  1. Magnetic x-ray linear dichroism of ultrathin Fe-Ni alloy films

    Energy Technology Data Exchange (ETDEWEB)

    Schumann, F.O.; Willis, R.F. [Pennsylvania State Univ., University Park, PA (United States); Goodman, K.W. [Lawrence Berkeley National Lab., CA (United States)] [and others

    1997-04-01

    The authors have studied the magnetic structure of ultrathin Fe-Ni alloy films as a function of Fe concentration by measuring the linear dichroism of the 3p-core levels in angle-resolved photoemission spectroscopy. The alloy films, grown by molecular-beam epitaxy on Cu(001) surfaces, were fcc and approximately four monolayers thick. The intensity of the Fe dichroism varied with Fe concentration, with larger dichroisms at lower Fe concentrations. The implication of these results to an ultrathin film analogue of the bulk Invar effect in Fe-Ni alloys will be discussed. These measurements were performed at the Spectromicroscopy Facility (Beamline 7.0.1) of the Advanced Light Source.

  2. Manipulating magnetic anisotropy of the ultrathin Co{sub 2}FeAl full-Heusler alloy film via growth orientation of the Pt buffer layer

    Energy Technology Data Exchange (ETDEWEB)

    Wen, F.S., E-mail: wenfsh03@126.com [State Key Lab of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Xiang, J.Y.; Hao, C.X.; Zhang, F.; Lv, Y.F. [State Key Lab of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China); Wang, W.H. [Institute of Physics, Chinese Academy of Science, Beijing 100080 (China); Hu, W.T.; Liu, Z.Y. [State Key Lab of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China)

    2013-12-15

    The ultrathin films of Co{sub 2}FeAl (CFA) full-Heusler alloy were prepared between two Pt layers on MgO single crystals by magnetron sputtering. By controlling the substrate temperature, different growth orientations of the Pt underlayers were realized, and their effects were investigated on the magnetic anisotropy of the ultrathin CFA film. It was revealed that different Pt orientations lead to distinctly different magnetic anisotropy for the sandwiched ultrathin CFA films. The Pt (111) orientation favors the perpendicular anisotropy, while the appearance of partial Pt (001) orientation leads to the quick decrease of perpendicular anisotropy and the complete Pt (001) orientation gives rise to the in-plane anisotropy. With the Pt (111) orientation, the temperature and thickness-induced spin reorientation transitions were investigated in the sandwiched ultrathin CFA films. - Highlights: • Different Pt orientations lead to different magnetic anisotropy for sandwiched ultrathin CFA films. • The Pt (111) orientation favors the perpendicular anisotropy for CFA layer. • Temperature and thickness-induced spin reorientation transitions were investigated in sandwiched ultrathin CFA films. • 0.8 nm CFA film is good candidate as electrode in magnetic tunnel junctions.

  3. Manipulating magnetic anisotropy of the ultrathin Co2FeAl full-Heusler alloy film via growth orientation of the Pt buffer layer

    International Nuclear Information System (INIS)

    Wen, F.S.; Xiang, J.Y.; Hao, C.X.; Zhang, F.; Lv, Y.F.; Wang, W.H.; Hu, W.T.; Liu, Z.Y.

    2013-01-01

    The ultrathin films of Co 2 FeAl (CFA) full-Heusler alloy were prepared between two Pt layers on MgO single crystals by magnetron sputtering. By controlling the substrate temperature, different growth orientations of the Pt underlayers were realized, and their effects were investigated on the magnetic anisotropy of the ultrathin CFA film. It was revealed that different Pt orientations lead to distinctly different magnetic anisotropy for the sandwiched ultrathin CFA films. The Pt (111) orientation favors the perpendicular anisotropy, while the appearance of partial Pt (001) orientation leads to the quick decrease of perpendicular anisotropy and the complete Pt (001) orientation gives rise to the in-plane anisotropy. With the Pt (111) orientation, the temperature and thickness-induced spin reorientation transitions were investigated in the sandwiched ultrathin CFA films. - Highlights: • Different Pt orientations lead to different magnetic anisotropy for sandwiched ultrathin CFA films. • The Pt (111) orientation favors the perpendicular anisotropy for CFA layer. • Temperature and thickness-induced spin reorientation transitions were investigated in sandwiched ultrathin CFA films. • 0.8 nm CFA film is good candidate as electrode in magnetic tunnel junctions

  4. Ag-related alloy formation and magnetic phases for Ag/Co/Ir(111) ultrathin films

    International Nuclear Information System (INIS)

    Tsay, Jyh-Shen; Tsai, Du-Cheng; Chang, Cheng-Hsun-Tony; Chen, Wei-Hsiang

    2013-01-01

    The Kerr intensity versus the Ag thickness for Ag grown on the top of Co/Ir(111) exhibits an oscillating behavior with a period around one monolayer which should be due to the morphological change related electronic structure differences of the Ag layer. From systematical investigations of Ag/Co/Ir(111) films with the Co layer thinner than 4 monolayers at temperatures below 900 K, a magnetic phase diagram has been established. As the annealing temperature increases for Ag/Co/Ir(111) films, enhancements of the coercive force occur in both the polar and longitudinal configurations due to the intermixing of Ag and Co at the interface and the formation of Co–Ir alloy. The disappearance of ferromagnetism is mainly attributed to the reduced atomic percent of cobalt in Co–Ir alloy, the lowered Curie temperature by a reduction of the thickness of magnetic layers, and the intermixing of Ag and Co at the Ag/Co interface. - Highlights: • An oscillating behavior occurs due to the morphological change for Ag on Co/Ir(111). • A magnetic phase diagram has been established for Ag/Co/Ir(111). • Some Ag atoms intermix with the underlying Co layer at high temperatures. • Polar coercive force is enhanced due to the compositional change

  5. Individual Magnetic Molecules on Ultrathin Insulating Surfaces

    Science.gov (United States)

    El Hallak, Fadi; Warner, Ben; Hirjibehedin, Cyrus

    2012-02-01

    Single molecule magnets have attracted ample interest because of their exciting magnetic and quantum properties. Recent studies have demonstrated that some of these molecules can be evaporated on surfaces without losing their magnetic properties [M. Mannini et al., Nature 468, 417, (2010)]. This remarkable progress enhances the chances of real world applications for these molecules. We present STM imaging and spectroscopy data on iron phthalocyanine molecules deposited on Cu(100) and on a Cu2N ultrathin insulating surface. These molecules have been shown to display a large magnetic anisotropy on another thin insulating surface, oxidized Cu(110) [N. Tsukahara et al., Phys. Rev. Lett. 102, 167203 (2009)]. By using a combination of elastic and inelastic electron tunnelling spectroscopy, we investigate the binding of the molecules to the surface and the impact that the surface has on their electronic and magnetic properties.

  6. Elementary spin excitations in ultrathin itinerant magnets

    Energy Technology Data Exchange (ETDEWEB)

    Zakeri, Khalil, E-mail: zakeri@mpi-halle.de

    2014-12-10

    Elementary spin excitations (magnons) play a fundamental role in condensed matter physics, since many phenomena e.g. magnetic ordering, electrical (as well as heat) transport properties, ultrafast magnetization processes, and most importantly electron/spin dynamics can only be understood when these quasi-particles are taken into consideration. In addition to their fundamental importance, magnons may also be used for information processing in modern spintronics. Here the concept of spin excitations in ultrathin itinerant magnets is discussed and reviewed. Starting with a historical introduction, different classes of magnons are introduced. Different theoretical treatments of spin excitations in solids are outlined. Interaction of spin-polarized electrons with a magnetic surface is discussed. It is shown that, based on the quantum mechanical conservation rules, a magnon can only be excited when a minority electron is injected into the system. While the magnon creation process is forbidden by majority electrons, the magnon annihilation process is allowed instead. These fundamental quantum mechanical selection rules, together with the strong interaction of electrons with matter, make the spin-polarized electron spectroscopies as appropriate tools to excite and probe the elementary spin excitations in low-dimensional magnets e.g ultrathin films and nanostructures. The focus is put on the experimental results obtained by spin-polarized electron energy loss spectroscopy and spin-polarized inelastic tunneling spectroscopy. The magnon dispersion relation, lifetime, group and phase velocity measured using these approaches in various ultrathin magnets are discussed in detail. The differences and similarities with respect to the bulk excitations are addressed. The role of the temperature, atomic structure, number of atomic layers, lattice strain, electronic complexes and hybridization at the interfaces are outlined. A possibility of simultaneous probing of magnons and phonons

  7. Ultra-thin zirconia films on Zr-alloys

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Joong Il Jake; Mayr-Schmoelzer, Wernfried; Mittendorfer, Florian; Redinger, Josef; Diebold, Ulrike; Schmid, Michael [Institute of Applied Physics, Vienna University of Technology (Austria); Li, Hao; Rupprechter, Guenther [Institute of Materials Chemistry, Vienna University of Technology (Austria)

    2014-07-01

    Zirconia ultra-thin films have been prepared by oxidation of Pt{sub 3}Zr(0001) and showed a structure equivalent to (111) of cubic zirconia. Following previous work, we have prepared ultra-thin zirconia by oxidation of a different alloy, Pd{sub 3}Zr(0001), which resulted in a similar structure with a slightly different lattice parameter, 351.2 ±0.4 pm. Unlike the oxide on Pt{sub 3}Zr, where Zr of the oxide binds to Pt in the substrate, here the oxide binds to substrate Zr via oxygen. This causes stronger distortion of the oxide structure, i.e. a stronger buckling of Zr in the oxide. After additional oxidation of ZrO{sub 2}/Pt{sub 3}Zr, a different ultra-thin zirconia phase is observed. A preliminary structure model for this film is based on (113)-oriented cubic zirconia. 3D oxide clusters are also present after growing ultra-thin zirconia films. They occur at the step edges, and the density is higher on Pd{sub 3}Zr. These clusters also appear on terraces after additional oxidation. XPS reveals different core level shifts of the oxide films, bulk, and oxide clusters.

  8. Ultrathin magnetic structures II measurement techniques and novel magnetic properties

    CERN Document Server

    Heinrich, Bretislav

    2006-01-01

    The ability to understand and control the unique properties of interfaces has created an entirely new field of magnetism, with profound impact in technology and serving as the basis for a revolution in electronics. Our understanding of the physics of magnetic nanostructures has also advanced significantly. This rapid development has generated a need for a comprehensive treatment that can serve as an introduction to the field for those entering it from diverse fields, but which will also serve as a timely overview for those already working in this area. The four-volume work Ultra-Thin Magnetic

  9. Ultrathin Interface Regime of Core-Shell Magnetic Nanoparticles for Effective Magnetism Tailoring.

    Science.gov (United States)

    Moon, Seung Ho; Noh, Seung-Hyun; Lee, Jae-Hyun; Shin, Tae-Hyun; Lim, Yongjun; Cheon, Jinwoo

    2017-02-08

    The magnetic exchange coupling interaction between hard and soft magnetic phases has been important for tailoring nanoscale magnetism, but spin interactions at the core-shell interface have not been well studied. Here, we systematically investigated a new interface phenomenon termed enhanced spin canting (ESC), which is operative when the shell thickness becomes ultrathin, a few atomic layers, and exhibits a large enhancement of magnetic coercivity (H C ). We found that ESC arises not from the typical hard-soft exchange coupling but rather from the large magnetic surface anisotropy (K S ) of the ultrathin interface. Due to this large increase in magnetism, ultrathin core-shell nanoparticles overreach the theoretical limit of magnetic energy product ((BH) max ) and exhibit one of the largest values of specific loss power (SLP), which testifies to their potential capability as an effective mediator of magnetic energy conversion.

  10. Electronic and magnetic properties of ultrathin rhodium nanowires

    CERN Document Server

    Wang Bao Lin; Ren-Yun; Sun Hou Qian; Chen Xiao Shuang; Zhao Ji Jun

    2003-01-01

    The structures of ultrathin rhodium nanowires are studied using empirical molecular dynamics simulations with a genetic algorithm. Helical multishell cylindrical and pentagonal packing structures are found. The electronic and magnetic properties of the rhodium nanowires are calculated using an spd tight-binding Hamiltonian in the unrestricted Hartree-Fock approximation. The average magnetic moment and electronic density of states are obtained. Our results indicate that the electronic and magnetic properties of the rhodium nanowires depend not only on the size of the wire but also on the atomic structure. In particular, centred pentagonal and hexagonal structures can be unusually ferromagnetic.

  11. Ultrathin magnetic structures IV applications of nanomagnetism

    CERN Document Server

    Heinrich, Bretislav

    2004-01-01

    The ability to understand and control the unique properties of interfaces has created an entirely new field of magnetism which already has a profound impact in technology and is providing the basis for a revolution in electronics. The last decade has seen dramatic progress in the development of magnetic devices for information technology but also in the basic understanding of the physics of magnetic nanostructures. Volume III describes thin film magnetic properties and methods for characterising thin film structure topics that underpin the present 'spintronics' revolution in which devices are based on combined magnetic materials and semiconductors. The present volume (IV) deals with the fundamentals of spintronics: magnetoelectronic materials, spin injection and detection, micromagnetics and the development of magnetic random access memory based on GMR and tunnel junction devices. Together these books provide readers with a comprehensive account of an exciting and rapidly developing field. The treatment is de...

  12. Ultrathin magnetic structures III fundamentals of nanomagnetism

    CERN Document Server

    Bland, JAC

    2004-01-01

    The ability to understand and control the unique properties of interfaces has created an entirely new field of magnetism which already has a profound impact in technology and is providing the basis for a revolution in electronics. The last decade has seen dramatic progress in the development of magnetic devices for information technology but also in the basic understanding of the physics of magnetic nanostructures. This volume describes thin film magnetic properties and methods for characterising thin film structure topics that underpin the present 'spintronics' revolution in which devices are based on combined magnetic materials and semiconductors. Volume IV deals with the fundamentals of spintronics: magnetoelectronic materials, spin injection and detection, micromagnetics and the development of magnetic random access memory based on GMR and tunnel junction devices. Together these books provide readers with a comprehensive account of an exciting and rapidly developing field. The treatment is designed to be ...

  13. Magnetic anisotropies in ultrathin bismuth iron garnet films

    International Nuclear Information System (INIS)

    Popova, Elena; Franco Galeano, Andres Felipe; Deb, Marwan; Warot-Fonrose, Bénédicte; Kachkachi, Hamid; Gendron, François; Ott, Frédéric

    2013-01-01

    Ultrathin bismuth iron garnet Bi 3 Fe 5 O 12 films were grown epitaxially on (001)-oriented gadolinium gallium garnet substrates. Film thickness varied from two to three dozens of unit cells. Bi 3 Fe 5 O 12 films grow pseudomorphically on substrates up to a thickness of 20 nm, and then a lattice relaxation occurs. Magnetic properties of the films were studied as a function of bismuth iron garnet thickness. The magnetization and cubic anisotropy decrease with decreasing film thickness. The uniaxial magnetocrystalline anisotropy is constant for all film thicknesses. For two unit cell thick films, the easy magnetization axis changes from in-plane to perpendicular to the plane direction. Such a reorientation takes place as a result of the competition of constant uniaxial perpendicular anisotropy with weakening film magnetization. - Highlights: ► Ultrathin Bi 3 Fe 5 O 12 films were grown epitaxially on structure-matching substrates. ► Magnetic properties of Bi 3 Fe 5 O 12 were studied down to the thickness of 2.5 nm. ► Reorientation of easy magnetization axis as a function of film thickness was observed

  14. Magnetic anisotropies in ultrathin bismuth iron garnet films

    Energy Technology Data Exchange (ETDEWEB)

    Popova, Elena, E-mail: popova@physique.uvsq.fr [Groupe d' Etude de la Matière Condensée (GEMaC), CNRS/Université de Versailles-Saint-Quentin, 45 Avenue des Etats-Unis, 78035 Versailles (France); Franco Galeano, Andres Felipe [Laboratoire PROcédés, Matériaux et Energie Solaire (PROMES), CNRS/Université de Perpignan Via Domitia, 52 Avenue Paul Alduy, 66860 Perpignan (France); Deb, Marwan [Groupe d' Etude de la Matière Condensée (GEMaC), CNRS/Université de Versailles-Saint-Quentin, 45 Avenue des Etats-Unis, 78035 Versailles (France); Warot-Fonrose, Bénédicte [Centre d' Elaboration de Matériaux et d' Etudes Structurales (CEMES), CNRS, 29 rue Jeanne Marvig, 31055 Toulouse (France); Transpyrenean Associated Laboratory for Electron Microscopy (TALEM), CEMES-INA, CNRS–Universidad de Zaragoza (Spain); Kachkachi, Hamid [Laboratoire PROcédés, Matériaux et Energie Solaire (PROMES), CNRS/Université de Perpignan Via Domitia, 52 Avenue Paul Alduy, 66860 Perpignan (France); Gendron, François [Institut des NanoSciences de Paris (INSP), CNRS/Université Pierre et Marie Curie-Paris 6, 4 place Jussieu, Boîte courrier 840, 75252 Paris Cedex 05 (France); Ott, Frédéric [Laboratoire Léon Brillouin (LLB), CNRS/CEA, Bâtiment 563, CEA Saclay, 91191 Gif sur Yvette Cedex (France); and others

    2013-06-15

    Ultrathin bismuth iron garnet Bi{sub 3}Fe{sub 5}O{sub 12} films were grown epitaxially on (001)-oriented gadolinium gallium garnet substrates. Film thickness varied from two to three dozens of unit cells. Bi{sub 3}Fe{sub 5}O{sub 12} films grow pseudomorphically on substrates up to a thickness of 20 nm, and then a lattice relaxation occurs. Magnetic properties of the films were studied as a function of bismuth iron garnet thickness. The magnetization and cubic anisotropy decrease with decreasing film thickness. The uniaxial magnetocrystalline anisotropy is constant for all film thicknesses. For two unit cell thick films, the easy magnetization axis changes from in-plane to perpendicular to the plane direction. Such a reorientation takes place as a result of the competition of constant uniaxial perpendicular anisotropy with weakening film magnetization. - Highlights: ► Ultrathin Bi{sub 3}Fe{sub 5}O{sub 12} films were grown epitaxially on structure-matching substrates. ► Magnetic properties of Bi{sub 3}Fe{sub 5}O{sub 12} were studied down to the thickness of 2.5 nm. ► Reorientation of easy magnetization axis as a function of film thickness was observed.

  15. Grindability of dental magnetic alloys.

    Science.gov (United States)

    Hayashi, Eisei; Kikuchi, Masafumi; Okuno, Osamu; Kimura, Kohei

    2005-06-01

    In this study, the grindability of cast magnetic alloys (Fe-Pt-Nb magnetic alloy and magnetic stainless steel) was evaluated and compared with that of conventional dental casting alloys (Ag-Pd-Au alloy, Type 4 gold alloy, and cobalt-chromium alloy). Grindability was evaluated in terms of grinding rate (i.e., volume of metal removed per minute) and grinding ratio (i.e., volume ratio of metal removed compared to wheel material lost). Solution treated Fe-Pt-Nb magnetic alloy had a significantly higher grinding rate than the aged one at a grinding speed of 750-1500 m x min(-1). At 500 m x min(-1), there were no significant differences in grinding rate between solution treated and aged Fe-Pt-Nb magnetic alloys. At a lower speed of 500 m x min(-1) or 750 m x min(-1), it was found that the grinding rates of aged Fe-Pt-Nb magnetic alloy and stainless steel were higher than those of conventional casting alloys.

  16. Rare earth metal alloy magnets

    International Nuclear Information System (INIS)

    Harris, I.R.; Evans, J.M.; Nyholm, P.S.

    1979-01-01

    This invention relates to rare earth metal alloy magnets and to methods for their production. The technique is based on the fact that rare earth metal alloys (for e.g. cerium or yttrium) which have been crumbled to form a powder by hydride formation and decomposition can be used for the fabrication of magnets without the disadvantages inherent in alloy particle size reduction by mechanical milling. (UK)

  17. Spin-Swapping Transport and Torques in Ultrathin Magnetic Bilayers

    KAUST Repository

    Saidaoui, Hamed Ben Mohamed; Manchon, Aurelien

    2016-01-01

    Planar spin transport in disordered ultrathin magnetic bilayers comprising a ferromagnet and a normal metal (typically used for spin pumping, spin Seebeck and spin-orbit torque experiments) is investigated theoretically. Using a tight-binding model that puts the extrinsic spin Hall effect and spin swapping on equal footing, we show that the nature of spin-orbit coupled transport dramatically depends on the ratio between the layer thickness d and the mean free path λ. While the spin Hall effect dominates in the diffusive limit (d≫λ), spin swapping dominates in the Knudsen regime (d≲λ). A remarkable consequence is that spin swapping induces a substantial fieldlike torque in the Knudsen regime.

  18. Spin-Swapping Transport and Torques in Ultrathin Magnetic Bilayers

    KAUST Repository

    Saidaoui, Hamed Ben Mohamed

    2016-07-12

    Planar spin transport in disordered ultrathin magnetic bilayers comprising a ferromagnet and a normal metal (typically used for spin pumping, spin Seebeck and spin-orbit torque experiments) is investigated theoretically. Using a tight-binding model that puts the extrinsic spin Hall effect and spin swapping on equal footing, we show that the nature of spin-orbit coupled transport dramatically depends on the ratio between the layer thickness d and the mean free path λ. While the spin Hall effect dominates in the diffusive limit (d≫λ), spin swapping dominates in the Knudsen regime (d≲λ). A remarkable consequence is that spin swapping induces a substantial fieldlike torque in the Knudsen regime.

  19. Magnetic x-ray dichroism in ultrathin epitaxial films

    Energy Technology Data Exchange (ETDEWEB)

    Tobin, J.G.; Goodman, K.W. [Lawrence Berkeley National Lab., CA (United States); Cummins, T.R. [Univ. of Missouri, Rolla, MO (United States)] [and others

    1997-04-01

    The authors have used Magnetic X-ray Linear Dichroism (MXLD) and Magnetic X-ray Circular Dichroism (MXCD) to study the magnetic properties of epitaxial overlayers in an elementally specific fashion. Both MXLD and MXCD Photoelectron Spectroscopy were performed in a high resolution mode at the Spectromicroscopy Facility of the ALS. Circular Polarization was obtained via the utilization of a novel phase retarder (soft x-ray quarter wave plate) based upon transmission through a multilayer film. The samples were low temperature Fe overlayers, magnetic alloy films of NiFe and CoNi, and Gd grown on Y. The authors results include a direct comparison of high resolution angle resolved Photoelectron Spectroscopy performed in MXLD and MXCD modes as well as structural studies with photoelectron diffraction.

  20. Magnetic x-ray dichroism in ultrathin epitaxial films

    International Nuclear Information System (INIS)

    Tobin, J.G.; Goodman, K.W.; Cummins, T.R.

    1997-01-01

    The authors have used Magnetic X-ray Linear Dichroism (MXLD) and Magnetic X-ray Circular Dichroism (MXCD) to study the magnetic properties of epitaxial overlayers in an elementally specific fashion. Both MXLD and MXCD Photoelectron Spectroscopy were performed in a high resolution mode at the Spectromicroscopy Facility of the ALS. Circular Polarization was obtained via the utilization of a novel phase retarder (soft x-ray quarter wave plate) based upon transmission through a multilayer film. The samples were low temperature Fe overlayers, magnetic alloy films of NiFe and CoNi, and Gd grown on Y. The authors results include a direct comparison of high resolution angle resolved Photoelectron Spectroscopy performed in MXLD and MXCD modes as well as structural studies with photoelectron diffraction

  1. Photoelectron diffraction of magnetic ultrathin films: Fe/Cu(001)

    Energy Technology Data Exchange (ETDEWEB)

    Tobin, J.G. (Lawrence Livermore National Lab., CA (USA)); Wagner, M.K. (Wisconsin Univ., Madison, WI (USA). Dept. of Chemistry); Guo, X.Q.; Tong, S.Y. (Wisconsin Univ., Milwaukee, WI (USA). Dept. of Physics)

    1991-01-03

    The preliminary results of an ongoing investigation of Fe/Cu(001) are presented here. Energy dependent photoelectron diffraction, including the spin-dependent variant using the multiplet split Fe3s state, is being used to investigate the nanoscale structures formed by near-monolayer deposits of Fe onto Cu(001). Core-level photoemission from the Fe3p and Fe3s states has been generated using synchrotron radiation as the tunable excitation source. Tentatively, a comparison of the experimental Fe3p cross section measurements with multiple scattering calculations indicates that the Fe is in a fourfold hollow site with a spacing of 3.6{Angstrom} between it and the atom directly beneath it, in the third layer. This is consistent with an FCC structure. The possibility of utilizing spin-dependent photoelectron diffraction to investigate magnetic ultrathin films will be demonstrated, using our preliminary spectra of the multiplet-split Fe3s os near-monolayer Fe/Cu(001). 18 refs., 10 figs.

  2. Descriptipn of giant changes of domain sizes in ultrathin magnetic films

    Czech Academy of Sciences Publication Activity Database

    Kisielewski, M.; Maziewski, A.; Zablotskyy, Vitaliy A.

    2004-01-01

    Roč. 282, - (2004), s. 39-43 ISSN 0304-8853 Grant - others:SCSR(PL) 4T11B 006 24 Institutional research plan: CEZ:AV0Z1010914 Keywords : magnetic domains * ultrathin films Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.031, year: 2004

  3. Magnetic structures in ultra-thin Holmium films: Influence of external magnetic field

    Energy Technology Data Exchange (ETDEWEB)

    Rodrigues, L.J. [Departamento de Física Teórica e Experimental, Universidade Federal do Rio Grande do Norte, Natal 59600-900, RN (Brazil); Departamento de Física, Universidade do Estado do Rio Grande do Norte, Mossoró 59625-620, RN (Brazil); Mello, V.D. [Departamento de Física, Universidade do Estado do Rio Grande do Norte, Mossoró 59625-620, RN (Brazil); Anselmo, D.H.A.L. [Departamento de Física Teórica e Experimental, Universidade Federal do Rio Grande do Norte, Natal 59600-900, RN (Brazil); Vasconcelos, M.S., E-mail: mvasconcelos@ect.ufrn.br [Escola de Ciência e Tecnologia, Universidade Federal do Rio Grande do Norte, 59072-970 Natal, RN (Brazil)

    2015-03-01

    We address the magnetic phases in very thin Ho films at the temperature interval between 20 K and 132 K. We show that slab size, surface effects and magnetic field due to spin ordering impact significantly the magnetic phase diagram. Also we report that there is a relevant reduction of the external field strength required to saturate the magnetization and for ultra-thin films the helical state does not form. We explore the specific heat and the susceptibility as auxiliary tools to discuss the nature of the phase transitions, when in the presence of an external magnetic field and temperature effects. The presence of an external field gives rise to the magnetic phase Fan and the spin-slip structures. - Highlights: • We analyze the magnetic phases of very thin Ho films in the temperature interval 20–132 K. • We show that slab size, etc. due to spin ordering may impact the magnetic phase diagram. • All magnetic phase transitions, for strong magnetic fields, are marked by the specific heat. • The presence of an external field gives rise to the magnetic phase Fan and the spin-slip one.

  4. Dynamics and morphology of chiral magnetic bubbles in perpendicularly magnetized ultra-thin films

    Science.gov (United States)

    Sarma, Bhaskarjyoti; Garcia-Sanchez, Felipe; Nasseri, S. Ali; Casiraghi, Arianna; Durin, Gianfranco

    2018-06-01

    We study bubble domain wall dynamics using micromagnetic simulations in perpendicularly magnetized ultra-thin films with disorder and Dzyaloshinskii-Moriya interaction. Disorder is incorporated into the material as grains with randomly distributed sizes and varying exchange constant at the edges. As expected, magnetic bubbles expand asymmetrically along the axis of the in-plane field under the simultaneous application of out-of-plane and in-plane fields. Remarkably, the shape of the bubble has a ripple-like part which causes a kink-like (steep decrease) feature in the velocity versus in-plane field curve. We show that these ripples originate due to the nucleation and interaction of vertical Bloch lines. Furthermore, we show that the Dzyaloshinskii-Moriya interaction field is not constant but rather depends on the in-plane field. We also extend the collective coordinate model for domain wall motion to a magnetic bubble and compare it with the results of micromagnetic simulations.

  5. Orbital hybridization, crystal structure and anomalous resistivity of ultrathin CrZrx alloy films on polymeric substrates

    International Nuclear Information System (INIS)

    Evans, Drew; Zuber, Kamil; Merkens, Kerstin; Murphy, Peter

    2012-01-01

    The orbital hybridization and crystal structure are experimentally explored for ultrathin chrome zirconium (CrZr x ) alloy films co-sputtered on precoated polymeric substrates. We determine the level of orbital hybridization and crystal structure using X-ray photoelectron spectroscopy and electron diffraction. Body-centred cubic and Ω-hexagonally close-packed phases are observed to coexist in the sputtered Cr-based films. Experiments reveal the orbital hybridization and crystal structure combine to produce anomalous resistivity for these ultrathin films.

  6. Hybrid Spintronic Structures With Magnetic Oxides and Heusler Alloys

    DEFF Research Database (Denmark)

    Xu, Y. B.; Hassan, S. S. A.; Wong, P. K. J.

    2008-01-01

    Hybrid spintronic structures, integrating half-metallic magnetic oxides and Heusler alloys with their predicted high spin polarization, are important for the development of second-generation spintronics with high-efficient spin injection. We have synthesized epitaxial magnetic oxide Fe3O4 on Ga......As(100) and the unit cell of the Fe3O4 was found to be rotated by 45 degrees to match the gallium arsenide GaAs. The films were found to have a bulk-like moment down to 3-4 nm and a low coercivity indicating a high-quality magnetic interface. The magnetization hysteresis loops of the ultrathin films...... are controlled by uniaxial magnetic anisotropy. The dynamic response of the sample shows a heavily damped precessional response to the applied field pulses. In the Heusler alloy system of Co-2 MnGa on GaAs, we found that the magnetic moment was reduced for thicknesses down to 10 nm, which may account...

  7. Magnetic properties of ultrathin Co/Ge(111) and Co/Ge(100) films

    International Nuclear Information System (INIS)

    Cheng, W. C.; Tsay, J. S.; Yao, Y. D.; Lin, K. C.; Yang, C. S.; Lee, S. F.; Tseng, T. K.; Neih, H. Y.

    2001-01-01

    The orientation of the magnetization and the occurrence of interfacial ferromagnetic inactive layers for ultrathin Co films grown on Ge(111) and Ge(100) surfaces have been studied using the in situ surface magneto-optic Kerr effect. On a Ge(111) substrate, cobalt films (≤28 monolayers) with in-plane easy axis of magnetization have been observed; however, on a Ge(100) substrate, ultrathin Co films (14 - 16 monolayers) with canted out-of-plane easy axis of magnetization were measured. The ferromagnetic inactive layers were formed due to the intermixing of Co and Ge and lowering the Curie temperature by reducing Co film thickness. The Co - Ge compound inactive layers were 3.8 monolayers thick for Co films grown on Ge(111) and 6.2 monolayers thick for Co films deposited on Ge(100). This is attributed to the difference of the density of surface atoms on Ge(111) and Ge(100). [copyright] 2001 American Institute of Physics

  8. Superaerophobic Ultrathin Ni-Mo Alloy Nanosheet Array from In Situ Topotactic Reduction for Hydrogen Evolution Reaction.

    Science.gov (United States)

    Zhang, Qian; Li, Pengsong; Zhou, Daojin; Chang, Zheng; Kuang, Yun; Sun, Xiaoming

    2017-11-01

    Hydrogen evolution reaction (HER) has prospect to becoming clean and renewable technology for hydrogen production and Ni-Mo alloy is among the best HER catalysts in alkaline electrolytes. Here, an in situ topotactic reduction method to synthesize ultrathin 2D Ni-Mo alloy nanosheets for electrocatalytic hydrogen evolution is reported. Due to its ultrathin structure and tailored composition, the as-synthesized Ni-Mo alloy shows an overpotential of 35 mV to reach a current density of 10 mA cm -2 , along with a Tafel slope of 45 mV decade -1 , demonstrating a comparable intrinsic activity to state-of-art commercial Pt/C catalyst. Besides, the vertically aligned assemble structure of the 2D NiMo nanosheets on conductive substrate makes the electrode "superaerophobic," thus leading to much faster bubble releasing during HER process and therefore shows faster mass transfer behavior at high current density as compared with drop drying Pt/C catalyst on the same substrate. Such in situ topotactic conversion finds a way to design and fabricate low-cost, earth-abundant non-noble metal based ultrathin 2D nanostructures for electrocatalytic issues. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  9. Thermal-driven evolution of magnetic domain structures in ultrathin films

    Czech Academy of Sciences Publication Activity Database

    Zablotskyy, Vitaliy A.; Maziewski, A.; Polyakova, T.

    2006-01-01

    Roč. 112, - (2006), s. 101-108 ISSN 1012-0394. [International School on Physics and Chemistry of Condensed Matter /17./ and International Symposium on Physics in Material Science /5./. Bialoweza, 21.06.2005-29.06.2005] EU Projects: European Commission(XE) 3177 - NANOMAG- LAB Grant - others:PSCSR(PL) 4T11B00624 Institutional research plan: CEZ:AV0Z10100520 Keywords : ultrathin magnetic films * magnetic domain * phase transitions Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.493, year: 2005

  10. Structural alloys for high field superconducting magnets

    International Nuclear Information System (INIS)

    Morris, J.W. Jr.

    1985-08-01

    Research toward structural alloys for use in high field superconducting magnets is international in scope, and has three principal objectives: the selection or development of suitable structural alloys for the magnet support structure, the identification of mechanical phenomena and failure modes that may influence service behavior, and the design of suitable testing procedures to provide engineering design data. This paper reviews recent progress toward the first two of these objectives. The structural alloy needs depend on the magnet design and superconductor type and differ between magnets that use monolithic and those that employ force-cooled or ICCS conductors. In the former case the central requirement is for high strength, high toughness, weldable alloys that are used in thick sections for the magnet case. In the latter case the need is for high strength, high toughness alloys that are used in thin welded sections for the conductor conduit. There is productive current research on both alloy types. The service behavior of these alloys is influenced by mechanical phenomena that are peculiar to the magnet environment, including cryogenic fatigue, magnetic effects, and cryogenic creep. The design of appropriate mechanical tests is complicated by the need for testing at 4 0 K and by rate effects associated with adiabatic heating during the tests. 46 refs

  11. Enhanced thermoelectric power in ultrathin topological insulators with magnetic doping

    KAUST Repository

    Tahir, M.

    2014-09-07

    We derive analytical expressions for the magnetic moment and orbital magnetization as well as for the corresponding thermal conductivity and thermoelectric power of a topological insulator film. We demonstrate enhancement of the thermoelectric transport for decreasing film thickness and for application of an exchange field due to the tunable band gap. Combining hybridization and exchange field is particularly suitable for heat to electric energy conversion and thermoelectric cooling.

  12. Enhanced thermoelectric power in ultrathin topological insulators with magnetic doping

    KAUST Repository

    Tahir, M.; Manchon, Aurelien; Schwingenschlö gl, Udo

    2014-01-01

    We derive analytical expressions for the magnetic moment and orbital magnetization as well as for the corresponding thermal conductivity and thermoelectric power of a topological insulator film. We demonstrate enhancement of the thermoelectric transport for decreasing film thickness and for application of an exchange field due to the tunable band gap. Combining hybridization and exchange field is particularly suitable for heat to electric energy conversion and thermoelectric cooling.

  13. Alloy formation during the electrochemical growth of a Ag-Cd ultrathin film on Au(1 1 1)

    International Nuclear Information System (INIS)

    Barrio, M.C. del; Garcia, S.G.; Salinas, D.R.

    2009-01-01

    The electrodeposition of a Ag/Cd ultrathin film on a Au(1 1 1) surface and the formation of a surface alloy during this process have been studied using classical electrochemical techniques and in situ Scanning Tunneling Microscopy (STM). The films were obtained from separate electrolytes containing Ag + or Cd 2+ ions and from a multicomponent solution containing both ions. First, the polarization conditions were adjusted in order to form a Ag film by overpotential deposition. Afterwards, a Cd monolayer was formed onto this Au(1 1 1)/Ag modified surface by underpotential deposition. The voltammetric behavior of the Cd UPD and the in situ STM images indicated that the ultrathin Ag films were uniformly deposited and epitaxially oriented with respect to the Au(1 1 1) surface. Long time polarization experiments showed that a significant Ag-Cd surface alloying accompanied the formation of the Cd monolayer on the Au(1 1 1)/Ag modified surface, independent of the Ag film thickness. In the case of an extremely thin Ag layer (1 Ag ML) the STM images and long time polarization experiments revealed a solid state diffusion process of Cd, Ag, and Au atoms which can be responsible for the formation of different Ag-Cd or Au-Ag-Cd alloy phases.

  14. Magnetic properties of metals and alloys

    International Nuclear Information System (INIS)

    Lyuborskij, F.E.; Livingston, D.D.; Chin, Zh.I.

    1987-01-01

    The nature of magnetic properties of materials and their dependence on the composition and the material structure are described. Properties and application of such materials as the alloys of the Fe-Ni-Co, Fe-Cr-Co, Co-rare earth, Fe-Si, Ni-Se system are considered. Application outlook for amorphous alloys of the (Fe, Ni, Co) 80 (metalloid) 20 type is shown. Methods for magnetic property measurement are pointed out

  15. Robust ultra-thin RuMo alloy film as a seedless Cu diffusion barrier

    International Nuclear Information System (INIS)

    Hsu, Kuo-Chung; Perng, Dung-Ching; Wang, Yi-Chun

    2012-01-01

    Highlights: ► A 5 nm-thick Mo added Ru film has been investigated as a Cu diffusion barrier layer. ► RuMo film provides over 175 °C improvement in thermal stability than that of pure Ru layer. ► The 5 nm-thick RuMo film shows excellent barrier performance against Cu diffusion upon 725 °C. - Abstract: This study investigated the properties of 5 nm-thick RuMo film as a Cu diffusion barrier. The sheet resistance variation and X-ray diffraction patterns show that the RuMo alloy film has excellent barrier performance and that it is stable upon annealing at 725 °C against Cu. The transmission electron microscopy micrograph and diffraction patterns show that the RuMo film is an amorphous-like structure, whereas pure Ru film is a nano-crystalline structure. The elements’ depth profiles, analyzed by X-ray photoelectron spectroscopy, indicate no inter-diffusion behavior between the Cu and Si layer, even annealing at 700 °C. Lower leakage current has been achieved from the Cu/barrier/insulator/Si test structure using RuMo film as the barrier layer. A 5 nm ultrathin RuMo film provided two orders of magnitude improvement in leakage current and also exhibited a 175 °C improvement in thermal stability than that of the pure Ru film. It is a potential candidate as a seedless Cu diffusion barrier for advanced Cu interconnects.

  16. Temperature dependence of magnetic anisotropies in ultrathin Fe film on vicinal Si(111)

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Yong-Sheng; He, Wei; Ye, Jun; Hu, Bo; Tang, Jin; Zhang, Xiang-Qun [State Key Laboratory of Magnetism and Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); Cheng, Zhao-Hua, E-mail: zhcheng@aphy.iphy.ac.cn [State Key Laboratory of Magnetism and Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); School of Physical Sciences, University of Chinese Academy of Sciences, Beijing 100190 (China)

    2017-05-01

    The temperature dependence of magnetic anisotropy of ultrathin Fe film with different thickness epitaxially grown on vicinal Si(111) substrate has been quantitatively investigated using the anisotropic magnetoresistance(AMR) measurements. Due to the effect of the vicinal substrate, the magnetic anisotropy is the superposition of a four-fold, a two-fold and a weakly six-fold contribution. It is found that the temperature dependence of the first-order magnetocrystalline anisotropies coefficient follows power laws of the reduced magnetization m(T)(=M(T)/M(0)) being consistent with the Callen and Callen's theory. However the temperature dependence of uniaxial magnetic anisotropy (UMA) shows novel behavior that decreases roughly as a function of temperature with different power law for samples with different thickness. We also found that the six-fold magnetocrystalline anisotropy is almost invariable over a wide temperature range. Possible mechanisms leading to the different exponents are discussed.

  17. Origin of temperature and field dependence of magnetic skyrmion size in ultrathin nanodots

    Science.gov (United States)

    Tomasello, R.; Guslienko, K. Y.; Ricci, M.; Giordano, A.; Barker, J.; Carpentieri, M.; Chubykalo-Fesenko, O.; Finocchio, G.

    2018-02-01

    Understanding the physical properties of magnetic skyrmions is important for fundamental research with the aim to develop new spintronic device paradigms where both logic and memory can be integrated at the same level. Here, we show a universal model based on the micromagnetic formalism that can be used to study skyrmion stability as a function of magnetic field and temperature. We consider ultrathin, circular ferromagnetic magnetic dots. Our results show that magnetic skyrmions with a small radius—compared to the dot radius—are always metastable, while large radius skyrmions form a stable ground state. The change of energy profile determines the weak (strong) size dependence of the metastable (stable) skyrmion as a function of temperature and/or field.

  18. Theory of Random Anisotropic Magnetic Alloys

    DEFF Research Database (Denmark)

    Lindgård, Per-Anker

    1976-01-01

    A mean-field-crystal-field theory is developed for random, multicomponent, anisotropic magnetic alloys. It is specially applicable to rare-earth alloys. A discussion is given of multicritical points and phase transitions between various states characterized by order parameters with different...... spatial directions or different ordering wave vectors. Theoretical predictions based on known parameters for the phase diagrams and magnetic moments for the binary rare-earth alloys of Tb, Dy, Ho, and Er, Tb-Tm, Nd-Pr, and pure double-hcp Nd agree qualitatively with the experimental observations...... fluctuation corrections in the mean-field results is also discussed....

  19. Modelling study of magnetic and concentration phase transition in ultrathin antiferromagnetic films

    International Nuclear Information System (INIS)

    Leonid, Afremov; Aleksandr, Petrov

    2014-01-01

    Using the method of the ''average spin'' a modelling study of magnetic and concentration phase transition in ultrathin antiferromagnetic of different crystalline structure has been carried out. It has been shown, that relative change of Neel temperature is subject to the power law with negative index which doesn't depend on the film's crystal kind. The calculation of the dependence of phase transition critical concentration in diluted magnetic material on the film thickness has been made out. The legitimacy of the use of the method developed for modelling of magnetic and concentration phase transition in different nanostructures is certified by accordance between the results of calculations and the experimental data

  20. Quantum capacitance of an ultrathin topological insulator film in a magnetic field

    KAUST Repository

    Tahir, M.; Sabeeh, K.; Schwingenschlö gl, Udo

    2013-01-01

    We present a theoretical study of the quantum magnetocapacitance of an ultrathin topological insulator film in an external magnetic field. The study is undertaken to investigate the interplay of the Zeeman interaction with the hybridization between the upper and lower surfaces of the thin film. Determining the density of states, we find that the electron-hole symmetry is broken when the Zeeman and hybridization energies are varied relative to each other. This leads to a change in the character of the magnetocapacitance at the charge neutrality point. We further show that in the presence of both Zeeman interaction and hybridization the magnetocapacitance exhibits beating at low and splitting of the Shubnikov de Haas oscillations at high perpendicular magnetic field. In addition, we address the crossover from perpendicular to parallel magnetic field and find consistency with recent experimental data.

  1. Shape induced magnetic vortex state in hexagonal ordered cofe nanodot arrays using ultrathin alumina shadow mask

    Science.gov (United States)

    Sellarajan, B.; Saravanan, P.; Ghosh, S. K.; Nagaraja, H. S.; Barshilia, Harish C.; Chowdhury, P.

    2018-04-01

    The magnetization reversal process of hexagonal ordered CoFe nanodot arrays was investigated as a function of nanodot thickness (td) varying from 10 to 30 nm with fixed diameter. For this purpose, ordered CoFe nanodots with a diameter of 80 ± 4 nm were grown by sputtering using ultra-thin alumina mask. The vortex annihilation and the dynamic spin configuration in the ordered CoFe nanodots were analyzed by means of magnetic hysteresis loops in complement with the micromagnetic simulation studies. A highly pinched hysteresis loop observed at 20 nm thickness suggests the occurrence of vortex state in these nanodots. With increase in dot thickness from 10 to 30 nm, the estimated coercivity values tend to increase from 80 to 175 Oe, indicating irreversible change in the nucleation/annihilation field of vortex state. The measured magnetic properties were then corroborated with the change in the shape of the nanodots from disk to hemisphere through micromagnetic simulation.

  2. Quantum capacitance of an ultrathin topological insulator film in a magnetic field

    KAUST Repository

    Tahir, M.

    2013-02-12

    We present a theoretical study of the quantum magnetocapacitance of an ultrathin topological insulator film in an external magnetic field. The study is undertaken to investigate the interplay of the Zeeman interaction with the hybridization between the upper and lower surfaces of the thin film. Determining the density of states, we find that the electron-hole symmetry is broken when the Zeeman and hybridization energies are varied relative to each other. This leads to a change in the character of the magnetocapacitance at the charge neutrality point. We further show that in the presence of both Zeeman interaction and hybridization the magnetocapacitance exhibits beating at low and splitting of the Shubnikov de Haas oscillations at high perpendicular magnetic field. In addition, we address the crossover from perpendicular to parallel magnetic field and find consistency with recent experimental data.

  3. Oxygen-enabled control of Dzyaloshinskii-Moriya Interaction in ultra-thin magnetic films

    KAUST Repository

    Belabbes, Abderrezak

    2016-04-22

    The search for chiral magnetic textures in systems lacking spatial inversion symmetry has attracted a massive amount of interest in the recent years with the real space observation of novel exotic magnetic phases such as skyrmions lattices, but also domain walls and spin spirals with a defined chirality. The electrical control of these textures offers thrilling perspectives in terms of fast and robust ultrahigh density data manipulation. A powerful ingredient commonly used to stabilize chiral magnetic states is the so-called Dzyaloshinskii-Moriya interaction (DMI) arising from spin-orbit coupling in inversion asymmetric magnets. Such a large antisymmetric exchange has been obtained at interfaces between heavy metals and transition metal ferromagnets, resulting in spin spirals and nanoskyrmion lattices. Here, using relativistic first-principles calculations, we demonstrate that the magnitude and sign of DMI can be entirely controlled by tuning the oxygen coverage of the magnetic film, therefore enabling the smart design of chiral magnetism in ultra-thin films. We anticipate that these results extend to other electronegative ions and suggest the possibility of electrical tuning of exotic magnetic phases.

  4. Transport and magnetic properties of HITPERM alloys

    Science.gov (United States)

    Pekala, K.; Latuch, J.; Pekala, M.; Skorvanek, I.; Jaskiewicz, P.

    2003-02-01

    Nanocrystalline HITPERM alloys Fe44.6Co43.3X7.4B3.7Cu1 (X = Nb, Zr, Hf) prepared by crystallization of amorphous precursors are studied by magnetization and electrical resistivity measurements for the first time. Structural and magnetic components of the electrical resistivity are separated. The electrical resistivity of the nanocrystalline α' (FeCo) phase calculated using the Maxwell Garnett relation proves strong electron scattering on the grain boundaries. The temperature variation of the crystalline fraction during the first crystallization stage is calculated for the Hf based alloy.

  5. Periodic reversal of magneto-optic Faraday rotation on uniaxial birefringence crystal with ultrathin magnetic films

    Directory of Open Access Journals (Sweden)

    C. W. Su

    2013-07-01

    Full Text Available An experimental approach of inclined incidence magneto-optic Faraday effect observed in the polar plane is applied. Three samples containing ferromagnetic cobalt ultrathin films on a semiconductor zinc oxide (0001 single crystal substrate with in-plane and out-of-plane anisotropy are evaluated. Through the fine adjustment of crossed polarizers in the magneto-optic effect measurement completely recorded the detail optical and magneto-optical responses from the birefringent crystal substrate and the magnetic film, especially for the signal induced from the substrate with uniaxial optical axis. The angle dependency of interference phenomena periodically from the optical and magneto-optical responses is attributed to the birefringence even in the absence of a magnetic field. The new type of observation finds that the transmission Faraday intensity in the oblique incidence includes a combination of polarization rotations, which results from optical compensation from the substrate and magneto-optical Faraday effects from the film. The samples grown at different rates and examined by this method exhibit magnetic structure discriminations. This result can be applied in the advanced polarized-light technologies to enhance the spatial resolution of magnetic surfaces with microstructural information under various magnetic field direction.

  6. Hyperfine magnetic fields in substituted Finemet alloys

    Energy Technology Data Exchange (ETDEWEB)

    Brzózka, K., E-mail: k.brzozka@uthrad.pl [University of Technology and Humanities in Radom, Department of Physics (Poland); Sovák, P. [P.J. Šafárik University, Institute of Physics (Slovakia); Szumiata, T.; Gawroński, M.; Górka, B. [University of Technology and Humanities in Radom, Department of Physics (Poland)

    2016-12-15

    Transmission Mössbauer spectroscopy was used to determine the hyperfine fields of Finemet-type alloys in form of ribbons, substituted alternatively by Mn, Ni, Co, Al, Zn, V or Ge of various concentration. The comparative analysis of magnetic hyperfine fields was carried out which enabled to understand the role of added elements in as-quenched as well as annealed samples. Moreover, the influence of the substitution on the mean direction of the local hyperfine magnetic field was examined.

  7. Asymmetric driven dynamics of Dzyaloshinskii domain walls in ultrathin ferromagnetic strips with perpendicular magnetic anisotropy

    Energy Technology Data Exchange (ETDEWEB)

    Sánchez-Tejerina, L. [Dpto. Electricidad y Electrónica, Facultad de Ciencias, Universidad de Valladolid, 47011 Valladolid (Spain); Alejos, Ó., E-mail: oscaral@ee.uva.es [Dpto. Electricidad y Electrónica, Facultad de Ciencias, Universidad de Valladolid, 47011 Valladolid (Spain); Martínez, E. [Dpto. Física Aplicada, Facultad de Ciencias, Universidad de Salamanca, 37011 Salamanca (Spain); Muñoz, J.M. [Dpto. Electricidad y Electrónica, Facultad de Ciencias, Universidad de Valladolid, 47011 Valladolid (Spain)

    2016-07-01

    The dynamics of domain walls in ultrathin ferromagnetic strips with perpendicular magnetic anisotropy is studied from both numerical and analytical micromagnetics. The influence of a moderate interfacial Dzyaloshinskii–Moriya interaction associated to a bi-layer strip arrangement has been considered, giving rise to the formation of Dzyaloshinskii domain walls. Such walls possess under equilibrium conditions an inner magnetization structure defined by a certain orientation angle that make them to be considered as intermediate configurations between Bloch and Néel walls. Two different dynamics are considered, a field-driven and a current-driven dynamics, in particular, the one promoted by the spin torque due to the spin-Hall effect. Results show an inherent asymmetry associated with the rotation of the domain wall magnetization orientation before reaching the stationary regime, characterized by a constant terminal speed. For a certain initial DW magnetization orientation at rest, the rotation determines whether the reorientation of the DW magnetization prior to reach stationary motion is smooth or abrupt. This asymmetry affects the DW motion, which can even reverse for a short period of time. Additionally, it is found that the terminal speed in the case of the current-driven dynamics may depend on either the initial DW magnetization orientation at rest or the sign of the longitudinally injected current. - Highlights: • The asymmetric response of domain walls in bilayer strips with PMA is studied. • Out-of-plane fields and SHE longitudinal currents are applied. • The response is associated to the rotation of the domain wall inner magnetization. • Clockwise and counter-clockwise magnetization rotations are not equivalent. • The asymmetry results in different travelled distances and/or terminal speeds.

  8. Asymmetric driven dynamics of Dzyaloshinskii domain walls in ultrathin ferromagnetic strips with perpendicular magnetic anisotropy

    International Nuclear Information System (INIS)

    Sánchez-Tejerina, L.; Alejos, Ó.; Martínez, E.; Muñoz, J.M.

    2016-01-01

    The dynamics of domain walls in ultrathin ferromagnetic strips with perpendicular magnetic anisotropy is studied from both numerical and analytical micromagnetics. The influence of a moderate interfacial Dzyaloshinskii–Moriya interaction associated to a bi-layer strip arrangement has been considered, giving rise to the formation of Dzyaloshinskii domain walls. Such walls possess under equilibrium conditions an inner magnetization structure defined by a certain orientation angle that make them to be considered as intermediate configurations between Bloch and Néel walls. Two different dynamics are considered, a field-driven and a current-driven dynamics, in particular, the one promoted by the spin torque due to the spin-Hall effect. Results show an inherent asymmetry associated with the rotation of the domain wall magnetization orientation before reaching the stationary regime, characterized by a constant terminal speed. For a certain initial DW magnetization orientation at rest, the rotation determines whether the reorientation of the DW magnetization prior to reach stationary motion is smooth or abrupt. This asymmetry affects the DW motion, which can even reverse for a short period of time. Additionally, it is found that the terminal speed in the case of the current-driven dynamics may depend on either the initial DW magnetization orientation at rest or the sign of the longitudinally injected current. - Highlights: • The asymmetric response of domain walls in bilayer strips with PMA is studied. • Out-of-plane fields and SHE longitudinal currents are applied. • The response is associated to the rotation of the domain wall inner magnetization. • Clockwise and counter-clockwise magnetization rotations are not equivalent. • The asymmetry results in different travelled distances and/or terminal speeds.

  9. Nanocrystalline magnetic alloys and ceramics

    Indian Academy of Sciences (India)

    R. Narasimhan (Krishtel eMaging) 1461 1996 Oct 15 13:05:22

    exchange anisotropy in magnetic core-shell structures where the core and the shell com- prise of a ferromagnetic metal and antiferromagnetic oxide respectively (Prados et al. 1999). A number of techniques both physical and chemical have been developed to prepare nanosized magnetic particles. In this paper, the various ...

  10. Preparing magnetic yttrium iron garnet nanodot arrays by ultrathin anodic alumina template on silicon substrate

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Hui; Han, Mangui, E-mail: han-mangui@yahoo.com; Deng, Longjiang [National Engineering Research Center of Electromagnetic Radiation Control Materials, University of Electronic Science and Technology of China, Chengdu 610054 (China); Zheng, Liang; Zheng, Peng; Qin, Huibin [Institute of Electron Device and Application, Hangzhou Dianzi University, Hangzhou 310008 (China); Wu, Qiong [Magnetism Key Laboratory of Zhejiang Province, China Jiliang University, Hangzhou 310018 (China)

    2015-08-10

    Ultrahigh density periodically ordered magnetic yttrium iron garnet (Y{sub 3}Fe{sub 5}O{sub 12}, YIG) nanodot arrays have been prepared by pulsed laser deposition through an ultrathin alumina mask (UTAM). UTAM having periodically ordered circularly shaped holes with 350 nm in diameter, 450 nm in inter-pore distance, and 700 nm in height has been prepared on silicon substrate. Furthermore, the microstructure and magnetic properties of YIG nanodot arrays have been characterized. Nanodot arrays with a sharp distribution in diameter centered at 340 nm with standard deviation of 10 nm have been fabricated. Moreover, typical hysteresis loops and ferromagnetic resonance spectra in in-plane and out-of-plane revealed that this unique structure greatly influences the magnetics properties of YIG. First, coercivity of YIG nanodot arrays in in-plane was increased about from 15 Oe of YIG films to 500 Oe. Then, the degree of uniformity about nanodot height decided that two or more resonance peaks in out-of-plane were detected in the spectra. The peak-to-peak linewidth values were about 94 Oe and 40 Oe in the parallel and perpendicular directions, respectively, which indicated that the values were larger by the two-magnon scattering. Consequently, this pattering method creates opportunities for studying physics in oxide nanomagnets and may be applied in spin-wave devices.

  11. Perpendicular magnetic anisotropy at the interface between ultrathin Fe film and MgO studied by angular-dependent x-ray magnetic circular dichroism

    Energy Technology Data Exchange (ETDEWEB)

    Okabayashi, J. [Research Center for Spectrochemistry, The University of Tokyo, Bunkyo-ku, Tokyo 113-0033 (Japan); Koo, J. W.; Mitani, S. [National Institute for Materials Science (NIMS), Tsukuba 305-0047 (Japan); Graduate School of Pure and Applied Sciences, University of Tsukuba, Tsukuba 305-8577 (Japan); Sukegawa, H. [National Institute for Materials Science (NIMS), Tsukuba 305-0047 (Japan); Takagi, Y.; Yokoyama, T. [Institute of Molecular Science, Okazaki, Aichi 444-8585 (Japan)

    2014-09-22

    Interface perpendicular magnetic anisotropy (PMA) in ultrathin Fe/MgO (001) has been investigated using angular-dependent x-ray magnetic circular dichroism (XMCD). We found that anisotropic orbital magnetic moments deduced from the analysis of XMCD contribute to the large PMA energies, whose values depend on the annealing temperature. The large PMA energies determined from magnetization measurements are related to those estimated from the XMCD and the anisotropic orbital magnetic moments through the spin-orbit interaction. The enhancement of anisotropic orbital magnetic moments can be explained mainly by the hybridization between the Fe 3d{sub z}{sup 2} and O 2p{sub z} states.

  12. Temperature-induced transitions between domain structures of ultrathin magnetic films

    International Nuclear Information System (INIS)

    Polyakova, T.; Zablotskii, V.

    2005-01-01

    Full text: Understanding of the influence of temperature on behavior of domain patterns of ultrathin magnetic films is of high significance for the fundamental physics of nanomagnetism as well as for technological applications. A thickness-dependent Curie temperature of ultrathin films may cause many interesting phenomena in the thermal evolution of domain structures (DS): i) nontrivial changes of the anisotropy constants as a function of the film thickness; ii) so-called inverse melting of DSs (processes where a more symmetric domain phase is found at lower temperatures than at higher temperatures - the inverse phase sequence) [1]; iii) temperature-induced transitions between domain structures. The possibility of such transitions is determined by lowering of the potential barriers separating different magnetization states as the film temperature approaches the Curie point. In this case with an increase of temperature, due to a significant decrease of the anisotropy constant, the domain wall energy is low enough and allows the system to reach equilibrium by a change of the domain wall number in the sample. This manifests itself in a transition from a metastable DS to a more stable DS which corresponds to new values of the anisotropy constant and magnetizations saturation. Thus, the temperature-induced transitions are driven by temperature changes of the magnetic parameters of the film. The key parameters controlling the DS geometry and period are the characteristic length, l c =σ/4πM S 2 (the ratio between the domain wall and demagnetization energies), and the quality factor Q =K/2πM S 2 (K is the first anisotropy constant). We show that for films with a pronounced nonmonotonic temperature dependence of l c one can expect a counter thermodynamic behavior: the inverse phase sequence and cooling-induced disordering. On changing temperature the existing domain structure should accommodate itself under new magnitudes of l c and Q. There are the two possible

  13. Magnetic properties of magnetic glass-like carbon prepared from furan resin alloyed with magnetic fluid

    Energy Technology Data Exchange (ETDEWEB)

    Nakamura, Kazumasa, E-mail: naka@sss.fukushima-u.ac.jp [Materials Science Area, Graduate School of Symbiotic Systems Science and Technology, Fukushima University, 1 Kanayagawa, Fukushima 960-1296 (Japan); Okuyama, Kyoko [Materials Science Area, Graduate School of Symbiotic Systems Science and Technology, Fukushima University, 1 Kanayagawa, Fukushima 960-1296 (Japan); Takase, Tsugiko [Institute of Environmental Radioactivity (IER), Fukushima University, 1 Kanayagawa, Fukushima 960-1296 (Japan)

    2017-03-01

    Magnetic glass-like carbons that were heat-treated at different temperatures or were filled with different magnetic nanoparticle contents were prepared from furan resin alloyed with magnetic fluid (MF) or Fe{sub 3}O{sub 4} powder in their liquid-phase states during mixing. Compared to the Fe{sub 3}O{sub 4} powder-alloyed carbon, the MF-alloyed carbon has highly dispersed the nanoparticles, and has the excellent saturation magnetization and coercivity. It is implied that saturation magnetizations are related to changes in the types of phases for the nanoparticles and the relative intensities of X-ray diffraction peaks for iron and iron-containing compounds in the carbons. Additionally, the coercivities are possibly affected by the size and crystallinity of the nanoparticles, the relative amounts of iron, and the existence of amorphous compounds on the carbon surfaces. - Highlights: • Magnetic glass-like carbons were prepared from furan resin alloyed with magnetic fluid. • The nanoparticles of MF-alloyed GLCs were highly dispersed. • MF-alloyed GLCs had excellent magnetic properties compared to powder-alloyed ones. • The magnetic properties changed with treatment temperature and nanoparticle content. • The changes in magnetic properties were investigated with XRD and FE-SEM.

  14. Magnetoresistance and magnetic breakdown phenomenon in amorphous magnetic alloys

    International Nuclear Information System (INIS)

    Chen Hui-yu; Gong Xiao-yu

    1988-01-01

    Transverse magnetoresistance in amorphous magnetic alloys (Fe/sub 1-//sub x/CO/sub x/) 82 Cu/sub 0.4/Si/sub 4.4/B/sub 13.2/ were measured at room temperature and in the magnetic field range 0--15 kOe. For large magnetic field, three different functional dependences of magnetoresistance on magnetic field strength have been found as follows: (1) Δrho/rho approaches saturation. (2) Δrho/rho increases proportionally to H 2 . (3) For x = 0.15, a sharp Δrho/rho peak appears at a certain magnetic field strength in spatial angular orientation of both magnetic field and electric currents. Case (3) is a magnetic breakdown phenomenon. Magnetic breakdown occurs at the gap between the spin-up and spin-down sheets of the Fermi surface. This gap is the spin-orbit gap and its magnitude is a sensitive function of magnetization. Hence the magnitude and width of the magnetoresistance peak and the magnetic field strength at the peak point are functions of angular orientation of both magnetic field and electric current

  15. Ab initio investigations of magnetic properties of ultrathin transition-metal films on 4d substrates

    Energy Technology Data Exchange (ETDEWEB)

    Al-Zubi, Ali

    2010-12-22

    In this thesis, we investigate the magnetic properties of 3d transition-metal monolayers on 4d transition-metal substrates by means of state of the art first-principles quantum theory. In order to reveal the underlying physics of these systems we study trends by performing systematic investigations across the transition-metal series. Case studies are presented for which Rh has been chosen as exemplary 4d substrate. We consider two substrate orientations, a square lattice provided by Rh(001) and a hexagonal lattice provided by Rh(111). We find, all 3d transition-metal (V, Cr, Mn, Fe, Co and Ni) monolayers deposited on the Rh substrate are magnetic and exhibit large local moments which follow Hund's rule with a maximum magnetic moment for Mn of about 3.7 {mu}{sub B} depending on the substrate orientation. The largest induced magnetic moment of about 0.46 {mu}{sub B} is found for Rh atoms adjacent to the Co(001)-film. On Rh(001) we predict a ferromagnetic (FM) ground state for V, Co and Ni, while Cr, Mn and Fe monolayers favor a c(2 x 2) antiferromagnetic (AFM) state, a checkerboard arrangement of up and down magnetic moments. The magnetic anisotropy energies of these ultrathin magnetic films are calculated for the FM and the AFM states. With the exception of V and Cr, the easy axis of the magnetization is predicted to be in the film plane. With the exception of Fe, analogous results are obtained for the 3d-metal monolayers on Rh(111). For Fe on Rh(111) a novel magnetic ground state is predicted, a double-row-wise antiferromagnetic state along the [11 anti 2] direction, a sequence of ferromagnetic double-rows of atoms, whose magnetic moments couple antiferromagnetically from double row to double row. The magnetic structure can be understood as superposition of a left- and right-rotating flat spin spiral. In a second set of case studies the properties of an Fe monolayer deposited on varies hexagonally terminated hcp (0001) and fcc (111) surfaces of 4d

  16. Ab initio investigations of magnetic properties of ultrathin transition-metal films on 4d substrates

    Energy Technology Data Exchange (ETDEWEB)

    Al-Zubi, Ali

    2010-12-22

    In this thesis, we investigate the magnetic properties of 3d transition-metal monolayers on 4d transition-metal substrates by means of state of the art first-principles quantum theory. In order to reveal the underlying physics of these systems we study trends by performing systematic investigations across the transition-metal series. Case studies are presented for which Rh has been chosen as exemplary 4d substrate. We consider two substrate orientations, a square lattice provided by Rh(001) and a hexagonal lattice provided by Rh(111). We find, all 3d transition-metal (V, Cr, Mn, Fe, Co and Ni) monolayers deposited on the Rh substrate are magnetic and exhibit large local moments which follow Hund's rule with a maximum magnetic moment for Mn of about 3.7 {mu}{sub B} depending on the substrate orientation. The largest induced magnetic moment of about 0.46 {mu}{sub B} is found for Rh atoms adjacent to the Co(001)-film. On Rh(001) we predict a ferromagnetic (FM) ground state for V, Co and Ni, while Cr, Mn and Fe monolayers favor a c(2 x 2) antiferromagnetic (AFM) state, a checkerboard arrangement of up and down magnetic moments. The magnetic anisotropy energies of these ultrathin magnetic films are calculated for the FM and the AFM states. With the exception of V and Cr, the easy axis of the magnetization is predicted to be in the film plane. With the exception of Fe, analogous results are obtained for the 3d-metal monolayers on Rh(111). For Fe on Rh(111) a novel magnetic ground state is predicted, a double-row-wise antiferromagnetic state along the [11 anti 2] direction, a sequence of ferromagnetic double-rows of atoms, whose magnetic moments couple antiferromagnetically from double row to double row. The magnetic structure can be understood as superposition of a left- and right-rotating flat spin spiral. In a second set of case studies the properties of an Fe monolayer deposited on varies hexagonally terminated hcp (0001) and fcc (111) surfaces of 4d-transition metals

  17. Ab initio investigations of magnetic properties of ultrathin transition-metal films on 4d substrates

    International Nuclear Information System (INIS)

    Al-Zubi, Ali

    2010-01-01

    In this thesis, we investigate the magnetic properties of 3d transition-metal monolayers on 4d transition-metal substrates by means of state of the art first-principles quantum theory. In order to reveal the underlying physics of these systems we study trends by performing systematic investigations across the transition-metal series. Case studies are presented for which Rh has been chosen as exemplary 4d substrate. We consider two substrate orientations, a square lattice provided by Rh(001) and a hexagonal lattice provided by Rh(111). We find, all 3d transition-metal (V, Cr, Mn, Fe, Co and Ni) monolayers deposited on the Rh substrate are magnetic and exhibit large local moments which follow Hund's rule with a maximum magnetic moment for Mn of about 3.7 μ B depending on the substrate orientation. The largest induced magnetic moment of about 0.46 μ B is found for Rh atoms adjacent to the Co(001)-film. On Rh(001) we predict a ferromagnetic (FM) ground state for V, Co and Ni, while Cr, Mn and Fe monolayers favor a c(2 x 2) antiferromagnetic (AFM) state, a checkerboard arrangement of up and down magnetic moments. The magnetic anisotropy energies of these ultrathin magnetic films are calculated for the FM and the AFM states. With the exception of V and Cr, the easy axis of the magnetization is predicted to be in the film plane. With the exception of Fe, analogous results are obtained for the 3d-metal monolayers on Rh(111). For Fe on Rh(111) a novel magnetic ground state is predicted, a double-row-wise antiferromagnetic state along the [11 anti 2] direction, a sequence of ferromagnetic double-rows of atoms, whose magnetic moments couple antiferromagnetically from double row to double row. The magnetic structure can be understood as superposition of a left- and right-rotating flat spin spiral. In a second set of case studies the properties of an Fe monolayer deposited on varies hexagonally terminated hcp (0001) and fcc (111) surfaces of 4d-transition metals (Tc, Ru, Rh

  18. Electric-field control of magnetic domain-wall velocity in ultrathin cobalt with perpendicular magnetization.

    Science.gov (United States)

    Chiba, D; Kawaguchi, M; Fukami, S; Ishiwata, N; Shimamura, K; Kobayashi, K; Ono, T

    2012-06-06

    Controlling the displacement of a magnetic domain wall is potentially useful for information processing in magnetic non-volatile memories and logic devices. A magnetic domain wall can be moved by applying an external magnetic field and/or electric current, and its velocity depends on their magnitudes. Here we show that the applying an electric field can change the velocity of a magnetic domain wall significantly. A field-effect device, consisting of a top-gate electrode, a dielectric insulator layer, and a wire-shaped ferromagnetic Co/Pt thin layer with perpendicular anisotropy, was used to observe it in a finite magnetic field. We found that the application of the electric fields in the range of ± 2-3 MV cm(-1) can change the magnetic domain wall velocity in its creep regime (10(6)-10(3) m s(-1)) by more than an order of magnitude. This significant change is due to electrical modulation of the energy barrier for the magnetic domain wall motion.

  19. Magnetic susceptibility measurements on Bi - Sn alloys

    International Nuclear Information System (INIS)

    Mustaffa bin Haji Abdullah

    1985-01-01

    Magnetic susceptibility measurements on eight samples of tin-rich and three samples of bismuth-rich Bi-Sn alloys were made from 85K to 300K by Faraday's method. The susceptibilities of the eight tin-rich samples are positive and greater than the susceptibility of pure tin. The values are approximately constant at low temperatures but decreasing a little bit with increasing temperature. This result is interpreted as due to the predominant contribution of the Pauli spin paramagnetic susceptibility. A small decrease in susceptibility with temperature is interpreted as due to the effect of the second order term in the expression for spin paramagnetic susceptibility. The fluctuation of the susceptibility for alloys of different composition is interpreted as due to the effect of the density of states at the Fermi levels. The three samples of bismuth-rich alloys show a transition to diamagnetic property, where the diamagnetism is increased with temperature. This result is predominant and due to the diamagnetic contribution from the ions. The increase in susceptibility with temperature is interpreted as due to an increase in the effective radii of the ions due to thermal expansion. (author)

  20. On the coexistence of the magnetic phases in chromium alloys

    DEFF Research Database (Denmark)

    Lebech, Bente; Mikke, K.

    1969-01-01

    Detailed neutron diffraction investigations have been performed on Cr-Re alloys in order to explain the several observations in Cr alloys of the coexistence of a commensurable and an oscillatory magnetic phase. It is concluded that the individual magnetic phases probably occur in separate domains....

  1. X-ray magnetic circular dichroism study of epitaxial magnetite ultrathin film on MgO(100)

    Energy Technology Data Exchange (ETDEWEB)

    Liu, W. Q.; Xu, Y. B., E-mail: yongbing.xu@york.ac.uk, E-mail: rzhang@nju.edu.cn [York-Nanjing International Center for Spintronics (YNICS), School of Electronics Science and Engineering, Nanjing University, Nanjing 210093 (China); Spintronics and Nanodevice Laboratory, Department of Electronics, University of York, York YO10 5DD (United Kingdom); Song, M. Y.; Lin, J. G. [Center for Condensed Matter Sciences, National Taiwan University, Taipei 106, Taiwan (China); Maltby, N. J.; Li, S. P. [Spintronics and Nanodevice Laboratory, Department of Electronics, University of York, York YO10 5DD (United Kingdom); Samant, M. G.; Parkin, S. S. P. [IBM Research Division, Almaden Research Center, San Jose, California 95120 (United States); Bencok, P.; Steadman, Paul; Dobrynin, Alexey [Diamond Light Source, Didcot OX11 0DE (United Kingdom); Zhang, R., E-mail: yongbing.xu@york.ac.uk, E-mail: rzhang@nju.edu.cn [York-Nanjing International Center for Spintronics (YNICS), School of Electronics Science and Engineering, Nanjing University, Nanjing 210093 (China)

    2015-05-07

    The spin and orbital magnetic moments of the Fe{sub 3}O{sub 4} epitaxial ultrathin film synthesized by plasma assisted simultaneous oxidization on MgO(100) have been studied with X-ray magnetic circular dichroism. The ultrathin film retains a rather large total magnetic moment, i.e., (2.73 ± 0.15) μ{sub B}/f.u., which is ∼70% of that for the bulk-like Fe{sub 3}O{sub 4}. A significant unquenched orbital moment up to 0.54 ± 0.05 μ{sub B}/f.u. was observed, which could come from the symmetry breaking at the Fe{sub 3}O{sub 4}/MgO interface. Such sizable orbital moment will add capacities to the Fe{sub 3}O{sub 4}-based spintronics devices in the magnetization reversal by the electric field.

  2. Magnetic properties of the binary Nickel/Bismuth alloy

    Energy Technology Data Exchange (ETDEWEB)

    Keskin, Mustafa; Şarlı, Numan, E-mail: numansarli82@gmail.com

    2017-09-01

    Highlights: • We model and investigate the magnetic properties of the Ni/Bi alloy within the EFT. • Magnetizations of the Ni/Bi alloy are observed as Bi1 > Bi2 > Ni/Bi > Ni at T < Tc. • Magnetization of the Bi1 is dominant and Ni is at least dominant T < Tc. • Total magnetization of the Ni/Bi alloy is close to those of Ni at T < Tc. • Hysteresis curves are overlap at T < 0.1 and they behave separately at T > 0.1. - Abstract: Magnetic properties of the binary Nickel/Bismuth alloy (Ni/Bi) are investigated within the effective field theory. The Ni/Bi alloy has been modeled that the rhombohedral Bi lattice is surrounded by the hexagonal Ni lattice. According to lattice locations, Bi atoms have two different magnetic properties. Bi1 atoms are in the center of the hexagonal Ni atoms (Ni/Bi1 single layer) and Bi2 atoms are between two Ni/Bi1 bilayers. The Ni, Bi1, Bi2 and Ni/Bi undergo a second-order phase transition from the ferromagnetic phase to paramagnetic phase at Tc = 1.14. The magnetizations of the Ni/Bi alloy are observed as Bi1 > Bi2 > Ni/Bi > Ni at T < Tc; hence the magnetization of the Bi1 is dominant and Ni is at least dominant. However, the total magnetization of the Ni/Bi alloy is close to magnetization of the Ni at T < Tc. The corcivities of the Ni, Bi1, Bi2 and Ni/Bi alloy are the same with each others, but the remanence magnetizations are different. Our theoretical results of M(T) and M(H) of the Ni/Bi alloy are in quantitatively good agreement with the some experimental results of binary Nickel/Bismuth systems.

  3. Silicon nitride gradient film as the underlayer of ultra-thin tetrahedral amorphous carbon overcoat for magnetic recording slider

    Energy Technology Data Exchange (ETDEWEB)

    Wang Guigen, E-mail: wanggghit@yahoo.com [Shenzhen Graduate School, Harbin Institute of Technology, Shenzhen 518055 (China); Kuang Xuping; Zhang Huayu; Zhu Can [Shenzhen Graduate School, Harbin Institute of Technology, Shenzhen 518055 (China); Han Jiecai [Shenzhen Graduate School, Harbin Institute of Technology, Shenzhen 518055 (China); Center for Composite Materials, Harbin Institute of Technology, Harbin 150080 (China); Zuo Hongbo [Center for Composite Materials, Harbin Institute of Technology, Harbin 150080 (China); Ma Hongtao [SAE Technologies Development (Dongguan) Co., Ltd., Dongguan 523087 (China)

    2011-12-15

    Highlights: Black-Right-Pointing-Pointer The ultra-thin carbon films with different silicon nitride (Si-N) film underlayers were prepared. Black-Right-Pointing-Pointer It highlighted the influences of Si-N underlayers. Black-Right-Pointing-Pointer The carbon films with Si-N underlayers obtained by nitriding especially at the substrate bias of -150 V, can exhibit better corrosion protection properties - Abstract: There are higher technical requirements for protection overcoat of magnetic recording slider used in high-density storage fields for the future. In this study, silicon nitride (Si-N) composition-gradient films were firstly prepared by nitriding of silicon thin films pre-sputtered on silicon wafers and magnetic recording sliders, using microwave electron cyclotron resonance plasma source. The ultra-thin tetrahedral amorphous carbon films were then deposited on the Si-N films by filtered cathodic vacuum arc method. Compared with amorphous carbon overcoats with conventional silicon underlayers, the overcoats with Si-N underlayers obtained by plasma nitriding especially at the substrate bias of -150 V, can provide better corrosion protection for high-density magnetic recording sliders.

  4. Silicon nitride gradient film as the underlayer of ultra-thin tetrahedral amorphous carbon overcoat for magnetic recording slider

    International Nuclear Information System (INIS)

    Wang Guigen; Kuang Xuping; Zhang Huayu; Zhu Can; Han Jiecai; Zuo Hongbo; Ma Hongtao

    2011-01-01

    Highlights: ► The ultra-thin carbon films with different silicon nitride (Si-N) film underlayers were prepared. ► It highlighted the influences of Si-N underlayers. ► The carbon films with Si-N underlayers obtained by nitriding especially at the substrate bias of −150 V, can exhibit better corrosion protection properties - Abstract: There are higher technical requirements for protection overcoat of magnetic recording slider used in high-density storage fields for the future. In this study, silicon nitride (Si-N) composition-gradient films were firstly prepared by nitriding of silicon thin films pre-sputtered on silicon wafers and magnetic recording sliders, using microwave electron cyclotron resonance plasma source. The ultra-thin tetrahedral amorphous carbon films were then deposited on the Si-N films by filtered cathodic vacuum arc method. Compared with amorphous carbon overcoats with conventional silicon underlayers, the overcoats with Si-N underlayers obtained by plasma nitriding especially at the substrate bias of −150 V, can provide better corrosion protection for high-density magnetic recording sliders.

  5. FINEMET type alloy without Si: Structural and magnetic properties

    International Nuclear Information System (INIS)

    Muraca, D.; Cremaschi, V.; Moya, J.; Sirkin, H.

    2008-01-01

    Magnetic and structural properties of a Finemet type alloy (Fe 73.5 Ge 15.5 Nb 3 B 7 Cu 1 ) without Si and high Ge content were studied. Amorphous material was obtained by the melt spinning technique and was heat treated at different temperatures for 1 h under high vacuum to induce the nanocrystallization of the sample. The softest magnetic properties were obtained between 673 and 873 K. The role of Ge on the ferromagnetic paramagnetic transition of the as-quenched alloys and its influence on the crystallization process were studied using a calorimetric technique. Moessbauer spectroscopy was employed in the nanocrystallized alloy annealed at 823 K to obtain the composition of the nanocrystals and the amorphous phase fraction. Using this data and magnetic measurements of the as-quenched alloy, the magnetic contribution of nanocrystals to the alloy annealed at 823 K was estimated via a linear model

  6. Magnetic characterization of the stator core of a high-speed motor made of an ultrathin electrical steel sheet using the magnetic property evaluation system

    Directory of Open Access Journals (Sweden)

    Mohachiro Oka

    2018-04-01

    Full Text Available Recently, the application areas for electric motors have been expanding. For instance, electric motors are used in new technologies such as rovers, drones, cars, and robots. The motor used in such machinery should be small, high-powered, highly-efficient, and high-speed. In such motors, loss at high-speed rotation must be especially minimal. Eddy-current loss in the stator core is known to increase greatly during loss at high-speed rotation of the motor. To produce an efficient high-speed motor, we are developing a stator core for a motor using an ultrathin electrical steel sheet with only a small amount of eddy-current loss. Furthermore, the magnetic property evaluation for efficient, high-speed motor stator cores that use conventional commercial frequency is insufficient. Thus, we made a new high-speed magnetic property evaluation system to evaluate the magnetic properties of the efficient high-speed motor stator core. This system was composed of high-speed A/D converters, D/A converters, and a high-speed power amplifier. In experiments, the ultrathin electrical steel sheet dramatically suppressed iron loss and, in particular, eddy-current loss. In addition, a new high-speed magnetic property evaluation system accurately evaluated the magnetic properties of the efficient high-speed motor stator core.

  7. Magnetic characterization of the stator core of a high-speed motor made of an ultrathin electrical steel sheet using the magnetic property evaluation system

    Science.gov (United States)

    Oka, Mohachiro; Enokizono, Masato; Mori, Yuji; Yamazaki, Kazumasa

    2018-04-01

    Recently, the application areas for electric motors have been expanding. For instance, electric motors are used in new technologies such as rovers, drones, cars, and robots. The motor used in such machinery should be small, high-powered, highly-efficient, and high-speed. In such motors, loss at high-speed rotation must be especially minimal. Eddy-current loss in the stator core is known to increase greatly during loss at high-speed rotation of the motor. To produce an efficient high-speed motor, we are developing a stator core for a motor using an ultrathin electrical steel sheet with only a small amount of eddy-current loss. Furthermore, the magnetic property evaluation for efficient, high-speed motor stator cores that use conventional commercial frequency is insufficient. Thus, we made a new high-speed magnetic property evaluation system to evaluate the magnetic properties of the efficient high-speed motor stator core. This system was composed of high-speed A/D converters, D/A converters, and a high-speed power amplifier. In experiments, the ultrathin electrical steel sheet dramatically suppressed iron loss and, in particular, eddy-current loss. In addition, a new high-speed magnetic property evaluation system accurately evaluated the magnetic properties of the efficient high-speed motor stator core.

  8. Magnetic Shape Memory Alloy Actuator for Instrument Applications

    Data.gov (United States)

    National Aeronautics and Space Administration — This project will develop a simple actuator based on magnetic shape memory alloy (MSMA), a novel new family of crystalline materials which exhibit strain deformation...

  9. Narrow-gap physical vapour deposition synthesis of ultrathin SnS1-xSex (0 ≤ x ≤ 1) two-dimensional alloys with unique polarized Raman spectra and high (opto)electronic properties.

    Science.gov (United States)

    Gao, Wei; Li, Yongtao; Guo, Jianhua; Ni, Muxun; Liao, Ming; Mo, Haojie; Li, Jingbo

    2018-05-10

    Here we report ultrathin SnS1-xSex alloyed nanosheets synthesized via a narrow-gap physical vapour deposition approach. The SnS1-xSex alloy presents a uniform quadrangle shape with a lateral size of 5-80 μm and a thickness of several nanometers. Clear orthorhombic symmetries and unique in-plane anisotropic properties of the 2D alloyed nanosheets were found with the help of X-ray diffraction, high resolution transmission electron microscopy and polarized Raman spectroscopy. Moreover, 2D alloyed field-effect transistors were fabricated, exhibiting a unipolar p-type semiconductor behavior. This study also provided a lesson that the thickness of the alloyed channels played the major role in the current on/off ratio, and the high ratio of 2.10 × 102 measured from a large ultrathin SnS1-xSex device was two orders of magnitude larger than that of previously reported SnS, SnSe nanosheet based transistors because of the capacitance shielding effect. Obviously enhanced Raman peaks were also found in the thinner nanosheets. Furthermore, the ultrathin SnS0.5Se0.5 based photodetector showed a highest responsivity of 1.69 A W-1 and a short response time of 40 ms under illumination of a 532 nm laser from 405 to 808 nm. Simultaneously, the corresponding highest external quantum efficiency of 392% and detectivity of 3.96 × 104 Jones were also achieved. Hopefully, the narrow-gap synthesis technique provides us with an improved strategy to obtain large ultrathin 2D nanosheets which may tend to grow into thicker ones for stronger interlayer van der Waals forces, and the enhanced physical and (opto)electrical performances in the obtained ultrathin SnS1-xSex alloyed nanosheets prove their great potential in the future applications for versatile devices.

  10. Study of anisotropy, magnetization reversal and damping in ultrathin Co films on MgO (0 0 1) substrate

    Science.gov (United States)

    Mallik, Srijani; Bedanta, Subhankar

    2018-01-01

    Ultrathin Co films of 3 nm thickness have been prepared on MgO (0 0 1) substrate in presence or absence of substrate pre-annealing. Uniaxial anisotropy is induced in the samples due to the deposition under oblique angle of incidence. Along with the oblique deposition induced anisotropy, another uniaxial anisotropy contribution has been observed due to pre-annealing. However, no cubic anisotropy has been observed here as compared to the thicker films. Angle dependent ferromagnetic resonance (FMR) measurement confirms the presence of two anisotropies in the pre-annealed sample with ∼18° misalignment with each other. The two anisotropy constants were calculated from both superconducting quantum interference device (SQUID) magnetometry and FMR spectroscopy. The magnetization reversal is governed by nucleation dominated aftereffect followed by domain wall motion for the pre-annealed sample. Branched domains are observed for the sample prepared without pre-annealing which indicates grain disorientation of Co. However, in the thicker (25 nm) Co films ripple domains were observed in contrary to ultrathin (3 nm) films.

  11. Ultrathin Carbon with Interspersed Graphene/Fullerene-like Nanostructures: A Durable Protective Overcoat for High Density Magnetic Storage.

    Science.gov (United States)

    Dwivedi, Neeraj; Satyanarayana, Nalam; Yeo, Reuben J; Xu, Hai; Ping Loh, Kian; Tripathy, Sudhiranjan; Bhatia, Charanjit S

    2015-06-25

    One of the key issues for future hard disk drive technology is to design and develop ultrathin (Forming carbon overcoats (COCs) having interspersed nanostructures by the filtered cathodic vacuum arc (FCVA) process can be an effective approach to achieve the desired target. In this work, by employing a novel bi-level surface modification approach using FCVA, the formation of a high sp(3) bonded ultrathin (~1.7 nm) amorphous carbon overcoat with interspersed graphene/fullerene-like nanostructures, grown on magnetic hard disk media, is reported. The in-depth spectroscopic and microscopic analyses by high resolution transmission electron microscopy, scanning tunneling microscopy, time-of-flight secondary ion mass spectrometry, and Raman spectroscopy support the observed findings. Despite a reduction of ~37% in COC thickness, the FCVA-processed thinner COC (~1.7 nm) shows promising functional performance in terms of lower coefficient of friction (~0.25), higher wear resistance, lower surface energy, excellent hydrophobicity and similar/better oxidation corrosion resistance than current commercial COCs of thickness ~2.7 nm. The surface and tribological properties of FCVA-deposited COC was further improved after deposition of lubricant layer.

  12. Understanding the magnetic anisotropy in Fe-Si amorphous alloys

    Energy Technology Data Exchange (ETDEWEB)

    Diaz, J.; Hamdan, N.M.; Jalil, P.; Hussain, Z.; Valvidares, S.M.; Alameda, J.M.

    2002-08-01

    The origin of the magnetic anisotropy in a very disordered Fe-Si alloy has been investigated. The alloy containing 40 percent at. Si was prepared in the form of a thin film in a DC magnetron sputtering chamber. Structural disorder was obtained from Extended X-ray Absorption Fine Structure spectroscopy. The uniformity and lack of inhomogeneities at a microscopic level was checked by measuring their transverse magnetic susceptibility and hysteresis loops. The orbital component of the magnetic moment was measured by X-ray Magnetic Circular Dichroism spectroscopy. The orbital moment was extraordinary high, 0.4mB. Such a high value contrasted with the relatively small uniaxial anisotropy energy of the thin film (2kJ/m3). This suggests that the cause of the magnetic anisotropy in this alloy was a small degree of correlation in the orientation of the local orbital moments along a preferential direction.

  13. Understanding the magnetic anisotropy in Fe-Si amorphous alloys

    International Nuclear Information System (INIS)

    Diaz, J.; Hamdan, N.M.; Jalil, P.; Hussain, Z.; Valvidares, S.M.; Alameda, J.M.

    2002-01-01

    The origin of the magnetic anisotropy in a very disordered Fe-Si alloy has been investigated. The alloy containing 40 percent at. Si was prepared in the form of a thin film in a DC magnetron sputtering chamber. Structural disorder was obtained from Extended X-ray Absorption Fine Structure spectroscopy. The uniformity and lack of inhomogeneities at a microscopic level was checked by measuring their transverse magnetic susceptibility and hysteresis loops. The orbital component of the magnetic moment was measured by X-ray Magnetic Circular Dichroism spectroscopy. The orbital moment was extraordinary high, 0.4mB. Such a high value contrasted with the relatively small uniaxial anisotropy energy of the thin film (2kJ/m3). This suggests that the cause of the magnetic anisotropy in this alloy was a small degree of correlation in the orientation of the local orbital moments along a preferential direction

  14. Effects of Cold Rolling Reduction and Initial Goss Grains Orientation on Texture Evolution and Magnetic Performance of Ultra-thin Grain-oriented Silicon Steel

    Directory of Open Access Journals (Sweden)

    LIANG Rui-yang

    2017-06-01

    Full Text Available The ultra-thin grain-oriented silicon steel strips with a thickness of 0.06-0.12mm were produced by one-step-rolling methods with different Goss-orientation of grain-oriented silicon steel sheets. The effect of cold rolling reduction and initial Goss-orientation of samples on texture evolution and magnetic performance of ultra-thin grain-oriented silicon steel strips was studied by EBSD. The result shows that with the increase of cold rolling reduction and decrease of strips thickness, the recrystallization texture is enhanced after annealing.When the cold rolling reduction is 70%,RD//〈001〉 recrystallization texture is the sharpest, and the magnetic performance is the best. The higher degree of Goss orientation in initial sample is, the better magnetic performance of ultra-thin grain-oriented silicon steel.Therefore, for producing an ultra-thin grain-oriented silicon steel with high performance, a material with a concentrated orientation of Goss grains can be used.

  15. Compositional disorder, magnetism, and their interplay in metallic alloys

    International Nuclear Information System (INIS)

    Johnson, D.D.; Staunton, J.B.; Pinski, F.J.; Gyorffy, B.L.; Stocks, G.M.

    1992-01-01

    Chemical disorder leads to a variety of intriguing phenomena in alloys which have yet to be fully understood, particularly those phenomena occurring when chemical and magnetic effects interplay with one another. For example, magnetic order gives rise to chemical ordering in alloys, as in Ni-rich NiFe alloys. Two examples of the interplay of chemical disorder and magnetism will be discussed. Our recently developed ab-initio Landau (mean-field) theory for calculating the chemical-chemical, magneto-chemical, and magnetic-magnetic correlation functions in substitutional random alloys is used to describe electronic/magnetic mechanisms (e.g. in FeV) which give rise to the chemical short-range order as determined by neutron, X-ray, or electron diffuse scattering intensities. New developments within this approach that account for charge rearrangement effect will be mentioned. These calculations are performed within the multiple-scattering framework, developed by Korringa, Kohn, and Rostoker (KKR), combined with the coherent potential approximation (CPA) to describe the disorder. This approach allows a first-principles description of the electronic structure of the high-temperature, chemically disordered state and its instability to ordering a low temperatures. This paper reports that this method provides not only a direct comparison of diffuse scattering data with theory but a means to understand more fully the underlying mechanisms which drive chemical and/or magnetic ordering

  16. Interfacial magnetic coupling in ultrathin all-manganite La0.7Sr0.3MnO3-TbMnO3 superlattices

    KAUST Repository

    Tian, Y. F.

    2014-04-14

    We report the growth and magnetic properties of all-manganite superlattices composed of ultrathin double-exchange ferromagnetic La0.7Sr0.3MnO3 and noncollinear multiferroic TbMnO3 layers. Spontaneous magnetization and hysteresis loops are observed in such superlattices with individual La0.7Sr0.3MnO3 layers as thin as two unit cells, which are accompanied by pronounced exchange bias and enhanced coercivity. Our results indicate substantial interfacial magnetic coupling between spin sublattices in such superlattices, providing a powerful approach towards tailoring the properties of artificial magnetic heterostructures.

  17. Interfacial magnetic coupling in ultrathin all-manganite La0.7Sr0.3MnO3-TbMnO3 superlattices

    KAUST Repository

    Tian, Y. F.; Lebedev, O. I.; Roddatis, V. V.; Lin, W. N.; Ding, J. F.; Hu, S. J.; Yan, S. S.; Wu, Tao

    2014-01-01

    We report the growth and magnetic properties of all-manganite superlattices composed of ultrathin double-exchange ferromagnetic La0.7Sr0.3MnO3 and noncollinear multiferroic TbMnO3 layers. Spontaneous magnetization and hysteresis loops are observed in such superlattices with individual La0.7Sr0.3MnO3 layers as thin as two unit cells, which are accompanied by pronounced exchange bias and enhanced coercivity. Our results indicate substantial interfacial magnetic coupling between spin sublattices in such superlattices, providing a powerful approach towards tailoring the properties of artificial magnetic heterostructures.

  18. Fabrication and Magnetic Properties of Co₂MnAl Heusler Alloys by Mechanical Alloying.

    Science.gov (United States)

    Lee, Chung-Hyo

    2018-02-01

    We have applied mechanical alloying (MA) to produce nanocrystalline Co2MnAl Heusler alloys using a mixture of elemental Co50Mn25Al25 powders. An optimal milling and heat treatment conditions to obtain a Co2MnAl Heusler phase with fine microstructure were investigated by X-ray diffraction, differential scanning calorimeter and vibrating sample magnetometer measurements. α-(Co, Mn, Al) FCC phases coupled with amorphous phase are obtained after 3 hours of MA without any evidence for the formation of Co2MnAl alloys. On the other hand, a Co2MnAl Heusler alloys can be obtained by the heat treatment of all MA samples up to 650 °C. X-ray diffraction result shows that the average grain size of Co2MnAl Heusler alloys prepared by MA for 5 h and heat treatment is in the range of 95 nm. The saturation magnetization of MA powders decreases with MA time due to the magnetic dilution by alloying with nonmagnetic Mn and Al elements. The magnetic hardening due to the reduction of the grain size with ball milling is also observed. However, the saturation magnetization of MA powders after heat treatment increases with MA time and reaches to a maximum value of 105 emu/g after 5 h of MA. It can be also seen that the coercivity of 5 h MA sample annealed at 650 °C is fairly low value of 25 Oe.

  19. Effects of Zr alloying on the microstructure and magnetic properties of Alnico permanent magnets

    Science.gov (United States)

    Rehman, Sajjad Ur; Ahmad, Zubair; Haq, A. ul; Akhtar, Saleem

    2017-11-01

    Alnico-8 permanent magnets were produced through casting and subsequent thermal treatment process. Magnetic alloy of nominal composition 32.5 Fe-7.5 Al-1.0 Nb-35.0 Co-4.0 Cu-14.0 Ni-6.0 Ti were prepared by arc melting and casting technique. The Zr was added to 32.5 Fe-7.5 Al-1.0 Nb-35.0 Co-4.0 Cu-14.0 Ni-6.0 Ti alloy ranging from 0.3 to 0.9 wt%. The magnets were developed by employing two different heat treatment cycles known as conventional treatment and thermo-magnetic annealing treatment. The samples were characterized by X-ray diffraction method, Scanning electron microscope and magnetometer by plotting magnetic hysteresis demagnetization curves. The results indicate that magnetic properties are strongly depended upon alloy chemistry and process. The 0.6 wt% Zr added alloys yielded the best magnetic properties among the studied alloys. The magnetic properties obtained through conventional heat treatment are Hc = 1.35 kOe, Br = 5.2 kG and (BH)max = 2 MGOe. These magnetic properties were enhanced to Hc = 1.64 kOe, Br = 6.3 kG and (BH)max = 3.7 MGOe by thermo-magnetic annealing treatment.

  20. Barrier breakdown mechanism in nano-scale perpendicular magnetic tunnel junctions with ultrathin MgO barrier

    Science.gov (United States)

    Lv, Hua; Leitao, Diana C.; Hou, Zhiwei; Freitas, Paulo P.; Cardoso, Susana; Kämpfe, Thomas; Müller, Johannes; Langer, Juergen; Wrona, Jerzy

    2018-05-01

    Recently, the perpendicular magnetic tunnel junctions (p-MTJs) arouse great interest because of its unique features in the application of spin-transfer-torque magnetoresistive random access memory (STT-MRAM), such as low switching current density, good thermal stability and high access speed. In this paper, we investigated current induced switching (CIS) in ultrathin MgO barrier p-MTJs with dimension down to 50 nm. We obtained a CIS perpendicular tunnel magnetoresistance (p-TMR) of 123.9% and 7.0 Ω.μm2 resistance area product (RA) with a critical switching density of 1.4×1010 A/m2 in a 300 nm diameter junction. We observe that the extrinsic breakdown mechanism dominates, since the resistance of our p-MTJs decreases gradually with the increasing current. From the statistical analysis of differently sized p-MTJs, we observe that the breakdown voltage (Vb) of 1.4 V is 2 times the switching voltage (Vs) of 0.7 V and the breakdown process exhibits two different breakdown states, unsteady and steady state. Using Simmons' model, we find that the steady state is related with the barrier height of the MgO layer. Furthermore, our study suggests a more efficient method to evaluate the MTJ stability under high bias rather than measuring Vb. In conclusion, we developed well performant p-MTJs for the use in STT-MRAM and demonstrate the mechanism and control of breakdown in nano-scale ultrathin MgO barrier p-MTJs.

  1. Magnetic field induced superconductor-insulator transitions for ultra-thin Bi films on the different underlayers

    International Nuclear Information System (INIS)

    Makise, K; Kawaguti, T; Shinozaki, B

    2009-01-01

    This work shows the experimental results of the superconductor-insulator (S-I) transition for ultra-thin Bi films in magnetic fields. The quench-condensed (q-c) Bi film onto insulating underlayers have been interpreted to be homogeneous. In contrast, the Bi film without underlayers has been regarded as a granular film. The electrical transport properties of ultra-thin metal films near the S-I transition depend on the structure of the film. In order to confirm the effect of the underlayer to the homogeneity of the superconducting films, we investigate the characteristics of S-I transitions of q-c nominally homogeneous Bi films on underlayers of two insulating materials, SiO, and Sb. Under almost the same deposition condition except for the material of underlayer, we prepared the Bi films by repeating the additional deposition and performed in-situ electrical measurement. It is found that the transport properties near the S-I transitions show the remarkable difference between two films on different underlayers. As for Bi films on SiO, it turned out that the temperature dependence of resistance per square R sq (T) of the field-tuned transition and the thickness-tuned transition shows similar behavior; it was a thermally activated form. On the other hand, the R sq (T) of Bi films on Sb for thickness-tuned S-I transition showed logarithmic temperature dependence, but that for field-tuned S-I transition showed a thermally activated form.

  2. Mossbauer analysis of the atomic and magnetic structure of alloys

    CERN Document Server

    Ovchinnikov, VV

    2007-01-01

    The monograph indicates the key problems that have to be solved for the further development of the Mössbauer methods for analysis of the nuclear and magnetic structure of alloys, and offer solution variants for some of these problems based on the generalised results of a wide range of theoretical and experimental investigations,including original work by the author of the book and his colleagues. Contents 1. Description of the nature of the Mössbauer effect 2. Interpretation of the ossbauer spectra of alloys 3.Electrical and magnetics hyperfine interactions of resonant nuclei in metals and

  3. Magnetic properties of three pseudobinary RCo5 alloy systems

    International Nuclear Information System (INIS)

    Heinrich, J.P.

    1976-01-01

    The field dependence of the magnetization was measured in the magnetically easy and hard directions as a function of composition and temperature in the pseudobinary systems Pr/sub x-/ Sm/sub 1-x/Co 5 , Y/sub x/Nd/sub 1-x/Co 5 , and Gd/sub x/Nd/sub 1-x/Co 5 . The saturation magnetization was determined and the anisotropy constants K 1 and K 2 were calculated from hard direction magnetization data. It was assumed that the net magnetization and anisotropy of the alloys could be divided into components representing the cobalt-cobalt, rare earth-cobalt, and rare earth-rare earth interactions. Data on YCo 5 was employed to account for the effect of the first interaction and the remaining two interactions were separated by means of some simple and physically reasonable assumptions. The resulting rare earth-rare earth magnetization and anisotropy data was then tested to see if it could be described by the single ion model. It was concluded that the single ion model did not describe the rare earth-rare earth interaction well in these alloys. This conclusion is in agreement with published results on light rare earth metals and alloys. It was further observed that some of the characteristics of the rare earth-rare earth interaction could be accounted for by assuming the existence of a band-type interaction between the rare earth atoms. All the alloys which contained Nd were found to exhibit low-temperature magnetization anomalies which were thought to be due to the existence of relatively strong basal plane anisotropy in these alloys

  4. Magnetic Phase Transition in Ion-Irradiated Ultrathin CoN Films via Magneto-Optic Faraday Effect.

    Science.gov (United States)

    Su, Chiung-Wu; Chang, Yen-Chu; Chang, Sheng-Chi

    2013-11-15

    The magnetic properties of 1 nm thick in-plane anisotropic Co ultrathin film on ZnO(0001) were investigated through successive 500 eV nitrogen-ion sputtering. Magneto-optical Faraday effects were used to observe the evolution of the ion-irradiated sample in longitudinal and perpendicular magnetic fields. The ferromagnetic phase of the initial in-plane anisotropic fcc β-Co phase transformation to β-Co(N) phase was terminated at paramagnetic CoN x phase. In-plane anisotropy with weak out-of-plane anisotropy of the Co/ZnO sample was initially observed in the as-grown condition. In the sputtering process, the N⁺ ions induced simultaneous sputtering and doping. An abrupt spin reorientation behavior from in-plane to out-of-plane was found under prolonged sputtering condition. The existence of perpendicular anisotropy measured from the out-of-plane Faraday effect may be attributed to the co-existence of residual β-Co and Co₄N exchange bonding force by the gradual depletion of Co-N thickness.

  5. Synthesis of FeSiBPNbCu nanocrystalline soft-magnetic alloys with high saturation magnetization

    Energy Technology Data Exchange (ETDEWEB)

    Li, Zongzhen [China Iron and Steel Research Institute Group, Advanced Technology and Materials Co., Ltd., Beijing 100081 (China); Wang, Anding; Chang, Chuntao [Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, 519 Zhuangshi Road, Zhenhai District, Ningbo, Zhejiang 315201 (China); Wang, Yanguo [Institute of Physics, Chinese Academy of Sciences, PO Box 603, Beijing 100080 (China); Dong, Bangshao [China Iron and Steel Research Institute Group, Advanced Technology and Materials Co., Ltd., Beijing 100081 (China); Zhou, Shaoxiong, E-mail: sxzhou@atmcn.com [China Iron and Steel Research Institute Group, Advanced Technology and Materials Co., Ltd., Beijing 100081 (China)

    2014-10-25

    Highlights: • Thermal stability of the FeSiBPNbCu alloys is strongly dependent on the Fe content. • The FeSiBPNbCu alloys with high Fe content exhibit good soft magnetic properties. • The coexistence of Cu, P and Nb leads to the excellent soft magnetic properties. - Abstract: A series of [Fe{sub 0.76+x}(Si{sub 0.4}B{sub 0.4}P{sub 0.2}){sub 0.24−x}]{sub 98.25}Nb{sub 1}Cu{sub 0.75} (x = 0–0.08) nanocrystalline soft-magnetic alloys with high saturation magnetization were synthesized by adjusting Fe content and improving the crystallization behavior, soft-magnetic properties and microstructure. It is found that the temperature interval between the two crystallization peaks is significantly enlarged from 50 to 180 °C when the Fe content of the alloys increases from x = 0 to x = 0.08, which greatly expands the optimum annealing temperature range. The alloys with higher Fe content are prone to form more uniform nanocomposite microstructure with better thermal stability and soft magnetic properties. The Fe-rich FeSiBPNbCu nanocrystalline alloys with x = 0.08 exhibit excellent soft-magnetic properties, including the high saturation magnetic flux density of up to 1.74 T, low coercivity of about 3.3 A/m and high effective permeability of more than 2.2 × 10{sup 4} at 1 kHz under a field of 1 A/m. The combination of excellent soft-magnetic properties, low cost and good productivity makes the FeSiBPNbCu alloys to be a kind of promising soft-magnetic materials for electrical and electronic industry applications.

  6. Magnetic alloy nanowire arrays with different lengths: Insights into the crossover angle of magnetization reversal process

    Energy Technology Data Exchange (ETDEWEB)

    Samanifar, S.; Alikhani, M. [Department of Physics, University of Kashan, Kashan 87317-51167 (Iran, Islamic Republic of); Almasi Kashi, M., E-mail: almac@kashanu.ac.ir [Department of Physics, University of Kashan, Kashan 87317-51167 (Iran, Islamic Republic of); Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan 87317-51167 (Iran, Islamic Republic of); Ramazani, A. [Department of Physics, University of Kashan, Kashan 87317-51167 (Iran, Islamic Republic of); Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan 87317-51167 (Iran, Islamic Republic of); Montazer, A.H. [Institute of Nanoscience and Nanotechnology, University of Kashan, Kashan 87317-51167 (Iran, Islamic Republic of)

    2017-05-15

    Nanoscale magnetic alloy wires are being actively investigated, providing fundamental insights into tuning properties in magnetic data storage and processing technologies. However, previous studies give trivial information about the crossover angle of magnetization reversal process in alloy nanowires (NWs). Here, magnetic alloy NW arrays with different compositions, composed of Fe, Co and Ni have been electrochemically deposited into hard-anodic aluminum oxide templates with a pore diameter of approximately 150 nm. Under optimized conditions of alumina barrier layer and deposition bath concentrations, the resulting alloy NWs with aspect ratio and saturation magnetization (M{sub s}) up to 550 and 1900 emu cm{sup −3}, respectively, are systematically investigated in terms of composition, crystalline structure and magnetic properties. Using angular dependence of coercivity extracted from hysteresis loops, the reversal processes are evaluated, indicating non-monotonic behavior. The crossover angle (θ{sub c}) is found to depend on NW length and M{sub s}. At a constant M{sub s}, increasing NW length decreases θ{sub c}, thereby decreasing the involvement of vortex mode during the magnetization reversal process. On the other hand, decreasing M{sub s} decreases θ{sub c} in large aspect ratio (>300) alloy NWs. Phenomenologically, it is newly found that increasing Ni content in the composition decreases θ{sub c}. The angular first-order reversal curve (AFORC) measurements including the irreversibility of magnetization are also investigated to gain a more detailed insight into θ{sub c}. - Highlights: • Magnetic alloy NWs with aspect ratios up to 550 were fabricated into hard-AAO templates. • Morphology, composition, crystal structure and magnetic properties were investigated. • Angular dependence of coercivity was used to describe the magnetization reversal process. • The crossover angle of magnetization reversal was found to depend on NW length and M{sub s}.

  7. Amorphous magnetism in Mnx Sn1-x alloys

    International Nuclear Information System (INIS)

    Drago, V.; Saitovitch, E.M.B.; Abd-Elmeguid, M.M.

    1988-01-01

    Systematic low temperature in situ 119 Sn Moessbauer effect (ME) studies in vapor quenched amorphous Mn x Sn 1-x (0.09≤ x ≤0,95) alloys between 150 and 4.2 K, are presented. Its is shown that the magnetic behavior of the system is correctly displayed by the transferred magnetic hyperfine (hf) interactions, at the 119 Sn site. A complete magnetic phase diagram is proposed, and the effect of an external magnetic field (up to about 3T) on the spin correlations in the spin-glass state is also discussed. (author) [pt

  8. Magnetic susceptibility of Dirac fermions, Bi-Sb alloys, interacting Bloch fermions, dilute nonmagnetic alloys, and Kondo alloys

    Energy Technology Data Exchange (ETDEWEB)

    Buot, Felix A., E-mail: fbuot@gmu.edu [Computational Materials Science Center, George Mason University, Fairfax, VA 22030 (United States); TCSE Center, Spintronics Group, Physics Department, University of San Carlos, Talamban, Cebu 6000 (Philippines); C& LB Research Institute, Carmen, Cebu 6005 (Philippines); Otadoy, Roland E.S.; Rivero, Karla B. [TCSE Center, Spintronics Group, Physics Department, University of San Carlos, Talamban, Cebu 6000 (Philippines)

    2017-03-01

    Wide ranging interest in Dirac Hamiltonian is due to the emergence of novel materials, namely, graphene, topological insulators and superconductors, the newly-discovered Weyl semimetals, and still actively-sought after Majorana fermions in real materials. We give a brief review of the relativistic Dirac quantum mechanics and its impact in the developments of modern physics. The quantum band dynamics of Dirac Hamiltonian is crucial in resolving the giant diamagnetism of bismuth and Bi-Sb alloys. Quantitative agreement of the theory with the experiments on Bi-Sb alloys has been achieved, and physically meaningful contributions to the diamagnetism has been identified. We also treat relativistic Dirac fermion as an interband dynamics in uniform magnetic fields. For the interacting Bloch electrons, the role of translation symmetry for calculating the magnetic susceptibility avoids any approximation to second order in the field. The expressions for magnetic susceptibility of dilute nonmagnetic alloys give a firm theoretical foundation of the empirical formulas used in fitting experimental results. The unified treatment of all the above calculations is based on the lattice Weyl-Wigner formulation of discrete phase-space quantum mechanics. For completeness, the magnetic susceptibility of Kondo alloys is also given since Dirac fermions in conduction band and magnetic impurities exhibit Kondo effect.

  9. Electrical and Magnetic Properties of Binary Amorphous Transition Metal Alloys.

    Science.gov (United States)

    Liou, Sy-Hwang

    The electrical, superconductive and magnetic properties of several binary transition metal amorphous and metastable crystalline alloys, Fe(,x)Ti(,100-x) (30 (LESSTHEQ) x (LESSTHEQ) 100), Fe(,x)Zr(,100-x) (20 (LESSTHEQ) x (LESSTHEQ) 93), Fe(,x)Hf(,100-x) (20 (LESSTHEQ) x (LESSTHEQ) 100), Fe(,x)Nb(,100 -x) (22 (LESSTHEQ) x (LESSTHEQ) 85), Ni(,x)Nb(,100-x) (20 (LESSTHEQ) x (LESSTHEQ) 80), Cu(,x)Nb(,100-x) (10 (LESSTHEQ) x (LESSTHEQ) 90) were studied over a wide composition range. Films were made using a magnetron sputtering system, and the structure of the films was investigated by energy dispersive x-ray diffraction. The composition region of each amorphous alloys system was determined and found in good agreement with a model proposed by Egami and Waseda. The magnetic properties and hyperfine interactions in the films were investigated using a conventional Mossbauer spectrometer and a ('57)Co in Rh matrix source. In all Fe-early transition metal binary alloys systems, Fe does not retain its moment in the low iron concentration region and the result is that the critical concentration for magnetic order (x(,c)) is much larger than anticipated from percolation considerations. A direct comparison between crystalline alloys and their amorphous counterparts of the same composition illustrate no clear correlation between crystalline and amorphous states. Pronounced discontinuities in the magnetic properties with variation in Fe content of all Fe-early transition metal alloys at phase boundaries separating amorphous and crystalline states have been observed. This is caused by the differences in the atomic arrangement and the electronic structure between crystalline and amorphous solids. The temperature dependence of resistivity, (rho)(T), of several binary amorphous alloys of Fe-TM (where TM = Ti, Zr, Hf, Nb etc.) has been studied from 2K to 300K. The Fe-poor (x x(,c)) samples have distinctive differences in (rho)(T) at low temperature (below 30K). All the magnetic samples

  10. Laser ablation synthesis of monodispersed magnetic alloy nanoparticles

    International Nuclear Information System (INIS)

    Seto, Takafumi; Koga, Kenji; Akinaga, Hiroyuki; Takano, Fumiyoshi; Orii, Takaaki; Hirasawa, Makoto

    2006-01-01

    Monodispersed CoPt alloy nanoparticles were synthesized by a pulsed laser ablation (PLA) technique coupled with a low-pressure operating differential mobility analyzer (LP-DMA). The CoPt alloy nanoparticles were generated by laser ablating a solid Co-Pt target. In CoPt alloy nanoparticles synthesized from a target with a Co composition of 75 at%, the nanoparticle surfaces were covered by an oxide layer and exhibited a core-shell structure. In contrast, no shell was observed in particles generated from a target with a Co:Pt ratio of 50:50 at%. According to an EDX analysis, the compositions of the individual nanoparticles were almost the same as that of the target material. Finally, the magnetic hysteresis loops of the CoPt alloy nanoparticles exhibited ferromagnetism

  11. Laser ablation synthesis of monodispersed magnetic alloy nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Seto, Takafumi, E-mail: t.seto@aist.go.jp; Koga, Kenji; Akinaga, Hiroyuki; Takano, Fumiyoshi; Orii, Takaaki; Hirasawa, Makoto [National Institute of Advanced Industrial Science and Technology (AIST), Research Consortium for Synthetic Nano-Function Materials Project (SYNAF) (Japan)

    2006-08-15

    Monodispersed CoPt alloy nanoparticles were synthesized by a pulsed laser ablation (PLA) technique coupled with a low-pressure operating differential mobility analyzer (LP-DMA). The CoPt alloy nanoparticles were generated by laser ablating a solid Co-Pt target. In CoPt alloy nanoparticles synthesized from a target with a Co composition of 75 at%, the nanoparticle surfaces were covered by an oxide layer and exhibited a core-shell structure. In contrast, no shell was observed in particles generated from a target with a Co:Pt ratio of 50:50 at%. According to an EDX analysis, the compositions of the individual nanoparticles were almost the same as that of the target material. Finally, the magnetic hysteresis loops of the CoPt alloy nanoparticles exhibited ferromagnetism.

  12. The influence of alloying on the phase formation sequence of ultra-thin nickel silicide films and on the inheritance of texture

    Science.gov (United States)

    Geenen, F. A.; Solano, E.; Jordan-Sweet, J.; Lavoie, C.; Mocuta, C.; Detavernier, C.

    2018-05-01

    The controlled formation of silicide materials is an ongoing challenge to facilitate the electrical contact of Si-based transistors. Due to the ongoing miniaturisation of the transistor, the silicide is trending to ever-thinner thickness's. The corresponding increase in surface-to-volume ratio emphasises the importance of low-energetic interfaces. Intriguingly, the thickness reduction of nickel silicides results in an abrupt change in phase sequence. This paper investigates the sequence of the silicides phases and their preferential orientation with respect to the Si(001) substrate, for both "thin" (i.e., 9 nm) and "ultra-thin" (i.e., 3 nm) Ni films. Furthermore, as the addition of ternary elements is often considered in order to tailor the silicides' properties, additives of Al, Co, and Pt are also included in this study. Our results show that the first silicide formed is epitaxial θ-Ni2Si, regardless of initial thickness or alloyed composition. The transformations towards subsequent silicides are changed through the additive elements, which can be understood through solubility arguments and classical nucleation theory. The crystalline alignment of the formed silicides with the substrate significantly differs through alloying. The observed textures of sequential silicides could be linked through texture inheritance. Our study illustrates the nucleation of a new phase drive to reduce the interfacial energy at the silicide-substrate interface as well as at the interface with the silicide which is being consumed for these sub-10 nm thin films.

  13. The role of adaptive martensite in magnetic shape memory alloys

    Czech Academy of Sciences Publication Activity Database

    Niemann, R.; Rößler, U.K.; Gruner, M.E.; Heczko, Oleg; Schultz, L.; Fähler, S.

    2012-01-01

    Roč. 14, č. 8 (2012), s. 562-581 ISSN 1438-1656 Grant - others:AVČR(CZ) M100100913 Institutional research plan: CEZ:AV0Z10100520 Keywords : Ni-Mn-Ga * magnetic shape memory alloy * ferromagnetic martensite * modulated structure * adaptive phase * mobility of twin boundary Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.608, year: 2012

  14. Magnetic properties of fcc Ni-based transition metal alloy

    Czech Academy of Sciences Publication Activity Database

    Kudrnovský, Josef; Drchal, Václav; Bruno, P.

    2008-01-01

    Roč. 77, č. 22 (2008), 224422/1-224422/8 ISSN 1098-0121 R&D Projects: GA MŠk OC 150; GA AV ČR IAA100100616; GA ČR GA202/07/0456 Institutional research plan: CEZ:AV0Z10100520 Keywords : Ni-based alloys * magnetic properties * Curie temperatures Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.322, year: 2008

  15. Simple Magnetic Device Indicates Thickness Of Alloy 903

    Science.gov (United States)

    Long, Pin Jeng; Rodriguez, Sergio; Bright, Mark L.

    1995-01-01

    Handheld device called "ferrite indicator" orginally designed for use in determining ferrite content of specimen of steel. Placed in contact with specimen and functions by indicating whether magnet attracted more strongly to specimen or to calibrated reference sample. Relative strength of attraction shows whether alloy overlay thinner than allowable.

  16. Magnetic moment distribution in Co-V alloys

    International Nuclear Information System (INIS)

    Cable, J.W.

    1982-01-01

    Magnetization and neutron scattering measurements were made on Co-V alloys containing 10, 15, and 20 at.% V to determine the local environment effects on the magnetic moment distribution in this system. The magnetization data agree with earlier results and suggest the presence of some hcp phase in the 10% sample. This was confirmed by the neutron data which showed both fcc and hcp phases in an approximate 4:1 volume ratio for this alloy. The other two samples were single phase fcc but the 15% alloy was disordered while the 20% alloy was ordered in the Cu 3 Au-type structure with the maximum order consistent with the concentration. In this ordered alloy, the excess Co occupies the V sites. These ''wrong sited'' Co atoms have 12 Co nearest neighbors and larger magnetic moments than the ''properly sited'' Co atoms which have an average of 8.8 Co nearest neighbors. The average moments associated with these two types of sites were determined from flipping-ratio measurements on the superlattice and fundamental reflections. The values obtained are 0.28 μ/sub B//Co for the proper-site atoms and 1.3 μ/sub B//Co for the wrong-site atoms. Average moments at the Co and V sites were determined from the diffuse scattering for the 10% and 15% alloys. The results are 1.38 μ/sub B//Co and -0.26 μ/sub B//V for the 10% sample and 1.05 μ/sub B//Co and -0.11 μ/sub B//V for the 15% sample

  17. Spatially Resolved Large Magnetization in Ultrathin BiFeO3

    KAUST Repository

    Guo, Er-Jia

    2017-06-19

    Here, a quantitative magnetic depth profile across the planar interfaces in BiFeO3 /La0.7 Sr0.3 MnO3 (BFO/LSMO) superlattices using polarized neutron reflectometry is obtained. An enhanced magnetization of 1.83 ± 0.16 μB /Fe in BFO layers is observed when they are interleaved between two manganite layers. The enhanced magnetic order in BFO persists up to 200 K. The depth dependence of magnetic moments in BFO/LSMO superlattices as a function of the BFO layer thickness is also explored. The results show the enhanced net magnetic moment in BFO from the LSMO/BFO interface extends 3-4 unit cells into BFO. The interior part of a thicker BFO layer has a much smaller magnetization, suggesting it still keeps the small canted AFM state. The results exclude charge transfer, intermixing, epitaxial strain, and octahedral rotations/tilts as dominating mechanisms for the large net magnetization in BFO. An explanation-one suggested by others previously and consistent with the observations-attributes the temperature dependence of the net magnetization of BFO to strong orbital hybridization between Fe and Mn across the interfaces. Such orbital reconstruction would establish an upper temperature limit for magnetic ordering of BFO.

  18. Structural and magnetic properties of nanocrystalline Fe–Co–Ni alloy processed by mechanical alloying

    International Nuclear Information System (INIS)

    Raanaei, Hossein; Eskandari, Hossein; Mohammad-Hosseini, Vahid

    2016-01-01

    In this present work, a nanostructured iron–cobalt–nickel alloy with Fe_5_0Co_3_0Ni_2_0 composition has been processed by mechanical alloying. The structural and magnetic properties have been investigated by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy and vibrating sample magnetometer. It is shown that the crystallize size reaches to about 18.7 nm after 32 h milling time. A remarkable decrease in coercivity after 16 h milling time and also a continuous increase in remanent magnetization during the mechanical alloying process are observed. Heat treatment of the samples milled at 32 and 48 h demonstrates the crystalline constituent elements and also Fe_3O_4 crystalline phase. - Highlights: • This article focuses on mechanical alloying of Fe_5_0Co_3_0Ni_2_0 composition. • Structural and magnetic properties were investigated. • Saturation magnetization was increased sharply after 16 h of milling time. • The heat treatment revealed the signature of Fe_3O_4 as well as FeNi_3 and Co crystalline phases.

  19. Structural and magnetic properties of nanocrystalline Fe–Co–Ni alloy processed by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Raanaei, Hossein, E-mail: hraanaei@yahoo.com [Department of Physics, Persian Gulf University, Bushehr 75169 (Iran, Islamic Republic of); Eskandari, Hossein [Department of Mechanical Engineering, Persian Gulf University, Bushehr 75169 (Iran, Islamic Republic of); Mohammad-Hosseini, Vahid [Department of Physics, Persian Gulf University, Bushehr 75169 (Iran, Islamic Republic of)

    2016-01-15

    In this present work, a nanostructured iron–cobalt–nickel alloy with Fe{sub 50}Co{sub 30}Ni{sub 20} composition has been processed by mechanical alloying. The structural and magnetic properties have been investigated by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray spectroscopy and vibrating sample magnetometer. It is shown that the crystallize size reaches to about 18.7 nm after 32 h milling time. A remarkable decrease in coercivity after 16 h milling time and also a continuous increase in remanent magnetization during the mechanical alloying process are observed. Heat treatment of the samples milled at 32 and 48 h demonstrates the crystalline constituent elements and also Fe{sub 3}O{sub 4} crystalline phase. - Highlights: • This article focuses on mechanical alloying of Fe{sub 50}Co{sub 30}Ni{sub 20} composition. • Structural and magnetic properties were investigated. • Saturation magnetization was increased sharply after 16 h of milling time. • The heat treatment revealed the signature of Fe{sub 3}O{sub 4} as well as FeNi{sub 3} and Co crystalline phases.

  20. Thermoelectric power in ultrathin films, quantum wires and carbon nanotubes under classically large magnetic field: Simplified theory and relative comparison

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, A.; Choudhury, S. [Electronics and Communication Engineering, Sikkim Manipal Institute of Technology, Majitar, East Sikkim 737 132 (India); Saha, S. [Electronics and Communication Engineering, Mallabhum Institute of Technology College Campus, Brajaradhanagar, P.O. Gosaipur, P.S. Bishnupur, District - Bankura 722 122 (India); Pahari, S. [Administration Department, Jadavpur University, Kolkata 700 032 (India); De, D. [Department of Computer Science Engineering, West Bengal University of Technology, BF 142, Sector 1, Kolkatta 700 064, West Bengal (India); Bhattacharya, S. [Nano Scale Device Research Laboratory, Center for Electronics Design and Technology, Indian Institute of Science, Bangalore 560 012 (India); Ghatak, K.P., E-mail: kamakhyaghatak@yahoo.co.i [Department of Electronic Science, University Calcutta, 92 Acharyya Prafulla Chandra Road, Kolkata 700 009 (India)

    2010-01-01

    We study the thermoelectric power under classically large magnetic field (TPM) in ultrathin films (UFs), quantum wires (QWs) of non-linear optical materials on the basis of a newly formulated electron dispersion law considering the anisotropies of the effective electron masses, the spin-orbit splitting constants and the presence of the crystal field splitting within the framework of k.p formalism. The results of quantum confined III-V compounds form the special cases of our generalized analysis. The TPM has also been studied for quantum confined II-VI, stressed materials, bismuth and carbon nanotubes (CNs) on the basis of respective dispersion relations. It is found taking quantum confined CdGeAs{sub 2}, InAs, InSb, CdS, stressed n-InSb and Bi that the TPM increases with increasing film thickness and decreasing electron statistics exhibiting quantized nature for all types of quantum confinement. The TPM in CNs exhibits oscillatory dependence with increasing carrier concentration and the signature of the entirely different types of quantum systems are evident from the plots. Besides, under certain special conditions, all the results for all the materials gets simplified to the well-known expression of the TPM for non-degenerate materials having parabolic energy bands, leading to the compatibility test.

  1. Constitution and magnetism of iron and its alloys

    CERN Document Server

    Pepperhoff, Werner

    2001-01-01

    Iron played an important role in the development of the industrial society and has not lost any of its significance since today. This book provides the foundations of understanding the physical nature of iron and its alloys. Basics and recent developments concerning its constitution and magnetism are presented as well as its thermal properties. The exceptional role of iron with its wide spectrum of most different technological and physical properties relies on its versatility, its polymorphism of its crystal structure and its magnetism. Therefore it is the aim of the book to link together the constitution and magnetism of iron.

  2. Spatially Resolved Large Magnetization in Ultrathin BiFeO3

    KAUST Repository

    Guo, Er-Jia; Petrie, Jonathan R.; Roldan, Manuel A.; Li, Qian; Desautels, Ryan D.; Charlton, Timothy; Herklotz, Andreas; Nichols, John; van Lierop, Johan; Freeland, John W.; Kalinin, Sergei V.; Lee, Ho Nyung; Fitzsimmons, Michael R.

    2017-01-01

    . The results show the enhanced net magnetic moment in BFO from the LSMO/BFO interface extends 3-4 unit cells into BFO. The interior part of a thicker BFO layer has a much smaller magnetization, suggesting it still keeps the small canted AFM state. The results

  3. Abnormal magnetization behaviors in Sm–Ni–Fe–Cu alloys

    International Nuclear Information System (INIS)

    Yang, W.Y.; Zhang, Y.F.; Zhao, H.; Chen, G.F.; Zhang, Y.; Du, H.L.; Liu, S.Q.; Wang, C.S.; Han, J.Z.; Yang, Y.C.; Yang, J.B.

    2016-01-01

    The magnetization behaviors in Sm–Ni–Fe–Cu alloys at low temperatures have been investigated. It was found that the hysteresis loops show wasp-waisted character at low temperatures, which has been proved to be related to the existence of multi-phases, the Fe/Ni soft magnetic phases and the CaCu 5 -type hard magnetic phase. A smooth-jump behavior of the magnetization is observed at T>5 K, whereas a step-like magnetization process appears at T<5 K. The CaCu 5 -type phase is responsible for such abnormal magnetization behavior. The magnetic moment reversal model with thermal activation is used to explain the relation of the critical magnetic field (H cm ) to the temperature (T>5 K). The reversal of the moment direction has to cross over an energy barrier of about 6.6×10 −15 erg. The step-like jumps of the magnetization below 5 K is proposed to be resulted from a sharp increase of the sample temperature under the heat released by the irreversible domain wall motion. - Highlights: • Two different magnetization mechanisms, controlled by temperature, have been found in the Sm–Ni–Fe–Cu alloys. The smooth-jump behavior of the magnetization is observed at T>5 K and the step-like magnetization process appears at T<5 K. • The magnetic moment reversal model with thermal activation has been successfully used to explain the relation of the critical magnetic field (H cm ) to the temperature (T>5 K). The energy barrier for the reversal of the moment direction has been found to be about 6.6×10 −15 erg. • The transition field for the step-like jumps is very strict, independent from the magnetic sweep rate. This is remarkably different from the similar step-like jump behavior in reference [20]. • According to the SEM images and EDX analysis, two kinds of regions are found in the alloys. The Fe–Ni–Cu regions are surrounded by the 1:5 Sm–Ni–Fe–Cu regions and shows fish-bone like structure. An interesting thing is that the Fe–Ni–Cu regions are

  4. Microstructure and properties of step aged rare earth alloy magnets

    International Nuclear Information System (INIS)

    Mishra, R.K.; Thomas, G.; Yoneyama, T.; Fukuno, A.; Ojima, T.

    1980-11-01

    Alloys with compositions Co-25.5 wt/o Sm-8 w/o Cu-15 w/o Fe-3 w/o Zr and Co-Sm-Cu-Fe-1.5 w/o Zr have been step aged to produce magnets with coercive force (iHc) in the range of 10 to 25k0e. The high coercive force magnets are typically aged at 800 to 850 0 C for 10 to 30 hours following the solution treatment at 1150 0 C. Subsequently, these are step aged to produce materials with high coercivity. The microstructure in all these alloys has a 2 phase cellular morphology with 2:17 phase surrounded by a 1:5 boundary phase. The long aging treatments at 800 to 850 0 C lead to coarsening of the two phase structure. The subsequent step-aging does not change the morphology, but only changes the chemical composition of the two phases. Best properties are obtained in materials with a coherent microstructure of optimum boundary phase thickness and optimum chemical composition. The highest values of iHc obtained so far are approx. 26k0e and approx. 16 k0e for the 3% Zr and 1.5% Zr alloys respectively. The best hard magnetic properties of (BH) max = 33 MG0e and iHc = 13k0e are for a 25% Sm-20% Fe-4 Cu-2% Zr alloy

  5. Oxygen-enabled control of Dzyaloshinskii-Moriya Interaction in ultra-thin magnetic films

    KAUST Repository

    Belabbes, Abderrezak; Bihlmayer, Gustav; Blü gel, Stefan; Manchon, Aurelien

    2016-01-01

    ferromagnets, resulting in spin spirals and nanoskyrmion lattices. Here, using relativistic first-principles calculations, we demonstrate that the magnitude and sign of DMI can be entirely controlled by tuning the oxygen coverage of the magnetic film, therefore

  6. Magnetic phase diagram of HoxTm1-x alloys

    DEFF Research Database (Denmark)

    Sarthour, R.S.; Cowley, R.A.; Ward, R.C.C.

    2000-01-01

    The magnetic phase diagram of the competing anisotropy system, Ho/Tm, has been determined by neutron-scattering techniques and the results compared with calculations based on a mean-field model. The crystal-field interactions in Ho favor alignment of the magnetic moments in the basal plane whereas......, with long-range order, were identified and the magnetic phase diagram, including a pentacritical point, determined. A mean-field model was used to explain the results and the results are in good agreement with the experimental results....... in Tm they favor alignment along the c axis. Single-crystal alloys were grown with molecular-beam epitaxy techniques in Oxford. The components of the magnetic moment alone the c direction and in the basal plane were determined from the neutron-scattering measurements. Five distinct magnetic phases...

  7. Dependence of magnetic permeability on residual stresses in alloyed steels

    Directory of Open Access Journals (Sweden)

    E. Hristoforou

    2018-04-01

    Full Text Available A method for the monitoring of residual stress distribution in steels has been developed based on non-destructive surface magnetic permeability measurements. In order to investigate the potential utilization of the magnetic method in evaluating residual stresses, the magnetic calibration curves of various ferromagnetic alloyed steels’ grade (AISI 4140, TRIP and Duplex were examined. X-Ray diffraction technique was used for determining surface residual stress values. The overall measurement results have shown that the residual stress determined by the magnetic method was in good agreement with the diffraction results. Further experimental investigations are required to validate the preliminary results and to verify the presence of a unique normalized magnetic stress calibration curve.

  8. Dependence of magnetic permeability on residual stresses in alloyed steels

    Science.gov (United States)

    Hristoforou, E.; Ktena, A.; Vourna, P.; Argiris, K.

    2018-04-01

    A method for the monitoring of residual stress distribution in steels has been developed based on non-destructive surface magnetic permeability measurements. In order to investigate the potential utilization of the magnetic method in evaluating residual stresses, the magnetic calibration curves of various ferromagnetic alloyed steels' grade (AISI 4140, TRIP and Duplex) were examined. X-Ray diffraction technique was used for determining surface residual stress values. The overall measurement results have shown that the residual stress determined by the magnetic method was in good agreement with the diffraction results. Further experimental investigations are required to validate the preliminary results and to verify the presence of a unique normalized magnetic stress calibration curve.

  9. Microstructure and magnetic properties of alnico permanent magnetic alloys with Zr-B additives

    Science.gov (United States)

    Rehman, Sajjad Ur; Jiang, Qingzheng; Ge, Qing; Lei, Weikai; Zhang, Lili; Zeng, Qingwen; ul Haq, A.; Liu, Renhui; Zhong, Zhenchen

    2018-04-01

    Alnico alloys are prepared with nominal composition of 31.4-xFe-7.0Al-36.0Co-4.0Cu-1.0Nb-14.0Ni-6.0Ti-0.6Zr-xB (x = 0.02, 0.04, 0.06, 0.08, in wt%) by arc melting and casting techniques and subsequent heat treatment. The alloys are characterized by X-ray diffraction method, optical microscope, scanning electron microscope and pulse field magnetometer by plotting magnetic hysteresis demagnetization curve. The results of HRSEM show at least two new phases at α-grain boundaries and triple junctions. These phases, when retained at low concentration, help in enhancing magnetic properties of alnico alloys by purifying spinodal phases and reducing the adverse effects of impurity elements. Two different heat treatment cycles are employed. In the first phase, the alloys are processed by using heat treatment cycles without magnetic field; and Hc of 1.35 kOe, Br of 4.87 kGs and (BH)max of 1.96 MGOe are obtained by furnace cooling below TC and subsequent tempering at 680 °C and 550 °C. In the second phase, the alloy with best magnetic properties is treated thermo-magnetically; and Hc of 1.68 kOe, Br of 7.1 kG and (BH)max of 4.45 MGOe are obtained.

  10. Magnetic susceptibility of transition metal alloys with a hcp structure

    International Nuclear Information System (INIS)

    Volkenshtejn, N.V.; Galoshina, Eh.V.; Gorina, N.B.; Korenovskij, N.L.; Polyakova, V.P.; Savitskij, E.M.

    1978-01-01

    The angular dependence of the magnetic susceptibility of single crystals of Ru-Nb, Re-W and Os-Re alloys is investigated in the region of the hexagonal closely packed structure. The spin susceptibility is estimated on the basis of available data on the electron specific heat. The principal values of the orbital component of the susceptibility are determined under the assumption of isotopy of the spin contribution to the susceptibility. In Ru-Nb alloys the magnitudes of the orbital contributions and the susceptibility anisotropy are found to increase; in Re-W the spin contribution is noticeably greater whereas the orbital susceptibility is smaller, as is the anistropy. In the Os-Re alloy the orbital contributions increase and the susceptibility anisotropy is constant. It is suggested that the addition of the second component changes the overlapping of the d-electron wave functions

  11. Magnetic regimes in amorphous Ni--Fe--P--B alloys

    International Nuclear Information System (INIS)

    Durand, J.

    1976-10-01

    A complete substitution of iron for nickel was obtained by splat-cooling in amorphous alloys of composition (Ni/sub 100-y/Fe/sub y/) 79 P 13 B 8 . Results of high-field magnetization (up to 70 kOe), ac and dc low-field susceptibility, Curie temperature, and resistivity measurements over a temperature range of 1.7 to 300 0 K are reported. The Ni 79 P 13 B 8 alloy is not ferromagnetic, but the magnetization behavior as a function of field and temperature is typically that of alloys in the critical concentration range for ferromagnetism. The Fe 79 P 13 B 8 alloy is ferromagnetic with a Curie temperature T/sub c/ of 616 0 K. For y = 1 at. percent, the Fe atoms are magnetic. The variation of the moment per Fe atom as a function of y is discussed. When y is increased, the Ni atoms are likely to be polarized progressively and the moment per Ni atom would be roughly constant for y equal to or greater than 30 at. percent. Various magnetic behaviors were defined as a function of the Fe content. The value of T/sub c/ reaches a maximum for y similarly ordered 90 at. percent and extrapolates to zero for y similarly ordered 7 at. percent. Alloys within the range 1 equal to or less than y equal to or less than 10 at. percent did not exhibit well-defined Curie transition, but sharp maxima in low-field susceptibility measurements were observed at T/sub M/. The value of T/sub M/ is proportional to y for 1 equal to or less than y equal to or less than 4 at. percent, as in classical spin-glass regimes. For 4 less than y equal to or less than 10 at. percent, the variation of T/sub M/ as a function of y implies a more complicated type of magnetic ordering (micromagnetism or superparamagnetism). Homogeneous ferromagnetic ordering emerges only for y greater than 10 at. percent. Results of resistivity measurements are discussed in relation to the magnetic properties of different regimes in the magnetic phase diagram. 6 figures, 2 tables

  12. High-resolution structural studies of ultra-thin magnetic, transition metal overlayers and two-dimensional transition metal oxides using synchrotron radiation

    International Nuclear Information System (INIS)

    Kellar, S.A.; Lawrence Berkeley National Lab., CA

    1997-05-01

    This thesis report the surface-structure determination of three, ultra-thin magnetic transition-metal films, Fe/Au(100), Mn/Ni(100), and Mn/Cu(100) using Angle-Resolved Photoemission Extended Fine Structure (ARPEFS) and photoelectron holography. These structural studies are the first to use non-s initial states in the ARPEFS procedure. This thesis also reports an ARPEFS surface-structure determination of a two-dimensional transition-metal oxide, [(1 x 1)O/W(110)] x 12. The authors have analyzed the ARPFES signal from the Au 4f 7/5 core level of the Au(1 ML)/Fe(15 ML)/Au(100) system. The analysis shows that the Fe grows layer by layer with one monolayer of gold, acting as a surfactant, remaining on top of the growing Fe layers. These surface gold atoms sit in the four-fold hollow site, 1.67 ± 0.02 A above the iron surface. The grown Fe layer is very much like the bulk, bcc iron, with an interlayer spacing of 1.43 ± 0.03 A. Analysis of the Mn 3p ARPEFS signals from c(2 x 2)Mn/Ni(100) and c(2 x 2)Mn/Cu(100) shows that the Mn forms highly corrugated surface alloys. The corrugation of the Mn/Ni(100) and Mn/Cu(100) systems are 0.24 ± 0.02 A and 0.30 ± 0.04 A respectively. In both cases the Mn is sticking above the plane of the surface substrate atoms. For the Mn/Ni(100) system the first layer Ni is contracted 4% from the bulk value. The Mn/Cu(100) system shows bulk spacing for the substrate Cu. Photoelectron holography shows that the Mn/Ni interface is very abrupt with very little Mn leaking into the second layer, while the Mn/Cu(100) case has a significant amount of Mn leaking into the second layer. A new, five-element electrostatic electron lens was developed for hemispherical electron-energy analyzers. This lens system can be operated at constant transverse or constants angular magnification, and has been optimized for use with the very small photon-spot sizes. Improvements to the hemispherical electron-energy analyzer are also discussed

  13. High-resolution structural studies of ultra-thin magnetic, transition metal overlayers and two-dimensional transition metal oxides using synchrotron radiation

    Energy Technology Data Exchange (ETDEWEB)

    Kellar, S.A. [Univ. of California, Berkeley, CA (United States). Dept. of Chemistry]|[Lawrence Berkeley National Lab., CA (United States). Advanced Light Source Div.

    1997-05-01

    This thesis report the surface-structure determination of three, ultra-thin magnetic transition-metal films, Fe/Au(100), Mn/Ni(100), and Mn/Cu(100) using Angle-Resolved Photoemission Extended Fine Structure (ARPEFS) and photoelectron holography. These structural studies are the first to use non-s initial states in the ARPEFS procedure. This thesis also reports an ARPEFS surface-structure determination of a two-dimensional transition-metal oxide, [(1 x 1)O/W(110)] x 12. The authors have analyzed the ARPFES signal from the Au 4f{sub 7/5} core level of the Au(1 ML)/Fe(15 ML)/Au(100) system. The analysis shows that the Fe grows layer by layer with one monolayer of gold, acting as a surfactant, remaining on top of the growing Fe layers. These surface gold atoms sit in the four-fold hollow site, 1.67 {+-} 0.02 A above the iron surface. The grown Fe layer is very much like the bulk, bcc iron, with an interlayer spacing of 1.43 {+-} 0.03 A. Analysis of the Mn 3p ARPEFS signals from c(2 x 2)Mn/Ni(100) and c(2 x 2)Mn/Cu(100) shows that the Mn forms highly corrugated surface alloys. The corrugation of the Mn/Ni(100) and Mn/Cu(100) systems are 0.24 {+-} 0.02 A and 0.30 {+-} 0.04 A respectively. In both cases the Mn is sticking above the plane of the surface substrate atoms. For the Mn/Ni(100) system the first layer Ni is contracted 4% from the bulk value. The Mn/Cu(100) system shows bulk spacing for the substrate Cu. Photoelectron holography shows that the Mn/Ni interface is very abrupt with very little Mn leaking into the second layer, while the Mn/Cu(100) case has a significant amount of Mn leaking into the second layer. A new, five-element electrostatic electron lens was developed for hemispherical electron-energy analyzers. This lens system can be operated at constant transverse or constants angular magnification, and has been optimized for use with the very small photon-spot sizes. Improvements to the hemispherical electron-energy analyzer are also discussed.

  14. Crystallographic, hyperfine and magnetic characterization of a maraging-400 alloy

    Energy Technology Data Exchange (ETDEWEB)

    Alves, T. J. B.; Nunes, G. C. S. [Universidade Estadual de Maringá (Brazil); Sarvezuk, P. W. C. [Universidade Tecnológica Federal do Paraná (Brazil); Ivashita, F. F. [Universidade Estadual de Maringá (Brazil); Andrade, A. M. H. de [Universidade Federal do Rio Grande do Sul (Brazil); Viegas, A. [Universidade Federal de Santa Catarina (Brazil); Paesano, A., E-mail: andrea.paesano@pq.cnpq.br [Universidade Estadual de Maringá (Brazil)

    2017-11-15

    Maraging400-like alloys were made by arc-melting iron with the alloy elements (i.e., Ni, Co, Ti and Mo), followed by a high temperature heat-treatment for solubilization. The solubilized alloys were further heat-treated (480 °C and 580 °C, by 3 h), for aging. The samples were finely characterized by X-ray diffraction (Rietveld refinement), Mössbauer spectroscopy and magnetization techniques. The results revealed that the as-solubilized sample is martensitic and ferromagnetic. Its residual induction and coercive field increase monotonically with the maximum applied field of a magnetization minor loop and both curves presented very similar shapes. The area of the minor loops varies parabolically with this maximum applied field. The aging induced an atomic rearrangement in the martensite phase, involving change in the composition and lattice parameters, reversion of austenite and the formation of the Fe {sub 3} Mo {sub 2} intermetallic compound. Comparisons are presented between the results obtained by us for these alloys and those obtained for Maraging-350 steel samples.

  15. Alloying element's substitution in titanium alloy with improved oxidation resistance and enhanced magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Ang-Yang, E-mail: ayyu@imr.ac.cn; Wei, Hua; Hu, Qing-Miao; Yang, Rui

    2017-01-15

    First-principles method is used to characterize segregation and magnetic properties of alloyed Ti/TiO{sub 2}interface. We calculate the segregation energy of the doped Ti/TiO{sub 2} interface to investigate alloying atom's distribution. The oxidation resistance of Ti/TiO{sub 2} interface is enhanced by elements Fe and Ni but reduced by element Co. Magnetism could be produced by alloying elements such as Co, Fe and Ni in the bulk of titanium and the surface of Ti at Ti/TiO{sub 2} interface. The presence of these alloying elements could transform the non-magnetic titanium alloys into magnetic systems. We have also calculated the temperature dependence of magnetic permeability for the doped and pure Ti/TiO{sub 2} interfaces. Alloying effects on the Curie temperature of the Ti/TiO{sub 2} interface have been elaborated. - Highlights: • We consider the segregation of alloying atoms on the Ti(101¯0)/TiO{sub 2}(100) interface. • Alloying the Ti//TiO{sub 2} interface with Fe and Ni has a great advantage of improving the oxidation resistance. • Fe, Co and Nican enhance the magnetic properties of the investigated system. • The variation of permeability with temperature has been presented.

  16. Microstructure and magnetic behavior of Cu–Co–Si ternary alloy synthesized by mechanical alloying and isothermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Chabri, Sumit, E-mail: sumitchabri2006@gmail.com [Department of Metallurgy & Materials Engineering, Indian Institute of Engineering Science and Technology, Shibpur, Howrah 711103 (India); Bera, S. [Department of Metallurgical & Materials Engineering, National Institute of Technology, Durgapur 713209 (India); Mondal, B.N. [Department of Central Scientific Services, Indian Association for the Cultivation of Science, Jadavpur, Kolkata 700032 (India); Basumallick, A.; Chattopadhyay, P.P. [Department of Metallurgy & Materials Engineering, Indian Institute of Engineering Science and Technology, Shibpur, Howrah 711103 (India)

    2017-03-15

    Microstructure and magnetic behavior of nanocrystalline 50Cu–40Co–10Si (at%) alloy prepared by mechanical alloying and subsequent isothermal annealing in the temperature range of 450–650 °C have been studied. Phase evolution during mechanical alloying and isothermal annealing is characterized by X-ray diffraction (XRD), differential thermal analyzer (DTA), high resolution transmission electron microscopy (HRTEM) and magnetic measurement. Addition of Si has been found to facilitate the metastable alloying of Co in Cu resulting into the formation of single phase solid solution having average grain size of 9 nm after ball milling for 50 h duration. Annealing of the ball milled alloy improves the magnetic properties significantly and best combination of magnetic properties has been obtained after annealing at 550 °C for 1 h duration.

  17. Phase diagram of Fe1-xCox ultrathin film

    International Nuclear Information System (INIS)

    Fridman, Yu.A.; Klevets, Ph.N.; Voytenko, A.P.

    2008-01-01

    Concentration-driven reorientation phase transitions in ultrathin magnetic films of FeCo alloy have been studied. It is established that, in addition to the easy-axis and easy-plane phases, a spatially inhomogeneous phase (domain structure), a canted phase, and also an 'in-plane easy-axis' phase can exist in the system. The realization of the last phase is associated with the competition between the single-ion anisotropy and the magnetoelastic interaction. The critical values of Co concentration corresponding to the phase transitions are evaluated, the types of phase transitions are determined, and the phase diagrams are constructed

  18. Magnetic properties in MnBi alloy of small crystallites for permanent magnet devices

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, S. K.; Prakash, H. R.; Ram, S., E-mail: jms.sanjeev@gmail.com [Materials Science Centre, Indian Institute of Technology, Kharagpur-721302 (India)

    2016-05-06

    A rare-earth free alloy like MnBi is a potential candidate for developing small magnets and devices. In a commercially viable method, a MnBi alloy was prepared by arc melting Mn and Bi metals in a 1:1 ratio. In terms of the X-ray diffraction a single crystalline MnBi phase is formed of the as prepared alloy. FESEM images delineate thin MnBi layers (25 – 40 nm thickness) of average EDX composition throughout the specimen. A large coercivity 5.501 kOe (6.5 emu/g magnetization) observed in an M-H at 300 K is decreased to 0.171 (9.0 emu/g magnetization) at 100 K in decreasing upon cooling.

  19. Emergence of magnetic order in ultra-thin pyrochlore iridate films

    Science.gov (United States)

    Cheema, Suraj; Serrao, Claudy; Mundy, Julia; Patankar, Shreyas; Birgeneau, Robert; Orenstein, Joseph; Salahuddin, Sayeef; Ramesh, Ramamoorthy

    We report on thickness-dependent magnetotransport in (111) - oriented Pb2Ir2O7-x (Pb227) epitaxial thin films. For thicknesses greater than 4 nm, the magnetoresistance (MR) of metallic Pb227 is positive, linear and non-saturated up to 14 T. Meanwhile at 4 nm, the conduction turns nonmetallic and the MR becomes negative and asymmetric upon field-cooling; such traits are reminiscent of all-in-all-out (AIAO) magnetic order in the insulating pyrochlore iridates. Hysteretic low-field MR dips and trained-untrained resistivity bifurcations suggest the presence of magnetic conducting domain walls within the chiral AIAO spin structure. Beyond just AIAO order, angular-dependent MR indicates a magnetic phase space hosting 2-in-2-out (2I2O) spin ice order. Such anomalous magnetotransport calls for re-evaluation of the pyrochlore iridate phase diagram, as epitaxially strained Pb227 exhibits traits reminiscent of both the insulating magnetic and metallic spin-liquid members. Furthermore, these results open avenues for realizing topological phase predictions in (111) - oriented pyrochlore slabs of kagome-triangular iridate heterostructures. This work is supported by the Office of Basic Energy Sciences of the US Department of Energy under Contract No. DE-AC02-05CH11231.

  20. Magnetic properties of fcc Ni-based transition metal alloy

    Czech Academy of Sciences Publication Activity Database

    Kudrnovský, Josef; Drchal, Václav

    2009-01-01

    Roč. 100, č. 9 (2009), s. 1193-1196 ISSN 1862-5282 R&D Projects: GA MŠk OC 150; GA AV ČR IAA100100616 Institutional research plan: CEZ:AV0Z10100520 Keywords : transition metal alloys * Ni-based * pair exchange interactions * Curie temperatures * renormalized RPA Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.862, year: 2009

  1. Magnetic shape-memory alloys: thermomechanical modelling and analysis

    Czech Academy of Sciences Publication Activity Database

    Roubíček, Tomáš; Stefanelli, U.

    2014-01-01

    Roč. 26, č. 6 (2014), s. 783-810 ISSN 0935-1175 R&D Projects: GA ČR GAP201/10/0357 Institutional support: RVO:61388998 Keywords : magnetic shape- memory alloys * martensitic phase transformation * ferro/paramagnetic phase transformation Subject RIV: BA - General Mathematics Impact factor: 1.779, year: 2014 http://link.springer.com/article/10.1007/s00161-014-0339-8#

  2. Extractive photometric determination of zirconium in magnetic alloys

    International Nuclear Information System (INIS)

    Kutyrev, I.M.; Chernysheva, G.M.; Basargin, N.N.; Mikheev, N.I.

    1996-01-01

    A method for extractive photometric determination of Zr in magnetic alloys is presented. Extractive system - trioctylamine in toluene -H 2 SO 4 -Zr ensure selective and rapid (in single extraction) separation of Zr from Fe(3), Fe(2), Co, Ni, Cu, Al, Ti, Cr(3), Mn, Si, P, Nb, and Ta. The reliability of the method is confirmed in determination of Zr in the standerd sample SS 132c

  3. Magnetic domains in martensite of Ni-Mg-Ga alloy

    International Nuclear Information System (INIS)

    Kokorin, V.V.; Babij, O.M.; Dubinko, S.V.; Prokopov, A.R.

    2006-01-01

    The structural changes attendant on intermartensitic transformation in a Ni-Mg-Ga shape memory alloy are considered using magneto-optical visualization with the help of ferrite-garnet monocrystalline films. It is established that on the intermartensitic transformation the complete reorganization of martensite macrostructure fails. Martensite crystals resulted from the basic transformation change somewhat their sizes on intermartensitic transition. The existence of large-scale labyrinth magnetic domain structure is revealed [ru

  4. Role of magnetism on the martensitic transformation in Ni–Mn-based magnetic shape memory alloys

    International Nuclear Information System (INIS)

    Sánchez-Alarcos, V.; Recarte, V.; Pérez-Landazábal, J.I.; Gómez-Polo, C.; Rodríguez-Velamazán, J.A.

    2012-01-01

    The effect of magnetism on the martensitic structural transformation has been analyzed through the evolution of the transformation temperatures of several Ni–Mn–Ga and Ni–Mn–In alloys subjected to high-temperature quenching and post-quench annealing thermal treatments. It is found that the atomic order variations associated with the thermal treatments affect the structural transformation in different ways depending on the character of the magnetic ordering in the austenitic and the martensitic phases. In particular, regardless of composition, the variation in the atomic order affects the martensitic transformation temperature only in those alloys in which at least one of the structural phases show magnetic order at the transformation temperature, whereas those transformations taking place between paramagnetic phases remain unaffected. The observed behaviors are explained in terms of the effect of the magnetic exchange coupling variations on the free energy difference between austenite and martensite. The results confirm the key role of magnetism in the martensitic transformation.

  5. Soft magnetic characteristics of laminated magnetic block cores assembled with a high Bs nanocrystalline alloy

    Directory of Open Access Journals (Sweden)

    Atsushi Yao

    2018-05-01

    Full Text Available This paper focuses on an evaluation of core losses in laminated magnetic block cores assembled with a high Bs nanocrystalline alloy in high magnetic flux density region. To discuss the soft magnetic properties of the high Bs block cores, the comparison with amorphous (SA1 block cores is also performed. In the high Bs block core, both low core losses and high saturation flux densities Bs are satisfied in the low frequency region. Furthermore, in the laminated block core made of the high Bs alloy, the rate of increase of iron losses as a function of the magnetic flux density remains small up to around 1.6 T, which cannot be realized in conventional laminated block cores based on amorphous alloy. The block core made of the high Bs alloy exhibits comparable core loss with that of amorphous alloy core in the high-frequency region. Thus, it is expected that this laminated high Bs block core can achieve low core losses and high saturation flux densities in the high-frequency region.

  6. Tailoring of magnetic properties of ultrathin epitaxial Fe films by Dy doping

    Directory of Open Access Journals (Sweden)

    A. A. Baker

    2015-07-01

    Full Text Available We report on the controlled modification of relaxation parameters and magnetic moments of epitaxial Fe thin films through Dy doping. Ferromagnetic resonance measurements show that an increase of Dy doping from 0.1% to 5% gives a tripling in Gilbert damping, and more importantly a strongly enhanced anisotropic damping that can be qualitatively understood through the slow-relaxing impurity model. X-ray magnetic circular dichroism measurements show a pronounced suppression of the orbital moment of the Fe with Dy doping, leading to an almost threefold drop in the orbital to spin moment ratio, ml/ms. Doping with Dy can therefore be used to control both dynamic and static properties of thin ferromagnetic films for improved performance in spintronics device applications, mediated through the antiferromagnetic interaction of the 4f and 3d states.

  7. Tailoring of magnetic properties of ultrathin epitaxial Fe films by Dy doping

    Energy Technology Data Exchange (ETDEWEB)

    Baker, A. A. [Department of Physics, Clarendon Laboratory, University of Oxford, Oxford, OX1 3PU (United Kingdom); Magnetic Spectroscopy Group, Diamond Light Source, Didcot, OX11 0DE (United Kingdom); Figueroa, A. I.; Laan, G. van der [Magnetic Spectroscopy Group, Diamond Light Source, Didcot, OX11 0DE (United Kingdom); Hesjedal, T. [Department of Physics, Clarendon Laboratory, University of Oxford, Oxford, OX1 3PU (United Kingdom)

    2015-07-15

    We report on the controlled modification of relaxation parameters and magnetic moments of epitaxial Fe thin films through Dy doping. Ferromagnetic resonance measurements show that an increase of Dy doping from 0.1% to 5% gives a tripling in Gilbert damping, and more importantly a strongly enhanced anisotropic damping that can be qualitatively understood through the slow-relaxing impurity model. X-ray magnetic circular dichroism measurements show a pronounced suppression of the orbital moment of the Fe with Dy doping, leading to an almost threefold drop in the orbital to spin moment ratio, m{sub l}/m{sub s}. Doping with Dy can therefore be used to control both dynamic and static properties of thin ferromagnetic films for improved performance in spintronics device applications, mediated through the antiferromagnetic interaction of the 4f and 3d states.

  8. Nanocrystalline Fe-Pt alloys. Phase transformations, structure and magnetism

    Energy Technology Data Exchange (ETDEWEB)

    Lyubina, J.V.

    2006-12-21

    This work has been devoted to the study of phase transformations involving chemical ordering and magnetic properties evolution in bulk Fe-Pt alloys composed of nanometersized grains. Nanocrystalline Fe{sub 100-x}Pt{sub x} (x=40-60) alloys have been prepared by mechanical ball milling of elemental Fe and Pt powders at liquid nitrogen temperature. The as-milled Fe-Pt alloys consist of {proportional_to} 100 {mu}m sized particles constituted by randomly oriented grains having an average size in the range of 10-40 nm. Depending on the milling time, three major microstructure types have been obtained: samples with a multilayer-type structure of Fe and Pt with a thickness of 20-300 nm and a very thin (several nanometers) A1 layer at their interfaces (2 h milled), an intermediate structure, consisting of finer lamellae of Fe and Pt (below approximately 100 nm) with the A1 layer thickness reaching several tens of nanometers (4 h milled) and alloys containing a homogeneous A1 phase (7 h milled). Subsequent heat treatment at elevated temperatures is required for the formation of the L1{sub 0} FePt phase. The ordering develops via so-called combined solid state reactions. It is accompanied by grain growth and thermally assisted removal of defects introduced by milling and proceeds rapidly at moderate temperatures by nucleation and growth of the ordered phases with a high degree of the long-range order. In a two-particle interaction model elaborated in the present work, the existence of hysteresis in recoil loops has been shown to arise from insufficient coupling between the low- and the high-anisotropy particles. The model reveals the main features of magnetisation reversal processes observed experimentally in exchange-coupled systems. Neutron diffraction has been used for the investigation of the magnetic structure of ordered and partially ordered nanocrystalline Fe-Pt alloys. (orig.)

  9. An experimental study of the magnetic ordering in Pd-based Fe and Mn alloys

    International Nuclear Information System (INIS)

    Verbeek, B.H.

    1979-01-01

    This thesis presents the results of an investigation on the magnetic ordering phenomena in some Pd based alloys with small concentrations of magnetic impurities. It has been the object to explore the ordering mechanisms in these alloys which lead to various types of magnetism at low temperature. The experimental techniques used are described. (Auth.)

  10. The correlation between mechanical stress and magnetic anisotropy in ultrathin films

    International Nuclear Information System (INIS)

    Sander, D.

    1999-01-01

    The impact of stress-driven structural transitions and of film strain on the magnetic properties of nm ferromagnetic films is discussed. The stress-induced bending of film-substrate composites is analysed to derive information on film stress due to lattice mismatch or due to surface-stress effects. The magneto-elastic coupling in epitaxial films is determined directly from the magnetostrictive bending of the substrate. The combination of stress measurements with magnetic investigations by the magneto-optical Kerr effect (MOKE) reveals the modification of the magnetic anisotropy by film stress. Stress-strain relations are derived for various epitaxial orientations to facilitate the analysis of the substrate curvature. Biaxial film stress and magneto-elastic coupling coefficients are measured in epitaxial Fe films in situ on W single-crystal substrates. Tremendous film stress of more than 10 GPa is measured in pseudomorphic Fe layers, and the important role of film stress as a driving force for the formation of misfit distortions and for inducing changes of the growth mode in monolayer thin films is presented. The direct measurement of the magneto-elastic coupling in epitaxial films proves that the magnitude and sign of the magneto-elastic coupling deviate from the respective bulk value. Even a small film strain of order 0.1% is found to induce a significant change of the effective magneto-elastic coupling coefficient. This peculiar behaviour is ascribed to a second-order strain dependence of the magneto-elastic energy density, in contrast to the linear strain dependence that is valid for bulk samples. (author)

  11. Capping layer-tailored interface magnetic anisotropy in ultrathin Co2FeAl films

    International Nuclear Information System (INIS)

    Belmeguenai, M.; Zighem, F.; Chérif, S. M.; Gabor, M. S.; Petrisor, T.; Tiusan, C.

    2015-01-01

    Co 2 FeAl (CFA) thin films of various thicknesses (2 nm ≤ d ≤ 50 nm) have been grown on (001) MgO single crystal substrates and then capped with Cr, V, and Ta. Their magnetic and structural properties have been studied by x-ray diffraction (XRD), vibrating sample magnetometry, and broadband microstrip ferromagnetic resonance (MS-FMR). The XRD revealed that the films are epitaxial with the cubic [001] CFA axis normal to the substrate plane and that the chemical order varies from the B2 phase to the A2 phase when decreasing the thickness. The deduced lattice parameters showed that the Cr-capped films exhibit a larger tetragonal distortion, as compared with the films capped with V or Ta. The presence of magnetic dead layers has been observed in CFA samples capped with V and Ta but not in the case of the Cr-capped ones. The effective magnetization, deduced from the fit of MS-FMR measurements, increases (decreases) linearly with the CFA inverse thickness (1/d) for the Cr-capped (Ta-capped) films while it is constant for the V-capped ones. This allows quantifying the perpendicular surface anisotropy coefficients of −0.46 erg/cm 2 and 0.74 erg/cm 2 for Cr and Ta-capped films, respectively. Moreover, the fourfold and the uniaxial anisotropy fields, measured in these films, showed different trends with a respect to the CFA inverse thickness. This allows inferring that a non-negligible part of the fourfold magnetocrystalline term is of interfacial origin

  12. Mechanically alloyed PrFeB nanocrystalline magnets

    International Nuclear Information System (INIS)

    Kaszuwara, W.; Leonowicz, M.

    1998-01-01

    Mechanically alloyed PrFeB nanocrystalline magnets were prepared by extensive ball milling of Pr, Fe and Fe 80 B 20 powders, followed by diffusion annealing. After milling, the material consisted of nanocrystalline α-Fe crystallites embedded in amorphous Pr-rich matrix. Thermomagnetic and calorimetric investigations of the transformations which occurred during annealing showed that the amorphous phase crystallised at 240 C, leading to the formation of crystalline Pr having lattice constants 10% greater than those shown in the ASTM data. This fact indicated that mechanical alloying and low temperature annealing led to the formation of a solid solution of either Fe or B in Pr, which does not exist in the equilibrium state. The Pr 2 Fe 14 B phase was subsequently formed within a temperature range of 420-620 C. The magnetic properties of magnets depend on the phase structure and grain size. Milling time appears to be a decisive processing parameter for the tailoring of the magnetic properties. Depending on the phase structure, the coercivities varied from 100 to 1200 kA/m and, respectively, the remanences from 0.98 T to 0.6 T. The highest maximum energy product was 80 kJ/m 3 . (orig.)

  13. Controlling the formation and stability of ultra-thin nickel silicides - An alloying strategy for preventing agglomeration

    Science.gov (United States)

    Geenen, F. A.; van Stiphout, K.; Nanakoudis, A.; Bals, S.; Vantomme, A.; Jordan-Sweet, J.; Lavoie, C.; Detavernier, C.

    2018-02-01

    The electrical contact of the source and drain regions in state-of-the-art CMOS transistors is nowadays facilitated through NiSi, which is often alloyed with Pt in order to avoid morphological agglomeration of the silicide film. However, the solid-state reaction between as-deposited Ni and the Si substrate exhibits a peculiar change for as-deposited Ni films thinner than a critical thickness of tc = 5 nm. Whereas thicker films form polycrystalline NiSi upon annealing above 450 ° C , thinner films form epitaxial NiSi2 films that exhibit a high resistance toward agglomeration. For industrial applications, it is therefore of utmost importance to assess the critical thickness with high certainty and find novel methodologies to either increase or decrease its value, depending on the aimed silicide formation. This paper investigates Ni films between 0 and 15 nm initial thickness by use of "thickness gradients," which provide semi-continuous information on silicide formation and stability as a function of as-deposited layer thickness. The alloying of these Ni layers with 10% Al, Co, Ge, Pd, or Pt renders a significant change in the phase sequence as a function of thickness and dependent on the alloying element. The addition of these ternary impurities therefore changes the critical thickness tc. The results are discussed in the framework of classical nucleation theory.

  14. Cobalt-Free Permanent Magnet Alloys.

    Science.gov (United States)

    1984-10-01

    ThC Ferrites (Zn, Mn. Cu, Fe)O A12O. Al TiC Kaolin Al203.Si02-Fe2O3 Fe2O3 Li B4C Spodumene LiAI (SiOs) 2 ThO2 Ni UC Rhodonite NtnO. SiO2 MnOs Fe TaC...minutes. X-ray diffraction pattern indicated the presence of magnetic T phase. Hysteresis loop was measured on the heat treated powder dispersed in wax...fmgei * T phse Hysersi loo was mesue on the. heat - treated ,--". " powder dispersed in wax... The’ result wer as"- follows: • , " • "• . I TABLE 6

  15. Magnetic structures of holmium-lutetium alloys and superlattices

    DEFF Research Database (Denmark)

    Swaddling, P.P.; Cowley, R.A.; Ward, R.C.C.

    1996-01-01

    Alloys and superlattices of Ho and Lu have been grown using molecular beam epitaxy and their magnetic structures determined using neutron-scattering techniques. The 4f moments in the alloys form a helix at all compositions with the moments aligned in the basal plane perpendicular to the wave vector...... of the helix remaining coherent through the nonmagnetic Lu blocks. The neutron scattering from the superlattices is consistent with a model in which there are different phase advances of the helix turn angle through the Ho and Lu blocks, but with a localized moment on the Ho sites only. A comparison...... of Ho and Lu. At low temperatures, for superlattices with fewer than approximately twenty atomic planes of Ho, the Ho moments within a block undergo a phase transition from helical to ferromagnetic order, with the coupling between successive blocks dependent on the thickness of the Lu spacer....

  16. The Recovery of a Magnetically Dead Layer on the Surface of an Anatase (Ti,CoO2 Thin Film via an Ultrathin TiO2 Capping Layer

    Directory of Open Access Journals (Sweden)

    Thantip S. Krasienapibal

    2017-03-01

    Full Text Available The effect of an ultrathin TiO2 capping layer on an anatase Ti0.95Co0.05O2−δ (001 epitaxial thin film on magnetism at 300 K was investigated. Films with a capping layer showed increased magnetization mainly caused by enhanced out-of-plane magnetization. In addition, the ultrathin capping layer was useful in prolonging the magnetization lifetime by more than two years. The thickness dependence of the magnetic domain structure at room temperature indicated the preservation of magnetic domain structure even for a 13 nm thick film covered with a capping layer. Taking into account nearly unchanged electric conductivity irrespective of the capping layer’s thickness, the main role of the capping layer is to prevent surface oxidation, which reduces electron carriers on the surface.

  17. Magnetic hysteresis and refrigeration capacity of Ni–Mn–Ga alloys near Martensitic transformation

    International Nuclear Information System (INIS)

    Bin, Fu; Yi, Long; Jing-Fang, Duan; Chao-Lun, Wang; Yong-Qin, Chang; Rong-Chang, Ye; Guang-Heng, Wu

    2010-01-01

    This paper studies the magnetic hysteresis and refrigeration capacity of Ni-Mn-Ga alloys in detail during heating and cooling isothermal magnetisation processes. The Ni-Mn-Ga alloys show larger magnetic hysteresis when they transform from austenite to martensite, but smaller magnetic hysteresis when they transform from martensite to austenite. This behaviour is independent of either the pure Ni-Mn-Ga alloys or the alloys doped with other elements. Because of the existence of the magnetic hysteresis, the relation between the magnetic entropy change and refrigeration capacity is not simply linear. For practical consideration, magnetocaloric effect of Ni-Mn-Ga alloys should be investigated both on cooling and heating processes. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  18. Hyperfine magnetic fields at 111Cd in Heusler alloys

    International Nuclear Information System (INIS)

    Styczen, B.; Szytula, A.; Walus, W.

    1977-01-01

    The magnitudes and signs of the hyperfine magnetic field on 111 Cd nuclei at Z sites in the ordered ferromagnetic Heusler alloys X 2 MnZ and XMnZ (where X is Cu, Ni, Pd while Z is In, Sn and Sb) have been investigated at liquid nitrogen and room temperatures using TDPAC method. Their signs have been found to be negative. The results have been compared with the predictions of Caroli-Blandin and Campbell-Blandin models and RKKY theory. (author)

  19. Determination of localized magnetic moments in Fe-Cr-Al alloys and the electron structure

    International Nuclear Information System (INIS)

    Blau, W.

    1977-01-01

    The localized magnetic moments of Fe and Cr are determined by combination of saturation magnetization measurements and magnetic diffuse scattering. Power series characterizing the interactions between the different kinds of atoms in the alloys are chosen to describe the concentration dependence of the magnetic moments. The different terms are discussed on the basis of band structure models valid for dilute alloys taking into account their modification by impurity interactions. (author)

  20. Curie temperature and magnetic phase transition of nanostructured ultrathin Fe/GaAs (001). Size dependence and relevance of dipolar coupling

    Energy Technology Data Exchange (ETDEWEB)

    Meier, Roland

    2009-07-01

    In the present work the impact of lateral patterning of ultrathin ferromagnetic films down to the nanometer range on the magnetic phase transition has been investigated. In this respect on the one hand a size effect on the Curie temperature and, referring to that, the relevance of dipolar coupling were a matter of particular interest. On the other hand the characteristics of the critical behavior itself, becoming apparent by the accurate evaluation of the curvature shape of the magnetization as a function of temperature at T{sub c}, were analyzed with regard to potential and expected size effects. The investigation of similar nanostructures with respect to an effect on Curie temperature respectively phase transition may draw up a correlation. Therefore more than hundred samples were fabricated for this work extensively by means of MBE (Molecular Beam Epitaxy) and ESL (Electron Beam Epitaxy) methods, measured by MOKE (Magneto-Optical Kerr Effect) technique and systematically evaluated. (orig.)

  1. Nature of the magnetic susceptibility of dysprosium. Paramagnetic susceptibility of dysprosium - yttrium alloys

    International Nuclear Information System (INIS)

    Demidov, V.G.; Levitin, R.Z.; Chistyakov, O.D.

    1976-01-01

    The paramagnetic susceptibility of single crystals of dysprosium-yttirum alloys is measured in the basal plane and along the hexagonal axis. It is shown that the susceptibility of the alloys obeys the Curie-Weiss law, the effective magnetic moments allong the different directions being the same and the paramagnetic Curie temperatures being different. The difference between the paramagnetic Curie temperatures in the basal plane and along the hexagonal axis is independent of the dysprosium concentration in the alloy. As a comparison with the theoretical models of magnetic anisotropy shows, this is an indication that the magnetic anisotropy of dysprosium - yttrium alloys is of a single-ion nature

  2. Ultrafast magnetization dynamics of lanthanide metals and alloys

    Energy Technology Data Exchange (ETDEWEB)

    Sultan, Muhammad

    2012-05-14

    In this study, the laser-induced magnetization dynamics of the lanthanide ferromagnets Gadolinium (Gd), Terbium (Tb) and their alloys is investigated using femtosecond (fs) time-resolved x-ray magnetic circular dichroism (XMCD), the magneto-optical Kerr effect (MOKE) and magnetic second harmonic generation (MSHG). The magnetization dynamics is analyzed from the time scale of a few fs up to several hundred picoseconds (ps). The contributions of electrons, phonons, spin fluctuations, as well as the temporal regimes corresponding to the spin-orbit and exchange interactions are disentangled. In addition to possible applications in magnetic storage devices, understanding magnetization dynamics in lanthanides is also important because of their different magnetic structure compared to well-studied itinerant ferromagnets. Lanthanides are model Heisenberg-ferromagnets with localized 4f magnetic moments and long range magnetic ordering through indirect exchange interaction. By optical excitation of the conduction electrons, which mediate the exchange interaction, and studying the induced dynamics of the localized 4f and delocalized 5d6s magnetic moments, one can obtain insight into the angular momentum transfer at ultrafast time scales. Moreover, lanthanides offer the possibility to tune spin-lattice coupling via the 4f shell occupation and the concomitant changes in the 4f spin and orbital moments due to Hund's rules. Utilizing this fact, the importance of spin-lattice coupling in laser-induced demagnetization is also analyzed by comparing the magnetization dynamics in Gd and Tb. By investigating the magnetization dynamics of localized 4f moments of Gd and Tb using time-resolved XMCD, it is found that the demagnetization proceeds in both metals in two time scales, following fs laser excitation, which are classified as: (i) non-equilibrium (t > 1 ps), with respect to equilibration of electron and phonon temperatures. The

  3. Atomic and magnetic correlations in a copper - 5% manganese alloy

    Energy Technology Data Exchange (ETDEWEB)

    Murani, A P; Schaerpf, O; Andersen, K [Institut Max von Laue - Paul Langevin (ILL), 38 - Grenoble (France); Raphel, R [Centre National de la Recherche Scientifique (CNRS), 38 - Grenoble (France)

    1997-04-01

    Interest in magnetism of Cu-Mn alloys has been revived and sustained by a number of very interesting neutron investigations on single-crystal samples which show `spin-density wave` (SDW) peaks at incommensurate wave-vectors. Recently such peaks have been observed even in very dilute samples with Mn concentration as low as {approx} 0.5 at.%. The proposed interpretation by the authors that these peaks represent incommensurate antiferromagnetic ordering, therefore, questions the widely-held view that at low enough temperatures the solute spins in this and similar alloys freeze with random or quasi-random orientations, forming a spin-glass state. Atomic and magnetic correlations have been investigated in a single crystal of Cu-5 at.% Mn within the first Brillouin zone using polarised neutrons and making use of the multi-angle three-dimensional polarisation analysis capability of the D7 spectrometer as a firs step in our aim to shed further light on the phenomenon. (author). 6 refs.

  4. Enhancement of magnetic properties of Co{sub 2}MnSi Heusler alloy prepared by mechanical alloying method

    Energy Technology Data Exchange (ETDEWEB)

    Rabie, Naeemeh; Gordani, Gholam Reza; Ghasemi, Ali, E-mail: ali13912001@yahoo.com

    2017-07-15

    Highlights: • Ferromagnetic Heusler alloys of Co{sub 2}MnSi were synthesized at low temperature. • There is an at least 30% reduction in the phase formation temperature. • Saturation magnetization of alloy was increased significantly after annealing. - Abstract: Ferromagnetic Heusler alloys of Co{sub 2}MnSi were synthesized by mechanical alloying method at low temperature. The effect of milling time and annealing process on structural and magnetic properties of ferromagnetic alloy samples were studied by X-ray diffraction, scanning electron microscopy and vibration sample magnetometer methods, respectively. Structural characteristics such as crystallite size, phase percentage, and lattice parameter determined using the Rietveld method. The values of these parameters were obtained 362.9 nm, 5.699 Å and 98.7%, respectively for annealed sample. Magnetization studies show that the Co2MnSi phase is formed at 15 h of milling and is optimized after 20 h of milling. VSM results showed that saturation magnetization (M{sub s}) of milled samples reduces from 112 to 75 (emu/g) with increasing milling time and then increased gradually to 95 emu/g. The effect of post-annealing on the structural and magnetic properties of milled samples was also investigated. The saturation magnetization of annealed sample (120 emu/g) is higher than the optimum milled sample (95 emu/g) due to increasing preferential ordered L2{sub 1} structure.

  5. Enhancement of magnetic properties of Co2MnSi Heusler alloy prepared by mechanical alloying method

    International Nuclear Information System (INIS)

    Rabie, Naeemeh; Gordani, Gholam Reza; Ghasemi, Ali

    2017-01-01

    Highlights: • Ferromagnetic Heusler alloys of Co 2 MnSi were synthesized at low temperature. • There is an at least 30% reduction in the phase formation temperature. • Saturation magnetization of alloy was increased significantly after annealing. - Abstract: Ferromagnetic Heusler alloys of Co 2 MnSi were synthesized by mechanical alloying method at low temperature. The effect of milling time and annealing process on structural and magnetic properties of ferromagnetic alloy samples were studied by X-ray diffraction, scanning electron microscopy and vibration sample magnetometer methods, respectively. Structural characteristics such as crystallite size, phase percentage, and lattice parameter determined using the Rietveld method. The values of these parameters were obtained 362.9 nm, 5.699 Å and 98.7%, respectively for annealed sample. Magnetization studies show that the Co2MnSi phase is formed at 15 h of milling and is optimized after 20 h of milling. VSM results showed that saturation magnetization (M s ) of milled samples reduces from 112 to 75 (emu/g) with increasing milling time and then increased gradually to 95 emu/g. The effect of post-annealing on the structural and magnetic properties of milled samples was also investigated. The saturation magnetization of annealed sample (120 emu/g) is higher than the optimum milled sample (95 emu/g) due to increasing preferential ordered L2 1 structure.

  6. High field magnetic behavior in Boron doped Fe{sub 2}VAl Heusler alloys

    Energy Technology Data Exchange (ETDEWEB)

    Venkatesh, Ch., E-mail: venkyphysicsiitm@gmail.com [Department of Physics, Indian Institute of Technology, Kharagpur (India); DCMP & MS, Tata Institute of Fundamental Research, Mumbai (India); Vasundhara, M., E-mail: vasu.mutta@gmail.com [Materials Science and Technology Division, National Institute for Interdisciplinary Science and Technology, CSIR, Trivandrum 695019 (India); Srinivas, V. [Department of Physics, Indian Institute of Technology, Chennai (India); Rao, V.V. [Cryogenic Engineering Centre, Indian Institute of Technology, Kharagpur (India)

    2016-11-15

    We have investigated the magnetic behavior of Fe{sub 2}VAl{sub 1−x}B{sub x} (x=0, 0.03, 0.06 and 0.1) alloys under high temperature and high magnetic field conditions separately. Although, the low temperature DC magnetization data for the alloys above x>0 show clear magnetic transitions, the zero field cooled (ZFC) and field cooled (FC) curves indicate the presence of spin cluster like features. Further, critical exponent (γ) deduced from the initial susceptibility above the T{sub c}, does not agree with standard models derived for 3 dimensional long range magnetic systems. The deviation in γ values are consistent with the short range magnetic nature of these alloys. We further extend the analysis of magnetic behavior by carrying the magnetization measurements at high temperatures and high magnetic fields distinctly. We mainly emphasize the following observations; (i) The magnetic hysteresis loops show sharp upturns at lower fields even at 900 K for all the alloys. (ii) High temperature inverse susceptibility do not overlap until T=900 K, indicating the persistent short range magnetic correlations even at high temperatures. (iii) The Arrott's plot of magnetization data shows spontaneous moment (M{sub S}) for the x=0 alloy at higher magnetic fields which is absent at lower fields (<50 kOe), while the Boron doped samples show feeble M{sub S} at lower fields. The origin of this short range correlation is due to presence of dilute magnetic heterogeneous phases which are not detected from the X-ray diffraction method. - Highlights: • Short range magnetic character has been confirmed by the critical exponents analysis. • Magnetoresistace is about −14% with non-saturating tendency even at 150 kOe for Fe{sub 2}VAl alloy. • Boron doped Fe{sub 2}VAl alloys show a weak magnetism even at T=900 K.

  7. Magnetic induction heating of FeCr nanocrystalline alloys

    International Nuclear Information System (INIS)

    Gómez-Polo, C.; Larumbe, S.; Pérez-Landazábal, J.I.; Pastor, J.M.; Olivera, J.; Soto-Armañanzas, J.

    2012-01-01

    In this work the thermal effects of magnetic induction heating in (FeCr) 73.5 Si 13.5 Cu 1 B 9 Nb 3 amorphous and nanocrystalline wires were analyzed. A single piece of wire was immersed in a glass capillary filled with water and subjected to an ac magnetic field (frequency, 320 kHz). The initial temperature rise enabled the determination of the effective Specific Absorption Rate (SAR). Maximum SAR values are achieved for those samples displaying high magnetic susceptibility, where the eddy current losses dominate the induction heating behavior. Moreover, the amorphous sample with Curie temperature around room temperature displays characteristic features of self-regulated hyperthermia. - Highlights: ► Amorphous and nanocrystalline Fe based alloys with tailored Curie temperature of the amorphous phase. ► Induction heating effects under the action of a ac magnetic field. ► Self-regulated characteristics based on the control of the Curie temperature. ► Dominant role of the eddy-current losses in the self-heating phenomena.

  8. Microstructure and magnetic properties of rapidly solidified nanocrystalline Fe81Zr7B12 alloy

    International Nuclear Information System (INIS)

    Xiong, X.Y.; Muddle, B.C.; Finlayson, T.R.

    2000-01-01

    Full text: Nanocrystalline Fe-Zr-B alloys have aroused extensive research interest due to their high saturation magnetization. There have been several studies [Suzuki et al., 1994; Kim et al., 1994] of the effect of boron on the formation of nanocrystalline structure and magnetic properties, showing that the addition of boron to Fe-Zr alloys improves the glass-forming ability and refines the primary bcc α-Fe grains during crystallization. However, when the boron content is increased to 8 at.%, the magnetic permeability is observed to decrease. There has been no detailed work to date concerning the microstructural evolution and magnetic properties in those alloys with higher boron content

  9. High thermal stability in W/MgO/CoFeB/W/CoFeB/W stacks via ultrathin W insertion with perpendicular magnetic anisotropy

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Yi; Yu, Tao [School of Physics and Nuclear Energy Engineering, Beihang University, Beijing 100191 (China); Zhu, Zhengyong; Zhong, Huicai [Institute of Microelectronics, Chinese Academy of Sciences, Beijing 100029 (China); Khamis, Khamis Masoud [School of Physics and Nuclear Energy Engineering, Beihang University, Beijing 100191 (China); Zhu, Kaigui, E-mail: kgzhu@buaa.edu.cn [School of Physics and Nuclear Energy Engineering, Beihang University, Beijing 100191 (China); Key Laboratory of Micro-Nano Measurement-Manipulation and Physics, Ministry of Education, Beihang University, Beijing 100191 (China)

    2016-07-15

    The perpendicular magnetic anisotropy (PMA) of a series of top MgO/CoFeB/W stacks were studied. In these stacks, the thickness of CoFeB is limited in a range of 1.1–2.2 nm. It was found that the stack can still maintain PMA in a 1.9 nm thick CoFeB free layer. Besides, we investigated the thermal stability factor ∆ of a spin transfer torque magnetic random access memory (STT-MRAM) by inserting an ultra-thin W film of 0.8 nm between two CoFeB films. The result shows a clear PMA behavior for the samples with CoFeB thickness up to 2.5 nm, and an in-plane magnetic anisotropy (IMA) when the CoFeB is thicker than 2.5 nm. Moreover, the thermal stability factor ∆ of the CoFeB stack with W insertion is about 132 for a 50 nm size STT-MRAM device, which is remarkably improved compared to 112 for a sample without W insertion. Our results represent an alternative way to realize the endurance at high annealing temperature, high-density and high ∆ in STT-MRAM device by ultra-thin W insertion. - Highlights: • The MgO/CoFeB/W multilayer can still maintain PMA in a CoFeB thickness of 1.9 nm. • The sample with 2.5 nm thickness of CoFeB by W insertion can still maintain PMA. • The sample with W insertion can still maintain PMA until the annealing temperature as high as 350 °C. • The thermal stability factor ∆ of sample with W insertion could be increase to about 132 for a 50 nm size STT-MRAM device.

  10. Neutron irradiation effects on magnetic properties of some Heusler alloys

    International Nuclear Information System (INIS)

    Onodera, Hideya; Shinohara, Takeshi; Yamamoto, Hisao; Watanabe, Hiroshi

    1975-01-01

    The neutron irradiation effects were studied with measurements of temperature dependence of magnetization in ordered and disordered Heusler alloys. The irradiation was carried out in JMTR with a total flux of fast neutrons of 10 20 nvt. Fully ordered Cu 2 MnIn, partially ordered Cu 2 MnAl and completely disordered Cu 2 MnSn were prepared with various temperature treatments. The magnetization-temperature curves of each specimen were measured before and after irradiation. In the irradiated Cu 2 MnIn, the disordering by the irradiation gave rise to a decrease of magnetization, and the temperature dependence of magnetization showed that the disordered region contained various regions with different degrees of disorder. For the distribution of the disordered region, the calculation based on the theory of temperature spike by Seitz and Koekler gave a feasible result that a disordered region comprised a central core with a radius of 5.4 A which was completely disordered and a periphery of 3.3 A thickness which was partially disordered. From the magnetization-temperature curves of Cu 2 MnAl, it was considered that the disordered regions induced by the irradiation had different properties from those induced by the heat treatment. The former were the localized and comprised regions corresponding to various degrees of disorder, while the latter spread spatially in a wide range with a certain degree of disorder. The ordering by enhanced diffusion occurred simultaneously to an extent comparable to the disordering, and so it played an important role in the magnetization in the partially disordered Cu 2 MnAl. In the disordered Cu 2 MnSn, however, the ordering effect was very small. It is supposed to be difficult for the A2 structure to transform into the L2 1 structure by the enhanced diffusion. (auth.)

  11. Novel pre-alloyed powder processing of modified alnico 8: Correlation of microstructure and magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, I. E., E-mail: andersoni@ameslab.gov; Kassen, A. G.; White, E. M. H.; Zhou, L.; Tang, W.; Palasyuk, A.; Dennis, K. W.; McCallum, R. W.; Kramer, M. J. [Ames Laboratory (USDOE), Iowa State University, Ames, Iowa 50011 (United States)

    2015-05-07

    Progress is reviewed on development of an improved near-final bulk magnet fabrication process for alnico 8, as a non-rare earth permanent magnet with promise for sufficient energy density and coercivity for electric drive motors. This study showed that alnico bulk magnets in near-final shape can be made by simple compression molding from spherical high purity gas atomized pre-alloyed powder. Dwell time at peak sintering temperature (1250 °C) greatly affected grain size of the resulting magnet alloys. This microstructure transformation was demonstrated to be useful for gaining partially aligned magnetic properties and boosting energy product. While a route to increased coercivity was not identified by these experiments, manufacturability of bulk alnico magnet alloys in near-final shapes was demonstrated, permitting further processing and alloy modification experiments that can target higher coercivity and better control of grain anisotropy during grain growth.

  12. Influence of Fe2O3 on alloying and magnetic properties of Fe–Al

    Czech Academy of Sciences Publication Activity Database

    Jirásková, Yvonna; Buršík, Jiří; Zitovski, O.; Cuda, J.

    2014-01-01

    Roč. 186, AUG (2014), s. 73-78 ISSN 0921-5107 R&D Projects: GA ČR(CZ) GAP108/11/1350; GA MŠk 7AMB12SK009 Institutional support: RVO:68081723 Keywords : Fe–Al alloy * Mechanical alloying * Microstructure * Intergrain interaction * magnetic properties Subject RIV: BM - Solid Matter Physics ; Magnetism; BM - Solid Matter Physics ; Magnetism (UFM-A) Impact factor: 2.169, year: 2014

  13. Effect of external magnetic effect of external magnetic field annealing on magnetic texture of Mo containing NANOPERM-type alloys

    International Nuclear Information System (INIS)

    Kanuch, T.; Miglierini, M.; Greneche, J.-M.; Skorvanek, I.; Schaaf, P.

    2006-01-01

    External magnetic fields are known to modify microstructure of materials during their solidification and/or crystallisation. In an external magnetic field strong particle to particle interactions lead to a highly anisotropic microstructure. If the alloy is in ferromagnetic state, stronger particle magnetization - external field interactions and also particle-to-particle couplings are expected. To reveal the magnetic texture, originally amorphous precursors of Fe 76 Mo 8 Cu 1 B 15 were annealed at 510 grad C and 550 grad C in an external longitudinal and transverse magnetic field of 0.025 T and 0.8 T, respectively. Magnetic measurements were applied to follow the changes of saturation magnetization and coercive force. Moessbauer experiments were performed at room and liquid nitrogen temperature to provide an information about orientation of with respect to an external magnetic field. The obtained results were compared with those achieved on zero field annealed samples. We can conclude that such a low external magnetic fields applied during crystallisation cause no significant changes in the magnetic microstructural anisotropy. Afterwards, magneto-optical Kerr effect (MOKE) was applied to investigate possible changes at the surface of the ribbon as a function of annealing temperature and applied magnetic field. We observed combination of uniaxial anisotropy, which originates from the shape anisotropy, and four-fold anisotropy, which is a contribution from crystallites of nanometre size embedded in the residual amorphous matrix. We expect more pronounced effects on cobalt substituted (Fe1 -x Co x ) 76 Mo 8 Cu 1 B 15 alloy. (authors)

  14. Structure, magnetic ordering, and spin filtering efficiency of NiFe{sub 2}O{sub 4}(111) ultrathin films

    Energy Technology Data Exchange (ETDEWEB)

    Matzen, S.; Moussy, J.-B., E-mail: jean-baptiste.moussy@cea.fr [CEA, IRAMIS, SPCSI, F-91191 Gif-sur-Yvette (France); Wei, P. [Francis Bitter Magnet Laboratory, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139 (United States); Gatel, C. [CEMES-CNRS, F-31055 Toulouse (France); Cezar, J. C. [ESRF, F-38043 Grenoble (France); Arrio, M. A.; Sainctavit, Ph. [IMPMC, F-75015 Paris (France); Moodera, J. S. [Francis Bitter Magnet Laboratory, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139 (United States); Physics Department, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139 (United States)

    2014-05-05

    NiFe{sub 2}O{sub 4}(111) ultrathin films (3–5 nm) have been grown by oxygen-assisted molecular beam epitaxy and integrated as effective spin-filter barriers. Structural and magnetic characterizations have been performed in order to investigate the presence of defects that could limit the spin filtering efficiency. These analyses have revealed the full strain relaxation of the layers with a cationic order in agreement with the inverse spinel structure but also the presence of antiphase boundaries. A spin-polarization up to +25% has been directly measured by the Meservey-Tedrow technique in Pt(111)/NiFe{sub 2}O{sub 4}(111)/γ-Al{sub 2}O{sub 3}(111)/Al tunnel junctions. The unexpected positive sign and relatively small value of the spin-polarization are discussed, in comparison with predictions and previous indirect tunnelling magnetoresistance measurements.

  15. Structural and magnetic properties of Fe60Al40 alloys prepared by means of a magnetic mill

    International Nuclear Information System (INIS)

    Bernal-Correa, R.; Rosales-Rivera, A.; Pineda-Gomez, P.; Salazar, N.A.

    2010-01-01

    A study on synthesis, structural and magnetic characterization of Fe 60 Al 40 (at.%) alloys prepared by means of mechanical alloying process is presented. The mechanical alloying was performed using a milling device with magnetically controlled ball movement (Uni-Ball-Mill 5 equipment) at several milling times. The characterization was carried out via X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). The effects of milling time on the structural state, morphological evolution and magnetic behaviour of the Fe 60 Al 40 (at.%) alloys are discussed. Besides, in this current study we emphasize the result that indicating a ferro-para-ferromagnetic transition from a correlation between X-ray diffraction and magnetization data.

  16. Electrodeposition of quaternary alloys in the presence of magnetic field

    Science.gov (United States)

    2010-01-01

    Electrodeposition of Ni-Co-Fe-Zn alloys was done in a chloride ion solution with the presence and absence of a Permanent Parallel Magnetic Field (PPMF). The PPMF was applied parallel to the cathode surface. The deposition profile was monitored chronoamperometrically. It was found that the electrodeposition current was enhanced in the presence of PPMF (9 T) compared to without PPMF. The percentage of current enhancement (Γ%) was increased in the presence of PPMF, with results of Γ% = 11.9%, 16.7% and 18.5% at -1.1, -1.2 and -1.3 V respectively for a 2400 sec duration. In chronoamperometry, the Composition Reference Line (CRL) for Ni was around 57%, although the nobler metals (i.e. Ni, Co) showed anomalous behaviour in the presence of Zn and Fe. The anomalous behaviour of the Ni-Co-Fe-Zn electrodeposition was shown by the Energy Dispersive X-Ray (EDX) results. From Atomic Force Microscopy (AFM) measurements, it was found that the surface roughness of the Ni-Co-Fe-Zn alloy films decreased in the presence of a PPMF. PMID:20604934

  17. Microstructural and magnetic characterization of iron precipitation in Ni-Fe-Al alloys

    International Nuclear Information System (INIS)

    Duman, Nagehan; Mekhrabov, Amdulla O.; Akdeniz, M. Vedat

    2011-01-01

    The influence of annealing on the microstructural evolution and magnetic properties of Ni 50 Fe x Al 50-x alloys for x = 20, 25, and 30 has been investigated. Solidification microstructures of as-cast alloys reveal coarse grains of a single B2 type β-phase and typical off eutectic microstructure consisting of proeutectic B2 type β dendrites and interdendritic eutectic for x = 20 and x > 20 at.% Fe respectively. However, annealing at 1073 K results in the formation of FCC γ-phase particles along the grain boundaries as well as grain interior in x = 20 at.% Fe alloy. The volume fraction of interdentritic eutectic regions tend to decrease and their morphologies start to degenerate by forming FCC γ-phase for x > 20 at.% Fe alloys with increasing annealing temperatures. Increasing Fe content of alloys induce an enhancement in magnetization and a rise in the Curie transition temperature (T C ). Temperature scan magnetic measurements and transmission electron microscopy reveal that a transient rise in the magnetization at temperatures well above the T C of the alloys would be attributed to the precipitation of a nano-scale ferromagnetic BCC α-Fe phase. Retained magnetization above the Curie transition temperature of alloy matrix, together with enhanced room temperature saturation magnetization of alloys annealed at favorable temperatures support the presence of ferromagnetic precipitates. These nano-scale precipitates are shown to induce significant precipitation hardening of the β-phase in conjunction with enhanced room temperature saturation magnetization in particular when an annealing temperature of 673 K is used. - Research Highlights: → Evolution of microstructure and magnetic properties with varying Fe content. → Transient rise in magnetization via the formation of ferromagnetic phase. → Enhancements in saturation magnetization owing to precipitated ferromagnetic phase. → Nanoscale precipitation of ferromagnetic BCC α-Fe confirmed by TEM.

  18. Structure and magnetic properties of nanostructured MnNi alloys fabricated by mechanical alloying and annealing treatments

    Science.gov (United States)

    Jalal, T.; Hossein Nedjad, S.; Khalili Molan, S.

    2013-05-01

    A nearly equiatomic MnNi alloy was fabricated from the elemental powders by means of mechanical alloying in a planetary ball milling apparatus. X-ray diffraction (XRD), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and measurements of magnetization were conducted to identify the structural states and properties of the prepared alloys. After ball milling for 20 h, a disordered face-centered cubic (f.c.c.) solid solution was formed which increased in lattice parameter by further milling up to 50 h. An exothermic reaction took place at around 300-400°C during continuous heating of the disordered f.c.c. solid solution. This reaction is attributed to a structural ordering leading to the formation of a face-centered tetragonal (f.c.t.) phase with L10 type ordering. Examination of the magnetic properties indicated that the structural ordering increases remnant magnetization and decreases coerecivity.

  19. Effect of heat treatment on the microstructure and properties of Ni based soft magnetic alloy.

    Science.gov (United States)

    Li, Chunhong; Ruan, Hui; Chen, Dengming; Li, Kejian; Guo, Donglin; Shao, Bin

    2018-04-20

    A Ni-based alloy was heat treated by changing the temperature and ambient atmosphere of the heat treatment. Morphology, crystal structure, and physical performance of the Ni-based alloy were characterized via SEM, XRD, TEM, and PPMS. Results show that due to the heat treatment process, the grain growth of the Ni-based alloy and the removal of impurities and defects are promoted. Both the orientation and stress caused by rolling are reduced. The permeability and saturation magnetization of the alloy are improved. The hysteresis loss and coercivity are decreased. Higher heat treatment temperature leads to increased improvement of permeability and saturation magnetization. Heat treatment in hydrogen is more conducive to the removal of impurities. At the same temperature, the magnetic performance of the heat-treated alloy in hydrogen is better than that of an alloy with heat treatment in vacuum. The Ni-based alloy shows an excellent magnetic performance on 1,373 K heat treatment in hydrogen atmosphere. In this process, the µ m , B s , P u , and H c of the obtained alloy are 427 mHm -1 , 509 mT, 0.866 Jm -3 , and 0.514 Am -1 , respectively. At the same time, the resistivity of alloy decreases and its thermal conductivity increases in response to heat treatment. © 2018 Wiley Periodicals, Inc.

  20. Crystal field symmetry and magnetic interactions in rare earth-silver amorphous alloys

    International Nuclear Information System (INIS)

    Pappa, Catherine.

    1979-01-01

    A study has been made of the following rare earth based amorphous alloys: Ndsub(x)Agsub(100-x), Prsub(x)Agsub(100-x), Gdsub(x)Agsub(100-x), Tlsub(x)Agsub(100-x). In rare earth based amorphous alloys, the symmetrical distribution of the crystal field is very wide and hence not very sensitive to the content of the alloys. The existence of preponderant negative magnetic interactions leads to an upset magnetic order, the magnetization of a small volume not being nil. The magnetic behaviour of alloys with a small concentration of rare earths is governed by the existence of clusters of statistical origin, within which a rare earth ion has at least one other rare earth ion in the position of first neighbour. The presence of a high anisotropy at low temperatures make the magnetic interactions between clusters inoperative [fr

  1. Structural, thermal and magnetic investigations on immiscible Ag–Co nanocrystalline alloy with addition of Mn

    Energy Technology Data Exchange (ETDEWEB)

    Mondal, B.N., E-mail: bholanath_mondal@yahoo.co.in [Department of Central Scientific Services, Indian Association for the Cultivation of Science, Jadavpur, Kolkata 700 032 (India); Chabri, S. [Department of Metallurgy and Materials Engineering, Bengal Engineering and Science University, Shibpur, Howrah 711 103 (India); Sardar, G. [Department of Zoology, Baruipur College, South 24 Parganas 743610 (India); Nath, D.N. [Department of Physical Chemistry, Indian Association for the Cultivation of Science, Jadavpur, Kolkata 700 032 (India); Chattopadhyay, P.P. [Department of Metallurgy and Materials Engineering, Bengal Engineering and Science University, Shibpur, Howrah 711 103 (India)

    2016-08-15

    50Ag–50Co (at%) and 40Ag–40Co–20Mn (at%) alloys prepared by ball milling up to 50 h and subsequent isothermal annealing at the temperature range of 350–650 °C for 1 h has been investigated systematically. Mn promotes early formation of the nanostructures and solid solutions of the alloys by ball milling. In contrast, annealing at 350 °C of Ag–Co alloy resulted the dissolution of hcp Co. Annealing above 350 °C decomposes the metastable Ag–Co alloy into the polycrystalline and segregated Ag and fcc Co. Enthalpy of mixing of both the alloy has increased with increase in milling time. Both the nanocrystalline alloys prepared by ball milling and annealing have been revealed the ferromagnetic behavior. The most significant improvement of magnetic properties is yielded in as-milled Ag–Co–Mn alloy obtained after annealing at 550 °C for 1 h. - Highlights: • A complete solid solution of Ag–Co–Mn alloy obtained after 50 h of milling. • A complete solid solution of milled Ag–Co alloy forms annealed at 350 {sup °}C for 1 h. • Precipitation of fcc Co are observed after annealing above 350 °C. • Enthalpy of mixing of the alloys increased with increase in milling time. • The superior magnetic properties achieved of Ag–Co–Mn alloy annealed at 550 °C.

  2. Magnetic properties of Zn(P/sub x/As/sub 1-x/)2 alloys

    International Nuclear Information System (INIS)

    Vitkina, T.Z.; Smolyarenko, E.M.; Trukhan, V.M.

    1987-01-01

    The authors study the magnetic properties of Zn(P/sub x/As/sub 1-x/) 2 alloys. The concentration-dependent magnetic susceptibility of these alloys is shown, as is the temperature dependence of the magnetic susceptibility in solid solutions of the alloys. The diamagnetic susceptibility associated with the valence electrons displays a marked change for a transition to the bound state inasmuch as the valence electrons constitute the chemical bonding in the crystal. The diamagnetic component of the susceptibility of the valence electrons is calculated according to the MO LCAO approximation on the assumption that there is sp 3 -hybridization of the atomic wave function

  3. Effects of phase constitution of Zr-Nb alloys on their magnetic susceptibilities

    International Nuclear Information System (INIS)

    Nomura, Naoyuki; Tanaka, Yuko; Suyalatu; Kondo, Ryota; Doi, Hisashi; Tsutsumi, Yusuke; Hanawa, Takao

    2009-01-01

    The magnetic susceptibilities and microstructures of Zr-Nb binary alloys were investigated to develop a new metallic biomaterial with a low magnetic susceptibility for magnetic resonance imaging (MRI). The magnetic susceptibility was measured with a magnetic susceptibility balance, and the microstructure was evaluated with an X-ray diffractometer (XRD), an optical microscope (OM), and a transmission electron microscope (TEM). Zr-Nb alloys as-cast showed a minimum value of magnetic susceptibility between 3 and 9 mass% Nb, and the value abruptly increased up to 20 mass% Nb, followed by a gradual increase with the increase of the Nb content. XRD, OM, and TEM revealed that the minimum value of the susceptibility was closely related to the appearance of the athermal ω phase in the β phase. Since the magnetic susceptibility of Zr-3Nb alloy consisting of an α' phase was as low as that of Zr-9Nb alloy consisting of the β and ω phases, that of the ω phase was lower than that of the α' and β phases. When Zr-16Nb alloy was heat-treated, the isothermal ω phase appeared, and, simultaneously, the magnetic susceptibility decreased. Therefore, the ω phase contributes to the decrease of the magnetic susceptibility, independently of the formation process of the ω phase. The magnetic susceptibility of the Zr-3Nb alloy as-cast was almost one-third that of Ti-6Al-4V alloy, which is commonly used for medical implant devices. Zr-Nb alloys are useful for medical devices used under MRI. (author)

  4. Field Induced Magnetic Moments in a Metastable Iron-Mercury Alloy

    DEFF Research Database (Denmark)

    Pedersen, M.S.; Mørup, Steen; Linderoth, Søren

    1996-01-01

    The magnetic properties of a metastable iron-mercury alloy have been investigated in the temperature range from 5 to 200 K by Mossbauer spectroscopy and magnetization measurements. At low temperature the magnetic moment per iron atom is larger than af alpha-Fe. The effective spontaneous magnetic ....... It was found that the field-induced increase of the magnetic moment in the metastable iron-mecury alloy was about 0.06 Bohr magnetons per iron atom in the temperature range from 5 to 200 K for a field change from 6 to 12 T....

  5. Magnetic Susceptibility of liquid Gd-NM (NM = Cu, Ga, Ge alloys

    Directory of Open Access Journals (Sweden)

    Shimakura Hironori

    2017-01-01

    Full Text Available For rare earth alloys, the indirect interaction of RKKY is at work between rare-earth atoms. Therefore, the magnetism of them depends on the number of conduction electrons and the distance between rare-earth metals. In this work, to reveal the relationship between the number of conduction electrons and magnetic property of rare earth metal alloys, magnetic susceptibility measurements for liquid Gd-NM (NM = Cu, Ga, Ge was performed by Faraday method. As the results, it was observed that the sign of paramagnetic Curie temperature of Cu-Gd alloys are positive at all composition, while Ga-Gd and Ge-Gd alloys show negative paramagnetic Curie temperature at certain composition. Moreover, it was indicated when the alloy at certain composition shows highest melting temperature, it has the lowest paramagnetic Curie temperature.

  6. Phase stability and magnetism in NiPt and NiPd alloys

    International Nuclear Information System (INIS)

    Paudyal, Durga; Mookerjee, Abhijit

    2004-01-01

    We show that the differences in stability of 3d-5d NiPt and 3d-4d NiPd alloys arise mainly due to relativistic corrections. The magnetic properties of disordered NiPd and NiPt alloys also differ due to these corrections, which lead to increase in the separation between the s-d bands of 5d elements in these alloys. For the magnetic case we also analyse the results in terms of splitting of majority and minority spin d band centres of the 3d elements. We further examine the effect of relativistic corrections to the pair energies and order-disorder transition temperatures in these alloys. The magnetic moments and Curie temperatures have also been studied along with the short range ordering/segregation effects in NiPt/NiPd alloys

  7. Temperature dependence of magnetic susceptibility in the vicinity of martensitic transformation in ferromagnetic shape memory alloys

    Czech Academy of Sciences Publication Activity Database

    Zablotskyy, Vitaliy A.; Pérez-Landazábal, J.I.; Recarte, V.; Gómez-Polo, C.

    2010-01-01

    Roč. 22, č. 31 (2010), 316004/1-316004/7 ISSN 0953-8984 Institutional research plan: CEZ:AV0Z10100520 Keywords : shape memory alloys * magnetic susceptibility * martensitic transition * magnetic domains Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.332, year: 2010

  8. Design and development of novel MRI compatible zirconium- ruthenium alloys with ultralow magnetic susceptibility

    Science.gov (United States)

    Li, H.F.; Zhou, F.Y.; Li, L.; Zheng, Y.F.

    2016-01-01

    In the present study, novel MRI compatible zirconium-ruthenium alloys with ultralow magnetic susceptibility were developed for biomedical and therapeutic devices under MRI diagnostics environments. The results demonstrated that alloying with ruthenium into pure zirconium would significantly increase the strength and hardness properties. The corrosion resistance of zirconium-ruthenium alloys increased significantly. High cell viability could be found and healthy cell morphology observed when culturing MG 63 osteoblast-like cells and L-929 fibroblast cells with zirconium-ruthenium alloys, whereas the hemolysis rates of zirconium-ruthenium alloys are alloys and Ti-based alloys, the magnetic susceptibilities of the zirconium-ruthenium alloys (1.25 × 10−6 cm3·g−1–1.29 × 10−6 cm3·g−1 for zirconium-ruthenium alloys) are ultralow, about one-third that of Ti-based alloys (Ti–6Al–4V, ~3.5 × 10−6 cm3·g−1, CP Ti and Ti–6Al–7Nb, ~3.0 × 10−6 cm3·g−1), and one-sixth that of Co–Cr alloys (Co–Cr–Mo, ~7.7 × 10−6 cm3·g−1). Among the Zr–Ru alloy series, Zr–1Ru demonstrates enhanced mechanical properties, excellent corrosion resistance and cell viability with lowest magnetic susceptibility, and thus is the optimal Zr–Ru alloy system as therapeutic devices under MRI diagnostics environments. PMID:27090955

  9. Tunable magnetic properties by interfacial manipulation of L1(0)-FePt perpendicular ultrathin film with island-like structures.

    Science.gov (United States)

    Feng, C; Wang, S G; Yang, M Y; Zhang, E; Zhan, Q; Jiang, Y; Li, B H; Yu, G H

    2012-02-01

    Based on interfacial manipulation of the MgO single crystal substrate and non-magnetic AIN compound, a L1(0)-FePt perpendicular ultrathin film with the structure of MgO/FePt-AIN/Ta was designed, prepared, and investigated. The film is comprised of L1(0)-FePt "magnetic islands," which exhibits a perpendicular magnetic anisotropy (PMA), tunable coercivity (Hc), and interparticle exchange coupling (IEC). The MgO substrate promotes PMA of the film because of interfacial control of the FePt lattice orientation. The AIN compound is doped to increase the difference of surface energy between FePt layer and MgO substrate and to suppress the growth of FePt grains, which takes control of island growth mode of FePt atoms. The AIN compound also acts as isolator of L1(0)-FePt islands to pin the sites of FePt domains, resulting in the tunability of Hc and IEC of the films.

  10. Magnetic excitations in CuMn spin-glass alloys

    International Nuclear Information System (INIS)

    Tsunoda, Y.; Kunitomi, N.; Cable, J.W.

    1985-01-01

    Recent neutron scattering measurements have helped to clarify two important features of CuMn spin glasses. Murani and co-workers have studied the dynamical behavior of spin-glass systems and have observed characteristic ferromagnetic spin correlations with a broad distribution of relaxation times and a dynamical freezing process. By means of the polarization analysis technique, Cable and co-workers have observed the coexistence of two types of magnetic short-range order (MSRO): one is a modulated-spin structure, and the other is a ferromagnetic cluster associated with the atomic short-range order (ASRO). These ordered regions produce diffraction maxima which are found at the (1 1/2 +/- delta 0) and the (1 1/2 0) reciprocal lattice points, respectively. Both of these observations seem to be essential for understanding the CuMn spin-glass system. However, the physical relationship of these properties is not yet understood. The authors have studied the inelastic scattering of neutrons around the magnetic diffuse peak positions of a Cu/sub 78.7/Mn/sub 21.3/ single crystal. The spin-glass freezing temperature of a CuMn alloy with this Mn concentration is estimated to be T/sub f/ approx. 90 K. Most of the data were taken by scanning along the [0 1 0] direction from the (1 0 0) to the (1 1 0) reciprocal lattice points

  11. Magnetization curves of sintered heavy tungsten alloys for applications in MRI-guided radiotherapy

    International Nuclear Information System (INIS)

    Kolling, Stefan; Oborn, Bradley M.; Keall, Paul J.; Horvat, Joseph

    2014-01-01

    Purpose: Due to the current interest in MRI-guided radiotherapy, the magnetic properties of the materials commonly used in radiotherapy are becoming increasingly important. In this paper, measurement results for the magnetization (BH) curves of a range of sintered heavy tungsten alloys used in radiation shielding and collimation are presented. Methods: Sintered heavy tungsten alloys typically contain >90 % tungsten and 0 and the BH curve derived. Results: The iron content of the alloys was found to play a dominant role, directly influencing the magnetizationM and thus the nonlinearity of the BH curve. Generally, the saturation magnetization increased with increasing iron content of the alloy. Furthermore, no measurable magnetization was found for all alloys without iron content, despite containing up to 6% of nickel. For two samples from different manufacturers but with identical quoted nominal elemental composition (95% W, 3.5% Ni, 1.5% Fe), a relative difference in the magnetization of 11%–16% was measured. Conclusions: The measured curves show that the magnetic properties of sintered heavy tungsten alloys strongly depend on the iron content, whereas the addition of nickel in the absence of iron led to no measurable effect. Since a difference in the BH curves for two samples with identical quoted nominal composition from different manufacturers was observed, measuring of the BH curve for each individual batch of heavy tungsten alloys is advisable whenever accurate knowledge of the magnetic properties is crucial. The obtained BH curves can be used in FEM simulations to predict the magnetic impact of sintered heavy tungsten alloys

  12. Perpendicular magnetic anisotropy in CoXPd100-X alloys for magnetic tunnel junctions

    Science.gov (United States)

    Clark, B. D.; Natarajarathinam, A.; Tadisina, Z. R.; Chen, P. J.; Shull, R. D.; Gupta, S.

    2017-08-01

    CoFeB/MgO-based perpendicular magnetic tunnel junctions (p-MTJ's) with high anisotropy and low damping are critical for spin-torque transfer random access memory (STT-RAM). Most schemes of making the pinned CoFeB fully perpendicular require ferrimagnets with high damping constants, a high temperature-grown L10 alloy, or an overly complex multilayered synthetic antiferromagnet (SyAF). We report a compositional study of perpendicular CoxPd alloy-pinned Co20Fe60B20/MgO based MTJ stacks, grown at moderate temperatures in a planetary deposition system. The perpendicular anisotropy of the CoxPd alloy films can be tuned based on the layer thickness and composition. The films were characterized by alternating gradient magnetometry (AGM), energy-dispersive X-rays (EDX), and X-ray diffraction (XRD). Current-in-plane tunneling (CIPT) measurements have also been performed on the compositionally varied CoxPd MTJ stacks. The CoxPd alloy becomes fully perpendicular at approximately x = 30% (atomic fraction) Co. Full-film MTJ stacks of Si/SiO2/MgO (13)/CoXPd100-x (50)/Ta (0.3)/CoFeB (1)/MgO (1.6)/CoFeB (1)/Ta (5)/Ru (10), with the numbers enclosed in parentheses being the layer thicknesses in nm, were sputtered onto thermally oxidized silicon substrates and in-situ lamp annealed at 400 °C for 5 min. CIPT measurements indicate that the highest TMR is observed for the CoPd composition with the highest perpendicular magnetic anisotropy.

  13. Synthesis and magnetic properties of rare-earth free MnBi alloy: A high-energy hard magnetic material

    Science.gov (United States)

    Sharma, Sanjeev Kumar; Prakash, H. R.; Ram, S.; Pradhan, D.

    2018-04-01

    MnBi is a rare-earth free high-energy magnetic material useful for the permanent magnet based devices. In a simple method, a MnBi alloy was prepared by arc melting method using Mn and Bi metals in 60:40 atomic ratio. In terms of the X-ray diffraction, a crystalline MnBi phase is formed with Bi as impurity phase of the as-prepared alloy. FESEM image of chemically etched sample shows small grains throughout the alloy. SEAD pattern and lattice image were studied to understand the internal microstructure of the alloy. The thermomagnetic curves measured in ZFC-FC cycles over 5-380 K temperatures at 500 Oe field, shows the induced magnetization of 5-25 % in the sample. The coercivity values, 7.455 kOe (13.07 emu/g magnetization) at 380 K, and 5.185k Oe (14.75 emu/g magnetization) at 300 K, are observed in the M-H hysteresis loops. A decreased value 0.181kOe (18.05 emu/g magnetization) appears at 100 K due to the change in the magnetocrystalline anisotropy. The results are useful to fabricate small MnBi magnets for different permanent magnets based devices.

  14. Co and In doped Ni-Mn-Ga magnetic shape memory alloys: a thorough structural, magnetic and magnetocaloric study

    Czech Academy of Sciences Publication Activity Database

    Fabbrici, S.; Porcari, G.; Cugini, F.; Solzi, M.; Kamarád, Jiří; Arnold, Zdeněk; Cabassi, R.; Albertini, F.

    2014-01-01

    Roč. 16, č. 4 (2014), s. 2204-2222 ISSN 1099-4300 Institutional support: RVO:68378271 Keywords : magnetic shape memory materials * magnetocaloric effect * multifunctional Heusler alloys Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.502, year: 2014

  15. Magnetic properties of Co and Ni based alloy nanoparticles dispersed in a silica matrix

    Energy Technology Data Exchange (ETDEWEB)

    De Julian Fernandez, C. E-mail: dejulian@padova.infm.it; Sangregorio, C.; Mattei, G.; Maurizio, C.; Battaglin, G.; Gonella, F.; Lascialfari, A.; Lo Russo, S.; Gatteschi, D.; Mazzoldi, P.; Gonzalez, J.M.; D' Acapito, F

    2001-04-01

    A comparative study of the magnetic properties of Co and Ni based alloy nanoparticles (Ni-Co, Ni-Cu and Co-Cu) formed in a silica matrix by ion implantation is presented. Different ion doses and implantation sequences were realized in order to obtain different nanostructures. The structural and magnetic properties observed for the Cu{sub 50}Ni{sub 50} nanoparticles are similar to those of the Cu{sub 60}Ni{sub 40} bulk alloy. The crystal structure of Co{sub x}Ni{sub 1-x} (0{<=}x{<=}1) nanoparticles is similar to that of the corresponding bulk alloy. The magnetic properties depend on the ion-implanted dose and on the alloy composition. The samples prepared by implanting a 15x10{sup 16} ions/cm{sup 2} total dose contain nanoparticles, which are superparamagnetic at room temperature and their magnetic behavior is influenced by dipolar interparticle interactions. The magnetization of the CoNi samples at high magnetic field is larger than that of the corresponding bulk alloy and follows the same composition dependence of that quantity measured in the alloy.

  16. Magnetic properties of Co and Ni based alloy nanoparticles dispersed in a silica matrix

    International Nuclear Information System (INIS)

    De Julian Fernandez, C.; Sangregorio, C.; Mattei, G.; Maurizio, C.; Battaglin, G.; Gonella, F.; Lascialfari, A.; Lo Russo, S.; Gatteschi, D.; Mazzoldi, P.; Gonzalez, J.M.; D'Acapito, F.

    2001-01-01

    A comparative study of the magnetic properties of Co and Ni based alloy nanoparticles (Ni-Co, Ni-Cu and Co-Cu) formed in a silica matrix by ion implantation is presented. Different ion doses and implantation sequences were realized in order to obtain different nanostructures. The structural and magnetic properties observed for the Cu 50 Ni 50 nanoparticles are similar to those of the Cu 60 Ni 40 bulk alloy. The crystal structure of Co x Ni 1-x (0≤x≤1) nanoparticles is similar to that of the corresponding bulk alloy. The magnetic properties depend on the ion-implanted dose and on the alloy composition. The samples prepared by implanting a 15x10 16 ions/cm 2 total dose contain nanoparticles, which are superparamagnetic at room temperature and their magnetic behavior is influenced by dipolar interparticle interactions. The magnetization of the CoNi samples at high magnetic field is larger than that of the corresponding bulk alloy and follows the same composition dependence of that quantity measured in the alloy

  17. Magnetic properties of amorphous alloys of Fe with La, Lu, Y, and Zr

    International Nuclear Information System (INIS)

    Heiman, N.; Kazama, N.

    1979-01-01

    In order to study the systematics of the Fe-Fe exchange in amorphous rare-earth--Fe alloys, without the complications associated with the magnetic characteristics of the rare-earth elements, amorphous films of Fe alloyed with La, Lu, Y, and Zr have been prepared with a wide range of Fe concentrations. Magnetization and Moessbauer-effect measurements were made. The magnetic properties of the alloys depended critically on the choice of rare earth (or rare-earth-like element). YFe and LuFe alloys were found to have spin-glass characteristics while LaFe and ZrFe alloys were found to be ferromagnetic, but with evidence that exchange fluctuations were nearly as large as the average exchange. Thus the nature of the Fe-Fe exchange interaction depends critically upon the species of the rare earth. The most important parameter in determining the magnetic behavior of these alloys appears to be the size of the rare-earth atom, with large rare-earth atoms resulting in a smaller ratio of exchange fluctuations to exchange. The same dependence of the magnetic properties upon rare-earth size appears to be important in the case of magnetic-rare-earth atoms; however, the effect of rare-earth--Fe exchange also becomes important and these effects are discussed

  18. Mechanochemical synthesis of nanocrystalline Fe and Fe–B magnetic alloys

    International Nuclear Information System (INIS)

    Mohammadi, Majid; Ghasemi, Ali; Tavoosi, Majid

    2016-01-01

    Mechanochemical synthesis and magnetic characterization of nanocrystalline Fe and Fe–B magnetic alloys was the goal of this study. In this regard, different Fe_2O_3–B_2O_3 powder mixtures with sufficient amount of CaH_2 were milled in a planetary ball mill in order to produce nanocrystalline Fe, Fe_9_5B_5 and Fe_8_5B_1_5 alloys. The produced samples were characterized using X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). The results showed that, nanocrystalline Fe, Fe_9_5B_5 and Fe_8_5B_1_5 alloys can be successfully synthesized by the reduction reaction of Fe_2O_3 and B_2O_3 with CaH_2 during mechanical alloying. The structure of produced Fe_9_5B_5 and Fe_8_5B_1_5 alloys was a combination of Fe and Fe_2B phases with average crystallite sizes of about 15 and 10 nm, respectively. The produced nanocrystalline alloys exhibited soft magnetic properties with the coercivity and saturation of magnetization in the range of 170–240 Oe and 9–28 emu/g, respectively. Increasing the boron content has a destructive effect on soft magnetic properties of Fe–B alloys. - Highlights: • We study the mechanochemical synthesis of nanocrystalline boron, Fe and Fe–B alloys. • We study the reduction reaction of B_2O_3–CaH_2 during milling. • We study the reduction reaction of Fe_2O_3–CaH_2 during milling. • We study the reduction reaction of Fe_2O_3–B_2O_3–CaH_2 during milling. • We study the effect of B on magnetic properties of nanocrystalline Fe–B alloys.

  19. A theory for the anisotropic interaction between two substitutional magnetic impurities and the magnetic anisotropic effect in dilute magnetic alloys

    International Nuclear Information System (INIS)

    Satter, M.A.

    1990-08-01

    In this paper, a formalism for studying the anisotropic interaction between two substitutional magnetic impurities and the magnetic anisotropic effect in a dilute noble metal- transition metal magnetic alloy has been developed from relativistic scattering theory. The theoretical development and the computational techniques of this formalism are based on relativistic spin-polarized scattering theory and relativistic band structure frameworks. For studying the magnetic anisotropic effect a convenient ''working'' frame of reference with its axes oriented along the fcc crystal axes is set up. This formalism is applied to study the situation for two Fe impurities in paramagnetic Au hosts. For AuFe dilute alloy, the two impurity site interaction as a function of separation is not oscillatory and the anisotropic effect is found to be less than the two site interaction itself only by an order of magnitude. Apart from the anisotropic coupling of the two impurity spins to the separation vector, for the first time, another weak anisotropic coupling to the crystal axes is also contained in the two site interaction. These anisotropic effects are the results of the relativistic spin-orbit interaction which are incorporated into the formalism. (author). 22 refs, 5 figs

  20. Thermal and microstructural analysis of an aluminium A356 alloy solidified by magnetic agitation

    International Nuclear Information System (INIS)

    Bustos, O; Ordonez, S; Jarami, Dario; Colas, R

    2008-01-01

    A magnetic agitation device was designed using a permanently rotating magnetic field, in order to study the effect of applying a variable magnetic field to agitate cast metals during the solidification process. The procedure used to verify the machine's functioning involved smelting and casting a predefined amount of A356 alloy in the device with and without the application of the magnetic field and then characterizing the material obtained with standard procedures of metallographic analysis. The results obtained show that the application of a permanently rotating magnetic field produces a destruction of the cast dendritic structure. This is explained by the fact that a magnetic field that varies over time induces a f.e.m. in a fluid conductor that becomes an increased convective transport through the Lorentz force. This work also studied the kinetics of solidification. The alloy was heated to 680 o C and was cast in molds preheated to 200 o C. Tests were carried out with and without the application of magnetic agitation. The cooling curves were recorded to evaluate the effect of the magnetic agitation on the alloy's form of solidification. The thermal analysis of the cooling curves shows a decrease in the temperatures under which the formation of dendrites from the primary phase as well as from the eutectic Al-Si phase begins when a magnetic field is imposed. A series of intermetallic AlFeSi type compounds appear in these alloys, which display noticeable refining and redistribution from the magnetic agitation (au)

  1. Structural and magnetic study of mechanically deformed Fe rich FeAlSi ternary alloys

    International Nuclear Information System (INIS)

    Legarra, E.; Apiñaniz, E.; Plazaola, F.

    2012-01-01

    Highlights: ► Addition of Si to binary Fe–Al alloys makes the disordering more difficult. ► Si addition opposes the large volume increase found in FeAl alloys with deformation. ► Disordering induces a redistribution of non-ferrous atoms around Fe atoms in Fe 75 Al 25−x Si x and Fe 70 Al 30−x Si x . ► Addition of Si to binary Fe 75 Al 25 and Fe 70 Al 30 alloys opposes the magnetic behavior induced by Al in the magnetism of Fe. ► Si inhibits the para-ferro transition found in Fe 60 Al 40 alloy with disordering. - Abstract: In this work we study systematically the influence of different Al/Si ratios on the magnetic and structural properties of mechanically disordered powder Fe 75 Al 25−x Si x , Fe 70 Al 30−x Si x and Fe 60 Al 40−x Si x alloys by means of Mössbauer spectroscopy, X-ray diffraction and magnetic measurements. In order to obtain different stages of disorder the alloys were deformed by different methods: crushing induction melted alloys and ball milling annealed (ordered) alloys using different number of balls and speed. X-ray and Mössbauer data show that mechanical deformation induces the disordered A2 structure in these alloys. The results indicate that addition of Si to binary Fe–Al alloys makes the disordering more difficult. In addition, X-ray diffraction patterns show that the normalized lattice parameter variation of the disordered alloys of each composition decreases monotonically with Si content, indicating clearly that Si addition opposes the large volume increase found in FeAl alloys with deformation. The study of the hyperfine fields indicates that there is a redistribution of non-ferrous atoms around Fe atoms with the disordering; indeed, there is an inversion of the behavior of the hyperfine field of the Fe atoms. On the other hand, the magnetic measurements indicate that addition of Si to binary Fe 75 Al 25 and Fe 70 Al 30 alloys opposes the magnetic behavior induced by Al in the magnetism of Fe.

  2. Thermal relaxation of magnetic clusters in amorphous Hf57Fe43 alloy

    International Nuclear Information System (INIS)

    Pajic, Damir; Zadro, Kreso; Ristic, Ramir; Zivkovic, Ivica; Skoko, Zeljko; Babic, Emil

    2007-01-01

    The magnetization processes in binary magnetic/non-magnetic amorphous alloy Hf 57 Fe 43 are investigated by the detailed measurement of magnetic hysteresis loops, temperature dependence of magnetization, relaxation of magnetization and magnetic ac susceptibility, including a nonlinear term. Blocking of magnetic moments at lower temperatures is accompanied by the slow relaxation of magnetization and magnetic hysteresis loops. All of the observed properties are explained by the superparamagnetic behaviour of the single domain magnetic clusters inside the non-magnetic host, their blocking by the anisotropy barriers and thermal fluctuation over the barriers accompanied by relaxation of magnetization. From magnetic viscosity analysis based on thermal relaxation over the anisotropy barriers it is found that magnetic clusters occupy the characteristic volume from 25 up to 200 nm 3 . The validity of the superparamagnetic model of Hf 57 Fe 43 is based on the concentration of iron in the Hf 100-x Fe x system that is just below the threshold for long range magnetic ordering. This work also throws more light on the magnetic behaviour of other amorphous alloys

  3. Path E alloys: ferritic material development for magnetic fusion energy applications

    International Nuclear Information System (INIS)

    Holmes, J.J.

    1980-09-01

    The application of ferritic materials in irradiation environments has received greatly expanded attention in the last few years, both internationally and in the United States. Ferritic materials are found to be resistant to irradiation damage and have in many cases superior properties to those of AISI 316. It has been shown that for magnetic fusion energy applications the low thermal expansion behavior of the ferritic alloy class will result in lower thermal stresses during reactor operation, leading to significantly longer ETF operating lifetimes. The Magnetic Fusion Energy Program therefore now includes a ferritic alloy option for alloy selection and this option has been designated Path E

  4. Magnetic susceptibility of Inconel alloys 718, 625, and 600 at cryogenic temperatures

    Science.gov (United States)

    Goldberg, Ira B.; Mitchell, Michael R.; Murphy, Allan R.; Goldfarb, Ronald B.; Loughran, Robert J.

    1990-01-01

    After a hydrogen fuel bleed valve problem on the Discovery Space Shuttle was traced to the strong magnetization of Inconel 718 in the armature of the linear variable differential transformer near liquid hydrogen temperatures, the ac magnetic susceptibility of three samples of Inconel 718 of slightly different compositions, one sample of Inconel 625, and on sample of Inconel 600 were measured as a function of temperature. Inconel 718 alloys are found to exhibit a spin glass state below 16 K. Inconel 600 exhibits three different magnetic phases, the lowest-temperature state (below 6 K) being somewhat similar to that of Inconel 718. The magnetic states of the Inconel alloys and their magnetic susceptibilities appear to be strongly dependent on the exact composition of the alloy.

  5. Phase diagram of Fe{sub 1-x}Co{sub x} ultrathin film

    Energy Technology Data Exchange (ETDEWEB)

    Fridman, Yu.A. [V.I. Vernadskiy Taurida National University, Vernadskiy Avenue 4, Simferopol, Crimea 95007 (Ukraine)], E-mail: frid@tnu.crimea.ua; Klevets, Ph.N.; Voytenko, A.P. [V.I. Vernadskiy Taurida National University, Vernadskiy Avenue 4, Simferopol, Crimea 95007 (Ukraine)

    2008-12-15

    Concentration-driven reorientation phase transitions in ultrathin magnetic films of FeCo alloy have been studied. It is established that, in addition to the easy-axis and easy-plane phases, a spatially inhomogeneous phase (domain structure), a canted phase, and also an 'in-plane easy-axis' phase can exist in the system. The realization of the last phase is associated with the competition between the single-ion anisotropy and the magnetoelastic interaction. The critical values of Co concentration corresponding to the phase transitions are evaluated, the types of phase transitions are determined, and the phase diagrams are constructed.

  6. Nickel-base alloy overlay weld with improved ultrasonic flaw detection by magnetic stirring welding

    International Nuclear Information System (INIS)

    Takashi, Hirano; Kenji, Hirano; Masayuki, Watando; Takahiro, Arakawa; Minoru, Maeda

    2001-01-01

    Ultrasonic flaw detection is more difficult in Nickel-base alloy welds containing dendrites owing to the decrease ultrasonic transmissibility they cause. The present paper discusses application of magnetic stirring welding as a means for reducing dendrite growth with consequent improvement in ultrasonic transmissibility. Single pass and multi-pass welding tests were conducted to determine optimal welding conditions. By PT and macro observation subsequent to welding was carried out, optimal operation conditions were clarified. Overlay welding tests and UT clearly indicated ultrasonic beam transmissibility in overlay welds to be improved and detection capacity to be greater through application of magnetic stirring welding. Optimal operation conditions were determined based on examination of temper bead effects in the heat affected zone of low alloy steel by application of magnetic stirring welding to the butt welded joints between low alloy and stainless steel. Hardness in this zone of low alloy steel after the fourth layer was less than 350 HV. (author)

  7. Study of soft magnetic iron cobalt based alloys processed by powder injection molding

    International Nuclear Information System (INIS)

    Silva, Aline; Lozano, Jaime A.; Machado, Ricardo; Escobar, Jairo A.; Wendhausen, Paulo A.P.

    2008-01-01

    As a near net shape process, powder injection molding (PIM) opens new possibilities to process Fe-Co alloys for magnetic applications. Due to the fact that PIM does not involve plastic deformation of the material during processing, we envisioned the possibility of eliminating vanadium (V), which is generally added to Fe-Co alloys to improve the ductility in order to enable its further shaping by conventional processes such as forging and cold rolling. In our investigation we have found out two main futures related to the elimination of V, which lead to a cost-benefit gain in manufacturing small magnetic components where high-saturation induction is needed at low frequencies. Firstly, the elimination of V enables the achievement of much better magnetic properties when alloys are processed by PIM. Secondly, a lower sintering temperature can be used when the alloy is processed starting with elemental Fe and Co powders without the addition of V

  8. Study of Nd-Fe-B alloys with nonstoichiometric Nd content in optimal magnetic state

    Directory of Open Access Journals (Sweden)

    Ćosović V.

    2009-01-01

    Full Text Available Characterization of two rapid-quenched Nd-Fe-B alloys with nonstoichiometric Nd content in the optimized magnetic state was carried out using the X-ray diffractometry (XRD, 57Fe Mössbauer spectroscopic phase analysis (MS, electron microscopy (TEM, high resolution TEM (HREM and Superconducting Quantum Interference Device (SQUID magnetometer. The experimental results demonstrate the fundamental difference in the structure and magnetic properties of the two investigated alloys in the optimized magnetic state. The Nd-Fe-B alloy with the reduced Nd content (Nd4.5Fe77B18.5 was found to have the nanocomposite structure of Fe3B/Nd2Fe14B and partly α-Fe/Nd2Fe14B, with mean grain size below 30 nm. On the other side, the overstoichiometric Nd14Fe79B7 alloy has almost a monophase structure with the dominant content of the hard magnetic phase Nd2Fe14B (up to 95 wt. % and a mean crystallite size about 60 nm, as determined by XRD and TEM analysis. The results of magnetic measurements on SQUID magnetometer also suggest the nanocomposite structure of the Nd-low alloy and nanocrystalline decoupled structure of the Nd-rich alloy after the optimal heat treatment.

  9. Magnetic and structural characterization of Mo-Hitperm alloys with different Fe/Co ratio

    Energy Technology Data Exchange (ETDEWEB)

    Conde, C.F., E-mail: conde@us.es [Departamento de Fisica de la Materia Condensada, ICMSE-CSIC, Universidad de Sevilla, P.O. Box 1065, 41080 Sevilla (Spain); Borrego, J.M.; Blazquez, J.S.; Conde, A. [Departamento de Fisica de la Materia Condensada, ICMSE-CSIC, Universidad de Sevilla, P.O. Box 1065, 41080 Sevilla (Spain); Svec, P.; Janickovic, D. [Department of Metal Physics, Institute of Physics, Slovak Academy of Sciences, Dubravska Cesta 9, 845 11 Bratislava (Slovakia)

    2011-02-03

    Research highlights: > Nanocrystallization kinetics results based on isothermal (TMG) and non-isothermal (DSC) experiments agree describing a strongly inhibited grain growth process. > The crystalline volume fraction at the end of the nanocrystallization process is practically not affected with the increase of Co in the alloy, although it is lower than in the corresponding Co free alloy. The lattice parameter and the crystal size of the {alpha}-FeCo(Mo) phase nanocrystals decreases as the Co content in the alloy increases. > Moessbauer spectra were analyzed in the frame of three different contributions: pure crystalline, interface and amorphous contribution. Comparison between TEM, XRD and Moessbauer data indicates that some Mo could be present inside the nanocrystals. > Changing the Fe/Co ratio allows to increase the Curie temperature of the amorphous alloys for these compositions between room temperature and {approx}800 K, and therefore, allows tuning the temperature at which the maximum magnetocaloric effect takes place opening a possibility for these alloys as potential low cost magnetic refrigerants. - Abstract: The influence of the Co content on the microstructure and magnetic behaviour of a series of amorphous and nanocrystalline (FeCo){sub 79}Mo{sub 8}Cu{sub 1}B{sub 12} alloys is reported. Changes in the magnetic properties provoked by the microstructural evolution upon different thermal treatments of as-cast samples are analyzed as well. Kinetics of nanocrystallization process can be described by an isokinetic approach. As the Co content in the alloy increases, the Curie temperature of the amorphous as-cast samples increases while the crystallization onset temperature decreases. The crystalline volume fraction as well as the mean grain size of the nanocrystals at the end of the nanocrystallization process are slightly higher for the lowest Co content alloy but smaller than in similar Hitperm Mo-free alloys. The average magnetic field and the average isomer

  10. Minor-Cu doped soft magnetic Fe-based FeCoBCSiCu amorphous alloys with high saturation magnetization

    Science.gov (United States)

    Li, Yanhui; Wang, Zhenmin; Zhang, Wei

    2018-05-01

    The effects of Cu alloying on the amorphous-forming ability (AFA) and magnetic properties of the P-free Fe81Co5B11C2Si1 amorphous alloy were investigated. Addition of ≤ 1.0 at.% Cu enhances the AFA of the base alloy without significant deterioration of the soft magnetic properties. The Fe80.5Co5B11C2Si1Cu0.5 alloy with the largest critical thickness for amorphous formation of ˜35 μm possesses a high saturation magnetization (Bs) of ˜1.78 T, low coercivity of ˜14.6 A/m, and good bending ductility upon annealing in a wide temperature range of 513-553 K with maintaining the amorphous state. The fabrication of the new high-Fe-content Fe-Co-B-C-Si-Cu amorphous alloys by minor doping of Cu gives a guideline to developing high Bs amorphous alloys with excellent AFA.

  11. A model considering mechanical anisotropy of magnetic-field-induced superelastic strain in magnetic shape memory alloys

    International Nuclear Information System (INIS)

    Zhu, Yuping; Yu, Kai

    2013-01-01

    Highlights: ► The model analyzes mechanical anisotropy of magnetic shape memory alloy. ► The numerical evaluation of Eshelby tensor of shape memory alloy is obtained. ► Interaction energy of magnetic shape memory alloy is analyzed. - Abstract: Under applied mechanical load and magnetic field, a micromechanics-based thermodynamic model taking account of mechanical anisotropy of magnetic shape memory alloys (MSMAs) is developed in this work. Considering the crystallographic and magnetic microstructure, the internal state variables are chosen and the model can capture the magnetic shape memory effect caused by the martensitic variant reorientation process. It is assumed that the Gibbs free energy is consisted of the mechanical potential energy of anisotropic matrix, the Zeeman energy and the magnetocrystalline anisotropy energy in the model. In terms of the balance between the thermodynamic driving force derived from the reduction of Gibbs free energy and the resistive force for the variant reorientation, the kinetic equation is established and the Eshelby tensor of anisotropic MSMAs is then obtained by using numerical evaluation. At last, the effects of the anisotropy on interaction energy and macroscopic strain are discussed. The assumption of isotropy tends to underestimate interaction energy and macroscopic strain. The results considering mechanical anisotropy are in good agreement with the experimental data.

  12. Interplay between structure and magnetism in HoxPr1-x alloys. 2. Resonant x-ray magnetic scattering

    DEFF Research Database (Denmark)

    Vigliante, A.; Christensen, M.J.; Hill, J.P.

    1998-01-01

    X-ray-scattering techniques have been used to study the crystal and magnetic structures of HoxPr1-x alloys in the form of thin films. Three distinct crystal structures are found as a function of concentration x, each of which has a characteristic magnetic structure. For x greater than or equal to 0.......6 a hexagonal-close-packed phase is found with the magnetic moments ordered in a basal-plane helix, whereas for 0.4 less than or equal to x... hexagonal-close-packed and remain nonmagnetic down to the lowest temperatures studied. Using x-ray magnetic resonance scattering techniques, we demonstrate that a small, static spin-density wave is induced within the alloy 5d band at both the Pr and Ho sites in both of the magnetically ordered phases...

  13. Quantitative measurements of magnetic polaron binding on acceptors in CdMnTe alloys

    Science.gov (United States)

    Nhung, Tran Hong; Planel, R.

    1983-03-01

    The acceptor binding energy is measured as a function of Temperature and composition in Cd1-x Mnx Te alloys, by time resolved spectroscopy. The Bound magnetic polaron effect is measured and compared with a theory accouting for magnetic saturation and fluctuations.

  14. Magnetic properties analysis of intermetallic alloys Rni5 (R = Rare Earths)

    International Nuclear Information System (INIS)

    Barthem, V.M.T.S.

    1988-01-01

    SmNi 5 and TmNi 5 alloys were analysed by magnetization measures, susceptibility, resistivity and only for TmNi 5 by magnetostriction and thermal expansion. The results are distinguished by powerful magnetic anisotropy of these materials. (C.G.C.) [pt

  15. Magnetocaloric effect of Gd 5 Si 2 Ge 2 alloys in low magnetic field

    Indian Academy of Sciences (India)

    The magnetocaloric effect (MCE) is studied by measuring magnetic entropy change ( M) and adiabatic temperature change ( ad) in a magnetic field of 1.5 T using a vibrating sample magnetometer (VSM) and a home-made magnetocaloric effect measuring apparatus, respectively. The maximum M of the alloys ...

  16. Nanostructure, Composition, and Magnetic Behavior of Mechanically Alloyed Fe-Mo

    Czech Academy of Sciences Publication Activity Database

    Jirásková, Yvonna; Buršík, Jiří; Turek, Ilja

    2013-01-01

    Roč. 26, č. 5 (2013), s. 1717-1721 ISSN 1557-1939. [ICSM 2012 /3./. Istanbul, 29.04.2012-04.05.2012] R&D Projects: GA ČR(CZ) GAP108/11/1350 Keywords : Nanostructured material * Mechanical alloying * Magnetic properties * Grain core * Defects Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.930, year: 2013

  17. Spontaneous magnetization of thin films of ordered and disordered alloys of transition metals

    International Nuclear Information System (INIS)

    Nguyen Nhat Khanh.

    1989-12-01

    A method of calculation of spontaneous magnetization of thin films of transition metal alloys is described. The method is based on the Hubbard model for d electrons. Use of the Bragg-Williams approximation and two-dimensional canonical transformations has allowed to calculate the magnetization. Results for a Ni 3 Fe thin film are presented. (author). 11 refs, 1 fig

  18. Magnetic properties of ND Rich Melt-Spun ND-FE-B alloy

    Directory of Open Access Journals (Sweden)

    Grujić Aleksandar

    2005-01-01

    Full Text Available As a part of these experimental investigations of melt-spun Nd-Fe-B alloy with Nd rich content in relation to Nd2Fe14B prepared by rapid quenching process for optimally selected cooling rate and heat treatment, the influence of the chosen chemical composition on magnetic properties was observed. The results of X-ray diffraction, Mössbauer spectroscopy phase analysis and magnetic measurement of investigated melt-spun Nd14.5Fe78.5B7 alloy are presented to bring some new information concerning the relation between their structure and magnetic properties.

  19. Chemical, electronic, and magnetic structure of LaFeCoSi alloy: Surface and bulk properties

    Energy Technology Data Exchange (ETDEWEB)

    Lollobrigida, V. [Dipartimento di Scienze, Università Roma Tre, I-00146 Rome (Italy); Dipartimento di Matematica e Fisica, Università Roma Tre, I-00146 Rome (Italy); Basso, V.; Kuepferling, M.; Coïsson, M.; Olivetti, E. S.; Celegato, F. [Istituto Nazionale di Ricerca Metrologica (INRIM), I-10135 Torino (Italy); Borgatti, F. [CNR, Istituto per lo Studio dei Materiali Nanostrutturati (ISMN), I-40129 Bologna (Italy); Torelli, P.; Panaccione, G. [CNR, Istituto Officina dei Materiali (IOM), Lab. TASC, I-34149 Trieste (Italy); Tortora, L. [Laboratorio di Analisi di Superficie, Dipartimento di Matematica e Fisica, Università Roma Tre, I-00146 Rome (Italy); Dipartimento di Ingegneria Meccanica, Università Tor Vergata, I-00133 Rome (Italy); Stefani, G.; Offi, F. [Dipartimento di Scienze, Università Roma Tre, I-00146 Rome (Italy)

    2014-05-28

    We investigate the chemical, electronic, and magnetic structure of the magnetocaloric LaFeCoSi compound with bulk and surface sensitive techniques. We put in evidence that the surface retains a soft ferromagnetic behavior at temperatures higher than the Curie temperature of the bulk due to the presence of Fe clusters at the surface only. This peculiar magnetic surface effect is attributed to the exchange interaction between the ferromagnetic Fe clusters located at the surface and the bulk magnetocaloric alloy, and it is used here to monitor the magnetic properties of the alloy itself.

  20. Chemical, electronic, and magnetic structure of LaFeCoSi alloy: Surface and bulk properties

    Science.gov (United States)

    Lollobrigida, V.; Basso, V.; Borgatti, F.; Torelli, P.; Kuepferling, M.; Coïsson, M.; Olivetti, E. S.; Celegato, F.; Tortora, L.; Stefani, G.; Panaccione, G.; Offi, F.

    2014-05-01

    We investigate the chemical, electronic, and magnetic structure of the magnetocaloric LaFeCoSi compound with bulk and surface sensitive techniques. We put in evidence that the surface retains a soft ferromagnetic behavior at temperatures higher than the Curie temperature of the bulk due to the presence of Fe clusters at the surface only. This peculiar magnetic surface effect is attributed to the exchange interaction between the ferromagnetic Fe clusters located at the surface and the bulk magnetocaloric alloy, and it is used here to monitor the magnetic properties of the alloy itself.

  1. Chemical, electronic, and magnetic structure of LaFeCoSi alloy: Surface and bulk properties

    International Nuclear Information System (INIS)

    Lollobrigida, V.; Basso, V.; Kuepferling, M.; Coïsson, M.; Olivetti, E. S.; Celegato, F.; Borgatti, F.; Torelli, P.; Panaccione, G.; Tortora, L.; Stefani, G.; Offi, F.

    2014-01-01

    We investigate the chemical, electronic, and magnetic structure of the magnetocaloric LaFeCoSi compound with bulk and surface sensitive techniques. We put in evidence that the surface retains a soft ferromagnetic behavior at temperatures higher than the Curie temperature of the bulk due to the presence of Fe clusters at the surface only. This peculiar magnetic surface effect is attributed to the exchange interaction between the ferromagnetic Fe clusters located at the surface and the bulk magnetocaloric alloy, and it is used here to monitor the magnetic properties of the alloy itself.

  2. Gigantic transverse x-ray magnetic circular dichroism in ultrathin Co in Au/Co/Au(001)

    International Nuclear Information System (INIS)

    Koide, T; Mamiya, K; Asakura, D; Osatune, Y; Fujimori, A; Suzuki, Y; Katayama, T; Yuasa, S

    2014-01-01

    Transverse-geometry x-ray magnetic circular dichroism (TXMCD) measurements on Au/Co-staircase/Au(001) reveal the orbital origin of intrinsic in-plane magnetic anisotropy A gigantic TXMCD was successfully observed at the Co L 3,2 edges for Co thickness (t C0 ) in the 2-monolayer regime. A TXMCD-sum-rule analysis shows a remarkable enhancement of an orbital-moment anisotropy (Δm orb ) and of an in-plane magnetic dipole moment (m || T ). Both Δm orb and m || T exhibit close similarity in t Co dependence, reflecting the in-plane magnetic anisotropy These observations evidence that extremely strong, intrinsic, in-plane magnetic anisotropy originates from the anisotropic orbital part of the wave function, dominating the dipole-dipole-interaction-derived, extrinsic, in-plane magnetic anisotropy.

  3. Gigantic transverse x-ray magnetic circular dichroism in ultrathin Co in Au/Co/Au(001)

    Science.gov (United States)

    Koide, T.; Mamiya, K.; Asakura, D.; Osatune, Y.; Fujimori, A.; Suzuki, Y.; Katayama, T.; Yuasa, S.

    2014-04-01

    Transverse-geometry x-ray magnetic circular dichroism (TXMCD) measurements on Au/Co-staircase/Au(001) reveal the orbital origin of intrinsic in-plane magnetic anisotropy A gigantic TXMCD was successfully observed at the Co L3,2 edges for Co thickness (tC0) in the 2-monolayer regime. A TXMCD-sum-rule analysis shows a remarkable enhancement of an orbital-moment anisotropy (Δmorb) and of an in-plane magnetic dipole moment (m||T). Both Δmorb and m||T exhibit close similarity in tCo dependence, reflecting the in-plane magnetic anisotropy These observations evidence that extremely strong, intrinsic, in-plane magnetic anisotropy originates from the anisotropic orbital part of the wave function, dominating the dipole-dipole-interaction-derived, extrinsic, in-plane magnetic anisotropy.

  4. Structural and magnetic properties of FeCoC system obtained by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Rincón Soler, A. I. [Universidad Tecnológica de Pereira, Fac. de Ciencias, Depto. de Física (Colombia); Rodríguez Jacobo, R. R., E-mail: rrrodriguez@uao.edu.co [Universidad Autónoma de Occidente, Fac. de Ciencias Básicas, Depto. de Física (Colombia); Medina Barreto, M. H.; Cruz-Muñoz, B. [Universidad Tecnológica de Pereira, Fac. de Ciencias, Depto. de Física (Colombia)

    2017-11-15

    Fe{sub 96−X}Co{sub X}C{sub 4} (x = 0, 10, 20, 30, 40 at. %) alloys were obtained by mechanical alloying of Fe, C and Co powders using high-energy milling. The structural and magnetic properties of the alloy system were analyzed by X-ray diffraction, Scanning Electron Microscopy (SEM), Vibrating Sample Magnetometer (VSM) and Mössbauer Spectrometry at room temperature. The X-ray diffraction patterns showed a BCC-FeCoC structure phase for all samples, as well as a lattice parameter that slightly decreases with Co content. The saturation magnetization and coercive field were analyzed as a function of Co content. The Mössbauer spectra were fitted with a hyperfine magnetic field distribution showing the ferromagnetic behavior and the disordered character of the samples. The mean hyperfine magnetic field remained nearly constant (358 T) with Co content.

  5. The Magnetic Properties of Metal-Alloy Glass Composites Prepared by Ion Implantation

    International Nuclear Information System (INIS)

    Julian Fernandez, Cesar de; Mattei, Giovanni; Sada, Cinzia; Maurizio, Chiara; Padovani, Sara; Mazzoldi, Paolo; Sangregorio, Claudio; Gatteschi, Dante

    2003-01-01

    The structural and magnetic properties of Co-Ni, Co-Fe and Ni-Cu alloy nanoparticles formed in silica matrix by sequential ion implantation are presented. These nanoparticles show crystal structure similar to the corresponding bulk alloys. In the Co-Ni and Co-Fe, magnetization saturation and coercive field depend on the the alloy composition, crystal structure and size effects. Ferromagnetic resonance studies show that collective magnetic processes are present and these are determined by the film-like morphology of the implanted region. The temperature dependence of the magnetization of the NixCu100-x samples indicates that their Curie Temperatures are larger than the corresponding bulk ones. This feature is discussed considering the composition of the nanoparticles and the size effects

  6. Atomic scale properties of magnetic Mn-based alloys probed by emission Mössbauer spectroscopy

    CERN Multimedia

    Mn-based alloys are characterized by a wealth of properties, which are of interest both from fundamental physics point of view and particularly attractive for different applications in modern technology: from magnetic storage to sensing and spin-based electronics. The possibility to tune their magnetic properties through post-growth thermal processes and/or stoichiometry engineering is highly important in order to target different applications (i.e. Mn$_{x}$Ga) or to increase their Curie temperature above room temperature (i.e. off-stoichiometric MnSi). In this project, the Mössbauer effect will be applied at $^{57}$Fe sites following implantation of radioactive $^{57}$Mn, to probe the micro-structure and magnetism of Mn-based alloys on the atomic-scale. The proposed experimental plan is devoted to establish a direct correlation between the local structure and bulk magnetism (and other physical properties) of Mn-based alloys.

  7. Structural and magnetic properties of FeCoC system obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Rincón Soler, A. I.; Rodríguez Jacobo, R. R.; Medina Barreto, M. H.; Cruz-Muñoz, B.

    2017-01-01

    Fe 96−X Co X C 4 (x = 0, 10, 20, 30, 40 at. %) alloys were obtained by mechanical alloying of Fe, C and Co powders using high-energy milling. The structural and magnetic properties of the alloy system were analyzed by X-ray diffraction, Scanning Electron Microscopy (SEM), Vibrating Sample Magnetometer (VSM) and Mössbauer Spectrometry at room temperature. The X-ray diffraction patterns showed a BCC-FeCoC structure phase for all samples, as well as a lattice parameter that slightly decreases with Co content. The saturation magnetization and coercive field were analyzed as a function of Co content. The Mössbauer spectra were fitted with a hyperfine magnetic field distribution showing the ferromagnetic behavior and the disordered character of the samples. The mean hyperfine magnetic field remained nearly constant (358 T) with Co content.

  8. Magnetization jumps in nanostructured Nd–Fe–B alloy at low temperatures

    International Nuclear Information System (INIS)

    Neznakhin, D.S.; Bolyachkin, A.S.; Volegov, A.S.; Markin, P.E.; Andreev, S.V.; Kudrevatykh, N.V.

    2015-01-01

    Magnetic properties of the nanostructured isotropic alloy on the base of Nd 2 Fe 14 B type phase were investigated at low temperatures. The evaluated average grain size of this phase was much smaller than its critical single domain diameter. Hence the magnetization and demagnetization processes were expected to be performed by coherent magnetization rotation. For such coercivity type system magnetization jumps were revealed on the demagnetization hysteresis loop branch in the vicinity of the coercive force at temperatures below 4 K. It was shown that magnetization jumps have a stochastic behavior and their number strongly depends on the temperature and the mass of measured samples. High temperature spikes corresponding to magnetization discontinuities were observed. All these results allowed to propose that magnetization jumps in nanostructured magnetics with magnetization rotation reversal processes comply with the local heating model. - Highlights: • Magnetization reversals of the nanostructured Nd–Fe–B-type alloy were obtained below 4 K. • Magnetization jumps were first observed for magnetization rotation coercivity type magnets. • Staircase magnetization reversal was explained within the framework of the local heating model

  9. Local magnetic moments in dilute Cr-Nb alloys: the effects of applied magnetic field and Nb concentration

    International Nuclear Information System (INIS)

    Souza, P E N de; Oliveira, L M de; Ortiz, W A; Camargo, P C de; Oliveira, A J A de

    2005-01-01

    In this work we present magnetic susceptibility results for Cr-x at.% Nb alloys (x = 0.2, 0.6, 0.7, 1.4, and 2.0), showing that a local short-range order spin-density wave (L-SDW) appears at a characteristic temperature (T loc ) above the Neel temperature. The evidence for L-SDW is based on a Curie-Weiss-like behaviour, which is suppressed when large magnetic fields are applied or for alloys with Nb concentration above x = 2.0 at.%

  10. Design and development of novel MRI compatible zirconium- ruthenium alloys with ultralow magnetic susceptibility.

    Science.gov (United States)

    Li, H F; Zhou, F Y; Li, L; Zheng, Y F

    2016-04-19

    In the present study, novel MRI compatible zirconium-ruthenium alloys with ultralow magnetic susceptibility were developed for biomedical and therapeutic devices under MRI diagnostics environments. The results demonstrated that alloying with ruthenium into pure zirconium would significantly increase the strength and hardness properties. The corrosion resistance of zirconium-ruthenium alloys increased significantly. High cell viability could be found and healthy cell morphology observed when culturing MG 63 osteoblast-like cells and L-929 fibroblast cells with zirconium-ruthenium alloys, whereas the hemolysis rates of zirconium-ruthenium alloys are zirconium-ruthenium alloys (1.25 × 10(-6) cm(3)·g(-1)-1.29 × 10(-6) cm(3)·g(-1) for zirconium-ruthenium alloys) are ultralow, about one-third that of Ti-based alloys (Ti-6Al-4V, ~3.5 × 10(-6) cm(3)·g(-1), CP Ti and Ti-6Al-7Nb, ~3.0 × 10(-6) cm(3)·g(-1)), and one-sixth that of Co-Cr alloys (Co-Cr-Mo, ~7.7 × 10(-6) cm(3)·g(-1)). Among the Zr-Ru alloy series, Zr-1Ru demonstrates enhanced mechanical properties, excellent corrosion resistance and cell viability with lowest magnetic susceptibility, and thus is the optimal Zr-Ru alloy system as therapeutic devices under MRI diagnostics environments.

  11. Influence of Weak External Magnetic Field on Amorphous and Nanocrystalline Fe-based Alloys

    Science.gov (United States)

    Degmová, J.; Sitek, J.

    2010-07-01

    Nanoperm, Hitperm and Finamet amorphous and nanocrystalline alloys were measured by Mössbauer spectrometry in a weak external magnetic field of 0.5 T. It was shown that the most sensitive parameters of Mössbauer spectra are the intensities of the 2nd and the 5th lines. Rather small changes were observed also in the case of internal magnetic field values. The spectrum of nanocrystalline Nanoperm showed the increase in A23 parameter (ratio of line intensities) from 2.4 to 3.7 and decrease of internal magnetic field from 20 to 19 T for amorphous subspectrum under the influence of magnetic field. Spectrum of nanocrystalline Finemet shown decrease in A23 parameter from 3.5 to 2.6 almost without a change in the internal magnetic field value. In the case of amorphous Nanoperm and Finemet samples, the changes are almost negligible. Hitperm alloy showed the highest sensitivity to the weak magnetic field, when the A23 parameter increased from 0.4 to 2.5 in the external magnetic fields. The A23 parameter of crystalline subspectrum increased from 2.7 to 3.8 and the value of internal magnetic field corresponding to amorphous subspectrum increased from 22 to 24 T. The behavior of nanocrystalline alloys under weak external magnetic field was analyzed within the three-level relaxation model of magnetic dynamics in an assembly of single-domain particles.

  12. Magnetic ordering in dilute YTb and YEr alloys

    International Nuclear Information System (INIS)

    Rainford, B.D.; Kilcoyne, S.H.; Mohammed, K.A.; Lanchester, P.C.; Stanley, H.B.; Caudron, R.

    1988-01-01

    Dilute YEr alloys (Er concentration between 3% and 10%) show the existence of sinusoidally modulated antiferromagnetism down to the lowest impurity concentrations studied. Extrapolation of the Neel temperatures for both YEr and YTb suggests a critical concentration is ≅ 0.8% Tb, Er. Ordering in such dilute alloys may result from exchange enhancement in the yttrium host

  13. Magnetic ordering in dilute YTb and YEr alloys

    Energy Technology Data Exchange (ETDEWEB)

    Rainford, B.D.; Kilcoyne, S.H.; Mohammed, K.A.; Lanchester, P.C.; Stanley, H.B.; Caudron, R.

    1988-12-01

    Dilute YEr alloys (Er concentration between 3% and 10%) show the existence of sinusoidally modulated antiferromagnetism down to the lowest impurity concentrations studied. Extrapolation of the Neel temperatures for both YEr and YTb suggests a critical concentration is /approx equal/ 0.8% Tb, Er. Ordering in such dilute alloys may result from exchange enhancement in the yttrium host.

  14. Microstructural evolution and magnetic properties of binder jet additive manufactured Ni-Mn-Ga magnetic shape memory alloy foam

    International Nuclear Information System (INIS)

    Mostafaei, Amir; Kimes, Katerina A.; Stevens, Erica L.; Toman, Jakub; Krimer, Yuval L.; Ullakko, Kari; Chmielus, Markus

    2017-01-01

    This study investigated microstructural evolution, phase transformation and magnetic behavior of additively manufactured magnetic shape memory alloy foam. Pre-alloyed angular Ni-Mn-Ga ball-milled powder was binder jet printed and sintered at 1020 °C for 4 h in both vacuum and argon atmospheres. Porosity of the manufactured foams was studied using micro-computed x-ray tomography and it was found that the relative density of the sintered parts was about 50–60%. In the printed sample that was sintered in argon, electron microscopy with elemental analysis showed no compositional gradient. X-ray diffraction indicated that 10M modulated martensite was present in the pre-alloyed powder as well as the sample sintered in argon. Differential scanning calorimetry and thermomagnetic results showed that martensitic transformation of the sample sintered in argon was at 34 °C, while barely detectable in the sample sintered in vacuum. Saturation magnetization of the printed sample sintered in argon atmosphere was around 68.4 Am"2/kg. Production of a magnetic shape memory alloy by printing would enable complex-shaped elements for demanding applications, and intentionally including porosity could allow these polycrystals to exhibit the magnetic shape memory effect. Therefore, a facile method for sintering of Ni–Mn–Ga printed parts has been presented for the first time.

  15. Influence of grain size on the extraordinary Hall effect in magnetic granular alloys

    International Nuclear Information System (INIS)

    Granovsky, Alexander B.; Kalitsov, Alan V.; Khanikaev, Alexander B.; Kioussis, Nicholas

    2003-01-01

    A quantum statistical theory of the influence of grain size on the residual extraordinary Hall effect (EHE) in magnetic metal-insulator granular alloys is presented. It is shown that under certain conditions the quasi-classical size-effect (QSE) can lead to similar behaviors of EHE in metal-metal and metal-insulator alloys. The possible dependences of EHE coefficient on the grain size and the role of the QSE in the giant EHE in nanocomposites are discussed

  16. Influence of grain size on the extraordinary Hall effect in magnetic granular alloys

    Energy Technology Data Exchange (ETDEWEB)

    Granovsky, Alexander B. E-mail: granov@magn.ru; Kalitsov, Alan V.; Khanikaev, Alexander B.; Kioussis, Nicholas

    2003-03-01

    A quantum statistical theory of the influence of grain size on the residual extraordinary Hall effect (EHE) in magnetic metal-insulator granular alloys is presented. It is shown that under certain conditions the quasi-classical size-effect (QSE) can lead to similar behaviors of EHE in metal-metal and metal-insulator alloys. The possible dependences of EHE coefficient on the grain size and the role of the QSE in the giant EHE in nanocomposites are discussed.

  17. Effect of cold plastic deformation on the properties of semihard-magnetic alloys

    International Nuclear Information System (INIS)

    Kovalev, P.M.; Khazanov, S.A.; Chernyak, A.A.

    1982-01-01

    The effect of pass and overall reduction during cold plastic deformation on magnetic properties of the 25KKh15 and 25KFN14 iron-cobalt alloys has been studied. It has been found out that gamma-α transformation which intensity id defined by the deformation temperature occurs during the 25KFN14 and 25KKh15 alloy cold rolling. The pass reduction decrease fostering complete proceeding of #betta#-α transformation is equivalent to the increase of overall reduction

  18. Magnetic exchange coupling in amorphous Fe80-xDy xB20 alloys

    International Nuclear Information System (INIS)

    Annouar, F.; Lassri, H.; Ayadi, M.; Omri, M.; Lassri, M.; Krishnan, R.

    2005-01-01

    Amorphous Fe 80-x Dy x B 20 alloys have been prepared by melt spinning and their magnetic properties have been studied. The mean field theory has been used to explain the temperature dependence of the magnetization. The exchange interactions between Co-Co and Dy-Co atom pairs have been evaluated. High-field magnetization studies on samples with stoichiometry close to that of a compensated ferrimagnet show a magnetic behavior that is characteristic of a non-collinear magnetic structure of the Dy and Fe sublattices. The region of the canted moments can be described by a phase diagram in the H-T plane

  19. Technology of magnetic abrasive finishing in machining of difficult-to-machine alloy complex surface

    Directory of Open Access Journals (Sweden)

    Fujian MA

    2016-10-01

    Full Text Available The technology of magnetic abrasive finishing is one of the important finishing technologies. Combining with low-frequency vibration and ultrasonic vibration, it can attain higher precision, quality and efficiency. The characteristics and the related current research of magnetic abrasive finishing, vibration assisted magnetic abrasive finishing and ultrasonic assisted magnetic abrasive finishing are introduced. According to the characteristics of the difficult-to-machine alloy's complex surface, the important problems for further study are presented to realize the finishing of complex surface with the technology of magnetic abrasive finishing, such as increasing the machining efficiency by enhancing the magnetic flux density of machining gap and compounding of magnetic energy and others, establishing of the control function during machining and the process planning method for magnetic abrasive finishing of complex surface under the space geometry restraint of complex surface on magnetic pole, etc.

  20. Structural and magnetic properties of holmium-scandium alloys and superlattices

    DEFF Research Database (Denmark)

    Bryn-Jacobsen, C.; Cowley, R.A.; McMorrow, D.F.

    1997-01-01

    The properties of Ho-Sc alloys and superlattices grown by molecular-beam epitaxy have been investigated using x-ray and neutron-diffraction techniques. Structural studies reveal that the alloy samples have different a lattice parameters for the Sc-seed layer and the Ho:Sc alloy grown on top...... of the seed layer; while the superlattices have different a lattice parameters for the Sc seed, and for both the Ho and Sc in the superlattice layers. The structural characteristics are related to the large lattice mismatches (of the order 7%) between the constituent elements. The magnetic moments...

  1. Chemical short range order and magnetic correction in liquid manganese–gallium zero alloy

    Energy Technology Data Exchange (ETDEWEB)

    Grosdidier, B. [Laboratoire de Chimie Physique – Approche Multi-Echelle des Milieux Complexes, Institut Jean Bariol, Université de Lorraine, Institut de Chimie, Physique et Matériaux, 1 Bd Arago, 57078 Metz Cedex 3 (France); Ben Abdellah, A. [Laboratoire de Chimie Physique – Approche Multi-Echelle des Milieux Complexes, Institut Jean Bariol, Université de Lorraine, Institut de Chimie, Physique et Matériaux, 1 Bd Arago, 57078 Metz Cedex 3 (France); Innovation and Management of Industrial Systems, Abdelmalek Essaadi University, College of Sciences and Techniques of Tangier , P.O. Box 416, Postal code 90000, Tangier (Morocco); Université Internationale de Rabat, Parc Technopolis Rabat-Shore, 11100 Sala El Jadida (Morocco); Osman, S.M., E-mail: osm@squ.edu.om [Physics Department, College of Science, Sultan Qaboos University, P.O. Box 36, Postal Code 123, Al-Khod, Muscat (Oman); Ataati, J. [Innovation and Management of Industrial Systems, Abdelmalek Essaadi University, College of Sciences and Techniques of Tangier, P.O. Box 416, Postal code 90000, Tangier (Morocco); Gasser, J.G. [Laboratoire de Chimie Physique – Approche Multi-Echelle des Milieux Complexes, Institut Jean Bariol, Université de Lorraine, Institut de Chimie, Physique et Matériaux, 1 Bd Arago, 57078 Metz Cedex 3 (France)

    2015-12-15

    The Mn{sub 66}Ga{sub 34} alloy at this particular composition is known to be zero alloy in which the linear combination of the two neutron scattering lengths weighted by the atomic compositions vanish. Thus for this specific concentration, the effect of the partial structure factors S{sub NN} and S{sub NC} is cancelled by a weighted term, which value is zero. Then the measured total structure factor S(q) gives directly the concentration–concentration structure factor S{sub CC}(q). We present here the first experimental results of neutron diffraction on the Mn{sub 66}Ga{sub 34} “null matrix alloy” at 1050 °C. The main peak of the experimental S{sub CC}(q) gives a strong evidence of a hetero-atomic chemical order in this coordinated alloy. This order also appears in real space radial distribution function which is calculated by the Fourier transform of the structure factor. The degree of hetero-coordination is discussed together with other manganese-polyvalent alloys. However manganese also shows abnormal magnetic scattering in the alloy structure factor which must be corrected. This correction gives an experimental information on the mean effective spin of manganese in this liquid alloy. We present the first critical theoretical calculations of the magnetic correction factor in Mn–Ga zero-alloy based on our accurate experimental measurements of S{sub CC}(q).

  2. Magnetic properties of metastable bcc and fcc Fe-Cu alloys produced by vapor quenching

    International Nuclear Information System (INIS)

    Sumiyama, Kenji; Yoshitake, Tsutomu; Nakamura, Yoji

    1984-01-01

    High concentration Fesub(1-x)Cusub(x) alloys have been obtained by rf sputtering technique and investigated by X-ray diffraction and magnetization measurements. The bcc phase is extended over the region with x=0-0.4, while the fcc phase with x=0.6-1.0. For x=0.4-0.6, we have the mixed phase of bcc and fcc. The lattice constant of bcc phase increases slightly and that of fcc phase decreases with increasing x. In the bcc alloys, the average magnetic moment decreases with increasing x and deviates upwards from the simple dilution law. In the fcc alloys, the magnetic moment also decreases with increasing x but it deviates downwards from the simple dilution law. The Curie temperature, Tsub(c), of the Fesub(1-x)Cusub(x) alloys decreases abruptly with increasing x: Tsub(c) is higher than 750 K for the bcc alloys, while it is lower than 320 K for the fcc alloys and become 0 K at about x=0.92. (author)

  3. Direct observation of magnetic domains by Kerr microscopy in a Ni-Mn-Ga magnetic shape-memory alloy

    Czech Academy of Sciences Publication Activity Database

    Perevertov, Oleksiy; Heczko, Oleg; Schaefer, R.

    2017-01-01

    Roč. 95, č. 14 (2017), s. 1-5, č. článku 144431. ISSN 2469-9950 R&D Projects: GA ČR GA15-00262S Institutional support: RVO:68378271 Keywords : shape memory * magnetic domains * Kerr microscopy * N-Mn-Ga alloy Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 3.836, year: 2016

  4. Microstructure Formation in Strip-Cast RE-Fe-B Alloys for Magnets

    Science.gov (United States)

    Yamamoto, Kazuhiko; Matsuura, Masashi; Sugimoto, Satoshi

    2017-07-01

    During the manufacturing of sintered NdFeB magnets, it is well known that the microstructure of the starting alloy has a strong influence on the processing and the magnetic properties of the product. In this study, we clarify the microstructure formation in strip-cast rare earth (R)-Fe-B alloys used to produce magnets. The microstructure of the alloy surface in contact with the cooling roll and its cross-section were observed using laser microscopy, field emission electron microprobe analysis, and transmission electron microscopy. The orientations of crystal grains were determined by X-ray diffraction and electron backscatter diffraction analyses. Petal-shaped structures were found to cover the alloy surface in contact with the cooling roll, each consisting of a central nucleation region and radially grown Nd2Fe14B dendritic structures. The nucleation region, consisting of a "disc" and "predendrites", occurs in the super-cooled region of the contact area between the cooling roll and melt. In the disc region, spherical Nd2Fe14B particles in the thickness direction increase in volume. These discs and predendrites observed in the super-cooled area negatively influence the magnetic orientation and sinterability in the produced magnets. Therefore, it is important to avoid excessive super-cooling to obtain optimum magnetic properties.

  5. Cluster-Expansion Model for Complex Quinary Alloys: Application to Alnico Permanent Magnets

    Science.gov (United States)

    Nguyen, Manh Cuong; Zhou, Lin; Tang, Wei; Kramer, Matthew J.; Anderson, Iver E.; Wang, Cai-Zhuang; Ho, Kai-Ming

    2017-11-01

    An accurate and transferable cluster-expansion model for complex quinary alloys is developed. Lattice Monte Carlo simulation enabled by this cluster-expansion model is used to investigate temperature-dependent atomic structure of alnico alloys, which are considered as promising high-performance non-rare-earth permanent-magnet materials for high-temperature applications. The results of the Monte Carlo simulations are consistent with available experimental data and provide useful insights into phase decomposition, selection, and chemical ordering in alnico. The simulations also reveal a previously unrecognized D 03 alloy phase. This phase is very rich in Ni and exhibits very weak magnetization. Manipulating the size and location of this phase provides a possible route to improve the magnetic properties of alnico, especially coercivity.

  6. Review of properties of magnetic shape memory (MSM) alloys and MSM actuator designs

    International Nuclear Information System (INIS)

    Gabdullin, N; Khan, S H

    2015-01-01

    Magnetic shape memory alloys are a new group of ''smart'' materials that exhibit large strain of 6-12% when subjected to magnetic fields. This indicates their enormous potential to be used in different electromagnetic (EM) devices such as actuators, sensors, energy harvesters and dampers. Shape change in MSM materials is controlled by magnetic field and doesn't involve phase transformation, allowing it to overcome a number of disadvantages of conventional shape memory alloys (SMAs). MSM devices are capable of producing large force and stroke output in considerably small dimensions. At the same time they can have fast response and potentially very long lifetime. This paper discusses different modern designs and approaches to MSM actuator design with their advantages and disadvantages. An overview on characteristics of MSM alloys is also presented in order to highlight how different properties of the material influence the total output of a device

  7. Nanocrystallinity and magnetic property enhancement in melt-spun iron-rare earth-base hard magnetic alloys

    International Nuclear Information System (INIS)

    Davies, H.A.; Manaf, A.; Zhang, P.Z.

    1993-01-01

    Refinement of the grain size below ∼35 nm mean diameter in melt-spun FeNdB-base alloys leads to enhancement of remanent polarization, J r , above the level predicted by the Stoner-Wohlfarth theory for an aggregate of independent, randomly oriented, and uniaxial magnetic particles. This article summarizes the results of the recent systematic research on this phenomenon, including the influence of alloy composition and processing conditions on the crystallite size, degree of enhancement of J r , and maximum energy product (BH) max . It has been shown that the effect can also occur in ternary FeNdB alloys, without the addition of silicon or aluminum, which was originally thought necessary, providing the nanocrystallites are not magnetically decoupled by a paramagnetic second phase. Values of (BH) max above 160 kJ. m -3 have been achieved. The relationship between grain size, J r , intrinsic coercivity, J H c , and (BH) max are discussed in terms of magnetic exchange coupling, anisotropy, and other parameters. Recent extension of this work to the enhancement of properties in Fe-Mischmental-Boron-base alloys and to bonded magnets with a nanocrystalline structure is also described

  8. Stress-induced magnetic anisotropy in nanocrystalline alloys

    International Nuclear Information System (INIS)

    Varga, L.K.; Gercsi, Zs.; Kovacs, Gy.; Kakay, A.; Mazaleyrat, F.

    2003-01-01

    Stress-annealing experiments were extended to both nanocrystalline alloy families, Finemet and Nanoperm (Hitperm), and, for comparison, to amorphous Fe 62 Nb 8 B 30 alloy. For both Finemet and bulk amorphous, stress-annealing results in a strong induced transversal anisotropy (flattening of hysteresis loop) but yields longitudinal induced anisotropy (square hysteresis loop) in Nanoperm and Hitperm. These results are interpreted in terms of back-stress theory

  9. Soft magnetic properties of FeRuGaSi alloy films: SOFMAX

    International Nuclear Information System (INIS)

    Hayashi, K.; Hayakawa, M.; Ishikawa, W.; Ochiai, Y.; Iwasaki, Y.; Aso, K.

    1988-01-01

    To advance new soft magnetic materials of an FeGaSi alloy into the commercial world, improvements on various properties were designed by introducing additive elements without sacrificing its high saturation magnetic induction. The detailed studies on the diversified properties, such as saturation magnetic induction, film internal stress, wear resistivity, and so on, were performed. High-frequency permeability of the laminated structure film was also investigated. As a result, the Ru-added FeRuGaSi alloy films, whose typical compositions are Fe 72 Ru 4 Ga 7 Si 17 and Fe 68 Ru 8 Ga 7 Si 17 (at. %), prove to be excellent soft magnetic materials especially appropriate for the magnetic recording/playback head core use

  10. The effect of axial external magnetic field on tungsten inert gas welding of magnesium alloy

    Science.gov (United States)

    Li, Caixia; Zhang, Xiaofeng; Wang, Jing

    2018-04-01

    The influences of axial external magnetic field on the microstructure and mechanical property of the AZ31 magnesium (Mg) alloy joints were studied. The microstructure of Mg alloy joint consisted of the weld seam, heat affected zone and base metal zone. The average grain size of weld seam welded with magnetic field is 39 μm, which is 38% smaller than that of the joint welded with absence of magnetic field. And the microhardness of weld seam increases with the help of magnetic field treatment, owing to the coarse grain refinement. With coil current of 2.0A, the maximum mechanical property of joint increases 6.7% to 255 MPa over the specimen without magnetic field treatment. Furthermore, fracture location is near heat affected area and the fracture surface is characterized with ductile fracture.

  11. Anti-Invar properties and magnetic order in fcc Fe-Ni-C alloy

    International Nuclear Information System (INIS)

    Nadutov, V.M.; Kosintsev, S.G.; Svystunov, Ye.O.; Garamus, V.M.; Willumeit, R.; Eckerlebe, H.; Ericsson, T.; Annersten, H.

    2011-01-01

    Anti-Invar effect was revealed in the fcc Fe-25.3%Ni-0.73%C (wt%) alloy, which demonstrates high values of thermal expansion coefficient (TEC) (15-21)x10 -6 K -1 accompanied by almost temperature-insensitive behavior in temperature range of 122-525 K. Alloying with carbon considerably expanded the low temperature range of anti-Invar behavior in fcc Fe-Ni-based alloy. The Curie temperature of the alloy T C =195 K was determined on measurements of temperature dependences of magnetic susceptibility and saturation magnetization. The Moessbauer and small-angle neutron scattering (SANS) experiments on the fcc Fe-25.3%Ni-(0.73-0.78)%C alloys with the varying temperatures below and above the Curie point and in external magnetic field of 1.5-5 T were conducted. Low value of the Debye temperature Θ D =180 K was estimated using the temperature dependence of the integral intensity of Moessbauer spectra for specified temperature range. The inequality B eff =(0.7-0.9)B ext was obtained in external field Moessbauer measurement that points to antiferromagnetically coupled Fe atoms, which have a tendency to align their spins perpendicular to B ext . Nano length scale magnetic inhomogeneities nearby and far above T C were revealed, which assumed that it is caused by mixed antiferromagnetically and ferromagnetically coupled Fe atom spins. The anti-Invar behavior of Fe-Ni-C alloy is explained in terms of evolution of magnetic order with changing temperature resulting from thermally varied interspin interaction and decreasing stiffness of interatomic bond. - Highlights: → Anti-Invar effect was revealed in the fcc Fe-25.3%Ni-0.73%C (wt%) alloy. → Carbon expanded the temperature range of anti-Invar behavior in Fe-Ni-based alloy. → Moessbauer data point to mixed interspin interaction and low the Dedye temperature. → The SANS experiments reveal nano length scale magnetic inhomogeneities ≤6 nm. → Anti-Invar behavior of Fe-Ni-C alloy explained by thermally varied magnetic order.

  12. Electrochemical alloying of immiscible Ag and Co for their structural and magnetic analyses

    Energy Technology Data Exchange (ETDEWEB)

    Santhi, Kalavathy [Material Science Centre, Department of Nuclear Physics, University of Madras, Guindy Campus, Chennai 600025 (India); Department of Physics, Women’s Christian College, Chennai 600006 (India); Kumarsan, Dhanapal [Material Science Centre, Department of Nuclear Physics, University of Madras, Guindy Campus, Chennai 600025 (India); Vengidusamy, Naryanan [Department of Inorganic Chemistry, University of Madras, Guindy Campus, Chennai 600025 (India); Arumainathan, Stephen, E-mail: stephen_arum@hotmail.com [Material Science Centre, Department of Nuclear Physics, University of Madras, Guindy Campus, Chennai 600025 (India)

    2017-07-01

    Highlights: • Ag-Co alloy has been prepared using pulsed electrodeposition method. • Wide range of Ag composition in the alloy was obtained. • XPS measurement evident the Ag and Co in metallic nature. • The electrodeposition method develop dendrite like morphology. • Detailed analysis of magnetic behaviour is carried out. - Abstract: Electrochemical alloying of immiscible Ag and Co was carried out at different current densities from electrolytes of two different concentrations, after optimizing the electrolytic bath and operating conditions. The samples obtained were characterized using X-ray diffraction to confirm the simultaneous deposition of Ag and Co and to determine their crystallographic structure. The atomic percentage of Ag and Co contents in the granular alloy was determined by ICP-OES analysis. The XPS spectra were observed to confirm the presence of Ag and Co in the metallic form in the granular alloy samples. The micrographs observed using scanning and transmission electron microscopes threw light on the surface morphology and the size of the particles. The magnetic nature of the samples was analyzed at room temperature by a vibration sample magnetometer. Their magnetic phase transition while heating was also studied to provide further evidence for the magnetic behaviour and the structure of the deposits.

  13. Magnetic properties of doped Mn-Ga alloys made by mechanical milling and heat treatment

    Energy Technology Data Exchange (ETDEWEB)

    Brown, Daniel R. [Department of Material Science and Engineering, Florida State University, Tallahassee, FL 32304 (United States); National High Magnetic Field Laboratory, Tallahassee, FL 32310 (United States); Han, Ke; Niu, Rongmei [National High Magnetic Field Laboratory, Tallahassee, FL 32310 (United States); Siegrist, Theo; Besara, Tiglet [Department of Material Science and Engineering, Florida State University, Tallahassee, FL 32304 (United States); Department of Chemical Engineering, Florida Agricultural and Mechanical University-Florida State University, Tallahassee, FL 32304 (United States)

    2016-05-15

    Mn-Ga alloys have shown hard magnetic properties, even though these alloys contain no rare-earth metals. However, much work is needed before rare-earth magnets can be replaced. We have examined the magnetic properties of bulk alloys made with partial replacement of both the Mn and Ga elements in the Mn{sub 0.8}Ga{sub 0.2} system. Bulk samples of Mn-Ga-Bi, Mn-Ga-Al, Mn-Fe-Ga and Mn-(FeB)-Ga alloys were fabricated and studied using mechanically milling and heat treatments while altering the atomic percentage of the third element between 2.5 and 20 at%. The ternary alloy exhibits all hard magnetic properties at room temperature with large coercivity. Annealed Mn-Ga-X bulk composites exhibit high coercivities up to 16.6 kOe and remanence up to 9.8 emu/g, that is increased by 115% over the binary system.

  14. Magnetic properties of doped Mn-Ga alloys made by mechanical milling and heat treatment

    Directory of Open Access Journals (Sweden)

    Daniel R. Brown

    2016-05-01

    Full Text Available Mn-Ga alloys have shown hard magnetic properties, even though these alloys contain no rare-earth metals. However, much work is needed before rare-earth magnets can be replaced. We have examined the magnetic properties of bulk alloys made with partial replacement of both the Mn and Ga elements in the Mn0.8Ga0.2 system. Bulk samples of Mn-Ga-Bi, Mn-Ga-Al, Mn-Fe-Ga and Mn-(FeB-Ga alloys were fabricated and studied using mechanically milling and heat treatments while altering the atomic percentage of the third element between 2.5 and 20 at%. The ternary alloy exhibits all hard magnetic properties at room temperature with large coercivity. Annealed Mn-Ga-X bulk composites exhibit high coercivities up to 16.6 kOe and remanence up to 9.8 emu/g, that is increased by 115% over the binary system.

  15. Electrochemical alloying of immiscible Ag and Co for their structural and magnetic analyses

    International Nuclear Information System (INIS)

    Santhi, Kalavathy; Kumarsan, Dhanapal; Vengidusamy, Naryanan; Arumainathan, Stephen

    2017-01-01

    Highlights: • Ag-Co alloy has been prepared using pulsed electrodeposition method. • Wide range of Ag composition in the alloy was obtained. • XPS measurement evident the Ag and Co in metallic nature. • The electrodeposition method develop dendrite like morphology. • Detailed analysis of magnetic behaviour is carried out. - Abstract: Electrochemical alloying of immiscible Ag and Co was carried out at different current densities from electrolytes of two different concentrations, after optimizing the electrolytic bath and operating conditions. The samples obtained were characterized using X-ray diffraction to confirm the simultaneous deposition of Ag and Co and to determine their crystallographic structure. The atomic percentage of Ag and Co contents in the granular alloy was determined by ICP-OES analysis. The XPS spectra were observed to confirm the presence of Ag and Co in the metallic form in the granular alloy samples. The micrographs observed using scanning and transmission electron microscopes threw light on the surface morphology and the size of the particles. The magnetic nature of the samples was analyzed at room temperature by a vibration sample magnetometer. Their magnetic phase transition while heating was also studied to provide further evidence for the magnetic behaviour and the structure of the deposits.

  16. What are the mesoscopic magnetic inhomogeneities in the dilute PdFeMn alloy? Polarized neutron study

    Energy Technology Data Exchange (ETDEWEB)

    Gordeev, G.; Axelrod, L.; Zabenkin, V.; Lazebnik, I.; Grigoriev, S.; Wagner, V.; Eckerlebe, H

    2003-07-01

    The 3D analysis of neutron depolarization was carried out for different thermomagnetic treatment of the dilute PdFeMn alloy versus temperature and magnetic field applied in magnetizing/demagnetizing cycles. Both the macroscopic magnetization and the mean fluctuation of local magnetization behavior were subtracted from experimental data. A complicated behavior of the latter was observed. The hysteresis of local magnetization fluctuations is found out but that of macroscopic magnetization is practically absent. The effort to apply the simple model for the description of magnetic inhomogeneities was made in order to understand the mesostructure of this alloy.

  17. Magnetic properties of melt-spun FeMnAlB alloys

    International Nuclear Information System (INIS)

    Betancourt, I.; Nava, F.

    2007-01-01

    Magnetic properties of melt spun Fe 89-x Mn 11 Al x (x=2,4,8,15) and Fe 87-y Mn 11 Al 2 By(y=6,8,10) alloy series were studied by vibrating sample magnetometry and complex permeability measurements. The saturation magnetization exhibited an initial high value of 210emu/g followed by a decreasing tendency with increasing Al and B additions (up to 139emu/g). On the other hand, the initial permeability showed variations within the range 1000-2000, whereas the relaxation frequency displayed a maximum of 2MHz for the 4at% Al alloy

  18. Evidence of new high-pressure magnetic phases in Fe-Pt Invar alloy

    International Nuclear Information System (INIS)

    Matsushita, M.; Endo, S.; Miura, K.; Ono, F.

    2003-01-01

    To investigate the magnetic properties of disordered Fe 70 Pt 30 Invar alloy under high pressure, measurements of the real part of the AC susceptibility (χ) were made under pressure up to 7.5 GPa in the temperature range 4.2-385 K using a cubic anvil high-pressure apparatus. The Curie temperature (T C ) decreased with increasing pressure, and then, two new high-pressure magnetic phases appeared. These results show that the ferromagnetism of Fe-Pt Invar alloy becomes weaker, and the antiferromagnetic interaction becomes dominant with increasing pressure

  19. Higher order magnetic modulation structures in rare earth metal, alloys and compounds under extreme conditions

    International Nuclear Information System (INIS)

    Kawano, S.

    2003-01-01

    Magnetic materials consisting of rare earth ions form modulation structures such as a helical or sinusoidal structure caused by the oscillating magnetic interaction between rare earth ions due to RKKY magnetic interaction. These modulation structures, in some cases, develop further to higher order modulation structures by additional modulations caused by higher order crystalline electric field, magnetic interactions such as spin-lattice interaction, external magnetic field and pressure. The higher order modulation structures are observed in a spin-slip structure or a helifan structure in Ho, and a tilt helix structure in a TbEr alloy. Paramagnetic ions originated from frustration generate many magnetic phases under applied external magnetic field. KUR neutron diffraction groups have performed the development and adjustment of high-pressure instruments and external magnetic fields for neutron diffraction spectrometers. The studies of 'neutron diffraction under extreme conditions' by the seven groups are described in this report. (Y. Kazumata)

  20. Industrialization of nanocrystalline Fe–Si–B–P–Cu alloys for high magnetic flux density cores

    International Nuclear Information System (INIS)

    Takenaka, Kana; Setyawan, Albertus D.; Sharma, Parmanand; Nishiyama, Nobuyuki; Makino, Akihiro

    2016-01-01

    Nanocrystalline Fe–Si–B–P–Cu alloys exhibit high saturation magnetic flux density (B s ) and extremely low magnetic core loss (W), simultaneously. Low amorphous-forming ability of these alloys hinders their application potential in power transformers and motors. Here we report a solution to this problem. Minor addition of C is found to be effective in increasing the amorphous-forming ability of Fe–Si–B–P–Cu alloys. It allows fabrication of 120 mm wide ribbons (which was limited to less than 40 mm) without noticeable degradation in magnetic properties. The nanocrystalline (Fe 85.7 Si 0.5 B 9.5 P 3.5 Cu 0.8 ) 99 C 1 ribbons exhibit low coercivity (H c )~4.5 A/m, high B s ~1.83 T and low W~0.27 W/kg (@ 1.5 T and 50 Hz). Success in fabrication of long (60–100 m) and wide (~120 mm) ribbons, which are made up of low cost elements is promising for mass production of energy efficient high power transformers and motors - Highlights: • Minor addition of C in FeSiBPCu alloy increases amorphous-forming ability. • The FeSiBPCuC alloy exhibits B s close to Si-steel and Core loss lower than it. • Excellent soft magnetic properties were obtained for 120 mm wide ribbons. • Nanocrystalline FeSiBPCuC alloy can be produced at industrial scale with low cost. • The alloy is suitable for making low energy loss power transformers and motors.

  1. Mechanochemical synthesis of nanocrystalline Fe and Fe–B magnetic alloys

    Energy Technology Data Exchange (ETDEWEB)

    Mohammadi, Majid; Ghasemi, Ali, E-mail: ali13912001@yahoo.com; Tavoosi, Majid

    2016-12-01

    Mechanochemical synthesis and magnetic characterization of nanocrystalline Fe and Fe–B magnetic alloys was the goal of this study. In this regard, different Fe{sub 2}O{sub 3}–B{sub 2}O{sub 3} powder mixtures with sufficient amount of CaH{sub 2} were milled in a planetary ball mill in order to produce nanocrystalline Fe, Fe{sub 95}B{sub 5} and Fe{sub 85}B{sub 15} alloys. The produced samples were characterized using X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). The results showed that, nanocrystalline Fe, Fe{sub 95}B{sub 5} and Fe{sub 85}B{sub 15} alloys can be successfully synthesized by the reduction reaction of Fe{sub 2}O{sub 3} and B{sub 2}O{sub 3} with CaH{sub 2} during mechanical alloying. The structure of produced Fe{sub 95}B{sub 5} and Fe{sub 85}B{sub 15} alloys was a combination of Fe and Fe{sub 2}B phases with average crystallite sizes of about 15 and 10 nm, respectively. The produced nanocrystalline alloys exhibited soft magnetic properties with the coercivity and saturation of magnetization in the range of 170–240 Oe and 9–28 emu/g, respectively. Increasing the boron content has a destructive effect on soft magnetic properties of Fe–B alloys. - Highlights: • We study the mechanochemical synthesis of nanocrystalline boron, Fe and Fe–B alloys. • We study the reduction reaction of B{sub 2}O{sub 3}–CaH{sub 2} during milling. • We study the reduction reaction of Fe{sub 2}O{sub 3}–CaH{sub 2} during milling. • We study the reduction reaction of Fe{sub 2}O{sub 3}–B{sub 2}O{sub 3}–CaH{sub 2} during milling. • We study the effect of B on magnetic properties of nanocrystalline Fe–B alloys.

  2. Recovery of cobalt-rare earth alloy particles by hydration-disintegration in a magnetic field

    International Nuclear Information System (INIS)

    McFarland, C.M.; Lerman, T.B.; Rockwood, A.C.

    1975-01-01

    A process for recovering magnetic alloy particles from a reaction product cake. The cake is placed in a reactor where it is contacted with a flowing water vapor-carrying gas which reacts with its calcium content to disintegrate the cake and produce a hydrated powder comprised substantially of calcium hydroxide and the alloy particles. A magnetic zone is generated into a cross-section of the reactor substantially encircling the inside wall thereof. The zone is generated by at least two poles of opposite polarity running the length of the zone. The hydrated powder is fluidized to dissociate and pass the calcium hydroxide out of the reactor. Finer-sized alloy particles carried by the fluidizing gas into the magnetic zone are subjected to the magnetic field where the poles are rotated or reversed at a rate which reverses the positions of the particles sufficiently to release adherent calcium hydroxide leaving the finer-sized alloy particles substantially within the magnetic zone. (auth)

  3. Effect of natural and magnetic convections on the structure of electrodeposited zinc-nickel alloy

    Energy Technology Data Exchange (ETDEWEB)

    Levesque, A., E-mail: alexandra.levesque@univ-reims.fr [LACMDTI URCA, BP 1039, 51687 Reims Cedex2 (France); Chouchane, S. [Faculte des Sciences, Universite Badji Mokhtar, Annaba (Algeria); Douglade, J. [LACMDTI URCA, BP 1039, 51687 Reims Cedex2 (France); Rehamnia, R. [Faculte des Sciences, Universite Badji Mokhtar, Annaba (Algeria); Chopart, J.-P. [LACMDTI URCA, BP 1039, 51687 Reims Cedex2 (France)

    2009-06-30

    The effects of a magnetic field applied in a direction parallel or perpendicular to the cathode substrate plane, during electrodeposition process of Zn-Ni alloy have been investigated by means of chronoamperometric measurements, X-ray diffraction and EDX analysis. The modification of crystal orientation of the alloy by the superimposition of a high magnetic field is discussed for alloys with a content of nickel range 6-13 at%. Whatever the phase composition obtained without magnetic field, either {gamma}-Ni{sub 5}Zn{sub 21} or a mixture of the {gamma} and zinc phases, which depends on the concentration of Ni{sup 2+} in the electrolyte bath, the preferential orientation (1 0 1) of the zinc phase is always favoured with perpendicular and parallel magnetic field. There is no saturation of this effect with amplitude of B up to 8 T. A study of different geometric configurations of the cathode, which induce more or less natural convection, consolidates these results. The structural modifications of Zn-Ni alloy electrodeposits are thus probably due to a magnetohydrodynamic effect. An additional phenomenon is observed in presence of a perpendicular applied magnetic field since the (3 3 0) preferential orientation of the {gamma}-Ni{sub 5}Zn{sub 21} disappears with high values of B.

  4. Effect of natural and magnetic convections on the structure of electrodeposited zinc-nickel alloy

    International Nuclear Information System (INIS)

    Levesque, A.; Chouchane, S.; Douglade, J.; Rehamnia, R.; Chopart, J.-P.

    2009-01-01

    The effects of a magnetic field applied in a direction parallel or perpendicular to the cathode substrate plane, during electrodeposition process of Zn-Ni alloy have been investigated by means of chronoamperometric measurements, X-ray diffraction and EDX analysis. The modification of crystal orientation of the alloy by the superimposition of a high magnetic field is discussed for alloys with a content of nickel range 6-13 at%. Whatever the phase composition obtained without magnetic field, either γ-Ni 5 Zn 21 or a mixture of the γ and zinc phases, which depends on the concentration of Ni 2+ in the electrolyte bath, the preferential orientation (1 0 1) of the zinc phase is always favoured with perpendicular and parallel magnetic field. There is no saturation of this effect with amplitude of B up to 8 T. A study of different geometric configurations of the cathode, which induce more or less natural convection, consolidates these results. The structural modifications of Zn-Ni alloy electrodeposits are thus probably due to a magnetohydrodynamic effect. An additional phenomenon is observed in presence of a perpendicular applied magnetic field since the (3 3 0) preferential orientation of the γ-Ni 5 Zn 21 disappears with high values of B.

  5. Compositional trends and magnetic excitations in binary and ternary Fe–Pd–X magnetic shape memory alloys

    International Nuclear Information System (INIS)

    Gruner, Markus Ernst; Hamann, Sven; Brunken, Hayo; Ludwig, Alfred; Entel, Peter

    2013-01-01

    Highlights: ► We discuss compositional trends in Fe–Pd–Cu and Fe–Pd–Mn magnetic shape memory alloys. ► We combine density functional theory and combinatorial thin film experiments. ► Magnetic excitations contribute decisively to the structural transformation behavior. -- Abstract: High throughput thin film experiments and first-principles calculations are combined in order to get insight into the relation between finite temperature transformation behavior and structural ground state properties of ternary Fe–Pd–X alloys. In particular, we consider the binding surface, i.e., the energy of the disordered alloy calculated along the Bain path between bcc and fcc which we model by a 108 atom supercell. We compare stoichiometric Fe 75 Pd 25 with ternary systems, where 4.6% of the Fe atoms were substituted by Cu and Mn, respectively. The computational trends are related to combinatorial experiments on thin film libraries for the systems Fe–Pd–Mn and Fe–Pd–Cu which reveal a systematic evolution of the martensitic start temperature with composition within the relevant concentration range for magnetic shape memory (MSM) applications. Our calculations include atomic relaxations, which were shown to be relevant for a correct description of the structural properties. Furthermore, we find that magnetic excitations can substantially alter the binding surface. The comparison of experimental and theoretical trends indicates that, both, compositional changes and magnetic excitations contribute significantly to the structural stability which may thus be tailored by specifically adding antiferromagnetic components

  6. Evaluation of microstructural difference in low alloy steel (SA508 CI.3) by magnetic measurements

    International Nuclear Information System (INIS)

    Chi, Se Hwan; Park, Duck Gun; Hong, Jun Hwa; Kuk, Il Hium; Song, Sook Hyang; Shur, Dong Soo

    1997-01-01

    Magnetic measurements on SA 508 Cl. 3 low alloy reactor pressure vessel (RPV) steels of three different refining processes were conducted to prepare baseline magnetic properties for future comparison with that of irradiated one and to examine the correlation between microstructures and magnetic parameters. TEM(transmission electron microscopy) on thin films and carbon replications were performed for microstructural investigation, and microhardness, tensile and fracture toughness tests were conducted for mechanical properties measurement. Barkhausen noise analysis was conducted and hysteresis parameters were measured. Microstructure, mechanist and magnetic properties were interpreted together to explore their inter-relationship. Also the applicability of a magnetic nondestructive evaluation method for monitoring fine microstructural changes in low alloy steels of complicated microstructure was examined. The results showed that, of all magnetic parameters, Barkhausen noise amplitudes show consistent change with microstructure (grain size, carbide microstructure, lath width) and hardness of the materials. For monitoring microstructural and mechanical property changes of low alloy steel under service environment of reactor pressure vessel steels, Barkhausen noise amplitude and coercivity appear to be as key magnetic parameters useful for nondestructive evaluation.

  7. Study of magnetism in Ni-Cr hardface alloy deposit on 316LN stainless steel using magnetic force microscopy

    Science.gov (United States)

    Kishore, G. V. K.; Kumar, Anish; Chakraborty, Gopa; Albert, S. K.; Rao, B. Purna Chandra; Bhaduri, A. K.; Jayakumar, T.

    2015-07-01

    Nickel base Ni-Cr alloy variants are extensively used for hardfacing of austenitic stainless steel components in sodium cooled fast reactors (SFRs) to avoid self-welding and galling. Considerable difference in the compositions and melting points of the substrate and the Ni-Cr alloy results in significant dilution of the hardface deposit from the substrate. Even though, both the deposit and the substrate are non-magnetic, the diluted region exhibits ferromagnetic behavior. The present paper reports a systematic study carried out on the variations in microstructures and magnetic behavior of American Welding Society (AWS) Ni Cr-C deposited layers on 316 LN austenitic stainless steels, using atomic force microscopy (AFM) and magnetic force microscopy (MFM). The phase variations of the oscillations of a Co-Cr alloy coated magnetic field sensitive cantilever is used to quantitatively study the magnetic strength of the evolved microstructure in the diluted region as a function of the distance from the deposit/substrate interface, with the spatial resolution of about 100 nm. The acquired AFM/MFM images and the magnetic property profiles have been correlated with the variations in the chemical compositions in the diluted layers obtained by the energy dispersive spectroscopy (EDS). The study indicates that both the volume fraction of the ferromagnetic phase and its ferromagnetic strength decrease with increasing distance from the deposit/substrate interface. A distinct difference is observed in the ferromagnetic strength in the first few layers and the ferromagnetism is observed only near to the precipitates in the fifth layer. The study provides a better insight of the evolution of ferromagnetism in the diluted layers of Ni-Cr alloy deposits on stainless steel.

  8. Correlation of electrical transport and magnetism in amorphous Mn-B alloys

    Science.gov (United States)

    Bryden, W. A.; Morgan, J. S.; Kistenmacher, T. J.; Moorjani, K.

    1987-04-01

    X-ray scattering, magnetism, and electrical transport studies on amorphous thin films of MnxB100-x alloys with x=52 and 48 are reported. Each alloy exhibits a low-field (5 G) static susceptibility peak (10 K, x=52; 16 K, x=48) associated with a spin-glass transition. Isothermal magnetization data (6 K) are analyzed within the random anisotropy model of Chudnovsky, Saslow, and Serota. The magnetization isotherm for the x=52 alloy is dominated at high fields (>24 kG) by field-induced moments, while for x=48 a term (αH-1/2) arising from a ferromagnet with a wandering axis prevails to the highest field strength (44 kG). Initially the electrical resistance for these Mn-B alloys decreases monotonically with decreasing temperature, reaching a minimum (Tm) at 22 K (x=52) and 45 K (x=48). For T>Tm, a quadratic form can be effectively employed, with a negative T2 coefficient and a positive linear coefficient. The rise in resistivity for Talloys display only weakly field-dependent (to 10 kG) magnetoresistance.

  9. Microstructure and magnetic properties of Nd-Fe-B-(Re, Ti alloys

    Directory of Open Access Journals (Sweden)

    Hasiak Mariusz

    2015-03-01

    Full Text Available The microstructure and magnetic properties of nanocomposite hard magnetic Nd-Fe-B-(Re, Ti materials with different Nd and Fe contents are studied. The role of Re and Ti addition in phase composition and volume fraction of the Nd-Fe-B phase is determined. All samples are annealed at the same temperature of 993 K for 10 min. Mössbauer spectroscopy shows that the addition of 4 at.% of Re to the Nd8Fe78B14 alloy leads to creation of an ineligible amount of the magnetically hard Nd2Fe14B phase. Moreover, the microstructure and magnetic characteristics recorded in a wide range of temperatures for the Nd8Fe79−xB13Mx (x = 4; M = Re or Ti alloys are also analyzed.

  10. Plasma spraying of hard magnetic coatings based on Sm-Co alloys

    International Nuclear Information System (INIS)

    KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" data-affiliation=" (Siberian State Aerospace University named after Academician M.F. Reshetnev 31 KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" >Saunin, V N; KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" data-affiliation=" (Siberian State Aerospace University named after Academician M.F. Reshetnev 31 KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" >Telegin, S V

    2015-01-01

    Our research is focused on the formation of hard magnetic coatings by plasma spraying an arc-melted Sm-Co powder. We have studied basic magnetic characteristics depending on the components ratio in the alloy. A sample with a 40 wt.% Sm coating exhibits the highest coercive force (63 kOe) as compared to near-to-zero coercive force in the starting powder. X-ray structure analysis of the starting alloy and the coating reveals that the amount of SmCo 5 phase in the sprayed coating increases occupying up to 2/3 of the sample. We have also studied temperature dependence of the coating and have been able to obtain plasma sprayed permanent magnets operating within the temperature range from -100 to +500 °C. The technique used does not involve any additional thermal treatment and allows a coating to be formed right on the magnetic conductor surface irrespective of the conductor geometry

  11. Magnetic behavior of the nanophase of YbNi2 alloys

    Science.gov (United States)

    Ivanshin, V. A.; Gataullin, E. M.; Sukhanov, A. A.; Ivanshin, N. A.; Rojas, D. P.; Fernández Barquín, L.

    2017-04-01

    Variations in magnetic properties of the heavy-fermion YbNi2 alloy when milled in a high energy ball milling system have been investigated. The ferromagnetic transition ( T C = 10.4 K) in the initial sample almost vanishes after milling, which leads to the appearance of a magnetic transition at T* = 3.2 K in nanocrystallites. Before milling, processes of spin-lattice relaxation of the Orbach-Aminov type with the participation of the first excited Stark sublevel of the Yb3+ ion located at 75 K are dominating in the electron spin dynamics in the paramagnetic phase of the alloy. A comparative study of the temperature dependence of the magnetic properties and spectra of electron paramagnetic resonance in poly- and nanocrystalline samples indicates the existence of a magnetic inhomogeneity of the compound arising upon milling.

  12. Preparation of rare earth-cobalt magnet alloy by reduction-diffusion process

    International Nuclear Information System (INIS)

    Krishnan, T.S.

    1980-01-01

    Preparation of rare earth-cobalt alloys by reduction-diffusion (R-D) process is described. The process essentially involves mixing of the rare earth oxide and cobalt/cobalt oxide powders in proper proportion and high temperature reduction of the charge in hydrogen atmosphere, followed by aqueous leaching of the reduced mass to yield the alloy powder. Comparison is made of the magnetic properties of the R-D powder with those of the powder prepared by the direct melting (DM) route and it is observed from the reported values for SmCo 5 that the energy product of the R-D powder (approximately 22 MGOe) is only marginally lower than that of the directly melted alloy (approximately 25 MGOe). The paper also includes the results of studies carried out at the Bhabha Atomic Research Centre, Bombay, on the preparation of misch metal-cobalt alloy by the R-D process. (auth.)

  13. Evidence of the extended orientational order in amorphous alloys obtained from magnetic measurements

    International Nuclear Information System (INIS)

    Chudnovsky, E.M.; Tejada, J.

    1993-01-01

    Magnetic measurements of R-Fe-B (R = rare earth) amorphous alloys show that magnetic anisotropy axes are correlated on the scale ∼ 100 A. The X-ray study of these materials does not reveal any positional correlations beyond the 10 A scale. These observations support theoretical suggestions that the orientational order in amorphous systems can be much more extended than the positional order. (orig.)

  14. Fully Relativistic Temperature-Dependent Electronic Transport Properties of Magnetic Alloys From the First Principles.

    Czech Academy of Sciences Publication Activity Database

    Wagenknecht, David; Carva, K.; Turek, Ilja

    2017-01-01

    Roč. 53, č. 11 (2017), č. článku 1700205. ISSN 0018-9464 R&D Projects: GA ČR GA15-13436S Institutional support: RVO:68081723 Keywords : electronic transport * magnetic alloys * ab initio theory Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 1.243, year: 2016

  15. Phase and magnetic studies of the high-energy alloyed Ni-Fe

    Czech Academy of Sciences Publication Activity Database

    Jirásková, Yvonna; Buršík, Jiří; Turek, Ilja; Hapla, Miroslav; Titov, A.; Životský, O.

    2014-01-01

    Roč. 594, May (2014), s. 133-140 ISSN 0925-8388 R&D Projects: GA ČR(CZ) GAP108/11/1350 Grant - others:VŠB(CZ) CZ.1.07/2.3.00/20.0074 Institutional support: RVO:68081723 Keywords : Ni-Fe * mechanical alloying * magnetic properties * microstructure * particle interactions Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.999, year: 2014

  16. Magnetic and electrical properties of several Mn-based amorphous alloys

    Science.gov (United States)

    Obi, Y.; Morita, H.; Fujimori, H.

    1987-03-01

    Magnetic and electrical properties of amorphous Mn-Y, Mn-Zr, and Mn-Nb alloys have been investigated. All these alloys have a temperature-dependent susceptibility which is well fitted by a Curie-Weiss law. This implies the existence of localized magnetic moments associated with the Mn atoms. In addition, amorphous Mn-Y alloys exhibit spin-glass characteristics at low temperature. The experimental results of the electrical resistivity show that the temperature coefficient of resistivity (TCR) of both Mn-Y and Mn-Zr are negative, while Mn-Nb has a positive TCR. On the other hand, the resistivity-temperature curves of Mn-Zr and Mn-Nb have nearly the same tendency but are different from that of Mn-Y.

  17. Formation of soft magnetic high entropy amorphous alloys composites containing in situ solid solution phase

    Science.gov (United States)

    Wei, Ran; Sun, Huan; Chen, Chen; Tao, Juan; Li, Fushan

    2018-03-01

    Fe-Co-Ni-Si-B high entropy amorphous alloys composites (HEAACs), which containing high entropy solid solution phase in amorphous matrix, show good soft magnetic properties and bending ductility even in optimal annealed state, were successfully developed by melt spinning method. The crystallization phase of the HEAACs is solid solution phase with body centered cubic (BCC) structure instead of brittle intermetallic phase. In addition, the BCC phase can transformed into face centered cubic (FCC) phase with temperature rise. Accordingly, Fe-Co-Ni-Si-B high entropy alloys (HEAs) with FCC structure and a small amount of BCC phase was prepared by copper mold casting method. The HEAs exhibit high yield strength (about 1200 MPa) and good plastic strain (about 18%). Meanwhile, soft magnetic characteristics of the HEAs are largely reserved from HEAACs. This work provides a new strategy to overcome the annealing induced brittleness of amorphous alloys and design new advanced materials with excellent comprehensive properties.

  18. Magnetic susceptibility of CoFeBSiNb alloys in liquid state

    Energy Technology Data Exchange (ETDEWEB)

    Sidorov, V., E-mail: vesidor@mail.ru [Ural State Pedagogical University, Ekaterinburg (Russian Federation); Hosko, J. [Institute of Physics SAS, Bratislava (Slovakia); Mikhailov, V.; Rozkov, I.; Uporova, N. [Ural State Pedagogical University, Ekaterinburg (Russian Federation); Svec, P.; Janickovic, D.; Matko, I.; Svec Sr, P. [Institute of Physics SAS, Bratislava (Slovakia); Malyshev, L. [Ural Federal University, Ekaterinburg (Russian Federation)

    2014-03-15

    The influence of small additions of gallium and antimony on magnetic susceptibility of the bulk glass forming Co{sub 47}Fe{sub 20.9}B{sub 21.2}Si{sub 4.6}Nb{sub 6.3} alloy was studied in a wide temperature range up to 1830 K by the Faraday’s method. The undercooling for all the samples was measured experimentally. Both Ga and Sb additions were found to increase liquidus and solidification temperatures. However, gallium atoms strengthen interatomic interaction in the melts, whereas antimony atoms reduce it. - Highlights: • Bulk metallic glasses from CoFeBSiNb-based alloys were produced as in situ composites. • Magnetic susceptibility of these alloys was measured in a wide temperature range including liquid state. • Undercooling of these melts was measured experimentally. • Ga additions strengthen interatomic interaction in BMG melts, whereas Sb atoms reduce it.

  19. Crystallization behavior and magnetic properties in High Fe content FeBCSiCu alloy system

    Energy Technology Data Exchange (ETDEWEB)

    Fan, X.D., E-mail: fanxd@seu.edu.cn; Shen, B.L., E-mail: blshen@seu.edu.cn

    2015-07-01

    High Fe content FeBCSiCu nanocrystalline alloys are prepared by annealing melt-spun amorphous ribbons with aim at increasing saturation magnetic flux density. Microstructures identified by XRD and TEM reveal that Cu addition inhibits the surface crystallization of Fe{sub 86}B{sub 7}C{sub 7} alloy and improve its glass-forming ability. Activation energy of crystallization calculated by Kissinger's equation indicates that both Cu and Si addition promotes the precipitation of α-Fe phase and improves the thermal stability. VSM and DC B–H loop tracer measurements show that the Fe{sub 85.5}B{sub 7}C{sub 6}Si{sub 1}Cu{sub 0.5} nanocrystalline alloy exhibits high saturation magnetic flux density of 1.8 T and low coercivity of 10 A/m, respectively. AC properties measured by AC B–H analyzer show this alloy exhibits low core loss of 0.35 W/kg at 1 T at 50 Hz. Low material cost and convenient productivity make the Fe{sub 85.5}B{sub 7}C{sub 6}Si{sub 1}Cu{sub 0.5} nanocrystalline alloy an economical application in industry. - Highlights: • Cu addition inhibits the surface crystallization and improves the GFA. • The competitive formation of Fe{sub 3}C and α-Fe phase impedes the devitrification. • Fe{sub 85.5}B{sub 7}C{sub 6}Si{sub 1}Cu{sub 0.5} nanocrystalline alloy exhibits excellent magnetic properties. • The alloy system has an economical advantage and convenient productivity.

  20. Magnetic properties of exchange-coupled trilayers of amorphous rare-earth-cobalt alloys

    International Nuclear Information System (INIS)

    Wuechner, S.; Toussaint, J.C.; Voiron, J.

    1997-01-01

    From amorphous thin films from alloys of rare earths (Gd, Sm), yttrium or zirconium with cobalt we have prepared trilayers with very clean interfaces appropriate for the study of magnetic coupling. The sandwiches were typically Y-Co/Gd-Co/Y-Co and Sm-Co/X/Sm-Co ' (X=Gd-Co, Co-Zr, Co). The three individual layers are coupled magnetically by exchange interactions between cobalt moments throughout the entire sample. This coupling associated with the specific properties of the given alloy (magnetic moment, anisotropy, coercivity) leads to ferrimagnetic or ferromagnetic structures of the magnetization of adjacent layers and to novel magnetization processes. For systems consisting of magnetically hard external layers with different coercivities and a soft central layer (Sm-Co/X/Sm-Co ' , X=Gd-Co, Co-Zr), the influence of the central layer close-quote s thickness and type of the material on coupling and magnetization processes have been studied quantitatively. Numerical simulations using a one-dimensional model for describing the magnetization processes observed in sandwich systems fit the magnetization curves of these model systems particularly well. copyright 1997 The American Physical Society

  1. Capping layer-tailored interface magnetic anisotropy in ultrathin Co{sub 2}FeAl films

    Energy Technology Data Exchange (ETDEWEB)

    Belmeguenai, M., E-mail: belmeguenai.mohamed@univ-paris13.fr; Zighem, F.; Chérif, S. M. [LSPM (CNRS-UPR 3407), Université Paris 13, Sorbonne Paris Cité, 99 Avenue Jean-Baptiste Clément, 93430 Villetaneuse (France); Gabor, M. S., E-mail: mihai.gabor@phys.utcluj.ro; Petrisor, T. [Center for Superconductivity, Spintronics and Surface Science, Department of Physics and Chemistry, Technical University of Cluj-Napoca, Str. Memorandumului No. 28, RO-400114 Cluj-Napoca (Romania); Tiusan, C. [Center for Superconductivity, Spintronics and Surface Science, Department of Physics and Chemistry, Technical University of Cluj-Napoca, Str. Memorandumului No. 28, RO-400114 Cluj-Napoca (Romania); Institut Jean Lamour, CNRS, Lorraine Université, BP 70239, F-54506 Vandoeuvre (France)

    2015-01-14

    Co{sub 2}FeAl (CFA) thin films of various thicknesses (2 nm ≤ d ≤ 50 nm) have been grown on (001) MgO single crystal substrates and then capped with Cr, V, and Ta. Their magnetic and structural properties have been studied by x-ray diffraction (XRD), vibrating sample magnetometry, and broadband microstrip ferromagnetic resonance (MS-FMR). The XRD revealed that the films are epitaxial with the cubic [001] CFA axis normal to the substrate plane and that the chemical order varies from the B2 phase to the A2 phase when decreasing the thickness. The deduced lattice parameters showed that the Cr-capped films exhibit a larger tetragonal distortion, as compared with the films capped with V or Ta. The presence of magnetic dead layers has been observed in CFA samples capped with V and Ta but not in the case of the Cr-capped ones. The effective magnetization, deduced from the fit of MS-FMR measurements, increases (decreases) linearly with the CFA inverse thickness (1/d) for the Cr-capped (Ta-capped) films while it is constant for the V-capped ones. This allows quantifying the perpendicular surface anisotropy coefficients of −0.46 erg/cm{sup 2} and 0.74 erg/cm{sup 2} for Cr and Ta-capped films, respectively. Moreover, the fourfold and the uniaxial anisotropy fields, measured in these films, showed different trends with a respect to the CFA inverse thickness. This allows inferring that a non-negligible part of the fourfold magnetocrystalline term is of interfacial origin.

  2. Growth, Characterization and Properties of Ultrathin Magnetic Films and Multilayers. Materials Research Society Symposium Proceedings. Volume 151

    Science.gov (United States)

    1990-05-01

    Prinz, X. Liu, A. Petrou, and L. Salamanca-Young ELECTRON-SPIN POLARIZATION IN TUNNEL JUNCTIONS WITH FERROMAGNETIC EuS BARRIERS 167 Xin Hao, J.S...931837-48-0 Volume 84-Scientific Basis for Nuclear Waste Management X, J. K. Bates, W. B. Seefeldt , 1987, ISBN 0-931837-49-9 Volume 85-Microstructural...feature makes up approximately 28% of the spec- trum’s intensity. With the magnetic field this is reduced to less than 3%. The energy barrier supplied

  3. Enhancement of TE polarized light extraction efficiency in nanoscale (AlN)m /(GaN)n (m>n) superlattice substitution for Al-rich AlGaN disorder alloy: ultra-thin GaN layer modulation

    International Nuclear Information System (INIS)

    Jiang, Xin-he; Shi, Jun-jie; Zhong, Hong-xia; Huang, Pu; Ding, Yi-min; Yu, Tong-jun; Shen, Bo; Lu, Jing; Zhang, Min; Wang, Xihua

    2014-01-01

    The problem of achieving high light extraction efficiency in Al-rich Al x Ga 1−x N is of paramount importance for the realization of AlGaN-based deep ultraviolet (DUV) optoelectronic devices. To solve this problem, we investigate the microscopic mechanism of valence band inversion and light polarization, a crucial factor for enhancing light extraction efficiency, in Al-rich Al x Ga 1−x N alloy using the Heyd–Scuseria–Ernzerhof hybrid functional, local-density approximation with 1/2 occupation, and the Perdew–Burke–Ernzerhof functional, in which the spin–orbit coupling effect is included. We find that the microscopic Ga-atom distribution can effectively modulate the valence band structure of Al-rich Al x Ga 1−x N. Moreover, we prove that the valence band arrangement in the decreasing order of heavy hole, light hole, and crystal-field split-off hole can be realized by using nanoscale (AlN) m /(GaN) n (m>n) superlattice (SL) substituting for Al-rich Al x Ga 1−x N disorder alloy as the active layer of optoelectronic devices due to the ultra-thin GaN layer modulation. The valence band maximum, i.e., the heavy hole band, has p x - and p y -like characteristics and is highly localized in the SL structure, which leads to the desired transverse electric (TE) polarized (E⊥c) light emission with improved light extraction efficiency in the DUV spectral region. Some important band-structure parameters and electron/hole effective masses are also given. The physical origin for the valence band inversion and TE polarization in (AlN) m /(GaN) n SL is analyzed in depth. (paper)

  4. Effects of Cd{sub 1-x}Zn{sub x}S alloy composition and post-deposition air anneal on ultra-thin CdTe solar cells produced by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Clayton, A.J., E-mail: Andrew.J.Clayton@Swansea.ac.uk [Centre for Solar Energy Research, College of Engineering, Swansea University, OpTIC, St. Asaph, LL17 0JD (United Kingdom); Baker, M.A.; Babar, S.; Grilli, R. [The Surface Analysis Laboratory, Department of Mechanical Engineering Sciences, University of Surrey, Guildford, GU2 7XH (United Kingdom); Gibson, P.N. [Institute for Health and Consumer Protection, Joint Research Centre of the European Commission, 21027, Ispra, VA (Italy); Kartopu, G.; Lamb, D.A. [Centre for Solar Energy Research, College of Engineering, Swansea University, OpTIC, St. Asaph, LL17 0JD (United Kingdom); Barrioz, V. [Engineering and Environment, Department of Physics and Electrical Engineering, Northumbria University, Newcastle, NE1 8ST (United Kingdom); Irvine, S.J.C. [Centre for Solar Energy Research, College of Engineering, Swansea University, OpTIC, St. Asaph, LL17 0JD (United Kingdom)

    2017-05-01

    Ultra-thin CdTe:As/Cd{sub 1-x}Zn{sub x}S photovoltaic solar cells with an absorber thickness of 0.5 μm were deposited by metal-organic chemical vapour deposition on indium tin oxide coated boro-aluminosilicate substrates. The Zn precursor concentration was varied to compensate for Zn leaching effects after CdCl{sub 2} activation treatment. Analysis of the solar cell composition and structure by X-ray photoelectron spectroscopy depth profiling and X-ray diffraction showed that higher concentrations of Zn in the Cd{sub 1-x}Zn{sub x}S window layer resulted in suppression of S diffusion across the CdTe/Cd{sub 1-x}Zn{sub x}S interface after CdCl{sub 2} activation treatment. Excessive Zn content in the Cd{sub 1-x}Zn{sub x}S alloy preserved the spectral response in the blue region of the solar spectrum, but increased series resistance for the solar cells. A modest increase in the Zn content of the Cd{sub 1-x}Zn{sub x}S alloy together with a post-deposition air anneal resulted in an improved blue response and an enhanced open circuit voltage and fill factor. This device yielded a mean efficiency of 8.3% over 8 cells (0.25 cm{sup 2} cell area) and best cell efficiency of 8.8%. - Highlights: • CdCl{sub 2} anneal treatment resulted in S diffusing to the back contact. • High Zn levels created mixed cubic/hexagonal structure at the p-n junction. • Increased Zn in Cd{sub 1-x}Zn{sub x}S supressed S diffusion into CdTe. • Device V{sub oc} was enhanced overall with an additional back surface air anneal.

  5. Magnetic properties of (Mn1-xRux)3Ga alloys

    International Nuclear Information System (INIS)

    Hori, T.; Akimitsu, M.; Miki, H.; Ohoyoama, K.; Yamaguchi, Y.

    2002-01-01

    We found that the pseudo binary alloys Mn 1-x Ru x 3 Ga, with 0.33≤x≤0.67, have an ordered b.c.c. structure. The lattice constant a is almost constant with respect to x: a=6.000 A for x=0.33 and a=5.992 A for x=0.67. For the alloy with x=0.33, i.e. Mn 2 RuGa, the magnetization is almost saturated in a field of 20 kOe. The saturation magnetization at 4.2 K is 23 emu/g, and the Curie temperature, T C , is 460 K. The T C of (Mn 1-x Ru x ) 3 Ga decreases almost linearly with increasing x, and it vanishes around x=0.67 (MnRu 2 Ga). We also determined atomic and magnetic structures from neutron diffraction experiments. The alloy Mn 2 RuGa (x=0.33) has an ordered structure of CuHg 2 Ti type; the magnetic Mn atoms mainly occupy the 4a (0,0,0) and 4d (3/4,3/4,3/4) sites. We also observed that the magnetic moments of Mn atoms on the 4a and 4d sites are antiparallel to each other; values of the magnetic moment are μ a =4.6 and μ d =3.3 μ B per Mn atom. (orig.)

  6. Effect of crystallization rate of initial alloy on magnetic properties of amorphous tape

    International Nuclear Information System (INIS)

    Roshchin, V.E.; Gribanov, V.P.; Shcherbakov, D.G.; Gun'kin, V.E.

    1994-01-01

    An investigation is made into mechanism and character of cooling rate effect when castings crytallizing on magnetic properties of rapidly quenched amorphous tape of Fe 78 B 12 Si 9 Ni 1 alloy. The increase of cooling rate and holding at heat for superheated melt is shown to result in a rise of Curie point of amorphous tape

  7. Neutronic irradiation effect in FeNi alloys, observed by magnetic measurements

    International Nuclear Information System (INIS)

    Sciani, V.; Lucki, G.

    1986-01-01

    In this work some aspects of radiation damage are analysed through the influence of neutron irradiation on magnetic properties of FeNi alloys. The main points emphasized are: radiation enhanced diffusion, determination of the activation energy for diffusion process and vacancies supersaturation, which is an important parameter from technological point of view and a necessary condition for the void formation. (Author) [pt

  8. Sc-45 nuclear magnetic resonance analysis of precipitation in dilute Al-Sc alloys

    NARCIS (Netherlands)

    Celotto, S; Bastow, TJ

    Nuclear magnetic resonance (NMR) with Sc-45 is used to determine the solid solubility of scandium in aluminium and to follow the precipitation of Al3Sc during the ageing of an Al-0.06 at.% Sc alloy via the two fully resolved peaks, corresponding to Sc in the solid solution Al matrix and to Sc in the

  9. Synthesis of Fe–Si–B–Mn-based nanocrystalline magnetic alloys ...

    Indian Academy of Sciences (India)

    Administrator

    ing/alloying is employed for the synthesis of amorphous and other materials ... applications in aerospace and chemical industries. Pro- duction of magnetic .... a2 = −1∙7756 from Cauchy constants from the Langford table. The lattice strain could ...

  10. Mechanism of magnetic recovery in the disorder-order transformation of Fe70Al30 mechanically deformed alloys

    International Nuclear Information System (INIS)

    Rodriguez, D. Martin; Apinaniz, E.; Plazaola, F.; Garitaonandia, J.S.; Jimenez, J.A.; Schmool, D.S.; Cuello, G.J.

    2005-01-01

    The degree of order in Fe-Al intermetallic alloys has an important influence on their magnetic properties. Moreover, the deformation of ordered alloys causes a dramatic increase of magnetization. If deformed alloys are heated, their magnetic properties decrease again. The reordering process was monitored by neutron diffraction, Moessbauer spectroscopy, and calorimetric measurements on the Fe 70 Al 30 crushed alloy. This indicates that the reordering process occurs in two stages. In the first (150-200 deg. C) new small B2 phase domains are nucleated due to vacancy migration. A second reordering stage occurs between 300 and 450 deg. C, where dislocation motion induces B2 domain growth and A2 phase elimination. The main mechanism responsible for this decrease of magnetization during the reordering process is the decrease of the disordered A2 phase content in the alloy

  11. Interfacial exchange, magnetic coupling and magnetoresistance in ultra-thin GdN/NbN/GdN tri-layers

    Science.gov (United States)

    Takamura, Yota; Goncalves, Rafael S.; Cascales, Juan Pedro; Altinkok, Atilgan; de Araujo, Clodoaldo I. L.; Lauter, Valeria; Moodera, Jagadeesh S.; MIT Team

    Superconducting spin-valve structures with a superconductive (SC) spacer sandwiched between ferromagnetic (FM) insulating layers [Li PRL 2013, Senapati APL 2013, Zhu Nat. Mat. 2016.] are attractive since the SC and FM characteristics can mutually be controlled by the proximity effect. We investigated reactively sputtered GdN/NbN/GdN tri-layer structures with various (SC) NbN spacer thicknesses (dNbN) from superconducting to normal layers. Magnetoresistive behavior similar to GMR in metallic magnetic multilayers was observed in the tri-layers with dNbN between 5-10 monolayers (ML), where thinner NbN layers did not show superconductivity down to 4.2 K. The occurrence of GMR signal indicates the presence of a ML of FM metallic layers at the GdN/NbN interfaces. Susceptibility and transport measurements in these samples revealed that the interface layers (ILs) are ferromagnetically coupled with adjacent GdN layers. The thickness of each of the IL is deduced to be about 1.25 ML, and as a result for dNbN magnetically coupled and switched simultaneously. These findings and interfacial characterization by various techniques will be presented. Work supported by NSF and ONR Grants.

  12. Structural, morphological and magnetic characterization of electrodeposited Co–Fe–W alloys

    Energy Technology Data Exchange (ETDEWEB)

    Noce, R. Della, E-mail: rodrnoce@iq.unesp.br [Instituto de Química, Universidade Estadual Paulista, UNESP, 14800-900 Araraquara, SP (Brazil); Benedetti, A.V.; Magnani, M. [Instituto de Química, Universidade Estadual Paulista, UNESP, 14800-900 Araraquara, SP (Brazil); Passamani, E.C. [Departamento de Física, Universidade Federal do Espírito Santo, 29075-910 Vitória, ES (Brazil); Kumar, H.; Cornejo, D.R. [Instituto de Física, Universidade de São Paulo, USP, 05508-090 São Paulo, SP (Brazil); Ospina, C.A. [Electron Microscopy Laboratory, Brazilian Nanotechnology National Laboratory, 13083-970 Campinas, SP (Brazil)

    2014-10-25

    Highlights: • Small W additions (up to 9 at.%) to the Co{sub 35}Fe{sub 65} binary system. • Electrodeposited Co–Fe–W alloys characterization by XRD, SEM, TEM, Mössbauer spectroscopy and magnetic measurements. • Production of Co–Fe–W alloys with low values of coercivity and high saturation magnetization. • Potential materials for applications in magnetic devices such as read/write heads and hard disks. - Abstract: Structural, morphological and magnetic characterization of electrodeposited Co–Fe–W alloys, containing small amounts of W (up to 9 at.%), were performed using X-ray diffractometry, scanning (SEM) and transmission (TEM) electron microscopy, Mössbauer spectroscopy and magnetization measurements. Electrodeposited (Co{sub 100−x}Fe{sub x}){sub 100−y}W{sub y} films (x = 63–72 at.% Fe, y = 4–9 at.% W) were successfully produced varying the applied cathodic current density (i{sub c}) between 0.5 and 10 mA cm{sup −2}. X-ray diffraction results revealed a bcc-like structure for all studied compositions with average crystallite size ranging from 16 to 35 nm, as also confirmed by TEM results. SEM images indicated that needle-type morphology is dominant for the deposits containing lower W content (up to 4.5 at.%.), while a cauliflower-type behavior is observed for higher W content deposits. Room temperature Mössbauer spectra indicate the presence of two magnetic species for all samples; one component associated with an ordered Co–Fe–W fraction (crystalline grain core) and a magnetic disordered Co–Fe–W contribution, which can be attributed to the grain boundaries/grain surfaces. Magnetization was observed to be in the film plane along the film direction, except the sample prepared at i{sub c} = 10 mA cm{sup −2} that is slightly canted from in- to out-of-plane geometry. Magnetic measurements show high saturation magnetization values accompanied by low coercivity ones for the electrodeposited Co–Fe–W alloys, making these

  13. Structure and magnetism of ultrathin Co and Fe films epitaxially grown on Pd/Cu(0 0 1)

    International Nuclear Information System (INIS)

    Lu, Y.F.; Przybylski, M.; Yan, L.; Barthel, J.; Meyerheim, H.L.; Kirschner, J.

    2005-01-01

    A contribution originating from the Co/Pd and Fe/Pd interfaces to the magneto-optical Kerr effect (MOKE) rotation is analyzed for Co and/or Fe films grown on a Pd-buffer-monolayer on Cu(0 0 1). A clear increase of the MOKE signal in comparison to the Co(Fe) films grown directly on Cu(0 0 1) is detected. An interpretation is supported by similar observations for Co films grown on Pd(1 1 0) and Pd(0 0 1). In particular, the sign reversal of the Kerr loops with increasing thickness of the Co(Fe) films is discussed. Magneto-optical effects are separated from the real magnetization and its dependence on the film thickness

  14. Magnetic properties of Co and Fe on Pt(111), Rh(111) and Pd(111): From single atoms to ultrathin films

    Energy Technology Data Exchange (ETDEWEB)

    Lehnert, Anne; Rusponi, Stefano; Etzkorn, Markus; Moulas, Geraud; Brune, Harald [IPN, EPF-Lausanne (Switzerland); Gambardella, Pietro [CREA, Catalan Institute of Nanotechnology (Spain); Bencok, Peter [ESRF, Grenoble (France)

    2009-07-01

    Single atoms of Co on Pt(111) are known to have a giant magnetic anisotropy energy (MAE) of 9.3 meV/atom. This is due to the reduced coordination and the strong spin-orbit coupling of the Pt 5d-states. In order to study the contribution of a highly polarizable substrate to the MAE, we investigated single Co atoms on Pd(111) and Rh(111) using X-ray magnetic circular dichroism (XMCD). We find a decreasing MAE moving from a 5d-substrate (Pt) to 4d-substrates (Pd and Rh). Co has a large orbital moment L of about 0.7 independent of the substrate. The easy axis is out-of-plane for Pt(111) and Pd(111) whereas it is in-plane for Co/Rh(111). Fe has on all substrates an out-of-plane easy axis, a very small anisotropy energy, and a L/S ratio of about 0.1. With increasing coverage the coordination number of the adatom increases and generally leads to a reduced MAE and orbital moment compared to the single atom. We measure one monolayer of Co and Fe on Pt(111) and Rh(111) and find MAE values <0.5 meV/atom. For 1 ML Co we find a substantial decrease in the L/S ratio to 0.19. However, the L/S ratio for 1 ML Fe on both substrates does not change much compared with the Fe single atom.

  15. Magnetoelectric coupling characteristics in multiferroic heterostructures with different thickness of nanocrystalline soft magnetic alloy

    Science.gov (United States)

    Chen, Lei; Wang, Yao

    2016-05-01

    Magnetoelectric(ME) coupling characteristics in multiferroic heterostructures with different thickness of nanocrystalline soft magnetic alloy has been investigated at low frequency. The ME response with obvious hysteresis, self-biased and dual-peak phenomenon is observed for multiferroic heterostructures, which results from strong magnetic interactions between two ferromagnetic materials with different magnetic properties, magnetostrictions and optimum bias magnetic fields Hdc,opti. The proposed multiferroic heterostructures not only enhance ME coupling significantly, but also broaden dc magnetic bias operating range and overcomes the limitations of narrow bias range. By optimizing the thickness of nanocrystalline soft magnetic alloy Tf, a significantly zero-biased ME voltage coefficient(MEVC) of 14.8mV/Oe (185 mV/cmṡ Oe) at Tf = 0.09 mm can be obtained, which is about 10.8 times as large as that of traditional PZT/Terfenol-D composite with a weak ME coupling at zero bias Hdc,zero. Furthermore, when Tf increases from 0.03 mm to 0.18 mm, the maximum MEVC increases nearly linearly with the increased Tf at Hdc,opti. Additionally, the experimental results demonstrate the ME response for multiferroic heterostructures spreads over a wide magnetic dc bias operating range. The excellent ME performance provides a promising and practicable application for both highly sensitive magnetic field sensors without bias and ME energy harvesters.

  16. Electron paramagnetic resonance studies of defects in dilute magnetic alloys

    International Nuclear Information System (INIS)

    Suss, J.T.; Raizman, A.

    1980-01-01

    The EPR spectrum of erbium was used to study the effects of cold-working (rolling and mechanical polishing) in dilute gold-erbium alloys. Variation in the EPR linewidth, intensity and asymmetry parameter (A/B ratio) were investigated. Most of the results could be interpreted in terms of segregation of erbium ions to subgrain boundaries (dislocations) in a surface layer of a few thousand Angstroms. (author)

  17. Change of magnetic properties of nanocrystalline alloys under influence of external factors

    Science.gov (United States)

    Sitek, Jozef; Holková, Dominika; Dekan, Julius; Novák, Patrik

    2016-10-01

    Nanocrystalline (Fe3Ni1)81Nb7B12 alloys were irradiated using different types of radiation and subsequently studied by Mössbauer spectroscopy. External magnetic field of 0.5 T, electron-beam irradiation up to 4 MGy, neutron irradiation up to 1017 neutrons/cm2 and irradiation with Cu ions were applied on the samples. All types of external factors had an influence on the magnetic microstructure manifested as a change in the direction of the net magnetic moment, intensity of the internal magnetic field and volumetric fraction of the constituent phases. The direction of the net magnetic moment was the most sensitive parameter. Changes of the microscopic magnetic parameters were compared after different external influence and results of nanocrystalline samples were compared with their amorphous precursors.

  18. Magnetic hysteresis properties of melt-spun Nd-Fe-B alloys prepared by centrifugal method

    International Nuclear Information System (INIS)

    Andreev, S.V.; Kudrevatykh, N.V.; Pushkarsky, V.I.; Markin, P.E.; Zaikov, N.K.; Tarasov, E.N.

    1998-01-01

    Magnetic hysteresis properties and microstructure peculiarities of melt spun Nd-Fe-B alloys (ribbons) prepared by melt quenching onto the internal surface of an iron spinning wheel at tangential speeds in the range 5-20 m/s are reported. The alloy composition was Nd-36% wt, B-1.2% wt. and Fe-remainder. It was found that the coercivity of ribbons does not practically depend on the wheel speed in applied range (18 kOe at 5 m/s and 22 kOe at 20 m/s), whereas the grain size of the basic phase (2-14-1) ste[ily decreases when the speed rises, starting from 2-3 μm for 5 m/s alloy down to the 200-300 nm for 20 m/s alloy. All ribbons have normal convex demagnetization curves, even those prepared at low wheel speeds (without peculiar step near H∝0, which usually exists on such curves for tr[itionally prepared underquenched melt-spun Nd-Fe-B alloys). Grinding the ribbon in a vibration mill causes the coercivity drop to 7 kOe after 120 min of treatment. However, this operation increases the powder alignment ability and, as a result, the energy product for a fully dense magnet from anisotropic powder prepared from some ribbons rises to 20-23 MGOe. (orig.)

  19. Magnetic properties of centrifugally prepared melt-spun Nd-Fe-B alloys and their powders

    International Nuclear Information System (INIS)

    Andreev, S.V.; Kudrevatykh, N.V.; Kozlov, A.I.; Markin, P.E.; Pushkarskiy, V.I.

    1998-01-01

    Magnetic hysteresis properties and microstructure peculiarities of melt spun Nd-Fe-B alloys (ribbons) prepared by melt quenching on to the internal surface of an iron spinning wheel at the tangential speeds in the range 5-20 m/sec are reported. The alloy composition was Nd-36% wt. B-1.2% wt. and Fe-reminder. It was found that the coercivity of ribbons does not practically depend on the wheel speed in the applied range (1430 kA/m at 5 m/sec and 1750 kA/m at 20 m/sec), whereas the grain size of the basic phase (2-14-1) steadily decreases when the speed rises, starting from 2-3 μm for 5 m sec alloy down to the 200-300 nm for 20 m/sec alloy. All ribbons have normal convex demagnetization curves, even those prepared at low wheel speeds (without peculiar step near H∝0, which usually exists on such curves for traditionally prepared underquenched melt-spun Nd-Fe-B alloys). Grinding the ribbons subjected to hydrogen and annealing treatments causes the coercivity drop. However, this operations increase the powder alignment ability and, as a result, the energy product for fully dense magnet from such powder rises to 160-180 kJ/m 3 . (orig.)

  20. Magnetic susceptibilities of liquid Cr-Au, Mn-Au and Fe-Au alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ohno, S.; Shimakura, H. [Niigata University of Pharmacy and Applied Life Sciences, Higashijima, Akiha-ku, Niigata 956-8603 (Japan); Tahara, S. [Faculty of Science, University of the Ryukyus, Nishihara-cho, Okinawa 903-0213 (Japan); Okada, T. [Niigata College of Technology, Kamishin’eicho, Nishi-ku, Niigata 950-2076 (Japan)

    2015-08-17

    The magnetic susceptibility of liquid Cr-Au, Mn-Au, Fe-Au and Cu-Au alloys was investigated as a function of temperature and composition. Liquid Cr{sub 1-c}Au{sub c} with 0.5 ≤ c and Mn{sub 1-c}Au{sub c} with 0.3≤c obeyed the Curie-Weiss law with regard to their dependence of χ on temperature. The magnetic susceptibilities of liquid Fe-Au alloys also exhibited Curie-Weiss behavior with a reasonable value for the effective number of Bohr magneton. On the Au-rich side, the composition dependence of χ for liquid TM-Au (TM=Cr, Mn, Fe) alloys increased rapidly with increasing TM content, respectively. Additionally, the composition dependences of χ for liquid Cr-Au, Mn-Au, and Fe-Au alloys had maxima at compositions of 50 at% Cr, 70 at% Mn, and 85 at% Fe, respectively. We compared the composition dependences of χ{sub 3d} due to 3d electrons for liquid binary TM-M (M=Au, Al, Si, Sb), and investigated the relationship between χ{sub 3d} and E{sub F} in liquid binary TM-M alloys at a composition of 50 at% TM.

  1. Magnetic Properties Studies on Thermal Aged Fe-Cu Alloys for the Simulation of Radiation Damage

    Energy Technology Data Exchange (ETDEWEB)

    Lee, C. K.; Kishore, M.B.; Park, D. G. [KAERI, Daejeon (Korea, Republic of); Son, De Rac. [Hannam University, Daejeon (Korea, Republic of)

    2016-05-15

    We evaluated the changes in magnetic properties due to cold rolling and thermal ageing of a Fe-1%Cu model alloy in this study. Initially, the alloy was 10% cold rolled, and isothermally aged at 400 .deg. C for 1, 10, 100 and 1000 hr. The samples were prepared at various thermal aging conditions and all the conditions were interpreted. The hysteresis loops, Magnetic Barkhausen noise (BN). The change of magnetic properties can be interpreted in terms of the domain wall motion and dislocation dynamics associated with copper rich precipitates (CRPs).The results were interpreted in terms of ageing time dependence of the precipitates evolution such as the volume fraction and size distribution. In order to evaluate the radiation embrittlement of RPV steel, A Cold rolled Fe-Cu model Alloy was prepared, The prepared samples were thermally aged by annealing at 400 .deg. C for various times, the magnetic properties of the annealed samples were measured, The Barkhausen noise and BH Loop shows a considerable trend corresponding to the Ageing time. The magnetic properties were interpreted and correlated to the CRPs formed through annealing process.

  2. Magnetic properties of point defect interaction with impurity atoms in Fe-Cr alloys

    Science.gov (United States)

    Nguyen-Manh, D.; Lavrentiev, M. Yu.; Dudarev, S. L.

    2009-04-01

    An integrated ab initio and statistical Monte Carlo investigation has been recently carried out to model the thermodynamic and kinetic properties of Fe-Cr alloys. We found that the conventional Fe-Cr phase diagram is not adequate at low temperature region where the magnetic contribution to the free energy plays an important role in the prediction of an ordered Fe 15Cr phase and its negative enthalpy of formation. The origin of the anomalous thermodynamic and magnetic properties of Fe-Cr alloys can be understood using a tight-binding Stoner model combined with the charge neutrality condition. We investigate the environmental dependence of magnetic moment distributions for various self-interstitial atom dumbbells configurations using spin density maps found using density functional theory calculations. The mixed dumbbell Fe-Cr and Fe-Mn binding energies are found to be positive due to magnetic interactions. Finally, we discuss the relationship between the migration energy of vacancy in Fe-Cr alloys and magnetism at the saddle point configuration.

  3. The influence of Cr content in Fe-Cr-Co alloys on the magnetic properties and Moessbauer effect

    International Nuclear Information System (INIS)

    Yan Yong; Sho Hanru; Li Dexin; Li Guodong; Li Dongshen; Zhen Jinshan

    1986-01-01

    Fe-xCr-8Co (x=24, 25, 27, 29 and 32 wt%) permanent magnetic alloys have been studied by Moessbauer effect, magnetic balance and vibrating-sample magnetometer. It is indicated that the optimum permanent magnetic properties obtained for the composition of the alloys at about x=27. The value of Cr content in these alloys sigificantly influences the average hyperfine field, the saturation magnetic moment, the proportion of paramagnetic phase and orientation of magnetic moment in these alloys. The intrinsic coercive force is gradually reduced with the temperature decreasing from 290 to 77 K. The paramagnetic peak in the spectrum disappears at about 125 K. The certain mechanism has been suggested to explain the experimental results. (Auth.)

  4. Metal Amorphous Nanocomposite (MANC) Alloy Cores with Spatially Tuned Permeability for Advanced Power Magnetics Applications

    Science.gov (United States)

    Byerly, K.; Ohodnicki, P. R.; Moon, S. R.; Leary, A. M.; Keylin, V.; McHenry, M. E.; Simizu, S.; Beddingfield, R.; Yu, Y.; Feichter, G.; Noebe, R.; Bowman, R.; Bhattacharya, S.

    2018-06-01

    Metal amorphous nanocomposite (MANC) alloys are an emerging class of soft magnetic materials showing promise for a range of inductive components targeted for higher power density and higher efficiency power conversion applications including inductors, transformers, and rotating electrical machinery. Magnetization reversal mechanisms within these alloys are typically determined by composition optimization as well as controlled annealing treatments to generate a nanocomposite structure composed of nanocrystals embedded in an amorphous precursor. Here we demonstrate the concept of spatially varying the permeability within a given component for optimization of performance by using the strain annealing process. The concept is realized experimentally through the smoothing of the flux profile from the inner to outer core radius achieved by a monotonic variation in tension during the strain annealing process. Great potential exists for an extension of this concept to a wide range of other power magnetic components and more complex spatially varying permeability profiles through advances in strain annealing techniques and controls.

  5. Macroscopic and microscopic magnetism of metal-metalloid amorphous alloys

    International Nuclear Information System (INIS)

    Vasconcellos, M.A.Z.; Fichtner, P.F.P.; Livi, F.P.; Costa, M.I. da; Baibich, M.N.

    1984-01-01

    In this paper is investigated the interrelation between macroscopic and microscopic magnetic phenomena using experimetnal data from Moessbauer effect and the magnetization of layers of amorphous (Fe 1-x Ni x ) 80 B 20 . The Moessbauer effect measurement show a distribution of hyperfine fields in Fe site as well as a likely distribution of isomeric shifts (M.W.O.) [pt

  6. Magnetic properties of Co-Ni alloy nanoparticles prepared by the sol-gel technique

    International Nuclear Information System (INIS)

    Sangregorio, C.; Fernandez, C. de Julian; Battaglin, G.; De, G.; Gatteschi, D.; Mattei, G.; Mazzoldi, P.

    2004-01-01

    The magnetic properties of Co, Ni and Co x Ni 1-x alloy nanoparticles with different composition (0 < x < 1), prepared by the sol-gel route, were investigated. ZFC and FC magnetization measurements show that the blocking temperature increases with the Co content, while a maximum in the anisotropy constant was found for x=0.7. Room temperature FMR measurements, suggest that in samples with larger Co content (x≥0.66) interparticle interactions play a relevant role in determining their magnetic properties

  7. Magnetic properties of Co-Ni alloy nanoparticles prepared by the sol-gel technique

    Energy Technology Data Exchange (ETDEWEB)

    Sangregorio, C. E-mail: claudio.sangregorio@unifi.it; Fernandez, C. de Julian; Battaglin, G.; De, G.; Gatteschi, D.; Mattei, G.; Mazzoldi, P

    2004-05-01

    The magnetic properties of Co, Ni and Co{sub x}Ni{sub 1-x} alloy nanoparticles with different composition (0 < x < 1), prepared by the sol-gel route, were investigated. ZFC and FC magnetization measurements show that the blocking temperature increases with the Co content, while a maximum in the anisotropy constant was found for x=0.7. Room temperature FMR measurements, suggest that in samples with larger Co content (x{>=}0.66) interparticle interactions play a relevant role in determining their magnetic properties.

  8. Magnetic and Moessbauer studies of amorphous Fe72-xYxHo8B20 alloys

    International Nuclear Information System (INIS)

    Krishnan, R.; Dumond, Y.; Ajan, A.; Shringi, S.N.; Prasad, S.

    1996-01-01

    We have carried out magnetic and Moessbauer studies of amorphous Fe 72-x Y x Ho 8 B 20 alloys. The Fe moment decreases with the addition of Y and a magnetic compensation occurs at 4 K for x=16. The temperature and field dependences of the magnetization have been interpreted using the mean field theory and Chudnovsky's model, respectively. These analyses yield some interesting parameters such as the random anisotropy, the exchange interactions J Fe-Fe , J Fe-Ho , etc. The Moessbauer studies show that the average hyperfine field decreases linearly with the addition of Y, in accordance with the decrease in the Fe moment. (orig.)

  9. Selective tuning of magnetization dynamics damping in Tb- and Nd-doped permalloy ultrathin films by adjacent copper nanolayers

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Dong, E-mail: physzd@yahoo.com [School of Physics Science and Information Engineering, Key Lab. of Communication Science and Technology of Shandong Province, Liaocheng University, Liaocheng 252059 (China); Physics Department, Southeast University, Nanjing 211189 (China); Yue, Jinjin; Jiang, Sheng [Physics Department, Southeast University, Nanjing 211189 (China); Zhai, Ya, E-mail: yazhai@seu.edu.cn [Physics Department, Southeast University, Nanjing 211189 (China); National Laboratory of Solid Microstructures, Nanjing University, Nanjing 210093 (China); Du, Jun; Zhai, Hongru [National Laboratory of Solid Microstructures, Nanjing University, Nanjing 210093 (China)

    2016-07-05

    The mechanism of angular dependence of ferromagnetic resonance linewidth of dilute Tb and Nd doping in permalloy thin films with various thicknesses of adjacent copper layer are investigated by experimental approach and theoretical fitting by considering the contributions from intrinsic spin-orbit coupling, inhomogeneous broadening and two-magnon scattering. The results show that the damping coefficient α, by intrinsic contribution extracted from ferromagnetic resonance linewidth, increases from 0.0153 to 0.0218 for NiFe–Nd films and from 0.0193 to 0.0261 for NiFe–Tb films resulting from the spin pumping effect at the interface of NiFe–Nd(or Tb)/Cu as the thickness of copper layer increases from 1 nm to 15 nm. The surface magnetic anisotropy constant K{sub 1} is obtained and shows an decreasing trend from positive to negative, which implies that the copper layer could reduce the surface perpendicular anisotropy. The fitting spin mixed conductivity is (2.72 ± 0.18) × 10{sup 15} cm{sup −2} at NiFe–Tb/Cu interface and (2.4 ± 0.2) × 10{sup 15} cm{sup −2} at Cu/NiFe–Nd interface, respectively. - Highlights: • The thickness of Cu buffer layer affects the surface perpendicular anisotropy of FM layer. • The interface roughness could be investigated by using FMR linewidth. • The damping coefficient is enhanced by spin-pumping effect.

  10. Designing magnetic compensated states in tetragonal Mn{sub 3}Ge-based Heusler alloys

    Energy Technology Data Exchange (ETDEWEB)

    You, Yurong; Xu, Guizhou, E-mail: gzxu@njust.edu.cn; Hu, Fang; Gong, Yuanyuan; Liu, Er; Peng, Guo; Xu, Feng, E-mail: xufeng@njust.edu.cn

    2017-05-01

    Magnetic compensated materials attracted much interests due to the observed large exchange bias and large coercivity, and also their potential applications in the antiferromagnetic spintronics with merit of no stray field. In this work, by using ab-initio studies, we designed several Ni (Pd, Pt) doped Mn{sub 3}Ge-based D0{sub 22}-type tetragonal Heusler alloys with fully compensated states. Theoretically, we find the total moment change is asymmetric across the compensation point (at ~x=0.3) in Mn{sub 3-x}Y{sub x}Ge (Y=Ni, Pd, Pt). In addition, an uncommon discontinuous jump is observed across the critical zero-moment point, indicating that some non-trivial properties may emerge at this point. Further electronic analyses of these compensated alloys reveal high spin polarizations at the Fermi level, which is advantageous for spin transfer torque applications. - Highlights: • Several new fully compensated magnetic states are identified in Mn{sub 3}Ge-based tetragonal alloys. • The magnetic moment changes are asymmetric upon Ni, Pd and Pt substitution. • Discontinuous jumps exist across the compensated points. • The three compensated alloys possess large spin polarizations.

  11. Study of magnetism in Ni–Cr hardface alloy deposit on 316LN stainless steel using magnetic force microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Kishore, G.V.K.; Kumar, Anish, E-mail: anish@igcar.gov.in; Chakraborty, Gopa; Albert, S.K; Rao, B. Purna Chandra; Bhaduri, A.K.; Jayakumar, T.

    2015-07-01

    Nickel base Ni–Cr alloy variants are extensively used for hardfacing of austenitic stainless steel components in sodium cooled fast reactors (SFRs) to avoid self-welding and galling. Considerable difference in the compositions and melting points of the substrate and the Ni–Cr alloy results in significant dilution of the hardface deposit from the substrate. Even though, both the deposit and the substrate are non-magnetic, the diluted region exhibits ferromagnetic behavior. The present paper reports a systematic study carried out on the variations in microstructures and magnetic behavior of American Welding Society (AWS) Ni Cr–C deposited layers on 316 LN austenitic stainless steels, using atomic force microscopy (AFM) and magnetic force microscopy (MFM). The phase variations of the oscillations of a Co–Cr alloy coated magnetic field sensitive cantilever is used to quantitatively study the magnetic strength of the evolved microstructure in the diluted region as a function of the distance from the deposit/substrate interface, with the spatial resolution of about 100 nm. The acquired AFM/MFM images and the magnetic property profiles have been correlated with the variations in the chemical compositions in the diluted layers obtained by the energy dispersive spectroscopy (EDS). The study indicates that both the volume fraction of the ferromagnetic phase and its ferromagnetic strength decrease with increasing distance from the deposit/substrate interface. A distinct difference is observed in the ferromagnetic strength in the first few layers and the ferromagnetism is observed only near to the precipitates in the fifth layer. The study provides a better insight of the evolution of ferromagnetism in the diluted layers of Ni–Cr alloy deposits on stainless steel. - Highlights: • Study of evolution of ferromagnetism in Comonoy-6 deposit on austenitic steel. • Magnetic force microscopy (MFM) exhibited ferromagnetic matrix in first two layers. • The maximum MFM

  12. Moessbauer effect studies of magnetic interactions in iron and dilute iron alloys

    International Nuclear Information System (INIS)

    Woude, F. van der; Schurer, P.J.; Sawatzky, G.A.

    1975-01-01

    A temperature-dependent Moessbauer study was conducted in FeX alloys, where X = Al, Si, Ti, V, Cr, Mn, Co, and Ni, aimed at solving the problem of 'what is localized and what is itinerant in iron ferromagnetism'. The experimental results are interpreted using a phenomenological model based on a modified Zener-Vonsovskij theory. Absorption spectra of FeX alloys were measured as a function of temperature. It was found that the 3d magnetic moments in iron were mainly localized while exchange coupling was provided by partly itinerant 3d electrons. (L.D.)

  13. Magnetic properties of CoP alloys electrodeposited at room temperature

    International Nuclear Information System (INIS)

    Lucas, I.; Perez, L.; Aroca, C.; Sanchez, P.; Lopez, E.; Sanchez, M.C.

    2005-01-01

    CoP alloys have been electrodeposited at room temperature from electrolytes with different pH values and their magnetic properties have been studied. Cracks and fractures appear when using stiff substrates, showing that high internal stresses, due to hydrogen evolution, are involved in the electrodeposition process. Samples electrodeposited onto flexible substrates do not show cracks on the surface. We also report an increment in the coercivity of the alloys when the pH of the electrolyte decreases, and therefore, the hydrogen evolution and the internal stresses increase

  14. Large roomtemperature magnetocaloric effect with negligible magnetic hysteresis losses in Mn1-xVxCoGe alloys

    International Nuclear Information System (INIS)

    Ma, S.C.; Zheng, Y.X.; Xuan, H.C.; Shen, L.J.; Cao, Q.Q.; Wang, D.H.; Zhong, Z.C.; Du, Y.W.

    2012-01-01

    The magnetic and magnetocaloric properties have been investigated in a series of Mn 1-x V x CoGe (x=0.01, 0.02, 0.03, and 0.05) alloys. The substitution of V for Mn reduces the structural transformation temperature of MnCoGe alloy effectively and results in a second-order magnetic transition in Mn 0.95 V 0.05 CoGe alloys. Large room temperature magnetocaloric effect and almost zero magnetic hysteresis losses are simultaneously achieved in the alloys with x=0.01, 0.02, and 0.03. The reasons for the negligible magnetic hysteresis losses and the potential application for the roomtemperature magnetic refrigeration are discussed. - Highlights: → V-substitution for Mn reduces the structural transformation temperature of MnCoGe. → FM-PM transition presents the second-order nature in Mn0.95V0.05CoGe. → The first-order FM-PM transitions are observed for alloys with x=0.01, 0.02, and 0.03. → Large room temperature MCEs are achieved in these alloys. → Negligible magnetic HL is achieved for these alloys simultaneously.

  15. Thermal, magnetic, and structural properties of soft magnetic FeCrNbCuSiB alloy ribbons

    International Nuclear Information System (INIS)

    Rosales-Rivera, A.; Valencia, V.H.; Quintero, D.L.; Pineda-Gomez, P.; Gomez, M.

    2006-01-01

    The thermal, magnetic and structural properties of amorphous magnetic Fe 73.5-x Cr x Nb 3 Cu 1 Si 13.5 B 9 alloy ribbons, with x=0, 2, 4, 6, 8, and 10, were studied by using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), magneto-impedance measurements and X-ray diffraction (XRD). The ribbons exhibit ultrasoft magnetic behavior, especially giant magneto-impedance effect, GMI. A three-peak behavior was observed in GMI curves. Particular attention has been given to observation of crystallization kinetics via DSC and TGA. The primary crystallization T pcr , and Curie T c , temperatures were determined from DSC and TGA data, respectively. The effect of partial substitution of iron by Cr on the thermal and magnetic properties is discussed

  16. Moessbauer and magnetic investigation of Fe-Mn alloy

    International Nuclear Information System (INIS)

    Yousif, A.A.

    1994-01-01

    Moessbauer, X-ray, magnetization and susceptibility measurements were performed to study Fe 100-x Mn x , x = 5, 15, 39, 50. The different phases of Fe-Mn were identified, and hyperfine interaction parameters and average magnetic moments of some samples were determined. The average hyperfine field and average magnetic moment decrease as x increases. The influence of the Mn neighbourhood on the derived parameters is discussed in the light of calculations using the first principle discrete variational method in the local density approximation. (orig.)

  17. Effect of alloying on the electronic structure and magnetic properties ...

    Indian Academy of Sciences (India)

    Unknown

    We analyse the effect of local environment and the hybridization between the constituent bands on the elec- tronic and magnetic ..... statements made earlier that although the augmented .... ics, Trieste, for the financial help through its Network.

  18. Activation of structural alloys in fusion reactor magnets

    International Nuclear Information System (INIS)

    Mann, F.M.; Doran, D.G.

    1986-01-01

    Using the REAC2 code system, both short-term and long-term activation were calculated for possible structural and magnet materials at the shield-magnet interface. The flux was taken from the STARFIRE conceptual design and a 30-year lifetime was assumed. Short-term activation does not seem to be a problem. Only materials with large amounts of niobium appear to be a potential problem for long-term activation. 2 tabs

  19. Creep deformation of a soft magnetic iron-cobalt alloy

    OpenAIRE

    Fingers, Richard T.; Coate, Jack E.; Dowling, Norman E.

    1999-01-01

    The U.S. Air Force is in the process of developing magnetic bearings, as well as an aircraft integrated power unit and an internal starter/generator for main propulsion engines. These developments are the driving force for the new emphasis on the development of high saturation, low loss magnets capable of maintaining structural integrity in high stress and high temperature environments. It is this combination of desired material characteristics that is the motivation of this effort to measure...

  20. Structural and magnetic properties of Fe{sub 60}Al{sub 40} alloys prepared by means of a magnetic mill

    Energy Technology Data Exchange (ETDEWEB)

    Bernal-Correa, R. [Laboratorio de Magnetismo y Materiales Avanzados, Facultad de Ciencias Exactas y Naturales, Universidad Nacional de Colombia, Manizales (Colombia); Rosales-Rivera, A., E-mail: arosalesr@unal.edu.c [Laboratorio de Magnetismo y Materiales Avanzados, Facultad de Ciencias Exactas y Naturales, Universidad Nacional de Colombia, Manizales (Colombia); Pineda-Gomez, P. [Laboratorio de Magnetismo y Materiales Avanzados, Facultad de Ciencias Exactas y Naturales, Universidad Nacional de Colombia, Manizales (Colombia); Universidad de Caldas, Manizales (Colombia); Salazar, N.A. [Laboratorio de Magnetismo y Materiales Avanzados, Facultad de Ciencias Exactas y Naturales, Universidad Nacional de Colombia, Manizales (Colombia)

    2010-04-16

    A study on synthesis, structural and magnetic characterization of Fe{sub 60}Al{sub 40} (at.%) alloys prepared by means of mechanical alloying process is presented. The mechanical alloying was performed using a milling device with magnetically controlled ball movement (Uni-Ball-Mill 5 equipment) at several milling times. The characterization was carried out via X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). The effects of milling time on the structural state, morphological evolution and magnetic behaviour of the Fe{sub 60}Al{sub 40} (at.%) alloys are discussed. Besides, in this current study we emphasize the result that indicating a ferro-para-ferromagnetic transition from a correlation between X-ray diffraction and magnetization data.

  1. Ultra-soft magnetic Co-Fe-B-Si-Nb amorphous alloys for high frequency power applications

    Science.gov (United States)

    Ackland, Karl; Masood, Ansar; Kulkarni, Santosh; Stamenov, Plamen

    2018-05-01

    With the continuous shrinkage of the footprint of inductors and transformers in modern power supplies, higher flux, while still low-loss metallic replacements of traditional ferrite materials are becoming an intriguing alternative. One candidate replacement strategy is based on amorphous CoFeBSi soft-magnetic alloys, in their metallic glass form. Here the structural and magnetic properties of two different families of CoFeBSi-based soft magnetic alloys, prepared by arc-melting and subsequent melt spinning (rapid quenching) are presented, targeting potential applications at effective frequencies of 100 kHz and beyond. The nominal alloy compositions are Co67Fe4B11Si16Mo2 representing commercial Vitrovac and Co72-xFexB28-y (where B includes non-magnetic elements such as Boron, Silicon etc. x varies between 4 and 5 % and y is varied from 0 to 2 %) denoted Alloy #1 and prepared as a possible higher performance alternative, i.e. lower power loss and lower coercivity, to commercial Vitrovac. Room temperature magnetization measurements of the arc-melted alloys reveal that compared to Vitrovac, Alloy #1 already presents a ten-fold decrease in coercivity, with Hc ˜ 1.4 Am-1 and highest figure of merit of (Ms/Hc > 96). Upon melt-spinning the alloys into thin (< 30 μm) ribbons, the alloys are essentially amorphous when analyzed by XRD. Magnetization measurements of the melt-spun ribbons demonstrate that Alloy #1 possesses a coercivity of just 2 Am-1, which represents a significant improvement compared to melt-spun ribbons of Vitrovac (17 Am-1). A set of prototype transformers of approximately 10 turns of Alloy #1 ribbon exhibits systematically Hc < 10 Am-1 at 100 kHz, without a noticeable decrease in coupled flux and saturation.

  2. Magnetic cluster mean-field description of spin glasses in amorphous La-Gd-Au alloys

    International Nuclear Information System (INIS)

    Poon, S.J.; Durand, J.

    1978-03-01

    Bulk magnetic properties of splat-cooled amorphous alloys of composition La/sub 80-x/Gd/sub x/Au 20 (0 less than or equal to x less than or equal to 80) were studied. Zero-field susceptibility, high-field magnetization (up to 75 kOe) and saturated remanence were measured between 1.8 and 290 0 K. Data were analyzed using a cluster mean-field approximation for the spin-glass and mictomagnetic alloys (x less than or equal to 56). Mean-field theories can account for the experimental freezing-temperatures of dilute spin-glasses in which the Ruderman-Kittel-Kasuya-Yosida interaction is dominant. For the dilute alloys, the role of amorphousness on the magnetic interactions is discussed. By extending the mean-field approximation, the concentrated spin-glasses are represented by rigid ferromagnetic clusters as individual spin-entities interacting via random forces. Scaling laws for the magnetization M and saturation remanent magnetization M/sub rs/ are obtained and presented graphically for the x less than or equal to 32 alloys in which M/x = g(H/x*, T/x), M/sub rs/(T)/x = M/sub rs/(0)/x/ exp (-α*T/x/sup p/) where x* is the concentration of clusters, α* is a constant, and p is the freezing-temperature exponent given by T/sub M/ infinity x/sup p/. It is found that p = 1 and 1.3 for the regions 4 less than or equal to x less than or equal to 40 respectively. An attempt is also made to account for the freezing temperatures of concentrated spin glasses. The strength of the interaction among clusters is determined from high-field magnetization measurements using the Larkin-Smith method modified for clusters. It is shown that for the x < 24 alloys, the size of the clusters can be correlated to the structural short-range order in the amorphous state. More concentrated alloys are marked by the emergence of cluster percolation

  3. Field-induced non-collinear magnetic structures in amorphous Co80-xDy xB20 alloys

    International Nuclear Information System (INIS)

    Annouar, F.; Roky, K.; Lassri, H.; Elmoussaoui, A.; Driouch, L.; Ayadi, M.; Omri, M.; Krishnan, R.

    2005-01-01

    Amorphous Co 80-x Dy x B 20 alloys have been prepared by melt spinning technique and their magnetic properties have been studied. The mean field theory has been used to explain the temperature dependence of the magnetization. High-field magnetization studies performed at 4.2 K in magnetic fields up to 38 T have revealed, for samples with stoichiometry close to that of a compensated ferrimagnet, a magnetic behavior that is characteristic of a non-collinear magnetic structure of the Dy and Co sublattices. From the non-collinear regime the exchange interactions between the Co and Dy magnetic sublattices and the magnetic anisotropy constants have been evaluated

  4. Surface crystallization and magnetic properties of amorphous Fe80B20 alloy

    International Nuclear Information System (INIS)

    Vavassori, P.; Ronconi, F.; Puppin, E.

    1997-01-01

    We have studied the effects of surface crystallization on the magnetic properties of Fe 80 B 20 amorphous alloys. The surface magnetic properties have been studied with magneto-optic Kerr measurements, while those of bulk with a vibrating sample magnetometer. This study reveals that surface crystallization is similar to the bulk process but occurs at a lower temperature. At variance with previous results on other iron-based amorphous alloys the surface crystalline layer does not induce bulk magnetic hardening. Furthermore, both the remanence to saturation ratio and the bulk magnetic anisotropy do not show appreciable variations after the formation of the surface crystalline layer. The Curie temperature of the surface layer is lower with respect to the bulk of the sample. These effects can be explained by a lower boron concentration in the surface region of the as-cast amorphous alloy. Measurements of the chemical composition confirm a reduction of boron concentration in the surface region. copyright 1997 American Institute of Physics

  5. Fabrication and magnetic investigations of highly uniform CoNiGa alloy nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Li, Wen-Jing; Khan, U.; Irfan, Muhammad [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, University of Chinese Academy of Sciences, Chinese Academy of Sciences, Beijing 100190 (China); Javed, K. [Department of Physics, Forman Christian College, Lahore 5400 (Pakistan); Liu, P. [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, University of Chinese Academy of Sciences, Chinese Academy of Sciences, Beijing 100190 (China); School of Physical Science and Technology, Inner Mongolia University, Hohhot 010021 (China); Ban, S.L. [School of Physical Science and Technology, Inner Mongolia University, Hohhot 010021 (China); Han, X.F., E-mail: xfhan@iphy.ac.cn [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, University of Chinese Academy of Sciences, Chinese Academy of Sciences, Beijing 100190 (China)

    2017-06-15

    Highlights: • Highly ordered CoNiGa alloy nanowires with different compositions were fabricated by DC electrodeposition. • The magnetic properties of CoNiGa nanowires can be easily tailored by varying its components. • Magnetostatic interactions plays an important role in the magnetization reversal process. • A linear dependence of coercivity on temperature was found for Co{sub 55}Ni{sub 28}Ga{sub 17} samples. - Abstract: CoNiGa ternary alloy nanowire arrays were successfully fabricated by simple DC electrodeposition into the anodized aluminum oxide (AAO) templates. A systematic study of the potential and components of the electrolyte were conducted to obtain different components of CoNiGa nanowires. The largest Ga content in the prepared alloy nanowires was about 17%, while for Co and Ni contents which can be controlled in a wide range by adjusting the composition and pH value of the electrolyte appropriately. X-ray diffraction analysis confirmed that the as-grown CoNiGa nanowire arrays were polycrystal with fcc phase of Co where Co atoms partially substituted by Ni and Ga. Magnetization curves of samples with different composition were measured at room temperature as well as low temperature. The results showed that the components of the alloy nanowires have a great impact on its magnetic properties. For Co{sub 55}Ni{sub 28}Ga{sub 17} nanowires, the magnetization reversal mode changes from curling mode to coherent rotation as the angle increases, and the temperature dependence of coercivity can be well described by the thermal activation effect.

  6. Structural order and magnetism of rare-earth metallic amorphous alloys

    International Nuclear Information System (INIS)

    Maurer, M.

    1984-01-01

    Local symmetry (as evaluated from the electric field gradient tensor) and radial distribution functions (obtained by EXAFS measurement) are determined in a series of amorphous rare-earth base alloys. Local order is found to increase with the extent of heteroatomic interactions. Various magnetic phases (including ferromagnetic, spin-glass, reentrant spin-glass) occur for europium alloys with simple metals (Mg, Zn, Cd, Al, Au, ...). This variety reflects the sensitivity of exchange interactions to the presence of non-s conduction electrons. Asperomagnetic structures are established for the Dy alloys. The crystalline electric field interactions at the Dy 3+ ions are interpreted with the help of local symmetry data. Quadratic axial and non-axial crystal field terms are sufficient and necessary in order to account for the hyperfine and bulk experimental results [fr

  7. Microstructure, soft magnetic properties and applications of amorphous Fe-Co-Si-B-Mo-P alloy

    Science.gov (United States)

    Hasiak, Mariusz; Miglierini, Marcel; Łukiewski, Mirosław; Łaszcz, Amadeusz; Bujdoš, Marek

    2018-05-01

    DC thermomagnetic properties of Fe51Co12Si16B8Mo5P8 amorphous alloy in the as-quenched and after annealing below crystallization temperature are investigated. They are related to deviations in the microstructure as revealed by Mössbauer spectrometry. Study of AC magnetic properties, i.e. hysteresis loops, relative permeability and core losses versus maximum induction was aimed at obtaining optimal initial parameters for simulation process of a resonant transformer for a rail power supply converter. The results obtained from numerical analyses including core losses, winding losses, core mass, and dimensions were compared with the same parameters calculated for Fe-Si alloy and ferrite. Moreover, Steinmetz coefficients were also calculated for the as-quenched Fe51Co12Si16B8Mo5P8 amorphous alloy.

  8. Microstructure, soft magnetic properties and applications of amorphous Fe-Co-Si-B-Mo-P alloy

    Directory of Open Access Journals (Sweden)

    Mariusz Hasiak

    2018-05-01

    Full Text Available DC thermomagnetic properties of Fe51Co12Si16B8Mo5P8 amorphous alloy in the as-quenched and after annealing below crystallization temperature are investigated. They are related to deviations in the microstructure as revealed by Mössbauer spectrometry. Study of AC magnetic properties, i.e. hysteresis loops, relative permeability and core losses versus maximum induction was aimed at obtaining optimal initial parameters for simulation process of a resonant transformer for a rail power supply converter. The results obtained from numerical analyses including core losses, winding losses, core mass, and dimensions were compared with the same parameters calculated for Fe-Si alloy and ferrite. Moreover, Steinmetz coefficients were also calculated for the as-quenched Fe51Co12Si16B8Mo5P8 amorphous alloy.

  9. Magnetic and calorimetric investigations of ferromagnetic shape memory alloy Ni54Fe19Ga27

    International Nuclear Information System (INIS)

    Sharma, V K; Chattopadhyay, M K; Kumar, Ravi; Ganguli, Tapas; Kaul, Rakesh; Majumdar, S; Roy, S B

    2007-01-01

    We report results of magnetization and differential scanning calorimetry measurements in the ferromagnetic shape memory alloy Ni 54 Fe 19 Ga 27 . This alloy undergoes an austenite-martensite phase transition in its ferromagnetic state. The nature of the ferromagnetic state, both in the austenite and the martensite phase, is studied in detail. The ferromagnetic state in the martensite phase is found to have higher anisotropy energy as compared with the austenite phase. The estimated anisotropy constant is comparable to that of a well-studied ferromagnetic shape memory alloy system NiMnGa. Further, the present study highlights various interesting features accompanying the martensitic transition (MT). These features suggest the possibility of either a premartensitic transition and/or an inter-MT in this system

  10. Magnetic anisotropy induced by crystallographic orientation and morphological alignment in directionally-solidified eutectic Mn-Sb alloy

    Energy Technology Data Exchange (ETDEWEB)

    Lou, Chang-Sheng [School of Materials Science and Engineering, Shenyang Ligong University, Shenyang 110159 (China); Key Laboratory of Electromagnetic Processing of Materials (Ministry of Education), Northeastern University, Shenyang 110819 (China); Liu, Tie, E-mail: liutie@epm.neu.edu.cn [Key Laboratory of Electromagnetic Processing of Materials (Ministry of Education), Northeastern University, Shenyang 110819 (China); Dong, Meng; Wu, Chun; Shao, Jian-Guo; Wang, Qiang [Key Laboratory of Electromagnetic Processing of Materials (Ministry of Education), Northeastern University, Shenyang 110819 (China)

    2017-02-15

    The influences of the crystallographic orientation and morphological alignment upon the magnetic anisotropic behavior of polycrystalline materials were investigated. Microstructures obtained in eutectic Mn-Sb alloys via directional solidification simultaneously displayed crystallographic orientation and morphological alignment. Both the crystallographic orientation and the morphological alignment were able to induce magnetic anisotropy in the alloys, wherein the influence of the crystallographic orientation and the morphological alignment upon the magnetic anisotropic behavior of the alloys strongly depended upon their directions and exhibited either mutual promotion or competition. These findings may provide useful guidance for the fabrication design of functional magnetic materials. - Highlights: • We study effects of orientation in crystal and morphology on magnetic anisotropy. • Both orientation in crystal and morphology can induce magnetic anisotropy. • Their effects depend on direction and exhibit either mutual promotion or competition.

  11. Development of a high gradient rf system using a nanocrystalline soft magnetic alloy

    Directory of Open Access Journals (Sweden)

    Chihiro Ohmori

    2013-11-01

    Full Text Available The future high intensity upgrade project of the J-PARC (Japan Proton Accelerator Research Complex MR (Main Ring includes developments of high gradient rf cavities and magnet power supplies for high repetition rate. The scenario describing the cavity replacements is reported. By the replacement plan, the total acceleration voltage will be almost doubled, while the number of rf stations remains the same. The key issue is the development of a high gradient rf system using high impedance magnetic alloy, FT3L. The FT3L is produced by the transverse magnetic field annealing although the present cavity for the J-PARC adopts the magnetic alloy, FT3M, which is annealed without magnetic field. After the test production using a large spectrometer magnet in 2011, a dedicated production system for the FT3L cores was assembled in 2012. This setup demonstrated that we can produce material with 2 times higher μ_{p}^{′}Qf product compared to the cores used for present cavities. In this summer, the production system was moved to the company from J-PARC and is used for mass production of 280 FT3L cores for the J-PARC MR. The cores produced in the first test production are already used for standard machine operation. The operation experience shows that the power loss in the cores was reduced significantly as expected.

  12. Evaluation of phase transformation in ferromagnetic shape memory Fe-Pd alloy by magnetic Barkhausen noise

    Science.gov (United States)

    Furuya, Yasubumi; Tamoto, Shizuka; Kubota, Takeshi; Okazaki, Teiko; Hagood, Nesbitt W.; Spearing, S. Mark

    2002-07-01

    The possibility to detect the phase transformation with martensites by heating or cooling as well as stress-loading in ferromagnetic shape memory Fe-30at percent Pd alloy thin foil by using magnetic Markhausen noise sensor was studied. MBHN is caused by the irregular interactions between magnetic domain and thermally activated martensite twins during magnetization. In general, the envelope of the MBHN voltage versus time signals in Fe-29at percent Pd ribbon showed two peaks during magnetization, where secondary peak at intermediate state of magnetization process decreased with increasing temperature, while the MBHN envelopes in pure iron did not change with increasing temperature. The variety of MBHN due to the phase transformation was apt to arise at higher frequency part of spectrum during intermediate state of magnetization process and it decreased with disappearance of martensite twins. Besides, MBHN increased monotonically with increasing loading stress and then, it decreased with unloading, however MBHN showed large hysteresis between loading and unloading passes. Based on the experimental results from MBHN measurements for both thermoelastic and stress-induced martensite phase transformations in Fe-30at percent Pd ribbon samples, MBHN method seems a useful technique to non-destructive evaluation of martensite phase transformation of ferromagnetic shape memory alloy.

  13. Facile directing agent-free synthesis and magnetism of nanocrystalline Fe–Ni alloy with tunable shape

    International Nuclear Information System (INIS)

    Mohamed, Marwa A.A.

    2014-01-01

    Highlights: • Simple directing agent-free wet chemical method for high-yield synthesis of nc Fe-Ni particles with tunable shape. • The alloy morphology is controlled by varying synthesis conditions; concentration of metal ions and pH of reaction. • Synthesis conditions control the final shape of alloy particles via controlling their growth rate and capping with OH − ions. • The alloy magnetic behavior is driven away from soft magnetic toward hard one, by particles anisotropy and size reduction. • The branched wires morphology can be considered a new morphology of distinctive magnetic behavior, for nc Fe-Ni alloy. - Abstract: This article reports the synthesis of nanocrystalline (nc) Fe 20 Ni 80 particles with tunable shape, using a heterogeneous directing agent-free aqueous wet chemical method of mild synthesis conditions. The particle morphology has been controlled by varying synthesis conditions. The results demonstrate that the morphology of alloy particles changes from quasi-isotropic to anisotropic architecture by decreasing concentration of metal ions or increasing pH of reaction solution. Deep interpretations of such phenomena are reported. Magnetic behavior of the alloy is driven away from soft magnetic and toward hard magnetic behavior, by anisotropy and size reduction of alloy particles. This broadens practical applications of nc Fe 20 Ni 80 alloy. Overall, the study provides an effective economical way for high-yield synthesis of nc Fe–Ni particles with tailored shape and subsequently magnetic properties for a specific technological application. Additionally, it adds a new morphology, highly branched wires, of distinctive magnetic behavior to the known morphologies of nc Fe–Ni particles

  14. Ti2FeZ (Z=Al, Ga, Ge) alloys: Structural, electronic, and magnetic properties

    International Nuclear Information System (INIS)

    Liping, Mao; Yongfan, Shi; Yu, Han

    2014-01-01

    Using the first-principle projector augmented wave potential within the generalized gradient approximation taking into account the on-site Coulomb repulsive, we investigate the structural, electronic and magnetic properties of Ti 2 FeZ (Z=Al, Ga, Ge) alloys with Hg 2 CuTi-type structure. These alloys are found to be half-metallic ferrimagnets. The total magnetic moments of the Heusler alloys Ti 2 FeZ follow the µ t =Z t −18 rule and agree with the Slater–Pauling curve quite well. The band gaps are mainly determined by the bonding and antibonding states created from the hybridizations of the d states between the Ti(A)–Ti(B) coupling and Fe atom. - Highlights: • Ti 2 FeZ (Z=Al, Ga, Ge) are found to be half-metallic ferrimagnets. • The band gaps are mainly determined by the hybridizations of the d states between the Ti(A)–Ti(B) coupling and Fe atom. • The s–p elements play an important role in the half-metallicity of these Heusler alloys

  15. Laser surface modification of medical grade alloys for reduced heating in a magnetic resonance imaging environment

    Energy Technology Data Exchange (ETDEWEB)

    Benafan, O., E-mail: othmane.benafan@nasa.gov, E-mail: raj@ucf.edu; Vaidyanathan, R., E-mail: othmane.benafan@nasa.gov, E-mail: raj@ucf.edu [Advanced Materials Processing and Analysis Center (AMPAC), Materials Science and Engineering, Mechanical and Aerospace Engineering, University of Central Florida, Orlando, Florida 32816 (United States); Chen, S.-Y.; Kar, A. [Laser-Advanced Materials Processing Laboratory, Center for Research and Education in Optics and Lasers (CREOL), College of Optics and Photonics, University of Central Florida, Orlando, Florida 32816 (United States)

    2015-12-15

    Nanoscale surface modification of medical grade metallic alloys was conducted using a neodymium-doped yttrium aluminum garnet laser-based dopant diffusion technique. The objective of this approach was to minimize the induction heating by reducing the absorbed radio frequency field. Such an approach is advantageous in that the dopant is diffused into the alloy and is not susceptible to detachment or spallation as would an externally applied coating, and is expected to not deteriorate the mechanical and electrical properties of the base alloy or device. Experiments were conducted using a controlled environment laser system with the ability to control laser properties (i.e., laser power, spot size, and irradiation time) and dopant characteristics (i.e., temperature, concentration, and pressure). The reflective and transmissive properties of both the doped and untreated samples were measured in a radio frequency (63.86 MHz) magnetic field using a system comprising a high power signal generator, a localized magnetic field source and sensor, and a signal analyzer. The results indicate an increase in the reflectivity of the laser-treated samples compared to untreated samples. The effect of reflectivity on the heating of the alloys is investigated through a mathematical model incorporating Maxwell’s equations and heat conduction.

  16. Crystallization kinetics and magnetic properties of FeSiCr amorphous alloy powder cores

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Hu-ping [School of Logistics Engineering, Wuhan University of Technology, Wuhan 430063 (China); Wang, Ru-wu, E-mail: ruwuwang@hotmail.com [National Engineering Research Center For Silicon Steel, Wuhan 430080 (China); College of Materials Science and Metallurgical Engineering, Wuhan University of Science and Technology, Wuhan 430081 (China); Wei, Ding [School of Optical and Electronic Information, Huazhong University of Science and Technology, Wuhan 430074 (China); Zeng, Chun [National Engineering Research Center For Silicon Steel, Wuhan 430080 (China)

    2015-07-01

    The crystallization kinetics of FeSiCr amorphous alloy, characterized by the crystallization activation energy, Avrami exponent and frequency factor, was studied by non-isothermal differential scanning calorimetric (DSC) measurements. The crystallization activation energy and frequency factor of amorphous alloy calculated from Augis–Bennett model were 476 kJ/mol and 5.5×10{sup 18} s{sup −1}, respectively. The Avrami exponent n was calculated to be 2.2 from the Johnson–Mehl–Avrami (JMA) equation. Toroid-shaped Fe-base amorphous powder cores were prepared from the commercial FeSiCr amorphous alloy powder and subsequent cold pressing using binder and insulation. The characteristics of FeSiCr amorphous alloy powder and the effects of compaction pressure and insulation content on the magnetic properties, i.e., effective permeability μ{sub e}, quality factor Q and DC-bias properties of FeSiCr amorphous alloy powder cores, were investigated. The FeSiCr amorphous alloy powder cores exhibit a high value of quality factor and a stable permeability in the frequency range up to 1 MHz, showing superior DC-bias properties with a “percent permeability” of more than 82% at H=100 Oe. - Highlights: • The crystallization kinetics of FeSiCr amorphous alloy was investigated. • The FeSiCr powder cores exhibit a high value of Q and a stable permeability. • The FeSiCr powder cores exhibit superior DC-bias properties.

  17. Temperature dependence of the extraordinary Hall effect in magnetic granular alloys

    International Nuclear Information System (INIS)

    Granovsky, A.; Kalitsov, A.; Khanikaev, A.; Sato, H.; Aoki, Y.

    2003-01-01

    We present the results of theoretical investigation of the temperature dependence of the extraordinary Hall effect (EHE) in granular metal-metal and metal-insulator alloys in the case of electron-phonon scattering at high temperatures. Skew scattering is assumed to be the dominant mechanism of the EHE. The calculations were carried out using Zhang-Levy model and the effective-medium approximation. The single-site electron-phonon interaction model was considered by analogy to that one in the theory of disordered alloys. In the case of strong spin-dependent scattering there is an additional term in the temperature dependence of the EHE coefficient of magnetic granular alloys in comparison with that for bulk ferromagnets. This term is linear with T 3 . The similar temperature dependence for the EHE conductivity in granular metal-metal and metal-insulator alloys takes place in spite of the different origin of giant magnetoresistance in these systems. The strong temperature dependence of the EHE coefficient can be viewed as an evidence of enhanced spin-orbit interaction at interfaces between granules and the matrix. We show a linear correlation between the interface contribution to the EHE coefficient and the interface contribution to alloy resistivity. The obtained results are in a qualitative agreement with the recent experimental data for nanocomposites

  18. Temperature dependence of the extraordinary Hall effect in magnetic granular alloys

    Energy Technology Data Exchange (ETDEWEB)

    Granovsky, A. E-mail: granov@magn.ru; Kalitsov, A.; Khanikaev, A.; Sato, H.; Aoki, Y

    2003-02-01

    We present the results of theoretical investigation of the temperature dependence of the extraordinary Hall effect (EHE) in granular metal-metal and metal-insulator alloys in the case of electron-phonon scattering at high temperatures. Skew scattering is assumed to be the dominant mechanism of the EHE. The calculations were carried out using Zhang-Levy model and the effective-medium approximation. The single-site electron-phonon interaction model was considered by analogy to that one in the theory of disordered alloys. In the case of strong spin-dependent scattering there is an additional term in the temperature dependence of the EHE coefficient of magnetic granular alloys in comparison with that for bulk ferromagnets. This term is linear with T{sup 3}. The similar temperature dependence for the EHE conductivity in granular metal-metal and metal-insulator alloys takes place in spite of the different origin of giant magnetoresistance in these systems. The strong temperature dependence of the EHE coefficient can be viewed as an evidence of enhanced spin-orbit interaction at interfaces between granules and the matrix. We show a linear correlation between the interface contribution to the EHE coefficient and the interface contribution to alloy resistivity. The obtained results are in a qualitative agreement with the recent experimental data for nanocomposites.

  19. The magnetic properties of Ce/Pd surface alloys investigated using DFT

    KAUST Repository

    Shuttleworth, I.G.

    2014-01-01

    The surface alloys that form between Ce and Pd(1 1 1), Pd(1 0 0) and both unreconstructed and missing-row type Pd(1 1 0) at low Ce coverage ( θCe=19ML) have shown permanent magnetism that is mediated in part by an RKKY-like delocalized Ce 6s-Pd 5s interaction. The Pd 4d states are significantly affected by alloying and their behavior cannot be explained by a purely spin-dependent Hamiltonian. Experimental observations of changes to the Pd 4d states are explained and the implications of Ce/Pd magnetism in reforming catalysis are discussed. © 2014 Elsevier B.V. All rights reserved.

  20. Fe based amorphous and compounds metallic alloys for magnetic and structural use

    International Nuclear Information System (INIS)

    Lavorato, G; Bassi, F; De Rosa, H; Moya, J

    2008-01-01

    Massive amorphous metals (thicker than 1mm) are new types of material that could have a wide range of future applications due to a unique combination of their physical properties, mechanics and magnetics. Among these are the elevated tension of fracture and hardness, and excellent soft magnetic properties. Since 1960, when an amorphous metallic alloy was first discovered, progress has continued on the application possibilities for these materials. One of their main limitations, maximum obtainable thickness, has continued to increase, since at first thicknesses of a few microns were obtained. Now amorphous alloys more than 70 mm thick are obtained using different metallic elements. Since 1995 massive amorphous metals can be produced using Fe as the base element. At first they were made in order to achieve good soft magnetic properties (thicknesses of ∼5 mm) and later a renewed interest in their use as structural material led to the development of materials with thicknesses of 16 mm and paramagnetics at room temperature. Increasing the toughness of these materials is also a challenge and investigators have proposed several solutions, among them is the development of composite materials where dendrites from a solid solution act as crack stoppers of fissures that are spread by an amorphous matrix. This work presents the results of studies with two types of synthesized materials using the rapid cooling technique from injection copper mold casting at air temperature: 1) a massive amorphous metallic alloy with composition (Fe 0.375 Co 0 .375 B 0.2 Si 0.05 )96Nb 4 (at.%) and 2) a composite of solid solution dendrites α-(FeCo) scattered in an amorphous matrix with a composition similar to alloy 1. Using the samples obtained structural studies were made (optic and electronic microscopy SEM, XRD, EDAX, DTA), magnetic studies (coercive field and saturation magnetization) and mechanical studies (Vickers microhardness). The fully amorphous alloy could be obtained with a

  1. The magnetic properties of Ce/Pd surface alloys investigated using DFT

    KAUST Repository

    Shuttleworth, I.G.

    2014-06-01

    The surface alloys that form between Ce and Pd(1 1 1), Pd(1 0 0) and both unreconstructed and missing-row type Pd(1 1 0) at low Ce coverage ( θCe=19ML) have shown permanent magnetism that is mediated in part by an RKKY-like delocalized Ce 6s-Pd 5s interaction. The Pd 4d states are significantly affected by alloying and their behavior cannot be explained by a purely spin-dependent Hamiltonian. Experimental observations of changes to the Pd 4d states are explained and the implications of Ce/Pd magnetism in reforming catalysis are discussed. © 2014 Elsevier B.V. All rights reserved.

  2. High-field magnetization behavior in random anisotropy amorphous Co-Er alloys

    Science.gov (United States)

    Lassri, H.; Driouch, L.; Krishnan, R.

    1994-05-01

    Amorphous Co1-xErx ribbons with x=55 and 65 were prepared by the melt-spinning technique. Magnetization measurements were carried out in the temperature range 4-100 K under high magnetic fields up to 20 T. Even at 20 T the saturation is not fully attained. Assuming that Co has no moment in the alloy with x=65 the Er moment is found to be 7.0μB which indicates a speromagnetic spin structure. The Co moment in the alloy with x=55 is then found to be 0.1μB, which is negligibly small. By analyzing the approach to saturation using Chudnovsky's theory we have extracted some fundamental parameters.

  3. Magnetic Behavior of Ni-Fe Core-Shell and Alloy Nanowires

    Science.gov (United States)

    Tripathy, Jagnyaseni; Vargas, Jose; Spinu, Leonard; Wiley, John

    2013-03-01

    Template assisted synthesis was used to fabricate a series of Ni-Fe core-shell and alloy nanowires. By controlling reaction conditions as well as pore structure, both systems could be targeted and magnetic properties followed as a function of architectures. In the core-shell structure coercivity increases with decrease in shell thickness while for the alloys, coercivity squareness improve with increase pore diameter. Details on the systematic studies of these materials will be presented in terms of hysteretic measurements, including first order reversal curves (FORC), and FMR data. Magnetic variation as a function of structure and nanowire aspect ratios will be presented and the origins of these behaviors discussed. Advanced Material Research Institute

  4. Effect of steady and time-harmonic magnetic fields on macrosegragation in alloy solidification

    Energy Technology Data Exchange (ETDEWEB)

    Incropera, F.P.; Prescott, P.J. [Purdue Univ., West Lafayette, IN (United States)

    1995-12-31

    Buoyancy-induced convection during the solidification of alloys can contribute significantly to the redistribution of alloy constituents, thereby creating large composition gradients in the final ingot. Termed macrosegregation, the condition diminishes the quality of the casting and, in the extreme, may require that the casting be remelted. The deleterious effects of buoyancy-driven flows may be suppressed through application of an external magnetic field, and in this study the effects of both steady and time-harmonic fields have been considered. For a steady magnetic field, extremely large field strengths would be required to effectively dampen convection patterns that contribute to macrosegregation. However, by reducing spatial variations in temperature and composition, turbulent mixing induced by a time-harmonic field reduces the number and severity of segregates in the final casting.

  5. Feedforward-feedback hybrid control for magnetic shape memory alloy actuators based on the Krasnosel'skii-Pokrovskii model.

    Directory of Open Access Journals (Sweden)

    Miaolei Zhou

    Full Text Available As a new type of smart material, magnetic shape memory alloy has the advantages of a fast response frequency and outstanding strain capability in the field of microdrive and microposition actuators. The hysteresis nonlinearity in magnetic shape memory alloy actuators, however, limits system performance and further application. Here we propose a feedforward-feedback hybrid control method to improve control precision and mitigate the effects of the hysteresis nonlinearity of magnetic shape memory alloy actuators. First, hysteresis nonlinearity compensation for the magnetic shape memory alloy actuator is implemented by establishing a feedforward controller which is an inverse hysteresis model based on Krasnosel'skii-Pokrovskii operator. Secondly, the paper employs the classical Proportion Integration Differentiation feedback control with feedforward control to comprise the hybrid control system, and for further enhancing the adaptive performance of the system and improving the control accuracy, the Radial Basis Function neural network self-tuning Proportion Integration Differentiation feedback control replaces the classical Proportion Integration Differentiation feedback control. Utilizing self-learning ability of the Radial Basis Function neural network obtains Jacobian information of magnetic shape memory alloy actuator for the on-line adjustment of parameters in Proportion Integration Differentiation controller. Finally, simulation results show that the hybrid control method proposed in this paper can greatly improve the control precision of magnetic shape memory alloy actuator and the maximum tracking error is reduced from 1.1% in the open-loop system to 0.43% in the hybrid control system.

  6. Feedforward-feedback hybrid control for magnetic shape memory alloy actuators based on the Krasnosel'skii-Pokrovskii model.

    Science.gov (United States)

    Zhou, Miaolei; Zhang, Qi; Wang, Jingyuan

    2014-01-01

    As a new type of smart material, magnetic shape memory alloy has the advantages of a fast response frequency and outstanding strain capability in the field of microdrive and microposition actuators. The hysteresis nonlinearity in magnetic shape memory alloy actuators, however, limits system performance and further application. Here we propose a feedforward-feedback hybrid control method to improve control precision and mitigate the effects of the hysteresis nonlinearity of magnetic shape memory alloy actuators. First, hysteresis nonlinearity compensation for the magnetic shape memory alloy actuator is implemented by establishing a feedforward controller which is an inverse hysteresis model based on Krasnosel'skii-Pokrovskii operator. Secondly, the paper employs the classical Proportion Integration Differentiation feedback control with feedforward control to comprise the hybrid control system, and for further enhancing the adaptive performance of the system and improving the control accuracy, the Radial Basis Function neural network self-tuning Proportion Integration Differentiation feedback control replaces the classical Proportion Integration Differentiation feedback control. Utilizing self-learning ability of the Radial Basis Function neural network obtains Jacobian information of magnetic shape memory alloy actuator for the on-line adjustment of parameters in Proportion Integration Differentiation controller. Finally, simulation results show that the hybrid control method proposed in this paper can greatly improve the control precision of magnetic shape memory alloy actuator and the maximum tracking error is reduced from 1.1% in the open-loop system to 0.43% in the hybrid control system.

  7. The magnetic anisotropy of Gd-Y alloys

    Science.gov (United States)

    Phu Thuy, Nguyen; Verdonk, H. J.; Menovsky, A.; Franse, J. J. M.; Gersdorf, R.

    1983-02-01

    Magnetic torque curves on single crystals of Gd 1- xY x ( x ⩽ 0.1) show a reduction of the anomalous contribution that was observed in pure Gd, with increasing Y-content. Several explanations of this phenomenon are indicated in this paper.

  8. New look at magnetism in single-crystal Gd-Y alloys

    International Nuclear Information System (INIS)

    Ito, T.; Legvold, S.; Beaudry, B.J.

    1981-01-01

    Magnetic susceptibility, electrical resistivity, and specific-heat measurements have been made on a number of polycrystalline and single-crystal samples of Gd-rich Gd-Y alloys. It has been found (i) that samples with more than 30 at. % Y exhibit a helical structure phase; (ii) that samples between 10 and 30 at. % Y exhibit two different Curie-Weiss regimes leading to ''double'' ferromagnetism; and (iii) that samples with less than 10 at. % Y have Gd-like behavior

  9. Effects of atomic and magnetic order on electronic transport in Pd-richPd-Fe alloys

    Czech Academy of Sciences Publication Activity Database

    Kudrnovský, Josef; Drchal, Václav; Khmelevskyi, S.; Turek, Ilja

    2011-01-01

    Roč. 84, č. 21 (2011), "214436-1"-"214436-8" ISSN 1098-0121 R&D Projects: GA ČR(CZ) GAP204/11/1228 Institutional research plan: CEZ:AV0Z10100520; CEZ:AV0Z20410507 Keywords : residual resistivity * anisotropic magnetoresistance * anomalous Hall effect * PdFe-alloys * spin-orbit coupling * theory Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.691, year: 2011

  10. Magnetism and atomic short-range order in Ni-Rh alloys

    Science.gov (United States)

    Carnegie, D. W., Jr.; Claus, H.

    1984-07-01

    Low-field ac susceptibility measurements of Ni-Rh samples of various concentrations are presented. Giant effects of the metallurgical state on the magnetic ordering temperature are associated with changes in the degree of atomic short-range order. By careful control of this degree of short-range order, it is possible to demonstrate the existence of a spin-glass state in Ni-Rh alloys.

  11. Magnetic properties of the CrMnFeCoNi high-entropy alloy

    International Nuclear Information System (INIS)

    Schneeweiss, Oldřich; Friák, Martin; Masaryk University, Brno; Dudová, Marie; Holec, David

    2017-01-01

    In this paper, we present experimental data showing that the equiatomic CrMnFeCoNi high-entropy alloy undergoes two magnetic transformations at temperatures below 100 K while maintaining its fcc structure down to 3 K. The first transition, paramagnetic to spin glass, was detected at 93 K and the second transition of the ferromagnetic type occurred at 38 K. Field-assisted cooling below 38 K resulted in a systematic vertical shift of the hysteresis curves. Strength and direction of the associated magnetization bias was proportional to the strength and direction of the cooling field and shows a linear dependence with a slope of 0.006 ± 0.001 emu T. The local magnetic moments of individual atoms in the CrMnFeCoNi quinary fcc random solid solution were investigated by ab initio (electronic density functional theory) calculations. Results of the numerical analysis suggest that, irrespective of the initial configuration of local magnetic moments, the magnetic moments associated with Cr atoms align antiferromagnetically with respect to a cumulative magnetic moment of their first coordination shell. The ab initio calculations further showed that the magnetic moments of Fe and Mn atoms remain strong (between 1.5 and 2 μ B ), while the local moments of Ni atoms effectively vanish. Finally, these results indicate that interactions of Mn- and/or Fe-located moments with the surrounding magnetic structure account for the observed macroscopic magnetization bias.

  12. Hard magnetic properties and coercivity mechanism of melt-spun Misch Metal-Fe-B alloy

    Energy Technology Data Exchange (ETDEWEB)

    Quan, Ningtao; Luo, Yang, E-mail: eluoyang@foxmail.com; Yan, Wenlong; Yuan, Chao; Yu, Dunbo; Sun, Liang; Lu, Shuo; Li, Hongwei; Zhang, Hongbin

    2017-09-01

    Highlights: • Melt-spun MM{sub 13}Fe{sub 81}B{sub 6} alloy shows that the distributions of the La, Ce, Pr, Nd, Fe and B elements is uniformly distributed, and the grain size is in the range of 30–40 nm, it can be seen that Pr-rich and La-rich phases concentrated on grain boundaries, which resulted in the coercivity augment with the increase of MMFe{sub 2} content, and the grain size is around 40–50 nm in MM{sub 16}Fe{sub 78}B{sub 6}. • There is a significant formation of MMFe{sub 2} with abundant Pr and La, and a small amount of Ce and Nd enriched at the interfacial region in MM{sub 16}Fe{sub 78}B{sub 6}, thus an inhomogeneous region was formed. It is considered that the inhomogeneous region is effective in increasing the coercivity. • The optimum-quenched MM{sub 13}Fe{sub 81}B{sub 6} alloy have been shown to exhibit a coercive force of 6.9 kOe and an energy product of 8.5 MGOe, which is superior to anisotropic ferrite magnets of 4.5 MGOe. - Abstract: Magnetic and structural properties of Misch Metal (MM)-Fe-B alloys, were examined in the melt-spun ribbons. Melt-spun MM-Fe-B samples were prepared at the surface velocities of 18–30 m/s. Crystalline structure and their room-temperature magnetization characteristics were analyzed, and the optimum surface velocity of 20 m/s and nominal composition of MM{sub 13}Fe{sub 81}B{sub 6} were obtained. Microstructural analyses indicate that the grain size is approximately 30–50 nm in the alloys with the optimum characteristics. In the MM{sub 16}Fe{sub 78}B{sub 6} alloys, Pr-rich and La-rich phases concentrated on grain boundaries, which resulted in the coercivity augment with the increase of MMFe{sub 2} content. Dependence of coercivity on applied magnetic field suggested that the mechanism of coercivity in moderate MM-content samples was inhomogeneous domain wall pinning type. The melt-spun ribbons in the optimum condition exhibit a coercive force of 6.9 kOe and an energy product of 8.5 MGOe, which can be used as

  13. Localization in presence of magnetic field in 2-D disordered binary alloys

    International Nuclear Information System (INIS)

    Brezini, A.; Zekri, N.

    1993-08-01

    The conductance fluctuations in the presence of a magnetic field B for a disordered binary alloy are numerically examined. The Hamiltonian is quite different from the Anderson model. We calculate the participation ration for finite systems in the whole range spectrum to discriminate the nature of eigenstates. We then evaluate the conductivity from the usual Kubo Greenwood formula. The fluctuations are therefore extracted as a function of energy for a given value of B and system size L. The data predict a delocalization of the eigenstates due to the magnetic field and a factor of 2 reduction of the universal conductance fluctuations in agreement with the theory. (author). 28 refs, 3 figs

  14. External influence on magnetic properties of Fe-based nanocrystalline alloys

    Energy Technology Data Exchange (ETDEWEB)

    Sitek, Jozef [Department of Nuclear Physics and Technology, Faculty of Electrical Engineering and Information Technology, Slovak University of Technology, Ilkovicova 3, 812 19 Bratislava (Slovakia)]. E-mail: jozef.sitek@stuba.sk; Degmova, Jarmila [Department of Nuclear Physics and Technology, Faculty of Electrical Engineering and Information Technology, Slovak University of Technology, Ilkovicova 3, 812 19 Bratislava (Slovakia); Sedlackova, Katarina [Department of Nuclear Physics and Technology, Faculty of Electrical Engineering and Information Technology, Slovak University of Technology, Ilkovicova 3, 812 19 Bratislava (Slovakia); Butvin, Pavol [Institute of Physics, Slovak Academy of Sciences, Dubravska cesta 9, 845 11 Bratislava (Slovakia)

    2006-09-15

    Amorphous and nanocrystalline ribbons of NANOPERM, FINEMET and HITPERM were studied by Moessbauer spectroscopy (MS) after the influence of external factors: different annealing atmospheres, tensile stress and several kinds of corrosion. MS is a suitable tool for such studies because the spectral parameters are very sensitive to changes in the vicinity of the probe -{sup 57}Fe nuclei. The most sensitive parameters were hyperfine magnetic field in crystalline component, average hyperfine field in amorphous component and direction of net magnetic moments. Influence of external factors modified also the structure of the alloys, i.e. new or modified phases were identified by MS phase analysis.

  15. External influence on magnetic properties of Fe-based nanocrystalline alloys

    International Nuclear Information System (INIS)

    Sitek, Jozef; Degmova, Jarmila; Sedlackova, Katarina; Butvin, Pavol

    2006-01-01

    Amorphous and nanocrystalline ribbons of NANOPERM, FINEMET and HITPERM were studied by Moessbauer spectroscopy (MS) after the influence of external factors: different annealing atmospheres, tensile stress and several kinds of corrosion. MS is a suitable tool for such studies because the spectral parameters are very sensitive to changes in the vicinity of the probe - 57 Fe nuclei. The most sensitive parameters were hyperfine magnetic field in crystalline component, average hyperfine field in amorphous component and direction of net magnetic moments. Influence of external factors modified also the structure of the alloys, i.e. new or modified phases were identified by MS phase analysis

  16. Electronic, magnetic and transport properties of quaternary (Cu,Ni)MnSb alloys

    Czech Academy of Sciences Publication Activity Database

    Kudrnovský, Josef; Drchal, Václav; Máca, František; Turek, Ilja

    2008-01-01

    Roč. 88, 18-20 (2008), s. 2739-2746 ISSN 1478-6435 R&D Projects: GA ČR GA202/07/0456; GA MŠk OC 150; GA AV ČR IAA100100616 Institutional research plan: CEZ:AV0Z10100520; CEZ:AV0Z20410507 Keywords : density functional theory * exchange interaction * effective Heisenberg model * magnetic disorder * Curie temperature * quaternary Heusler alloys Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.384, year: 2008

  17. Magnetic and other properties and sputtering behavior of Co-base amorphous alloy films

    International Nuclear Information System (INIS)

    Hayashi, K.; Hayakawa, M.; Ochiai, Y.; Matsuda, H.; Ishikawa, W.; Iwasaki, Y.; Aso, K.

    1987-01-01

    Magnetic and other properties of Co-base amorphous alloy films prepared by sputtering are investigated. A detailed magnetic phase diagram with saturation magnetic flux density, crystallization temperature, and zero-magnetostrictive line on Co-Ta-Zr amorphous alloys were obtained, and the technical knowhow to make a film with well-reproducible characteristics by widely changing the sputtering conditions was related with these physical properties. Especially on alloy sputtering, a phenomenological model for elucidating a composition difference between film and target is presented. After these studies, the film characteristics of B/sub s/ = 12 kG, T/sub x/ = 450 0 C, chemical bondλ/sub s/chemical bond -8 , H/sub c/<10 mOe, and permeabilities of μ(1 MHz) = 7000, μ(100 MHz) = 2000 for the single film of 2 μm in thickness and of μ(1 MHz) = 4000, μ(100 MHz) = 800 for the insulator-sandwiched multilayered film of 10 μm are obtained, and these well-balanced values enable us to apply the materials for high-frequency recording head

  18. CPA theory of the magnetization in rare earth transition metal alloys

    International Nuclear Information System (INIS)

    Szpunar, B.; Lindgaard, P.A.

    1976-11-01

    Calculations were made of the magnetic moment per atom of the transition metal and the rare earth metal in the intermetallic compounds, Gdsub(1-x)Nisub(x), Gdsub(1-x)Fesub(x), Gdsub(1-x)Cosub(x), and Ysub(1-x)Cosub(x). A simple model of the disordered alloy consisting of spins localized on the rare earth atoms and interacting with a narrow d-band is considered. The magnetic moment of the alloy at zero temperature is calculated within the molecular field and Hartree-Fock approximations. Disorder is treated in the coherent potential approximation. Results are in good agreement with the experimental data obtained for the crystalline and amorphous intermetallic compounds. It is shown that the temperature dependence of the magnetic moments and Curie and ferrimagnetic compensation temperatures can be accounted for by a simple model assuming a RKKY interaction between the rare-earth moments and the transition metal pseudo spin. The interaction is mediated by an effective alloy medium calculated using the CPA theory and elliptic densities of states. (Auth.)

  19. Effect of boron addition on the magnetic properties of the Fe-Nd-Al alloys prepared by suction casting

    International Nuclear Information System (INIS)

    Bai, Q.; Xu, H.; Tan, X.H.; Zhang, S.Y.

    2007-01-01

    The microstructure and magnetic properties of the Fe-Nd-Al alloys prepared by suction casting with boron addition have been investigated. The increasing boron content in the Fe-Nd-Al alloys significantly increases the intrinsic coercivity ( i H c ) and decreases the proportion of the amorphous phase. The magnetization at the maximum applied field (σ ' s ) of the Fe-Nd-Al-B alloys decreases, while the coercivity increases markedly after annealing. The high intrinsic coercivity is due to the presence of the Nd 2 Fe 14 B phase

  20. Structural health monitoring for DOT using magnetic shape memory alloy cables in concrete

    Science.gov (United States)

    Davis, Allen; Mirsayar, Mirmilad; Sheahan, Emery; Hartl, Darren

    2018-03-01

    Embedding shape memory alloy (SMA) wires in concrete components offers the potential to monitor their structural health via external magnetic field sensing. Currently, structural health monitoring (SHM) is dominated by acoustic emission and vibration-based methods. Thus, it is attractive to pursue alternative damage sensing techniques that may lower the cost or increase the accuracy of SHM. In this work, SHM via magnetic field detection applied to embedded magnetic shape memory alloy (MSMA) is demonstrated both experimentally and using computational models. A concrete beam containing iron-based MSMA wire is subjected to a 3-point bend test where structural damage is induced, thereby resulting in a localized phase change of the MSMA wire. Magnetic field lines passing through the embedded MSMA domain are altered by this phase change and can thus be used to detect damage within the structure. A good correlation is observed between the computational and experimental results. Additionally, the implementation of stranded MSMA cables in place of the MSMA wire is assessed through similar computational models. The combination of these computational models and their subsequent experimental validation provide sufficient support for the feasibility of SHM using magnetic field sensing via MSMA embedded components.

  1. Pressure dependence of the magnetic properties of various weakly ferromagnetic transition metal alloys

    International Nuclear Information System (INIS)

    Buis, N.

    1979-01-01

    A large number of experimental results are summarized obtained in an apparatus designed for the measurement of magnetization under high pressures (up to 5k bar gas pressure), at temperatures from 4.2K to room temperature and in magnetic fields up to 5.1 T. Two alloy systems studied were Zr (Fesub(1-x)Cosub(x)) 2 and Y(Fesub(x)Cosub(1-x)) 2 and no consistent picture could be deduced from the large pressure effects on the magnetization. Apparently, one cannot apply the model for weak itinerant ferromagnetism on Zr(Fesub(1-x)Cosub(x)) 2 or a simple giant moment model on Y(Fesub(x)Cosub(1-x)) 2 with small iron content, because the magnetic behaviour of both systems is too complicated. (C.F.)

  2. Annealing influence on the atomic ordering and magnetic moment in a Ni-Mn-Ga alloy

    International Nuclear Information System (INIS)

    Gutierrez, J.; Lazpita, P.; Barandiaran, J.M.; Fdez-Gubieda, M.L.; Chaboy, J.; Kawamura, N.

    2007-01-01

    We have studied an alloy of composition Ni 51 Mn 28 Ga 21 prepared by rapid quenching in the form of a ribbon, with transformation temperature T M =337 K below the magnetic-order temperature, T C =344 K. Annealing of the samples was performed at 600 K for different times. From magnetic characterization a clear increase of the saturation magnetization accompanied with an increase of T C (up to 20 K) and T M (about 10 K) has been observed. XMCD measurements of both as-quenched and annealed samples have revealed great changes for the Mn and also the existence of a strong Ni signal. These results point out a possible non-negligible role of Ni, through the polarization of the conduction band, into driving the interplay between annealing and the magnetic properties in these materials

  3. Magnetic properties of the CrMnFeCoNi high-entropy alloy

    Czech Academy of Sciences Publication Activity Database

    Schneeweiss, Oldřich; Friák, Martin; Dudová, Marie; Holec, D.; Šob, Mojmír; Kriegner, D.; Holý, V.; Beran, Přemysl; George, E. P.; Neugebauer, J.; Dlouhý, Antonín

    2017-01-01

    Roč. 96, č. 1 (2017), č. článku 014437. ISSN 2469-9950 R&D Projects: GA ČR(CZ) GA14-22834S; GA MŠk(CZ) LQ1601 Institutional support: RVO:68081723 ; RVO:61389005 Keywords : high-entropy alloys * magnetism * low-temperatures * quantum-mechanical calculations * magnetic transitions Subject RIV: BM - Solid Matter Physics ; Magnetism; BM - Solid Matter Physics ; Magnetism (UJF-V) OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.); Condensed matter physics (including formerly solid state physics, supercond.) (UFM-A); Condensed matter physics (including formerly solid state physics, supercond.) (UJF-V) Impact factor: 3.836, year: 2016

  4. Random magnetism in amorphous rare-earth alloys (invited)

    Science.gov (United States)

    Sellmyer, D. J.; Nafis, S.

    1985-04-01

    Several aspects of the magnetic transitions seen in rare-earth metallic glasses are discussed, particularly with reference to recent theoretical work. These include: (a) apparent double transitions observed in Gd glasses where exchange fluctuations are important, (b) evidence for a correlated speromagnetic state recently predicted by Chudnovsky and Serota, and (c) the analysis of a Tb glass with strong random anisotropy in terms of an Ising-type spin-glass transition.

  5. Influence of Radiation Damage and Isochronal Annealing on the Magnetic Susceptibility of Pu1-xAmx Alloys

    International Nuclear Information System (INIS)

    McCall, Scott K.; Fluss, Michael J.; Chung, Brandon W.; Haire, Richard G.

    2008-01-01

    Results of radiation damage in Pu and Pu 1-x Am x alloys studied with magnetic susceptibility, χ(T), and resistivity are presented. Damage accumulated at low temperatures increases χ(T) for all measured alloys, with the trend generally enhanced as the lattice expands. There is a trend towards saturation observable in the damage induced magnetic susceptibility data. that is not evident in similar damage induced resistivity data taken on the same specimen. A comparison of isochronal annealing curves measured by both resistivity and magnetic susceptibility on a 4.3 at% Ga stabilized δ-Pu specimen show that Stage I annealing, where interstitials begin to move, is largely transparent to the magnetic measurement. This indicates that interstitials have little impact on the damage induced increase in the magnetic susceptibility. The isochronal annealing curves of the Pu 1-x Am x alloys do not show distinct annealing stages as expected for alloys. However, samples near 20% Am concentration show an unexpected increase in magnetization beginning when specimens are annealed to 35 K. This behavior is also reflected in a time dependent increase in the magnetic susceptibility of damaged specimens indicative of first order kinetics. These results suggest there may be a metastable phase induced by radiation damage and annealing in Pu 1-x Am x alloys. (authors)

  6. Low-energy mechanically milled τ-phase MnAl alloys with high coercivity and magnetization

    International Nuclear Information System (INIS)

    Lu, Wei; Niu, Junchao; Wang, Taolei; Xia, Kada; Xiang, Zhen; Song, Yiming; Zhang, Hong; Yoshimura, Satoru; Saito, Hitoshi

    2016-01-01

    The high cost of rare earth elements makes the use of high-performance permanent magnets commercially very expensive. MnAl magnetic material is one of the most promising Rare-Earth-free permanent magnets due to its obvious characteristics. However, the coercivity of MnAl alloys produced by melt spinning followed by appropriate treatment is relatively low. In this investigation, a high coercivity up to 5.3 kOe and saturation magnetization of ∼62 emu/g (with an applied magnetic field of 19.5 kOe) were obtained in the mechanically milled τ-phase Mn_5_7Al_4_3 alloy. As milling time goes on, the coercivity firstly increases and then decreases, leading to the formation of knee-point coercivity, while the saturation magnetization decreases simultaneously. The structural imperfections such as disordering and defects play the most important role in the changes of magnetic properties of τ-phase MnAl alloys processed by low-energy mechanical milling. The present results will be helpful for the development of processing protocols for the optimization of τ-phase MnAl alloys as high performance Rare-Earth-free permanent magnets. - Highlights: • Successful fabrication of pure τ-phase Mn_5_7Al_4_3 alloy by melt spinning and low-energy ball milling processes. • High coercivity (~5.3 kOe) and magnetization (~62 emu/g) were obtained in τ-phase Mn_5_7Al_4_3 alloy. • Disordering and defects play the most important role in the changes of magnetic properties.

  7. Low-energy mechanically milled τ-phase MnAl alloys with high coercivity and magnetization

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Wei, E-mail: weilu@tongji.edu.cn [School of Materials Science and Engineering, Shanghai Key Lab. of D& A for Metal-Functional Materials, Tongji University, Shanghai 200092 (China); Research Center for Engineering Science, Akita University, Akita 010-8502 Japan (Japan); Niu, Junchao; Wang, Taolei; Xia, Kada; Xiang, Zhen; Song, Yiming [School of Materials Science and Engineering, Shanghai Key Lab. of D& A for Metal-Functional Materials, Tongji University, Shanghai 200092 (China); Zhang, Hong; Yoshimura, Satoru; Saito, Hitoshi [Research Center for Engineering Science, Akita University, Akita 010-8502 Japan (Japan)

    2016-08-05

    The high cost of rare earth elements makes the use of high-performance permanent magnets commercially very expensive. MnAl magnetic material is one of the most promising Rare-Earth-free permanent magnets due to its obvious characteristics. However, the coercivity of MnAl alloys produced by melt spinning followed by appropriate treatment is relatively low. In this investigation, a high coercivity up to 5.3 kOe and saturation magnetization of ∼62 emu/g (with an applied magnetic field of 19.5 kOe) were obtained in the mechanically milled τ-phase Mn{sub 57}Al{sub 43} alloy. As milling time goes on, the coercivity firstly increases and then decreases, leading to the formation of knee-point coercivity, while the saturation magnetization decreases simultaneously. The structural imperfections such as disordering and defects play the most important role in the changes of magnetic properties of τ-phase MnAl alloys processed by low-energy mechanical milling. The present results will be helpful for the development of processing protocols for the optimization of τ-phase MnAl alloys as high performance Rare-Earth-free permanent magnets. - Highlights: • Successful fabrication of pure τ-phase Mn{sub 57}Al{sub 43} alloy by melt spinning and low-energy ball milling processes. • High coercivity (~5.3 kOe) and magnetization (~62 emu/g) were obtained in τ-phase Mn{sub 57}Al{sub 43} alloy. • Disordering and defects play the most important role in the changes of magnetic properties.

  8. Ab initio study of effect of Co substitution on the magnetic properties of Ni and Pt-based Heusler alloys

    Energy Technology Data Exchange (ETDEWEB)

    Roy, Tufan, E-mail: tufanroyburdwan@gmail.com [Theory and Simulations Lab, HRDS, Raja Ramanna Centre for Advanced Technology, Indore 452013 (India); Homi Bhabha National Institute, Training School Complex, Anushaktinagar, Mumbai 400094 (India); Chakrabarti, Aparna [Theory and Simulations Lab, HRDS, Raja Ramanna Centre for Advanced Technology, Indore 452013 (India); Homi Bhabha National Institute, Training School Complex, Anushaktinagar, Mumbai 400094 (India)

    2017-04-25

    Using density functional theory based calculations, we have carried out in-depth studies of effect of Co substitution on the magnetic properties of Ni and Pt-based shape memory alloys. We show the systematic variation of the total magnetic moment, as a function of Co doping. A detailed analysis of evolution of Heisenberg exchange coupling parameters as a function of Co doping has been presented here. The strength of RKKY type of exchange interaction is found to decay with the increase of Co doping. We calculate and show the trend, how the Curie temperature of the systems vary with the Co doping. - Highlights: • We discuss the effects of Co doping on magnetic properties of Ni/Pt based Heusler alloys. • Indirect RKKY interaction is maximum for shape memory alloy like systems. • We predict Pt{sub 2}MnSn as a probable ferromagnetic shape memory alloy.

  9. Microstructure and Properties of Cobalt-and Zinc-Containing Magnetic Magnesium Alloys Processed by High-Pressure Die Casting

    Science.gov (United States)

    Klose, Christian; Demminger, Christian; Maier, Hans Jürgen

    The inherent magnetic properties of lightweight alloys based on magnesium and cobalt offer a novel way in order to measure mechanical loads throughout the entire structural component using the magnetoelastic effect. Because the solubility of cobalt in the magnesium matrix is negligible, the magnetic properties mainly originate from Co-rich precipitates. Thus, the size and distribution of Co-containing phases within the alloy's microstructure wields a major influence on the amplitude of the load-sensitive properties which can be measured by employing the harmonic analysis of eddy-current signals. In this study, Mg-Co-based alloys are produced by several casting methods which allow the application of different cooling rates, e.g. gravity die casting and high-pressure die casting. The differences between the manufactured alloys' micro- and phase structures are compared depending on the applied cooling rate and the superior magnetic and mechanical properties of the high-pressure die cast material are demonstrated.

  10. Study on soft magnetic properties of Finemet-type nanocrystalline alloys with Mo substituting for Nb

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Dehui; Zhou, Bingwen; Jiang, Boyu; Ya, Bin; Zhang, Xingguo [School of Materials Science and Engineering, Dalian University of Technology, Dalian (China)

    2017-10-15

    The thermal stability, microstructure, and soft magnetic properties as a function of annealing time were studied for Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 3-x}Mo{sub x} (x = 0, 1, 2, 3) (atom percent, at.%,) ribbons. It was found that substituting Nb by Mo reduced the thermal stability. After 15 min short time vacuum annealing, Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 2}Mo{sub 1} and Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 1}Mo{sub 2} samples obtained higher permeability and similar coercivity compared to the original Finemet alloy (Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 3}), Mo substituting Nb reduced the optimum annealing time in Finemet-type alloys, and meanwhile marginally increased the saturation magnetization. Substituting all Nb by Mo led to the earlier formation of non-soft magnetic phase, thus deteriorated the soft magnetic properties. XRD and TEM structural analysis showed that in Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 2}Mo{sub 1} and Fe{sub 73.5}Si{sub 13.5}B{sub 9}Cu{sub 1}Nb{sub 1}Mo{sub 2} samples (annealed for 15 min), nanocrystals ∝10 nm in size were obtained, and the good soft magnetic properties of these alloys could be attributed to the small grain size. The relationship between annealing time, soft magnetic properties, and microstructure was established. Reducing annealing time and temperature to obtain best soft magnetic properties could cut down the production costs of Finemet-type alloys. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  11. Quantifying the strain-induced dissolution of precipitates in Al alloy microstructures using nuclear magnetic resonance

    International Nuclear Information System (INIS)

    Hutchinson, C.R.; Loo, P.T.; Bastow, T.J.; Hill, A.J.; Costa Teixeira, J. da

    2009-01-01

    Nuclear magnetic resonance (NMR) has been used for the first time to directly monitor the dynamic partitioning of Cu atoms from shearable precipitates into the solid solution as a function of straining at room temperature in two Al-Cu-based alloys. Al-3Cu-0.05Sn (wt.%) and Al-2.5Mg-1.5Cu (wt.%) alloys were heat-treated to provide a fine distribution of ∼5 nm Guinier-Preston (GP) zones and <1 nm Guinier-Preston-Bagaryatsky (GPB) zones, respectively, and were then subjected to rolling strains up to 100%. It is shown that in the Al-Cu-0.05Sn alloy, strains up to ∼40% can pump solute from the ∼5 nm GP zones back into solid solution for the temperature and strain-rate of deformation employed here. In the case of the Al-Cu-Mg alloy, no dissolution of the GPB zones is observed. A simple model for the strain-induced dissolution of the shearable precipitates is given and compared with the experimental results. The dependence of the Cu repartitioning process on the precipitate size is emphasized. These observations and modeling give guidelines for the design of Al-Cu-based alloys to exploit the dynamic interplay of strain-induced Cu partitioning between metastable states, e.g. solid solution and GP (or GPB) zones, for tailoring ultimate mechanical properties. It is proposed that this strain-induced phase transformation is a form of dynamically responding microstructure that can be employed to obtain aluminum alloys with well-designed microstructures.

  12. Alloy design of Nd2, Fe14B permanent magnets

    International Nuclear Information System (INIS)

    Horton, J.A.; Herchenroeder, J.W.

    2000-01-01

    This report summarizes the results of research conducted as part of CRADA ORNL94-0279 between Oak Ridge National Laboratory and Magnequench International, Inc. The objective was to gain a better understanding of the fracture process in the rare earth based permanent magnets in order to possibly improve the mechanical properties of these inherently brittle intermetallics. The first part of the study established a technique for measuring a critical property, fracture toughness, and surveying currently available commercial material made by a number of different processes

  13. Effect Of DyMn Alloy-Powder Addition On Microstructure And Magnetic Properties Of NdFeB Sintered Magnets

    Directory of Open Access Journals (Sweden)

    Lee M.-W.

    2015-06-01

    Full Text Available Micostructural change and corresponding effect on coercivity of a NdFeB sintered magnet mixed with small amount of DyMn powder was investigated. In the sintered magnet mixed with the DyMn alloy-powder Dy-rich shell was formed at outer layer of the main grains, while Mn was mostly concentrated at Nd-rich triple junction phase (TJP, lowering melting temperature of the Nd-rich phase that eventually improved the microstructural characteristics of the gain boundary phase. The coercivity of a magnet increased more than 3.5 kOe by the mixing of the DyMn alloy-powder.

  14. Perpendicular magnetic anisotropy in granular multilayers of CoPd alloyed nanoparticles

    Science.gov (United States)

    Vivas, L. G.; Rubín, J.; Figueroa, A. I.; Bartolomé, F.; García, L. M.; Deranlot, C.; Petroff, F.; Ruiz, L.; González-Calbet, J. M.; Pascarelli, S.; Brookes, N. B.; Wilhelm, F.; Chorro, M.; Rogalev, A.; Bartolomé, J.

    2016-05-01

    Co-Pd multilayers obtained by Pd capping of pre-deposited Co nanoparticles on amorphous alumina are systematically studied by means of high-resolution transmission electron microscopy, x-ray diffraction, extended x-ray absorption fine structure, SQUID-based magnetometry, and x-ray magnetic circular dichroism. The films are formed by CoPd alloyed nanoparticles self-organized across the layers, with the interspace between the nanoparticles filled by the non-alloyed Pd metal. The nanoparticles show atomic arrangements compatible with short-range chemical order of L 10 strucure type. The collective magnetic behavior is that of ferromagnetically coupled particles with perpendicular magnetic anisotropy, irrespective of the amount of deposited Pd. For increasing temperature three magnetic phases are identified: hard ferromagnetic with strong coercive field, soft-ferromagnetic as in an amorphous asperomagnet, and superparamagnetic. Increasing the amount of Pd in the system leads to both magnetic hardness increment and higher transition temperatures. Magnetic total moments of 1.77(4) μB and 0.45(4) μB are found at Co and Pd sites, respectively, where the orbital moment of Co, 0.40(2) μB, is high, while that of Pd is negligible. The effective magnetic anisotropy is the largest in the capping metal series (Pd, Pt, W, Cu, Ag, Au), which is attributed to the interparticle interaction between de nanoparticles, in addition to the intraparticle anisotropy arising from hybridization between the 3 d -4 d bands associated to the Co and Pd chemical arrangement in a L 10 structure type.

  15. Soft magnetic properties and damping parameter of (FeCo-Al alloy thin films

    Directory of Open Access Journals (Sweden)

    Isao Kanada

    2017-05-01

    Full Text Available For high frequency device applications, a systematic study of the soft magnetic properties and magnetization dynamics of (FeCo-Al alloy thin films has been carried out. A low effective damping parameter αeff of 0.002 and a high saturation magnetization of about 1,800 emu/cc are obtained at y=0.2∼0.3 for (Fe1-yCoy98Al2 alloy thin films deposited onto fused silica and MgO(100 at an ambient temperature during deposition. Those films are of the bcc structure with the orientation normal to the film plane. They possess a columnar structure, grown along the film normal. The column width is found to be about 20 nm for y=0.25. It is concluded that the (FeCo-Al thin films with a damping parameter as low as 0.002 and high saturation magnetization of about 1,800 emu/cc have been successfully fabricated, and that they are potential for future high frequency device applications.

  16. Magnetic and thermal properties of amorphous TbFeCo alloy films

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Ke, E-mail: K.Wang@hqu.edu.cn; Dong, Shuo; Huang, Ya; Qiu, Yuzhen

    2017-07-15

    Highlights: • Significant increase in magnetization is observed in TbFeCo upon crystallization. • The crystallization temperature is determined in the range between 400 and 450 °C. • The activation barriers for structural changes are obtained successfully. • Better thermal stability against crystallization and oxidation is demonstrated in FeCo-rich sample than Tb-rich type. - Abstract: Amorphous TbFeCo material with perpendicular magnetic anisotropy is currently attracting more attention for potential applications in spintronic devices and logic memories. We systematically investigate magnetic, structural, thermal, optical and electrical properties of TbFeCo alloy films. It shows out-of-plane easy axis of the films turns into in-plane orientation after annealing. Significant increase in saturation magnetization in the temperature range between 400 and 450 °C is revealed by thermomagnetic measurements. The occurrence of crystallization and oxidation at high temperatures is confirmed by X-ray diffraction measurements. Pronounced changes in optical reflectance and sheet resistance are observed with temperature, in line with structural relaxation and change. The activation barriers for crystallization and oxidation are determined to be 1.01 eV and 0.83 eV, respectively, for FeCo-rich and Tb-rich samples. Better thermal stability against crystallization and oxidation is demonstrated in the FeCo-rich sample than the Tb-rich type. Our results provide some useful information for the alloy used in device fabrication.

  17. Effect of Co addition on the magnetic properties and microstructure of FeNbBCu nanocrystalline alloys

    Energy Technology Data Exchange (ETDEWEB)

    Xue, Lin [School of Materials Science and Engineering, Southeast University, Nanjing 211189 (China); Ningbo Institute of Industrial Technology, Chinese Academy of Sciences, Ningbo 315201 (China); School of Sciences, China University of Mining and Technology, Xuzhou 221116 (China); Yang, Weiming [School of Sciences, China University of Mining and Technology, Xuzhou 221116 (China); Liu, Haishun, E-mail: liuhaishun@126.com [School of Sciences, China University of Mining and Technology, Xuzhou 221116 (China); Men, He [Ningbo Institute of Industrial Technology, Chinese Academy of Sciences, Ningbo 315201 (China); Wang, Anding, E-mail: anding@nimte.ac.cn [Ningbo Institute of Industrial Technology, Chinese Academy of Sciences, Ningbo 315201 (China); Chang, Chuntao [Ningbo Institute of Industrial Technology, Chinese Academy of Sciences, Ningbo 315201 (China); Shen, Baolong, E-mail: blshen@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189 (China)

    2016-12-01

    Through gradient substitution of Co for Fe, the magnetic properties and microstructures of (Fe{sub 1−x}Co{sub x}){sub 83}Nb{sub 2}B{sub 14}Cu{sub 1} (x=0.1, 0.2, 0.3, 0.4, 0.5) nanocrystalline alloys were investigated. Because of the strong ferromagnetic exchange coupling between Co and Fe, substantial improvement in saturation magnetization was achieved with proper levels of Co addition. Meanwhile, the Curie temperature increased noticeably with increasing Co addition. After heat treatment, the (Fe{sub 0.9}Co{sub 0.1}){sub 83}Nb{sub 2}B{sub 14}Cu{sub 1} nanocrystalline alloy showed a refined microstructure with an average grain size of 10–20 nm, exhibiting a comparatively high saturation magnetization of 1.82 T and a lower coercivity of 12 A/m compared to other Hitperm-type alloys with higher Co contents. Additionally, the Curie temperature reached 1150 K upon introduction of Co. As the soft magnetic properties are strengthened by adding a small amount of Co, the combination of fine, soft magnetic properties and low cost make this nanocrystalline alloy a potential magnetic material. - Highlights: • New (Fe{sub 1−x}Co{sub x}){sub 83}Nb{sub 2}B{sub 14}Cu{sub 1} nanocrystalline alloys are successfully synthesized. • Minor Co addition improves the Curie temperature of (Fe{sub 1−x}Co{sub x}){sub 83}Nb{sub 2}B{sub 14}Cu{sub 1} alloy system. • (Fe{sub 1−x}Co{sub x}){sub 83}Nb{sub 2}B{sub 14}Cu{sub 1} nanocrystalline alloys exhibit high saturation magnetization above 1.82 T.

  18. Obtained of magnetic alloys at base of rare earths-transition metals (4f/3d) by calciothermal reduction

    International Nuclear Information System (INIS)

    Paschoal, J.O.A.; Lima, L.F.C.P. de; Faria Junior, R.N.; Monzani, D.; Takiishi, H.; Caldas, S.H.R.; Gulherme, E.G.; Carvalho, P.A.; Acevedo, M.T.

    1989-01-01

    The phases of preparation of powder of the alloys Sm-Co and Nd-Fe-B are studied. These phases were developed and optimized like part of the permanent magnet program of the Energetic and Nuclear Research Institute (IPEN), in Brazil, that has the objective of obtain magnets of high product of energy (BxH). (V.R.B.)

  19. Effect of magnetostatic interactions on twin boundary motion in Ni-Mn-Ga magnetic shape memory alloy

    Czech Academy of Sciences Publication Activity Database

    Heczko, Oleg; Vokoun, David; Kopecký, Vít; Beleggia, M.

    2015-01-01

    Roč. 6, Jul (2015), s. 1000204 ISSN 1949-307X R&D Projects: GA ČR GA15-00262S Institutional support: RVO:68378271 Keywords : magnetism in solids * demagnetization factors * magnetostatic interactions * shape memory alloys Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.978, year: 2015

  20. Microemulsion synthesis and magnetic properties of FexNi(1-x) alloy nanoparticles

    Science.gov (United States)

    Beygi, H.; Babakhani, A.

    2017-01-01

    This paper investigates synthesis of FexNi(1-x) bimetallic nanoparticles by microemulsion method. Through studying the mechanism of nanoparticles formation, it is indicated that synthesis of nanoparticles took placed by simultaneous reduction of metal ions and so nanoparticles structure is homogeneous alloy. FexNi(1-x) nanoparticles with different sizes, morphologies and compositions were synthesized by changing the microemulsion parameters such as water/surfactant/oil ratio, presence of co-surfactant and NiCl2·6H2O to FeCl2·4H2O molar ratio. Synthesized nanoparticles were characterized by transmission electron microscopy, particle size analysis, X-ray diffraction, atomic absorption and thermogravimetric analyses. The results indicated that, presence of butanol as co-surfactant led to chain-like arrangement of nanoparticles. Also, finer nanoparticles were synthesized by decreasing the amount of oil and water and increasing the amount of CTAB. The results of vibrating sample magnetometer suggested that magnetic properties of FexNi(1-x) alloy nanoparticles were affected by composition, size and morphology of the particles. Spherical and chain-like FexNi(1-x) alloy nanoparticles were superparamagnetic and ferromagnetic, respectively. Furthermore, higher iron in the composition of nanoparticles increases the magnetic properties.

  1. The effect of additional elements on the magnetic properties of hot-rolled Nd-Fe-B alloys

    International Nuclear Information System (INIS)

    Chang, W.C.; Nakamura, H.; Paik, C.R.; Sugimoto, S.; Okada, M.; Homma, M.

    1992-01-01

    The magnetic properties of hot-rolled Nd 16 Fe bal. B 6 M 1.5 (M = Cu, Ga and Al) and Nd 16 Fe 76 B 5.5 Ga 1.5 Al 1 alloys were investigated, in order to study the role of additive elements in improving the magnetic properties in the Nd-Fe-B system. It is found that the original grain size of Cu, Ga or Ga-Al added alloys is much finer than that of the ternary and Al added alloys. But the grain size is almost identical for all the alloys after hot-rolling at 1000degC with 90% reduction in thickness. The coercivity of hot-rolled alloys with Cu, Ga or Ga-Al addition is not improved as was expected, because Nd-rich liquid phase in these alloys is very easily squeezed out during high-reduction-ratio rolling. Less quantity and nonuniform distribution of Nd-rich phase between distributed grains are believed to be the main reasons to depress the effect on the grain boundary smoothing. This effect is not the same as those observed in the Pr-Fe-B system. The highest magnetic properties achieved in this study are B r = 10 kG, i H c = 8.2 kOe, (BH) max = 18.5 MGOe for the Nd 16 Fe 76.5 B 6 Al 1.5 alloy. (orig.)

  2. Quantitative description of the magnetization curves of amorphous alloys of the series a-DyxGd1-xNi

    International Nuclear Information System (INIS)

    Barbara, B.; Filippi, J.; Amaral, V.S.

    1992-01-01

    The magnetization curves of the series of amorphous alloys Dy x Gd 1-x Ni measured between 1.5 and 4.2 K and up to 15 T, have been fitted to the zero kelvin analytical model of Chudnovsky. The results of these fits allow a detailed understanding of the magnetization curves of amorphous alloys with ferromagnetic interactions. In particular, the ratio D/J of the local anisotropy and exchange energies, and the magnetic and atomic correlation lengths, are accurately determined. (orig.)

  3. Perpendicular magnetic anisotropy in Co{sub X}Pd{sub 100−X} alloys for magnetic tunnel junctions

    Energy Technology Data Exchange (ETDEWEB)

    Clark, B.D.; Natarajarathinam, A.; Tadisina, Z.R. [Center for Materials for Information Technology, University of Alabama, Tuscaloosa, AL 35487 (United States); Chen, P.J.; Shull, R.D. [National Institute of Standards and Technology, Gaithersburg, MD 20899 (United States); Gupta, S., E-mail: Sgupta@eng.ua.edu [Center for Materials for Information Technology, University of Alabama, Tuscaloosa, AL 35487 (United States)

    2017-08-15

    Highlights: • CoPd alloy perpendicular anisotropy dependent on composition and thickness. • CIPT results show that TMR tracks with PMA of CoPd. • Potential replacement for Co/Pd multilayers. - Abstract: CoFeB/MgO-based perpendicular magnetic tunnel junctions (p-MTJ’s) with high anisotropy and low damping are critical for spin-torque transfer random access memory (STT-RAM). Most schemes of making the pinned CoFeB fully perpendicular require ferrimagnets with high damping constants, a high temperature-grown L1{sub 0} alloy, or an overly complex multilayered synthetic antiferromagnet (SyAF). We report a compositional study of perpendicular Co{sub x}Pd alloy-pinned Co{sub 20}Fe{sub 60}B{sub 20}/MgO based MTJ stacks, grown at moderate temperatures in a planetary deposition system. The perpendicular anisotropy of the Co{sub x}Pd alloy films can be tuned based on the layer thickness and composition. The films were characterized by alternating gradient magnetometry (AGM), energy-dispersive X-rays (EDX), and X-ray diffraction (XRD). Current-in-plane tunneling (CIPT) measurements have also been performed on the compositionally varied Co{sub x}Pd MTJ stacks. The Co{sub x}Pd alloy becomes fully perpendicular at approximately x = 30% (atomic fraction) Co. Full-film MTJ stacks of Si/SiO{sub 2}/MgO (13)/Co{sub X}Pd{sub 100−x} (50)/Ta (0.3)/CoFeB (1)/MgO (1.6)/CoFeB (1)/Ta (5)/Ru (10), with the numbers enclosed in parentheses being the layer thicknesses in nm, were sputtered onto thermally oxidized silicon substrates and in-situ lamp annealed at 400 °C for 5 min. CIPT measurements indicate that the highest TMR is observed for the CoPd composition with the highest perpendicular magnetic anisotropy.

  4. Preparation of Pr-Fe-Co-B-Nb-M (M= Al, P, Cu, Ga and/or Gd) HDDR magnets and alloys and characterization of their magnetic properties and corrosion resistance

    International Nuclear Information System (INIS)

    Oliveira, Mara Cristina Lopes de

    2009-01-01

    HDDR process has attracted great interest for producing polymer- bonded rare earth based magnets. It presents commercial advantages when compared with conventional sintered magnets owing to easy and low cost manufacturing. With the development of anisotropic powders using praseodymium, the expectations about this process grow e also the need for studying new compositions and alloy additions. In this work the magnetic properties of polymer-bonded magnets prepared with PrFeB magnetic alloys using HDDR process have been studied. Pr 14 Fe bal Co 16 B 6 Nb 0,1 was used as the reference alloy Phosphorus, copper, aluminium, gallium and gadolinium additions have been performed to increase the magnetic properties of the reference alloy. The microstructural characterization of the magnets has been carried out through optical microscopy and SEM. The complex microstructure influences the electrochemical behavior of the magnetic alloys. The literature about this subject is scarce. Thus, the corrosion resistance of the different alloys prepared during this work was evaluated using electrochemical impedance spectroscopy and potentiodynamic polarization curves. A correlation between the microstructural features and the electrochemical behavior of the alloys has been established. The results showed that phosphorus and aluminium additions up to 1.0wt% had a beneficial effect on the magnetic properties and corrosion resistance of the alloys. Copper additions, on the other hand, strongly diminished the magnetic properties of the reference alloy. (author)

  5. Studying the initial stages of film electrodeposition of magnetic cobalt-tungsten alloys

    International Nuclear Information System (INIS)

    Rachinskas, V.S.; Orlovskaya, L.V.; Parfenov, V.A.; Yasulajtene, V.V.

    1996-01-01

    Initial stages of magnetic film electrodeposition by recording potentiodynamic polarization and j c ,t-curves, determination of surface structure of electrolytically deposited films by the method of XPS and study of thin coating properties have been considered. It is shown that at initial stage of electrodeposition of magnetic Co-W-films a sharp decrease in cathode process rate and formation of Co(OH) 2 , WO 3 and/or WO 4 2- occur on Cu-cathode surface. Electrodeposition of metallic magnetic Co-W-alloy, consisting of Co, W and containing basic compounds of co-deposited metals, takes place after a certain time period depending on deposition E c . 6 refs.; 3 figs

  6. Study of the effect of short ranged ordering on the magnetism in FeCr alloys

    Energy Technology Data Exchange (ETDEWEB)

    Jena, Ambika Prasad, E-mail: apjena@bose.res.in [Department of Condensed Matter and Materials Science, S N Bose National Centre for Basic Sciences, JD Block, Sector III, Salt Lake City, Kolkata 700098 (India); Sanyal, Biplab, E-mail: biplab.sanyal@physics.uu.se [Department of Physics and Astronomy, Uppsala University, Box 516, SE-75120 Uppsala (Sweden); Mookerjee, Abhijit, E-mail: abhijit.mookerjee61@gmail.com [Department of Condensed Matter and Materials Science, S N Bose National Centre for Basic Sciences, JD Block, Sector III, Salt Lake City, Kolkata 700098 (India)

    2014-01-15

    For the study of magnetism in systems where the local environment plays an important role, we propose a marriage between the Monte Carlo simulation and Zunger's special quasi-random structures. We apply this technique on disordered FeCr alloys and show that our estimates of the transition temperature is in good agreement with earlier experiments. - Highlights: • The magnetism in FeCr is sensitively depended on the ordering of the atoms : disordered or with short ranged ordering. • This work uses the SQS technique suggested by Zunger has been used to generate various degrees of short range ordering in FeCr. • The electronic structure and pair energies have been obatined from first principles ASR and Lichtenstein methods. • The effect of chemical ordering on magnetic ordering is studied in detail. • Only those situations where the chemical ordering is complete have been studied.

  7. Study of the effect of short ranged ordering on the magnetism in FeCr alloys

    International Nuclear Information System (INIS)

    Jena, Ambika Prasad; Sanyal, Biplab; Mookerjee, Abhijit

    2014-01-01

    For the study of magnetism in systems where the local environment plays an important role, we propose a marriage between the Monte Carlo simulation and Zunger's special quasi-random structures. We apply this technique on disordered FeCr alloys and show that our estimates of the transition temperature is in good agreement with earlier experiments. - Highlights: • The magnetism in FeCr is sensitively depended on the ordering of the atoms : disordered or with short ranged ordering. • This work uses the SQS technique suggested by Zunger has been used to generate various degrees of short range ordering in FeCr. • The electronic structure and pair energies have been obatined from first principles ASR and Lichtenstein methods. • The effect of chemical ordering on magnetic ordering is studied in detail. • Only those situations where the chemical ordering is complete have been studied

  8. Investigation of thermal, mechanical and magnetic behaviors of the Cu-11%Al alloy with Ag and Mn additions

    International Nuclear Information System (INIS)

    Silva, R.A.G.; Paganotti, A.; Gama, S.; Adorno, A.T.; Carvalho, T.M.; Santos, C.M.A.

    2013-01-01

    The investigation of thermal, mechanical and magnetic behaviors of the Cu-11%Al, Cu-11%Al-3%Ag, Cu-11%Al-10%Mn and Cu-11%Al-10%Mn-3%Ag alloys was made using microhardness measurements, differential scanning calorimetry, X-ray diffractometry, scanning electron microscopy, energy dispersion X-ray spectroscopy and magnetic moment change with applied field measurement. The results indicated that the Mn addition changes the phase stability range, the microhardness values and makes undetectable the eutectoid reaction in annealed Cu-11%Al and Cu-11%Al-3%Ag alloys while the presence of Ag does not modify the phase transformation sequence neither microhardness values of the annealed Cu-11%Al and Cu-11%Al-10%Mn alloys, but it increases the magnetic moment of this latter at about 2.7 times and decreases the rates of eutectoid and peritectoid reactions of the former. - Highlights: ► The microstructure of Cu-Al alloy is modified in the Ag presence. ► (α + γ) phase is stabilized down to room temperature when Ag is added to Cu-Al alloy. ► Ag-rich phase modifies the magnetic characteristics of Cu–Al–Mn alloy.

  9. Martensitic transformation and magnetic properties of manganese-rich Ni-Mn-In and Ni-Mn-Sn Heusler alloys

    International Nuclear Information System (INIS)

    Krenke, T.

    2007-01-01

    In the present work, the martensitic transition and the magnetic properties of Manganese rich Ni 50 Mn 50-x Sn x and Ni 50 Mn 50-y In y alloys with 5 at%≤x(y)≤25 at% were investigated. Calorimetry, X-ray and neutron diffraction, magnetization, and strain measurements were performed on polycrystalline samples. It was shown that alloys close to the stoichiometric composition Ni 50 Mn 25 Sn 25 and Ni 50 Mn 25 Sn 25 do not exhibit a structural transition on lowering of the temperature, whereas alloys with x≤15 at% Tin and y≤16 at% Indium transform martensitically. The structural transition temperatures increase linearly with decreasing Tin or Indium content. The crystal structures of the low temperature martensite are modulated as well as unmodulated. Alloys with compositions close to stoichiometry are dominated by ferromagnetic interactions, whereas those close to the binary composition Ni 50 Mn 50 order antiferromagnetically. Ferromagnetic order and structural instability coexist in a narrow composition range between 13 at%≤x≤15 at% and 15 at%≤x≤16 at% for Ni 50 Mn 50-x Sn x and Ni 50 Mn 50-y In y respectively. As a consequence, interesting magnetoelastic effects are observed. The Ni 50 Mn 34 In 16 alloy shows a magnetic field-induced structural transition, whereby application of an external magnetic field in the martensitic state stabilizes the high temperature L2 1 structure. Evidence for this was given by neutron diffraction experiments in external magnetic fields. Moreover, the structural transition temperatures of this alloy show large magnetic field dependencies. By use of calorimetry, M(T), and strain measurements, changes in M s up to -11 K/Tesla are observed. Such large values have, until now, not been observed in Heusler alloys. Since during transformation the volume changes reversibly, magnetic field-induced strains of about 0.12 % appear. Additionally, the alloys Ni 50 Mn 35 Sn 15 , Ni 50 Mn 37 Sn 13 , Ni 50 Mn 34 In 16 , Ni 51.5 Mn 33 In

  10. Study of magnetic hardening in Sm(Co/sub 1-x/Cu/sub x/)/sub 5/ alloy

    International Nuclear Information System (INIS)

    Awan, M.S.; Bhatti, A.S.; Farooque, M.

    2008-01-01

    Magnetic hardening has been examined in the samarium (Sm), cobalt (Co) and copper (Cu) fused permanent magnets by correlating the magnetic properties with annealing temperature and microstructure of the samples. For the Sm(Co/sub 1-x/Cu/sub x/)/sub 5/ system, with various copper contents (x=0, 0.2, 0.3, 0.4 and 0.5) the shape of initial magnetization curve indicated that the magnetic hardening process involved in these types of magnets consists of domain wall pinning type. This is consistent with the microstructure studies which show the existence of nonmagnetic Cu-rich precipitates in the Co-rich matrix. Copper substituted samples were annealed in the temperature range (300 -1000) degree C for 3h under the protective atmosphere of argon (Ar) gas. Both cast and annealed samples prepared by tri-arc melting technique exhibit two-phase microstructure responsible for enhanced magnetic properties. Metallographic and surface studies were carried out using a digital optical microscope (OM). X-ray diffraction (XRD) studies confirmed that the alloys solidefied in the hexagonal crystal structure. The lattice parameters and unit cell volume increase with increasing Cu content. Scanning electron microscope (SEM) coupled with energy dispersive X-ray (EDX) was used to examine the surface morphology, compositional variations, elemental segregations, formation and effect of annealing on the different phases. Later these parameters were related to the magnetic properties. Copper-rich phase precipitates in the Co- rich matrix may serves as the pinning centers for the domain wall motion. Introduction of these pinning centers improved the magnetic hardening of the alloy. Annealing the Cu-substituted alloy further improved the magnetic properties. During annealing, diffusion of copper played the key role for enhanced magnetic properties. It was found that both Cu substitution and subsequent annealing are the dominating factors determining the magnetic properties of these magnetic

  11. Influence of cobalt content on the structure and hard magnetic properties of nanocomposite (Fe,Co)-Pt-B alloys

    Energy Technology Data Exchange (ETDEWEB)

    Grabias, A., E-mail: agnieszka.grabias@itme.edu.pl [Institute of Electronic Materials Technology, Wólczyńska 133, 01-919 Warsaw (Poland); Kopcewicz, M. [Institute of Electronic Materials Technology, Wólczyńska 133, 01-919 Warsaw (Poland); Latuch, J.; Oleszak, D. [Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warsaw (Poland); Pękała, M. [Department of Chemistry, University of Warsaw, Al. Żwirki i Wigury 101, 02-089 Warsaw (Poland); Kowalczyk, M. [Faculty of Materials Science and Engineering, Warsaw University of Technology, Wołoska 141, 02-507 Warsaw (Poland)

    2017-07-15

    Highlights: • Nanocomposite alloys were formed by annealing of the rapidly quenched alloys. • Magnetically hard L1{sub 0} (Fe,Co)Pt and soft (Fe,Co){sub 2}B or (Fe,Co)B were formed. • Mössbauer spectra revealed Co substitution for Fe in L1{sub 0} FePt, FeB and Fe{sub 2}B phases. • Annealed alloys exhibit hard magnetic properties which depend on phase compositions. • Co addition was found to decrease the magnetization and the energy product. - Abstract: The influence of Co content on the structural and hard magnetic properties of two sets of nanocrystalline Fe{sub 52−x}Co{sub x}Pt{sub 28}B{sub 20} (x = 0–26) and Fe{sub 60−y}Co{sub y}Pt{sub 25}B{sub 15} (y = 0–40) alloys was studied. The alloys were prepared as ribbons by the rapid quenching technique. The nanocomposite structure in the alloys was obtained by annealing at 840–880 K for 30 min. Structural characterization of the samples was performed using the Mössbauer spectroscopy and X-ray diffraction. Magnetic properties of the samples were studied by the measurements of the hysteresis loops and of the magnetization at increasing temperatures. An amorphous phase prevailed in the as-quenched Fe{sub 52−x}Co{sub x}Pt{sub 28}B{sub 20} alloys while a disordered solid solution of fcc-(Fe,Co)Pt was a dominating phase in the Fe{sub 60−y}Co{sub y}Pt{sub 25}B{sub 15} ribbons. Differential scanning calorimetry measurements revealed one or two exothermic peaks at temperatures up to 993 K, depending on the composition of the alloys. Thermal treatment of the samples led to the formation of the magnetically hard ordered L1{sub 0} tetragonal (Fe,Co)Pt nanocrystallites and magnetically softer phases of (Fe,Co)B (for Fe{sub 52−x}Co{sub x}Pt{sub 28}B{sub 20}) or (Fe,Co){sub 2}B (for Fe{sub 60−y}Co{sub y}Pt{sub 25}B{sub 15}). Detailed Mössbauer spectroscopy studies revealed that cobalt substituted for iron in both the L1{sub 0} phase and in iron borides. The nanocomposite Fe{sub 60−y}Co{sub y

  12. Lattice dynamics, elasticity and magnetic abnormality in ordered crystalline alloys Fe3Pt at high pressures

    Science.gov (United States)

    Cheng, Tai-min; Yu, Guo-Liang; Su, Yong; Ge, Chong-Yuan; Zhang, Xin-Xin; Zhu, Lin; Li, Lin

    2018-05-01

    The ordered crystalline Invar alloy Fe3Pt is in a special magnetic critical state, under which the lattice dynamic stability of the system is extremely sensitive to external pressures. We studied the pressure dependence of enthalpy and magnetism of Fe3Pt in different crystalline alloys by using the first-principles projector augmented-wave method based on the density functional theory. Results show that the P4/mbm structure is the ground state structure and is more stable relative to other structures at pressures below 18.54 GPa. The total magnetic moments of L12, I4/mmm and DO22 structures decrease rapidly with pressure and oscillate near the ferromagnetic collapse critical pressure. At the pressure of 43 GPa, the ferrimagnetic property in DO22 structure becomes apparently strengthened and its volume increases rapidly. The lattice dynamics calculation for L12 structures at high pressures shows that the spontaneous magnetization of the system in ferromagnetic states induces the softening of the transverse acoustic phonon TA1 (M), and there exists a strong spontaneous volume magnetostriction at pressures below 26.95 GPa. Especially, the lattice dynamics stability is sensitive to pressure, in the pressure range between the ferromagnetic collapse critical pressure (41.9 GPa) and the magnetism completely disappearing pressure (57.25 GPa), and near the pressure of phase transition from L12 to P4/mbm structure (27.27 GPa). Moreover, the instability of magnetic structure leads to a prominent elastic modulus oscillation, and the spin polarizability of electrons near the Fermi level is very sensitive to pressures in that the pressure range. The pressure induces the stability of the phonon spectra of the system at pressures above 57.25 GPa.

  13. Magnetic structure at the surface of a FeZrB alloy

    International Nuclear Information System (INIS)

    Pavuk, M.; Miglierini, M.; Sitek, J.

    2013-01-01

    The aim of this work was to examine two structural states of the "5"7Fe_9_0Zr_7B_3 alloy from the point of view of their domain structure. As the method for obtaining the image of a domain structure we used the magnetic force microscopy (MFM). Its advantage is that besides the image of a domain structure, it also records the image of topography. Another advantage is the high spatial resolution. From both of these advantages, one can benefit in the study of nanocrystalline alloys. Nevertheless, the use of MFM in the study of nanocrystalline materials is so far only rare. Additional structural characterization was obtained by the help of Conversion Electron Moessbauer Spectrometry (CEMS). (authors)

  14. Magnetic and transport properties of amorphous Ce-Al alloy

    Science.gov (United States)

    Amakai, Yusuke; Murayama, Shigeyuki; Momono, Naoki; Takano, Hideaki; Kuwai, Tomohiko

    2018-05-01

    Amorphous (a-)Ce50Al50 has been prepared by DC high-rate sputter method. The structure of the obtained sample has been confirmed to have an amorphous structure because there are no Bragg peaks in the X-ray diffraction measurement and have a clear exothermic peak by the differential scanning calorimetry measurement. We have measured the resistivity ρ, magnetic susceptibility χ, specific heat Cp and thermoelectric power S for a-Ce50Al50. The temperature dependence of ρ exhibits a small temperature dependence less than 10% in the whole temperature region. χ follows a Curie-Weiss behavior in the high-temperature region of T>90 K. The effective paramagnetic moment peff, estimated from C is 2.18 μB/Ce-atom. The low-temperature Cp/T increases rapidly with decreasing temperature and tends to a saturation. S(T) exhibits negative values in a wide temperature region. A minimum of S appear at around 60 K, and S decreases linearly with decreasing temperature down to 10 K. The low-temperature S is almost 0 μV/K down to 2 K. From these results, we have pointed out that present a-Ce50Al50 would be an incoherent Kondo material.

  15. Impact of Ion Bombardment on the Structure and Magnetic Properties of Fe78Si13B9 Amorphous Alloy

    Science.gov (United States)

    Wu, Yingwei; Peng, Kun

    2018-06-01

    Amorphous Fe78Si13B9 alloy ribbons were bombarded by ion beams with different incident angles ( θ ). The evolution of the microstructure and magnetic properties of ribbons caused by ion beam bombardment was investigated by x-ray diffraction, transmission electron microscope and vibrating sample magnetometer analysis. Low-incident-angle bombardment led to atomic migration in the short range, and high-incident-angle bombardment resulted in the crystallization of amorphous alloys. Ion bombardment induces magnetic anisotropy and affects magnetic properties. The effective magnetic anisotropy was determined by applying the law of approach to saturation, and it increased with the increase of the ion bombardment angle. The introduction of effective magnetic anisotropy will reduce the permeability and increase the relaxation frequency. Excellent high-frequency magnetic properties can be obtained by selecting suitable ion bombardment parameters.

  16. Effects of annealing on the microstructure and magnetic property of the mechanically alloyed FeSiBAlNiM (M=Co, Cu, Ag) amorphous high entropy alloys

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Xiaoxia; Zhou, Xuan; Yu, Shuaishuai; Wei, Congcong; Xu, Jing; Wang, Yan, E-mail: mse_wangy@ujn.edu.cn

    2017-05-15

    The effects of annealing treatment on the microstructure, thermal stability, and magnetic properties of the mechanical alloyed FeSiBAlNiM (M=Co, Cu, Ag) amorphous high entropy alloys (HEAs) have been investigated in this project. The simple crystallization products in FeSiBAlNi amorphous HEAs with Co and Ag addition reveal the high phase stability during heating process. At high annealing treatment, the crystallized HEAs possess the good semi-hard magnetic property. It can conclude that crystallization products containing proper FeSi-rich and FeB-rich phases are beneficial to improve the magnetic property. Annealing near the exothermic peak temperature presents the best enhancing effect on the semi-hard magnetic property of FeSiBAlNiCo. It performs both large saturated magnetization and remanence ratio of 13.0 emu/g and near 45%, which exhibit 465% and 105% enhancement compared with as-milled state, respectively. - Highlights: • Co, Cu, Ag additions affect crystallization behavior of FeSiBAlNi amorphous HEAs. • Crystallization products in FeSiBAlNi Co/Ag reveal high phase stability. • Proper FeSi-rich and FeB-rich phases are beneficial to improve magnetic property. • Annealing treatment improves semi-hard magnetic property compared to as-milled state. • Annealing near exothermic peak temperature shows best enhancing effect on magnetism.

  17. Annealing and thickness effects on magnetic properties of Co2FeAl alloy films

    Science.gov (United States)

    Wang, Ke; Xu, Zhan; Ling, Fujin; Wang, Yahong; Dong, Shuo

    2018-03-01

    Co2FeAl (CFA) films in a wide thickness range between 2 and 100 nm are sputtered at room temperature. Perpendicular magnetic anisotropy (PMA) is achieved in the annealed structure of Pd/CFA/MgO with CFA thickness ranging between 2.3 and 4.9 nm. PMA as high as 2 × 106 erg/cm3 is demonstrated in the structures annealed in the temperature range between 300 and 350 °C. Positive contributions to the PMA made by the interfaces of Pd/CFA and CFA/MgO are identified. For the as-deposited structure of MgO/CFA/Ta with thick CFA alloy up to 5 nm or above a high effective saturation magnetization of 983.9 ± 30.1 emu/cc is derived from the fitting and an in-plane uniaxial magnetic anisotropy of 104 erg/cm3 in magnitude is revealed by angular dependent magnetic measurements. In addition to the increase in saturation magnetization, a fourfold cubic magnetic anisotropy is found to develop with annealing, in line with the improvement of the crystalline structure confirmed by X-ray diffraction measurements. Out results provide some useful information for the design of the CFA-based magnetoelectronic devices.

  18. Artificial neural network methodology: Application to predict magnetic properties of nanocrystalline alloys

    International Nuclear Information System (INIS)

    Hamzaoui, R.; Cherigui, M.; Guessasma, S.; ElKedim, O.; Fenineche, N.

    2009-01-01

    This paper is dedicated to the optimization of magnetic properties of iron based magnetic materials with regard to milling and coating process conditions using artificial neural network methodology. Fe-20 wt.% Ni and Fe-6.5 wt.% Si, alloys were obtained using two high-energy ball milling technologies, namely a planetary ball mill P4 vario ball mill from Fritsch and planetary ball mill from Retch. Further processing of Fe-Si powder allowed the spraying of the feedstock material using high-velocity oxy-fuel (HVOF) process to obtain a relatively dense coating. Input parameters were the disc Ω and vial ω speed rotations for the milling technique, and spray distance and oxygen flow rate in the case of coating process. Two main magnetic parameters are optimized namely the saturation magnetization and the coercivity. Predicted results depict clearly coupled effects of input parameters to vary magnetic parameters. In particular, the increase of saturation magnetization is correlated to the increase of the product Ωω (shock power) and the product of spray parameters. Largest coercivity values are correlated to the increase of the ratio Ω/ω (shock mode process) and the increase of the product of spray parameters.

  19. Synthesis of Fe Ni Alloy Nano materials by Proteic Sol-Gel Method: Crystallographic, Morphological, and Magnetic Properties

    International Nuclear Information System (INIS)

    Santos, C.M.D.; Martins, A.F.N.; Sasaki, J.M.; Costa, B. C.; Ribeiro, T.S.; Braga, T.P.; Soares, J.M.

    2016-01-01

    Proteic Sol-Gel method was used for the synthesis of Fe Ni alloy at different temperature conditions and flow reduction. The solids were characterized by XRD, H_2-TPR, SEM, TEM, Moessbauer spectroscopy, and VSM. It was observed by X-ray diffraction pure Fe Ni alloy in the samples reduced at 600 degree (40 ml/min H_2 flow) and 700 degree (25 ml/min H_2 flow). The Fe Ni alloy presented stability against the oxidizing atmosphere up to 250 degree. The morphology exhibited agglomerates relatively spherical and particles in the range of 10-40 nm. Moessbauer spectroscopy showed the presence of disordered ferromagnetic Fe Ni alloy, and magnetic hysteresis loop revealed a typical behavior of soft magnetic material.

  20. Synthesis of FeNi Alloy Nanomaterials by Proteic Sol-Gel Method: Crystallographic, Morphological, and Magnetic Properties

    Directory of Open Access Journals (Sweden)

    Cássio Morilla dos Santos

    2016-01-01

    Full Text Available Proteic Sol-Gel method was used for the synthesis of FeNi alloy at different temperature conditions and flow reduction. The solids were characterized by XRD, H2-TPR, SEM, TEM, Mössbauer spectroscopy, and VSM. It was observed by X-ray diffraction pure FeNi alloy in the samples reduced at 600°C (40 mL/min H2 flow and 700°C (25 mL/min H2 flow. The FeNi alloy presented stability against the oxidizing atmosphere up to 250°C. The morphology exhibited agglomerates relatively spherical and particles in the range of 10–40 nm. Mössbauer spectroscopy showed the presence of disordered ferromagnetic FeNi alloy, and magnetic hysteresis loop revealed a typical behavior of soft magnetic material.

  1. Magnetic and thermal properties of amorphous TbFeCo alloy films

    Science.gov (United States)

    Wang, Ke; Dong, Shuo; Huang, Ya; Qiu, Yuzhen

    2017-07-01

    Amorphous TbFeCo material with perpendicular magnetic anisotropy is currently attracting more attention for potential applications in spintronic devices and logic memories. We systematically investigate magnetic, structural, thermal, optical and electrical properties of TbFeCo alloy films. It shows out-of-plane easy axis of the films turns into in-plane orientation after annealing. Significant increase in saturation magnetization in the temperature range between 400 and 450 °C is revealed by thermomagnetic measurements. The occurrence of crystallization and oxidation at high temperatures is confirmed by X-ray diffraction measurements. Pronounced changes in optical reflectance and sheet resistance are observed with temperature, in line with structural relaxation and change. The activation barriers for crystallization and oxidation are determined to be 1.01 eV and 0.83 eV, respectively, for FeCo-rich and Tb-rich samples. Better thermal stability against crystallization and oxidation is demonstrated in the FeCo-rich sample than the Tb-rich type. Our results provide some useful information for the alloy used in device fabrication.

  2. Magnetic, transport, and magnetocaloric properties of boron doped Ni-Mn-In alloys

    Energy Technology Data Exchange (ETDEWEB)

    Pandey, S.; Quetz, A.; Aryal, A.; Dubenko, I.; Ali, N. [Department of Physics, Southern Illinois University, Carbondale, Illinois 62902 (United States); Rodionov, I. D.; Blinov, M. I.; Titov, I. S.; Prudnikov, V. N.; Granovsky, A. B. [Faculty of Physics, Lomonosov Moscow State University, Moscow 119991 (Russian Federation); Stadler, S. [Department of Physics and Astronomy, Louisiana State University, Baton Rouge, Louisiana 70803 (United States)

    2015-05-14

    The impact of B substitution in Ni{sub 50}Mn{sub 35}In{sub 15−x}B{sub x} Heusler alloys on the structural, magnetic, transport, and parameters of the magnetocaloric effect (MCE) has been studied by means of room-temperature X-ray diffraction and thermomagnetic measurements (in magnetic fields (H) up to 5 T, and in the temperature interval 5–400 K). Direct adiabatic temperature change (ΔT{sub AD}) measurements have been carried out for an applied magnetic field change of 1.8 T. The transition temperatures (T-x) phase diagram has been constructed for H = 0.005 T. The MCE parameters were found to be comparable to those observed in other MCE materials such as Ni{sub 50}Mn{sub 34.8}In{sub 14.2}B and Ni{sub 50}Mn{sub 35}In{sub 14}X (X=In, Al, and Ge) Heusler alloys. The maximum absolute value of ΔT{sub AD} = 2.5 K was observed at the magnetostructural transition for Ni{sub 50}Mn{sub 35}In{sub 14.5}B{sub 0.5}.

  3. Magnetic, transport, and magnetocaloric properties of boron doped Ni-Mn-In alloys

    International Nuclear Information System (INIS)

    Pandey, S.; Quetz, A.; Aryal, A.; Dubenko, I.; Ali, N.; Rodionov, I. D.; Blinov, M. I.; Titov, I. S.; Prudnikov, V. N.; Granovsky, A. B.; Stadler, S.

    2015-01-01

    The impact of B substitution in Ni 50 Mn 35 In 15−x B x Heusler alloys on the structural, magnetic, transport, and parameters of the magnetocaloric effect (MCE) has been studied by means of room-temperature X-ray diffraction and thermomagnetic measurements (in magnetic fields (H) up to 5 T, and in the temperature interval 5–400 K). Direct adiabatic temperature change (ΔT AD ) measurements have been carried out for an applied magnetic field change of 1.8 T. The transition temperatures (T-x) phase diagram has been constructed for H = 0.005 T. The MCE parameters were found to be comparable to those observed in other MCE materials such as Ni 50 Mn 34.8 In 14.2 B and Ni 50 Mn 35 In 14 X (X=In, Al, and Ge) Heusler alloys. The maximum absolute value of ΔT AD  = 2.5 K was observed at the magnetostructural transition for Ni 50 Mn 35 In 14.5 B 0.5

  4. Measurement and modeling of magnetic hysteresis under field and stress application in iron–gallium alloys

    International Nuclear Information System (INIS)

    Evans, Phillip G.; Dapino, Marcelo J.

    2013-01-01

    Measurements are performed to characterize the hysteresis in magnetomechanical coupling of iron–gallium (Galfenol) alloys. Magnetization and strain of production and research grade Galfenol are measured under applied stress at constant field, applied field at constant stress, and alternately applied field and stress. A high degree of reversibility in the magnetomechanical coupling is demonstrated by comparing a series of applied field at constant stress measurements with a single applied stress at constant field measurement. Accommodation is not evident and magnetic hysteresis for applied field and stress is shown to be coupled. A thermodynamic model is formulated for 3-D magnetization and strain. It employs a stress, field, and direction dependent hysteron that has an instantaneous loss mechanism, similar to Coulomb-friction or Preisach-type models. Stochastic homogenization is utilized to account for the smoothing effect that material inhomogeneities have on bulk processes. - Highlights: ► We conduct coupled experiments and develop nonlinear thermodynamic models for magnetostrictive iron–gallium (Galfenol) alloys. ► The measurements show unexpected kinematic reversibility in the magnetomechanical coupling. ► This is in contrast with the magnetomechanical coupling in steel which is both thermodynamically and kinematically irreversible. ► The model accurately describes the measurements and provides a framework for understanding hysteresis in ferromagnetic materials which exhibit kinematically reversible magnetomechanical coupling.

  5. Magnetic properties of nanocrystalline Fe–10%Ni alloy obtained by planetary ball mills

    International Nuclear Information System (INIS)

    Hamzaoui, Rabah; Elkedim, Omar

    2013-01-01

    Highlights: •Solid solution formation accompanied by a grain refinement for nanocrystalline Fe-Ni. •The shock mode process (SMP) prevails when Ω > >ω. •The friction mode process (FMP) is stronger when Ω < <ω. •The FMP leads to the formation of alloys exhibiting a soft magnetic behavior. -- Abstract: Planetary ball mill PM 400 from Retsch (with different milling times for Ω = 400 rpm, ω = 800 rpm) and P4 vario ball mill from Fritsch (with different milling conditions (Ω/ω), Ω and ω being the disc and the vial rotation speeds, respectively) are used for obtaining nanocrystalline Fe–10wt% Ni. The structure and magnetic properties are studied by using X-ray diffraction, SEM and hysteresis measurements, respectively. The bcc-Fe(Ni) phase formation is identified by X-ray diffraction. The higher the shock power and the higher milling time are, the larger the bcc lattice parameter and the lower the grain size. The highest value of the coercivity is 1600 A/m for Fe–10 wt.%Ni (with shock mode (424 rpm/100 rpm) after 36 h of milling), while the lowest value is 189 A/m for (400 rpm/800 rpm) after 72 h of milling. The milling performed in the friction mode has been found to lead the formation of alloys exhibiting a soft magnetic behavior for nanocrystalline Fe–10%Ni

  6. Study of the effect of magnetic ordering on order–disorder transitions in binary alloys

    Energy Technology Data Exchange (ETDEWEB)

    Jena, Ambika Prasad [Department of Condensed Matter and Materials Science, S.N. Bose National Centre for Basic Sciences, JD Block, Sector III, Salt Lake City, Kolkata 700098 (India); Sanyal, Biplab [Department of Physics and Astronomy, Uppsala University, Box 516, SE-75120 Uppsala (Sweden); Mookerjee, Abhijit, E-mail: abhijit@bose.res.in [Department of Condensed Matter and Materials Science, S.N. Bose National Centre for Basic Sciences, JD Block, Sector III, Salt Lake City, Kolkata 700098 (India)

    2014-06-01

    We set up a mean-field approximation in a random Ising model characterized by two order parameters: the local sublattice magnetization and a mean-field occupation variable which act as an order parameter for the order–disorder transition. In the effective model Hamiltonian the two order-parameters are coupled. We solve the coupled equations arising from this to describe the total phase diagram. The exchange energies for FeCo alloys have then been accurately obtained from first-principles based on the technique of orbital peeling and a Monte Carlo analysis using a coupled Metropolis-Kawasaki updating has been carried out. Our results reasonably successfully agree with earlier experimental data. - Highlights: • In this paper we study the effect of magnetic ordering on order–disorder transitions in binary alloys. • It describes a system with two order parameters, magnetic and chemical ordering, which are coupled. • We set up a mean-field theory for initial understanding and then carry out Monte Carlo simulations. • One parameter follows Kawasaki-dynamics and the other Metropolis. • It is an interesting system for study and we apply it to FeCo with exchanges calculated from first principles techniques.

  7. AC magnetic properties of the soft magnetic composites based on Supermalloy nanocrystalline powder prepared by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Neamtu, B.V., E-mail: bogdan.neamtu@stm.utcluj.ro [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania); Institut Neel, CNRS/Universite J. Fourier, BP166, 38042 Grenoble, Cedex 9 (France); Geoffroy, O. [Institut Neel, CNRS/Universite J. Fourier, BP166, 38042 Grenoble, Cedex 9 (France); Grenoble Electrical Engineering, University J. Fourier, BP 46, F-38402 Saint-Martin d' Heres Cedex (France); Chicinas, I. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 400614 Cluj-Napoca (Romania); Isnard, O. [Institut Neel, CNRS/Universite J. Fourier, BP166, 38042 Grenoble, Cedex 9 (France)

    2012-05-25

    Highlights: Black-Right-Pointing-Pointer Nanocrystalline soft magnetic composites were obtained. Black-Right-Pointing-Pointer The cutting frequency of the produced nanocrystalline SMC exceeds 100 kHz. Black-Right-Pointing-Pointer A long annealing at low temperature leads to an improvement of the permeability (12%). - Abstract: The preparation and characterization of the nanocrystalline soft magnetic composite core based on Supermalloy powder obtained via mechanical alloying route are presented. The AC magnetic properties of the compacts were determined in frequency range from 100 Hz to 100 kHz for flux densities of 0.05 and 0.1 T. Composite materials were obtained by covering the Supermalloy particles with a polymer binder, then compacted into toroidal shape and finally polymerized. It is found that an increase of the compacting pressure from 600 MPa to 800 MPa leads to an increase of the compacts permeability by more than 8%. Also, reducing the polymer content from 2 wt.% to 0.5 wt.% leads to an increase of the magnetic losses (at 100 kHz and 0.1 T) by 380%. The removal of the stresses induced during compaction has been accomplished by a heat treatment at 170 Degree-Sign C for 120 h. This leads to a significant increase (12%) of the relative initial permeability of the compacts.

  8. Method of making active magnetic refrigerant, colossal magnetostriction and giant magnetoresistive materials based on Gd-Si-Ge alloys

    Science.gov (United States)

    Gschneidner, Jr., Karl A.; Pecharsky, Alexandra O.; Pecharsky, Vitalij K.

    2003-07-08

    Method of making an active magnetic refrigerant represented by Gd.sub.5 (Si.sub.x Ge.sub.1-x).sub.4 alloy for 0.ltoreq.x.ltoreq.1.0 comprising placing amounts of the commercially pure Gd, Si, and Ge charge components in a crucible, heating the charge contents under subambient pressure to a melting temperature of the alloy for a time sufficient to homogenize the alloy and oxidize carbon with oxygen present in the Gd charge component to reduce carbon, rapidly solidifying the alloy in the crucible, and heat treating the solidified alloy at a temperature below the melting temperature for a time effective to homogenize a microstructure of the solidified material, and then cooling sufficiently fast to prevent the eutectoid decomposition and improve magnetocaloric and/or the magnetostrictive and/or the magnetoresistive properties thereof.

  9. Effect of Co content on structure and magnetic behaviors of high induction Fe-based amorphous alloys

    Energy Technology Data Exchange (ETDEWEB)

    Roy, Rajat K., E-mail: rajat@nmlindia.org; Panda, Ashis K.; Mitra, Amitava

    2016-11-15

    The replacement of Fe with Co is investigated in the (Fe{sub 1−x}Co{sub x}){sub 79}Si{sub 8.5}B{sub 8.5}Nb{sub 3}Cu{sub 1} (x=0, 0.05, 0.2, 0.35, 0.5) amorphous alloys. The alloys are synthesized in the forms of ribbons by single roller melt spinning technique, and the structural and magnetic properties of annealed ribbons are characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM), B–H curve tracer, respectively. All as-cast alloys are structurally amorphous, however, their magnetic properties are varying with Co addition. The Co addition within 5–20 at% results in moderate thermal stability, saturation induction, Curie temperature and lowest coercivity, while 35 at% Co causes highest saturation induction, coercivity, Curie temperature and lowest thermal stability. On devitrification, the magnetic properties change with the generation of α-FeCo nanocrystallites and (FeCo){sub 23}B{sub 6}, Fe{sub 2}B phases during primary and secondary crystallization stages, respectively. A small amount Co is advantageous for maintaining finer nanocrystallites in amorphous matrix even after annealing at 600 °C, leading to high saturation magnetization (>1.5 T) and low coercivity (~35 A/m). The improved magnetic properties at elevated temperatures indicate these alloys have a potential for high frequency transformer core applications. - Highlights: • The structural and magnetic behaviors of Fe based amorphous alloys have been investigated with the effect of Co content. • The Co has no adverse effect on amorphization of alloys. • A small amount Co causes the superior improvement of magnetic properties at elevated temperatures. • Therefore, it is important not only for academic research but also for industrial applied research.

  10. Structural and magnetic characterization of Nd-based Nd-Fe and Nd-Fe-Co-Al metastable alloys

    International Nuclear Information System (INIS)

    Kumar, G.

    2005-01-01

    The aim of the present work is to characterize a metastable hard magnetic phase referred to as ''A1'' in Nd-Fe alloys, which forms as a part of the fine eutectic depending on the composition and cooling rate. In order to define the range of composition for the formation of A1, Nd 100-x Fe x (x=20,25,40) alloys are cooled at about 150 K/s. The effect of cooling rate on the formation of hard magnetic A1 is studied by investigating the Nd 80 Fe 20 alloys cooled at different rates. The Nd-richer regions are identified as dhcp Nd and fcc Nd-Fe solid solution. However, the Fe-richer regions also referred to as A1, are diffuse and give an average composition of Nd 56 Fe 44 . HRTEM images of the Fe-richer regions reveal the presence of 5-10 nm crystallites embedded in an amorphous phase. The demagnetization curves the hard magnetic Nd80Fe20 measured at temperatures above 30 K are typical of a hard magnetic material. The measurements of initial magnetization, field dependence of coercivity, and temperature dependence of coercivity suggest the Stoner-Wohlfarth type magnetization reversal process for the hard magnetic A1. The values of anisotropy constant are estimated by fitting the magnetization data to the law-of-approach to saturation. The temperature dependence of anisotropy constant and the coercivity indicate that the origin of coercivity is magnetic anisotropy

  11. Phase evolution and its effects on the magnetic performance of nanocrystalline SmCo7 alloy

    International Nuclear Information System (INIS)

    Zhang Zhexu; Song Xiaoyan; Xu Wenwu

    2011-01-01

    The evolution of the phase constitution and the microstructure, as well as their effects on magnetic performance, were investigated systematically using a prepared nanocrystalline single-phase SmCo 7 alloy as the starting material for a series of annealing processes. The SmCo 7 (1:7 H) phase was discovered to have a good single-phase stability from room temperature up to 600 deg. C. The destabilization of the SmCo 7 phase results in the formation of the Sm 2 Co 17 (2:17 R) and SmCo 5 (1:5 H) phases, which exist as phase-transformation twins and particulate precipitates, respectively, with a completely coherent relationship with the 1:7 H parent phase. For the first time the formation mechanism of the 2:17 R phase-transformation twins has been proposed, in which the ordered substitution of 1/3 of the Sm atoms by Co-Co dumbbell pairs along two particular crystal directions was demonstrated. The characteristic width values of the 2:17 R phase-transformation twins, as deduced from this model of the mechanism, were unambiguously verified by the experimental results. Among the SmCo 7 alloys with various phase constitutions and microstructures, the best magnetic properties were obtained in the nanocrystalline 1:7 H single-phase alloys. The present work may promote a new understanding of nanoscale-stabilized single-phase SmCo 7 and its potential applications as unique high-temperature permanent magnets.

  12. Thermal evolution of nanocrystalline co-sputtered Ni–Zr alloy films: Structural, magnetic and MD simulation studies

    International Nuclear Information System (INIS)

    Bhattacharya, Debarati; Rao, T.V. Chandrasekhar; Bhushan, K.G.; Ali, Kawsar; Debnath, A.; Singh, S.; Arya, A.; Bhattacharya, S.; Basu, S.

    2015-01-01

    Monophasic and homogeneous Ni 10 Zr 7 nanocrystalline alloy films were successfully grown at room temperature by co-sputtering in an indigenously developed three-gun DC/RF magnetron sputtering unit. The films could be produced with long-range crystallographic and chemical order in the alloy, thus overcoming the widely acknowledged inherent proclivity of the glass forming Ni–Zr couple towards amorphization. Crystallinity of these alloys is a desirable feature with regard to improved efficacy in applications such as hydrogen storage, catalytic activity and nuclear reactor engineering, to name a few. Thermal stability of this crystalline phase, being vital for transition to viable applications, was investigated through systematic annealing of the alloy films at 473 K, 673 K and 923 K for various durations. While the films were stable at 473 K, the effect of annealing at 673 K was to create segregation into nanocrystalline Ni (superparamagnetic) and amorphous Ni + Zr (non-magnetic) phases. Detailed analyses of the physical and magnetic structures before and after annealing were performed through several techniques effectual in analyzing stratified configurations and the findings were all consistent with each other. Polarized neutron and X-ray reflectometry, grazing incidence x-ray diffraction, time-of-flight secondary ion mass spectroscopy and X-ray photoelectron spectroscopy were used to gauge phase separation at nanometer length scales. SQUID based magnetometry was used to investigate macroscopic magnetic properties. Simulated annealing performed on this system using molecular dynamic calculations corroborated well with the experimental results. This study provides a thorough understanding of the creation and thermal evolution of a crystalline Ni–Zr alloy. - Highlights: • Nanocrystalline Ni 10 Zr 7 alloy thin films deposited successfully by co-sputtering. • Creation of a crystalline alloy in a binary system with a tendency to amorphize. • Quantitative

  13. Nanostructure and magnetic properties of CoNi-alloy-based nanoparticles dispersed in a silica matrix

    International Nuclear Information System (INIS)

    De Julian, C.; Sangregorio, C.; Mattei, G.; Battaglin, G.; Cattaruzza, E.; Gonella, F.; Lo Russo, S.; D'Orazio, F.; Lucari, F.; De, G.; Gatteschi, D.; Mazzoldi, P.

    2001-01-01

    A comparative study of the magnetic behavior of FCC alloy CoNi (1:1) nanoparticles, embedded in a silica matrix and prepared by the ion implantation and sol-gel techniques, is presented. The blocking temperature is related to the size distribution, and, at least for the ion-implanted samples, only an enhanced effective anisotropy explains the experimental results. The hysteretic behavior is explained in terms of the temperature dependence of the anisotropy and of the particle volume fraction that determines the dipolar interactions

  14. Nanostructure and magnetic properties of CoNi-alloy-based nanoparticles dispersed in a silica matrix

    Energy Technology Data Exchange (ETDEWEB)

    De Julian, C. E-mail: dejulian@padova.infm.it; Sangregorio, C.; Mattei, G.; Battaglin, G.; Cattaruzza, E.; Gonella, F.; Lo Russo, S.; D' Orazio, F.; Lucari, F.; De, G.; Gatteschi, D.; Mazzoldi, P

    2001-05-01

    A comparative study of the magnetic behavior of FCC alloy CoNi (1:1) nanoparticles, embedded in a silica matrix and prepared by the ion implantation and sol-gel techniques, is presented. The blocking temperature is related to the size distribution, and, at least for the ion-implanted samples, only an enhanced effective anisotropy explains the experimental results. The hysteretic behavior is explained in terms of the temperature dependence of the anisotropy and of the particle volume fraction that determines the dipolar interactions.

  15. Influence of Nd content on magnetic properties of amorphous FeB alloys

    Science.gov (United States)

    Hassanain, N.; Lassri, H.; Krishnan, R.; Berrada, A.

    The influence of the addition of Nd on the magnetic properties ( TC, M0, Hc, …) of FeB amorphous alloys is investigated. Using Chudnovsky's model we have analyzed our data and obtained some fundamental parameters. For instance, with the addition of Nd atoms the local anisotropy is 2.0 × 10 7 erg cm -3 and the exchange constant. A decreases from 38 × 10 -8 to 21.7 × 10 -8 erg cm -1 as the Nd concentration increases from 0 to 15%. The ferromagnetic exchange correlation length also decreases drastically from 353 to 80 Å in the same concentration range.

  16. Magnetic Shape Memory Alloys as smart materials for micro-positioning devices

    Directory of Open Access Journals (Sweden)

    A. Hubert

    2012-10-01

    Full Text Available In the field of microrobotics, actuators based on smart materials are predominant because of very good precision, integration capabilities and high compactness. This paper presents the main characteristics of Magnetic Shape Memory Alloys as new candidates for the design of micromechatronic devices. The thermo-magneto-mechanical energy conversion process is first presented followed by the adequate modeling procedure required to design actuators. Finally, some actuators prototypes realized at the Femto-ST institute are presented, including a push-pull bidirectional actuator. Some results on the control and performances of these devices conclude the paper.

  17. Magnetisation processes and magnetic viscosity of mechanically alloyed SmCo5

    International Nuclear Information System (INIS)

    Ding, J.; Smith, P.A.I.; McCormick, P.G.; Street, R.

    1996-01-01

    Mechanically alloyed SmCo 5 materials with coercivities in the range of 50-75 kOe were studied in this work. Irreversible magnetisation processes were investigated by measuring remanences after initial magnetisation and after demagnetisation. A large deviation of the demagnetisation remanence from the Wohlfarth relationship indicated that interactions between grains play an important role in the irreversible magnetisation process. Viscosity tests showed nearly linear relationship between the magnetic field and the viscosity parameter for the initial magnetisation, while the viscosity was not strongly dependent on the field for the demagnetisation. High values of the viscosity parameter, Λ, between 120 to 220 Oe were measured at fields near coercivity. (orig.)

  18. Investigation of non-magnetic alloys for the suppression of tritium permeation

    International Nuclear Information System (INIS)

    1980-07-01

    The present work was aimed at identification of alloys which might combine low tritium permeation with other properties desired in fusion reactor vessels, heat exchangers, lithium-handling plumbing and other components likely to contain tritium. These properties include low radiation damage, low magnetic permeability, high temperature strength, and compatibility with potential heat transfer and blanket materials. The work consisted of two tasks: problem definition, and literature search and analysis. Task I was complicated by the incomplete status of fusion reactor development, particularly with respect to selection of coolant and blanket materials and temperatures. The approach taken was to establish a probable range of requirements

  19. Measurement of RF characteristics of magnetic alloys for an RF cavity of the accumulator cooler ring

    International Nuclear Information System (INIS)

    Watanabe, M.; Chiba, Y.; Katayama, T.; Koseki, T.; Ohtomo, K.; Tsutsui, H.

    2004-01-01

    The magnetic alloy (MA)-loaded RF cavity has been studied for an RF stacking system of the accumulator cooler ring (ACR). RF characteristics of several high-permeability MA cores were measured in the frequency range between 1 and 50 MHz. The effects of the cut-core configuration, cutting the core and leaving air gaps between two circular halves, were also investigated. The results show that the shunt impedance remains high and the appropriate inductance and Q-value can be obtained by increasing the gap width of the cut core in the frequency region of the ACR cavity

  20. Method of making active magnetic refrigerant materials based on Gd-Si-Ge alloys

    Science.gov (United States)

    Pecharsky, Alexandra O.; Gschneidner, Jr., Karl A.; Pecharsky, Vitalij K.

    2006-10-03

    An alloy made of heat treated material represented by Gd.sub.5(Si.sub.xGe.sub.1-x).sub.4 where 0.47.ltoreq.x.ltoreq.0.56 that exhibits a magnetic entropy change (-.DELTA.S.sub.m) of at least 16 J/kg K, a magnetostriction of at least 2000 parts per million, and a magnetoresistance of at least 5 percent at a temperature of about 300K and below, and method of heat treating the material between 800 to 1600 degrees C. for a time to this end.

  1. Penetration of a magnetic field into superconducting lead and lead-indium alloys

    International Nuclear Information System (INIS)

    Egloff, C.; Raychaudhuri, A.K.; Rinderer, L.

    1983-01-01

    The temperature dependence of the magnetic field penetration depth of superconducting lead and lead-indium alloys has been studied over the temperature range between about 2 K and T/sub c/. Data are analyzed in terms of the microscopic theory. The difficulties of a unique analysis of the penetration data are pointed out and a strategy for the analysis is discussed. The penetration depth at T = 0K for pure lead is determined as 522 A. This value, though higher than the previously accepted value for lead, is nevertheless consistent with the strong coupling character of lead

  2. Microstructural and magnetic behavior of nanostructured soft alloys prepared by mechanical grinding and gas atomization

    International Nuclear Information System (INIS)

    Marin, P.; Lopez, M.; Garcia-Escorial, A.; Lieblich, M.

    2007-01-01

    Nanocrystalline powder of Fe-Si-B-Cu-Nb has been obtained by means of mechanical milling of the corresponding nanocrystalline ribbons. Gas atomization technique has been used to minimize the magnetic hardening due to stress effects observed in ball-milled samples. Fe-Si-B-Cu-Nb and Fe-Si nanocrystalline samples have been prepared by gas atomization. The aim of our work is to analyse the particle size dependence of coercivity in this nanostructured alloys and to show the analogies and differences between ball-milled and gas atomized samples

  3. The role of sub-micron grain size in the development of rare earth hard magnetic alloys

    International Nuclear Information System (INIS)

    Davies, H.A.; Wang, Z.C.

    2004-01-01

    The magnetic properties of nanocrystalline melt spun rare earth-iron-boron alloys based on Nd or Pr and on Nd-Pr mixtures are compared for a wide range of RE:Fe ratio. Their magnetic properties are compared with those of corresponding alloy ribbons based on Nd. The Pr containing alloys have generally higher coercivity than their Nd counterparts because of the higher anisotropy constant of the Pr 2 Fe 14 B phase. Co substitution for Fe increases the Curie temperature and thermal stability for the nanophase alloys. Excellent magnetic property combinations were achieved for single phase Pr 12 (Fe 100-x Co x ) 82 B 6 (x=0-20) alloys, processed by overquenching and devitrification annealing. In contrast, in the case of nanocomposite Pr 10 (Fe 100-x Co x ) 84 B 6 alloys, based on Pr 2 Fe 14 B/α-Fe mixtures, only for 30% substitution of Fe by Co could useful enhancement of (BH) max be achieved, due to generally rather coarse α-Fe crystallites

  4. Effect of a high magnetic field on the microstructures in directionally solidified Zn–Cu peritectic alloys

    International Nuclear Information System (INIS)

    Li, Xi; Gagnoud, Annie; Wang, Jiang; Li, Xiaolong; Fautrelle, Yves; Ren, Zhongming; Lu, Xionggang; Reinhart, Guillaume; Nguyen-Thi, Henri

    2014-01-01

    The effect of an axial high magnetic field on the microstructures in directionally solidified Zn–Cu peritectic alloys was investigated. The experimental results indicated that the magnetic field induced the destabilization of the liquid–solid interface and the formation of a band-like structure. The magnetic field also caused the disruption of the columnar η-Zn and ε-Zn 5 Cu dendrites. As the applied magnetic field increased, the columnar-to-equiaxed transition occurred, and the size of the equiaxed grains gradually decreased. The magnetic effects, the magnetic moment and the thermoelectric magnetic effects during the directional solidification of Zn–Cu peritectic alloys under an axial magnetic field were studied. Regular ε-Zn 5 Cu hexagons appeared on the transverse section of the sample fabricated with a high magnetic field (i.e. 16 T). In addition, electron backscatter diffraction analysis revealed that the 〈0 0 0 1〉-crystal direction of the Zn 5 Cu crystal is not only its easy magnetization direction but also its preferred growth direction. The thermoelectric magnetic effects were numerically simulated. The results indicated that a thermoelectric magnetic force acts on the solid near the liquid–solid interface and increases linearly with an increase in the magnetic field. As the effect of the magnetic moment arising from the magnetic crystalline anisotropy is eliminated, the thermoelectric magnetic effect has a substantial effect on the solidification structure. Therefore, the destabilization of the liquid–solid interface and the disruption of the dendrites during directional solidification under the magnetic field are primarily due to the thermoelectric magnetic force acting on the solid

  5. Thermal and magnetic hysteresis associated with martensitic and magnetic phase transformations in Ni52Mn25In16Co7 Heusler alloy

    Science.gov (United States)

    Madiligama, A. S. B.; Ari-Gur, P.; Ren, Y.; Koledov, V. V.; Dilmieva, E. T.; Kamantsev, A. P.; Mashirov, A. V.; Shavrov, V. G.; Gonzalez-Legarreta, L.; Grande, B. H.

    2017-11-01

    Ni-Mn-In-Co Heusler alloys demonstrate promising magnetocaloric performance for use as refrigerants in magnetic cooling systems with the goal of replacing the lower efficiency, eco-adverse fluid-compression technology. The largest change in entropy occurs when the applied magnetic field causes a merged structural and magnetic transformation and the associated entropy changes of the two transformations works constructively. In this study, magnetic and crystalline phase transformations were each treated separately and the effects of the application of magnetic field on thermal hystereses associated with both structural and magnetic transformations of the Ni52Mn25In16Co7 were studied. From the analysis of synchrotron diffraction data and thermomagnetic measurements, it was revealed that the alloy undergoes both structural (from cubic austenite to a mixture of 7M &5M modulated martensite) and magnetic (ferromagnetic to a low-magnetization phase) phase transformations. Thermal hysteresis is associated with both transformations, and the variation of the thermal hystereses of the magnetic and structural transformations with applied magnetic field is significantly different. Because of the differences between the hystereses loops of the two transformations, they merge only upon heating under a certain magnetic field.

  6. Critical current degradation in superconducting niobium-titanium alloys in external magnetic fields under loading

    International Nuclear Information System (INIS)

    Bojko, V.S.; Lazareva, M.B.; Starodubov, Ya.D.; Chernyj, O.V.; Gorbatenko, V.M.

    1992-01-01

    The effect of external magnetic fields on the stress at which the critical current starts to degrade (the degradation threshold σ 0 e ) under mechanical loads in superconducting Nb-Ti alloys is studied and a possible mechanism of realization of the effect observed is proposed.It is assumed that additional stresses on the transformation dislocation from the external magnetic fields are beneficial for the growth of martensite inclusions whose superconducting parameters (critical current density j k and critical temperature T k ) are lower then those in the initial material.The degradation threshold is studied experimentally in external magnetic fields H up to 7 T.The linear dependence σ 0 e (H) is observed.It is shown that external magnetic fields play an important role in the critical current degradation at the starting stages of deformation.This fact supports the assumption that the degradation of superconducting parameters under loading are due to the phenomenon of superelasticity,i.e. a reversible load-induced change in the martensite inclusions sizes rather than the reversible mechanical twinning.The results obtained are thought to be important to estimating superconducting solenoid stability in a wide range of magnetic fields

  7. Effect of Annealing in Magnetic Field on Ferromagnetic Nanoparticle Formation in Cu-Al-Mn Alloy with Induced Martensite Transformation.

    Science.gov (United States)

    Titenko, Anatoliy; Demchenko, Lesya

    2016-12-01

    The paper considers the influence of aging of high-temperature phase on subsequent martensitic transformation in Cu-Al-Mn alloy. The morphology of behavior of martensitic transformation as a result of alloy aging under annealing in a constant magnetic field with different sample orientation relatively to the field direction and without field was studied for direct control of the processes of martensite induction at cooling. Temperature dependences of electrical resistance, magnetic susceptibility, and magnetization, as well as field dependences of magnetization, and phase composition were found. The tendency to the oriented growth of precipitated ferromagnetic phase nanoparticles in a direction of applied field and to an increase of their volume fraction under thermal magnetic treatment of material that favors a reversibility of induced martensitic transformation is observed.

  8. Polymer stabilized Ni-Ag and Ni-Fe alloy nanoclusters: Structural and magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Kabir, L.; Mandal, A.R. [Department of Physics, Visva-Bharati, Santiniketan-731 235 (India); Mandal, S.K., E-mail: sk_mandal@hotmail.co [Department of Physics, Visva-Bharati, Santiniketan-731 235 (India)

    2010-04-15

    We report here the structural and magnetic behaviors of nickel-silver (Ni-Ag) and nickel-iron (Ni-Fe) nanoclusters stabilized with polymer (polypyrrole). High resolution transmission electron microscopy (HRTEM) indicates Ni-Ag nanoclusters to stabilize in core-shell configuration while that of Ni-Fe nanoclusters in a mixed type of geometry. Structural characterizations by X-ray diffraction (XRD) reveal the possibility of alloying in such bimetallic nanoclusters to some extent even at temperatures much lower than that of bulk alloying. Electron paramagnetic resonance (EPR) spectra clearly reveal two different absorption behaviors: one is ascribed to non-isolated Ni{sup 2+} clusters surrounded by either silver or iron giving rise to a broad signal, other (very narrow signal) being due to the isolated superparamagnetic Ni{sup 2+} clusters or bimetallic alloy nanoclusters. Results obtained for Ni-Ag and Ni-Fe nanoclusters have been further compared with the behavior exhibited by pure Ni nanoclusters in polypyrrole host. Temperature dependent studies (at 300 and 77 K) of EPR parameters, e.g. linewidth, g-value, line shape and signal intensity indicating the significant influence of surrounding paramagnetic silver or ferromagnetic iron within polymer host on the EPR spectra have been presented.

  9. Polymer stabilized Ni-Ag and Ni-Fe alloy nanoclusters: Structural and magnetic properties

    Science.gov (United States)

    Kabir, L.; Mandal, A. R.; Mandal, S. K.

    2010-04-01

    We report here the structural and magnetic behaviors of nickel-silver (Ni-Ag) and nickel-iron (Ni-Fe) nanoclusters stabilized with polymer (polypyrrole). High resolution transmission electron microscopy (HRTEM) indicates Ni-Ag nanoclusters to stabilize in core-shell configuration while that of Ni-Fe nanoclusters in a mixed type of geometry. Structural characterizations by X-ray diffraction (XRD) reveal the possibility of alloying in such bimetallic nanoclusters to some extent even at temperatures much lower than that of bulk alloying. Electron paramagnetic resonance (EPR) spectra clearly reveal two different absorption behaviors: one is ascribed to non-isolated Ni 2+ clusters surrounded by either silver or iron giving rise to a broad signal, other (very narrow signal) being due to the isolated superparamagnetic Ni 2+ clusters or bimetallic alloy nanoclusters. Results obtained for Ni-Ag and Ni-Fe nanoclusters have been further compared with the behavior exhibited by pure Ni nanoclusters in polypyrrole host. Temperature dependent studies (at 300 and 77 K) of EPR parameters, e.g. linewidth, g-value, line shape and signal intensity indicating the significant influence of surrounding paramagnetic silver or ferromagnetic iron within polymer host on the EPR spectra have been presented.

  10. Polymer stabilized Ni-Ag and Ni-Fe alloy nanoclusters: Structural and magnetic properties

    International Nuclear Information System (INIS)

    Kabir, L.; Mandal, A.R.; Mandal, S.K.

    2010-01-01

    We report here the structural and magnetic behaviors of nickel-silver (Ni-Ag) and nickel-iron (Ni-Fe) nanoclusters stabilized with polymer (polypyrrole). High resolution transmission electron microscopy (HRTEM) indicates Ni-Ag nanoclusters to stabilize in core-shell configuration while that of Ni-Fe nanoclusters in a mixed type of geometry. Structural characterizations by X-ray diffraction (XRD) reveal the possibility of alloying in such bimetallic nanoclusters to some extent even at temperatures much lower than that of bulk alloying. Electron paramagnetic resonance (EPR) spectra clearly reveal two different absorption behaviors: one is ascribed to non-isolated Ni 2+ clusters surrounded by either silver or iron giving rise to a broad signal, other (very narrow signal) being due to the isolated superparamagnetic Ni 2+ clusters or bimetallic alloy nanoclusters. Results obtained for Ni-Ag and Ni-Fe nanoclusters have been further compared with the behavior exhibited by pure Ni nanoclusters in polypyrrole host. Temperature dependent studies (at 300 and 77 K) of EPR parameters, e.g. linewidth, g-value, line shape and signal intensity indicating the significant influence of surrounding paramagnetic silver or ferromagnetic iron within polymer host on the EPR spectra have been presented.

  11. Linear arrangement of nano-scale magnetic particles formed in Cu-Fe-Ni alloys

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Sung, E-mail: k3201s@hotmail.co [Department of Materials Engineering (SEISAN), Yokohama National University, 79-5 Tokiwadai, Hodogayaku, Yokohama, 240-8501 (Japan); Takeda, Mahoto [Department of Materials Engineering (SEISAN), Yokohama National University, 79-5 Tokiwadai, Hodogayaku, Yokohama, 240-8501 (Japan); Takeguchi, Masaki [Advanced Electron Microscopy Group, National Institute for Materials Science (NIMS), Sakura 3-13, Tsukuba, 305-0047 (Japan); Bae, Dong-Sik [School of Nano and Advanced Materials Engineering, Changwon National University, Gyeongnam, 641-773 (Korea, Republic of)

    2010-04-30

    The structural evolution of nano-scale magnetic particles formed in Cu-Fe-Ni alloys on isothermal annealing at 878 K has been investigated by means of transmission electron microscopy (TEM), electron dispersive X-ray spectroscopy (EDS), electron energy-loss spectroscopy (EELS) and field-emission scanning electron microscopy (FE-SEM). Phase decomposition of Cu-Fe-Ni occurred after an as-quenched specimen received a short anneal, and nano-scale magnetic particles were formed randomly in the Cu-rich matrix. A striking feature that two or more nano-scale particles with a cubic shape were aligned linearly along <1,0,0> directions was observed, and the trend was more pronounced at later stages of the precipitation. Large numbers of <1,0,0> linear chains of precipitates extended in three dimensions in late stages of annealing.

  12. Magnetic properties of the UMn2-UFe2 and UMn2-UCO2 system alloys

    International Nuclear Information System (INIS)

    Meskhishvili, A.I.; Pletyushkin, V.A.; Slovyanskikh, V.K.; Chechernikov, V.I.; Shavishvili, T.M.

    1978-01-01

    The magnetic properties of compounds UMn 2 and UCo 2 , and solid solutions UMn 2 -UFe 2 and UMn 2 -UCo 2 have been examined. It has been established, that in substituting iron ions with manganese ions, the temperature of the ferromagnetic transformation of UFe 2 decreases, and within the region of 50 at.% UFe 2 the ferromagnetic ordering disappears. The Curie-Weiss law holds within a limited temperature range. In the solid solutions of two paramagnets UMn 2 and UCo 2 , which are independent of temperature, at a concentration of 45 to 50 at.% UCo 2 , the magnetic susceptibility and its dependence on temperature attain their maximum values. The results obtained are connected with the collectivization of d-, f-, and s-electrons of an alloy

  13. Heat Treatment of Iron-Carbon Alloys in a Magnetic Field (Phase 2)

    Energy Technology Data Exchange (ETDEWEB)

    Ludtka, Gerard Michael [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-11-01

    Thermomagnetic processing was shown to shift the phase transformation temperatures and therefore microstructural evolution in the high performance engine valve spring 9254 steel alloy by applying a high magnetic field during cooling. These effects would be anticipated to improve performance such as high cycle fatigue as demonstrated in prior projects. Thermomagnetic processing of gears and crank shafts was constrained by the size of the prototype equipment currently available at ORNL. However, the commercial procurement viability of production scale 9-Tesla, 16-inch diameter bore thermomagnetic processing equipment for truck idler gears up to ~11-inch diameter and potential crank shaft applications was shown, as multiple superconducting magnet manufacturing companies (in conjunction with an induction heat treating company, AjaxTOCCO Magnethermic) offered cryogen-free or cryocooler equipment designs to Cummins.

  14. Magnetic Properties of Nanocrystalline FexCu1-x Alloys Prepared by Ball Milling

    International Nuclear Information System (INIS)

    Yousif, A.; Bouziane, K.; Elzain, M. E.; Ren, X.; Berry, F. J.; Widatallah, H. M.; Al Rawas, A.; Gismelseed, A.; Al-Omari, I. A.

    2004-01-01

    X-ray diffraction, Moessbauer and magnetization measurements were used to study Fe x Cu 1-x alloys prepared by ball-milling. The X-ray data show the formation of a nanocrystalline Fe-Cu solid solution. The samples with x≥0.8 and x≤0.5 exhibit bcc or fcc phase, respectively. Both the bcc and fcc phases are principally ferromagnetic for x≥0.2, but the sample with x=0.1 remains paramagnetic down to 78 K. The influence of the local environment on the hyperfine parameters and the local magnetic moment are discussed using calculations based on the discrete-variational method in the local density approximation.

  15. Structure and magnetic properties of nanocrystalline Fe75Si25 powders prepared by mechanical alloying

    International Nuclear Information System (INIS)

    Kalita, M.P.C.; Perumal, A.; Srinivasan, A.

    2008-01-01

    Nanocrystalline Fe 75 Si 25 powders were prepared by mechanical alloying in a planetary ball mill. The evolution of the microstructure and magnetic properties during the milling process were studied by X-ray diffraction, scanning electron microscope and vibrating sample magnetometer measurements. The evolution of non-equilibrium solid solution Fe (Si) during milling was accompanied by refinement of crystallite size down to 10 nm and the introduction of high density of dislocations of the order of 10 17 m -2 . During the milling process, Fe sites get substituted by Si. This structural change and the resulting disorder are reflected in the lattice parameters and average magnetic moment of the powders milled for various time periods. A progressive increase of coercivity was also observed with increasing milling time. The increase of coercivity could be attributed to the introduction of dislocations and reduction of powder particle size as a function of milling time

  16. Influence of milling time on microstructure and magnetic properties of Fe{sub 80}P{sub 11}C{sub 9} alloy produced by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Taghvaei, A.H. [Department of Materials Science and Engineering, Shiraz University of Technology, Shiraz (Iran, Islamic Republic of); Ghajari, F., E-mail: fati.ghajari@gmail.com [Department of Materials Science and Engineering, Shiraz University, Shiraz (Iran, Islamic Republic of); Markó, D. [IFW Dresden, Institute for Complex Materials, Helmholtzstr. 20, 01069 Dresden (Germany); Prashanth, K.G. [IFW Dresden, Institute for Complex Materials, Helmholtzstr. 20, 01069 Dresden (Germany); Additive manufacturing Center, Sandvik AB, 81181 Sandviken (Sweden)

    2015-12-01

    Fe{sub 80}P{sub 11}C{sub 9} alloy with amorphous/nanocrytalline microstructure has been synthesized by mechanical alloying of the elemental powders. The microstructure, thermal behavior and morphology of the produced powders have been studied by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM), respectively. The crystallite size, lattice strain and fraction of the amorphous phase have been calculated by Rietveld refinement method. The results indicate that the powders microstructure consists of α-Fe(P,C) nanocrystals with an average diameter of 9 nm±1 nm dispersed in the amorphous matrix after 90 h of milling. Moreover, the fraction of amorphous phase initially increases up to 90 h of milling and then decreases after 120 h of milling, as a result of mechanical crystallization and formation of Fe{sub 2}P phase. The magnetic measurements show that while the saturation magnetization decreases continuously with the milling time, the coercivity exhibits a complicated trend. The correlation between microstructural changes and magnetic properties has been discussed in detail. - Highlights: • Glass formation was investigated in Fe{sub 80}P{sub 11}C{sub 9} by mechanical alloying. • Structural parameters were calculated by Rietveld refinement method. • Milling first increased and then decreased the fraction of amorphous phase. • Magnetic properties were significantly changed upon milling.

  17. Magnetic and structural properties of mechanically alloyed Tb0.257-xNdxFe0.743 alloys, with x = 0 and 0.257

    International Nuclear Information System (INIS)

    Rojas Martinez, Y.; Bustos Rodriguez, H.; Oyola Lozano, D.; Perez Alcazar, G. A.; Paz, J. C.

    2007-01-01

    The alloys between a transition metal and a rare earth present magnetic and magneto optical properties of exceptional interest for the production of magnetic devices for information storage. In this work we report the magnetic and structural properties, obtained by Moessbauer spectrometry (MS) and X-ray diffraction (XRD), of Tb 0.257-x Nd x Fe 0.743 alloys with x = 0 and 0.257 prepared by mechanical alloying during 12, 24 and 48 h, to study the influence of the milling time in their magnetic and structural properties. The X-rays results show for all the samples that the α and an amorphous phase are always present. The first decreases and the second increases with the increase of the milling time. Moessbauer results show that the amorphous phase in samples with Nd is ferromagnetic and appears as a hyperfine field distribution and a broad doublet, and that as the milling time increases the paramagnetic contribution increases. For samples with Tb the amorphous phase is paramagnetic and appears as a broad doublet which increases with the milling time and for 48 h milling it appears an additional broad singlet.

  18. Fabrication of magnetic nano liquid metal fluid through loading of Ni nanoparticles into gallium or its alloy

    Energy Technology Data Exchange (ETDEWEB)

    Xiong, Mingfeng; Gao, Yunxia [Key Lab of Cryogenics and Beijing Key Lab of CryoBiomedical Engineering, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190 (China); Liu, Jing, E-mail: jliu@mail.ipc.ac.cn [Key Lab of Cryogenics and Beijing Key Lab of CryoBiomedical Engineering, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190 (China); Department of Biomedical Engineering, School of Medicine, Tsinghua University, Beijing 100084 (China)

    2014-03-15

    In this study, Ni nanoparticles were loaded into the partially oxidized gallium and its alloys to fabricate desired magnetic nanofluid. It was disclosed that the Ni nanoparticles sharply increased the freezing temperature and latent heat of the obtained magnetic nano liquid metal fluid, while the melting process was less affected. For the gallium sample added with 10 vol% coated Ni particles, a hysteresis loop was observed and the magnetization intensity decreased with the increase of the temperature. The slope for the magnetization-temperature curve within 10–30 K was about 20 times of that from 40 K to 400 K. Further, the dynamic impact experiments of striking magnetic liquid metal droplets on the magnet revealed that the regurgitating of the leading edge of the liquid disk and the subsequent wave that often occurred in the gallium-indium droplets would disappear for the magnetic fluids case due to attraction force of the magnet. - Graphical abstract: High speed videos for the impact of striking GaIn{sub 24.5} based magnetic liquid metal droplets on a magnet plate. - Highlights: • A feasible way to fabricate magnetic nano liquid metal fluid was presented. • Ni nanoparticles sharply increased freezing temperature and latent heat of magnetic nanofluid. • A hysteresis loop phenomenon was observed for the magnetic nanofluid. • Temperature dependent magnetization spanning from 10 K to 400 K was measured. • Impact phenomena of striking magnetic droplets on magnet were disclosed.

  19. Phase-Field simulation of phase decomposition in Fe-Cr-Co alloy under an external magnetic field

    Science.gov (United States)

    Koyama, Toshiyuki; Onodera, Hidehiro

    2004-07-01

    Phase decomposition during isothermal aging of a Fe-Cr-Co ternary alloy under an external magnetic field is simulated based on the phase-field method. In this simulation, since the Gibbs energy available from the thermodynamic CALPHAD database of the equilibrium phase diagram is employed as a chemical free energy, the present calculation provides the quantitative microstructure changes directly linked to the phase diagram. The simulated microstructure evolution demonstrates that the lamella like microstructure elongated along the external magnetic field is evolved with the progress of aging. The morphological and temporal developments of the simulated microstructures are in good agreement with experimental results that have been obtained for this alloy system.

  20. Atomic disorder and the magnetic, electrical, and optical properties of a Co2CrAl Heusler alloy

    International Nuclear Information System (INIS)

    Svyazhin, A. D.; Shreder, E. I.; Voronin, V. I.; Berger, I. F.; Danilov, S. E.

    2013-01-01

    Two Co 2 CrAl alloy samples subjected to different heat treatment regimes are studied. An exact distribution of atoms over the sublattices in the samples is determined by X-ray diffraction and neutron diffraction methods. These data are used to perform ab initio density of states calculations and to calculate the magnetic moments of the samples in a coherent potential approximation. The calculated magnetic moments are compared to the experimental values. The effect of atomic ordering on the electronic structure near the Fermi level is analyzed using optical methods. The possible causes of the detected temperature dependence of the electrical resistivity, unusual for metallic alloys, are discussed.

  1. Microstructural and magnetic properties study of Fe–P rolled sheet alloys

    International Nuclear Information System (INIS)

    Jafari, S.; Beitollahi, A.; EftekhariYekta, B.; Kanada, Keiu; Ohkubo, T.; Gopalan, R.; Herzer, Giselher; Hono, K.

    2014-01-01

    In the work presented here, the soft magnetic properties of Fe 1−x P x (x=0.36, 0.7, 1.1 at%) rolled sheet alloys were investigated. In this respect, the as-rolled sheets were subjected to a two steps annealing processes; the first one between 800 and 1000 °C for 1 h referred as first stage annealing and the second one at lower temperatures (500 and 600 °C) for 30 min, referred as second step annealing. BH tracer measurements at 50 Hz showed that for all of the phosphorous containing alloys, in general, the magnitude of coercivity decreased by applying these two annealing steps compared to those of as-rolled samples. For all of the studied samples, the B 50 values measured at 50 Hz were in the range of 1.6–1.7 tesla (T). Samples having highest amount of phosphorous (1.1 at%) exhibited lower eddy current loss compared to the rest of the specimens due to the increased electrical resistivity. Besides, microstructural studies revealed that the prepared samples were free from Fe 3 P phase precipitation and the average grain size increased (∼three times) with increasing the phosphorous content giving rise to the decrease of hysteresis losses. Further, amongst the whole prepared samples, the alloy containing 1.1 at% P showed the lowest hysteresis loss (6.99 W/kg), eddy current loss (9.25 W/kg) as well as the highest magnetic induction (1.7 T) at 5000 A/M (B 50 ). - Highlights: • We have studied magnetic properties and microstructure of Fe 1−x P x rolled sheet alloys. • Increasing phosphorous content increases the B 50 from 1.65 to 1.70 T. • Increasing phosphorous content causes the decline of the eddy current loss. • The grain size increases about 3 times with increasing phosphorous concentration. • The hysteresis loss decreases with increasing the phosphorous content (88%)

  2. Microstructural and magnetic properties study of Fe–P rolled sheet alloys

    Energy Technology Data Exchange (ETDEWEB)

    Jafari, S. [Center of Excellence for Ceramics in Energy and Environment, School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran 16846-13114 (Iran, Islamic Republic of); Beitollahi, A., E-mail: beitolla@iust.ac.ir [Center of Excellence for Ceramics in Energy and Environment, School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran 16846-13114 (Iran, Islamic Republic of); EftekhariYekta, B. [Center of Excellence for Ceramics in Energy and Environment, School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran 16846-13114 (Iran, Islamic Republic of); Kanada, Keiu [Toyota Motor Corporation, Aichi Prefecture, Toyota (Japan); Ohkubo, T.; Gopalan, R. [Magnetic Materials Unit, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba 305-0047 (Japan); Herzer, Giselher [Vacuumschmelze GmBH, D-63450 Hanau (Germany); Hono, K. [Magnetic Materials Unit, National Institute for Materials Science, 1-2-1 Sengen, Tsukuba 305-0047 (Japan)

    2014-05-01

    In the work presented here, the soft magnetic properties of Fe{sub 1−x}P{sub x} (x=0.36, 0.7, 1.1 at%) rolled sheet alloys were investigated. In this respect, the as-rolled sheets were subjected to a two steps annealing processes; the first one between 800 and 1000 °C for 1 h referred as first stage annealing and the second one at lower temperatures (500 and 600 °C) for 30 min, referred as second step annealing. BH tracer measurements at 50 Hz showed that for all of the phosphorous containing alloys, in general, the magnitude of coercivity decreased by applying these two annealing steps compared to those of as-rolled samples. For all of the studied samples, the B{sub 50} values measured at 50 Hz were in the range of 1.6–1.7 tesla (T). Samples having highest amount of phosphorous (1.1 at%) exhibited lower eddy current loss compared to the rest of the specimens due to the increased electrical resistivity. Besides, microstructural studies revealed that the prepared samples were free from Fe{sub 3}P phase precipitation and the average grain size increased (∼three times) with increasing the phosphorous content giving rise to the decrease of hysteresis losses. Further, amongst the whole prepared samples, the alloy containing 1.1 at% P showed the lowest hysteresis loss (6.99 W/kg), eddy current loss (9.25 W/kg) as well as the highest magnetic induction (1.7 T) at 5000 A/M (B{sub 50}). - Highlights: • We have studied magnetic properties and microstructure of Fe{sub 1−x}P{sub x} rolled sheet alloys. • Increasing phosphorous content increases the B{sub 50} from 1.65 to 1.70 T. • Increasing phosphorous content causes the decline of the eddy current loss. • The grain size increases about 3 times with increasing phosphorous concentration. • The hysteresis loss decreases with increasing the phosphorous content (88%)

  3. Temperature-dependent rigidity and magnetism of polyamide 6 nanocomposites based on nanocrystalline Fe-Ni alloy of various geometries

    Directory of Open Access Journals (Sweden)

    M. A. A. Mohamed

    2016-10-01

    Full Text Available The focus of this study is to explore the potential use of Polyamide 6 nanocomposite reinforced with nanocrystalline (nc Fe20Ni80 alloy (Fe20Ni80/PA6 PNC in electromagnetic applications and provide understanding of how the alloy particle geometry is controlling the nanocomposite’s physical properties. Thermomechanical rigidity, room-temperature soft magnetic performance and thermal soft magnetic stability of Fe20Ni80/PA6 PNCs based on spherical-sea urchin alloy particles (UMB2-SU and necklace-like alloy chains (UMB2-NC have been investigated. Both PNCs have considerably superior bulk properties compared to neat PA6 and UMB2-SU exhibits the most remarkable overall performance. Morphological observations disclose two relevant phenomena: i improved dispersion and distribution of the SU alloy particles than the NC ones within PA6 matrix, leading to stronger filler-matrix interfacial interactions within the UMB2-SU as compared to the UMB2-NC and ii presence of constraint polymer regions in between alloy segments within the UMB2-SU that provide secondary reinforcing and soft magnetic mechanisms. Such phenomena along with the lower alloy crystallite size and PA6 γ-crystal type content within the UMB2-SU than in the UMB2-NC, are considered the main responsible factors for the distinctive performance of UMB2-SU. Overall, compared to various ferromagnetic nanocrystalline metallic materials, the research proposes the SU nc Fe20Ni80 alloy as a valuable nanofiller in polymers for electromagnetic applications.

  4. Investigation of (Fe,Co)NbB-Based Nanocrystalline Soft Magnetic Alloys by Lorentz Microscopy and Off-Axis Electron Holography.

    Science.gov (United States)

    Zheng, Changlin; Kirmse, Holm; Long, Jianguo; Laughlin, David E; McHenry, Michael E; Neumann, Wolfgang

    2015-04-01

    The relationship between microstructure and magnetic properties of a (Fe,Co)NbB-based nanocrystalline soft magnetic alloy was investigated by analytical transmission electron microscopy (TEM). The microstructures of (Fe0.5Co0.5)80Nb4B13Ge2Cu1 nanocrystalline alloys annealed at different temperatures were characterized by TEM and electron diffraction. The magnetic structures were analyzed by Lorentz microscopy and off-axis electron holography, including quantitative measurement of domain wall width, induction, and in situ magnetic domain imaging. The results indicate that the magnetic domain structure and particularly the dynamical magnetization behavior of the alloys strongly depend on the microstructure of the nanocrystalline alloys. Smaller grain size and random orientation of the fine particles decrease the magneto-crystalline anisotropy and suggests better soft magnetic properties which may be explained by the anisotropy model of Herzer.

  5. NdFeB alloy as a magnetic electrode material for lithium-ion batteries

    International Nuclear Information System (INIS)

    Zhang, J.; Shui, J.L.; Zhang, S.L.; Wei, X.; Xiang, Y.J.; Xie, S.; Zhu, C.F.; Chen, C.H.

    2005-01-01

    The search for a reliable indicator of state of charge and even the remaining energy of a lithium-ion cell is of great importance for various applications. This study was an exploratory effort to use magnetic susceptibility as the indicator. In this work, for the first time the change of ac susceptibility of cells was in situ monitored during charge-discharge process. A strong permanent magnetic material, NdFeB alloy, was investigated as an anode material for rechargeable lithium batteries. Both original and partially oxidized NdFeB powders were made into electrodes. Structural characterization was performed on the NdFeB electrodes by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis. An alloy (core)-oxide (shell) structure was found for those partially oxidized samples. The electrochemical cycling of cells made of the NdFeB electrodes against lithium was measured. The first lithium intercalation capacity of a treated NdFeB can be up to about 831 mAh/g, while a rather reversible capacity of up to 352 mAh/g can be obtained. With a specially designed cell, we were able to monitor in situ the change of relative ac susceptibility during charge and/or discharge steps. A clearly monotonous relationship is found between the ac susceptibility of a cell and its depth-of-discharge (DOD). A mechanism based on skin effect and eddy current change is proposed to explain this susceptibility versus DOD relationship

  6. NdFeB alloy as a magnetic electrode material for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, J. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China); Shui, J.L. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China); Zhang, S.L. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China); Wei, X. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China); Xiang, Y.J. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China); Xie, S. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China); Zhu, C.F. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China); Chen, C.H. [Department of Materials Science and Engineering, University of Science and Technology of China, Anhui Hefei 230026 (China)]. E-mail: cchchen@ustc.edu.cn

    2005-04-05

    The search for a reliable indicator of state of charge and even the remaining energy of a lithium-ion cell is of great importance for various applications. This study was an exploratory effort to use magnetic susceptibility as the indicator. In this work, for the first time the change of ac susceptibility of cells was in situ monitored during charge-discharge process. A strong permanent magnetic material, NdFeB alloy, was investigated as an anode material for rechargeable lithium batteries. Both original and partially oxidized NdFeB powders were made into electrodes. Structural characterization was performed on the NdFeB electrodes by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis. An alloy (core)-oxide (shell) structure was found for those partially oxidized samples. The electrochemical cycling of cells made of the NdFeB electrodes against lithium was measured. The first lithium intercalation capacity of a treated NdFeB can be up to about 831 mAh/g, while a rather reversible capacity of up to 352 mAh/g can be obtained. With a specially designed cell, we were able to monitor in situ the change of relative ac susceptibility during charge and/or discharge steps. A clearly monotonous relationship is found between the ac susceptibility of a cell and its depth-of-discharge (DOD). A mechanism based on skin effect and eddy current change is proposed to explain this susceptibility versus DOD relationship.

  7. Study of structural, electronic and magnetic properties of CoFeIn and Co2FeIn Heusler alloys

    International Nuclear Information System (INIS)

    El Amine Monir, M.; Khenata, R.; Baltache, H.; Murtaza, G.; Abu-Jafar, M.S.; Bouhemadou, A.; Bin Omran, S.

    2015-01-01

    The structural, electronic and magnetic properties of half-Heusler CoFeIn and full-Heusler Co 2 FeIn alloys have been investigated by using the state of the art full-potential linearized augmented plane wave (FP-LAPW) method. The exchange-correlation potential was treated with the generalized gradient approximation (PBE-GGA) for the calculation of the structural properties, whereas the PBE-GGA+U approximation (where U is the Hubbard Coulomb energy term) is applied for the computation of the electronic and magnetic properties in order to treat the “d” electrons. The structural properties have been calculated in the paramagnetic and ferromagnetic phases where we have found that both the CoFeIn and Co 2 FeIn alloys have a stable ferromagnetic phase. The obtained results of the spin-polarized band structure and the density of states show that the CoFeIn alloy is a metal and the Co 2 FeIn alloy has a complete half-metallic nature. Through the obtained values of the total spin magnetic moment, we conclude that in general, the Co 2 FeIn alloy is half-metallic ferromagnet material whereas the CoFeIn alloy has a metallic nature. - Highlights: • Based on DFT calculations, CoFeIn and Co2FeIn Heusler alloys were investigated. • The magnetic phase stability was determined from the total energy calculations. • Electronic properties reveal the metallic (half-metallic) nature for CoFeIn (Co2FeIn)

  8. Influence of thermal debinding on the final properties of Fe–Si soft magnetic alloys for metal injection molding (MIM)

    Energy Technology Data Exchange (ETDEWEB)

    Páez-Pavón, A.; Jiménez-Morales, A. [Dpto. Ciencia e Ing. de materiales e Ing. Química, Universidad Carlos III de Madrid, 28911 Leganés, Madrid (Spain); Santos, T.G. [UNIDEMI, Departamento de Engenharia Mecânica e Industrial, Faculdade de Ciências e Tecnologia, Universidade Nova de Lisboa, 2829-516 Caparica (Portugal); Quintino, L. [Instituto Superior Técnico, Universidade de Lisboa, 1049-001 Lisboa (Portugal); Torralba, J.M. [Dpto. Ciencia e Ing. de materiales e Ing. Química, Universidad Carlos III de Madrid, 28911 Leganés, Madrid (Spain)

    2016-10-15

    Metal injection molding (MIM) may be used to produce soft magnetic materials with optimal mechanical and magnetic properties. Unlike other techniques, MIM enables the production of complex and small Fe–Si alloy parts with silicon contents greater than 3% by weight. In MIM process development, it is critical to design a proper debinding cycle not only to ensure complete removal of the binder system but also to obtain improved properties in the final part. This work is a preliminary study on the production of Fe-3.8Si soft magnetic parts by MIM using pre-alloyed powders and a non-industrialized binder. Two different heating rates during thermal debinding were used to study their effect on the final properties of the part. The final properties of the sintered parts are related to thermal debinding. It has been demonstrated that the heating rate during thermal debinding has a strong influence on the final properties of Fe–Si soft magnetic alloys. - Highlights: • The properties of MIM Fe-Si alloy are influenced by the debinding heating rate. • The slow debinding led to a lower porosity, lower oxygen content and grain growth. • The magnetization of the sintered samples improved after a slow thermal debinding.

  9. The observation of resistivity change on the ultrasonic treated Fe-Cr ODS sinter alloy under magnetic field influence

    Science.gov (United States)

    Silalahi, Marzuki; Purwanto, Setyo; Mujamilah; Dimyati, Arbi

    2018-03-01

    About the observation of resistivity change on the ultrasonic treated Fe-Cr ODS sinter alloy under magnetic field influence. This paper reported about the observation of the resistivity change in the ultrasonic pre-treated Fe-Cr ODS sinter alloy under the influence of magnetic field at the Center for Science and Technology of Advanced Material, Nuclear Energy Agency of Indonesia. Fe-Cr ODS alloy were sinthesized by vacuum sintering of Fe- and Cr-powder dispersed Y2O3. However, before sintering the powder mixture was subjected to the irradiation process by ultrasonic for 50 hours at 20 kHz and then isostatic pressed up to 50.91 MPa to form a coin of 10 mm in diameter. LCR meassurement revealed the decreasing of resistivity about 3 times by increasing of applied magnetic field from 0 to 70 mT. In addition, VSM meassurement was performed on both as powder material and as sintered sample. The results showed increasing the magnetization with increasing magnetic field and the curve exhibits almost exact symmetry S-form with small hysterese indicating fast changing magnetization and demagnetization capability without energy loss. This opens strong speculations about the existence of magnetoresistant property of the material which is important for many application in field of sensors or electro magnetic valves.

  10. Toward Monte Carlo simulation of general cases of static muon spin relaxation in disordered magnetic materials: long-range magnetic order in alloys

    International Nuclear Information System (INIS)

    Noakes, D.R.

    2001-01-01

    Monte Carlo simulations of zero-field (ZF) muon spin relaxation (μSR) functions generated by long-range-ordered states with disorder are presented, for the completely static limit. Understanding of this is necessary before Monte Carlo simulation of the effect of short-range magnetic ordering on μSR in spin glasses can begin. Alloy disorder, controlled by the magnetic ion concentration parameter f m , and partial ordering of each moment, controlled by the order parameter f o , are considered. Qualitatively different behavior is seen depending on whether the dense moment, perfect-order limit ( f m =1, f o =1) field at the muon site is non-zero, or cancels (as can happen in high-symmetry materials). Around the edges of the two-dimensional ( f m ,f o ) parameter space, four limit cases with qualitatively different behavior are identified: (A) f o →0, the random frozen spin glass for arbitrary magnetic ion concentration; (B) f o →1, nearly perfect magnetic ordering in a alloy of arbitrary magnetic ion concentration; (C) f m →0, magnetic order developing (as f o increases) in a dilute magnetic alloy; (D) f m →1, magnetic order developing (as f o increases) in a dense magnetic material. Case A was discussed in a previous publication. The results for case D answer the question of how the Gaussian Kubo-Toyabe relaxation function for perfect disorder develops into an oscillating function as magnetic order develops in a material. Case C indicates that the effects of magnetic ordering in the dilute moment limit produce only subtle effects in ZF-μSR spectra that would be difficult to unambiguously identify as due to ordering in a real-world experiment. Case B generates complicated multi-frequency behavior

  11. Magnetic domain structure and magnetically-induced reorientation in Ni–Mn–Ga magnetic shape memory alloy

    Czech Academy of Sciences Publication Activity Database

    Heczko, Oleg; Bradshaw, V.

    2017-01-01

    Roč. 131, č. 4 (2017), s. 1063-1065 ISSN 0587-4246 R&D Projects: GA ČR GA15-00262S Institutional support: RVO:68378271 Keywords : magnetic shape memory effect * magnetic domain structure * 3D visualization * domain mirroring Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 0.469, year: 2016

  12. First-principles calculation on dilute magnetic alloys in zinc blend crystal structure

    International Nuclear Information System (INIS)

    Ullah, Hamid; Inayat, Kalsoom; Khan, S.A; Mohammad, S.; Ali, A.; Alahmed, Z.A.; Reshak, A.H.

    2015-01-01

    Ab-initio calculations are performed to investigate the structural, electronic and magnetic properties of spin-polarized diluted magnetic alloys in zinc blende structure. The first-principles study is carried out on Mn doped III–V semiconductors. The calculated band structures, electronic properties and magnetic properties of Ga 1−x Mn x X (X=P, As) compounds reveal that Ga 0.75 Mn 0.25 P is half metallic turned to be metallic with increasing x to 0.5 and 0.75, whereas substitute P by As cause to maintain the half-metallicity nature in both of Ga 0.75 Mn 0.25 As and Ga 0.5 Mn 0.5 As and tune Ga 0.25 Mn 0.75 As to be metallic. Calculated total magnetic moments and the robustness of half-metallicity of Ga 0.75 Mn 0.25 P, Ga 0.75 Mn 0.25 As and Ga 0.5 Mn 0.5 As with respect to the variation in lattice parameters are also discussed. The predicted theoretical evidence shows that some Mn-doped III–V semiconductors can be effectively used in spintronic devices

  13. Effect of milling on the magnetic properties of Al–Mn obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Betancourt, Mirna; Silva, Pedro; Gonzalez, Gema

    2012-01-01

    Highlights: ► Al–42 at.% Mn transforms to α-Mn(Al) by mechanical milling after 5 h of milling. ► Transformation to nano β-Mn is reached after 50 h of milling with 6 nm grain size. ► Milling strongly affects magnetic behavior. - Abstract: Al–Mn powders were prepared to obtain the compound Mn 42 Al 58 by mechanical alloying. The powders were milled during different periods (1 h, 5 h, 11.5 h, 15 h, 20 h and 50 h) using a SPEX 8000 mixer mill in nitrogen atmosphere. The materials were characterized by X-ray diffraction (XRD) and magnetic properties at room temperature, using a vibrating sample magnetometer (VSM). XRD shows partial transformation to α-Mn after only 1 h of milling and a mixture of α-Mn and β-Mn after 11.5 h of milling and further milling resulted in transformation to β-Mn phase with a grain size of 6 nm after 50 h. The change in magnetic properties with milling time is quite dramatic, from a ferromagnetic behavior for α-Mn(Al) to paramagnetic after 11.5 h of milling and showing again ferromagnetic behavior, with a strong increase of magnetization values of 5.5 emu/g, after 50 h of milling with formation of β-Mn(Al).

  14. First-principles calculation on dilute magnetic alloys in zinc blend crystal structure

    Energy Technology Data Exchange (ETDEWEB)

    Ullah, Hamid, E-mail: hamidullah@yahoo.com [Department of Physics, Government Post Graduate Jahanzeb College, Saidu Sharif Swat (Pakistan); Inayat, Kalsoom [Department of Physics, Government Post Graduate Jahanzeb College, Saidu Sharif Swat (Pakistan); Khan, S.A; Mohammad, S. [Department of Physics, Materials Modeling Laboratory, Hazara University, Mansehra 21300 (Pakistan); Ali, A. [Department of Advanced Materials Science & Engineering, Hanseo University, Seosan-si, Chungnam-do 356-706 (Korea, Republic of); Alahmed, Z.A. [Department of Physics and Astronomy, King Saud University, Riyadh 11451 (Saudi Arabia); Reshak, A.H. [New Technologies-Research Center, University of West Bohemia, Univerzitni 8, 306 14 Pilsen (Czech Republic); Center of Excellence Geopolymer and Green Technology, School of Material Engineering, University Malaysia Perlis, 01007 Kangar, Perlis (Malaysia)

    2015-07-01

    Ab-initio calculations are performed to investigate the structural, electronic and magnetic properties of spin-polarized diluted magnetic alloys in zinc blende structure. The first-principles study is carried out on Mn doped III–V semiconductors. The calculated band structures, electronic properties and magnetic properties of Ga{sub 1−x}Mn{sub x}X (X=P, As) compounds reveal that Ga{sub 0.75}Mn{sub 0.25}P is half metallic turned to be metallic with increasing x to 0.5 and 0.75, whereas substitute P by As cause to maintain the half-metallicity nature in both of Ga{sub 0.75}Mn{sub 0.25}As and Ga{sub 0.5}Mn{sub 0.5}As and tune Ga{sub 0.25}Mn{sub 0.75}As to be metallic. Calculated total magnetic moments and the robustness of half-metallicity of Ga{sub 0.75}Mn{sub 0.25}P, Ga{sub 0.75}Mn{sub 0.25}As and Ga{sub 0.5}Mn{sub 0.5}As with respect to the variation in lattice parameters are also discussed. The predicted theoretical evidence shows that some Mn-doped III–V semiconductors can be effectively used in spintronic devices.

  15. Growth dependent magnetization reversal in Co2MnAl full Heusler alloy thin films

    Science.gov (United States)

    Barwal, Vineet; Husain, Sajid; Behera, Nilamani; Goyat, Ekta; Chaudhary, Sujeet

    2018-02-01

    Angular dependent magnetization reversal has been investigated in Co2MnAl (CMA) full Heusler alloy thin films grown on Si(100) at different growth temperatures (Ts) by DC-magnetron sputtering. An M -shaped curve is observed in the in-plane angular (0°-360°) dependent coercivity (ADC) by magneto-optical Kerr effect measurements. The dependence of the magnetization reversal on Ts is investigated in detail to bring out the structure-property correlation with regards to ADC in these polycrystalline CMA thin films. This magnetization reversal ( M -shaped ADC behavior) is well described by the two-phase model, which is a combination of Kondorsky (domain wall motion) and Stoner Wohlfarth (coherent rotation) models. In this model, magnetization reversal starts with depinning of domain walls, with their gradual displacement explained by the Kondorsky model, and at a higher field (when the domain walls merge), the system follows coherent rotation before reaching its saturation following the Stoner Wohlfarth model. Further, the analysis of angular dependent squareness ratio (Mr/Ms) indicates that our films clearly exhibited twofold uniaxial anisotropy, which is related to self-steering effect arising due to the obliquely incident flux during the film-growth.

  16. Co2FeSi Heusler alloy prepared by arc melting and planar flow casting methods: microstructure and magnetism.

    Czech Academy of Sciences Publication Activity Database

    Titov, Andrii; Životský, O.; Hendrych, A.; Janičkovič, D.; Buršík, Jiří; Jirásková, Yvonna

    2017-01-01

    Roč. 131, č. 4 (2017), s. 654-656 ISSN 0587-4246. [CSMAG 2016 - Czech and Slovak Conference on Magnetism /16./. Košice, 13.06.2016-17.06.2016] Institutional support: RVO:68081723 Keywords : Heusler alloy * Surface morphology * Magnetic properties * Arc melting * Planar flow casting Subject RIV: BM - Solid Matter Physics ; Magnetism; BM - Solid Matter Physics ; Magnetism (UFM-A) OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 0.469, year: 2016

  17. Model for field-induced reorientation strain in magnetic shape memory alloy with tensile and compressive loads

    International Nuclear Information System (INIS)

    Zhu Yuping; Dui Guansuo

    2008-01-01

    A model based on the micromechanical and the thermodynamic theory is presented for field-induced martensite reorientation in magnetic shape memory alloy (MSMA) single crystals. The influence of variants morphology and the material property to constitutive behavior is considered. The nonlinear and hysteretic strain and magnetization response of MSMA are investigated for two main loading cases, namely the magnetic field-induced reorientation of variants under constant compressive stress and tensile stress. The predicted results have shown that increasing tensile loading reduces the required field for actuation, while increasing compressive loads result in the required magnetic field growing considerably. It is helpful to design the intelligent composite with MSMA fibers

  18. Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

    Directory of Open Access Journals (Sweden)

    Xingjie Jia

    2018-05-01

    Full Text Available Addition of minor Mn effectively improves the amorphous-forming ability and thermal stability of the Fe85Si2B8P4Cu1 alloy. With increasing the Mn content from 0 to 3 at.%, the critical thickness for amorphous formation and onset temperature of the primary crystallization increase from 14 μm and 659 K to 27 μm and 668 K, respectively. The fine nanocrystalline structure with α-Fe grains in size (D of < 20 nm was obtained for the annealed amorphous alloys, which show excellent soft magnetic properties. The alloying of Mn reduces the coercivity (Hc by decreasing the D value and widens the optimum annealing temperature range for obtaining low Hc, although the saturation magnetic flux density (Bs is decreased slightly. The Fe83Mn2Si2B8P4Cu1 nanocrystalline alloy possesses fine structure with a D of ∼17.5 nm, and exhibits a high Bs of ∼1.75 T and a low Hc of ∼5.9 A/m. The mechanism related to the alloying effects on the structure and magnetic properties was discussed in term of the crystallization activation energy.

  19. Structure and soft magnetic properties of Fe-Si-B-P-Cu nanocrystalline alloys with minor Mn addition

    Science.gov (United States)

    Jia, Xingjie; Li, Yanhui; Wu, Licheng; Zhang, Wei

    2018-05-01

    Addition of minor Mn effectively improves the amorphous-forming ability and thermal stability of the Fe85Si2B8P4Cu1 alloy. With increasing the Mn content from 0 to 3 at.%, the critical thickness for amorphous formation and onset temperature of the primary crystallization increase from 14 μm and 659 K to 27 μm and 668 K, respectively. The fine nanocrystalline structure with α-Fe grains in size (D) of < 20 nm was obtained for the annealed amorphous alloys, which show excellent soft magnetic properties. The alloying of Mn reduces the coercivity (Hc) by decreasing the D value and widens the optimum annealing temperature range for obtaining low Hc, although the saturation magnetic flux density (Bs) is decreased slightly. The Fe83Mn2Si2B8P4Cu1 nanocrystalline alloy possesses fine structure with a D of ˜17.5 nm, and exhibits a high Bs of ˜1.75 T and a low Hc of ˜5.9 A/m. The mechanism related to the alloying effects on the structure and magnetic properties was discussed in term of the crystallization activation energy.

  20. Investigation of structural and magnetic properties of rapidly-solidified iron-silicon alloys at ambient and elevated temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Jayaraman, T. V.; Meka, V. M.; Jiang, X.; Overman, N. R.; Doyle, J.; Shield, J. E.; Mathaudhu, S. N.

    2018-04-01

    In this work, we investigated the ambient temperature structural properties (~300 K) and the ambient and high temperature (up to 900 K) direct current (DC) magnetic properties of melt-spun Fe-x wt.% Si (x = 3, 5, & 8) alloys. The wheel surface speeds selected for the study were 30 m/s and 40 m/s. The thickness, width, lattice parameter, saturation magnetization (MS), and intrinsic coercivity (HCI) of the melt spun ribbons are presented and compared with data in the literature. The ribbons produced at the lower wheel surface speed (30 m/s) were continuous having relatively uniform edges compared to the ribbons produced at the higher wheel surface speed. The thickness and the width of the melt-spun ribbons ranged between ~15-60 μm and 500-800 μm, respectively. The x-ray diffraction spectra of the melt-spun ribbons indicated the presence of disordered α-phase, irrespective of the composition, and the wheel-surface speed. The lattice parameter decreased gradually as a function of increasing silicon content from ~0.2862 nm (Fe-3 wt.% Si) to ~0.2847 nm (Fe-8 wt.% Si). Wheel surface speed was not shown to have a significant effect on the magnetization, but primarily impacted the ribbon structure. A decreasing trend in the saturation magnetization was observed as a function of increased silicon content. The intrinsic coercivity of the melt-spun alloys ranged between ~50 to 200 A/m. Elevated temperature evaluation of the magnetization in the case of Fe-3 & 5 wt.% Si alloy ribbons was distinctly different from the Fe-8 wt.% Si alloy ribbons. The curves of the as-prepared Fe-3 wt.% Si and Fe-5 wt.% Si alloy ribbons were irreversible while that of Fe-8 wt.% Si was reversible. The MS for any of the combinations of wheel surface speed and composition decreased monotonically with the increase in temperature (from 300 – 900 K). The percentage decrease in MS from 300 K to 900 K for the Fe-3 wt.% Si and Fe-5 wt.% Si alloys was ~19-22 %, while the percentage decrease in the same

  1. Posterior magnetic effect on the pure and doped Fe-Ni alloy under neutron irradiation

    International Nuclear Information System (INIS)

    Ferreira, Iris

    1974-01-01

    Polycrystalline specimens of unirradiated and neutron irradiated Fe-Ni alloys have been studied in the temperature range RT - 500 deg C. The study was carried out in pure (50-50) as well as in Si, A1, Cr and Mo doped samples. Initial magnetic permeability was measured in unirradiated (virgin)and in neutron irradiated samples, during isochronal and linear thermal treatments. The main results are: a magnetic After Effect (MAE) is detected in the temperature range 370 deg C - Tc, where Tc is the Curie Temperature. In this range an activation energy of 3.2 ± 0.2 eV was determined for the Cr doped Fe-Ni alloy (impurity content: 0.1%); measurements made in the irradiated samples, during a linear temperature treatment, show the existence of several MAE zones in the temperature range RT - Tc. The isochronal annealing experiments show that these MAE zones are accompanied by a decrease in the room temperature value of the magnetic permeability, for zones between RT and a certain temperature T 1 . Above this range there is a steep increase in the room temperature permeability. Activation energies were determined for pure and Mo-doped (0.1%) samples for the first MAE zone (50 deg C - 120 deg C). The values obtained 1.25 - 0.08 eV and 1.42 ± 0.09 eV, respectively; the impurity - doped samples show a different behaviour relative to the pure ones: samples with low impurity content (0.1% and 0.5% of Si, Al or Mo) present an enhancement in the amplitude and also an overlapping of the diffusion stages. On the other hand, samples with higher impurity content (2 and 4% of Mo) show a decrease in these amplitudes. (author)

  2. Phase transformation and magnetic anisotropy of an iron-palladium ferromagnetic shape-memory alloy

    International Nuclear Information System (INIS)

    Cui, J.; Shield, T.W.; James, R.D.

    2004-01-01

    Martensitic phase transformations in an Fe 7 Pd 3 alloy were studied using various experimental techniques: visual observation, differential scanning calorimeter (DSC) measurements and X-ray diffraction. Magnetic measurements on this alloy were made using a vibrating sample magnetometer (VSM) and a Susceptibility Kappa bridge. The VSM measurements were made with the sample in a compression fixture to bias the martensite phase to a single variant. Both X-ray and DSC measurements show that the FCC-FCT transformation is a weak first-order thermoelastic transition. The average lattice parameters are a=3.822±0.001 A and c=3.630±0.001 A for the FCT martensite, and a 0 =3.756±0.001 A for the FCC austenite. The latent heat of the FCC-FCT transformation is 10.79±0.01 J/cm 3 . A Susceptibility Kappa bridge measurement determined the Curie temperature to be 450 deg. C. The saturation magnetization from VSM data is m s =1220±10 emu/cm 3 at -20 deg. C for the martensite and m s =1080±10 emu/cm 3 at 60 deg. C for the austenite. The easy axes of a single variant of FCT martensite are the [1 0 0] and [0 1 0] directions (the a-axes of the FCT lattice) and the [0 0 1] direction (FCT c-axis) is the hard direction. The cubic magnetic anisotropy constant K 1 is -5±2x10 3 erg/cm 3 for the austenite at 60 deg. C, and the tetragonal anisotropy constant K 1 +K 2 is 3.41 ± 0.02 x 10 5 erg/cm 3 for the martensite at a temperature of -20 deg. C and under 8 MPa of compressive stress in the [0 0 1] direction

  3. Magneto-optical detection of the relaxation dynamics of alloy nanoparticles with a high-stability magnetic circular dichroism setup

    International Nuclear Information System (INIS)

    Cavigli, L.; Julian Fernandez, C. de; Gatteschi, D.; Gurioli, M.; Sangregorio, C.; Mattei, G.; Mazzoldi, P.; Bogani, L.

    2007-01-01

    We present a versatile high-stability and high-sensitivity magneto-optical setup that allows transmission and reflection measurements at high fields and low temperatures. We apply the technique to measure the decay in time of the magnetization of highly monodisperse 3.3nm Co 33 Ni 67 alloy nanoparticles embedded in a silica host. We demonstrate the possibility of observing the dynamics of the magnetization over a macroscopic timescale in dilute samples, where other techniques are unavailable

  4. Phase composition, structure and magnetic behaviour of low neodymium rapid-quenched Nd-Fe-B alloys

    Czech Academy of Sciences Publication Activity Database

    Ćosović, V.; Žák, Tomáš; Talijan, N.; Grujić, A.; Stajić-Trošić, J.

    2008-01-01

    Roč. 456, 1-2 (2008), s. 251-256 ISSN 0925-8388 R&D Projects: GA MŠk 1M0512 Institutional research plan: CEZ:AV0Z20410507 Keywords : multiphase Nd(Pr)-Fe-B alloys * rapid solidification * magnetic measurements * Mossbauer spectroscopy * X-ray diffraction * Nanocrystalline composite Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.510, year: 2008

  5. Magneto-optical detection of the relaxation dynamics of alloy nanoparticles with a high-stability magnetic circular dichroism setup

    Science.gov (United States)

    Cavigli, L.; de Julián Fernández, C.; Gatteschi, D.; Gurioli, M.; Sangregorio, C.; Mattei, G.; Mazzoldi, P.; Bogani, L.

    2007-09-01

    We present a versatile high-stability and high-sensitivity magneto-optical setup that allows transmission and reflection measurements at high fields and low temperatures. We apply the technique to measure the decay in time of the magnetization of highly monodisperse 3.3 nm Co33Ni67 alloy nanoparticles embedded in a silica host. We demonstrate the possibility of observing the dynamics of the magnetization over a macroscopic timescale in dilute samples, where other techniques are unavailable.

  6. Anomalous magnetic ordering in DyxPr1-x alloys

    DEFF Research Database (Denmark)

    Clegg, P.S.; Cowley, R.A.; Goff, J.P.

    2000-01-01

    Epitaxial thin-films of DyxPr1-x alloys have been studied using neutron diffraction and magnetization measurements. The crystal structure changes from HCP to Sm type to DHCP as x decreases; each crystal phase has different magnetic behaviour. Surprisingly, long-range order is suppressed in the DH...... allays, a possible explanation is outlined. (C) 2000 Elsevier Science B.V. All rights reserved....

  7. Magnetic and magnetocaloric properties of martensitic Ni2Mn1.4Sn0.6 Heusler alloy

    International Nuclear Information System (INIS)

    Chernenko, Volodymyr A.; Barandiarán, Jose M.; Rodriguez Fernández, Jesus; Rojas, Daniel P.; Gutiérrez, Jon; Lázpita, Patricia; Orue, Iñaki

    2012-01-01

    The evolutions of magnetic properties at low temperatures and the influence of magnetic field on the temperature dependence of specific heat in martensitic Ni 2 Mn 1.4 Sn 0.6 Heusler alloy are studied. The frequency-dependent blocking temperature and considerable exchange bias below it are measured in the martensitic phase. From the analysis of the specific heat curves under magnetic field, a large inverse magnetocaloric effect manifested as the magnetic field induced rise of isothermal magnetic entropy and/or magnetic field induced adiabatic temperature decrease in the vicinity of the reverse magnetostructural transformation and a significant value of the conventional magnetocaloric effect at the Curie temperature are obtained. The Debye temperature and electronic coefficient equal to Θ D =310±2 K and γ= 16.6±0.3 mJ/K 2 mol, respectively, do not depend on the magnetic field.

  8. Magnetic properties of melt-spun Nd-rich NdFeB alloys with Dy and Ga substitutions

    International Nuclear Information System (INIS)

    Harland, C.L.; Davies, H.A.

    1998-01-01

    The results of a systematic investigation of the effects of Dy and Ga additions on the magnetic properties of a Nd-rich NdFeB alloy are presented and discussed. Particular attention is given to the effect of increasing Dy substitutions on the coercivity of the Nd 18 Fe 76 B 6 alloy. Substitution of 30% of the Nd by Dy resulted in a coercivity increase from 1590 to 3290 kA m -1 . However, contrary to previous suggestions, substitution of 1% of the Fe by Ga was found to have only a small influence on the magnetic properties of all the alloys in the compositional series (Nd 100-x Dy x ) 18 Fe 76 B 6 (x=0-30). (orig.)

  9. Magnetic spin configuration in Fe{sub 50}Pt{sub 50-x}Rh{sub x} alloys

    Energy Technology Data Exchange (ETDEWEB)

    Fenske, J.; Lott, D.; Schreyer, A. [GKSS Research Centre (Germany); Mankey, G.J. [University of Alabama, MINT Center (United States); Schmidt, W.; Schmalzl, K. [Juelich Research Centre (Germany); Tartakowskaya, E. [Institute for Magnetism, National Ukrainian Accademy of Science (Ukraine)

    2010-07-01

    FePt-based alloys are typically the material of choice for magnetic information storage media. The high magnetic moment of Fe gives a large magnetization and the large atomic number of Pt results in a high magnetic anisotropy. This combination enables the written bits to be smaller than ever before. One way to control the magnetic properties in these materials is through the introduction of a third element into the crystal matrix e.g. Rh. When Rh is added to replace Pt in the equiatomic alloy, new magnetic phases emerge. Bulk samples of Fe{sub 50}Pt{sub 50-x}Rh{sub x} studied by magnetization measurements refer to three different phase transitions with increasing temperature: (I) An antiferromagnetic (AF)-paramagnetic (PM) transition for 30magnetic field. By the use of polarized and unpolarized neutron diffraction we could develop a detailed model of the magnetic spin structure in these thin films.

  10. The Magnetization Reversal Processes Of Bulk (Nd, Y-(Fe, Co-B Alloy In The As-Quenched State

    Directory of Open Access Journals (Sweden)

    Dośpiał M.

    2015-09-01

    Full Text Available The magnetization reversal processes of bulk Fe64Co5Nd6Y6B19 alloy in the as-quenched state have been investigated. From the analysis of the initial magnetization curve and differential susceptibility versus an internal magnetic field it was deduced, that the main mechanism of magnetization reversal process is the pinning of domain walls at the grain’s boundaries of the Nd2Fe14B phase. Basing on the dependence of the reversible magnetization component as a function of magnetic field it was found that reversible rotation of a magnetic moment vector and motion of domain walls in multi-domain grains result in high initial values of the reversible component. The presence of at least two maxima on differential susceptibility of irreversible magnetization component in function of magnetic field imply existence of few pinning sites of domain walls in Fe64Co5Nd6Y6B19 alloy. The dominant interactions between particles have been determined on the basis of the Wohlfarth dependence. Such a behavior of Wohlfarth’s plot implies that the dominant interaction between grains becomes short range exchange interactions.

  11. Ultrathin metallized PBI paper

    Science.gov (United States)

    Chenevey, E. C.

    1978-01-01

    A study to determine the feasibility of preparing ultrathin papers with a target weight of 3.5 g/m squared from polybenzimidazole (PBI) fibrids was undertaken. Small hand sheets of target weight were fabricated. They were light brown, low density materials with sufficient strength to be readily handleable. Characterization of these sheets included strength, fold endurance, thermal gravimetric analysis in air and nitrogen and photomicrographs. Two different batches of PBI fibrids were studied and differences in fabrication performance were noted. In neither case could target weight papers be prepared using conventional paper making techniques.

  12. Structural analysis and magnetic properties of solid solutions of Co–Cr system obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Betancourt-Cantera, J.A.; Sánchez-De Jesús, F.; Bolarín-Miró, A.M.; Betancourt, I.; Torres-Villaseñor, G.

    2014-01-01

    In this paper, a systematic study on the structural and magnetic properties of Co 100−x Cr x alloys (0 1−x Cr x (0 2 /kg) for the Co 90 Cr 10 , which decreases with the increasing of the Cr content up to x=80, as a consequence of the dilution effect of the magnetic moment which is caused by the Cr content and by the competition between ferromagnetic and antiferromagnetic exchange interactions. The coercivity increases up to 34 kA/m (435 Oe) for Co 40 Cr 60 . For Cr rich compositions, it is observed an important decrease reaching 21 kA/m (272 Oe) for Co 10 Cr 90, it is related to the grain size and the structural change. Besides, the magnetic anisotropy constant was determined for each composition. Magnetic thermogravimetric analysis allowed to obtain Curie temperatures corresponding to the formation of hcp-Co(Cr) and fcc-Co(Cr) solid solutions. - Highlights: • Mechanical alloying (MA) induces the formation of solid solutions of Co–Cr system in non-equilibrium. • We report the crystal structure and the magnetic behavior of Co–Cr alloys produced by MA. • MA improves the magnetic properties of Co–Cr system

  13. Investigation of finely dispersed grind of magnetically hard SmCo5 and Nd2Fe14B alloys

    International Nuclear Information System (INIS)

    Balalaev, Yu.N.; Kosobudskij, I.D.

    2000-01-01

    Possibility of preparation of finely dispersed powders of SmCo 5 and Nd 2 Fe 14 B allays investigated and comparison of different types of grinding processes is conducted. Results of comparison of the processes in vibrational mills and disintegrators permit to conclude that density and structure of grindable materials effect on the rate and quality of grinding of magnetically hard alloys [ru

  14. Fabrication of a Textured Non-Magnetic Ni-12at.%V Alloy Substrate for Coated Conductors

    DEFF Research Database (Denmark)

    Gao, M. M.; Grivel, Jean-Claude; Suo, H. L.

    2011-01-01

    Ni-12at.%V alloy is a promising candidate for non-magnetic cube textured metallic substrates used for high temperature coated conductors. In this work, a textured Ni-12at.%V substrate has been fabricated by powder metallurgy route. After cold rolling and recrystallization annealing, a cube texture...

  15. Magnetic properties of ball-milled Fe0.6Mn0.1Al0.3 alloys

    International Nuclear Information System (INIS)

    Rebolledo, A.F.; Romero, J.J.; Cuadrado, R.; Gonzalez, J.M.; Pigazo, F.; Palomares, F.J.; Medina, M.H.; Perez Alcazar, G.A.

    2007-01-01

    The FeMnAl-disordered alloy system exhibits, depending on the composition and the temperature, a rich variety of magnetic phases including the occurrence of ferromagnetism, antiferromagnetism, paramagnetism and spin-glass and reentrant spin glass behaviors. These latter phases result from the presence of atomic disorder and magnetic dilution and from the competing exchange interactions taking place between an Fe atom and its Mn and Fe first neighbors. The use of mechanical alloying in order to prepare these alloys is specially interesting since it allows to introduce in a progressive way large amounts of disorder. In this work, we describe the evolution with the milling time of the temperature dependence of the magnetic properties of mechanically alloyed Fe 0.6 Mn 0.1 Al 0.3 samples. The materials were prepared in a planetary ball mill using a balls-to-powder mass ratio of 15:1 and pure (99.95 at%) Fe, Mn and Al powders for times up to 19 h. The X-rays diffraction (XRD) spectra show the coexistence of three phases at short milling times. For milling times over 6 h, only the FeMnAl ternary alloy BCC phase is observed. Moesbauer spectroscopy reveals the complete formation of the FeMnAl alloy after 9 h milling time. The magnetic characterization showed that all the samples were ferromagnetic at room temperature with coercivities decreasing from 105 Oe (3 h milled sample) down to 5 Oe in the case of the sample milled for 19 h

  16. Magnetic features of Fe-Cr-Co alloys with tailoring chromium content fabricated by spark plasma sintering

    Energy Technology Data Exchange (ETDEWEB)

    Rastabi, Reza Amini; Ghasemi, Ali, E-mail: ali13912001@yahoo.com; Tavoosi, Majid; Ramazani, Mazaher

    2017-03-15

    Structural and magnetic characterization of Fe-Cr-Co alloys during milling, annealing and consolidation processes was the goal of this study. In this regards, different powder mixtures of Fe{sub 80−x}Cr{sub x}Co{sub 20} (15≤x≤35) were mechanically milled in a planetary ball mill and then were consolidated by spark plasma sintering (SPS). The produced samples were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). According to achieved results, the structure of as-milled samples in different compositions consists of single α phase solid solution with coercivity and saturation of magnetization in the range of 110–200 Oe and 150–220 emu/g, respectively. The magnetic properties of consolidated samples depend on the kinds of formed precipitates in microstructure and the maximum values of coercive force and saturation of magnetization obtained in Fe{sub 55}Cr{sub 25}Co{sub 20} magnetic (with single α phase) alloy were 107 Oe and Ms 172 emu/g, respectively. In fact, the formation of non-magnetic σ and γ phases has a destructive effect on magnetic properties of consolidated samples with higher Cr content. Since such magnet requires less cobalt, and contains similar magnetic feature with superior ductility compare to the AlNiCo 5, it could be considered as a promising candidate for employing instead of AlNiCo 5. - Highlights: • Milled samples consist of single phase α-solid solution. • Saturation of magnetization of Fe{sub 65}Cr{sub 15}Co{sub 20} reached to 172 emu/g. • Fe{sub 65}Cr{sub 15}Co{sub 20} alloy is the suitable composition fabricated by SPS.

  17. Magnetic features of Fe-Cr-Co alloys with tailoring chromium content fabricated by spark plasma sintering

    International Nuclear Information System (INIS)

    Rastabi, Reza Amini; Ghasemi, Ali; Tavoosi, Majid; Ramazani, Mazaher

    2017-01-01

    Structural and magnetic characterization of Fe-Cr-Co alloys during milling, annealing and consolidation processes was the goal of this study. In this regards, different powder mixtures of Fe 80−x Cr x Co 20 (15≤x≤35) were mechanically milled in a planetary ball mill and then were consolidated by spark plasma sintering (SPS). The produced samples were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). According to achieved results, the structure of as-milled samples in different compositions consists of single α phase solid solution with coercivity and saturation of magnetization in the range of 110–200 Oe and 150–220 emu/g, respectively. The magnetic properties of consolidated samples depend on the kinds of formed precipitates in microstructure and the maximum values of coercive force and saturation of magnetization obtained in Fe 55 Cr 25 Co 20 magnetic (with single α phase) alloy were 107 Oe and Ms 172 emu/g, respectively. In fact, the formation of non-magnetic σ and γ phases has a destructive effect on magnetic properties of consolidated samples with higher Cr content. Since such magnet requires less cobalt, and contains similar magnetic feature with superior ductility compare to the AlNiCo 5, it could be considered as a promising candidate for employing instead of AlNiCo 5. - Highlights: • Milled samples consist of single phase α-solid solution. • Saturation of magnetization of Fe 65 Cr 15 Co 20 reached to 172 emu/g. • Fe 65 Cr 15 Co 20 alloy is the suitable composition fabricated by SPS.

  18. Influence of strain and polycrystalline ordering on magnetic properties of high moment rare earth metals and alloys

    International Nuclear Information System (INIS)

    Scheunert, G; Ward, C; Hendren, W R; Bowman, R M; Lapicki, A A; Hardeman, R; Mooney, M; Gubbins, M

    2014-01-01

    Despite being the most suitable candidates for solenoid pole pieces in state-of-the-art superconductor-based electromagnets, the intrinsic magnetic properties of heavy rare earth metals and their alloys have gained comparatively little attention. With the potential of integration in micro and nanoscale devices, thin films of Gd, Dy, Tb, DyGd and DyTb were plasma-sputtered and investigated for their in-plane magnetic properties, with an emphasis on magnetization versus temperature profiles. Based on crystal structure analysis of the polycrystalline rare earth films, which consist of a low magnetic moment fcc layer at the seed interface topped with a higher moment hcp layer, an experimental protocol is introduced which allows the direct magnetic analysis of the individual layers. In line with the general trend of heavy lanthanides, the saturation magnetization was found to drop with increasing unit cell size. In situ annealed rare earth films exceeded the saturation magnetization of a high-moment Fe 65 Co 35 reference film in the cryogenic temperature regime, proving their potential for pole piece applications; however as-deposited rare earth films were found completely unsuitable. In agreement with theoretical predictions, sufficiently strained crystal phases of Tb and Dy did not exhibit an incommensurate magnetic order, unlike their single-crystal counterparts which have a helical phase. DyGd and DyTb alloys followed the trends of the elemental rare earth metals in terms of crystal structure and magnetic properties. Inter-rare-earth alloys hence present a desirable blend of saturation magnetization and operating temperature. (paper)

  19. Magnetic ageing study of high and medium permeability nanocrystalline FeSiCuNbB alloys

    Energy Technology Data Exchange (ETDEWEB)

    Lekdim, Atef, E-mail: atef.lekdim@univ-lyon1.fr; Morel, Laurent; Raulet, Marie-Ange

    2017-04-15

    increasing the energy efficiency is one of the most important issues in modern power electronic systems. In aircraft applications, the energy efficiency must be associated with a maximum reduction of mass and volume, so a high components compactness. A consequence from this compactness is the increase of operating temperature. Thus, the magnetic materials used in these applications, have to work at high temperature. It raises the question of the thermal ageing problem. The reliability of these components operating at this condition becomes a real problem which deserves serious interest. Our work takes part in this context by studying the magnetic material thermal ageing. The nanocrystalline materials are getting more and more used in power electronic applications. Main advantages of nanocrystalline materials compared to ferrite are: high saturation flux density of almost 1.25 T and low dynamic losses for low and medium frequencies. The nanocrystalline Fe{sub 73.5}Cu{sub 1}Nb{sub 3}Si{sub 15.5}B{sub 7} alloys have been chosen in our aging study. This study is based on monitoring the magnetic characteristics for several continuous thermal ageing (100, 150, 200 and 240 °C). An important experimental work of magnetic characterization is being done following a specific monitoring protocol. Elsewhere, X-Ray Diffraction and magnetostriction measurements were carried out to support the study of the anisotropy energies evolution with ageing. This latter is discussed in this paper to explain and give hypothesis about the ageing phenomena. - Highlights: • The magnetic ageing of the nanocrystalline materials is related to their annealing. • The degradations with ageing are not related to a change of the grain size diameter. • The amount of anisotropies introduced with ageing depends just on ageing conditions.

  20. Structural, magnetic, and mechanical properties of electrodeposited cobalt–tungsten alloys: Intrinsic and extrinsic interdependencies

    International Nuclear Information System (INIS)

    Tsyntsaru, N.; Cesiulis, H.; Pellicer, E.; Celis, J.-P.; Sort, J.

    2013-01-01

    The mapping of structural, magnetic, and mechanical properties of Co–W coatings galvanostatically electrodeposited from a citrate–borate bath is investigated. The intrinsic characteristics of the coatings, such as crystallite size or tungsten content are correlated with the extrinsic growth parameters, such as pH, complexes distribution, and current density. The increase in pH from 5 to 8 results in an increase of the W content in the deposits from 2 at.% up to 36 at.% in a controlled way, and it correlates with an increase in concentration of W(VI) complexes in the bath. The crystallite size estimated from XRD patterns, decreases from 39 to 5 nm with increasing W content from 3 to 25 at.% respectively. The obtained coatings show highly tunable mechanical and magnetic properties. The hardness increases with W content from ∼3 GPa up to ∼13 GPa. A semi-hard ferromagnetic behavior with a coercivity of ∼470 Oe along the perpendicular-to-plane direction is observed for Co–W alloys containing small amounts of W in the range of ∼2–3 at.%. At higher tungsten contents the coatings are magnetically softer, and the electrodeposits become non-ferromagnetic beyond ∼30 at.% W. Because of this combination of physical properties, electrodeposited Co–W coatings may become suitable materials for multi-scale technologies

  1. Structural, transport, magnetic, magnetocaloric properties and critical analysis of Ni-Co-Mn-Ga Heusler alloys

    Science.gov (United States)

    Arumugam, S.; Devarajan, U.; Esakki Muthu, S.; Singh, Sanjay; Thiyagarajan, R.; Raja, M. Manivel; Rama Rao, N. V.; Banerjee, Alok

    2017-11-01

    In this work, we have investigated structural, transport, magnetic, magnetocaloric (MC) properties and critical exponents analysis of the (Ni2.1-xCox)Mn0.9 Ga (x = 0, 0.04, 0.12 and 0.2) Heusler alloys. For all compositions, cubic austenite (A) phase with metallic character is observed at room temperature (RT). With increasing of Co content, magnitude of resistivity decreases, whereas residual resistivity (ρ0) and electron scattering factor (A) increases linearly. Magnetic measurements exhibit that ferromagnetic (FM) Curie temperature (TCA) increases towards RT by increasing Co concentration. All samples show conventional MC and maximum magnetic entropy change (ΔSMpeak) of -2.8 Jkg-1 K-1 is observed for x = 0.12 at 147 K under 5 T. Further, hysteresis is observed between cooling and warming cycles around FM-PM (TCA) transition in x = 0, 0.04 samples, which suggests that first order nature of transition. However, there is no hysteresis across TCA for x = 0.12 and 0.2 samples suggesting second-order nature of the transition. The critical exponents are calculated for x = 0.12 sample around TCA using Arrott plot and Kouvel-Fisher method, the estimated critical exponents are found closer to the mean-field model reveals the long range ferromagnetic ordering in this composition.

  2. Thickness dependencies of structural and magnetic properties of cubic and tetragonal Heusler alloy bilayer films

    Science.gov (United States)

    Ranjbar, R.; Suzuki, K. Z.; Sugihara, A.; Ando, Y.; Miyazaki, T.; Mizukami, S.

    2017-07-01

    The thickness dependencies of the structural and magnetic properties for bilayers of cubic Co-based Heusler alloys (CCHAs: Co2FeAl (CFA), Co2FeSi (CFS), Co2MnAl (CMA), and Co2MnSi (CMS)) and D022-MnGa were investigated. Epitaxy of the B2 structure of CCHAs on a MnGa film was achieved; the smallest thickness with the B2 structure was found for 3-nm-thick CMS and CFS. The interfacial exchange coupling (Jex) was antiferromagnetic (AFM) for all of the CCHAs/MnGa bilayers except for unannealed CFA/MnGa samples. A critical thickness (tcrit) at which perpendicular magnetization appears of approximately 4-10 nm for the CMA/MnGa and CMS/MnGa bilayers was observed, whereas this thickness was 1-3 nm for the CFA/MnGa and CFS/MnGa films. The critical thickness for different CCHAs materials is discussed in terms of saturation magnetization (Ms) and the Jex .

  3. Microstructure and composition in rapidly quenched NdFeB-based hard magnet alloys

    International Nuclear Information System (INIS)

    Nguyen, T.D.; Krishnan, K.M.; Lewis, L.H.; Zhu, Y.; Welch, D.O.

    1996-01-01

    A detailed study of the microstructure and composition in hot-pressed (MQ-2) and die-upset (MQ-3) magnet alloys based on the Nd 2 Fe 14 B composition, utilizing high resolution and analytical transmission electron microscopy, is reported. The initial magnetic properties of the two samples show different behaviors, which are attributed to the difference in the anisotropy of the grain structure and the grain boundaries. The hot-pressed sample shows faceted grains of the 2-14-1 phase, while die-upset sample shows plate-like grains, together with larger equiaxed grains that contain a speckling of precipitates in the grain interior. The grain structure and composition remain rather similar in the two samples. The grain boundary phase averages ∼1 endash approx-gt 10 nm in width. The thicker grain boundaries are Nd-rich, while the thinner grain boundaries in the hot-pressed sample exhibit an Fe-rich composition near that of the NdFe 3 phase. Nd-rich phases are found at the grain boundary junctions of both samples, with the Nd:Fe ratio near 7:3 in the die-upset sample, and up to 3:2 in the hot-pressed sample. The significance of the microstructure and the grain boundary phases on the magnetic behavior in the two samples is discussed. copyright 1996 American Institute of Physics

  4. Hysteresis Curve Fitting Optimization of Magnetic Controlled Shape Memory Alloy Actuator

    Directory of Open Access Journals (Sweden)

    Fuquan Tu

    2016-11-01

    Full Text Available As a new actuating material, magnetic controlled shape memory alloys (MSMAs have excellent characteristics such as a large output strain, fast response, and high energy density. These excellent characteristics are very attractive for precision positioning systems. However, the availability of MSMAs in practical precision positioning is poor, caused by weak repeatability under a certain stimulus. This problem results from the error of a large magnetic hysteresis in an external magnetic field. A suitable hysteresis modelling method can reduce the error and improve the accuracy of the MSMA actuator. After analyzing the original hysteresis modelling methods, three kinds of hysteresis modelling methods are proposed: least squares method, back propagation (BP artificial neural network, and BP artificial neural network based on genetic algorithms. Comparing the accuracy and convergence rate of three kinds of hysteresis modelling methods, the results show that the convergence rate of least squares method is the fastest, and the convergence accuracy of BP artificial neural networks based on genetic algorithms is the highest.

  5. Ultrathin (Nanocellulose Paper

    Science.gov (United States)

    Wu, Jingda; Lin, Lih Y.

    2017-03-01

    Conventional approaches to flexible optoelectronic devices typically require depositing the active materials on external substrates. This is mostly due to the weak bonding between individual molecules or nanocrystals in the active materials, which prevents sustaining a freestanding thin film. Herein we demonstrate an ultrathin freestanding ZnO quantum dot (QD) active layer with nanocellulose structuring, and its corresponding device fabrication method to achieve substrate-free flexible optoelectronic devices. The ultrathin ZnO QD-nanocellulose composite is obtained by hydrogel transfer printing and solvent-exchange processes to overcome the water capillary force which is detrimental to achieving freestanding thin films. We achieved an active nanocellulose paper with ~550 nm thickness, and >91% transparency in the visible wavelength range. The film retains the photoconductive and photoluminescent properties of ZnO QDs and is applied towards substrate-free Schottky photodetector applications. The device has an overall thickness of ~670 nm, which is the thinnest freestanding optoelectronic device to date, to the best of our knowledge, and functions as a self-powered visible-blind ultraviolet photodetector. This platform can be readily applied to other nano materials as well as other optoelectronic device applications.

  6. HDDR in Sm-Co alloys - a new method for magnetic hardening of Sm-Co permanent magnets

    Energy Technology Data Exchange (ETDEWEB)

    Kubis, M.; Handstein, A.; Gebel, B.; Mueller, K.-H.; Schultz, L. [Institut fuer Festkoerper- und Werkstofforschung Dresden e.V. (Germany). Inst. fuer Metallische Werkstoffe; Gutfleisch, O. [Institut fuer Festkoerper- und Werkstofforschung Dresden e.V. (Germany). Inst. fuer Metallische Werkstoffe]|[Birmingham Univ. (United Kingdom). School of Metallurgy and Materials

    1998-07-01

    Investigations on the hydrogen absorption behavior of different Sm-Co alloys with 1:5 and 2:17 structure by differential scanning calorimetry (DSC) at enhanced hydrogen pressures between 1 MPa and 7 MPa indicated different hydrogen absorption events. X-ray diffraction (XRD) studies and microstructural investigations showed clearly the disproportionation of the Sm-Co phases into Sm hydride and Co or Co-rich phases for hydrogen pressures above 0.5 MPa. The favourable effect of high hydrogen pressures can be explained in terms of a decrease of the free enthalpy of the samarium hydride for increasing hydrogen pressures. Additionally, Sm-Co alloys of both types were reactively milled under hydrogen at enhanced temperatures. The reactively milled powders showed again the products of the disproportionation reaction. A recombination of Sm-Co phases by removing the hydrogen in a second heat treatment was successful for both methods. Investigations of the magnetic properties showed coercivities {mu}{sub OJ}H{sub C} of up to 2.1 T for high pressure HDDR powders of SmCo{sub 5} material, demonstrating clearly the positive effect of the hydrogen treatment on the coercivity. The reactively milled powders showed for recombination temperatures {<=}700 C a remanence enhancement which could be attributed to the exchange coupling of the nanoscaled grains. A maximum coercivity {mu}{sub OJ}H{sub C} of 3.7 T was achieved for SmCo{sub 5} and a maximum energy product (BH){sub max} of 82 kJ/m{sup 3} was measured for an Sm-rich Sm{sub 2}Co{sub 17} sample. (orig.)

  7. HDDR in Sm-Co alloys - a new method for magnetic hardening of Sm-Co permanent magnets

    International Nuclear Information System (INIS)

    Kubis, M.; Handstein, A.; Gebel, B.; Mueller, K.-H.; Schultz, L.; Gutfleisch, O.; Birmingham Univ.

    1998-01-01

    Investigations on the hydrogen absorption behavior of different Sm-Co alloys with 1:5 and 2:17 structure by differential scanning calorimetry (DSC) at enhanced hydrogen pressures between 1 MPa and 7 MPa indicated different hydrogen absorption events. X-ray diffraction (XRD) studies and microstructural investigations showed clearly the disproportionation of the Sm-Co phases into Sm hydride and Co or Co-rich phases for hydrogen pressures above 0.5 MPa. The favourable effect of high hydrogen pressures can be explained in terms of a decrease of the free enthalpy of the samarium hydride for increasing hydrogen pressures. Additionally, Sm-Co alloys of both types were reactively milled under hydrogen at enhanced temperatures. The reactively milled powders showed again the products of the disproportionation reaction. A recombination of Sm-Co phases by removing the hydrogen in a second heat treatment was successful for both methods. Investigations of the magnetic properties showed coercivities μ OJ H C of up to 2.1 T for high pressure HDDR powders of SmCo 5 material, demonstrating clearly the positive effect of the hydrogen treatment on the coercivity. The reactively milled powders showed for recombination temperatures ≤700 C a remanence enhancement which could be attributed to the exchange coupling of the nanoscaled grains. A maximum coercivity μ OJ H C of 3.7 T was achieved for SmCo 5 and a maximum energy product (BH) max of 82 kJ/m 3 was measured for an Sm-rich Sm 2 Co 17 sample. (orig.)

  8. Westendorf effect in the magnet alloy Nd-Dy-Fe-Co-B

    International Nuclear Information System (INIS)

    Piskorskij, V.P.; Valeev, R.A.; Sychev, I.V.

    2006-01-01

    Sintered magnets of the composition as follows, at. %: (Nd 0.6 Dy 0.4 ) 15 (Fe 1-x Co x ) rest Al 1 B 8 , are under study. It is revealed that the course of coercive force dependence on the temperature of heat treatment varies with a cobalt content increase (within a range of 0.19 - 0.26). The dependence of coercive force on heat treatment temperature for the alloys studied has a pronounced minimum at 700 deg C which is known as a Westendorf effect. This effect is taken to be due to the presence of R(Fe, Co) 4 B phase where R is the sum of REM [ru

  9. Investigation of non-magnetic alloys for the suppression of tritium permeation. Final report

    International Nuclear Information System (INIS)

    1980-07-01

    This report describes a small (300 man hour) literature survey relating to the suppression of tritium loss by permeation through the walls of fusion reactors. The program was based on prior in-house Thermacore work to suppress hydrogen permeation into high temperature (800 0 C) heat pipes. The Thermacore approach involves selection of a steel with a small (.5 to 5%) aluminum content. The aluminum is diffused to the surface and oxidized. The present work was aimed at identification of alloys which might combine low tritium permeation with other properties desired in fusion reactor vessels, heat exchangers, lithium-handling plumbing and other components likely to contain tritium. These properties include low radiation damage, low magnetic permeability, high temperature strength, and compatibility with potential heat transfer and blanket materials. The work consisted of two tasks: Problem Definition and Literature Search and Analysis

  10. Compositional optimization for nanocrystalline hard magnetic MRE–Fe–B–Zr alloys via modifying RE and B contents

    Energy Technology Data Exchange (ETDEWEB)

    Qian, D.Y.; Hussain, M.; Zheng, Z.G.; Zhong, X.C. [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); Gao, X.X. [State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China); Liu, Z.W., E-mail: zwliu@scut.edu.cn [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China)

    2015-06-15

    To reduce the rare earth content and maintain good magnetic properties for NdFeB based alloys, the effects of RE and B contents on the micro-structure and magnetic properties of nanocrystalline MRE{sub 11−y}Fe{sub 79.5}B{sub 8+y}Zr{sub 1.5} (MRE=Nd{sub 0.8}(Dy{sub 0.5}Y{sub 0.5}){sub 0.2}, y=0–3) alloys have been investigated. Increasing B concentration leads to the appearance and increase of soft magnetic Fe{sub 3}B phase and reduced grain size. With decreasing MRE and increasing B concentrations, the coercivity decreased from 1159.8 kA/m for y=0 to 619.0 kA/m for y=3. The saturation magnetization and remanence increased with B content until y=2 then decreases. The B content also has effects on the exchange coupling, microstructure and thermal stability. While comparing MRE{sub 10}Fe{sub 82.5}B{sub 6}Zr{sub 1.5} alloy with MRE{sub 11−y}Fe{sub 79.5}B{sub 8+y}Zr{sub 1.5} (y=1 and 2) alloys, the alloy with 9 at% MRE can achieve similar magnetic properties as that with 10 at% MRE. The magnetic properties with coercivity of 792.2 kA/m, (BH){sub max} of 128 kJ/m{sup 3} and good thermal stability have been obtained for MRE{sub 9}Fe{sub 79.5}B{sub 10}Zr{sub 1.5} alloy. - Highlights: • Nanocomposite NdFeB composition is optimized to reduce RE from 10 to 9 at.%. • Increasing B content benefits microstructure, exchange coupling, thermal stability. • Alloy with 9% RE has H{sub c}=792kA/m, (BH){sub max}=128kJ/m{sup 3} and low temperature coefficients.

  11. Surface modification and its role in the preparation of FeSi gradient alloys with good magnetic property and ductility

    Science.gov (United States)

    Yu, Haiyuan; Bi, Xiaofang

    2018-04-01

    Realization of the effective Si penetration at a lower processing temperature is a challenge, but of significance in reducing the strict requirements for the equipment and realizing cost-cutting in production. In this work, we have modified the surface microstructure of Fe-3 wt%Si alloy by using surface mechanical attrition treatment. The modified surface microstructure is characteristic of nanocrystalline, which is found to significantly enhance the efficiency of subsequent Si penetration into the alloy, and successively leading to the decrease of penetration temperature up to 200 °C. As a consequence, the Si gradient distribution across thickness can be readily controlled by changing penetration time, and FeSi alloys with various gradients are prepared by chemical vapor deposition along with subsequent annealing process. The dependence of magnetic and mechanical properties on Si gradient for demonstrates that the increase of Si gradient reduces core losses, especially at higher frequencies, and meanwhile improves ductility of FeSi alloys as well. The mechanism underlying the effect of Si gradient is clarified by combining magnetostriction measurement and domain structure observations. This work provides a facile and effective way for achieving gradient FeSi alloys with good magnetic property and ductility.

  12. Effect of boron addition to the hard magnetic bulk Nd60Fe30Al10 amorphous alloy

    International Nuclear Information System (INIS)

    Kong, H.Z.; Li, Y.; Ding, J.

    2000-01-01

    A detailed study of the effect of boron addition to crystallinity, magnetic properties and thermal properties was carried out for alloys Nd 60-x Fe 30 Al 10 B x with x=0, 1, 3 and 5 produced by copper mold chill casting and melt-spinning. The cast rods of alloys Nd 60-x Fe 30 Al 10 B x were largely amorphous. Remanence up to 0.154 T and coercivity up to 355 kA/m were observed, which were higher than those of the bulk amorphous Nd 60 Fe 30 Al 10 rod of the same diameter. A step in hysteresis loop was observed for the hard magnetic cast rod and ribbon melt-spun at a low speed of 5 m/s of the alloys with boron addition. Consistent increase in the amplitude of the step and magnetic field (H) at which the step was observed as the boron content increased. A single magnetic phase with low coercivity was observed for fully amorphous ribbon melt-spun at high speed of 30 m/s. Full crystallization due to heat treatment resulted in transition of hard magnetic amorphous phase of Nd 55 Fe 30 Al 10 B 5 cast rod to paramagnetic crystalline phases. TEM results of the as-cast rods illustrated the existence of numerous minute Nd-crystallites in amorphous matrix

  13. Martensitic transition near room temperature and the temperature- and magnetic-field-induced multifunctional properties of Ni49CuMn34In16 alloy

    Science.gov (United States)

    Sharma, V. K.; Chattopadhyay, M. K.; Khandelwal, A.; Roy, S. B.

    2010-11-01

    A near room-temperature martensitic transition is observed in the ferromagnetic austenite state of Ni50Mn34In16 alloy with 2% Cu substitution at the Ni site. Application of magnetic field in the martensite state induces a reverse martensitic transition in this alloy. dc magnetization, magnetoresistance and strain measurements in this alloy reveal that associated with this martensitic transition there exist a large magnetocaloric effect, a large magnetoresitance and a magnetic-field temperature-induced strain. This NiMnIn alloy system thus is an example of an emerging class of magnetic materials whose physical properties can be tuned by suitable chemical substitutions, to achieve magnetic-field and temperature-induced multifunctional properties at and around room temperature

  14. Effect of crystalline electric fields and long-range magnetic order on superconductivity in rare earth alloys and compounds

    International Nuclear Information System (INIS)

    McCallum, R.W.

    1977-01-01

    The behavior of rare earth ions in a superconducting matrix has been studied in two distinct regimes. First, the effects of crystal field splitting of the 4f levels of a magnetic rare earth ion in the alloy system (LaPr)Sn 3 were investigated in the limit of low Pr 3+ concentration. In this system the rare earth impurity ions occupy random La sites in the crystal lattice. Second, the interaction of long-range magnetic order and superconductivity was explored in the ternary rare earth molybdenum chalcogenide systems. In these compounds the rare earth ions occupy periodic lattice sites in contrast to the random distribution of magnetic ions in dilute impurity alloy systems such as (LaPr)Sn 3

  15. Structural, magnetic and transport studies of Mn0.8Cr0.2CoGe alloy

    Science.gov (United States)

    Das, S. C.; Dutta, P.; Pramanick, S.; Chatterjee, S.

    2018-04-01

    Different physical and functional properties of Mn0.8Cr0.2CoGe alloy has been investigated through structural, magnetic and electrical transport measurements. Substitution of Cr for Mn results significant decrease in both structural and magnetic transition temperature and brings them well below the room temperature. A reasonable amount of conventional magnetocaloric effect (ΔS˜ - 2.22 J/kg-K for magnetic field (H) changing from 0 to 50 kOe) with large relative cooling power (251.7 J/kg for H changing from 0 to 50 kOe) has also been observed around the region of transition. On thermal cycling through the structural transition, noticeable training effect is found to be associated with the resistivity of the alloy.

  16. Fracture toughness and flexural strength of Sm(Co,Fe,Cu,Zr){sub 7-8} magnetic alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ren, Libo. E-mail: ren@me.udel.edu; Hadjipanayis, George C.; Parvizi-Majidi, Azar

    2003-02-01

    This paper presents the results of a parametric investigation of the strength and fracture toughness of Sm{sub 2}Co{sub 17} type permanent magnets in the Sm(Co,Fe,Cu,Zr){sub 7-8} family of alloys. The strength and fracture toughness of the as-received materials were characterized as a function of temperature, loading direction, and magnetization. Since these magnets are candidates for applications with service temperatures up to 450 deg. C, the effect of thermal exposure on the mechanical properties was determined by characterizing the properties after a thermal treatment of 40 h at 450 deg. C00.

  17. Fracture toughness and flexural strength of Sm(Co,Fe,Cu,Zr)7-8 magnetic alloys

    International Nuclear Information System (INIS)

    Ren, Libo.; Hadjipanayis, George C.; Parvizi-Majidi, Azar

    2003-01-01

    This paper presents the results of a parametric investigation of the strength and fracture toughness of Sm 2 Co 17 type permanent magnets in the Sm(Co,Fe,Cu,Zr) 7-8 family of alloys. The strength and fracture toughness of the as-received materials were characterized as a function of temperature, loading direction, and magnetization. Since these magnets are candidates for applications with service temperatures up to 450 deg. C, the effect of thermal exposure on the mechanical properties was determined by characterizing the properties after a thermal treatment of 40 h at 450 deg. C

  18. Magnetic and Mössbauer studies of amorphous Fe 72- xY xHo 8B 20 alloys

    Science.gov (United States)

    Krishnan, R.; Driouch, L.; Lassri, H.; Dumond, Y.; Ajan, Antony; Shringi, S. N.; Prasad, Shiva

    1996-11-01

    We have carried out magnetic and Mössbauer studies of amorphous Fe 72- xY xHo 8B 20 alloys. The Fe moment decreases with the addition of Y and a magnetic compensation occurs at 4 K for x = 16. The temperature and field dependences of the magnetization have been interpreted using the mean field theory and Chudnovsky's model, respectively. These analyses yield some interesting parameters such as the random anisotropy, the exchange interactions JFe-Fe, JFe-Ho, etc. The Mössbauer studies show that the average hyperfine field decreases linearly with the addition of Y, in accordance with the decrease in the Fe moment.

  19. Effect of the low magnetic field on the electrodeposition of Co{sub x}Ni{sub 100−x} alloys

    Energy Technology Data Exchange (ETDEWEB)

    Olvera, S. [Instituto Politécnico Nacional, ESIQIE, Departamento de Ingeniería en Metalurgia y Materiales, 07738 México, D.F., México (Mexico); Universidad Autónoma de Madrid, Facultad de Ciencias, Departamento de Química-Física Aplicada, 28049 Madrid (Spain); Arce Estrada, E.M. [Instituto Politécnico Nacional, ESIQIE, Departamento de Ingeniería en Metalurgia y Materiales, 07738 México, D.F., México (Mexico); Sanchez-Marcos, J. [Universidad Autónoma de Madrid, Facultad de Ciencias, Departamento de Química-Física Aplicada, 28049 Madrid (Spain); Palomares, F.J.; Vazquez, L. [Instituto de Ciencia de Materiales de Madrid, ICMM-CSIC, Cantoblanco, 28049 Madrid (Spain); Herrasti, P., E-mail: pilar.herrasti@uam.es [Universidad Autónoma de Madrid, Facultad de Ciencias, Departamento de Química-Física Aplicada, 28049 Madrid (Spain)

    2015-07-15

    Magnetic, chemical and structural properties of electrosynthesized Co{sub x}Ni{sub 100−x} have been studied. The electrodeposition has been conducted both in the presence and absence of a low magnetic field. The application of a perpendicular magnetic field during the synthesis modified slightly the morphology of the alloys. These changes depend more on the film composition than on the applied field, as demonstrated by AFM images. In the absence of magnetic field, the Co{sub x}Ni{sub 100−x} film grows along the (200) direction. However, when the magnetic field was applied, a preferential orientation along the (111) direction was observed. No important magnetic changes are induced by the presence of the magnetic field during the growth. Based on X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray spectroscopy (EDX) experiments, the chemical composition of the films was preserved during preparation regardless of whether or not magnetic field is applied. There has been observed an increase in deposition rate in the presence of field even at these low magnetic fields. - Highlights: • CoNi alloys were electrosynthesized in the absence and presence of a low magnetic field. • Application of a magnetic field produced an orientation in the (111) plane of the alloy. • An external field changes the voltammetric curves reducing the energy required for the alloy formation. • The composition and magnetic properties were constant in the absence and presence of magnetic field.

  20. The effect of Mn and B on the magnetic and structural properties of nanostructured Fe60Al40 alloys produced by mechanical alloying.

    Science.gov (United States)

    Rico, M M; Alcázar, G A Pérez; Zamora, L E; González, C; Greneche, J M

    2008-06-01

    The effect of Mn and B on the magnetic and structural properties of nanostructured samples of the Fe60Al40 system, prepared by mechanical alloying, was studied by 57Fe Mössbauer spectrometry, X-ray diffraction and magnetic measurements. In the case of the Fe(60-x)Mn(x)Al40 system, 24 h milling time is required to achieve the BCC ternary phase. Different magnetic structures are observed according to the temperature and the Mn content for alloys milled during 48 h: ferromagnetic, antiferromagnetic, spin-glass, reentrant spin-glass and superparamagnetic behavior. They result from the bond randomness behaviour induced by the atomic disorder introduced by the MA process and from the competitive interactions of the Fe-Fe ferromagnetic interactions and the Mn-Mn and Fe-Mn antiferromagnetic interactions and finally the presence of Al atoms acting as dilutors. When B is added in the Fe60Al40 alloy and milled for 12 and 24 hours, two crystalline phases were found: a prevailing FeAl BCC phase and a Fe2B phase type. In addition, one observes an additional contribution attributed to grain boundaries which increases when both milling time and boron composition increase. Finally Mn and B were added to samples of the Fe60Al40 system prepared by mechanical alloying during 12 and 24 hours. Mn content was fixed to 10 at.% and B content varied between 0 and 20 at.%, substituting Al. X-ray patterns show two crystalline phases, the ternary FeMnAl BCC phase, and a (Fe,Mn)2B phase type. The relative proportion of the last phase increases when the B content increases, in addition to changes of the grain size and the lattice parameter. Such behavior was observed for both milling periods. On the other hand, the magnetic hyperfine field distributions show that both phases exhibit chemical disorder, and that the contribution attributed to the grain boundaries is less important when the B content increases. Coercive field values of about 10(2) Oe slightly increase with boron content

  1. Oxygen vacancy induced magnetization switching in Fe{sub 3}O{sub 4} epitaxial ultrathin films on GaAs(100)

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Zhaocong, E-mail: zhaocong.huang@gmail.com [Department of Physics, Southeast University, Nanjing 211189 (China); Spintronics and Nanodevice Laboratory, Department of Electronics, University of York, York YO10 5DD (United Kingdom); School of Electronic Science and Engineering, Southeast University, Nanjing 210096 (China); Chen, Qian; Zhai, Ya, E-mail: yazhai@seu.edu.cn, E-mail: jlwang@seu.edu.cn; Wang, Jinlan, E-mail: yazhai@seu.edu.cn, E-mail: jlwang@seu.edu.cn [Department of Physics, Southeast University, Nanjing 211189 (China); Xu, Yongbing [Spintronics and Nanodevice Laboratory, Department of Electronics, University of York, York YO10 5DD (United Kingdom); Wang, Baoping [School of Electronic Science and Engineering, Southeast University, Nanjing 210096 (China)

    2015-05-04

    The magnetic and transport properties of half metallic Fe{sub 3}O{sub 4}, which are sensitive to the stoichiometry, are the key issue for applications in spintronics. An anomalous enlargement of the saturation magnetic moment is found in a relatively thick sample of epitaxial Fe{sub 3}O{sub 4} film by post-growth oxidation method. The investigation of the thickness dependence of magnetic moment suggests that the enhanced magnetism moment may come from the existence of oxygen vacancies. First-principles calculations reveal that with oxygen vacancies in Fe{sub 3}O{sub 4} crystal the spin of Fe ions in the tetrahedron site near the vacancy is much easier to switch parallel to the Fe ions in the octahedron site by temperature disturbance, supported by the temperature dependence of magnetic moment of Fe{sub 3}O{sub 4} films in experiment.

  2. Investigation of structural relaxation, crystallization process and magnetic properties of the Fe-Ni-Si-B-C amorphous alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kalezic-Glisovic, A. [Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Systems, Technical Faculty Cacak, Svetog Save 65, 32000 Cacak (Serbia and Montenegro)]. E-mail: aleksandrakalezic@eunet.yu; Novakovic, L. [Faculty of Physics, Studentski trg 16, 11000 Belgrade (Serbia and Montenegro); Maricic, A. [Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Systems, Technical Faculty Cacak, Svetog Save 65, 32000 Cacak (Serbia and Montenegro); Minic, D. [Faculty of Physical Chemistry, Studentski trg 16, 11000 Belgrade (Serbia and Montenegro); Mitrovic, N. [Joint Laboratory for Advanced Materials of SASA, Section for Amorphous Systems, Technical Faculty Cacak, Svetog Save 65, 32000 Cacak (Serbia and Montenegro)]. E-mail: nmitrov@tfc.kg.ac.yu

    2006-07-15

    The differential scanning calorimetry method was used for investigating the crystallization process of the Fe{sub 89.8}Ni{sub 1.5}Si{sub 5.2}B{sub 3}C{sub 0.5} amorphous alloy. It was shown that the examined alloy crystallizes in three stages. The first crystallization stage occurs at 799 K, the second at 820 K and the third at 888 K. Temperature dependence of the magnetic susceptibility relative change was investigated by the modified Faraday method in the temperature region from room temperature up to 900 K. It has been established that the Curie temperature is about 700 K for amorphous state. The magnetic susceptibility increases by 30% after the first heating up to 710 K. During the second heating up to 840 K the alloy loses its ferromagnetic features in the temperature region from 710 to 750 K, upon which it again regains the same. After the second heating magnetic susceptibility decreases by 23% as compared to the amorphous starting value and by 53% as compared to the value before the second heating. The crystallized alloy maintains ferromagnetic features in the whole temperature region during the heating up to 900 K.

  3. Investigation of structural relaxation, crystallization process and magnetic properties of the Fe-Ni-Si-B-C amorphous alloy

    International Nuclear Information System (INIS)

    Kalezic-Glisovic, A.; Novakovic, L.; Maricic, A.; Minic, D.; Mitrovic, N.

    2006-01-01

    The differential scanning calorimetry method was used for investigating the crystallization process of the Fe 89.8 Ni 1.5 Si 5.2 B 3 C 0.5 amorphous alloy. It was shown that the examined alloy crystallizes in three stages. The first crystallization stage occurs at 799 K, the second at 820 K and the third at 888 K. Temperature dependence of the magnetic susceptibility relative change was investigated by the modified Faraday method in the temperature region from room temperature up to 900 K. It has been established that the Curie temperature is about 700 K for amorphous state. The magnetic susceptibility increases by 30% after the first heating up to 710 K. During the second heating up to 840 K the alloy loses its ferromagnetic features in the temperature region from 710 to 750 K, upon which it again regains the same. After the second heating magnetic susceptibility decreases by 23% as compared to the amorphous starting value and by 53% as compared to the value before the second heating. The crystallized alloy maintains ferromagnetic features in the whole temperature region during the heating up to 900 K

  4. Structural and magnetic characterization of Fe2CrSi Heusler alloy nanoparticles as spin injectors and spin based sensors

    Science.gov (United States)

    Saravanan, G.; Asvini, V.; Kalaiezhily, R. K.; Parveen, I. Mubeena; Ravichandran, K.

    2018-05-01

    Half-metallic ferromagnetic [HMF] nanoparticles are of considerable interest in spintronics applications due to their potential use as a highly spin polarized current source. HMF exhibits a semiconductor in one spin band at the Fermi level Ef and at the other spin band they poses strong metallic nature which shows 100 % spin polarization at Ef. Fe based full Heusler alloys are primary interest due to high Curie temperature. Fe2CrSi Heusler alloys are synthesized using metallic powders of Fe, Cr and Si by mechanical alloying method. X-Ray diffractions studies were performed to analyze the structural details of Fe2CrSi nanoparticles with High resolution scanning electron microscope (HRSEM) studies for the morphological details of nanoparticles and magnetic properties were studied using Vibrating sample magnetometer (VSM). XRD Data analysis conforms the Heusler alloy phase showing the existence of L21 structure. Magnetic properties are measured for synthesized samples exhibiting a soft magnetic property possessing low coercivity (HC = 60.5 Oe) and saturation magnetic moment of Fe2CrSi is 3.16 µB, which is significantly higher than the ideal value of 2 µB from the Slater-Pauling rule due to room temperature measurement. The change in magnetic properties are half-metallic nature of Fe2CrSi is due to the shift of the Fermi level with respect to the gap were can be used as spin sensors and spin injectors in magnetic random access memories and other spin dependent devices.

  5. Thermal evolution of nanocrystalline co-sputtered Ni–Zr alloy films: Structural, magnetic and MD simulation studies

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharya, Debarati, E-mail: debarati@barc.gov.in [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Rao, T.V. Chandrasekhar; Bhushan, K.G. [Technical Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Ali, Kawsar [Material Science Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Debnath, A. [Technical Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Singh, S. [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Arya, A. [Material Science Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Bhattacharya, S. [Technical Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Basu, S. [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India)

    2015-11-15

    Monophasic and homogeneous Ni{sub 10}Zr{sub 7} nanocrystalline alloy films were successfully grown at room temperature by co-sputtering in an indigenously developed three-gun DC/RF magnetron sputtering unit. The films could be produced with long-range crystallographic and chemical order in the alloy, thus overcoming the widely acknowledged inherent proclivity of the glass forming Ni–Zr couple towards amorphization. Crystallinity of these alloys is a desirable feature with regard to improved efficacy in applications such as hydrogen storage, catalytic activity and nuclear reactor engineering, to name a few. Thermal stability of this crystalline phase, being vital for transition to viable applications, was investigated through systematic annealing of the alloy films at 473 K, 673 K and 923 K for various durations. While the films were stable at 473 K, the effect of annealing at 673 K was to create segregation into nanocrystalline Ni (superparamagnetic) and amorphous Ni + Zr (non-magnetic) phases. Detailed analyses of the physical and magnetic structures before and after annealing were performed through several techniques effectual in analyzing stratified configurations and the findings were all consistent with each other. Polarized neutron and X-ray reflectometry, grazing incidence x-ray diffraction, time-of-flight secondary ion mass spectroscopy and X-ray photoelectron spectroscopy were used to gauge phase separation at nanometer length scales. SQUID based magnetometry was used to investigate macroscopic magnetic properties. Simulated annealing performed on this system using molecular dynamic calculations corroborated well with the experimental results. This study provides a thorough understanding of the creation and thermal evolution of a crystalline Ni–Zr alloy. - Highlights: • Nanocrystalline Ni{sub 10}Zr{sub 7} alloy thin films deposited successfully by co-sputtering. • Creation of a crystalline alloy in a binary system with a tendency to amorphize.

  6. Evidence of magnetic dipolar interaction in micrometric powders of the Fe50Mn10Al40 system: Melted alloys

    International Nuclear Information System (INIS)

    Pérez Alcázar, G.A.; Zamora, L.E.; Tabares, J.A.; Piamba, J.F.; González, J.M.; Greneche, J.M.; Martinez, A.; Romero, J.J.; Marco, J.F.

    2013-01-01

    Powders of melted disordered Fe 50 Mn 10 Al 40 alloy were separated at different mean particle sizes as well as magnetically and structurally characterized. All the samples are BCC and show the same nanostructure. Particles larger than 250 μm showed a lamellar shape compared to smaller particles, which exhibited a more regular form. All the samples are ferromagnetic at room temperature and showed reentrant spin-glass (RSG) and superparamagnetic (SP)-like behaviors between 30 and 60 K and 265 and > 280 K, respectively, as a function of frequency and particle size. The freezing temperature increases with increasing particle size while the blocking one decreases with particle size. The origin of these magnetic phenomena relies in the internal disordered character of samples and the competitive interaction of Fe and Mn atoms. The increase of their critical freezing temperature with increasing mean particle size is due to the increase of the magnetic dipolar interaction between the magnetic moment of each particle with the field produced by the other magnetic moments of their surrounding particles. - Highlights: ► The effect of particle size in microsized powders of Fe 50 Mn 10 Al 40 melted disordered alloy is studied. ► Dipolar magnetic interaction between particles exists and this changes with the particle size. ► For all the particle sizes the reentrant spin- glass and the superparamagnetic-like phases exist. ► RSG and SP critical temperatures increase with increasing the dipolar magnetic interaction (the mean particle size).

  7. ANOMALOUS ELECTRODEPOSITION OF Fe-Ni ALLOY COATING FROM SIMPLE AND COMPLEX BATHS AND ITS MAGNETIC PROPERTY

    Directory of Open Access Journals (Sweden)

    M A Islam

    2010-03-01

    Full Text Available Electrodeposition of Fe-Ni thin films has been carried on copper substrate under various electrodeposition conditions from two simple and six complex baths. Sulfate baths composing of NiSO4. 7H2O, FeSO4.7H2O, H3BO3 and Na2SO4KEYWORDS: Anomalous Electrodeposition, Fe-Ni Coating, Complexing agent, Current Density, Magnetic Property. 1. INTRODUCTION Alloy electrodeposition technologies can extend tremendously the potential of electrochemical deposition processes to provide coatings that require unique mechanical, chemical and physical properties [1]. There has been a great research interest in the development and characterization of iron-nickel (Fe-Ni thin films due to their operational capacity, economic interest, magnetic and other properties [2]. Due to their unique low coefficient of thermal expansion (CTE and soft magnetic properties, Fe-Ni alloys have been used in industrial applications for over 100 years [3]. Typical examples of applications that are based on the low CTE of Fe-Ni alloys include: thermostatic bimetals, glass sealing, integrated circuit packaging, cathode ray tube, shadow masks, membranes for liquid natural gas tankers; applications based on the soft magnetic properties include: read-write heads for magnetic storage, magnetic actuators, magnetic shielding, high performance transformer cores. comprise the simple baths whereas complex baths were prepared by adding ascorbic acid, saccharin and citric acid in simple baths. The effect of bath composition, pH and applied current density on coating appearance, composition, morphology and magnetic property were studied. Wet chemical analysis technique was used to analyze the coating composition whereas SEM and VSM were used to study the deposit morphology and magnetic property respectively. Addition of complexing agents in plating baths suppressed the anomalous nature of Fe-Ni alloy electrodeposition. Coatings obtained from simple baths were characterized by coarse grained non

  8. Ferrimagnetic Tb-Fe Alloy Thin Films: Composition and Thickness Dependence of Magnetic Properties and All-Optical Switching

    Directory of Open Access Journals (Sweden)

    Birgit eHebler

    2016-02-01

    Full Text Available Ferrimagnetic rare earth - transition metal Tb-Fe alloy thin films exhibit a variety of different magnetic properties, which depends strongly on composition and temperature. In this study, first the influence of the film thickness (5 - 85 nm on the sample magnetic properties was investigated in a wide composition range between 15 at.% and 38 at.% of Tb. From our results, we find that the compensation point, remanent magnetization, and magnetic anisotropy of the Tb-Fe films depend not only on the composition but also on the thickness of the magnetic film up to a critical thickness of about 20-30 nm. Beyond this critical thickness, only slight changes in magnetic properties are observed. This behavior can be attributed to a growth-induced modification of the microstructure of the amorphous films, which affects the short range order. As a result, a more collinear alignment of the distributed magnetic moments of Tb along the out-of-plane direction with film thickness is obtained. This increasing contribution of the Tb sublattice magnetization to the total sample magnetization is equivalent to a sample becoming richer in Tb and can be referred to as an effective composition. Furthermore, the possibility of all-optical switching, where the magnetization orientation of Tb-Fe can be reversed solely by circularly polarized laser pulses, was analyzed for a broad range of compositions and film thicknesses and correlated to the underlying magnetic properties.

  9. Ultrathin Shape Change Smart Materials.

    Science.gov (United States)

    Xu, Weinan; Kwok, Kam Sang; Gracias, David H

    2018-02-20

    With the discovery of graphene, significant research has focused on the synthesis, characterization, and applications of ultrathin materials. Graphene has also brought into focus other ultrathin materials composed of organics, polymers, inorganics, and their hybrids. Together, these ultrathin materials have unique properties of broad significance. For example, ultrathin materials have a large surface area and high flexibility which can enhance conformal contact in wearables and sensors leading to improved sensitivity. When porous, the short transverse diffusion length in these materials allows rapid mass transport. Alternatively, when impermeable, these materials behave as an ultrathin barrier. Such controlled permeability is critical in the design of encapsulation and drug delivery systems. Finally, ultrathin materials often feature defect-free and single-crystal-like two-dimensional atomic structures resulting in superior mechanical, optical, and electrical properties. A unique property of ultrathin materials is their low bending rigidity, which suggests that they could easily be bent, curved, or folded into 3D shapes. In this Account, we review the emerging field of 2D to 3D shape transformations of ultrathin materials. We broadly define ultrathin to include materials with a thickness below 100 nm and composed of a range of organic, inorganic, and hybrid compositions. This topic is important for both fundamental and applied reasons. Fundamentally, bending and curving of ultrathin films can cause atomistic and molecular strain which can alter their physical and chemical properties and lead to new 3D forms of matter which behave very differently from their planar precursors. Shape change can also lead to new 3D architectures with significantly smaller form factors. For example, 3D ultrathin materials would occupy a smaller space in on-chip devices or could permeate through tortuous media which is important for miniaturized robots and smart dust applications. Our

  10. Mixed hyperfine interaction - a tool to investigate the short range order and the strange magnetic behaviour of amorphous Fe-based binary alloys

    International Nuclear Information System (INIS)

    Fries, S.M.; Crummenauer, J.; Gonser, U.; Schaaf, P.; Chien, C.L.

    1989-01-01

    The Moessbauer study of the mixed magnetic dipole and electric quadrupole interaction in the paramagnetic state of amorphous Fe-Zr and Fe-Hf alloys is presented. Strong evidence for chemical short range order of the iron-pure alloys is found. The hyperfine parameters of the iron-rich alloys are marked by a complex applied field and temperature dependence, suggesting a not negligible spin-correlation well above Tc. (orig.)

  11. Material properties of Ni-Cr-Al alloy and design of a 4 GPa class non-magnetic high-pressure cell

    CERN Document Server

    Uwatoko, Y; Ueda, K; Uchida, A; Kosaka, M; Mori, N; Matsumoto, T

    2002-01-01

    The Ni-Cr-Al Russian alloy was prepared. Its magnetic and mechanical properties were better than those of MP35N alloy. We fabricated the a piston-cylinder-type hybrid high-pressure cell using the Ni-Cr-Al alloy. It has been found that the maximum working pressure can be repeatedly raised to 3.5 GPa at T = 2 K without any difficulties.

  12. Effective-medium theory for nonlinear magneto-optics in magnetic granular alloys: cubic nonlinearity

    International Nuclear Information System (INIS)

    Granovsky, Alexander B.; Kuzmichov, Michail V.; Clerc, J.-P.; Inoue, Mitsuteru

    2003-01-01

    We propose a simple effective-medium approach for calculating the effective dielectric function of a magnetic metal-insulator granular alloy in which there is a weakly nonlinear relation between electric displacement D and electric field E for both constituent materials of the form D i =ε i (0) E i +χ i (3) |E i | 2 E i . We assume that linear ε i (0) and cubic nonlinear χ i (3) dielectric functions are diagonal and linear with magnetization non-diagonal components. For such metal-insulator composite magneto-optical effects depend on a light intensity and the effective cubic dielectric function χ eff (3) can be significantly greater (up to 10 3 times) than that for constituent materials. The calculation scheme is based on the Bergman and Stroud-Hui theory of nonlinear optical properties of granular matter. The giant cubic magneto-optical nonlinearity is found for composites with metallic volume fraction close to the percolation threshold and at a resonance of optical conductivity. It is shown that a composite may exhibit nonlinear magneto-optics even when both constituent materials have no cubic magneto-optical nonlinearity

  13. Effective-medium theory for nonlinear magneto-optics in magnetic granular alloys: cubic nonlinearity

    Energy Technology Data Exchange (ETDEWEB)

    Granovsky, Alexander B. E-mail: granov@magn.ru; Kuzmichov, Michail V.; Clerc, J.-P.; Inoue, Mitsuteru

    2003-03-01

    We propose a simple effective-medium approach for calculating the effective dielectric function of a magnetic metal-insulator granular alloy in which there is a weakly nonlinear relation between electric displacement D and electric field E for both constituent materials of the form D{sub i}={epsilon}{sub i}{sup (0)}E{sub i} +{chi}{sub i}{sup (3)}|E{sub i}|{sup 2}E{sub i}. We assume that linear {epsilon}{sub i}{sup (0)} and cubic nonlinear {chi}{sub i}{sup (3)} dielectric functions are diagonal and linear with magnetization non-diagonal components. For such metal-insulator composite magneto-optical effects depend on a light intensity and the effective cubic dielectric function {chi}{sub eff}{sup (3)} can be significantly greater (up to 10{sup 3} times) than that for constituent materials. The calculation scheme is based on the Bergman and Stroud-Hui theory of nonlinear optical properties of granular matter. The giant cubic magneto-optical nonlinearity is found for composites with metallic volume fraction close to the percolation threshold and at a resonance of optical conductivity. It is shown that a composite may exhibit nonlinear magneto-optics even when both constituent materials have no cubic magneto-optical nonlinearity.

  14. Effect of a Traveling Magnetic Field on Micropore Formation in Al-Cu Alloys

    Directory of Open Access Journals (Sweden)

    Yanjin Xu

    2018-06-01

    Full Text Available The effect of traveling magnetic fields (TMFs on the grain and micro-pore formation in an Al alloy was studied by scanning electron microscope and X-ray microtomography in this work. The results show that with the increasing magnetic flux density, the three-dimensional morphology of the micro-pores transformed from dendrite to a relatively equiaxed structure. Quantified results show that both the micro-pore volume fraction and the average grain size of the primary phase decreased as the TMF density increased. The analyses show that the forced convection induced by TMF can break the dendrites, refine the grain size, and promote the liquid feeding, leading to the decrease in the volume fraction of the porosity and improved mechanical property. The TMF performed at different stages during solidification reveal that the maximum effect of TMF on reducing the micro-pore formation was found when TMF was applied in the stage of nucleation and the early stage of grain growth during solidification.

  15. CaO-matrix processing of MnBi alloys for permanent magnets

    Directory of Open Access Journals (Sweden)

    A. M. Gabay

    2017-05-01

    Full Text Available The possibility to suppress agglomeration of MnBi alloy particles during milling and their unwanted sintering during subsequent annealing was explored by embedding the particles in CaO through co-milling. A 15 h annealing of the micron-sized MnBi particles embedded in the CaO matrix at 300 °C is not accompanied by sintering or growth of the particles while it significantly increases their coercivity – presumably by healing the milling-induced crystal defects. After separation from the CaO matrix, the annealed MnBi powder combines a calculated energy product of 10 MGOe with a room-temperature coercivity of 14.4 kOe. At the same time, the partial loss and degradation of the MnBi low-temperature phase during warm compaction of the powders makes the effect of the CaO-matrix annealing less pronounced in the case of fully dense magnets; the residue from the solvents employed for the removal of the CaO might have contributed to the decline of the properties. Still, a relatively high room-temperature coercivity of 8.5 kOe was obtained for the fuslly-dense MnBi magnet exhibiting an energy product of 5.3 MGOe.

  16. Magnetic studies of melt spun NdFeAl-C alloys

    International Nuclear Information System (INIS)

    Rodriguez Torres, C.E.; Cabrera, A.F.; Sanchez, F.H.; Billoni, O.V.; Urreta, S.E.; Fabietti, L.M.

    2004-01-01

    Alloys with compositions Nd 60-x C x Fe 30 Al 10 (x=0, 1, 5 and 10) were processed by melt spinning at a tangential speed of 5 m/s. The as-cast ribbons were characterized by X-ray diffraction, Moessbauer Effect spectroscopy and their room temperature hysteresis loops. The substitution of Nd by C is found to affect the phase selection, from mainly DHCP-Nd for x=0 to DHCP-Nd /FCC-Nd for the other ones. Moessbauer spectra of all the as-cast samples indicate that Fe is present in crystalline magnetic phases as well as in a paramagnetic one. The major crystalline phase was identified as a μ-type (or A1) metastable phase, which is reported to have a large anisotropy field and a relatively high saturation polarization. Interstitial C stabilizes the μ-type phase and improves its average hyperfine field. The magnetic measurements display an increase of coercivity and remanence with the C concentration

  17. Ultra-thin film encapsulation processes for micro-electro-mechanical devices and systems

    International Nuclear Information System (INIS)

    Stoldt, Conrad R; Bright, Victor M

    2006-01-01

    A range of physical properties can be achieved in micro-electro-mechanical systems (MEMS) through their encapsulation with solid-state, ultra-thin coatings. This paper reviews the application of single source chemical vapour deposition and atomic layer deposition (ALD) in the growth of submicron films on polycrystalline silicon microstructures for the improvement of microscale reliability and performance. In particular, microstructure encapsulation with silicon carbide, tungsten, alumina and alumina-zinc oxide alloy ultra-thin films is highlighted, and the mechanical, electrical, tribological and chemical impact of these overlayers is detailed. The potential use of solid-state, ultra-thin coatings in commercial microsystems is explored using radio frequency MEMS as a case study for the ALD alloy alumina-zinc oxide thin film. (topical review)

  18. Research on low strain magnetic mechanical hysteresis damping performance of Fe-15Cr-3Mo-0.5Si alloy

    International Nuclear Information System (INIS)

    Wang, Hui; Huang, Huawei; Hong, Xiaofeng; Yin, Changgeng; Huang, Zhaohua; Chen, Le

    2015-01-01

    Highlights: • Heat treatment system has a great effect on the alloy damping performance. • Damping performance does not improve monotonously with temperature. • Furnace cooling is higher than that of alloy after air cooling. • There is an optimum annealing temperature and grain size to obtain high damping. - Abstract: This paper studies the preparation of Fe-15Cr-3Mo-0.5Si alloy by using vacuum induction melting furnace and vacuum annealing furnace, the damping performance of which in different heat treatment states is tested with dynamic mechanical thermal analyzer (DMA). Through microstructure observation with metallographic microscope (OM), grain boundary observation with scanning electron microscopy (SEM), phase structure analysis with X-ray diffraction (XRD) and internal stress of S-B model analysis, the effect law of annealing temperature, types of cooling, holding time and grain sizes on the damping performance of alloy and the related mechanism can be concluded as follows. The annealing temperature and grain sizes have a significant impact on the damping strain amplitude as well as the magnetic and mechanical damping performance of this ferromagnetic alloy. Proper annealing temperature and grain size is the necessary condition to get high damping performance of the alloy. It is not conducive to improvement of the damping performance if the annealing temperature is too high or too low and the grain size is too small or too large. For Fe-15Cr-3Mo-0.5Si alloy, within the range of the low strain amplitude, alloy damping performance does not improve monotonously with the increase of the annealing temperature and grain size. The maximum value appears at the annealing temperature of 1100 °C/1 h with the grain size of about 300 μm. At high annealing temperature of 1100 °C, the damping performance of alloy in the slow cooling furnace is higher than that with air cooling treatment. The extension or shortening of the holding time, to a certain extent

  19. Research on low strain magnetic mechanical hysteresis damping performance of Fe-15Cr-3Mo-0.5Si alloy

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hui, E-mail: qinghe5525@163.com; Huang, Huawei; Hong, Xiaofeng; Yin, Changgeng; Huang, Zhaohua; Chen, Le

    2015-02-15

    Highlights: • Heat treatment system has a great effect on the alloy damping perfor