  1. Corrosion behavior of ion implanted nickel-titanium orthodontic wire in fluoride mouth rinse solutions.

    Science.gov (United States)

    Iijima, Masahiro; Yuasa, Toshihiro; Endo, Kazuhiko; Muguruma, Takeshi; Ohno, Hiroki; Mizoguchi, Itaru

    2010-01-01

    This study investigated the corrosion properties of ion implanted nickel-titanium wire (Neo Sentalloy Ionguard) in artificial saliva and fluoride mouth rinse solutions (Butler F Mouthrinse, Ora-Bliss). Non ion implanted nickel-titanium wire (Neo Sentalloy) was used as control. The anodic corrosion behavior was examined by potentiodynamic polarization measurement. The surfaces of the specimens were examined with SEM. The elemental depth profiles were characterized by XPS. Neo Sentalloy Ionguard in artificial saliva and Butler F Mouthrinse (500 ppm) had a lower current density than Neo Sentalloy. In addition, breakdown potential of Neo Sentalloy Ionguard in Ora-Bliss (900 ppm) was much higher than that of Neo Sentalloy although both wires had similar corrosion potential in Ora-Bliss (450 and 900 ppm). The XPS results for Neo Sentalloy Ionguard suggested that the layers consisted of TiO(2) and TiN were present on the surface and the layers may improve the corrosion properties.

  2. Uranium fluorides analysis. Titanium spectrophotometric determination

    International Nuclear Information System (INIS)

    Anon.

    Titanium determination in uranium hexafluoride in the range 0.7 to 100 microgrammes after transformation of uranium fluoride in sulfate. Titanium is separated by extraction with N-benzoylphenylhydroxylamine, reextracted by hydrochloric-hydrofluoric acid. The complex titanium-N-benzoylphenylhydroxylamine is extracted by chloroform. Spectrophotometric determination at 400 nm [fr

  3. Erosion-inhibiting effect of sodium fluoride and titanium tetrafluoride treatment in vitro

    NARCIS (Netherlands)

    Rijkom, Hans van; Ruben, J.; Vieira, A.; Huysmans, M.C.; Truin, G-J.; Mulder, J.

    2003-01-01

    The prevention of dental erosion with fluoride is still largely unknown territory. It was the aim of this study to determine the erosion-inhibiting effect of topical neutral 1% sodium fluoride (NaF) application and an application of a 4% titanium tetrafluoride (TiF4) solution compared with no

  4. Application of Titanium Compounds to Reduce Fluoride Ion in Water Resources with High Fluoride Ion Contents

    Directory of Open Access Journals (Sweden)

    Fariborz Riahi

    2005-06-01

    Full Text Available The present work describes studies on the sorption of fluoride ions from water by titanium compounds used in water treatment to reduce fluoride content in water resources. There are different methods of reducing fluoride ion in water, each associated with specific problems such as secondary contamination, environmental contamination, high costs, or the need for primary and secondary treatment. In this study, application of titanium sulfate and Metatitanic acid produced from titanium ore concentrate (ileminite is investigated in the removal of fluoride ion and the possibility of complete purification of fluorine containing wastewater is examined to determine the optimal conditions. Metatitanic acid has a great sorption property for fluoride ion. Also titanium sulfate is a suitable and more effective material for this purpose. Efficiency of this material in reducing fluoride ion content is 99.9% and it is possible to refresh sorbet material for reuse without problems arising from Ti+4 ion contamination.

  5. Effect of titanium tetrafluoride, amine fluoride and fluoride varnish on enamel erosion in vitro

    NARCIS (Netherlands)

    Vieira, A; Ruben, JL; Huysmans, MCDNJM

    2005-01-01

    This study aimed at evaluating the effect of 1 and 4% titanium tetrafluoride (TiF4) gels, amine fluoride (AmF) 1 and 0.25% and a fluoride varnish (FP) on the prevention of dental erosion. Two experimental groups served as controls, one with no pretreatment and another one pre-treated with a

  6. Streptococcus mutans adhesion to titanium after brushing with fluoride and fluoride-free toothpaste simulating 10 years of use.

    Science.gov (United States)

    Fais, Laiza M G; Carmello, Juliana C; Spolidorio, Denise M P; Adabo, Gelson L

    2013-01-01

    To assess the influence of fluoride on the adhesion of Streptococcus mutans to titanium using an experimental paradigm simulating 10 years of brushing. Commercially pure titanium (cpTi) and titanium alloy (Ti-6Al-4V) disks (6 mm in diameter and 4 mm thick) were mirror-polished and randomly assigned to one of the following six groups (n = 6): immersion (I) or brushing (B) in deionized water (groups IW [control] and BW), fluoride-free toothpaste (groups IT and BT), or fluoridated toothpaste (groups IFT and BFT). Specimens subjected to immersion were statically submerged into the solutions without brushing. For the brushed specimens, a linear brushing machine with a soft-bristled toothbrush was used. The experiments lasted a total of 244 hours. Before and after treatment, the specimens were analyzed under an atomic force microscope to determine the mean roughness (Ra) and the mean of the maximum peak-to-valley heights of the profile (Rtm). The disks were contaminated with standard strains of S mutans in well plates with brain-heart infusion broth. Adhesion was analyzed based on the numbers of colony-forming units (CFU/mL) of adhered viable cells using scanning electronic microscopy. Differences in CFU/mL between the groups were analyzed by one-way analysis of variance. Immersion did not affect either surface. As suggested by Ra and Rtm, BW, BT, and BFT induced changes on the surface of cpTi, whereas only BT and BTF induced changes on the surface of Ti-6Al-4V. No significant differences were observed regarding CFU/mL among the cpTi or Ti-6Al-4V groups. S mutans adhesion was similar for all surfaces. The changes in titanium induced by 10 years of simulated brushing with fluoride toothpaste did not increase the adhesion of S mutans.

  7. Fluoride removal from aqueous solution by pumice: case study on ...

    African Journals Online (AJOL)

    EJIRO

    conditions, the fluoride removal efficiency from Kuhbonan water by 2.8 mg/L fluoride was 74.64%. Eventually ... industrial wastewater containing fluoride is a key ..... solution using silica ceramic: Adsorption kinetics and equilibrium studies.

  8. Uranyl fluoride luminescence in acidic aqueous solutions

    International Nuclear Information System (INIS)

    Beitz, J.V.; Williams, C.W.

    1996-01-01

    Luminescence emission spectra and decay rates are reported for uranyl species in acidic aqueous solutions containing HF or added NaF. The longest luminescence lifetime, 0.269 ± 0.006 ms, was observed from uranyl in 1 M HF + 1 M HClO 4 at 296 K and decreased with increasing temperature. Based on a luminescence dynamics model that assumes equilibrium among electronically excited uranyl fluoride species and free fluoride ion, this long lived uranyl luminescence in aqueous solution is attributed primarily to UO 2 F 2 . Studies on the effect of added LiNO 3 or Na 2 WO 4 ·2H 2 O showed relatively weak quenching of uranyl fluoride luminescence which suggests that high sensitivity determination of the UF 6 content of WF 6 gas should be feasible via uranyl luminescence analysis of hydrolyzed gas samples of impure WF 6

  9. Preparation of Bioactive Titanium Surfaces via Fluoride and Fibronectin Retention

    Directory of Open Access Journals (Sweden)

    Carlos Nelson Elias

    2012-01-01

    Full Text Available Statement of Problem. The chemical or topographic modification of the dental implant surface can affect bone healing, promote accelerated osteogenesis, and increase bone-implant contact and bonding strength. Objective. In this work, the effects of dental implant surface treatment and fibronectin adsorption on the adhesion of osteoblasts were analyzed. Materials and Methods. Two titanium dental implants (Porous-acid etching and PorousNano-acid etching followed by fluoride ion modification were characterized by high-resolution scanning electron microscopy, atomic force microscopy, and X-ray diffraction before and after the incorporation of human plasma fibronectin (FN. The objective was to investigate the biofunctionalization of these surfaces and examine their effects on the interaction with osteoblastic cells. Results. The evaluation techniques used showed that the Porous and PorousNano implants have similar microstructural characteristics. Spectrophotometry demonstrated similar levels of fibronectin adsorption on both surfaces (80%. The association indexes of osteoblastic cells in FN-treated samples were significantly higher than those in samples without FN. The radioactivity values associated with the same samples, expressed as counts per minute (cpm, suggested that FN incorporation is an important determinant of the in vitro cytocompatibility of the surfaces. Conclusion. The preparation of bioactive titanium surfaces via fluoride and FN retention proved to be a useful treatment to optimize and to accelerate the osseointegration process for dental implants.

  10. Corrosion and hydrogen absorption of commercially pure zirconium in acid fluoride solutions

    International Nuclear Information System (INIS)

    Yokoyama, Ken’ichi; Yamada, Daisuke; Sakai, Jun’ichi

    2013-01-01

    Highlights: •Zirconium corrodes and absorbs hydrogen in acid fluoride solutions. •Hydrogen thermal desorption is observed at 300–700 °C. •The resistance to hydrogen absorption of zirconium is higher than that of titanium. -- Abstract: The corrosion and hydrogen absorption of commercially pure zirconium have been investigated in acidulated phosphate fluoride (APF) solutions. Upon immersion in 2.0% APF solution of pH 5.0 at 25 °C, a granular corrosion product (Na 3 ZrF 7 ) deposits over the entire side surface of the specimen, thereby inhibiting further corrosion. In 0.2% APF solution, marked corrosion is observed from the early stage of immersion; no deposition of the corrosion product is observed by scanning electron microscopy. A substantial amount of hydrogen absorption is confirmed in both APF solutions by hydrogen thermal desorption analysis. The amount of absorbed hydrogen of the specimen immersed in the 2.0% APF solution is smaller than that in the 0.2% APF solution in the early stage of immersion. The hydrogen absorption behavior is not always consistent with the corrosion behavior. Hydrogen thermal desorption occurs in the temperature range of 300–700 °C for the specimen without the corrosion product. Under the same immersion conditions, the amount of absorbed hydrogen in commercially pure zirconium is smaller than that in commercially pure titanium as reported previously. The present results suggest that commercially pure zirconium, compared with commercially pure titanium, is highly resistant to hydrogen absorption, although corrosion occurs in fluoride solutions

  11. Analysis of titanium content in titanium tetrachloride solution

    Science.gov (United States)

    Bi, Xiaoguo; Dong, Yingnan; Li, Shanshan; Guan, Duojiao; Wang, Jianyu; Tang, Meiling

    2018-03-01

    Strontium titanate, barium titan and lead titanate are new type of functional ceramic materials with good prospect, and titanium tetrachloride is a commonly in the production such products. Which excellent electrochemical performance of ferroelectric tempreature coefficient effect.In this article, three methods are used to calibrate the samples of titanium tetrachloride solution by back titration method, replacement titration method and gravimetric analysis method. The results show that the back titration method has many good points, for example, relatively simple operation, easy to judgment the titration end point, better accuracy and precision of analytical results, the relative standard deviation not less than 0.2%. So, it is the ideal of conventional analysis methods in the mass production.

  12. [Corrosion resistance of casted titanium by compound treatments in the artificial saliva with different fluoride concentrations].

    Science.gov (United States)

    Wang, Xian-li; Guo, Tian-wen

    2012-09-01

    To study the corrosion resistance of casted titanium by plasma nitriding and TiN-coated compound treatments in the artificial saliva with different fluoride concentrations and to investigate whether compound treatments can increase the corrosion resistance of casted titanium. Potentiodynamic polarization technique was used to depict polarization curve and to measured the current density of corrosion (Icorr) and the electric potential of corrosion (Ecorr) of casted titanium (Group A) and casted titanium by compound treatments (Group B) in the artificial saliva with different fluoride concentrations. After electrochemical experiment, the microstructure was observed by scanning electron microscope (SEM). The Icorrs of Group A and B in the artificial saliva of different fluoride concentrations were (1530.23 ± 340.12), (2290.36 ± 320.10), (4130.52 ± 230.17) nA and (2.62 ± 0.64), (7.37 ± 3.59), (10.76 ± 6.05) nA, respectively. The Ecorrs were (-0.93 ± 0.10), (-0.89 ± 0.21), (-0.57 ± 0.09) V and (-0.21 ± 0.04), (-0.17 ± 0.03), (-0.22 ± 0.03) V, respectively.The Icorrs of Group B were significantly lower (P compound treatments can significantly increase the corrosion resistance of casted titanium.

  13. Fluoride influences nickel-titanium orthodontic wires′ surface texture and friction resistance

    Directory of Open Access Journals (Sweden)

    Mona Aly Abbassy

    2016-01-01

    Full Text Available Objectives: The aim of this study was to investigate the effects exerted by the acidulated fluoride gel on stainless steel and nickel-titanium (Ni-Ti orthodontic wires. Materials and Methods: Sixty stainless steel and Ni-Ti orthodontic archwires were distributed into forty archwires used for in vitro study and twenty for in situ study. Fluoride was applied for 1 h in the in vitro experiment while it was applied for 5 min in the in situ experiment. The friction resistance of all wires with ceramic brackets before/after topical fluoride application was measured using a universal testing machine at 1 min intervals of moving wire. Moreover, surface properties of the tested wires before/after fluoride application and before/after friction test were examined by a scanning electron microscope (SEM. Dunnett′s t-test was used to compare frictional resistance of as-received stainless steel wires and Ni-Ti wires to the wires treated by fluoride in vitro and in situ (P < 0.05. Two-way ANOVA was used to compare the effect of fluoride application and type of wire on friction resistance in vitro and in situ (P < 0.05. Results: Ni-Ti wires recorded significantly high friction resistance after fluoride application when compared to stainless steel wires in vitro, P < 0.05. Fluoride application did not significantly affect the friction resistance of the tested wires in situ, P < 0.05. SEM observation revealed deterioration of the surface texture of the Ni-Ti wires after fluoride application in vitro and in situ. Conclusions: The in vitro fluoride application caused an increase in friction resistance of Ni-Ti wires when compared to stainless steel wires. In vitro and in situ fluoride application caused deterioration in surface properties of Ni-Ti wires.

  14. Titanium surface topography after brushing with fluoride and fluoride-free toothpaste simulating 10 years of use.

    Science.gov (United States)

    Fais, Laiza M G; Fernandes-Filho, Romeu B; Pereira-da-Silva, Marcelo A; Vaz, Luis G; Adabo, Gelson L

    2012-04-01

    To conduct a controlled study contrasting titanium surface topography after procedures that simulated 10 years of brushing using toothpastes with or without fluoride. Commercially pure titanium (cp Ti) and Ti-6Al-4V disks (6 mm Ø×4 mm) were mirror-polished and treated according to 6 groups (n=6) as a function of immersion (I) or brushing (B) using deionised water (W), fluoride-free toothpaste (T) and fluoride toothpaste (FT). Surface topography was evaluated at baseline (pretreatment) and post-treatment, using atomic force microscope in order to obtain three-dimensional images and mean roughness. Specimens submitted to immersion were submerged in the vehicles without brushing. For brushed specimens, procedures were conducted using a linear brushing machine with a soft-bristled toothbrush. Immersion and brushing were performed for 244 h. IFT and BFT samples were analysed under scanning electron microscope with Energy-Dispersive X-ray Spectroscopy (EDS). Pre and post-treatment values were compared using the paired Student T-test (α=.05). Intergroup comparisons were conducted using one-way ANOVA with Tukey post-test (α=.05). cp Ti mean roughness (in nanometers) comparing pre and post-treatment were: IW, 2.29±0.55/2.33±0.17; IT, 2.24±0.46/2.02±0.38; IFT, 2.22±0.53/1.95±0.36; BW, 2.22±0.42/3.76±0.45; BT, 2.27±0.55/16.05±3.25; BFT, 2.27±0.51/22.39±5.07. Mean roughness (in nanometers) measured in Ti-6Al-4V disks (pre/post-treatment) were: IW, 1.79±0.25/2.01±0.25; IT, 1.61±0.13/1.74±0.19; IFT, 1.92±0.39/2.29±0.51; BW, 2.00±0.71/2.05±0.43; BT, 2.37±0.86/11.17±2.29; BFT, 1.83±0.50/15.73±1.78. No significant differences were seen after immersions (p>.05). Brushing increased the roughness of cp Ti and of Ti-6Al-4V (p<.01); cp Ti had topographic changes after BW, BT and BFT treatments whilst Ti-6Al-4V was significantly different only after BT and BTF. EDS has not detected fluoride or sodium ions on metal surfaces. Exposure to toothpastes (immersion

  15. Synthesis and characterization of titania nanotubes by anodizing of titanium in fluoride containing electrolytes

    Science.gov (United States)

    Ahmad, Akhlaq; Haq, Ehsan Ul; Akhtar, Waseem; Arshad, Muhammad; Ahmad, Zubair

    2017-11-01

    Titania nanotubular structure was prepared by anodizing titanium metal in the fluoride containing electrolytes and studied for hydrogen reduction using photo electrochemical cell. Potentiodynamic scan was performed before actual anodizing to optimize the anodizing conditions. The morphology of the TiO2 nanotubes was investigated by SEM and the presence of TiO2 nanotubes was confirmed. Raman spectroscopy was done to confirm the different phases present. Hydrogen generation capability was revealed by electrochemical testing in three-electrode system in dark and in visible light at 200 W power using Gamry Potentiostat. The corrosion potential of TiO2 nanotubes produced was found to be more active side in potassium hydroxide solution under visible light than in the dark condition. Cathodic polarization behavior of specimens in the presence of light showed more activity towards hydrogen generation than in dark condition. In comparison, the hydrogen generation capability of specimen anodized in 2H15 electrolyte was higher than specimens anodized in other electrolytes. Electrochemical impedance spectroscopy was used to study the charge transfer resistance of the nanotubes produced. The results showed that TiO2 nanotubular structure is a promising material for photoelectrochemical cell. Low-charge transfer resistance also depicts that it can be efficiently used to harvest solar energy.

  16. In Vivo Remineralization of Artificial Carious Lesions using Calcifying Solution and Fluoride Solution

    Directory of Open Access Journals (Sweden)

    Els Sunarsih Budipramana

    2015-10-01

    Full Text Available The remineralization potential of fluoride and calcifying solution was studiedas in situ model. Matched enamel discs of artifically demineralized human enamel were attached to an acrylic mandibular removable appliance of 6 adult volunteers who rinsed their mouth with a solution containing either 50 ppm F-, 200 ppm F- in amine fluoride, calcifying solution (formula BR21 or placebo as a control. The volunteers were asked to rinse 3 times a day for 3 minutes with 15 ml of the solution for 6 days (18 times. On the 7th day enamel discs were taken out from the partial denture. Three kinds of measurements were done: enamel permeability testing, depth lesion testing and fluoride retention testing. New demineralized enamel discs were attached to the partial dentures and the volunteers were asked to start rinsing with other solutions using the same protocols. The purpose of this study was to answer the question why the calcifying solutions were no more used as a remineralizing solution. The data ws analyzed using SPSS/PC for two factors Anova and one way Anova for enamel permeability and Kruskal Wallis for studying enamel depth lesion and fluoride retention. There was no significant difference after rinsing with calcifying solution and placebo in enamel permeability, depth lesions, and fluoride retention when compared to fluoride solution. To get a better result in remineralizing carious teeth fluoride contents in solution must be higher than 50 ppm F-.

  17. Removal of fluoride ions from aqueous solution by waste mud

    International Nuclear Information System (INIS)

    Kemer, Baris; Ozdes, Duygu; Gundogdu, Ali; Bulut, Volkan N.; Duran, Celal; Soylak, Mustafa

    2009-01-01

    The present study was carried out to assess the ability of original waste mud (o-WM) and different types of activated waste mud which are acid-activated (a-WM) and precipitated waste mud (p-WM), in order to remove excess of fluoride from aqueous solution by using batch technique. The p-WM exhibited greater performance than the others. Adsorption studies were conducted as a function of pH, contact time, initial fluoride concentration, adsorbent concentration, temperature, etc. Studies were also performed to understand the effect of some co-existing ions present in aqueous solutions. Adsorption process was found to be almost independent of pH for all types of waste mud. Among the kinetic models tested for p-WM, pseudo-second-order model fitted the kinetic data well with a perfect correlation coefficient value of 1.00. It was found that the adequate time for the adsorption equilibrium of fluoride was only 1 h. Thermodynamic parameters including the Gibbs free energy (ΔG o ), enthalpy (ΔH o ), and entropy (ΔS o ) revealed that adsorption of fluoride ions on the p-WM was feasible, spontaneous and endothermic in the temperature range of 0-40 deg. C. Experimental data showed a good fit with the Langmuir and Freundlich adsorption isotherm models. Results of this study demonstrated the effectiveness and feasibility of WM for removal of fluoride ions from aqueous solution.

  18. Removal of fluoride ions from aqueous solution by waste mud

    Energy Technology Data Exchange (ETDEWEB)

    Kemer, Baris; Ozdes, Duygu; Gundogdu, Ali; Bulut, Volkan N.; Duran, Celal [Karadeniz Technical University, Faculty of Arts and Sciences, Department of Chemistry, 61080 Trabzon (Turkey); Soylak, Mustafa, E-mail: soylak@erciyes.edu.tr [Erciyes University, Faculty of Arts and Sciences, Department of Chemistry, 38039 Kayseri (Turkey)

    2009-09-15

    The present study was carried out to assess the ability of original waste mud (o-WM) and different types of activated waste mud which are acid-activated (a-WM) and precipitated waste mud (p-WM), in order to remove excess of fluoride from aqueous solution by using batch technique. The p-WM exhibited greater performance than the others. Adsorption studies were conducted as a function of pH, contact time, initial fluoride concentration, adsorbent concentration, temperature, etc. Studies were also performed to understand the effect of some co-existing ions present in aqueous solutions. Adsorption process was found to be almost independent of pH for all types of waste mud. Among the kinetic models tested for p-WM, pseudo-second-order model fitted the kinetic data well with a perfect correlation coefficient value of 1.00. It was found that the adequate time for the adsorption equilibrium of fluoride was only 1 h. Thermodynamic parameters including the Gibbs free energy ({Delta}G{sup o}), enthalpy ({Delta}H{sup o}), and entropy ({Delta}S{sup o}) revealed that adsorption of fluoride ions on the p-WM was feasible, spontaneous and endothermic in the temperature range of 0-40 deg. C. Experimental data showed a good fit with the Langmuir and Freundlich adsorption isotherm models. Results of this study demonstrated the effectiveness and feasibility of WM for removal of fluoride ions from aqueous solution.

  19. Development and evaluation of two PVD-coated β-titanium orthodontic archwires for fluoride-induced corrosion protection.

    Science.gov (United States)

    Krishnan, Vinod; Krishnan, Anand; Remya, R; Ravikumar, K K; Nair, S Asha; Shibli, S M A; Varma, H K; Sukumaran, K; Kumar, K Jyothindra

    2011-04-01

    The present research was aimed at developing surface coatings on β titanium orthodontic archwires capable of protection against fluoride-induced corrosion. Cathodic arc physical vapor deposition PVD (CA-PVD) and magnetron sputtering were utilized to deposit thin films of titanium aluminium nitride (TiAlN) and tungsten carbide/carbon (WC/C) coatings on β titanium orthodontic archwires. Uncoated and coated specimens were immersed in a high fluoride ion concentration mouth rinse, following a specially designed cycle simulating daily use. All specimens thus obtained were subjected to critical evaluation of parameters such as electrochemical corrosion behaviour, surface analysis, mechanical testing, microstructure, element release, and toxicology. The results confirm previous research that β titanium archwires undergo a degradation process when in contact with fluoride mouth rinses. The study confirmed the superior nature of the TiAlN coating, evident as many fewer changes in properties after fluoride treatment when compared with the WC/C coating. Thus, coating with TiAlN is recommended in order to reduce the corrosive effects of fluorides on β titanium orthodontic archwires. Copyright © 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  20. Fluoride

    Science.gov (United States)

    Opalescence® ... Fluoride is used to prevent tooth decay. It is taken up by teeth and helps to strengthen ... and block the cavity-forming action of bacteria. Fluoride usually is prescribed for children and adults whose ...

  1. Corrosion behaviour and galvanic coupling of titanium and welded titanium in LiBr solutions

    International Nuclear Information System (INIS)

    Blasco-Tamarit, E.; Igual-Munoz, A.; Garcia Anton, J.; Garcia-Garcia, D.

    2007-01-01

    Corrosion resistance and galvanic coupling of Grade 2 commercially pure titanium in its welded and non-welded condition were systematically analyzed in LiBr solutions. Galvanic corrosion was evaluated through two different methods: anodic polarization (according to the Mixed Potential Theory) and electrochemical noise (using a zero-resistance ammeter). Samples have been etched to study the microstructure. The action of lithium chromate as corrosion inhibitor has been evaluated. Titanium and welded titanium showed extremely low corrosion current densities and elevated pitting potential values (higher than 1 V). The results of both methods, anodic polarization and electrochemical noise, showed that the welded titanium was always the anodic element of the pair titanium-welded titanium, so that its corrosion resistance decreases due to the galvanic effect

  2. Determination of fluoride content in UO2F2 and ADUF solution by ion selective electrode

    International Nuclear Information System (INIS)

    Samanta, Papu; Kumar, Pradeep; Bagchi, A.C.

    2017-01-01

    During production of uranium metal powder, liquid solution UO 2 F 2 and ADUF containing high content of fluoride gets generated. Fluoride being corrosive in nature, fluorides concentration needs to determined. Ion selective electrode, LaF 3 (Eu) crystal, has been used. Uranium was found to interfere with fluoride analysis. Study was carried out to selectively remove uranium by solvent extraction employing D2EHPA+Cyanex 923 and TBP in dodecane. The TBP was found effective to remove uranium. (author)

  3. Radiolysis of titanium potassium oxalate in aqueous solution. [. gamma. rays

    Energy Technology Data Exchange (ETDEWEB)

    Bundo, Y; Ono, I [Industrial Research Inst. of Kanagawa Prefecture, Yokohama (Japan); Ogawa, T

    1975-01-01

    The dissolution state of titanium potassium oxalate in aqueous solution is different according to the pH. The yellowish brown titanium complex produced by the reaction of titanium potassium oxalate and hydrogen peroxide seems to be different in its structure according to the pH. Considering these points, gamma-ray irradiation was carried out on the sample by dissolving titanium potassium oxalate in purified water under the conditions of oxygen saturation and nitrogen saturation, and the relation between irradiation dose and the production of titanium complex was determined. On the basis of the experimental result, the mechanism of forming hydrogen peroxide was presumed. The radiation source used was 2,000 Ci of /sup 60/Co. For photometric analysis, a 139 type photoelectric spectrophotometer of Hitachi Ltd. was used. From the experimental results, in neutral water, titanium potassium oxalate exists in the state that two oxalic acid ions are coordinated to titanyl ion, while in case of the pH lowered by the addition of sulfuric acid, it can exist in the state that one oxalic acid ion is coordinated to titanyl ion. The yield of hydrogen peroxide produced by irradiating titanium potassium oxalate aqueous solution with gamma-ray is the sum of the molecular product from water and the radiolysis product from titanium potassium oxalate.

  4. Fluoride removal from diluted solutions by Donnan dialysis using full factorial design

    Energy Technology Data Exchange (ETDEWEB)

    Boubakri, Ali; Helali, Nawel; Tlili, Mohamed; Amor, Mohamed Ben [Center of Researches and Water Technologies, Soliman (Turkey)

    2014-03-15

    Excessive fluoride concentration in potable water can lead to fluorosis of teeth and bones. In the present study, Donnan dialysis (DD) is applied for the removal of fluoride ions from diluted sodium fluoride solutions. A four factor two level (2{sup 4}) full factorial design was used to investigate the influence of different physico-chemical parameters on fluoride removal efficiency (Y{sub F}) and fluoride flux (J{sub F}) through anion exchange membrane. The statistical design determines factors which have the important effects on Donnan dialysis performance and studies all interactions among the considered parameters. The four significant factors were initial fluoride concentration, feed flow rate, temperature and agitation speed. The experimental results and statistical analysis show that the temperature and agitation speed have positive effects on fluoride removal efficiency and the initial fluoride concentration has a negative effect. In the case of fluoride flux, feed flow rate and initial concentration are the main effect and all factors have a positive effect. The interaction between studied parameters was not negligible on two responses. A maximum fluoride removal of 75.52% was obtained under optimum conditions and the highest value of fluoride flux obtained was 2.4 mg/cm{sup 2}·h. Empirical regression models were also obtained and used to predict the flux and the fluoride removal profiles with satisfactory results.

  5. Fluoride removal from aqueous solution by pumice: case study on ...

    African Journals Online (AJOL)

    The fluoride removal from synthetic water by pumice was studied at batch experiments in this study. The effect of pH, contact time, fluoride concentration and adsorbent dose on the fluoride sequestration was investigated. The optimum conditions were studied on Kuhbonan water as a case study. The results showed that ...

  6. Chemical milling solution reveals stress corrosion cracks in titanium alloy

    Science.gov (United States)

    Braski, D. N.

    1967-01-01

    Solution of hydrogen flouride, hydrogen peroxide, and water reveals hot salt stress corrosion cracks in various titanium alloys. After the surface is rinsed in water, dried, and swabbed with the solution, it can be observed by the naked eye or at low magnification.

  7. Rapid determination of fluoride in uranyl nitrate solution obtained in conversion process of uranium tetrafluoride

    International Nuclear Information System (INIS)

    Levin, R.; Feldman, R.; Sahar, E.

    1976-01-01

    In uranium production the conversion of impure uranium tetrafluoride by sodium hydroxide was chosen as a current process. A rapid method for determination of fluoride in uranyl-nitrate solution was developed. The method includes precipitation of uranium as diuranate, separation by centrifugation, and subsequent determination of fluoride in supernate by titration with thorium nitrate. Fluoride can be measured over the range 0.15-2.5 gr/gr U, with accuracy of +-5%, within 15 minutes. (author)

  8. Defect structure of cubic solid solutions of alkaline earth and rare earth fluorides

    NARCIS (Netherlands)

    DenHartog, HW

    1996-01-01

    In this paper we will consider the disorder in some cubic solid solutions consisting of one of the alkaline earth fluorides and one of the rare earth fluorides. This is an attractive group of model materials, because these materials have a rather simple overall cubic structure. We will discuss the

  9. Dynamics of ligand exchange and association processes in solutions of transition 3d-metal fluorides

    International Nuclear Information System (INIS)

    Nazmutdinova, G.A.; Shtyrlin, V.G.; Zakharov, A.V.; Sal'nikov, Yu.I.

    1993-01-01

    By 19 NMR in combination with ESR spectroscopy rate constants and activation parameters of fluoride-ion exchange reactions in solutions of VOF 5 3- and FeF 6 3- complexes were determined. Associative character of the studied reactions of ligand exchange is shown. Dependence of fluoride complex reactivity on the charge, electron structure of the central ion and formation of hydrogen bonds of coordinated F - ions with solvent molecules was demonstrated. Stability constants, rates of formation and dissociation of intercomplex associates in fluoride solutions were ascertained

  10. In Vitro and In Vivo Osteogenic Activity of Titanium Implants Coated by Pulsed Laser Deposition with a Thin Film of Fluoridated Hydroxyapatite

    Directory of Open Access Journals (Sweden)

    Luyuan Chen

    2018-04-01

    Full Text Available To enhance biocompatibility, osteogenesis, and osseointegration, we coated titanium implants, by krypton fluoride (KrF pulsed laser deposition, with a thin film of fluoridated hydroxyapatite (FHA. Coating was confirmed by scanning electron microscopy (SEM and scanning probe microscopy (SPM, while physicochemical properties were evaluated by attenuated reflectance Fourier transform infrared spectroscopy (ATR-FTIR. Calcium deposition, osteocalcin production, and expression of osteoblast genes were significantly higher in rat bone marrow mesenchymal stem cells seeded on FHA-coated titanium than in cells seeded on uncoated titanium. Implantation into rat femurs also showed that the FHA-coated material had superior osteoinductive and osseointegration activity in comparison with that of traditional implants, as assessed by microcomputed tomography and histology. Thus, titanium coated with FHA holds promise as a dental implant material.

  11. A Review on Adsorption of Fluoride from Aqueous Solution

    Science.gov (United States)

    Habuda-Stanić, Mirna; Ergović Ravančić, Maja; Flanagan, Andrew

    2014-01-01

    Fluoride is one of the anionic contaminants which is found in excess in surface or groundwater because of geochemical reactions or anthropogenic activities such as the disposal of industrial wastewaters. Among various methods used for defluoridation of water such as coagulation, precipitation, membrane processes, electrolytic treatment, ion-exchange, the adsorption process is widely used. It offers satisfactory results and seems to be a more attractive method for the removal of fluoride in terms of cost, simplicity of design and operation. Various conventional and non-conventional adsorbents have been assessed for the removal of fluoride from water. In this review, a list of various adsorbents (oxides and hydroxides, biosorbents, geomaterials, carbonaceous materials and industrial products and by-products) and its modifications from literature are surveyed and their adsorption capacities under various conditions are compared. The effect of other impurities on fluoride removal has also been discussed. This survey showed that various adsorbents, especially binary and trimetal oxides and hydroxides, have good potential for the fluoride removal from aquatic environments. PMID:28788194

  12. Influence of noble metals alloying additions on the corrosion behaviour of titanium in a fluoride-containing environment.

    Science.gov (United States)

    Rosalbino, F; Delsante, S; Borzone, G; Scavino, G

    2012-05-01

    Titanium alloys exhibit excellent corrosion resistance in most aqueous media due to the formation of a stable oxide film, and some of these alloys (particularly Ti-6Al-7Nb) have been chosen for surgical and odontological implants for their resistance and biocompatibility. Treatment with fluorides (F(-)) is known to be the main method for preventing plaque formation and dental caries. Toothpastes, mouthwashes, and prophylactic gels can contain from 200 to 20,000 ppm F(-) and can affect the corrosion behaviour of titanium alloy devices present in the oral cavity. In this work, the electrochemical corrosion behaviour of Ti-1M alloys (M = Ag, Au, Pd, Pt) was assessed in artificial saliva of pH = 3.0 containing 910 ppm F(-) (0.05 M NaF) through open circuit potential, E(OC), and electrochemical impedance spectroscopy (EIS) measurements. The corrosion behaviour of the Ti-6Al-7Nb commercial alloy was also evaluated for comparison. E (OC) measurements show an active behaviour for all the titanium alloys in fluoridated acidified saliva due to the presence of significant concentrations of HF and HF(2) (-) species that dissolve the spontaneous air-formed oxide film giving rise to surface activation. However, an increase in stability of the passive oxide layer and consequently a decrease in surface activation is observed for the Ti-1M alloys. This behaviour is confirmed by EIS measurements. In fact, the Ti-6Al-7Nb alloy exhibits lower impedance values as compared with Ti-1M alloys, the highest values being measured for the Ti-1Au alloy. The experimental results show that the corrosion resistance of the studied Ti-1M alloys is similar to or better than that of Ti-6Al-7Nb alloy currently used as biomaterial, suggesting their potential for dental applications.

  13. Investigation of Fluoride Removal Efficiency from Aqueous Solution by Pistachio and Almonds Crust

    Directory of Open Access Journals (Sweden)

    Maryam Khodadadi

    2015-06-01

    Full Text Available Introduction: Fluoride and its compounds are widely used in industries and then through effluent are released into the environment. The purpose of this study was to evaluate Efficiency of low cost adsorbents (pistachios coal in the removal of fluoride from aqueous solutions.  Methods: For the preparation of adsorbent, crust of pistachios deride, then washed with distilled water, then powder in the furnace for burning for 2 hours at temperatures of 500, 600, and 700 °C. The effect of changing pH, burning temperature of adsorbent, stirring speed, initial concentration of fluoride, retention time and adsorbent dose was studied. Concentration of fluoride measured according to standard method using spectrophotometer the data were analyzed using Excel software. Results: The results of these experiments showed that the burning adsorbent, temperature 500 ° C, PH of solution in the neutral range (pH = 7, adsorbent dose of 2 g/L for absorbing almonds and adsorbent dose of 3 g pistachio, contact time of 40 minutes for both adsorbent, initial fluoride concentration (5ppm for both absorbent without mixing, the optimal conditions for the efficiency of the absorber is as much as 90-80 percent. Discussion: According to the results, pistachio coal can be used with high efficiency for fluoride removal. 

  14. Crevice corrosion of alloy 22 in fluoride and chloride containing solutions

    International Nuclear Information System (INIS)

    Carranza, Ricardo M.; Rodriguez, Martin A.

    2005-01-01

    Alloy 22 (N06022) is highly resistant to localized corrosion. Alloy 22 may be susceptible to crevice corrosion in pure chloride (Cl - ) solutions under aggressive environmental conditions. The effect of the fluoride (F - ) on the susceptibility to crevice corrosion induced by chloride ions is still not well established. The objective of the present work was to explore the crevice corrosion resistance of this alloy to different mixtures of fluorides and chlorides. Cyclic potentiodynamic polarization (CPP) tests were conducted in deaerated aqueous solutions of pure halide ions and also in different mixtures of chloride and fluoride at 90 C degrees and pH 6. The range of chloride concentration [Cl - ] was 0.001 M ≤ [Cl - ] ≤ 1 M and the range of molar fluoride to chloride ratio [F - ]/[Cl - ] was 0.1≤ [F - ]/[Cl - ] ≤ 10. Results showed that Alloy 22 was susceptible to crevice corrosion in all the pure chloride solutions but not in the pure fluoride solutions. A molar ratio [F - ]/[Cl - ] ranging from 5 to 10 was required for the inhibition of crevice corrosion to be complete in the halide mixtures. A moderate or nil inhibitive effect was observed for molar ratios [F - ]/[Cl - ] [es

  15. Chemical treatment of ammonium fluoride solution in uranium reconversion plant

    International Nuclear Information System (INIS)

    Carvalho Frajndlich, E.U. de.

    1992-01-01

    A chemical procedure is described for the treatment of the filtrate, produced from the transformation of uranium hexafluoride (U F 6 ) into ammonium uranyl carbonate (AUC). This filtrate is an intermediate product in the U F 6 to uranium dioxide (U O 2 ) reconversion process. The described procedure recovers uranium as ammonium peroxide fluoro uranate (APOFU) by precipitation with hydrogen peroxide (H 2 O 2 ), and as later step, its calcium fluoride (CaF 2 ) co-precipitation. The recovered uranium is recycled to the AUC production plant. (author)

  16. Application of a new adsorbent for fluoride removal from aqueous solutions

    International Nuclear Information System (INIS)

    Srivastav, Arun Lal; Singh, Prabhat K.; Srivastava, Varsha; Sharma, Yogesh C.

    2013-01-01

    Highlights: • A new adsorbent has been prepared. • The adsorbent is non-toxic and easy to synthesize. • HBO 1 has displayed best capacity for the removal of fluoride. • Unlike most adsorbents, HBO 1 is suitable for the removal of fluoride from water. • The process of removal has been optimized. -- Abstract: Hydrous bismuth oxides (HBOs) have been investigated as a possible adsorbent for fluoride removal from water. Apart from bismuth trioxide (Bi 2 O 3 ) compound, three additional HBOs, named as HBO 1 , HBO 2 , and HBO 3 were synthesized in the laboratory and examined for their relative potentials for fluoride removal from aqueous solutions. HBO 1 was observed to have highest fluoride removal at 10 mg/L initial concentration in aqueous environment. Among competitive anions, sulfate and chloride affect the fluoride removal by HBO 1 more adversely than bicarbonate. Characterization of HBOs using X-ray diffraction (XRD) pattern analyses indicated crystalline structures, and the broad chemical composition of materials showed successive increase of Bi(OH) 3 from HBO 1 to HBO 3 , with decrease of BiOCl in the same order. Fourier Transform Infrared (FTIR) spectroscopy analyses indicated presence of Bi-O bond and successively increasing number of peaks corresponding to OH ion from HBO 1 to HBO 3 . Scanning Electron Microscopic (SEM) images of HBOs show rough and porous structure of the materials. Presence of higher proportion of chloride compound in HBO 1 with respect to others appears to be the factor responsible for its better performance in fluoride removal from aqueous solutions

  17. Removal of fluoride from aqueous solution by adsorption on hydroxyapatite (HAp using response surface methodology

    Directory of Open Access Journals (Sweden)

    M. Mourabet

    2015-11-01

    Full Text Available A study on the adsorption of fluoride onto hydroxyapatite was conducted and the process parameters were optimized using Response Surface Methodology (RSM. Hydroxyapatite has been characterized by using different physicochemical methods. In order to determine the effects of process parameters namely temperature (20–40 °C, initial solution pH (4–11, adsorbent dose (0.1–0.3 g and initial fluoride concentration (10–20 mg L−1 on fluoride uptake from aqueous solution, a three-level, four-factor, Box–Behnken design has been employed. The second order mathematical model was developed by regression analysis of the experimental data obtained from 29 batch runs. The optimum pH, temperature, adsorbent dose and initial concentration were found by desirability function to be 4.16, 39.02 °C, 0.28 g and 20 mg L−1, respectively. Fluoride removal was 86.34% at the optimum combination of process parameters. Dynamic adsorption data were applied to pseudo-first-order and pseudo-second-order rate equations. The time data fitted well to pseudo second order kinetic model. According to the correlation coefficients, the adsorption of fluoride on the hydroxyapatite was correlated well with the Langmuir and Freundlich models.

  18. Corrosive effects of fluoride on titanium: investigation by X-ray photoelectron spectroscopy, atomic force microscopy, and human epithelial cell culturing.

    Science.gov (United States)

    Stájer, Anette; Ungvári, Krisztina; Pelsoczi, István K; Polyánka, Hilda; Oszkó, Albert; Mihalik, Erzsébet; Rakonczay, Zoltán; Radnai, Márta; Kemény, Lajos; Fazekas, András; Turzó, Kinga

    2008-11-01

    High fluoride (F(-)) concentrations and acidic pH impair the corrosion resistance of titanium (Ti). Effects of F(-)-containing caries-preventive prophylactic rinses, and gels on Ti were investigated by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). Human epithelial cell attachment and proliferation were investigated by dimethylthiazol-diphenyl tetrazolium bromide (MTT) and protein content assays. Aqueous 1% NaF solution (3800 ppm F(-), pH 4.5) or high (12,500 ppm) F(-) content gel (pH 4.8) strongly corroded the surface and modified its composition. XPS revealed formation of a strongly bound F(-)-containing complex (Na(2)TiF(6)). AFM indicated an increase in roughness (R(a)) of the surfaces: 10-fold for the NaF solution and smaller for the gel or a mouthwash (250 ppm F(-), pH 4.4). MTT revealed that cell attachment was significantly increased by the gel, but was not disturbed by either the mouthwash or the NaF. Cell proliferation determined by MTT decreased significantly only for the NaF-treated samples; protein content assay experiments showed no such effect. This study indicates that epithelial cell culturing results can depend on the method used, and the adverse effects of a high F(-) concentration and low pH should be considered when prophylactic gels are applied by patients with Ti implants or other dental devices.

  19. Corrosion resistance of stainless steel, nickel-titanium, titanium molybdenum alloy, and ion-implanted titanium molybdenum alloy archwires in acidic fluoride-containing artificial saliva: An in vitro study

    Directory of Open Access Journals (Sweden)

    Venith Jojee Pulikkottil

    2016-01-01

    Full Text Available Objective: (1 To evaluate the corrosion resistance of four different orthodontic archwires and to determine the effect of 0.5% NaF (simulating high fluoride-containing toothpaste of about 2250 ppm on corrosion resistance of these archwires. (2 To assess whether surface roughness (Ra is the primary factor influencing the corrosion resistance of these archwires. Materials and Methods: Four different archwires (stainless steel [SS], nickel-titanium [NiTi], titanium molybdenum alloy [TMA], and ion-implanted TMA were considered for this study. Surface characteristics were analyzed using scanning electron microscopy, atomic force microscopy (AFM, and energy dispersive spectroscopy. Linear polarization test, a fast electrochemical technique, was used to evaluate the corrosion resistance, in terms of polarization resistance of four different archwires in artificial saliva with NaF concentrations of 0% and 0.5%. Statistical analysis was performed by one-way analysis of variance. Results: The potentiostatic study reveals that the corrosion resistance of low-friction TMA (L-TMA > TMA > NiTi > SS. AFM analysis showed the surface Ra of TMA > NiTi > L-TMA > SS. This indicates that the chemical composition of the wire is the primary influential factor to have high corrosion resistance and surface Ra is only secondary. The corrosion resistance of all wires had reduced significantly in 0.5% acidic fluoride-containing artificial saliva due to formation of fluoride complex compound. Conclusion: The presence of 0.5% NaF in artificial saliva was detrimental to the corrosion resistance of the orthodontic archwires. Therefore, complete removal of residual high-fluorinated toothpastes from the crevice between archwire and bracket during tooth brushing is mandatory.

  20. Corrosion resistance of titanium-containing dental orthodontic wires in fluoride-containing artificial saliva

    International Nuclear Information System (INIS)

    Lee, T.-H.; Wang, C.-C.; Huang, T.-K.; Chen, L.-K.; Chou, M.-Y.; Huang, H.-H.

    2009-01-01

    This study was to investigate the corrosion resistance of different Ti-containing dental orthodontic wires (including Ni-Ti, Ni-Ti-Cu, Ti-Mo-Zr-Sn, and Ti-Nb alloys) in acidic fluoride-containing artificial saliva using cyclic potentiodynamic polarization curve measurements. Different NaF concentrations (0%, 0.2%, and 0.5%), simulating the fluoride contents in commercial toothpastes, were added to the artificial saliva. Surface characterization was analyzed using X-ray photoelectron spectrometry. Cyclic potentiodynamic polarization curves showed that the presence of fluoride ions, especially 0.5% NaF, was detrimental to the protective ability of the TiO 2 -based film on the Ti-containing wires. This might lead to a decrease in the corrosion resistance of the tested alloys, i.e. an increase in the corrosion rate and anodic current density and a decrease in the passive film breakdown potential. Among the tested Ti-containing wires, the Ni-Ti and Ni-Ti-Cu wires containing mainly TiO 2 on surface film were more susceptible to fluoride-enhanced corrosion, while the Ti-Mo-Zr-Sn and Ti-Nb wires containing MoO 3 /ZrO 2 /SnO and Nb 2 O 5 , respectively, along with TiO 2 on surface film were pitting corrosion resistant and showed a lower susceptibility to fluoride-enhanced corrosion. The difference in corrosion resistance of the tested commercial Ti-containing dental orthodontic wires was significantly dependent on the passive film characteristics on wires' surface.

  1. Corrosion resistance of titanium-containing dental orthodontic wires in fluoride-containing artificial saliva

    Energy Technology Data Exchange (ETDEWEB)

    Lee, T.-H. [Institute of Medicine, Chung Shan Medical University, Taichung 402, Taiwan (China); Department of Dentistry, Chung Shan Medical University Hospital, Taichung 402, Taiwan (China); Wang, C.-C. [Department of Dental Laboratory Technology, Min-Hwei College of Health Care Management, Tainan County 736, Taiwan (China); Huang, T.-K. [College of Dental Medicine, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Chen, L.-K. [Department of Dentistry, Taipei City Hospital, Taipei 115, Taiwan (China); Chou, M.-Y. [Institute of Medicine, Chung Shan Medical University, Taichung 402, Taiwan (China); Department of Dentistry, Chung Shan Medical University Hospital, Taichung 402, Taiwan (China); Huang, H.-H., E-mail: hhhuang@ym.edu.t [Department of Dentistry, Taipei City Hospital, Taipei 115, Taiwan (China); Department of Dentistry, National Yang-Ming University, Taipei 112, Taiwan (China); Institute of Oral Biology, National Yang-Ming University, Taipei 112, Taiwan (China)

    2009-11-20

    This study was to investigate the corrosion resistance of different Ti-containing dental orthodontic wires (including Ni-Ti, Ni-Ti-Cu, Ti-Mo-Zr-Sn, and Ti-Nb alloys) in acidic fluoride-containing artificial saliva using cyclic potentiodynamic polarization curve measurements. Different NaF concentrations (0%, 0.2%, and 0.5%), simulating the fluoride contents in commercial toothpastes, were added to the artificial saliva. Surface characterization was analyzed using X-ray photoelectron spectrometry. Cyclic potentiodynamic polarization curves showed that the presence of fluoride ions, especially 0.5% NaF, was detrimental to the protective ability of the TiO{sub 2}-based film on the Ti-containing wires. This might lead to a decrease in the corrosion resistance of the tested alloys, i.e. an increase in the corrosion rate and anodic current density and a decrease in the passive film breakdown potential. Among the tested Ti-containing wires, the Ni-Ti and Ni-Ti-Cu wires containing mainly TiO{sub 2} on surface film were more susceptible to fluoride-enhanced corrosion, while the Ti-Mo-Zr-Sn and Ti-Nb wires containing MoO{sub 3}/ZrO{sub 2}/SnO and Nb{sub 2}O{sub 5}, respectively, along with TiO{sub 2} on surface film were pitting corrosion resistant and showed a lower susceptibility to fluoride-enhanced corrosion. The difference in corrosion resistance of the tested commercial Ti-containing dental orthodontic wires was significantly dependent on the passive film characteristics on wires' surface.

  2. The removal of fluoride from aqueous solution by a lateritic soil adsorption: Kinetic and equilibrium studies.

    Science.gov (United States)

    Iriel, Analia; Bruneel, Stijn P; Schenone, Nahuel; Cirelli, Alicia Fernández

    2018-03-01

    The use of natural sorbents to remove fluoride from drinking water is a promising alternative because of its low-cost and easy implementation. In this article, fluoride adsorption on a latosol soil from Misiones province (Argentina) was studied regarding kinetic and equilibrium aspects. Experiments were conducted in batch at room temperature under controlled conditions of pH 4-8) and ionic strength (1-10mM KNO 3 ). Experimental data indicated that adsorption processes followed a PSO kinetic where initial rates have showed to be influenced by pH solution. The necessary time to reach an equilibrium state had resulted approximately 30min. Equilibrium adsorption studies were performed at pH 8 which is similar to the natural groundwater. For that, fluoride adsorption data were successfully adjusted to Dubinin-Ataskhov model determining that the fluoride adsorption onto soil particles mainly followed a physical mechanism with a removal capacity of 0.48mgg -1 . Finally, a natural groundwater was tested with laterite obtaining a reduction close to 30% from initial concentration and without changing significantly the physicochemical properties of the natural water. Therefore, it was concluded that the use of lateritic soils for fluoride removal is very promising on a domestic scale. Copyright © 2017 Elsevier Inc. All rights reserved.

  3. Removal of Fluoride Ion from Aqueous Solution by Nanocomposite Hydrogel Based on Starch/Sodium Acrylate/Nano Aluminum Oxide

    Directory of Open Access Journals (Sweden)

    Aboulfazl Barati

    2014-01-01

    Full Text Available Determination of fluoride in drinking water has received increasing interest, due to its beneficial and detrimental effects on health. Contamination of drinking water by fluoride can cause potential hazards to human health. In recent years, considerable attention has been given to different methods for the removal of fluoride from drinking and waste waters. The aim of this research was to investigate the effect of nano composite hydrogel based on starch/sodium acrylate/aluminum oxide in reduction of fluoride concentration in drinking water and industrial waste water. In a batch system, the dynamic and equilibrium adsorption of fluoride ions were studied with respect to changes in determining parameters such as pH, contact time, initial fluoride concentration, starch/acrylic acid weight ratio and weight percent of nano aluminum oxide. The obtained equilibrium adsorption data were fitted with Langmuir and Freundlich models, as well as the kinetic data with pseudo-first order and pseudo- second order models. The results showed that optimum pH was found to be in the range of 5 to 7. Removal efficiency of fluoride was increased with decreases in initial concentration of fluoride. Sixty percent of initial value of fluoride solution was removed by nano composite hydrogel (4 wt% of nano aluminum oxide at 240 min (initial fluoride concentration = 5 ppm, pH 6.8 and temperature = 25ºC. Under the same condition, the equilibrium adsorption of fluoride ions was 85% and 68% for initial solution concentration of 5 and 10 ppm, respectively. Adsorption isotherm data showed that the fluoride sorption followed the Langmuir model. Kinetics of sorption of fluoride onto nano composite hydrogel was described by pseudo-first order model.

  4. Ion spatial distributions at the liquid-vapor interface of aqueous potassium fluoride solutions

    Energy Technology Data Exchange (ETDEWEB)

    Brown, M A; D' Auria, R; Kuo, I W; Krisch, M J; Starr, D E; Bluhm, H; Tobias, D J; Hemminger, J C

    2008-04-23

    X-ray photoemission spectroscopy operating under ambient pressure conditions is used to probe ion distributions throughout the interfacial region of a free-flowing aqueous liquid micro-jet of 6 M potassium fluoride. Varying the energy of the ejected photoelectrons by carrying out experiments as a function of x-ray wavelength measures the composition of the aqueous-vapor interfacial region at various depths. The F{sup -} to K{sup +} atomic ratio is equal to unity throughout the interfacial region to a depth of 2 nm. The experimental ion profiles are compared with the results of a classical molecular dynamics simulation of a 6 M aqueous KF solution employing polarizable potentials. The experimental results are in qualitative agreement with the simulations when integrated over an exponentially decaying probe depth characteristic of an APPES experiment. First principles molecular dynamics simulations have been used to calculate the potential of mean force for moving a fluoride anion across the air-water interface. The results show that the fluoride anion is repelled from the interface, and this is consistent with the depletion of F{sup -} at the interface revealed by the APPES experiment and polarizable force field-based molecular dynamics simulation. Together, the APPES and MD simulation data provide a detailed description of the aqueous-vapor interface of alkali fluoride systems. This work offers the first direct observation of the ion distribution at a potassium fluoride aqueous solution interface. The current experimental results are compared to those previously obtained for saturated solutions of KBr and KI to underscore the strong difference in surface propensity between soft/large and hard/small halide ions in aqueous solution.

  5. Titanium

    Science.gov (United States)

    Woodruff, Laurel G.; Bedinger, George M.; Piatak, Nadine M.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

    2017-12-19

    Titanium is a mineral commodity that is essential to the smooth functioning of modern industrial economies. Most of the titanium produced is refined into titanium dioxide, which has a high refractive index and is thus able to impart a durable white color to paint, paper, plastic, rubber, and wallboard. Because of their high strength-to-weight ratio and corrosion resistance, titanium metal and titanium metal alloys are used in the aerospace industry as well as for welding rod coatings, biological implants, and consumer goods.Ilmenite and rutile are currently the principal titanium-bearing ore minerals, although other minerals, including anatase, perovskite, and titanomagnetite, could have economic importance in the future. Ilmenite is currently being mined from two large magmatic deposits hosted in rocks of Proterozoic-age anorthosite plutonic suites. Most rutile and nearly one-half of the ilmenite produced are from heavy-mineral alluvial, fluvial, and eolian deposits. Titanium-bearing minerals occur in diverse geologic settings, but many of the known deposits are currently subeconomic for titanium because of complications related to the mineralogy or because of the presence of trace contaminants that can compromise the pigment production process.Global production of titanium minerals is currently dominated by Australia, Canada, Norway, and South Africa; additional amounts are produced in Brazil, India, Madagascar, Mozambique, Sierra Leone, and Sri Lanka. The United States accounts for about 4 percent of the total world production of titanium minerals and is heavily dependent on imports of titanium mineral concentrates to meet its domestic needs.Titanium occurs only in silicate or oxide minerals and never in sulfide minerals. Environmental considerations for titanium mining are related to waste rock disposal and the impact of trace constituents on water quality. Because titanium is generally inert in the environment, human health risks from titanium and titanium

  6. Fluorescent molecule incorporated metal-organic framework for fluoride sensing in aqueous solution

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Xudong, E-mail: zhaoxd_tykj@163.com; Wang, Yuanyang; Hao, Xiuli; Liu, Wen, E-mail: 13700509372@163.com

    2017-04-30

    Highlights: • Fluorescein sodium was successfully encapsulated in UiO-66 via in-situ synthesis. • FS@UiO-66 is one of the few Zr-MOF-based probes for fluoride so far. • FS@UiO-66 is a highly effective, fast-response and naked-eye sensor for fluoride. - Abstract: In this work, the fluorescent molecule (fluorescein sodium, FS) was successfully incorporated in the zirconium-based MOF (UiO-66) via in-situ synthesis method, which can be confirmed by FTIR spectra and fluorescence microscopic images. Based on this in-situ synthesis strategy, FS molecule can be immobilized tightly in the framework. Furthermore, the resulting FS@UiO-66 demonstrates to be a highly selective, real-time and naked-eye chemical sensor for fluoride in aqueous solution, which is mainly due to the release of FS molecule from FS@UiO-66 into the aqueous solution. Meanwhile, to the best of our knowledge, such Zr-MOF-based fluoride sensor is very rare so far. These results provide a promising approach to rationally design novel MOF-based fluorescent sensor for the target molecules.

  7. Pulse-radiolytic investigation of the reduction of titanium(III) ions in aqueous solutions

    International Nuclear Information System (INIS)

    Micic, O.I.; Nenadovic, M.T.

    1979-01-01

    The absorption spectrum and decay kinetics of intermediates formed by the reaction of titanium(III) ions with H atoms, hydrated electrons, and carboxyl radicals have been studied in aqueous solution using the pulse-radiolysis technique. The product of the reaction with H atoms in acid solution is a Ti 3+ -H hydride intermediate which decomposes by a first-order process with a half-life of ca. 3 s. Titanium(II) is formed by reaction with hydrated electrons and CO 2 H radicals. The absorption spectrum of titanium(II) and the kinetics of its reactions are reported and discussed. The formation of molecular hydrogen by reaction of Ti 2+ with water is suppressed by the other solutes in the solutions. Titanium(III) reacts with CO 2 H, CH 2 CO 2 H, and CH(CO 2 H) 2 radicals to give titanium-radical complexes. (author)

  8. Characterization of Titanium Oxide Nanoparticles Obtained by Hydrolysis Reaction of Ethylene Glycol Solution of Alkoxide

    International Nuclear Information System (INIS)

    Uekawa, N.; Endo, N.; Ishii, K.; Kojima, T.; Kakegawa, K.

    2012-01-01

    Transparent and stable sols of titanium oxide nanoparticles were obtained by heating a mixture of ethylene glycol solution of titanium tetraisopropoxide (TIP) and a NH 3 aqueous solution at 368 K for 24 h. The concentration of NH 3 aqueous solution affected the structure of the obtained titanium oxide nanoparticles. For NH 3 aqueous solution concentrations higher than 0.2 mol/L, a mixture of anatase TiO 2 nanoparticles and layered titanic acid nanoparticles was obtained. The obtained sol was very stable without formation of aggregated precipitates and gels. Coordination of ethylene glycol to Ti4+ ions inhibited the rapid hydrolysis reaction and aggregation of the obtained nanoparticles. The obtained titanium oxide nanoparticles had a large specific surface area: larger than 350 m2/g. The obtained titanium oxide nanoparticles showed an enhanced adsorption towards the cationic dye molecules. The selective adsorption corresponded to presence of layered titanic acid on the obtained anatase TiO 2 nanoparticles.

  9. Characterization of Titanium Oxide Nanoparticles Obtained by Hydrolysis Reaction of Ethylene Glycol Solution of Alkoxide

    OpenAIRE

    Naofumi Uekawa; Naoya Endo; Keisuke Ishii; Takashi Kojima; Kazuyuki Kakegawa

    2012-01-01

    Transparent and stable sols of titanium oxide nanoparticles were obtained by heating a mixture of ethylene glycol solution of titanium tetraisopropoxide (TIP) and a NH3 aqueous solution at 368 K for 24 h. The concentration of NH3 aqueous solution affected the structure of the obtained titanium oxide nanoparticles. For NH3 aqueous solution concentrations higher than 0.2 mol/L, a mixture of anatase TiO2 nanoparticles and layered titanic acid nanoparticles was obtained. The obtained sol was very...

  10. Effect of Copper Oxide, Titanium Dioxide, and Lithium Fluoride on the Thermal Behavior and Decomposition Kinetics of Ammonium Nitrate

    Science.gov (United States)

    Vargeese, Anuj A.; Mija, S. J.; Muralidharan, Krishnamurthi

    2014-07-01

    Ammonium nitrate (AN) is crystallized along with copper oxide, titanium dioxide, and lithium fluoride. Thermal kinetic constants for the decomposition reaction of the samples were calculated by model-free (Friedman's differential and Vyzovkins nonlinear integral) and model-fitting (Coats-Redfern) methods. To determine the decomposition mechanisms, 12 solid-state mechanisms were tested using the Coats-Redfern method. The results of the Coats-Redfern method show that the decomposition mechanism for all samples is the contracting cylinder mechanism. The phase behavior of the obtained samples was evaluated by differential scanning calorimetry (DSC), and structural properties were determined by X-ray powder diffraction (XRPD). The results indicate that copper oxide modifies the phase transition behavior and can catalyze AN decomposition, whereas LiF inhibits AN decomposition, and TiO2 shows no influence on the rate of decomposition. Possible explanations for these results are discussed. Supplementary materials are available for this article. Go to the publisher's online edition of the Journal of Energetic Materials to view the free supplemental file.

  11. Use of response surface methodology for optimization of fluoride adsorption in an aqueous solution by Brushite

    Directory of Open Access Journals (Sweden)

    M. Mourabet

    2017-05-01

    Full Text Available In the present study, Response surface methodology (RSM was employed for the removal of fluoride on Brushite and the process parameters were optimized. Four important process parameters including initial fluoride concentration (40–50 mg/L, pH (4–11, temperature (10–40 °C and B dose (0.05–0.15 g were optimized to obtain the best response of fluoride removal using the statistical Box–Behnken design. The experimental data obtained were analyzed by analysis of variance (ANOVA and fitted to a second-order polynomial equation using multiple regression analysis. Numerical optimization applying desirability function was used to identify the optimum conditions for maximum removal of fluoride. The optimum conditions were found to be initial concentration = 49.06 mg/L, initial solution pH = 5.36, adsorbent dose = 0.15 g and temperature = 31.96 °C. A confirmatory experiment was performed to evaluate the accuracy of the optimization procedure and maximum fluoride removal of 88.78% was achieved under the optimized conditions. Several error analysis equations were used to measure the goodness-of-fit. Kinetic studies showed that the adsorption followed a pseudo-second order reaction. The equilibrium data were analyzed using Langmuir, Freundlich, and Sips isotherm models at different temperatures. The Langmuir model was found to be describing the data. The adsorption capacity from the Langmuir isotherm (QL was found to be 29.212, 35.952 and 36.260 mg/g at 298, 303, and 313 K respectively.

  12. Study of the physicochemical properties of the interface between titanium dioxide and various aqueous solutions

    International Nuclear Information System (INIS)

    Mazilier, C.

    1988-01-01

    The aim of this work is the study of ion exchange capacity of titanium dioxide in view of high temperature water purification and radioactive effluent processing because of its resistance to heat and radiations. Titanium dioxide is obtained by alkaline hydrolysis of an aqueous solution of Ti (IV) and is characterized by analytical physical chemistry methods. Interface between Ti0 2 and simple aqueous solutions (electrolytes) is more particularly studied by potentiometry [fr

  13. Efficiency Comparison of Modified-Clay and Lime-Marlin the Adsorption of Fluoride from Aqueous Solution

    Directory of Open Access Journals (Sweden)

    Mohammad Taghi Samadi

    2016-06-01

    Full Text Available Background and purpose: Fluoride is one of the common anion in water that its concentration varies in different water supplies. Most of the body's requirement for fluoride is supplied through drinking water. Fluoride in low concentration is essential for human health but in high concentration is very hazardous for human health. The efficiency of modified-clay and lime-marl were investigated in this research as an adsorbent for the elimination of fluoride from aqueou solution.  Methods: In this study, the capability of modified-clay and lime-marl to adsorb fluoride ions was conducted using a series of batch tests in a shaker-incubator instrument. The effect of experimental parameters such as pH (4,7,10,  adsorbent dosage (1,5,10 g/L, initial fluoride concentration  (5,10,15 mg/L andcontact time (15-120 min were evaluated. The morphological and micro-structural character of  modified-clay and lime-marl have performed by using X-ray diffraction (XRD. The formation of the carboxylic functional groups was verified by Fourier transform infrared spectra (FT-IR.  Findings: results well demonstrate higher removal efficiency of fluoride was 95.23% and 28.71 by clay-modified and lime-marl, respectively; at 10 mg/L of fluoride concentration and 60 min contact time. The adsorption kinetics fitted well using the pseudo second-order kinetic model; however, equlibrium data were best fitted onto Langmiur isotherm model. The maximum adsorption capacities of modified-clay and lime-marl for fluoride were found to be 4.43 mg/g and 1.32 mg/g, respectively. Conclusion: According to our finding, it proposed that adsorption process by using modified clay is very efficient and economic process for fluoride removal from aqueous solution.

  14. The Mechanical Behavior Variation of Nickel - Titanium Orthodontic Wires in Different Fluoride Mouthwash

    Directory of Open Access Journals (Sweden)

    Ilnaz haj Hemati

    2016-12-01

    Full Text Available In this study, an orthodontic arch wire of Ni-Ti alloy made by Germany in four different mouthwashes contain fluoride was investigated in mechanical behavior. This research focused on the mechanical behavior changes in different mouthwashes. The Mouthwashes were chosen from most popular one in Iran including Oral-B, Gum, and Behsa Mouthwash. The wires after 3 month in touch with mouthwashes were studied and the result was presented. The result show that the lowest power to reshape the wire, is for the wire in Crest case (3. The maximum power assigns to wire in Behsa case (1. Also, the shortest treatment period is for wire in Behsa mouthwash case (1 with 0.087 Nm strain energy and the maximum duration of therapy is related to case (3 Crest mouthwash with 0.039 Nm. Moreover, the wires in Oral-b (0.095 Nm has the lowest and Gum mouthwash (0.140 Nm has the highest energy intake. The energy absorbed by the wires in Behsa and Crest is in the middle. Finally, it is proposed that patient could used all mouthwash but based on their condition, one product will be useful.

  15. The influence of salivary variables on fluoride retention in dental plaque exposed to a mineral-enriching solution.

    Science.gov (United States)

    Kato, K; Nakagaki, H; Arai, K; Pearce, E I F

    2002-01-01

    This study was carried out to examine interindividual differences in salivary variables related to plaque accumulation and to estimate their influence on the fluoride retention in plaque in vivo by a mineral-enriching solution. Two saliva samples were taken from 10 subjects, once after brushing and once after 24 h without brushing. Calcium, phosphate and monofluorophosphatase (MFPase) activity in the saliva samples were determined. The salivary flow rate and the debris index were also recorded. After plaque had formed over 3 days within in situ plaque-generating devices, subjects were instructed to rinse with a mineral-enriching mouthrinse three times a day on 4 consecutive days. Plaque exposed to distilled water plus flavoring agents served as a control. Fluoride-free dentifrice was used during the experimental period. Twenty-four hours after the last rinsing, the samples were removed from the mouth, and fluoride and mineral distributions in plaque analyzed using a method previously reported by the authors. Salivary flow, MFPase activity and calcium concentration in saliva were significantly higher after 24 h of plaque accumulation. Rinsing with the mineral-enriching solution produced retention of fluoride and phosphate in the outer and middle layers of plaque. Salivary calcium concentration had a direct effect on fluoride uptake in plaque, but no obvious relationship was found between other salivary variables and the plaque fluoride retention. The salivary calcium effect may be due to enhanced bacterial cell wall binding of fluoride via calcium bridging. Copyright 2002 S. Karger AG, Basel

  16. Mg-doped nano ferrihydrite - A new adsorbent for fluoride removal from aqueous solutions

    Energy Technology Data Exchange (ETDEWEB)

    Mohapatra, M., E-mail: mamatamohapatra@yahoo.com [Institute of Minerals and Materials Technology, Bhubaneswar 751 013, Orissa (India); Hariprasad, D.; Mohapatra, L.; Anand, S.; Mishra, B.K. [Institute of Minerals and Materials Technology, Bhubaneswar 751 013, Orissa (India)

    2012-03-01

    The present study evaluates synthesized Mg-doped nano ferrihydrite powder as an adsorbent for F{sup -} removal from aqueous solutions. High surface area Mg-doped ferrihydrite was prepared by co-precipitation method under controlled conditions. Samples were prepared by varying Mg content in the range of 0.39-1.12%. Preliminary test work revealed that under similar conditions, with the increase in Mg content from 0.39 to 0.98% in doped ferrihydrite, % F{sup -} adsorption increased from 66 to 91%. Hence this sample was characterized by XRD, TEM, SAED and TG-DTA. Batch adsorption experiments were carried out by varying contact time (30-480 min), initial pH (1.0-10), initial fluoride concentration (10-150 mg/L), adsorbent dose (0.5-4 g/L), temperature (20-45 Degree-Sign C) and Cl{sup -} or SO{sub 4}{sup 2-} concentrations (nil to 50 mg/L). The results showed 0.98% Mg-doped ferrihydrite to be an excellent fluoride adsorbent giving maximum adsorption capacity of 64 mg/g. The time data fitted well to pseudo second order kinetic model. The isothermal data followed Langmuir model. Thermodynamic parameters confirmed the adsorption process to be spontaneous and endothermic. 89% of fluoride could be desorbed from loaded sample using 1 M NaOH.

  17. One-Step Synthesis of Titanium Oxyhydroxy-Fluoride Rods and Research on the Electrochemical Performance for Lithium-ion Batteries and Sodium-ion Batteries.

    Science.gov (United States)

    Li, Biao; Gao, Zhan; Wang, Dake; Hao, Qiaoyan; Wang, Yan; Wang, Yongkun; Tang, Kaibin

    2015-12-01

    Titanium oxyhydroxy-fluoride, TiO0.9(OH)0.9F1.2 · 0.59H2O rods with a hexagonal tungsten bronze (HTB) structure, was synthesized via a facile one-step solvothermal method. The structure, morphology, and component of the products were characterized by X-ray powder diffraction (XRD), thermogravimetry (TG), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), inductively coupled plasma optical emission spectroscopy (ICP-OES), ion chromatograph, energy-dispersive X-ray (EDX) analyses, and so on. Different rod morphologies which ranged from nanoscale to submicron scale were simply obtained by adjusting reaction conditions. With one-dimension channels for Li/Na intercalation/de-intercalation, the electrochemical performance of titanium oxyhydroxy-fluoride for both lithium-ion batteries (LIBs) and sodium-ion batteries (SIBs) was also studied. Electrochemical tests revealed that, for LIBs, titanium oxyhydroxy-fluoride exhibited a stabilized reversible capacity of 200 mAh g(-1) at 25 mA g(-1) up to 120 cycles in the electrode potential range of 3.0-1.2 V and 140 mAh g(-1) at 250 mA g(-1) up to 500 cycles, especially; for SIBs, a high capacity of 100 mAh g(-1) was maintained at 25 mA g(-1) after 115 cycles in the potential range of 2.9-0.5 V.

  18. Photocatalytic Degradation of Oil using Polyvinylidene Fluoride/Titanium Dioxide Composite Membrane for Oily Wastewater Treatment

    Directory of Open Access Journals (Sweden)

    Rusli Ummi Nadiah

    2016-01-01

    Full Text Available Production of industrial wastewater is increasing as the oil and gas industry grows rapidly over the years. The constituents in the industrial wastewater such as organic and inorganic matters, dispersed and lubricant oil and metals which have high toxicity become the major concern to the environment and ecosystem. There are many technologies are being used for oil removal from industrial wastewater. However, there are still needs to find an effective technology to treat oily wastewater before in can be discharge safely to the environment. Membrane technology is an attractive separation technology to treat oily wastewater. The aim of this study is to fabricate polyvinylidene/titanium dioxide (PVDF/TiO2 composite membrane with further treatment using hot pressed method to enhance the adhesion between TiO2 with the membrane surfaces. In this study the structural and physical properties of fabricated membrane were conducted using X-ray diffraction (XRD and Fourier transform infrared spectroscopy (FTIR respectively. The photocatalytic degradation of oil was measured using UV-Vis Spectroscopy. The FTIR results confirmed that, hot pressed PVDF/TiO2 membrane TiO2 was successfully deposited onto PVDF membranes surface and XRD results shows that the XRD pattern of PVDF//TiO2 found that the crystalline structure was remained unchanged after hot pressed. Clear water was obtained after synthetic oily wastewater was exposed to visible light for at least 6 hours. In conclusion, PVDF/TiO2 composite membrane can be a potential candidate to degrade oil in oily wastewater and suggested to possess an excellent performance if perform simultaneously with membrane separation process.

  19. Synthesis of pillar and microsphere-like magnesium oxide particles and their fluoride adsorption performance in aqueous solutions

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Sang Gool; Ha, Jong-Wook; Sohn, Eun-Ho; Park, In Jun; Lee, Soo-Bok [Korea Research Institute of Chemical Technology, Daejeon (Korea, Republic of)

    2017-10-15

    We synthesized pillar and microsphere-like MgO particles and their fluoride removal performance. Samples of MgO were synthesized by calcination of precursors derived from MgCO{sub 3}·3H{sub 2}O and characterized using field emission scanning electron microscopy, X-ray diffraction, and N{sub 2} adsorption-desorption isotherms. The fluoride removal performance of the MgO samples was investigated in terms of adsorption kinetics and adsorption equilibrium. The effects of pH and the presence of other anions on the fluoride adsorption were also considered. The adsorption capacities of pillar and microsphere-like MgO particles were 151.51 and 166.66mg/g, respectively. The pH of the aqueous solutions did not significantly affect the fluoride adsorption at pH 9 or lower. Except for phosphate, the effect of co-existing anions on fluoride adsorption was not considerable. Fluoride removal occurred through the substitution of hydroxyl groups on the surface of MgO with fluorides.

  20. Factors influencing the removal of fluoride from aqueous solution by calcined Mg-Al-CO{sub 3} layered double hydroxides

    Energy Technology Data Exchange (ETDEWEB)

    Lv Liang [Key Laboratory of Science and Technology of Controllable Chemical Reactions, Ministry of Education, Beijing University of Chemical Technology, Box 98, 15 Bei San Huan Dong Lu, Chao Yang District, Beijing 100029 (China); West Branch of Zhejiang University of Technology, Zhejiang 324006 (China); He Jing [Key Laboratory of Science and Technology of Controllable Chemical Reactions, Ministry of Education, Beijing University of Chemical Technology, Box 98, 15 Bei San Huan Dong Lu, Chao Yang District, Beijing 100029 (China); Wei Min [Key Laboratory of Science and Technology of Controllable Chemical Reactions, Ministry of Education, Beijing University of Chemical Technology, Box 98, 15 Bei San Huan Dong Lu, Chao Yang District, Beijing 100029 (China); Evans, D.G. [Key Laboratory of Science and Technology of Controllable Chemical Reactions, Ministry of Education, Beijing University of Chemical Technology, Box 98, 15 Bei San Huan Dong Lu, Chao Yang District, Beijing 100029 (China); Duan Xue [Key Laboratory of Science and Technology of Controllable Chemical Reactions, Ministry of Education, Beijing University of Chemical Technology, Box 98, 15 Bei San Huan Dong Lu, Chao Yang District, Beijing 100029 (China)]. E-mail: duanx@mail.buct.edu.cn

    2006-05-20

    Layered double hydroxides (LDH) calcined at different temperatures (denoted as CLDH) have been demonstrated to recover their original layered structure in the presence of appropriate anions. In the light of this so-called 'memory effect', a study of removal of fluoride from aqueous solution by calcined Mg-Al-CO{sub 3}-LDH has been carried out. The LDH calcined at 500 deg. C had the highest capacity of removal of fluoride ion, because of retention of its intrinsic structure. The CLDH with an Mg/Al ratio of 2 has a remarkable ability to adsorb anions. The adsorption loading is higher for the calcined Mg-Al-LDH than for calcined Zn-Al and Ni-Al-LDH. The influence of varying the conditions for removal of fluoride, such as the pH of aqueous solution, the initial fluoride concentration, the dosage of adsorbent, and temperature on removal of fluoride have been investigated. The influence of co-existing anions in fluoride aqueous solution indicates that the percentage of removal of fluoride increased in order PO{sub 4} {sup 3-} < Cl{sup -} {approx} SO{sub 4} {sup 2-} < Br{sup -} << NO{sub 3} {sup -}. It was found that maximum removal of fluoride from aqueous solutions was obtained in 6 h at pH 6.0 with an initial concentration of 50 mg/L, and that the retention of fluoride ions by the CLDH material was 98% or higher. The residual fluoride concentration was found to be 0.4 mg/L with an initial concentration of 20 mg/L, which meets the national standard for drinking water quality. The Freundlich isotherm and Langmuir isotherm were used to fit the data of equilibrium experiments. The results of X-ray diffraction, FT-IR and TG-MS demonstrate that the adsorption phenomenon is accompanied by rehydration with concomitant uptake of fluoride ions to rebuild the initial layered structure.

  1. Synthesis of hydroxyapatite/multi-walled carbon nanotubes for the removal of fluoride ions from solution

    International Nuclear Information System (INIS)

    Ruan, Zhongyuan; Tian, Yaxi; Ruan, Jifu; Cui, Guijia; Iqbal, Kanwal; Iqbal, Anam; Ye, Herui; Yang, Zhangzhong; Yan, Shiqiang

    2017-01-01

    Graphical abstract: Hydroxyapatite nucleated and grown on Multi-walled carbon nanotubes (HA-MWCNTs) showed enhanced fluoride removal performance. - Highlights: • Noval HA nanoparticles and HA-MWCNTs composites were successfully synthesized for the first time. • The synthesized HA-MWCNTs composites exhibited a higher defluoridation capacity of 39.22 mg g"−"1. • It could reduced the fluoride concentration of the real waste water from 8.79 mg L"−"1 to approximately 0.25 mg L"−"1. - Abstract: A novel composite material, hydroxyapatite (HA)-multi-walled carbon nanotubes (MWCNTs), was prepared using a simple in-situ sol-gel method, and was used for the first time to remove fluoride from water. The novel HA-MWCNTs were characterized using TEM, FT-IR, BET and XRD analysis. The TEM and SAED results revealed that the MWCNTs were uniformly encapsulated by hydroxyapatite nanoparticles. The synthesized HA-MWCNTs had a high specific surface area (180.504 m"2 g"−"1), with an average pore width (14.607 nm) and pore volume (0.774 cm"3 g"−"1), which produced a defluoridation capacity (DC) of 30.22 mgF"− g"−"1. This value was greater than unmodified hydroxyapatite (HA), which exhibited a larger specific surface area (172.233 m"2 g"−"1) and an excellent DC of 17.80 mgF"− g"−"1. A number of pertinent parameters that could affect the defluoridation performance of the HA/MWCNTs including weight ratios of the two key materials, solution pH and competing anions were carefully and comprehensively examined. It was found that the adsorption results followed the Langmuir and Freundlich isotherm model, and the sorption kinetics of the F"− appeared to exhibit a pseudo second order. Moreover, the adsorption reaction was spontaneous and endothermic and appeared to exhibit a higher initial adsorption rate. This reaction appeared to occur result from both anion exchange and electrostatic interactions. When the HA-MWCNTs (MH6) were at an adsorbent dose of 2.0 g L"−"1

  2. Synthesis of hydroxyapatite/multi-walled carbon nanotubes for the removal of fluoride ions from solution

    Energy Technology Data Exchange (ETDEWEB)

    Ruan, Zhongyuan; Tian, Yaxi [College of Chemistry and Chemical Engineering, Lanzhou University, Lanzhou 730000 (China); Ruan, Jifu [Chemistry Teaching and Research Group, No.1 Middle School of Queshan, Henan 463200 (China); Cui, Guijia; Iqbal, Kanwal; Iqbal, Anam [College of Chemistry and Chemical Engineering, Lanzhou University, Lanzhou 730000 (China); Ye, Herui; Yang, Zhangzhong [Northwest Regional Office of Nuclear and Radiation Safety, Ministry of Environmental Protection, Lanzhou 730000 (China); Yan, Shiqiang, E-mail: yansq@lzu.edu.cn [College of Chemistry and Chemical Engineering, Lanzhou University, Lanzhou 730000 (China)

    2017-08-01

    Graphical abstract: Hydroxyapatite nucleated and grown on Multi-walled carbon nanotubes (HA-MWCNTs) showed enhanced fluoride removal performance. - Highlights: • Noval HA nanoparticles and HA-MWCNTs composites were successfully synthesized for the first time. • The synthesized HA-MWCNTs composites exhibited a higher defluoridation capacity of 39.22 mg g{sup −1}. • It could reduced the fluoride concentration of the real waste water from 8.79 mg L{sup −1} to approximately 0.25 mg L{sup −1}. - Abstract: A novel composite material, hydroxyapatite (HA)-multi-walled carbon nanotubes (MWCNTs), was prepared using a simple in-situ sol-gel method, and was used for the first time to remove fluoride from water. The novel HA-MWCNTs were characterized using TEM, FT-IR, BET and XRD analysis. The TEM and SAED results revealed that the MWCNTs were uniformly encapsulated by hydroxyapatite nanoparticles. The synthesized HA-MWCNTs had a high specific surface area (180.504 m{sup 2} g{sup −1}), with an average pore width (14.607 nm) and pore volume (0.774 cm{sup 3} g{sup −1}), which produced a defluoridation capacity (DC) of 30.22 mgF{sup −} g{sup −1}. This value was greater than unmodified hydroxyapatite (HA), which exhibited a larger specific surface area (172.233 m{sup 2} g{sup −1}) and an excellent DC of 17.80 mgF{sup −} g{sup −1}. A number of pertinent parameters that could affect the defluoridation performance of the HA/MWCNTs including weight ratios of the two key materials, solution pH and competing anions were carefully and comprehensively examined. It was found that the adsorption results followed the Langmuir and Freundlich isotherm model, and the sorption kinetics of the F{sup −} appeared to exhibit a pseudo second order. Moreover, the adsorption reaction was spontaneous and endothermic and appeared to exhibit a higher initial adsorption rate. This reaction appeared to occur result from both anion exchange and electrostatic interactions. When the

  3. A method for the determination of free nitric acid in aqueous plutonium nitrate solutions - potassium fluoride method

    International Nuclear Information System (INIS)

    Mair, M.A.

    1988-06-01

    Plutonium IV and VI, and certain other hydrolysable metals which may be present, are converted to non-interfering species by the addition of the sample to potassium fluoride solution. The free acid is then titrated with standard sodium hydroxide solution using phenolphthalein as an indicator. (author)

  4. Inhibitor effect on corrosion of titanium alloys in muriatic solutions of titanium-magnesium production

    International Nuclear Information System (INIS)

    Dobrunov, Yu.V.; Volynskij, V.V.; Kolobov, G.A.; Kuznetsov, S.I.

    1977-01-01

    Corrosion tests of titanium alloys VTI-0, OT4, VT5-1 and steel Kh18N1OT in 10% and 18% HCl with additions of carnallite at 40 deg C have been carried out. It has been established that titanium alloys in 10% and 18% HCl containing 5 and 10% carnallite are sufficiently corrosion resistant in the presence of 0.1-1% FeCl or HNO 3 and can be used for manufacturing the equipment of recirculation gas scrubbers. Steel Kh18N10T is unstable in all the media tested. It is subjected to intensive pitting. Specimens of steel Kh18N10T have also revealed edge cracking

  5. Difference in surface reactions between titanium and zirconium in Hanks' solution to elucidate mechanism of calcium phosphate formation on titanium using XPS and cathodic polarization

    International Nuclear Information System (INIS)

    Tsutsumi, Y.; Nishimura, D.; Doi, H.; Nomura, N.; Hanawa, T.

    2009-01-01

    Titanium and zirconium were immersed in Hanks' solution with and without calcium and phosphate ions, and the surfaces were characterized with X-ray photoelectron spectroscopy (XPS) to determine the mechanism of calcium phosphate formation on titanium in simulated body fluids and in a living body. In addition, they were cathodically polarized in the above solutions. XPS characterization and cathodic polarization revealed differences in the surface properties in the ability of calcium phosphate formation between titanium and zirconium. The surface oxide film on titanium is not completely oxidized and is relatively reactive; that on zirconium is more passive and protective than that on titanium. Neither calcium nor phosphate stably exists alone on titanium, and calcium phosphate is naturally formed on it; calcium phosphate formed on titanium is stable and protective. On the other hand, calcium is never incorporated on zirconium, while zirconium phosphate, which is easily formed on zirconium, is highly stable and protective. Our study presents new information regarding the surface property of titanium and demonstrates that the characteristics of titanium and zirconium may be applied to various medical devices and new surface modification techniques.

  6. Low temperature sol-gel process for optical coatings based on magnesium fluoride and titanium dioxide; Niedertemperatur Sol-Gel Verfahren fuer optische Schichtsysteme auf Basis von Magnesiumfluorid und Titandioxid

    Energy Technology Data Exchange (ETDEWEB)

    Krueger, Hannes

    2009-09-24

    This work deals with the development of a low temperature sol-gel spincoating process for thin films with thicknesses in the nanometer range based on metal oxides and metal fluorides. Optical films such as anti-reflective (AR) or high reflective coatings are of much interest and consist of alternating dielectric layers of low and high refractive index materials. Regarding the general procedure for the metal fluorides a novel nonaqueous sol-gel synthesis starting from metal alkoxides and alcohol-dissolved HF was used. The coatings were dried and calcined at 100 C. The morphology of these films was characterised with REM, TEM and AFM. EDX and XPS were used to identify the chemical composition and ellipsometry and UV-vis spectroscopy to determine the optical properties of the films. This new process allows the preparation of homogeneous magnesium fluoride and titanium dioxide layers with low roughness (R{sub a} {<=} 1,9 nm) on silicon and quartz substrates. The magnesium fluoride layers are partially amorphous or microcrystalline with crystallite sizes from 2 nm to 10 nm. The titanium dioxide layers are predominantly amorphous. The thicknesses of the magnesium fluoride and titanium dioxide single layers were adjustable between 25 nm and 500 nm depending on the number of coating steps and on the concentration of the used sols. The magnesium fluoride layers had a refractive index of n{sub 500} = 1,36 and the titanium dioxide layers a refraction index of n{sub 500} = 2,05. For the first time, an alternating metal fluoride and oxide multilayer system was produced with a low temperature sol-gel method (consisting of magnesium fluoride and titanium dioxide). Based on the determined optical constants of the magnesium fluoride and titanium dioxide single layers, AR and HR multilayer systems were calculated and fabricated. The transmission spectra of the designs and the corresponding multilayer were in good agreement. Similar results were obtained with the reflection spectra

  7. Tantalum(V) impurity extraction by octanol from niobium(V) fluoride solutions

    International Nuclear Information System (INIS)

    Majorov, V.G.; Nikolaev, A.I.; Kopkov, V.K.

    2002-01-01

    The conditions of the niobium and tantalum extraction separation by octanol in the fluoride solutions, depending on the metals and free hydrofluoric acid concentration as well as on the organic and water phases voluminous relation, are studied for the purpose of developing the technology of niobium deep purification from the tantalum impurities. The technological scheme of the niobium solutions(V) extraction purification from the tantalum impurities(V), which provides for obtaining the niobium oxide(V), containing less than 0.005 mass % Ta 2 O 5 , is proposed on the basis of the established optimal separation conditions. The possibility of using the developed technology by the pyrochlore reprocessing is indicated [ru

  8. Characterization of Titanium Oxide Nanoparticles Obtained by Hydrolysis Reaction of Ethylene Glycol Solution of Alkoxide

    Directory of Open Access Journals (Sweden)

    Naofumi Uekawa

    2012-01-01

    Full Text Available Transparent and stable sols of titanium oxide nanoparticles were obtained by heating a mixture of ethylene glycol solution of titanium tetraisopropoxide (TIP and a NH3 aqueous solution at 368 K for 24 h. The concentration of NH3 aqueous solution affected the structure of the obtained titanium oxide nanoparticles. For NH3 aqueous solution concentrations higher than 0.2 mol/L, a mixture of anatase TiO2 nanoparticles and layered titanic acid nanoparticles was obtained. The obtained sol was very stable without formation of aggregated precipitates and gels. Coordination of ethylene glycol to Ti4+ ions inhibited the rapid hydrolysis reaction and aggregation of the obtained nanoparticles. The obtained titanium oxide nanoparticles had a large specific surface area: larger than 350 m2/g. The obtained titanium oxide nanoparticles showed an enhanced adsorption towards the cationic dye molecules. The selective adsorption corresponded to presence of layered titanic acid on the obtained anatase TiO2 nanoparticles.

  9. Synthesis of hydroxyapatite/multi-walled carbon nanotubes for the removal of fluoride ions from solution

    Science.gov (United States)

    Ruan, Zhongyuan; Tian, Yaxi; Ruan, Jifu; Cui, Guijia; Iqbal, Kanwal; Iqbal, Anam; Ye, Herui; Yang, Zhangzhong; Yan, Shiqiang

    2017-08-01

    A novel composite material, hydroxyapatite (HA)-multi-walled carbon nanotubes (MWCNTs), was prepared using a simple in-situ sol-gel method, and was used for the first time to remove fluoride from water. The novel HA-MWCNTs were characterized using TEM, FT-IR, BET and XRD analysis. The TEM and SAED results revealed that the MWCNTs were uniformly encapsulated by hydroxyapatite nanoparticles. The synthesized HA-MWCNTs had a high specific surface area (180.504 m2 g-1), with an average pore width (14.607 nm) and pore volume (0.774 cm3 g-1), which produced a defluoridation capacity (DC) of 30.22 mgF- g-1. This value was greater than unmodified hydroxyapatite (HA), which exhibited a larger specific surface area (172.233 m2 g-1) and an excellent DC of 17.80 mgF- g-1. A number of pertinent parameters that could affect the defluoridation performance of the HA/MWCNTs including weight ratios of the two key materials, solution pH and competing anions were carefully and comprehensively examined. It was found that the adsorption results followed the Langmuir and Freundlich isotherm model, and the sorption kinetics of the F- appeared to exhibit a pseudo second order. Moreover, the adsorption reaction was spontaneous and endothermic and appeared to exhibit a higher initial adsorption rate. This reaction appeared to occur result from both anion exchange and electrostatic interactions. When the HA-MWCNTs (MH6) were at an adsorbent dose of 2.0 g L-1, they were able to decrease the fluoride concentration of actual nuclear industry wastewater from 8.79 mg L-1 to about 0.25 mg L-1 (97.15% removal efficiency). The experimental results of this study showed that the HA-MWCNTs composites have application potential for the removal of fluoride ions from wastewater.

  10. Effect of the oxygen content in solution on the static and cyclic deformation of titanium foams.

    Science.gov (United States)

    Lefebvre, L P; Baril, E; Bureau, M N

    2009-11-01

    It is well known that interstitials affect the mechanical properties of titanium and titanium alloys. Their effects on the fatigue properties of titanium foams have not, however, been documented in the literature. This paper presents the effect of the oxygen content on the static and dynamic compression properties of titanium foams. Increasing the oxygen content from 0.24 to 0.51 wt% O in solution significantly increases the yield strength and reduces the ductility of the foams. However, the fatigue limit is not significantly affected by the oxygen content and falls within the 92 MPa +/- 12 MPa range for all specimens investigated in this study. During cyclic loading, deformation is initially coming from cumulative creep followed by the formation of microcracks. The coalescence of these microcracks is responsible for the rupture of the specimens. Fracture surfaces of the specimens having lower oxygen content show a more ductile aspect than the specimens having higher oxygen content.

  11. Anodic films grown on magnesium and magnesium alloys in fluoride solutions

    Energy Technology Data Exchange (ETDEWEB)

    Ono, S. [Dept. of Applied Chemistry, Kogakuin Univ., Tokyo (Japan); Masuko, N. [Dept. of Metallurgical Engineering, Chiba Inst. of Tech., Narashino, Chiba (Japan)

    2003-07-01

    Formation behavior of anodic oxide films on magnesium in fluoride electrolytes was investigated with attention to the effects of anodizing voltage and aluminum content. In the range of voltage between 2 V and 100 V, porous film was formed in alkaline fluoride solution associated with high current density at around 5 V and at breakdown voltage. The critical voltage of breakdown to allow maximum current flow was approximately 60 V and relatively independent on substrate purity. The films formed at breakdown voltage showed a lava-like porous structure similar to those obtained on aluminum and other valve metals. Barrier films or semi-barrier films, which were composed of hydrated outer layer and relatively dense inner layer, were formed at the other voltages. In the case of AZ91D, the critical voltage increased to 70 V and peculiar phenomenon at 5 V was not observed, so that only barrier films were formed at less than the breakdown voltage. These phenomena can be explained by the effects of aluminum incorporation into the film to prevent dissolution and to promote passivation of magnesium. The depth profiles of constituent elements showed that aluminum distributed in whole depth of the film. (orig.)

  12. Low Energy Gamma Radiation Induced Effects on Ultrasonic Velocity and Acoustic Parameters in Polyvinylidene Fluoride Solution

    Directory of Open Access Journals (Sweden)

    S. S. Kulkarni

    2016-01-01

    Full Text Available The modification of polyvinylidene fluoride (PVDF polymer properties with irradiation is of interest as it possesses unique piezo-, pyro-, and ferroelectric properties. In this paper, we report the results of acoustic parameters of irradiated PVDF mixed with dimethylacetamide (DMAC solution with low energy γ-source (Cs-137. The polymer solution covered with mica film assures only γ-ray passage and the duration was increased from 18 to 50 hours to achieve the higher dose rate. The dose rate was estimated using the strength of the radioactive source and the duration of the exposure. The ultrasonic velocity (v, density (ρ, and viscosity (η of 0.2 wt% and 0.5 wt% PVDF dissolved in pure DMAC solution, irradiated with different dose rate were measured using ultrasonic interferometer (Mittal make, Pyknometer, and Oswald’s viscometer, respectively. It is observed that the values of v, ρ, and η change with dose rate. The acoustic parameters such as adiabatic compressibility (β, intermolecular free path length (Lf, acoustic impedance (Z, relative association (RA, ultrasonic attenuation (α/f2, and relaxation time (τ are calculated using the experimental data. These results are interpreted in terms of the solute-solvent interaction in a polymer solution and scissoring chain damage.

  13. Eggshell Powder as an Adsorbent for Removal of Fluoride from Aqueous Solution: Equilibrium, Kinetic and Thermodynamic Studies

    Directory of Open Access Journals (Sweden)

    R. Bhaumik

    2012-01-01

    Full Text Available A new medium, eggshell powder has been developed for fluoride removal from aqueous solution. Fluoride adsorption was studied in a batch system where adsorption was found to be pH dependent with maximum removal efficiency at 6.0. The experimental data was more satisfactorily fitted with Langmuir isotherm model. The kinetics and the factor controlling adsorption process fully accepted by pseudo-second-order model were also discussed. Ea was found to be 45.98 kJmol-1 by using Arrhenius equation, indicating chemisorption nature of fluoride onto eggshell powder. Thermodynamic study showed spontaneous nature and feasibility of the adsorption process with negative enthalpy (∆H0 value also supported the exothermic nature. Batch experiments were performed to study the applicability of the adsorbent by using fluoride contaminated water collected from affected areas. These results indicate that eggshell powder can be used as an effective, low-cost adsorbent to remove fluoride from aqueous solution as well as groundwater.

  14. Effect of Fluoride Prophylactic Agents on the Mechanical Properties of Nickel-Titanium Wires: An in vitro Study

    Directory of Open Access Journals (Sweden)

    S R Harish Koushik

    2011-01-01

    Conclusion : The results suggest that using topical fluoride agents with NiTi wire could decrease the functional unloading mechanical properties of the wire and contribute to prolonged orthodontic treatment.

  15. COMPARISON OF STATISTICALLY CONTROLLED MACHINING SOLUTIONS OF TITANIUM ALLOYS USING USM

    Directory of Open Access Journals (Sweden)

    R. Singh

    2010-06-01

    Full Text Available The purpose of the present investigation is to compare the statistically controlled machining solution of titanium alloys using ultrasonic machining (USM. In this study, the previously developed Taguchi model for USM of titanium and its alloys has been investigated and compared. Relationships between the material removal rate, tool wear rate, surface roughness and other controllable machining parameters (power rating, tool type, slurry concentration, slurry type, slurry temperature and slurry size have been deduced. The results of this study suggest that at the best settings of controllable machining parameters for titanium alloys (based upon the Taguchi design, the machining solution with USM is statistically controlled, which is not observed for other settings of input parameters on USM.

  16. Hydrothermal calcification of alkali treated titanium in CaHPO{sub 4} solution

    Energy Technology Data Exchange (ETDEWEB)

    Fu, T., E-mail: taofu@xjtu.edu.cn [Key Laboratory of Biomedical Information Engineering of Ministry of Education, School of Life Science and Technology, Xi’an Jiaotong University, Shaanxi, 710049 (China); Fan, J.T., E-mail: jitang_fan@hotmail.com [State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing, 100081 (China); Shen, Y.G. [Department of Mechanical and Biomedical Engineering, City University of Hong Kong, Kowloon, Hong Kong (China); Sun, J.M. [Key Laboratory of Biomedical Information Engineering of Ministry of Education, School of Life Science and Technology, Xi’an Jiaotong University, Shaanxi, 710049 (China)

    2017-03-01

    The alkali treated titanium was hydrothermally treated in water and 10 mM CaHPO{sub 4} solution (nominal concentration) at 80–180 °C to crystallize the titanate hydrogel layer and calcify the alkali treated titanium. Surface structure and elemental composition of the samples were analyzed by scanning electron microscopy, energy dispersive x-ray analysis, x-ray photoelectron spectroscopy, x-ray diffraction and Raman spectroscopy. Porous titanate hydrogel layer is formed on titanium after the alkali treatment. For the hydrothermal treatment in water, the hydrogel layer is crystallized as anatase TiO{sub 2} with nanoporous or nanofibrous structure at 100 and 120 °C, and the layer is converted to anatase nanoparticles at 150 and 180 °C. For the hydrothermal treatment in the CaHPO{sub 4} solution, hydroxyapatite nanocrystallites are deposited at the samples surface at 80–120 °C, but only anatase nanoparticles are formed at 150 and 180 °C. The growth of hydroxyapatite nanocrystallites is influenced by pH and temperature variations of the solution. The present alkali-hydrothermal treatment can avoid higher temperatures involved in the traditional alkali-heat treatments, which is applicable for bioactive surface modification of the thermally sensitive titanium alloys. The results also show that Raman spectroscopy is a useful technique to analyze the microstructure of TiO{sub 2} and apatite films. - Highlights: • The alkali treated titanium is hydrothermally calcified in a CaHPO{sub 4} solution. • HA nanocrystallites are formed at 80–120 °C, but TiO{sub 2} nanoparticles at 150–180 °C. • The growth mechanism of HA nanocrystallites is discussed. • This low-temperature method is fit for some special titanium alloys.

  17. Hydrothermal calcification of alkali treated titanium in CaHPO_4 solution

    International Nuclear Information System (INIS)

    Fu, T.; Fan, J.T.; Shen, Y.G.; Sun, J.M.

    2017-01-01

    The alkali treated titanium was hydrothermally treated in water and 10 mM CaHPO_4 solution (nominal concentration) at 80–180 °C to crystallize the titanate hydrogel layer and calcify the alkali treated titanium. Surface structure and elemental composition of the samples were analyzed by scanning electron microscopy, energy dispersive x-ray analysis, x-ray photoelectron spectroscopy, x-ray diffraction and Raman spectroscopy. Porous titanate hydrogel layer is formed on titanium after the alkali treatment. For the hydrothermal treatment in water, the hydrogel layer is crystallized as anatase TiO_2 with nanoporous or nanofibrous structure at 100 and 120 °C, and the layer is converted to anatase nanoparticles at 150 and 180 °C. For the hydrothermal treatment in the CaHPO_4 solution, hydroxyapatite nanocrystallites are deposited at the samples surface at 80–120 °C, but only anatase nanoparticles are formed at 150 and 180 °C. The growth of hydroxyapatite nanocrystallites is influenced by pH and temperature variations of the solution. The present alkali-hydrothermal treatment can avoid higher temperatures involved in the traditional alkali-heat treatments, which is applicable for bioactive surface modification of the thermally sensitive titanium alloys. The results also show that Raman spectroscopy is a useful technique to analyze the microstructure of TiO_2 and apatite films. - Highlights: • The alkali treated titanium is hydrothermally calcified in a CaHPO_4 solution. • HA nanocrystallites are formed at 80–120 °C, but TiO_2 nanoparticles at 150–180 °C. • The growth mechanism of HA nanocrystallites is discussed. • This low-temperature method is fit for some special titanium alloys.

  18. Room temperature synthesis of protonated layered titanate sheets using peroxo titanium carbonate complex solution.

    Science.gov (United States)

    Sutradhar, Narottam; Sinhamahapatra, Apurba; Pahari, Sandip Kumar; Bajaj, Hari C; Panda, Asit Baran

    2011-07-21

    We report the synthesis of peroxo titanium carbonate complex solution as a novel water-soluble precursor for the direct synthesis of layered protonated titanate at room temperature. The synthesized titanates showed excellent removal capacity for Pb(2+) and methylene blue. Based on experimental observations, a probable mechanism for the formation of protonated layered dititanate sheets is also discussed.

  19. Comparison of antimicrobial effects of titanium tetrafluoride, chlorhexidine, xylitol and sodium fluoride on streptococcus mutans: An in-vitro study.

    Science.gov (United States)

    Eskandarian, Tahereh; Motamedifar, Mohammad; Arasteh, Peyman; Eghbali, Seyed Sajad; Adib, Ali; Abdoli, Zahra

    2017-03-01

    No studies have yet documented the bactericidal effects of TiF4, and its role in the treatment of dental caries, and no definite protocol has been introduced to regulate its use. The aim of this study was to determine the antimicrobial/bactericidal effects of TiF4 on Streptococcus Mutans ( S. Mutans ) and to compare it with chlorhexidine (Chx), sodium fluoride (NaF) and xylitol. This study was conducted at the Shiraz University of Medical Sciences microbiology laboratory during March 2015 to September 2015. In this in-vitro study, first a bacterial suspension was prepared and adjusted to a 0.5 McFarland standard (equivalent to 1×10 8 CFU/ml). The minimal inhibitory concentration (MIC) and minimal bactericidal concentrations (MBC) of TiF4, Chx, NaF and xylitol were assessed using broth microdilution assay and disk diffusion methods. In order to neutralize the acidic nature of TiF4, we used a sodium hydroxide preparation to obtain a pH of 7.2 and repeated all of the previous tests with the neutralized TiF4 solution. We reported the final results as percentages where appropriate. The MIC of TiF4, NaF and Chx for S. Mutans were 12.5%, 12.5% and 6.25%, respectively. At a concentration of 12.5% the inhibition zone diameters were 9 mm, 15mm and 14mm for TiF4, NaF and Chx, respectively. The MBC was 25%, 12.5% and 12.5% for TiF4, NaF and Chx, respectively. Xylitol failed to show any bactericidal or growth inhibitory effect in all of its concentrations. When we repeated the tests with an adjusted pH, identical results were obtained. TiF4 solutions have anti-growth and bactericidal effects on S. Mutans at a concentration of 12.5% which is comparable with chlorhexidine and NaF, indicating the possible use of this solution in dental practice as an anti-cariogenic agent, furthermore the antimicrobial activity is unaffected by pH of the environment.

  20. Enhanced Hydrophilicity and Protein Adsorption of Titanium Surface by Sodium Bicarbonate Solution

    Directory of Open Access Journals (Sweden)

    Shengnan Jia

    2015-01-01

    Full Text Available The aim of this study was to investigate a novel and convenient method of chemical treatment to modify the hydrophilicity of titanium surfaces. Sand-blasted and acid-etched (SLA titanium surfaces and machined titanium surfaces were treated with sodium bicarbonate (NaHCO3 solution. The wetting behavior of both kinds of surfaces was measured by water contact angle (WCA test. The surface microstructure was assessed with scanning electron microscopy (SEM and three-dimensional (3D optical microscopy. The elemental compositions of the surfaces were analyzed by X-ray photoelectron spectroscopy (XPS. The protein adsorption analysis was performed with fibronectin. Results showed that, after 1 M NaHCO3 treatment, the hydrophilicity of both SLA and machined surfaces was enhanced. No significant microstructural change presented on titanium surfaces after NaHCO3 treatment. The deprotonation and ion exchange activities might cause the enhanced hydrophilicity of titanium surfaces. The increased protein adsorption of NaHCO3-treated SLA surfaces might indicate their improved tissue-integration in clinical use.

  1. Titanium and zirconium based wrought alloys and bulk metallic glasses for fluoride ion containing 11.5 M HNO3 medium

    International Nuclear Information System (INIS)

    Jayaraj, J.; Ningshen, S.; Mallika, C.; Kamachi Mudali, U.

    2016-01-01

    Aqueous reprocessing of plutonium-rich mixed oxide fuels require fluoride as a catalyst in boiling nitric acid for an effective dissolution of the spent fuel. The corrosion behavior of the candidate dissolver materials zircaloy-4 (Zr-4) and commercial pure titanium (CP-Ti grade 2) in boiling 11.5 M HNO 3 + 0.05 M NaF has been established. High corrosion rates were obtained for Zr- 4 and CP-Ti in nitric acid containing fluoride ions. Complexing the fluoride ions either with Al(NO 3 ) 3 or ZrO(NO 3 ) 2 aided in decreasing the corrosion rates of Zr-4 and CP-Ti. High corrosion resistance is claimed as one of the principal property of the amorphous alloy when compared to the crystalline alloy. Thus Ni 60 Nb 40 and Ni 60 Nb 30 Ta 10 amorphous ribbons were prepared and exposed in boiling 11.5 M HNO 3 and 11.5 M HNO 3 + 0.05 M NaF. In nitric acid these alloys did not show any sign of corrosion attack. XPS analysis confirmed that the passivity was due to the formation passive films of thickness ≈3 nm enriched with Nb 2 O 5 and of ≈1.5 nm enriched with both Nb 2 O 5 and Ta 2 O 5 on the respective surfaces of the ribbons. In boiling 11.5 M HNO 3 + 0.05 M NaF, severe corrosion attack was observed on Ni 60 Nb 40 ribbon, due to the instability of the oxide/metal interface. The Ni 60 Nb 30 Ta 10 amorphous ribbon exhibited corrosion resistance of at least an order of magnitude higher than that for Ni 60 Nb 40 ribbon

  2. Application of membrane LaF3 electrode in the determination of stability constants of Uranyl Fluoride complex in solution

    International Nuclear Information System (INIS)

    Muzakky; Iswani GS; Mintolo

    1996-01-01

    A membrane electrode LaF 3 has been applied in the determination of uranyl fluoride complex stability constant in solution. The determination is based on the detection of free F ion in solution as a result of hydrolysis reaction (process) of uranyl ions into the uranyl hydroxide form at low pH. The experiment results showed that there was no effect of ammonium carbonate 2 M titran, flow rate on the electrode response. The F release is optimum at pH 1. The free F ion in solution is calculated from the standard curve at pH 1, after the fluoride concentration at the same pH has been corrected. Using the plot of average number of ligand binding (n) versus minus log of free ligand (-log F) the value of β1 = 4.4, β2 = 7.48, β3=9.73, and β4 = 11.67

  3. Titanium

    DEFF Research Database (Denmark)

    Fage, Simon W; Muris, Joris; Jakobsen, Stig S

    2016-01-01

    Exposure to titanium (Ti) from implants and from personal care products as nanoparticles (NPs) is common. This article reviews exposure sources, ion release, skin penetration, allergenic effects, and diagnostic possibilities. We conclude that human exposure to Ti mainly derives from dental...... and medical implants, personal care products, and foods. Despite being considered to be highly biocompatible relative to other metals, Ti is released in the presence of biological fluids and tissue, especially under certain circumstances, which seem to be more likely with regard to dental implants. Although...... most of the studies reviewed have important limitations, Ti seems not to penetrate a competent skin barrier, either as pure Ti, alloy, or as Ti oxide NPs. However, there are some indications of Ti penetration through the oral mucosa. We conclude that patch testing with the available Ti preparations...

  4. Manufacture of nanosized apatite coatings on titanium with different surface treatments using a supersaturated calcification solution

    Directory of Open Access Journals (Sweden)

    Adrian Paz Ramos

    Full Text Available The biomimetic method is used for the deposition of calcium phosphate coatings (Ca - P on the surface of different biomaterials. However, the application of this method requires long exposure times in order to obtain a suitable layer thickness for its use in medical devices. In this paper, we present a fast approach to obtain apatite coatings on titanium, using a combination of supersaturated calcification solution (SCS with chemical modification of the titanium surface. Also, it was evaluated the effect of four different surface treatments on the apatite deposition rate. Commercially pure titanium plates were activated by chemical or thermochemical treatments. Then, the activated samples were immersed in a solution with high content of calcium and phosphate ions at 37 ºC for 24 h, mimicking the physiological conditions. The coatings were studied by Fourier transform infrared spectroscopy (FTIR, X-ray diffraction (XRD, scanning electron microscopy (SEM and energy dispersive X-ray spectroscopy (EDX. The use of SCS solutions allowed the formation of crystalline hydroxyapatite coatings within a period of 24 h with a thickness between 1 and 5.3 µm. Besides, precipitates of hydroxyapatite nanoparticles with a globular configuration, forming aggregates with submicrometer size, were found in SCS solutions.

  5. Titanium Implant Osseointegration Problems with Alternate Solutions Using Epoxy/Carbon-Fiber-Reinforced Composite

    Directory of Open Access Journals (Sweden)

    Richard C. Petersen

    2014-12-01

    Full Text Available The aim of the article is to present recent developments in material research with bisphenyl-polymer/carbon-fiber-reinforced composite that have produced highly influential results toward improving upon current titanium bone implant clinical osseointegration success. Titanium is now the standard intra-oral tooth root/bone implant material with biocompatible interface relationships that confer potential osseointegration. Titanium produces a TiO2 oxide surface layer reactively that can provide chemical bonding through various electron interactions as a possible explanation for biocompatibility. Nevertheless, titanium alloy implants produce corrosion particles and fail by mechanisms generally related to surface interaction on bone to promote an inflammation with fibrous aseptic loosening or infection that can require implant removal. Further, lowered oxygen concentrations from poor vasculature at a foreign metal surface interface promote a build-up of host-cell-related electrons as free radicals and proton acid that can encourage infection and inflammation to greatly influence implant failure. To provide improved osseointegration many different coating processes and alternate polymer matrix composite (PMC solutions have been considered that supply new designing potential to possibly overcome problems with titanium bone implants. Now for important consideration, PMCs have decisive biofunctional fabrication possibilities while maintaining mechanical properties from addition of high-strengthening varied fiber-reinforcement and complex fillers/additives to include hydroxyapatite or antimicrobial incorporation through thermoset polymers that cure at low temperatures. Topics/issues reviewed in this manuscript include titanium corrosion, implant infection, coatings and the new epoxy/carbon-fiber implant results discussing osseointegration with biocompatibility related to nonpolar molecular attractions with secondary bonding, carbon fiber in vivo

  6. Work function tuning of tin-doped indium oxide electrodes with solution-processed lithium fluoride

    Energy Technology Data Exchange (ETDEWEB)

    Ow-Yang, C.W., E-mail: cleva@sabanciuniv.edu [Materials Science and Engineering Program, Sabanci University, Orhanli, Tuzla, 34956 Istanbul (Turkey); Nanotechnology Application Center, Sabanci University, Orhanli, Tuzla, 34956 Istanbul (Turkey); Jia, J. [Graduate School of Science and Engineering, Aoyama Gakuin University, 5-10-1 Fuchinobe, Chuo, Sagamihara, Kanagawa 252-5258 (Japan); Aytun, T. [Materials Science and Engineering Program, Sabanci University, Orhanli, Tuzla, 34956 Istanbul (Turkey); Zamboni, M.; Turak, A. [Department of Engineering Physics, McMaster University, Hamilton, Ontario L8S 4L8 (Canada); Saritas, K. [Materials Science and Engineering Program, Sabanci University, Orhanli, Tuzla, 34956 Istanbul (Turkey); Shigesato, Y. [Graduate School of Science and Engineering, Aoyama Gakuin University, 5-10-1 Fuchinobe, Chuo, Sagamihara, Kanagawa 252-5258 (Japan)

    2014-05-30

    Solution-processed lithium fluoride (sol-LiF) nanoparticles synthesized in polymeric micelle nanoreactors enabled tuning of the surface work function of tin-doped indium oxide (ITO) films. The micelle reactors provided the means for controlling surface coverage by progressively building up the interlayer through alternating deposition and plasma etch removal of the polymer. In order to determine the surface coverage and average interparticle distance, spatial point pattern analysis was applied to scanning electron microscope images of the nanoparticle dispersions. The work function of the sol-LiF modified ITO, obtained from photoelectron emission yield spectroscopy analysis, was shown to increase with surface coverage of the sol-LiF particles, suggesting a lateral depolarization effect. Analysis of the photoelectron emission energy distribution in the near threshold region revealed the contribution of surface states for surface coverage in excess of 14.1%. Optimization of the interfacial barrier was achieved through contributions from both work function modification and surface states. - Highlights: • Work function of indium tin oxide increased with LiF nanoparticle coverage. • Work function was analyzed via photoelectron emission yield (PEYS). • At higher surface coverage, the energy distribution of PEYS increased. • Pre-threshold increase in PEYS consistent with emission from surface states.

  7. Cow bones char as a green sorbent for fluorides removal from aqueous solutions: batch and fixed-bed studies.

    Science.gov (United States)

    Nigri, Elbert M; Cechinel, Maria Alice P; Mayer, Diego A; Mazur, Luciana P; Loureiro, José M; Rocha, Sônia D F; Vilar, Vítor J P

    2017-01-01

    Cow bone char was investigated as sorbent for the defluoridation of aqueous solutions. The cow bone char was characterized in terms of its morphology, chemical composition, and functional groups present on the bone char surface using different analytical techniques: SEM, EDS, N 2 -BET method, and FTIR. Batch equilibrium studies were performed for the bone chars prepared using different procedures. The highest sorption capacities for fluoride were obtained for the acid washed (q = 6.2 ± 0.5 mg/g) and Al-doped (q = 6.4 ± 0.3 mg/g) bone chars. Langmuir and Freundlich models fitted well the equilibrium sorption data. Fluoride removal rate in batch system is fast in the first 5 h, decreasing after this time until achieving equilibrium due to pore diffusion. The presence of carbonate and bicarbonate ions in the aqueous solution contributes to a decrease of the fluoride sorption capacity of the bone char by 79 and 31 %, respectively. Regeneration of the F-loaded bone char using 0.5 M NaOH solution leads to a sorption capacity for fluoride of 3.1 mg/g in the second loading cycle. Fluoride breakthrough curve obtained in a fixed-bed column presents an asymmetrical S-shaped form, with a slow approach of C/C 0  → 1.0 due to pore diffusion phenomena. Considering the guideline value for drinking water of 1.5 mg F - /L, as recommended by World Health Organization, the service cycle for fluoride removal was of 71.0 h ([F - ] feed  ∼ 9 mg/L; flow rate = 1 mL/min; m sorbent  = 12.6 g). A mass transfer model considering the pore diffusion was able to satisfactorily describe the experimental data obtained in batch and continuous systems.

  8. Electrochemical behaviour of titanium coated stainless steel by r.f. sputtering in synthetic sweat solutions for electrode applications

    International Nuclear Information System (INIS)

    Fonseca, C.; Vaz, F.; Barbosa, M.A.

    2004-01-01

    The r.f. sputtering technique was used to deposit titanium thin films on stainless steel substrates, aiming at the application of the coated samples as skin contact materials for 'dry' active electrodes. In this work the electrochemical behaviour of the coated samples was investigated in synthetic sweat solutions and their performance was compared with that of uncoated stainless steel and bulk titanium. The characterisation of the samples was carried out by electrochemical techniques and scanning electron microscopy. The coated samples displayed corrosion resistance values in synthetic sweat solutions much higher than stainless steel samples and of the same order of the values measured for bulk titanium in the same conditions

  9. Fluoride metabolism in plants

    Energy Technology Data Exchange (ETDEWEB)

    Peters, R; Shorthouse, M

    1964-04-04

    Grass seedlings exposed to inorganic fluoride solutions do not take up appreciable amounts of fluoride until concentrations of more than 1.0 mM (19 p.p.m.) are used. No formation of organic fluoride has been found, even with exposure to 15.75 mM fluoride, indicating that there is no formation of fluoroacetate or similar compounds. 8 references, 2 tables.

  10. Interactive effects of soil acidity and fluoride on soil solution aluminium chemistry and barley (Hordeum vulgare L.) root growth

    International Nuclear Information System (INIS)

    Manoharan, V.; Loganathan, P.; Tillman, R.W.; Parfitt, R.L.

    2007-01-01

    A greenhouse study was conducted to determine if concentrations of fluoride (F), which would be added to acid soils via P fertilisers, were detrimental to barley root growth. Increasing rates of F additions to soil significantly increased the soil solution concentrations of aluminium (Al) and F irrespective of the initial adjusted soil pH, which ranged from 4.25 to 5.48. High rates of F addition severely restricted root growth; the effect was more pronounced in the strongly acidic soil. Speciation calculations demonstrated that increasing rates of F additions substantially increased the concentrations of Al-F complexes in the soil. Stepwise regression analysis showed that it was the combination of the activities of AlF 2 1+ and AlF 2+ complexes that primarily controlled barley root growth. The results suggested that continuous input of F to soils, and increased soil acidification, may become an F risk issue in the future. - Addition of high rates of fluoride to strongly acidic soils can reduce barley root growth due to the toxicity of aluminium-fluoride complexes formed in soil solution

  11. Highly efficient fluoride adsorption from aqueous solution by nepheline prepared from kaolinite through alkali-hydrothermal process.

    Science.gov (United States)

    Wang, Hao; Feng, Qiming; Liu, Kun; Li, Zishun; Tang, Xuekun; Li, Guangze

    2017-07-01

    A direct alkali-hydrothermal induced transformation process was adopted to prepare nepheline from raw kaolinite (shortened form RK in this paper) and NaOH solution in this paper. Structure and morphology characterizations of the synthetic product showed that the nepheline possessed high degree of crystallinity and uniform surface morphology. Specific surface area of nepheline is 18 m 2 /g, with a point of zero charge at around pH 5.0-5.5. The fluoride (F - ions) adsorption by the synthetic nepheline (shortened form SN in this paper) from aqueous solution was also investigated under different experimental conditions. The adsorption process well matched the Langmuir isotherm model with an amazing maximum adsorption capacity of 183 mg/g at 323 K. The thermodynamic parameters (ΔG 0 , ΔH 0 , and ΔS 0 ) for adsorption on SN were also determined from the temperature dependence. The adsorption capacities of fluoride on SN increased with increasing of temperature and initial concentration. Initial pH value also had influence on adsorption process. Adsorption of fluoride was rapidly increased in 5-60 min and thereafter increased slowly to reach the equilibrium in about 90-180 min under all conditions. The adsorption followed a pseudo-second order rate law. Copyright © 2017 Elsevier Ltd. All rights reserved.

  12. Fluoride adsorption from aqueous solution by magnetic core-shell Fe_3O_4@alginate-La particles fabricated via electro-coextrusion

    International Nuclear Information System (INIS)

    Zhang, Yahui; Lin, Xiaoyan; Zhou, Quisheng; Luo, Xuegang

    2016-01-01

    Graphical abstract: The magnetic core-shell Fe_3O_4@Alg-La particles were fabricated successfully by a simple method of electro-coextrusion, and employed as an adsorbent for separation of fluoride from aqueous solution. - Highlights: • Magnetic core-shell Fe_3O_4@Alg-La particles were prepared by electro-coextrusion. • The maximum adsorption capacity for fluoride at 298.15 K was 45.230 mg/g. • The adsorbent has a good saturation magnetization value. • The adsorbent has a great potential in removing the fluoride. - Abstract: The magnetic core-shell Fe_3O_4@Alg-La particles were fabricated successfully by a simple method of electro-coextrusion, and employed as an adsorbent for separation of fluoride from aqueous solution. Main factors affecting the removal of fluoride, including pH, adsorbent dosage, initial concentration, temperature and contact time were investigated. The adsorption isotherm and adsorption kinetics were studied to understand the adsorption process in detail. The experimental data were fitted well by the non-linear Freundlich isotherm and linear pseudo-second-order model, the maximum fluoride adsorption capacity was 45.230 mg/g at pH 4, 298.15 K. Thermodynamic parameters indicated that the fluoride adsorption process was feasible and spontaneous. The presence of other anions like Cl"−, SO_4"2"−, HCO_3"− and PO_4"3"− had almost no effect on the fluoride adsorption. The adsorbent can be easily separated from the solution by a magnet. The magnetic core-shell Fe_3O_4@Alg-La particles before and after fluoride adsorption were studied by SEM, FTIR, EDX and XPS, which indicated that the adsorption mechanism may be related to electrostatic attraction and Lewis acid-base interaction.

  13. Fluoride adsorption from aqueous solution by magnetic core-shell Fe{sub 3}O{sub 4}@alginate-La particles fabricated via electro-coextrusion

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Yahui [School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, Sichuan (China); Engineering Research Center of Biomass Materials, Ministry of Education, Mianyang 621010, Sichuan (China); Lin, Xiaoyan, E-mail: lxy20100205@163.com [School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010, Sichuan (China); Engineering Research Center of Biomass Materials, Ministry of Education, Mianyang 621010, Sichuan (China); Zhou, Quisheng [A State Key Laboratory of Pulp & Paper Engineering, South China University of Technology, Guangzhou 510640 (China); Luo, Xuegang [Engineering Research Center of Biomass Materials, Ministry of Education, Mianyang 621010, Sichuan (China)

    2016-12-15

    Graphical abstract: The magnetic core-shell Fe{sub 3}O{sub 4}@Alg-La particles were fabricated successfully by a simple method of electro-coextrusion, and employed as an adsorbent for separation of fluoride from aqueous solution. - Highlights: • Magnetic core-shell Fe{sub 3}O{sub 4}@Alg-La particles were prepared by electro-coextrusion. • The maximum adsorption capacity for fluoride at 298.15 K was 45.230 mg/g. • The adsorbent has a good saturation magnetization value. • The adsorbent has a great potential in removing the fluoride. - Abstract: The magnetic core-shell Fe{sub 3}O{sub 4}@Alg-La particles were fabricated successfully by a simple method of electro-coextrusion, and employed as an adsorbent for separation of fluoride from aqueous solution. Main factors affecting the removal of fluoride, including pH, adsorbent dosage, initial concentration, temperature and contact time were investigated. The adsorption isotherm and adsorption kinetics were studied to understand the adsorption process in detail. The experimental data were fitted well by the non-linear Freundlich isotherm and linear pseudo-second-order model, the maximum fluoride adsorption capacity was 45.230 mg/g at pH 4, 298.15 K. Thermodynamic parameters indicated that the fluoride adsorption process was feasible and spontaneous. The presence of other anions like Cl{sup −}, SO{sub 4}{sup 2−}, HCO{sub 3}{sup −} and PO{sub 4}{sup 3−} had almost no effect on the fluoride adsorption. The adsorbent can be easily separated from the solution by a magnet. The magnetic core-shell Fe{sub 3}O{sub 4}@Alg-La particles before and after fluoride adsorption were studied by SEM, FTIR, EDX and XPS, which indicated that the adsorption mechanism may be related to electrostatic attraction and Lewis acid-base interaction.

  14. Electrochemical Behavior of Biomedical Titanium Alloys Coated with Diamond Carbon in Hanks' Solution

    Science.gov (United States)

    Gnanavel, S.; Ponnusamy, S.; Mohan, L.; Radhika, R.; Muthamizhchelvan, C.; Ramasubramanian, K.

    2018-03-01

    Biomedical implants in the knee and hip are frequent failures because of corrosion and stress on the joints. To solve this important problem, metal implants can be coated with diamond carbon, and this coating plays a critical role in providing an increased resistance to implants toward corrosion. In this study, we have employed diamond carbon coating over Ti-6Al-4V and Ti-13Nb-13Zr alloys using hot filament chemical vapor deposition method which is well-established coating process that significantly improves the resistance toward corrosion, wears and hardness. The diamond carbon-coated Ti-13Nb-13Zr alloy showed an increased microhardness in the range of 850 HV. Electrochemical impedance spectroscopy and polarization studies in SBF solution (simulated body fluid solution) were carried out to understand the in vitro behavior of uncoated as well as coated titanium alloys. The experimental results showed that the corrosion resistance of Ti-13Nb-13Zr alloy is relatively higher when compared with diamond carbon-coated Ti-6Al-4V alloys due to the presence of β phase in the Ti-13Nb-13Zr alloy. Electrochemical impedance results showed that the diamond carbon-coated alloys behave as an ideal capacitor in the body fluid solution. Moreover, the stability in mechanical properties during the corrosion process was maintained for diamond carbon-coated titanium alloys.

  15. Ion exchange of some transition metal cations on hydrated titanium dioxide in aqueous ammonia solutions

    International Nuclear Information System (INIS)

    Bilewicz, A.; Narbutt, J.; Dybczynski, R.

    1992-01-01

    The adsorption of transition metal cations on hydrated titanium dioxide in complexing ammonia and amine solutions has been studied as a function of ammonia (amine) concentration. The relationships between the distribution coefficients and ammonia concentration as well as the effects of various amines on sorption of transition metals indicate that a coordinate bond is formed between the metal ions and the hydroxy groups of the sorbent. The distribution coefficients of silver(I) and cobalt(II), which form strong ammonia complexes in aqueous solutions, decrease with increasing concentration of ammonia already at concentrations exceeding 10 -3 *mol*dm -3 . Cations of zinc, manganese and mercury which form much weaker ammonia complexes do not exhibit any effect of ammonia concentration in the whole range investigated. In the case of sorption of macroamounts of ammonia or amine complexes of silver, the molecular sieve effect plays an important role. The differences in the affinity of hydrated titanium dioxide for ammonia solvates of various transition metal ions can serve as a tool for effective separation of these ions in ammonia solutions. (author) 10 refs.; 4 figs.; 1 tab

  16. Transport of titanium dioxide nanoparticles in saturated porous media under various solution chemistry conditions

    International Nuclear Information System (INIS)

    Wang Yu; Gao Bin; Morales, Verónica L.; Tian Yuan; Wu Lei; Gao Jie; Bai Wei; Yang Liuyan

    2012-01-01

    Because of its wide applications, nanosized titanium dioxide may become a potential environmental risk to soil and groundwater system. It is therefore important to improve current understanding of the environmental fate and transport of titanium oxides nanoparticles (TONPs). In this work, the effect of solution chemistry (i.e., pH, ionic strength, and natural organic matter (NOM) concentration) on the deposition and transport of TONPs in saturated porous media was examined in detail. Laboratory columns packed with acid-cleaned quartz sand were used in the experiment as porous media. Transport experiments were conducted with various chemistry combinations, including four ionic strengths, three pH levels, and two NOM concentrations. The results showed that TONP mobility increased with increasing solution pH, but decreased with increasing solution ionic strength. It is also found that the presence of NOM in the system enhanced the mobility of TONPs in the saturated porous media. The Derjaguin–Landau–Verwey–Overbeek (DLVO) theory was used to justify the mobility trends observed in the experimental data. Predictions from the theory agreed excellently with the experimental data.

  17. Fluoridated Water

    Science.gov (United States)

    ... Genetics Services Directory Cancer Prevention Overview Research Fluoridated Water On This Page What is fluoride, and where is it found? What is water fluoridation? When did water fluoridation begin in the ...

  18. Investigation of holmium(5) complexing in hydrofluoric acid solutions in the presence of alkali metal and ammonium fluorides

    International Nuclear Information System (INIS)

    Tsikaeva, D.V.; Agulyanskij, A.I.; Balabanov, Yu.I.; Kuznetsov, V.Ya.; Kalinnikov, V.T.

    1989-01-01

    Method of vibrational spectroscopy is used to study niobium-containing solutions of hydrofluoric acid in the presence of alkali metal and ammonium fluorides. It is shown that NbF 6 - and NbOF 5 2- ions co-exists in solutions, therewith, additions shift equilibrium to the second complex side. Methods of IR spectroscopy, roentgenometry, crystal optics and chemical analysis are used to identify precipitated from solutions solid phases. Three new phases, which composition by chemical analysis corresponds to M 3 Nb 2 OF 11 , where M=NH 4 , K, Rb, are detected. Their roentgenometric data displayed in tetragonal crystal system with a and c parameters equalling 15,710 and 7,744; 14,877 and 7,697; 15,511 and 7,785 A respectively, are presented

  19. Structural transitions in the titanium alloy β-CEZ studied by precipitation mechanisms after solution treatment

    International Nuclear Information System (INIS)

    Angelier, C.; Bechet, J.

    1994-01-01

    The β-CEZ, a high strength titanium alloy developed for aerospace engine applications, is a α/β near β alloy. A wide variety of phase transformations and attendant nodular, lamellar and mixed microstructures are possible according to thermomechanical treatment conditions. The aim of this present paper is to illustrate the influence of solution treat-ment temperature on equilibrium microstructures and continuous cooling transformations. Solution treatment temperature controls the volume fraction of primary α particles and composition of the β-matrix. Therefore the transformation during continuous cooling from α/β or β field depends on β-matrix stability and potential sites amount of α precipitation. After a β solution treatment, the α particles are disappeared and the β phase contains all alloying elements; the continuous cooling transformation produces a Widmanstaetten structure. If the cooling rate or/and the solution treatment temperature in the α/β field are sufficiently low, the microstructure consists only of nodular morphology. During α particles growth the α volume fraction increases as equilibrium and the decreasing of growth kinetic leads to supersaturated β matrix and Widmanstaetten α precipitation. The final microstructures are mixed. The influence of solution trat-ment temperature and cooling rate on nucleation and growth mechanisms is specially developed. (orig.)

  20. Corrosion of chromium, nickel, titanium and steels in solutions of sodium and ammonium thiosulfates

    International Nuclear Information System (INIS)

    Grebenshchikova, S.V.; Kochergin, V.P.; Doronina, I.V.

    1983-01-01

    Results of gravimetric determinatiion of average rate of chromium, nickel, titatnium and steels 12Kh18N10T and VSt.3 corrosion rate in solutions 50 mass.% (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 in the air and nitrogen atmosphere at 333 K have been generalized. Anodic polarization curves are recorded and stationary potentials of metals and steels under the conditions are measured. It is shown that in (NH 4 ) 2 S 2 O 3 solution the rate of metal and steels corrosion is higher than in Na 2 S 2 O 3 solution indepenent of the nature of gaseous medium contacting with solution. In the series Ni → VSt.3 → 12Kh18N10T → VT1 → chromium in (NH 4 ) 2 S 2 O 3 and Na 2 S 2 O 3 solutions at 333 K corrosion resistance increases. Chromium, titanium and chromium-nickel steel 12Kh18N10T possess a high corrosion resistance

  1. Composition, structure and electrical properties of alumina barrier layers grown in fluoride-containing oxalic acid solutions

    Energy Technology Data Exchange (ETDEWEB)

    Jagminas, A. [Institute of Chemistry, A. Gostauto 9, LT-01108 Vilnius (Lithuania)], E-mail: jagmin@ktl.mii.lt; Vrublevsky, I. [Department of Microelectricals, Belarusian State University of Informatics and Radioelectricals, 6 Brovka Street, Minsk 220013 (Belarus); Kuzmarskyte, J.; Jasulaitiene, V. [Institute of Chemistry, A. Gostauto 9, LT-01108 Vilnius (Lithuania)

    2008-04-15

    The composition, structure and electrical properties of alumina barrier layers grown by anodic oxidation in F{sup -}-containing (FC) and F{sup -}-free (FF) oxalic acid solutions were studied using the re-anodizing/dissolution technique, Fourier-transformed infrared and X-ray photoelectron spectroscopy. These results confirmed formation in FC anodizing solutions of films structurally different from ones grown in FF oxalic acid baths. It was found that the barrier layer of FC alumina films is composed of two layers differing in the dissolution rate. These differences are related to the formation in the FC electrolyte of a barrier layer composed of a more microporous outer part and a thin, non-porous and non-scalloped inner part consisting of aluminum oxide and aluminum fluoride.

  2. Application of Kramers-Kronig relationships for titanium impedance data validation in a Ringer's solution

    Directory of Open Access Journals (Sweden)

    Bastidas, D. M.

    2004-08-01

    Full Text Available This paper studies the applicability of Kramers-Kronig (KK relationships to assess the validity of real and imaginary impedance measurements for titanium in a Ringer's solution using the electrochemical impedance spectroscopy (EIS method. Nyquist and Bode plots showed a capacitive behaviour with a high impedance modulus including two time constants. Two procedures were employed in the implementation of the KK integral relationships based on an equivalent circuit which satisfies KK relationships and an ohmic resistance shunted to the measured EIS data. The titanium's EIS data satisfied the KK relationships.

    Este artículo estudia la aplicabilidad de las relaciones de Kramers-Kronig (KK al estudio de la validez de las medidas de impedancia (EIS, parte real y parte imaginaria, del titanio en contacto con la solución de Ringer. Los diagramas de Nyquist y Bode muestran un comportamiento capacitivo, con un módulo de impedancia elevado y con dos constantes de tiempo. En la implementación de las integrales de KK se emplearon dos procedimientos, que se basan en un circuito equivalente que cumple las relaciones de KK y en una resistencia óhmica en paralelo añadida a los datos de impedancia medidos. Los resultados de impedancia del titanio satisfacen las relaciones de KK.

  3. An In Vitro Study on the Effect of Amorphous Calcium Phosphate and Fluoride Solutions on Color Improvement of White Spot Lesions

    Directory of Open Access Journals (Sweden)

    Fahimeh Farzanegan

    2018-06-01

    Full Text Available The ability of remineralizing agents to improve the color of white spot lesions (WSL is an important aspect that should be investigated. The aim of this study was to evaluate the effects of 0.05% amorphous calcium phosphate (ACP, 0.5% ACP, and 0.05% fluoride solutions, as well as artificial saliva on the color improvement of white spot lesions (WSLs. In this in vitro study, 50 human premolar teeth were randomly classified into five groups. At baseline, all the samples were assessed by using a colorimeter (E0. Then, white spot lesions were induced on the surface of the teeth by means of a pH-cycling model, and the colorimeter was used again (E1. Afterwards, samples of the 1st and 2nd groups were kept in 0.05% ACP and 0.5% ACP solutions for 1 min/day, respectively. The 3rd group specimens were placed in 0.05% fluoride solution for 1 min/day. The other two groups were kept in artificial saliva and distilled in water separately. All the samples were assessed by the colorimeter for a third time (E2. We found no significant difference between the groups in ∆E1. There was also no significant difference among 0.05% ACP solution, 0.5% ACP solution, 0.05% fluoride solution, and artificial saliva considering ∆E2. However, a significant difference was noted between the above-mentioned solutions and distilled water in ∆E2. With respect to ∆E3, there were considerable differences between ACP solution and artificial saliva. The same results were obtained for the difference between fluoride solution and artificial saliva. However, no significant difference was found among 0.05% ACP, 0.5% ACP, and 0.05% fluoride solutions in terms of ∆E3. In Conclusion, ACP is as effective as fluoride in the color improvement of WSLs and the recommended treatment for this purpose is daily use of 0.05% ACP, 0.5% ACP or 0.05% fluoride solutions.

  4. Crevice-corrosion kinetics on titanium and a Ti-Ni-Mo alloy in chloride solutions at elevated temperature

    International Nuclear Information System (INIS)

    McKay, P.

    1987-01-01

    The results of an electrochemical investigation of the crevice-corrosion kinetics on titanium and a dilute Ti-Ni-Mo alloy (0.8% Ni, 0.3% Mo), in concentrated chloride solutions at 150 0 C, are presented. The current-time transients, obtained on creviced electrodes under both potentiostatic and galvanic (coupling to a large area of uncreviced titanium) conditions, are interpreted in terms of crevice acidification leading to the formation of an active-passive cell, maintained by iR gradient in the electrolyte. The passivating effect of the Ni and Mo additions on the crevice corrosion of titanium are described, together with the results of an electrochemical study, carried out in bulk acid chloride solutions, that were used to substantiate a proposed mechanism of crevice passivation. (author)

  5. Characteristics of selective fluoride adsorption by biocarbon-Mg/Al layered double hydroxides composites from protein solutions: kinetics and equilibrium isotherms study.

    Science.gov (United States)

    Ma, Wei; Lv, Tengfei; Song, Xiaoyan; Cheng, Zihong; Duan, Shibo; Xin, Gang; Liu, Fujun; Pan, Decong

    2014-03-15

    In the study, two novel applied biocarbon-Mg/Al layered double hydroxides composites (CPLDH and CPLDH-Ca) were successfully prepared and characterized by TEM, ICP-AES, XFS, EDS, FTIR, XRD, BET and pHpzc. The fluoride removal efficiency (RF) and protein recovery ratio (RP) of the adsorbents were studied in protein systems of lysozyme (LSZ) and bovine serum albumin (BSA). The results showed that the CPLDH-Ca presented remarkable performance for selective fluoride removal from protein solution. It reached the maximum RF of 92.1% and 94.8% at the CPLDH-Ca dose of 2.0g/L in LSZ and BSA system, respectively. The RP in both systems of LSZ and BSA were more than 90%. Additionally, the RP of CPLDH-Ca increased with the increase of ionic strengths, and it almost can be 100% with more than 93% RF. Fluoride adsorption by the CPLDH-Ca with different initial fluoride concentrations was found to obey the mixed surface reaction and diffusion controlled adsorption kinetic model, and the overall reaction rate is probably controlled by intra-particle diffusion, boundary layer diffusion and reaction process. The adsorption isotherms of fluoride in BSA system fit the Langmuir-Freundlich model well. The BSA has synergistic effect on fluoride adsorption and the degree increased with the increase of the initial BSA concentration. Copyright © 2014 Elsevier B.V. All rights reserved.

  6. Uranium determination by spectrophotometry, in chloride solutions, using titanium (III) as reducer; Determinacao de uranio por espectrofotometria, em solucoes cloridricas, utilizando titanio (III) como redutor

    Energy Technology Data Exchange (ETDEWEB)

    Bastos, E T.R.; Bastos, M B.R.

    1986-08-01

    A simple method for determining uranium in uranium (VI) solutions with the presence of uranium (IV), iron (II), and titanium (IV) in chloridic solution is described. The method comprises in uranium (VI) reduction with titanium (III), acidity adjustment and uranium (IV) spectrophotometry in hydrochloric acid 2 M. (C.G.C.).

  7. In situ characterization of Ti-peroxy gel during formation on titanium surfaces in hydrogen peroxide containing solutions

    International Nuclear Information System (INIS)

    Muyco, Julie J.; Gray, Jeremy J.; Ratto, Timothy V.; Orme, Christine A.; McKittrick, Joanna; Frangos, John

    2006-01-01

    Three possible functions of Ti-peroxy gel are: reduction of the inflammatory response through the reduction of hydrogen peroxide and other reactive oxygen species; creation of a favorable surface for calcium phosphate nucleation; and as a transitional layer between the compliant surrounding tissue and the stiff titanium. Traditional surface characterization techniques operate in high vacuum environments that alter the actual sample-solution interface. Our studies used techniques that allowed samples to remain in solution and be observed over time. Atomic force microscopy (AFM) force-distance curves, electrochemical impedance spectroscopy (EIS), and Raman spectroscopy were each used in situ to define kinetic and mechanical properties of Ti-peroxy gel as it formed over time on titanium during exposure to hydrogen peroxide. Our studies enabled us to monitor real-time changes in the native oxide layer on titanium in hydrogen peroxide containing solution, including the formation of a Ti-peroxy gel layer above the native oxide. Peaks attributed to Ti-peroxy gel were seen to emerge over the course of several hours using in situ Raman spectroscopy. Force-distance curves suggest a layer that thickens with time on the titanium sample surface. EIS data showed that changes in the surface layers could be monitored in solution over time

  8. Titanium condenser tubes. Problems and their solution for wider application to large surface condensers. [PWR

    Energy Technology Data Exchange (ETDEWEB)

    Sato, S; Sugiyama, S; Nagata, K; Nanba, K; Shimono, M [Sumitomo Light Metal Industries Ltd., Tokyo (Japan)

    1977-06-01

    The corrosion resistance of titanium in sea water is extremely excellent, but titanium tubes are expensive, and the copper alloy tubes resistant in polluted sea water were developed, therefore they were not used practically. In 1970, ammonia attack was found on the copper alloy tubes in the air-cooled portion of condensers, and titanium tubes have been used as the countermeasure. As the result of the use, the galvanic attack on copper alloy tube plates with titanium tubes as cathode and the hydrogen absorption at titanium tube ends owing to excess electrolytic protection was observed, but the corrosion resistance of titanium tubes was perfect. These problems can be controlled by the application of proper electrolytic protection. The condensers with all titanium tubes adopted recently in USA are intended to realize perfectly no-leak condensers as the countermeasure to the corrosion in steam generators of PWR plants. Regarding large condensers of nowadays, three problems are pointed out, namely the vibration of condenser tubes, the method of joining tubes and tube plates, and the tubes of no coolant leak. These three problems in case of titanium tubes were studied, and the problem of the fouling of tubes was also examined. The intervals of supporting plates for titanium tubes should be narrowed. The joining of titanium tubes and titanium tube plates by welding is feasible and promising. The cleaning with sponge balls is effective to control fouling.

  9. Fluoride release from fluoride varnishes under acidic conditions.

    Science.gov (United States)

    Lippert, F

    2014-01-01

    The aim was to investigate the in vitro fluoride release from fluoride varnishes under acidic conditions. Poly(methyl methacrylate) blocks (Perspex, n=3 per group) were painted with 80 ± 5 mg fluoride varnish (n=10) and placed into artificial saliva for 30 min. Then, blocks were placed into either 1% citric acid (pH 2.27) or 0.3% citric acid (pH 3.75) solutions (n=3 per solution and varnish) for 30 min with the solutions being replaced every 5 min. Saliva and acid solutions were analyzed for fluoride content. Data were analyzed using three-way ANOVA (varnish, solution, time). The three-way interaction was significant (p>0.0001). Fluoride release and release patterns varied considerably between varnishes. Fluoride release in saliva varied by a factor of more than 10 between varnishes. Some varnishes (CavityShield, Nupro, ProFluorid, Vanish) showed higher fluoride release in saliva than during the first 5 min of acid exposure, whereas other varnishes (Acclean, Enamel-Pro, MI Varnish, Vella) showed the opposite behavior. There was little difference between acidic solutions. Fluoride release from fluoride varnishes varies considerably and also depends on the dissolution medium. Bearing in mind the limitations of laboratory research, the consumption of acidic drinks after fluoride varnish application should be avoided to optimize the benefit/risk ratio.

  10. Interactive effects of soil acidity and fluoride on soil solution aluminium chemistry and barley (Hordeum vulgare L.) root growth.

    Science.gov (United States)

    Manoharan, V; Loganathan, P; Tillman, R W; Parfitt, R L

    2007-02-01

    A greenhouse study was conducted to determine if concentrations of fluoride (F), which would be added to acid soils via P fertilisers, were detrimental to barley root growth. Increasing rates of F additions to soil significantly increased the soil solution concentrations of aluminium (Al) and F irrespective of the initial adjusted soil pH, which ranged from 4.25 to 5.48. High rates of F addition severely restricted root growth; the effect was more pronounced in the strongly acidic soil. Speciation calculations demonstrated that increasing rates of F additions substantially increased the concentrations of Al-F complexes in the soil. Stepwise regression analysis showed that it was the combination of the activities of AlF2(1+) and AlF(2+) complexes that primarily controlled barley root growth. The results suggested that continuous input of F to soils, and increased soil acidification, may become an F risk issue in the future.

  11. A2TiF5.nH2O (A=K, Rb, or Cs; n=0 or 1): Synthesis, structure, characterization, and calculations of three new uni-dimensional titanium fluorides

    International Nuclear Information System (INIS)

    Jo, Vinna; Woo Lee, Dong; Koo, Hyun-Joo; Ok, Kang Min

    2011-01-01

    Three new uni-dimensional alkali metal titanium fluoride materials, A 2 TiF 5 .nH 2 O (A=K, Rb, or Cs; n=0 or 1) have been synthesized by hydrothermal reactions. The structures of A 2 TiF 5 .nH 2 O have been determined by single-crystal X-ray diffraction. The Ti 4+ cations have been reduced to Ti 3+ during the synthesis reactions. All three A 2 TiF 5 .nH 2 O materials contain novel 1-D chain structures that are composed of the slightly distorted Ti 3+ F 6 corner-sharing octahedra attributable to the Jahn-Teller distortion. The coordination environment of the alkali metal cations plays an important role to determine the degree of turning in the chain structures. Complete structural analyses, Infrared and UV-vis diffuse reflectance spectra, and thermal analyses are presented, as are electronic structure calculations. -- Graphical abstract: Ball-and-stick and polyhedral representations for (a) β-K 2 TiF 5 and (b) Rb 2 TiF 5 .H 2 O or Cs 2 TiF 5 .H 2 O with the K + and Rb + (or Cs + ) coordination environment emphasized. Display Omitted Research highlights: → Synthesis, structure, characterization, and calculation of new titanium fluorides. → Study of reduction of starting Ti 4+ cations to Ti 3+ by DMF. → Novel 1-D chain structures with Jahn-Teller distorted TiF 6 octahedra.

  12. Simple solution-processed titanium oxide electron transport layer for efficient inverted polymer solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Liang [CAS Key Laboratory of Bio-based Materials, Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Shen, Wenfei [CAS Key Laboratory of Bio-based Materials, Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Institute of Hybrid Materials, Laboratory of New Fiber Materials and Modern Textile—The Growing Base for State Key Laboratory, Qingdao University, Qingdao 266071 (China); Chen, Weichao [CAS Key Laboratory of Bio-based Materials, Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Bao, Xichang, E-mail: baoxc@qibebt.ac.cn [CAS Key Laboratory of Bio-based Materials, Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China); Wang, Ning; Dou, Xiaowei; Han, Liangliang; Wen, Shuguang [CAS Key Laboratory of Bio-based Materials, Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101 (China)

    2014-12-31

    Titanium oxide (TiO{sub X}) is an effective electron transport layer (ETL) in polymer solar cells (PSCs). We report efficient inverted PSCs with a simple solution-processed amorphous TiO{sub X} (s-TiO{sub X}) film as an ETL. The s-TiO{sub X} film with high light transmittance was prepared by spin-coating titanium (IV) isopropoxide isopropanol solution on indium tin oxide coated glass in inert and then placed in air under room temperature for 60 min. The introduction of s-TiO{sub X} ETL greatly improved the short circuit current density of the devices. PSCs based on poly(3-hexylthiophene):[6,6]-phenyl-C61-butyric acid methyl ester and poly(4,8-bis-alkyloxy-benzo[1,2-b:4,5-b′]dithiophene-alt-alkylcarbonyl -thieno[3,4-b]thiophene):[6,6]-phenyl- C71-butyric acid methyl ester using s-TiO{sub X} film as ETL shows high power conversion efficiency of 4.29% and 6.7% under the illumination of AM 1.5G, 100 mW/cm{sup 2}, which shows enhancements compared to the conventional PSCs with poly(styrenesulfonate)-doped poly(ethylenedioxythiophene) as anode buffer layer. In addition, the device exhibits good stability in a humid ambient atmosphere without capsulation. The results indicate that the annealing-free, simple solution processed s-TiO{sub X} film is an efficient ETL for high-performance PSCs. - Highlights: • High quality s-TiO{sub X} films were prepared by a simple, solution method without thermal treatment. • The s-TiO{sub X} films with high transmittance are very smooth. • The organic photovoltaic performance with s-TiO{sub X} film improved greatly and exhibited good stability. • The annealing-free, simple prepared s-TiO{sub X} film will be much compatible with flexible substrates.

  13. Photocatalytic degradation of furfural in aqueous solution by N-doped titanium dioxide nanoparticles.

    Science.gov (United States)

    Veisi, Farzaneh; Zazouli, Mohammad Ali; Ebrahimzadeh, Mohammad Ali; Charati, Jamshid Yazdani; Dezfoli, Amin Shiralizadeh

    2016-11-01

    The photocatalytic degradation of furfural in aqueous solution was investigated using N-doped titanium dioxide nanoparticles under sunlight and ultraviolet radiation (N-TiO 2 /Sun and N-TiO 2 /UV) in a lab-scale batch photoreactor. The N-TiO 2 nanoparticles prepared using a sol-gel method were characterized using XRD, X-ray photoelectron spectroscopy (XPS), and SEM analyses. Using HPLC to monitor the furfural concentration, the effect of catalyst dosage, contact time, initial solution pH, initial furfural concentration, and sunlight or ultraviolet radiation on the degradation efficiency was studied. The efficiency of furfural removal was found to increase with increased reaction time, nanoparticle loading, and pH for both processes, whereas the efficiency decreased with increased furfural concentration. The maximum removal efficiencies for the N-TiO 2 /UV and N-TiO 2 /Sun processes were 97 and 78 %, respectively, whereas the mean removal efficiencies were 80.71 ± 2.08 % and 62.85 ± 2.41 %, respectively. In general, the degradation and elimination rate of furfural using the N-TiO 2 /UV process was higher than that using the N-TiO 2 /Sun process.

  14. Corrosion of titanium alloys in concentrated chloride solutions at temperature up to 160 deg C

    International Nuclear Information System (INIS)

    Ruskol, Yu.S.; Viter, L.I.; Balakin, A.I.; Fokin, M.N.

    1982-01-01

    Resistance of VT1-0 titanium and 4200, 4207 titanium alloys to pitting and total corrosion in chlorides of cadmium, potassium, nickel, ammonium, barium, calcium, lithium, magnesium in respect to pH value and temperature (120,140,160 deg C) is determined. The results obtained are presented as nomograms of stability. Possible reasons for corrosion behaviour of titanium in each of the chlorides are discussed

  15. Solution High-Energy Burst Assembly (SHEBA) results from subprompt critical experiments with uranyl fluoride fuel

    International Nuclear Information System (INIS)

    Cappiello, C.C.; Butterfield, K.B.; Sanchez, R.G.; Bounds, J.A.; Kimpland, R.H.; Damjanovich, R.P.; Jaegers, P.J.

    1997-01-01

    Experiments were performed to measure a variety of parameters for SHEBA: behavior of the facility during transient and steady-state operation; characteristics of the SHEBA fuel; delayed-critical solution height vs solution temperature; initial reactor period and reactivity vs solution height; calibration of power level vs reactor power instrumentation readings; flux profile in SHEBA; radiation levels and neutron spectra outside the assembly for code verification and criticality alarm and dosimetry purposes; and effect on reactivity of voids in the fuel

  16. Determination of titanium and vanadium in aqueous solutions by potentiometric titration

    International Nuclear Information System (INIS)

    Sibirkin, A.A.; Elliev, Yu.E.

    1996-01-01

    Possibility of titanium and vanadium determination at their combined presence by bichromatometric chromometric titration with potentiometric indication of end point is shown. The technique is developed which allows to determine titanium and vanadium with relative standard derivation ±2% in amounts not less than 50 and 100 mg respectively

  17. Solution High-Energy Burst Assembly (SHEBA) results from subprompt critical experiments with uranyl fluoride fuel

    International Nuclear Information System (INIS)

    Cappiello, C.C.; Butterfield, K.B.; Sanchez, R.G.

    1997-10-01

    The Solution High-Energy Burst Assembly (SHEBA) was originally constructed during 1980 and was designed to be a clean free-field geometry, right-circular, cylindrically symmetric critical assembly employing U(5%)O 2 F 2 solution as fuel. A second version of SHEBA, employing the same fuel but equipped with a fuel pump and shielding pit, was commissioned in 1993. This report includes data and operating experience for the 1993 SHEBA only. Solution-fueled benchmark work focused on the development of experimental measurements of the characterization of SHEBA; a summary of the results are given. A description of the system and the experimental results are given in some detail in the report. Experiments were designed to: (1) study the behavior of nuclear excursions in a low-enrichment solution, (2) evaluate accidental criticality alarm detectors for fuel-processing facilities, (3) provide radiation spectra and dose measurements to benchmark radiation transport calculations on a low-enrichment solution system similar to centrifuge enrichment plants, and (4) provide radiation fields to calibrate personnel dosimetry. 15 refs., 37 figs., 10 tabs

  18. Preparation of Atomically Flat Si(111)-H Surfaces in Aqueous Ammonium Fluoride Solutions Investigated by Using Electrochemical, In Situ EC-STM and ATR-FTIR Spectroscopic Methods

    International Nuclear Information System (INIS)

    Bae, Sang Eun; Oh, Mi Kyung; Min, Nam Ki; Paek, Se Hwan; Hong, Suk In; Lee, Chi-Woo J.

    2004-01-01

    Electrochemical, in situ electrochemical scanning tunneling microscope (EC-STM), and attenuated total reflectance-FTIR (ATR-FTIR) spectroscopic methods were employed to investigate the preparation of atomically flat Si(111)-H surface in ammonium fluoride solutions. Electrochemical properties of atomically flat Si(111)-H surface were characterized by anodic oxidation and cathodic hydrogen evolution with the open circuit potential (OCP) of ca. .0.4 V in concentrated ammonium fluoride solutions. As soon as the natural oxide-covered Si(111) electrode was immersed in fluoride solutions, OCP quickly shifted to near .1 V, which was more negative than the flat band potential of silicon surface, indicating that the surface silicon oxide had to be dissolved into the solution. OCP changed to become less negative as the oxide layer was being removed from the silicon surface. In situ EC-STM data showed that the surface was changed from the initial oxide covered silicon to atomically rough hydrogen-terminated surface and then to atomically flat hydrogen terminated surface as the OCP moved toward less negative potentials. The atomically flat Si(111)-H structure was confirmed by in situ EC-STM and ATR-FTIR data. The dependence of atomically flat Si(111)-H terrace on mis-cut angle was investigated by STM, and the results agreed with those anticipated by calculation. Further, the stability of Si(111)-H was checked by STM in ambient laboratory conditions

  19. Avaliação da superfície de braquetes de titânio após a aplicação de fluoreto de sódio Evaluation of titanium brackets surface after immersion in sodium fluoride

    Directory of Open Access Journals (Sweden)

    Luciane Macedo de Menezes

    2006-06-01

    the same described procedures. All brackets were evaluated by macroscopic (visual appearence and scanning microscopy (Philips, model XL 30, before and after the procedures. RESULTS: titanium brackets submitted to fluoride (NaF, groups B and C, presented discoloration (matte gray color when compared to group A. Stainless steel brackets showed no color alteration. CONCLUSION: titanium and stainless steel brackets showed no change in surface roughness or chemical components when immersed in sodium fluoride solution.

  20. Titanium condenser tubes--problems and their solutions for wider application to large surface condensers

    Energy Technology Data Exchange (ETDEWEB)

    Sato, S; Sugiyama, Y; Nagata, K; Namba, K; Shimono, M

    1978-01-01

    To meet the demand for high reliability condensers for thermal and nuclear power plants, especially for PWR plants, the condensers installed entirely with titanium tubes have been investigated and used. Some difficulties from conventional copper alloy tubes exist. Further investigations are necessary on three items: (1) tube vibration; (2) joining tubes to tube plate; (3) fouling (bio-fouling) control. Literature survey on the tube vibration suggests that the probability of tube vibration due to decreased stiffness of titanium tubes in comparison with conventional copper alloy tubes can be decreased by designing the proper span length between supports. Experiments on seal welding of tubes to a tube plate have successfully proved that pulsed TIG arc welding is applicable to get reliable and strong joints, even on site, by suitable countermeasures. Experiments on the fouling (bio-fouling) of titanium tubes in marine application reveal that the increased fouling of titanium tubes could be controlled by proper application of sponge ball cleaning.

  1. Surface properties of anatase TiO2 nanowire films grown from a fluoride-containing solution.

    Science.gov (United States)

    Berger, Thomas; Anta, Juan A; Morales-Flórez, Víctor

    2013-06-03

    Controlling the surface chemistry of nucleating seeds during wet-chemical synthesis allows for the preparation of morphologically well-defined nanostructures. Synthesis conditions play a key role in the surface properties, which directly affect the functional properties of the material. Therefore, it is important to establish post-synthesis treatments to facilitate the optimization of surface properties with respect to a specific application, without losing the morphological peculiarity of the nanostructure. We studied the surface properties of highly crystalline and porous anatase TiO2 nanowire (NW) electrodes, grown by chemical-bath deposition in fluoride-containing solutions, using a combined electrochemical and spectroscopic approach. As-deposited films showed low capacity for catechol adsorption and a poor photoelectrocatalytic activity for water oxidation. Mild thermal annealing at 200 °C resulted in a significant improvement of the electrode photoelectrocatalytic activity, whereas the bulk properties of the NWs (crystal structure, band-gap energy) remained unchanged. Enhancement of the functional properties of the material is discussed on the basis of adsorption capacity and electronic properties. The temperature-induced decrease of recombination centers, along with the concomitant increase of adsorption and reaction sites upon thermal annealing are called to be responsible for such improved performance. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  2. The effect of fluoride on the scavenging of organophosphates by human butyrylcholinesterase in buffer solutions and human plasma

    International Nuclear Information System (INIS)

    Ashani, Yacov; Segev, Omri; Balan, Ayala

    2004-01-01

    Fluoride ion is a reversible inhibitor of human butyrylcholinesterase (HuBChE) that is a viable drug candidate against organophosphates (OPs) toxicity. Since large numbers of communities in many countries are occasionally exposed to relatively high amount of fluoride, its effect on the kinetics of inhibition of HuBChE by OPs was investigated. In saline phosphate, pH 7.4, fluoride in the lower millimolar range significantly slowed the inhibition of HuBChE by paraoxon, DFP, echothiophate, soman, sarin, and VX. The kinetics of the inhibition was found consistent with the formation of a reversible fluoride-HuBChE complex that is at least 25-fold less active towards phosphorylation or phosphonylation than the free enzyme. Heat inactivation experiments indicate that the binding of fluoride to HuBChE probably involves enhanced cross-domain interaction via hydrogen bonds formation that may decrease enzyme activity. In spite of distinct structural differences among the OP used, the dissociation constants of the fluoride-HuBChE reversible complex varied over a narrow range (K F , 0.31-0.70 mM); however, K F in human plasma increased to 2.75-3.40 mM. 19 F-NMR spectroscopy revealed that fluoride ion is complexed to plasma components, an observation that explains in part the apparent increase in K F . Results suggest that an estimate of the relative decrease in the rate of OPs sequestration in presence of fluoride can be obtained from the fraction of the free HuBChE (1 + [F]/K F ) -1 . Considering K F values in human plasma, it is concluded that the scavenging efficacy of OPs by HuBChE is not compromised by the normal concentration range of circulating fluoride ions

  3. Corrigendum to "Synthesis of hydroxyapatite/multi-walled carbon nanotubes for the removal of fluoride ions from solution" [Appl. Surf. Sci. 412 (2017) 578-590

    Science.gov (United States)

    Ruan, Zhongyuan; Tian, Yaxi; Ruan, Jifu; Cui, Guijia; Iqbal, Kanwal; Iqbal, Anam; Ye, Herui; Yang, Zhangzhong; Yan, Shiqiang

    2018-04-01

    In our recent paper [1], we reported the synthesis of hydroxyapatite/multi-walled carbon nanotubes (HA-MWCNTs) and studied their performance for the removal of fluoride ions from solution. However, we have made some writing mistakes, especially in the section on adsorption kinetics analysis. Our mistakes were spotted by Prof. Yuandong Huang, who graciously noticed these errors. We are grateful to him, and have decided to write a "Corrigendum".

  4. The recovery of 99Mo from solutions of irradiated Uranium using a column with nanoparticles of Titanium Dioxide

    International Nuclear Information System (INIS)

    Androne, G. E.; Petre, M.; Lazar, C. G.

    2016-01-01

    Molyibdenum-99 (T½ = 66.02 h) decays by beta emission to 99 Tcm (T½ = 6.02 h). The latter nuclide is used in many nuclear medicine applications. The 99 Mo is produced from irradiated high (HEU) or low (LEU) enriched uranium. In this work a sensitive and selective method for recovering Mo from uranium solution, using a column with titanium dioxide nanoparticles, is developed. The titanium dioxide (TiO 2 ) nanoparticles were synthesized via sol-gel method using titanium tetra-chloride as starting material and urea as a reacting medium. A 40 ml uranium solution containing 450 g/L uranyl nitrate, 1 M HNO 3 , and 4 mg Mo was loaded on a column containing 6 g of TiO 2 sorbent at 75°C. After loading, the column was washed with 1 M HNO 3 and H 2 O. Mo was stripped from the column with 0.1 M NaOH at 25°C. The ICP-MS results indicate that 80-95% of the initial mass of Mo was loaded on the column, and 90-94% of this quantity was recovered in the strip fraction. (authors)

  5. Determination of total fluoride in HF/HNO3/H2SiF6 etch solutions by new potentiometric titration methods.

    Science.gov (United States)

    Weinreich, Wenke; Acker, Jörg; Gräber, Iris

    2007-03-30

    In the photovoltaic industry the etching of silicon in HF/HNO(3) solutions is a decisive process for cleaning wafer surfaces or to produce certain surface morphologies like polishing or texturization. With regard to cost efficiency, a maximal utilisation of etch baths in combination with highest quality and accuracy is strived. To provide an etch bath control realised by a replenishment with concentrated acids the main constituents of these HF/HNO(3) etch solutions including the reaction product H(2)SiF(6) have to be analysed. Two new methods for the determination of the total fluoride content in an acidic etch solution based on the precipitation titration with La(NO(3))(3) are presented within this paper. The first method bases on the proper choice of the reaction conditions, since free fluoride ions have to be liberated from HF and H(2)SiF(6) at the same time to be detected by a fluoride ion-selective electrode (F-ISE). Therefore, the sample is adjusted to a pH of 8 for total cleavage of the SiF(6)(2-) anion and titrated in absence of buffers. In a second method, the titration with La(NO(3))(3) is followed by a change of the pH-value using a HF resistant glass-electrode. Both methods provide consistent values, whereas the analysis is fast and accurate, and thus, applicable for industrial process control.

  6. High temperature thermodynamics of H2 and D2 in titanium, and in dilute titanium oxygen solid solutions

    International Nuclear Information System (INIS)

    Dantzer, P.

    1983-01-01

    The Tian Calvet microcalorimetric method has been improved in order to determine ΔH-barsub(H)(D), the partial molar enthalpy of mixing of hydrogen (deuterium) in the Ti-H 2 (D 2 ) solid systems for compositions 0 2 solid solutions (y = (O/Ti)) at 745 K. The combined calorimetric and equilibrium method allows a precise evaluation of the partial molar entropies. The results of this study differ substantially from earlier published data. (author)

  7. Fluoride retention by kaolin clay

    DEFF Research Database (Denmark)

    Kau, P. M. H.; Smith, D. W.; Binning, Philip John

    1997-01-01

    To evaluate the potential effectiveness of kaolin clay liners in storage of fluoride contaminated waste, an experimental study of the sorption and desorption behaviour of fluoride in kaolin clay was conducted. The degree of fluoride sorption by kaolin was found to depend on solution p......H and available fluoride concentration with equilibrium being achieved within 24 h. A site activation process involving the uptake of fluoride was also observed at the initial stages of sorption. This behaviour was attributed to a layer expansion process of the clay during sorption. The maximum fluoride sorption...... capacity was found to be 18.3 meq/100 g at pH 6 and 8.6 meq/100 g at pH 7. A competitive Langmuir sorption isotherm where sorption is dependant on both pH and fluoride concentration is employed to characterise the experimental sorption and desorption data. The sorption and desorption isotherms revealed...

  8. Electrochemical and stress corrosion cracking behaviour of titanium in n-propanol and iso-propanol solutions

    International Nuclear Information System (INIS)

    Trasatti, S.P.; Sivieri, E.

    2004-01-01

    Titanium shows severe localised corrosion in non-aqueous media in the presence of applied stress and crevice. The present work brings a contribution to the behaviour of Ti in non-aqueous media by studying the role of water on the electrochemical properties and stress corrosion cracking (SCC) sensitivity of Ti in n-propanol and iso-propanol solutions. The anodic behaviour of titanium in n-propanol-H 2 O and iso-propanol-H 2 O systems is quite similar to that observed in methanol-H 2 O and ethanol-H 2 O systems. The minimum water content needed for the passive film to be stable is 2% for n-propanol and 0.1% for iso-propanol. In methanol and ethanol it is 20 and 8%, respectively. The minimum water content decreases as the number of carbon atoms increases and the lowest water content in iso-propanol is strictly related to the capability of the alcohol to dehydrate. The possibility of predicting by means of polarisation curves the conditions of occurrence of SCC of titanium has been confirmed by simply analysing when corrosion potential is higher than breakdown potential

  9. Arsenic removal from aqueous solutions by sorption onto zirconium- and titanium-modified sorbents

    Directory of Open Access Journals (Sweden)

    Ignjatović Ljubiša

    2011-01-01

    Full Text Available Arsenic reduction in drinking water can include treatment by adsorption, switching to alternative water sources, or blending with water that has a lower arsenic concentration. Commercial sorbents MTM, Greensand and BIRM (Clack Corporation were modified with zirconium and titanium after activation. The modifications were performed with titanium tetrachloride and zirconium tetrachloride. The modified sorbents were dried at different temperatures. The sorption of arsenate and arsenite dissolved in drinking water (200μg L-1 onto the sorbents were tested using a batch procedure. After removal of the sorbent, the concentration of arsenic was determined by HG-AAS. Zirconium-modified BIRM showed the best performance for the removal of both arsenite and arsenate. Modification of the greensand did not affect arsenic sorption ability. Zirconium-modified BIRM diminished the concentration of total As to below 5 μg L-1.

  10. Comparative evaluation of fluoride release from PRG-composites and compomer on application of topical fluoride: An in-vitro study

    Directory of Open Access Journals (Sweden)

    Dhull K

    2009-03-01

    Full Text Available Aims and Objective: To determine the fluoride release from Giomer and Compomer, using different topical fluoride regimes, and to compare the amount of fluoride release from giomer with that of compomer. Materials and Method: Forty-eight specimens of each giomer and compomer were divided into four treatment groups, namely, control group, fluoridated dentifrice (500 ppm once daily group, fluoridated dentifrice (500 ppm twice daily group, fluoridated dentifrice (500 ppm once daily + fluoridated mouthwash (225 ppm group. Each specimen was suspended in demineralizing solution for six hours and remineralizing solution for 18 hours. Fluoride release was measured in both the demineralizing solution and remineralizing solution daily for seven days. Total daily fluoride release for each specimen was calculated by adding the amount released in the demineralizing solution to that released in remineralizing solution. Results and Conclusion: The fluoride release (ppm was found to be more in Giomer when compared to Compomer. The fluoride released from Giomer and Compomer was significantly greater in the acidic demineralizing solution than in the neutral remineralizing solution. It was found that increasing fluoride exposure significantly increased fluoride release from the giomer and compomer. It was found that the fluoride release from the subgroups of giomer and compomer was in the following order: fluoridated dentifrice twice daily > fluoridated dentifrice once daily + fluoridated mouthwash > fluoridated dentifrice once daily > control group. It was found that the giomer showed a greater fluoride uptake than the compomer.

  11. Fluoride analysis

    Energy Technology Data Exchange (ETDEWEB)

    Brandt, C S

    1963-01-01

    The methods and procedures for the detection and estimation of fluoride are varied and numerous. The problems of sampling, contamination, and loss in sampling waters, plant and animal tissues and atmospheres are discussed, along with brief descriptors of methods most commonly used. Techniques for separating fluorides from matrixes are discussed, as well as gravimetric, calorimetric, and spectrophotometric analytical techniques.

  12. Adsorption of polymethacrylic acid from aqueous solutions on disperse titanium dioxide

    Science.gov (United States)

    Yaremko, Z. M.; Tkachenko, N. G.; Fedushinskaya, L. B.

    2011-10-01

    The state of macromolecules of polymethacrylic acid adsorbed on the surface of disperse titanium dioxide was assessed using a combination of the differential concentration approach to the determination of adsorption and methods for determining the size of disperse adsorbents by dynamic light scattering and sedimentation analysis in the field of centrifugal forces. Three sections were found on the isotherm of adsorption: in the first, isolated islands of adsorbed macromolecules formed; in the second, layers of macromolecules with a different degree of deformation were observed; in the third, determining the adsorption of macromolecules is complicated by other accompanying processes, and assessing the state of macromolecules in the adsorption layer becomes difficult.

  13. Effects of light irradiation on bleaching by a 3.5% hydrogen peroxide solution containing titanium dioxide

    International Nuclear Information System (INIS)

    Suemori, T; Kato, J; Nakazawa, T; Akashi, G; Igarashi, A; Hirai, Y; Kumagai, Y; Kurata, H

    2008-01-01

    A low-concentration hydrogen peroxide solution containing titanium dioxide as a photocatalyst has attracted attention as a safe office bleaching agent. In this study, the influence of different kinds of light on the bleaching effect of this agent was examined. The bleaching agent was applied to hematoporphyrin-stained paper strips that were then irradiated with a 405-nm diode laser (800 mW/cm 2 ), a halogen lamp (720 mW/cm 2 ), or an LED (835 mW/cm 2 ) for 5 minutes. The color was measured spectrophotometrically before treatment and every 30 seconds thereafter, and the effects of bleaching on the strip were assessed using the CIE 1976 L * a * b * color coordinate system. Of the three different irradiation conditions, 405-nm laser irradiation gave the strongest bleaching effect with 3.5% hydrogen peroxide containing titanium dioxide. The laser provides strong irradiance at 405 nm, which corresponds to the absorption range of the bleaching agent, and consequently the largest effect was obtained

  14. Non-ferrous metals, anorganic and organic materials resistent to fluorides

    International Nuclear Information System (INIS)

    Hauffe, K.

    1986-01-01

    Aluminium and its alloys are resistant in fluoride solutions up to 400 K. Aluminium is also a suitable reactor material for the thermal decomposition of acidic fluorides between 750 and 825 K. Brass corrodes at room temperature in a 0,1 m KF solution with and without inhibitors very slowly ( -1 ). Nickel and the nickel alloys Inconel 600, Hastelloy N and Monel 500 are the most resistant materials against fluoride solutions and melts. A similar behavior exhibit zirconium-titanium-iron and zirconium-titanium-molybdenum alloys, respectively. From the inorganic compounds, compressed graphite, Al 2 O 3 and hexaborides of earth and rare earth metals, particularly LaB 6 , are extraordinarily resistant against fluorine ions at high temperatures. If the reaction temperature remains below 370 K, then polymers and resins, e.g. polyolefines, PVC, acrylic and epoxy resins and fluorcarbon resins can be employed as coating or compound material (resin + carbon fibers) resistant against fluorine ions up to 370 K. (orig.) [de

  15. Fluoridation Basics

    Science.gov (United States)

    ... return on investment for community water fluoridation (including productivity losses) ranged from $4 in small communities of ... National Center for Chronic Disease Prevention and Health Promotion Email Recommend Tweet YouTube Instagram Listen Watch RSS ...

  16. Fluoride free new nano-particles-Mn-Biotite synthesis for removal of some toxic heavy metals, Th(IV) and U(VI) from aqueous solutions

    International Nuclear Information System (INIS)

    Elsabawy, K. M.; Abou-Sekkina, M. M.

    2013-01-01

    The present paper aims to synthesize new family of fluoride free Mn- Biotite type having the optimized formula NaMn/sub 2.5/(Al,Si)/sub 4/O/sub 10/(OH)/sub 2/. The free fluoride Mn- Biotite was prepared carefully by using solid- state reaction technique using nominal compositions of individual oxides in the main formula for the potential removal of some heavy metals and some radioactive elements from aqueous solution. The crystal structure of Mn-Biotite was well characterized via powder X-ray diffraction (XRD). The particle size was estimated and found to be 54 nm. Analysis of XRD profile indicated that Mn- Biotite is belonging mainly to the monoclinic crystal structure. Infrared spectroscopy (IR) showed the most intensive absorption peaks for monoclinic phase observed at 3420, 2360, 1620, 1440cm/sup -1/. Furthermore the morphological microstructure was investigated by SE-microscopy (SEM), the estimated grain size was found to be in between (0.8-7.7) micro m. Electron spin resonance (ESR) proved that Mn-biotite has paramagnetic behavior. Also DC- electrical conductivity and TGA were investigated. In conclusion results suggest that the synthesized Mn- biotite can be used as good ion exchanger with high performance to remove heavy metals and some radioactive species from wastewater. (author)

  17. Stability constants of the fluoride complexes of actinides in aqueous solution and their correlation with fundamental properties

    International Nuclear Information System (INIS)

    Chaudhuri, N.K.; Sawant, R.M.

    1997-09-01

    Stability constants of the fluoride complexes of the actinides in different oxidation states measured by potentiometric method using fluoride ion selective electrode have been presented. Procedure and precautions required to overcome certain difficulties particular to actinide ions have been discussed. Literature data from various sources have been compiled. In order to have a reasonable comparison the stability constant (β 1 ) values obtained in diverse ionic strength media are converted to thermodynamic stability constant, β 1 0 , using Davies equation (a modification of Debye-Huckel equation). A correlation of the β 1 0 values with the fundamental properties of the actinide ions using various models available in the literature has been attempted. A semiempirical relation recently developed by Brown, Sylva and Ellis (BSE equation) appears to be most suitable. Using the values of ionic radii and best available values of the stability constants of a large number of metal ions from recent compilations a comparative study of the various models or relations available in the literature has been tried. For metal ions in general, the best correlation is obtained with the BSE equation. In an attempt to accommodate the unusual trend in the stability constants of the tetravalent actinides a modification in a parameter of the BSE equation has been proposed. Good agreement between the theoretically calculated and experimentally determined values for actinides in different oxidation states is then obtained in most of the cases. (author)

  18. Properties of experimental titanium cast investment mixing with water reducing agent solution.

    Science.gov (United States)

    Zhang, Zutai; Ding, Ning; Tamaki, Yukimichi; Hotta, Yasuhiro; Han-Cheol, Cho; Miyazaki, Takashi

    2012-01-01

    This study aimed to develop a dental investment for titanium casting. ZrO(2) and Al(2)O(3) were selected as refractory materials to prepare three investments (Codes: A-C) according to the quantity of Zr. Al(2)O(3) cement was used as a binder at a ratio of 15%, they were mixed with special mixing liquid. B1 was used as a control mixed with water. Fundamental examinations were statistically evaluated. A casting test was performed with investment B. Fluidities, setting times, and green strengths showed no remarkable differences; however, they were significantly different from those of B1. Expansion values for A, B, C, and B1 at 850°C were 1.03%±0.08%, 1.96%±0.17%, 4.35%±0.23%, and 1.50%±0.28%, respectively. Castings were covered by only small amounts of mold materials. The hardness test showed no significant differences between castings from B and the ones from commercial investments. The experimental special mixing liquid effectively reduced the water/powder ratio and improved the strength and thermal expansion.

  19. Synthesis of titanium oxide nanoparticles using DNA-complex as template for solution-processable hybrid dielectric composites

    Energy Technology Data Exchange (ETDEWEB)

    Ramos, J.C. [Center for Sustainable Materials Chemistry, 153 Gilbert Hall, Oregon State University, Corvallis, OR (United States); Mejia, I.; Murphy, J.; Quevedo, M. [Department of Materials Science and Engineering, University of Texas at Dallas, Dallas, TX (United States); Garcia, P.; Martinez, C.A. [Engineering and Technology Institute, Autonomous University of Ciudad Juarez, Ciudad Juarez, Chihuahua (Mexico)

    2015-09-15

    Highlights: • We developed a synthesis method to produce TiO{sub 2} nanoparticles using a DNA complex. • The nanoparticles were anatase phase (~6 nm diameter), and stable in alcohols. • Composites showed a k of 13.4, 4.6 times larger than the k of polycarbonate. • Maximum processing temperature was 90 °C. • Low temperature enables their use in low-voltage, low-cost, flexible electronics. - Abstract: We report the synthesis of TiO{sub 2} nanoparticles prepared by the hydrolysis of titanium isopropoxide (TTIP) in the presence of a DNA complex for solution processable dielectric composites. The nanoparticles were incorporated as fillers in polycarbonate at low concentrations (1.5, 5 and 7 wt%) to produce hybrid dielectric films with dielectric constant higher than thermally grown silicon oxide. It was found that the DNA complex plays an important role as capping agent in the formation and suspension stability of nanocrystalline anatase phase TiO{sub 2} at room temperature with uniform size (∼6 nm) and narrow distribution. The effective dielectric constant of spin-cast polycarbonate thin-films increased from 2.84 to 13.43 with the incorporation of TiO{sub 2} nanoparticles into the polymer host. These composites can be solution processed with a maximum temperature of 90 °C and could be potential candidates for its application in low-cost macro-electronics.

  20. Solution and precipitation hardening of two-phase gamma titanium alloy; Mischkristall- und Ausscheidungshaertung zweiphasiger Gamma-Titanaluminidlegierungen

    Energy Technology Data Exchange (ETDEWEB)

    Christoph, U. [GKSS-Forschungszentrum Geesthacht GmbH (Germany). Inst. fuer Werkstofforschung

    1997-12-31

    The present study on solution and precipitation hardening of two-phase gamma titanium aluminides was directed towards improved creep resistance. Alloys were systematically doped with carbon up to 0.37 atomic percent. Solid solutions and precipitates of carbon were formed by different thermal treatments. The hardening obtained as a result of the different precipitate conditions was measured by deformation experiments between 293 and 973 K. An increase of yield stress of up to 300 MPa was observed for finely distributed perovskite precipitates. This increase of yield stress was maintained up to 973 K and was shown to be dominantly athermal in character from activation parameter measurements. Electron microscopic investigations confirmed the athermal nature of the perovskite precipitates to dislocation motion. The precipitates thus act as barriers to dislocation glide over a wide temperature range and can therefore increase the creep resistance at the anticipated operation temperature of 973 K. In addition to studying the mechanism of precipitation hardening, the pinning of dislocations by the formation of impurity atmospheres has also been investigated. This phenomenon is effective at intermediate temperatures of around 550 K and is thought to be caused by very mobile elements such as iron and boron. These elements are present in all alloys of technical relevance. (orig.) 158 refs.

  1. Effects of electrode distance and nature of electrolyte on the diameter of titanium dioxide nanotube

    Energy Technology Data Exchange (ETDEWEB)

    Abbasi, S., E-mail: sum.abbasi@gmail.com; Mohamed, N. M., E-mail: noranimuti-mohamed@petronas.com.my; Singh, B. S. M., E-mail: balbir@petronas.com.my [Department of Fundamental and Applied Sciences Unviersiti Teknologi PETRONAS, 31750, Bandar Seri Iskandar (Malaysia); Abbasi, S. H., E-mail: sarfrazabbasi@gmail.com [SABIC Plastic Application Development Center, Riyadh Technovalley, Riyadh (Saudi Arabia)

    2015-07-22

    The titanium nanotubes were synthesized using viscous electrolytes consisting of ethylene glycol and non-viscous electrolytes consisting of aqueous solution of hydrofluoric acid. Sodium fluoride and ammonium fluoride were utilized as the source of fluorine ions. The samples were then characterized by field emission scanning electron microscope (FE-SEM). Their morphologies were investigated under different anodic potentials and various electrolyte compositions. It was found out that nanotubes can be obtained in fluoride ions and morphology is dependent on various parameters like anodic potential, time, electrolyte composition and the effects by varying the distance between the electrodes on the morphology was also investigated. It was found that by altering the distance between the electrodes, change in the diameter and the porosity was observed.

  2. Studying titanium-molybdenum-zirconium alloys of increased corrosion resistance in acid solutions

    International Nuclear Information System (INIS)

    Tomashov, N.D.; Kazarin, V.I.; Mikheev, V.S.; Goncharenko, B.A.; Sigalovskaya, T.M.; Kalyanova, M.P.

    1977-01-01

    New promising Ti-Mo-Nb-Zr system alloys, possessing good workability and a high corrosion resistance in non-oxidizing solutions of acids, have been developed. The alloys may be recommended as structural materials for equipment operating in severely agressive acid media, such as hydrochloric, sulphuric and phosphoric acids. The corrosion resistance of alloys of the above system in solutions of H 2 SO 4 , HCl and H 3 PO 4 acids may be maximized by increasing the overall alloying to 42% (keeping the ratio of the alloying components Mo/Nb/Zr=4/1/1 unchanged), while retaining sufficiently good plasticity and workability

  3. Scandium fluorides

    International Nuclear Information System (INIS)

    Melnikov, P.; Nalin, M.; Messaddeq, Y.

    1997-01-01

    A new modification of scandium fluoride has been synthesised. The compound is deficient in fluorine, with the composition ScF 2.76 . It belongs to the tetragonal system, lattice parameters being a=3.792 and c=6.740 A and may be obtained at low temperatures by the decomposition of the precursor NH 4 ScF 4 . The reaction is topotactic, tetragonal parameters of the precursor are a=4.021 and c=6.744 A. Structural relationships with various fluorides and ammonium aminofluorides are discussed. This synthesis route with IR-assisted decomposition should be considered as a soft-chemistry approach. (orig.)

  4. Polysaccharide-thickened aqueous fluoride solutions for rapid destruction of the nerve agent VX. Introducing the opportunity for extensive decontamination scenarios.

    Science.gov (United States)

    Elias, Shlomi; Saphier, Sigal; Columbus, Ishay; Zafrani, Yossi

    2014-01-01

    Among the chemical warfare agents, the extremely toxic nerve agent VX (O-ethyl S-2-(diisopropylamino)ethyl methylphosphonothioate) is a target of high importance in the development of decontamination methods, due to its indefinite persistence on common environmental surfaces. Liquid decontaminants are mostly characterized by high corrosivity, usually offer poor coverage, and tend to flow and accumulate in low areas. Therefore, the development of a noncorrosive decontaminant, sufficiently viscous to resist dripping from the contaminated surface, is necessary. In the present paper we studied different polysaccharides-thickened fluoride aqueous solutions as noncorrosive decontaminants for rapid and efficient VX degradation to the nontoxic product EMPA (ethyl methylphosphonic acid). Polysaccharides are environmentally benign, natural, and inexpensive. Other known decontaminants cannot be thickened by polysaccharides, due to the sensitivity of the latter toward basic or oxidizing agents. We found that the efficiency of VX degradation in these viscous solutions in terms of kinetics and product identity is similar to that of KF aqueous solutions. Guar gum (1.5 wt %) with 4 wt % KF was chosen for further evaluation. The benign nature, rheological properties, adhering capabilities to different surfaces, and decontamination from a porous matrix were examined. This formulation showed promising properties for implementation as a spray decontaminant for common and sensitive environmental surfaces.

  5. Photocatalysis of zinc oxide nanotip array/titanium oxide film heterojunction prepared by aqueous solution deposition

    Science.gov (United States)

    Lee, Ming-Kwei; Lee, Bo-Wei; Kao, Chen-Yu

    2017-05-01

    A TiO2 film was prepared on indium tin oxide (ITO)/glass by aqueous solution deposition (ASD) with precursors of ammonium hexafluoro-titanate and boric acid at 40 °C. The photocatalysis of annealed TiO2 film increases with increasing growth time and decreases with increasing growth times longer than 60 min. A ZnO nanotip array was prepared on ZnO seed layer/TiO2 film/glass by aqueous solution deposition with precursors of zinc nitrate and ammonium hydroxide at 70 °C. The photocatalysis of ASD-ZnO/ASD-TiO2 film/ITO glass can be better than that of P25.

  6. Characteristics of zinc oxide nanorod array/titanium oxide film heterojunction prepared by aqueous solution deposition

    Science.gov (United States)

    Lee, Ming-Kwei; Hong, Min-Hsuan; Li, Bo-Wei

    2016-07-01

    The characteristics of a ZnO nanorod array/TiO2 film heterojunction were investigated. A TiO2 film was prepared on glass by aqueous solution deposition with precursors of ammonium hexafluorotitanate and boric acid at 40 °C. Then, a ZnO seed layer was prepared on a TiO2 film/glass substrate by RF sputtering. A vertically oriented ZnO nanorod array was grown on a ZnO seed layer/TiO2 film/glass substrate by aqueous solution deposition with precursors of zinc nitrate and hexamethylenetetramine (HMT) at 70 °C. After thermal annealing in N2O ambient at 300 °C, this heterojunction used as an oxygen gas sensor shows much better rise time, decay time, and on/off current ratio than as-grown and annealed ZnO nanorods.

  7. Solution equilibrium behind the room-temperature synthesis of nanocrystalline titanium dioxide

    Science.gov (United States)

    Seisenbaeva, Gulaim A.; Daniel, Geoffrey; Nedelec, Jean-Marie; Kessler, Vadim G.

    2013-03-01

    Formation of nanocrystalline and monodisperse TiO2 from a water soluble and stable precursor, ammonium oxo-lactato-titanate, (NH4)8Ti4O4(Lactate)8.4H2O, often referred to as TiBALDH or TALH, is demonstrated to be due to a coordination equilibrium. This compound, individual in the solid state, exists in solution in equilibrium with ammonium tris-lactato-titanate, (NH4)2Ti(Lactate)3 and uniform crystalline TiO2 nanoparticles (anatase) stabilized by surface-capping with lactate ligands. This equilibrium can be shifted towards nano-TiO2via application of a less polar solvent like methanol or ethanol, dilution of the solution, introduction of salts or raising the temperature, and reverted on addition of polar and strongly solvating media such as dimethyl sulfoxide, according to NMR. Aggregation and precipitation of the particles were followed by DLS and could be achieved by a decrease in their surface charge by adsorption of strongly hydrogen-bonding cations, e.g. in solutions of ammonia, ethanolamine or amino acid arginine or by addition of ethanol. The observed equilibrium may be involved in formation of nano-titania on the surface of plant roots exerting chelating organic carboxylate ligands and thus potentially influencing plant interactions.Formation of nanocrystalline and monodisperse TiO2 from a water soluble and stable precursor, ammonium oxo-lactato-titanate, (NH4)8Ti4O4(Lactate)8.4H2O, often referred to as TiBALDH or TALH, is demonstrated to be due to a coordination equilibrium. This compound, individual in the solid state, exists in solution in equilibrium with ammonium tris-lactato-titanate, (NH4)2Ti(Lactate)3 and uniform crystalline TiO2 nanoparticles (anatase) stabilized by surface-capping with lactate ligands. This equilibrium can be shifted towards nano-TiO2via application of a less polar solvent like methanol or ethanol, dilution of the solution, introduction of salts or raising the temperature, and reverted on addition of polar and strongly solvating

  8. Interaction of titanium and zirconium hydroxides with aqueous solutions of lead(2) salts

    International Nuclear Information System (INIS)

    Savenko, V.G.; Sakharov, V.V.; Nurgalieva, A.A.; Petrov, K.I.

    1980-01-01

    The mixed phases, characterized by the Pb : Zr 4 ratio are synthesized during the process of geterophase interaction of zirconium hydroxide with solutions of lead nitrate and acetate. The process of the mixed phases thermolysis on the base of amorphous zirconium hydroxides is investigated by the methods of DTA, X-ray phase analysis and IR spectroscopy. The metastable phases are formed during the thermolysis process

  9. Influence of solution treatment on microstructure evolution of TC21 titanium alloy with near equiaxed β grains fabricated by laser additive manufacture

    International Nuclear Information System (INIS)

    Zhang, Q.; Chen, J.; Tan, H.; Lin, X.; Huang, W.D.

    2016-01-01

    Laser additive manufacture (LAM) is a novel technique in which metal components can be fabricated layer by layer. In this paper, the effects of solution temperature and cooling rate on microstructure evolution of the LAMed TC21 titanium alloy which containing near equiaxed prior β grains were studied. The LAMed and solution treated samples were investigated by optical microscopy (OM), scanning election microscope (SEM) and X-ray diffractometer (XRD). The results indicate that both the α phase volume fraction and α laths width are affected by the solution temperature and cooling rate. Different microstructure characterization leads to different Vickers hardness values. However, the solution temperatures selected in this study have insignificant effects on the β and α phase texture. The near equiaxed prior β grains exhibits much weaker texture intensity than the typical columnar prior β grains. The comparison of the calculated and measured α phase texture indicates that variant selection occurred during the solution treatment. The martensite α′ phase precipitated during the layer by layer process shows weak variant selection tendency. - Highlights: • LAMed TC21 titanium alloy containing near equiaxed β grains was fabricated. • Near equiaxed β grains exhibit weaker texture intensity than columnar β grains. • The solution treatment below T_β had insignificant effect on α phase texture. • Variant selection occurred during the solution treatment.

  10. Fracture of nickel-titanium superelastic alloy in sodium hypochlorite solution

    International Nuclear Information System (INIS)

    Yokoyama, Ken'ichi; Kaneko, Kazuyuki; Yabuta, Eiji; Asaoka, Kenzo; Sakai, Jun'ichi

    2004-01-01

    Fracture of the Ni-Ti superelastic alloy for endodontic instruments such as files was investigated with a sustained tensile-loading test in sodium hypochlorite (NaOCl) solution of various concentrations. It was found that the time to fracture was reduced when the applied stress exceeded the critical stress for martensite transformation. When the applied stress was higher than the critical stress, the 0.3 mm diameter wires of the Ni-Ti superelastic alloy sometimes fractured within 60 min. From the results of observations of the fracture surface using a scanning electron microscope, it was revealed that the fracture of the Ni-Ti superelastic alloy is significantly influenced by corrosion when the applied stress was higher than the critical stress for martensite transformation. The results of the present study suggest that one of the causes of the fracture of Ni-Ti files during clinical use is corrosion under the applied stress above the critical stress for martensite transformation in NaOCl solution

  11. Electrochemical formation of GaAs honeycomb structure using a fluoride-containing (NH{sub 4}){sub 2}SO{sub 4} solution

    Energy Technology Data Exchange (ETDEWEB)

    Morishita, Yoshitaka, E-mail: morisita@cc.tuat.ac.jp; Yamamoto, Hitoshi; Yokobori, Kuniyuki

    2014-04-01

    GaAs substrates were anodized in the (NH{sub 4}){sub 2}SO{sub 4} electrolyte with various fluoride concentrations. Scanning electron microscope (SEM) observation showed that highly regular honeycomb hollows were formed on the substrates anodized in the (NH{sub 4}){sub 2}SO{sub 4} electrolyte with a small amount of HF concentration. The regularity of hollows decreased with the increase of HF concentration. The average diameter of hollows increased with increasing anodizing voltage. The regularity of hollow diameters increased with the increase of anodizing time, irrespective of the anodizing voltage. Cross-sectional SEM image showed that the average depth of regular hollows was about 5 nm. In addition to the peak in the region of fundamental adsorption of GaAs with the peak wavelength at about 870 nm, photoluminescence spectra of samples anodized in the (NH{sub 4}){sub 2}SO{sub 4} electrolyte with HF concentration of 0.5 ml showed several peaks at about 610, 635, 670 and 720 nm. - Highlights: • We report on the electrochemical formation of GaAs honeycomb structure. • High regular hollows were formed by anodization in HF-containing (NH{sub 4}){sub 2}SO{sub 4} solution. • A thin porous layer was formed by anodization in HF-containing (NH{sub 4}){sub 2}SO{sub 4} solution. • This process is useful for preparing patterned substrate with a thin porous layer.

  12. Electrochemically formed passive layers on titanium - preparation and biocompatibility assessment in Hank's balanced salt solution

    International Nuclear Information System (INIS)

    Zhao, B.; Jerkiewicz, G.

    2006-01-01

    Uniform and crack-free passive layers on Ti are prepared using AC voltage in 7.5 wt.% aq. NH 4 ·BF 4 at 25 o C. The passive layers possess coloration (wide spectrum of colors) that depends on the experimental conditions. The biocompatibility of such prepared passive layers is evaluated using corrosion science and analytical techniques. Their corrosion behavior, Ti-ion release, surface roughness, and wettability in Hank's Balanced Salt Solution (HBSS) at 37 o C are the main focus of this work. Open-circuit potential and polarization measurements demonstrate that the corrosion potential (E corr ) of the passive layers becomes more positive than that of the untreated Ti. The value of E corr increases as we increase the AC voltage (VAC). Their corrosion rate (CR) is lower than that of the untreated Ti, and they reduced the Ti-ion release level from 230 to 15 ppb. An increase in the AC voltage frequency (f) leads to a slightly higher level of the Ti-ion release (∼50 ppb). Surface profilometry, optical microscopy, and scanning electron microscopy (SEM) analyses show that prolonged exposure of the passive layers to HBSS results in changes to their surface topography. The passive layers prepared by the application of AC voltage are rougher and more hydrophilic than the untreated Ti. Our methodology of preparing biocompatible passive layers on Ti might be applied as a new surface treatment procedure for Ti implants. (author)

  13. Bottled Water and Fluoride

    Science.gov (United States)

    ... Private Wells Infant Formula Fluorosis Public Health Service Recommendation Water Operators & Engineers Water Fluoridation Additives Shortages of Fluoridation Additives Drinking Water Pipe Systems CDC-Sponsored Water Fluoridation Training Links to Other ...

  14. Other Fluoride Products

    Science.gov (United States)

    ... Private Wells Infant Formula Fluorosis Public Health Service Recommendation Water Operators & Engineers Water Fluoridation Additives Shortages of Fluoridation Additives Drinking Water Pipe Systems CDC-Sponsored Water Fluoridation Training Links to Other ...

  15. Growth of ceramic coatings on AZ91D magnesium alloys by micro-arc oxidation in aluminate-fluoride solutions and evaluation of corrosion resistance

    International Nuclear Information System (INIS)

    Guo, H.F.; An, M.Z.

    2005-01-01

    Micro-arc oxidization of AZ91D magnesium alloys was studied in solutions containing sodium aluminate and potassium fluoride at constant applied current densities. The influence of applied current densities, concentration and constituents of the electrolyte as well as treatment time on micro-arc oxidization process was investigated, respectively; surface morphology and phase structure were analyzed using scanning electron microscope (SEM) and X-ray powder diffraction (XRD). Potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS) were used to evaluate the corrosion resistance of ceramic coatings formed on magnesium alloys. XRD analyses indicate that the ceramic coatings fabricated on the surface of magnesium alloys by micro-arc oxidization are composed of spinel phase MgAl 2 O 4 and intermetallic phase Al 2 Mg; variation of treatment time arises no obvious difference to phase structure of the ceramic coatings. A few circular pores and micro-cracks are also observed to remain on the ceramic coating surface; the number of the pores is decreasing, while the diameter of the pores is apparently increasing with prolonging of treatment time. The corrosion resistance of ceramic coatings is improved more than 100 times compared with magnesium alloy substrate

  16. Fluoride absorption: independence from plasma fluoride levels

    International Nuclear Information System (INIS)

    Whitford, G.M.; Williams, J.L.

    1986-01-01

    The concept that there are physiologic mechanisms to homeostatically regulate plasma fluoride concentrations has been supported by results in the literature suggesting an inverse relationship between plasma fluoride levels and the absorption of the ion from the gastrointestinal tract of the rat. The validity of the relationship was questioned because of possible problems in the experimental design. The present work used four different methods to evaluate the effect of plasma fluoride levels on the absorption of the ion in rats: (i) the percentage of the daily fluoride intake that was excreted in the urine; (ii) the concentration of fluoride in femur epiphyses; (iii) the net areas under the time-plasma fluoride concentration curves after intragastric fluoride doses; and (iv) the residual amounts or fluoride in the gastrointestinal tracts after the intragastric fluoride doses. None of these methods indicated that plasma fluoride levels influence the rate or the degree or fluoride absorption. It was concluded that, unless extremely high plasma fluoride levels are involved (pharmacologic or toxic doses), the absorption of the ion is independent of plasma levels. The results provide further evidence that plasma fluoride concentrations are not homeostatically regulated

  17. Corrosion behaviour of nanometre sized cerium oxide and titanium oxide incorporated aluminium in NaCl solution

    International Nuclear Information System (INIS)

    Ashraf, P. Muhamed; Edwin, Leela

    2013-01-01

    Highlights: ► Corrosion resistant aluminium incorporated with nano oxides of cerium and titanium. ► 0.2% nano CeO 2 and 0.05% nano TiO 2 showed increased corrosion resistance. ► Nano TiO 2 concentration influenced the optimum performance of the material. ► Comparison of Micro and nano CeO 2 and TiO 2 aluminium showed the latter is best. - Abstract: The study highlights the development of an aluminium matrix composite by incorporating mixture of nanometre sized cerium oxide and titanium oxide in pure aluminium and its corrosion resistance in marine environment. The mixed nanometre sized oxides incorporated aluminium exhibited improved microstructure and excellent corrosion resistance. Corrosion resistance depends on the concentration of nanometre sized titanium oxide. Electrochemical characteristics improved several folds in nanometre sized mixed oxides incorporated aluminium than micrometre sized oxides incorporated aluminium.

  18. DISSOLUTION OF LANTHANUM FLUORIDE PRECIPITATES

    Science.gov (United States)

    Fries, B.A.

    1959-11-10

    A plutonium separatory ore concentration procedure involving the use of a fluoride type of carrier is presented. An improvement is given in the derivation step in the process for plutonium recovery by carrier precipitation of plutonium values from solution with a lanthanum fluoride carrier precipitate and subsequent derivation from the resulting plutonium bearing carrier precipitate of an aqueous acidic plutonium-containing solution. The carrier precipitate is contacted with a concentrated aqueous solution of potassium carbonate to effect dissolution therein of at least a part of the precipitate, including the plutonium values. Any remaining precipitate is separated from the resulting solution and dissolves in an aqueous solution containing at least 20% by weight of potassium carbonate. The reacting solutions are combined, and an alkali metal hydroxide added to a concentration of at least 2N to precipitate lanthanum hydroxide concomitantly carrying plutonium values.

  19. Effect of nitriding surface treatment on the corrosion resistance of dental nickel-titanium files in 5.25% sodium hypochlorite solution

    International Nuclear Information System (INIS)

    Liu, J.-F.; Lin, M.-C.; Hsu, M.-L.; Li, U.-M.; Lin, C.-P.; Tsai, W.-F.; Ai, C.-F.; Chen, L.-K.; Huang, H.-H.

    2009-01-01

    This study investigated the effect of nitriding surface treatment on the corrosion resistance of commercial dental alloy, in the form of helical nickel-titanium (Ni-Ti) files, when treated with 5.25% sodium hypochlorite (NaOCl) solution. The surface of dental helical Ni-Ti files was modified using nitriding treatment at 200 deg. C, 250 deg. C and 300 deg. C in an NH 3 -containing environment. The surface morphology and chemical composition of the Ni-Ti files were analyzed using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), respectively. The corrosion resistance of the Ni-Ti files when treated with a clinical solution of 5.25% NaOCl was evaluated using the linear polarization method and by potentiodynamic polarization curve measurement. The nitriding treatments at different temperatures created titanium nitride (TiN) on the surface of the helical Ni-Ti files. The Ni-Ti files nitrided at 200 deg. C and 250 deg. C showed higher polarization resistance and higher passive film breakdown potential together with a lower passive current than untreated files. The presence of TiN on dental Ni-Ti files significantly increased the corrosion resistance of the files in the presence of 5.25% NaOCl solution.

  20. Effect of nitriding surface treatment on the corrosion resistance of dental nickel-titanium files in 5.25% sodium hypochlorite solution

    Energy Technology Data Exchange (ETDEWEB)

    Liu, J.-F. [Department of Dentistry, National Yang-Ming University, Taipei, Taiwan (China); Department of Dentistry, Taichung Veterans General Hospital, Taichung, Taiwan (China); Lin, M.-C. [Department of Dentistry, National Yang-Ming University, Taipei, Taiwan (China); Department of Dental Laboratory Technology, Central Taiwan University of Science and Technology, Taichung, Taiwan (China); Hsu, M.-L. [Department of Dentistry, National Yang-Ming University, Taipei, Taiwan (China); Li, U.-M. [Dental Department, Cardinal Tien Hospital, Hsintien, Taiwan (China); Lin, C.-P. [Department of Dentistry, National Taiwan University, Taipei, Taiwan (China); Tsai, W.-F.; Ai, C.-F. [Institute of Nuclear Energy Research, Atomic Energy Council, Taoyuan, Taiwan (China); Chen, L.-K. [Department of Dentistry, Taipei City Hospital, Taipei, Taiwan (China); Huang, H.-H. [Department of Dentistry, National Yang-Ming University, Taipei, Taiwan (China); Department of Dentistry, Taipei City Hospital, Taipei, Taiwan (China); Institute of Oral Biology, National Yang-Ming University, Taipei, Taiwan (China)], E-mail: hhhuang@ym.edu.tw

    2009-05-05

    This study investigated the effect of nitriding surface treatment on the corrosion resistance of commercial dental alloy, in the form of helical nickel-titanium (Ni-Ti) files, when treated with 5.25% sodium hypochlorite (NaOCl) solution. The surface of dental helical Ni-Ti files was modified using nitriding treatment at 200 deg. C, 250 deg. C and 300 deg. C in an NH{sub 3}-containing environment. The surface morphology and chemical composition of the Ni-Ti files were analyzed using scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), respectively. The corrosion resistance of the Ni-Ti files when treated with a clinical solution of 5.25% NaOCl was evaluated using the linear polarization method and by potentiodynamic polarization curve measurement. The nitriding treatments at different temperatures created titanium nitride (TiN) on the surface of the helical Ni-Ti files. The Ni-Ti files nitrided at 200 deg. C and 250 deg. C showed higher polarization resistance and higher passive film breakdown potential together with a lower passive current than untreated files. The presence of TiN on dental Ni-Ti files significantly increased the corrosion resistance of the files in the presence of 5.25% NaOCl solution.

  1. Anodic processes in the chemical and electrochemical etching of Si crystals in acid-fluoride solutions: Pore formation mechanism

    Energy Technology Data Exchange (ETDEWEB)

    Ulin, V. P.; Ulin, N. V.; Soldatenkov, F. Yu., E-mail: f.soldatenkov@mail.ioffe.ru [Ioffe Physical–Technical Institute (Russian Federation)

    2017-04-15

    The interaction of heavily doped p- and n-type Si crystals with hydrofluoric acid in the dark with and without contact with metals having greatly differing work functions (Ag and Pd) is studied. The dependences of the dissolution rates of Si crystals in HF solutions that contain oxidizing agents with different redox potentials (FeCl{sub 3}, V{sub 2}O{sub 5} and CrO{sub 3}) on the type and level of silicon doping are determined. Analysis of the experimental data suggests that valence-band holes in silicon are not directly involved in the anodic reactions of silicon oxidation and dissolution and their generation in crystals does not limit the rate of these processes. It is also shown that the character and rate of the chemical process leading to silicon dissolution in HF-containing electrolytes are determined by the interfacial potential attained at the semiconductor–electrolyte interface. The mechanism of electrochemical pore formation in silicon crystals is discussed in terms of selfconsistent cooperative reactions of nucleophilic substitution between chemisorbed fluorine anions and coordination- saturated silicon atoms in the crystal subsurface layer. A specific feature of these reactions for silicon crystals is that vacant nonbonding d{sup 2}sp{sup 3} orbitals of Si atoms, associated with sixfold degenerate states corresponding to the Δ valley of the conduction band, are involved in the formation of intermediate complexes. According to the suggested model, the pore-formation process spontaneously develops in local regions of the interface under the action of the interfacial potential in the adsorption layer and occurs as a result of the detachment of (SiF{sub 2}){sub n} polymer chains from the crystal. Just this process leads to the preferential propagation of pores along the <100> crystallographic directions. The thermodynamic aspects of pore nucleation and the effect of the potential drop across the interface, conduction type, and free-carrier concentration

  2. Titanium ; dream new material

    International Nuclear Information System (INIS)

    Lee, Yong Tae; Kim Seung Eon; Heoon, Yong Taek; Jung, Hui Won

    2001-11-01

    The contents of this book are history of Titanium, present situation of Titanium industry, property of Titanium alloy, types of it, development of new alloy of Titanium smelting of Titanium, cast of Titanium and heat treatment of Titanium, Titanium alloy for plane, car parts, biological health care, and sport leisure and daily life, prospect, and Titanium industrial development of Titanium in China.

  3. Recovery of fluoride ion selective electrode

    International Nuclear Information System (INIS)

    Monteiro, R.P.G.

    1988-01-01

    A recovery procedure of fluoride ion selective electrode based upon the body radiography of inactive electrode and introduction of suitable internal regeneration solution, is developed. The recovered electrode was tested in standard solutions of fluoride ions (10 sup5) to 10 -1M showing as good performance as the new one. The fluor determination by potentiometric measurements with selective electrode is used in nuclear fuel cycle for quality control of thorium and uranium mixed oxide pellets and pellets of uranium dioxides. (author) [pt

  4. Acute toxicity of ingested fluoride.

    Science.gov (United States)

    Whitford, Gary Milton

    2011-01-01

    This chapter discusses the characteristics and treatment of acute fluoride toxicity as well as the most common sources of overexposure, the doses that cause acute toxicity, and factors that can influence the clinical outcome. Cases of serious systemic toxicity and fatalities due to acute exposures are now rare, but overexposures causing toxic signs and symptoms are not. The clinical course of systemic toxicity from ingested fluoride begins with gastric signs and symptoms, and can develop with alarming rapidity. Treatment involves minimizing absorption by administering a solution containing calcium, monitoring and managing plasma calcium and potassium concentrations, acid-base status, and supporting vital functions. Approximately 30,000 calls to US poison control centers concerning acute exposures in children are made each year, most of which involve temporary gastrointestinal effects, but others require medical treatment. The most common sources of acute overexposures today are dental products - particularly dentifrices because of their relatively high fluoride concentrations, pleasant flavors, and their presence in non-secure locations in most homes. For example, ingestion of only 1.8 ounces of a standard fluoridated dentifrice (900-1,100 mg/kg) by a 10-kg child delivers enough fluoride to reach the 'probably toxic dose' (5 mg/kg body weight). Factors that may influence the clinical course of an overexposure include the chemical compound (e.g. NaF, MFP, etc.), the age and acid-base status of the individual, and the elapsed time between exposure and the initiation of treatment. While fluoride has well-established beneficial dental effects and cases of serious toxicity are now rare, the potential for toxicity requires that fluoride-containing materials be handled and stored with the respect they deserve. Copyright © 2011 S. Karger AG, Basel.

  5. Fluoride release and recharge abilities of contemporary fluoride-containing restorative materials and dental adhesives.

    Science.gov (United States)

    Dionysopoulos, Dimitrios; Koliniotou-Koumpia, Eugenia; Helvatzoglou-Antoniades, Maria; Kotsanos, Nikolaos

    2013-01-01

    The aim of this study was to evaluate the fluoride release of five fluoride-releasing restorative materials and three dental adhesives, before and after NaF solution treatment. Five restorative materials (Fuji IX GP, GC Corp.; Ketac N100, 3M ESPE; Dyract Extra, Dentsply; Beautifil II, Shofu Inc.; Wave, SDI) and three dental adhesives (Stae, SDI; Fluorobond II - Shofu Inc.; Prime & Bond NT, Dentsply) were investigated before and after NaF solution treatment. A fluoride ion-selective electrode was to measure fluoride concentrations. During the 86-day period before NaF solution treatment, Fuji IX GP released the highest amount of fluoride among the restorative materials while Prime & Bond NT was the highest among the dental adhesives. After NaF solution treatment, Fuji IX GP again ranked the highest in fluoride release among the restorative materials while Fluorobond II ranked the highest among dental adhesives. It was concluded that the compositions and setting mechanisms of fluoride-containing dental materials influenced their fluoride release and recharge abilities.

  6. Machining of titanium alloys

    CERN Document Server

    2014-01-01

    This book presents a collection of examples illustrating the resent research advances in the machining of titanium alloys. These materials have excellent strength and fracture toughness as well as low density and good corrosion resistance; however, machinability is still poor due to their low thermal conductivity and high chemical reactivity with cutting tool materials. This book presents solutions to enhance machinability in titanium-based alloys and serves as a useful reference to professionals and researchers in aerospace, automotive and biomedical fields.

  7. Anodic growth of titanium dioxide nanostructures

    DEFF Research Database (Denmark)

    2010-01-01

    Disclosed is a method of producing nanostructures of titanium dioxide (TiO 2 ) by anodisation of titanium (Ti) in an electrochemical cell, comprising the steps of: immersing a non-conducting substrate coated with a layer of titanium, defined as the anode, in an electrolyte solution...... an electrical contact to the layer of titanium on the anode, where the electrical contact is made in the electrolyte solution...

  8. Fluoride remediation using floating macrophytes

    Directory of Open Access Journals (Sweden)

    Naba Kumar Mondal

    2014-04-01

    Full Text Available Six aquatic macrophytes, such as Pistia stratiotes, Ceratophyllum demersum, Nymphoides indica, Lemna major, Azolla pinnata,and Eichhornia crassipes were considered for remove fluoride from aqueous solution. Five different concentrations (10, 30, 50, and 100 ppm of fluoride solution were taken in 1 L plastic container. Fixed weight (20 g of macrophytes along with 500 ml fluoride solution was taken in each plastic container for 72 hours observation. Results demonstrated all the macrophytes show highest fluoride removal during 24 h to 48 h, but after 72 h their efficiency reduced drastically. The species N. indica showed better removal efficiency than other experimental macrophytes. In general, pigment measurement data indicated higher concentration at 72 h. However, Pistia sp. showed higher concentration of pigmentation at intermediate time interval (48 h. Higher level of dry weight to fresh weight ratio was recorded for L. major and A. pinnata at all concentrations, excepting at 10 ppm. In addition, all macrophytes showed lower RGR at higher concentration. Isotherm study indicated that macrophyte C. demersum is a good fitted with Freundlich and Langmuir isotherm whereas L. major with Langmuir isotherm during 24 hours.

  9. Fluoride varnish or fluoride mouth rinse?

    DEFF Research Database (Denmark)

    Keller, M K; Klausen, BJ; Twetman, S

    2016-01-01

    OBJECTIVE: In many Danish communities, school-based fluoride programs are offered to children with high caries risk in adjunct to tooth brushing. The purpose of this field trial was to compare the caries-preventive effectiveness of two different fluoride programs in 6-12 year olds. BASIC RESEARCH...... different schools were enrolled after informed consent and their class unit was randomly allocated to one of two fluoride programs. INTERVENTIONS: One group received a semi-annual fluoride varnish applications (FV) and the other group continued with an existing program with fluoride mouth rinses once per...... in caries development over two years among children participating in a school-based fluoride varnish or mouth rinse program....

  10. Fluoride ions vs removal technologies: A study

    Directory of Open Access Journals (Sweden)

    Jagvir Singh

    2016-11-01

    Full Text Available Literature reported that drinking water is a precious and scarce resource and it has to be protected and kept free from any kind of contamination. Further, it has to be used carefully without wasting. Literature also reported that fluoride bearing rocks are abundant in India, as a result, fluoride leaches out and contaminates the adjacent water and soil resources. A high concentration of fluoride ions in ground water increases up to more than 30 mg/L. This high concentration of fluoride ions causes many harmful and dangerous effects on our datum. Fluoride ions in larger quantities i.e. 20–80 mg/day taken over a period of 10–20 years result in crippling and skeletal fluorosis, severely damaging the bone. In the present scenario, there is a continuously increasing worldwide concern for the development of fluoride treatment technologies. Possibilities of reducing the high fluorine content in groundwater are by defluorination process/dilution with the surface water which is a very simple technique but the addition of Ca2+ ions to a solution in contact with fluorite when experimented in distilled water caused an appreciable decrease in fluoride concentration. In this review article, we emphasized the relationship between high concentrations of fluoride ions and their compounds and their health impact.

  11. Adsorbent synthesis of polypyrrole/TiO(2) for effective fluoride removal from aqueous solution for drinking water purification: Adsorbent characterization and adsorption mechanism.

    Science.gov (United States)

    Chen, Jie; Shu, Chiajung; Wang, Ning; Feng, Jiangtao; Ma, Hongyu; Yan, Wei

    2017-06-01

    More than 20 countries are still suffering problems of excessive fluoride containing water, and greater than 8mg/L fluoride groundwater has been reported in some villages in China. In order to meet the challenge in the drinking water defluoridation engineering, a high efficiency and affinity defluoridation adsorbent PPy/TiO 2 composite was designed and synthetized by in-situ chemical oxidative polymerization. Fourier Transform Infrared Spectroscopy (FTIR), X-ray diffraction Investigator (XRD), X-ray photoelectron spectroscopy (XPS), Thermogravimetric analysis (TG), N 2 isotherm analysis, Scanning Electron Microscopy (SEM) and Zeta potential analysis were conducted to characterize surface and textural properties of the as-prepared PPy/TiO 2 , and the possibility of fluoride adsorption was carefully estimated by adsorption isotherm and kinetic studies. Characterization investigations demonstrate the uniqueness of surface and textural properties, such as suitable specific surface area and abundant positively charged nitrogen atoms (N + ), which indicate the composite is a suitable material for the fluoride adsorption. Adsorption isotherms and kinetics follow better with Langmuir and pseudo-second-order model, respectively. The maximum adsorption capacity reaches 33.178mg/g at 25°C according to Langmuir model, and particular interest was the ability to reduce the concentration of fluoride from 11.678mg/L to 1.5mg/L for drinking water at pH of 7 within 30min. Moreover, the adsorbent can be easily recycled without the loss of adsorption capacity after six cycles, greatly highlighting its outstanding affinity to fluoride, low-cost and novel to be used in the purification of fluoride containing water for drinking. Furthermore, the adsorption mechanism was extensively investigated and discussed by FTIR investigation and batch adsorption studies including effect of pH, surface potential and thermodynamics. The adsorption is confirmed to be a spontaneous and exothermic

  12. Calcium fluoride

    International Nuclear Information System (INIS)

    King, C.W.; Nestor, O.H.

    1989-01-01

    A new process for producing large, single, oriented crystals of calcium fluoride (CaF 2 ) has been developed which overcomes the limitations of current growing methods. This process has been reduced to practice and has yielded oriented crystals 17.5 x 17.5 x 5 cm 3 . Currently nearing completion is a system for producing 35 x 35 x 7.5 cm 3 single crystals. A scale up to one-meter-square is considered feasible. This crystal growing process makes possible the fabrication of very large CaF 2 windows. Suitability for very high power lasers, however, requires attention to properties beyond mere size. A process to generate higher purity growth stock (starting material) was also developed. The additional purification of the growth stock contributes to lower bulk absorption, the absence of color centers and increased radiation hardness. Also identified were several specific impurities which correlate with radiation hardness. A correlation was found between color centers induced by laser radiation and ionizing radiation. Other CaF 2 crystal properties such as tensile strength, absorption and laser damage thresholds were studied and are discussed

  13. No calcium-fluoride-like deposits detected in plaque shortly after a sodium fluoride mouthrinse.

    Science.gov (United States)

    Vogel, G L; Tenuta, L M A; Schumacher, G E; Chow, L C

    2010-01-01

    Plaque 'calcium-fluoride-like' (CaF(2)-like) and fluoride deposits held by biological/bacterial calcium fluoride (Ca-F) bonds appear to be the source of cariostatic concentrations of fluoride in plaque fluid. The aim of this study was to quantify the amounts of plaque fluoride held in these reservoirs after a sodium fluoride rinse. 30 and 60 min after a 228 microg/g fluoride rinse, plaque samples were collected from 11 volunteers. Each sample was homogenized, split into 2 aliquots (aliquots 1 and 2), centrifuged, and the recovered plaque fluid combined and analyzed using microelectrodes. The plaque mass from aliquot 1 was retained. The plaque mass from aliquot 2 was extracted several times with a solution having the same fluoride, calcium and pH as the plaque fluid in order to extract the plaque CaF(2)-like deposits. The total fluoride in both aliquots was then determined. In a second experiment, the extraction completeness was examined by applying the above procedure to in vitro precipitates containing known amounts of CaF(2)-like deposits. Nearly identical fluoride concentrations were found in both plaque aliquots. The extraction of the CaF(2)-like precipitates formed in vitro removed more than 80% of these deposits. The results suggest that either CaF(2)-like deposits were not formed in plaque or, if these deposits had been formed, they were rapidly lost. The inability to form persistent amounts of CaF(2)-like deposits in plaque may account for the relatively rapid loss of plaque fluid fluoride after the use of conventional fluoride dentifrices or rinses. (c) 2010 S. Karger AG, Basel.

  14. Story of Fluoridation

    Science.gov (United States)

    ... Home Health Info Health Topics Fluoride Share The Story of Fluoridation It started as an observation, that ... this time using photospectrographic analysis, a more sophisticated technology than that used by McKay. Churchill asked an ...

  15. Fluoride in diet

    Science.gov (United States)

    Diet - fluoride ... bones and teeth. Too much fluoride in the diet is very rare. Rarely, infants who get too ... of essential vitamins is to eat a balanced diet that contains a variety of foods from the ...

  16. Removal of fluoride from aqueous nitric acid

    International Nuclear Information System (INIS)

    Pruett, D.J.; Howerton, W.B.; Mailen, J.C.

    1981-06-01

    Several methods for removing fluoride from aqueous nitric acid were investigated and compared with the frequently used aluminum nitrate-calcium nitrate (Ca 2+ -Al 3+ ) chemical trap-distillation system. Zirconium oxynitrate solutions were found to be superior in preventing volatilization of fluoride during distillation of the nitric acid, producing decontamination factors (DFs) on the order of 2 x 10 3 (vs approx. 500 for the Ca 2+ -Al 3+ system). Several other metal nitrate systems were tested, but they were less effective. Alumina and zirconia columns proved highly effective in removing HF from HF-HNO 3 vapors distilled through the columns; fluoride DFs on the order of 10 6 and 10 4 , respectively, were obtained. A silica gel column was very effective in adsorbing HF from HF-HNO 3 solutions, producing a fluoride DF of approx. 10 4

  17. Comparative study on the corrosion behavior of Ti-Nb and TMA alloys for dental application in various artificial solutions

    International Nuclear Information System (INIS)

    Bai, Y.J.; Wang, Y.B.; Cheng, Y.; Deng, F.; Zheng, Y.F.; Wei, S.C.

    2011-01-01

    The corrosion behavior of Ti-Nb dental alloy in artificial saliva with and without the addition of lactic acid and sodium fluoride was investigated by electrochemical techniques, with the commercial Titanium-molybdenum alloy (TMA) as a comparison. The chemical composition, microstructure and constitutional phase were characterized via energy dispersive spectrometry, optical microscope and X-ray diffraction, meanwhile the open circuit potential, electrochemical impedance spectroscopy and potentiodynamic polarization measurements were carried out to study the corrosion resistance of experimental alloys, with the corroded surface being further characterized by scanning electron microscopy and X-ray photoelectron spectroscopy. It was found that the corrosion behavior of Ti-Nb alloy was similar to those TMA alloy samples in both artificial and acidified saliva solutions, whereas statistical analysis of the electrochemical impedance spectroscopy and polarization parameters showed Ti-Nb alloy exhibited better corrosion resistance in fluoridated saliva and fluoridated acidified saliva. SEM observation indicated that TMA alloy corroded heavily than Ti-Nb alloy in fluoride containing saliva. XPS surface analysis suggested that Nb 2 O 5 played an important role in anti-corrosion from the attack of fluoride ion. Based on the above finding, Ti-Nb alloy is believed to be suitable for the usage in certain fluoride treated dental works with excellent corrosion resistance in fluoride-containing oral media.

  18. Chemico-therapeutic approach to prevention of dental caries. [using stannous fluoride gel

    Science.gov (United States)

    Shannon, I. L.

    1975-01-01

    The program of chemical preventive dentistry is based primarily upon the development of a procedure for stabilizing stannous fluoride in solution by forcing it into glycerin. New topical fluoride treatment concentrates, fluoride containing gels and prophylaxis pastes, as well as a completely stable stannous fluoride dentifrice are made possible by the development of a rather complicated heat application method to force stannous fluoride into solution in glycerin. That the stannous fluoride is clinically effective in such a preparation is demonstrated briefly on orthodontic patients.

  19. Hydroxyapatite, fluor-hydroxyapatite and fluorapatite produced via the sol-gel method: bonding to titanium and scanning electron microscopy.

    Science.gov (United States)

    Tredwin, Christopher J; Georgiou, George; Kim, Hae-Won; Knowles, Jonathan C

    2013-05-01

    Hydroxyapatite (HA), fluor-hydroxyapatite (FHA) with varying levels of fluoride ion substitution and fluorapatite (FA) production has been characterised and optimised by the sol-gel method and the dissolution and biological properties of these materials were investigated. It was the objective of this study to investigate the potential bond strength and interaction of these materials with titanium. HA, FHA and FA were synthesised by a sol-gel method. Calcium nitrate and triethyl phosphite were used as precursors under an ethanol-water based solution. Different amounts of ammonium fluoride (NH4F) were incorporated for the preparation of the FHA and FA sol-gels. Using a spin coating technique the sol-gels were coated onto commercially pure titanium disks and crystallised at various temperatures. Using scanning electron microscopy (SEM) and elemental analysis, the surface characteristics, coating thickness and interaction of the Ti substrate and coating were investigated. The bond strengths of the coating to the Ti were investigated using an Instron Universal Load Testing Machine. Statistical analysis was performed with a two-way analysis of variance and post hoc testing with a Bonferroni correction. (1) Coating speed inversely influenced the coating thickness. (2) Increasing fluoride ion substitution and heating temperature significantly increased bond strength and (3) increasing fluoride ion substitution increased the coating thickness. FHA and FA synthesised using the sol-gel technique may offer a superior alternative to coating titanium implants with HA and plasma spraying. HA, FHA and FA materials synthesised by the sol-gel method may also have a use as bone grafting materials. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  20. Fluoride method for silicon determination i silicovadium

    International Nuclear Information System (INIS)

    Komarnitskaya, N.N.; Sergeev, K.I.; Shamraj, Z.Ya.

    1977-01-01

    The method used was based on formation of a silicon-potassium fluoride-sodium sediment in strongly acid medium in the presence of excess potassium chloride which decreased the sediment solubility. The sediment was dissolved in hot water to titrate the resultant hydrofluoric acid with a caustic potash solution in the presence of phenolphthalein. Gravity hydrochloric and volumetric fluoride methods were used to compare the results of silicon estimation

  1. The effectiveness of the biannual application of silver nitrate solution followed by sodium fluoride varnish in arresting early childhood caries in preschool children: study protocol for a randomised controlled trial.

    Science.gov (United States)

    Chu, Chun-Hung; Gao, Sherry Shiqian; Li, Samantha Ky; Wong, May Cm; Lo, Edward Cm

    2015-09-25

    The application of 38 % silver diamine fluoride (SDF) has been shown to be effective in arresting early childhood caries (ECC). Since SDF is not available in certain countries, some dentists use adjunctive application of 25 % silver nitrate (AgNO3) and 5 % sodium fluoride (NaF) to arrest ECC. This randomised controlled trial will systematically compare the efficacy of a 25 % AgNO3 solution followed by 5 % NaF varnish with that of a 38 % SDF solution in arresting ECC when applied at half-yearly intervals over a 30-month period. This study is a randomised, double-blinded, non-inferiority clinical trial. The hypothesis tested is that adjunctive application of 25 % AgNO3 followed by 5 % NaF is at least not appreciably worse than a 38 % SDF in arresting ECC. Approximately 3100 kindergarten children aged 3-4 years will be screened and at least 1070 children with caries will be recruited. This sample size is sufficient for an appropriate statistical analysis (power at 90 % (β = 0.10) with a 2-sided type-I error of α = 0.05), allowing for an overall 20 % drop-out rate. The children will be randomly allocated into 2 groups to treat their caries over a 30-month period: Group A - biannual adjunctive application of a 25 % AgNO3 solution and a 5 % NaF varnish, and Group B - biannual adjunctive application of a 38 % SDF solution followed by a placebo varnish. Clinical examinations will be conducted at 6-month intervals. Primary outcome measured is the number of active caries surfaces which are arrested. Information on confounding factors such as oral hygiene habits will be collected through a parental questionnaire. We expect that adjunctive application of 25 % AgNO3 solution and 5 % NaF varnish and of 38 % SDF solution can both effectively arrest ECC. Lower concentrations of silver and fluoride are contained in 25 % AgNO3 and 5 % NaF, respectively, than in 38 % SDF; therefore, AgNO3/NaF are more favourable for use in young children. Because its use for caries management is

  2. Fluoride glass fiber optics

    CERN Document Server

    Aggarwal, Ishwar D

    1991-01-01

    Fluoride Glass Fiber Optics reviews the fundamental aspects of fluoride glasses. This book is divided into nine chapters. Chapter 1 discusses the wide range of fluoride glasses with an emphasis on fluorozirconate-based compositions. The structure of simple fluoride systems, such as BaF2 binary glass is elaborated in Chapter 2. The third chapter covers the intrinsic transparency of fluoride glasses from the UV to the IR, with particular emphasis on the multiphonon edge and electronic edge. The next three chapters are devoted to ultra-low loss optical fibers, reviewing methods for purifying and

  3. Effect of 4% titanium tetrafluoride solution on the erosion of permanent and deciduous human enamel: an in situ/ex vivo study

    Directory of Open Access Journals (Sweden)

    Ana Carolina Magalhães

    2009-02-01

    Full Text Available This in situ/ex vivo study assessed the effect of titanium tetrafluoride (TiF4 solution on erosion of permanent (P and deciduous (d human enamel. Ten volunteers wore acrylic palatal appliances containing 4 enamel samples, divided into two rows: TiF4 and no - TiF4 (control. Each row contained one deciduous and one permanent enamel sample. During the 1st day, formation of a salivary pellicle was allowed. At the 2nd day, the 4% TiF4 solution was applied on one row (TiF4, while the other row remained untreated (control. From the 3rd until the 7th day, the samples were subjected to erosion by immersion in a cola drink for 5 min, 4 times/day. Enamel alterations were determined by microhardness testing (%SMHC. Data were analyzed using 2 two-way ANOVA and Tukey's post hoc test (α=0.05. The mean %SMHC (±SD amounted to: P (TiF4 - 73.32 ± 5.16 and control - 83.49 ± 4.59 and d (TiF4 - 83.01 ± 7.41 and control - 75.75 ± 2.57. In conclusion, the application of 4% TiF4 solution reduced the softening of permanent enamel but not of deciduous enamel significantly. However, no significant differences were detected between the permanent and deciduous enamel when the factor substrate was considered.

  4. The effect of daily fluoride mouth rinsing on enamel erosive/abrasive wear in situ.

    Science.gov (United States)

    Stenhagen, K R; Hove, L H; Holme, B; Tveit, A B

    2013-01-01

    It is not known whether application of fluoride agents on enamel results in lasting resistance to erosive/abrasive wear. We investigated if one daily mouth rinse with sodium fluoride (NaF), stannous fluoride (SnF(2)) or titanium tetrafluoride (TiF(4)) solutions protected enamel against erosive/abrasive wear in situ (a paired, randomised and blind study). Sixteen molars were cut into 4 specimens, each with one amalgam filling (measurement reference surface). Two teeth (2 × 4 specimens) were mounted bilaterally (buccal aspects) on acrylic mandibular appliances and worn for 9 days by 8 volunteers. Every morning, the specimens were brushed manually with water (30 s) extra-orally. Then fluoride solutions (0.4% SnF(2) pH 2.5; 0.15% TiF(4) pH 2.1; 0.2% NaF pH 6.5, all 0.05 M F) were applied (2 min). Three of the specimens from each tooth got different treatment, and the fourth served as control. At midday, the specimens were etched for 2 min in 300 ml fresh 0.01 M hydrochloric acid and rinsed in tap water. This etch procedure was repeated in the afternoon. Topographic measurements were performed by a white-light interferometer. Mean surface loss (±SD) for 16 teeth after 9 days was: SnF(2) 1.8 ± 1.9 µm, TiF(4) 3.1 ± 4.8 µm, NaF 26.3 ± 4.7 µm, control 32.3 ± 4.4 µm. Daily rinse with SnF(2), TiF(4) and NaF resulted in 94, 90 and 18% reduction in enamel erosive/abrasive wear, respectively, compared with control (p < 0.05). The superior protective effect of daily rinse with either stannous or titanium tetrafluoride solutions on erosive/abrasive enamel wear is promising. Copyright © 2012 S. Karger AG, Basel.

  5. Electrochemical capacitance performance of titanium nitride nanoarray

    Energy Technology Data Exchange (ETDEWEB)

    Xie, Yibing, E-mail: ybxie@seu.edu.cn [School of Chemistry and Chemical Engineering, Southeast University, Nanjing 211189 (China); Suzhou Research Institute of Southeast University, Suzhou 215123 (China); Wang, Yong [School of Chemistry and Chemical Engineering, Southeast University, Nanjing 211189 (China); Du, Hongxiu [School of Chemistry and Chemical Engineering, Southeast University, Nanjing 211189 (China); Suzhou Research Institute of Southeast University, Suzhou 215123 (China)

    2013-12-01

    Highlights: • TiN nanoarray is formed by a nitridation process of TiO{sub 2} in ammonia atmosphere. • TiN nanoarray exhibits much higher EDLC capacitance than TiO{sub 2} nanoarray. • The specific capacitance of TiN nanoarray achieves a high level of 99.7 mF cm{sup −2}. • A flexible solid-state supercapacitor is constructed by TiN nanoarray and PVA gel. -- Abstract: In this study, titanium nitride (TiN) nanoarrays with a short nanotube and long nanopore structure have been prepared by an anodization process of ultra thin titanium foil in ethylene glycol (EG) solution containing ammonium fluoride, subsequent calcination process in an air atmosphere, and final nitridation process in an ammonia atmosphere. The morphology and microstructure characterization has been conducted using field emission scanning electron microscope and X-ray diffraction. The electrochemical properties have been investigated through cyclic voltammetry and electrochemical impedance spectrum measurements. The electrochemical capacitance performance has been investigated by galvanostatic charge–discharge measurements in the acidic, neural and alkali electrolyte solution. Well-defined TiN nanoarrays contribute a much higher capacitance performance than titania (TiO{sub 2}) in the supercapacitor application due to the extraordinarily improved electrical conductivity. Such an electrochemical capacitance can be further enhanced by increasing aspect ratio of TiN nanoarray from short nanotubes to long nanopores. A flexible supercapacitor has been constructed using two symmetrical TiN nanoarray electrodes and a polyvinyl alcohol (PVA) gel electrolyte with H{sub 2}SO{sub 4}–KCl–H{sub 2}O–EG. Such a supercapacitor has a highly improved potential window and still keeps good electrochemical energy storage. TiN nanoarray with a high aspect ratio can act well as an ultra thin film electrode material of flexible supercapacitor to contribute a superior capacitance performance.

  6. Influence of the reuse of the electrolytic solution on the properties of hydroxyapatite coatings produced by plasma electrolytic oxidation of grade 4 titanium

    Energy Technology Data Exchange (ETDEWEB)

    Antonio, Cesar A.; Rangel, Elidiane Cipriano; Cruz, Nilson Cristino, E-mail: cesar.augustoa@hotmail.com [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), Sorocaba, SP (Brazil)

    2016-07-01

    Full text: Plasma electrolytic oxidation (PEO) is a process able to produce oxide coatings on light metals, such as Al, Ti, V, Mg, Ta and Nb. In this technique, the application of a voltage, in the range of hundreds of volts, between the sample and a cathode immersed in an electrolyte solution produces electrical fields intense enough to breakdown the insulating oxide layer on the sample surface giving rise to micro electric sparks[1]. These micro-arcs can locally melt the substrate alloying it with elements in the electrolyte solution [2]. In this work PEO has been used to produce coatings with high concentration of hydroxyapatite on Grade 4 titanium disks. The treatments were performed in a 1 liter stainless steel tank. The tank wall was used as the cathode and the coatings were produced during 120 s using calcium acetate and sodium glycerophosphate water solutions as electrolyte. The samples were biased with 480 V pulses with frequency and duty cycle of 100 Hz and 60%, respectively. Using profilometry, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction it has been evaluated the influence of the number of reuses of the solution on the coating properties. The coating produced contains around 85% of HA and it has not been observed any significant changes in their properties when the same solution was reused up to 5 times. [1] A.L. Yerokhin, X. Nie, A. Leyland, A. Matthews, Surf. Coat. Technol. 130 (2000) 195 206. [2] C. A. Antonio, N. C. Cruz, et al. Materials Research. 17(6) 2014; 1427-1433. (author)

  7. Study of superficial films and of electrochemical behaviour of some nickel base alloys and titanium base alloys in solution representation of granitic, argillaceous and salted ground waters

    International Nuclear Information System (INIS)

    Quang, K.V.; Da Cunha Belo, M.; Benabed, M.S.; Bourelier, F.; Jallerat, N.; Pari, F.L.

    1985-01-01

    The corrosion behaviour of the stainless steels 304, 316 Ti, 25Cr-20Ni-Mo-Ti, nickel base alloys Hastelloy C4, Inconel 625, Incoloy 800, Ti and Ti-0.2% Pd alloy has been studied in the aerated or deaerated solutions at 20 0 C and 90 0 C whose compositions are representative of interstitial ground waters: granitic or clay waters or salt brine. The electrochemical techniques used are voltametry, polarization resistance and complexe impedance measurements. Electrochemical data show the respective influence of the parameters such as temperature, solution composition and dissolved oxygen, addition of soluble species chloride, fluoride, sulfide and carbonates, on which depend the corrosion current density, the passivation and the pitting potential. The inhibition efficiency of carbonate and bicarbonate activities against pitting corrosion is determined. In clay water at 90 0 C, Ti and Ti-Pd show very high passivation aptitude and a broad passive potential range. Alloying Pd increases cathodic overpotential and also transpassive potential. It makes the alloy less sensitive to the temperature effect. Optical Glow Discharge Spectra show three parts in the composition depth profiles of surface films on alloys. XPS and SIMS spectrometry analyses are also carried out. Electron microscopy observation shows that passive films formed on Ti and Ti-Pd alloy have amorphous structure. Analysis of the alloy constituents dissolved in solutions, by radioactivation in neutrons, gives the order of magnitude of the Ni base alloy corrosion rates in various media. It also points out the preferential dissolution of alloying iron and in certain cases of chromium

  8. Effects of fluoridated milk on root dentin remineralization.

    Directory of Open Access Journals (Sweden)

    Wolfgang H Arnold

    Full Text Available The prevalence of root caries is increasing with greater life expectancy and number of retained teeth. Therefore, new preventive strategies should be developed to reduce the prevalence of root caries. The aim of this study was to investigate the effects of fluoridated milk on the remineralization of root dentin and to compare these effects to those of sodium fluoride (NaF application without milk.Thirty extracted human molars were divided into 6 groups, and the root cementum was removed from each tooth. The dentin surface was demineralized and then incubated with one of the following six solutions: Sodium chloride NaCl, artificial saliva, milk, milk+2.5 ppm fluoride, milk+10 ppm fluoride and artificial saliva+10 ppm fluoride. Serial sections were cut through the lesions and investigated with polarized light microscopy and quantitative morphometry, scanning electron microscopy (SEM and energy-dispersive X-ray spectroscopy (EDS. The data were statistically evaluated using a one-way ANOVA for multiple comparisons.The depth of the lesion decreased with increasing fluoride concentration and was the smallest after incubation with artificial saliva+10 ppm fluoride. SEM analysis revealed a clearly demarcated superficial remineralized zone after incubation with milk+2.5 ppm fluoride, milk+10 ppm fluoride and artificial saliva+10 ppm fluoride. Ca content in this zone increased with increasing fluoride content and was highest after artificial saliva+10 ppm fluoride incubation. In the artificial saliva+10 ppm fluoride group, an additional crystalline layer was present on top of the lesion that contained elevated levels of F and Ca.Incubation of root dentin with fluoridated milk showed a clear effect on root dentin remineralization, and incubation with NaF dissolved in artificial saliva demonstrated a stronger effect.

  9. Spectrophotometric determination of fluoride with alizarin complexone

    Energy Technology Data Exchange (ETDEWEB)

    Marczenko, Z; Lenarczyk, L [Politechnika Warszawska (Poland)

    1976-01-01

    The modification of direct spectrophotometric method of fluoride determination by alizarin complexone has been developed. It was shown that the lanthanum alizarin complexone chelate is more convenient than that of cerium (3). The influence of acetone, dioxane and dimethyl sulphoxide in water solution on the increase of sensitivity of the method and the rate of colour reaction has been determined. The optimal pH ranges for the reaction with lanthanum and cerium (3) have been estimated. Some amines having a large molecule are useful for extraction of blue fluoride complex with isobutanol. Dioctylamine was applied in a new extraction spectrophotometric procedure of fluoride determination. Conditions in reagent have been established. Both variants of the method have been applied to the fluoride determination in several chemicals. The obtained results show a good precision and accuracy.

  10. HOUSEHOLD PURIFICATION OF FLUORIDE CONTAMINATED MAGADI (TRONA)

    DEFF Research Database (Denmark)

    Nielsen, Joan Maj; Dahi, Elian

    1997-01-01

    Purification of fluoride contaminated magadi is studied using bone char sorption and calcium precipitation. The bone char treatment is found to be workable both in columns and in batches where the magadi is dissolved in water prior to treatment. The concentrations in the solutions were 89 g magadi....../L and 95 and 400 mg F/L respectively in natural and synthetic solutions. The fluoride removal capacities observed were 4.6 mg F/g bone char for the column system and 2.7 mg F/g bone char for the batch system in case of synthetic magadi solution. It is however concluded that the batch system is the best...... treatment method. A procedure for purification of fluoride contaminated magadi at household level is described....

  11. Effect of fluoride pretreatment on the solubility of synthetic carbonated apatite.

    Science.gov (United States)

    Barry, A B; Zhuang, H; Baig, A A; Higuchi, W I

    2003-03-01

    The purpose of this research was to address the following question: How is the solubility of fluoride-pretreated carbonated apatite (CAP) in aqueous acidic media related to the equilibrium solution fluoride and/or the CAP adsorbed fluoride levels? A CAP sample prepared by a precipitation method at 70 degrees C containing approximately 6% carbonate was fluoride-treated (F adsorption from neutral aqueous solutions) to yield a approximately 1000 ppm F CAP and a approximately 3300 ppm F CAP. Metastable equilibrium solubility distributions were determined in acetate buffers at pH 5.0. Solution fluoride, calcium, phosphate, and pH were determined from the equilibrated solutions. The equilibrium solution fluoride levels were extremely low, e.g., as low as approximately 0.10 ppb to approximately 0.30 ppb at 50% dissolved for the two CAP preparations. The approximately 3300 ppm F CAP yielded a lower solubility than the approximately 1000 ppm F CAP (shift in the mean pKHAP value of 1.5-2 units). This can be attributed to the lower solution F(-) for the sample containing approximately 1000 ppm fluoride compared with the approximately 3300 ppm fluoride-containing CAP. These important findings suggest that a fluoride treatment simply may provide an adsorption fluoride depot for subsequent release, providing a solution fluoride effect upon the CAP solubility and not necessarily any intrinsic alteration of the mineral solubility.

  12. Effect of fluoride addition on the properties of dental alginate impression materials.

    Science.gov (United States)

    Lee, Yong-Keun; Lim, Bum-Soon; Kim, Cheol-We

    2004-03-01

    Fluoride-containing dental alginate impression materials can exert a considerable reduction in enamel solubility. The objective was to evaluate the effects of fluoride addition in the alginate impression materials on the properties and subsequent release of fluoride. Four experimental alginate impression materials were studied. Materials were mixed with distilled water (control) or 100-ppm fluoride solution. One or two percent NaF, or 1% SnF2 was added to the materials, which were mixed with distilled water. Fluoride release, flexibility, recovery from deformation, setting time, compressive strength and elastic modulus were determined in accordance with the ISO 1563 and ANSI/ADA Spec. 18. Fluoride release increased after addition of fluoride, and the released amount was 0.762-14.761 ppm. Addition of NaF or SnF2 resulted in higher fluoride release than the control group (p alginate impression material may result in effective release of fluoride without deteriorating the properties of material itself.

  13. Fluoride and Oral Health.

    Science.gov (United States)

    O'Mullane, D M; Baez, R J; Jones, S; Lennon, M A; Petersen, P E; Rugg-Gunn, A J; Whelton, H; Whitford, G M

    2016-06-01

    The discovery during the first half of the 20th century of the link between natural fluoride, adjusted fluoride levels in drinking water and reduced dental caries prevalence proved to be a stimulus for worldwide on-going research into the role of fluoride in improving oral health. Epidemiological studies of fluoridation programmes have confirmed their safety and their effectiveness in controlling dental caries. Major advances in our knowledge of how fluoride impacts the caries process have led to the development, assessment of effectiveness and promotion of other fluoride vehicles including salt, milk, tablets, toothpaste, gels and varnishes. In 1993, the World Health Organization convened an Expert Committee to provide authoritative information on the role of fluorides in the promotion of oral health throughout the world (WHO TRS 846, 1994). This present publication is a revision of the original 1994 document, again using the expertise of researchers from the extensive fields of knowledge required to successfully implement complex interventions such as the use of fluorides to improve dental and oral health. Financial support for research into the development of these new fluoride strategies has come from many sources including government health departments as well as international and national grant agencies. In addition, the unique role which industry has played in the development, formulation, assessment of effectiveness and promotion of the various fluoride vehicles and strategies is noteworthy. This updated version of 'Fluoride and Oral Health' has adopted an evidence-based approach to its commentary on the different fluoride vehicles and strategies and also to its recommendations. In this regard, full account is taken of the many recent systematic reviews published in peer reviewed literature.

  14. Private Well Water and Fluoride

    Science.gov (United States)

    ... Private Wells Infant Formula Fluorosis Public Health Service Recommendation Water Operators & Engineers Water Fluoridation Additives Shortages of Fluoridation Additives Drinking Water Pipe Systems CDC-Sponsored Water Fluoridation Training Links to Other ...

  15. Equilibrium Studies of Fluoride Adsorption onto a Ferric Poly ...

    African Journals Online (AJOL)

    African countries along the Great Rift Valley are among areas of the world where excess fluoride in water sources is a major public health problem. In this work, the removal of fluoride (F) from water solutions using a ferric poly-mineral (FPM) from Kenya was therefore studied using batch adsorption experiments. The effect of ...

  16. Sulfochlorphenol S as reagent for direct photometric determination of fluorides

    International Nuclear Information System (INIS)

    Dzhashi, D.O.; Dedkova, V.P.; Savvin, S.B.

    1978-01-01

    The system of zirconium-sulfochlorphenol S-fluoride was studied by the spectrophotometry method. The effect of pH, temperature and time on the formation of zirconium complexes with sulfochlorphenol S was investigated. A comparison of the above method of determining fluorides with other methods (using alizarinecomplexonate, quinalizarincomplexonate, cerium chelates, lanthanum, arsenazo 3) is presented. The sensitivity of determining fluorides with arsenazo 3 is lower than that with sulfochlorphenol S. The molar absorption coefficient is 3x10 4 , the reaction of determining fluorides with the aid of sulfochlorphenol S is highly selective. The method was used to determine fluorides in the supply water, zirconium solutions and electrolyzer cell. The range of concentration determination for fluorides is 0-3 μg/25 ml

  17. Neutron diffraction radiation of solid solution of carbon and hydrogen in the α-titanium in the homogeneity domain

    International Nuclear Information System (INIS)

    Mirzaev, B.B.; Khidirov, I.; Mukhtarova, N.N.

    2005-01-01

    In the work by the neutron-graph the homogeneity domain of the introduction solid solution TiC x H y is determined. The sample neutron grams have been taken on the neutron diffractometer (λ=.1085 nm) installed at the thermal column of the WWR-SM reactor (INF AN RUz). For the phase analysis and estimation of solid solutions homogeneity the X-ray graph was used. X-ray grams were taken on the X-ray diffractometer DRON-3M with use of CuK α radiation (λ=0.015418 nm)

  18. Automatic photometric titration of fluoride with thorium nitrate and alizarin S as indicator

    International Nuclear Information System (INIS)

    Bliefert, C.; Sobek, M.

    1978-01-01

    The photometric titration of fluoride with thorium nitrate and Alizarin S as indicator has been automated and optimized for fluoride levels between 1 and 20mg/85ml solution. The interference of several ions has been investigated. This procedure is particularly useful for the determination of fluoride after fusion with peroxides as fluxing agents. (orig.) [de

  19. Determination of the stability constants of a number of metal fluoride complexes and their rates of formation

    International Nuclear Information System (INIS)

    Hammer, R.R.

    1979-08-01

    The stability constants of the fluoride complexes of Al +3 , H 3 BO 3 , Cr +3 , Cr +6 , Fe +3 , Gd +3 , Nb +5 , UO 2 +2 , and Zr +4 were determined in 0.96 and 2.88 M HNO 3 solutions in the temperature range 25 to 60 0 C with a fluoride specific ion electrode. These data can be used to calculate the concentration of chemical species in solution and will be used to correlate solution properties with solution composition. The solubilities of some fluoride precipitates were also measured in nitric acid solutions. The rates of formation of the fluoborates, aluminum fluoride, and zirconium fluoride complexes were measured with a fluoride specific ion electrode at 25, 35, and 45 0 C. The rates of formation of all complexes, except BF 4 - , AlF +2 , and a fluoride complex with aluminum containing more than three fluorides associated with it, were too fast to measure with the instrumentation used

  20. Microstructure and mechanical properties of a novel Ti–Al–Cr–Fe titanium alloy after solution treatment

    International Nuclear Information System (INIS)

    Wang, Zhenguo; Cai, Haijiao; Hui, Songxiao

    2015-01-01

    Highlights: • Microstructure and mechanical properties of a novel Ti–3.0Al–3.7Cr–2.0Fe alloy were studied. • The effects of cooling rates and solution temperature were considered. • The strength–ductility combination were investigated through different heat treatment. - Abstract: The relationship between microstructure and mechanical properties of a novel Ti–3.0Al–3.7Cr–2.0Fe alloy were studied. The effects of cooling rates and solution temperature were considered. The analysis methods of optical microscope (OM), X-ray diffractometer (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM) were used. The results indicate that β and α phase in this alloy are obtained after solution treated at 1183 K on the cooling ways of air cooling and furnace cooling; and β and α″ martensite are observed after quenching in water. Besides, the volume of α phase is decreased with increasing solution temperature. In the present study, the ultimate strength 1065 MPa with 12.0% in elongation of the alloy is acquired under the heat treatment condition of 1183 K/30 min/AC, and the strength–ductility combination in this case is also the best. Under the heat treatment condition of 1183 K/30 min/WQ, the elasticity modulus of the alloy is only 91.3 GPa, as a result of the lower elasticity modulus of β phase

  1. Electrodeposition of niobium and titanium in molten salts

    International Nuclear Information System (INIS)

    Sartori, A.F.; Chagas, H.C.

    1988-01-01

    The electrodeposition of niobium and titanium in molten fluorides from the additions of fluorine niobates and fluorine titanates of potassium is described in laboratory and pilot scale. The temperature influence, the current density and the time deposition over the current efficiency, the deposits structure and the deposits purity are studied. The conditions for niobium coating over copper and carbon steel and for titanium coating over carbon steel are also presented. (C.G.C.) [pt

  2. Fluoride removal from water by nano filtration

    International Nuclear Information System (INIS)

    Bejaoui, Imen; Mnif, Amine; Hamrouni, Bechir

    2009-01-01

    As any oligo element, fluoride is necessary and beneficial for human health to low concentrations, but an excess amount of fluoride ions in drinking water has been known to cause undesirable effects, especially tooth and bones fluoro sis. The maximum acceptable concentration of fluoride in drinking water was fixed by the World Health Organization according to the climate in the range of 1 mg.L -1 to 1,2 mg.L -1 . Many methods have been used to remove fluoride from water such as precipitation, adsorption, electrocoagulation and membrane processes. Technologies using membrane processes are being used in many applications, particularly for brackish water desalination. Nano filtration seems to be the best process for a good selective defluorination of fluorinated waters. The main objective of this work was to investigate the retention of fluoride anions by nano filtration. The first part of this study deals with the characterisation of the NF HL2514TF membrane. The influence of various experimental parameters such as initial fluoride content, feed pressure, permeate flux, ionic strength, type of cation associated to fluoride and pH were studied in the second part. Results show that the retention order for the salts tested was TR(Na 2 SO 4 ) > TR(CaCl 2 ) > TR(NaCl), showing a retention sequence inversely proportional to the salt diffusion coefficients in water. It was also shown that charge effects could not be neglected, and a titration experiments confirmed that the NF membrane carry a surplus of negatively charged groups. Fluoride retention exceeds 60 pour cent, and increases with increasing concentration, where the rejection mechanism is related to the dielectric effects. Speigler-Kedem model was applied to experimental results in the aim to determine phenomenological parametersσand P s respectively, the reflexion coefficient of the membrane and the solute permeability of ions. The convective and diffusive parts of the mass transfer were quantified with

  3. Studies of the hydrous titanium oxide ion exchanger. 4. Rate of the isotopic exchange of sodium ions between the exchanger in the Na+ form and aqueous solution

    International Nuclear Information System (INIS)

    Inoue, Yasushi; Yamazaki, Hiromichi; Kasuga, Fuminori

    1995-01-01

    The isotopic exchange rate of Na + between hydrous titanium(IV) oxides, precipitated at pH 6 and 13, in the Na + form and aqueous solution of sodium salt was determined radiochemically. The rate in the exchanger precipitated at pH 6 is controlled by the diffusion of Na + in the exchanger particles (particle diffusion). The diffusion coefficient and its activation energy are 1.9 x 10 -11 m 2 s -1 (pH 12, 5.0degC) and 29 kJ mol -1 (pH 12), respectively. The rate in the exchanger precipitated at pH 13 is also controlled by the particle diffusion. The rate is much slower than that in the other; this can be explained by assuming the existence of two kinds of independently diffusing ions (fast and slow species) in the exchanger. The diffusion coefficients are of the order of 10 -12 and 10 -13 m 2 s -1 for the fast and the slow species, respectively. Their activation energies are 48-60 kJ mol -1 at pH 12. The marked difference in kinetics between two exchanges was interpreted in terms of the difference in the acid-base property and in the microstructure of the matrix. (author)

  4. Effect of fluoridated varnish and silver diamine fluoride solution on enamel demineralization: pH-cycling study Efeito do verniz fluoretado e da solução de diamino fluoreto de prata na desmineralização do esmalte: estudo utilizando modelo de ciclagem de pH

    Directory of Open Access Journals (Sweden)

    Alberto Carlos Botazzo Delbem

    2006-04-01

    Full Text Available OBJECTIVE: In the present investigation, the anticariogenic effect of fluoride released by two products commonly applied in infants was evaluated. METHODS: Bovine sound enamel blocks were randomly allocated to each one of the treatment groups: control (C, varnish (V and diamine silver fluoride solution (D. The blocks were submitted to pH cycles in an oven at 37ºC. Next, surface and cross-sectional microhardness were assessed to calculate the percentage loss of surface microhardness (%SML and the mineral loss (deltaZ. The fluoride present in enamel was also determined. RESULTS: F/Px10-3 (ANOVA, pOBJETIVOS: Este trabalho avaliou o efeito anticariogênico do flúor liberado por dois produtos comumente aplicados em crianças. MÉTODOS: Para isto, utilizaram-se blocos de esmalte de dentes bovinos distribuídos aleatoriamente em três grupos de tratamento: controle (C, verniz fluoretado (V e solução de diamino fluoreto de prata (D. Os blocos foram submetidos à ciclagem de pH a 37ºC. Após, realizou-se o teste de microdureza de superfície (para o cálculo da % da perda de microdureza de superfície - %SML e em secção longitudinal do esmalte (% de alteração da área mineral - %deltaZ e a determinação do flúor presente no esmalte (F/P x 10-3. RESULTADOS: As concentrações de flúor (ANOVA, p<0,05 na 1ª camada do esmalte, antes da ciclagem de pH, foram (C, V e D: 1,6ª; 21,6b e 4,0c. Os resultados de %SML (Kruskal-Wallis, p<0.05 foram: -64,0ª, -45,2b e -53,1c. Os valores de %deltaZ (ANOVA, p<0.05 foram: -18,7ª, -7,7b e -17,3ª. CONCLUSÃO: Os dados sugerem que o flúor liberado pelo verniz apresentou maior interação com o esmalte promovendo menor perda mineral quando comparado à solução de diamino de prata.

  5. Fluoride Rinses, Gels and Foams

    DEFF Research Database (Denmark)

    Twetman, Svante; Keller, Mette K

    2016-01-01

    AIM: The aim of this conference paper was to systematically review the quality of evidence and summarize the findings of clinical trials published after 2002 using fluoride mouth rinses, fluoride gels or foams for the prevention of dental caries. METHODS: Relevant papers were selected after...... (6 on fluoride mouth rinse, 10 on fluoride gel and 3 on fluoride foam); 6 had a low risk of bias while 2 had a moderate risk. All fluoride measures appeared to be beneficial in preventing crown caries and reversing root caries, but the quality of evidence was graded as low for fluoride mouth rinse......, moderate for fluoride gel and very low for acidulated fluoride foam. No conclusions could be drawn on the cost-effectiveness. CONCLUSIONS: This review, covering the recent decade, has further substantiated the evidence for a caries-preventive effect of fluoride mouth rinse, fluoride gel and foam...

  6. Determination of fluoride in drainage by ion electrode method

    International Nuclear Information System (INIS)

    Terakado, Shigeru; Ochiai, Ken-ichi; Motoyama, Shigeji; Tsutsumi, Ken-ichi

    1975-01-01

    The fluoride ion selective electrode method for rapidly and precisely determining fluoride in drainage was studied. This method enables the analysis of the samples with fluoride concentration above 0.1 mg/l in about five minutes. Six buffer solutions were selected to compare the masking effect against aluminum. Solution A is TISAB made by dissolving 57 ml of gracial acetic acid and 10 g of sodium chloride in 500 ml of water, thereafter adjusting pH to 5.5 and diluting to 1 liter with water. Solution B is phosphoric acid solution (17 M/L). Solution C is 3 M ammonium phosphate dibasic aqueous solution. Solution D is 1 M sodium citrate aqueous solution adjusted to pH 6 with hydrochloric acid. Solution E is 0.5 M sodium phosphate dibasic aqueous solution. Solution F is 2 M ammonium phosphate monobasic aqueous solution. As a result of studying the effect of coexisting elements, the buffer solutions A,B,E and F were greatly influenced by the coexistence of aluminum, while C and D show remarkable masking effect against aluminum. The amount of interfering ions in normal drainage is so small that no problem is anticipated for D. When fluoride recovery treatment is performed, it is important in dilution measurement to confirm whether the measured values are accurate or not, because there are high and low concentrations of fluoride at the same potential. (Iwakiri, K.)

  7. Mapping the surface (hydr)oxo-groups of titanium oxide and its interface with an aqueous solution: the state of the art and a new approach.

    Science.gov (United States)

    Panagiotou, George D; Petsi, Theano; Bourikas, Kyriakos; Garoufalis, Christos S; Tsevis, Athanassios; Spanos, Nikos; Kordulis, Christos; Lycourghiotis, Alexis

    2008-10-01

    In this article the "titanium oxide/electrolyte solution" interface is studied by taking in advantage the recent developments in the field of Surface and Interface Chemistry relevant to this oxide. Ab-initio calculations were performed in the frame of the DFT theory for estimating the charge of the titanium and oxygen atoms exposed on the anatase (1 0 1), (1 0 0), (0 0 1), (1 0 3)(f) and rutile (1 1 0) crystal faces. These orientations have smaller surface energy with respect to other ones and thus it is more probable to be the real terminations of the anatase and rutile nanocrystallites in the titania polycrystalline powders. Potentiometric titrations for obtaining "fine structured" titration curves as well as microelectrophoresis and streaming potential measurements have been performed. On the basis of ab-initio calculations, and taking into account the relative contribution of each crystal face to the whole surface of the nanocrystals involved in the titania aggregates of a suspension, the three most probable surface ionization models have been derived. These models and the Music model are then tested in conjunction with the "Stern-Gouy-Chapman" and "Basic Stern" electrostatic models. The finally selected surface ionization model (model A) in combination with each one of the two electrostatic models describes very well the protonation/deprotonation behavior of titania. The description is also very good if this model is combined with the Three Plane (TP) model. The application of the "A/(TP)" model allowed mapping the surface (hydr)oxo-groups [TiO(H) and Ti(2)O(H)] of titania exposed in aqueous solutions. At pH>pzc almost all terminal oxygens [TiO] are non-protonated whereas even at low pH values the non-protonated terminal oxygens predominate. The acid-base behavior of the bridging oxygens [Ti(2)O] is different. Thus, even at pH=10 the greater portion of them is protonated. The application of the "A/TP" model in conjunction with potentiometric titrations

  8. Study of the heat conductivity of double and triple disordered solid solutions in the titanium-zirconium-hafnium system

    Energy Technology Data Exchange (ETDEWEB)

    Zarichnyak, Yu.P.; Lisnenko, T.A.

    1977-10-01

    Measurements are presented of the heat physical properties of trinary alloys in the system Ti-Zr-Hf. The possibility is shown of summarizing the results of the measurement and prediction of the heat conductivity of trinary continuous disordered solid solutions. Comparison of calculated results with experimental data shows that the method of modeling of the structure and prediction of heat conductivity suggested yields good qualitative and quantitative agreement throughout the entire range of change of concentration of the components. The maximum disagreement between calculated and experimental results is about 10%. 8 references, 2 figures, 1 table.

  9. Determination of the total nitrate content of thorium nitrate solution with a selective electrode

    International Nuclear Information System (INIS)

    Wirkner, F.M.

    1979-01-01

    The nitrate content of thorium nitrate solutions is determined with a liquid membrane nitrate selective electrode utilizing the known addition method in 0.1 M potassium fluoride medium as ionic strength adjustor. It is studied the influence of pH and the presence of chloride, sulphate, phosphate, meta-silicate, thorium, rare earths, iron, titanium, uranium and zirconium at the same concentrations as for the aqueous feed solutions in the thorium purification process. The method is tested in synthetic samples and in samples proceeding from nitric dissolutions of thorium hidroxide and thorium oxicarbonate utilized as thorium concentrates to be purified [pt

  10. A fundamental approach to adhesion: Synthesis, surface analysis, thermodynamics and mechanics. [acid-base properties of titanium 6-4 surfaces

    Science.gov (United States)

    Siriwardane, R.; Wightman, J. P.

    1980-01-01

    The acid-base properties of titanium 6-4 plates (low surface area) were investigated after three different pretreatments, namely Turco, phosphate-fluoride and Pasa-Jell. A series of indicators was used and color changes were detected using diffuse reflectance visible spectroscopy. Electron spectroscopy for chemical analysis was used to examine the indicator on the Ti 6-4 surface. Specular reflectance infra-red spectroscopy was used to study the adsorption of stearic acid from cyclohexane solutions on the Ti 6-4 surface.

  11. Fluoride varnishes and enamel caries

    NARCIS (Netherlands)

    Bruyn, Hugo de

    1987-01-01

    Topical fluoride applications have the aim of increasing the fluoride uptake in enamel and consequently reducing caries. In the early ‘60s fluoride varnishes were introduced because they had a long contact period with the enamel which resulted in a higher fluoride uptake than from other topical

  12. Antibacterial Effect of Silver Diamine Fluoride on Cariogenic Organisms.

    Science.gov (United States)

    Lou, Yali; Darvell, Brain W; Botelho, Michael G

    2018-05-01

    To screen the possible antimicrobial activity of a range of clinically used, silver-based compounds on cariogenic organisms: silver diamine fluoride (SDF), silver fluoride, and silver nitrate. Preliminary screening disk-diffusion susceptibility tests were conducted on Mueller-Hinton agar plates inoculated with Streptococcus mutans, Lactobacillus acidophilus, and Actinomyces naeslundii, organisms known to be cariogenic. In order to identify which component of the silver compounds was responsible for any antibacterial (AB) effect, and to provide controls, the following were also investigated at high and low concentrations: sodium fluoride, ammonium fluoride, ammonium chloride, sodium fluoride, sodium chloride, and sodium nitrate, as well as deionized water as control. A volume of 10 pL of a test solution was dispensed onto a paper disk resting on the inoculated agar surface, and the plate incubated anaerobically at 37°C for 48 hours. The zones of inhibition were then measured. Silver diamine fluoride, silver fluoride, silver nitrate, and ammonium fluoride had significant AB effect (p effect at low concentration; the remaining other compounds had no effect. Silver ions appear to be the principal AB agent at both high and low concentration; fluoride ions only have an AB effect at high concentration, while ammonium, nitrate, chloride and sodium ions have none. The anticaries effect of topical silver solutions appears restricted to that of the silver ions. Silver compounds, such as SDF, silver fluoride, and silver nitrate have AB effect against cariogenic organisms and these may have clinical impact in arresting or preventing dental decay. Sodium fluoride did not have AB effect under the conditions tested.

  13. Study of fluoride in polluted and unpolluted estuarine environments

    Digital Repository Service at National Institute of Oceanography (India)

    Zingde, M.D.; Mandalia, A.V.

    estuary, significant deviation from the theoretical dilution line (TDL) in the chlorinity range 0.5-8ppt was observed in Mindhola River estuary due to the externally added fluoride which largely remained in solution. The excess of fluroide over...

  14. Niobium electrodeposition from molten fluorides

    International Nuclear Information System (INIS)

    Sartori, A.F.

    1987-01-01

    Niobium electrodeposition from molten alkali fluorides has been studied aiming the application of this technic to the processes of electrorefining and galvanotechnic of this metal. The effects of current density, temperature, niobium concentration in the bath, electrolysis time, substrate nature, ratio between anodic and cathodic areas, electrodes separation and the purity of anodes were investigated in relation to the cathodic current efficiency, electrorefining, electroplating and properties of the deposit and the electrolytic solution. The work also gives the results of the conctruction and operation of a pilot plant for refractory metals electrodeposition and shows the electrorefining and electroplating compared to those obtained at the laboratory scale. (author) [pt

  15. Amorphous and nanocrystalline titanium nitride and carbonitride materials obtained by solution phase ammonolysis of Ti(NMe2)4

    International Nuclear Information System (INIS)

    Jackson, Andrew W.; Shebanova, Olga; Hector, Andrew L.; McMillan, Paul F.

    2006-01-01

    Solution phase reactions between tetrakisdimethylamidotitanium (Ti(NMe 2 ) 4 ) and ammonia yield precipitates with composition TiC 0.5 N 1.1 H 2.3 . Thermogravimetric analysis (TGA) indicates that decomposition of these precursor materials proceeds in two steps to yield rocksalt-structured TiN or Ti(C,N), depending upon the gas atmosphere. Heating to above 700 deg. C in NH 3 yields nearly stoichiometric TiN. However, heating in N 2 atmosphere leads to isostructural carbonitrides, approximately TiC 0.2 N 0.8 in composition. The particle sizes of these materials range between 4-12 nm. Heating to a temperature that corresponds to the intermediate plateau in the TGA curve (450 deg. C) results in a black powder that is X-ray amorphous and is electrically conducting. The bulk chemical composition of this material is found to be TiC 0.22 N 1.01 H 0.07 , or Ti 3 (C 0.17 N 0.78 H 0.05 ) 3.96 , close to Ti 3 (C,N) 4 . Previous workers have suggested that the intermediate compound was an amorphous form of Ti 3 N 4 . TEM investigation of the material indicates the presence of nanocrystalline regions x (C,N) y crystalline phases

  16. The cariostatic mechanisms of fluoride

    OpenAIRE

    Kata Rošin-Grget; Kristina Peroš; Ivana Šutej; Krešimir Bašić

    2013-01-01

    This article discusses the possible cariostatic mechanisms of the action of fluoride. In the past, fluoride inhibition of caries was ascribed to reduced solubility of enamel due to incorporation of fluoride (F–) into the enamel minerals. The present evidence from clinical and laboratory studies suggests that the caries-preventive mode of action of fluoride is mainly topical. There is convincing evidence that fluoride has a major effect on demineralisation and remineralisation of dental hard t...

  17. Magnetic interactions through fluoride

    DEFF Research Database (Denmark)

    Pedersen, Kasper Steen; Sigrist, Marc; Weihe, Høgni

    2014-01-01

    support the parameter values and resolve |E| ≈ 0.04 cm(-1). The exchange coupling constant (J) is 1 order of magnitude smaller than that found in comparable systems with linear oxide bridging but comparable to typical magnitudes through cyanide, thus underlining the potential of fluoride complexes......The nature of the magnetic interaction through fluoride in a simple, dinuclear manganese(III) complex (1), bridged by a single fluoride ion in a perfectly linear fashion, is established by experiment and density functional theory. The magnitude of the antiferromagnetic exchange interaction...

  18. An In-vitro Study of the Load Deflection Characteristics of the Thermal Wires Immersed in Different Fluoride Prophylactic Agents

    Directory of Open Access Journals (Sweden)

    Sami K. Al-Joubori

    2018-04-01

    Full Text Available Background: Fluoridated prophylactic agents have been reported to cause corrosion and discoloration of titanium alloys. Degradation in the mechanical properties lead to a decrease in a suitable orthodontic force, thereby causing delayed leveling of crooked teeth. This study was designed to evaluate the load deflection characteristics of thermal nickel titanium arch wires during unloading phase after ninety minutes immersion in three different fluoride agents. Material and methods: Forty specimens of thermal wires were obtained from Ortho Technology Company, which had 0.019” × 0.025” rectangular in cross section. Ten specimens from the wire size were immersed in one of the tested fluoride prophylactic agents (neutral sodium fluoride gel, stannous fluoride gel or Phos-Flur® mouth rinse or in the controlled medium of normal saline and incubated at 37°C for ninety minutes. A Wp 300 universal material testing machine was modified and used to perform a three-point bending test in a water path at 37 ± 1°C. The statistical difference between the different agents was analyzed using ANOVA and least significant difference tests. Results: The unloading forces at 0.5 mm, 1.0 mm, and 1.5 mm where significantly reduced especially in acidulated phosphate fluoride treated specimens followed by neutral fluoride treated specimens. Conclusion: Based on the results found in this study it can be preferred to use fluoride prophylactic agents with the least acidity and fluoride ions concentration.

  19. Study of the Changes in Composition of Ammonium Diuranate with Progress of Precipitation, and Study of the Properties of Ammonium Diuranate and its Subsequent Products Produced from both Uranyl Nitrate and Uranyl Fluoride Solutions

    Directory of Open Access Journals (Sweden)

    Subhankar Manna

    2017-04-01

    Full Text Available Uranium metal used for fabrication of fuel for research reactors in India is generally produced by magnesio-thermic reduction of UF4. Performance of magnesio-thermic reaction and recovery and quality of uranium largely depends on properties of UF4. As ammonium diuranate (ADU is first product in powder form in the process flow-sheet, properties of UF4 depend on properties of ADU. ADU is generally produced from uranyl nitrate solution (UNS for natural uranium metal production and from uranyl fluoride solution (UFS for low enriched uranium metal production. In present paper, ADU has been produced via both the routes. Variation of uranium recovery and crystal structure and composition of ADU with progress in precipitation reaction has been studied with special attention on first appearance of the precipitate Further, ADU produced by two routes have been calcined to UO3, then reduced to UO2 and hydroflorinated to UF4. Effect of two different process routes of ADU precipitation on the characteristics of ADU, UO3, UO2 and UF4 were studied here.

  20. Study of the changes in composition of ammonium diuranate with progress of precipitation, and study of the properties of ammonium diuranate and its subsequent products produced from both uranyl nitrate and uranyl fluoride solutions

    Energy Technology Data Exchange (ETDEWEB)

    Manna, Subhankar; Kumar, Raj; Satpati, Santosh K.; Roy, Saswati B. [Bhabha Atomic Research Centre, Trombay, Mumbai (India); Joshi, Jyeshtharaj B. [Dept. of Chemical Engineering, Institute of Chemical Technology, Mumbai (India)

    2017-04-15

    Uranium metal used for fabrication of fuel for research reactors in India is generally produced by magnesio-thermic reduction of UF{sub 4}. Performance of magnesio-thermic reaction and recovery and quality of uranium largely depends on properties of UF{sub 4}. As ammonium diuranate (ADU) is first product in powder form in the process flow-sheet, properties of UF{sub 4} depend on properties of ADU. ADU is generally produced from uranyl nitrate solution (UNS) for natural uranium metal production and from uranyl fluoride solution (UFS) for low enriched uranium metal production. In present paper, ADU has been produced via both the routes. Variation of uranium recovery and crystal structure and composition of ADU with progress in precipitation reaction has been studied with special attention on first appearance of the precipitate Further, ADU produced by two routes have been calcined to UO{sub 3}, then reduced to UO{sub 2} and hydroflorinated to UF{sub 4}. Effect of two different process routes of ADU precipitation on the characteristics of ADU, UO{sub 3}, UO{sub 2} and UF{sub 4} were studied here.

  1. Study of the changes in composition of ammonium diuranate with progress of precipitation, and study of the properties of ammonium diuranate and its subsequent products produced from both uranyl nitrate and uranyl fluoride solutions

    International Nuclear Information System (INIS)

    Manna, Subhankar; Kumar, Raj; Satpati, Santosh K.; Roy, Saswati B.; Joshi, Jyeshtharaj B.

    2017-01-01

    Uranium metal used for fabrication of fuel for research reactors in India is generally produced by magnesio-thermic reduction of UF 4 . Performance of magnesio-thermic reaction and recovery and quality of uranium largely depends on properties of UF 4 . As ammonium diuranate (ADU) is first product in powder form in the process flow-sheet, properties of UF 4 depend on properties of ADU. ADU is generally produced from uranyl nitrate solution (UNS) for natural uranium metal production and from uranyl fluoride solution (UFS) for low enriched uranium metal production. In present paper, ADU has been produced via both the routes. Variation of uranium recovery and crystal structure and composition of ADU with progress in precipitation reaction has been studied with special attention on first appearance of the precipitate Further, ADU produced by two routes have been calcined to UO 3 , then reduced to UO 2 and hydroflorinated to UF 4 . Effect of two different process routes of ADU precipitation on the characteristics of ADU, UO 3 , UO 2 and UF 4 were studied here

  2. Comparative evaluation of fluoride release and recharge of pre-reacted glass ionomer composite and nano-ionomeric glass ionomer with daily fluoride exposure: An in vitro study

    Directory of Open Access Journals (Sweden)

    Jayanthi Mungara

    2013-01-01

    Full Text Available Aim: This in vitro study was designed to investigate the effects of daily fluoride exposures on fluoride release and recharge by prereacted glass ionomer (PRG composite and nano-ionomeric glass ionomer. Materials and Methods: Seventy-two specimens (36 of each material were prepared and by placing the restorative materials into Teflon mold. Each specimen was subjected to one of three daily treatments (n = 12: (1 No fluoride treatment (control; (2 application of a fluoride dentifrice (1,000 ppm once daily; and (3 the same regimen as (2, plus immersion in a 0.05% sodium fluoride (NaF mouth rinse (225 ppm immediately following the dentifrice application. Specimens were suspended in a storage vial containing 10 ml demineralizing solution for 6 h and transferred to a new test tube containing 10 ml remineralizing solution for 18 h. Fluoride treatments of the specimens were completed every day prior to their immersion in the demineralizing solution. Media solutions were buffered with equal volumes of total ionic strength adjustment buffer (TISAB II; fluoride levels were measured using a digital ion analyzer and fluoride electrode throughout the 21 day duration of the experiment. Results: Nano-ionomeric glass ionomer showed a better amount of fluoride release than PRG composite irrespective of the fluoride treatment supplementation (P < 0.01. Additional fluoride supplementation improved fluoride release and recharge ability for both the materials when compared to their respective control groups. The fluoride recharge for both materials did not show any sustained pattern of release. Conclusion: Nano-ionomeric glass ionomer demonstrated a greater ability to release and recharge compared with that of PRG composite.

  3. Preparation of bromine fluoride

    International Nuclear Information System (INIS)

    Domange, Pr; Duflo, J.

    1958-05-01

    This note addresses the preparation of bromine fluoride. It indicates the implemented process for the reaction, used products (fluorine and bromine), and column characteristics. It describes the operating mode. Apparatus drawing is provided

  4. Solubility and fluoride release in ionomers and compomers.

    Science.gov (United States)

    Bertacchini, S M; Abate, P F; Blank, A; Baglieto, M F; Macchi, R L

    1999-03-01

    The degree of solubility and the fluoride release of glass-ionomer cements and "compomers" were determined as a function of time. Three conventional glass-ionomer cements, three hybrid ionomers, and two compomers were included in the study. Disk-shaped specimens were prepared and immersed in a lactic acid solution. Solubility was evaluated from determinations of loss of mass as a function of time. To evaluate fluoride release, similar specimens were immersed in 50 mL of deionized water to which 50 mL of buffer solution was added. A fluoride ion detector was used to read the concentration of fluoride ion in the overall solution at different times after immersion. Material and time factors had a significant influence on results. The compomers showed less corrosion and fluoride release than the ionomers. Some correlation was found between solubility and fluoride leakage values. Components of both the ionomers and compomers that were studied can dissolve in water. The materials leak fluoride ions in amounts that differ according to the characteristics of the individual products.

  5. Titanium by design: TRIP titanium alloy

    Science.gov (United States)

    Tran, Jamie

    elements in titanium to model the effect of alloying elements on the Ms temperature in titanium. Available atomic volume data and collaborative first principles quantum mechanical calculations are combined to model the composition dependence of the transformation molar volume change. Composition analysis of the beta phase from the LEAP and Bolling-Richman experimental measurement of the M ssigma temperature defining mechanical transformation stability of the beta phase in Ti5111 provided a calibration of transformation models. Using the near-alpha Ti5111 alloy as a reference alloy, the feasibility was assessed for application of transformation toughening to maintain the high toughness of Ti5111 at the higher 120ksi (827MPa) yield strength of Ti-6Al-4V. Combined with models of solution and grain refinement strengthening, a modification of the Ti5111 composition was designed meeting the transformation stability requirement while increasing the calculated transformation volume change by 10% for efficient toughening. A design prototype was created and mechanically tested resulting in a room temperature yield strength of >120ksi and M ssigma(ut) at room temperature confirming strength and transformation stability predictions.

  6. Growth of anatase titanium dioxide nanotubes via anodization

    Directory of Open Access Journals (Sweden)

    Ed Adrian Dilla

    2012-06-01

    Full Text Available In this work, titanium dioxide nanotubes were grown via anodization of sputtered titanium thin films using different anodization parameters in order to formulate a method of producing long anatase titanium dioxide nanotubes intended for solar cell applications. The morphological features of the nanotubes grown via anodization were explored using a Philips XL30 Field Emission Scanning Electron Microscope. Furthermore, the grown nanotubes were also subjected to X-ray diffraction and Raman spectroscopy in order to investigate the effect of the predominant crystal orientation of the parent titanium thin film on the crystal phase of the nanotubes. After optimizing the anodization parameters, nanotubes with anatase TiO2 crystal phase and tube length more than 2 microns was produced from parent titanium thin films with predominant Ti(010 crystal orientation and using ammonium fluoride in ethylene glycol as an electrolyte with a working voltage equal to 60V during 1-hour anodization runs.

  7. Effects of Fluoride on NiTi Orthodontic Archwires: An X-ray Diffraction Study

    Directory of Open Access Journals (Sweden)

    Sumit Kumar Yadav

    2013-01-01

    Results: Unloading force values of NiTi orthodontic wires were significantly decreased after exposure to both fluoride solutions (p < 0.001. Corrosive changes in surface topography were observed for both fluoride solutions. Wires exposed to acidic fluoride appeared as more severely affected. X-ray diffraction analysis showed no change in crystal lattice of NiTi wires in both solutions. Conclusion: The results suggest that using topical fluoride agents with NiTi wire could decrease the functional unloading mechanical properties of the wire and contribute to prolonged orthodontic treatment.

  8. Appcelerator Titanium patterns and best practices

    CERN Document Server

    Pollentine, Boydlee

    2013-01-01

    The book takes a step-by-step approach to help you understand CommonJS and Titanium architecture patterns, with easy to follow samples and plenty of in-depth explanations If you're an existing Titanium developer or perhaps a new developer looking to start off your Titanium applications "the right way", then this book is for you. With easy to follow examples and a full step-by-step account of architecting a sample application using CommonJS and MVC, along with chapters on new features such as ACS, you'll be implementing enterprise grade Titanium solutions in no time. You should have some JavaSc

  9. Water Fluoridation Statistics - Percent of PWS population receiving fluoridated water

    Data.gov (United States)

    U.S. Department of Health & Human Services — 2000-2014. Water Fluoridation Statistics is a biennial report of the percentage and number of people receiving fluoridated water from 2000 through 2014, originally...

  10. Water Fluoridation Statistics - Percent of PWS population receiving fluoridated water

    Data.gov (United States)

    U.S. Department of Health & Human Services — 2000-2014 Water Fluoridation Statistics is a biennial report of the percentage and number of people receiving fluoridated water from 2000 through 2014, originally...

  11. Study On Precipitation Of UO2 Ex-AUC Powder. Part I: Precipitation Of AUC By (NH4)2CO3 From Uranyl Fluoride Solution

    International Nuclear Information System (INIS)

    Nguyen Trong Hung; Le Ba Thuan; Do Van Khoai; Nguyen Thanh Thuy; Nguyen Van Tung

    2011-01-01

    In this paper, Ammonium Uranyl Carbonate (AUC) powders were prepared by precipitation method in solution. UO 2 F 2 /HF, ammonium carbonate (AC), and ammonium hydroxide solution were used as precursors for precipitation. The influence of C/U ratio (mol/mol), AC concentration (g/L), reaction temperature ( o C), on characteristics of AUC powders was also investigated. Then, the synthesized AUC powders were analyzed (to define) phase composition (X-ray), fluorine content, morphology (by SEM), and specific surface area (BET). (author)

  12. Effect of 0.02% NaF solution on enamel demineralization and fluoride uptake by deciduous teeth in vitro Efeito da solução de NaF a 0,02% na desmineralização e incorporação de fluoreto pelo esmalte de dentes decíduos in vitro

    Directory of Open Access Journals (Sweden)

    Silvia José Chedid

    2004-03-01

    Full Text Available The application of 0.02% NaF solution on teeth with a cotton swab instead of brushing with fluoride dentifrice has been suggested for young children to reduce the risk of dental fluorosis, but its anticariogenic effect has not been evaluated. Thus, we studied the in vitro effect of 0.02% NaF solution on enamel demineralization and fluoride uptake in deciduous teeth; non-fluoride dentifrice and fluoride dentifrice (1,100 mg F/g were used, respectively, as negative and positive controls. The treatment with fluoride dentifrice was more effective in reducing enamel demineralization (p A aplicação da solução de NaF a 0,02%, no lugar de dentifrício fluoretado, tem sido sugerida para ser aplicada com cotonete nos dentes de bebês para reduzir o risco de fluorose dental. Como o efeito anticariogênico dessa recomendação não tem sido estudado, avaliou-se in vitro seu efeito na redução da desmineralização e incorporação de fluoreto no esmalte de dentes decíduos; dentifrício não fluoretado e fluoretado (1.100 mg F/g foram utilizados como controles negativo e positivo, respectivamente. O dentifrício fluoretado foi mais efetivo que a solução de NaF a 0,02% na redução de desmineralização e na incorporação de fluoreto no esmalte (p < 0,05. Os dados sugerem que uso alternativo de NaF a 0,02% ao invés de dentifrício fluoretado para reduzir o risco de fluorose dental deve ser reavaliado, especialmente se a cárie dental precisa ser controlada.

  13. The cariostatic mechanisms of fluoride

    Directory of Open Access Journals (Sweden)

    Kata Rošin-Grget

    2013-11-01

    Full Text Available This article discusses the possible cariostatic mechanisms of the action of fluoride. In the past, fluoride inhibition of caries was ascribed to reduced solubility of enamel due to incorporation of fluoride (F– into the enamel minerals. The present evidence from clinical and laboratory studies suggests that the caries-preventive mode of action of fluoride is mainly topical. There is convincing evidence that fluoride has a major effect on demineralisation and remineralisation of dental hard tissue. The source of this fluoride could either be fluorapatite (formed due to the incorporation of fluoride into enamel or calcium fluoride (CaF2-like precipitates, which are formed on the enamel and in the plaque after application of topical fluoride. Calcium fluoride deposits are protected from rapid dissolution by a phosphate –protein coating of salivary origin. At lower pH, the coating is lost and an increased dissolution rate of calcium fluoride occurs. The CaF2, therefore, act as an efficient source of free fluoride ions during the cariogenic challenge. The current evidence indicates that fluoride has a direct and indirect effect on bacterial cells, although the in vivo implications of this are still not clear. Conclusion. A better understanding of the mechanisms of the action of fluoride is very important for caries prevention and control. The effectiveness of fluoride as a cariostatic agent depends on the availability of free fluoride in plaque during cariogenic challenge, i.e. during acid production. Thus, a constant supply of low levels of fluoride in biofilm/saliva/dental interference is considered the most beneficial in preventing dental caries.

  14. The cariostatic mechanisms of fluoride.

    Science.gov (United States)

    Rošin-Grget, Kata; Peroš, Kristina; Sutej, Ivana; Bašić, Krešimir

    2013-11-01

    This article discusses the possible cariostatic mechanisms of the action of fluoride. In the past, fluoride inhibition of caries was ascribed to reduced solubility of enamel due to incorporation of fluoride (F-) into the enamel minerals. The present evidence from clinical and laboratory studies suggests that the caries-preventive mode of action of fluoride is mainly topical. There is convincing evidence that fluoride has a major effect on demineralisation and remineralisation of dental hard tissue. The source of this fluoride could either be fluorapatite (formed due to the incorporation of fluoride into enamel) or calcium fluoride (CaF2)-like precipitates, which are formed on the enamel and in the plaque after application of topical fluoride. Calcium fluoride deposits are protected from rapid dissolution by a phosphate -protein coating of salivary origin. At lower pH, the coating is lost and an increased dissolution rate of calcium fluoride occurs. The CaF2, therefore, act as an efficient source of free fluoride ions during the cariogenic challenge. The current evidence indicates that fluoride has a direct and indirect effect on bacterial cells, although the in vivo implications of this are still not clear. A better understanding of the mechanisms of the action of fluoride is very important for caries prevention and control. The effectiveness of fluoride as a cariostatic agent depends on the availability of free fluoride in plaque during cariogenic challenge, i.e. during acid production. Thus, a constant supply of low levels of fluoride in biofilm/saliva/dental interference is considered the most beneficial in preventing dental caries. Copyright © 2013 by Academy of Sciences and Arts of Bosnia and Herzegovina.

  15. Amelioration of Fluoride Toxicity with the Use of Indigenous Inputs

    Directory of Open Access Journals (Sweden)

    Maitra A.

    2013-08-01

    Full Text Available An assessment was undertaken to study the efficacy of bacterial consortia isolated from different sources viz. rhizosphere of rice plant, oil spill sites of a petrol pump and from the sludge of a pharmaceutical waste water drain against the impact of fluoride. The experiments were conducted with two crops. In this mung bean experiment Vigna radiata was selected as a test crop. The seeds were sown in the field with bacterial consortia, compost and reduced dose (25% less nitrogen than recommended dose of chemical fertilizer. After 30days of seed sowing (DAS, plants were collected from the field and dipped into the sodium fluoride solution with different concentrations for 48 hours. Thereafter, the impact of fluoride on chlorophyll, sugar, proline and relative water content (% were evaluated. Scanning electron microscopy (SEM of the stem section was performed. SEM studies revealed that anatomical structure deformed with 1.5 mg/l sodium fluoride solution. It was observed that such treatment combination during the sowing of crops leads to combat the impact of lower doses of sodium fluoride (0.2 mg/l. Another experiment was also conducted within plastic pots with and without bacterial consortia isolated from rhizosphere of rice plant and oil spilled soil of petrol pump with the same field soil. Each pot was filled with 5 kg of soil + 2lt of water (on the basis of soil saturation. Oryza sativa seedlings were transplanted with different strength of sodium fluoride solution (25 mgNaF/kg, 50 mgNaF/kg, 100 mgNaF/kg and 500mgNaF/kg within the above pots. In second experiment, rice plants dried in all pots after 500 mgNaF/kg concentration of sodium fluoride. In this pot experiment bacterial strain are capable of reducing fluoride content in soil as noted by measuring fluoride in the pot soil after the experiment.

  16. Influence of Irradiance, Flow Rate, Reactor Geometry, and Photopromoter Concentration in Mineralization Kinetics of Methane in Air and in Aqueous Solutions by Photocatalytic Membranes Immobilizing Titanium Dioxide

    Directory of Open Access Journals (Sweden)

    Ignazio Renato Bellobono

    2008-01-01

    Full Text Available Photomineralization of methane in air (10.0–1000 ppm (mass/volume of C at 100% relative humidity (dioxygen as oxygen donor was systematically studied at 318±3 K in an annular laboratory-scale reactor by photocatalytic membranes immobilizing titanium dioxide as a function of substrate concentration, absorbed power per unit length of membrane, reactor geometry, and concentration of a proprietary vanadium alkoxide as photopromoter. Kinetics of both substrate disappearance, to yield intermediates, and total organic carbon (TOC disappearance, to yield carbon dioxide, were followed. At a fixed value of irradiance (0.30 W⋅cm-1, the mineralization experiments in gaseous phase were repeated as a function of flow rate (4–400 m3⋅h−1. Moreover, at a standard flow rate of 300 m3⋅h−1, the ratio between the overall reaction volume and the length of the membrane was varied, substantially by varying the volume of reservoir, from and to which circulation of gaseous stream took place. Photomineralization of methane in aqueous solutions was also studied, in the same annular reactor and in the same conditions, but in a concentration range of 0.8–2.0 ppm of C, and by using stoichiometric hydrogen peroxide as an oxygen donor. A kinetic model was employed, from which, by a set of differential equations, four final optimised parameters, k1 and K1, k2 and K2, were calculated, which is able to fit the whole kinetic profile adequately. The influence of irradiance on k1 and k2, as well as of flow rate on K1 and K2, is rationalized. The influence of reactor geometry on k values is discussed in view of standardization procedures of photocatalytic experiments. Modeling of quantum yields, as a function of substrate concentration and irradiance, as well as of concentration of photopromoter, was carried out very satisfactorily. Kinetics of hydroxyl radicals reacting between themselves, leading to hydrogen peroxide, other than with substrate or

  17. Fluoride and Water (For Parents)

    Science.gov (United States)

    ... risk of tooth decay" on the label. The Controversy Over Fluoride Opponents of water fluoridation have questioned ... Us Contact Us Partners Editorial Policy Permissions Guidelines Privacy Policy & Terms of Use Notice of Nondiscrimination Visit ...

  18. Development of a Novel Solid-State Sensor Electrode Based on Titanium Thin Film as an Indicator Electrode in Potentiometric and Conductometric Acid-Base Titration in Aqueous Solution

    OpenAIRE

    Abu Ghalwa, Nasser

    2012-01-01

    A modified Ti/(SnO2 + Sb2O3) electrode was prepared by thermal deposition on titanium substrate and its use as indicator electrode to potentiometric and conductometric acid-base titration in aqueous solution at 298 K was developed. The E-pH curve is linear with slope of 0.0512 V/dec at 298 K. The standard potential of this electrode, E0, was determined with respect to the SCE as reference electrode. The recovery percentages for potentiometric and conductometric acid-base titration for acetic ...

  19. Thermal decomposition of the b.c.c. β-solid solution of titanium alloy containing 6.7 at% Mo, 3 at% Zr, and 1.8 at% Sn. 1

    International Nuclear Information System (INIS)

    Zakharova, M.I.; Khundzhua, A.K.; Kertesz, L.; Szasz, A.

    1981-01-01

    Changes in the crystal structure of the titanium alloy, containing 6.7 at% Mo, 3 at% Zr, and 1.8 at% Sn, during thermal decomposition are followed by means of X-ray and electron diffraction methods. Parallel to these tests the alteration in the electron structure and chemical bonds of the alloy are investigated with the help of the soft-x-ray emission (SXES) method. Attention is focussed on the at room temperature not equilibrated b.c.c. β-solid solution, on the metastable transition phase ω, and on the equilibrium phase α. (author)

  20. Preparation of rare earth fluorides from apatite concentrate

    International Nuclear Information System (INIS)

    Mulyarchuk, I.F.; Voloshchenko, M.V.; Zen'kovich, E.G.; Sumenkova, V.V.; AN Ukrainskoj SSR, Kiev. Inst. Problem Lit'ya)

    1980-01-01

    The processes of preparation of the rare earths element sum from apatite concentrate of the Khibins, connected with preliminary extraction of rare earth phosphates from nitric acid extract using solvent extraction or direct precipitation from the extract by solution of potassium and ammonium fluorides. The sequence of the processes of the first variant is the following: solvent extraction of rare earths by tributylphosphate from clarified nitric acid extract of apatite with subsequent reextraction of rare earths with water and precipitation of rare earth phosphates from aqueous solution during neutralization by ammonia. In case of fluoride preparation from rare earth phosphate the main attention is paid to precipitation and filtration of fluorides. Technological scheme and cost price of industry for the production of 1800 t of rare earth trifluorides a year are calculated. When taking account of TBP losses according to its solubility the industry cost price is 1O times lower the modern cost of rare earth fluorides

  1. Purification of Drinking Water from Fluorides by Reverse Osmosis

    Directory of Open Access Journals (Sweden)

    Aleksander A.

    2018-03-01

    Full Text Available Introduction: An important task in the sphere of sanitary and epidemiological welfare of the population of the Russian Federation is provision of drinking water. Tap water must not contain pathogenic bacteria and dangerous chemicals. Purification systems regulate the concentration of fluoride ions in drinking water. The aim of this paper is to study the possibility of purifying tap water from fluoride ions by reverse osmosis. Materials and Methods: We used the Alfa Laval PilotUnit 2.5 "RO/NF with a set of spiral-type membrane elements RO99-2517/48 to remove fluoride ions. We measured the concentration of fluoride ions by the potentiometric method using the Hanna HI 2211 (pH/mV/T. Fluoride-selective electrode ELIS 131 F was used as an indicator electrode and the standard chloride-silver electrode EVL-1M3 was used as a reference electrode. Both the calibration and buffer solutions were prepared from chemically pure reagents and A. R. purity for analysis reagents according to GOST 4386-89. Results: A single passage of water through the reverse osmosis membrane reduced the concentration of fluoride ions from 2.29 ± 0.02 to 0.240 ± 0.015 mg/l. Double passage of water reduced the concentration by a factor of two. As the concentration of fluoride ions increased in the retentate, the concentration in the filtrate slightly increased too. Purification of water reduced the concentration of fluoride ions from 20 mg/l, to 0.5 mg/l. Discussion and Conclusions: Thus, using the Alfa Laval PilotUnit 2.5" RO/NF with a set of spiral-type membrane elements RO99-2517/48 filters tap water of ions of fluoride to the maximum allowable concentration. This study opens the perspective of using reverse osmosis to purify tap water with high concentration of fluoride ions.

  2. Fluoride resistance in Streptococcus mutans

    NARCIS (Netherlands)

    Liao, Ying

    2017-01-01

    Fluoride has been used as the most effective anti-caries agent for over five decades. It functions not only on the dental hard tissues, but also as an antimicrobial agent. It is known that oral bacteria are able to develop resistance to fluoride, which may affect the effectiveness of fluoride in

  3. Urinary fluoride excretion after application of fluoride varnish and use of fluoride toothpaste in young children

    DEFF Research Database (Denmark)

    Lockner, Frida; Twetman, Svante; Stecksén-Blicks, Christina

    2017-01-01

    BACKGROUND: The efficacy and safety of combined use of topical fluoride products are essential issues that must be monitored. AIM: To assess urinary excretion of fluoride after application of two different dental varnishes containing 2.26% fluoride in 3- to 4-year-old children and to compare...... the levels with and without parallel use of fluoride toothpaste. DESIGN: Fifteen healthy children were enrolled to a randomized crossover trial that was performed in two parts: Part I with twice-daily tooth brushing with fluoride toothpaste and Part II with twice-daily brushing with a non-fluoride toothpaste....... After a 1-week run-in period, 0.1 mL of the two fluoride varnishes (Duraphat and Profluorid Varnish) was topically applied in a randomized order. Baseline and experimental urine was collected during 6-h periods. The fluoride content was determined with an ion-sensitive electrode. RESULTS...

  4. Spatial distribution mapping of drinking water fluoride levels in Karnataka, India: fluoride-related health effects.

    Science.gov (United States)

    Chowdhury, Chitta R; Shahnawaz, Khijmatgar; Kumari, Divya; Chowdhury, Avidyuti; Bedi, Raman; Lynch, Edward; Harding, Stewart; Grootveld, Martin

    2016-11-01

    (1) To estimate the concentrations of fluoride in drinking water throughout different zones and districts of the state of Karnataka. (2) To investigate the variation of fluoride concentration in drinking water from different sources, and its relationships to daily temperature and rainfall status in the regional districts. (3) To develop an updated fluoride concentration intensity map of the state of Karnataka, and to evaluate these data in the context of fluoride-related health effects such as fluorosis and their prevalence. Aqueous standard solutions of 10, 100 and 1,000 ppm fluoride (F - ) were prepared with analytical grade Na + /F - and a buffer; TISAB II was incorporated in both calibration standard and analysis solutions in order to remove the potentially interfering effects of trace metal ions. This analysis was performed using an ion-selective electrode (ISE), and mean determination readings for n = 5 samples collected at each Karnataka water source were recorded. The F - concentration in drinking water in Karnataka state was found to vary substantially, with the highest mean values recorded being in the north-eastern zone (1.61 ppm), and the lowest in the south-western one (only 0.41 ppm). Analysis of variance (ANOVA) demonstrated that there were very highly significant 'between-zone' and 'between-districts-within-zones' sources of variation (p water source F - levels within this state. The southern part of Karnataka has low levels of F - in its drinking water, and may require fluoridation treatment in order to mitigate for dental caries and further ailments related to fluoride deficiency. However, districts within the north-eastern region have contrastingly high levels of fluoride, an observation which has been linked to dental and skeletal fluorosis. This highlights a major requirement for interventional actions in order to ensure maintenance of the recommended range of fluoride concentrations (0.8-1.5 ppm) in Karnataka's drinking water

  5. [The effect of fluoride-containing tooth paste on dental plaque and on fluoride level in the mouth].

    Science.gov (United States)

    Oomori, H

    1989-01-01

    Various kinds of fluoride have been used for a long time and there are many reports concerning fluorides and their effects. Recently, the caries-inhibiting action of fluoride-containing tooth paste has been given much attention. In this study, I tried to clarify the residual time and amount of fluoride derived from the fluoride-containing tooth paste in the mouth, as well as to assess possible variation in bacterial composition in the dental plaque bacteriologically and biochemically. In the study on the fluoride clearance from the mouth, both 1.0 g and 0.5 g of paste showed the same reduction rates; and about an 80% reduction was recognized between the value at 3 minutes and that at 30 minutes, and about a 40% reduction from the 30-minute to the 60-minute interval. Next, a study on the variation in plaque bacteria was carried out. The total number of the CFU on each plate was not different between samples obtained before and after the use of the tooth paste; moreover, no difference was noted between aerobic and anaerobic culture. However, when plaque before and after brushing with fluoride-containing tooth paste were cultured in 10% sucrose solution, the differences of acid production such as lactic acid, acetic acid, and formic acid were demonstrated. Namely, these acid productions were inhibited after the use of fluoride, especially lactic acid was strongly inhibited. On the other hand, when Str. mutans from the plaque obtained after the use of fluoride-containing tooth paste was cultured in fluoride-free BHI broth, the inhibition of acid from carbohydrates was not shown clearly.(ABSTRACT TRUNCATED AT 250 WORDS)

  6. The effect of different fluoride application methods on the remineralization of initial carious lesions.

    Science.gov (United States)

    Byeon, Seon Mi; Lee, Min Ho; Bae, Tae Sung

    2016-05-01

    The purpose of this study was to assess the effect of single and combined applications of fluoride on the amount of fluoride release, and the remineralization and physical properties of enamel. Each of four fluoride varnish and gel products (Fluor Protector, FP, Ivoclar Vivadent; Tooth Mousse Plus, TM, GC; 60 Second Gel, A, Germiphene; CavityShield, CS, 3M ESPE) and two fluoride solutions (2% sodium fluoride, N; 8% tin(ii) fluoride, S) were applied on bovine teeth using single and combined methods (10 per group), and then the amount of fluoride release was measured for 4 wk. The electron probe microanalysis and the Vickers microhardness measurements were conducted to assess the effect of fluoride application on the surface properties of bovine teeth. The amount of fluoride release was higher in combined applications than in single application (p < 0.05). Microhardness values were higher after combined applications of N with FP, TM, and CS than single application of them, and these values were also higher after combined applications of S than single application of A (p < 0.05). Ca and P values were higher in combined applications of N with TM and CS than single application of them (p < 0.05). They were also increased after combined applications of the S with A than after single application (p < 0.05). Combined applications of fluoride could be used as a basis to design more effective methods of fluoride application to provide enhanced remineralization.

  7. Application of Electrocoagulation Process Using Iron and Aluminum Electrodes for Fluoride Removal from Aqueous Environment

    Directory of Open Access Journals (Sweden)

    Edris Bazrafshan

    2012-01-01

    Full Text Available Fluoride in drinking water above permissible level is responsible for human being affected by skeletal fluorosis. The present study was carried out to assess the ability of electrocoagulation process with iron and aluminum electrodes in order to removal of fluoride from aqueous solutions. Several working parameters, such as fluoride concentration, pH, applied voltage and reaction time were studied to achieve a higher removal capacity. Variable concentrations (1, 5 and 10 mg L-1 of fluoride solutions were prepared by mixing proper amount of sodium fluoride with deionized water. The varying pH of the initial solution (3, 7 and 10 was also studied to measure their effects on the fluoride removal efficiency. Results obtained with synthetic solution revealed that the most effective removal capacities of fluoride could be achieved at 40 V electrical potential. In addition, the increase of electrical potential, in the range of 10-40 V, enhanced the treatment rate. Also comparison of fluoride removal efficiency showed that removal efficiency is similar with iron and aluminum electrodes. Finally it can be concluded that the electrocoagulation process has the potential to be utilized for the cost-effective removal of fluoride from water and wastewater.

  8. Diffusion of fluoride in bovine enamel

    International Nuclear Information System (INIS)

    Flim, G.J.; Arends, J.; Kolar, Z.

    1976-01-01

    The uptake of 18 F and the penetration of both F and 18 F in bovine enamel was investigated. Sodium fluoride solutions buffered at pH 7 were employed. The uptake of 18 F was measured by a method described by R. Duckworth and M. Braden, Archs. Oral. Biol., 12(1967), pp. 217-230. The penetration concentration profiles of fluoride (F, 18 F) in the enamel were measured by a sectioning technique. The 18 F uptake in enamel was proportional to approximately tsup(3/4); t being the uptake time. The 18 F concentration as a function of the position in the enamel can be described by: c*(x,t) = c 0 *(t)exp[-α*(t)x]. After correction for the initial fluoride concentration in enamel, for unlabelled fluoride the same dependency is obtained. A model based on simultaneous diffusion and chemical reaction in the pores and diffusion into the hydroxyapatite crystallites will be presented. The results show that diffusion coefficients of the pores are approximately equal to 10 -10 cm 2 s -1 and in the apatite crystallites approximately equal to 10 -17 cm 2 s -1 . The limitations and the approximations of the model are discussed

  9. FLUORIDE SORPTION USING MORRINGA INDICA-BASED ACTIVATED CARBON

    Directory of Open Access Journals (Sweden)

    G. Karthikeyan, S. Siva Ilango

    2007-01-01

    Full Text Available Batch adsorption experiments using activated carbon prepared from Morringa Indica bark were conducted to remove fluoride from aqueous solution. A minimum contact time of 25 min was required for optimum fluoride removal. The influence of adsorbent, dose, pH, co-ions (cations and anions on fluoride removal by the activated carbon has been experimentally verified. The adsorption of fluoride was studied at 30 C, 40 C and 50 C. The kinetics of adsorption and adsorption isotherms at different temperatures were studied. The fluoride adsorption obeyed both Langmuir and Freundlich isotherms and followed a pseudo first order kinetic model. The thermodynamic studies revealed that the fluoride adsorption by Morringa Indica is an endothermic process indicating an increase in sorption rate at higher temperatures. The negative values of G indicate the spontaneity of adsorption. SEM and XRD studies confirmed the surface morphological characteristics of the adsorbent and the deposition of fluoride on the surface of the material.

  10. Small molecule fluoride toxicity agonists.

    Science.gov (United States)

    Nelson, James W; Plummer, Mark S; Blount, Kenneth F; Ames, Tyler D; Breaker, Ronald R

    2015-04-23

    Fluoride is a ubiquitous anion that inhibits a wide variety of metabolic processes. Here, we report the identification of a series of compounds that enhance fluoride toxicity in Escherichia coli and Streptococcus mutans. These molecules were isolated by using a high-throughput screen (HTS) for compounds that increase intracellular fluoride levels as determined via a fluoride riboswitch reporter fusion construct. A series of derivatives were synthesized to examine structure-activity relationships, leading to the identification of compounds with improved activity. Thus, we demonstrate that small molecule fluoride toxicity agonists can be identified by HTS from existing chemical libraries by exploiting a natural fluoride riboswitch. In addition, our findings suggest that some molecules might be further optimized to function as binary antibacterial agents when combined with fluoride. Copyright © 2015 Elsevier Ltd. All rights reserved.

  11. Fluoride and Oral Health

    DEFF Research Database (Denmark)

    O'Mullane, D M; Baez, R J; Jones, S

    2016-01-01

    and strategies is noteworthy. This updated version of ‘Fluoride and Oral Health’ has adopted an evidence-based approach to its commentary on the different fl uoride vehicles and strategies and also to its recommendations. In this regard, full account is taken of the many recent systematic reviews published...

  12. Corrosion resistant materials for fluorine and hydrogen fluoride

    Energy Technology Data Exchange (ETDEWEB)

    Hauffe, K.

    1984-12-01

    Aluminum and Duralumin are resistant against fluorine and hydrogen fluoride up to 600 and 700 K, respectively. The resistance of nickel and its alloys, particularly monel, against fluorine and hydrogen fluoride is fairly good up to 900 and 800 K. During the attack of nickel-chromium alloys by fluorine between 1000 and 1300 K, it appears an inner fluorination similarly to the inner oxidation. The resistance of titanium in water-free liquid fluorine at lower temperatures with <0,3 mm.a/sup -1/ is comparable to that of nickel and monel. However, the corrosion of titanium in gaseous fluorine amounts at 377 K only 0,0082 mm.a/sup -1/. In spite of their limited resistance against fluorine and hydrogen fluoride, very pure molybdenum and tungsten are employed as construction materials in the rocket technology because of their large strength at high temperatures if fluorine-hydrogen and fluorine-hydrazine flames are used. Lanthanum and calcium borides are only little attacked by fluorine hydrazine flames between 1400 and 1800 K; they are superior to all special grade alloys. The same is true in a lower temperature region (290-400 K) with fluorcarbon resins. Organic materials substitute in increasing extent metal alloys and non-metal inorganic materials.

  13. Corrosion resistant materials for fluorine and hydrogen fluoride

    International Nuclear Information System (INIS)

    Hauffe, K.

    1984-01-01

    Aluminum and Duralumin are resistant against fluorine and hydrogen fluoride up to 600 and 700 K, respectively. The resistance of nickel and its alloys, particularly monel, against fluorine and hydrogen fluoride is fairly good up to 900 and 800 K. During the attack of nickel-chromium alloys by fluorine between 1000 and 1300 K, it appears an inner fluorination similarly to the inner oxidation. The resistance of titanium in water-free liquid fluorine at lower temperatures with -1 is comparable to that of nickel and monel. However, the corrosion of titanium in gaseous fluorine amounts at 377 K only 0,0082 mm.a -1 . In spite of their limited resistance against fluorine and hydrogen fluoride, very pure molybdenum and tungsten are employed as construction materials in the rocket technology because of their large strength at high temperatures if fluorine-hydrogen and fluorine-hydrazine flames are used. Lanthanum and calcium borides are only little attacked by fluorine hydrazine flames between 1400 and 1800 K; they are superior to all special grade alloys. The same is true in a lower temperature region (290-400 K) with fluorcarbon resins. Organic materials substitute in increasing extent metal alloys and non-metal inorganic materials. (orig.) [de

  14. On the use of titanium hydride for powder injection moulding of titanium-based alloys

    International Nuclear Information System (INIS)

    Carrenoo-Morelli, E.; Bidaux, J.-E.

    2009-01-01

    Full text: Titanium and titanium-based alloys are excellent materials for a number of engineering applications because of their high strength, lightweight, good corrosion resistance, non magnetic characteristic and biocompatibility. The current processing steps are usually costly, and there is a growing demand for net-shape solutions for manufacturing parts of increasing complexity. Powder injection moulding is becoming a competitive alternative, thanks to the advances in production of good quality base-powders, binders and sintering facilities. Titanium hydride powders, have the attractiveness of being less reactive than fine titanium powders, easier to handle, and cheaper. This paper summarizes recent advances on PIM of titanium and titanium alloys from TiH2 powders, including shape-memory NiTi alloys. (author)

  15. Stress corrosion cracking of titanium alloys

    Science.gov (United States)

    May, R. C.; Beck, F. H.; Fontana, M. G.

    1971-01-01

    Experiments were conducted to study (1) the basic electrochemical behavior of titanium in acid chloride solutions and (2) the response of the metal to dynamic straining in the same evironment. The aim of this group of experiments was to simulate, as nearly as possible, the actual conditions which exist at the tip of a crack. One of the foremost theories proposed to explain the propagation of stress corrosion cracks is a hydrogen embrittlement theory involving the precipitation of embrittling titanium hydrides inside the metal near the crack tip. An initial survey of the basic electrochemical literature indicated that surface hydrides play a critical role in the electrochemistry of titanium in acid solutions. A comprehensive analysis of the effect of surface films, particularly hydrides, on the electrochemical behavior of titanium in these solution is presented.

  16. Sorption of cesium on titanium and zirconium phosphates

    International Nuclear Information System (INIS)

    Lebedev, V.N.; Mel'nik, N.A.; Rudenko, A.V.

    2003-01-01

    Titanium and zirconium phosphates were prepared from mineral raw materials of the Kola Peninsula. Their capability to recover cesium cations from the model solutions and liquid radioactive waste (LRW) was studied. Titanium phosphate prepared from solutions formed by titanite breakdown demonstrates greater distribution coefficients of cesium as compared to zirconium phosphate. Titanium phosphate as a cheaper agent featuring greater sorption capacity was recommended for treatment of LRW to remove cesium [ru

  17. Opportunities in the electrowinning of molten titanium from titanium dioxide

    CSIR Research Space (South Africa)

    Van Vuuren, DS

    2005-10-01

    Full Text Available used, the following forms of titanium are produced: titanium sponge, sintered electrode sponge, powder, molten titanium, electroplated titanium, hydride powder, and vapor-phase depos- ited titanium. Comparing the economics of alter- native...-up for producing titanium via the Kroll process is approximately as follows: ilmenite ($0.27/kg titanium sponge); titanium slag ($0.75/kg titanium sponge); TiCl4 ($3.09/kg titanium sponge); titanium sponge raw materials costs ($5.50/kg titanium sponge); total...

  18. Monitoring of fluoride in water samples using a smartphone

    Energy Technology Data Exchange (ETDEWEB)

    Levin, Saurabh [Akvo Foundation (Netherlands); Krishnan, Sunderrajan [INREM Foundation (India); Rajkumar, Samuel; Halery, Nischal; Balkunde, Pradeep [Akvo Foundation (Netherlands)

    2016-05-01

    In several parts of India, groundwater is the only reliable, year round source for drinking water. Prevention of fluorosis, a chronic disease resulting from excess intake of fluoride, requires the screening of all groundwater sources for fluoride in endemic areas. In this paper, the authors present a field deployable colorimetric analyzer based on an inexpensive smartphone embedded with digital camera for taking photograph of the colored solution as well as an easy-fit, and compact sample chamber (Akvo Caddisfly). Phones marketed by different smartphone makers were used. Commercially available zirconium xylenol orange reagent was used for determining fluoride concentration. A software program was developed to use with the phone for recording and analyzing the RGB color of the picture. Linear range for fluoride estimation was 0–2 mg l{sup −1}. Around 200 samples, which consisted of laboratory prepared as well as field samples collected from different locations in Karnataka, India, were tested with Akvo Caddisfly. The results showed a significant positive correlation between Ion Selective Electrode (ISE) method and Akvo Caddisfly (Phones A, B and C), with correlation coefficient ranging between 0.9952 and 1.000. In addition, there was no significant difference in the mean fluoride content values between ISE and Phone B and C except for Phone A. Thus the smartphone method is economical and suited for groundwater fluoride analysis in the field. - Highlights: • Fluoride is an inorganic pollutant in ground water, affecting human health. • A colorimetric method for measurement of fluoride in drinking water with smartphone • Measurement is by mixing water with zirconyl xylenol orange complex reagent. • Results are comparable with laboratory-based ion selective fluoride electrode method.

  19. Monitoring of fluoride in water samples using a smartphone

    International Nuclear Information System (INIS)

    Levin, Saurabh; Krishnan, Sunderrajan; Rajkumar, Samuel; Halery, Nischal; Balkunde, Pradeep

    2016-01-01

    In several parts of India, groundwater is the only reliable, year round source for drinking water. Prevention of fluorosis, a chronic disease resulting from excess intake of fluoride, requires the screening of all groundwater sources for fluoride in endemic areas. In this paper, the authors present a field deployable colorimetric analyzer based on an inexpensive smartphone embedded with digital camera for taking photograph of the colored solution as well as an easy-fit, and compact sample chamber (Akvo Caddisfly). Phones marketed by different smartphone makers were used. Commercially available zirconium xylenol orange reagent was used for determining fluoride concentration. A software program was developed to use with the phone for recording and analyzing the RGB color of the picture. Linear range for fluoride estimation was 0–2 mg l"−"1. Around 200 samples, which consisted of laboratory prepared as well as field samples collected from different locations in Karnataka, India, were tested with Akvo Caddisfly. The results showed a significant positive correlation between Ion Selective Electrode (ISE) method and Akvo Caddisfly (Phones A, B and C), with correlation coefficient ranging between 0.9952 and 1.000. In addition, there was no significant difference in the mean fluoride content values between ISE and Phone B and C except for Phone A. Thus the smartphone method is economical and suited for groundwater fluoride analysis in the field. - Highlights: • Fluoride is an inorganic pollutant in ground water, affecting human health. • A colorimetric method for measurement of fluoride in drinking water with smartphone • Measurement is by mixing water with zirconyl xylenol orange complex reagent. • Results are comparable with laboratory-based ion selective fluoride electrode method.

  20. In Vitro Inhibition of Enamel Demineralisation by Fluoride-releasing Restorative Materials and Dental Adhesives.

    Science.gov (United States)

    Dionysopoulos, Dimitrios; Koliniotou-Koumpia, Eugenia; Helvatzoglou-Antoniades, Maria; Kotsanos, Nikolaos

    2016-01-01

    To determine the ability of 5 contemporary fluoride-releasing restoratives and 3 fluoride-releasing adhesives to inhibit enamel demineralisation surrounding restorations, and the associations between inhibition and the levels of fluoride released from these materials. Five fluoride-releasing restoratives (Fuji IX GP, Ketac N100, Dyract Extra, Beautifil II and Wave) and 3 fluoride-releasing adhesives (Stae, Prime & Bond NT and Fluoro Bond II) were investigated. Eight disks of each material were prepared. Fluoride release was measured daily using a fluoride-ion-selective electrode for 15 days. Twenty-four cavities for each group were restored with a restorative and an adhesive. Specimens were subjected to thermal stress and stored for 30 days in saline solution. After a 15-day pH-cycling regimen, two 150-μm-thick sections were derived from each specimen. Enamel lesion depth was measured at 0, 100, and 200 μm from each restoration's margin via polarised light microscopy. Of the restoratives investigated, Fuji IX GP released the most fluoride. The fluoride-releasing restoratives tested exhibited shallower enamel lesions than did the control group at all distances tested (p < 0.05). Fuji IX GP yielded significantly lower enamel lesion depth than did the other experimental materials. The depths of enamel lesions did not differ significantly when comparing restoratives applied with a fluoride-releasing adhesive with those applied with a non-fluoride-releasing adhesive. The fluoride-releasing materials tested reduced enamel demineralisation but to different extents, depending on their levels of fluoride release. Fluoride-releasing adhesives did not influence enamel lesion formation.

  1. Inhibitors for the corrosion of reactive metals: titanium and zirconium and their alloys in acid media

    International Nuclear Information System (INIS)

    Petit, J.A.; Chatainier, G.; Dabosi, F.

    1981-01-01

    The search for effective corrosion inhibitors for titanium and zirconium in acid media is growing because of the considerable increase in the use of these materials in chemical process equipment. It still remains limited, as appears from this review, because of the exceptionally high corrosion resistance of the metals. Titanium has received the greater attention. Its corrosion rate can be lowered by introduction in the medium of multivalent ions, inorganic and organic oxidants. Care should be taken to hold the concentration at a level exceeding some critical value, otherwise the corrosion rate increases. Complexing organic agents do not show such hazardous behaviour. The very rapid corrosion of titanium and zirconium in fluoride media may be lessened by complexing the fluoride ions. Though rarely encountered, localized corrosion may be avoided by using inhibitors. In some cases good corrosion inhibitors for titanium are dissolution accelerators for zirconium. (author)

  2. The effects of fluoride, strontium, theobromine and their combinations on caries lesion rehardening and fluoridation.

    Science.gov (United States)

    Lippert, Frank

    2017-08-01

    The aim was to investigate the effects of fluoride, strontium, theobromine and their combinations on caries lesion rehardening and fluoridation (EFU) under pH cycling conditions. Human enamel specimens were demineralized at 37°C for 24h using a pH 5.0 solution containing 50mM lactic acid and 0.2% Carbopol 907 which was 50% saturated with respect to hydroxyapatite. Lesions were assigned to nine treatment groups (n=16) based on Knoop surface microhardness indentation length. aqueous solutions were: placebo, 11.9mM sodium fluoride (F), 23.8mM sodium fluoride (2×F), 1.1mM strontium chloride hexahydrate (Sr), 1.1mM F theobromine, Sr+theobromine, F+Sr, F+theobromine, F+Sr+theobromine. Lesions were pH cycled for 5d (daily protocol: 3×1min-treatment; 2×60min-demineralization; 4×60min & overnight-artificial saliva). Knoop indentation length was measured again and%surface microhardness recovery (%SMHr) calculated. EFU was determined using the acid-etch technique. Data were analysed using ANOVA. Model showed fluoride dose-response for both variables (2×F>F>placebo). For%SMHr, F+Sr+/-theobromine resulted in more rehardening than F, however less than 2×F. F+theobromine was similar to F. For EFU, F+Sr was inferior to F, F+theobromine and F+Sr+theobromine which were similar and inferior to 2×F. In absence of fluoride, Sr, theobromine or Sr+theobromine were virtually indistinguishable from placebo and inferior to F. It can be concluded that a) strontium aids rehardening but not EFU and only in presence of fluoride; b) theobromine does not appear to offer any anti-caries benefits in this model; c) there are no synergistic effects between strontium and theobromine in the presence or absence of fluoride. Copyright © 2017 Elsevier Ltd. All rights reserved.

  3. Industrial fluoride pollution: chronic fluoride poisoning in Cornwall Island cattle

    Energy Technology Data Exchange (ETDEWEB)

    Krook, L.; Maylin, G.A.

    1979-04-01

    An aluminum plant on the south bank of the St. Lawrence River, southwest of Cornwall Island, Ontario, Canada, has emitted 0.816 metric tons of fluoride daily since 1973. Considerably higher amounts were emitted from 1959 to 1973. The plant was designated as the major source of fluoride emissions impacting on Cornwall Island. Cattle located on this island showed signs of chronic fluoride poisoning. This poisoning was manifested clinically by stunted growth and dental fluorosis to a degree of severe interference with drinking and mastication. This Cornwall Island herds study indicates that the established tolerance level of fluoride for performance of dairy and beef cattle is not valid since the tolerance level was set based on experiments with healthy calves which were exposed to dietary fluoride from 3 to 4 months of age and not on cattle which were chronically exposed to fluoride from conception to death. 56 references.

  4. The determination of small amounts of fluoride in uranium compounds by use of an ion-selective electrode

    International Nuclear Information System (INIS)

    Shelton, B.M.

    1975-01-01

    A method is presented for the determination of fluoride in uranium metal and oxide at levels from 16 p.p.m. upwards. Uranium is separated from fluoride by extraction into a solution of di(2-ethylhexyl)-phosphoric acid (HDEHP) in carbon tetrachloride. The fluoride remaining in the aqueous phase is determined by potentiometric measurement with an ion-selective electrode. A correction is made for the fluoride lost during the dissolution or extraction step, or both, which is based on a determination of the apparent loss of fluoride on spiked samples that are taken through the whole procedure [af

  5. PREPARATION AND CHARACTERIZATION OF STRONTIUM FLUORIDE POWDERS ACTIVATED BY NEODYMIUM FLUORIDE

    Directory of Open Access Journals (Sweden)

    S. V. Kuznetsov

    2015-07-01

    Full Text Available Subject of Study. The paper deals with preparation processes of ultradisperse, homogeneous powder Sr1-хNdхF2+х (х= 0.003-0.2, with use of ammonium fluoride as the fluorinating agent taken over 114-120 % from stoichiometry. Method. Nitrate of strontium, neodymium nitrate hexahydrate, with the content equal to 99. 99 % of the basic substance and ammonium fluoride were used as the source of substances. Activated powders of strontium fluoride were obtained by the method of deposition from aqueous solutions by washing the precipitate with a solution of ammonium fluoride, taken over 114 - 120% from stoichiometry. The washed precipitate was centrifuged for 5-7 min, dried in the air at 30-350 C. Heat treatment of the dried precipitate was carried out in two stages: the first stage at the temperature of 200- 2500 C for 0.5-1 hour, the second one at 550- 6000 C for 2-3 hours. X-ray analysis of the synthesized samples was carried out on a Bruker D8 Advance diffractometer, radiation Cu K. The size and shape measuring of the particles of activated strontium fluoride was carried out by means of electron microscope Carl Zeiss NVision 40. The content of neodymium in activated powders of strontium fluoride was determined by the method of spectral emission analysis on the device LEA - S500. Chemical analysis for determination of ammonium ion (NH4+ content in the obtained samples was performed by the method of Kjeldahl. Calculations of lattice parameters, size of coherent scattering regions and the values of micro-deformations were carried out by TOPAS program. Main Results. Preparation processes of ultradisperse, homogeneous powder Sr1-хNdхF2+х (х= 0.003-0.2, with use of ammonium fluoride as the fluorinating agent taken over 114-120 % from stoichiometry, provides obtaining the firm solution Sr1-x-yNdx(NH4yF2+x-y of the cubic fluorite structure. It has been found out that the morphology and size of the resulting product depend on the quantity of

  6. Application of fluorides as reagents in exothermal reducing processes

    International Nuclear Information System (INIS)

    Solov'ev, A.I.; Maksimov, Yu.M.; Dedov, N.V.; Malyutina, V.M.; Avramchik, A.N.

    2002-01-01

    Thermodynamic calculations were made and the process of calcium-thermic reduction of titanium and zirconium tetrafluorides and their mixtures was experimentally studied. Compound TiF 4 and its mixture with ZrF 4 in amount no more than 34.3 % are reduced producing a well-formed ingot. When ZrF 4 content is exceeded in the mixture to be reduced as well as during reduction of pure ZrF 4 and the mixture of unseparated rare earth metal fluorides, metal and alloys are produced as embedded particles in solidified slag. Additional heat should be brought to produce qualitative ingot during the reducing process. Qualitative ingots of metal in weight up to 10 kg were produced during calcium-thermic reduction of zirconium and rare earth fluorides with application of high-frequency induction heating [ru

  7. Effect of Sodium Fluoride Mouthwash on the Frictional Resistance of Orthodontic Wires

    Directory of Open Access Journals (Sweden)

    Allahyar Geramy

    2017-12-01

    Full Text Available Objectives: The friction between the brackets and orthodontic wire during sliding mechanics inflicts difficulties such as decreasing the applied force and tooth movement and also the loss of anchorage. Therefore, many studies have focused on the factors that affect the friction. The purpose of this study was to assess the effect of 0.05% sodium fluoride mouthwash on the friction between orthodontic brackets and wire.Materials and Methods: Four types of orthodontic wires including rectangular standard stainless steel (SS, titanium molybdenum alloy (TMA, nickel-titanium (NiTi and copper-nickel-titanium (Cu-NiTi were selected. In each group, half of the samples were immersed in 0.05% sodium fluoride mouthwash and the others were immersed in artificial saliva for 10 hours. An elastomeric ligature was used for ligating the wires to brackets. The frictional test was performed in a universal testing machine at the speed of 10 mm/minute. Two-way ANOVA was used for statistical analysis of the friction rate.Results: The friction rate was significantly higher after immersion in 0.05% sodium fluoride mouthwash in comparison with artificial saliva (P=0.00. Cu-NiTi wire showed the highest friction value followed by TMA, NiTi and SS wires.  Conclusions: According to the results of the current study, 0.05% sodium fluoride mouthwash increased the frictional characteristics of all the evaluated orthodontic wires.

  8. Physiology and toxicity of fluoride

    Directory of Open Access Journals (Sweden)

    Dhar Vineet

    2009-01-01

    Full Text Available Fluoride has been described as an essential element needed for normal development and growth of animals and extremely useful for human beings. Fluoride is abundant in the environment and the main source of fluoride to humans is drinking water. It has been proved to be beneficial in recommended doses, and at the same time its toxicity at higher levels has also been well established. Fluoride gets accumulated in hard tissues of the body and has been know to play an important role in mineralization of bone and teeth. At high levels it has been known to cause dental and skeletal fluorosis. There are suggested effects of very high levels of fluoride on various body organs and genetic material. The purpose of this paper is to review the various aspects of fluoride and its importance in human life.

  9. Physiology and toxicity of fluoride.

    Science.gov (United States)

    Dhar, Vineet; Bhatnagar, Maheep

    2009-01-01

    Fluoride has been described as an essential element needed for normal development and growth of animals and extremely useful for human beings. Fluoride is abundant in the environment and the main source of fluoride to humans is drinking water. It has been proved to be beneficial in recommended doses, and at the same time its toxicity at higher levels has also been well established. Fluoride gets accumulated in hard tissues of the body and has been know to play an important role in mineralization of bone and teeth. At high levels it has been known to cause dental and skeletal fluorosis. There are suggested effects of very high levels of fluoride on various body organs and genetic material. The purpose of this paper is to review the various aspects of fluoride and its importance in human life.

  10. Histopathological changes of renal tissue following sodium fluoride administration in two consecutive generations of mice. Correlation with the urinary elimination of fluoride.

    Science.gov (United States)

    Dimcevici Poesina, Nicoleta; Bălălău, Cristian; Nimigean, Vanda Roxana; Nimigean, Victor; Ion, Ion; Baconi, Daniela; Bârcă, Maria; Băran Poesina, Violeta

    2014-01-01

    The present study was designed to investigate the toxic effects (evaluated as histopathological changes) of sodium fluoride on the kidney in two consecutive generations of NMRI mice. An attempt to correlate the toxicity with the urinary elimination of fluoride has been made, as urinary fluoride excretion has been widely used as an indicator of fluoride intake and exposure. Six mixed (males and females) animal groups have been constituted by dividing the populations of mice derived from pregnant females (named "mothers" 0.5 mg sodium fluoride) treated with 0.5 mg sodium fluoride by daily gavage and pregnant females (named "mothers" 0.25 mg sodium fluoride) treated with 0.25 mg sodium fluoride by daily gavage; three types of sodium fluoride treatments were administrated: homeopathic, allopathic-homeopathic and allopathic. When the animals reached the adulthood, by randomization, they were selected in pairs for giving birth to the second generation of mice. No treatments were administrated to the second generation of mice; thus, the urinary elimination of fluoride in the second generation is attributed to exposure at sodium fluoride before birth. The administration of sodium fluoride to the first generation (F1) is realized until the mice reached the adulthood. For the first generation, the urine was collected at three times, every three weeks: at the age of four weeks, seven weeks and 11 weeks; single sampling urine, at the age of four weeks, has been conducted for the second generation. The urine samples have been analyzed using the ion selective electrode method for fluoride. For the histopathological examination, the animals were killed by cervical dislocation; the kidneys were collected in a 10% formalin solution. The preparation of samples for optical microscopy was realized with Hematoxylin-Eosin staining. The results indicate that the elimination of fluoride was similar (at the second evaluation, at 7-week-old of the first generation) for the both generations

  11. Effect of different frequencies of fluoride dentifrice and mouthrinse administration: an in situ study

    Directory of Open Access Journals (Sweden)

    Daniela Correia Cavalcante Souza

    2010-12-01

    Full Text Available The effect of a combination of topical fluoridation methods for inhibition of enamel demineralization in the face of a cariogenic challenge has not been clearly established. This in situ crossover study aimed to assess whether the addition of daily use of fluoride mouthrinse (FR to that of fluoride dentifrice (FD is equivalent to increasing the frequency of FD application in terms of the effect on enamel demineralization and fluoride content. Over 3 phases of 14 days each, 12 volunteers wore appliances containing enamel blocks exposed to a 20 % sucrose solution 8 times/day. During each phase the blocks underwent one of the following treatments: 2x/day FD, 2x/day FD + 1x/day FR, and 3x/day FD. The blocks were assessed for hardness and fluoride content. Three x/day FD did not differ from 2x/day + 1x/day FR, however it enhanced demineralization protection when compared to 2x/day FD. All treatments produced an increase in enamel fluoride content compared to no treatment (sound blocks (p < 0.05, but the differences between them were not significant. The results of this study suggest that the daily use of fluoride mouthrinse combined with that of fluoride dentifrice has similar effects on enamel demineralization and fluoride content when compared to increasing the frequency of fluoride dentifrice use.

  12. Magnesium fluoride recovery method

    International Nuclear Information System (INIS)

    Gay, R.L.; McKenzie, D.E.

    1989-01-01

    A method of obtaining magnesium fluoride substantially free from radioactive uranium from a slag formed in the production of metallic uranium by the reduction of depleted uranium tetrafluoride with metallic magnesium in a retort wherein the slag contains the free metals magnesium and uranium and also oxides and fluorides of the metals. The slag having a radioactivity level of at least about 7,000 rhoCi/gm. The method comprises the steps of: grinding the slag to a median particle size of about 200 microns; contacting the ground slag in a reaction zone with an acid having a strength of from about 0.5 to 1.5 N for a time of from about 4 to about 20 hours in the presence of a catalytic amount of iron; removing the liquid product; treating the particulate solid product; repeating the last two steps at least one more time to produce a solid residue consisting essentially of magnesium fluoride substantially free of uranium and having a residual radioactivity level of less than about 1000 rhoCi/gm

  13. Sustainable approach for recycling waste lamb and chicken bones for fluoride removal from water followed by reusing fluoride-bearing waste in concrete.

    Science.gov (United States)

    Ismail, Zainab Z; AbdelKareem, Hala N

    2015-11-01

    Sustainable management of waste materials is an attractive approach for modern societies. In this study, recycling of raw waste lamb and chicken bones for defluoridation of water has been estimated. The effects of several experimental parameters including contact time, pH, bone dose, fluoride initial concentration, bone grains size, agitation rate, and the effect of co-existing anions in actual samples of wastewater were studied for fluoride removal from aqueous solutions. Results indicated excellent fluoride removal efficiency up to 99.4% and 99.8% using lamb and chicken bones, respectively at fluoride initial concentration of 10 mg F/L and 120 min contact time. Maximum fluoride uptake was obtained at neutral pH range 6-7. Fluoride removal kinetic was well described by the pseudo-second order kinetic model. Both, Langmuir and Freundlich isotherm models could fit the experimental data well with correlation coefficient values >0.99 suggesting favorable conditions of the process. Furthermore, for complete sustainable management of waste bones, the resulted fluoride-bearing sludge was reused in concrete mixes to partially replace sand. Tests of the mechanical properties of fluoride sludge-modified concrete mixes indicated a potential environmentally friendly approach to dispose fluoride sludge in concrete and simultaneously enhance concrete properties. Copyright © 2015 Elsevier Ltd. All rights reserved.

  14. Physiology and toxicity of fluoride

    OpenAIRE

    Dhar Vineet; Bhatnagar Maheep

    2009-01-01

    Fluoride has been described as an essential element needed for normal development and growth of animals and extremely useful for human beings. Fluoride is abundant in the environment and the main source of fluoride to humans is drinking water. It has been proved to be beneficial in recommended doses, and at the same time its toxicity at higher levels has also been well established. Fluoride gets accumulated in hard tissues of the body and has been know to play an important role in mineralizat...

  15. Chemistry of titanium, zirconium and thorium picramates

    International Nuclear Information System (INIS)

    Srivastava, R.S.; Agrawal, S.P.; Bhargava, H.N.

    1976-01-01

    Picramates of titanium, zirconium and thorium are prepared by treating the aqueous sulphate, chloride and nitrate solutions with sodium picramate. Micro-analysis, colorimetry and spectrophotometry are used to establish the compositions (metal : ligand ratio) of these picramates as 1 : 2 (for titanium and zirconium) and 1 : 4 (for thorium). IR studies indicate H 2 N → Me coordination (where Me denotes the metal). A number of explosive properties of these picramates point to the fact that the zirconium picramate is thermally more stable than the picramates of titanium and thorium. (orig.) [de

  16. Leaching of Titanium and Silicon from Low-Grade Titanium Slag Using Hydrochloric Acid Leaching

    Science.gov (United States)

    Zhao, Longsheng; Wang, Lina; Qi, Tao; Chen, Desheng; Zhao, Hongxin; Liu, Yahui; Wang, Weijing

    2018-05-01

    Acid-leaching behaviors of the titanium slag obtained by selective reduction of vanadium-bearing titanomagnetite concentrates were investigated. It was found that the optimal leaching of titanium and silicon were 0.7% and 1.5%, respectively. The titanium and silicon in the titanium slag were firstly dissolved in the acidic solution to form TiO2+ and silica sol, and then rapidly reprecipitated, forming hydrochloric acid (HCl) leach residue. Most of the silicon presented in the HCl leach residue as floccules-like silica gel, while most of the titanium was distributed in the nano-sized rod-like clusters with crystallite refinement and intracrystalline defects, and, as such, 94.3% of the silicon was leached from the HCl leach residue by alkaline desilication, and 96.5% of the titanium in the titanium-rich material with some rutile structure was then digested by the concentrated sulfuric acid. This provides an alternative route for the comprehensive utilization of titanium and silicon in titanium slag.

  17. Fluoride removal performance of glass derived hydroxyapatite

    International Nuclear Information System (INIS)

    Liang, Wen; Zhan, Lei; Piao, Longhua; Russel, Christian

    2011-01-01

    Research highlights: → Novel sodium calcium borate glass derived hydroxyapatite (G-HAP) is prepared. → Micro-G-HAP adsorbs F - ions in solutions more effectively than commercial nano-HAP. → The adsorption kinetics and isotherms are well fitted by a second order kinetic model and Freundlich isotherm model. -- Abstract: A novel sodium calcium borate glass derived hydroxyapatite (G-HAP) with different ranges of particle size was prepared by immersion sodium calcium borate glass in 0.1 M K 2 HPO 4 solution by the ratio of 50 g L -1 for 7 days. The unique advantage of G-HAP for the adsorption of fluoride ions in solutions was studied. The effects of size and quantity of particles, pH value and adsorption time on adsorption performance were investigated. The maximum adsorption capacity was 17.34 mg g -1 if 5 g L -1 , - in solution more effectively than commercial nano-HAP, which makes potential application of the G-HAP in removing the fluoride ions from wastewater. The adsorption kinetics and isotherms for F - could be well fitted by a second order kinetic model and Freundlich isotherm model respectively, which could be used to describe the adsorption behavior. The mechanism of G-HAP in immobilizing F - from aqueous solutions was investigated by the X-ray diffraction (XRD), infrared spectra (IR) and scanning electron microscopy (SEM).

  18. Development of a Novel Solid-State Sensor Electrode Based on Titanium Thin Film as an Indicator Electrode in Potentiometric and Conductometric Acid-Base Titration in Aqueous Solution

    Directory of Open Access Journals (Sweden)

    Nasser Abu Ghalwa

    2012-01-01

    Full Text Available A modified Ti/(SnO2 + Sb2O3 electrode was prepared by thermal deposition on titanium substrate and its use as indicator electrode to potentiometric and conductometric acid-base titration in aqueous solution at 298 K was developed. The E-pH curve is linear with slope of 0.0512 V/dec at 298 K. The standard potential of this electrode, E0, was determined with respect to the SCE as reference electrode. The recovery percentages for potentiometric and conductometric acid-base titration for acetic acid against NaOH were calculated. The cell constant, specific conductance, and the molar conductance with dilution for some common electrolytes were measured.

  19. Removal of fluoride from water using aluminium containing compounds

    Institute of Scientific and Technical Information of China (English)

    M. Karthikeyan; K. P. Elango

    2009-01-01

    Batch adsorption studies were undertaken to assess the suitability of aluminium titanate (AT) and bismuth aluminate (BA) to remove fluoride ions from water.The effect of pH,dose of adsorbent,contact time,initial concentration,co-ions and temperature on fluoride removal efficiency were studied.The amounts of fluoride ions adsorbed,at 30℃ from 4 mg/L of fluoride ion solution,by AT and BA are 0.85 and 1.55 mg/g,respectively.The experimental data fitted well to the Freundlich and Langmuir isotherms.Thermodynamic parameters such as △H~0,△S~0 and △G~0 indicated that the removal of fluoride ions by AT is exothermic and non-spontaneous while that by BA is endothermic and spontaneous.Furrier transform infrared (FT-IR) analysis and X-ray diffraction (XRD) patterns of the adsorbent before and after adsorption indicated that fluoride ions are chemisorbed by these adsorbents.

  20. Sorption of fluoride using chemically modified Moringa oleifera leaves

    Science.gov (United States)

    Dan, Shabnam; Chattree, Amit

    2018-05-01

    Contamination of drinking water due to fluoride is a severe health hazard problem. Excess of fluoride (> 1.5 mg/L) in drinking water is harmful to human health. Various treatment technologies for removing fluoride from groundwater have been investigated. The present study showed that the leaves of Moringa oleifera, a herbal plant is an effective adsorbent for the removal of fluoride from aqueous solution. Acid treated Moringa oleifera leaves powder showed good adsorption capacity than alkali treated Moringa oleifera leaves powder. Batch sorptive defluoridation was conducted under the variable experimental condition such as pH, contact time, adsorbent dose and initial fluoride ion concentration. Maximum defluoridation was achieved at pH 1. The percentage of fluoride removal increases with adsorbent dose. The equilibrium sorption data were fitted into Langmuir, Freundlich and Temkin isotherms. Of the three adsorption isotherms, the R 2 value of Langmuir isotherm model was the highest. The maximum monolayer coverage ( Q max) from Langmuir isotherm model was determined to be 1.1441 mg/g, the separation factor indicating a favorable sorption experiment is 0.035. It was also discovered that the adsorption did not conform to the Freundlich adsorption isotherm. The heat of sorption process was estimated from Temkin Isotherm model to be - 0.042 J/mol which vividly proved that the adsorption experiment followed a physical process.

  1. The antimicrobial sensitivity of Streptococcus mutans and Streptococcus sangius to colloidal solutions of different nanoparticles applied as mouthwashes

    Directory of Open Access Journals (Sweden)

    Farzaneh Ahrari

    2015-01-01

    Full Text Available Background: Metal nanoparticles have been recently applied in dentistry because of their antibacterial properties. This study aimed to evaluate antibacterial effects of colloidal solutions containing zinc oxide (ZnO, copper oxide (CuO, titanium dioxide (TiO 2 and silver (Ag nanoparticles on Streptococcus mutans and Streptococcus sangius and compare the results with those of chlorhexidine and sodium fluoride mouthrinses. Materials and Methods: After adding nanoparticles to a water-based solution, six groups were prepared. Groups I to IV included colloidal solutions containing nanoZnO, nanoCuO, nanoTiO 2 and nanoAg, respectively. Groups V and VI consisted of 2.0% sodium fluoride and 0.2% chlorhexidine mouthwashes, respectively as controls. We used serial dilution method to find minimum inhibitory concentrations (MICs and with subcultures obtained minimum bactericidal concentrations (MBCs of the solutions against S. mutans and S. sangius. The data were analyzed by analysis of variance and Duncan test and P < 0.05 was considered as significant. Results: The sodium fluoride mouthrinse did not show any antibacterial effect. The nanoTiO 2 -containing solution had the lowest MIC against both microorganisms and also displayed the lowest MBC against S. mutans (P < 0.05. The colloidal solutions containing nanoTiO 2 and nanoZnO showed the lowest MBC against S. sangius (P < 0.05. On the other hand, chlorhexidine showed the highest MIC and MBC against both streptococci (P < 0.05. Conclusion: The nanoTiO 2 -containing mouthwash proved to be an effective antimicrobial agent and thus it can be considered as an alternative to chlorhexidine or sodium fluoride mouthrinses in the oral cavity provided the lack of cytotoxic and genotoxic effects on biologic tissues.

  2. Studies on Pu(IV)/(III)-oxalate precipitation from nitric acid containing high concentration of calcium and fluoride ions

    International Nuclear Information System (INIS)

    Kalsi, P.K.; Pawar, S.M.; Ghadse, D.R.; Joshi, A.R.; Ramakrishna, V.V.; Vaidya, V.N.; Venugopal, V.

    2003-01-01

    Plutonium (IV)/(III) oxalate precipitation from nitric acid solution, containing large amount of calcium and fluoride ions was investigated. It was observed that direct precipitation of Pu (IV) oxalate from nitric acid containing large amount of calcium and fluoride ions did not give good decontamination of Pu from calcium and fluoride impurities. However, incorporation of hydroxide precipitation using ammonium hydroxide prior to Pu (IV) oxalate precipitation results into PuO 2 with much less calcium and fluoride impurities. Whereas, good decontamination from calcium and fluoride impurities could be obtained by employing Pu (III) oxalate precipitation directly from nitric acid containing large amount of calcium and fluoride ions. A method was also developed to recover Pu from the oxalate waste containing calcium and fluoride ions. (author)

  3. Molecular mechanisms of fluoride toxicity.

    Science.gov (United States)

    Barbier, Olivier; Arreola-Mendoza, Laura; Del Razo, Luz María

    2010-11-05

    Halfway through the twentieth century, fluoride piqued the interest of toxicologists due to its deleterious effects at high concentrations in human populations suffering from fluorosis and in in vivo experimental models. Until the 1990s, the toxicity of fluoride was largely ignored due to its "good reputation" for preventing caries via topical application and in dental toothpastes. However, in the last decade, interest in its undesirable effects has resurfaced due to the awareness that this element interacts with cellular systems even at low doses. In recent years, several investigations demonstrated that fluoride can induce oxidative stress and modulate intracellular redox homeostasis, lipid peroxidation and protein carbonyl content, as well as alter gene expression and cause apoptosis. Genes modulated by fluoride include those related to the stress response, metabolic enzymes, the cell cycle, cell-cell communications and signal transduction. The primary purpose of this review is to examine recent findings from our group and others that focus on the molecular mechanisms of the action of inorganic fluoride in several cellular processes with respect to potential physiological and toxicological implications. This review presents an overview of the current research on the molecular aspects of fluoride exposure with emphasis on biological targets and their possible mechanisms of involvement in fluoride cytotoxicity. The goal of this review is to enhance understanding of the mechanisms by which fluoride affects cells, with an emphasis on tissue-specific events in humans. Copyright © 2010 Elsevier Ireland Ltd. All rights reserved.

  4. Melt cationic and anionic composition effect on titanium group metal corrosion in halogenides of alkali earths

    International Nuclear Information System (INIS)

    Tkhaj, V.; Kovalik, O.Yu.; Dikunov, Yu.G.; P'yankova, S.P.

    1997-01-01

    A study was made on interaction of titanium group metals with melts of chlorides and chloride-fluorides of alkaline earth metals and magnesium. It was revealed that the rate of metal corrosion increased from BaCl 2 2 2 2 in chloride series. It is explained by amplification of oxidation activity of salt cation in the series: Ba 2+ 2+ 2+ 2+ . It was also determined that corrosion rate of titanium exceeded the one of zirconium and hafnium, became reducing power of titanium was the highest in the given group

  5. Titanium and titanium alloys: fundamentals and applications

    National Research Council Canada - National Science Library

    Leyens, C; Peters, M

    2003-01-01

    ... number of titanium alloys have paved the way for light metals to vastly expand into many industrial applications. Titanium and its alloys stand out primarily due to their high specific strength and excellent corrosion resistance, at just half the weight of steels and Ni-based superalloys. This explains their early success in the aerospace and the...

  6. Development of an empirical model for fluoride removal from photovoltaic wastewater by electrocoagulation process

    KAUST Repository

    Drouiche, Nadjib

    2011-05-01

    Electrocoagulation experiments were conducted with bipolar aluminium electrodes to determine the optimum conditions for the fluoride removal from synthetic photovoltaic wastewater. A high fluoride concentration in community water supplies can cause fluorosis which has a detrimental effect on human health in particular on teeth and bones. A full 23 factorial design of experiments was used to obtain the best conditions of fluoride removal from water solutions. The three factors considered were initial fluoride concentration, applied potential, and supporting electrolyte dosage. Two levels for each factor were used; supporting electrolyte (0 and 100), applied potential (10 and 30 V), and initial fluoride concentration (20 and 25 mg/L). Results showed that the optimum conditions for fluoride removal from photovoltaic wastewater containing an initial fluoride concentration of 20 mg/L were a supporting electrolyte dose of 100 mg/L and an applied potential of 30 V. These gave a residual fluoride concentration of 8.6 mg/L which was below the standard discharge limit. A mathematical equation showing the relation between residual fluoride concentration and the effective variables was also developed. © 2011 Desalination Publications. All rights reserved.

  7. Risk Assessment Study of Fluoride Salts: Probability-Impact Matrix of Renal and Hepatic Toxicity Markers.

    Science.gov (United States)

    Usuda, Kan; Ueno, Takaaki; Ito, Yuichi; Dote, Tomotaro; Yokoyama, Hirotaka; Kono, Koichi; Tamaki, Junko

    2016-09-01

    The present risk assessment study of fluoride salts was conducted by oral administration of three different doses of sodium and potassium fluorides (NaF, KF) and zinc fluoride tetrahydrate (ZnF2 •4H2O) to male Wistar rats. The rats were divided into control and nine experimental groups, to which oral injections of 0.5 mL distilled water and 0.5 mL of fluoride solutions, respectively, were given. The dosage of fluoride compounds was adjusted to contain 2.1 mg (low-dose group, LG), 4.3 mg (mid-dose group, MG), and 5.4 mg fluoride per 200 g rat body weight (high-dose group, HG) corresponding to 5, 10, and 12.5 % of LD50 values for NaF. The 24-h urine volume, N-acetyl-β-D-glucosaminidase (NAG) and creatinine clearance (Ccr) were measured as markers of possible acute renal impact. The levels of alanine aminotransferase (ALT) and aspartate aminotransferase (AST) were determined in serum samples as markers of acute hepatic impact. The levels of serum and urinary fluoride were determined to evaluate fluoride bioavailability. The results reveal that higher doses of NaF, KF, and ZnF2 induced renal damage as indicated by higher urinary NAG (p fluoride is a potential, dose-dependent risk factor of renal tubular damage.

  8. Development of an empirical model for fluoride removal from photovoltaic wastewater by electrocoagulation process

    KAUST Repository

    Drouiche, Nadjib; Aoudj, Salaheddine; Lounici, Hakim; Mahmoudi, Hacè ne; Ghaffour, NorEddine; Goosen, Mattheus F A

    2011-01-01

    Electrocoagulation experiments were conducted with bipolar aluminium electrodes to determine the optimum conditions for the fluoride removal from synthetic photovoltaic wastewater. A high fluoride concentration in community water supplies can cause fluorosis which has a detrimental effect on human health in particular on teeth and bones. A full 23 factorial design of experiments was used to obtain the best conditions of fluoride removal from water solutions. The three factors considered were initial fluoride concentration, applied potential, and supporting electrolyte dosage. Two levels for each factor were used; supporting electrolyte (0 and 100), applied potential (10 and 30 V), and initial fluoride concentration (20 and 25 mg/L). Results showed that the optimum conditions for fluoride removal from photovoltaic wastewater containing an initial fluoride concentration of 20 mg/L were a supporting electrolyte dose of 100 mg/L and an applied potential of 30 V. These gave a residual fluoride concentration of 8.6 mg/L which was below the standard discharge limit. A mathematical equation showing the relation between residual fluoride concentration and the effective variables was also developed. © 2011 Desalination Publications. All rights reserved.

  9. Fluoride Removal From Drinking Water by Electrocoagulation Using Iron and Aluminum Electrodes

    Directory of Open Access Journals (Sweden)

    Takdastan

    2014-07-01

    Full Text Available Background Existence of fluoride in drinking water above the permissible level causes human skeletal fluorosis. Objectives Electrocoagulation by iron and aluminum electrodes was proposed for removing fluoride from drinking water. Materials and Methods Effects of different operating conditions such as treatment time, initial pH, applied voltage, type and number of electrodes, the spaces between aluminum and iron electrodes, and energy consumption during electrocoagulation were investigated in the batch reactor. Variable concentrations of fluoride solution were prepared by mixing proper amounts of sodium fluoride with deionized water. Results Experimental results showed that aluminum electrode is more effective in fluoride removal than iron, as in 40 minutes and initial pH of 7.5 at 20 V, the fluoride removal process reached to 97.86%. The final recommendable limit of fluoride (1.5 mg/L was obtained in 10 minutes at 20 V with the aluminum electrode. Conclusions In electrocoagulation with iron and aluminum electrodes, increase of voltage, number of electrodes and reaction time as well as decrease of the spaces between electrodes, enhanced the fluoride removal efficiency from drinking water. In addition the effect of pH and initial concentration of fluoride varied with types of electrodes.

  10. Fluoride in weathered rock aquifers of southern India: Managed Aquifer Recharge for mitigation.

    Science.gov (United States)

    Brindha, K; Jagadeshan, G; Kalpana, L; Elango, L

    2016-05-01

    Climatic condition, geology, and geochemical processes in an area play a major role on groundwater quality. Impact of these on the fluoride content of groundwater was studied in three regions-part of Nalgonda district in Telangana, Pambar River basin, and Vaniyar River basin in Tamil Nadu, southern India, which experience semi-arid climate and are predominantly made of Precambrian rocks. High concentration of fluoride in groundwater above 4 mg/l was recorded. Human exposure dose for fluoride through groundwater was higher in Nalgonda than the other areas. With evaporation and rainfall being one of the major contributors for high fluoride apart from the weathering of fluoride rich minerals from rocks, the effect of increase in groundwater level on fluoride concentration was studied. This study reveals that groundwater in shallow environment of all three regions shows dilution effect due to rainfall recharge. Suitable managed aquifer recharge (MAR) methods can be adopted to dilute the fluoride rich groundwater in such regions which is explained with two case studies. However, in deep groundwater, increase in fluoride concentration with increase in groundwater level due to leaching of fluoride rich salts from the unsaturated zone was observed. Occurrence of fluoride above 1.5 mg/l was more in areas with deeper groundwater environment. Hence, practicing MAR in these regions will increase the fluoride content in groundwater and so physical or chemical treatment has to be adopted. This study brought out the fact that MAR cannot be practiced in all regions for dilution of ions in groundwater and that it is essential to analyze the fluctuation in groundwater level and the fluoride content before suggesting it as a suitable solution. Also, this study emphasizes that long-term monitoring of these factors is an important criterion for choosing the recharge areas.

  11. 49 CFR 173.163 - Hydrogen fluoride.

    Science.gov (United States)

    2010-10-01

    ... 49 Transportation 2 2010-10-01 2010-10-01 false Hydrogen fluoride. 173.163 Section 173.163... Hydrogen fluoride. (a) Hydrogen fluoride (hydrofluoric acid, anhydrous) must be packaged as follows: (1) In... filling ratio of 0.84. (b) A cylinder removed from hydrogen fluoride service must be condemned in...

  12. Growth of fluoride treated Kalanchoe pinnata plants

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, H N; Applegate, H G

    1962-01-01

    Kalanchoe pinnata plants can absorb fluoride through roots. The absorption is related to the amount of fluoride applied to the soil. There appeared to be a relationship between the amount of fluoride adsorbed and the subsequent growth of the plants. Plants which adsorbed the largest amounts of fluoride had the greatest increase in growth.

  13. ITO electrode/photoactive layer interface engineering for efficient inverted polymer solar cells based on P3HT and PCBM using a solution-processed titanium chelate

    International Nuclear Information System (INIS)

    Zhang Wenqing; Zheng Hua; Tan Zhan'ao; Qian Deping; Li Liangjie; Xu Qi; Li Shusheng; Li Yongfang

    2012-01-01

    We report efficient inverted polymer solar cells (PSCs) based on poly(3-hexylthiophene) (P3HT) and [6,6]-phenyl-C 61 -butyric acid methyl ester (PCBM) using alcohol-soluble titanium (diisopropoxide) bis (2,4-pentanedionate) (TIPD) as an electron selective layer between the indium tin oxide (ITO) electrode and the photoactive layer. The thermally annealed TIPD layer is highly transparent in the visible range and shows effective electron collection ability. By optimizing the electron-collecting layer, the photoactive layer and the hole-collecting layer, the power conversion efficiency (PCE) of the inverted device with the structure ITO/TIPD/P3HT : PCBM/MoO 3 /Ag reaches 4.10% under the illumination of AM1.5G, 100 mW cm -2 , which is among the highest values for inverted PSCs based on P3HT : PCBM. The PCE of the inverted device is improved in comparison with the conventional device (3.77%) under the same experimental conditions. (paper)

  14. Synthesis and characterization of polyacrylic acid- grafted-carboxylic graphene/titanium nanotube composite for the effective removal of enrofloxacin from aqueous solutions: Adsorption and photocatalytic degradation studies.

    Science.gov (United States)

    Anirudhan, Thayyath S; Shainy, F; Christa, J

    2017-02-15

    Polyacrylic acid-grafted-carboxylic graphene/titanium nanotube (PAA-g-CGR/TNT) composite was synthesized. It was effectively used as adsorbent as well as photocatalyst. The composite was characterized by FTIR, XRD, SEM, TEM, Surface Area Analyzer, XPS and DRS. The photocatalytic activity of PAA-g-CGR/TNT composite was evaluated on the basis of the degradation of pollutants by using sunlight. The band gap of the prepared photocatalyst was found to be 2.6eV. The removal of the antibiotic enrofloxacin (ENR) was achieved by two step mechanism based on adsorption and photodegradation. The maximum adsorption was observed at pH 5.0. The best fitted kinetic model was found to be pseudo-second-order. The maximum adsorption was observed at 30°C. The maximum adsorption capacity was found to be 13.40mg/g. The kinetics of photodegradation of ENR onto PAA-g-CGR/TNT composite follow first-order kinetics and optimum pH was found to be 5.0. The regeneration and reuse of the adsorbent-cum-photocatalyst were also examined upto five cycles. Copyright © 2016 Elsevier B.V. All rights reserved.

  15. modified bentonite clay for the removal of fluoride from aqueous ...

    African Journals Online (AJOL)

    NICOLAAS

    reagents and Total Ionic Solution Buffer (TISAB-III) were .... Equation 3 and it is used to describe liquid–solid phase adsorp- .... 0 and 1 indicating adsorption process was favourable at room temperature for all the adsorbate concentrations tested. 3.2.3. .... Marathe, Arsenic and fluoride contaminated groundwaters: a review.

  16. Adsorption of fluoride ions onto naturally occurring earth materials ...

    African Journals Online (AJOL)

    Batch sorption system using two naturally occurring earth materials (EM) as adsorbents was investigated to remove fluoride ions from aqueous solution. The system variables studied include initial concentration of the sorbate, agitation time, adsorbent dose, pH, co-ions and temperature. The experimental data fitted well to ...

  17. Ionometric determination of fluorides at low temperatures

    International Nuclear Information System (INIS)

    Kostyukova, I.S.; Ennan, A.A.; Dzerzhko, E.K.; Leivikova, A.A.

    1995-01-01

    A method for determining fluoride ions in solution at low temperatures using a solid-contact fluorine-selective electrode (FSE) has been developed. The effect of temperature (60 to -15 degrees C) on the calibration slope, potential equilibrium time, and operational stability is studied; the effect of an organic additive (cryoprotector) on the calibration slope is also studied. The temperature relationships obtained for the solid-contact FSEs allow appropriate corrections to be applied to the operational algorithm of the open-quotes Ftoringclose quotes hand-held semiautomatic HF gas analyzer for the operational temperature range of -16 to 60 degrees C

  18. FLUORIDE TOXICITY – A HARSH REALITY

    OpenAIRE

    Bandlapalli Pavani; Mandava Ragini; David Banji; Otilia J F Banji; N Gouri Pratusha

    2011-01-01

    There are many incidents of fluoride toxicity whether it is acute or chronic. Fluoride toxicity is an environmental hazard which arises from the upper layers of geological crust and is dissolved in water. Prolonged drinking of such water causes chronic fluoride toxicity. Use of fluoride containing compounds for various purposes such as dental products, metal, glass, refrigerator and chemical industries act as a source of fluoride poisoning and increase the risk of toxicity. This review reflec...

  19. Root caries prevention via sodium fluoride, chlorhexidine and silver diamine fluoride in vitro.

    Science.gov (United States)

    Göstemeyer, Gerd; Kohls, Anna; Paris, Sebastian; Schwendicke, Falk

    2018-01-31

    Uncertainty exists as to how to best prevent root caries development. The aim of the present study was to compare sodium fluoride (NaF), chlorhexidine (CHX) and silver diamine fluoride (SDF) varnishes (V) and rinses (R) regarding their caries preventive effect in an artificial caries biofilm model. 140 bovine root dentin samples were cut, polished and embedded. Samples were allocated to seven treatment groups (n = 20/group): Four varnishes (applied once prior biofilm challenge): 38% SDF (SDFV), 35% CHX-varnish (CHXV), 22,600 ppm NaF-varnish (NaFV), placebo-varnish (PV); two rinses (applied once daily during biofilm challenge): 500 ppm NaF solution (NaFR), 0.1% CHX solution (CHXR); one untreated group. Caries was induced in a multi-station, continuous-culture Lactobacillus rhamnosus GG (LGG) biofilm model. Bacteria were inoculated 1 × daily, while 2% sucrose was supplied 8 ×/day followed by artificial saliva for 10 min. After 12 days, mineral loss (ΔZ) was measured in the effect area and adjacent to the varnished areas. Bacterial counts were assessed on de-Man-Rogosa-Sharpe agar. ΔZ was significantly lower in the NaFR group compared with all other groups. Varnishes did not significantly prevent mineral loss in adjacent areas. None of the agents had a significant antimicrobial effect on LGG. Regular fluoride rinses showed highest root caries-preventive effect.

  20. Molten fluoride fuel salt chemistry

    International Nuclear Information System (INIS)

    Toth, L.M.; Del Cul, G.D.; Dai, S.; Metcalf, D.H.

    1995-01-01

    The chemistry of molten fluorides is traced from their development as fuels in the Molten Salt Reactor Experiment with important factors in their selection being discussed. Key chemical characteristics such as solubility, redox behavior, and chemical activity are explained as they relate to the behavior of molten fluoride fuel systems. Development requirements for fitting the current state of the chemistry to modern nuclear fuel system are described. It is concluded that while much is known about molten fluoride behavior which can be used effectively to reduce the amount of development required for future systems, some significant molten salt chemical questions must still be addressed. copyright American Institute of Physics 1995

  1. Strontium-90 fluoride data sheet

    Energy Technology Data Exchange (ETDEWEB)

    Fullam, H.T.

    1981-06-01

    This report is a compilation of available data and appropriate literature references on the properties of strontium-90 fluoride and nonradioactive strontium fluoride. The objective of the document is to compile in a single source pertinent data to assist potential users in the development, licensing, and use of /sup 90/SrF/sub 2/-fueled radioisotope heat sources for terrestrial power conversion and thermal applications. The report is an update of the Strontium-90 Fluoride Data Sheet (BNWL-2284) originally issued in April 1977.

  2. Morphological and Structural Analysis of Nano-hydroxyapatite (n-hap) Coatings Electrodeposited on Titanium Substrate : Effect of Deposition Solution Concentration

    International Nuclear Information System (INIS)

    Nik Norziehana Che Isa; Norjanah Yury; Yusairie Mohd

    2011-01-01

    Various concentration of deposition solutions containing CaCl 2 and NH 4 H 2 PO 4 (with Ca/P ratio equal to 1.67) were used to study the effect of deposition solution concentration on the surface morphology and structure of Hydroxyapatite (HAp) coatings. Each HAp coating was deposited onto Ti substrate by applying a constant potential of 1.5 V (vs Ag/ AgCl) at 80 degree Celsius. The formation of HAp coatings was confirmed by FTIR and XRD analyses. Various morphologies consisting of HAp nanoparticles were produced from different deposition solutions as observed by SEM. The concentration of deposition solution has significantly affected the morphology of n-HAp coatings. (author)

  3. Colorimetric determination of the fluoride ion - application to uranium metal and to uranous fluoride

    International Nuclear Information System (INIS)

    Hering, H.; Hure, J.; Legrand, S.

    1949-12-01

    In the determination described for fluoride in U metal, the U is brought into H 2 SO 4 solution by anodic oxidation, the fluo-silicic acid is distilled by entrainment in water vapor, and the F ion is determined in the distillate by using the fact that it complexes Zr and thus prevents the formation of the Zr-alizarin S lake. For F ion in UF 4 , the compound is dissolved in a Na 2 CO 3 -H 2 O 2 mixture, and F is determined in the solution by the colorimetric method described. (author)

  4. Coating NiTi archwires with diamond-like carbon films: reducing fluoride-induced corrosion and improving frictional properties.

    Science.gov (United States)

    Huang, S Y; Huang, J J; Kang, T; Diao, D F; Duan, Y Z

    2013-10-01

    This study aims to coat diamond-like carbon (DLC) films onto nickel-titanium (NiTi) orthodontic archwires. The film protects against fluoride-induced corrosion and will improve orthodontic friction. 'Mirror-confinement-type electron cyclotron resonance plasma sputtering' was utilized to deposit DLC films onto NiTi archwires. The influence of a fluoride-containing environment on the surface topography and the friction force between the brackets and archwires were investigated. The results confirmed the superior nature of the DLC coating, with less surface roughness variation for DLC-coated archwires after immersion in a high fluoride ion environment. Friction tests also showed that applying a DLC coating significantly decreased the fretting wear and the coefficient of friction, both in ambient air and artificial saliva. Thus, DLC coatings are recommended to reduce fluoride-induced corrosion and improve orthodontic friction.

  5. The precipitation of double fluoride salts of uranium

    Energy Technology Data Exchange (ETDEWEB)

    Muir, C. W.A.

    1963-02-15

    Bench-scale kinetic tests were conducted to study the reduction and precipitation reactions involved in the preparation of ammonium uranous fluoride from high-purity uranyl nitrate solutions. Sulphur dioxide and formic acid were used to form the active reducing agent, nascent hyposulphite ion. The reduction was affected in the presence of ammonium fluoride, resulting in the precipitation of the highly insoluble double salt. It was found that uranium was precipituted at a constant rate throughout the progress of the reaction. It is postulated that the reducing agent was continuously regenerated, and that this reaction was rate controlling. As a result of this study, a reaction mechanism is proposed. (auth)

  6. Profile of Fluoride Release from a Nanohybrid Composite Resin

    Directory of Open Access Journals (Sweden)

    Raquel Assed Bezerra Silva

    2015-02-01

    Full Text Available The aim of this study was to evaluate in vitro the amount and profile of fluoride release from a fluoride-containing nanohybrid composite resin (Tetric® N-Ceram by direct potentiometry. Thirty specimens (5 mm diameter x 3 mm high; n=10/material were made of Tetric® N-Ceram, Vitremer® resin-modified glass ionomer cement (RMGIC (positive control or Filtek® Z350 nanofill composite resin (negative control. The specimens were stored individually in plastic tubes containing 1 mL of artificial saliva at 37°C, which was daily renewed during 15 days. At each renewal of saliva, the amount of fluoride ions released in the solution was measured using a fluoride ion-selective electrode with ion analyzer, and the values obtained in mV were converted to ppm (µg/mL. Data were analyzed statistically by ANOVA and Tukey’s post-hoc test at a significance level of 5%. The results showed that the resins Tetric® N-Ceram and Filtek® Z350 did not release significant amounts of fluoride during the whole period of evaluation (p>0.05. Only Vitremer® released significant amounts of fluoride ions during the 15 days of the experiment, with greater release in first 2 days (p0.05. In conclusion, the nanohybrid composite resin Tetric® N-Ceram did not present in vitro fluoride-releasing capacity throughout the 15 days of study.

  7. In situ hydride formation in titanium during focused ion milling.

    Science.gov (United States)

    Ding, Rengen; Jones, Ian P

    2011-01-01

    It is well known that titanium and its alloys are sensitive to electrolytes and thus hydrides are commonly observed in electropolished foils. In this study, focused ion beam (FIB) milling was used to prepare thin foils of titanium and its alloys for transmission electron microscopy. The results show the following: (i) titanium hydrides were observed in pure titanium, (ii) the preparation of a bulk sample in water or acid solution resulted in the formation of more hydrides and (iii) FIB milling aids the precipitation of hydrides, but there were never any hydrides in Ti64 and Ti5553.

  8. Surface modification of porous titanium with rice husk as space holder

    Science.gov (United States)

    Wang, Xinsheng; Hou, Junjian; Liu, Yanpei

    2018-06-01

    Porous titanium was characterized after its surface modification by acid and alkali solution immersion. The results show that the acid surface treatment caused the emergence of flocculent sodium titanate and induced apatite formation. The surface modification of porous titanium promotes biological activation, and the application of porous titanium is also improved as an implant material because of the existence of C and Si.

  9. The effect of dynamic aging on the strain hardening rate of titanium

    International Nuclear Information System (INIS)

    Monteiro, S.N.; Reed-Hill, R.E.

    1974-01-01

    A study is made of the effect due to the interaction of solute atoms with mobile dislo cations, known as dynamic aging on the strain hardening characteristics of titanium between 150 and 477K. The results obtained with commercially pure titanium are compared with those obtained using high - purity titanium in order to evaluate the extent of effect [pt

  10. Fluoride removal performance of glass derived hydroxyapatite

    Energy Technology Data Exchange (ETDEWEB)

    Liang, Wen, E-mail: wliang@ecust.edu.cn [Research Institute of Biomaterials, School of Materials Science and Engineering, East China University of Science and Technology (China); Zhan, Lei; Piao, Longhua [Research Institute of Biomaterials, School of Materials Science and Engineering, East China University of Science and Technology (China); Russel, Christian [Otto-Schott-Institut, Universitaet Jena, Jena (Germany)

    2011-02-15

    Research highlights: {yields} Novel sodium calcium borate glass derived hydroxyapatite (G-HAP) is prepared. {yields} Micro-G-HAP adsorbs F{sup -} ions in solutions more effectively than commercial nano-HAP. {yields} The adsorption kinetics and isotherms are well fitted by a second order kinetic model and Freundlich isotherm model. -- Abstract: A novel sodium calcium borate glass derived hydroxyapatite (G-HAP) with different ranges of particle size was prepared by immersion sodium calcium borate glass in 0.1 M K{sub 2}HPO{sub 4} solution by the ratio of 50 g L{sup -1} for 7 days. The unique advantage of G-HAP for the adsorption of fluoride ions in solutions was studied. The effects of size and quantity of particles, pH value and adsorption time on adsorption performance were investigated. The maximum adsorption capacity was 17.34 mg g{sup -1} if 5 g L{sup -1}, <100 {mu}m G-HAP was added to a solution with an initial pH value of 6.72 and the adsorption time was 12 h. The results showed that the micro-G-HAP could immobilize F{sup -} in solution more effectively than commercial nano-HAP, which makes potential application of the G-HAP in removing the fluoride ions from wastewater. The adsorption kinetics and isotherms for F{sup -} could be well fitted by a second order kinetic model and Freundlich isotherm model respectively, which could be used to describe the adsorption behavior. The mechanism of G-HAP in immobilizing F{sup -} from aqueous solutions was investigated by the X-ray diffraction (XRD), infrared spectra (IR) and scanning electron microscopy (SEM).

  11. Fluoride ions sorption of the water using natural and modified hematite with aluminium hydroxide

    International Nuclear Information System (INIS)

    Teutli S, E. A.

    2011-01-01

    Fluorine is a mineral known for its dental benefits, but fluoride ions can cause fluoro sis in excessive quantities. There are many epidemiological studies on possible adverse effects resulting from prolonged ingestion of fluoride through drinking water. These studies demonstrate that fluoride mainly affects the bone tissue (bones and teeth), may produce an adverse effect on tooth enamel and can cause mild dental fluoro sis at concentrations from 0.9 to 1.2 mg/L in drinking water. In several states of Mexico, water contaminated with fluoride ions can be found, such as Aguascalientes, Chihuahua, Coahuila, Durango, Guanajuato, Sonora, Zacatecas, San Luis Potosi and Jalisco, where the fluoride ions levels are higher than 1.5 mg/L, established by the Mexican Official Standard (NOM-127-Ssa-2000) which sets the permissible limits of water for human use and consumption. Currently, several technologies have been proposed to remove fluoride ions from water such as precipitation methods which are based on the addition of chemicals to water and sorption methods to removed fluoride ions by sorption or ion exchange reactions by some suitable substrate capable of regenerate and reuse. In this work, the sorption of fluoride ions using unmodified and modified hematite with aluminum hydroxide to remove fluoride ions from water by bath experiments was studied. The hematite was modified by treating it with aluminum hydroxide, NaOH and Al 2 (SO 4 ) 3 solutions. The characterization of hematite before and after modification with aluminum hydroxide was studied by X-ray diffraction, scanning electron microscopy, EDS and Bet. The effect of ph, contact time, concentration of fluoride ions, and the dose of sorbent on the sorption of fluoride ions by the modified hematite were studied. Equilibrium was reached within 48 hours of contact time and the maximum sorption of fluoride ions were in the range pH eq between 2.3 and 6.2. Sorption capacities of fluoride ions as a function of dose of

  12. Beryllium production using beryllium fluoride

    International Nuclear Information System (INIS)

    Hubler, Carlos Henrique

    1993-01-01

    This work presents the beryllium production by thermal decomposition of the ammonium beryllium fluoride, followed by magnesium reduction, obtained in the small pilot plant of the Brazilian National Nuclear Energy Commission - Nuclear Engineering Institute

  13. Determination of fluoride in spices using microwave induced oxygen combustion

    Directory of Open Access Journals (Sweden)

    Emanuel Šucman

    2012-01-01

    Full Text Available Fluorine is essential in human and/or animal nutrition; therefore, so it is important to know its concentration in a diet. One of the possible sources of fluorine for humans is spice, containing various amounts of this trace element. This work describes the method for fluoride determination in various kinds ofspices using microwave-supported sample preparation in high pressure oxygen atmosphere followed by potentiometry with a fluoride ion-selective electrode. Parameters of the microwave device for combustion procedure were checked and optimized in order to find settings ensuring complete sample combustion and/or absorption of the analyte in the absorption solution. For the ion-selective electrode measurement, the technique of standard straight line was chosen. Concentrations of fluorides in spices and spice blends under investigation ranged from 3.15 mg·kg-1 to 26.08 mg·kg-1. In order to check the accuracy of the method Certified Reference Material Fluoride in Vegetation NIST 2695 was used and a good agreement between certified and found values was found. The precision expressed as the relative standard deviation ranged from 0.6% to 5.0%. The method is fast, accurate and reliable for this kind of analysis. In recent literature data on fluoride concentrations in spices and/or spice blends have not been found.

  14. Chronic Fluoride Toxicity: Dental Fluorosis

    OpenAIRE

    DenBesten, Pamela; Li, Wu

    2011-01-01

    Dental fluorosis occurs as a result of excess fluoride ingestion during tooth formation. Enamel fluorosis and primary dentin fluorosis can only occur when teeth are forming, and therefore fluoride exposure (as it relates to dental fluorosis) occurs during childhood. In the permanent dentition, this would begin with the lower incisors, which complete mineralization at approximately 2–3 years of age, and end after mineralization of the third molars. The white opaque appearance of fluorosed enam...

  15. Development of chitosan supported zirconium(IV) tungstophosphate composite for fluoride removal

    Energy Technology Data Exchange (ETDEWEB)

    Viswanathan, Natrayasamy, E-mail: natrayasamy_viswanathan@rediffmail.com [Department of Chemistry, Anna University Tiruchirappalli - Dindigul Campus, Dindigul 624622, Tamil Nadu (India); Meenakshi, S., E-mail: drs_meena@rediffmail.com [Department of Chemistry, Gandhigram Rural University, Gandhigram 624302, Tamil Nadu (India)

    2010-04-15

    A new biocomposite was prepared by incorporating inorganic ion exchanger namely zirconium(IV) tungstophosphate (ZrWP) into the chitosan biopolymeric matrix. The sorption behaviour of fluoride from aqueous solutions by this ZrWP/chitosan (ZrWPCs) composite has been investigated by batch technique. The fluoride sorption was studied as a function of contact time, pH, initial fluoride concentration, competing co-ions and temperature. The defluoridation capacity (DC) of the adsorbent was found to be 2025 mgF{sup -} kg{sup -1}. The composite was characterized using FTIR and SEM with EDAX analysis. The equilibrium sorption data were fitted to Freundlich and Langmuir isotherms. The kinetics of sorption was found to follow pseudo-second-order and intraparticle diffusion models. The values of thermodynamic parameters indicate the nature of sorption is spontaneous and endothermic. The biocomposite was successfully used for the removal of fluoride from the field water taken in a nearby fluoride endemic village.

  16. A calcite permeable reactive barrier for the remediation of Fluoride from spent potliner (SPL) contaminated groundwater

    DEFF Research Database (Denmark)

    Turner, B.D.; Binning, Philip John; Sloan, S.W.

    2008-01-01

    The use of calcite (CaCO3) as a substrate for a permeable reactive barrier (PRB) for removing fluoride from contaminated groundwater is proposed and is illustrated by application to groundwater contaminated by spent potliner leachate (SPL), a waste derived from the aluminium smelting process...... leachate indicate that the complex chemical matrix of the SPL leachate can impact fluoride removal significantly. For SPL contaminant mixtures, fluoride removal is initially less than expected from idealized, pure, solutions. However, with time, the effect of other contaminants on fluoride removal...... diminishes. Column tests also show that pH control is important for optimizing fluoride removal with the mass removed increasing with decreasing pH. Barrier pH can be regulated by CO2 addition with the point of injection being critical for optimising the remediation performance. Experimental and model...

  17. Hydroxyapatite electrodeposition on anodized titanium nanotubes for orthopedic applications

    Energy Technology Data Exchange (ETDEWEB)

    Parcharoen, Yardnapar [Department of Biological Engineering, Faculty of Engineering, King Mongkut' s University of Technology Thonburi, Bangkok (Thailand); Kajitvichyanukul, Puangrat [Center of Excellence on Environmental Research and Innovation, Faculty of Engineering, Naresuan University, Phitsanulok (Thailand); Sirivisoot, Sirinrath [Department of Biological Engineering, Faculty of Engineering, King Mongkut' s University of Technology Thonburi, Bangkok (Thailand); Termsuksawad, Preecha, E-mail: preecha.ter@kmutt.ac.th [Division of Materials Technology, School of Energy, Environment and Materials, King Mongkut' s University of Technology Thonburi, 126 Pracha Uthit Rd., Bang Mod, ThungKhru, Bangkok 10140 (Thailand)

    2014-08-30

    Highlights: • We found that different anodization time of titanium significantly effects on nanotube length which further impacts adhesion strength of hydroxyapatite coating layers. • Adhesion strength of Hydroxyapatite (HA) coated on titanium dioxide nanotubes is better than that of HA coated on titanium plate. • Hydroxyapatite coated on titanium dioxide nanotubes showed higher cell density and better spreading of MC3T3-E1 cells (bone-forming cells) than that coated on titanium plate surface. - Abstract: Nanotubes modification for orthopedic implants has shown interesting biological performances (such as improving cell adhesion, cell differentiation, and enhancing osseointegration). The purpose of this study is to investigate effect of titanium dioxide (TiO{sub 2}) nanotube feature on performance of hydroxyapatite-coated titanium (Ti) bone implants. TiO{sub 2} nanotubes were prepared by anodization using ammonium fluoride electrolyte (NH{sub 4}F) with and without modifiers (PEG400 and Glycerol) at various potential forms, and times. After anodization, the nanotubes were subsequently annealed. TiO{sub 2} nanotubes were characterized by scanning electron microscope and X-ray diffractometer. The amorphous to anatase transformation due to annealing was observed. Smooth and highly organized TiO{sub 2} nanotubes were found when high viscous electrolyte, NH{sub 4}F in glycerol, was used. Negative voltage (−4 V) during anodization was confirmed to increase nanotube thickness. Length of the TiO{sub 2} nanotubes was significantly increased by times. The TiO{sub 2} nanotube was electrodeposited with hydroxyapatite (HA) and its adhesion was estimated by adhesive tape test. The result showed that nanotubes with the tube length of 560 nm showed excellent adhesion. The coated HA were tested for biological test by live/dead cell straining. HA coated on TiO{sub 2} nanotubes showed higher cells density, higher live cells, and more spreading of MC3T3-E1 cells than that

  18. Matrix supported tailored polymer for solid phase extraction of fluoride from variety of aqueous streams

    International Nuclear Information System (INIS)

    Thakur, Neha; Kumar, Sanjukta A.; Wagh, D.N.; Das, Sadananda; Pandey, Ashok K.; Kumar, Sangita D.; Reddy, A.V.R.

    2012-01-01

    Highlights: ► Th complexed with poly (bis[2-(methacryloyloxy)-ethyl]phosphate) as tailored polymer membranes. ► Membranes offered high capacity and selectivity for fluoride in aqueous media. ► Quantitative uptake (80 ± 5%) of fluoride. ► Fast sorption kinetics. ► Reusability of polymer membranes. - Abstract: Fluoride related health hazards (fluorosis) are a major environmental problem in many regions of the world. It affects teeth; skeleton and its accumulation over a long period can lead to changes in the DNA structure. It is thus absolutely essential to bring down the fluoride levels to acceptable limits. Here, we present a new inorganic–organic hybrid polymer sorbent having tailored fixed-sites for fluoride sorption. The matrix supported poly (bis[2-(methacryloyloxy)-ethyl]phosphate) was prepared by photo-initiator induced graft-polymerization in fibrous and microporous (sheet) host poly(propylene) substrates. These substrates were conditioned for selective fluoride sorption by forming thorium complex with phosphate groups on bis[2-methacryloyloxy)-ethyl] phosphate (MEP). These tailored sorbents were studied for their selectivity towards fluoride in aqueous media having different chemical conditions. The fibrous sorbent was found to take up fluoride with a faster rate (15 min for ≈76% sorption) than the sheet sorbent. But, the fluoride loading capacity of sheet sorbent (4320 mg kg −1 ), was higher than fibrous and any other sorbent reported in the literature so far. The sorbent developed in the present work was found to be reusable after desorption of fluoride using NaOH solution. It was tested for solid phase extraction of fluoride from natural water samples.

  19. Fluoride in groundwater: toxicological exposure and remedies.

    Science.gov (United States)

    Jha, S K; Singh, R K; Damodaran, T; Mishra, V K; Sharma, D K; Rai, Deepak

    2013-01-01

    Fluoride is a chemical element that is found most frequently in groundwater and has become one of the most important toxicological environmental hazards globally. The occurrence of fluoride in groundwater is due to weathering and leaching of fluoride-bearing minerals from rocks and sediments. Fluoride when ingested in small quantities (dental health by reducing dental caries, whereas higher concentrations (>1.5 mg/L) may cause fluorosis. It is estimated that about 200 million people, from among 25 nations the world over, may suffer from fluorosis and the causes have been ascribed to fluoride contamination in groundwater including India. High fluoride occurrence in groundwaters is expected from sodium bicarbonate-type water, which is calcium deficient. The alkalinity of water also helps in mobilizing fluoride from fluorite (CaF2). Fluoride exposure in humans is related to (1) fluoride concentration in drinking water, (2) duration of consumption, and (3) climate of the area. In hotter climates where water consumption is greater, exposure doses of fluoride need to be modified based on mean fluoride intake. Various cost-effective and simple procedures for water defluoridation techniques are already known, but the benefits of such techniques have not reached the rural affected population due to limitations. Therefore, there is a need to develop workable strategies to provide fluoride-safe drinking water to rural communities. The study investigated the geochemistry and occurrence of fluoride and its contamination in groundwater, human exposure, various adverse health effects, and possible remedial measures from fluoride toxicity effects.

  20. Release of titanium ions from an implant surface and their effect on cytokine production related to alveolar bone resorption

    International Nuclear Information System (INIS)

    Wachi, Takanori; Shuto, Takahiro; Shinohara, Yoshinori; Matono, Yoshinari; Makihira, Seicho

    2015-01-01

    Although interest in peri-implant mucositis and peri-implantitis has recently been increasing, the mechanisms driving these diseases remain unknown. Here, the effects of titanium ions on the inflammation and bone resorption around an implant were investigated. First, the accumulated amount of Ti ions released into gingival and bone tissues from an implant exposed to sodium fluoride solution was measured using inductively coupled plasma mass spectrometry. Next, the cellular responses in gingival and bone tissues to Ti ions and/or Porphyromonas gingivalis-lipopolysaccharide (P. gingivalis-LPS) were assessed using a rat model. More Ti ions were detected in the gingival tissues around an implant after treatment with sodium fluoride (pH 4.2) than in its absence, which suggests that the fluoride corroded the implant surface under salivary buffering capacity. The injection of Ti ions (9 ppm) significantly increased the mRNA expression and protein accumulation of chemokine (C–C motif) ligand 2, as well as the ratio of receptor activator of nuclear factor-κB ligand to osteoprotegerin, in rat gingival tissues exposed to P. gingivalis-LPS in a synergistic manner. In addition, the enhanced localization of toll-like receptor 4, which is an LPS receptor, was observed in gingival epithelium loaded with Ti ions (9 ppm). These data suggest that Ti ions may be partly responsible for the infiltration of monocytes and osteoclast differentiation by increasing the sensitivity of gingival epithelial cells to microorganisms in the oral cavity. Therefore, Ti ions may be involved in the deteriorating effects of peri-implant mucositis, which can develop into peri-implantitis accompanied by alveolar bone resorption

  1. Short term serum pharmacokinetics of diammine silver fluoride after oral application.

    Science.gov (United States)

    Vasquez, Elsa; Zegarra, Graciela; Chirinos, Edgar; Castillo, Jorge L; Taves, Donald R; Watson, Gene E; Dills, Russell; Mancl, Lloyd L; Milgrom, Peter

    2012-12-31

    There is growing interest in the use of diammine silver fluoride (DSF) as a topical agent to treat dentin hypersensitivity and dental caries as gauged by increasing published research from many parts of the world. While DSF has been available in various formulations for many years, most of its pharmacokinetic aspects within the therapeutic concentration range have never been fully characterized. This preliminary study determined the applied doses (3 teeth treated), maximum serum concentrations, and time to maximum serum concentration for fluoride and silver in 6 adults over 4 h. Fluoride was determined using the indirect diffusion method with a fluoride selective electrode, and silver was determined using inductively coupled plasma-mass spectrometry. The mean amount of DSF solution applied to the 3 teeth was 7.57 mg (6.04 μL). Over the 4 hour observation period, the mean maximum serum concentrations were 1.86 μmol/L for fluoride and 206 nmol/L for silver. These maximums were reached 3.0 h and 2.5 h for fluoride and silver, respectively. Fluoride exposure was below the U.S. Environmental Protection Agency (EPA) oral reference dose. Silver exposure exceeded the EPA oral reference dose for cumulative daily exposure over a lifetime, but for occasional use was well below concentrations associated with toxicity. This preliminary study suggests that serum concentrations of fluoride and silver after topical application of DSF should pose little toxicity risk when used in adults. NCT01664871.

  2. Effect of phosphate/fluoride electrolytes on mass and dimensional stability of anodization bath manufactured by FDM

    Directory of Open Access Journals (Sweden)

    Strnad Gabriela

    2017-01-01

    Full Text Available Present paper is an experimental study on mass and dimensional stability of components manufactured by additive technology of Fused Deposition Modeling (FDM from PLA and ABS filaments, components to be subjected to the action of aqueous phosphate/fluoride solutions during the process of surface modification and TiO2 nanotubes development on the surface of titanium based materials by electrochemical anodization. Several specimens were printed with 30% and 100% fill density; we used control samples of PP, PLA and ABS in order to compare the results. The specimens and control samples were in contact with 1M H3PO4 + 0.5 wt% HF electrolyte, for 2 hours and 48 hours. Regarding mass stability we found that the specimens’ mass is increasing after exposure to electrolyte, showing absorption on to the material, the mass gain being up to 0.2% from initial mass. Dimensional stability is also questionable; there are modifications of up to 0.05 mm after 48 hours exposure to electrolyte. All of our results lead to the conclusion that, even if FDM has certain advantages in terms of flexibility of design and short design to product time, drawbacks appear in terms of mass and dimensional stability when the printed components work in aqueous acid solutions, raising questions regarding their safe utilization over time.

  3. Chronic fluoride toxicity: dental fluorosis.

    Science.gov (United States)

    Denbesten, Pamela; Li, Wu

    2011-01-01

    Dental fluorosis occurs as a result of excess fluoride ingestion during tooth formation. Enamel fluorosis and primary dentin fluorosis can only occur when teeth are forming, and therefore fluoride exposure (as it relates to dental fluorosis) occurs during childhood. In the permanent dentition, this would begin with the lower incisors, which complete mineralization at approximately 2-3 years of age, and end after mineralization of the third molars. The white opaque appearance of fluorosed enamel is caused by a hypomineralized enamel subsurface. With more severe dental fluorosis, pitting and a loss of the enamel surface occurs, leading to secondary staining (appearing as a brown color). Many of the changes caused by fluoride are related to cell/matrix interactions as the teeth are forming. At the early maturation stage, the relative quantity of amelogenin protein is increased in fluorosed enamel in a dose-related manner. This appears to result from a delay in the removal of amelogenins as the enamel matures. In vitro, when fluoride is incorporated into the mineral, more protein binds to the forming mineral, and protein removal by proteinases is delayed. This suggests that altered protein/mineral interactions are in part responsible for retention of amelogenins and the resultant hypomineralization that occurs in fluorosed enamel. Fluoride also appears to enhance mineral precipitation in forming teeth, resulting in hypermineralized bands of enamel, which are then followed by hypomineralized bands. Enhanced mineral precipitation with local increases in matrix acidity may affect maturation stage ameloblast modulation, potentially explaining the dose-related decrease in cycles of ameloblast modulation from ruffle-ended to smooth-ended cells that occur with fluoride exposure in rodents. Specific cellular effects of fluoride have been implicated, but more research is needed to determine which of these changes are relevant to the formation of fluorosed teeth. As further

  4. Organoboron compounds as Lewis acid receptors of fluoride ions in polymeric membranes.

    Science.gov (United States)

    Jańczyk, Martyna; Adamczyk-Woźniak, Agnieszka; Sporzyński, Andrzej; Wróblewski, Wojciech

    2012-07-06

    Newly synthesized organoboron compounds - 4-octyloxyphenylboronic acid (OPBA) and pinacol ester of 2,4,6-trifluorophenylboronic acid (PE-PBA) - were applied as Lewis acid receptors of fluoride anions. Despite enhanced selectivity, the polymer membrane electrodes containing the lipophilic receptor OPBA exhibited non-Nernstian slopes of the responses toward fluoride ions in acidic conditions. Such behavior was explained by the lability of the B-O bond in the boronic acids, and the OH(-)/F(-) exchange at higher fluoride content in the sample solution. In consequence, the stoichiometry of the OPBA-fluoride complexes in the membrane could vary during the calibration, changing the equilibrium concentration of the primary anion in membrane and providing super-Nernstian responses. The proposed mechanism was supported by (19)F NMR studies, which indicated that the fluoride complexation proceeds more effectively in acidic solution leading mainly to PhBF(3)(-) species. Finally, the performances of the membranes based on the phenylboronic acid pinacol ester, with a more stable B-O bond, were tested. As it was expected, Nernstian fluoride responses were recorded for such membranes with worsened fluoride selectivity. Copyright © 2012 Elsevier B.V. All rights reserved.

  5. Weakening of thickness dependence of J{sub C} in YBa{sub 2}Cu{sub 3}O{sub 7-δ} films using a titanium-added MOD precursor solution

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, H.L., E-mail: zhanghuiliang@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); School of Science, Hebei University of Engineering, Handan 056038 (China); Ding, F.Z., E-mail: dingfazhu@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Gu, H.W., E-mail: guhw@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Dong, Z.B. [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Qu, F.; Zhang, H.; Shang, H.J. [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China)

    2017-04-15

    Highlights: • The thickness dependence of J{sub C} in YBCO film was weakened by introducing BaTiO{sub 3} nanoparticles into YBCO matrix. • The high I{sub C} value of 430 MA/cm-width was obtained in the BaTiO{sub 3}-doped YBCO film prepared by the MOD method. • The YBCO composite thick film prepared by using the precursor solution with polyethyleneglycol shows a compact and smooth surface. - Abstract: BaTiO{sub 3} (BTO)-doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) films were prepared by the metal-organic deposition method using a precursor solution with titanium ion. These YBCO films were deposited on (00l)-oriented LaAlO{sub 3} single-crystal substrates using an automated dip coater. The thickness dependence of critical current density (J{sub C}) in the BTO-doped YBCO films was investigated. The J{sub C} value of the YBCO composite film was reduced from 6.3 to 4.6 MA/cm{sup 2} with increasing film thickness from 450 to 930 nm in self-filed at 77 K, which arose mainly from degradation of texture and roughening of the film. However, relative to undoped YBCO thick films, J{sub C} values of the YBCO composite thick films were greatly improved, and more importantly, the reduction in J{sub C} with increasing film thickness was hindered, especially in a high magnetic field. This result indicated that the introduction of BTO nanoparticles as pinning centers into YBCO matrix weakened the thickness dependence of J{sub C}.

  6. Sealing glasses for titanium and titanium alloys

    Science.gov (United States)

    Brow, Richard K.; McCollister, Howard L.; Phifer, Carol C.; Day, Delbert E.

    1997-01-01

    Barium lanthanoborate sealing-glass compositions are provided comprising various combinations (in terms of mole-%) of boron oxide (B.sub.2 O.sub.3), barium oxide (BaO), lanthanum oxide (La.sub.2 O.sub.3), and at least one other oxide selected from the group consisting of aluminum oxide (Al.sub.2 O.sub.3), calcium oxide (CaO), lithium oxide (Li.sub.2 O), sodium oxide (Na.sub.2 O), silicon dioxide (SiO.sub.2), or titanium dioxide (TiO.sub.2). These sealing-glass compositions are useful for forming hermetic glass-to-metal seals with titanium and titanium alloys having an improved aqueous durability and favorable sealing characteristics. Examples of the sealing-glass compositions are provided having coefficients of thermal expansion about that of titanium or titanium alloys, and with sealing temperatures less than about 900.degree. C., and generally about 700.degree.-800.degree. C. The barium lanthanoborate sealing-glass compositions are useful for components and devices requiring prolonged exposure to moisture or water, and for implanted biomedical devices (e.g. batteries, pacemakers, defibrillators, pumps).

  7. Repercussion of noni mouthwash on surface characterization of Nickel-Titanium archwire

    Directory of Open Access Journals (Sweden)

    Dhivya Dilipkumar

    2017-01-01

    Full Text Available Objective: Maintaining oral hygiene is very important during orthodontic therapy mouthwashes are prescribed as an adjunct to improve patient's oral hygiene. Commercially available mouthwashes e.g. Chlorhexidine, Listerine, fluoride containing mouthwashes have shown to alter the surface characteristics of orthodontic wires. Hence the purpose of the study was to evaluate the effect of Noni mouthwash on surface quality and compositional changes of Nickel Titanium orthodontic wires. Materials and Methods: In this in vitro study pre-formed 0.014 inch NiTi arch wire was used. The study comprised of two samples, one control and one test sample which were 25mm in length. Control sample was stored at room temperature without any manipulation while test sample was immersed in Noni mouthwash solution for 1.5 hours, after which the test specimen was removed from the mouthwash solution and rinsed with distilled water. Both control and test samples were sent for scanning electron microscopy analysis, to qualitatively characterize the topography of the wire surface. Electron dispersion spectrum analysis was done to evaluate the various components of both the wires. Results: No significant difference in the average surface roughness for both wire samples was observed. There was no significant difference seen in the composition of wire after immersion in Noni mouthwash. Conclusion: Noni mouthwash did not have significant influence on the surface roughness or altered the composition of the Ni-Ti wire. Hence Noni mouthwash may be prescribed as a natural, non-destructive prophylactic agent for orthodontic patients.

  8. Wear properties of Ti-13Zr-13Nb (wt.%) near β titanium alloy containing 0.5 wt.% boron in dry condition, Hank's solution and bovine serum

    International Nuclear Information System (INIS)

    Majumdar, P.; Singh, S.B.; Chakraborty, M.

    2010-01-01

    The effect of heat treatment on the microstructure, hardness and sliding wear behaviour of Ti-13Zr-13Nb (wt.%) containing 0.5 wt.% B (TZNB) has been studied and compared with that of Ti-13Zr-13Nb (wt.%) (TZN) alloy. The wear properties were tested in dry condition and in simulated body fluid (Hank's solution and bovine serum) to understand the effect of different medium on wear behaviour of the TZNB alloy. Depending on the heat treatment condition the microstructure of the alloy consisted of α/martensite and TiB in β matrix. In general, the hardness of all the heat treated samples varied in a narrow range and in most of the cases addition of boron to the TZN alloy decreased the hardness. Almost all cases, no significant variation of the wear rate in dry condition with heat treatment was observed. Compared with the wear rate in dry condition, the wear rate in Hank's solution of the all the TZNB samples increased substantially. Moreover, the wear was found to be most severe in bovine serum. Addition of boron to TZN alloy did not result in any improvement in the wear resistance in all the media studied.

  9. Fluoride level in saliva after bonding orthodontic brackets with a fluoride containing adhesive

    NARCIS (Netherlands)

    Ogaard, B; Arends, J; Helseth, H; Dijkman, G; vanderKuijl, M

    The fluoride level in saliva is considered an important parameter in caries prevention. Elevation of the salivary fluoride level by a fluoride-releasing orthodontic bonding adhesive would most likely be beneficial in the prevention of enamel caries. In this study, the fluoride level in saliva was

  10. Urinary fluoride excretion in preschool children after intake of fluoridated milk and use of fluoride-containing toothpaste

    DEFF Research Database (Denmark)

    Norman, M; Twetman, S; Hultgren Talvilahti, A

    2017-01-01

    Objective: To assess the urinary fluoride excretion in preschool children after drinking fluoridated milk with 0.185 mg F and 0.375 mg F and to study the impact of use of fluoride toothpaste. Basic research design: Double-blind cross-over study. Participants: Nine healthy children, 2.5-4.5 years...

  11. Production and use of carrier-free 18F in studies on the effect of trace amounts of fluoride on the metabolism of the oral cariogenic bacterium Streptococcus mutans

    International Nuclear Information System (INIS)

    Psarros, N.; Duschner, H.

    1988-01-01

    The utilization of carrier-free ionic 18 F is a convenient method for studying the effects of very low extracellular fluoride concentrations on the metabolism of the cariogenic bacterium Streptococcus mutans. A method was developed for the preparation of carrier-free aqueous solutions of ionic 18 F with high specific activity (about 70 7 Bq/ml). Fluoride distribution and fluoride binding experiments show that submicromolar fluoride concentrations had a negative effect on the metabolism of Streptococcus mutans. (author) 10 refs

  12. Water Fluoridation Reporting System (Public Water Systems)

    Data.gov (United States)

    U.S. Department of Health & Human Services — The Water Fluoridation Reporting System (WFRS) has been developed to provide tools to assist states in managing fluoridation programs. WFRS is designed to track all...

  13. ADSORPTIVE REMOVAL OF FLUORIDE FROM WATER USING ...

    African Journals Online (AJOL)

    Preferred Customer

    Currently available treatment methods for removal of excess fluoride from water are broadly divided into three ... the application of nanoparticles as sorbents for fluoride removal. Sundaram [26] studied the ... Characterization of adsorbent.

  14. A rapid method for the determination on fluoride in geological samples

    International Nuclear Information System (INIS)

    Josephson, M.; Cook, E.B.T.; Dixon, K.

    1977-01-01

    An account is given of a rapid procedure for the determination by use of the specific-ion electrode of fluoride in geological samples. The sample is fused with sodium hydroxide in a nickel crucible in a muffle furnace. The melt is leached with water, a buffer solution of ammonium citrate is added, and the fluoride activity is measured with a specific-ion electrode. All operations are carried out in the crucible, making possible approximately 100 determinations a day. The precision of the method is approximately 10 per cent at a fluoride concentration of 500 p.p.m., which is acceptable for geological-survey work [af

  15. Determination of fluoride ions in water by condutometric titration with lanthanum nitrates

    International Nuclear Information System (INIS)

    Alves, J.C.

    1986-01-01

    An alternative method for determining fluoride ions in drinking water by condutometric titration using La(NO 3 ) 3 as titrant is presented. The method is based on previous separation of fluoride from sample by distillation at 135 0 C. The pH of the distillated is adjusted between 5,5 - 6,0; ethanol is adicioned in 50% titrating the resultant solution with La(NO 3 ) 3 . In these conditions, fluoride ions are determined with accuracy respectively, 5% and 4%. Natural samples of drinking water were analysed by this method and by the ion selective method, with agreement among the results. (author) [pt

  16. Classification of titanium dioxide

    International Nuclear Information System (INIS)

    Macias B, L.R.; Garcia C, R.M.; Maya M, M.E.; Ita T, A. De; Palacios G, J.

    2002-01-01

    In this work the X-ray diffraction (XRD), Scanning Electron Microscopy (Sem) and the X-ray Dispersive Energy Spectroscopy techniques are used with the purpose to achieve a complete identification of phases and mixture of phases of a crystalline material as titanium dioxide. The problem for solving consists of being able to distinguish a sample of titanium dioxide being different than a titanium dioxide pigment. A standard sample of titanium dioxide with NIST certificate is used, which indicates a purity of 99.74% for the TiO 2 . The following way is recommended to proceed: a)To make an analysis by means of X-ray diffraction technique to the sample of titanium dioxide pigment and on the standard of titanium dioxide waiting not find differences. b) To make a chemical analysis by the X-ray Dispersive Energy Spectroscopy via in a microscope, taking advantage of the high vacuum since it is oxygen which is analysed and if it is concluded that the aluminium oxide appears in a greater proportion to 1% it is established that is a titanium dioxide pigment, but if it is lesser then it will be only titanium dioxide. This type of analysis is an application of the nuclear techniques useful for the tariff classification of merchandise which is considered as of difficult recognition. (Author)

  17. No Calcium-Fluoride-Like Deposits Detected in Plaque Shortly after a Sodium Fluoride Mouthrinse

    OpenAIRE

    Vogel, G.L.; Tenuta, L.M.A.; Schumacher, G.E.; Chow, L.C.

    2010-01-01

    Plaque ‘calcium-fluoride-like’ (CaF2-like) and fluoride deposits held by biological/bacterial calcium fluoride (Ca-F) bonds appear to be the source of cariostatic concentrations of fluoride in plaque fluid. The aim of this study was to quantify the amounts of plaque fluoride held in these reservoirs after a sodium fluoride rinse. 30 and 60 min after a 228 μg/g fluoride rinse, plaque samples were collected from 11 volunteers. Each sample was homogenized, split into 2 aliquots (aliquots 1 and 2...

  18. Acute toxicity of uranium hexafluoride, uranyl fluoride and hydrogen fluoride

    International Nuclear Information System (INIS)

    Just, R.A.

    1988-01-01

    Uranium hexafluoride (UF 6 ) released into the atmosphere will react rapidly with moisture in the air to form the hydrolysis products uranyl fluoride (UO 2 F 2 ) and hydrogen fluoride (HF). Uranium compounds such as UF 6 and UO 2 F 2 exhibit both chemical toxicity and radiological effects, while HF exhibits only chemical toxicity. This paper describes the development of a methodology for assessing the human health consequences of a known acute exposure to a mixture of UF 6 , UO 2 F 2 , and HF. 4 refs., 2 figs., 5 tabs

  19. The efficacy of amine fluoride/stannous fluoride in the suppression of morning breath odour.

    Science.gov (United States)

    Quirynen, Marc; Avontroodt, Pieter; Soers, Catherine; Zhao, Hong; Pauwels, Martine; Coucke, Wim; van Steenberghe, Daniel

    2002-10-01

    Breath odour is a complaint encountered worldwide, often linked to microbial overload in the oral cavity. This double blind, crossover, randomised study assessed the efficacy of several antiseptic mouthrinses or slurry vs. a control solution in the prevention of morning bad breath during an experimental period of 7 days without mechanical plaque control. Sixteen dental students with a healthy periodontium abolished, after a thorough professional cleaning, all means of mechanical plaque control during five experimental periods of 7 days, interleaved by washout periods of at least 3 weeks. During each experimental period, as the only oral hygiene measure, the students rinsed twice a day with one of the following formulations (in a randomised order): a 0.2% chlorhexidine-alcohol mouthrinse (CHX-Alc), a 0.05% CHX + 0.05% cetylpyridinium chloride + 0.14% zinc lactate mouthrinse (CHX-CPC-Zn), an amine fluoride/stannous fluoride (125 ppm F-/125 ppm F-) containing mouthrinse (AmF/SnF2Mr), a slurry of a tooth paste (AmF/SnF2Sl) containing amine fluoride (350 ppm F-) and stannous fluoride (1050 ppm F-) and a placebo solution (placebo). At days 0, 3 and 7, morning breath was scored via VSC level measurements of the mouth air, and organoleptic ratings of the mouth air and tongue coating. At the same visits both the degree of gingival inflammation and the de novo plaque formation were rated. At the end of each period a questionnaire for subjective ratings was completed and microbiological samples were taken from the tongue dorsum, the saliva and the supragingival plaque for anaerobic and aerobic culturing. Although oral hygiene during the experimental periods was limited to rinsing, bad breath parameters systematically improved (P bacterial load (aerobic & anaerobic) in the saliva (>or= 0.5 log reduction with a superiority (P bacterial load on the tongue dorsum could only be detected for the CHX-Alc solution (0.5 log). The antibacterial effect of the placebo solution and the

  20. Comparison of Antibacterial Effect of Fluoride and Chlorhexidine on Two Cariogenic Bacteria: An in Vitro Study

    Directory of Open Access Journals (Sweden)

    Poureslami HR

    2014-09-01

    Full Text Available Statement of problem: Dental plaque is the main source for dental caries and there is no proper vaccine that can affect dental plaques. Objectives: Daily use of an efficient anti-plaque product can be very beneficial in plaque control and, thus, prevention of caries. This study aims to evaluate the antibacterial effects of four products of Chlorhexidine and Fluoride on two types of cariogenic bacteria. Materials and Methods: In this in vitro study, the antibacterial effect of Chlorhexidine and Fluoride (gel and solution against Streptococci Sanguis and Sobrinus was evaluated. Chlorhexidine gluconate 1% gel (Corosodyl, France, Chlorhexidine gluconate 2% solution (Consepsis, Ultradent, US, Sodium fluoride 0.2% solution (Oral-B, US and Acidulated Phosphate Fluoride 1.23% gel ( Denti-Care, Canada were used. The disc diffusion method was used for testing bacterial sensitivity. The data were analyzed using paired t-test and Chi-square test. Results: In comparison with the negative control, each of the four gels and solutions showed antibacterial effects but the effects were not statistically significant for fluoride solution (P=0.217. For S. Sobrinus, the mean diameter of inhibition zone around the discs coated with fluoride gel (F g, fluoride solution (F s, Chlorhexidine gel (CHX g and Chlorhexidine solution (CHX s were 19, 9, 21.5 and 27.5mm, respectively. For S. Sanguis, the mean diameter of inhibition zone around the discs coated with F g, F s, CHX g and CHX s were 17, 11, 17 and 25mm, respectively. CHX s had the most effect on both bacteria and F s had the least. CHX g and F g were less effective than CHX s, respectively. Conclusion: The results demonstrated that 2% CHX s and 1.23% F g can be effective on inhibition of the growth of some of cariogenic bacteria. Therefore, these agents can be used in the prevention of Early Childhood Caries.

  1. Effect of Fluoride Mouthrinse and Toothpaste on Number of Streptococcal Colony Forming Units of Dental Plaque

    Directory of Open Access Journals (Sweden)

    SE Jabbarifar

    2005-11-01

    Full Text Available Background: Frequent topical fluoride therapy through toothpaste, mouthrinse, professional gels and solutions causes decrease in incidence, pause and repair of dental caries in the enamel. These mechanisms are done through penetration of fluoride ions (F- and their replacement with hydroxyl ions (OH- of hydroxyappatite of enamel, interfere with microbial metabolism of dental plaque and bacteriostatic effect on some cariogenic bacterial strains such as streptococci. The aim of this study was to examine the effect of fluoride mouthrinse and toothpaste on the number of streptococcal colony forming units of dental plaque. Methods: 62 children with 6-7 years old were put in two groups. Samples of dental plaque from each group were collected both before and after use of the fluoride mouthrinse and or toothpaste. The samples were cultured on blood agar to find the number of streptococcal colony forming units (CFU. The mean colony forming unit was compared inter and intra groups before and after application of Fluoride products. Results: The streptococcal CFU of dental plaque before and after use of the mouthrinse and toothpaste respectively was (1240±1367, 1253±1341.5 and (551±716, 898±1151. Statistically, the streptococcal CFU in each group before and after use of the toothpaste and mouthrinse was significantly different. Conclusion: The findings of this study indicated that the fluoride toothpaste and mouthrinse reduce number of streptococcal colony forming units of dental plaque. Also this reduction was not depended on level of (F- Ions, sort of vehicle of fluoride and frequent application of the fluoride mouthrinse and toothpaste. Keywords: fluoride mouthrinse, fluoride toothpaste, colony forming unit (CFU, streptococcus

  2. Phase equilibria and thermodynamic studies in the titanium-nickel and titanium-nickel-oxygen systems

    International Nuclear Information System (INIS)

    Chattopadhyay, G.; Kleykamp, H.; Laumer, W.

    1983-01-01

    The isothermal section of the Ti-Ni-O system was examined at 1200 K in the regions between the Ni(Ti) solid solution and the binary oxides of titanium. The relative partial Gibbs energies of oxygen over the Ti 2 O 3 -Ti 3 O 5 region and of titanium in the Ni(Ti) solid solution as well as the Gibbs energies of formation of NiTiO 3 , Ti 3 O 5 and TiNi 3 were determined between 1100 and 1300 K by use of solid electrolyte galvanic cells. (orig.) [de

  3. Effects of fluorides on plants

    Energy Technology Data Exchange (ETDEWEB)

    Yamazoe, F

    1975-11-01

    Fluorine compounds known to be air pollutants, such as hydrogen fluoride and silicon tetrachloride, are highly poisonous to plants even at ppm - ppb levels. As solid microparticles, acidic sodium fluoride and cryolite cause problems by adhering to plant leaves and absorbing into plant bodies. Plants are classified by their susceptibility to hydrogen fluoride: gladiolus, apricot, buckwheat, turnip and Vaccinium vitis-idaea are most susceptible showing slight injury at less than 5 ppb for 7-9 days; maize, pepper, and dahlia are fairly susceptible, followed by azalea, rose, lilac, and alfalfa, then by oak and tomato. Gladiolus is used as an indicator plant. The exposure factor for one species was known. The symptoms of plants exposed to gaseous fluorine compounds are described in detail at various concentrations. The causal mechanism of the injuries due to fluorine compounds is described in detail, with the method of determining the fluorine content of plant parts. 7 references.

  4. Photosynthesis of ammonium uranous fluoride

    International Nuclear Information System (INIS)

    El-Fekey, S.A.; Zaki, M.R.; Farah, M.Y.

    1975-01-01

    This study pertains to utilisation of solar energy for ethanol photosynthesis of ammonium uranous fluoride, that satisfies nuclear specifications needed for calcio- or magnesiothermy. Insolation in autumn using 4-10% ethanol in 5-20 g uranium/litre at initial pH 3.25 gave practically 99.8% yield in two hours, independant of 1.0 to 2.0 stoichiometric NH 4 F. With ultraviolet light, the yield varied between 30 and 60%, even after four hours irradiation. Stirring and heating to 60 0 C raised the tap density of the dried double fluorides from 1.48 at 30 0 C, to 1.85 g/cm 3 at 60 0 C. The texture increased also in fineness to 100% 50μ aggregates. The powders satisfy nuclear purity specifications. Thermograms indicated preferential decomposition of double fluoride at 375 0 C in controlled atmosphere to obtain nuclear pure anhydrous uranium tetrafluoride

  5. Anhydrous hydrogen fluoride electrolyte battery. [Patent application

    Science.gov (United States)

    Not Available

    1972-06-26

    It is an object of the invention to provide a primary cell or battery using ammonium fluoride--anhydrous hydrogen fluoride electrolyte having improved current and power production capabilities at low temperatures. It is operable at temperatures substantially above the boiling point of hydrogen fluoride. (GRA)

  6. Electrowinning molten titanium from titanium dioxide

    CSIR Research Space (South Africa)

    Van Vuuren, DS

    2005-10-01

    Full Text Available the Manufacturing and Materials Industry in it quest for global competitiveness CSIR Manufacturing and Materials Technology 3 Rationale – Titanium Cost Build-up Material Cost Ilmenite $0.27/kg Ti sponge Titanium slag $0.75/kg Ti Sponge TiCl4 and TiO2 $3....10/kg Ti Sponge Ti Sponge raw materials costs $5.50/kg Ti Sponge Total Ti Sponge cost $9-$11/kg Ti Sponge Ti ingot $15-17/kg Ti Aluminium $1.7/kg Al Supporting the Manufacturing and Materials Industry in its quest for global competitivenessorting...

  7. Effect of Fluoride Mouthrinse and Toothpaste on Number of Streptococcal Colony Forming Units of Dental Plaque

    OpenAIRE

    SE Jabbarifar; SA Tabibian; F Poursina

    2005-01-01

    Background: Frequent topical fluoride therapy through toothpaste, mouthrinse, professional gels and solutions causes decrease in incidence, pause and repair of dental caries in the enamel. These mechanisms are done through penetration of fluoride ions (F-) and their replacement with hydroxyl ions (OH-) of hydroxyappatite of enamel, interfere with microbial metabolism of dental plaque and bacteriostatic effect on some cariogenic bacterial strains such as streptococci. The aim of this study was...

  8. SBIR-Long fluoride fiber

    Science.gov (United States)

    Jaeger, Raymond E.; Vacha, Lubos J.

    1987-08-01

    This report summarizes results obtained under a program aimed at developing new techniques for fabricating long lengths of heavy metal fluoride glass (HMFG) optical fiber. A new method for overcladding conventional HMFG preforms with a low melting oxide glass was developed, and improvements in the rotational casting method were made to increase preform length. The resulting composite glass canes consist of a fluoride glass overcoat layer to enhance strength and chemical durability. To show feasibility, prototype optical fiber preforms up to 1.6 cm in diameter with lengths of 22 cm were fabricated. These were drawn into optical fibers with lengths up to 900 meters.

  9. Conductance Studies on Complex Formation between c-Methylcalix[4]resorcinarene and Titanium (III in Acetonitrile-H2O Binary Solutions

    Directory of Open Access Journals (Sweden)

    Naghmeh Saadati

    2013-09-01

    Full Text Available Calixresorcinarenes have proved to be unique molecules for molecular recognition via hydrogen bonding, hydrophobic and ionic interactions with suitable substrates such as cations. The study of the interactions involved in the complexation of different cations with calixresorcinarenes in solvent mixtures is important for a better understanding of the mechanism of biological transport, molecular recognition, and other analytical applications. This article summarizes different aspects of the complexes of the Ti3+ metal cation with c-methylcalix[4]resorcinarene (CMCR as studied by conductometry in acetonitrile (AN–water (H2O binary mixtures at different temperatures. Conductance data show that the metal cation/ligand (ML stoichiometry of the complexes in solution is 1:1 in all cases. Non-linear behaviour was observed for the variation of logKf of the complexes vs. the composition of the binary solvent mixtures. Selectivity of CMCR for the Ti3+ cation is sensitive to solvent composition; in some cases and at certain compositions of the mixed solvent systems, the selectivity order is changed. Values of thermodynamic parameters (, for formation of the CMCR–Ti3+ complexes in AN–H2O binary systems were obtained from the temperature dependence of stability constants, and the results show that the thermodynamics of complexation reactions are affected by the nature and composition of the mixed solvents.

  10. Silver diamine fluoride: a caries "silver-fluoride bullet".

    Science.gov (United States)

    Rosenblatt, A; Stamford, T C M; Niederman, R

    2009-02-01

    The antimicrobial use of silver compounds pivots on the 100-year-old application of silver nitrate, silver foil, and silver sutures for the prevention and treatment of ocular, surgical, and dental infections. Ag(+) kills pathogenic organisms at concentrations of linings, water purification systems, hospital gowns, and caries prevention. To distill the current best evidence relative to caries, this systematic review asked: Will silver diamine fluoride (SDF) more effectively prevent caries than fluoride varnish? A five-database search, reference review, and hand search identified 99 human clinical trials in three languages published between 1966 and 2006. Dual review for controlled clinical trials with the patient as the unit of observation, and excluding cross-sectional, animal, in vitro studies, and opinions, identified 2 studies meeting the inclusion criteria. The trials indicated that SDF's lowest prevented fractions for caries arrest and caries prevention were 96.1% and 70.3%, respectively. In contrast, fluoride varnish's highest prevented fractions for caries arrest and caries prevention were 21.3% and 55.7%, respectively. Similarly, SDF's highest numbers needed to treat for caries arrest and caries prevention were 0.8 (95% CI=0.5-1.0) and 0.9 (95% CI=0.4-1.1), respectively. For fluoride varnish, the lowest numbers needed to treat for caries arrest and prevention were 3.7 (95% CI=3.4-3.9) and 1.1 (95% CI=0.7-1.4), respectively. Adverse events were monitored, with no significant differences between control and experimental groups. These promising results suggest that SDF is more effective than fluoride varnish, and may be a valuable caries-preventive intervention. As well, the availability of a safe, effective, efficient, and equitable caries-preventive agent appears to meet the criteria of both the WHO Millennium Goals and the US Institute of Medicine's criteria for 21st century medical care.

  11. Accumulation of fluoride by plants and vegetables

    International Nuclear Information System (INIS)

    Njenga, L.W.; Kariuki, D.N.

    1994-01-01

    Fluoride in plant and vegetable samples has been determined using ion selective electrode. The analysis was carried out after ashing the sample on an open flame, adding perchloric acid and allowing the hydrogen fluoride to diffuse into sodium hydroxide layer.The results obtained show that kale and pumpkins can accumulate more than ten times their normal values of fluoride while plants were found to accumulate upto 100μg/g fluoride when exposed to highlevels of fluoride in water or soil. (author)

  12. Toxic effects of fluoride on organisms.

    Science.gov (United States)

    Zuo, Huan; Chen, Liang; Kong, Ming; Qiu, Lipeng; Lü, Peng; Wu, Peng; Yang, Yanhua; Chen, Keping

    2018-04-01

    Accumulation of excess fluoride in the environment poses serious health risks to plants, animals, and humans. This endangers human health, affects organism growth and development, and negatively impacts the food chain, thereby affecting ecological balance. In recent years, numerous studies focused on the molecular mechanisms associated with fluoride toxicity. These studies have demonstrated that fluoride can induce oxidative stress, regulate intracellular redox homeostasis, and lead to mitochondrial damage, endoplasmic reticulum stress and alter gene expression. This paper reviews the present research on the potential adverse effects of overdose fluoride on various organisms and aims to improve our understanding of fluoride toxicity. Copyright © 2018 Elsevier Inc. All rights reserved.

  13. Chitosan patterning on titanium alloys

    OpenAIRE

    Gilabert Chirivella, Eduardo; Pérez Feito, Ricardo; Ribeiro, Clarisse; Ribeiro, Sylvie; Correia, Daniela; González Martin, María Luisa; Manero Planella, José María; Lanceros Méndez, Senentxu; Gallego Ferrer, Gloria; Gómez Ribelles, José Luis

    2017-01-01

    Titanium and its alloys are widely used in medical implants because of their excellent properties. However, bacterial infection is a frequent cause of titanium-based implant failure and also compromises its osseointegration. In this study, we report a new simple method of providing titanium surfaces with antibacterial properties by alternating antibacterial chitosan domains with titanium domains in the micrometric scale. Surface microgrooves were etched on pure titanium disks at i...

  14. Production of titanium tetrachloride

    International Nuclear Information System (INIS)

    Perillo, P.M.; Botbol, O.

    1990-01-01

    This report presents a summary of results from theoperation of a laboratory scale for the production in batches of approximately 100 gs of titanium tetrachloride by chlorination with chloroform and carbon tetrachloride between 340 deg C and 540 deg C. Chlorination agent vapors were passed through a quartz column reacting with titanium oxide powder agglomerated in little spheres. Obtained titanium tetrachloride was condensed in a condenser, taken in a ballon and then purified by fractional distillation. Optimun temperature for chloroform was 400 deg C with 74 % yield and for carbon tetrachloride was 500 deg C with 69 % yield. (Author) [es

  15. Modified zirconium-eriochrome cyanine R determination of fluoride

    Science.gov (United States)

    Thatcher, L.L.

    1957-01-01

    The Eriochrome Cyanine R method for determining fluoride in natural water has been modified to provide a single, stable reagent solution, eliminate interference from oxidizing agents, extend the concentration range to 3 p.p.m., and extend the phosphate tolerance. Temperature effect was minimized; sulfate error was eliminated by precipitation. The procedure is sufficiently tolerant to interferences found in natural and polluted waters to permit the elimination of prior distillation for most samples. The method has been applied to 500 samples.

  16. Influence of Surfactants and Fluoride against Enamel Erosion.

    Science.gov (United States)

    Zanatta, Rayssa Ferreira; Ávila, Daniele Mara da Silva; Miyamoto, Karen Mayumi; Torres, Carlos Rocha Gomes; Borges, Alessandra Bühler

    2018-06-06

    This study investigated the effect of surfactants associated with sodium fluoride (NaF) on enamel erosion prevention, using an erosion-remineralization in vitro model. Sodium lauryl sulfate (SLS), polysorbate 20 (P20), and cocoamidopropyl betaine (CAPB) were tested, at concentrations of 1.0 and 1.5%, and associated or not with NaF (275 ppm). The control groups were distilled water and the NaF solution. Bovine enamel samples (n = 12) were prepared and submitted to a 5-day cycling model: acid challenge (0.3% citric acid, pH 2.6, 4×/day), human saliva (2 h, 4×/day), and the treatment solutions (2 min, 2×/day). The protective potential of the agents against initial erosion was assessed by microhardness and the surface loss by profilometry. Enamel surface wettability was determined by goniometry, protein adsorption was measured by spectroscopy (FTIR), and the KOH-soluble fluoride was quantified. Goniometry showed that SLS and CAPB increased enamel wettability. No differences were found among the surfactants regarding protein adsorption. Microhardness showed that SLS reduced NaF protection. P20 (1 and 1.5%) and CAPB 1.5% presented a protective effect, but lower than the NaF solution. Profilometry showed that CAPB protected enamel, but no agent associated with NaF promoted a higher protection than the NaF solution alone. KOH-soluble fluoride analysis showed that all surfactants reduced the fluoride adsorption on the enamel surface. Therefore, the surfactants tested (except for P20) changed the enamel surface energy. The SLS decreased the protective potential of NaF on initial erosion, but no tested agent interfered with the protective effect of NaF on enamel erosive wear. © 2018 S. Karger AG, Basel.

  17. Extraction of fluoride metal complexes by octanols

    International Nuclear Information System (INIS)

    Baklanova, I.V.; Nikolaev, A.I.; Il'in, E.G.; Majorov, V.G.

    2005-01-01

    The extraction of niobium(V) and tantalum(V) by octanols, including 1-octanol, 2-octanol, and iso-octanol (2-ethylhexanol), was studied. The composition of the octanols and their solubility in various aqueous solutions were evaluated. The capacity of the octanols for tantalum(V) and niobium(V), the extraction properties of the octanols, the viscosity of extracts under conditions of metal fluoride extraction, and the temperature dependence of the viscosity of the octanols were studied. The composition of the extracted complexes was studied by IR and NMR spectroscopy and chemical analysis, and the hydration-solvation mechanism of the extraction of tantalum(V) and niobium(V) was supported [ru

  18. Method of converting uranium fluoride to intermediate product for uranium oxide manufacture with recycling or reusing valuable materials

    International Nuclear Information System (INIS)

    Baran, V.; Moltasova, J.

    1982-01-01

    Uranium fluoride is acted upon by water with nitrate containing a cation capable of binding fluoride ions. The uranium is extracted, for instance, with tributyl phosphate with the generated organic phase containing the prevalent proportion of uranium and representing the required intermediate product and the aqueous phase from which is isolated the fluorine component which may be used within the fuel cycle. The nitrate component of the aqueous phase is recycled following treatment. It is also possible to act on uranium fluoride directly with an aqueous solution. Here the cations of nitrate form with the fluorides soluble nondissociated complexes and reduce the concentration of free fluoride ions. The nitrate +s mostly used in an amount corresponding to its solubility in the system prior to the introduction of UF 6 . The uranium from the solution with the reduced concentration of free fluoride ions is extracted into the reaction system under such conditions as to make the prevalent majority of fluorides and an amount of uranium smaller than 5x10 -2 mol/l remain in the aqueous phase and that such an amount of fluorides should remain in the organic phase which is smaller than corresponds to the fluorine/uranium molar ratio in the organic phase. Uranium contained in the organic phase is processed into uranium oxide, with advantage into UO 2 . From the isolated compounds of fluorine and the cation of the nitrate gaseous HF is released which is used either inside or outside of the fuel cycle. (J.P.)

  19. Quaternary ammonium promoted ultra selective and sensitive fluorescence detection of fluoride ion in water and living cells.

    Science.gov (United States)

    Li, Long; Ji, Yuzhuo; Tang, Xinjing

    2014-10-21

    Highly selective and sensitive fluorescent probes with a quaternary ammonium moiety have been rationally designed and developed for fast and sensitive fluorescence detection of fluoride ion (F(-) from NaF, not TBAF) in aqueous solution and living cells. With the sequestration effect of quaternary ammonium, the detection time was less than 2 min and the detection limit of fluoride ion was as low as 0.57 ppm that is among the lowest detection limits in aqueous solutions of many fluoride fluorescence probes in the literature.

  20. Effectivity of fluoride treatment on hydrogen and corrosion product generation in temporal implants for different magnesium alloys.

    Science.gov (United States)

    Trinidad, Javier; Arruebarrena, Gurutze; Marco, Iñigo; Hurtado, Iñaki; Sáenz de Argandoña, Eneko

    2013-12-01

    The increasing interest on magnesium alloys relies on their biocompatibility, bioabsorbility and especially on their mechanical properties. Due to these characteristics, magnesium alloys are becoming a promising solution to be used, as temporary implants. However, magnesium alloys must overcome their poor corrosion resistance. This article analyses the corrosion behaviour in phosphate-buffered saline solution of three commercial magnesium alloys (AZ31B, WE43 and ZM21) as well as the influence of fluoride treatment on their corrosion behaviour. It is shown that the corrosion rate of all the alloys is decreased by fluoride treatment. However, fluoride treatment affects each alloy differently.

  1. Alimentary fluoride intake in preschool children

    Directory of Open Access Journals (Sweden)

    Lencova Erika

    2011-10-01

    Full Text Available Abstract Background The knowledge of background alimentary fluoride intake in preschool children is of utmost importance for introducing optimal and safe caries preventive measures for both individuals and communities. The aim of this study was to assess the daily fluoride intake analyzing duplicate samples of food and beverages. An attempt was made to calculate the daily intake of fluoride from food and swallowed toothpaste. Methods Daily alimentary fluoride intake was measured in a group of 36 children with an average age of 4.75 years and an average weight of 20.69 kg at baseline, by means of a double plate method. This was repeated after six months. Parents recorded their child's diet over 24 hours and collected duplicated portions of food and beverages received by children during this period. Pooled samples of food and beverages were weighed and solid food samples were homogenized. Fluoride was quantitatively extracted from solid food samples by a microdiffusion method using hexadecyldisiloxane and perchloric acid. The content of fluoride extracted from solid food samples, as well as fluoride in beverages, was measured potentiometrically by means of a fluoride ion selective electrode. Results Average daily fluoride intake at baseline was 0.389 (SD 0.054 mg per day. Six months later it was 0.378 (SD 0.084 mg per day which represents 0.020 (SD 0.010 and 0.018 (SD 0.008 mg of fluoride respectively calculated per kg bw/day. When adding the values of unwanted fluoride intake from the toothpaste shown in the literature (0.17-1.21 mg per day the estimate of the total daily intake of fluoride amounted to 0.554-1.594 mg/day and recalculated to the child's body weight to 0.027-0.077 mg/kg bw/day. Conclusions In the children studied, observed daily fluoride intake reached the threshold for safe fluoride intake. When adding the potential fluoride intake from swallowed toothpaste, alimentary intake reached the optimum range for daily fluoride intake

  2. Electroplating on titanium alloy

    Science.gov (United States)

    Lowery, J. R.

    1971-01-01

    Activation process forms adherent electrodeposits of copper, nickel, and chromium on titanium alloy. Good adhesion of electroplated deposits is obtained by using acetic-hydrofluoric acid anodic activation process.

  3. Lithium1.3Aluminum0.3Titanium1.7Phosphate as a solid state Li-ion conductor: Issues with microcracking and stability in aqueous solutions

    Science.gov (United States)

    Jackman, Spencer D.

    Lithium aluminum titanium phosphate (LATP) with formula Li1.3Al0.3Ti1.7(PO4)3 was analyzed and tested to better understand its applicability as a solid state ion conducting ceramic material for electrochemical applications. Sintered samples were obtained from Ceramatec, Inc. in Salt Lake City and characterized in terms of density, phase-purity, fracture toughness, Young's modulus, thermal expansion behavior, mechanical strength, a.c. and d.c. ionic conductivity, and susceptibility to static and electrochemical corrosion in aqueous Li salt solutions. It was shown that LATP is prone to microcrack generation because of high thermal expansion anisotropy. A.c. impedance spectra of high-purity LATP of varying grain sizes showed that microcracking had a negative impact on the ionic conduction of Li along grain boundaries, with fine-grained (1.7±0.7 µm) LATP having twice the ionic conductivity of the same purity of coarse-grained (4.8±1.9 µm) LATP at 50°C. LATP with detectible secondary phases had lower ionic conductivity for similar grain sizes, as would be expected. The Young's modulus of fine-grained LATP was measured to be 115 GPa, and the highest biaxial strength was 191±11 MPa when tested in mineral oil, 144±13 MPa as measured in air, and 26±7 MPa after exposure to deionized water, suggesting that LATP undergoes stress-corrosion cracking. After exposure to LiOH, the strength was 76±19 MPa. This decrease in strength was observed despite there being no measureable change in a.c. impedance spectra, X-ray diffraction, or sample mass, suggesting phosphate glasses at grain boundaries. The chemical and electrochemical stability of high-purity LATP in aqueous electrochemical cells was evaluated using LiOH, LiCl, LiNO3, and LiCOOCH3 salts as the Li source. LATP was found to be most stable between pH 8-9, with the longest cell operating continuously at 25 mA cm-2 for 625 hours at 40°C in LiCOOCH3. At pH values outside of the 7-10 range, eventual membrane degradation

  4. Titanium oxide fever

    International Nuclear Information System (INIS)

    De Jonge, D.; Visser, J.

    2012-01-01

    One measure to improve air quality is to apply photo-catalytic substances that capture NOx onto the road surface or onto baffle boards alongside the roads. The effect of titanium oxide containing clinkers with coating was discussed in the report 'Demonstration project of air-purifying pavement in Hengelo, The Netherlands' that was published in May 2011. This article examines the way in which the effectiveness of this study was determined. Can titanium oxide containing clinkers and coatings indeed capture NOx?. [nl

  5. Effect of topical applications of neutral sodium fluoride on dental careis in the rat.

    Science.gov (United States)

    Poulsen, S; Larson, R H

    1975-01-01

    A study on various regimens by which the same total amount of neutral sodium fluoride is applied to the teeth of rats showed that greater effects were observed after frequent application of 0.2% solutions than after less frequent application of more concentrated solutions.

  6. Vanadium and titanium determination by resorcinalhydrazide of salicylic acid

    Energy Technology Data Exchange (ETDEWEB)

    Karpova, O I; Pilipenko, A T; Lukachina, V V [AN Ukrainskoj SSR, Kiev. Inst. Kolloidnoj Khimii i Khimii Vody

    1979-02-01

    The complexing of titanium and vanadium with resorcinalhydrazyl of salicylic acid (RHSA) in water-organic media is studied. Titanium (4) forms a complex at pH 0.8-1.8, vanadium - at pH 2.5-5.6, and at pH 7.6-9.8. The complexes are well extracted by polar and nonpolar solvents from acid solutions. The techniques are developed for the determination of titanium and vanadium by the RHSA agent in nickel alloys.

  7. Study polymeric membranes PVDF/TiO2 photocatalytic applications with synthesized by solution blow spinning

    International Nuclear Information System (INIS)

    Gimenes, T.C.; Pereira, E.A.; Montanhera, M.A.; Paula, F.R. de; Spada, E.R.

    2016-01-01

    In this study we obtained nanofibers titanium dioxide (TiO2) incorporated into the poly (vinylidene fluoride) - PVDF in different concentrations, using a new technique denominated Solution Blow Spinning. This technique has the merits of simplicity, low cost and high efficiency in the production of nanofibers, compared with the technique of Electrospinning, using pressurized gas instead of high voltage, is not limited to the dielectric constant of the material and provides a processing period of at least 100 times faster. The obtained nanofibers exhibit little account and a very smooth morphology, with diameters ranging from 400 to 700 nm and with presence of crystalline anatase phase. The tests showed photocatalytic degradation of Rhodamine B dye, being more degradation shown by the PVDF nanofibers containing 0,7 g of TiO 2 , approximately 75 % of degraded dye. However nanofibers obtained the PVDF/TiO2 applications of this material are numerous, as filters, conductive nanofibers, photocatalysis and sensors. (author)

  8. Dentifrice fluoride and abrasivity interplay on artificial caries lesions.

    Science.gov (United States)

    Nassar, Hani M; Lippert, Frank; Eckert, George J; Hara, Anderson T

    2014-01-01

    Incipient caries lesions on smooth surfaces may be subjected to toothbrushing, potentially leading to remineralization and/or abrasive wear. The interplay of dentifrice abrasivity and fluoride on this process is largely unknown and was investigated on three artificially created lesions with different mineral content/distribution. 120 bovine enamel specimens were randomly allocated to 12 groups (n = 10), resulting from the association of (1) lesion type [methylcellulose acid gel (MeC); carboxymethylcellulose solution (CMC); hydroxyethylcellulose gel (HEC)], (2) slurry abrasive level [low (REA 4/ RDA 69); high (REA 7/RDA 208)], and (3) fluoride concentration [0/275 ppm (14.5 mM) F as NaF]. After lesion creation, specimens were brushed in an automated brushing machine with the test slurries (50 strokes 2×/day). Specimens were kept in artificial saliva in between brushings and overnight. Enamel surface loss (SL) was determined by optical profilometry after lesion creation, 1, 3 and 5 days. Two enamel sections (from baseline and post-brushing areas) were obtained and analyzed microradiographically. Data were analyzed by analysis of variance and Tukey's tests (α = 5%). Brushing with high-abrasive slurry caused more SL than brushing with low-abrasive slurry. For MeC and CMC lesions, fluoride had a protective effect on SL from day 3 on. Furthermore, for MeC and CMC, there was a significant mineral gain in the remaining lesions except when brushed with high-abrasive slurries and 0 ppm F. For HEC, a significant mineral gain took place when low-abrasive slurry was used with fluoride. The tested lesions responded differently to the toothbrushing procedures. Both slurry fluoride content and abrasivity directly impacted SL and mineral gain of enamel caries lesions.

  9. Eukaryotic resistance to fluoride toxicity mediated by a widespread family of fluoride export proteins.

    Science.gov (United States)

    Li, Sanshu; Smith, Kathryn D; Davis, Jared H; Gordon, Patricia B; Breaker, Ronald R; Strobel, Scott A

    2013-11-19

    Fluorine is an abundant element and is toxic to organisms from bacteria to humans, but the mechanisms by which eukaryotes resist fluoride toxicity are unknown. The Escherichia coli gene crcB was recently shown to be regulated by a fluoride-responsive riboswitch, implicating it in fluoride response. There are >8,000 crcB homologs across all domains of life, indicating that it has an important role in biology. Here we demonstrate that eukaryotic homologs [renamed FEX (fluoride exporter)] function in fluoride export. FEX KOs in three eukaryotic model organisms, Neurospora crassa, Saccharomyces cerevisiae, and Candida albicans, are highly sensitized to fluoride (>200-fold) but not to other halides. Some of these KO strains are unable to grow in fluoride concentrations found in tap water. Using the radioactive isotope of fluoride, (18)F, we developed an assay to measure the intracellular fluoride concentration and show that the FEX deletion strains accumulate fluoride in excess of the external concentration, providing direct evidence of FEX function in fluoride efflux. In addition, they are more sensitive to lower pH in the presence of fluoride. These results demonstrate that eukaryotic FEX genes encode a previously unrecognized class of fluoride exporter necessary for survival in standard environmental conditions.

  10. Peroxy-Titanium Complex-based inks for low temperature compliant anatase thin films.

    Science.gov (United States)

    Shabanov, N S; Asvarov, A Sh; Chiolerio, A; Rabadanov, K Sh; Isaev, A B; Orudzhev, F F; Makhmudov, S Sh

    2017-07-15

    Stable highly crystalline titanium dioxide colloids are of paramount importance for the establishment of a solution-processable library of materials that could help in bringing the advantages of digital printing to the world of photocatalysis and solar energy conversion. Nano-sized titanium dioxide in the anatase phase was synthesized by means of hydrothermal methods and treated with hydrogen peroxide to form Peroxy-Titanium Complexes (PTCs). The influence of hydrogen peroxide on the structural, optical and rheological properties of titanium dioxide and its colloidal solutions were assessed and a practical demonstration of a low temperature compliant digitally printed anatase thin film given. Copyright © 2017 Elsevier Inc. All rights reserved.

  11. An In-Vitro Study on the Release of Fluoride from Two Restorative Materials and Their Rechargeability after Exposure to Daily 1000 ppm Fluoride

    Directory of Open Access Journals (Sweden)

    A. Kowsari

    2005-09-01

    Full Text Available Statement of Problem: Since the fluoride releases from materials with the property of releasing fluoride are decreasing gradually, it seems that probably the material rechargeability is more important than their long-term fluoride release.Purpose: the objective of this study was to asses the fluoride release and rechargeability of 2 types of fluoride releasing restorative materials, a resin modified glass ionomer(Vitremer and a compomer (Compoglass F, after exposure to daily NaF solutionscontaining 1000 ppm F, for 1 minute.Materials and Methods: Twelve discs ( 8 mm ×2 mm of each of the materials were fabricated, and divided into 2 groups (test and control. All discs were stored in 4 mL artificial saliva at 37°C. In group 1 (N=6, the specimens were immersed in artificialsaliva which was changed daily for 25 days. In group 2 (N=6, in addition to receiving the same treatment as group 1, the specimens were immersed in NaF solution (1000ppm F, ph=6.9 for 1 minute before daily saliva change. A potentiometer was used to determine the amount of fluoride released on days 1, 2, 3, 5, 10, 15, 20 and 25, after the daily saliva change, in all study groups. Data were analyzed by the t-student test after confirmation of the equality of variances by Leven’s test.Results: Both materials continued releasing fluoride throughout the whole study period. For each material, the release was highest on day one. During the first 3 days,glass ionomer released significantly higher amounts of fluoride as compared to compomer (p0.05. After exposure to NaF solution, none of the materials showed statistically significant rechargeability (p>0.05 and the amount of fluoride-releasecontinued to drop during the study period in similar patterns for both the test and the control groups.Conclusion: It may be concluded that rechargeability of glass ionomer and compomer,using daily neutral fluoride mouth rinses and toothpastes does not occur in reliable amounts.

  12. Rapid detection of fluoride in potable water using a novel fluorogenic compound 7-O-tert-butyldiphenylsilyl-4-methylcoumarin

    Directory of Open Access Journals (Sweden)

    Ravi Chavali

    2015-12-01

    Full Text Available In the present work, we have synthesized a new water soluble colorless chemical compound 7-O-tert-butyldiphenylsilyl-4-methylcoumarin (TBDPSC that releases fluorescent molecules imparting blue fluorescence to the solution, upon interaction with fluoride ions in water. The blue fluorescence can be visualized using simple hand held ultraviolet (UV lamps. TBDPSC has excellent sensitivity and selectivity towards fluoride and our results indicate that fluoride concentrations as low as 0.2 mg/L can be accurately detected within a few seconds. Fluoride testing with TBDPSC is simple and rapid compared to the conventional methodologies without the requirement of trained personnel. Hence, the present fluoride detection method can be easily field deployable and particularly useful for monitoring water quality in limited resource communities.

  13. Physical and chemical characterization of titanium-alginate samples for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Morani, L.M.; Ribeiro, A.A.; Oliveira, M.V. de; Dantas, F.M.L., E-mail: marize.varella@int.gov.b [Instituto Nacional de Tecnologia (INT), Rio de Janeiro, RJ (Brazil); Leao, M.H.M.R. [Universidade Federal do Rio de Janeiro (EQ/UFRJ), RJ (Brazil). Escola de Quimica

    2010-07-01

    The sol-gel technique combined with powder metallurgy may be an alternative to produce titanium parts for bioengineering, with the advantage of eliminating the powder compaction step, which may introduce defects. The present work introduces a system consisted of titanium powder and sodium alginate suspension, which undergoes reticulation in contact with a calcium salt solution, obtaining titanium/calcium alginate hydrogel with granule morphology. The characterization of the raw materials and granules of calcium alginate and titanium/calcium alginate was performed by x-ray fluorescence spectroscopy and thermogravimetric analysis. The granules topography was analyzed by scanning electron microscopy/EDS. Titanium and sodium alginate chemical composition were adequate for use as raw materials, showing that the methodology used is suitable for processing titanium samples for further consolidation by sintering, in order to produce titanium parts. (author)

  14. Titanium zirconium and hafnium coordination compounds with vanillin thiosemicarbazone

    International Nuclear Information System (INIS)

    Konunova, Ts.B.; Kudritskaya, S.A.

    1987-01-01

    Coordination compounds of titanium zirconium and hafnium tetrachlorides with vanillin thiosemicarbazone of MCl 4 x nLig composition, where n=1.5, 4 for titanium and 1, 2, 4 for zirconium and hafnium, are synthesized. Molar conductivity of ethanol solutions is measured; IR spectroscopic and thermochemical investigation are carried out. The supposition about ligand coordination via sulfur and azomethine nitrogen atoms is made. In all cases hafnium forms stable compounds than zirconium

  15. Mechanism of cesium sorption on potassium titanium hexacyanoferrate

    International Nuclear Information System (INIS)

    Sun Yongxia; Xu Shiping; Song Chongli

    1998-01-01

    The mechanism of cesium sorption on potassium titanium hexacyanoferrate is described. The dependence of the sorption speed on temperature, particle granule size, and the stirring speed is studied. The results show that the sorption process is controlled by liquid film diffusion and particle diffusion. An exchange reaction occurs mainly between K + in the exchanger and Cs + in the solution, i.e. potassium titanium hexacyanoferrate, and Cs + of simulated high-level liquid waste

  16. Groundwater fluoride contamination: A reappraisal

    Directory of Open Access Journals (Sweden)

    Amlan Banerjee

    2015-03-01

    Full Text Available Dissolution of fluorite (CaF2 and/or fluorapatite (FAP [Ca5(PO43F], pulled by calcite precipitation, is thought to be the dominant mechanism responsible for groundwater fluoride (F− contamination. Here, one dimensional reactive–transport models are developed to test this mechanism using the published dissolution and precipitation rate kinetics for the mineral pair FAP and calcite. Simulation results correctly show positive correlation between the aqueous concentrations of F− and CO32− and negative correlation between F− and Ca2+. Results also show that precipitation of calcite, contrary to the present understanding, slows down the FAP dissolution by 106 orders of magnitude compared to the FAP dissolution by hydrolysis. For appreciable amount of fluoride contamination rock–water interaction time must be long and of order 106 years.

  17. Effects of hydrogen fluoride on plants

    Energy Technology Data Exchange (ETDEWEB)

    Yamazoe, F

    1970-07-15

    Symptoms of fluorosis in plants are chlorotic markings around the tip or edges of young leaves. Examples of damage to plants and livestock by fluorides are listed, including the retarded growth of silkworms fed on mulberry leaves polluted by more than 30 ppm fluorides. Plants can be classified into six groups according to their resistance to hydrogen fluoride. Threshold values of the fluoride concentration range from 5-10 ppb for the plants. Gladiolus is normally employed as a plant indicator for hydrogen fluoride and silkworms as indicator insects. The relationship between plant damage by fluorides and exposure time, density, soil, fertilizer, meteorology and location are examined. Several preventive measures are listed, including the spraying of water or lime on plant leaves. It is concluded that the establishment of an environmental standard is difficult because of the extremely high sensitivity of the plants to the gas. 8 references.

  18. Thermodynamic data for uranium fluorides

    International Nuclear Information System (INIS)

    Leitnaker, J.M.

    1983-03-01

    Self-consistent thermodynamic data have been tabulated for uranium fluorides between UF 4 and UF 6 , including UF 4 (solid and gas), U 4 F 17 (solid), U 2 F 9 (solid), UF 5 (solid and gas), U 2 F 10 (gas), and UF 6 (solid, liquid, and gas). Included are thermal function - the heat capacity, enthalpy, and free energy function, heats of formation, and vaporization behavior

  19. Titanium(IV), zirconium, hafnium and thorium

    International Nuclear Information System (INIS)

    Brown, Paul L.; Ekberg, Christian

    2016-01-01

    Titanium can exist in solution in a number of oxidation states. The titanium(IV) exists in acidic solutions as the oxo-cation, TiO 2+ , rather than Ti 4+ . Zirconium is used in the ceramics industry and in nuclear industry as a cladding material in reactors where its reactivity towards hydrolysis reactions and precipitation of oxides may result in degradation of the cladding. In nature, hafnium is found together with zirconium and as a consequence of the contraction in ionic radii that occurs due to the 4f -electron shell, the ionic radius of hafnium is almost identical to that of zirconium. All isotopes of thorium are radioactive and, as a consequence of it being fertile, thorium is important in the nuclear fuel cycle. The polymeric hydrolysis species that have been reported for thorium are somewhat different to those identified for zirconium and hafnium, although thorium does form the Th 4 (OH) 8 8+ species.

  20. Precipitated nanosized titanium dioxide for electrochemical applications

    Energy Technology Data Exchange (ETDEWEB)

    Kirillov, S.A. [Joint Department of Electrochemical Energy Systems, 38A Vernadsky Ave., 03142 Kyiv (Ukraine); Institute for Sorption and Problems of Endoecology, 13 Gen. Naumov St., 03164 Kyiv (Ukraine); Lisnycha, T.V. [Institute for Sorption and Problems of Endoecology, 13 Gen. Naumov St., 03164 Kyiv (Ukraine); Chernukhin, S.I. [Joint Department of Electrochemical Energy Systems, 38A Vernadsky Ave., 03142 Kyiv (Ukraine)

    2011-02-15

    Two types of titanium dioxide samples precipitated from aqueous solutions of titanium tetrachloride are investigated. Crystalline materials are obtained by means of neutralization of TiCl{sub 4} with the solution of an alkali metal hydroxide. The change of the order of mixing leads to amorphous materials. The evolution of the samples upon the thermal treatment is characterized using XRD, SEM, TEM and porosity studies. The application of crystalline TiO{sub 2} as an electrode material in lithium-ion 2016 sample cells enable one to yield specific currents up to 3350 mA g{sup -1}. On the other hand, the thermal treatment of initially amorphous materials does not lead to complete crystallization, and the presence of amorphous TiO{sub 2} is well seen as the so-called capacity behavior of cyclic voltammetry curves. (author)

  1. Purification process of uranium hexafluoride containing traces of plutonium fluoride and/or neptunium fluoride

    International Nuclear Information System (INIS)

    Aubert, J.; Bethuel, L.; Carles, M.

    1983-01-01

    In this process impure uranium hexafluoride is contacted with a metallic fluoride chosen in the group containing lead fluoride PbF 2 , uranium fluorides UFsub(4+x) (0 3 at a temperature such as plutonium and/or neptunium are reduced and pure uranium hexafluoride is recovered. Application is made to uranium hexafluoride purification in spent fuel reprocessing [fr

  2. The fluoride content of an anion exchange resin in the fluoride form

    International Nuclear Information System (INIS)

    Kleijn, J.P. de; Zanten, B. van

    1977-01-01

    The fluoride content of an anion exchange resin in the F - -form depends on the material of the equipment used for the preparation. If a glass equipment is used too much fluorine is introduced. The experimental results are explained by taking into account a competition of F - and SiF 6 2- for the hydroxyl positions of the resin (OH - ). Because SiF 6 2- is bivalent and has a lower hydration energy than F - , the resin has a much larger affinity for this species than for F - . If a higher concentration of SiF 6 2- is generated by an intensive contact of the HF solution with glass, two OH-groups may be replaced by one SiF 6 2- . This results in a resin with 3 times as much fluorine as calculated from the chloride capacity. If the formation of SiF 6 2- is impossible as for example in teflon equipment, the same capacity is obtained for chloride and fluoride. (T.G.)

  3. Fluoride ions vs removal technologies: A study

    OpenAIRE

    Singh, Jagvir; Singh, Prashant; Singh, Anuradha

    2016-01-01

    Literature reported that drinking water is a precious and scarce resource and it has to be protected and kept free from any kind of contamination. Further, it has to be used carefully without wasting. Literature also reported that fluoride bearing rocks are abundant in India, as a result, fluoride leaches out and contaminates the adjacent water and soil resources. A high concentration of fluoride ions in ground water increases up to more than 30 mg/L. This high concentration of fluoride ions ...

  4. Gramicidin D enhances the antibacterial activity of fluoride

    OpenAIRE

    Nelson, James W.; Zhou, Zhiyuan; Breaker, Ronald R.

    2014-01-01

    Fluoride is a toxic anion found in many natural environments. One of the major bacterial defenses against fluoride is the cell envelope, which limits passage of the membrane-impermeant fluoride anion. Accordingly, compounds that enhance the permeability of bacterial membranes to fluoride should also enhance fluoride toxicity. In this study, we demonstrate that the pore-forming antibiotic gramicidin D increases fluoride uptake in B. subtilis and that the antibacterial activity of this compound...

  5. Titanium metal: extraction to application

    Energy Technology Data Exchange (ETDEWEB)

    Gambogi, Joseph (USGS, Reston, VA); Gerdemann, Stephen J.

    2002-09-01

    In 1998, approximately 57,000 tons of titanium metal was consumed in the form of mill products (1). Only about 5% of the 4 million tons of titanium minerals consumed each year is used to produce titanium metal, with the remainder primarily used to produce titanium dioxide pigment. Titanium metal production is primarily based on the direct chlorination of rutile to produce titanium tetrachloride, which is then reduced to metal using the Kroll magnesium reduction process. The use of titanium is tied to its high strength-to-weight ratio and corrosion resistance. Aerospace is the largest application for titanium. In this paper, we discuss all aspects of the titanium industry from ore deposits through extraction to present and future applications. The methods of both primary (mining of ore, extraction, and purification) and secondary (forming and machining) operations will be analyzed. The chemical and physical properties of titanium metal will be briefly examined. Present and future applications for titanium will be discussed. Finally, the economics of titanium metal production also are analyzed as well as the advantages and disadvantages of various alternative extraction methods.

  6. Industrial experience with titanium

    International Nuclear Information System (INIS)

    Ikeda, B.M.; Shoesmith, D.W.

    1997-09-01

    Titanium is a reference material for the construction of waste containers in the Canadian Nuclear Fuel Waste Management Program. It has been in industrial service for over 30 a, often in severe corrosion environments, but it is still considered a relatively exotic material with limited operating history. This has arisen because of the aerospace applications of this material and the misconception that the high strength-to-weight ratio dominates the choice of this material. In fact, the advantage of titanium lies in its high reliability and excellent corrosion resistance. It has a proven record in seawater heat exchanger service and a demonstrated excellent reliability even in polluted water. For many reasons it is the technically correct choice of material for marine applications. In this report we review the industrial service history of titanium, particularly in hot saline environments, and demonstrate that it is a viable waste container material, based upon this industrial service history and operating experience. (author)

  7. Surface modification of titanium and titanium alloys by ion implantation.

    Science.gov (United States)

    Rautray, Tapash R; Narayanan, R; Kwon, Tae-Yub; Kim, Kyo-Han

    2010-05-01

    Titanium and titanium alloys are widely used in biomedical devices and components, especially as hard tissue replacements as well as in cardiac and cardiovascular applications, because of their desirable properties, such as relatively low modulus, good fatigue strength, formability, machinability, corrosion resistance, and biocompatibility. However, titanium and its alloys cannot meet all of the clinical requirements. Therefore, to improve the biological, chemical, and mechanical properties, surface modification is often performed. In view of this, the current review casts new light on surface modification of titanium and titanium alloys by ion beam implantation. (c) 2010 Wiley Periodicals, Inc.

  8. Urinary fluoride output in children following the use of a dual-fluoride varnish formulation

    Directory of Open Access Journals (Sweden)

    Kelly Polido Kaneshiro Olympio

    2009-06-01

    Full Text Available OBJECTIVE: This study evaluated the bioavailability of fluoride after topical application of a dual-fluoride varnish commercially available in Brazil, when compared to DuraphatTM. MATERIAL AND METHODS: The urinary fluoride output was evaluated in seven 5-year-old children after application of the fluoride varnishes, in two different phases. In the first phase (I, children received topical application of the fluoride varnish Duofluorid XII (2.92% fluorine, calcium fluoride + 2.71% fluorine, sodium fluoride, FGM TM. After 1-month interval (phase II, the same amount (0.2 mL of the fluoride varnish Duraphat (2.26% fluorine, sodium fluoride, ColgateTM was applied. Before each application all the volunteers brushed their teeth with placebo dentifrice for 7 days. Urinary collections were carried out 24 h prior up to 48 h after the applications. Fluoride intake from the diet was also estimated. Fluoride concentration in diet samples and urine was analyzed with the fluoride ion-specific electrode and a miniature calomel reference electrode coupled to a potentiometer. Data were tested by ANOVA and Tukey's post hoc test (p<0.05. RESULTS: There were significant differences in the urinary fluoride output between phases I and II. The use of Duofluorid XII did not significantly increase the urinary fluoride output, when compared to baseline levels. The application of Duraphat caused a transitory increase in the urinary fluoride output, returning to baseline levels 48 h after its use. CONCLUSIONS: The tested varnish formulation, which has been shown to be effective in in vitro studies, also can be considered safe.

  9. Fluoride barriers in Nb/Pb Josephson junctions

    Science.gov (United States)

    Asano, H.; Tanabe, K.; Michikami, O.; Igarashi, M.; Beasley, M. R.

    1985-03-01

    Josephson tunnel junctions are fabricated using a new class of artificial barriers, metal fluorides (Al fluoride and Zr fluoride). These fluoride barriers are deposited on the surface of a Nb base electrode, which are previously cleaned using a CF4 cleaning process, and covered by a Pb counterelectrode. The junctions with both Al fluoride and Zr fluoride barriers exhibit good tunneling characteristics and have low specific capacitance. In the case of Zr fluoride, it is observed that reasonable resistances are obtained even at thickness greater than 100 A. This phenomenon might be explained by tunneling via localized states in Zr fluoride.

  10. Application of fluoridated hydroxyapatite thin film coatings using KrF pulsed laser deposition.

    Science.gov (United States)

    Hashimoto, Yoshiya; Ueda, Mamoru; Kohiga, Yu; Imura, Kazuki; Hontsu, Shigeki

    2018-06-08

    Fluoridated hydroxyapatite (FHA) was investigated for application as an implant coating for titanium bone substitute materials in dental implants. A KrF pulsed excimer deposition technique was used for film preparation on a titanium plate. The compacts were ablated by laser irradiation at an energy density of 1 J/cm 2 on an area 1×1 mm 2 with the substrate at room temparature. Energydispersive spectrometric analysis of the FHA film revealed peaks of fluorine in addition to calcium and phosphorus. X-ray diffraction revealed the presence of crystalline FHA on the FHA film after a 10 h post annealing treatment at 450°C. The FHA film coating exhibited significant dissolution resistance to sodium phosphate buffer for up to 21 days, and favorable cell attachment of human mesenchymal stem cells compared with HA film. The results of this study suggest that FHA coatings are suitable for real-world implantation applications.

  11. Minimally invasive monitoring of skeletal muscle hypermetabolism induced by the phosphodiesterase-III-inhibitor milrinone and sodium fluoride.

    Science.gov (United States)

    Schuster, Frank; Johannsen, Stephan; Roewer, Norbert; Anetseder, Martin

    2013-04-01

    We hypothesized that the phosphodiesterase-III-inhibitor milrinone and the non-specific G-protein activator sodium fluoride increase the skeletal muscular lactate levels as a sign of a hypermetabolic response. With approval of the local animal care committee Sprague-Dawley rats were killed and artificially perfused either with Ringer's solution or sodium fluoride 110 mM, while milrinone 1.32 mM or Ringer's solution at 1 μl/min was applied via microdialysis probes in both hind limbs. Lactate was measured spectrophotometrically in the dialysate. Baseline lactate levels before drug application did not differ between hind limbs. Local infusion of milrinone via microdialysis did not significantly increase intramuscular lactate concentrations compared with the Ringer control group. Muscular perfusion with sodium fluoride resulted in a significant increase of lactate and was potentiated by combination with local milrinone. Phosphodiesterase-III-inhibition alone does not significantly influence the lactate levels in skeletal muscle of sacrificed rats. Sodium fluoride infusion leads to an intramuscular lactate increase, which was further potentiated by local inhibition of phosphodiesterase-III. The fluoride-mediated hypermetabolic response following sodium fluoride could be a possible explanation for the observed myotoxic adverse effects in individuals treated by fluoride-containing agents. © 2012 The Authors. JPP © 2012. Royal Pharmaceutical Society.

  12. A Survey of Fluoride Dosage in Driniking Water and DMF Index in Damghan City

    Directory of Open Access Journals (Sweden)

    Hamid Reza Nasehi nia

    2004-05-01

    Full Text Available Fluoride is one of the important elements. There are so many controversial scientific points of view regarding fluoride and its presence in food chain. Water fluoridation is the best and most reliable method for the control of dental caries. In this research, the presence and concentration of fluoride in drinking water resources in the city of Damghan and DMF index (decayed, missed, filled between 560 school students (12-15 was investigated. The mean concentration of fluoride in water supplies of Damaghan city was measured in low rain seasons 0.37 mg/l and high rain seasons 0.6 mg/l the DMF index for 12 year sold student was equal 2.00 that comparing these data with the WHO classify cation for DMF index, showed them to be considered in the second surface (low classificatino. For conclusion, based on the mentioned data, a significant correlation may be found between the two parameters in different communities, and the most logic solution for the control of dental cavities in these communities, is the adjusment of fluoride concentration in drinking water.

  13. Effects of fluoride and 6 benzylaminopurine on growth and respiration of corn and cotton roots

    Energy Technology Data Exchange (ETDEWEB)

    Thompson, C R

    1967-01-01

    Corn and cotton plants exhibit a wide difference in their susceptibility to atmospheric fluoride. Corn shows leaf lesions when 100 ..gamma../gm on a dry weight basis are accumulated but cotton can tolerate 5000 ..gamma../gm without showing leaf necrosis. A comparison of respirational response of potted seedlings of the two species to 10 ..gamma../M/sup 3/ HF caused an increase of about 10%. Addition of 2 x 10/sup 2/M F/sup -/ to solutions for germinating the plants showed that cotton accumulated about twice as much as F/sup -/ in seedling roots. Growth was reduced about one half by 2 x 10/sup -3/M F/sup -/ in both species but respirational rates of root tips from control and fluoride treated tissues were equal. Prolonged treatment of excised root tips with fluoride reduced respiration. Because fluoride causes cellular changes in roots similar to aging and kinetin seems to act to reverse these changes, corn was germinated with 2 x 10/sup -3/M F/sup -/ and increasing levels of 6-benzylaminopurine. Root growth inhibition (63%) was reversed significantly at 0.2 - 0.8..gamma.. ml. Respirational rates of root tips grown in fluoride, fluoride plus 6-benzylaminopurine and controls were equal.

  14. Fluoride Sorption Efficiency of Vermiculite Functionalised with Cationic Surfactant: Isotherm and Kinetics

    Directory of Open Access Journals (Sweden)

    Tayo Oladipo Ologundudu

    2016-09-01

    Full Text Available Groundwater is a major source of water, especially in rural communities. The presence of excess fluoride in groundwater has been a health concern for many decades because it causes fluorosis. The persistence of this problem led to the development of several approaches for reducing fluoride in groundwater to ≤1.5 mg/L, which is the World Health Organization’s (WHO permissible limit. Despite recorded success in fluoride reduction, drawbacks such as cost and efficiency have remained apparent, thus necessitating further research on defluoridation. This paper aims at assessing the defluoridation capacity of a clay mineral, vermiculite, when modified with the cationic surfactant hexadecyltrimethylammonium bromide. The effects of experimental parameters such as pH, agitation time, mass of adsorbent, and temperature were examined to determine the most favourable adsorption conditions. Using batch technique, the results showed a fluoride sorption of 51% from an 8 mg/L fluoride solution. The adsorption conformed more to Freundlich than Langmuir isotherm with an adsorption capacity of 2.36 mg/g, while the kinetics conformed to a pseudo-second-order reaction. pH emerged as the most influential factor in optimisation. The findings of this study indicated that modified vermiculite could be efficient in reducing fluoride in groundwater to more tolerable limits, but requires adequate pH control.

  15. Thermogravimetric experiments with titanium

    International Nuclear Information System (INIS)

    Porter, L.J.; Longhurst, G.R.

    1991-02-01

    In the process of preparing for pyrophoricity experiments involving uranium, we conducted hydriding and air-exposure experiments on titanium. In these experiments the hydriding reactions and response to air-exposure was generally within the range expected based on work reported by others. One aberrant behavior was a sudden weight gain followed by a significant weight loss. We speculate that loss may be due to hydrogen evolution from the TiH 2 resulting from local heating by oxidation reactions. We verified that titanium is not pyrophoric at temperatures less than 750 degree C. 18 refs. 1 fig

  16. Short term serum pharmacokinetics of diammine silver fluoride after oral application

    Directory of Open Access Journals (Sweden)

    Vasquez Elsa

    2012-12-01

    Full Text Available Abstract Background There is growing interest in the use of diammine silver fluoride (DSF as a topical agent to treat dentin hypersensitivity and dental caries as gauged by increasing published research from many parts of the world. While DSF has been available in various formulations for many years, most of its pharmacokinetic aspects within the therapeutic concentration range have never been fully characterized. Methods This preliminary study determined the applied doses (3 teeth treated, maximum serum concentrations, and time to maximum serum concentration for fluoride and silver in 6 adults over 4 h. Fluoride was determined using the indirect diffusion method with a fluoride selective electrode, and silver was determined using inductively coupled plasma-mass spectrometry. The mean amount of DSF solution applied to the 3 teeth was 7.57 mg (6.04 μL. Results Over the 4 hour observation period, the mean maximum serum concentrations were 1.86 μmol/L for fluoride and 206 nmol/L for silver. These maximums were reached 3.0 h and 2.5 h for fluoride and silver, respectively. Conclusions Fluoride exposure was below the U.S. Environmental Protection Agency (EPA oral reference dose. Silver exposure exceeded the EPA oral reference dose for cumulative daily exposure over a lifetime, but for occasional use was well below concentrations associated with toxicity. This preliminary study suggests that serum concentrations of fluoride and silver after topical application of DSF should pose little toxicity risk when used in adults. Clinical trials registration NCT01664871.

  17. The Effects of Remineralization via Fluoride Versus Low-Level Laser IR810 and Fluoride Agents on the Mineralization and Microhardness of Bovine Dental Enamel

    Directory of Open Access Journals (Sweden)

    Edith Lara-Carrillo

    2018-01-01

    Full Text Available The objective of this study was to assess the mineralization and microhardness of bovine dental enamel surfaces treated with fluoride, tri-calcium phosphate, and infrared (IR 810 laser irradiation. The study used 210 bovine incisors, which were divided into six groups (n = 35 in each: Group A: Untreated (control, Group B: Fluoride (Durapath-Colgate, Group C: Fluoride+Tri-calcium phosphate (Clin-Pro White-3 M, Group D: Laser IR 810 (Quantum, Group E: Fluoride+laser, and Group F: Fluoride+tri-calcium phosphate+laser. Mineralization was measured via UV-Vis spectroscopy for phosphorus and via atomic absorption spectroscopy for calcium upon demineralization and remineralization with proven agents. Microhardness (SMH was measured after enamel remineralization. Mineral loss data showed differences between the groups before and after the mineralizing agents were placed (p < 0.05. Fluoride presented the highest remineralization tendency for both calcium and phosphate, with a Vickers microhardness of 329.8 HV0.1/11 (p < 0.05. It was observed that, if remineralization solution contained fewer minerals, the microhardness surface values were higher (r = −0.268 and −0.208; p < 0.05. This study shows that fluoride has a remineralizing effect compared with calcium triphosphate and laser IR810. This in vitro study imitated the application of different remineralizing agents and showed which one was the most efficient for treating non-cavitated injuries. This can prevent the progression of lesions in patients with white spot lesions.

  18. Semi-transparent ordered TiO{sub 2} nanostructures prepared by anodization of titanium thin films deposited onto the FTO substrate

    Energy Technology Data Exchange (ETDEWEB)

    Szkoda, Mariusz, E-mail: mariusz-szkoda@wp.pl [Department of Chemistry and Technology of Functional Materials, Faculty of Chemistry, Gdańsk University of Technology, Narutowicza 11/12, Gdańsk 80-233 (Poland); Lisowska-Oleksiak, Anna [Department of Chemistry and Technology of Functional Materials, Faculty of Chemistry, Gdańsk University of Technology, Narutowicza 11/12, Gdańsk 80-233 (Poland); Grochowska, Katarzyna [Centre for Plasma and Laser Engineering, Szewalski Institute of Fluid-Flow Machinery, Polish Academy of Science, Fiszera 14, 80-231 Gdańsk (Poland); Skowroński, Łukasz [Institute of Mathematics and Physics, UTP University of Science and Technology, Kaliskiego 7, 85-796 Bydgoszcz (Poland); Karczewski, Jakub [Faculty of Applied Physics and Mathematics, Gdańsk University of Technology, Narutowicza 11/12, 80-233 Gdańsk (Poland); Siuzdak, Katarzyna [Centre for Plasma and Laser Engineering, Szewalski Institute of Fluid-Flow Machinery, Polish Academy of Science, Fiszera 14, 80-231 Gdańsk (Poland)

    2016-09-15

    Highlights: • High quality titanium coatings were doposited using industrial magnetron sputtering equipment. • Semi-transparent TiO{sub 2} were prepared via anodization realized in various conditions. • Depending on electrolyte type, ordered tubular or porous TiO{sub 2} layers were obtained. • Prepared material can act as semiconducting layer in photovoltaic cells. - Abstract: In a significant amount of cases, the highly ordered TiO{sub 2} nanotube arrays grow through anodic oxidation of a titanium metal plate immersed in electrolyte containing fluoride ions. However, for some practical applications, e.g. solar cells or electrochromic windows, the semi-transparent TiO{sub 2} formed directly on the transparent, conductive substrate is very much desired. This work shows that high-quality Ti coating could be formed at room temperature using an industrial magnetron sputtering system within 50 min. Under optimized conditions, the anodization process was performed on 2 μm titanium films deposited onto the FTO (fluorine-tin-oxide) support. Depending on the electrolyte type, highly ordered tubular or porous titania layers were obtained. The fabricated samples, after their thermal annealing, were investigated using scanning electron microscopy, Raman spectroscopy and UV–vis spectroscopy in order to investigate their morphology, crystallinity and absorbance ability. The photocurrent response curves indicate that materials are resistant to the photocorrosion process and their activity is strongly connected to optical properties. The most transparent TiO{sub 2} films were fabricated when Ti was anodized in water electrolyte, whereas the highest photocurrent densities (12 μA cm{sup −2}) were registered for titania received after Ti anodization in ethylene glycol solution. The obtained results are of significant importance in the production of thin, semi-transparent titania nanostructures on a commercial scale.

  19. Semi-transparent ordered TiO_2 nanostructures prepared by anodization of titanium thin films deposited onto the FTO substrate

    International Nuclear Information System (INIS)

    Szkoda, Mariusz; Lisowska-Oleksiak, Anna; Grochowska, Katarzyna; Skowroński, Łukasz; Karczewski, Jakub; Siuzdak, Katarzyna

    2016-01-01

    Highlights: • High quality titanium coatings were doposited using industrial magnetron sputtering equipment. • Semi-transparent TiO_2 were prepared via anodization realized in various conditions. • Depending on electrolyte type, ordered tubular or porous TiO_2 layers were obtained. • Prepared material can act as semiconducting layer in photovoltaic cells. - Abstract: In a significant amount of cases, the highly ordered TiO_2 nanotube arrays grow through anodic oxidation of a titanium metal plate immersed in electrolyte containing fluoride ions. However, for some practical applications, e.g. solar cells or electrochromic windows, the semi-transparent TiO_2 formed directly on the transparent, conductive substrate is very much desired. This work shows that high-quality Ti coating could be formed at room temperature using an industrial magnetron sputtering system within 50 min. Under optimized conditions, the anodization process was performed on 2 μm titanium films deposited onto the FTO (fluorine-tin-oxide) support. Depending on the electrolyte type, highly ordered tubular or porous titania layers were obtained. The fabricated samples, after their thermal annealing, were investigated using scanning electron microscopy, Raman spectroscopy and UV–vis spectroscopy in order to investigate their morphology, crystallinity and absorbance ability. The photocurrent response curves indicate that materials are resistant to the photocorrosion process and their activity is strongly connected to optical properties. The most transparent TiO_2 films were fabricated when Ti was anodized in water electrolyte, whereas the highest photocurrent densities (12 μA cm"−"2) were registered for titania received after Ti anodization in ethylene glycol solution. The obtained results are of significant importance in the production of thin, semi-transparent titania nanostructures on a commercial scale.

  20. Development and Characterization of Titanium Compound N anostructures

    Science.gov (United States)

    Zhou, Zhou

    The development and characterization of titanium compound nanostructures have been achieved, for potential applications in energy industry. Oil and gas, one of the traditional industry fields, observes accumulating demands on active implementations of nanotechnology, for the numerous advantages that nanomaterials can introduce to both product performances and field operations. By using chemical vapor deposition and liquid exfoliation, various titanium compound nanostructures have been synthesized through this project. Attractively, these two material fabrication methods have been recognized to be industrial friendly in terms of cost efficiency and productivity. The development of nanostructures, aiming at oil and gas field applications, presents novel solutions for existing issues, such as low durability of drilling tools, high friction in mechanical operations and ineffective heat dissipation. Titanium compound nanostructures, including titanium borides, nitrides and sulfides are therefore investigated for such applications as protective coating, lubrication and thermal management.

  1. Sorption kinetics of cesium on hydrous titanium dioxide

    International Nuclear Information System (INIS)

    Altas, Y.; Tel, H.; Yaprak, G.

    2003-01-01

    Two types of hydrous titanium dioxide possessing different surface properties were prepared and characterized to study the sorption kinetics of cesium. The effect of pH on the adsorption capacity were determined in both type sorbents and the maximum adsorption percentage of cesium were observed at pH 12. To elucidate the kinetics of ion-exchange reaction on hydrous titanium dioxide, the isotopic exchange rates of cesium ions between hydrous titanium dioxides and aqueous solutions were measured radiochemically and compared with each other. The diffusion coefficients of Cs + ion for Type1 and Type2 titanium dioxides at pH 12 were calculated as 2.79 x 10 -11 m 2 s -1 and 1.52 x 10 -11 m 2 s -1 , respectively, under particle diffusion controlled conditions. (orig.)

  2. Curcumin based optical sensing of fluoride in organo-aqueous media using irradiation technique

    Science.gov (United States)

    Venkataraj, Roopa; Radhakrishnan, P.; Kailasnath, M.

    2017-06-01

    The present work describes the degradation of natural dye Curcumin in organic-aqueous media upon irradiation by a multi-wavelength source of light like mercury lamp. The presence of anions in the solution leads to degradation of Curcumin and this degradation is especially enhanced in the case of fluoride ion. The degradation of Curcumin is investigated by studying the change in its absorption and fluorescence characteristics in organoaqueous solution upon irradiation. A broad detection range of fluoride ranging from 2.3×10-6-2.22×10-3 M points to the potential of the method of visible light irradiation enabling aqueous based sensing of fluoride using Curcumin.

  3. Knowledge and attitude of the primary school male students about the Iranian fluoride mouth rinse

    Directory of Open Access Journals (Sweden)

    Hamid Reza Poureslami DDS, MSc

    2012-04-01

    Full Text Available BACKGROUND: This study was designed to assess the knowledge and attitude of male students of Kerman primaryschools about 0.2% sodium fluoride mouthwash solution that students used it once a week.METHODS: In this cross-sectional study, a total of 502 boys, eight to nine year-old and students of Kerman primaryschools were selected for the study. The data related to their knowledge and attitude about the sodium fluoridemouthwash were collected by questionnaire.RESULTS: The boy students’ knowledge about the sodium fluoride mouthwash solution was good but their attitude wasnegative.CONCLUSIONS: The oral health education program concerning the optimal use of the fluoride mouthwash in dentalcaries prevention is highly recommended. It is suggested that its taste is improved

  4. FLUORIDE LEVELS IN COMMERCIALLY AVAILABLE RICE IN ...

    African Journals Online (AJOL)

    Preferred Customer

    2013-05-05

    May 5, 2013 ... Rice is one of the commonly consumed cereals for more than half of the ... also used as flour, for making rice wine, as ingredient for beer and liquor, ... Fluoride is a necessary element to human health, and a moderate amount of fluoride intake ... For Ethiopian red rice (ERR) Fogera was selected to collect.

  5. Biomonitoring Equivalents for interpretation of urinary fluoride.

    Science.gov (United States)

    Aylward, L L; Hays, S M; Vezina, A; Deveau, M; St-Amand, A; Nong, A

    2015-06-01

    Exposure to fluoride is widespread due to its natural occurrence in the environment and addition to drinking water and dental products for the prevention of dental caries. The potential health risks of excess fluoride exposure include aesthetically unacceptable dental fluorosis (tooth mottling) and increased skeletal fragility. Numerous organizations have conducted risk assessments and set guidance values to represent maximum recommended exposure levels as well as recommended adequate intake levels based on potential public health benefits of fluoride exposure. Biomonitoring Equivalents (BEs) are estimates of the average biomarker concentrations corresponding to such exposure guidance values. The literature on daily urinary fluoride excretion rates as a function of daily fluoride exposure was reviewed and BE values corresponding to the available US and Canadian exposure guidance values were derived for fluoride in urine. The derived BE values range from 1.1 to 2.1mg/L (1.2-2.5μg/g creatinine). Concentrations of fluoride in single urinary spot samples from individuals, even under exposure conditions consistent with the exposure guidance values, may vary from the predicted average concentrations by several-fold due to within- and across-individual variation in urinary flow and creatinine excretion rates and due to the rapid elimination kinetics of fluoride. Thus, the BE values are most appropriately applied to screen population central tendency estimates for biomarker concentrations rather than interpretation of individual spot sample concentrations. Copyright © 2015. Published by Elsevier Inc.

  6. Topographic assessment of human enamel surface treated with different topical sodium fluoride agents: Scanning electron microscope consideration

    Directory of Open Access Journals (Sweden)

    Gurlal Singh Brar

    2017-01-01

    Full Text Available Introduction: Continuous balanced demineralization and remineralization are natural dynamic processes in enamel. If the balance is interrupted and demineralization process dominates, it may eventually lead to the development of carious lesions in enamel and dentine. Fluoride helps control decay by enhancing remineralization and altering the structure of the tooth, making the surface less soluble. Methodology: One hundred and twenty sound human permanent incisors randomly and equally distributed into six groups as follows: Group I - Control, II - Sodium fluoride solution, III - Sodium fluoride gel, IV - Sodium fluoride varnish, V - Clinpro Tooth Crème (3M ESPE, and VI-GC Tooth Mousse Plus or MI Paste Plus. The samples were kept in artificial saliva for 12 months, and the topical fluoride agents were applied to the respective sample groups as per the manufacturer instructions. Scanning electron microscope (SEM evaluation of all the samples after 6 and 12 months was made. Results: Morphological changes on the enamel surface after application of fluoride in SEM revealed the presence of globular precipitate in all treated samples. Amorphous, globular, and crystalline structures were seen on the enamel surface of the treated samples. Clear differences were observed between the treated and untreated samples. Conclusion: Globular structures consisting of amorphous CaF2precipitates, which acted as a fluoride reservoir, were observed on the enamel surface after action of different sodium fluoride agents. CPP-ACPF (Tooth Mousse and Tricalcium phosphate with fluoride (Clinpro tooth crème are excellent delivery vehicles available in a slow release amorphous form to localize fluoride at the tooth surface.

  7. Surface Functionalization of Orthopedic Titanium Implants with Bone Sialoprotein.

    Directory of Open Access Journals (Sweden)

    Andreas Baranowski

    Full Text Available Orthopedic implant failure due to aseptic loosening and mechanical instability remains a major problem in total joint replacement. Improving osseointegration at the bone-implant interface may reduce micromotion and loosening. Bone sialoprotein (BSP has been shown to enhance bone formation when coated onto titanium femoral implants and in rat calvarial defect models. However, the most appropriate method of BSP coating, the necessary level of BSP coating, and the effect of BSP coating on cell behavior remain largely unknown. In this study, BSP was covalently coupled to titanium surfaces via an aminosilane linker (APTES, and its properties were compared to BSP applied to titanium via physisorption and untreated titanium. Cell functions were examined using primary human osteoblasts (hOBs and L929 mouse fibroblasts. Gene expression of specific bone turnover markers at the RNA level was detected at different intervals. Cell adhesion to titanium surfaces treated with BSP via physisorption was not significantly different from that of untreated titanium at any time point, whereas BSP application via covalent coupling caused reduced cell adhesion during the first few hours in culture. Cell migration was increased on titanium disks that were treated with higher concentrations of BSP solution, independent of the coating method. During the early phases of hOB proliferation, a suppressive effect of BSP was observed independent of its concentration, particularly when BSP was applied to the titanium surface via physisorption. Although alkaline phosphatase activity was reduced in the BSP-coated titanium groups after 4 days in culture, increased calcium deposition was observed after 21 days. In particular, the gene expression level of RUNX2 was upregulated by BSP. The increase in calcium deposition and the stimulation of cell differentiation induced by BSP highlight its potential as a surface modifier that could enhance the osseointegration of orthopedic implants

  8. Titanium and zirconium alloys

    International Nuclear Information System (INIS)

    Pinard Legry, G.

    1994-01-01

    Titanium and zirconium pure and base alloys are protected by an oxide film with anionic vacancies which gives a very good resistance to corrosion in oxidizing medium, in some ph ranges. Results of pitting and crevice corrosion are given for Cl - , Br - , I - ions concentration with temperature and ph dependence, also with oxygenated ions effect. (A.B.). 32 refs., 6 figs., 3 tabs

  9. Diethylenetriaminium hexafluoridotitanate(IV fluoride

    Directory of Open Access Journals (Sweden)

    J. Lhoste

    2008-11-01

    Full Text Available The title compound, (C6H21N4[TiF6]F, was synthesized by the reaction of TiO2, tris(2-aminoethylamine, HF and ethanol at 463 K in a microwave oven. The crystal structure consists of two crystallographically independent [TiF6]2− anions, two fluoride anions and two triply-protonated tris(2-aminoethylamine cations. The Ti atoms are coordinated by six F atoms within slightly distorted octahedra. The anions and cations are connected by intermolecular N—H...F hydrogen bonds.

  10. Thermodynamic data for uranium fluorides

    Energy Technology Data Exchange (ETDEWEB)

    Leitnaker, J.M.

    1983-03-01

    Self-consistent thermodynamic data have been tabulated for uranium fluorides between UF/sub 4/ and UF/sub 6/, including UF/sub 4/ (solid and gas), U/sub 4/F/sub 17/ (solid), U/sub 2/F/sub 9/ (solid), UF/sub 5/ (solid and gas), U/sub 2/F/sub 10/ (gas), and UF/sub 6/ (solid, liquid, and gas). Included are thermal function - the heat capacity, enthalpy, and free energy function, heats of formation, and vaporization behavior.

  11. Measurement of fluoride in bone

    International Nuclear Information System (INIS)

    Mernagh, J.R.; Harrision, J.E.; Hancock, R.; McNeill, K.G.

    1977-01-01

    The fluorine concentration in bone biopsy samples was measured by neutron activation analysis. The fluorine content was expressed in terms of the calcium content. Samples were irradiated in a reactor to induce the 19 F(n,γ) 20 F and 48 Ca(n,γ) 49 Ca reactions and after rapid transport from the reactor the resulting activities were measured with a Ge(Li) detector. Reproducibility was better than 10% for the F/Ca ratio. The detection limit for F is 50 μg. This nondestructive technique will be used to assess the effect of fluoride therapy on bone metabolism of patients with idiopathic osteoporosis. (author)

  12. The Fitness Cost of Fluoride Resistance for Different Streptococcus mutans Strains in Biofilms

    Directory of Open Access Journals (Sweden)

    Yanling Cai

    2017-08-01

    Full Text Available The cariogenic bacterium Streptococcus mutans can develop stable resistance to fluoride through chromosomal mutations in vitro. Fluoride-resistant S. mutans has seldom been isolated in clinical settings, despite the wide application of fluoride in oral-care products. One explanation is that the fluoride-resistant S. mutans strains have decreased fitness. However, so far, there has been no conclusive evidence to support this idea. The aim of this study was to investigate the fitness cost of 48-h biofilms of two fluoride-resistant S. mutans strains, UF35 and UA159-FR (UAFR, using the wild-type fluoride-sensitive strain UA159 as a reference. The engineered UF35 strain contains one point mutation, whereas UAFR, selected from NaF-containing agar plates, has multiple chromosomal mutations. All biofilms were formed for 48 h under a constantly neutral pH or a pH-cycling (8 h of neutral pH and 16 h of pH 5.5 condition in the absence of fluoride. The biomass of the biofilms was quantified with a crystal violet assay. The biofilms were also treated with chlorhexidine or solutions at pH 3.0, after which their lactic acid production was quantified. Compared to the UF35 and UA159 biofilms, the biomass of UAFR biofilms was two–four fold higher, and the UAFR biofilms were more resistant to chlorhexidine and low pH in terms of lactic acid production. No difference in biomass and lactic acid production was detected between UF35 and UA159 biofilms. The fluoride resistance of UAFR and UF35 strains in biofilms was further confirmed by treating the biofilms with NaF solutions. The level of NaF resistance of the three biofilms is generally ranked as follows: UAFR > UF35 > UA159. In conclusion, there is indeed a fitness consequence in UAFR, but surprisingly, this fluoride-resistant strain performs better than UF35 and UA159 under the described conditions. In addition, UF35 did not display a reduced fitness; it performed as well as the wild-type fluoride

  13. Determination of Fluoride in Different Toothpaste Formulations

    International Nuclear Information System (INIS)

    Kamau, N.G.; Njoroge, M.; Njau, M.

    1998-01-01

    Fluoride ion selective electrode was used to determine fluoride ion concentrations in seven brands of toothpaste. These were the only available formulations found in Kenya. The brands were classified into three groups-fluoridated, non fluoridated or not indicated. However, there was no independent indication of their quantitative composition. The analysed brands had fluoride content between 0.0033% and 0.096%. These values compared favourably with those obtained elsewhere. The calculated lowest limit of detection (LLD) was 0.01 ppmF- . The mean calibration curve gave a slope of of -50.0mV. which was not significantly different from the theoretical value of 5.88mV at 23 degrees celsius at 95% confidence level

  14. Inhibition of cellular oxidation by fluoride

    Energy Technology Data Exchange (ETDEWEB)

    Borei, H

    1945-01-01

    An attempt has been made to investigate the inhibition by fluoride of the oxidative processes which occur in the cell by way of the cytochrome oxidase-cytochrome system. Some chemical and physical properties of the fluoride ion are discussed, together with certain quantitative methods for the determination of fluoride. An exhaustive review of the literature concerning the effect of fluoride on enzymic processes has been compiled. The experiments have shown that the point of the attack by fluoride is to be found among the cytochromes. The inhibitory mechanism appears to be such that the haemoprotein is prevented from taking part in the preceding and succeeding links in the reaction chain. The blocking action leaves the prosthetic group of the haemoprotein completely unchanged. The experimental results indicate the formation of a fluorophosphoprotein complex, analogous to that found in the case of enolase. Magnesium may possibly play a part in this process.

  15. Formation of Fluorohydroxyapatite with Silver Diamine Fluoride.

    Science.gov (United States)

    Mei, M L; Nudelman, F; Marzec, B; Walker, J M; Lo, E C M; Walls, A W; Chu, C H

    2017-09-01

    Silver diamine fluoride (SDF) is found to promote remineralization and harden the carious lesion. Hydroxyapatite crystallization is a crucial process in remineralization; however, the role of SDF in crystal formation is unknown. We designed an in vitro experiment with calcium phosphate with different SDF concentrations (0.38, 1.52, 2.66, 3.80 mg/mL) to investigate the effect of this additive on the nucleation and growth of apatite crystals. Two control groups were also prepared-calcium phosphate (CaCl 2 ·2H 2 O + K 2 HPO 4 in buffer solution) and SDF (Ag[NH 3 ] 2 F in buffer solution). After incubation at 37 o C for 24 h, the shape and organization of the crystals were examined by bright-field transmission electron microscopy and electron diffraction. Unit cell parameters of the obtained crystals were determined with powder X-ray diffraction. The vibrational and rotational modes of phosphate groups were analyzed with Raman microscopy. The transmission electron microscopy and selected-area electron diffraction confirmed that all solids precipitated within the SDF groups were crystalline and that there was a positive correlation between the increased percentage of crystal size and the concentration of SDF. The powder X-ray diffraction patterns indicated that fluorohydroxyapatite and silver chloride were formed in all the SDF groups. Compared with calcium phosphate control, a contraction of the unit cell in the a-direction but not the c-direction in SDF groups was revealed, which suggested that small localized fluoride anions substituted the hydroxyl anions in hydroxyapatite crystals. This was further evidenced by the Raman spectra, which displayed up-field shift of the phosphate band in all the SDF groups and confirmed that the chemical environment of the phosphate functionalities indeed changed. The results suggested that SDF reacted with calcium and phosphate ions and produced fluorohydroxyapatite. This preferential precipitation of fluorohydroxyapatite with

  16. Crystallization of modified hydroxyapatite on titanium implants

    International Nuclear Information System (INIS)

    Golovanova, O A; Izmailov, R R; Zaits, A V; Ghyngazov, S A

    2016-01-01

    Carbonated-hydroxyapatite (CHA) and Si-hydroxyapatite (Si-HA) precipitation have been synthesized from the model bioliquid solutions (synovial fluid and SBF). It is found that all the samples synthesized from the model solutions are single-phase and represent hydroxyapatite. The crystallization of the modified hydroxyapatite on alloys of different composition, roughness and subjected to different treatment techniques was investigated. Irradiation of the titanium substrates with the deposited biomimetic coating can facilitate further growth of the crystal and regeneration of the surface. (paper)

  17. Hydrogen in niobium-titanium alloys

    International Nuclear Information System (INIS)

    Silva, J.R.G. da; Cabral, F.A.O.; Florencio, O.

    1985-01-01

    High purity Nb-Ti polycrystalline alloys were doped with hydrogen in equilibrium with the gaseous atmosphere at a pressure of 80 torr. at different temperatures. The partial molar enthalpy and entropy of the hydrogen solution at high dilution, ΔH sup(-) 0 and ΔS sup(-) 0 , were calculated from the equilibrium solubility data. The ΔH sup(-) 0 values are compared with the electron screened proton model of metal-hydrogen solutions. The addition of titanium to niobium has the effect to increase the hydrogen solubility at a given equilibrium temperature. (Author) [pt

  18. Quantification of trace level of fluoride content in uranium oxide produced by deconversion of HEX gas by ion chromatography

    International Nuclear Information System (INIS)

    Unnikrishnan, E.K.; Padmakumar, P.R.; Shanmugavelu, P.; Sudhakar, T.M.; Bhowmik, A.

    2015-01-01

    Fluoride content in nuclear fuel is detrimental due to its corrosion behavior with cladding material. It is essential to monitor and control the fluoride concentration in nuclear material at various processing stages. Deconversion of upgraded HEX gas is carried out to produce uranium oxide. The performance of the deconversion process of HEX gas is evaluated for which trace level of fluoride concentration accompanying uranium oxide is considered as a marker. An analytical method has been developed for testing the uranium oxide produced from deconversion process of HEX gas. The method involves sample pretreatment followed by analysis using ion chromatography. The test method was validated for its performance using in house synthetic uranyl fluoride (UO 2 F 2 ) standard solutions prepared with different level of fluoride content. The results are in agreement with the expected values with the recovery in the range of 80-95%. This method has been successfully implemented for routine analysis of samples at our lab. Since UO 2 F 2 reference material is not available to validate this method, in house UO 2 F 2 standards were prepared from U 3 O 8 prepared from nuclear grade uranyl nitrate solution. UO 2 F 2 standards were prepared by converting U 3 O 8 to UO 2 F 2 by the addition of HF followed by H 2 O 2 at 200°C on a hot plate. The entire yellow colored UO 2 F 2 was dissolved in nano pure water and recrystallised several times to ensure that all free HF is removed. The crystals dried in air oven at 120° for three hours. Samples containing 1000 mg kg -1 fluoride prepared from this UO 2 F 2 , and subsequently from this sample containing 5 mg kg -1 to 35 mg kg -1 fluoride samples were prepared and analysed against fluoride CRM and the fluoride concentration obtained was analysed

  19. Carbon Dioxide Induced Alkene Extrusion from Bis(pentamethylcyclopentadienyl)titanium(III) Alkyls

    NARCIS (Netherlands)

    Luinstra, Gerrit A.; Teuben, Jan H.

    1987-01-01

    Reaction of titanium(III) alkyls, (η5-C5Me5)2TiR (R = Et or Prn), in toluene solution with CO2 proceeds at room temperature with formation of the titanium formate (η5-C5Me5)2TiO2CH, and the corresponding alkene (ethene or propene).

  20. Multi-criteria assessment of community-based fluoride-removal technologies for rural Ethiopia.

    Science.gov (United States)

    Osterwalder, Lars; Johnson, C Annette; Yang, Hong; Johnston, Richard B

    2014-08-01

    Elevated concentrations of naturally-occurring fluoride in groundwater pose a serious health risk to millions of people living in the Ethiopian Rift Valley. In the absence of low-fluoride water resources of sufficient capacity, fluoride removal from drinking water is the accepted mitigation option. To date, five different community-level fluoride-removal technologies have been implemented in Ethiopia, although only a few units have been found in a functional state in the field. Which technology should be promoted and up-scaled is the subject of controversial debate amongst key stakeholders. This paper describes a multi-criteria decision analysis exercise, which was conducted with the participation of stakeholders in Ethiopia during a one-day workshop, to assess in an objective and transparent manner the available technology options. Criteria for technology comparison were selected and weighted, thus enabling the participants to assess the advantages and disadvantages of the different technologies and hear the views of other stakeholders. It was shown that there is no single most-preferable, technical solution for fluoride removal in Ethiopia. Selection of the most suitable solution depends on location-specific parameters and on the relative importance given to different criteria by the stakeholders involved. The data presented in this paper can be used as reference values for Ethiopia. © 2013. Published by Elsevier B.V. All rights reserved.

  1. Effect of strong acids on red mud structural and fluoride adsorption properties.

    Science.gov (United States)

    Liang, Wentao; Couperthwaite, Sara J; Kaur, Gurkiran; Yan, Cheng; Johnstone, Dean W; Millar, Graeme J

    2014-06-01

    The removal of fluoride using red mud has been improved by acidifying red mud with hydrochloric, nitric and sulphuric acid. The acidification of red mud causes sodalite and cancrinite phases to dissociate, confirmed by the release of sodium and aluminium into solution as well as the disappearance of sodalite bands and peaks in infrared and X-ray diffraction data. The dissolution of these mineral phases increases the amount of available iron and aluminium oxide/hydroxide sites that are accessible for the adsorption of fluoride. However, concentrated acids have a negative effect on adsorption due to the dissolution of these iron and aluminium oxide/hydroxide sites. The removal of fluoride is dependent on the charge of iron and aluminium oxide/hydroxides on the surface of red mud. Acidifying red mud with hydrochloric, nitric and sulphuric acid resulted in surface sites of the form ≡SOH2(+) and ≡SOH. Optimum removal is obtained when the majority of surface sites are in the form ≡SOH2(+) as the substitution of a fluoride ion does not cause a significant increase in pH. This investigation shows the importance of having a low and consistent pH for the removal of fluoride from aqueous solutions using red mud. Copyright © 2014 Elsevier Inc. All rights reserved.

  2. Bacterial adherence to anodized titanium alloy

    International Nuclear Information System (INIS)

    Peremarch, C Perez-Jorge; Tanoira, R Perez; Arenas, M A; Matykina, E; Conde, A; De Damborenea, J J; Gomez Barrena, E; Esteban, J

    2010-01-01

    The aim of this study was to evaluate Staphylococcus sp adhesion to modified surfaces of anodized titanium alloy (Ti-6Al-4V). Surface modification involved generation of fluoride-containing titanium oxide nanotube films. Specimens of Ti-6Al-4V alloy 6-4 ELI-grade 23- meets the requirements of ASTM F136 2002A (AMS 2631B class A1) were anodized in a mixture of sulphuric/hydrofluoric acid at 20 V for 5 and 60 min to form a 100 nm-thick porous film of 20 nm pore diameter and 230 nm-thick nanotube films of 100 nm in diameter. The amount of fluorine in the oxide films was of 6% and of 4%, respectively. Collection strains and six clinical strains each of Staphylococcus aureus and Staphylococcus epidermidis were studied. The adherence study was performed using a previously published protocol by Kinnari et al. The experiments were performed in triplicates. As a result, lower adherence was detected for collection strains in modified materials than in unmodified controls. Differences between clinical strains were detected for both species (p<0.0001, Kruskal-Wallis test), although global data showed similar results to that of collection strains (p<0.0001, Kruskal-Wallis test). Adherence of bacteria to modified surfaces was decreased for both species. The results also reflect a difference in the adherence between S. aureus and S. epidermidis to the modified material. As a conclusion, not only we were able to confirm the decrease of adherence in the modified surface, but also the need to test multiple clinical strains to obtain more realistic microbiological results due to intraspecies differences.

  3. Electrochemical Behaviour and Galvanic Effects of Titanium Implants Coupled to Metallic Suprastructures in Artificial Saliva

    Science.gov (United States)

    Mellado-Valero, Ana; Igual Muñoz, Anna; Guiñón Pina, Virginia

    2018-01-01

    The aim of the present study is to analyze the electrochemical behavior of five different dental alloys: two cobalt-chromium alloys (CoCr and CoCr-c), one nickel-chromium-titanium alloy (NiCrTi), one gold-palladium alloy (Au), and one titanium alloy (Ti6Al4V), and the galvanic effect when they are coupled to titanium implants (TiG2). It was carried out by electrochemical techniques (open circuit measurements, potentiodynamic curves and Zero-Resistance Ammetry) in artificial saliva (AS), with and without fluorides in different acidic conditions. The studied alloys are spontaneously passivated, but NiCrTi alloy has a very narrow passive domain and losses its passivity in presence of fluorides, so is not considered as a good option for implant superstructures. Variations of pH from 6.5 to 3 in artificial saliva do not change the electrochemical behavior of Ti, Ti6Al4V, and CoCr alloys, and couples, but when the pH of the artificial saliva is below 3.5 and the fluoride content is 1000 ppm Ti and Ti6Al4V starts actively dissolving, and CoCr-c superstructures coupled to Ti show acceleration of corrosion due to galvanic effects. Thus, NiCrTi is not recommended for implant superstructures because of risk of Ni ion release to the body, and fluorides should be avoided in acidic media because Ti, Ti6Al4V, and CoCr-c superstructures show galvanic corrosion. The best combinations are Ti/Ti6Al4V and Ti/CoCr as alternative of noble gold alloys. PMID:29361767

  4. Hydroxyapatite electrodeposition on anodized titanium nanotubes for orthopedic applications

    Science.gov (United States)

    Parcharoen, Yardnapar; Kajitvichyanukul, Puangrat; Sirivisoot, Sirinrath; Termsuksawad, Preecha

    2014-08-01

    Nanotubes modification for orthopedic implants has shown interesting biological performances (such as improving cell adhesion, cell differentiation, and enhancing osseointegration). The purpose of this study is to investigate effect of titanium dioxide (TiO2) nanotube feature on performance of hydroxyapatite-coated titanium (Ti) bone implants. TiO2 nanotubes were prepared by anodization using ammonium fluoride electrolyte (NH4F) with and without modifiers (PEG400 and Glycerol) at various potential forms, and times. After anodization, the nanotubes were subsequently annealed. TiO2 nanotubes were characterized by scanning electron microscope and X-ray diffractometer. The amorphous to anatase transformation due to annealing was observed. Smooth and highly organized TiO2 nanotubes were found when high viscous electrolyte, NH4F in glycerol, was used. Negative voltage (-4 V) during anodization was confirmed to increase nanotube thickness. Length of the TiO2 nanotubes was significantly increased by times. The TiO2 nanotube was electrodeposited with hydroxyapatite (HA) and its adhesion was estimated by adhesive tape test. The result showed that nanotubes with the tube length of 560 nm showed excellent adhesion. The coated HA were tested for biological test by live/dead cell straining. HA coated on TiO2 nanotubes showed higher cells density, higher live cells, and more spreading of MC3T3-E1 cells than that growing on titanium plate surface.

  5. The Effect of Fluoridated and Non Fluoridated Mouth Washes on Color Stability of Different Aesthetic Arch Wires At Different Time Intervals (An in Vitro Study

    Directory of Open Access Journals (Sweden)

    Lubna Maky Hussein

    2018-01-01

    Full Text Available Background:The color stability of aesthetic arch wires is an important factor in the success of an aesthetic orthodontic treatment, but the color of these arch wires tends to change with time.This study was performed to assess the effect of two types of mouth washes on the color  stability of different types of aesthetic arch wires at different time intervals. Materials and methods:Four brands of nickel titanium coated aesthetic arch wires were used: epoxy coated (Orthotechnology and G&H and Teflon coated (Dany and Hubit.Thirty six samples were prepared, each sample contains ten halves of the aesthetic arch wires. They were divided into three groups according to the immersion media (distilled water as a control media, Listerine with fluoride and Listerine without fluoride and immersed for 30 seconds twice daily according to manufacturer's instructions to measure color change after 1 week, 3 weeks and 6 weeks by using spectrophotometer VITA Easyshade Compact according to Commission Internationale de l’Eclairage L*a*b* color space system. Results:It was found that there were highly significant differences in color change values of aesthetic arch wires among all immersion media at different time intervals and color change value increases as the time of immersion increases.Additionally, Listerine with fluoride mouth wash caused higher color change values of aesthetic arch wires than Listerine without fluoride and Hubit aesthetic arch wires were the least color stable while Orthotechnology aesthetic arch wires were the most color stable. Conclusions: We can conclude that the daily use of Listerine mouth washes could affect on the color stability of aesthetic arch wires. Although all tested aesthetic arch wires revealed color changes at variable degrees but some of these changes were not  visible and the others were clinically acceptable while the remaining were clinically unacceptable.

  6. Anticaries potential of commercial dentifrices as determined by fluoridation and remineralization efficiency.

    Science.gov (United States)

    Casals, Elias; Boukpessi, Tchilalo; McQueen, Christina M; Eversole, Sandy L; Faller, Robert V

    2007-11-01

    The aim of this in vitro study was to investigate fluoride uptake in human enamel after use of commercially available toothpastes containing different fluoride compounds, or combinations of fluoride actives formulated into a single product, as a means of determining the efficiency of each formula for delivering caries preventing fluoride to demineralized (caries active) enamel. Four test dentifrices and two controls were assessed and placed in groups as follows: Group 1: Lacer (Spain); Group 2: Positive control-USP Reference Standard 1100 ppm F; Group 3: Fluocaril Bi-Fluoré 250 (France); Group 4: Colgate Fluor Active (Denmark); Group 5: Elmex (France); and Group 6: A placebo (formulated the same as the USP Reference Standard toothpaste with the exception that it contained < 1 ppm F). Cores 3 mm in diameter were removed from erupted human enamel specimens (extracted by local oral surgeons for orthodontic reasons) and stored in 1% Thymol solution prior to use. They were ground and polished to remove the natural fluoride rich enamel layer, then exposed to a demineralization solution, and assessed for surface microhardness to enable randomization for use in the study. Each group of five specimens underwent a daily pH cycling procedure that involved exposure to pooled human saliva (refreshed three times daily). The groups were then exposed to dentifrice slurries four times daily for one minute per exposure and to a demineralization solution for three hours. The cycling procedure was repeated for five days. Specimens were again analyzed for surface microhardness and fluoride uptake upon completion of five days of treatment. Average surface hardness: Groups 2 and 3 showed a statistically significant greater (p<0.05) change indicating greater remineralization compared to all other groups. The average change was 23.45 for Group 2 and 22.65 for Group 3. All other groups had changes ranging from 4.25-8.62. No other statistically significant differences were observed between

  7. A novel approach to fabrication of three-dimensional porous titanium with controllable structure

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Dong; Li, Qiuyan; Xu, Mingqin; Jiang, Guofeng; Zhang, Yunxia [Shanghai Key Laboratory of Materials Laser Processing and Modification, and State Key Laboratory of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); He, Guo, E-mail: ghe@sjtu.edu.cn [Shanghai Key Laboratory of Materials Laser Processing and Modification, and State Key Laboratory of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai 200240 (China)

    2017-02-01

    A new approach to fabrication of porous titanium by using the molybdenum wire as space holder was developed, in which titanium liquid was cast into the entangled molybdenum wires in a vacuum environment, and followed by etching off the space holder material in an aqua regia solution. This infiltration casting and acid corrosion method fabricated the porous titanium with different porosities with a pore diameter of 0.4 mm. The porous titanium with the porosity of 32–47% exhibited the Young's modulus in the range of 23–62 GPa and the yielding strength in the range of 76–192 MPa. The adhesion and spreadability of the bovine osteoblast cells on the porous titanium were also evaluated in vitro. The porous titanium with 47% porosity has great potential for implant applications. - Highlights: • A new approach to fabrication of porous titanium was developed. • The 3D morphology of the interconnected porous structure can be exactly controlled. • The as-prepared porous titanium exhibits adequate yielding strength. • The elastic modulus of the porous titanium matches well with that of cortical bone. • The as-prepared porous titanium has great potential for implant applications.

  8. Studies on the comparative effect of sodium fluoride on collagen ...

    African Journals Online (AJOL)

    Fluoride is an essential element for the normal development and growth of human beings. The main source of fluoride for humans is the intake of groundwater. At high levels, fluoride causes dental and skeletal fluorosis. In this study, control and sodium fluoride (NaF) treated groups of rats had significant (p < 0.05) higher ...

  9. Crystalline hydroxyapatite coatings synthesized under hydrothermal conditions on modified titanium substrates

    International Nuclear Information System (INIS)

    Suchanek, Katarzyna; Bartkowiak, Amanda; Gdowik, Agnieszka; Perzanowski, Marcin; Kąc, Sławomir; Szaraniec, Barbara; Suchanek, Mateusz; Marszałek, Marta

    2015-01-01

    Hydroxyapatite coatings were successfully produced on modified titanium substrates via hydrothermal synthesis in a Ca(EDTA) 2− and (NH 4 ) 2 HPO 4 solution. The morphology of modified titanium substrates as well as hydroxyapatite coatings was studied using scanning electron microcopy and phase identification by X-ray diffraction, and Raman and FTIR spectroscopy. The results show that the nucleation and growth of hydroxyapatite needle-like crystals with hexagonal symmetry occurred only on titanium substrates both chemically and thermally treated. No hydroxyapatite phase was detected on only acid etched Ti metal. This finding demonstrates that only a particular titanium surface treatment can effectively induce the apatite nucleation under hydrothermal conditions. - Highlights: • Bioactivation of titanium substrate by chemical and heat treatments • Precipitation of hydroxyapatite on modified titanium plates • Hydrothermal crystallization of hydroxyapatite by chelate decomposition method

  10. Effect of titanium on microstructural changes in SUS 316 stainless steels

    International Nuclear Information System (INIS)

    Kawanishi, H.; Yamada, M.; Fukuya, K.; Ishino, S.

    1982-01-01

    The microstructural changes have been examined in order to study the effect of titanium addition to type 316 stainless steels on void swelling. Titanium ions of 400 keV from an accelerator have been implanted at room temperature to solution treated SUS 316 stainless steels which have the original titanium content of 0.02 wt.% to the concentration increase of titanium by 0.01, 0.02 and 0.1 wt.%. Following the preinjection of 20 at.ppm helium at ambient temperature, 400 keV-aluminium ions have been irradiated to the specimen to 40 dpa at 550, 625 and 675 0 C. The TEM observations have revealed that the void number density is drastically increased in the specimen with the content of implanted titanium of more than 0.01 wt.%, whereas the void diameter is remarkably decreased with the titanium content. (orig.)

  11. Crystalline hydroxyapatite coatings synthesized under hydrothermal conditions on modified titanium substrates

    Energy Technology Data Exchange (ETDEWEB)

    Suchanek, Katarzyna, E-mail: Katarzyna.Suchanek@ifj.edu.pl [The Henryk Niewodniczański Institute of Nuclear Physics, Polish Academy of Sciences, Radzikowskiego Street 152, 31-342 Krakow (Poland); Bartkowiak, Amanda [The Henryk Niewodniczański Institute of Nuclear Physics, Polish Academy of Sciences, Radzikowskiego Street 152, 31-342 Krakow (Poland); Gdowik, Agnieszka [Faculty of Physics and Applied Computer Science, AGH University of Science and Technology, Mickiewicza 30, 30-059 Krakow (Poland); Perzanowski, Marcin [The Henryk Niewodniczański Institute of Nuclear Physics, Polish Academy of Sciences, Radzikowskiego Street 152, 31-342 Krakow (Poland); Kąc, Sławomir [Faculty of Metals Engineering and Industrial Computer Science, AGH University of Science and Technology, Mickiewica 30, 30-059 Krakow (Poland); Szaraniec, Barbara [Department of Biomaterials, AGH University of Science and Technology, Mickiewicza 30, 30-059 Krakow (Poland); Suchanek, Mateusz [Department of Chemistry and Physics, University of Agriculture in Krakow, Mickiewicza 21, 31-120 Krakow (Poland); Marszałek, Marta [The Henryk Niewodniczański Institute of Nuclear Physics, Polish Academy of Sciences, Radzikowskiego Street 152, 31-342 Krakow (Poland)

    2015-06-01

    Hydroxyapatite coatings were successfully produced on modified titanium substrates via hydrothermal synthesis in a Ca(EDTA){sup 2−} and (NH{sub 4}){sub 2}HPO{sub 4} solution. The morphology of modified titanium substrates as well as hydroxyapatite coatings was studied using scanning electron microcopy and phase identification by X-ray diffraction, and Raman and FTIR spectroscopy. The results show that the nucleation and growth of hydroxyapatite needle-like crystals with hexagonal symmetry occurred only on titanium substrates both chemically and thermally treated. No hydroxyapatite phase was detected on only acid etched Ti metal. This finding demonstrates that only a particular titanium surface treatment can effectively induce the apatite nucleation under hydrothermal conditions. - Highlights: • Bioactivation of titanium substrate by chemical and heat treatments • Precipitation of hydroxyapatite on modified titanium plates • Hydrothermal crystallization of hydroxyapatite by chelate decomposition method.

  12. Comparison of galvanic corrosion potential of metal injection molded brackets to that of conventional metal brackets with nickel-titanium and copper nickel-titanium archwire combinations.

    Science.gov (United States)

    Varma, D Praveen Kumar; Chidambaram, S; Reddy, K Baburam; Vijay, M; Ravindranath, D; Prasad, M Rajendra

    2013-05-01

    The aim of the study is to investigate the galvanic corrosion potential of metal injection molding (MIM) brackets to that of conventional brackets under similar in vitro conditions with nickel-titanium and copper nickel-titanium archwires. Twenty-five maxillary premolar MIM stainless steel brackets and 25 conventional stainless steel brackets and archwires, 0.16 inch, each 10 mm length, 25 nickeltitanium wires, 25 copper nickel-titanium wires were used. They were divided into four groups which had five samples each. Combination of MIM bracket with copper nickel-titanium wire, MIM bracket with nickel-titanium wire and conventional stainless steel brackets with copper nickel-titanium wire and conventional stainless steel brackets with nickel-titanium wires which later were suspended in 350 ml of 1 M lactic acid solution media. Galvanic corrosion potential of four groups were analyzed under similar in vitro conditions. Precorrosion and postcorrosion elemental composition of MIM and conventional stainless steel bracket by scanning electron microscope (SEM) with energy dispersive spectroscope (EDS) was done. MIM bracket showed decreased corrosion susceptibility than conventional bracket with copper nickeltitanium wire. Both MIM and conventional bracket showed similar corrosion resistance potential in association with nickel-titanium archwires. It seems that both brackets are more compatible with copper nickel-titanium archwires regarding the decrease in the consequences of galvanic reaction. The EDS analysis showed that the MIM brackets with copper nickel-titanium wires released less metal ions than conventional bracket with copper nickeltitanium wires. MIM brackets showed decreased corrosion susceptibility, copper nickel-titanium archwires are compatible with both the brackets than nickel-titanium archwires. Clinically MIM and conventional brackets behaved more or less similarly in terms of corrosion resistance. In order to decrease the corrosion potential of MIM

  13. Evaluation of toxic action of fluorides on agricultural plants

    Directory of Open Access Journals (Sweden)

    V. N. Grishko

    2007-03-01

    Full Text Available The toxicity of potassium fluoride, sodium fluoride and ammonium fluoride for pea, maize, oat and onion was studied. It was found that the level of the toxic influence had grown with increase of fluoride concentration in the media of growth (from 5 to 100 mg of F–/l. By increase of the toxic influence the agricultural crops are disposed in the following row: oat < onion < maize < pea. Ammonium fluoride demonstrates lesser toxicity, than potassium and sodium fluorides. Under low concentrations of fluoride compounds (5 and 10 mg of F–/l stimulation of roots growth is noted only for the oat.

  14. The differences in healthcare utilization for dental caries based on the implementation of water fluoridation in South Korea.

    Science.gov (United States)

    Cho, Myung-Soo; Han, Kyu-Tae; Park, Sohee; Moon, Ki Tae; Park, Eun-Cheol

    2016-11-08

    There were some debates about the water fluoridation program in South Korea, even if the program had generally substantial effectiveness. Because the out-of-pocket expenditures for dental care were higher in South Korea than in other countries, an efficient solution was needed. Therefore, we examined the relationship between the implementation of water fluoridation and the utilization of dental care. We used the National Health Insurance Service National Sample Cohort. In this study, data finally included 472,250 patients who were newly diagnosed with dental caries during 2003-2013. We performed survival analysis using cox proportional hazard model, negative binomial-regression, and regression analyses using generalized estimating equation models. There were 48.49 % outpatient dental care visit during study period. Individuals with water fluoridation had a lower risk of dental care visits (HR = 0.949, 95 % CI = 0.928-0.971). Among the individuals who experienced a dental care visit, those with water fluoridation program had a lower number of dental care visits (β = -0.029), and the period of water fluoridation had an inverse association with the dental care expenditures. The implementation of water fluoridation programs and these periods are associated with reducing the utilization of dental health care. Considering these positive impacts, healthcare professionals must consider preventive strategies for activating water fluoridation programs, such as changes in public perception and relations, for the effective management of dental care in South Korea.

  15. The sampling of hydrogen fluoride in air with impregnated filter paper

    NARCIS (Netherlands)

    Huygen, C.

    1963-01-01

    A method isproposed for the quantitative collection of hydrogen fluoride in air by drawing a known quantity of the air through filter paper impregnated with solutions of potassium hydroxide and glycerol or triethanolamine. Somu possibilities and limitations of the method are discussed.

  16. Recovery of plutonium from nitric acid containing oxalate and fluoride by a macroporous bifunctional phosphinic acid resin (MPBPA)

    International Nuclear Information System (INIS)

    Venugopal Chetty, K.; Godbole, A.G.; Swarup, R.; Vaidya, V.N.; Venugopal, V.; Vasudeva Rao, P.R.

    2006-01-01

    The sorption of Pu from nitric acid solutions containing oxalate/fluoride was studied using an indigenously available macroporous bifunctional phosphinic acid (MPBPA) resin. Batch experiments were carried out to obtain the distribution data of Pu(IV) with a view to optimize conditions for its recovery from nitric acid waste solutions containing oxalate or fluoride ions. The measurements showed high distribution ratio (D) values even in the presence of strong complexing ions, like oxalate and fluoride, indicating the possibility of recovery of Pu from these types of waste solution. Column studies were carried out using this resin to recover Pu from the oxalate supernatant waste solution, which showed that up to 99% of Pu could be adsorbed on the resin. Elution of Pu loaded on the resin was studied using different eluting agents. (author)

  17. Physiologic Conditions Affect Toxicity of Ingested Industrial Fluoride

    Directory of Open Access Journals (Sweden)

    Richard Sauerheber

    2013-01-01

    Full Text Available The effects of calcium ion and broad pH ranges on free fluoride ion aqueous concentrations were measured directly and computed theoretically. Solubility calculations indicate that blood fluoride concentrations that occur in lethal poisonings would decrease calcium below prevailing levels. Acute lethal poisoning and also many of the chronic effects of fluoride involve alterations in the chemical activity of calcium by the fluoride ion. Natural calcium fluoride with low solubility and toxicity from ingestion is distinct from fully soluble toxic industrial fluorides. The toxicity of fluoride is determined by environmental conditions and the positive cations present. At a pH typical of gastric juice, fluoride is largely protonated as hydrofluoric acid HF. Industrial fluoride ingested from treated water enters saliva at levels too low to affect dental caries. Blood levels during lifelong consumption can harm heart, bone, brain, and even developing teeth enamel. The widespread policy known as water fluoridation is discussed in light of these findings.

  18. Physiologic conditions affect toxicity of ingested industrial fluoride.

    Science.gov (United States)

    Sauerheber, Richard

    2013-01-01

    The effects of calcium ion and broad pH ranges on free fluoride ion aqueous concentrations were measured directly and computed theoretically. Solubility calculations indicate that blood fluoride concentrations that occur in lethal poisonings would decrease calcium below prevailing levels. Acute lethal poisoning and also many of the chronic effects of fluoride involve alterations in the chemical activity of calcium by the fluoride ion. Natural calcium fluoride with low solubility and toxicity from ingestion is distinct from fully soluble toxic industrial fluorides. The toxicity of fluoride is determined by environmental conditions and the positive cations present. At a pH typical of gastric juice, fluoride is largely protonated as hydrofluoric acid HF. Industrial fluoride ingested from treated water enters saliva at levels too low to affect dental caries. Blood levels during lifelong consumption can harm heart, bone, brain, and even developing teeth enamel. The widespread policy known as water fluoridation is discussed in light of these findings.

  19. Current status of fluoride volatility method development

    Energy Technology Data Exchange (ETDEWEB)

    Uhlir, J.; Marecek, M.; Skarohlid, J. [UJV - Nuclear Research Institute, Research Centre Rez, CZ-250 68 Husinec - Rez 130 (Czech Republic)

    2013-07-01

    The Fluoride Volatility Method is based on a separation process, which comes out from the specific property of uranium, neptunium and plutonium to form volatile hexafluorides whereas most of fission products (mainly lanthanides) and higher transplutonium elements (americium, curium) present in irradiated fuel form nonvolatile tri-fluorides. Fluoride Volatility Method itself is based on direct fluorination of the spent fuel, but before the fluorination step, the removal of cladding material and subsequent transformation of the fuel into a powdered form with a suitable grain size have to be done. The fluorination is made with fluorine gas in a flame fluorination reactor, where the volatile fluorides (mostly UF{sub 6}) are separated from the non-volatile ones (trivalent minor actinides and majority of fission products). The subsequent operations necessary for partitioning of volatile fluorides are the condensation and evaporation of volatile fluorides, the thermal decomposition of PuF{sub 6} and the finally distillation and sorption used for the purification of uranium product. The Fluoride Volatility Method is considered to be a promising advanced pyrochemical reprocessing technology, which can mainly be used for the reprocessing of oxide spent fuels coming from future GEN IV fast reactors.

  20. Preparation of potassium tantalum fluoride from tantalum hydroxide

    International Nuclear Information System (INIS)

    Silva, F.T. da; Espinola, A.; Dutra, A.J.B.

    1987-01-01

    Potassium tantalum fluoride (K 2 TaF 7 ) is an intermediary product in the processing of tantaliferous materials; it is the basic raw material for both reduction processes in use presently: reduction by metallic sodium and electrolysis in molten halides. It is normally obtained from a fluorotantalic acid solution to which potassium ions are added the precipitation of white acicular crystals of K 2 TaF 7 . The conditions for precipitation and recrystallization were studied, and crystal characterization were done by scanning electron microscopy, X-ray diffraction and thermogravimetric and thermodifferential analyses. (Author) [pt

  1. Corrosion behavior of zirconia in acidulated phosphate fluoride

    Directory of Open Access Journals (Sweden)

    Anie Thomas

    2016-02-01

    Full Text Available ABSTRACT Objective The corrosion behavior of zirconia in acidulated phosphate fluoride (APF representing acidic environments and fluoride treatments was studied. Material and Methods Zirconia rods were immersed in 1.23% and 0.123% APF solutions and maintained at 37°C for determined periods of time. Surfaces of all specimens were imaged using digital microscopy and scanning electron microscopy (SEM. Sample mass and dimensions were measured for mass loss determination. Samples were characterized by powder X-ray diffraction (XRD to detect changes in crystallinity. A biosensor based on electrochemical impedance spectroscopy (EIS was used to detect ion dissolution of material into the immersion media. Results Digital microscopy revealed diminishing luster of the materials and SEM showed increased superficial corrosion of zirconia submerged in 1.23% APF. Although no structural change was found, the absorption of salts (sodium phosphate onto the surface of the materials bathed in 0.123% APF was significant. EIS indicated a greater change of impedance for the immersion solutions with increasing bathing time. Conclusion Immersion of zirconia in APF solutions showed deterioration limited to the surface, not extending to the bulk of the material. Inferences on zirconia performance in acidic oral environment can be elucidated from the study.

  2. Electrical characteristic of the titanium mesh electrode for transcutaneous intrabody communication to monitor implantable artificial organs.

    Science.gov (United States)

    Okamoto, Eiji; Kikuchi, Sakiko; Mitamura, Yoshinori

    2016-09-01

    We have developed a tissue-inducing electrode using titanium mesh to obtain mechanically and electrically stable contact with the tissue for a new transcutaneous communication system using the human body as a conductive medium. In this study, we investigated the electrical properties of the titanium mesh electrode by measuring electrode-tissue interface resistance in vivo. The titanium mesh electrode (Hi-Lex Co., Zellez, Hyogo, Japan) consisted of titanium fibers (diameter of 50 μm), and it has an average pore size of 200 μm and 87 % porosity. The titanium mesh electrode has a diameter of 5 mm and thickness of 1.5 mm. Three titanium mesh electrodes were implanted separately into the dorsal region of the rat. We measured the electrode-electrode impedance using an LCR meter for 12 weeks, and we calculated the tissue resistivity and electrode-tissue interface resistance. The electrode-tissue interface resistance of the titanium mesh electrode decreased slightly until the third POD and then continuously increased to 75 Ω. The electrode-tissue interface resistance of the titanium mesh electrode is stable and it has lower electrode-tissue interface resistance than that of a titanium disk electrode. The extracted titanium mesh electrode after 12 weeks implantation was fixed in 10 % buffered formalin solution and stained with hematoxylin-eosin. Light microscopic observation showed that the titanium mesh electrode was filled with connective tissue, inflammatory cells and fibroblasts with some capillaries in the pores of the titanium mesh. The results indicate that the titanium mesh electrode is a promising electrode for the new transcutaneous communication system.

  3. Mechanochemistry of titanium oxides

    Directory of Open Access Journals (Sweden)

    Veljković Ivana

    2009-01-01

    Full Text Available Mechanochemistry represents an alternative route in synthesis of nanomaterials. Mechanochemical routes are attractive because of their simplicity, flexibility, and ability to prepare materials by solid state reactions at room temperature. The aim of this work is the mechanochemical synthesis of nanostructured titanium oxides of different composition starting from mixtures of Ti and TiO2, TiO and TiO2 or Ti2O3 and TiO2. Emphasis is on the Magneli phases Ti4O7 and Ti5O9 because their mixture is commercially known as EBONEX material. The materials prepared were characterized by XRPD, TG/DTA analysis, SEM and optical microscopy. Titanium monoxide and several Magneli oxides, Ti4O7, Ti5O9 and Ti6O11, are successfully prepared. The results are very interesting because the EBONEX materials were prepared at lower than usual temperature, which would decrease the effective cost of production.

  4. New Insight on the Response of Bacteria to Fluoride

    OpenAIRE

    Breaker, R.R.

    2012-01-01

    Fluoride has been used for decades to prevent caries and it is well established that this anion can inhibit the growth of bacteria. However, the precise effects that fluoride has on bacteria and the mechanisms that bacteria use to overcome fluoride toxicity have largely remained unexplored. Recently, my laboratory reported the discovery of biological systems that bacteria use to sense fluoride and reduce fluoride toxicity. These sensors and their associated genes are very widespread in biolog...

  5. Physiologic Conditions Affect Toxicity of Ingested Industrial Fluoride

    OpenAIRE

    Richard Sauerheber

    2013-01-01

    The effects of calcium ion and broad pH ranges on free fluoride ion aqueous concentrations were measured directly and computed theoretically. Solubility calculations indicate that blood fluoride concentrations that occur in lethal poisonings would decrease calcium below prevailing levels. Acute lethal poisoning and also many of the chronic effects of fluoride involve alterations in the chemical activity of calcium by the fluoride ion. Natural calcium fluoride with low solubility and toxicity ...

  6. Potential fluoride toxicity from oral medicaments: A review

    OpenAIRE

    Rizwan Ullah; Muhammad Sohail Zafar; Nazish Shahani

    2017-01-01

    The beneficial effects of fluoride on human oral health are well studied. There are numerous studies demonstrating that a small amount of fluoride delivered to the oral cavity decreases the prevalence of dental decay and results in stronger teeth and bones. However, ingestion of fluoride more than the recommended limit leads to toxicity and adverse effects. In order to update our understanding of fluoride and its potential toxicity, we have described the mechanisms of fluoride metabolism, tox...

  7. Fatigue of orthodontic nickel-titanium (NiTi) wires in different fluids under constant mechanical stress

    International Nuclear Information System (INIS)

    Prymak, O.; Klocke, A.; Kahl-Nieke, B.; Epple, M.

    2003-01-01

    The aim of this study was to analyze in vitro the fatigue resistance of nickel-titanium (NiTi) and CuNiTi orthodontic wires when subjected to forces and fluids which are present intraorally. The wires were subjected to dynamic mechanical analysis (DMA) while they were immersed into different fluids with mechanical loading parameters similar to those that are subjected in the mouth. The characteristic temperatures of transitions and a rough surface structure on the perimeter of the wires were determined by differential scanning calorimetry (DSC) and scanning electron microscopy (SEM), respectively, before and after the DMA experiments. Stainless steel wires were used for comparison. In general, NiTi wires fractured earlier than the stainless steel specimens. Survival times were lower for the NiTi wires when immersed in fluids (water, citric acid, NaCl solution, artificial saliva, and fluoridated artificial saliva) than in air. SEM surface analysis showed that the NiTi and CuNiTi wires had a rougher surface than steel wires. The fracture occurred within a short number of loading cycles. Until fracture occurred, the mechanical properties remained mostly constant

  8. Fatigue of orthodontic nickel-titanium (NiTi) wires in different fluids under constant mechanical stress

    Energy Technology Data Exchange (ETDEWEB)

    Prymak, O.; Klocke, A.; Kahl-Nieke, B.; Epple, M

    2003-07-25

    The aim of this study was to analyze in vitro the fatigue resistance of nickel-titanium (NiTi) and CuNiTi orthodontic wires when subjected to forces and fluids which are present intraorally. The wires were subjected to dynamic mechanical analysis (DMA) while they were immersed into different fluids with mechanical loading parameters similar to those that are subjected in the mouth. The characteristic temperatures of transitions and a rough surface structure on the perimeter of the wires were determined by differential scanning calorimetry (DSC) and scanning electron microscopy (SEM), respectively, before and after the DMA experiments. Stainless steel wires were used for comparison. In general, NiTi wires fractured earlier than the stainless steel specimens. Survival times were lower for the NiTi wires when immersed in fluids (water, citric acid, NaCl solution, artificial saliva, and fluoridated artificial saliva) than in air. SEM surface analysis showed that the NiTi and CuNiTi wires had a rougher surface than steel wires. The fracture occurred within a short number of loading cycles. Until fracture occurred, the mechanical properties remained mostly constant.

  9. Effects of storage methods on time-related changes of titanium surface properties and cellular response

    International Nuclear Information System (INIS)

    Lu Haibin; Zhou Lei; Wan Lei; Li Shaobing; Rong Mingdeng; Guo Zehong

    2012-01-01

    Titanium implants are sold in the market as storable medical devices. All the implants have a certain shelf life during which they maintain their sterility, but variations of the surface properties through this duration have not been subject to a comprehensive assessment. The aim of this study was to investigate the effects of storage methods on time-related changes of titanium surface properties. Acid-etched titanium discs (Sa = 0.82 µm) were placed in a sealed container (tradition method) or submerged in the ddH 2 O/NaCl solution (0.15 mol L −1 )/CaCl 2 solution (0.15 mol L −1 ), and new titanium discs were used as a control group. SEM and optical profiler showed that surface morphology and roughness did not change within different groups, but the XPS analysis confirmed that the surface chemistry altered by different storage protocols as the storage duration increased, and the contact angle also varied with storage methods. The storage method also affected the protein adsorption capacity and cellular response on the titanium surface. All titanium discs stored in the solution maintained their excellent bioactivity even after four weeks storage time, but titanium discs stored in a traditional manner decreased substantially in an age-dependent manner. Much effort is needed to improve the storage methods in order to maintain the bioactivity of a titanium dental implant. (paper)

  10. Properties of titanium-alloyed DLC layers for medical applications

    Science.gov (United States)

    Joska, Ludek; Fojt, Jaroslav; Cvrcek, Ladislav; Brezina, Vitezslav

    2014-01-01

    DLC-type layers offer a good potential for application in medicine, due to their excellent tribological properties, chemical resistance, and bio-inert character. The presented study has verified the possibility of alloying DLC layers with titanium, with coatings containing three levels of titanium concentration prepared. Titanium was present on the surface mainly in the form of oxides. Its increasing concentration led to increased presence of titanium carbide as well. The behavior of the studied systems was stable during exposure in a physiological saline solution. Electrochemical impedance spectra practically did not change with time. Alloying, however, changed the electrochemical behavior of coated systems in a significant way: from inert surface mediating only exchange reactions of the environment in the case of unalloyed DLC layers to a response corresponding rather to a passive surface in the case of alloyed specimens. The effect of DLC layers alloying with titanium was tested by the interaction with a simulated body fluid, during which precipitation of a compound containing calcium and phosphorus - basic components of the bone apatite - occurred on all doped specimens, in contrast to pure DLC. The results of the specimens' surface colonization with cells test proved the positive effect of titanium in the case of specimens with a medium and highest content of this element. PMID:25093457

  11. Electrodeposition of amine-terminatedpoly(ethylene glycol) to titanium surface

    International Nuclear Information System (INIS)

    Tanaka, Yuta; Doi, Hisashi; Iwasaki, Yasuhiko; Hiromoto, Sachiko; Yoneyama, Takayuki; Asami, Katsuhiko; Imai, Hachiro; Hanawa, Takao

    2007-01-01

    The immobilization of poly(ethylene glycol), PEG, to a solid surface is useful to functionalize the surface, e.g., to prevent the adsorption of proteins. No successful one-stage technique for the immobilization of PEG to base metals has ever been developed. In this study, PEG in which both terminals or one terminal had been modified with amine bases was immobilized onto a titanium surface using electrodeposition. PEG was dissolved in a NaCl solution, and electrodeposition was carried out at 310 K with - 5 V for 300 min. The thickness of the deposited PEG layer was evaluated using ellipsometry, and the bonding manner of PEG to the titanium surface was characterized using X-ray photoelectron spectroscopy after electrodeposition. The results indicated that a certain amount of PEG was adsorbed on titanium through both electrodeposition and immersion when PEG was terminated by amine. However, terminated amines existed at the surface of titanium and were combined with titanium oxide as N-HO by electrodeposition, while amines randomly existed in the molecule and showed an ionic bond with titanium oxide by immersion. The electrodeposition of PEG was effective for the inhibition of albumin adsorption. This process is useful for materials that have electroconductivity and a complex morphology

  12. Formation of an ascorbate-apatite composite layer on titanium

    Energy Technology Data Exchange (ETDEWEB)

    Ito, Atsuo [National Institute of Advanced Industrial Science and Technology (AIST), Institute for Human Science and Biomedical Engineering, Central 6, Higashi 1-1-1, Tsukuba, Ibaraki 305-8566 (Japan); Sogo, Yu [National Institute of Advanced Industrial Science and Technology (AIST), Institute for Human Science and Biomedical Engineering, Central 6, Higashi 1-1-1, Tsukuba, Ibaraki 305-8566 (Japan); Ebihara, Yuko [School of Science and Technology, Waseda University, 3-4-1 Okubo, Sinjuku-ku, Tokyo 169-8050 (Japan); Onoguchi, Masahiro [School of Science and Technology, Waseda University, 3-4-1 Okubo, Sinjuku-ku, Tokyo 169-8050 (Japan); Oyane, Ayako [National Institute of Advanced Industrial Science and Technology (AIST), Nanotechnology Research Institute, Central 4, Higashi 1-1-1, Tsukuba, Ibaraki 305-8562 (Japan); Ichinose, Noboru [School of Science and Technology, Waseda University, 3-4-1 Okubo, Sinjuku-ku, Tokyo 169-8050 (Japan)

    2007-09-15

    An ascorbate-apatite composite layer was successfully formed on NaOH- and heat-treated titanium by coprecipitating L-ascorbic acid phosphate and low-crystalline apatite in a supersaturated calcium phosphate solution at 37 {sup 0}C for 48 h. The supersaturated calcium phosphate solutions used have chemical compositions attainable by mixing infusion fluids officially approved for clinical use. The amount of immobilized L-ascorbic acid phosphate ranged from 1.0 to 2.3 {mu}g mm{sup -2}, which is most likely to be sufficient for the in vitro osteogenic differentiation of mesenchymal stem cells on titanium. Since ascorbate is important for the collagen synthesis and subsequent osteogenesis of mesenchymal stem cells, titanium coated with the ascorbate-apatite composite layer would be useful as a scaffold in bone tissue engineering and as a bone substitute.

  13. Formation of an ascorbate-apatite composite layer on titanium

    International Nuclear Information System (INIS)

    Ito, Atsuo; Sogo, Yu; Ebihara, Yuko; Onoguchi, Masahiro; Oyane, Ayako; Ichinose, Noboru

    2007-01-01

    An ascorbate-apatite composite layer was successfully formed on NaOH- and heat-treated titanium by coprecipitating L-ascorbic acid phosphate and low-crystalline apatite in a supersaturated calcium phosphate solution at 37 0 C for 48 h. The supersaturated calcium phosphate solutions used have chemical compositions attainable by mixing infusion fluids officially approved for clinical use. The amount of immobilized L-ascorbic acid phosphate ranged from 1.0 to 2.3 μg mm -2 , which is most likely to be sufficient for the in vitro osteogenic differentiation of mesenchymal stem cells on titanium. Since ascorbate is important for the collagen synthesis and subsequent osteogenesis of mesenchymal stem cells, titanium coated with the ascorbate-apatite composite layer would be useful as a scaffold in bone tissue engineering and as a bone substitute

  14. Industrial experience with titanium

    Energy Technology Data Exchange (ETDEWEB)

    Ikeda, B M; Shoesmith, D W

    1997-09-01

    Titanium is a reference material for the construction of waste containers in the Canadian Nuclear Fuel Waste Management Program. It has been in industrial service for over 30 a, often in severe corrosion environments, but it is still considered a relatively exotic material with limited operating history. This has arisen because of the aerospace applications of this material and the misconception that the high strength-to-weight ratio dominates the choice of this material. In fact, the advantage of titanium lies in its high reliability and excellent corrosion resistance. It has a proven record in seawater heat exchanger service and a demonstrated excellent reliability even in polluted water. For many reasons it is the technically correct choice of material for marine applications. In this report we review the industrial service history of titanium, particularly in hot saline environments, and demonstrate that it is a viable waste container material, based upon this industrial service history and operating experience. (author) 83 refs., 17 tabs., 3 figs.

  15. Advances in titanium alloys

    International Nuclear Information System (INIS)

    Seagle, S.R.; Wood, J.R.

    1993-01-01

    As described above, new developments in the aerospace market are focusing on higher temperature alloys for jet engine components and higher strength/toughness alloys for airframe applications. Conventional alloys for engines have reached their maximum useful temperature of about 1000 F (540 C) because of oxidation resistance requirements. IMI 834 and Ti-1100 advanced alloys show some improvement, however, the major improvement appears to be in gamma titanium aluminides which could extend the maximum usage temperature to about 1500 F (815 C). This puts titanium alloys in a competitive position to replace nickel-base superalloys. Advanced airframe alloys such as Ti-6-22-22S, Beta C TM , Ti-15-333 and Ti-10-2-3 with higher strength than conventional Ti-6-4 are being utilized in significantly greater quantities, both in military and commercial applications. These alloys offer improved strength with little or no sacrifice in toughness and improved formability, in some cases. Advanced industrial alloys are being developed for improved corrosion resistance in more reducing and higher temperature environments such as those encountered in sour gas wells. Efforts are focused on small precious metal additions to optimize corrosion performance for specific applications at a modest increase in cost. As these applications develop, the usage of titanium alloys for industrial markets should steadily increase to approach that for aerospace applications. (orig.)

  16. Eukaryotic resistance to fluoride toxicity mediated by a widespread family of fluoride export proteins

    OpenAIRE

    Li, Sanshu; Smith, Kathryn D.; Davis, Jared H.; Gordon, Patricia B.; Breaker, Ronald R.; Strobel, Scott A.

    2013-01-01

    Although fluoride is plentiful in the environment and is commonly used at high concentrations in oral hygiene products, little has been known about how biological systems overcome the toxic effects of this anion. We demonstrate that a protein called FEX in many fungi is essential for cell survival in the presence of high fluoride concentrations. The protein is required for the rapid expulsion of cytoplasmic fluoride, indicating that many eukaryotic species that carry FEX genes likely avoid fl...

  17. Fluoride releasing and enamel demineralization around orthodontic brackets by fluoride-releasing composite containing nanoparticles.

    Science.gov (United States)

    Melo, Mary A S; Morais, Weslanny A; Passos, Vanara F; Lima, Juliana P M; Rodrigues, Lidiany K A

    2014-05-01

    Fluoride-containing materials have been suggested to control enamel demineralization around orthodontic brackets during the treatment with fixed appliances. The improvement of their properties has been made through innovations, such as the application of nanotechnology by incorporation of nanofillers. This in vitro study evaluated the capacity of fluoride releasing and enamel demineralization inhibition of fluoride-releasing nanofilled cement around orthodontic brackets using an artificial caries biofilm model. Forty bovine enamel discs were selected by evaluating surface microhardness and randomized into four groups (n = 10): non-fluoride-releasing microfilled composite, fluoride-releasing microfilled composite, resin-modified glass ionomer cement (RMGI), and fluoride-releasing nanofilled composite (FN). After brackets bonding in each disc, the specimens were subjected to a cariogenic challenge through a Streptococcus mutans biofilm model. After the experimental period, the biofilm formed around the brackets was collected for fluoride analysis and the mineral loss around the brackets was determined by integrated demineralization via cross-sectional microhardness measurement at 20 and 70 μm from the bracket margin. Additionally, samples of each group were subjected to energy-dispersive X-ray spectroscopy (EDX) analysis examined under a scanning electron microscopy (SEM). ANOVA followed by Tukey test were applied for fluoride concentration and mineral loss data, respectively. At both distances, only RMGI statistically differed from the other groups presenting the lowest demineralization, although there was a trend to a lower demineralization of enamel around brackets in FN group. Similar condition was found to fluoride concentration and EDX/SEM analysis. Under the cariogenic exposure condition of this study, the fluoride-releasing nanofilled material had similar performance to fluoride-releasing microfilled materials. The presence of nanofillers in the fluoride

  18. Fluoride exposure and indicators of thyroid functioning in the Canadian population: implications for community water fluoridation.

    Science.gov (United States)

    Barberio, Amanda M; Hosein, F Shaun; Quiñonez, Carlos; McLaren, Lindsay

    2017-10-01

    There are concerns that altered thyroid functioning could be the result of ingesting too much fluoride. Community water fluoridation (CWF) is an important source of fluoride exposure. Our objectives were to examine the association between fluoride exposure and (1) diagnosis of a thyroid condition and (2) indicators of thyroid functioning among a national population-based sample of Canadians. We analysed data from Cycles 2 and 3 of the Canadian Health Measures Survey (CHMS). Logistic regression was used to assess associations between fluoride from urine and tap water samples and the diagnosis of a thyroid condition. Multinomial logistic regression was used to examine the relationship between fluoride exposure and thyroid-stimulating hormone (TSH) level (low/normal/high). Other available variables permitted additional exploratory analyses among the subset of participants for whom we could discern some fluoride exposure from drinking water and/or dental products. There was no evidence of a relationship between fluoride exposure (from urine and tap water) and the diagnosis of a thyroid condition. There was no statistically significant association between fluoride exposure and abnormal (low or high) TSH levels relative to normal TSH levels. Rerunning the models with the sample constrained to the subset of participants for whom we could discern some source(s) of fluoride exposure from drinking water and/or dental products revealed no significant associations. These analyses suggest that, at the population level, fluoride exposure is not associated with impaired thyroid functioning in a time and place where multiple sources of fluoride exposure, including CWF, exist. © Article author(s) (or their employer(s) unless otherwise stated in the text of the article) 2017. All rights reserved. No commercial use is permitted unless otherwise expressly granted.

  19. Effect of dispersed particles of calcium fluoride on the molybdenum solubility in iron

    International Nuclear Information System (INIS)

    Shvejkin, G.P.; Antsiferov, V.N.; Postnikov, V.S.

    1981-01-01

    The results of the investigation of compositions containing 20 at% Mo and 12 vol.% CaF 2 are presented. The sample diffractograms of compositions Fe+20 at% Mo and (Fe+20 at% Mo)+12 vol.% CaF 2 are given. It is shown that the introduction of calcium fluoride results in formation of continuos series of solid solutions of molybdenum in iron. The results of X-ray diffraction investigations on exceeding solubility limit of molybdenum in iron in the presence of calcium fluoride are confirmed

  20. Decontamination of soils and materials containing medium-fired PuO{sub 2} using inhibited fluorides with polymer filtration technology

    Energy Technology Data Exchange (ETDEWEB)

    Temer, D.J.; Villarreal, R.; Smith, B.F. [Los Alamos National Lab., NM (United States)

    1997-10-01

    The decontamination of soils and/or materials from medium-fired plutonium oxide (PuO{sub 2}) with an effective and efficient decontamination agent that will not significantly dissolve the matrix requires a new and innovative technology. After testing several decontamination agents and solutions for dissolution of medium-fired PuO{sub 2}, the most successful decontamination solutions were fluoride compounds, which were effective in breaking the Pu-oxide bond but would not extensively dissolve soil constituents and other materials. The fluoride compounds, tetra fluoboric acid (HBF{sub 4}) and hydrofluorosilicic acid (H{sub 2}F{sub 6}Si), were effective in dissolving medium-fired PuO{sub 2}, and did not seem to have the potential to dissolve the matrix. In both compounds, the fluoride atom is attached to a boron or silicon atom that inhibits the reactivity of the fluoride towards other compounds or materials containing atoms less attracted to the fluoride atom in an acid solution. Because of this inhibition of the reactivity of the fluoride ion, these compounds are termed inhibited fluoride compounds or agents. Both inhibited fluorides studied effectively dissolved medium-fired PuO{sub 2} but exhibited a tendency to not attack stainless steel or soil. The basis for selecting inhibited fluorides was confirmed during leaching tests of medium-fired PuO{sub 2} spiked into soil taken from the Idaho National Engineering Laboratory (INEL). When dissolved in dilute HNO{sub 3}, HCl, or HBr, both inhibited fluoride compounds were effective at solubilizing the medium-fired PuO{sub 2} from spiked INEL soil.

  1. Titanium fasteners. [for aircraft industry

    Science.gov (United States)

    Phillips, J. L.

    1972-01-01

    Titanium fasteners are used in large quantities throughout the aircraft industry. Most of this usage is in aluminum structure; where titanium structure exists, titanium fasteners are logically used as well. Titanium fasteners offer potential weight savings to the designer at a cost of approximately $30 per pound of weight saved. Proper and least cost usage must take into consideration type of fastener per application, galvanic couples and installation characteristics of protective coatings, cosmetic appearance, paint adhesion, installation forces and methods available and fatigue performance required.

  2. Joining of Gamma Titanium Aluminides

    National Research Council Canada - National Science Library

    Baeslack, William

    2002-01-01

    .... Although organized and presented by joining process, many of the observations made and relationships developed, particularly those regarding the weldability and welding metallurgy of gamma titanium...

  3. Development of an environmentally friendly protective coating for the depleted uranium-0.75 wt% titanium alloy

    International Nuclear Information System (INIS)

    Roeper, Donald F.; Chidambaram, Devicharan; Clayton, Clive R.; Halada, Gary P.; Derek Demaree, J.

    2006-01-01

    Molybdenum oxide-based conversion coatings have been formed on the surface of the depleted uranium-0.75 wt% titanium alloy using either concentrated nitric acid or fluorides for surface activation prior to coating formation. The acid-activated surface forms a coating that offers corrosion protection after a period of aging, when uranium species have migrated to the surface. X-ray photoelectron spectroscopy (XPS) revealed that the protective coating is primarily a polymolybdate bound to a uranyl ion. Rutherford backscattering spectroscopy (RBS) on the acid-activated coatings also shows uranium dioxide migrating to the surface. The fluoride-activated surface does not form a protective coating and there are no uranium species on the surface as indicated by XPS. The coating on the fluoride-activated samples has been found to contain a mixture of molybdenum oxides of which the main component is molybdenum trioxide and a minor component of an Mo(V) oxide

  4. Comparative in vitro biocompatibility of nickel-titanium, pure nickel, pure titanium, and stainless steel: genotoxicity and atomic absorption evaluation.

    Science.gov (United States)

    Assad, M; Lemieux, N; Rivard, C H; Yahia, L H

    1999-01-01

    The genotoxicity level of nickel-titanium (NiTi) was compared to that of its pure constituents, pure nickel (Ni) and pure titanium (Ti) powders, and also to 316L stainless steel (316L SS) as clinical reference material. In order to do so, a dynamic in vitro semiphysiological extraction was performed with all metals using agitation and ISO requirements. Peripheral blood lymphocytes were then cultured in the presence of all material extracts, and their comparative genotoxicity levels were assessed using electron microscopy-in situ end-labeling (EM-ISEL) coupled to immunogold staining. Cellular chromatin exposition to pure Ni and 316L SS demonstrated a significantly stronger gold binding than exposition to NiTi, pure Ti, or the untreated control. In parallel, graphite furnace atomic absorption spectrophotometry (AAS) was also performed on all extraction media. The release of Ni atoms took the following decreasing distribution for the different resulting semiphysiological solutions: pure Ni, 316L SS, NiTi, Ti, and controls. Ti elements were detected after elution of pure titanium only. Both pure titanium and nickel-titanium specimens obtained a relative in vitro biocompatibility. Therefore, this quantitative in vitro study provides optimistic results for the eventual use of nickel-titanium alloys as surgical implant materials.

  5. Beryllium fluoride exchange rate accelerated by Mg²⁺ as discovered by ¹⁹F NMR.

    Science.gov (United States)

    Liu, Yixiang; Mao, Xi-an; Liu, Maili; Jiang, Ling

    2015-01-08

    Beryllium fluoride is widely used as a phosphoryl analogue in macromolecular studies, which are not only fluoride-sensitive but also magnesium-dependent. The beryllium fluorides are a mixture of different species including BeF3(-) and BeF4(2-) exchanging under thermodynamic equilibrium in neutral aqueous solutions. In the cases of mimicking phosphate group transfer, both beryllium fluoride and the magnesium ion are generally needed. However, the impact of magnesium on the bioactivity of beryllium fluoride is not clear. We have found by (19)F NMR spectroscopy that Mg(2+) can severely affect the chemical exchange kinetics between BeF3(-) and BeF4(2-). When the F(-) concentration is relatively low, the presence of 10.0 mM Mg(2+) can accelerate the exchange rate 3-4 fold. However, when the F(-) concentration is relatively high, the Mg(2+) effect on the chemical exchange vanishes. On the basis of these findings, we proposed a possible mechanism that BeF4(2-) and Mg(2+) form an ion pair that affects the distribution of beryllium fluoride species and thus the activity in the solution.

  6. Study of interaction of uranium, plutonium and rare earth fluorides with some metal oxides in fluoric salt melts

    International Nuclear Information System (INIS)

    Gorbunov, V.F.; Novoselov, G.P.; Ulanov, S.A.

    1976-01-01

    Interaction of plutonium, uranium, and rare-earth elements (REE) fluorides with aluminium and calcium oxides in melts of eutectic mixture LiF-NaF has been studied at 800 deg C by X-ray diffraction method. It has been shown that tetravalent uranium and plutonium are coprecipitated by oxides as a solid solution UO 2 -PuO 2 . Trivalent plutonium in fluorides melts in not precipitated in the presence of tetravalent uranium which can be used for their separation. REE are precipitated from a salt melt by calcium oxide and are not precipitated by aluminium oxide. Thus, aluminium oxide in a selective precipitator for uranium and plutonium in presence of REE. Addition of aluminium fluoride retains trivalent plutonium and REE in a salt melt in presence of Ca and Al oxides. The mechanism of interacting plutonium and REE trifluorides with metal oxides in fluoride melts has been considered

  7. Fluoride Removal from pretreated Photovoltaic Wastewater by Electrocoagulation: An Investigation of The Effect of Operational Parameters

    KAUST Repository

    Drouiche, Nadjib; Aoudj, Saleh; Lounici, Hakim; Drouiche, M.; Ouslimane, Tarik; Ghaffour, Norredine

    2012-01-01

    In this paper, application of electrocoagulation using common iron electrode to a simulated photovoltaic wastewater after precipitation with lime (Ca(OH)2) was investigated. Electrocoagulation process delivers the coagulant in situ as the sacrificial anode corrodes, while the simultaneous evolution of hydrogen at the cathode allows pollutant removal by flotation. Several working parameters, such as initial pH, applied potential and distance between the electrodes, were studied in an attempt to achieve higher fluoride removal efficiency. The optimum conditions for the process were identified as pH = 6, the distance between electrodes = 1 and an applied potential of 30 V. Furthermore fluoride removal is under the direct discharge standards.Results showed high effectivenessof the electrocoagulation method in removing fluoride from aqueous solutions.

  8. Fluoride Removal from pretreated Photovoltaic Wastewater by Electrocoagulation: An Investigation of The Effect of Operational Parameters

    KAUST Repository

    Drouiche, Nadjib

    2012-03-20

    In this paper, application of electrocoagulation using common iron electrode to a simulated photovoltaic wastewater after precipitation with lime (Ca(OH)2) was investigated. Electrocoagulation process delivers the coagulant in situ as the sacrificial anode corrodes, while the simultaneous evolution of hydrogen at the cathode allows pollutant removal by flotation. Several working parameters, such as initial pH, applied potential and distance between the electrodes, were studied in an attempt to achieve higher fluoride removal efficiency. The optimum conditions for the process were identified as pH = 6, the distance between electrodes = 1 and an applied potential of 30 V. Furthermore fluoride removal is under the direct discharge standards.Results showed high effectivenessof the electrocoagulation method in removing fluoride from aqueous solutions.

  9. Turn-on fluorescence chemosensor for fluoride ions and its applicability in imaging of living cells

    Energy Technology Data Exchange (ETDEWEB)

    Ponnuvel, Kandasamy; Padmini, Vediappen, E-mail: padimini_tamilenthi@yahoo.co.in

    2016-01-15

    The study was easy to prepare fluorescent chemosensor, the urea based triphenylamine conjugated ligand and structurally simple anion probes displayed great selectivity for the fluoride anion over other anions in an aqueous tetrahydrofuran solution. The probe was characterized using NMR spectroscopy, UV–visible, emission spectroscopy and mass spectrometry. The sensor showed spectral shifts and intensity changes in the presence of fluoride anions. The Job’s plot analysis indicates that the binding stoichiometry to be 1:1. Furthermore, by means of confocal fluorescent microscopy experiments, it has been demonstrated that it can be used as a fluorescent probe for monitoring fluoride ions in the living cells. - Highlights: • A novel fluorescent chemosensor for the detection of F{sup −} anions. • Detection of F{sup −} anions can be performed in water at pH=7.4. • The chemosensor could be efficiently delivered to live cells for bioimaging of F{sup −}.

  10. Method for identifying particulate fluoride compounds

    Energy Technology Data Exchange (ETDEWEB)

    Tufts, B J

    1960-01-01

    A method is described for identifying particulates containing fluorides and other complex fluorine compounds such as fluorosilicate in samples collected on membrane filters. The filter is treated with lead chloride to precipitate lead chlorofluoride at each fluoride-containing spot. This microspot is identified by examination in a light microscope. Sulfate and phosphate, which also precipitate if present, can be distinguished and do not interfere. Calibrations are given for the fluorides and the more insoluble salts, relating the original particle size to the reaction site size. Thus, the mass of the particles can be calculated. Results of some field tests in an area of fluoride pollution are given, and compared with standard testing procedures.

  11. Fluoride absorption from the rat urinary bladder: a pH-dependent event

    International Nuclear Information System (INIS)

    Whitford, G.M.; Pashley, D.H.; Reynolds, K.E.

    1977-01-01

    Urinary bladder absorption of stable and radiofluoride was studied as a function of pH in anesthetized rats to further evaluate the influence of pH gradients on fluoride transport. Buffered pH values and stable fluoride concentrations ranged from 1.85 to 7.90 and from 0.012 to 8.81 mM, respectively. [ 14 C]inulin served as a marker for solute concentration changes due to water migration or dilution. The results indicate that bladder fluoride absorption is inversely related to pH over the 1.85 to 5.50 range. Mean, 15-min radiofluoride absorption values of 70 percent at pH 1.85, 37 percent at pH 3.95, and 5 percent at pH 5.50 were observed. These fractional absorption values were not significantly influenced by carrier fluoride concentration, the buffers used, or the presence of urine. Above pH 5.50, pH-independent absorption occurs to a slight extent. The results are consistent with a first-order absorptive process which occurs by the nonionic diffusion of hydrogen fluoride

  12. Fluoride contamination in the lakes region of the Ethiopian rift: origin, mechanism and evolution

    International Nuclear Information System (INIS)

    Travi, Y.; Chernet, T.

    1998-01-01

    The closed lake basins occupying the Main Ethiopian Rift are characterised by unique hydrogeological conditions which have resulted in very high contents of fluoride associated with highly concentrated sodium bicarbonate waters. The origin, mechanism and evolution of fluoride contents have been examined successively by studying (i) the reservoirs which provide this element in solution, (ii) the hydrochemical context, and (iii) the hydrological evolution which modifies the concentrations. Groundwaters of the ignimbrites present low values compared to those of the lacustrine sediments which can provide contents 5 to 10 times greater. The non equilibrium initial stage between the alkalinity and the calcium, derived from weathering of volcanic rocks, is responsible for the specific chemical evolution and the very high fluoride values. Furthermore, in the thermal waters, the high temperatures (especially those up to 100 deg. C) and the presence of large amounts of CO 2 coming from depth increase significantly the fluoride contents. Finally, the fluoride concentrations can change depending on the interrelation of ancient or present surface waters and groundwaters (mixing) and on the hydrological balance (concentration and dilution processes). (author)

  13. Antibacterial Properties of Calcium Fluoride-Based Composite Materials: In Vitro Study

    Science.gov (United States)

    Zarzycka, Beata; Grzegorczyk, Janina; Sokołowski, Krzysztof; Półtorak, Konrad; Sokołowski, Jerzy

    2016-01-01

    The aim of the study was to evaluate antibacterial activity of composite materials modified with calcium fluoride against cariogenic bacteria S. mutans and L. acidophilus. One commercially available conventional light-curing composite material containing fluoride ions (F2) and two commercially available flowable light-curing composite materials (Flow Art and X-Flow) modified with 1.5, 2.5, and 5.0 wt% anhydrous calcium fluoride addition were used in the study. Composite material samples were incubated in 0.95% NaCl at 35°C for 3 days; then dilution series of S. mutans and L. acidophilus strains were made from the eluates. Bacteria dilutions were cultivated on media afterwards. Colony-forming unit per 1 mL of solution (CFU/mL) was calculated. Composite materials modified with calcium fluoride highly reduced (p composite materials containing fluoride compounds. The greatest reduction in bacteria growth was observed for composite materials modified with 1.5% wt. CaF2. All three tested composite materials showed statistically greater antibacterial activity against L. acidophilus than against S. mutans. PMID:28053976

  14. Chemical changes of titanium and titanium dioxide under electron bombardment

    Directory of Open Access Journals (Sweden)

    Romins Brasca

    2007-09-01

    Full Text Available The electron induced effect on the first stages of the titanium (Ti0 oxidation and titanium dioxide (Ti4+ chemical reduction processes has been studied by means of Auger electron spectroscopy. Using factor analysis we found that both processes are characterized by the appearance of an intermediate Ti oxidation state, Ti2O3 (Ti3+.

  15. Plasmonic Titanium Nitride Nanostructures via Nitridation of Nanopatterned Titanium Dioxide

    DEFF Research Database (Denmark)

    Guler, Urcan; Zemlyanov, Dmitry; Kim, Jongbum

    2017-01-01

    Plasmonic titanium nitride nanostructures are obtained via nitridation of titanium dioxide. Nanoparticles acquired a cubic shape with sharper edges following the rock-salt crystalline structure of TiN. Lattice constant of the resulting TiN nanoparticles matched well with the tabulated data. Energy...

  16. Methods for determination of zirconium in titanium alloys

    International Nuclear Information System (INIS)

    1985-01-01

    Two methods for determining zirconium content in titanium alloys are specified in this standard. One is the ion-exchange/mandelic acid gravimetry for Zr content below 20 % down to 1 % while the other is the mandelic acid gravimetry for Zr content below 20 % down to 0.5 %. In the former, a specimen is decomposed by hydrochloric acid and hydrofluoric acid. After substances such as titanium are oxidized by adding nitric acid, the liquid is adjusted into a 4N hydrochloric acid - gN hydrofluoric acid solution, which is them passed through an ion-exchange column. The niobium and tantalum contents are absorbed while the titanium and zirconium contents flow out. Perchloric acid and sulfuric acid are poured in the solution to remove hydrofluoric acid. Aqueous ammonia is added to produce hydroxide of titanium and zirconium, which is then filtered out. The hydroxyde is dissolved in hydrochloric acid, and mandelic acid is poured to precipitate the zirconium content. The precipitate is ignited and the weight of the oxide formed is measured. The coprecipitated titanium content is determined by the absorptiometric method using hydrogen peroxide. Finally, the weight of the oxide is corrected. In the latter determination method, on the other hand, only several steps of the above procedure are used, namely, decomposition by hydrochloric acid, precipitation of zirconium, ignition of precipitate, measurement of oxide weight and weight correction. (Nogami, K.)

  17. Tunable functionality and toxicity studies of titanium dioxide nanotube layers

    International Nuclear Information System (INIS)

    Feschet-Chassot, E.; Raspal, V.; Sibaud, Y.; Awitor, O.K.; Bonnemoy, F.; Bonnet, J.L.; Bohatier, J.

    2011-01-01

    In this study, we have developed a simple process to fabricate scalable titanium dioxide nanotube layers which show a tunable functionality. The titanium dioxide nanotube layers were prepared by electrochemical anodization of Ti foil in 0.4 wt.% hydrofluoric acid solution. The nanotube layers structure and morphology were characterized using X-ray diffraction and scanning electron microscopy. The surface topography and wettability were studied according to the anodization time. The sample synthesized displayed a higher contact angle while the current density reached a local minimum. Beyond this point, the contact angles decreased with anodization time. Photo-degradation of acid orange 7 in aqueous solution was used as a probe to assess the photocatalytic activity of titanium dioxide nanotube layers under UV irradiation. We obtained better photocatalytic activity for the sample fabricated at higher current density. Finally we used the Ciliated Protozoan T. pyriformis, an alternative cell model used for in vitro toxicity studies, to predict the toxicity of titanium dioxide nanotube layers in a biological system. We did not observe any characteristic effect in the presence of the titanium dioxide nanotube layers on two physiological parameters related to this organism, non-specific esterases activity and population growth rate.

  18. Flotation and screening recovery of titanium minerals from a monazite mineral sands circuit

    International Nuclear Information System (INIS)

    Bruckard, W.J.; Heyes, G.W.; Guy, P.J.

    2001-01-01

    Investigations were undertaken to assess the suitability of CSIRO flotation methods for improving the efficiency of separation of heavy minerals in the monazite circuit at the Westralian Sands Limited operations at Capel, Western Australia. Flotation work was conducted on two plant samples. The first was a high-titanium product containing considerable amounts of zircon and silica as quartz and aluminosilicates, and the second was a low monazite/zircon material containing high levels of silica. A three-stage process including reverse flotation was developed to treat the first sample. In this process monazite, zircon, quartz, and aluminosilicates were selectively concentrated by flotation and screening to produce a titanium-rich product. In the first stage, an acid amine float, monazite, zircon, and some non-zircon silica were recovered and in the second stage, an alkaline amine float using a fluoride activator, more quartz and staurolite were floated. The titanium minerals were thus concentrated in the unfloated fraction. In the third stage, the titanium-rich flotation tail was screened at 250 μm to remove the remaining coarse aluminosilicates. In a single pass, the three-stage process yielded a TiO 2 recovery of 64.0 per cent with the titanium-rich product assaying 70.3 per cent TiO 2

  19. Corrosion resistance improvement of titanium base alloys

    Directory of Open Access Journals (Sweden)

    Mihai V. Popa

    2010-01-01

    Full Text Available The corrosion resistance of the new Ti-6Al-4V-1Zr alloy in comparison with ternary Ti-6Al-4V alloy in Ringer-Brown solution and artificial Carter-Brugirard saliva of different pH values was studied. In Ringer-Brown solution, the new alloy presented an improvement of all electrochemical parameters due to the alloying with Zr; also, impedance spectra revealed better protective properties of its passive layer. In Carter-Brugirard artificial saliva, an increase of the passive film thickness was proved. Fluoride ions had a slight negative influence on the corrosion and ion release rates, without to affect the very good stability of the new Ti-6Al-4V-1Zr alloy.

  20. Enhanced compatibility of chemically modified titanium surface with periodontal ligament cells

    International Nuclear Information System (INIS)

    Kado, T.; Hidaka, T.; Aita, H.; Endo, K.; Furuichi, Y.

    2012-01-01

    Highlights: ► Cell-adhesive molecules were covalently immobilized on a Ti surface. ► Immobilized cell-adhesive molecules maintained native function on the Ti surface. ► Immobilized collagen enhanced adhesion of periodontal ligament cells to the Ti. - Abstract: A simple chemical modification method was developed to immobilize cell-adhesive molecules on a titanium surface to improve its compatibility with human periodontal ligament cells (HPDLCs).The polished titanium disk was immersed in 1% (v/v) p-vinylbenzoic acid solution for 2 h to introduce carboxyl groups onto the surface. After rinsing with distilled deionized water, the titanium disk was dipped into 1.47% 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide solution containing 0.1 mg/ml Gly-Arg-Gly-Asp-Ser (GRGDS), human plasma fibronectin (pFN), or type I collagen from calf skin (Col) to covalently immobilize the cell-adhesive molecules on the titanium surface via formation of peptide bonds. X-ray photoelectron spectroscopy analyses revealed that cell-adhesive molecules were successfully immobilized on the titanium surfaces. The Col-immobilized titanium surface revealed higher values regarding nano rough characteristics than the as-polished titanium surface under scanning probe microscopy. The number of HPDLCs attached to both the pFN- and Col-immobilized titanium surfaces was twice that attached to the as-polished titanium surfaces. The cells were larger with the cellular processes that stretched to a greater extent on the pFN- and Col-immobilized titanium surfaces than on the as-polished titanium surface (p < 0.05). HPDLCs on the Col-immobilized titanium surfaces showed more extensive expression of vinculin at the tips of cell projections and more contiguously along the cell outline than on the as-polished, GRGDS-immobilized and pFN-immobilized titanium surfaces. It was concluded that cell-adhesive molecules successfully immobilized on the titanium surface and improved the compatibility of the surface

  1. Hydroxyapatite coating by biomimetic method on titanium alloy ...

    Indian Academy of Sciences (India)

    Unknown

    Abstract. This article reports a biomimetic approach for coating hydroxyapatite on titanium alloy at ambient temperature. In the present study, coating was obtained by soaking the substrate in a 5 times concentrated simulated body fluid (5XSBF) solution for different periods of time with and without the use of CaO–SiO2.

  2. Improved compatibility between polystyrene and poly(vinylidene fluoride) by the addition of urea

    International Nuclear Information System (INIS)

    Melad, O.; Teim, O.A.; Sobeh, E.

    2005-01-01

    The viscosity behavior of dilute urea solution of dimethylformamide (Dmf) of Polystyrene-Poly(vinylidene fluoride) has been studied at 25 degree C. The results show that the polymer mixtures are incompatible in DMF solution in the absence of urea. The influence of urea addition on the degree of compatibility of the polymer mixture has been studied in terms of the compatibility parameters (A6/M, kbm , A [77] ,a and /?) respectively

  3. Fluoride loaded polymeric nanoparticles for dental delivery.

    Science.gov (United States)

    Nguyen, Sanko; Escudero, Carlos; Sediqi, Nadia; Smistad, Gro; Hiorth, Marianne

    2017-06-15

    The overall aim of the present paper was to develop fluoride loaded nanoparticles based on the biopolymers chitosan, pectin, and alginate, for use in dental delivery. First, the preparation of nanoparticles in the presence of sodium fluoride (NaF) as the active ingredient by ionic gelation was investigated followed by an evaluation of their drug entrapment and release properties. Chitosan formed stable, spherical, and monodisperse nanoparticles in the presence of NaF and tripolyphoshate as the crosslinker, whereas alginate and pectin were not able to form any definite nanostructures in similar conditions. The fluoride loading capacity was found to be 33-113ppm, and the entrapment efficiency 3.6-6.2% for chitosan nanoparticles prepared in 0.2-0.4% (w/w) NaF, respectively. A steady increase in the fluoride release was observed for chitosan nanoparticles prepared in 0.2% NaF both in pH5 and 7 until it reached a maximum at time point 4h and maintained at this level for at least 24h. Similar profiles were observed for formulations prepared in 0.4% NaF; however the fluoride was released at a higher level at pH5. The low concentration, but continuous delivery of fluoride from the chitosan nanoparticles, with possible expedited release in acidic environment, makes these formulations highly promising as dental delivery systems in the protection against caries development. Copyright © 2017 Elsevier B.V. All rights reserved.

  4. Well Waters Fluoride in Enugu, Nigeria

    Directory of Open Access Journals (Sweden)

    ISI Ogbu

    2012-03-01

    Full Text Available Abnormal fluoride levels in drinking water have been associated with adverse health effects. To determine the fluoride content of well waters in Enugu, southeastern Nigeria, water samples from 50 artisan wells chosen by multistage sampling procedure from the 5 zones of Enugu municipality were analyzed in duplicates for their fluoride content. The zonal mean values were 0.60, 0.70, 0.62, 0.62, and 0.63 mg/L for Abakpa Nike, Achara Layout, Obiagu/ Ogui, Trans Ekulu and Uwani, respectively (p<0.05. The mean value for the whole city was 0.63 mg/L. Although, the mean level of fluoride recorded in this study is currently within safe limits (1.5 mg/L, WHO 2011, it is important to monitor continuously the fluoride content of well waters in the municipality in view of the increasing industrial activities going on in the city and heavy reliance on well water for domestic purposes and the widespread use of consumer products containing fluoride.

  5. THE USE OF FLUORIDE AND ITS EFFECT ON HEALTH

    Directory of Open Access Journals (Sweden)

    Domen Kanduti

    2016-07-01

    Full Text Available Appropriate oral health care is fundamental for any individual’s health. Dental caries is still one of the major public health problems. The most effective way of caries prevention is the use of fluoride. Fluoride occurs naturally in our environment and is always present in our lives. However, the concentration differs from area to area. Exposure can occur through diet, respiration and fluoride supplements. During pregnancy, the placenta acts as a barrier. The fluoride, therefore, crosses the placenta in low concentrations. Drinking water in Slovenia is not fluoridated; the amount of naturally present fluoride is very low. Fluoride can be toxic in extremely high concentrations. The most important effect of fluoride on caries incidence is through its role in the process of remineralisation and demineralisation of tooth enamel. The European Academy of Paediatric Dentistry (EAPD recommends a preventive topical use of fluoride supplements because of their cariostatic effect. 

  6. The characteristics of corrosion, radiation degradation and dissolution of titanium alloys

    International Nuclear Information System (INIS)

    Sung, K. W.; Na, J. W.; Choi, B. S.; Lee, D. J.; Chang, M. H.

    2001-12-01

    In order to establish the technical bases of water chemistry design requirement related titanium alloys, we investigated the characteristics of corrosion, activation, radiation degradation, radiation hydrogen embrittlement of titanium alloys and dissolution of titanium dioxide. Titanium alloys generally have high corrosion resistance. Corrosion product release from PT-7M and PT-3V titanium alloy surface for 18 months of operation is negligible, and the corrosion penetration for about 30 years is about 1 μm, while the corrosion rates is not higher than one third of that of austenitic steel. Titanium only converts into Sc-46 with 85 day halflife after neutron irradiation, and its radioactivity is not higher than one thousandth of that produced from nickel. Therefore, under the condition without any neutron irradiation, the radiation damage of titanium alloys would have no problem. Titanium dioxide, that protects the metals from the corrosion, has retrograde solubility in neutral solutions. It does not form any complexes with ligands such as ammonia, but Ti(IV) gets more stable by complexing with water molecules. In conclusion, it is estimated that titanium alloys such as PT-7M would be applicable to steam generator materials

  7. Corrosion-resistant titanium nitride coatings formed on stainless steel by ion-beam-assisted deposition

    International Nuclear Information System (INIS)

    Baba, K.; Hatada, R.

    1994-01-01

    Titanium films 70nm thick were deposited on austenitic type 316L stainless steel substrates, and these specimens were irradiated with titanium ions of energy 70kV at a fluence of 1x10 17 ioncm -2 , using a metal vapor vacuum arc (MEVVA) IV metallic ion source at room temperature. After irradiation, titanium nitride (TiN) films were deposited by titanium evaporation and simultaneous irradiation by a nitrogen ion beam, with transport ratios of Ti to N atoms from 0.5 to 10.0 and an ion acceleration voltage of 2kV. The preferred orientation of the TiN films varied from left angle 200 right angle to left angle 111 right angle normal to the surface when the transport ratio was increased. With the help of Auger electron spectroscopy, interfacial mixing was verified. Nitrogen atoms were present in the state of titanium nitride for all transport ratios from 0.5 up to 10.0. However, the chemical bonding state of titanium changed from titanium nitride to the metallic state with increasing transport ratio Ti/N. The corrosion behavior was evaluated in an aqueous solution of sulfuric acid saturated with oxygen, using multisweep cyclic voltammetry measurements. Thin film deposition of pure titanium and titanium implantation prior to TiN deposition have beneficial effects on the suppression of transpassive chromium dissolution. ((orig.))

  8. Physical metallurgy of titanium alloys

    International Nuclear Information System (INIS)

    Collings, E.W.

    1988-01-01

    Researches in electric, magnetic, thermophysical properties of titanium alloys in the wide range of temperatures (from helium upto elevated one), as well as stability of phases in alloys of different types are generalized. Fundamental description of physical properties of binary model alloys is given. Acoustic emission, shape memory and Bauschinger effects, pseudoelasticity, aging and other aspects of physical metallurgy of titanium alloys are considered

  9. Dense and porous titanium substrates with a biomimetic calcium phosphate coating

    Energy Technology Data Exchange (ETDEWEB)

    Ribeiro, A.A., E-mail: aantunesr@yahoo.com.br [Powder Technology Laboratory, Materials Processing and Characterization Division, National Institute of Technology, No. 82 Venezuela Avenue, Room 602, 20081-312 Rio de Janeiro, RJ (Brazil); Balestra, R.M. [Powder Technology Laboratory, Materials Processing and Characterization Division, National Institute of Technology, No. 82 Venezuela Avenue, Room 602, 20081-312 Rio de Janeiro, RJ (Brazil); Rocha, M.N. [Metallurgical and Materials Engineering Program, COPPE, Federal University of Rio de Janeiro, P.O. Box 68505, 21941-972 Rio de Janeiro, RJ (Brazil); Peripolli, S.B. [Materials Metrology Division, National Institute of Metrology, Normalization and Quality, No. 50 Nossa Senhora das Gracas Street, Building 3, 25250-020 Duque de Caxias, RJ (Brazil); Andrade, M.C. [Polytechnic Institute of Rio de Janeiro, Rio de Janeiro State University, s/n, Alberto Rangel Street, 28630-050 Nova Friburgo, RJ (Brazil); Pereira, L.C. [Metallurgical and Materials Engineering Program, COPPE, Federal University of Rio de Janeiro, P.O. Box 68505, 21941-972 Rio de Janeiro, RJ (Brazil); Oliveira, M.V. [Powder Technology Laboratory, Materials Processing and Characterization Division, National Institute of Technology, No. 82 Venezuela Avenue, Room 602, 20081-312 Rio de Janeiro, RJ (Brazil)

    2013-01-15

    Highlights: Black-Right-Pointing-Pointer A biomimetic coating method with simplified solution is proposed. Black-Right-Pointing-Pointer Titanium substrates are submitted to chemical and heat treatments. Black-Right-Pointing-Pointer Titanium substrates are coated with biocompatible calcium phosphate phases. Black-Right-Pointing-Pointer The simplified solution shows potential to be applied as a coating technique. - Abstract: The present work studied a biomimetic method using a simplified solution (SS) with calcium and phosphorus ions for coating titanium substrates, in order to improve their bioactivity. Commercially pure titanium dense sheet, microporous and macroporous titanium samples, both produced by powder metallurgy, were treated in NaOH solution followed by heat-treating and immersed in SS for 7, 14 or 21 days. The samples characterization was performed by quantitative metallographic analysis, confocal scanning optical microscopy, scanning electron microscopy, energy dispersive spectroscopy and low angle X-ray diffraction. The results showed coatings with calcium phosphate precipitation in all samples, with globular or plate-like morphology, typical of hydroxyapatite and octacalcium phosphate, respectively, indicating that the solution (SS) has potential for coating titanium substrates. In addition, the different surfaces of substrates had an effect on the formed calcium phosphate phase and thickness of coatings, depending on the substrate type and imersion time in the simplified solution.

  10. Chemisorption of uranium hexa-fluoride on sodium fluoride pellets

    Energy Technology Data Exchange (ETDEWEB)

    Kalburgi, A K; Sanyal, A; Puranik, V D; Bhattacharjee, B [Chemical Technology Division, Bhabha Atomic Research Centre, Mumbai (India)

    1994-06-01

    This paper comprises kinetics of chemical reaction or rather chemisorption of uranium hexafluoride gas on sodium fluoride pellets. The chemisorption is essentially irreversible at room temperature, while the process reverses at high temperature above 280 deg C. This chemisorption process was experimentally conducted in static condition at room temperature and its kinetics was studied. In the experiments, practically pure UF{sub 6} was used and the effects of gas pressure and weight of NaF pellets, were studied. In this heterogenous reaction, in which diffusion through ash layer is followed by chemical reaction, the reaction part is instantaneous and is first order with respect to gas concentration. Since the process of chemisorption is not only pure chemical reaction but also gas diffusion through ash layer, the rate constant depreciates with the percentage loading of UF{sub 6} on NaF pellets. The kinetic equation for the above process has been established for a particular size of NaF pellets and pellet porosity. (author). 5 refs., 3 figs., 3 tabs.

  11. Titanium for salt water service

    International Nuclear Information System (INIS)

    Gadiyar, H.S.; Shibad, P.R.

    1980-01-01

    Titanium has potential as major material of construction in desalination plants, in condensers and heat exchangers, in view of its excellent corrosion resistance to salt water upto at least 120deg C. The advantages of titanium in such applications are brought out. The various specific problems such as pitting, crevice and galvanic corrosion and the preventive methods, for adopting titanium have been discussed. The hydriding problem can be overcome by suitably controlling the operating parameters such as temperature and surface preparation. A case has been made to prove the economic viability of titanium in comparison to Al-brass and Cu-Ni alloy. The future of titanium seems to be very promising in view of the negligible tube failures and outages. (auth.)

  12. Daily Fluoride Intake from Iranian Green Tea: Evaluation of Various Flavorings on Fluoride Release

    Directory of Open Access Journals (Sweden)

    Afshin Maleki

    2016-01-01

    Full Text Available With increased awareness of the health benefits of the compounds in green tea, especially polyphenols, its consumption is rising. The main purpose of this study is to determine the effect of different additives on the released fluoride into tea liquor and also daily fluoride intake. The concentrations of fluoride, nitrate, sulfate, and chloride were measured in 15 different flavored green teas (Refah-Lahijan. The fluoride and other anion concentrations were measured by ion chromatography method. The data were analyzed with Statistical Package for the Social Sciences version 16.0. The results showed that the minimum and maximum concentrations of fluoride in the green tea infusions were 0.162 mg/L (cinnamon-flavored green tea and 3.29 mg/L (bagged peach-flavored green tea, respectively. The mean concentration of fluoride in the green tea leaves was 52 mg/kg, and approximately 89% of the fluoride was released from the green tea leaves into the infusions after brewing. The fluoride concentrations varied significantly among the examined green teas ( P 0.05. Finally, drinking of the studied green teas cannot make a significant contribution to the daily dietary intake of F for consumers.

  13. Fluoride release, recharge and flexural properties of polymethylmethacrylate containing fluoridated glass fillers.

    Science.gov (United States)

    Al-Bakri, I A; Swain, M V; Naoum, S J; Al-Omari, W M; Martin, E; Ellakwa, A

    2014-06-01

    The purpose of this study was to investigate the effect of fluoridated glass fillers on fluoride release, recharge and the flexural properties of modified polymethylmethacrylate (PMMA). Specimens of PMMA denture base material with various loading of fluoridated glass fillers (0%, 1%, 2.5%, 5% and 10% by weight) were prepared. Flexural properties were evaluated on rectangular specimens (n = 10) aged in deionized water after 24 hours, 1 and 3 months. Disc specimens (n = 10) were aged for 43 days in deionized water and lactic acid (pH 4.0) and fluoride release was measured at numerous intervals. After ageing, specimens were recharged and fluoride re-release was recorded at 1, 3 and 7 days after recharge. Samples containing 2.5%, 5% and 10% glass fillers showed significantly (p glass fillers specimens. All experimental specimens exhibited fluoride release in both media. The flexural strength of specimens decreased in proportion to the percentage filler inclusion with the modulus of elasticity values remaining within ISO Standard 1567. The modified PMMA with fluoridated glass fillers has the ability to release and re-release fluoride ion. Flexural strength decreased as glass filler uploading increased. © 2014 Australian Dental Association.

  14. Fluoride release and cariostatic potential of orthodontic adhesives with and without daily fluoride rinsing.

    NARCIS (Netherlands)

    Chin, M.Y.; Sandham, A.; Rumachik, E.N.; Ruben, J.L.; Huysmans, M.C.D.N.J.M.

    2009-01-01

    INTRODUCTION: In this study, we aimed to evaluate the fluoride-release profiles and caries lesion development in an enamel model with brackets cemented with 4 orthodontic adhesives with and without daily fluoride exposure. METHODS: Four orthodontic adhesives (Ketac Cem mu, 3M ESPE, Seefeld, Germany;

  15. Fluoride release and cariostatic potential of orthodontic adhesives with and without daily fluoride rinsing

    NARCIS (Netherlands)

    Chin, Yeen; Sandham, John; Rumachik, Elena N.; Ruben, Jan L.; Huysmans, Marie-Charlotte D. N. J. M.

    2009-01-01

    Introduction: In this study, we aimed to evaluate the fluoride-release profiles and caries lesion development in an enamel model with brackets cemented with 4 orthodontic adhesives with and without daily fluoride exposure. Methods: Four orthodontic adhesives (Ketac Cem mu, 3M ESPE, Seefeld, Germany;

  16. Oral fluoride levels 1 h after use of a sodium fluoride rinse: effect of sodium lauryl sulfate.

    Science.gov (United States)

    Vogel, Gerald L; Schumacher, Gary E; Chow, Laurence C; Tenuta, Livia M A

    2015-01-01

    Increasing the concentration of free fluoride in oral fluids is an important goal in the use of topical fluoride agents. Although sodium lauryl sulfate (SLS) is a common dentifrice ingredient, the influence of this ion on plaque fluid and salivary fluid fluoride has not been examined. The purpose of this study was to investigate the effect of SLS on these parameters and to examine the effect of this ion on total (or whole) plaque fluoride, an important source of plaque fluid fluoride after a sufficient interval following fluoride administration, and on total salivary fluoride, a parameter often used as a surrogate measure of salivary fluid fluoride. Ten subjects accumulated plaque for 48 h before rinsing with a 12 mmol/l NaF (228 µg/g F) rinse containing or not containing 0.5% (w/w) SLS. SLS had no statistically significant effect on total plaque and total saliva fluoride but significantly increased salivary fluid and plaque fluid fluoride (by 147 and 205%, respectively). These results suggest that the nonfluoride components of topical agents can be manipulated to improve the fluoride release characteristics from oral fluoride reservoirs and that statistically significant change may be observed in plaque fluid and salivary fluid fluoride concentrations that may not be observed in total plaque and total saliva fluoride concentrations.

  17. Widespread genetic switches and toxicity resistance proteins for fluoride.

    Science.gov (United States)

    Baker, Jenny L; Sudarsan, Narasimhan; Weinberg, Zasha; Roth, Adam; Stockbridge, Randy B; Breaker, Ronald R

    2012-01-13

    Most riboswitches are metabolite-binding RNA structures located in bacterial messenger RNAs where they control gene expression. We have discovered a riboswitch class in many bacterial and archaeal species whose members are selectively triggered by fluoride but reject other small anions, including chloride. These fluoride riboswitches activate expression of genes that encode putative fluoride transporters, enzymes that are known to be inhibited by fluoride, and additional proteins of unknown function. Our findings indicate that most organisms are naturally exposed to toxic levels of fluoride and that many species use fluoride-sensing RNAs to control the expression of proteins that alleviate the deleterious effects of this anion.

  18. Influence of the method of fluoride administration on toxicity and fluoride concentrations in Japanese quail

    Science.gov (United States)

    Fleming, W.J.; Schuler, C.A.

    1988-01-01

    Young Japanese quail (Coturnix japonica) were administered NaF for 16 d either in their diet or by esophageal intubation. Based on the total fluoride ion (Emg F-) intake over the l6-d experimental period, fluoride administered by intubation was at least six times more toxic than that fed in the diet. Dietary concentrations of 1,000 ppm F- (Emg F- for 16 d = approx. 144) produced no mortality, whereas intubated doses produced 73% or greater mortality in all groups administered 54 mg F- /kg/d or more (Emg F- for 16 d _ approx. 23 mg). GraphIc companson of the regression of log F- ppm in femurs/mg F- intake showed that fluoride levels in the femurs of quail administered fluoride by intubation were higher than in those administered fluoride in the diet.

  19. The evaluation of organic inhibitors for the protection of grade 5 titanium in chloride media

    International Nuclear Information System (INIS)

    Popa, L.; Tunaru, M.; Velciu, L.

    2013-01-01

    The corrosion failures of titanium and titanium alloys are inevitably associated with the non-observance of environmental limits prescribed in corrosion handbooks, such as its use in solutions chloride. Titanium alloys are often used in the thermal transfer technology especially in the heat exchangers cooled with sea cooled water. However, it is not indicated its use in strong oxidant and any concentrated chloride environments. For the evaluation of grade 5 titanium alloy samples behaviour in solutions containing chloride ions in presence, respectively, absence of some organic inhibitors were performed by potentiodynamic polarization method. On the basis of our experimental results we consider that the most adequate inhibitor for the system Ti- 5 alloys/0 .083 M NaCl solution is the resorcinol. (authors)

  20. Separation of chloride and fluoride from uranium compounds and their determination by ion selective electrodes

    International Nuclear Information System (INIS)

    Pires, M.A.F.; Abrao, A.

    1982-01-01

    Fluoride and chloride must be rigorously controlled in uranium compounds, especially in ceramic grade UO 2 . Their determination is very difficult without previous uranium separation, particularly when both are at a low concentration. A simple procedure is described for this separation using a strong cationic resin to retain the uranyl ion. Both anions are determined in the effluent solution. Uranium compounds of nuclear fuel cycle, especially ammonium diuranate, ammonium uranyl tricarbonate, sodium diuranate, uranium trioxide and dioxide and uranium peroxide are dissolved in nitric acid and the solutions are percolated through the resin column. Chloride and fluoride are determined in the effluent by selective electrodes, the detection limits being 0.02 μg F - /ml and 1.0 μg Cl - /ml. The dissolution of the sample, the acidity of the solution, the measurement conditions and the sensitivity of the method are discussed. (Author) [pt