Magnetic orientation of nontronite clay in aqueous dispersions and its effect on water diffusion.
Abrahamsson, Christoffer; Nordstierna, Lars; Nordin, Matias; Dvinskikh, Sergey V; Nydén, Magnus
2015-01-01
The diffusion rate of water in dilute clay dispersions depends on particle concentration, size, shape, aggregation and water-particle interactions. As nontronite clay particles magnetically align parallel to the magnetic field, directional self-diffusion anisotropy can be created within such dispersion. Here we study water diffusion in exfoliated nontronite clay dispersions by diffusion NMR and time-dependant 1H-NMR-imaging profiles. The dispersion clay concentration was varied between 0.3 and 0.7 vol%. After magnetic alignment of the clay particles in these dispersions a maximum difference of 20% was measured between the parallel and perpendicular self-diffusion coefficients in the dispersion with 0.7 vol% clay. A method was developed to measure water diffusion within the dispersion in the absence of a magnetic field (random clay orientation) as this is not possible with standard diffusion NMR. However, no significant difference in self-diffusion coefficient between random and aligned dispersions could be observed. Copyright © 2014 Elsevier Inc. All rights reserved.
Kimura, Yuji; Haraguchi, Kazutoshi
2017-05-16
Clay-alcohol-water ternary dispersions were compared with alcohol-water binary mixtures in terms of viscosity and optical absorbance. Aqueous clay dispersions to which lower alcohols (ethanol, 1-propanol, 2-propanol, and tert-butanol) were added exhibited significant viscosity anomalies (maxima) when the alcohol content was 30-55 wt %, as well as optical absorbance anomalies (maxima). The maximum viscosity (η max ) depended strongly on the clay content and varied between 300 and 8000 mPa·s, making it remarkably high compared with the viscosity anomalies (2 mPa·s) observed in alcohol-water binary mixtures. The alcohol content at η max decreased as the hydrophobicity of the alcohol increased. The ternary dispersions with viscosity anomalies exhibited thixotropic behaviors. The effects of other hydrophilic solvents (glycols) and other kinds of clays were also clarified. Based on these findings and the average particle size changes, the viscosity anomalies in the ternary dispersions were explained by alcohol-clustering-induced network formation of the clay nanosheets. It was estimated that 0.9, 1.7, and 2.5 H 2 O molecules per alcohol molecule were required to stabilize the ethanol, 2-propanol, and tert-butanol, respectively, in the clay-alcohol-water dispersions.
Infiltration of water in disturbed soil columns as affected by clay dispersion and aggregate slaking
Amezketa, E.; Aragües, R.; Gazol, R.
2004-01-01
Soil crusting negatively affects the productivity and sustainability of irrigated agriculture, reducing water infiltration and plant emergence, and enhancing surface runoff and erosion. Clay dispersion and slaking of the aggregates at the soil surface are the main processes responsible for crusting. The infiltration rates (IR) of ten arid-zone soils in disturbed soil columns were measured and their relative susceptibilities to dispersion and slaking were determined. It was also examined wheth...
The magnetic fabrics of experimentally deformed artificial clay-water dispersions
Richter, Carl; Frisch, Wolfgang; Ratschbacher, Lothar; Schwarz, Hans-Ulrich
1991-12-01
The development of magnetic fabrics in artificial clay-water dispersions and natural, hematite-bearing mudstones is investigated in plane-strain pure shear laboratory experiments under strain rates of 1.6 × 10 -5 and 2 × 10 -4s-1. The mixtures contain 0,15, 30 and 45% chlorite in an illite matrix, and 0, 1, 3, 6 and 8% magnetite in a kaolin matrix. Shortening up to 40% is imposed. The resulting fabrics show the following characteristics: (1) In the clay mixtures, the principal susceptibility axes ( kmax ≥ kint ≥ kmin) rotate away from the well defined initial fabric orientations into the princip strain directions ( e1 ≥ e2 ≥ e3) at strains > 30%. (2) Both mineralogical composition and initial magnetic fabric, but not the applied strain, influence the magnitudes of the principal susceptibility axes. (3) The illite-chlorite mixture series show an almost linear correlation between mineral concentration and susceptibility magnitudes. (4) Magnetite dominates the fabric of the magnetite-kaolin mixtures; the fabric is independent of the magnetite concentration.
Development and characterization of clay facial mask containing turmeric extract solid dispersion.
Pan-On, Suchiwa; Rujivipat, Soravoot; Ounaroon, Anan; Tiyaboonchai, Waree
2018-04-01
To develop clay facial mask containing turmeric extract solid dispersion (TESD) for enhancing curcumin water solubility and permeability and to determine suitable clay based facial mask. The TESD were prepared by solvent and melting solvent method with various TE to polyvinylpyrrolidone (PVP) K30 mass ratios. The physicochemical properties, water solubility, and permeability were examined. The effects of clay types on physical stability of TESD, water adsorption, and curcumin adsorption capacity were evaluated. The TESD prepared by solvent method with a TE to PVP K30 mass ratio of 1:2 showed physically stable, dry powders, when mixed with clay. When TESD was dissolved in water, the obtained TESD micelles showed spherical shape with mean size of ∼100 nm resulting in a substantial enhancement of curcumin water solubility, ∼5 mg/ml. Bentonite (Bent) and mica (M) showed the highest water adsorption capacity. The TESD's color was altered when mixed with Bent, titanium dioxide (TiO 2 ) and zinc oxide (ZnO) indicating curcumin instability. Talcum (Talc) showed the greatest curcumin adsorption followed by M and kaolin (K), respectively. Consequently, in vitro permeation studies of the TESD mixed with Talc showed lowest curcumin permeation, while TESD mixed with M or K showed similar permeation profile as free TESD solutions. The developed TESD-based clay facial mask showed lower curcumin permeation as compared to those formulations with Tween 80. The water solubility and permeability of curcumin in clay based facial mask could be improved using solid dispersion technique and suitable clay base composed of K, M, and Talc.
Clay Dispersibility and Soil Friability-Testing the Soil Clay-to-Carbon Saturation Concept
DEFF Research Database (Denmark)
Schjønning, Per; de Jonge, Lis Wollesen; Munkholm, Lars Juhl
2012-01-01
Soil organic carbon (OC) influences clay dispersibility, which affects soil tilth conditions and the risk of vertical migration of clay colloids. No universal lower threshold of OC has been identified for satisfactory stabilization of soil structure. We tested the concept of clay saturation with OC...... as a predictor of clay dispersibility and soil friability. Soil was sampled 3 yr in a field varying in clay content (∼100 to ∼220 g kg−1 soil) and grown with different crop rotations. Clay dispersibility was measured after end-over-end shaking of field-moist soil and 1- to 2-mm sized aggregates either air......-dried or rewetted to −100 hPa matric potential. Tensile strength of 1- to 2-, 2- to 4-, 4- to 8-, and 8- to 16-mm air-dried aggregates was calculated from their compressive strength, and soil friability estimated from the strength–volume relation. Crop rotation characteristics gave only minor effects on clay...
Clay dispersibility and soil friability – testing the soil clay-to-carbon saturation concept
Schjønning, P.; de Jonge, L.W.; Munkholm, L.J.; Moldrup, P.; Christensen, B.T.; Olesen, J.E.
2011-01-01
Soil organic carbon (OC) influences clay dispersibility, which affects soil tilth conditions and the risk of vertical migration of clay colloids. No universal lower threshold of OC has been identified for satisfactory stabilization of soil structure. We tested the concept of clay saturation with OC as a predictor of clay dispersibility and soil friability. Soil was sampled three years in a field varying in clay content (~100 to ~220 g kg-1 soil) and grown with different crop rotations. Clay ...
International Nuclear Information System (INIS)
Garcia, Claudia P.; Delpech, Marcia C.; Coutinho, Fernanda M.B.; Mello, Ivana L.
2009-01-01
Nanocomposites based on water bone polyurethane (NWPU's) were synthesized based on poli(propylene glycol), dimethylolpropionic acid (DMPA), isophorone diisocyanate (IPDI) and hydrazine (HYD), as chain extender. Two kinds of clays were employed: hydrophilic and organophilic. The nanocomposites were characterized by infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electronic microscopy (SEM) and the mechanical properties were evaluated. The FTIR results showed the presence of specific groups of clay and the XRD suggested that occurred their intercalation/exfoliation through polyurethane matrix. The mechanical resistance of the systems showed significant increase when compared to water dispersions synthesized without clay. (author)
Clay squirt: Local flow dispersion in shale-bearing sandstones
DEFF Research Database (Denmark)
Sørensen, Morten Kanne; Fabricius, Ida Lykke
2017-01-01
Dispersion of elastic-wave velocity is common in sandstone and larger in shaly sandstone than in clean sandstone. Dispersion in fluid-saturated shaly sandstone often exceeds the level expected from the stress-dependent elastic moduli of dry sandstone. The large dispersion has been coined clay...... squirt and is proposed to originate from a pressure gradient between the clay microporosity and the effective porosity. We have formulated a simple model that quantifies the clay-squirt effect on bulk moduli of sandstone with homogeneously distributed shale laminae or dispersed shale. The model...... predictions were compared with the literature data. For sandstones with dispersed shale, agreement was found, whereas other sandstones have larger fluid-saturated bulk modulus, possibly due to partially load-bearing shales or heterogeneous shale distribution. The data that agree with the clay-squirt model...
Development of photopolymerizable clay nanocomposites utilizing reactive dispersants
Owusu-Adom, Kwame
Nanocomposites hold tremendous promise for expanding the utility of polymeric materials. However, accessing particulate sizes in the nanoscale domain continues to be a scientific challenge, especially in highly cross-linked photopolymerizable systems. In this study, photopolymerizable nanocomposites utilizing clay nanoparticles and reactive dispersants have been developed. The influence of particle size, dispersant-clay interactions, and surfactant concentration on photopolymerization behavior and nanoparticle dispersion has been elucidated. Clay particles serve as templates upon which surfactants aggregate during photopolymerization. This results in higher photopolymerization rates with addition of increasing concentrations of polymerizable surfactants. Furthermore, polymerizable surfactants induce faster photopolymerization rates compared to non-polymerizable analogues in systems that have ionically-bound dispersants on the particle surface. Utilizing reactive organoclays induces significant changes to the photopolymerization behavior depending on the choice of reactive functionality employed. Faster acrylate photopolymerization rates occur in photopolymer systems containing thiol-modified clays, while much slower rates occur for nonpolymerizable organoclay systems. In addition, chemical compatibility between monomer and clay dispersant (based on chemical similarity or polarity) allows enhancement of exfoliation in photopolymerizable formulations. With polymerizable dispersants, exfoliation is readily achieved in various multifunctional acrylate systems. The degree of exfoliation depends on the position of the reactive group relative to the surfactant's cationic site and the type of functionality. Thiolated organoclays exfoliate during polymerization, while methacrylated clays show substantially less dependence on polymerization behavior. Interestingly, changes in the physical properties of the resulting nanocomposite are independent of the degree of exfoliation
International Nuclear Information System (INIS)
Miranda, G.S.; Delpechi, M.C.; Santo, W.L.E.
2010-01-01
Several studies involving the formation of polyurethane nanocomposites employing clays of montmorillonite modified. This involves the presence of quaternary ammonium salts, the cation exchange needed to increase the interlayer space of clays that incorporate more than one step to the process, generates a higher cost. In this paper the synthesis of nanocomposite polyurethanes dispersed in water allowed not only the production of materials less harmful to the environment, but also the incorporation of hydrophilic clays, calcium and sodium in nature, without any modifications. Dispersions produced from 0.5, 1.0 and 2.5% clay (on the mass of prepolymer) were characterized in terms of total solids content, the films obtained by casting were evaluated for adhesiveness, diffraction X-rays, scanning electron microscopy. Most systems showed intercalated and partially exfoliated structures. (author)
Experimental design applied optimization of a state in epoxy clay dispersion
International Nuclear Information System (INIS)
Paz, Juliana D'Avila; Bertholdi, Jonas; Folgueras, Marilena Valadares; Pezin, Sergio Henrique; Coelho, Luiz Antonio Ferreira
2010-01-01
This paper presents some analysis showed that the exfoliation / intercalation of a montmorillonite clay in epoxy resin such as viscosity, X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). Increasing the viscosity of epoxy resin diglycidyl ether bisphenol A with the addition of clay associated with the sonification system at the time of dispersion is a good indication of exfoliation. The X-ray diffraction already cured composite shows a decrease of crystallinity of clay and EDS microanalysis of SEM, non-uniform dispersion of clay in epoxy resin. Thermal analysis TG composite clay / epoxy shows an increase in thermal stability relative to pure epoxy. (author)
Energy Technology Data Exchange (ETDEWEB)
Kim, Doohyun; Ock, Hyun Geun; Ahn, Kyung Hyun; Lee, Seung Jong [Seoul National University, Seoul (Korea, Republic of)
2015-12-15
In this study, structural developments of polypropylene / ionomer / clay ternary composites were investigated depending on the dispersion and localization of clay. The changes in physical properties were observed adding organoclays 1-10wt% to 90% polypropylene and 10% ionomer blends. The organoclays were localized inside of the dispersed phase under the composition of 3wt%, however, over that composition, clay particles formed stiff network structure in the dispersed phase and additional clays were localized at the interface between two phases. According to the developments of microstructure, the interaction of ternary composites changed from polypropylene-ionomer to polypropylene- ionomer and ionomer-clay which affected rheological properties. The storage modulus (G') of the composites was similar to the blends when clays were localized inside of dispersed phase but increased when clays were localized at interface. Also, the fractured morphology of the composites showed phase boundary and growing radius of dispersed phase depending on addition of fillers when clays were found inside. However, when fillers found at the interface between blends, the radius of the dispersed phase decreased and compatibilized morphology were observed. The interfacial interaction of the ternary composite was quantified depending on the structural development of dispersed phase and localization of clay particles by the rheological properties. The interaction of composites at solid state which was measured through peel adhesion strength increased by growth of interfacial interaction of each component. Furthermore, the crystallinity of the composites was decreased when the clay particles were localized at the interface.
International Nuclear Information System (INIS)
Kim, Doohyun; Ock, Hyun Geun; Ahn, Kyung Hyun; Lee, Seung Jong
2015-01-01
In this study, structural developments of polypropylene / ionomer / clay ternary composites were investigated depending on the dispersion and localization of clay. The changes in physical properties were observed adding organoclays 1-10wt% to 90% polypropylene and 10% ionomer blends. The organoclays were localized inside of the dispersed phase under the composition of 3wt%, however, over that composition, clay particles formed stiff network structure in the dispersed phase and additional clays were localized at the interface between two phases. According to the developments of microstructure, the interaction of ternary composites changed from polypropylene-ionomer to polypropylene- ionomer and ionomer-clay which affected rheological properties. The storage modulus (G') of the composites was similar to the blends when clays were localized inside of dispersed phase but increased when clays were localized at interface. Also, the fractured morphology of the composites showed phase boundary and growing radius of dispersed phase depending on addition of fillers when clays were found inside. However, when fillers found at the interface between blends, the radius of the dispersed phase decreased and compatibilized morphology were observed. The interfacial interaction of the ternary composite was quantified depending on the structural development of dispersed phase and localization of clay particles by the rheological properties. The interaction of composites at solid state which was measured through peel adhesion strength increased by growth of interfacial interaction of each component. Furthermore, the crystallinity of the composites was decreased when the clay particles were localized at the interface.
Directory of Open Access Journals (Sweden)
J. Soulestin
2012-03-01
Full Text Available The effect of injection molding parameters (screw rotational speed, back pressure, injec-tion flow rate and holding pressure on the nanofiller dispersion of melt-mixed PP/clay nanocomposites was investigated. The nanocomposites containing 4 wt% clay were obtained by dilution of a PP/clay masterbatch into a PP matrix. The evaluation of the dispersion degree was obtained from dynamic rheological measurements. The storage modulus and complex viscosity exhibit significant dependence on the injection molding parameters. PP/clay nanocomposite molded using more severe injection parameters (high shear and long residence time displays the highest storage modulus and complex viscosity, which illustrates the improved dispersion of clay platelets. This better dispersion leads to better mechanical properties particularly higher Young modulus, tensile strength and unnotched impact strength. A Taguchi analysis was used to identify the influence of individual process parameters. The major individual parameter is the injection flow rate, whose increase improves nanoclay dispersion. The combination of high back pressure and high screw rotational speed is also necessary to optimize the dispersion of clay nanoplatelets.
Influence of clay, surfactant and presence of dispersant in the non-aqueous fluids rheology
International Nuclear Information System (INIS)
Gomes, N.L.; Guedes, I.C.; Menezes, R.R.; Campos, L.F.A.; Ferreira, H.S.
2012-01-01
The bentonite clay used as a thickening agent in production of non-aqueous fluids and can not be used without a prior treatment to their organic surfaces become hydrophobic. These treated clays are called organoclays, and are usually obtained by adding, in aqueous solution, a quaternary ammonium salt. This work makes a detailed study of the variables involved in the dispersion of the bentonite clays in organophilization process, as well, the type of clay, type of surfactant and the presence of dispersant. It was observed this study that the process variables involved in the dispersion of the clays and organophilization, observed through characterization, have low influence on the peaks related to interplanar basal distance caused by the incorporation of the surfactant and bentonite clays been influential the type of clay and surfactant and the presence of sodium as dispersant agent, on the rheological properties. (author)
DEFF Research Database (Denmark)
Sørensen, Morten Kanne; Fabricius, Ida Lykke
2013-01-01
Compliant porosity in the form of cracks is known to cause significant attenuation and velocity dispersion through pore pressure gradients and consequent relaxation, dubbed squirt flow. Squirt flow from cracks vanish at high confining stress due to crack closing. Studies on clay bearing sandstones......-squirt flow on the bulk modulus of a clay bearing sandstone. The predicted magnitude of the clay-squirt effect on the bulk modulus is compared with experimental data. The clay-squirt effect is found to possibly account for a significant portion of the deviances from Gassmann fluid substitution in claybearing...... sandstones....
Applications of fractional calculus to diffusion transport in clay-water system
International Nuclear Information System (INIS)
Korosak, D.; Cvikl, B.; Kramer, J.; Jecl, R.; Praprotnik, A.; Veselic, M.
2005-01-01
The analysis of the low-frequency conductivity spectra of the clay-water mixtures is presented. The conductivity spectra for samples at different water content values are shown to collapse to a single master curve when appropriately rescaled. The frequency dependence of the conductivity is shown to follow the power-law with the exponent η=0,67 before reaching the frequency-independent part. It is argued that the observed conductivity dispersion is a consequence of the anomalously diffusing ions in the clay-water system. The fractional Langevin equation is then used to describe the stochastic dynamics of the single ion. (author)
Aqueous dispersion of red clay-based ceramic powder with the addition of starch
Directory of Open Access Journals (Sweden)
Maria Victoria Alcantar Umaran
2013-04-01
Full Text Available The optimum dispersion and rheological properties of red clay-based ceramic suspension loaded with unary and binary starch were investigated in aqueous medium. The aqueous ceramic suspension was prepared consisting of red clay, quartz, feldspar, and distilled water. Using a polyelectrolyte dispersant (Darvan 821A, the ternary ceramic powder was initially optimized to give the smallest average particle size at 0.8 wt. (% dispersant dosage as supported by sedimentation test. This resulted into an optimum high solid loading of 55 wt. (%. The addition of either unary or binary starches to the optimized ceramic slurry increased the viscosity but maintained an acceptable fluidity. The mechanism of such viscosity increase was found to be due to an adsorption of starch granules onto ceramic surfaces causing tolerable agglomeration. Correspondingly, the rheological evaluations showed that the flow behaviors of all starch-loaded ceramic slurries can be described using Herschel-Bulkley model. The parameters from this model indicated that all ceramic slurries loaded with starch are shear thinning that is required for direct casting process.
Multisensor on-the-go mapping of readily dispersible clay, particle size and soil organic matter
Debaene, Guillaume; Niedźwiecki, Jacek; Papierowska, Ewa
2016-04-01
Particle size fractions affect strongly the physical and chemical properties of soil. Readily dispersible clay (RDC) is the part of the clay fraction in soils that is easily or potentially dispersible in water when small amounts of mechanical energy are applied to soil. The amount of RDC in the soil is of significant importance for agriculture and environment because clay dispersion is a cause of poor soil stability in water which in turn contributes to soil erodibility, mud flows, and cementation. To obtain a detailed map of soil texture, many samples are needed. Moreover, RDC determination is time consuming. The use of a mobile visible and near-infrared (VIS-NIR) platform is proposed here to map those soil properties and obtain the first detailed map of RDC at field level. Soil properties prediction was based on calibration model developed with 10 representative samples selected by a fuzzy logic algorithm. Calibration samples were analysed for soil texture (clay, silt and sand), RDC and soil organic carbon (SOC) using conventional wet chemistry analysis. Moreover, the Veris mobile sensor platform is also collecting electrical conductivity (EC) data (deep and shallow), and soil temperature. These auxiliary data were combined with VIS-NIR measurement (data fusion) to improve prediction results. EC maps were also produced to help understanding RDC data. The resulting maps were visually compared with an orthophotography of the field taken at the beginning of the plant growing season. Models were developed with partial least square regression (PLSR) and support vector machine regression (SVMR). There were no significant differences between calibration using PLSR or SVMR. Nevertheless, the best models were obtained with PLSR and standard normal variate (SNV) pretreatment and the fusion with deep EC data (e.g. for RDC and clay content: RMSECV = 0,35% and R2 = 0,71; RMSECV = 0,32% and R2 = 0,73 respectively). The best models were used to predict soil properties from the
THE STUDYING OF COLLOIDAL-CHEMICAL PROPERTIES OF CLAY MINERALS DISPERSIONS
Directory of Open Access Journals (Sweden)
A. F. Tymchuk
2015-02-01
Full Text Available The element structure is studied, the microscopic analysis of fine-dispersed mineral systems (ground sediments of a mouth of the river Danube is carried out. The sedimentation process of clay minerals dispersions in solutions of surfactants and macromolecular substances is studied. Concentration intervals of stabilization of investigating dispersions were defined.
Directory of Open Access Journals (Sweden)
Herry Poernomo
2010-12-01
Full Text Available The experiment of sorption and dispersion characteristics of strontium in the mixture of bentonite-quartz, clay-quartz, bentonite-clay-quartz as candidate of raw material for backfill material in the radioactive waste repository has been performed. The objective of this research is to know the grain size effect of bentonite, clay, and quartz on the weight percent ratio of bentonite to quartz, clay to quartz, bentonite to clay to-quartz can be gives physical characteristics of best such as bulk density (rb, effective porosity (e, permeability (K, best sorption characteristic such as distribution coefficient (Kd, and best dispersion characteristics such as dispersivity (a and effective dispersion coefficient (De of strontium in the backfill material candidate. The experiment was carried out in the column filled by the mixture of bentonite-quartz, clay-quartz, bentonite-clay-quartz with the weight percent ratio of bentonite to quartz, clay to quartz, bentonite to clay to quartz of 100/0, 80/20, 60/40, 40/60, 20/80, 0/100 respectively at saturated condition of water, then flowed 0.1 N Sr(NO32 as buffer solution with tracer of 0.05 Ci/cm3 90Sr as strontium radionuclide simulation was leached from immobilized radioactive waste in the radioactive waste repository. The concentration of 90Sr in the effluents represented as Ct were analyzed by Ortec b counter every 30 min, then by using profile concentration of Co and Ct, values of Kd, a and De of 90Sr in the backfill material was determined. The experiment data showed that the best results were -80+120 mesh grain size of bentonite, clay, quartz respectively on the weight percent ratio of bentonite to clay to quartz of 70/10/20 with physical characteristics of rb = 0.658 g/cm3, e = 0.666 cm3/cm3, and K = 1.680x10-2 cm/sec, sorption characteristic of Kd = 46.108 cm3/g, dispersion characteristics of a = 5.443 cm, and De = 1.808x10-03 cm2/sec can be proposed as candidate of raw material of backfill material
Labruyère, Céline; Monteverde, Fabien; Alexandre, Michaël; Dubois, Philippe
2009-04-01
Poly(dimethylsiloxane) (PDMS)/montmorillonite (MMT) composites have been prepared using a newly synthesized omega-ammonium functionalized poly(dimethylsiloxane) compatibilizer coupled with a dispersion technique in water. The organoclay containing the new siloxane surfactant was characterized by TGA and XRD. For the first time, a nanoscopic dispersion of MMT nanoplatelets in the PDMS composite cured by hydrosilylation and a good compatibility between clay layers and matrix were obtained. The beneficial effect of both the surfactant and the water onto clay nanoplatelet dispersion was evaluated by different microscopy techniques and by measuring different properties such as the viscosity of the uncured PDMS/MMT nanodispersions, and the swelling rate and Young's modulus of the cured PDMS/MMT nanocomposites.
J. Soulestin; J. J. Rajesh; M. F. Lacrampe; P. Krawczak
2012-01-01
The effect of injection molding parameters (screw rotational speed, back pressure, injec-tion flow rate and holding pressure) on the nanofiller dispersion of melt-mixed PP/clay nanocomposites was investigated. The nanocomposites containing 4 wt% clay were obtained by dilution of a PP/clay masterbatch into a PP matrix. The evaluation of the dispersion degree was obtained from dynamic rheological measurements. The storage modulus and complex viscosity exhibit significant dependence on the injec...
Directory of Open Access Journals (Sweden)
João Tavares Filho
2010-10-01
Full Text Available A by-product of Wastewater Treatment Stations is sewage sludge. By treatment and processing, the sludge is made suitable for rational and environmentally safe use in agriculture. The aim of this study was to assess the influence of different doses of limed sewage sludge (50 % on clay dispersion in soil samples with different textures (clayey and medium. The study was conducted with soil samples collected from native forest, on a Red Latosol (Brazilian classification: Latossolo Vermelho distroférrico loamy soil in Londrina (PR and a Red-Yellow Latosol (BC: Latossolo Vermelho-Amarelo distrófico medium texture soil in Jaguapitã (PR. Pots were filled with 3 kg of air-dried fine earth and kept in greenhouse. The experiment was arranged in a randomized block design with six treatments: T1 control, and treatments with limed sewage sludge (50 % as follows: T2 (3 t ha-1, T3 (6 t ha-1, T4 (12 t ha-1, T5 (24 t ha-1 and T6 (48 t ha-1 and five replications. The incubation time was 180 days. At the end of this period, the pots were opened and two sub-samples per treatment collected to determine pH-H2O, pH KCl (1 mol L-1, organic matter content, water-dispersible clay, ΔpH (pH KCl - pH-H2O and estimated PZC (point of zero charge: PZC = 2 pH KCl - pH-H2O, as well as the mineralogy of the clay fraction, determined by X ray diffraction. The results showed no significant difference in the average values for water-dispersible clay between the control and the other treatments for the two soil samples studied and ΔpH was the variable that correlated best with water-dispersible clay in both soils.As Estações de Tratamento de Esgoto Sanitário (ETES geram um subproduto (lodo de esgoto que, quando tratado e processado, adquire características que permitem sua utilização agrícola de maneira racional e ambientalmente segura. Este trabalho objetivou avaliar a influência de diferentes doses de lodo de esgoto caleado (50 % na dispersão de argilas em amostras de
Unique morphology of dispersed clay particles in a polymer nanocomposite
CSIR Research Space (South Africa)
Malwela, T
2011-02-01
Full Text Available This communication reports a unique morphology of dispersed clay particles in a polymer nanocomposite. A nanocomposite of poly[butylene succinate)-co-adipate] (PBSA) with 3 wt% of organically modified montmorillonite was prepared by melt...
Effect of mechanical and chemical clay removals by hydrocyclone and dispersants on coal flotation
Energy Technology Data Exchange (ETDEWEB)
Oats, W.J.; Ozdemir, O.; Nguyen, A.V. [University of Queensland, Brisbane, Qld. (Australia). School of Chemical Engineering
2010-04-15
Fine minerals, mostly clays, are known to have a detrimental effect on coal flotation. This paper focuses on the effect of mechanical and chemical removals of fine minerals by hydrocyclone and dispersants on coal flotation. The experimental results showed that the flotation recovery slightly increased from medium acidic to medium alkaline ranges. The flotation experiments carried out with dispersants at different dosages showed that the dispersants did not enhance the flotation recovery significantly. However, the removal of the fine fraction from the feed using a hydrocyclone significantly increased the flotation recovery. The bubble-particle attachment tests also indicated that the attachment time between an air bubble and the coal particles increased in the presence of clay particles. These attachment time results clearly showed that the clay particles adversely affected the flotation of coal particles by covering the coal surfaces which reduced the efficiency of bubble-coal attachment. An analysis based on the colloid stability theory showed that the clay coating was governed by the van der Waals attraction and that the double-layer interaction played a secondary role. It was also concluded that the best way to increase the flotation recovery in the presence of clays was to remove these fine minerals by mechanical means such as hydrocylones.
Energy Technology Data Exchange (ETDEWEB)
Kim, Yeongho; Lee, Minho; Jeon, Hyeon Yeol; Min, Byong Hun; Kim, Jeong Ho [Univ. of Suwon, Hwaseong (Korea, Republic of); Lee, Young Chul [Korea Institute of Industrial Technology, Seoul (Korea, Republic of)
2016-02-15
Eco-friendly acrylic resin/clay nanocomposites containing pristine montmorillonite (PM) or modified clays (30B and 25A) were prepared from acrylic and styrenic monomers using non-aqueous dispersion (NAD) polymerization. Effect of nanoclays on physical properties of polymerization product and resulting nanocomposites was investigated. In view of NAD particle stability, addition of nanoclay at the beginning of polymerization is proved to be good. Results of gel fraction, acid value and viscosity of the NAD product showed that nanocomposites containing clay 25A showed better physical properties than the ones with other clays. GPC results exhibit the increase in molecular weight and decrease in polydispersity index for the 25A nanocomposite. Increase in layer distance confirmed from XRD analysis showed good dispersion of 25A in the nanocomposite. Thermal and dynamic mechanical analysis showed that highest glass transition temperature and storage modulus for 25A nanocomposites. These results indicate that 25A nanoclay gives the best properties in the process of non-aqueous dispersion polymerization of acrylic resin/nanoclay nanocomposites.
International Nuclear Information System (INIS)
Kim, Yeongho; Lee, Minho; Jeon, Hyeon Yeol; Min, Byong Hun; Kim, Jeong Ho; Lee, Young Chul
2016-01-01
Eco-friendly acrylic resin/clay nanocomposites containing pristine montmorillonite (PM) or modified clays (30B and 25A) were prepared from acrylic and styrenic monomers using non-aqueous dispersion (NAD) polymerization. Effect of nanoclays on physical properties of polymerization product and resulting nanocomposites was investigated. In view of NAD particle stability, addition of nanoclay at the beginning of polymerization is proved to be good. Results of gel fraction, acid value and viscosity of the NAD product showed that nanocomposites containing clay 25A showed better physical properties than the ones with other clays. GPC results exhibit the increase in molecular weight and decrease in polydispersity index for the 25A nanocomposite. Increase in layer distance confirmed from XRD analysis showed good dispersion of 25A in the nanocomposite. Thermal and dynamic mechanical analysis showed that highest glass transition temperature and storage modulus for 25A nanocomposites. These results indicate that 25A nanoclay gives the best properties in the process of non-aqueous dispersion polymerization of acrylic resin/nanoclay nanocomposites
International Nuclear Information System (INIS)
Paumier, S.
2007-11-01
Smectite are swelling clays widely used in industry. Their mechanical properties are unequal according to their mineralogical and physico-chemical characteristics. The aim of this study is to improve the knowledge of the interlayer cation impact on the structure built by the smectite-water system according to the concentration. Homo-ionic (Na + et Ca 2+ ) and bi-ionic systems are observed. This study cross checks mineralogical methods, physicochemical analysis and broad range of rheometric tests. At low concentration (less than 60 g/l) the calcium dispersions are shear thinning and few viscous due to the layer association in huge deformable flocks. The sodium smectite layers are dispersed; the dispersions are highly viscous. The lowest viscosity is detected for mix of 20 % of sodium smectite and 80 % of calcium smectite. At higher concentration (60 to 100 g/l), the yield stress and viscoelastic properties are studied by creep-recovery tests, oscillatory tests and imposed shear step. At the liquid state, the flow is first heterogeneous with a shear banding effect then homogeneous. The results make it possible to define the concentration area characteristic of each mechanical behavior (viscosity, shear thinning and yield stress) according to the saturation cation. The thixotropic properties are characterized with de-structuring-restructuring tests. Two kinetics are determined. Finally we realize a data base with 12 natural and industrial bentonite. The rheograms would be efficient to differentiate the natural calcium bentonite (Newtonian law), natural sodium bentonite (Herschel-Bulkley law) and activated calcium bentonite (Bingham law). (author)
Preparation and properties of biodegradable starch–clay nanocomposites
Chung, Yi-Lin; Ansari, Seema; Estevez, Luis; Hayrapetyan, Suren; Giannelis, Emmanuel P.; Lai, Hsi-Mei
2010-01-01
Well-dispersed starch-clay nanocomposites were prepared by adding a dilute clay dispersion to a solution of starch followed by coprecipitation in ethanol. The clay didn't significantly influence the type of crystalline structure of starch molecules although the amount of crystallinity appears to be somewhat lower in the nanocomposites. The nanocomposites show improved modulus and strength without a decrease in elongation at break. The increase in modulus and strength is 65% and 30%, respectively for the nanocomposite containing 5 wt.% clay compared to the unfilled starch materials. Further increases in clay result in deterioration in properties most likely due to poorer clay dispersion and lower polymer crystallinity. As the amount of water increases, the modulus of both pure starch and starch nanocomposites decreases, although the change is less pronounced in the nanocomposites suggesting that the addition of clay to form nanocomposites can improve the stability of starch-based products during transportation and storage. © 2009 Elsevier Ltd. All rights reserved.
Preparation and properties of biodegradable starch–clay nanocomposites
Chung, Yi-Lin
2010-01-01
Well-dispersed starch-clay nanocomposites were prepared by adding a dilute clay dispersion to a solution of starch followed by coprecipitation in ethanol. The clay didn\\'t significantly influence the type of crystalline structure of starch molecules although the amount of crystallinity appears to be somewhat lower in the nanocomposites. The nanocomposites show improved modulus and strength without a decrease in elongation at break. The increase in modulus and strength is 65% and 30%, respectively for the nanocomposite containing 5 wt.% clay compared to the unfilled starch materials. Further increases in clay result in deterioration in properties most likely due to poorer clay dispersion and lower polymer crystallinity. As the amount of water increases, the modulus of both pure starch and starch nanocomposites decreases, although the change is less pronounced in the nanocomposites suggesting that the addition of clay to form nanocomposites can improve the stability of starch-based products during transportation and storage. © 2009 Elsevier Ltd. All rights reserved.
Water diffusion in clays with added organic surfactants
International Nuclear Information System (INIS)
Pineda-Pinon, J; Mendoza-Lopez, M L; Manzano-RamIrez, A; Perez-Robles, J F; Vega-Duran, J T
2007-01-01
Tensoactive agents may decrease water absorption in clay products like adobes. They modify the characteristics of the surface of clay particles. Characterization of water diffusion through the pores of modified clays is important to apply appropriate surface modifiers and to improve their performance. We established a simple model for water diffusion in test samples of defined dimensions to estimate real physical parameters and their effect on water absorption. Adsorption mechanisms are examined based on experimental results. The fitting of the experimental data to the model provides a deep understanding of water adsorption in chemically modified clays. A better agreement between the model and the experimental data is achieved for complex molecules
Photophysical and adsorption properties of pyronin B in natural bentonite clay dispersion
Energy Technology Data Exchange (ETDEWEB)
Rostami, Mohammad Reza [Department of Chemistry, Faculty of Sciences, Atatürk University, 25240, Erzurum (Turkey); Kaya, Mehmet [Recep Tayyip Erdoğan University, Faculty of Arts and Sciences, 53100 Rize (Turkey); Gür, Bahri; Onganer, Yavuz [Department of Chemistry, Faculty of Sciences, Atatürk University, 25240, Erzurum (Turkey); Meral, Kadem, E-mail: kademm@atauni.edu.tr [Department of Chemistry, Faculty of Sciences, Atatürk University, 25240, Erzurum (Turkey)
2015-12-30
Graphical abstract: The molecular aggregation of PyB in bentonite aqueous dispersion is observed by using molecular absorption spectrum. - Highlights: • Molecular behavior of PyB adsorbed on bentonite was spectroscopically followed. • H-aggregates of PyB in bentonite aqueous dispersion were formed. • The adsorption characteristics of PyB on bentonite particles were determined. - Abstract: The present study focused on the adsorption and photophysical properties of pyronin B (PyB) in bentonite aqueous dispersion. The photophysical properties of PyB in the aqueous dispersion were studied by using UV–vis absorption, steady-state and time-resolved fluorescence spectroscopy techniques. In this concept, the interaction of the dye with bentonite particles in the aqueous dispersion was spectroscopically followed depending on certain parameters such as interaction time, pH and the dye concentration. Obtained spectral data revealed that the aggregate structures (H-type) of PyB in the aqueous dispersion were formed in the dye concentration range studied. The non-fluorescence nature of H-aggregates and the clay minerals governed the fluorescence property of PyB. The mentioned non-radiative processes caused the fluorescence lifetime of the dye to decrease compared to that in water. The adsorption process of PyB on bentonite was examined depending on contact time and initial adsorbate concentration. An adsorption isotherm was good-fitted by the Freundlich model with a linear regression correlation value of 0.999. The adsorption of PyB on bentonite particles was in agreement with pseudo second-order kinetics.
International Nuclear Information System (INIS)
Zaioncz, Soraia; Soares, Bluma G.
2009-01-01
Nanocomposites of epoxy resin modified with PMMA and montmorillonite organophilic were synthesized with clay content equal to 0.1, 1, 2.5, 5 and 7 (wt %). Dispersion state and the nano structure of materials has been investigated using small angle X-ray scattering (SAXS). The nanocomposites containing 0.1 (wt %) of clay showed an exfoliated morphology, while the nanocomposites with higher clay content (1 to 7 wt %) show that the dispersion state is less uniform and that large aggregates coexist with tactoids stacks of two or three platelets. The nano structure of materials was correlated with its thermomechanical properties obtained by DMTA. The results showed an increase in Tg of the materials to clay content of up to 5 wt % and an increase in the storage modulus for the epoxy matrix. (author)
Clay minerals behaviour in thin sandy clay-rich lacustrine turbidites (Lake Hazar, Turkey)
El Ouahabi, Meriam; Hubert-Ferrari, Aurelia; Lamair, Laura; Hage, Sophie
2017-04-01
Turbidites have been extensively studied in many different areas using cores or outcrop, which represent only an integrated snapshot of a dynamic evolving flow. Laboratory experiments provide the missing relationships between the flow characteristics and their deposits. In particular, flume experiments emphasize that the presence of clay plays a key role in turbidity current dynamics. Clay fraction, in small amount, provides cohesive strength to sediment mixtures and can damp turbulence. However, the degree of flocculation is dependent on factors such as the amount and size of clay particles, the surface of clay particles, chemistry and pH conditions in which the clay particles are dispersed. The present study focuses on thin clayey sand turbidites found in Lake Hazar (Turkey) occurring in stacked thin beds. Depositional processes and sources have been previously studied and three types were deciphered, including laminar flows dominated by cohesion, transitional, and turbulence flow regimes (Hage et al., in revision). For the purpose of determine the clay behavior in the three flow regimes, clay mineralogical, geochemical measurements on the cores allow characterising the turbidites. SEM observations provide further information regarding the morphology of clay minerals and other clasts. The study is particularly relevant given the highly alkaline and saline water of the Hazar Lake. Clay minerals in Hazar Lake sediments include kaolinite (1:1-type), illite and chlorite (2:1-type). Hazar lake water is alkaline having pH around 9.3, in such alkaline environment, a cation-exchange reaction takes place. Furthermore, in saline water (16‰), salts can act as a shield and decrease the repulsive forces between clay particle surfaces. So, pH and salt content jointly impact the behaviour of clays differently. Since the Al-faces of clay structures have a negative charge in basic solutions. At high pH, all kaolinite surfaces become negative-charged, and then kaolinite
Rheological properties of purified illite clays in glycerol/water suspensions
Dusenkova, I.; Malers, J.; Berzina-Cimdina, L.
2015-04-01
There are many studies about rheological properties of clay-water suspensions, but no published investigations about clay-glycerol suspensions. In this work apparent viscosity of previously purified illite containing clay fraction clay minerals were almost totally removed by centrifugation. All obtained suspensions behaved as shear-thinning fluids with multiple times higher viscosity than pure glycerol/water solutions. Reduction of clay fraction concentration by 5% decreased the apparent viscosity of 50% glycerol/water suspensions approximately 5 times. There was basically no difference in apparent viscosity between all four 50% glycerol/water suspensions, but in 90% glycerol/water suspensions samples from Iecava deposit showed slightly higher apparent viscosity, which could be affected by the particle size distribution.
Preparation and characterization of bentonite organo clay
International Nuclear Information System (INIS)
Bertagnolli, C.; Almeida Neto, A.F.; Silva, M.G.C.
2009-01-01
Bentonite clays organically modified have great potential use for environmental remediation, especially in the separation of organic compounds from the water. The aim of this work was the preparation of organophilic clays from 'Verde-Lodo' bentonite clay with the quaternary ammonium salts cetyl-pyridinium chloride and benzalkonium chloride. The materials obtained were characterized by XRD, thermogravimetric analyses, Helium picnometry, SEM and energy dispersive X-ray techniques. The results show consistently successful synthesis of the organoclay through the increase in the basal spacing, as well as salt elimination picks and presence of carbon and chlorine in the modified clays; they are inexistent elements in the natural clay. (author)
Heteroaggregation of titanium dioxide nanoparticles with natural clay colloids.
Labille, Jérôme; Harns, Carrie; Bottero, Jean-Yves; Brant, Jonathan
2015-06-02
To better understand and predict the fate of engineered nanoparticles in the water column, we assessed the heteroaggregation of TiO2 nanoparticles with a smectite clay as analogues for natural colloids. Heteroaggregation was evaluated as a function of water salinity (10(-3) and 10(-1) M NaCl), pH (5 and 8), and selected nanoparticle concentration (0-4 mg/L). Time-resolved laser diffraction was used, coupled to an aggregation model, to identify the key mechanisms and variables that drive the heteroaggregation of the nanoparticles with colloids. Our data show that, at a relevant concentration, nanoparticle behavior is mainly driven by heteroaggregation with colloids, while homoaggregation remains negligible. The affinity of TiO2 nanoparticles for clay is driven by electrostatic interactions. Opposite surface charges and/or high ionic strength favored the formation of primary heteroaggregates via the attachment of nanoparticles to the clay. The initial shape and dispersion state of the clay as well as the nanoparticle/clay concentration ratio also affected the nature of the heteroaggregation mechanism. With dispersed clay platelets (10(-3) M NaCl), secondary heteroaggregation driven by bridging nanoparticles occurred at a nanoparticle/clay number ratio of greater than 0.5. In 10(-1) M NaCl, the clay was preaggregated into larger and more spherical units. This favored secondary heteroaggregation at lower nanoparticle concentration that correlated to the nanoparticle/clay surface area ratio. In this latter case, a nanoparticle to clay sticking efficiency could be determined.
Energy Technology Data Exchange (ETDEWEB)
Miranda, G.S.; Delpechi, M.C.; Santo, W.L.E., E-mail: mcd@uerj.b [Universidade do Estado do Rio de Janeiro (UERJ), RJ (Brazil)
2010-07-01
Several studies involving the formation of polyurethane nanocomposites employing clays of montmorillonite modified. This involves the presence of quaternary ammonium salts, the cation exchange needed to increase the interlayer space of clays that incorporate more than one step to the process, generates a higher cost. In this paper the synthesis of nanocomposite polyurethanes dispersed in water allowed not only the production of materials less harmful to the environment, but also the incorporation of hydrophilic clays, calcium and sodium in nature, without any modifications. Dispersions produced from 0.5, 1.0 and 2.5% clay (on the mass of prepolymer) were characterized in terms of total solids content, the films obtained by casting were evaluated for adhesiveness, diffraction X-rays, scanning electron microscopy. Most systems showed intercalated and partially exfoliated structures. (author)
Water-clay interactions. Experimental study
International Nuclear Information System (INIS)
Gaucher, Eric
1998-01-01
Clay minerals contribute to the chemical composition of soil and sediment groundwaters via surface and dissolution/precipitation reactions. The understanding of those processes is still today fragmentary. In this context, our experimental purpose is to identify the contribution of each reaction in the chemical composition of water in a water/clay System. Kaolinite, illite, montmorillonite are the reference clays. After a fine mineralogical study, the exchange equilibria between K + and H + are characterised. Different exchange sites are identified and the exchange capacities and selectivity coefficients are quantified. Then, mixtures of the three clays are equilibrated with acidic and basic (I≤10 -2 M) solutions at 25 deg. C, 60 deg. C, 80 deg. C, during 320 days. The System evolution is observed by chemical analysis of the solutions and mineralogical analysis by TEM. We show that montmorillonite is unstable compared to the kaolinite/amorphous silica assemblage for solutions of pH<7. Aqueous silica is probably controlled by the kinetics of dissolution of the montmorillonite in moderate pH media. In more acidic solutions, amorphous silica precipitates. Al is under control of 'kaolinite' neo-formations. The use of the selectivity coefficients in a numerical simulation shows that K + concentration depends on exchange reactions. The pH has a more complicated evolution, which is not completely understood. This evolution depends on both exchange equilibria and organic acid occurrence. In this type of experiments, we have demonstrated that the equilibrium equations between smectite and kaolinite are inexact. The problem of the thermodynamic nature of clays remains and is not resolved by these solubility experiments. (author) [fr
Polyethersulfone/clay membranes and its water permeability
International Nuclear Information System (INIS)
Cavalho, Thamyres Cardoso de; Medeiros, Vanessa da Nobrega; Araujo, Edcleide Maria de; Lira, Helio Lucena; Leite, Amanda Melissa Damiao
2017-01-01
Membranes can be considered polymeric or inorganic films that function as a semipermeable barrier to filtration on a molecular scale, separating two phases and restricting, totally or partially, the transportation of one or more chemical species (solute) present in the solution. Therefore, the aim of this work is to produce polyethersulfone membranes (PES) and polyethersulfone/clay by phase inversion technique and evaluate the presence of clay in obtaining membranes for wastewater treatment. The used solvent was dimethylformamide (DMF) and clays were Brasgel PA (MMT) and Cloisite Na (CL Na) in the proportion of 3 to 5% (wt.). By Xray diffraction (XRD), the membranes with 3% of MMT and CL Na clays apparently had partially exfoliated structures. For the composition with 5% of CL Na a small peak was observed, which indicates that this is possibly an intercalated structure or microcomposite. By scanning electron microscopy (SEM), visualizes that the pure surface of the pure PES membrane a structure apparently without pores was observed in the used magnification and without roughness surface when compared to membranes with clay. The measurements of contact angle indicated that the inclusion of clay altered the wetting ability of the membranes. The flow with distilled water for all membranes started high and over time reached a stabilization level. Thus, it can be concluded that the presence and the content of clay altered the morphology of the membrane, contributing to an increase in water flow. (author)
Dynamics of confined reactive water in smectite clay-zeolite composites.
Pitman, Michael C; van Duin, Adri C T
2012-02-15
The dynamics of water confined to mesoporous regions in minerals such as swelling clays and zeolites is fundamental to a wide range of resource management issues impacting many processes on a global scale, including radioactive waste containment, desalination, and enhanced oil recovery. Large-scale atomic models of freely diffusing multilayer smectite particles at low hydration confined in a silicalite cage are used to investigate water dynamics in the composite environment with the ReaxFF reactive force field over a temperature range of 300-647 K. The reactive capability of the force field enabled a range of relevant surface chemistry to emerge, including acid/base equilibria in the interlayer calcium hydrates and silanol formation on the edges of the clay and inner surface of the zeolite housing. After annealing, the resulting clay models exhibit both mono- and bilayer hydration structures. Clay surface hydration redistributed markedly and yielded to silicalite water loading. We find that the absolute rates and temperature dependence of water dynamics compare well to neutron scattering data and pulse field gradient measures from relevant samples of Ca-montmorillonite and silicalite, respectively. Within an atomistic, reactive context, our results distinguish water dynamics in the interlayer Ca(OH)(2)·nH(2)O environment from water flowing over the clay surface, and from water diffusing within silicalite. We find that the diffusion of water when complexed to Ca hydrates is considerably slower than freely diffusing water over the clay surface, and the reduced mobility is well described by a difference in the Arrhenius pre-exponential factor rather than a change in activation energy.
Modified montmorillonite clay microparticles for stable oil-in-seawater emulsions.
Dong, Jiannan; Worthen, Andrew J; Foster, Lynn M; Chen, Yunshen; Cornell, Kevin A; Bryant, Steven L; Truskett, Thomas M; Bielawski, Christopher W; Johnston, Keith P
2014-07-23
Environmentally benign clay particles are of great interest for the stabilization of Pickering emulsions. Dodecane-in-synthetic seawater (SSW) emulsions formed with montmorillonite (MMT) clay microparticles modified with bis(2-hydroxyethyl)oleylamine were stable against coalescence, even at clay concentrations down to 0.1% w/v. Remarkably, as little as 0.001% w/v surfactant lowered the hydrophilicity of the clay to a sufficient level for stabilization of oil-in-SSW emulsions. The favorable effect of SSW on droplet size reduction and emulsion stability enhancement is hypothesized to be due to reduced electrostatic repulsion between adsorbed clay particles and a consequent increase in the continuous phase (an aqueous clay suspension) viscosity. Water/oil (W/O) emulsions were inverted to O/W either by decreasing the mass ratio of surfactant-to-clay (transitional inversion) or by increasing the water volume fraction (catastrophic inversion). For both types of emulsions, coalescence was minimal and the sedimentation or creaming was highly correlated with the droplet size. For catastrophic inversions, the droplet size of the emulsions was smaller in the case of the preferred curvature. Suspensions of concentrated clay in oil dispersions in the presence of surfactant were stable against settling. The mass transfer pathways during emulsification of oil containing the clay particles were analyzed on the droplet size/stability phase diagrams to provide insight for the design of dispersant systems for remediating surface and subsurface oceanic oil spills.
[Mechanism of tritium persistence in porous media like clay minerals].
Wu, Dong-Jie; Wang, Jin-Sheng; Teng, Yan-Guo; Zhang, Ke-Ni
2011-03-01
To investigate the mechanisms of tritium persistence in clay minerals, three types of clay soils (montmorillonite, kaolinite and illite) and tritiated water were used in this study to conduct the tritium sorption tests and the other related tests. Firstly, the ingredients, metal elements and heat properties of clay minerals were studied with some instrumental analysis methods, such as ICP and TG. Secondly, with a specially designed fractionation and condensation experiment, the adsorbed water, the interlayer water and the structural water in the clay minerals separated from the tritium sorption tests were fractionated for investigating the tritium distributions in the different types of adsorptive waters. Thirdly, the location and configuration of tritium adsorbed into the structure of clay minerals were studied with infrared spectrometry (IR) tests. And finally, the forces and mechanisms for driving tritium into the clay minerals were analyzed on the basis of the isotope effect of tritium and the above tests. Following conclusions have been reached: (1) The main reason for tritium persistence in clay minerals is the entrance of tritium into the adsorbed water, the interlayer water and the structural water in clay minerals. The percentage of tritium distributed in these three types of adsorptive water are in the range of 13.65% - 38.71%, 0.32% - 5.96%, 1.28% - 4.37% of the total tritium used in the corresponding test, respectively. The percentages are different for different types of clay minerals. (2) Tritium adsorbed onto clay minerals are existed in the forms of the tritiated hydroxyl radical (OT) and the tritiated water molecule (HTO). Tritium mainly exists in tritiated water molecule for adsorbed water and interlayer water, and in tritiated hydroxyl radical for structural water. (3) The forces and effects driving tritium into the clay minerals may include molecular dispersion, electric charge sorption, isotope exchange and tritium isotope effect.
Bore, Thierry; Wagner, Norman; Delepine Lesoille, Sylvie; Taillade, Frederic; Six, Gonzague; Daout, Franck; Placko, Dominique
2016-01-01
Broadband electromagnetic frequency or time domain sensor techniques present high potential for quantitative water content monitoring in porous media. Prior to in situ application, the impact of the relationship between the broadband electromagnetic properties of the porous material (clay-rock) and the water content on the frequency or time domain sensor response is required. For this purpose, dielectric properties of intact clay rock samples experimental determined in the frequency range from 1 MHz to 10 GHz were used as input data in 3-D numerical frequency domain finite element field calculations to model the one port broadband frequency or time domain transfer function for a three rods based sensor embedded in the clay-rock. The sensor response in terms of the reflection factor was analyzed in time domain with classical travel time analysis in combination with an empirical model according to Topp equation, as well as the theoretical Lichtenecker and Rother model (LRM) to estimate the volumetric water content. The mixture equation considering the appropriate porosity of the investigated material provide a practical and efficient approach for water content estimation based on classical travel time analysis with the onset-method. The inflection method is not recommended for water content estimation in electrical dispersive and absorptive material. Moreover, the results clearly indicate that effects due to coupling of the sensor to the material cannot be neglected. Coupling problems caused by an air gap lead to dramatic effects on water content estimation, even for submillimeter gaps. Thus, the quantitative determination of the in situ water content requires careful sensor installation in order to reach a perfect probe clay rock coupling. PMID:27096865
Directory of Open Access Journals (Sweden)
Thierry Bore
2016-04-01
Full Text Available Broadband electromagnetic frequency or time domain sensor techniques present high potential for quantitative water content monitoring in porous media. Prior to in situ application, the impact of the relationship between the broadband electromagnetic properties of the porous material (clay-rock and the water content on the frequency or time domain sensor response is required. For this purpose, dielectric properties of intact clay rock samples experimental determined in the frequency range from 1 MHz to 10 GHz were used as input data in 3-D numerical frequency domain finite element field calculations to model the one port broadband frequency or time domain transfer function for a three rods based sensor embedded in the clay-rock. The sensor response in terms of the reflection factor was analyzed in time domain with classical travel time analysis in combination with an empirical model according to Topp equation, as well as the theoretical Lichtenecker and Rother model (LRM to estimate the volumetric water content. The mixture equation considering the appropriate porosity of the investigated material provide a practical and efficient approach for water content estimation based on classical travel time analysis with the onset-method. The inflection method is not recommended for water content estimation in electrical dispersive and absorptive material. Moreover, the results clearly indicate that effects due to coupling of the sensor to the material cannot be neglected. Coupling problems caused by an air gap lead to dramatic effects on water content estimation, even for submillimeter gaps. Thus, the quantitative determination of the in situ water content requires careful sensor installation in order to reach a perfect probe clay rock coupling.
Bore, Thierry; Wagner, Norman; Lesoille, Sylvie Delepine; Taillade, Frederic; Six, Gonzague; Daout, Franck; Placko, Dominique
2016-04-18
Broadband electromagnetic frequency or time domain sensor techniques present high potential for quantitative water content monitoring in porous media. Prior to in situ application, the impact of the relationship between the broadband electromagnetic properties of the porous material (clay-rock) and the water content on the frequency or time domain sensor response is required. For this purpose, dielectric properties of intact clay rock samples experimental determined in the frequency range from 1 MHz to 10 GHz were used as input data in 3-D numerical frequency domain finite element field calculations to model the one port broadband frequency or time domain transfer function for a three rods based sensor embedded in the clay-rock. The sensor response in terms of the reflection factor was analyzed in time domain with classical travel time analysis in combination with an empirical model according to Topp equation, as well as the theoretical Lichtenecker and Rother model (LRM) to estimate the volumetric water content. The mixture equation considering the appropriate porosity of the investigated material provide a practical and efficient approach for water content estimation based on classical travel time analysis with the onset-method. The inflection method is not recommended for water content estimation in electrical dispersive and absorptive material. Moreover, the results clearly indicate that effects due to coupling of the sensor to the material cannot be neglected. Coupling problems caused by an air gap lead to dramatic effects on water content estimation, even for submillimeter gaps. Thus, the quantitative determination of the in situ water content requires careful sensor installation in order to reach a perfect probe clay rock coupling.
Energy Technology Data Exchange (ETDEWEB)
Paz, Juliana D' Avila; Bertholdi, Jonas; Folgueras, Marilena Valadares; Pezin, Sergio Henrique; Coelho, Luiz Antonio Ferreira, E-mail: julianadpaz@yahoo.com.b [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Centro de Ciencias Tecnologicas
2010-07-01
This paper presents some analysis showed that the exfoliation / intercalation of a montmorillonite clay in epoxy resin such as viscosity, X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). Increasing the viscosity of epoxy resin diglycidyl ether bisphenol A with the addition of clay associated with the sonification system at the time of dispersion is a good indication of exfoliation. The X-ray diffraction already cured composite shows a decrease of crystallinity of clay and EDS microanalysis of SEM, non-uniform dispersion of clay in epoxy resin. Thermal analysis TG composite clay / epoxy shows an increase in thermal stability relative to pure epoxy. (author)
Point-of-use water purification using clay pot water filters and copper ...
African Journals Online (AJOL)
2011-11-24
Nov 24, 2011 ... clay pot water filters (CPWFs) were fabricated using terracotta clay and sawdust. The sawdust was .... developed by educational initiatives and non-governmental .... est filtration rate, it had the disadvantage of not being able to.
Colloid and phosphorus leaching from undisturbed soil cores sampled along a natural clay gradient
DEFF Research Database (Denmark)
Vendelboe, Anders Lindblad; Møldrup, Per; Heckrath, Goswin Johann
2011-01-01
correlated to the accumulated outflow and was described as a diffusion controlled process, using ¾(accumulated outflow). The mass of leached particles was positively correlated to the clay content as well as to water-dispersible colloids. Particulate phosphorus (P) was linearly correlated to concentration......The presence of strongly sorbing compounds in groundwater and tile drains can be a result of colloid-facilitated transport. Colloid and phosphorus leaching from macropores in undisturbed soil cores sampled across a natural clay gradient at Aarup, Denmark, were studied. The aim of the study...... was to correlate easily measurable soil properties, such as clay content and water-dispersible colloids, to colloid and phosphorus leaching. The clay contents across the gradient ranged from 0.11 to 0.23 kg kgj1. Irrigating with artificial rainwater, all samples showed a high first flush of colloids and phosphorus...
Evaluation of the Efficiency of Clay Pots in Removal of Water Impurities
Directory of Open Access Journals (Sweden)
K Naddafi , AH Mahvi, S Nasseri, M Mokhtari, H Zeraati
2005-04-01
Full Text Available Recently, inexpensive technologies for drinking water supply in small communities are highly considered in developing countries. One of these technologies is the application of ceramic filters that are usually made of diatomaceous earth or clay soil. This research was carried out to determine the efficiency of clay pots (as a filter in removing water impurities. Pilot and the related clay parts were manufactured and its efficiency in removing TDS, hardness, NO3-, color and turbidity was measured by passing water through the clay pipes. The results showed that the clay filters had not the potential to remove hardness, EC, TDS and nitrate of water. However, they showed excellent efficiency in turbidity removal (≥ 90% and could significantly decrease the color of the water (≥ 60%.
Validation of water sorption-based clay prediction models for calcareous soils
DEFF Research Database (Denmark)
Arthur, Emmanuel; Razzaghi, Fatemeh; Moosavi, Ali
2017-01-01
on prediction accuracy. The soils had clay content ranging from 9 to 61% and CaCO3 from 24 to 97%. The three water sorption models considered showed a reasonably fair prediction of the clay content from water sorption at 28% relative humidity (RMSE and ME values ranging from 10.6 to 12.1 and −8.1 to −4......Soil particle size distribution (PSD), particularly the active clay fraction, mediates soil engineering, agronomic and environmental functions. The tedious and costly nature of traditional methods of determining PSD prompted the development of water sorption-based models for determining the clay...... fraction. The applicability of such models to semi-arid soils with significant amounts of calcium carbonate and/or gypsum is unknown. The objective of this study was to validate three water sorption-based clay prediction models for 30 calcareous soils from Iran and identify the effect of CaCO3...
Soil-Water Characteristic Curves of Red Clay treated by Ionic Soil Stabilizer
Cui, D.; Xiang, W.
2009-12-01
The relationship of red clay particle with water is an important factor to produce geological disaster and environmental damage. In order to reduce the role of adsorbed water of red clay in WuHan, Ionic Soil Stabilizer (ISS) was used to treat the red clay. Soil Moisture Equipment made in U.S.A was used to measure soil-water characteristic curve of red clay both in natural and stabilized conditions in the suction range of 0-500kPa. The SWCC results were used to interpret the red clay behavior due to stabilizer treatment. In addition, relationship were compared between the basic soil and stabilizer properties such as water content, dry density, liquid limit, plastic limit, moisture absorption rate and stabilizer dosages. The analysis showed that the particle density and specific surface area increase, the dehydration rate slows and the thickness of water film thins after treatment with Ionic Soil Stabilizer. After treatment with the ISS, the geological disasters caused by the adsorbed water of red clay can be effectively inhibited.
Water retention properties of Callovo-Oxfordian clay-stone
International Nuclear Information System (INIS)
Wan, Min; Delage, Pierre; Tang, Anh Minh; GATMIRI, Behrouz
2012-01-01
Document available in extended abstract form only. Many investigations were carried out on the Callovo-Oxfordian (COx) clay-stone that has been selected by the French radioactive waste management agency (ANDRA) as a potential host rock for high level radioactive waste disposal at great depth. Various authors demonstrated the significant water sensitivity of clay-stones. Some cracks generated by desaturation have been observed in the Tournemire URL (France) excavated in clay-stone. By carrying out some ESEM (environmental scanning electron microscope) observations on COx clay-stone samples submitted to cyclic changes in relative humidity, Montes et al. (2004) evidenced the water sensitivity of the clay fraction, with significant successive openings and closures of cracks and pores. Hysteresis effects have been observed in the water retention curve, in the ultrasonic velocity evolution and in the strain changes induced by hydration cycles on COx samples submitted to controlled relative humidities by Pham et al., (2007). Better knowledge of the mechanism of desaturation of the clay-stone is necessary to further understand the changes in hydro-mechanical properties of the excavation damaged zone (EDZ) that becomes significantly de-saturated all around the galleries because of ventilation. In this framework, a detailed study of the water retention properties of the COx clay-stone was carried out i) to complete existing observations with respect to volume changes under suction cycles and ii) to determine the main drying and wetting curves so as to better investigate hysteresis effects in the water retention curve.. Particular attention was paid to the characterization of the initial state in the laboratory (where samples are provided unsaturated due to the combined effect of coring, storage and transportation) and to the volume changes and changes in degree of saturation along the main wetting and drying paths. The determination of the water retention properties was
Studies on Tagged Clay Migration Due to Water Movement
International Nuclear Information System (INIS)
Scharpenseel, H.W.; Kerpen, W.
1967-01-01
55 Fe-tagged clay minerals, produced by hydrothermal synthesis, serve to clarify the question whether clay migration or clay formation in situ is the predominating mechanism in the B t -development of Parabraunerde (sol brun lessive, grey brown podsolic, hapludalf, dernopodsol). They further indicate the possibilities of clay transportation caused by water percolation. Suitable experimental approaches, such as thin-layer chromatography and autoradiography, translocation tests in columns filled with monotypical textural fractions or with undisturbed soil profiles, and synchronous hydrothermal treatment of 55 Fe-con raining material from different horizons of Parabraunerde, to reveal the specific readiness of the different profile zones for 55 Fe-clay production, are described. The possibilities of clay percolation are discussed. (author)
International Nuclear Information System (INIS)
Tachi, Yukio; Suyama, Tadahiro; Ochs, Michael
2014-01-01
To predict the long-term migration of radionuclides (RNs) under variable conditions within the framework of safety analyses for geological disposal, thermodynamic sorption models are very powerful tools. The integrated sorption and diffusion (ISD) model for compacted bentonite was developed to achieve a consistent combination of clay–water interaction, sorption, and diffusion models. The basic premise considered in the ISD model was to consistently use the same simple surface model design and parameters for describing RNs sorption/diffusion as well as clay surface and porewater chemistry. A simple 1-site non-electrostatic surface complexation model in combination with a 1-site ion exchange model was selected to keep sorption model characteristics relatively robust for compacted systems. Fundamental parameters for the proposed model were evaluated from surface titration data for purified montmorillonite. The resulting basic model was then parameterized on the basis of selected published sorption data-sets for Np(V), Am(III), and U(VI) in dispersed systems, which cover a range of key geochemical conditions such as pH, ionic strength, and carbonate concentration. The sorption trends for these RNs can be quantitatively described by the model considering a full suite of surface species including hydrolytic and carbonate species. The application of these models to the description of diffusive-sorptive transport in compacted bentonites is presented in Part 2. (author)
Use of the crumb test as a preliminary indicator of dispersive soils
CSIR Research Space (South Africa)
Maharaj, A
2011-07-01
Full Text Available to overcome them. Keywords: Dispersive soils, dispersion, failure, identification, crumb test, shortcomings Introduction Dispersive soils are those soils, which when immersed in relatively pure and still water will deflocculate causing the clay particles... developed by Emerson for the classification of soils. Immerse dry aggregates in water Slaking No slaking Complete Dispersion (Class 1) Some Dispersion (Class 2) No Dispersion Swelling (Class 7) No Swelling (Class 8) Remould at water...
Clay with Desiccation Cracks is an Advection Dominated Environment
Baram, S.; Kurtzman, D.; Sher, Y.; Ronen, Z.; Dahan, O.
2012-04-01
Heavy clay sediments are regarded "safe" from the hydrological point of view due to their low hydraulic conductivities. However, the formation of desiccation cracks in dispersive clays may dramatically change their bulk hydraulic properties. The impact of desiccation cracks on water percolation, dissolved salts and contaminants transport and redox related reactions (microbial ammonium oxidation and denitrification) were investigated in 6 -12 m clay layer near a diary farm waste lagoon. The study implemented unique vadose-zone monitoring systems that enable in-situ measurements of the temporal variation of the sediment's water content along with frequent sampling of the sediment's pore water along the entire vadose zone (> 30 m). Results from four years of continuous measurements showed quick rises in sediment water content following rain events and temporal wastewater overflows. The percolation pattern indicated dominance of preferential flow through a desiccation-cracks network crossing the entire clay sediment layer. High water-propagation velocities (0.4 - 23.6 m h-1) were observed, indicating that the desiccation-crack network remains open and serves as a preferential flow pathway year-round, even at high sediment water content (~0.50 m3 m-3). The rapid percolation bypassed the most bio-geo-active parts of the soil, transporting even highly sorptive contaminants (testosterone and estrogen) in to the deep sections of the vadose zone, accelerating the underlying groundwater contamination. The ammonium and nitrate concentrations in the vadose zone and the high number of nitrifying and denitrifying bacteria (~108 gene copies gdry-sediemt-1, each) found in the sediment indicated that the entire vadose zone is aerated even at high water content conditions (~0.55 m3 m-3). The dissolved salts concentration in the pore-water and the δ2H-H2O and δ18O-H2O values of the pore-water substantially increased with depth (becoming less depleted) in the clay sediment
Water diffusion through compacted clays analyzed by neutron scattering and tracer experiments
Energy Technology Data Exchange (ETDEWEB)
Gonzalez Sanchez, F
2007-11-15
Clay minerals are aluminium phyllosilicates, mostly products of the chemical alteration and mechanical breakdown of igneous and metamorphic rocks. Their physical and chemical properties can be directly related to their layered, fine-grained (large surface area) structure. These properties such as large water retention, low hydraulic conductivity, heat resistance and ionic exchange capacities, make clays ideal for many different applications, e.g. as sealing material for the underground disposal of radioactive waste. The long-term disposal of radioactive waste in an underground geological repository is based on a multibarrier concept. In the barrier of highly compacted clay, water is intercalated and confined between the clay layers. The narrow pores are responsible that under natural hydraulic gradients, molecular diffusion through water is the dominant transport mechanism for released radionuclides. The properties of water at the water-clay interface differ from that of bulk water. Therefore, a good and deep understanding of the water structure and dynamics in compacted clay systems is fundamental. This knowledge is the base for the progressing research about transport of pollutants through the compacted clays and argillaceous rock of radioactive waste barriers. This study focusses on four different types of pure clays, two of them charged, namely montmorillonite and illite (both in a Na and Ca form), and two uncharged, namely kaolinite and pyrophyllite. Their structural differences result in a significantly different behaviour in contact with water. In case of montmorillonite, water is located in between particles and in the interlayer space. In illite, water is found only in between particles, because the interlayer surfaces are tightly linked by potassium cations. The layers of kaolinite and pyrophyllite are uncharged and, consequently, water is located only in between particles. The clay powders were compacted to reach a high bulk dry density of about 1.9 g
Water diffusion through compacted clays analyzed by neutron scattering and tracer experiments
International Nuclear Information System (INIS)
Gonzalez Sanchez, F.
2007-11-01
Clay minerals are aluminium phyllosilicates, mostly products of the chemical alteration and mechanical breakdown of igneous and metamorphic rocks. Their physical and chemical properties can be directly related to their layered, fine-grained (large surface area) structure. These properties such as large water retention, low hydraulic conductivity, heat resistance and ionic exchange capacities, make clays ideal for many different applications, e.g. as sealing material for the underground disposal of radioactive waste. The long-term disposal of radioactive waste in an underground geological repository is based on a multibarrier concept. In the barrier of highly compacted clay, water is intercalated and confined between the clay layers. The narrow pores are responsible that under natural hydraulic gradients, molecular diffusion through water is the dominant transport mechanism for released radionuclides. The properties of water at the water-clay interface differ from that of bulk water. Therefore, a good and deep understanding of the water structure and dynamics in compacted clay systems is fundamental. This knowledge is the base for the progressing research about transport of pollutants through the compacted clays and argillaceous rock of radioactive waste barriers. This study focusses on four different types of pure clays, two of them charged, namely montmorillonite and illite (both in a Na and Ca form), and two uncharged, namely kaolinite and pyrophyllite. Their structural differences result in a significantly different behaviour in contact with water. In case of montmorillonite, water is located in between particles and in the interlayer space. In illite, water is found only in between particles, because the interlayer surfaces are tightly linked by potassium cations. The layers of kaolinite and pyrophyllite are uncharged and, consequently, water is located only in between particles. The clay powders were compacted to reach a high bulk dry density of about 1.9 g
Directory of Open Access Journals (Sweden)
Vincenzo Baglio
2012-06-01
Full Text Available Water and methanol transport behavior, solvents adsorption and electrochemical properties of filler-free Nafion and nanocomposites based on two smectite clays, were investigated using impedance spectroscopy, DMFC tests and NMR methods, including spin-lattice relaxation and pulsed-gradient spin-echo (PGSE diffusion under variable temperature conditions. Synthetic (Laponite and natural (Swy-2 smectite clays, with different structural and physical parameters, were incorporated into the Nafion for the creation of exfoliated nanocomposites. Transport mechanism of water and methanol appears to be influenced from the dimensions of the dispersed platelike silicate layers as well as from their cation exchange capacity (CEC. The details of the NMR results and the effect of the methanol solution concentration are discussed. Clays particles, and in particular Swy-2, demonstrate to be a potential physical barrier for methanol cross-over, reducing the methanol diffusion with an evident blocking effect yet nevertheless ensuring a high water mobility up to 130 °C and for several hours, proving the exceptional water retention property of these materials and their possible use in the DMFCs applications. Electrochemical behavior is investigated by cell resistance and polarization measurements. From these analyses it is derived that the addition of clay materials to recast Nafion decreases the ohmic losses at high temperatures extending in this way the operating range of a direct methanol fuel cell.
Studies on Tagged Clay Migration Due to Water Movement
Energy Technology Data Exchange (ETDEWEB)
Scharpenseel, H. W. [Institut fuer Bodenkunde der Universitaet Bonn, Federal Republic of Germany (Germany); Kerpen, W. [Arbeitsgruppe, Institut fuer Landwirtschaft der KFA Juelich, Bonn, Federal Republic of Germany (Germany)
1967-11-15
{sup 55}Fe-tagged clay minerals, produced by hydrothermal synthesis, serve to clarify the question whether clay migration or clay formation in situ is the predominating mechanism in the B{sub t}-development of Parabraunerde (sol brun lessive, grey brown podsolic, hapludalf, dernopodsol). They further indicate the possibilities of clay transportation caused by water percolation. Suitable experimental approaches, such as thin-layer chromatography and autoradiography, translocation tests in columns filled with monotypical textural fractions or with undisturbed soil profiles, and synchronous hydrothermal treatment of {sup 55}Fe-con raining material from different horizons of Parabraunerde, to reveal the specific readiness of the different profile zones for {sup 55}Fe-clay production, are described. The possibilities of clay percolation are discussed. (author)
Kauffman, S.J.; Herman, J.S.; Jones, B.F.
1998-01-01
The influence of clay units on ground-water composition was investigated in a heterogeneous carbonate aquifer system of Miocene age in southwest Florida, known as the Intermediate aquifer system. Regionally, the ground water is recharged inland, flows laterally and to greater depths in the aquifer systems, and is discharged vertically upward at the saltwater interface along the coast. A depth profile of water composition was obtained by sampling ground water from discrete intervals within the permeable carbonate units during coring and by squeezing pore water from a core of the less-permeable clay layers. A normative salt analysis of solute compositions in the water indicated a marine origin for both types of water and an evolutionary pathway for the clay water that involves clay diagenesis. The chemical composition of the ground water in the carbonate bedrock is significantly different from that of the pore water in the clay layers. Dissolution of clays and opaline silica results in high silica concentrations relative to water in other parts of the Intermediate aquifer system. Water enriched in chloride relative to the overlying and underlying ground water recharges the aquifer inland where the confining clay layer is absent, and it dissolves carbonate and silicate minerals and reacts with clays along its flow path, eventually reaching this coastal site and resulting in the high chloride and silica concentrations observed in the middle part of the Intermediate aquifer system. Reaction-path modeling suggests that the recharging surficial water mixes with sulfate-rich water upwelling from the Upper Floridan aquifer, and carbonate mineral dissolution and precipitation, weathering and exchange reactions, clay mineral diagenesis, clay and silica dissolution, organic carbon oxidation, and iron and sulfate reduction result in the observed water compositions.A study was conducted to clarify the influence of clay units on ground-water composition in a heterogeneous
Selective Clay Placement Within a Silicate-Clay Epoxy Blend Nanocomposite
Miller, Sandi G (Inventor)
2013-01-01
A clay-epoxy nanocomposite may be prepared by dispersing a layered clay in an alkoxy epoxy, such as a polypropylene oxide based epoxide before combining the mixture with an aromatic epoxy to improve the nanocomposite's thermal and mechanical properties.
Water Retention Curves of Opalinus Clay
International Nuclear Information System (INIS)
Villar, M. V.; Romero, F. J.
2012-01-01
The water retention curve of Opalinus clay samples was determined under different conditions: total and matric suction, stress or no-stress conditions, wetting and drying paths. Through the fitting of these results to the van Genuchten expression the P parameter, related to the air entry value (AEV), was obtained. The AEV is the suction value above which air is able to enter the pores of the sample, and consequently, above which 2-phase flow can take place in the soil pore structure. The samples used in this research came from two different boreholes, BHT-1 and BHG-D1, but the behaviour of them did not depend on their location, what was probably due to the fact that both were drilled in the shay facies of the Opalinus clay. There was not a distinct difference between the results obtained under total or matric suctions. In the drying paths, both the water contents and the degrees of saturation tended to be higher when total suction was applied, however the reverse trend was observed for the water contents reached in wetting paths. As well, no clear difference was observed in the water retention curves obtained in odometers under matric and total suctions, what points to the osmotic component of suction in Opalinus clay not being significant. Overall, the water contents were lower and the degrees of saturation higher when suction was applied under vertical stress, what would indicate that the water retention capacity was lower under 8 MPa vertical stress than under free volume conditions. This vertical stress value is slightly higher than the maximum in situ stress. Also, the samples showed hysteresis according to the expected behaviour, i.e. the water contents for a given suction were higher during a drying path than during a wetting path. The P values obtained were between 6 and 34 MPa, and tended to be higher for the samples tested under stress, in drying paths and when total suction was used. The air entry value calculated from the mercury intrusion porosimetry
Water Retention Curves of Opalinus Clay
Energy Technology Data Exchange (ETDEWEB)
Villar, M. V.; Romero, F. J.
2012-11-01
The water retention curve of Opalinus clay samples was determined under different conditions: total and matric suction, stress or no-stress conditions, wetting and drying paths. Through the fitting of these results to the van Genuchten expression the P parameter, related to the air entry value (AEV), was obtained. The AEV is the suction value above which air is able to enter the pores of the sample, and consequently, above which 2-phase flow can take place in the soil pore structure. The samples used in this research came from two different boreholes, BHT-1 and BHG-D1, but the behaviour of them did not depend on their location, what was probably due to the fact that both were drilled in the shay facies of the Opalinus clay. There was not a distinct difference between the results obtained under total or matric suctions. In the drying paths, both the water contents and the degrees of saturation tended to be higher when total suction was applied, however the reverse trend was observed for the water contents reached in wetting paths. As well, no clear difference was observed in the water retention curves obtained in odometers under matric and total suctions, what points to the osmotic component of suction in Opalinus clay not being significant. Overall, the water contents were lower and the degrees of saturation higher when suction was applied under vertical stress, what would indicate that the water retention capacity was lower under 8 MPa vertical stress than under free volume conditions. This vertical stress value is slightly higher than the maximum in situ stress. Also, the samples showed hysteresis according to the expected behaviour, i.e. the water contents for a given suction were higher during a drying path than during a wetting path. The P values obtained were between 6 and 34 MPa, and tended to be higher for the samples tested under stress, in drying paths and when total suction was used. The air entry value calculated from the mercury intrusion porosimetry
Effects of modified Clay on the morphology and thermal stability of PMMA/clay nanocomposites
International Nuclear Information System (INIS)
Tsai, Tsung-Yen; Lin, Mei-Ju; Chuang, Yi-Chen; Chou, Po-Chiang
2013-01-01
The potential to improve the mechanical, thermal, and optical properties of poly(methyl methacrylate) (PMMA)/clay nanocomposites prepared with clay containing an organic modifier was investigated. Pristine sodium montmorillonite clay was modified using cocoamphodipropionate, which absorbs UVB in the 280–320 nm range, via ion exchange to enhance the compatibility between the clay platelets and the methyl methacrylate polymer matrix. PMMA/clay nanocomposites were synthesized via in situ free-radical polymerization. Three types of clay with various cation-exchange capacities (CEC) were used as inorganic layered materials in these organic–inorganic hybrid nanocomposites: CL42, CL120, and CL88 with CEC values of 116, 168, and 200 meq/100 g of clay, respectively. We characterized the effects of the organoclay dispersion on UV resistance, effectiveness as an O 2 gas barrier, thermal stability, and mechanical properties of PMMA/clay nanocomposites. Gas permeability analysis demonstrated the excellent gas barrier properties of the nanocomposites, consistent with the intercalated or exfoliated morphologies observed. The optical properties were assessed using UV–Visible spectroscopy, which revealed that these materials have good optical clarity, UV resistance, and scratch resistance. The effect of the dispersion capability of organoclay on the thermal properties of PMMA/clay nanocomposites was investigated by thermogravimetric analysis and differential scanning calorimetry; these analyses revealed excellent thermal stability of some of the modified clay nanocomposites. - Highlights: ► We control the dispersion morphology by protonation of K2 into the clay. ► The CL120 and CL88, with the higher CEC, are more random intercalated by K2. ► We report these materials have good optical clarity, and UV resistance
Herich, Hanna; Tritscher, Torsten; Wiacek, Aldona; Gysel, Martin; Weingartner, Ernest; Lohmann, Ulrike; Baltensperger, Urs; Cziczo, Daniel J
2009-09-28
Airborne mineral dust particles serve as cloud condensation nuclei (CCN), thereby influencing the formation and properties of warm clouds. It is therefore of atmospheric interest how dust aerosols with different mineralogy behave when exposed to high relative humidity (RH) or supersaturation (SS) with respect to liquid water. In this study the subsaturated hygroscopic growth and the supersaturated cloud condensation nucleus activity of pure clays and real desert dust aerosols were determined using a hygroscopicity tandem differential mobility analyzer (HTDMA) and a cloud condensation nuclei counter (CCNC), respectively. Five different illite, montmorillonite and kaolinite clay samples as well as three desert dust samples (Saharan dust (SD), Chinese dust (CD) and Arizona test dust (ATD)) were investigated. Aerosols were generated both with a wet and a dry disperser. The water uptake was parameterized via the hygroscopicity parameter kappa. The hygroscopicity of dry generated dust aerosols was found to be negligible when compared to processed atmospheric aerosols, with CCNC derived kappa values between 0.00 and 0.02 (the latter corresponds to a particle consisting of 96.7% by volume insoluble material and approximately 3.3% ammonium sulfate). Pure clay aerosols were generally found to be less hygroscopic than natural desert dust particles. The illite and montmorillonite samples had kappa approximately 0.003. The kaolinite samples were less hygroscopic and had kappa=0.001. SD (kappa=0.023) was found to be the most hygroscopic dry-generated desert dust followed by CD (kappa=0.007) and ATD (kappa=0.003). Wet-generated dust showed an increased water uptake when compared to dry-generated samples. This is considered to be an artifact introduced by redistribution of soluble material between the particles. Thus, the generation method is critically important when presenting such data. These results indicate any atmospheric processing of a fresh mineral dust particle which
Enrichment and activation of smectite-poor clay
Energy Technology Data Exchange (ETDEWEB)
Sarcevica, Inese; Kostjukovs, Juris; Actint, Andris, E-mail: inese.sarcevicha@gmail.com [Department of Chemistry, University of Latvia, Kr. Valdemara street 48, Riga (Latvia)
2011-06-23
A new method of smectite clay enrichment has been developed. The method is based on dispersing clay in a phosphate solution and sequential coagulation. The product of enrichment is characterized with X-ray powder diffraction, wavelength dispersive X-ray fluorescence spectrometry, differential thermal analysis and thermogravimetry. Sorption of methylene blue and hexadecylpyridinium bromide on raw and purified clays was studied.
Radiation synthesis and characterization of thermo-sensitive PNIPA/clay hydrogels
International Nuclear Information System (INIS)
Song Hongyan; He Suqin; Liu Wentao; Zhu Chengshen; Yang Mingcheng
2007-01-01
In this work, the thermo-sensitive hydrogels of PNIPA/Clay were synthesized by 60 Co-γ rays irradiation. The effects of organically modified clay and Na + clay, clay content, and dispersing condition on swelling behavior of PNIPA/clay hydrogels were investigated. The results showed that the equilibrium swelling ratio (SR) of the PNIPA/clay hydrogels is better than PNIPA, and the SR of PNIPA/organically modified clay hydrogels is the highest. With clay content increases, the SR of hydrogels became better. The deswelling behavior of hydrogel was improved, the deswelling ratio of the hydrogel with organically modified clay is highest, and ratio of losing water is 83%, while PNIPA is about 50%. The compressive properties of hydrogel composites were also examined. The results showed that the compressive properties of the PNIPA/clay hydrogels were improved distinctly than that of the conventional hydrogels without clay. And with increasing of clay content, the compressive properties of hydrogel composites improve rapidly. When the content of clay is 15%, the maximum compression force of the PNIPA/clay hydrogel is 5.28N, which is 14 times of PNIPA hydrogel and compression strength is 2.5 times. (authors)
Influence of Clay Content, Mineralogy and Fabric On Radar Frequency Response of Aquifer Materials
West, L. J.; Handley, K.
High frequency electromagnetic methods such as ground penetrating radar (GPR) and time domain reflectometry (TDR) are widely employed to measure water saturation in the vadose zone and water filled porosity in the saturated zone. However, previous work has shown that radar frequency dielectric properties are strongly influenced by clay as well as by water content. They have also shown that that the dielectric response of clay minerals is strongly frequency dependent, and that even a small proportion of clay such as that present in many sandstone aquifers can have a large effect at typi- cal GPR frequencies (around 100MHz). Hence accurate water content/porosity deter- mination requires clay type and content to be taken into account. Reported here are dielectric measurements on clay-sand mixtures, aimed at investigating the influence of clay mineralogy, particle shape, and the geometrical arrangement of the mixture constituents on GPR and TDR response. Dielectric permittivity (at 50-1000MHz) was measured for mixtures of Ottawa Sand and various clay minerals or clay size quartz rock flour, using a specially constructed dielectric cell. Both homogeneous and layered mixtures were tested. The influence of pore water salinity, clay type, and particle arrangement on the dielectric response is interpreted in terms of dielectric dispersion mechanisms. The appropriateness of var- ious dielectric mixing rules such as the Complex Refractive Index Method (CRIM) for determination of water content or porosity from field GPR and TDR data are dis- cussed.
Contact angles at the water-air interface of hydrocarbon-contaminated soils and clay minerals
Sofinskaya, O. A.; Kosterin, A. V.; Kosterina, E. A.
2016-12-01
Contact angles at the water-air interface have been measured for triturated preparations of clays and soils in order to assess changes in their hydrophobic properties under the effect of oil hydrocarbons. Tasks have been to determine the dynamics of contact angle under soil wetting conditions and to reveal the effect of chemical removal of organic matter from soils on the hydrophilicity of preparations. The potentialities of static and dynamic drop tests for assessing the hydrophilic-hydrophobic properties of soils have been estimated. Clays (kaolinite, gumbrine, and argillite) have been investigated, as well as plow horizons of soils from the Republic of Tatarstan: heavy loamy leached chernozem, medium loamy dark gray forest soil, and light loamy soddy-calcareous soil. The soils have been contaminated with raw oil and kerosene at rates of 0.1-3 wt %. In the uncontaminated and contaminated chernozem, capillary water capacity has been maintained for 250 days. The contact angles have been found to depend on the degree of dispersion of powdered preparation, the main type of clay minerals in the soil, the presence and amount of oxidation-resistant soil organic matter, and the soil-water contact time. Characteristic parameters of mathematical models for drop behavior on triturated preparations have been calculated. Contamination with hydrocarbons has resulted in a reliable increase in the contact angles of soil preparations. The hydrophobization of soil surface in chernozem is more active than in soils poorer in organic matter. The complete restoration of the hydrophilic properties of soils after hydrocarbon contamination is due to the oxidation of easily oxidizable organic matter at the low content of humus, or to wetting during several months in the absence of the mazut fraction.
Directory of Open Access Journals (Sweden)
Maria Dolores Fidelibus
2018-03-01
Full Text Available Studies dating almost a century relate clay properties with the structure of the diffuse double layer (DDL, where the charged surfaces of clay crystal behave like an electric capacitor, whose dielectric is the interstitial fluid. The intensity of the inner electric field relates to the concentration and type of ions in the DDL. Other important implications of the model are less stressed: this part of the clay soil system, energetically speaking, is conservative. External contribution of energy, work of overburden or sun driven capillarity and long exposure to border low salinity waters can modify the concentration of pore-waters, thus affecting the DDL geometry, with electric field and energy storage variations. The study of clay soils coming from various natural geomorphological and hydrogeological contexts, determining a different salinity of interacting groundwater, shows how the clay interaction with freely circulating waters at the boundaries produces alterations in the native pore water salinity, and, at the nano-scale, variations of electric field and stored energy from external work. The swelling and the shrinkage of clay soil with their volumetric and geotechnical implications should be regarded as variations of the electrostatic and mechanical energy of the system. The study is based on tests on natural clay soil samples coming from a formation of stiff blue clays, widespread in southern Italy. Geotechnical identification and oedometer tests have been performed, and pore waters squeezed out from the specimens have been analyzed. Tested samples have similar grain size, clay fraction and plasticity; sorted according to the classified geomorphological/hydrogeological contexts, they highlight good correlations among dry density, mechanical work performed in selected stages of the oedometric test, swelling and non-swelling behaviour, and electrical conductivity of the squeezed pore waters. The work performed for swelling and non
Experimental Study on Unconfined Compressive Strength of Basalt Fiber Reinforced Clay Soil
Gao, Lei; Hu, Guohui; Xu, Nan; Fu, Junyi; Xiang, Chao; Yang, Chen
2015-01-01
In order to study the mechanism and effect of basalt fiber reinforced clay soil, a series of unconfined compressive strength tests conducted on clay soil reinforced with basalt fiber have been performed under the condition of optimum water content and maximum dry density. Both the content and length of basalt fiber are considered in this paper. When the effect of content is studied, the 12 mm long fibers are dispersed into clay soil at different contents of 0.05%, 0.1%, 0.15%, 0.20%, 0.25%, 0...
Clay Ceramic Filter for Water Treatment
Directory of Open Access Journals (Sweden)
Zereffa Enyew Amare
2017-05-01
Full Text Available Ceramic water filters were prepared from different proportions of kaolin and soft wood and sintered at 900 °C, 950 °C, and 1000 °C. The flow rate, conductivity, pH of filtered water and removal efficiency (microbial, water hardness agent’s, nitrite and turbidity were analysed. The ceramic filter with 15 % saw dust, 80 % clay and 5 % grog that was fired at temperature of 950 °C or 1000 °C showed the best removal efficiency. Statistical ANOVA tests showed a significant difference between ceramic filters with various compositions in their removal efficiencies.
Economic effectiveness of using a dispersing agent in preparing drilling fluids
Energy Technology Data Exchange (ETDEWEB)
Ubaydullayev, S R
1978-01-01
A technique is suggested for preparing argillaceous solutions with the help of a dispersing agent for laboratory studies and a set of formulas for evaluating the economic effectiveness of the obtained solution. Initially an original argillaceous solution from clay powder with viscosity of 25 s is prepared. Then the solution is treated in a laboratory ultrasonic dispersing device until the condition ''does not flow.'' After this, by adding water, viscosity of the solution is brought to 25 s, and density to 1.2 g/cm/sup 3/. In this case the output of solution after treatment by the dispersing agent is improved by 35.2%. As a result annual saving of clay of about 365 T for the Pamukskiy clay plant or R 4745 in a monetary expression is reached.
Water balance of an earth fill built of organic clay
Directory of Open Access Journals (Sweden)
Birle Emanuel
2016-01-01
Full Text Available The paper presents investigations on the water balance of an earth fill built of organic clay in humid climate. As the organic soil used for the fill contains geogenetically elevated concentrations of arsenic, particular attention is paid on the seepage flow through the fill. The test fill is 5 m high, 30 m long and 25 m wide. The fill consists of the organic clay compacted at water contents wet and dry of Proctor Optimum covered by a drainage mat and a 60 cm thick top layer. For the determination of the water balance extensive measuring systems were installed. The seepage at the bottom measured so far was less than 2 % of the precipitation. The interflow in the drainage mat above the compacted organic clay was of similar magnitude. The estimated evapotranspiration reached approx. 84 % of the precipitation. According to these measurements the percolation is much lower than the percolation of many landfill covers in humid climates.
Energy Technology Data Exchange (ETDEWEB)
Bertagnolli, C.; Almeida Neto, A.F. [Universidade Estadual de Campinas (UNICAMP), SP (Brazil). Fac. de Engenharia Quimica. Lab. de Engenharia Ambiental; Silva, M.G.C., E-mail: meuris@feq.unicamp.b [Universidade Estadual de Campinas (UNICAMP), SP (Brazil). Fac. de Engenharia Quimica
2009-07-01
Bentonite clays organically modified have great potential use for environmental remediation, especially in the separation of organic compounds from the water. The aim of this work was the preparation of organophilic clays from 'Verde-Lodo' bentonite clay with the quaternary ammonium salts cetyl-pyridinium chloride and benzalkonium chloride. The materials obtained were characterized by XRD, thermogravimetric analyses, Helium picnometry, SEM and energy dispersive X-ray techniques. The results show consistently successful synthesis of the organoclay through the increase in the basal spacing, as well as salt elimination picks and presence of carbon and chlorine in the modified clays; they are inexistent elements in the natural clay. (author)
Investigation of isothermal water infiltration into fired clay brick by scattered neutrons
International Nuclear Information System (INIS)
El Abd, A.; Abdel-Monem, A.M.; Kansouh, W.A.
2012-01-01
A method based on neutron scattering was proposed to investigate isothermal water infiltration in porous media. Two different kinds of fired clay bricks were investigated. While the sample absorb water, scattered neutrons from the different wetted regions, along the flow direction were continuously recorded. The results were discussed in terms of the theory of water infiltration in unsaturated porous media as well as by an anomalous diffusion approach. It was shown that the infiltration process in the Canadian clay brick (CCB) is Fickian and the water diffusivity was analytically determined, while it is non-Fickian in the Egyptian clay brick (ECB). The infiltration process in ECB can be modeled as a two stage Fickian process, at the low and high absorption times. The anomalous diffusion approach failed to describe the diffusion process in the ECB at all water contents. (author)
Evaluation of natural clay Brasgel as adsorbent in removal of lead in synthetic waste water
International Nuclear Information System (INIS)
Lima, W.S.; Rodrigues, M.G.F.; Mota, M.F.; Patricio, A.C.L.; Silva, M.M.
2012-01-01
The smectite clays have high adsorption capacity and cation exchange. Due to its chemical and physical characteristics, they can be effectively used as adsorbent of pollutants (such as metal ions). The initial objective of this study was to characterize the clay Brasgel through the techniques of X-Ray Diffraction (XRD), X-Ray Spectrometry by Energy Dispersive (EDX) and nitrogen adsorption (BET method), seeking its use in removing lead (Pb 2+ ) from synthetic effluents. System was used in finite bath to assess the potential removal of lead (Pb 2+ ), following a 2 2 factorial experimental design with three center point experiments, taking as input variables: pH and initial concentrations of lead (Pb 2+ ). The clay has Brasgel clay in its composition that characterize it as a smectite clay. By having a large surface area, this clay showed great potential on the adsorption of metal ions. (author)
Directory of Open Access Journals (Sweden)
Vladimir Alvarado
2011-10-01
Full Text Available This research aims at providing evidence of particle suspension contributions to emulsion stability, which has been cited as a contributing factor in crude oil recovery by low-salinity waterflooding. Kaolinite and silica particle dispersions were characterized as functions of brine salinity. A reference aqueous phase, representing reservoir brine, was used and then diluted with distilled water to obtain brines at 10 and 100 times lower Total Dissolved Solid (TDS. Scanning Electron Microscope (SEM and X-ray Diffraction (XRD were used to examine at the morphology and composition of clays. The zeta potential and particle size distribution were also measured. Emulsions were prepared by mixing a crude oil with brine, with and without dispersed particles to investigate emulsion stability. The clay zeta potential as a function of pH was used to investigate the effect of particle charge on emulsion stability. The stability was determined through bottle tests and optical microscopy. Results show that both kaolinite and silica promote emulsion stability. Also, kaolinite, roughly 1 mm in size, stabilizes emulsions better than larger clay particles. Silica particles of larger size (5 µm yielded more stable emulsions than smaller silica particles do. Test results show that clay particles with zero point of charge (ZPC at low pH become less effective at stabilizing emulsions, while silica stabilizes emulsions better at ZPC. These result shed light on emulsion stabilization in low-salinity waterflooding.
International Nuclear Information System (INIS)
Yeh, Jui-Ming; Chang, Kung-Chin; Peng, Chih-Wei; Lai, Mei-Chun; Hung, Chih-Bing; Hsu, Sheng-Chieh; Hwang, Shyh-Shin; Lin, Hong-Ru
2009-01-01
In this study, PMMA/clay nanocomposite (PCN) materials with two kinds of organoclay were prepared via in situ bulk polymerization. The as-prepared PCN materials were then characterized by Fourier transformation infrared (FTIR) spectroscopy, wide-angle X-ray diffraction (WAXRD) and transmission electron microscopy (TEM). WAXRD and TEM analysis revealed that combination of both intercalated and exfoliated nanocomposites was formed and the silicate layers of the clay were uniformly dispersed at a nanometer scale in PMMA matrix. The molecular weights of PMMA extracted from PCN materials and bulk PMMA were determined by gel permeation chromatography (GPC) with THF used as the eluant. The PCN materials were used to produce foams by a batch process in an autoclave using nitrogen as foaming agent. The cellular structure analysis of foams was examined by SEM. The effect of dispersion capability of organoclay on the dielectric and thermal transport properties of PCN materials and foams and mechanical properties of PCN foams were investigated by LCR meter, transient plane source (TPS) technique and dynamic mechanical analysis (DMA), respectively.
Subsurface water and clay mineral formation during the early history of Mars.
Ehlmann, Bethany L; Mustard, John F; Murchie, Scott L; Bibring, Jean-Pierre; Meunier, Alain; Fraeman, Abigail A; Langevin, Yves
2011-11-02
Clay minerals, recently discovered to be widespread in Mars's Noachian terrains, indicate long-duration interaction between water and rock over 3.7 billion years ago. Analysis of how they formed should indicate what environmental conditions prevailed on early Mars. If clays formed near the surface by weathering, as is common on Earth, their presence would indicate past surface conditions warmer and wetter than at present. However, available data instead indicate substantial Martian clay formation by hydrothermal groundwater circulation and a Noachian rock record dominated by evidence of subsurface waters. Cold, arid conditions with only transient surface water may have characterized Mars's surface for over 4 billion years, since the early-Noachian period, and the longest-duration aqueous, potentially habitable environments may have been in the subsurface.
Organically modified clay removes oil from water
International Nuclear Information System (INIS)
Alther, G.R.
1995-01-01
When bentonite or other clays and zeolites are modified with quaternary amines, they become organophilic. Such modified bentonites are used to remove mechanically emulsified oil and grease, and other sparingly soluble organics. If the organoclay is granulated, it is placed into a liquid phase carbon filter vessel to remove FOG's and chlorinated hydrocarbons. In this application the clay is mixed with anthrazite to prevent early plugging of the filter by oil or grease droplets. In batch systems a powered organoclay is employed. Types of oil found in water can include fats, lubricants, cutting fluids, heavy hydrocarbons such as tars, grease, crude oil, diesel oils; and light hydrocarbons such as kerosene, jet fuel, and gasoline
Molecular dynamics of interfacial water and cations associated with clay minerals
International Nuclear Information System (INIS)
Cygan, Randall T.; Greathouse, Jeffery A.; Teich-McGoldrick, Stephanie L.; Nenoff, Tina M.; Daemen, Luke L.
2012-01-01
Document available in extended abstract form only. Clay mineral interfaces, including interlayer and external surfaces, play an essential role in many geochemical processes. Adsorption, dissolution, precipitation, nucleation, and growth mechanisms, in particular, are controlled by the interplay of structure, thermodynamics, kinetics, and transport at clay mineral-water interfaces. Molecular details of these geochemical processes are especially important in evaluating the fate of radionuclide waste in the environment. Such details are typically beyond the sensitivity of experimental and analytical methods and therefore require accurate models and simulations. Also, the basal surfaces and interlayers of clay minerals offer structurally constrained interfacial environments to better evaluate the local molecular chemistry. We have developed and used classical and quantum methods to examine the complex behavior of clay mineral-water interfaces and dynamics of interlayer species. Bulk structures, swelling behavior, diffusion, and adsorption processes are evaluated and compared to experimental and spectroscopic findings. In particular, inelastic neutron scattering methods provide a successful probe of vibrational behavior of interlayer species to help guide the simulations. Librations involving rock, wag, and twist motions of water molecules are particularly sensitive to the interlayer environment of smectite minerals such as montmorillonite and beidellite. Trends in librational modes for interlayer water as a function of clay structure and cation hydration energy are readily explained using structural and vibrational analysis derived from molecular simulation. Molecular dynamics simulations of virtual phases, including hydrated pyrophyllite, help to explain the behavior of interlayer water that is not associated with cation species. Additionally, we use large-scale molecular dynamics simulations of other layered minerals, such as muscovite, to evaluate adsorption
Raman spectroscopy of adsorbed water in clays: first attempt at band assignment
Energy Technology Data Exchange (ETDEWEB)
Ligny, Dominique de; Guillaud, Emmanuel [Institut Lumiere Matiere, CNRS, Universite Lyon 1, 12 rue Ada Byron, 69622 Villeurbanne (France); Gailhanou, Helene; Blanc, Philippe [BRGM, Service D3E, 3 avenue Claude Guillemin, 45000 Orleans (France)
2013-07-01
Raman spectroscopy can be a useful tool to determine water content within clays, or even in highly saturated solutions. The following assignment is proposed for the OH region of SAz-2: the two large bands at 3260 and 3475 cm{sup -1} are assigned to water in pores, the first one to water molecules coordinated to the interlayer cations, and the second one to structural Al-OH groups The band at 3600 cm{sup -1} is therefore more likely related to adsorbed water on the clay surface. Simple intensity ratios of these different bands give good estimates of water content. (authors)
Retention and loss of water extractable carbon in soils: effect of clay properties.
Nguyen, Trung-Ta; Marschner, Petra
2014-02-01
Clay sorption is important for organic carbon (C) sequestration in soils, but little is known about the effect of different clay properties on organic C sorption and release. To investigate the effect of clay content and properties on sorption, desorption and loss of water extractable organic C (WEOC), two experiments were conducted. In experiment 1, a loamy sand alone (native) or mixed with clay isolated from a surface or subsoil (78 and 96% clay) resulting in 90, 158 and 175 g clay kg(-1) soil. These soil treatments were leached with different WEOC concentrations, and then CO2 release was measured for 28 days followed by leaching with reverse osmosis water at the end of experiment. The second experiment was conducted to determine WEOC sorption and desorption of clays isolated from the loamy sand (native), surface soil and subsoil. Addition of clays isolated from surface and subsoil to sandy loam increased WEOC sorption and reduced C leaching and cumulative respiration in percentage of total organic C and WEOC added when expressed per g soil and per g clay. Compared to clays isolated from the surface and subsoil, the native clay had higher concentrations of illite and exchangeable Ca(2+), total organic C and a higher CEC but a lower extractable Fe/Al concentration. This indicates that compared to the clay isolated from the surface and the subsoil, the native clay had fewer potential WEOC binding sites because it had lower Fe/Al content thus lower number of binding sites and the existing binding sites are already occupied native organic matter. The results of this study suggest that in the soils used here, the impact of clay on WEOC sorption and loss is dependent on its indigenous organic carbon and Fe and/or Al concentrations whereas clay mineralogy, CEC, exchangeable Ca(2+) and surface area are less important. © 2013.
International Nuclear Information System (INIS)
Fontanive, A.; Gragnani, R.; Mignuzzi, C.; Spat, G.
1985-01-01
The geochemical characters of clay formations and of their pore water are fundamental with regards to the mobility of the radionuclides as well as to the corrosion processes on enginered barriers. Experimental researches have been carried out in different types of clay, which represent Italian formations, for the characterization of pore water. A squeezer system, which reaches 1500 Kg/cm 2 in pressure, and an analytical micro-scale methodology, for the determination of dissolved constituents in pore water, were set up. The extracted pore water ranges from 60% to 85% in relation to consolidation state of clay. The chemical composition of the extracted fluid has been checked during the squeezing. During this step the observed variations were smaller than those between the different specimens of the same sample. The comparison between the results obtained by squeezing and by a multiple washing technique, using increasing water/sediment ratios, shows that the last one does not give reliable results on the chemical composition of pore water. This is due to the presence of easily weatherable minerals and to the exchange processes between the clayey minerals and the solution. Nevertheless both these techniques have supplied complementary information about geochemical processes in water-rock interaction. The salinity of pore water ranges from 0.45 g/l to 24.5 g/l and the chemism always shows a high content of calcium-magnesium sulfate, or sodium chloride or calcium-magnesium-sulfate with sodium chloride. The correlation between geochemical composition of pore water and mineralogical composition of clay is not significant
Zang, Limin; Qiu, Jianhui; Yang, Chao; Sakai, Eiichi
2016-02-01
In this work, composite nanoparticles containing polypyrrole, silver and attapulgite (PPy/Ag/ATP) were prepared via UV-induced dispersion polymerization of pyrrole using ATP clay as a templet and silver nitrate as photoinitiator. The effects of ATP concentration on morphology, structure and electrical conductivity were studied. The obtained composite nanoparticles with an interesting beads-on-a-string morphology can be obtained in a short time (10 min), which indicates the preparation method is facile and feasible. To explore the potential applications of the prepared PPy/Ag/ATP composite nanoparticles, they were served as multifunctional filler and blended with poly(butylene succinate) (PBS) matrix to prepare biodegradable composite material. The distribution of fillers in polymer matrix and the interfacial interaction between fillers and PBS were confirmed by scanning electron microscope, elemental mapping and dynamic mechanical analysis. The well dispersed fillers in PBS matrix impart outstanding antibacterial property to the biodegradable composite material as well as enhanced storage modulus due to Ag nanoparticles and ATP clay. The biodegradable composite material also possesses modest surface resistivity (106 ~ 109 Ω/◻).
Zang, Limin; Qiu, Jianhui; Yang, Chao; Sakai, Eiichi
2016-02-03
In this work, composite nanoparticles containing polypyrrole, silver and attapulgite (PPy/Ag/ATP) were prepared via UV-induced dispersion polymerization of pyrrole using ATP clay as a templet and silver nitrate as photoinitiator. The effects of ATP concentration on morphology, structure and electrical conductivity were studied. The obtained composite nanoparticles with an interesting beads-on-a-string morphology can be obtained in a short time (10 min), which indicates the preparation method is facile and feasible. To explore the potential applications of the prepared PPy/Ag/ATP composite nanoparticles, they were served as multifunctional filler and blended with poly(butylene succinate) (PBS) matrix to prepare biodegradable composite material. The distribution of fillers in polymer matrix and the interfacial interaction between fillers and PBS were confirmed by scanning electron microscope, elemental mapping and dynamic mechanical analysis. The well dispersed fillers in PBS matrix impart outstanding antibacterial property to the biodegradable composite material as well as enhanced storage modulus due to Ag nanoparticles and ATP clay. The biodegradable composite material also possesses modest surface resistivity (10(6)~ 10(9) Ω/◻).
Quality of clay-powders of industrial assortment
Energy Technology Data Exchange (ETDEWEB)
Lityayeva, Z A; Dzetl, B G; Goncharenko, N N; Naurova, I V; Rybchenko, V I; Voyevodin, L I
1979-01-01
Nomenclature was developed for the quality indicators of clay powders which took into consideration the foreign experience, and it is suggested that a suspension of clay powders be viewed as the simplest type of drilling. In this case the technique of preparing the suspensions approaches the maximum to that used in the recommended standard (TU-39-043-074). The output of solution is determined with standardized effective viscosity /eta/ ef =/sup 20/ /SUP cP/ on a series domestic rotary viscosimeter VSN-3 with gradient of shear velocity EPSILON=666 sec/sup -1/; with EPSILON=1022 sec /sup -1//eta/ /SUB ef/ = 15 cP. This makes it possible to obtain data comparable to the foreign standards regarding the output of the fluid from the powders. According to the suggested technique, the clay powder is dispersed for 20-30 minutes in water or saturated solution of NaC1 in a mixing unit ''Voronezh2'' with rotation frequency of 9000 rpm, is left to rest and is again dispersed for 15 minutes. Then the dynamic shear stress (P /SUB k2/ ), plastic viscosity (/eta/ /SUB ef/ ), coefficients of coagulation (K /SUB c/ ) and thyxotropic (K /SUB T/ ) structure-formation are defined. Measurements are made on the instrument FLR-1 of water output with 0.7 (B) or 0.1 (B) MPa. According to this technique, a comparison was made of the domestic powders of industrial assortment with the powder ''Aquagel'' widely used abroad. It was established that only the modified concrete powders with correct selection of reagents can compete with the foreign.
Oscillatory shear response of moisture barrier coatings containing clay of different shape factor.
Kugge, C; Vanderhoek, N; Bousfield, D W
2011-06-01
Oscillatory shear rheology of barrier coatings based on dispersed styrene-butadiene latex and clay of various shape factors or aspect ratio has been explored. Barrier performance of these coatings when applied to paperboard has been assessed in terms of water vapour transmission rates and the results related to shape factor, dewatering and critical strain. It has been shown that a system based on clay with high shape factor gives a lower critical strain, dewatering and water vapour transmission rate compared with clays of lower shape factor. The dissipated energy, as calculated from an amplitude sweep, indicated no attractive interaction between clay and latex implying a critical strain that appears to be solely dependent on the shape factor at a constant volume fraction. Particle size distribution was shown to have no effect on the critical strain while coatings of high elasticity exhibited high yield strains as expected. The loss modulus demonstrated strain hardening before the elastic to viscous transition. The loss modulus peak was identified by a maximum strain which was significantly lower for a coating based on clay with a high shape factor. The characteristic elastic time was found to vary between 0.6 and 1.3s. The zero shear viscosity of barrier dispersion coatings were estimated from the characteristic elastic time and the characteristic modulus to be of the order of 25-100 Pa s. Copyright © 2011 Elsevier Inc. All rights reserved.
Impact of Oriented Clay Particles on X-Ray Spectroscopy Analysis
Lim, A. J. M. S.; Syazwani, R. N.; Wijeyesekera, D. C.
2016-07-01
Understanding the engineering properties of the mineralogy and microfabic of clayey soils is very complex and thus very difficult for soil characterization. Micromechanics of soils recognize that the micro structure and mineralogy of clay have a significant influence on its engineering behaviour. To achieve a more reliable quantitative evaluation of clay mineralogy, a proper sample preparation technique for quantitative clay mineral analysis is necessary. This paper presents the quantitative evaluation of elemental analysis and chemical characterization of oriented and random oriented clay particles using X-ray spectroscopy. Three different types of clays namely marine clay, bentonite and kaolin clay were studied. The oriented samples were prepared by placing the dispersed clay in water and left to settle on porous ceramic tiles by applying a relatively weak suction through a vacuum pump. Images form a Scanning Electron Microscope (SEM) was also used to show the comparison between the orientation patterns of both the sample preparation techniques. From the quantitative analysis of the X-ray spectroscopy, oriented sampling method showed more accuracy in identifying mineral deposits, because it produced better peak intensity on the spectrum and more mineral content can be identified compared to randomly oriented samples.
On the effect of hot water vapor on MX-80 clay
International Nuclear Information System (INIS)
Pusch, Roland
2000-10-01
Earlier experiments with smectite clay exposed to hot water vapor have indicated that the expandability may be largely lost. If such conditions prevail in a HLW repository the buffer clay may deteriorate and lose its isolating potential. The present study aimed at checking this by hydrothermal treatment at 90 to 110 deg C of rather dense MX-80 clay with subsequent oedometer testing for determining the hydration rate, swelling pressure and hydraulic conductivity, which are all expected to be quite different from those of untreated clay if the expandability is actually reduced. The results show that the swelling pressure of MX-80 clay is not noticeably altered by exposing it to vapor with a temperature of up to 110 deg C for one month while the hydraulic conductivity is increased by about 10% due to some permanent microstructural alteration. The overall change in physical properties of MX-80 clay under the prevailing laboratory conditions is not very significant
On the effect of hot water vapor on MX-80 clay
Energy Technology Data Exchange (ETDEWEB)
Pusch, Roland [Geodevelopment AB, Lund (Sweden)
2000-10-01
Earlier experiments with smectite clay exposed to hot water vapor have indicated that the expandability may be largely lost. If such conditions prevail in a HLW repository the buffer clay may deteriorate and lose its isolating potential. The present study aimed at checking this by hydrothermal treatment at 90 to 110 deg C of rather dense MX-80 clay with subsequent oedometer testing for determining the hydration rate, swelling pressure and hydraulic conductivity, which are all expected to be quite different from those of untreated clay if the expandability is actually reduced. The results show that the swelling pressure of MX-80 clay is not noticeably altered by exposing it to vapor with a temperature of up to 110 deg C for one month while the hydraulic conductivity is increased by about 10% due to some permanent microstructural alteration. The overall change in physical properties of MX-80 clay under the prevailing laboratory conditions is not very significant.
Water-mineral interaction in hygromechanics of clays exposed to environmental loads
International Nuclear Information System (INIS)
Hueckel, T.A.
1992-01-01
Water-mineral interaction in narrow interstices (<3 nm) in dense, saturated clays is discussed in view of recent experimental findings and molecular dynamics simulations. Consequences to the macroscopic behavior are considered. A mixture theory for two interacting constituents is developed. Effects of temperature and chemicals are discussed. A postulate of mass transfer of absorbed water from solid to fluid fraction caused by thermal or chemical load is then discussed. Theory of plasticity of clays affected by heat or chemicals is developed to deal with the effects of thermal and chemical consolidation
Energy Technology Data Exchange (ETDEWEB)
Pearson, F.J., E-mail: fjpearson@gmail.com [Ground-Water Geochemistry, 5108 Trent Woods Dr., New Bern, NC 28562 (United States); Tournassat, Christophe; Gaucher, Eric C. [BRGM, B.P. 36009, 45060 Orleans Cedex 2 (France)
2011-06-15
Highlights: > Equilibrium models of water-rock reactions in clay rocks are reviewed. > Analyses of pore waters of the Opalinus Clay from boreholes in the Mont Terri URL, Switzerland, are tabulated. > Results of modelling with various mineral controls are compared with the analyses. > Best agreement results with calcite, dolomite and siderite or daphnite saturation, Na-K-Ca-Mg exchange and/or kaolinite, illite, quartz and celestite saturation. > This approach allows calculation of the chemistry of pore water in clays too impermeable to yield water samples. - Abstract: The chemistry of pore water (particularly pH and ionic strength) is an important property of clay rocks being considered as host rocks for long-term storage of radioactive waste. Pore waters in clay-rich rocks generally cannot be sampled directly. Instead, their chemistry must be found using laboratory-measured properties of core samples and geochemical modelling. Many such measurements have been made on samples from the Opalinus Clay from the Mont Terri Underground Research Laboratory (URL). Several boreholes in that URL yielded water samples against which pore water models have been calibrated. Following a first synthesis report published in 2003, this paper presents the evolution of the modelling approaches developed within Mont Terri URL scientific programs through the last decade (1997-2009). Models are compared to the composition of waters sampled during dedicated borehole experiments. Reanalysis of the models, parameters and database enabled the principal shortcomings of the previous modelling efforts to be overcome. The inability to model the K concentrations correctly with the measured cation exchange properties was found to be due to the use of an inappropriate selectivity coefficient for Na-K exchange; the inability to reproduce the measured carbonate chemistry and pH of the pore waters using mineral-water reactions alone was corrected by considering clay mineral equilibria. Re
Investigating the pore-water chemistry effects on the volume change behaviour of Boom clay
Deng, Y. F.; Cui, Y. J.; Tang, A. M.; Nguyen, X. P.; Li, X. L.; Van Geet, M.
The Essen site has been chosen as an alternative site for nuclear waste disposal in Belgium. The soil formation involved at this site is the same as at Mol site: Boom clay. However, owing to its geographical situation closer to the sea, Boom clay at Essen presents a pore water salinity 4-5 times higher than Boom clay at Mol. This study aims at studying the effects of pore water salinity on the hydro-mechanical behaviour of Boom clay. Specific oedometer cells were used allowing “flushing” the pore water in soil specimen by synthetic pore water or distilled water. The synthetic pore water used was prepared with the chemistry as that for the site water: 5.037 g/L for core Ess83 and 5.578 g/L for core Ess96. Mechanical loading was then carried out on the soil specimen after flushing. The results show that water salinity effect on the liquid limit is negligible. The saturation or pore water replacement under the in situ effective stress of 2.4 MPa does not induce significant volume change. For Ess83, hydro-mechanical behaviour was found to be slightly influenced by the water salinity; on the contrary, no obvious effect was identified on the hydro-mechanical behaviour of Ess96. This can be attributed to the higher smectite content in Ess83 than in Ess96.
Nafion–clay nanocomposite membranes: Morphology and properties
Herrera Alonso, Rafael; Estevez, Luis; Lian, Huiqin; Kelarakis, Antonios; Giannelis, Emmanuel P.
2009-01-01
A series of Nafion-clay nanocomposite membranes were synthesized and characterized. To minimize any adverse effects on ionic conductivity the clay nanoparticles were H+ exchanged prior to mixing with Nafion. Well-dispersed, mechanically robust, free-standing nanocomposite membranes were prepared by casting from a water suspension at 180 °C under pressure. SAXS profiles reveal a preferential orientation of Nafion aggregates parallel to the membrane surface, or normal plane. This preferred orientation is induced by the platy nature of the clay nanoparticles, which tend to align parallel to the surface of the membrane. The nanocomposite membranes show dramatically reduced methanol permeability, while maintaining high levels of proton conductivity. The hybrid films are much stiffer and can withstand much higher temperatures compared to pure Nafion. The superior thermomechanical, electrochemical and barrier properties of the nanocomposite membranes are of significant interest for direct methanol fuel cell applications. © 2009 Elsevier Ltd. All rights reserved.
Nafion–clay nanocomposite membranes: Morphology and properties
Herrera Alonso, Rafael
2009-05-01
A series of Nafion-clay nanocomposite membranes were synthesized and characterized. To minimize any adverse effects on ionic conductivity the clay nanoparticles were H+ exchanged prior to mixing with Nafion. Well-dispersed, mechanically robust, free-standing nanocomposite membranes were prepared by casting from a water suspension at 180 °C under pressure. SAXS profiles reveal a preferential orientation of Nafion aggregates parallel to the membrane surface, or normal plane. This preferred orientation is induced by the platy nature of the clay nanoparticles, which tend to align parallel to the surface of the membrane. The nanocomposite membranes show dramatically reduced methanol permeability, while maintaining high levels of proton conductivity. The hybrid films are much stiffer and can withstand much higher temperatures compared to pure Nafion. The superior thermomechanical, electrochemical and barrier properties of the nanocomposite membranes are of significant interest for direct methanol fuel cell applications. © 2009 Elsevier Ltd. All rights reserved.
Sorption and desorption of carbamazepine from water by smectite clays.
Zhang, Weihao; Ding, Yunjie; Boyd, Stephen A; Teppen, Brian J; Li, Hui
2010-11-01
Carbamazepine is a prescription anticonvulsant and mood stabilizing pharmaceutical administered to humans. Carbamazepine is persistent in the environment and frequently detected in water systems. In this study, sorption and desorption of carbamazepine from water was measured for smectite clays with the surface negative charges compensated with K+, Ca2+, NH4+, tetramethylammonium (TMA), trimethylphenylammonium (TMPA) and hexadecyltrimethylammonium (HDTMA) cations. The magnitude of sorption followed the order: TMPA-smectite≥HDTMA-smectite>NH4-smectite>K-smectite>Ca-smectite⩾TMA-smectite. The greatest sorption of carbamazepine by TMPA-smectite is attributed to the interaction of conjugate aromatic moiety in carbamazepine with the phenyl ring in TMPA through π-π interaction. Partitioning process is the primary mechanism for carbamazepine uptake by HDTMA-smectite. For NH4-smectite the urea moiety in carbamazepine interacts with exchanged cation NH4+ by H-bonding hence demonstrating relatively higher adsorption. Sorption by K-, Ca- and TMA-smectites from water occurs on aluminosilicate mineral surfaces. These results implicate that carbamazepine sorption by soils occurs primarily in soil organic matter, and soil mineral fractions play a secondary role. Desorption of carbamazepine from the sorbents manifested an apparent hysteresis. Increasing irreversibility of desorption vs. sorption was observed for K-, Ca-, TMA-, TMPA- and HDTMA-clays as aqueous carbamazepine concentrations increased. Desorption hysteresis of carbamazepine from K-, Ca-, NH4-smectites was greater than that from TMPA- and HDTMA-clays, suggesting that the sequestrated carbamazepine molecules in smectite interlayers are more resistant to desorption compared to those sorbed by organic phases in smectite clays. Copyright © 2010 Elsevier Ltd. All rights reserved.
Polyurethane/organo clay nano composite materials via in-situ polymerization
International Nuclear Information System (INIS)
Rehab, A.; Agag, T; Akelah, A.; Shalaby, N.
2005-01-01
Polyurethane/organo clay nano composites have been synthesized via in situ polymerization. The organo clay firstly prepared by intercalation of lyamine or amino lauric acid into montmorillonite-clay (MMT) through ion exchange process. The syntheses of polyurethane/organo clay hybrid films containing different ratio of clay were carried out by swelling the organo clay, into diol and diamine or into different kinds of diols, followed by addition of diisocyanate. The nano composites with dispersed structure of MMT was obtained as evidence by scanning electron microscope and x-ray diffraction. X-ray analysis showed that the d-spacing increased to more than 44A since there is no peaks corresponding to do spacing in organo clay with all the ratios (1, 5, 10, 20%). Also, SEM results confirm the dispersion of nanometer silicate layers in the polyurethane matrix. This indicated that the clay was completely exfoliated and homogeneous dispersion in the polyurethane matrix. Also, it was found that the presence of organo clay leads to improvement the mechanical properties. Since, the tensile strength increased with increasing the organo clay contents to 20% by the ratio 194% in compared to the 1H: with 0% organo clay. Also, the elongation is a decreases with increasing the organo clay contents. The results shown the tensile strength of PU/SMA/ALA-MMT nano composites is high by 6-7 times than the corresponding to PU/Tvr-MMT
Effects of exchangeable Ca:Mg ratio on the dispersion of soils some ...
African Journals Online (AJOL)
The soils studied were acidic, low in nutrient level, showed high dispersion rate, high water- dispersible clay content and the textural class were loamy sand and sandy loam. The exchangeable Ca2+ and Mg2+ contents of the soils dominated the exchange complex. The cation exchange capacity (CEC) ranges between 4 ...
Organically modified clay removes oil from water
International Nuclear Information System (INIS)
Alther, G.R.
1995-01-01
When bentonite or other clays and zeolite are modified with quaternary amines, they become organophilic. Such modified bentonites are used to remove mechanically emulsified oil and grease, and other sparingly soluble organics. Types of oil found in water can include fats, lubricants, cutting fluids, heavy hydrocarbons such as tars, grease, crude oil, diesel oils; and light hydrocarbons such as kerosene, jet fuel, and gasoline. If the organoclay is granulated, it is placed into a liquid phase carbon filter vessel to remove FOGs (Free Oil and Grease) and chlorinated hydrocarbons. In this application the clay is mixed with anthrazite to prevent early plugging of the filter by oil or grease droplets. In batch systems a powdered organoclay is employed. Organoclay removes mechanically emulsified oil and grease at 5--7 times the rate of activated carbon, or 50% of its dry weight. Oil and grease and other large sparingly soluble chlorinated hydrocarbons and NOMs (Natural Organic Matter) blind the pores of activated carbon (and ion-exchange resins), reducing its effectiveness significantly. It is therefore economically advantageous for the end user to prepolish the water before it enters carbon vessels. Operating costs can often be reduced by 50% or more
Directory of Open Access Journals (Sweden)
M. Colonna
2017-05-01
Full Text Available Nanocomposites of bisphenol A polycarbonate with organically modified clays have been prepared for the first time by in-situ polymerization using bis(methyl salicyl carbonate as activated carbonate. The use of the activated carbonate permits to conduct the polymerization reaction at lower temperature and with shorter polymerization time with respect to those necessary for traditional melt methods that uses diphenyl carbonate, affording a nanocomposite with improved color. Moreover, an imidazolium salt with two long alkyl chains has been used to modify the montmorillonite, providing an organically modified clay with high thermal stability and wide d-spacing. The addition of ionic groups at the end of the polymer chain increases the interaction between the clay surface and the polymer producing a better dispersion of the clay. The presence of the clay increases the thermal stability of the polymer.
International Nuclear Information System (INIS)
Fedodeev, V.I.
1975-01-01
A microviscosity model of proton relaxation in pure liquids and in solutions of paramagnetic ions is examined. It is shown that the influence of adsorbed paramagnetic centers on proton relaxation in finely dispersed substances is significantly weaker than in solutions. A 'two-phase' relaxation model is used in determining the parameters of the bound liquid (water) using nuclear magnetic resonance data. The relations obtained with the model are used to compute the viscosity of water in clay. The value is of the same order of magnitude as that obtained by other methods
Energy Technology Data Exchange (ETDEWEB)
Fedodeev, V I
1975-09-01
A microviscosity model of proton relaxation in pure liquids and in solutions of paramagnetic ions is examined. It is shown that the influence of adsorbed paramagnetic centers on proton relaxation in finely dispersed substances is significantly weaker than in solutions. A 'two-phase' relaxation model is used in determining the parameters of the bound liquid (water) using nuclear magnetic resonance data. The relations obtained with the model are used to compute the viscosity of water in clay. The value is of the same order of magnitude as that obtained by other methods.
Method for preventing plugging of water wells by clay
Energy Technology Data Exchange (ETDEWEB)
Blazhkov, V I
1966-01-01
A method is suggested for preventing the plugging of water-bearing sands by clay from drilling fluids. It consists in placing a cement plug in the upper nipple above the filter, in order to prevent its plugging during the installation. The drilling mud passes through the rinsing windows and fills the internal void of the filter column, thus preventing further percolation and plugging of the filter during its lowering. When a 2-filter column is lowered, the clay solution is pumped into the interval between the cement plug and the next filter; this is done gradually in proportion to the addition of new pipes. When the drilling mud level lowers in the annular space between the pipes, the mud cake, together with water-saturated sand, passes through the rinsing windows into the pipes and is removed to the surface by airlift or other methods. This procedure is described in detail, discussed for various conditions of well structure, and illustrated by schematic drawings. Its advantage is in the possibility of separate testing and production of all water-bearing zones in the well, and it does not require the use of pure water for well washing.
Multi-scale modeling of the behaviour of water and ions clays
International Nuclear Information System (INIS)
Rotenberg, B.
2007-10-01
Predicting the fate of radioactive waste stored in a clay formation requires a good understanding of the transport properties of water and ions in clays. Their diffusion in this charged porous medium is described by empirical parameters such as their partitioning coefficient Kd which accounts for the interactions with the mineral surfaces. The present work deals with the relevance of this concept and its definition based on microscopic grounds. We have first modeled the ionic contribution to the dielectric properties of clays and suggested an experimental determination of Kd from dielectric spectroscopy measurements. Using microscopic simulations (Monte-Carlo and Molecular Dynamics), we then have computed the Gibbs free energy and enthalpy for ionic exchange in the case of alkaline cations. They control the value of Kd and its evolution with the temperature. The results for cesium are in good agreement with both microcalorimetric measurements and the determination of Kd at different temperatures. We have participated in the development of a new lattice simulation method (Lattice Fokker-Planck), which we have then used to link explicitly the microscopic dynamics of ions to the diffusion-reaction model underlying the definition of Kd. Finally, we have used Molecular Dynamics to investigate the kinetics of exchange of water and ions between clay particles (interlayer) and the extra-particle porosity. The results confirm the generally admitted idea that water and ions can explore the whole porosity, whereas anions are excluded from the interlayers. (author)
Pharmaceutical grade phyllosilicate dispersions: the influence of shear history on floc structure.
Viseras, C; Meeten, G H; Lopez-Galindo, A
1999-05-10
The effect of mixing conditions on the flow curves of some clay-water dispersions was studied. Two Spanish fibrous phyllosilicates (sepiolite from Vicálvaro and palygorskite from Turón) and a commercial bentonite (Bentopharm Copyright, UK) were selected as model clays. The disperse systems were made up using a rotor-stator mixer working at two different mixing rates (1000 and 8000 rpm), for periods of 1 and 10 min. Rheological measurements were taken and the corresponding flow curves obtained immediately after interposition and then after a period of 24 h under low shear caused by a roller apparatus. Aqueous sepiolite dispersions showed the highest viscosity and were easily interposed, whereas palygorskite dispersions were more difficult to obtain, resulting in low to medium viscosity gels. Bentonite dispersions provided medium viscosity systems, which greatly increased their viscosity after the low shear treatment (as a result of swelling), whereas the viscosity of the fibrous clays stayed at approximately the same values or even decreased. A linear relation was found between mixing energy and apparent viscosity in the bentonite systems, while apparent viscosity in the sepiolite samples was related to mixing power, with minor influence of mixing times. All the systems studied had thixotropic behaviour, changing from clearly positive to even negative thixotropy in some palygorskite systems. Finally, we studied the effect of drastic pH changes on the system structure. Results showed that rheological properties were highly sensitive to pH in the fibrous dispersions, but less sensitive behaviour was found in the laminar clay systems. Copyright.
Kasmerchak, C. S.; Mason, J. A.
2016-12-01
Along the prairie-forest ecotone, Alfisols with distinct clay-enriched B horizons are found under forest, established only within the past 4 ka, including outlying patches of prairie groves surrounded by prairie. Grassland soils only 5-10 km away from the vegetation boundary show much weaker texture-contrast. In order for clay to be dispersed it must first be released from aggregates upper horizons, which occurs when exposed top soil undergoes wetting and mechanical stress. The relationship between physiochemical soil characteristics and soil aggregation/clay dispersion is of particular interest in explaining texture-contrast development under forest. Soil samples were collected along a transect in northern Minnesota on gentle slopes in similar glacial sediment. Aggregate stability experiments show Mollisol A and B horizons have the most stable aggregates, while Alfisol E horizons have the weakest aggregates and disintegrate rapidly. This demonstrates the strong influence of OM and exchange chemistry on aggregation. Analysis of other physiochemical soil characteristics such as base saturation and pH follow a gradual decreasing eastward trend across the study sites, and do not abruptly change at the prairie-forest boundary like soil morphology does. Linear models show the strongest relationship between rapid aggregate disintegration and ECEC, although they only explain 47-50% of the variance. Higher surface charge enhances aggregation by allowing for greater potential of cation bridging between OM and clay particles. ECEC also represents multiple soil characteristics such as OC, clay, mineralogy, and carbonate presence, suggesting the relationship between aggregation stability and soil characteristics is not simple. Given the parent material consists of calcareous glacial sediment, abundant Ca2+ and Mg2+ from carbonates weathering also contributes to enhanced aggregation in upper horizons. Differences in the rates of bioturbation, most likely also contribute
Clay facial masks: physicochemical stability at different storage temperatures.
Zague, Vivian; de Almeida Silva, Diego; Baby, André Rolim; Kaneko, Telma Mary; Velasco, Maria Valéria Robles
2007-01-01
Clay facial masks--formulations that contain a high percentage of solids dispersed in a liquid vehicle--have become of special interest due to specific properties presented by clays, such as particle size, cooling index, high adsorption capacity, and plasticity. Although most of the physicochemical properties of clay dispersions have been studied, specific aspects concerning the physicochemical stability of clay mask products remain unclear. This work aimed at investigating the accelerated physicochemical stability of clay mask formulations stored at different temperatures. Formulations were subjected to centrifuge testing and to thermal treatment for 15 days, during which temperature was varied from -5.0 degrees to 45.0 degrees C. The apparent viscosity and visual aspect (homogeneity) of all formulations were affected by temperature variation, whereas color, odor, and pH value remained unaltered. These results, besides the estimation of physicochemical stability under aging, can be useful in determining the best storage conditions for clay-based formulations.
Pore-water chemistry effects on the compressibility behaviour of Boom Clay
International Nuclear Information System (INIS)
Deng, Y.F.; Cui, Y.J.; Tang, A.M.; Nguyen, X.P.; Li, X.L.; Maarten, V.G.
2010-01-01
Document available in extended abstract form only. Boom clay is a thick deposit of over-consolidated marine clay, and belongs to the Oligocene series. Its hydraulic conductivity has been investigated since many years in Belgium within the site characterization program related to the performance assessment of potential geological disposal of high-level radioactive waste in this formation. Recently, the work of Wemaere et al. (2008) shows a significant variability of the hydraulic conductivity of the Boom clay. Indeed, they performed measurements on soil cores taken from four distant boreholes at various depths. The vertical hydraulic conductivity was found to vary from 3 x 10 -12 to 10 x 10 -12 m/s. It is suspected that this variability would be partly related to the water chemistry effects. Indeed, De Craen et al. (2006) shows that the pore-water chemical composition of soil cores taken from the Essen site is significantly different from that at the Mol site. If the pore water chemistry has strong effect on the hydraulic conductivity, its effect on the mechanical behaviour needs to be investigated too. The aim of this paper is to verify whether there are significant effects of pore-water chemistry on the soil compressibility. This study would be helpful to transpose the knowledge obtained from the Mol site to other sites of Boom clay formation where the geochemical components are different from the former site, as the hydro-mechanical characteristics of Boom clay at the Mol site has been widely investigated since the last decades. Two soil cores were taken from the Essen site at a depth of 227 m (Ess83) and 240 m (Ess96). Based on the geochemical analysis presented by De Craen et al. (2006), synthetic water having similar chemical composition of the in-situ pore-water was prepared. The identification geotechnical characteristics of these cores are shown in Table 2. It can be observed that the clay content (particle size < 2 μm) is relatively high (more than 50
Fracture behavior of polypropylene/clay nanocomposites.
Chen, Ling; Wang, Ke; Kotaki, Masaya; Hu, Charmaine; He, Chaobin
2006-12-01
Polypropylene (PP)/clay nanocomposites have been prepared via a reactive compounding approach with an epoxy based masterbatch. Compared with PP and common PP/organoclay nanocomposites, the PP/clay nanocomposites based on epoxy/clay masterbatch have higher impact strength. The phenomenon can be attributed to the epoxy phase dispersed uniformly in the PP matrix, which may act as impact energy absorber and helps to form a large damage zone, thus a higher impact strength value is achieved.
Energy Technology Data Exchange (ETDEWEB)
Campos, L.F.A.; Ferreira, H.S.; Amorim, L.V.; Franca, K.B.; Ferreira, H.C. [Universidade Federal de Campina Grande (UFCG), PB (Brazil)
2008-07-01
The aim of this paper is study influences of electrolytes and cellulose polymers on rheological and water loss properties of dispersions of bentonite compositions. Evaluate the action of degradation additives CaSO{sub 4}, MgCl{sub 2} and CaCl{sub 2} and polymeric additives to protect and recover water and clay based. The results show a negative effect of degradation additives the rheological and water loss properties of drilling fluids. The cellulose polymers can be successfully applied to protect and recover of the rheological properties and water loss of the dispersions contaminated. (author)
Determination of membrane behaviour during transport of pollutants n clay barriers
International Nuclear Information System (INIS)
Musso, M.; Pejon, O.
2010-01-01
The study of the transport of contaminants in clay barriers had a extensive development in environmental geotechnics. The most studied transport processes are solutes by advection - dispersion and diffusion generated by hydraulic and chemical gradients respectively. Greater attention should be given to the chemical - osmotic flow and behavior membrane clay barriers, since in one case the water molecules move through the existence of a chemical gradient and on the other the means totally or partially inhibits the passage of solutes. The team developed to measure these processes was constructed based on items international literature and performance was verified using two types of materials KCl solution . One material is a bentonite geocomposite (Geosynthetic Clay Liner GCL ) similar to that used by other researchers. The other material is a soil barrier compacted clay (Compacted Clay Liner CCL) Fm. Corumbataí (Permian), belonging to the Paraná basin in the state of Sao Paulo, Brazil . The results show the proper performance of the equipment built . Osmotic pressure generation and membrane performance was verified for both samples. Further corroborated influence of the type of clay mineral in the osmotic pressure generated value and membrane behavior
Directory of Open Access Journals (Sweden)
Marwa Akkari
2016-12-01
Full Text Available In this study, ZnO/SiO2-clay heterostructures were successfully synthesized by a facile two-step process applied to two types of clays: montmorillonite layered silicate and sepiolite microfibrous clay mineral. In the first step, intermediate silica–organoclay hybrid heterostructures were prepared following a colloidal route based on the controlled hydrolysis of tetramethoxysilane in the presence of the starting organoclay. Later on, pre-formed ZnO nanoparticles (NP dispersed in 2-propanol were incorporated under ultrasound irradiation to the silica–organoclay hybrid heterostructures dispersed in 2-propanol, and finally, the resulting solids were calcinated to eliminate the organic matter and to produce ZnO nanoparticles (NP homogeneously assembled to the clay–SiO2 framework. In the case of montmorillonite the resulting materials were identified as delaminated clays of ZnO/SiO2-clay composition, whereas for sepiolite, the resulting heterostructure is constituted by the assembling of ZnO NP to the sepiolite–silica substrate only affecting the external surface of the clay. The structural and morphological features of the prepared heterostructures were characterized by diverse physico-chemical techniques (such as XRD, FTIR, TEM, FE-SEM. The efficiency of these new porous ZnO/SiO2-clay heterostructures as potential photocatalysts in the degradation of organic dyes and the removal of pharmaceutical drugs in water solution was tested using methylene blue and ibuprofen compounds, respectively, as model of pollutants.
Study of the Effect of Clay Particles on Low Salinity Water Injection in Sandstone Reservoirs
Directory of Open Access Journals (Sweden)
Sina Rezaei Gomari
2017-03-01
Full Text Available The need for optimal recovery of crude oil from sandstone and carbonate reservoirs around the world has never been greater for the petroleum industry. Water-flooding has been applied to the supplement primary depletion process or as a separate secondary recovery method. Low salinity water injection is a relatively new method that involves injecting low salinity brines at high pressure similar to conventional water-flooding techniques, in order to recover crude oil. The effectiveness of low salinity water injection in sandstone reservoirs depends on a number of parameters such as reservoir temperature, pressure, type of clay particle and salinity of injected brine. Clay particles present on reservoir rock surfaces adsorb polar components of oil and modify wettability of sandstone rocks to the oil-wet state, which is accountable for the reduced recovery rates by conventional water-flooding. The extent of wettability alteration caused by three low salinity brines on oil-wet sandstone samples containing varying clay content (15% or 30% and type of clay (kaolinite/montmorillonite were analyzed in the laboratory experiment. Contact angles of mica powder and clay mixture (kaolinite/montmorillonite modified with crude oil were measured before and after injection with three low salinity sodium chloride brines. The effect of temperature was also analyzed for each sample. The results of the experiment indicate that samples with kaolinite clay tend to produce higher contact angles than samples with montmorillonite clay when modified with crude oil. The highest degree or extent of wettability alteration from oil-wet to intermediate-wet state upon injection with low salinity brines was observed for samples injected with brine having salinity concentration of 2000 ppm. The increase in temperature tends to produce contact angles values lying in the higher end of the intermediate-wet range (75°–115° for samples treated at 50 °C, while their corresponding
Water storage change estimation from in situ shrinkage measurements of clay soils
Brake, te B.; Ploeg, van der M.J.; Rooij, de G.H.
2012-01-01
Water storage in the unsaturated zone is a major determinant of the hydrological behaviour of the soil, but methods to quantify soil water storage are limited. The objective of this study is to assess the applicability of clay soil surface elevation change measurements to estimate soil water storage
Geochemical of clay formations : study of Spanish clay REFERENCE
International Nuclear Information System (INIS)
Turrero, M. J.; Pena, J.
2003-01-01
Clay rocks are investigated in different international research programs in order to assess its feasibility for the disposal of high level radioactive wastes. This is because different sepcific aspects: they have low hydraulic conductivity (10''-11-10''-15 m/s), a high sorption capacity, self-sealing capacity of facults and discontinuities and mechanical resistance. Several research programs on clay formations are aimed to study the chemistry of the groundwater and the water-rock reactions that control it: e. g. Boom Clay (Mol, Belgium), Oxford Clay /Harwell, United Kingdom), Toarcian Clay (Tournemire, France), Palfris formation (Wellenberg, Switzerland), Opalinus Clay (Bure, France). Based on these studies, considerable progress in the development of techniques for hydrologic, geochemical and hydrogeochemical characterization of mudstones has been accomplished (e. g. Beaufais et al. 1994, De Windt el al. 1998. Thury and Bossart 1999, Sacchi and Michelot 2000) with important advances in the knowledge of geochemical process in these materials (e. g. Reeder et al. 1993, Baeyens and Brandbury 1994, Beaucaire et al. 2000, Pearson et al., 2003).Furtermore, geochemical modeling is commonly used to simulate the evolution of water chemistry and to understand quantitatively the processes controlling the groundwater chemistry (e. g. Pearson et al. 1998, Tempel and Harrison 2000, Arcos et al., 2001). The work presented here is part of a research program funded by Enresa in the context of its R and D program. It is focused on the characterization of a clay formation (reference Argillaceous Formation, RAF) located within the Duero Basin (north-centralSpain). The characterisation of th ephysical properties,, fluid composition, mineralogy, water-rock reaction processes, geochemical modelling and sorption properties of the clays from the mentioned wells is the main purpose of this work. (Author)
Mainil, Michaël; Alexandre, Michaël; Monteverde, Fabien; Dubois, Philippe
2006-02-01
High density polyethylene (HDPE)/clay nanocomposites have been prepared using three different functionalized polyethylene compatibilizers: an ethylene/vinyl acetate copolymer, a polyethylene grafted with maleic anhydride functions and a (styrene-b-ethylene/butylene-b-styrene) block copolymer. The nanocomposites were prepared via two different routes: (1) the dispersion in HDPE of a masterbatch prepared from the compatibilizer and the clay or (2) the direct melt blending of the three components. For each compatibilizer, essentially intercalated nanocomposites were formed as determined by X-ray diffraction and transmission electron microscopy. With the ethylene/vinyl acetate copolymer, a significant delamination of the intercalated clay in thin stacks was observed. This dispersion of thin intercalated stacks within the polymer matrix allowed increasing significantly the stiffness and the flame resistance of the nanocomposite. A positive effect of shear rate and blending time has also been put into evidence, especially for the process based on the masterbatch preparation, improving both the formation of thin stacks of intercalated clay and the mechanical properties and the flame resistance of the formed nanocomposites.
Energy Technology Data Exchange (ETDEWEB)
Hussain, Syed Arshad, E-mail: sa_h153@hotmail.com [Department of Physics, Tripura University, Suryamaninagar-799022 (India); Chakraborty, S.; Bhattacharjee, D. [Department of Physics, Tripura University, Suryamaninagar-799022 (India); Schoonheydt, R.A. [Centres for Surface Chemistry and Catalysis, K.U. Leuven, Kasteelpark Arenberg 23, 3001 Leuven (Belgium)
2013-06-01
In general cationic amphiphiles are used to prepare organo-clay hybrid film in Langmuir–Blodgett (LB) technique. In this present communication we demonstrated a unique technique to prepare the organo–clay hybrid films using an anionic amphiphile. The T–O–T type clay saponite was incorporated onto a floating stearic acid monolayer via a divalent cation Mg{sup 2+}. Salt MgCl{sub 2} was mixed along with the clay dispersion in the LB trough and amphiphile solution was spread onto the subphase in order to make the organo-clay hybrid films. It was observed that salt (MgCl{sub 2}) concentration on the subphase affects the organization of nano-dimensional clay platelet (saponite) in organo-clay hybrid films at air–water interface as well as in LB films. Noticeable changes in area per molecule and shape of the isotherms were observed and measured at subphases with different salt concentrations. Infrared reflection absorption spectroscopy studies reveal that only an in-plane (996 cm{sup −1}) vibration of ν (Si-O) band occurred when the salt concentration was 10 mM. However, both in-plane (996 cm{sup −1}) and out-of-plane (1063 cm{sup −1}) vibrations of the ν (Si-O) band of saponite occurred when the subphase salt concentration was 100 mM. Also the out-of-plane vibration of ν (OH) of saponite was prominent at higher salt concentration. This is because at lower salt concentration clay sheets remain flat on the surface whereas; at higher MgCl{sub 2} concentration they aggregated and form stacks of saponite layers. Also they may be slightly tilted with a very small tilt angle at higher salt concentration making a favorable condition for both in-plane and out-of-plane vibrations of ν (Si-O) in the hybrid films. Observed decrease in starting area per molecule in the pressure area isotherm measured at higher salt concentration also supports the tilting of clay layers at air–clay dispersion interface. Attentuated total reflectance Fourier transform infrared
Directory of Open Access Journals (Sweden)
E. Cortes-Trivino
2018-07-01
Full Text Available The addition of inorganic fillers into a bioplastic could increase its mechanical properties, which will be influenced strongly by the type of the clay dispersion. In this work, we have used montmorillonite nanoclays (MMT to prepare biocomposites by means of an extrusion process. We present herein the effect of the pH and the addition of montmorillonite nanoclays (MMT on the barrier and mechanical properties of wheat gluten based bioplastics. The pH of the samples was modified by adding aqueous solution of a strong acid or base (H2SO4 and NaOH. Tensile, dynamic mechanical thermal analysis (DMTA, water absorption and X-ray tests were carried out to study the influence of the above-mentioned variables on the physicochemical properties and rheological behaviour of bioplastics and biocomposites obtained. Tensile results showed that both Young’s modulus and tensile strength are higher at unmodified pH. However, the addition of MMT to an alkaline biopolymer matrix produced remarkable improvements in the rheological and mechanical properties because of a high exfoliation of the nanoclay noticeable in X-ray results. To summarise, extrusion process and the use of nanoclays present an excellent opportunity to develop wheat gluten bioplastics able to replace conventional products.
Probing Interfacial Water on Nanodiamonds in Colloidal Dispersion.
Petit, Tristan; Yuzawa, Hayato; Nagasaka, Masanari; Yamanoi, Ryoko; Osawa, Eiji; Kosugi, Nobuhiro; Aziz, Emad F
2015-08-06
The structure of interfacial water layers around nanoparticles dispersed in an aqueous environment may have a significant impact on their reactivity and on their interaction with biological species. Using transmission soft X-ray absorption spectroscopy in liquid, we demonstrate that the unoccupied electronic states of oxygen atoms from water molecules in aqueous colloidal dispersions of nanodiamonds have a different signature than bulk water. X-ray absorption spectroscopy can thus probe interfacial water molecules in colloidal dispersions. The impacts of nanodiamond surface chemistry and concentration on interfacial water electronic signature are discussed.
Valence holes observed in nanodiamonds dispersed in water
Petit, Tristan; Pflüger, Mika; Tolksdorf, Daniel; Xiao, Jie; Aziz, Emad F.
2015-02-01
Colloidal dispersion is essential for most nanodiamond applications, but its influence on nanodiamond electronic properties remains unknown. Here we have probed the electronic structure of oxidized detonation nanodiamonds dispersed in water by using soft X-ray absorption and emission spectroscopies at the carbon and oxygen K edges. Upon dispersion in water, the π* transitions from sp2-hybridized carbon disappear, and holes in the valence band are observed.Colloidal dispersion is essential for most nanodiamond applications, but its influence on nanodiamond electronic properties remains unknown. Here we have probed the electronic structure of oxidized detonation nanodiamonds dispersed in water by using soft X-ray absorption and emission spectroscopies at the carbon and oxygen K edges. Upon dispersion in water, the π* transitions from sp2-hybridized carbon disappear, and holes in the valence band are observed. Electronic supplementary information (ESI) available: Experimental methods, details on XAS/XES normalization and background correction procedures. See DOI: 10.1039/c4nr06639a
Hou, Chang-Yu; Feng, Ling; Seleznev, Nikita; Freed, Denise E
2018-04-11
In this work, we establish an effective medium model to describe the low-frequency complex dielectric (conductivity) dispersion of dilute clay suspensions. We use previously obtained low-frequency polarization coefficients for a charged oblate spheroidal particle immersed in an electrolyte as the building block for the Maxwell Garnett mixing formula to model the dilute clay suspension. The complex conductivity phase dispersion exhibits a near-resonance peak when the clay grains have a narrow size distribution. The peak frequency is associated with the size distribution as well as the shape of clay grains and is often referred to as the characteristic frequency. In contrast, if the size of the clay grains has a broad distribution, the phase peak is broadened and can disappear into the background of the canonical phase response of the brine. To benchmark our model, the low-frequency dispersion of the complex conductivity of dilute clay suspensions is measured using a four-point impedance measurement, which can be reliably calibrated in the frequency range between 0.1 Hz and 10 kHz. By using a minimal number of fitting parameters when reliable information is available as input for the model and carefully examining the issue of potential over-fitting, we found that our model can be used to fit the measured dispersion of the complex conductivity with reasonable parameters. The good match between the modeled and experimental complex conductivity dispersion allows us to argue that our simplified model captures the essential physics for describing the low-frequency dispersion of the complex conductivity of dilute clay suspensions. Copyright © 2018 Elsevier Inc. All rights reserved.
CSIR Research Space (South Africa)
Bandyopadhyay, J
2012-04-01
Full Text Available To understand the change in dispersion and orientation of clay platelets in three-dimensional space during tensile test, neat polymer and its nanocomposite samples were studied by small- and wide-angle X-ray scattering (SWAXS). The samples after...
Adsorption of Dissolved Gases (CH4, CO2, H2, Noble Gases) by Water-Saturated Smectite Clay Minerals
Bourg, I. C.; Gadikota, G.; Dazas, B.
2016-12-01
Adsorption of dissolved gases by water-saturated clay minerals plays important roles in a range of fields. For example, gas adsorption in on clay minerals may significantly impact the formation of CH4 hydrates in fine-grained sediments, the behavior of CH4 in shale, CO2 leakage across caprocks of geologic CO2 sequestration sites, H2 leakage across engineered clay barriers of high-level radioactive waste repositories, and noble gas geochemistry reconstructions of hydrocarbon migration in the subsurface. Despite its importance, the adsorption of gases on clay minerals remains poorly understood. For example, some studies have suggested that clay surfaces promote the formation of CH4 hydrates, whereas others indicate that clay surfaces inhibit the formation of CH4 hydrates. Here, we present molecular dynamics (MD) simulations of the adsorption of a range of gases (CH4, CO2, H2, noble gases) on clay mineral surfaces. Our results indicate that the affinity of dissolved gases for clay mineral surfaces has a non-monotone dependence on the hydrated radius of the gas molecules. This non-monotone dependence arises from a combination of two effects: the polar nature of certain gas molecules (in particular, CO2) and the templating of interfacial water structure by the clay basal surface, which results in the presence of interfacial water "cages" of optimal size for intermediate-size gas molecules (such as Ne or Ar).
International Nuclear Information System (INIS)
Guillaud, Emmanuel Bertrand
2017-01-01
Clay are complex minerals with a multi-scale porosity and a remarkable ability to swell under humid atmosphere. These materials have many applications in catalysis, waste management, construction industry... However, the properties of confined water are still not fully understood, due in particular to the complexity of water itself. The aim of this work is, using mainly molecular simulations and vibrational spectroscopy, to understand the structure and the dynamics of water confined in clay minerals. To evaluate the accuracy of numerical models to describe water confined in clay minerals, and to understand the origin of its structural and dynamical properties, a large part of the work was devoted to the building blocks of clays: pure bulk water, water at the surface of a solid, and salt water. To this extent, the viscoelastic properties of water from the deeply supercooled regime to the boiling temperature were investigated using classical molecular dynamics. The evolution of the friction properties of water on a prototypical solid surface was also analyzed, and the accuracy of ab initio approaches and empirical salt models was studied. In a second part, those results were confronted to the properties of water confined in clay minerals at low and room temperature, studied both experimentally and numerically. Experimental work consisted mostly in extensive far- and -mid infrared absorption spectrometry measurements, whereas numerical work mainly consisted in empirical molecular dynamics simulations. Especially, the existence of confinement- or temperature-induced phase transitions of confined water was investigated. (author)
Landrou, Gnanli; Brumaud, Coralie; Habert, Guillaume
2017-06-01
In the ceramic industry and in many sectors, clay minerals are widely used. In earthen construction technique, clay plays a crucial role in the processing. The purpose of this research is to understand and modify the clay properties in earth material to propose an innovative strategy to develop a castable earth-based material. To do so, we focused on the modification of clay properties at fresh state with inorganic additives. As the rheological behaviour of clays is controlled by their surface charge, the addition of phosphate anion allows discussing deep the rheology of concentrated clay suspensions. We highlighted the thixotropic and shear thickening behaviour of a dispersed kaolinite clay suspensions. Indeed, by adding sodium hexametaphosphate the workability of clay paste increases and the behaviour is stable during time after a certain shear is applied. Moreover, we stress that the aging and the shift in critical strain in clay system are due to the re-arrangement of clay suspension and a decrease of deformation during time. The understanding of both effect: thixotropy and aging are crucial for better processing of clay-based material and for self-compacting clay concrete. Yet, studies need to pursue to better understand the mechanism.
Bumanis, G.; Bajare, D.; Dembovska, L.
2015-11-01
Alkali activation technology can be applied for a wide range of alumo-silicates to produce innovative materials with various areas of application. Most researches focuse on the application of alumo-silicate materials in building industry as cement binder replacement to produce mortar and concrete [1]. However, alkali activation technology offers high potential also in biotechnologies [2]. In the processes where certain pH level, especially alkaline environment, must be ensured, alkali activated materials can be applied. One of such fields is water treatment systems where high level pH (up to pH 10.5) ensures efficient removal of water pollutants such as manganese [3]. Previous investigations had shown that alkali activation technology can be applied to calcined clay powder and aluminium scrap recycling waste as a foam forming agent to create porous alkali activated materials. This investigation focuses on the structural investigation of calcined kaolin and illite clay alkali activation processes. Chemical and mineralogical composition of both clays were determined and structural investigation of alkali activated materials was made by using XRD, DTA, FTIR analysis; the microstructure of hardened specimens was observed by SEM. Physical properties of the obtained material were determined. Investigation indicates the essential role of chemical composition of the clay used in the alkali activation process, and potential use of the obtained material in water treatment systems.
International Nuclear Information System (INIS)
1993-01-01
This report describes a large scale laboratory investigation into the movements of gas and water through clay barriers exposed to the environment. The test beds, each 3m square were constructed and filled with clay to a depth of 400 mm, after compaction. One test bed contained London Clay, the other Glacial Till. The clays were subjected to accelerated environmental cycling and tests carried out on samples of the clays at appropriate intervals. The tests included measurements of the mechanical, physical and chemical properties of the clays and their permeability to gas and water. Gas permeability emerged as the more appropriate for the clays being investigated. The report discusses the difficulties of measuring the permeability of partially saturated clays and the need to define the measuring techniques when specifying limiting acceptability values. 55 refs., 8 figs., 7 tabs., 27 plates
Osmotic pressure in Ca/Na montmorillonite dispersions: Monte Carlo simulations
International Nuclear Information System (INIS)
Joensson, Bo; Aakesson, T.; Segad, M.; Cabane, B.
2010-01-01
Document available in extended abstract form only. In the past, clay-water systems have been extensively studied. due to its importance in agricultural as well as technological applications. A more recent use of clay is as sealing material for nuclear waste. The success for such a containment depends on the clay structure and its swelling properties. This means that the clay should be able to sustain considerable changes in the surrounding ground water including salinities of glacial melt water as well as sea water, while still being an effective hydraulic barrier. We have approached this problem using statistical mechanical simulation techniques. The osmotic pressure in Ca/Na montmorillonite dispersions has been calculated via Monte Carlo simulations. For a clay system in equilibrium with pure water, Monte Carlo simulations predict a large swelling when the clay counterions are monovalent, while in presence of divalent counterions a limited swelling is predicted with an aqueous layer between the clay lamellae of about 1 nm - in excellent agreement with SAXS data. Montmorillonite in contact with a salt reservoir with e.g. both Na and Ca counterions will only show a modest swelling unless the Na + concentration in the bulk is several orders of magnitude larger than the Ca 2+ concentration. This is true both for a clay repository surrounded by ground water as well as sea water of high salinity. The limited swelling of clay in presence of divalent counterions is a consequence of ion-ion correlations, which both reduce the entropic repulsion and give rise to an attractive component in the total osmotic pressure. Ion-ion correlations also favour divalent counterions when competing with monovalent ones. This is an important aspect for the retention of radioactive charged species. A more fundamental result of ion-ion correlations is that the osmotic pressure as a function of clay sheet separation becomes non-monotonic - which indicates the possibility of a phase
Mineral acquisition from clay by budongo forest chimpanzees
Reynolds, Vernon; Lloyd, Andrew W.; English, Christopher J.; Lyons, Peter; Dodd, Howard; Hobaiter, Catherine; Newton-Fisher, Nicholas; Mullins, Caroline; Lamon, Noemie; Schel, Anne Marijke; Fallon, Brittany
2015-01-01
Chimpanzees of the Sonso community, Budongo Forest, Uganda were observed eating clay and drinking clay-water from waterholes. We show that clay, clay-rich water, and clay obtained with leaf sponges, provide a range of minerals in different concentrations. The presence of aluminium in the clay
Pranoto; Inayati; Firmansyah, Fathoni
2018-04-01
Water is a natural resource that is essential for all living creatures. In addition, water also caused of disease affecting humans. The existence of one of heavy metal pollutants cadmium (Cd) in the body of water is an environmental problem having a negative impact on the quality of water resources. Adsorption is one of the ways or methods that are often used for the treatment of wastewater. Clay and allophanic soil were used as Cd adsorbent by batch method. Ceramic filter was used to reduce Cd concentration in the ground water. This study aims to determine the effect of the composition of clay and Allophane, activation temperature and contact time on the adsorption capacity of Cd in the model solution. The optimum adsorption condition and the effectiveness of drinking water treatment in accordance with Regulation of the Minister of Health using clay/Andisol adsorbents in ensnare heavy metals Cd and bacterial pathogens. Identification and characterization of adsorbent is done by using NaF, Infrared Spectroscopy (FTIR), X-ray diffraction (XRD), specific surface area and total acidity specific. The Cd metal concentrations were analysed by atomic absorption spectroscopy. Adsorption isotherms determined by Freundlich and Langmuir equations. Modified water purification technology using ceramic filters are made with a mixture of clay and Andisol composition. The results showed samples of clay and Andisol containing minerals. The optimum condition of adsorption was achieved at 200 °C of activation temperature, 60 minutes of contact time and the 60:40 of clay:Andisol adsorbent composition. Freundlich isotherm represented Cd adsorption on the clay/Andisol adsorbent with a coefficient of determination (R2=0.99) and constant (k=1.59), higher than Langmuir (R2=0.89). The measurement results show the water purification technology using ceramic filters effectively reduce E. coli bacterial and Cd content in the water.
International Nuclear Information System (INIS)
Kitagawa, Ryuji; Kakitani, Satoru; Kuroda, Yoshimatsu; Matsuo, Sadao; Suzuoki, Tetsuro.
1980-01-01
The deuterium content of the constitutional and interlayer water extracted from the clay minerals (illite, montmorillonite, interstratified illite-montmorillonite mineral, kaolinite, halloysite) constituting the clay veins found in the granitic rocks in Hiroshima Prefecture was measured. The clay minerals were heated at 270 deg C to extract the interlayer water, then heated to 1,400 or 1,500 deg C to extract the constitutional water. The deuterium content of the local surface water collected from sampling points was measured. In the clay veins formed along perpendicular joints, the constituent clay minerals change from lower to upper part: illite → montmorillonite → kaolinite → halloysite. The deuterium content values of the constitutional water for illite and montmorillonite were estimated to be -67 to -69% and -86 to -89%, respectively. The deuterium content values of the constitutional water for halloysite range from -68 to -80% and for kaolinite from -63 to -67%. (J.P.N.)
Nanjunda Reddy, B. H.; Ranjan Rauta, Pradipta; Venkatalakshimi, V.; Sreenivasa, Swamy
2018-02-01
The aim of this research is to inspect the effect of Cloisite-30B (C30B) modified clay dispersed poly (acrylamide-co-Sodiumalginate)/AgNp hydrogel nanocomposites (PASA/C30B/Ag) for drug delivery and antibacterial activity. A novel hydrogel composite based sodium alginate (SA) and the inorganic modified clay with silver nano particle (C30B/AgNps)polymer hydrogel composites are synthesized via the graft copolymerization of acrylamide (AAm) in an aqueous medium with methylene bisacrylamide (MBA) as a crosslinking agent and ammonium per sulfate(APS) as an initiator. The UV/Visible spectroscopy of obtained composites is successfully studied, which confirms the occurrence of AgNps in the hydrogel composites. And the swelling capacity and bovine serum albumin (BSA) protein as model drug delivery study for these hydrogel nanocomposites have been carried out. The C30B/Ag filled hydrogel composites exhibit superior water absorbency or swelling capacity compared to pure samples and it is establish that the formulations with clay (C30B) dispersed silver nanocomposite hydrogels show improved and somewhat faster rate of drug delivery than other formulations(pure systems) and SEM and TEM reports suggests that the size of AgNps in the composite hydrogels is in the range of 5-10 nm with shrunken surface and the antibacterial characterizations for gram positive and gram negative bacteria are carried out by using Streptococcus faecalis (S. Faecalis) and Escherichia coli (E.coli) as model bacteria and the hydrogel composites of PASA/C30B/Ag shows exceptional antibacterial activity against both the bacteria as compared to pure hydrogel composites samples.
Estimation of soil water storage change from clay shrinkage using satellite radar interferometry
Brake, te Bram
2017-01-01
Measurements of soil water storage are hard to obtain on scales relevant for water management and policy making. Therefore, this research develops a new measurement methodology for soil water storage estimation in clay containing soils. The proposed methodology relies on the specific property of
International Nuclear Information System (INIS)
Medeiros, Keila Machado de
2010-01-01
Microporous membranes were obtained from nanocomposites polyamide66 and regional bentonite clay, through the technique of immersion precipitation. The nanocomposites were obtained by solution with a pre-established reaction time. The clay was treated with quaternary ammonium salt (Cetremide®) in order to make it organophilic. Untreated and treated clay were characterized by X-ray fluorescence (XRF) spectroscopy, Fourier transform infrared (FTIR), X-ray diffraction (XRD) and thermogravimetry (TG), which confirmed the insertion of the Cetremide® salt in the layers of clay and their thermal stability. While the membranes were characterized by XRD, TG, differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and flow measurements. The results of XRD, TG and DSC confirmed the thermal stability and morphological structure with intercalated/partially exfoliated lamellae of clay in the polymer matrix. By SEM, it was revealed an asymmetric morphology consisting of a skin layer and a porous sublayer. The higher clay content in the membrane give the lower film thickness. This influencing directly the flow measurements of the membranes produced from the nanocomposites. In general, the initial flow with distilled water through the membranes decrease and stabilise after 60 min, this due to a compression or swelling occurred in the membranes. In tests of water-oil separation it was found that the relationship J/J0 tends to be greater when using emulsions with lower concentration. The water-oil separation tests at concentrations of 300 and 500 ppm for all membranes showed a significant reduction in oil concentration in the permeate, thus showing that these membranes have potential for this application. (author)
Water repellency of clay, sand and organic soils in Finland
Directory of Open Access Journals (Sweden)
K. RASA
2008-12-01
Full Text Available Water repellency (WR delays soil wetting process, increases preferential flow and may give rise to surface runoff and consequent erosion. WR is commonly recognized in the soils of warm and temperate climates. To explore the occurrence of WR in soils in Finland, soil R index was studied on 12 sites of different soil types. The effects of soil management practice, vegetation age, soil moisture and drying temperature on WR were studied by a mini-infiltrometer with samples from depths of 0-5 and 5-10 cm. All studied sites exhibited WR (R index >1.95 at the time of sampling. WR increased as follows: sand (R = 1.8-5.0 < clay (R = 2.4-10.3 < organic (R = 7.9-undefined. At clay and sand, WR was generally higher at the soil surface and at the older sites (14 yr., where organic matter is accumulated. Below 41 vol. % water content these mineral soils were water repellent whereas organic soil exhibited WR even at saturation. These results show that soil WR also reduces water infiltration at the prevalent field moisture regime in the soils of boreal climate. The ageing of vegetation increases WR and on the other hand, cultivation reduces or hinders the development of WR.;
Nanoporous polymer--clay hybrid membranes for gas separation.
Defontaine, Guillaume; Barichard, Anne; Letaief, Sadok; Feng, Chaoyang; Matsuura, Takeshi; Detellier, Christian
2010-03-15
Nanohybrid organo-inorgano clay mineral-polydimethylsiloxane (PDMS) membranes were prepared by the reaction of pure and/or modified natural clay minerals (Sepiolite and montmorillonite) with PDMS in hexane, followed by evaporation of the solvent at 70 degrees C. The membranes were characterized by means of XRD, SEM, ATD-TG and solid state (29)Si magic angle spinning (MAS) and cross-polarization (CP) CP/MAS NMR. The morphology of the membranes depends on the content loading of clay mineral. For low content, the membrane composition is homogeneous, with well dispersed nanoparticles of clay into the polymer matrix, whereas for higher clay content, the membranes are constituted also of a mixture of well dispersed nanoparticles into the polymer, but in the presence of agglomerations of small clay particles. Quantitative (29)Si MAS NMR demonstrated a strong correlation between the clay content of the membrane and the average length of the PDMS chain, indicating that the nanohybrid material is made of clay particles covalently linked to the PDMS structure. This is particularly the case for Sepiolite with has a high density of Q(2) silanol sites. The separation performances of the prepared membranes were tested for CO(2)/CH(4) and O(2)/N(2) mixtures. The observed separation factors showed an increase of the selectivity in the case of CO(2)/CH(4) in comparison with membranes made from PDMS alone under the same conditions. 2009 Elsevier Inc. All rights reserved.
Inter-layered clay stacks in Jurassic shales
Pye, K.; Krinsley, D. H.
1983-01-01
Scanning electron microscopy in the backscattered electron mode is used together with energy-dispersive X-ray microanalysis to show that Lower Jurassic shales from the North Sea Basin contain large numbers of clay mineral stacks up to 150 microns in size. Polished shale sections are examined to determine the size, shape orientation, textural relationships, and internal compositional variations of the clays. Preliminary evidence that the clay stacks are authigenic, and may have formed at shallow burial depths during early diagenesis, is presented.
Directory of Open Access Journals (Sweden)
Landrou Gnanli
2017-01-01
Full Text Available In the ceramic industry and in many sectors, clay minerals are widely used. In earthen construction technique, clay plays a crucial role in the processing. The purpose of this research is to understand and modify the clay properties in earth material to propose an innovative strategy to develop a castable earth-based material. To do so, we focused on the modification of clay properties at fresh state with inorganic additives. As the rheological behaviour of clays is controlled by their surface charge, the addition of phosphate anion allows discussing deep the rheology of concentrated clay suspensions. We highlighted the thixotropic and shear thickening behaviour of a dispersed kaolinite clay suspensions. Indeed, by adding sodium hexametaphosphate the workability of clay paste increases and the behaviour is stable during time after a certain shear is applied. Moreover, we stress that the aging and the shift in critical strain in clay system are due to the re-arrangement of clay suspension and a decrease of deformation during time. The understanding of both effect: thixotropy and aging are crucial for better processing of clay-based material and for self-compacting clay concrete. Yet, studies need to pursue to better understand the mechanism.
Dispersion of radioactive materials in air and water
International Nuclear Information System (INIS)
Tolksdorf, P.; Meurin, G.
1976-01-01
A review of current analytical methods for treating the dispersion of radioactive material in air and water is given. It is shown that suitable calculational models, based on experiments, exist for the dispersion in air. By contrast, the analysis of the dispersion of radioactive material in water still depends on the evaluation of experiments with site-specific models. (orig.) [de
International Nuclear Information System (INIS)
Sergeant, C.; Vesvres, M.H.; Barsotti, V.; Stroes-Gascoyne, S.; Hamon, C.J.; Neble, S.; Shippers, A.; Le Marrec, C.; Vinsot, A.; Schwyn, B.
2010-01-01
Document available in extended abstract form only. Exploration of deep subsurface microbial life has increased for very diverse motives. One of them is that these environments are potential host rocks for radioactive waste repositories and that microorganisms may influence geochemical conditions around such sites and migration properties of radionuclides. The pore water Chemistry experiment (PC) was conducted at the Mont Terri-RL to measure in situ the pH, Eh, and other geochemical parameters within the pore water of the Opalinus Clay formation. The borehole for PC was drilled with N 2 under clean but not aseptic conditions, filled immediately with synthetic pore water, which was circulated and monitored for five years. Soon after initiation of PC it was evident that microbial activity affected the borehole water geochemistry. Microbial analyses, including molecular biology and culturing methods, were performed repeatedly during PC (2003-2006), with detailed analysis of water and over-core clay upon termination in 2007. Results indicated the presence of heterotrophic aerobes and anaerobes, nitrate-reducers, iron-reducers, sulphate-reducers and Archaea, which together with geochemical data suggested a reducing environment with sulphate reduction in the water and adjacent clay. A black precipitate containing pyrite and a strong H 2 S smell confirmed the occurrence of sulphate reduction. Specific species identified (> 98% similarity) in PC water included Pseudomonas stutzeri, Bacillus licheniformis, and Desulfosporosinus sp., with similar and additional species (e.g., Trichococcus sp.; Koccuria sp.) in the clay. The origin of these (mostly anaerobic) species cannot be determined with certainty. Some species likely resulted from contamination, but others could be revived species indigenous in the Opalinus Clay. The microbial processes that occurred in PC are not representative of the processes in the undisturbed formation but illustrate the potential for microbial
Effect of Water on Elastic and Creep Properties of Self-Standing Clay Films.
Carrier, Benoit; Vandamme, Matthieu; Pellenq, Roland J-M; Bornert, Michel; Ferrage, Eric; Hubert, Fabien; Van Damme, Henri
2016-02-09
We characterized experimentally the elastic and creep properties of thin self-standing clay films, and how their mechanical properties evolved with relative humidity and water content. The films were made of clay montmorillonite SWy-2, obtained by evaporation of a clay suspension. Three types of films were manufactured, which differed by their interlayer cation: sodium, calcium, or a mixture of sodium with calcium. The orientational order of the films was characterized by X-ray diffractometry. The films were mechanically solicited in tension, the resulting strains being measured by digital image correlation. We measured the Young's modulus and the creep over a variety of relative humidities, on a full cycle of adsorption-desorption for what concerns the Young's modulus. Increasing relative humidity made the films less stiff and made them creep more. Both the elastic and creep properties depended significantly on the interlayer cation. For the Young's modulus, this dependence must originate from a scale greater than the scale of the clay layer. Also, hysteresis disappeared when plotting the Young's modulus versus water content instead of relative humidity. Independent of interlayer cation and of relative humidity greater than 60%, after a transient period, the creep of the films was always a logarithmic function of time. The experimental data gathered on these mesoscale systems can be of value for modelers who aim at predicting the mechanical behavior of clay-based materials (e.g., shales) at the engineering macroscopic scale from the one at the atomistic scale, for them to validate the first steps of their upscaling scheme. They provide also valuable reference data for bioinspired clay-based hybrid materials.
Sakaki, T.; Vogt, T.; Komatsu, M.; Müller, H. R.
2013-12-01
The spatiotemporal variation of water content in the near field rock around repository tunnels for radioactive waste in clay formations is one of the essential quantities to be monitored for safety assessment in many waste disposal programs. Reliable measurements of water content are important not only for the understanding and prediction of coupled hydraulic-mechanic processes that occur during tunnel construction and ventilation phase, but also for the understanding of coupled thermal-hydraulic-mechanical (THM) processes that take place in the host rock during the post closure phase of a repository tunnel for spent fuel and high level radioactive waste (SF/HLW). The host rock of the Swiss disposal concept for SF/HLW is the Opalinus Clay formation (age of approx. 175 Million years). To better understand the THM effects in a full-scale heater-engineered barrier-rock system in Opalinus Clay, a full-scale heater test, namely the Full-Scale Emplacement (FE) experiment, was initiated in 2010 at the Mont Terri underground rock laboratory in north-western Switzerland. The experiment is designed to simulate the THM evolution of a SF/HLW repository tunnel based on the Swiss disposal concept in a realistic manner during the construction, emplacement, backfilling, and post-closure phases. The entire experiment implementation (in a 50 m long gallery with approx. 3 m diameter) as well as the post-closure THM evolution will be monitored using a network of several hundred sensors. The sensors will be distributed in the host rock, the tunnel lining, the engineered barrier, which consists of bentonite pellets and blocks, and on the heaters. The excavation is completed and the tunnel is currently being ventilated. Measuring water content in partially saturated clay-rich high-salinity rock with a deformable grain skeleton is challenging. Therefore, we use the ventilation phase (before backfilling and heating) to examine the applicability of commercial water content sensors and to
Evaluation of Water Vapor Sorption Hysteresis in Soils: The Role of Organic Matter and Clay
DEFF Research Database (Denmark)
Arthur, Emmanuel; Tuller, Markus; Moldrup, Per
2015-01-01
an important role. It is clear that modeling physical and biological soil processes is more accurate when SWC hysteresis is considered, particularly at low potentials where small differences in water content are associated with large changes in potential energy. The objectives of the presented study were to......: (i) evaluate and compare recently developed methods (MBET-n, Dh and SPN) for quantifying hysteresis in soils and pure clays, and (ii) investigate the role of organic matter (OM) and clay content and type on hysteresis. Five pure clays and two sets of soils with gradients in organic matter and clay....... For the SPN method, large contents of organic matter and clay in soils are associated with increased hysteresis. For both MBET-n and Dh methods, no clear trends of clay or OM contents effects on hysteresis was observed....
Park, Soo-Jin; Seo, Dong-Il; Lee, Jae-Rock
2002-07-01
In this work, the effect of surface treatments on smectitic clay was investigated in surface energetics and thermal behaviors of epoxy/clay nanocomposites. The pH values, X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR) were used to analyze the effect of cation exchange on clay surface and the exfoliation phenomenon of clay interlayer. The surface energetics of clay and thermal properties of epoxy/clay nanocomposites were investigated in contact angles and thermogravimetric analysis (TGA), respectively. From the experimental results, the surface modification of clay by dodecylammonium chloride led to the increases in both distance between silicate layers of about 8 A and surface acid values, as well as in the electron acceptor component (gamma(+)(s)) of surface free energy, resulting in improved interfacial adhesion between basic (or electron donor) epoxy resins and acidic (electron acceptor) clay interlayers. Also, the thermal stability of nanocomposites was highly superior to pure epoxy resin due to the presence of the well-dispersed clay nanolayer, which has a barrier property in a composite system.
Structure and mechanical properties of polyamide 6/Brazilian clay nanocomposites
Directory of Open Access Journals (Sweden)
Amanda Melissa Damião Leite
2009-06-01
Full Text Available Recent interest in polymer/organoclays nanocomposites systems is motivated by the possibility of achieving enhanced properties and added functionality at lower clay loading as compared to conventional micron size fillers. By adding montmorillonite clay to polyamide 6 increases the Young modulus, yield strength and also improves barrier properties. In this work, nanocomposites of polyamide 6 with montmorillonite clay were obtained. The clay was chemically modified with three different quaternary ammonium salts such as: Dodigen, Genamin and Cetremide. In this case, a dispersion of Na-MMT was stirred and a salt equivalent to 1:1 of cation exchange capacity (CEC of Na-MMT was added to the dispersion. The montmorillonite clay (untreated and treated by ammonium salts and nanocomposites were characterized by X ray diffractions. Also the nanocomposites were characterized by transmission electron microscopy and mechanical properties. The results indicated that all the quaternary ammonium salts were intercalated between the layers of clay, leading to an expansion of the interlayer spacing. The obtained nanocomposites showed better mechanical properties when compared to polyamide 6. The clay acted as reinforcing filler, increasing the rigidity of nanocomposites and decreasing its ductility.
Reitzel, Kasper; Balslev, Kristiane Astrid; Jensen, Henning S
2017-11-15
A 12 days laboratory study on potential desorption of Lanthanum (La) from a commercial La modified clay (Phoslock) was conducted using lake water from 17 Danish lakes with alkalinities between 0.02 and 3.7 meq L -1 and varying concentrations of DOC and humic acids (HA's). A similar study was conducted in artificial lake water with alkalinities from 0 to 2.5 meq L -1 in order to exclude interference from dissolved HA's. To test if La in solution (FLa) was associated with fine particles, the water samples were filtered sequentially through three filter sizes (1.2 μm, 0.45 μm and 0.2 μm), and finally, ultracentrifugation was used in an attempt to separate colloidal La from dissolved La. The study showed that higher FLa (up to 2.5 mg L -1 or 14% of the total La in the Phoslock) concentrations were found in soft water lakes compared to hard water lakes, probably due to dispersion of the clay at low alkalinities. In addition, this study showed that HA's seem to increase the FLa concentrations in soft water lakes, most likely through complexation of La retained in the Phoslock matrix. In summary, we conclude that elevated La concentrations in lake water after a Phoslock treatment should only be expected in soft water lakes rich in DOC and HA's. Copyright © 2017 Elsevier Ltd. All rights reserved.
Methods for obtention of PS/clay nanocomposites
International Nuclear Information System (INIS)
Lins, Pedro G.; Valera, Ticiane S.; Coelho, Caio P.D.; Demarquette, Nicole R.
2009-01-01
In this work, nanocomposites of Polystyrene (PS) and organoclay were obtained using a twin-screw extruder and a mixer Haake. A commercial clay named Cloisite 20A was used. The clay and the nanocomposites were characterized by X-Ray Diffraction. The rheological properties were investigated carrying out small amplitude oscillatory strain (SAOS). The results of X-ray diffraction showed that the polymer was incorporated by the organoclay. The results of SAOS indicated a better clay dispersion for the samples obtained using the mixer. (author)
DEFF Research Database (Denmark)
Arthur, E.; Tuller, M.; Møldrup, Per
2015-01-01
Soil texture, in particular the clay fraction, governs numerous environmental, agricultural and engineering soil processes. Traditional measurement methods for clay content are laborious and impractical for large-scale soil surveys. Consequently, clay prediction models that are based on water...... within a RH range from 3 to 93%. The clay contents, which ranged between 1 and 56%, were measured with a combination of sieving and sedimentation methods. Two regression models were developed for both adsorption and desorption at 10 RH levels (5, 10, 20, 30, 40, 50, 60, 70, 80 and 90%). While the first...
Clay exfoliation and polymer/clay aerogels by supercritical carbon dioxide
Directory of Open Access Journals (Sweden)
Simona eLongo
2013-11-01
Full Text Available Supercritical carbon dioxide (scCO2 treatments of a montmorillonite (MMT intercalated with ammonium cations bearing two long hydrocarbon tails (organo-modified MMT, OMMT led to OMMT exfoliation, with loss of the long-range order in the packing of the hydrocarbon tails and maintenance of the long-range order in the clay layers. The intercalated and the derived exfoliated OMMT have been deeply characterized, mainly by X-ray diffraction analyses. Monolithic composite aerogels, with large amounts of both intercalated and exfoliated OMMT and including the nanoporous-crystalline δ form of syndiotactic polystyrene (s-PS, have been prepared, by scCO2 extractions of s-PS-based gels. Also for high OMMT content, the gel and aerogel preparation procedures occur without re-aggregation of the exfoliated clay, which is instead observed for other kinds of polymer processing. Aerogels with the exfoliated OMMT have more even dispersion of the clay layers, higher elastic modulus and larger surface area than aerogels with the intercalated OMMT. Extremely light materials with relevant transport properties could be prepared. Moreover, s-PS-based aerogels with exfoliated OMMT could be helpful for the handling of exfoliated clay minerals.
Energy Technology Data Exchange (ETDEWEB)
Paumier, S
2007-11-15
Smectite are swelling clays widely used in industry. Their mechanical properties are unequal according to their mineralogical and physico-chemical characteristics. The aim of this study is to improve the knowledge of the interlayer cation impact on the structure built by the smectite-water system according to the concentration. Homo-ionic (Na{sup +} et Ca{sup 2+}) and bi-ionic systems are observed. This study cross checks mineralogical methods, physicochemical analysis and broad range of rheometric tests. At low concentration (less than 60 g/l) the calcium dispersions are shear thinning and few viscous due to the layer association in huge deformable flocks. The sodium smectite layers are dispersed; the dispersions are highly viscous. The lowest viscosity is detected for mix of 20 % of sodium smectite and 80 % of calcium smectite. At higher concentration (60 to 100 g/l), the yield stress and viscoelastic properties are studied by creep-recovery tests, oscillatory tests and imposed shear step. At the liquid state, the flow is first heterogeneous with a shear banding effect then homogeneous. The results make it possible to define the concentration area characteristic of each mechanical behavior (viscosity, shear thinning and yield stress) according to the saturation cation. The thixotropic properties are characterized with de-structuring-restructuring tests. Two kinetics are determined. Finally we realize a data base with 12 natural and industrial bentonite. The rheograms would be efficient to differentiate the natural calcium bentonite (Newtonian law), natural sodium bentonite (Herschel-Bulkley law) and activated calcium bentonite (Bingham law). (author)
Single clay sheets inside electrospun polymer nanofibers
Sun, Zhaohui
2005-03-01
Nanofibers were prepared from polymer solution with clay sheets by electrospinning. Plasma etching, as a well controlled process, was used to supply electrically excited gas molecules from a glow discharge. To reveal the structure and arrangement of clay layers in the polymer matrix, plasma etching was used to remove the polymer by controlled gasification to expose the clay sheets due to the difference in reactivity. The shape, flexibility, and orientation of clay sheets were studied by transmission and scanning electron microscopy. Additional quantitative information on size distribution and degree of exfoliation of clay sheets were obtained by analyzing electron micrograph of sample after plasma etching. Samples in various forms including fiber, film and bulk, were thinned by plasma etching. Morphology and dispersion of inorganic fillers were studied by electron microscopy.
International Nuclear Information System (INIS)
Medeiros, P.S.S.; Medeiros, K.M.; Araujo, E.M.; Lira, H.L.
2014-01-01
The petroleum refining industries have faced major problems in relation to the treatment of their effluents before disposal into the environment. Among the conventional technologies treatment of these effluents, the process of oil-water separation by means of membranes has been extensively used, for having enormous potentiality. Therefore, in this study, hybrid membranes of polyamide 6/ bentonite clay were produced by the technique of phase inversion and by precipitation of the solution from the nanocomposites obtained by melt intercalation. The clay was organically modified with the quaternary ammonium salt (Cetremide®). The nanocomposites were obtained from (PA6) with untreated (AST) and treated clay (ACT), which were subsequently characterized by X-ray diffraction (XRD). Already membranes were characterized by XRD, scanning electron microscopy (SEM) and flow measurements. From the XRD results, it was observed an exfoliated and/or partially exfoliated structure for the nanocomposites and for the membranes. From SEM images it was observed that the presence of AST and ACT clays in the polymeric matrix caused changes in membrane morphology and pore formation. The flow with distilled water in the membranes showed a decrease initially and then followed by stability. All membranes tested in the process of separating emulsions of oil in water, particularly those of nanocomposites obtained a significant reduction of oil concentration in the permeate, thus showing that these membranes have a great potential to be applied to the water-oil separation. (author)
Boom clay pore water, home of a diverse microbial community
International Nuclear Information System (INIS)
Wouters, Katinka; Moors, Hugo; Leys, Natalie
2012-01-01
Document available in extended abstract form only. Boom Clay pore water (BCPW) has been studied in the framework of geological disposal of nuclear waste for over two decades, thereby mainly addressing its geochemical properties. A reference composition for synthetic clay water has been derived earlier by modelling and spatial calibration efforts, mainly based on interstitial water sampled from different layers within the Boom clay. However, since microbial activity is found in a range of extreme circumstances, the possibility of microbes interacting with future radioactive waste in a host formation like Boom Clay, cannot be ignored. In this respect, BCPW was sampled from different Boom Clay layers using the Morpheus piezometer and subsequently analysed by a complementary set of microbiological and molecular techniques, in search for overall shared and abundant microorganisms. Similar to the previous characterization of the 'average' BCPW chemical composition, the primary aim of this microbiological study is to determine a representative BCPW microbial community which can be used in laboratory studies. Secondly, the in situ activity and the metabolic properties of members of this community were addressed, aiming to assess their survival and proliferation chances in repository conditions. In a first approach, total microbial DNA of the community was extracted from the BCPW samples. This molecular approach allows a broad insight in the total microbial ecology of the BCPW samples. By polymerase chain reaction (PCR) on the highly conserved 16S rRNA genes in this DNA pool and subsequent sequencing and bio-informatics analysis, operational taxonomic units (OTUs) could be assigned to the microbial community. The bacterial community was found to be quite diverse, with OTUs belonging to 8 different phyla (Proteobacteria, Actinobacteria, Firmicutes, Bacteroidetes, Chlorobi, Spirochetes, Chloroflexi and Deinococcus-Thermus). These results provide an overall view of the
Boom clay pore water, home of a diverse microbial community
Energy Technology Data Exchange (ETDEWEB)
Wouters, Katinka; Moors, Hugo; Leys, Natalie [SCK.CEN, Environment, Health and Safety Institute, B-2400 Mol (Belgium)
2012-10-15
Document available in extended abstract form only. Boom Clay pore water (BCPW) has been studied in the framework of geological disposal of nuclear waste for over two decades, thereby mainly addressing its geochemical properties. A reference composition for synthetic clay water has been derived earlier by modelling and spatial calibration efforts, mainly based on interstitial water sampled from different layers within the Boom clay. However, since microbial activity is found in a range of extreme circumstances, the possibility of microbes interacting with future radioactive waste in a host formation like Boom Clay, cannot be ignored. In this respect, BCPW was sampled from different Boom Clay layers using the Morpheus piezometer and subsequently analysed by a complementary set of microbiological and molecular techniques, in search for overall shared and abundant microorganisms. Similar to the previous characterization of the 'average' BCPW chemical composition, the primary aim of this microbiological study is to determine a representative BCPW microbial community which can be used in laboratory studies. Secondly, the in situ activity and the metabolic properties of members of this community were addressed, aiming to assess their survival and proliferation chances in repository conditions. In a first approach, total microbial DNA of the community was extracted from the BCPW samples. This molecular approach allows a broad insight in the total microbial ecology of the BCPW samples. By polymerase chain reaction (PCR) on the highly conserved 16S rRNA genes in this DNA pool and subsequent sequencing and bio-informatics analysis, operational taxonomic units (OTUs) could be assigned to the microbial community. The bacterial community was found to be quite diverse, with OTUs belonging to 8 different phyla (Proteobacteria, Actinobacteria, Firmicutes, Bacteroidetes, Chlorobi, Spirochetes, Chloroflexi and Deinococcus-Thermus). These results provide an overall view of the
Energy Technology Data Exchange (ETDEWEB)
Cavalho, Thamyres Cardoso de; Medeiros, Vanessa da Nobrega; Araujo, Edcleide Maria de; Lira, Helio Lucena, E-mail: thamyrescc@gmail.com, E-mail: vanismedeiros@gmail.com, E-mail: edcleide.araujo@ufcg.edu.br, E-mail: helio.lira@ufcg.edu.br [Universidade Federal de Campina Grande (UAEMa/CCT/UFCG), PB (Brazil). Unidade Academica de Engenharia de Materiais; Leite, Amanda Melissa Damiao, E-mail: amanda.leite@ect.ufrn.br [Universidade Federal do Rio Grande do Norte (ECT/UFRN), Natal, RN (Brazil). Escola de Ciencia e Tecnologia
2017-04-15
Membranes can be considered polymeric or inorganic films that function as a semipermeable barrier to filtration on a molecular scale, separating two phases and restricting, totally or partially, the transportation of one or more chemical species (solute) present in the solution. Therefore, the aim of this work is to produce polyethersulfone membranes (PES) and polyethersulfone/clay by phase inversion technique and evaluate the presence of clay in obtaining membranes for wastewater treatment. The used solvent was dimethylformamide (DMF) and clays were Brasgel PA (MMT) and Cloisite Na (CL Na) in the proportion of 3 to 5% (wt.). By Xray diffraction (XRD), the membranes with 3% of MMT and CL Na clays apparently had partially exfoliated structures. For the composition with 5% of CL Na a small peak was observed, which indicates that this is possibly an intercalated structure or microcomposite. By scanning electron microscopy (SEM), visualizes that the pure surface of the pure PES membrane a structure apparently without pores was observed in the used magnification and without roughness surface when compared to membranes with clay. The measurements of contact angle indicated that the inclusion of clay altered the wetting ability of the membranes. The flow with distilled water for all membranes started high and over time reached a stabilization level. Thus, it can be concluded that the presence and the content of clay altered the morphology of the membrane, contributing to an increase in water flow. (author)
Directory of Open Access Journals (Sweden)
B. M. A. Brito
Full Text Available Abstract Over the past few years, considerable research has been conducted using the techniques of mixture delineation and statistical modeling. Through this methodology, applications in various technological fields have been found/optimized, especially in clay technology, leading to greater efficiency and reliability. This work studied the influence of carboxymethylcellulose on the rheological and filtration properties of bentonite dispersions to be applied in water-based drilling fluids using experimental planning and statistical analysis for clay mixtures. The dispersions were prepared according to Petrobras standard EP-1EP-00011-A, which deals with the testing of water-based drilling fluid viscosifiers for oil prospecting. The clay mixtures were transformed into sodic compounds, and carboxymethylcellulose additives of high and low molar mass were added, in order to improve their rheology and filtrate volume. Experimental planning and statistical analysis were used to verify the effect. The regression models were calculated for the relation between the compositions and the following rheological properties: apparent viscosity, plastic viscosity, and filtrate volume. The significance and validity of the models were confirmed. The results showed that the 3D response surfaces of the compositions with high molecular weight carboxymethylcellulose added were the ones that most contributed to the rise in apparent viscosity and plastic viscosity, and that those with low molecular weight were the ones that most helped in the reduction of the filtrate volume. Another important observation is that the experimental planning and statistical analysis can be used as an important auxiliary tool to optimize the rheological properties and filtrate volume of bentonite clay dispersions for use in drilling fluids when carboxymethylcellulose is added.
International Nuclear Information System (INIS)
Baldi, G.; Hueckel, T.; Peano, A.; Pellegrini, R.
1991-01-01
The results of two years of research on thermomechanics of clays performed within CEC contract Fl1W/0150 are described herein. Previous studies (research contracts with CEC/WAS/380.83.7 l) performed by ISMES have evidenced the need for an improved modelling of the volumetric response of natural clays. In a coupled approach, this leads to an improved prediction of pore-pressure development and dissipation. This is crucial for assessing conditions of a possible local thermal failure as verified in laboratory tests done at ISMES. The first part of the study lays the foundations of a comprehensive theoretical treatment of the interaction between water and soil skeleton. It consists in: (a) developing a framework for inclusion of water/soil particle thermally induced interaction into a thermodynamically consistent mixture theory approach (Section 2); (b) studying possible modelling approaches of considering the effective thermal expansion coefficient of pore water dependency on pore water status (Section 2); (c) testing artificial clays to assess pore water thermal expansion dependence on temperature in the presence of different amounts of active clay minerals and also Boom clay (Section 3); (d) performing a laboratory test campaign on Boom clay with special attention to the response in the overconsolidated domain (Section 4). 89 figs., 18 tabs., 102 refs
Thixotropic Properties of Latvian Clays
Lakevičs, Vitālijs; Stepanova, Valentīna; Ruplis, Augusts
2015-01-01
This research studies Latvia originated Devon (Tūja, Skaņkalne), quaternary (Ceplīši), Jurassic, (Strēļi) and Triassic (Vadakste) deposit clays as well as Lithuania originated Triassic (Akmene) deposit clays. Thixotropic properties of clay were researched by measuring relative viscosity of clay in water suspensions. Relative viscosity is measured with a hopper method. It was detected that, when concentration of suspension is increased, clay suspension’s viscosity also increases. It happens un...
Effluent dispersion in natural water receivers (tracer examination)
International Nuclear Information System (INIS)
Szpilowski, S.; Owczarczyk, A.; Chmielewski, A.G.
1993-01-01
Tracer methods constitute very convenient means for observation and examination of effluent dispersion and dilution processes in natural water receivers. In the report there are presented methods developed and used by the Institute of Nuclear Chemistry and Technology (INCT) to measure mixing parameters in natural streams to determine distances of complete transverse mixing as well as to assess and predict dispersion of sewage in large water reservoirs. There are also presented the methods of predicting initial stage of dispersion of sewage discharged into large water reservoirs through underwater out falls and the method for determining the decomposition rates of effluent entering a natural water receiver. The methods presented can be used in analysis of pollution in a given water region, in selection of optimal sewage out fall locations as well as in prediction of effluent dilution intensity at different hydro- and meteorological conditions. (author). 27 refs, 15 figs, 2 tabs
International Nuclear Information System (INIS)
Landesman, C.; Grambow, B.; Bailly, C.; Ribet, S.; Perrigaud, K.; Baty, V.; Giffaut, E.
2010-01-01
Document available in extended abstract form only. Full text of publication entered in this record. For assessing the mass transfer resistance of the Callovo-Oxfordian clay rock formation in case of implementing a nuclear waste repository, various strongly coupled processes need to be understood and quantified both in near and far field: multi-species diffusion/advection, mineral/pore water interaction, interaction with the waste matrix and engineered barrier material, radionuclide retention, colloid transport, pore water chemistry evolution etc. To study many of these processes in their interrelationship simultaneously, a series of high pressure stainless steel advection cell was designed and clay cores from different locations of different calcite and clay contents were machined to fit the inner diameter of the cells with a precision of 50 μm. After assembling, simulated oxygen free clay pore water with bromine tracer was pushed by a High Pressure pump through the reactor by a pressure of up 100 bars at temperatures between 20 and 90 deg. C and the out-flowing water was collected, protected from air and analyzed by ICP-MS, COT meter and ion chromatography in regular time intervals. The water flow rate was between 0.02 and 1.2 mL/ d, corresponding to a clay rock permeabilities between 10 -12 and 10 -14 m/s at 25 deg. C. Permeabilities increase with temperature as expected due to reduction of viscosity of water. The experiments last up to 2 years. The first drops of out flowing allow estimating the initial pore water composition. This is particular useful to assess mobile natural organic matter contents, Se concentrations and temperature effect on clay water composition. Results show that only very small organic molecules are mobile. Temperature had only little effect on water composition. After few months both tritiated (HTO) water and 36 Cl were added and from the evolution of the activities in the out flowing water dispersion coefficients and accessible
Water-Sensitivity Characteristics of Briquettes Made from High-Rank Coal
Directory of Open Access Journals (Sweden)
Geng Yunguang
2016-01-01
Full Text Available In order to study the water sensitivity characteristics of the coalbed methane (CBM reservoir in the southern Qinshui Basin, the scanning electron microscopy, mineral composition and the water sensitivity of main coalbed 3 cores were tested and analyzed. Because CBM reservoirs in this area are characterized by low porosity and low permeability, the common water sensitivity experiment of cores can’t be used, instead, the briquettes were chose for the test to analysis the water sensitivity of CBM reservoirs. Results show that: the degree of water sensitivity in the study area varies from week to moderate. The controlling factors of water sensitivity are clay mineral content and the occurrence type of clay minerals, permeability and liquid flow rate. The water sensitivity damage rate is positively correlated with clay mineral content and liquid flow rate, and is negatively correlated with core permeability. The water sensitivity of CBM reservoir exist two damage mechanisms, including static permeability decline caused by clay mineral hydration dilatation and dynamic permeability decline caused by dispersion/migration of clay minerals.
Directory of Open Access Journals (Sweden)
S. Benali
2008-01-01
Full Text Available Exfoliated nanocomposites are prepared by dispersion of poly(ε-caprolactone (PCL grafted montmorillonite nanohybrids used as masterbatches in poly(styrene-co-acrylonitrile (SAN. The PCL-grafted clay nanohybrids with high inorganic content are synthesized by in situ intercalative ring-opening polymerization of ε-caprolactone between silicate layers organomodified by alkylammonium cations bearing two hydroxyl functions. The polymerization is initiated by tin alcoholate species derived from the exchange reaction of tin(II bis(2-ethylhexanoate with the hydroxyl groups borne by the ammonium cations that organomodified the clay. These highly filled PCL nanocomposites (25 wt% in inorganics are dispersed as masterbatches in commercial poly(styrene-co-acrylonitrile by melt blending. SAN-based nanocomposites containing 3 wt% of inorganics are accordingly prepared. The direct blend of SAN/organomodified clay is also prepared for sake of comparison. The clay dispersion is characterized by wide-angle X-ray diffraction (WAXD, atomic force microscopy (AFM, and solid state NMR spectroscopy measurements. The thermal properties are studied by thermogravimetric analysis. The flame retardancy and gas barrier resistance properties of nanocomposites are discussed both as a function of the clay dispersion and of the matrix/clay interaction.
Plasma treatment of diamond nanoparticles for dispersion improvement in water
International Nuclear Information System (INIS)
Yu Qingsong; Kim, Young Jo; Ma, Hongbin
2006-01-01
Low-temperature plasmas of methane and oxygen mixtures were used to treat diamond nanoparticles to modify their surface characteristics and thus improve their dispersion capability in water. It was found that the plasma treatment significantly reduced water contact angle of diamond nanoparticles and thus rendered the nanoparticles with strong water affinity for dispersion enhancement in polar media such as water. Surface analysis using Fourier transform infrared spectroscopy confirmed that polar groups were imparted on nanoparticle surfaces. As a result, improved suspension stability was observed with plasma treated nanoparticles when dispersed in water
Effect of addition of organo clay on mechanical properties and dynamic-mechanical based TPV
International Nuclear Information System (INIS)
Honorato, Luciana R.; Silva, Adriana A.; Soares, Bluma G.; Soares, Ketly P.
2011-01-01
The effect of organophilic clay on the mechanical and dynamical-mechanical properties of thermoplastic elastomers based on polypropylene (PP) and nitrile rubber (NBR) was investigated. The addition of clay was performed from a master batch prepared by a solution intercalation of NBR inside the clay galleries. Since the PP/NBR blend is highly incompatible, PP functionalized with maleic anhydride (PP-g-MA) and carboxylated NBR (XNBR) were employed as compatibilizing system together with triethylene-tetramine (TETA) used as coupling agent. The addition of Clay inside the elastomeric phase of the TPV resulted in a significant decrease of the elongation at break without changes on the tensile strength. The presence of clay also promoted a slight increase of the storage modulus and the glass transition temperature. The small angle X ray scattering confirmed the high dispersion of clay inside the TPV. Analysis of light scattering small angle (SAXS) confirmed the high dispersion of clay in the matrix of the TPV. (author)
Dynamics of water confined in clay minerals
International Nuclear Information System (INIS)
Le Caer, S.; Pommeret, S.; Renault, J.Ph.; Lima, M.; Righini, R.; Gosset, D.; Simeone, D.; Bergaya, F.
2012-01-01
Ultrafast infrared spectroscopy of the O-D stretching mode of dilute HOD in H 2 O probes the local environment and the hydrogen bond network of confined water. The dynamics of water molecules confined in the interlayer space of montmorillonites (Mt) and in interaction with two types of cations (Li + and Ca 2+ ) but also with the negatively charged siloxane surface are studied. The results evidence that the OD vibrational dynamics is significantly slowed down in confined media: it goes from 1.7 ps in neat water to 2.6 Ps in the case of Li + cations with two water pseudo-layers (2.2-2.3 ps in the case of Ca 2+ cations) and to 4.7 ps in the case of Li + cations with one water pseudo-layer. No significant difference between the two cations is noticed. In this 2D confined geometry (the interlayer space being about 0.6 nm for two water pseudo-layers), the relaxation time constants obtained are comparable to the ones measured in analogous concentrated salt solutions. Nevertheless, and in strong opposition to the observations performed in the liquid phase, anisotropy experiments evidence the absence of rotational motions on a 5 ps time scale, proving that the hydrogen bond network in the interlayer space of the clay mineral is locked at this time scale. (authors)
End Functionalized Nonionic Water-Dispersible Conjugated Polymers.
Zhan, Ruoyu; Liu, Bin
2017-09-01
2,7-Dibromofluorene monomers carrying two or four oligo(ethylene glycol) (OEG) side chains are synthesized. Heck coupling between the monomers and 1,4-divinylbenzene followed by end capping with [4-(4-bromophenoxy)butyl]carbamic acid tert-butyl ester leads to two nonionic water-dispersible poly(fluorene-alt-1,4-divinylenephenylene)s end-functionalized with amine groups after hydrolysis. In water, the polymer with a lower OEG density (P1) has poor water dispersibility with a quantum yield of 0.24, while the polymer with a higher OEG density (P2) possesses excellent water-dispersibility with a high quantum yield of 0.45. Both polymers show fluorescence enhancement and blue-shifted absorption and emission maxima in the presence of surfactant sodium dodecyl sulfate and dodecyltrimethylammonium bromide. The polymers are also resistant to ionic strength with minimal nonspecific interactions to bovine serum albumin. When biotin is incorporated into the end of the polymer backbones through N-hydroxysuccinimide/amine coupling reaction, the biotinylated polymers interact specifically with streptavidin on solid surface. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
The effect of organo-clay on the dielectric properties of silicone rubber
International Nuclear Information System (INIS)
Razzaghi-Kashani, M; Gharavi, N; Javadi, S
2008-01-01
Dielectric elastomers are highly deformable and fast response smart materials capable of actuation under electric fields. Among commercially available dielectric elastomers, silicone rubber can be compounded with different fillers in order to modify its electrical and mechanical properties. To study the effect of organically modified montmorillonite (OMMT) on the dielectric properties of silicone rubber, OMMT was added to this rubber at two levels, 2% and 5%, using two methods, low-shear and high-shear mixing. Composites were characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). The XRD patterns showed different crystallite structures for silicate platelets in the rubber matrix as a result of the two different mixing methods. In low-shear mixing, the ordered crystallite structure of the clay remains almost unchanged, whereas in high-shear mixing it loses its ordered structure, leading to the disappearance of the diffraction peaks. SEM and AFM micrographs depicted better dispersion and more uniform distribution of the organo-clay under high-shear mixing compared to those obtained by low-shear mixing. The tensile properties also confirmed the different degree of dispersion of the nano-clay resulting from the two different methods of mixing. The dielectric properties of the composites were measured under AC electric fields, and the results were compared with reference silicone rubbers with no OMMT. It was shown that the order of organo-clay layers in the less dispersed structure of the clay imparts an additional ionic polarization and higher dielectric permittivity compared to the case where the clay layers are more dispersed and lost their order. The storage and loss dielectric constants of base silicone rubber increase when it is compounded with OMMT
Aristilde, Ludmilla; Galdi, Stephen M.; Kelch, Sabrina E.; Aoki, Thalia G.
2017-08-01
Understanding the hydrodynamics in clay nanopores is important for gaining insights into the trapping of water, nutrients, and contaminants in natural and engineered soils. Previous investigations have focused on the interlayer organization and molecular diffusion coefficients (D) of cations and water molecules in cation-saturated interlayer nanopores of smectite clays. Little is known, however, about how these interlayer dynamic properties are influenced by the ubiquitous presence of small organic compounds such as sugars in the soil environment. Here we probed the effects of glucose molecules on montmorillonite interlayer properties. Molecular dynamics simulations revealed re-structuring of the interlayer organization of the adsorptive species. Water-water interactions were disrupted by glucose-water H-bonding interactions. ;Dehydration; of the glucose-populated nanopore led to depletion in the Na solvation shell, which resulted in the accumulation of both Na ions (as inner-sphere complexes) and remaining hydrated water molecules at the mineral surface. This accumulation led to a decrease in both DNa and Dwater. In addition, the reduction in Dglucose as a function of increasing glucose content can be explained by the aggregation of glucose molecules into organic clusters H-bonded to the mineral surface on both walls of the nanopore. Experimental nuclear magnetic resonance and X-ray diffraction data were consistent with the theoretical predictions. Compared to clay interlayers devoid of glucose, increased intensities and new peaks in the 23Na nuclear magnetic resonance spectra confirmed increasing immobilization of Na as a function of increasing glucose content. And, the X-ray diffraction data indicated a reduced collapse of glucose-populated interlayers exposed to decreasing moisture conditions, which led to the maintenance of hydrated clay nanopores. The coupling of theoretical and experimental findings sheds light on the molecular to nanoscale mechanisms that
Change of microstructure of clays due to the presence of heavy metal ions in pore water
Directory of Open Access Journals (Sweden)
Saiyouri N.
2010-06-01
Full Text Available The compressibility of engineered barrier clays is, to a large extent, controlled by microstructure change due to the presence of chemical ions in clay-water system. This paper aims to investigate the change of microstructure of clays due to the presence of heavy metal ions in pore water. We use two pure clays (kaolinite and bentonite in the study. One-dimensional consolidation tests were performed on reconstituted samples, which are prepared with distilled water and three types of heavy metal solutions (Pb(NO32, Cu(NO32, Zn(NO32,. In order to better understand the impact of chemical pore fluid on microstructure of the two clays, following the consolidation test, scanning electron microscope (SEM observations and mercury intrusion pore size distribution measurements (MIP were conducted. Due to the measurement range of MIP, which is only allowed to measure the minimal pore size 20 Å, BET method by gas sorption, whose measurement pore size range is from 3.5 Å to 500 Å, is used to measure the micropore size distribution. By this method, specific surface area of the soils can be also determined. It can be employed to demonstrate the difference of creep performance between the soils. Furthermore, a series of batch equilibrium tests were conducted to better understand the physical-chemical interactions between the particles of soils and the heavy metal ions. With the further consideration of the interparticle electrical attractive and repulsive force, an attempt has been made to predict the creep behaviour by using the modified Gouy-Chapman double layer theory. The results of calculation were compared with that of tests. The comparison shows that the prediction of compressibility of the clays according to the modified double diffuse layer theory can be reasonably agreement with the experimental data.
International Nuclear Information System (INIS)
Quagliano, J; García, Irma Gavilán
2012-01-01
In this contribution we report the results of studying the incorporation of exfoliated bentonitic clays into polyurethane foams. A suspension in water of a sodium bentonite from Argentine Patagonia was interchanged with cetyl trimethyl ammonium bromide (CTAB) for 4 h at 80°C, rendering an exfoliated clay, which is nanometric in only one dimension. This nanoclay, when dispersed in the polyurethane, resulted in the same fire retardancy rating (UL-94) than when polyurethane was treated with a commercial nanoclay. Scanning electron microscopy (SEM) at low augmentations of polyurethane samples treated with the synthethized nanoclay (2,5% w/w) showed no differences respect to untreated polyurethane, except for the irregularity of void edges.
Development of SBR-Nano clay Composites with Epoxidized Natural Rubber as Compatibilizer
International Nuclear Information System (INIS)
Rajasekar, R.; Das, Ch.K.; Gert Heinrich, G.; Das, A.
2009-01-01
The significant factor that determines the improvement of properties in rubber by the incorporation of nano clay is its distribution in the rubber matrix. The simple mixing of nonpolar rubber and organically modified nano clay will not contribute for the good dispersion of nano filler in the rubbery matrix. Hence a polar rubber like epoxidized natural rubber (ENR) can be used as a compatibilizer in order to obtain a better dispersion of the nano clay in the matrix polymer. Epoxidized natural rubber and organically modified nano clay composites (EC) were prepared by solution mixing. The nano clay employed in this study is Cloisite 20A. The obtained nano composites were incorporated in styrene butadiene-rubber (SBR) compounds with sulphur as a curing agent. The morphology observed through X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HR-TEM) shows that the nano clay is highly intercalated in ENR, and further incorporation of EC in SBR matrix leads to partial exfoliation of the nano clay. Dynamic mechanical thermal analysis showed an increase in storage modulus and lesser damping characteristics for the compounds containing EC loading in SBR matrix. In addition, these compounds showed improvement in the mechanical properties.
Influence of clay minerals on curcumin properties: Stability and singlet oxygen generation
Gonçalves, Joyce L. S.; Valandro, Silvano R.; Poli, Alessandra L.; Schmitt, Carla C.
2017-09-01
Curcumin (CUR) has showed promising photophysical properties regarding to biological and chemical sciences. However, the main barrier for those applications are their low solubility and stability in aqueous solution. The effects of two different clay minerals, the montmorillonite (SWy-2) and the Laponite RD (Lap) nanoclay, on the stabilization of Curcumin were investigated. Their effects were compared with two well-established environments (acidic and neutral aqueous media). CUR/clay hybrids were prepared using a simple and fast method, where CUR solution was added into clay suspensions, to obtain well dispersed hybrids in water. The degradation process of CUR and CUR/clays hybrids was investigated using UV-Vis spectroscopic. For both studied hybrids, the CUR degradation process was suppressed by the presence of the clay particles. Furthermore, the Lap showed a great stabilization effect than SWy-2. This behavior was due to the smaller particle size and higher exfoliation ability of Lap, providing a large surface for CUR adsorption compared to SWy-2. The degradation process of CUR solutions and CUR/clay hybrids was also studied in the presence of light. CUR photodegradation process was faster not only in the aqueous solution but also in the clay suspension compared to those studied in the dark. The presence of clay particles accelerated the photodegradation of CUR due to the products formation in the reactions between CUR and oxygen radicals. Our results showed that the singlet oxygen quantum yield (ΦΔ) of CUR were about 59% higher in the clay suspensions than CUR in aqueous solution. Therefore, the formation of CUR/clay hybrids, in particularly with Lap, suppressed the degradation in absence light of CUR and increased the singlet oxygen generation, which makes this hybrids of CUR/clay a promising material to enlarge the application of CUR in the biological sciences.
Behrends, T.; Veen, I. van der; Hoving, A.; Griffioen, J.
2016-01-01
The Rupel Clay member in the Netherlands largely corresponds to the Boom Formation in Belgium, and this marine, clay-rich deposit is a potential candidate to host radioactive waste disposal facilities. Prediction of the speciation of radionuclides in Rupel Clay pore water and their retardation by
Mineral Acquisition from Clay by Budongo Forest Chimpanzees.
Directory of Open Access Journals (Sweden)
Vernon Reynolds
Full Text Available Chimpanzees of the Sonso community, Budongo Forest, Uganda were observed eating clay and drinking clay-water from waterholes. We show that clay, clay-rich water, and clay obtained with leaf sponges, provide a range of minerals in different concentrations. The presence of aluminium in the clay consumed indicates that it takes the form of kaolinite. We discuss the contribution of clay geophagy to the mineral intake of the Sonso chimpanzees and show that clay eaten using leaf sponges is particularly rich in minerals. We show that termite mound soil, also regularly consumed, is rich in minerals. We discuss the frequency of clay and termite soil geophagy in the context of the disappearance from Budongo Forest of a formerly rich source of minerals, the decaying pith of Raphia farinifera palms.
Mineral Acquisition from Clay by Budongo Forest Chimpanzees.
Reynolds, Vernon; Lloyd, Andrew W; English, Christopher J; Lyons, Peter; Dodd, Howard; Hobaiter, Catherine; Newton-Fisher, Nicholas; Mullins, Caroline; Lamon, Noemie; Schel, Anne Marijke; Fallon, Brittany
2015-01-01
Chimpanzees of the Sonso community, Budongo Forest, Uganda were observed eating clay and drinking clay-water from waterholes. We show that clay, clay-rich water, and clay obtained with leaf sponges, provide a range of minerals in different concentrations. The presence of aluminium in the clay consumed indicates that it takes the form of kaolinite. We discuss the contribution of clay geophagy to the mineral intake of the Sonso chimpanzees and show that clay eaten using leaf sponges is particularly rich in minerals. We show that termite mound soil, also regularly consumed, is rich in minerals. We discuss the frequency of clay and termite soil geophagy in the context of the disappearance from Budongo Forest of a formerly rich source of minerals, the decaying pith of Raphia farinifera palms.
Synthesis, thermal properties and applications of polymer-clay nanocomposites
International Nuclear Information System (INIS)
Meneghetti, Paulo; Qutubuddin, Syed
2006-01-01
Polymer-clay nanocomposites constitute a new class of materials in which the polymer matrix is reinforced by uniformly dispersed inorganic particles (usually 10 wt.% or less) having at least one dimension in the nanometer scale. Nanocomposites exhibit improved properties when compared to pure polymer or conventional composites, such as enhanced mechanical and thermal properties, reduced gas permeability, and improved chemical stability. In this work, the synthesis of poly(methyl methacrylate) (PMMA)/clay nanocomposites is described via two methods: in situ and emulsion polymerization. The in situ technique follows a two-step process: ion-exchange of the clay to make it hydrophobic, and polymerization after dispersing the functionalized clay in the monomer. The emulsion technique combines the two steps of the in situ method into one by conducting ion-exchange and polymerization in an aqueous medium in the same reactor. The clay (montmorillonite, MMT) is functionalized with a zwitterionic surfactant, octadecyl-dimethyl betaine (C18DMB). Partially exfoliated nanocomposite, observed by transmission electron microscopy (TEM), was obtained by emulsion polymerization with 10 wt.% clay. Glass transition temperature (T g ) of this nanocomposite was 18 deg. C higher than pure PMMA. With the same clay content, in situ polymerization produced intercalated nanocomposite with T g 10 deg. C lower than the emulsion nanocomposite. The storage modulus of partially exfoliated nanocomposite was superior to the intercalated structure and to the pure polymer. Using nanocomposite technology, novel PMMA nanocomposite gel electrolytes were synthesized exhibiting improved ionic conductivity and stable lithium interfacial resistance. Nanocomposites can also be used for gas storage and packaging applications as demonstrated by high barrier polymer-clay films
Synthesis, thermal properties and applications of polymer-clay nanocomposites
Energy Technology Data Exchange (ETDEWEB)
Meneghetti, Paulo [Chemical Engineering Department, Case Western Reserve University, 10900 Euclid Ave. Cleveland, OH 44106 (United States); Qutubuddin, Syed [Chemical Engineering Department, Case Western Reserve University, 10900 Euclid Ave. Cleveland, OH 44106 (United States)]. E-mail: sxq@case.edu
2006-03-15
Polymer-clay nanocomposites constitute a new class of materials in which the polymer matrix is reinforced by uniformly dispersed inorganic particles (usually 10 wt.% or less) having at least one dimension in the nanometer scale. Nanocomposites exhibit improved properties when compared to pure polymer or conventional composites, such as enhanced mechanical and thermal properties, reduced gas permeability, and improved chemical stability. In this work, the synthesis of poly(methyl methacrylate) (PMMA)/clay nanocomposites is described via two methods: in situ and emulsion polymerization. The in situ technique follows a two-step process: ion-exchange of the clay to make it hydrophobic, and polymerization after dispersing the functionalized clay in the monomer. The emulsion technique combines the two steps of the in situ method into one by conducting ion-exchange and polymerization in an aqueous medium in the same reactor. The clay (montmorillonite, MMT) is functionalized with a zwitterionic surfactant, octadecyl-dimethyl betaine (C18DMB). Partially exfoliated nanocomposite, observed by transmission electron microscopy (TEM), was obtained by emulsion polymerization with 10 wt.% clay. Glass transition temperature (T {sub g}) of this nanocomposite was 18 deg. C higher than pure PMMA. With the same clay content, in situ polymerization produced intercalated nanocomposite with T {sub g} 10 deg. C lower than the emulsion nanocomposite. The storage modulus of partially exfoliated nanocomposite was superior to the intercalated structure and to the pure polymer. Using nanocomposite technology, novel PMMA nanocomposite gel electrolytes were synthesized exhibiting improved ionic conductivity and stable lithium interfacial resistance. Nanocomposites can also be used for gas storage and packaging applications as demonstrated by high barrier polymer-clay films.
Water storage change estimation from in situ shrinkage measurements of clay soils
Brake, te B.; Ploeg, van der M.J.; Rooij, de G.H.
2013-01-01
The objective of this study is to assess the applicability of clay soil elevation change measurements to estimate soil water storage changes, using a simplified approach. We measured moisture contents in aggregates by EC-5 sensors, and in multiple aggregate and inter-aggregate spaces (bulk soil) by
DEFF Research Database (Denmark)
Plackett, David; Siu, Ana; Li, Qingfeng
2011-01-01
dispersion of modified laponite clay was achieved in polybenzimidazole (PBI) solutions which, when cast and allowed to dry, resulted in homogeneous and transparent composite membranes containing up to 20 wt% clay in the polymer. The clay was organically modified using a series of ammonium and pyr...
Dielectric properties of clay-rock and their influence on water content measurement with TDR probes
International Nuclear Information System (INIS)
Bore, T.; Coelho, D.; Robinet, J.C.; Delepine-Lesoille, S.; Placko, D.; Gatabin, C.; Sabouroux, P.; Six, G.; Taillade, F.
2012-01-01
Document available in extended abstract form only. Clays constitute major components for radioactive waste repositories managed by Andra. Water content monitoring is one of the indicators chosen to evaluate the health of the structure. In this perspective, several TDR probes have been installed in various structures, made of three types of clay materials: the bentonite, the clay-rock (Callovo-Oxfordian mud-stone) and the compacted crushed clay-rock. . The technique consists of a time-of-flight measurement of an electric pulse along the TDR probes. To convert flight time propagation delay into water content, calibrations are required. This conversion is however neither accurate, nor generalizable for other mixtures. For precise understanding and modeling of the sensing chain, a better knowledge the complex permittivity of clay materials is necessary. Chosen TDR sensing lines make use of a step electric pulse (such as Campbell TDR100). Considering the rise time of this system, the frequency content of the measured TDR wave form extends from about 20 kHz to roughly 1.5 GHz. Material dielectric must thus be characterized over a broad band frequency. The determination of the electromagnetic properties using non resonant method is fundamentally deduced from their impedance and the wave velocities in the materials. This kind of technique relies on a device able to direct the electromagnetic energy towards a material and to collect the reflected and transmitted parts. In a first step, we designed a transmission line to provide electromagnetic characterizations of clay material. The clay material under test is inserted into a brass coaxial cell specifically designed for our purposes. Two conical transition units surround the specimen holder. The electromagnetic properties of the sample are based on the reflection from the material and the transmission through the material measured by a vector network analyser (VNA). The determination of the electromagnetic properties from
Thixotropic Properties of Latvian Illite Containing Clays
Lakevičs, Vitālijs; Stepanova, Valentīna; Niedra, Santa; Dušenkova, Inga; Ruplis, Augusts
2015-01-01
Thixotropic properties of Latvian Devonian and Quaternary clays were studied. Dynamic viscosity of the water clay suspensions were measured with a rotating viscometer. Influence of concentration, pH and modifiers on the thixotropic clay properties was analyzed. It was found that Latvian clays have thixotropic properties. Stability of clay suspensions is described with the thixotropy hysteresis loop. Increasing the speed of the viscometer rotation, dynamic viscosity of the clay suspension decr...
Directory of Open Access Journals (Sweden)
Mohammad Bashar
2014-01-01
Full Text Available The effects of organic modifier and processing method on morphology and mechanical properties of epoxy-clay nanocomposites were investigated. In this study, the preparation of nanocomposites by exfoliation-adsorption method involved an ultrasonic mixing procedure, and mechanical blending was used for in situ intercalative polymerization. The microstructure study revealed that the organoclay, which was ultrasonically mixed with the epoxy, partially exfoliated and intercalated. In contrast, organoclay remained in phase-separated and flocculated state after the mechanical blending process. Tensile stiffness increased significantly for the nanocomposite prepared by ultrasonic dispersion method through realizing the reinforcing potential of exfoliated silicate layers. Nanocomposites with exfoliated and intercalated nanoclay morphology were ineffective in enhancing the fracture toughness whereas nanocomposites with phase-separated and flocculated morphology have improved crack resistance predominantly by crack deflecting and pinning mechanisms.
Controlling harmful algae blooms using aluminum-modified clay.
Liu, Yang; Cao, Xihua; Yu, Zhiming; Song, Xiuxian; Qiu, Lixia
2016-02-15
The performances of aluminum chloride modified clay (AC-MC), aluminum sulfate modified clay (AS-MC) and polyaluminum chloride modified clay (PAC-MC) in the removal of Aureococcus anophagefferens were compared, and the potential mechanisms were analyzed according to the dispersion medium, suspension pH and clay surface charges. The results showed that AC-MC and AS-MC had better efficiencies in removing A.anophagefferens than PAC-MC. The removal mechanisms of the three modified clays varied. At optimal coagulation conditions, the hydrolysates of AC and AS were mainly monomers, and they transformed into Al(OH)3(am) upon their addition to algae culture, with the primary mechanism being sweep flocculation. The PAC mainly hydrolyzed to the polyaluminum compounds, which remained stable when added to the algae culture, and the flocculation mainly occurred through polyaluminum compounds. The suspension pH significantly influenced the aluminum hydrolysate and affected the flocculation between the modified clay and algae cells. Copyright © 2016 Elsevier Ltd. All rights reserved.
Energy Technology Data Exchange (ETDEWEB)
Ferreira, Heber S; Martins, Alice B; Costa, Danubia L. da; Ferreira, Heber C; Neves, Gelmires de A; Melo, Tomas J.A. de [Universidade Federal de Campina Grande (UFCG), PB (Brazil); Teixeira Neto, Erico [Universidade Federal do ABC (UFABC), Santo Andre, SP (Brazil)
2008-07-01
The organophilic clays are widely used as an agent dispersed in the composition of oil based drilling fluids. The organophilic clays are gotten from bentonite clays treated, in watery way, with ionic surfactants, that are adsorbed in the surface of interlayer of the clays, re-covered them with a organic layer. A fundamental stage of production of the organophilic clays is the dispersion of bentonite clays, in way that variables like: speed of agitation, temperature and time of cure, influences directly in plastic and apparent viscosities of these dispersions, together with other variables of organophilization process, like, temperature and time of cure of organophilization, has direct influence in efficiency of the organophilization process. This work considers a study of these variable, using bentonite clays: Brasgel PA{sup R} and Cloisite Na{sup +R}, treated with the ionic surfactant Praepagem WB{sup R}. The organophilic clays gotten had been characterized by rays X diffraction, Foster's swelling, and the results were compared with the commercial organophilic clay VG-69{sup R}, industrially treated with ionic surfactant. Viscosities plastic and apparent of the dispersions had been measured in the midst of organic dispersant diesel oil used to obtain the oil based drilling fluids. Preliminary results of Foster's swelling and preparation of fluids show that the clays have affinity with the means liquid organic dispersants, and the fluids meet specifications of PETROBRAS (N-22581-1997 and N-2259 to 1997) for use in the of diesel oil based drilling fluids. (author)
Boekel, van E.M.P.M.; Roelsma, J.; Massop, H.T.L.; Hendriks, R.F.A.; Goedhart, P.W.; Jansen, P.C.
2013-01-01
The nitrate concentrations measured in drainage water and groundwater at LMM farms (farms participating in the National Manure Policy Effects Measurement Network (LLM)) in marine clay areas have decreased with 50% since the mid-nineties. The nitrate concentrations in marine clay areas are on average
Dispersion of phyllosilicates in aqueous suspensions: role of the nature and amount of surfactant.
Houta, Nadia; Lecomte-Nana, Gisèle-Laure; Tessier-Doyen, Nicolas; Peyratout, Claire
2014-07-01
The present work aims at investigating the effect of pH values and additives on the dispersion of two 1:1 dioctahedral phyllosilicates in the presence of water. Two model clays are used for this purpose, BIP kaolin and NZCC halloysite, presenting the same surface chemistry but different morphologies. The effect of sodium hexametaphosphate, sodium silicate and sodium carbonate is discussed. Kaolin and halloysite powders were first characterized using X-ray diffraction, thermogravimetric analysis and scanning electron microscopy. Subsequently, suspensions containing 8 mass% of each clay were prepared with or without additives. Experimental measurements regarding the pH values, the zeta potential and the rheological behavior were performed to determine the most suitable additive. Results show that the conformation of halloysite particles changes regarding pH values of suspensions and is strongly related to the surface charges of these particles. At their natural pH values, halloysite and kaolin suspensions exhibit zeta potentials equal to -50 and -20 mV respectively. This trend indicates that halloysite-based suspensions are well dispersed compared to kaolin-based suspensions. Sodium hexametaphosphate is the most suitable dispersant for both clays. The rheological characterization regarding further applications in casting process indicates a shear-thinning behavior for all studied compositions. Copyright © 2014 Elsevier Inc. All rights reserved.
Kaur, A; Fanourakis, G C
2016-01-01
Knowledge of the physical properties of soils, including the clay content, is of utmost importance in the field of geotechnical engineering. The hydrometer analysis is the most widely used technique for the analysis of the particle size distribution of the fine-grained fraction of a soil, calculated using sedimentation principles. The hydrometer analysis utilises a dispersing agent - Calgon 33:7 (comprising 33 grams of sodium hexametaphosphate and 7 grams of sodium carbonate when mixed in 1 l...
Mars, clays and the origins of life
Hartman, Hyman
1989-01-01
To detect life in the Martian soil, tests were designed to look for respiration and photosynthesis. Both tests (labeled release, LR, and pyrolytic release, PR) for life in the Martian soils were positive. However, when the measurement for organic molecules in the soil of Mars was made, none were found. The interpretation given is that the inorganic constituents of the soil of Mars were responsible for these observations. The inorganic analysis of the soil was best fitted by a mixture of minerals: 60 to 80 percent clay, iron oxide, quartz, and soluble salts such as halite (NaCl). The minerals most successful in simulating the PR and LR experiments are iron-rich clays. There is a theory that considers clays as the first organisms capable of replication, mutation, and catalysis, and hence of evolving. Clays are formed when liquid water causes the weathering of rocks. The distribution of ions such as aluminum, magnesium, and iron play the role of bases in the DNA. The information was stored in the distribution of ions in the octahedral and tetrahedral molecules, but that they could, like RNA and DNA, replicate. When the clays replicated, each sheet of clay would be a template for a new sheet. The ion substitutions in one clay sheet would give rise to a complementary or similar pattern on the clay synthesized on its surface. It was theorized that it was on the surface of replicating iron-rich clays that carbon dioxide would be fixed in the light into organic acids such as formic or oxalic acid. If Mars had liquid water during a warm period in its past, clay formation would have been abundant. These clays would have replicated and evolved until the liquid water was removed due to cooling of Mars. It is entirely possible that the Viking mission detected life on Mars, but it was clay life that awaits the return of water to continue its evolution into life based on organic molecules.
Phosphonium modified clay/polyimide nanocomposites
International Nuclear Information System (INIS)
Ceylan, Hatice; Çakmakçi, Emrah; Beyler-Çiǧil, Asli; Kahraman, Memet Vezir
2014-01-01
In this study, octyltriphenylphosphonium bromide [OTPP-Br] was prepared from the reaction of triphenylphosphine and 1 -bromooctane. The modification of clay was done by ion exchange reaction using OTPP-Br in water medium. Poly(amic acid) was prepared from the reaction of 3,3',4,4'-Benzophenonetetracarboxylic dianhydride (BTDA) and 4,4'-Oxydianiline (ODA). Polyimide(PI)/clay hybrids were prepared by blending of poly(amic acid) and organically modified clay as a type of layered clays. The morphology of the Polyimide/ phosphonium modified clay hybrids was characterized by scanning electron microscopy (SEM). Chemical structures of polyimide and Polyimide/ phosphonium modified clay hybrids were characterized by FTIR. SEM and FTIR results showed that the Polyimide/ phosphonium modified clay hybrids were successfully prepared. Thermal properties of the Polyimide/ phosphonium modified clay hybrids were characterized by thermogravimetric analysis (TGA)
Viscosity and Plasticity of Latvian Illite Clays
Jurgelāne, I; Vecstaudža, J; Stepanova, V; Mālers, J; Bērziņa-Cimdiņa, L
2012-01-01
Due to viscosity and plasticity, clays and clay minerals are used in civil engineering, pottery and also in cosmetics and medicine as thickening agents and emulsion and suspension stabilizers. The rheological properties of clay suspensions are complex. Mostly it is an interaction between mineral composition, clay particle size and pH value and also depends on clay minerals. Clay-water suspension is non-Newtonian fluid showing thixotropic and pseudoplastic properties. Results showed that plast...
International Nuclear Information System (INIS)
Batool, S.
2016-01-01
Dispersion of dispersive soil occurs when it comes in contact with water and clay particles deflocculate and disperse away from each other. Thus dispersive soils undergo erosion under low seepage velocity leading to instability problems of slopes and earth retaining structures. The amount of dispersion depends upon the mineralogy and geochemistry of clayey soil as well as the dissolved salts of the pore fluid. The dispersivity of the soil mainly depends on the amount of exchangeable sodium present in its formation. Under saturated conditions, the attractive forces are less than the repulsive forces and this will help the particles to disperse and go into colloidal suspension. The use of chemical stabilizers such as lime and cement to bind the clay particles and reduce the dispersivity of soil and to improve the compaction and CBR characteristics of bauxite rich dispersive soil present in Khushab district have been studied in this research. Soil behavior was studied after addition of 2%, 4%, 6% and 8% Lime and Cement, at optimum level of 6% for Lime and Cement; it has been observed that the CBR and compaction characteristics of Khushab soil have been improved. (author)
Experimental Study on Unconfined Compressive Strength of Basalt Fiber Reinforced Clay Soil
Directory of Open Access Journals (Sweden)
Lei Gao
2015-01-01
Full Text Available In order to study the mechanism and effect of basalt fiber reinforced clay soil, a series of unconfined compressive strength tests conducted on clay soil reinforced with basalt fiber have been performed under the condition of optimum water content and maximum dry density. Both the content and length of basalt fiber are considered in this paper. When the effect of content is studied, the 12 mm long fibers are dispersed into clay soil at different contents of 0.05%, 0.1%, 0.15%, 0.20%, 0.25%, 0.30%, and 0.35%. When the effect of length is researched, different lengths of basalt fibers with 4 mm, 8 mm, 12 mm, and 15 mm are put into soil at the same content of 0.05%. Experimental results show that basalt fiber can effectively improve the UCS of clay soil. And the best content and length are 0.25% and 12 mm, respectively. The results also show that the basalt fiber reinforced clay soil has the “poststrong” characteristic. About the reinforcement mechanism, the fiber and soil column-net model is proposed in this paper. Based on this model and SEM images, the effect of fiber content and length is related to the change of fiber-soil column and formation of effective fiber-soil net.
CSIR Research Space (South Africa)
Chen, H
2014-03-01
Full Text Available SU-8/Clay nanocomposite is considered as a candidate material for microcantilever sensor fabrication. Organically modified montmorillonite clay nanoparticles are dispersed in the universally used negative photoresist polymer SU-8, for a low cost...
New test for oil soluble/water dispersible gas pipeline inhibitors
Energy Technology Data Exchange (ETDEWEB)
Stegmann, D.W.; Asperger, R.G.
1987-01-01
The wheel test provides good mixing of the condensate and water phases, the coupons are exposed to both phases. Therefore, the wheel test cannot distinguish between inhibitors that need continuous mixing of the these phases to maintain a water dispersion of the inhibitor and inhibitors that will self disperse into the water. This concept becomes important for pipelines in stratified flow where the water can settle out. In these cases with low turbulence, the inhibitor must self disperse into the water to be effective. The paper describes a test method to measure the effectiveness of an inhibitor and its ability to self disperse. The effectiveness of several inhibitors as predicted by the new test method is discussed relative to data from the wheel test and breaker tests. Field performance of these inhibitors in a gas gathering line, with liquids in stratified flow, are cities and compared with the results of the various laboratory tests.
Structural characterization of clays commercially used in red ceramics
International Nuclear Information System (INIS)
Brito, E.M.; Moura, J.K.L.; Souza, R.B.; Brandim, A.S.
2014-01-01
The use of clays hills being an alternative to clay floodplain, due to environmental protection laws. The research project aims at the morphological and chemical characterization of hills clays used industrially for the production of ceramic tiles and blocks. Therefore, two types of methods were known commercially in the region of Teresina-PI through diffraction of X-rays (X-DR), scanning electron microscopy (SEM) and energy dispersive spectrometry X-ray (EDS). It can be observed that the samples have a high percentage of quartz, hematite still having in its constitution aluminum oxide, zirconium oxide and titanium oxide. The results show that the clays are clays and montmorillonites may be used for the production of ceramic tiles and blocks, but as the proportion of using the same will be focusing the next job. (author)
Clay based polymeric composites: Preparation and quality characterization
International Nuclear Information System (INIS)
Aloisi, G.G.; Elisei, F.; Nocchetti, M.; Camino, G.; Frache, A.; Costantino, U.; Latterini, L.
2010-01-01
Commercial clays Cloisites Na + , 30B and 20A were labelled with the fluorescent dye Rhodamine B and used as fillers of polypropylene in order to prepare composites to be studied with confocal fluorescence microscopy. The dye uptake by clays was monitored by X-ray powder diffraction and spectroscopic analyses and clear evidences of intercalated dye in the organically modified montmorillonites Clo30B and Clo20A were obtained. Clay-Rhodamine B hybrids were investigated by steady-state absorption and emission spectroscopy to explore the effect of dye arrangement on the optical properties. The obtained information was used to rationalize fluorescence behaviour of composites. Confocal fluorescence imaging gave rise to bright fluorescent images of Cloisite aggregated labelled with the dye allowing to easily and directly visualize the 3-D dispersion of the labelled fillers in the polymer matrix in a non-invasive manner. The images were analyzed in terms of size distribution of the fluorescence grains to quantify the dispersion degree. The data indicate that Clo20A is able to homogeneously distribute in the polymer matrix forming a composite material.
Characterization and analysis of epoxy/clay nanotubes composites
International Nuclear Information System (INIS)
Sene, Tarcisio S.; Kock, Thyago; Coelho, Luiz A.F.; Becker, Daniela
2011-01-01
An DGEBA epoxy matrix was used aiming to achieve a nanocomposite material, through the dispersion of (CNT) via mechanical stirring followed by sonication. In this work the following characterization were performed: mechanical characterization, differential scanning calorimetry (DSC), wide angle X-ray diffraction (WXRD) and scanning electron microscopy (SEM). The addition of CNT and modified clays promoted the increase of modulus of the epoxy matrix, and a synergistic effect between CNT and both clays could be presumed. SEM images of the fracture surface show the difference between the fracture surface area and the presence of clusters among the samples, allowing a correlation with the modulus of elasticity. X-ray diffractograms from 2Θ = 5 deg showed no peaks for modified clay samples, however it is possible to affirm that modified clay platelets are forming a less organized structure compared to the structure of the clay as natural in epoxy. (author)
International Nuclear Information System (INIS)
Aroui, L.; Zerroual, L.; Boutahala, M.
2012-01-01
Graphical abstract: The replacement of Na by Pb in the interlayer space of the smectite leads to a decrease in the intensity of the the (0 0 1) reflection as the concentration of lead nitrate increases. A significant restructuring at the particle scale is observed leading probably to the exfoliation of the caly. In addition, the thermal behaviour of the montmorillonite samples with regard to their dehydration and dehydroxilation capacities is significantly influenced. This leads to a lowering of the water content and a decrease in the ionic conductivity of the clay. Highlights: ► In the clay, Pb replaces Na ions and a significant restructuring at the particle scale is observed. ► Pb influenced significantly the thermal behaviour of the clay with regard to its dehydration. ► In the interlayer space, the exchange of Na by Pb leads to a decrease in the protonic conductivity. ► A PbO 2 -clay nanocomposite material with good conductivity is synthesized. -- Abstract: The aim of this paper is to present the results obtained with Pb(II) sorption on an Algerian Clay. The experiments were carried out using a batch process. Powder X-rays diffraction patterns (PXRD) prove that in the montmorillonite Pb replaces Na ions. A significant restructuring at the particle scale is observed leading to the disappearance of the d 001 reflection of the clay at high concentrations of lead. The replacement of hydrated Na with Pb ions influenced significantly the thermal behaviour of the montmorillonite samples with regard to their dehydration and dehydroxilation capacities with a lowering of the water content. A PbO 2 -clay composite material with good electrical conductivity is synthesized.
Energy Technology Data Exchange (ETDEWEB)
Ferreira, Heber S.; Martins, Alice B.; Costa, Danubia L. da; Ferreira, Heber C.; Neves, Gelmires de A.; Melo, Tomas J.A. de [Universidade Federal de Campina Grande (UFCG), PB (Brazil); Teixeira Neto, Erico [Universidade Federal do ABC (UFABC), Santo Andre, SP (Brazil)
2008-07-01
The organophilic clays are widely used as an agent dispersed in the composition of oil based drilling fluids. The organophilic clays are gotten from bentonite clays treated, in watery way, with ionic surfactants, that are adsorbed in the surface of interlayer of the clays, re-covered them with a organic layer. A fundamental stage of production of the organophilic clays is the dispersion of bentonite clays, in way that variables like: speed of agitation, temperature and time of cure, influences directly in plastic and apparent viscosities of these dispersions, together with other variables of organophilization process, like, temperature and time of cure of organophilization, has direct influence in efficiency of the organophilization process. This work considers a study of these variable, using bentonite clays: Brasgel PA{sup R} and Cloisite Na{sup +R}, treated with the ionic surfactant Praepagem WB{sup R}. The organophilic clays gotten had been characterized by rays X diffraction, Foster's swelling, and the results were compared with the commercial organophilic clay VG-69{sup R}, industrially treated with ionic surfactant. Viscosities plastic and apparent of the dispersions had been measured in the midst of organic dispersant diesel oil used to obtain the oil based drilling fluids. Preliminary results of Foster's swelling and preparation of fluids show that the clays have affinity with the means liquid organic dispersants, and the fluids meet specifications of PETROBRAS (N-22581-1997 and N-2259 to 1997) for use in the of diesel oil based drilling fluids. (author)
Power ultrasound effects for in situ compatibilization of polymer-clay nanocomposites
International Nuclear Information System (INIS)
Ryu, Joung Gul; Park, Sang Wan; Kim, Hyungsu; Lee, Jae Wook
2004-01-01
Polymer-clay nanocomposites of various concentrations were prepared by ultrasonically assisted polymerization and melt mixing processes. The sonication process using power ultrasonic wave was employed to enhance nano-scale dispersion during melt mixing of monomer, polymer and organically modified clay. According to the unique mode of power ultrasound wave, we expected enhanced breakup of layered silicate bundle and further reduction in the size of dispersed phase with better homogeneity compared to the in situ polymerization. The optimum conditions to perform stable exfoliated nanocomposites were studied by various compositions and conditions. Dispersion characteristics and morphology of the nanocomposites were verified by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Rheological behaviors were measured under dynamic frequency sweep mode using Rheometric science ARES
In situ analysis of microbial reduction of a nitrate plume in Opalinus clay
International Nuclear Information System (INIS)
Bleyen, N.; Smets, S.; Valcke, E.; Albrecht, A.; De Canniere, P.; Schwyn, B.; Wittebroodt, C.
2012-01-01
Document available in extended abstract form only. In several countries, such as Belgium, France and Switzerland, clay formations are foreseen as the host rock for geological disposal of bituminized low-level and intermediate-level long-lived radioactive waste. Suitable clay formations exhibit favorable hydro-mechanical and geochemical characteristics, which are expected to retard the migration of leached radionuclides. Along with radionuclides, certain classes of bituminized radioactive waste may also contain high concentrations of NaNO 3 , dispersed into the hydrophobic bitumen matrix used to stabilize the waste. During and after saturation of the disposal gallery, this bituminized waste will start to take up water due to osmosis, resulting in the leaching of significant amounts of NaNO 3 and soluble organic bitumen degradation products (BDP) into the clay pore water. This nitrate plume could cause several geochemical and biochemical processes in the clay surrounding the waste disposal gallery, potentially affecting the barrier function of the host rock. To study these processes, an in situ experiment in the Opalinus Clay, named the Bitumen-Nitrate-Clay interaction (BN) experiment, is being performed at the Mont Terri Rock Laboratory (CH). The experiment consists of a vertical borehole rigged with a downhole equipment containing three packed-off intervals, each lined with a cylindrical sintered stainless steel filter screen to allow contact with the surrounding clay. Prior to the start of the tests, the intervals were injected with an artificial Opalinus Clay pore water, containing all major ions at pore water concentrations at Mont Terri, but no organic matter, and were equilibrated with the surrounding clay for ∼8 months. To ensure a continuous water flow during the tests, each interval is connected to a stainless steel water circulation unit, equipped with water sampling containers, circulation pumps and flow meters. In addition, to continuously monitor the
Performance of Kaolin Clay on the Concrete Pavement
Abdullah, M. E.; Jaya, R. P.; Shahafuddin, M. N. A.; Yaacob, H.; Ibrahim, M. H. Wan; Nazri, F. M.; Ramli, N. I.; Mohammed, A. A.
2018-05-01
This paper investigates the performance of concrete pavement containing kaolin clay with their engineering properties and to determine the optimum kaolin clay content. The concrete used throughout the study was designed as grade 30 MPa strength with constant water to cement ratio of 0.49. The compressive strength, flexural strength and water absorption test was conducted in this research. The concrete mix designed with kaolin clay as cement replacement comprises at 0%, 5%, 10% and 15% by the total weight of cement. The results indicate that the strength of pavement concrete decreases as the percentage of kaolin clay increases. It also shows that the water absorption increases with the percentage of cement replacement. However, 5% kaolin clay is found to be the optimum level to replace cement in a pavement concrete.
Disinfection of water with new chitosan-modified hybrid clay composite adsorbent
Directory of Open Access Journals (Sweden)
Emmanuel I. Unuabonah
2017-08-01
Full Text Available Hybrid clay composites were prepared from Kaolinite clay and Carica papaya seeds via modification with chitosan, Alum, NaOH, and ZnCl2 in different ratios, using solvothermal and surface modification techniques. Several composite adsorbents were prepared, and the most efficient of them for the removal of gram negative enteric bacteria was the hybrid clay composite that was surface-modified with chitosan, Ch-nHYCA1:5 (Chitosan: nHYCA = 1:5. This composite adsorbent had a maximum adsorption removal value of 4.07 × 106 cfu/mL for V. cholerae after 120 min, 1.95 × 106 cfu/mL for E. coli after ∼180 min and 3.25 × 106 cfu/mL for S. typhi after 270 min. The Brouers-Sotolongo model was found to better predict the maximum adsorption capacity (qmax of Ch-nHYCA1:5 composite adsorbent for the removal of E. coli with a qmax of 103.07 mg/g (7.93 × 107 cfu/mL and V. cholerae with a qmax of 154.18 mg/g (1.19 × 108 cfu/mL while the Sips model best described S. typhi adsorption by Ch-nHYCA1:5 composite with an estimated qmax of 83.65 mg/g (6.43 × 107 cfu/mL. These efficiencies do far exceed the alert/action levels of ca. 500 cfu/mL in drinking water for these bacteria. The simplicity of the composite preparation process and the availability of raw materials used for its preparation underscore the potential of this low-cost chitosan-modified composite adsorbent (Ch-nHYCA1:5 for water treatment.
Electrochemical masstransfer of oil hydrocarbons in dispersed soils
Energy Technology Data Exchange (ETDEWEB)
Nekrasova, M.A.; Zvolinsky, V.P.; Kanev, M.V. [Russian Friendship Peoples Univ., Dept. of Eecological Monitoring and Forecasting, Moscow (Russian Federation)
2001-07-01
A large-scale pollution of the geological environment is a result of imperfect processes of mining, refining, haul of oil and irrational use of petroleum. The processes of masstransfer of hydrocarbons in dispersed soils and the problems of forming of a dual electric layer (DEL) on the demarcations 'water-oil' and 'mineral-water' are still insufficiently studied. Therefore, one of the most important problems in the field of the ecological geology is the analysis of ways of cleaning of soils from hydrocarbons. The kaolinitic clay from the Tirlianskoye deposit (K{sub 2}, st. Jabik, Bashkiria) and average polymineral loam (prlllkl, Moscow region, the south-east of town Zvenigorod) was chosen as the objects of the experimental study. The mixture of West Siberian oils was used for model pollution. The experimental laboratory researches of electrochemical migration of hydrocarbons were carried out on dispersiblis clayey soils. (orig.)
Iodide uptake by negatively charged clay interlayers?
International Nuclear Information System (INIS)
Miller, Andrew; Kruichak, Jessica; Mills, Melissa; Wang, Yifeng
2015-01-01
Understanding iodide interactions with clay minerals is critical to quantifying risk associated with nuclear waste disposal. Current thought assumes that iodide does not interact directly with clay minerals due to electrical repulsion between the iodide and the negatively charged clay layers. However, a growing body of work indicates a weak interaction between iodide and clays. The goal of this contribution is to report a conceptual model for iodide interaction with clays by considering clay mineral structures and emergent behaviors of chemical species in confined spaces. To approach the problem, a suite of clay minerals was used with varying degrees of isomorphic substitution, chemical composition, and mineral structure. Iodide uptake experiments were completed with each of these minerals in a range of swamping electrolyte identities (NaCl, NaBr, KCl) and concentrations. Iodide uptake behaviors form distinct trends with cation exchange capacity and mineral structure. These trends change substantially with electrolyte composition and concentration, but do not appear to be affected by solution pH. The experimental results suggest that iodide may directly interact with clays by forming ion-pairs (e.g., NaI (aq) ) which may concentrate within the interlayer space as well as the thin areas surrounding the clay particle where water behavior is more structured relative to bulk water. Ion pairing and iodide concentration in these zones is probably driven by the reduced dielectric constant of water in confined space and by the relatively high polarizability of the iodide species. - Highlights: • Iodide sorption experiments were completed with a diverse array of clay minerals. • Iodide uptake trended with CEC and swamping electrolyte identity and concentration. • Results can be explained by considering the formation of ion pairs in clay interlayers
Environmental Degradation and Durability of Epoxy-Clay Nanocomposites
Directory of Open Access Journals (Sweden)
Raman P. Singh
2010-01-01
Full Text Available This experimental investigation reports on the durability of epoxy-clay nanocomposites upon exposure to multiple environments. Nanocomposites are fabricated by mixing the clay particles using various combinations of mechanical mixing, high-shear dispersion, and ultrasonication. Clay morphology is characterized using X-ray diffraction and transmission electron microscopy. Specimens of both neat epoxy and the epoxy-clay nanocomposite are subjected to two environmental conditions: combined UV radiation and condensation on 3-hour repeat cycle and constant temperature-humidity, for a total exposure duration of 4770 hours. The presence of nanoscale clay inhibits moisture uptake, as demonstrated by exposure to constant temperature-humidity. Nonetheless, both materials lose mass under exposure to combined UV radiation and condensation due to the erosion of epoxy by a synergistic process. Surprisingly, the epoxy-clay specimens exhibit greater mass loss, as compared to neat epoxy. Mechanical testing shows that either environment does not significant affect the flexure modulus of either material. On the other hand, both materials undergo degradation in flexural strength when exposed to either environment. However, the epoxy-clay nanocomposite retains 37% more flexure strength than the neat epoxy after 4072 hours of exposure.
Environmental Degradation and Durability of Epoxy-Clay Nanocomposites
International Nuclear Information System (INIS)
Singh, R.P.; Zunjarrao, S.C.; Pandey, G.; Khait, M.; Korach, C.S.
2010-01-01
This experimental investigation reports on the durability of epoxy-clay nanocomposites upon exposure to multiple environments. Nanocomposites are fabricated by mixing the clay particles using various combinations of mechanical mixing, high-shear dispersion, and ultrasonication. Clay morphology is characterized using X-ray diffraction and transmission electron microscopy. Specimens of both neat epoxy and the epoxy-clay nanocomposite are subjected to two environmental conditions: combined UV radiation and condensation on 3-hour repeat cycle and constant temperature-humidity, for a total exposure duration of 4770 hours. The presence of nanoscale clay inhibits moisture uptake, as demonstrated by exposure to constant temperature-humidity. Nonetheless, both materials lose mass under exposure to combined UV radiation and condensation due to the erosion of epoxy by a synergistic process. Surprisingly, the epoxy-clay specimens exhibit greater mass loss, as compared to neat epoxy. Mechanical testing shows that either environment does not significant affect the flexure modulus of either material. On the other hand, both materials undergo degradation in flexural strength when exposed to either environment. However, the epoxy-clay nanocomposite retains 37% more flexure strength than the neat epoxy after 4072 hours of exposure.
Influence of clay and surfactant content in non-aqueous fluid rheology
International Nuclear Information System (INIS)
Guedes, I.C.; Gomes, N.L.; Menezes, R.R.; Campos, L.F.A.; Ferreira, H.S.
2012-01-01
The bentonite clay used as viscosity agent in the production of non-aqueous fluids cannot be used without organic treatment for their surfaces to become hydrophobic. These clays are called organophilic clays, and are generally obtained by adding, in an aqueous way, ionic or a nonionic surfactant. Recent studies of the variables involved in the dispersion of bentonite clays and in the process of organophilization, showed their lack of influence. This work aims to study the influence of clay content and surfactants on the rheology of nonaqueous fluids. To this end, the clays were treats and characterized, evidencing the incorporation of the surfactant, and then formulated non-aqueous fluids, following PETROBRAS standards, being possible to verify the influence of clay content and surfactant both from the point of view as the characterizing and rheological behavior. (author)
Iodide uptake by negatively charged clay interlayers?
Miller, Andrew; Kruichak, Jessica; Mills, Melissa; Wang, Yifeng
2015-09-01
Understanding iodide interactions with clay minerals is critical to quantifying risk associated with nuclear waste disposal. Current thought assumes that iodide does not interact directly with clay minerals due to electrical repulsion between the iodide and the negatively charged clay layers. However, a growing body of work indicates a weak interaction between iodide and clays. The goal of this contribution is to report a conceptual model for iodide interaction with clays by considering clay mineral structures and emergent behaviors of chemical species in confined spaces. To approach the problem, a suite of clay minerals was used with varying degrees of isomorphic substitution, chemical composition, and mineral structure. Iodide uptake experiments were completed with each of these minerals in a range of swamping electrolyte identities (NaCl, NaBr, KCl) and concentrations. Iodide uptake behaviors form distinct trends with cation exchange capacity and mineral structure. These trends change substantially with electrolyte composition and concentration, but do not appear to be affected by solution pH. The experimental results suggest that iodide may directly interact with clays by forming ion-pairs (e.g., NaI(aq)) which may concentrate within the interlayer space as well as the thin areas surrounding the clay particle where water behavior is more structured relative to bulk water. Ion pairing and iodide concentration in these zones is probably driven by the reduced dielectric constant of water in confined space and by the relatively high polarizability of the iodide species. Copyright © 2015 Elsevier Ltd. All rights reserved.
Water-dispersible nanoparticles via interdigitation of sodium ...
Indian Academy of Sciences (India)
Unknown
Abstract. This paper describes the formation of water-dispersible gold nano- particles capped with a bilayer of sodium dodecylsulphate (SDS) and octadecylamine. (ODA) molecules. Vigorous shaking of a biphasic mixture consisting of ODA-capped gold nanoparticles in chloroform and SDS in water results in the rapid ...
Study of smectite clays of the city Pedra Lavrada - PB for use in water-based drilling fluids
International Nuclear Information System (INIS)
Silva, I.A. da; Costa, J.M.R.; Cardoso, M.A.F.; Neves, G.A.; Ferreira, H.C.
2011-01-01
Paraiba has large reserves of bentonite clays, with the largest deposits in Boa Vista, PB. Recently new deposits were discovered in the cities of Cubati and Pedra Lavrada-PB, creating great expectations for further expansion of reserves for industrial production. The aim of this work is the study of smectite clays from the city of Pedra Lavrada, PB for use in drilling fluids water based. The characterization was made by the diffraction of laser (AG), thermogravimetric and differential thermal analysis (TGA and DTA), chemical composition by X-ray fluorescence (EDX), X-ray diffraction (XRD), exchange capacity of cations (ECC) and surface area (SA). The results obtained so far showed that the samples presented at its mineral composition smectite, kaolinite and quartz. In relation to rheological properties showed that the bentonite clay sample Dark presents promising features for use in water based drilling fluids. (author)
DEFF Research Database (Denmark)
Manoli, Gabriele; Chambon, Julie Claire Claudia; Christiansen, Camilla Maymann
2010-01-01
with interspersed sand lenses and stringers. The transport model couples diffusion dominated transport in the clay matrix, with advective‐dispersive transport in the fractures and higher permeability sand lenses. The reactive model calculates sequential reductive dechlorination of TCE (trichloroethylene) to its...... a contamination of trichloroethylene located in a fractured clay till. The site is simulated using the model developed. Fracture geometry, site parameters and degradation rates are based on observations from the site and lab studies. The risk for drinking water is assessed and cleanup times are simulated using...
Water states and types of water in materials from different argillaceous formations
International Nuclear Information System (INIS)
Fernandez, A.M.; Melon, A.
2010-01-01
Document available in extended abstract form only. Depending of their structure and degree of compaction, clays can be hydrated by a variable amount of water molecules in the inter-lamellar space and on external surfaces. Due to the fact that the structure and nature of water molecules (properties of liquid water) is influenced by the clay surfaces; different types of waters are involved in clayey systems (internal/external water, adsorbed/free water) giving a double porosity structure. The water volume accessible to ions is a key parameter in order to determine the pore water chemistry affecting the radionuclide transport in clay-rocks. In the case of argillaceous formations, natural consolidation induces significant physical and structural changes to clays as a function of time, leading to a progressive compaction and agglomeration of particles, reduction of crystallinity and an increase of micro-strain, which affects both the tetrahedral and octahedral layers. Structure and dynamics of water are modified when water molecules are close to interfaces or confined in porous spaces. At high degrees of compaction, the diffusive transport of the solvated ions and the solvent molecules in clays is substantially retarded compared with the free electrolyte solution because of the surface complexation of ions and the strong ordering of solvent molecules at the solid-liquid interface. Besides, mud-rocks contain a variable amount of different types of clays, such as illite, kaolinite, chlorites, smectite and illite/smectite mixed layers; as well as other main and accessory minerals which influence also the amount of water adsorbed and types of waters in these systems. Structural and dynamic properties of water confined among basal planes of clays have been extensively studied by means of water adsorption isotherms, neutron scattering, molecular dynamics (MD) and Monte- Carlo simulations. However, most of the works are related to purified clays and dispersed systems. In real
Piri, Somayeh; Zanjani, Zahra Alikhani; Piri, Farideh; Zamani, Abbasali; Yaftian, Mohamadreza; Davari, Mehdi
2016-01-01
Nowadays significant attention is to nanocomposite compounds in water cleaning. In this article the synthesis and characterization of conductive polyaniline/clay (PANI/clay) as a hybrid nanocomposite with extended chain conformation and its application for water purification are presented. Clay samples were obtained from the central plain of Abhar region, Abhar, Zanjan Province, Iran. Clay was dried and sieved before used as adsorbent. The conductive polyaniline was inflicted into the layers of clay to fabricate a hybrid material. The structural properties of the fabricated nanocomposite are studied by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscope (SEM). The elimination process of Pb(II) and Cd(II) ions from synthetics aqueous phase on the surface of PANI/clay as adsorbent were evaluated in batch experiments. Flame atomic absorption instrument spectrophotometer was used for determination of the studied ions concentration. Consequence change of the pH and initial metal amount in aqueous solution, the procedure time and the used adsorbent dose as the effective parameters on the removal efficiency was investigated. Surface characterization was exhibited that the clay layers were flaked in the hybrid nanocomposite. The results show that what happen when a nanocomposite polyaniline chain is inserted between the clay layers. The adsorption of ions confirmed a pH dependency procedure and a maximum removal value was seen at pH 5.0. The adsorption isotherm and the kinetics of the adsorption processes were described by Temkin model and pseudo-second-order equation. Time of procedure, pH and initial ion amount have a severe effect on adsorption efficiency of PANI/clay. By using suggested synthesise method, nano-composite as the adsorbent simply will be prepared. The prepared PANI/clay showed excellent adsorption capability for decontamination of Pb ions from contaminated water. Both of suggested synthesise and
Memory effect of polymer dispersed liquid crystal by hybridization with nanoclay
Directory of Open Access Journals (Sweden)
2010-01-01
Full Text Available The electro-optical performances of polymer dispersed liquid crystal (PDLC were investigated in the presence of organically modified clays. With the addition and increasing amount of modified clay, driving voltage and memory effect, viz. transparent state of the film after the electricity is off simultaneously increased due most likely to the increased viscosity. Among the two types of modifier, 4-(4-aminophenyl benzonitrile having greater chemical affinity with LC than hexylamine, gave finer dispersion of clay in liquid crystal, greater viscosity, larger driving voltage and response time, and greater memory effect.
Effects of varied porosity on the physic-mechanical properties of sintered ceramic from Ifon clay
Directory of Open Access Journals (Sweden)
Fatai Olufemi ARAMIDE
2017-12-01
Full Text Available The effects of saw dust admixture on the physic-mechanical properties of sintered clay bonded carbonized palm kernel shell ceramic was investigated. Composite mixtures of powdered carbonized palm kernel shell and clay from Ifon deposit were produced using equal amount of clay and carbonized palm kernel shell. These were then mixed with varied amount of saw dust (0%, 5% and 10% in a ball mill for 6 hours. From this standard sample specimens were produced using uniaxial compression after mixing each mixture with 10% moisture of clay contents. The compressed samples were sintered at 9500C and soaked for one hour. The sintered samples were characterized for various physic-mechanical properties using state of the art equipment’s. The fired samples were also characterized using ultra-high-resolution field emission scanning electron microscope (UHR-FEGSEM equipped with energy dispersive spectroscopy (EDX. It was observed that the apparent porosity and water absorption of the clay bonded carbonized palm kernel shell ceramic increased with increased amount of saw dust admixture, cold crushing strength, Young’ modulus of elasticity and absorbed energy of the sample reduced with increased amount of saw dust admixture. It was concluded that the sample with 0% saw dust admixture is judged to possess optimum physic-mechanical properties.
Studies on structural properties of clay magnesium ferrite nano composite
Energy Technology Data Exchange (ETDEWEB)
Kaur, Manpreet, E-mail: manpreetchem@pau.edu; Singh, Mandeep [Department of Chemistry, Punjab Agricultural University, Ludhiana-141004 (India); Jeet, Kiran, E-mail: kiranjeet@pau.edu; Kaur, Rajdeep [Electron Microscopy and Nanoscience Laboratory, Punjab Agricultural University, Ludhiana-141004 (India)
2015-08-28
Magnesium ferrite-bentonite clay composite was prepared by sol-gel combustion method employing citric acid as complexing agent and fuel. The effect of clay on the structural properties was studied with X-ray diffraction (XRD), Fourier transform infrared (FT-IR) Spectroscopy, Scanning electron microscopy (SEM), SEM- Energy dispersive Spectroscope (EDS) and BET surface area analyzer. Decrease in particle size and density was observed on addition of bentonite clay. The BET surface area of nano composite containing just 5 percent clay was 74.86 m{sup 2}/g. Whereas porosity increased from 40.5 per cent for the pure magnesium ferrite to 81.0 percent in the composite showing that nano-composite has potential application as an adsorbent.
International Nuclear Information System (INIS)
Silva, I.A.; Costa, J.M.R.; Neves, G.A.; Ferreira, H.C.; Ferreira, H.S.
2010-01-01
The use of nonionic surfactants has been replacing the traditional ionic surfactants among others by its high potential for resistance to thermal degradation. This work aims at the development of organoclay by the addition of nonionic surfactants for use in drilling fluids for oil wells based oil. The bentonite clay was organophilized and then characterized by X-ray diffraction and swelling Foster, seeking the most appropriate choice of surfactant to liquid organic dispersing media: ester, diesel and paraffin. With the obtained dispersions were measured apparent viscosities and plastic. The results showed that incorporation of surfactants used in the clay interlayer spacing increased significantly and that the dispersions showed rheological properties within the specifications of PETROBRAS, for the use of organophilic clays in drilling fluids in a non-aqueous base. (author)
Modification of clay-based waste containment materials
International Nuclear Information System (INIS)
Adu-Wusu, K.; Whang, J.M.; McDevitt, M.F.
1997-01-01
Bentonite clays are used extensively for waste containment barriers to help impede the flow of water in the subsurface because of their low permeability characteristics. However, they do little to prevent diffusion of contaminants, which is the major transport mechanism at low water flows. A more effective way of minimizing contaminant migration in the subsurface is to modify the bentonite clay with highly sorptive materials. Batch sorption studies were conducted to evaluate the sorptive capabilities of organo-clays and humic- and iron-based materials. These materials proved to be effective sorbents for the organic contaminants 1,2,4-trichlorobenzene, nitrobenzene, and aniline in water, humic acid, and methanol solution media. The sorption capacities were several orders of magnitude greater than that of unmodified bentonite clay. Modeling results indicate that with small amounts of these materials used as additives in clay barriers, contaminant flux through walls could be kept very small for 100 years or more. The cost of such levels of additives can be small compared to overall construction costs
Ray, Sudip; Bhowmick, Anil K.; Sarma, K. S. S.; Majali, A. B.; Tikku, V. K.
2002-12-01
A novel process of surface modification of clay filler has been developed by coating this with an acrylate monomer, trimethylol propane triacrylate (TMPTA) or a silane coupling agent, triethoxy vinyl silane (TEVS) followed by electron beam irradiation. Characterization of these surface modified fillers has been carried out by Fourier-transform infrared analysis (FTIR), electron spectroscopy for chemical analysis (ESCA), wettability by dynamic wicking method measuring the rise of a liquid through a filler-packed capillary tube and water flotation test, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), thermogravimetric analysis (TGA), and X-ray diffraction (XRD). Presence of the acrylate and the silane coupling agent on the modified fillers has been confirmed from FTIR, ESCA, and EDX studies, which has also been supported by TGA studies. The contact angle measurement by dynamic wicking method suggests improvement in hydrophobicity of the treated fillers, which is supported by water flotation test especially in the case of silanized clay. However, XRD studies demonstrate that the entire modification process does not affect the bulk properties of the fillers. Finally, both unmodified and modified clay fillers have been incorporated in styrene butadiene rubber (SBR) and nitrile rubber (NBR). Rheometric and mechanical properties reveal that there is a definite improvement using these modified fillers specially in the case of silanized clay compared to the control sample, probably due to successful enhancement in interaction between the treated clay and the base polymer.
International Nuclear Information System (INIS)
Ray, Sudip; Bhowmick, Anil K.; Sarma, K.S.S.; Majali, A.B.; Tikku, V.K.
2002-01-01
A novel process of surface modification of clay filler has been developed by coating this with an acrylate monomer, trimethylol propane triacrylate (TMPTA) or a silane coupling agent, triethoxy vinyl silane (TEVS) followed by electron beam irradiation. Characterization of these surface modified fillers has been carried out by Fourier-transform infrared analysis (FTIR), electron spectroscopy for chemical analysis (ESCA), wettability by dynamic wicking method measuring the rise of a liquid through a filler-packed capillary tube and water flotation test, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), thermogravimetric analysis (TGA), and X-ray diffraction (XRD). Presence of the acrylate and the silane coupling agent on the modified fillers has been confirmed from FTIR, ESCA, and EDX studies, which has also been supported by TGA studies. The contact angle measurement by dynamic wicking method suggests improvement in hydrophobicity of the treated fillers, which is supported by water flotation test especially in the case of silanized clay. However, XRD studies demonstrate that the entire modification process does not affect the bulk properties of the fillers. Finally, both unmodified and modified clay fillers have been incorporated in styrene butadiene rubber (SBR) and nitrile rubber (NBR). Rheometric and mechanical properties reveal that there is a definite improvement using these modified fillers specially in the case of silanized clay compared to the control sample, probably due to successful enhancement in interaction between the treated clay and the base polymer
DEFF Research Database (Denmark)
Chakraborti, Michelle; Jackson, John K.; Plackett, David
2012-01-01
and quantitation of the unbound fraction by UV/Vis absorbance or HPLC analysis. Drug release from layered double hydroxide clay/drug complexes dispersed in polymeric films was measured by incubation in phosphate-buffered saline (pH 7.4) at 37 °C using absorbance or HPLC analysis. Antimicrobial activity of drug......Many sites of bacterial infection such as in-dwelling catheters and orthopedic surgical sites require local rather than systemic antibiotic administration. However, currently used controlled release vehicles, such as polymeric films, release water-soluble antibiotics too quickly, whereas nonporous...... released from film composites was determined using zonal inhibition studies against S. epidermidis. All drugs bound to the clay particles to various degrees. Generally, drugs released with a large burst phase of release (except DOX) with little further drug release after 4 days. Dispersion of drug...
Paumier, S; Pantet, A; Monnet, P
2008-09-01
Smectites are swelling clay materials with pronounced colloidal properties that are widely used in industry. These properties originate in the electrokinetic properties of the smectite layers and their linkage capacities. Thin layers may be dispersed or aggregated according to many parameters, such as concentration, particle size and morphology, exchangeable cation nature and chemical environment (pH, ionic strength). The literature usually provides general rules, like the sodium dispersion contains a lot of small units whereas the calcium dispersion contains a few large units. A volume of water molecules bound to the clay surface is considered as the immobile water phase that behaves like the solid phase obstructing the flow. The water immobilized around layers and trapped inside aggregates cannot participate to the flow. In this study, we evaluated the volume occupied by calcium and sodium units inside the dispersion containing the immobile water phase. First, the smectite was cautiously extracted from a raw bentonite and its physicochemical properties were determined. A large quantity of extracted and saturated smectite (Na-smectite and Ca-smectite) was obtained. Second, the unit size and a shape factor for each sample were evaluated using granulometry and scanning transmission electron microscopy on wet samples (Wet STEM) and some flow curves. Na-smectite dispersions contain 0.13 microm(2) surface units with a shape factor of 50. Ca-smectite dispersions contain 0.32 microm(2) surface units with a shape factor of 3.3. Finally, rheometry allowed us to evaluate the unit occupancy using an adaptation of the Krieger-Dougherty law. We used shape factors and evaluated the concentration from which the entire immobile volume was connected (6.4% for Na-smectite and 11.9% for Ca-smectite). This study explains the evolution of flow properties with increasing concentrations by the evolution of layer interactions at the microscopic scale for homoionic smectite particles in
Geotechnical properties of Karwar marine clay
Digital Repository Service at National Institute of Oceanography (India)
Bhat, S.T.; Nayak, B.U.; Naik, R.L.
Karwar marine clay possesses high plasticity characteristics with natural water content higher than the liquid limit. Liquidity index was as high as 1.7. Predominant clay mineral was kaolinite. Undrained shear strength showed an increasing trend...
International Nuclear Information System (INIS)
Zulfiqar, Sonia; Ahmad, Zahoor; Ishaq, Muhammad; Sarwar, Muhammad Ilyas
2009-01-01
New type of aromatic-aliphatic polyamide/montmorillonite nanocomposites were produced using solution intercalation technique in dimethylacetamide. The modification of clay was carried out with ammonium salt of long chain alkyl amine. The nanocomposites were probed for organoclay dispersion, mechanical, thermal and water absorption measurements. Formation of delaminated and intercalated nanostructures was confirmed by X-ray diffraction and TEM studies. Improvement in tensile strength and modulus was observed for nanocomposites with optimum organoclay content (8-wt.%). Thermogravimetric analysis indicated an increase in thermal stability of nanocomposites as compared to pristine polyamide. Differential scanning calorimetric results revealed increase in glass transition temperatures (T g ) with augmenting organoclay in the nanocomposites. Water uptake of the nanocomposites reduced than the neat polyamide rendering decreased permeability.
Energy Technology Data Exchange (ETDEWEB)
Zulfiqar, Sonia [Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan); Ahmad, Zahoor [Department of Chemistry, Faculty of Science, Kuwait University, P. O. Box: 5969, Safat 13060 (Kuwait); Ishaq, Muhammad [Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan); Sarwar, Muhammad Ilyas, E-mail: ilyassarwar@hotmail.com [Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan); Department of Materials Science and Engineering, University of Delaware, Newark, DE 19716 (United States)
2009-11-15
New type of aromatic-aliphatic polyamide/montmorillonite nanocomposites were produced using solution intercalation technique in dimethylacetamide. The modification of clay was carried out with ammonium salt of long chain alkyl amine. The nanocomposites were probed for organoclay dispersion, mechanical, thermal and water absorption measurements. Formation of delaminated and intercalated nanostructures was confirmed by X-ray diffraction and TEM studies. Improvement in tensile strength and modulus was observed for nanocomposites with optimum organoclay content (8-wt.%). Thermogravimetric analysis indicated an increase in thermal stability of nanocomposites as compared to pristine polyamide. Differential scanning calorimetric results revealed increase in glass transition temperatures (T{sub g}) with augmenting organoclay in the nanocomposites. Water uptake of the nanocomposites reduced than the neat polyamide rendering decreased permeability.
Stimuli-Responsive Polymer-Clay Nanocomposites under Electric Fields
Piao, Shang Hao; Kwon, Seung Hyuk; Choi, Hyoung Jin
2016-01-01
This short Feature Article reviews electric stimuli-responsive polymer/clay nanocomposites with respect to their fabrication, physical characteristics and electrorheological (ER) behaviors under applied electric fields when dispersed in oil. Their structural characteristics, morphological features and thermal degradation behavior were examined by X-ray diffraction pattern, scanning electron microscopy and transmission electron microscopy, and thermogravimetric analysis, respectively. Particular focus is given to the electro-responsive ER characteristics of the polymer/clay nanocomposites in terms of the yield stress and viscoelastic properties along with their applications. PMID:28787852
Characterization of clay minerals
International Nuclear Information System (INIS)
Diaz N, C.; Olguin, M.T.; Solache R, M.; Alarcon H, T.; Aguilar E, A.
2002-01-01
The natural clays are the more abundant minerals on the crust. They are used for making diverse industrial products. Due to the adsorption and ion exchange properties of these, a great interest for developing research directed toward the use of natural clays for the waste water treatment has been aroused. As part of such researches it is very important to carry out previously the characterization of the interest materials. In this work the results of the mineral and elemental chemical composition are presented as well as the morphological characteristics of clay minerals from different regions of the Mexican Republic. (Author)
Simulation of field scale water flow and bromide transport in a cracked clay soil
Dam, van J.C.
2000-01-01
Single domain models may seriously underestimate leaching of nutrients and pesticides to groundwater in clay soils with shrinkage cracks. Various two-domain models have been developed, either empirical or physically based, which take into account the effects of cracks on water flow and solute
Epoxy based nanocomposites with fully exfoliated unmodified clay: mechanical and thermal properties.
Li, Binghai; Zhang, Xiaohong; Gao, Jianming; Song, Zhihai; Qi, Guicun; Liu, Yiqun; Qiao, Jinliang
2010-09-01
The unmodified clay has been fully exfoliated in epoxy resin with the aid of a novel ultrafine full-vulcanized powdered rubber. Epoxy/rubber/clay nanocomposites with exfoliated morphology have been successfully prepared. The microstructures of the nanocomposites were characterized by means of X-ray diffraction and transmission electron microscopy. It was found that the unmodified clay was fully exfoliated and uniformly dispersed in the resulting nanocomposite. Characterizations of mechanical properties revealed that the impact strength of this special epoxy/rubber/clay nanocomposite increased up 107% over the neat epoxy resin. Thermal analyses showed that thermal stability of the nanocomposite was much better than that of epoxy nanocomposite based on organically modified clay.
Thermal volume changes in clays and clay-stones
International Nuclear Information System (INIS)
Delage, P.; Sulem, J.; Mohajerani, M.; Tang, A.M.; Monfared, M.
2012-01-01
Document available in extended abstract form only. The disposal of high activity exothermic radioactive waste at great depth in clay host rocks will induce a temperature elevation that has been investigated in various underground research laboratories in Belgium, France and Switzerland through in-situ tests. Thermal effects are better known in clays (in particular Boom clay) than in clay-stone (e.g. Opalinus clay and Callovo-Oxfordian clay-stone). In terms of volume changes, Figure 1 confirms the findings of Hueckel and Baldi (1990) that volume changes depend on the over-consolidation ratio (OCR) of the clay. In drained conditions, normally consolidated clays exhibit plastic contraction when heated, whereas over-consolidated clay exhibit elastic dilation. The nature of thermal volume changes in heated clays obviously has a significant effect on thermally induced pore pressures, when drainage is not instantaneous like what occurs in-situ. Compared to clays, the thermal volume change behaviour of clay-stones is less well known than that of clays. clay-stone are a priori suspected to behave like over-consolidated clays. In this paper, a comparison of recent results obtained in the laboratory on the drained thermal volume changes of clay-stones is presented and discussed. It is difficult to run drained mechanical tests in clay-stones like the Opalinus clay and the Callovo-Oxfordian clay-stone because of their quite low permeability (10 -12 - 10 -13 m/s). This also holds true for thermal tests. Due to the significant difference in thermal expansion coefficient between minerals and water, it is necessary to adopt very slow heating rate (0.5 - 1 C/h) to avoid any thermal pressurization. To do so, a new hollow cylinder apparatus (100 mm external diameter, 60 mm internal diameter) with lateral drainages reducing the drainage length to half the sample thickness (10 mm) has been developed (Monfared et al. 2011). The results of a drained cyclic thermal test carried out on
Physical capture and release of drug molecules, water and cations by a smectite clay
DEFF Research Database (Denmark)
Carvalho dos Santos, Éverton
-fluorohectorite (LiFh, Li1.2(Mg4.8Li1.2)Si8O20F4), a synthetic clay mineral from the smectite family, have been experimentally analyzed. By means of X-rays powder diffraction (XRD), using both an in-house instrument and synchrotron radiation, UV-Vis spectroscopy, Thermogravimetric Analysis coupled to an Infrared......-analysis and inelastic neutron scattering data we established that the drug presence into the interlayer space of Fh is weakening the water-clay interactions. Furthermore, CIPRO’s release from Fh in synthetic gastric acid juice (SGA) as a function of time and temperature was also carefully followed. Our studies showed...... and toxicological tests, we demonstrated that the effectiveness and toxicity of pure CIPRO is unaffected in the clay-drug complex. To conclude, the high drug adsorption capacity as well as the slow and gradual release from CIPRO when intercalated in Fh adds this synthetic smectite to the list of promising drug...
Films, Buckypapers and Fibers from Clay, Chitosan and Carbon Nanotubes
Directory of Open Access Journals (Sweden)
Marc in het Panhuis
2011-04-01
Full Text Available The mechanical and electrical characteristics of films, buckypapers and fiber materials from combinations of clay, carbon nanotubes (CNTs and chitosan are described. The rheological time-dependent characteristics of clay are maintained in clay–carbon nanotube–chitosan composite dispersions. It is demonstrated that the addition of chitosan improves their mechanical characteristics, but decreases electrical conductivity by three-orders of magnitude compared to clay–CNT materials. We show that the electrical response upon exposure to humid atmosphere is influenced by clay-chitosan interactions, i.e., the resistance of clay–CNT materials decreases, whereas that of clay–CNT–chitosan increases.
Oerter, Erik; Finstad, Kari; Schaefer, Justin; Goldsmith, Gregory R.; Dawson, Todd; Amundson, Ronald
2014-07-01
In isotope-enabled hydrology, soil and vadose zone sediments have been generally considered to be isotopically inert with respect to the water they host. This is inconsistent with knowledge that clay particles possessing an electronegative surface charge and resulting cation exchange capacity (CEC) interact with a wide range of solutes which, in the absence of clays, have been shown to exhibit δ18O isotope effects that vary in relation to the ionic strength of the solutions. To investigate the isotope effects caused by high CEC clays in mineral-water systems, we created a series of monominerallic-water mixtures at gravimetric water contents ranging from 5% to 32%, consisting of pure deionized water of known isotopic composition with homoionic (Mg, Ca, Na, K) montmorillonite. Similar mixtures were also created with quartz to determine the isotope effect of non-, or very minimally-, charged mineral surfaces. The δ18O value of the water in these monominerallic soil analogs was then measured by isotope ratio mass spectrometry (IRMS) after direct headspace CO2 equilibration. Mg- and Ca-exchanged homoionic montmorillonite depleted measured δ18O values up to 1.55‰ relative to pure water at 5% water content, declining to 0.49‰ depletion at 30% water content. K-montmorillonite enriched measured δ18O values up to 0.86‰ at 5% water content, declining to 0.11‰ enrichment at 30% water. Na-montmorillonite produces no measureable isotope effect. The isotope effects observed in these experiments may be present in natural, high-clay soils and sediments. These findings have relevance to the interpretation of results of direct CO2-water equilibration approaches to the measurement of the δ18O value of soil water. The adsorbed cation isotope effect may bear consideration in studies of pedogenic carbonate, plant-soil water use and soil-atmosphere interaction. Finally, the observed isotope effects may prove useful as molecular scale probes of the nature of mineral-water
Fault creep and stress drops in saturated silt-clay gouge
International Nuclear Information System (INIS)
Bombolakis, E.G.; Hepburn, J.C.; Roy, D.C.
1978-01-01
An analysis of physicochemical processes in saturated silt-clay gouge indicates that this type of fault zone material can account for for the following phenomena: (1) the nonlinear mechanical behavior indicated by certain geophysical measurements along the San Andreas fault zone, (2) the low stress drops associated with earthquakes to several kilometers' depth, and (3) the recurrence of creep-induced instabilities at shallow depths along fault zones. A rheological model is described for a gouge consisting of colloidal size clay platelets with absorbed water, brittle silt size particles, and 'free' pore water. Recurrence of shallow earthquakes or accelerated creep is explained in the model by thixotropic hardening of the colloidal phase following shear deformation, i.e., by electrochemical reorientation of clay platelets from a dispersed structure to a face-to-edge type of structure during a quiescent period. The silt phase must support part of the effective mean stress for thixotropic hardening to occur at several kilometers' depth. The peak shear strength of the gouge in this case is expressed in functional form by S/sub p/=f[kappaP/sub e/+sigma-bar/sub c/ tan psi/sub e/; sigma-bar/sub s/ tan psi/sub s/], where kappa, P/sub e/, and psi/sub e/ are Hvorslev parameters; sigma-bar/sub c/ is the effective stress in the colloidal phase, acting normal to the shear zone; sigma-bar/sub s/ is the effective stress in the silt phase, acting normal to the shear zone; and psi/sub s/ is the 'friction angle' of the silt phase. The peak shear strength is time dependent owing to viscous type contacts between absorbed water layers surrounding the colloidal platelets. The time-dependent nature of S/sub p/ may be responsible for certain nonlinear behavior noted in fault zones and for the small stress drops associated with earthquakes occurring at several kilometers' depth
Brazilian clay organophilization aiming its use in oil / water removal
International Nuclear Information System (INIS)
Mota, M.F.; Lima, W.S.; Oliveira, G.C.; Silva, M.M.; Rodrigues, M.G.F.
2012-01-01
Clays when subjected to modification with the addition of organic surfactant are called organoclays acquire hydrophobic character, they have an affinity for organic compounds. The organoclays can be used as adsorbents are considered promising agents in environmental control. The objective is to prepare organoclays clays from commercial use in order to remove organic contaminants. The clay used was gray, as polycationic, supplied by Süd-Chemie company and the quaternary ammonium salt was cetyltrimethylammonium bromide (Cetremide). The fresh samples and organoclay were characterized by the technique of X-ray diffraction (XRD), Cation Exchange Capacity, testing expansion and affinity with organic compounds: Swelling of Foster and adsorption capacity. The results showed appropriate conditions organophilic process. Through XRD confirmed the increase in basal spacing for the modified clay in relation to the clay in nature. (author)
Energy Technology Data Exchange (ETDEWEB)
Robinet, J.O. [Euro-Geomat-Consulting (France)]|[Institut National des Sciences Appliquees (INSA), 35 - Rennes (France); Plas, F. [Agence Nationale pour la Gestion des Dechets Radioactifs (ANDRA), 92 - Chatenay Malabry (France)
2005-07-01
The modelling of heat, mass transfer and the behaviour coupled thermo-hydro-mechanical in swelling clay require the development of appropriate constitutive laws as well as experimental data. This former approach, allows the quantitative validation of the theoretical models. In general modelling approaches consider dominant mechanisms, (i) Fourier law for diffusion of heat, (ii) generalized Darcy law for convection of liquid water, (iii) Flick law for diffusion of water vapour, and elastic-plastic models wit h hydric hardening and thermal damage/expansion for strain-stress behaviour. Transfer of dry air and water under thermal gradient and capillary (e.g. suction) gradient in unsaturated compacted swelling clays consider evaporation, migration and condensation. These transfers take into account the capillary effect. This effect is an evaporation of liquid water in the hot part for temperature higher than 100 C associated with a, diffusion of water vapor towards cold part then condensation, and convection of liquid water with gradient of suction in the opposite direction of the water vapour diffusion. High values of the diffusion coefficient of the vapour water are considered about 10{sup -7}m{sup 2}/s. Some thermal experiments related (i) low values of the water vapour diffusion coefficient in compacted swelling clays, 2004) and (ii) a significant drying associated with a water transfer even for temperature lower than 100 C. Other enhancement phenomena are used to explain these data and observations: the vaporization is a continuous process. At short term the mechanism of drying at short term is the thermal effect on the capillary pressure (e.g. surface tension depending of temperature); the thermal gradient is a driving force. When a temperature gradient is applied, diffusion occurs in order to reach equilibrium, e.g. to make the chemical potential (m) of each component uniform throughout. This mechanism is called thermal diffusion. This paper proposes a discussion
Removal of clay by stingless bees: load size and moisture selection.
Costa-Pereira, Raul
2014-09-01
Some organisms disperse energy, associated with the transportation of resource, which is not necessarily food. Stingless bees of Central Amazonia (Melipona flavolineata and M. lateralis) collect clay in banks along streams for nest building. The moisture of the clay varies along the bank, and bees collect clay from specific location, indicating that there is some sort of preference regarding their selection. This study aims at identifying: if larger bees carry more clay; if there is a preference for moisture of substrates; and if bees are less efficient accumulating and transporting clay when it is wet. In order to do so, I measured the size of the bees and of the pellets of clay found in the corbicula. I set up a field experiment to test substrate preferences. The amount of clay transported, increased exponentially in accordance to the size of the bee, and the preferred substrate was the driest clay. The amount and the efficiency of removal of clay were not affected by the moisture of the substrate. Despite the wet clay being denser, it does not reduce the efficiency of exploitation of the resource, but suggests that bees spend more energy to carry the same quantity of wet clay, which may be the underlying mechanism explaining their preference for removing drier clay.
International Nuclear Information System (INIS)
Komatsu, L.G.H.; Oliani, W.L.; Lugao, A.B.; Parra, D.F.
2014-01-01
The evaluation of HMSPP (high melt strength polypropylene) properties in nanocomposites was done in composites of 0.1; 1; 3; 5; 10 wt% of Cloisite 20A clay. The PP-g-MA (polypropylene graft maleic anhydride) was the compatibilizer agent in the process of extrusion in twin-screw. Mechanical tests performed in the nanocomposites with higher clay content showed higher values of rupture in 5 and 10 wt% of Cloisite. The thermal properties were evaluate utilizing Calorimetry Differential Exploratory (DSC) and in the sample of 10 wt% of Cloisite were observed increase of the melting temperature and increase of crystallinity. The morphology was investigated by the Scanning Electron Microscopy (SEM) and Fourier Transformed Infrared (FTIR), in which the sample with lower clay amount, 1 wt% of Cloisite showed better dispersion of the clay. X-Ray Diffraction reported the clay intercalation in the sample with 5 wt% of clay. (author)
Energy Technology Data Exchange (ETDEWEB)
Li, Y
1996-04-16
Filtration properties of model drilling fluids composed of water, clays, electrolytes and water soluble polymers have been studied in static and dynamic conditions on paper filters and rock slices. Filtration experiments combined with cake observations by cryo-S.E.M. and T.E.M., show the influence of the size shape of clay particles as well as their associating mode in suspension, on the texture of the cake, its permeability, and relaxation properties. These parameters depend on the nature of the electrolyte. The polymer reduces the cake permeability by enhancing the dispersion of the clay within the suspension, but mainly by plugging the porous network due its auto aggregation properties. The cake construction in dynamic conditions, is related to the state of aggregation of the initial suspension, its poly-dispersity, its sensitivity to shear rates, and also, to the permeability of the cake built at the beginning of the filtration. In all cases, the rate of thickening of the cake is slower and larger filtrate volumes are obtained compared to the static conditions. Shear rate has two effects: first, to dissociate the weak aggregates in suspension, second, to impose a size selection of the particles in the case of a poly-dispersed suspension. At high shear rates, a cake of constant thin thickness is quickly obtained. The thickness of this limiting cake depends on the fraction of small particles present in suspension, or that can be formed by dissociation of weak aggregates under shear rate. The permeability of this limiting cake formed in dynamic conditions is, as in static conditions, controlled by the size and the shape of the particles that form the cake or by the presence of a build loss reducer water soluble polymer. Filtrations carried out on Fontainebleau sandstones allow to visualize the internal cake and to precise the risks of formation damage by the drilling fluid. (author) 127 refs.
Flocculation and dispersion behaviour of two kaolinitic soil clays as ...
African Journals Online (AJOL)
This showed that crystalline Fe oxides were important in stabilizing the structure of the soils studied. The amorphous Fe oxides, however, did not play a stabilizing role. The clays whose crystalline Fe oxides, amorphous Fe oxides and organic matter were successively removed were the most flocculated and therefore had ...
International Nuclear Information System (INIS)
Juranyi, Fanni; Gonzalez Sanchez, Fatima; Gimmi, Thomas; Bestel, Martina; Van Loon, Luc; Diamond, Larryn W.
2013-01-01
Observable water diffusion processes in clays and their parameters depend on the spatial- and time-scale of the measurement. Comparing the diffusion coefficients of quasielastic neutron scattering and tracer through-diffusion, 'chemical' and 'geometrical' effects can be distinguished and quantified. Results for montmorillonite and illite in the Na- and Ca- form illustrate this very well. Swelling clays such as montmorillonite are especially interesting because of the interlayer water. This water is confined in form of few layers such that the diffusion occurs essentially in 2D. Furthermore the ratio of interlayer- and external- (macro-pore) water changes as a function of bulk dry density and degree of water saturation. Therefore it is of interest to describe the diffusion process using these parameters. Finally, the activation energy of the diffusion should be equal for both methods assuming that the geometrical factor does not depend on temperature. For the montmorillonites this was not the case, which might also indicate that the main processes on the two scales are different. We conclude that the geometrical factor and the electrostatic constraint can be determined from a comparison of the diffusion coefficients measured by the two different techniques: quasielastic neutron scattering and tracer through diffusion. Furthermore, activation energies obtained at the two scales are similar for clays having no interlayer water. For montmorillonite the activation energy values are different. Further investigations are required to clarify the reason. (authors)
Se of polymers to control clay swelling
Energy Technology Data Exchange (ETDEWEB)
Slobod, R L; Beiswanger, J P.G.
1968-01-01
The injection of water to displace oil is one of the main methods used to increase oil recovery. High injection rates are generally desired, and in some cases the flood will not be economic unless high rates are maintained. The presence of clays which swell in the presence of water offers a complication to the problem of maintaining adequate injectivity. In the course of this study it was observed that certain polymers, when present in dilute concentrations in the water, had the ability to reduce the response of these clays to fresh water. Two polymers, one an anionic and the other nonionic, were found to be very effective in controlling the clays present in Berea cores. Successful control of clay swelling was obtained by use of solutions containing as little as 1.0 ppM of polymer, but at this low concentration appreciable volumes of treating solution were required. These results suggest that some minimum amount of polymer must be adsorbed to prevent clay swelling. In Berea sandstone this minimum amount appeared to be of the order of 0.03 mg per cc of pore space. A series of tests made using 10.0 ppM polymer showed that the polymer could be made through the porous system in which 0.066 per mg of polymer was adsorbed per cc of pore space.
Rapid Stabilization/Polymerization of Wet Clay Soils; Literature Review
2009-01-15
MacDonald, W. A., Pitman, D., and Ryan, T. G. (1999). "High Tempera- ture Non-aqueous Dispersion Polymerization of Aromatic Main Chain Liquid...of Dispersive Soils by Using Different Additives." Indian Geotechnical Journal, 14(3), 202-216. 36. Charleson, D. A. and Widger, R. A. (1989...Baghdadi, Z. A., and Khan, A. M. (1991). "Overconsolidated Beha- vior of Phosphoric Acid and Lime-Stabilized Kaolin Clay." Transportation Research
Energy Technology Data Exchange (ETDEWEB)
Lima, W.S.; Rodrigues, M.G.F.; Mota, M.F.; Patricio, A.C.L.; Silva, M.M., E-mail: wsl_20@yahoo.com.br [Universidade Federal de Campina Grande (LABNOV/UFCG), PB (Brazil). Unidade Academica de Engenharia Quimica. Lab. de Desenvolvimento de Novos Materiais
2012-07-01
The smectite clays have high adsorption capacity and cation exchange. Due to its chemical and physical characteristics, they can be effectively used as adsorbent of pollutants (such as metal ions). The initial objective of this study was to characterize the clay Brasgel through the techniques of X-Ray Diffraction (XRD), X-Ray Spectrometry by Energy Dispersive (EDX) and nitrogen adsorption (BET method), seeking its use in removing lead (Pb{sup 2+}) from synthetic effluents. System was used in finite bath to assess the potential removal of lead (Pb{sup 2+}), following a 2{sup 2} factorial experimental design with three center point experiments, taking as input variables: pH and initial concentrations of lead (Pb{sup 2+}). The clay has Brasgel clay in its composition that characterize it as a smectite clay. By having a large surface area, this clay showed great potential on the adsorption of metal ions. (author)
Effect of water content on dispersion of transferred solute in unsaturated porous media
Energy Technology Data Exchange (ETDEWEB)
Latrille, C. [CEA Saclay, DEN/DANS/DPC/SECR/L3MR, 91191 Gif sur Yvette (France)
2013-07-01
Estimating contaminant migration in the context of waste disposal and/or environmental remediation of polluted soils requires a complete understanding of the underlying transport processes. In unsaturated porous media, water content impacts directly on porous solute transfer. Depending on the spatial distribution of water content, the flow pathway is more complex than in water saturated media. Dispersivity is consequently dependent on water content. Non-reactive tracer experiments performed using unsaturated sand columns confirm the dependence of dispersivity with pore velocity; moreover, a power law relationship between dispersivity and water content is evidenced. (authors)
International Nuclear Information System (INIS)
Montes-Hernandez, G.
2002-10-01
This work deals with the study of water sorption and clays swelling (MX80 bentonite and Paris basin argilites). A new approach by environmental scanning electron microscopy (ESEM) coupled to digital image analysis is proposed to estimate the swelling with time and the relative humidity. The ESEM is a new generation tool, not much used in the clays domain, which allows to study hydrated materials in different conditions of relative humidity. In this work, it is shown that qualitative and quantitative information about clays swelling at the aggregate scale can be obtained. The study of the kinetics allows to identify three swelling steps which are described by a first order kinetic model. The study of water sorption by raw bentonite and the exchange of different cation (Na + , Li + , K + , Ca 2+ , Mg 2+ ) has permitted to analyze the cation influence on the swelling potential. The adsorption kinetics, described by a second order model, depends directly on the relative humidity, on the mass of the sample and on the compensating cation. The study of the texture of the compacted MX80 bentonite in dry and humid conditions has permitted to observe the morphological evolution of the porous network (macro-porosity) during the hydration/dehydration. From different analytical approaches, a diminution of the macro-pores and/or meso-pores size and the opening of inter-aggregate pores is observed when the apparent density increases. The study of the influence of the instantaneous water condensation/evaporation on the argilites shows that the sensitiveness to water increases when the proportion of clay increases. In particular, it is characterized by a cracking partially reversible or irreversible after several condensation/evaporation cycles. (J.S.)
Thermal Behaviour of clay formations
International Nuclear Information System (INIS)
Tassoni, E.
1985-01-01
The programme carried out by ENEA to model the thermal-hydraulic-mechanical behaviour of the clay formations and to measure, in situ and in laboratory, the thermal properties of these rocks, is presented. An in situ heating experiment has been carried out in an open clay quarry in the area of Monterotondo, near Rome. The main goal of the experiment was to know the temperature field and the thermal effects caused by the high level radioactive waste disposed of in a clayey geological formation. The conclusions are as follows: - the thermal conduction codes are sufficiently accurate to forecast the temperature increases caused in the clay by the dissipation of the heat generated by high level radioactive waste; - the thermal conductivity deduced by means of the ''curve fitting'' method ranges from 0.015 to 0.017 W.cm -1 . 0 C -1 - the temperature variation associated with the transport of clay interstitial water caused by temperature gradient is negligible. A laboratory automated method has been designed to measure the thermal conductivity and diffusivity in clay samples. A review of experimental data concerning thermomechanical effects in rocks as well as results of thermal experiments performed at ISMES on clays are presented. Negative thermal dilation has been found both in the elastic and plastic range under constant stress. Thermoplastic deformation appears ten times greater than the thermoelastic one. A mathematical model is proposed in order to simulate the above and other effects that encompass thermal-elastic-plastic-pore water pressure response of clays at high temperature and effective pressure with undrained and transient drainage conditions. Implementation of the two versions into a finite element computer code is described
International Nuclear Information System (INIS)
Morelli, Fernanda C.; Ruvolo Filho, Adhemar
2009-01-01
In this work were prepared nanocomposites of polypropylene and organophilic montmorillonite Cloisite 20A with concentrations of 1.5%, 2.5%, 5.0% and 7.5% clay and graft polypropylene with maleic anhydride as compatibilizer. The mixture was made in the melt state using a twin screw extruder. The materials were characterized by x-ray diffraction, infrared spectroscopy with Fourier transform and analysis of water vapor permeation. The results of x-ray diffraction and infrared spectroscopy indicates the formation of nanocomposites with structures probably exfoliate and / or intercalated for concentrations of 1.5% and 2.5% clay, and provided a marked decrease in the water permeability, corroborating with other analysis. (author)
Clay shale as host rock. A geomechanical contribution about Opalinus clay
International Nuclear Information System (INIS)
Lempp, Christof; Menezes, Flora; Sachwitz, Simon
2016-01-01
The Opalinuston is a prominent rock representing the type of organic clay shales or clay stones within the sequence of Triassic and Jurassic marine sediments in Southern Germany. The rock forms a homogenous unit some ten meters thick. The degree of consolidation of this type of pelitic rock depends mainly on the former load conditions, but is also dependent on the long-term weathering and even on the present exposition. The geomechanical parameters such as shear strength, tensional strength and permeability vary with the state of consolidation and become important when the use is discussed of such rocks for radioactive waste disposal. A tunneling project at the northern escarpment of the Swabian Alb (Southwest Germany) within the Opalinus clay offered the rare opportunity to obtain fresh unweathered rock samples in greater amounts compared to fresh drilling cores from which geomechanical investigations are usually undertaken. Consequently, the results of geomechanical laboratory testings are presented in order to compare here the results of multistep triaxial compression tests, of hydraulic fracturing laboratory tests and of some other tests for rock characterization with the corresponding results of Opalinus clay sites in Switzerland that were investigated by the Swiss Nagra Company for host rock characterization. After a discussion of the relevant state of fresh Opalinus clay, especially of suction pressure conditions and saturation state, the results of triaxial shear tests are presented. Increasing shear deformation at increasing pressure and unchanged water saturation do not result in a significant strength reduction of the Opalinus clay. The rock shows increasing cohesion and stiffness, if multiple loading has repeatedly reached the failure point. Thus there is no increased permeability with continued shearing. Only at the beginning of the shearing process is a temporarily increased permeability to be expected due to dilatation processes. An increased
Pickering emulsions stabilized by paraffin wax and Laponite clay particles.
Li, Caifu; Liu, Qian; Mei, Zhen; Wang, Jun; Xu, Jian; Sun, Dejun
2009-08-01
Emulsions containing wax in dispersed droplets stabilized by disc-like Laponite clay particles are prepared. Properties of the emulsions prepared at different temperatures are examined using stability, microscopy and droplet-size analysis. At low temperature, the wax crystals in the oil droplets can protrude through the interface, leading to droplet coalescence. But at higher temperatures, the droplet size decreases with wax concentration. Considering the viscosity of the oil phase and the interfacial tension, we conclude that the wax is liquid-like during the high temperature emulsification process, but during cooling wax crystals appear around the oil/water interface and stabilize the droplets. The oil/water ratio has minimal effect on the emulsions between ratios of 3:7 and 7:3. The Laponite is believed to stabilize the emulsions by increasing the viscosity of the continuous phase and also by adsorbing at the oil/water interface, thus providing a physical barrier to coalescence.
Studying the Effect of Crystal Size on Adsorption Properties of Clay
International Nuclear Information System (INIS)
Abdellatif, M.M.
2012-01-01
Sorption of radionuclides on mineral surfaces strongly affects their fate and mobility in the geosphere. Therefore using of clay minerals as a barrier In LLW repositories can delay the dispersion of radionuclides into environment. That is of fundamental importance for maintaining environmental quality and for the safety and long-term performance of waste repositories. In this study XRD analysis was applied to investigate three different types of clay minerals for quantitative analysis of each type and the Mud Master program for the measurement of the crystallite thickness distribution (CTD) according to of the BWA (Bertaut-Warren Averbach) technique. Six sample s of the three types of clay (Kaolin, Aswan clay and Ball clay) were studied. XRD and Mud Master were used to investigate the relation between CTD and Cs -137 uptake mechanism onto the clay. It was found that the best adsorption capacity related to the kaolinite content and the lowest CTD
International Nuclear Information System (INIS)
Shin, Jeong Rae
1987-02-01
This book deals with the medicine of water handling, which includes medicine for dispersion and cohesion, zeta-potential, congelation with Shalze Hardy's law, inorganic coagulants, inorganic high molecule coagulants, aid coagulant such as fly ash and sodium hydroxide, and effect of aluminum and iron on cohesion of clay suspension, organic coagulants like history of organic coagulants, a polyelectrolyte, coagulants for cation, and organic polymer coagulant, heavy metal and cyan exfoliants, application of drugs of water treatment.
Organo-clay/anthracite filtration for oil removal
International Nuclear Information System (INIS)
Moazed, H.; Viragahavan, T.
1999-01-01
An advantage of organo-clay compared to other sorbents is that it can selectively remove organic pollutants from contaminated waters. An investigation was conducted to determine the potential of an organo-clay/anthracite mixture as a filter media for the removal of oil from synthetic and real oily waters. Also included in the study were column filtration studies using synthetic and real waste waters to determine the sorptive capacity of the material. In general, oil removal efficiencies in a 300 mm organo-clay/anthracite bed decreased with an increase in flow rates. Results of eight hour studies indicated that the depth of an organo-clay/anthracite bed has a direct effect on oil removal efficiency. The Thomas equation provides a reasonable fit of the data based on breakthrough studies. The model can be used to determine the parameters needed to design full-scale filtration columns. The uptake of oil by an organo-clay/anthracite mixture is well described by an equation including time such as the Weber or Moris model. The maximum solid-phase concentration of the solute values obtained from the Thomas equation were comparable to the values found by a mass balance approach. 12 refs., 8 figs., 4 tabs
International Nuclear Information System (INIS)
Davloor, R.; Harper, B.
2011-01-01
Bruce Power's Bruce Nuclear Generating Station 'A', located on Lake Huron, has a treatment system that processes all aqueous radioactive waste water originating from the station. This Active Liquid Waste Treatment System (ALWTS) consists of collection tanks for the collection of radioactive waste water, a Pre-Treatment System (PTS) for the removal of bulk contaminants and suspended solids, a Reverse Osmosis System (ROS) to remove dissolved solids, an Evaporation and Solidification System (ESS) to concentrate and immobilize solids contained in concentrated waste streams from the ROS, and discharge tanks for the dispersal of the treated water. The ALWTS has been in continuous service since 1999 and is used to treat approximately 100,000 litres of Active Liquid Waste (ALW) each day. With the exception of tritium, it discharges waste water containing near zero concentrations of radioactive and conventional contaminants to the lake. The original design of the Bruce A ALWTS used a Backwashable Filtration System (BFS) to provide solids free water to the ROS, as measured by the Silt Density Index (SDI). During commissioning, the BFS was not successful in backwashing the solids from the filter elements. For approximately one year, a temporary solution was implemented using a Disposable Filtration System (DFS). A cationic polymer was added upstream of the DFS to agglomerate the solids. The system proved to be highly unreliable. It was difficult to agglomerate solids in the waste stream containing high amounts of detergent. As a result, DFS consumption was high and very costly. The SDI specification for the RO membrane was not always met, resulting in a quick decline of performance of the first stage ROS membranes in the treatment process. In addition, the excess cationic polymer in the RO feed caused the membranes to become fouled. In-house station staff, together with personnel from Colloid Environmental Technologies (CETCO) Company, worked to develop and
Energy Technology Data Exchange (ETDEWEB)
Davloor, R.; Harper, B. [Bruce Power, Tiverton, ON (Canada)
2011-07-01
Bruce Power's Bruce Nuclear Generating Station 'A', located on Lake Huron, has a treatment system that processes all aqueous radioactive waste water originating from the station. This Active Liquid Waste Treatment System (ALWTS) consists of collection tanks for the collection of radioactive waste water, a Pre-Treatment System (PTS) for the removal of bulk contaminants and suspended solids, a Reverse Osmosis System (ROS) to remove dissolved solids, an Evaporation and Solidification System (ESS) to concentrate and immobilize solids contained in concentrated waste streams from the ROS, and discharge tanks for the dispersal of the treated water. The ALWTS has been in continuous service since 1999 and is used to treat approximately 100,000 litres of Active Liquid Waste (ALW) each day. With the exception of tritium, it discharges waste water containing near zero concentrations of radioactive and conventional contaminants to the lake. The original design of the Bruce A ALWTS used a Backwashable Filtration System (BFS) to provide solids free water to the ROS, as measured by the Silt Density Index (SDI). During commissioning, the BFS was not successful in backwashing the solids from the filter elements. For approximately one year, a temporary solution was implemented using a Disposable Filtration System (DFS). A cationic polymer was added upstream of the DFS to agglomerate the solids. The system proved to be highly unreliable. It was difficult to agglomerate solids in the waste stream containing high amounts of detergent. As a result, DFS consumption was high and very costly. The SDI specification for the RO membrane was not always met, resulting in a quick decline of performance of the first stage ROS membranes in the treatment process. In addition, the excess cationic polymer in the RO feed caused the membranes to become fouled. In-house station staff, together with personnel from Colloid Environmental Technologies (CETCO) Company, worked to develop and
Wang, Yawen; Duo, Fangfang; Peng, Shiqi; Jia, Falong; Fan, Caimei
2014-09-15
In this paper, we report a novel polyol process to synthesize highly water-dispersible anatase titanium dioxide (TiO2) nanoparticles (∼5 nm) by the introduction of inorganic oxidizing agent--KIO3. The obtained TiO2 nanoparticles are well dispersible in water at pH≥5.0 and the resulting aqueous dispersion remains stable over months. The superior water-dispersibility of as-formed TiO2 is ascribed to the electrostatic repulsion from carboxylic acid group modified on TiO2 nanoparticles, which is the oxidation product of solvent diethylene glycol (DEG) by KIO3. Based on the characterization results, the formation processes of water-dispersibility TiO2 nanoparticles are proposed. Meanwhile, the synthesized TiO2 nanoparticles are found to be doped by iodine and exhibit excellent photocatalytic activity on degradation of rhodamine-B (RhB) under visible-light irradiation. The further tests demonstrate that the O(2-) is the main active species during photodegradation of RhB. Copyright © 2014 Elsevier Inc. All rights reserved.
Removal of clay by stingless bees: load size and moisture selection
Directory of Open Access Journals (Sweden)
RAUL COSTA-PEREIRA
2014-09-01
Full Text Available Some organisms disperse energy, associated with the transportation of resource, which is not necessarily food. Stingless bees of Central Amazonia (Melipona flavolineata and M. lateralis collect clay in banks along streams for nest building. The moisture of the clay varies along the bank, and bees collect clay from specific location, indicating that there is some sort of preference regarding their selection. This study aims at identifying: if larger bees carry more clay; if there is a preference for moisture of substrates; and if bees are less efficient accumulating and transporting clay when it is wet. In order to do so, I measured the size of the bees and of the pellets of clay found in the corbicula. I set up a field experiment to test substrate preferences. The amount of clay transported, increased exponentially in accordance to the size of the bee, and the preferred substrate was the driest clay. The amount and the efficiency of removal of clay were not affected by the moisture of the substrate. Despite the wet clay being denser, it does not reduce the efficiency of exploitation of the resource, but suggests that bees spend more energy to carry the same quantity of wet clay, which may be the underlying mechanism explaining their preference for removing drier clay.
Preconcentration of uranium in water samples using dispersive ...
African Journals Online (AJOL)
Preconcentration of uranium in water samples using dispersive liquid-liquid micro- extraction coupled with solid-phase extraction and determination with inductively coupled plasma-optical emission spectrometry.
Soil water retention curves of remoulded clay on drying and wetting paths
International Nuclear Information System (INIS)
Zhang Xiwei; Zhang Jian
2010-01-01
The present research focuses on the laboratory measurement of the Soil Water Retention Curve (SWRC), that expresses the relationship between water content (gravimetric or volumetric) or degree of saturation and soil suction. The SWRC plays an important role in an unsaturated soil mechanics framework and is required for the numerical modelling of any process of flow and transport in unsaturated soil problems, already as a part of constitutive model of unsaturated soil. Six remoulded London Clay samples were performed SWRC testing on the drying and wetting path, meanwhile measurement the volume change. The effect of initial water content and various drying/wetting paths were considered in the tests. The results of SWRC show that hysteretic characteristic in boundary drying/wetting curve, the water holding capacity was increased due to the increase of the initial water content. The shape of the SWRC strongly depended on the volume change. (authors)
Directory of Open Access Journals (Sweden)
Aeknarin Thanakitpairin
2014-01-01
Full Text Available This research aims to describe the nitrogen and phosphorus removal in Recirculating Aquaculture System (RAS by crop plants biomass production. The 3 experiment systems consisted of 1 treatment (fish tank + baked clay beads + Chinese cabbage and 2 controls as control-1 (fish tank only and control-2 (fish tank + baked clay beads, were performed. With all experimental RAS, Nile tilapia (Oreochromis niloticus was cultured at 2 kg/m3 density. The baked clay beads (8-16 mm in diameter were filled as a layer of 10 cm in the water treatment tank of control-2. While in the treatment tank, Chinese cabbage (Brassica pekinensis was planted at 334 plants/m2 in baked clay beads layer. During 35 days of experiment, the average fish wet-weight in control-1, control-2 and treatment systems increased from 16.31±1.49, 15.18±1.28 and 11.31±1.49 g to 29.43±7.06, 28.65±3.12 and 27.20±6.56 g, respectively. It was found that the growth rate of 0.45±0.15 g-wet weight/day in a treatment tank was higher than in those 2 controls, which were rather similar at 0.37±0.16 and 0.38±0.05 g-wet weight/day, respectively. The fish survival rate of all experimental units was 100%. The average Chinese cabbage wet-weight in treatment system increased from 0.15±0.02 g to 1.00±0.38 g. For water quality, all parameters were within the acceptable range for aquaculture. The assimilation inorganic nitrogen in a treatment tank showed a slower rate and lower nitrite accumulation relative to those in control tanks. The nitrogen and phosphorus balance analysis illustrated that most of the nitrogen and phosphorus input in all systems was from feed (82-87% and 21-87% while at the final day of experiments, nitrogen and phosphorus in tilapia culture revealed at 15-19% and 4-13%. The accumulation of nitrogen and phosphorus in the water, up to 56% and 70%, was found in control-1 while water in the tank with baked clay beads had substantial lower nitrogen and phosphorus concentration. The
Effect of illite clay and divalent cations on bitumen recovery
Energy Technology Data Exchange (ETDEWEB)
Ding, X. [SNC-Lavalin Inc., Calgary, AB (Canada); Repka, C. [Baker Petrolite Corp., Fort McMurray, AB (Canada); Xu, Z.; Masliyah, J. [Alberta Univ., Edmonton, AB (Canada). Dept. of Chemical and Materials Engineering
2006-12-15
Nearly 35 per cent of Canada's petroleum needs can be met from the Athabasca oil sands, particularly as conventional sources of petroleum decline. The interactions between bitumen and clay minerals play a key role in the recovery process of bitumen because they affect bitumen aeration. The 2 clays minerals found in various oil sands extraction process streams are kaolinite and illite. In this study, doping flotation tests using deionized water and electrokinetic studies were performed to examine the effect of illite clays on bitumen recovery. The effect of magnesium ions was also examined and compared with calcium ions. This paper also discussed the effects of temperature and tailings water chemistry. The negative effect of illite clay on bitumen recovery was found to be associated with its acidity. Denver flotation cell measurements indicated that the addition of calcium or magnesium ions to the flotation deionized water had only a slight effect on bitumen recovery, but the co-addition of illite clay and divalent cations resulted in a dramatic reduction in bitumen recovery. The effect was more significant at lower process temperature and low pH values. Zeta potential distributions of illite suspensions and bitumen emulsions were measured individually and as a mixture to determine the effect of divalent cations on the interaction between bitumen and illite clay. The presence of 1 mM calcium or magnesium ions in deionized water had a pronounced effect on the interactions between bitumen and illite clay. Slime coating of illite onto bitumen was not observed in zeta potential distribution measurements performed in alkaline tailings water. When tests were conducted using plant recycle water, the combination of illite clay and divalent cations did not have an adverse effect on bitumen recovery. 25 refs., 3 tabs., 15 figs.
Influence of acidification of circulating water on differential distribution of dispersed phase
Directory of Open Access Journals (Sweden)
Oleksandr B. Gulyaenko
2015-06-01
Full Text Available The paper analyzes the connection between processing technologies of circulating water cooling tower and coagulation-aggregation properties of colloidal particles of the dispersed phase. In circulating water cooling tower when clarifying additional water the reduction of HCO3- and CO32- concentrations happens with corresponding pH increase. Absorption of atmospheric carbon dioxide by cooling tower circulating water offsets this increase. The estimation of the probability of adhesion to the surface of the dispersed phase, distributed in the volume of circulation water, and the heat exchange surface of the condenser for different degrees of evaporation of the coolant is made. The distribution of cooling water micro-disperse particles which are adsorbed on the heat exchange surfaces of the condenser (deposit formation and on the surface of larger particles (particle aggregation reflects the efficiency of applied water treatment technology. It is shown that acidification of additional water facilitates solution of most fine fractions and increases hardness of treated water.
Evaluation of the degree of dispersion of organoclay on nanocomposites with PP/EPDM
International Nuclear Information System (INIS)
Braga, F.C.F.; Oliveira, M.G.
2010-01-01
Nanocomposites of thermoplastic elastomer (TPE) composed by PP/EPDM 1/1 blend and organoclay were obtained by the melt intercalation in an internal chamber mix. Initially, a masterbatch of maleinized polypropylene (PP-MA) and clay modified with alkyl ammonium salt in the ratio 3:1 was prepared, and then, added to TPE matrix to obtain loads of 2,5; 5 and 7 wt% of clay in the nanocomposite. The dispersion degree of clay in TPE matrix was evaluated by X-ray diffraction and parallel plate rheometry. The intercalation/exfoliate degree or the degree of dispersion varied with clay content, as observed by X-ray diffraction. This behavior was confirmed by the profile of the curves of elastic modulus versus frequency, which presented different slopes in the region of low frequency, due to the presence of clay and PP-MA. (author)
Investigations of salt mortar containing saliferous clay
International Nuclear Information System (INIS)
Walter, F.
1992-01-01
Saliferous clay mortar might be considered for combining individual salt bricks into a dense and tight long-term seal. A specific laboratory program was started to test mortars consisting of halite powder and grey saliferous clay of the Stassfurt from the Bleicherode salt mine. Clay fractions between 0 and 45% were used. The interest focused upon obtaining good workabilities of the mixtures as well as upon the permeability and compression strength of the dried mortar samples. Test results: 1) Without loss of quality the mortar can be mixed using fresh water. Apprx. 18 to 20 weight-% of the solids must be added as mixing water. 2) The porosity and the permeability of the mortar samples increases distinctly when equally coarse-grained salt power is used for mixing. 3) The mean grain size and the grain size distribution of the saliferous clay and the salt powder should be very similar to form a useful mortar. 4) The permeability of the mortar samples decreases with increasing clay fraction from 2 10 -12 m 2 to 2 10 -14 m 2 . The investigated samples, however, were large and dried at 100degC. 5) The uniaxial compressive strength of the clay mortar equals, at an average, only 4 MPa and decreases clearly with increasing clay fraction. Moist mortar samples did not show any measurable compressive strength. 6) Moistened saliferous clay mortar may show little temporary swelling. (orig./HP)
Removal of blue 1 dye of aqueous solutions with a modified clay with iron chloride
International Nuclear Information System (INIS)
Hernandez H, K. A.
2012-01-01
At the present time, several technologies have been proposed to remove dyes from water, adsorption is one of the most feasible methods and adsorbents with different properties, such as activated carbon, zeolites, clays and hydrogels among others. In this work, the sorption behavior of blue 1 dye by a natural clay from a site located in the Center-East of Mexico, and other modified with iron chloride were determined. The materials were characterized by X-ray diffraction to analyze its crystal structure, by scanning electron microscopy and elemental microanalysis of energy dispersive X-ray spectrometry to determine the composition and morphology, and the zero point charges were also determined to know the charge distribution on the surface of the clay. The ph effect, contact time, dye concentration and temperature were the parameters considered in this study. The results showed that clay does not suffer any important changes in its structure after the chemical treatments (modification with ferric chloride and contact with blue 1 solutions). The ph influences lightly the adsorption of the dye with natural clay, but the same effect is not observed in the ferric modified clay among the factor ph 6 and 8. The equilibrium time and the sorption capacity for natural clay were 48 hours and 6.16 mg/g, while for the ferric clay were 24 hours and 14.22 mg/g. Adsorption kinetics results were best adjusted to the pseudo first and pseudo second order models. Adsorption isotherms were best adjusted to the Langmuir model, indicating that both clays have a homogeneous surface. Thermodynamic parameters (E, ΔS and ΔG and ΔH) were calculated for the dye adsorption by the natural clay using data of the adsorption kinetics at temperatures between 20 and 50 C, indicating that the adsorption process is exothermic. For the case of ferric clay, it was not possible to calculate these thermodynamic parameters because the adsorption capacities were similar in the range of selected
MEASUREMENT OF THE VISCOELASTIC PROPERTIES OF WATER-SATURATED CLAY SEDIMENTS.
The complex shear modulus of both kaolin -water and bentonite-water mixtures has been determined in the laboratory. The method involved measuring the...range two to forty-three kHz. Dispersed sediments behaved like Newtonian liquids. Undispersed sediments, however, were viscoelastic in character, and...their shear moduli exhibited no dependence on frequency. For undispersed kaolin mixtures, a typical result is (21.6 + i 1.2) x 1,000 dynes per square
Shivaraju, H Puttaiah; Egumbo, Henok; Madhusudan, P; Anil Kumar, K M; Midhun, G
2018-02-01
Affordable clay-based ceramic filters with multifunctional properties were prepared using low-cost and active ingredients. The characterization results clearly revealed well crystallinity, structural elucidation, extensive porosity, higher surface area, higher stability, and durability which apparently enhance the treatment efficiency. The filtration rates of ceramic filter were evaluated under gravity and the results obtained were compared with a typical gravity slow sand filter (GSSF). All ceramic filters showed significant filtration rates of about 50-180 m/h, which is comparatively higher than the typical GSSF. Further, purification efficiency of clay-based ceramic filters was evaluated by considering important drinking water parameters and contaminants. A significant removal potential was achieved by the clay-based ceramic filter with 25% and 30% activated carbon along with active agents. Desired drinking water quality parameters were achieved by potential removal of nitrite (98.5%), nitrate (80.5%), total dissolved solids (62%), total hardness (55%), total organic pollutants (89%), and pathogenic microorganisms (100%) using ceramic filters within a short duration. The remarkable purification and disinfection efficiencies were attributed to the extensive porosity (0.202 cm 3 g -1 ), surface area (124.61 m 2 g -1 ), stability, and presence of active nanoparticles such as Cu, TiO 2 , and Ag within the porous matrix of the ceramic filter.
Organic waste treatment with organically modified clays
International Nuclear Information System (INIS)
Evans, J.C.; Pancoski, S.E.; Alther, G.
1989-01-01
The use of organically modified clays in hazardous waste management applications offers a significant new and untapped potential. These clays may be used in the stabilization of organic wastes and organically contaminated soils, for waste water treatment, for oil spill control, for liner systems beneath fuel oil storage tanks, and as a component within liner systems of hazardous waste storage treatment and disposal facilities. Organically modified clays (organophilic clays) may be employed in each of these systems to adsorb organic waste constituents, enhancing the performance of the applications
Anomalous dispersion of magnetic spiky particles for enhanced oil emulsions/water separation.
Chen, Hui-Jiuan; Hang, Tian; Yang, Chengduan; Liu, Guishi; Lin, Di-An; Wu, Jiangming; Pan, Shuolin; Yang, Bo-Ru; Tao, Jun; Xie, Xi
2018-01-25
In situ effective separation of oil pollutants including oil spills and oil emulsions from water is an emerging technology yet remains challenging. Hydrophobic micro- or nano-materials with ferromagnetism have been explored for oil removal, yet the separation efficiency of an oil emulsion was compromised due to the limited dispersion of hydrophobic materials in water. A surfactant coating on microparticles prevented particle aggregation, but reduced oil absorption and emulsion cleaning ability. Recently, polystyrene microbeads covered with nanospikes have been reported to display anomalous dispersion in phobic media without surfactants. Inspired by this phenomenon, here magnetic microparticles attached with nanospikes were fabricated for enhanced separation of oil emulsions from water. In this design, the particle surfaces were functionalized to be superhydrophobic/superoleophilic for oil absorption, while the surface of the nanospikes prevented particle aggregation in water without compromising surface hydrophobicity. The magnetic spiky particles effectively absorbed oil spills on the water surface, and readily dispersed in water and offered facile cleaning of the oil emulsion. In contrast, hydrophobic microparticles without nanospikes aggregated in water limiting the particle-oil contact, while surfactant coating severely reduced particle hydrophobicity and oil absorption ability. Our work provides a unique application scope for the anomalous dispersity of microparticles and their potential opportunities in effective oil-water separation.
Considering Organic Carbon for Improved Predictions of Clay Content from Water Vapor Sorption
DEFF Research Database (Denmark)
Arthur, Emmanuel; Tuller, Markus; Moldrup, Per
2014-01-01
Accurate determination of the soil clay fraction (CF) is of crucial importance for characterization of numerous environmental, agricultural, and engineering processes. Because traditional methods for measurement of the CF are laborious and susceptible to errors, regression models relating the CF...... to water vapor sorption isotherms that can be rapidly measured with a fully automated vapor sorption analyzer are a viable alternative. In this presentation we evaluate the performance of recently developed regression models based on comparison with standard CF measurements for soils with high organic...... carbon (OC) content and propose a modification to improve prediction accuracy. Evaluation of the CF prediction accuracy for 29 soils with clay contents ranging from 6 to 25% and with OC contents from 2.0 to 8.4% showed that the models worked reasonably well for all soils when the OC content was below 2...
Organic or organometallic template mediated clay synthesis
Gregar, Kathleen C.; Winans, Randall E.; Botto, Robert E.
1994-01-01
A method for incorporating diverse Varieties of intercalants or templates directly during hydrothermal synthesis of clays such as hectorite or montmorillonite-type layer-silicate clays. For a hectorite layer-silicate clay, refluxing a gel of silica sol, magnesium hydroxide sol and lithium fluoride for two days in the presence of an organic or organometallic intercalant or template results in crystalline products containing either (a) organic dye molecules such as ethyl violet and methyl green, (b) dye molecules such as alcian blue that are based on a Cu(II)-phthalocyannine complex, or (c) transition metal complexes such as Ru(II)phenanthroline and Co(III)sepulchrate or (d) water-soluble porphyrins and metalloporphyrins. Montmorillonite-type clays are made by the method taught by U.S. Pat. No. 3,887,454 issued to Hickson, Jun. 13, 1975; however, a variety of intercalants or templates may be introduced. The intercalants or templates should have (i) water-solubility, (ii) positive charge, and (iii) thermal stability under moderately basic (pH 9-10) aqueous reflux conditions or hydrothermal pressurized conditions for the montmorillonite-type clays.
Role of clay as catalyst in Friedel–Craft alkylation
Indian Academy of Sciences (India)
component of soil and plays a crucial role in agriculture, po- tteries and ceramics ... platelets leading to dispersion of the catalyst samples was studied using XRD. .... Acidity of clay is a main factor for catalysis to take place. Among the various ...
International Nuclear Information System (INIS)
Gautschi, Andreas
2001-01-01
As part of the Swiss programme for high-level radioactive-waste, the National Cooperative for the Disposal of Radioactive Waste (Nagra) is currently investigating the Jurassic (Aalenian) Opalinus Clay as a potential host formation (Nagra 1988, 1994). The Opalinus Clay consists of indurated dark grey micaceous Clay-stones (shales) that are subdivided into several litho-stratigraphic units. Some of them contain thin sandy lenses, limestone concretions or siderite nodules. The clay mineral content ranges from 40-80 weight per cent (9-29% illite, 3-10% chlorite, 6-20% kaolinite and 4-22% illite/smectite mixed layers in the ratio 70/30). Other minerals are quartz (15-30%), calcite (6-40%), siderite (2-3%), ankerite (0-3%), feldspars (1-7%), pyrite (1-3%) and organic carbon (<1%). The total water content ranges from 4-19% (Mazurek 1999, Nagra 2001). Faults are mainly represented by fault gouge and fault breccias, partly associated with minor veins of calcite. A key question in safety assessment is, whether these faults may represent preferential pathways for radionuclide transport. An extensive hydrogeological data base - part of which derives from strongly tectonized geological environments - suggests that advective transport through faults in the Opalinus Clay at depth > 200 m is insignificant. This conclusion is also supported by independent evidence from clay pore water hydrochemical and isotopic data. The lack of hydrochemical anomalies and the lack of extensive mineral veining suggest that there was also no significant paleo-flow through such faults. These observations can only be reconciled with a strong self-sealing capacity of the faults. Therefore it is concluded, that reactivated existing faults or newly induced fractures will not act as pathways for significant fluid flow at anytime due to self-healing processes. These conclusions are supported by results from laboratory hydro-frac and flow-through tests, and from field-tests in the Mont Terri underground
International Nuclear Information System (INIS)
Rinnert, E.
2004-01-01
The study of the feasibility of a deep geological disposal facility conducted by ANDRA - the French national radioactive waste management agency -, requires the knowledge of water status and water content in clays. Thanks to an original lab-built device coupling vibrational spectroscopies and water adsorption isotherms, adsorbed water and clay's structure are described quantitatively and qualitatively. A multidisciplinary approach allows the description of hydration mechanisms and water molecules network in the inter lamellar space of synthetic saponites. The effects of density and nature of inter-foliar cations and the influence of temperature on hydration are presented. Using mechanisms and important parameters established on saponites, hydration of bentonite MX80 is carried out. In order to describe and quantify simultaneously two different water states, a simple but relevant method of spectra analysis was developed. (author)
Selbig, William R.; Balster, Nicholas
2010-01-01
The U.S. Geological Survey, in cooperation with a consortium of 19 cities, towns, and villages in Dane County, Wis., undertook a study to compare the capability of rain gardens with different vegetative species and soil types to infiltrate stormwater runoff from the roof of an adjacent structure. Two rain gardens, one planted with turf grass and the other with native prairie species, were constructed side-by-side in 2003 at two locations with different dominant soil types, either sand or clay. Each rain garden was sized to a ratio of approximately 5:1 contributing area to receiving area and to a depth of 0.5 foot. Each rain garden, regardless of vegetation or soil type, was capable of storing and infiltrating most of the runoff over the 5-year study period. Both rain gardens in sand, as well as the prairie rain garden in clay, retained and infiltrated 100 percent of all precipitation and snowmelt events during water years 2004-07. The turf rain garden in clay occasionally had runoff exceed its confining boundaries, but was still able to retain 96 percent of all precipitation and snowmelt events during the same time period. Precipitation intensity and number of antecedent dry days were important variables that influenced when the storage capacity of underlying soils would become saturated, which resulted in pooled water in the rain gardens. Because the rooftop area that drained runoff to each rain garden was approximately five times larger than the area of the rain garden itself, evapotranspiration was a small percentage of the annual water budget. For example, during water year 2005, the maximum evapotranspiration of total influent volume ranged from 21 percent for the turf rain garden in clay to 25 percent for the turf rain garden in sand, and the minimum ranged from 12 percent for the prairie rain garden in clay to 19 percent for the prairie rain garden in sand. Little to no runoff left each rain garden as effluent and a small percentage of runoff returned to the
A Study of Clay-Epoxy Nanocomposites Consisting of Unmodified Clay and Organo Clay
Directory of Open Access Journals (Sweden)
Graham Edward
2006-04-01
Full Text Available Clay-epoxy nanocomposites were synthesized from DGEBA resin and montmorillonite clay with an in-situ polymerization. One type of untreated clay and two types of organo clay were used to produce the nanocompsoites. The aims of this study were to examine the nanocomposite structure using different tools and to compare the results between the unmodified clay and modified clays as nanofillers. Although diffractogram in reflection mode did not show any apparent peak of both types of materials, the transmitted XRD (X-Ray Difraction graphs, DSC (Differential Scanning Calorimeter analysis and TEM (Transmission Electron Microscope images revealed that the modified clay-epoxy and unmodified clay-epoxy provides different results. Interestingly, the micrographs showed that some of the modified clay layers possessed non-exfoliated layers in the modified clay-epoxy nanocomposites. Clay aggregates and a hackle pattern were found from E-SEM images for both types of nanocomposite materials. It is shown that different tools should be used to determine the nanocomposite structure.
Clays causing adhesion with tool surfaces during mechanical tunnel driving
Spagnoli, G.; Fernández-Steeger, T.; Stanjek, H.; Feinendegen, M.; Post, C.; Azzam, R.
2009-04-01
During mechanical excavation with a tunnel boring machine (TBM) it is possible that clays stick to the cutting wheel and to other metal parts. The resulting delays in the progress of construction work, cause great economic damage and often disputes between the public awarding authorities and executing companies. One of the most important factors to reduce successfully the clay adhesion is the use of special polymers and foams. But why does the clay stick to the metal parts? A first step is to recognize which kind of clay mineralogy shows serious adhesion problems. The mechanical properties of clay and clay suspensions are primarily determined by surface chemistry and charge distribution at the interfaces, which in turn affect the arrangement of the clay structure. As we know, clay is a multi-phase material and its behaviour depends on numerous parameters such as: clay mineralogy, clay fraction, silt fraction, sand fraction, water content, water saturation, Atterberg limits, sticky limit, activity, cation exchange capacity, degree of consolidation and stress state. It is therefore likely that adhesion of clay on steel is also affected by these clay parameters. Samples of clay formations, which caused problems during tunnel driving, will be analyzed in laboratory. Mineralogical analyses (diffractometry, etc.) will be carried out to observe which minerals are responsible for adherence problems. To manipulate the physical properties, batch tests will be carried out in order to eliminate or reduce the adhesion on tool surfaces through variation of the zeta potential. Second step is the performance of vane shear tests on clay samples. Different pore fluid (distilled water, pure NaCl solution, ethanol and methanol) will be used to study the variation of the mechanical behaviour of clay depending on the dielectric constant of the fluids. This project is funded by the German Federal Ministry of Education and Research (BMBF) and the DFG (German Research Foundation) in the
Fixing of heavy metals by some inflated Tunisian clays
International Nuclear Information System (INIS)
Gharsalli, Jamel
2009-01-01
At the time of discharge of the water polluted in a natural environment and thanks to the properties of retention, adsorption and exchange of ions, clays constitute a natural barrier which will be able to limit the toxicity and the propagation of the pollutants. To contribute to the development of clays layers of Tunisia in the field of water treatments, we undertook with a mineralogical and physicochemical characterization of some inflating clays. The characteristics of these clays will be exploited for the study of the retention by adsorption of some heavy metals. The isotherms of adsorption, of heavy metals in aqueous solution by these natural clays before and after acid activation, are studied. The influence of several parameters on the fixing of heavy metals on clay such as the factors relating to the medium of adsorption (agitation, pH, time of contact, temperature. etc) and those relating to the adsorbent (mass, granulometry, impurities. etc) was studied in order to optimize the operating conditions of adsorptions.
Keurentjes, J.T.F.; Doornbusch, G.I.; Riet, van 't K.
1991-01-01
Fatty acids can be extracted from an oil phase by forming a dispersed phase of saponified fatty acids/water/isopropanol in oil. This dispersion can be separated in the two phases by two membranes of opposite polarity in series. In this study the separation of the water phase from the dispersion by a
Miller, Sandi G.; Scheiman, Daniel A; Kohlmman, Lee W.
2009-01-01
Many epoxy systems under consideration for composite pressure vessels are composed of toughened epoxy resins. In this work, epoxy blends containing both rigid aromatic and flexible aliphatic components were prepared, to model toughened systems, and determine the optimum route of silicate addition. Compositions were chosen such that both glassy and rubbery resins were obtained at room temperature. The physical properties of the nanocomposites varied with T(g) and silicate placement, however, nanocomposite T(g)s were observed which exceeded that of the base resin by greater than 10 C. The tensile strength of the glassy resin remained constant or decreased on the dispersion of clay while that of the rubbery material doubled. Selectively placing the clay in the aliphatic component of the rubbery blend resulted in a greater than 100% increase in material toughness.
Clays and Clay Minerals and their environmental application in Food Technology
del Hoyo Martínez, Carmen; Cuéllar Antequera, Jorge; Sánchez Escribano, Vicente; Solange Lozano García, Marina; Cutillas Díez, Raul
2013-04-01
The clay materials have led to numerous applications in the field of public health (del Hoyo, 2007; Volzone, 2007) having been demonstrated its effectiveness as adsorbents of all contaminants. Some biodegradable materials are used for for adsorption of chemical contaminants: lignins (Valderrabano et al., 2008) and also clays and clay minerals, whose colloidal properties, ease of generating structural changes, abundance in nature, and low cost make them very suitable for this kind of applications. Among the strategies used at present to preserve the quality of the water and this way to diminish the environmental risk that supposes the chemical pollution, stands out the use of adsorbents of under cost, already they are natural or modified, to immobilize these compounds and to avoid the pollution of the water with the consequent reduction of environmental and economic costs Thanks to the development of the science and the technology of the nourishment in the last 50 years, there have revealed itself several new substances that can fulfill beneficial functions in the food, and these substances, named food additives, are today within reach of all. The food additives recover a very important role in the complex nourishing supply. The additives fulfill several useful functions in the food, which often we give for sat. Nevertheless the widespread use of food additives in the food production also influences the public health. The food industries, which are very important for the economy, spill residues proved from its activity that they have to be controlled to evaluate the environmental impact and to offer the necessary information about the quantitative evaluation of the chemical risk of the use of food additives for the public health. We have studied the adsorption of several contaminants by natural or modified clays, searching their interaction mechanisms and the possible recycling of these materials for environmental purposes and prevention of the health. References
Magnetic resonance imaging of clays: swelling, sedimentation, dissolution
Dvinskikh, Sergey; Furo, Istvan
2010-05-01
While most magnetic resonance imaging (MRI) applications concern medical research, there is a rapidly increasing number of MRI studies in the field of environmental science and technology. In this presentation, MRI will be introduced from the latter perspective. While many processes in these areas are similar to those addressed in medical applications of MRI, parameters and experimental implementations are often quite different and, in many respects, far more demanding. This hinders direct transfer of existing methods developed for biomedical research, especially when facing the challenging task of obtaining spatially resolved quantitative information. In MRI investigation of soils, clays, and rocks, mainly water signal is detected, similarly to MRI of biological and medical samples. However, a strong variation of water mobility and a wide spread of water spin relaxation properties in these materials make it difficult to use standard MRI approaches. Other significant limitations can be identified as following: T2 relaxation and probe dead time effects; molecular diffusion artifacts; varying dielectric losses and induced currents in conductive samples; limited dynamic range; blurring artifacts accompanying drive for increasing sensitivity and/or imaging speed. Despite these limitations, by combining MRI techniques developed for solid and liquid states and using independent information on relaxation properties of water, interacting with the material of interest, true images of distributions of both water, material and molecular properties in a wide range of concentrations can be obtained. Examples of MRI application will be given in the areas of soil and mineral research where understanding water transport and erosion processes is one of the key challenges. Efforts in developing and adapting MRI approaches to study these kinds of systems will be outlined as well. Extensive studies of clay/water interaction have been carried out in order to provide a quantitative
Oil spill dispersants. Risk assessment for Swedish waters
International Nuclear Information System (INIS)
Lindgren, C.; Lager, H.; Fejes, J.
2001-12-01
IVL has compiled a list of the international usage of oil spill dispersants and presents the technical limitations with the use of such agents as well as the biological effects of these chemical products. IVL, has also conducted an analysis of the pros and cons to using dispersants against oil spills in waters and has applied this with a risk assessment of chemical methods to combat oil spills in the Kattegat and Skagerrak and the Baltic Sea
Concrete-Opalinus clay interaction
International Nuclear Information System (INIS)
Jenni, A.; Maeder, U.; Lerouge, C.; Gaboreau, S.; Schwyn, B.
2012-01-01
Document available in extended abstract form only. Designs for deep geologic disposal of radioactive waste foresee cementitious materials as structural elements, backfill or waste matrix. Therefore, studies of interactions between cement and all other materials involved are important. Interactions are mostly driven by chemical gradients in pore water and might lead to mineralogical alterations in the barrier system, which in turn influence properties like swelling pressure, permeability, or specific retention in case of clay materials. Existing laboratory and in-situ studies using clay-stone revealed significant alteration in both cement and clay-stone. Phase dissolution, precipitation, and carbonation, were found to cause an overall porosity increase in the cement with a possible decrease close to the interface, and clogging in the clay-stone [2]. Most of the work was done on cement pastes rather than concretes to avoid analytical complications caused by aggregates, and the scale of investigation was chosen in the range of centimetres rather than micrometers. The Cement-Clay Interaction (CI) experiment at the Mont Terri Underground Laboratory (St. Ursanne, Switzerland) aims at replicating some of the processes at interfaces to be expected.For this purpose, two vertical cylindrical boreholes (384 mm diameter, up to 10 m length) in Opalinus Clay (OPA) were filled with layers of three different concretes and bentonite. The concrete formulations are based on common aggregate content and grain size distributions, combined with three different cements: Portland cement (OPC), ESDRED cement especially designed for repository applications (40% of cement substituted with silica fume), and low alkali cement (LAC, containing slag and nano-silica).In this study, we present a characterisation of the three concrete-OPA interfaces after two years of alteration and deduce possible mechanisms. Backscattered electron (BE) imaging and energy dispersive spectrum (EDX) element mapping
Characterization of kaolin dispersion using acoustic and electroacoustic spectroscopy
Directory of Open Access Journals (Sweden)
Dohnalová Ž.
2008-01-01
Full Text Available The objective of this work is the investigation of the kaolin dispersion by the ultrasonic techniques. In contact with aqueous solution clay minerals show cation - exchange properties and certain degree of dissolution or rather selective leaching of components. The work is divided into two main parts - determination of zeta potential and particle size distribution. The first part is focused on measuring of zeta potential. Effects of concentration of solid, different kind of electrolytes (0.01 M KCl, 0.01 M MgCl2 and 0.01 M CaCl2, pH and temperature of the dispersions are investigated. The isoelectric points (IEP of kaolin suspension are about pH 4-5. Electrolytes containing monovalent cations such as K+ become zeta potential more negative compared to the values obtained with water. Such behavior is explained by the exchange of K+ ions with H+ ions in the system. When the electrolyte is formed by divalent cations such as Mg2+ or Ca2+, the values of zeta potential become less negative than zeta potential of kaolin in water. The second part is focused on the determination of particle size distribution with respect to dispersing conditions, such as the optimal dispersing agent (Na2SiO3, (NaPO36, Na4P2O7 or Busperse, time and power of ultrasonication and also the tracking of dispersion stability that is expressed by the measuring of particle size distribution during certain time period.
Clays in natural and engineered barriers for radioactive waste confinement
International Nuclear Information System (INIS)
2007-01-01
The meeting covers all topics concerning natural argillaceous geological barriers and the clay material based engineered barrier systems, investigated by means of: laboratory experiments on clay samples (new analytical developments), in situ experiments in underground research laboratories, mock-up demonstrations, natural analogues, as well as numerical modelling and global integration approaches (including up-scaling processes and treatment of uncertainties). The works presented deal with: examples of broad research programs (national or international) on the role of natural and artificial clay barriers for radionuclide confinement; clay-based repository concepts: repository designs, including technological and safety issues related to the use of clay for nuclear waste confinement; geology and clay characterisation: mineralogy, sedimentology, paleo-environment, diagenesis, dating techniques, discontinuities in rock clay, fracturing, self sealing processes, role of organic matter and microbiological processes; geochemistry: pore water geochemistry, clay thermodynamics, chemical retention, geochemical modelling, advanced isotopic geochemistry; mass transfer: water status and hydraulic properties in low permeability media, pore space geometry, water, solute and gas transfer processes, colloid mediated transport, large scale movements, long-term diffusion; alteration processes: oxidation effects, hydration-dehydration processes, response to thermal stress, iron-clay interactions, alkaline perturbation; geomechanics: thermo-hydro-mechanical behaviour of clay, rheological models, EDZ characterisation and evolution, coupled behaviour and models (HM, THM, THMC). A particular interest is given to potential contributions coming from fields of activities other than radioactive waste management, which take advantage of the confinement properties of the clay barrier (oil and gas industries, gas geological storage, CO 2 geological sequestration, chemical waste isolation
Clays in natural and engineered barriers for radioactive waste confinement
Energy Technology Data Exchange (ETDEWEB)
NONE
2007-07-01
The meeting covers all topics concerning natural argillaceous geological barriers and the clay material based engineered barrier systems, investigated by means of: laboratory experiments on clay samples (new analytical developments), in situ experiments in underground research laboratories, mock-up demonstrations, natural analogues, as well as numerical modelling and global integration approaches (including up-scaling processes and treatment of uncertainties). The works presented deal with: examples of broad research programs (national or international) on the role of natural and artificial clay barriers for radionuclide confinement; clay-based repository concepts: repository designs, including technological and safety issues related to the use of clay for nuclear waste confinement; geology and clay characterisation: mineralogy, sedimentology, paleo-environment, diagenesis, dating techniques, discontinuities in rock clay, fracturing, self sealing processes, role of organic matter and microbiological processes; geochemistry: pore water geochemistry, clay thermodynamics, chemical retention, geochemical modelling, advanced isotopic geochemistry; mass transfer: water status and hydraulic properties in low permeability media, pore space geometry, water, solute and gas transfer processes, colloid mediated transport, large scale movements, long-term diffusion; alteration processes: oxidation effects, hydration-dehydration processes, response to thermal stress, iron-clay interactions, alkaline perturbation; geomechanics: thermo-hydro-mechanical behaviour of clay, rheological models, EDZ characterisation and evolution, coupled behaviour and models (HM, THM, THMC). A particular interest is given to potential contributions coming from fields of activities other than radioactive waste management, which take advantage of the confinement properties of the clay barrier (oil and gas industries, gas geological storage, CO{sub 2} geological sequestration, chemical waste isolation
International Nuclear Information System (INIS)
Merceron, T.; Mossmann, J.R.; Neerdael, B.; Canniere, P. de; Beaucaire, C.; Toulhoat, P.; Daumas, S.; Bianchi, A.; Christen, R.
1993-01-01
Clay formations are candidate host environments to high level radioactive waste repository. The radioelements could be partially released from the waste into the host geological formation after a very long time. Understanding behaviour of the natural chemical species is considered as a fundamental prerequisite before the disturbed system will be studied. Additional laboratory studies are also essential in order to forecast, by analogy, the behaviour of radioelements released from the radioactive waste repository. The ARCHIMEDE-ARGILE project has two main goals. The first is to gain an understanding of the mechanisms of acquisition and regulation of the water chemistry in a clay environment. This step is essential to predict both the behaviour and the migration in solution of artificial elements which are initially absent in the clay formation. The second is to test and validate in clay the measured physico chemical parameters which are the basis for the geochemical modelling of the behaviour of the natural and artificial radioelements. The paper presents the main results previously obtained on granitic waters and the research strategy established for the ARCHIMEDE project. (authors). 2 figs., 2 refs
International Nuclear Information System (INIS)
Barbosa, Renata; Souza, Dayanne Diniz; Araujo, Edcleide Maria; Nobrega, Karine Castro; Melo, Tomas Jeferson Alves
2009-01-01
Paraiba is the main natural bentonite producing state of Brazil. Besides the advantage of abundance of bentonite clays, its transformation in organoclay is a simple method and there is only little study about the commercialization of Brazilian organoclays. In this work, Brazilian bentonite clay was organophilized with different quantity of a quaternary ammonium salt, such as 100, 125 and 150 wt.% in relation to Cationic Exchange Capacity (CEC) of the clay. The clays were characterized by X-ray Fluorescence (XRF), X-ray Diffraction (XRD), Thermogravimetry (TG) and Nuclear Magnetic Resonance (NMR). It was observed that with increasing amount of salt the degree of dispersion of the clay increased, leading in some cases to the delamination of the clay layers and its loss of thermal stability. (author)
LDPE/HDPE/Clay Nano composites: Effects of Compatibilizer on the Structure and Dielectric Response
International Nuclear Information System (INIS)
David, Z.E.; Ngo, A.D.
2013-01-01
PE/clay nano composites were prepared by mixing a commercially available premixed polyethylene/O-MMT master batch into a polyethylene blend matrix containing 80 wt% low-density polyethylene and 20 wt% high-density polyethylene with and without anhydride modified polyethylene (PE-MA) as the compatibilizer using a corotating twin-screw extruder. In this study, the effect of nano clay and compatibilizer on the structure and dielectric response of PE/clay nano composites has been investigated. The microstructure of PE/clay nano composites was characterized using wide-angle X-ray diffraction (WAXD) and a scanning electron microscope (SEM). Thermal properties were examined using differential scanning calorimetry (DSC). The dielectric response of neat PE was compared with that of PE/clay nano composite with and without the compatibilizer. The XRD and SEM results showed that the PE/O-MMT nano composite with the PE-MA compatibilizer was better dispersed. In the nano composite materials, two relaxation modes are detected in the dielectric losses. The first relaxation is due to a Maxwell-Wagner-Sillars interfacial polarization, and the second relaxation can be related to dipolar polarization. A relationship between the degree of dispersion and the relaxation rate f m ax of Maxwell-Wagner-Sillars was found and discussed.
Multi scale experimental study of water and ionic transport in porous charged media: clays
International Nuclear Information System (INIS)
Cadene, A.
2005-10-01
Clays are porous media of industrial interest. Due to their retention capacities and low permeability to water, they are the principal candidate for the conception of engineered barriers radioactive waste disposal. The main interest of this study is the experimental determination of the cationic and water dynamics in montmorillonite and fluoro-hectorite at low water contents This latter synthetic smectite has been used as a model clay to help the interpretation of the results issued from the first natural one. After a summary on the clayey system, this work reports the many experimental techniques (Atomic Force Microscopy, Photo-Correlation Spectroscopy, Micro-calorimetry, Powder Diffraction) used during the preliminary study concerning structural characterisation of the samples. The study of the sodic form of smectites with the use of a combination of quasi-elastic neutron scattering techniques (Time of Flight and Spin Echo) succeeded to water diffusion coefficients but also to a discernment of the limits of such techniques. Experiments with montmorillonite samples are in agreement with the simulations, so tending to a validation of the models. Experimental data obtained from synthetic hectorites will be in the near future compared to simulations In the last part, this work shows the application of Broad Band Dielectric Spectroscopy for the investigation of ionic dynamic in these porous media. Many models have been developed for the interpretation of the experimental raw data obtained with this technique. (author)
Sail or sink: novel behavioural adaptations on water in aerially dispersing species.
Hayashi, Morito; Bakkali, Mohammed; Hyde, Alexander; Goodacre, Sara L
2015-07-03
Long-distance dispersal events have the potential to shape species distributions and ecosystem diversity over large spatial scales, and to influence processes such as population persistence and the pace and scale of invasion. How such dispersal strategies have evolved and are maintained within species is, however, often unclear. We have studied long-distance dispersal in a range of pest-controlling terrestrial spiders that are important predators within agricultural ecosystems. These species persist in heterogeneous environments through their ability to re-colonise vacant habitat by repeated long-distance aerial dispersal ("ballooning") using spun silk lines. Individuals are strictly terrestrial, are not thought to tolerate landing on water, and have no control over where they land once airborne. Their tendency to spread via aerial dispersal has thus been thought to be limited by the costs of encountering water, which is a frequent hazard in the landscape. In our study we find that ballooning in a subset of individuals from two groups of widely-distributed and phylogenetically distinct terrestrial spiders (linyphiids and one tetragnathid) is associated with a hitherto undescribed ability of those same individuals to survive encounters with both fresh and marine water. Individuals that showed a high tendency to adopt 'ballooning' behaviour adopted elaborate postures to seemingly take advantage of the wind current whilst on the water surface. The ability of individuals capable of long-distance aerial dispersal to survive encounters with water allows them to disperse repeatedly, thereby increasing the pace and spatial scale over which they can spread and subsequently exert an influence on the ecosystems into which they migrate. The potential for genetic connectivity between populations, which can influence the rate of localized adaptation, thus exists over much larger geographic scales than previously thought. Newly available habitat may be particularly influenced
Removal of waterborne microorganisms by filtration using clay-polymer complexes.
Undabeytia, Tomas; Posada, Rosa; Nir, Shlomo; Galindo, Irene; Laiz, Leonila; Saiz-Jimenez, Cesareo; Morillo, Esmeralda
2014-08-30
Clay-polymer composites were designed for use in filtration processes for disinfection during the course of water purification. The composites were formed by sorption of polymers based on starch modified with quaternary ammonium ethers onto the negatively charged clay mineral bentonite. The performance of the clay-polymer complexes in removal of bacteria was strongly dependent on the conformation adopted by the polycation on the clay surface, the charge density of the polycation itself and the ratio between the concentrations of clay and polymer used during the sorption process. The antimicrobial effect exerted by the clay-polymer system was due to the cationic monomers adsorbed on the clay surface, which resulted in a positive surface potential of the complexes and charge reversal. Clay-polymer complexes were more toxic to bacteria than the polymers alone. Filtration employing our optimal clay-polymer composite yielded 100% removal of bacteria after the passage of 3L, whereas an equivalent filter with granular activated carbon (GAC) hardly yielded removal of bacteria after 0.5L. Regeneration of clay-polymer complexes saturated with bacteria was demonstrated. Modeling of the filtration processes permitted to optimize the design of filters and estimation of experimental conditions for purifying large water volumes in short periods. Copyright © 2014 Elsevier B.V. All rights reserved.
Nafion–clay hybrids with a network structure
Burgaz, Engin; Lian, Huiqin; Alonso, Rafael Herrera; Estevez, Luis; Kelarakis, Antonios; Giannelis, Emmanuel P.
2009-01-01
Nafion-clay hybrid membranes with a unique microstructure were synthesized using a fundamentally new approach. The new approach is based on depletion aggregation of suspended particles - a well-known phenomenon in colloids. For certain concentrations of clay and polymer, addition of Nafion solution to clay suspensions in water leads to a gel. Using Cryo-TEM we show that the clay particles in the hybrid gels form a network structure with an average cell size in the order of 500 nm. The hybrid gels are subsequently cast to produce hybrid Nafion-clay membranes. Compared to pure Nafion the swelling of the hybrid membranes in water and methanol is dramatically reduced while their selectivity (ratio of conductivity over permeability) increases. The small decrease of ionic conductivity for the hybrid membranes is more than compensated by the large decrease in methanol permeability. Lastly the hybrid membranes are much stiffer and can withstand higher temperatures compared to pure Nafion. Both of these characteristics are highly desirable for use in fuel cell applications, since a) they will allow the use of a thinner membrane circumventing problems associated with the membrane resistance and b) enable high temperature applications. © 2009 Elsevier Ltd. All rights reserved.
Nafion–clay hybrids with a network structure
Burgaz, Engin
2009-05-01
Nafion-clay hybrid membranes with a unique microstructure were synthesized using a fundamentally new approach. The new approach is based on depletion aggregation of suspended particles - a well-known phenomenon in colloids. For certain concentrations of clay and polymer, addition of Nafion solution to clay suspensions in water leads to a gel. Using Cryo-TEM we show that the clay particles in the hybrid gels form a network structure with an average cell size in the order of 500 nm. The hybrid gels are subsequently cast to produce hybrid Nafion-clay membranes. Compared to pure Nafion the swelling of the hybrid membranes in water and methanol is dramatically reduced while their selectivity (ratio of conductivity over permeability) increases. The small decrease of ionic conductivity for the hybrid membranes is more than compensated by the large decrease in methanol permeability. Lastly the hybrid membranes are much stiffer and can withstand higher temperatures compared to pure Nafion. Both of these characteristics are highly desirable for use in fuel cell applications, since a) they will allow the use of a thinner membrane circumventing problems associated with the membrane resistance and b) enable high temperature applications. © 2009 Elsevier Ltd. All rights reserved.
Directory of Open Access Journals (Sweden)
Kevin Magniez
2013-08-01
Full Text Available The role of processing conditions and intercalant chemistry in montmorillonite clays on the dispersion, morphology and mechanical properties of two epoxy/clay nanocomposite systems was investigated in this paper. This work highlights the importance of employing complementary techniques (X-ray diffraction, small angle X-ray scattering, optical microscopy and transmission electron microscopy to correlate nanomorphology to macroscale properties. Materials were prepared using an out of autoclave manufacturing process equipped to generate rapid heating rates and mechanical vibration. The results suggested that the quaternary ammonium surfactant on C30B clay reacted with the epoxy during cure, while the primary ammonium surfactant (I.30E catalysed the polymerisation reaction. These effects led to important differences in nanocomposite clay morphologies. The use of mechanical vibration at 4 Hz prior to matrix gelation was found to facilitate clay dispersion and to reduce the area fraction of I.30E clay agglomerates in addition to increasing flexural strength by over 40%.
Nuhiji, Betime; Attard, Darren; Thorogood, Gordon; Hanley, Tracey; Magniez, Kevin; Bungur, Jenny; Fox, Bronwyn
2013-01-01
The role of processing conditions and intercalant chemistry in montmorillonite clays on the dispersion, morphology and mechanical properties of two epoxy/clay nanocomposite systems was investigated in this paper. This work highlights the importance of employing complementary techniques (X-ray diffraction, small angle X-ray scattering, optical microscopy and transmission electron microscopy) to correlate nanomorphology to macroscale properties. Materials were prepared using an out of autoclave manufacturing process equipped to generate rapid heating rates and mechanical vibration. The results suggested that the quaternary ammonium surfactant on C30B clay reacted with the epoxy during cure, while the primary ammonium surfactant (I.30E) catalysed the polymerisation reaction. These effects led to important differences in nanocomposite clay morphologies. The use of mechanical vibration at 4 Hz prior to matrix gelation was found to facilitate clay dispersion and to reduce the area fraction of I.30E clay agglomerates in addition to increasing flexural strength by over 40%. PMID:28811457
Magnesium incorporated bentonite clay for defluoridation of drinking water
International Nuclear Information System (INIS)
Thakre, Dilip; Rayalu, Sadhana; Kawade, Raju; Meshram, Siddharth; Subrt, J.; Labhsetwar, Nitin
2010-01-01
Low cost bentonite clay was chemically modified using magnesium chloride in order to enhance its fluoride removal capacity. The magnesium incorporated bentonite (MB) was characterized by using XRD and SEM techniques. Batch adsorption experiments were conducted to study and optimize various operational parameters such as adsorbent dose, contact time, pH, effect of co-ions and initial fluoride concentration. It was observed that the MB works effectively over wide range of pH and showed a maximum fluoride removal capacity of 2.26 mg g -1 at an initial fluoride concentration of 5 mg L -1 , which is much better than the unmodified bentonite. The experimental data fitted well into Langmuir adsorption isotherm and follows pseudo-first-order kinetics. Thermodynamic study suggests that fluoride adsorption on MB is reasonably spontaneous and an endothermic process. MB showed significantly high fluoride removal in synthetic water as compared to field water. Desorption study of MB suggest that almost all the loaded fluoride was desorbed (∼97%) using 1 M NaOH solution however maximum fluoride removal decreases from 95.47 to 73 (%) after regeneration. From the experimental results, it may be inferred that chemical modification enhances the fluoride removal efficiency of bentonite and it works as an effective adsorbent for defluoridation of water.
Energy Technology Data Exchange (ETDEWEB)
Mazurek, M. [Institute of Geological Sciences, University of Berne, Berne (Switzerland); Haller de, A. [Earth and Environmental Sciences, University of Geneva, Geneva (Switzerland)
2017-04-15
Data pertinent to pore-water composition in Opalinus Clay in the Mont Terri and Mont Russelin anticlines have been collected over the last 20 years from long-term in situ pore-water sampling in dedicated boreholes, from laboratory analyses on drill cores and from the geochemical characteristics of vein infills. Together with independent knowledge on regional geology, an attempt is made here to constrain the geochemical evolution of the pore-waters. Following basin inversion and the establishment of continental conditions in the late Cretaceous, the Malm limestones acted as a fresh-water upper boundary leading to progressive out-diffusion of salinity from the originally marine pore-waters of the Jurassic low-permeability sequence. Model calculations suggest that at the end of the Palaeogene, pore-water salinity in Opalinus Clay was about half the original value. In the Chattian/Aquitanian, partial evaporation of sea-water occurred. It is postulated that brines diffused into the underlying sequence over a period of several Myr, resulting in an increase of salinity in Opalinus Clay to levels observed today. This hypothesis is further supported by the isotopic signatures of SO{sub 4}{sup 2-} and {sup 87}Sr/{sup 86}Sr in current pore-waters. These are not simple binary mixtures of sea and meteoric water, but their Cl{sup -} and stable water-isotope signatures can be potentially explained by a component of partially evaporated sea-water. After the re-establishment of fresh-water conditions on the surface and the formation of the Jura Fold and Thrust Belt, erosion caused the activation of aquifers embedding the low-permeability sequence, leading to the curved profiles of various pore-water tracers that are observed today. Fluid flow triggered by deformation events during thrusting and folding of the anticlines occurred and is documented by infrequent vein infills in major fault structures. However, this flow was spatially focussed and of limited duration and so did not
Yang, Liping; Phua, Si Lei; Teo, Jun Kai Herman; Toh, Cher Ling; Lau, Soo Khim; Ma, Jan; Lu, Xuehong
2011-08-01
A facile biomimetic method was developed to enhance the interfacial interaction in polymer-layered silicate nanocomposites. By mimicking mussel adhesive proteins, a monolayer of polydopamine was constructed on clay surface by a controllable coating method. The modified clay (D-clay) was incorporated into an epoxy resin, it is found that the strong interfacial interactions brought by the polydopamine benefits not only the dispersion of the D-clay in the epoxy but also the effective interfacial stress transfer, leading to greatly improved thermomechanical properties at very low inorganic loadings. Rheological and infrared spectroscopic studies show that the interfacial interactions between the D-clay and epoxy are dominated by the hydrogen bonds between the catechol-enriched polydopamine and the epoxy.
Enhanced thermal conductivity of nano-SiC dispersed water based ...
Indian Academy of Sciences (India)
Silicon carbide (SiC) nanoparticle dispersed water based nanofluids were prepared using up to 0.1 vol% of nanoparticles. Use of suitable stirring routine ensured uniformity and stability of dispersion. Thermal conductivity ratio of nanofluid measured using transient hot wire device shows a significant increase of up to 12% ...
California Bearing Ratio (CBR) test on stabilization of clay with lime addition
Hastuty, I. P.; Roesyanto; Limbong, M. N.; Oberlyn, S. J.
2018-02-01
Clay is a type of soil with particles of certain minerals giving plastic properties when mixed with water. Soil has an important role in a construction, besides as a building material in a wide variety of civil engineering works, soil is also used as supporting foundation of the building. Basic properties of clay are rock-solid in dry and plastic with medium water content. In high water content, clay becomes sticky like (cohesive) and soften. Therefore, clay stabilization is necessary to repair soil’s mechanical properties. In this research, lime is use as a stabilizer that contains the Ca+ element to bond bigger particles. Lime used is slaked lime Ca(OH)2. Clay used has liquid limitation (LL) value of 47.33%, plasticity index of 29.88% and CBR value 6.29. The results explain about 10% lime mixture variation gives the optimum stabilized clay with CBR value of 8.75%.
International Nuclear Information System (INIS)
Morelli, Fernanda C.; Ruvolo Filho, Adhemar
2010-01-01
In this work nano composites were prepared from polypropylene, graft polypropylene with maleic anhydride as compatibilizer and organophilic montmorillonite Cloisite 20A with concentrations of 1.5, 2.5, 5.0 and 7.5% clay. The mixture was made in the melt state using a twin screw extruder. The materials were characterized by X ray diffraction, infrared spectroscopy with Fourier transform and analysis of water vapor permeation. The results of X ray diffraction and absorption infrared spectroscopy indicates the formation of nano composites with structures probably exfoliate and or intercalated for concentrations of 1.5 and 2.5% clay, and provided a marked decrease in the water permeability, corroborating with other analyses. (author)
Morariu, Simona; Bercea, Maria
2012-01-12
The viscoelastic properties of 2% poly(ethylene glycol) aqueous solutions containing Laponite RD from 1% to 4% were investigated by oscillatory and flow measurements in the temperature range of 15-40 °C. The enhancement of the clay content from mixture causes the increase of the viscoelastic moduli and the change of the flow from liquid-like behavior (Maxwellian fluid) to a solid-like one at a set temperature. The longest relaxation times (τ(1)) of the mixtures with low clay concentrations (1% and 2%) are not affected by changes in temperature unlike the samples having high content of clay at which τ(1) increases above 30 °C and below 17.5 °C. The characteristic behavior of the mixtures with the high clay concentration could be explained by considering the effect of Brownian motion on the network structure formed in these dispersions as well as by the poor solubility of poly(ethylene glycol) in water at high temperatures. The flow activation energy was determined and discussed. An abrupt increase of the flow activation energy was evidenced between 2% and 3% Laponite RD. The rheological measurements carried out at different rest times showed a decrease of the gelation time from 1 week to 2 h when the clay concentration increases from 2% to 4%. The aging kinetics of poly(ethylene glycol)/Laponite RD/water mixtures, investigated at 25 °C, revealed the increase of the viscosity-rate kinetic constant by increasing the clay concentration.
Towards an assessment of colloid transport in undisturbed clay stone
International Nuclear Information System (INIS)
Durce, D.; Landesman, C.; Grambow, B.; Giffaut, E.
2010-01-01
Document available in abstract form only. Full text of publication follows: Colloids are known as a potentially important transport vector for sparingly soluble radionuclides in natural water environments. For assessing the mass transfer resistance of the Callovo-Oxfordian clay rock formation for colloid transport, a series of percolation experiments have been performed, using high pressure stainless steel advection cells of different diameters containing clay cores machined to about 50 μm of accuracy to the inner diameter of the cells. Synthetic clay pore water was pushed by a high pressure syringe pump across the clay core. In order to assess the cut-off size for colloid transport, molecules of different molecular weight were injected. C 14 labeled polymaleic acid (PMA) of sizes of 2 and 50 kDa were used. The effect of clay permeability, of water flow rate (injection pressure) and of ionic strength was studied. Low ionic strength experiments (I = 0.001) were realized by replacing the pore water by advective displacement with the required composition. Clay rock permeabilities were between 10 -12 and 10 -14 m/s. Hydrodynamic parameters were determined by HTO and 36 Cl injection. The results show already at 2 kDa and a permeability of 10 -12 m/s strong retention by partial filtration. The experimental results were modeled using simple chromatographic theory. (authors)
Energy Technology Data Exchange (ETDEWEB)
Ceron Loayza, Maria L., E-mail: malucelo@hotmail.com; Bravo Cabrejos, Jorge A.; Mejia Santillan, Mirian E. [Universidad Nacional Mayor de San Marcos, Laboratorio de Analisis de Suelos, Laboratorio de Espectroscopia Moessbauer, Facultad de Ciencias Fisicas (Peru)
2011-11-15
The purpose of this work is to report the advances in the elemental and structural characterization of the clay fraction of soils from the terraces of the Moray Archaeological site, located 38 km north of the city of Cusco, Cusco Region. One sample was collected from each of the twelve terraces of this site and its clay fraction was separated by sedimentation. Previously the pH of the raw samples was measured resulting that all of the samples were from alkaline to strongly alkaline. Energy dispersive X-ray fluorescence (EDXRF) was used for the elemental characterization, and X-ray diffractometry (XRD) and transmission Moessbauer spectroscopy (TMS), using the {gamma} 14.4 keV nuclear resonance transition in {sup 57}Fe, were used for the structural characterization of the clays and clay minerals present in each sample. The EDXRF analyses of all the samples show the presence of relatively high concentrations of sulfur in some of the samples and relatively high concentrations of calcium in all of the samples, which may be related to the high alkalinity of the samples. By XRD it is observed the presence of quartz, calcite, gypsum, cronstedtite, 2:1 phyllosilicates, and iron oxides. The mineralogical analysis of Fe by TMS shows that it is present in the form of hematite and occupying Fe{sup 2 + } and Fe{sup 3 + } sites in phyllosilicates, cronstedtite, and other minerals not yet identified.
Development of polymer nanocomposites with regional bentonite clay
International Nuclear Information System (INIS)
Araujo, Edcleide M.; Leite, Amanda M.D.; Paz, Rene A. da; Medeiros, Keila M. de; Melo, Tomas J.A.; Barbosa, Josiane D.V.; Barbosa, Renata
2011-01-01
nanocomposites with regional bentonite clay were prepared by melt intercalation technique. The clays were studied without modification and modified with four quaternary ammonium salts. It was evidenced by X-ray diffraction that salts were incorporated into the clay structure thus confirming its organophilization. The nanocomposites were evaluated by means of thermal mechanic and flammability tests where presented properties significantly improved their pure polymers. The process of biodegradation of obtained bio nanocomposites was accelerated by the presence of clay. The produced membranes from nanocomposites have potential in the oil-water separation. (author)
Directory of Open Access Journals (Sweden)
E. N. Cabrera Álvarez
2012-01-01
Full Text Available In situ anionic homo- and copolymerization of caprolactam (CL and laurolactam (LL with sodium montmorillonite clay (NaMMT was carried out using two different initiators, sodium caprolactamate (CLNa and caprolactam magnesium bromide (CLMgBr. Degree of conversion and final molecular weight were used to assess the advancement and efficiency of the polymerization reaction and X-ray diffraction and electron microscopy were used to evaluate the sodium montmorillonite clay intercalation/exfoliation. The use of CLNa as initiator produced a higher conversion degree and molecular weight than the use of CLMgBr. Through DSC, it was observed that CLNa and CLMgBr tended to produce random and block copolymer structures, respectively, and either random or block, this eventually has an effect on the clay dispersion within the polymer matrix. In all cases, increasing the LL content produced a decrease in the conversion degree and in the molecular weight of the resulting polymer.
Structure and crystallinity of water dispersible photoactive nanoparticles for organic solar cells
DEFF Research Database (Denmark)
Pedersen, Emil Bøje Lind; Pedersen, M.C.; Simonsen, Søren Bredmose
2015-01-01
Water based inks would be a strong advantage for large scale production of organic photovoltaic devices. Formation of water dispersible nanoparticles produced by the Landfester method is a promising route to achieve such inks. We provide new insights into the key ink properties of poly(3-hexylthi......Water based inks would be a strong advantage for large scale production of organic photovoltaic devices. Formation of water dispersible nanoparticles produced by the Landfester method is a promising route to achieve such inks. We provide new insights into the key ink properties of poly(3......-hexylthiophene) (P3HT) and [6,6]-phenyl-C61-butyric acid methyl ester (PCBM) nanoparticles such as the internal structure and crystallinity of the dispersed nanoparticles and the previously unreported drastic changes that occur when the inks are cast into a film. We observe through transmission electron...
Glass transition and relaxation dynamics of propylene glycol-water solutions confined in clay
Elamin, Khalid; Björklund, Jimmy; Nyhlén, Fredrik; Yttergren, Madeleine; Mârtensson, Lena; Swenson, Jan
2014-07-01
The molecular dynamics of aqueous solutions of propylene glycol (PG) and propylene glycol methylether (PGME) confined in a two-dimensional layer-structured Na-vermiculite clay has been studied by broadband dielectric spectroscopy and differential scanning calorimetry. As typical for liquids in confined geometries the intensity of the cooperative α-relaxation becomes considerably more suppressed than the more local β-like relaxation processes. In fact, at high water contents the calorimetric glass transition and related structural α-relaxation cannot even be observed, due to the confinement. Thus, the intensity of the viscosity related α-relaxation is dramatically reduced, but its time scale as well as the related glass transition temperature Tg are for both systems only weakly influenced by the confinement. In the case of the PGME-water solutions it is an important finding since in the corresponding bulk system a pronounced non-monotonic concentration dependence of the glass transition related dynamics has been observed due to the growth of hydrogen bonded relaxing entities of water bridging between PGME molecules [J. Sjöström, J. Mattsson, R. Bergman, and J. Swenson, Phys. Chem. B 115, 10013 (2011)]. The present results suggest that the same type of structural entities are formed in the quasi-two-dimensional space between the clay platelets. It is also observed that the main water relaxation cannot be distinguished from the β-relaxation of PG or PGME in the concentration range up to intermediate water contents. This suggests that these two processes are coupled and that the water molecules affect the time scale of the β-relaxation. However, this is most likely true also for the corresponding bulk solutions, which exhibit similar time scales of this combined relaxation process below Tg. Finally, it is found that at higher water contents the water relaxation does not merge with, or follow, the α-relaxation above Tg, but instead crosses the
International Nuclear Information System (INIS)
Huang Jianhua; Liu Yuanfa; Jin Qingzhe; Wang Xingguo; Yang Jun
2007-01-01
The removal of water-soluble Reactive Red MF-3B from aqueous media by sonication-surfactant-modified attapulgite clay was studied in a batch system. The surfactant used was octodecyl trimethyl ammonium chloride (OTMAC). Adsorbent characterizations were investigated using X-ray diffraction, infrared spectroscopy, and surface area analysis. The effects of pH, contact time, initial solute concentration, adsorbent dose, and temperature on the adsorption of Reactive Red MF-3B onto modified clay were investigated. On the basis of kinetic studies, specific rate constants involved in the processes were calculated and second-order adsorption kinetics was observed in the case. Film diffusion was found to be the rate-limiting step. Reactive Red MF-3B adsorption was found to increase with increase temperature. The Reactive Red MF-3B equilibrium adsorption data were fitted to Freundlich and Langmuir isotherm models, the former being found to provide the better fit of the experimental data. Thermodynamic parameters were calculated. From the results it can be concluded that the surfactant-modified clay could be a good adsorbent for treating Reactive Red MF-3B-contaminated waters
International Nuclear Information System (INIS)
2013-01-01
A wide spectrum of argillaceous media are being considered in Nuclear Energy Agency (NEA) member countries as potential host rocks for the final, safe disposal of radioactive waste, and/or as major constituent of repository systems in which wastes will be emplaced. In this context, the NEA established the Working Group on the 'Characterisation, the Understanding and the Performance of Argillaceous Rocks as Repository Host Formations' in 1990, informally known as the 'Clay Club'. The Clay Club examines various argillaceous rocks that are being considered for the underground disposal of radioactive waste, ranging from soft clays to indurated shales. Very generally speaking, these clay rocks are composed of fine-grained minerals showing pore sizes from < 2 nm (micropores) up to > 50 nm (macro-pores). The water flow, solute transport and mechanical properties are largely determined by this microstructure, the spatial arrangement of the minerals and the chemical pore water composition. Examples include anion accessible ('geochemical') porosity and macroscopic membrane effects (chemical osmosis, hyper-filtration), geomechanical properties and the characteristics of two-phase flow properties (relevant for gas transport). At the current level of knowledge, there is a strong need to improve the nanoscale description of the phenomena observed at a more macroscopic scale. However, based on the scale of individual clay-minerals and pore sizes, for most of the imaging techniques this resolution is a clear challenge. The workshop, hosted by the Institute for Nuclear Waste Disposal (INE), Karlsruhe Institute of Technology (KIT) in the Akademiehotel Karlsruhe (Germany) from 6 to 8 September 2011, was intended to give, inter alia, a discussion platform on: - The current state-of-the-art of different spectro-microscopic methods - New developments addressing the above mentioned knowledge gaps in clays. - The perception of the interplay between geometry
Energy Technology Data Exchange (ETDEWEB)
Medeiros, R.C.A. de; Amorim, L.V.; Santana, L.N. de L. [Universidade Federal de Campina Grande (UFCG), PB (Brazil)], e-mail: nalealves@hotmail.com
2008-07-01
In the onshore drilling of wells are commonly used aqueous fluids containing bentonite clays. However, to perform their functions generally there is the necessity of additives to drilling fluids, like viscositying, filtered reducer and lubricant. Thus, this work aims to develop water and clay base drilling fluids with low solid text, and with polymeric and lubricants additives. Were studied a sample of industrialized sodium bentonite clays, three polymeric compounds in the ternary form and a sample of lubricant, in different concentrations. Were determined the flow curves, the apparent and plastic viscosities, the yield limit and gel force in Fann 35A viscometer, the filtered volume in API filter-press and the lubricity coefficient in Ofite lubricimeter. The results showed that the fluid had pseudoplastic behavior, the polymeric additives adjusts their rheological properties and filtration and the addition of 1% of lubricant is sufficient to improve the lubricity of fluids. (author)
Chemical processes at the surface of various clays on acid-base titration
International Nuclear Information System (INIS)
Park, K. K.; Park, Y. S.; Jung, E. C.
2010-01-01
The chemical reaction of radionuclides at the interface between groundwater and geological mineral is an important process determining their retardation of transport through groundwater flow in a nuclear waste disposal. Clay minerals are major components of soil and argillaceous rock, and some of them are considered to be important base materials in the design of high-level nuclear waste repository due to their large swelling, low-permeability, large surface area, and strong and large sorption of radionuclides. Clay materials are phyllosilicates containing accessory minerals such as metal oxides, hydroxides, oxyhydroxides. Their structures are condensed 1:1 or 2:1 layers of tetrahedral SiO 3/2 OH and octahedral Al(OH) 6/2 sheets. An accurate knowledge about the properties of clay surface is required as a parameter for a long-term estimation of radionuclide retardation effects. Electric surface charge is a primary property determining ion exchange and surface complexation of radionuclides on its surface. The sources of electric surface charge are a permanent structural negative charge on a basal plane and a dissociable charge at an edge surface. Investigation of proton sorption is a prerequisite to the understanding of radionuclide sorption. The reactions on a permanently charged site and on an edge site are measured by an electrokinetic measurement and by potentiometric titration, respectively. However, side reactions such as complexation, proton/cation exchange, dissolution, hydrolysis, precipitation and re adsorption, and the reaction of secondary minerals hinder an experimental measurement of accurate acid-base properties. This presentation describes the pH change on dispersing various clays in water and adding acid, base or Eu(III) ion to these solutions, and the effect of Eu(III) ion on acid-base titration of clay solutions
Chemical processes at the surface of various clays on acid-base titration
Energy Technology Data Exchange (ETDEWEB)
Park, K. K.; Park, Y. S.; Jung, E. C. [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)
2010-10-15
The chemical reaction of radionuclides at the interface between groundwater and geological mineral is an important process determining their retardation of transport through groundwater flow in a nuclear waste disposal. Clay minerals are major components of soil and argillaceous rock, and some of them are considered to be important base materials in the design of high-level nuclear waste repository due to their large swelling, low-permeability, large surface area, and strong and large sorption of radionuclides. Clay materials are phyllosilicates containing accessory minerals such as metal oxides, hydroxides, oxyhydroxides. Their structures are condensed 1:1 or 2:1 layers of tetrahedral SiO{sub 3/2}OH and octahedral Al(OH){sub 6/2} sheets. An accurate knowledge about the properties of clay surface is required as a parameter for a long-term estimation of radionuclide retardation effects. Electric surface charge is a primary property determining ion exchange and surface complexation of radionuclides on its surface. The sources of electric surface charge are a permanent structural negative charge on a basal plane and a dissociable charge at an edge surface. Investigation of proton sorption is a prerequisite to the understanding of radionuclide sorption. The reactions on a permanently charged site and on an edge site are measured by an electrokinetic measurement and by potentiometric titration, respectively. However, side reactions such as complexation, proton/cation exchange, dissolution, hydrolysis, precipitation and re adsorption, and the reaction of secondary minerals hinder an experimental measurement of accurate acid-base properties. This presentation describes the pH change on dispersing various clays in water and adding acid, base or Eu(III) ion to these solutions, and the effect of Eu(III) ion on acid-base titration of clay solutions
Iodide Sorption to Clays and the Relationship to Surface Charge and Clay Texture - 12356
Energy Technology Data Exchange (ETDEWEB)
Miller, Andrew; Kruichiak, Jessica; Tellez, Hernesto; Wang, Yifeng [Sandia National Laboratories, Albuquerque, NM 87185 (United States)
2012-07-01
Iodine is assumed to behave conservatively in clay barriers around nuclear waste repositories and in natural sediments. Batch experiments tend to show little to no sorption, while in column experiments iodine is often retarded relative to tritiated water. Current surface complexation theory cannot account for negatively charged ion sorption to a negatively charged clay particle. Surface protonation and iodide sorption to clay minerals were examined using surface titrations and batch sorption experiments with a suite of clay minerals. Surface titrations were completed spanning a range of both pH values and ionic strengths. For reference, similar titrations were performed on pure forms of an Al-O powder. The titration curves were deconvoluted to attain the pKa distribution for each material at each ionic strength. The pKa distribution for the Al-O shows two distinct peaks at 4.8 and 7.5, which are invariant with ionic strength. The pKa distribution of clays was highly variable between the different minerals and as a function of ionic strength. Iodide sorption experiments were completed at high solid:solution ratios to exacerbate sorption properties. Palygorskite and kaolinite had the highest amount of iodide sorption and montmorillonite had the least. (authors)
Discobiol program : investigation of dispersant use in coastal and estuarine waters
Energy Technology Data Exchange (ETDEWEB)
Merlin, F.X.; Le Floch, S.; Dussauze, M. [Cedre, Brest Cedex (France); Theron, M. [Brest Univ., European University of Britanny, Rennes (France); Quentel, C. [AFSSA, French Food Safety Agency, Paris (France); Thomas, H. [LIENS, CNRS-Univ. of La Rochelle, La Rochelle Cedex (France)
2009-07-01
This paper reported on the Discobiol work program designed to acquire comparable information on the impact of mechanically and chemically dispersed oil on different habitats and resources, particularly in estuaries or close to bays. The study involved 3 phases for the analysis of lethal and sub-lethal effects in pelagic and benthic communities, notably organisms in the water column, mudflats and salt marshes. The ultimate objective was to use the information to make recommendations regarding the use of dispersants in these 3 areas. Dispersants are known to be effective for offshore oil spill response when dilution conditions are high and dispersed oil concentrations decrease rapidly below levels that could harm the environment. However, dilution can be restricted in coastal areas, thus limiting the use of dispersant. All the tests conducted in this study were conducted using brut Arabian light oil that was pre-evaporated to simulate realistic conditions. The study examined whether the presence of oil leads to different effects than the control and whether the chemically dispersed oil gave different effects than the mechanical dispersion. The comparison with chemical dispersion in clear sea water examined whether the presence of suspended materials change the effect of the chemical dispersion. Results for the different phases of the project were presented. The preliminary results tend to open the use of chemical dispersion of oil slicks in coastal areas. The mixture of dispersant plus oil seems to be less detrimental than oil alone, particularly for turbot. The final conclusion regarding chemical dispersion of oil slicks in coastal areas will have to be formulated at the end of the project because coastal ecosystems depend on biotic and abiotic factors. The final phase will take place in a realistic environment in a salt marsh ecosystem at La Rochelle, France. 6 refs., 6 tabs., 6 figs.
Discobiol program : investigation of dispersant use in coastal and estuarine waters
International Nuclear Information System (INIS)
Merlin, F.X.; Le Floch, S.; Dussauze, M.; Theron, M.; Quentel, C.; Thomas, H.
2009-01-01
This paper reported on the Discobiol work program designed to acquire comparable information on the impact of mechanically and chemically dispersed oil on different habitats and resources, particularly in estuaries or close to bays. The study involved 3 phases for the analysis of lethal and sub-lethal effects in pelagic and benthic communities, notably organisms in the water column, mudflats and salt marshes. The ultimate objective was to use the information to make recommendations regarding the use of dispersants in these 3 areas. Dispersants are known to be effective for offshore oil spill response when dilution conditions are high and dispersed oil concentrations decrease rapidly below levels that could harm the environment. However, dilution can be restricted in coastal areas, thus limiting the use of dispersant. All the tests conducted in this study were conducted using brut Arabian light oil that was pre-evaporated to simulate realistic conditions. The study examined whether the presence of oil leads to different effects than the control and whether the chemically dispersed oil gave different effects than the mechanical dispersion. The comparison with chemical dispersion in clear sea water examined whether the presence of suspended materials change the effect of the chemical dispersion. Results for the different phases of the project were presented. The preliminary results tend to open the use of chemical dispersion of oil slicks in coastal areas. The mixture of dispersant plus oil seems to be less detrimental than oil alone, particularly for turbot. The final conclusion regarding chemical dispersion of oil slicks in coastal areas will have to be formulated at the end of the project because coastal ecosystems depend on biotic and abiotic factors. The final phase will take place in a realistic environment in a salt marsh ecosystem at La Rochelle, France. 6 refs., 6 tabs., 6 figs.
Sorption of VX to Clay Minerals and Soils: Thermodynamic and Kinetic Studies
2012-12-01
Kaolinite, a member of the kaolin family, is a 1:1 clay, consisting of a single silicon-containing tetrahedral sheet linked to a single aluminum...14,15,18,19 The kaolinite is a white-firing, plastic kaolinite mined from claystone deposits in Georgia. This clay, identified as no. 6 tile kaolin , was...Validation of Model Predictions for the Dispersion and Fate of Reactive Chemical Releases in a Sub- Estuary of the Chesapeake Bay. Presented at the 2011
Water and solute transport in agricultural soils predicted by volumetric clay and silt contents
DEFF Research Database (Denmark)
Karup, Dan; Møldrup, Per; Paradelo Pérez, Marcos
2016-01-01
tracer mass could be well fitted to an analytical solution to the classical convection-dispersion equation. Both cumulative tracer mass and concentration as a function of time were hereby reasonable well predicted from the simple inputs of bulk density, clay and silt contents, and applied tracer mass......Solute transport through the soil matrix is heterogeneous and greatly affected by soil texture, soil structure, and macropore networks. This study examined the relationship between tracer breakthrough characteristics, soil hydraulic properties, and basic soil properties. Hundred...... of the soil structure rather than the actual formation of macropores causing preferential flow. The arrival times of 5 % and up to 50 % of the tracer mass were found to be strongly correlated with volumetric fines content. The hereby predicted tracer concentration breakthrough points up to 50% of applied...
Effect of smectite clays storage in their rheological properties
International Nuclear Information System (INIS)
Silva, I.A. da; Sousa, F.K.A. de; Neves, G. de A.; Ferreira, H.C.; Ferreira, H.S.; Ferreira, H.S.
2017-01-01
This work investigates the storage influence of natural and industrial smectite clays in their rheological properties, since the salt metathesis reaction that occurs following treatment of polycationic clays with Na_2 CO_3 is reversible. The phenomena involved in this reaction are not yet fully known and previous studies show improvement in some properties. The rheological properties were determined in sodium-clays in 1995 and polycationic clays added with sodium carbonate (Na_2 CO_3 ) in 2015. Physical, chemical and mineralogical characterizations of the samples were performed using the following techniques: particle size analysis by laser diffraction, chemical composition by X-ray fluorescence, X-ray diffraction and thermal analysis (DTA and TGA). The rheology of dispersions was determined by the apparent viscosity, plastic viscosity and filtrate volume, which were later considered the oil industry standards only as a benchmark. The results showed that the storage conditions, humidity and particle size of the samples resulted in improvements in their rheological properties over the years, indicating the non-reversibility of the reaction of cation exchange, which is important in their validity after manufacturing. (author)
LDPE/HDPE/Clay Nanocomposites: Effects of Compatibilizer on the Structure and Dielectric Response
Directory of Open Access Journals (Sweden)
B. Zazoum
2013-01-01
Full Text Available PE/clay nanocomposites were prepared by mixing a commercially available premixed polyethylene/O-MMT masterbatch into a polyethylene blend matrix containing 80 wt% low-density polyethylene and 20 wt% high-density polyethylene with and without anhydride modified polyethylene (PE-MA as the compatibilizer using a corotating twin-screw extruder. In this study, the effect of nanoclay and compatibilizer on the structure and dielectric response of PE/clay nanocomposites has been investigated. The microstructure of PE/clay nanocomposites was characterized using wide-angle X-ray diffraction (WAXD and a scanning electron microscope (SEM. Thermal properties were examined using differential scanning calorimetry (DSC. The dielectric response of neat PE was compared with that of PE/clay nanocomposite with and without the compatibilizer. The XRD and SEM results showed that the PE/O-MMT nanocomposite with the PE-MA compatibilizer was better dispersed. In the nanocomposite materials, two relaxation modes are detected in the dielectric losses. The first relaxation is due to a Maxwell-Wagner-Sillars interfacial polarization, and the second relaxation can be related to dipolar polarization. A relationship between the degree of dispersion and the relaxation rate fmax of Maxwell-Wagner-Sillars was found and discussed.
Deciphering the science behind electrocoagulation to remove suspended clay particles from water.
Holt, P K; Barton, G W; Mitchell, C A
2004-01-01
Electrocoagulation removes pollutant material from water by a combination of coagulant delivered from a sacrificial aluminium anode and hydrogen bubbles evolved at an inert cathode. Rates of clay particle flotation and settling were experimentally determined in a 7 L batch reactor over a range of currents (0.25-2.0 A) and pollutant loadings (0.1-1.7 g/L). Sedimentation and flotation are the dominant removal mechanism at low and high currents, respectively. This shift in separation mode can be explained by analysing the reactor in terms of a published dissolved air flotation model.
Interaction between water and wind as a driver of passive dispersal in mangroves.
Directory of Open Access Journals (Sweden)
Tom Van der Stocken
Full Text Available Although knowledge on dispersal patterns is essential for predicting long-term population dynamics, critical information on the modalities of passive dispersal and potential interactions between vectors is often missing. Here, we use mangrove propagules with a wide variety of morphologies to investigate the interaction between water and wind as a driver of passive dispersal. We imposed 16 combinations of wind and hydrodynamic conditions in a flume tank, using propagules of six important mangrove species (and genera, resulting in a set of dispersal morphologies that covers most variation present in mangrove propagules worldwide. Additionally, we discussed the broader implications of the outcome of this flume study on the potential of long distance dispersal for mangrove propagules in nature, applying a conceptual model to a natural mangrove system in Gazi Bay (Kenya. Overall, the effect of wind on dispersal depended on propagule density (g l(-1. The low-density Heritiera littoralis propagules were most affected by wind, while the high-density vertically floating propagules of Ceriops tagal and Bruguiera gymnorrhiza were least affected. Avicennia marina, and horizontally floating Rhizophora mucronata and C. tagal propagules behaved similarly. Morphological propagule traits, such as the dorsal sail of H. littoralis, explained another part of the interspecific differences. Within species, differences in dispersal velocities can be explained by differences in density and for H. littoralis also by variations in the shape of the dorsal sail. Our conceptual model illustrates that different propagule types have a different likelihood of reaching the open ocean depending on prevailing water and wind currents. Results suggest that in open water, propagule traits (density, morphology, and floating orientation appear to determine the effect of water and wind currents on dispersal dynamics. This has important implications for inter- and intraspecific
Interphase vs confinement in starch-clay bionanocomposites.
Coativy, Gildas; Chevigny, Chloé; Rolland-Sabaté, Agnès; Leroy, Eric; Lourdin, Denis
2015-03-06
Starch-clay bionanocomposites containing 1-10% of natural montmorillonite were elaborated by melt processing in the presence of water. A complex macromolecular dynamics behavior was observed: depending on the clay content, an increase of the glass transition temperature and/or the presence of two overlapped α relaxation peaks were detected. Thanks to a model allowing the prediction of the average interparticle distance, and its comparison with the average size of starch macromolecules, it was possible to associate these phenomena to different populations of macromolecules. In particular, it seems that for high clay content (10%), the slowdown of segmental relaxation due to confinement of the starch macromolecules between the clay tactoïds is the predominant phenomenon. While for lower clay contents (3-5%), a significant modification of chain relaxation seems to occur, due to the formation of an interphase by the starch macromolecules in the vicinity of clay nanoparticles coexisting with the bulk polymer. Copyright © 2014 Elsevier Ltd. All rights reserved.
Permeability response of oil-contaminated compacted clays
International Nuclear Information System (INIS)
Silvestri, V.; Mikhail, N.; Soulie, M.
1997-01-01
This paper presents the results of a laboratory investigation on the behavior of motor oil-contaminated, partially saturated compacted clays. For the study, both a natural clay and an artificially purified kaolinite, contaminated with 0 to 8% of motor oil, were firstly compacted following the ASTM standard procedure. Secondly, permeability tests were carried out in a triaxial cell on 10 cm-diameter compacted clay specimens. The results of the investigation indicate that increasing percentages of motor oil decrease both the optimum water content and the optimum dry density of the two clays. However, whereas the optimum water content on the average decreases by about 6% when the percentage contamination increases from 0 to 8%, the corresponding decrease in the optimum dry density is less than 3%. Even though the optimum dry density decreases as the percentage of oil increases from 0 to 8%, there is, however, a range in oil content varying between 2 and 4% for which the optimum dry density is slightly greater than that of the untreated soils. As far as the permeability tests are concerned, the results indicate that as the percentage of oil increases, the coefficient of permeability decreases substantially, especially for clay specimens which were initially compacted on the dry side of optimum
Can the water content of highly compacted bentonite be increased by applying a high water pressure?
International Nuclear Information System (INIS)
Pusch, R.; Kasbohm, J.
2001-10-01
A great many laboratory investigations have shown that the water uptake in highly compacted MX-80 clay takes place by diffusion at low external pressure. It means that wetting of the clay buffer in the deposition holes of a KBS-3 repository is very slow if the water pressure is low and that complete water saturation can take several tens of years if the initial degree of water saturation of the buffer clay and the ability of the rock to give off water are low. It has therefore been asked whether injection of water can raise the degree of water saturation and if a high water pressure in the nearfield can have the same effect. The present report describes attempts to moisten highly compacted blocks of MX-80 clay with a dry density of 1510 kg/m 3 by injecting water under a pressure of 650 kPa through a perforated injection pipe for 3 and 20 minutes, respectively. The interpretation was made by determining the water content of a number of samples located at different distances from the pipe. An attempt to interpret the pattern of distribution of injected uranium acetate solution showed that the channels into which the solution went became closed in a few minutes and that dispersion in the homogenized clay gave low U-concentrations. The result was that the water content increased from about 9 to about 11-12 % within a distance of about 1 centimeter from the injection pipe and to slightly more than 9 % at a distance of about 4-5 cm almost independently of the injection time. Complete water saturation corresponds to a water content of about 30 % and the wetting effect was hence small from a practical point of view. By use of microstructural models it can be shown that injected water enters only the widest channels that remain after the compaction and that these channels are quickly closed by expansion of the hydrating surrounding clay. Part of the particles that are thereby released become transported by the flowing water and cause clogging of the channels, which is
Bio composites from polypropylene/ clay/eva polymers and kenaf natural fiber
International Nuclear Information System (INIS)
Siti Hasnah Kamarudin; Khalina Abdan; Bernard Maringgal; Wan Mohd Zin Wan Yunus
2009-01-01
Full text: There is an increasing need to investigate more environmental friendly, sustainable materials to replace existing materials as industry attempts to lessen dependence on petroleum based fuels and products. The natural fiber composites offer specific properties comparable to those of conventional fiber composites. In this experiment, mixing process of polymer/nano clay composites from polypropylene, organo clay and ethylene vinyl acetate were prepared using a Brabender twin screw compounder. The composites sheets were then laminated with kenaf fibers and subjected to hot and cold press machine to form a bio composite. The mechanical properties such as flexural and impact strength are compare favourably between polymers reinforced kenaf fiber and polymers without kenaf fiber. In addition, various analysis techniques were used to characterize the dispersion and the properties of nano composites, using scanning electron micrograph (SEM), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). These results suggest that kenaf fibers are a viable alternative to inorganic mineral-based reinforcing fibers as long as the right processing conditions are used and they are used in applications where the higher water absorption is not critical. (author)
International Nuclear Information System (INIS)
Alonso, E. E.; Alcoverro, J.
1999-01-01
Stage 3 of CATSIUS CLAY Project: Validation Exercises at a Large in situ Scale includes two Benchmarks: Benchmark 3.1: In situ Hydration of Boom Clay Pellets (BACCHUS 2) and Benchmark 3.2: FEBEX Mock-up Test. The BACCHUS 2 in situ test was performed in the HADES underground laboratory (Mol, Belgium) to demonstrate and optimize an installation procedure for a clay based material and to study its hydration process. After drilling a vertical shaft (540 mm in diameter, 3.0 m in length) in the host Boom clay, a central filter (90 mm in diameter) was placed, the remaining space was filled with a mixture of clay pellets and clay powder and the assembly was sealed at the upper end by a resin plug (0.20 m in thickness) over which concrete was poured. The test was instrumented so that it could be used as a validation experiment. Total stress, pore water pressure and water content measurements were performed both in the backfill material and in the surrounding clay massif. Once the installation was complete, the natural hydration of the backfill material began (day 0). To accelerate the hydration process, on day 516 water was injected through the central filter. On day 624, after the saturation of the backfill was reached, the hydraulic circuit was closed and the undrained response of the system backfill-host clay was monitored until an overall steady state was reached. Partners were asked to provide predictions for the evolution of the pore water pressure and total pressure of various points where appropriate sensors are installed. This benchmark addresses the Hydro-Mechanical response of an unsaturated low density clay barrier under natural and artificial hydration. (Author)
Energy Technology Data Exchange (ETDEWEB)
Alonso, E E; Alcoverro, J
1999-07-01
Stage 3 of CATSIUS CLAY Project: Validation Exercises at a Large in situ Scale includes two Benchmarks: Benchmark 3.1: In situ Hydration of Boom Clay Pellets (BACCHUS 2) and Benchmark 3.2: FEBEX Mock-up Test. The BACCHUS 2 in situ test was performed in the HADES underground laboratory (Mol, Belgium) to demonstrate and optimize an installation procedure for a clay based material and to study its hydration process. After drilling a vertical shaft (540 mm in diameter, 3.0 m in length) in the host Boom clay, a central filter (90 mm in diameter) was placed, the remaining space was filled with a mixture of clay pellets and clay powder and the assembly was sealed at the upper end by a resin plug (0.20 m in thickness) over which concrete was poured. The test was instrumented so that it could be used as a validation experiment. Total stress, pore water pressure and water content measurements were performed both in the backfill material and in the surrounding clay massif. Once the installation was complete, the natural hydration of the backfill material began (day 0). To accelerate the hydration process, on day 516 water was injected through the central filter. On day 624, after the saturation of the backfill was reached, the hydraulic circuit was closed and the undrained response of the system backfill-host clay was monitored until an overall steady state was reached. Partners were asked to provide predictions for the evolution of the pore water pressure and total pressure of various points where appropriate sensors are installed. This benchmark addresses the Hydro-Mechanical response of an unsaturated low density clay barrier under natural and artificial hydration. (Author)
Magnesium incorporated bentonite clay for defluoridation of drinking water.
Thakre, Dilip; Rayalu, Sadhana; Kawade, Raju; Meshram, Siddharth; Subrt, J; Labhsetwar, Nitin
2010-08-15
Low cost bentonite clay was chemically modified using magnesium chloride in order to enhance its fluoride removal capacity. The magnesium incorporated bentonite (MB) was characterized by using XRD and SEM techniques. Batch adsorption experiments were conducted to study and optimize various operational parameters such as adsorbent dose, contact time, pH, effect of co-ions and initial fluoride concentration. It was observed that the MB works effectively over wide range of pH and showed a maximum fluoride removal capacity of 2.26 mgg(-1) at an initial fluoride concentration of 5 mg L(-1), which is much better than the unmodified bentonite. The experimental data fitted well into Langmuir adsorption isotherm and follows pseudo-first-order kinetics. Thermodynamic study suggests that fluoride adsorption on MB is reasonably spontaneous and an endothermic process. MB showed significantly high fluoride removal in synthetic water as compared to field water. Desorption study of MB suggest that almost all the loaded fluoride was desorbed ( approximately 97%) using 1M NaOH solution however maximum fluoride removal decreases from 95.47 to 73 (%) after regeneration. From the experimental results, it may be inferred that chemical modification enhances the fluoride removal efficiency of bentonite and it works as an effective adsorbent for defluoridation of water. Copyright 2010 Elsevier B.V. All rights reserved.
Clay behaviour under thermal gradients elastic and plastic strains
International Nuclear Information System (INIS)
Pintado, Xavier; Autio, Jorma; Punkkinen, Olli
2010-01-01
Document available in extended abstract form only. The nuclear waste repositories will generate strong temperature gradients at the clay barrier. The heat and water transport generate volume change in the clay. An experimental work is proposed here. The clay reference is the MX-80. The test device imposes a fixed heat flow in one side of the sample and maintains constant the temperature on the other side. Two samples are tested for symmetry. The samples are unconfined and the total mass of water remains constant. This situation creates a strong thermal gradient in the samples. The final radial strains in some places of the sample, the total vertical strain and the water content distribution will be measured just at the end of the test and some weeks later in order to distinguish the elastic strains from the plastic strains. The test period mustn't be longer than two weeks because a large quantity of water loses through the rubber membrane and the heads of the sample. The maximum temperature reached in the cooper is 90 degrees because with higher temperature, the rubber membrane is damaged. This test is already simulated by a numerical code. Thermal, thermo-hydraulic and thermo-hydro-mechanical analyses are being done. These analyses allow studying the different fluxes inside the sample and its quantification. Water content distribution is compared with the water content calculated from the reference parameters in the clay. The water distribution and the change of diameter after the test will also be studied. This experimental work will allow to know what is the percentage of the strains elastic or plastic and check the mechanical model. The experimental diameter change is compared with the diameter change calculated from the reference parameters of the clay. (authors)
Almazán-Sánchez, Perla Tatiana; Solache-Ríos, Marcos J; Linares-Hernández, Ivonne; Martínez-Miranda, Verónica
2016-01-01
Indigo blue dye is mainly used in dyeing of denim clothes and its presence in water bodies could have adverse effects on the aquatic system; for this reason, the objective of this study was to promote the removal of indigo blue dye from aqueous solutions by iron and copper electrochemically modified clay and activated carbon and the saturated materials were regenerated by a Fenton-like process. Montmorillonite clay was modified at pH 2 and 7; activated carbon at pH 2 and pH of the system. The elemental X-ray dispersive spectroscopy analysis showed that the optimum pH for modification of montmorillonite with iron and copper was 7 and for activated carbon was 2. The dye used in this work was characterized by infrared. Unmodified and modified clay samples showed the highest removal efficiencies of the dye (90-100%) in the pH interval from 2 to 10 whereas the removal efficiencies decrease as pH increases for samples modified at pH 2. Unmodified clay and copper-modified activated carbon at pH 2 were the most efficient activated materials for the removal of the dye. The adsorption kinetics data of all materials were best adjusted to the pseudo-second-order model, indicating a chemisorption mechanism and the adsorption isotherms data showed that the materials have a heterogeneous surface. The iron-modified clay could be regenerated by a photo-Fenton-like process through four adsorption-regeneration cycles, with 90% removal efficiency.
International Nuclear Information System (INIS)
Cerón Loayza, María L.; Bravo Cabrejos, Jorge A.; Mejía Santillán, Mirian E.
2011-01-01
The purpose of this work is to report the advances in the elemental and structural characterization of the clay fraction of soils from the terraces of the Moray Archaeological site, located 38 km north of the city of Cusco, Cusco Region. One sample was collected from each of the twelve terraces of this site and its clay fraction was separated by sedimentation. Previously the pH of the raw samples was measured resulting that all of the samples were from alkaline to strongly alkaline. Energy dispersive X-ray fluorescence (EDXRF) was used for the elemental characterization, and X-ray diffractometry (XRD) and transmission Mössbauer spectroscopy (TMS), using the γ 14.4 keV nuclear resonance transition in 57 Fe, were used for the structural characterization of the clays and clay minerals present in each sample. The EDXRF analyses of all the samples show the presence of relatively high concentrations of sulfur in some of the samples and relatively high concentrations of calcium in all of the samples, which may be related to the high alkalinity of the samples. By XRD it is observed the presence of quartz, calcite, gypsum, cronstedtite, 2:1 phyllosilicates, and iron oxides. The mineralogical analysis of Fe by TMS shows that it is present in the form of hematite and occupying Fe 2 + and Fe 3 + sites in phyllosilicates, cronstedtite, and other minerals not yet identified.
Complex resistivity signatures of ethanol in sand-clay mixtures
Personna, Yves Robert; Slater, Lee; Ntarlagiannis, Dimitrios; Werkema, Dale D.; Szabo, Zoltan
2013-01-01
We performed complex resistivity (CR) measurements on laboratory columns to investigate changes in electrical properties as a result of varying ethanol (EtOH) concentration (0% to 30% v/v) in a sand–clay (bentonite) matrix. We applied Debye decomposition, a phenomenological model commonly used to fit CR data, to determine model parameters (time constant: τ, chargeability: m, and normalized chargeability: mn). The CR data showed a significant (P ≤ 0.001) time-dependent variation in the clay driven polarization response (~ 12 mrad) for 0% EtOH concentration. This temporal variation probably results from the clay–water reaction kinetics trending towards equilibrium in the sand–clay–water system. The clay polarization is significantly suppressed (P ≤ 0.001) for both measured phase (ϕ) and imaginary conductivity (σ″) with increasing EtOH concentration. Normalized chargeability consistently decreases (by up to a factor of ~ 2) as EtOH concentration increases from 0% to 10% and 10 to 20%, respectively. We propose that such suppression effects are associated with alterations in the electrical double layer (EDL) at the clay–fluid interface due to (a) strong EtOH adsorption on clay, and (b) complex intermolecular EtOH–water interactions and subsequent changes in ionic mobility on the surface in the EDL. Changes in the CR data following a change of the saturating fluid from EtOH 20% to plain water indicate strong hysteresis effects in the electrical response, which we attribute to persistent EtOH adsorption on clay. Our results demonstrate high sensitivity of CR measurements to clay–EtOH interactions in porous media, indicating the potential application of this technique for characterization and monitoring of ethanol contamination in sediments containing clays.
Performance of polymeric films based thermoplastic starch and organophilic clay
International Nuclear Information System (INIS)
Cipriano, P.B.; Costa, A.N.M.; Araujo, S.S.; Araujo, A.R.A.; Canedo, E.L.; Carvalho, L.H.
2010-01-01
The aim of this work was the development and investigation of the properties of flat films of LDPE/corn thermoplastic starch (TPS). A bentonite clay (Argel) was organophilized and characterized by XRD. This clay (1%) in both pristine and organophilic forms was added to the matrix (LDPE) and to LDPE/TPS systems with TPS contents varying from 5-20% w/w. The films manufactured (LDPE, LDPE/Clay, LDPE/TPS, LDPE/TPS/Clay) were characterized. Results indicate that water vapor permeability is dependent and increases with TPS content which was attributed to the higher affinity of water by TPS. TPS and Clay addition to LDPE led to significant changes in film properties with respect to the neat LDPE. In general,tensile and perforation forces increased with clay and TPS contents; the strength of thermo sealed films lowered with natural clay addition and increased with TPS and organoclay incorporation and, in general, dynamic friction coefficient decrease with organoclay and TPS addition. Best overall properties were obtained for the systems containing the organoclay and optimal properties were achieved for the 5%TPS10 LDPE1% ANO system. (author)
Corrosion behaviour of carbon steel in the Tournemire clay
International Nuclear Information System (INIS)
Foct, F.; Dridi, W.; Cabrera, J.; Savoye, S.
2004-01-01
Carbon steels are possible materials for the fabrication of nuclear waste containers for long term geological disposal in argillaceous environments. Experimental studies of the corrosion behaviour of such materials has been conducted in various conditions. Concerning the numerous laboratory experiments, these conditions (water and clay mixture or compacted clay) mainly concern the bentonite clay that would be used for the engineered barrier. On the opposite, only few in-situ experiments has been conducted directly in the local clay of the repository site (such as Boom clay, etc.). In order to better estimate the corrosion behaviour of carbon steels in natural clay site conditions, an experimental study has been conducted jointly by EDF and IRSN in the argillaceous French site of Tournemire. In this study, A42 carbon steel specimens have been exposed in 3 different zones of the Tournemire clay formation. The first type of environmental conditions concerns a zone where the clay has not been affected by the excavation (EDZ) of the main tunnel neither by the main fracture zone of the clay formation. The second and third ones are located in the EDZ of the tunnel. In the second zone, an additional aerated water flows from the tunnel, whereas it does not in the third place. Some carbon steel specimens have been extracted after several years of exposure to these conditions. The average corrosion rate has been measured by the weight loss technique and the pitting corrosion depth has been evaluated under an optical microscope. Corrosion products have also been characterised by scanning electron microscopy and X-ray diffraction technique. Results are then discussed regarding the surrounding environmental conditions. Calculations of the oxygen transport from the tunnel through the clay and of the clay re-saturation can explain, in a first approach, the corrosion behaviour of the carbon steel in the different tested zones. (authors)
Irrigation with saline-sodic water: effects on two clay soils
Directory of Open Access Journals (Sweden)
Giovanna Cucci
2013-05-01
Full Text Available The results of a 4-year experiment aimed at evaluating the effect of irrigation with saline-sodic water on the soil are reported. The research was carried out at the Campus of the Agricultural Faculty of Bari University (Italy on 2 clay soils (Bologna – T1 and Locorotondo – T2. The soils were cropped to borlotto bean (Phaseolus vulgaris L., capsicum (Capsicum annuum L., sunflower (Helianthus annuus L., wheat (Triticum durum Desf grown in succession; the crops were irrigated with 9 saline-sodic types of water and subjected to two different leaching fractions (10% and 20% of the watering volume. The 9 solutions were obtained dissolving in de-ionised water weighted amounts of sodium chloride (NaCl and calcium chloride (CaCl2, deriving from the combination of 3 saline concentrations and 3 sodicity levels. The crops were irrigated whenever the water lost by evapotranspiration from the soil contained in the pots was equal to 30% of the soil maximum available water. The results showed that, though the soils were leached during the watering period, they showed a high salt accumulation. Consequently, the saturated soil extract electrical conductivity increased from initial values of 0.65 and 0.68 dS m-1 to 11.24 and 13.61 dS m-1 at the end of the experiment, for the soils T1 and T2, respectively. The saline concentration increase in irrigation water caused in both soils a progressive increase in exchangeable sodium, and a decrease in exchangeable calcium and non-significant variations in exchangeable potassium (K and magnesium (Mg.
DEFF Research Database (Denmark)
Getahun, Gizachew Tarekegn; Munkholm, Lars Juhl; Schjønning, Per
2016-01-01
× SOC according to Dexter et al. (2008). NCC was a better predictor of dispersible clay than total clay and SOC at all depths in natural aggregates, while tensile strength and derived parameters were generally better explained by the total amount of clay in remoulded aggregates. Remoulded aggregates had...
Energy Technology Data Exchange (ETDEWEB)
Cui, Mingjun [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); University of Chinese Academy of Sciences, Beijing 100039 (China); Ren, Siming [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); University of Chinese Academy of Sciences, Beijing 100039 (China); Chen, Jia; Liu, Shuan [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Zhang, Guangan [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Zhao, Haichao, E-mail: zhaohaichao@nimte.ac.cn [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Wang, Liping, E-mail: wangliping@nimte.ac.cn [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Xue, Qunji, E-mail: qjxue@lzb.ac.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China)
2017-03-01
Highlights: • Hexagonal boron nitride nanosheets were well dispersed by using water-soluble carboxylated aniline trimer as dispersant. • The best corrosion performance of waterborne epoxy coatings was achieved with the addition of 1 wt% h-BN. • The decrease of the pores and defects of coating matrix inhibits the diffusion and water absorption of corrosive medium in the coating. - Abstract: Homogenous dispersion of hexagonal boron nitride (h-BN) nanosheets in solvents or in the polymer matrix is crucial to initiate their many applications. Here, homogeneous dispersion of hexagonal boron nitride (h-BN) in epoxy matrix was achieved with a water-soluble carboxylated aniline trimer derivative (CAT{sup −}) as a dispersant, which was attributed to the strong π-π interaction between h-BN and CAT{sup −}, as proved by Raman and UV–vis spectra. Transmission electron microscopy (TEM) analysis confirmed a random dispersion of h-BN nanosheets in the waterborne epoxy coatings. The deterioration process of water-borne epoxy coating with and without h-BN nanosheets during the long-term immersion in 3.5 wt% NaCl solution was investigated by electrochemical measurements and water absorption test. Results implied that the introduction of well dispersed h-BN nanosheets into waterborne epoxy system remarkably improved the corrosion protection performance to substrate. Moreover, 1 wt% BN/EP composite coated substrate exhibited higher impedance modulus (1.3 × 10{sup 6} Ω cm{sup 2}) and lower water absorption (4%) than those of pure waterborne epoxy coating coated electrode after long-term immersion in 3.5 wt% NaCl solution, demonstrating its superior anticorrosive performance. This enhanced anticorrosive performance was mainly ascribed to the improved water barrier property of epoxy coating via incorporating homogeneously dispersed h-BN nanosheets.
Removal of Phenol in Aqueous Solution Using Kaolin Mineral Clay
International Nuclear Information System (INIS)
Sayed, M.S.
2008-01-01
Kaolin clay were tested for phenol removal as toxic liquid waste from aqueous waste water. Several experimental conditions such as weight and particle size of clay were investigated to study batch kinetic techniques, also the ph and concentration of the phenol solution were carried out. The stability of the Langmuir adsorption model of the equilibrium data were studied for phenol sorbent clay system. Infrared spectra, thermogravimetric and differential thermal analysis techniques were used to characterize the behavior of kaolin clay and kaolin clay saturated with phenol. The results obtained showed that kaolin clay could be used successfully as an efficient sorbent material to remove phenol from aqueous solution
Liu, Wei-ping; Fang, Zhuo; Liu, Hui-jun; Yang, Wei-chun
2002-04-01
Adsorption of chloroacetanilide herbicides on homoionic montmorillonite, soil humic acid, and their mixtures was studied by coupling batch equilibration and FT-IR analysis. Adsorption isotherms of acetochlor, alachlor, metolachlor and propachlor on Ca(2+)-, Mg(2+)-, Al(3+)- and Fe(3+)-saturated clays were well described by the Freundlich equation. Regardless of the type of exchange cations, Kf decreased in the order of metolachlor > acetolachlor > alachlor > propachlor on the same clay. FT-IR spectra showed that the carbonyl group of the herbicide molecule was involved in binding, probably via H-bond with water molecules in the clay interlayer. The type and position of substitutions around the carbonyl group may have affected the electronegativity of oxygen, thus influencing the relative adsorption of these herbicides. For the same herbicide, adsorption on clay increased in the order of Mg2+ < Ca2+ < Al3+ < or = Fe3+ which coincided with the increasing acidity of homoionic clays. Acidity of cations may have affected the protonation of water, and thus the strength of H-bond between the clay water and herbicide. Complexation of clay and humic acid resulted in less adsorption than that expected from independent adsorption by the individual constituents. The effect varied with herbicides, but the greatest decrease in adsorption occurred at a 60:40 clay-to-humic acid ratio for all the herbicides. Causes for the decreased adsorption need to be characterized to better understand adsorption mechanisms and predict adsorption from soil compositions.
Energy Technology Data Exchange (ETDEWEB)
Luo, K.; Li, H.; Feng, F. (and others) [Chinese Academy of Sciences, Beijing (China)
2007-04-15
About 160 samples of coal, pyritic coal balls, coal seam gangue, clay, corn, capsicum and drinking water were collected from the endemic fluorosis area of Zhenxiong and Weixin county, China to determine the fluorine content, distribution pattern and source in this fluorosis area. The study shows that the average fluorine content in the coal samples collected from 3 coal mines of the Late Permian coals in Zhenxiong and Weixin county, Zhaotong City, which are the main mining coals there, is 77.13 mg/kg. The average fluorine content coals collected form thee typical fluorosis villages in 72.56 mg/kg. Both of them are close to the world average and little low than the Chinese average. The fluorine content of drinking water is lower than 0.35 mg/L, the clay used as an additive for coal-burning and as a binfer in briquette-making by local residents has a high content of fluorine, ranging from 367-2,435 mg/kg, with the majority higher than 600 mg/kg and an average of 1,084.2 mg/kg. 29 refs., 5 tabs.
An oxidized asphalt mastic - ''Jastab'' a clay shale stabilizer
Energy Technology Data Exchange (ETDEWEB)
1979-01-01
Reported on is the devepment in Poland of a new compound - Jastab, which is introduced into clay solutions on a water base for ensuring stability of the walls of drilled wells, complexed with clay shales. Jastab is oxidized asphalt, which is a brown powder with a specific weight of 1.55-1.6 g/cm/sup 3/. The solution which consists of 100 parts by weight of Jastab and 160 parts by weight of diesel fuel, has a viscosity of 15 centapoise, a specific weight of 0.92 g/cm/sup 3/ and a water output at a temperature of 20/sup 0/C of 2.15 cm/sup 3//30 min. It i established that the introduction of Jastab into the clay muds makes it possible to control the osmosis process and to strongly limit the process of hydration of the clay shales, and to improve the rheological properties of the clay muds. The wide introduction of the Jastab compound is recommended in the passage of wells in the region of the Carpathians and in slanted wells.
preconcentration of uranium in water samples using dispersive
African Journals Online (AJOL)
B. S. Chandravanshi
Atomic Energy Organization of Iran, P.O. Box 14395-836, Tehran, Iran. 2Department of ... A new liquid phase microextraction method based on the dispersion of an extraction solvent into aqueous phase ... optical emission spectrometry, Uranium, Water samples ..... The validation of the presented procedure was performed ...
Raman scattering temperature measurements for water vapor in nonequilibrium dispersed two-phase flow
International Nuclear Information System (INIS)
Anastasia, C.M.; Neti, S.; Smith, W.R.; Chen, J.C.
1982-09-01
The objective of this investigation was to determine the feasibility of using Raman scattering as a nonintrusive technique to measure vapor temperatures in dispersed two-phase flow. The Raman system developed for this investigation is described, including alignment of optics and optimization of the photodetector for photon pulse counting. Experimentally obtained Raman spectra are presented for the following single- and two-phase samples: liquid water, atmospheric nitrogen, superheated steam, nitrogen and water droplets in a high void fraction air/water mist, and superheated water vapor in nonequilibrium dispersed flow
Compound Method to Disperse CaCO3 Nanoparticles to Nano-Size in Water.
Gu, Sui; Cai, Jihua; Wang, Jijun; Yuan, Ye; Chang, Dewu; Chikhotkin, Viktor F
2015-12-01
The invalidation of CaCO3 nanoparticles (nCaCO3) is often caused by the fact of agglomeration and inhomogeneous dispersion which limits its application into water-based drilling muds for low permeability reservoirs such as coalbed methane reservoir and shale gas/oil reservoir. Effective methods to disperse nCaCO3 to nano-size (≤ 100 nm) in water have seldom been reported. Here we developed a compound method containing mechanical stirring, ultrasonic treatment, the use of surfactant and stabilizer to disperse nCaCO3 in water. It comprises the steps adding 2% nCaCO3, 1% sodium dodecyl sulfonate (SDS), 2% cetyltrimethyl ammonium bromide (CTAB), 2% OP-10, 3% to 4% biopolymer (XC) in water successively, stirring it at a shear rate of 6000 to 8000 r/min for 15 minutes and treating it with ultrasonic at a frequency of 28 KHz for 30 to 40 minutes. The dispersed nCaCO3 was characterized with scanning electron microscope (SEM), transmission electron microscope (TEM) and particle size distribution (PSD) tests. We found that nCaCO3 could be dispersed to below 100 nm in water and the medium value of nCaCO3 was below 50 nm. This method paved the way for the utilization of nCaCO3 in drilling fluid and completion fluid for low permeability reservoirs such as coal seams and shale gas/oil formations.
Hydration Phase Diagram of Clay Particles from Molecular Simulations.
Honorio, Tulio; Brochard, Laurent; Vandamme, Matthieu
2017-11-07
Adsorption plays a fundamental role in the behavior of clays. Because of the confinement between solid clay layers on the nanoscale, adsorbed water is structured in layers, which can occupy a specific volume. The transition between these states is intimately related to key features of clay thermo-hydro-mechanical behavior. In this article, we consider the hydration states of clays as phases and the transition between these states as phase changes. The thermodynamic formulation supporting this idea is presented. Then, the results from grand canonical Monte Carlo simulations of sodium montmorillonite are used to derive hydration phase diagrams. The stability analysis presented here explains the coexistence of different hydration states at clay particle scale and improves our understanding of the irreversibilities of clay thermo-hydro-mechanical behavior. Our results provide insights into the mechanics of the elementary constituents of clays, which is crucial for a better understanding of the macroscopic behavior of clay-rich rocks and soils.
On the freezing of clay soil and water migration into the pavement design
Directory of Open Access Journals (Sweden)
Sergeev Andrey Sergeevich
2014-03-01
Full Text Available The freezing of the surface layers of the Earth’s crust causes the volume deformation of soil and is expressed in the increase of volume and differential movement of their surface due to freezing of water and formation of ice inclusions. Underestimation of the frost heaving of soils, as well as the untimely application of anti — heaving measures cause the enormous damage to the national economy. All of this results in life reduction and condition deterioration of auto-road operation, as well as increase in non-manufacturing labor costs, building materials and financial means. During the experimental studies we have found that after four stages of freezing and defrosting the physical properties of clay soil change, i.e. the formation of 2-3 mm ice lenses is taking place at the junction of clay soil and sand. The number and dimensions of ice lenses increase with a further tightening of moisture up to 5-6 mm, and 3 zones related to the intensity of freezing are formed.
Directory of Open Access Journals (Sweden)
Kebede Woldetsadik
2011-06-01
Full Text Available Water shortage is one of the major constraints for production of horticultural crops in arid and semiarid regions. A field experiment was conducted to determine irrigation water and fertilizer use efficiency, growth and yield of tomato under clay pot irrigation at the experimental site of Sekota Dryland Agricultural Research Center, Lalibela, Ethiopia in 2009/10. The experiment comprised of five treatments including furrow irrigated control and clay pot irrigation with different plant population and fertilization methods, which were arranged in Randomized Complete Block Design with three replications. The highest total and marketable fruit yields were obtained from clay pot irrigation combined with application of nitrogen fertilizer with irrigation water irrespective of difference in plant population. The clay pot irrigation had seasonal water use of up to 143.71 mm, which resulted in significantly higher water use efficiency (33.62 kg m-3 as compared to the furrow irrigation, which had a seasonal water use of 485.50 mm, and a water use efficiency of 6.67 kg m-3. Application of nitrogen fertilizer with irrigation water in clay pots improved fertilizer use efficiency of tomato by up to 52% than band application with furrow or clay pot irrigation. Thus, clay pot irrigation with 33,333 plants ha-1 and nitrogen fertilizer application with irrigation water in clay pots was the best method for increasing the yield of tomato while economizing the use of water and nitrogen fertilizer in a semiarid environment.
Absorption characteristics of Kupravas deposit clays modified by phosphoric acid
International Nuclear Information System (INIS)
Ruplis, A.; Mezinskis, G.; Chaghuri, M.
1998-01-01
Literature data suggested that clays may be used as sorbents for waste water treatment. The surface and sorption properties of minerals changes due to the influence of acid rains. The process of recession of clay properties has been modeled in laboratory by treatment of clays with mineral acids at higher temperature that in natural conditions. The present paper is devoted to the study of influence of phosphoric acid on the sorption properties of Kupravas deposit clays. Natural clay samples and samples treated with phosphoric acid were characterized by means of x-ray diffraction an differential thermal analysis (DTA) methods These methods were used also to identify the sample of Lebanese clays. X-ray diffraction analysis data show that the samples of clays from the deposit of Kuprava contain illite and kaolinite while sample of Lebanese clay contains quartz, calcite, and montmorillonite. DTA results show characteristic features of Kuprava clays described in reference with DTA of Lebanese clay clearly demonstrate the presence of large quantity of calcite
Experimental investigation of clay fly ash bricks for gamma-ray shielding
Energy Technology Data Exchange (ETDEWEB)
Mann Harjinder Singh; Mudahar, Gumel Singh [Dept. of Physics, Punjabi University, Patiala (India); Brar, Gurdarshan Singh [Dept. of Higher Education, Additional Project Director, Chandigarh (India); Mann, Kulwinder Singh [Dept. of Applied Sciences, I.K. Gujral Punjab Technical University, Jalandhar (India)
2016-10-15
This study aims to determine the effect of fly ash with a high replacing ratio of clay on the radiation shielding properties of bricks. Some interaction parameters (mass attenuation coefficients, half value layer, effective atomic number, effective electron density, and absorption efficiency) of clay fly ash bricks were measured with a NaI(Tl) detector at 661.6 keV, 1,173.2 keV, and 1,332.5 keV. For the investigation of their shielding behavior, fly ash bricks were molded using an admixture to clay. A narrow beam transmission geometry condition was used for the measurements. The measured values of these parameters were found in good agreement with the theoretical calculations. The elemental compositions of the clay fly ash bricks were analyzed by using an energy dispersive X-ray fluorescence spectrometer. At selected energies the values of the effective atomic numbers and effective electron densities showed a very modest variation with the composition of the fly ash. This seems to be due to the similarity of their elemental compositions. The obtained results were also compared with concrete, in order to study the effect of fly ash content on the radiation shielding properties of clay fly ash bricks. The clay fly ash bricks showed good shielding properties for moderate energy gamma rays. Therefore, these bricks are feasible and eco-friendly compared with traditional clay bricks used for construction.
Mimides, T; Perraki, T
2000-05-15
Heavy metal attenuation properties of selected clay material collected from miscellaneous Greek sites is investigated and tested in the laboratory for their suitability, either as liners in hydrologically unsafe sites or as earth covers for sanitary landfill sites. Eleven potentially hazardous elements (As, Be, Cd, Cr, Cu, Hg, Ni, Pb, Se, V, and Zn) generated by a co-disposal landfill leachate have been considered. Experimental column and static equilibrium methods for the determination of dispersion and adsorption are described. Molecular diffusion dominates the migration phenomena with a velocity range between 1.3 x 10(-5) and 3.5 x 10(-4) cm/s throughout the experiments. A simple way to evaluate dispersion coefficients from breakthrough curves gave values of between 3.90 x 10(-6) and 3.5 x 10(-4) cm2/s, with a mean value of 1.5 x 10(-5). Static adsorption equilibrium studies supported by column runs showed that Freundlich (F = kCn) isotherms express in a better way the assimilative capacities of the tested clays, with k and n values ranging from 0.06 to 1.99 and 0.55 to 1.48 correspondingly. Mathematical models involving non-linear parabolic equations are involved. The experimental data, together with finite difference techniques and some physical clay characteristics, produced trilinear textural diagrams and predictive flow transport convection-dispersion breakthrough curves for a quick estimation of the attenuating properties of clays for heavy metals.
Lime as an Anti-Plasticizer for Self-Compacting Clay Concrete
Directory of Open Access Journals (Sweden)
Gnanli Landrou
2016-04-01
Full Text Available This paper focuses on the modification of clay properties with inorganic additives to deflocculate and flocculate inorganic soil for the development of a material that would be as easy to use as the current concrete products, but with a much lower environmental impact. Considering that the rheological behaviour of clays is controlled by their surface charge, we first introduce potential determining ions to deflocculate the clay particles and to reduce the yield stress of the earth material. Their efficiency is characterized using zeta potential measurements and rheological tests. We then achieve the flocculation of clay particles by using natural minerals that slowly dissolve in the interstitial liquid and ultimately precipitate calcium silicate hydrate (C–S–H. The precipitation products are identified by X-ray diffraction and the consequences of this delayed precipitation are followed by oscillatory rheometric measurements. Finally, it is suggested that in this process, C–S–H precipitation is not used as a binding vector but as an anti-plasticizer that removes the inorganic dispersant additives.
Neoformation of clay in lateral root catchments of mallee eucalypts: a chemical perspective
Verboom, William H.; Pate, John S.; Aspandiar, Mehrooz
2010-01-01
Background and Aims A previous paper (Annals of Botany 103: 673–685) described formation of clayey pavements in lateral root catchments of eucalypts colonizing a recently formed sand dune in south-west Western Australia. Here chemical and morphological aspects of their formation at the site are studied. Methods Chemical and physical examinations of soil cores through pavements and sand under adjacent heath assessed build-up of salts, clay and pH changes in or below pavements. Relationships of root morphology to clay deposition were examined and deposits subjected to scanning electron microscopy and energy-dispersive X-ray analysis. Xylem transport of mineral elements in eucalypt and non-eucalypt species was studied by analysis of xylem (tracheal) sap from lateral roots. Key Results The columns of which pavements are composed develop exclusively on lower-tier lateral roots. Such sites show intimate associations of fine roots, fungal filaments, microbiota and clay deposits rich in Si, Al and Fe. Time scales for construction of pavements by eucalypts were assessed. Cores through columns of pavemented profiles showed gross elevations of bulk density, Al, Fe and Si in columns and related increases in pH, Mg and Ca status in lower profiles. A cutting through the dune exhibited pronounced alkalinity (pH 7–10) under mallee woodland versus acidity (pH 5–6·5) under proteaceous heath. Xylem sap analyses showed unusually high concentrations of Al, Fe, Mg and Si in dry-season samples from column-bearing roots. Conclusions Deposition of Al–Fe–Si-rich clay is pivotal to pavement construction by eucalypts and leads to profound chemical and physical changes in relevant soil profiles. Microbial associates of roots are likely to be involved in clay genesis, with parent eucalypts supplying the required key mineral elements and carbon sources. Acquisition of the Al and Fe incorporated into clay derives principally from hydraulic uplift from ground water via deeply
Synthetic clay excels in 90Sr removal
International Nuclear Information System (INIS)
Komarneni, Sridhar; Kodama, Tatsuya; Paulus, William J.; Carlson, C.
2000-01-01
Tests with actual ground water from Hanford site, and fundamental studies of 2Na + →Sr 2+ exchange equilibria revealed that a synthetic clay is extremely selective for 90 Sr with a high capacity for uptake. Comparative studies with existing Sr selective ion exchangers clearly revealed that the present synthetic clay exhibited the best performance for 90 Sr removal from actual ground water collected from three different locations at Hanford. This novel Sr ion sieve is expected to be useful for the decontamination of the environment after accidental release and contamination with 90 Sr. (c) 2000 Materials Research Society
Directory of Open Access Journals (Sweden)
Angela de Mello Ferreira Guimarães
2007-03-01
Full Text Available This work describes the process for functionalization of laponite through the grafting of 3-mercaptopropyltrimethoxysilane (MPTS. Laponite is synthetic smectite clay with surface area of 350 m²/g. The samples, prior to and after functionalization, were characterized by chemical analyses, thermogravimetric analysis (TGA, x ray diffraction (XRD, diffuse reflectance infrared Fourier transform spectroscopy (DRIFT, scanning electron microscopy and energy dispersive spectrometry (MEV/EDS. Infrared spectroscopy and elemental analyses confirmed the presence of organic chains and thiol groups in the modified clay. The immobilized and available thiol group, measured according to the Volhard method, totaled 1.4 meq/g of clay, with approximately 90% accessible for Ag+ trapping. These results represent an improvement as compared to other works concerning the functionalization of smectite-type clays in which the effect produced by functional group blockage limits the access of species to less than 10% of the complexing sites.
International Nuclear Information System (INIS)
Lerouge, C.; Grangeon, S.; Wille, G.; Flehoc, C.; Gailhanou, H.; Gaucher, E.C.; Tournassat, C.; Vinsot, A.; Made, B.; Altmann, S.
2013-01-01
In the pore water chemistry model of the Callovian-Oxfordian clay formation, the divalent cations Ca, Mg, and Fe are controlled by equilibrium reactions with pure carbonates: calcite for Ca, dolomite for Mg, and siderite for Fe. Results of a petrological study and computing of the Ca/Mg and Ca/Fe activity ratios based on natural pore water chemistry provide evidence that equilibrium with pure calcite and pure dolomite is a reasonable assumption for undisturbed pore waters; on the other hand, siderite cannot be considered at equilibrium with pore waters at the formation scale. (authors)
Energy Technology Data Exchange (ETDEWEB)
Lerouge, C.; Grangeon, S.; Wille, G.; Flehoc, C.; Gailhanou, H.; Gaucher, E.C.; Tournassat, C. [BRGM av. Claude Guillemin BP6009 45060 Orleans cedex 2 (France); Vinsot, A. [ANDRA Meuse/Haute-Marne Underground research Laboratory (URL), RD 960, 55290 Bure (France); Made, B.; Altmann, S. [ANDRA - Parc de la Croix Blanche, 1-7 rue Jean Monnet, 92298 Chatenay-Malabry Cedex (France)
2013-07-01
In the pore water chemistry model of the Callovian-Oxfordian clay formation, the divalent cations Ca, Mg, and Fe are controlled by equilibrium reactions with pure carbonates: calcite for Ca, dolomite for Mg, and siderite for Fe. Results of a petrological study and computing of the Ca/Mg and Ca/Fe activity ratios based on natural pore water chemistry provide evidence that equilibrium with pure calcite and pure dolomite is a reasonable assumption for undisturbed pore waters; on the other hand, siderite cannot be considered at equilibrium with pore waters at the formation scale. (authors)
International Nuclear Information System (INIS)
Perdicakis, Michel
2012-01-01
Document available in extended abstract form only. In many countries, it is planned that the long life highly radioactive nuclear spent fuel will be stored in deep argillaceous rocks. The sites selected for this purpose are anoxic and satisfy several recommendations as mechanical stability, low permeability and low redox potential. Pyrite (FeS 2 ), iron(II) carbonate, iron(II) bearing clays and organic matter that are present in very small amounts (about 1% w:w) in soils play a major role in their reactivity and are considered today as responsible for the low redox potential values of these sites. In this communication, we describe an electrochemical technique derived from 'Salt matrix voltammetry' and allowing the almost in-situ voltammetric characterization of air-sensitive samples of soils after the only addition of the minimum humidity required for electrolytic conduction. Figure 1 shows the principle of the developed technique. It consists in the entrapment of the clay sample between a graphite working electrode and a silver counter/quasi-reference electrode. The sample was previously humidified by passing a water saturated inert gas through the electrochemical cell. The technique leads to well-defined voltammetric responses of the electro-active components of the clays. Figure 2 shows a typical voltammogram relative to a Callovo-Oxfordian argillite sample from Bure, the French place planned for the underground nuclear waste disposal. During the direct scan, one can clearly distinguish the anodic voltammetric signals for the oxidation of the iron (II) species associated with the clay and the oxidation of pyrite. The reverse scan displays a small cathodic signal for the reduction of iron (III) associated with the clay that demonstrates that the majority of the previously oxidized iron (II) species were transformed into iron (III) oxides reducible at lower potentials. When a second voltammetric cycle is performed, one can notice that the signal for iron (II
Re-dispersion of alumina particles in water: influence of the surface state
International Nuclear Information System (INIS)
Desset, Sabine
1999-01-01
The aim of this work was to determine the mechanisms by which suspensions of alpha alumina particles may be dried and then re-dispersed spontaneously in water. To get reproducible results, we designed appropriate protocols: (i) for preparing the surface state, and for generating controlled interparticle contacts (presence of water or complexing agents); (ii) for measuring the amount of re-dispersed material with a proper averaging over all interparticle bonds (turbidity). These results show that there are thresholds, determined by the conditions of drying and re-dispersion, where all the powder goes from the aggregated state to the dispersed state. With hydrated powders, it was found that mild changes in the chemical conditions (pH) and application of very weak mechanical forces (sedimentation) were enough to cause significant change in re-dispersion. According to these thresholds, a re-dispersion mechanism could be identified. Re-dispersion is ruled, indeed, by a balance of forces and the displacement of the re-dispersion thresholds indicates a shift in the balance of forces. These forces are the well known forces that control colloidal stability: van der Waals attraction, electrostatic repulsion and hydration forces. We found that hydration acts as a repulsive wall corresponding to one or two monolayers of water on each surface and depends on the Relative Humidity of drying. We also found that electrostatic repulsions at short separations are much weaker than the predictions based on the Poisson Boltzmann equation, but should be modelled according to the triple layer model. Repulsions to be considered are those calculated with the screened charges of the particles. Another aim of this work was to facilitate re-dispersion by using complexing agents that bind to the surfaces and add a steric repulsion We have found that molecules with carboxylic and hydroxyl groups can be efficient in this respect, if they are bound to surfaces before aggregation, if they are not
Re-dispersion of alumina particles in water: influence of the surface state
International Nuclear Information System (INIS)
Desset, Sabine
1999-01-01
The aim of this work was to determine the mechanisms by which suspensions of alpha alumina particles may be dried and then re-dispersed spontaneously in water. To get reproducible results, we designed appropriate protocols: (i) for preparing the surface state, and for generating controlled interparticle contacts (presence of water or complexing agents); (ii) for measuring the amount of re-dispersed material with a proper averaging over all interparticle bonds (turbidity). These results show that there are thresholds, determined by the conditions of drying and re-dispersion, where all the powder goes from the aggregated state to the dispersed state. With hydrated powders, it was found that mild changes in the chemical conditions (pH) and application of very weak mechanical forces (sedimentation) were enough to cause significant change in re-dispersion. According to these thresholds, a re-dispersion mechanism could be identified. Re-dispersion is ruled, indeed, by a balance of forces and the displacement of the re-dispersion thresholds indicates a shift in the balance of forces. These forces are the well-known forces that control colloidal stability: van der Waals attraction, electrostatic repulsion and hydration forces. We found that hydration acts as a repulsive wall corresponding to one or two monolayers of water on each surface and depends on the Relative Humidity of drying. We also found that electrostatic repulsions at short separations are much weaker than the predictions based on the Poisson Boltzmann equation, but should be modelled according to the triple layer model. Repulsions to be considered are those calculated with the screened charges of the particles. Another aim of this work was to facilitate re-dispersion by using complexing agents that bind to the surfaces and add a steric repulsion We have found that molecules with carboxylic and hydroxyl groups can be efficient in this respect, if they are bound to surfaces before aggregation, if they are not
Clay slurry and engineered soils as containment technologies for remediation of contaminated sites
International Nuclear Information System (INIS)
Williams, J.R.; Dudka, S.; Miller, W.P.; Johnson, D.O.
1997-01-01
Clay Slurry and Engineered Soils are containment technologies for remediation of waste disposal sites where leaching, groundwater plumes and surface runoff of contaminants are serious ecological hazards to adjacent environments. This technology is a patent-pending process which involves the use of conditioned clay materials mixed with sand and water to form a readily pourable suspension, a clay slurry, which is either placed into a trench barrier system or allowed to de-water to create Engineered Soils. The Engineered Soil forms a layer impervious to water and air, therefore by inhibiting both water and oxygen from penetrating through the soil the material. This material can be installed in layers and as a vertical barrier to create a surface barrier containment system. The clay percentage in the clay slurry and Engineered Soils varies depending on site characteristics and desired performance standards. For example Engineered Soils with 1-2% of clay (dry wt.) had a hydraulic conductivity (K) of 10 -8 to 10 -1 cm/sec. Tests of tailing materials from a kyanite and pyrite mine showed that the clay slurry was effective not only in reducing the permeability of the treated tailings, but also in decreasing their acidity due to the inherent alkalinity of the clay. The untreated tailings had pH values in the range of 2.4 - 3.1; whereas, the effluent from clay and tailings mixtures had pH values in a slightly alkaline range (7.7-7.9). Pug-mills and high volume slurry pumps can be readily adapted for use in constructing and placing caps and creating Engineered Soils. Moreover, material on site or from a local sand supply can be used to create clay slurries and engineered soils. Clay materials used in cap construction are likewise readily available commercially. As a result, the clay slurry system is very cost effective compared to other capping systems, including the commonly used High Density Polyethylene (HDPE) liner systems
Investigations of excavated clay-stone as backfill/seal material
International Nuclear Information System (INIS)
Zhang, Chun-Liang
2012-01-01
Document available in extended abstract form only. Crushed clay-stone produced by excavation activities of repository drifts has been investigated as backfill/seal material at the GRS laboratory. The raw aggregate with coarse grains is considered to be used for backfilling the repository openings and, in mixture with bentonite, for sealing the boreholes, drifts and shafts. The GRS research programme focused on characterizing the thermo-hydro-mechanical properties of the excavated Callovo-Oxfordian clay-stone (COX) and the clay-stone-bentonite mixtures, including mechanical compaction, gas and water permeability as function of porosity, water retention and saturation, swelling capacity, and thermal properties of the materials. The most important results are presented in this paper. Figure 1 shows the compaction and permeability behaviour of the excavated clay-stone with grains up to a size of 32 mm. The results were obtained on large samples of 280 mm diameter and 680 mm height under quasi-hydrostatic compression. The porosity and permeability decrease with increasing load. The porosity-mean stress relation is non-linear and may be expressed by an exponential function. The backfill becomes stiffer at low porosities and can sustain certain deviatoric loads. At porosity of ∼21 %, the strength is characterized by an inherent cohesion of 3.7 MPa and an internal friction angle of 12 deg.. Additionally, the compaction is also dependent on time or loading rate, water content, and temperature. The compaction of the porous backfill material leads to a reduction in permeability. The measured gas permeability decreases much faster at low porosities below ∼25 %. The gas permeability at porosity of ∼20 % becomes as low as that of 10 -20 - 10 -21 m 2 for the intact clay rock. This is probably due to disconnection of the pore network during the compaction. As sealing material, powdered COX clay-stone was mixed with MX80 bentonite powder in different ratios and compacted to
International Nuclear Information System (INIS)
Vasconcelos, P.N.M.; Sousa, A.B.; Sousa, A.K.F.; Rodrigues, M.G.F.; Laborde, H.M.
2012-01-01
The clays exhibit interesting properties in adsorption of heavy metals in wastewater. This property can be modified by thermal activation. In this work, the characterization of clay Brasgel before and after thermal activation (200 deg C 300 deg C 400 deg C and 500 deg C) is performed by cation exchange capacity (CEC), X-ray Spectroscopy for Energy Dispersion (EDX), X-ray diffraction (XRD) and Differential Thermal Analysis and Gravimetric (DTA / TG). The main differences between natural and activated clays are the structural changes observed by XRD and DTA / TG. (author)
Study of process variables on organophilization of Cubati-PB bentonite clays with ionic surfactants
International Nuclear Information System (INIS)
Silva, C.D. da; Lima, R.C.O.; Costa, J.M.R.; Silva, E.I.A.; Neves, G.A.; Ferreira, H.C.
2012-01-01
The organophilic clays used as agent in the composition dispersed in petroleum drilling fluids, play important roles during drilling. This work aims at the development of several varieties of smectites Cubati-PB for use in drilling fluids for oil with the use of ionic surfactants. We used the following materials: natural bentonite clay Cinza Superior and Verde Superior, from the district of Cubati-PB and ionic quaternary ammonium salt: Praepagen WB®, with 45% active matter. The organoclays were characterized by the laser diffraction, chemical composition by x-ray, differential thermal analysis, thermal gravimetric analysis and x-ray diffraction. Globally found that clays have diffraction and thermal behavior typical of bentonite clay. The results showed showed that the clay used has the potential for application in the process of organophilic and, with respect the process variables has been observed that they do not alter the process organophilization. (author)
Mechanisms associated with the high adsorption of dibenzo-p-dioxin from water by smectite clays.
Liu, Cun; Li, Hui; Teppen, Brian J; Johnston, Cliff T; Boyd, Stephen A
2009-04-15
Clay minerals may be an important unrecognized sorptive phase for dioxins in soils and clay deposits. Smectites, especially Cs-saponite, effectively adsorbed dibenzo-p-dioxin (DD) from water, reaching 0.8% (wt/wt). Adsorption was promoted by exchangeable cations with low hydration energies, and negative charge in the smectite arising from the tetrahedral siloxane sheets. X-ray diffraction measurements revealed that as DD loading increased to > or =8000 mg/kg the clay basal spacing increased abruptly from 12.3 to 15.2 A demonstrating DD intercalation. The 12.3 A spacing provides an interlayer distance that closely matches the molecular thickness of DD. In this configuration DD is essentially dehydrated as it interacts with the opposing hydrophobic siloxane sheets and with coplanar Cs+ via one of the dioxin ring oxygens. Ab initio calculations suggest that geometrical structures form at higher loadings in which intercalated DD molecules adopt a butterfly geometry sandwiched between dehydrated interlayer Cs+ and the siloxane surface, consistent with the 15.2 A spacing, wherein Cs+ interacts with dioxin ring oxygens and benzene ring pi-electrons. Fourier transformation infrared measurements confirm that adsorbed DD is present in orientations that are not parallel with the interlayer planar siloxane surfaces of smectite.
Active containment systems incorporating modified pillared clays
International Nuclear Information System (INIS)
Lundie, P.; McLeod, N.
1997-01-01
The application of treatment technologies in active containment systems provides a more advanced and effective method for the remediation of contaminated sites. These treatment technologies can be applied in permeable reactive walls and/or funnel and gate systems. The application of modified pillared clays in active containment systems provides a mechanism for producing permeable reactive walls with versatile properties. These pillared clays are suitably modified to incorporate reactive intercalatants capable of reacting with both a broad range of organic pollutants of varying molecular size, polarity and reactivity. Heavy metals can be removed from contaminated water by conventional ion-exchange and other reactive processes within the clay structure. Complex contamination problems can be addressed by the application of more than one modified clay on a site specific basis. This paper briefly describes the active containment system and the structure/chemistry of the modified pillared clay technology, illustrating potential applications of the in-situ treatment process for contaminated site remediation
Energy Technology Data Exchange (ETDEWEB)
Honorato, Luciana R.; Silva, Adriana A.; Soares, Bluma G. [Universidade Federal do Rio de Janeiro - UFRJ, Instituto de Macromoleculas Professora Eloisa Mano, Rio de Janeiro, RJ (Brazil); Soares, Ketly P. [Centro Universitario do Leste de Minas Gerais (UNILESTEMG) - Coronel Fabriciano, MG (Brazil)
2011-07-01
The effect of organophilic clay on the mechanical and dynamical-mechanical properties of thermoplastic elastomers based on polypropylene (PP) and nitrile rubber (NBR) was investigated. The addition of clay was performed from a master batch prepared by a solution intercalation of NBR inside the clay galleries. Since the PP/NBR blend is highly incompatible, PP functionalized with maleic anhydride (PP-g-MA) and carboxylated NBR (XNBR) were employed as compatibilizing system together with triethylene-tetramine (TETA) used as coupling agent. The addition of Clay inside the elastomeric phase of the TPV resulted in a significant decrease of the elongation at break without changes on the tensile strength. The presence of clay also promoted a slight increase of the storage modulus and the glass transition temperature. The small angle X ray scattering confirmed the high dispersion of clay inside the TPV. Analysis of light scattering small angle (SAXS) confirmed the high dispersion of clay in the matrix of the TPV. (author)
High-performance 3D printing of hydrogels by water-dispersible photoinitiator nanoparticles.
Pawar, Amol A; Saada, Gabriel; Cooperstein, Ido; Larush, Liraz; Jackman, Joshua A; Tabaei, Seyed R; Cho, Nam-Joon; Magdassi, Shlomo
2016-04-01
In the absence of water-soluble photoinitiators with high absorbance in the ultraviolet (UV)-visible range, rapid three-dimensional (3D) printing of hydrogels for tissue engineering is challenging. A new approach enabling rapid 3D printing of hydrogels in aqueous solutions is presented on the basis of UV-curable inks containing nanoparticles of highly efficient but water-insoluble photoinitiators. The extinction coefficient of the new water-dispersible nanoparticles of 2,4,6-trimethylbenzoyl-diphenylphosphine oxide (TPO) is more than 300 times larger than the best and most used commercially available water-soluble photoinitiator. The TPO nanoparticles absorb significantly in the range from 385 to 420 nm, making them suitable for use in commercially available, low-cost, light-emitting diode-based 3D printers using digital light processing. The polymerization rate at this range is very fast and enables 3D printing that otherwise is impossible to perform without adding solvents. The TPO nanoparticles were prepared by rapid conversion of volatile microemulsions into water-dispersible powder, a process that can be used for a variety of photoinitiators. Such water-dispersible photoinitiator nanoparticles open many opportunities to enable rapid 3D printing of structures prepared in aqueous solutions while bringing environmental advantages by using low-energy curing systems and avoiding the need for solvents.
Advanced 2D and 3D Electron Microscopy Analysis of Clay/PP Nanocomposites
DEFF Research Database (Denmark)
Mosca, Alessandra; Roberts, Ashley; Daviðsdóttir, Svava
2011-01-01
) equipped with field emission gun (FEG) and through lens detector (TLD) was used for high resolution 3D imaging of the material via slice-and-view technique [2]. Image analysis was performed using Matlab. Results and Discussion Figure 1 (a) shows a TEM micrograph of a clay/PP nanocomposite, where the clay...... of nanometres and are rather uniformly oriented, distributed, and spaced from each other. Image analysis from these micrographs is very useful since a rather large field view is analysed as compared to TEM micrographs, which are traditionally used to study such properties. Figure 3 (a) shows a high resolution......Introduction Clay/polypropylene (PP) nanocomposites with engineered properties are attractive in developing novel components of interest in a plurality of application fields [1]. An understanding of clay dispersion and intercalation in the polymeric matrix is of great importance to explain...
Senior, Lisa A.; Koerkle, Edward H.
2003-01-01
The Christina River Basin drains 565 square miles (mi2) in Pennsylvania, Maryland, and Delaware. Water from the basin is used for recreation, drinking water supply, and to support aquatic life. The Christina River Basin includes the major subbasins of Brandywine Creek, White Clay Creek, and Red Clay Creek. The White Clay Creek is the second largest of the subbasins and drains an area of 108 mi2. Water quality in some parts of the Christina River Basin is impaired and does not support designated uses of the streams. A multi-agency water-quality management strategy included a modeling component to evaluate the effects of point and nonpoint-source contributions of nutrients and suspended sediment on stream water quality. To assist in non point-source evaluation, four independent models, one for each of the three major subbasins and for the Christina River, were developed and calibrated using the model code Hydrological Simulation Program—Fortran (HSPF). Water-quality data for model calibration were collected in each of the four main subbasins and in smaller subbasins predominantly covered by one land use following a nonpoint-source monitoring plan. Under this plan, stormflow and base- flow samples were collected during 1998 at two sites in the White Clay Creek subbasin and at nine sites in the other subbasins.The HSPF model for the White Clay Creek Basin simulates streamflow, suspended sediment, and the nutrients, nitrogen and phosphorus. In addition, the model simulates water temperature, dissolved oxygen, biochemical oxygen demand, and plankton as secondary objectives needed to support the sediment and nutrient simulations. For the model, the basin was subdivided into 17 reaches draining areas that ranged from 1.37 to 13 mi2. Ten different pervious land uses and two impervious land uses were selected for simulation. Land-use areas were determined from 1995 land-use data. The predominant land uses in the White Clay Creek Basin are agricultural, forested
Clay membrane made of natural high plasticity clay
DEFF Research Database (Denmark)
Foged, Niels; Baumann, Jens
1998-01-01
Leachate containment in Denmark has through years been regulated by the DIF Recommendation for Sanitary Landfill Liners (DS/R 466). It states natural clay deposits may be used for membrane material provided the membrane and drainage system may contain at least 95% of all leachate created throughout...... ion transport as well as diffusion.Clay prospection for clays rich in smectite has revealed large deposits of Tertiary clay of very high plasticity in the area around Rødbyhavn on the Danish island Lolland. The natural clay contains 60 to 75% smectite, dominantly as a sodium-type. The clay material...... has been evaluated using standardised methods related to mineralogy, classification, compaction and permeability, and initial studies of diffusion properties have been carried out. Furthermore, at a test site the construction methods for establishing a 0.15 to 0.3m thick clay membrane have been tested...
Clay membrane made of natural high plasticity clay:
DEFF Research Database (Denmark)
Foged, Niels; Baumann, Jens
1999-01-01
Leachate containment in Denmark has throughout the years been regulated by the DIF Recommendation for Sanitary Landfill Liners (DS/R4669. It states that natural clay deposits may be used as membrane material provided the membrane and drainage system contains at least 95% of all leachate created...... into account advective ion transport as well as diffusion. Clay prospecting for clays rich in smectite has revealed large deposits of Tertiary clay of very high plasticity in the area around Rødbyhavn on the Danish island of Lolland. The natural clay contains 60-75% smectite, dominantly as a sodium......-type. The clay material has been evaluated using the standardized methods related to mineralogy, classification, compaction and permeability, and initial studies of diffusion properties have been carried out. Furthermore, at a test site the construction methods for establishing a 0.15-0.3 m thick clay membrane...
Charlet, Laurent; Alt-Epping, Peter; Wersin, Paul; Gilbert, Benjamin
2017-08-01
Clay rocks are low permeability sedimentary formations that provide records of Earth history, influence the quality of water resources, and that are increasingly used for the extraction or storage of energy resources and the sequestration of waste materials. Informed use of clay rock formations to achieve low-carbon or carbon-free energy goals requires the ability to predict the rates of diffusive transport processes for chemically diverse dissolved and gaseous species over periods up to thousands of years. We survey the composition, properties and uses of clay rock and summarize fundamental science challenges in developing confident conceptual and quantitative gas and solute transport models.
International Nuclear Information System (INIS)
Baldi, G.; Hueckel, T.; Peano, A.; Pellegrini, R.
1991-01-01
This study is composed of two parts: The first part (Volume 1) lays the foundations of a comprehensive theoretical treatment of the interaction between water and soil skeleton during thermal dilatation. The second part (volume 2) is devoted to the development and the application of advance constitutive modelling of mechanical behaviour of clays taking into account the extensive tests of Boom clay reported in the first volume. The development concentrated on the improvement of prediction of the volumetric response of clay skeleton: (a) improving the dilatancy prediction at low to high overconsolidation ratios (Section 2). An elasto-plastic constitutive model has been developed to account for this effect (Section 3.2.); (b) modelling of swelling effects (Section 2.5). A preliminary interpretative model for swelling prediction has been developed (Section 2.5). The application part consisted in interpreting the experimental results obtained for Boom clay to calibrate a set of constants (Section 3) for performing numerical analyses (Section 4) for the thermomechanical model already calibrated for Boom clay (Appendix). Interpretation of the tests required an assessment of influence of the strong anisotropy effects revealed by Boom clay on the basis of an interpretative model characterized by a kinematic hardening plasticity and coupled elasticity (section 3)
Zolfaghari-Baghbaderani, Azadeh; Emtyazjoo, Mozhgan; Poursafa, Parinaz; Mehrabian, Sedigheh; Bijani, Samira; Farkhani, Daryoush; Mirmoghtadaee, Parisa
2012-01-01
To determine the most effective and biodegradable dispersant of spilled oil in water surrounding two Persian Gulf provinces. This study compared the effects of three dispersants, Pars 1, Pars 2, and Gamlen OD4000 on removal of oil in two Persian Gulf provinces' water. Overall, 16 stations were selected. Using the Well method, the growth rate of isolated bacteria and fungi was identified. To specify the growth rate of microorganisms and their usage of oil in the presence of the above-mentioned dispersants, as exclusive sources of carbon, the bacteria were grown in culture medium for 28 days at 120 rpm, 30°C, and their optical density was measured by spectrophotometry. Then, we tested biological oxygen demand (BOD) and chemical oxygen demand (COD) in microorganisms. The highest growth rate was documented for the growth of microorganisms on either Pars 1 or Pars 2 dispersants or their mixtures with oil. However, the culture having microorganisms grown on Pars 1 had higher BOD and COD than the other two dispersants (9200 and 16800 versus 500 and 960, P microorganisms grown on Pars 2 had maximum amount of BOD and COD in comparison with Pars 1 and Gamlen dispersants (7100 and 15200 versus 6000 and 10560, P < 0.05). Pars 1 and Pars 2 were the most effective dispersants with highest degradability comparing Gamlen. In each region, the most suitable compound for removing oil spill from offshores with least secondary contamination should be investigated.
Hydro-mechanical properties of the red salt clay (T4) - Natural analogue of a clay barrier
International Nuclear Information System (INIS)
Minkley, W.; Popp, T.; Salzer, K.; Gruner, M.; Boettge, V.
2010-01-01
Document available in extended abstract form only. Long-term storage of high-level radioactive waste in deep geologic formations is worldwide the only accepted solution to warranty long term safety. Besides clay and crystalline rocks, salt is one of the potential host-rock candidates, mainly favored in Germany. As salts rocks are highly soluble their barrier integrity against water inflow from the cap rock is questionable. Argillaceous cap rocks or intercalated clay layers may act as protective shield in the hanging wall above a repository, thus providing a multi-barrier system. The aims of our study are twofold: 1) to characterize the mineralogical, hydraulic and rock-mechanical properties of the so-called Red Salt Clay (T4) as natural analogue of a clay barriers represented by different states of induration corresponding to various depth of burial diagenesis; 2) to demonstrate the favoured barrier properties of an argillaceous layer in the top of a salt formation undergoing dynamic processes such as rock bursts. The so-called Red Salt Clay (T4) is deposited as clay rich clastic sediment at the base of the Aller-series forming a persistent lateral layer above the lower Zechstein-series. The thickness of the clay-formation becomes smaller with decreasing distance from the border of the basin, i.e. from ∼15 m at Rossleben, over 7 m at Bernburg to 3.5 m at Zielitz, all in Saxony-Anhalt, D). The mineralogical composition of the Red Salt Clay varies, e.g. average composition for the Teutschenthal area: clay minerals 54% (Chlorite: 8%; Illite/Muscovite: 46%); quartz: 22%; anhydrite: 15%; accessory gypsum; Halite: 6%, Hematite: ∼ 2%). The geochemical and mineralogical composition of the Red Salt Clay represents a final state of natural salt-clay-systems, thus standing as a natural analogue for bentonite-based sealing systems in contact with high-saline solutions (e.g. saturated NaCl-solution, solutions with various Mg 2+ -, K + -, SO 4 2- - concentrations). The
Cui, Mingjun; Ren, Siming; Chen, Jia; Liu, Shuan; Zhang, Guangan; Zhao, Haichao; Wang, Liping; Xue, Qunji
2017-03-01
Homogenous dispersion of hexagonal boron nitride (h-BN) nanosheets in solvents or in the polymer matrix is crucial to initiate their many applications. Here, homogeneous dispersion of hexagonal boron nitride (h-BN) in epoxy matrix was achieved with a water-soluble carboxylated aniline trimer derivative (CAT-) as a dispersant, which was attributed to the strong π-π interaction between h-BN and CAT-, as proved by Raman and UV-vis spectra. Transmission electron microscopy (TEM) analysis confirmed a random dispersion of h-BN nanosheets in the waterborne epoxy coatings. The deterioration process of water-borne epoxy coating with and without h-BN nanosheets during the long-term immersion in 3.5 wt% NaCl solution was investigated by electrochemical measurements and water absorption test. Results implied that the introduction of well dispersed h-BN nanosheets into waterborne epoxy system remarkably improved the corrosion protection performance to substrate. Moreover, 1 wt% BN/EP composite coated substrate exhibited higher impedance modulus (1.3 × 106 Ω cm2) and lower water absorption (4%) than those of pure waterborne epoxy coating coated electrode after long-term immersion in 3.5 wt% NaCl solution, demonstrating its superior anticorrosive performance. This enhanced anticorrosive performance was mainly ascribed to the improved water barrier property of epoxy coating via incorporating homogeneously dispersed h-BN nanosheets.
Halloysite nanotubule clay for efficient water purification.
Zhao, Yafei; Abdullayev, Elshad; Vasiliev, Alexandre; Lvov, Yuri
2013-09-15
Halloysite clay has chemical structure similar to kaolinite but it is rolled in tubes with diameter of 50 nm and length of ca. 1000 nm. Halloysite exhibits higher adsorption capacity for both cationic and anionic dyes because it has negative SiO2 outermost and positive Al2O3 inner lumen surface; therefore, these clay nanotubes have efficient bivalent adsorbancy. An adsorption study using cationic Rhodamine 6G and anionic Chrome azurol S has shown approximately two times better dye removal for halloysite as compared to kaolin. Halloysite filters have been effectively regenerated up to 50 times by burning the adsorbed dyes. Overall removal efficiency of anionic Chrome azurol S exceeded 99.9% for 5th regeneration cycle of halloysite. Chrome azurol S adsorption capacity decreases with the increase of ionic strength, temperature and pH. For cationic Rhodamine 6G, higher ionic strength, temperature and initial solution concentration were favorable to enhanced adsorption with optimal pH 8. The equilibrium adsorption data were described by Langmuir and Freundlich isotherms. Copyright © 2013 Elsevier Inc. All rights reserved.
Clay and plant materials such as wood are the raw materials used in manufacture of ceramic water filtration devices around the world. A step by step manufacturing procedure which includes initial mixing, molding and sintering is used. The manufactured ceramic filters have numerous pores which help i...
The molecular aggregation of pyronin Y in natural bentonite clay suspension
International Nuclear Information System (INIS)
Meral, Kadem; Yilmaz, Nuray; Kaya, Mehmet; Tabak, Ahmet; Onganer, Yavuz
2011-01-01
The molecular aggregation and spectroscopic properties of Pyronin Y (PyY) in the suspension containing natural bentonite clay were studied using molecular absorption, steady-state and time-resolved fluorescence spectroscopy techniques. Interaction between the clay particles and the cationic dye compounds in aqueous solution resulted in significant changes in spectral properties of PyY compared to its molecular behavior in deionized water at the same concentration. These changes were due to the formation of dimer and aggregate of PyY in the clay suspension as well as the presence of the dye monomer. The H-type aggregates of PyY in the clay suspension were identified by the observation of a blue-shifted absorption band of the dye compared to that of its monomer. In spite of diluted dye concentrations, the H-aggregate of PyY in the clay suspension was formed. The intensive aggregation in the clay suspension attributed to the localized high dye concentration on the negatively charged clay surfaces. Adsorption sites of PyY on the clay particles were discussed by deconvulated absorption and excitation spectra. Fluorescence spectroscopy studies revealed that the fluorescence intensity of PyY in the clay suspension is decreased by H-aggregates drastically. Moreover, the presence of H-aggregates in the clay suspension resulted in the decrease of fluorescence lifetime and quantum yield of PyY compared to those in deionized water. - Highlights: → Molecular behavior of PyY adsorbed on clay surface was followed spectroscopically. → H-aggregates of PyY in the clay suspension were formed at very low dye concentrations. → The intensive H-aggregate structure drastically reduced the fluorescence intensity of PyY. → The fluorescence lifetime and quantum yield of PyY in the clay suspension was discussed.
Impact of monovalent cations on soil structure. Part II. Results of two Swiss soils
Farahani, Elham; Emami, Hojat; Keller, Thomas
2018-01-01
In this study, we investigated the impact of adding solutions with different potassium and sodium concentrations on dispersible clay, water retention characteristics, air permeability, and soil shrinkage behaviour using two agricultural soils from Switzerland with different clay content but similar organic carbon to clay ratio. Three different solutions (including only Na, only K, and the combination of both) were added to soil samples at three different cation ratio of soil structural stability levels, and the soil samples were incubated for one month. Our findings showed that the amount of readily dispersible clay increased with increasing Na concentrations and with increasing cation ratio of soil structural stability. The treatment with the maximum Na concentration resulted in the highest water retention and in the lowest shrinkage capacity. This was was associated with high amounts of readily dispersible clay. Air permeability generally increased during incubation due to moderate wetting and drying cycles, but the increase was negatively correlated with readily dispersible clay. Readily dispersible clay decreased with increasing K, while readily dispersible clay increased with increasing K in Iranian soil (Part I of our study). This can be attributed to the different clay mineralogy of the studied soils (muscovite in Part I and illite in Part II).
Development of silver and clay-starch bio-nanocomposites
Abreu, Ana S.; Oliveira, M.; Machado, A. V.
2014-01-01
Starch, among biopolymers is that had the lowest production cost, wide availability, fully biodegradability and is a renewable agriculture resource. Starch due to its sensitivity to humidity and poor mechanical properties cannot be used in many applications. For that, the dispersion of clays in this material improves their physical and mechanical properties, at very low filler loadings. On the other hand, the incorporation of silver nanoparticles into biocompatible and biod...
Thomas, J.R.; Gibson, D.J.; Middleton, B.A.
2005-01-01
Riparian corridors promote dispersal of several species of exotic invasives worldwide. Dispersal plays a role in the colonization of exotic invasive species into new areas and this study was conducted to determine if the invasiveness of Dioscorea oppositifolia L. (Chinese yam) is facilitated by secondary dispersal of vegetative diaspores (bulbils) by water. Since seed production of this plant has not been observed in the United States, bulbils represent the only means of dispersal to new habitats. Dispersal was monitored by placing aquatic traps, tethered bulbils, and painted bulbil caches in a tributary of Drury Creek, Giant City State Park, Illinois. Results indicate that high-energy flow in the creek accelerated secondary dispersal of bulbils downstream and onto the floodplain. The longest recorded dispersal distance was 206.2 m downstream. Dispersal distance of tethered bulbils was not related to rainfall or flow velocity in the creek; however the total number of bulbils trapped was positively related to flow velocity. We conclude that secondary dispersal by water in streams can facilitate dispersal of vegetative bulbils of this exotic species.
Directory of Open Access Journals (Sweden)
Parvin Zakeri-Milani
2011-06-01
Full Text Available Introduction: Prednisolone is a class II substance according to the Biopharmaceutics Classification System. It is a poorly water soluble agent. The aim of the present study was to improve dissolution rate of a poorly water-soluble drug, prednisolone, by a solid dispersion technique. Methods: Solid dispersion of prednisolone was prepared with PEG 6000 or different carbohydrates such as lactose and dextrin with various ratios of the drug to carrier i.e., 1:10, 1:20 and 1:40. Solid dispersions were prepared by coevaporation method. The evaluation of the properties of the dispersions was performed using dissolution studies, Fourier-transform infrared spectroscopy and x-ray powder diffractometery. Results: The results indicated that lactose is suitable carriers to enhance the in vitro dissolution rate of prednisolone. The data from the x-ray diffraction showed that the drug was still detectable in its solid state in all solid dispersions except solid dispersions prepared by dextrin as carrier. The results from infrared spectroscopy showed no well-defined drug–carrier interactions for coevaporates. Conclusion: Solid dispersion of a poorly water-soluble drug, prednisolone may alleviate the problems of delayed and inconsistent rate of dissolution of the drug.
Boni, A; Albertazzi, L.; Innocenti, C; Gemmi, M; Bifone, A
2013-01-01
A novel and facile method for water dispersal of hydrophobic iron oxide nanoparticles based on the amphiphilic PAMAM-C-12 dendrimer is described. Stable and highly concentrated water dispersions of multifunctional, magnetic nanoparticles were obtained with this single-step approach, and showed
SODIUM TITANATE NANOBELT AS A MICROPARTICLE TO INDUCE CLAY FLOCCULATION WITH CPAM
Directory of Open Access Journals (Sweden)
Wenxia Liu
2010-07-01
Full Text Available Sodium titanate nanobelt was synthesized by treating titanium dioxide hydrothermally in concentrated sodium hydroxide solution. The product was characterized by SEM analysis and zeta potential measurement. It served as a microparticle to constitute a microparticle retention system with cationic polyacrylamide (CPAM, while the microparticle system was employed to induce the flocculation of kaolin clay. The flocculation behavior of kaolin clay in such a system was investigated by using a photometric dispersion analyzer connected with a dynamic drainage jar. It was found that the sodium titanate nanobelt carried negative charges and had a lower zeta potential at higher pH. It gave a large synergistic flocculation effect with CPAM at a very low dosage, and showed higher flocculation effect with CPAM under neutral and weak alkaline conditions. A suitably high shear level was helpful for the re-flocculation of clay by sodium titanate nanobelt. The clay flocculation induced by CPAM/titanate nanobelt system demonstrated high shear resistance and also generated dense flocs.
Ramasamy, Shamala; Abdullah, Mohd Mustafa Al Bakri; Huang, Yue; Hussin, Kamarudin; Wang, Jin; Shahedan, Noor Fifinatasha
2017-09-01
Geopolymer is an uprising technology that is being studied worldwide. Geopolymer raw materials are basically aluminosilicate source materials. However, this technology is yet to infiltrate into pipelines and coating industries which initiated our research idea. The idea of creating universal geopolymer based coating material is mainly to help oil and gas industry reduce its maintenance cost. Kaolin based geopolymer paste was coated on glass reinforced epoxy (GRE) substrates which are majorly used as pipeline material in the oil and gas industry at Saudi Arabia. Kaolin and white clay was chosen as raw material to study the possibilities of utilizing underused aluminosilicate raw materials for geopolymer coating. To obtain suitable formulation, Na2SiO3/NaOH ratio was varied from 0.40 untill 0.60 while other parameters such as solid/liquid ratio and NaOH molarity were kept constant at values as per previous works. Geopolymer coated GRE substrates were then subjected to water absorption, flexural strength and hardness test to validate our findings. Water absorption is a crucial test as for coating materials which justifies the pratical usability of the coating product. Upon testing, kaolin and white clay based geopolymer coating each shows promising properties at Na2SiO3/NaOH ratio of 0.45 and 0.50 each.
International Nuclear Information System (INIS)
Aikman, M.; Mirotchnik, K.; Kantzas, A.
1997-01-01
A potential remediation method for hydrocarbon contaminated soils was discussed. The new method was based on the use of proven and economic petroleum reservoir engineering methods for soil remediation. The methods that were applied included water and gas displacement methods together with horizontal boreholes as the flow inlet and outlets. This system could be used in the case of spills that seep beneath a plant or other immovable infrastructure which requires in-situ treatment schemes to decontaminate the soil. A study was conducted to characterize native soils and water samples from industrial plants in central Alberta and Sarnia, Ontario and to determine the variables that impact upon the flow conditions of synthetic test materials. The methods used to characterize the soils included X-Ray computed tomographic analysis, grain size and density measurements, and X-Ray diffraction. Clay content, initial water saturation, and water and gas flow rate were the variables that impacted on the flow conditions
Migration of leachate solution through clay soil
Energy Technology Data Exchange (ETDEWEB)
Abdel Warith, M M
1987-01-01
The problem of domestic solid wastes buried in landfill sites is viewed from the aspect of leachate contamination and migration in the substrate, and the efficiency of natural clay barriers as an expedient economic lining material is assessed. Various chemical constituents of the landfill leachate of an actual waste containment site at Lachenaie (35 km east of Montreal) were determined from samples collected from specially designed basins. Data for companion tests on laboratory columns are also presented. Chemical analysis on samples from the basins and leachates from the columns measured changes in the concentration of: (a) cations (Na, K, Ca, and Mg), (b) anions (Cl, HCO/sub 3/, and CO/sub 3/) (c) total organic carbon (TOC), and (d) heavy metals (Fe, Zn, Pb, and Cu). The physical parameters measured included: (a) pH, and (b) specific conductivity. Predictions, using a dispersion-convection model for concentration profile development for either adsorbed or retained contaminants, were compared with the experimentally determined profiles (both in leaching columns and landfill laboratory model). Another set of experiments was also conducted to evaluate the effect of some organic fluids on the geotechnical properties of different clay soils (natural clay and two reference clay soils: illite and kaolinite). The results from this study have demonstrated that the natural clay soil can be used to adequately contain the different contaminant species usually present in the leachate solutions. Furthermore, the data suggested that under favorable soil conditions, landfill leachates containing low levels of trace metals will not pose a substantial contamination threat to the subsurface environment, provided that a proper thickness of barrier is used.
International Nuclear Information System (INIS)
Rivard, C.; Pelletier, M.; Villieras, F.; Michau, N.
2012-01-01
Document available in extended abstract form only. In the context of the geological disposal of high-level radioactive waste, it is of prime importance to understand the interaction mechanisms between the geological matrix, Callovo-Oxfordian clay rock (COx) and metallic iron, from the package overpack. In order to evidence the individual role of each clay component entering in the mineralogy of the COx, interactions between metallic iron and pure clays (smectites, illite and kaolinite) were first conducted. To investigate the role of the other minerals, the reactivity of COx, COx clay fraction (COxCF) and mixtures between COxCF and quartz, calcite or pyrite, was studied. Clays and additional minerals were put in contact with powder metallic iron with a weight ratio iron:clay fixed at 1:3 and a clay:solution ratio of 1:20. Proportions of non-clay minerals were deduced from the average COx composition: 50% clays, 24.5% quartz, 24.5% calcite and 1% pyrite. Batch experiments were carried out in anoxic conditions at 90 deg. C in the presence of background electrolyte (NaCl 0.02 M.L -1 , CaCl 2 0.04 M.L -1 ) in Parr reactors for durations of one, three or nine months. After reaction, solid and liquid phases were separated by centrifugation and characterized by classical techniques combining chemical analyses (liquid analyses, transmission electron microscopy combined with Energy Dispersive of X-rays spectroscopy TEM-EDS), mineralogical (X-ray diffraction), spectroscopic ( 57 Fe Moessbauer) and morphometric techniques (TEM, scanning electron microscopy and N 2 adsorption). For COx, COxCF and all the pure clay phases, major evolutions were observed during the first month, which shows that the oxidation of metallic iron is rapid in our experimental conditions. Release of iron cations in solution, pH increase (8-10) and Eh decrease (reductive conditions) are responsible for the partial dissolution of initial clay phases. Released iron is involved in the crystallization of Fe
Directory of Open Access Journals (Sweden)
Azadeh Zolfaghari-Baghbaderani
2012-01-01
Full Text Available Objective. To determine the most effective and biodegradable dispersant of spilled oil in water surrounding two Persian Gulf provinces. Methods. This study compared the effects of three dispersants, Pars 1, Pars 2, and Gamlen OD4000 on removal of oil in two Persian Gulf provinces' water. Overall, 16 stations were selected. Using the Well method, the growth rate of isolated bacteria and fungi was identified. To specify the growth rate of microorganisms and their usage of oil in the presence of the above-mentioned dispersants, as exclusive sources of carbon, the bacteria were grown in culture medium for 28 days at 120 rpm, 30∘C, and their optical density was measured by spectrophotometry. Then, we tested biological oxygen demand (BOD and chemical oxygen demand (COD in microorganisms. Results. The highest growth rate was documented for the growth of microorganisms on either Pars 1 or Pars 2 dispersants or their mixtures with oil. However, the culture having microorganisms grown on Pars 1 had higher BOD and COD than the other two dispersants (9200 and 16800 versus 500 and 960, P<0.05. Mixture of oil and Pars 2 as well as oil and Pars 1 dispersants showed the highest BODs and CODs, respectively. In the Bahregan province, microorganisms grown on Pars 2 had maximum amount of BOD and COD in comparison with Pars 1 and Gamlen dispersants (7100 and 15200 versus 6000 and 10560, P<0.05. Conclusion. Pars 1 and Pars 2 were the most effective dispersants with highest degradability comparing Gamlen. In each region, the most suitable compound for removing oil spill from offshores with least secondary contamination should be investigated.
International Nuclear Information System (INIS)
Zolfaghari-Baghbaderani, A.; Bijani, S.; Zolfaghari-Baghbaderani, A.; Bijani, S.; Emtyazjoo, M.; Emtyazjoo, M.; Poursafa, P.; Mehrabian, S.; Farkhani, D.; Mirmoghtadaee, P.
2012-01-01
Objective. To determine the most effective and biodegradable dispersant of spilled oil in water surrounding two Persian Gulf provinces. Methods. This study compared the effects of three dispersants, Pars 1, Pars 2, and Gamlen OD4000 on removal of oil in two Persian Gulf provinces' water. Overall, 16 stations were selected. Using the Well method, the growth rate of isolated bacteria and fungi was identified. To specify the growth rate of microorganisms and their usage of oil in the presence of the above-mentioned dispersants, as exclusive sources of carbon, the bacteria were grown in culture medium for 28 days at 120 rpm, 30 C, and their optical density was measured by spectrophotometry. Then, we tested biological oxygen demand (BOD) and chemical oxygen demand (COD) in microorganisms. Results. The highest growth rate was documented for the growth of microorganisms on either Pars 1 or Pars 2 dispersants or their mixtures with oil. However, the culture having microorganisms grown on Pars 1 had higher BOD and COD than the other two dispersants (9200 and 16800 versus 500 and 960, P<0.05). Mixture of oil and Pars 2 as well as oil and Pars 1 dispersants showed the highest BODs and CODs, respectively. In the Bahregan province, microorganisms grown on Pars 2 had maximum amount of BOD and COD in comparison with Pars 1 and Gamlen dispersants (7100 and 15200 versus 6000 and 10560, P<0.05). Conclusion. Pars 1 and Pars 2 were the most effective dispersants with highest degradability comparing Gamlen. In each region, the most suitable compound for removing oil spill from off shores with least secondary contamination should be investigated.
The effect of clay amendment on substrate properties and growth of woody plants
Directory of Open Access Journals (Sweden)
Tomáš Meisl
2012-01-01
Full Text Available This work deals with the effect of two clay products differing in particle size distribution on properties of growing substrate and on growth of containerized woody plants in substrates amended with these clay products. Fine and coarse clay were added to a peat substrate, each at two rates. The peat substrate without clay was used as a control. The substrates were tested in experiments with two woody ornamentals (Thuja occidentalis ’Smaragd’ and Prunus cistena. Chemical and physical properties of the substrates were measured according to European Standards before planting. Proportion of water categories differing in availability to the plants were calculated from retention curves measured on the sand box. Properties of substrates in containers with and without plants were evaluated in the same way at the end of the culture. Clay addition changed chemical and physical properties of the tested substrates in terms: available nutrients content, particle density, bulk density, total pore volume, easy available water, water buffering capacity, air capacity, and shrinkage. The effect of fine clay was much stronger. In comparison with the clear effect of clay addition on the substrate chemical and physical properties, the effect on the growth and quality of model woody plants was not so explicit.
Moučka, Filip; Svoboda, Martin; Lísal, Martin
2017-06-28
To address the high salinity of flow-back water during hydraulic fracturing, we have studied the equilibrium partitioning of NaCl and water between the bulk phase and clay pores. In shale rocks, such a partitioning can occur between fractures with a bulk-like phase and clay pores. We use an advanced Grand Canonical Monte Carlo (GCMC) technique based on fractional exchanges of dissolved ions and water molecules. We consider a typical shale gas reservoir condition of a temperature of 365 K and pressure of 275 bar, and we represent clay pores by pyrophyllite and Na-montmorillonite slits of a width ranging from about 7 to 28 Å, covering clay pores from dry clay to clay pores with a bulk-like layer in the middle of the pore. We employ the Joung-Cheatham model for ions, SPC/E model for water and CLAYFF for the clay pores. We first determine the chemical potentials for NaCl and water in the bulk phase using Osmotic Ensemble Monte Carlo simulations. The chemical potentials are then used in GCMC to simulate the adsorption of ions and water molecules in the clay pores, and in turn to predict the salt solubility in confined solutions. Besides the thermodynamic properties, we evaluate the structure and in-plane diffusion of the adsorbed fluids, and ion conductivities.
The secondary permeability of Italian clays. A review
International Nuclear Information System (INIS)
Gera, F.
1998-01-01
Over the years several studies have been performed in Italy on the permeability of various argillaceous formations for the purpose of assessing their potential utilization for the isolation of long-lived radioactive waste. An extensive survey was made of tunnels intersecting clay formations for the purpose of identifying water inflows and of interpreting them in relation to the nature of the water-bearing features present outside the lining. The main objective of the 'Faults in Clays' project was to improve the sensitivity and resolution of geophysical techniques for identifying and characterizing faults intersecting clay strata. The first obvious conclusion is that generalizations are not possible: argillaceous formations are characterized by extreme variability in respect to intrinsic properties, sedimentological and structural set-up, consolidation history and regional stress conditions. As a result of this complexity widely different permeability, for both gas and water, has been observed even in apparently similar materials. In addition, gas data indicate that flow, at a particular location, can vary also as a function of time. (R.P.)
Rogers, Liz; Steffan, Dana
2009-01-01
This article describes how to use clay as a potential material for young children to explore. As teachers, the authors find that their dialogue about the potential of clay as a learning medium raises many questions: (1) What makes clay so enticing? (2) Why are teachers noticing different play and conversation around the clay table as compared to…
Effects of clay on resistivity index thin bed: case from Western Niger ...
African Journals Online (AJOL)
Certain clays produce micro-porosities that retain a relatively thick water layer and enhance the path for conductivity of electric currents through capillary forces. Saturation exponent (n) in clay-rich fields is less than the value of 2, usually assumed in well-logging. Accurately determined clay-corrected saturation exponent ...
Primordial clays on Mars formed beneath a steam or supercritical atmosphere.
Cannon, Kevin M; Parman, Stephen W; Mustard, John F
2017-12-06
On Mars, clay minerals are widespread in terrains that date back to the Noachian period (4.1 billion to 3.7 billion years ago). It is thought that the Martian basaltic crust reacted with liquid water during this time to form hydrated clay minerals. Here we propose, however, that a substantial proportion of these clays was formed when Mars' primary crust reacted with a dense steam or supercritical atmosphere of water and carbon dioxide that was outgassed during magma ocean cooling. We present experimental evidence that shows rapid clay formation under conditions that would have been present at the base of such an atmosphere and also deeper in the porous crust. Furthermore, we explore the fate of a primordial clay-rich layer with the help of a parameterized crustal evolution model; we find that the primordial clay is locally disrupted by impacts and buried by impact-ejected material and by erupted volcanic material, but that it survives as a mostly coherent layer at depth, with limited surface exposures. These exposures are similar to those observed in remotely sensed orbital data from Mars. Our results can explain the present distribution of many clays on Mars, and the anomalously low density of the Martian crust in comparison with expectations.
International Nuclear Information System (INIS)
Meneghetti, Paulo; Qutubuddin, Syed; Webber, Andrew
2004-01-01
Polymer nanocomposite gel electrolytes consisting of high molecular weight poly(methyl methacrylate) PMMA-clay nanocomposite, ethylene carbonate (EC)/propylene carbonate (PC) as plasticizer, and LiClO 4 electrolyte are reported. Montmorillonite clay was ion exchanged with a zwitterionic surfactant (octadecyl dimethyl betaine) and dispersed in methyl methacrylate, which was then polymerized to synthesize PMMA-clay nanocomposites. The nanocomposite was dissolved in a mixture of EC/PC with LiClO 4 , heated and pressed to obtain polymer gel electrolyte. X-ray diffraction (XRD) of the gels indicated intercalated clay structure with d-spacings of 2.85 and 1.40 nm. In the gel containing plasticizer, the clay galleries shrink suggesting intercalation rather than partial exfoliation observed in the PMMA-clay nanocomposite. Ionic conductivity varied slightly and exhibited a maximum value of 8 x 10 -4 S/cm at clay content of 1.5 wt.%. The activation energy was determined by modeling the conductivity with a Vogel-Tamman-Fulcher expression. The clay layers are primarily trapped inside the polymer matrix. Consequently, the polymer does not interact significantly with LiClO 4 electrolyte as shown by FTIR. The presence of the clay increased the glass transition temperature (Tg) of the gel as determined by differential scanning calorimetry. The PMMA nanocomposite gel electrolyte shows a stable lithium interfacial resistance over time, which is a key factor for use in electrochemical applications
Hydration of swelling clay and bacteria interaction. An experimental in situ reaction study
International Nuclear Information System (INIS)
Berger, J.
2008-01-01
This study reports on the physical-chemical behaviour of swelling di-octahedral clays (smectites) and their interaction with aqueous solutions and bacteria (Shewanella putrefaciens). Experimental results are presented for compacted clays, hydrated under confined volume conditions, using a new type of reaction-cell (the 'wet-cell' of Warr and Hoffman, 2004) that was designed for in situ X-ray diffraction (XRD) measurement. For comparison, dispersed clay systems were studied using standard batch solutions subjected to varying degrees of agitation. The combination of time-dependent in situ XRD measurements with gravimetric measurements and calculated diffraction patterns using the CALCMIX software (Plancon and Drits, 1999) allowed to successful quantification of the dynamics of water uptake and storage. This analytical procedure combined with published water vapour adsorption data enabled determination of the abundance of structured water layers, developed in the interlayer space, and the amount of water contained in different storage sites (interlayers, surfaces and pore spaces). Qualitative information on surface area and textural organization was also estimated based on calculated changes in the average particle thickness and the organization of water layer structures (ordering). Abiotic smectite hydration experiments, using a range of natural and industrial bentonites (SWy-2, IBECO, MX80, TIXOTON), focused on defining the role of the interlayer cation, variable clay packing densities and the ionic strength of the infiltrating solution. The rate of smectite hydration, as expected, was seen to be highly dependent on the type of interlayer cation (enhanced for Ca as opposed to Na) and the ionic strength of solution (enhanced uptake rates with saline solutions, particularly as they infiltrate Na-smectite). A range of dynamic changes in micro textural state occurred as a function of packing density. These changes explain the differences in hydration behaviour observed
Assessment of clay stiffness and strength parameters using index properties
Directory of Open Access Journals (Sweden)
Sayed M. Ahmed
2018-06-01
Full Text Available A new approach is developed to determine the shear wave velocity in saturated soft to firm clays using measurements of the liquid limit, plastic limit, and natural water content with depth. The shear wave velocity is assessed using the site-specific variation of the natural water content with the effective mean stress. Subsequently, an iterative process is envisaged to obtain the clay stiffness and strength parameters. The at-rest earth pressure coefficient, as well as bearing capacity factor and rigidity index related to the cone penetration test, is also acquired from the analyses. Comparisons are presented between the measured clay parameters and the results of corresponding analyses in five different case studies. It is demonstrated that the presented approach can provide acceptable estimates of saturated clay stiffness and strength parameters. One of the main privileges of the presented methodology is the site-specific procedure developed based on the relationships between clay strength and stiffness parameters, rather than adopting direct correlations. Despite of the utilized iterative processes, the presented approach can be easily implemented using a simple spreadsheet, benefiting both geotechnical researchers and practitioners. Keywords: Soft to firm clays, Atterberg limits, Shear wave velocity, Small-strain shear modulus, Constrained modulus, Undrained shear strength, Effective friction angle, Cone penetration test
Clay minerals in sandstone uranium deposits: radwaste applications
International Nuclear Information System (INIS)
Brookins, D.G.
1990-01-01
Clay minerals play an important role in the genesis of uranium deposits in sandstones. They incorporate the rate earths (REE), U, Sb, Th, Cs, Rb, Sr, Y, Ba, and even small amounts of chalcophiles. These minerals possess analog elements for many of the radwaste fission products as well as actinides and some actinide daughters. In sandstone uranium deposits, clay minerals are also associated with sulfide minerals, usually pyrite, and organic carbonaceous matter. The primary clay minerals are usually smectites, illites, chlorites and mixed layer varieties. The integrity of these clay minerals is demonstrated by their retention of formational-mineralization ages determined by Rb-Sr geochronologic investigation of the Grants Mineral Belt of the United States. The importance of the clay minerals as analog for parts of the multi-barrier concept in radwaste disposal is their ability to impede water penetration into - and movement of key elements out of uranium rich zones. The clay minerals further sorb and in other ways incorporate into their structures many fission products and actinide analogs from man-made nuclear wastes. 22 refs., 1 fig., 3 tabs
Acidity of clay edges from ab-initio simulations
International Nuclear Information System (INIS)
Tazi, Sami; Salanne, Mathieu; Rotenberg, Benjamin; Turq, Pierre; Sprik, Michiel; Sulpizi, Marialore
2012-01-01
Document available in extended abstract form only. One of the most important factor to understand and predict the sorption of cations on clay surfaces is the protonation state of the surface sites, which is difficult to determine experimentally. Indeed, titration provides a global measure only; it does not probe the status of different silanol (Si-OH) and aluminol sites (Al-OH and Al-OH 2 ) present along the edges of clay sheets in the presence of water. A novel method has been recently designed to quantify the acidity of chemical species. This method allows to estimate pKa values from First Principles Molecular Dynamics by thermodynamic integration. We have applied it to the case of pyrophyllite clay edge sites. These calculations will allow us to subsequently perform classical Molecular Dynamic simulations with realistic surface structures (protonated/deprotonated sites) for natural clays in the presence of water. After presenting the method, we show its application to the (010) edge of pyrophyllite. We find that the most acidic group is Si-OH while the least acidic one is Al-OH, which never deprotonates in water because of its high pKa value (22.1). We further provide a microscopic understanding of the solvation structure and reactivity of the edges of neutral clays. In particular we address the tendency to deprotonation of the different reactive groups on the (010) face of pyrophyllite, showing the important role of solvation and its rearrangements after deprotonation. Finally, we compare our results to the one predicted by the empiric method MUSIC and the estimate from deprotonation energies in the vacuum, confirming the important role of solvation in both the protonated and deprotonated states. (authors)
Virta, R.L.
2001-01-01
Part of the 2000 annual review of the industrial minerals sector. A general overview of the ball clay industry is provided. In 2000, sales of ball clay reached record levels, with sanitary ware and tile applications accounting for the largest sales. Ball clay production, consumption, prices, foreign trade, and industry news are summarized. The outlook for the ball clay industry is also outlined.
Ventilation test at Mont Terri. Geoelectric monitoring of the opalinus clay desaturation. Phase 2
International Nuclear Information System (INIS)
Wieczorek, Klaus; Zhang, Chun-Liang; Rothfuchs, Tilmann
2008-04-01
Between December 2001 and May 2004, a ventilation experiment (VE) was performed in the Mont Terri Underground Research Laboratory (URL) and co-financed by the Commission of the European Communities. The objective was to investigate the desaturation of consolidated clay formations in consequence of the ventilation of underground openings of a repository in such a formation. The results of the geoelectric measurements performed in the second phase of the Mont Terri ventilation test can be summarized as follows: Geoelectric tomography has been found suitable for monitoring ventilation-induced saturation changes in the Opalinus clay. During ventilation with dry air a desaturation down to below 50% could be detected in both desaturation cycles. The desaturated zone extends less than 0.5 m into the rock around the microtunnel. During the second resaturation phase, ventilation with humid air led to quick resaturation at the tunnel surface, while resaturation of the rock mass took months. The still ongoing third resaturation phase seems to imply that resaturation of the rock mass may take years with no air circulation in the tunnel. The laboratory investigations on the Opalinus clay included the determination of water retention capacity, swelling pressure, free swelling/shrinking strains induced by moisture changes, and response of normal and large hollow clay samples to the ventilation of the central boreholes at different air humidity values. The Opalinus clay has a high water absorption capacity. The amount of water uptake in unconstraint conditions is much higher than the water content in the naturally confined state, indicating that the pore water in the natural clay rock is predominantly bound on clay minerals. The swelling pressure induced by wetting with vapour is very close to the major lithostatic stress at the sampling location. Water uptake from vapour causes a large free expansion of up to 12% over 8 months and even a breakdown along bedding planes. Release of
Torsional, tensile and structural properties of acrylonitrile–butadiene–styrene clay nanocomposites
International Nuclear Information System (INIS)
Singh, Priyanka; Ghosh, Anup K.
2014-01-01
Highlights: • Torsional behaviour of ABS and its nanocomposites is established. • Rheology is used as a tool to investigate the structure development of ABS nanocomposites. • Effect of nanoclay on resilience, toughness and ductility of ABS nanoclay is quantified. • ABS clay nanocomposites is correlated with rheological, mechanical and torsional behaviour. - Abstract: Torsional and tensile behaviour of acrylonitrile–butadiene–styrene (ABS)-clay nano-composites have been investigated and correlated with morphological and rheological characterisations. Nano-composites of ABS are prepared by melt compounding with different loading levels of nanoclay (Cloisite 30B) in a twin screw extruder and have been characterised in terms of torsional, axial and impact behaviour for their application in external orthotic devices. Tensile stress strain curve of nanocomposites are investigated to quantify resilience, toughness and ductility. Torque values of the nanocomposites are observed under torsion (10°–90°) and compared with that of neat ABS. Performance of ABS under torsional load improved by addition of nanoclay. Both modulus of elasticity and rigidity are found to improve in presence of nanoclay. State of dispersion in nano-composites is investigated using conventional methods such as transmission electron microscopy (TEM), X-ray diffraction (XRD), as well as by parallel plate rheometry. Addition of clay exhibits shear thinning effect and results in increase in storage modulus as well as complex viscosity of the nanocomposites. Zero shear viscosity rises tenfold with 1–2% addition of nanoclay, indicating the formation of structural network. It is found that state of dispersion of nanoclay governs the torsional and mechanical properties in ABS-clay nanocomposites
Influence of clay mineralogy on clay based ceramic products
International Nuclear Information System (INIS)
Radzali Othman; Tuan Besar Tuan Sarif; Zainal Arifin Ahmad; Ahmad Fauzi Mohd Noor; Abu Bakar Aramjat
1996-01-01
Clay-based ceramic products can either be produced directly from a suitable clay source without the need further addition or such products can be produced from a ceramic body formulated by additions of other raw materials such as feldspar and silica sand. In either case, the mineralogical make-up of the clay component plays a dominating role in the fabrication and properties of the ceramic product. This study was sparked off by a peculiar result observed in one of five local ball clay samples that were used to reformulate a ceramic body. Initial characterisation tests conducted on the clays indicated that these clays can be classified as kaolinitic. However, one of these clays produced a ceramic body that is distinctively different in terms of whiteness, smoothness and density as compared to the other four clays. Careful re-examination of other characterisation data, such as particle size distribution and chemical analysis, failed to offer any plausible explanation. Consequently, the mineralogical analysis by x-ray diffraction was repeated by paying meticulous attention to specimen preparation. Diffraction data for the clay with anomalous behaviour indicated the presence of a ∼ 10A peak that diminished when the same specimen was re-tested after heating in an oven at 12O degree C whilst the other four clays only exhibit the characteristic kaolinite (Al sub 2 O sub 3. 2SiO sub 2. 2H sub 2 0) and muscovite peaks at ∼ 7A and ∼ 10A before and after heat treatment. This suggests the presence of the mineral halloysite (A1 sub 2 0 sub 3. 2SiO sub 2.4H sub 2 0) in that particular clay. This difference in mineralogy can be attributed to account for the variations in physical properties of the final product. Consequently, this paper reviews in general the precautionary measures that must be adhered to during any mineralogical investigation of clay minerals or clay-based materials. The common pitfalls during specimen preparation, machine settings and interpretation of
A Classification of Clay-Rich Subaqueous Density Flow Structures
Hermidas, N.; Eggenhuisen, Joris T.; Jacinto, Ricardo Silva; Luthi, S.M.; Toth, Ferenc; Pohl, Florian
2018-01-01
This study presents a classification for subaqueous clay-laden sediment gravity flows. A series of laboratory flume experiments were performed using 9%, 15%, and 21% sediment mixture concentrations composed of sand, silt, clay, and tap water, on varying bed slopes of 6°, 8°, and 9.5°, and with
International Nuclear Information System (INIS)
Blanchart, Pascale; Faure, Pierre; Michels, Raymond; Bruggeman, Christophe; De Craen, Mieke; Parant, Stephane
2012-01-01
Document available in extended abstract form only. The Boom Clay is considered by the Belgian radioactive waste management agency Ondraf/Niras as a possible host rock for the geological disposal of high-level and long-lived radioactive waste. The drilling of galleries and corings in the Boom Clay (Mol, Belgium) leads to perturbations of the initial physical and chemical conditions. In piezometers, the DOC may show considerable and irregular variations through time, with values ranging from 80 to 425 mg/L. The origin and bio-physico-chemical controls of such variations are yet unknown but oxidation and biodegradation were considered as most likely. Three categories of samples were collected with the aim of determining and quantifying different molecular markers representative for the oxidation process: - Fresh as well as air-oxidized Boom Clay samples were collected in the Underground Research Facility HADES of EURIDICE (Mol, Belgium): they represent a natural series of oxidation; - A fresh Boom Clay sample was submitted to laboratory air oxidation (artificial series). In these experiments, powdered clay was heated at 80 deg. C under air flow during 1, 3, 6, 9, 12, 18 months; - Four water samples were collected during January 2010 from different horizons in the Boom Clay by means of piezometers located in the Underground Research Facility. The DOM (dissolved organic matter) of Boom Clay samples (artificial and natural series) was isolated by Soxhlet using pure water as well as by leaching experiments. The quantitative analysis shows an increasing in DOC (Dissolved Organic Carbon) content with oxidation. Qualitative characterizations including spectroscopic (3D-fluorescence) as well as molecular analyses (flash pyrolysis - gas chromatography - mass spectrometry (PyGC-MS) and size exclusion chromatography (SEC-HPLC)) show an evolution of the DOM chemistry with oxidation: - An enrichment in oxygen bearing molecules (acidic poly functional groups); - A decrease in
Study of adsorption of zinc in clay smectite type Bofe in system of finite bath
International Nuclear Information System (INIS)
Souza, R.S.; Mota, J.D.; Lima, W.S.; Rodrigues, M.G.F.
2012-01-01
Clays are demonstrably excellent adsorbents, both for their physical and chemical characteristics and the wide coverage and low cost. Among the various groups of clay minerals, the smectite are noted for having large surface areas. The initial objective of this study was to characterize the clay Bofe through the techniques of X-Ray Diffraction (XRD), X-Ray Spectrometry by Energy Dispersive (EDX) and nitrogen adsorption (BET). To evaluate the adsorption of metal ions zinc (synthetic sewage), we used a system in finite bath, following a factorial design 2 2 , taking as input variables: pH and initial concentrations of zinc (Zn2 +) and output variables: percentage removal and removal capacity. The characterization results showed that Bofe clay belongs to the family of smectite and therefore has great potential for adsorption. (author)
Directory of Open Access Journals (Sweden)
Hu Xueting
2016-01-01
Full Text Available Highly water-dispersible and very small TiO2 nanoparticles (~3 nm anatase with large specific surface area have been synthesized by hydrolysis and hydrothermal reactions of titanium butoxide and used for the removal of three azo dyes (Congo red, orange II, and methyl orange with different molecular structure from simulated wastewaters. The synthesized TiO2 nanoparticles are well dispersed in water with large specific surface area up to 417 m2 g−1. Adsorption experiments demonstrated that the water-dispersible TiO2 nanoparticles possess excellent adsorption capacities for Congo red, orange II, and methyl orange, which could be attributed to their good water-dispersibility and large specific surface area.
Characterization of clay minerals; Caracterizacion de minerales arcillosos
Energy Technology Data Exchange (ETDEWEB)
Diaz N, C.; Olguin, M.T.; Solache R, M.; Alarcon H, T.; Aguilar E, A. [Gerencia de Ciencias Basicas, Direccion de Investigacion Cientifica, Instituto Nacional de Investigaciones Nucleares, A.P. 18-1027, 11801 Mexico D.F. (Mexico)
2002-07-01
The natural clays are the more abundant minerals on the crust. They are used for making diverse industrial products. Due to the adsorption and ion exchange properties of these, a great interest for developing research directed toward the use of natural clays for the waste water treatment has been aroused. As part of such researches it is very important to carry out previously the characterization of the interest materials. In this work the results of the mineral and elemental chemical composition are presented as well as the morphological characteristics of clay minerals from different regions of the Mexican Republic. (Author)
Influence of clay content on wave-induced liquefaction
DEFF Research Database (Denmark)
Kirca, V.S. Ozgur; Sumer, B. Mutlu; Fredsøe, Jørgen
2014-01-01
of measurements were carried out: (1) pore-water pressure measurements across the soil depth and (2) water-surface elevation measurements. These measurements were synchronized with video recordings of the liquefaction process from the side. The ranges of the various quantities in the experiments were wave height...... of silt and clay was not liquefied. Sand may become prone to liquefaction with the introduction of clay, contrary to the general perception that this type of sediment is normally liquefaction-resistant under waves. For instance, sand with d50 50:4 mmwas liquefied with CC510:8%, whereas sand with d50 50...
Isotopic exchange of 65Zn with stable Zn adsorbed on reference clay minerals
International Nuclear Information System (INIS)
Bourg, A.C.M.; Filby, R.H.
1976-01-01
For reference clays of low organic content, Zn adsorbed on the clay minerals is in kinetic equilibrium with 65 Zn in solution. Thus the specific activity approach applied to the transport of 65 Zn(II) at the water-reference clay interface is intrinsically valid. (author)
Probing surface charge potentials of clay basal planes and edges by direct force measurements.
Zhao, Hongying; Bhattacharjee, Subir; Chow, Ross; Wallace, Dean; Masliyah, Jacob H; Xu, Zhenghe
2008-11-18
The dispersion and gelation of clay suspensions have major impact on a number of industries, such as ceramic and composite materials processing, paper making, cement production, and consumer product formulation. To fundamentally understand controlling mechanisms of clay dispersion and gelation, it is necessary to study anisotropic surface charge properties and colloidal interactions of clay particles. In this study, a colloidal probe technique was employed to study the interaction forces between a silica probe and clay basal plane/edge surfaces. A muscovite mica was used as a representative of 2:1 phyllosilicate clay minerals. The muscovite basal plane was prepared by cleavage, while the edge surface was obtained by a microtome cutting technique. Direct force measurements demonstrated the anisotropic surface charge properties of the basal plane and edge surface. For the basal plane, the long-range forces were monotonically repulsive within pH 6-10 and the measured forces were pH-independent, thereby confirming that clay basal planes have permanent surface charge from isomorphic substitution of lattice elements. The measured interaction forces were fitted well with the classical DLVO theory. The surface potentials of muscovite basal plane derived from the measured force profiles were in good agreement with those reported in the literature. In the case of edge surfaces, the measured forces were monotonically repulsive at pH 10, decreasing with pH, and changed to be attractive at pH 5.6, strongly suggesting that the charge on the clay edge surfaces is pH-dependent. The measured force profiles could not be reasonably fitted with the classical DLVO theory, even with very small surface potential values, unless the surface roughness was considered. The surface element integration (SEI) method was used to calculate the DLVO forces to account for the surface roughness. The surface potentials of the muscovite edges were derived by fitting the measured force profiles with the
Directory of Open Access Journals (Sweden)
Mohie Eldin Elmashad
2016-08-01
Full Text Available This paper presents the results of an experimental investigation performed to quantify the effect of mixing clayey soils with saltwater on consistency and swelling characteristics of clays. Massive natural clay deposits and compacted clay backfills either exist or are used in certain important and sensitive applications such as dams, liners, barriers and buffers in waste disposal facilities. In many cases, the clay deposits in these applications are subjected to saltwater. However, in standard laboratory classification tests, distilled or potable water are usually used in mixing test samples. This may lead to faulty interpretation of the actual in-situ consistency and volume change behaviors. In this research, an attempt is made to quantify the changes in consistency and swelling of clay soils from various locations around the Nile valley and possessing a wide range of consistency, when mixed with natural seawater with different salt concentrations. The results showed that the increase of the salt concentration of the mixing water may result in major decrease in the liquid limit and swelling characteristics of high plasticity montmorillonite clays. The reduction in the swelling of the clay soils is also proportional to the rate of saltwater infiltration. In an attempt to correlate the swelling of clays to the rate of water infiltration, a new simplified laboratory apparatus is proposed where swelling and infiltration are measured in one simple test “the swelling infiltrometer”.
Energy Technology Data Exchange (ETDEWEB)
Amorim, Luciana V.; Pereira, Melquesedek S.; Ferreira, Heber C. [Universidade Federal de Campina Grande (UFCG), PB (Brazil)
2008-07-01
The aim of this work is to provide continuity for UFCG studies presenting results of rheological, filtration and the lubricity behaviors obtained with fluids prepared with bentonite clays from Paraiba, in binary compositions, after treatment with lubricants agents. It was selected two samples of bentonite clays and four lubricants (Lub 1, Lub 2, Lub 3 and Lub 4). The results showed that: depending on the composition, the drilling fluids presented bingham and pseudo plastic rheological behaviors, and with the additives bingham behavior; among the rheological and filtration properties evaluated, the apparent viscosity, yield limiting and the water loss are the have changes with the addition of lubricants; the values of the lubricity coefficient (LC) of fluids without additives were next of 0.50, independent of the composition of the bentonite clay mixture; after addition of the lubricants, the LC of fluids reduced for values next to 0,11, independent of its concentration and lubricants the best-performing are the Lub 2 and Lub 4. (author)
Universal sol state behavior and gelation kinetics in mixed clay dispersions.
Pujala, Ravi Kumar; Pawar, Nisha; Bohidar, H B
2011-05-03
Sol and gel state behavior, in aqueous salt free dispersions, of clays Laponite (L) and Na montmorillonite (MMT) was studied at various mixing ratios (L:MMT = r = 1:0.5, 1:1, and 1:2). In the sol state, the zeta potential and gelation concentration of L-MMT obeyed the universal relation, X(L-MMT) = (rX(L) + X(MMT))/(1 + r), where X is zeta potential or gelation concentration (c(g)), implying that these properties are linear combinations of the same of their individual components. The low frequency storage modulus (G(0)'), relative viscosity (η(r)), and apparent cluster size (R) could be universally described by the power-law, G(0)' ∼ ((c/c(g)) - 1)(t) (c > c(g)), and η(r), R ∼ (1 - (c/c(g)))(-k,ν) (c < c(g)), with t = 1.5, k = 1.1, and υ = 0.8 close to the gelation concentration, for r = 1:1 cogel, consistent with the percolation model description of gelation. Interestingly, the hyperscaling relation δ = t/(k + t) yielded δ = 0.56 not too different from the predicted value ∼0.7, while the experimental value of δ obtained from G''(ω) ∼ ω(δ) close to c ≈ c(g) yielded δ = 1.5, which was at variance with the hyperscaling result. The experimental data, on hand, mostly supported percolation type gelation mechanism. As the cogels were slowly heated, at a characteristic temperature, T(g), a sharp increase in G' value was noticed, implying a transition to gel hardening (a new phase state). The temperature-dependent behavior followed the power-law description, G' ∼ (T(g) - T)(-γ) (T < T(g)), with γ = 0.40 ± 0.05 invariant of composition of the cogel, whereas for MMT and Laponite, γ = 0.25 and 0.55, respectively. It has been shown that the cogel has significantly enhanced mechanical (G(0) increased by 10 times for r = 1:1 cogel) and thermal properties (T(g) increased by 13 °C for 1:1 cogel) that can be exploited to design customized soft materials.
Evaluation of treated black liquor used as dispersant of concentrated coal-water slurry
Energy Technology Data Exchange (ETDEWEB)
Mingsong Zhou; Qian Kong; Bing Pan; Xueqing Qiu; Dongjie Yang; Hongming Lou [South China University of Technology, Guangzhou (China). State Key Laboratory of Pulp and Paper Engineering
2010-03-15
The paper making waste liquor is a great water pollution source and much work has been done over the years to overcome this challenge. We present here a solution of black liquor used as dispersant of coal-water slurry (abbreviated as CWS) following chemical treatment. The treated black liquor (abbreviated as TBL) is used to prepare CWS for three bituminous coals, and the factors influencing its dispersing ability and the properties of CWS are investigated. The results show that the increasing sulfonating agent and formaldehyde dosage increase the sulfonic group content while reducing the molecular weight of TBL. The comparison with a naphthalene dispersant shows that TBL has a similar or better dispersing ability, and the large quantity of sulfonic groups engrafted in lignin molecules and the markedly increase of molecular weight are considered the key reason for the excellent performance of TBL. Moreover, the change of the molecular configuration from globular to flocculent in solution observed by TEM is also considered as an important reason for the excellent dispersing effect of TBL for CWS. 25 refs., 6 figs., 7 tabs.
International Nuclear Information System (INIS)
Klinkenberg, M.; Dohrmann, R.; Kaufhold, S.; Siegesmund, S.
2010-01-01
Document available in extended abstract form only. The potential use of clay stones as host rock for radioactive waste disposal is currently investigated. For this application, hydraulic conductivity, swelling properties, water uptake, rheological and mechanical properties are of great importance. The Opalinus Clay (Mont-Terri, Switzerland) and the Callovo- Oxfordian clay stone (France) are the most frequently studied clay stones. One goal is to develop a numerical model being able to predict the mechanical behaviour of clay stones under repository-like conditions. Experimental investigations reveal that Opalinus Clay and Callovo-Oxfordian clay stone behave different with respect to the dependence of mechanical strength on the carbonate content. The failure strength of Opalinus Clay decreases with increasing carbonate content, whereas it increases with increasing carbonate content when Callovo-Oxfordian clay stone is considered. To supply proper data and enable reliable model assumptions, the use of suitable experimental techniques for the description of the microstructure is indispensable. After mechanical testing, samples were taken perpendicular to the bedding and polished sections were prepared. The micro-fabrics were investigated using scanning electron microscopy (SEM) and image analysis. Backscattered electron (BSE) images were used for the image analysis because carbonates can be extracted by grey level analysis. The image analysis of the extracted particles provides the following parameters: area, longest and shortest axis of an ellipse (surrounding the particle), perimeter, the angle to horizontal (longest axis), and the aspect ratio (longest axis/shortest axis). Callovo-Oxfordian clay stone shows a homogenous distribution of fine-grained carbonates and dovetail connection of calcium carbonate with the clayey matrix. In contrast Opalinus Clay shows large elongated carbonate grains (high aspect ratios) of shell fragments. Cracks are mostly related to these
Study of methods for electrical modification of a clay suspension
Energy Technology Data Exchange (ETDEWEB)
Karimov, R A; Kudaktina, T T; Parpiyev, T R
1982-01-01
As a result of the conducted experiments it was established that the viscosity and maximum static shear stress of the drilling muds prepared on electrically treated water increases 2-3-fold as compared to the muds prepared on standard water. This is explained by the fact that the unipolar treatment results in deep change in the water structure. Under the influence of the electrical current, there is activation, rise in the electrical conductivity, decrease in surface tension, considerable rise in the pH value, etc. The output of clay mud increases 1.5-fold in the clay suspension that is prepared on electrically treated water.
Characteristics of waterflooding of oil pools with clay-containing reservoir rocks
Energy Technology Data Exchange (ETDEWEB)
Zheltov, Yu V; Stupochenko, V E; Khavkin, A Ya; Martos, V N
1981-01-01
When planning the development of oil fields with reservoir pressure maintenance by the injection of water or activated solutions (surfactants, alkali, etc.), it is necessary to take into account the consequences of phenomena related to clay swelling. For this purpose, it is necessary to measure on a core the parameters characterizing the change and hysteresis of the filtration and storage properties of the reservoir rocks. Swelling of the clay component of the rock along with reducing these properties in the sweep zone can promote an increase of the efficiency of displacing oil by water. Theoretical investigations showed that the maximum displacement efficiency in homogeneous clay-containing rocks does not depend on the time of starting stimulation by demineralized waters. The efficiency from changing the mineralization of the stimulating agent increases with increase of viscosity of the oil. Under certain physical and geologic conditions, a purposeful change of the filtration and storage properties by increasing or decreasing clay swelling can increase the efficiency of developing the field and can increase oil recovery.
Tansel, Berrin; Lee, Mengshan; Berbakov, Jillian; Tansel, Derya Z.; Koklonis, Urpiana
2014-04-01
Effectiveness of Corexit 9500A for dispersing Louisiana crude oil was evaluated in salt water solutions containing natural materials in relation to salinity and dispersant-to-oil ratio (DOR). Experimental results showed that both salinity and DOR had significant effects on dispersion of Louisiana crude oil in the presence of different natural materials. The natural materials added to the salt water solutions included sea sand (South Beach, Miami, Florida), red mangrove leaves (Rhizophora mangle), seaweed (Sargassum natans), and sea grass (Halodule wrightii). Dispersant effectiveness (amount of oil dispersed into the water) was reduced significantly with increasing salinity with the minimum effectiveness observed in the salinity range between 30 and 50 ppt in all aqueous samples containing natural materials. When significant amounts of floating oil were present, the partially submerged natural materials enhanced the transfer of oil into the water column, which improved the dispersion effectiveness. However, dispersant effectiveness was significantly reduced when the amount of floating oil was relatively small and could not be released back to the water column. Surface tension may not be an adequate parameter for monitoring the effectiveness of dispersants in salt water environment. When distilled water was used (i.e., zero salinity), surface tension was significantly reduced with increasing dispersant concentration. However, there was no clear trend in the surface tension of the salt water solutions (17-51 ppt) containing crude oil and natural materials with increasing dispersant concentration.
Mud peeling and horizontal crack formation in drying clays
Style, Robert W.
2011-03-01
Mud peeling is a common phenomenon whereby horizontal cracks propagate parallel to the surface of a drying clay. Differential stresses then cause the layer of clay above the crack to curl up to form a mud peel. By treating the clay as a poroelastic solid, we analyze the peeling phenomenon and show that it is caused by the gradient in tensile stress at the surface of the clay, analogously to the spalling of thermoelastic materials. For a constant water evaporation rate at the clay surface we derive equations for the depth of peeling and the time of peeling as functions of the evaporation rate. Our model predicts a simple relationship between the radius of curvature of a mud peel and the depth of peeling. The model predictions are in agreement with the available experimental data. Copyright 2011 by the American Geophysical Union.
Production of polyol carbonates and their intercalation into Smectite clays
Shaheen, Uzma
2017-01-01
In hyper-saline conditions, clays in geosynthetic clay liners contract and fail to form a hydraulic barrier due to removal of water from the interlayer spaces of smectite, which is the swelling mineral component of bentonites used in geosynthetic clay liners. Five-membered cyclic carbonates such as propylene carbonate have been reported to form stable intercalated complexes with hydrated Na-smectite, which maintain swollen states at 1M). Glycerol carbonate was selected as an alternative c...
Energy dispersion X-ray fluorescence techniques in water pollution analysis
International Nuclear Information System (INIS)
Holynska, B.
1980-01-01
Advantages and limitations of energy dispersion X-ray fluorescence methods for analysis of pollutants in water are discussed. The necessary equipment for X-ray measurement of insoluble and dissolved trace metals in water is described. Different techniques of enrichment of trace metals are presented: ion exchange on selective Chelex-100 exchanger, precipitation with chelating agents DDTC and APDC, and adsorption on activated carbon. Some results obtained using different preconcentration methods for trace metals determination in different waters are presented. (author)
Fine-grained sediment dispersal along the California coast
Warrick, Jonathan A.; Storlazzi, Curt D.
2013-01-01
Fine-grained sediment (silt and clay) enters coastal waters from rivers, eroding coastal bluffs, resuspension of seabed sediment, and human activities such as dredging and beach nourishment. The amount of sediment in coastal waters is an important factor in ocean ecosystem health, but little information exists on both the natural and human-driven magnitudes of fine-grained sediment delivery to the coastal zone, its residence time there, and its transport out of the system—information upon which to base environmental assessments. To help fill these information gaps, the U.S. Geological Survey has partnered with Federal, State, and local agencies to monitor fine-grained sediment dispersal patterns and fate in the coastal regions of California. Results of these studies suggest that the waves and currents of many of the nearshore coastal settings of California are adequately energetic to transport fine-grained sediment quickly through coastal systems. These findings will help with the management and regulation of fine-grained sediment along the U.S. west coast.
Solid state synthesis of water-dispersible silicon nanoparticles from silica nanoparticles
International Nuclear Information System (INIS)
Kravitz, Keren; Kamyshny, Alexander; Gedanken, Aharon; Magdassi, Shlomo
2010-01-01
A solid state synthesis for obtaining nanocrystalline silicon was performed by high temperature reduction of commercial amorphous nanosilica with magnesium powder. The obtained silicon powder contains crystalline silicon phase with lattice spacings characteristic of diamond cubic structure (according to high resolution TEM), and an amorphous phase. In 29 Si CP MAS NMR a broad multicomponent peak corresponding to silicon is located at -61.28 to -69.45 ppm, i.e. between the peaks characteristic of amorphous and crystalline Si. The powder has displayed red luminescence while excited under UV illumination, due to quantum confinement within the nanocrystals. The silicon nanopowder was successfully dispersed in water containing poly(vinyl alcohol) as a stabilizing agent. The obtained dispersion was also characterized by red photoluminescence with a band maximum at 710 nm, thus enabling future functional coating applications. - Graphical abstract: High temperature reduction of amorphous nanosilica with magnesium powder results in the formation of powder containing crystalline silicon phase The powder displays red luminescence while excited under UV illumination, due to quantum confinement within the Si nanocrystals, and can be successfully dispersed in water containing poly(vinyl alcohol) as a stabilizing agent. The obtained dispersion was also characterized by red photoluminescence, thus enabling future functional coating applications.
Magnetic chitosan/clay beads: A magsorbent for the removal of cationic dye from water
Energy Technology Data Exchange (ETDEWEB)
Bée, Agnès, E-mail: agnes.bee@upmc.fr [Sorbonne Universités, UPMC Univ Paris 06, CNRS, Laboratoire PHENIX, F-75005 Paris (France); Obeid, Layaly, E-mail: lghannoum@hotmail.fr [Sorbonne Universités, UPMC Univ Paris 06, CNRS, Laboratoire PHENIX, F-75005 Paris (France); CertiNergy Solutions, 33 avenue du Maine, BP 195, 75755 Paris Cedex 15 (France); Mbolantenaina, Rakotomalala, E-mail: mbolantenaina@yahoo.fr [Sorbonne Universités, UPMC Univ Paris 06, CNRS, Laboratoire PHENIX, F-75005 Paris (France); Welschbillig, Mathias, E-mail: welschbillig@certinergysolutions.com [CertiNergy Solutions, 33 avenue du Maine, BP 195, 75755 Paris Cedex 15 (France); Talbot, Delphine, E-mail: delphine.talbot@upmc.fr [Sorbonne Universités, UPMC Univ Paris 06, CNRS, Laboratoire PHENIX, F-75005 Paris (France)
2017-01-01
A magnetic composite material composed of magnetic nanoparticles and clay encapsulated in cross-linked chitosan beads was prepared, characterized and used as a magsorbent for the removal of a cationic dye, methylene blue (MB), from aqueous solutions. The magnetic properties of these beads represent an advantage to recover them at the end of the depollution process. The optimal weight ratio R=clay:chitosan for the removal of MB in a large range of pH was determined. For beads without clay, the maximal adsorption capacity of MB occurs in the pH range [9–12], while for beads with clay, the pH range extends by increasing the amount of clay to reach [3–12] for R>0.5. Adsorption isotherms show that the adsorption capacity of magnetic beads is equal to 82 mg/g. Moreover, the kinetics of dye adsorption is relatively fast since 50% of the dye is removed in the first 13 min for an initial MB concentration equal to 100 mg/L. The estimation of the number of adsorption sites at a given pH shows that the main driving force for adsorption of MB in a large range of pH is the electrostatic interaction between the positively charged dye and the permanent negative charges of clay. - Highlights: • A magsorbent based on magnetic nanoparticles and clay encapsulated in chitosan beads was prepared and characterized. • Clay played significant role for the removal of a cationic dye. • The magnetic beads exhibit a maximum adsorption capacity of 82 mg/g for methylene blue. • The pH range of the maximum adsorption extends from [9–12] to [3–12] by increasing the amount of clay. • The magsorbent could be magnetically removed from solution.
Effect of Subsurface Irrigation with Porous Clay Capsules on Quantitative and Quality of Grape Plant
Directory of Open Access Journals (Sweden)
H. Ghorbani Vaghei
2016-02-01
Full Text Available Introduction: Maintaining soil moisture content at about field capacity and reducing water loss in near root zone plays a key role for developing soil and water management programs. Clay pot or porous pipe is a traditional sub-irrigation method and is ideal for many farms in the world’s dry land with small and medium sized farms and gardens and is still used limitedly in dry lands of India, Iran, Pakistan, the Middle East, and Latin-America. Clay capsule is one of porous pipes in sub irrigation that is able to release water in near root zone with self- regulative capacity. Watering occurs only in amounts that the plants actually need (this amount is equal to field capacity and released water in near root zone without electricity or use of an automatic dispenser. Materials and Methods: A study was carried out in 2013 on the experimental field of agriculture faculty of Tarbiat Modares University, to study the effect of two irrigation types on qualitative and quantitative characters in grape production (Vitis vinifera L.. In order to provide the water requirement of grape plant were used porous clay capsules for sub irrigation with height and diameter of 12 cm and 3.5 cm and dripper with Neta film type for drip irrigation, respectively. Porous clay capsules provided from soil science group at Tarbiat Modares University. In this research, the volume of water delivered to grape plants during entire growth period in two different irrigation methods was measured separately with water-meters installed at all laterals. The water consumption, yield production and water use efficiency were evaluated and compared in two drip and porous clay irrigation systems at veraison phonological stages. In the veraison stages, cluster weight, cluster length, solid solution and pH content were measured in grape fruits. Leaf chlorophyll content and leaf water content were also measured in two irrigation systems. Results and Discussion: The results of fruit quality
Calcined clay lightweight ceramics made with wood sawdust and sodium silicate
Energy Technology Data Exchange (ETDEWEB)
Santis, Bruno Carlos de; Rossignolo, Joao Adriano, E-mail: desantis.bruno@gmail.com [Universidade de Sao Paulo (USP), Pirassununga, SP (Brazil); Morelli, Marcio Raymundo [Universidade Federal de Sao Carlos (UFSCar), SP (Brazil). Departamento de Engenharia de Materiais
2016-11-15
This paper aims to study the influence of including wood sawdust and sodium silicate in the production process of calcined clay lightweight ceramics. In the production process first, a sample used by a company that produces ceramic products in Brazil was collected. The sample was analysed by techniques of liquidity (LL) and plasticity (LP) limits, particle size analysis, specific mass, X-ray diffraction (XRD) and X ray fluorescence spectrometry (XRF). From the clay, specimens of pure clay and mixtures with wood sawdust (10%, 20% and 30% by mass) and sodium silicate were produced and fired at a temperature of 900 deg C. These specimens were submitted to tests of water absorption, porosity, specific mass and compressive strength. Results of this research indicate that the incorporation of wood sawdust and sodium silicate in the ceramic paste specimens can be useful to make calcined clay lightweight ceramics with special characteristics (low values of water absorption and specific mass and high values of compressive strength), which could be used to produce calcined clay lightweight aggregates to be used in structural concrete. (author)
Engineered clay-shredded tyre mixtures as barrier materials
International Nuclear Information System (INIS)
Al-Tabbaa, A.; Aravinthan, T.
1997-01-01
An engineered clay consisting of kaolin and bentonite was mixed with shredded tyre in various weight percentages and examined for use as a constituent in a landfill liner. The clay-tyre mixtures properties in terms of compaction, unconfined compressive strength, permeability to water and paraffin, leachability, stress-strain behaviour, free swell behaviour and swelling pressure were investigated. The results show that the dry density and strength reduced with the addition of tyre and also with increased tyre content but that good interaction was developed between the clay and tyre. The strain at failure increased showing reinforcing effect of the tyre. The permeability to paraffin was considerably reduced compared to that to water due to the presence of the tyre which caused high swelling pressures to develop. The leachability results indicate initial high concentrations leaching out of the soil-tyre mixtures which will be subjected to dilution in the environment. This work adds evidence to the potential advantages of using soil-tyre mixtures as a landfill liner material
Analysis on Wetting Deformation Properties of Silty Clay
Directory of Open Access Journals (Sweden)
Xinrong Liu
2014-06-01
Full Text Available Changes in water level that cause deformation and stability problems often occur in foundation pit engineering. Water damage is one of the main problems that will lead to disasters in foundation pit engineering. Research findings with regard to properties of wetting deformation due to water damage can be applied not only in foundation pit engineering, slope engineering, hydraulic engineering, and mining engineering but also in related issues in the field of theoretical research and practice. In this study, the characteristics of silty clay deformation after wetting are examined from the perspective of the effect of wetting on the side wall of foundation pit, and wetting experiments on silty clay of a selected area’s stratum located in Chongqing Municipality are conducted under different confining pressures and stress levels through a multi-function triaxial apparatus. Then, laws of silty clay wetting deformation are obtained, and the relationship between wetting stress level and wetting deformation amount is also figured out. The study reveals that the maximum values of wetting deformation under different confining pressures have appear at a particular stress level; therefore, the related measures should be taken to avoid this deformation in the process of construction.
Role of interlayer hydration in lincomycin sorption by smectite clays.
Wang, Cuiping; Ding, Yunjie; Teppen, Brian J; Boyd, Stephen A; Song, Cunyi; Li, Hui
2009-08-15
Lincomycin, an antibiotic widely administered as a veterinary medicine, is frequently detected in water. Little is known about the soil-water distribution of lincomycin despite the fact that this is a major determinant of its environmental fate and potential for exposure. Cation exchange was found to be the primary mechanism responsible for lincomycin sorption by soil clay minerals. This was evidenced by pH-dependent sorption, and competition with inorganic cations for sorptive sites. As solution pH increased, lincomycin sorption decreased. The extent of reduction was consistent with the decrease in cationic lincomycin species in solution. The presence of Ca2+ in solution diminished lincomycin sorption. Clay interlayer hydration status strongly influenced lincomycin adsorption. Smectites with the charge deficit from isomorphic substitution in tetrahedral layers (i.e., saponite) manifest a less hydrated interlayer environment resulting in greater sorption than that by octahedrally substituted clays (i.e., montmorillonite). Strongly hydrated exchangeable cations resulted in a more hydrated clay interlayer environment reducing sorption in the order of Ca- smectite. X-ray diffraction revealed that lincomycin was intercalated in smectite clay interlayers. Sorption capacity was limited by clay surface area rather than by cation exchange capacity. Smectite interlayer hydration was shown to be a major, yet previously unrecognized, factor influencing the cation exchange process of lincomycin on aluminosilicate mineral surfaces.
Laboratory study of the Flandres clay swelling
International Nuclear Information System (INIS)
Khaddaj, Said
1992-01-01
The first chapter contains a survey about the swelling of soils, and about the experimental methods used to characterize this phenomenon. A classification of soils in function of their swelling potential is proposed. The second chapter deals with the properties of Flandres clay. Chemical and mineralogical compositions, mechanical properties and free swell index are given. The third chapter contains a presentation of the study of the swelling potential of Flandres clay using the oedometer. Four methods are described and used (free-swell, different pressures, pre-swell and direct-swell). A numerical simulation of free-swell tests is also given. The fourth chapter includes a presentation of the study of the swelling behaviour of Flandres clay using a triaxial cell. Three methods are used: free-swell, pre-swell and different-pressures. The last chapter contains a parametric study of the swelling behaviour of Flandres clay. The influence of some parameters such as sample thickness, initial water content, vertical load and load history is presented. (author) [fr
Process for preparing organoclays for aqueous and polar-organic systems
Chaiko, David J.
2001-01-01
A process for preparing organoclays as thixotropic agents to control the rheology of water-based paints and other aqueous and polar-organic systems. The process relates to treating low-grade clay ores to achieve highly purified organoclays and/or to incorporate surface modifying agents onto the clay by adsorption and/or to produce highly dispersed organoclays without excessive grinding or high shear dispersion. The process involves the treatment of impure, or run-of-mine, clay using an aqueous biphasic extraction system to produce a highly dispersed clay, free of mineral impurities and with modified surface properties brought about by adsorption of the water-soluble polymers used in generating the aqueous biphasic extraction system. This invention purifies the clay to greater than 95%.
Geochemical porosity values obtained in core samples from different clay-rocks
International Nuclear Information System (INIS)
Fernandez, A.M.
2010-01-01
Document available in extended abstract form only. Argillaceous formations of low permeability are considered in many countries as potential host rocks for the disposal of high level radioactive wastes (HLRW). In order to determine their suitability for waste disposal, evaluations of the hydro-geochemistry and transport mechanisms from such geologic formations to the biosphere must be undertaken. One of the key questions about radionuclide diffusion and retention is to know the chemistry and chemical reactions and sorption processes that will occur in the rock and their effects on radionuclide mobility. In this context, the knowledge of the pore water chemistry is essential for performance assessment purposes. This information allows to establish a reliable model for the main water-rock interactions, which control the physico-chemical parameters and the chemistry of the major elements of the system. An important issue in order to model the pore water chemistry in clayey media is to determine the respective volume accessible to cations and anions, i.e, the amount of water actually available for chemical reactions/solute transport. This amount is usually referred as accessible porosity or geochemical porosity. By using the anion inventories, i.e. the anion content obtained from aqueous leaching, and assuming that all Cl - , Br - and SO4 2- leached in the aqueous extracts originates from pore water, the concentration of a conservative ion can be converted into the real pore water concentration if the accessible porosity is known. In this work, the accessible porosity or geochemical porosity has been determined in core samples belonging to four different formations: Boom Clay from Hades URL (Belgium, BE), Opalinus Clay from Mont Terri (Switzerland, CH), and Callovo-Oxfordian argillite from Bure URL (France, FR). The geochemical or chloride porosity was defined as the ratio between the pore water volume containing Cl-bearing pore water and the total volume of a sample
Mobility of the dissolved organic matter through intact boom clay cores
International Nuclear Information System (INIS)
Put, M.J.; Dierckx, A.; Aertsens, M.; Canniere, P. de
1998-01-01
Performance assessment studies are expected to predict the enhancement of the migration of trivalent lanthanides and actinides due to their complexation with organic matter, which play a role as a transport agent [1]. Therefore, the mobility of the dissolved organic matter in the interstitial boom clay water is studied. For the first time, the mobile fraction present in the clay water is concentrated and labelled with a radioisotope to study the mobility of the organic matter in clay and the interaction of the mobile with the non-mobile. The isotopes tested as label are 125 I and 14 C. The 125 I label proved to be unstable and hence discarded. The labelled organic matter is then diluted for migration experiments on boom clay cores under anaerobic conditions. The influence of the molecular size on its mobility is studied by the separation of the labelled organic matter in different size fractions. (orig.)
Energy Technology Data Exchange (ETDEWEB)
Alonso, E E; Alcoverro, J
1999-07-01
Stage 2 of CATSIUS CLAY Project: Validation Exercises at Laboratory Scale includes two Benchmarks, Benchmark 2.1: Oedometer Suction Controlled Tests on Samples of compacted Boom Clay and Benchmark 2.2: Small Scale Weltting-Heating Test on Compacted Bentonite. BM 2.1 had two parts: BM 2.1A (volumetric deformation upon wetting-drying cycles) and BM 2.1 B (swelling pressure test). In BM 2.1A, participants were asked to model the results of a series of five tests on samples of compacted Boom clay. In BM 2.1B, a swelling pressure test in which suction, vertical and horizontal stresses were monitored, was proposed as a blind exercise. Participants were asked to use, without further changes, the models calibrated in BM 2.1A. This exercise provides an evaluation of the capabilities of current mechanical constitutive models for unsaturated clay behaviour. It was found that, even if a calibration exercise on the basis of known experimental data is satisfactory, blind predictions of tests involving different paths may prove difficult. The test set up for BM 2.2 consisted of a stainless stell cell filled with highly expansive compacted bentonite (S2 clay from Almeria, Spain). The clay was subjected to a simultaneous central heating and a progressive water inflow through the botton plate. Temperature at various locations within the sample and the boundary radial stress were monitored throughout the test. Water content distribution was also measured at the end of the experiment. Predictions for this benchmark required the solution of field equations for flow, temperature distribution and mechanical analysis. Model parameters were derived from the extensive set of available experiments on this clay. Comparison between model predictions and measurements revealed the significance of water transport in vapour phase, the difficulties to predict boundary stresses and the general good agreement between measured and calculated temperatures. The report provides a detailed accojnt of the
International Nuclear Information System (INIS)
Alonso, E. E.; Alcoverro, J.
1999-01-01
Stage 2 of CATSIUS CLAY Project: Validation Exercises at Laboratory Scale includes two Benchmarks, Benchmark 2.1: Oedometer Suction Controlled Tests on Samples of compacted Boom Clay and Benchmark 2.2: Small Scale Weltting-Heating Test on Compacted Bentonite. BM 2.1 had two parts: BM 2.1A (volumetric deformation upon wetting-drying cycles) and BM 2.1 B (swelling pressure test). In BM 2.1A, participants were asked to model the results of a series of five tests on samples of compacted Boom clay. In BM 2.1B, a swelling pressure test in which suction, vertical and horizontal stresses were monitored, was proposed as a blind exercise. Participants were asked to use, without further changes, the models calibrated in BM 2.1A. This exercise provides an evaluation of the capabilities of current mechanical constitutive models for unsaturated clay behaviour. It was found that, even if a calibration exercise on the basis of known experimental data is satisfactory, blind predictions of tests involving different paths may prove difficult. The test set up for BM 2.2 consisted of a stainless stell cell filled with highly expansive compacted bentonite (S2 clay from Almeria, Spain). The clay was subjected to a simultaneous central heating and a progressive water inflow through the botton plate. Temperature at various locations within the sample and the boundary radial stress were monitored throughout the test. Water content distribution was also measured at the end of the experiment. Predictions for this benchmark required the solution of field equations for flow, temperature distribution and mechanical analysis. Model parameters were derived from the extensive set of available experiments on this clay. Comparison between model predictions and measurements revealed the significance of water transport in vapour phase, the difficulties to predict boundary stresses and the general good agreement between measured and calculated temperatures. The report provides a detailed accojnt of the
Experimental research on dispersion parameters of ground water around the area of CIAE
International Nuclear Information System (INIS)
Yu Jun
1993-01-01
The dispersion are important parameters in modeling the migration of pollutant in the ground water. Due to the complexity of geological media, variant dispersion is expected according to the difference of the geological media. Three parts are included in physical simulation in the laboratory column, tracer experiment in the field and the prediction of dispersion using the stochastic model. Experimental results show that the dispersion obtained in the column are three orders of magnitude smaller than that obtained in the field. Using the field values of conductivity and stochastic theory, the calculated asymptotic longitudinal and lateral dispersion are 370 and 0.45 meters respectively and the correlation length is 400 meters approximately. Using the dispersion obtained from the formula in the paper can enhance the precision of the model prediction, the distance heeded to reach the Fick's dispersion is 6 km approximately
The Effects of High Salinity Groundwater on the Performance of Clay Barriers
International Nuclear Information System (INIS)
Savage, David
2005-08-01
Potential changes in groundwater chemistry during the operational or post-closure periods of the Swedish repository for spent fuel could affect the performance of both the bentonite buffer and repository backfill. For example, the up-coning of saline groundwater could lead to decreased swelling pressures in both the bentonite buffer and tunnel backfills, and could also induce 'piping'. SKB is considering these issues as part of its 'SR-Can' safety assessment. This report reviews evidence for the behaviour of swelling clays in groundwaters of varying salinity with special relevance to the SKB programme. Smectite clays can absorb water into clay inter-layers with the most important parameters being: the surface density of charge of the clay; the charge and solvation behaviour of the inter-layer ions; and the electrolyte concentration or activity of water. Two categories of swelling are generally observed: innercrystalline swelling caused by the hydration of the exchangeable cations in the dry clay; and osmotic swelling, resulting from concentration gradients in ion concentrations between clay surfaces and pore water. Several models exist to interpret and predict the swelling behaviour of clays. SKB currently prefer an interpretation of clay swelling pressure where clay particles are viewed as 'macro-ions' and the entire clay-water system can be considered as a 'polyelectrolyte'. SKB use the term 'Donnan exclusion' to estimate the amount of introduced ions into the clay and hence the amount of reduced swelling pressure due to contact with a saline solution. Donnan exclusion is the process whereby the migration of anions through the narrow aqueous film surrounding clay platelets is restricted due to the repulsion by the negative charge of the clay platelets. SKB's experimental work shows that: There is an exponential relation between swelling pressure and mean basal interlamellar spacing of the clay. Ions from the external electrolyte solution enter the clay volume
The Effects of High Salinity Groundwater on the Performance of Clay Barriers
Energy Technology Data Exchange (ETDEWEB)
Savage, David [Quintessa Ltd., Nottingham (United Kingdom)
2005-07-01
Potential changes in groundwater chemistry during the operational or post-closure periods of the Swedish repository for spent fuel could affect the performance of both the bentonite buffer and repository backfill. For example, the up-coning of saline groundwater could lead to decreased swelling pressures in both the bentonite buffer and tunnel backfills, and could also induce 'piping'. SKB is considering these issues as part of its 'SR-Can' safety assessment. This report reviews evidence for the behaviour of swelling clays in groundwaters of varying salinity with special relevance to the SKB programme. Smectite clays can absorb water into clay inter-layers with the most important parameters being: the surface density of charge of the clay; the charge and solvation behaviour of the inter-layer ions; and the electrolyte concentration or activity of water. Two categories of swelling are generally observed: innercrystalline swelling caused by the hydration of the exchangeable cations in the dry clay; and osmotic swelling, resulting from concentration gradients in ion concentrations between clay surfaces and pore water. Several models exist to interpret and predict the swelling behaviour of clays. SKB currently prefer an interpretation of clay swelling pressure where clay particles are viewed as 'macro-ions' and the entire clay-water system can be considered as a 'polyelectrolyte'. SKB use the term 'Donnan exclusion' to estimate the amount of introduced ions into the clay and hence the amount of reduced swelling pressure due to contact with a saline solution. Donnan exclusion is the process whereby the migration of anions through the narrow aqueous film surrounding clay platelets is restricted due to the repulsion by the negative charge of the clay platelets. SKB's experimental work shows that: There is an exponential relation between swelling pressure and mean basal interlamellar spacing of the clay. Ions from the
DEFF Research Database (Denmark)
Grathwohl, Peter; Haberer, Cristina; Ye, Yu
Diffusive–dispersive mass transfer in the capillary fringe is important for many groundwater quality issues such as transfer of volatile compounds into (and out of) the groundwater, the supply of oxygen for aerobic degradation of hydrocarbons as well as for precipitation of minerals (e.g. iron...... hydroxides). 2D-laboratory scale experiments were used to investigate the transfer of oxygen into groundwater under non-reactive and reactive conditions, at steady state and with water table fluctuations. Results show that transfer of oxygen is limited by transverse dispersion in the capillary fringe...... and the dispersion coefficients are the same as below the water table. Water table fluctuations cause temporarily increased fluxes of oxygen into groundwater during draining conditions and entrapped air after water table rise. High-permeability inclusions in the capillary fringe enhance mass transfer of oxygen...
Hydrothermal field test with french candidate clay embedding steel heater in the Stripa mine
International Nuclear Information System (INIS)
Pusch, R.; Karnland, O.; Lajudie, A.; Lechelle, J.; Bouchet, A.
1992-12-01
Field experiments with French kaolinite/smectite clay heated up to 170 degrees C in boreholes in granite were conducted for 8 months and 4 years. The clay heated for 8 months has a considerably higher water content and it had undergone much less changes in mineralogy and physical properties than the clay exposed to heating for 4 years. The drying of the latter clay was probably caused by hydrogen gas from corrosion of the heater. The clay next to the heater turned into clay-stone despite conversion of the kaolinite component to smectite. (42 refs)
Schmitz, Birger; Andersson, Per; Dahl, Jeremy
1988-01-01
Microbial activity and redox-controlled precipitation have been of major importance in the process of metal accumulation in the strongly Ir-enriched Cretaceous-Tertiary (K-T) boundary clay, the Fish Clay, at Stevns Klint in Denmark. Two important findings support this view: 1) Kerogen, recovered by leaching the Fish Clay in HCl and HF, shows an Ir concentration of 1100 ppb; this represents about 50% of the Ir present in the bulk sample Fish Clay. Strong organometallic complexes is the most probable carrier phase for this fraction of Ir. Kerogen separated from the K-T boundary clay at Caravaca, Spain, similarly exhibits enhanced Ir concentrations. 2) Sulfur isotope analyses of metal-rich pyrite spherules, which occur in extreme abundance (about 10% by weight) in the basal Fish Clay, give a δ 34S value of -32%.. This very low value shows that sulfide formation by anaerobic bacteria was intensive in the Fish Clay during early diagenesis. Since the pyrite spherules are major carriers of elements such as Ni, Co, As, Sb and Zn, microbial activity may have played an important role for concentrating these elements. In the Fish Clay large amounts of rare earth elements have precipitated from sea water on fish scales. Analyses reveal that, compared with sea water, the Fish Clay is only about four times less enriched in sea-water derived lanthanides than in Ir. This shows that a sea-water origin is plausible for elements that are strongly enriched in the clay, but whose origin cannot be accounted for by a lithogenic precursor.
International Nuclear Information System (INIS)
Almeida, Lidiane A.; Marques, Maria F.V.; Oliveira, Jaqueline S.
2011-01-01
Polymer nanocomposites present highly improved general properties in comparison with original polymer and their conventional composites. The mayor disadvantage in preparing these materials is the difficulty in the dispersion of the nanofillers in the polymer matrix. In the present work, the synthesis of bisupported (MgCl 2 /clay) catalyst was performed for obtaining polyethylene and polypropylene nanocomposites by in situ polymerization with the aim to achieve higher dispersion of the nanofillers in the polyolefin matrix. Moreover, the influence of ammonium salt (employed in the organophilization of the clay) on the fixation of the catalyst components and therefore, on the catalyst activity was evaluated. The catalysts were characterized by TGA, SEM, EDX, and XRD. Polymers were characterized by DSC, isotactic index through heptane extractables (HS), TGA, EDX, XRD, and optical microscopy (OM). The results showed that the type of clay modifier has a great influence on the catalyst performance. (author)
Effect of clay content in rock on oil extraction under alkaline seam conditions
Energy Technology Data Exchange (ETDEWEB)
Vezirov, D Sh; Gorbunov, A T; Kasimov, Sh A; Kashchavtsev, V E; Tairov, N D
1978-01-01
When oil beds are flooded with alkaline solutions, the alkaline concentration in the solution can be significantly reduced as a result of the interaction between clay and alkali. Large losses of alkali in the bed can render the flooding method ineffective. Experimental studies were conducted on porous media containing up to 25% clay at a constant permeability of 1 D in order to determine the oil extraction indices for clay-containing rock. Constant permeability is maintained by using clays, marshalite, and quartz sand in various proportions. Oil having a viscosity of 99.17 sP, and containing a large amount of surfactants, including 1.1% naphthenic acid, was extracted by fresh water and a 0.25% solution of NaOH. The extraction of oil by fresh water and NaOH solution from quartz sand indicated the advantage of using alkaline solutions. The extraction coefficient increased by 11% with the use of this method. As clay is added to the sand, the extraction coefficient decreases, and is reduced to 12.7% when the clay content reaches 25%. Nevertheless, a comparison of data obtained for quartz sand with fresh water on a porous medium containing 25% clay with an alkaline solution, indicates that the extraction coefficient is just 1.5% lower even in the presence of such a large amount of clay. Consequently, alkaline flooding should still be given preference over the usual methods under specific conditions and where the rock has a comparatively large amount of clay, in view of all the basic factors that influence the extraction process. The results obtained can be used for selecting alkaline concentration in evaluating the efficiency of flooding oil beds with alkaline solutions. 2 figures, 2 tables.
Water-Dispersible Multi-Walled Carbon Nanotubes and Novel Hybrid Nanostructures
Pham, Tuan Anh; Son, Se Mo; Jeong, Yeon Tae
2010-01-01
Water-dispersible multi-walled carbon nanotubes (MWNTs) were successfully prepared by the chemical grafting of acylated MWNTs with adenosine. The MWNTs were first purified and oxidized in order to obtain carboxylic acid funcionalized MWNTs, which was further acylated with thionyl chloride to give
Large scale laboratory diffusion experiments in clay rocks
International Nuclear Information System (INIS)
Garcia-Gutierrez, M.; Missana, T.; Mingarro, M.; Martin, P.L.; Cormenzana, J.L.
2005-01-01
Full text of publication follows: Clay formations are potential host rocks for high-level radioactive waste repositories. In clay materials the radionuclide diffusion is the main transport mechanism. Thus, the understanding of the diffusion processes and the determination of diffusion parameters in conditions as similar as possible to the real ones, are critical for the performance assessment of deep geological repository. Diffusion coefficients are mainly measured in the laboratory using small samples, after a preparation to fit into the diffusion cell. In addition, a few field tests are usually performed for confirming laboratory results, and analyse scale effects. In field or 'in situ' tests the experimental set-up usually includes the injection of a tracer diluted in reconstituted formation water into a packed off section of a borehole. Both experimental systems may produce artefacts in the determination of diffusion coefficients. In laboratory the preparation of the sample can generate structural change mainly if the consolidated clay have a layered fabric, and in field test the introduction of water could modify the properties of the saturated clay in the first few centimeters, just where radionuclide diffusion is expected to take place. In this work, a large scale laboratory diffusion experiment is proposed, using a large cylindrical sample of consolidated clay that can overcome the above mentioned problems. The tracers used were mixed with clay obtained by drilling a central hole, re-compacted into the hole at approximately the same density as the consolidated block and finally sealed. Neither additional treatment of the sample nor external monitoring are needed. After the experimental time needed for diffusion to take place (estimated by scoping calculations) the block was sampled to obtain a 3D distribution of the tracer concentration and the results were modelled. An additional advantage of the proposed configuration is that it could be used in 'in situ
International Nuclear Information System (INIS)
Olchitzky, E.
2002-02-01
The use of swelling clay for engineered safety barriers of radioactive waste disposal require the understanding of its thermal-hydro-mechanical behaviour. This work concerns particularly the characterization and the modelling of the behaviour of one of these clays: the FoCa7 clay. The characteristics of the studied material are: the sorption (desorption) curve and the water permeability. For each of them, new experiments have allowed to acquire data in fields still few explored: in temperature (between 20 and 80 C) for the sorption curve and in the unsaturated field for the water permeability. The analysis of these results and of bibliographic data has allowed in one hand to estimate the importance of the hysteresis phenomenon and the temperature influence on the sorption curve and in another hand, to establish the requirement to introduce in the modelling of the sorption curve, a plastic parameter due to the irreversible deformations occurring during the compaction. Moreover, the tests carried out for data acquirement have been used too to give validation elements to the non linear behaviour laws proposed by O. Coussy and P. Dangla for the non saturated porous media. The particularity of these laws is to suppose the existence of an effective constraint in the non saturated field, this shows the importance of the validation elements presented here. (O.M.)
Modeling of Cation Binding in Hydrated 2:1 Clay Minerals - Final Report
International Nuclear Information System (INIS)
Smith, David E.
2000-01-01
Hydrated 2:1 clay minerals are high surface area, layered silicates that play a unique role in determining the fate of radionuclides in the environment. This project consisted of developing and implementing computer simulation methods for molecular characterization of the swelling and ion exchange properties of Hydrated 2:1 clay minerals, and the subsequent analysis and theoretical modeling with a view toward improving contaminant transport modeling as well as soil remediation and radionuclide containment strategies. Project results included the (a) development of simulation methods to treat clays under environmentally relevant conditions of variable water vapor pressure; (b) calculation of clay swelling thermodynamics as a function of interlayer ion size and charge (calculated quantities include immersion energies, free energies, and entropies of swelling); and (c) calculation of ion exchange free energies, including contributions from changing interlayer water contents and layer spacing
Characterisation of the wall-slip during extrusion of heavy-clay products
Kocserha, I.; Gömze, A. L.; Kulkov, S.; Kalatur, E.; Buyakova, S. P.; Géber, R.; Buzimov, A. Y.
2017-01-01
During extrusion through the extrusion die, heavy-clay compounds are usually show plug flow with extensive slip at the wall of the die. In this study, the viscosity and the thickness of the slip layer were investigated. For the examination a brick-clay from Malyi (Hungary) deposit was applied as a raw material. The clay was characterised by XRPD, BET, SEM and granulometry. As the slip layer consists of suspension of the fine clay fraction so the clay minerals content of the clay (dviscosity of suspension with different water content was measured by means of rotational viscosimeter. The thickness of the slip layer was calculated from the measured viscosity and other data obtained from an earlier study with capillary rheometer. The calculated thickness value showed a tendency to reach a limit value by increasing the extrusion speed.
Bio-Based Nano Composites from Plant Oil and Nano Clay
Lu, Jue; Hong, Chang K.; Wool, Richard P.
2003-03-01
We explored the combination of nanoclay with new chemically functionalized, amphiphilic, plant oil resins to form bio-based nanocomposites with improved physical and mechanical properties. These can be used in many new applications, including the development of self-healing nanocomposites through controlled reversible exfoliation/intercalation, and self-assembled nano-structures. Several chemically modified triglyceride monomers of varying polarity, combined with styrene (ca 30include acrylated epoxidized soybean oil (AESO), maleated acrylated epoxidized soybean oil (MAESO) and soybean oil pentaerythritol glyceride maleates (SOPERMA), containing either hydroxyl group or acid functionality or both. The clay used is a natural montmorillonite modified with methyl tallow bis-2-hydroxyethyl quaternary ammonium chloride, which has hydroxyl groups. Both XRD and TEM showed a completely exfoliated structure at 3 wtwhen the clay content is above 5 wtconsidered a mix of intercalated and partially exfoliated structure. The controlled polarity of the monomer has a major effect on the reversible dispersion of clay in the polymer matrix. The bio-based nanocomposites showed a significant increase in flexural modulus and strength. Supported by EPA and DoE
International Nuclear Information System (INIS)
Villar, M.V.
1995-01-01
This report refers to the work carried out by Technic Geologic Division of CIEMAT (CIEMAT.DT.TG) coordinated by SCK/CEN (Belgium), participating besides UPC-DIT and University of Wales on the framework of CEC Contract F12W-CT91-0102 (DOEO). It presents the results obtained. The total results on the project will be published by CE in the EUR series. The role of CIEMAT in this project was to carry out tests in which the conditions of the clay barrier in the repository were simulated. The interaction of heat coming from the wastes and of water coming from the geological medium has been reproduced on compacted clay blocks. For the performance of tests on high density compacted clay blocks (Task 2.1) and for the cementation and chemical-mineralogical transformation studies two different cells were designed and constructed in stainless steel: a thermohydraulic cell and an alteration cell. The experiments performed in these cells have provided us with a better knowledge of the heat source, hydration system and sensors, as well as interesting data on heat and water diffusion. A revision of the experiments performed on the thermohydraulic cell was presented at the ''International Workshop on Thermomechanics of Clays and Clay Barriers'' held in Bergamo in October'93 (Villar et al. 1993)
Aluminium - Cobalt-Pillared Clay for Dye Filtration Membrane
Darmawan, A.; Widiarsih
2018-04-01
The manufacture of membrane support from cobalt aluminium pillared clay has been conducted. This research was conducted by mixing a clay suspension with pillared solution prepared from the mixture of Co(NO3)2.6H2O and AlCl3.6H2O. The molar ratio between Al and Co was 75:25 and the ratio of [OH-]/[metal] was 2. The clay suspension was stirred for 24 hours at room temperature, filtered and dried. The dried clay was then calcined at 200°C, 300°C and 400°C with a ramp rate of 2°C/min. Aluminium-cobalt-pillared clay was then characterized by XRD and GSA and moulded become a membrane support for subsequent tests on dye filtration. The XRD analysis showed that basal spacing (d 001) value of aluminium cobalt was 19.49 Å, which was higher than the natural clay of 15.08Å however, the basal spacing decreased with increasing calcination temperature. The result of the GSA analysis showed that the pore diameter of the aluminium cobalt pillared clay membrane was almost the same as that of natural clay that were 34.5Å and 34.2Å, respectively. Nevertheless, the pillared clay has a more uniform pore size distribution. The results of methylene blue filtration measurements demonstrated that the membrane filter support could well which shown by a clear filtrate at all concentrations tested. The value of rejection and flux decreased with the increasing concentration of methylene blue. The values of dye rejection and water flux reached 99.89% and 5. 80 x 10-6 kg min-1, respectively but they decreased with increasing concentration of methylene blue. The results of this study indicates that the aluminium-pillared clay cobalt could be used as membrane materials especially for ultrafiltration.
Influence of natural mobile organic matter on europium retention on Bure clay rock
International Nuclear Information System (INIS)
Vu-Do, Laurence
2013-01-01
Bure clay rock (CR) was chosen as host rock for the French high and intermediate level long lived radioactive waste repository. This choice is mostly explained by the retention ability of the Callovo-Oxfordian rock (COx). Bure clay rock contains natural organic matter (OM) that could have an influence on radionuclide retention. The aim of this work is to assess the influence of natural mobile OM on the retention of Eu on clay rock. Eu was chosen as a chemical model for trivalent actinides contained in vitrified waste. Three organic molecules were studied: suberic, sorbic and tiglic acids, small organic acids identified in COx pore water. All the experiments were carried out in an environment recreating COx water (pH=7.5; I=0.1 mol/L; PCO 2 =10 -2 bar).Clay rock sample characterization showed that the sample used in this work was similar to those previously extracted from the area of interest and that it was necessary to maintain pH at 7.5 to avoid altering the clay rock. The Eu-OM system study indicated that organic acids had no influence on Eu speciation in COx water. The Eu-CR system experimental study confirmed that retention implied sorption on CR (C(Eu)≤6.10 -6 mol/L) and precipitation in COx water (C(Eu)≥6.10 -6 mol/L). Distribution coefficient Rd (quantifying sorption) was estimated at 170 ± 30 L/g. This high value is consistent with literature values obtained on clay rocks. The ternary Eu-OM-CR system study showed a slight increase of sorption in the presence of organic matter. This synergistic effect is very satisfactory in terms of storage security: the presence of small organic acids in clay rock does not question retention properties with respect to europium and trivalent actinides. (author)
Pedro, Cathy
2011-01-01
In this article, the author describes a project designed for fourth-graders that involves making clay relief sculptures of houses. Knowing the clay houses will become a family heirloom makes this lesson even more worth the time. It takes three classes to plan and form the clay, and another two to underglaze and glaze the final products.
Effect of Sonification Time on Synthesisi and Corrosion Resistance of Epoxy-Clay Nanocomposite
Directory of Open Access Journals (Sweden)
Niloufar Bahrami Panah
2016-09-01
Full Text Available In recent years many research works have been carried out on anti-corrosive nanocomposites coatings containing mineral reinforcements. The most important criteria in these attempts are polymerization method and the type of matrix and reinforcement of nanocomposites. In this regard, the physical and mechanical properties of the polymers in which a small amount of filler is used can be improved. In this research, an epoxy-clay nanocomposite was synthesized by in-situ polymerization method using a resin matrix based on bisphenol-A type epoxy and montmorillonite clay (Closite 15A. The treatment was used at different ultrasonic stirring times to disperse 1-4 weight percentages of clay particles into the matrix. The structure of synthesized epoxy-clay nanocomposite was studied by scanning electron microscopy and X-ray diffraction techniques. The average size of clay particles was determined by X-ray diffraction measurement. Then, anti-corrosion properties of epoxy-clay coatings, prepared under different ultrasonic durations and applied on carbon steel panels, were investigated by Tafel and electrochemical impedance spectroscopy techniques. For this purpose, the carbon steel panels coated with these coatings were immersed in 3.5% sodium chloride solution and tested at different immersion times. The results indicated that a nanocomposite containing 1% clay, synthesized, stirred 60 min ultrasonically, produced smaller particle size, lower corrosion current density and higher coating corrosion resistance than the other composite formulations. This nanocomposite provided superior protection against corrosion in sodium chloride solution.
Effects of biochar on hydraulic conductivity of compacted kaolin clay.
Wong, James Tsz Fung; Chen, Zhongkui; Wong, Annie Yan Yan; Ng, Charles Wang Wai; Wong, Ming Hung
2018-03-01
Compacted clay is widely used as capillary barriers in landfill final cover system. Recently, biochar amended clay (BAC) has been proposed as a sustainable alternative cover material. However, the effects of biochar on saturated hydraulic conductivity (k sat ) of clay with high degree of compaction is not yet understood. The present study aims to investigate the effects of biochar on k sat of compacted kaolin clay. Soil specimens were prepared by amending kaolin clay with biochar derived from peanut-shell at 0, 5 and 20% (w/w). The k sat of soil specimens was measured using a flexible water permeameter. The effects of biochar on the microstructure of the compacted clay was also investigated using MIP. Adding 5% and 20% of biochar increased the k sat of compacted kaolin clay from 1.2 × 10 -9 to 2.1 × 10 -9 and 1.3 × 10 -8 ms -1 , respectively. The increase in k sat of clay was due to the shift in pore size distribution of compacted biochar-amended clay (BAC). MIP results revealed that adding 20% of biochar shifted the dominant pore diameter of clay from 0.01-0.1 μm (meso- and macropores) to 0.1-4 μm (macropores). Results reported in this communication revealed that biochar application increased the k sat of compacted clay, and the increment was positively correlated to the biochar percentage. Copyright © 2017 Elsevier Ltd. All rights reserved.
Geotechnical studies of Jaitapur marine clay
Digital Repository Service at National Institute of Oceanography (India)
Bhat, S.T.; Nayak, B.U.
characterisEd. by high water content and high Atterberg limits. Undrained shear strength varied from 1.8 to 6 KPa. These were moderately sensitive clays. Carbonate content which varied from 3 to 27%, was found to influence engineering properties of the soil...
Energy Technology Data Exchange (ETDEWEB)
Lempp, Christof; Menezes, Flora; Sachwitz, Simon [Halle-Wittenberg Univ., Halle (Saale) (Germany). Inst. fuer Geowissenschaften und Geographie
2016-12-15
The Opalinuston is a prominent rock representing the type of organic clay shales or clay stones within the sequence of Triassic and Jurassic marine sediments in Southern Germany. The rock forms a homogenous unit some ten meters thick. The degree of consolidation of this type of pelitic rock depends mainly on the former load conditions, but is also dependent on the long-term weathering and even on the present exposition. The geomechanical parameters such as shear strength, tensional strength and permeability vary with the state of consolidation and become important when the use is discussed of such rocks for radioactive waste disposal. A tunneling project at the northern escarpment of the Swabian Alb (Southwest Germany) within the Opalinus clay offered the rare opportunity to obtain fresh unweathered rock samples in greater amounts compared to fresh drilling cores from which geomechanical investigations are usually undertaken. Consequently, the results of geomechanical laboratory testings are presented in order to compare here the results of multistep triaxial compression tests, of hydraulic fracturing laboratory tests and of some other tests for rock characterization with the corresponding results of Opalinus clay sites in Switzerland that were investigated by the Swiss Nagra Company for host rock characterization. After a discussion of the relevant state of fresh Opalinus clay, especially of suction pressure conditions and saturation state, the results of triaxial shear tests are presented. Increasing shear deformation at increasing pressure and unchanged water saturation do not result in a significant strength reduction of the Opalinus clay. The rock shows increasing cohesion and stiffness, if multiple loading has repeatedly reached the failure point. Thus there is no increased permeability with continued shearing. Only at the beginning of the shearing process is a temporarily increased permeability to be expected due to dilatation processes. An increased
DEFF Research Database (Denmark)
Hermansen, Cecilie; Knadel, Maria; Møldrup, Per
2016-01-01
The ratios of mineral fines (carbon (OC), consisting of the n-ratio (i.e., the clay/OC ratio) and m-ratio (i.e., the fines/OC ratio) have recently been used to analyze and predict soil functional properties such as tilth conditions, clay dispersibility, degree...... from seven Danish and one Greenlandic fields, with a large textural range (clay: 0.027–0.355 kg kg−1; OC: 0.011–0.084 kg kg−1; n-ratio: 0.49–16.80; m-ratio: 1.46–32.14), were analyzed for texture and OC and subsequently scanned with a vis-NIR spectrometer from 400 to 2500 nm. The spectral data were...
Comparative study of organophilic clays to be used in the gas and petrol industry
International Nuclear Information System (INIS)
Rodrigues, S.C.G.; Queiroz, M.B.; Rodrigues, M.G.F.; Pereira, K.R.O.; Valenzuella- Diaz, F.R.
2009-01-01
The mixture oil/water occurs in the operations of production, transportation and refining, as well as during the use of its derivatives in the petroleum industry. This kind of water turns into a problem of how to be purified, and how to improve its quality. Researchers have been developed in order to find out water/oil separation processes that will be cheaper and more effective. One of the processes has been the use of organophilic clay utilized as a solver. This project studied two organophilic clays, Brasgel clay PA (sodic activated) and silt clay, which passed through a process of cation exchange with quaternary salt of ammonium cethyltrimethylammonium bromide by direct method. The samples were characterized by X-ray diffraction (XRD), Infrared Spectroscopy (IR), Scanning Electron Microscopy (SEM) and Foster's swelling in petroleum derivative. Foster's swelling was carried out with and without agitation in gasoline, diesel, toluene and lubricating oil. The results indicated the samples was organophilic materials, with improved efficiency of Brasgel clay in gasoline and diesel and when compared to silt clay in the test of capacity for adsorption and Foster's swelling, the results were similar to kerosene and lubricating oil. (author)
Clay, Water, and Salt: Controls on the Permeability of Fine-Grained Sedimentary Rocks.
Bourg, Ian C; Ajo-Franklin, Jonathan B
2017-09-19
The ability to predict the permeability of fine-grained soils, sediments, and sedimentary rocks is a fundamental challenge in the geosciences with potentially transformative implications in subsurface hydrology. In particular, fine-grained sedimentary rocks (shale, mudstone) constitute about two-thirds of the sedimentary rock mass and play important roles in three energy technologies: petroleum geology, geologic carbon sequestration, and radioactive waste management. The problem is a challenging one that requires understanding the properties of complex natural porous media on several length scales. One inherent length scale, referred to hereafter as the mesoscale, is associated with the assemblages of large grains of quartz, feldspar, and carbonates over distances of tens of micrometers. Its importance is highlighted by the existence of a threshold in the core scale mechanical properties and regional scale energy uses of shale formations at a clay content X clay ≈ 1/3, as predicted by an ideal packing model where a fine-grained clay matrix fills the gaps between the larger grains. A second important length scale, referred to hereafter as the nanoscale, is associated with the aggregation and swelling of clay particles (in particular, smectite clay minerals) over distances of tens of nanometers. Mesoscale phenomena that influence permeability are primarily mechanical and include, for example, the ability of contacts between large grains to prevent the compaction of the clay matrix. Nanoscale phenomena that influence permeability tend to be chemomechanical in nature, because they involve strong impacts of aqueous chemistry on clay swelling. The second length scale remains much less well characterized than the first, because of the inherent challenges associated with the study of strongly coupled nanoscale phenomena. Advanced models of the nanoscale properties of fine-grained media rely predominantly on the Derjaguin-Landau-Verwey-Overbeek (DLVO) theory, a mean field
Speciation of uranium in surface-modified, hydrothermally treated, (UO2)2+-exchanged smectite clays
International Nuclear Information System (INIS)
Giaquinta, D.M.; Soderholm, L.; Yuchs, S.E.; Wasserman, S.R.
1997-01-01
A successful solution to the problem of disposal and permanent storage of water soluble radioactive species must address two issues: exclusion of the radionuclides from the environment and the prevention of leaching from the storage media into the environment. Immobilization of radionuclides in clay minerals has been studied. In addition to the use of clays as potential waste forms, information about the interactions of radionuclides with clays and how such interactions affect their speciations is crucial for successful modeling of actinide-migration. X-ray absorption spectroscopy (XAS) is used to determine the uranium speciation in exchanged and surface-modified clays. The XAS data from uranyl-loaded bentonite clay are compared with those obtained after the particle surfaces have been coated with alkylsilanes. These silane films, which render the surface of the clay hydrophobic, are added in order to minimize the ability of external water to exchange with the water in the clay interlayer, thereby decreasing the release rate of the exchanged-uranium species. Mild hydrothermal conditions are used in an effort to mimic potential geologic conditions that may occur during long-term radioactive waste storage. The XAS spectra indicate that the uranyl monomer species remain unchanged in most samples, except in those samples that were both coated with an alkylsilane and hydrothermally treated. When the clay was coated with an organic film, formed by the acidic deposition of octadecyltrimethoxysilane, hydrothermal treatment results in the formation of aggregated uranium species in which the uranium is reduced from U VI to U IV
Directory of Open Access Journals (Sweden)
2008-11-01
Full Text Available The dielectric dispersion behaviour of montmorillonite (MMT clay nanoparticles colloidal suspension in poly(vinyl pyrrolidone-ethylene glycol (PVP-EG blends were investigated over the frequency range 20 Hz to 1 MHz at 30°C. The 0, 1, 2, 3, 5 and 10 wt% MMT clay concentration of the weight of total solute (MMT+PVP were prepared in PVP-EG blends using EG as solvent. The complex relative dielectric function, alternating current (ac electrical conductivity, electric modulus and impedance spectra of these materials show the relaxation processes corresponding to the micro-Brownian motion of PVP chain, ion conduction and electrode polarization phenomena. The real part of ac conductivity spectra of these materials obeys Jonscher power law σ′(ω =σdc + Aωn in upper frequency end of the measurement, whereas dispersion in lower frequency end confirms the presence of electrode polarization effect. It was observed that the increase of clay concentration in the PVP-EG blends significantly increases the ac conductivity values, and simultaneously reduces the ionic conductivity relaxation time and electric double layer relaxation time, which suggests that PVP segmental dynamics and ionic motion are strongly coupled. The intercalation of EG structures in clay galleries and exfoliation of clay sheets by adsorption of PVP-EG structures on clay surfaces are discussed by considering the hydrogen bonding interactions between the hydroxyl group (–OH of EG molecules, carbonyl group (C=O of PVP monomer units, and the hydroxylated aluminate surfaces of the MMT clay particles. Results suggest that the colloidal suspension of MMT clay nano particles in the PVP-EG blends provide a convenient way to obtain an electrolyte solution with tailored electrical conduction properties.
International Nuclear Information System (INIS)
1989-01-01
This reference method describes a simple procedure for comparing the toxicity of oil, oil dispersants, and mixtures thereof, to marine animals. It allows the toxicity of different dispersants to be rapidly compared to that of oil, or of a mixture of oil an oil dispersant. It is designed for routine monitoring and screening purposes and is not appropriate as a research method. The physical and chemical properties of oil dispersants create many difficulties in the measurements of their toxicity to marine organisms. Strictly speaking, their toxicity can only be accurately estimated using complex procedures and apparatus. (A relatively simple apparatus for preparing oil/water or oil/water/oil dispersant emulsions is described in Appendix B). Simpler methods can provide useful information, provided their limitations are clearly understood and taken into consideration in the assessment and application of their results. Some of the special considerations relating to the measurement of the toxicity of oil and oil dispersants are described in Appendix A. The Appendix also explains the rationale and limitations of the method described here. 3 refs, 4 figs, 2 tabs
Energy Technology Data Exchange (ETDEWEB)
Bayer, I.S., E-mail: ibayer1@illinois.edu [Department of Aerospace Engineering, University of Illinois at Urbana-Champaign, IL 61801 (United States); Steele, A.; Martorana, P.J. [Department of Aerospace Engineering, University of Illinois at Urbana-Champaign, IL 61801 (United States); Loth, E. [Department of Aerospace Engineering, University of Illinois at Urbana-Champaign, IL 61801 (United States); Department of Mechanical and Aerospace Engineering, University of Virginia, VA 22904 (United States)
2010-11-15
Nano-structured polyurethane/organoclay composite films were fabricated by dispersing moisture-curable polyurethanes and fatty amine/amino-silane surface modified montmorillonite clay (organoclay) in cyclomethicone-in-water emulsions. Cyclomethicone Pickering emulsions were made by emulsifying decamethylcyclopentasiloxane (D{sub 5}), dodecamethylcyclohexasiloxane (D{sub 6}) and aminofunctional siloxane polymers with water using montmorillonite particles as emulsion stabilizers. Polyurethane and organoclay dispersed emulsions were spray coated on aluminum surfaces. Upon thermosetting, water repellent self-cleaning coatings were obtained with measured static water contact angles exceeding 155{sup o} and low contact angle hysteresis (<8{sup o}). Electron microscopy images of the coating surfaces revealed formation of self-similar hierarchical micro- and nano-scale surface structures. The surface morphology and the coating adhesion strength to aluminum substrates were found to be sensitive to the relative amounts of dispersed polyurethane and organoclay in the emulsions. The degree of superhydrophobicity was analyzed using static water contact angles as well as contact angle hysteresis measurements. Due to biocompatibility of cyclomethicones and polyurethane, developed coatings can be considered for specific bio-medical applications.
International Nuclear Information System (INIS)
Bayer, I.S.; Steele, A.; Martorana, P.J.; Loth, E.
2010-01-01
Nano-structured polyurethane/organoclay composite films were fabricated by dispersing moisture-curable polyurethanes and fatty amine/amino-silane surface modified montmorillonite clay (organoclay) in cyclomethicone-in-water emulsions. Cyclomethicone Pickering emulsions were made by emulsifying decamethylcyclopentasiloxane (D 5 ), dodecamethylcyclohexasiloxane (D 6 ) and aminofunctional siloxane polymers with water using montmorillonite particles as emulsion stabilizers. Polyurethane and organoclay dispersed emulsions were spray coated on aluminum surfaces. Upon thermosetting, water repellent self-cleaning coatings were obtained with measured static water contact angles exceeding 155 o and low contact angle hysteresis ( o ). Electron microscopy images of the coating surfaces revealed formation of self-similar hierarchical micro- and nano-scale surface structures. The surface morphology and the coating adhesion strength to aluminum substrates were found to be sensitive to the relative amounts of dispersed polyurethane and organoclay in the emulsions. The degree of superhydrophobicity was analyzed using static water contact angles as well as contact angle hysteresis measurements. Due to biocompatibility of cyclomethicones and polyurethane, developed coatings can be considered for specific bio-medical applications.
International Nuclear Information System (INIS)
Bragg, J.R.; Yang, S.H.
1995-01-01
Natural interactions of fine mineral particles with residue oil and seawater, in a process called clay-oil flocculation, were found to create solids-stabilized oil-in-water emulsions on shoreline sediments at numerous locations in Prince William Sound following the Exxon Valdez spill. In laboratory tests using oiled sediment samples from Prince William Sound, these emulsions were shown to facilitate natural cleansing and dispersion of oil from sediments by moving water. To investigate the effect of flocculation on natural cleansing, studies were conducted to determine the hydrodynamic energy needed for seawater to remove flocculated oil residues from sediments sampled from shorelines. Water was pumped at different velocities through a column packed with oiled sediment, and the amount and composition of oil removed from the sediment were measured as functions of water velocity and sediment movement. In separate tests, oil removal was observed in a wave tank that generated wave heights less than and greater than needed to move sediments. 28 refs., 13 figs., 7 tabs
Clarification of olive mill and winery wastewater by means of clay-polymer nanocomposites.
Rytwo, Giora; Lavi, Roy; Rytwo, Yuval; Monchase, Hila; Dultz, Stefan; König, Tom N
2013-01-01
Highly polluted effluents from olive mills and wineries, among others, are unsuitable for discharge into standard sewage-treatment plants due to the large amounts of organic and suspended matter. Efficiency of all management practices for such effluents depends on an effective pretreatment that lowers the amount of suspended solids. Such pretreatments are usually based on three separate stages, taking a total of 2 to 6h: coagulation-neutralizing the colloids, flocculation-aggregating the colloids into larger particles, and separation via filtration or decanting. Previous studies have presented the concept of coagoflocculation based on the use of clay-polymer nanocomposites. This process adds a higher density clay particle to the flocs, accelerating the process to between 15 and 60 min. This study examined suitable nanocomposites based on different clays and polymers. The charge of the compounds increased proportionally to the polymer-to-clay ratio. X-ray diffraction (XRD) measurements indicated that in sepiolite-based nanocomposites there is no change in the structure of the mineral, whereas in smectite-based nanocomposites, the polymer intercalates between the clay layers and increases the spacing depending on the polymer-to-clay ratio. Efficiency of the coagoflocculation process was studied with a dispersion analyzer. Sequential addition of olive mill or winery effluents with a boosting dose of nanocomposites may yield a very efficient and rapid clarification pretreatment. Copyright © 2012 Elsevier B.V. All rights reserved.
The systems containing clays and clay minerals from modified drug release: a review.
Rodrigues, Luís Alberto de Sousa; Figueiras, Ana; Veiga, Francisco; de Freitas, Rivelilson Mendes; Nunes, Lívio César Cunha; da Silva Filho, Edson Cavalcanti; da Silva Leite, Cleide Maria
2013-03-01
Clays are materials commonly used in the pharmaceutical industry, either as ingredients or as active ingredients. It was observed that when they are administered concurrently, they may interact with drugs reducing their absorption. Therefore, such interactions can be used to achieve technological and biopharmaceutical advantages, regarding the control of release. This review summarizes bibliographic (articles) and technological (patents) information on the use of systems containing clays and clay minerals in modified drug delivery. In this area, formulations such natural clay, commercial clay, synthetic clay, composites clay-polymers, nanocomposites clay-polymers, films and hidrogels composites clay-polymers are used to slow/extend or vectorize the release of drugs and consequently they increase their bioavailability. Finally, this review summarizes the fields of technology and biopharmaceutical applications, where clays are applied. Copyright © 2012 Elsevier B.V. All rights reserved.
Energy Technology Data Exchange (ETDEWEB)
Vidal, Emanuella Layne Ferreira; Araujo, Bruno Alysson Barbosa Duarte; Borges, Mauricio Rodrigues; Garcia, Rosangela Balaban [Universidade Federal do Rio Grande do Norte (UFRN), Natal, RN (Brazil)
2008-07-01
During the drilling, in general, there are layers of clays which water absorption easily as smectites. In drilling with clays swelling when is applied water-base fluid there is necessary the use of the clay inhibitors to avoid the incorporation of the cutting to the drilling fluid. The most used chemical inhibitors in drilling fluids are sodium and potassium chlorides. However, the cationic inhibitors have been used as alternative form to increase the inhibition power of the drilling fluids. In this work was evaluated the behaviour of the activated clay test bodies in the presence of distilled water, aqueous solution potassium chlorides, and cationic inhibitors. The solutions were submitted at Capillary Suction Timer tests to evaluation the capacity of the water retention in activated clay samples. At the interpretation of the results was used Design of Experiments (DOE) by Response Surface Methodology (RSM), using Umetrics MODDE 7.0{sup TM} programme. It was observed that the clay samples when in contact with the solutions presented lower water retention than in the presence of distilled water only. This result indicates that the clay was inhibited. (author)
International Nuclear Information System (INIS)
Moore, D.E.; Morrow, C.A.; Byerlee, J.D.
1982-01-01
The injection of swelling-clay slurries into joints or faults at a deep-burial nuclear waste disposal site may result in signficant permeability reductions for the effective containment of radioactive wastes. In an experiment conducted to illustrate the permeability change accompanying clay swelling, a coarse stone with interconnected pore spaces was injected with a clay-electrolyte slurry, modelling the pressure-grouting of a fractured repository rock. Subsequently, solutions with lower electroylte concentrations were driven through the clay-filled stone, corresponding to migration of lower salinity ground-waters through the clay-grouted fracture. The initial injection procedure reduced the permeability of the stone from 1--10 darcies to 700 nanodarcies; the changes in solution composition decreased permeability by more than 2 additional orders of magnitude to 3 nanodarcies. For application at a nuclear waste repository, the electrolyte concentration of the injected clay slurry should be made higher than that of the ground-water in the host rock. Subesquent interaction of the ground-water with the clays would initiate swelling and create the additional, post-injection permeability reductions that may be important in preventing the escape of buried radioactive wastes. The measured permeability of the clay filling is considerably lower than that of cement tested for borehole plugging. Clays also have the advantage over cement and chemical grouts in that they are geologically stable at relatively low temperatures and have a high capacity for radionuclide adsorption
Quality evaluation of processed clay soil samples.
Steiner-Asiedu, Matilda; Harrison, Obed Akwaa; Vuvor, Frederick; Tano-Debrah, Kwaku
2016-01-01
This study assessed the microbial quality of clay samples sold on two of the major Ghanaian markets. The study was a cross-sectional assessing the evaluation of processed clay and effects it has on the nutrition of the consumers in the political capital town of Ghana. The items for the examination was processed clay soil samples. Staphylococcus spp and fecal coliforms including Klebsiella, Escherichia, and Shigella and Enterobacterspp were isolated from the clay samples. Samples from the Kaneshie market in Accra recorded the highest total viable counts 6.5 Log cfu/g and Staphylococcal count 5.8 Log cfu/g. For fecal coliforms, Madina market samples had the highest count 6.5 Log cfu/g and also recorded the highest levels of yeast and mould. For Koforidua, total viable count was highest in the samples from the Zongo market 6.3 Log cfu/g. Central market samples had the highest count of fecal coliforms 4.6 Log cfu/g and yeasts and moulds 6.5 Log cfu/g. "Small" market recorded the highest staphylococcal count 6.2 Log cfu/g. The water activity of the clay samples were low, and ranged between 0.65±0.01 and 0.66±0.00 for samples collected from Koforidua and Accra respectively. The clay samples were found to contain Klebsiella spp. Escherichia, Enterobacter, Shigella spp. staphylococcus spp., yeast and mould. These have health implications when consumed.
Characterization and evaluation of ceramic properties of clay used in structural ceramics
International Nuclear Information System (INIS)
Savazzini-Reis, A.; Della-Sagrillo, V.P.; Valenzuela-Diaz, F.R.
2016-01-01
The Brazilian red ceramic industry monthly consumes about 10.3 million tons of clay, its main raw material. In most potteries, characterization of the clay is made empirically, which can result in tiles and blocks not according to standards. This sense, this paper aims to characterize clays used in the manufacturing of red ceramic products in factory located in Colatina-ES, which appears as a ceramic pole with about twenty small and midsize industries. The clays were characterized by: Xray fluorescence, X-ray diffraction, thermal analysis (TG/DSC), granulometry and Atterberg limits. Specimens of clay and mixture containing four clays were shaped. Specimens were shaped, dried at 110°C, and burned in a kiln for 24 h. The ceramics and mechanical characteristics were evaluated: flexural strength, water absorption, apparent porosity, apparent specific mass and shrinkage by drying and firing. The characterization showed that kaolinitic clay presents high plasticity, but high porosity. The mixture formed by the four clays does not meet the requirements of the Brazilian standard clays for red ceramic. (author)
Spears, B.M.; Lürling, M.F.L.L.W.; Yasseri, S.; Castro-Castellon, A.T.; Gibbs, M.; Meis, S.; McDonald, C.; McIntosh, J.; Sleep, D.; Oosterhout, van F.
2013-01-01
Phoslock is a lanthanum (La) modified bentonite clay that is being increasingly used as a geo-engineering tool for the control of legacy phosphorus (P) release from lake bed sediments to overlying waters. This study investigates the potential for negative ecological impacts from elevated La
Impact of monovalent cations on soil structure. Part I. Results of an Iranian soil
Farahani, Elham; Emami, Hojat; Keller, Thomas; Fotovat, Amir; Khorassani, Reza
2018-01-01
This study investigated the impact of monovalent cations on clay dispersion, aggregate stability, soil pore size distribution, and saturated hydraulic conductivity on agricultural soil in Iran. The soil was incubated with treatment solutions containing different concentrations (0-54.4 mmol l-1) of potassium and sodium cations. The treatment solutions included two levels of electrical conductivity (EC=3 or 6 dS m-1) and six K:Na ratios per electrical conductivity level. At both electrical conductivity levels, spontaneously dispersible clay increased with increasing K concentration, and with increasing K:Na ratio. A negative linear relationship between percentage of water-stable aggregates and spontaneously dispersible clay was observed. Clay dispersion generally reduced the mean pore size, presumably due to clogging of pores, resulting in increased water retention. At both electrical conductivity levels, hydraulic conductivity increased with increasing exchangeable potassium percentage at low exchangeable potassium percentage values, but decreased with further increases in exchangeable potassium percentage at higher exchangeable potassium percentage. This is in agreement with earlier studies, but seems in conflict with our data showing increasing spontaneously dispersible clay with increasing exchangeable potassium percentage. Our findings show that clay dispersion increased with increasing K concentration and increasing K:Na ratio, demonstrating that K can have negative impacts on soil structure.
Influence of clay particles on microfluidic-based preparation of hydrogel composite microsphere
Hong, Joung Sook
2016-05-01
For the successful fabrication of a hydrogel composite microsphere, this study aimed to investigate the influence of clay particles on microsphere formation in a microfluidic device which has flow focusing and a 4.5:1 contraction channel. A poly alginic acid solution (2.0 wt.%) with clay particles was used as the dispersed phase to generate drops in an oil medium, which then merged with drops of a CaCl2 solution for gelation. Drop generations were observed with different flow rates and particles types. When the flow rate increased, drop generation was enhanced and drop size decreased by the build-up of more favorable hydrodynamic flow conditions to detach the droplets. The addition of a small amount of particles insignificantly changed the drop generation behavior even though it reduced interfacial tension and increased the viscosity of the solution. Instead, clays particles significantly affected hydro-gelation depending on the hydrophobicity of particles, which produced further heterogeneity in the shape and size of microsphere.
Energy Technology Data Exchange (ETDEWEB)
Silva, A.A. [Universidade Federal de Campina Grande (UFCG), PB (Brazil). Engenharia de Processos], email: adriana_anp@yahoo.com.br; Pereira, K.R de O.; Wiebeck, H.; Valenzuela-Diaz, F.R. [Universidade de Sao Paulo (EPUSP), SP (Brazil). Escola Politecnica. Dept. de Engenharia Metalurgica e de Materiais; Rodrigues, M. G.F. [Universidade Federal de Campina Grande (UFCG), PB (Brazil). CCT. Dept. de Engenharia Quimica
2006-07-01
Water mixed with oil is produced in great volume in industrial processes and in petroleum refineries. This mixture must be treated to return to environment or can be reused in the same process. The refine of this water is expensive and presents a difficult execution. The process of separation of oil in water used organophilic clays can be a new option. In this work, the process of preparation of organophilic clays using smectitic clay polycationic and a industrial sodium bentonite both from Paraiba State, Brazil is described. The samples were characterized by two techniques: X-ray Diffraction and Thermal Analysis. After preparation of the organophilic clays it was determined theirs swelling in organic solvents and oil adsorption capacity. The organophilic clays presented higher capacity of oil adsorption when compared to activated carbon. (author)
Modifying Silicates for Better Dispersion in Nanocomposites
Campbell, Sandi
2005-01-01
An improved chemical modification has been developed to enhance the dispersion of layered silicate particles in the formulation of a polymer/silicate nanocomposite material. The modification involves, among other things, the co-exchange of an alkyl ammonium ion and a monoprotonated diamine with interlayer cations of the silicate. The net overall effects of the improved chemical modification are to improve processability of the nanocomposite and maximize the benefits of dispersing the silicate particles into the polymer. Some background discussion is necessary to give meaning to a description of this development. Polymer/silicate nanocomposites are also denoted polymer/clay composites because the silicate particles in them are typically derived from clay particles. Particles of clay comprise layers of silicate platelets separated by gaps called "galleries." The platelet thickness is 1 nm. The length varies from 30 nm to 1 m, depending on the silicate. In order to fully realize the benefits of polymer/silicate nanocomposites, it is necessary to ensure that the platelets become dispersed in the polymer matrices. Proper dispersion can impart physical and chemical properties that make nanocomposites attractive for a variety of applications. In order to achieve nanometer-level dispersion of a layered silicate into a polymer matrix, it is typically necessary to modify the interlayer silicate surfaces by attaching organic functional groups. This modification can be achieved easily by ion exchange between the interlayer metal cations found naturally in the silicate and protonated organic cations - typically protonated amines. Long-chain alkyl ammonium ions are commonly chosen as the ion-exchange materials because they effectively lower the surface energies of the silicates and ease the incorporation of organic monomers or polymers into the silicate galleries. This completes the background discussion. In the present improved modification of the interlayer silicate surfaces
R7T7 nuclear waste glass behavior in moist clay: role of the clay mass/glass surface area ratio
International Nuclear Information System (INIS)
Godon, N.; Vernaz, E.
1989-01-01
R7T7 glass alteration was investigated in the presence of various moist clays. In contact with smectite 4a, selected in France as a potential engineered barrier material, the glass was significantly corroded: after 6 months the glass corrosion rate was practically the same as the initial alteration rate in double-distilled water. Substantially lower alteration was observed in contact with bentonite 6 activated by sodium carbonate. Smectite 4a consumes silicon released by glass corrosion, and thus retards the rise to high silicon concentrations in solution at which the glass corrosion rate diminishes. Glass can therefore in some cases be altered as much in moist clay as in water with high renewal rates. Other experiments with smaller quantities of smectite 4a showed that the phenomenon becomes less important in time: its duration is proportional to the ratio between the clay mass (C) and the glass surface area (SA). Comparing the results of studies at different C/SA ratios indicates that low glass corrosion rates are obtained more slowly at higher C/SA ratios. Tests with 239 Pu-doped R7T7 glass also showed that the radionuclide retention factor in the alteration film at the glass surface is only 6, compared with a factor of nearly 50 in double-distilled water
CSIR Research Space (South Africa)
Neppalli, R
2014-01-01
Full Text Available In this work, polylactic acid (PLA)-based nanocomposites filled with different kinds of clay were prepared and their structure, morphology and degradation behavior were compared. A similar degree of dispersion was achieved in the case of cationic...
p-Nitrophenol, phenol and aniline sorption by organo-clays
International Nuclear Information System (INIS)
Ko, C.H.; Fan Chihhao; Chiang, P.N.; Wang, M.K.; Lin, K.C.
2007-01-01
The aims of this study were to make use of organo-clays (i.e., Cloisite-10A, Cloisite-15A, Cloisite-30B and Cloisite-93A), to remove p-nitrophenol, phenol and aniline of organic pollutants. The organo-clays were characterized by X-ray diffraction (XRD). Sorption isotherm, kinetic and pH effect of p-nitrophenol, phenol and aniline sorbed by four organo-clays were evaluated. The d-spacings (0 0 1) of the XRD peak of Cloisite-10A, Cloisite-15A, Cloisite-30B and Cloisite-93A are 1.98, 2.76, 1.93 and 2.64 nm, respectively. The d(0 0 1)-spacings of XRD indicated that these p-nitropheno, phenol and aniline could penetrate into the interlayer of clays and expand the d(0 0 1)-spacings. The linear sorption isotherm of constant partition was employed to describe the sorption isotherms of phenols sorbed by organo-clays through hydrophobic-hydrophobic chemical reactions. The parabolic diffusion and power-function of kinetic models were employed to describe properly the kinetic experiments. The rate limiting step of the p-nitrophenol sorption reactions on organo-clays were diffusion-controlled processes (i.e., 15A, 30B, 93A) and chemical-controlled process for 10A organo-clays. The pre-exponential factor of the p-nitrophenol sorbed by four organo-clays showed the trend as follows: 10A > 30B > 93A > 15A. The efficiency of these organo-clays in removing phenol compounds in water treatments merit further study
ADSORPTION OF ACID DYE ONTO ACTIVATED ALGERIAN CLAY ...
African Journals Online (AJOL)
In this work, activated clay from Algeria was used as adsorbent for the ... paper, cosmetics, printing, and plastics are one of the major sources of water pollution. These ..... Mohammadi, S.Z.; Shamspur, T.; Baghelani, Y.M. Combination of flame atomic absorption ... and determination of trace amount of lead in water samples.
Energy Technology Data Exchange (ETDEWEB)
Jennings, David; White, Jake; Pogoson, Oje [Baker Hughes Inc., Houston, TX (United States); Barros, Dalmo; Ramachandran, Kartik; Bonin, George; Waltrich, Paulo; Shecaira, Farid [PETROBRAS America, Houston, TX (United States); Ziglio, Claudio [Petroleo Brasileiro S.A. (CENPES/PETROBRAS), Rio de Janeiro, RJ (Brazil). Centro de Pesquisa e Desenvolvimento
2012-07-01
This paper discusses a paraffin dispersant (in seawater) application to clean paraffin deposition from a severely restricted 17.4-mile dual subsea flow line system in the Gulf of Mexico Cottonwood development. In principle, dispersant treatments are simple processes requiring effective dispersant packages and agitation to break-up and disperse deposition. Dispersants have been used onshore for treating wax deposition for decades. Implementation of a treatment in a long deep water production system, however, poses numerous challenges. The Cottonwood application was one of the first ever deep water dispersant applications. The application was designed in four separate phases: pre-treatment displacement for hydrate protection, dispersant treatment for paraffin deposition removal, pigging sequence for final flow line cleaning, and post-treatment displacement for hydrate protection. In addition, considerable job planning was performed to ensure the application was executed in a safe and environmentally responsible manner. Two dynamically positioned marine vessels were used for pumping fluids and capturing returns. The application was extremely successful in restoring the deep water flow lines back to near pre-production state. Final pigging operations confirmed the flow lines were cleaned of all restrictions. Significant paraffin deposition was removed in the application. Approximately 900 bbls of paraffin sludge was recovered from the 4000 bbl internal volume flow line loop. Furthermore, the application was completed with zero discharge of fluids. The application provided significant value for the Cottonwood development. It allowed production from wells to be brought on-line at a higher capacity, thereby generating increased revenue. It also allowed resumption of routine pigging operations. As such, the Cottonwood dispersant application illustrates that with proper planning and execution, paraffin dispersant treatments can be highly effective solutions for cleaning
Olivato, J B; Marini, J; Pollet, E; Yamashita, F; Grossmann, M V E; Avérous, L
2015-03-15
The incorporation of nano-sized sepiolite clays into thermoplastic starch/poly(butylene adipate-co-terephthalate) (TPS/PBAT) blends has been investigated with the goal of improving the matrix properties. TPS/PBAT nano-biocomposites were elaborated with two different proportions of the polymeric phases. The influence of the sepiolite nanoclays on the mechanical, thermal and structural properties of the corresponding blends was evaluated. SEM images confirmed the good dispersion of the sepiolite clay, with a low occurrence of small aggregates in the polymeric matrix. Wide-angle X-ray diffraction showed no significant alteration of the crystalline structures of PBAT and starch induced by the sepiolite clay. The addition of sepiolite slightly affected the thermal degradation of the nano-biocomposites; however, the mechanical tests revealed an increase in some mechanical properties, demonstrating that sepiolite is a promising nanofiller for TPS-based materials. Copyright © 2014 Elsevier Ltd. All rights reserved.
Chemo-hydro-mechanical behaviour of unsaturated clays
International Nuclear Information System (INIS)
Mokni, N.; Olivella, S.; Alonso, E.E.; Romero, E.
2010-01-01
Document available in extended abstract form only. Understanding of the chemical effects on clays is essential for many problems ranging from pollution studies and waste-containment. Several studies examined the effect of changes in pore fluid composition on the mechanical and hydraulic properties. Volume changes (contraction/ expansion) have been measured on clay specimens upon exposure to salt solutions or permeation with organic liquids. Moreover, it was shown that permeation of clay with brine induces an increase of the shear strength. In addition, several models have been proposed to describe the chemo-mechanical behaviour of saturated clays under saturated conditions. A new chemo-hydro-mechanical model for unsaturated clays is under development. The chemo-mechanical effects are described within an elasto-plastic framework using the concept that chemical effects act on the plastic properties by increasing or decreasing the pre-consolidation stress. The model is based on the distinction within the material of a microstructural and a macro-structural levels. Chemical loading has a significant effect on the microstructure. The negative pressure associated with the capillary water plays its role in the interconnected macro pores. By adopting simple assumptions concerning the coupling between the two levels it is intended to reproduce the features of the behaviour of unsaturated clays when there is a change in pore fluid composition (increase or decrease of concentration). A yield surface which defines the set of yield pre-consolidation stress values, for each associated capillary suction and concentration of pore fluid should be defined. In addition, the behaviour of clays under unsaturated condition and the behaviour at full saturation under chemical loading represent two limiting cases of the framework. Studies on the compatibility of Boom Clay with large amounts of nitrate- bearing bituminized radioactive waste have recently raised a particular interest on the
Processes of cation migration in clay-rocks: Final Scientific Report of the CatClay European Project
International Nuclear Information System (INIS)
Altmann, S.; Aertsens, M.; Appelo, T.; Bruggeman, C.; Gaboreau, S.; Glaus, M.; Jacquier, P.; Kupcik, T.; Maes, N.; Montoya, V.; Rabung, T.; Robinet, J.-C.; Savoye, S.; Schaefer, T.; Tournassat, C.; Van Laer, L.; Van Loon, L.
2015-07-01
illite and clay rocks, even though some assumptions made have to be verified. In parallel, actual 3D geometrical pore size distributions of compacted illite, and in less extent, clay rock samples, were successfully determined by combining TEM and FIB-nt analyses on materials maintained in a water-like saturation state by means of an extensive impregnation step. Based on this spatial distribution of pores, first numerical diffusion experiments were carried at the pore scale through virtual illite, enabling a better understanding of how transfer pathways are organized in the porous media. Finally, the EC CatClay project allowed a better understanding of the migration of strongly sorbing tracers through low permeability 'clay rock' formations, increasing confidence in our capacity to demonstrate that the models used to predict radionuclide migration through these rocks are scientifically sound. (authors)
Characterization of karak clay from pakistan for pharmaceutical and cosmetic applications
International Nuclear Information System (INIS)
Shah, L.A.; Silva-Valenzuela, M.G.; Valenzuela-Diaz, F.R.; Sayeg, I.J.; Carvalho, F.M.S.
2012-01-01
Full text: Clay, the most important, plentiful, and low cost naturally occurring mineral, is widely used in variety of industrial application including Pharmaceutical and cosmetic. Clay is the fine grained aluminosilicate mineral which shows the property of plasticity at appropriate water content, and becomes hard upon drying. In Pakistan there are different types of clay but till now neither of them properly identified nor characterize for specific industrial application. The objective of this work is to characterize Karak clay for pharmaceutical and cosmetic applications collected from deposit located at Shagai region, District Karak, Pakistan. The clay was characterized through Xray diffractometry (XRD), X-ray Fluorescence (XRF), trace elemental Analysis, Microbiological analysis, Cation exchange capacity (CEC), pH and swelling assays according to European, United States of America and Brazilian Pharmacopeias. Bulk Chemical analysis shows that the Aluminum oxide and silica oxide are present in large quantity which was confirmed by XRD that this sample has montmorillonite as a major while illite and kaolinite as minor clay minerals. Quartz of small quantity was also found as a non-clay mineral. After analyzing the results for sample it was concluded that the clay is a strong candidate for cosmetic purposes. (author)