146 to 120 K. It follows that employing the laser beam welding process mitigates the solidification cracking susceptibility for type 310S stainless steel welds.

  10. Preliminary Study for Development of Welds Integrity Verification Equipment for the Small Bore Piping

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Geun Suk; Lee, Jong Eun; Ryu, Jung Hoon; Cho, Kyoung Youn; Sohn, Myoung Sung [KEA, Seoul (Korea, Republic of); Lee, Sanghoon [Korea Institute of Materials Science, Changwon (Korea, Republic of); Sung, Gi Ho [SUNG IL(SIM)Co., Busan (Korea, Republic of); Cho, Hong Seok [KEPCO KPS, Naju (Korea, Republic of)

    2016-10-15

    It has been reported leakage accident of small-bore piping in Korea. Leakage accident of small-bore pipes are those that will increase due to the aging of the nuclear power plant. And if leakage of the pipe is repaired by using the clamping device when it occur accident, it is economically benefits. The clamping device is a fastening device used to hold or secure objects tightly together to prevent movement or separation through the application of inward pressure. However, when the accident occurs, it can't immediately respond because maintenance and repairing technology are not institutionalized in KEPIC. Thus it appears an economic loss. The technology for corresponding thereto is necessary for the safety of the operation of nuclear power plants. The purpose of this research is to develop an online repairing technology of socket welded pipe and vibration monitoring system of small-bore pipe in the nuclear power plant. Specifically, detailed studies are as follows : • Development of weld overlay method of safety class socket welded connections • Development of Mechanical Clamping Devices for Safety Class 2, 3 small-bore pipe. The purpose of this study is to develop an online repairing technology of socket welded pipe and vibration monitoring system of small-bore pipe, resulting in degraded plant systems. And it is necessary to institutionalize the technology. The fatigue crack testing of socket welded overlay will be performed and fatigue life evaluation method will be developed in second year. Also prototype fabrication of mechanical clamping device will be completed. Base on final goal, the intent is to propose practical evaluation tools, design and fabrication methods for socket welded connection integrity. And result of this study is to development of KEPIC code case approved technology for on-line repairing system of socket welded connection and fabrication of mechanical clamping device.

  11. Improving fatigue performance of rail thermite welds

    Directory of Open Access Journals (Sweden)

    Winiar L.

    2010-06-01

    Full Text Available Rail transport development offers economic and ecological interests. Nevertheless, it requires heavy investments in rolling material and infrastructure. To be competitive, this transportation means must rely on safe and reliable infrastructure, which requires optimization of all implemented techniques and structure. Rail thermite (or aluminothermic welding is widely used within the railway industry for in-track welding during re-rail and defect replacement. The process provides numerous advantages against other welding technology commonly used. Obviously, future demands on train traffic are heavier axle loads, higher train speeds and increased traffic density. Thus, a new enhanced weld should be developed to prevent accidents due to fracture of welds and to lower maintenance costs. In order to improve such assembly process, a detailed metallurgical study coupled to a thermomechanical modelling of the phenomena involved in the thermite welding process is carried out. Obtained data enables us to develop a new improved thermite weld (type A. This joint is made by modifying the routinely specified procedure (type B used in a railway rail by a standard gap alumino-thermic weld. Joints of type A and B are tested and compared. Based on experimental temperature measurements, a finite element analysis is used to calculate the thermal residual stresses induced. In the vicinity of the weld, the residual stress patterns depend on the thermal conditions during welding as it also shown by litterature [1, 2]. In parallel, X-Ray diffraction has been used to map the residual stress field that is generated in welded rail of types A and B. Their effect on fatigue crack growth in rail welds is studied. An experimental study based on fatigue tests of rails welded by conventional and improved processes adjudicates on the new advances and results will be shown.

  12. Improving Fatigue Performance of AHSS Welds

    Energy Technology Data Exchange (ETDEWEB)

    Feng, Zhili [ORNL; Yu, Xinghua [ORNL; ERDMAN III, DONALD L [ORNL; Wang, Yanli [ORNL; Kelly, Steve [ArcelorMittal USA; Hou, Wenkao [ArcelorMittal USA; Yan, Benda [ArcelorMittal USA; Wang, Zhifeng [Colorado School of Mines, Golden; Yu, Zhenzhen [Colorado School of Mines, Golden; Liu, Stephen [Colorado School of Mines, Golden

    2015-03-01

    Reported herein is technical progress on a U.S. Department of Energy CRADA project with industry cost-share aimed at developing the technical basis and demonstrate the viability of innovative in-situ weld residual stresses mitigation technology that can substantially improve the weld fatigue performance and durability of auto-body structures. The developed technology would be costeffective and practical in high-volume vehicle production environment. Enhancing weld fatigue performance would address a critical technology gap that impedes the widespread use of advanced high-strength steels (AHSS) and other lightweight materials for auto body structure light-weighting. This means that the automotive industry can take full advantage of the AHSS in strength, durability and crashworthiness without the concern of the relatively weak weld fatigue performance. The project comprises both technological innovations in weld residual stress mitigation and due-diligence residual stress measurement and fatigue performance evaluation. Two approaches were investigated. The first one was the use of low temperature phase transformation (LTPT) weld filler wire, and the second focused on novel thermo-mechanical stress management technique. Both technical approaches have resulted in considerable improvement in fatigue lives of welded joints made of high-strength steels. Synchrotron diffraction measurement confirmed the reduction of high tensile weld residual stresses by the two weld residual stress mitigation techniques.

  13. Structural degradation of heterogeneous welded joints

    Directory of Open Access Journals (Sweden)

    Eva Schmidová

    2012-09-01

    Full Text Available Developing the techniques of welding materials with higher dynamic strength onto the rolling surfaces of rails is one of the options for increasing their operational endurance. The subject of this paper is an analyses of heterogeneous weld interfaces experimentally manufactured by welding medium-carbon austenitic steels onto high-carbon unalloyed pearlitic steels. The analyses focus on examinations of the marginal mixing of the materials at the weld interface and the circumstances under which intercrystalline cracks form in the weld deposit layers. Structural analyses, chemical microanalyses and a hardness assessment were performed in order to identify the corresponding structural changes. The proportion of zonal vs. interdendritic segregation of the alloying elements in the degradation of the welded joint was distinguished. We described the nature of the structural heterogeneities produced, locally connected with the martensitic transformation. The chemical heterogeneity leading to the formation of martensite at grain boundaries was identified as the limiting effect.

  14. Friction Stir Welding of Steel Alloys

    Science.gov (United States)

    Ding, R. Jeffrey; Munafo, Paul M. (Technical Monitor)

    2001-01-01

    The friction stir welding process has been developed primarily for the welding of aluminum alloys. Other higher melting allows such, as steels are much more difficult to join. Special attention must be given to pin tool material selection and welding techniques. This paper addresses the joining of steels and other high melting point materials using the friction stir welding process. Pin tool material and welding parameters will be presented. Mechanical properties of weldments will also be presented. Significance: There are many applications for the friction stir welding process other than low melting aluminum alloys. The FSW process can be expanded for use with high melting alloys in the pressure vessel, railroad and ship building industries.

  15. Nondestructive Online Detection of Welding Defects in Track Crane Boom Using Acoustic Emission Technique

    Directory of Open Access Journals (Sweden)

    Yong Tao

    2014-04-01

    Full Text Available Nondestructive detection of structural component of track crane is a difficult and costly problem. In the present study, acoustic emission (AE was used to detect two kinds of typical welding defects, that is, welding porosity and incomplete penetration, in the truck crane boom. Firstly, a subsidiary test specimen with special preset welding defect was designed and added on the boom surface with the aid of steel plates to get the synchronous deformation of the main boom. Then, the AE feature information of the welding defect could be got without influencing normal operation of equipment. As a result, the rudimentary location analysis can be attained using the linear location method and the two kinds of welding defects can be distinguished clearly using AE characteristic parameters such as amplitude and centroid frequency. Also, through the comparison of two loading processes, we concluded that the signal produced during the first loading process was mainly caused by plastic deformation damage and during the second loading process the stress release and structure friction between sections in welding area are the main acoustic emission sources. Thus, the AE is an available tool for nondestructive online detection of latent welding defects of structural component of track crane.

  16. Development of a telerobotic welding virtual environment for nuclear pipeline maintenance

    Energy Technology Data Exchange (ETDEWEB)

    Dong, N.; Li, H.C.; Gao, H.M.; Ni, J.; Wu, L. [Harbin Inst. of Technology (China). National Key Laboratory of Advanced Welding Production Technology

    2009-03-11

    Telerobotic welding is used to maintain nuclear pipelines in hazardous and narrow environments. This paper presented a virtual environment designed to both visualize and operate a telerobotic system. The system was designed to allow operators to handle the virtual robot at local sites using a keyboard or mouse as well as to control data transfer and the robot's motor. Sensor information transfer was directed from the robot to the virtual environment via photoelectricity encoder data, visual data, force data, laser disposed data and welding data. Sensor information was presented in the virtual environment. The virtual environment design included both modelling and calibration capabilities for designing static and dynamic objects. A kinematic analysis of the 9 degrees of freedom pipeline welding robot was presented. Pipeline calibration was conducted using a surface tracking strategy with a shared force control technique. Results of the study showed that the virtual environment increased the accuracy of the telerobotic system. 5 refs., 2 tabs., 8 figs.

  17. Controlling Angular Distortion in Manual Metal Arc Welding of Austenitic Stainless Steels Using Back-step Technique

    Directory of Open Access Journals (Sweden)

    Abdul Sameea Jasim Abdul Zehra Jilabi

    2018-01-01

    Full Text Available Nowadays, austenitic stainless steels (A.S.S. have many industrial applications in the fields of chemical and petrochemical processing, marine, medicine, water treatment, petroleum refining, food and drinks processing, nuclear power generation etc. The secret behind this wide range of applications is the fact that A.S.S. have great corrosion resistance, high strength and scale resistance at elevated temperatures, good ductility at low temperatures approached to absolute zero in addition to notable weldability. On the other hand, manual metal arc (MMA is probably the most common process used for the welding of A.S.S. Unfortunately, MMA welding of A.S.S. could be associated with considerable distortion. Uncontrolled or excessive distortion usually increases the cost of the production process due to the high expense of rectification or replacing the weldment by a non-distorted one. MMA welding of A.S.S. was carried out using the back-step technique with various bead lengths, and without using this technique for comparison. Results have showed that the angular distortion was a function of the bead length in the back-step welding of A.S.S. The angular distortion decreased by (14.32% when the back-step technique was used with a (60 mm length for each bead, and by (41.08% when the bead length was (40 mm. On the other hand, it increased by (25% when the back-step technique was done with a (30 mm length for each bead.

  18. AISI/DOE Technology Roadmap Program: Development of Appropriate Resistance Spot Welding Practice for Transformation-Hardened Steels

    Energy Technology Data Exchange (ETDEWEB)

    Wayne Chuko; Jerry Gould

    2002-07-08

    This report describes work accomplished in the project, titled ''Development of Appropriate Resistance Spot Welding Practice for Transformation-Hardened Steels.'' The Phase 1 of the program involved development of in-situ temper diagrams for two gauges of representative dual-phase and martensitic grades of steels. The results showed that tempering is an effective way of reducing hold-time sensitivity (HTS) in hardenable high-strength sheet steels. In Phase 2, post-weld cooling rate techniques, incorporating tempering, were evaluated to reduce HTS for the same four steels. Three alternative methods, viz., post-heating, downsloping, and spike tempering, for HTS reduction were investigated. Downsloping was selected for detailed additional study, as it appeared to be the most promising of the cooling rate control methods. The downsloping maps for each of the candidate steels were used to locate the conditions necessary for the peak response. Three specific downslope conditions (at a fix ed final current for each material, timed for a zero-, medium-, and full-softening response) were chosen for further metallurgical and mechanical testing. Representative samples, were inspected metallographically, examining both local hardness variations and microstructures. The resulting downslope diagrams were found to consist largely of a C-curve. The softening observed in these curves, however, was not supported by subsequent metallography, which showed that all welds made, regardless of material and downslope condition, were essentially martensitic. CCT/TTT diagrams, generated based on microstructural modeling done at Oak Ridge National Laboratories, showed that minimum downslope times of 2 and 10 s for the martensitic and dual-phase grades of steels, respectively, were required to avoid martensite formation. These times, however, were beyond those examined in this study. These results show that downsloping is not an effective means of reducing HTS for

  19. A six-year follow-up of full-arch immediate restorations fabricated with an intraoral welding technique.

    Science.gov (United States)

    Degidi, Marco; Nardi, Diego; Piattelli, Adriano

    2013-06-01

    The aim of this study was to evaluate the 6-year effectiveness of maxillary and mandibular full-arch immediately loaded prostheses fabricated using an intraoral welding technique. All patients received the same day of surgery a fixed, full-arch prosthesis supported by an intraorally welded titanium framework created directly in the patient's mouth using a titanium bar. Life table analysis of implant survival, complications, and any other adverse events were recorded at yearly follow-up for a period of 6 years. One hundred twenty-four (86.11%) of 144 implants placed in maxillary cases and 87 (77.68%) of 112 implants placed in mandible cases completed the planned 6-year follow-up. At the 72-month follow-up, the accumulated mean marginal bone loss was, respectively, 1.39 mm (SD = 0.67) for the implants placed in the maxilla (n = 124) and 1.29 mm (SD = 0.71) for the implants placed in the mandible (n = 87). Fracturing of the composite resin superstructure was the most common adverse event. After a 6-year follow-up period, the intraoral welding technique proved to be a predictable technique for successfully rehabilitating the fully edentulous patient with a fixed and immediate prosthesis.

  20. Computerized adaptive control weld skate with CCTV weld guidance project

    Science.gov (United States)

    Wall, W. A.

    1976-01-01

    This report summarizes progress of the automatic computerized weld skate development portion of the Computerized Weld Skate with Closed Circuit Television (CCTV) Arc Guidance Project. The main goal of the project is to develop an automatic welding skate demonstration model equipped with CCTV weld guidance. The three main goals of the overall project are to: (1) develop a demonstration model computerized weld skate system, (2) develop a demonstration model automatic CCTV guidance system, and (3) integrate the two systems into a demonstration model of computerized weld skate with CCTV weld guidance for welding contoured parts.

  1. Development of New Materials and Technologies for Welding and Surfacing at Research and Production Center "Welding Processes and Technologies"

    Science.gov (United States)

    Kozyrev, N. A.; Kryukov, R. E.; Galevsky, G. V.; Titov, D. A.; Shurupov, V. M.

    2015-09-01

    The paper provides description of research into the influence of new materials and technologies on quality parameters of welds and added metal carried out at research and production center «Welding processes and technologies». New welding technologies of tanks for northern conditions are considered, as well as technologies of submerged arc welding involving fluxing agents AN - 348, AN - 60, AN - 67, OK. 10.71 and carbon-fluorine containing additives, new flux cored wires and surfacing technologies, teaching programs and a trainer for welders are designed.

  2. New developments for the ultrasonic inspection of austenitic stainless steel welds

    Energy Technology Data Exchange (ETDEWEB)

    Chassignole, Bertrand; Doudet, Loic; Dupond, Olivier; Fouquet, Thierry; Richard, Benoit [Electricite de France - EDF, 2, rue Louis-Murat, 75008 Paris (France)

    2006-07-01

    EDF R and D undertakes studies in non destructive testing (NDT) for better understanding the influence of various parameters (material, type of defect, geometry) on the 'controllability' of the critical components for nuclear safety. In the field of ultrasonic testing, one of the principal research orientations is devoted to the study of the austenitic stainless steel welds of the primary cooling system. Indeed, the structure of these welds present characteristics making difficult their examination, for example: - a strong anisotropy of the properties of elasticity which, coupled with the heterogeneity of the grain orientations, can involve phenomena of skewing, division and distortion of the beam; - a significant scattering of the waves by the grains involving an high attenuation and sometimes backscattered signals. For several years, actions have been launched to improve comprehension of these disturbing phenomena and to evaluate the controllability of those welds. This work is based on the one hand on experimental analyses on representative mock-ups and on the other hand on the developments of modelling codes taking into account the characteristics of the materials. We present in this document a synthesis of this work by developing the following points in particular: - a description of the phenomena of propagation; - the works undertaken to characterize the structure of the welds; - an example of study coupling experimental and modelling analyses for a butt weld achieved by manual arc welding with coated electrodes. The paper has the following contents: 1. Context; 2. Presentation of the problem; 3. Characterization of austenitic welds; 4. From comprehension to industrial application; 5. Conclusion and perspectives; 5. Conclusion and perspectives. This synthesis shows that each austenitic stainless steel weld is a particular case for the ultrasonic testing. This work allowed to better apprehend the disturbances of the ultrasonic propagation in the

  3. Online resistance spot weld NDE using infrared thermography

    Science.gov (United States)

    Chen, Jian; Feng, Zhili

    2017-04-01

    A new online resistance spot weld non-destructive evaluation (NDE) technique based on infrared (IR) thermography has been developed. It is capable of both real-time online (during welding) and post-weld online/offline (after welding) inspections. The system mainly consists of an IR camera and a computer program with proprietary thermal imaging analysis algorithms integrated into existing production lines. For real-time inspection, the heat flow generated from the welding process (with temperature exceeding 1000°C) is monitored by the IR camera. For post-weld inspection, a novel auxiliary heating device is applied to locally heat the weld region, resulting in temperature changes on the order of 10°C, and the transmitted heat flow is monitored. Unlike the conventional IR NDE method that requires surface coating to reduce the influence of unknown emissivity, the new method can be applied on as-is bare metal surface thanks to the unique "thermal signatures" extracted from infrared thermal images, which positively correlates to weld quality with a high degree of confidence. The new method can be used to reliably detect weld size, surface indents and defects such as cold weld with sufficient accuracy for welds made from various combinations of materials, thickness, stack-up configuration, surface coating conditions and welding conditions.

  4. New welding information system on the internet (Prediction of the properties of weld heat-affected zones

    Directory of Open Access Journals (Sweden)

    M Fujita

    2003-08-01

    Full Text Available To promote continuous transfer and development of welding technology, a new system for predicting the microstructures and mechanical properties of welded joins has been built on the Internet. It combines a database system containing continuous cooling transformation diagrams (CCT diagrams for welding and an expert system for computing weld thermal histories. In addition, this system employs a technique which was invented during the development of another distributed database system called "Data-Free-Way" , which was designed to contain information advanced nuclear materials and materials obtained from other programs of welding research at NIMS in the past. This paper describes the current state of our new system for computing weld thermal histories to predict the properties of welded joints using the CCT diagrams database, which is now available on the Internet. Some problems encountered with the database used in such a system are also referred to.

  5. Development of electromagnetic welding facility of flat plates for nuclear industry

    Science.gov (United States)

    Kumar, Rajesh; Sahoo, Subhanarayan; Sarkar, Biswanath; Shyam, Anurag

    2017-04-01

    Electromagnetic pulse welding (EMPW) process, one of high speed welding process uses electromagnetic force from discharged current through working coil, which develops a repulsive force between the induced current flowing parallel and in opposite direction. For achieving the successful weldment using this process the design of working coil is the most important factor due to high magnetic field on surface of work piece. In case of high quality flat plate welding factors such as impact velocity, angle of impact standoff distance, thickness of flyer and overlap length have to be chosen carefully. EMPW has wide applications in nuclear industry, automotive industry, aerospace, electrical industries. However formability and weldability still remain major issues. Due to ease in controlling the magnetic field enveloped inside tubes, the EMPW has been widely used for tube welding. In case of flat components control of magnetic field is difficult. Hence the application of EMPW gets restricted. The present work attempts to make a novel contribution by investigating the effect of process parameters on welding quality of flat plates. The work emphasizes the approaches and engineering calculations required to effectively use of actuator in EMPW of flat components.

  6. Advanced product design principles applied for developing a reconfigurable multi-station welding workbench

    Directory of Open Access Journals (Sweden)

    Merticaru Vasile

    2017-01-01

    Full Text Available The research results presented in the paper are part of a larger approach concerning the improvement of product design process sustainability by enhancing the effectiveness and efficiency of Product Design activities. As case study, an applied educational project is exemplified as result sample, particularly referring to applying such advanced design principles in developing a reconfigurable multi-station welding workbench, intended to solve the problem of the lack of space which usually most of the welding workshops have to confront with.

  7. PENETRATION AND DEFECT FORMATION IN HIGH CURRENT ARC WELDING

    Energy Technology Data Exchange (ETDEWEB)

    MENDEZ,P.F.; EAGAR, T.W.

    2003-01-01

    The work performed during the three previous years can be roughly divided into two main categories: (1) development of advanced modeling techniques; and (2) modeling of arc welding process. The work in the first category comprised the development of the Order of Magnitude Scaling (OMS) technique, which is complementary to numerical modeling techniques such as finite elements, but it provides approximate formulas instead of just numerical results. Borrowing concepts from OMS, another modeling technique based on empirical data was also developed. During this stage special software was also developed. The second category comprised the application of OMS to the three main subsystems of arc welding: the weld pool, the arc, and the electrode. For each of these subsystems they found scaling laws and regimes. With this knowledge, they analyzed the generation of weld pool defects during high current arc welding, proposed a mechanistic description of the process, and possible solutions.

  8. The analysis of spot welding joints of steel sheets with closed profile by ultrasonic method

    OpenAIRE

    Dariusz Ulbrich; Jakub Kowalczyk; Marian Jósko; Jarosław Selech

    2015-01-01

    Resistance spot welding is widely used in the fabrication of vehicle bodies and parts of their equipment. The article presents the methodology and the results of non-destructive ultrasonic testing of resistance spot welded joints of thin steel sheet with closed profile. Non-destructive test results were verified on the basis of welded joint area after destructive testing. The obtained results were used to develop an assessment technique for spot welded joints of closed profile with steel shee...

  9. Standard practice for examination of welds using the alternating current field measurement technique

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2007-01-01

    1.1 This practice describes procedures to be followed during alternating current field measurement examination of welds for baseline and service-induced surface breaking discontinuities. 1.2 This practice is intended for use on welds in any metallic material. 1.3 This practice does not establish weld acceptance criteria. 1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. The values stated in each system might not be exact equivalents; therefore, each system shall be used independently of the other. 1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

  10. Optimization and Characterization of the Friction Stir Welded Sheets of AA 5754-H111: Monitoring of the Quality of Joints with Thermographic Techniques.

    Science.gov (United States)

    De Filippis, Luigi Alberto Ciro; Serio, Livia Maria; Palumbo, Davide; De Finis, Rosa; Galietti, Umberto

    2017-10-11

    Friction Stir Welding (FSW) is a solid-state welding process, based on frictional and stirring phenomena, that offers many advantages with respect to the traditional welding methods. However, several parameters can affect the quality of the produced joints. In this work, an experimental approach has been used for studying and optimizing the FSW process, applied on 5754-H111 aluminum plates. In particular, the thermal behavior of the material during the process has been investigated and two thermal indexes, the maximum temperature and the heating rate of the material, correlated to the frictional power input, were investigated for different process parameters (the travel and rotation tool speeds) configurations. Moreover, other techniques (micrographs, macrographs and destructive tensile tests) were carried out for supporting in a quantitative way the analysis of the quality of welded joints. The potential of thermographic technique has been demonstrated both for monitoring the FSW process and for predicting the quality of joints in terms of tensile strength.

  11. Self-Reacting Friction Stir Welding for Aluminum Alloy Circumferential Weld Applications

    Science.gov (United States)

    Bjorkman, Gerry; Cantrell, Mark; Carter, Robert

    2003-01-01

    Friction stir welding is an innovative weld process that continues to grow in use, in the commercial, defense, and space sectors. It produces high quality and high strength welds in aluminum alloys. The process consists of a rotating weld pin tool that plasticizes material through friction. The plasticized material is welded by applying a high weld forge force through the weld pin tool against the material during pin tool rotation. The high weld forge force is reacted against an anvil and a stout tool structure. A variation of friction stir welding currently being evaluated is self-reacting friction stir welding. Self-reacting friction stir welding incorporates two opposing shoulders on the crown and root sides of the weld joint. In self-reacting friction stir welding, the weld forge force is reacted against the crown shoulder portion of the weld pin tool by the root shoulder. This eliminates the need for a stout tooling structure to react the high weld forge force required in the typical friction stir weld process. Therefore, the self-reacting feature reduces tooling requirements and, therefore, process implementation costs. This makes the process attractive for aluminum alloy circumferential weld applications. To evaluate the application of self-reacting friction stir welding for aluminum alloy circumferential welding, a feasibility study was performed. The study consisted of performing a fourteen-foot diameter aluminum alloy circumferential demonstration weld using typical fusion weld tooling. To accomplish the demonstration weld, weld and tack weld development were performed and fourteen-foot diameter rings were fabricated. Weld development consisted of weld pin tool selection and the generation of a process map and envelope. Tack weld development evaluated gas tungsten arc welding and friction stir welding for tack welding rings together for circumferential welding. As a result of the study, a successful circumferential demonstration weld was produced leading

  12. Ductile damage development in friction stir welded aluminum (AA2024) joints

    DEFF Research Database (Denmark)

    Nielsen, Kim Lau

    2008-01-01

    Ductile damage development in a friction stir welded aluminum joint subjected to tension is analyzed numerically by FE-analysis, based on a total Lagrangian formulation. An elastic-viscoplastic constitutive relation that accounts for nucleation and growth of microvoids is applied. Main focus in t...

  13. Passive Visual Sensing in Automatic Arc Welding

    DEFF Research Database (Denmark)

    Liu, Jinchao

    For decades much work has been devoted to the research and development of automatic arc welding systems. However, it has remained a challenging problem. Besides the very complex arc welding process itself, the lack of ability to precisely sense the welding process, including the seam geometry...... and the weld pool, has also prevented the realization of a closed-loop control system for many years, even though a variety of sensors have been developed. Among all the sensor systems, visual sensors have the advantage of receiving visual information and have been drawn more and more attentions. Typical...... industrial solutions for seam detection such as using laser scanners suer from several limitations. For instance, it must be positioned some distance ahead to the molten pool and may cause problem when dealing with shiny surfaces. Existing techniques for weld pool sensing mostly rely on auxiliary light...

  14. Research on the microstructure and properties of laser-MIG hybrid welded joint of Invar alloy

    Science.gov (United States)

    Zhan, Xiaohong; Zhang, Dan; Wei, Yanhong; Wang, Yuhua

    2017-12-01

    In order to solve the problem of large deformation, low production efficiency and high tendency of hot cracking in welding 19.05 mm thick plates of Fe36Ni Invar alloy, laser-MIG hybrid multi-layer welding technique (LMHMW) has been developed. To investigate the influence of different welding parameters on the joint properties, optical microscope observation, SEM, EDS and microhardness measurement were conducted. Experimental results illustrated that different matching of welding parameters significantly affected the depth-to-width ratio, formation of defects and HAZ width. Besides, weld zone were consisted of two regions according to the different grain shape. The region near center of weld seam (region 1) was columnar dendrite induced by laser, while the region far away from weld seam center (region 2) was cellular dendrite which was mainly caused by MIG arc. The peak value of microhardness appeared at the center of weld seam since the grains in region 1 were relatively fine, and the lowest hardness value was obtained in HAZ. In addition, results showed that the sheets can be welded at optimum process parameters, with few defects such as, surface oxidation, porosity, cracks and lack of penetration in the welding seam: laser power of backing weld P = 5500 W, welding current I = 240 A, welding speed v = 1 m/min. laser power of filling weld P = 2000 W, welding current I = 220 A, welding speed v = 0.35 m/min. laser power of cosmetic weld P = 2000 W, welding current I = 300 A, welding speed v = 0.35 m/min.

  15. Development of method to remove weld scallop and ceramic backing material of wedge type and its application

    Science.gov (United States)

    Kang, Sung-Koo; Yang, Jong-Soo; Kim, Ho-Kyung

    2015-06-01

    The weld scallop has been used for joining T-bars. There are a lot of weld scallops in shipbuilding. It is difficult to perform scallop welding due to the inconvenient welding position. This results in many problems such as porosity, slag inclusion, etc. In this study, a new method is devised to remove weld scallops by incorporating a Ceramic Backing Material (CBM). The weld scallop is removed by an elongation of the v groove. In order to insert a CBM into the groove without a weld scallop, a wedge-shaped CBM is developed. The top side of the developed CBM is similar to the shape of a general back bead. The bottom surface has a saw-toothed shape for cutting at a suitable length. This can be attached to the root side of a face plate using adhesive tape, just like a general CBM. Welding experiments in normal and abnormal conditions are carried out and the possibility of burn-through is examined. This CBM's applicability to shipbuilding is verified.

  16. Development of method to remove weld scallop and ceramic backing material of wedge type and its application

    Directory of Open Access Journals (Sweden)

    Sung-Koo Kang

    2015-03-01

    Full Text Available The weld scallop has been used for joining T-bars. There are a lot of weld scallops in shipbuilding. It is difficult to perform scallop welding due to the inconvenient welding position. This results in many problems such as porosity, slag inclusion, etc. In this study, a new method is devised to remove weld scallops by incorporating a Ceramic Backing Material (CBM. The weld scallop is removed by an elongation of the v groove. In order to insert a CBM into the groove without a weld scallop, a wedge-shaped CBM is developed. The top side of the developed CBM is similar to the shape of a general back bead. The bottom surface has a saw-toothed shape for cutting at a suitable length. This can be attached to the root side of a face plate using adhesive tape, just like a general CBM. Welding experiments in normal and abnormal conditions are carried out and the possibility of burn-through is examined. This CBM’s applicability to shipbuilding is verified.

  17. Development of laser decontamination technique

    Energy Technology Data Exchange (ETDEWEB)

    Ogawa, Ryuichiro; Fukui, Yasutaka; Tanimoto, Kenichi [Japan Nuclear Cycle Development Inst., Oarai, Ibaraki (Japan). Oarai Engineering Center

    2002-06-01

    For decommissioning of nuclear fuel facilities, a laser decontamination technique has been developed. The technique was expected to decontaminate high-level radioactive waste to back ground levels, keep the amount of secondary waste low, and be operated by remote control. In the development, a decontamination experiment was executed. Type and operation mode of the laser oscillator, Type and flow rate of the assist gas, repetition rate of the laser pulse, moving velocity of the laser nozzle and irradiation energy were parameters in the experiment. Hot radioactive waste could be decontaminated to background levels uniformly with optimized parameters, which were determined by comparative evaluation. (author)

  18. Ultrasonic assessment of tension shear strength in resistance spot welding

    Science.gov (United States)

    Moghanizadeh, Abbas

    2015-05-01

    Resistance spot welding is extensively used to join sheet steel in the automotive industry. Ultrasonic non-destructive techniques for evaluation of the mechanical properties of resistance spot welding are presented. The aim of this study is to develop the capability of the ultrasonic techniques as an efficient tool in the assessment of the welding characterization. Previous researches have indicated that the measurements of ultrasonic attenuation are sensitive to grain- size variations in an extensive range of metallic alloys. Other researchers have frequently described grain sizes which are able to have significant effects on the physical characteristics of the material. This research provides a novel method to estimate the tension-shear strengths of the resistance spot welding directly from the ultrasonic attenuation measurements. The effects of spot welding parameters on the ultrasonic waves are further investigated. The results confirm that it is possible to determine the spot welding parameters for individual quality by using ultrasonic test.

  19. A density-adaptive SPH method with kernel gradient correction for modeling explosive welding

    Science.gov (United States)

    Liu, M. B.; Zhang, Z. L.; Feng, D. L.

    2017-09-01

    Explosive welding involves processes like the detonation of explosive, impact of metal structures and strong fluid-structure interaction, while the whole process of explosive welding has not been well modeled before. In this paper, a novel smoothed particle hydrodynamics (SPH) model is developed to simulate explosive welding. In the SPH model, a kernel gradient correction algorithm is used to achieve better computational accuracy. A density adapting technique which can effectively treat large density ratio is also proposed. The developed SPH model is firstly validated by simulating a benchmark problem of one-dimensional TNT detonation and an impact welding problem. The SPH model is then successfully applied to simulate the whole process of explosive welding. It is demonstrated that the presented SPH method can capture typical physics in explosive welding including explosion wave, welding surface morphology, jet flow and acceleration of the flyer plate. The welding angle obtained from the SPH simulation agrees well with that from a kinematic analysis.

  20. Heating coil welding technique for connection of large-diameter PE pipes using universally applicable, flexible taped joints; Heizwendelschweissverfahren fuer die Verbindung von PE-Grossrohren mittels universal anwendbarer, flexibler Wickelmuffen

    Energy Technology Data Exchange (ETDEWEB)

    Baudrit, Benjamin; Kraus, Eduard; Heidemeyer, Peter; Bastian, Martin [Sueddeutsche Kunststoff-Zentrum, Wuerzburg (Germany); Kern, Juergen; Neufeld, Wjatscheslaw [Frank und Krah Wickelrohr GmbH, Woelfersheim (Germany)

    2011-07-01

    This research project (Heating coil welding technique for connection of large-diameter PE pipes using universally applicable, flexible taped joints) was carried out by SKZ (Sueddeutsches Kunststoff-Zentrum) in close coopearation with Messrs. Frank and Krah Wickelrohr GmbH with the intention to develop a high-quality, economically efficient joining process for large-diameter pipes. The technique is based on the new technology of heating coil joints which permits the use of any desired joint geometries at acceptable cost. The new technique was validated for joints up to a diameter of 1,000 mm. With the welding parameters calculated in the project, even larger diameter joints are possible in theory.

  1. Tensometry technique for X-ray diffraction in applied analysis of welding; Tensometria por tecnica de difracao de raios X aplicada na analise de soldagens

    Energy Technology Data Exchange (ETDEWEB)

    Turibus, S.N.; Caldas, F.C.M.; Miranda, D.M.; Monine, V.I.; Assis, J.T., E-mail: snturibus@iprj.uerj.b [Universidade do Estado do Rio de Janeiro (IPRJ/UERJ), Nova Friburgo, RJ (Brazil). Inst. Politecnico

    2010-07-01

    This paper presents the analysis of residual stress introduced in welding process. As the stress in a material can induce damages, it is necessary to have a method to identify this residual stress state. For this it was used the non-destructive X-ray diffraction technique to analyze two plates from A36 steel jointed by metal inert gas (MIG) welding. The stress measurements were made by the sin{sup 2{psi}} method in weld region of steel plates including analysis of longitudinal and transverse residual stresses in fusion zone, heat affected zone (HAZ) and base metal. To determine the stress distribution along the depth of the welded material it was used removing of superficial layers made by electropolishing. (author)

  2. STRUCTURAL DEGRADATION OF HETEROGENEOUS WELDED JOINTS

    Directory of Open Access Journals (Sweden)

    Eva Schmidová

    2012-10-01

    Full Text Available Developing the techniques of welding materials with higher dynamic strength onto the rolling surfaces of rails is one of the options for increasing their operational endurance. The subject of this paper is an analysis of heterogeneous weld joints experimentally manufactured by welding medium-carbon austenitic steels onto high-carbon unalloyed pearlitic steels. The analyses focus on examinations of the marginal mixing of the materials at the fusion line and the circumstances under which intercrystalline cracks form in the weld deposit layers. Structural analyses, chemical microanalyses and a hardness assessment were performed in order to identify the corresponding structural changes. The proportion of zonal vs. interdendritic segregation of the alloying elements in the degradation of the welded joint was distinguished. We described the nature of the structural heterogeneities produced, locally connected with the martensitic transformation. The chemical heterogeneity leading to the formation of martensite at grain boundaries was identified as the limiting effect.

  3. Improvement of stable technique and welding efficiency of digital controlled pulse MAG welder; Digital seigyo pulse MAG yosetsuki ni okeru anteika gijutsu to yosetsu seino no kojo

    Energy Technology Data Exchange (ETDEWEB)

    Nakamata, T.; Uezono, T. [Daihen Corporation, Osaka (Japan)

    1996-10-01

    This paper describes the digital control technology of pulse MAG welders for stable operation and performance improvement. Pulse welding forms a droplet at a wire tip during pulse period, and separates the droplet by pinching it by pulse electromagnetic pinch force. This technology automatically optimizes and stabilizes welding current waveform by digital control to obtain such smooth one pulse- one droplet transfer under various welding conditions, and also controls external characteristics of welding power sources to obtain a constant arc length regardless of the distance between the tip and matrix. The technology offers superior welding stability in a small current range below 100A, and superior high-speed weldability, arc startability and transient responsibility. The newly developed pulse MAG welder mounts the control function of penetration for the first time as pulse welder, and allows stable penetration regardless of torch height. In addition, the welder allows reduction of noise level, superior weldability of galvanized steel sheets, superior basic welding performance, and automatic setting of welding conditions. 2 refs., 19 figs.

  4. Development of Metallographic Etchants for the Microstructure Evolution of A6082-T6 BFSW Welds

    Directory of Open Access Journals (Sweden)

    Abbas Tamadon

    2017-10-01

    Full Text Available BACKGROUND—The solid-phase joining of A6082-T6 plates by bobbin friction stir welding (BFSW is problematic. Better methods are needed to evaluate the microstructural evolution of the weld. However, conventional Al reagents (e.g., Keller’s and Kroll’s do not elucidate the microstructure satisfactorily, specifically regarding grain size and morphology within the weld region. APPROACH—We developed innovative etchants for metallographic observations for optical microscopy. RESULTS—The macrostructure and microstructure of A6082-T6 BFSW welds were clearly demonstrated by optical microscopy analysis. The microetching results demonstrated different microstructures of the Stir Zone (S.Z distinct from the Base Metal (B.M and Heat Affected Zone (HAZ & Thermo-mechanical Affected Zone (TMAZ. The micrographs showed a significant decrease in grain size from 100 μm in B.M to ultrafine 4–10 μm grains for the S.Z. Also, the grain morphology changed from directional columnar in the B.M to equiaxed in the S.Z. Furthermore, thermomechanical recrystallization was observed by the morphological flow of the grain distortion in HAZ and TMAZ. The etchants also clearly show the polycrystalline structure, microflow patterns, and the incoherent interface around inclusion defects. ORIGINALITY—Chemical compositions are identified for a suite of etchant reagents for metallographic examination of the friction-stir welded A6082-T6 alloy. The reagents have made it possible to reveal microstructures not previously evident with optical microscopy.

  5. XRD and DTA Analysis of Developed Agglomerated Fluxes for Submerged Arc Welding

    Directory of Open Access Journals (Sweden)

    Ajay Kumar

    2013-01-01

    Full Text Available A unique study of structural and chemical analysis of crystalline phases in developed agglomerated fluxes was carried out. Thirty-two fluxes were developed by using a mixture of oxides, halides, carbonates, silicates, and ferroalloys for submerged arc welding. The present paper focuses on only ten (out of thirty-two fluxes which were analyzed by X-ray diffraction (XRD to know the different types of oxides formed and changed in oxidation number of metallic centers after sintering process at around 850∘C. To know the effect of temperature over phase transformation and melting of different compounds, differential thermal analysis (DTA was carried out from 1000 to 1400∘C. This study aims to know the quantity of ions present (percentage and melting behavior of developed agglomerated fluxes for submerged arc welding process.

  6. Finite element simulation of laser transmission welding of dissimilar ...

    African Journals Online (AJOL)

    Now-a-days, metal to plastic micro-welding is of great interest in the field of biomedical and electronics applications. Laser transmission welding (LTW) has emerged as the most suitable technique for such applications. In this paper, a three-dimensional finite element (FE) thermal model is developed to simulate the laser ...

  7. Report Summarizing the Effort Required to Initiate Welding of Irradiated Materials within the Welding Cubicle

    Energy Technology Data Exchange (ETDEWEB)

    Frederick, Greg [Electric Power Research Institute (EPRI), Palo Alto, CA (United States); Sutton, Benjamin J. [Electric Power Research Institute (EPRI), Palo Alto, CA (United States); Tatman, Jonathan K. [Electric Power Research Institute (EPRI), Palo Alto, CA (United States); Vance, Mark Christopher [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Smith, Allen W. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Clark, Scarlett R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Feng, Zhili [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Miller, Roger G. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Chen, Jian [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Tang, Wei [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Hu, Xunxiang [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Gibson, Brian T. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-06-01

    The advanced welding facility within a hot cell at the Radiochemical Engineering Development Center of Oak Ridge National Laboratory (ORNL), which has been jointly funded by the U.S. Department of Energy (DOE), Office of Nuclear Energy, Light Water Reactor Sustainability Program and the Electric Power Research Institute, Long Term Operations Program and the Welding and Repair Technology Center, is in the final phase of development. Research and development activities in this facility will involve direct testing of advanced welding technologies on irradiated materials in order to address the primary technical challenge of helium induced cracking that can arise when conventional fusion welding techniques are utilized on neutron irradiated stainless steels and nickel-base alloys. This report details the effort that has been required since the beginning of fiscal year 2017 to initiate welding research and development activities on irradiated materials within the hot cell cubicle, which houses welding sub-systems that include laser beam welding (LBW) and friction stir welding (FSW) and provides material containment within the hot cell.

  8. X-Ray diffraction technique applied to study of residual stresses after welding of duplex stainless steel plates

    Energy Technology Data Exchange (ETDEWEB)

    Monin, Vladimir Ivanovitch; Assis, Joaquim Teixeira de [Instituto Politecnico do Rio e Janeiro (IPRJ), Nova Friburgo, RJ (Brazil); Lopes, Ricardo Tadeu; Turibus, Sergio Noleto; Payao Filho, Joao C., E-mail: sturibus@nuclear.ufrj.br [Universidade Federal do Rio de Janeiro (UFRJ), Rio de Janeiro, RJ (Brazil)

    2014-08-15

    Duplex stainless steel is an example of composite material with approximately equal amounts of austenite and ferrite phases. Difference of physical and mechanical properties of component is additional factor that contributes appearance of residual stresses after welding of duplex steel plates. Measurements of stress distributions in weld region were made by X-ray diffraction method both in ferrite and austenite phases. Duplex Steel plates were joined by GTAW (Gas Tungsten Arc Welding) technology. There were studied longitudinal and transverse stress components in welded butt joint, in heat affected zone (HAZ) and in points of base metal 10 mm from the weld. Residual stresses measured in duplex steel plates jointed by welding are caused by temperature gradients between weld zone and base metal and by difference of thermal expansion coefficients of ferrite and austenite phases. Proposed analytical model allows evaluating of residual stress distribution over the cross section in the weld region. (author)

  9. Remote Welding, NDE and Repair of DOE Standardized Canisters

    Energy Technology Data Exchange (ETDEWEB)

    Eric Larsen; Art Watkins; Timothy R. McJunkin; Dave Pace; Rodney Bitsoi

    2006-05-01

    The U.S. Department of Energy (DOE) created the National Spent Nuclear Fuel Program (NSNFP) to manage DOE’s spent nuclear fuel (SNF). One of the NSNFP’s tasks is to prepare spent nuclear fuel for storage, transportation, and disposal at the national repository. As part of this effort, the NSNFP developed a standardized canister for interim storage and transportation of SNF. These canisters will be built and sealed to American Society of Mechanical Engineers (ASME) Section III, Division 3 requirements. Packaging SNF usually is a three-step process: canister loading, closure welding, and closure weld verification. After loading SNF into the canisters, the canisters must be seal welded and the welds verified using a combination of visual, surface eddy current, and ultrasonic inspection or examination techniques. If unacceptable defects in the weld are detected, the defective sections of weld must be removed, re-welded, and re-inspected. Due to the high contamination and/or radiation fields involved with this process, all of these functions must be performed remotely in a hot cell. The prototype apparatus to perform these functions is a floor-mounted carousel that encircles the loaded canister; three stations perform the functions of welding, inspecting, and repairing the seal welds. A welding operator monitors and controls these functions remotely via a workstation located outside the hot cell. The discussion describes the hardware and software that have been developed and the results of testing that has been done to date.

  10. Final Report of Project Curriculum Development: Pulsed Tig Welding, 1978-1979.

    Science.gov (United States)

    Atlantic County Area Vocational-Technical School, NJ.

    Designed to help unemployed and disadvantaged workers find new career opportunities, this curriculum provides vocational students with a basic course of instruction in pulsed tungsten inert gas (TIG) welding. The first of four sections provides a general background of welding, the welding industry, and welding processes. Section 2 focuses on…

  11. Microstructure and Mechanical Properties of an Ultrasonic Spot Welded Aluminum Alloy: The Effect of Welding Energy

    National Research Council Canada - National Science Library

    He Peng; Daolun Chen; Xianquan Jiang

    2017-01-01

    The aim of this study is to evaluate the microstructures, tensile lap shear strength, and fatigue resistance of 6022-T43 aluminum alloy joints welded via a solid-state welding technique-ultrasonic spot welding (USW...

  12. Initial Development in Joining of ODS Alloys Using Friction Stir Welding

    Energy Technology Data Exchange (ETDEWEB)

    Ren, Weiju [ORNL; Feng, Zhili [ORNL

    2007-08-01

    Solid-state welding of oxide-dispersion-strengthened (ODS) alloy MA956 sheets using friction stir welding (FSW) was investigated. Butt weld was successfully produced. The weld and base metals were characterized using optical microscopy, scanning electronic microscopy, transmission electronic microscopy, and energy dispersion x-ray spectrum. Microhardness mapping was also conducted over the weld region. Analyses indicate that the distribution of the strengthening oxides was preserved in the weld. Decrease in microhardness of the weld was observed but was insignificant. The preliminary results seem to confirm the envisioned feasibility of FSW application to ODS alloy joining. For application to Gen IV nuclear reactor heat exchanger, further investigation is suggested.

  13. Development of remote-controlled circumferential TIG welding system. Enkaku sosashiki TIG enshu jido yosetsu koho no kaihatsu

    Energy Technology Data Exchange (ETDEWEB)

    Fujimoto, T.; Shiga, A. (Kawasaki Steel Corp., Tokyo (Japan))

    1991-03-01

    Development was made of remotely controlled circumferential tungsten inert gas (TIG) welding system. Outer surface of pipe is installed with a welding head truck, while remotely controlling post is done with a remotely controlling board, mounted with power source, control unit, display and speaker, torch cooling unit by water, etc. The operator commences the welding, only after presetting the standard welding condition in the program box, and minutely adjusts the welding condition, truck speed, etc. through monitoring the image and sound. All those items of operation are remotely controlled. The torch is equipped with a molten pool observation camera and microphone, to catch arc noise, therearound. If there is peripheral room, 200mm in radial space, circumferentially outside the pipe, the operation can be safely made even from a very narrow on-ground post. Liberation being made from skillfulness and heavy labor, inconvenience can be immediately confronted and corrected, and welding defect can be prevented from occurring. The present system, upon being applied to on-site welding of city water supply use stainless pipe and gas pipe, was confirmed to be good in practicability. 2 refs., 13 figs., 6 tabs.

  14. Development of a Human and Organizational Factors (HOF) Annex for underwater welding.

    OpenAIRE

    Cullen, Shawn.

    1997-01-01

    CIVINS (Civilian Institutions) Thesis document Recent improvements in underwater welding have led to the increased use of wet and dry hyperbaric welding within the marine construction industry. The general acceptance of underwater welding processes has been further advanced by the standardization of methods, procedures, and certification requirements provided by the American National Standards Institute (ANSI)/American Welding Society (AWS) D3.6 Specification for Underwater Welding. A dedi...

  15. A Neural Network Approach for GMA Butt Joint Welding

    DEFF Research Database (Denmark)

    Christensen, Kim Hardam; Sørensen, Torben

    2003-01-01

    This paper describes the application of the neural network technology for gas metal arc welding (GMAW) control. A system has been developed for modeling and online adjustment of welding parameters, appropriate to guarantee a certain degree of quality in the field of butt joint welding with full...... penetration, when the gap width is varying during the welding process. The process modeling to facilitate the mapping from joint geometry and reference weld quality to significant welding parameters has been based on a multi-layer feed-forward network. The Levenberg-Marquardt algorithm for non-linear least...... squares has been used with the back-propagation algorithm for training the network, while a Bayesian regularization technique has been successfully applied for minimizing the risk of inexpedient over-training. Finally, a predictive closed-loop control strategy based on a so-called single-neuron self...

  16. Physics of arc welding

    Science.gov (United States)

    Eagar, T. W.

    1982-05-01

    A discussion of the factors controlling the size and shape of the weld fusion zone is presented along with a description of current theories of heat and fluid flow phenomena in the plasma and the molten metal weld pool. Although experimental results confirm that surface tension, plasma jets, and weld pool convection all strongly influence the fusion zone shape; no comprehensive model is available from which to predict welding behavior. It is proposed that the lack of such an understanding is a major impediment to development of automated welding processes. In addition, sensors for weld torch positioning are reviewed in terms of the mechnical and electromagnetic energy spectra which have been used. New developments in this area are also needed in order to advance the technology of automated welding.

  17. Development of automatic reactor vessel inspection systems: development of data acquisition and analysis system for the nuclear vessel weld

    Energy Technology Data Exchange (ETDEWEB)

    Park, C. H.; Lim, H. T.; Um, B. G. [Korea Advanced Institute of Science and Technology, Taejeon (Korea)

    2001-03-01

    The objective of this project is to develop an automated ultrasonic data acquisition and data analysis system to examine the reactor vessel weldsIn order to examine nuclear vessel welds including reactor pressure vessel(RPV), huge amount of ultrasonic data from 6 channels should be able to be on-line processed. In addition, ultrasonic transducer scanning device should be remotely controlled, because working place is high radiation area. This kind of an automated ultrasonic testing equipment has not been developed domestically yet In order to develop an automated ultrasonic testing system, RPV ultrasonic testing equipments developed in foreign countries were investigated and the capability of high speed ultrasonic signal processing hardwares was analyzed in this study, ultrasonic signal processing system was designed. And also, ultrasonic data acquisition and analysis software was developed. 11 refs., 6 figs., 9 tabs. (Author)

  18. Integrated sensors for robotic laser welding

    NARCIS (Netherlands)

    Iakovou, D.; Aarts, Ronald G.K.M.; Meijer, J.; Beyer, E.; Dausinger, F; Ostendorf, A; Otto, A.

    2005-01-01

    A welding head is under development with integrated sensory systems for robotic laser welding applications. Robotic laser welding requires sensory systems that are capable to accurately guide the welding head over a seam in three-dimensional space and provide information about the welding process as

  19. The development of in situ fracture toughness evaluation techniques in hydrogen environment

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jy-An John [ORNL; Ren, Fei [ORNL; Tan, Ting [ORNL; Liu, Ken C [ORNL

    2014-01-01

    Fracture behavior and fracture toughness are of great interest regarding reliability of hydrogen pipelines and storage tanks, however, many conventional fracture testing techniques are difficult to be realized under the presence of hydrogen, in addition to the inherited specimen size effect. Thus it is desired to develop novel in situ fracture toughness evaluation techniques to study the fracture behavior of structural materials in hydrogen environments. In this study, a torsional fixture was developed to utilize an emerging fracture testing technique, Spiral Notch Torsion Test (SNTT). The in situ testing results indicated that the exposure to H2 significantly reduces the fracture toughness of 4340 high strength steels by up to 50 percent. Furthermore, SNTT tests conducted in air demonstrated a significant fracture toughness reduction in samples subject to simulated welding heat treatment using Gleeble, which illustrated the effect of welding on the fracture toughness of this material.

  20. Development of a test method for determining the cracking susceptibility of resistance spot welded high strength steel sheets

    OpenAIRE

    Rethmeier, Michael; Suwala, Hubert

    2014-01-01

    In this study a test method for determining the cracking susceptibility of resistance spot welded high strength steel sheets was investigated. The development of a suitable test procedure is based on the External-Loaded Hot Crack Test (PVC-Test). The test modification for resistance spot welding contains a constant tensile force load. The test method for determining the cracking susceptibility was experimentally verified for a high strength steel, a transformation induced plasticity steel (TR...

  1. Concurrent ultrasonic weld evaluation system

    Science.gov (United States)

    Hood, Donald W.; Johnson, John A.; Smartt, Herschel B.

    1987-01-01

    A system for concurrent, non-destructive evaluation of partially completed welds for use in conjunction with an automated welder. The system utilizes real time, automated ultrasonic inspection of a welding operation as the welds are being made by providing a transducer which follows a short distance behind the welding head. Reflected ultrasonic signals are analyzed utilizing computer based digital pattern recognition techniques to discriminate between good and flawed welds on a pass by pass basis. The system also distinguishes between types of weld flaws.

  2. Experimental study of cyclic creep and high-cycle fatigue of welded joints of St3 steel by the DIC technique

    Energy Technology Data Exchange (ETDEWEB)

    Kibitkin, Vladimir V., E-mail: vvk@ispms.tsc.ru; Solodushkin, Andrey I., E-mail: s.ai@sibmail.com; Pleshanov, Vasily S., E-mail: vsp@ispms.tsc.ru [Institute of Strength Physics and Materials Science SB RAS, Tomsk, 634055 (Russian Federation)

    2015-10-27

    In the paper the mechanisms of plastic deformation and fracture of welded joints of steel St3 were investigated at high-cycle fatigue and cyclic creep by the digital image correlation (DIC) technique. The evolution of strain rate is studied for the following regions: base metal, HAZ, and fusion zone. This strain rate evolution can be considered as a mechanical response of material. Three stages of deformation evolution are shown: deformation hardening (I), fatigue crack initiation (II), and the last stage is related to main crack (III). Two criteria are offered to evaluate the current mechanical state of welded joints.

  3. Modeling Stress-Strain State in Butt-Welded Joints after TIG Welding

    Directory of Open Access Journals (Sweden)

    V. Atroshenko

    2015-09-01

    Full Text Available In this paper mathematical model was developed for definition of thermal-welding cycle influence on welding deformations distribution in flat samples of austenitic steels after TIG welding and developed recommendations to reduce the welding deformation on o the machinery for welding with a copper backing.

  4. Development of automatic reactor vessel inspection systems; development of data acquisition and analysis system for the nuclear vessel weld

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jong Po; Park, C. H.; Kim, H. T.; Noh, H. C.; Lee, J. M.; Kim, C. K.; Um, B. G. [Research Institute of KAITEC, Seoul (Korea)

    2002-03-01

    The objective of this project is to develop an automated ultrasonic data acquisition and data analysis system to examine heavy vessel welds. In order to examine nuclear vessel welds including reactor pressure vessel(RPV), huge amount of ultrasonic data from 6 channels should be able to be on-line processed. In addition, ultrasonic transducer scanning device should be remotely controlled, because working place is high radiation area. This kind of an automated ultrasonic testing equipment has not been developed domestically yet. In order to develop an automated ultrasonic testing system, RPV ultrasonic testing equipments developed in foreign countries were investigated and the capability of high speed ultrasonic signal processing hardwares was analyzed. In this study, ultrasonic signal processing system was designed. And also, ultrasonic data acquisition software was developed. The new systems were tested on the RPV welds of Ulchin Unit 6 to confirm their functions and capabilities. They worked very well as designed and the tests were successfully completed. 13 refs., 34 figs., 11 tabs. (Author)

  5. The analysis of spot welding joints of steel sheets with closed profile by ultrasonic method

    Directory of Open Access Journals (Sweden)

    Dariusz Ulbrich

    2015-11-01

    Full Text Available Resistance spot welding is widely used in the fabrication of vehicle bodies and parts of their equipment. The article presents the methodology and the results of non-destructive ultrasonic testing of resistance spot welded joints of thin steel sheet with closed profile. Non-destructive test results were verified on the basis of welded joint area after destructive testing. The obtained results were used to develop an assessment technique for spot welded joints of closed profile with steel sheet, which could be used in factories employing such joints. In addition, the article makes comparison between the costs of the developed assessment technique and currently used destructive method.

  6. Hybrid laser arc welding: State-of-art review

    Science.gov (United States)

    Acherjee, Bappa

    2018-02-01

    Hybrid laser arc welding simultaneously utilizes the arc welding and the laser welding, in a common interaction zone. The synergic effects of laser beam and eclectic arc in the same weld pool results in an increase of welding speed and penetration depth along with the enhancement of gap bridging capability and process stability. This paper presents the current status of this hybrid technique in terms of research, developments and applications. Effort is made to present a comprehensive technical know-how about this process through a systematic review of research articles, industrial catalogues, technical notes, etc. In the introductory part of the review, an overview of the hybrid laser arc welding is presented, including operation principle, process requirements, historical developments, benefits and drawbacks of the process. This is followed by a detailed discussion on control parameters those govern the performance of hybrid laser arc welding process. Thereafter, a report of improvements of performance and weld qualities achieved by using hybrid welding process is presented based on review of several research papers. The succeeding sections furnish the examples of industrial applications and the concluding remarks.

  7. The Development of a Composite Consumable Insert for Submerged ARC Welding

    National Research Council Canada - National Science Library

    1980-01-01

    .... When the submerged arc process was utilized to weld the butt joint in large flat plate structures, the repositioning of the plate for welding of the reverse side was a costly time consuming procedure...

  8. Welding and Brazing Silicon Carbide

    Science.gov (United States)

    Moore, T. J.

    1986-01-01

    Hot isostatic pressing and conventional furnace brazing effective under right conditions. Study performed showed feasibility of welding SiC using several welding and brazing techniques. Use of SiC improves engine efficiency by allowing increase in operating temperature. SiC successfully hot-pressure-welded at 3,550 degrees F (1,950 degrees C) in argon. Refinements of solid-state welding and brazing procedures used sufficient for some specific industrial applications.

  9. Filler wire for aluminum alloys and method of welding

    Science.gov (United States)

    Bjorkman, Jr., Gerald W. O. (Inventor); Cho, Alex (Inventor); Russell, Carolyn K. (Inventor)

    2003-01-01

    A weld filler wire chemistry has been developed for fusion welding 2195 aluminum-lithium. The weld filler wire chemistry is an aluminum-copper based alloy containing high additions of titanium and zirconium. The additions of titanium and zirconium reduce the crack susceptibility of aluminum alloy welds while producing good weld mechanical properties. The addition of silver further improves the weld properties of the weld filler wire. The reduced weld crack susceptibility enhances the repair weldability, including when planishing is required.

  10. Studies of welded joints

    Directory of Open Access Journals (Sweden)

    J. M. Krupa

    2010-07-01

    Full Text Available Studies of a welded joint were described. The joint was made as a result of the reconstruction of a truss and one of the possible means to make a repair. The studies were of a simulation character and were targeted at the detection of welding defects and imperfections thatshould be eliminated in a real structure. A model was designed and on this model the tests and examinations were carried out. The modelwas made under the same conditions as the conditions adopted for repair. It corresponded to the real object in shape and dimensions, and in the proposed technique of welding and welding parameters. The model was composed of five plates joined together with twelve beads.The destructive and non-destructive tests were carried out; the whole structure and the respective welds were also examined visually. Thedefects and imperfections in welds were detected by surface methods of inspection, penetration tests and magnetic particle flaw detection.The model of the welded joint was prepared by destructive methods, a technique that would never be permitted in the case of a realstructure. For the investigations it was necessary to cut out the specimens from the welded joint in direction transverse to the weld run. The specimens were subjected to metallographic examinations and hardness measurements. Additionally, the joint cross-section was examined by destructive testing methods to enable precise determination of the internal defects and imperfections. The surface methods were applied again, this time to determine the severity of welding defects. The analysis has proved that, fabricated under proper conditions and with parameters of the welding process duly observed, the welded joint has good properties and repairs of this type are possible in practice.

  11. Plasma arc welding repair of space flight hardware

    Science.gov (United States)

    Hoffman, David S.

    1993-01-01

    Repair and refurbishment of flight and test hardware can extend the useful life of very expensive components. A technique to weld repair the main combustion chamber of space shuttle main engines has been developed. The technique uses the plasma arc welding process and active cooling to seal cracks and pinholes in the hot-gas wall of the main combustion chamber liner. The liner hot-gas wall is made of NARloyZ, a copper alloy previously thought to be unweldable using conventional arc welding processes. The process must provide extensive heat input to melt the high conductivity NARloyZ while protecting the delicate structure of the surrounding material. The higher energy density of the plasma arc process provides the necessary heat input while active water cooling protects the surrounding structure. The welding process is precisely controlled using a computerized robotic welding system.

  12. Developing Fighting Technique Through Visualization

    Directory of Open Access Journals (Sweden)

    Tim Lajcik

    2012-07-01

    Full Text Available Visualization is a training technique that involves creating a detailed mental “movie” of successful performance. This article describes a type of visualization called “mental rehearsal” and explains how it can be used to reinforce the neuromuscular pattern of proper fighting technique. Drawing on his experience as a professional fighter and college coach, his studies in sport psychology as a college student, and his exposure to mental training techniques at the U.S. Olympic Training Center, the author reveals how to use mental imagery to facilitate the mastery of martial art technique.    

  13. Hybrid/Tandem Laser-Arc Welding of Thick Low Carbon Martensitic Stainless Steel Plates =

    Science.gov (United States)

    Mirakhorli, Fatemeh

    High efficiency and long-term life of hydraulic turbines and their assemblies are of utmost importance for the hydropower industry. Usually, hydroelectric turbine components are made of thick-walled low carbon martensitic stainless steels. The assembly of large hydroelectric turbine components has been a great challenge. The use of conventional welding processes involves typical large groove design and multi-pass welding to fill the groove which exposes the weld to a high heat input creating relatively large fusion zone and heat affected zone. The newly-developed hybrid/tandem laser-arc welding technique is believed to offer a highly competitive solution to improve the overall hydro-turbine performance by combining the high energy density and fast welding speed of the laser welding technology with the good gap bridging and feeding ability of the gas metal arc welding process to increase the productivity and reduce the consumable material. The main objective of this research work is to understand different challenges appearing during hybrid laser-arc welding (HLAW) of thick gauge assemblies of low carbon 13%Cr- 4%Ni martensitic stainless steel and find a practical solution by adapting and optimizing this relatively new welding process in order to reduce the number of welding passes necessary to fill the groove gap. The joint integrity was evaluated in terms of microstructure, defects and mechanical properties in both as-welded and post-welded conditions. A special focus was given to the hybrid and tandem laser-arc welding technique for the root pass. Based on the thickness of the low carbon martensitic stainless steel plates, this work is mainly focused on the following two tasks: • Single pass hybrid laser-arc welding of 10-mm thick low carbon martensitic stainless steel. • Multi-pass hybrid/tandem laser-arc welding of 25-mm thick martensitic stainless steel.

  14. Welding of 316L Austenitic Stainless Steel with Activated Tungsten Inert Gas Process

    Science.gov (United States)

    Ahmadi, E.; Ebrahimi, A. R.

    2015-02-01

    The use of activating flux in TIG welding process is one of the most notable techniques which are developed recently. This technique, known as A-TIG welding, increases the penetration depth and improves the productivity of the TIG welding. In the present study, four oxide fluxes (SiO2, TiO2, Cr2O3, and CaO) were used to investigate the effect of activating flux on the depth/width ratio and mechanical property of 316L austenitic stainless steel. The effect of coating density of activating flux on the weld pool shape and oxygen content in the weld after the welding process was studied systematically. Experimental results indicated that the maximum depth/width ratio of stainless steel activated TIG weld was obtained when the coating density was 2.6, 1.3, 2, and 7.8 mg/cm2 for SiO2, TiO2, Cr2O3, and CaO, respectively. The certain range of oxygen content dissolved in the weld, led to a significant increase in the penetration capability of TIG welds. TIG welding with active fluxes can increase the delta-ferrite content and improves the mechanical strength of the welded joint.

  15. State-of-art and prospects of development of electron beam welding of aerospace vehicles

    Science.gov (United States)

    Kazakov, V. A.; Nazarenko, O. K.

    The paper presents information about industrial application of technological processes of electron beam welding EBW of aerospace objects. The characteristics of advanced equipment are given for welding electron guns, power sources, and control systems. Different types of EBW equipment of chamber-type, with a local and mobile evacuation of welding zone, are described.

  16. Comparative testing of radiographic testing, ultrasonic testing and phased array advanced ultrasonic testing non destructive testing techniques in accordance with the AWS D1.5 bridge welding code.

    Science.gov (United States)

    2014-02-01

    A comprehensive body of non-destructive testing data was collected from steel bridge welds under real-world conditions in a fabricators shop. Three different non-destructive testing (NDT) techniques were used on each weld inspection, these being R...

  17. Automatic welding quality classification for the spot welding based on the Hopfield associative memory neural network and Chernoff face description of the electrode displacement signal features

    Science.gov (United States)

    Zhang, Hongjie; Hou, Yanyan; Zhao, Jian; Wang, Lijing; Xi, Tao; Li, Yafeng

    2017-02-01

    To develop an automatic welding quality classification method for the spot welding based on the Chernoff face image created by the electrode displacement signal features, an effective pattern feature extraction method was proposed by which the Chernoff face images were converted to binary ones, and each binary image could be characterized by a binary matrix. According to expression categories on the Chernoff face images, welding quality was classified into five levels and each level just corresponded to a kind of expression. The Hopfield associative memory neural network was used to build a welding quality classifier in which the pattern feature matrices of some weld samples with different welding quality levels were remembered as the stable states. When the pattern feature matrix of a test weld is input into the classifier, it can be converged to the most similar stable state through associative memory, thus, welding quality corresponding to this finally locked stable state can represent the welding quality of the test weld. The classification performance test results show that the proposed method significantly improves the applicability and efficiency of the Chernoff faces technique for spot welding quality evaluation and it is feasible, effective and reliable.

  18. Design and development of fixture and force measuring system for friction stir welding process using strain gauges

    Energy Technology Data Exchange (ETDEWEB)

    Parida, Biswajit; Vishwakarma, Shiv Dayal; Pal, Sukhomay [IIT Guwahati, Guwahati (India)

    2015-02-15

    We developed a clamping system and an instrumented setup for a vertical milling machine for friction stir welding (FSW) operations and measuring the process forces. Taking into account the gap formation (i.e., lateral movement) and transverse movement of the workpiece, a new type of adjustable fixture was designed to hold the workpiece being welded. For force measurement, a strain gauge based force dynamometer was designed, developed and fabricated. The strain gauges were fitted into the specially designed octagonal members to support the welding plates. When the welding force was applied onto the plates, the load was transferred to the octagonal members and strain was induced in the member. The strains of the strain gauges were measured in terms of voltages using a Wheatstone bridge. To acquire forces in FSW operations, a data acquisition system with the necessary hardware and software was devised and connected to the developed setup. The developed setup was tested in actual welding operations. It is found that the proposed setup can be used in milling machine to perform FSW operations.

  19. Optimization and Characterization of the Friction Stir Welded Sheets of AA 5754-H111: Monitoring of the Quality of Joints with Thermographic Techniques

    Directory of Open Access Journals (Sweden)

    Luigi Alberto Ciro De Filippis

    2017-10-01

    Full Text Available Friction Stir Welding (FSW is a solid-state welding process, based on frictional and stirring phenomena, that offers many advantages with respect to the traditional welding methods. However, several parameters can affect the quality of the produced joints. In this work, an experimental approach has been used for studying and optimizing the FSW process, applied on 5754-H111 aluminum plates. In particular, the thermal behavior of the material during the process has been investigated and two thermal indexes, the maximum temperature and the heating rate of the material, correlated to the frictional power input, were investigated for different process parameters (the travel and rotation tool speeds configurations. Moreover, other techniques (micrographs, macrographs and destructive tensile tests were carried out for supporting in a quantitative way the analysis of the quality of welded joints. The potential of thermographic technique has been demonstrated both for monitoring the FSW process and for predicting the quality of joints in terms of tensile strength.

  20. Development of procedure using plasma welding process to produce {sup 125}I seeds; Desenvolvimento de procedimento utilizando processo de soldagem plasma para confeccao de sementes de {sup 125}I

    Energy Technology Data Exchange (ETDEWEB)

    Feher, Anselmo

    2006-07-01

    The prostate cancer, which is the second cause of death by cancer in men, overcome only by lung cancer, is a problem of public health in Brazil. Brachytherapy is among the possible available treatments for prostate cancer, in which small seeds containing {sup 125}I radioisotope are implanted in the prostate. The seed consists of a titanium sealed capsule with 0.8 mm external diameter and 4.5 mm length, containing a central silver wire with adsorbed {sup 125}I. The plasma arc welding is one of the viable techniques for the sealing process. The equipment used in this technique is less costly than in other processes. The main objective of this work was the development and the validation of the welding procedure using plasma welding process and the elaboration of a sealing routine according to Good Manufacturing Practices. The development of this work has presented the following phases: cut and cleaning of the titanium material, determination of the welding parameters, development of a device for holding the titanium tube during the welding process, validation of sealed sources according to ISO 2919 Sealed Radioactive Sources - General Requirements and Classification, leakage test according to ISO 9978 Sealed Radioactive Sources - Leakage Test Methods and metallographic assays. The developed procedure, to seal {sup 125}I seeds using plasma welding process, has shown to be efficient, satisfying all the established requirements of ISO 2919. The results obtained in this work have given the possibility to establish a routine production process according to the orientations presented in resolution RDC number 59 - Good Manufacturing Practices do Medical Products of the ANVISA - Brazilian Nacional Agency of Sanitary Surveillance. (author)

  1. Robot welding process control

    Science.gov (United States)

    Romine, Peter L.

    1991-01-01

    This final report documents the development and installation of software and hardware for Robotic Welding Process Control. Primary emphasis is on serial communications between the CYRO 750 robotic welder, Heurikon minicomputer running Hunter & Ready VRTX, and an IBM PC/AT, for offline programming and control and closed-loop welding control. The requirements for completion of the implementation of the Rocketdyne weld tracking control are discussed. The procedure for downloading programs from the Intergraph, over the network, is discussed. Conclusions are made on the results of this task, and recommendations are made for efficient implementation of communications, weld process control development, and advanced process control procedures using the Heurikon.

  2. Experimental Development of Dual Phase Steel Laser-arc Hybrid Welding and its Comparison to Laser and Gas Metal Arc Welding

    Directory of Open Access Journals (Sweden)

    Wagner Duarte Antunes

    Full Text Available Abstract Dual phase DP600 steels have been used in many automobile structures and laser welding has been the standard method for the joining of different sections. This work proposed a comparison between laser welding with arc welding (GMAW and with hybrid laser-arc welding in order to access the microstructures and the mechanical behavior. The laser and hybrid welds are competitive in terms of microstructure and mechanical behavior, presenting both acceptable and tough welds. The maximum ductility of the laser and hybrid welds are very similar, around 14%, and near to the values observed in the base material. The GMAW presents low ductility due to the softening caused by tampering of the martensite, and thus is unacceptable as the welding procedure.

  3. Development of a Powder-feed Device and Procedures for the Application of an Experimental Alloy in Overhead PTA-P Welding

    OpenAIRE

    Alves, Jônathas Alexandre; Silva, Régis Henrique Gonçalves e; Dutra, Jair Carlos

    2015-01-01

    Abstract: When they are damaged by cavitation, hydroelectric power plant turbine blades must be repaired using operations that could benefit from developments in welding technologies. In light of this, the LABSOLDA welding laboratory at the Federal University of Santa Catarina is making efforts to enhance the flexibility and robustness of the powder-fed plasma transferred arc (PTA-P) process so that it can be used in any welding position and with different powders. The use of consumables in p...

  4. ASPECTS REGARDING WOOD WELDING IN THE CONTEXT OF APPLICABILITY IN THE LEAST DEVELOPED COUNTRIES

    Directory of Open Access Journals (Sweden)

    Ramona-Elena DUMITRAȘCU

    2015-12-01

    Full Text Available Furniture, as traditional sector in Romania, is one of the few areas that bring profit. It is a field that contributes to the economical competitiveness through the variety of products for import and export. In this context, joining wood is essential for the production of wood products. Therefore, knowing the environmentally-friendly methods for wood joints could lead to performance and progress. Welding technology of wood as an alternative method to bonding wood elements or wooden structures has not been addressed in Romania until now. The paper presents a review performed with the aim of contribute to the knowledge of this innovative technology, to show the problems and the possibilities, of least developed countries, to contribute at this area of reasearch. The general aim is to present the main methods and to analyze their advantages and disadvantages in the context of development in the least developed countries. The results showed that both methods, at low and hight temperature, has benefits but there are and some economic and knowledge barriers for extended the technology.The overall conclusion of this research is to find efficient solutions for wood welding in order to obtain new better and cleaner wood products

  5. Welding. Performance Objectives. Basic Course.

    Science.gov (United States)

    Vincent, Kenneth

    Several intermediate performance objectives and corresponding criterion measures are listed for each of eight terminal objectives for a basic welding course. The materials were developed for a 36-week (2 hours daily) course developed to teach the fundamentals of welding shop work, to become familiar with the operation of the welding shop…

  6. New measurement technique of ductility curve for ductility-dip cracking susceptibility in Alloy 690 welds

    Energy Technology Data Exchange (ETDEWEB)

    Kadoi, Kota, E-mail: kadoi@hiroshima-u.ac.jp [Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8527 (Japan); Uegaki, Takanori; Shinozaki, Kenji; Yamamoto, Motomichi [Graduate School of Engineering, Hiroshima University, 1-4-1 Kagamiyama, Higashi-Hiroshima, Hiroshima 739-8527 (Japan)

    2016-08-30

    The coupling of a hot tensile test with a novel in situ observation technique using a high-speed camera was investigated as a high-accuracy quantitative evaluation method for ductility-dip cracking (DDC) susceptibility. Several types of Alloy 690 filler wire were tested in this study owing to its susceptibility to DDC. The developed test method was used to directly measure the critical strain for DDC and high temperature ductility curves with a gauge length of 0.5 mm. Minimum critical strains of 1.3%, 4.0%, and 3.9% were obtained for ERNiCrFe-7, ERNiCrFe-13, and ERNiCrFe-15, respectively. The DDC susceptibilities of ERNiCrFe-13 and ERNiCrFe-15 were nearly the same and quite low compared with that of ERNiCrFe-7. This was likely caused by the tortuosity of the grain boundaries arising from the niobium content of around 2.5% in the former samples. Besides, ERNiCrFe-13 and ERNiCrFe-15 indicated higher minimum critical strains even though these specimens include higher content of sulfur and phosphorus than ERNiCrFe-7. Thus, containing niobium must be more effective to improve the susceptibility compared to sulfur and phosphorous in the alloy system.

  7. Developments in luminescence measurement techniques

    DEFF Research Database (Denmark)

    Thomsen, Kristina Jørkov; Bøtter-Jensen, L.; Denby, Phil M.

    2006-01-01

    intended for use with the Riso TL/OSL reader. We have investigated the potential of new more powerful blue (455 nm) and green (530nm) LEDs, and of gated counting combined with pulsed stimulation light techniques using conventional LEDs. Measurement of time-resolved OSL has resulted in a method of real...

  8. Ultrasonic Stir Welding

    Science.gov (United States)

    Nabors, Sammy

    2015-01-01

    NASA Marshall Space Flight Center (MSFC) developed Ultrasonic Stir Welding (USW) to join large pieces of very high-strength metals such as titanium and Inconel. USW, a solid-state weld process, improves current thermal stir welding processes by adding high-power ultrasonic (HPU) energy at 20 kHz frequency. The addition of ultrasonic energy significantly reduces axial, frictional, and shear forces; increases travel rates; and reduces wear on the stir rod, which results in extended stir rod life. The USW process decouples the heating, stirring, and forging elements found in the friction stir welding process allowing for independent control of each process element and, ultimately, greater process control and repeatability. Because of the independent control of USW process elements, closed-loop temperature control can be integrated into the system so that a constant weld nugget temperature can be maintained during welding.

  9. Ultrasonic Evaluation of Weld Strength for Aluminum Ultrasonic Spot Welds

    Science.gov (United States)

    Ghaffari, Bita; Hetrick, Elizabeth T.; Mozurkewich, George; Reatherford, Larry V.

    2005-04-01

    The goal of this work is to determine the feasibility of using an ultrasonic, non-destructive technique for post-process evaluation of aluminum ultrasonic spot welds. A focused immersion transducer was utilized to obtain a C-scan of the weld interface, from which a weighted ultrasonic contact area was estimated. Weldments were subsequently tested destructively to determine the weld strength. The square root of the weld contact area displayed a relatively good correlation with weld strength, r2=0.85.

  10. Application of infrared imaging for quality inspection in resistance spot welds

    Science.gov (United States)

    Woo, Wanchuck; Chin, Charles W.; Feng, Zhili; Wang, Hsin; Zhang, Wei; Xu, Hanbing; Sklad, Philip S.

    2009-05-01

    Infrared thermal imaging method was applied for the development of a non-destructive inspection technique to determine the quality of resistance spot welds. The current work is an initial feasibility study based on post-mortem inspection. First, resistance spot welds were fabricated on dual phase steel sheets (DP 590 steel) with carefullycontrolled welding parameters. It created welds with desirable and undesirable qualities in terms of nugget size, indentation depth, and voids and cracks. Second, five different heating and cooling methods were evaluated. The heating or cooling source was applied on one side of the weld stack while the surface temperature change on the other side of the weld was recorded using an infrared camera. Correlation between the weld quality and the "thermal signature" of each weld was established. Finally, a simplified thermal finite element analysis was developed to simulate the heat flow during inspection. The thermal model provided insight into the effect of the nugget size and indentation depth on the peak temperature and heating rate. The results reported in this work indicate that the IR thermography technique is feasible for weld quality inspection due to the distinguish temperature profiles for different welds and the repeatability and consistency in measurement.

  11. Experimental Evaluation and Characterization of Electron Beam Welding of 2219 AL-Alloy

    Directory of Open Access Journals (Sweden)

    Mohamed Sobih

    2016-01-01

    Full Text Available Aiming to reduce the weight of components, thus allowing a profit in terms of energy saving, automotive industry as well as aircraft industry extensively uses aluminum alloys. The most widely used joining technology in aircraft industry is riveting, while welding seems to be used in the car industry in the case of aluminum alloys. However, welding technology is characterized by many defects, such as gas porosity; oxide inclusions; solidification cracking (hot tearing; and reduced strength in both the weld and the heat affected zones which could limit its development. Many techniques are used for aluminum alloys welding, among them is electron beam welding (EBW, which has unique advantages over other traditional fusion welding methods due to high-energy density, deep penetration, large depth-to-width ratio, and small heat affected zone. The welding parameters that yield to optimal weld joint have been previously obtained. These optimal parameters were validated by welding a specimen using these parameters. To evaluate this optimal weld joint, complete, microstructural observations and characterization have been carried out using scanning electron microscopy, optical microscopy, and energy dispersive X-ray analysis. This evaluation leads to description and quantification of the solidification process within this weld joint.

  12. Effect of tool rotational speed and penetration depth on dissimilar aluminum alloys friction stir spot welds

    Directory of Open Access Journals (Sweden)

    Joaquín M. Piccini

    2017-03-01

    Full Text Available In the last years, the automotive industry is looking for the use of aluminum parts in replace of steel parts in order to reduce the vehicles weight. These parts have to be joined, for instance, by welding processes. The more common welding process in the automotive industry is the Resistance Spot Welding (RSW technique. However, RSW of aluminum alloys has many disadvantages. Regarding this situation, a variant of the Friction Stir Welding process called Friction Stir Spot Welding (FSSW has been developed, showing a strong impact in welding of aluminum alloys and dissimilar materials in thin sheets. Process parameters affect the characteristics of the welded joints. However, the information available on this topic is scarce, particularly for dissimilar joints and thin sheets. The aim of this work was to study the effect of the rotational speed and the tool penetration depth on the characteristics of dissimilar FSS welded joints. Defects free joints have been achieved with higher mechanical properties than the ones reported. The maximum fracture load was 5800 N. It was observed that the effective joint length of the welded spots increased with the tool penetration depth, meanwhile the fracture load increased and then decreased. Finally, welding at 1200 RPM produced welded joints with lower mechanical properties than the ones achieved at 680 and 903 RPM.

  13. Development of Simplified Ultrasonic CT System for Imaging of Weld Metal and It's Comparison with TOFD Method

    Science.gov (United States)

    Kim, Kyung-Cho; Fukuhara, Hiroaki; Yamawaki, Hisashi

    In this paper, as a new measurement method to estimate the structure change of weld metal, the simplified ultrasonic CT system, which uses the information of three directions, that is, 90°, +45° and -45° about inspection plane is developed. Use of simplified ultrasonic CT system has two merits: Firstly, the measurement time is very short comparing with general CT. Secondly, it can detect sensitively very infinitesimal defect in vertical or slant direction about inspection plane because the obtained image is not C scan image but CT image calculated from three directions. From these merits, this method can be considered as a very effective method for the evaluation of material condition. In order to compare the performance of simplified ultrasonic CT, the CT image obtained from several specimens with several simple defects was compared with the D scan image obtained by TOFD (Time of Flight Diffraction) method. We can see simple defects more clearly by new proposed method. Experimental results on several kinds of specimen, having welded joint by electron beam welding, welded joint by electron beam welding and fatigue crack showed that the obtained C scan or CT image has better resolution than the D scan image by TOFD method and shows similar image to actual shape.

  14. The Development and Microstructure Analysis of High Strength Steel Plate NVE36 for Large Heat Input Welding

    Science.gov (United States)

    Peng, Zhang; Liangfa, Xie; Ming, Wei; Jianli, Li

    In the shipbuilding industry, the welding efficiency of the ship plate not only has a great effect on the construction cost of the ship, but also affects the construction speed and determines the delivery cycle. The steel plate used for large heat input welding was developed sufficiently. In this paper, the composition of the steel with a small amount of Nb, Ti and large amount of Mn had been designed in micro-alloyed route. The content of C and the carbon equivalent were also designed to a low level. The technology of oxide metallurgy was used during the smelting process of the steel. The rolling technology of TMCP was controlled at a low rolling temperature and ultra-fast cooling technology was used, for the purpose of controlling the transformation of the microstructure. The microstructure of the steel plate was controlled to be the mixed microstructure of low carbon bainite and ferrite. Large amount of oxide particles dispersed in the microstructure of steel, which had a positive effects on the mechanical property and welding performance of the steel. The mechanical property of the steel plate was excellent and the value of longitudinal Akv at -60 °C is more than 200 J. The toughness of WM and HAZ were excellent after the steel plate was welded with a large heat input of 100-250 kJ/cm. The steel plate processed by mentioned above can meet the requirement of large heat input welding.

  15. WOOD WELDING

    OpenAIRE

    Marcos Theodoro Muller; Rafael Rodolfo de Melo; Diego Martins Stangerlin

    2010-01-01

    The term "wood welding" designates what can be defined as "welding of wood surfaces". This new process, that it provides the joint of wood pieces without the use of adhesives or any other additional material, provokes growing interest in the academic environment, although it is still in laboratorial state. Linear friction welding induced bymechanical vibration yields welded joints of flat wood surfaces. The phenomenon of the welding occurs in less time than 10 seconds, with the temperature in...

  16. Gas Shielding Technology for Welding and Brazing

    Science.gov (United States)

    Nunes, Arthur J.; Gradl, Paul R.

    2012-01-01

    Welding is a common method that allows two metallic materials to be joined together with high structural integrity. When joints need to be leak-tight, light-weight, or free of contaminant-trapping seams or surface asperities, welding tends to be specified. There are many welding techniques, each with its own advantages and disadvantages. Some of these techniques include Forge Welding, Gas Tungsten Arc Welding, Friction Stir Welding, and Laser Beam Welding to name a few. Whichever technique is used, the objective is a structural joint that meets the requirements of a particular component or assembly. A key practice in producing quality welds is the use of shielding gas. This article discusses various weld techniques, quality of the welds, and importance of shielding gas in each of those techniques. Metallic bonds, or joints, are produced when metals are put into intimate contact. In the solid-state "blacksmith welding" process, now called Forge Welding (FOW), the site to be joined is pounded into intimate contact. The surfaces to be joined usually need to be heated to make it easier to deform the metal. The surfaces are sprinkled with a flux to melt surface oxides and given a concave shape so that surface contamination can be squeezed out of the joint as the surfaces are pounded together; otherwise the surface contamination would be trapped in the joint and would weaken the weld. In solid-state welding processes surface oxides or other contamination are typically squeezed out of the joint in "flash."

  17. Welding technology for rails. Rail no setsugo gijutsu

    Energy Technology Data Exchange (ETDEWEB)

    Okumura, M.; Karimine, K. (Nippon Steel Corp., Tokyo (Japan)); Uchino, K.; Sugino, K. (Nippon Steel Corp., Kitakyushu, Fukuoka (Japan). Technical Research Inst. of Yawata Works); Ueyama, K. (JR Railway Technical Research Inst., Tokyo (Japan))

    1993-08-01

    The rail joining technology is indispensable for making long welded rails. Flush butt welding, gas welding, enclosed arc welding, and thermit welding are used properly as the welding methods. A method for improving the joint reliability by controlling the residual stress distribution of welded joint is investigated to prepare high carbon component weld metal similar to the rail. Problems with each of the welding methods and the newly developed technology to solve the problems are outlined. Composition of the coating is improved also, and a high C system welding rod is developed which has satisfactory weldability. High performance and high efficient new enclosed arc welding technology not available by now is developed which utilizes high carbon welding metal as a new EA welding work technology, and put to practical use. As a result of this study, useful guides are obtained for the establishment of satisfactory thermit welding technology. 17 refs., 16 figs., 1 tab.

  18. Gas tungsten arc welding of vanadium alloys with impurity control

    Science.gov (United States)

    Grossbeck, M. L.; King, J. F.; Nagasaka, T.; David, S. A.

    2002-12-01

    Gas tungsten arc welding in vanadium alloys is controlled by interstitial impurities. Techniques have been developed to weld V-4Cr-4Ti in a high-purity argon atmosphere resulting in a DBTT of -20 °C. The atmosphere was controlled by a Zr-Al getter which is activated at high temperature to obtain a clean surface then cooled and allowed to absorb hydrogen and oxygen impurities. Through the use of low-oxygen base metal and high-purity weld filler wire, a DBTT of -145 °C was obtained. Experiments using electron beam welding have shown that grain size also has an important effect on weld ductility. Introduction of nitrogen and yttrium has been used to study their effect on grain size. Using a combination of atmosphere control, alloy purity control, and grain size control, it is anticipated that V-Cr-Ti alloys will be weldable in field conditions.

  19. Development of Alloy and Superalloy Large Shafts by Friction Welding Process

    Science.gov (United States)

    Jeong, H. S.; Cho, J. R.; Choi, S. K.; Oh, J. S.; Kim, E. N.

    2010-06-01

    The aim of this study is to examine the process parameters of superalloy and alloy steel inertia welding using FE simulation and to evaluate the mechanical properties of a welded joint. FE simulation was carried out to optimize the inertia welding process parameters. Disk of rotor shaft and head of exhaust valve spindle are made by the hot closed die forging. Dissimilar inertia welding for large exhaust valve spindle manufacturing composed of the Nimonic 80 A valve head of 540 mm diameter and the SNCrW valve stem of 115 mm diameter, and for large rotor shaft manufacturing composed of the 310 mm diameter disk and the 140 mm diameter shaft were carried out with optimal process parameter conditions obtained simulation result. Inertia friction welded joint part was joined by inertia friction welder, MTI model 400. Mechanical and metallurgical properties of welded joints were evaluated by using microstructure, tensile, hardness and fatigue tests.

  20. Texture Development and Material Flow Behavior During Refill Friction Stir Spot Welding of AlMgSc

    Science.gov (United States)

    Shen, Junjun; Lage, Sara B. M.; Suhuddin, Uceu F. H.; Bolfarini, Claudemiro; dos Santos, Jorge F.

    2018-01-01

    The microstructural evolution during refill friction stir spot welding of an AlMgSc alloy was studied. The primary texture that developed in all regions, with the exception of the weld center, was determined to be 〈110〉 fibers and interpreted as a simple shear texture with the 〈110〉 direction aligned with the shear direction. The material flow is mainly driven by two components: the simple shear acting on the horizontal plane causing an inward-directed spiral flow and the extrusion acting on the vertical plane causing an upward-directed or downward-directed flow. Under such a complex material flow, the weld center, which is subjected to minimal local strain, is the least recrystallized. In addition to the geometric effects of strain and grain subdivision, thermally activated high-angle grain boundary migration, particularly continuous dynamic recrystallization, drives the formation of refined grains in the stirred zone.

  1. Texture Development and Material Flow Behavior During Refill Friction Stir Spot Welding of AlMgSc

    Science.gov (United States)

    Shen, Junjun; Lage, Sara B. M.; Suhuddin, Uceu F. H.; Bolfarini, Claudemiro; dos Santos, Jorge F.

    2017-10-01

    The microstructural evolution during refill friction stir spot welding of an AlMgSc alloy was studied. The primary texture that developed in all regions, with the exception of the weld center, was determined to be 〈110〉 fibers and interpreted as a simple shear texture with the 〈110〉 direction aligned with the shear direction. The material flow is mainly driven by two components: the simple shear acting on the horizontal plane causing an inward-directed spiral flow and the extrusion acting on the vertical plane causing an upward-directed or downward-directed flow. Under such a complex material flow, the weld center, which is subjected to minimal local strain, is the least recrystallized. In addition to the geometric effects of strain and grain subdivision, thermally activated high-angle grain boundary migration, particularly continuous dynamic recrystallization, drives the formation of refined grains in the stirred zone.

  2. Explosive Welding of Pipes

    Science.gov (United States)

    Drennov, Oleg; Drennov, Andrey; Burtseva, Olga

    2013-06-01

    For connection by welding it is suggested to use the explosive welding method. This method is rather new. Nevertheless, it has become commonly used among the technological developments. This method can be advantageous (saving material and physical resources) comparing to its statical analogs (electron-beam welding, argon-arc welding, plasma welding, gas welding, etc.), in particular, in hard-to-reach areas due to their geographic and climatic conditions. Explosive welding of cylindrical surfaces is performed by launching of welded layer along longitudinal axis of construction. During this procedure, it is required to provide reliable resistance against radial convergent strains. The traditional method is application of fillers of pipe cavity, which are dense cylindrical objects having special designs. However, when connecting pipes consecutively in pipelines by explosive welding, removal of the fillers becomes difficult and sometimes impossible. The suggestion is to use water as filler. The principle of non-compressibility of liquid under quasi-dynamic loading is used. In one-dimensional gasdynamic and elastic-plastic calculations we determined non-deformed mass of water (perturbations, which are moving in the axial direction with sound velocity, should not reach the layer end boundaries for 5-7 circulations of shock waves in the radial direction). Linear dimension of the water layer from the zone of pipe coupling along axis in each direction is >= 2R, where R is the internal radius of pipe.

  3. Midinfrared Temperature Measurement Technique Developed

    Science.gov (United States)

    Santosuosso, George R.

    2003-01-01

    Infrared thermography is the measuring of the temperature of an object by examining the spectral quantities of light emission. The microgravity combustion experiment Solid Inflammability Boundary at Low-Speeds (SIBAL) calls for full-field temperature measurements of a thin sheet of cellulosic fuel as a flame front moves across the fuel, and infrared thermography is the only technique that can accomplish this task. The thermography is accomplished by imaging the fuel with a midinfrared camera that is sensitive in the 3.0- to 5.0-microns wavelength region in conjunction with a 3.7 - to 4.1-microns bandpass filter to eliminate unwanted infrared radiation from components other than the fuel.

  4. Welding. Performance Objectives. Intermediate Course.

    Science.gov (United States)

    Vincent, Kenneth

    Several intermediate performance objectives and corresponding criterion measures are listed for each of nine terminal objectives for an intermediate welding course. The materials were developed for a 36-week (3 hours daily) course designed to prepare the student for employment in the field of welding. Electric welding and specialized (TIG & MIG)…

  5. Automatic welding of stainless steel tubing

    Science.gov (United States)

    Clautice, W. E.

    1978-01-01

    The use of automatic welding for making girth welds in stainless steel tubing was investigated as well as the reduction in fabrication costs resulting from the elimination of radiographic inspection. Test methodology, materials, and techniques are discussed, and data sheets for individual tests are included. Process variables studied include welding amperes, revolutions per minute, and shielding gas flow. Strip chart recordings, as a definitive method of insuring weld quality, are studied. Test results, determined by both radiographic and visual inspection, are presented and indicate that once optimum welding procedures for specific sizes of tubing are established, and the welding machine operations are certified, then the automatic tube welding process produces good quality welds repeatedly, with a high degree of reliability. Revised specifications for welding tubing using the automatic process and weld visual inspection requirements at the Kennedy Space Center are enumerated.

  6. Numerical simulation and experimental validation of arc welding of DMR-249A steel

    Directory of Open Access Journals (Sweden)

    Rishi Pamnani

    2016-08-01

    Full Text Available The thermo-mechanical attributes of DMR-249A steel weld joints manufactured by shielded metal arc welding (SMAW and activated gas tungsten arc welding (A-GTAW processes were studied using Finite Element Model (FEM simulation. The thermal gradients and residual stresses were analyzed with SYSWELD software using double ellipsoidal heat source distribution model. The numerically estimated temperature distribution was validated with online temperature measurements using thermocouples. The predicted residual stresses profile across the weld joints was compared with the values experimentally measured using non-destructive techniques. The measured and predicted thermal cycles and residual stress profile was observed to be comparable. The residual stress developed in double sided A-GTAW joint were marginally higher in comparison to five pass SMAW joint due to phase transformation associated with high heat input per weld pass for A-GTAW process. The present investigations suggest the applicability of numerical modeling as an effective approach for predicting the thermo-mechanical properties influenced by welding techniques for DMR-249A steel weld joints. The tensile, impact and micro-hardness tests were carried to compare the welds. Considering benefits of high productivity and savings of labor and cost associated with A-GTAW compared to SMAW process, the minor variation in residual stress build up of A-GTAW joint can be neglected to develop A-GTAW as qualified alternative welding technique for DMR-249A steel.

  7. Fine welding with lasers.

    Science.gov (United States)

    MacLellan, D

    2008-01-01

    The need for micro joining metallic alloys for surgical instruments, implants and advanced medical devices is driving a rapid increase in the implementation of laser welding technology in research, development and volume production. This article discusses the advantages of this welding method and the types of lasers used in the process.

  8. Analytical techniques for biopharmaceutical development

    National Research Council Canada - National Science Library

    Wehr, Tim; Rodríguez-Díaz, Roberto; Tuck, Stephen (Stephen F.)

    2005-01-01

    ... for biopharmaceutical development / Tim Wehr, Roberto RodriguezDiaz, Stephen Tuck, editors. p. ; cm. Includes bibliographical references and index. ISBN 0-8247-2667-7 (alk. paper) 1. Protein drugs--Analysis--Laboratory manuals. [DNLM: 1. Pharmaceutical Preparations--analysis--Laboratory Manuals. 2. Biopharmaceutics--methods--Laboratory Ma...

  9. Development of Recuperator Manufacturing Techniques. Phase 2

    Science.gov (United States)

    1983-06-01

    The extensive tack welding necessary to assure joint positioning during furnace heat up. the cost of filler metal preforms and the difficulties in... crowns shall be smooth and blend into the adjacent base metal #without undercutting. There shall be no cracks, crack-like indications or blow holes...Strtfniri_ ("T fnh497 II. CONTROLLING OFFIdE NAME AND ADDRESS 12. REPORT DATE US Army Tank Automotive Command C7 ’’V. /-9.3 Metals /Welding Subfunction 13

  10. Alternative welding reconditioning solutions without post welding heat treatment of pressure vessel

    Science.gov (United States)

    Cicic, D. T.; Rontescu, C.; Bogatu, A. M.; Dijmărescu, M. C.

    2017-08-01

    In pressure vessels, working on high temperature and high pressure may appear some defects, cracks for example, which may lead to failure in operation. When these nonconformities are identified, after certain examination, testing and result interpretation, the decision taken is to repair or to replace the deteriorate component. In the current legislation it’s stipulated that any repair, alteration or modification to an item of pressurised equipment that was originally post-weld heat treated after welding (PWHT) should be post-weld heat treated again after repair, requirement that cannot always be respected. For that reason, worldwide, there were developed various welding repair techniques without PWHT, among we find the Half Bead Technique (HBT) and Controlled Deposition Technique (CDT). The paper presents the experimental results obtained by applying the welding reconditioning techniques HBT and CDT in order to restore as quickly as possible the pressure vessels made of 13CrMo4-5. The effects of these techniques upon the heat affected zone are analysed, the graphics of the hardness variation are drawn and the resulted structures are compared in the two cases.

  11. Recent developments in building diagnosis techniques

    CERN Document Server

    2016-01-01

    This book presents a collection of recent research on building diagnosis techniques related to construction pathology, hygrothermal behavior and durability, and diagnostic techniques. It highlights recent advances and new developments in the field of building physics, building anomalies in materials and components, new techniques for improved energy efficiency analysis, and diagnosis techniques such as infrared thermography. This book will be of interest to a wide readership of professionals, scientists, students, practitioners, and lecturers.

  12. Laser welding study for further development in essential power plant part repairs

    Directory of Open Access Journals (Sweden)

    Isarawit Chaopanich

    2015-06-01

    Full Text Available The objective of this research work was to study the effects of laser welding when compared with shield metal arc welding (SMAW process on the heat input, welded deposit rate, residual stress, distortion, microstructure and micro hardness. The martensitic stainless steel grade 431 specimens were overlay welded with the stainless steel filler metals. From the results, the heat input of 0.26 kJ/mm in laser welding calculated was significantly lower than that of 1.66 kJ/mm in SMAW, and contributed to low level residual stress, minimal distortion, very small penetration depth and heat affected zone (HAZ of less than 100 µm. The micro hardness results indicated that the maximum value from laser welding in the HAZ was 370.2 HV lower than the value from SMAW of 525.5 HV. The welded deposit rate for laser welding was with 26.5 mm3 /min remarkably lower than the rate for SMAW of 1,800 mm3 /min.

  13. Potential Applications of Friction Stir Welding to the Hydrogen Economy. Hydrogen Regional Infrastructure Program In Pennsylvania, Materials Task

    Energy Technology Data Exchange (ETDEWEB)

    Brendlinger, Jennifer [Concurrent Technologies Corporation, Johnstown, PA (United States)

    2009-07-17

    Friction Stir Welding (FSW) is a solid-state welding technique developed by The Welding Institute (TWI) of Cambridge, UK in the early 1990’s. The process uses a non-consumable rotating tool to develop frictional heat and plastically deform workpieces to be joined, resulting in a solid-state weld on the trailing side of the advancing tool. Since the materials to be joined are not melted, FSW results in a finer grain structure and therefore enhanced properties, relative to fusion welds. And unlike fusion welding, a relatively small number of key process parameters exist for FSW: tool rotational speed, linear weld velocity and force perpendicular to the joining surface. FSW is more energy efficient than fusion welding and can be accomplished in one or two passes, versus many more passes required of fusion welding thicker workpieces. Reduced post-weld workpiece distortion is another factor that helps to reduce the cost of FSW relative to fusion welding. Two primary areas have been identified for potential impact on the hydrogen economy: FSW of metallic pipes for hydrogen transmission and FSW of aluminum pressure vessels for hydrogen storage. Both areas have been under active development and are explored in this paper.

  14. Numerical simulation of the laser welding process for the prediction of temperature distribution on welded aluminium aircraft components

    Science.gov (United States)

    Tsirkas, S. A.

    2018-03-01

    The present investigation is focused to the modelling of the temperature field in aluminium aircraft components welded by a CO2 laser. A three-dimensional finite element model has been developed to simulate the laser welding process and predict the temperature distribution in T-joint laser welded plates with fillet material. The simulation of the laser beam welding process was performed using a nonlinear heat transfer analysis, based on a keyhole formation model analysis. The model employs the technique of element ;birth and death; in order to simulate the weld fillet. Various phenomena associated with welding like temperature dependent material properties and heat losses through convection and radiation were accounted for in the model. The materials considered were 6056-T78 and 6013-T4 aluminium alloys, commonly used for aircraft components. The temperature distribution during laser welding process has been calculated numerically and validated by experimental measurements on different locations of the welded structure. The numerical results are in good agreement with the experimental measurements.

  15. Experimental assessment of the influence of welding process parameters on Lamb wave transmission across ultrasonically welded thermoplastic composite joints

    Science.gov (United States)

    Ochôa, Pedro; Fernandez Villegas, Irene; Groves, Roger M.; Benedictus, Rinze

    2018-01-01

    One of the advantages of thermoplastic composites relative to their thermoset counterparts is the possibility of assembling components through welding. Ultrasonic welding in particular is very promising for industrialization. However, uncertainty in the fatigue and fracture behaviour of composites is still an obstacle to the full utilisation of these materials. Health monitoring is then of vital importance, and Lamb wave techniques have been widely recognised as some of the most promising approaches for that end. This paper presents the first experimental study about the influence of welding travel on the transmission of Lamb waves across ultrasonically welded thermoplastic composite joints in single-lap configuration. The main aim of this research is to start to understand how guided waves interact with the internal structure of ultrasonic welds, so that benign, manufacturing-related structural features can be distinguished from damaging ones in signal interpretation. The power transmission coefficient and the correlation coefficient proved to be suitable for analysing the wave propagation phenomena, allowing quantitative identification of small variations of weld-line thickness and intermolecular diffusion at the weld interface. The conclusions are used to develop a tentative damage detection criterion which can later on assist the design of a Lamb wave based structural health monitoring system for thermoplastic composite structures. The Lamb wave test results are backed up by phased-array inspections, which also provide some extra insight on the internal structure of ultrasonic welds.

  16. Automatic welding systems for large ship hulls

    Science.gov (United States)

    Arregi, B.; Granados, S.; Hascoet, JY.; Hamilton, K.; Alonso, M.; Ares, E.

    2012-04-01

    Welding processes represents about 40% of the total production time in shipbuilding. Although most of the indoor welding work is automated, outdoor operations still require the involvement of numerous operators. To automate hull welding operations is a priority in large shipyards. The objective of the present work is to develop a comprehensive welding system capable of working with several welding layers in an automated way. There are several difficulties for the seam tracking automation of the welding process. The proposed solution is the development of a welding machine capable of moving autonomously along the welding seam, controlling both the position of the torch and the welding parameters to adjust the thickness of the weld bead to the actual gap between the hull plates.

  17. TECHNOLOGICAL ISSUES IN MECHANISED FEED WIG/TIG WELDING SURFACING OF WELDING

    Directory of Open Access Journals (Sweden)

    BURCA Mircea

    2016-09-01

    manual welding tests in the light of using the process for welding surfacing being known that in such applications mechanised operations are recommended whenever possible given the latter strengths i.e. increased productivity and quality deposits. The research also aims at achieving a comparative a study between wire mechanised feed based WIG manual welding and the manual rod entry based manual welding in terms of geometry deposits, deposits aesthetics, operating technique, productivity, etc . In this regard deposits were made by means of two welding procedures, and subsequently welding surfacing was made with the optimum values of the welding parameters in this case.

  18. Development of ceramic support the base of cordierite for one-side welding; Desenvolvimento de suporte ceramico a base de cordierita para soldagem unilateral

    Energy Technology Data Exchange (ETDEWEB)

    Almeida, L.L.P. de; Vieira, C.M.F.; Paranhos, R.P.R.; Tatagiba, L.C.S. [Universidade Estadual do Norte Fluminense Darcy Ribeiro (LAMAV/UENF), Campos dos Goytacazes, RJ (Brazil). Lab. de Materiais Avancados

    2009-07-01

    This work has as objective develops ceramic backing for the execution of one side welds in steel. The backing consists the mixture of refractory mineral (Cordierite), adhesive (sodium silicate) and water. Test coupons produced by uniaxial pressing and burned to 1100 deg C they were submitted to physical and mechanical tests for determination the water absorption and flexion strength, respectively. The microstructure of ceramics produced was evaluated by diffraction of X-Ray, scanning electron microscopy and optical microscopy. After the production of the ceramic backing, welding tests were accomplished by the process MIG-MAG to evaluate the format of the weld bead. Based on the results obtained, during and after the welding accomplished with the employment of the ceramic backing, has shown that it is technically feasible for one-side welding. (author)

  19. Laser Welding in Space

    Science.gov (United States)

    Workman, Gary L.; Kaukler, William F.

    1989-01-01

    Solidification type welding process experiments in conditions of microgravity were performed. The role of convection in such phenomena was examined and convective effects in the small volumes obtained in the laser weld zone were observed. Heat transfer within the weld was affected by acceleration level as indicated by the resulting microstructure changes in low gravity. All experiments were performed such that both high and low gravity welds occurred along the same weld beam, allowing the effects of gravity alone to be examined. Results indicate that laser welding in a space environment is feasible and can be safely performed IVA or EVA. Development of the hardware to perform the experiment in a Hitchhiker-g platform is recomended as the next step. This experiment provides NASA with a capable technology for welding needs in space. The resources required to perform this experiment aboard a Shuttle Hitchhiker-pallet are assessed. Over the four year period 1991 to 1994, it is recommended that the task will require 13.6 manyears and $914,900. In addition to demonstrating the technology and ferreting out the problems encountered, it is suggested that NASA will also have a useful laser materials processing facility for working with both the scientific and the engineering aspects of materials processing in space. Several concepts are also included for long-term optimization of available solar power through solar pumping solid state lasers directly for welding power.

  20. Simulation of the welding of irradiated materials

    Energy Technology Data Exchange (ETDEWEB)

    Lin, Hua Tay

    1989-07-01

    Helium was uniformly implanted using the ''tritium trick'' technique to levels of 0.18, 2.5, 27, 105 and 256 atomic part per million (appm) for type 316 stainless steel, and 0.3 and 1 appm for Sandvik HT-9 (12 Cr-1MoVW). Both full penetration as well as partial penetration welds were then produced on control and helium-containing materials using the autogenous gas tungsten arc (GTA) welding process under full constraint conditions. For full penetration welds, both materials were successfully welded when they contained less than 0.3 appm helium. However, welds of both materials, when containing greater than 1 appm helium, were found to develop cracks during cooling of the weld. Transmission and scanning electron microscopy indicated that the HAZ cracking was caused by the growth and coalescence of grain boundary (GB) helium bubbles. This cracking occurred as a result of the combination of high temperatures and high shrinkage tensile stresses. The cracking in the fusion zone was found to result from the precipitation of helium along dendrite interfaces. A model based on the kinetics of diffusive cavity growth is presented to explain the observed results. The model proposes a helium bubble growth mechanism which leads to final intergranular rupture in the heat-affected zone. Results of the present study demonstrate that the use of conventional fusion welding techniques to repair materials degraded by exposure to irradiation environments may be difficult if the irradiation results in the generation of helium equal to or greater than 1 appm.

  1. A review on the effect of welding on the corrosion of magnesium alloys

    Science.gov (United States)

    Mohamed, N. S.; Alias, J.

    2017-10-01

    Welding is an important joining technique for lightweight alloys with their increasing applications in aerospace, aircraft, automotive, electronics and other industries. The applications of lightweight alloys particularly magnesium alloys increased rapidly due to their beneficial properties such as low density, high strength-to-mass ratio, good dimensional stability, electromagnetic shielding and good recyclability. The effect of welding on the corrosion of magnesium alloys are reviewed in this paper, which closely related to the developed microstructure by the welding process. The paper focuses particularly on friction stir and laser welding. The basic principles of friction stir and laser welding are discussed, to present the likelihood of defects which significantly affect the corrosion of magnesium alloy. The finding in corrosion demonstrated the morphology of corrosion occurrence on each welded region, and observation on the potential and current values are also included.

  2. Residual stress in a laser welded EUROFER blanket module assembly using non-destructive neutron diffraction techniques

    CERN Document Server

    Hughes, D J; Heeley, E L

    2014-01-01

    Whilst the structural integrity and lifetime considerations in welded joints for blanket modules can be predicted using finite element software, it is essential to prove the validity of these simulations. This paper provides detailed analysis for the first time, of the residual stress state in a laser-welded sample with integral cooling channels. State-of-the-art non-destructive neutron diffraction was employed to determine the triaxial stress state and to understand microstructural changes around the heat affected zone. Synchrotron X-ray diffraction was used to probe the variation of strain-free lattice reference parameter around the weld zone allowing correction of the neutron measurements. This paper details an important experimental route to validation of predicted stresses in complex safety-critical reactor components for future applications.

  3. Optimization of hybrid laser - TIG welding of 316LN steel using response surface methodology (RSM)

    Science.gov (United States)

    Ragavendran, M.; Chandrasekhar, N.; Ravikumar, R.; Saxena, Rajesh; Vasudevan, M.; Bhaduri, A. K.

    2017-07-01

    In the present study, the hybrid laser - TIG welding parameters for welding of 316LN austenitic stainless steel have been investigated by combining a pulsed laser beam with a TIG welding heat source at the weld pool. Laser power, pulse frequency, pulse duration, TIG current were presumed as the welding process parameters whereas weld bead width, weld cross-sectional area and depth of penetration (DOP) were considered as the process responses. Central composite design was used to complete the design matrix and welding experiments were conducted based on the design matrix. Weld bead measurements were then carried out to generate the dataset. Multiple regression models correlating the process parameters with the responses have been developed. The accuracy of the models were found to be good. Then, the desirability approach optimization technique was employed for determining the optimum process parameters to obtain the desired weld bead profile. Validation experiments were then carried out from the determined optimum process parameters. There was good agreement between the predicted and measured values.

  4. Development of a robotic manipulator for orbital welding; Desenvolvimento de um manipulador robotico para a sondagem orbital

    Energy Technology Data Exchange (ETDEWEB)

    Carvalho, Renon Steinbach; Dutra, Jair Carlos [Universidade Federal de Santa Catarina (UFSC), Florianopolis, SC (Brazil). Lab. de Soldagem; Bonacorso, Nelso Gauze [Centro Federal de Educacao Tecnologica de Santa Catarina (CEFET/SC), Florianopolis, SC (Brazil). Lab. da Automacao Hidraulica e Pneumatica (LAHP)

    2008-07-01

    On the national oil scenario, the pipelines have a high cost, specially on the long time spent on its constructions. Thus, this transaction optimizations become highly attractive. A form of improvement this task is to automate the process of welding. In this context it is interesting the use of a robot manipulator for the orbital welding. In the international market, there are dedicates solutions that meet the restrictions associated mainly with the ease of handling and dimensions. However,since these manipulators use foreign technology this makes the acquisition and maintenance costs high. The project aims to create subsides for greater efficiency in the task of union of pipelines through the development of a robotic manipulator. However it is clear that only the design of such a handler does not guarantee the quality of the root pass. Therefore, it is also being studied the use of the process MIG (Metal Inert Gas), through parametrization of CCC (Short-circuit controlled) in order to have a robust process of welding. The CCC monitors the process of welding and acts when there is detection od short circuit. It is obtained then higher pass from scratch controllability and drastically reduces the amount of spay. (author)

  5. Real time computer controlled weld skate

    Science.gov (United States)

    Wall, W. A., Jr.

    1977-01-01

    A real time, adaptive control, automatic welding system was developed. This system utilizes the general case geometrical relationships between a weldment and a weld skate to precisely maintain constant weld speed and torch angle along a contoured workplace. The system is compatible with the gas tungsten arc weld process or can be adapted to other weld processes. Heli-arc cutting and machine tool routing operations are possible applications.

  6. Welding Technician

    Science.gov (United States)

    Smith, Ken

    2009-01-01

    About 95% of all manufactured goods in this country are welded or joined in some way. These welded products range in nature from bicycle handlebars and skyscrapers to bridges and race cars. The author discusses what students need to know about careers for welding technicians--wages, responsibilities, skills needed, career advancement…

  7. Mathematical Model Of Variable-Polarity Plasma Arc Welding

    Science.gov (United States)

    Hung, R. J.

    1996-01-01

    Mathematical model of variable-polarity plasma arc (VPPA) welding process developed for use in predicting characteristics of welds and thus serves as guide for selection of process parameters. Parameters include welding electric currents in, and durations of, straight and reverse polarities; rates of flow of plasma and shielding gases; and sizes and relative positions of welding electrode, welding orifice, and workpiece.

  8. Laser welding and post weld treatment of modified 9Cr-1MoVNb steel.

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Z. (Nuclear Engineering Division)

    2012-04-03

    Laser welding and post weld laser treatment of modified 9Cr-1MoVNb steels (Grade P91) were performed in this preliminary study to investigate the feasibility of using laser welding process as a potential alternative to arc welding methods for solving the Type IV cracking problem in P91 steel welds. The mechanical and metallurgical testing of the pulsed Nd:YAG laser-welded samples shows the following conclusions: (1) both bead-on-plate and circumferential butt welds made by a pulsed Nd:YAG laser show good welds that are free of microcracks and porosity. The narrow heat affected zone has a homogeneous grain structure without conventional soft hardness zone where the Type IV cracking occurs in conventional arc welds. (2) The laser weld tests also show that the same laser welder has the potential to be used as a multi-function tool for weld surface remelting, glazing or post weld tempering to reduce the weld surface defects and to increase the cracking resistance and toughness of the welds. (3) The Vicker hardness of laser welds in the weld and heat affected zone was 420-500 HV with peak hardness in the HAZ compared to 240 HV of base metal. Post weld laser treatment was able to slightly reduce the peak hardness and smooth the hardness profile, but failed to bring the hardness down to below 300 HV due to insufficient time at temperature and too fast cooling rate after the time. Though optimal hardness of weld made by laser is to be determined for best weld strength, methods to achieve the post weld laser treatment temperature, time at the temperature and slow cooling rate need to be developed. (4) Mechanical testing of the laser weld and post weld laser treated samples need to be performed to evaluate the effects of laser post treatments such as surface remelting, glazing, re-hardening, or tempering on the strength of the welds.

  9. Artificial Intelligence Techniques: Applications for Courseware Development.

    Science.gov (United States)

    Dear, Brian L.

    1986-01-01

    Introduces some general concepts and techniques of artificial intelligence (natural language interfaces, expert systems, knowledge bases and knowledge representation, heuristics, user-interface metaphors, and object-based environments) and investigates ways these techniques might be applied to analysis, design, development, implementation, and…

  10. Development of a Novel Method for Determination of Residual Stresses in a Friction Stir Weld

    Science.gov (United States)

    Reynolds, Anthony P.

    2001-01-01

    Material constitutive properties, which describe the mechanical behavior of a material under loading, are vital to the design and implementation of engineering materials. For homogeneous materials, the standard process for determining these properties is the tensile test, which is used to measure the material stress-strain response. However, a majority of the applications for engineering materials involve the use of heterogeneous materials and structures (i.e. alloys, welded components) that exhibit heterogeneity on a global or local level. Regardless of the scale of heterogeneity, the overall response of the material or structure is dependent on the response of each of the constituents. Therefore, in order to produce materials and structures that perform in the best possible manner, the properties of the constituents that make up the heterogeneous material must be thoroughly examined. When materials exhibit heterogeneity on a local level, such as in alloys or particle/matrix composites, they are often treated as statistically homogenous and the resulting 'effective' properties may be determined through homogenization techniques. In the case of globally heterogeneous materials, such as weldments, the standard tensile test provides the global response but no information on what is Occurring locally within the different constituents. This information is necessary to improve the material processing as well as the end product.

  11. Electron Beam Welding of Thick Copper Material

    Energy Technology Data Exchange (ETDEWEB)

    Broemssen, Bernt von [IVF Industriforskning och utveckling AB, Stockholm (Sweden)

    2002-08-01

    The purpose of this study was to review the two variants of the Electron Beam Welding (EBW) processes developed (or used) by 1- SKB, Sweden with assistance from TWI, England and 2 - POSIVA, Finland with assistance from Outokumpu, Finland. The aim was also to explain the principle properties of the EBW method: how it works, the parameters controlling the welding result but also giving rise to benefits, and differences between the EBW variants. The main conclusions are that both SKB and POSIVA will within a few years succeed to qualify their respective EBW method for welding of copper canisters. The Reduced Pressure EBW that SKB use today seems to be very promising in order to avoid root defects. If POSIVA does not succeed to avoid root defects with the high vacuum method and the beam oscillation technique it should be possible for POSIVA to incorporate the Reduced Pressure technique albeit with significant changes to the EBW equipment. POSIVA has possibly an advantage over SKB with the beam oscillation technique used, which gives an extra degree of freedom to affect the weld quality. The beam oscillation could be of importance for closing of the keyhole. Before EBW of lids, the material certification showing the alloy content (specifying min and max impurity percentages) and the mechanical properties should be checked. The welded material needs also to be tested for mechanical properties. If possible the weld should have a toughness level equal to that of the unwelded parent material. Specifically some conclusions are reported regarding the SKB equipment. Suggestions for further development are also given in the conclusion chapter.

  12. Development of a Powder-feed Device and Procedures for the Application of an Experimental Alloy in Overhead PTA-P Welding

    Directory of Open Access Journals (Sweden)

    Jônathas Alexandre Alves

    2015-12-01

    Full Text Available Abstract: When they are damaged by cavitation, hydroelectric power plant turbine blades must be repaired using operations that could benefit from developments in welding technologies. In light of this, the LABSOLDA welding laboratory at the Federal University of Santa Catarina is making efforts to enhance the flexibility and robustness of the powder-fed plasma transferred arc (PTA-P process so that it can be used in any welding position and with different powders. The use of consumables in powder form in PTA-P welding allows experiments to be carried out to develop an alloy with special properties suitable for use in generator repairs. To this end, the RV-F PF powder feeder, which can operate with consumables with non-standard morphologies and particle sizes, was developed. The feeder was required to provide a regular flow of consumable material in out-of-position welding operations without the need for high gas flow rates and regardless of the morphology or particle size of the consumables. The RV-F PF is shown to operate efficiently with materials whose properties differ greatly from those of standard consumables. It is also suitable for overhead PTA-P welding and provides a constant supply of filler material efficiently with normal gas flow rates. The welding tests carried out involved deposition of a mixture of two alloys and were followed by cavitation testing of the resulting coating.

  13. Correlation of Stress Concentration Factors for T-Welded Connections – Finite Element Simulations and Fatigue Behavior

    Directory of Open Access Journals (Sweden)

    Gerardo Terán Méndez

    Full Text Available Abstract The stress concentration factors (SCFs in welded connections usually occur at zones with high stress levels. Stress concentrations reduce the fatigue behavior of welded connections in offshore structures and cracking can develop. By using the grinding technique, cracking can be eliminated. Stress concentration factors are defined as a ratio of maximum stress at the intersection to nominal stress on the brace. Defining the stress concentration factor is an important stage in the fatigue behavior of welded connections. Several approaches have evolved for designing structures with the classical S-N approach for estimating total life. This work correlates to the stress concentration factors of T-welded connections and the fatigue behavior. Stress concentration factors were computed with the finite element employing 3D T-welded connections with intact and grinding depth conditions. Then, T-welded connections were constructed with A36 plate steel and welded with E6013 electrodes to obtain the stress-life (S-N approach. The methodology from previous works was used to compute the SCF and fabricate the T-welded connections. The results indicated that the grinding process could restore the fatigue life of the T-welded connections for SCFs values in the range of 1.29. This value can be considered to be a low SCF value in T-welded connection. However, for higher SCF values, the fatigue life decreased, compromising and reducing the structural integrity of the T-welded connections.

  14. Modified protocol of the intraoral welding technique for immediate implant-supported rehabilitation of the edentulous maxilla.

    Science.gov (United States)

    Marchesi, Marcello; Ferrari, Carla; Superbi, Simone; Jimbo, Ryo; Galli, Silvia

    2015-02-01

    The aim of this study was to report the outcomes of a treatment option of immediate loading with intraoral welding on only 4 implants for the restoration of patients with maxillary edentulism. Seventeen consecutive patients were rehabilitated with 2 parallel and 2 tilted implants in the maxilla. Immediately after implant placement, angulated abutments were screwed on the implants to create better parallelism among the implants; thereafter, a titanium bar was intraorally welded to the welding pins to create a superstructure that rigidly splinted the implants. A fixed full-arch durable prosthesis was delivered on the same day of the surgery. The patients were followed for 26.5 months on average. During the follow-up time, 2 implants were lost giving an implant survival rate of 97%. Nonetheless, all the prostheses remained in function and the prosthetic success was 100%. The rehabilitation of the edentulous maxilla with an immediately loaded full-arch prosthesis, obtained through intraoral welding on only 4 implants, is a functionally and esthetically successful treatment.

  15. A Brief Introduction to the Theory of Friction Stir Welding

    Science.gov (United States)

    Nunes, Arthur C., Jr.

    2008-01-01

    Friction stir welding (FSW) is a solid state welding process invented in 1991 at The Welding Institute in the United Kingdom. A weld is made in the FSW process by translating a rotating pin along a weld seam so as to stir the sides of the seam together. FSW avoids deleterious effects inherent in melting and is already an important welding process for the aerospace industry, where welds of optimal quality are demanded. The structure of welds determines weld properties. The structure of friction stir welds is determined by the flow field in the weld metal in the vicinity of the weld tool. A simple kinematic model of the FSW flow field developed at Marshall Space Flight Center, which enables the basic features of FSW microstructure to be understood and related to weld process parameters and tool design, is explained.

  16. Weld overlay cladding with iron aluminides

    Energy Technology Data Exchange (ETDEWEB)

    Goodwin, G.M. [Oak Ridge National Lab., TN (United States)

    1997-12-01

    The author has established a range of compositions for these alloys within which hot cracking resistance is very good, and within which cold cracking can be avoided in many instances by careful control of welding conditions, particularly preheat and postweld heat treatment. For example, crack-free butt welds have been produced for the first time in 12-mm thick wrought Fe{sub 3}Al plate. Cold cracking, however, still remains an issue in many cases. The author has developed a commercial source for composite weld filler metals spanning a wide range of achievable aluminum levels, and are pursuing the application of these filler metals in a variety of industrial environments. Welding techniques have been developed for both the gas tungsten arc and gas metal arc processes, and preliminary work has been done to utilize the wire arc process for coating of boiler tubes. Clad specimens have been prepared for environmental testing in-house, and a number of components have been modified and placed in service in operating kraft recovery boilers. In collaboration with a commercial producer of spiral weld overlay tubing, the author is attempting to utilize the new filler metals for this novel application.

  17. Factors affecting weld root morphology in laser keyhole welding

    Science.gov (United States)

    Frostevarg, Jan

    2018-02-01

    Welding production efficiency is usually optimised if full penetration can be achieved in a single pass. Techniques such as electron and laser beam welding offer deep high speed keyhole welding, especially since multi-kilowatt lasers became available. However, there are limitations for these techniques when considering weld imperfections such as weld cap undercuts, interior porosity or humps at the root. The thickness of sheets during full penetration welding is practically limited by these root humps. The mechanisms behind root morphology formation are not yet satisfactory understood. In this paper root humping is studied by reviewing previous studies and findings and also by sample examination and process observation by high speed imaging. Different process regimes governing root quality are presented, categorized and explained. Even though this study mainly covers laser beam and laser arc hybrid welding, the presented findings can generally be applied full penetration welding in medium to thick sheets, especially the discussion of surface tension effects. As a final result of this analysis, a map of methods to optimise weld root topology is presented.

  18. Programmable Automated Welding System (PAWS): Control of welding through software and hardware

    Science.gov (United States)

    Kline, Martin D.; Doyle, Thomas E.

    1994-01-01

    The ATD phase of the PAWS program ended in November 1992 and the follow-on ManTech program was started in September 1993. The system will be industrially hardened during the first year of this program. Follow-on years will focus upon the transition into specific end-user sites. These implementations will also expand the system into other welding processes (e.g. FCAW, GTAW, PAW). In addition, the architecture is being developed for application to other non-welding robotic processes (e.g. inspection, surface finishing). Future development is anticipated to encompass hardening for extreme environments, expanded exception handling techniques, and application to a range of manipulators.

  19. [Dental welding titanium and its clinical usage].

    Science.gov (United States)

    Li, H; Xiao, M; Zhao, Y

    1998-09-01

    Due to its excellent biocompatibility, desirable chemical and mechanical properties, Titanium has been used for implant denture, RPD and FPD, where welding techniques were indispensable. This paper introduces 5 useful modern ways to weld Titanium and their clinical usage. They are: laser, plasma welding, TIG, infraned brazing and Hruska electrowelding.

  20. Portable electron beam weld chamber

    Science.gov (United States)

    Lewis, J. R.; Dimino, J. M.

    1972-01-01

    Development and characteristics of portable vacuum chamber for skate type electron beam welding are discussed. Construction and operational details of equipment are presented. Illustrations of equipment are provided.

  1. Survey of welding processes.

    Science.gov (United States)

    2003-07-01

    The current KYTC SPECIAL PROVISION NO. 4 WELDING STEEL BRIDGES prohibits the use of welding processes other than shielded metal arc welding (SMAW) and submerged arc welding (SAW). Nationally, bridge welding is codified under ANSI/AASHTO/AWS D1....

  2. Tensile Residual Stress Mitigation Using Low Temperature Phase Transformation Filler Wire in Welded Armor Plates

    Energy Technology Data Exchange (ETDEWEB)

    Feng, Zhili [ORNL; Bunn, Jeffrey R [ORNL; Tzelepis, Demetrios A [ORNL; Payzant, E Andrew [ORNL; Yu, Xinghua [ORNL

    2016-01-01

    Hydrogen induced cracking (HIC) has been a persistent issue in welding of high-strength steels. Mitigating residual stresses is one of the most efficient ways to control HIC. The current study develops a proactive in-process weld residual stress mitigation technique, which manipulates the thermal expansion and contraction sequence in the weldments during welding process. When the steel weld is cooled after welding, martensitic transformation will occur at a temperature below 400 C. Volume expansion in the weld due to the martensitic transformation will reduce tensile stresses in the weld and heat affected zone and in some cases produce compressive residual stresses in the weld. Based on this concept, a customized filler wire which undergoes a martensitic phase transformation during cooling was developed. The new filler wire shows significant improvement in terms of reducing the tendency of HIC in high strength steels. Bulk residual stress mapping using neutron diffraction revealed reduced tensile and compressive residual stresses in the welds made by the new filler wire.

  3. Metal Cutting Theory and Friction Stir Welding Tool Design

    Science.gov (United States)

    Payton, Lewis N.

    2003-01-01

    Friction Stir Welding (FSW) is a relatively new industrial process that was invented at The Weld Institute (TWI, United Kingdom) and patented in 1992 under research funded by in part by the National Aeronautics and Space Administration (NASA). Often quoted advantages of the process include good strength and ductility along with minimization of residual stress and distortion. Less well advertised are the beneficial effects of this solid state welding process in the field of occupational and environmental safety. It produces superior weld products in difficult to weld materials without producing any toxic fumes or solid waste that must be controlled as hazardous waste. In fact, it reduces noise pollution in the workspace as well. In the early days of FSW, most welding was performed on modified machine tools, in particular on milling machines with modified milling cutters. In spite of the obvious milling heritage of the process, the techniques and lessons learned from almost 250 years of successful metalworking with milling machines have not been applied in the field of modern Friction Stir Welding. The goal of the current research was to study currently successful FSW tools and parameterize the process in such a way that the design of new tools for new materials could be accelerated. Along the way, several successful new tooling designs were developed for current issues at the Marshall Space Flight Center with accompanying patent disclosures

  4. Numerical Modeling of Fluid Flow, Heat Transfer and Arc-Melt Interaction in Tungsten Inert Gas Welding

    Science.gov (United States)

    Li, Linmin; Li, Baokuan; Liu, Lichao; Motoyama, Yuichi

    2017-04-01

    The present work develops a multi-region dynamic coupling model for fluid flow, heat transfer and arc-melt interaction in tungsten inert gas (TIG) welding using the dynamic mesh technique. The arc-weld pool unified model is developed on basis of magnetohydrodynamic (MHD) equations and the interface is tracked using the dynamic mesh method. The numerical model for arc is firstly validated by comparing the calculated temperature profiles and essential results with the former experimental data. For weld pool convection solution, the drag, Marangoni, buoyancy and electromagnetic forces are separately validated, and then taken into account. Moreover, the model considering interface deformation is adopted in a stationary TIG welding process with SUS304 stainless steel and the effect of interface deformation is investigated. The depression of weld pool center and the lifting of pool periphery are both predicted. The results show that the weld pool shape calculated with considering the interface deformation is more accurate.

  5. EFFECT OF POST-WELD HEAT TREATMENT ON THE ...

    African Journals Online (AJOL)

    Effect of post- weld heat treatment on the microstructure and mechanical properties of arc welded medium carbon steel was investigated. Medium carbon steel samples were butt- welded by using the shielded metal arc welding technique and, thereafter, heat treated by annealing, normalising and quench hardening in ...

  6. Technical specifications on the welding in fuel reprocessing plants

    Energy Technology Data Exchange (ETDEWEB)

    Karino, Motonobu; Uryu, Mitsuru; Matsui, N.; Nakazawa, Fumio; Imanishi, Makoto; Koizumi; Kazuhiko; Sugawara, Junichi; Tanaka, Hideo

    1999-04-01

    The past specifications SGN of the welding in JNC was reexamined for the reprocessing plants in order to further promote the quality control. The specification first concerns the quality of raw materials, items of the quality tests, material management, and qualification standards of the welders. It extends over details of the welding techniques, welding design, welding testings, inspection and the judgment standards. (H. Baba)

  7. Development of Mathematic Model of Cold Welding at Drawing-up the Flange Joint of Pneumohydraulic Systems

    Science.gov (United States)

    Boyko, Y. S.

    2002-01-01

    Provision of high airtightness of joints of pipe- lines of pneumohydraulic systems (PHS) operating under high pressure, is an important task for designing and operation of launch vehicles. In the process of assembly and tests of PHS of launch vehicles, it was found that detachable flange joints do not lose their airtightness after removal of fastening elements, even in conditions of standard loads. The task of this work is in studying a phenomenon connected with initiation of the observed effect of adhesion and also stresses in the zone of contact at drawing- up the flange detachable joints with a plastic gasket. Investigations have shown that density of the joint is kept due to cold welding, as the created conditions are helpful for that process. As a result of the investigations performed, we have developed a mathematic model which is based on application of the theory of metal bonds; that theory explains the essence of the effect observed. Basic factors which provide optimum mode of cold welding, are effort which can cause microplastic deformation and form maximum contact, and also quality of processing the material of the surfaces joined. Strength of all- metal joint depends on factual area of contact. So, surface processing quality defines a configuration of microbulges which come into contact not simultaneously, and their stressed state is different, and it influences the character of dependence of the contact area on loading. Results of calculations by the mathematic model are expressed by dependencies of factual area of contact and a single diameter of the contact spot on the load applied which compresses the materials with various physical properties, and on the surface processing quality. The mathematic model allows to explain the common character of the cold welding process in detachable flange joints with the plastic gasket, to determine the nature and the character of acting forces, to define kinetics and the mechanism of formation of cold welding of

  8. Evaluation of Distortion in Welding Unions of 304 Stainless Steel with Elliptic Trajectory Using a Welding Robot

    Science.gov (United States)

    Carrasco-González, L. A.; Hurtado-Delgado, E.; Reyes-Valdés, F. A.

    The aim of this investigation is to evaluate the distortions generated in welding unions of stainless steel 304 by effect of the welding temperature and the microestructural changes. The joint design is a 100 × 100 mm steel plate of 3 mm thickness. The plate was joined to a tube of 50 mm diameter and 2 mm thickness, which has a defined angular cut; therefore, the trajectory followed by the seam has an elliptic form. Temperature data acquisition was developed by type K thermocouples, placed in pairs at 0°, 90°, 180° and 270° along the welding trajectory and connected to a data acquisition device yo obtain the measures to generate time-temperature plots. The welding process was executed by a KUKA ®; KR16 welding robot with an integrated GMAW (Gas metal arc welding) process where the input parameters of voltage, wire feed and travel speed are set to constant. The distortion of the work piece was measured using a laser scanning technique that generates a point cloud with the VXelements TM software for comparison between the pre and post-weld condition. Microstructural evaluation was performed on transversal sections of the seam, at the mentioned angles for correlation.

  9. Soldadura (Welding). Spanish Translations for Welding.

    Science.gov (United States)

    Hohhertz, Durwin

    Thirty transparency masters with Spanish subtitles for key words are provided for a welding/general mechanical repair course. The transparency masters are on such topics as oxyacetylene welding; oxyacetylene welding equipment; welding safety; different types of welds; braze welding; cutting torches; cutting with a torch; protective equipment; arc…

  10. Development of laser cutting/welding depth control using laser spectroscopy and open architecture control of a robotic system

    Energy Technology Data Exchange (ETDEWEB)

    McKee, G.R.; Meirans, L.; Schmitt, D.J.; Small, D.; Watterberg, P.A. [Sandia National Labs., Albuquerque, NM (United States); Siegel, S. [PaR Systems, Inc., Shoreview, MN (United States)

    1998-03-01

    This project was driven by the need to identify and provide unique, state-of-the-art solutions to the robotic path planning and precision motion execution problems that face automated processes such as welding and cutting using lasers. The initial LDRD proposal was for a full three years program with a schedule that would create a precision robotic platform capable of providing path planning and precision motion execution using sensor and graphical programming technologies as the first year milestone. Milestones for year two were centered in developing and deploying sensor technologies that support welding and cutting. And year three milestones included the integration of any developed sensors onto the robotic platform under software control to achieve autonomous control of laser welding and cutting processes. The work performed was directed at the goal of establishing a precision robotics platform with the capability to integrate graphical programming, CAD model based path planning, and motion execution under real-time sensor based control. This report covers the progress made toward that goal during the one year of funding.

  11. WELDING TORCH

    Science.gov (United States)

    Correy, T.B.

    1961-10-01

    A welding torch into which water and inert gas are piped separately for cooling and for providing a suitable gaseous atmosphere is described. A welding electrode is clamped in the torch by a removable collet sleeve and a removable collet head. Replacement of the sleeve and head with larger or smaller sleeve and head permits a larger or smaller welding electrode to be substituted on the torch. (AEC)

  12. TIG-dressing of High Strength Steel Butt Welded Connections. Part 1 : Weld Toe Geometry and Local Hardness

    NARCIS (Netherlands)

    Van Es, S.H.J.; Kolstein, M.H.; Pijpers, R.J.M.; Bijlaard, F.S.K.

    2014-01-01

    This paper presents the results of extensive measurements on weld toe geometry of as-welded and TIG-dressed butt welded connections in high strength steels S460, S690 and very high strength steels S890 and S1100. Descriptions of the measurement techniques and data analysis are presented. Four weld

  13. TIG-dressing of high strength steel butt welded connections - Part 1: weld toe geometry and local hardness

    NARCIS (Netherlands)

    Es, S.H.J. van; Kolstein, M.H.; Pijpers, R.J.M.; Bijlaard, F.S.K.

    2013-01-01

    This paper presents the results of extensive measurements on weld toe geometry of as-welded and TIG-dressed butt welded connections in high strength steels S460, S690 and very high strength steels S890 and S1100. Descriptions of the measurement techniques and data analysis are presented. Four weld

  14. Electron Beam Welding of a Depleted Uranium Alloy to Niobium Using a Calibrated Electron Beam Power Density Distribution

    Science.gov (United States)

    Elmer, J. W.; Teruya, A. T.; Terrill, P. E.

    2000-08-01

    Electron beam test welds were made joining flat plates of commercially pure niobium to a uranium-6wt%Nb (binary) alloy. The welding parameters and joint design were specifically developed to minimize mixing of the niobium with the U-6%Nb alloy. A Modified Faraday Cup (MFC) technique using computer-assisted tomography was employed to determine the precise power distribution of the electron beam so that the welding parameters could be directly transferred to other welding machines and/or to other facilities.

  15. Classification of weld defect based on information fusion technology for radiographic testing system

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Hongquan; Liang, Zeming, E-mail: heavenlzm@126.com; Gao, Jianmin; Dang, Changying [State Key Laboratory for Manufacturing System Engineering, Department of Mechanical Engineering, Xi’an Jiaotong University, Xi’an 710049 (China)

    2016-03-15

    Improving the efficiency and accuracy of weld defect classification is an important technical problem in developing the radiographic testing system. This paper proposes a novel weld defect classification method based on information fusion technology, Dempster–Shafer evidence theory. First, to characterize weld defects and improve the accuracy of their classification, 11 weld defect features were defined based on the sub-pixel level edges of radiographic images, four of which are presented for the first time in this paper. Second, we applied information fusion technology to combine different features for weld defect classification, including a mass function defined based on the weld defect feature information and the quartile-method-based calculation of standard weld defect class which is to solve a sample problem involving a limited number of training samples. A steam turbine weld defect classification case study is also presented herein to illustrate our technique. The results show that the proposed method can increase the correct classification rate with limited training samples and address the uncertainties associated with weld defect classification.

  16. Optimum Design and Development of High Strength and Toughness Welding Wire for Pipeline Steel

    Science.gov (United States)

    Chen, Cuixin; Xue, Haitao; Yin, Fuxing; Peng, Huifen; Zhi, Lei; Wang, Sixu

    Pipeline steel with higher strength(>800MPa) has been gradually used in recent years, so how to achieve good match of base metal and weld deposit is very important for its practical application. Based on the alloy system of 0.02-0.04%C, 2.0%Mn and 0.5%Si, four different kinds of welding wires were designed and produced. The effects of alloy elements on phase transformation and mechanical properties were analyzed. Experimental results show that the designed steels with the addition of 2-4% Ni+Cr+Mo and 800MPa) and good elongation (>15%). The microstructure of deposits metal is mainly composed of granular bainite and M-A constituents with the mean size of 0.2-07μm are dispersed on ferritic matrix. The deposited metals have good match of strength (>800MPa) and impact toughness (>130J) which well meet the requirement of pipeline welding.

  17. Closed circuit television welding alignment system

    Energy Technology Data Exchange (ETDEWEB)

    Darner, G.S.

    1976-09-01

    Closed circuit television (CCTV) weld targeting systems were developed to provide accurate and repeatable positioning of the electrode of an electronic arc welder with respect to the parts being joined. A sliding mirror electrode holder was developed for use with closed circuit television equipment on existing weld fixturing. A complete motorized CCTV weld alignment system was developed to provide weld targeting for even the most critical positioning requirements.

  18. Primary Water Stress Corrosion Cracks in Nickel Alloy Dissimilar Metal Welds: Detection and Sizing Using Established and Emerging Nondestructive Examination Techniques

    Energy Technology Data Exchange (ETDEWEB)

    Braatz, Brett G.; Cumblidge, Stephen E.; Doctor, Steven R.; Prokofiev, Iouri

    2012-12-31

    The U.S. Nuclear Regulatory Commission has established the Program to Assess the Reliability of Emerging Nondestructive Techniques (PARENT) as a follow-on to the international cooperative Program for the Inspection of Nickel Alloy Components (PINC). The goal of PINC was to evaluate the capabilities of various nondestructive evaluation (NDE) techniques to detect and characterize surface-breaking primary water stress corrosion cracks in dissimilar-metal welds (DMW) in bottom-mounted instrumentation (BMI) penetrations and small-bore (≈400-mm diameter) piping components. A series of international blind round-robin tests were conducted by commercial and university inspection teams. Results from these tests showed that a combination of conventional and phased-array ultrasound techniques provided the highest performance for flaw detection and depth sizing in dissimilar metal piping welds. The effective detection of flaws in BMIs by eddy current and ultrasound shows that it may be possible to reliably inspect these components in the field. The goal of PARENT is to continue the work begun in PINC and apply the lessons learned to a series of open and blind international round-robin tests that will be conducted on a new set of piping components including large-bore (≈900-mm diameter) DMWs, small-bore DMWs, and BMIs. Open round-robin testing will engage universities and industry worldwide to investigate the reliability of emerging NDE techniques to detect and accurately size flaws having a wide range of lengths, depths, orientations, and locations. Blind round-robin testing will invite testing organizations worldwide, whose inspectors and procedures are certified by the standards for the nuclear industry in their respective countries, to investigate the ability of established NDE techniques to detect and size flaws whose characteristics range from easy to very difficult to detect and size. This paper presents highlights of PINC and reports on the plans and progress for

  19. Local zone wise elastic and plastic properties of electron beam welded Ti-6Al-4V alloy using digital image correlation technique: A comparative study between uniform stress and virtual fields method

    Science.gov (United States)

    Saranath, K. M.; Ramji, M.

    2015-05-01

    Joining of materials using welding results in the formation of material zones with varying microstructure across the weld. Extraction of the mechanical properties of those individual heterogeneous zones are important in designing components and structures comprised of welds. In this study, the zone wise local extraction of the elastic and plastic properties of an electron beam welded Ti-6Al-4V titanium alloy has been carried out using both the uniform stress method (USM) and the virtual fields method (VFM) involving digital image correlation (DIC) technique. The surface strain field obtained using DIC technique from a transverse weld specimen tensile testing is used for extracting the zone wise strain evolution. Initially, using uniform stress assumption, zone wise full range stress-strain curves are extracted. In USM methodology, the elastic and plastic material models are fitted to the zone wise stress-strain curves and required parameters are extracted from it. But inherent disadvantage is lot of images need to be processed for the parameter extraction. Recently, VFM is gaining lot of popularity in characterization domain as it is robust, accurate and faster. VFM is based on the principle of virtual work where, the weak form of local equilibrium equations and kinematically admissible virtual displacement fields are utilized for parameter extraction. Hollomon's power law is used here as the hardening rule. Young's modulus, Poisson's ratio, yield stress, strength coefficient and strain hardening exponent are the parameters extracted zone wise using both USM and VFM. A Vicker's microhardness measurement is also conducted across the weld zone towards mapping the strength behavior. Fusion zone has reported higher yield strength, strength coefficient and Poisson's ratio. Young's modulus value is found decreasing from base metal towards the fusion zone. The trend observed in parameter variation across the weld zone obtained by both USM and VFM compares very well. Due

  20. Measuring weld heat to evaluate weld integrity

    Energy Technology Data Exchange (ETDEWEB)

    Schauder, V., E-mail: schauder@hks-prozesstechnik.de [HKS-Prozesstechnik GmbH, Halle (Germany)

    2015-11-15

    Eddy current and ultrasonic testing are suitable for tube and pipe mills and have been used for weld seam flaw detection for decades, but a new process, thermography, is an alternative. By measuring the heat signature of the weld seam as it cools, it provides information about weld integrity at and below the surface. The thermal processes used to join metals, such as plasma, induction, laser, and gas tungsten arc welding (GTAW), have improved since they were developed, and they get better with each passing year. However, no industrial process is perfect, so companies that conduct research in flaw detection likewise continue to develop and improve the technologies used to verify weld integrity: ultrasonic testing (UT), eddy current testing (ET), hydrostatic, X-ray, magnetic particle, and liquid penetrant are among the most common. Two of these are used for verifying the integrity of the continuous welds such as those used on pipe and tube mills: UT and ET. Each uses a transmitter to send waves of ultrasonic energy or electrical current through the material and a receiver (probe) to detect disturbances in the flow. The two processes often are combined to capitalize on the strengths of each. While ET is good at detecting flaws at or near the surface, UT penetrates the material, detecting subsurface flaws. One drawback is that sound waves and electrical current waves have a specific direction of travel, or an alignment. A linear defect that runs parallel to the direction of travel of the ultrasonic sound wave or a flaw that is parallel to the coil winding direction of the ET probe can go undetected. A second drawback is that they don't detect cold welds. An alternative process, thermography, works in a different fashion: It monitors the heat of the material as the weld cools. Although it measures the heat at the surface, the heat signature provides clues about cooling activity deep in the material, resulting in a thorough assessment of the weld's integrity It

  1. The development of digital monitoring technique

    Energy Technology Data Exchange (ETDEWEB)

    Koo, In Soo; Kim, D. H.; Kim, J. S.; Kim, C. H.; Kim, G. O.; Park, H. Y.; Suh, S. Y.; Sung, S. H.; Song, S. J.; Lee, C. K.; Jang, G. S.; Hur, S.

    1997-08-01

    A study has been performed for advanced DSP technology for the digital nuclear I and C systems for the monitoring and diagnosis techniques for high-pressurized structures integrity in NSSS. In the development of advanced DSP technology, real time process, communication network and signal validation were selected as the essential technologies of the digital signal process, and the requirements and methodology for the application of these technologies in NPP were established through technical analysis. Based on its results, the DPIS and the signal validation algorithm were developed. For the real-time process, the necessary requirements were define and the methodology of real-time software modeling was developed. For the communication network, the methodology of selection of the communication technique and developing procedure were established with an extraction of requirements. Functions, requirements, structure and technical specification were developed for the DPIS, and a real-time signal validation algorithm was developed and implemented for the signal validation. In a study on monitoring techniques for abnormal conditions, test and experimental facilities have been set up in order to carry out the required tests during research activities. Studies concentrated on how to acquire proper vibration or emission signals from mechanical structures and equipments, and to diagnose effectively the abnormal conditions of high pressure structure integrity. The algorithms of automatic signal analysis and diagnosis for abnormal conditions have been developed in this study to assist the operator`s monitoring and diagnosis activities on structure integrity using new technologies. (author). 23 refs., 68 tabs., 196 figs.

  2. Plasma arc welding weld imaging

    Science.gov (United States)

    Rybicki, Daniel J. (Inventor); Mcgee, William F. (Inventor)

    1994-01-01

    A welding torch for plasma arc welding apparatus has a transparent shield cup disposed about the constricting nozzle, the cup including a small outwardly extending polished lip. A guide tube extends externally of the torch and has a free end adjacent to the lip. First and second optical fiber bundle assemblies are supported within the guide tube. Light from a strobe light is transmitted along one of the assemblies to the free end and through the lip onto the weld site. A lens is positioned in the guide tube adjacent to the second assembly and focuses images of the weld site onto the end of the fiber bundle of the second assembly and these images are transmitted along the second assembly to a video camera so that the weld site may be viewed continuously for monitoring the welding process.

  3. Infrared thermography for monitoring heat generation in a linear friction welding process of Ti6Al4V alloy

    Science.gov (United States)

    Maio, L.; Liberini, M.; Campanella, D.; Astarita, A.; Esposito, S.; Boccardi, S.; Meola, C.

    2017-03-01

    The increasing use of titanium alloys in a wider range of applications requires the development of new techniques and processes capable to decrease production costs and manufacturing times. In this regard welding and other joining techniques play an important role. Today, solid state friction joining processes, such as friction stir welding, friction spot welding, inertia friction welding, continuous-drive friction welding and linear friction welding (LFW), represent promising methods for part manufacturing. They allow for joining at temperature essentially below the melting point of the base materials being joined, without the addition of filler metal. However, the knowledge of temperature is essential to understand and model the phenomena involved in metal welding. A global measured value represents only a clue of the heat generation during the process; while, a deep understanding of welding thermal aspects requires temperature field measurement. This paper is focused on the use of infrared thermography applied to the linear friction welding process of Ti6Al4V alloy. The attention is concentrated on thermal field that develops on the outer wall of the two parts to be joined (i.e. heat generated in the friction zone), and on the maximum temperature that characterizes the process before and after the flash formation.

  4. Complete Status Report Documenting Development of Friction Stir Welding for Joining Thin Wall Tubing of ODS Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Hoelzer, David T. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Bunn, Jeffrey R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Gussev, Maxim N. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-08-01

    The development of friction stir welding (FSW) for joining thin sections of the advanced oxide dispersion strengthened (ODS) 14YWT ferritic alloy was initiated in Fuel Cycle Research and Development (FCRD), now the Nuclear Technology Research and Development (NTRD), in 2015. The first FSW experiment was conducted in late FY15 and successfully produced a bead-on-plate stir zone (SZ) on a 1 mm thick plate of 14YWT (SM13 heat). The goal of this research task is to ultimately demonstrate that FSW is a feasible method for joining thin wall (0.5 mm thick) tubing of 14YWT.

  5. Study on visual image information detection of external angle weld based on arc welding robot

    Science.gov (United States)

    Liu, Xiaorui; Liu, Nansheng; Sheng, Wei; Hu, Xian; Ai, Xiaopu; Wei, Yiqing

    2009-11-01

    Nowadays, the chief development trend in modern welding technology is welding automation and welding intelligence. External angle weld has a certain proportion in mechanical manufacture industries. In the real-time welding process, due to hot deformation and the fixture of workpieces used frequently, torch will detach welding orbit causes deviation, which will affect welding quality. Therefore, elimination weld deviation is the key to the weld automatic tracking system. In this paper, the authors use the self-developed structured light vision sensor system which has significant advantage compared with arc sensors to capture real-time weld images. In the project of VC++6.0 real-time weld image processing, after binaryzation with threshold value seventy, 3*1 median filter, thinning, obtain weld main stripe. Then, using the extraction algorithm this paper proposed to obtain weld feature points, and compute position of weld. Experiment result verified that the extraction algorithm can locate feature points rapidly and compute the weld deviation accurately.

  6. Width Criterion For Weld-Seam-Tracking Data

    Science.gov (United States)

    Lincir, Mark R.

    1993-01-01

    Image-processing algorithm in "through-torch-vision" (T3V) system developed to guide gas/tungsten arc welding robot along weld seam modified, according to proposal, reducing incidence of inaccurate tracking of weld seam. Developmental system intended to provide closed-loop control of motion of welding robot along weld seam on basis of lines in T3V image identified by use of image-processing algorithm and assumed to coincide with edges of weld seam. Use of width criterion prevents tracking of many false pairs of lines, with consequent decrease in incidence of inaccurate tracking and increase in confidence in weld-tracking capability of robotic welding system.

  7. Development of ultrasonic test specifications for heavy welded rotor parts during the past few decades; Entwicklung der Ultraschallpruefanforderungen an schweren Rotor-Schmiedeteilen ueber die letzten Jahrzehnte

    Energy Technology Data Exchange (ETDEWEB)

    Vrana, Johannes; Heinrich, Werner [Siemens Energy, Berlin (Germany); Zimmer, Alexander [Saarschmiede, Voelklingen (Germany); Bailey, Kevin; Zombo, Paul; Shannon, Robert E. [Siemens Energy, Orlando, FL (United States); Lohmann, Hans-Peter [Siemens Energy, Muelheim an der Ruhr (Germany)

    2011-07-01

    Heavy welded rotor parts, e.g. in land-based turbines and generators for power generation, are tested before they are put in operation, e.g. by ultrasonic methods. The tests were introduced several decades ago in an attempt to ensure component integrity. In the early years, the tests were carried out manually in contact using longitudinal wave test probes in pulse-echo operation, at first without fixed registration or decision limits. The development of inspection techniques, the change in construction requirements, the further development of fracture-mechanical calculations, new findings in rotor operation, experience with the inspection method, and theoretical reflections on detection probabilities all contributed to the changes that led to the current inspection requirements. The development of size measuring techniques led to the establishment of registration and decision limits. Angles and transmitter-receiver test probes were introduced, and automatic equipment came next. All this resulted in more sensitive techniques based on theoretical specifications, and modern ultrasonic methods were introduced at the same time. This publication describes the development of ultrasonic test specifications during the past few decades and also gives an outlook to the future.

  8. Collision Welding of Dissimilar Materials by Vaporizing Foil Actuator: A Breakthrough Technology for Dissimilar Metal Joining

    Energy Technology Data Exchange (ETDEWEB)

    Daehn, Glenn S. [The Ohio State Univ., Columbus, OH (United States). Dept. of Materials Science and Engineering; Vivek, Anupam [The Ohio State Univ., Columbus, OH (United States). Dept. of Materials Science and Engineering; Liu, Bert C. [The Ohio State Univ., Columbus, OH (United States). Dept. of Materials Science and Engineering

    2016-09-30

    This work demonstrated and further developed Vaporizing Foil Actuator Welding (VFAW) as a viable technique for dissimilar-metal joining for automotive lightweighting applications. VFAW is a novel impact welding technology, which uses the pressure developed from electrically-assisted rapid vaporization of a thin aluminum foil (the consumable) to launch and ultimately collide two of more pieces of metal to create a solid-state bond between them. 18 dissimilar combinations of automotive alloys from the steel, aluminum and magnesium alloy classes were screened for weldability and characterized by metallography of weld cross sections, corrosion testing, and mechanical testing. Most combinations, especially a good number of Al/Fe pairs, were welded successfully. VFAW was even able to weld combinations of very high strength materials such as 5000 and 6000 series aluminum alloys to boron and dual phase steels, which is difficult to impossible by other joining techniques such as resistance spot welding, friction stir welding, or riveting. When mechanically tested, the samples routinely failed in a base metal rather than along the weld interface, showing that the weld was stronger than either of the base metals. As for corrosion performance, a polymer-based protective coating was used to successfully combat galvanic corrosion of 5 Al/Fe pairs through a month-long exposure to warm salt fog. In addition to the technical capabilities, VFAW also consumes little energy compared to conventional welding techniques and requires relatively light, flexible tooling. Given the technical and economic advantages, VFAW can be a very competitive joining technology for automotive lightweighting. The success of this project and related activities has resulted in substantial interest not only within the research community but also various levels of automotive supply chain, which are collaborating to bring this technology to commercial use.

  9. TIG-dressing of high strength butt welded connection - Part 2: physical testing and modelling

    NARCIS (Netherlands)

    Es, S.H.J. van; Kolstein, M.H.; Pijpers, R.J.M.; Bijlaard, F.S.K.

    2013-01-01

    Weld improvement techniques are aimed at reducing the notch effects of welds and generally focus on two aspects: a change of geometry of the weld toe and a change of the weld residual stresses. In this paper, fatigue tests are discussed, performed on butt welded specimens in steel grades ranging

  10. TIG-dressing of High Strength Butt Welded Connection. Part 2 : Physical Testing and Modelling

    NARCIS (Netherlands)

    Van Es, S.H.J.; Kolstein, M.H.; Pijpers, R.J.M.; Bijlaard, F.S.K.

    2014-01-01

    Weld improvement techniques are aimed at reducing the notch effects of welds and generally focus on two aspects: a change of geometry of the weld toe and a change of the weld residual stresses. In this paper, fatigue tests are discussed, performed on butt welded specimens in steel grades ranging

  11. Current developments in composite materials and techniques.

    Science.gov (United States)

    Dietschi, D; Dietschi, J M

    1996-09-01

    General reduction of dental caries and patient interest in dental aesthetics have resulted in the development of new restorative materials and techniques. Composite materials and adhesive techniques have become the foundation of modern restorative dentistry. Mechanical performance, wear resistance, and aesthetic potential of composite resins have been significantly improved, and the material is now used in cases ranging from the restoration of initial decays and cosmetic corrections to the veneering in extended prosthetic rehabilitation. Polymerization shrinkage of the resin matrix remains a challenge and still imposes limitations in the application of direct techniques. The learning objective of this article is to review the most significant advances of composite materials and the importance of utilizing the available treatment options with discretion, selecting those which preserve the tooth structure and require the least maintenance.

  12. Study of the mechanical properties of welded joints by wet sub sea welding technique with tubular electrode; Estudo das propriedades mecanicas de juntas soldadas pela tecnica de soldagem subaquatica molhada com eletrodo tubular

    Energy Technology Data Exchange (ETDEWEB)

    Teichmann, Erwin Werner; Baixo, Carlos Eduardo Iconomos; Dutra, Jair Carlos [Santa Catarina Univ., Florianopolis, SC (Brazil). Dept. de Engenharia Mecanica. Lab. de Soldagem e Mecatronica - LABSOLDA]. E-mail: erwin@labsolda.ufsc.br; Santos, Valter Rocha dos [Centro Federal de Educacao Tecnologica (CEFET), Rio de Janeiro, RJ (Brazil); Teixeira, Jose Claudio [PETROBRAS, Rio de Janeiro, RJ (Brazil). Centro de Pesquisas

    1997-07-01

    Some experiments conducted at LABSOLDA/UFSC - a welding laboratory of Santa Catarina Univ., Florianopolis, Brazil - in order to identify mechanical properties, weld bead geometry and the quantity and dimensions of pores in weld beads produced by sub sea wet FCAW are described. Welding in shallow water with power source adjusted to operate in constant current characteristic mode and a set of parameters to establish an open arc transfer mode it was obtained weld beads with regular geometry and an acceptable profile, with low level of defects incidence, no pores and crack free. The tenacity measured by Charpy tests (0C) was 34 J and hardness of 119 HV-10 measured by Vickers tests. The methodology used in the experiments and the results obtained are discussed in the paper. (author)

  13. Prediction of solidification and phase transformation in weld metals for welding of high performance stainless steels; Kotaishoku kotainetsu stainless koyo yosetsu kinzoku no gyoko hentai no yosoku gijutsu

    Energy Technology Data Exchange (ETDEWEB)

    Koseki, T.; Inoue, H.; Morimoto, H.; Okita, S. [Nippon Steel Corp., Tokyo (Japan)

    1995-02-28

    Prediction technology is introduced on the solidification and transformation of weld metals used for high performance stainless steel. A model has been developed which uses Thermo Calc, a multiple balanced calculation program, as a means to analyze the solidification of multi-component alloys including the polyphase solidification such as eutectic and peritectic. Verification has been in progress concerning the adequacy of this model and the adaptability as a practical steel. The following are the prediction technologies for solidification and transformation which have been derived from experiments and applied to welding techniques: the effects of nitrogen on the solidification mode and residual {gamma}quantity of a welding metal that is required for controlling the welding/solidification of high nitrogen content {gamma}system stainless steel; the structural control of weld metal for high corrosion resistance high Mo stainless steel, in which high Ni and high Mo contents are indispensable for attaining the optimum structure; the structural control of weld metal for two-phase stainless steel containing Mo and N, in which it is essential to secure a high nitrogen content and a {delta}/{gamma}phase balance in a weld metal; and the precipitation prediction of intermetallic compound in a high alloy weld metal for a high alloy stainless steel, for which an explanation is there by Cieslak et al. based on the phase stability theory. 22 refs., 16 figs.

  14. Welding of Aluminum Alloys to Steels: An Overview

    Science.gov (United States)

    2013-08-01

    UNCLASSIFIED 7 UNCLASSIFIED 2.1. Fusion welding methods 2.1.1. Gas metal arc (MIG) welding and tungsten inert gas ( TIG ) welding techniques...UNCLASSIFIED 8 UNCLASSIFIED Fig.3. (a) Schematic of the butt TIG welding for joining the aluminum to steel and (b) formation of the cracks at the...dissimilar metals TIG welding -brazing of aluminum alloy to stainless steel, Materials Science and Engineering A 509 (2009) 31-40. [28] S.B. Lin, J.L. Song

  15. Complete Status Report Documenting Weld Development for Thin Wall Tubing of ODS Ferritic Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Hoelzer, David T. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Edmondson, Philip D. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Gussev, Maxim N. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Tang, Wei [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Feng, Zhili [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2016-09-16

    Beginning in 2015, research in the FCRD program began the development of FSW for joining thin sections of 14YWT in the form of thin (0.5 mm) plate and ultimately thin wall tubing. In the previous fiscal year, a ~1 mm thick plate, or sheet, of 14YWT was produced by hot rolling with no edge cracking. The initial FSW experiment was performed on the 1 mm thick plate and involved a bead-on-plate weld in which the spinning pin tool is plunged into the plate surface, but does not penetrate the thickness of the plate, and then travels the length of the plate. The FSW run successfully produced a bead-on-plate stir zone on the 1 mm thick plate of 14YWT, but no characterization studies of the stir zone were performed by the end of FY15. Therefore, the results presented in this report cover the microstructural analysis of the bead-on-plate stir zone and the initial research task on obtaining tensile properties of the stir zone using the digital image correlation (DIC) approach during testing of miniature tensile specimens to assess the quality of the FSW parameters used in the initial experiment. The results of the microstructural characterization study using optical, scanning electron and scanning transmission electron microscopies showed the grain structure in the SZ to have isotropic and irregular shape but very similar size compared to the highly elongated grains oriented horizontally with the plane of the plate that were observed in the unaffected zone of 14YWT. Several cracks oriented horizontally were observed mostly on the retreating side of the SZ in both the SZ and TMAZ. These cracks may have formed due to insufficient pressure being exerted on the top surface of the plate by the shoulder and pin tool during the FSW run. High resolution STEM-EDS analysis showed the presence of the Y-Ti-O particles in the SZ, but that some particles exhibited coarsening. Overall, the FSW parameters used to produce the bead-on-plate SZ in the 0.1 cm thick plate of 14YWT were nearly

  16. Dynamics of space welding impact and corresponding safety welding study.

    Science.gov (United States)

    Fragomeni, James M; Nunes, Arthur C

    2004-03-01

    This study was undertaken in order to be sure that no hazard would exist from impingement of hot molten metal particle detachments upon an astronauts space suit during any future electron beam welding exercises or experiments. The conditions under which molten metal detachments might occur in a space welding environment were analyzed. The safety issue is important during welding with regards to potential molten metal detachments from the weld pool and cold filler wire during electron beam welding in space. Theoretical models were developed to predict the possibility and size of the molten metal detachment hazards during the electron beam welding exercises at low earth orbit. Some possible ways of obtaining molten metal drop detachments would include an impulse force, or bump, to the weld sample, cut surface, or filler wire. Theoretical models were determined for these detachment concerns from principles of impact and kinetic energies, surface tension, drop geometry, surface energies, and particle dynamics. A weld pool detachment parameter for specifying the conditions for metal weld pool detachment by impact was derived and correlated to the experimental results. The experimental results were for the most part consistent with the theoretical analysis and predictions. c2003 Elsevier Ltd. All rights reserved.

  17. Dynamics of space welding impact and corresponding safety welding study

    Science.gov (United States)

    Fragomeni, James M.; Nunes, Arthur C.

    2004-03-01

    This study was undertaken in order to be sure that no hazard would exist from impingement of hot molten metal particle detachments upon an astronauts space suit during any future electron beam welding exercises or experiments. The conditions under which molten metal detachments might occur in a space welding environment were analyzed. The safety issue is important during welding with regards to potential molten metal detachments from the weld pool and cold filler wire during electron beam welding in space. Theoretical models were developed to predict the possibility and size of the molten metal detachment hazards during the electron beam welding exercises at low earth orbit. Some possible ways of obtaining molten metal drop detachments would include an impulse force, or bump, to the weld sample, cut surface, or filler wire. Theoretical models were determined for these detachment concerns from principles of impact and kinetic energies, surface tension, drop geometry, surface energies, and particle dynamics. A weld pool detachment parameter for specifying the conditions for metal weld pool detachment by impact was derived and correlated to the experimental results. The experimental results were for the most part consistent with the theoretical analysis and predictions.

  18. Measurement of weld penetration depths in thin structures using transmission coefficients of laser-generated Lamb waves and neural network.

    Science.gov (United States)

    Yang, Lei; Ume, I Charles

    2017-07-01

    The Laser/EMAT ultrasonic (LEU) technique has shown the capability to measure weld penetration depths in thick structures based on ray-tracing of laser-generated bulk and surface waves. The ray-tracing method is not applicable to laser-generated Lamb waves when the LEU technique is used to measure weld penetration depths in thin structures. In this work, transmission coefficients of Lamb waves present in the LEU signals are investigated against varying weld penetration depths. An artificial neural network is developed to use transmission coefficients of sensitive Lamb waves and LEU signal energy to predict weld penetration depths accurately. The developed method is very attractive because it allows a quick inspection of weld penetration depths in thin structures. Copyright © 2017 Elsevier B.V. All rights reserved.

  19. Heat-affected zone and phase composition of 0.09 C-2 Mn-1 Si-Fe steel depending on welding technique

    Science.gov (United States)

    Popova, Natalya; Ozhiganov, Eugeniy; Nikonenko, Elena; Ababkov, Nikolay; Smirnov, Aleksander; Koneva, Nina

    2017-11-01

    The paper presents the transmission electron microscopy (TEM) investigations of the structure and phase composition of the heat-affected zone (HAZ) in welded joint modified by four types of welding, namely: electrode welding and electropercussive welding both with and without the introduction of artificial flaws. Artificial flows are aluminum pieces. TEM investigations are carried out within HAZ between the deposited and base metal at 1 mm distance to the latter. The type 0.09C-2Mn-1Si-Fe steel is used as weld material. It is shown that the welding process has an effect on the material morphology, phase composition, faulted structure and its parameters. Long-range stresses are divided into plastic and elastic components. It is demonstrated that the type of welding does not change the structural quality of welded joint represented by perlite and ferrite as contrasted with their volume fraction. According to observations, any type of welding with the introduction of artificial flaws results in the destruction of perlite. Polarization of the dislocation structure occurs. The amplitude of mean internal stresses does not practically depend on the welding type. It is shown that the introduction of artificial flaws both during electrode and electropercussive welding reduce the quantitative parameters of the faulted structure.

  20. Recent developments in monoclonal antibody radiolabeling techniques

    Energy Technology Data Exchange (ETDEWEB)

    Srivastava, S.C.; Mease, R.C.

    1989-01-01

    Monoclonal antibodies (MAbs) have shown the potential to serve as selective carriers of radionuclides to specific in vivo antigens. Accordingly, there has been an intense surge of research activity in an effort to develop and evaluate MAb-based radiopharmaceuticals for tumor imaging (radioimmunoscintigraphy) and therapy (radioimmunotherapy), as well as for diagnosing nonmalignant diseases. A number of problems have recently been identified, related to the MAbs themselves and to radiolabeling techniques, that comprise both the selectivity and the specificity of the in vivo distribution of radiolabeled MAbs. This paper will address some of these issues and primarily discuss recent developments in the techniques for radiolabeling monoclonal antibodies that may help resolve problems related to the poor in vivo stability of the radiolabel and may thus produce improved biodistribution. Even though many issues are identical with therapeutic radionuclides, the discussion will focus mainly on radioimmunoscintigraphic labels. 78 refs., 6 tabs.

  1. Laser Beam Submerged Arc Hybrid Welding

    Science.gov (United States)

    Reisgen, Uwe; Olschok, Simon; Jakobs, Stefan; Schleser, Markus; Mokrov, Oleg; Rossiter, Eduardo

    The laser beam-submerged arc hybrid welding method originates from the knowledge that, with increasing penetration depth, the laser beam process has a tendency to pore formation in the lower weld regions. The coupling with the energy-efficient submerged-arc process improves degassing and reduces the tendency to pore formation. The high deposition rate of the SA process in combination with the laser beam process offers, providing the appropriate choice of weld preparation, the possibility of welding plates with a thickness larger than 20° mm in a single pass, and also of welding thicker plates with the double-sided single pass technique.

  2. Scanning Technique In Developing Students Reading Comprehension

    OpenAIRE

    Thamrin, Nur Sehang

    2012-01-01

    One of the objectives of teaching English for university students is the students are expected to understand the reading text. However, it is very difficult for the students to catch the message from the reading text as they have limited words and reading strategies. This research was intended to solve the students' problem relating to the reading comprehension. The aim of this research is to prove whether the implementation of scanning technique is effective to develop students' reading comp...

  3. The development of human behavior analysis techniques

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jung Woon; Lee, Yong Hee; Park, Geun Ok; Cheon, Se Woo; Suh, Sang Moon; Oh, In Suk; Lee, Hyun Chul; Park, Jae Chang

    1997-07-01

    In this project, which is to study on man-machine interaction in Korean nuclear power plants, we developed SACOM (Simulation Analyzer with a Cognitive Operator Model), a tool for the assessment of task performance in the control rooms using software simulation, and also develop human error analysis and application techniques. SACOM was developed to assess operator`s physical workload, workload in information navigation at VDU workstations, and cognitive workload in procedural tasks. We developed trip analysis system including a procedure based on man-machine interaction analysis system including a procedure based on man-machine interaction analysis and a classification system. We analyzed a total of 277 trips occurred from 1978 to 1994 to produce trip summary information, and for 79 cases induced by human errors time-lined man-machine interactions. The INSTEC, a database system of our analysis results, was developed. The MARSTEC, a multimedia authoring and representation system for trip information, was also developed, and techniques for human error detection in human factors experiments were established. (author). 121 refs., 38 tabs., 52 figs.

  4. Techniques to develop data for hydrogeochemical models

    Energy Technology Data Exchange (ETDEWEB)

    Thompson, C.M.; Holcombe, L.J.; Gancarz, D.H.; Behl, A.E. (Radian Corp., Austin, TX (USA)); Erickson, J.R.; Star, I.; Waddell, R.K. (Geotrans, Inc., Boulder, CO (USA)); Fruchter, J.S. (Battelle Pacific Northwest Lab., Richland, WA (USA))

    1989-12-01

    The utility industry, through its research and development organization, the Electric Power Research Institute (EPRI), is developing the capability to evaluate potential migration of waste constitutents from utility disposal sites to the environment. These investigations have developed computer programs to predict leaching, transport, attenuation, and fate of inorganic chemicals. To predict solute transport at a site, the computer programs require data concerning the physical and chemical conditions that affect solute transport at the site. This manual provides a comprehensive view of the data requirements for computer programs that predict the fate of dissolved materials in the subsurface environment and describes techniques to measure or estimate these data. In this manual, basic concepts are described first and individual properties and their associated measurement or estimation techniques are described later. The first three sections review hydrologic and geochemical concepts, discuss data requirements for geohydrochemical computer programs, and describe the types of information the programs produce. The remaining sections define and/or describe the properties of interest for geohydrochemical modeling and summarize available technique to measure or estimate values for these properties. A glossary of terms associated with geohydrochemical modeling and an index are provided at the end of this manual. 318 refs., 9 figs., 66 tabs.

  5. Weld overlay cladding with iron aluminides

    Energy Technology Data Exchange (ETDEWEB)

    Goodwin, G.M. [Oak Ridge National Lab., TN (United States)

    1995-08-01

    The hot and cold cracking tendencies of some early iron aluminide alloy compositions have limited their use in applications where good weldability is required. Using hot crack testing techniques invented at ORNL, and experimental determinations of preheat and postweld heat treatment needed to avoid cold cracking, we have developed iron aluminide filler metal compositions which can be successfully used to weld overlay clad various substrate materials, including 9Cr-1Mo steel, 2-1/4Cr-1Mo steel, and 300-series austenitic stainless steels. Dilution must be carefully controlled to avoid crack-sensitive deposit compositions. The technique used to produce the current filler metal compositions is aspiration-casting, i.e. drawing the liquid from the melt into glass rods. Future development efforts will involve fabrication of composite wires of similar compositions to permit mechanized gas tungsten arc (GTA) and/or gas metal arc (GMA) welding.

  6. Preventing Contamination In Electron-Beam Welds

    Science.gov (United States)

    Goodin, Wesley D.; Gulbrandsen, Kevin A.; Oleksiak, Carl

    1990-01-01

    Simple expedient eliminates time-consuming, expensive manual hand grinding. Use of groove and backup tube greatly reduces postweld cleanup in some electron-beam welding operations. Tube-backup method developed for titanium parts, configurations of which prevents use of solid-block backup. In new welding configuration, tube inserted in groove to prevent contact between alumina beads and molten weld root. When welding complete and beads and tube removed, only minor spatter remains and is ground away easily.

  7. Welding multiple plies with an electron beam

    Science.gov (United States)

    Kiluk, F. J.

    1980-01-01

    Method for electron-beam welding of multi-ply metal sheets eliminates ply separation and minimizes porosity. Method was developed for assembling bellows made of four plies of iron/nickel alloy sheets. Method consists of making successive stitch welds with electron beam until weld seam is completely filled in and all plies have been penetrated.

  8. Technology of welding aluminum alloys-III

    Science.gov (United States)

    Harrison, J. R.; Kor, L. J.; Oleksiak, C. E.

    1978-01-01

    Control of porosity in weld beads was major objective in development of aluminum welding program. Porosity, most difficult defect to control, is caused by hydrogen gas unable to escape during solidification. Hard tooling allows hotter bead than free-fall tooling so hydrogen bubbles can boil out instead of forming pores. Welding position, moisture, and cleanliness are other important factors in control of porosity.

  9. On the development of a new pre-weld thermal treatment procedure for preventing heat-affected zone (HAZ) liquation cracking in nickel-base IN 738 superalloy

    Science.gov (United States)

    Ola, O. T.; Ojo, O. A.; Chaturvedi, M. C.

    2014-10-01

    Hot cracking in the heat-affected zone (HAZ) of precipitation strengthened nickel-base superalloys, such as IN 738, during fusion welding remains a major factor limiting reparability of nickel-base gas turbine components. The problem of HAZ intergranular cracking can be addressed by modifying the microstructure of the pre-weld material through thermal treatment, which requires significant understanding of the critical factors controlling cracking behaviour. The decomposition of Mo-Cr-W-and Cr-rich borides in the alloy, among other factors, has been observed to contribute significantly to non-equilibrium intergranular liquation and, hence, intergranular liquation cracking during welding. Gleeble physical simulation of HAZ microstructure has also shown that non-equilibrium liquation is more severe in the vicinity of decomposed borides in the alloy and can occur at temperatures as low as 1,150 °C. Although currently existing pre-weld heat treatments for IN 738 superalloy minimize the contributions of dissolution of second phases, including borides, to HAZ intergranular liquation, these heat treatments are not industrially feasible due to process-related difficulties. Therefore, a new industrially feasible and effective pre-weld thermal treatment process, designated as FUMT, was developed during the present research by controlling both the formation of borides and the segregation of boron at the grain boundaries in the pre-weld heat-treated material. This thermal treatment was observed to very significantly reduce intergranular HAZ cracking in welded IN 738 superalloy. The details of the development process and developed procedure are presented in this paper.

  10. Upgraded HFIR Fuel Element Welding System

    Energy Technology Data Exchange (ETDEWEB)

    Sease, John D [ORNL

    2010-02-01

    The welding of aluminum-clad fuel plates into aluminum alloy 6061 side plate tubing is a unique design feature of the High Flux Isotope Reactor (HFIR) fuel assemblies as 101 full-penetration circumferential gas metal arc welds (GMAW) are required in the fabrication of each assembly. In a HFIR fuel assembly, 540 aluminum-clad fuel plates are assembled into two nested annular fuel elements 610 mm (24-inches) long. The welding process for the HFIR fuel elements was developed in the early 1960 s and about 450 HFIR fuel assemblies have been successfully welded using the GMAW process qualified in the 1960 s. In recent years because of the degradation of the electronic and mechanical components in the old HFIR welding system, reportable defects in plate attachment or adapter welds have been present in almost all completed fuel assemblies. In October 2008, a contract was awarded to AMET, Inc., of Rexburg, Idaho, to replace the old welding equipment with standard commercially available welding components to the maximum extent possible while maintaining the qualified HFIR welding process. The upgraded HFIR welding system represents a major improvement in the welding system used in welding HFIR fuel elements for the previous 40 years. In this upgrade, the new inner GMAW torch is a significant advancement over the original inner GMAW torch previously used. The innovative breakthrough in the new inner welding torch design is the way the direction of the cast in the 0.762 mm (0.030-inch) diameter aluminum weld wire is changed so that the weld wire emerging from the contact tip is straight in the plane perpendicular to the welding direction without creating any significant drag resistance in the feeding of the weld wire.

  11. Advantages of new micro-jet welding technology on weld microstructure control

    Directory of Open Access Journals (Sweden)

    Jan PIWNIK

    2013-01-01

    Full Text Available An innovative apparatus to welding process with micro-jet cooling of the weld made it possible to carry out technological tests, which have proved theoretical considerations about this problem. This project gives real opportunities for professional development in the field of welding with controlling the parameters of weld structure. These tests have proved that the new micro-jet technology has the potential for growth. It may be great achievement of welding technology in order to increase weld metal strength. The new technology with micro-jet cooling may have many practical applications in many fields, for example such as in the transport industry or to repair damaged metal elements. The advantages of the new device over the traditional system are the ability to control the structure of the weld, the weld mechanical performance increases and improve the quality of welded joints.

  12. Process Parameters Optimization for Friction Stir Welding of Pure Aluminium to Brass (CuZn30 using Taguchi Technique

    Directory of Open Access Journals (Sweden)

    Elfar O. M. R.

    2016-01-01

    Full Text Available In this research, the friction stir welding of dissimilar commercial pure aluminium and brass (CuZn30 plates was investigated and the process parameters were optimized using Taguchi L9 orthogonal array. The considered process parameters were the rotational speed, traverse speed and pin offset. The optimum setting was determined with reference to ultimate tensile strength of the joint. The predicted optimum value of ultimate tensile strength was confirmed by experimental run using optimum parameters. Analysis of variance revealed that traverse speed is the most significant factor in controlling the joint tensile strength and pin offset also plays a significant role. In this investigation, the optimum tensile strength is 50% of aluminium base metal. Metallographic examination revealed that intermetallic compounds were formed in the interface of the optimum joint where the tensile failure was observed to take place.

  13. Finite element modelling and characterization of friction welding on UNS S31803 duplex stainless steel joints

    Directory of Open Access Journals (Sweden)

    Mohammed Asif. M

    2015-12-01

    Full Text Available Solid state joining techniques are increasingly employed in joining duplex stainless steel materials due to their high integrity. Continuous drive friction welding is a solid state welding technique which is used to join similar and dissimilar materials. This joining technique is characterized by short cycle time, low heat input and narrow heat affected zones. The simulation becomes an important tool in friction welding because of short welding cycle. In the present work, a three dimensional non-linear finite element model was developed. The thermal history and axial shortening profiles were predicted using ANSYS, a software tool. This numerical model was validated using experimental results. The results show that the frictional heating stage of the process has more influence on temperature and upsetting stage has more impact on axial shortening. The knowledge of these parameters would lead to optimization of input parameters and improvement of design and machine tools.

  14. Development of an automation system for iodine-125 brachytherapy seed production by ND:YAG laser welding

    Energy Technology Data Exchange (ETDEWEB)

    Somessari, Samir L.; Feher, Anselmo; Sprenger, Francisco E.; Rostellato, Maria Elisa C.M.; Costa, Fabio E.; Calvo, Wilson A.P., E-mail: somessar@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP) Sao Paulo, SP (Brazil)

    2009-07-01

    The aim of this work is to develop an automation system for iodine-125 radioactive seed production by Nd:YAG laser welding, which has been used successfully in low dose rate brachytherapy treatment. This small seed consists of a welded titanium capsule, with 0.8 mm in diameter and 4.5 mm in length, containing iodine-125 adsorbed onto a silver rod. The iodine-125 seeds are implanted into the human prostate to irradiate the tumor for cancer treatment. Nowadays, the Radiation Technology Center, at IPEN-CNEN/SP imports and distributes 36,000 iodine-125 seeds per year, for the clinics and hospitals in the country. However, the Brazilian market potential is now over 8,000 iodine-125 seeds per month. The local production of these iodine-125 radioactive sources became a priority for the Institute, in order to reduce the price and the problems of prostate cancer management. It will permit to spread their use to a larger number of patients in Brazil. On the other hand, the industrial automation plays an important role for iodine-125 seeds in order to increase the productivity, with high quality and assurance, avoiding human factors, implementing and operating with good manufacturing practices. The technology consists of appliance electronic and electro-mechanical parts and components to control machines and processes. The automation system technology for iodine-125 seed production developed in this work was mainly assembled employing a Programmable Logic Controller, a stepper motor, an Nd:YAG laser welding machine and a supervisory. (author)

  15. Development of Microstructure and Crystallographic Texture in a Double-Sided Friction Stir Welded Microalloyed Steel

    Science.gov (United States)

    Rahimi, S.; Wynne, B. P.; Baker, T. N.

    2017-01-01

    The evolution of microstructure and crystallographic texture has been investigated in double-sided friction stir welded microalloyed steel, using electron backscatter diffraction (EBSD). The microstructure analyses show that the center of stirred zone reached a temperature between Ac1 and Ac3 during FSW, resulting in a dual-phase austenitic/ ferritic microstructure. The temperatures in the thermo-mechanically affected zone and the overlapped area between the first and second weld pass did not exceed the Ac1. The shear generated by the rotation probe occurs in austenitic/ferritic phase field where the austenite portion of the microstructure is transformed to a bainitic ferrite, on cooling. Analysis of crystallographic textures with regard to shear flow lines generated by the probe tool shows the dominance of simple shear components across the whole weld. The austenite texture at Ac1 - Ac3 is dominated by the B { {1bar{1}2} }phase textures formed on cooling were inherited from the shear textures of the austenite phase with relatively strong variant selection. The ferrite portion of the stirred zone and the ferrites in the thermo-mechanically affected zones and the overlapped area underwent shear deformation with textures dominated by the D1 { {bar{1}bar{1}2} }< 111rangle and D2 { {11bar{2}} }< 111rangle simple shear texture components. The formation of ultrafine equiaxed ferrite with submicron grain size has been observed in the overlapped area between the first and second weld pass. This is due to continuous dynamic strain-induced recrystallization as a result of simultaneous severe shear deformation and drastic undercooling.

  16. Development of mechanoluminescence technique for impact studies

    Energy Technology Data Exchange (ETDEWEB)

    Chandra, B.P., E-mail: bpchandra4@yahoo.co.i [Disha Academy of Research and Education, Disha Institute of Management and Technology, Satya Vihar, Vidhansabha-Chandrakhuri Marg, Raipur 492101 (C.G.) (India)

    2011-06-15

    A new technique called, mechanoluminescence technique, is developed for measuring the parameters of impact. This technique is based on the phenomenon of mechanoluminescence (ML), in which light emission takes place during any mechanical action on solids. When a small solid ball makes an impact on the mechanoluminescent thin film coated on a solid, then initially the elastico ML (EML) intensity increases with time, attains a maximum value I{sub m} at a particular time t{sub m}, and later on it decreases with time. The contact time T{sub c} of ball, can be determined from the relation T{sub c}=2t{sub c}, where t{sub c} is the time at which the EML emission due to compression of the sample becomes negligible. The area from where the EML emission occurs can be taken as the contact area A{sub c}. The maximum compression h is given by h=A{sub c}/({pi}r), where r is the radius of the impacting ball, and thus, h can be determined from the known values of A{sub c} and r. The maximum force at contact is given by F{sub m}=(2mU{sub 0})/T{sub c}, where m is the mass of the impacting ball and U{sub 0} is the velocity of the ball at impact. The maximum impact stress {sigma}{sub m} can be obtained from the relation, {sigma}{sub m}=F{sub m}/A{sub c}=(2mU{sub 0})/(T{sub c}A{sub c}). Thus, ML provides a real-time technique for determining the impact parameters such as T{sub c}, A{sub c}, h, F{sub m} and {sigma}{sub m}. Using the ML technique, the impact parameters of the SrAl{sub 2}O{sub 4}:Eu film and ZnS:Mn coating are determined. The ML technique can be used to determine the impact parameters in the elastic region and plastic region as well as fracture. ML can also be used to determine the impact parameters for the collision between solid and liquid, if the mechanoluminescent material is coated on the surface of the solid. The measurement of fracto ML in microsecond and nanosecond range may provide a tool for studying the fragmentations in solids by the impact. Using the fast

  17. Tailoring defect free fusion welds based on phenomenological modeling

    Science.gov (United States)

    Kumar, Amit

    principles still remains an important milestone in changing welding from almost an empirical art to a mainstream science-based technology. The ability to determine multiple welding variable sets to achieve desired weld attributes, based on scientific principles, would be an important step to achieve this goal. Furthermore, no comprehensive unified theoretical model exists today that can predict the formation of commonly occurring humping defects considering the effects of important welding variables such as the arc current, voltage, welding speed, nature of the shielding gas, electrode geometry, torch angle and ambient pressure. In this research work, a model is developed to achieve desired weld attributes and avoid high speed weld defects like humping. (Abstract shortened by UMI.)

  18. Resistance spot welding of galvanized steel: Part II. Mechanisms of spot weld nugget formation

    Science.gov (United States)

    Gedeon, S. A.; Eagar, T. W.

    1986-12-01

    Dynamic inspection monitoring of the weld current, voltage, resistance, electrode displacement, and force was performed in conjunction with a detailed study of the effects of material variations and weld process parameter modifications on resistance spot welding of coated and uncoated steels. In order to determine the mechanisms of weld nugget formation and growth, scanning electron microscopy photos were taken of the developing nugget. These physical changes were then related to the dynamic inspection curves and the welding current lobe. The effects of material variations and weld process modifications, the results of which were presented in Part I, can be explained through an understanding of these mechanisms.

  19. Microstructural Development in a TRIP-780 Steel Joined by Friction Stir Welding (FSW: Quantitative Evaluations and Comparisons with EBSD Predictions

    Directory of Open Access Journals (Sweden)

    Gladys Perez Medina

    Full Text Available Abstract The present work describes the effect of FSW on the result microstructure in the stir zone (SZ, thermo-mechanically affected zone (TMAZ, heat affected zone (HAZ and base metal (BM of a TRIP-780 steel. X-ray diffraction (XRD, optical microscopy (OM and EBSD were used for determinations retained austenite (RA in the SZ, It was found that the amount of RA developed in SZ was relatively large, (approximately 11% to 15%. In addition, recrystallization and the formation of a grain texture were resolved using EBSD. During FSW, the SZ experienced severe plastic deformation which lead to an increase in the temperature and consequently grain recrystallization. Moreover, it was found that the recrystallized grain structure and relatively high martensite levels developed in the SZ lead to a significant drop in the mechanical properties of the steel. In addition, microhardness profiles of the welded regions indicated that the hardness in both the SZ and TMAZ were relatively elevated confirming the development of martensite in these regions. In particular, to evaluate the mechanical strength of the weld, lap shear tensile test was conducted; exhibited the fracture zone in the SZ with shear fracture with uniformly distributed elongation shear dimples.

  20. Experimental Investigation and Optimization of TIG Welding Parameters on Aluminum 6061 Alloy Using Firefly Algorithm

    Science.gov (United States)

    Kumar, Rishi; Mevada, N. Ramesh; Rathore, Santosh; Agarwal, Nitin; Rajput, Vinod; Sinh Barad, AjayPal

    2017-08-01

    To improve Welding quality of aluminum (Al) plate, the TIG Welding system has been prepared, by which Welding current, Shielding gas flow rate and Current polarity can be controlled during Welding process. In the present work, an attempt has been made to study the effect of Welding current, current polarity, and shielding gas flow rate on the tensile strength of the weld joint. Based on the number of parameters and their levels, the Response Surface Methodology technique has been selected as the Design of Experiment. For understanding the influence of input parameters on Ultimate tensile strength of weldment, ANOVA analysis has been carried out. Also to describe and optimize TIG Welding using a new metaheuristic Nature - inspired algorithm which is called as Firefly algorithm which was developed by Dr. Xin-She Yang at Cambridge University in 2007. A general formulation of firefly algorithm is presented together with an analytical, mathematical modeling to optimize the TIG Welding process by a single equivalent objective function.

  1. Overview on the welding technologies of CLAM steel and the DFLL TBM fabrication

    Directory of Open Access Journals (Sweden)

    Junyu Zhang

    2016-12-01

    Full Text Available Dual Functional Lithium Lead (DFLL blanket was proposed for its advantages of high energy exchange efficiency and on-line tritium extraction, and it was selected as the candidate test blanket module (TBM for China Fusion Engineering Test Reactor (CFETR and the blanket for Fusion Design Study (FDS series fusion reactors. Considering the influence of high energy fusion neutron irradiation and high heat flux thermal load on the blanket, China Low Activation Martensitic (CLAM steel was selected as the structural material for DFLL blanket. The structure of the blanket and the cooling internal components were pretty complicated. Meanwhile, high precision and reliability were required in the blanket fabrication. Therefore, several welding techniques, such as hot isostatic pressing diffusion bonding, tungsten inner gas welding, electron beam welding and laser beam welding were developed for the fabrication of cooling internals and the assembly of the blanket. In this work, the weldability on CLAM steel by different welding methods and the properties of as-welded and post-weld heat-treated joints were investigated. Meanwhile, the welding schemes and the assembly strategy for TBM fabrication were raised. Many tests and research efforts on scheme feasibility, process standardization, component qualification and blanket assembly were reviewed.

  2. Syllabus in Trade Welding.

    Science.gov (United States)

    New York State Education Dept., Albany. Bureau of Secondary Curriculum Development.

    The syllabus outlines material for a course two academic years in length (minimum two and one-half hours daily experience) leading to entry-level occupational ability in several welding trade areas. Fourteen units covering are welding, gas welding, oxyacetylene welding, cutting, nonfusion processes, inert gas shielded-arc welding, welding cast…

  3. A new technique for the strengthening of aluminum tungsten inert gas weld metals: using carbon nanotube/aluminum composite as a filler metal.

    Science.gov (United States)

    Fattahi, M; Nabhani, N; Rashidkhani, E; Fattahi, Y; Akhavan, S; Arabian, N

    2013-01-01

    The effect of multi-walled carbon nanotube (MWCNT) on the mechanical properties of aluminum multipass weld metal prepared by the tungsten inert gas (TIG) welding process was investigated. High energy ball milling was used to disperse MWCNT in the aluminum powder. Carbon nanotube/aluminum composite filler metal was fabricated for the first time by hot extrusion of ball-milled powders. After welding, the tensile strength, microhardness and MWCNT distribution in the weld metal were investigated. The test results showed that the tensile strength and microhardness of weld metal was greatly increased when using the filler metal containing 1.5 wt.% MWCNT. Therefore, according to the results presented in this paper, it can be concluded that the filler metal containing MWCNT can serve as a super filler metal to improve the mechanical properties of TIG welds of Al and its alloys. Copyright © 2013 Elsevier Ltd. All rights reserved.

  4. ARDENT to develop advanced dosimetric techniques

    CERN Multimedia

    Antonella Del Rosso

    2012-01-01

    Earlier this week, the EU-supported Marie Curie training network ARDENT kicked off at a meeting held at CERN. The overall aim of the project is the development of advanced instrumentation for radiation dosimetry. The applications range from radiation measurements around particle accelerators, onboard commercial flights and in space, to the characterization of radioactive waste and medicine, where accurate dosimetry is of vital importance.   The ARDENT (Advanced Radiation Dosimetry European Network Training) project is both a research and a training programme, which aims at developing new dosimetric techniques while providing 15 Early-Stage Researchers (ESR) with state-of-the-art training. The project, coordinated by CERN, is funded by the European Union with a contribution of about 3.9 million euros over four years. The ARDENT initiative will focus on three main technologies: gas detectors, in particular Gas Electron Multipliers (GEM) and Tissue Equivalent Proportional Counters (TEPC); solid stat...

  5. Study on local vacuum electron beam welding of flange rim

    CERN Document Server

    He Cheng Dan; Ying Lei; Xu Qi Jin

    2002-01-01

    Local vacuum electron beam welding and its application prospect in military and civil industry are introduced. A home made local vacuum electron beam welding is completed. Its main technical parameters and key techniques are also presented

  6. Effect of Austenitic and Austeno-Ferritic Electrodes on 2205 Duplex and 316L Austenitic Stainless Steel Dissimilar Welds

    Science.gov (United States)

    Verma, Jagesvar; Taiwade, Ravindra V.

    2016-11-01

    This study addresses the effect of different types of austenitic and austeno-ferritic electrodes (E309L, E309LMo and E2209) on the relationship between weldability, microstructure, mechanical properties and corrosion resistance of shielded metal arc welded duplex/austenitic (2205/316L) stainless steel dissimilar joints using the combined techniques of optical, scanning electron microscope, energy-dispersive spectrometer and electrochemical. The results indicated that the change in electrode composition led to microstructural variations in the welds with the development of different complex phases such as vermicular ferrite, lathy ferrite, widmanstatten and intragranular austenite. Mechanical properties of welded joints were diverged based on compositions and solidification modes; it was observed that ferritic mode solidified weld dominated property wise. However, the pitting corrosion resistance of all welds showed different behavior in chloride solution; moreover, weld with E2209 was superior, whereas E309L exhibited lower resistance. Higher degree of sensitization was observed in E2209 weld, while lesser in E309L weld. Optimum ferrite content was achieved in all welds.

  7. Laser welding of micro plastic parts

    Science.gov (United States)

    Haberstroh, E.; Hoffmann, W.-M.

    2007-02-01

    Most welding processes for plastics do not meet the demands of micro technology and thus cannot be applied in this innovative industrial sector. One of the few techniques which are applicable in this sector is the laser transmission welding, which has distinctive advantages like low mechanical and thermal load of the joining parts. This makes the laser particularly suitable for the welding of micro plastics parts. Thereby, contour welding is a process variant of laser transmission welding enabling the welding of complex and even three-dimensional weld contours. But so far it has not yet been applied for welding plastics parts of micro scale in the industrial practice. Recent research at the Institute of Plastics Processing (IKV) at the RWTH Aachen University shows the feasibility of this process to weld small and complex micro parts. Good mechanical properties can be achieved. However, it is necessary to apply measures to reduce the formation of flash. Moreover, it can be shown that there is a strong influence of some material parameters on the laser welding process so that some plastics are more suitable than others for the contour welding in micro technology.

  8. Intelligent hybrid system of welding parameters for robotic arc-welding task-level offline programming

    Science.gov (United States)

    Peng, Pai; Tian, Jiansong; Wu, Lin; Dai, Ming

    2000-10-01

    Welding process parameters are indispensable to program arc welding robot. To simplify off-line programming (OLP) for robotic arc welding, we develop an arc welding expert system whcih can generate welding process parameters automatically. Its input data came from the feature database of welding part, which is set up by our feature modeling system. The expert system has become an important module of our RAWTOLPS (Robotic Arc Welding Task-level Off-Line System). It combines case-based reasoning with heuristic rule-based reasoning methods to deal with the welding process design. Moreover, artificial neural networks are introduced to the systems for reasoning and machine learning, and several network modules are developed to learn from welding process database, based on back-propagation neural networks. After some groups of actual welding process data were used to train the network models, several network models are established to both design the welding process and to predict the weld bead shape. Besides the ANN-based learning, cased-based learning are used in the expert system. These two methods have respectively their own characteristics, and can meet qualifications of different users. The experimental data show that the system can accomplish re-learning and expanding of welding process knowledge, and satisfy the command of the off-line programming system.

  9. Virtual Welded - Joint Design Integrating Advanced Materials and Processing Technology

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Zhishang; Ludewig, Howard W.; Babu, S. Suresh

    2005-06-30

    Virtual Welede-Joint Design, a systematic modeling approach, has been developed in this project to predict the relationship of welding process, microstructure, properties, residual stress, and the ultimate weld fatique strength. This systematic modeling approach was applied in the welding of high strength steel. A special welding wire was developed in this project to introduce compressive residual stress at weld toe. The results from both modeling and experiments demonstrated that more than 10x fatique life improvement can be acheived in high strength steel welds by the combination of compressive residual stress from the special welding wire and the desired weld bead shape from a unique welding process. The results indicate a technology breakthrough in the design of lightweight and high fatique performance welded structures using high strength steels.

  10. Monte Carlo Simulation of Alloy Design Techniques: Fracture and Welding Studied Using the BFS Method for Alloys

    Science.gov (United States)

    Bozzolo, Guillermo H.; Good, Brian; Noebe, Ronald D.; Honecy, Frank; Abel, Phillip

    1999-01-01

    Large-scale simulations of dynamic processes at the atomic level have developed into one of the main areas of work in computational materials science. Until recently, severe computational restrictions, as well as the lack of accurate methods for calculating the energetics, resulted in slower growth in the area than that required by current alloy design programs. The Computational Materials Group at the NASA Lewis Research Center is devoted to the development of powerful, accurate, economical tools to aid in alloy design. These include the BFS (Bozzolo, Ferrante, and Smith) method for alloys (ref. 1) and the development of dedicated software for large-scale simulations based on Monte Carlo- Metropolis numerical techniques, as well as state-of-the-art visualization methods. Our previous effort linking theoretical and computational modeling resulted in the successful prediction of the microstructure of a five-element intermetallic alloy, in excellent agreement with experimental results (refs. 2 and 3). This effort also produced a complete description of the role of alloying additions in intermetallic binary, ternary, and higher order alloys (ref. 4).

  11. Effects of conventional welding and laser welding on the tensile strength, ultimate tensile strength and surface characteristics of two cobalt-chromium alloys: a comparative study.

    Science.gov (United States)

    Madhan Kumar, Seenivasan; Sethumadhava, Jayesh Raghavendra; Anand Kumar, Vaidyanathan; Manita, Grover

    2012-06-01

    The purpose of this study was to evaluate the efficacy of laser welding and conventional welding on the tensile strength and ultimate tensile strength of the cobalt-chromium alloy. Samples were prepared with two commercially available cobalt-chromium alloys (Wironium plus and Diadur alloy). The samples were sectioned and the broken fragments were joined using Conventional and Laser welding techniques. The welded joints were subjected to tensile and ultimate tensile strength testing; and scanning electron microscope to evaluate the surface characteristics at the welded site. Both on laser welding as well as on conventional welding technique, Diadur alloy samples showed lesser values when tested for tensile and ultimate tensile strength when compared to Wironium alloy samples. Under the scanning electron microscope, the laser welded joints show uniform welding and continuous molt pool all over the surface with less porosity than the conventionally welded joints. Laser welding is an advantageous method of connecting or repairing cast metal prosthetic frameworks.

  12. Obtaining in an electric arc furnace alloys of the Fe-Mn-Cr-C system and slag destined to the development of welding consumables

    Directory of Open Access Journals (Sweden)

    Lorenzo Perdomo-González

    2018-01-01

    Full Text Available The production of chromium manganese ferroalloys for the use in the development of alloying loads of welding consumables is presented. On the basis of variations in the proportions of the chromium and manganese minerals in the loads, different combinations are established, which allow obtaining multicomponent ferroalloys with composition ranging from 9 to 32 % chromium and from 24 to 65 % manganese. The melting-reduction process is carried out in an electric arc furnace with a graphite crucible and with the presence of coke as a reducing component which guarantees the obtaining of high carbon alloys (5–6 %. The use of the multicomponent ferroalloy in the formulation of welding consumables simplifies and makes cheaper the obtaining of these materials. As result of metallurgical processing, slag formed by the silicon, aluminum, magnesium, manganese and calcium oxides are obtained, which are feasible to use in the production of flux matrices for submerged arc welding process.

  13. Slag-metal reactions during welding: Part II. Theory

    Science.gov (United States)

    Mitra, U.; Eagar, T. W.

    1991-02-01

    A kinetic model is developed to describe the transfer of alloying elements between the slag and the metal during flux-shielded welding. The model accounts for changes in alloy recovery based on the geometry of the resulting weld bead. It also distinguishes compositional differences between single-pass and multiple-pass weld beads. It is further shown that the final weld metal oxygen content is directly related to the weld solidification time as well as the type of flux used.

  14. Laser welding of selected aerospace alloys

    Science.gov (United States)

    Ebadan, Gracie E.

    The study was aimed at developing an understanding of the microstructural effects of the laser welding process on the alloys, and assessing the structural integrity of the resultant welds. The effect of laser processing parameters such as laser power, laser beam traverse speed, lens focal length, and the manipulation of these parameters on the welding efficiency and weld area integrity was also investigated. Other tasks within the project included a study on the possibility of using an anodic film to enhance the laser weld ability of Al 6061. Finally, attempts were made to identify phases observed in the weld area of the composite materials. Nimonics C263 and PE11 exhibited laser welds free of cracks and porosity. The difference in composition between the two alloys did not result in any significant dissimilarities in their response to the laser welding process. The welds in both alloys exhibited a fine columnar dendritic microstructure, and while carbides were observed in the interdendritic regions of the welds, electron optical analysis did not reveal any gamma' precipitates in this region. It was concluded that for the welding of thin gage materials above a threshold laser power the resultant welding efficiency shows a greater dependence on laser beam mode, and laser spot size, than on laser power, and beam traverse speed. Aluminum 6061 was not easily welded with a laser in its as received form, and the welds showed some degree of porosity. Anodizing was found to improve the welding efficiency in this material. While the presence of an anodic film on the metal surface increased the welding efficiency of the alloy, no relationship was found between the thickness of the anodic film and welding efficiency in the range of film thicknesses investigated. Weld regions were observed to be cellular dendritic in structure, with narrow heat affected zones. No precipitates or low melting point phases could be identified in the weld region. Melt zones were successfully

  15. Pulsed welding plasma source

    Science.gov (United States)

    Knyaz'kov, A.; Pustovykh, O.; Verevkin, A.; Terekhin, V.; Shachek, A.; Tyasto, A.

    2016-04-01

    It is shown that in order to form the current pulse of a near rectangular shape, which provides conversion of the welding arc into a dynamic mode, it is rational to connect a forming element made on the basis of an artificial forming line in series to the welding DC circuit. The paper presents a diagram of a pulsed device for welding with a non-consumable electrode in argon which was developed using the forming element. The conversion of the arc into the dynamic mode is illustrated by the current and voltage oscillograms of the arc gap and the dynamic characteristic of the arc within the interval of one pulse generation time in the arc gap. The background current travels in the interpulse interval.

  16. Study of the effect of low-power pulse laser on arc plasma and magnesium alloy target in hybrid welding by spectral diagnosis technique

    Science.gov (United States)

    Liu, Liming; Hao, Xinfeng

    2008-10-01

    In order to study the effect of laser pulses on arc plasma and target metal in the hybrid welding process, the spectra of the plasmas in the welding process of magnesium alloys are analysed in this paper. The acquisition system of plasma spectra is set up and the spectral lines of welding plasma are acquired. Compared with tungsten-inert gas (TIG) welding, the intensities of the spectral lines of magnesium increase sharply while those of Ar decrease for strong evaporation and ionization of magnesium alloys in low-power laser/arc hybrid welding. The electron temperature and density are estimated by the Boltzmann plot method and the Stark broadening effect. The result shows that the electron temperature of arc plasma in the hybrid welding process is much lower than that in TIG welding, especially in the laser beam-affected zone. In contrast, the electron density of the plasma is enhanced. The influences of laser parameters on electron temperature are also studied. The changes in electron temperature and density indicate that the effect of laser pulse on the target metal is the dominant factor influencing the electron temperature and density in low-power laser/arc hybrid welding.

  17. Simulation of inverse heat conduction problems in fusion welding with extended analytical heat source models

    Science.gov (United States)

    Karkhin, V. A.; Pittner, A.; Schwenk, C.; Rethmeier, M.

    2011-06-01

    The paper presents bounded volume heat sources and the corresponding functional-analytical expressions for the temperature field. The power density distributions considered here are normal, exponential and parabolic. The sources model real heat sources like the welding arc, laser beam, electron beam, etc., the convection in the weld pool as well as the latent heat due to fusion and solidification. The parameters of the heat source models are unknown a priori and have to be evaluated by solving an inverse heat conduction problem. The functional-analytical technique for calculating 3D temperature fields in butt welding is developed. The proposed technique makes it possible to reduce considerably the total time for data input and solution. It is demonstrated with an example of laser beam welding of steel plates.

  18. Welded joints integrity analysis and optimization for fiber laser welding of dissimilar materials

    Science.gov (United States)

    Ai, Yuewei; Shao, Xinyu; Jiang, Ping; Li, Peigen; Liu, Yang; Liu, Wei

    2016-11-01

    Dissimilar materials welded joints provide many advantages in power, automotive, chemical, and spacecraft industries. The weld bead integrity which is determined by process parameters plays a significant role in the welding quality during the fiber laser welding (FLW) of dissimilar materials. In this paper, an optimization method by taking the integrity of the weld bead and weld area into consideration is proposed for FLW of dissimilar materials, the low carbon steel and stainless steel. The relationships between the weld bead integrity and process parameters are developed by the genetic algorithm optimized back propagation neural network (GA-BPNN). The particle swarm optimization (PSO) algorithm is taken for optimizing the predicted outputs from GA-BPNN for the objective. Through the optimization process, the desired weld bead with good integrity and minimum weld area are obtained and the corresponding microstructure and microhardness are excellent. The mechanical properties of the optimized joints are greatly improved compared with that of the un-optimized welded joints. Moreover, the effects of significant factors are analyzed based on the statistical approach and the laser power (LP) is identified as the most significant factor on the weld bead integrity and weld area. The results indicate that the proposed method is effective for improving the reliability and stability of welded joints in the practical production.

  19. Development of High Heat Input Welding Offshore Steel as Normalized Condition

    Science.gov (United States)

    Deng, Wei; Qin, Xiaomei

    The heavy plate used for offshore structure is one of the important strategic products. In recent years, there is an increasing demand for heavy shipbuilding steel plate with excellent weldability in high heat input welding. During the thermal cycle, the microstructure of the heat affected zone (HAZ) of plates was damaged, and this markedly reduced toughness of HAZ. So, how to improve the toughness of HAZ has been a key subject in the fields of steel research. Oxide metallurgy is considered as an effective way to improve toughness of HAZ, because it could be used to retard grain growth by fine particles, which are stable at the high temperature.The high strength steel plate, which satisfies the low temperature specification, has been applied to offshore structure. Excellent properties of the plates and welded joints were obtained by oxide metallurgy technology, latest controlled rolling and accelerated cooling technology using Ultra-Fast Cooling (an on-line accelerated cooling system). The 355MPa-grade high strength steel plates with normalizing condition were obtained, and the steels have excellent weldability with heat input energy of 79 287kJ/cm, and the nil ductility transition (NDT) temperature was -70°C, which can satisfy the construction of offshore structure in cold regions.

  20. Analysis of factors affecting fractures of rails welded by alumino-thermic welding

    Directory of Open Access Journals (Sweden)

    Sergejs MIKHAYLOVS

    2008-01-01

    Full Text Available On Latvian Railway the use of the alumino-thermic welding is widespread using the Elektro-Thermit Company technology. Today it is a basic method for rail joints on railway switches. The analysis of the metal structure in the thermic welding and in the thermic welded zone of rails showed that the weld metal had inclusions small pores and nonmetallics. Pores and nonmetallics are not reduce hardness but it is concentrators of stresses and sources of cracks development.

  1. Electron beam welding of iridium heat source capsules

    Science.gov (United States)

    Mustaleski, Thomas M.; Yearwood, J. Cecil; Burgan, Clyde E.; Green, L. A.

    1991-01-01

    The development of the welding procedures for the production of DOP-26 iridium alloy cups for heat source encapsulation is described. All the final assembly welds were made using the electron beam welding process. The welding of the 0.13-mm weld shield required the use of computer controlled X-Y table and a run-off tab. Welding of the frit vent to the cup required that a laser weld be made to hold the frit assembly edges together for the final electron beam weld. Great care is required in tooling design and beam placement to achieve acceptable results. Unsuccessful attempts to use laser beam welding for heat shield butt weld are discussed.

  2. Pulsed Magnetic Welding for Advanced Core and Cladding Steel

    Energy Technology Data Exchange (ETDEWEB)

    Cao, Guoping [Univ. of Wisconsin, Madison, WI (United States); Yang, Yong [Univ. of Florida, Gainesville, FL (United States)

    2013-12-19

    To investigate a solid-state joining method, pulsed magnetic welding (PMW), for welding the advanced core and cladding steels to be used in Generation IV systems, with a specific application for fuel pin end-plug welding. As another alternative solid state welding technique, pulsed magnetic welding (PMW) has not been extensively explored on the advanced steels. The resultant weld can be free from microstructure defects (pores, non-metallic inclusions, segregation of alloying elements). More specifically, the following objectives are to be achieved: 1. To design a suitable welding apparatus fixture, and optimize welding parameters for repeatable and acceptable joining of the fuel pin end-plug. The welding will be evaluated using tensile tests for lap joint weldments and helium leak tests for the fuel pin end-plug; 2 Investigate the microstructural and mechanical properties changes in PMW weldments of proposed advanced core and cladding alloys; 3. Simulate the irradiation effects on the PWM weldments using ion irradiation.

  3. Experimental analysis of cut welding in aluminium

    DEFF Research Database (Denmark)

    Dorph, Pernille; De Chiffre, Leonardo; Bay, Niels

    1993-01-01

    Cut welding is a newly developed cold pressure welding process. In the present work, an experimental investigation was carried out analyzing the mechanisms involved in cut welding of a block to a strip. Experiments were carried out in technically pure aluminium. The investigation has involved...... tensile testing and metallographic investigations of the welds. The results show that this variant of cut welding is a very reproducible process giving a weld strength equal to 30-40% the strength of the parent material. The experiments have shown that the reason for this relatively low strength...... is an uneven pressure distribution along the weld due to a wave formed during sliding. Attempts to alter the material flow during sliding are presented....

  4. Numerical Simulation of Duplex Steel Multipass Welding

    Directory of Open Access Journals (Sweden)

    Giętka T.

    2016-12-01

    Full Text Available Analyses based on FEM calculations have significantly changed the possibilities of determining welding strains and stresses at early stages of product design and welding technology development. Such an approach to design enables obtaining significant savings in production preparation and post-weld deformation corrections and is also important for utility properties of welded joints obtained. As a result, it is possible to make changes to a simulated process before introducing them into real production as well as to test various variants of a given solution. Numerical simulations require the combination of problems of thermal, mechanical and metallurgical analysis. The study presented involved the SYSWELD software-based analysis of GMA welded multipass butt joints made of duplex steel sheets. The analysis of the distribution of stresses and displacements were carried out for typical welding procedure as during real welding tests.

  5. Elementary TIG Welding Skills.

    Science.gov (United States)

    Pierson, John E., III

    The text was prepared to help deaf students develop the skills needed by an employed welder. It uses simplified language and illustrations to present concepts which should be reinforced by practical experience with welding skills. Each of the 12 lessons contains: (1) an information section with many illustrations which presents a concept or…

  6. Design of Friction Stir Spot Welding Tools by Using a Novel Thermal-Mechanical Approach.

    Science.gov (United States)

    Su, Zheng-Ming; Qiu, Qi-Hong; Lin, Pai-Chen

    2016-08-09

    A simple thermal-mechanical model for friction stir spot welding (FSSW) was developed to obtain similar weld performance for different weld tools. Use of the thermal-mechanical model and a combined approach enabled the design of weld tools for various sizes but similar qualities. Three weld tools for weld radii of 4, 5, and 6 mm were made to join 6061-T6 aluminum sheets. Performance evaluations of the three weld tools compared fracture behavior, microstructure, micro-hardness distribution, and welding temperature of welds in lap-shear specimens. For welds made by the three weld tools under identical processing conditions, failure loads were approximately proportional to tool size. Failure modes, microstructures, and micro-hardness distributions were similar. Welding temperatures correlated with frictional heat generation rate densities. Because the three weld tools sufficiently met all design objectives, the proposed approach is considered a simple and feasible guideline for preliminary tool design.

  7. Comparative microscopic study of human and rat lungs after overexposure to welding fume.

    Science.gov (United States)

    Antonini, James M; Roberts, Jenny R; Schwegler-Berry, Diane; Mercer, Robert R

    2013-11-01

    Welding is a common industrial process used to join metals and generates complex aerosols of potentially hazardous metal fumes and gases. Most long-time welders experience some type of respiratory disorder during their time of employment. The use of animal models and the ability to control the welding fume exposure in toxicology studies have been helpful in developing a better understanding of how welding fumes affect health. There are no studies that have performed a side-by-side comparison of the pulmonary responses from an animal toxicology welding fume study with the lung responses associated with chronic exposure to welding fume by a career welder. In this study, post-mortem lung tissue was donated from a long-time welder with a well-characterized work background and a history of extensive welding fume exposure. To simulate a long-term welding exposure in an animal model, Sprague-Dawley rats were treated once a week for 28 weeks by intratracheal instillation with 2mg of a stainless steel, hard-surfacing welding fume. Lung tissues from the welder and the welding fume-treated rats were examined by light and electron microscopy. Pathological analysis of lung tissue collected from the welder demonstrated inflammatory cell influx and significant pulmonary injury. The poor and deteriorating lung condition observed in the welder examined in this study was likely due to exposure to very high levels of potentially toxic metal fumes and gases for a significant number of years due to work in confined spaces. The lung toxicity profile for the rats treated with welding fume was similar. For tissue samples from both the welder and treated rats, welding particle accumulations deposited and persisted in lung structures and were easily visualized using light microscopic techniques. Agglomerates of deposited welding particles mostly were observed within lung cells, particularly alveolar macrophages. Analysis of individual particles within the agglomerates showed that these

  8. Evaluation of Residual Stress Measurements Before and After Post-Weld Heat Treatment in the Weld Repairs

    Science.gov (United States)

    Pardowska, Anna M.; Price, John W. H.; Finlayson, Trevor R.; Ibrahim, R.

    2010-11-01

    Welding repairs are increasingly a structural integrity concern for aging pressure vessel and piping components. It has been demonstrated that the residual stress distribution near repair welds can be drastically different from that of the original weld. Residual stresses have a significant effect on the lifetime performance of a weld, and a reduction of these stresses is normally desirable. The aim of this paper is to investigate residual stresses in various weld repair arrangements using the non-destructive neutron diffraction technique. This research is focused on characterization of the residual stress distribution: (i) in the original weld; (ii) in a shallow toe weld repair; and (iii) after conventional post-weld heat treatment. The focus of the measurements is on the values of the subsurface strain/stress variations across the weld.

  9. Thermomechanical Modelling of Resistance Welding

    DEFF Research Database (Denmark)

    Bay, Niels; Zhang, Wenqi

    2007-01-01

    The present paper describes a generic programme for analysis, optimization and development of resistance spot and projection welding. The programme includes an electrical model determining electric current and voltage distribution as well as heat generation, a thermal model calculating heat...

  10. Laser Peening Effects on Friction Stir Welding

    Science.gov (United States)

    Hatamleh, Omar

    2011-01-01

    Friction Stir Welding (FSW) is a welding technique that uses frictional heating combined with forging pressure to produce high strength bonds. It is attractive for aerospace applications. Although residual stresses in FSW are generally lower when compared to conventional fusion welds, recent work has shown that significant tensile residual stresses can be present in the weld after fabrication. Therefore, laser shock peening was investigated as a means of moderating the tensile residual stresses produced during welding. This slide presentation reviews the effect of Laser Peening on the weld, in tensile strength, strain, surface roughness, microhardness, surface wear/friction, and fatigue crack growth rates. The study concluded that the laser peening process can result in considerable improvement to crack initiaion, propagation and mechanical properties in FSW.

  11. Femtosecond fiber laser welding of dissimilar metals.

    Science.gov (United States)

    Huang, Huan; Yang, Lih-Mei; Bai, Shuang; Liu, Jian

    2014-10-01

    In this paper, welding of dissimilar metals was demonstrated for the first time, to the best of our knowledge, by using a high-energy high-repetition-rate femtosecond fiber laser. Metallurgical and mechanical properties were investigated and analyzed under various processing parameters (pulse energy, repetition rate, and welding speed). Results showed that the formation of intermetallic brittle phases and welding defects could be effectively reduced. Strong welding quality with more than 210 MPa tensile strength for stainless steel-aluminum and 175 MPa tensile strength for stainless steel-magnesium has been demonstrated. A minimal heat affected zone and uniform and homogenous phase transformation in the welding region have been demonstrated. This laser-welding technique can be extended for various applications in semiconductor, automobile, aerospace, and biomedical industries.

  12. Tool For Friction Stir Tack Welding of Aluminum Alloys

    Science.gov (United States)

    Bjorkman, Gerald W.; Dingler, Johnny W.; Loftus, Zachary

    2003-01-01

    A small friction-stir-welding tool has been developed for use in tack welding of aluminum-alloy workpieces. It is necessary to tack-weld the workpieces in order to hold them together during friction stir welding because (1) in operation, a full-size friction-stir-welding tool exerts a large force that tends to separate the workpieces and (2) clamping the workpieces is not sufficient to resist this force. It is possible to tack the pieces together by gas tungsten arc welding, but the process can be awkward and time-consuming and can cause sufficient damage to necessitate rework. Friction stir tack welding does not entail these disadvantages. In addition, friction stir tack welding can be accomplished by use of the same automated equipment (except for the welding tool) used in subsequent full friction stir welding. The tool for friction stir tack welding resembles the tool for full friction stir welding, but has a narrower shoulder and a shorter pin. The shorter pin generates a smaller workpiece-separating force so that clamping suffices to keep the workpieces together. This tool produces a continuous or intermittent partial-penetration tack weld. The tack weld is subsequently consumed by action of the larger tool used in full friction stir welding tool.

  13. Advanced Welding Tool

    Science.gov (United States)

    1982-01-01

    Accutron Tool & Instrument Co.'s welder was originally developed as a tool specifically for joining parts made of plastic or composite materials in any atmosphere to include the airless environment of space. Developers decided on induction or magnetic heating to avoid causing deformation and it also can be used with almost any type of thermoplastic material. Induction coil transfers magnetic flux through the plastic to a metal screen that is sandwiched between the sheets of plastic to be joined. When welder is energized, alternating current produces inductive heating on the screen causing the adjacent plastic surfaces to melt and flow into the mesh, creating a bond on the total surface area. Dave Brown, owner of Great Falls Canoe and Kayak Repair, Vienna, VA, uses a special repair technique based on operation of the Induction Toroid Welder to fix canoes. Whitewater canoeing poses the problem of frequent gashes that are difficult to repair. The main reason is that many canoes are made of plastics. The commercial Induction model is a self-contained, portable welding gun with a switch on the handle to regulate the temperature of the plastic melting screen. Welder has a broad range of applications in the automobile, appliance, aerospace and construction industries.

  14. Convection in arc weld pools

    Energy Technology Data Exchange (ETDEWEB)

    Oreper, G.M.; Eagar, T.W.; Szekely, J.

    1982-11-01

    A mathematical model was developed to account for convection and temperature distributions in stationary arc weld pools driven by buoyancy, electromagnetic and surface tension forces. It is shown that the electromagnetic and surface tension forces dominate the flow behavior. In some cases, these forces produce double circulation loops, which are indirectly confirmed by experimental measurements of segregation in the weld pool. It is also shown that the surface tension driven flows are very effective in dissipating the incident energy flux on the pool surface which, in turn, reduces the vaporization from the weld pool.

  15. Plasticity Theory of Fillet Welds

    DEFF Research Database (Denmark)

    Hansen, Thomas

    2005-01-01

    This paper deals with simple methods for calculation of fillet welds based on the theory of plasticity. In developing the solutions the lower-bound theorem is used. The welding material and parts of the base material are subdivided into triangular regions with homogeneous stress fields; thereby...... a safe and statically admissible stress distribution is established. The plasticity solutions are compared with tests carried out at the Engineering Academy of Denmark, Lyngby, in the early nineties, and old fillet weld tests. The new failure conditions are in very good agreement with the yield load...

  16. Analysis of the Corrosion Behavior of an A-TIG Welded SS 409 Weld Fusion Zone

    Science.gov (United States)

    Vidyarthy, R. S.; Dwivedi, D. K.

    2017-11-01

    AISI 409 (SS 409) ferritic stainless steel is generally used as the thick gauge section in freight train wagons, in ocean containers, and in sugar refinery equipment. Activating the flux tungsten inert gas (A-TIG) welding process can reduce the welding cost during fabrication of thick sections. However, corrosion behavior of the A-TIG weld fusion zone is a prime concern for this type of steel. In the present work, the effect of the A-TIG welding process parameters on the corrosion behavior of a weld fusion zone made of 8-mm-thick AISI 409 ferritic stainless-steel plate has been analyzed. Potentiodynamic polarization tests were performed to evaluate the corrosion behavior. The maximum corrosion potential ( E corr) was shown by the weld made using a welding current of 215 A, a welding speed of 95 mm/min, and a flux coating density of 0.81 mg/cm2. The minimum E corr was observed in the weld made using a welding current of 190 A, a welding speed of 120 mm/min, and a flux coating density of 1.40 mg/cm2. The current study also presents the inclusive microstructure-corrosion property relationships using the collective techniques of scanning electron microscopy, energy-dispersive x-ray spectroscopy, and x-ray diffraction.

  17. Fatique Resistant, Energy Efficient Welding Program, Final Technical Report

    Energy Technology Data Exchange (ETDEWEB)

    Egland, Keith; Ludewig, Howard

    2006-05-25

    The program scope was to affect the heat input and the resultant weld bead geometry by synchronizing robotic weave cycles with desired pulsed waveform shapes to develop process parameters relationships and optimized pulsed gas metal arc welding processes for welding fatique-critical structures of steel, high strength steel, and aluminum. Quality would be addressed by developing intelligent methods of weld measurement that accurately predict weld bead geometry from process information. This program was severely underfunded, and eventually terminated. The scope was redirected to investigate tandem narrow groove welding of steel butt joints during the one year of partial funding. A torch was designed and configured to perform a design of experiments of steel butt weld joints that validated the feasability of the process. An initial cost model estimated a 60% cost savings over conventional groove welding by eliminating the joint preparation and reducing the weld volume needed.

  18. Predicting the combined effect of TiO{sub 2} nano-particles and welding input parameters on the hardness of melted zone in submerged arc welding by fuzzy logic

    Energy Technology Data Exchange (ETDEWEB)

    Aghakhani, Masood; Ghaderi, Mohammad Reza; Jalilian, Maziar Mahdipour; Derakhshan, Ali Ashraf [Razi University, Kermanshah (Iran, Islamic Republic of)

    2013-07-15

    Submerged arc welding (SAW) is a high-quality arc welding process used in heavy industries for welding thick plates. In this process, selecting appropriate values for the input parameters is required for high productivity and cost effectiveness. A very important weld quality characteristic affected by welding input parameters is the hardness of melted zone (HMZ). This paper reports the applicability of fuzzy logic (FL) to predict HMZ in the SAW process which is affected by the combined effect of TiO{sub 2} nano-particles and welding input parameters. The arc voltage, welding current, welding speed, contact tip-to-plate distance, and TiO{sub 2} nano-particles were used as input parameters and HMZ as the response to develop FL model. A five-level five-factor central composite rotatable design (CCRD) was used in the experiments to generate experimental data. Experiments were performed, and HMZs were measured. The predicted results from FL were compared with the experimental data. The correlation factor value obtained was 99.99% between the measured and predicted values of HMZ. The results showed that FL is an accurate and reliable technique for predicting HMZ because of its low error rate.

  19. Effect of A-TIG Welding Process on the Weld Attributes of Type 304LN and 316LN Stainless Steels

    Science.gov (United States)

    Vasudevan, M.

    2017-03-01

    The specific activated flux has been developed for enhancing the penetration performance of TIG welding process for autogenous welding of type 304LN and 316LN stainless steels through systematic study. Initially single-component fluxes were used to study their effect on depth of penetration and tensile properties. Then multi-component activated flux was developed which was found to produce a significant increase in penetration of 10-12 mm in single-pass TIG welding of type 304LN and 316LN stainless steels. The significant improvement in penetration achieved using the activated flux developed in the present work has been attributed to the constriction of the arc and as well as reversal of Marangoni flow in the molten weld pool. The use of activated flux has been found to overcome the variable weld penetration observed in 316LN stainless steel with TIG welds compared to that of the welds produced by conventional TIG welding on the contrary the transverse strength properties of the 304LN and 316LN stainless steel welds produced by A-TIG welding exceeded the minimum specified strength values of the base metals. Improvement in toughness values were observed in 316LN stainless steel produced by A-TIG welding due to refinement in the weld microstructure in the region close to the weld center. Thus, activated flux developed in the present work has greater potential for use during the TIG welding of structural components made of type 304LN and 316LN stainless steels.

  20. Process Simulation of Resistance Weld Bonding and Automotive Light-weight Materials

    DEFF Research Database (Denmark)

    Zhang, Wenqi; Chergui, Azeddine; Nielsen, Chris Valentin

    This paper presents the latest developments in numerical simulation of resistance welding especially with the new functions for simulation of microstructures, weld bonding and spot welding of new light-weight materials. The fundamental functions in SORPAS® are built on coupled modeling...... of mechanical, electrical, thermal and metallurgical processes, which are essential for simulation of resistance welding process to predict the welding results and evaluate the weldability of materials. These functions have been further extended with new functions for optimization of welding process parameters...... and predicting welding process window, for weld planning with optimal welding parameter settings, and for modeling microstructures and hardness distribution after welding. Latest developments have been made on simulation of resistance welding with nonconductive materials for applications in weld bonding...

  1. Study and development of solid fluxes for gas tungsten arc welding applied to titanium and its alloys and stainless steels; Etude et developpement des flux solides en vue d'application en soudage ATIG applique au titane et ses alliages ainsi qu'aux aciers inoxydables

    Energy Technology Data Exchange (ETDEWEB)

    Perry, N

    2000-06-15

    Gas Tungsten Arc Welding uses an electric arc between the refractory tungsten electrode and the plates to be welded under an argon shielding gas. As a result, the joint quality is excellent, no pollution nor defects are to be feared, consequently this process is used in nuclear, aeronautic, chemical and food industries. Despite of this good qualities, GTAW is limited because of, on the one side, a poor penetrating weld pool and, on the other side, a week productivity rate. Indeed, up to 3 mm thick plates, machining and filler metal is needed. Multiple runs increase the defect's risks, the manufactory time and increase the deformations and the heat affected zone. The goal of this study is to break through this limits without any device investment. Active GTA welding (or ATIG) is a new technique with GTA device and an activating flux to be spread on the upper plate before welding. The arc, by plasma electrochemical equilibrium modifications, and the pool with the inner connective flows inversion, allow 7 mm thick joints in one run without edges machining or filler metal for both stainless steel and titanium alloys. This manuscript describes the development of these fluxes, highlights the several phenomena and presents the possibilities of this new process. This work, in collaboration with B.S.L. industries, leads to two flux formulations (stainless steel and titanium alloys) now in a commercial phase with CASTOLIN S.A. Moreover, B.S.L.industries produces a pressure device (nitrate column) with the ATIG process using more than 2800 ATIG welds. (author)

  2. Characterization of duplex stainless steel weld metals obtained by hybrid plasma-gas metal arc welding

    Directory of Open Access Journals (Sweden)

    Koray Yurtisik

    2013-09-01

    Full Text Available Despite its high efficiency, autogenous keyhole welding is not well-accepted for duplex stainless steels because it causes excessive ferrite in as-welded duplex microstructure, which leads to a degradation in toughness and corrosion properties of the material. Combining the deep penetration characteristics of plasma arc welding in keyhole mode and metal deposition capability of gas metal arc welding, hybrid plasma - gas metal arc welding process has considered for providing a proper duplex microstructure without compromising the welding efficiency. 11.1 mm-thick standard duplex stainless steel plates were joined in a single-pass using this novel technique. Same plates were also subjected to conventional gas metal arc and plasma arc welding processes, providing benchmarks for the investigation of the weldability of the material. In the first place, the hybrid welding process enabled us to achieve less heat input compared to gas metal arc welding. Consequently, the precipitation of secondary phases, which are known to be detrimental to the toughness and corrosion resistance of duplex stainless steels, was significantly suppressed in both fusion and heat affected zones. Secondly, contrary to other keyhole techniques, proper cooling time and weld metal chemistry were achieved during the process, facilitating sufficient reconstructive transformation of austenite in the ferrite phase.

  3. Distortion Control during Welding

    OpenAIRE

    Akbari Pazooki, A.M.

    2014-01-01

    The local material expansion and contraction involved in welding result in permanent deformations or instability i.e., welding distortion. Considerable efforts have been made in controlling welding distortion prior to, during or after welding. Thermal Tensioning (TT) describes a group of in-situ methods to control welding distortion. In these methods local heating and/or cooling strategies are applied during welding. Additional heating and/or cooling sources can be implemented either stationa...

  4. Welding process modelling and control

    Science.gov (United States)

    Romine, Peter L.; Adenwala, Jinen A.

    1993-01-01

    The research and analysis performed, and software developed, and hardware/software recommendations made during 1992 in development of the PC-based data acquisition system for support of Welding Process Modeling and Control is reported. A need was identified by the Metals Processing Branch of NASA Marshall Space Flight Center, for a mobile data aquisition and analysis system, customized for welding measurement and calibration. Several hardware configurations were evaluated and a PC-based system was chosen. The Welding Measurement System (WMS) is a dedicated instrument, strictly for the use of data aquisition and analysis. Although the WMS supports many of the functions associated with the process control, it is not the intention for this system to be used for welding process control.

  5. The IGISOL technique : three decades of developments

    NARCIS (Netherlands)

    Moore, I.D.; Dendooven, Peter; Ärje, J.

    The Ion Guide Isotope SeparatorOn-Line (IGISOL) technique, conceived in the early 1980s as a novel variation to the helium-jet method, has been used to provide radioactive ion beams of short-lived exotic nuclei for fundamental nuclear structure research and applications for three decades. This

  6. Big data for development : applications and techniques

    NARCIS (Netherlands)

    Ali, Anwaar; Qadir, Junaid; ur Rasool, Raihan; Sathiaseelan, Arjuna; Zwitter, Andrej; Crowcroft, Jon

    2016-01-01

    With the explosion of social media sites and proliferation of digital computing devices and Internet access, massive amounts of public data is being generated on a daily basis. Efficient techniques/algorithms to analyze this massive amount of data can provide near real-time information about

  7. Microstructural evolutions of friction stir welded F82H steel for fusion applications

    Energy Technology Data Exchange (ETDEWEB)

    Noh, Sang Hoon; Shim, Jae Won; Kim, Tae Kyu [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Tani Gawa, Hiro Yasu [JAEA, Rokasho (Japan); Fujii, Hideto Shi [Osaka Univ., Osaka (Japan); Kim Ura, Aki Hiko [Kyoto Univ., Kyoto (Japan)

    2012-10-15

    A blanket is the most important component functionalized as plasma confining, tritium breeding, heat exchanging, and irradiation shielding from severe thermo neutron loads in a fusion reactor. Its structure consists of first walls, side walls, a back board, and coolant channels mainly made of reduced activation ferritic/martensitic (RAFM) steel, which is the most promising candidate as a structural material for fusion reactors. To fabricate this blanket structure, some welding and joining methods have being carefully applied. However, when fusion welding, such as tungsten inert gas (TIG) welding, electron beam, and laser welding was performed between F82H and itself, the strength of welds significantly deteriorated due to the development of {delta} ferrite and precipitate dissolution. Post welding heat treatment (PWHT) should be followed to restore the initial microstructure. Nevertheless, microstructural discontinuity inevitably occurs between the weld metal, heat affected zone and base metal and this seriously degrades the entire structural stability under pulsed operation at high temperature in test blanket module (TBM). A phase transformation can also be an issue to be solved, which leads to a difficult replacement of the blanket module. Therefore, a reliable and field applicable joining technique should be developed not to accompany with PWHT after the joining process. Friction stir welding (FSW) is one of the solid state processes that does not create a molten zone at the joining area, so the degradation of the featured microstructures may be avoided or minimized. In this study, FSW was employed to join F82H steels to develop a potential joining technique for RAFM steel. The microstructural features on the joint region were investigated to evaluate the applicability of the FSW.

  8. Genesis of the microstructures during friction stir welding of aluminium alloys of the series 2000 and 5000 and resulting mechanical behavior; Genese des microstructures lors du soudage par friction malaxage d'alliages d'aluminium de la serie 2000 et 5000 et comportement mecanique resultant

    Energy Technology Data Exchange (ETDEWEB)

    Genevois, C.

    2004-09-15

    The 2024 alloy (Al-Cu-Mg) is used for minimizing the weight of structural components in the transportation industry. However, this alloy is not easy to weld by traditional techniques. Friction stir welding (FSW) is a recently developed solid state process which removes the solidification defects. In this study, the microstructures of FSW welds of this alloy were finely characterized by SAXS, DSC, TEM, SEM, EBSD and optical microscopy. In order to highlight the interactions between deformation, precipitation and recrystallization, which all take place during the welding of the 2024 alloy, model experiments were carried out as well as a comparative study between the alloys 5251 and 2024. The combination of the welding characterisation and the model experiments allow to define the metallurgical phenomena controlling the mechanical strength of the welded joints and their microstructure. In addition, a detailed characterisation of the mechanical behaviour of the welded joints was carried out, validated by a finite element model. (author)

  9. Contamination and solid state welds.

    Energy Technology Data Exchange (ETDEWEB)

    Mills, Bernice E.

    2007-05-01

    Since sensitivity to contamination is one of the verities of solid state joining, there is a need for assessing contamination of the part(s) to be joined, preferably nondestructively while it can be remedied. As the surfaces that are joined in pinch welds are inaccessible and thus provide a greater challenge, most of the discussion is of the search for the origin and effect of contamination on pinch welding and ways to detect and mitigate it. An example of contamination and the investigation and remediation of such a system is presented. Suggestions are made for techniques for nondestructive evaluation of contamination of surfaces for other solid state welds as well as for pinch welds. Surfaces that have good visual access are amenable to inspection by diffuse reflection infrared Fourier transform (DRIFT) spectroscopy. Although other techniques are useful for specific classes of contaminants (such as hydrocarbons), DRIFT can be used most classes of contaminants. Surfaces such as the interior of open tubes or stems that are to be pinch welded can be inspected using infrared reflection spectroscopy. It must be demonstrated whether or not this tool can detect graphite based contamination, which has been seen in stems. For tubes with one closed end, the technique that should be investigated is emission infrared spectroscopy.

  10. Development of API 5L X80 pipes by UOE process, using SAW (Submerged Arc Welding) welding; Desenvolvimento de tubos API 5L X80 pelo processo UOE, utilizando soldagem SAW (Submerged Arc Welding)

    Energy Technology Data Exchange (ETDEWEB)

    Kojima, Sergio S.; Roza, Juliana E. [Tenaris Confab, Pindamonhangaba, SP (Brazil)

    2004-07-01

    High strength API X80 grade pipe constitute a new class of product manufactured either by the TMCP or TMCR process, which aim to obtain high values of yield strength, tensile strength and good toughness required by line pipe specifications, which are becoming more rigorous everyday. High strength steels have many advantages, due to low overall project costs associated principally with reduced wall thickness causing low transport and pipe installation costs. X80 material can be used in Onshore and Offshore constructions. This paper deals with X80 material produced by TMCR and welded by the longitudinal SAW process (submerged arc welding) by TENARIS CONFAB. The material was characterized by conducting tensile and Charpy impact tests, hardness measurements and metallographic analysis. The mechanical properties and microstructural features of the material are discussed and the advantages of using X80 grade steels in offshore projects are highlighted. The results obtained were found to be in accordance with the requirements of API 5L Standard (2000), 42nd edition. (author)

  11. Modelling of ultrasonic impact treatment (UIT of welded joints and its effect on fatigue strength

    Directory of Open Access Journals (Sweden)

    K.L. Yuan

    2015-10-01

    Full Text Available Ultrasonic impact treatment (UIT is a remarkable post-weld technique applying mechanical impacts in combination with ultrasound into the welded joints. In the present work, a 3D simulation method including welding simulation, numerical modelling of UIT-process and an evaluation of fatigue crack growth has been developed. In the FE model, the actual treatment conditions and local mechanical characteristics due to acoustic softening are set as input parameters. The plastic deformation and compressive stress layer are found to be more pronounced when acoustic softening takes place. The predicted internal residual stress distributions of welded joint before and after UIT are compared with experimental results, showing a fairly good agreement with each other. Finally, simulated results of fatigue crack growth in various residual stress fields are well compared with test results, so that the proposed model may provide an effective tool to simulate UIT-process in engineering structures.

  12. Optimization in Friction Stir Welding - With Emphasis on Thermo-mechanical Aspects

    DEFF Research Database (Denmark)

    Tutum, Cem Celal

    This book deals with the challenging multidisciplinary task of combining variant thermal and thermo-mechanical simulations for the manufacturing process of friction stir welding (FSW) with numerical optimization techniques in the search for optimal process parameters. The FSW process......-mechanical models of the process were developed to simulate temperature and stress evolution during welding and subsequent cooling, i.e. eventually leading to the residual stress state and reduced mechanical properties, as well as to predict the final weld's load carrying capacity. These models were finally...... combined with classical single-objective and evolutionary multi-objective optimization algorithms (i.e. SQP and NSGA-II), to find the optimum process parameters (heat input, rotational and traverse welding speeds) that would result in favorable thermo-mechanical conditions for the process....

  13. Influence of the arc plasma parameters on the weld pool profile in TIG welding

    Science.gov (United States)

    Toropchin, A.; Frolov, V.; Pipa, A. V.; Kozakov, R.; Uhrlandt, D.

    2014-11-01

    Magneto-hydrodynamic simulations of the arc and fluid simulations of the weld pool can be beneficial in the analysis and further development of arc welding processes and welding machines. However, the appropriate coupling of arc and weld pool simulations needs further improvement. The tungsten inert gas (TIG) welding process is investigated by simulations including the weld pool. Experiments with optical diagnostics are used for the validation. A coupled computational model of the arc and the weld pool is developed using the software ANSYS CFX. The weld pool model considers the forces acting on the motion of the melt inside and on the surface of the pool, such as Marangoni, drag, electromagnetic forces and buoyancy. The experimental work includes analysis of cross-sections of the workpieces, highspeed video images and spectroscopic measurements. Experiments and calculations have been performed for various currents, distances between electrode and workpiece and nozzle diameters. The studies show the significant impact of material properties like surface tension dependence on temperature as well as of the arc structure on the weld pool behaviour and finally the weld seam depth. The experimental weld pool profiles and plasma temperatures are in good agreement with computational results.

  14. WELDING PROCESS

    Science.gov (United States)

    Zambrow, J.; Hausner, H.

    1957-09-24

    A method of joining metal parts for the preparation of relatively long, thin fuel element cores of uranium or alloys thereof for nuclear reactors is described. The process includes the steps of cleaning the surfaces to be jointed, placing the sunfaces together, and providing between and in contact with them, a layer of a compound in finely divided form that is decomposable to metal by heat. The fuel element members are then heated at the contact zone and maintained under pressure during the heating to decompose the compound to metal and sinter the members and reduced metal together producing a weld. The preferred class of decomposable compounds are the metal hydrides such as uranium hydride, which release hydrogen thus providing a reducing atmosphere in the vicinity of the welding operation.

  15. The characteristics of welded joints for air conditioning application

    Science.gov (United States)

    Weglowski, M. St.; Weglowska, A.; Miara, D.; Kwiecinski, K.; Błacha, S.; Dworak, J.; Rykala, J.; Pikula, J.; Ziobro, G.; Szafron, A.; Zimierska-Nowak, P.; Richert, M.; Noga, P.

    2017-10-01

    In the paper the results of metallographic examination of welded joints for air-conditioning elements are presented. The European directives 2006/40/EC on the greenhouse gasses elimination demand to stop using traditional refrigerant and to change it to R744 (CO2) medium in air conditioning installation. The R744 refrigerant is environmental friendly medium if compared with standard solution such as R12, R134a or R1234yf and safer for passengers than R1234yf. The non-standard thermodynamic parameters of the R744 which translate into high pressure and high temperature require specific materials to develop the shape and to specify the technology of manufacturing for the particular elements of the conduits and moreover the technologies of joining for the whole structure, which would meet the exploitation requirements of the new air-conditioning system. To produce the test welded joints of stainless steels four different joining technologies were applied: laser welding, plasma welding, electron beam welding as well as high speed rotation welding. This paper describes the influence of the selected welding process on the macrostructure and microstructure of welded joints of AISI 304 and AISI 316L steels. The results indicated that plasma welding laser welding and electron beam welding technologies guaranty the proper quality of welded joints and can be used for the air conditioning application in automotive industry. However, high speed rotation welding not guarantee the good quality of welded joints and cannot be used for above application.

  16. A Neural Network Approach for GMA Butt Joint Welding

    DEFF Research Database (Denmark)

    Christensen, Kim Hardam; Sørensen, Torben

    2003-01-01

    This paper describes the application of the neural network technology for gas metal arc welding (GMAW) control. A system has been developed for modeling and online adjustment of welding parameters, appropriate to guarantee a certain degree of quality in the field of butt joint welding with full...... penetration, when the gap width is varying during the welding process. The process modeling to facilitate the mapping from joint geometry and reference weld quality to significant welding parameters has been based on a multi-layer feed-forward network. The Levenberg-Marquardt algorithm for non-linear least...

  17. A numerical model for cold welding of metals

    DEFF Research Database (Denmark)

    Zhang, Wenqi; Bay, Niels

    1996-01-01

    at the weld interface. Accordingly, the general model for bond strength in cold welding earlier developed by Bay has been extended and modified. The new model presented in this paper simulates the whole cold welding process including the deformation of base metals and the establishment of welds bonding......Based on experimental investigations of cold welding of different metal combinations applying various surface preparation methods, the understanding of the mechanisms of bond formation in cold welding has been improved by introducing two parameters representing the properties of surface layers...

  18. Development of methodology for measurements of residual stresses in welded joint based on displacement of points in a coordinated table

    Directory of Open Access Journals (Sweden)

    Aníbal Veras Siqueira Filho

    2013-04-01

    Full Text Available Residual stresses in a welded joint of ASTM A131 grade AH32 steel was measured either by the X-ray diffraction or by displacements of referenced points measured on a coordinate measuring machine before and after heat treatment. For all tests, the welding was performed with Shielded Metal Arc Welding, vertical-up position, by a certified welder. After welding, some specimens were subjected to marking, made through small holes evenly spaced and mapped on a coordinate measuring machine. After labeling, the samples were subjected to heat treatment at temperatures nearby recrystallization. After heat treatment, the samples were subjected to new measurements by coordinate measuring machine to evaluate the displacements of the points produced by the recrystallization. In parallel, residual stress measurements were made by XRD for validation of this new methodology. The results obtained either by X-ray or by coordinate measuring machine showed a good correlation between the two measurement methodologies employed.

  19. Models for selecting GMA Welding Parameters for Improving Mechanical Properties of Weld Joints

    Science.gov (United States)

    Srinivasa Rao, P.; Ramachandran, Pragash; Jebaraj, S.

    2016-02-01

    During the process of Gas Metal Arc (GMAW) welding, the weld joints mechanical properties are influenced by the welding parameters such as welding current and arc voltage. These parameters directly will influence the quality of the weld in terms of mechanical properties. Even small variation in any of the cited parameters may have an important effect on depth of penetration and on joint strength. In this study, S45C Constructional Steel is taken as the base metal to be tested using the parameters wire feed rate, voltage and type of shielding gas. Physical properties considered in the present study are tensile strength and hardness. The testing of weld specimen is carried out as per ASTM Standards. Mathematical models to predict the tensile strength and depth of penetration of weld joint have been developed by regression analysis using the experimental results.

  20. Friction Stir Welding

    Science.gov (United States)

    Nunes, Arthur C., Jr.

    2008-01-01

    Friction stir welding (FSW) is a solid state welding process invented in 1991 at The Welding Institute in the United Kingdom. A weld is made in the FSW process by translating a rotating pin along a weld seam so as to stir the sides of the seam together. FSW avoids deleterious effects inherent in melting and promises to be an important welding process for any industries where welds of optimal quality are demanded. This article provides an introduction to the FSW process. The chief concern is the physical effect of the tool on the weld metal: how weld seam bonding takes place, what kind of weld structure is generated, potential problems, possible defects for example, and implications for process parameters and tool design. Weld properties are determined by structure, and the structure of friction stir welds is determined by the weld metal flow field in the vicinity of the weld tool. Metal flow in the vicinity of the weld tool is explained through a simple kinematic flow model that decomposes the flow field into three basic component flows: a uniform translation, a rotating solid cylinder, and a ring vortex encircling the tool. The flow components, superposed to construct the flow model, can be related to particular aspects of weld process parameters and tool design; they provide a bridge to an understanding of a complex-at-first-glance weld structure. Torques and forces are also discussed. Some simple mathematical models of structural aspects, torques, and forces are included.

  1. Automatic Gap Detection in Friction Stir Welding Processes (Preprint)

    National Research Council Canada - National Science Library

    Yang, Yu; Kalya, Prabhanjana; Landers, Robert G; Krishnamurthy, K

    2006-01-01

    .... This paper develops a monitoring algorithm to detect gaps in Friction Stir Welding (FSW) processes. Experimental studies are conducted to determine how the process parameters and the gap width affect the welding process...

  2. System of video observation for electron beam welding process

    Science.gov (United States)

    Laptenok, V. D.; Seregin, Y. N.; Bocharov, A. N.; Murygin, A. V.; Tynchenko, V. S.

    2016-04-01

    Equipment of video observation system for electron beam welding process was developed. Construction of video observation system allows to reduce negative effects on video camera during the process of electron beam welding and get qualitative images of this process.

  3. Effects Of Heat Sinks On VPPA Welds

    Science.gov (United States)

    Nunes, Arthur C.; Steranka, Paul O., Jr.

    1991-01-01

    Report describes theoretical and experimental study of absorption of heat by metal blocks in contact with metal plate while plate subjected to variable-polarity plasma-arc (VPPA) welding. Purpose of study to contribute to development of comprehensive mathematical model of temperature in weld region. Also relevant to welding of thin sheets of metal to thick blocks of metal, heat treatment of metals, and hotspots in engines.

  4. Uncertainty quantification methodologies development for stress corrosion cracking of canister welds

    Energy Technology Data Exchange (ETDEWEB)

    Dingreville, Remi Philippe Michel [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Bryan, Charles R. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2016-09-30

    This letter report presents a probabilistic performance assessment model to evaluate the probability of canister failure (through-wall penetration) by SCC. The model first assesses whether environmental conditions for SCC – the presence of an aqueous film – are present at canister weld locations (where tensile stresses are likely to occur) on the canister surface. Geometry-specific storage system thermal models and weather data sets representative of U.S. spent nuclear fuel (SNF) storage sites are implemented to evaluate location-specific canister surface temperature and relative humidity (RH). As the canister cools and aqueous conditions become possible, the occurrence of corrosion is evaluated. Corrosion is modeled as a two-step process: first, pitting is initiated, and the extent and depth of pitting is a function of the chloride surface load and the environmental conditions (temperature and RH). Second, as corrosion penetration increases, the pit eventually transitions to a SCC crack, with crack initiation becoming more likely with increasing pit depth. Once pits convert to cracks, a crack growth model is implemented. The SCC growth model includes rate dependencies on both temperature and crack tip stress intensity factor, and crack growth only occurs in time steps when aqueous conditions are predicted. The model suggests that SCC is likely to occur over potential SNF interim storage intervals; however, this result is based on many modeling assumptions. Sensitivity analyses provide information on the model assumptions and parameter values that have the greatest impact on predicted storage canister performance, and provide guidance for further research to reduce uncertainties.

  5. Effect of Submerged Arc Welding Parameters on the Microstructure of SA516 and A709 Steel Welds

    Science.gov (United States)

    Amanie, James

    The effects of submerged arc welding (SAW) current and speed on the microstructures of SA516 grade 70 and A709 grade 50 steel welds were studied in this research. Steel plates 17 mm-thick were submerged arc welded using different welding currents (from 700 to 850 A) and welding speeds (from 5.3 to 15.3 mm/s). The effect of heat input on the weld metal chemistry, morphologies and chemistry of inclusions and nucleation of acicular ferrite (AF), grain boundary ferrite (GBF) and Widmanstatten ferrite (WF) were evaluated. Optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) microanalysis and transmission electron microscopy (TEM) were used to examine the microstructures of the developed weld joints. PAX-it image analysis software program was utilized for quantitative analysis of the microstructures. The results showed that it is difficult to ascribe changes in the microstructure that occurred in the heat affected zone (HAZ) and the weld metal regions to a single welding process parameter. Inclusion analysis revealed two types of inclusions formed in the weld metals for both steels. They are spherical and faceted inclusions. It was also observed that acicular ferrite nucleated only on the spherical inclusions. EDS analysis showed that the two inclusions have different chemical compositions. The results further showed that the total oxygen content of the weld metals of both steels generally increased with welding current, but decreased with increasing welding speed. The prior austenite grain width decreased with increasing welding speed, but increased with increasing welding current (increased heat input). For both SA516 and A709 steel welds, the proportion of acicular ferrite (AF) in the weld metals increased initially, while those of grain boundary ferrite (GBF) and Widmanstatten ferrite (WF) decreased with increasing welding current when welding current was increased from 700 A to 800 A. With further increase in the

  6. Artificial neural networks application for modeling of friction stir welding effects on mechanical properties of 7075-T6 aluminum alloy

    Science.gov (United States)

    Maleki, E.

    2015-12-01

    Friction stir welding (FSW) is a relatively new solid-state joining technique that is widely adopted in manufacturing and industry fields to join different metallic alloys that are hard to weld by conventional fusion welding. Friction stir welding is a very complex process comprising several highly coupled physical phenomena. The complex geometry of some kinds of joints makes it difficult to develop an overall governing equations system for theoretical behavior analyse of the friction stir welded joints. Weld quality is predominantly affected by welding effective parameters, and the experiments are often time consuming and costly. On the other hand, employing artificial intelligence (AI) systems such as artificial neural networks (ANNs) as an efficient approach to solve the science and engineering problems is considerable. In present study modeling of FSW effective parameters by ANNs is investigated. To train the networks, experimental test results on thirty AA-7075-T6 specimens are considered, and the networks are developed based on back propagation (BP) algorithm. ANNs testing are carried out using different experimental data that they are not used during networks training. In this paper, rotational speed of tool, welding speed, axial force, shoulder diameter, pin diameter and tool hardness are regarded as inputs of the ANNs. Yield strength, tensile strength, notch-tensile strength and hardness of welding zone are gathered as outputs of neural networks. According to the obtained results, predicted values for the hardness of welding zone, yield strength, tensile strength and notch-tensile strength have the least mean relative error (MRE), respectively. Comparison of the predicted and the experimental results confirms that the networks are adjusted carefully, and the ANN can be used for modeling of FSW effective parameters.

  7. ROV inspection of welds -- A reality

    Energy Technology Data Exchange (ETDEWEB)

    Raine, G.A. [Technical Software Consultants Ltd., Milton Keynes (United Kingdom)

    1995-12-31

    Remote Operated Vehicles (ROV) have been in use since the early 1970`s but these could only carry out a limited number of mechanical tasks. During the 1980`s a new range of vehicles were developed that could carry out cleaning, visual inspection and flooded member detection, but were still unable to inspect welds. These tasks increased until it was possible to reduce the proportion of combined diving and ROV program to 10% for diving operations. New inspection techniques and computer aided manipulators were also being developed and were being combined in an attempt to resolve this inspection problem. Trials were carried out with electromagnets and eddy current techniques, but the problem of access and accurate weld tracking still produced problems. The development of the Alternating Current Field Measurement (ACFM) technique and its successful use during diving inspection made it a possible contender for use with an ROV. Because of its ability to detect and size surface breaking cracks without electrical contact or complex scanning procedures it is possible to produce inspection heads that do not need accurate placement by an ROV. A fully integrated ROV deployment system using ACFM multi element array technology has now been produced for a North Sea Operator. This can be used with any work class ROV and it does not require accurate weld toe tracking. This system has been subject to extensive tank Probability of Detection and Sizing Trials and a very high success rate was achieved with a very low number of false indications. In addition good sizing accuracy was produced for both length and depth measurements. Further front end tools have also been developed for different geometry`s and access.

  8. Microstructure and Microsegregation of an Inconel 625 Weld Overlay Produced on Steel Pipes by the Cold Metal Transfer Technique

    National Research Council Canada - National Science Library

    M. Rozmus-Górnikowska; Ł. Cieniek; M. Blicharski; J. Kusiński

    2014-01-01

    The aim of this work was to investigate the development of microstructure and variations in chemical composition in commercial Inconel 625 coatings on a ferritic-pearlitic steel overlaid by the CMT method...

  9. Microstructure and Microsegregation of an Inconel 625 Weld Overlay Produced on Steel Pipes by the Cold Metal Transfer Technique

    OpenAIRE

    Rozmus-Górnikowska M.; Cieniek Ł.; Blicharski M.; Kusiński J.

    2014-01-01

    The aim of this work was to investigate the development of microstructure and variations in chemical composition in commercial Inconel 625 coatings on a ferritic-pearlitic steel overlaid by the CMT method.

  10. Microstructure and Microsegregation of an Inconel 625 Weld Overlay Produced on Steel Pipes by the Cold Metal Transfer Technique

    Directory of Open Access Journals (Sweden)

    Rozmus-Górnikowska M.

    2014-10-01

    Full Text Available The aim of this work was to investigate the development of microstructure and variations in chemical composition in commercial Inconel 625 coatings on a ferritic-pearlitic steel overlaid by the CMT method.

  11. Control system of power supply for resistance welding machine

    Directory of Open Access Journals (Sweden)

    Світлана Костянтинівна Поднебенна

    2017-06-01

    Full Text Available This article describes the existing methods of heat energy stabilizing, which are realized in thyristor power supplies for resistance welding machines. The advantages and features of thyristor power supplies have been described. A control system of power supply for resistance welding machine with stabilization of heat energy in a welding spot has been developed. Measurements are performed in primary winding of a welding transformer. Weld spot heating energy is calculated as the difference between the energy, consumed from the mains, and the energy losses in the primary and secondary circuits of the welding transformer as well as the energy losses in the transformer core. Algorithms of digital signal processing of the developed control system are described in the article. All measurements and calculations are preformed automatically in real-time. Input signals to the control system are: transformer primary voltage and current, temperature of the welding circuit. The designed control system ensures control of the welding heat energy and is not influenced by the supply voltage and impedance changes caused by insertion of the ferromagnetic mass in the welding circuit, the temperature change during the welding process. The developed control system for resistance welding machine makes it possible to improve the quality of welded joints, increase the efficiency of the resistance welding machine

  12. Modeling of transverse welds formation during liquid–solid extrusion directly following vacuum infiltration of magnesium matrix composite

    Directory of Open Access Journals (Sweden)

    Jian Liu

    2015-09-01

    Full Text Available Liquid–solid extrusion directly following vacuum infiltration (LSEVI is an infiltration–extrusion integrated forming technique, and transverse weld between upper residual magnesium alloy and magnesium matrix composites is a common internal defect, which can severely reduce the yield of composite products. To improve current understanding on the mechanism of transverse welding phenomenon, a thermo-mechanical numerical model of LSEVI for magnesium matrix composites was developed. The formation of transverse weld during extrusion was visualized using finite element simulation method, and the formation mechanism was discussed from the aspect of velocity field using a point tracking technique. The simulation results were verified by the experimental results in term of weld shape.

  13. Identification of optimum friction stir spot welding process parameters controlling the properties of low carbon automotive steel joints

    Directory of Open Access Journals (Sweden)

    A.K. Lakshminarayanan

    2015-07-01

    Full Text Available Friction stir spot welding is a novel solid state process that has recently received considerable attention from various industries including automotive sectors due to many advantages over the resistance spot welding. However to apply this technique, the process parameters must be optimized to obtain improved mechanical properties compared to resistance spot welding. To achieve this, in this investigation, design of experiments was used to conduct the experiments for exploring the interdependence of the process parameters. A second order quadratic model for predicting the lap shear tensile strength of friction stir spot welded low carbon automotive steel joints was developed from the experimental obtained data. It is found that dwell time plays a major role in deciding the joint properties, which is followed by rotational speed and plunge depth. Further optimum process parameters were identified for maximum lap shear tensile strength using numerical and graphical optimization techniques.

  14. Welding and Joining of Titanium Aluminides

    Science.gov (United States)

    Cao, Jian; Qi, Junlei; Song, Xiaoguo; Feng, Jicai

    2014-01-01

    Welding and joining of titanium aluminides is the key to making them more attractive in industrial fields. The purpose of this review is to provide a comprehensive overview of recent progress in welding and joining of titanium aluminides, as well as to introduce current research and application. The possible methods available for titanium aluminides involve brazing, diffusion bonding, fusion welding, friction welding and reactive joining. Of the numerous methods, solid-state diffusion bonding and vacuum brazing have been most heavily investigated for producing reliable joints. The current state of understanding and development of every welding and joining method for titanium aluminides is addressed respectively. The focus is on the fundamental understanding of microstructure characteristics and processing–microstructure–property relationships in the welding and joining of titanium aluminides to themselves and to other materials. PMID:28788113

  15. Welding and Joining of Titanium Aluminides.

    Science.gov (United States)

    Cao, Jian; Qi, Junlei; Song, Xiaoguo; Feng, Jicai

    2014-06-25

    Welding and joining of titanium aluminides is the key to making them more attractive in industrial fields. The purpose of this review is to provide a comprehensive overview of recent progress in welding and joining of titanium aluminides, as well as to introduce current research and application. The possible methods available for titanium aluminides involve brazing, diffusion bonding, fusion welding, friction welding and reactive joining. Of the numerous methods, solid-state diffusion bonding and vacuum brazing have been most heavily investigated for producing reliable joints. The current state of understanding and development of every welding and joining method for titanium aluminides is addressed respectively. The focus is on the fundamental understanding of microstructure characteristics and processing-microstructure-property relationships in the welding and joining of titanium aluminides to themselves and to other materials.

  16. Welding and Joining of Titanium Aluminides

    Directory of Open Access Journals (Sweden)

    Jian Cao

    2014-06-01

    Full Text Available Welding and joining of titanium aluminides is the key to making them more attractive in industrial fields. The purpose of this review is to provide a comprehensive overview of recent progress in welding and joining of titanium aluminides, as well as to introduce current research and application. The possible methods available for titanium aluminides involve brazing, diffusion bonding, fusion welding, friction welding and reactive joining. Of the numerous methods, solid-state diffusion bonding and vacuum brazing have been most heavily investigated for producing reliable joints. The current state of understanding and development of every welding and joining method for titanium aluminides is addressed respectively. The focus is on the fundamental understanding of microstructure characteristics and processing–microstructure–property relationships in the welding and joining of titanium aluminides to themselves and to other materials.

  17. A Study to Increase Weld Penetration in P91 Steel During TIG Welding by using Activating Fluxes

    Science.gov (United States)

    Singh, Akhilesh Kumar; Kumar, Mayank; Dey, Vidyut; Naresh Rai, Ram

    2017-08-01

    Activated Flux TIG (ATIG) welding is a unique joining process, invented at Paton Institute of electric welding in 1960. ATIG welding process is also known as flux zoned TIG (FZTIG). In this process, a thin layer of activating flux is applied along the line on the surface of the material where the welding is to be carries out. The ATIG process aids to increase the weld penetration in thick materials. Activating fluxes used in the literature show the use of oxides like TiO2, SiO2, Cr2O3, ZnO, CaO, Fe2O3, and MnO2 during welding of steels. In the present study, ATIG was carried out on P-91 steel. Though, Tungsten Inert Gas welding gives excellent quality welds, but the penetration obtained in such welding is still demanding. P91 steel which is ferritic steel is used in high temperature applications. As this steel is, generally, used in thick sections, fabrication of such structures with TIG welding is limited, due to its low depth of penetration. To increase the depth of penetration in P91while welding with ATIG, the role of various oxides were investigated. Apart from the oxides mentioned above, in the present study the role of B2O3, V2O5 and MgO, during ATIG welding of P91 was investigated. It was seen that, compared to TIG welding, there was phenomenal increase in weld penetration during ATIG welding. Amongst all the oxides used in this study, maximum penetration was achieved in case of B2O3. The measurements of weld penetration, bead width and heat affected zone of the weldings were carried out using an image analysis technique.

  18. Testbed For Aerothermal Test Technique Development Project

    Data.gov (United States)

    National Aeronautics and Space Administration — It is proposed that a very low cost wind tunnel could be developed at JSC to provide engineers with the ability to directly run small tests focused on improving...

  19. Introduction to Welding.

    Science.gov (United States)

    Fortney, Clarence; Gregory, Mike

    This curriculum guide provides six units of instruction on basic welding. Addressed in the individual units of instruction are the following topics: employment opportunities for welders, welding safety and first aid, welding tools and equipment, basic metals and metallurgy, basic math and measuring, and procedures for applying for a welding job.…

  20. Distortion Control during Welding

    NARCIS (Netherlands)

    Akbari Pazooki, A.M.

    2014-01-01

    The local material expansion and contraction involved in welding result in permanent deformations or instability i.e., welding distortion. Considerable efforts have been made in controlling welding distortion prior to, during or after welding. Thermal Tensioning (TT) describes a group of in-situ

  1. Finite element modelling and updating of friction stir welding (FSW joint for vibration analysis

    Directory of Open Access Journals (Sweden)

    Zahari Siti Norazila

    2017-01-01

    Full Text Available Friction stir welding of aluminium alloys widely used in automotive and aerospace application due to its advanced and lightweight properties. The behaviour of FSW joints plays a significant role in the dynamic characteristic of the structure due to its complexities and uncertainties therefore the representation of an accurate finite element model of these joints become a research issue. In this paper, various finite elements (FE modelling technique for prediction of dynamic properties of sheet metal jointed by friction stir welding will be presented. Firstly, nine set of flat plate with different series of aluminium alloy; AA7075 and AA6061 joined by FSW are used. Nine set of specimen was fabricated using various types of welding parameters. In order to find the most optimum set of FSW plate, the finite element model using equivalence technique was developed and the model validated using experimental modal analysis (EMA on nine set of specimen and finite element analysis (FEA. Three types of modelling were engaged in this study; rigid body element Type 2 (RBE2, bar element (CBAR and spot weld element connector (CWELD. CBAR element was chosen to represent weld model for FSW joints due to its accurate prediction of mode shapes and contains an updating parameter for weld modelling compare to other weld modelling. Model updating was performed to improve correlation between EMA and FEA and before proceeds to updating, sensitivity analysis was done to select the most sensitive updating parameter. After perform model updating, total error of the natural frequencies for CBAR model is improved significantly. Therefore, CBAR element was selected as the most reliable element in FE to represent FSW weld joint.

  2. Role of heat equation in lap joint for welding process

    Science.gov (United States)

    Kumar, P.; Rohit, Sooraj

    2017-07-01

    Welding is predominantly used in industrial purposes and growth in their industry, which gives exact welding and more efficient. The major advantage of using this welding technique at initial stage it takes very low heat to weld the portion and gives a good result of low distortion in modules. In this context, two dissimilar metals copper and nickel are chosen for analysis in tungsten inert gas welding (TIG) in which length is 300 mm and breadth is 100 mm thickness 15 mm welded at room temperature a welded portion zone is formed simulation analysis has done on CATIA® and ANSYS®and MATLAB® code is generated for calculating temperatures at each node to calculate temperature at each node a new technique is used tri-diagonal matrix algorithm is used (TDMA) Steady state one dimension heat is calculated results compared between simulation analysis and analytical analysis temperature at each node is calculated both the temperatures are equal with error.

  3. Experimental and simulation study on the microstructure of TA15 titanium alloy laser beam welded joints

    Science.gov (United States)

    Zhan, Xiaohong; Peng, Qingyu; Wei, Yanhong; Ou, Wenmin

    2017-09-01

    Laser beam welding technique offers obvious advantages over other fusion welding processes in terms of joining titanium alloy. The microstructure of welded seam and heat affected zone resulted from diverse welding speeds and laser powers were investigated after simulating welding heat treatment. The analysis of the thermal transport properties successfully explained the morphology. Optimal process parameters were obtained. The simulation results were consistent with the corresponding experimental observations.

  4. Development of Radiation Technique for Environmental Treatment

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Myun Joo; Kuk, Il Hiun; Jin, Joon Ha (and others)

    2007-02-15

    The purpose of this research is to development of technologies for 1) the removal of toxic organic chemicals in sewage sludges and the volume reduction of the sewage sludge 2) the recycling/reuse of sewage sludge 3) the reconvey of resource from fishery waste by using radiation technologies. This research project focused on the study of treatment, disposal, and recycling/reuse of sewage sludge by radiation technology, and recovery of highly value-added resources from the wastes. As basic studies with a radiation technology, an enhancement of dewaterbilities of sewage sludge, development of dewatering conditioner, reduction of trace toxic organic chemicals, and the toxicities of the byproducts were studied. Based on the basic experimental results, we developed the pilot-scale system with the continuous e-beam and dewatering unit and the advanced treatment system with the use of carbon source recovered from sewage sludge.

  5. Development of lidar techniques for environmental studies

    Energy Technology Data Exchange (ETDEWEB)

    Andersson, Mats

    1996-09-01

    The lidar group in Lund has performed many DIAL measurements with a mobile lidar system that was first described in 1987. The lidar system is based on a Nd:YAG-pumped dye laser. During the last few years the lidar group has focused on fluorescence imaging and mercury measurements in the troposphere. In 1994 we performed two campaigns: one fluorescence imaging measurement campaign outside Avignon, France and one unique lidar campaign at a mercury mine in Almaden, Spain. Both campaigns are described in this thesis. This thesis also describes how the mobile lidar system was updated with the graphical programming language LabVIEW to obtain a user friendly lidar system. The software controls the lidar system and analyses measured data. The measurement results are shown as maps of species concentration. All electronics and the major parts of the program are described. A new graphical technique to estimate wind speed from plumes is also discussed. First measurements have been performed with the new system. 31 refs, 19 figs, 1 tab

  6. Tomographical process monitoring of laser transmission welding with OCT

    Science.gov (United States)

    Ackermann, Philippe; Schmitt, Robert

    2017-06-01

    Process control of laser processes still encounters many obstacles. Although these processes are stable, a narrow process parameter window during the process or process deviations have led to an increase on the requirements for the process itself and on monitoring devices. Laser transmission welding as a contactless and locally limited joining technique is well-established in a variety of demanding production areas. For example, sensitive parts demand a particle-free joining technique which does not affect the inner components. Inline integrated non-destructive optical measurement systems capable of providing non-invasive tomographical images of the transparent material, the weld seam and its surrounding areas with micron resolution would improve the overall process. Obtained measurement data enable qualitative feedback into the system to adapt parameters for a more robust process. Within this paper we present the inline monitoring device based on Fourier-domain optical coherence tomography developed within the European-funded research project "Manunet Weldable". This device, after adaptation to the laser transmission welding process is optically and mechanically integrated into the existing laser system. The main target lies within the inline process control destined to extract tomographical geometrical measurement data from the weld seam forming process. Usage of this technology makes offline destructive testing of produced parts obsolete. 1,2,3,4

  7. Microcomputer Techniques for Developing Hardwood Conservation Strategies

    Science.gov (United States)

    Steve McNiel

    1991-01-01

    Hardwoods are disappearing from the California landscape at alarming rates. This is due to a variety of influences, both natural and man made. It is clear that conservation and rehabilitation of hardwood resources will require a large effort on the part of research institutes, universities, government agencies, special interest groups, private developers, maintenance...

  8. Gestalt Therapy: Development, Theory, and Techniques.

    Science.gov (United States)

    Witchel, Robert

    This paper presents a full review of the literature in the area of Gestalt Therapy and could be helpful in familiarizing people with this discipline. The roots contributing to the development of Gestalt therapy as presently practiced are explored briefly. Gestalt theory is presented in a developmental way, initially exploring the relationship…

  9. Manganese in occupational arc welding fumes--aspects on physiochemical properties, with focus on solubility.

    Science.gov (United States)

    Taube, Fabian

    2013-01-01

    Physicochemical properties, such as particle sizes, composition, and solubility of welding fumes are decisive for the bioaccessibility of manganese and thereby for the manganese cytotoxic and neurotoxic effects arising from various welding fumes. Because of the diverse results within the research on welding fume solubility, this article aims to review and discuss recent literature on physicochemical properties of gas metal arc welding, shielded metal arc welding, and flux-cored arc welding fumes, with focus on solubility properties. This article also presents a short introduction to the literature on arc welding techniques, health effects from manganese, and occupational exposure to manganese among welders.

  10. Structural and mechanical properties of welded joints of reduced activation martensitic steels

    Energy Technology Data Exchange (ETDEWEB)

    Filacchioni, G. E-mail: gianni.filacchioni@casaccia.enea.it; Montanari, R.; Tata, M.E.; Pilloni, L

    2002-12-01

    Gas tungsten arc welding and electron beam welding methods were used to realise welding pools on plates of reduced activation martensitic steels. Structural and mechanical features of these simulated joints have been investigated in as-welded and post-welding heat-treated conditions. The research allowed to assess how each welding technique affects the original mechanical properties of materials and to find suitable post-welding heat treatments. This paper reports results from experimental activities on BATMAN II and F82H mod. steels carried out in the frame of the European Blanket Project - Structural Materials Program.

  11. Friction Welding For Cladding Applications: Processing, Microstructure and Mechanical Properties of Inertia Friction Welds of Stainless Steel to Low Carbon Steel and Evaluation of Wrought and Welded Austenitic Stainless Steels for Cladding Applications in Acidchloride Service

    Science.gov (United States)

    Switzner, Nathan

    -state mixing. Thirdly, the corrosion resistance of multiple austenitic stainless steels (types 304, 316, and 309) processed in varying ways was compared for acid chloride environments using advanced electrochemical techniques. Physical simulation of fusion claddings and friction weld claddings (wrought stainless steels) was used for sample preparation to determine compositional and microstructural effects. Pitting resistance correlated firstly with Cr content, with N and Mo additions providing additional benefits. The high ferrite fraction of as-welded samples reduced their corrosion resistance. Wrought type 309L outperformed as-welded type 309L in dissolved mass loss and reverse corrosion rate from the potentiodynamic scan in 1.0 N HCl/3.5% NaCl solution. Electrochemical impedance results indicated that wrought 309L and 316L developed a corrosion resistant passive film more rapidly than other alloys in 0.1 N HCl/3.5% NaCl, and also performed well in long term (160-day) corrosion testing in the same environment. Fourthly, to prove the concept of internal CR lining by friction welding, a conical work piece of 304L stainless steel was friction welded internally to 1018 steel.

  12. A Comparative Study of Welded ODS Cladding materials for AFCI/GNEP Applications

    Energy Technology Data Exchange (ETDEWEB)

    Indrajit Charit; Megan Frary; Darryl Butt; K.L. Murty; Larry Zirker; James Cole; Mitchell Meyer; Rajiv S. Mishra; Mark Woltz

    2011-03-31

    This research project involved working on the pressure resistance welding of oxide dispersion strengthened (ODS) alloys which will have a large role to play in advanced nuclear reactors. The project also demonstrated the research collaboration between four universities and one nation laboratory (Idaho National Laboratory) with participation from an industry for developing for ODS alloys. These alloys contain a high number density of very fine oxide particles that can impart high temperature strength and radiation damage resistance suitable for in-core applications in advanced reactors. The conventional fusion welding techniques tend to produce porosity-laden microstructure in the weld region and lead to the agglomeration and non-uniform distribution of the neededoxide particles. That is why two solid state welding methods - pressure resistance welding (PRW) and friction stir welding (FSW) - were chosen to be evaluated in this project. The proposal is expected to support the development of Advanced Burner Reactors (ABR) under the GNEP program (now incorporated in Fuel Cycle R&D program). The outcomes of the concluded research include training of graduate and undergraduate students and get them interested in nuclear related research.

  13. Development of new structural health monitoring techniques

    Science.gov (United States)

    Fekrmandi, Hadi

    During the past two decades, many researchers have developed methods for the detection of structural defects at the early stages to operate the aerospace vehicles safely and to reduce the operating costs. The Surface Response to Excitation (SuRE) method is one of these approaches developed at FIU to reduce the cost and size of the equipment. The SuRE method excites the surface at a series of frequencies and monitors the propagation characteristics of the generated waves. The amplitude of the waves reaching to any point on the surface varies with frequency; however, it remains consistent as long as the integrity and strain distribution on the part is consistent. These spectral characteristics change when cracks develop or the strain distribution changes. The SHM methods may be used for many applications, from the detection of loose screws to the monitoring of manufacturing operations. A scanning laser vibrometer was used in this study to investigate the characteristics of the spectral changes at different points on the parts. The study started with detecting a load on a plate and estimating its location. The modifications on the part with manufacturing operations were detected and the Part-Based Manufacturing Process Performance Monitoring (PbPPM) method was developed. Hardware was prepared to demonstrate the feasibility of the proposed methods in real time. Using low-cost piezoelectric elements and the non-contact scanning laser vibrometer successfully, the data was collected for the SuRE and PbPPM methods. Locational force, loose bolts and material loss could be easily detected by comparing the spectral characteristics of the arriving waves. On-line methods used fast computational methods for estimating the spectrum and detecting the changing operational conditions from sum of the squares of the variations. Neural networks classified the spectrums when the desktop -- DSP combination was used. The results demonstrated the feasibility of the SuRE and PbPPM methods.

  14. Non-destructive Magnetic Evaluation of Laser Weld Quality in Hot Rolled Coils

    Science.gov (United States)

    Mohapatra, J. N.; Chakradhar, I.; Rao, K. R. C.; Rao, V. V. L.; Kaza, Marutiram

    2015-06-01

    Weld quality evaluation was conducted on laser welded thin sectsions (2 mm) of hot-rolled (HR) low-carbon steel coils during cold rolling process. The analysis revealed that the poor welds consisting of the weld defects like incomplete fusion, cluster of porosity, and large difference in hardness between the weld zone and base metal were responsible for the weld failures. Experiments were conducted by varying the welding parameters; laser power and welding speed to optimize the parameters for minimizing the weld defects. The optimized weld process parameters have helped elimination of weld defects and the results are verified with microscopy and microhardness measurements. As destructive evaluation techniques are time consuming and not always permitted in industrial applications, attempts have been made in the present investigation for the utilization of suitable non-destructive techniques for the evaluation of weld quality. Non-destructive magnetic techniques of magnetic hysteresis loop and magnetic Barkhausen emissions were used in the present investigation to establish possible correlations of magnetic properties across the weld seam with the mechanical property (microhardness) for evaluation of weld quality. It is inferred that the magnetic properties of coercivity and inverse of root mean square voltage can be effectively utilized to determine weld quality in HR steel coils.

  15. Qualification of phased array ultrasonic examination on T-joint weld of austenitic stainless steel for ITER vacuum vessel

    Energy Technology Data Exchange (ETDEWEB)

    Kim, G.H. [ITER Korea, National Fusion Research Institute, Daejeon 305-333 (Korea, Republic of); Park, C.K., E-mail: love879@hanmail.net [ITER Korea, National Fusion Research Institute, Daejeon 305-333 (Korea, Republic of); Jin, S.W.; Kim, H.S.; Hong, K.H.; Lee, Y.J.; Ahn, H.J.; Chung, W. [ITER Korea, National Fusion Research Institute, Daejeon 305-333 (Korea, Republic of); Jung, Y.H.; Roh, B.R. [Hyundai Heavy Industries Co. Ltd., Ulsan 682-792 (Korea, Republic of); Sa, J.W.; Choi, C.H. [ITER Organization, Route de Vinon-sur-Verdon, CS 90 046, 13067 St. Paul Lez Durance Cedex (France)

    2016-11-01

    Highlights: • PAUT techniques has been developed by Hyundai Heavy Industries Co., LTD (HHI) and Korea Domestic Agency (KODA) to verify and settle down instrument calibration, test procedures, image processing, and so on. As the first step of development for PAUT technique, Several dozens of qualification blocks with artificial defects, which are parallel side drilled hole, embedded lack of fusion, embedded repair weld notch, and so on, have been designed and fabricated to simulate all potential defects during welding process. Real UT qualification group-1 for T-joint weld was successfully conducted in front of ANB inspector. • In this paper, remarkable progresses of UT qualification are presented for ITER vacuum vessel. - Abstract: Full penetration welding and 100% volumetric examination are required for all welds of pressure retaining parts of the ITER Vacuum Vessel (VV) according to RCC-MR Code and French Order of Nuclear Pressure Equipment (ESPN). The NDE requirement is one of important technical issues because radiographic examination (RT) is not applicable to many welding joints. Therefore the ultrasonic examination (UT) has been selected as an alternative method. Generally the UT on the austenitic welds is regarded as a great challenge due to the high attenuation and dispersion of the ultrasonic signal. In this paper, Phased array ultrasonic examination (PAUT) has been introduced on double sided T-shape austenitic welds of the ITER VV as a major NDE method as well as RT. Several dozens of qualification blocks with artificial defects, which are parallel side drilled hole, embedded lack of fusion, embedded repair weld notch, embedded parallel vertical notch, and so on, have been designed and fabricated to simulate all potential defects during welding process. PAUT techniques on the thick austenitic welds have been developed taking into account the acceptance criteria. Test procedure including calibration of equipment is derived and qualified through

  16. Development of ammonium nitrate based explosives to optimize explosive properties and explosive welding parameters used during explosion cladding

    Science.gov (United States)

    Hurley, Christoph

    The ability to accurately measure and predict the velocity of explosively driven flyer plates has been a subject of significant work by the explosives community for some time. The majority of this work has focused on the use of high-energy, ideal explosives that are of interest for defense applications. Several attempts have been made to modify the experimental methods developed for these ideal explosives for use in testing low-energy, non-ideal explosive compounds (including industrially useful mixtures of ammonium nitrate, fuels, and additives) with varying degrees of success. The detonation properties of non-ideal explosives are difficult to measure precisely due to the effect of physical, environmental, and geometric factors on the detonation of these materials. The work presented in this document attempts to mitigate the variability inherent in measurements of non-ideal, ammonium nitrate-based explosives by performing testing using charge geometry similar to that used in the industrial process of explosion welding. A method to measure flyer plate velocity with optical high-speed imaging using commercially available equipment is described. Flyer plate velocity data from both experimental measurements and numerical modeling is presented. A new formula for predicting explosive energy based on the detonation velocity of an ammonium nitrate based explosive in a planar geometry is proposed and applied to a theoretical explosive cladding scenario.

  17. Welding of Prosthetic Alloys

    Directory of Open Access Journals (Sweden)

    Wojciechowska M.

    2015-04-01

    Full Text Available This paper presents the techniques of joining metal denture elements, used in prosthetic dentistry: the traditional soldering technique with a gas burner and a new technique of welding with a laser beam; the aim of the study was to make a comparative assessment of the quality of the joints in view of the possibility of applying them in prosthetic structures. Fractographic examinations were conducted along with tensile strength and impact strength tests, and the quality of the joints was assessed compared to the solid metal. The experiments have shown that the metal elements used to make dentures, joined by the technique which employs a laser beam, have better strength properties than those achieved with a gas burner.

  18. A Water-Drop Method of Hardening of the Welded Joints of Drill Pipes

    Science.gov (United States)

    Maisuradze, M. V.; Yudin, Yu. V.; Eismondt, Yu. G.

    2015-09-01

    A combined computational and experimental technique is developed for implementing a scientifically based approach to the selection of a technology of heat hardening of welded joints of drill pipes made of steel 25KhGM with the use of water-drop quenching. The basic service characteristics of the water-drop cooling device are presented. An analytic model that relates the parameters of the water-drop quenching device (standard size and number of jets in device, pressure of fed water, distance from the jet nozzle to the cooled surface) to the properties of the welded joint is proposed. With the new technique the construction of a quenching device may be developed and the technology of heat treatment of the welded joints of drill pipes optimized in order to increase the level of mechanical properties.

  19. Welding the AT-400A Containment Vessel

    Energy Technology Data Exchange (ETDEWEB)

    Brandon, E.

    1998-11-01

    Early in 1994, the Department of Energy assigned Sandia National Laboratories the responsibility for designing and providing the welding system for the girth weld for the AT-400A containment vessel. (The AT-400A container is employed for the shipment and long-term storage of the nuclear weapon pits being returned from the nation's nuclear arsenal.) Mason Hanger Corporation's Pantex Plant was chosen to be the production facility. The project was successfully completed by providing and implementing a turnkey welding system and qualified welding procedure at the Pantex Plant. The welding system was transferred to Pantex and a pilot lot of 20 AT-400A containers with W48 pits was welded in August 1997. This document is intended to bring together the AT-400A welding system and product (girth weld) requirements and the activities conducted to meet those requirements. This document alone is not a complete compilation of the welding development activities but is meant to be a summary to be used with the applicable references.

  20. Insights into intermetallic phases on pulse welded dissimilar metal joints

    OpenAIRE

    Beyer, E.; Brenner, B; Göbel, G.; Herrmannsdörfer, T.; Kaspar, J.

    2010-01-01

    The Magnetic Pulse Welding (MPW) process has been developed to an industrially used joining method which is considered to be a fast, noncontact, clean and "cold" solid state welding process. Unlike fusion welding, the absence of direct heat during the welding cycle makes it possible to join dissimilar metals, for instance aluminium to copper or copper to steel, without noticeable detrimental metallurgical defects. This is very desirable, as today s industry lacks technologies to join often no...

  1. Friction Stir Spot Welding of 6061 Aluminum-to-Copper

    Science.gov (United States)

    Heideman, Robert J.

    Friction stir spot welding (FSSW) between 1.5mm thick 6061 Al on top and 1.5mm thick Cu at bottom was conducted. First, weld parameters and the weld macrostructure that were necessary to form good quality welds, as determined using lap shear weld strength, were identified. Tool rotation speed and tool pin length are key variables that control weld strength. To obtain high quality strong welds, a Cu ring extruded upward from the lower Cu sheet into the upper 6061 Al-sheet, which promoted bonding and interlocking between the sheets, and an Al-rich stir zone between Cu ring and weld keyhole were both necessary. Second, a technique where the tool remained in the sample after FSSW helped determine the material flow that takes place during high quality weld formation and the functions of the welding tool features. The tool threads cause 6061 Al from the upper sheet to move downward into the region near the threads. The tool shoulder causes a counter flow movement of 6061 Al that results in the formation of the Al-rich stir zone and also causes the upward extrusion of the lower Cu sheet. This technique also identified that a Cu-rich material forms on the tool tip, that this material sheds and rebuilds during subsequent welds, and that this material can form large Cu-rich particles that can completely fill the tool threads, impede proper material flow and lead to a low strength, poor quality weld. Third, to further understand welding parameters, weld temperatures, torque, and vertical forces were measured. Temperature data was collected using a tool holder that permitted wireless thermocouple data collection. Through these measurements, rotational plunge weld energy was recognized as important in determining if a quality weld formed, and weld plunge rate was identified as the welding parameter that significantly impacted rotational weld plunge energy. The final phase of research was to improve weld quality consistency. Through repetitive trials with a single tool

  2. Investigation and control of factors influencing resistance upset butt welding.

    NARCIS (Netherlands)

    Kerstens, N.F.H.

    2010-01-01

    The purpose of this work is to investigate the factors influencing the resistance upset butt welding process to obtain an understanding of the metal behaviour and welding process characteristics, so that new automotive steels can be welded with reduced development time and fewer failures in

  3. A Neural Network Approach for GMA Butt Joint Welding

    DEFF Research Database (Denmark)

    Christensen, Kim Hardam; Sørensen, Torben

    2003-01-01

    This paper describes the application of the neural network technology for gas metal arc welding (GMAW) control. A system has been developed for modeling and online adjustment of welding parameters, appropriate to guarantee a certain degree of quality in the field of butt joint welding with full...

  4. ISOL techniques, present status and new developments

    CERN Document Server

    Huyse, M

    2002-01-01

    On-line mass separation has recently gained extra momentum due to two extremes of applications. On the one side, beams from on-line mass separators have been decelerated in order to inject them in ion traps for precise experiments. On the other side, beams from on-line mass separators have been post-accelerated in order to use the secondary beam for nuclear reaction studies. Both applications put stringent requirements on the ISOL beams. These requirements relate to: - the element range of the beam, including refractory elements; - to the time span of the separated isotopes, down to the millisecond region; - to the intensity of the beam, dealing with high-intensity targets; - to the charge state of the beam, breeding it up from 1 sup + to n sup +; - to the purity of the beam, in mass as well as element selection; - and to the ion-optical quality, related to energy as well as time. This contribution deals with the recent developments in each direction and will give an outlook for further studies. Special empha...

  5. Exercises for Development of Cycling Technique on Cycling Indoor Track

    OpenAIRE

    Petr, Lukáš

    2006-01-01

    Exercises Enhancing the track cycling technique Aim: The aim of this thesis is to compile and verify in practice exercises for inventory development and training proper techniques bike ride along the bike path. These exercises should be included in the beginning and during the cycling training. In conclusion, the thesis is whether Applications should exercise for the development of proper riding techniques on the bike path positive impact on the group of competitors, or if they had no effect....

  6. Technique development for photoacoustic imaging guided interventions

    Science.gov (United States)

    Cheng, Qian; Zhang, Haonan; Yuan, Jie; Feng, Ting; Xu, Guan; Wang, Xueding

    2015-03-01

    Laser-induced thermotherapy (LITT), i.e. tissue destruction induced by a local increase of temperature by means of laser light energy transmission, has been frequently used for minimally invasive treatments of various diseases such as benign thyroid nodules and liver cancer. The emerging photoacoustic (PA) imaging, when integrated with ultrasound (US), could contribute to LITT procedure. PA can enable a good visualization of percutaneous apparatus deep inside tissue and, therefore, can offer accurate guidance of the optical fibers to the target tissue. Our initial experiment demonstrated that, by picking the strong photoacoustic signals generated at the tips of optical fibers as a needle, the trajectory and position of the fibers could be visualized clearly using a commercial available US unit. When working the conventional US Bscan mode, the fibers disappeared when the angle between the fibers and the probe surface was larger than 60 degree; while working on the new PA mode, the fibers could be visualized without any problem even when the angle between the fibers and the probe surface was larger than 75 degree. Moreover, with PA imaging function integrated, the optical fibers positioned into the target tissue, besides delivering optical energy for thermotherapy, can also be used to generate PA signals for on-line evaluation of LITT. Powered by our recently developed PA physio-chemical analysis, PA measurements from the tissue can provide a direct and accurate feedback of the tissue responses to laser ablation, including the changes in not only chemical compositions but also histological microstructures. The initial experiment on the rat liver model has demonstrated the excellent sensitivity of PA imaging to the changes in tissue temperature rise and tissue status (from native to coagulated) when the tissue is treated in vivo with LITT.

  7. Welding of a metal-polymer laminate

    NARCIS (Netherlands)

    Gower, H.L.

    2007-01-01

    The purpose of this work is to investigate the weldability of a metal polymer sandwich structure. The welding of the sandwich material proceeds first by welding of the skin layer. The material selected for this research is Steelite, a sandwich structure developed by Corus, with 0.12 mm thick mild

  8. Defects detection on the welded reinforcing steel with self-shielded wires by vibration tests

    Directory of Open Access Journals (Sweden)

    Crâştiu Ion

    2017-01-01

    Full Text Available The aim of this paper is the development and validation of a vibroacustic technique to welding defects detection, especially for welded reinforcing structures. In welded structures subjected to dynamic cyclic loads may appear and propagate fatigue cracks due to local structural damage. These cracks may initiate due to the technological parameters used in welding process, or due to environmental operating conditions. By the means of Finite Element Method (FEM, the natural frequencies and shape modes of more welded steel specimens are determined. The analysis is carried out in undamaged condition as well as damaged one, after artificially induced damages. The experimental measurement of the vibroacustic response is carried out by using a condenser microphone, which is suitable for high-fidelity acoustic measurements in the frequency range of 20 – 20.000 Hz. The vibration responses of the welded specimens, in free-free conditions, are carried out using algorithms based on Fast Fourier Transform (FFT, and Prony's series. The results are compared to modal parameters estimated using FE Analysis.

  9. Laser Submerged Arc Welding (LUPuS) with Solid State Lasers

    Science.gov (United States)

    Reisgen, Uwe; Olschok, Simon; Jakobs, Stefan

    The laser beam-submerged arc hybrid welding method originates from the knowledge that, with increasing penetration depth, the laser beam process has a tendency to pore formation in the lower weld regions. The coupling with the energy-efficient submerged-arc process improves degassing and reduces the tendency to pore formation. The newly developed hybrid welding process allows the welding of plates with a thickness larger than 20 mm in a single pass and the welding of thicker plates with the double-sided single pass technique. In this special hybrid process, the use of CO2-lasers causes problems when forward sliding flux of slag meets the laser beam path and forms an uncontrollable plasma plume in the beam path. This plasma then shields the work piece from the laser power and thus provokes the collapse of the laser keyhole and leads to process instability. The substitution of the CO2-laser with a modern solid-state laser significantly improves the performance and the stability of the hybrid process. This contribution will demonstrate the latest results and improvements by means of welding results gained with steel plates with a thickness of up to 40mm.

  10. Friction stir welding of F82H steel for fusion applications

    Energy Technology Data Exchange (ETDEWEB)

    Noh, Sanghoon, E-mail: shnoh@kaeri.re.kr [Fusion Structural Materials Division, Japan Atomic Energy Agency, Rokkasho, Aomori (Japan); Nuclear Materials Division, Korea Atomic Energy Research Institute, Yuseong-gu, Daejeon (Korea, Republic of); Ando, Masami; Tanigawa, Hiroyasu [Fusion Structural Materials Division, Japan Atomic Energy Agency, Rokkasho, Aomori (Japan); Fujii, Hidetoshi [Joining and Welding Research Institute, Osaka University, Ibaraki, Osaka (Japan); Kimura, Akihiko [Institute of Advanced Energy, Kyoto University, Gokasho, Uji, Kyoto (Japan)

    2016-09-15

    In the present study, friction stir welding was employed to join F82H steels and develop a potential joining technique for a reduced activation ferritic/martensitic steel. The microstructures and mechanical properties on the joint region were investigated to evaluate the applicability of friction stir welding. F82H steel sheets were successfully butt-joined with various welding parameters. In welding conditions, 100 rpm and 100 mm/min, the stirred zone represented a comparable hardness distribution with a base metal. Stirred zone induced by 100 rpm reserved uniformly distributed precipitates and very fine ferritic grains, whereas the base metal showed a typical tempered martensite with precipitates on the prior austenite grain boundary and lath boundary. Although the tensile strength was decreased at 550 °C, the stirred zone treated at 100 rpm showed comparable tensile behavior with base metal up to 500 °C. Therefore, friction stir welding is considered a potential welding method to preserve the precipitates of F82H steel.

  11. Joining of hybrid AA6063-6SiCp-3Grp composite and AISI 1030 steel by friction welding

    Directory of Open Access Journals (Sweden)

    N. Rajesh Jesudoss Hynes

    2017-10-01

    Full Text Available Joining of metals and aluminium hybrid metal matrix composites has significant applications in aviation, ship building and automotive industries. In the present work, investigation is carried out on Friction Welding of AISI 1030 steel and hybrid AA6063-6SiCp-3Grpcomposite, that are difficult to weld by fusion welding technique. Silicon carbide and graphite particle reinforced AA6063 matrix hybrid composite was developed successfully using stir casting method and the joining feasibility of AISI1030 steel with AA6063-6SiCp-3Grp hybrid composite was tried out by friction stud welding technique. During friction stage of welding process, the particulates (SiC & Graphite used for reinforcement, tend to increase the viscosity and lead to improper mixing of matrix and reinforcement. This eventually results in lower strength in dissimilar joints. To overcome this difficulty AA1100 interlayer is used while joining hybrid composite to AISI 1030 steel. Experimentation was carried out using Taguchi based design of experiments (DOE technique. Multiple regression methods were applied to understand the relationship between process parameters of the friction stud welding process. Micro structural examination reveals three separate zones namely fully plasticized zone, partially deformed zone and unaffected base material zone. Ultra fine dynamically recrystallized grains of about 341 nm were observed at the fully plasticized zone. EDX analysis confirms the presence of intermetallic compound Fe2Al5 at the joint interface. According to the experimental analysis using DOE, rotational speed and interlayer sheet thickness contribute about 39% and 36% respectively in determining the impact strength of the welded joints. It is found that joining with 0.5 mm interlayer sheet provides efficient joints. Developed regression model could be used to predict the axial shortening distance and impact strength of the welded joint with reasonable accuracy.

  12. Highly efficient welding power supply. Final report, May 1, 1978-September 30, 1980

    Energy Technology Data Exchange (ETDEWEB)

    Thommes, J M

    1980-09-01

    The results and findings of an energy efficient welding power development project are presented. The power source developed is to be used for electric arc welding processes in which 3.5 trillion Btu of energy (1978 example year) can be saved annually. The power source development incorporates the use of switch mode power supply techniques in order to convert industrial supply mains (230/460 VAC 3 phi 60 Hz) to appropriate welding voltages and currents (up to 32 volts/up to 300 amps). A series capacitor switch mode power circuit was the circuit technique chosen in order to optimize energy efficiency, costs, reliability, size/weight, and welding performance. Test results demonstrated an effective efficiency (taking into account idle power consumption) of 80 to 91% for the energy efficient power source while the conventional types of power sources tested ranged from 41 to 74% efficiency. Line power factor was also improved for the energy efficient power source. Field tests indicated additional refinements of weld process performance and power source audible noise emission reduction could be beneficial.

  13. Effect of buffer-layered buttering on microstructure and mechanical properties of dissimilar metal weld joints for nuclear plant application

    Energy Technology Data Exchange (ETDEWEB)

    Rathod, Dinesh W., E-mail: dineshvrathod@gmail.com [Department of Mechanical Enggineering, Indian Institute of Technology Delhi, Hauz-khas, New Delhi 110016 (India); Singh, P.K. [Bhabha Atomic Research Centre, Mumbai 400085 (India); Pandey, Sunil; Aravindan, S. [Department of Mechanical Enggineering, Indian Institute of Technology Delhi, Hauz-khas, New Delhi 110016 (India)

    2016-06-01

    In this study, we present the metallurgical and mechanical investigation of four dissimilar welds between SA508Gr.3Cl.1 and SS304LN. The welding processes for buttering deposition and fill-pass welding were varied with ERNiCr-3/ENiCrFe-3 consumables. The Ni-Fe alloy buffer layer was introduced as intermediate layer in buttering and then the joints (with and without buffer layer in buttering) were fabricated. The effect of Ni-Fe buffer layered buttering and welding processes on the resulting weld joints properties has been addressed. Metallurgical and mechanical properties, fracture toughness were measured and various examinations were carried out for integrity assessment on all the weld joints. Addition of a Ni-Fe buttering layer leads to the development of more favourable properties than observed in welded joints made using the current practice without a buffer layer. Control of carbon migration and its subsequent effect on metallurgical, mechanical properties due to buffer layer has been justified in the study. Conventional procedure of DMW fabrication has been proven to be the least favourable against the new technique suggested. Modification in current integrity assessment procedure would be possible by considering the properties at interfacial regions, introduction of yield strength ratio mismatch and the plastic instability strength in the integrity assessment.

  14. A newly developed snow vehicle (SM100S) for Antarctica. Part 3: Low temperature toughness of the welded joints of the structural steel

    Science.gov (United States)

    Sakui, Shin; Nakajima, Masashi

    1992-11-01

    For the purpose of developing a new snow vehicle (common use at temperature about -50 C) for the deep ice coring project at Dome Fuji, East Antarctica, the low temperature toughness of the welded joints of structural steel was investigated. It is empirically well known that in case of vehicles employed in a cold air temperature of about -50 C, the low temperature brittle fracture of the structural members does not take place, if one uses semi-killed or killed steel, for which 50 percent FATT's (fracture appearance transition temperature) of the Charpy impact test is about -50 C and Charpy impact values at -50 C are 20 to 29 J/sq cm. In the present report, the Charpy impact test has been performed for both single pass SMAW (shield metal arc welding) and CO2 arc welded joints of JIS (Japan Industrial Standards) steels of SS400, SL2N255, STPL380, and STPL450. The test results show that the JIS steels of SL2N255 and STPL450 can be used for the new vehicle, considering their toughness.

  15. Analysis and Comparison of Friction Stir Welding and Laser Assisted Friction Stir Welding of Aluminum Alloy.

    Science.gov (United States)

    Campanelli, Sabina Luisa; Casalino, Giuseppe; Casavola, Caterina; Moramarco, Vincenzo

    2013-12-18

    Friction Stir Welding (FSW) is a solid-state joining process; i.e. , no melting occurs. The welding process is promoted by the rotation and translation of an axis-symmetric non-consumable tool along the weld centerline. Thus, the FSW process is performed at much lower temperatures than conventional fusion welding, nevertheless it has some disadvantages. Laser Assisted Friction Stir Welding (LAFSW) is a combination in which the FSW is the dominant welding process and the laser pre-heats the weld. In this work FSW and LAFSW tests were conducted on 6 mm thick 5754H111 aluminum alloy plates in butt joint configuration. LAFSW is studied firstly to demonstrate the weldability of aluminum alloy using that technique. Secondly, process parameters, such as laser power and temperature gradient are investigated in order to evaluate changes in microstructure, micro-hardness, residual stress, and tensile properties. Once the possibility to achieve sound weld using LAFSW is demonstrated, it will be possible to explore the benefits for tool wear, higher welding speeds, and lower clamping force.

  16. Effect of Post-Weld Heat Treatment on Creep Rupture Properties of Grade 91 Steel Heavy Section Welds

    Energy Technology Data Exchange (ETDEWEB)

    Li, Leijun

    2012-11-02

    This project will conduct a systematic metallurgical study on the effect of post-weld heat treatment (PWHT) on the creep rupture properties of P91 heavy section welds. The objective is to develop a technical guide for selecting PWHT parameters, and to predict expected creep-rupture life based on the selection of heat treatment parameters. The project consists of four interdependent tasks: Experimentally and numerically characterize the temperature fields of typical post-weld heat treatment procedures for various weld and joint configurations to be used in Gen IV systems. Characterize the microstructure of various regions, including the weld fusion zone, coarse-grain heat-affected zone, and fine-grain heat affected zone, in the welds that underwent the various welding and PWHT thermal histories. Conduct creep and creep-rupture testing of coupons extracted from actual and physically simulated welds. Establish the relationship among PWHT parameters, thermal histories, microstructure, creep, and creep-rupture properties.

  17. Sensor based robot laser welding - based on feed forward and gain sceduling algorithms

    DEFF Research Database (Denmark)

    Andersen, Henrik John

    2001-01-01

    A real-time control system forlaser welding of thick steel plates are developed and tested in a industrial environment. The robotic execution of the laser welding process is based on measure weld joint geometry and impirically established welding procedures. The influence of industrial production...

  18. A COMPARATIVE STUDY OF GROOVE DESIGN AND WELDING PROCESS ON SHRINKAGE STRESS, RESIDUAL STRESS AND TENSILE PROPERTIES OF P91 STEEL

    OpenAIRE

    Vinay Kumar Pal*, Dr. L. P. Singh, C.Pandey

    2017-01-01

    Present research work deals with the selection of appropriate range of welding parameters and procedure that is used for conventional and narrow groove welding of thick sections at different welding process.The development of narrow gap welding procedure by P-GMAW process is carried out for joining of thick sections by appropriate reduction in number of weld passes and amount of weld metal. Study of the effect of variation in groove design and welding processes was performed by summarizing th...

  19. Critical Assessment of Temperature Distribution in Submerged Arc Welding Process

    Directory of Open Access Journals (Sweden)

    Vineet Negi

    2013-01-01

    Full Text Available Temperature distribution during any welding process holds the key for understanding and predicting several important welding attributes like heat affected zone, microstructure of the weld, residual stress, and distortion during welding. The accuracy of the analytical approaches for modeling temperature distribution during welding has been constrained by oversimplified assumptions regarding boundary conditions and material properties. In this paper, an attempt has been made to model the temperature distribution during submerged arc welding process using finite element modeling technique implemented in ANSYS v12. In the present analysis, heat source is assumed to be double-ellipsoidal with Gaussian volumetric heat generation. Furthermore, variation of material properties with temperature and both convective and radiant heat loss boundary condition have been considered. The predicted temperature distribution is then validated against the experimental results obtained by thermal imaging of the welded plate, and they are found to be in a good agreement.

  20. Low temperature friction stir welding of P91 steel

    Directory of Open Access Journals (Sweden)

    Prasad Rao Kalvala

    2016-08-01

    Full Text Available Bead-on-plate friction stir welds were made on P91 alloy with low and high rotational speeds (100 and 1000 RPM to study their effects on weld microstructural changes and impression creep behavior. Temperatures experienced by the stir zone were recorded at the weld tool tip. Different zones of welds were characterized for their microstructural changes, hardness and creep behavior (by impression creep tests. The results were compared with submerged arc fusion weld. Studies revealed that the stir zone temperature with 100 RPM was well below Ac1 temperature of P91 steel while it was above Ac3 with 1000 RPM. The results suggest that the microstructural degradation in P91 welds can be controlled by low temperature friction stir welding technique.

  1. PRODUCTION OF METAL CHEMICAL WELDING ADDITIVE WITH NANODISPERSED PARTICLES OF TITANIUM DIOXIDE

    Directory of Open Access Journals (Sweden)

    BOLDYREV Alexander Mikhaylovich

    2013-12-01

    Full Text Available When welding bridge structures automatic welding under a gumboil layer with metal chemical additive (MCA is widely applied in the modern bridge building. MCA consists of a chopped welding wire (granulated material, which is powdered by modifying chemical additive of titanium dioxide (TiO₂ in the cylindrical mixer «drunk cask». Chemical composition of all welding materials including welding wire, gumboil, electrodes, are strictly normalized and controlled. However, the existing technology of producing MCA doesn’t allow precise controlling of its structure under working conditions and that causes an impact on the stability of welded connections properties. Therefore the aim of this work is to develop a technology to produce stable MCA structure. The paper compares the existing and proposed manufacturing techniques of the metal chemical additive (MCA which is applied in automatic welding of butt connections for bridge structures. It is shown that production of MCA in a high-energy planetary mill provides more stable structure of the additive introduced into a welded joint. The granulometric analysis of the powder TiO₂ showed that when processing MCA in a planetary mill TiO₂ particles are crashed to nanodimensional order. This process is accompanied by crushing of granulated material too. The proposed method for production of MCA in a planetary mill provides stronger cohesion of dioxide with the granulate surface and, as a consequence, more stable MCA chemical structure. Application of MCA which has been mechanical intensified in a planetary mill, increases stability of mechanical properties, if compare with applied technology, in single-order by breaking point and almost twice by impact viscosity.

  2. Testing and Debugging Techniques for Answer Set Solver Development

    OpenAIRE

    Brummayer, Robert; Järvisalo, Matti

    2010-01-01

    This paper develops automated testing and debugging techniques for answer set solver development. We describe a flexible grammar-based black-box ASP fuzz testing tool which is able to reveal various defects such as unsound and incomplete behavior, i.e. invalid answer sets and inability to find existing solutions, in state-of-the-art answer set solver implementations. Moreover, we develop delta debugging techniques for shrinking failure-inducing inputs on which solvers exhibit defective behavi...

  3. Weld microstructure and hardness prediction for in-service hot-tap welds

    Energy Technology Data Exchange (ETDEWEB)

    Wentao Cheng; Yong-Yi Wang [Engineering Mechanics Corporation of Columbus, OH (United States)]. E-mail: wcheng@emc-sq.com; ywang@emc-sq.com; Amend, William [Southern California Gas Co., Los Angeles, CA (United States)]. E-mail: bamend@semprautilities.com

    2005-07-01

    Welding onto an in-service pipeline is frequently required to repair damaged areas and for system modifications. There are often significant economic and environmental incentives to perform in-service welding, including the ability to maintain operations during welding and to avoid venting the contents to the atmosphere. Welds made onto in-service pipelines tend to cool at an accelerated rate. These welds are likely to have high heat-affected zone (HAZ) hardness which increases their susceptibility to hydrogen cracking. Accurate prediction of HAZ hardness is critical in developing successful welding procedures for in-service hot-tap welds. The present PRCI thermal analysis software for hot-tap welding uses an empirical-formula-based HAZ hardness prediction procedure. This paper describes an effort funded by PRCI to produce a significantly improved HAZ hardness prediction procedure over the procedure in the current PRCI thermal analysis software. A markedly improved hardness prediction procedure was developed and systematically validated using extensive experimental data of actual welds. The underlying hardness calculation algorithms were based on the proven state-of-the-art phase transformation models. Although on the average the procedure under-predicts the measured hardness by a small amount, the new hardness prediction procedure is a significant improvement in overall accuracy over the procedure in the current PRCI thermal analysis software. The procedure developed here lays the foundation for a much more accurate hardness prediction module in the future version of the PRCI thermal analysis software. (author)

  4. Microstructure characterization of Friction Stir Spot Welded TRIP steel

    DEFF Research Database (Denmark)

    Lomholt, Trine Colding; Adachi, Yoshitaka; Peterson, Jeremy

    2012-01-01

    Transformation Induced Plasticity (TRIP) steels have not yet been successfully joined by any welding technique. It is desirable to search for a suitable welding technique that opens up for full usability of TRIP steels. In this study, the potential of joining TRIP steel with Friction Stir Spot...

  5. Reprocessing weld and method

    Energy Technology Data Exchange (ETDEWEB)

    Killian, M.L.; Lewis, H.E.

    1993-08-03

    A process is described for improving the fatigue resistance of a small primary structural weld at a joint between structural members of a weldment, the weld having been made with the welding energy input of E[sub 1], the process comprising: applying a reprocessing weld on at least a portion of either one or both toes of the primary structural weld, thereby covering said toe portion, the reprocessing weld containing a filler metal and having a cross-sectional area which is less than the corresponding cross-sectional area of the primary structural weld, the reprocessing weld extending onto the face of the primary structural weld at one side of the toe portion covered and onto the structural member at the other side of the toe portion covered, and the total welding energy input, E[sub 2], used in said reprocessing the primary structural weld being less than the welding energy input E[sub 1] of the primary structural weld.

  6. Virtual Welded-Joint Design Integrating Advanced Materials and Processing Technologies

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Z.; Dong, P.; Liu, S.; Babu, S.; Olson, G.; DebRoy, T.

    2005-04-15

    The primary goal of this project is to increase the fatigue life of a welded-joint by 10 times and to reduce energy use by 25% through product performance and productivity improvements using an integrated modeling approach. The fatigue strength of a welded-joint is currently the bottleneck to design high performance and lightweight welded structures using advanced materials such as high strength steels. In order to achieve high fatigue strength in a welded-joint it is necessary to manage the weld bead shape for lower stress concentration, produce preferable residual stress distribution, and obtain the desired microstructure for improved material toughness and strength. This is a systems challenge that requires the optimization of the welding process, the welding consumable, the base material, as well as the structure design. The concept of virtual welded-joint design has been proposed and established in this project. The goal of virtual welded-joint design is to develop a thorough procedure to predict the relationship of welding process, microstructure, property, residual stress, and the ultimate weld fatigue strength by a systematic modeling approach. The systematic approach combines five sub-models: weld thermal-fluid model, weld microstructure model, weld material property model, weld residual stress model, and weld fatigue model. The systematic approach is thus based on interdisciplinary applied sciences including heat transfer, computational fluid dynamics, materials science, engineering mechanics, and material fracture mechanics. The sub-models are based on existing models with further development. The results from modeling have been validated with critical experiments. The systematic modeling approach has been used to design high fatigue resistant welds considering the combined effects of weld bead geometry, residual stress, microstructure, and material property. In particular, a special welding wire has been developed in this project to introduce

  7. Using the Delphi Technique to Support Curriculum Development

    Science.gov (United States)

    Sitlington, Helen Barbara; Coetzer, Alan John

    2015-01-01

    Purpose: The purpose of this paper is to present an analysis of the use of the Delphi technique to support curriculum development with a view to enhancing existing literature on use of the technique for renewal of business course curricula. Design/methodology/approach: The authors outline the Delphi process for obtaining consensus amongst a…

  8. SLAM examination of solar cells and solar cell welds

    Science.gov (United States)

    Stella, P. M.; Vorres, C. L.; Yuhas, D. E.

    The scanning laser acoustic microscope (SLAM) has been evaluated for non-destructive examination of solar cells and interconnector bonds. Using this technique, it is possible to view through materials in order to reveal regions of discontinuity such as microcracks and voids. Of particular interest is the ability to evaluate, in a unique manner, the bonds produced by parallel gap welding. It is possible to not only determine the area and geometry of the bond between the tab and cell, but also to reveal any microcracks incurred during the welding. By correlating the SLAM results with conventional techniques of weld evaluation a more confident weld parameter optimization can be obtained.

  9. Heat Sink Welding for Preventing Hot Cracking in Alloy 2195 Intersection Welds: A Feasibility Study

    Science.gov (United States)

    Yang, Yu-Ping; Dong, Pingsha; Rogers, Patrick

    2000-01-01

    Two concepts, stationary cooling and trailing cooling, were proposed to prevent weld intersection cracking. Finite element analysis was used to demonstrate the potential effectiveness of those two concepts. Both stationary and trailing heat sink setups were proposed for preventing intersection cracking. The cooling media could be liquid nitrogen, or pressured air knife. Welding experiments on the small test panel with the localized heat sink confirmed the feasibility of using such a stationary cooling technique. The required cooling was achieved in this test panel. Systematic welding experiments should be conducted in the future to validate and refine the heat sink technique for preventing intersection cracking.

  10. Handbook of Plastic Welding

    DEFF Research Database (Denmark)

    Islam, Aminul

    The purpose of this document is to summarize the information about the laser welding of plastic. Laser welding is a matured process nevertheless laser welding of micro dimensional plastic parts is still a big challenge. This report collects the latest information about the laser welding of plastic...... materials and provides an extensive knowhow on the industrial plastic welding process. The objectives of the report include: - Provide the general knowhow of laser welding for the beginners - Summarize the state-of-the-art information on the laser welding of plastics - Find the technological limits in terms...... of design, materials and process - Find the best technology, process and machines adaptive to Sonion’s components - Provide the skills to Sonion’s Design Engineers for successful design of the of the plastic components suitable for the laser welding The ultimate goal of this report is to serve...

  11. Identification of the Quality Spot Welding used Non Destructive Test-Ultrasonic Testing: (Effect of Welding Time)

    Science.gov (United States)

    Sifa, A.; Endramawan, T.; Badruzzaman

    2017-03-01

    Resistance Spot Welding (RSW) is frequently used as one way of welding is used in the manufacturing process, especially in the automotive industry [4][5][6][7]. Several parameters influence the process of welding points. To determine the quality of a welding job needs to be tested, either by damaging or testing without damage, in this study conducted experimental testing the quality of welding or identify quality of the nugget by using Non-Destructive Test (NDT) -Ultrasonic Testing (UT), in which the identification of the quality of the welding is done with parameter thickness of worksheet after welding using NDT-UT with use same material worksheet and have more thickness of worksheet, the thickness of the worksheet single plate 1mm, with the capability of propagation Ultrasonic Testing (UT) standard limited> 3 mm [1], welding process parameters such as the time difference between 1-10s and the welding current of 8 KV, visually Heat Affected Zone ( HAZ ) have different results due to the length of time of welding. UT uses a probe that is used with a frequency of 4 MHz, diameter 10 mm, range 100 and the couplant used is oil. Identification techniques using drop 6dB, with sound velocity 2267 m / s of Fe, with the result that the effect of the Welding time affect the size of the HAZ, identification with the lowest time 1s show results capable identified joined through NDT - UT.

  12. A comparison of two types of neural network for weld quality prediction in small scale resistance spot welding

    Science.gov (United States)

    Wan, Xiaodong; Wang, Yuanxun; Zhao, Dawei; Huang, YongAn

    2017-09-01

    Our study aims at developing an effective quality monitoring system in small scale resistance spot welding of titanium alloy. The measured electrical signals were interpreted in combination with the nugget development. Features were extracted from the dynamic resistance and electrode voltage curve. A higher welding current generally indicated a lower overall dynamic resistance level. A larger electrode voltage peak and higher change rate of electrode voltage could be detected under a smaller electrode force or higher welding current condition. Variation of the extracted features and weld quality was found more sensitive to the change of welding current than electrode force. Different neural network model were proposed for weld quality prediction. The back propagation neural network was more proper in failure load estimation. The probabilistic neural network model was more appropriate to be applied in quality level classification. A real-time and on-line weld quality monitoring system may be developed by taking advantages of both methods.

  13. The Influence of Friction Stir Weld Tool Form and Welding Parameters on Weld Structure and Properties: Nugget Bulge in Self-Reacting Friction Stir Welds

    Science.gov (United States)

    Schneider, Judy; Nunes, Arthur C., Jr.; Brendel, Michael S.

    2010-01-01

    Although friction stir welding (FSW) was patented in 1991, process development has been based upon trial and error and the literature still exhibits little understanding of the mechanisms determining weld structure and properties. New concepts emerging from a better understanding of these mechanisms enhance the ability of FSW engineers to think about the FSW process in new ways, inevitably leading to advances in the technology. A kinematic approach in which the FSW flow process is decomposed into several simple flow components has been found to explain the basic structural features of FSW welds and to relate them to tool geometry and process parameters. Using this modelling approach, this study reports on a correlation between the features of the weld nugget, process parameters, weld tool geometry, and weld strength. This correlation presents a way to select process parameters for a given tool geometry so as to optimize weld strength. It also provides clues that may ultimately explain why the weld strength varies within the sample population.

  14. Fine particles in welding workshop; Hitsaamon pienhiukkaset

    Energy Technology Data Exchange (ETDEWEB)

    Haenninen, H.; Koskinen, A. [Helsinki Unviv. of Technology, Materials Sciences and Engineering, Espoo (Finland)

    2006-10-15

    The objectives of the project were to research ultra- fine particles developed in the welding and cutting processes, to classify the particles in the welding fume, as well as to assess how they transform in air and drift in the internal air. Also it was attempted to decrease the amount of ultra-fine particles in the welding processes and in the internal air. Experiments were performed in the laboratory environments so that the results are valid and comparable. The fine particles in the fumes were measured and sampled by cascade impactors (ELPI, DLPI), by SMPS and by filter samplers (personal and area). The composition, size, shape and activity of the particles were determined. During the project efficiency of personal welding helmets, fume extraction welding guns and MFI-precipitator were tested. Tests were carried out in the laboratory and in the industrial workshops. The three-year project started in the beginning of February 2003. (orig.)

  15. The Establishment of a New Friction Stir Welding Process Development Facility at NASA/MSFC

    Science.gov (United States)

    Vaughn, Timothy P.

    2012-01-01

    The primary objective of full scale development is to mitigate scale-up issues before the vehicle ever reaches production and verify assembly design models. Only at full scale can the true challenges associated with production be identified and dealt with. Also, only at full scale can the delta shift between lab and subscale hardware manufacture and assembly be assessed.

  16. Friction stir welding of Aluminium matrix composites – A Review

    Directory of Open Access Journals (Sweden)

    Subramanya Prabhu

    2018-01-01

    Full Text Available Friction stir welding (FSW is established as one of the prominent welding techniques to join aluminium matrix composites (AMCs. It is a solid state welding process, takes place well below the melting temperature of the material, eliminates the detrimental effects of conventional fusion welding process. Although the process is capable to join AMCs, challenges are still open that need to be fulfill to widen its applications. This paper gives the outline of the friction stir welding technique used to join AMCs. Effect of process variables on the microstructure and mechanical properties of the joints, behavior of reinforcing materials during welding, effect of tool profiles on the joint strength are discussed in detail. Few improvements and direction for future research are also proposed.

  17. Fatigue Crack Growth in Peened Friction Stir Welds

    Science.gov (United States)

    Forth, Scott C.; Hatamleh, Omar

    2008-01-01

    Friction stir welding induces residual stresses that accelerates fatigue crack growth in the weld nugget. Shot peening over the weld had little effect on growth rate. Laser peening over the weld retarded the growth rate: Final crack growth rate was comparable to the base, un-welded material. Crack tunneling evident from residual compressive stresses. 2195-T8 fracture surfaces were highly textured. Texturing makes comparisons difficult as the material system is affecting the data as much as the processing. Material usage becoming more common in space applications requiring additional work to develop useful datasets for damage tolerance analyses.

  18. Numerical modeling of electron-beam welding of dissimilar metals

    Science.gov (United States)

    Krektuleva, R. A.; Cherepanov, O. I.; Cherepanov, R. O.

    2016-11-01

    This paper is devoted to numerical modeling of heat transfer processes and estimation of thermal stresses in weld seams created by electron beam welding of heterogeneous metals. The mathematical model is based on a system of equations that includes the Lagrange's variational equation of theory of plasticity and variational equation of M. Biot's principle to simulate the heat transfer processes. The two-dimensional problems (plane strain and plane stress) are considered for estimation of thermal stresses in welds considering differences of mechanical properties of welded materials. The model is developed for simulation of temperature fields and stresses during electron beam welding.

  19. Development of automated welding process for field fabrication of thick walled pressure vessels. Technical progress report, second quarter, FY 1980, ending March 28, 1980

    Energy Technology Data Exchange (ETDEWEB)

    Schneider, U.A.

    1980-01-01

    Progress on a metallurgical contract is reported: (1) specifications of 2 1/4 chromium-1 molybdenum low alloy steel plate for a coal gasification project; (2) methods of welding and analyses of helium-argon mixtures for welding; and (3) tensile properties of welded joints. (LTN)

  20. Instructional Guidelines. Welding.

    Science.gov (United States)

    Fordyce, H. L.; Doshier, Dale

    Using the standards of the American Welding Society and the American Society of Mechanical Engineers, this welding instructional guidelines manual presents a course of study in accordance with the current practices in industry. Intended for use in welding programs now practiced within the Federal Prison System, the phases of the program are…

  1. Determination of the sensitization of two coatings by steel welding 308l by the EPR-Dl and Astm A-262 practice A techniques; Determinacion de la sensibilizacion de dos revestimientos por soldadura de acero 308L por las tecnicas EPR-DL y ASTM A-262 practica A

    Energy Technology Data Exchange (ETDEWEB)

    Arganis J, C. R.; Zenteno S, J. C.; Robles F, J. L.; Rodriguez M, E.; Vazquez P, A., E-mail: carlos.arganis@inin.gob.mx [ININ, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico)

    2014-10-15

    A stainless steel 308l coating was deposited by the shielded metal arc welding (SMAW) on steel A36 with a thickness of 4.726 mm in three layers. The sensitization was measured with the technique of Electrochemical Potentiodynamic Reactivation of Double-loop (EPR-Dl), using a portable cell and other of conventional window. The standard Astm A-262, practice A was used to verify the sensitization values. Two samples were used, a welding on a plate of 323 x 172 x 76.2 mm and the second welding on the end of a plate of 12.7 mm of thickness and 280 mm of longitude, with a post-welding process with gas tungsten arc welding (GTAW) with electrode ERNiCr{sub 3} and a process SMAW with electrode ENICRFe{sub 3}. The coating on the plate showed low values of sensitization grade (DOS) in all the points, indicating a very quick heat extraction and an inter dendritic structure type step. The second sample presented DOS values that are related with a structure of low sensitization and the influence of the heat of the post-welding process and a structure of recrystallized grains. (Author)

  2. Weld-brazing of titanium

    Science.gov (United States)

    Bales, T. T.; Royster, D. M.; Arnold, W. E., Jr.

    1974-01-01

    A joining process, designated weld-brazing, which combines resistance spotwelding and brazing has been developed at the NASA Langley Research Center. Resistance spot-welding is employed to position and align the parts and to establish a suitable faying surface gap for brazing; it contributes to the integrity of the joint. Brazing enhances the properties of the joint and reduces the stress concentrations normally associated with spotwelds. Ti-6Al-4V titanium alloy joints have been fabricated using 3003 aluminum braze both in a vacuum furnace and in a retort containing an inert gas environment.

  3. Performance of repair welds on aged Cr-Mo piping girth welds

    Science.gov (United States)

    Viswanathan, R.; Gandy, D. W.

    1999-10-01

    This article documents the results of an industry survey of weld repair practices and describes the results of experimental evaluations performed on service-aged 21/4 Cr-1Mo steel piping using SMAW with both conventional postweld heat treatments and temper bead repair techniques. The overall results of this program provide substantial evidence that service-aged piping systems can be successfully weld repaired with and without postweld heat treatments and that life extension by several decades is achievable under the right design and repair conditions. Weld repairs performed on degraded exservice welds resulted in restoration or improvement of tensile and creep properties. Microhardness test results within the heat-affected zone of each weldment indicated that the temper bead weld repairs produced only slightly higher peak hardness values than those measured for the fully postweld heat treated repairs. Finally, in terms of toughness, temper bead weld repairs consistently produced higher impact properties than those measured for the postweld heat treated weldments. Gas tungsten arc weld repairs with postweld heat treatment resulted in the best combination of tensile strength, uniform microhardness distribution across the weld, Charpy toughness, and creep rupture life.

  4. Modeling and experimental investigation of induction welding of thermoplastic composites and comparison with other welding processes

    NARCIS (Netherlands)

    Gouin O'Shaughnessey, P.; Dube, M; Fernandez Villegas, I.

    2016-01-01

    A three-dimensional finite element model of the induction welding of carbon fiber/polyphenylene sulfide thermoplastic composites is developed. The model takes into account a stainless steel mesh heating element located at the interface of the two composite adherends to be welded. This heating

  5. A study of gas flow pattern, undercutting and torch modification in variable polarity plasma arc welding

    Science.gov (United States)

    Mcclure, John C.; Hou, Haihui Ron

    1994-01-01

    A study on the plasma and shield gas flow patterns in variable polarity plasma arc (VPPA) welding was undertaken by shadowgraph techniques. Visualization of gas flow under different welding conditions was obtained. Undercutting is often present with aluminum welds. The effects of torch alignment, shield gas flow rate and gas contamination on undercutting were investigated and suggestions made to minimize the defect. A modified shield cup for the welding torch was fabricated which consumes much less shield gas while maintaining the weld quality. The current torch was modified with a trailer flow for Al-Li welding, in which hot cracking is a critical problem. The modification shows improved weldablility on these alloys.

  6. Assessing mechanical properties of the dissimilar metal welding between P92 steels and alloy 617 at high temperature

    Energy Technology Data Exchange (ETDEWEB)

    Lee, J. H.; Hwang, J. H.; Park, Y. S.; Kim, T. M.; Bae, D. H. [Sungkyunkwan University, Suwon (Korea, Republic of); Seo, W. B. [Institute of Mechanical Engineering, Yeungnam University, Daegu (Korea, Republic of); Han, J. W. [School of Mechanical Engineering, Hoseo University, Cheonan (Korea, Republic of)

    2016-10-15

    In this study, a new welding technology of dissimilar materials, Cr-based P92 steels and Ni-based Alloy 617 is introduced and demonstrated to investigate its reliability. Firstly, multi-pass dissimilar metal welding between P92 steel and Alloy 617 was performed using DCEN TIG welding technology, buttering welding technique and a narrow gap groove. After welding, in order to understand characteristics of the dissimilar metal welds, metallurgical micro-structures analysis by optical observation and static tensile strength assessment of the dissimilar welded joints were conducted at 700°C.

  7. Heat sink effects in VPPA welding

    Science.gov (United States)

    Steranka, Paul O., Jr.

    1990-01-01

    The development of a model for prediction of heat sink effects associated with the Variable Polarity Plasma Arc (VPPA) Welding Process is discussed. The long term goal of this modeling is to provide means for assessing potential heat sink effects and, eventually, to provide indications as to changes in the welding process that could be used to compensate for these effects and maintain the desired weld quality. In addition to the development of a theoretical model, a brief experimental investigation was conducted to demonstrate heat sink effects and to provide an indication of the accuracy of the model.

  8. The Development of a Snubber Management System for Welds in Nuclear Power Plants

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Hyun Ju; Cho, Yong-Bae; Kim, Yoo Sung [KHNP CRI, Daejeon (Korea, Republic of)

    2016-10-15

    There are snubbers, spring hanger, anchors, rigid supports for the structures which support the static and/or dynamic loads such as thermal load, pressure, impact and vibration from components and pipings of nuclear power plants. Snubbers constrain the displacements generated by loads transmitted to components and systems abruptly. When the loss of function of snubber during normal operation, the thermal load and pressure transmit directly to structures such as pipings and components, and additional loads, which were not considered during the design stage, act on the structures. Therefore, according to regulatory requirement to confirm the stability of supporting system, the inspection for the snubber is reflected to in-service inspection (ISI) and in-service test (IST) plans. In order to comply with the regulatory requirement, KHNP has performed the ISI and IST and inspected the snubbers. As the increment of operating year of nuclear power plants in Korea, the possibility of deterioration of equipment is higher. Therefore, the security related to the integrity of equipment becomes more important. The snubber takes an important role related to the structural integrity equipped on principal pipings. 100% snubbers are inspected during pre-service inspection and 10% snubbers are inspected during in-service inspection as a sample in nuclear power plants in Korea. KHNP has been developed a snubber management system because there was no management tool for snubbers to show the inspection and maintenance results systematically. The inspection and maintenance results of snubbers can be easily reached by plants, head office and CRI. Moreover, the information related to inspection history and condition of snubber can be effectively inquired.

  9. Development Tread and NDT Progress of Metal Additive Manufacture Technique

    Directory of Open Access Journals (Sweden)

    YANG Ping-hua

    2017-09-01

    Full Text Available The application and new development trend of metal additive manufacture technique were introduced, as well as the characteristic and NDT difficulty of metal additive manufacture products. The research progress of NDT was analyzed in emphasis, including the classification of metal additive manufacture technique, the characteristics of defect and microstructure, the influence of defects on mechanical properties, the latest development of NDT methods and standards. Based on that, the key issues that will be focused were summarized at last, that is the application of new NDT methods, on-line monitoring technology, numerical simulation, measurement and characterization of stress, as well as the establishment and development of NDT standards.

  10. Optical sensor for real-time weld defect detection

    Science.gov (United States)

    Ancona, Antonio; Maggipinto, Tommaso; Spagnolo, Vincenzo; Ferrara, Michele; Lugara, Pietro M.

    2002-04-01

    In this work we present an innovative optical sensor for on- line and non-intrusive welding process monitoring. It is based on the spectroscopic analysis of the optical VIS emission of the welding plasma plume generated in the laser- metal interaction zone. Plasma electron temperature has been measured for different chemical species composing the plume. Temperature signal evolution has been recorded and analyzed during several CO2-laser welding processes, under variable operating conditions. We have developed a suitable software able to real time detect a wide range of weld defects like crater formation, lack of fusion, excessive penetration, seam oxidation. The same spectroscopic approach has been applied for electric arc welding process monitoring. We assembled our optical sensor in a torch for manual Gas Tungsten Arc Welding procedures and tested the prototype in a manufacturing industry production line. Even in this case we found a clear correlation between the signal behavior and the welded joint quality.

  11. Development of Improved Oil Field Waste Injection Disposal Techniques

    Energy Technology Data Exchange (ETDEWEB)

    Terralog Technologies

    2002-11-25

    The goals of this project have was to: (1) assemble and analyze a comprehensive database of past waste injection operations; (2) develop improved diagnostic techniques for monitoring fracture growth and formation changes; (3) develop operating guidelines to optimize daily operations and ultimate storage capacity of the target formation; and (4) to apply these improved models and guidelines in the field.

  12. Involute Spur Gear Template Development by Parametric Technique ...

    African Journals Online (AJOL)

    There are many methods available for developing profiles of gear and spline teeth. Most of the techniques are inaccurate because they use only an approximation of the involute curve profile. The parametric method developed in this paper provides accurate involute curve creation using formulas and exact geometric ...

  13. Involute Spur Gear Template Development by Parametric Technique ...

    African Journals Online (AJOL)

    Nekky Umera

    Abstract. There are many methods available for developing profiles of gear and spline teeth. Most of the techniques are inaccurate because they use only an approximation of the involute curve profile. The parametric method developed in this paper provides accurate involute curve creation using formulas and exact ...

  14. Mosquito Control Techniques Developed for the US Military

    Science.gov (United States)

    The USDA developed and field tested new techniques to reduce the risk to deployed military troops from vector-borne diseases. Some of the methods developed included (1) novel military personal protection methods, (2) barrier treatments of artificial materials and natural vegetation, and (3) ground a...

  15. Mechanics Model of Plug Welding

    Science.gov (United States)

    Zuo, Q. K.; Nunes, A. C., Jr.

    2015-01-01

    An analytical model has been developed for the mechanics of friction plug welding. The model accounts for coupling of plastic deformation (material flow) and thermal response (plastic heating). The model predictions of the torque, energy, and pull force on the plug were compared to the data of a recent experiment, and the agreements between predictions and data are encouraging.

  16. Studies regarding the use of a neuro-fuzzy mathematical model in order to determine the technological parameters of the polyethylene pipes butt welding process

    Directory of Open Access Journals (Sweden)

    Gligor Alina

    2017-01-01

    Full Text Available The paper analyzes the possibility to use a neuro-fuzzy type mathematical model, with the final goal of establishing the welding parameters for new types and dimensions of pipes and fittings. Anticipating the developing dynamic of polyethylene-made elements, especially pipes and fittings, starting from the current situation when already a wide range of pipes and fittings with different wall thicknesses and nominal working pressures is produced and commercialized, and taking into account also new development, it was considered necessary to find out the welding parameters for any new pipe type and dimension. The usage of existing welding equipment for new pipe dimensions is impossible without a preliminary set of welding parameters: pressure, temperature, time. Based on experimentally validated data for discreet values of the characteristic welding parameters, there was generated, using mathematical laws and functions, a new model that can estimate the necessary values of the welding parameters for any value within their variation range. As a result, the mathematical model created using neuro-fuzzy techniques allows the obtaining of the correct value for certain parameters (e.g. required welding pressure for any values of the input variables pipe diameter and pipe thickness.

  17. Assessment of delta ferrite in multipass TIG welds of 40 mm thick SS 316L: A comparative study of ferrite number (FN) prediction and measurements

    Science.gov (United States)

    Buddu, Ramesh Kumar; Raole, P. M.; Sarkar, B.

    2017-04-01

    Austenitic stainless steels are widely used in the fabrication of fusion reactor major systems like vacuum vessel, divertor, cryostat and other structural components development. Multipass welding is used for the development of thick plates for the structural components fabrication. Due to the repeated weld thermal cycles, the microstructure adversely alters owing to the presence of complex phases like austenite, ferrite and delta ferrite and subsequently influences the mechanical properties like tensile and impact toughness of joints. The present paper reports the detail analysis of delta ferrite phase in welded region of 40 mm thick SS316L plates welded by special design multipass narrow groove TIG welding process under three different heat input conditions. The correlation of delta ferrite microstructure of different type structures acicular and vermicular is observed. The chemical composition of weld samples was used to predict the Ferrite Number (FN), which is representative form of delta ferrite in welds, with Schaeffler’s, WRC-1992 diagram and DeLong techniques by calculating the Creq and Nieq ratios and compared with experimental data of FN from Feritescope measurements. The low heat input conditions (1.67 kJ/mm) have produced higher FN (7.28), medium heat input (1.72 kJ/mm) shown FN (7.04) where as high heat input (1.87 kJ/mm) conditions has shown FN (6.68) decreasing trend and FN data is compared with the prediction methods.

  18. Optimization and verification of ultrasonic testability of acoustically anisotropic materials on austenitic and dissimilar welds; Optimierung und Nachweis der Ultraschallpruefbarkeit von akustisch anisotropen Werkstoffen an austenitischen Schweiss- und Mischverbindungen

    Energy Technology Data Exchange (ETDEWEB)

    Pudovikov, Sergey

    2013-11-21

    Austenitic and dissimilar welds with respect to the ultrasonic testing (UT) methods are considered normally as ''difficult-to-test'' objects. During the solidification process in such welds a distinct dendrite microstructure evolves, which is coarse-grained, anisotropic and inhomogeneous simultaneously. The reliability of available ultrasonic methods on austenitic welds depends significantly on the selected UT-parameters as well as on the inspection personnel experience. In the present dissertation, an ultrasonic testing method was developed, which allows the flaw detection and evaluation in acoustically anisotropic inhomogeneous materials, especially in austenitic and dissimilar welds with a quantitative statement to the defect size, type, and location. The principle of synthetic focusing with taking into account the material anisotropy and inhomogeneity along with two- and three-dimensional visualization provides a reliable and quantitative assessment of the inspection results in acoustically anisotropic inhomogeneous test objects. Among others, an iterative algorithm for the determination of unknown elastic properties of inhomogeneous anisotropic materials has been developed. It allows practical application of the developed UT method, since the anisotropy of most of austenitic and dissimilar welds (especially of hand-welded joints) in practice is usually unknown. The functionality of the developed inspection technique has been validated by many experiments on welded austenitic specimens having artificial and natural defects. For the practical application of the new ultrasonic technique different testing strategies are proposed, which can be used depending on the current inspection task.

  19. Fluor Hanford Nuclear Material Stabilization Project Welding Manual

    Energy Technology Data Exchange (ETDEWEB)

    BERKEY, J.R.

    2000-10-20

    The purpose of this section of the welding manual is to: (1) Provide a general description of the major responsibilities of the organizations involved with welding. (2) Provide general guidance concerning the application of codes related to welding. This manual contains requirements for welding for all Fluor Hanford (FH) welding operators working on the W460 Project, in the Plutonium Finishing Plant (PFP) at the U. S. Department of Energy (DOE) Hanford facilities. These procedures and any additional requirements for these joining processes can be used by all FH welding operators that are qualified. The Welding Procedure Specifications (WPS) found in this document were established from Procedure Qualification Records (PQR) qualified by FH specifically for the W460 Project. PQRs are permanent records of the initial testing and qualification program and are used to backup, and support, the WPS. The identification numbers of the supporting PQR(s) are recorded on each WPS. All PQRs are permanently stored under the supervision of the Fluor Hanford Welding Engineer (FHWE). New PQRs and WPSs will continue to be developed as necessary. The qualification of welders, welding operators and welding procedures will be performed for FH under supervision and concurrent of the FHWE. All new welding procedures to be entered in this manual or welder personnel to be added to the welder qualification database, shall be approved by the FHWE.

  20. Numerical aspects for efficient welding computational mechanics

    Directory of Open Access Journals (Sweden)

    Aburuga Tarek Kh.S.

    2014-01-01

    Full Text Available The effect of the residual stresses and strains is one of the most important parameter in the structure integrity assessment. A finite element model is constructed in order to simulate the multi passes mismatched submerged arc welding SAW which used in the welded tensile test specimen. Sequentially coupled thermal mechanical analysis is done by using ABAQUS software for calculating the residual stresses and distortion due to welding. In this work, three main issues were studied in order to reduce the time consuming during welding simulation which is the major problem in the computational welding mechanics (CWM. The first issue is dimensionality of the problem. Both two- and three-dimensional models are constructed for the same analysis type, shell element for two dimension simulation shows good performance comparing with brick element. The conventional method to calculate residual stress is by using implicit scheme that because of the welding and cooling time is relatively high. In this work, the author shows that it could use the explicit scheme with the mass scaling technique, and time consuming during the analysis will be reduced very efficiently. By using this new technique, it will be possible to simulate relatively large three dimensional structures.