  1. Preparation and photocatalytic activity of chemically-bonded phosphate ceramics containing TiO2

    Science.gov (United States)

    Martins, Monize Aparecida; de Lima, Bruna de Oliveira; Ferreira, Leticia Patrício; Colonetti, Emerson; Feltrin, Jucilene; De Noni, Agenor

    2017-05-01

    Titanium dioxide was incorporated into chemically-bonded phosphate ceramic for use as photocatalytic inorganic coating. The coatings obtained were applied to unglazed ceramic tiles and cured at 350 °C. The surfaces were characterized by photocatalytic activity, determined in aqueous medium, based on the degradation of methylene blue dye. The effects of the percentage of TiO2 and the thickness of the layer on the photocatalytic efficiency were evaluated. The influence of the incorporation of TiO2 on the consolidation of the phosphate matrix coating was investigated using the wear resistance test. The crystalline phases of the coatings obtained were determined by XRD. The microstructure of the surfaces was analyzed by SEM. The thermal curing treatment did not cause a phase transition from anatase to rutile. An increase in the photocatalytic activity of the coating was observed with an increase in the TiO2 content. The dye degradation indices ranged from 14.9 to 44.0%. The photocatalytic efficiency was not correlated with the thickness of the coating layer deposited. The resistance to wear decreased with an increase in the TiO2 content. Comparison with a commercial photocatalytic ceramic coating indicated that there is a range of values for the TiO2 contents which offer potential for photocatalytic applications.

  2. Functionalized TiO2 nanoparticle containing isocyanate groups

    International Nuclear Information System (INIS)

    Ou, Baoli; Li, Duxin; Liu, Qingquan; Zhou, Zhihua; Liao, Bo

    2012-01-01

    Functionalized TiO 2 nanoparticle containing isocyanate groups can extend the TiO 2 nanoparticle chemistry, and may promote their many potential applications such as in polymer composites and coatings. This paper describes a facile method to prepare functionalized TiO 2 nanoparticle with highly reactive isocyanate groups on its surface, via the reaction between toluene-2, 4-diisocyanate (TDI) and hydroxyl on TiO 2 nanoparticle surface. The main effect factors on the reaction of TiO 2 with TDI were studied by determining the reaction extent of hydroxyl groups on TiO 2 surface. Fourier-transformed infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA) confirmed that reactive isocyanate groups were covalently attached to the TiO 2 nanoparticle surface. The dispersion of the TDI-functionalized TiO 2 nanoparticle was studied by transmission electron microscopy (TEM). Owing to the TDI molecules covalently bonded on TiO 2 nanoparticle surface, it was established that the TiO 2 nanoparticle can be uniformly dispersed in toluene, thus indicating that this functionalization method can prevent TiO 2 nanoparticle from agglomerating. -- Highlights: ► TiO 2 nanoparticle was functionalized with toluene-2, 4-diisocyanate. ► Functionalized TiO 2 nanoparticle can be uniformly dispersed in xylene. ► Compatibility of TiO 2 nanoparticle and organic solvent is significantly improved. ► TiO 2 containing isocyanate groups can extend the TiO 2 nanoparticle chemistry.

  3. Fate of pristine TiO2 nanoparticles and aged paint-containing TiO2 nanoparticles in lettuce crop after foliar exposure.

    Science.gov (United States)

    Larue, Camille; Castillo-Michel, Hiram; Sobanska, Sophie; Trcera, Nicolas; Sorieul, Stéphanie; Cécillon, Lauric; Ouerdane, Laurent; Legros, Samuel; Sarret, Géraldine

    2014-05-30

    Engineered TiO2 nanoparticles (TiO2-NPs) are present in a large variety of consumer products, and are produced in largest amount. The building industry is a major sector using TiO2-NPs, especially in paints. The fate of NPs after their release in the environment is still largely unknown, and their possible transfer in plants and subsequent impacts have not been studied in detail. The foliar transfer pathway is even less understood than the root pathway. In this study, lettuces were exposed to pristine TiO2-NPs and aged paint leachate containing TiO2-NPs and microparticles (TiO2-MPs). Internalization and in situ speciation of Ti were investigated by a combination of microscopic and spectroscopic techniques. Not only TiO2-NPs pristine and from aged paints, but also TiO2-MPs were internalized in lettuce leaves, and observed in all types of tissues. No change in speciation was noticed, but an organic coating of TiO2-NPs is likely. Phytotoxicity markers were tested for plants exposed to pristine TiO2-NPs. No acute phytotoxicity was observed; variations were only observed in glutathione and phytochelatin levels but remained low as compared to typical values. These results obtained on the foliar uptake mechanisms of nano- and microparticles are important in the perspective of risk assessment of atmospheric contaminations. Copyright © 2014 Elsevier B.V. All rights reserved.

  4. Coaxial nanofibers containing TiO2 in the shell for water treatment applications

    Science.gov (United States)

    Kizildag, N.; Geltmeyer, J.; Ucar, N.; De Buysser, K.; De Clerck, K.

    2017-10-01

    In recent years, the basic electrospinning setup has undergone many modifications carried out to enhance the quality and improve the functionality of the resulting nanofibers. Being one of these modifications, coaxial electrospinning has attracted great attention. It enables to use different materials in nanofiber production and produce multi-layered and functional nanofibers in one step. In this study, TiO2 has been added to the shell layer of coaxial nanofibers to develop functional nanofibers which may be used in water treatment applications. The coaxial nanofibers containing TiO2 in the shell layer are compared to uniaxial nanofibers containing TiO2 in bulk fiber structure, regarding their morphology and photocatalytic activity. Uniform uniaxial and coaxial nanofibers with TiO2 were obtained. The average nanofiber diameter of coaxial nanofibers were higher. Coaxial nanofibers, which contained lower amount of TiO2, displayed similar performance to uniaxial nanofibers with TiO2 in terms of photocatalytic degradation ability against isoproturon.

  5. Preparation of Oleyl Phosphate-Modified TiO2/Poly(methyl methacrylate Hybrid Thin Films for Investigation of Their Optical Properties

    Directory of Open Access Journals (Sweden)

    Masato Fujita

    2015-01-01

    Full Text Available TiO2 nanoparticles (NPs modified with oleyl phosphate were synthesized through stable Ti–O–P bonds and were utilized to prepare poly(methyl methacrylate- (PMMA- based hybrid thin films via the ex situ route for investigation of their optical properties. After surface modification of TiO2 NPs with oleyl phosphate, IR and 13C CP/MAS NMR spectroscopy showed the presence of oleyl groups. The solid-state 31P MAS NMR spectrum of the product revealed that the signal due to oleyl phosphate (OP shifted upon reaction, indicating formation of covalent Ti–O–P bonds. The modified TiO2 NPs could be homogeneously dispersed in toluene, and the median size was 16.1 nm, which is likely to be sufficient to suppress Rayleigh scattering effectively. The TEM images of TiO2/PMMA hybrid thin films also showed a homogeneous dispersion of TiO2 NPs, and they exhibited excellent optical transparency even though the TiO2 content was 20 vol%. The refractive indices of the OP-modified TiO2/PMMA hybrid thin films changed higher with increases in TiO2 volume fraction, and the hybrid thin film with 20 vol% of TiO2 showed the highest refractive index (n = 1.86.

  6. Promising psyllium-based composite containing TiO2 nanoparticles as aspirin-carrier matrix

    Directory of Open Access Journals (Sweden)

    Marcela-Corina Rosu

    2014-06-01

    Full Text Available Composite nanomaterials represent a new trend in the biomedical field. Coupling inorganic/organic constituents with non-toxicity/biocompatibility properties leads to develop the new systems having special characteristics that can be used in various bio-applications. This paper describes the preparation and characterization of psyllium-based composites containing TiO2 nanoparticles in order to develop new therapeutic strategies for aspirin drug delivery. The structural characteristics of obtained materials were investigated by FTIR spectroscopy. The UV–vis spectrophotometric analysis was performed to evaluate the aspirin release behavior under different pH conditions at 37 °C. Combining psyllium (as an excellent source of fiber with TiO2 inorganic unit (as vehicle of aspirin it was found that polymeric-TiO2 networks have promising potential for controlled aspirin release as therapeutic agent.

  7. Testing of Flame Sprayed Al2O3 Matrix Coatings Containing TiO2

    Directory of Open Access Journals (Sweden)

    Czupryński A.

    2016-09-01

    Full Text Available The paper presents the results of the properties of flame sprayed ceramic coatings using oxide ceramic materials coating of a powdered aluminium oxide (Al2O3 matrix with 3% titanium oxide (TiO2 applied to unalloyed S235JR grade structural steel. A primer consisting of a metallic Ni-Al-Mo based powder has been applied to plates with dimensions of 5×200×300 mm and front surfaces of Ø40×50 mm cylinders. Flame spraying of primer coating was made using a RotoTec 80 torch, and an external coating was made with a CastoDyn DS 8000 torch. Evaluation of the coating properties was conducted using metallographic testing, phase composition research, measurement of microhardness, substrate coating adhesion (acc. to EN 582:1996 standard, erosion wear resistance (acc. to ASTM G76-95 standard, and abrasive wear resistance (acc. to ASTM G65 standard and thermal impact. The testing performed has demonstrated that flame spraying with 97% Al2O3 powder containing 3% TiO2 performed in a range of parameters allows for obtaining high-quality ceramic coatings with thickness up to ca. 500 µm on a steel base. Spray coating possesses a structure consisting mainly of aluminium oxide and a small amount of NiAl10O16 and NiAl32O49 phases. The bonding primer coat sprayed with the Ni-Al-Mo powder to the steel substrate and external coating sprayed with the 97% Al2O3 powder with 3% TiO2 addition demonstrates mechanical bonding characteristics. The coating is characterized by a high adhesion to the base amounting to 6.5 MPa. Average hardness of the external coating is ca. 780 HV. The obtained coatings are characterized by high erosion and abrasive wear resistance and the resistance to effects of cyclic thermal shock.

  8. Photocatalytic degradation of NOx gases using TiO2-containing paint: a real scale study.

    Science.gov (United States)

    Maggos, Th; Bartzis, J G; Liakou, M; Gobin, C

    2007-07-31

    An indoor car park was appropriately equipped in order to test the de-polluting efficiency of a TiO(2)-containing paint in an indoor polluted environment, under real scale configuration. Depollution tests were performed in an artificially closed area of the parking, which was polluted by a car exhaust during the testing period. The ceiling surface of the car park was covered with white acrylic TiO(2)-containing paint (PP), which was developed in the frame of the EU project 'PICADA' (Photocatalytic Innovative Coverings Application for Depollution Assessment). The closed area was fed with car exhaust gases. As soon as the system reached steady state, the UV lamps were turned on for 5h. The difference between the final and the initial steady state concentration indicates the removal of the pollutants due to both the photocatalytic paint and car emission reduction. Results showed a significant photocatalytic oxidation of NO(x) gases. The photocatalytic removal of NO and NO(2) was calculated to 19% and 20%, respectively, while the photocatalytic rate (microgm(-2)s(-1)) ranged between 0.05 and 0.13 for NO and between 0.09 and 0.16 for NO(2).

  9. Preparation of TiO2 thin films from autoclaved sol containing needle-like anatase crystals

    International Nuclear Information System (INIS)

    Ge Lei; Xu Mingxia; Fang Haibo; Sun Ming

    2006-01-01

    A new inorganic sol-gel method was introduced in this paper to prepare TiO 2 thin films. The autoclaved sol with needle-like anatase crystals was synthesized using titanyl sulfate (TiOSO 4 ) and peroxide (H 2 O 2 ) as starting materials. The transparent anatase TiO 2 thin films were prepared on glass slides from the autoclaved sol by sol-gel dip-coating method. A wide range of techniques such as Fourier transform infrared transmission spectra (FT-IR), X-ray diffraction (XRD), thermogravimetry-differential thermal analysis (TG-DTA), scanning electron microscopes, X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible spectrum were applied to characterize the autoclaved sol and TiO 2 thin films. The results indicate that the autoclaved sol is flavescent, semitransparent and stable at room temperature. The anatase crystals of TiO 2 films connect together to form net-like structure after calcined and the films become uniform with increasing heating temperature. The surface of the TiO 2 films contain not only Ti and O elements, but also a small amount of N and Na elements diffused from substrates during heat treatment. The TiO 2 films are transparent and their maximal light transmittances exceed 80% under visible light region

  10. Phosphate glasses, containing nitrogen

    International Nuclear Information System (INIS)

    Lisitsyna, E.A.; Khalilev, V.D.; Koryavin, A.A.; Goncharova, L.N.

    1987-01-01

    Possibilities of nitrogen-containing glass synthesis by the introduction into the charge of ammonium salts, as well as aluminium nitride, are studied. Zinc alumoyttrium phosphate glass (mol. %) Zn(PO 3 ) 2 - 4O, Al(PO 3 ) 3 - 3O, Y(PO 3 ) 3 -3O is suggested as a matrix. It is shown that the effect of amide and imide groups on the properties of the glass is less noticeable than the effect of nitride groups. Direct introduction of nitride constituent was realized using AlN, but aluminium introduction was taken into account so that the oxide was subtracted. The attempt to introduce more than 2.5 mass % of nitrogen into initial matrix by aluminium nitride has failed due to repeated restoration of glass with amorphous phosphorus isolation

  11. Preparation and characterization of TiO2 and Si-doped octacalcium phosphate composite coatings on zirconia ceramics (Y-TZP) for dental implant applications

    Science.gov (United States)

    Bao, Lei; Liu, Jingxiao; Shi, Fei; Jiang, Yanyan; Liu, Guishan

    2014-01-01

    In order to prevent the low temperature degradation and improve the bioactivity of zirconia ceramic implants, TiO2 and Si-doped octacalcium phosphate composite coating was prepared on zirconia substrate. The preventive effect on low temperature degradation and surface morphology of the TiO2 layer were studied. Meanwhile, the structure and property changes of the bioactive coating after doping Si were discussed. The results indicate that the dense TiO2 layer, in spite of some microcracks, inhibited the direct contact of the water vapor with the sample's surface and thus prevented the low temperature degradation of zirconia substrates. The acceleration aging test shows that the ratio of the monoclinic phase transition decreased from 10% for the original zirconia substrate to 4% for the TiO2-coated substrate. As to the Si-doped octacalcium phosphate coating prepared by biomimetic method, the main phase composition of the coating was octacalcium phosphate. The morphology of the coating was lamellar-like, and the surface was uniform and continuous with no cracks being observed. It is suggested that Si was added into the coating both through substituting for PO43- and doping as NaSiO3.

  12. Phosphate Changes Effect of Humic Acids on TiO2 Photocatalysis: From Inhibition to Mitigation of Electron-Hole Recombination.

    Science.gov (United States)

    Long, Mingce; Brame, Jonathon; Qin, Fan; Bao, Jiming; Li, Qilin; Alvarez, Pedro J J

    2017-01-03

    A major challenge for photocatalytic water purification with TiO 2 is the strong inhibitory effect of natural organic matter (NOM), which can scavenge photogenerated holes and radicals and occlude ROS generation sites upon adsorption. This study shows that phosphate counteracts the inhibitory effect of humic acids (HA) by decreasing HA adsorption and mitigating electron-hole recombination. As a measure of the inhibitory effect of HA, the ratios of first-order reaction rate constants between photocatalytic phenol degradation in the absence versus presence of HA were calculated. This ratio was very high, up to 5.72 at 30 mg/L HA and pH 4.8 without phosphate, but was decreased to 0.76 (5 mg/L HA, pH 8.4) with 2 mM phosphate. The latter ratio indicates a surprising favorable effect of HA on TiO 2 photocatalysis. FTIR analyses suggest that this favorable effect is likely due to a change in the conformation of adsorbed HA, from a multiligand exchange arrangement to a complexation predominantly between COOH groups in HA and the TiO 2 surface in the presence of phosphate. This configuration can reduce hole consumption and facilitate electron transfer to O 2 by the adsorbed HA (indicated by linear sweep voltammetry), which mitigates electron-hole recombination and enhances contaminant degradation. A decrease in HA surface adsorption and hole scavenging (the predominant inhibitory mechanisms of HA) by phosphate (2 mM) was indicated by a 50% decrease in the photocatalytic degradation rate of HA and 80% decrease in the decay rate coefficient of interfacial-related photooxidation in photocurrent transients. These results, which were validated with other compounds (FFA and cimetidine), indicate that anchoring phosphate - or anions that exert similar effects on the TiO 2 surface - might be a feasible strategy to counteract the inhibitory effect of NOM during photocatalytic water treatment.

  13. Photocatalytic properties of aqueous systems containing TiO2 nanoparticles

    Czech Academy of Sciences Publication Activity Database

    Paušová, Š.; Krýsa, J.; Jirkovský, Jaromír; Forano, C.; Prevot, V.; Mailhot, G.

    2011-01-01

    Roč. 161, č. 1 (2011), s. 140-146 ISSN 0920-5861 R&D Projects: GA MŠk 1M0577 Institutional research plan: CEZ:AV0Z40400503 Keywords : TiO2 nanoparticles * photocatalysis * aging Subject RIV: CG - Electrochemistry Impact factor: 3.407, year: 2011

  14. Topography and surface energy dependent calcium phosphate formation on Sol-Gel derived TiO2 coatings.

    Science.gov (United States)

    Järn, Mikael; Areva, Sami; Pore, Viljami; Peltonen, Jouko; Linden, Mika

    2006-09-12

    Heterogeneous nucleation and growth of calcium phosphate (CaP) on sol-gel derived TiO(2) coatings was investigated in terms of surface topography and surface energy. The topography of the coatings was derived from AFM measurements, while the surface energy was determined with contact angle measurements. The degree of precipitation was examined with scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The precipitation of CaP was found to be dependent on both topography and surface energy. A high roughness value when combining the RMS roughness parameter S(q) with the number of local maxima per unit area parameter S(ds) enhances CaP formation. The hydrophilicity of the coating was also found to be of importance for CaP formation. We suggest that the water contact angle, which is a direct measure of the hydrophilicity of the surface, may be used to evaluate the surface energy dependent precipitation kinetics rather than using the often applied Lewis base parameter.

  15. Development of TiO2 containing hardmasks through plasma-enhanced atomic layer deposition

    Science.gov (United States)

    De Silva, Anuja; Seshadri, Indira; Chung, Kisup; Arceo, Abraham; Meli, Luciana; Mendoza, Brock; Sulehria, Yasir; Yao, Yiping; Sunder, Madhana; Truong, Hoa; Matham, Shravan; Bao, Ruqiang; Wu, Heng; Felix, Nelson M.; Kanakasabapathy, Sivananda

    2017-04-01

    With the increasing prevalence of complex device integration schemes, trilayer patterning with a solvent strippable hardmask can have a variety of applications. Spin-on metal hardmasks have been the key enabler for selective removal through wet strip when active areas need to be protected from dry etch damage. As spin-on metal hardmasks require a dedicated track to prevent metal contamination and are limited in their ability to scale down thickness without compromising on defectivity, there has been a need for a deposited hardmask solution. Modulation of film composition through deposition conditions enables a method to create TiO2 films with wet etch tunability. This paper presents a systematic study on development and characterization of plasma-enhanced atomic layer deposited (PEALD) TiO2-based hardmasks for patterning applications. We demonstrate lithographic process window, pattern profile, and defectivity evaluation for a trilayer scheme patterned with PEALD-based TiO2 hardmask and its performance under dry and wet strip conditions. Comparable structural and electrical performance is shown for a deposited versus a spin-on metal hardmask.

  16. Development of TiO2 containing hardmasks through PEALD deposition

    Science.gov (United States)

    De Silva, Anuja; Seshadri, Indira; Chung, Kisup; Arceo, Abraham; Meli, Luciana; Mendoza, Brock; Sulehria, Yasir; Yao, Yiping; Sunder, Madhana; Truong, Hao; Matham, Shravan; Bao, Ruqiang; Wu, Heng; Felix, Nelson M.; Kanakasabapathy, Sivananda

    2017-03-01

    With the increasing prevalence of complex device integration schemes, tri layer patterning with a solvent strippable hardmask can have a variety of applications. Spin-on metal hardmasks have been the key enabler for selective removal through wet strip when active areas need to be protected from dry etch damage. As spin-on metal hardmasks require a dedicated track to prevent metal contamination, and are limited in their ability to scale down thickness without comprising on defectivity, there has been a need for a deposited hardmask solution. Modulation of film composition through deposition conditions enables a method to create TiO2 films with wet etch tunability. This paper presents a systematic study on development and characterization of PEALD deposited TiO2-based hardmasks for patterning applications. We demonstrate lithographic process window, pattern profile, and defectivity evaluation for a tri layer scheme patterned with PEALD based TiO2 hardmask and its performance under dry and wet strip conditions. Comparable structural and electrical performance is shown for a deposited vs a spin-on metal hardmask.

  17. Study on the water durability of zinc boro-phosphate glasses doped with MgO, Fe2O3, and TiO2

    Science.gov (United States)

    Hwang, Moon Kyung; Ryu, Bong Ki

    2016-07-01

    The water durability of zinc boro-phosphate (PZB) glasses with the composition 60P2O5-20ZnO-20B2O3- xMeO ( x = 0, 2, 4, 6 and MeO = MgO, Fe2O3, or TiO2) (mol%) was measured, and PZB glass was studied in terms of its thermal properties, density, and FTIR characteristics. The surface conditions and corrosion byproducts were analyzed using scanning electron microscopy. When MgO, Fe2O3, and TiO2 were doped into the PZB glass, Q2 was decreased and Q1 was increased in the phosphate structure, while the number of BO4 structures increased with increasing MeO content. The density of the PZB glass was increased by the addition of Fe2O3 and TiO2, while the glass transition temperature ( T g ) and dilatometric softening temperature ( T d ) were increased when additional MgO, Fe2O3, and TiO2 were added. From the weight loss analysis (95 ◦ C, 96 h), TiO2 doped glass showed the lowest weight loss (1.70 × 10 -3 g/cm2) while MgO doped glass showed the highest value (2.44 × 10 -3 g/cm2), compared with PZB glass (3.07 × 10 -3 g/cm2). These results were discussed in terms of the Me n+ ions in the glass structure, and their different coordination numbers and bonding strengths.

  18. Synthesis of molecularly imprinted photocatalysts containing low TiO_2 loading: Evaluation for the degradation of pharmaceuticals

    International Nuclear Information System (INIS)

    Coelho de Escobar, Cícero; Lansarin, Marla Azário; Zimnoch dos Santos, João Henrique

    2016-01-01

    Highlights: • Molecularly imprinted photocatalyst (MIP) containing low TiO_2 loading were prepared by acid-catalyzed sol–gel process. • Seven pharmaceutical compounds were evaluated as a template. • Comparing to the P25, MIP has shown an increase of adsorption up to 752%. • Comparing to the P25, MIP has shown an increase of degradation up to 427%. • The presence of specific cavities on the silica domain could explain the better results for MIP. - Abstract: A molecularly imprinted (MI) photocatalyst containing a low TiO_2 loading (7.00–16.60 mg L"−"1 of TiO_2) was prepared via an acid-catalyzed sol–gel route using different classes of pharmaceutical compounds (i.e., Atorvastatin, Diclofenac, Ibuprofen, Tioconazole, Valsartan, Ketoconazole and Gentamicine) as the template. Herein, our main goal was to test the hypothesis that photocatalysts based on molecular imprinting may improve the degradation performance of pharmaceutical compounds compared to that of a commercial sample (Degussa P25) due to presence of specific cavities in the silica domain. To elucidate certain trends between the performance of photocatalysts and their structural and textural properties, as well the effect of the structure of the drugs on molecular imprinting, the data were analyzed in terms of pore diameter, pore volume, surface area, zeta potential and six-membered ring percentage of silica. In comparison to the commercial sample (P25), we have shown that adsorption and degradation were enhanced from 48 to 752% and from 5 to 427%, respectively. A comparison with the control system (non-imprinted) indicates that the increased performance of the MI systems was due to the presence of specific cavities on the silica domain, and the textural and structural aspects also support this conclusion. The MI photocatalyst was reusable for seven cycles of reuse in which approximately 60% of its photocatalytic efficiency was preserved for the system containing Diclofenac as the template.

  19. Enhanced photoelectrochemical properties of F-containing TiO2 sphere thin film induced by its novel hierarchical structure

    International Nuclear Information System (INIS)

    Dong Xiang; Tao Jie; Li Yingying; Zhu Hong

    2009-01-01

    The novel nanostructured F-containing TiO 2 (F-TiO 2 ) sphere was directly synthesized on the surface of Ti foil in the solution of NH 4 F and HCl by one-step hydrothermal approach under low-temperature condition. The samples were characterized respectively by means of field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The results showed that the F-TiO 2 sphere was hierarchical structure, which composed of porous octahedron crystals with one truncated cone, leading to a football-like morphology. XPS results indicated that F - anions were just physically adsorbed on the surface of TiO 2 microspheres. The studies on the optical properties of the F-TiO 2 were carried out by UV-vis light absorption spectrum. The surface fluorination of the spheres, the unique nanostructure induced accessible macropores or mesopores, and the increased light-harvesting abilities were crucial for the high photoelectrochemical activity of the synthesized F-TiO 2 sphere for water-splitting. The photocurrent density of the F-TiO 2 sphere thin film was more than two times than that of the P25 thin film. Meanwhile, a formation mechanism was briefly proposed. This approach could provide a facile method to synthesize F-TiO 2 microsphere with a special morphology and hierarchical structure in large scale.

  20. Monitoring of TiO2-catalytic UV-LED photo-oxidation of cyanide contained in mine wastewater and leachate.

    Science.gov (United States)

    Kim, Seong Hee; Lee, Sang Woo; Lee, Gye Min; Lee, Byung-Tae; Yun, Seong-Taek; Kim, Soon-Oh

    2016-01-01

    A photo-oxidation process using UV-LEDs and TiO2 was studied for removal of cyanide contained in mine wastewater and leachates. This study focused on monitoring of a TiO2-catalyzed LED photo-oxidation process, particularly emphasizing the effects of TiO2 form and light source on the efficiency of cyanide removal. The generation of hydroxyl radicals was also examined during the process to evaluate the mechanism of the photo-catalytic process. The apparent removal efficiency of UV-LEDs was lower than that achieved using a UV-lamp, but cyanide removal in response to irradiation as well as consumption of electrical energy was observed to be higher for UV-LEDs than for UV-lamps. The Degussa P25 TiO2 showed the highest performance of the TiO2 photo-catalysts tested. The experimental results indicate that hydroxyl radicals oxidize cyanide to OCN(-), NO2(-), NO3(-), HCO3(-), and CO3(2-), which have lower toxicity than cyanide. In addition, the overall efficacy of the process appeared to be significantly affected by diverse operational parameters, such as the mixing ratio of anatase and rutile, the type of gas injected, and the number of UV-LEDs used. Copyright © 2015 Elsevier Ltd. All rights reserved.

  1. The roles of phosphate and tungstate species in surface acidities of TiO2-ZrO2 binary oxides - A comparison study

    Science.gov (United States)

    Chaudhary, Manchal; Shen, Po-fan; Chang, Sue-min

    2018-05-01

    Porous tungstated and phosphated TiO2-ZrO2 (TZ) binary oxides with high and strong acidity were successfully prepared by means of sol-gel or impregnation approaches. In addition, the influences of the two types of modifiers on the microstructures and acidity were systematically examined, compared, and clarified. The TZ oxide derived from a surfactant-templating method exhibited a high surface area of 195 m2/g with a pore size of 6.3 nm. Moreover, it had a high acidity of 859 μmol/g with a density of 4.4 μmol/nm2 because of defective surface. Phosphation significantly increased the acidity to 1547 μmol/g and showed the highest acid density of 6.7 μmol/nm2 at a surface P density of 22.7P/nm2. On the other hand, tungstated compounds just showed the highest acidity of 972 μmol/g and the highest acid density of 4.8 μmol/nm2 at 4.7 W/nm2. Compared to tungstate species, phosphate anions are more capable of promoting the acidity because they are able to distort the host network and inhibit elemental rearrangement. While Lewis acidity prevailed in the tungstated compounds, Brønsted acidity was dominant in the phosphated oxides. The Wdbnd O and Psbnd OH groups were responsible for strong acidity in the modified compounds. Phosphated compounds formed strong Brønsted acid sites on the Psbnd OH groups with a particular strength, and tungstation produced Lewis acid sites with a continuous strength on the metal ions adjacent to the tungstate moieties. Cyclic NH3 adsorption-desorption processes revealed that the active sites for NH3 adsorption were stable in both the tungstate and phosphate modified compounds, revealing that these solid acids are promising as the adsorbents for removal of base gases.

  2. Photocatalytic and antibacterial properties of a TiO2/nylon-6 electrospun nanocomposite mat containing silver nanoparticles

    International Nuclear Information System (INIS)

    Pant, Hem Raj; Pandeya, Dipendra Raj; Nam, Ki Taek; Baek, Woo-il; Hong, Seong Tshool; Kim, Hak Yong

    2011-01-01

    Silver-impregnated TiO 2 /nylon-6 nanocomposite mats exhibit excellent characteristics as a filter media with good photocatalytic and antibacterial properties and durability for repeated use. Silver nanoparticles (NPs) were successfully embedded in electrospun TiO 2 /nylon-6 composite nanofibers through the photocatalytic reduction of silver nitrate solution under UV-light irradiation. TiO 2 NPs present in nylon-6 solution were able to cause the formation of a high aspect ratio spider-wave-like structure during electrospinning and facilitated the UV photoreduction of AgNO 3 to Ag. TEM images, UV-visible and XRD spectra confirmed that monodisperse Ag NPs (approximately 4 nm in size) were deposited selectively upon the TiO 2 NPs of the prepared nanocomposite mat. The antibacterial property of a TiO 2 /nylon-6 composite mat loaded with Ag NPs was tested against Escherichia coli, and the photoactive property was tested against methylene blue. All of the results showed that TiO 2 /nylon-6 nanocomposite mats loaded with Ag NPs are more effective than composite mats without Ag NPs. The prepared material has potential as an economically friendly photocatalyst and water filter media because it allows the NPs to be reused.

  3. Surface properties of anatase TiO2 nanowire films grown from a fluoride-containing solution.

    Science.gov (United States)

    Berger, Thomas; Anta, Juan A; Morales-Flórez, Víctor

    2013-06-03

    Controlling the surface chemistry of nucleating seeds during wet-chemical synthesis allows for the preparation of morphologically well-defined nanostructures. Synthesis conditions play a key role in the surface properties, which directly affect the functional properties of the material. Therefore, it is important to establish post-synthesis treatments to facilitate the optimization of surface properties with respect to a specific application, without losing the morphological peculiarity of the nanostructure. We studied the surface properties of highly crystalline and porous anatase TiO2 nanowire (NW) electrodes, grown by chemical-bath deposition in fluoride-containing solutions, using a combined electrochemical and spectroscopic approach. As-deposited films showed low capacity for catechol adsorption and a poor photoelectrocatalytic activity for water oxidation. Mild thermal annealing at 200 °C resulted in a significant improvement of the electrode photoelectrocatalytic activity, whereas the bulk properties of the NWs (crystal structure, band-gap energy) remained unchanged. Enhancement of the functional properties of the material is discussed on the basis of adsorption capacity and electronic properties. The temperature-induced decrease of recombination centers, along with the concomitant increase of adsorption and reaction sites upon thermal annealing are called to be responsible for such improved performance. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  4. Phosphate Recovery From Sewage Sludge Containing Iron Phosphate

    NARCIS (Netherlands)

    Wilfert, P.K.

    2018-01-01

    The scope of this thesis was to lay the basis for a phosphate recovery technology that can be applied on sewage sludge containing iron phosphate. Such a technology should come with minimal changes to the existing sludge treatment configuration while keeping the use of chemicals or energy as small as

  5. Synthesis of TiO2 nanoparticles containing Fe, Si, and V using multiple diffusion flames and catalytic oxidation capability of carbon-coated nanoparticles

    KAUST Repository

    Ismail, Mohamed

    2016-01-19

    Titanium dioxide (TiO2) nanoparticles containing iron, silicon, and vanadium are synthesized using multiple diffusion flames. The growth of carbon-coated (C–TiO2), carbon-coated with iron oxide (Fe/C–TiO2), silica-coated (Si–TiO2), and vanadium-doped (V–TiO2) TiO2 nanoparticles is demonstrated using a single-step process. Hydrogen, oxygen, and argon are utilized to establish the flame, with titanium tetraisopropoxide (TTIP) as the precursor for TiO2. For the growth of Fe/C–TiO2 nanoparticles, TTIP is mixed with xylene and ferrocene. While for the growth of Si–TiO2 and V–TiO2, TTIP is mixed with hexamethyldisiloxane (HMDSO) and vanadium (V) oxytriisopropoxide, respectively. The synthesized nanoparticles are characterized using high-resolution transmission electron microscopy (HRTEM) with energy-filtered TEM for elemental mapping (of Si, C, O, and Ti), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), nitrogen adsorption BET surface area analysis, and thermogravimetric analysis. Anatase is the dominant phase for the C–TiO2, Fe/C–TiO2, and Si–TiO2 nanoparticles, whereas rutile is the dominant phase for the V–TiO2 nanoparticles. For C–TiO2 and Fe/C–TiO2, the nanoparticles are coated with about 3-5-nm thickness of carbon. The iron-based TiO2 nanoparticles significantly improve the catalytic oxidation of carbon, where complete oxidation of carbon occurs at a temperature of 470 °C (with iron) compared to 610 °C (without iron). Enhanced catalytic oxidation properties are also observed for model soot particles, Printex-U, when mixed with Fe/C-TiO2. With regards to Si–TiO2 nanoparticles, a uniform coating of 3 to 8 nm of silicon dioxide is observed around the TiO2 particles. This coating mainly occurs due to variance in the chemical reaction rates of the precursors. Finally, with regards to V–TiO2, vanadium is doped within the TiO2 nanoparticles as visualized by HRTEM and XPS further confirms the formation of

  6. Synthesis of TiO2 nanoparticles containing Fe, Si, and V using multiple diffusion flames and catalytic oxidation capability of carbon-coated nanoparticles

    KAUST Repository

    Ismail, Mohamed; Memon, Nasir K.; Hedhili, Mohamed N.; Anjum, Dalaver H.; Chung, Suk-Ho

    2016-01-01

    Titanium dioxide (TiO2) nanoparticles containing iron, silicon, and vanadium are synthesized using multiple diffusion flames. The growth of carbon-coated (C–TiO2), carbon-coated with iron oxide (Fe/C–TiO2), silica-coated (Si–TiO2), and vanadium-doped (V–TiO2) TiO2 nanoparticles is demonstrated using a single-step process. Hydrogen, oxygen, and argon are utilized to establish the flame, with titanium tetraisopropoxide (TTIP) as the precursor for TiO2. For the growth of Fe/C–TiO2 nanoparticles, TTIP is mixed with xylene and ferrocene. While for the growth of Si–TiO2 and V–TiO2, TTIP is mixed with hexamethyldisiloxane (HMDSO) and vanadium (V) oxytriisopropoxide, respectively. The synthesized nanoparticles are characterized using high-resolution transmission electron microscopy (HRTEM) with energy-filtered TEM for elemental mapping (of Si, C, O, and Ti), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), nitrogen adsorption BET surface area analysis, and thermogravimetric analysis. Anatase is the dominant phase for the C–TiO2, Fe/C–TiO2, and Si–TiO2 nanoparticles, whereas rutile is the dominant phase for the V–TiO2 nanoparticles. For C–TiO2 and Fe/C–TiO2, the nanoparticles are coated with about 3-5-nm thickness of carbon. The iron-based TiO2 nanoparticles significantly improve the catalytic oxidation of carbon, where complete oxidation of carbon occurs at a temperature of 470 °C (with iron) compared to 610 °C (without iron). Enhanced catalytic oxidation properties are also observed for model soot particles, Printex-U, when mixed with Fe/C-TiO2. With regards to Si–TiO2 nanoparticles, a uniform coating of 3 to 8 nm of silicon dioxide is observed around the TiO2 particles. This coating mainly occurs due to variance in the chemical reaction rates of the precursors. Finally, with regards to V–TiO2, vanadium is doped within the TiO2 nanoparticles as visualized by HRTEM and XPS further confirms the formation of

  7. Synthesis and characterization of two new TiO2-containing benzothiazole-based imine composites for organic device applications.

    Science.gov (United States)

    Różycka, Anna; Iwan, Agnieszka; Bogdanowicz, Krzysztof Artur; Filapek, Michal; Górska, Natalia; Pociecha, Damian; Malinowski, Marek; Fryń, Patryk; Hreniak, Agnieszka; Rysz, Jakub; Dąbczyński, Paweł; Marzec, Monika

    2018-01-01

    The effect of the presence of titanium dioxide in two new imines, ( E , E )-(butane-1,4-diyl)bis(oxybutane-4,1-diyl) bis(4-{[(benzo[ d ][1,3]thiazol-2-yl)methylidene]amino}benzoate) (SP1) and ( E )- N -[(benzo[ d ][1,3]thiazol-2-yl)methylidene]-4-dodecylaniline (SP2), on the properties and stability of imine:TiO 2 composites for organic device applications were examined. The investigated titanium dioxide (in anatase form, obtained via the sol-gel method) exhibited a surface area of 59.5 m 2 /g according to Brunauer-Emmett-Teller theory, and its structure is a combination of both meso- and microporous. The average pore diameter calculated by the Barrett-Joyner-Halenda method was 6.2 nm and the cumulative volume of pores was 0.117 m 3 /g. The imine SP1 exhibited columnar organization (Col), while SP2 revealed a hexagonal columnar crystalline phase (Col hk ). The imine:TiO 2 mixtures in various weight ratio (3:0, 3:1, 3:2, 3:3) showed a lower energy gap and HOMO-LUMO energy levels compared to pure TiO 2 . This implies that TiO 2 provides not only a larger surface area for sensitizer adsorption and good electron collection, but also causes a shift of the imine energy levels resulting from intermolecular interaction. Also the temperature of the phase transition was slightly affected with the increase of TiO 2 concentration in imine-based composites. The changes observed in the Fourier transform middle-infrared absorption (FT-MIR) spectra confirmed the significant influence of TiO 2 on structural properties of both investigated imines. Similar interactions of oxygen vacancies existing on the TiO 2 surface with SP1 and SP2 were observed. The imine:TiO 2 mixtures showed good air stability and reusability, which demonstrates its potential for organic device applications.

  8. Synthesis and characterization of two new TiO2-containing benzothiazole-based imine composites for organic device applications

    Science.gov (United States)

    Różycka, Anna; Bogdanowicz, Krzysztof Artur; Filapek, Michal; Górska, Natalia; Pociecha, Damian; Malinowski, Marek; Fryń, Patryk; Hreniak, Agnieszka; Rysz, Jakub; Dąbczyński, Paweł

    2018-01-01

    The effect of the presence of titanium dioxide in two new imines, (E,E)-(butane-1,4-diyl)bis(oxybutane-4,1-diyl) bis(4-{[(benzo[d][1,3]thiazol-2-yl)methylidene]amino}benzoate) (SP1) and (E)-N-[(benzo[d][1,3]thiazol-2-yl)methylidene]-4-dodecylaniline (SP2), on the properties and stability of imine:TiO2 composites for organic device applications were examined. The investigated titanium dioxide (in anatase form, obtained via the sol–gel method) exhibited a surface area of 59.5 m2/g according to Brunauer–Emmett–Teller theory, and its structure is a combination of both meso- and microporous. The average pore diameter calculated by the Barrett–Joyner–Halenda method was 6.2 nm and the cumulative volume of pores was 0.117 m3/g. The imine SP1 exhibited columnar organization (Col), while SP2 revealed a hexagonal columnar crystalline phase (Colhk). The imine:TiO2 mixtures in various weight ratio (3:0, 3:1, 3:2, 3:3) showed a lower energy gap and HOMO–LUMO energy levels compared to pure TiO2. This implies that TiO2 provides not only a larger surface area for sensitizer adsorption and good electron collection, but also causes a shift of the imine energy levels resulting from intermolecular interaction. Also the temperature of the phase transition was slightly affected with the increase of TiO2 concentration in imine-based composites. The changes observed in the Fourier transform middle-infrared absorption (FT-MIR) spectra confirmed the significant influence of TiO2 on structural properties of both investigated imines. Similar interactions of oxygen vacancies existing on the TiO2 surface with SP1 and SP2 were observed. The imine:TiO2 mixtures showed good air stability and reusability, which demonstrates its potential for organic device applications. PMID:29600135

  9. Microstructure and cytotoxicity evaluation of duplex-treated silver-containing antibacterial TiO2 coatings

    International Nuclear Information System (INIS)

    Zhang, Xiangyu; Wu, Haibo; Geng, Zhenhua; Huang, Xiaobo; Hang, Ruiqiang; Ma, Yong; Yao, Xiaohong; Tang, Bin

    2014-01-01

    Implant-related infection is one of the most common and serious complications associated with biomedical implantation. To prevent bacterial adhesion, a series of porous TiO 2 coatings with different concentrations of silver (designated as M0, M1, M2 and M3) were prepared on pure titanium substrates by a duplex-treatment technique combining magnetron sputtering with micro-arc oxidation. All coatings are porous with pore size less than 5 μm and the concentrations of silver in the M0, M1, M2 and M3 are 0, 0.95, 1.36 and 1.93 wt.%, respectively. Silver is found to be distributed throughout the thickness of the coatings by scanning electron microscopy. The release of silver from the TiO 2 coatings was confirmed by an inductively-coupled plasma mass spectroscopy. The antibacterial effects of these coatings were tested against Gram-positive Staphylococcus aureus (S. aureus) and Gram-negative Escherichia coli (E. coli), and the cytotoxicity was evaluated using the mouse pre-osteoblast cells. The results indicate that the antibacterial activities of TiO 2 coatings are greatly improved due to the incorporation of silver. No cytotoxic effect is found for the M1 surfaces from the observation of pre-osteoblast cell by MTT assay and fluorescence microscopy. Although the M2 and M3 coatings appeared to be toxic for pre-osteoblast cells after 1 day in culture, the cell viability on M2 and M3 surfaces was greatly raised after culturing for 2 days. Our results suggested that the TiO 2 coatings incorporated with an optimum amount of silver can possess excellent antibacterial activities without cytotoxic effect, which has promising applications in biomedical devices. - Highlights: • Porous TiO 2 coatings with various concentration of Ag on titanium were prepared. • Ag element was distributed throughout the thickness of the coatings. • The antibacterial activities were greatly improved due to the incorporation of Ag. • The release amounts of Ag were initially high and gradually decreased with time. • The antibacterial coating doped with 0.95 wt.% Ag showed no cytotoxicity

  10. Effects of nano anatase-rutile TiO2 volume fraction with natural dye containing anthocyanin on the dye sensitized solar cell performance

    Science.gov (United States)

    Agustini, S.; Wahyuono, R. A.; Sawitri, D.; Risanti, D. D.

    2013-09-01

    Since its first development, efforts to improve efficiency of Dye Sensitized Solar Cell (DSSC) are continuously carried out, either through selection of dye materials, the type of semiconductor, counter electrode design or the sandwiched structure. It is widely known that anatase and rutile are phases of TiO2 that often being used for fabrication of DSSC. Rutile is thermodynamically more stable phase having band-gap suitable for absorption of sunlight spectrum. On the other hand, anatase has higher electrical conductivity, capability to adsorp dye as well as higher electron diffusion coefficient than those of rutile. Present research uses mangosteen pericarp and Rhoeo spathacea extracted in ethanol as natural dye containing anthocyanin. These dyes were characterized by using UV-Vis and FTIR, showing that the absorption maxima peaks obtained at 389 nm and 413 nm, for mangosteen and Rhoeo spathacea, respectively. The nano TiO2 was prepared by means of co-precipitation method. The particle size were 9-11 nm and 54.5 nm for anatase and rutile, respectively, according to Scherrer's equation. DSSCs were fabricated in various volume fractions of anatase and rutile TiO2. The fabricated DSSCs were tested under 17 mW/cm2 of solar irradiation. The current-voltage (I-V) characteristic of DSSCs employing 75%: 25% volume fraction of anatase and rutile TiO2 have outstanding result than others. The highest conversion efficiencies of 0.037% and 0.013% are obtained for DSSC employing natural dye extract from mangosteen pericarp and Rhoeo spathacea, respectively.

  11. TiO2-Containing Carbon Derived from a Metal-Organic Framework Composite: A Highly Active Catalyst for Oxidative Desulfurization.

    Science.gov (United States)

    Bhadra, Biswa Nath; Song, Ji Yoon; Khan, Nazmul Abedin; Jhung, Sung Hwa

    2017-09-13

    A new metal-organic framework (MOF) composite consisting of Ti- and Zn-based MOFs (ZIF-8(x)@H 2 N-MIL-125; in brief, ZIF(x)@MOF) was designed and synthesized. The pristine MOF [H 2 N-MIL-125 (MOF)]- and an MOF-composite [ZIF(30)@MOF]-derived mesoporous carbons consisting of TiO 2 nanoparticles were prepared by pyrolysis (named MDC-P and MDC-C, respectively). MDC-C showed a higher surface area, larger pore sizes, and larger mesopore volumes than MDC-P. In addition, the TiO 2 nanoparticles on MDC-C have more uniform shapes and sizes and are smaller than those of MDC-P. The obtained MDC-C and MDC-P [together with MOF, ZIF(30)@MOF, pure/nanocrystalline TiO 2 , and activated carbon] were applied in the oxidative desulfurization reaction of dibenzothiophene in a model fuel. The MDC-C, even with a lower TiO 2 content than that of MDC-P, showed an outstanding catalytic performance, especially with a very low catalyst dose (i.e., a very high quantity of dibenzothiophene was converted per unit weight of the catalyst), fast kinetics (∼3 times faster than that for MDC-P), and a low activation energy (lower than that for any reported catalyst) for the oxidation of dibenzothiophene. The large mesopores of MDC-C and the well-dispersed/small TiO 2 might be the dominant factors for the superior catalytic conversions. The oxidative desulfurization of other sulfur-containing organic compounds with various electron densities was also studied with MDC-C to understand the mechanism of catalysis. Moreover, the MDC-C catalyst can be reused many times in the oxidative desulfurization reaction after a simple washing with acetone. Finally, composing MOFs and subsequent pyrolysis is suggested as an effective way to prepare a catalyst with well-dispersed active sites, large pores, and high mesoporosity.

  12. Ceramic containers for spent nuclear fuel. II. Reactions between TiO2 and the steel canning during hot isostatic processing

    International Nuclear Information System (INIS)

    Bergman, B.; Forberg, S.

    1984-01-01

    Rutile was selected for some practical studies of processing and properties of ceramic containers. Hot isostatic pressing at 1280 0 C has resulted in reaction zones between the TiO 2 powder and the steel canning. The phases ilmenite, pseudobrookite, rutile, and iron have been identified by x-ray diffraction and by microprobe analysis. The microstructures have been interpreted by classical metallographic methods, and some microstructures obtained by hot pressing and rapid cooling have also been examined for purposes of comparison. Some implications of the microstructures have been discussed in terms of microcracking and slow crack growth. 13 refs., 7 figs

  13. Investigation on H-containing shallow trap of hydrogenated TiO2 with in situ Fourier transform infrared diffuse reflection spectroscopy.

    Science.gov (United States)

    Han, Bing; Hang Hu, Yun

    2017-07-28

    A novel technique, high temperature high pressure in situ Fourier transform infrared diffuse reflection spectroscopy, was successfully used to investigate the formation and stability of shallow trap states in P25 TiO 2 nanoparticles. Two types of shallow traps (with and without H atoms) were identified. The H-containing shallow trap can be easily generated by heating in H 2 atmosphere. However, the trap is unstable in vacuum at 600 °C. In contrast, the H-free shallow trap, which can be formed by heating in vacuum, is stable even at 600 °C. The energy gaps between shallow trap states and the conduction band are 0.09 eV for H-containing shallow trap and 0.13 eV for H-free shallow trap, indicating that the H-containing shallow trap state is closer to the conduction band than that without H.

  14. Radionuclide containment in soil by phosphate treatment

    International Nuclear Information System (INIS)

    Lee, S.Y.; Francis, C.W.; Timpson, M.E.; Elless, M.P.

    1995-01-01

    Radionuclide transport from a contaminant source to groundwater and surface water is a common problem faced by most US Department of Energy (DOE) facilities. Containment of the radionuclide plume, including strontium-90 and uranium, is possible using phosphate treatment as a chemical stabilizer. Such a chemical process occurs in soils under natural environmental conditions. Therefore, the concept of phosphate amendment for radiostrontium and uranium immobilization is already a proven principle. In this presentation, results of bench-scale experiments and the concept of a field-scale demonstration are discussed. The phosphate treatment is possible at the source or near the advancing contaminant plume. Cleanup is still the ideal concept; however, containment through stabilization is a more practical and costeffective concept that should be examined by DOE Environmental Restoration programs

  15. Characterization and Comparison of Photocatalytic Activity Silver Ion doped on TiO2(TiO2/Ag+) and Silver Ion doped on Black TiO2(Black TiO2/Ag+)

    Science.gov (United States)

    Kim, Jin Yi; Sim, Ho Hyung; Song, Sinae; Noh, Yeoung Ah; Lee, Hong Woon; Taik Kim, Hee

    2018-03-01

    Titanium dioxide (TiO2) is one of the representative ceramic materials containing photocatalyst, optic and antibacterial activity. The hydroxyl radical in TiO2 applies to the intensive oxidizing agent, hence TiO2 is suitable to use photocatalytic materials. Black TiO2was prepared through reduction of amorphous TiO2 conducting under H2 which leads to color changes. Its black color is proven that absorbs 100% light across the whole-visible light, drawing enhancement of photocatalytic property. In this study, we aimed to compare the photocatalytic activity of silver ion doped on TiO2(TiO2/Ag+) and silver ion doped on black TiO2(black TiO2/Ag+) under visible light range. TiO2/Ag+ was fabricated following steps. 1) TiO2 was synthesized by a sol-gel method from Titanium tetraisopropoxide (TTIP). 2) Then AgNO3 was added during an aging process step for silver ion doping on the surface of TiO2. Moreover, Black TiO2/Ag+ was obtained same as TiO2/Ag+ except for calcination under H2. The samples were characterized X-ray diffraction (XRD), UV-visible reflectance (UV-vis DRS), and Methylene Blue degradation test. XRD analysis confirmed morphology of TiO2. The band gap of black TiO2/Ag+ was confirmed (2.6 eV) through UV-vis DRS, which was lower than TiO2/Ag+ (2.9 eV). The photocatalytic effect was conducted by methylene blue degradation test. It demonstrated that black TiO2/Ag+ had a photocatalytic effect under UV light also visible light.

  16. Ultra-fine structural characterization and bioactivity evaluation of TiO2 nanotube layers.

    Science.gov (United States)

    Jang, JaeMyung; Kwon, TaeYub; Kim, KyoHan

    2008-10-01

    For an application as biomedical materials of high performance with a good biocompatibility, the TiO2 nanotube-type oxide film on Ti substrate has been fabricated by electrochemical method, and the effects of surface characteristics of TiO2 naotube layer have been investigated. The surface morphology of TiO2 nanotube layer depends on factors such as anodizing time, current density, and electrolyte temperature. Moreover, the cell and pore size gradually were increased with the passage of anodizing time. X-ray diffraction (XRD) results indicated that the TiO2 nanotube layer formed in acidic electrolytes was mainly composed of anatase structure containing rutile. From the analysis of chemical states of TiO2 nanotube layer using X-ray photoelectron spectroscopy (XPS), Ti2p, P2p and O1s were observed in the nanotubes layer, which were penetrated from the electrolyte into the oxide layer during anodic process. The incorporated phosphate species were found mostly in the forms of HPO4-, PO4-, and PO3-. From the result of biological evaluation in simulated body fluid (SBF) the TiO2 nanotube layer was effective for bioactive property.

  17. Preparation of Transparent Bulk TiO2/PMMA Hybrids with Improved Refractive Indices via an in Situ Polymerization Process Using TiO2 Nanoparticles Bearing PMMA Chains Grown by Surface-Initiated Atom Transfer Radical Polymerization.

    Science.gov (United States)

    Maeda, Satoshi; Fujita, Masato; Idota, Naokazu; Matsukawa, Kimihiro; Sugahara, Yoshiyuki

    2016-12-21

    Transparent TiO 2 /PMMA hybrids with a thickness of 5 mm and improved refractive indices were prepared by in situ polymerization of methyl methacrylate (MMA) in the presence of TiO 2 nanoparticles bearing poly(methyl methacrylate) (PMMA) chains grown using surface-initiated atom transfer radical polymerization (SI-ATRP), and the effect of the chain length of modified PMMA on the dispersibility of modified TiO 2 nanoparticles in the bulk hybrids was investigated. The surfaces of TiO 2 nanoparticles were modified with both m-(chloromethyl)phenylmethanoyloxymethylphosphonic acid bearing a terminal ATRP initiator and isodecyl phosphate with a high affinity for common organic solvents, leading to sufficient dispersibility of the surface-modified particles in toluene. Subsequently, SI-ATRP of MMA was achieved from the modified surfaces of the TiO 2 nanoparticles without aggregation of the nanoparticles in toluene. The molecular weights of the PMMA chains cleaved from the modified TiO 2 nanoparticles increased with increases in the prolonging of the polymerization period, and these exhibited a narrow distribution, indicating chain growth controlled by SI-ATRP. The nanoparticles bearing PMMA chains were well-dispersed in MMA regardless of the polymerization period. Bulk PMMA hybrids containing modified TiO 2 nanoparticles with a thickness of 5 mm were prepared by in situ polymerization of the MMA dispersion. The transparency of the hybrids depended significantly on the chain length of the modified PMMA on the nanoparticles, because the modified PMMA of low molecular weight induced aggregation of the TiO 2 nanoparticles during the in situ polymerization process. The refractive indices of the bulk hybrids could be controlled by adjusting the TiO 2 content and could be increased up to 1.566 for 6.3 vol % TiO 2 content (1.492 for pristine PMMA).

  18. Simultaneous enrichment of cysteine-containing peptides and phosphopeptides using a cysteine-specific phosphonate adaptable tag (CysPAT) in combination with titanium dioxide (TiO2) chromatography

    DEFF Research Database (Denmark)

    Huang, Honggang; Pedersen, Martin Haar; Ibañez-Vea, Maria

    2016-01-01

    to selectively label cysteine-containing peptides (Cys peptides) followed by their enrichment with titanium dioxide (TiO2) and subsequent mass spectrometric analysis. The CysPAT strategy was developed using a synthetic peptide, a standard protein and subsequently the strategy was applied to protein lysates from...

  19. High dielectric constant and energy density induced by the tunable TiO2 interfacial buffer layer in PVDF nanocomposite contained with core-shell structured TiO2@BaTiO3 nanoparticles

    Science.gov (United States)

    Hu, Penghao; Jia, Zhuye; Shen, Zhonghui; Wang, Peng; Liu, Xiaoru

    2018-05-01

    To realize application in high-capacity capacitors and portable electric devices, large energy density is eagerly desired for polymer-based nanocomposite. The core-shell structured nanofillers with inorganic buffer layer are recently supposed to be promising in improving the dielectric property of polymer nanocomposite. In this work, core-shell structured TO@BT nanoparticles with crystalline TiO2 buffer layer coated on BaTiO3 nanoparticle were fabricated via solution method and heat treatment. The thickness of the TO buffer layer can be tailored by modulating the additive amount of the titanate coupling agent in preparation process, and the apparent dielectric properties of nanocomposite are much related to the thickness of the TO layer. The relatively thin TO layer prefer to generate high polarization to increase dielectric constant while the relatively thick TO layer would rather to homogenize field to maintain breakdown strength. Simulation of electric field distribution in the interfacial region reveals the improving effect of the TO buffer layer on the dielectric properties of nanocomposite which accords with the experimental results well. The optimized nanoparticle TO@BT-2 with a mean thickness of 3-5 nm buffer layer of TO is effective in increasing both the ε and Eb in the PVDF composite film. The maximal discharged energy density of 8.78 J/cm3 with high energy efficiency above 0.6 is obtained in TO@BT-2/PVDF nanocomposite with 2.5 vol% loading close to the breakdown strength of 380 kV/mm. The present study demonstrates the approach to optimize the structure of core-shell nanoparticles by modulating buffer layer and provides a new way to further enlarge energy density in polymer nanocomposite.

  20. Water diffusion in phosphate-containing hydrogels

    International Nuclear Information System (INIS)

    George, K.A.; Wentrup-Byrne, E.; Hill, D.J.T.; Whittaker, A.K.

    2003-01-01

    An understanding of the kinetics and diffusion of liquids through polymeric hydrogels is critical for the successful design and application of these materials in biomedical field, particularly as controlled drug delivery systems. In this study, the mechanisms of water transport and parameters that describe the diffusion process in crosslinked poly(2-hydroxyethylmethacrylate-co-methyloxyethylene phosphate), poly(HEMA-co-MOEP) polymers were investigated. The copolymerisation of HEMA with MOEP was initiated by γ radiolysis with full conversion of monomer to polymer. The sorption of water into the polymers with 0 - 30 mol% MOEP was monitored gravimetrically over a period of 2 - 3 weeks. This study provided an insight into the diffusion mechanism and showed that the PHEMA hydrogel displayed concentration-independent Fickian diffusion. As the concentration of MOEP in the network increased, the diffusion rate and the rigidity of the network also increased in a linear fashion. NMR imaging was used in conjunction with the gravimetric study to elucidate the transport mechanisms, diffusion coefficients and proportionality constants governing the water diffusion in the phosphate-containing polymers. The hydrogels with 3 - 20 mol% MOEP exhibited exponential concentration-dependent Fickian diffusion and the transport mechanism in the system with 30 mol% MOEP was shown to be anomalous. The systems with greater concentrations of MOEP displayed a high degree of fracturing during water sorption and resulted in the ultimate destruction of the cylindrical geometry

  1. Heteropoly acid promoted V2O5/TiO2 catalysts for NO abatement with ammonia in alkali containing flue gases

    DEFF Research Database (Denmark)

    Putluru, Siva Sankar Reddy; Jensen, Anker Degn; Riisager, Anders

    2011-01-01

    V2O5/TiO2 and heteropoly acid promoted V2O5/TiO2 catalysts were prepared and characterized by N2 physisorption, XRPD and NH3-TPD. The influence of the calcination temperature from 400 to 700 1C on crystallinity and acidic properties was studied and compared with the activity for the selective...... catalytic reduction (SCR) of NO with ammonia. The SCR activity of heteropoly acid promoted catalysts was found to be much higher than for unpromoted catalysts. The stability of heteropoly acid promoted catalysts is dependent on calcination temperature and there is a gradual decrease in SCR activity...... and acidity with increase in calcination temperatures. Furthermore, the heteropoly acid promoted V2O5/TiO2 catalysts showed excellent alkali deactivation resistance and might therefore be alternative deNOx catalysts in biomass fired power plants....

  2. Method of stripping plutonium from tributyl phosphate solution which contains dibutyl phosphate-plutonium stable complexes

    International Nuclear Information System (INIS)

    Ochsenfeld, W.; Schmieder, H.

    1976-01-01

    Fast breeder fuel elements which have been highly burnt-up are reprocessed by extracting uranium and plutonium into an organic solution containing tributyl phosphate. The tributyl phosphate degenerates at least partially into dibutyl phosphate and monobutyl phosphate, which form stable complexes with tetravalent plutonium in the organic solution. This tetravalent plutonium is released from its complexed state and stripped into aqueous phase by contacting the organic solution with an aqueous phase containing tetravalent uranium. 6 claims, 1 drawing figure

  3. Surface characterization of poly(methylmethacrylate) based nanocomposite thin films containing Al2O3 and TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Lewis, S.; Haynes, V.; Wheeler-Jones, R.; Sly, J.; Perks, R.M.; Piccirillo, L.

    2010-01-01

    Poly(methylmethacrylate) (PMMA) based nanocomposite electron beam resists have been demonstrated by spin coating techniques. When TiO 2 and Al 2 O 3 nanoparticles were directly dispersed into the PMMA polymer matrix, the resulting nanocomposites produced poor quality films with surface roughnesses of 322 and 402 nm respectively. To improve the surface of the resists, the oxide nanoparticles were encapsulated in toluene and methanol. Using the zeta potential parameter, it was found that the stabilities of the toluene/oxide nanoparticle suspensions were 7.7 mV and 19.4 mV respectively, meaning that the suspension was not stable. However, when the TiO 2 and Al 2 O 3 nanoparticles were encapsulated in methanol the zeta potential parameter was 31.9 mV and 39.2 mV respectively. Therefore, the nanoparticle suspension was stable. This method improved the surface roughness of PMMA based nanocomposite thin films by a factor of 6.6 and 6.4, when TiO 2 and Al 2 O 3 were suspended in methanol before being dispersed into the PMMA polymer.

  4. Removal of organic wastes containing tributyl phosphate

    International Nuclear Information System (INIS)

    Drobnik, S.

    TBP in dodecane and kerosene is one of the waste solutions from the reprocessing of spent nuclear fuels by the Purex process. The following methods were investigated for removing the organic solvents: adsorption on suitable solids, extraction, reaction with neutral salts, and saponification with acids or alkalis. Results showed that the best method of TBP removal is saponification with alkali hydroxides, either with dibutyl phosphate or with ortho-phosphate

  5. Fabrication of a TiO2-P25/(TiO2-P25+TiO2 nanotubes junction for dye sensitized solar cells

    Directory of Open Access Journals (Sweden)

    Nguyen Huy Hao

    2016-08-01

    Full Text Available The dye sensitized solar cell (DSSC, which converts solar light into electric energy, is expected to be a promising renewable energy source for today's world. In this work, dye sensitized solar cells, one containing a single layer and one containing a double layer, were fabricated. In the double layer DSSC structure, the under-layer was TiO2-P25 film, and the top layer consisted of a mixture of TiO2-P25 and TiO2 nanotubes. The results indicated that the efficiency of the DSSC with the double layer structure was a significant improvement in comparison to the DSSC consisting of only a single film layer. The addition of TiO2-P25 in the top layer caused an improvement in the adsorption of dye molecules on the film rather than on the TiO2 nanotubes only. The presence of the TiO2 nanotubes together with TiO2-P25 in the top layer revealed the enhancement in harvesting the incident light and an improvement of electron transport through the film.

  6. Effect of submarine groundwater discharge containing phosphate on coral calcification

    Science.gov (United States)

    Yasumoto, J.; Yasumoto, K.; Iijima, M.; Nozaki, M.; Asai, K.; Yasumoto, M. H.

    2017-12-01

    It is well known that the anthropogenic eutrophication enriched with various substances including phosphate in coastal waters has resulted in coral degradation. However, to the best of our knowledge, the phosphate threshold value to inhibit the coral calcification has been unclear, due to the unknown mechanisms involved in the inhibition of the calcification by phosphate. In island regions, groundwater is one of the most important clues to transport the nutrients contained in livestock or agricultural wastewaters. However, the actual conditions of coastal pollution with such nutrients have not been understood because of unperceived submarine groundwater discharge (SGD). In this study, to quantify of extremely rapid and localized SGD from Ryukyu limestone aquifer, we investigated the rate and concentration of phosphate of SGD using automated seepage mater in Yoron Island, which is located southern part of Japan. And, to elucidate the inhibition mechanisms for phosphate against coral calcification, we examined its effect on the bottom skeleton formation in primary polyps of Acropora digitifera by using the fluorescence derivatizing reagent having phosphate group (FITC-AA). As a result, the SGD was found to contain 1 to 2 µM of phosphate as much as the concentration in the coastal ground water under agricultural land. Moreover, the amount of phosphate contained in the surface layers of bottom calcareous sands close to the region of SGD were about 5 µmol/g. When the primary polyps were treated with 50 µM of FITC-AA, the bottom skeleton of the primary polyps showed the fluorescence from FITC-AA within a few minutes, suggesting the phosphate binding. Furthermore, when the polyps were treated with 10 µM of FITC-AA, irregular patterns of the elongated skeleton were observed. These results led us to conclude that phosphate is transported via a paracellular pathway to the subcalicoblastic extracellular calcifying medium. These results indicate that the phosphate adsorbed

  7. Physical and optical studies of BaO-TeO2-TiO2-B2O3 glasses containing Cu2+ transition metal ion

    Science.gov (United States)

    Srinivas, B.; Kumar, R. Vijaya; Hameed, Abdul; Sagar, D. Karuna; Chary, M. Narasimha; Shareefuddin, Md.

    2018-05-01

    Glasses with the composition xBaO-(30-x) TeO2-10TiO2-59B2O3-1CuO (where x = 10, 15, 20 and 25 mole %) were prepared by melt quenching technique. The XRD studies were made on these glass samples at room temperature. The amorphous nature of the glass samples was confirmed from the XRD patterns. The physical parameters such as density (ρ), molar volume (Vm), average boron-boron separation (dB-B) and oxygen packing density (OPD) were calculated. The change in density and molar volume has been investigated in terms of the variation of BaO in the glass composition. The optical absorption spectra have been recorded at room temperature. The values of optical band gap have been estimated from the ASF and Tauc's methods. Both Tauc's and ASF methods have been showing progressively increasing indirect optical band gap values with the increase of BaO concentrations.

  8. Iron phosphate glass containing simulated fast reactor waste: Characterization and comparison with pristine iron phosphate glass

    International Nuclear Information System (INIS)

    Joseph, Kitheri; Asuvathraman, R.; Venkata Krishnan, R.; Ravindran, T.R.; Govindaraj, R.; Govindan Kutty, K.V.; Vasudeva Rao, P.R.

    2014-01-01

    Detailed characterization was carried out on an iron phosphate glass waste form containing 20 wt.% of a simulated nuclear waste. High temperature viscosity measurement was carried out by the rotating spindle method. The Fe 3+ /Fe ratio and structure of this waste loaded iron phosphate glass was investigated using Mössbauer and Raman spectroscopy respectively. Specific heat measurement was carried out in the temperature range of 300–700 K using differential scanning calorimeter. Isoconversional kinetic analysis was employed to understand the crystallization behavior of the waste loaded iron phosphate glass. The glass forming ability and glass stability of the waste loaded glass were also evaluated. All the measured properties of the waste loaded glass were compared with the characteristics of pristine iron phosphate glass

  9. Photoassist-phosphorylated TiO2 as a catalyst for direct formation of 5-(hydroxymethyl)furfural from glucose.

    Science.gov (United States)

    Hattori, Masashi; Kamata, Keigo; Hara, Michikazu

    2017-02-01

    Photo-assisted phosphorylation of an anatase TiO 2 catalyst was examined to improve its catalytic performance for the direct production of 5-(hydroxymethyl)furfural (HMF), a versatile chemical platform, from glucose. In phosphorylation based on simple esterification between phosphoric acid and surface OH groups on anatase TiO 2 with water-tolerant Lewis acid sites, the density of phosphates immobilized on TiO 2 is limited to 2 phosphates nm -2 , which limits selective HMF production. Phosphorylation of the TiO 2 surface under fluorescent light irradiation increases the surface phosphate density to 50%, which is higher than the conventional limit, thus preventing the adsorption of hydrophilic glucose molecules on TiO 2 and resulting in a more selective HMF production over photoassist-phosphorylated TiO 2 .

  10. The effect of calcium phosphate-containing desensitizing agent on ...

    African Journals Online (AJOL)

    Objective: The aim of this study was to investigate the effect of calcium phosphate containing desensitizing pretreatments on the microtensile bond strength (MTBS) and microleakage of the multimode adhesive agent to dentin. Materials and Methods: In this study, twelve noncarious, freshly extracted human third molar teeth ...

  11. Corrosion of alloy 22 in phosphate and chloride containing solutions

    International Nuclear Information System (INIS)

    Carranza, Ricardo M.

    2007-01-01

    Alloy C-22 is a Ni-based alloy (22% Cr, 13% Mo, 3% W y 3% Fe in weight per cent) that exhibits an excellent uniform and localized corrosion resistance due to its protective passive film. It was designed to resist the most aggressive environments for industrial applications. Alloy 22 is one of the candidates to be considered for the outer shell of the canister that would contain high level radioactive nuclear wastes. The effect of phosphate ion in chloride containing solutions at 90 C degrees was studied under aggressive conditions were this material might be susceptible to crevice corrosion. The electrolyte solution, which consisted of 1M NaCl and different phosphate concentrations (between 10 -3 M and 1M), was deoxygenated by bubbling with nitrogen. Electrochemical tests, electron microscope observations (SEM) and energy dispersive spectrometer analysis (EDS) were conducted. Crevice corrosion was not detected and the comparison of the potentiodynamic polarization tests showed an increase of the passivity range in phosphate containing solutions. The passive current value was 1 μA/cm 2 approximately in all the tests that were performed in this work. The differences in composition of the anodic film formed on the samples suggest that phosphate is responsible for the increase of the passivity range by incorporation to the passive film. (author)

  12. Setting time and sealing ability of alpha-tricalcium phosphate cement containing titanic oxide.

    Science.gov (United States)

    Yoshikawa, M; Terada, Y; Toda, T

    1998-10-01

    We developed a new type of calcium phosphate cement for clinical use in endodontics as a root canal sealer or pulp cupping agent. The solid phase of the sealer is composed of 70% of alpha-tricalcium phosphate (alpha-TCP) and 30% of titanic oxide (TiO2), and the liquid phase is 37% citric acid, 5% tannic acid and 58% distilled water. TiO2 was added to control setting time and handling of the cement. We used commercially available calcium phosphate root canal sealer as a control. ISO standards specify that new endodontic products should be examined thoroughly before clinical use. It is important to carry out in vitro cytotoxicity and in vivo histocompatibility tests. We first did in vitro test of setting time and root canal sealing ability of the cement. We found that this developed calcium phosphate cement had an appropriate setting time and excellent sealing ability as a root canal sealer, and concluded that it was suitable for clinical use as a root canal sealer.

  13. Pulmonary toxicity screening studies in male rats with TiO2 particulates substantially encapsulated with pyrogenically deposited, amorphous silica

    Directory of Open Access Journals (Sweden)

    Webb TR

    2006-01-01

    Full Text Available Abstract The aim of this study was to evaluate the acute lung toxicity in rats of intratracheally instilled TiO2 particles that have been substantially encapsulated with pyrogenically deposited, amorphous silica. Groups of rats were intratracheally instilled either with doses of 1 or 5 mg/kg of hydrophilic Pigment A TiO2 particles or doses of 1 or 5 mg/kg of the following control or particle-types: 1 R-100 TiO2 particles (hydrophilic in nature; 2 quartz particles, 3 carbonyl iron particles. Phosphate-buffered saline (PBS instilled rats served as additional controls. Following exposures, the lungs of PBS and particle-exposed rats were evaluated for bronchoalveolar lavage (BAL fluid inflammatory markers, cell proliferation, and by histopathology at post-instillation time points of 24 hrs, 1 week, 1 month and 3 months. The bronchoalveolar lavage results demonstrated that lung exposures to quartz particles, at both concentrations but particularly at the higher dose, produced significant increases vs. controls in pulmonary inflammation and cytotoxicity indices. Exposures to Pigment A or R-100 TiO2 particles produced transient inflammatory and cell injury effects at 24 hours postexposure (pe, but these effects were not sustained when compared to quartz-related effects. Exposures to carbonyl iron particles or PBS resulted only in minor, short-term and reversible lung inflammation, likely related to the effects of the instillation procedure. Histopathological analyses of lung tissues revealed that pulmonary exposures to Pigment A TiO2 particles produced minor inflammation at 24 hours postexposure and these effects were not significantly different from exposures to R-100 or carbonyl iron particles. Pigment A-exposed lung tissue sections appeared normal at 1 and 3 months postexposure. In contrast, pulmonary exposures to quartz particles in rats produced a dose-dependent lung inflammatory response characterized by neutrophils and foamy (lipid-containing

  14. Photocatalytic activities of heterostructured TiO2-graphene porous microspheres prepared by ultrasonic spray pyrolysis

    International Nuclear Information System (INIS)

    Yang, Jikai; Zhang, Xintong; Li, Bing; Liu, Hong; Sun, Panpan; Wang, Changhua; Wang, Lingling; Liu, Yichun

    2014-01-01

    Highlights: • USP method is used to prepare TiO 2 -graphene porous microspheres. • XPS shows GO sheets in the composites has been reduced to graphene. • TiO 2 -graphene microspheres display a red-shifted absorption edge. • PL spectra indicate graphene can accept the photoexcited electrons from TiO 2 . • TiO 2 -graphene shows higher photocatalytic activity than TiO 2 under solar light. -- Abstract: TiO 2 -graphene porous microspheres were prepared by ultrasonic spray pyrolysis (USP) of aqueous suspension of graphene oxide containing TiO 2 nanoparticles (Degussa P25). The composite microspheres were characterized with SEM, XPS, photoluminescence, Raman and UV–Vis absorption spectra. TiO 2 -graphene porous microspheres displayed higher photocatalytic activity for the degradation of methylene blue solution than pristine TiO 2 microspheres under the irradiation of Xe lamp, and the highest activity was obtained at a weight percentage of graphene around 1%. The effect of graphene on photocatalytic activity of porous microsphere was discussed in terms of the enhanced charge separation by TiO 2 -graphene heterojunction, increased absorption of the visible light, as well as the possible hindrance of mass transportation in microspheres

  15. Reflectance spectroscopy from TiO2 particles embedded in polyurethane

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy; Canulescu, Stela; Johansen, Villads Egede

    2013-01-01

    This paper presents the results of a physical simulation carried out using TiO2-Polyurethane composite coating on bright aluminium surface to understand the light scattering effect for designing white surfaces. Polyurethane matrix is selected due to the matching refractive index (1.7) with Al2O3...... layer on anodized aluminium surfaces. Three different TiO2 particle distributions were dispersed in polyurethane and spin coated onto high gloss and caustic etched aluminium substrates. Reflectance spectra of TiO2-polyurethane films of various concentrations were analysed using an integrating sphere....... The results show that the TiO2-polyurethane coatings have a high diffuse reflectance as a result of multiple scattering from TiO2 particles. Diffuse reflectance spectra of TiO2 containing films vary weakly with particle concentration and reach a steady state value at a concentration of 0.75 wt.%. Using...

  16. An innovative approach to synthesize highly-ordered TiO2 nanotubes.

    Science.gov (United States)

    Isimjan, Tayirjan T; Yang, D Q; Rohani, Sohrab; Ray, Ajay K

    2011-02-01

    An innovative route to prepare highly-ordered and dimensionally controlled TiO2 nanotubes has been proposed using a mild sonication method. The nanotube arrays were prepared by the anodization of titanium in an electrolyte containing 3% NH4F and 5% H2O in glycerol. It is demonstrated that the TiO2 nanostructures has two layers: the top layer is TiO2 nanowire and underneath is well-ordered TiO2 nanotubes. The top layer can easily fall off and form nanowires bundles by implementing a mild sonication after a short annealing time. We found that the dimensions of the TiO2 nanotubes were only dependent on the anodizing condition. The proposed technique may be extended to fabricate reproducible well-ordered TiO2 nanotubes with large area on other metals.

  17. Activity and deactivation of sulphated TiO2- and ZrO2-based V, Cu, and Fe oxide catalysts for NO abatement in alkali containing flue gases

    DEFF Research Database (Denmark)

    Kustov, Arkadii; Rasmussen, Søren Birk; Fehrmann, Rasmus

    2007-01-01

    Vanadia, copper and iron oxide catalysts supported on conventional TiO2, ZrO2, and sulphated-TiO2 and ZrO2 have been prepared. These catalysts were characterized by elemental analysis, N-2-BET, XRD, and NH3-TPD methods. The influence of potassium oxide additives on the acidity and activity...... of the catalysts with potassium leads to a considerable decrease of their catalytic activity. In the case of the traditional carriers (TiO2, ZrO2), the poisoning of the catalyst with small amounts of potassium oxide (K/metal ratio...

  18. Recovery of uranium from 30 vol % tributyl phosphate solvents containing dibutyl phosphate

    International Nuclear Information System (INIS)

    Mailen, J.C.; Tallent, O.K.

    1986-01-01

    A number of solid sorbents were tested for the removal of uranium and dibutyl phosphate (DBP) from 30% tributyl phosphate (TBP) solvent. The desired clean uranium product can be obtained either by removing the DBP, leaving the uranium in the solvent for subsequent stripping, or by removing the uranium, leaving the DBP in the solvent for subsequent treatment. The tests performed show that it is relatively easy to preferentially remove uranium from solvents containing uranium and DBP, but quite difficult to remove DBP preferentially. The current methods could be used by removing the uranium (as by a cation exchange resin) and then using either an anion exchange resin in the hydroxyl form or a conventional treatment with a basic solution to remove the DBP. Treatment of a solvent with a cation exchange resin could be useful for recovery of valuable metals from solvents containing DBP and might be used to remove cations before scrubbing a solvent with a basic solution to minimize emulsion formation. 6 refs., 9 figs

  19. Properties of phases in HfO2-TiO2 system

    International Nuclear Information System (INIS)

    Red'ko, V.P.; Terekhovskij, P.B.; Majster, I.M.; Shevchenko, A.V.; Lopato, L.M.; Dvernyakova, A.A.

    1990-01-01

    A study was made on axial and linear coefficients of thermal expansion (CTE) of HfO 2 -TiO 2 system samples in concentration range of 25-50 mol% TiO 2 . Samples, containing 35 and 37 mol% TiO 2 , are characterized by the lowest values of linear CTE. Dispersion of the basic substances doesn't affect CTE value. Correlation with axial and linear CTE of samples in ZrO 2 -TiO 2 system was conducted. Presence of anisotropy of change of lattice parameters was supported for samples, containing 37.5 and 40 mol% TiO 2 . Polymorphous transformations for hafnium titanate were not revealed

  20. Preparation and characterization of phosphate glasses containing titanium and vanadium

    Energy Technology Data Exchange (ETDEWEB)

    Kaoua, S. [Laboratoire de Chimie du Solide, Faculte des Sciences Ain Chock, Casablanca (Morocco); Krimi, S. [Laboratoire de Chimie du Solide, Faculte des Sciences Ain Chock, Casablanca (Morocco)]. E-mail: krimisaida@yahoo.fr; El Jazouli, A. [Laboratoire de Chimie des Materiaux Solides, Faculte des Sciences Ben M' Sik, Casablanca (Morocco); Hlil, E.K. [Laboratoire de Cristallographie du CNRS, Grenoble (France)]. E-mail: hlil@grenoble.cnrs.fr; Waal, D. de [Department of Chemistry, University of Pretoria, 0002 Pretoria (South Africa)

    2007-02-21

    Na{sub 5-x}Ti{sub 1-x}V {sub x}(PO{sub 4}){sub 3} (0 {<=} x {<=} 1) phosphates glasses have been obtained in air by direct fusion of Na{sub 2}CO{sub 3}, TiO{sub 2}, V{sub 2}O{sub 5} and (NH{sub 4}){sub 2}HPO{sub 4}. Vitreous Na{sub 5}Ti(PO{sub 4}){sub 3} is colourless while the glasses containing vanadium are green, due to the reduction of V{sup 5+} to V{sup 4+}. Glass transition and crystallization temperatures (T {sub g}, T {sub c}) decrease when the amount of vanadium increases. EPR, Raman and UV-vis spectra have been investigated. The results are consistent with the presence of V{sup 4+} ions in distorted octahedra with very strong V-O bond.

  1. Structural, optical and ferromagnetic properties of Cr doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Choudhury, Biswajit; Choudhury, Amarjyoti

    2013-01-01

    Graphical abstract: Doping of Cr 3+ distorts the lattice of TiO 2 , generate oxygen vacancies and create d-band states in the mid band gap of TiO 2 . Incorporation of Cr 3+ also imparts magnetism in non-magnetic TiO 2 by undergoing coupling with the neighboring oxygen vacancies. -- Highlights: • Incorporation of Cr 3+ increases the concentration of oxygen vacancies in TiO 2 nanoparticles. • Doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ into TiO 2 . • Pure and doped TiO 2 nanoparticles contain emission peaks related to oxygen vacancies. • Pure TiO 2 shows diamagnetism while Cr doped TiO 2 shows ferromagnetism. • The ferromagnetism is due to the interaction of Cr 3+ ions via oxygen vacancies. -- Abstract: Cr doped TiO 2 nanoparticles are prepared with three different concentrations of chromium, 1.5%, 3.0% and 4.5 mol% respectively. Doping decreases the crystallinity and increases the width of the X-ray diffraction peak. The Raman active E g peak of TiO 2 nanoparticles become asymmetric and shifted to higher energy on doping of 4.5% chromium. Electron paramagnetic resonance spectra reveal the presence of Cr 3+ in the host TiO 2 matrix. The absorption spectra of Cr doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ in octahedral coordination. Most of the visible emission peaks are due to the electrons trapped in the oxygen vacancy centers. Undoped TiO 2 nanoparticles show diamagnetism at room temperature while all chromium doped samples show ferromagnetism. The magnetization of the doped samples increases at 1.5% and 3.0% and decreases at 4.5%. The ferromagnetism arises owing to the interaction of the neighboring Cr 3+ ions via oxygen vacancies. The decrease of magnetization at the highest doping is possibly due to the antiferromagnetic interactions of Cr 3+ pairs or due to Cr 3+ -O 2− -Cr 3+ superexchange interaction in the lattice

  2. Tricalcium Phosphate Containing Sodium Hexametaphosphate as Polymer Suspension Stabilizer

    Directory of Open Access Journals (Sweden)

    K. Rahbar Shamskar

    2008-12-01

    Full Text Available Tricalcium phosphate as hydroxyapatite is used as a suspension stabilizer in styrene polymerization process. Particle size of TCP plays an essential role in the particles’ size distribution and geometrical form of polystyrene products. As the particle size of TCP is reduced, there will be much better chance to engulf the styrene particles. The higher the number of TCP particles surrounding each styrene particle, the lesser will be their tendency to form a large particle after collision. Therefore, there will be higher percentages of spherical polystyrene with small particle size and narrower size distribution in the product. Experimental results have indicated that the addition of sodium hexametaphosphate (SHMP to the reaction mixture of lime and phosphoric acid, after drying the product by spray dryer, lead to decrease the size of TCP particles from ca. 5 μm (without SHMP to ca. 1.5 μm (with SHMP. In this study, the role of TCP containing SHMP as polymer suspension stabilizer and consequently the beads size of polystyrene is investigated in laboratory scale. The results show that despite addition of SHMP to the reaction mixture of lime and phosphoric acid decreases the TCP particles size and the mean bead size of the product of polystyrene become larger than the product prepared by TCP without SHMP.

  3. SAXS Studies of TiO2 Nanoparticles in Polymer Electrolytes and in Nanostructured Films

    Directory of Open Access Journals (Sweden)

    Sigrid Bernstorff

    2010-11-01

    Full Text Available Polymer electrolytes as nanostructured materials are very attractive components for batteries and opto-electronic devices. (PEO8ZnCl2 polymer electrolytes were prepared from PEO and ZnCl2. The nanocomposites (PEO8ZnCl2/TiO2 themselves contained TiO2 nanograins. In this work, the influence of the TiO2 nanograins on the morphology and ionic conductivity of the nanocomposite was systematically studied by transmission small-angle X-ray scattering (SAXS simultaneously recorded with wide-angle X-ray diffraction (WAXD and differential scanning calorimetry (DSC at the synchrotron ELETTRA. Films containing nanosized grains of titanium dioxide (TiO2 are widely used in the research of optical and photovoltaic devices. The TiO2 films, prepared by chemical vapor deposition and e-beam epitaxy, were annealed in hydrogen atmospheres in the temperature range between 20 °C and 900 °C in order to study anatase-rutile phase transition at 740 °C. Also, grazing-incidence small angle X-ray scattering (GISAXS spectra for each TiO2 film were measured in reflection geometry at different grazing incident angles. Environmentally friendly galvanic cells, as well as solar cells of the second generation, are to be constructed with TiO2 film as working electrode, and nanocomposite polymer as electrolyte.

  4. Photocatalytic oxidative desulfurization of dibenzothiophene catalyzed by amorphous TiO2 in ionic liquid

    International Nuclear Information System (INIS)

    Zhu, Wenshuai; Xu, Yehai; Li, Huaming; Dai, Bilian; Xu, Hui; Wang, Chao; Chao, Yanhong; Liu, Hui

    2014-01-01

    Three types of TiO 2 were synthesized by a hydrolysis and calcination method. The catalysts were characterized by X-ray powder diffraction (XRD), diffuse reflectance spectrum (DRS), Raman spectra, and X-ray photoelectron spectroscopy (XPS). The XRD and Raman spectra indicated that amorphous TiO 2 was successfully obtained at 100 .deg. C. The results indicated that amorphous TiO 2 achieved the highest efficiency of desulfurization. The photocatalytic oxidation of dibenzothiophene (DBT), benzothiophene (BT), 4,6-dimethyldibenzothiophene (4,6-DMDBT) and dodecanethiol (RSH) in model oil was studied at room temperature (30 .deg. C) with three catalysts. The system contained amorphous TiO 2 , H 2 O 2 , and [Bmim]BF 4 ionic liquid, ultraviolet (UV), which played vitally important roles in the photocatalytic oxidative desulfurization. Especially, the molar ratio of H 2 O 2 and sulfur (O/S) was only 2 : 1, which corresponded to the stoichiometric reaction. The sulfur removal of DBT-containing model oil with amorphous TiO 2 could reach 96.6%, which was apparently superior to a system with anatase TiO 2 (23.6%) or with anatase - rutile TiO 2 (18.2%). The system could be recycled seven times without a signicant decrease in photocatalytic activity

  5. Preparation and tribological properties of self-lubricating TiO2/graphite composite coating on Ti6Al4V alloy

    International Nuclear Information System (INIS)

    Mu, Ming; Zhou, Xinjian; Xiao, Qian; Liang, Jun; Huo, Xiaodi

    2012-01-01

    Highlights: ► A TiO 2 /graphite composite coating is produced on Ti alloy by one-step PEO process. ► The TiO 2 /graphite composite coating exhibits excellent self-lubricating behavior. ► The self-lubricating composite coating improves the wear resistance by comparison to the conventional PEO coating. - Abstract: One-step plasma electrolytic oxidation (PEO) process in a graphite-dispersed phosphate electrolyte was used to prepare a graphite-containing oxide composite coating on Ti6Al4V alloy. The composition and microstructure of the oxide coatings produced in the phosphate electrolytes with and without addition of graphite were analyzed by X-ray diffractometer (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The tribological properties of the uncoated Ti6Al4V alloy and oxide coatings were evaluated using a reciprocating ball-on-disk tribometer. Results showed that the graphite-containing oxide composite coating can be successfully produced on Ti6Al4V alloy in the graphite-dispersed phosphate electrolyte using PEO process. The graphite-containing oxide composite coating registered much lower friction coefficient and wear rate than the uncoated Ti6Al4V alloy and the oxide coating without graphite under dry sliding condition, exhibiting excellent self-lubricating property.

  6. Investigation on the Photoelectrocatalytic Activity of Well-Aligned TiO2 Nanotube Arrays

    Directory of Open Access Journals (Sweden)

    Xiaomeng Wu

    2012-01-01

    Full Text Available Well-aligned TiO2 nanotube arrays were fabricated by anodizing Ti foil in viscous F− containing organic electrolytes, and the crystal structure and morphology of the TiO2 nanotube array were characterized and analyzed by XRD, SEM, and TEM, respectively. The photocatalytic activity of the TiO2 nanotube arrays was evaluated in the photocatalytic (PC and photoelectrocatalytic (PEC degradation of methylene blue (MB dye in different supporting solutions. The excellent performance of ca. 97% for color removal was reached after 90 min in the PEC process compared to that of PC process which indicates that a certain external potential bias favors the promotion of the electrode reaction rate on TiO2 nanotube array when it is under illumination. In addition, it is found that PEC process conducted in supporting solutions with low pH and containing Cl− is also beneficial to accelerate the degradation rate of MB.

  7. Synthesis and photocatalytic activity of Ce-doped TiO2 and TiO2 nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Arruda, L.B.; Pereira, E.A.; Paula, F.R.; Lisboa Filho, P.N. [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), SP (Brazil)

    2016-07-01

    samples with pH 7, XRD measurements showed the coexistence of TiO2 and sodium titanate phase. By decreasing the pH during acid washing the sodium content was eliminated leaving only the main phase. This behavior was observed for samples containing Cerium concentrations up to 0.2%. The obtained nanotubes presented multiple walls, having dimensions of 5 nm of diameter and about 200 nm of length. Energy dispersive X-ray spectroscopy analyzes revealed that nanotubes are mainly composed of titanium and oxygen, with small amounts of sodium when pH is 7 and sodium no was observed for the sample obtained at pH 4. It shows that synthesis conditions are very important in order to obtain single-phase structures. In addition, TiO2 nanotubes showed good photocatalytic activity with degradation around 100 minutes.(author)

  8. Synthesis and photocatalytic activity of Ce-doped TiO2 and TiO2 nanotubes

    International Nuclear Information System (INIS)

    Arruda, L.B.; Pereira, E.A.; Paula, F.R.; Lisboa Filho, P.N.

    2016-01-01

    samples with pH 7, XRD measurements showed the coexistence of TiO2 and sodium titanate phase. By decreasing the pH during acid washing the sodium content was eliminated leaving only the main phase. This behavior was observed for samples containing Cerium concentrations up to 0.2%. The obtained nanotubes presented multiple walls, having dimensions of 5 nm of diameter and about 200 nm of length. Energy dispersive X-ray spectroscopy analyzes revealed that nanotubes are mainly composed of titanium and oxygen, with small amounts of sodium when pH is 7 and sodium no was observed for the sample obtained at pH 4. It shows that synthesis conditions are very important in order to obtain single-phase structures. In addition, TiO2 nanotubes showed good photocatalytic activity with degradation around 100 minutes.(author)

  9. Preparation and solar-light photocatalytic activity of TiO2 composites: TiO2/kaolin, TiO2/diatomite, and TiO2/zeolite

    Science.gov (United States)

    Li, Y.; Li, S. G.; Wang, J.; Li, Y.; Ma, C. H.; Zhang, L.

    2014-12-01

    Three TiO2 loaded composites, TiO2/kaolin, TiO2/diatomite, and TiO2/zeolite, were prepared in order to improve the solar-light photocatalytic activity of TiO2. The results showed that the photocatalytic activity could obviously be enhanced by loading appropriate amount of inorganic mineral materials. Meanwhile, TiO2 content, heat-treatment temperature and heat-treatment time on the photocatalytic activity were reviewed. Otherwise, the effect of solar light irradiation time and dye concentration on the photocatalytic degradation of Acid Red B was investigated. Furthermore, the degradation mechanism and adsorption process were also discussed.

  10. Optical properties of TiO2 nanotube arrays fabricated by the electrochemical anodization method

    International Nuclear Information System (INIS)

    Ly, Ngoc Tai; Nguyen, Van Chien; Dao, Thi Hoa; Hoang To, Le Hong; Pham, Duy Long; Do, Hung Manh; Vu, Dinh Lam; Le, Van Hong

    2014-01-01

    Perpendicularly self-aligned TiO 2 nanotube samples of size of 3 × 5 cm 2 were fabricated by the electrochemical anodization method using a solution containing NH 4 F. Influences of the technological conditions such as NH 4 F concentration and anodization voltage were studied. It was found that NH 4 F concentration in the solution and anodization voltage significantly affect the diameter and length of a TiO 2 nanotube. The diameter and the length of a TiO 2 nanotube were observed and estimated by using scanning electron microscopy. It has shown that the largest diameter and the longest length of about 80 nm and 20 μm, respectively, were obtained for the sample anodized in a solution containing 0.4% of NH 4 F, under a voltage of 48 V. Photoluminescence spectra excited by laser lights having wavelengths of 325 and 442 nm (having energies higher and lower than the band gap energy of TiO 2 ) was recorded at room temperature for the TiO 2 nanotube arrays. An abnormal luminescence result was observed. It is experimental evidence that the manufactured TiO 2 nanotube array is an expected material for hydrogen splitting from water by photochemical effect under sunlight as well as for the nano solar cells. (paper)

  11. Structural and optical properties of AgCl-sensitized TiO2 (TiO2 @AgCl prepared by a reflux technique under alkaline condition

    Directory of Open Access Journals (Sweden)

    V. A. Mu’izayanti

    Full Text Available Abstract The AgCl-sensitized TiO2 (TiO2@AgCl has been prepared from the precursor of TiO2-rutile type which on its surface adsorb chloride anion (Cl- and various amounts of silver using AgNO3 as starting material: AgNO3/(AgNO3+TiO2 mass ratio of 0.00, 1.14, 3.25, 6.38 and 10.32%. Reflux under alkaline condition was the employed technique. All samples were characterized by X-ray diffraction (XRD and diffuse reflectance UV-vis spectroscopy. The sample without the addition of AgNO3 was analyzed by scanning electron microscope and surface area analyzer. The morphology of the sample showed a distribution of microspheres of approximately 0.5 to 1.0 µm and the specific surface area was 68 m2/g. XRD patterns indicated that the sample without the addition of AgNO3 contained two types of TiO2: rutile (major and anatase (minor, whereas the samples with the addition of AgNO3 consisted of one phase of AgCl and two types of TiO2: rutile and anatase. The bandgaps of the samples were in the range of 2.97 to 3.24 eV, which were very close to the bandgap of intrinsic TiO2 powder. The presence of 0.8, 2.6 and 4.4 wt% of AgCl in each sample resulted in an additional bandgap in visible light region of 1.90, 1.94 and 2.26 eV, respectively, whereas the presence of 9.4 wt% of AgCl in the sample resulted in two bandgaps in visible light region of 1.98 and 1.88 eV.

  12. A Facile Method for Loading CeO2 Nanoparticles on Anodic TiO2 Nanotube Arrays.

    Science.gov (United States)

    Liao, Yulong; Yuan, Botao; Zhang, Dainan; Wang, Xiaoyi; Li, Yuanxun; Wen, Qiye; Zhang, Huaiwu; Zhong, Zhiyong

    2018-04-03

    In this paper, a facile method was proposed to load CeO 2 nanoparticles (NPs) on anodic TiO 2 nanotube (NT) arrays, which leads to a formation of CeO 2 /TiO 2 heterojunctions. Highly ordered anatase phase TiO 2 NT arrays were fabricated by using anodic oxidation method, then these individual TiO 2 NTs were used as tiny "nano-containers" to load a small amount of Ce(NO 3 ) 3 solutions. The loaded anodic TiO 2 NTs were baked and heated to a high temperature of 450 °C, under which the Ce(NO 3 ) 3 would be thermally decomposed inside those nano-containers. After the thermal decomposition of Ce(NO 3 ) 3 , cubic crystal CeO 2 NPs were obtained and successfully loaded into the anodic TiO 2 NT arrays. The prepared CeO 2 /TiO 2 heterojunction structures were characterized by a variety of analytical technologies, including XRD, SEM, and Raman spectra. This study provides a facile approach to prepare CeO 2 /TiO 2 films, which could be very useful for environmental and energy-related areas.

  13. Physicochemical Study of Photocatalytic Activity of TiO2 Supported Palygorskite Clay Mineral

    Directory of Open Access Journals (Sweden)

    Lahcen Bouna

    2013-01-01

    Full Text Available This study deals with the influence of physicochemical parameters, namely, the photocatalyst loading, dye concentration, and pH of polluted solutions, on the degradation efficiency of Orange G (OG solutions containing TiO2 nanoparticles supported on palygorskite clay mineral (TiO2-Pal. The TiO2 photocatalyst attached to natural palygorskite fibers was elaborated by colloidal sol-gel route. It exhibits the anatase structure that is the most photoactive crystallographic form. The highest performances of supported photocatalyst on OG degradation were found using an optimum amount of TiO2-Pal around 0.8 g·L−1, which corresponds properly to ca. 0.4 g·L−1 of TiO2. This amount is interestingly lower than the 2.5 g·L−1 generally reported when using pure unsupported TiO2 powder. The photodegradation rate increases by decreasing OG initial concentration, and it was found significantly higher when the OG solution is either acidic (pH<4 or basic (pH≈11. For OG concentrations in the range 5×10-6– 5×10-4 M, the kinetic law of the OG degradation in presence of TiO2-Pal is similar to that reported for unsupported TiO2 nanopowder. It follows a Langmuir-Hinshelwood model with a first-order reaction and an apparent rate constant of about 2.9×10-2 min−1.

  14. Enhancement of tributyltin degradation under natural light by N-doped TiO2 photocatalyst

    International Nuclear Information System (INIS)

    Bangkedphol, S.; Keenan, H.E.; Davidson, C.M.; Sakultantimetha, A.; Sirisaksoontorn, W.; Songsasen, A.

    2010-01-01

    Photo-degradation of tributyltin (TBT) has been enhanced by TiO 2 nanoparticles doped with nitrogen (N-doped TiO 2 ). The N-doped catalyst was prepared by a sol-gel reaction of titanium (IV) tetraisopropoxide with 25% ammonia solution and calcined at various temperatures from 300 to 600 deg. C. X-ray diffraction results showed that N-doped TiO 2 remained amorphous at 300 deg. C. At 400 deg. C the anatase phase occurred then transformed to the rutile phase at 600 deg. C. The crystallite size calculated from Scherrer's equation was in the range of 16-51 nm which depended on the calcination temperature. N-doped TiO 2 calcined at 400 deg. C which contained 0.054% nitrogen, demonstrated the highest photocatalytic degradation of TBT at 28% in 3 h under natural light when compared with undoped TiO 2 and commercial photocatalyst, P25-TiO 2 which gave 14.8 and 18% conversion, respectively.

  15. Nanocomposites of TiO2/cyanoethylated cellulose with ultra high dielectric constants

    International Nuclear Information System (INIS)

    Madusanka, Nadeesh; Shivareddy, Sai G; Hiralal, Pritesh; Choi, Youngjin; Amaratunga, Gehan A J; Eddleston, Mark D; Oliver, Rachel A

    2016-01-01

    A novel dielectric nanocomposite containing a high permittivity polymer, cyanoethylated cellulose (CRS) and TiO 2 nanoparticles was successfully prepared with different weight percentages (10%, 20% and 30%) of TiO 2 . The intermolecular interactions and morphology within the polymer nanocomposites were analysed. TiO 2 /CRS nanofilms on SiO 2 /Si wafers were used to form metal–insulator–metal type capacitors. Capacitances and loss factors in the frequency range of 1 kHz–1 MHz were measured. At 1 kHz CRS-TiO 2 nanocomposites exhibited ultra high dielectric constants of 118, 176 and 207 for nanocomposites with 10%, 20% and 30% weight of TiO 2 respectively, significantly higher than reported values of pure CRS (21), TiO 2 (41) and other dielectric polymer-TiO 2 nanocomposite films. Furthermore, all three CRS-TiO 2 nanocomposites show a loss factor <0.3 at 1 kHz and low leakage current densities (10 −6 –10 −7 A cm −2 ). Leakage was studied using conductive atomic force microscopy and it was observed that the leakage is associated with TiO 2 nanoparticles embedded in the CRS polymer matrix. A new class of ultra high dielectric constant hybrids using nanoscale inorganic dielectrics dispersed in a high permittivity polymer suitable for energy management applications is reported. (paper)

  16. TiO2 (NanoParticles Extracted from Sugar-Coated Confectionery

    Directory of Open Access Journals (Sweden)

    Martina Lorenzetti

    2017-01-01

    Full Text Available As the debate about TiO2 food additive safety is still open, the present study focuses on the extraction and characterisation of TiO2 (nanoparticles added as a whitening agent to confectionary products, that is, chewing gum pellets. The aim was to (1 determine the colloidal properties of suspensions mutually containing TiO2 and all other chewing gum ingredients in biologically relevant media (preingestion conditions; (2 characterise the TiO2 (nanoparticles extracted from the chewing gum coating (after ingestion; and (3 verify their potential photocatalysis. The particle size distribution, in agreement with the zeta potential results, indicated that a small but significant portion of the particle population retained mean dimensions close to the nanosize range, even in conditions of moderate stability, and in presence of all other ingredients. The dispersibility was enhanced by proteins (i.e., albumin, which acted as surfactants and reduced particle size. The particle extraction methods involved conventional techniques and no harmful chemicals. The presence of TiO2 particles embedded in the sugar-based coating was confirmed, including 17–30% fraction in the nanorange (<100 nm. The decomposition of organics under UV irradiation proved the photocatalytic activity of the extracted (nanoparticles. Surprisingly, photocatalysis occurred even in presence of an amorphous SiO2 layer surrounding the TiO2 particles.

  17. One-step preparation and photocatalytic performance of vanadium doped TiO2 coatings

    International Nuclear Information System (INIS)

    Vasilić, R.; Stojadinović, S.; Radić, N.; Stefanov, P.; Dohčević-Mitrović, Z.; Grbić, B.

    2015-01-01

    In this paper, we have investigated one-step preparation of vanadium doped TiO 2 coatings formed by plasma electrolytic oxidation (PEO) of titanium in electrolyte containing 10 g/L Na 3 PO 4 ·12H 2 O + 0.5 g/L NH 4 VO 3 . The morphology, phase structure, and elemental composition of the formed coatings were characterized by atomic force microscopy (AFM), x-ray diffraction (XRD), and x-ray photoelectron spectroscopy (XPS) techniques. Ultraviolet–visible diffuse reflectance spectroscopy (UV–Vis DRS) was employed to evaluate the band gap energy of obtained coatings. Vanadium doped TiO 2 coatings are partly crystallized and mainly composed of anatase phase TiO 2 , with up to about 2 wt% of vanadium present in the surface layer of the oxide. The valence band photoelectron spectra and UV–Vis DRS showed that vanadium doped TiO 2 coatings exhibit notable red shift with respect to the pure TiO 2 coatings. The photocatalytic activity was evaluated by monitoring the degradation of methyl orange under simulated sunlight conditions. Photocatalytic activity of vanadium doped TiO 2 coatings increases with PEO time. Prolonged PEO times result in higher roughness of obtained coatings, thus increasing surface area available for methyl orange degradation. Vanadium doped TiO 2 coatings obtained after 180 s of PEO time exhibit the best photocatalytic activity and about 67% of methyl orange is degraded after 12 h of irradiation under simulated sunlight. - Highlights: • One-step preparation of V-doped TiO 2 coatings in 10 g/L Na 3 PO 4 ·12H 2 O + 0.5 g/L NH 4 VO 3 . • Properties of obtained coatings strongly depend on microdischarge characteristics. • Band gap of V-doped TiO 2 coatings is shifted towards red side of the spectrum. • V-doped TiO 2 coatings have better photocatalytic activity than pure TiO 2 . • After 12 h of simulated sunlight irradiation, 67% of methyl orange was decomposed

  18. Lead iron phosphate glass as a containment medium for disposal of high-level nuclear waste

    International Nuclear Information System (INIS)

    Boatner, L.A.; Sales, B.C.

    1989-01-01

    This patent describes lead-iron phosphate glasses containing a high level of Fe 2 O 3 for use as a storage medium for high-level radioactive nuclear waste. By combining lead-iron phosphate glass with various types of simulated high-level nuclear waste, a highly corrosion resistant, homogeneous, easily processed glass can be formed. For corroding solutions at 90 0 C, with solution pH values in the range between 5 and 9, the corrosion rate of the lead-iron phosphate nuclear waste glass is at least 10 2 to 10 3 times lower than the corrosion rate of a comparable borosilicate nuclear waste glass. The presence of Fe 2 O 3 in forming the lead-iron phosphate glass is critical. The lead-iron phosphate waste glasses can be prepared with minimal modification of the technology developed for processing borosilicate glass nuclear wasteforms

  19. Instability of Hydrogenated TiO2

    Energy Technology Data Exchange (ETDEWEB)

    Nandasiri, Manjula I.; Shutthanandan, V.; Manandhar, Sandeep; Schwarz, Ashleigh M.; Oxenford, Lucas S.; Kennedy, John V.; Thevuthasan, Suntharampillai; Henderson, Michael A.

    2015-11-06

    Hydrogenated TiO2 (H-TiO2) is toted as a viable visible light photocatalyst. We report a systematic study on the thermal stability of H-implanted TiO2 using X-ray photoelectron spectroscopy (XPS), ultraviolet photoelectron spectroscopy (UPS), Rutherford backscattering spectrometry (RBS) and nuclear reaction analysis (NRA). Protons (40 keV) implanted at a ~2 atom % level within a ~120 nm wide profile of rutile TiO2(110) were situated ~300 nm below the surface. NRA revealed that this H-profile broadened preferentially toward the surface after annealing at 373 K, dissipated out of the crystal into vacuum at 473 K, and was absent within the beam sampling depth (~800 nm) at 523 K. Photoemission showed that the surface was reduced in concert with these changes. Similar anneals had no effect on pristine TiO2(110). The facile bulk diffusivity of H in rutile, as well as its activity toward interfacial reduction, significantly limits the utilization of H-TiO2 as a photocatalyst. This work was supported by the US Department of Energy, Office of Science, Office of Basic Energy Sciences, Division of Chemical Sciences, Geosciences & Biosciences. Pacific Northwest National Laboratory (PNNL) is a multiprogram national laboratory operated for DOE by Battelle. The research was performed using the Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by the Department of Energy's Office of Biological and Environmental Research and located at Pacific Northwest National Laboratory.

  20. Preparation of TiO2 Nanocrystallite Powders Coated with 9 mol% ZnO for Cosmetic Applications in Sunscreens

    Directory of Open Access Journals (Sweden)

    Moo-Chin Wang

    2012-02-01

    Full Text Available The preparation of TiO2 nanocrystallite powders coated with and without 9 mol% ZnO has been studied for cosmetic applications in sunscreens by a co-precipitation process using TiCl4 and Zn(NO32·6H2O as starting materials. XRD results show that the phases of anatase TiO2 and rutile TiO2 coexist for precursor powders without added ZnO (T-0Z and calcined at 523 to 973 K for 2 h. When the T-0Z precursor powders are calcined at 1273 K for 2 h, only the rutile TiO2 appears. In addition, when the TiO2 precursor powders contain 9 mol% ZnO (T-9Z are calcined at 873 to 973 K for 2 h, the crystallized samples are composed of the major phase of rutile TiO2 and the minor phases of anatase TiO2 and Zn2Ti3O8. The analyses of UV/VIS/NIR spectra reveal that the absorption of the T-9Z precursor powders after being calcined has a red-shift effect in the UV range with increasing calcination temperature. Therefore, the TiO2 nanocrystallite powders coated with 9 mol% ZnO can be used as the attenuate agent in the UV-A region for cosmetic applications in sunscreens.

  1. TiO2-TiO2 composite resistive humidity sensor: ethanol crosssensitivity

    International Nuclear Information System (INIS)

    Ghalamboran, Milad; Saedi, Yasin

    2016-01-01

    The fabrication method and characterization results of a TiO 2 -TiO 2 composite bead used for humidity sensing along with its negative cross-sensitivity to ethanol vapor are reported. The bead shaped resistive sample sensors are fabricated by the drop-casting of a TiO 2 slurry on two Pt wire segments. The dried bead is pre-fired at 750°C and subsequently impregnated with a Ti-based sol. The sample is ready for characterization after a thermal annealing at 600°C in air. Structurally, the bead is a composite of the micron-sized TiO 2 crystallites embedded in a matrix of nanometric TiO 2 particle aggregates. The performance of the beads as resistive humidity sensors is recorded at room temperature in standard humidity level chambers. Results evince the wide dynamic range of the sensors fabricated in the low relative humidity range. While the sensor conductance is not sensitive to ethanol vapor in dry air, in humid air, sensor's responses are negatively affected by the contaminant. (paper)

  2. EFFECT OF THE REDUCTION TEMPERATURE INTO CATALYTIC ACTIVITY OF Ni SUPPORTED BY TiO2, AL2O2 AND TiO2/AL2O3 FOR CONVERSION CO2 INTO METHANE

    Directory of Open Access Journals (Sweden)

    Hery Haerudin

    2010-06-01

    Full Text Available Nickel catalysts, containing 6% (w/w of nickel, have been prepared using TiO2, Al2O3 and mixture of TiO2-Al2O3 (1:9. The catalysts were used for CO2 conversion into methane. The characteristics of catalysts were studied by determination of its specific surface area, temperature programmed reaction technique and X-ray diffraction. The specific surface area were varied slightly by different temperature of reduction, namely after reduction at 300°C it was 39, 120 and 113 m2/g and after reduction at 400°C it was 42, 135  and 120 m2/g for 6% nickel catalysts supported on TiO2, Al2O3 and mixture of TiO2-Al2O3 (1:9 respectively. Temperature program reaction studies (TPO and TPR showed that NiTiOx species were possibly formed during the pretreatments which has shown by the shift of its peak to the lower temperature on Ni catalyst, that supported on mixture of TiO2-Al2O3 compared with catalysts supported on individual TiO2 or Al2O3. The nickel species on reduced Ni catalysts supported on TiO2 and on mixture of TiO2-Al2O3 could be detected by X-ray diffraction. The catalyst's activities toward CH4 formation were affected by the reduction temperature. Activity for CH4 formation was decreased in the following order: Ni/ TiO2 > Ni/ TiO2: Al2O3 > Ni/ Al2O3 and Ni/ TiO2: Al2O3 > Ni/ TiO2> Ni/ Al2O3, when catalysts were reduced at 300°C or 400°C respectively. The CO2 conversion was decreased in the following order: Ni/ Al2O3 > Ni/ TiO2: Al2O3 > Ni/ TiO2 when catalysts were reduced at 300°C or 400°C respectively.   Keywords: nickel catalyst, carbondioxide, methane

  3. Data on the effect of improved TiO2/FTO interface and Ni(OH2 cocatalyst on the photoelectrochemical performances and stability of CdS cased ZnIn2S4/TiO2 heterojunction

    Directory of Open Access Journals (Sweden)

    Mahadeo A. Mahadik

    2018-04-01

    Full Text Available This data article presents the experimental evidences of the effect of TiO2-fluorine doped tin oxide interface annealing and Ni(OH2 cocatalysts on the photoelectrochemical, structural, morphological and optical properties of Ni(OH2/CdS/ZnIn2S4/TiO2 heterojunction. The Raman spectroscopy exhibits the sharp features of the rutile phase of TiO2 and in agreement with the X-ray diffraction data. The band gap energy of the 500 °C sample was found to be 3.12 eV, further it was increased to 3.20, 3.22 eV for samples annealed at 600 and 700 °C respectively. The decrease in the band gap energy at 500 °C related to the oxygen vacancies and was analysed by photoluminescence spectroscopy analysis. The synthesis, characterization methods and other experimental details of TiO2 based heterostructure are also provided. The presence of CdS and ZnIn2S4 coating on surface of TiO2 electrodes providing a high surface area, extended visible absorption and helps to improve the change separation. This data article contains data related to the research article entitled “Highly efficient and stable 3D Ni(OH2/CdS/ZnIn2S4/TiO2 heterojunction under solar light: Effect of an improved TiO2/FTO interface and cocatalyst” (Mahadik et al., 2017 [1]. Keywords: Annealed TiO2 nanorods, CdS/ZnIn2S4/TiO2 heterostructure, Ni(OH2 cocatalyst, TiO2-FTO interface

  4. Influence of substrate temperature and silver-doping on the structural and optical properties of TiO_2 films

    International Nuclear Information System (INIS)

    Fischer, Dieter

    2016-01-01

    Evaporation of titanium together with activated oxygen is used to grow TiO_2 films and simultaneously with silver to grow Ag–TiO_2 films (5 at.% Ag) onto sapphire substrates at three different substrate temperatures: − 190, 30, and 200 °C. The obtained films were characterized by X-ray powder diffraction, Raman, X-ray photoelectron, ultraviolet–visible spectroscopy, and transmission electron microscope investigations. The properties of TiO_2 films varied with the substrate temperature. Amorphous, transparent TiO_2 films were grown at − 190 °C and opaque, polycrystalline films at 200 °C, respectively. Surprisingly, at room temperature black, amorphous TiO_2 films are obtained which transform at 350 °C into a mixture of the anatase and brookite polymorph. In the amorphous state of the TiO_2 films a predefined rutile arrangement is suggested by Raman investigations, and the contraction of the lattice constant c of anatase phases (tetragonal, space group I 4_1/amd) depending on the substrate temperature is experimentally observed. The silver-doped TiO_2 films deposited at − 190 and 30 °C contain Ag-particles with 2 nm in size inside the TiO_2 matrix, which after annealing segregate under increasing particle sizes. The silver-doping stabilizes the anatase polymorph and yields to reduced titanium species in the films especially during deposition at 30 °C. The Ag–TiO_2 films deposited at − 190 °C are transparent up to 350 °C. In the undoped as well as silver-doped TiO_2 films the rutile polymorph is directly formed at 200 °C as main phase. - Highlights: • At room temperature black, amorphous TiO_2 films are obtained. • A predefined rutile arrangement is suggested in amorphous TiO_2 films. • Annealed TiO_2 films crystallize to a mixture of the anatase and brookite polymorph. • In TiO_2 and Ag-doped TiO_2 films the rutile polymorph is directly formed at 200 °C. • Ag-doped TiO_2 films stabilize the anatase polymorph and reduced titanium

  5. Treatment of organic waste solutions containing tributyl phosphate

    International Nuclear Information System (INIS)

    Drobnik, S.

    The two processes developed in the laboratory for treating waste solutions containing TBP, namely TBP separation with phosphoric acid and saponification were tested on a semi-industrial scale. A waste solution from the first phase of the Karlsruhe reprocessing plant was used

  6. Crystal Structure And Optical Properties Of TiO2 Thin Films Prepared By Reactive RF Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Goto S.

    2015-06-01

    Full Text Available In sputtering deposition process of TiO2, metal Ti or sintered TiO2 target is used as deposition source. In this study, we have compared the characteristic of target materials. When TiO2 target was used, stoichiometric TiO2 films was deposited under the Ar atmosphere containing 1.0% of oxygen. The highest sputtering rate under this atmosphere was 3.9nm/min at 3.4W/cm2. But, sintered TiO2 target is fragile and cannot endure higher density of input power than 3.4W/cm2. On the other hand, Ti target needs higher oxygen concentration (8% in sputtering gas atmosphere for obtaining rutile/anatase. Even though Ti target can be input twice power density of 7.9W/cm2, the highest deposition rate for Ti target was 1.4/nm, which was ~35% of the highest rate for TiO2 target. Then we have study out the composite target consisting of Ti plate and TiO2 chips. Using the composite target, stoichiometric TiO2 films were prepared in the rate of 9.6nm/min at 6.8 W/cm2 under the atmosphere of Ar/2.5%O2. Furthermore, we have found that the TiO2 films obtained from the composite target consisted of about 100% anatase, whereas TiO2 films obtained from other target have rutile dominant structure. The optical band gap energy of the film is determined by using the Tauc plot. The calculated band gap energies for the films deposited by Ti target and composite target were 2.95 and 3.24eV, which are equivalent to that of rutile and anatase structure, respectively.

  7. Application of a TiO2 nanocomposite in earplugs, a case study of noise reduction.

    Science.gov (United States)

    Ibrahimi Ghavamabadi, Leila; Fouladi Dehaghi, Behzad; Hesampour, Morteza; Ahmadi Angali, Kambiz

    2018-03-13

    Use of hearing protection devices (HPDs) has become necessary when other control measures cannot reduce noise to a safe and standard level. In most countries, more effective hearing protection devices are in demand. The aim of this study was to examine the effects of titanium dioxide (TiO 2 ) nanoparticles on noise reduction efficiency in a polyvinyl chloride (PVC) earplug. An S-60 type PVC polymer as main matrix and TiO 2 with 30 nm size were used. PVC/TiO 2 nanocomposite was mixed at a temperature of 160 °C and 40 rounds per minute (rpm) and the samples were prepared with 0, 0.2 and 0.5 wt% of TiO 2 nanoparticle concentrations. Earplug samples with PVC/TiO 2 (0.2, 0.5 wt%) nanoparticles, when compared with raw earplugs, showed almost equal noise attenuation at low frequencies (500- 125 Hz). However, at high frequencies (2-8 kHz), the power of noise reduction of earplugs containing TiO 2 nanoparticles was significantly increased. The results of the present study showed that samples containing nanoparticles of TiO 2 had more noticeable noise reduction abilities at higher frequencies in comparison with samples without the nanoparticles.

  8. Formation of chelating agent driven anodized TiO2 nanotubular membrane and its photovoltaic application

    Science.gov (United States)

    Banerjee, Subarna; Misra, Mano; Mohapatra, Susanta K.; Howard, Cameron; Mohapatra, Srikanta K.; Kamilla, Sushanta K.

    2010-04-01

    Titania (TiO2) nanotubular arrays provide an exciting material for dye sensitizing solar cells (DSSC) because of their large surface area, lower recombination losses, and fast charge transport properties along the nanotubes. In this paper, design of a next generation DSSC using a TiO2 nanotubular membrane is discussed. A single step, green process is developed to produce stable large area, free-standing TiO2 nanotubular films (in a short time, 30-60 min) by anodizing Ti using an organic electrolyte, containing disodium salt of ethylene diaminetetraacetic acid (Na2[H2EDTA]) as complexing agent, and subsequent drying. Transparent, crack-free TiO2 films, 20-41 µm thick containing ordered hexagonal TiO2 nanotubes are achieved by this process. Films having a geometrical area up to 16.5 cm2 with pore openings of 182 nm have been obtained. These films have been etched to form membranes which provide an exciting prospect for front side illuminated DSSC with good mass and photon transport properties as well as wettability. A photovoltaic efficiency of 2.7% is achieved using a front side illuminated DSSC compared to 1.77% using back side illumination.

  9. Formation of chelating agent driven anodized TiO(2) nanotubular membrane and its photovoltaic application.

    Science.gov (United States)

    Banerjee, Subarna; Misra, Mano; Mohapatra, Susanta K; Howard, Cameron; Mohapatra, Srikanta K; Kamilla, Sushanta K

    2010-04-09

    Titania (TiO(2)) nanotubular arrays provide an exciting material for dye sensitizing solar cells (DSSC) because of their large surface area, lower recombination losses, and fast charge transport properties along the nanotubes. In this paper, design of a next generation DSSC using a TiO(2) nanotubular membrane is discussed. A single step, green process is developed to produce stable large area, free-standing TiO(2) nanotubular films (in a short time, 30-60 min) by anodizing Ti using an organic electrolyte, containing disodium salt of ethylene diaminetetraacetic acid (Na(2)[H(2)EDTA]) as complexing agent, and subsequent drying. Transparent, crack-free TiO(2) films, 20-41 microm thick containing ordered hexagonal TiO(2) nanotubes are achieved by this process. Films having a geometrical area up to 16.5 cm(2) with pore openings of 182 nm have been obtained. These films have been etched to form membranes which provide an exciting prospect for front side illuminated DSSC with good mass and photon transport properties as well as wettability. A photovoltaic efficiency of 2.7% is achieved using a front side illuminated DSSC compared to 1.77% using back side illumination.

  10. Formation of chelating agent driven anodized TiO2 nanotubular membrane and its photovoltaic application

    International Nuclear Information System (INIS)

    Banerjee, Subarna; Misra, Mano; Mohapatra, Susanta K; Howard, Cameron; Mohapatra, Srikanta K; Kamilla, Sushanta K

    2010-01-01

    Titania (TiO 2 ) nanotubular arrays provide an exciting material for dye sensitizing solar cells (DSSC) because of their large surface area, lower recombination losses, and fast charge transport properties along the nanotubes. In this paper, design of a next generation DSSC using a TiO 2 nanotubular membrane is discussed. A single step, green process is developed to produce stable large area, free-standing TiO 2 nanotubular films (in a short time, 30-60 min) by anodizing Ti using an organic electrolyte, containing disodium salt of ethylene diaminetetraacetic acid (Na 2 [H 2 EDTA]) as complexing agent, and subsequent drying. Transparent, crack-free TiO 2 films, 20-41 μm thick containing ordered hexagonal TiO 2 nanotubes are achieved by this process. Films having a geometrical area up to 16.5 cm 2 with pore openings of 182 nm have been obtained. These films have been etched to form membranes which provide an exciting prospect for front side illuminated DSSC with good mass and photon transport properties as well as wettability. A photovoltaic efficiency of 2.7% is achieved using a front side illuminated DSSC compared to 1.77% using back side illumination.

  11. Water Adsorption on TiO2

    DEFF Research Database (Denmark)

    Hammer, Bjørk; Wendt, Stefan; Besenbacher, Flemming

    2010-01-01

    Scanning Tunneling Microscopy (STM) studies and Density Functional Theory (DFT) investigations of the interaction of water with the rutile TiO2 (110) surface are summarized. From high-resolution STM the following reactions have been revealed: water adsorption and diffusion in the Ti troughs, water...... dissociation in bridging oxygen vacancies, assembly of adsorbed water monomers into rapidly diffusing water dimers, and formation of water dimers by reduction of oxygen molecules. The STM results are rationalized based on DFT calculations, revealing the bonding geometries and reaction pathways of the water...

  12. Nuclear microscopy as a tool in TiO2 nanoparticles bioaccumulation studies in aquatic species

    Science.gov (United States)

    Pinheiro, Teresa; Moita, Liliana; Silva, Luís; Mendonça, Elsa; Picado, Ana

    2013-07-01

    Engineered Titanium nanoparticles are used for a wide range of applications from coatings, sunscreen cosmetic additives to solar cells or water treatment agents. Inevitably environmental exposure can be expected and data on the ecotoxicological evaluation of nanoparticles are still scarce. The potential effects of nanoparticles of titanium dioxide (TiO2) on two model organisms, the water flea, Daphnia magna and the duckweed Lemna minor, were examined in semichronic toxicity tests. Daphnia and Lemna were exposed to TiO2 nanoparticles (average particle size value of 28 ± 11 nm (n = 42); concentration range, 1.4-25 mg/L) by dietary route and growth in medium containing the nanoparticles of TiO2, respectively. Both morphology and microdistribution of Ti in the individuals were examined by nuclear microscopy techniques. A significant amount of TiO2 was found accumulated in Daphnia exposed to nanoparticles. Nuclear microscopy imaging revealed that Ti was localized only in the digestive tract of the Daphnia, which displayed difficulty in eliminating the nanoparticles from their body. Daphnia showed higher mortality when exposed to higher concentrations of TiO2 (>10 mg/L). The exposure to TiO2 nanoparticles above 25 mg/L caused morphological alterations in Lemna. The roots became stiff and fronds colorless. The Ti mapping of cross-sections of roots and fronds showed that Ti was mainly deposited in the epidermis of the fronds and roots, with minor internalization. In summary, exposure of aquatic organisms to TiO2 nanoparticles may alter the physiology of these organisms at individual and population levels, posing risks to aquatic ecosystems.

  13. Nuclear microscopy as a tool in TiO2 nanoparticles bioaccumulation studies in aquatic species

    International Nuclear Information System (INIS)

    Pinheiro, Teresa; Moita, Liliana; Silva, Luís; Mendonça, Elsa; Picado, Ana

    2013-01-01

    Engineered Titanium nanoparticles are used for a wide range of applications from coatings, sunscreen cosmetic additives to solar cells or water treatment agents. Inevitably environmental exposure can be expected and data on the ecotoxicological evaluation of nanoparticles are still scarce. The potential effects of nanoparticles of titanium dioxide (TiO 2 ) on two model organisms, the water flea, Daphnia magna and the duckweed Lemna minor, were examined in semichronic toxicity tests. Daphnia and Lemna were exposed to TiO 2 nanoparticles (average particle size value of 28 ± 11 nm (n = 42); concentration range, 1.4–25 mg/L) by dietary route and growth in medium containing the nanoparticles of TiO 2 , respectively. Both morphology and microdistribution of Ti in the individuals were examined by nuclear microscopy techniques. A significant amount of TiO 2 was found accumulated in Daphnia exposed to nanoparticles. Nuclear microscopy imaging revealed that Ti was localized only in the digestive tract of the Daphnia, which displayed difficulty in eliminating the nanoparticles from their body. Daphnia showed higher mortality when exposed to higher concentrations of TiO 2 (>10 mg/L). The exposure to TiO 2 nanoparticles above 25 mg/L caused morphological alterations in Lemna. The roots became stiff and fronds colorless. The Ti mapping of cross-sections of roots and fronds showed that Ti was mainly deposited in the epidermis of the fronds and roots, with minor internalization. In summary, exposure of aquatic organisms to TiO 2 nanoparticles may alter the physiology of these organisms at individual and population levels, posing risks to aquatic ecosystems

  14. Cosensitization Properties of Glutathione-Protected Au25 Cluster on Ruthenium Dye-Sensitized TiO2 Photoelectrode

    Directory of Open Access Journals (Sweden)

    Kazuya Nakata

    2013-01-01

    Full Text Available Cosensitization by glutathione-protected Au25 clusters on Ru complex, N719-sensitized TiO2 photoelectrodes is demonstrated. Glutathione-protected Au25 clusters showed no significant changes in properties after adsorption onto TiO2 particles, as confirmed by optical absorption spectroscopy, transmission electron microscopy, and laser desorption/ionization mass spectrometry. Adsorption property of the glutathione-protected Au25 clusters depends on the pH, which affects the incident photon-to-current conversion efficiency (IPCE of the TiO2 photoelectrode containing Au25 clusters. When pH 7. The IPCE of a TiO2 photoelectrode sensitized by both glutathione-protected Au25 clusters and N719 was increased compared with photoelectrodes containing either glutathione-protected Au25 clusters or N719, which suggests that glutathione-protected Au25 clusters act as a coadsorbent for N719 on TiO2 photoelectrodes. This is also supported by the results that the IPCE of N719-sensitized TiO2 photoelectrodes increased upon addition of glutathione. Furthermore, cosensitization by glutathione-protected Au25 clusters on N719-sensitized TiO2 photoelectrodes allows that wavelength of photoelectric conversion was extended to the near infrared (NIR region. These results suggest that glutathione-protected Au25 clusters act not only as a coadsorbent to increase IPCE but also as an NIR-active sensitizer.

  15. New insights into the origin of visible-light photocatalytic activity in Se-modified anatase TiO2 from screened coulomb hybrid DFT calculations

    KAUST Repository

    Harb, Moussab

    2013-01-01

    ), TiO(2-x)Sex (containing Se2- species), and TiO(2-x)Se2x (containing Se2 2- species) reveal significant enhanced visible-light optical absorption spectra with new absorption features appearing at 500, 600, and 690 nm, respectively. Our calculated

  16. TiO2 Deposition on AZ31 Magnesium Alloy Using Plasma Electrolytic Oxidation

    Directory of Open Access Journals (Sweden)

    Leon White

    2013-01-01

    Full Text Available Plasma electrolytic oxidation (PEO has been used in the past as a useful surface treatment technique to improve the anticorrosion properties of Mg alloys by forming protective layer. Coatings were prepared on AZ31 magnesium alloy in phosphate electrolyte with the addition of TiO2 nanoparticles using plasma electrolytic oxidation (PEO. This present work focuses on developing a TiO2 functional coating to create a novel electrophotocatalyst while observing the surface morphology, structure, composition, and corrosion resistance of the PEO coating. Microstructural characterization of the coating was investigated by X-ray diffraction (XRD and scanning electron microscopy (SEM followed by image analysis and energy dispersive spectroscopy (EDX. The corrosion resistance of the PEO treated samples was evaluated with electrochemical impedance spectroscopy (EIS and DC polarization tests in 3.5 wt.% NaCl. The XRD pattern shows that the components of the oxide film include Mg from the substrate as well as MgO and Mg2TiO4 due to the TiO2 nanoparticle addition. The results show that the PEO coating with TiO2 nanoparticles did improve the corrosion resistance when compared to the AZ31 substrate alloy.

  17. Bactericidal Effects of HVOF-Sprayed Nanostructured TiO2 on Pseudomonas aeruginosa

    Science.gov (United States)

    Jeffery, B.; Peppler, M.; Lima, R. S.; McDonald, A.

    2010-01-01

    Titanium dioxide (TiO2) has been shown to exhibit photocatalytic bactericidal activity. This preliminary study focused on examining the photocatalytic activity of high-velocity oxy-fuel (HVOF) sprayed nanostructured TiO2 coatings to kill Pseudomonas aeruginosa. The surfaces of the nanostructured TiO2 coatings were lightly polished before addition of the bacterial solution. Plates of P. aeruginosa were grown, and then suspended in a phosphate buffer saline (PBS) solution. The concentration of bacteria used was determined by a photo-spectrometer, which measured the amount of light absorbed by the bacteria-filled solution. This solution was diluted and pipetted onto the coating, which was exposed to white light in 30-min intervals, up to 120 min. It was found that on polished HVOF-sprayed coatings exposed to white light, 24% of the bacteria were killed after exposure for 120 min. On stainless steel controls, approximately 6% of the bacteria were not recovered. These preliminary results show that thermal-sprayed nanostructured TiO2 coatings exhibited photocatalytic bactericidal activity with P. aeruginosa.

  18. Lead iron phosphate glass as a containment medium for disposal of high-level nuclear waste

    Science.gov (United States)

    Boatner, Lynn A.; Sales, Brian C.

    1989-01-01

    Lead-iron phosphate glasses containing a high level of Fe.sub.2 O.sub.3 for use as a storage medium for high-level radioactive nuclear waste. By combining lead-iron phosphate glass with various types of simulated high-level nuclear waste, a highly corrosion resistant, homogeneous, easily processed glass can be formed. For corroding solutions at 90.degree. C., with solution pH values in the range between 5 and 9, the corrosion rate of the lead-iron phosphate nuclear waste glass is at least 10.sup.2 to 10.sup.3 times lower than the corrosion rate of a comparable borosilicate nuclear waste glass. The presence of Fe.sub.2 O.sub.3 in forming the lead-iron phosphate glass is critical. Lead-iron phosphate nuclear waste glass can be prepared at temperatures as low as 800.degree. C., since they exhibit very low melt viscosities in the 800.degree. to 1050.degree. C. temperature range. These waste-loaded glasses do not readily devitrify at temperatures as high as 550.degree. C. and are not adversely affected by large doses of gamma radiation in H.sub.2 O at 135.degree. C. The lead-iron phosphate waste glasses can be prepared with minimal modification of the technology developed for processing borosilicate glass nuclear wasteforms.

  19. Efficient bioconversion of rice straw to ethanol with TiO2/UV pretreatment.

    Science.gov (United States)

    Kang, Hee-Kyoung; Kim, Doman

    2012-01-01

    Rice straw is a lignocellulosic biomass that constitutes a renewable organic substance and alternative source of energy; however, its structure confounds the liberation of monosaccharides. Pretreating rice straw using a TiO(2)/UV system facilitated its hydrolysis with Accellerase 1000(™), suggesting that hydroxyl radicals (OH·) from the TiO(2)/UV system could degrade lignin and carbohydrates. TiO(2)/UV pretreatment was an essential step for conversion of hemicellulose to xylose; optimal conditions for this conversion were a TiO(2) concentration of 0.1% (w/v) and an irradiation time of 2 h with a UV-C lamp at 254 nm. After enzymatic hydrolysis, the sugar yields from rice straw pretreated with these parameters were 59.8 ± 0.7% of the theoretical for glucose (339 ± 13 mg/g rice straw) and 50.3 ± 2.8% for xylose (64 ± 3 mg/g rice straw). The fermentation of enzymatic hydrolysates containing 10.5 g glucose/L and 3.2 g xylose/L with Pichia stipitis produced 3.9 g ethanol/L with a corresponding yield of 0.39 g/g rice straw. The maximum possible ethanol conversion rate is 76.47%. TiO(2)/UV pretreatment can be performed at room temperature and atmospheric pressure and demonstrates potential in large-scale production of fermentable sugars.

  20. Solar photocatalytic degradation of isoproturon over TiO2/H-MOR composite systems

    International Nuclear Information System (INIS)

    Sharma, Mangalampalli V. Phanikrishna; Durgakumari, Valluri; Subrahmanyam, Machiraju

    2008-01-01

    The photocatalytic degradation and mineralization of isoproturon herbicide was investigated in aqueous solution containing TiO 2 over H-mordenite (H-MOR) photocatalysts under solar light. The catalysts are characterized by X-ray diffraction (XRD), UV-Vis diffused reflectance spectra (UV-Vis DRS), Fourier transform-infra red spectra (FT-IR) and scanning electron microscopy (SEM) techniques. The effect of TiO 2 , H-MOR support and different wt% of TiO 2 over the support on the photocatalytic degradation and influence of parameters such as TiO 2 loading, catalyst amount, pH and initial concentration of isoproturon on degradation are evaluated. 15 wt% TiO 2 /H-MOR composite is found to be optimum. The degradation reaction follows pseudo-first order kinetics and is discussed in terms of Langmuir-Hinshelwood (L-H) kinetic model. The extent of isoproturon mineralization studied with chemical oxygen demand (COD) and total organic carbon (TOC) measurements and ∼80% mineralization occurred in 5 h. A plausible mechanism is proposed based on the intermediates identified by liquid chromatography-mass spectroscopy (LC-MS)

  1. Solar photocatalytic degradation of isoproturon over TiO2/H-MOR composite systems.

    Science.gov (United States)

    Sharma, Mangalampalli V Phanikrishna; Durgakumari, Valluri; Subrahmanyam, Machiraju

    2008-12-30

    The photocatalytic degradation and mineralization of isoproturon herbicide was investigated in aqueous solution containing TiO2 over H-mordenite (H-MOR) photocatalysts under solar light. The catalysts are characterized by X-ray diffraction (XRD), UV-Vis diffused reflectance spectra (UV-Vis DRS), Fourier transform-infra red spectra (FT-IR) and scanning electron microscopy (SEM) techniques. The effect of TiO2, H-MOR support and different wt% of TiO2 over the support on the photocatalytic degradation and influence of parameters such as TiO2 loading, catalyst amount, pH and initial concentration of isoproturon on degradation are evaluated. 15wt% TiO2/H-MOR composite is found to be optimum. The degradation reaction follows pseudo-first order kinetics and is discussed in terms of Langmuir-Hinshelwood (L-H) kinetic model. The extent of isoproturon mineralization studied with chemical oxygen demand (COD) and total organic carbon (TOC) measurements and approximately 80% mineralization occurred in 5h. A plausible mechanism is proposed based on the intermediates identified by liquid chromatography-mass spectroscopy (LC-MS).

  2. Ecotoxicity of TiO2 to Daphnia similis under irradiation

    International Nuclear Information System (INIS)

    Marcone, Glauciene P.S.; Oliveira, Ádria C.; Almeida, Gilberto; Umbuzeiro, Gisela A.; Jardim, Wilson F.

    2012-01-01

    Graphical abstract: EC50 (mg L −1 ) values to TiO 2 samples obtained in toxicity tests with Daphnia similis under different conditions of illumination (UV A and visible radiation) and in the dark (as standard protocols). P25: commercial sample containing 30% rutile and 70% anatase; M-S: synthesized sample containing 30% rutile and 70% anatase; Anatase-S: synthesized sample containing 100% anatase; Rutile-S: synthesized sample containing 100% rutile and P25*: commercial sample containing 100% rutile. Highlights: ► Some key physicochemical parameters of nano TiO 2 explain the toxicity observed. ► Under UV A radiation, TiO 2 becomes more toxic to D. similis. ► Toxicity tests of photoactive nano materials require photons as control parameter. - Abstract: Currently, there are a large number of products (sunscreen, pigments, cosmetics, plastics, toothpastes and photocatalysts) that use TiO 2 nanoparticles. Due to this large production, these nanoparticles can be released into the aquatic, terrestrial and aerial environments at relative high concentration. TiO 2 in natural water has the capacity to harm aquatic organisms such as the Daphnia (Cladocera) species, mainly because the photocatalytic properties of this semiconductor. However, very few toxicity tests of TiO 2 nanoparticles have been conducted under irradiation. The aim of this study was to evaluate anatase and rutile TiO 2 toxicity to Daphnia similis exploring their photocatalytic properties by incorporating UV A and visible radiation as a parameter in the assays. Anatase and rutile TiO 2 samples at the highest concentration tested (100 mg L −1 ) were not toxic to D. similis, neither in the dark nor under visible light conditions. The anatase form and a mixture of anatase and rutile, when illuminated by a UV A black light with a peak emission wavelength of 360 nm, presented photo-dependent EC50 values of 56.9–7.8 mg L −1 , which indicates a toxicity mechanism caused by ROS (reactive oxygen species

  3. Corrosion of alloy 22 in phosphate ions effect and chloride containing solutions

    International Nuclear Information System (INIS)

    Carranza, Ricardo M.

    2009-01-01

    Alloy 22 belongs to Ni-Cr-Mo family. This alloy resists the most aggressive environments for industrial applications, in oxidizing as well as reducing conditions, because exhibits an excellent uniform and localized corrosion resistance in aqueous solution. Because of its outstanding corrosion resistant, this alloy is one of the candidate to be considered for the outer shell of the canister that would contain high level radioactive nuclear wastes in a geological repository. The aim of this work is to study ion phosphate influence over Alloy 22 corrosion behavior under aggressive conditions, such as high temperature and high ion chloride concentration, where this material might be susceptible to crevice corrosion. Two different types of samples were used: cylinder specimens for uniform corrosion behavior studies and Prismatic Crevice Assembly (PCA) specimens for localized corrosion studies. Electrochemical tests were performed in deaerated aqueous solution of 1 M NaCl and 1 M NaCl with different phosphate additions at 90 C degrees and pH near neutral. The anodic film and corrosion products obtained were studied by SEM/EDS. Cyclic Potentiodynamic Polarization (CPP) curves obtained for uniform corrosion studies, showed an increase of the passivity range in phosphate containing solutions. The passive current value was 1 μA/cm 2 approximately in all the tests. PCA electrochemical tests, that combined a CPP with a potentiostatic polarization step for 2 hours in between the forward and reverse scan, showed crevice corrosion development in some cases. The repassivation potential value, determined by the intersection of the forward and the reverse scan, increased with phosphate addition. A complete crevice corrosion inhibition effect was found for phosphate concentration higher than 0.3 M. These results indicate that the passivity potential range depend on phosphate presence and might be related with the incorporation of the anion in the passive film. Results of the tests

  4. Sol–gel synthesis of highly TiO2 aerogel photocatalyst via high temperature supercritical drying

    Directory of Open Access Journals (Sweden)

    Rebah Moussaoui

    2017-09-01

    Full Text Available Nanocrystalline powders of TiO2 xerogel and aerogel were prepared by using acid-modified sol–gel approach. For TiO2 aerogel material (TA, the solvent was high temperature supercritically extracted at 300 °C and 100 bars. However, the TiO2 xerogel material (TX was dried at 200 °C and ambient pressure. The effects of the drying processes on the crystalline structure, phase transformation and grain growth were determined by Raman spectroscopy, SAED and X-ray diffraction (XRD analyses using Rietveld refinement method. The TiO2 aerogel was composed of anatase crystalline structure. The TiO2 xerogel material was composed of anatase, brookite and small amount of amorphous phase with anatase as dominant phase. The TX sample still contains a relatively high concentration of carbon than that of TA, indicating the amorphous character of TiO2 xerogel. These materials were applied as catalyst for the degradation of indigo carmine in aqueous medium. Photo-degradation ability of TA and TX was compared to the TiO2 commercial Degussa P25. The photo-catalytic results showed that the degradation efficiency was in the order TA > P25 > TX. The photo-degradation of indigo carmine followed pseudo first order reaction kinetics.

  5. Study of the highly ordered TiO2 nanotubes physical properties prepared with two-step anodization

    Science.gov (United States)

    Pishkar, Negin; Ghoranneviss, Mahmood; Ghorannevis, Zohreh; Akbari, Hossein

    2018-06-01

    Highly ordered hexagonal closely packed titanium dioxide nanotubes (TiO2 NTs) were successfully grown by a two-step anodization process. The TiO2 NTs were synthesized by electrochemical anodization of titanium foils in an ethylene glycol based electrolyte solution containing 0.3 wt% NH4F and 2 vol% deionized (DI) water at constant potential (50 V) for 1 h at room temperature. Physical properties of the TiO2 NTs, which were prepared via one and two-step anodization, were investigated. Atomic Force Microscopy (AFM) analysis revealed that anodization and subsequently peeled off the TiO2 NTs caused to the periodic pattern on the Ti surface. In order To study the nanotubes morphology, Field Emission Scanning Electron Microscopy (FESEM) was used, which was revealed that the two-step anodization resulted highly ordered hexagonal TiO2 NTs. Crystal structures of the TiO2 NTs were mainly anatase, determined by X-ray diffraction analysis. Optical studies were performed by Diffuse Reflection Spectra (DRS) and Photoluminescence (PL) analysis showed that the band gap of TiO2 NTs prepared via two-step anodization was lower than the band gap of samples prepared by one-step anodization process.

  6. Visible photoenhanced current-voltage characteristics of Au : TiO2 nanocomposite thin films as photoanodes

    International Nuclear Information System (INIS)

    Naseri, N; Amiri, M; Moshfegh, A Z

    2010-01-01

    In this investigation, the effect of annealing temperature and concentration of gold nanoparticles on the photoelectrochemical properties of sol-gel deposited Au : TiO 2 nanocomposite thin films is studied. Various gold concentrations have been added to the TiO 2 thin films and their properties are compared. All the deposited samples are annealed at different temperatures. The optical density spectra of the films show the formation of gold nanoparticles in the films. The optical bandgap energy of the Au : TiO 2 films decreases with increasing Au concentration. The crystalline structure of the nanocomposite films is studied by x-ray diffractometry indicating the formation of gold nanocrystals in the anatase TiO 2 nanocrystalline thin films. X-ray photoelectron spectroscopy reveals that the presence of gold in the metallic state and the formation of TiO 2 are stoichiometric. The photoelectrochemical properties of the Au : TiO 2 samples are characterized using a compartment cell containing H 2 SO 4 and KOH as cathodic and anodic electrolytes, respectively. It is found that the addition of Au nanoparticles in TiO 2 films enhances the photoresponse of the layer and the addition of gold nanocrystals with an optimum value of 5 mol% resulted in the highest photoelectrochemical activity. Moreover, the photoresponse of the samples is also enhanced with an increase in the annealing temperature.

  7. Novel Nanotechnology of TiO2 Improves Physical-Chemical and Biological Properties of Glass Ionomer Cement

    Directory of Open Access Journals (Sweden)

    Daniela Dellosso Cibim

    2017-01-01

    Full Text Available The aim of this study was to assess the performance of glass ionomer cement (GIC added with TiO2 nanotubes. TiO2 nanotubes [3%, 5%, and 7% (w/w] were incorporated into GIC’s (Ketac Molar EasyMix™ powder component, whereas unblended powder was used as control. Physical-chemical-biological analysis included energy dispersive spectroscopy (EDS, surface roughness (SR, Knoop hardness (SH, fluoride-releasing analysis, cytotoxicity, cell morphology, and extracellular matrix (ECM composition. Parametric or nonparametric ANOVA were used for statistical comparisons (α≤0.05. Data analysis revealed that EDS only detected Ti at the 5% and 7% groups and that GIC’s physical-chemical properties were significantly improved by the addition of 5% TiO2 as compared to 3% and GIC alone. Furthermore, regardless of TiO2 concentration, no significant effect was found on SR, whereas GIC-containing 7% TiO2 presented decreased SH values. Fluoride release lasted longer for the 5% and 7% TiO2 groups, and cell morphology/spreading and ECM composition were found to be positively affected by TiO2 at 5%. In conclusion, in the current study, nanotechnology incorporated in GIC affected ECM composition and was important for the superior microhardness and fluoride release, suggesting its potential for higher stress-bearing site restorations.

  8. Synergistic operation of photocatalytic degradation and Fenton process by magnetic Fe3O4 loaded TiO2

    Science.gov (United States)

    Sun, Qiong; Hong, Yong; Liu, Qiuhong; Dong, Lifeng

    2018-02-01

    The magnetic Fe3O4 loaded anatase TiO2 photocatalysts with different mass ratios were successfully synthesized by a one-step convenient calcining method. The morphology and structure analysis revealed that Fe3O4 was formed in TiO2 with very fine-grained particles. After a small amount of Fe3O4 loaded onto TiO2, the photocatalytic property enhanced obviously for the degradation of organic dye. Furthermore, the photo-Fenton-like catalysis of the iron-containing samples could also be induced after the addition of hydrogen peroxide. The apparent kinetic constant of the reaction that catalyzed by Fe-TiO2 was about 5.3 and 8.3 times of that catalyzed by TiO2 or Fe3O4 only, respectively, proving an effective synergistic contribution of the photocatalysis and Fenton reaction in the composite. Compared with Fe3O4 or free Fe3+ ions, only 13% of iron in TiO2 dissolved into acidic solution (25% for Fe3O4 and 100% for Fe3+) after the reaction, which confirmed the iron had been well immobilized onto TiO2. In addition, the extremely stable photocatalytic activity in cycling experiments proved the immobilized iron had been tightly attached onto TiO2, indicating the great potential of the catalyst for practical applications.

  9. Evaluation of the content of TiO2 nanoparticles in the coatings of chewing gums.

    Science.gov (United States)

    Dudefoi, William; Terrisse, Hélène; Popa, Aurelian Florin; Gautron, Eric; Humbert, Bernard; Ropers, Marie-Hélène

    2018-02-01

    Titanium dioxide is a metal oxide used as a white pigment in many food categories, including confectionery. Due to differences in the mass fraction of nanoparticles contained in TiO 2 , the estimated intakes of TiO 2 nanoparticles differ by a factor of 10 in the literature. To resolve this problem, a better estimation of the mass of nanoparticles present in food products is needed. In this study, we focused our efforts on chewing gum, which is one of the food products contributing most to the intake of TiO 2 . The coatings of four kinds of chewing gum, where the presence of TiO 2 was confirmed by Raman spectroscopy, were extracted in aqueous phases. The extracts were analysed by transmission electron microscopy (TEM), X-ray diffraction, Fourier Transform Raman spectroscopy, and inductively coupled plasma atomic emission spectroscopy (ICP-AES) to establish their chemical composition, crystallinity and size distribution. The coatings of the four chewing gums differ chemically from each other, and more specifically the amount of TiO 2 varies from one coating to another. TiO 2 particles constitute the entire coating of some chewing gums, whereas for others, TiO 2 particles are embedded in an organic matrix and/or mixed with minerals like calcium carbonate, talc, or magnesium silicate. We found 1.1 ± 0.3 to 17.3 ± 0.9 mg TiO 2 particles per piece of chewing gum, with a mean diameter of 135 ± 42 nm. TiO 2 nanoparticles account for 19 ± 4% of all particles, which represents a mass fraction of 4.2 ± 0.1% on average. The intake of nanoparticles is thus highly dependent on the kind of chewing gum, with an estimated range extending from 0.04 ± 0.01 to 0.81 ± 0.04 mg of nano-TiO 2 per piece of chewing gum. These data should serve to refine the exposure scenario.

  10. Synthesis, characterization and photocatalytic activity of porous WO3/TiO2 hollow microspheres

    International Nuclear Information System (INIS)

    Yang, Liuyang; Si, Zhichun; Weng, Duan; Yao, Youwei

    2014-01-01

    Porous WO 3 /TiO 2 hollow microspheres were prepared by a spray drying method for photodegradation of methylene blue and phenol. The catalysts were characterized by X-ray diffraction, Field Emission Scanning Electron Microscope, High Resolution Transmission Electron Microscope, N 2 adsorption–desorption measurements, Raman spectrometer, UV–Vis Diffuse Reflectance Spectroscopy and Zeta-Meter measurements. The results showed that the tungsten oxides mainly existed in highly dispersed amorphous form on anatase when the loading amount of tungsten oxide was below 3 mol%. The improved photocatalytic activity under UV light irradiation of the WO 3 /TiO 2 catalyst mainly arises from the enhanced charge separation efficiency rather than the improved light absorbance by highly dispersed amorphous tungsten oxides. Highly dispersed amorphous WO x can form a shallowly trapped site due to its similar band structure with TiO 2 . The strongly electron-withdrawing of tungsten oxide in highly dispersed state facilitates the electron transition between titanium and WO x , and consequently improves the charge separation. The enhanced acidity of catalyst by WO x in reactant environment also improved the charge separation efficiency due to the timely transition of holes and electrons accumulated on TiO 2 and WO x , respectively. However, the improved photocatalytic activity under visible light irradiation of the WO 3 /TiO 2 catalyst mainly arises from light harvest. TiO 2 containing 3 mol% WO 3 displayed the highest photocatalytic activity under UV light irradiation while that containing 4 mol% WO 3 present highest activity under visible light irradiation

  11. Investigations of percutaneous uptake of ultrafine TiO2 particles at the high energy ion nanoprobe LIPSION

    International Nuclear Information System (INIS)

    Menzel, F.; Reinert, T.; Vogt, J.; Butz, T.

    2004-01-01

    Micronised TiO 2 particles with a diameter of about 15 nm are used in sunscreens as physical UV filter. Due to the small particle size it may be supposed that TiO 2 particles can pass through the uppermost horny skin layer (stratum corneum) via intercellular channels and penetrate into deeper vital skin layers. Accumulations of TiO 2 particles in the skin can decrease the threshold for allergies of the immune system or cause allergic reactions directly. Spatially resolved ion beam analysis (PIXE, RBS, STIM and secondary electron imaging) was carried out on freeze-dried cross-sections of biopsies of pig skin, on which four different formulations containing TiO 2 particles were applied. The investigations were carried out at the high energy ion nanoprobe LIPSION in Leipzig with a 2.25 MeV proton beam, which was focused to a diameter of 1 μm. The analysis concentrated on the penetration depth and on pathways of the TiO 2 particles into the skin. In these measurements a penetration of TiO 2 particles through the s. corneum into the underlying stratum granulosum via intercellular space was found. Hair follicles do not seem to be important penetration pathways because no TiO 2 was detected inside. The TiO 2 particle concentration in the stratum spinosum was below the minimum detection limit of about 1 particle/μm 2 . These findings show the importance of coating the TiO 2 particles in order to prevent damage of RNA and DNA of skin cells by photocatalytic reactions of the penetrated particles caused by absorption of UV light

  12. Synthesis and Mechanical Properties Investigation of Nano TiO2/Glass/Epoxy Hybrid Nanocomposite

    Directory of Open Access Journals (Sweden)

    Hamid Reza Salehi

    2015-10-01

    Full Text Available Mechanical properties of epoxy and glass/epoxy filled with 0.25, 0.5 and 1 vol% of TiO2 nanoparticles have been studied using tensile and three-point bending tests. For the TiO2/epoxy nanocomposites, the results showed that the strength and stiffness were improved, though the strain at ultimate strength point and breaking strain decreased. Moreover, the hybrid nanocomposites composed of 4 layers of woven E-glass fabric and TiO2/epoxy matrix were fabricated and cut onaxis and 45° off-axis by water jet. The results of tensile and three-point bending tests indicated a remarkable improvement in the strength and stiffness that could not be related to the mechanical improvement of the matrix. The samples containing 1 vol% nano TiO2 were improved relative to samples without the nanoparticles. The tensile strength of the on-axis and off-axis samples containing 1 vol% TiO2 increased by about 25.9% and 17.9%, in the order given, compared to that of the glass/epoxy specimens. In three-point bending test, the strength of the on-axis and off-axis specimens was improved 26% and 23.2%, respectively. In addition, the tensile stiffness of the onaxis and off-axis samples containing 1 vol% TiO2 increased, respectively, by about 14.4% and 17.5% compared to that of the glass/epoxy specimens. Also for the same on-axis and off-axis samples the three-point bending stiffness increased about 19.8% and 14.6%, respectively. The whole investigation on the microstructure of the hybrid nanocomposites illustrated that stronger interfaces between the fiber and TiO2/epoxy matrix were formed and improvement was noticed on mechanical properties of ternary composite compared to those of the fiber/epoxy composites. The analysis of damage zones of hybrid nanocomposites showed that the surface area of the damaged zone declined considerably due to the brittle behavior of TiO2-filled specimens but the area below the stress-strain curve, showing energy absorption during the test

  13. TiO2 beads and TiO2-chitosan beads for urease immobilization

    International Nuclear Information System (INIS)

    Ispirli Doğaç, Yasemin; Deveci, İlyas; Teke, Mustafa; Mercimek, Bedrettin

    2014-01-01

    The aim of the present study is to synthesize TiO 2 beads for urease immobilization. Two different strategies were used to immobilize the urease on TiO 2 beads. In the first method (A), urease enzyme was immobilized onto TiO 2 beads by adsorption and then crosslinking. In the second method (B), TiO 2 beads were coated with chitosan-urease mixture. To determine optimum conditions of immobilization, different parameters were investigated. The parameters of optimization were initial enzyme concentration (0.5; 1; 1.5; 2 mg/ml), alginate concentration (1; 2; 3%), glutaraldehyde concentration (1; 2; 3% v/v) and chitosan concentration (2; 3; 4 mg/ml). The optimum enzyme concentrations were determined as 1.5 mg/ml for A and 1.0 mg/ml for B. The other optimum conditions were found 2.0% (w/v) for alginate concentration (both A and B); 3.0 mg/ml for chitosan concentration (B) and 2.0% (v/v) for glutaraldehyde concentration (A). The optimum temperature (20-60 °C), optimum pH (3.0-10.0), kinetic parameters, thermal stability (4–70 °C), pH stability (4.0-9.0), operational stability (0-230 min) and reusability (20 times) were investigated for characterization. The optimum temperatures were 30 °C (A), 40 °C (B) and 35 °C (soluble). The temperature profiles of the immobilized ureases were spread over a large area. The optimum pH values for the soluble urease and immobilized urease prepared by using methods (A) and (B) were found to be 7.5, 7.0, 7.0, respectively. The thermal stabilities of immobilized enzyme sets were studied and they maintained 50% activity at 65 °C. However, at this temperature free urease protected only 15% activity. - Highlights: • TiO 2 and TiO 2 -chitosan beads for urease immobilization have been prepared and characterized. • The beads used in this work are good matrices for the immobilization of urease. • The immobilized urease was shown to have good properties and stabilities (pH and thermal stability, operational stability). • The 50% activity was protected after 11 cycles for method A and 16 cycles for method B

  14. Flexible Bench-Scale Recirculating Flow CPC Photoreactor for Solar Photocatalytic Degradation of Methylene Blue Using Removable TiO2 Immobilized on PET Sheets

    Directory of Open Access Journals (Sweden)

    Doaa M. EL-Mekkawi

    2016-01-01

    Full Text Available TiO2 immobilized on polyethylene (PET nonwoven sheet was used in the solar photocatalytic degradation of methylene blue (MB. TiO2 Evonik Aeroxide P25 was used in this study. The amount of loaded TiO2 on PET was approximately 24%. Immobilization of TiO2 on PET was conducted by dip coating process followed by exposing to mild heat and pressure. TiO2/PET sheets were wrapped on removable Teflon rods inside home-made bench-scale recirculating flow Compound Parabolic Concentrator (CPC photoreactor prototype (platform 0.7 × 0.2 × 0.4 m3. CPC photoreactor is made up of seven low iron borosilicate glass tubes connected in series. CPC reflectors are made of stainless steel 304. The prototype was mounted on a platform tilted at 30°N local latitude in Cairo. A centrifugal pump was used to circulate water containing methylene blue (MB dye inside the glass tubes. Efficient photocatalytic degradation of MB using TiO2/PET was achieved upon the exposure to direct sunlight. Chemical oxygen demand (COD analyses reveal the complete mineralization of MB. Durability of TiO2/PET composite was also tested under sunlight irradiation. Results indicate only 6% reduction in the amount of TiO2 after seven cycles. No significant change was observed for the physicochemical characteristics of TiO2/PET after the successive irradiation processes.

  15. Most consumed processed foods by patients on hemodialysis: Alert for phosphate-containing additives and the phosphate-to-protein ratio.

    Science.gov (United States)

    Watanabe, Marcela T; Araujo, Raphael M; Vogt, Barbara P; Barretti, Pasqual; Caramori, Jacqueline C T

    2016-08-01

    Hyperphosphatemia is common in patients with chronic kidney disease (CKD) stages IV and V because of decreased phosphorus excretion. Phosphatemia is closely related to dietary intake. Thus, a better understanding of sources of dietary phosphate consumption, absorption and restriction, particularly inorganic phosphate found in food additives, is key to prevent consequences of this complication. Our aims were to investigate the most commonly consumed processed foods by patients with CKD on hemodialysis, to analyze phosphate and protein content of these foods using chemical analysis and to compare these processed foods with fresh foods. We performed a cross-sectional descriptive analytical study using food frequency questionnaires to rank the most consumed industrialized foods and beverages. Total phosphate content was determined by metavanadate colorimetry, and nitrogen content was determined by the Kjeldahl method. Protein amounts were estimated from nitrogen content. The phosphate-to-protein ratio (mg/g) was then calculated. Processed meat protein and phosphate content were compared with the nutritional composition of fresh foods using the Brazilian Food Composition Table. Phosphate measurement results were compared with data from the Food Composition Table - Support for Nutritional Decisions. An α level of 5% was considered significant. Food frequency questionnaires were performed on 100 patients (mean age, 59 ± 14 years; 57% male). Phosphate additives were mentioned on 70% of the product labels analyzed. Proteins with phosphate-containing additives provided approximately twice as much phosphate per gram of protein compared with that of fresh foods (p processed foods are higher than those of fresh foods, as well as phosphate-to-protein ratio. A better understanding of phosphate content in foods, particularly processed foods, may contribute to better control of phosphatemia in patients with CKD. Copyright © 2016 European Society for Clinical Nutrition and

  16. Properties and solubility of chrome in iron alumina phosphate glasses containing high level nuclear waste

    International Nuclear Information System (INIS)

    Huang, W.; Day, D.E.; Ray, C.S.; Kim, C.W.; Reis, S.T.D.

    2004-01-01

    Chemical durability, glass formation tendency, and other properties of iron alumina phosphate glasses containing 70 wt% of a simulated high level nuclear waste (HLW), doped with different amounts of Cr 2 O 3 , have been investigated. All of the iron alumina phosphate glasses had an outstanding chemical durability as measured by their small dissolution rate (1 . 10 -9 g/(cm 2 . min)) in deionized water at 90 C for 128 d, their low normalized mass release as determined by the product consistency test (PCT) and a barely measurable corrosion rate of 2 . d) after 7 d at 200 C by the vapor hydration test (VHT). The solubility limit for Cr 2 O 3 in the iron phosphate melts was estimated at 4.1 wt%, but all of the as-annealed melts contained a few percent of crystalline Cr 2 O 3 that had no apparent effect on the chemical durability. The chemical durability was unchanged after deliberate crystallization, 48 h at 650 C. These iron phosphate waste forms, with a waste loading of at least 70 wt%, can be readily melted in commercial refractory crucibles at 1250 C for 2 to 4 h, are resistant to crystallization, meet all current US Department of Energy requirements for chemical durability, and have a solubility limit for Cr 2 O 3 which is at least three times larger than that for borosilicate glasses. (orig.)

  17. Photocatalytic activity of Sulfer-doped TiO2 fiber under visible light illumination (Joint research)

    International Nuclear Information System (INIS)

    Takeyama, Akinori; Yamamoto, Shunya; Yoshikawa, Masahito; Hasegawa, Yoshio; Awatsu, Satoshi

    2007-03-01

    The Sol-Gel derived precursor fiber was annealed under hydrogen disulfeid (H 2 S) following oxygen atmosphere, Sulfur-doped TiO 2 fiber was obtained. Crystal structure of the fiber was identified as anatase phase of TiO 2 . The energy band gap of the fiber was narrower by about 0.06 eV than that of anatase, which showed that it could absorb visible light. The fiber contains about 0.58 atomic % of Sulfur, and they located at the oxygen lattice site of TiO 2 . Under visible light illumination, the fiber degraded Trichloroethylen (TCE) and produced carbon dioxide (CO 2 ). This shows Sulfur-doped TiO 2 fiber has the photocatalytic activity under visible light illumination. (author)

  18. Controlled Directional Growth of TiO2 Nanotubes

    DEFF Research Database (Denmark)

    In, Su-il; Hou, Yidong; Abrams, Billie

    2010-01-01

    We demonstrate how the anodization direction and growth rate of vertically aligned, highly ordered TiO2 nanotube (NT) arrays can be controlled and manipulated by the local concentration of O-2 in the electrolyte. This leads to the growth of highly active TiO2 NT arrays directly on nonconducting s...

  19. Silicon protected with atomic layer deposited TiO2

    DEFF Research Database (Denmark)

    Seger, Brian; Tilley, S. David; Pedersen, Thomas

    2013-01-01

    The present work demonstrates that tuning the donor density of protective TiO2 layers on a photocathode has dramatic consequences for electronic conduction through TiO2 with implications for the stabilization of oxidation-sensitive catalysts on the surface. Vacuum annealing at 400 °C for 1 hour o...

  20. Preparation, characterization and photocatalytic activity of TiO2 ...

    Indian Academy of Sciences (India)

    Photocatalyst; TiO2 nanoparticle; polyaniline; conducting polymer; core-shell nanocomposite. 1. Introduction ..... tine TiO2 nanoparticles, HCl-doped PANI and PANI/TiO2 ..... Karim M R, Lim K T, Lee M S, Kim K and Yeum J H 2009 Synth. Met.

  1. Glass-ceramic nuclear waste forms obtained by crystallization of SiO 2-Al 2O 3-CaO-ZrO 2-TiO 2 glasses containing lanthanides (Ce, Nd, Eu, Gd, Yb) and actinides (Th): Study of the crystallization from the surface

    Science.gov (United States)

    Loiseau, P.; Caurant, D.

    2010-07-01

    Glass-ceramic materials containing zirconolite (nominally CaZrTi 2O 7) crystals in their bulk can be envisaged as potential waste forms for minor actinides (Np, Am, Cm) and Pu immobilization. In this study such matrices are synthesized by crystallization of SiO 2-Al 2O 3-CaO-ZrO 2-TiO 2 glasses containing lanthanides (Ce, Nd, Eu, Gd, Yb) and actinides (Th) as surrogates. A thin partially crystallized layer containing titanite and anorthite (nominally CaTiSiO 5 and CaAl 2Si 2O 8, respectively) growing from glass surface is also observed. The effect of the nature and concentration of surrogates on the structure, the microstructure and the composition of the crystals formed in the surface layer is presented in this paper. Titanite is the only crystalline phase able to significantly incorporate trivalent lanthanides whereas ThO 2 precipitates in the layer. The crystal growth thermal treatment duration (2-300 h) at high temperature (1050-1200 °C) is shown to strongly affect glass-ceramics microstructure. For the system studied in this paper, it appears that zirconolite is not thermodynamically stable in comparison with titanite growing form glass surface. Nevertheless, for kinetic reasons, such transformation (i.e. zirconolite disappearance to the benefit of titanite) is not expected to occur during interim storage and disposal of the glass-ceramic waste forms because their temperature will never exceed a few hundred degrees.

  2. Linear and nonlinear optical studies of bare and copper doped TiO2 nanoparticles via sol gel technique

    Science.gov (United States)

    Rajamannan, B.; Mugundan, S.; Viruthagiri, G.; Praveen, P.; Shanmugam, N.

    2014-01-01

    In general, the nanoparticles of TiO2 may exist in the phases of anatase, rutile and brookite. In the present work, we used titanium terta iso propoxide and 2-propanol as a common starting material to prepare the precursors of bare and copper doped nanosized TiO2. Then the synthesized products were calcinated at 500 °C and after calcination the pure TiO2 nanoparticles in anatase phase were harvested. The crystallite sizes of bare and copper doped TiO2 nanoparticles were calculated from X-ray diffraction analysis. The existence of functional groups of the samples was identified by Fourier transform infrared spectroscopy. The optical properties of bare and doped samples were carried out using UV-DRS and photoluminescence measurements. The surface morphology and the element constitution of the copper doped TiO2 nanoparticles were studied by scanning electron microscope fitted with energy dispersive X-ray spectrometer arrangement. The nonlinear optical properties of the products were confirmed by Kurtz second harmonic generation (SHG) test and the output power generated by the nanoparticle was compared with that of potassium di hydrogen phosphate (KDP).

  3. Self-organized TiO2 nanotubular arrays for photoelectrochemical hydrogen generation: effect of crystallization and defect structures

    International Nuclear Information System (INIS)

    Mahajan, V K; Misra, M; Raja, K S; Mohapatra, S K

    2008-01-01

    The effect of crystallization and surface chemistry of nanotubular titanium dioxide (TiO 2 ) in connection with the photoelectrochemical process is reported in this investigation. TiO 2 nanotubular arrays were synthesized by a simple anodization process in an acidified fluoride electrolyte at room temperature. The TiO 2 nanotubes were amorphous in as-anodized condition; their transformation to crystalline phases was a function of annealing temperature and gaseous environment. The anatase phase was observed predominantly after annealing in non-oxidizing atmospheres, whereas annealing in an oxygen environment showed a mixture of anatase and rutile phases. X-ray photoelectron spectroscopy was used to determine the chemical environment of the surface, which revealed the presence of phosphate, oxygen vacancies and pentacoordinated Ti in hydrogen annealed samples. Diffuse reflectance photospectrometry of non-oxygen annealed samples showed long absorption tails extending in the visible region. The photoelectrochemical response of the TiO 2 nanotubes annealed in different conditions was investigated. Photoelectrochemical performance under simulated solar light was improved by annealing the nanotubular TiO 2 samples in non-oxidizing environment

  4. Fabricating TiO2 nanocolloids by electric spark discharge method at normal temperature and pressure

    Science.gov (United States)

    Tseng, Kuo-Hsiung; Chang, Chaur-Yang; Chung, Meng-Yun; Cheng, Ting-Shou

    2017-11-01

    In this study, TiO2 nanocolloids were successfully fabricated in deionized water without using suspending agents through using the electric spark discharge method at room temperature and under normal atmospheric pressure. This method was exceptional because it did not create nanoparticle dispersion and the produced colloids contained no derivatives. The proposed method requires only traditional electrical discharge machines (EDMs), self-made magnetic stirrers, and Ti wires (purity, 99.99%). The EDM pulse on time (T on) and pulse off time (T off) were respectively set at 50 and 100 μs, 100 and 100 μs, 150 and 100 μs, and 200 and 100 μs to produce four types of TiO2 nanocolloids. Zetasizer analysis of the nanocolloids showed that a decrease in T on increased the suspension stability, but there were no significant correlations between T on and particle size. Colloids produced from the four production configurations showed a minimum particle size between 29.39 and 52.85 nm and a zeta-potential between -51.2 and -46.8 mV, confirming that the method introduced in this study can be used to produce TiO2 nanocolloids with excellent suspension stability. Scanning electron microscopy with energy dispersive spectroscopy also indicated that the TiO2 colloids did not contain elements other than Ti and oxygen.

  5. Fabricating TiO2 nanocolloids by electric spark discharge method at normal temperature and pressure.

    Science.gov (United States)

    Tseng, Kuo-Hsiung; Chang, Chaur-Yang; Chung, Meng-Yun; Cheng, Ting-Shou

    2017-11-17

    In this study, TiO 2 nanocolloids were successfully fabricated in deionized water without using suspending agents through using the electric spark discharge method at room temperature and under normal atmospheric pressure. This method was exceptional because it did not create nanoparticle dispersion and the produced colloids contained no derivatives. The proposed method requires only traditional electrical discharge machines (EDMs), self-made magnetic stirrers, and Ti wires (purity, 99.99%). The EDM pulse on time (T on ) and pulse off time (T off ) were respectively set at 50 and 100 μs, 100 and 100 μs, 150 and 100 μs, and 200 and 100 μs to produce four types of TiO 2 nanocolloids. Zetasizer analysis of the nanocolloids showed that a decrease in T on increased the suspension stability, but there were no significant correlations between T on and particle size. Colloids produced from the four production configurations showed a minimum particle size between 29.39 and 52.85 nm and a zeta-potential between -51.2 and -46.8 mV, confirming that the method introduced in this study can be used to produce TiO 2 nanocolloids with excellent suspension stability. Scanning electron microscopy with energy dispersive spectroscopy also indicated that the TiO 2 colloids did not contain elements other than Ti and oxygen.

  6. Studies on the recovery of 233U from phosphate containing aqueous waste using DBDECMP as extractant

    International Nuclear Information System (INIS)

    Sagar, V.B.; Oak, M.S.; Pawar, S.M.; Sivaramakrishnan, C.K.; Patil, S.K.

    1990-01-01

    A method for the recovery and purification of 233 U from phosphate containing analytical waste is developed. Extraction studies with Di-butyl N,N-diethylcarbamoylmethylphosphonate (DBDECMP) in xylene were carried out to explore the feasibility of separation and purification of 233 U from such wastes. Based on the data obtained, optimum conditions for the recovery of 233 U are suggested. (author) 11 refs.; 1 fig.; 3 tabs

  7. Treatment of phosphate-containing oily wastewater by coagulation and microfiltration.

    Science.gov (United States)

    Zhang, Jin; Sun, Yu-xin; Huang, Zhi-feng; Liu, Xing-qin; Meng, Guang-yao

    2006-01-01

    The oily wastewater generated from pretreatment unit of electrocoating industry contains oils, phosphate, organic solvents, and surfactants. In order to improve the removal efficiencies of phosphate and oils, to mitigate the membrane fouling, coagulation for ceramic membrane microfiltration of oily wastewater was performed. The results of filtration tests show that the membrane fouling decreased and the permeate flux and quality increased with coagulation as pretreatment. At the coagulant Ca (OH)2 dosage of 900 mg/L, the removal efficiency of phosphate was increased from 46.4% without coagulation to 99.6%; the removal of COD and oils were 97.0% and 99.8%, respectively. And the permeate flux was about 70% greater than that when Ca(OH)2 was not used. The permeate obtained from coagulation and microfiltration can be reused as make-up water, and the recommended operation conditions for pilot and industrial application are transmembrane pressure of 0.10 MPa and cross-flow velocity of 5 m/s. The comparison results show that 0.2 microm ZrO2 microfilter with coagulation could be used to perform the filtration rather than conventional ultrafilter, with very substantial gain in flux and removal efficiency of phosphate.

  8. Optimized nanostructured TiO2 photocatalysts

    Science.gov (United States)

    Topcu, Selda; Jodhani, Gagan; Gouma, Pelagia

    2016-07-01

    Titania is the most widely studied photocatalyst. In it’s mixed-phase configuration (anatase-rutile form) -as manifested in the commercially available P25 Degussa material- titania was previously found to exhibit the best photocatalytic properties reported for the pure system. A great deal of published research by various workers in the field have not fully explained the underlying mechanism for the observed behavior of mixed-phase titania photocatalysts. One of the prevalent hypothesis in the literature that is tested in this work involves the presence of small, active clusters of interwoven anatase and rutile crystallites or “catalytic “hot-spots””. Therefore, non-woven nanofibrous mats of titania were produced and upon calcination the mats consisted of nanostructured fibers with different anatase-rutile ratios. By assessing the photocatalytic and photoelectrochemical properties of these samples the optimized photocatalyst was determined. This consisted of TiO2 nanostructures annealed at 500˚C with an anatase /rutile content of 90/10. Since the performance of this material exceeded that of P25 complete structural characterization was employed to understand the catalytic mechanism involved. It was determined that the dominant factors controlling the photocatalytic behavior of the titania system are the relative particle size of the different phases of titania and the growth of rutile laths on anatase grains which allow for rapid electron transfer between the two phases. This explains how to optimize the response of the pure system.

  9. Lack of awareness among future medical professionals about the risk of consuming hidden phosphate-containing processed food and drinks.

    Directory of Open Access Journals (Sweden)

    Yoshiko Shutto

    Full Text Available Phosphate toxicity is an important determinant of mortality in patients with chronic kidney disease (CKD, particularly those undergoing hemodialysis treatments. CKD patients are advised to take a low phosphate-containing diet, and are additionally prescribed with phosphate-lowering drugs. Since these patients usually seek guidance from their physicians and nurses for their dietary options, we conducted a survey to determine the levels of awareness regarding the high phosphate content in commercially processed food and drinks among medical and nursing students at the Hirosaki University School of Medicine in Japan. For this survey, 190 medical and nursing students (average age 21.7±3 years were randomly selected, and provided with a list of questions aimed at evaluating their awareness of food and drinks containing artificially added phosphate ingredients. While 98.9% of these students were aware of the presence of sugar in commercially available soda drinks, only 6.9% were aware of the presence of phosphate (phosphoric acid. Similarly, only 11.6% of these students were aware of the presence of phosphate in commercially processed food, such as hamburgers and pizza. Moreover, around two thirds of the surveyed students (67.7% were unaware of the harmful effects of unrestricted consumption of phosphate-containing food and drinks. About 28% of the surveyed students consume such "fast food" once a week, while 40% drink at least 1∼5 cans of soda drinks/week. After realizing the potential long-term risks of consuming excessive phosphate-containing food and drinks, 40.5% of the survey participants considered reducing their phosphate intake by minimizing the consumption of commercially processed "fast food" items and soda drinks. Moreover, another 48.4% of students showed interest in obtaining more information on the negative health effects of consuming excessive amounts of phosphate. This survey emphasizes the need for educational initiative to raise

  10. Bi-functional TiO2 cemented Ag grid under layer for enhancing the photovoltaic performance of a large-area dye-sensitized solar cell

    International Nuclear Information System (INIS)

    Lan Zhang; Wu Jihuai; Lin Jianming; Huang, Miaoliang

    2012-01-01

    Graphical abstract: Enhanced photovoltaic performance of large-area DSSC with conductive grids in the photo and counter electrodes. Highlights: ► TiO 2 protected Ag grids is made for using as electrode in large-area DSSC. ► The electrode has high conductivity and low internal resistance. ► TiO 2 protected Ag grids electrode avoids iodine corrosion in electrolyte. ► The TiO 2 layer also play a blocking layer role. ► Above factors enhance the photovoltaic performance of large-area DSSC. - Abstract: A bi-functional TiO 2 cemented Ag grid under layer for enhanced the photovoltaic performance of a large-area dye-sensitized solar cell (DSSC) is prepared with a simple way. The conductive printing paste contains micro-sized Ag powders and nano-sized TiO 2 cementing agent. The conductive printing paste can be well cemented on the FTO glass and form high conductive grids with Ag powders sintered together by the nano-sized TiO 2 particles. The formed conductive grid is protected with a TiO 2 thin layer and TiO 2 sol treatment to avoid the iodine corrosion. The addition of the TiO 2 cemented conductive grid can decrease the internal resistance of the large-area dye-sensitized solar cell when it is prepared in the photo and counter electrodes. Furthermore, the protecting TiO 2 thin layer and the TiO 2 sol treatment can be done on the whole area of the large-area photo electrode to both play as the blocking under layer at the same time, which can also enhance the photovoltaic performance of the large-area dye-sensitized solar cell.

  11. The Electrochemical Properties of Low-crystallinity TiO2(B)-Carbon Composite as an Anode Material in Lithium Ion Battery

    International Nuclear Information System (INIS)

    Furuya, Yasuyuki; Zhao, Wenwen; Unno, Masashi; Noguchi, Hideyuki

    2014-01-01

    Highlights: • TiO 2 (B)-carbon composites was synthesized from Lepidocrocite-type compounds. • Tight adhesion between TiO 2 (B) and CNT in the composite is confirmed. • TiO 2 (B)-carbon composite delivers higher capacity than that of bare TiO 2 (B). • TiO 2 (B)-carbon composite exhibits improved rate performance. - Abstract: We have prepared two types TiO 2 (B)-carbon composites from Lepidocrocite-type compounds (K 0.86 Li 0.26 T i1.72 O 4 ) heated at 700 and 900 °C under presence of carbon nanotube (CNT) and glucose as carbon sources. The XRD data shows that it contains a single phase of TiO 2 (B) and the existence of carbon was confirmed by Raman spectra. TEM image confirms that TiO 2 (B) primary particles and carbon nanotube are scattered randomly and contact tightly in the composite. Carbon content in the composite was found to be 5 - 8% and CNT is the major carbonaceous material. The charge and discharge curves of TiO 2 (B)-carbon composite prepared from precursor heated at 700 °C resemble with that of amorphous TiO 2 . The calculated discharge capacity of the composite is 323 mAh g −1 at a cut off voltage of 0.9 V, which is higher than that of bare TiO 2 (B). It is suggested that the electrochemical performance of this material is strongly influenced by both the operating temperature and cut off voltage. The discharge capacity can reach 198 mAh g −1 at 4.5 C rate at a cut off voltage 1.3 V and the coulombic efficiency is over 99.8% after 10 th cycles

  12. Nano titanium dioxide photocatalytic protein tyrosine nitration: A potential hazard of TiO2 on skin

    International Nuclear Information System (INIS)

    Lu, Naihao; Zhu Zhening; Zhao Xuqi; Tao Ran; Yang Xiangliang; Gao Zhonghong

    2008-01-01

    Protein tyrosine nitration is a prevalent post-translational modification which occurs as a result of oxidative and nitrative stress, it may be directly involved in the onset and/or progression of diseases. Considering the existence of nano titanium dioxide (TiO 2 ) in environment and sunscreen products along with the high content of nitrite in sweat, the UV-exposed skin may be a significant target for the photosensitized damage. In this paper, tyrosine nitration of bovine serum albumin (BSA) was initiated in the UV-irradiated reaction mixture containing 0.2-3.0 mg/ml of three commercially nano TiO 2 products and 0.25-1.0 mM NO 2 - . It was found that anatase TiO 2 and Degussa P25 TiO 2 showed prominent photocatalytic activity on promoting the formation of protein tyrosine nitration, and the optimum condition for the reaction was around physiological pH. Meanwhile, the photocatalytic effect of rutile on protein tyrosine nitration was subtle. The potential physiological significance of nano TiO 2 -photocatalytic protein nitration was also demonstrated in mouse skin homogenate. Although the relationship between photocatalytic protein tyrosine nitration and chronic cutaneous diseases needs further study, the toxicity of nano TiO 2 to the skin disease should be paid more attention in the production and utilization process

  13. Oriented epitaxial TiO2 nanowires for water splitting

    Science.gov (United States)

    Hou, Wenting; Cortez, Pablo; Wuhrer, Richard; Macartney, Sam; Bozhilov, Krassimir N.; Liu, Rong; Sheppard, Leigh R.; Kisailus, David

    2017-06-01

    Highly oriented epitaxial rutile titanium dioxide (TiO2) nanowire arrays have been hydrothermally grown on polycrystalline TiO2 templates with their orientation dependent on the underlying TiO2 grain. Both the diameter and areal density of the nanowires were tuned by controlling the precursor concentration, and the template surface energy and roughness. Nanowire tip sharpness was influenced by precursor solubility and diffusivity. A new secondary ion mass spectrometer technique has been developed to install additional nucleation sites in single crystal TiO2 templates and the effect on nanowire growth was probed. Using the acquired TiO2 nanowire synthesis knowhow, an assortment of nanowire arrays were installed upon the surface of undoped TiO2 photo-electrodes and assessed for their photo-electrochemical water splitting performance. The key result obtained was that the presence of short and dispersed nanowire arrays significantly improved the photocurrent when the illumination intensity was increased from 100 to 200 mW cm-2. This is attributed to the alignment of the homoepitaxially grown nanowires to the [001] direction, which provides the fastest charge transport in TiO2 and an improved pathway for photo-holes to find water molecules and undertake oxidation. This result lays a foundation for achieving efficient water splitting under conditions of concentrated solar illumination.

  14. TiO2 assisted photo-oxidative pretreatment of wheat straw for biogas production

    DEFF Research Database (Denmark)

    Awais, Muhammad; Alvarado-Morales, Merlin; Tsapekos, Panagiotis

    Photo-catalytic oxidation is an advanced oxidation process in which a catalyst is used to absorb light energy and oxidize the target substrates such as organic polymers. A number of metal oxides and metal ions can efficiently increase substrate’s depolymerisation during the process of photo...... to be markedly higher in the pretreated samples that were exposed for 180min with 1.5 wt% and 2 wt% of TiO2 compared to the untreated wheat straw. Moreover, it was concluded that the products of lignin oxidation and also, the presence of TiO2 did not inhibit the AD process. Finally, UV treatment or TiO2 alone......-catalytic oxidation. Titanium oxide (TiO2) is a photo-catalyst that in its rutile and anatase forms presents the property to enhance the photo-oxidation of lignin-containing substrates. Due to lignin is one of the major obstacles in methane production from lignocellulosic biomass, its destruction is a necessary step...

  15. Preparation and spectroscopic characterization of visible light sensitized N doped TiO2 (rutile)

    International Nuclear Information System (INIS)

    Livraghi, S.; Czoska, A.M.; Paganini, M.C.; Giamello, E.

    2009-01-01

    Nitrogen doped TiO 2 represents one of the most promising material for photocatalitic degradation of environmental pollutants with visible light. However, at present, a great deal of activity is devoted to the anatase polymorph while few data about rutile are available. In the present paper we report an experimental characterization of N doped polycrystalline rutile TiO 2 prepared via sol-gel synthesis. Nitrogen doping does not affect the valence band to conduction band separation but, generates intra band gap localized states which are responsible of the on set of visible light absorption. The intra band gap states correspond to a nitrogen containing defect similar but not coincident with that recently reported for N doped anatase. - Graphical abstract: Nitrogen doped TiO 2 represents one of the most promising material for photocatalitic degradation of environmental pollutants with visible light. However, at present, a great deal of activity is devoted to the anatase polymorph while few data about rutile are available. In the present paper we report an experimental characterization of N doped polycrystalline rutile TiO 2 prepared via sol-gel synthesis

  16. Dimensional stability under wet curing of mortars containing high amounts of nitrates and phosphates

    International Nuclear Information System (INIS)

    Benard, P.; Cau Dit Coumes, C.; Garrault, S.; Nonat, A.; Courtois, S.

    2008-01-01

    Investigations were carried out in order to solidify in cement some aqueous streams resulting from nuclear decommissioning processes and characterized by a high salinity (300 g/L), as well as important concentrations of nitrate (150-210 g/L) and phosphate ions (0-50 g/L). Special attention was paid to the influence of these compounds on the dimensional variations under wet curing of simulated solidified waste forms. The length changes of mortars containing nitrate salts only (KNO 3 , NaNO 3 ) were shown to be governed by a concentration effect which involved osmosis: the higher their concentration in the mixing solution, the higher the swelling. The expansion of mortars containing high amounts of phosphates (≥ 30 g/L in the mixing solution) was preceded by a shrinkage which increased with the phosphate concentration, and which could be suppressed by seeding the cement used with hydroxyapatite crystals. This transitory shrinkage was attributed to the conversion into hydroxyapatite of a precursor readily precipitated in the cement paste after mixing

  17. Lead-iron phosphate glass as a containment medium for the disposal of high-level nuclear wastes

    Science.gov (United States)

    Boatner, L.A.; Sales, B.C.

    1984-04-11

    Disclosed are lead-iron phosphate glasses containing a high level of Fe/sub 2/O/sub 3/ for use as a storage medium for high-level radioactive nuclear waste. By combining lead-iron phosphate glass with various types of simulated high-level nuclear waste

  18. Microstructure and corrosion performance of steam-based conversion coatings produced in the presence of TiO2 particles on aluminium alloys

    DEFF Research Database (Denmark)

    Din, Rameez Ud; Gudla, Visweswara Chakravarthy; Jellesen, Morten Stendahl

    2016-01-01

    The steam-based conversion coatings containing TiO2 particleswere prepared using a two-step process comprising of spin coating of particles onto an aluminiumsubstrate followed by a high-pressure steam treatment. Process has resulted in the formation of aluminium oxide layer (~1.3 μm thick) embedded...... to the coatings without TiO2 particles, while the shift in thepitting potential was a function of the steam treatment time and degree of particle incorporation into the oxide....... with TiO2 particles. The electrochemical measurements showthe beneficial effect of TiO2 particles in the oxide layer by exhibiting lowestanodic and cathodic activities, and reduced pit depth. The presence of TiO2 particles shifts the corrosion potentialvalues to positive side (noble side) when compared...

  19. The effect of TiO2 nanocrystal shape on the electrical properties of poly(styrene-b-methyl methacrylate) block copolymer based nanocomposites for solar cell application

    International Nuclear Information System (INIS)

    Cano, Laida; Gutierrez, Junkal; Di Mauro, A. Evelyn; Curri, M. Lucia; Tercjak, Agnieszka

    2015-01-01

    Titanium dioxide (TiO 2 ) nanocrystals were synthesized into two shapes, namely spherical and rod-like and used for the fabrication of polystyrene-block-poly(methyl methacrylate) (PSMMA) block copolymer based nanocomposites, which were employed as the active top layer of electro-devices for solar cell application. Electro-devices were designed using nanocomposites with high TiO 2 nanocrystal contents (50-70 wt%) and for comparison as-synthesized TiO 2 nanospheres (TiO 2 NSs) and TiO 2 nanorods (TiO 2 NRs) were also used. The morphology of the electro-devices was studied by atomic force microscopy showing good nanocrystal dispersion. The electrical properties of the devices were investigated by PeakForce tunneling atomic force microscopy and Keithley semiconductor analyzer, which showed higher electrical current values for devices containing TiO 2 NRs in comparison to TiO 2 NSs. Remarkably, the influence of the PSMMA block copolymer on the improvement of the conductivity of the electro-devices was also assessed, demonstrating that the self-assembling ability of block copolymer can be beneficial to improve charge transfer in the fabricated electro-devices, thus representing relevant systems to be potentially developed for photovoltaic applications. Moreover, the absorbance of the prepared electro-devices in solar irradiation range was confirmed by UV–vis spectroscopy characterization.

  20. Bactericidal effect of blue LED light irradiated TiO2/Fe3O4 particles on fish pathogen in seawater

    International Nuclear Information System (INIS)

    Cheng, T.C.; Yao, K.S.; Yeh, N.; Chang, C.I.; Hsu, H.C.; Gonzalez, F.; Chang, C.Y.

    2011-01-01

    This study uses blue LED light (λ max = 475 nm) activated TiO 2 /Fe 3 O 4 particles to evaluate the particles' photocatalytic activity efficiency and bactericidal effects in seawater of variable salinities. Different TiO 2 to Fe 3 O 4 mole ratios have been synthesized using sol-gel method. The synthesized particles contain mainly anatase TiO 2 , Fe 3 O 4 and FeTiO 3 . The study has identified TiO 2 /Fe 3 O 4 's bactericidal effect to marine fish pathogen (Photobacterium damselae subsp. piscicida BCRC17065) in seawater. The SEM photo reveals the surface destruction in bacteria incubated with blue LED irradiated TiO 2 /Fe 3 O 4 . The result of this study indicates that 1) TiO 2 /Fe 3 O 4 acquires photocatalytic activities in both the freshwater and the seawater via blue LED irradiation, 2) higher photocatalytic activities appear in solutions of higher TiO 2 /Fe 3 O 4 mole ratio, and 3) photocatalytic activity decreases as salinity increases. These results suggest that the energy saving blue LED light is a feasible light source to activate TiO 2 /Fe 3 O 4 photocatalytic activities in both freshwater and seawater.

  1. Analysis of genomic responses in a rat lung model treated with a humidifier sterilizer containing polyhexamethyleneguanidine phosphate.

    Science.gov (United States)

    Kim, Min-Seok; Jeong, Seok Won; Choi, Seong-Jin; Han, Jin-Young; Kim, Sung-Hwan; Yoon, Seokjoo; Oh, Jung-Hwa; Lee, Kyuhong

    2017-02-15

    The antimicrobial biocide polyhexamethyleneguanidine (PHMG) phosphate is the main ingredient in the commercially available humidifier disinfectant. PHMG phosphate-based humidifier disinfectants can cause pulmonary fibrosis and induce inflammatory and fibrotic responses both in vivo and in vitro. However, toxicological mechanisms including genomic alterations induced by inhalation exposure to PHMG phosphate have not been elucidated. Therefore, this study evaluated the toxicological effects of the PHMG phosphate-containing humidifier disinfectant. We used DNA microarray to identify global gene expression changes in rats treated with PHMG phosphate-containing humidifier disinfectant for 4 weeks and 10 weeks. Functional significance of differentially expressed genes (DEGs) was estimated by gene ontology (GO) analysis. Four weeks post-exposure, 320 and 392 DEGs were identified in female and male rats, respectively (>2-fold, pPHMG phosphate exposure. In addition, 21 genes were upregulated and 4 genes were downregulated in response to PHMG phosphate in a time-dependent manner. Thus, we predict that changes in genomic responses could be a significant molecular mechanism underlying PHMG phosphate toxicity. Further studies are required to determine the detailed mechanism of PHMG phosphate-induced pulmonary toxicity. Copyright © 2016. Published by Elsevier B.V.

  2. Short-term in vivo evaluation of zinc-containing calcium phosphate using a normalized procedure

    Energy Technology Data Exchange (ETDEWEB)

    Calasans-Maia, Monica, E-mail: monicacalasansmaia@gmail.com [Dental Clinical Research Center, Dentistry School, Fluminense Federal University, Niteroi, Rio de Janeiro (Brazil); Calasans-Maia, José, E-mail: josecalasans@gmail.com [Dental Clinical Research Center, Dentistry School, Fluminense Federal University, Niteroi, Rio de Janeiro (Brazil); Santos, Silvia, E-mail: silviaquimica@gmail.com [LABIOMAT, Brazilian Center for Physics Research, CBPF, Rio de Janeiro (Brazil); Mavropoulos, Elena, E-mail: elena@cbpf.br [LABIOMAT, Brazilian Center for Physics Research, CBPF, Rio de Janeiro (Brazil); Farina, Marcos, E-mail: mfarina@anato.ufrj.br [Institute of Biomedical Sciences, Federal University of Rio de Janeiro, Rio de Janeiro (Brazil); Lima, Inayá, E-mail: inayacorrea@gmail.com [Nuclear Instrumentation Laboratory, Nuclear Engineering Program, COPPE, Federal University of Rio de Janeiro, Rio de Janeiro (Brazil); Lopes, Ricardo Tadeu [Nuclear Instrumentation Laboratory, Nuclear Engineering Program, COPPE, Federal University of Rio de Janeiro, Rio de Janeiro (Brazil); Rossi, Alexandre, E-mail: rossi@cbpf.br [LABIOMAT, Brazilian Center for Physics Research, CBPF, Rio de Janeiro (Brazil); Granjeiro, José Mauro, E-mail: jmgranjeiro@gmail.com [Dental Clinical Research Center, Dentistry School, Fluminense Federal University, Niteroi, Rio de Janeiro (Brazil); Bioengineering Division, National Institute of Metrology, Quality and Technology, Duque de Caxias, Rio de Janeiro (Brazil)

    2014-08-01

    The effect of zinc-substituted calcium phosphate (CaP) on bone osteogenesis was evaluated using an in vivo normalized ISO 10993-6 protocol. Zinc-containing hydroxyapatite (ZnHA) powder with 0.3% by wt zinc (experimental group) and stoichiometric hydroxyapatite (control group) were shaped into cylindrical implants (2 × 6 mm) and were sintered at 1000 °C. Thermal treatment transformed the ZnHA cylinder into a biphasic implant that was composed of Zn-substituted HA and Zn-substituted β-tricalcium phosphate (ZnHA/βZnTCP); the hydroxyapatite cylinder was a highly crystalline and poorly soluble HA implant. In vivo tests were performed in New Zealand White rabbits by implanting two cylinders of ZnHA/βZnTCP in the left tibia and two cylinders of HA in the right tibia for 7, 14 and 28 days. Incorporation of 0.3% by wt zinc into CaP increased the rate of Zn release to the biological medium. Microfluorescence analyses (μXRF-SR) using synchrotron radiation suggested that some of the Zn released from the biomaterial was incorporated into new bone near the implanted region. In contrast with previous studies, histomorphometric analysis did not show significant differences between the newly formed bone around ZnHA/βZnTCP and HA due to the dissolution profile of Zn-doped CaP. Despite the great potential of Zn-containing CaP matrices for future use in bone regeneration, additional in vivo studies must be conducted to explain the mobility of zinc at the CaP surface and its interactions with a biological medium. - Highlights: • We produced a hydroxyapatite containing a low concentration (0.3 wt.%) of zinc. • The biomaterial underwent characterization before and after in vivo implant. • In vivo tests were performed according to ISO 10993-6. • Zinc-containing calcium phosphate promotes osteoconduction and bone regeneration. • Zinc-containing calcium phosphate may be useful for clinical applications.

  3. Short-term in vivo evaluation of zinc-containing calcium phosphate using a normalized procedure

    International Nuclear Information System (INIS)

    Calasans-Maia, Monica; Calasans-Maia, José; Santos, Silvia; Mavropoulos, Elena; Farina, Marcos; Lima, Inayá; Lopes, Ricardo Tadeu; Rossi, Alexandre; Granjeiro, José Mauro

    2014-01-01

    The effect of zinc-substituted calcium phosphate (CaP) on bone osteogenesis was evaluated using an in vivo normalized ISO 10993-6 protocol. Zinc-containing hydroxyapatite (ZnHA) powder with 0.3% by wt zinc (experimental group) and stoichiometric hydroxyapatite (control group) were shaped into cylindrical implants (2 × 6 mm) and were sintered at 1000 °C. Thermal treatment transformed the ZnHA cylinder into a biphasic implant that was composed of Zn-substituted HA and Zn-substituted β-tricalcium phosphate (ZnHA/βZnTCP); the hydroxyapatite cylinder was a highly crystalline and poorly soluble HA implant. In vivo tests were performed in New Zealand White rabbits by implanting two cylinders of ZnHA/βZnTCP in the left tibia and two cylinders of HA in the right tibia for 7, 14 and 28 days. Incorporation of 0.3% by wt zinc into CaP increased the rate of Zn release to the biological medium. Microfluorescence analyses (μXRF-SR) using synchrotron radiation suggested that some of the Zn released from the biomaterial was incorporated into new bone near the implanted region. In contrast with previous studies, histomorphometric analysis did not show significant differences between the newly formed bone around ZnHA/βZnTCP and HA due to the dissolution profile of Zn-doped CaP. Despite the great potential of Zn-containing CaP matrices for future use in bone regeneration, additional in vivo studies must be conducted to explain the mobility of zinc at the CaP surface and its interactions with a biological medium. - Highlights: • We produced a hydroxyapatite containing a low concentration (0.3 wt.%) of zinc. • The biomaterial underwent characterization before and after in vivo implant. • In vivo tests were performed according to ISO 10993-6. • Zinc-containing calcium phosphate promotes osteoconduction and bone regeneration. • Zinc-containing calcium phosphate may be useful for clinical applications

  4. Bare TiO2 and graphene oxide TiO2 photocatalysts on the degradation of selected pesticides and influence of the water matrix

    Science.gov (United States)

    Cruz, Marta; Gomez, Cristina; Duran-Valle, Carlos J.; Pastrana-Martínez, Luisa M.; Faria, Joaquim L.; Silva, Adrián M. T.; Faraldos, Marisol; Bahamonde, Ana

    2017-09-01

    The photocatalytic activity of a home-made titanium dioxide (TiO2) and its corresponding composite based on graphene oxide (GO), the GO-TiO2 catalyst, has been investigated under UV-vis in the photodegradation of a mixture of four pesticides classified by the European Union as priority pollutants: diuron, alachlor, isoproturon and atrazine. The influence of two water matrices (ultrapure or natural water) was also studied. Natural water led to a decrease on the degradation of the studied pollutants when the bare TiO2 photocatalyst was employed, since this water contains both inorganic and organic species that are dissolved and commonly restrain the photocatalytic process. On the contrary, the photo-efficiency of the GO-TiO2 composite seems to be less affected by water matrix variation, with very good initial pesticide photodegradation rates under both natural and ultrapure water matrices. A comparative study between GO-TiO2 and the commercial Evonik TiO2 P25 catalyst was also carried out to analyze the photocatalytic degradation of these pesticides under visible light illumination conditions. Once again, a higher photocatalytic activity was found for the GO-TiO2 composite.

  5. Solution-Processed Ultrathin TiO2 Compact Layer Hybridized with Mesoporous TiO2 for High-Performance Perovskite Solar Cells.

    Science.gov (United States)

    Jeong, Inyoung; Park, Yun Hee; Bae, Seunghwan; Park, Minwoo; Jeong, Hansol; Lee, Phillip; Ko, Min Jae

    2017-10-25

    The electron transport layer (ETL) is a key component of perovskite solar cells (PSCs) and must provide efficient electron extraction and collection while minimizing the charge recombination at interfaces in order to ensure high performance. Conventional bilayered TiO 2 ETLs fabricated by depositing compact TiO 2 (c-TiO 2 ) and mesoporous TiO 2 (mp-TiO 2 ) in sequence exhibit resistive losses due to the contact resistance at the c-TiO 2 /mp-TiO 2 interface and the series resistance arising from the intrinsically low conductivity of TiO 2 . Herein, to minimize such resistive losses, we developed a novel ETL consisting of an ultrathin c-TiO 2 layer hybridized with mp-TiO 2 , which is fabricated by performing one-step spin-coating of a mp-TiO 2 solution containing a small amount of titanium diisopropoxide bis(acetylacetonate) (TAA). By using electron microscopies and elemental mapping analysis, we establish that the optimal concentration of TAA produces an ultrathin blocking layer with a thickness of ∼3 nm and ensures that the mp-TiO 2 layer has a suitable porosity for efficient perovskite infiltration. We compare PSCs based on mesoscopic ETLs with and without compact layers to determine the role of the hole-blocking layer in their performances. The hybrid ETLs exhibit enhanced electron extraction and reduced charge recombination, resulting in better photovoltaic performances and reduced hysteresis of PSCs compared to those with conventional bilayered ETLs.

  6. Influence of silver on photocatalytic activity of TiO2

    International Nuclear Information System (INIS)

    Kisen, Carla Yuri; Teodoro, Vinicius; Zaghete, Maria Ap.; Perazolli, Leinig Antonio; Longo, Elson

    2016-01-01

    Full text: This work studied the influence of silver on photo activity of TiO 2 , prepared by Pechini method, in the photodegradation of Rhodamine-B. The catalysts were prepared with different percentage of silver (0.0, 0.5 and 1.0 %) and different calcination temperatures (500, 600 and 700°C), characterized by X-ray diffraction (DRX) and field emission gun - scanning electron microscopy (FEG-SEM), The powders' photo catalytic activity was defined by Rhodamine-B decolorisation test. The solution containing the dye and the catalyst, in the concentration of 0,01 mmol L -1 e 1,0 g L -1 respectively, were submitted to radiation with 9W germicidal lamp for 120 minutes. The control samples, for comparison effects, were made with TiO 2 anatase (Synth brand) and photolysis tests. In the micrographs, obtained by SEM, all the temperatures and compositions employed presented similar morphologies, it is assumed the calcination temperature rise leads to a decreased apparent porosity and the generation of particles clusters. The X-ray diffractograms indicates the calcination temperature influence in the generation of distinct TiO 2 phases during the catalysts synthesis. Regardless of the TiO 2 proportions, the only actual phase with 500°C calcination is the anatase. At 600°C, the rutile phase coexisting with the anatase phase disappears, and the rutile phase predominates. Among the catalysts, what presented greater activity was the TiO 2 with 0.5% Ag and calcination temperature of 500°C, which degraded around 100% in 60 minutes. References: [1] P. Cozolli, E. Fanizza and A. Agostiano. J. Phys.Chem. B108, 9623-9630, 2004. (author)

  7. Development of phosphate glass microspheres containing holmium for selective internal radiotherapy

    International Nuclear Information System (INIS)

    Barros Filho, Eraldo Cordeiro

    2016-01-01

    The selective internal radiotherapy is an alternative for some kinds of cancer as the hepatocellular carcinoma (HCC) or primary liver cancer treatment. In this treatment, glass or polymer microspheres containing radionuclides inside their structure are introduced in the liver through hepatic artery and trapped at the arterioles that feed the tumor. In this work, the development of phosphate glasses containing holmium for production of microspheres and their application in Brazil are proposed. The developed glasses presented suitable chemical durability, density of 2,7(3) g/cm 3 , high thermal stability and the impurities contained therein do not preclude the treatment. The microspheres were produced by the flame method and the gravitational fall method, and were characterized by means of several techniques to evaluate shape, average particle size, activity and biocompatibility suitable for selective internal radiotherapy. Based in the main results, the submission to in vivo tests is proposed. (author)

  8. Fabrication and Characteristics of Macroporous TiO2 Photocatalyst

    Directory of Open Access Journals (Sweden)

    Guiyun Yi

    2014-01-01

    Full Text Available Macroporous TiO2 photocatalyst was synthesized by a facile nanocasting method using polystyrene (PS spherical particles as the hard template. The synthesized photocatalyst was characterized by transmission electron microscope (TEM, scanning electron microscopy (SEM, thermogravimetry-differential thermogravimetry (TG-DTG, X-ray diffraction (XRD, and N2-sorption. TEM, SEM, and XRD characterizations confirmed that the macroporous TiO2 photocatalyst is composed of anatase phase. The high specific surface area of 87.85 m2/g can be achieved according to the N2-sorption analysis. Rhodamine B (RhB was chosen as probe molecule to evaluate the photocatalytic activity of the TiO2 catalysts. Compared with the TiO2 materials synthesized in the absence of PS spherical template, the macroporous TiO2 photocatalyst sintered at 500°C exhibits much higher activity on the degradation of RhB under the UV irradiation, which can be assigned to the well-structured macroporosity. The macroporous TiO2 material presents great potential in the fields of environmental remediation and energy conversion and storage.

  9. High pressure synthesis of amorphous TiO2 nanotubes

    Directory of Open Access Journals (Sweden)

    Quanjun Li

    2015-09-01

    Full Text Available Amorphous TiO2 nanotubes with diameters of 8-10 nm and length of several nanometers were synthesized by high pressure treatment of anatase TiO2 nanotubes. The structural phase transitions of anatase TiO2 nanotubes were investigated by using in-situ high-pressure synchrotron X-ray diffraction (XRD method. The starting anatase structure is stable up to ∼20GPa, and transforms into a high-density amorphous (HDA form at higher pressure. Pressure-modified high- to low-density transition was observed in the amorphous form upon decompression. The pressure-induced amorphization and polyamorphism are in good agreement with the previous results in ultrafine TiO2 nanoparticles and nanoribbons. The relationship between the LDA form and α-PbO2 phase was revealed by high-resolution transmission electron microscopy (HRTEM study. In addition, the bulk modulus (B0 = 158 GPa of the anatase TiO2 nanotubes is smaller than those of the corresponding bulks and nanoparticles (180-240 GPa. We suggest that the unique open-ended nanotube morphology and nanosize play important roles in the high pressure phase transition of TiO2 nanotubes.

  10. Taking a fresh look at optical crowding of TiO2: the role of nanocarbonate as synergistic optical extender

    Science.gov (United States)

    Ridgway, Cathy J.; Gane, Patrick A. C.

    2013-10-01

    The light scattering potential of titanium dioxide (TiO2) is maximized when the TiO2 particles are correctly spaced in relation to the size of the particles, their spacing distance and the refractive index contrast with the surrounding medium. Nanoparticle extenders are claimed to improve TiO2 spacing due to the small particles acting to separate larger TiO2 particles (void size in respect to the separation of the surfaces ˜0.2 µm) and so preventing the TiO2 particles from reaching optical crowding. This concept has been challenged by previous work (Diebold 2011 J. Coat. Technol. Res. 8 541-52) using a combination of Monte Carlo simulations and image analysis techniques. Surprisingly in the light of traditional interpretations, the results showed that nanoparticles did not, in fact, space TiO2 particles under any conditions examined. Instead, TiO2 distributions and spacings were completely indifferent to the presence of smaller particles. This current paper undertakes to study why in certain cases extenders do in fact deliver significant synergy allowing TiO2 levels to be reduced in practice. The use of nano-calcium carbonate is demonstrated to provide a wide range of synergistic extension of TiO2 when in combination with synthetic latex binder, but, as found in the previous theoretical work, only a limited synergistic range in direct pigment packing studies using slurry pigment mixes only. A schematic model of the action of calcium carbonate containing a high nanoparticle fraction in the presence of binder is proposed, and is related to a combination of the potential reduction of contact between latex and TiO2 related to an increase in effective pigment volume fraction and surface area as well as the potential for differential flocculation. This model is supported by electron microscopy images and a measure of the ‘hardness’ of the skeletal elements making up the coating structure, determined via the bulk modulus using mercury intrusion porosimetry, enabling

  11. Taking a fresh look at optical crowding of TiO2: the role of nanocarbonate as synergistic optical extender

    International Nuclear Information System (INIS)

    Ridgway, Cathy J; Gane, Patrick A C

    2013-01-01

    The light scattering potential of titanium dioxide (TiO 2 ) is maximized when the TiO 2 particles are correctly spaced in relation to the size of the particles, their spacing distance and the refractive index contrast with the surrounding medium. Nanoparticle extenders are claimed to improve TiO 2 spacing due to the small particles acting to separate larger TiO 2 particles (void size in respect to the separation of the surfaces ∼0.2 µm) and so preventing the TiO 2 particles from reaching optical crowding. This concept has been challenged by previous work (Diebold 2011 J. Coat. Technol. Res. 8 541–52) using a combination of Monte Carlo simulations and image analysis techniques. Surprisingly in the light of traditional interpretations, the results showed that nanoparticles did not, in fact, space TiO 2 particles under any conditions examined. Instead, TiO 2 distributions and spacings were completely indifferent to the presence of smaller particles. This current paper undertakes to study why in certain cases extenders do in fact deliver significant synergy allowing TiO 2 levels to be reduced in practice. The use of nano-calcium carbonate is demonstrated to provide a wide range of synergistic extension of TiO 2 when in combination with synthetic latex binder, but, as found in the previous theoretical work, only a limited synergistic range in direct pigment packing studies using slurry pigment mixes only. A schematic model of the action of calcium carbonate containing a high nanoparticle fraction in the presence of binder is proposed, and is related to a combination of the potential reduction of contact between latex and TiO 2 related to an increase in effective pigment volume fraction and surface area as well as the potential for differential flocculation. This model is supported by electron microscopy images and a measure of the ‘hardness’ of the skeletal elements making up the coating structure, determined via the bulk modulus using mercury intrusion

  12. Data on the effect of improved TiO2/FTO interface and Ni(OH)2 cocatalyst on the photoelectrochemical performances and stability of CdS cased ZnIn2S4/TiO2 heterojunction.

    Science.gov (United States)

    Mahadik, Mahadeo A; Shinde, Pravin S; Lee, Hyun Hwi; Cho, Min; Jang, Jum Suk

    2018-04-01

    This data article presents the experimental evidences of the effect of TiO 2 -fluorine doped tin oxide interface annealing and Ni(OH) 2 cocatalysts on the photoelectrochemical, structural, morphological and optical properties of Ni(OH) 2 /CdS/ZnIn 2 S 4 /TiO 2 heterojunction. The Raman spectroscopy exhibits the sharp features of the rutile phase of TiO 2 and in agreement with the X-ray diffraction data. The band gap energy of the 500 °C sample was found to be 3.12 eV, further it was increased to 3.20, 3.22 eV for samples annealed at 600 and 700 °C respectively. The decrease in the band gap energy at 500 °C related to the oxygen vacancies and was analysed by photoluminescence spectroscopy analysis. The synthesis, characterization methods and other experimental details of TiO 2 based heterostructure are also provided. The presence of CdS and ZnIn 2 S 4 coating on surface of TiO 2 electrodes providing a high surface area, extended visible absorption and helps to improve the change separation. This data article contains data related to the research article entitled "Highly efficient and stable 3D Ni(OH) 2 /CdS/ZnIn 2 S 4 /TiO 2 heterojunction under solar light: Effect of an improved TiO 2 /FTO interface and cocatalyst" (Mahadik et al., 2017) [1].

  13. TiO2-ITO and TiO2-ZnO nanocomposites: application on water treatment

    Directory of Open Access Journals (Sweden)

    Bessais B.

    2012-06-01

    Full Text Available One of the most promising ideas to enhance the photocatalytic efficiency of the TiO2 is to couple this photocatalyst with other semiconductors. In this work, we report on the development of photo-catalytic properties of two types of composites based on TiO2 – ITO (Indium Tin Oxide and TiO2 – ZnO deposited on conventional ceramic substrates. The samples were characterized by X-ray diffraction (XRD and transmission Electron Microscopy (TEM. The photo-catalytic test was carried out under UV light in order to reduce/oxidize a typical textile dye (Cibacron Yellow. The experiment was carried out in a bench scale reactor using a solution having a known initial dye concentration. After optimization, we found that both nanocomposites exhibit better photocatalytic activity compared to the standard photocatalyst P25 TiO2.

  14. Comparison Study on the Microstructure of Nanocrystalline TiO2 in Different Ti-Si Binary Oxides

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    Three different Ti-Si oxide structuares, silica supported titania, silica coated titania and intimately mixed silicatitania, containing 10%-40% SiO2, were made by sol-gel process. The variations of microstructure parameters of nanocrystalline (nc) TiO2-anatase in the three kirds of binary oxides, including in-plane spacing d, cell constants (a0, CQ), cell volume V, cell axial ratio c0/a0 and crystal grain size, were comparatively investigated by high resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD). It is found that the microstructure parameters vary remarkably with increasing SiO2 content and annealing temperature. Different structured Ti-Si binary oxides lead to different variation tendencies of microstructure parameters. The more SiO2 the binary oxide contains, the more lattice defects of nc TiO2-anatase appear; diffusion or migration of Si cations could be an important influential factor in the variations of microstructure. The grain size of nc TiO2 in the three kinds of binary oxides not only depends on SiO2 content and annealing temperature but also on the degree of lattice microstrain and distortion of nc TiO2-anatase. Both grain size and phase transformation of nc TiO2-anatase are effectively inhibited with increasing SiOa content.

  15. The efficiency of child formula dentifrices containing different calcium and phosphate compounds on artificial enamel caries.

    Science.gov (United States)

    Rirattanapong, Praphasri; Vongsavan, Kadkao; Saengsirinavin, Chavengkiat; Khumsub, Ploychompoo

    2016-01-01

    Fluoride toothpaste has been extensively used to prevent dental caries. However, the risk of fluorosis is concerning, especially in young children. Calcium phosphate has been an effective remineralizing agent and is present in commercial dental products, with no risk of fluorosis to users. This in vitro study aimed to compare the effects of different calcium phosphate compounds and fluoride-containing dentifrices on artificial caries in primary teeth. Fifty sound primary incisors were coated with nail varnish, leaving two 1 mm 2 windows on the labial surface before immersion in demineralizing solution for 96 hours to produce artificial enamel lesions. Subsequently, one window from each tooth was coated with nail varnish, and all 50 teeth were divided into five groups ( n = 10); group A - deionized water; group B - casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste (Tooth Mousse); group C - 500 ppm F (Colgate Spiderman ® ); group D - nonfluoridated toothpaste with triple calcium phosphate (Pureen ® ); and group E - tricalcium phosphate (TCP). Polarized light microscopy and Image-Pro ® Plus software were used to evaluate lesions. After a 7-day pH-cycle, mean lesion depths in groups A, B, C, D, and E had increased by 57.52 ± 10.66%, 33.28 ± 10.16%, 17.04 ± 4.76%, 32.51 ± 8.99%, and 21.76 ± 8.15%, respectively. All data were processed by the Statistical Package for the Social Sciences (version 16.0) software package. Comparison of percentage changes using one-way analysis of variance and Fisher's least squares difference tests at a 95% level of confidence demonstrated that group A was significantly different from the other groups ( P < 0.001). Lesions in groups B and D had a significant lesion progression when compared with groups C and E. All toothpastes in this study had the potential to delay the demineralization progression of artificial enamel caries in primary teeth. The fluoride 500 ppm and TCP toothpastes were equal in the deceleration of

  16. Structure-solubility relationships in fluoride-containing phosphate based bioactive glasses

    Science.gov (United States)

    Shaharyar, Yaqoot

    The dissolution of fluoride-containing bioactive glasses critically affects their biomedical applications. Most commercial fluoride-releasing bioactive glasses have been designed in the soda-lime-silica system. However, their relatively slow chemical dissolution and the adverse effect of fluoride on their bioactivity are stimulating the study of novel biodegradable materials with higher bioactivity, such as biodegradable phosphate-based bioactive glasses, which can be a viable alternative for applications where a fast release of active ions is sought. In order to design new biomaterials with controlled degradability and high bioactivity, it is essential to understand the connection between chemical composition, molecular structure, and solubility in physiological fluids.Accordingly, in this work we have combined the strengths of various experimental techniques with Molecular Dynamics (MD) simulations, to elucidate the impact of fluoride ions on the structure and chemical dissolution of bioactive phosphate glasses in the system: 10Na2O - (45-x) CaO - 45P2O5 - xCaF2, where x varies between 0 -- 10 mol.%. NMR and MD data reveal that the medium-range atomic-scale structure of thse glasses is dominated by Q2 phosphate units followed by Q1 units, and the MD simulations further show that fluoride tends to associate with network modifier cations to form alkali/alkaline-earth rich ionic aggregates. On a macroscopic scale, we find that incorporating fluoride in phosphate glasses does not affect the rate of apatite formation on the glass surface in simulated body fluid (SBF). However, fluoride has a marked favorable impact on the glass dissolution in deionized water. Similarly, fluoride incorporation in the glasses results in significant weight gain due to adsorption of water (in the form of OH ions). These macroscopic trends are discussed on the basis of the F effect on the atomistic structure of the glasses, such as the F-induced phosphate network re-polymerization, in a

  17. Simultaneous removal and recovery of uranium from aqueous solution using TiO_2 photoelectrochemical reduction method

    International Nuclear Information System (INIS)

    Huichao He; Meirong Zong; Faqin Dong; Southwest University of Science and Technology, Sichuan; Pengpan Yang; Gaili Ke; Mingxue Liu; Xiaoqin Nie; Wei Ren; Liang Bian; Southwest University of Science and Technology, Sichuan; Chinese Academy of Sciences, Xinjiang

    2017-01-01

    U(VI)-containing wastewater has potential radiation hazard to the environment, but contains valuable uranium resource. Based on the reduction of U(VI) and the difference in solubility between U(VI) and U(IV), here we construct a TiO_2-based photoelectrochemical cell to remove U(VI) and recover uranium from aqueous solution. By irradiating TiO_2 photoanode at E = 0.45 V versus SCE, U(VI) can be simultaneously removed from aqueous solution and recovered as solid uranium compounds on a FTO glass cathode. Since ethanol can act as hole scavenger to protect the formed U(IV) and provide CO_2"−"· as reductant, ethanol adding improved the U(VI) reduction efficiency of TiO_2-based photoelectrochemical cell. (author)

  18. Synthesis of biphasic calcium phosphate containing nanostructured films by micro arc oxidation on magnesium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Seyfoori, A., E-mail: klm.1985@yahoo.com [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, 16846-13114 Tehran (Iran, Islamic Republic of); National Cell Bank, Pasteur Institute of Iran, 13164 Tehran (Iran, Islamic Republic of); Mirdamadi, Sh.; Seyedraoufi, Z.S.; Khavandi, A. [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, 16846-13114 Tehran (Iran, Islamic Republic of); Aliofkhazraei, M. [Department of Materials Engineering, Faculty of Engineering, Tarbiat Modares University, 14115-143 Tehran (Iran, Islamic Republic of)

    2013-10-01

    The present research reports the synthesis of an innovative nanostructured composite film containing biphasic calcium phosphate (BCP) by the micro arc oxidation (MAO) method on AZ31 magnesium alloy. Nanometric structure of the used hydroxyapatite powder and the coatings were characterized by means of transmission and field-emission scanning electron microscope, respectively. Electrochemical behaviors of the pure MAO and nanocomposite films were also evaluated by electrochemical impedance spectroscopy and potentiodynamic polarization tests in simulated body fluid (SBF) environment. The results showed higher corrosion resistance of nanocomposite film compared to pure MAO coating, which was related to the blocking feature of the nanoparticles from the diffusing of the corrosive medium through the substrate. In addition, by immersing the specimens in simulated body fluid, greater apatite forming ability of the nanocomposite coating was proved. - Highlights: • Synthesis of innovative biphasic calcium phosphate containing nanostructured films via micro arc oxidation. • Nanocomposite film has lower degradation rate than pure MAO film. • Greater apatite forming ability for nanocomposite coating compared with pure MAO film is obtained.

  19. Synthesis of biphasic calcium phosphate containing nanostructured films by micro arc oxidation on magnesium alloy

    International Nuclear Information System (INIS)

    Seyfoori, A.; Mirdamadi, Sh.; Seyedraoufi, Z.S.; Khavandi, A.; Aliofkhazraei, M.

    2013-01-01

    The present research reports the synthesis of an innovative nanostructured composite film containing biphasic calcium phosphate (BCP) by the micro arc oxidation (MAO) method on AZ31 magnesium alloy. Nanometric structure of the used hydroxyapatite powder and the coatings were characterized by means of transmission and field-emission scanning electron microscope, respectively. Electrochemical behaviors of the pure MAO and nanocomposite films were also evaluated by electrochemical impedance spectroscopy and potentiodynamic polarization tests in simulated body fluid (SBF) environment. The results showed higher corrosion resistance of nanocomposite film compared to pure MAO coating, which was related to the blocking feature of the nanoparticles from the diffusing of the corrosive medium through the substrate. In addition, by immersing the specimens in simulated body fluid, greater apatite forming ability of the nanocomposite coating was proved. - Highlights: • Synthesis of innovative biphasic calcium phosphate containing nanostructured films via micro arc oxidation. • Nanocomposite film has lower degradation rate than pure MAO film. • Greater apatite forming ability for nanocomposite coating compared with pure MAO film is obtained

  20. Preparation and characterization of a novel injectable strontium-containing calcium phosphate cement with collagen

    Directory of Open Access Journals (Sweden)

    Zhou Ziqiang

    2015-07-01

    Full Text Available Purpose: To develop a novel injectable strontium-containing calcium phosphate cement with collagen. Methods: A novel calcium phosphate bone cement (CPC was prepared with the addition of strontium element, collagenⅠ, and modified starch; the injectability, solidification time, microstructure, phase composition, compressive strength, anti-collapsibility and histological properties of material were evaluated. Results: The results showed that the material could be injected with an excellent performance; the modified starch significantly improved the anti-washout property of cement; with the liquid to solid ratio of 0.3, the largest compressive strength of cement was obtained (48.0 MPa ± 2.3 MPa; histological examination of repair tissue showed that the bone was repaired after 16 weeks; the degradation of cement was consistent with the new bone growth. Conclusion: A novel injectable collagen-strontium-containing CPC with excellent compressive strength and suitable setting time was prepared, with addition of modified starch. The CPC showed a good antiwashout property and the degradation time of the cement met with the new bone growing. This material is supposed to be used in orthopedic and maxillofacial surgery for bone defects.

  1. Labile Zn ions on octacalcium phosphate-derived Zn-containing hydroxyapatite surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Honda, Yoshitomo; Anada, Takahisa; Morimoto, Shinji [Division of Craniofacial Function Engineering (CFE), Tohoku University Graduate School of Dentistry, Sendai (Japan); Suzuki, Osamu, E-mail: suzuki-o@m.tohoku.ac.jp [Division of Craniofacial Function Engineering (CFE), Tohoku University Graduate School of Dentistry, Sendai (Japan)

    2013-05-15

    We previously synthesized and characterized zinc-containing octacalcium phosphate (OCP) and its hydrolyzed Ca-deficient hydroxyapatite (HA). In the present report, we attempted to define the state of Zn in the OCP-derived Zn-calcium phosphates (CaPs) in relation to the presence of specific amino acids. Zn-containing OCPs were prepared in solutions that included Zn ions up to a concentration of 3.5 mM, and their hydrolyzates [hydrolyzed (hy)-Zn-CaP] were obtained in hot water. The materials were characterized by x-ray diffraction and scanning electron microscopy. The concentration of Ca and Zn ions at room temperature was determined by analyzing the supernatant after incubating the materials in α-minimal essential medium (α-MEM) and HEPES buffer including cysteine, histidine, lysine, aspartic acid, and glutamic acid. Zn ions were more dissolved in α-MEM than HEPES buffer in the absence of amino acids. The inclusion of the amino acids enhanced Zn dissolution by several hundred fold, even in HEPES buffer. Among the amino acids, both cysteine and histidine enhanced the release of Zn. The effect was particularly remarkable with cysteine even in the presence of the other amino acids tested. These results indicate that Zn ions are present as a surface labile pool, which tends to be preferentially desorbed by cysteine, a ubiquitous molecule present in serum.

  2. Photoelectrochemical Performances and Potential Applications of TiO2 Nanotube Arrays Modified with Ag and Pt Nanoparticles

    International Nuclear Information System (INIS)

    Xu, Guangqing; Liu, Haipeng; Wang, Jinwen; Lv, Jun; Zheng, Zhixiang; Wu, Yucheng

    2014-01-01

    TiO 2 nanotube arrays (NTAs) modified with Ag (Ag/TiO 2 ) and Pt (Pt/TiO 2 ) nanoparticles were fabricated by anodic oxidation combined with photoreduction and hydrothermal methods, respectively. Structures, element components and morphologies of TiO 2 , Ag/TiO 2 and Pt/TiO 2 NTAs were measured by X-ray diffraction diffractometer, X-ray photoelectron spectroscopy, scanning electron microscope and transmission electron microscope. The photoeletrochemical performances of TiO 2 , Pt/TiO 2 and Ag/TiO 2 NTAs were characterized by cyclic voltammetry and amperometry in phosphate buffer solution in absence and presence of glucose. Modifications of Ag and Pt nanoparticles play different roles in the photoelectrochemical process and have different potential applications. Ag nanoparticles decrease the photocurrent in buffer solution but increase the photocurrent response to organic compounds, which is fit for electrochemical detection of organic compounds due to the low background photocurrent and high photocurrent response. Ag/TiO 2 NTAs achieve the best detection performance with sensitivity of 0.152 μA/μM and detection limit of 0.53 μM. On the contrary, Pt nanoparticles can enhance the photocurrent of TiO 2 NTAs in buffer solution but decrease the photocurrent response to organic compounds, which are benefit for photocatalytic water splitting but not for photoelectrochemical detection

  3. Electrochemiluminescent pH sensor measured by the emission potential of TiO2 nanocrystals and its biosensing application.

    Science.gov (United States)

    Liu, Xuan; Wang, Nianyue; Zhao, Wei; Jiang, Hui

    2015-02-01

    This work reports for the first time a potential-based nano-electrochemiluminescent (ECL) pH sensor, using anatase TiO2 nanocrystals (NCs) as the ECL probe. The first ECL peak potential of the TiO2 NCs shifted negatively with increasing pH, showing a linear range from -0.47 V (vs Ag/AgCl) at pH 3 to -1.06 V at pH 10. This phenomenon was attributed to the absorption of 'potential-determining ions' of OH(-) on the surface of TiO2 NCs, leading to larger impedance of the electron injection. Other common 'potential-determining ions', such as phosphate, induced a slight potential shift of 0.03 V at a concentration of 0.1 M. Using urease as an enzyme model, a urea biosensor was developed by the simultaneous modification of urease and TiO2 NCs on indium-tin oxide (ITO) electrodes. The biosensor, measured on the basis of the pH increase caused by the enzyme catalysis reaction, had a linear range of 0.01-2.0 mM, with a potential shift of 0.175 V. The as-prepared pH sensor, which has simple construction procedures and acceptable sensitivity and selectivity, may provide new avenues for the construction of ECL bioanalytical methodologies. Copyright © 2014 John Wiley & Sons, Ltd.

  4. ??????????? ??????????????? ????? ??????-???????? ????????????? ?????????? ??????? ?aO?Al2O3?TiO2 ??? ???????? ?????? ?????

    OpenAIRE

    ???????, ????; ??????, ?????????

    2011-01-01

    ? ????? ?????? ?????????? ???????? ?????????????? ??????????? ????????????? ??? ??????-????????? ???????????????? ?????????? ??????? ?aO?Al2O3?TiO2, ?? ???????? ??????? ? ???????????? ??????? ??? ???????? ? ?????? ????????? ?????? ?????. ???????? ?????????? ???????? ??? ??????????? ?????????? ??????? ????????? ???????????? ?????????? ??? ??????????? 12000?, ?? ????????? ?????????????? ????????????? ???????, ????????? ???? ? ?????????? ????? ???????? ??????? ???????????. ????????, ?? ?? ...

  5. Biocorrosion of TiO2 nanoparticle coating of Ti–6Al–4V in DMEM under specific in vitro conditions

    International Nuclear Information System (INIS)

    Höhn, Sarah; Virtanen, Sannakaisa

    2015-01-01

    Highlights: • Possibility to fabricate a TiO 2 NP-coating on Ti–6Al–4V by a simple spin-coating method. • The NP-coating enhances biomimetic apatite formation on the surface immersed in DMEM. • The TiO 2 coating can efficiently reduce Al release from the alloy during immersion in DMEM. • TiO 2 NP-coating makes the surface more bioactive. - Abstract: A TiO 2 nanoparticle coating was prepared on a biomedical Ti–6Al–4V alloy using “spin-coating” technique with a colloidal suspension of TiO 2 nanopowders with the aim to optimize the surface morphology (e.g., roughness) for improved biocompatibility. The influence of a TiO 2 nanoparticle (NP) coating on the corrosion behavior, metal ion release, and biomimetic apatite formation was studied in DMEM, at 37.5 °C with a continuous supply of 5% CO 2 . Electrochemical impedance spectroscopy measurements indicate a formation of a new layer on the surface of the NP-coated sample upon 28 days immersion in DMEM. Scanning electron microscopy (SEM) and X-ray spectroscopy confirm that the surface of the NP-coated Ti–6Al–4V shows a complete coverage by a Ca–phosphate layer in contrast to the non-coated Ti–6Al–4V alloy. Hence, the TiO 2 -NP coating strongly enhances biomimetic apatite formation on the alloy surface. In addition, the TiO 2 -NP coating can efficiently reduce Al-release from the alloy, for which the bare Ti–6Al–4V alloy is significant for at least 28 days of immersion in DMEM

  6. Mechanical characterization and ion release of bioactive dental composites containing calcium phosphate particles.

    Science.gov (United States)

    Natale, Livia C; Rodrigues, Marcela C; Alania, Yvette; Chiari, Marina D S; Boaro, Leticia C C; Cotrim, Marycel; Vega, Oscar; Braga, Roberto R

    2018-08-01

    to verify the effect of the addition of dicalcium phosphate dihydrate (DCPD) particles functionalized with di- or triethylene glycol dimethacrylate (DEGDMA or TEGDMA) on the degree of conversion (DC), post-gel shrinkage (PS), mechanical properties, and ion release of experimental composites. Four composites were prepared containing a BisGMA/TEGDMA matrix and 60 vol% of fillers. The positive control contained only barium glass fillers, while in the other composites 15 vol% of the barium was replaced by DCPD. Besides the functionalized particles, non-functionalized DCPD was also tested. DC after 24 h (n = 3) was determined by FTIR spectroscopy. The strain gage method was used to obtain PS 5 min after photoactivation (n = 5). Flexural strength and modulus (n = 10) were calculated based on the biaxial flexural test results, after specimen storage for 24 h or 60 days in water. The same storage times were used for fracture toughness testing (FT, n = 10). Calcium and phosphate release up to 60 days was quantified by ICP-OES (n = 3). Data were analyzed by ANOVA/Tukey test (alpha: 5%). Composites containing functionalized DCPD presented higher DC than the control (p composites (p composite with DEGDMA-functionalized DCPD presented fracture strength similar to the control, while for flexural modulus only the composite with TEGDMA-functionalized particles was lower than the control (p composites containing DCPD was higher than the control after 60 days (p composite with non-functionalized DCPD at 15 days and no significant reductions were observed for composites with functionalized DCPD during the observation period (p composites, phosphate release was higher at 15 days than in the subsequent periods, and no difference among them was recorded at 45 and 60 days (p composite with DEGDMA-functionalized particles was the only material with strength similar to the control after 60 days in water; however, it also presented the highest

  7. Synthesis and characterization of Ag-containing calcium phosphates with various Ca/P ratios

    Energy Technology Data Exchange (ETDEWEB)

    Gokcekaya, Ozkan, E-mail: gokcekaya@dc.tohoku.ac.jp [Department of Materials Processing, Tohoku University, 6-6-02 Aza Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan); Ueda, Kyosuke; Narushima, Takayuki [Department of Materials Processing, Tohoku University, 6-6-02 Aza Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan); Ergun, Celaletdin [Faculty of Mechanical Engineering, Istanbul Technical University, 65 Inonu Street, Gumussuyu, Istanbul 34437 (Turkey)

    2015-08-01

    Ag-containing calcium phosphate (CaP) powders were synthesized by a precipitation method using aqueous solutions of calcium nitrate, silver nitrate, and ammonium phosphate. The powders were sintered at temperatures ranging from 1173 to 1473 K. The charged atomic ratios of (Ca + Ag)/P and Ag/(Ca + Ag) in solution were varied from 1.33 to 1.67 and from 0 to 0.30, respectively. The Ag content in the as-precipitated CaP powders increased with the charged Ag/(Ca + Ag) atomic ratio in solution and was lower than the charged Ag/(Ca + Ag) value. The as-precipitated CaP powders consisted of hydroxyapatite (HA) as the main phase. Ag nanoparticles were observed on the as-precipitated HA particles under all conditions of Ag addition. After the sintering, HA, β-TCP (tricalcium phosphate), α-TCP, and β-CPP (calcium pyrophosphate) were mainly detected as CaPs on the basis of the Ca/P atomic ratio of the as-precipitated powders. The addition of Ag stabilized the β-TCP phase, and the distribution of Ag in β-TCP was homogeneous. A metallic Ag phase coexisted with HA. The solubility of Ag in HA was estimated to be 0.0019–0.0061 (Ag/(Ca + Ag)) atomic ratio, which was lower than that in β-TCP (higher than 0.0536) and higher than that of β-CPP (below the detection limit of analyses). - Highlights: • The HA powders with Ag nanoparticles were synthesized by a precipitation method. • Metallic Ag particles were detected with the HA phase after sintering. • The distribution of Ag in β-TCP was homogeneous after sintering. • The addition of Ag stabilized the β-ΤCP phase. • β-TCP exhibited higher solubility of Ag than HA and β-CPP.

  8. Synthesis and characterization of Ag-containing calcium phosphates with various Ca/P ratios

    International Nuclear Information System (INIS)

    Gokcekaya, Ozkan; Ueda, Kyosuke; Narushima, Takayuki; Ergun, Celaletdin

    2015-01-01

    Ag-containing calcium phosphate (CaP) powders were synthesized by a precipitation method using aqueous solutions of calcium nitrate, silver nitrate, and ammonium phosphate. The powders were sintered at temperatures ranging from 1173 to 1473 K. The charged atomic ratios of (Ca + Ag)/P and Ag/(Ca + Ag) in solution were varied from 1.33 to 1.67 and from 0 to 0.30, respectively. The Ag content in the as-precipitated CaP powders increased with the charged Ag/(Ca + Ag) atomic ratio in solution and was lower than the charged Ag/(Ca + Ag) value. The as-precipitated CaP powders consisted of hydroxyapatite (HA) as the main phase. Ag nanoparticles were observed on the as-precipitated HA particles under all conditions of Ag addition. After the sintering, HA, β-TCP (tricalcium phosphate), α-TCP, and β-CPP (calcium pyrophosphate) were mainly detected as CaPs on the basis of the Ca/P atomic ratio of the as-precipitated powders. The addition of Ag stabilized the β-TCP phase, and the distribution of Ag in β-TCP was homogeneous. A metallic Ag phase coexisted with HA. The solubility of Ag in HA was estimated to be 0.0019–0.0061 (Ag/(Ca + Ag)) atomic ratio, which was lower than that in β-TCP (higher than 0.0536) and higher than that of β-CPP (below the detection limit of analyses). - Highlights: • The HA powders with Ag nanoparticles were synthesized by a precipitation method. • Metallic Ag particles were detected with the HA phase after sintering. • The distribution of Ag in β-TCP was homogeneous after sintering. • The addition of Ag stabilized the β-ΤCP phase. • β-TCP exhibited higher solubility of Ag than HA and β-CPP

  9. Chromium doped TiO2 sputtered thin films synthesis, physical investigations and applications

    CERN Document Server

    Hajjaji, Anouar; Gaidi, Mounir; Bessais, Brahim; El Khakani, My Ali

    2014-01-01

    This book presents co-sputtered processes ways to produce chrome doped TiO2 thin films onto various substrates such as quartz, silicon and porous silicon. Emphasis is given on the link between the experimental preparation and physical characterization in terms of Cr content. Moreover, the structural, optical and optoelectronic investigations are emphasized throughout. The book explores the potencial applications of devices based on Cr doped TiO2 thin films as gas sensors and in photocatalysis and in the photovoltaic industry. Also, this book provides extensive leads into research literature, and each chapter contains details which aim to develop awareness of the subject and the methods used. The content presented here will be useful for graduate students as well as researchers in materials science, physics, chemistry and engineering.

  10. Tensile properties of latex paint films with TiO2 pigment

    Science.gov (United States)

    Hagan, Eric W. S.; Charalambides, Maria N.; Young, Christina T.; Learner, Thomas J. S.; Hackney, Stephen

    2009-05-01

    The tensile properties of latex paint films containing TiO2 pigment were studied with respect to temperature, strain-rate and moisture content. The purpose of performing these experiments was to assist museums in defining safe conditions for modern paintings held in collections. The glass transition temperature of latex paint binders is in close proximity to ambient temperature, resulting in high strain-rate dependence in typical exposure environments. Time dependence of modulus and failure strain is discussed in the context of time-temperature superposition, which was used to extend the experimental time scale. Nonlinear viscoelastic material models are also presented, which incorporate a Prony series with the Ogden or Neo-Hookean hyperelastic function for different TiO2 concentrations.

  11. Influence of anodization parameters on the morphology of TiO 2 nanotube arrays

    Science.gov (United States)

    Omidvar, Hamid; Goodarzi, Saba; Seif, Ahmad; Azadmehr, Amir R.

    2011-07-01

    TiO 2 nanotube arrays can be fabricated by electrochemical anodization in organic and inorganic electrolytes. Morphology of these nanotube arrays changes when anodization parameters such as applied voltage, type of electrolyte, time and temperature are varied. Nanotube arrays fabricated by anodization of commercial titanium in electrolytes containing NH 4F solution and either sulfuric or phosphoric acid were studied at room temperature; time of anodization was kept constant. Applied voltage, fluoride ion concentration, and acid concentrations were varied and their influences on TiO 2 nanotubes were investigated. The current density of anodizing was recorded by computer controlled digital multimeter. The surface morphology (top-view) of nanotube arrays were observed by SEM. The nanotube arrays in this study have inner diameters in range of 40-80 nm.

  12. The use of nanoscale visible light-responsive photocatalyst TiO2-Pt for the elimination of soil-borne pathogens.

    Directory of Open Access Journals (Sweden)

    Ya-Lei Chen

    Full Text Available Exposure to the soil-borne pathogens Burkholderia pseudomallei and Burkholderia cenocepacia can lead to severe infections and even mortality. These pathogens exhibit a high resistance to antibiotic treatments. In addition, no licensed vaccine is currently available. A nanoscale platinum-containing titania photocatalyst (TiO(2-Pt has been shown to have a superior visible light-responsive photocatalytic ability to degrade chemical contaminants like nitrogen oxides. The antibacterial activity of the catalyst and its potential use in soil pathogen control were evaluated. Using the plating method, we found that TiO(2-Pt exerts superior antibacterial performance against Escherichia coli compared to other commercially available and laboratory prepared ultraviolet/visible light-responsive titania photocatalysts. TiO(2-Pt-mediated photocatalysis also affectively eliminates the soil-borne bacteria B. pseudomallei and B. cenocepacia. An air pouch infection mouse model further revealed that TiO(2-Pt-mediated photocatalysis could reduce the pathogenicity of both strains of bacteria. Unexpectedly, water containing up to 10% w/v dissolved soil particles did not reduce the antibacterial potency of TiO(2-Pt, suggesting that the TiO(2-Pt photocatalyst is suitable for use in soil-contaminated environments. The TiO(2-Pt photocatalyst exerted superior antibacterial activity against a broad spectrum of human pathogens, including B. pseudomallei and B. cenocepacia. Soil particles (<10% w/v did not significantly reduce the antibacterial activity of TiO(2-Pt in water. These findings suggest that the TiO(2-Pt photocatalyst may have potential applications in the development of bactericides for soil-borne pathogens.

  13. Synthesis and photocatalytic properties of porous TiO2 films prepared by ODA/sol-gel method

    International Nuclear Information System (INIS)

    Zhang Wenjie; Bai Jiawei

    2012-01-01

    Porous TiO 2 films were deposited on SiO 2 pre-coated glass-slides by sol-gel method using octadecylamine (ODA) as template. The amount of ODA in the sol played an important role on the physicochemical properties and photocatalytic performance of the TiO 2 films. The films prepared at different conditions were all composed of anatase titanium dioxide crystals, and TiO 2 crystalline size got larger with increasing ODA amount. The maximum specific surface area of 41.5 m 2 /g was obtained for TiO 2 powders prepared from titanium sol containing 2.0 g ODA. Methyl orange degradation rate was enhanced along with increasing ODA amount and reached the maximal value at 2.0 g addition of ODA. After 40 min of UV-light irradiation, methyl orange degradation rate reached 30.5% on the porous film, which was about 10% higher than that on the smooth film. Porous TiO 2 film showed almost constant activity with slight decrease from 30.5% to 28.5% after 4 times of recycles.

  14. Fast fabrication of long TiO2 nanotube array with high photoelectrochemical property on flexible stainless steel.

    Science.gov (United States)

    Tao, Jie; Wu, Tao; Gao, Peng

    2012-03-01

    Oriented highly ordered long TiO2 nanotube array films with nanopore structure and high photoelectrochemical property were fabricated on flexible stainless steel substrate (50 microm) by anodization treatment of titanium thin films in a short time. The samples were characterized by means of field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD) and photoelectrochemical methods, respectively. The results showed that Ti films deposited at the condition of 0.7 Pa Ar pressure and 96 W sputtering power at room temperature was uniform and dense with good homogeneity and high crystallinity. The voltage and the anodization time both played significant roles in the formation of TiO2 nanopore-nanotube array film. The optimal voltage was 60 V and the anodization time is less than 30 min by anodizing Ti films in ethylene glycerol containing 0.5% (w) NH4F and 3% (w) H2O. The growth rate of TiO2 nanotube array was as high as 340 nm/min. Moreover, the photocurrent-potential curves, photocurrent response curves and electrochemical impedance spectra results indicated that the TiO2 nanotube array film with the nanoporous structure exhibited a better photo-response ability and photoelectrochemical performance than the ordinary TiO2 nanotube array film. The reason is that the nanoporous structure on the surface of the nanotube array can separate the photo electron-hole pairs more efficiently and completely than the tubular structure.

  15. In situ modification of cell-culture scaffolds by photocatalysis of visible-light-responsive TiO2 film

    Science.gov (United States)

    Kono, Sho; Furusawa, Kohei; Kurotobi, Atsushi; Hattori, Kohei; Yamamoto, Hideaki; Hirano-Iwata, Ayumi; Tanii, Takashi

    2018-02-01

    We propose a novel process to modify the cell affinity of scaffolds in a cell-culture environment using the photocatalytic activity of visible-light (VL)-responsive TiO2. The proposed process is the improved version of our previous demonstration in which ultraviolet (UV)-responsive TiO2 was utilized. In that demonstration, we showed that cell-repellent molecules on TiO2 were decomposed and replaced with cell-permissive molecules upon UV exposure in the medium where cells are being cultured. However, UV irradiation involves taking the risk of inducing damage to the cells. In this work, a TiO2 film was sputter-deposited on a quartz coverslip at 640 °C without O2 gas injection to create a rutile structure containing oxygen defects, which is known to exhibit photocatalytic activity upon VL exposure. We show that the cell adhesion site and migration area can be controlled with the photocatalytic activity of the VL-responsive TiO2 film, while the cellular oxidative stress is reduced markedly by the substitution of VL for UV.

  16. Thermal degradation of TiO2 nanotubes on titanium

    Science.gov (United States)

    Shivaram, Anish; Bose, Susmita; Bandyopadhyay, Amit

    2014-10-01

    The objective of this research was to study thermal degradation behavior of TiO2 nanotubes on titanium (Ti). TiO2 nanotubes were grown via anodization method on commercially pure Ti (Cp-Ti) discs using two different electrolytes, 1 vol. % HF in deionized (DI) water and 1 vol. % HF + 0.5 wt. % NH4F + 10 vol. % DI water in ethylene glycol, to obtain nanotubes with two different lengths, 300 nm and 950 nm keeping the nanotube diameter constant at 100 ± 20 nm. As grown TiO2 nanotubes were subjected to heat treatment to understand thermal degradation as a function of both temperature and hold time. The signs of degradation were observed mainly when amorphous nanotubes started to crystallize, however the crystallization temperature varied based on TiO2 nanotubes length and anodizing condition. Overall, 300 nm nanotubes were thermally stable at least up to 400 °C for 12 h, while the 950 nm long nanotubes show signs of degradation from 400 °C for 6 h only. Clearly, length of nanotubes, heat treatment temperature as well as hold times show influence toward degradation kinetics of TiO2 nanotubes on titanium.

  17. Magnesium Potassium Phosphate Compound for Immobilization of Radioactive Waste Containing Actinide and Rare Earth Elements

    Directory of Open Access Journals (Sweden)

    Sergey E. Vinokurov

    2018-06-01

    Full Text Available The problem of effective immobilization of liquid radioactive waste (LRW is key to the successful development of nuclear energy. The possibility of using the magnesium potassium phosphate (MKP compound for LRW immobilization on the example of nitric acid solutions containing actinides and rare earth elements (REE, including high level waste (HLW surrogate solution, is considered in the research work. Under the study of phase composition and structure of the MKP compounds that is obtained by the XRD and SEM methods, it was established that the compounds are composed of crystalline phases—analogues of natural phosphate minerals (struvite, metaankoleite. The hydrolytic stability of the compounds was determined according to the semi-dynamic test GOST R 52126-2003. Low leaching rates of radionuclides from the compound are established, including a differential leaching rate of 239Pu and 241Am—3.5 × 10−7 and 5.3 × 10−7 g/(cm2∙day. As a result of the research work, it was concluded that the MKP compound is promising for LRW immobilization and can become an alternative material combining the advantages of easy implementation of the technology, like cementation and the high physical and chemical stability corresponding to a glass-like compound.

  18. Preparation of micro-porous bioceramic containing silicon-substituted hydroxyapatite and beta-tricalcium phosphate.

    Science.gov (United States)

    Fuh, Lih-Jyh; Huang, Ya-Jing; Chen, Wen-Cheng; Lin, Dan-Jae

    2017-06-01

    Dimensional instability caused by sintering shrinkage is an inevitable drawback for conventional processing of hydroxyapatite (HA). A new preparation method for biphasic calcium phosphates was developed to increase micro pores and biodegradation without significant dimensional change. Powder pressed HA discs, under 100MPa, were immersed in a colloidal mixture of tetraethoxysilane (TEOS) and ammonium hydroxide for 10min, followed by drying, and then were sintered at 900°C, 1050°C, and 1200°C, respectively. Comparing with pure HA discs, the newly prepared product sintered up to 1200°C contained silicon substituted HA, beta-tricalcium phosphate, and calcium silicate with better micro-porosity, high specific surface area, less sintering shrinkage and the strength maintained. The cytocompatibility test demonstrated a better viability for D1 mice stem cells cultured on TEOS treated HA for 14days compared to the pure HA. This simple TEOS sol-gel pretreatment has the potential to be applied to any existing manufacturing process of HA scaffold for better control of sintering shrinkage, create micropores, and increase biodegradation. Copyright © 2017 Elsevier B.V. All rights reserved.

  19. Food-grade TiO2 impairs intestinal and systemic immune homeostasis, initiates preneoplastic lesions and promotes aberrant crypt development in the rat colon.

    Science.gov (United States)

    Bettini, Sarah; Boutet-Robinet, Elisa; Cartier, Christel; Coméra, Christine; Gaultier, Eric; Dupuy, Jacques; Naud, Nathalie; Taché, Sylviane; Grysan, Patrick; Reguer, Solenn; Thieriet, Nathalie; Réfrégiers, Matthieu; Thiaudière, Dominique; Cravedi, Jean-Pierre; Carrière, Marie; Audinot, Jean-Nicolas; Pierre, Fabrice H; Guzylack-Piriou, Laurence; Houdeau, Eric

    2017-01-20

    Food-grade titanium dioxide (TiO 2 ) containing a nanoscale particle fraction (TiO 2 -NPs) is approved as a white pigment (E171 in Europe) in common foodstuffs, including confectionary. There are growing concerns that daily oral TiO 2 -NP intake is associated with an increased risk of chronic intestinal inflammation and carcinogenesis. In rats orally exposed for one week to E171 at human relevant levels, titanium was detected in the immune cells of Peyer's patches (PP) as observed with the TiO 2 -NP model NM-105. Dendritic cell frequency increased in PP regardless of the TiO 2 treatment, while regulatory T cells involved in dampening inflammatory responses decreased with E171 only, an effect still observed after 100 days of treatment. In all TiO 2 -treated rats, stimulation of immune cells isolated from PP showed a decrease in Thelper (Th)-1 IFN-γ secretion, while splenic Th1/Th17 inflammatory responses sharply increased. E171 or NM-105 for one week did not initiate intestinal inflammation, while a 100-day E171 treatment promoted colon microinflammation and initiated preneoplastic lesions while also fostering the growth of aberrant crypt foci in a chemically induced carcinogenesis model. These data should be considered for risk assessments of the susceptibility to Th17-driven autoimmune diseases and to colorectal cancer in humans exposed to TiO 2 from dietary sources.

  20. Data on the effect of the dispersion of functionalized nanoparticles TiO2 with photocatalytic activity in LDPE

    Directory of Open Access Journals (Sweden)

    Alvarado Jahell

    2018-02-01

    Full Text Available This article contains the dataset referring to the article ''Study of the effect of the dispersion of functionalized nanoparticles TiO2 with photocatalytic activity in LDPE'' (Jahell et al., 2016 [1]. It includes the FT-IR data of the functionalized nanoparticles of TiO2 with Hexadecyltrimethoxysilane in different degrees of functionalization, thermogravimetric analysis, distribution and particle size in the polymer matrix by scanning electron microscopy (SEM, carbonyl index, gravimetry and scanning electron microscopy of the nanocomposite degraded by UV radiation.

  1. Synthesis of titanate, TiO2 (B), and anatase TiO2 nanofibers from natural rutile sand

    International Nuclear Information System (INIS)

    Pavasupree, Sorapong; Suzuki, Yoshikazu; Yoshikawa, Susumu; Kawahata, Ryoji

    2005-01-01

    Titanate nanofibers were synthesized by hydrothermal method (150 deg. C for 72 h) using natural rutile sand as the starting materials. TiO 2 (B) and anatase TiO 2 (high crystallinity) nanofibers with the diameters of 20-100 nm and the lengths of 10-100 μm were obtained by calcined titanate nanofibers for 4 h at 400 and 700 deg. C (in air), respectively. The samples characterized by XRD, SEM, TEM, SAED, HRTEM, and BET surface area. This synthesis method provides a simple route to fabricate one-dimensional nanostructured TiO 2 from low cost material. -- Graphical abstract: Titanate nanofibers (b) were synthesized by hydrothermal method (150 deg. C for 72 h) using natural rutile sand (a) as the starting materials. TiO 2 (B) (c) and anatase TiO 2 (d) nanofibers with the diameters of 20-50 nm and the lengths of 10-100 μm were obtained by calcined titanate nanofibers for 4 h at 400 deg. C and 700 deg. C (in air), respectively

  2. Effect of TiO2 on the Gas Sensing Features of TiO2/PANi Nanocomposites

    Directory of Open Access Journals (Sweden)

    Duong Ngoc Huyen

    2011-02-01

    Full Text Available A nanocomposite of titanium dioxide (TiO2 and polyaniline (PANi was synthesized by in-situ chemical polymerization using aniline (ANi monomer and TiCl4 as precursors. SEM pictures show that the nanocomposite was created in the form of long PANi chains decorated with TiO2 nanoparticles. FTIR, Raman and UV-Vis spectra reveal that the PANi component undergoes an electronic structure modification as a result of the TiO2 and PANi interaction. The electrical resistor of the nanocomposite is highly sensitive to oxygen and NH3 gas, accounting for the physical adsorption of these gases. A nanocomposite with around 55% TiO2 shows an oxygen sensitivity of 600–700%, 20–25 times higher than that of neat PANi. The n-p contacts between TiO2 nanoparticles and PANi matrix give rise to variety of shallow donors and acceptor levels in the PANi band gap which enhance the physical adsorption of gas molecules.

  3. Fluorescence properties of Yb3+-Er3+ co-doped phosphate glasses containing silver nanoparticles

    Science.gov (United States)

    Martínez Gámez, Ma A.; Vallejo H, Miguel A.; Kiryanov, A. V.; Licea-Jiménez, L.; Lucio M, J. L.; Pérez-García, S. A.

    2018-04-01

    Er3+-Yb3+ co-doped phosphate glasses containing silver nitrate (SN), were fabricated. Transmission electron microscopy (TEM) and x-ray photoelectron spectroscopy (XPS) analyses were used to evidence the nucleation and presence of silver nanoparticles (SNP). The basic parameters of the glasses were inspected by means of absorption and fluorescence spectra, and fluorescence lifetimes under excitation at 916 nm (in-band of Yb3+), and at 406 nm (in-band of surface plasmon resonance given by the presence of SNP). The spectra as well as estimates for the basic parameters defining the lasing/amplifying potential of the glasses were studied as a function of SN concentration. The experimental results indicate that by increasing the SN content an enhancement of Er3+/Yb3+ fluorescence takes place.

  4. Enhancing phosphorus release from waste activated sludge containing ferric or aluminum phosphates by EDTA addition during anaerobic fermentation process.

    Science.gov (United States)

    Zou, Jinte; Zhang, Lili; Wang, Lin; Li, Yongmei

    2017-03-01

    The effect of ethylene diamine tetraacetic acid (EDTA) addition on phosphorus release from biosolids and phosphate precipitates during anaerobic fermentation was investigated. Meanwhile, the impact of EDTA addition on the anaerobic fermentation process was revealed. The results indicate that EDTA addition significantly enhanced the release of phosphorus from biosolids, ferric phosphate precipitate and aluminum phosphate precipitate during anaerobic fermentation, which is attributed to the complexation of metal ions and damage of cell membrane caused by EDTA. With the optimal EDTA addition of 19.5 mM (0.41 gEDTA/gSS), phosphorus release efficiency from biosolids was 82%, which was much higher than that (40%) without EDTA addition. Meanwhile, with 19.5 mM EDTA addition, almost all the phosphorus in ferric phosphate precipitate was released, while only 57% of phosphorus in aluminum phosphate precipitate was released. This indicates that phosphorus in ferric phosphate precipitate was much easier to be released than that in aluminum phosphate precipitate during anaerobic fermentation of sludge. In addition, proper EDTA addition facilitated the production of soluble total organic carbon and volatile fatty acids, as well as solid reduction during sludge fermentation, although methane production could be inhibited. Therefore, EDTA addition can be used as an alternative method for recovering phosphorus from waste activated sludge containing ferric or aluminum precipitates, as well as recovery of soluble carbon source. Copyright © 2016 Elsevier Ltd. All rights reserved.

  5. Study of hMSC proliferation and differentiation on Mg and Mg–Sr containing biphasic β-tricalcium phosphate and amorphous calcium phosphate ceramics

    International Nuclear Information System (INIS)

    Singh, Satish S.; Roy, Abhijit; Lee, Boeun; Kumta, Prashant N.

    2016-01-01

    Biphasic mixtures of either Mg"2"+ or combined Mg"2"+ and Sr"2"+ cation substituted β-tricalcium phosphate (β-TCP) and amorphous calcium phosphate (ACP) were prepared using a low temperature chemical phosphatizing and hydrolysis reaction approach. Scaffolds prepared using the cation substituted calcium phosphates were capable of supporting similar levels of human mesenchymal stem cell proliferation in comparison to commercially available β-TCP. The concentrations of Mg"2"+, Sr"2"+, and PO_4"3"− released from these scaffolds were also within the ranges desired from previous reports to support both hMSC proliferation and osteogenic differentiation. Interestingly, hMSCs cultured directly on scaffolds prepared with only Mg"2"+ substituted β-TCP were capable of supporting statistically significantly increased alkaline phosphatase activity, osteopontin, and osteoprotegerin expression in comparison to all compositions containing both Mg"2"+ and Sr"2"+, and commercially available β-TCP. hMSCs cultured in the presence of scaffold extracts also exhibited similar trends in the expression of osteogenic markers as was observed during direct culture. Therefore, it was concluded that the enhanced differentiation observed was due to the release of bioactive ions rather than the surface microstructure. The role of these ions on transforming growth factor-β and bone morphogenic protein signaling was also evaluated using a PCR array. It was concluded that the release of these ions may support enhanced differentiation through SMAD dependent TGF-β and BMP signaling. - Highlights: • Synthesis of Mg and Mg-Sr containing biphasic beta tricalcium phosphate ceramics • Magnesium substitution influences ALP activity compared to strontium content. • Solution extract plays a more dominant role on hMSC differentiation. • Direct and indirect Mg and Mg-Sr TCP culture show similar OPG and OPN expression.

  6. Study of hMSC proliferation and differentiation on Mg and Mg–Sr containing biphasic β-tricalcium phosphate and amorphous calcium phosphate ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Satish S., E-mail: sss42@pitt.edu [Department of Chemical & Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Roy, Abhijit, E-mail: abr20@pitt.edu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Lee, Boeun [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Kumta, Prashant N., E-mail: pkumta@pitt.edu [Department of Chemical & Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Center for Craniofacial Regeneration, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Mechanical Engineering and Materials Science, University of Pittsburgh, PA 15261 (United States)

    2016-07-01

    Biphasic mixtures of either Mg{sup 2+} or combined Mg{sup 2+} and Sr{sup 2+} cation substituted β-tricalcium phosphate (β-TCP) and amorphous calcium phosphate (ACP) were prepared using a low temperature chemical phosphatizing and hydrolysis reaction approach. Scaffolds prepared using the cation substituted calcium phosphates were capable of supporting similar levels of human mesenchymal stem cell proliferation in comparison to commercially available β-TCP. The concentrations of Mg{sup 2+}, Sr{sup 2+}, and PO{sub 4}{sup 3−} released from these scaffolds were also within the ranges desired from previous reports to support both hMSC proliferation and osteogenic differentiation. Interestingly, hMSCs cultured directly on scaffolds prepared with only Mg{sup 2+} substituted β-TCP were capable of supporting statistically significantly increased alkaline phosphatase activity, osteopontin, and osteoprotegerin expression in comparison to all compositions containing both Mg{sup 2+} and Sr{sup 2+}, and commercially available β-TCP. hMSCs cultured in the presence of scaffold extracts also exhibited similar trends in the expression of osteogenic markers as was observed during direct culture. Therefore, it was concluded that the enhanced differentiation observed was due to the release of bioactive ions rather than the surface microstructure. The role of these ions on transforming growth factor-β and bone morphogenic protein signaling was also evaluated using a PCR array. It was concluded that the release of these ions may support enhanced differentiation through SMAD dependent TGF-β and BMP signaling. - Highlights: • Synthesis of Mg and Mg-Sr containing biphasic beta tricalcium phosphate ceramics • Magnesium substitution influences ALP activity compared to strontium content. • Solution extract plays a more dominant role on hMSC differentiation. • Direct and indirect Mg and Mg-Sr TCP culture show similar OPG and OPN expression.

  7. Electrochemical synthesis of self-organized TiO2 crystalline nanotubes without annealing

    Science.gov (United States)

    Giorgi, Leonardo; Dikonimos, Theodoros; Giorgi, Rossella; Buonocore, Francesco; Faggio, Giuliana; Messina, Giacomo; Lisi, Nicola

    2018-03-01

    This work demonstrates that upon anodic polarization in an aqueous fluoride-containing electrolyte, TiO2 nanotube array films can be formed with a well-defined crystalline phase, rather than an amorphous one. The crystalline phase was obtained avoiding any high temperature annealing. We studied the formation of nanotubes in an HF/H2O medium and the development of crystalline grains on the nanotube wall, and we found a facile way to achieve crystalline TiO2 nanotube arrays through a one-step anodization. The crystallinity of the film was influenced by the synthesis parameters, and the optimization of the electrolyte composition and anodization conditions (applied voltage and time) were carried out. For comparison purposes, crystalline anatase TiO2 nanotubes were also prepared by thermal treatment of amorphous nanotubes grown in an organic bath (ethylene glycol/NH4F/H2O). The morphology and the crystallinity of the nanotubes were studied by field emission gun-scanning electron microscopy (FEG-SEM) and Raman spectroscopy, whereas the electrochemical and semiconducting properties were analyzed by means of linear sweep voltammetry, impedance spectroscopy, and Mott-Schottky plots. X-ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS) allowed us to determine the surface composition and the electronic structure of the samples and to correlate them with the electrochemical data. The optimal conditions to achieve a crystalline phase with high donor concentration are defined.

  8. Biofilm formation on a TiO2 nanotube with controlled pore diameter and surface wettability

    International Nuclear Information System (INIS)

    Anitha, V C; Narayan Banerjee, Arghya; Woo Joo, Sang; Lee, Jin-Hyung; Lee, Jintae; Ki Min, Bong

    2015-01-01

    Titania (TiO 2 ) nanotube arrays (TNAs) with different pore diameters (140 − 20 nm) are fabricated via anodization using hydrofluoric acid (HF) containing ethylene glycol (EG) by changing the HF-to-EG volume ratio and the anodization voltage. To evaluate the effects of different pore diameters of TiO 2 nanotubes on bacterial biofilm formation, Shewanella oneidensis (S. oneidensis) MR-1 cells and a crystal-violet biofilm assay are used. The surface roughness and wettability of the TNA surfaces as a function of pore diameter, measured via the contact angle and AFM techniques, are correlated with the controlled biofilm formation. Biofilm formation increases with the decreasing nanotube pore diameter, and a 20 nm TiO 2 nanotube shows the maximum biofilm formation. The measurements revealed that 20 nm surfaces have the least hydrophilicity with the highest surface roughness of ∼17 nm and that they show almost a 90% increase in the effective surface area relative to the 140 nm TNAs, which stimulate the cells more effectively to produce the pili to attach to the surface for more biofilm formation. The results demonstrate that bacterial cell adhesion (and hence, biofilm formation) can effectively be controlled by tuning the roughness and wettability of TNAs via controlling the pore diameters of TNA surfaces. This biofilm formation as a function of the surface properties of TNAs can be a potential candidate for both medical applications and as electrodes in microbial fuel cells. (paper)

  9. Photocatalytic degradation of diuron in aqueous solution by platinized TiO2

    International Nuclear Information System (INIS)

    Katsumata, Hideyuki; Sada, Maki; Nakaoka, Yusuke; Kaneco, Satoshi; Suzuki, Tohru; Ohta, Kiyohisa

    2009-01-01

    The photocatalytic degradation of diuron, which is one of phenylurea herbicides, was carried out in the presence of platinized TiO 2 photocatalyst. Platinization was found to increase the rate of diuron degradation. When 0.2 wt.% of platinum was deposited onto the surface of TiO 2 , an initial diuron concentration of 10 mg L -1 was completely degraded after 20 min. Furthermore, the first-order rate constant for diuron degradation by Pt-TiO 2 was ca. 4 times higher than P-25 TiO 2 . In addition, the photocatalytic activity of Pt-TiO 2 was appeared under visible light. The decrease of TOC as a result of mineralization of diuron was observed during the photocatalytic process. The degree of diuron mineralization was about 97% under UV irradiation after 8 h. The formations of chloride, nitrate and ammonium ions as end-products were observed during the photocatalytic system. The decomposition of diuron gave four kinds of intermediate products. The degradation mechanism of diuron was proposed on the base of the evidence of the identified intermediates. Based on these results, the photocatalytic reaction by Pt-TiO 2 could be useful technology for the treatment of wastewater containing diuron.

  10. Synthesis of anatase TiO2 nanoparticles with beta-cyclodextrin as a supramolecular shell.

    Science.gov (United States)

    Li, Landong; Sun, Xiaohong; Yang, Yali; Guan, Naijia; Zhang, Fuxiang

    2006-11-20

    We report a novel, green hydrothermal-synthesis route to well-dispersed anatase TiO2 nanoparticles with particle sizes of 9-16 nm in the presence of beta-CD (beta-cyclodextrin). During the synthesis process, the CD-containing synthesis mixture assembled in both longitudinal and latitudinal directions. Driven by the interaction between molecules, the beta-CDs assembled in the longitudinal direction to form long-chain compounds, whereas in the latitudinal direction, they tended to form regular aggregates through coordination with the Ti species from the hydrolysis of tetrabutyl titanate. In view of the effect of the coordination and the steric hindrance of beta-CDs as a supramolecular shell, homogeneous nuclei and slow growth of TiO2 crystals during the synthesis process was observed, which was responsible for the formation of uniform TiO2 nanoparticles. The low beta-CD dosage and the high product yield (>90%) demonstrated well the potential of this synthesis route in the large-scale industrial production of anatase nanoparticles.

  11. Pilarization TiO2 onto De-oiled spent bleaching clay using Rarasaponin as surfactant

    Science.gov (United States)

    Hindryawati, N.; Daniel; Erwin; Fadillah, N. D.

    2018-03-01

    Synthesis and characterization TiO2 pillared deoiled spent bleaching clay (DSBC) with rarasaponin as surfactant had been done. Activation DSBC have been done with H2SO4 1N, followed by pillarization with TiO2 using rarasaponin as surfactant. Characterization has done with Fourier transform infrared spectroscopy showed the rarasaponin as surfactant was successfully carried out in DSBC with the presence of absorption peak C=O stretching group in a sharp 1720.50 cm-1 wavelength range. As well as the C-CH2 stretching uptake peak is represented on wave number 1462.04 cm-1 and 1033,85 cm-1 for aromatic functional group C=C stretching. After pillared by TiO2, the XRD pattern on DSBC showed new peak appears on 2θ = 27,4460° 36,0850° and 55,3216° and the mineral contain on DSBC is rectorite with dioctahedral mica layer and dioctahedral smectite with ratio 2:1. This molecule have formula Na.Al4(Si, Al)8.O20.(OH)4. H2O. Crystallinty of pillared clay showed 72,5014 % after calcination and there is some Ti suspected on the layer based on SEM.

  12. Removal of Crotamiton from Reverse Osmosis Concentrate by a TiO2/Zeolite Composite Sheet

    Directory of Open Access Journals (Sweden)

    Qun Xiang

    2017-07-01

    Full Text Available Reverse osmosis (RO concentrate from wastewater reuse facilities contains concentrated emerging pollutants, such as pharmaceuticals. In this research, a paper-like composite sheet consisting of titanium dioxide (TiO2 and zeolite was synthesized, and removal of the antipruritic agent crotamiton from RO concentrate was studied using the TiO2/zeolite composite sheet. The RO concentrate was obtained from a pilot-scale municipal secondary effluent reclamation plant. Effective immobilization of the two powders in the sheet made it easy to handle and to separate the photocatalyst and adsorbent from purified water. The TiO2/zeolite composite sheet showed excellent performance for crotamiton adsorption without obvious inhibition by other components in the RO concentrate. With ultraviolet irradiation, crotamiton was simultaneously removed through adsorption and photocatalysis. The photocatalytic decomposition of crotamiton in the RO concentrate was significantly inhibited by the water matrix at high initial crotamiton concentrations, whereas rapid decomposition was achieved at low initial crotamiton concentrations. The major degradation intermediates were also adsorbed by the composite sheet. This result provides a promising method of mitigating secondary pollution caused by the harmful intermediates produced during advanced oxidation processes. The cyclic use of the HSZ-385/P25 composite sheet indicated the feasibility of continuously removing crotamiton from RO concentrate.

  13. UV light induced photodegradation of malachite green on TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Chen, C.C.; Lu, C.S.; Chung, Y.C.; Jan, J.L.

    2007-01-01

    The photodegradation of malachite green (MG), a cationic triphenylmethane dye, is examined both under different pH values and amounts of TiO 2 . After 15 W UV-365 nm irradiation for 4 h, ca. 99.9% of MG was degraded with addition of 0.5 g L -1 TiO 2 to solutions containing 50 mg L -1 of the MG dye. The HPLC-PDA-ESI-MS technique was used to obtain a better understanding on the mechanistic details of this TiO 2 -assisted photodegradation of the MG dye with UV irradiation. Five intermediates of the process were separated, identified, and characterized for the first time. The results indicated that the N-de-methylation degradation of MG dye took place in a stepwise manner to yield mono-, di-, tri-, and tetra-N-de-methylated MG species generated during the processes. Under acidic conditions, the results indicated that the photodegradation mechanism is favorable to cleavage of the whole conjugated chromophore structure of the MG dye. Under basic conditions, the results showed that the photodegradation mechanism is favorable to a formation of a series of N-de-methylated intermediates of the MG dye

  14. Discoloration of a red cationic dye by supported TiO2 photocatalysis

    International Nuclear Information System (INIS)

    Mounir, B.; Pons, M.N.; Zahraa, O.; Yaacoubi, A.; Benhammou, A.

    2007-01-01

    The degradation under UV, visible and sunlight irradiation of C.I. Basic Red 46 (BR 46) dye used for acrylic fibers dyeing has been studied in a lab-scale continuous system with two different immobilized TiO 2 systems. Catalyst I was based on TiO 2 particles deposited on cellulose fibers; Catalyst II combined TiO 2 particles deposited on a layer of cellulose fibers (as in Catalyst I) with a layer of carbon fibers and finally a layer of cellulose fibers. The treatment of aqueous dye solutions and industrial wastewater contaminated with the same dye has been evaluated in terms of color removal and chemical oxygen demand (COD) decrease. With UV light, aqueous solutions containing dye were decolorized slightly more rapidly with Catalyst II than with Catalyst I. Sunlight was also very effective and experiments involving sunlight irradiation showed Catalyst II to be the more efficient, giving more than 90% discoloration after 20 min of treatment. Comparing the discoloration yield by adsorption or under visible light for both catalysts, it was observed that the difference between them is below 5%. The adsorption kinetics was found to follow a second-order rate law for Catalyst I and a first-order rate law for Catalyst II. The kinetics of photocatalytic degradation under UV or sunlight were found to follow a first-order rate law for both catalytic systems. Under sunlight the COD removal yield for textile wastewater reaches 33% with Catalyst I against 93% with Catalyst II

  15. Composite TiO2/clays materials for photocatalytic NOx oxidation

    Science.gov (United States)

    Todorova, N.; Giannakopoulou, T.; Karapati, S.; Petridis, D.; Vaimakis, T.; Trapalis, C.

    2014-11-01

    TiO2 photocatalyst received much attention for air purification applications especially for removal of air pollutants like NOx, VOCs etc. It has been established that the activity of the photocatalyst can be significantly enhanced by its immobilization onto suitable substrates like inorganic minerals, porous silica, hydroxyapatite, adsorbent materials like activated carbon, various co-catalysts such as semiconductors, graphene, reduced graphite oxide, etc. In the present work, photocatalytic composite materials consisted of mineral substrate and TiO2 in weight ratio 1:1 were manufactured and examined for oxidation and removal of nitric oxides NOx (NO and NO2). Commercial titania P25 (Evonik-Degussa) and urea-modified P25 were used as photocatalytically active components. Inorganic minerals, namely kunipia, talk and hydrotalcite were selected as supporting materials due to their layered structure and expected high NOx adsorption capability. Al3+ and Ca2+ intercalation was applied in order to improve the dispersion of TiO2 and its loading into the supporting matrix. The X-ray diffraction analysis and Scanning Electron Microscopy revealed the binary structure of the composites and homogeneous dispersion of the photocatalyst into the substrates. The photocatalytic behavior of the materials in NOx oxidation and removal was investigated under UV and visible light irradiation. The composite materials exhibited superior photocatalytic activity than the bare titania under both types of irradiation. Significant visible light activity was recorded for the composites containing urea-modified titania that was accredited to the N-doping of the semiconductor. Among the different substrates, the hydrotalcite caused highest increase in the NOx removal, while among the intercalation ions the Ca2+ was more efficient. The results were related to the improved dispersion of the TiO2 and the synergetic activity of the substrates as NOx adsorbers.

  16. Influence of electrical parameters on morphology of nanostructured TiO2 layers developed by electrochemical anodization

    Directory of Open Access Journals (Sweden)

    Strnad Gabriela

    2017-01-01

    Full Text Available Ti6Al4V alloy micro rough surfaces with TiO2 self-organized nanostructured layers were synthesized using electrochemical anodization in phosphate/fluoride electrolyte, at different end potentials (5V, 10V, 15V, and 20 V. The current – time characteristics were recorded, and the link between current evolution and the morphology of developing oxide layers was investigated. On flat surfaces of Ti6Al4V alloy we developed TiO2 layers with different morphologies (random pores, nanopores of 25…50 nm, and highly organized nanotubes of 50…100 nm in diameter depending on electrical parameters of anodization process. In our anodization cell, in optimized conditions, we are able to superimpose nanostructured oxide layers (nanotubular or nanoporous over micro structured surfaces of titanium based materials used for biomedical implants.

  17. Photocatalytic Degradation of Methylene Blue under UV Light Irradiation on Prepared Carbonaceous TiO2

    Directory of Open Access Journals (Sweden)

    Zatil Amali Che Ramli

    2014-01-01

    Full Text Available This study involves the investigation of altering the photocatalytic activity of TiO2 using composite materials. Three different forms of modified TiO2, namely, TiO2/activated carbon (AC, TiO2/carbon (C, and TiO2/PANi, were compared. The TiO2/carbon composite was obtained by pyrolysis of TiO2/PANi prepared by in situ polymerization method, while the TiO2/activated carbon (TiO2/AC was obtained after treating TiO2/carbon with 1.0 M KOH solution, followed by calcination at a temperature of 450°C. X-ray powder diffraction (XRD, transmission electron microscopy (TEM, Fourier transform infrared (FTIR, thermogravimetric analysis (TG-DTA, Brunauer-Emmet-Teller (BET, and UV-Vis spectroscopy were used to characterize and evaluate the prepared samples. The specific surface area was determined to be in the following order: TiO2/AC > TiO2/C > TiO2/PANi > TiO2 (179 > 134 > 54 > 9 m2 g−1. The evaluation of photocatalytic performance for the degradation of methylene blue under UV light irradiation was also of the same order, with 98 > 84.7 > 69% conversion rate, which is likely to be attributed to the porosity and synergistic effect in the prepared samples.

  18. TiO2 effect on crystallization mechanism and physical properties of nano glass-ceramics of MgO-Al2O3-SiO2 glass system.

    Science.gov (United States)

    Jo, Sinae; Kang, Seunggu

    2013-05-01

    The effect of TiO2 on the degree of crystallization, thermal properties and microstructure for MgO-Al2O3-SiO2 glass-ceramics system containing 0-13 wt% TiO2 and 0-1.5 wt% B2O3 in which the cordierite is the main phase was studied. Using Kissinger and Augis-Bennett equations, the activation energy, 510 kJ/mol and Avrami constant, 1.8 were calculated showing the surface-oriented crystallization would be preferred. The alpha-cordierite phase was generated in the glass-ceramics of containing TiO2 of 0-5.6 wt%. However, for the glass-ceramics of TiO2 content above 7 wt%, an alpha-cordierite disappeared and micro-cordierite phase was formed. The glass-ceramics of no TiO2 added had spherical crystals of few tens nanometer size spread in the matrix. As TiO2 content increased up to 5.6 wt%, a lump of dendrite was formed. In the glass-ceramics containing TiO2 7-13 wt%, in which the main phase is micro-cordierite, the dendrite crystal disappeared and a few hundred nanometer sized crystal particles hold tightly each other were generated. The thermal conductivity of glass-ceramics of both a-cordierite and micro-cordierite base decreased with TiO2 contend added. The thermal conductivity of glass-ceramics of 1.5 wt% TiO2 added was 3.4 W/mK which is 36% higher than that of glass-ceramics of no TiO2 added. The sintering temperature for 1.5 wt% TiO2 glass-ceramics was 965 degrees C which could be concluded as to apply to LTCC process for LED packaging.

  19. Development of novel strontium containing bioactive glass based calcium phosphate cement.

    Science.gov (United States)

    D'Onofrio, A; Kent, N W; Shahdad, S A; Hill, R G

    2016-06-01

    The aim of this study was to investigate the effect on properties of increasing strontium substitution for calcium in bioactive glasses used as precursors for novel calcium phosphate cements. Glasses were produced by progressively substituting strontium for calcium. Cements were prepared by mixing the glass powder with Ca(H2PO4)2 powder with a 2.5% solution of Na2HPO4. Setting times and compressive strength were measured after 1h, 1 day, 7 days and 28 days immersion in Tris buffer solution. X-ray diffraction (XRD), Fourier transform infrared spectroscopy and radiopacity were measured and crystal morphology was assessed using scanning electron microscopy. A correlation between the phases formed, morphology of the crystallites, setting time and compressive strength were analyzed. Setting time increased proportionally with strontium substitution in the glass up to 25%, whereas for higher substitutions it decreased. Compressive strength showed a maximum value of 12.5MPa and was strongly influenced by the interlocking of the crystals and their morphology. XRD showed that the presence of strontium influenced the crystal phases formed. Octacalcium phosphate (Ca8H2(PO4)6·5H2O, OCP) was the main phase present after 1h and 1 day whereas after 28 days OCP was completely transformed to strontium-containing hydroxyapatite (SrxCa(10-x)(PO4)6(OH)2, SrHA). Radiopacity increased proportionally to strontium substitution in the glass. A novel method to develop a bone substitute forming in vitro SrHA as a final product by using a bioactive glass as a precursor was shown. These novel injectable bioactive glass cements are promising materials for dental and orthopedic applications. Further in vivo characterizations are being conducted. Copyright © 2016 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  20. Interactions of aqueous NOM with nanoscale TiO2: implications for ceramic membrane filtration-ozonation hybrid process.

    Science.gov (United States)

    Kim, Jeonghwan; Shan, Wenqian; Davies, Simon H R; Baumann, Melissa J; Masten, Susan J; Tarabara, Volodymyr V

    2009-07-15

    The combined effect of pH and calcium on the interactions of nonozonated and ozonated natural organic matter (NOM) with nanoscale TiO2 was investigated. The approach included characterization of TiO2 nanoparticles and NOM, extended Derjaguin-Landau-Verwey-Overbeek (XDLVO) modeling of NOM-TiO2 and NOM-NOM interactions, batch study on the NOM adsorption onto TiO2 surface, and bench-scale study on the treatment of NOM-containing feed waters using a hybrid process that combines ozonation and ultrafiltration with a 5 kDa ceramic (TiO2 surface) membrane. It was demonstrated that depending on pH and TiO2 loading, the adsorption of NOM species is controlled by either the availability of divalent cations or by preozonation of NOM. XDLVO surface energy analysis predicts NOM adsorption onto TiO2 in the ozone-controlled regime but not in the calcium-controlled regime. In both regimes, short-range NOM-NOM and NOM-TiO2 interactions were governed by acid-base and van der Waals forces, whereas the role of electrostatic forces was relatively insignificant. Ozonation increased the surface energy of NOM, contributing to the hydrophilic repulsion component of the NOM-NOM and NOM-TiO2 interactions. In the calcium-controlled regime, neither NOM-TiO2 nor NOM-NOM interaction controlled adsorption. Non-XDLVO interactions such as intermolecular bridging by calcium were hypothesized to be responsible for the observed adsorption behavior. Adsorption data proved to be highly predictive of the permeate flux performance.

  1. Enhanced the hydrophobic surface and the photo-activity of TiO2-SiO2 composites

    Science.gov (United States)

    Wahyuni, S.; Prasetya, A. T.

    2017-02-01

    The aim of this research is to develop nanomaterials for coating applications. This research studied the effect of various TiO2-SiO2 composites in acrylic paint to enhance the hydrophobic properties of the substrate. Titanium dioxide containing silica in the range 20-35 mol% has been synthesized using sol-gel route. The XRD’s spectra show that increasing SiO2 content in the composite, decreasing its crystalline properties but increasing the surface area. TiO2-SiO2 composite was dispersed in acrylic paint in 2% composition by weight. The largest contact angle was 70, which produced by the substrate coated with TS-35-modified acrylic paint. This study also investigated the enhanced photo-activity of TiO2-SiO2 modified with poly-aniline. The XRD spectra show that the treatment does not change the crystal structure of TiO2. The photo-activity of the composite was evaluated by degradation of Rhodamine-B with visible light. The best performance of the degradation process was handled by the composite treated with 0.1mL anilines per gram of TiO2-SiO2 composite (TSP-A). On the other side, the contact angle 70 has not shown an excellent hydrophobic activity. However, the AFM spectra showed that nanoroughness has started to form on the surface of acrylic paint modified with TiO2-SiO2 than acrylic alone.

  2. Dye-sensitized solar cells based on anatase TiO2/multi-walled carbon nanotubes composite nanofibers photoanode

    International Nuclear Information System (INIS)

    Du, Pingfan; Song, Lixin; Xiong, Jie; Li, Ni; Wang, Lijun; Xi, Zhenqiang; Wang, Naiyan; Gao, Linhui; Zhu, Hongliang

    2013-01-01

    Highlights: ► TiO 2 /multi-walled carbon nanotubes (MWCNTs) hybrid nanofibers are prepared via electrospinning. ► Dye-sensitized solar cells (DSSCs) are assembled using TiO 2 /MWCNTs nanofibers film as photoanode. ► Energy conversion efficiency of DSSCs is greatly dependent on the content of MWCNTs. ► Moderate MWCNTs incorporation can substantially enhance the performance of DSSCs. - Abstract: Anatase TiO 2 /multi-walled carbon nanotubes (TiO 2 /MWCNTs) hybrid nanofibers (NFs) film was prepared via a facile electrospinning method. Dye-sensitized solar cells (DSSCs) based on TiO 2 /MWCNTs composite NFs photoanodes with different contents of MWCNTs (0, 0.1, 0.3, 0.5, 1 wt.%) were assembled using N719 dye as sensitizer. Field emission scanning electron microscope (FESEM), transmission electron microscope (TEM), X-ray diffractometer (XRD), and Raman spectrometer were used to characterize the TiO 2 /MWCNTs electrode films. The photocurrent–voltage (I–V) characteristic, incident photo-to-current conversion efficiency (IPCE) spectrum, and electrochemical impedance spectroscopy (EIS) measurements were carried out to evaluate the photoelectric properties of the DSSCs. The results reveal that the energy conversion efficiency is greatly dependent on the content of MWCNTs in the composite NFs film, and a moderate incorporation of MWCNTs can substantially enhance the performance of DSSCs. When the electrode contains 0.3 wt.% MWCNTs, the corresponding solar cell yield the highest efficiency of 5.63%. This efficiency value is approximately 26% larger than that of the unmodified counterpart.

  3. Fabrication of TiO2/Carbon Photocatalyst using Submerged DC Arc Discharged in Ethanol/Acetic Acid Medium

    Science.gov (United States)

    Saraswati, T. E.; Nandika, A. O.; Andhika, I. F.; Patiha; Purnawan, C.; Wahyuningsih, S.; Rahardjo, S. B.

    2017-05-01

    This study aimed to fabricate a modified photocatalyst of TiO2/C to enhance its performance. The fabrication was achieved using the submerged direct current (DC) arc-discharge method employing two graphite electrodes, one of which was filled with a mixture of carbon powder, TiO2, and binder, in ethanol with acetic acid added in various concentrations. The arc-discharge method was conducted by flowing a current of 10-20 A (~20 V). X-ray diffraction (XRD) patterns showed significant placements of the main peak characteristics of TiO2, C graphite, and titanium carbide. The surface analysis using Fourier transform infrared spectroscopy (FTIR) revealed that fabricated TiO2/C nanoparticles had stretching vibrations of Ti-O, C-H, C═O, C-O, O-H and C═C in the regions of 450-550 cm-1, 2900-2880 cm-1, 1690-1760 cm-1, 1050-1300 cm-1, 3400-3700 cm-1 and ~1600 cm-1, respectively. In addition, the study investigated the photocatalysts of unmodified and modified TiO2/C for photodegradation of methylene blue (MB) dye solution under mercury lamp irradiation. The effectiveness of the degradation was defined by the decrease in 60-minute absorbance under a UV-Vis spectrophotometer. Modified TiO2/C proved to be significantly more efficient in reducing dye concentrations, reaching ~70%. It indicated that the oxygen-containing functional groups have been successfully attached to the surface of the nanoparticles and played a role in enhancing photocatalytic activity.

  4. Antibacterial activity and ion release of bonding agent containing amorphous calcium phosphate nanoparticles.

    Science.gov (United States)

    Chen, Chen; Weir, Michael D; Cheng, Lei; Lin, Nancy J; Lin-Gibson, Sheng; Chow, Laurence C; Zhou, Xuedong; Xu, Hockin H K

    2014-08-01

    Recurrent caries at the margins is a primary reason for restoration failure. The objectives of this study were to develop bonding agent with the double benefits of antibacterial and remineralizing capabilities, to investigate the effects of NACP filler level and solution pH on Ca and P ion release from adhesive, and to examine the antibacterial and dentin bond properties. Nanoparticles of amorphous calcium phosphate (NACP) and a quaternary ammonium monomer (dimethylaminododecyl methacrylate, DMADDM) were synthesized. Scotchbond Multi-Purpose (SBMP) primer and adhesive served as control. DMADDM was incorporated into primer and adhesive at 5% by mass. NACP was incorporated into adhesive at filler mass fractions of 10%, 20%, 30% and 40%. A dental plaque microcosm biofilm model was used to test the antibacterial bonding agents. Calcium (Ca) and phosphate (P) ion releases from the cured adhesive samples were measured vs. filler level and solution pH of 7, 5.5 and 4. Adding 5% DMADDM and 10-40% NACP into bonding agent, and water-aging for 28 days, did not affect dentin bond strength, compared to SBMP control at 1 day (p>0.1). Adding DMADDM into bonding agent substantially decreased the biofilm metabolic activity and lactic acid production. Total microorganisms, total streptococci, and mutans streptococci were greatly reduced for bonding agents containing DMADDM. Increasing NACP filler level from 10% to 40% in adhesive increased the Ca and P ion release by an order of magnitude. Decreasing solution pH from 7 to 4 increased the ion release from adhesive by 6-10 folds. Bonding agents containing antibacterial DMADDM and remineralizer NACP were formulated to have Ca and P ion release, which increased with NACP filler level from 10% to 40% in adhesive. NACP adhesive was "smart" and dramatically increased the ion release at cariogenic pH 4, when these ions would be most-needed to inhibit caries. Therefore, bonding agent containing DMADDM and NACP may be promising to inhibit

  5. Sulphur doped nanoparticles of TiO2

    Czech Academy of Sciences Publication Activity Database

    Szatmáry, Lórant; Bakardjieva, Snejana; Šubrt, Jan; Bezdička, Petr; Jirkovský, Jaromír; Bastl, Zdeněk; Brezová, V.; Korenko, M.

    2011-01-01

    Roč. 161, č. 1 (2011), s. 23-28 ISSN 0920-5861 R&D Projects: GA MŠk 1M0577 Institutional research plan: CEZ:AV0Z40400503; CEZ:AV0Z40320502 Keywords : photocatalyst * S-doped TiO2 * Thiourea Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 3.407, year: 2011

  6. Impedance spectroscopy studies of surface engineered TiO2 ...

    Indian Academy of Sciences (India)

    Administrator

    Impedance; nanoTiO2; self-assembled monolayers; electrical resistivity; permittivity. 1. Introduction ... search studies showed that nanostructured TiO2 ceramics possess ..... tion handbook (ed) J Cazes (New York: Marcel Dekker). 3rd ed, p ...

  7. Supercritical Flow Synthesis of TiO2

    DEFF Research Database (Denmark)

    Hellstern, Henrik Christian; Becker, Jacob; Hald, Peter

    2014-01-01

    A new, up-scaled supercritical flow synthesis apparatus has been constructed in Aarhus. A module based system allows for a range of parameter studies with improved parameter control. The dual-reactor setup enables both single phase and core-shell nanoparticle synthesis. TiO2 is a well-known mater...

  8. Fluoropolymer - TiO2 coatings and their superhydrophilicity

    DEFF Research Database (Denmark)

    Søgaard, Erik Gydesen; Simonsen, Morten Enggrob; Jepsen, Henrik

    In this work the superhydrophilicity of coatings on fluoropolymer were investigated. The different coatings were prepared by help of P25 Degussa TiO2 powder, titaniumisopropoxide, Lumiflon® and two different curing agents (BL 3175 and Cymel 303). The investigations were performed by help of a sta...

  9. High-pressure polymorphs of anatase TiO2

    DEFF Research Database (Denmark)

    Arlt, T.; Bermejo, M.; Blanco, M. A.

    2000-01-01

    The equation of state of anatase TiO2 has been determined experimentally-using polycrystalline as well as single-crystal material-and compared with theoretical calculations using the ab initio perturbed ion model. The results are highly consistent, the zero-pressure bulk modulus being 179(2) GPa ...

  10. Protein Corona Prevents TiO2 Phototoxicity.

    Directory of Open Access Journals (Sweden)

    Maja Garvas

    Full Text Available TiO2 nanoparticles have generally low toxicity in the in vitro systems although some toxicity is expected to originate in the TiO2-associated photo-generated radical production, which can however be modulated by the radical trapping ability of the serum proteins. To explore the role of serum proteins in the phototoxicity of the TiO2 nanoparticles we measure viability of the exposed cells depending on the nanoparticle and serum protein concentrations.Fluorescence and spin trapping EPR spectroscopy reveal that the ratio between the nanoparticle and protein concentrations determines the amount of the nanoparticles' surface which is not covered by the serum proteins and is proportional to the amount of photo-induced radicals. Phototoxicity thus becomes substantial only at the protein concentration being too low to completely coat the nanotubes' surface.These results imply that TiO2 nanoparticles should be applied with ligands such as proteins when phototoxic effects are not desired - for example in cosmetics industry. On the other hand, the nanoparticles should be used in serum free medium or any other ligand free medium, when phototoxic effects are desired - as for efficient photodynamic cancer therapy.

  11. Photochemistry of 1,1,1-Trifluoroacetone on Rutile TiO2(110)

    International Nuclear Information System (INIS)

    Zehr, Robert T.; Deskins, N. Aaron; Henderson, Michael A.

    2010-01-01

    The ultraviolet (UV) photon-induced photodecomposition of 1,1,1-trifluoroacetone (TFA) adsorbed on the rutile TiO2(110) surface has been investigated with photon stimulated desorption (PSD), temperature programmed desorption (TPD) and density functional theory (DFT). TFA adsorbed molecularly on the reduced surface (8% oxygen vacancies) in states desorbing below 300 K with trace thermal decomposition observed in TPD. Adsorption of TFA on a preoxidized TiO2(110) surface (accomplished by pre-exposure with 20 L O2) led to formation of a new TFA desorption state at 350 K, assigned to decomposition of a TFA-diolate species ((CF3)(CH3)COO). No TFA photochemistry was detected on the reduced surface. UV irradiation of TFA on the oxidized surface depleted TFA in the 350 K state, with TFA molecules in other TPD states unaffected. PSD measurements reveal that both carbonyl substituents (CH3 and CF3), as well as CO, were liberated during UV exposure at 95 K. Post-irradiation TPD showed evidence for both acetate (evolving as ketene at 650 K) and trifluoroacetate (evolving as CO2 at 600 K) as surface-bound photodecomposition products. The CO PSD product was not due to adsorbed CO, to mass spectrometer cracking of a CO-containing PSD product, or from background effects, but originated from complete fragmentation of an unidentified adsorbed TFA species. Thermodynamic analysis using DFT indicated that the photodecomposition of the TFA-diolate was likely not driven by thermodynamics alone as both pathways (CH3+trifluoroacetate and CF3+acetate) were detected when thermodynamics shows a clear preference for only one (CF3+acetate). These observations are in contrast to the photochemical behavior of acetone, butanone and acetaldehyde on TiO2(110), where only one of the two carbonyl substituent groups was observed, with a stoichiometric amount of carboxylate containing the other substituent left on the surface. We conclude that fluorination significantly alters the electronic structure of

  12. Sol-gel route to synthesis of microporous ceramic membranes: Thermal stability of TiO2-ZrO2 mixed oxides

    International Nuclear Information System (INIS)

    Qunyin Xu; Anderson, M.A.

    1993-01-01

    In this paper concerning the synthesis of microporous ceramic membranes, the authors focus on the preparation and thermal stability of unsupported microporous TiO 2 -ZrO 2 mixed-oxide membranes. It has been observed that, by adding up to 20% ZrO 2 into TiO 2 or up to 10% TiO 2 into ZrO 2 , these microporous membranes display improved thermal stability. They can be fired up to 500 C for 0.5 h without closing micropores. However, membranes containing almost equal percentages of each component have lost microporous features and have low surface areas and low porosities. A phase diagram of a two-component TiO 2 -ZrO 2 mixed-oxide membrane has been prepared based on DTA and X-ray diffraction data in order to better understand the microstructure changes upon firing

  13. TiO2--a prototypical memristive material.

    Science.gov (United States)

    Szot, K; Rogala, M; Speier, W; Klusek, Z; Besmehn, A; Waser, R

    2011-06-24

    Redox-based memristive switching has been observed in many binary transition metal oxides and related compounds. Since, on the one hand, many recent reports utilize TiO(2) for their studies of the memristive phenomenon and, on the other hand, there is a long history of the electronic structure and the crystallographic structure of TiO(2) under the impact of reduction and oxidation processes, we selected this material as a prototypical material to provide deeper insight into the mechanisms behind memristive switching. In part I, we briefly outline the results of the historical and recent studies of electroforming and resistive switching of TiO(2)-based cells. We describe the (tiny) stoichiometrical range for TiO(2 - x) as a homogeneous compound, the aggregation of point defects (oxygen vacancies) into extended defects, and the formation of the various Magnéli phases. Furthermore, we discuss the driving forces for these solid-state reactions from the thermodynamical point of view. In part II, we provide new experimental details about the hierarchical transformation of TiO(2) single crystals into Magnéli phases, and vice versa, under the influence of chemical, electrical and thermal gradients, on the basis of the macroscopic and nanoscopic measurements. Those include thermogravimetry, high-temperature x-ray diffraction (XRD), high-temperature conductivity measurements, as well as low-energy electron diffraction (LEED), x-ray photoelectron spectroscopy (XPS), and LC-AFM (atomic force microscope equipped with a conducting tip) studies. Conclusions are drawn concerning the relevant parameters that need to be controlled in order to tailor the memristive properties.

  14. Development of the scientific concept of the phosphate methods for actinide-containing waste handling (pyrochemical fuel reprocessing)

    International Nuclear Information System (INIS)

    Orlova, A.I.; Orlova, V.A.; Skiba, O.V.; Bychkov, A.V.; Volkov, Yu.F.; Lukinykh, A.N.; Tomilin, S.V.; Lizin, A.A.

    2008-01-01

    Full text of publication follows: The crystallochemical phosphate concept in question is developed successfully in the new pyro-electrochemical reprocessing technology of irradiated fuel in molten chlorides of alkaline elements at one of the leading scientific nuclear centers - Research Institute of Atomic Reactors. Irradiated fuel is dissolved in molten chlorides of alkaline elements by mean of treating by chlorine. Then uranium and plutonium dioxides are removed electrochemically. The melt, when used many times, is contaminated by the residual actinide and contains fission products and the so called 'process' elements. This melt is unacceptable for future use. Phosphate methods can be applied for the solution of the following tasks: a) reprocessing (purification) of molten chloride salt solvents; b) conversion of the spent chloride melts to the insoluble stable crystalline product for safe storage and disposal. Within the framework of task 'a' phosphate methods may be realized by the several ways: 1) phosphate concentrating of impurities and their extraction from molten chlorides into solid phase by mean of chemical precipitation, co-precipitation, ion exchange and other chemical interactions, 2) conversion of precipitated waste phosphates to stable crystalline phosphate powders or ceramics for safe storage and disposal. (authors)

  15. Bactericidal Activity of Aqueous Acrylic Paint Dispersion for Wooden Substrates Based on TiO2 Nanoparticles Activated by Fluorescent Light

    Directory of Open Access Journals (Sweden)

    Diana Di Gioia

    2013-08-01

    Full Text Available The photocatalytic effect of TiO2 has great potential for the disinfection of surfaces. Most studies reported in the literature use UV activation of TiO2, while visible light has been used only in a few applications. In these studies, high concentrations of TiO2, which can compromise surface properties, have been used. In this work, we have developed an acrylic-water paint dispersion containing low TiO2 content (2 vol % for the inactivation of microorganisms involved in hospital-acquired infections. The nanoparticles and the coating have been characterized using spectroscopic techniques and transmission electron microscopy, showing their homogenous dispersion in the acrylic urethane coating. A common fluorescent light source was used to activate the photocatalytic activity of TiO2. The paint dispersion showed antimicrobial activity against Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa. The coating containing the TiO2 nanoparticles maintained good UV stability, strong adhesion to the substrate and high hardness. Therefore, the approach used is feasible for paint formulation aimed at disinfection of healthcare surfaces.

  16. Studied Localized Surface Plasmon Resonance Effects of Au Nanoparticles on TiO2 by FDTD Simulations

    Directory of Open Access Journals (Sweden)

    Guo-Ying Yao

    2018-06-01

    substrate leads to the enhanced local enhanced electric field at the boundaries, which is favorable for the improvement of photocatalytic performance of TiO2. These findings could explain the underlying mechanism of some experimental observations in published experimental works, and helpful to design highly efficient composite photocatalysts that contain noble metal co-catalyst nanoparticles.

  17. In vitro assessments of experimental NaF dentifrices containing a prospective calcium phosphate technology.

    Science.gov (United States)

    Karlinsey, Robert L; Mackey, Allen C; Stookey, George K; Pfarrer, Aaron M

    2009-06-01

    To determine the fluoride dose response of experimental NaF dentifrices containing a prospective calcium phosphate technology, along with the corresponding relative enamel and dentin abrasion values. 3 mm diameter bovine enamel specimens were mounted, ground and polished, and softened in a carbopol-lactic acid solution (pH = 5.0) for 36 hours at 37 degrees C. Specimens were then measured for baseline Vickers microhardness and stratified (N = 18, mean VHN = 33) into eight groups. These groups consisted of a placebo paste, four test dentifrices (A, B, C, D) with three of the four (A, B, C) containing a promising calcium phosphate ingredient, Crest Cavity Protection, MI Paste Plus, and PreviDent Booster 5000. The groups were cycled in a lesion reversal pH cycling model consisting of four 2-minute treatment periods (diluted 1:3 with DI water) and one 4-hour acid challenge (carbopol-lactic acid, pH = 5.0) per day. Between these events, specimens were immersed in artificial saliva (pH = 7.0). After 20 days of cycling, the specimens were microdrilled and analyzed for fluoride content, and also measured for Vickers surface microhardness after 10 and 20 days of cycling and after a 2-hour and 16-hour post-cycle acid challenge (carbopol-lactic acid, pH = 5.0). Separately, relative dentin and enamel abrasion (RDA and REA) were performed using the ADA recommended radiotracer method. A fluoride dose response was observed for the test dentifrices after 10 and 20 days of pH cycling, with test dentifrice C promoting the highest remineralization among the groups while both the MI Paste Plus and PreviDent systems provide the least remineralization (one-way ANOVA, SNK, P dentin (one-way ANOVA, SNK, P < 0.05). Altogether, these data show the developmental test dentifrices demonstrate a fluoride dose response and show great promise in remineralizing white-spot enamel lesions relative to MI Paste Plus and PreviDent.

  18. Biocorrosion of TiO2 nanoparticle coating of Ti-6Al-4V in DMEM under specific in vitro conditions

    Science.gov (United States)

    Höhn, Sarah; Virtanen, Sannakaisa

    2015-02-01

    A TiO2 nanoparticle coating was prepared on a biomedical Ti-6Al-4V alloy using "spin-coating" technique with a colloidal suspension of TiO2 nanopowders with the aim to optimize the surface morphology (e.g., roughness) for improved biocompatibility. The influence of a TiO2 nanoparticle (NP) coating on the corrosion behavior, metal ion release, and biomimetic apatite formation was studied in DMEM, at 37.5 °C with a continuous supply of 5% CO2. Electrochemical impedance spectroscopy measurements indicate a formation of a new layer on the surface of the NP-coated sample upon 28 days immersion in DMEM. Scanning electron microscopy (SEM) and X-ray spectroscopy confirm that the surface of the NP-coated Ti-6Al-4V shows a complete coverage by a Ca-phosphate layer in contrast to the non-coated Ti-6Al-4V alloy. Hence, the TiO2-NP coating strongly enhances biomimetic apatite formation on the alloy surface. In addition, the TiO2-NP coating can efficiently reduce Al-release from the alloy, for which the bare Ti-6Al-4V alloy is significant for at least 28 days of immersion in DMEM.

  19. Photocatalytic Degradation of Chlorobenzene by TiO2 in High-Temperature and High-Pressure Water

    Directory of Open Access Journals (Sweden)

    N. Kometani

    2008-01-01

    Full Text Available A fluidized-bed-type flow reactor available for the photocatalytic treatment of the suspension of model soil under high-temperature, high-pressure conditions was designed. An aqueous suspension containing hydrogen peroxide (H2O2 as an oxidizer and inorganic oxides as a model soil, titania (TiO2, silica (SiO2, or kaoline (Al2Si2O5(OH4 was continuously fed into the reactor with the temperature and the pressure controlled to be T=20–400∘C and P = 30 MPa, respectively. The degradation of chlorobenzene (CB in water was chosen as a model oxidation reaction. It appeared that most of the model soils are not so harmful to the SCWO treatment of CB in solutions. When the TiO2 suspension containing H2O2 was irradiated with near-UV light, the promotion of the degradation caused by photocatalytic actions of TiO2 was observed at all temperatures. Persistence of the photocatalytic activity in the oxidation reaction in high-temperature, high-pressure water would open up a possibility of the development of the hybrid process based on the combination of SCWO process and TiO2 photocatalysis for the treatment of environmental pollutants in soil and water, which are difficult to handle by conventional SCWO process or catalytic SCWO process alone.

  20. Synergistic reinforcing effect of TiO2 and montmorillonite on potato starch nanocomposite films: Thermal, mechanical and barrier properties.

    Science.gov (United States)

    Oleyaei, Seyed Amir; Almasi, Hadi; Ghanbarzadeh, Babak; Moayedi, Ali Akbar

    2016-11-05

    In this study, ternary potato starch (PS) bionanocomposite films containing two types of nanoparticles, sodium montmorillonite (MMT), one-dimensional (1D) clay platelets, (3 and 5wt%) and TiO2, three-dimensional (3D) nanospheres, (0.5, 1 and 2wt%), are prepared using solvent casting method. X-ray diffraction (XRD) test confirms the completely exfoliated structure formed in the PS-MMT nanocomposites containing 3 and 5% MMT. The success of the formation of new hydrogen bonds between the hydroxyl groups of starch and nanofillers is confirmed by Fourier transform infrared (FTIR) spectroscopy. Tensile strength (TS), elongation at break (EB), glass transition temperature (Tg), and melting point (Tm) of the films are also enhanced after MMT and TiO2 incorporation. The water vapor permeability (WVP) and the visible, UVA, UVB and UVC lights transmittance decreases upon TiO2 and MMT content increasing. Generally, a synergistic effect is observed between MMT and TiO2 at lower concentrations of MMT. Copyright © 2016 Elsevier Ltd. All rights reserved.

  1. Favorable recycling photocatalyst TiO2/CFA: Effects of loading percent of TiO2 on the structural property and photocatalytic activity

    International Nuclear Information System (INIS)

    Shi Jianwen; Chen Shaohua; Ye Zhilong; Wang Shumei; Wu Peng

    2010-01-01

    A series of photocatalysts TiO 2 /CFA were prepared using coal fly ash (CFA), waste discharged from coal-fired power plant, as substrate, and then these photocatalysts were characterized by scanning electron microscope, X-ray diffraction analysis, nitrogen adsorption test and ultraviolet-visible absorption analysis. The effects of loading percent of TiO 2 on the photocatalytic activity and re-use property of TiO 2 /CFA were evaluated by the photocatalytic decoloration and mineralization of methyl orange solution. The results show that the pore volume and the specific surface area of the TiO 2 /CFA both increased with the increase in the loading percent of TiO 2 , which improved the photocatalytic activity of TiO 2 /CFA. However, when the loading percent of TiO 2 was too high (up to 54.51%), superfluous TiO 2 was easy to break away from CFA in the course of water treatment, which was disadvantaged to the recycling property of TiO 2 /CFA. In this study, the optimal loading percent of TiO 2 was 49.97%, and the efficiencies of photocatalytic decoloration and mineralization could be maintained above 99% and 90%, respectively, when the photocatalyst was used repeatedly, without any decline, even at the sixth cycle.

  2. Calcium phosphate coating containing silver shows high antibacterial activity and low cytotoxicity and inhibits bacterial adhesion

    Energy Technology Data Exchange (ETDEWEB)

    Ando, Yoshiki, E-mail: andoy@jmmc.jp [Division of Microbiology, Department of Pathology and Microbiology, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan); Research Department, Japan Medical Materials Corporation, Uemura Nissei Bldg.9F 3-3-31 Miyahara, Yodogawa-ku, Osaka 532-0003 (Japan); Miyamoto, Hiroshi [Division of Microbiology, Department of Pathology and Microbiology, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan); Noda, Iwao; Sakurai, Nobuko [Research Department, Japan Medical Materials Corporation, Uemura Nissei Bldg.9F 3-3-31 Miyahara, Yodogawa-ku, Osaka 532-0003 (Japan); Akiyama, Tomonori [Division of Microbiology, Department of Pathology and Microbiology, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan); Yonekura, Yutaka; Shimazaki, Takafumi; Miyazaki, Masaki; Mawatari, Masaaki; Hotokebuchi, Takao [Department of Orthopaedic Surgery, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan)

    2010-01-01

    Surgical site infection is one of the serious complications of orthopedic implants. In order to reduce the incidence of implant-associated infections, we developed a novel coating technology of calcium phosphate (CP) containing silver (Ag), designated Ag-CP coating, using a thermal spraying technique. In this study, we evaluated the antibacterial efficacy and biological safety of this coating. In vitro antibacterial activity tests showed that the growths of Escherichia coli, Staphylococcus aureus and methicillin-resistant S. aureus (MRSA) are completely suppressed on Ag-CP coating. In vitro bacterial adherence tests revealed that the number of adherent bacteria on the surface of this coating is significantly less (p < 0.02) than that on the surface of the CP coating. Moreover, the Ag-CP coating completely inhibits MRSA adhesion [<10 colony-forming units (CFU)] when 10{sup 2} CFU MRSA is inoculated. On the other hand, V79 Chinese hamster lung cells were found to grow on the Ag-CP coating as well as on the CP coating in a cytotoxicity test. These results indicate that the Ag-CP coating on the surface of orthopedic implants exhibits antibacterial activity and inhibits bacterial adhesion without cytotoxicity.

  3. Superhydrophilicity of TiO2 nano thin films

    International Nuclear Information System (INIS)

    Mohammadizadeh, M.R.; Ashkarran, A.A.

    2007-01-01

    Full text: Among the several oxide semiconductors, titanium dioxide has a more helpful role in our environmental purification due to its photocatalytic activity, photo-induced superhydrophilicity, and as a result of them non-toxicity, self cleaning, and antifogging effects. After the discovery of superhydrophilicity of titanium dioxide in 1997, several researches have been performed due to its nature and useful applications. The superhydrophilicity property of the surface allows water to spread completely across the surface rather than remains as droplets, thus making the surface antifog and easy-to-clean. The distinction of photo-induced catalytic and hydrophilicity properties of TiO 2 thin films has been accepted although, the origin of hydrophilicity property has not been recognized completely yet. TiO 2 thin films on soda lime glass were prepared by the sol-gel method and spin coating process. The calcination temperature was changed from 100 to 550 C. XRD patterns show increasing the content of polycrystalline anatase phase with increasing the calcination temperature. The AFM results indicate granular morphology of the films, which particle size changes from 22 to 166 nm by increasing the calcination temperature. The RBS, EDX and Raman spectroscopy of the films show the ratio of Ti:O∼0.5, and diffusion of sodium ions from substrate into the layer, by increasing the calcination temperature. The UV/Vis. spectroscopy of the films indicates a red shift by increasing the calcination temperature. The contact angle meter experiment shows that superhydrophilicity of the films depends on the formation of anatase crystal structure and diffused sodium content from substrate to the layer. The best hydrophilicity property was observed at 450 C calcination temperature, where the film is converted to a superhydrophilic surface after 10 minutes under 2mW/cm 2 UV irradiation. TiO 2 thin film on Si(111), Si(100), and quartz substrates needs less time to be converted to superhydrophilic surface rather than glass and polycrystalline Si substrates. Our results are consistent with the idea that UV-induced wetting of TiO 2 surface is caused by the removal of hydrophobic layers of hydrocarbons by TiO 2 -mediated photo-oxidation, which leads to the attractive interaction of water with clean TiO 2 surface. (authors)

  4. Multiwalled carbon nanotubes decorated with nitrogen, palladium co-doped TiO2 (MWCNT/N, Pd co-doped TiO2) for visible light photocatalytic degradation of Eosin Yellow in water

    Science.gov (United States)

    Kuvarega, Alex T.; Krause, Rui W. M.; Mamba, Bhekie B.

    2012-03-01

    Multiwalled carbon nanotube (MWCNT/N), Pd co-doped TiO2 nanocomposites were prepared by calcining the hydrolysis products of the reaction of titanium isopropoxide, Ti(OC3H7)4 containing multiwalled carbon nanotubes with aqueous ammonia. The prepared samples were characterised by Fourier transform infrared spectroscopy, Raman spectroscopy, thermogravimetric analysis, diffuse reflectance UV-Vis spectrophotometry (DRUV-Vis), XRD, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). DRUV-Vis analysis confirmed the red shift in the absorption edge at lower MWCNT percentages. SEM and TEM images showed the complete coverage of the MWCNTs with clusters of anatase TiO2 at low MWCNT percentages. Higher MWCNT levels led to their aggregation and consequently poor coverage by N, Pd co-doped TiO2. The photocatalytic activities of the nanocomposites were monitored by photodegradation of Eosin Yellow under simulated solar and visible light irradiation (λ > 450 nm). Irradiation with simulated solar radiation gave higher dye-degradation rates compared to visible radiation. The optimum MWCNT weight percentage in the composites was found to be 0.5. High degradation-rate constants of 3.42 × 10-2 and 5.18 × 10-3 min-1 were realised for the 0.5% MWCNT/N, Pd co-doped TiO2 composite, using simulated solar light and visible light, respectively.

  5. Antibacterial and remineralizing orthodontic adhesive containing quaternary ammonium resin monomer and amorphous calcium phosphate nanoparticles.

    Science.gov (United States)

    Liu, Yan; Zhang, Ling; Niu, Li-Na; Yu, Tao; Xu, Hockin H K; Weir, Michael D; Oates, Thomas W; Tay, Franklin R; Chen, Ji-Hua

    2018-05-01

    To evaluate the bonding performance, antibacterial activity, and remineralization effect on enamel of the orthodontic adhesive containing MAE-DB and NACP. Eighty non-carious human premolars were divided into 3 groups: Transbond XT (TB), PEHB + 5% MAE-DB (PD), and PEHB + 40% NACP + 5% MAE-DB (PND). Premolars were bonded with orthodontic brackets, the first subgroup (n = 10) and the second subgroup (n = 10) were subjected to shear bond strength testing after immersed in water for 1 day and in demineralization solution for 28 days respectively and then tested surface roughness, while the third subgroup (n = 6) was used for microhardness evaluation after aged in demineralization solution for 28 days. For each adhesive, fifty disk samples were prepared for antibacterial study. Specimens measuring 12 mm × 2 mm × 2 mm were fabricated for ion release test. Bond strengths were in the order TB = PND > PND = PD for "1-day in water", and in the order TB = PND > PD for "28-days in pH 4 solution". No significant difference in the ARI scores for the three adhesive. Numerous bacteria adhered to TB surface, while PD and PND had minimal bacterial growth and activity. PND showed high levels of Ca and P ions release and enamel hardness. The surface roughness of enamel in PND was much lower than TB and PD and showed no significant difference with the sound, control enamel. PND adhesive with 5% MAE-DB and 40% NACP exhibits antibacterial and remineralizing capabilities, and did not adversely affect bond strength compared to commercial adhesive. Novel adhesive containing quaternary ammonium monomer and nano-amorphous calcium phosphate represents a promising candidate in combating enamel white spot lesions and even dental caries. Copyright © 2018 Elsevier Ltd. All rights reserved.

  6. Synthesis of calcium-phosphorous doped TiO2 nanotubes by anodization and reverse polarization: A promising strategy for an efficient biofunctional implant surface

    International Nuclear Information System (INIS)

    Alves, Sofia A.; Patel, Sweetu B.; Sukotjo, Cortino; Mathew, Mathew T.; Filho, Paulo N.; Celis, Jean-Pierre

    2017-01-01

    Highlights: • A new surface modification methodology for bio-functionalization of TiO2 NTs is addressed • Bone-like structured TiO2 nanotubular surfaces containing Ca and P were synthesized. • Ca/P-doped TiO2 NTs enhanced adhesion and proliferation of osteoblastic-like cells. • The bio-functionalization granted improved bio-electrochemical stability to TiO2 NTs. - Abstract: The modification of surface features such as nano-morphology/topography and chemistry have been employed in the attempt to design titanium oxide surfaces able to overcome the current dental implants failures. The main goal of this study is the synthesis of bone-like structured titanium dioxide (TiO 2 ) nanotubes enriched with Calcium (Ca) and Phosphorous (P) able to enhance osteoblastic cell functions and, simultaneously, display an improved corrosion behavior. To achieve the main goal, TiO 2 nanotubes were synthetized and doped with Ca and P by means of a novel methodology which relied, firstly, on the synthesis of TiO 2 nanotubes by anodization of titanium in an organic electrolyte followed by reverse polarization and/or anodization, in an aqueous electrolyte. Results show that hydrophilic bone-like structured TiO 2 nanotubes were successfully synthesized presenting a highly ordered nano-morphology characterized by non-uniform diameters. The chemical analysis of such nanotubes confirmed the presence of CaCO 3 , Ca 3 (PO 4 ) 2 , CaHPO 4 and CaO compounds. The nanotube surfaces submitted to reverse polarization, presented an improved cell adhesion and proliferation compared to smooth titanium. Furthermore, these surfaces displayed a significantly lower passive current in artificial saliva, and so, potential to minimize their bio-degradation through corrosion processes. This study addresses a very simple and promising multidisciplinary approach bringing new insights for the development of novel methodologies to improve the outcome of osseointegrated implants.

  7. The chemical bonds effect of anthocyanin and chlorophyll dyes on TiO2 for dye-sensitized solar cell (DSSC)

    Science.gov (United States)

    Ahliha, A. H.; Nurosyid, F.; Supriyanto, A.; Kusumaningsih, T.

    2017-11-01

    Anthocyanin and chlorophyll dyes have been blended as the photosensitizer of Dye-Sensitized Solar Cell (DSSC). The results study showed the effect of chemical bond dyes on TiO2 and the efficiency of DSSC. Ratio blend of the anthocyanin and chlorophyll dyes are 1:1. The absorbance of dyes and TiO2 were characterized using UV-Vis Spectrophotometer. The chemical bonds contained in TiO2-dyes were characterized using FT-IR spectrophotometer. The efficiency of DSSC was calculated using I-V meter. The absorption spectra of chlorophyll: anthocyanin blend dye solutions and TiO2 films can increase after the dye adsorption. Absorbance characterization of anthocyanin and chlorophyll dye blend solutions showed three peaks at the wavelength of 412 nm; 535.5 nm; and 656.5 nm. Absorbance characterization of spinach before being blend with anthocyanin dyes solutions showed two peaks at the wavelength of 431 nm and 665.5 nm. The absorption spectra of TiO2 films can increase after the dyes adsorption at the wavelength of 400 nm. FT-IR spectra of TiO2 founded the functional groups C-Br, C=C, and O-H. The functional groups founded in anthocyanin: chlorophyll dye blended on the surface of TiO2 are C-Br, C-O, O-H, C-H, C=C, C=O, and O-H. The result showed that the greatest efficiency of 0.0544% at dye red cabbage-spinach. Adsorption blends of anthocyanin and chlorophyll dyes on the surface of TiO2 can be used as the photosensitizer for DSSC.

  8. Fe doped TiO2 photocatalyst for the removal of As(III) under visible radiation and its potential application on the treatment of As-contaminated groundwater

    International Nuclear Information System (INIS)

    Garza-Arévalo, J.I.; García-Montes, I.; Reyes, M.Hinojosa; Guzmán-Mar, J.L.; Rodríguez-González, V.

    2016-01-01

    Highlights: • Incorporation of Fe in TiO 2 lattice extended absorption to visible light region. • TiO 2 –Fe 1.0 in anatase crystalline form was synthesized by sol–gel method. • TiO 2 –Fe 1.0 showed the highest photocatalytic activity for As(III) oxidation. • TiO 2 –Fe 1.0 had the highest adsorption capacity for the removal of generated As(V). • TiO 2 –Fe is a promising material on the treatment of As contaminated groundwater. - Abstract: The Fe doped TiO 2 catalyst was evaluated under visible radiation for As(III) removal. The TiO 2 –Fe was synthesized by sol–gel technique at 0.0, 1.0, 2.5, 5.0 and 10.0 wt% iron doping concentrations. The semiconductors were characterized by X-ray diffraction, diffuse reflectance UV–vis, Raman spectroscopy, nitrogen physisorption, SEM–EDS and potentiometric titration for point of zero charge determination. The photocatalytic oxidation of As(III) was assessed in aqueous suspension contained 5 mg L −1 As(III) at pH 7 with 0.25 g L −1 catalyst loading. The incorporation of iron ions in TiO 2 lattice extended the absorption to visible light region and create surface oxygen vacancies which favor photocatalytic oxidation reaction of As(III) using a small doping amount of Fe (1.0 wt%) in TiO 2 powder. Additionally, TiO 2 –Fe 1.0 showed the highest adsorption capacity for As(V) removal compared to sol–gel TiO 2 and P25 indicating that this catalyst is a promising material for As contaminated groundwater treatment.

  9. Degradation of Semiconductor Manufacturing Wastewater by Using a Novel Magnetic Composite TiO2/Fe3O4 Photoreactor Design

    Directory of Open Access Journals (Sweden)

    Chen-Yu Chang

    2012-01-01

    Full Text Available The purpose of this research is to develop a photocatalytic TiO2 that can be activated by visible light and can be conveniently recollected for reusing. This research synthesizes the 20 to 40 nm TiO2/Fe3O4 particles with magnetization of 5.8 emu/g using the modified sol-gel method followed by 500°C calcinations. The experiment verified that visible fluorescent light (VFL, contains no UV-A could activate the photocatalytic activity of TiO2/Fe3O4 particles as did ultraviolet A light (UV-A, 360 nm. Regular magnets can be used to separate TiO2/Fe3O4 particles from solution. The results indicate that VFL-sirradiated TiO2/Fe3O4 particles could decompose isopropanol (IPA in the absence of UV-A and the issue of TiO2/Fe3O4 recollection from water for reusing is also resolved.

  10. High photocatalytic activity of hierarchical SiO2@C-doped TiO2 hollow spheres in UV and visible light towards degradation of rhodamine B.

    Science.gov (United States)

    Zhang, Ying; Chen, Juanrong; Hua, Li; Li, Songjun; Zhang, Xuanxuan; Sheng, Weichen; Cao, Shunsheng

    2017-10-15

    Ongoing research activities are targeted to explore high photocatalytic activity of TiO 2 -based photocatalysts for the degradation of environmental contaminants under UV and visible light irradiation. In this work, we devise a facile, cost-effective technique to in situ synthesize hierarchical SiO 2 @C-doped TiO 2 (SCT) hollow spheres for the first time. This strategy mainly contains the preparation of monodisperse cationic polystyrene spheres (CPS), sequential deposition of inner SiO 2 , the preparation of the sandwich-like CPS@SiO 2 @CPS particles, and formation of outer TiO 2 . After the one-step removal of CPS templates by calcination at 450°C, hierarchical SiO 2 @C-doped TiO 2 hollow spheres are in situ prepared. The morphology, hierarchical structure, and properties of SCT photocatalyst were characterized by TEM. SEM, STEM Mapping, BET, XRD, UV-vis spectroscopy, and XPS. Results strongly confirm the carbon doping in the outer TiO 2 lattice of SCT hollow spheres. When the as-synthesized SCT hollow spheres were employed as a photocatalyst for the degradation of Rhodamine B under visible-light and ultraviolet irradiation, the SCT photocatalyst exhibits a higher photocatalytic activity than commercial P25, effectively overcoming the limitations of poorer UV activity for many previous reported TiO 2 -based photocatalysts due to doping. Copyright © 2017 Elsevier B.V. All rights reserved.

  11. A mechanistic study on templated electrodeposition of one-dimensional TiO2 nanorods and nanotubes using TiOSO4 as a precursor

    KAUST Repository

    Teo, Gladys Y.

    2014-10-01

    One-dimensional (1D) TiO2 nanorods and nanotubes have been successfully synthesized by templated electrodeposition within an anodic aluminium oxide membrane (AAM) using an aqueous precursor containing TiOSO 4. The deposition voltages were found to influence the resultant nanostructure of TiO2. Using a precursor of aqueous TiOSO4 at pH 3 maintained at 10 °C, TiO2 nanorods were electrodeposited in the AAM between applied voltages of - 1.4 V to - 1.0 V (vs. Ag/AgCl), while TiO2 nanotubes were obtained at less negative voltages of - 1.0 V to - 0.3 V (vs. Ag/AgCl). Cyclic voltammetry (CV) revealed that nitrate reduction in the voltage range of - 0.3 V to - 1.4 V played an essential role in the formation of TiO2. The mechanism for TiO2 nanotube formation has been elucidated, paving the way for the future tailoring of metal oxide nanostructures by templated electrodeposition. © 2014 Elsevier B.V.

  12. The effect of TiO2 nanoparticles on water permeability and thermal and mechanical properties of high strength self-compacting concrete

    International Nuclear Information System (INIS)

    Nazari, Ali; Riahi, Shadi

    2010-01-01

    Research highlights: → TiO 2 nanoparticles effects on self-compacting concrete. → Strength assessments. → Water permeability. → Thermal properties. → Pore structure. → Microstructure evaluations. - Abstract: In this work, strength assessments and coefficient of water absorption of high performance self-compacting concrete containing different amounts of TiO 2 nanoparticles have been investigated. The results indicate that the strength and the resistance to water permeability of the specimens are improved by adding TiO 2 nanoparticles in the cement paste up to 4.0 wt%. TiO 2 nanoparticles, as a result of increased crystalline Ca(OH) 2 amount especially at the early age of hydration, could accelerate C-S-H gel formation and hence increase the strength of the concrete specimens. In addition, TiO 2 nanoparticles are able to act as nanofillers and recover the pore structure of the specimens by decreasing harmful pores. Several empirical relationships have been presented to predict flexural and split tensile strength of the specimens by means of the corresponding compressive strength at a certain age of curing. Accelerated peak appearance in conduction calorimetry tests, more weight loss in thermogravimetric analysis and more rapid appearance of the peaks related to hydrated products in X-ray diffraction results, all indicate that TiO 2 nanoparticles could improve mechanical and physical properties of the concrete specimens.

  13. A mechanistic study on templated electrodeposition of one-dimensional TiO2 nanorods and nanotubes using TiOSO4 as a precursor

    KAUST Repository

    Teo, Gladys Y.; Ryan, Mary P.; Riley, D. Jason

    2014-01-01

    One-dimensional (1D) TiO2 nanorods and nanotubes have been successfully synthesized by templated electrodeposition within an anodic aluminium oxide membrane (AAM) using an aqueous precursor containing TiOSO 4. The deposition voltages were found to influence the resultant nanostructure of TiO2. Using a precursor of aqueous TiOSO4 at pH 3 maintained at 10 °C, TiO2 nanorods were electrodeposited in the AAM between applied voltages of - 1.4 V to - 1.0 V (vs. Ag/AgCl), while TiO2 nanotubes were obtained at less negative voltages of - 1.0 V to - 0.3 V (vs. Ag/AgCl). Cyclic voltammetry (CV) revealed that nitrate reduction in the voltage range of - 0.3 V to - 1.4 V played an essential role in the formation of TiO2. The mechanism for TiO2 nanotube formation has been elucidated, paving the way for the future tailoring of metal oxide nanostructures by templated electrodeposition. © 2014 Elsevier B.V.

  14. Degradação fotocatalítica de tartrazina com TiO2 imobilizado em esferas de alginato

    Directory of Open Access Journals (Sweden)

    Ithiara Dalponte

    Full Text Available The potential of heterogeneous photocatalysis using TiO2 immobilized in alginate beads was evaluated for the degradation of tartrazine yellow azo dye. The treatment was performed under the action of a high-pressure mercury vapor lamp of 125 W and the degradation performance was investigated with the absorbance supplied by a photocolorimeter. Alginate beads with TiO2 were prepared and the catalyst was quantified by thermogravimetric analysis (TG and characterized by scanning electron microscopy (SEM with energy-dispersive X-ray spectroscopy (EDS and specific area analysis (BET. The immobilization was performed as a very simple and reproductible technique. The bead diameter was approximately 1 mm and its surface presented a homogeneous dispersion of catalytic sites containing about 1-2% (w/w of TiO2. The TiO2/alginate beads presented low density and can be easier separated than the TiO2 dispersed from the reacting medium, remaining available to be reused in another batch. The dye degradation reached 30% after 120 minutes of irradiation, for the following conditions: alcaline pH (pH=9.0, 3 g of TiO2/alginate beads and 20 mol L-1 dye concentration.

  15. Zirconium phosphate waste forms for low-temperature stabilization of cesium-137-containing waste streams

    International Nuclear Information System (INIS)

    Singh, D.; Wagh, A.S.; Tlustochowicz.

    1996-04-01

    Novel chemically bonded phosphate ceramics are being developed and fabricated for low-temperature stabilization and solidification of waste streams that are not amenable to conventional high-temperature stabilization processes because volatiles are present in the wastes. A composite of zirconium-magnesium phosphate has been developed and shown to stabilize ash waste contaminated with a radioactive surrogate of 137 Cs. Excellent retainment of cesium in the phosphate matrix system was observed in Toxicity Characteristic Leaching Procedure tests. This was attributed to the capture of cesium in the layered zirconium phosphate structure by intercalation ion-exchange reaction. But because zirconium phosphate has low strength, a novel zirconium/magnesium phosphate composite waste form system was developed. The performance of these final waste forms, as indicated by compression strength and durability in aqueous environments, satisfy the regulatory criteria. Test results indicate that zirconium-magnesium-phosphate-based final waste forms present a viable technology for treatment and solidification of cesium-contaminated wastes

  16. Oxidative desulfurization of thiophene on TiO2/ZSM-12 zeolite

    OpenAIRE

    Santos,Marília Ramalho Figueiredo dos; Pedrosa,Anne Michelle Garrido; Souza,Marcelo José Barros de

    2016-01-01

    In this work the hydrothermal synthesis of ZSM-12 zeolite was performed, varying the MTEACl/SiO2 ratio, where the synthesis temperature was 140 ºC and the crystallization time was 144 hours. The catalysts were characterized by XRD, FTIR and TG. TiO2/ZSM-12 catalysts were used with titanium ions concentrations of 5, 10 and 15%. The oxidative desulfurization (ODS) reactions were performed using a model mixture containing n-heptane as solvent and thiophene as sulfur compound, H2O2 as an oxidizin...

  17. Photocorrosion Mechanism of TiO2-Coated Photoanodes

    Directory of Open Access Journals (Sweden)

    Arjen Didden

    2015-01-01

    Full Text Available Atomic layer deposition was used to coat CdS photoanodes with 7 nm thick TiO2 films to protect them from photocorrosion during photoelectrochemical water splitting. Photoelectrochemical measurements indicate that the TiO2 coating does not provide full protection against photocorrosion. The degradation of the film initiates from small pinholes and shows oscillatory behavior that can be explained by an Avrami-type model for photocorrosion that is halfway between 2D and 3D etching. XPS analysis of corroded films indicates that a thin layer of CdS remains present on the surface of the corroded photoanode that is more resilient towards photocorrosion.

  18. Application of TIO2 as A sorbent for radioactive waste

    International Nuclear Information System (INIS)

    Zamroni, H.; Las, T.; Kamarz, H.

    1997-01-01

    The sorption properties of the neodymium has been studied by using TiO 2 sorbent. The experiment was carried out by batch methods to investigate the kinetic sorption, effect of pH and effect of NaNO 3 concentration in the solution. Neodymium uses for a model of trivalent actinide treated by TiO 2 which was known as materials having high thermal and radiation stabilities as well as potentially used for immobilization of waste with cement or vitrification. the results show that the optimum of kinetic sorption was obtained after one day experiment to reach the equilibrium in sorption on pH 4, and the increasing of NaNO 3 concentrations will increase the sorption of neodymium in solution (author)

  19. The structure, composition, and dimensions of TiO2 and ZnO nanomaterials in commercial sunscreens

    Science.gov (United States)

    Lewicka, Zuzanna A.; Benedetto, Angelo F.; Benoit, Denise N.; Yu, William W.; Fortner, John D.; Colvin, Vicki L.

    2011-09-01

    TiO2 and ZnO nanomaterials are widely used to block ultraviolet radiation in many skin care products, yet product labels do not specify their dimensions, shape, or composition. The absence of this basic information creates a data gap for both researchers and consumers alike. Here, we investigate the structural similarity of pigments derived from actual sunscreen products to nanocrystals which have been the subject of intense scrutiny in the nanotoxicity literature. TiO2 and ZnO particles were isolated from eight out of nine commercial suncare products using three extraction methods. Their dimension, shape, crystal phase, surface area, and elemental composition were examined using transmission and scanning electron microscopy, X-ray diffraction, Brunauer-Emmett-Teller (BET) specific surface area analysis, energy dispersive X-ray and inductively coupled plasma optical emission spectroscopy. TiO2 pigments were generally rutile nanocrystals (dimensions 25 nm) with needle-like or near-spherical shapes. ZnO pigments were wurtzite rods with a short axes less than 40 nm and longer dimensions often in excess of 100 nm. We identify two commercial sources of TiO2 and ZnO nanocrystals whose physical and chemical features are similar to the pigments found in sunscreens. These particular materials would be effective surrogates for the commercial product and could be used in studies of the health and environmental impacts of engineered nanomaterials contained in sunscreens.

  20. The structure, composition, and dimensions of TiO2 and ZnO nanomaterials in commercial sunscreens

    International Nuclear Information System (INIS)

    Lewicka, Zuzanna A.; Benedetto, Angelo F.; Benoit, Denise N.; Yu, William W.; Fortner, John D.; Colvin, Vicki L.

    2011-01-01

    TiO 2 and ZnO nanomaterials are widely used to block ultraviolet radiation in many skin care products, yet product labels do not specify their dimensions, shape, or composition. The absence of this basic information creates a data gap for both researchers and consumers alike. Here, we investigate the structural similarity of pigments derived from actual sunscreen products to nanocrystals which have been the subject of intense scrutiny in the nanotoxicity literature. TiO 2 and ZnO particles were isolated from eight out of nine commercial suncare products using three extraction methods. Their dimension, shape, crystal phase, surface area, and elemental composition were examined using transmission and scanning electron microscopy, X-ray diffraction, Brunauer–Emmett–Teller (BET) specific surface area analysis, energy dispersive X-ray and inductively coupled plasma optical emission spectroscopy. TiO 2 pigments were generally rutile nanocrystals (dimensions ∼25 nm) with needle-like or near-spherical shapes. ZnO pigments were wurtzite rods with a short axes less than 40 nm and longer dimensions often in excess of 100 nm. We identify two commercial sources of TiO 2 and ZnO nanocrystals whose physical and chemical features are similar to the pigments found in sunscreens. These particular materials would be effective surrogates for the commercial product and could be used in studies of the health and environmental impacts of engineered nanomaterials contained in sunscreens.

  1. Relationship between nano/micro structure and physical properties of TiO2-sodium caseinate composite films.

    Science.gov (United States)

    Montes-de-Oca-Ávalos, Juan Manuel; Altamura, Davide; Candal, Roberto Jorge; Scattarella, Francesco; Siliqi, Dritan; Giannini, Cinzia; Herrera, María Lidia

    2018-03-01

    Films obtained by casting, starting from conventional emulsions (CE), nanoemulsions (NE) or their gels, which led to different structures, with the aim of explore the relationship between structure and physical properties, were prepared. Sodium caseinate was used as the matrix, glycerol as plasticizer, glucono-delta-lactone as acidulant to form the gels, and TiO 2 nanoparticles as reinforcement to improve physical behavior. Structural characterization was performed by SAXS and WAXS (Small and Wide Angle X-ray Scattering, respectively), combined with confocal and scanning electron microscopy. The results demonstrate that the incorporation of the lipid phase does not notably modify the mechanical properties of the films compared to solution films. Films from NE were more stable against oil release than those from CE. Incorporation of TiO 2 improved mechanical properties as measured by dynamical mechanical analysis (DMA) and uniaxial tensile tests. TiO 2 macroscopic spatial distribution homogeneity and the nanostructure character of NE films were confirmed by mapping the q-dependent scattering intensity in scanning SAXS experiments. SAXS microscopies indicated a higher intrinsic homogeneity of NE films compared to CE films, independently of the TiO 2 load. NE-films containing structures with smaller and more homogeneously distributed building blocks showed greater potential for food applications than the films prepared from sodium caseinate solutions, which are the best known films. Copyright © 2017 Elsevier Ltd. All rights reserved.

  2. TiO2/ZnS/CdS Nanocomposite for Hydrogen Evolution and Orange II Dye Degradation

    Directory of Open Access Journals (Sweden)

    Václav Štengl

    2011-01-01

    Full Text Available TiO2/ZnS/CdS composites for photocatalytic hydrogen production from water were prepared by homogeneous hydrolysis of aqueous solutions mixture of TiOSO4, ZnSO4, and CdSO4 with thioacetamide. Hydrogen evolution was observed in the presence of palladium and platinum nanoparticles deposited on TiO2/ZnS/CdS composites. The morphology was obtained by scanning electron microscopy, the nitrogen adsorption-desorption was used for determination of surface area (BET and porosity. The method of UV-VIS diffuse reflectance spectroscopy was employed to estimate band-gap energies of prepared TiO2/ZnS/CdS nano-composites. The photocatalytic activity of the prepared samples were assessed by photocatalytic decomposition of Orange II dye in an aqueous slurry under UV irradiation at 365 nm wavelength and visible light up to 400 nm wavelength. Doped titanium dioxide by the CdS increased band-gap energy and doping with ZnS increased photocatalytic activity. The best photocatalytic activity for H2 evolution shows sample named TiZnCd7 on surface deposited with palladium, which contains 20.21% TiO2, 78.5% ZnS, and 1.29% CdS.

  3. H2O-EG-assisted synthesis of uniform urchinlike rutile TiO2 with superior lithium storage properties.

    Science.gov (United States)

    Chen, Jun Song; Liang, Yen Nan; Li, Yongmei; Yan, Qingyu; Hu, Xiao

    2013-10-23

    A facile green method to synthesize uniform nanostructured urchinlike rutile TiO2 is demonstrated. Titanium trichloride was selected as the TiO2 precursor, and a mixed solvent containing H2O and ethylene glycol was used. By using this binary medium, the nucleation and crystal growth of rutile TiO2 can be regulated, giving rise to very uniform urchinlike structures with tailorable sizes. As confirmed by the SEM and TEM analysis, large particles with dense aggregation of needle-like building blocks or small ones with loosely packed subunits could be obtained at different reaction conditions. The as-prepared samples were applied as the anode material for lithium-ion batteries, and they were shown to have superior properties with a high reversible capacity of 140 mA h g(-1) at a high current rate of 10 C for up to 300 cycles, which is almost unmatched by other rutile TiO2-based electrodes. A stable capacity of 88 mA h g(-1) can also be delivered at an extremely high rate of 50 C, suggesting the great potential of the as-prepared product for high-rate lithium-ion batteries.

  4. Preparation and in vitro evaluation of nanostructured TiO2/TCP composite coating by plasma electrolytic oxidation

    International Nuclear Information System (INIS)

    Hu, Hongjie; Liu, Xuanyong; Ding, Chuanxian

    2010-01-01

    Porous and nanostructured TiO 2 /tricalcium phosphate (TCP) composite coating on titanium substrate was prepared by plasma electrolytic oxidation (PEO). The microstructure and phase composition of the coating were characterized using scanning electron microscopy and X-ray diffraction. Its bioactivity was evaluated by simulated body fluid (SBF) immersion tests. MG63 cells were cultured on the surface of the coating to investigate its cytocompatibility. Potentiodynamic polarization tests were applied to measure its corrosion resistance. The results revealed that rough and hydrophilic TiO 2 /TCP composite coating with pores of several micrometers and grains of 50-200 nm was prepared by one-step PEO treatment. The TiO 2 /TCP composite coating showed good apatite-forming ability in SBF, and the TCP phase in the coating played an important role in inducing apatite formation. MG63 cells could adhere and proliferate on the surface of the coating, indicating its good cytocompatibility. The composite coating also exhibited good corrosion resistance in 0.9% NaCl solution.

  5. TiO2 and SiC nanostructured films, organized CNT structures

    Indian Academy of Sciences (India)

    sized nanostructured TiO2 films through hydrolysis of titanium tetra-isopropoxide. (TTIP) [9 ... structured TiO2 as a photocatalyst is as follows [15]:. TiO2(ns) ... The deposited films were easily detached from the silica tube and subjected to. SEM.

  6. Dye-Sensitized Solar Cells with Anatase TiO2 Nanorods Prepared by Hydrothermal Method

    Directory of Open Access Journals (Sweden)

    Ming-Jer Jeng

    2013-01-01

    Full Text Available The hydrothermal method provides an effective reaction environment for the synthesis of nanocrystalline materials with high purity and well-controlled crystallinity. In this work, we started with various sizes of commercial TiO2 powders and used the hydrothermal method to prepare TiO2 thin films. We found that the synthesized TiO2 nanorods were thin and long when smaller TiO2 particles were used, while larger TiO2 particles produced thicker and shorter nanorods. We also found that TiO2 films prepared by TiO2 nanorods exhibited larger surface roughness than those prepared by the commercial TiO2 particles. It was found that a pure anatase phase of TiO2 nanorods can be obtained from the hydrothermal method. The dye-sensitized solar cells fabricated with TiO2 nanorods exhibited a higher solar efficiency than those fabricated with commercial TiO2 nanoparticles directly. Further, triple-layer structures of TiO2 thin films with different particle sizes were investigated to improve the solar efficiency.

  7. Enhanced Bonding of Silver Nanoparticles on Oxidized TiO2(110)

    DEFF Research Database (Denmark)

    Hansen, Jonas Ørbæk; Salazar, Estephania Lira; Galliker, Patrick

    2010-01-01

    The nucleation and growth of silver nanoclusters on TiO2(110) surfaces with on-top O adatoms (oxidized TiO2), surface O vacancies and H adatoms (reduced TiO2) have been studied. From the interplay of scanning tunneling microscopy/photoelectron spectroscopy experiments and density functional theor...

  8. Effect of surface Fe2O3 clusters on the photocatalytic activity of TiO2 for phenol degradation in water

    International Nuclear Information System (INIS)

    Sun, Qiong; Leng, Wenhua; Li, Zhen; Xu, Yiming

    2012-01-01

    Graphical abstract: Surface modified TiO 2 with iron oxide clusters through adsorption and decomposition of a large Fe(III) complex shows an enhanced activity for phenol degradation in water under UV light. But it was only observed with the clusters in a small size and at very low coverage on anatase. Highlights: ► Iron oxide clusters are made by decomposition of a large Fe(III) complex on TiO 2 . ► The modified anatase shows an enhanced activity for phenol photodegradation. ► The composite catalyst is very stable during four repeated experiments. - Abstract: Surface modification of TiO 2 with Fe 2 O 3 clusters was made through chemisorption of ferric phthalocyaninetetracarboxylate onto TiO 2 , followed by sintering in air to remove organic moiety. Solid characterization with electron paramagnetic resonance spectroscopy and other techniques showed that ferric oxides were highly dispersed on TiO 2 as a noncrystallized cluster, while TiO 2 phases remained unchanged. For phenol degradation in aerated aqueous suspension, only the sample containing less than 0.3 at.% Fe was more active than bare TiO 2 under UV light, whereas no activity was found under visible light. As anatase thermally transferred into rutile, the Fe-containing catalyst became less active than bare TiO 2 , mainly ascribed to the increased size of Fe 2 O 3 clusters. In the presence of H 2 O 2 , all Fe-containing catalysts were more active than bare TiO 2 . Moreover, similar trend in activity among different catalysts was also observed with the formation of hydroxyl radicals, and with the generation of photocurrent measured under N 2 with Fe/TiO 2 electrode. Present work clearly shows that only Fe 2 O 3 clusters in a small size and at low coverage on TiO 2 are beneficial to the photocatalytic reaction, while excess iron oxide is detrimental. Possible mechanism is discussed in the text.

  9. Photocatalytic Water Treatment on TiO2 Thin Layers.

    Czech Academy of Sciences Publication Activity Database

    Šolcová, Olga; Spáčilová, L.; Maléterová, Ywetta; Morozová, Magdalena; Ezechiáš, Martin; Křesinová, Zdena

    2016-01-01

    Roč. 57, č. 25 (2016), s. 11631-11638 ISSN 1944-3994. [International Conference on Protection and Restoration of the Environment /12./. Skiathos Island, 29.06.2014-03.07.2014] R&D Projects: GA TA ČR TA01020804 Institutional support: RVO:67985858 ; RVO:61388971 Keywords : water purification * endocrine disruptor * photocatalytic * TiO2 layers Subject RIV: CI - Industrial Chemistry, Chemical Engineering; EE - Microbiology, Virology (MBU-M) Impact factor: 1.631, year: 2016

  10. TiO(2)-graphene nanocomposite as high performace photocatalysts

    Czech Academy of Sciences Publication Activity Database

    Štengl, Václav; Popelková, Daniela; Vláčil, P.

    2011-01-01

    Roč. 115, č. 51 (2011), s. 25209-25218 ISSN 1932-7447 R&D Projects: GA MPO(CZ) FI-IM3/061; GA MPO FI-IM5/239 Institutional research plan: CEZ:AV0Z40320502 Keywords : titanium-dioxide * visible-light * doped TiO2 * degradation * graphene * oxide Subject RIV: CA - Inorganic Chemistry Impact factor: 4.805, year: 2011

  11. Defects improved photocatalytic ability of TiO2

    International Nuclear Information System (INIS)

    Li, Lei; Tian, Hong-Wei; Meng, Fan-Ling; Hu, Xiao-Ying; Zheng, Wei-Tao; Sun, Chang Q.

    2014-01-01

    Highlights: • Defect improves the photocatalytic ability by band gap narrowing and carrier life prolonging. • Atomic undercoordination shortens the local bonds, entraps, and polarizes electrons. • Polarization lowers the local workfunction and lengthens carrier life. • Entrapment and polarization narrows the band gap tuning the wavelength of absorption. - Abstract: Defect generation forms an important means modulating the photocatalytic ability of TiO 2 with mechanisms that remain yet unclear. Here we show that a spectral distillation clarifies the impact of defect on modulating the band gap, electroaffinity, and work function of the substance. Firstly, by analyzing XPS measurements, we calibrated the 2p 3/2 level of 451.47 eV for an isolated Ti atom and its shifts by 2.14 and 6.94 eV, respectively, upon Ti and TiO 2 bulk formation. Spectral difference between the defected and the un-defected TiO 2 skin revealed then that the 2p 3/2 level shifts further from 6.94 to 9.67 eV due to the defect-induced quantum entrapment. This entrapment is associated with an elevation of the upper edges of both the 2p 3/2 and the conduction band by polarization. The shortening and strengthening of bonds between undercoordinated atoms densify and entrap the core electrons, which in turn polarize the dangling bond electrons of defect atoms. The entrapment and polarization mediate thus the band gap, the electroaffinity, the work function, and the photocatalytic ability of TiO 2

  12. Versatile preparation method for mesoporous TiO2 electrodes ...

    Indian Academy of Sciences (India)

    Unknown

    cyanate into CuI layer further enhanced the efficiency up to 2⋅75% under the irradiance .... an extremely easy way to dope films with virtually any .... to see the effect of ionic liquid on CuI, 1-ethyl-3-methyl- ... This analysis showed that TiO2 electrodes were polycrys- .... thin insulating layer of Al2O3 by using dip-coating meth-.

  13. Drug loading of nanoporous TiO2 films

    International Nuclear Information System (INIS)

    Ayon, Arturo A; Cantu, Michael; Chava, Kalpana; Agrawal, C Mauli; Feldman, Marc D; Johnson, Dave; Patel, Devang; Marton, Denes; Shi, Emily

    2006-01-01

    The loading of therapeutic amounts of drug on a nanoporous TiO 2 surface is described. This novel drug-loading scheme on a biocompatible surface, when employed on medical implants, will benefit patients who require the deployment of drug-eluting implants. Anticoagulants, analgesics and antibiotics can be considered on the associated implants for drug delivery during the time of maximal pain or risk for patients undergoing orthopedic procedures. Therefore, this scheme will maximize the chances of patient recovery. (communication)

  14. Lattice defects in rutile, TiO2

    International Nuclear Information System (INIS)

    Nakagawa, M.; Itoh, H.; Nakanishi, S.; Kondo, K.; Okada, M.; Atobe, K.

    1991-01-01

    Rutile, TiO 2 , having a relatively high melting point exhibits strong optical absorption after neutron irradiation (8 x 10 16 n f /cm 2 ) at 15K. The band peak is located near 0.96 μ, having a FWHM of 0.87 eV (at liquid nitrogen temperature). After inverse recovery at 120K, lattice defects due probably to F centers are annealed out at about 220K. (author)

  15. Microporous TiO2-WO3/TiO2 films with visible-light photocatalytic activity synthesized by micro arc oxidation and DC magnetron sputtering

    International Nuclear Information System (INIS)

    Wu, Kee-Rong; Hung, Chung-Hsuang; Yeh, Chung-Wei; Wu, Jiing-Kae

    2012-01-01

    Highlights: ► A simple MAO is used to prepare porous WO 3 /TiO 2 layer on Ti sheet as a visible-light enabled catalyst. ► The photocatalytic activity of the WO 3 /TiO 2 is enhanced by sputtering over an N,C-TiO 2 layer. ► This is ascribed to the synergetic effect of hybrid sample prepared by two-step method. - Abstract: This study reports the preparation of microporous TiO 2 -WO 3 /TiO 2 films with a high surface area using a two-step approach. A porous WO 3 /TiO 2 template was synthesized by oxidizing a titanium sheet using a micro arc oxidation (MAO) process. This sheet was subsequently overlaid with a visible light (Vis)-enabled TiO 2 (N,C-TiO 2 ) film, which was deposited by codoping nitrogen (N) and carbon (C) ions into a TiO 2 lattice using direct current magnetron sputtering. The resulting microporous TiO 2 -WO 3 /TiO 2 film with a 0.38-μm-thick N,C-TiO 2 top-layer exhibited high photocatalytic activity in methylene blue (MB) degradation among samples under ultraviolet (UV) and Vis irradiation. This is attributable to the synergetic effect of two-step preparation method, which provides a highly porous microstructure and the well-crystallized N,C-TiO 2 top-layer. This is because a higher surface area with high crystallinity favors the adsorption of more MB molecules and more photocatalytic active areas. Thus, the microporous TiO 2 -WO 3 /TiO 2 film has promising applications in the photocatalytic degradation of dye solution under UV and Vis irradiation. These results imply that the microporous WO 3 /TiO 2 can be used as a template of hybrid electrode because it enables rapid fabrication.

  16. Sensing and electrical properties of TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Usman, M.

    2011-01-01

    The purpose of this work was to synthesize TiO 2 nanoparticles using Coprecipitation method. 2 different samples were synthesized, one with a modifier and other without using a modifier. After synthesis, newly formed nanoparticles were characterized b different techniques to find various properties of these nanoparticles. Scanning electron Microscopy (SEM) was used to study structure and morphology of Cu nanoparticles and for compositional analysis Energy dispersive spectroscopy (EDS) was used. X-Ray Diffraction (XRD) Studies were also carried out to find phase an average particle Size. To find the band gap of our nanoparticles, UV-Visible Spectroscopy was also done. Non-Modified nanoparticles were as small as 12nm reported by SEM images which were synthesized using a modifier were as small as 10nm. Modified TiO 2 nanoparticles were used in humidity sensing devices and it properties as a humidity sensor were examined by doing Impedance spectroscopy, D measurements and Dielectric measurements. Our TiO 2 humidity sensor showed sensitivity for humidity at low and mid-range frequencies while its response time was 4 seconds when we changed RH% to 90 from 40% and measured the impedance. (author)

  17. Incorporation of chromium into TiO2 nanopowders

    International Nuclear Information System (INIS)

    Kollbek, Kamila; Sikora, Marcin; Kapusta, Czesław; Szlachetko, Jakub; Radecka, Marta; Lyson-Sypien, Barbara; Zakrzewska, Katarzyna

    2015-01-01

    Highlights: • Nanopowders of TiO 2 :Cr with different amount of Cr dopant were obtained by flame spray synthesis, FSS. • Increase in the optical absorption and a shift of the absorption edge were observed upon Cr doping. • HERFD-XANES measurements indicated that the average valence state of titanium ions was preserved. • Increasing magnetic susceptibility of a paramagnetic character was observed upon Cr doping. - Abstract: The paper reports on the results of a study of optical, electronic and magnetic properties of TiO 2 nanopowders doped with Cr ions. Diffused reflectance spectra reveal an increase in the optical absorption and a shift of the absorption edge towards lower energies upon Cr doping. Direct information on the Ti electronic state and the symmetry of its nearest environment is obtained from XANES Ti K-edge spectra. Magnetic behaviour is probed by means of the temperature dependence of DC magnetic susceptibility. Increasing magnetic susceptibility of a paramagnetic character is observed upon increasing chromium doping. The Curie constant of TiO 2 :10 at.% Cr sample (0.12 emu K/mol Oe) is lower than that expected for Cr 3+ (0.1875 emu K/mol Oe) possibly due to the appearance of Cr 4+ or the presence of the orbital contribution to the magnetic moment

  18. Sol-gel synthesis of TiO2 nanoparticles and photocatalytic degradation of methyl orange in aqueous TiO2 suspensions

    International Nuclear Information System (INIS)

    Yang Huaming; Zhang Ke; Shi Rongrong; Li Xianwei; Dong Xiaodan; Yu Yongmei

    2006-01-01

    Anatase TiO 2 nanoparticles of about 16 nm in crystal size have been successfully synthesized via a sol-gel method. Thermal treatment of the precursor at 500-600 deg. C results in the formation of different TiO 2 phase compositions. The samples were characterized by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Effects of the pH value of the solution, H 2 O 2 addition, TiO 2 phase composition and recycled TiO 2 on the photocatalytic degradation of methyl orange (MeO) in TiO 2 suspensions under ultraviolet (UV) illumination were primarily investigated. The results indicate that a low pH value, proper amount of H 2 O 2 and pure anatase TiO 2 will facilitate the photocatalytic oxidation of the MeO solution. The photodegradation degree decreases with increasing the pH value of the solution and varies with different amounts of H 2 O 2 . Pure anatase TiO 2 shows better photocatalytic activity for MeO decolorization than biphase TiO 2 . The photocatalytic mechanism of the as-synthesized TiO 2 nanoparticles was discussed

  19. OXIDACIÓN DE p -NITROFENOL USANDO TiO 2 -ADENOSINA MONOFOSFATO I OXIDATION OF p -NITROPHENOL USING TiO 2 -ADENOSIN MONOPHOSPHATE

    Directory of Open Access Journals (Sweden)

    Carlos F. Rivas

    2018-04-01

    Full Text Available The surface of TiO2 was modified with the nucleotides adenosine 3’-monophosphate (AMP’3 and Adenosine 5’-monophosphate (AMP’5. The adsorption of nucleotides was adjusted to Langmuir ́s adsorption model, determining that the optimal condition for TiO 2 modification was at neutral pH. UV-Visible Diffuse Reflectance and IR Attenuated Total Reflectance spectra show that the chemisorption of nucleotides take placed on TiO 2 anatase. The new catalysts (TiO 2 -nucleotide improved the photodegradation of p -nitrophenol in a wide range of pH as compared with the titanium dioxide precursor. Most photoactivity was generated by using the new photocatalytic in the degradation of p -nitrophenol at pH = 6, obtaining high values for the pseudo first order kinetic constant (0.0254 min -1 and 0.0244 min -1 for TiO 2 -AMP’3 and TiO 2 -AMP’5, respectively. For all pH, the trend obtained for the photodegradation was: TiO 2 -AMP ́3 @ TiO 2 -AMP’5 > TiO 2 . Langmuir-Hinshelwood kinetics shows that the contribution of the surface reac tion rate governs the oxidation of the contaminant.

  20. Photocatalytic effects for the TiO2-coated phosphor materials

    International Nuclear Information System (INIS)

    Yoon, Jin-Ho; Jung, Sang-Chul; Kim, Jung-Sik

    2011-01-01

    Research highlights: → The photocatalytic behavior of the coupling of TiO 2 with phosphorescent materials. → The photobleaching of an MB aqueous solution under visible light irradiation. → The ALD TiO 2 -coated phosphor composite showed much higher photocatalytic reactivity. → The light emitted from the phosphors contributed to the photo-generation. - Abstract: This study investigated the photocatalytic behavior of the coupling of TiO 2 with phosphorescent materials. A TiO 2 thin film was deposited on CaAl 2 O 4 :Eu 2+ ,Nd 3+ phosphor particles by using atomic layer deposition (ALD), and its photocatalytic reaction was investigated by the photobleaching of an aqueous solution of methylene-blue (MB) under visible light irradiation. To clarify the mechanism of the TiO 2 -phosphorescent materials, two different samples of TiO 2 -coated phosphor and TiO 2 -Al 2 O 3 -coated phosphor particles were prepared. The photocatalytic mechanisms of the ALD TiO 2 -coated phosphor powders were different from those of the pure TiO 2 and TiO 2 -Al 2 O 3 -coated phosphor. The absorbance in a solution of the ALD TiO 2 -coated phosphor decreased much faster than that of pure TiO 2 under visible irradiation. In addition, the ALD TiO 2 -coated phosphor showed moderately higher photocatalytic degradation of MB solution than the TiO 2 -Al 2 O 3 -coated phosphor did. The TiO 2 -coated phosphorescent materials were characterized by transmission electron microscopy (TEM), Auger electron spectroscopy (AES) and X-ray photon spectroscopy (XPS).

  1. Synthesis of nanostructured TiO2 (anatase) and TiO2(B) in ionic liquids

    Czech Academy of Sciences Publication Activity Database

    Mansfeldová, Věra; Lásková, Barbora; Krýsová, Hana; Zukalová, Markéta; Kavan, Ladislav

    2014-01-01

    Roč. 230, JUL 2014 (2014), s. 85-90 ISSN 0920-5861 R&D Projects: GA ČR GA13-07724S; GA MŠk 7E09117 Grant - others:European Commission(XE) NMP-229036 Institutional support: RVO:61388955 Keywords : TiO2(B) * ionic liquid * electrochemistry Subject RIV: CG - Electrochemistry Impact factor: 3.893, year: 2014

  2. Graphene-spindle shaped TiO2 mesocrystal composites: Facile synthesis and enhanced visible light photocatalytic performance

    International Nuclear Information System (INIS)

    Yang, Xiaofei; Qin, Jieling; Li, Yang; Zhang, Rongxian; Tang, Hua

    2013-01-01

    Highlights: • Graphene-TiO 2 mesocrystal composites were fabricated via a facile approach. • Graphene sheets were decorated with spindle-like TiO 2 mesocrystals. • Graphene causes enhanced light absorbance and visible light photocatalytic activity. • Oxygen-containing radicals are believed to responsible for its improved activity. -- Abstract: Graphene (GR)-TiO 2 mesocrystal composites were prepared by a facile template-free process based on the combination of sol–gel and solvothermal methods, and were characterized using field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), Raman spectroscopy, UV–vis diffuse reflectance spectroscopy (UV–vis DRS), nitrogen absorption and electron spin resonance (ESR). Visible light photocatalytic performance of GR-TiO 2 composites was evaluated for photocatalytic degradation of organic dye Rhodamine B. It was found that the amount of graphene oxide (GO) added obviously affects morphologies of TiO 2 mesocrystals and photocatalytic activities of as-prepared nanocomposites. Composites prepared in the presence of different amounts of GO all exhibit higher photocatalytic activity than pure TiO 2 mesocrystals and P25, the composite obtained by using 20 mg GO presents the most uniform TiO 2 mesocrystals in the composite and shows the highest photocatalytic efficiency. The mechanism for the generation of TiO 2 mesocrystals in the GR-TiO 2 composite is proposed and possible reasons for the enhancement in visible light photocatalytic efficiency are also discussed

  3. Bulk solubility and speciation of plutonium(VI) in phosphate-containing solutions

    International Nuclear Information System (INIS)

    Weger, H.T.; Okajima, S.; Cunnane, J.C.; Reed, D.T.

    1992-01-01

    The solubility and speciation of Pu(VI) with phosphate as a function of pH was investigated to determine the ability of phosphate to act as an actinide getter. The general properties were first investigated and are reported here with the goal of performing more quantitative experiments in the future. Solubility was approached from oversaturation at initial pH = 4, 10 and 13.4. Absorption spectra were recorded, the solution filtered and the filtrate counted. Absorption spectra were obtained at varying phosphate concentrations and at pH of 2.7 to 11.9. The effect of complexation on the 833 mn Pu(VI) band was characterized. Evidence for three phosphate complexes was obtained for pH -5 to 10 -6 M Pu(VI) was measured in the filtrate at pH ≤ 10 that were passed through a 50 mn filter. Pu(VI) complexes with phosphate over hydroxide at pH ≤ 11.6, but at pH ≥ 11.9, only hydrolyzed Pu(VI) was detected. At pH = 12, the concentration of Pu(VI) was as high as 10 -4 M

  4. Are TiO2 nanotubes worth using in photocatalytic purification of air and water?

    Science.gov (United States)

    Pichat, Pierre

    2014-09-19

    Titanium dioxide nanotubes (TNT) have mainly been used in dye sensitized solar cells, essentially because of a higher transport rate of electrons from the adsorbed photo-excited dye to the Ti electrode onto which TNT instead of TiO2 nanoparticles (TNP) are attached. The dimension ranges and the two main synthesis methods of TNT are briefly indicated here. Not surprisingly, the particular and regular texture of TNT was also expected to improve the photocatalytic efficacy for pollutant removal in air and water with respect to TNP. In this short review, the validity of this expectation is checked using the regrettably small number of literature comparisons between TNT and commercialized TNP referring to films of similar thickness and layers or slurries containing an equal TiO2 mass. Although the irradiated geometrical area differed for each study, it was identical for each comparison considered here. For the removal of toluene (methylbenzene) or acetaldehyde (ethanal) in air, the average ratio of the efficacy of TNT over that of TiO2 P25 was about 1.5, and for the removal of dyes in water, it was around 1. This lack of major improvement with TNT compared to TNP could partially be due to TNT texture disorders as seems to be suggested by the better average performance of anodic oxidation-prepared TNT. It could also come from the fact that the properties influencing the efficacy are more numerous, their interrelations more complex and their effects more important for pollutant removal than for dye sensitized solar cells and photoelectrocatalysis where the electron transport rate is the crucial parameter.

  5. Thermal catalytic oxidation of octachloronaphthalene over anatase TiO2 nanomaterial and its hypothesized mechanism

    Science.gov (United States)

    Su, Guijin; Li, Qianqian; Lu, Huijie; Zhang, Lixia; Huang, Linyan; Yan, Li; Zheng, Minghui

    2015-12-01

    As an environmentally-green technology, thermal catalytic oxidation of octachloronaphthalene (CN-75) over anatase TiO2 nanomaterials was investigated at 300 °C. A wide range of oxidation intermediates, which were investigated using various techniques, could be of three types: naphthalene-ring, single-benzene-ring, and completely ring-opened products. Reactive oxygen species on anatase TiO2 surface, such as O2-• and O2-, contributed to oxidative degradation. Based on these findings, a novel oxidation degradation mechanism was proposed. The reaction at (101) surface of anatase TiO2 was used as a model. The naphthalene-ring oxidative products with chloronaphthols and hydroxyl-pentachloronaphthalene-dione, could be formed via attacking the carbon of naphthalene ring at one or more positions by nucleophilic O2-. Lateral cleavage of the naphthalene ring at different C1-C10 and C4-C9, C1-C2 and C4-C9, C1-C2 or and C3-C4 bond positions by electrophilic O2-• could occur. This will lead to the formation of tetrachlorophenol, tetrachloro-benzoic acid, tetrachloro-phthalaldehyde, and tetrachloro-acrolein-benzoic acid, partially with further transformation into tetrachlorobenzene-dihydrodiol and tetrachloro-salicylic acid. Unexpectedly, the symmetric half section of CN-75 could be completely remained with generating the intricate oxidative intermediates characteristically containing tetrachlorobenzene structure. Complete cleavage of naphthalene ring could produce the ring-opened products, such as formic and acetic acids.

  6. Synergistic effects between TiO2 and carbon nanotubes (CNTs) in a TiO2/CNTs system under visible light irradiation.

    Science.gov (United States)

    Wu, Chung-Hsin; Kuo, Chao-Yin; Chen, Shih-Ting

    2013-01-01

    This study synthesized a TiO2/carbon nanotubes (CNTs) composite via the sol-gel method. The surface characteristics of the TiO2/CNTs composite were determined by X-ray diffraction, transmission electron microscopy, specific surface area analyser, ultraviolent (UV)-vis spectroscopy, X-ray photoelectron spectroscopy and Raman spectrometer. The photocatalytic activity ofthe TiO2/CNTs composite was evaluated by decolourizing C.I. Reactive Red 2 (RR2) under visible light irradiation. Furthermore, the effects of calcination temperature, pH, RR2 concentration, and the TiO2/CNTs composite dosage on RR2 decolourization were determined simultaneously. The optimal calcination temperature to generate TiO2 and the TiO2/CNTs composite was 673 K, as the percentage of anatase crystallization at this temperature was highest. The specific surface area of the TiO2/CNTs composite and TiO2 were 45 and 42 m2/g, respectively. The band gap of TiO2 and the TiO2/CNTs composite was 2.97 and 2.71 eV by UV-vis measurements, respectively. Experimental data indicate that the Ti-O-C bond formed in the TiO2/CNTs composite. The RR2 decolourization rates can be approximated by pseudo-first-order kinetics; moreover, only the TiO2/CNTs composite had photocatalytic activity under visible light irradiation. At pH 7, the RR2 decolourization rate constant of 0.5, 1 and 2 g/L TiO2/CNTs addition was 0.005, 0.0015, and 0.0047 min(-1), respectively. Decolourization rate increased as pH and the RR2 concentration decreased. The CNTs functioned as electron acceptors, promoting separation of photoinduced electron-hole pairs to retard their recombination; thus, photocatalytic activity of the TiO2/CNTs composite exceeded that of TiO2.

  7. High pressure structural phase transitions of TiO2 nanomaterials

    International Nuclear Information System (INIS)

    Li Quan-Jun; Liu Bing-Bing

    2016-01-01

    Recently, the high pressure study on the TiO 2 nanomaterials has attracted considerable attention due to the typical crystal structure and the fascinating properties of TiO 2 with nanoscale sizes. In this paper, we briefly review the recent progress in the high pressure phase transitions of TiO 2 nanomaterials. We discuss the size effects and morphology effects on the high pressure phase transitions of TiO 2 nanomaterials with different particle sizes, morphologies, and microstructures. Several typical pressure-induced structural phase transitions in TiO 2 nanomaterials are presented, including size-dependent phase transition selectivity in nanoparticles, morphology-tuned phase transition in nanowires, nanosheets, and nanoporous materials, and pressure-induced amorphization (PIA) and polyamorphism in ultrafine nanoparticles and TiO 2 -B nanoribbons. Various TiO 2 nanostructural materials with high pressure structures are prepared successfully by high pressure treatment of the corresponding crystal nanomaterials, such as amorphous TiO 2 nanoribbons, α -PbO 2 -type TiO 2 nanowires, nanosheets, and nanoporous materials. These studies suggest that the high pressure phase transitions of TiO 2 nanomaterials depend on the nanosize, morphology, interface energy, and microstructure. The diversity of high pressure behaviors of TiO 2 nanomaterials provides a new insight into the properties of nanomaterials, and paves a way for preparing new nanomaterials with novel high pressure structures and properties for various applications. (topical review)

  8. Low temperature fabrication of perovskite solar cells with TiO2 nanoparticle layers

    International Nuclear Information System (INIS)

    Kanayama, Masato; Oku, Takeo; Suzuki, Atsushi; Yamada, Masahiro; Sakamoto, Hiroki; Minami, Satoshi; Kohno, Kazufumi

    2016-01-01

    TiO 2 /CH 3 NH 3 PbI 3 -based photovoltaic devices were fabricated by a spin-coating method using a mixture solution. TiO 2 require high-temperature processing to achieve suitably high carrier mobility. TiO 2 electron transport layers and TiO 2 scaffold layers for the perovskite were fabricated from TiO 2 nanoparticles with different grain sizes. The photovoltaic properties and microstructures of solar cells were characterized. Nanoparticle sizes of these TiO 2 were 23 nm and 3 nm and the performance of solar cells was improved by combination of two TiO 2 nanoparticles

  9. Photocatalytic decouloration of malachite green dye by application of TiO2 nanotubes

    International Nuclear Information System (INIS)

    Prado, Alexandre G.S.; Costa, Leonardo L.

    2009-01-01

    The nanotubes of titania were synthesized in a hydrothermal system and characterized by scanning electronic microscopy (SEM), FT-IR, FT-Raman, and surface charge density by surface area analyzer. These nanomaterials were applied to photocatalyse malachite green dye degradation. Photodegradation capacity of TiO 2 nanotubes was compared to TiO 2 anatase photoactivity. Malachite dye was completely degraded in 75 and 105 min of reaction photocatalysed by TiO 2 nanotubes and TiO 2 anatase, respectively. Catalysts displayed high photodegradation activity at pH 4. TiO 2 nanotubes were easily recycled whereas the reuse of TiO 2 anatase was not effective. Nanotubes maintained 80% of their activity after 10 catalytic cycles and TiO 2 anatase presented only 8% of its activity after 10 cycles.

  10. First-principles atomistic Wulff constructions for an equilibrium rutile TiO2 shape modeling

    Science.gov (United States)

    Jiang, Fengzhou; Yang, Lei; Zhou, Dali; He, Gang; Zhou, Jiabei; Wang, Fanhou; Chen, Zhi-Gang

    2018-04-01

    Identifying the exposed surfaces of rutile TiO2 crystal is crucial for its industry application and surface engineering. In this study, the shape of the rutile TiO2 was constructed by applying equilibrium thermodynamics of TiO2 crystals via first-principles density functional theory (DFT) and Wulff principles. From the DFT calculations, the surface energies of six low-index stoichiometric facets of TiO2 are determined after the calibrations of crystal structure. And then, combined surface energy calculations and Wulff principles, a geometric model of equilibrium rutile TiO2 is built up, which is coherent with the typical morphology of fully-developed equilibrium TiO2 crystal. This study provides fundamental theoretical guidance for the surface analysis and surface modification of the rutile TiO2-based materials from experimental research to industry manufacturing.

  11. Composition of Surface Adsorbed Layer of TiO2 Stored in Ambient Air

    Directory of Open Access Journals (Sweden)

    Zakharenko V.S.

    2017-11-01

    Full Text Available The processes of dark, UV, and visible light promoted desorption of surface species were investigated for three different TiO2 samples: TiO2 prepared by dispersion of the titania single crystal, TiO2 prepared by combustion of a pyrotechnic mixture in air, and commercial TiO2 P25. The composition of the adsorbed layer was identified in the dark and under UV and visible light irradiation. The composition of desorption products showed the dependence of the adsorption layer state on the TiO2 nature. Methane photodesorption was detected only for the commercial TiO2 P25. Possible reasons for methane emission include the capturing of complete molecules during the TiO2 production process and photocatalytic hydrogenation of CO2 under UV-light.

  12. Immobilization of TiO2 nanoparticles on Fe-filled carbon nanocapsules for photocatalytic applications

    International Nuclear Information System (INIS)

    Huang, H.-C.; Huang, G.-L.; Chen, H.-L.; Lee, Y.-D.

    2006-01-01

    Using a simple sol-gel method, a novel magnetic photocatalyst was produced by immobilization of TiO 2 nano-crystal on Fe-filled carbon nanocapsules (Fe-CNC). High resolution TEM images indicated that the immobilization of TiO 2 on Fe-CNC was driven primarily by heterogeneous coagulation, whereas surface nucleation and growth was the dominant mechanism for immobilizing TiO 2 on acid-functionalized hollow CNC. The TiO 2 immobilized on Fe-CNC exhibited the anatase phase as revealed by the X-ray diffraction (XRD) patterns. In comparison with free TiO 2 and TiO 2 -coated CNC, TiO 2 -coated Fe-CNC displayed good performance in the removal of NO gas under UV exposure. Due to the advantages of easy recycling and good photocatalytic efficiency, the novel magnetic photocatalyst developed here has potential use in photocatalytic applications for pollution prevention

  13. Study of TiO2 nanotubes as an implant application

    International Nuclear Information System (INIS)

    Hazan, Roshasnorlyza; Sreekantan, Srimala; Mydin, Rabiatul Basria S. M. N.; Mat, Ishak; Abdullah, Yusof

    2016-01-01

    Vertically aligned TiO 2 nanotubes have become the primary candidates for implant materials that can provide direct control of cell behaviors. In this work, 65 nm inner diameters of TiO 2 nanotubes were successfully prepared by anodization method. The interaction of bone marrow stromal cells (BMSC) in term of cell adhesion and cell morphology on bare titanium and TiO 2 nanotubes is reported. Field emission scanning electron microscopy (FESEM) analysis proved interaction of BMSC on TiO 2 nanotubes structure was better than flat titanium (Ti) surface. Also, significant cell adhesion on TiO 2 nanotubes surface during in vitro study revealed that BMSC prone to attach on TiO 2 nanotubes. From the result, it can be conclude that TiO 2 nanotubes are biocompatible to biological environment and become a new generation for advanced implant materials

  14. Utilization of ruthenium volatilization at heating of residue containing phosphates and nitrates for ruthenium separation and for its qualitative proof

    International Nuclear Information System (INIS)

    Holgye, Z.

    1979-01-01

    The volatility of ruthenium during the heating of a residue after evaporation of a solution containing ruthenium, phosphates and nitrates may be utilized for the separation of ruthenium from various substances. Sup(103,106) Ru may be rapidly, selectively, and quantitatively separated from fission products mixture. Ruthenium may be also separated in this way from various inorganic salts or from biological material. The volatility of ruthenium may be used also for its qualitative proof. (author)

  15. Raman Microspectroscopic Mapping with Multivariate Curve Resolution-Alternating Least Squares (MCR-ALS) Applied to the High-Pressure Polymorph of Titanium Dioxide, TiO2-II.

    Science.gov (United States)

    Smith, Joseph P; Smith, Frank C; Ottaway, Joshua; Krull-Davatzes, Alexandra E; Simonson, Bruce M; Glass, Billy P; Booksh, Karl S

    2017-08-01

    The high-pressure, α-PbO 2 -structured polymorph of titanium dioxide (TiO 2 -II) was recently identified in micrometer-sized grains recovered from four Neoarchean spherule layers deposited between ∼2.65 and ∼2.54 billion years ago. Several lines of evidence support the interpretation that these layers represent distal impact ejecta layers. The presence of shock-induced TiO 2 -II provides physical evidence to further support an impact origin for these spherule layers. Detailed characterization of the distribution of TiO 2 -II in these grains may be useful for correlating the layers, estimating the paleodistances of the layers from their source craters, and providing insight into the formation of the TiO 2 -II. Here we report the investigation of TiO 2 -II-bearing grains from these four spherule layers using multivariate curve resolution-alternating least squares (MCR-ALS) applied to Raman microspectroscopic mapping. Raman spectra provide evidence of grains consisting primarily of rutile (TiO 2 ) and TiO 2 -II, as shown by Raman bands at 174 cm -1 (TiO 2 -II), 426 cm -1 (TiO 2 -II), 443 cm -1 (rutile), and 610 cm -1 (rutile). Principal component analysis (PCA) yielded a predominantly three-phase system comprised of rutile, TiO 2 -II, and substrate-adhesive epoxy. Scanning electron microscopy (SEM) suggests heterogeneous grains containing polydispersed micrometer- and submicrometer-sized particles. Multivariate curve resolution-alternating least squares applied to the Raman microspectroscopic mapping yielded up to five distinct chemical components: three phases of TiO 2 (rutile, TiO 2 -II, and anatase), quartz (SiO 2 ), and substrate-adhesive epoxy. Spectral profiles and spatially resolved chemical maps of the pure chemical components were generated using MCR-ALS applied to the Raman microspectroscopic maps. The spatial resolution of the Raman microspectroscopic maps was enhanced in comparable, cost-effective analysis times by limiting spectral resolution

  16. Optical Properties and Surface Morphology of Nano-composite PMMA: TiO2 Thin Films

    International Nuclear Information System (INIS)

    Lyly Nyl Ismail; Ahmad Fairoz Aziz; Habibah Zulkefle

    2011-01-01

    There are two nano-composite PMMA: TiO 2 solutions were prepared in this research. First solution is nano-composite PMMA commercially available TiO 2 nanopowder and the second solution is nano-composite PMMA with self-prepared TiO 2 powder. The self-prepared TiO 2 powder is obtained by preparing the TiO 2 sol-gel. Solvo thermal method were used to dry the TiO 2 sol-gel and obtained TiO 2 crystal. Ball millers were used to grind the TiO 2 crystal in order to obtained nano sized powder. Triton-X was used as surfactant to stabilizer the composite between PMMA: TiO 2 . Besides comparing the nano-composite solution, we also studied the effect of the thin films thickness on the optical properties and surface morphology of the thin films. The thin films were deposited by sol-gel spin coating method on glass substrates. The optical properties and surface characterization were measured with UV-VIS spectrometer equipment and atomic force microscopy (AFM). The result showed that nano-composite PMMA with self prepared TiO 2 give high optical transparency than nano-composite PMMA with commercially available TiO 2 nano powder. The results also indicate as the thickness is increased the optical transparency are decreased. Both AFM images showed that the agglomerations of TiO 2 particles are occurred on the thin films and the surface roughness is increased when the thickness is increased. High agglomeration particles exist in the AFM images for nano-composite PMMA: TiO 2 with TiO 2 nano powder compare to the other nano-composite solution. (author)

  17. Distinct toxic interactions of TiO2 nanoparticles with four coexisting organochlorine contaminants on algae.

    Science.gov (United States)

    Zhang, Shuai; Deng, Rui; Lin, Daohui; Wu, Fengchang

    Engineered nanoparticles are increasingly discharged into the environment. After discharge, these nanoparticles can interact with co-existing organic contaminants, resulting in a phenomena referred to as 'joint toxicity'. This study evaluated joint toxicities of TiO 2 nanoparticles (TiO 2 NPs) with four different (atrazine, hexachlorobenzene, pentachlorobenzene, and 3,3',4,4'-tetrachlorobiphenyl) organochlorine contaminants (OCs) toward algae (Chlorella pyrenoidosa). The potential mechanisms underlying the joint toxicity were discussed, including TiO 2 NPs-OC interactions, effects of TiO 2 NPs and OCs on biophysicochemical properties of algae and effects of TiO 2 NPs and OCs on each other's bioaccumulation in algae. The results indicate that coexposure led to a synergistic effect on the joint toxicity for TiO 2 NPs-atrazine, antagonistic effect for TiO 2 NPs-hexachlorobenzene and TiO 2 NPs-3,3',4,4'-tetrachlorobiphenyl, and an additive effect for TiO 2 NPs-pentachlorobenzene. There was nearly no adsorption of OCs by TiO 2 NPs, and the physicochemical properties of TiO 2 NPs were largely unaltered by the presence of OCs. However, both OCs and NPs affected the biophysicochemical properties of algal cells and thereby influenced the cell surface binding and/or internalization. TiO 2 NPs significantly increased the bioaccumulation of each OC. However, with the exception of atrazine, the bioaccumulation of TiO 2 NPs decreased when used with each OC. The distinct joint toxicity outcomes were a result of the balance between the increased toxicities of OCs (increased bioaccumulations) and the altered toxicity of TiO 2 NPs (bioaccumulation can either increase or decrease). These results can significantly improve our understanding of the potential environmental risks associated with NPs.

  18. Partitioning of L-methionine in aqueous two-phase systems containing poly(propylene glycol) and sodium phosphate salts

    Energy Technology Data Exchange (ETDEWEB)

    Salabat, Alireza, E-mail: a-salabat@araku.ac.ir [Chemistry Department, Arak University, P.O. Box 38156-879, Arak (Iran, Islamic Republic of); Sadeghi, Rahmat [Department of Chemistry, University of Kurdistan, Sanandaj, Kurdistan 66135 (Iran, Islamic Republic of); Moghadam, Somayeh Tiani [Chemistry Department, Arak University, P.O. Box 38156-879, Arak (Iran, Islamic Republic of); Jamehbozorg, Bahman [Department of Chemistry, University of Kurdistan, Sanandaj, Kurdistan 66135 (Iran, Islamic Republic of)

    2011-10-15

    Highlights: > Thermodynamics parameters for partitioning of L-methionine in ATPS. > Investigation of different effects on partition coefficient of the amino acid. > Propose the best condition for L-methionine partitioning. - Abstract: The partitioning behavior of L-methionine has been studied in aqueous two-phase systems of (poly(propylene glycol) + sodium phosphate salts + H{sub 2}O) at different temperatures. The salts used were sodium di-hydrogen phosphate (NaH{sub 2}PO{sub 4}), di-sodium hydrogen phosphate (Na{sub 2}HPO{sub 4}) and tri-sodium phosphate (Na{sub 3}PO{sub 4}). The effects of tie line length, salt type, and temperature on the partition coefficient of this amino acid have been studied. In addition, thermodynamic parameters ({Delta}H{sup o}, {Delta}S{sup o} and {Delta}G{sup o}) as a function of temperature were calculated. The results showed that increasing tie line length led to decreasing of the partition coefficient. We also showed that the partition coefficients of the amino acid in the systems containing Na{sub 3}PO{sub 4} are greater than the other two salts. Moreover, it is verified that increasing temperature led to decreasing the partition coefficient. The experimental partition coefficient data are correlated using a modified virial-type model.

  19. Partitioning of L-methionine in aqueous two-phase systems containing poly(propylene glycol) and sodium phosphate salts

    International Nuclear Information System (INIS)

    Salabat, Alireza; Sadeghi, Rahmat; Moghadam, Somayeh Tiani; Jamehbozorg, Bahman

    2011-01-01

    Highlights: → Thermodynamics parameters for partitioning of L-methionine in ATPS. → Investigation of different effects on partition coefficient of the amino acid. → Propose the best condition for L-methionine partitioning. - Abstract: The partitioning behavior of L-methionine has been studied in aqueous two-phase systems of (poly(propylene glycol) + sodium phosphate salts + H 2 O) at different temperatures. The salts used were sodium di-hydrogen phosphate (NaH 2 PO 4 ), di-sodium hydrogen phosphate (Na 2 HPO 4 ) and tri-sodium phosphate (Na 3 PO 4 ). The effects of tie line length, salt type, and temperature on the partition coefficient of this amino acid have been studied. In addition, thermodynamic parameters (ΔH o , ΔS o and ΔG o ) as a function of temperature were calculated. The results showed that increasing tie line length led to decreasing of the partition coefficient. We also showed that the partition coefficients of the amino acid in the systems containing Na 3 PO 4 are greater than the other two salts. Moreover, it is verified that increasing temperature led to decreasing the partition coefficient. The experimental partition coefficient data are correlated using a modified virial-type model.

  20. Optimized Li-Ion Electrolytes Containing Triphenyl Phosphate as a Flame-Retardant Additive

    Science.gov (United States)

    Smart, Marshall C.; Bugga, Ratnakumar V.; Prakash, G. K. Surya; Krause, Frederick C.

    2011-01-01

    A number of future NASA missions involving the exploration of the Moon and Mars will be human-rated and thus require high-specific-energy rechargeable batteries that possess enhanced safety characteristics. Given that Li-ion technology is the most viable rechargeable energy storage device for near-term applications, effort has been devoted to improving the safety characteristics of this system. There is also a strong desire to develop Li-ion batteries with improved safety characteristics for terrestrial applications, most notably for hybrid electric vehicle (HEV) and plug-in hybrid electric vehicle (PHEV) automotive applications. Therefore, extensive effort has been devoted recently to developing non-flammable electrolytes to reduce the flammability of the cells/battery. A number of electrolyte formulations have been developed, including systems that (1) incorporate greater concentrations of the flame-retardant additive (FRA); (2) use di-2,2,2-trifluoroethyl carbonate (DTFEC) as a co-solvent; (3) use 2,2,2- trifluoroethyl methyl carbonate (TFEMC); (4) use mono-fluoroethylene carbonate (FEC) as a co-solvent and/or a replacement for ethylene carbonate in the electrolyte mixture; and (5) utilize vinylene carbonate as a "SEI promoting" electrolyte additive, to build on the favorable results previously obtained. To extend the family of electrolytes developed under previous work, a number of additional electrolyte formulations containing FRAs, most notably triphenyl phosphate (TPP), were investigated and demonstrated in experimental MCMB (mesocarbon micro beads) carbon- LiNi(0.8)Co(0.2)O2 cells. The use of higher concentrations of the FRA is known to reduce the flammability of the electrolyte solution, thus, a concentration range was investigated (i.e., 5 to 20 percent by volume). The desired concentration of the FRA is the highest amount tolerable without adversely affecting the performance in terms of reversibility, ability to operate over a wide temperature range, and

  1. Hybrid matrices of TiO2 and TiO2–Ag nanofibers with silicone for high water flux photocatalytic degradation of dairy effluent

    DEFF Research Database (Denmark)

    Kanjwal, Muzafar Ahmad; Alm, Martin; Thomsen, Peter

    2016-01-01

    TiO2 and TiO2–Ag nanofibers were produced by electrospinning technique and surface coated on silicone elastomer (diameter: 10.0 mm; thickness: 2.0 mm) by dipcoating method. These coated hybrid nanoporous matrices were characterized by various morphological and physicochemical techniques (like SEM...

  2. TiO2/Cu2O composite based on TiO2 NTPC photoanode for photoelectrochemical (PEC) water splitting under visible light

    KAUST Repository

    Shi, Le

    2015-01-01

    in practice of water splitting with pure TiO2 material, one of the most popular semiconductor material used for photoelectrochemical water splitting, is still challenging. One dimensional TiO2 nanotubes is highly desired with its less recombination

  3. Charge transfer between biogenic jarosite derived Fe3+and TiO2 enhances visible light photocatalytic activity of TiO2.

    Science.gov (United States)

    Chowdhury, Mahabubur; Shoko, Sipiwe; Cummings, Fransciuos; Fester, Veruscha; Ojumu, Tunde Victor

    2017-04-01

    In this work, we have shown that mining waste derived Fe 3+ can be used to enhance the photocatalytic activity of TiO 2 . This will allow us to harness a waste product from the mines, and utilize it to enhance TiO 2 photocatalytic waste water treatment efficiency. An organic linker mediated route was utilized to create a composite of TiO 2 and biogenic jarosite. Evidence of FeOTi bonding in the TiO 2 /jarosite composite was apparent from the FTIR, EFTEM, EELS and ELNEFS analysis. The as prepared material showed enhanced photocatalytic activity compared to pristine TiO 2 , biogenic jarosite and mechanically mixed sample of jarosite and TiO 2 under both simulated and natural solar irradiation. The prepared material can reduce the electrical energy consumption by 4 times compared to pristine P25 for degradation of organic pollutant in water. The material also showed good recyclability. Results obtained from sedimentation experiments showed that the larger sized jarosite material provided the surface to TiO 2 nanoparticles, which increases the settling rate of the materials. This allowed simple and efficient recovery of the catalyst from the reaction system after completion of photocatalysis. Enhanced photocatalytic activity of the composite material was due to effective charge transfer between TiO 2 and jarosite derived Fe 3+ as was shown from the EELS and ELNEFS. Generation of OH was supported by photoluminesence (PL) experiments. Copyright © 2016. Published by Elsevier B.V.

  4. Structural properties of TiO2 nanomaterials

    Science.gov (United States)

    Kusior, Anna; Banas, Joanna; Trenczek-Zajac, Anita; Zubrzycka, Paulina; Micek-Ilnicka, Anna; Radecka, Marta

    2018-04-01

    The surface of solids is characterized by active, energy-rich sites that determine physicochemical interaction with gaseous and liquid media and possible applications in photocatalysis. The behavior of materials in such processes is related to their form and amount of various species, especially water and forms of oxygen adsorbed on the surface. The preparation of materials with controlled morphology, which includes modifications of the size, geometry, and composition, is currently an important way of optimizing properties, as many of them depend on not only the size and phase composition, but also on shape. Hydroxylated centers on the surface, which can be treated as trapping sites, are particularly significant. Water adsorbed on the surface bridging hydroxyl groups can distinctly modulate the properties of the surface of titania. The saturation of the surface with hydroxyl groups may improve the photocatalytic properties. TiO2 nanomaterials were obtained via different methods. SEM and TEM analysis were performed to study the morphology. The analysis of XRD and Raman data revealed a phase composition of obtained materials. To examine the surface properties, FTIR absorption spectra of TiO2 nanomaterials were recorded. The photocatalytic activity of titanium dioxide nanoparticles was investigated through the decomposition of methylene blue. It was demonstrated that each surface modification affects the amount of adsorbed hydroxyl groups. The different contributions of the two species to the ν(H2O) FTIR bands for different nanostructures result from the preparation conditions. It was noted that pre-adsorbed water (the surface-bridging hydroxyl) might significantly modulate the surface properties of the material. The increase in hydroxyl group density on the titanium dioxide surface enhances the effectiveness of the photocatalytic processes. It was demonstrated that flower-like titania obtained via hydrothermal synthesis exhibits the weakest catalytic activity, in contrast to the typical spherical TiO2.

  5. Structure and properties of nanophase TiO2

    International Nuclear Information System (INIS)

    Siegel, R.W.; Hahn, H.; Ramasamy, S.; Zongquan, Li; Ting, Lu; Gronsky, R.

    1987-07-01

    Ultrafine-grained, nanophase samples of TiO 2 (rutile) were synthesized by the gas-condensation method and subsequent in-situ compaction, and then studied by transmission electron microscopy, Vickers hardness measurements, and positron annihilation spectroscopy as a function of sintering temperature. The nanophase compacts densified rapidly above 500 0 C, with only a small increase in grain size. The hardness values obtained by this method are comparable to or greater than coarser-grained compacts, but at temperatures 400 to 600 0 C lower than conventional sintering temperatures and without the need for sintering aids. 11 refs., 3 figs

  6. On Multiple Zagreb Indices of TiO2 Nanotubes.

    Science.gov (United States)

    Malik, Mehar Ali; Imran, Muhammad

    2015-01-01

    The First and Second Zagreb indices were first introduced by I. Gutman and N. Trinajstic in 1972. It is reported that these indices are useful in the study of anti-inflammatory activities of certain chemical instances, and in elsewhere. Recently, the first and second multiple Zagreb indices of a graph were introduced by Ghorbani and Azimi in 2012. In this paper, we calculate the Zagreb indices and the multiplicative versions of the Zagreb indices of an infinite class of Titania nanotubes TiO(2)[m,n].

  7. Carrier recombination dynamics in anatase TiO 2 nanoparticles

    Science.gov (United States)

    Cavigli, Lucia; Bogani, Franco; Vinattieri, Anna; Cortese, Lorenzo; Colocci, Marcello; Faso, Valentina; Baldi, Giovanni

    2010-11-01

    We present an experimental study of the radiative recombination dynamics in size-controlled TiO 2 nanoparticles in the range 20-130 nm. Time-integrated photoluminescence spectra clearly show a dominance of self-trapped exciton (STE) emission, with main features not dependent on the nanoparticle size and on its environment. From picosecond time-resolved experiments as a function of the excitation density and the nanoparticle size we address the STE recombination dynamics as the result of two main processes related to the direct STE formation and to the indirect STE formation mediated by non-radiative surface states.

  8. Al-bound hole polarons in TiO2

    International Nuclear Information System (INIS)

    Stashans, Arvids; Bermeo, Sthefano

    2009-01-01

    Changes in the structural and electronic properties of TiO 2 (anatase and rutile) due to the Al-doping are studied using a quantum-chemical approach based on the Hartree-Fock theory. The formation of hole polarons trapped at oxygen sites near the Al impurity has been discovered and their spatial configuration are discussed. The occurrence of well-localized one-center hole polarons in rutile may influence its photocatalytic activity. Optical absorption energy for this hole center is obtained, 0.4 eV, using the ΔSCF approach.

  9. Tailoring the wettability of nanocrystalline TiO 2 films

    Science.gov (United States)

    Liang, Qiyu; Chen, Yan; Fan, Yuzun; Hu, Yong; Wu, Yuedong; Zhao, Ziqiang; Meng, Qingbo

    2012-01-01

    The water contact angle (WCA) of nanocrystalline TiO2 films was adjusted by fluoroalkylsilane (FAS) modification and photocatalytic lithography. FAS modification made the surface hydrophobic with the WCA up to ∼156°, while ultraviolet (UV) irradiation changed surface to hydrophilic with the WCA down to ∼0°. Both the hydrophobicity and hydrophilicity were enhanced by surface roughness. The wettability can be tailored by varying the concentration of FAS solution and soaking time, as well as the UV light intensity and irradiation time. Additionally, with the help of photomasks, hydrophobic-hydrophilic micropatterns can be fabricated and manifested via area-selective deposition of polystyrene particles.

  10. Highly uniform bipolar resistive switching characteristics in TiO2/BaTiO3/TiO2 multilayer

    International Nuclear Information System (INIS)

    Ma, W. J.; Zhang, X. Y.; Wang, Ying; Zheng, Yue; Lin, S. P.; Luo, J. M.; Wang, B.; Li, Z. X.

    2013-01-01

    Nanoscale multilayer structure TiO 2 /BaTiO 3 /TiO 2 has been fabricated on Pt/Ti/SiO 2 /Si substrate by chemical solution deposition method. Highly uniform bipolar resistive switching (BRS) characteristics have been observed in Pt/TiO 2 /BaTiO 3 /TiO 2 /Pt cells. Analysis of the current-voltage relationship demonstrates that the space-charge-limited current conduction controlled by the localized oxygen vacancies should be important to the resistive switching behavior. X-ray photoelectron spectroscopy results indicated that oxygen vacancies in TiO 2 play a crucial role in the resistive switching phenomenon and the introduced TiO 2 /BaTiO 3 interfaces result in the high uniformity of bipolar resistive switching characteristics

  11. Synthesis of Fe2O3/TiO2 nanorod-nanotube arrays by filling TiO2 nanotubes with Fe

    International Nuclear Information System (INIS)

    Mohapatra, Susanta K; Banerjee, Subarna; Misra, Mano

    2008-01-01

    Synthesis of hematite (α-Fe 2 O 3 ) nanostructures on a titania (TiO 2 ) nanotubular template is carried out using a pulsed electrodeposition technique. The TiO 2 nanotubes are prepared by the sonoelectrochemical anodization method and are filled with iron (Fe) by pulsed electrodeposition. The Fe/TiO 2 composite is then annealed in an O 2 atmosphere to convert it to Fe 2 O 3 /TiO 2 nanorod-nanotube arrays. The length of the Fe 2 O 3 inside the TiO 2 nanotubes can be tuned from 50 to 550 nm by changing the deposition time. The composite material is characterized by scanning electron microscopy, transmission electron microscopy and diffuse reflectance ultraviolet-visible studies to confirm the formation of one-dimensional Fe 2 O 3 /TiO 2 nanorod-nanotube arrays. The present approach can be used for designing variable one-dimensional metal oxide heterostructures

  12. UV-visible light-activated Ag-decorated, monodisperse TiO2 aggregates for treatment of the pharmaceutical oxytetracycline.

    Science.gov (United States)

    Han, Changseok; Likodimos, Vlassis; Khan, Javed Ali; Nadagouda, Mallikarjuna N; Andersen, Joel; Falaras, Polycarpos; Rosales-Lombardi, Pablo; Dionysiou, Dionysios D

    2014-10-01

    Noble metal Ag-decorated, monodisperse TiO2 aggregates were successfully synthesized by an ionic strength-assisted, simple sol-gel method and were used for the photocatalytic degradation of the antibiotic oxytetracycline (OTC) under both UV and visible light (UV-visible light) irradiation. The synthesized samples were characterized by X-ray diffraction analysis (XRD); UV-vis diffuse reflectance spectroscopy; environmental scanning electron microscopy (ESEM); transmission electron microscopy (TEM); high-resolution TEM (HR-TEM); micro-Raman, energy-dispersive X-ray spectroscopy (EDS); and inductively coupled plasma optical emission spectrometry (ICP-OES). The results showed that the uniformity of TiO2 aggregates was finely tuned by the sol-gel method, and Ag was well decorated on the monodisperse TiO2 aggregates. The absorption of the samples in the visible light region increased with increasing Ag loading that was proportional to the amount of Ag precursor added in the solution over the tested concentration range. The Brunauer, Emmett, and Teller (The BET) surface area slightly decreased with increasing Ag loading on the TiO2 aggregates. Ag-decorated TiO2 samples demonstrated enhanced photocatalytic activity for the degradation of OTC under UV-visible light illumination compared to that of pure TiO2. The sample containing 1.9 wt% Ag showed the highest photocatalytic activity for the degradation of OTC under both UV-visible light and visible light illumination. During the experiments, the detected Ag leaching for the best TiO2-Ag photocatalyst was much lower than the National Secondary Drinking Water Regulation for Ag limit (0.1 mg L(-1)) issued by the US Environmental Protection Agency.

  13. Alkali-corrosion synthesis and excellent DSSC performance of novel jujube-like hierarchical TiO2 microspheres

    Science.gov (United States)

    Xiao, Jiajia; Li, Po; Wen, Xiaogang

    2018-04-01

    Novel jujube-like hierarchical TiO2 microspheres (HTMs) were synthesized by an alkali-corrosion process of titanium phosphate (Ti2O3(H2PO4)2 · 2H2O) microspheres. The hierarchical titanium phosphate microsphere (HTPM) intermediates consisting of nanoflakes with a thickness of 20 nm were firstly prepared by a facile hydrothermal method. After reacting with diluted NaOH at low temperature and atmospheric pressure, followed by subsequent acid washing and a calcination process, the HTPM intermediates were transformed to TiO2 with the microsphere morphology well retained, while the nanoflakes became porous, and some new nanowires were formed between the nanoflakes. Finally, HTMs consisting of porous nanoflakes and nanowires were obtained. The possible growth mechanisms of HTPMs and HTMs are discussed. The HTMs demonstrate high specific surface area and excellent light-scattering ability. The performance of the dye sensitized solar cells (DSSCs) of the HTMs synthesized under different conditions is studied, and a total conversion efficiency of up to 8.93% was obtained. The improved DSSC performance was attributed to the enhanced dye loading, light-scattering, and charge transporting ability of the HTMs with a unique hierarchical nanostructure.

  14. Preparation of pure TiO2 sorption material

    International Nuclear Information System (INIS)

    Špendlíková, Irena; Raindl, Jakub; Němec, Mojmír

    2013-01-01

    Among the natural or anthropogenic radionuclides of very low concentrations nowadays measured in environmental samples, the radionuclide of 236 U has been recently included. In these ultra-trace analyses, the purity of sorption materials is very important and the traditional preparation procedures have to be optimized to minimize possible contamination. In the case of the determination of natural concentration of 236 U ( 236 U/ 238 U ∼ 10 -10 - 10 -14 ), the sample treatment procedure has to be modified in order to eliminate possible contamination from anthropogenic 236 U that may result even in more than ten thousand times higher 236 U/ 238 U ratios. Many inorganic and organic materials have been proposed for the extraction of uranium. However, only several of them are suitable for the uranium sorption from the solutions of low uranium concentration, but relatively high salt content, such as fresh water, sea water etc. At the same time they have to meet other limiting parameters such as fast kinetics, chemical stability, and low costs. Among the inorganic sorption materials, titanium dioxide has been studied for years with promising results. Titanium dioxides can be prepared via the hydrolysis of titanium compounds, either inorganic salts or organic derivatives, but their properties strongly depend on the preparation conditions. In classical procedures, titanium dioxides are prepared from commercial inorganic salts, such as sulphates or chlorides, or even from industrial intermediates of the titanium white production. Typically, the resulting titanium dioxides are contaminated with uranium already from the origin. Assuming that most organic compounds do not contain uranium and that it is possible to find 'uranium free' water, titanium dioxide free of uranium contamination could be prepared by the hydrolysis of organic titanium derivatives. The aim of this study was to find a suitable way of pure titanium dioxide preparation and to optimize the preparation

  15. Photocatalytic Decolorization Study of Methyl Orange by TiO2–Chitosan Nanocomposites

    Directory of Open Access Journals (Sweden)

    Imelda Fajriati

    2014-10-01

    Full Text Available The photocatalytic decolorization of methyl orange (MO by TiO2-chitosan nanocomposite has been studied. This study was started by synthesizing TiO2-chitosan nanocomposites using sol-gel method with various concentrations of Titanium(IV isopropoxide (TTIP as the TiO2 precursor. The structure, surface morphology, thermal and optical property of TiO2-chitosan nanocomposite were characterized by X-ray diffraction (XRD, fourier transform infra red (FTIR spectroscopy, scanning electron microscopy (SEM, thermogravimetric analysis (TGA, and diffuse reflectance ultra violet (DRUV spectroscopy. The photocatalytic activity of TiO2-chitosan nanocomposite was evaluated by photocatalytic decolorization of methyl orange as a model pollutant. The results indicate that the particle size of TiO2 increases with increasing ofthe concentration of TTIP, in which TiO2 with smallest particle size exhibit the highest photocatalytic activity. The highest photocatalytic decolorization was obtained at 5 h of contact time, initial concentration of MO at 20 ppm and at solution pH of 4. Using these conditions, over 90% of MO was able to be decolorized using 0.02 g of TiO2-chitosan nanocomposite under UV light irradiation. The TiO2-chitosan nanocomposite could be reused, which meant that the TiO2-chitosan nanocomposites can be developed as an effective and economical photocatalyst to decolorize or treat dye in wastewater.

  16. The Influence of NiO Addition in TiO2 Structure and Its Photoactivity

    Science.gov (United States)

    Wahyuningsih, S.; Ramelan, A. H.; Purwanti, P. D.; Munawaroh, H.; Ichsan, S.; Kristiawan, Y. R.

    2018-03-01

    The synthesis of TiO2 together with the TiO2-NiO composite using various annealing temperatures has been studied. The synthesis of TiO2 was performed by sol gel method using Titanium Tetra Isopropoxide (TTIP) precursor, whereas the synthesis of TiO2-NiO composite was done by wet impregnation method using NiNO3.6H2O precursor. This study aims to determine the influence of NiO addition in its structure and photoactivity. The diffraction of synthesized TiO2 at 400 °C temperature shows anatase TiO2 peak at 2θ = 25.35 °. The addition of NiO dopant to the synthesis of TiO2 process is carried out by annealing at 300 °C, 400 °C, 500 °C, 600 °C, and 700 °C, respectively. The TiO2-NiO composite has been prepared and shows the diffraction peak of NiO at 2θ=43° about 33.08 to 36.68%. The optimum result of Rhodamine B photodegradation with TiO2 was 43.15%, while the optimum result of Rhodamine B degradation with TiO2-NiO composite was 92.85%.

  17. A thick hierarchical rutile TiO2 nanomaterial with multilayered structure

    International Nuclear Information System (INIS)

    Zhu, Shengli; Xie, Guoqiang; Yang, Xianjin; Cui, Zhenduo

    2013-01-01

    Highlights: ► We synthesized a new rutile TiO 2 nanomaterial with a hierarchical nanostructure. ► The nano architecture structure consist of nanorods and nanoflower arrays. ► The rutile TiO 2 nanomaterial is thick in size (several 10 μm). ► The TiO 2 nanomaterials present a multilayer structure. - Abstract: In the present paper, we synthesized a new type of rutile TiO 2 nanomaterial with a hierarchical nanostructure using a novel method, which combined dealloying process with chemical synthesis. The structure characters were examined using X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The rutile TiO 2 nanomaterial is thick in size (several 10 μm). The hierarchical structure of the rutile TiO 2 nanomaterial consists of large quantities nanorods and nanoflower arrays. The nanoflowers consist of serveral nanopetals with diameter of 100–200 nm. The cross section of TiO 2 nanomaterials presents a multilayer structure with the layer thickness of about 3–5 μm. The rutile TiO 2 nanomaterial has high specific surface area. The formation mechanism of the rutile TiO 2 nanomaterial was discussed according to the experimental results. The rutile TiO 2 nanomaterial has potential applications in catalysis, photocatalysis and solar cells

  18. Parameters affecting the photocatalytic degradation of dyes using TiO2: a review

    Science.gov (United States)

    Reza, Khan Mamun; Kurny, ASW; Gulshan, Fahmida

    2017-07-01

    Traditional chemical, physical and biological processes for treating wastewater containing textile dye have such disadvantages as high cost, high energy requirement and generation of secondary pollution during treatment process. The advanced oxidation processes technology has been attracting growing attention for the decomposition of organic dyes. Such processes are based on the light-enhanced generation of highly reactive hydroxyl radicals, which oxidize the organic matter in solution and convert it completely into water, CO2 and inorganic compounds. In this presentation, the photocatalytic degradation of dyes in aqueous solution using TiO2 as photocatalyst under solar and UV irradiation has been reviewed. It is observed that the degradation of dyes depends on several parameters such as pH, catalyst concentration, substrate concentration and the presence of oxidants. Reaction temperature and the intensity of light also affect the degradation of dyes. Particle size, BET-surface area and different mineral forms of TiO2 also have influence on the degradation rate.

  19. Atomic Layer-Deposited TiO2 Coatings on NiTi Surface

    Science.gov (United States)

    Vokoun, D.; Racek, J.; Kadeřávek, L.; Kei, C. C.; Yu, Y. S.; Klimša, L.; Šittner, P.

    2018-02-01

    NiTi shape-memory alloys may release poisonous Ni ions at the alloys' surface. In an attempt to prepare a well-performing surface layer on an NiTi sample, the thermally grown TiO2 layer, which formed during the heat treatment of NiTi, was removed and replaced with a new TiO2 layer prepared using the atomic layer deposition (ALD) method. Using x-ray photoelectron spectroscopy, it was found that the ALD layer prepared at as low a temperature as 100 °C contained Ti in oxidation states + 4 and + 3. As for static corrosion properties of the ALD-coated NiTi samples, they further improved compared to those covered by thermally grown oxide. The corrosion rate of samples with thermally grown oxide was 1.05 × 10-5 mm/year, whereas the corrosion rate of the ALD-coated samples turned out to be about five times lower. However, cracking of the ALD coating occurred at about 1.5% strain during the superelastic mechanical loading in tension taking place via the propagation of a localized martensite band.

  20. TiO2-anatase modified by carbon as the photo catalyst under visible light

    International Nuclear Information System (INIS)

    Morawski, A.W.; Janus, M.; Tryba, B.; Kalucki, K.; Tryba, B.; Inagaki, M.

    2006-01-01

    The photo-catalytic oxidation of phenol in water under a visible light over anatase-type titanium dioxide (Tytanpol A11, Poland), modified by carbon deposited via n-hexane carbonization, was investigated. The catalysts, which had small (0-0.2 mass%) and high (0.69-0.85 mass%) contents of carbon showed a little lower catalytic photo-activity than pristine TiO 2 . However, the catalyst with high content of carbon (0.85 mass%) gave almost 14-times lower turbidity in the phenol solution after the photo-catalyst sedimentation. These two factors depend on the carbon content and have an influence on the 'practical efficiency' of the catalysts. The 'practical efficiency' of the catalyst under visible light, calculated from these two factors, was therefore 14-times higher for the catalyst containing 0.85 mass% carbon (whereas for UV radiation, it was found to be lower - 0.2 mass% -; this is the result of a previous work). The surface modification of the catalyst with 0.85% carbon seemed to be stable under visible light. The deposition of carbon on TiO 2 by carbonization of n-hexane was supposed to lead to obtain the catalyst, which could be easily used in a water-treatment system under visible light. (authors)

  1. Effect of TiO2 nanoparticles incorporation on antibacterial properties and shear bond strength of dental composite used in Orthodontics

    Directory of Open Access Journals (Sweden)

    Ahmad Sodagar

    Full Text Available ABSTRACT Introduction: Plaque accumulation and bond failure are drawbacks of orthodontic treatment, which requires composite for bonding of brackets. As the antimicrobial properties of TiO2 nanoparticles (NPs have been proven, the aim of this study was to evaluate the antimicrobial and mechanical properties of composite resins modified by the addition of TiO2 NPs. Methods: Orthodontics composite containing 0%, 1%, 5% and 10% NPs were prepared. 180 composite disks were prepared for elution test, disk agar diffusion test and biofilm inhibition test to collect the counts of microorganisms on three days, measure the inhibition diameter and quantify the viable counts of colonies consequently. For shear bond strength (SBS test, 48 intact bovine incisors were divided into four groups. Composites containing 0%, 1%, 5% and 10% NPs were used for bonding of bracket. The bracket/tooth SBS was measured by using an universal testing machine. Results: All concentration of TiO2 NPs had a significant effect on creation and extension of inhibition zone. For S. mutans and S. sanguinis, all concentration of TiO2 NPs caused reduction of the colony counts. Composite containing 10% TiO2 NPs had significant effect on reduction of colony counts for S. mutans and S. sanguinis in all three days. The highest mean shear bond strength belonged to the control group, while the lowest value was seen in 10% NPs composite. Conclusions: Incorporating TiO2 nanoparticles into composite resins confer antibacterial properties to adhesives, while the mean shear bond of composite containing 1% and 5% NPs still in an acceptable range.

  2. Preparation of rutile TiO(2) coating by thermal chemical vapor deposition for anticoking applications.

    Science.gov (United States)

    Tang, Shiyun; Wang, Jianli; Zhu, Quan; Chen, Yaoqiang; Li, Xiangyuan

    2014-10-08

    To inhibit the metal catalytic coking and improve the oxidation resistance of TiN coating, rutile TiO2 coating has been directly designed as an efficient anticoking coating for n-hexane pyrolysis. TiO2 coatings were prepared on the inner surface of SS304 tubes by a thermal CVD method under varied temperatures from 650 to 900 °C. The rutile TiO2 coating was obtained by annealing the as-deposited TiO2 coating, which is an alternative route for the deposition of rutile TiO2 coating. The morphology, elemental and phase composition of TiO2 coatings were characterized by SEM, EDX and XRD, respectively. The results show that deposition temperature of TiO2 coatings has a strong effect on the morphology and thickness of as-deposited TiO2 coatings. Fe, Cr and Ni at.% of the substrate gradually changes to 0 when the temperature is increased to 800 °C. The thickness of TiO2 coating is more than 6 μm and uniform by metalloscopy, and the films have a nonstoichiometric composition of Ti3O8 when the deposition temperature is above 800 °C. The anticoking tests show that the TiO2 coating at a deposition temperature of 800 °C is sufficiently thick to cover the cracks and gaps on the surface of blank substrate and cut off the catalytic coke growth effect of the metal substrate. The anticoking ratio of TiO2 coating corresponding to each 5 cm segments is above 65% and the average anticoking ratio of TiO2 coating is up to 76%. Thus, the TiO2 coating can provide a very good protective layer to prevent the substrate from severe coking efficiently.

  3. Exchange of TiO2 nanoparticles between streams and streambeds.

    Science.gov (United States)

    Boncagni, Natalia Ticiana; Otaegui, Justo Manuel; Warner, Evelyn; Curran, Trisha; Ren, Jianhong; de Cortalezzi, Maria Marta Fidalgo

    2009-10-15

    The expanding use of manufactured nanoparticles has increased the potential for their release into the natural environment. Particularly, TiO2 nanoparticles pose significant exposure risk to humans and other living species due to their extensive use in a wide range of fields. To better understand the environmental and health risks associated with the release of TiO2 nanoparticles, knowledge on their fate and transport is needed. This study evaluates the transport of two different TiO2 nanoparticles: one commercially available (P25 TiO2 and the other synthesized at a lab scale (synthesized TiO2). Laboratory flume, column, and batch experiments were conducted to investigate the processes dominating the transport of TiO2 nanoparticles between streams and streambeds and to characterize the properties of these nanoparticles under different physicochemical conditions. Results show that the synthesized TiO2 was more stable compared to the P25 TiO2, which underwent significant aggregation under the same experimental conditions. As a result, P25 TiO2 deposited at a faster rate than the synthesized TiO2 in the streambed. Both types of TiO2 nanoparticles deposited in the streambed were easily released when the stream velocity was increased. The aggregation and deposition of P25 TiO2 were highly dependent on pH. A process-based colloid exchange model was applied to interpret the observed transport behavior of the TiO2 nanoparticles.

  4. Metallic Nanoparticle (TiO2 and Fe3O4) Application Modifies Rhizosphere Phosphorus Availability and Uptake by Lactuca sativa.

    Science.gov (United States)

    Zahra, Zahra; Arshad, Muhammad; Rafique, Rafia; Mahmood, Arshad; Habib, Amir; Qazi, Ishtiaq A; Khan, Saud A

    2015-08-12

    Application of engineered nanoparticles (NPs) with respect to nutrient uptake in plants is not yet well understood. The impacts of TiO2 and Fe3O4 NPs on the availability of naturally soil-bound inorganic phosphorus (Pi) to plants were studied along with relevant parameters. For this purpose, Lactuca sativa (lettuce) was cultivated on the soil amended with TiO2 and Fe3O4 (0, 50, 100, 150, 200, and 250 mg kg(-1)) over a period of 90 days. Different techniques, such as scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), Raman, and Fourier transform infrared spectroscopy (FTIR) were used to monitor translocation and understand the possible mechanisms for phosphorus (P) uptake. The trends for P accumulation were different for roots (TiO2 > Fe3O4 > control) and shoots (Fe3O4 > TiO2 > control). Cystine and methionine were detected in the rhizosphere in Raman spectra. Affinities of NPs to adsorb phosphate ions, modifications in P speciation, and NP stress in the rhizosphere had possibly contributed to enhanced root exudation and acidification. All of these changes led to improved P availability and uptake by the plants. These promising results can help to develop an innovative strategy for using NPs for improved nutrient management to ensure food security.

  5. Microwave-assisted self-doping of TiO2 photonic crystals for efficient photoelectrochemical water splitting

    KAUST Repository

    Zhang, Zhonghai; Yang, Xiulin; Hedhili, Mohamed N.; Ahmed, Elaf S.; Shi, Le; Wang, Peng

    2014-01-01

    In this article, we report that the combination of microwave heating and ethylene glycol, a mild reducing agent, can induce Ti3+ self-doping in TiO2. A hierarchical TiO2 nanotube array with the top layer serving as TiO2 photonic crystals (TiO2 NTPCs

  6. Studies on the synthesis and characterization of cesium-containing iron phosphate glasses

    Science.gov (United States)

    Joseph, Kitheri; Govindan Kutty, K. V.; Chandramohan, P.; Vasudeva Rao, P. R.

    2009-02-01

    Isotopes of cesium and strontium can be utilized as radiation source for various industrial and medical applications after their separation from high level nuclear waste. However, these elements need to be immobilized in a suitable matrix. In the present work, a systematic approach has been made to immobilize inactive cesium into iron phosphate glass. Up to 36 mol% of Cs 2O has been loaded successfully without crystallization. The glass transition temperature of the cesium loaded glass was found to increase initially and then decrease as a function of Cs 2O content. Mössbauer studies show that the concentration of Fe 3+ ions in the cesium loaded glasses is >95%. Volatilization experiments at 1263 K show that the weight loss is >0.5% for a period of 4 h. The 36 mol% of Cs 2O loaded iron phosphate glass with high Fe 3+ content described in this paper is reported for the first time.

  7. La_2O_3-TiO_2系多孔質ガラスセラミックスの湿度センサーへの応用

    OpenAIRE

    清水, 康博; 岡田, 英昭; 荒井, 弘通

    1987-01-01

    The sodium borate glass system containing La2O3 and TiO2 shows a marked trend toward microphase separation after heat treatment, resulting in water-soluble sodium borate and water-insoluble La2O3-TiO2 ceramic phases. Then La2O3-TiO2-rich skeletons can be obtained by leaching out the sodium borate phase. The application of thus obtained porous glass-ceramics with interconnected pores to a humidity sensor is of interest. Microstructure, such as surface area and pore size distibution, of the ...

  8. Photoluminescence studies on Eu doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Ningthoujam, R.S.; Sudarsan, V.; Vatsa, R.K.; Kadam, R.M.; Jagannath; Gupta, A.

    2009-01-01

    Eu 3+ doped TiO 2 nanoparticles were prepared by urea hydrolysis in ethylene glycol medium at low temperature of 150 deg. C. X-ray diffraction study showed that anatase phase of tetragonal structure was formed below 500 deg. C; and above this temperature, additional peaks due to rutile phase were also observed. From luminescence study, it was found that as prepared nanoparticles showed the enhanced luminescence intensity due to energy transfer from host to europium ions. However, photoluminescence from these nanoparticles was found to disappear when the samples were heated above 900 deg. C. We established the origin of the reduction in the luminescence intensity from Eu 3+ when doped in TiO 2 and heated at 900 deg. C. Based on detailed studies at different heat-treatment temperatures using techniques such as X-ray diffraction, X-ray photoelectron spectroscopy, electron paramagnetic resonance, Raman spectroscopy, and Moessbauer spectroscopy, it has been established that formation of Eu 2 Ti 2 O 7 phase, wherein Eu 3+ ions occupy high symmetric environment (D 3d ) and also reduced distance between Eu 3+ and Eu 3+ ions is responsible for the decrease/loss in the luminescence intensity.

  9. Unconventional cells of TiO2 doped with erbium

    International Nuclear Information System (INIS)

    Ribeiro, P.C.; Campos, R.D.; Oliveira, A.S.; Wellen, R.; Diniz, V.C.S.; Costa, A.C.F.M. da

    2016-01-01

    The technology used in TiO_2 solar cells is in constant improvement, new configurations have been developed, aiming practicality and leading to efficiency increase of photovoltaic devices. This paper proposes a new technology for the production of solar cells in order to investigate a better utilization of solar spectrum of TiO2 doped with erbium (Er"3"+), proven by energetic conversion. The Ti_0_,_9Er_0_,_1O2 system was obtained by Pechini method. Nanoparticles have a crystallite size 65.30 nm and surface area 118.48 m"2/g. These characteristics are essential for the formation of the film to be deposited on the conductive glass substrate constituting the cell's photoelectrode. The other side of the cell is the platinum counter electrode. The cell will have the faces sealed by a thermoplastic and, finally the electrolyte will be inserted, then they will be electrically evaluated through energy efficiency and confronted with the literature data base. (author)

  10. Fabrication and characterization of TiO2-epoxy nanocomposite

    International Nuclear Information System (INIS)

    Chatterjee, Amit; Islam, Muhammad S.

    2008-01-01

    A systematic study has been conducted to investigate the matrix properties by introducing nanosize TiO 2 (5-40 nm, 0.5-2% by weight) fillers into an epoxy resin. Ultrasonic mixing process, via sonic cavitations, was employed to disperse the particles into the resin system. The thermal, mechanical, morphology and the viscoelastic properties of the nanocomposite and the neat resin were measured with TGA, DMA, TEM and Instron. The nano-particles are dispersed evenly throughout the entire volume of the resin. The nanofiller infusion improves the thermal, mechanical and viscoelastic properties of the epoxy resin. The nanocomposite shows increase in storage modulus, glass transition temperature, tensile modulus, flexural modulus and short beam shear strength from neat epoxy resin. The mechanical performance and thermal stability of the epoxy nanocomposites are depending on with the dispersion state of the TiO 2 in the epoxy matrix and are correlated with loading (0.0015-0.006% by volume). In addition, the nanocomposite shows enhanced flexural strength. Several reasons to explain these effects in terms of reinforcing mechanisms were discussed

  11. Novel selenium containing boro-phosphate glasses: Preparation and structural study

    International Nuclear Information System (INIS)

    Ciceo-Lucacel, R.; Radu, T.; Ponta, O.; Simon, V.

    2014-01-01

    We synthesized a new boro-phosphate glass system with different %mol SeO 2 content by conventional melt quenching technique. All samples were obtained in a glassy state with the vitreous structure confirmed by X-ray diffraction analysis. Scanning electron microscopy (SEM) revealed some non-homogeneous domains on the glasses surface, and their tendency to link each other once the selenium oxide content increases. Energy-dispersive X-ray analysis (EDAX) indicated similar elemental composition in different regions of each sample. X-ray photoelectron spectroscopy (XPS) was used to determine the nature of chemical bonding and the elemental composition at the sample surfaces, and Fourier transform infrared (FT-IR) spectroscopy was used to determine the structural groups in the obtained glass structure. Based on FT-IR results, the glass structure at short range order consists mainly of small phosphate units such as pyrophosphate (i.e. P 2 O 7 4− dimmers or terminating groups at the end of phosphate chains) and some metaphosphate (i.e. PO 3 − middle groups in the phosphate chains) units. The boron atoms are mainly placed in three-coordinated sites in BØ 3 or BØ 2 O − units. A small contribution of BØ 4 − units was also detected from the FT-IR spectra of glasses. For SeO 2 content higher than 5 mol%, the modifier role of selenium ions is strongly reflected on the local structure dominated in this case by pyrophosphate units. - Highlights: • New P 2 O 5 -CaO-B 2 O 3 -SeO 2 glasses synthesized by conventional melt quenching method. • Evidences for the Se ions modifier role in the local structure by FT-IR and XPS. • Significant advances in understanding the structural properties of the new system

  12. Novel selenium containing boro-phosphate glasses: preparation and structural study.

    Science.gov (United States)

    Ciceo-Lucacel, R; Radu, T; Ponta, O; Simon, V

    2014-06-01

    We synthesized a new boro-phosphate glass system with different %mol SeO2 content by conventional melt quenching technique. All samples were obtained in a glassy state with the vitreous structure confirmed by X-ray diffraction analysis. Scanning electron microscopy (SEM) revealed some non-homogeneous domains on the glasses surface, and their tendency to link each other once the selenium oxide content increases. Energy-dispersive X-ray analysis (EDAX) indicated similar elemental composition in different regions of each sample. X-ray photoelectron spectroscopy (XPS) was used to determine the nature of chemical bonding and the elemental composition at the sample surfaces, and Fourier transform infrared (FT-IR) spectroscopy was used to determine the structural groups in the obtained glass structure. Based on FT-IR results, the glass structure at short range order consists mainly of small phosphate units such as pyrophosphate (i.e. P2O7(4-) dimmers or terminating groups at the end of phosphate chains) and some metaphosphate (i.e. PO3(-) middle groups in the phosphate chains) units. The boron atoms are mainly placed in three-coordinated sites in BØ3 or BØ2O(-) units. A small contribution of BØ4(-) units was also detected from the FT-IR spectra of glasses. For SeO2 content higher than 5mol%, the modifier role of selenium ions is strongly reflected on the local structure dominated in this case by pyrophosphate units. Copyright © 2014 Elsevier B.V. All rights reserved.

  13. Ultrasonic and Thermal Properties of Borate and Phosphate Glasses Containing Bismuth and Lead

    International Nuclear Information System (INIS)

    Aziz, Sidek Hj. Abd.; Ahmad, Hamezan; Wahab, Zaidan A.; Sulaiman, Zainal Abidin; Talib, Zainal Abidin; Shaari, A. Halim; Senin, H. B.

    2007-01-01

    Systematic series of (B2O3,P2O5)-Bi2O3-PbO glasses have been successfully prepared by using the rapid quenching technique in which each oxide content changes for every series on the basis of its weight percentage. Their amorphous natures were confirmed earlier by the x-ray diffraction technique. The experimental results show that the density of both glasses, determined by using the Archimedes principle, increases with the glass modifier content. This is due to the replacement of Bi2O3 and PbO in the borate and phosphate glassy networks. The molar volume for borate glass increases with the addition of bismuth and lead oxides, but a reverse trend occurs for the phosphate glass. The longitudinal and shear ultrasound velocities, determined by the MBS 8000 system, of both lead bismuth borate and phosphate glasses show a decreasing trend as more PbO and Bi2O3 are added to the glass system. The increase in PbO/Bi2O3 content was probably related to the progressive increase in the concentration of non-bridging oxygen (NBOs). Thermal studies of the glass, using the Labsys DTA-Setaram machine, show that the value of the glass transition temperature (Tg) is closely related to the chemical bond in the system. In lead bismuth borate glasses, the addition of more Pb2+ and Bi3+ results in a more dominant ionic bond character in the system and hence decreases Tg of the sample. However, in lead bismuth phosphate glasses, the addition of Pb2+ and Bi3+ not only failed to weaken the covalent character in P-O-P bonds, but strengthened it further, leading to an increment in the values of Tg

  14. Photocatalytic antibacterial effects are maintained on resin-based TiO2 nanocomposites after cessation of UV irradiation.

    Directory of Open Access Journals (Sweden)

    Yanling Cai

    Full Text Available Photocatalysis induced by TiO2 and UV light constitutes a decontamination and antibacterial strategy utilized in many applications including self-cleaning environmental surfaces, water and air treatment. The present work reveals that antibacterial effects induced by photocatalysis can be maintained even after the cessation of UV irradiation. We show that resin-based composites containing 20% TiO2 nanoparticles continue to provide a pronounced antibacterial effect against the pathogens Escherichia coli, Staphylococcus epidermidis, Streptococcus pyogenes, Streptococcus mutans and Enterococcus faecalis for up to two hours post UV. For biomaterials or implant coatings, where direct UV illumination is not feasible, a prolonged antibacterial effect after the cessation of the illumination would offer new unexplored treatment possibilities.

  15. Superhydrophobicity construction with dye-sensitised TiO2 on fabric surface for both oil/water separation and water bulk contaminants purification

    Science.gov (United States)

    Yu, Linfeng; Zhang, Shengmiao; Zhang, Meng; Chen, Jianding

    2017-12-01

    For the promising material for both oil/water separation and water-soluble contaminants, the Dye@TiO2-TEOS/VTEO hybrid modified polyester fabric is developed by a simple dip-coating process, which combines Dye-sensitised TiO2 with silicon contained superhydrophobic coating to guarantee the long-term stability of Dye-sensitised TiO2 system as well as material's sustainability. The modified fabric possesses selective oil/water seperation properties towards water and oil, besides, mechanical, acid and alkali durability shows this material's appropriate performance on oil/water separation. UV-Vis absorption spectrum reveals the Dye 4-(2H-imidazol-2-ylazo) benzoic acid could sensitize the semiconductor TiO2 for visible light catalytic organic pollutant degradation that is also confirmed by methylene blue degradation experiment. Density Functional calculation (DFT) witnesses that HOMO, HOMO-1 of Dye contributed by oxygen bonding to TiO2 can insert into TiO2 band gap and result in low energy electron excitation. The ability of oil/water separation and water-soluble contaminants purification provides the material opportunity to practical applications in environmental restoration and human life.

  16. Photocatalytic activity of Al2O3-doped TiO2 thin films activated with visible light on the bacteria Escherichia coli

    International Nuclear Information System (INIS)

    Barajas-Ledesma, E.; Garcia-Benjume, M.L.; Espitia-Cabrera, I.; Bravo-Patino, A.; Espinoza-Beltran, F.J.; Mostaghimi, J.; Contreras-Garcia, M.E.

    2010-01-01

    Al 2 O 3 -doped TiO 2 thin films were prepared by combining electrophoretic deposition (EPD) with sputtering. A Corning* glass was used as a substrate, in which a titanium film was deposited by sputtering. Then, a precursor sol was prepared with Ti(n-OBu) 4 and Al(s-OBu) 3 and used as the medium for EPD. Next, the thin films were sintered and, finally, characterised by scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD). Several cultures of Escherichia coli, strain XL1-Blue, were prepared. Nine experiments were carried out. In three of them, an inoculum (a low amount of a product that contains bacteria) was prepared without a film; in the other six Al 2 O 3 -doped TiO 2 film-coated glass substrates were irradiated with visible light before they were introduced in the inoculum. The SEM and EDS results showed that TiO 2 -Al 2 O 3 films were obtained, covering all the glass substrate and with uniform size of particles forming them, and that the aluminium was distributed uniformly on the film. XRD results showed that rutile phase was obtained. By TEM, the structure of TiO 2 was demonstrated. Al 2 O 3 -doped TiO 2 thin films were successful at eliminating E. coli.

  17. Photocatalytic mechanism of high-activity anatase TiO2 with exposed (001) facets from molecular-atomic scale: HRTEM and Raman studies

    Science.gov (United States)

    Wu, Jun; Shi, Chentian; Zhang, Yupeng; Fu, Qiang; Pan, Chunxu

    2017-12-01

    Anatase TiO2 with a variant percentage of exposed (001) facets was prepared under hydrothermal processes by adjusting the volume of HF, and the photocatalytic mechanism was studied from atomic-molecular scale by HRTEM and Raman spectroscopy. It was revealed that: 1) From HRTEM observations, the surface of original TiO2 with exposed (001) facets was clean without impurity, and the crystal lattice was clear and completed; however, when mixed with methylene blue (MB) solution, there were many 1 nm molecular absorbed at the surface of TiO2; after the photocatalytic experiment, MB molecules disappeared and the TiO2 lattice image became fuzzy. 2) The broken path of the MB chemical bond was obtained by Raman spectroscopy, i.e., after the irradiation of the light, the vibrational mode of C-N-C disappeared due to the chemical bond breakage, and the groups containing C-N bond and carbon rings were gradually decomposed. Accordingly, we propose that the driving force for breaking the chemical bond and the disappearance of groups is from the surface lattice distortion of TiO2 during photocatalyzation.

  18. Application of TiO_2 nanofibers, electrospinning obtained, the production of hydrogen

    International Nuclear Information System (INIS)

    Soares, L.G.; Bergmann, C.P.; Alves, A.K.

    2014-01-01

    Electrospinning is a simple, low cost which promotes the production of a large amount of nanofibers. The process of applying an electrode connected to a high voltage source, inserted into the polymer solution contained in a capillary tube. With increasing voltage, the surface of the droplet elongates to form a cone when the electrostatic forces overcome the surface tension of a spray solution on the edge of the cone is ejected. In this work, TiO_2 nanofibers obtained by electrospinning, were thermally treated at 650, 700, 750 and 800 ° C, and its photoactivity was evaluated. The technique of X-ray diffraction (XRD) was employed to determine the crystal structure and crystallite size and morphology of the fibers was analyzed by scanning electron microscopy (SEM). The results indicate that the nanofibers containing the anatase phase in larger quantities can be applied to the production of hydrogen. (author)

  19. New insights into the origin of visible-light photocatalytic activity in Se-modified anatase TiO2 from screened coulomb hybrid DFT calculations

    KAUST Repository

    Harb, Moussab

    2013-12-05

    We report a systematic study on the optoelectronic properties of Se-modified anatase TiO2 investigated by DFT (including the perturbation theory approach DFPT) within the screened coulomb hybrid HSE06 formalism to guarantee accurate band gap and electronic excitation predictions. Various selenium species at substitutional sites for O or Ti, at interstitial sites, as well as at mixed substitutional/interstitial sites are studied. Among the explored structures, Ti(1-2x)O2Se2x (containing Se4+ species), TiO(2-x)Sex (containing Se2- species), and TiO(2-x)Se2x (containing Se2 2- species) reveal significant enhanced visible-light optical absorption spectra with new absorption features appearing at 500, 600, and 690 nm, respectively. Our calculated spectra are found to be in good agreement with those obtained in available experimental works. The band gap narrowing in these materials originates from incorporation of newly occupied electronic levels within 0.5-1.5 eV above the original valence band of TiO 2, leading to new narrowed band gaps of 2.5, 2.0, and 1.8 eV respectively. Our calculations also reveal suitable band positions of Ti (1-2x)O2Se2x and TiO(2-x)Se x for overall water splitting, whereas TiO(2-x)Se 2x shows an unsuitable valence band position for the oxygen evolution reaction. In contrast, the localized electronic character of the new occupied states on the Se 4p orbitals and only on the O 2p orbitals linked to the Se species makes the holes mobility limited in this material and the recombination rate of charge carriers greatly increased in the bulk. © 2013 American Chemical Society.

  20. Trace elements in rock phosphates and P containing mineral and organo-mineral fertilizers sold in Germany

    Energy Technology Data Exchange (ETDEWEB)

    Kratz, Sylvia, E-mail: sylvia.kratz@jki.bund.de; Schick, Judith; Schnug, Ewald

    2016-01-15

    68 rock phosphates and 162 P containing (organo-)mineral fertilizers sold in Germany were evaluated with regard to trace element contents. While Al, As, B, Be, Cd, Cr, Mo, Ni, Pb, Sb, Se, Tl, U, and Zn were higher in sedimentary than in igneous rock phosphates, the opposite was true for Co, Cu, Sn, Mn, Ti, Fe, and Sr. Comparing element concentrations to the currently valid legal limit values defined by the German Fertilizer Ordinance, it was found that some PK and many straight P fertilizers (superphosphate, triple superphosphate, partly acidulated rock phosphates) exceeded the limit of 50 mg Cd/kg P{sub 2}O{sub 5}. Mean values for As, Ni, Pb, and Tl remained below legal limits in almost all cases. While no legal limit has been defined for U in Germany yet, the limit of 50 mg U/kg P{sub 2}O{sub 5} for P containing fertilizers proposed by the German Commission for the Protection of Soils was clearly exceeded by mean values for all fertilizer types analyzed. A large share of the samples evaluated in this work contained essential trace elements at high concentrations, with many of them not being declared as such. Furthermore, trace elements supplied with these fertilizers at a fertilization rate leveling P uptake would exceed trace element uptake by crops. This may become most relevant for B and Fe, since many crops are sensitive to an oversupply of B, and Fe loads exceeding plant uptake may immobilize P supplies for the crops by forming Fe phosphate salts. The sample set included two products made from thermochemically treated sewage sludge ash. The products displayed very high concentrations of Fe and Mn and exceeded the legal limit for Ni, emphasizing the necessity to continue research on heavy metal removal from recycled raw materials and the development of environmentally friendly and agriculturally efficient fertilizer products. - Highlights: • Mineral fertilizers (MF) sold in Germany often exceed legal limits for Cd • MF sold in Germany contain high

  1. Study of the radionuclides contained in wastes produced by the phosphate industry and their impact on the environment

    International Nuclear Information System (INIS)

    Baetsle, L.H.

    1991-01-01

    This report reviews the present state of the management and disposal of waste associated with mining, milling and reprocessing of phosphate ores with regard to its content on naturally occurring radionuclides. The main areas of investigation are: phosphate ores and their characteristics and phosphate trade in the Member States of the European Community, production and processing methods of phosphoric acids and phosphates, interaction of phosphate products and wastes with the environment, standards and regulations for radioactivity released during processing in the phosphate industry

  2. Electrical conductivity characteristic of TiO2 nanowires from hydrothermal method

    International Nuclear Information System (INIS)

    Othman, Mohd Azlishah; Amat, Noor Faridah; Ahmad, Badrul Hisham; Rajan, Jose

    2014-01-01

    One dimensional nanostructures of titanium dioxide (TiO 2 ) were synthesized via hydrothermal method by mixing TiO 2 as precursor in aqueous solution of NaOH as solvent. Then, heat and washing treatment was applied. Thus obtained wires had diameter ∼15 nm. TiO 2 nanowires will be used as a network in solar cell such dye-sensitized solar cell in order to improve the performance of electron movement in the device. To improve the performance of electron movement, the characteristics of TiO 2 nanowires have been analyses using field emission scanning electron microscopy (FESEM) analysis, x-ray diffractometer (XRD) analysis and brunauer emmett teller (BET) analysis. Finally, electrical conductivity of TiO 2 nanowires was determined by measuring the resistance of the TiO 2 nanowires paste on microscope glass.

  3. Optimization of photoelectrochemical water splitting performance on hierarchical TiO 2 nanotube arrays

    KAUST Repository

    Zhang, Z.; Wang, Peng

    2012-01-01

    In this paper, we show that by varying the voltages during two-step anodization the morphology of the hierarchical top-layer/bottom-tube TiO 2 (TiO 2 NTs) can be finely tuned between nanoring/nanotube, nanopore/nanotube, and nanohole-nanocave/nanotube morphologies. This allows us to optimize the photoelectrochemical (PEC) water splitting performance on the hierarchical TiO 2 NTs. The optimized photocurrent density and photoconversion efficiency in this study, occurring on the nanopore/nanotube TiO 2 NTs, were 1.59 mA cm -2 at 1.23 V vs. RHE and 0.84% respectively, which are the highest values ever reported on pristine TiO 2 materials under illumination of AM 1.5G. Our findings contribute to further improvement of the energy conversion efficiency of TiO 2-based devices.

  4. Photodegradation of Reactive Golden Yellow R Dye Catalyzed by Effective Titania (TiO2)

    International Nuclear Information System (INIS)

    Bedurus, E.A.; Marinah Mohd Ariffin; Mohd Hasmizam Razali

    2015-01-01

    In the present research, Microwave Assisted Synthesis (MAS) method was applied to synthesize titania (TiO 2 ) at 150 degree Celsius in a range of 2-6 hours heating time. Each prepared TiO 2 were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and nitrogen gas (N 2 ) sorption analysis (Brunaeur-Emmett-Teller (BET) and Barrett-Joyner-Halenda (BJH) calculation) techniques. The TiO 2 prepared by MAS 150 degree Celsius (4 hours) has emerged with the highest photo catalytic activity. Within 4 hours, the TiO 2 managed to catalyze the degradation of Reactive Golden Yellow R dye up to 98.51 %. This is because of the TiO 2 possessed high crystallinity of anatase phase, small crystallite size and high pore volume compared to other prepared TiO 2 . (author)

  5. Optimization of photoelectrochemical water splitting performance on hierarchical TiO 2 nanotube arrays

    KAUST Repository

    Zhang, Z.

    2012-02-10

    In this paper, we show that by varying the voltages during two-step anodization the morphology of the hierarchical top-layer/bottom-tube TiO 2 (TiO 2 NTs) can be finely tuned between nanoring/nanotube, nanopore/nanotube, and nanohole-nanocave/nanotube morphologies. This allows us to optimize the photoelectrochemical (PEC) water splitting performance on the hierarchical TiO 2 NTs. The optimized photocurrent density and photoconversion efficiency in this study, occurring on the nanopore/nanotube TiO 2 NTs, were 1.59 mA cm -2 at 1.23 V vs. RHE and 0.84% respectively, which are the highest values ever reported on pristine TiO 2 materials under illumination of AM 1.5G. Our findings contribute to further improvement of the energy conversion efficiency of TiO 2-based devices.

  6. Engineering of highly ordered TiO2 nanopore arrays by anodization

    Science.gov (United States)

    Wang, Huijie; Huang, Zhennan; Zhang, Li; Ding, Jie; Ma, Zhaoxia; Liu, Yong; Kou, Shengzhong; Yang, Hangsheng

    2016-07-01

    Finite element analysis was used to simulate the current density distributions in the TiO2 barrier layer formed at the initial stage of Ti anodization. The morphology modification of the barrier layer was found to induce current density distribution change. By starting the anodization with proper TiO2 barrier layer morphology, the current density distribution can be adjusted to favor the formation of either nanotube arrays or nanopore arrays of anodic TiO2. We also found that the addition of sodium acetate into the electrolyte suppressed both the field-assisted chemical dissolution of TiO2 and the TiF62- hydrolysis induced TiO2 deposition during anodization, and thus further favored the nanopore formation. Accordingly, highly ordered anodic TiO2 nanopore arrays, similar to anodic aluminum oxide nanopore arrays, were successfully prepared.

  7. XRD analysis of undoped and Fe doped TiO2 nanoparticles by Williamson Hall method

    International Nuclear Information System (INIS)

    Bharti, Bandna; Barman, P. B.; Kumar, Rajesh

    2015-01-01

    Undoped and Fe doped titanium dioxide (TiO 2 ) nanoparticles were synthesized by sol-gel method at room temperature. The synthesized samples were annealed at 500°C. For structural analysis, the prepared samples were characterized by X-ray diffraction (XRD). The crystallite size of TiO 2 and Fe doped TiO 2 nanoparticles were calculated by Scherer’s formula, and was found to be 15 nm and 11 nm, respectively. Reduction in crystallite size of TiO 2 with Fe doping was observed. The anatase phase of Fe-doped TiO 2 nanoparticles was also confirmed by X-ray diffraction. By using Williamson-Hall method, lattice strain and crystallite size were also calculated. Williamson–Hall plot indicates the presence of compressive strain for TiO 2 and tensile strain for Fe-TiO 2 nanoparticles annealed at 500°C

  8. Effect of surface ethoxy groups on photoactivity of TiO2 nanocrystals

    International Nuclear Information System (INIS)

    Tian Lihong; Deng Kejian; Ye Liqun; Zan Lin

    2011-01-01

    TiO 2 nanocrystals modified by ethoxy groups were prepared by a facile nonhydrolytic solvothermal method and characterized by XRD, TEM, TG-DTA and XPS, which showed an enhanced visible-light photocatalytic activity on the degradation of Rhodamine B compared with TiO 2 modified by benzyloxy groups and the 'naked' TiO 2 . The adsorption and degradation pathway of Rhodamine B on TiO 2 modified by ethoxy groups were also investigated. The zeta-potential (ζ) results showed that the TiO 2 modified by ethoxy groups had high negative surface charge, which incited the positive -N(Et) 2 group of RhB absorbing on the TiO 2 surface and preferably led the N-dealkylation pathway under visible light irradiation.

  9. Graphene-enhanced Raman imaging of TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Naumenko, Denys; Snitka, Valentinas; Snopok, Boris; Arpiainen, Sanna; Lipsanen, Harri

    2012-01-01

    The interaction of anatase titanium dioxide (TiO 2 ) nanoparticles with chemical vapour deposited graphene sheets transferred on glass substrates is investigated by using atomic force microscopy, Raman spectroscopy and imaging. Significant electronic interactions between the nanoparticles of TiO 2 and graphene were found. The changes in the graphene Raman peak positions and intensity ratios indicate that charge transfer between graphene and TiO 2 nanoparticles occurred, increasing the Raman signal of the TiO 2 nanoparticles up to five times. The normalized Raman intensity of TiO 2 nanoparticles per their volume increased with the disorder of the graphene structure. The complementary reason for the observed enhancement is that due to the higher density of states in the defect sites of graphene, a higher electron transfer occurs from the graphene to the anatase TiO 2 nanoparticles. (paper)

  10. Enhanced photoelectrochemical and photocatalytic activity of WO3-surface modified TiO2 thin film

    Science.gov (United States)

    Qamar, Mohammad; Drmosh, Qasem; Ahmed, Muhammad I.; Qamaruddin, Muhammad; Yamani, Zain H.

    2015-02-01

    Development of nanostructured photocatalysts for harnessing solar energy in energy-efficient and environmentally benign way remains an important area of research. Pure and WO3-surface modified thin films of TiO2 were prepared by magnetron sputtering on indium tin oxide glass, and photoelectrochemical and photocatalytic activities of these films were studied. TiO2 particles were <50 nm, while deposited WO3 particles were <20 nm in size. An enhancement in the photocurrent was observed when the TiO2 surface was modified WO3 nanoparticles. Effect of potential, WO3 amount, and radiations of different wavelengths on the photoelectrochemical activity of TiO2 electrodes was investigated. Photocatalytic activity of TiO2 and WO3-modified TiO2 for the decolorization of methyl orange was tested.

  11. Electrochemical Behavior of TiO2 Nanoparticle Doped WO3 Thin Films

    Directory of Open Access Journals (Sweden)

    Suvarna R. Bathe

    2014-01-01

    Full Text Available Nanoparticle TiO2 doped WO3 thin films by pulsed spray pyrolysis technique have been studied on fluorine tin doped (FTO and glass substrate. XRD shows amorphous nature for undoped and anatase phase of TiO2 having (101 plane for nanoparticle TiO2 doped WO3 thin film. SEM shows microfibrous reticulated porous network for WO3 with 600 nm fiber diameter and nanocrystalline having size 40 nm for TiO2 nanoparticle doped WO3 thin film. TiO2 nanoparticle doped WO3 thin film shows ~95% reversibility due to may be attributed to nanocrystalline nature of the film, which helpful for charge insertion and deinsertion process. The diffusion coefficient for TiO2 nanoparticle doped WO3 film is less than undoped WO3.

  12. Ammonia Sensing Behaviors of TiO2-PANI/PA6 Composite Nanofibers

    Directory of Open Access Journals (Sweden)

    Fenglin Huang

    2012-12-01

    Full Text Available Titanium dioxide-polyaniline/polyamide 6 (TiO2-PANI/PA6 composite nanofibers were prepared by in situ polymerization of aniline in the presence of PA6 nanofibers and a sputtering-deposition process with a high purity titanium sputtering target. TiO2-PANI/PA6 composite nanofibers and PANI/PA6 composite nanofibers were fabricated for ammonia gas sensing. The ammonia sensing behaviors of the sensors were examined at room temperature. All the results indicated that the ammonia sensing property of TiO2-PANI/PA6 composite nanofibers was superior to that of PANI/PA6 composite nanofibers. TiO2-PANI/PA6 composite nanofibers had good selectivity to ammonia. It was also found that the content of TiO2 had a great influence on both the morphology and the sensing property of TiO2-PANI/PA6 composite nanofibers.

  13. Eco-friendly synthesis of TiO2, Au and Pt doped TiO2 nanoparticles for dye sensitized solar cell applications and evaluation of toxicity

    Science.gov (United States)

    Gopinath, K.; Kumaraguru, S.; Bhakyaraj, K.; Thirumal, S.; Arumugam, A.

    2016-04-01

    Driven by the demand of pure TiO2, Au and Pt doped TiO2 NPs were successfully synthesized using Terminalia arjuna bark extract. The eco-friendly synthesized NPs were characterized by UV-Vis-DRS, ATR-FT-IR, PL, XRD, Raman, SEM with EDX and TEM analysis. The synthesized NPs were investigation for dye sensitized solar cell applications. UV-Vis-Diffused Reflectance Spectra clearly showed that the expected TiO2 inter band absorption below 306 nm, incorporation of gold shows surface plasma resonant (SPR) near 555 nm and platinum incorporated TiO2 NPs shows absorbance at 460 nm. The energy conversion efficiency for Au doped TiO2 NPs when compared to pure and Pt doped TiO2 NPs. In addition to that, Au noble metal present TiO2 matrix and an improve open-circuit voltage (Voc) of DSSC. Synthesized NPs was evaluated into antibacterial and antifungal activities by disk diffusion method. It is observed that NPs have not shown any activities in all tested bacterial and fungal strains. In this eco-friendly synthesis method to provide non toxic and environmental friendly nanomaterials can be used for solar energy device application.

  14. TiO2 nanofiber solid-state dye sensitized solar cells with thin TiO2 hole blocking layer prepared by atomic layer deposition

    International Nuclear Information System (INIS)

    Li, Jinwei; Chen, Xi; Xu, Weihe; Nam, Chang-Yong; Shi, Yong

    2013-01-01

    We incorporated a thin but structurally dense TiO 2 layer prepared by atomic layer deposition (ALD) as an efficient hole blocking layer in the TiO 2 nanofiber based solid-state dye sensitized solar cell (ss-DSSC). The nanofiber ss-DSSCs having ALD TiO 2 layers displayed increased open circuit voltage, short circuit current density, and power conversion efficiency compared to control devices with blocking layers prepared by spin-coating liquid TiO 2 precursor. We attribute the improved photovoltaic device performance to the structural integrity of ALD-coated TiO 2 layer and consequently enhanced hole blocking effect that results in reduced dark leakage current and increased charge carrier lifetime. - Highlights: • TiO 2 blocking locking layer prepared by atomic layer deposition (ALD) method. • ALD-coated TiO 2 layer enhanced hole blocking effect. • ALD blocking layer improved the voltage, current and efficiency. • ALD blocking layer reduced dark leakage current and increased electron lifetime

  15. Stabilization Using Phosphate Bonded Ceramics. Salt Containing Mixed Waste Treatment. Mixed Waste Focus Area. OST Reference No. 117

    International Nuclear Information System (INIS)

    1999-01-01

    Throughout the Department of Energy (DOE) complex there are large inventories of homogeneous mixed waste solids, such as wastewater treatment residues, fly ashes, and sludges that contain relatively high concentrations (greater than 15% by weight) of salts. The inherent solubility of salts (e.g., nitrates, chlorides, and sulfates) makes traditional treatment of these waste streams difficult, expensive, and challenging. One alternative is low-temperature stabilization by chemically bonded phosphate ceramics (CBPCs). The process involves reacting magnesium oxide with monopotassium phosphate with the salt waste to produce a dense monolith. The ceramic makes a strong environmental barrier, and the metals are converted to insoluble, low-leaching phosphate salts. The process has been tested on a variety of surrogates and actual mixed waste streams, including soils, wastewater, flyashes, and crushed debris. It has also been demonstrated at scales ranging from 5 to 55 gallons. In some applications, the CBPC technology provides higher waste loadings and a more durable salt waste form than the baseline method of cementitious grouting. Waste form test specimens were subjected to a variety of performance tests. Results of waste form performance testing concluded that CBPC forms made with salt wastes meet or exceed both RCRA and recommended Nuclear Regulatory Commission (NRC) low-level waste (LLW) disposal criteria. Application of a polymer coating to the CBPC may decrease the leaching of salt anions, but continued waste form evaluations are needed to fully assess the deteriorating effects of this leaching, if any, over time.

  16. On calculation of the electrostatic potential of a phosphatidylinositol phosphate-containing phosphatidylcholine lipid membrane accounting for membrane dynamics.

    Directory of Open Access Journals (Sweden)

    Jonathan C Fuller

    Full Text Available Many signaling events require the binding of cytoplasmic proteins to cell membranes by recognition of specific charged lipids, such as phosphoinositol-phosphates. As a model for a protein-membrane binding site, we consider one charged phosphoinositol phosphate (PtdIns(3P embedded in a phosphatidylcholine bilayer. As the protein-membrane binding is driven by electrostatic interactions, continuum solvent models require an accurate representation of the electrostatic potential of the phosphoinositol phosphate-containing membrane. We computed and analyzed the electrostatic potentials of snapshots taken at regular intervals from molecular dynamics simulations of the bilayer. We observe considerable variation in the electrostatic potential of the bilayer both along a single simulation and between simulations performed with the GAFF or CHARMM c36 force fields. However, we find that the choice of GAFF or CHARMM c36 parameters has little effect on the electrostatic potential of a given configuration of the bilayer with a PtdIns(3P embedded in it. From our results, we propose a remedian averaging method for calculating the electrostatic potential of a membrane system that is suitable for simulations of protein-membrane binding with a continuum solvent model.

  17. Engineering the TiO2 -graphene interface to enhance photocatalytic H2 production.

    Science.gov (United States)

    Liu, Lichen; Liu, Zhe; Liu, Annai; Gu, Xianrui; Ge, Chengyan; Gao, Fei; Dong, Lin

    2014-02-01

    In this work, TiO2 -graphene nanocomposites are synthesized with tunable TiO2 crystal facets ({100}, {101}, and {001} facets) through an anion-assisted method. These three TiO2 -graphene nanocomposites have similar particle sizes and surface areas; the only difference between them is the crystal facet exposed in TiO2 nanocrystals. UV/Vis spectra show that band structures of TiO2 nanocrystals and TiO2 -graphene nanocomposites are dependent on the crystal facets. Time-resolved photoluminescence spectra suggest that the charge-transfer rate between {100} facets and graphene is approximately 1.4 times of that between {001} facets and graphene. Photoelectrochemical measurements also confirm that the charge-separation efficiency between TiO2 and graphene is greatly dependent on the crystal facets. X-ray photoelectron spectroscopy reveals that Ti-C bonds are formed between {100} facets and graphene, while {101} facets and {001} facets are connected with graphene mainly through Ti-O-C bonds. With Ti-C bonds between TiO2 and graphene, TiO2 -100-G shows the fastest charge-transfer rate, leading to higher activity in photocatalytic H2 production from methanol solution. TiO2 -101-G with more reductive electrons and medium interfacial charge-transfer rate also shows good H2 evolution rate. As a result of its disadvantageous electronic structure and interfacial connections, TiO2 -001-G shows the lowest H2 evolution rate. These results suggest that engineering the structures of the TiO2 -graphene interface can be an effective strategy to achieve excellent photocatalytic performances. Copyright © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  18. Comparison of one-, two-, and three-dimensional iron phosphates containing ethylenediamine

    International Nuclear Information System (INIS)

    Song Yanning; Zavalij, Peter Y.; Chernova, Natasha A.; Suzuki, Masatsugu; Whittingham, M.S.

    2003-01-01

    A new two-dimensional (2d) iron phosphate, (C 2 N 2 H 10 )Fe 2 O(PO 4 ) 2 , has been synthesized under hydrothermal conditions in the system of FeCl 3 -H 3 PO 4 -C 2 N 2 H 8 -H 2 O. The crystal data is: space group P2 1 /c, a=10.670(1) A, b=10.897(1) A, c=9.918(1) A, β=105.632(1) deg. , Z=4. The layered structure consists of double sheet layers, of composition Fe 2 O(PO 4 ) 2 , built from FeO 5 trigonal bipyramids and PO 4 tetrahedra. The amine holds the layers together via H-bonding. The study of the magnetic properties reveals two magnetic transitions at 160 and 30 K with spin-glass-like behavior below 160 K. By varying the hydrothermal conditions, three other iron phosphates were synthesized: the one-dimensional (1d) (C 2 N 2 H 10 )Fe(HPO 4 ) 2 (OH)·H 2 O, the 2d (C 2 N 2 H 10 )Fe 2 (PO 4 ) 2 (OH) 2 , and the three-dimensional (3d) (C 2 N 2 H 10 ) 2 Fe 4 O(PO 4 ) 4 ·H 2 O. The 1d compound can be used as the starting reagent in the synthesis of both the 2d compound and the 3d lipscombite Fe 3 (PO 4 ) 2 (OH) 2 due to the similar building blocks in their structures. In the 3d phosphate (C 2 N 2 H 10 ) 2 Fe 4 O(PO 4 ) 4 ·H 2 O, manganese can substitute for half of the iron atoms. Magnetic study shows ordering transitions at about 30 K, however, manganese substitution depresses the magnetic ordering temperature

  19. Biological performance of titania containing phosphate-based glasses for bone tissue engineering applications

    International Nuclear Information System (INIS)

    Abou Neel, Ensanya Ali; Chrzanowski, Wojciech; Knowles, Jonathan Campbell

    2014-01-01

    The interplay between glass chemistry, structure, degradation kinetics, and biological activity provides flexibility for the development of scaffolds with highly specific cellular response. The aim of this study was therefore to investigate the role of titania inclusion into the phosphate-based glass on its ability to stimulate osteoblast-like human osteosarcoma (HOS) cells to adhere, proliferate and differentiate. In depth morphological and biochemical characterisation was performed on HOS cells cultured on the surface of glass discs. Cell proliferation was also studied in the presence of the glass extract. Cell differentiation, through osteoblast phenotype genes, alkaline phosphatase (ALP) activity and osteocalcin production, was carried out using normal or osteogenic media. Both Thermanox® and titania free glass were used as controls. The data demonstrated that titania inclusion provides desired cytocompatible surface that supported initial cell attachment, sustained viability, and increased cell proliferation similar or significantly higher than Thermanox®. The modified glasses regulated osteoblastic cell differentiation as detected by osteoblast phenotype gene transcription and upregulated ALP and osteocalcin expression. Using osteogenic media had no significant effect on ALP activity and osteocalcin expression. Therefore, titania modified phosphate glasses may have future use as bone tissue engineering scaffolds. - Highlights: • This study investigated the role of titania on the biological response of phosphate glasses. • Incorporation of titania improved HOS cell attachment, viability and proliferation. • Titania modified glasses regulated osteoblastic cell differentiation. • Using osteogenic media had no significant effect on cell differentiation. • Titania modified glasses may have future use as bone tissue engineering scaffolds

  20. Novel selenium containing boro-phosphate glasses: Preparation and structural study

    Energy Technology Data Exchange (ETDEWEB)

    Ciceo-Lucacel, R.; Radu, T., E-mail: teodora.radu@phys.ubbcluj.ro; Ponta, O.; Simon, V.

    2014-06-01

    We synthesized a new boro-phosphate glass system with different %mol SeO{sub 2} content by conventional melt quenching technique. All samples were obtained in a glassy state with the vitreous structure confirmed by X-ray diffraction analysis. Scanning electron microscopy (SEM) revealed some non-homogeneous domains on the glasses surface, and their tendency to link each other once the selenium oxide content increases. Energy-dispersive X-ray analysis (EDAX) indicated similar elemental composition in different regions of each sample. X-ray photoelectron spectroscopy (XPS) was used to determine the nature of chemical bonding and the elemental composition at the sample surfaces, and Fourier transform infrared (FT-IR) spectroscopy was used to determine the structural groups in the obtained glass structure. Based on FT-IR results, the glass structure at short range order consists mainly of small phosphate units such as pyrophosphate (i.e. P{sub 2}O{sub 7}{sup 4−} dimmers or terminating groups at the end of phosphate chains) and some metaphosphate (i.e. PO{sub 3}{sup −} middle groups in the phosphate chains) units. The boron atoms are mainly placed in three-coordinated sites in BØ{sub 3} or BØ{sub 2}O{sup −} units. A small contribution of BØ{sub 4}{sup −} units was also detected from the FT-IR spectra of glasses. For SeO{sub 2} content higher than 5 mol%, the modifier role of selenium ions is strongly reflected on the local structure dominated in this case by pyrophosphate units. - Highlights: • New P{sub 2}O{sub 5}-CaO-B{sub 2}O{sub 3}-SeO{sub 2} glasses synthesized by conventional melt quenching method. • Evidences for the Se ions modifier role in the local structure by FT-IR and XPS. • Significant advances in understanding the structural properties of the new system.

  1. Characterization of manufactured TiO2 nanoparticles

    Science.gov (United States)

    Motzkus, C.; Macé, T.; Vaslin-Reimann, S.; Ausset, P.; Maillé, M.

    2013-04-01

    Technological advances in nanomaterials have allowed the development of new applications in industry, increasing the probability of finding airborne manufactured and engineered nano-objects in the workplace, as well as in ambient air. Scientific studies on health and environmental risks have indicated that airborne nano-objects in ambient air have potential adverse effects on the health of exposed workers and the general population. For regulatory purposes, ambient measurements of particulate matter are based on the determination of mass concentrations for PM10 and PM2.5, as regulated in the European Directive 2008/50/EC. However, this legislation is not suitable for airborne manufactured and engineered nano-objects. Parameters characterising ultrafine particles, such as particle number concentration and size distribution, are under consideration for future health-based legislation, to monitor workplaces and to control industrial processes. Currently, there are no existing regulations covering manufactured airborne nano-objects. There is therefore a clear, unaddressed need to focus on the toxicology and exposure assessment of nano-objects such as titanium dioxide (TiO2), which are manufactured and engineered in large quantities in industry. To perform reliable toxicology studies it is necessary to determine the relevant characteristics of nano-objects, such as morphology, surface area, agglomeration, chemical composition, particle size and concentration, by applying traceable methods. Manufacturing of nanomaterials, and their use in industrial applications, also require traceable characterisation of the nanomaterials, particularly for quality control of the process. The present study arises from the OECD WPMN sponsorship programme, supported by the French Agency for Environmental and Occupational Health Safety (ANSES), in order to develop analytical methods for the characterization of TiO2 nanoparticles in size and count size distribution, based on different techniques to characterize five different manufactured TiO2 nanoparticles. In this study, different measurement techniques have been implemented: Transmission Electron Microscopy (TEM), Scanning Mobility Particle Sizer (SMPS) and Aerodynamic Particle Sizer (APS). The TEM results lead to a relatively good agreement between data from the manufacturer and our characterizations of primary particle size. With regard to the dustiness, the results show a strong presence of agglomerates / aggregates of primary particles and a significant presence of emitted airborne nanoparticles with a diameter below 100 nm (composed of isolated primary particles and small aggregates / agglomerates formed from a few primary particles): the number proportion of these particles varies from 0 to 44 % in the measurement range 14-360 nm depending on the types of powders and corrections of measurements.

  2. Characterization of manufactured TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Motzkus, C; Macé, T; Vaslin-Reimann, S; Ausset, P; Maillé, M

    2013-01-01

    Technological advances in nanomaterials have allowed the development of new applications in industry, increasing the probability of finding airborne manufactured and engineered nano-objects in the workplace, as well as in ambient air. Scientific studies on health and environmental risks have indicated that airborne nano-objects in ambient air have potential adverse effects on the health of exposed workers and the general population. For regulatory purposes, ambient measurements of particulate matter are based on the determination of mass concentrations for PM10 and PM2.5, as regulated in the European Directive 2008/50/EC. However, this legislation is not suitable for airborne manufactured and engineered nano-objects. Parameters characterising ultrafine particles, such as particle number concentration and size distribution, are under consideration for future health-based legislation, to monitor workplaces and to control industrial processes. Currently, there are no existing regulations covering manufactured airborne nano-objects. There is therefore a clear, unaddressed need to focus on the toxicology and exposure assessment of nano-objects such as titanium dioxide (TiO 2 ), which are manufactured and engineered in large quantities in industry. To perform reliable toxicology studies it is necessary to determine the relevant characteristics of nano-objects, such as morphology, surface area, agglomeration, chemical composition, particle size and concentration, by applying traceable methods. Manufacturing of nanomaterials, and their use in industrial applications, also require traceable characterisation of the nanomaterials, particularly for quality control of the process. The present study arises from the OECD WPMN sponsorship programme, supported by the French Agency for Environmental and Occupational Health Safety (ANSES), in order to develop analytical methods for the characterization of TiO 2 nanoparticles in size and count size distribution, based on different techniques to characterize five different manufactured TiO 2 nanoparticles. In this study, different measurement techniques have been implemented: Transmission Electron Microscopy (TEM), Scanning Mobility Particle Sizer (SMPS) and Aerodynamic Particle Sizer (APS). The TEM results lead to a relatively good agreement between data from the manufacturer and our characterizations of primary particle size. With regard to the dustiness, the results show a strong presence of agglomerates / aggregates of primary particles and a significant presence of emitted airborne nanoparticles with a diameter below 100 nm (composed of isolated primary particles and small aggregates / agglomerates formed from a few primary particles): the number proportion of these particles varies from 0 to 44 % in the measurement range 14-360 nm depending on the types of powders and corrections of measurements.

  3. Some studies on the extraction of plutonium from phosphate containing nitric acid solutions using DBDECMP as extractant

    International Nuclear Information System (INIS)

    Sagar, V.B.; Oak, M.S.; Pawar, S.M.; Sivaramakrishnan, C.K.; Patil, S.K.

    1991-01-01

    Extraction studies have been carried out to explore the feasibility of separation of Pu(IV) from phosphate containing analytical wastes generated in the laboratory. Distribution data on the extraction of Pu(IV) from DBDECMP (di-butyl,N,N-diethylcarbamoyl methyl phosphonate) in xylene an aqueous nitric acid and its mixture with sulfuric as well as with sulfuric and phosphoric acids were obtained. Based on the data obtained, the conditions for the recovery of plutonium from such water solutions are suggested. (author) 7 refs.; 1 fig.; 3 tabs

  4. Effect of nanosecond UV laser irradiation on luminescence and absorption in silver- and copper-containing phosphate glasses

    Science.gov (United States)

    Murashov, A. A.; Sidorov, A. I.; Stoliarchuk, M. V.

    2018-03-01

    Experimental evidence is presented that nanosecond UV laser irradiation of silver- and copper-containing barium phosphate glasses leads to luminescence quenching in the visible range. Subsequent heat treatment induces an absorption in the range 350–500 nm. These effects are due to the ionisation and fragmentation of subnanometre molecular clusters by laser radiation and subsequent (heat treatment-induced) formation of nanoparticles possessing plasmon resonance. Our numerical modelling results demonstrate the feasibility of producing stable AgnCum hybrid molecular clusters in glass. Local modification of the optical properties of glass by laser light can be used for optical information recording.

  5. Determination of radioactive levels in phosphate-containing fertilizers, copper and gold ores by direct gamma ray spectroscopy

    International Nuclear Information System (INIS)

    Constantinescu, B.; Constantin, F.; Dusoiu, M.; Pascovici, G.; Macovei, M.

    1993-01-01

    Two particular aspects of the role played by the natural radiation background in Romanian industry: phosphates-containing fertilizer processing, and copper and gold mining, are presented. U-238, Th-232, K-40, Ra-226 values (Bq/Kg) for various imported phosphorites, superphosphates, concentrated Cu and Au Romanian ores, are reported. A simple and efficient radioactivity determination procedure based on a large volume NaI (Tl) detector coupled to a Romanian-designed portable multichannel analyzer is described. Potential radiological impacts on specialized workers are discussed. (Author)

  6. Positron annihilation lifetime characterization of oxygen ion irradiated rutile TiO2

    Science.gov (United States)

    Luitel, Homnath; Sarkar, A.; Chakrabarti, Mahuya; Chattopadhyay, S.; Asokan, K.; Sanyal, D.

    2016-07-01

    Ferromagnetic ordering at room temperature has been induced in rutile phase of TiO2 polycrystalline sample by O ion irradiation. 96 MeV O ion induced defects in rutile TiO2 sample has been characterized by positron annihilation spectroscopic techniques. Positron annihilation results indicate the formation of cation vacancy (VTi, Ti vacancy) in these irradiated TiO2 samples. Ab initio density functional theoretical calculations indicate that in TiO2 magnetic moment can be induced either by creating Ti or O vacancies.

  7. The effects of nanostructures on the mechanical and tribological properties of TiO2 nanotubes

    Science.gov (United States)

    Yoon, Yeoungchin; Park, Jeongwon

    2018-04-01

    TiO2 nanotubes were prepared by anodization on Ti substrates with a diameter variation of 30-100 nm, and the structure of the nanotubes were studied using x-ray diffraction and Raman spectroscopy, which confirmed the structure changes from the anatase phase to the rutile phase of TiO2 at a diameter below 50 nm. The tribological behaviors of TiO2 nanotubes were investigated with different diameters. The effectiveness of the rutile phase and the diameter size enhanced the frictional performance of TiO2 nanotubes.

  8. Annealing of TiO2 Films Deposited on Si by Irradiating Nitrogen Ion Beams

    International Nuclear Information System (INIS)

    Yokota, Katsuhiro; Yano, Yoshinori; Miyashita, Fumiyoshi

    2006-01-01

    Thin TiO2 films were deposited on Si at a temperature of 600 deg. C by an ion beam assisted deposition (IBAD) method. The TiO2 films were annealed for 30 min in Ar at temperatures below 700 deg. C. The as-deposited TiO2 films had high permittivities such 200 εo and consisted of crystallites that were not preferentially oriented to the c-axis but had an expanded c-axis. On the annealed TiO2 films, permittivities became lower with increasing annealing temperature, and crystallites were oriented preferentially to the (110) plane

  9. Synthesis of Nd3+doped TiO2 nanoparticles and Its Optical Behaviour

    Directory of Open Access Journals (Sweden)

    Ezhil Arasi S.

    2017-04-01

    Full Text Available Pure and Rare earth ion doped TiO2 nanoparticles were synthesized by Sol-gel method. The synthesized TiO2 nanoparticles were characterized by X-ray diffraction, Raman spectroscopy, UV–Vis spectroscopy and photoluminescence emission spectra. From the UV-visible measurement, the absorption edge of Nd3+-TiO2 was shifted to a higher wavelength side with decreasing band gap. Photoluminescence emission studies reveal the energy transfer mechanism of Nd3+ doped TiO2 nanoparticles explain.

  10. Defective TiO2 with oxygen vacancies: synthesis, properties and photocatalytic applications

    Science.gov (United States)

    Pan, Xiaoyang; Yang, Min-Quan; Fu, Xianzhi; Zhang, Nan; Xu, Yi-Jun

    2013-04-01

    Titanium dioxide (TiO2), as an important semiconductor metal oxide, has been widely investigated in the field of photocatalysis. The properties of TiO2, including its light absorption, charge transport and surface adsorption, are closely related to its defect disorder, which in turn plays a significant role in the photocatalytic performance of TiO2. Among all the defects identified in TiO2, oxygen vacancy is one of the most important and is supposed to be the prevalent defect in many metal oxides, which has been widely investigated both by theoretical calculations and experimental characterizations. Here, we give a short review on the existing strategies for the synthesis of defective TiO2 with oxygen vacancies, and the defect related properties of TiO2 including structural, electronic, optical, dissociative adsorption and reductive properties, which are intimately related to the photocatalytic performance of TiO2. In particular, photocatalytic applications with regard to defective TiO2 are outlined. In addition, we offer some perspectives on the challenge and new direction for future research in this field. We hope that this tutorial minireview would provide some useful contribution to the future design and fabrication of defective semiconductor-based nanomaterials for diverse photocatalytic applications.Titanium dioxide (TiO2), as an important semiconductor metal oxide, has been widely investigated in the field of photocatalysis. The properties of TiO2, including its light absorption, charge transport and surface adsorption, are closely related to its defect disorder, which in turn plays a significant role in the photocatalytic performance of TiO2. Among all the defects identified in TiO2, oxygen vacancy is one of the most important and is supposed to be the prevalent defect in many metal oxides, which has been widely investigated both by theoretical calculations and experimental characterizations. Here, we give a short review on the existing strategies for the synthesis of defective TiO2 with oxygen vacancies, and the defect related properties of TiO2 including structural, electronic, optical, dissociative adsorption and reductive properties, which are intimately related to the photocatalytic performance of TiO2. In particular, photocatalytic applications with regard to defective TiO2 are outlined. In addition, we offer some perspectives on the challenge and new direction for future research in this field. We hope that this tutorial minireview would provide some useful contribution to the future design and fabrication of defective semiconductor-based nanomaterials for diverse photocatalytic applications. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr00476g

  11. Enhancing lipid productivity of Chlorella vulgaris using oxidative stress by TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Kang, Nam Kyu; Lee, Bongsoo; Choi, Gang-Guk; Moon, Myounghoon; Park, Min S.; Yang, Ji-Won; Lim, JitKang

    2014-01-01

    Ability to increase the lipid production in microalgae is one of the heavily sought-after ideas to improve the economic feasibility of microalgae-derived transportation fuels for commercial applications. We used the oxidative stress by TiO 2 nanoparticles, a well-known photocatalyst, to induce lipid production in microalgae. Chlorella vulgaris UTEX 265 was cultivated under various concentrations of TiO 2 ranging from 0.1 to 5 g/L under UV-A illumination. Maximum specific growth rate was affected in responding to TiO 2 concentrations. In the presence of UV-A, chlorophyll concentration was decreased at the highest concentration of TiO 2 (5 g/L TiO 2 ) by oxidative stress. The fatty acid methyl ester (FAME) composition analysis suggested that oxidative stress causes the accumulation and decomposition of lipids. The highest FAME productivity was 18.2 g/L/d under low concentrations of TiO 2 (0.1 g/L) and a short induction time (two days). The controlled condition of TiO 2 /UV-A inducing oxidative stress (0.1 g/L TiO 2 and two days induction) could be used to increase the lipid productivity of C. vulgaris UTEX 265. Our results show the possibility of modulating the lipid induction process through oxidative stress with TiO 2 /UV-A

  12. Preparation and characterization of nanocrystalline porous TiO2/WO3 composite thin films

    International Nuclear Information System (INIS)

    Hsu, C.-S.; Lin, C.-K.; Chan, C.-C.; Chang, C.-C.; Tsay, C.-Y.

    2006-01-01

    TiO 2 materials possessing not only photocatalytic but also electrochromic properties have attracted many research and development interests. Though WO 3 exhibits excellent electrochromic properties, the much higher cost and water-sensitivity of WO 3 as compared with the TiO 2 may restrict the practical application of WO 3 materials. In the present study, the feasibility of preparing nanocrystalline porous TiO 2 /WO 3 composite thin films was investigated. Precursors of sols TiO 2 and/or WO 3 and polystyrene microspheres were used to prepare nanocrystalline pure TiO 2 , WO 3 , and composite TiO 2 /WO 3 thin films by spin coating. The spin-coated thin films were amorphous and, after heat treating at a temperature of 500 o C, nanocrystalline TiO 2 , TiO 2 /WO 3 , and WO 3 thin films with or without pores were prepared successfully. The heat-treated thin films were colorless and coloration-bleaching phenomena can be observed during cyclic voltammetry tests. The heat-treated thin films exhibited good reversible electrochromic behavior while the porous TiO 2 /WO 3 composite film exhibited improved electrochromic properties

  13. Flow-Regulated Growth of Titanium Dioxide (TiO2 ) Nanotubes in Microfluidics.

    Science.gov (United States)

    Fan, Rong; Chen, Xinye; Wang, Zihao; Custer, David; Wan, Jiandi

    2017-08-01

    Electrochemical anodization of titanium (Ti) in a static, bulk condition is used widely to fabricate self-organized TiO 2 nanotube arrays. Such bulk approaches, however, require extended anodization times to obtain long TiO 2 nanotubes and produce only vertically aligned nanotubes. To date, it remains challenging to develop effective strategies to grow long TiO 2 nanotubes in a short period of time, and to control the nanotube orientation. Here, it is shown that the anodic growth of TiO 2 nanotubes is significantly enhanced (≈16-20 times faster) under flow conditions in microfluidics. Flow not only controls the diameter, length, and crystal orientations of TiO 2 nanotubes, but also regulates the spatial distribution of nanotubes inside microfluidic devices. Strikingly, when a Ti thin film is deposited on silicon substrates and anodized in microfluidics, both vertically and horizontally aligned (relative to the bottom substrate) TiO 2 nanotubes can be produced. The results demonstrate previously unidentified roles of flow in the regulation of growth of TiO 2 nanotubes, and provide powerful approaches to effectively grow long, oriented TiO 2 nanotubes, and construct hierarchical TiO 2 nanotube arrays on silicon-based materials. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  14. One-component solution system to prepare nanometric anatase TiO2

    International Nuclear Information System (INIS)

    Trung, Tran; Ha, Chang-Sik

    2004-01-01

    A novel one-pot synthesis route was proposed to prepare nanometric anatase TiO 2 using trichloroethylene as reaction medium, which may have great advantage over multicomponent solution systems when TiO 2 is used as a reinforcing filler for polymers dissolved in trichloroethylene. The anatase TiO 2 nanoparticles were characterized using X-ray diffraction (XRD), scanning electron microscopy and small-angle X-ray scattering (SAXS). It was found that the diameters of TiO 2 nanoparticles are in the range from 5 to 13 nm

  15. Photodecomposition of volatile organic compounds using TiO2 nanoparticles.

    Science.gov (United States)

    Jwo, Ching-Song; Chang, Ho; Kao, Mu-Jnug; Lin, Chi-Hsiang

    2007-06-01

    This study examined the photodecomposition of volatile organic compounds (VOCs) using TiO2 catalyst fabricated by the Submerged Arc Nanoparticle Synthesis System (SANSS). TiO2 catalyst was employed to decompose volatile organic compounds and compare with Degussa-P25 TiO2 in terms of decomposition efficiency. In the electric discharge manufacturing process, a Ti bar, applied as the electrode, was melted and vaporized under high temperature. The vaporized Ti powders were then rapidly quenched under low-temperature and low-pressure conditions in deionized water, thus nucleating and forming nanocrystalline powders uniformly dispersed in the base solvent. The average diameter of the TiO2 nanoparticles was 20 nm. X-ray diffraction analysis confirmed that the nanoparticles in the deionized water were Anatase type TiO2. It was found that gaseous toluene exposed to UV irradiation produced intermediates that were even harder to decompose. After 60-min photocomposition, Degussa-P25 TiO2 reduced the concentration of gaseous toluene to 8.18% while the concentration after decomposition by SANSS TiO2 catalyst dropped to 0.35%. Under UV irradiation at 253.7 +/- 184.9 nm, TiO2 prepared by SANSS can produce strong chemical debonding energy, thus showing great efficiency, superior to that of Degussa-P25 TiO2, in decomposing gaseous toluene and its intermediates.

  16. Sugarcane bagasse derivative-based superabsorbent containing phosphate rock with water-fertilizer integration.

    Science.gov (United States)

    Zhong, Kang; Zheng, Xi-Liang; Mao, Xiao-Yun; Lin, Zuan-Tao; Jiang, Gang-Biao

    2012-10-01

    To improve the water-fertilizer utilization ratio and mitigate the environmental contamination, an eco-friendly superabsorbent polymer (SPA), modified sugarcane bagasse/poly (acrylic acid) embedding phosphate rock (MSB/PAA/PHR), was prepared. Ammonia, phosphate rock (PHR) and KOH were admixed in the presence of acrylic acid to provide nitrogen (N), phosphorus (P) and potassium (K) nutrients, respectively. Impacts on water absorption capacity of the superabsorbent polymer (SAP) were investigated. The maximum swelling capacity in distilled water and 0.9 wt.% (weight percent) NaCl solution reached 414 gg(-1) and 55 gg(-1) (water/prepared SAP), respectively. The available NPK contents of the combination system were 15.13 mgg(-1), 6.93 mgg(-1) and 52.05 mgg(-1), respectively. Moreover, the release behaviors of NPK in the MSB/PAA/PHR were also studied. The results showed that the MSB/PAA/PHR has outstanding sustained-release plant nutrients property. Copyright © 2012 Elsevier Ltd. All rights reserved.

  17. Crystal Analysis of Multi Phase Calcium Phosphate Nanoparticles Containing Different amount of Magnesium

    Science.gov (United States)

    Gozalian, Afsaneh; Behnamghader, Ali Asghar; Moshkforoush, Arash

    In this study, Mg doped hydroxyapatite [(Ca, Mg)10(PO4)6(OH)2] and β-tricalcium phosphate nanoparticles were synthesized via sol gel method. Triethyl phosphite, calcium nitrate tetrahydrate and magnesium nitrate hexahydrate were used as P, Ca and Mg precursors. The ratio of (Ca+Mg)/P and the amount of magnesium (x) were kept constant at 1.67 and ranging x = 0 up to 3 in molecular formula of Ca10-xMgx (PO4)6(OH)2, respectively. Phase composition and chemical structure were performed using X-ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). Phase percentages, crystallite size, degree of crystallinity and lattice parameters were investigated. The presence of magnesium led to form the Mg doped tricalcium phosphate (β-TCMP) and Mg doped hydroxyapatite (Mg-HA). Based on the results of this study, lattice parameters, degree of crystallinity and crystallite size decreased with magnesium content. In addition, with increasing magnesium content, the amount of CaO phase decreased whereas the amount of MgO phase increased significantly. Obtained results can be used for new biomaterials design.

  18. Phosphate-Containing Polyethylene Glycol Polymers Prevent Lethal Sepsis by Multidrug-Resistant Pathogens

    Energy Technology Data Exchange (ETDEWEB)

    Zaborin, Alexander; Defazio, Jennifer; Kade, Matthew; Kaiser, Brooke LD; Belogortseva, Natalia; Camp, David G.; Smith, Richard D.; Adkins, Joshua N.; Kim, Sangman M.; Alverdy, Alexandria; Goldfeld, David; Firestone, Millicent; Collier, Joel; Jabri, Bana; Tirrell, Matthew; Zaborina, Olga; Alverdy, John C.

    2014-02-01

    The gastrointestinal tract is the primary site of colonization for multi-drug resistant healthcare associated pathogens (HAPs) that are the principal source and cause of life-threatening infections in critically ill patients. We previously identified a high molecular weight co-polymer (PEG15-20) with mucoadhesive and cytoprotective actions on the intestinal epithelium. In this report we covalently bonded phosphate (Pi) to PEG15-20 ( termed Pi-PEG15-20) to enhance its cytoprotective activity against microbial virulence activation and invasion based on our previous work showing that Pi is a key environmental cue regulating microbial virulence across pathogens of clinical importance to hospitalized patients. We demonstrated that Pi-PEG15-20 can suppress phosphate-, iron-, and quorum sensing signal- mediated activation of bacterial virulence as well as inhibit intestinal epithelial IL-8 release during lipopolysaccharide (LPS) exposure. Pi-PEG15-20 also prevented mortality in C. elegans and mice exposed to several highly virulent and antibiotic(?)-resistant health care acquired pathogens (HAPs) while preserving the normal microbiota. Intestinal application Pi-PEG 15-20 has the potential to be a useful agent to prevent the pathogenic activation of microbes during critical illness where exposure to HAPs is ubiquitous.

  19. Characteristics and properties of a novel in situ method of synthesizing mesoporous TiO2 nanopowders by a simple coprecipitation process without adding surfactant

    International Nuclear Information System (INIS)

    Yeh, Shang-Wei; Ko, Horng-Huey; Chiang, Hsiu-Mei; Chen, Yen-Ling; Lee, Jian-Hong; Wen, Chiu-Ming; Wang, Moo-Chin

    2014-01-01

    Highlights: • The TiO 2 precursor powder contained anatase and 19.5% NH 4 Cl. • Mesoporous anatase TiO 2 nanopowders were successfully synthesized. • Uncalcined precursor powder contained the phases of type I NH 4 Cl and anatase TiO 2 . • Anatase size increases from 3.3 to 14.3 nm when calcined at 473–773 K for 2 h. • The average pore size between 3.80 and 14.0 nm when calcined between 473 and 773 K. - Abstract: In situ synthesis of mesoporous TiO 2 nanopowders using titanium tetrachloride (TiCl 4 ) and NH 4 OH as initial materials has been successfully fabricated by a coprecipitation process without the addition of surfactant. Characteristics and properties of the mesoporous TiO 2 nanopowders were investigated using differential scanning calorimetry/thermogravimetry (DSC/TG), X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) and Barrent–Joyner–Halenda (BJH) analyses, transmission electron microscopy (TEM), selected area electron diffraction (SAED) and high resolution TEM (HRTEM). The results of TG and XRD showed that the NH 4 Cl decomposed between 513 and 673 K. XRD results showed that the anatase TiO 2 only contained a single phase when the calcination temperature of the precursor powder was less than 673 K. Whereas phases of anatase and rutile TiO 2 coexist after calcining at 773 K for 2 h. The crystalline size of the anatase and rutile TiO 2 was 14.3 and 26.6 nm, respectively, when the precursor powder was calcined at 773 K for 2 h. The BET and BJH results showed a significant increase in surface area and pore volumes when the NH 4 Cl was completely decomposed. The maximum values of BET specific surface area and volume were 172.8 m 2 /g and 0.392 cm 3 /g, respectively. The average pore sizes when calcination was at 473 and 773 K for 2 h were 3.8 and 14.0 nm, respectively

  20. Enhanced bonding between TiO2-Graphene oxide

    DEFF Research Database (Denmark)

    Naknikham, Usuma; Buffa, Vittorio; Yue, Yuanzheng

    analysis. Besides, the study of Ti-O-C and Ti-C interface bonding was carried out using XPS. The band-gap energy was determined using a UV-VIS spectrophotometer equipped with an integrating sphere. Thus, it was possible for us to determine the reactivity of the new photocatalysts under the visible light...... as photocatalysts, which can efficiently react with organic species under solar light and can enhance the adsorption of water pollutants [3]. Many studies have shown that TiO2-GO heterostructures can quickly mineralize organic dyes in solution under UV-light. However, it is not clear if these materials can provide...... the same performances under sunlight and with complex real water systems. Hence, this research aims to study the photocatalystic property on GO-TiO2 composites with aqueous solutions of selected emerging pollutants under visible light. The samples were synthesized via the in-situ sol-gel nucleation...

  1. Low-energy ion irradiation in HiPIMS to enable anatase TiO2 selective growth

    Science.gov (United States)

    Cemin, Felipe; Tsukamoto, Makoto; Keraudy, Julien; Antunes, Vinícius Gabriel; Helmersson, Ulf; Alvarez, Fernando; Minea, Tiberiu; Lundin, Daniel

    2018-06-01

    High power impulse magnetron sputtering (HiPIMS) has already demonstrated great potential for synthesizing the high-energy crystalline phase of titanium dioxide (rutile TiO2) due to large quantities of highly energetic ions present in the discharge. In this work, it is shown that the metastable anatase phase can also be obtained by HiPIMS. The required deposition conditions have been identified by systematically studying the phase formation, microstructure and chemical composition as a function of mode of target operation as well as of substrate temperature, working pressure, and peak current density. It is found that films deposited in the metal and transition modes are predominantly amorphous and contain substoichiometric TiO x compounds, while in compound mode they are well-crystallized and present only O2‑ ions bound to Ti4+, i.e. pure TiO2. Anatase TiO2 films are obtained for working pressures between 1 and 2 Pa, a peak current density of ~1 A cm‑2 and deposition temperatures lower than 300 °C. Rutile is favored at lower pressures (2 A cm‑2), while amorphous films are obtained at higher pressures (5 Pa). Microstructural characterization of selected films is also presented.

  2. Nb-doped TiO2 cathode catalysts for oxygen reduction reaction of polymer electrolyte fuel cells

    KAUST Repository

    Arashi, Takuya

    2014-09-01

    Nb-doped TiO2 particles were studied as electrocatalysts for the oxygen reduction reaction (ORR) under acidic conditions. The Nb-doped TiN nanoparticles were first synthesized by meso-porous C3N4 and then fully oxidized to Nb-doped TiO2 by immersing in 0.1 M H 2SO4 at 353 K for 24 h. Although the ORR activity of the as-obtained sample was low, a H2 treatment at relatively high temperature (1173 K) dramatically improved the ORR performance. An onset potential as high as 0.82 VRHE was measured. No degradation of the catalysts was observed during the oxidation-reduction cycles under the ORR condition for over 127 h. H2 treatment at temperatures above 1173 K caused the formation of a Ti4O7 phase, resulting in a decrease in ORR current. Elemental analysis indicated that the Nb-doped TiO 2 contained 25 wt% residual carbon. Calcination in air at 673 or 973 K eliminated the residual carbon in the catalyst, which was accompanied by a dramatic decrease in ORR activity. This post-calcination process may reduce the conductivity of the sample by filling the oxygen vacancies, and the carbon residue in the particle aggregates may enhance the electrocatalytic activity for ORR. The feasibility of using conductive oxide materials as electrocatalysts is discussed. © 2013 Elsevier B.V.

  3. Remediation of Organic and Inorganic Arsenic Contaminated Groundwater using a Nonocrystalline TiO2 Based Adsorbent

    Energy Technology Data Exchange (ETDEWEB)

    Jing, C.; Meng, X; Calvache, E; Jiang, G

    2009-01-01

    A nanocrystalline TiO2-based adsorbent was evaluated for the simultaneous removal of As(V), As(III), monomethylarsonic acid (MMA), and dimethylarsinic acid (DMA) in contaminated groundwater. Batch experimental results show that As adsorption followed pseudo-second order rate kinetics. The competitive adsorption was described with the charge distribution multi-site surface complexation model (CD-MUSIC). The groundwater containing an average of 329 ?g L-1 As(III), 246 ?g L-1 As(V), 151 ?g L-1 MMA, and 202 ?g L-1 DMA was continuously passed through a TiO2 filter at an empty bed contact time of 6 min for 4 months. Approximately 11 000, 14 000, and 9900 bed volumes of water had been treated before the As(III), As(V), and MMA concentration in the effluent increased to 10 ?g L-1. However, very little DMA was removed. The EXAFS results demonstrate the existence of a bidentate binuclear As(V) surface complex on spent adsorbent, indicating the oxidation of adsorbed As(III). A nanocrystalline TiO2-based adsorbent could be used for the simultaneous removal of As(V), As(III), MMA, and DMA in contaminated groundwater.

  4. Distinctive toxicity of TiO2 rutile/anatase mixed phase nanoparticles on Caco-2 cells.

    Science.gov (United States)

    Gerloff, Kirsten; Fenoglio, Ivana; Carella, Emanuele; Kolling, Julia; Albrecht, Catrin; Boots, Agnes W; Förster, Irmgard; Schins, Roel P F

    2012-03-19

    Titanium dioxide has a long-standing use as a food additive. Micrometric powders are, e.g., applied as whiteners in confectionary or dairy products. Possible hazards of ingested nanometric TiO(2) particles for humans and the potential influence of varying specific surface area (SSA) are currently under discussion. Five TiO(2)-samples were analyzed for purity, crystallinity, primary particle size, SSA, ζ potential, and aggregation/agglomeration. Their potential to induce cytotoxicity, oxidative stress, and DNA damage was evaluated in human intestinal Caco-2 cells. Only anatase-rutile containing samples, in contrast to the pure anatase samples, induced significant LDH leakage or mild DNA damage (Fpg-comet assay). Evaluation of the metabolic competence of the cells (WST-1 assay) revealed a highly significant correlation between the SSA of the anatase samples and cytotoxicity. The anatase/rutile samples showed higher toxicity per unit surface area than the pure anatase powders. However, none of the samples affected cellular markers of oxidative stress. Our findings suggest that both SSA and crystallinity are critical determinants of TiO(2)-toxicity toward intestinal cells. © 2012 American Chemical Society

  5. Investigation of anodic TiO2 nanotube composition with high spatial resolution AES and ToF SIMS

    Science.gov (United States)

    Dronov, Alexey; Gavrilin, Ilya; Kirilenko, Elena; Dronova, Daria; Gavrilov, Sergey

    2018-03-01

    High resolution Scanning Auger Electron Spectroscopy (AES) and Time-of-Flight Secondary Ion Mass-Spectrometry (ToF SIMS) were used to investigate structure and elemental composition variation of both across an array of TiO2 nanotubes (NTs) and single tube of an array. The TiO2 NT array was grown by anodic oxidation of Ti foil in fluorine-containing ethylene glycol electrolyte. It was found that the studied anodic TiO2 nanotubes have a layered structure with rather sharp interfaces. The differences in AES depth profiling results of a single tube with the focused primary electron beam (point analysis) and over an area of 75 μm in diameter of a nanotube array with the defocused primary electron beam are discussed. Depth profiling by ToF SIMS was carried out over approximately the same size of a nanotube array to determine possible ionic fragments in the structure. The analysis results show that the combination of both mentioned methods is useful for a detailed analysis of nanostructures with complex morphology and multi-layered nature.

  6. Influence of TiO2 content on the crystallization and microstructure of machinable glass-ceramics

    Directory of Open Access Journals (Sweden)

    Debasis Pradip Mukherjee

    2016-03-01

    Full Text Available Glasses based on the SiO2–Al2O3–MgO–K2O–B2O3–MgF2 system added with TiO2 were synthesized and characterized by differential scanning calorimetry (DSC, X-ray powder diffraction (XRD, Fourier transform infrared spectroscopy (FTIR and scanning electron microscopy (SEM techniques. The results showed that by increasing the TiO2 content, glass transition temperature (Tg, both the crystallization peak temperature (TpI and TpII and activation energy (E increased. The interconnected large blocky card-like crystals were identified as fluorophlogopite as a major crystalline phase for all three glass-ceramic specimens by (XRD and subsequently confirmed by SEM. The Vickers hardness (Hv value for glass-ceramic specimens decreases with progressively increasing TiO2 content (1–10 wt% and Titania containing MGT-3 glass-ceramic specimen with interconnected large blocky card-like fluorophlogopite mica crystals possess lower Hv (4.26 GPa as well as good machinability (m = 0.12 useable for machinable applications. The study shows that Titania promoted initial crystallization of glass and can be used as an effective nucleting agent.

  7. Application of carbon-coated TiO2 for decomposition of methylene blue in a photocatalytic membrane reactor

    International Nuclear Information System (INIS)

    Mozia, Sylwia; Toyoda, Masahiro; Inagaki, Michio; Tryba, Beata; Morawski, Antoni W.

    2007-01-01

    An application of carbon-coated TiO 2 for decomposition of methylene blue (MB) in a photocatalytic membrane reactor (PMR), coupling photocatalysis and direct contact membrane distillation (DCMD) was investigated. Moreover, photodegradation of a model pollutant in a batch reactor without membrane distillation (MD) was also examined. Carbon-modified TiO 2 catalysts containing different amount of carbon and commercially available TiO 2 (ST-01) were used in this study. The carbon-coated catalyst prepared from a mixture of ST-01 and polyvinyl alcohol in the mass ratio of 70/30 was the most effective in degradation of MB from all of the photocatalysts applied. Photodecomposition of MB on the recovered photocatalysts was lower than on the fresh ones. The photodegradation of MB in the PMR was slower than in the batch reactor, what probably resulted from shorter time of exposure of the catalyst particles to UV irradiation. The MD process could be successfully applied for separation of photocatalyst and by-products from the feed solution

  8. Nb-doped TiO2 cathode catalysts for oxygen reduction reaction of polymer electrolyte fuel cells

    KAUST Repository

    Arashi, Takuya; Seo, Jeongsuk; Takanabe, Kazuhiro; Kubota, Jun; Domen, Kazunari

    2014-01-01

    Nb-doped TiO2 particles were studied as electrocatalysts for the oxygen reduction reaction (ORR) under acidic conditions. The Nb-doped TiN nanoparticles were first synthesized by meso-porous C3N4 and then fully oxidized to Nb-doped TiO2 by immersing in 0.1 M H 2SO4 at 353 K for 24 h. Although the ORR activity of the as-obtained sample was low, a H2 treatment at relatively high temperature (1173 K) dramatically improved the ORR performance. An onset potential as high as 0.82 VRHE was measured. No degradation of the catalysts was observed during the oxidation-reduction cycles under the ORR condition for over 127 h. H2 treatment at temperatures above 1173 K caused the formation of a Ti4O7 phase, resulting in a decrease in ORR current. Elemental analysis indicated that the Nb-doped TiO 2 contained 25 wt% residual carbon. Calcination in air at 673 or 973 K eliminated the residual carbon in the catalyst, which was accompanied by a dramatic decrease in ORR activity. This post-calcination process may reduce the conductivity of the sample by filling the oxygen vacancies, and the carbon residue in the particle aggregates may enhance the electrocatalytic activity for ORR. The feasibility of using conductive oxide materials as electrocatalysts is discussed. © 2013 Elsevier B.V.

  9. Plasma-assisted adsorption of elemental mercury on CeO2/TiO2 at low temperatures

    Science.gov (United States)

    Liu, Lu; Zheng, Chenghang; Gao, Xiang

    2017-11-01

    Mercury is a kind of pollutants contained in flue gas which is hazardous for human beings. In this work, CeO2 was packed in the discharge zone of a plasma reactor to adsorb elemental mercury at low temperatures. Plasma-catalyst reactor can remove Hg0 efficiently with CeO2/TiO2 catalysts packed in the discharge zone. The Hg0 concentration continued to decrease gradually when the plasma was turned on, but not sank rapidly. This tendency was different with other catalysts. The treatment of plasma to CeO2/TiO2 catalysts has a promotion effect on the adsorption of Hg0. Plasma has the effect of changing the surface properties of the catalysts and the changes would restitute if the condition changed. The long-running test demonstrated that this method is an effective way to remove Hg0. The removal efficiency remained at above 99% throughout 12 hours when plasma had been turned on (15kV, 0.5 g packed CeO2/TiO2).

  10. Bioactivity of sol-gel-derived TiO2 coating on polyetheretherketone: In vitro and in vivo studies.

    Science.gov (United States)

    Shimizu, Takayoshi; Fujibayashi, Shunsuke; Yamaguchi, Seiji; Yamamoto, Koji; Otsuki, Bungo; Takemoto, Mitsuru; Tsukanaka, Masako; Kizuki, Takashi; Matsushita, Tomiharu; Kokubo, Tadashi; Matsuda, Shuichi

    2016-04-15

    A polyetheretherketone (PEEK) surface was modified using a sol-gel-derived TiO2 coating in order to confer bone-bonding ability. To enhance the bonding strength of the coating layer, pretreatment with either O2 plasma or sandblasting was performed prior to sol-gel coating. Additionally, post-treatment with acid was carried out to confer apatite (calcium phosphate)-forming ability to the surface. Biomechanical and histological analyses performed using an in vivo rabbit tibia model showed that PEEK surfaces modified with sol-gel-derived TiO2 and acid post-treatment had better bone-bonding properties than uncoated PEEK surfaces. These modified surfaces also performed well in terms of their in vitro cell responses due to their modified surface chemistries and topographies. Although O2 plasma or sandblasting treatment were, for the most part, equivocal in terms of performance, we conclude that sol-gel-derived TiO2 coating followed by acid post-treatment significantly improves the bone bonding ability of PEEK surfaces, thus rendering them optimal for their use in surgical implants. The role of polyetheretherketone (PEEK) as an alternative biomaterial to conventional metallic implant materials has become increasingly important. However, its low bone bonding ability is yet to be resolved. This in vivo and in vitro investigation on the functionalization of PEEK surfaces highlights the utility of this material in clinical interventions that require implants, and may extend range of applications of PEEK. Copyright © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  11. N-Doped TiO2-Coated Ceramic Membrane for Carbamazepine Degradation in Different Water Qualities

    Science.gov (United States)

    Luster, Enbal; Avisar, Dror; Horovitz, Inna; Lozzi, Luca; Baker, Mark A.; Grilli, Rossana; Mamane, Hadas

    2017-01-01

    The photocatalytic degradation of the model pollutant carbamazepine (CBZ) was investigated under simulated solar irradiation with an N-doped TiO2-coated Al2O3 photocatalytic membrane, using different water types. The photocatalytic membrane combines photocatalysis and membrane filtration in a single step. The impact of each individual constituent such as acidity, alkalinity, dissolved organic matter (DOM), divalent cations (Mg2+ and Ca2+), and Cl− on the degradation of CBZ was examined. CBZ in water was efficiently degraded by an N-doped TiO2-coated Al2O3 membrane. However, elements added to the water, which simulate the constituents of natural water, had an impact on the CBZ degradation. Water alkalinity inhibited CBZ degradation mostly due to increase in pH while radical scavenging by carbonate was more dominant at higher values (>200 mg/L as CaCO3). A negative effect of Ca2+ addition on photocatalytic degradation was found only in combination with phosphate buffer, probably caused by deposition of CaHPO4 or CaHPO4·2H2O on the catalyst surface. The presence of Cl− and Mg2+ ions had no effect on CBZ degradation. DOM significantly inhibited CBZ degradation for all tested background organic compounds. The photocatalytic activity of N-doped TiO2-coated Al2O3 membranes gradually decreased after continuous use; however, it was successfully regenerated by 0.1% HCl chemical cleaning. Nevertheless, dissolution of metals like Al and Ti should be monitored following acid cleaning. PMID:28758982

  12. Wastewater Treatment from Batik Industries Using TiO2 Nanoparticles

    Science.gov (United States)

    Arifan, Fahmi; Nugraheni, FS; Rama Devara, Hafiz; Lianandya, Niken Elsa

    2018-02-01

    Batik is cultural patterned fabric, and the this industries produce wastewater that can pollute the aquatic environment. Besides dyes, batik wastewater also contains synthetic compounds that are hard degraded, such as heavy metals, suspended solids, or organic compounds. In this study, photocatalitic membrane TiO2 coated plastic sheets have been used to degrade batik wastewater under solar exposure. A total of 8 pieces of catalyst sheets are added on 1000 ml of the waste, and managed to degrade 50.41% of the initial concentration during 5-days irradiation. In this study, several parameters of the water quality such as chemical oxygen demand (COD), biological oxygen demand (BOD), and total suspensed solids (TSS) of the wastewater were observed to be decreasing during photodegradation process. The catalyst sheet also is stable to be used repeatedly in wastewater treatment.

  13. Preparation and characterisation of visible light responsive iodine doped TiO2 electrodes

    International Nuclear Information System (INIS)

    Lisowska-Oleksiak, Anna; Szybowska, Katarzyna; Jasulaitiene, Vitalija

    2010-01-01

    Characteristics are presented of new iodine doped TiO 2 (I-TiO 2 ) prepared via the hydrothermal method, where titania (IV) complexes with a ligand containing an iodine atom have been used as a precursor. The structure of samples has been examined by XPS, XRD, UV-vis and FT-IR-ATR techniques. These studies confirm that the obtained powder exhibits a decrease in the bandgap energy value (E g = 2.8 eV). The report presents electrochemical studies of I-TiO 2 films on a Pt electrode, which allow determination of the flatband potential E fb = -0.437 V vs. SCE (in 0.5 M Na 2 SO 4 ). Cyclic voltammetry measurements show anodic and cathodic activities under Vis and UV-vis radiation. The photocurrent enhancement due to visible light radiation reached 30% of the whole photoacitivity exhibited under UV-vis illumination.

  14. Phosphate sink containing two-component signaling systems as tunable threshold devices

    DEFF Research Database (Denmark)

    Amin, Munia; Kothamachu, Varun B; Feliu, Elisenda

    2014-01-01

    Synthetic biology aims to design de novo biological systems and reengineer existing ones. These efforts have mostly focused on transcriptional circuits, with reengineering of signaling circuits hampered by limited understanding of their systems dynamics and experimental challenges. Bacterial two......-component signaling systems offer a rich diversity of sensory systems that are built around a core phosphotransfer reaction between histidine kinases and their output response regulator proteins, and thus are a good target for reengineering through synthetic biology. Here, we explore the signal-response relationship...... rapid signal termination, whereby one of the RRs acts as a phosphate sink towards the other RR (i.e. the output RR), but also implements a sigmoidal signal-response relationship. We identify two mathematical conditions on system parameters that are necessary for sigmoidal signal-response relationships...

  15. Fabrication, characterization and photocatalytic properties of Ag nanoparticles modified TiO2 NTs

    International Nuclear Information System (INIS)

    Wang Qingyao; Yang Xiuchun; Liu Dan; Zhao Jianfu

    2012-01-01

    Graphical abstract: The TiO 2 NTs were first treated with bi-functional mercaptoacetic acid linkers (HOOC–R–S). The –OH group on the surface of TiO 2 NT provides a strong affinity with the carboxylate group in the linker molecules. The thiol functional group in the linker molecules facilitates the binding with Ag from AgNO 3 solution. After Ag + ions were reduced by NaBH 4 , Ag nanoparticles formed by nucleation and growth. Highlights: ► Ag nanoparticles with an average diameter of 9.2 nm were filled in the TiO 2 nanotubes by a successive ionic layer adsorption and reaction (SILAR) technique. ► Bi-functional mercaptoacetic acid linkers were used to bind TiO 2 nanotubes with Ag nanoparticles. ► Ag nanoparticles modification of TiO 2 NTs largely enhanced the photocatalytic degradation of methyl orange under ultraviolet light irradiation. - Abstract: Ordered anatase TiO 2 nanotubes (TiO 2 NTs) on Ti substrate were synthesized by electrochemical anodization and subsequently vapor-thermal treatment. Ag nanoparticles were decorated on TiO 2 NTs by successive ionic layer adsorption and reaction (SILAR) technique. Raman spectroscopy, X-ray absorption near edge spectroscopy (XANES), X-ray diffraction (XRD), UV–vis diffuse reflectance spectroscopy, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used for the characterization of surface morphology, phase composition, and microstructure of the original TiO 2 NTs, the vapor-thermally treated TiO 2 NTs and the Ag nanoparticles decorated TiO 2 NTs. The results indicate that vapor-thermal treatment favors to the transformation of amorphous TiO 2 into anatase phase. Increasing the SILAR cycle times favors to increase the loaded amounts of Ag nanoparticles in TiO 2 NTs. Ag nanoparticles are uniformly distributed in the TiO 2 NTs, and the SILAR process does not damage the ordered tubular structure. A possible formation mechanism of Ag/TiO 2 NTs has also been proposed. The photocatalytic results showed that the Ag nanoparticle modified TiO 2 NTs largely enhanced the photocatalytic degradation of methyl orange under ultraviolet light irradiation.

  16. The Effects of Anchor Groups on (1) TiO2-Catalyzed Photooxidation and (2) Linker-Assisted Assembly on TiO2

    Science.gov (United States)

    Anderson, Ian Mark

    Quantum dot-sensitized solar cells (QDSSCs) are a popular target for research due to their potential for highly efficient, easily tuned absorption. Typically, light is absorbed by quantum dots attached to a semiconductor substrate, such as TiO2, via bifunctional linker molecules. This research aims to create a patterned monolayer of linker molecules on a TiO2 film, which would in turn allow the attachment of a patterned layer of quantum dots. One method for the creation of a patterned monolayer is the functionalization of a TiO2 film with a linker molecule, followed by illumination with a laser at 355 nm. This initiates a TiO 2-catalyzed oxidation reaction, causing loss of surface coverage. A second linker molecule can then be adsorbed onto the TiO2 surface in the illuminated area. Towards that end, the behaviors of carboxylic and phosphonic acids adsorbed on TiO2 have been studied. TiO2 films were functionalized by immersion in solutions a single adsorbate and surface coverage was determined by IR spectroscopy. It is shown that phosphonic acids attain higher surface coverage than carboxylic acids, and will displace them from TiO2 when in a polar solvent. Alkyl chain lengths, which can influence stabilities of monolayers, are shown not to have an effect on this relationship. Equilibrium binding data for the adsorption of n-hexadecanoic acid to TiO2 from a THF solution are presented. It is shown that solvent polarity can affect monolayer stability; carboxylates and phosphonates undergo more desorption into polar solvents than nonpolar. Through illumination, it was possible to remove nearly all adsorbed linkers from TiO2. However, the illuminated areas were found not to be receptive to attachment by a second adsorbate. A possible reason for this behavior is presented. I also report on the synthesis and characterization of a straight-chain, thiol-terminated phosphonic acid. Initial experiments involving monolayer formation and quantum dot attachment are presented. Finally, it was found that quantum dots attach in high amounts to linker-functionalized TiO2 when suspended in pyridine. This increased surface attachment was present even when the linker molecule used lacked a functional group which would bind to the CdSe surface.

  17. The synthesis of aqueous-dispersible anatase TiO2 nanoplatelets

    International Nuclear Information System (INIS)

    Shan Guobin; Demopoulos, George P

    2010-01-01

    Aqueous well-dispersed and phase-pure anatase TiO 2 truncated octahedron nanoplatelets (NPLs) were prepared via controlled hydrolysis of titanium tetrachloride (TiCl 4 ) in ethylene glycol at 240 deg. C. Two shapes, square and hexagon, were observed by microscopy, exactly corresponding to the truncated octahedron NPLs. Ethylene glycol was found to produce water in situ that reacts with TiCl 4 to produce TiO 2 and HCl-the latter promoting TiO 2 colloid peptization. TiO 2 truncated octahedron NPLs are formed under the stabilizing action of ethylene glycol thermolysis derivatives, such as aldehydes. Crystal growth of the TiO 2 NPLs was affected by the reaction temperature that determines the water production rate and HCl-assisted peptization. TGA and FT-IR results showed ∼1.2% ethylene glycol thermolysis derivatives are attached to the surface of the TiO 2 NPLs, which prevents their agglomeration, hence making them easily dispersible in aqueous media. HR-TEM and SAED results showed that the TiO 2 NPLs are well crystallized and that the SAED patterns of the single TiO 2 NPL changes with its size and shape. XRD patterns showed that the TiO 2 NPLs are phase-pure anatase and the percentage of the {101} plane in the TiO 2 NPLs to be only 18%-a structural feature that renders the TiO 2 NPLs with enhanced UV absorption and reactivity properties.

  18. The Influence of Cr3+ on TiO2 Crystal Growth and Photoactivity Properties

    Science.gov (United States)

    Wahyuningsih, S.; Hidayatika, W. N.; Sari, P. L.; Sari, P. P.; Hidayat, R.; Munawaroh, H.; Ramelan, A. H.

    2018-03-01

    The photocatalyst technology is an integrated combination of photochemical processes and catalysis in order to carry out a chemical transformation reaction. One of the semiconductor materials that have good photocatalytic activity is TiO2 anatase. This study aim to determine the effect of the Cr3+ addition on the growth of TiO2 rutile crystal and the increasing of TiO2 photoactivity. Diffractogram X-Ray of the samples showed that the synthesized TiO2 at 400 °C has been produced 100% TiO2 anatase. Synthesis of TiO2 doped Cr3+ composite was using wet impregnation method. The TiO2 doped Cr3+ composites have beed grown by annealed at a temperature of 300, 400, 500, 600 and 700 °C, respectively Annealing process have capabled to gain to the TiO2 doped Cr3+ nanocomposite. The result product annealed at 500 °C only appear anatase phase due to the Cr3+ addition influence that was able to suppress the growth of rutile. Identification of TiO2 doped Cr3+ composite using Fourier Transform Infra-Red (FT-IR) showed O-Cr vibration at 2283.72 cm-1. The TiO2 doped Cr3+ photoactivity was studied to degrade Rhodamin B. The best result on photodegradation of Rhodamin B was performed by using TiO2 doped Cr3+ composite which was annealed at 700 °C i.e. 74.71%.

  19. Rapid detection of TiO2 (E171) in table sugar using Raman spectroscopy.

    Science.gov (United States)

    Tan, Chen; Zhao, Bin; Zhang, Zhiyun; He, Lili

    2017-02-01

    The potential toxic effects of titanium dioxide (TiO 2 ) to humans remain debatable despite its broad application as a food additive. Thus, confirmation of the existence of TiO 2 particles in food matrices and subsequently quantifying them are becoming increasingly critical. This study developed a facile, rapid (E171) from food products (e.g., table sugar) by Raman spectroscopy. To detect TiO 2 particles from sugar solution, sequential centrifugation and washing procedures were effectively applied to separate and recover 97% of TiO 2 particles from the sugar solution. The peak intensity of TiO 2 sensitively responded to the concentration of TiO 2 with a limit of detection (LOD) of 0.073 mg kg -1 . In the case of sugar granules, a mapping technique was applied to directly estimate the level of TiO 2 , which can be potentially used for rapid online monitoring. The plot of averaged intensity to TiO 2 concentration in the sugar granules exhibited a good linear relationship in the wide range of 5-2000 mg kg -1 , with an LOD of 8.46 mg kg -1 . Additionally, we applied Raman spectroscopy to prove the presence of TiO 2 in sugar-coated doughnuts. This study begins to fill in the analytical gaps that exist regarding the rapid detection and quantification of TiO 2 in food, which facilitate the risk assessment of TiO 2 through food exposure.

  20. Selective amplification and sequencing of cyclic phosphate-containing RNAs by the cP-RNA-seq method.

    Science.gov (United States)

    Honda, Shozo; Morichika, Keisuke; Kirino, Yohei

    2016-03-01

    RNA digestions catalyzed by many ribonucleases generate RNA fragments that contain a 2',3'-cyclic phosphate (cP) at their 3' termini. However, standard RNA-seq methods are unable to accurately capture cP-containing RNAs because the cP inhibits the adapter ligation reaction. We recently developed a method named cP-RNA-seq that is able to selectively amplify and sequence cP-containing RNAs. Here we describe the cP-RNA-seq protocol in which the 3' termini of all RNAs, except those containing a cP, are cleaved through a periodate treatment after phosphatase treatment; hence, subsequent adapter ligation and cDNA amplification steps are exclusively applied to cP-containing RNAs. cP-RNA-seq takes ∼6 d, excluding the time required for sequencing and bioinformatics analyses, which are not covered in detail in this protocol. Biochemical validation of the existence of cP in the identified RNAs takes ∼3 d. Even though the cP-RNA-seq method was developed to identify angiogenin-generating 5'-tRNA halves as a proof of principle, the method should be applicable to global identification of cP-containing RNA repertoires in various transcriptomes.

  1. Enhanced photoelectrocatalytic performance for degradation of diclofenac and mechanism with TiO2 nano-particles decorated TiO2 nano-tubes arrays photoelectrode

    International Nuclear Information System (INIS)

    Cheng, Xiuwen; Liu, Huiling; Chen, Qinghua; Li, Junjing; Wang, Pu

    2013-01-01

    In this study, TiO 2 nano-particles decorated TiO 2 nano-tubes arrays (TiO 2 NPs/TiO 2 NTAs) photoelectrodes have been successfully prepared through anodization, combined with ultrasonic strategy, followed by annealing post-treatment. The morphology and structure of the as-prepared TiO 2 NPs/TiO 2 NTAs photoelectrodes were characterized by scanning electrons microscopy (SEM), N 2 adsorption/desorption isotherms, X-ray diffraction (XRD) and UV–visible light diffuse reflection spectroscopy (DRS). In addition, the generation of hydroxyl radicals (·OH) was detected by a photoluminescence (PL) spectra using terephthalic acid (TA) as a probe molecule. Furthermore, the photoelectrochemical (PECH) properties of TiO 2 NPs/TiO 2 NTAs photoanode were investigated through transient open circuit potential (OCP), photocurrent response (PCR) and electrochemical impedance spectroscopy (EIS). It was found that TiO 2 NPs/TiO 2 NTAs photoelectrode exhibited a distinct decrease of OCP of −0.219 mV cm −2 and PCR of 0.049 mA cm −2 , while a significantly enhanced photoelectrocatalytic (PEC) efficiency of 63.6% (0.4 V vs. SCE) for the degradation of diclofenac. Moreover, the enhanced PEC mechanism of TiO 2 NPs/TiO 2 NTAs photoanode was proposed. The high PEC performance could be attributed to the decoration of TiO 2 NPs, which could improve the mobility and separation efficiency of photoinduced charge carriers under external potential

  2. Factors affecting color strength of printing on film-coated tablets by UV laser irradiation: TiO2 particle size, crystal structure, or concentration in the film, and the irradiated UV laser power.

    Science.gov (United States)

    Hosokawa, Akihiro; Kato, Yoshiteru

    2011-08-01

    The purpose of this article is to study factors affecting color strength of printing on film-coated tablets by ultraviolet (UV) laser irradiation: particle size, crystal structure, or concentration of titanium dioxide (TiO2) in film, and irradiated UV laser power. Hydroxypropylmethylcellulose films containing 4.0% of TiO2, of which BET particle sizes were ranging from 126.1 to 219.8 nm, were irradiated 3.14W of UV laser at a wavelength 355 nm to study effects of TiO2 particle size and crystal structure on the printing. The films containing TiO2 concentration ranging from 1.0 to 7.7% were irradiated 3.14 or 5.39W of the UV laser to study effect of TiO2 concentration on the printing. The film containing 4.0% of TiO2, was irradiated the UV laser up to 6.42W to study effect of the UV laser power on the printing. The color strength of the printed films was estimated by a spectrophotometer as total color difference (dE). Particle size, crystal structure, and concentration of TiO2 in the films did not affect the printing. In the relationship between the irradiated UV laser power and dE, there found an inflection point (1.6W). When the UV laser power was below 1.6W, the films were not printed. When it was beyond the point, total color difference increased linearly in proportion with the irradiated laser power. The color strength of the printing on film was not changed by TiO2 particle size, crystal structure, and concentration, but could be controlled by regulating the irradiated UV laser power beyond the inflection point.

  3. Formation of organobromine and organoiodine compounds by engineered TiO2 nanoparticle-induced photohalogenation of dissolved organic matter in environmental waters.

    Science.gov (United States)

    Hao, Zhineng; Yin, Yongguang; Wang, Juan; Cao, Dong; Liu, Jingfu

    2018-08-01

    There are increasing concerns about the adverse effects of released engineered nanoparticles and photochemically formed organohalogen compounds (OHCs) on human health and the environment. Herein, we report that titanium dioxide nanoparticles (TiO 2 NPs) can photocatalytically halogenate dissolved organic matter (DOM) to form a large number of organobromine compounds (OBCs) and organoiodine compounds (OICs), as characterized by negative ion electrospray ionization coupled with Fourier transform ion cyclotron resonance mass spectrometry. Compared with no OHCs produced in control samples in darkness and/or without TiO 2 NPs under sunlight irradiation, various OBCs and OICs were detected in freshwater and seawater under sunlight irradiation for 12h and 24h even in the presence of 1mgL -1 TiO 2 NPs, indicating the photocatalytic roles TiO 2 NPs played in DOM halogenation. Furthermore, TiO 2 NPs could result in the photodegradation of newly formed OHCs, as evidenced by the intensity and the number of some OHCs decreased with reaction time. In addition, many TiO 2 NP-induced OBCs contained two or three bromine atoms, and/or nitrogen and sulfur elements, belonging to lignin-like, tannin-like, unsaturated hydrocarbon and aliphatic compounds. While the OICs were primarily contained one iodine, and very few consisted of nitrogen and sulfur elements, most were lignin-like and tannin-like compounds. Finally, the OBCs in freshwater were found to be formed mainly via a substitution reaction or addition reaction and were accompanied by other reactions such as photooxidation, while the OBCs in seawater and OICs were formed primarily via substitution reactions. Given the abundance of produced OHCs and their toxicity, our findings call for further studies on the exact structure and toxicity of the formed OHCs, taking account the TiO 2 NP-induced DOM photohalogenation in aquatic environments during the evaluation of the environmental effects of engineered TiO 2 NPs. Copyright © 2018

  4. Trace recovery of uranium and rare earth contained in phosphates by liquid-liquid extraction in sulfuric attack liquor

    International Nuclear Information System (INIS)

    Bousquet, F.; Foraison, D.; Leveque, A.; Sabot, J.L.

    1980-06-01

    Uranium and rare earths can be recovered in sedimentary phosphates during the wet processing of the ore by sulfuric acid giving raw phosphoric acid at 30 per cent of P 2 O 5 . Practically all the uranium contained and only part of rare earths are put into solution in this treatment. Separation of these elements in the phosphoric solution is obtained by liquid-liquid extraction with alkylphosphoric acids and especially with their mono and di esters. Partition isotherms are determined and counter-current tests are effected. Uranium and rare earths reextraction from these solvents can be simultaneous or separate with aqueous solutions alkaline or containing HF or by antisynergism. Pros and cons of each reextraction process are discussed. In conclusion HDEHP or OPPA are recommended because of availability, stability and hydrodynamic, OPPA less selective with rare earths allows the recovery with uranium of ceric earths, yttrium and yttric earths [fr

  5. Modeling and calculation of RKKY exchange coupling to explain Ti-vacancy-induced ferromagnetism in Ta-doped TiO2

    Science.gov (United States)

    Majidi, Muhammad Aziz; Bupu, Annamaria; Fauzi, Angga Dito

    2017-12-01

    We present a theoretical study on Ti-vacancy-induced ferromagnetism in anatase TiO2. A recent experimental study has revealed room temperature ferromagnetism in Ta-doped anatase TiO2thin films (Rusydi et al., 2012) [7]. Ta doping assists the formation of Ti vacancies which then induce the formation of localized magnetic moments around the Ti vacancies. As neighboring Ti vacancies are a few unit cells apart, the ferromagnetic order is suspected to be mediated by itinerant electrons. We propose that such an electron-mediated ferromagnetism is driven by Ruderman-Kittel-Kasuya-Yosida (RKKY) exchange interaction. To examine our hypothesis, we construct a tight-binding based model Hamiltonian for the anatase TiO2 system. We calculate the RKKY exchange coupling constant of TiO2 as a function of distance between local magnetic moments at various temperatures. We model the system by taking only the layer containing a unit of TiO2, at which the Ti vacancy is believed to form, as our effective two-dimensional unit cell. Our model incorporates the Hubbard repulsive interactions between electrons occupying Ti d orbitals treated within mean-field approximation. The density of states profile resulting from the model captures the relevant electronic properties of TiO2, such as the energy gap of 3.4 eV and the n-type character, which may be a measure of the adequacy of the model. The calculated RKKY coupling constant shows that the ferromagnetic coupling extends up to 3-4 unit cells and enhances slightly as temperature is increased from 0 to 400 K. These results support our hypothesis that the ferromagnetism of this system is driven by RKKY mechanism.

  6. Degradation of Methyl Orange and Congo Red dyes by using TiO2 nanoparticles activated by the solar and the solar-like radiation.

    Science.gov (United States)

    Ljubas, Davor; Smoljanić, Goran; Juretić, Hrvoje

    2015-09-15

    In this study we used TiO2 nanoparticles as semiconductor photocatalysts for the degradation of Methyl Orange (MO) and Congo Red (CR) dyes in an aqueous solution. Since TiO2 particles become photocatalytically active by UV radiation, two sources of UV-A radiation were used - natural solar radiation which contains 3-5% UV-A and artificial, solar-like radiation, created by using a lamp. The optimal doses of TiO2 of 500 mg/L for the CR and 1500 mg/L for the MO degradation were determined in experiments with the lamp and were also used in degradation experiments with natural solar light. The efficiency of each process was determined by measuring the absorbance at two visible wavelengths, 466 nm for MO and 498 nm for CR, and the total organic carbon (TOC), i.e. decolorization and mineralization, respectively. In both cases, considerable potential for the degradation of CR and MO was observed - total decolorization of the solution was achieved within 30-60 min, while the TOC removal was in the range 60-90%. CR and MO solutions irradiated without TiO2 nanoparticles showed no observable changes in either decolorization or mineralization. Three different commercially available TiO2 nanoparticles were used: pure-phase anatase, pure-phase rutile, and mixed-phase preparation named Degussa P25. In terms of degradation kinetics, P25 TiO2 exhibited a photocatalytic activity superior to that of pure-phase anatase or rutile. The electric energy consumption per gram of removed TOC was determined. For nearly the same degradation effect, the consumption in the natural solar radiation experiment was more than 60 times lower than in the artificial solar-like radiation experiment. Copyright © 2015 Elsevier Ltd. All rights reserved.

  7. Comparative assessment of the efficiency of Fe-doped TiO2 prepared by two doping methods and photocatalytic degradation of phenol in domestic water suspensions

    Directory of Open Access Journals (Sweden)

    Mst. Shamsun Nahar, Kiyoshi Hasegawa, Shigehiro Kagaya and Shigeyasu Kuroda

    2007-01-01

    Full Text Available Fe-doped TiO2 particles responding to visible light were synthesized by impregnation and calcination method using TiO2 particle and Ti element, respectively. The optical and the chemical properties were characterized by measuring the X-ray diffraction (XRD and UV–visible spectroscopy. The onset of absorption shifted to longer wavelengths on doping TiO2 by the calcination process, which showed a better response as compared to the impregnation method. The photocatalytic reactivity was evaluated by the degradation of phenol with impregnated Fe-doped (0.5% w/w in Fe and calcined Fe-doped (FexTi1−xO2, x=0.005 (Fe/Ti molar ratio TiO2 separately in distilled and tap water. The characterization results have confirmed the advanced possibility of correlation between photoactivity and the special property of sulfur-containing calcined Fe-doped TiO2. In case of the coagulation of the undoped A-I and the Fe-doped B-I, the photoactivity showed a decrease due to the presence of natural electrolytes and due to the high pH of tap water, whereas in the case of the coagulation of calcined Fe-doped TiO2 prepared from sulfides (FexTiS2, the photoactivity showed an increase. In this study, highest catalytic activity was found to be strongly dependent both on catalyst structure and on the type of water used.

  8. Effect of TiO2 Nanofiller Concentration on the Mechanical, Thermal and Biological Properties of HDPE/TiO2 Nanocomposites

    Science.gov (United States)

    Mozumder, Mohammad Sayem; Mourad, Abdel-Hamid I.; Mairpady, Anusha; Pervez, Hifsa; Haque, Md Emdadul

    2018-05-01

    The necessity for advanced and effective biomimetic tissue engineering materials has increased massively as bone diseases such as osteoporosis and bone cancer have become a major public health problem. Therefore, the objective of this study is to develop titanium dioxide (TiO2) nanoparticles-enriched high-density polyethylene (HDPE) nanocomposites that could serve as potential biomaterials. HDPE/TiO2 nanocomposites with varying TiO2 nanoparticles content were fabricated by using injection molding technique and were subjected to mechanical, thermal and biological characterization. SEM-EDS analysis confirmed even dispersion of TiO2 nanoparticles into the HDPE matrix. It was observed from the mechanical testing that the addition of TiO2 nanoparticles to HDPE noticeably improved the stiffness (from 345 to 378 MPa) while maintaining almost similar yield strength of pure HDPE. The thermal analyses revealed that TiO2 nanoparticles inclusion to HDPE matrix enhanced the thermal stability of nanocomposites, as the overall rate of crystallization increased by almost 4%. Furthermore, biocompatibility of nanocomposites was also studied by means of various cell culture experiments; human osteoblasts (hFOB) were seeded on the HDPE/TiO2 nanocomposites and were visualized through SEM after 72 h of incubation; surface morphology revealed normal cell growth and spreading with more attachment on PNC-10 that contains 10 wt.% of TiO2. Moreover, cell viability assays (i.e., MTT and cell attachment) revealed consistent increase in cell count and metabolic activity when triplicate cultures were incubated for 1, 3 and 7 days.

  9. Development and Application of Binary Suspensions in the Ternary System Cr2O3-TiO2-Al2O3 for S-HVOF Spraying

    Science.gov (United States)

    Potthoff, Annegret; Kratzsch, Robert; Barbosa, Maria; Kulissa, Nick; Kunze, Oliver; Toma, Filofteia-Laura

    2018-04-01

    Compositions in the system Cr2O3-TiO2-Al2O3 are among the most used ceramic materials for thermally sprayed coating solutions. Cr2O3 coatings present good sliding wear resistance; Al2O3 coatings show excellent insulation behavior and TiO2 striking corrosion properties. In order to combine these properties, coatings containing more than one oxide are highly interesting. The conventional spraying process is limited to the availability of binary feedstock powders with defined compositions. The use of suspensions offers the opportunity for tailor-made chemical compositions: within the triangle of Cr2O3-TiO2-Al2O3, each mixture of oxides can be created. Criteria for the selection of raw materials as well as the relevant aspects for the development of binary suspensions in the Cr2O3-TiO2-Al2O3 system to be used as feedstock for thermal spraying are presented. This formulation of binary suspensions required the development of water-based single-oxide suspensions with suitable behavior; otherwise, the interaction between the particles while mixing could lead up to a formation of agglomerates, which affect both the stability of the spray process and the coating properties. For the validation of this formulation procedure, binary Cr2O3-TiO2 and Al2O3-TiO2 suspensions were developed and sprayed using the S-HVOF process. The binary coatings were characterized and discussed in terms of microstructure and microhardness.

  10. Effect of TiO2 Nanofiller Concentration on the Mechanical, Thermal and Biological Properties of HDPE/TiO2 Nanocomposites

    Science.gov (United States)

    Mozumder, Mohammad Sayem; Mourad, Abdel-Hamid I.; Mairpady, Anusha; Pervez, Hifsa; Haque, Md Emdadul

    2018-03-01

    The necessity for advanced and effective biomimetic tissue engineering materials has increased massively as bone diseases such as osteoporosis and bone cancer have become a major public health problem. Therefore, the objective of this study is to develop titanium dioxide (TiO2) nanoparticles-enriched high-density polyethylene (HDPE) nanocomposites that could serve as potential biomaterials. HDPE/TiO2 nanocomposites with varying TiO2 nanoparticles content were fabricated by using injection molding technique and were subjected to mechanical, thermal and biological characterization. SEM-EDS analysis confirmed even dispersion of TiO2 nanoparticles into the HDPE matrix. It was observed from the mechanical testing that the addition of TiO2 nanoparticles to HDPE noticeably improved the stiffness (from 345 to 378 MPa) while maintaining almost similar yield strength of pure HDPE. The thermal analyses revealed that TiO2 nanoparticles inclusion to HDPE matrix enhanced the thermal stability of nanocomposites, as the overall rate of crystallization increased by almost 4%. Furthermore, biocompatibility of nanocomposites was also studied by means of various cell culture experiments; human osteoblasts (hFOB) were seeded on the HDPE/TiO2 nanocomposites and were visualized through SEM after 72 h of incubation; surface morphology revealed normal cell growth and spreading with more attachment on PNC-10 that contains 10 wt.% of TiO2. Moreover, cell viability assays (i.e., MTT and cell attachment) revealed consistent increase in cell count and metabolic activity when triplicate cultures were incubated for 1, 3 and 7 days.

  11. Development and Application of Binary Suspensions in the Ternary System Cr2O3-TiO2-Al2O3 for S-HVOF Spraying

    Science.gov (United States)

    Potthoff, Annegret; Kratzsch, Robert; Barbosa, Maria; Kulissa, Nick; Kunze, Oliver; Toma, Filofteia-Laura

    2018-03-01

    Compositions in the system Cr2O3-TiO2-Al2O3 are among the most used ceramic materials for thermally sprayed coating solutions. Cr2O3 coatings present good sliding wear resistance; Al2O3 coatings show excellent insulation behavior and TiO2 striking corrosion properties. In order to combine these properties, coatings containing more than one oxide are highly interesting. The conventional spraying process is limited to the availability of binary feedstock powders with defined compositions. The use of suspensions offers the opportunity for tailor-made chemical compositions: within the triangle of Cr2O3-TiO2-Al2O3, each mixture of oxides can be created. Criteria for the selection of raw materials as well as the relevant aspects for the development of binary suspensions in the Cr2O3-TiO2-Al2O3 system to be used as feedstock for thermal spraying are presented. This formulation of binary suspensions required the development of water-based single-oxide suspensions with suitable behavior; otherwise, the interaction between the particles while mixing could lead up to a formation of agglomerates, which affect both the stability of the spray process and the coating properties. For the validation of this formulation procedure, binary Cr2O3-TiO2 and Al2O3-TiO2 suspensions were developed and sprayed using the S-HVOF process. The binary coatings were characterized and discussed in terms of microstructure and microhardness.

  12. Xanes and SR-XRF Study of Skin as a Barrier to Ultra-Fine Nanocrystals of TiO2

    International Nuclear Information System (INIS)

    Kwiatek, W.M.; Lekki, J.; Stachura, Z.; Hanson, A.; Ablett, J.

    2007-01-01

    Nanocrystalline TiO 2 is commonly used in cosmetic industry as a photoprotective agent. With recent advances in nanomaterial processing, the size of TiO 2 crystals decreased into the nanometre regime. There is no satisfactory evidence that crystals of such small size are harmless to the human population. An EU project NANODERM has been launched where several techniques have been applied to investigate the possibility of particle penetration through the protective horny layer into vital skin regions. Skin biopsies of the animal and human skin have been collected after exposition to formulations containing TiO 2 nanocrystals. The Ti depth distributions were measured by electron and ion microscopy. The microscopy studies did not detect penetration into vital tissue of healthy skin what does not exclude a possibility that TiO 2 could penetrate pathological skin with lowered barrier efficiency. Due to literature the physical effect of the UV irradiation of the TiO 2 nanoparticle is the shift from 4 th to 3 rd oxidation state of the Ti. Titanium at 3 rd oxidation state interact with environment producing free radicals and Reactive Oxygen Species. In order to quantify the oxidation state shift, XANES experiments were carried out with commercially available TiO 2 nanocrystals (6 - 100 nm size), both in anatase and rutile phase. The samples were irradiated with X-rays with, and without accompanying UV illumination at the NSLS X27A beam line. The corresponding XANES spectra were registered and the absorption edge was compared in UV - illuminated and not illuminated spectra. A shift of about 1 eV in the absorption edge position of the rutile sample exposed to UVA light (365 nm, 20 mW/cm 2 ) has been measured and attributed to the changed electron configuration. However, the direction of the shift detected in measured samples was opposite to the expected. (author)

  13. Photocatalytic degradation of paracetamol on TiO2 nanoparticles and TiO2/cellulosic fiber under UV and sunlight irradiation

    Directory of Open Access Journals (Sweden)

    Nabil Jallouli

    2017-05-01

    Full Text Available In the present study, photocatalytic degradation of acetaminophen ((N-(4-hydroxyphe-nylacetamide, an analgesic drug has been investigated in a batch reactor using TiO2 P25 as a photocatalyst in slurry and under UV light. Using TiO2 P25 nanoparticles, much faster photodegradation of paracetamol and effective mineralization occurred, more than 90% of 2.65 × 10−4 M paracetamol was degraded under UV irradiation. Changes in pH values affected the adsorption and the photodegradation of paracetamol. pH 9.0 is found to be the optimum for the photodegradation of paracetamol. HPLC detected hydroquinone, benzoquinone, p-nitrophenol, and 1,2,4-trihydroxybenzene during the TiO2-assisted photodegradation of paracetamol among which some pathway products are disclosed for the first time. The results showed that TiO2 suspension/UV system is more efficient than the TiO2/cellulosic fiber mode combined to solar light for the photocatalytic degradation of paracetamol. Nerveless the immobilization of TiO2 showed many advantages over slurry system because it can enhance adsorption properties while allowing easy separation of the photocatalyst from the treated solution with improved reusable performance.

  14. SiO2@TiO2 Coating: Synthesis, Physical Characterization and Photocatalytic Evaluation

    Directory of Open Access Journals (Sweden)

    A. Rosales

    2018-03-01

    Full Text Available Use of silicon dioxide (SiO2 and titanium dioxide (TiO2 have been widely investigated individually in coatings technology, but their combined properties promote compatibility for different innovative applications. For example, the photocatalytic properties of TiO2 coatings, when exposed to UV light, have interesting environmental applications, such as air purification, self-cleaning and antibacterial properties. However, as reported in different pilot projects, serious durability problems, associated with the adhesion between the substrate and TiO2, have been evidenced. Thus, the aim of this work is to synthesize SiO2 together with TiO2 to increase the durability of the photocatalytic coating without affecting its photocatalytic potential. Therefore, synthesis using sonochemistry, synthesis without sonochemistry, physical characterization, photocatalytic evaluation, and durability of the SiO2, SiO2@TiO2 and TiO2 coatings are presented. Results indicate that using SiO2 improved the durability of the TiO2 coating without affecting its photocatalytic properties. Thus, this novel SiO2@TiO2 coating shows potential for developing long-lasting, self-cleaning and air-purifying construction materials.

  15. Synthesis of TiO2-doped SiO2 composite films and its applications

    Indian Academy of Sciences (India)

    Wintec

    structure of the titanium oxide species in the TiO2-doped SiO2 composite films and the photocatalytic reactiv- ity in order to ... gaku D-max γA diffractometer with graphite mono- chromized ... FT–IR absorption spectra of TiO2-doped SiO2 com-.

  16. TiO2-Based Advanced Oxidation Nanotechnologies For Water Purification And Reuse

    Science.gov (United States)

    TiO2 photocatalysis, one of the UV-based advanced oxidation technologies (AOTs) and nanotechnologies (AONs), has attracted great attention for the development of efficient water treatment and purification systems due to the effectiveness of TiO2 to generate ...

  17. Oxidation and photo-oxidation of water on TiO2 surface

    DEFF Research Database (Denmark)

    Valdes, A.; Qu, Z.W.; Kroes, G.J.

    2008-01-01

    The oxidation and photo-oxidation of water on the rutile TiO2(110) surface is investigated using density functional theory (DFT) calculations. We investigate the relative stability of different surface terminations of TiO2 interacting with H2O and analyze the overpotential needed for the electrol...

  18. Hazards of TiO2 and amorphous SiO2 nanoparticles

    NARCIS (Netherlands)

    Reijnders, L.; Kahn, H.A.; Arif, I.A.

    2012-01-01

    TiO2 and amorphous SiO2 nanoparticles have been described as ‘safe’, ‘non-toxic’ and ‘environment friendly’ in scientific literature. However, though toxicity data are far from complete, there is evidence that these nanoparticles are hazardous. TiO2 nanoparticles have been found hazardous to humans

  19. Spectral Sensitization of TiO2 Substrates by Monolayers of Porphyrin Heterodimers

    NARCIS (Netherlands)

    Koehorst, R.B.M.; Boschloo, G.K.; Savenije, T.J.; Goossens, A.; Schaafsma, T.J.

    2000-01-01

    Photoelectrochemical cells have been constructed by depositing monolayers of oriented covalently linked zinc/free base porphyrin heterodimers onto ~30 nm nonporous layers of TiO2 on ITO, deposited by metal-organic chemical vapor deposition (MO-CVD), and onto ~100 nm porous, nanostructured TiO2

  20. Construction of hydrophobic wood surfaces by room temperature deposition of rutile (TiO2) nanostructures

    Science.gov (United States)

    Rongbo Zheng; Mandla A. Tshabalala; Qingyu Li; Hongyan Wang

    2015-01-01

    A convenient room temperature approach was developed for growing rutile TiO2 hierarchical structures on the wood surface by direct hydrolysis and crystallization of TiCl3 in saturated NaCl aqueous solution.The morphology and the crystal structure of TiO2 coated on the wood surface were characterized...

  1. TiO2 Based Photocatalyst: From Synthesis and Characterization to Optimization and Design

    DEFF Research Database (Denmark)

    Su, Ren

    2012-01-01

    TiO2 based photocatalyst has attracted gerat attentions from both fundamental and an applied aspects in water/air purifications and energy production. In this thesis, series of well-defined TiO2 photocatalyst with various parameters (i.e., polymorph composition, shape, impurity concentration, sur...

  2. Characterization of low temperature deposited atomic layer deposition TiO2 for MEMS applications

    NARCIS (Netherlands)

    Huang, Y.; Pandraud, G.; Sarro, P.M.

    2012-01-01

    TiO2 is an interesting and promising material for micro-/nanoelectromechanical systems (MEMS/NEMS). For high performance and reliable MEMS/NEMS, optimization of the optical characteristics, mechanical stress, and especially surface smoothness of TiO2 is required. To overcome the roughness issue of

  3. The Effects of Leaching Process to the TiO2 Synthesis from Bangka Ilmenite

    Science.gov (United States)

    Wahyuningsih, S.; Ramelan, A. H.; Pramono, E.; Argawan, P.; Djatisulistya, A.; Firdiyono, F.; Sulistiyono, E.; Sari, P. P.

    2018-03-01

    Ilmenite mineral is a naturally occurring iron titanate (FeTiO3) and is abundant in nature. The separation of components into TiO2 and Fe2O3 must be expand. The purpose of this research is to synthesis TiO2 nanoparticles from the filtrate of Bangka ilmenite leaching process. Leaching of ilmenite was done with H2SO4 and HCl at various concentrations. The formation of TiO2 crystal determined by hydrolysis conditions and condensation reaction. TiO2 synthesized from the filtrate of sulfuric acid leaching that produced from TiO2 anatase phase when hydrolyzed in an aquaregia solvent and low concentrations of HCl (0.1M). Hydrolysis conditions at higher concentrations of HCl (1M) was produced TiO2 anatase-rutile phase. The synthesis of TiO2 from the filtrate of hydrochloric acid leaching was produced anatase phase. While the condition under the alcoholic solvent (2-propanol: H2O (v/v) = 9: 1) anatase phase crystallites grow in the temperature range up to 550 °C, above this temperature, TiO2 transform into rutile phase.

  4. Hydrothermal synthesis of TiO2 Nanotubes: Microwave heating versus conventional heating

    CSIR Research Space (South Africa)

    Sikhwivhilu, LM

    2010-01-01

    Full Text Available The influence of the method of synthesis in the properties of the tubular structures derived from TiO2 was investigated using XRD, SEM and BET analysis. The use of microwave irradiation resulted in the formation of TiO2 tubes comprising anatase...

  5. TiO2 Photocatalysis Damages Lipids and Proteins in Escherichia coli

    NARCIS (Netherlands)

    Carre, Gaelle; Hamon, Erwann; Ennahar, Said; Estner, Maxime; Lett, Marie-Claire; Horvatovich, Peter; Gies, Jean-Pierre; Keller, Valerie; Keller, Nicolas; Andre, Philippe

    This study investigates the mechanisms of UV-A (315 to 400 nm) photocatalysis with titanium dioxide (TiO2) applied to the degradation of Escherichia coli and their effects on two key cellular components: lipids and proteins. The impact of TiO2 photocatalysis on E. coli survival was monitored by

  6. New TiO2/DSAT Immobilization System for Photodegradation of Anionic and Cationic Dyes

    Directory of Open Access Journals (Sweden)

    Wan Izhan Nawawi Wan Ismail

    2015-01-01

    Full Text Available A new immobilized TiO2 technique was prepared by coating TiO2 solution onto double-sided adhesive tape (DSAT as a thin layer binder without adding any organic additives. Glass plate was used as support material to immobilized TiO2/DSAT. Two different charges of dyes were applied, namely, anionic reactive red 4 (RR4 and cationic methylene blue (MB dyes. Photocatalytic degradation of RR4 and MB dyes was observed under immobilized TiO2/DSAT with the degradation rate slightly lower and higher, respectively, compared with TiO2 in suspension mode. It was observed that DSAT is able to provide a very strong intact between glass and TiO2 layers thus making the reusability of immobilized TiO2/DSAT be up to 30 cycles. In fact, a better photodegradation activity was observed by number of cycles due to increasing formation of pores on TiO2 surface observed by SEM analysis.

  7. Photocatalytic properties of porous TiO2/Ag thin films

    International Nuclear Information System (INIS)

    Chang, C.-C.; Chen, J.-Y.; Hsu, T.-L.; Lin, C.-K.; Chan, C.-C.

    2008-01-01

    In this study, nanocrystalline TiO 2 /Ag composite thin films were prepared by a sol-gel spin-coating technique. By introducing polystyrene (PS) spheres into the precursor solution, porous TiO 2 /Ag thin films were prepared after calcination at a temperature of 500 deg. C for 4 h. Three different sizes (50, 200, and 400 nm) of PS spheres were used to prepare porous TiO 2 films. The as-prepared TiO 2 and TiO 2 /Ag thin films were characterized by X-ray diffractometry (XRD) and by scanning electron microscopy to reveal structural and morphological differences. In addition, the photocatalytic properties of these films were investigated by degrading methylene blue under UV irradiation. When PS spheres of different sizes were introduced after calcination, the as-prepared TiO 2 films exhibited different porous structures. XRD results showed that all TiO 2 /Ag films exhibited a major anatase phase. The photodegradation of porous TiO 2 thin films prepared with 200 nm PS spheres and doped with 1 mol% Ag exhibited the best photocatalytic efficiency where ∼ 100% methylene blue was decomposed within 8 h under UV exposure

  8. Synthesis of nanocrystalline TiO2 thin films by liquid phase ...

    Indian Academy of Sciences (India)

    WINTEC

    goes degradation efficiently in presence of TiO2 thin films by exposing its aqueous solution to .... Figure 6. Photodegradation of IGOR organic dye by a. bare TiO2 thin film and b. ... Meng L-J and Dos Santos M P 1993 Thin Solid Films 226 22.

  9. Synthesis, structure and photocatalytic activity of nano TiO2 and ...

    Indian Academy of Sciences (India)

    salicylic acid over combustion-synthesized nano TiO2 under UV and solar exposure has been carried out. Under identical conditions of UV exposure, the initial degra- dation rate of phenol with combustion-synthesized TiO2 is two times higher than the initial degradation rate of phenol with Degussa P25, the commercial ...

  10. Microstructure and antibacterial property of in situ TiO(2) nanotube layers/titanium biocomposites.

    Science.gov (United States)

    Cui, C X; Gao, X; Qi, Y M; Liu, S J; Sun, J B

    2012-04-01

    The TiO(2) nanotube layer was in situ synthesized on the surface of pure titanium by the electrochemical anodic oxidation. The diameter of nano- TiO(2) nanotubes was about 70~100 nm. The surface morphology and phase compositions of TiO(2) nanotube layers were observed and analyzed using the scanning electron microscope (SEM). The important processing parameters, including anodizing voltage, reaction time, concentration of electrolyte, were optimized in more detail. The photocatalytic activity of the nano- TiO(2) nanotube layers prepared with optimal conditions was evaluated via the photodegradation of methylthionine in aqueous solution. The antibacterial property of TiO(2) nanotube layers prepared with optimal conditions was evaluated by inoculating Streptococcus mutans on the TiO(2) nanotube layers in vitro. The results showed that TiO(2) nanotube layers/Ti biocomposites had very good antibacterial activity to resist Streptococcus mutans. As a dental implant biomaterial, in situ TiO(2) nanotube layer/Ti biocomposite has better and wider application prospects. Copyright © 2012 Elsevier Ltd. All rights reserved.

  11. Growth and characterization of hydroxyapatite nanorice on TiO2 nanofibers

    KAUST Repository

    Chetibi, Loubna; Hamana, Djamel; Achour, Slimane

    2014-01-01

    with anatase TiO2 nanofibers. These nanofibers were prepared by in situ oxidation of Ti foils in a concentrated solution of H 2O2 and NaOH, followed by proton exchange and calcinations. Afterward, TiO2 nanofibers on Ti substrate were coated with HA

  12. Electrospinning processed nanofibrous TiO2 membranes for photovoltaic applications

    Science.gov (United States)

    Onozuka, Katsuhiro; Ding, Bin; Tsuge, Yosuke; Naka, Takayuki; Yamazaki, Michiyo; Sugi, Shinichiro; Ohno, Shingo; Yoshikawa, Masato; Shiratori, Seimei

    2006-02-01

    We have recently fabricated dye-sensitized solar cells (DSSCs) comprising nanofibrous TiO2 membranes as electrode materials. A thin TiO2 film was pre-deposited on fluorine doped tin oxide (FTO) coated conducting glass substrate by immersion in TiF4 aqueous solution to reduce the electron back-transfer from FTO to the electrolyte. The composite polyvinyl acetate (PVac)/titania nanofibrous membranes can be deposited on the pre-deposited thin TiO2 film coated FTO by electrospinning of a mixture of PVac and titanium isopropoxide in N,N-dimethylformamide (DMF). The nanofibrous TiO2 membranes were obtained by calcining the electrospun composite nanofibres of PVac/titania as the precursor. Spectral sensitization of the nanofibrous TiO2 membranes was carried out with a ruthenium (II) complex, cis-dithiocyanate-N,N'-bis(2,2'-bipyridyl-4,4'-dicarboxylic acid) ruthenium (II) dihydrate. The results indicated that the photocurrent and conversion efficiency of electrodes can be increased with the addition of the pre-deposited TiO2 film and the adhesion treatment using DMF. Additionally, the dye loading, photocurrent, and efficiency of the electrodes were gradually increased by increasing the average thickness of the nanofibrous TiO2 membranes. The efficiency of the fibrous TiO2 photoelectrode with the average membrane thickness of 3.9 µm has a maximum value of 4.14%.

  13. Nanoscale surface potential imaging of the photocatalytic TiO2 films on aluminum

    DEFF Research Database (Denmark)

    Daviðsdóttir, Svava; Dirscherl, Kai; Canulescu, Stela

    2013-01-01

    in the surface potential of TiO2 coatings upon UV-illumination are closely correlated to the band gap and thickness of the coatings. The inhomogeneity surface potential distribution of a 100 nm TiO2 film indicates a heterogeneous coating. Transition to a homogeneous surface potential distribution was observed...

  14. TiO2@C Core-Shell Nanoparticles Formed by Polymeric Nano-Encapsulation

    Directory of Open Access Journals (Sweden)

    Mitra eVasei

    2014-07-01

    Full Text Available TiO2 semiconducting nanoparticles are known to be photocatalysts of moderate activity due to their high band-gap and high rate of electron-hole recombination. The formation of a shell of carbon around the core of TiO2, i.e. the formation of TiO2@C nanoparticles, is believed to partly alleviate these problems. It is usually achieved by a hydrothermal treatment in a presence of a sugar derivative. We present here a novel method for the formation of highly uniform C shell around TiO2 nanoparticles. For this purpose, TiO2 nanoparticles were dispersed in water using an oligomeric dispersant prepared by Reversible Addition-Fragmentation chain Transfer (RAFT polymerization. Then the nanoparticles were engaged into an emulsion polymerization of acrylonitrile, resulting in the formation of a shell of polyacrylonitrile (PAN around each TiO2 nanoparticles. Upon pyrolisis, the PAN was transformed into carbon, resulting in the formation of TiO2@C nanoparticles. The structure of the resulting particles was elucidated by X-Ray diffraction, FTIR, UV-VIS and Raman spectroscopy as well as TEM microscopy. Preliminary results about the use of the TiO2@C particles as photocatalysts for the splitting of water are presented. They indicate that the presence of the C shell is responsible for a significant enhancement of the photocurrent.

  15. Hot corrosion performance of LVOF sprayed Al2O3–40% TiO2 ...

    Indian Academy of Sciences (India)

    ficients of thermal expansions of the two. ... size 40 mesh just prior to deposition of the coating. Al2O3–. 40% TiO2 ... the laboratory Kanthal wire tube furnace, which was cali- ... formation of TiO2, Al2O3 and Al2Ti7O15 phases in the coat- ing.

  16. Intrinsic Photocatalytic Assessment of Reactively Sputtered TiO2 Films

    NARCIS (Netherlands)

    Rafieian Boroujeni, Damon; Driessen, Rick Theodorus; Driessen, Rick T.; Ogieglo, Wojciech; Lammertink, Rob G.H.

    2015-01-01

    Thin TiO2 films were prepared by DC magnetron reactive sputtering at different oxygen partial pressures. Depending on the oxygen partial pressure during sputtering, a transition from metallic Ti to TiO2 was identified by spectroscopic ellipsometry. The crystalline nature of the film developed during

  17. Electrochemical characteristics of porous TiO2 encapsulated silicon anode

    International Nuclear Information System (INIS)

    Jeon, Bup Ju; Lee, Joong Kee

    2011-01-01

    Graphical abstract: Cycling performances of the TiO 2 coated silicon anode at different catalyst pH values. Display Omitted Highlights: → TiO 2 coated silicon was used as the anode material for lithium batteries. → TiO 2 layer acted as a buffer layer for reducing the volume expansion. → Pore size distribution of TiO 2 coated silicon influenced discharge capacity. → Higher capacity retention was exhibited at pH 10.7. - Abstract: TiO 2 coated silicon, which was prepared by the modified sol-gel method, was employed as the anode material for lithium secondary batteries and the relationship between the diffusivity and electrochemical characteristics was investigated. The results showed that the physical properties of the samples, such as their diffusivity and pore size distribution, enhanced the cycling efficiency of the TiO 2 coated silicon, probably due to the reduction of the side reactions, which may be closely related to the pore size distribution of the TiO 2 coating layer. The pore size of the coating layer plays an important role in retarding the lithium ion diffusion. In the experimental range studied herein, higher capacity retention was exhibited for the TiO 2 coated silicon prepared at pH 10.7.

  18. Fullerene C70 decorated TiO2 nanowires for visible-light-responsive photocatalyst

    International Nuclear Information System (INIS)

    Cho, Er-Chieh; Ciou, Jing-Hao; Zheng, Jia-Huei; Pan, Job; Hsiao, Yu-Sheng; Lee, Kuen-Chan; Huang, Jen-Hsien

    2015-01-01

    Graphical abstract: - Highlights: • TiO 2 nanowire decorated with C 60 and C 70 derivatives has been synthesized. • The fullerenes impede the charge recombination due to its high electron affinity. • The fullerenes expand the utilization of solar light from UV to visible light. • The modified-TiO 2 has great biocompatibility. - Abstract: In this study, we have synthesized C 60 and C 70 -modified TiO 2 nanowire (NW) through interfacial chemical bonding. The results indicate that the fullerenes (C 60 and C 70 derivatives) can act as sinks for photogenerated electrons in TiO 2 , while the fullerene/TiO 2 is illuminated under ultraviolet (UV) light. Therefore, in comparison to the pure TiO 2 NWs, the modified TiO 2 NWs display a higher photocatalytic activity under UV irradiation. Moreover, the fullerenes also can function as a sensitizer to TiO 2 which expand the utilization of solar light from UV to visible light. The results reveal that the C 70 /TiO 2 NWs show a significant photocatalytic activity for degradation of methylene blue (MB) in visible light region. To better understand the mechanism responsible for the effect of fullerenes on the photocatalytic properties of TiO 2 , the electron only devices and photoelectrochemical cells based on fullerenes/TiO 2 are also fabricated and evaluated.

  19. Complex impedance study on nano-CeO2 coating TiO2

    International Nuclear Information System (INIS)

    Zhang Mei; Wang Honglian; Wang Xidong; Li Wenchao

    2006-01-01

    Titanium dioxide (TiO 2 ) nanoparticles and cerium dioxide (CeO 2 ) nanoparticles coated titanium dioxide (TiO 2 ) nanoparticles (CeO 2 -TiO 2 nanoparticles) have been successfully synthesized by sol-gel method. The complex impedance of the materials was investigated. The grain resistance, boundary resistance and activation energy of the nanoparticles were calculated according to Arrhenius equation. According to calculating results, the active capacity of pure TiO 2 nanoparticles has been improved because of nano-CeO 2 coating. An optimal CeO 2 content of 4.9 mol% was achieved. The high resolution electron microscopy images of CeO 2 -TiO 2 nanoparticles showed that TiO 2 nanoparticles, as a core, were covered by CeO 2 nanoparticles. The average size of CeO 2 coating TiO 2 nanoparticles was about 70 nm. Scanning electron microscopy observation indicted that CeO 2 nanoparticle coating improved the separation, insulation, and stability the CeO 2 -TiO 2 nanoparticles, which was benefit to the activity of materials

  20. MoSe2 modified TiO2 nanotube arrays with superior photoelectrochemical performance

    Science.gov (United States)

    Zhang, Yaping; Zhu, Haifeng; Yu, Lianqing; He, Jiandong; Huang, Chengxing

    2018-04-01

    TiO2 nanotube arrays (TNTs) are first prepared by anodization Ti foils in ethylene glycol electrolyte. Then, MoSe2 deposites electrochemically on TNTs. The as-synthesized MoSe2/TiO2 composite has a much higher photocurrent density of 1.07 mA cm‑2 at 0 V than pure TNTs of 0.38 mA cm‑2, which suggests that the MoSe2/TiO2 composite film has optimum photoelectrocatalysis properties. The electron transport resistances of the MoSe2/TiO2 decreases to half of pure TiO2, at 295.6 ohm/cm2. Both photocurrent-time and Mott-Schottky plots indicate MoSe2 a p-type semiconductor characteristics. MoSe2/TiO2 composite can achieve a maximum 5 orders of magnitude enhancement in carrier density (4.650 × 1027 cm‑3) than that of pure TiO2 arrays. It can be attributed to p-n heterojunction formed between MoSe2 and TiO2, and the composite can be potentially applied in photoelectrochemical, photocatalysis fields.

  1. Azo dyes decomposition on new nitrogen-modified anatase TiO2 with high adsorptivity

    International Nuclear Information System (INIS)

    Janus, M.; Choina, J.; Morawski, A.W.

    2009-01-01

    New vis active photocatalyst was obtained by the modification of commercial anatase TiO 2 (Police, Poland) in pressure reactor in an ammonia water atmosphere at 100 o C for 4 h. The photocatalytic activity of new material was tested during three azo dyes decomposition: monoazo (Reactive Read), diazo (Reactive Black) and poliazodye (Direct Green). Obtained photocatalyst had new bands at 1430-1440 cm -1 attributed to the bending vibrations of NH 4 + and at 1535 cm -1 associated with NH 2 groups or NO 2 and NO. UV-vis/DR spectra of photocatalyst had also insignificant decrease in visible region. Fluorescence technique was used for studying the amount of hydroxyl radicals produced on TiO 2 surface during visible light irradiation. The hydroxyl radicals produced react with coumarin present in the solution to form 7-hydroxycoumarin which has fluorescent capacity. Photocatalytic activity of modified TiO 2 was compared with commercial titanium dioxide P25 (Degussa, Germany). The photocatalytic activity of TiO 2 /N was higher than that of unmodified material and P25 under visible light irradiation. The ability for dye adsorption (Reactive Red) on photocatalyst surface was also tested. Unmodified TiO 2 and P25 has isotherm of adsorption by Freundlich model, and nitrogen-modified TiO 2 by Langmuir model. The presence of nitrogen at the surface of TiO 2 significantly increased adsorption capacity of TiO 2 as well as OH· radicals formation under visible radiation.

  2. Y-doping TiO2 nanorod arrays for efficient perovskite solar cells

    Science.gov (United States)

    Deng, Xinlian; Wang, Yanqing; Cui, Zhendong; Li, Long; Shi, Chengwu

    2018-05-01

    To improve the electron transportation in TiO2 nanorod arrays and charge separation in the interface of TiO2/perovskite, Y-doping TiO2 nanorod arrays with the length of 200 nm, diameter of 11 nm and areal density of 1050 μm-2 were successfully prepared by the hydrothermal method and the influence of Y/Ti molar ratios of 0%, 3%, 5% in the hydrothermal grown solutions on the growth of TiO2 nanorod arrays was investigated. The results revealed that the appropriate Y/Ti molar ratios can increase the areal density of the corresponding TiO2 nanorod arrays and improve the charge separation in the interface of the TiO2/perovskite. The Y-doping TiO2 nanorod array perovskite solar cells with the Y/Ti molar ratio of 3% exhibited a photoelectric conversion efficiency (PCE) of 18.11% along with an open-circuit voltage (Voc) of 1.06 V, short-circuit photocurrent density (Jsc) of 22.50 mA cm-2 and fill factor (FF) of 76.16%, while the un-doping TiO2 nanorod array perovskite solar cells gave a PCE of 16.42% along with Voc of 1.04 V, Jsc of 21.66 mA cm-2 and FF of 72.97%.

  3. Zirconium phosphate containing membranes for the methanol fuel cell; Zirkoniumphosphathaltige Membranen fuer die Methanol-Brennstoffzelle

    Energy Technology Data Exchange (ETDEWEB)

    Dugaro, M.

    2004-07-01

    Successful applications of the direct methanol fuel cell depend on the development of suitable membranes for separating gas spaces. Suitable polymers must be found as membrane matrix materials. The polymermatrix must be modified for achieving optimum pervaporation characteristics and sufficient conductivity. Doping with colloidal particles with good proton conductivity is an interesting option. Protonated zirconium phosphate was selected because of its high proton conductivity and was doped additionally with bivalent, trivalent and tetravalent ions. The electrokinetic mobility, surface charge density, particle size and particle size distribution were measured as well as the swelling characteristics. Dispersions prepared in aqueous solvents did not yield useful membranes. Better results, and even quite good results in some cases, were achieved with water-free dispersions in DMF. Initially, zirconium hydrogen phosphates were modified with Ti4+ and Ti3+. Y3+ doped membranes were not sufficiently stable, so that bleaching chloride was used. Results were better with this modification, so that a combination of lead and titanium doping (Ti4+, Ti3+) was tried. No further improvement was possible. The best results were obtained with combinations of lead and aerosil. [German] Ein erfolgreicher Einsatz der Direkt-Methanol-Brennstoffzelle ist an die Entwicklung geeigneter Membranen gebunden, die die Gasraeume voneinander trennen. Ohne geeignete Membranen ist ein dauerhafter Einsatz unmoeglich. Probleme bereitet einmal die Auswahl geeigneter Polymere als Matrix der Membran. Um das richtige Pervaporationsverhalten und eine ausreichende Leitfaehigkeit zu erhalten, muss die Polymermatrix modifiziert werden. Eine der aussichtsreichen Moeglichkeiten ist der Einbau kolloidaler Teilchen, die eine Protonenleitfaehigkeit aufweisen. Ausgewaehlt wurde Zirkoniumphosphat in der protonierten Form, da diese Schichtverbindung eine beachtliche Protonenleitfaehigkeit besitzt. Um die

  4. Optical Properties and Photoactivity of The Pigmentary TiO2 Doped with P2O5, K2O, Al2O3 and Sb2O3

    International Nuclear Information System (INIS)

    Glen, M; Grzmil, B

    2011-01-01

    The influence of the increasing content of antimony calculated to Sb 2 O 3 (0.08-0.57 mol%) with the constant amount of the other additives (calculated to P 2 O 5 , K 2 O, Al 2 O 3 ) on the optical properties and photostability of doped rutile has been investigated. The properties of the obtained TiO 2 -PKAlSb samples were compared to the commercial TiO 2 -PKAl composition. The starting material was the concentrated suspension of technical-grade hydrated titanium dioxide (HTD). The dopant agents' solutions were introduced to HTD. Prepared samples were calcined with gradually increasing process temperature. The XRD analysis was used to determine the rutile content in the TiO 2 samples. Optical properties of modified titanium dioxide have been determined spectrophotometrically by measuring the colour in the white (brightness, white tone) and grey system (relative lightening power, grey tone). Photostability was characterized by the white lead-glycerin test with UV-Vis light. It was observed that with the increasing content of antimony in rutile TiO 2 , doped with phosphates, potassium and aluminium, the brightness and grey tone were increasing but white tone decreased. The changes of the relative lightening power values were insignificant. Comparing the samples of TiO 2 -PKAlSb with the TiO 2 -PKAl composition it was observed that titanium dioxide doped with antimony had better white and grey tone. The increasing Sb 2 O 3 content in the TiO 2 caused the improvement of the photostability.

  5. Improvement of light harvesting and device performance of dye-sensitized solar cells using rod-like nanocrystal TiO2 overlay coating on TiO2 nanoparticle working electrode

    International Nuclear Information System (INIS)

    Liu, Xueyang; Fang, Jian; Gao, Mei; Wang, Hongxia; Yang, Weidong; Lin, Tong

    2015-01-01

    Novel TiO 2 single crystalline nanorods were synthesized by electrospinning and hydrothermal treatment. The role of the TiO 2 nanorods on TiO 2 nanoparticle electrode in improvement of light harvesting and photovoltaic properties of dye-sensitized solar cells (DSSCs) was examined. Although the TiO 2 nanorods had lower dye loading than TiO 2 nanoparticle, they showed higher light utilization behaviour. Electron transfer in TiO 2 nanorods received less resistance than that in TiO 2 nanoparticle aggregation. By just applying a thin layer of TiO 2 nanorods on TiO 2 nanoparticle working electrode, the DSSC device light harvesting ability and energy conversion efficiency were improved significantly. The thickness of the nanorod layer in the working electrode played an important role in determining the photovoltaic property of DSSCs. An energy conversion efficiency as high as 6.6% was found on a DSSC device with the working electrode consisting of a 12 μm think TiO 2 nanoparticle layer covered with 3 μm thick TiO 2 nanorods. The results obtained from this study may benefit further design of highly efficient DSSCs. - Highlights: • Single crystalline TiO 2 nanorods were prepared for DSSC application. • TiO 2 nanorods show effective light scattering performance. • TiO 2 nanorods have higher electron transfer efficiency than TiO 2 nanoparticles. • TiO 2 nanorods on TiO 2 nanoparticle electrode improve DSSC efficiency

  6. First-Principles Modeling of Polaron Formation in TiO2 Polymorphs.

    Science.gov (United States)

    Elmaslmane, A R; Watkins, M B; McKenna, K P

    2018-06-21

    We present a computationally efficient and predictive methodology for modeling the formation and properties of electron and hole polarons in solids. Through a nonempirical and self-consistent optimization of the fraction of Hartree-Fock exchange (α) in a hybrid functional, we ensure the generalized Koopmans' condition is satisfied and self-interaction error is minimized. The approach is applied to model polaron formation in known stable and metastable phases of TiO 2 including anatase, rutile, brookite, TiO 2 (H), TiO 2 (R), and TiO 2 (B). Electron polarons are predicted to form in rutile, TiO 2 (H), and TiO 2 (R) (with trapping energies ranging from -0.02 eV to -0.35 eV). In rutile the electron localizes on a single Ti ion, whereas in TiO 2 (H) and TiO 2 (R) the electron is distributed across two neighboring Ti sites. Hole polarons are predicted to form in anatase, brookite, TiO 2 (H), TiO 2 (R), and TiO 2 (B) (with trapping energies ranging from -0.16 eV to -0.52 eV). In anatase, brookite, and TiO 2 (B) holes localize on a single O ion, whereas in TiO 2 (H) and TiO 2 (R) holes can also be distributed across two O sites. We find that the optimized α has a degree of transferability across the phases, with α = 0.115 describing all phases well. We also note the approach yields accurate band gaps, with anatase, rutile, and brookite within six percent of experimental values. We conclude our study with a comparison of the alignment of polaron charge transition levels across the different phases. Since the approach we describe is only two to three times more expensive than a standard density functional theory calculation, it is ideally suited to model charge trapping at complex defects (such as surfaces and interfaces) in a range of materials relevant for technological applications but previously inaccessible to predictive modeling.

  7. Positively charged TiO2 particles in non-polar system for electrophoretic display

    International Nuclear Information System (INIS)

    Chang, Young Seon

    2005-02-01

    Electrophoretic display uses a technique called electrophoresis to represent images and letters electronically with electronic ink. Although it has good characteristics such as wide viewing angle, high contrast ratio and extremely low power consumption, there are still several issues to be resolved to improve its performances. Higher mobility and stability of the ink particles are the most important issues among them. In this study, TiO 2 particles coated with acrylamide were found to be effective ink particles that satisfy higher mobility and stability. The TiO 2 particles coated with 5∼40% acrylamide were prepared by dispersion polymerization using monomers of methyl methacrylate (MMA) and acrylamide. The TiO 2 particles coated with acrylamide were dispersed in isopar-G with sorbitan esters such as span 20, span 80 and span 85. The size of the TiO 2 particles were changed from 200±150 nm to 350∼500 nm by the coating process. The morphology of coated particles was observed using a transmission electron microscope (TEM) and thermogravimetric analysis (TGA). From the TGA results, the weight fraction of TiO 2 and polymer in coated particle were calculated. From the zeta potential measurement, it was shown that as acrylamide concentration was increased from 5% to 30%, zeta potential of the coated TiO 2 particles was increased from 50mV to about 230mV. The zeta potential of the coated TiO 2 particles with 40% acrylamide was decreased to 50mV. As a stabilizer, span 85 was the most effective surfactant to improve stability of the TiO 2 particles coated with acrylamide among used surfactants in this study. Span 85 showed best stability in the storage test with TiO 2 particles coated with 10% acrylamide. The mobility of TiO 2 particles coated with acrylamide with span 85 in dye solution (Oil Blue-N dissolved in isopar-G) were measured by ITO cell test. The mobility of TiO 2 particles coated with 10∼30% acrylamide was over 600μm 2 /Vs while the mobility of TiO 2 particles coated with 40% acrylamide was about 400μm 2 /Vs. Span 85 was effective to improve the mobility of TiO 2 particles coated with acrylamide. As the concentration of span 85 was increased from 0 to 1.75 vol %, mobility of the TiO 2 particles coated with 20% acrylamide was increased from 250μm 2 /Vs to about 720μ 2 /Vs

  8. Synergistic effects for the TiO2/RuO2/Pt photodissociation of water

    Energy Technology Data Exchange (ETDEWEB)

    Blondel, G; Harriman, A; Williams, D

    1983-07-01

    Compressed discs of naked TiO2 or TiO2 coated with a thin film of a noble metal (e.g. Pt) do not photodissociate water upon illumination with UV light, but small amounts of H2 are generated if the TiO2 has been reduced in a stream of H2 at 600 C. Discs prepared from mixtures of TiO2/RuO2 facilitate the UV photodissociation of water into H2 and O2 although the yields are very low. When a thin (about 9 nm) film of Pt is applied to the TiO2/RuO2 discs, the yields of H2 and O2 observed upon irradiation with UV light are improved drastically. 25 references.

  9. Synthesis and Photocatalytic Activity of Anatase TiO2 Nanoparticles-coated Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Xie Yi

    2009-01-01

    Full Text Available Abstract A simple and straightforward approach to prepare TiO2-coated carbon nanotubes (CNTs is presented. Anatase TiO2 nanoparticles (NPs with the average size ~8 nm were coated on CNTs from peroxo titanic acid (PTA precursor even at low temperature of 100 °C. We demonstrate the effects of CNTs/TiO2 molar ratio on the adsorption capability and photocatalytic efficiency under UV–visible irradiation. The samples showed not only good optical absorption in visible range, but also great adsorption capacity for methyl orange (MO dye molecules. These properties facilitated the great enhancement of photocatalytic activity of TiO2 NPs-coated CNTs photocatalysts. The TiO2 NPs-coated CNTs exhibited 2.45 times higher photocatalytic activity for MO degradation than that of pure TiO2.

  10. Enhanced photoelectrochemical properties of TiO2 nanorod arrays decorated with CdS nanoparticles

    International Nuclear Information System (INIS)

    Xie, Zheng; Wang, Weipeng; Liu, Can; Li, Zhengcao; Liu, Xiangxuan; Zhang, Zhengjun

    2014-01-01

    TiO 2 nanorod arrays (TiO 2 NRAs) sensitized with CdS nanoparticles were fabricated via successive ion layer adsorption and reaction (SILAR), and TiO 2 NRAs were obtained by oxidizing Ti NRAs obtained through oblique angle deposition. The TiO 2 NRAs decorated with CdS nanoparticles exhibited excellent photoelectrochemical and photocatalytic properties under visible light, and the one decorated with 20 SILAR cycles CdS nanoparticles shows the best performance. This can be attributed to the enhanced separation of electrons and holes by forming heterojunctions of CdS nanoparticles and TiO 2 NRAs. This provides a promising way to fabricate the material for solar energy conversion and wastewater degradation. (paper)

  11. Preparation and performance of photocatalytic TiO2 immobilized on palladium-doped carbon fibers

    International Nuclear Information System (INIS)

    Zhu Yaofeng; Fu Yaqin; Ni Qingqing

    2011-01-01

    Pd-modified carbon fibers (CFs) are obtained by a facile oxidation-reduction method and then dip-coated in a sol-gel of titanium dioxide (TiO 2 ) to form supported TiO 2 /Pd-CF photocatalysts. The morphology of the Pd-modified CFs and the amount Pd deposited are characterized by field emission scanning electron microscopy and atomic absorption spectrometry, respectively. X-ray diffraction is used to investigate the crystal structures of the TiO 2 photocatalyst. Acid orange II is used as a model contaminant to evaluate the photocatalytic properties of the photocatalyst under UV irradiation. TiO 2 /Pd-CF exhibits higher catalytic activity than TiO 2 /CF towards the degradation of acid orange II. Optimum photocatalytic performance and support properties are achieved when the Pd particle loading is about 10.8 mg/g.

  12. Effects of highly ordered TiO2 nanotube substrates on the nucleation of Cu electrodeposits.

    Science.gov (United States)

    Ryu, Won Hee; Park, Chan Jin; Kwon, Hyuk Sang

    2010-05-01

    We investigated the effects of TiO2 nanotube substrates on the nucleation density of Cu during electrodeposition in a solution of CuSO4 and H2SO4 at 50 degrees C compared with those of pure Ti and micro-porous TiO2 substrates. During electrodeposition, the density of Cu nuclei on the TiO2 nanotube substrate increased and the average size of Cu nuclei decreased with increasing anodizing voltage and time for the synthesis of the substrate. In addition, the nucleation density of Cu electrodeposits on the highly ordered TiO2 nanotube substrate was much higher than that on pure Ti and micro-porous TiO2 substrates.

  13. Preparation of anatase TiO2 thin films by vacuum arc plasma evaporation

    International Nuclear Information System (INIS)

    Miyata, Toshihiro; Tsukada, Satoshi; Minami, Tadatsugu

    2006-01-01

    Anatase titanium dioxide (TiO 2 ) thin films with high photocatalytic activity have been prepared with deposition rates as high as 16 nm/min by a newly developed vacuum arc plasma evaporation (VAPE) method using sintered TiO 2 pellets as the source material. Highly transparent TiO 2 thin films prepared at substrate temperatures from room temperature to 400 deg. C exhibited photocatalytic activity, regardless whether oxygen (O 2 ) gas was introduced during the VAPE deposition. The highest photocatalytic activity and photo-induced hydrophilicity were obtained in anatase TiO 2 thin films prepared at 300 deg. C, which correlated to the best crystallinity of the films, as evidenced from X-ray diffraction. In addition, a transparent and conductive anatase TiO 2 thin film with a resistivity of 2.6 x 10 -1 Ω cm was prepared at a substrate temperature of 400 deg. C without the introduction of O 2 gas

  14. Three-dimensional observation of TiO2 nanostructures by electron tomography

    KAUST Repository

    Suh, Young Joon

    2013-03-01

    Three-dimensional nanostructures of TiO2 related materials including nanotubes, electron acceptor materials in hybrid polymer solar cells, and working electrodes of dye sensitized solar cells (DSSCs) were visualized by electron tomography as well as TEM micrographs. The regions on the wall of TiO2 nanotubes where the streptavidins were attached were elucidated by electron tomogram analysis. The coverage of TiO2 nanotubes by streptavidin was also investigated. The TiO2 nanostructures in hybrid polymer solar cells made by sol-gel and atomic layer deposition (ALD) methods and the morphologies of pores between TiO2 particles in DSSCs were also observed by reconstructed three-dimensional images made by electron tomography. © 2012 Elsevier Ltd.

  15. Antimicrobial and Barrier Properties of Bovine Gelatin Films Reinforced by Nano TiO2

    Directory of Open Access Journals (Sweden)

    R. Nassiri

    2013-11-01

    Full Text Available The effects of nano titanium dioxide incorporation were investigated on the water vaporpermeability, oxygen permeability, and antimicrobial properties of bovine gelatin films. The nano TiO2 (TiO2-N was homogenized by sonication and incorporated into bovine gelatin solutions at different concentrations(e.g. 1, 2, 3, and 5% w/w of dried gelatin. The permeability of the films to water vapor and oxygen wassignificantly decreased by incorporating of low concentration TiO2-N to gelatin solutions. TiO2-N gelatin filmsshowed an excellent antimicrobial activity against Staphylococcus aureus and Escherichia coli. Theseproperties suggest that TiO2-N has the potential as filler in gelatin-based films for using as an active packagingmaterials in pharmaceutical and food packaging industries.

  16. Optimized monolayer grafting of 3-aminopropyltriethoxysilane onto amorphous, anatase and rutile TiO 2

    Science.gov (United States)

    Song, Yan-Yan; Hildebrand, Helga; Schmuki, Patrik

    2010-02-01

    Experimental conditions were studied for optimized attachment of 3-aminopropyltriethoxysilane (APTES) onto amorphous, anatase and rutile titanium dioxide (TiO 2) surfaces. The attachment process and extent was characterized using X-ray photoelectron spectroscopy (XPS). In particular, the effect of attachment time, silane concentration, reaction temperature and the TiO 2 crystalline structure on the growth kinetics of the silane layers was studied. The measurements reveal that typically monolayers are more dense on amorphous than on crystalline TiO 2. The results show that critical experimental conditions exist where APTES attachment to the TiO 2 surface changes from a monolayer to a multilayer growth mode. The obtained results and parameters to produce optimized APTES layers are of a high practical relevance as APTES attachment often constitutes the initial step for organic modification of TiO 2 surface with biorelevant molecules such as proteins, enzymes or growth factors.

  17. One-Dimensional TiO2 Nanostructures as Photoanodes for Dye-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Jie Qu

    2013-01-01

    Full Text Available Titanium dioxide (TiO2 is star materials due to its remarkable optical and electronic properties, resulting in various applications, especially in the fields of dye-sensitized solar cells (DSSCs. Photoanode is the most important part of the DSSCs, which help to adsorb dye molecules and transport the injected electrons. The size, structure, and morphology of TiO2 photoanode have been found to show significant influence on the photovoltaic performance of DSSCs. In this paper, we briefly summarize the synthesis and properties of one-dimensional (1D TiO2 nanomaterials (bare 1D TiO2 nanomaterial and 1D hierarchical TiO2 and their photovoltaic performance in DSSCs.

  18. Excess electrons in reduced rutile and anatase TiO2

    Science.gov (United States)

    Yin, Wen-Jin; Wen, Bo; Zhou, Chuanyao; Selloni, Annabella; Liu, Li-Min

    2018-05-01

    As a prototypical photocatalyst, TiO2 is a material of scientific and technological interest. In photocatalysis and other applications, TiO2 is often reduced, behaving as an n-type semiconductor with unique physico-chemical properties. In this review, we summarize recent advances in the understanding of the fundamental properties and applications of excess electrons in reduced, undoped TiO2. We discuss the characteristics of excess electrons in the bulk and at the surface of rutile and anatase TiO2 focusing on their localization, spatial distribution, energy levels, and dynamical properties. We examine specific features of the electronic states for photoexcited TiO2, for intrinsic oxygen vacancy and Ti interstitial defects, and for surface hydroxyls. We discuss similarities and differences in the behaviors of excess electrons in the rutile and anatase phases. Finally, we consider the effect of excess electrons on the reactivity, focusing on the interaction between excess electrons and adsorbates.

  19. Photodegradation of phenol by N-Doped TiO2 anatase/rutile nanorods assembled microsphere under UV and visible light irradiation

    International Nuclear Information System (INIS)

    Mohamed, Mohamad Azuwa; Salleh, W.N.W.; Jaafar, Juhana; Ismail, A.F.; Nor, Nor Azureen Mohamad

    2015-01-01

    N-doped TiO 2 anatase/rutile nanorods assembled microspheres were successfully synthesized via a simple and direct sol–gel method containing titanium-n-butoxide Ti(OBu) 4 as a precursor material, nitric acid as a catalyst, and isopropanol as a solvent. By manipulating calcination temperature, the photocatalyst consisting of different phase compositions of anatase and rutile was obtained. The prepared TiO 2 nanoparticles were characterized by means of x-ray diffraction (XRD), field emission scanning microscope (FESEM), atomic force microscopy (AFM), Brunauer–Emmett–Teller (BET) analysis, UV–Vis–NIR spectroscopy, and fourier transform infrared (FTIR). The results from UV–Vis–NIR spectroscopy and FTIR revealed the direct incorporation of nitrogen in TiO 2 lattice since visible absorption capability was observed at 400–600 nm. XPS study indicated the incorporation of nitrogen as dopant in TiO 2 at binding energies of 396.8, 397.5, 398.7, 399.8, and 401 eV. Calcination temperature was observed to have a great influence on the photocatalytic activity of the TiO 2 nanorods. The photocatalytic activity of the prepared mixed phase of anatase/rutile TiO 2 nanoparticles was measured by photodegradation phenol in an aqueous solution under UV and visible irradiations. N-doped TiO 2 anatase/rutile nanorods assembled microsphere (consists of 38.3% anatase and 61.7% rutile) that was prepared at 400 °C exhibited the highest photocatalytic activity after irradiated under visible and UV light for 540 min. The high performance of photocatalyst materials could be obtained by adopting a judicious combination of anatase/rutile prepared at optimum calcination conditions. - Highlights: • Synthesis of N-Doped TiO 2 Anatase/Rutile Nanorods via simple preparation method. • Direct incorporation of HNO 3 as the nitrogen dopant source. • The photocatalytic properties were studied upon UV and visible light irradiation. • The optimum calcination temperature is 400 °C for

  20. Phosphate Salts

    Science.gov (United States)

    ... body. They are involved in cell structure, energy transport and storage, vitamin function, and numerous other processes ... Phosphate-containing foods and beverages include cola, wine, beer, whole grain cereals, nuts, dairy products and some ...

  1. ADSORCIÓN DE ALDEHÍDOS INSATURADOS SOBRE TiO2

    Directory of Open Access Journals (Sweden)

    Natalia Ortega

    2012-01-01

    Full Text Available En el presente trabajo se estudió la adsorción de aldehídos insaturados sobre la superficie del TiO2. Para evaluar su eficiencia como catalizador, se realizaron experimentos de fotocatálisis heterogénea de p-nitrofenol (PNF y una muestra proveniente de efluentes industriales. Se empleó un simulador solar y cuatro sistemas de TiO2: el TiO2-sólo (sin modificar y los sistemas TiO2-dienal constituidos por la adsorción química de 2,4 hexadienal, 2,4 heptadienal y el trans-cinamaldehído sobre la superficie del TiO2. La adsorción de los aldehídos insaturados sobre el TiO2 se cuantificó empleando los modelos de adsorción de Langmuir y Freundlich. Se evaluó la influencia del pH en los sistemas TiO2-dienal y su efecto en la degradación fotocatalítica del PNF. En condiciones básicas, la constante de velocidad del PNF es mayor al emplear los sistemas TiO2-dienal en comparación con el TiO2-sólo, mientras que en condiciones ácidas se encontró la tendencia opuesta. El sistema TiO2-cina resultó ser el fotocatalizador de mayor eficiencia.

  2. Synthesis and photocatalytic activity of graphene based doped TiO2 nanocomposites

    International Nuclear Information System (INIS)

    Gu, Yongji; Xing, Mingyang; Zhang, Jinlong

    2014-01-01

    Graphical abstract: - Highlights: • Graphene based doped TiO 2 nanocomposites were prepared. • The intimate contact between doped TiO 2 and graphene is achieved simultaneously. • These nanocomposites showed higher photocatalytic activity than TiO 2 and doped TiO 2 . • Photocatalytic mechanism was explained thoroughly. - Abstract: The nanocomposites of reduced graphene oxide based nitrogen doped TiO 2 (N–TiO 2 –RGO) and reduced graphene oxide based nitrogen and vanadium co-doped TiO 2 (N, V–TiO 2 –RGO) were prepared via a facile hydrothermal reaction of graphene oxide and TiO 2 in a water solvent. In this hydrothermal treatment, the reduction of graphene oxide and the intimate contact between nitrogen doped TiO 2 (N–TiO 2 ) or nitrogen and vanadium co-doped TiO 2 (N,V–TiO 2 ) and the RGO sheet is achieved simultaneously. Both N–TiO 2 –RGO and N,V–TiO 2 –RGO nanocomposites exhibit much higher visible light photocatalytic activity than N–TiO 2 and N,V–TiO 2 , and the order of visible light photocatalytic activity is N,V–TiO 2 –RGO > N–TiO 2 –RGO > N,V–TiO 2 > N–TiO 2 > TiO 2 . According to the characterization, the enhanced photocatalytic activity of the nanocomposites is attributed to reasons, such as enhancement of adsorption of pollutants, light absorption intensity, minimizing the recombination of photoinduced electrons and holes and more excited states of these nanocomposites under visible light irradiation. Overall, this work provides a more marked contrast of graphene based semiconductor nanocomposites and a more comprehensive explanation of the mechanism

  3. Recovery TiO2 by leaching process of carbothermic reduced Kalimantan ilmenite

    Science.gov (United States)

    Wahyuningsih, S.; Sari, P. P.; Ramelan, A. H.

    2018-05-01

    Ilmenite naturally occurred in iron titanate (FeTiO3) minerals. The separation of natural ilmenite into TiO2 and Fe2O3 need to be explored to gain the high purity separation product. A new combination method named of carbothermic reduction, acidic-leaching and complexation by EDTA were proposed for separation TiO2 from Ilmenite. Roasting of ilmenite was carried out at 950 °C for 1 h by the addition of activated carbon with mass ratio of ilmenite : activated carbon =4:3. The carbothermic reduction was carried out to yield a high separation of initial content of ilmenite that will be easily to dissolve within hydrochloric acid solution in leaching process. The composition of ilmenite observed by X-Ray Fluoresences (XRF) changed after the carbothermic reduction process and the dominant content is TiO2 (57.56%). X-Ray Diffraction (XRD) of roasted ilmenite composed of decomposed product of ilmenite i.e. hematite (Fe2O3), TiO2 anatase, TiO2 rutile, and inorganic salt. The leaching of the roasted ilmenite has been done by sulphuric acid solution (6 M) to gain the titanyl sulphate solution. Separation of iron impurities of TiO2 gel from titanyl sulphate (TiOSO4) solution was conducted by complexation method using EDTA as a complexation agent. The characteristic of TiO2 obtained using XRD showed that TiO2 is anatase type and the percentage of TiO2 using XRF showed that TiO2 content of 86,03%.

  4. Characterization and improved solar light activity of vanadium doped TiO2/diatomite hybrid catalysts

    International Nuclear Information System (INIS)

    Wang, Bin; Zhang, Guangxin; Leng, Xue; Sun, Zhiming; Zheng, Shuilin

    2015-01-01

    Highlights: • V-doped TiO 2 /diatomite composite photocatalyst was synthesized. • The physiochemical property and solar light photoactivity were characterized. • The presence and influence of V ions in TiO 2 matrix was systematically analyzed. • The photocatalysis for Rhodamine B were studied under solar light illumination. - Abstract: V-doped TiO 2 /diatomite composite photocatalysts with different vanadium concentrations were synthesized by a modified sol–gel method. The diatomite was responsible for the well dispersion of TiO 2 nanoparticles on the matrix and consequently inhibited the agglomeration. V-TiO 2 /diatomite hybrids showed red shift in TiO 2 absorption edge with enhanced absorption intensity. Most importantly, the dopant energy levels were formed in the TiO 2 bandgap due to V 4+ ions substituted to Ti 4+ sites. The 0.5% V-TiO 2 /diatomite photocatalyst displayed narrower bandgap (2.95 eV) compared to undoped sample (3.13 eV) and other doped samples (3.05 eV) with higher doping concentration. The photocatalytic activities of V doped TiO 2 /diatomite samples for the degradation of Rhodamine B under stimulated solar light illumination were significantly improved compared with the undoped sample. In our case, V 4+ ions incorporated in TiO 2 lattice were responsible for increased visible-light absorption and electron transfer to oxygen molecules adsorbed on the surface of TiO 2 to produce superoxide radicals ·O 2 – , while V 5+ species presented on the surface of TiO 2 particles in the form of V 2 O 5 contributed to e – –h + separation. In addition, due to the combination of diatomite as support, this hybrid photocatalyst could be separated from solution quickly by natural settlement and exhibited good reusability

  5. Efficient photodecomposition of herbicide imazapyr over mesoporous Ga2O3-TiO2 nanocomposites.

    Science.gov (United States)

    Ismail, Adel A; Abdelfattah, Ibrahim; Faisal, M; Helal, Ahmed

    2018-01-15

    The unabated release of herbicide imazapyr into the soil and groundwater led to crop destruction and several pollution-related concerns. In this contribution, heterogeneous photocatalytic technique was employed utilizing mesoporous Ga 2 O 3 -TiO 2 nanocomposites for degrading imazapyr herbicide as a model pollutant molecule. Mesoporous Ga 2 O 3 -TiO 2 nanocomposites with varied Ga 2 O 3 contents (0-5wt%) were synthesized through sol-gel process. XRD and Raman spectra exhibited extremely crystalline anatase TiO 2 phase at low Ga 2 O 3 content which gradually reduced with the increase of Ga 2 O 3 content. TEM images display uniform TiO 2 particles (10±2nm) with mesoporous structure. The mesoporous TiO 2 exhibits large surface areas of 167m 2 g -1 , diminished to 108m 2 g -1 upon 5% Ga 2 O 3 incorporation, with tunable mesopore diameter in the range of 3-9nm. The photocatalytic efficiency of synthesized Ga 2 O 3 -TiO 2 nanocomposites was assessed by degrading imazapyr herbicide and comparing with commercial photocatalyst UV-100 and mesoporous Ga 2 O 3 under UV illumination. 0.1% Ga 2 O 3 -TiO 2 nanocomposite is considered the optimum photocatalyst, which degrades 98% of imazapyr herbicide within 180min. Also, the photodegradation rate of imazapyr using 0.1% Ga 2 O 3 -TiO 2 nanocomposite is nearly 10 and 3-fold higher than that of mesoporous Ga 2 O 3 and UV-100, respectively. The high photonic efficiency and long-term stability of the mesoporous Ga 2 O 3 -TiO 2 nanocomposites are ascribed to its stronger oxidative capability in comparison with either mesoporous TiO 2 , Ga 2 O 3 or commercial UV-100. Copyright © 2017 Elsevier B.V. All rights reserved.

  6. The novel silicon-containing epoxy/PEPA phosphate flame retardant for transparent intumescent fire resistant coating

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Yanchao [School of Materials Science and Engineering, Tongji University, 4800 Cao' an Road, Shanghai 201804 (China); Wang, Guojian, E-mail: wanggj@tongji.edu.cn [School of Materials Science and Engineering, Tongji University, 4800 Cao' an Road, Shanghai 201804 (China); Key Laboratory of Advanced Civil Engineering Materials, Ministry of Education, 4800 Cao' an Road, Shanghai 201804 (China)

    2016-11-01

    Highlights: • The novel halogen-free flame retardant containing silicon and caged bicyclic phosphate was synthesized. • A novel transparent intumescent fire resistant coating was developed by the P-Si synergistic flame retardant and melamine formaldehyde resin. • Excellent fire protection of the transparent intumescent fire resistant coating. • The P-Si synergistic flame retardant could improve the thermo-oxidation resistance of transparent fire resistant coating. - Abstract: A series of novel silicon-containing epoxy/PEPA phosphate flame retardants (EPPSi) were synthesized by polyphosphoric acid (PPA), caged bicyclic phosphate 1-oxo-4-hydroxymethyl-2,6,7-trioxa-L-phosphabicyclo [2.2.2] octane (PEPA), and different ratios of silicon-containing epoxy 1,1,3,3-tetramethyl-1,3-bis(3-(oxiran-2-ylmethoxy)propyl)disiloxane (TMSEP) to 1,4-butanediol diglycidyl ether (BDE). The chemical structure of EPPSi was confirmed by Fourier transform infrared spectroscopy (FTIR) and {sup 1}H nuclear magnetic resonance spectroscopy ({sup 1}H NMR). Afterwards, the transparent intumescent fire resistant coatings were prepared by mixing EPPSi and melamine formaldehyde resin. The influence of silicon on the fire protection of coatings was intensively investigated by fire protection test, intumescence ratio, scanning electron microscope (SEM), compressive strength test, X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA) and real-time FTIR. It was found that the fire resistant coatings obtained the best fire protection when the ratio of TMESP/BDE was 20/100, while excessive TMSEP made the fire protection of coatings deceased sharply. The intumescence ratio, compressive strength test and SEM result showed that a synergistic effect existed between phosphorus and silicon, which improved the foam structure and compressive strength of the char layer significantly. XPS result proved the out-migration effect of silicon. The high concentration silicon on surface played

  7. Characterization of the Micro-Arc Coatings Containing β-Tricalcium Phosphate Particles on Mg-0.8Ca Alloy

    Directory of Open Access Journals (Sweden)

    Mariya B. Sedelnikova

    2018-04-01

    Full Text Available The characterization of the microstructure, morphology, topography, composition, and physical and chemical properties of the coatings containing β-tricalcium phosphate (β-TCP particles deposited by the micro-arc oxidation (MAO method on biodegradable Mg-0.8Ca alloy has been performed. The electrolyte for the MAO process included the following components: Na2HPO4·12H2O, NaOH, NaF, and β-Ca3(PO42 (β-TCP. The coating morphology, microstructure, and compositions have been studied using scanning electron microscopy (SEM, transmission electron microscopy (TEM, energy-dispersive X-ray spectroscopy (EDX, and X-ray diffraction (XRD. With increasing of the MAO voltage from 350 to 500 V, the coating thickness and surface average roughness of the coatings increased linearly from 6 to 150 µm and from 2 to 8 µm, respectively. The coating deposited at 350 V had more homogeneous porous morphology with numerous pores similar by sizes (2–3 µm than the coatings formed at 450–500 V. The β-TCP isometric particles were included in the coating surface. The XRD recognized the amorphous-crystalline structure in the coatings with incorporation of the following phases: β-TCP, α-TCP, MgO (periclase and hydroxyapatite (HA. The corrosion experiments showed that the biodegradation rate of the Mg-0.8Ca alloy coated by calcium phosphates is almost 10 times less than that of uncoated alloy.

  8. Thermal properties and surface reactivity in simulated body fluid of new strontium ion-containing phosphate glasses.

    Science.gov (United States)

    Massera, J; Petit, L; Cardinal, T; Videau, J J; Hupa, M; Hupa, L

    2013-06-01

    In this paper, we investigate the effect of SrO substitution for CaO in 50P₂O₅-10Na₂-(40-x)CaO-xSrO glass system (x from 0 to 40) on the thermal and structural properties and also on the glass reactivity in simulated body fluid (SBF) in order to find new glass candidates for biomedical glass fibers. The addition of SrO at the expense of CaO seems to restrain the leaching of phosphate ions in the solution limiting the reduction of the solution pH. We observed the formation of an apatite layer at the surface of the glasses when in contact with SBF. SrO and MgO were found in the apatite layer of the strontium ion-containing glasses, the concentration of which increases with an increase of SrO content. We think that it is the presence of MgO and SrO in the layer which limits the leaching of phosphate in the solution and thus the glass dissolution in SBF.

  9. Cytotoxicity of TiO2 nanoparticles and their detoxification in a freshwater system

    International Nuclear Information System (INIS)

    Dalai, Swayamprava; Pakrashi, Sunandan; Joyce Nirmala, M.; Chaudhri, Apoorvi; Chandrasekaran, N.; Mandal, A.B.; Mukherjee, Amitava

    2013-01-01

    Highlights: •TiO 2 NPs cytotoxicity at low exposure levels (≤1 μg/mL) to freshwater algae. •ROS generation, NP adsorption and internalization contributors to toxicity. •Observational evidence of genotoxicity by nanoparticles in an algal cell. •Reduced bioavailability thus detoxification of NPs by microalgae. •Possible role of EPS in detoxification. -- Abstract: In the current study, two aspects concerning (i) the cytotoxicity potential of TiO 2 nanoparticles (NPs) toward freshwater algal isolate Scenedesmus obliquus and (ii) the potential detoxification of NPs by the microalgae were assessed under light (UV-illumination) and dark conditions at low exposure levels (≤1 μg/mL), using sterile freshwater as the test medium. The statistically significant reduction in cell viability, increase in reactive oxygen species production and membrane permeability (light vs. dark) suggested photo-induced toxicity of TiO 2 NPs. The electron micrographs demonstrated adsorption of the NPs onto the cell surface and substantiated their internalization/uptake. The fluorescence micrographs and the confocal laser scanning (CLSM) images suggested the absence of a definite/intact nucleus in the light treated cells pointing toward the probable genotoxic effects of NPs. In a separate three cycle experiment, a continuous decrease in the cytotoxicity was observed, whereas, at the end of each cycle only fresh algae were added to the supernatant containing NPs from the previous cycle. The decreasing concentrations of the NPs in the subsequent cycles owing to agglomeration–sedimentation processes exacerbated by the algal interactions played a crucial role in the detoxification. In addition, the exo-polymeric substances produced by the cells could have rendered the available NPs less reactive, thereby, enhancing the detoxification effects

  10. Effects of silver adsorbed on fumed silica, silver phosphate glass, bentonite organomodified with silver and titanium dioxide in aquatic indicator organisms.

    Science.gov (United States)

    Tomacheski, Daiane; Pittol, Michele; Simões, Douglas Naue; Ribeiro, Vanda Ferreira; Santana, Ruth Marlene Campomanes

    2017-06-01

    In order to reduce the level of transmission of diseases caused by bacteria and fungi, the development of antimicrobial additives for use in personal care, hygiene products, clothing and others has increased. Many of these additives are based on metals such as silver and titanium. The disposal of these products in the environment has raised concerns pertaining to their potential harmfulness for beneficial organisms. The objective of this study was to evaluate the influence of the shape, surface chemistry, size and carrier of three additives containing silver and one with titanium dioxide (TiO 2 ) on microcrustacean survival. Daphnia magna was used as a bioindicator for acute exposure test in suspensions from 0.0001 to 10,000ppm. Ceriodaphnia dubia was used for chronic test in TiO 2 suspensions from 0.001 to 100ppm. D. magna populations presented high susceptibility to all silver based additives, with 100% mortality after 24hr of exposure. A different result was found in the acute experiments containing TiO 2 suspensions, with mortality rates only after 48hr of incubation. Even on acute and chronic tests, TiO 2 did not reach a linear concentration-response versus mortality, with 1ppm being more toxic than 10,000ppm on acute test and 0.001 more toxic than 0.01ppm on chronic assay. Silver based material toxicity was attributed to silver itself, and had no relation to either form (nano or ion) or carrier (silica, phosphate glass or bentonite). TiO 2 demonstrated to have a low acute toxicity against D. magna. Copyright © 2016. Published by Elsevier B.V.

  11. TiO2/Cu2O composite based on TiO2 NTPC photoanode for photoelectrochemical (PEC) water splitting under visible light

    KAUST Repository

    Shi, Le

    2015-05-01

    Water splitting through photoelectrochemical reaction is widely regarded as a major method to generate H2 , a promising source of renewable energy to deal with the energy crisis faced up to human being. Efficient exploitation of visible light in practice of water splitting with pure TiO2 material, one of the most popular semiconductor material used for photoelectrochemical water splitting, is still challenging. One dimensional TiO2 nanotubes is highly desired with its less recombination with the short distance for charge carrier diffusion and light-scattering properties. This work is based on TiO2 NTPC electrode by the optimized two-step anodization method from our group. A highly crystalized p-type Cu2O layer was deposited by optimized pulse potentiostatic electrochemical deposition onto TiO2 nanotubes to enhance the visible light absorption of a pure p-type TiO2 substrate and to build a p-n junction at the interface to improve the PEC performance. However, because of the real photocurrent of Cu2O is far away from its theoretical limit and also poor stability in the aqueous environment, a design of rGO medium layer was added between TiO2 nanotube and Cu2O layer to enhance the photogenerated electrons and holes separation, extend charge carrier diffusion length (in comparison with those of conventional pure TiO2 or Cu2O materials) which could significantly increase photocurrent to 0.65 mA/cm2 under visible light illumination (>420 nm) and also largely improve the stability of Cu2O layer, finally lead to an enhancement of water splitting performance.

  12. Interface actions between TiO2 and porous diatomite on the structure and photocatalytic activity of TiO2-diatomite

    International Nuclear Information System (INIS)

    Xia, Yue; Li, Fangfei; Jiang, Yinshan; Xia, Maosheng; Xue, Bing; Li, Yanjuan

    2014-01-01

    TiO 2 -diatomite photocatalysts were prepared by sol–gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption–desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO 2 , the anatase-to-rutile phase transition temperature of TiO 2 loaded on diatomite carrier is significantly increased to nearly 900 °C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange (MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H 3 PO 4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si–O–Ti bond, increase the binding strength between TiO 2 and diatomite, restrain crystal growth of loaded TiO 2 , and thus form thermal-stable mesoporous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO 2 -diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO 2 -diatomite pretreated by phosphoric acid.

  13. Interface actions between TiO2 and porous diatomite on the structure and photocatalytic activity of TiO2-diatomite

    Science.gov (United States)

    Xia, Yue; Li, Fangfei; Jiang, Yinshan; Xia, Maosheng; Xue, Bing; Li, Yanjuan

    2014-06-01

    TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 °C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange (MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable mesoporous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid.

  14. Imbalance of morphofunctional responses of Jurkat T lymphoblasts at short-term culturing with relief zinc- or copper-containing calcium phosphate coating on titanium.

    Science.gov (United States)

    Litvinova, L S; Shupletsova, V V; Dunets, N A; Khaziakhmatova, O G; Yurova, K A; Khlusova, M Yu; Slepchenko, G B; Cherempey, E G; Sharkeev, Yu P; Komarova, E G; Sedelnikova, M B; Khlusov, I A

    2017-01-01

    Morphofunctional response of Jurkat T cells that were cultured for 24 h on substrates prepared from commercially pure titanium with relief microarc bilateral calcium phosphate coating containing copper or zinc was studied. Changes in the concentration of essential trace elements contained in this coating can cause significant imbalance of molecular processes of differentiation, secretion, apoptosis, and necrosis and reduce tumor cell survival.

  15. A randomised study to compare salivary pH, calcium, phosphate and calculus formation after using anticavity dentifrices containing Recaldent(®) and functionalized tri-calcium phosphate.

    Science.gov (United States)

    Sharma, Ena; Vishwanathamurthy, Ramesh Alampalli; Nadella, Manjari; Savitha, A N; Gundannavar, Gayatri; Hussain, M Ahad

    2012-10-01

    The aim of this study was to estimate the pH of saliva, concentration of calcium and inorganic phosphate, and calculus formation before and after usage of Recaldent(®) (GC Tooth Mousse Plus™), Functionalized Tricalcium Phosphate (3M ESPE ClinPro™ Tooth Crème) and standard dentifrice (Colgate dental cream). Randomized double-blind study. A total of 50 subjects were recruited, the subjects were assessed at their first visit, on the 21(st) day and on the 42(nd) day. At the first visit, scaling was carried out and oral hygiene instructions were given. After 21 days, the subjects were given coded dentifrices where the operator and the subjects both were unaware of the type of dentifrice. Clinical parameters assessed were Plaque index, Gingival index, and Calculus index. Salivary samples were obtained to measure calcium, phosphate levels, and pH at 21(st) day and 42(nd) day. ANOVA test, t-test, Mann-Whitney test, Kruskal-Wallis test. The mean salivary calcium level and mean salivary phosphate level were higher in Group III (functionalized tricalcium phosphate (3M ESPE ClinPro™ Tooth Creme) as compared to Group II (Recaldent(®) GC Tooth Mousse Plus™) and Group I (Colgate dental cream) on the 42(nd) day after using dentifrices, which was statistically significant. This showed that the usage of remineralizing dentifrices led to an increase in the salivary calcium, phosphate, and pH but it did not reach the level of super saturation of the ions caused by elevated pH which could lead to calculus formation. Thought here was a statistically significant increase in salivary calcium and phosphate level in all three groups from baseline to 42(nd) day, there was no calculus formation.

  16. XAS study of TiO2-based nanomaterials

    Science.gov (United States)

    Schneider, K.; Zajac, D.; Sikora, M.; Kapusta, Cz.; Michalow-Mauke, K.; Graule, Th.; Rekas, M.

    2015-07-01

    X-Ray Absorption Spectroscopy studies of the W (0-1 at% W) and Mo-doped TiO2 (0-1 at% Mo) nanoparticle specimens at the K edges of titanium and molybdenum as well as at the L2 L3 edges of tungsten are presented. The materials were prepared with Flame Spray Synthesis process by oxidation of metal-organic precursors. The Ti:K edge spectra in the XANES range show pre-edge and post-edge features characteristic for anatase. A decrease of the amplitude of the EXAFS function with doping is observed and attributed to a softening of the crystal lattice. The Mo EXAFS functions show a considerable decrease of the second-neighbour-shell peak with increasing Mo content, which is attributed to an increased number of cation vacancies. For tungsten a less pronounced effect is observed. The Mo and W XANES spectra do not show noticeable changes with doping level, which indicates their unchanged oxidation states.

  17. Optical spectroscopy of rare earth ion-doped TiO2 nanophosphors.

    Science.gov (United States)

    Chen, Xueyuan; Luo, Wenqin

    2010-03-01

    Trivalent rare-earth (RE3+) ion-doped TiO2 nanophosphors belong to one kind of novel optical materials and have attracted increasing attention. The luminescence properties of different RE3+ ions in various TiO2 nanomaterials have been reviewed. Much attention is paid to our recent progresses on the luminescence properties of RE3+ (RE = Eu, Er, Sm, Nd) ions in anatase TiO2 nanoparticles prepared by a sol-gel-solvothermal method. Using Eu3+ as a sensitive optical probe, three significantly different luminescence centers of Eu3+ in TiO2 nanoparticles were detected by means of site-selective spectroscopy at 10 K. Based on the crystal-field (CF) splitting of Eu3+ at each site, C2v and D2 symmetries were proposed for Eu3+ incorporated at two lattice sites. A structural model for the formation of multiple sites was proposed based on the optical behaviors of Eu3+ at different sites. Similar multi-site luminescence was observed in Sm(3+)- or Nd(3+)-doped TiO2 nanoparticles. In Eu(3+)-doped TiO2 nanoparticles, only weak energy transfer from the TiO2 host to the Eu3+ ions was observed at 10 K due to the mismatch of energy between the TiO2 band-gap and the Eu3+ excited states. On the contrary, efficient host-sensitized luminescences were realized in Sm(3+)- or Nd(3+)-doped anatase TiO2 nanoparticles due to the match of energy between TiO2 band-gap and the Sm3+ and Nd3+ excited states. The excitation spectra of both Sm(3+)- and Nd(3+)-doped samples exhibit a dominant broad peak centered at approximately 340 nm, which is associated with the band-gap of TiO2, indicating that sensitized emission is much more efficient than direct excitation of the Sm3+ and Nd3+ ions. Single lattice site emission of Er3+ in TiO2 nanocrystals can be achieved by modifying the experimental conditions. Upon excitation by a Ti: sapphire laser at 978 nm, intense green upconverted luminescence was observed. The characteristic emission of Er3+ ions was obtained both in the ultraviolet-visible (UV-vis) and near-infrared regions through the high-resolution experiments at 10 K. The CF experienced by Er3+ in TiO2 nanocrystal was systematically studied by means of the energy level fitting.

  18. Mechanical properties and ion release from bioactive restorative composites containing glass fillers and calcium phosphate nano-structured particles.

    Science.gov (United States)

    Chiari, Marina D S; Rodrigues, Marcela C; Xavier, Tathy A; de Souza, Eugen M N; Arana-Chavez, Victor E; Braga, Roberto R

    2015-06-01

    To evaluate the effect of the replacement of barium glass by dicalcium phosphate dihydrate (DCPD) particles on the mechanical properties and degree of conversion (DC) of composites. Additionally, calcium and hydrogen phosphate (HPO4(2-)) release were followed for 28 days. Nine composites containing equal parts (in mols) of BisGMA and TEGDMA and 40, 50 or 60 vol% of total filler were manipulated. Filler phase was constituted by silanated barium glass and 0%, 10% or 20% of DCPD particles. DC was determined by near-FTIR. Biaxial flexural strength (BFS) and modulus (E) were tested using the "piston on three balls" method, while fracture toughness (KIc) used the "single edge notched beam" method. Specimens were tested after 24h and 28 days in water. Ion release was determined using inductively coupled plasma optical emission spectrometry (ICP-OES). Data were analyzed by ANOVA/Tukey (DC and ion release) or Kruskal-Wallis/Mann-Whitney (mechanical properties; alpha: 5%). DC was not affected by DCPD. The presence of DCPD reduced BFS for both storage times, while differences in E became evident after 28 days. After 24h, KIc increased with the addition of DCPD; after 28 days, however, KIc decreased only for DCPD-containing composites. Calcium release was similar for both DCPD contents and remained fairly constant during the 28-day period. Overall, HPO4(2-) release was higher at 7 days and did not decrease after 14 days. The composite with the highest filler level and 10% DCPD represented the best compromise between mechanical properties after aging in water and ion release. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  19. Photoactive layer-by-layer films of cellulose phosphate and titanium dioxide containing phosphotungstic acid

    Energy Technology Data Exchange (ETDEWEB)

    Ullah, Sajjad [Instituto de Química de São Carlos, Universidade de São Paulo, PO Box 780, São Carlos, São Paulo 13564-970 (Brazil); Acuña, José Javier Sáez [Centro de Ciências Naturais e Humanas, Universidade Federal do ABC, Santo Andre, Sao Paulo, 09210-170 (Brazil); Pasa, André Avelino [Surface and Thin Film Laboratory, Physics Department, Federal University of Santa Catarina, PO Box 476, Florianópolis, SC 88040-900 (Brazil); Bilmes, Sara A. [Universidad de Buenos Aires, Facultad Ciencias Exactas y Naturales, Instituto de Química Física de los Materiales, Medio Ambiente y Energía – INQUIMAE, Ciudad Universitaria, Pab. 2, Buenos Aires C1428EHA (Argentina); Vela, Maria Elena; Benitez, Guillermo [Laboratorio de Nanoscopías y Fisicoquímica de Superficies, Instituto de Investigaciones Fisicoquímicas Teóricas y Aplicadas (INIFTA), Universidad Nacional de La Plata – CONICET, diagonal 113 esquina 64. C.C.16.Suc.4, 1900 La Plata (Argentina); Rodrigues-Filho, Ubirajara Pereira, E-mail: uprf@iqsc.usp.br [Instituto de Química de São Carlos, Universidade de São Paulo, PO Box 780, São Carlos, São Paulo 13564-970 (Brazil)

    2013-07-15

    A versatile layer-by-layer (LbL) procedure for the preparation of highly dispersed, adherent and porous multilayer films of TiO{sub 2} nanoparticles (NPs) and phosphotungstic acid (HPW) on a variety of substrates at room temperature was developed based on the use of cellulose phosphate (CP) as an efficient and non-conventional polyelectrolyte. UV/vis absorption spectroscopy confirmed the linear and regular growth of the films with the number of immersion cycles and a strong adsorption ability of CP towards TiO{sub 2} NPs. FTIR spectroscopy showed that HPW binds to the surface of TiO{sub 2} through the oxygen atom at the corner of the Keggin structure. XPS results showed that the interaction between TiO{sub 2} and CP is through Ti–O–P linkage. A model is proposed for the TiO{sub 2}–HPW interaction based on XPS and FTIR results. FEG/SEM study of the surface morphology revealed a porous film structure with a homogenous distribution of the TiO{sub 2} NPs induced by CP. HRTEM studies showed that the resulting composite films consist of crystalline anatase and rutile phases and poly-nano-crystalline HPW with a semi-crystalline TiO{sub 2}–HPW interface. These CP/TiO{sub 2} and CP/TiO{sub 2}/HPW LbL films showed good photoactivity against both saturated and unsaturated species, for instance, stearic acid (SA), crystal violet (CV) and methylene blue (MB) under UV irradiation. The CP/HPW films formed on bacterial cellulose (BC) showed good photochromic response which is enhanced in presence of TiO{sub 2} due to an interfacial electron transfer from TiO{sub 2} to HPW. This simple and environmentally safe method can be used to form coatings on a variety of surfaces with photoactive TiO{sub 2} and TiO{sub 2}/HPW films.

  20. In situ controlled synthesis of various TiO2 nanostructured materials via a facile hydrothermal route

    International Nuclear Information System (INIS)

    Wang Hai; Liu Yong; Zhong Minyi; Xu Hongmei; Huang Hong; Shen Hui

    2011-01-01

    Various TiO 2 nanomaterials, such as nanosheets, nanoflowers, and nanowires were directly self assembled on titanium substrate on a large scale under hydrothermal conditions. The morphology of the formed TiO 2 nanomaterials could be easily tuned by varying the experimental parameters of temperature, reaction time, and the NaOH concentration. A possible formation mechanism was suggested on the basis of the shape evolution of TiO 2 nanostructures by SEM images in combination with XRD patterns of as-grown samples. The optical properties of TiO 2 nanosheets, nanoflowers, and nanowires were characterized by reflectance spectroscopy. The studies revealed that the absorption capability of visible light is obviously different for TiO 2 with different morphologies. Moreover, TiO 2 nanosheets exhibited better light trapping than TiO 2 nanoflowers and TiO 2 nanowires due to their unique nanostructure.

  1. Laser induced photocurrent and photovoltage transient measurements of dye-sensitized solar cells based on TiO_2 nanosheets and TiO_2 nanoparticles

    International Nuclear Information System (INIS)

    Ghaithan, Hamid M.; Qaid, Saif M.H.; Hezam, Mahmoud; Labis, Joselito P.; Alduraibi, Mohammad; Bedja, Idriss M.; Aldwayyan, Abdullah S.

    2016-01-01

    Dye-sensitized solar cells (DSSCs) based on TiO_2 nanoparticles and TiO_2 nanosheets with exposed {001} facets are investigated using laser-induced photovoltage and photocurrent transient decay (LIPVCD) measurements. We adopted a simplified version of LIPVCD technique, in which a single illumination light source and a laboratory oscilloscope could be conveniently used for the measurements. Although the {001} surface of TiO_2 nanosheets allowed a noticeably slower recombination with the electrolyte, this was counterpoised by a slower electron transport probably due to its planar morphology, resulting in a shorter diffusion length in TiO_2 nanosheets. The nanosheet morphology also resulted in less surface area and therefore reduced short circuit current density in the fabricated devices. Our work highlights the fact that the morphological parameters of TiO_2 nanosheets finally resulting after electrode film deposition is of no less importance than the reported efficient dye adsorption and slow electron recombination at the surface of individual nanosheets.

  2. Disruption of Autolysis in Bacillus subtilis using TiO2 Nanoparticles.

    Science.gov (United States)

    McGivney, Eric; Han, Linchen; Avellan, Astrid; VanBriesen, Jeanne; Gregory, Kelvin B

    2017-03-17

    In contrast to many nanotoxicity studies where nanoparticles (NPs) are observed to be toxic or reduce viable cells in a population of bacteria, we observed that increasing concentration of TiO 2 NPs increased the cell survival of Bacillus subtilis in autolysis-inducing buffer by 0.5 to 5 orders of magnitude over an 8 hour exposure. Molecular investigations revealed that TiO 2 NPs prevent or delay cell autolysis, an important survival and growth-regulating process in bacterial populations. Overall, the results suggest two potential mechanisms for the disruption of autolysis by TiO 2 NPs in a concentration dependent manner: (i) directly, through TiO 2 NP deposition on the cell wall, delaying the collapse of the protonmotive-force and preventing the onset of autolysis; and (ii) indirectly, through adsorption of autolysins on TiO 2 NP, limiting the activity of released autolysins and preventing further lytic activity. Enhanced darkfield microscopy coupled to hyperspectral analysis was used to map TiO 2 deposition on B. subtilis cell walls and released enzymes, supporting both mechanisms of autolysis interference. The disruption of autolysis in B. subtilis cultures by TiO 2 NPs suggests the mechanisms and kinetics of cell death may be influenced by nano-scale metal oxide materials, which are abundant in natural systems.

  3. Thiourea-Modified TiO2 Nanorods with Enhanced Photocatalytic Activity

    Directory of Open Access Journals (Sweden)

    Xiaofeng Wu

    2016-02-01

    Full Text Available Semiconductor TiO2 photocatalysis has attracted much attention due to its potential application in solving the problems of environmental pollution. In this paper, thiourea (CH4N2S modified anatase TiO2 nanorods were fabricated by calcination of the mixture of TiO2 nanorods and thiourea at 600 °C for 2 h. It was found that only N element was doped into the lattice of TiO2 nanorods. With increasing the weight ratio of thiourea to TiO2 (R from 0 to 8, the light-harvesting ability of the photocatalyst steady increases. Both the crystallization and photocatalytic activity of TiO2 nanorods increase first and then decrease with increase in R value, and R2 sample showed the highest crystallization and photocatalytic activity in degradation of Brilliant Red X3B (X3B and Rhodamine B (RhB dyes under visible light irradiation (λ > 420 nm. The increased visible-light photocatalytic activity of the prepared N-doped TiO2 nanorods is due to the synergistic effects of the enhanced crystallization, improved light-harvesting ability and reduced recombination rate of photo-generated electron-hole pairs. Note that the enhanced visible photocatalytic activity of N-doped nanorods is not based on the scarification of their UV photocatalytic activity.

  4. Adsorption and photodegradation of methylene blue on TiO_2-halloysite adsorbents

    International Nuclear Information System (INIS)

    Du, Yuanyuan; Zheng, Pengwu

    2014-01-01

    TiO_2-halloysite (TiO_2-HNT) composites were fabricated by depositing anatase TiO_2 on the halloysite (HNT) surfaces with calcination treatment at 100, 200, 300 and 500 .deg. C. The obtained composites were characterized by transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR) and X-Ray diffraction (XRD). HNT was attached with TiO_2 particles or clusters in sizes of 10-30 nm. With the increasing of calcination temperature, the crystalline of anatase became more perfect, but the structure of HNT could be destroyed at 500 .deg. C. The adsorption and photodegradation of methylene blue (MB) by TiO_2-HNTs were investigated. The kinetic adsorption fit the pseudo second-order, and the isotherm data followed the Langmuir model. The maximum adsorption capacities of MB were in the range of 38.57 to 54.29 mg/g. TiO_2-HNTs exhibited an efficient photocatalytic activity in the decomposition of MB. For TiO_2-HNT calcined at 300 .deg. C, 81.6% MB were degraded after 4 h treatment of UV irradiation

  5. High-performance thermoelectric materials based on ternary TiO2/CNT/PANI composites.

    Science.gov (United States)

    Erden, Fuat; Li, Hui; Wang, Xizu; Wang, FuKe; He, Chaobin

    2018-04-04

    In the present work, we report the fabrication of high-performance thermoelectric materials using TiO2/CNT/PANI ternary composites. We showed that a conductivity of ∼2730 S cm-1 can be achieved for the binary CNT (70%)/PANI (30%) composite, which is the highest recorded value for the reported CNT/PANI composites. We further demonstrated that the Seebeck coefficient of CNT/PANI composites could be enhanced by incorporating TiO2 nanoparticles into the binary CNT/PANI composites, which could be attributed to lower carrier density and the energy scattering of low-energy carriers at the interfaces of TiO2/a-CNT and TiO2/PANI. The resulting TiO2/a-CNT/PANI ternary system exhibits a higher Seebeck coefficient and enhanced thermoelectric power. Further optimization of the thermoelectric power was achieved by water treatment and by tuning the processing temperature. A high thermoelectric power factor of 114.5 μW mK-2 was obtained for the ternary composite of 30% TiO2/70% (a-CNT (70%)/PANI (30%)), which is the highest reported value among the reported PANI based ternary composites. The improvement of thermoelectric performance by incorporation of TiO2 suggests a promising approach to enhance power factor of organic thermoelectric materials by judicial tuning of the carrier concentration and electrical conductivity.

  6. Toxicity of nanotitanium dioxide (TiO2-NP) on human monocytes and their mitochondria.

    Science.gov (United States)

    Ghanbary, Fatemeh; Seydi, Enaytollah; Naserzadeh, Parvaneh; Salimi, Ahmad

    2018-03-01

    The effect of nanotitanium dioxide (TiO 2 -NP) in human monocytes is still unknown. Therefore, an understanding of probable cytotoxicity of TiO 2 -NP on human monocytes and underlining the mechanisms involved is of significant interest. The aim of this study was to assess the cytotoxicity of TiO 2 -NP on human monocytes. Using biochemical and flow cytometry assessments, we demonstrated that addition of TiO 2 -NP at 10 μg/ml concentration to monocytes induced cytotoxicity following 12 h. The TiO 2 -NP-induced cytotoxicity on monocytes was associated with intracellular reactive oxygen species (ROS) generation, mitochondrial membrane potential (MMP) collapse, lysosomal membrane injury, lipid peroxidation, and depletion of glutathione. According to our results, TiO 2 -NP triggers oxidative stress and organelles damages in monocytes which are important cells in defense against foreign agents. Finally, our findings suggest that use of antioxidants and mitochondrial/lysosomal protective agents could be of benefit for the people in the exposure with TiO 2 -NP.

  7. Single-Nanoparticle Photoelectrochemistry at a Nanoparticulate TiO2 -Filmed Ultramicroelectrode.

    Science.gov (United States)

    Peng, Yue-Yi; Ma, Hui; Ma, Wei; Long, Yi-Tao; Tian, He

    2018-03-26

    An ultrasensitive photoelectrochemical method for achieving real-time detection of single nanoparticle collision events is presented. Using a micrometer-thick nanoparticulate TiO 2 -filmed Au ultra-microelectrode (TiO 2 @Au UME), a sub-millisecond photocurrent transient was observed for an individual N719-tagged TiO 2 (N719@TiO 2 ) nanoparticle and is due to the instantaneous collision process. Owing to a trap-limited electron diffusion process as the rate-limiting step, a random three-dimensional diffusion model was developed to simulate electron transport dynamics in TiO 2 film. The combination of theoretical simulation and high-resolution photocurrent measurement allow electron-transfer information of a single N719@TiO 2 nanoparticle to be quantified at single-molecule accuracy and the electron diffusivity and the electron-collection efficiency of TiO 2 @Au UME to be estimated. This method provides a test for studies of photoinduced electron transfer at the single-nanoparticle level. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  8. Simplified TiO2 force fields for studies of its interaction with biomolecules

    Science.gov (United States)

    Luan, Binquan; Huynh, Tien; Zhou, Ruhong

    2015-06-01

    Engineered TiO2 nanoparticles have been routinely applied in nanotechnology, as well as in cosmetics and food industries. Despite active experimental studies intended to clarify TiO2's biological effects, including potential toxicity, the relation between experimentally inferred nanotoxicity and industry standards for safely applying nanoparticles remains somewhat ambiguous with justified concerns. Supplemental to experiments, molecular dynamics simulations have proven to be efficacious in investigating the molecular mechanism of a biological process occurring at nanoscale. In this article, to facilitate the nanotoxicity and nanomedicine research related to this important metal oxide, we provide a simplified force field, based on the original Matsui-Akaogi force field but compatible to the Lennard-Jones potentials normally used in modeling biomolecules, for simulating TiO2 nanoparticles interacting with biomolecules. The force field parameters were tested in simulating the bulk structure of TiO2, TiO2 nanoparticle-water interaction, as well as the adsorption of proteins on the TiO2 nanoparticle. We demonstrate that these simulation results are consistent with experimental data/observations. We expect that simulations will help to better understand the interaction between TiO2 and molecules.

  9. Titanium Dioxide (TiO2) Dye-Sensitized Solar Cells

    Science.gov (United States)

    Alseadi, Anwar Abdulaziz

    With the increasing global energy consumption and diminishing fossil fuels, various renewable and sustainable energies have been harvested in past decades and related devices have been fabricated. Dye-sensitized solar cells (DSSCs) are the most efficient third-generation solar cells to harvest solar energy into electricity directly. Titanium dioxide (TiO2) based DSSCs were invented in 1988 and have attracted more and more attention since then because of low-cost and high efficiency. TiO2 nanoparticles are one kind of popular anode materials of DSSC because of stability, abundance, environment safety, non-toxicity, and excellent photovoltaic properties. In the project, TiO2 nanoparticles with different crystallographic sizes were produced by ball-milling. Physical properties of the produced TiO 2 nanoparticles were characterized by X-ray powder diffraction, UV-visible spectroscopy, and Raman scattering. TiO2-based DSSCs were fabricated and their photovoltaic performances were tested. The effects of TiO2 layer thickness, crystallographic size, and microsphere fillings were investigated. The project enriched our understanding of TiO2-based DSSCs.

  10. Enhanced Photocatalytic Properties of Ag-Loaded N-Doped Tio2 Nanotube Arrays

    Directory of Open Access Journals (Sweden)

    Gao Dawei

    2018-03-01

    Full Text Available Highly ordered TiO2 nanotube (TiO2 NT arrays were prepared by anodic oxidizing method on the surface of the Ti substrate. Nitrogen-doped TiO2 nanotube (N-TiO2 NT arrays were carried out by ammonia solution immersion, and Ag nanoparticles loaded N-doped TiO2 nanotube (Ag/N-TiO2 NT arrays were obtained by successive ionic layer adsorption and reaction (SILAR technique. The samples were characterized by the X-ray diffraction (XRD, X-ray photoelectron spectroscopy (XPS, field emission scanning electron microscopy (FESEM, high-resolution transmission electron microscopy (HRTEM, photoluminescence (PL emission spectra, ultraviolet–visible (UV–vis diffuse reflectance spectroscopy (DRS. The result indicated that the diameter and wall thickness of the TiO2 NT are 100–120 and 20–30 nm, respectively. Moreover, the morphology and structure of the highly ordered TiO2 NTs were not affected by N-doping. Furthermore, Ag nanoparticles were evenly deposited on the surface of TiO2 NTs in the form of elemental silver. Finally, the photocatalytic activity of Ag/N-TiO2 NTs was evaluated by degradation of methyl orange (MO under visible-light irradiation. The Ag/N-TiO2 NTs exhibited enhanced photocatalytic properties, which could reach 95% after 90-min irradiation.

  11. Decolorization of dyeing wastewater in continuous photoreactors using tio2 coated glass tube media

    Directory of Open Access Journals (Sweden)

    Jutaporn Chanathaworn

    2014-02-01

    Full Text Available The present study deals with a decolorization development of malachite green (MG dyeing wastewater using TiO2 thin films coated glass tube media in photoreactor. The TiO2 photocatalyst was synthesized by three methods: TTIP sol-gel, TiO2 powder-modified sol, and TiO2 powder suspension coating on raschig ring glass tube media and was investigated crystallinity phase by SEM, XRD, and AFM. Degradation kinetics of the dyeing wastewater by photocatalytic was carried out under UV light irradiation. The Langmuir first-order model provided the best fit to the experimental data. The catalyst prepared by powder suspension technique and coated on glass tube had given the highest of decolorization kinetics and efficiency. Continuous photoreactor packed with the TiO2 coating media was designed and proven to be the high effectiveness for MG dyeing degradation and stable throughout the recyclability test. The light intensity, dye solution flow rate, and TiO2 loading were the most important parameters that response to decolorization efficiency. The optimum condition of photo decolorization of MG dye solution can be obtained from RSM model. Effectiveness of the synthesized TiO2 thin films using suspension technique and the continuous photoreactor design were obtained with a great potential to be proven for wastewater treatment at industrial scale.

  12. Light-induced antifungal activity of TiO2 nanoparticles/ZnO nanowires

    International Nuclear Information System (INIS)

    Haghighi, N.; Abdi, Y.; Haghighi, F.

    2011-01-01

    Antifungal activity of TiO 2 /ZnO nanostructures under visible light irradiation was investigated. A simple chemical method was used to synthesize ZnO nanowires. Zinc acetate dihydrate, Polyvinyl Pyrrolidone and deionized water were used as precursor, capping and solvent, respectively. TiO 2 nanoparticles were deposited on ZnO nanowires using an atmospheric pressure chemical vapor deposition system. X-ray diffraction pattern of TiO 2 /ZnO nano-composite has represented the diffraction peaks relating to the crystal planes of the TiO 2 (anatase and rutile) and ZnO. TiO 2 /ZnO nanostructure antifungal effect on Candida albicans biofilms was studied and compared with the activity of TiO 2 nanoparticles and ZnO nanowires. The high efficiency photocatalytic activity of TiO 2 nanoparticles leads to increased antifungal activity of ZnO nanowires. Scanning electron microscope was utilized to study the morphology of the as prepared nanostructures and the degradation of the yeast.

  13. Enhanced properties of nanostructured TiO2-graphene composites by rapid sintering

    Science.gov (United States)

    Shon, In-Jin; Yoon, Jin-Kook; Hong, Kyung-Tae

    2018-01-01

    Despite of many attractive properties of TiO2, the drawback of TiO2 ceramic is low fracture toughness for widely industrial application. The method to improve the fracture toughness and hardness has been reported by addition of reinforcing phase to fabricate a nanostructured composite. In this regard, graphene has been evaluated as an ideal second phase in ceramics. Nearly full density of nanostructured TiO2-graphene composite was achieved within one min using pulsed current activated sintering. The effect of graphene on microstructure, fracture toughness and hardness of TiO2-graphene composite was evaluated using Vickers hardness tester and field emission scanning electron microscopy. The grain size of TiO2 in the TiO2-x vol% (x = 0, 1, 3, and 5) graphene composite was greatly reduced with increase in addition of graphene. Both hardness and fracture toughness of TiO2-graphene composites simultaneously increased in the addition of graphene.

  14. ALMA observations of TiO2 around VY Canis Majoris

    Science.gov (United States)

    De Beck, E.; Vlemmings, W.; Muller, S.; Black, J. H.; O'Gorman, E.; Richards, A. M. S.; Baudry, A.; Maercker, M.; Decin, L.; Humphreys, E. M.

    2015-08-01

    Context. Titanium dioxide, TiO2, is a refractory species that could play a crucial role in the dust-condensation sequence around oxygen-rich evolved stars. To date, gas phase TiO2 has been detected only in the complex environment of the red supergiant VY CMa. Aims: We aim to constrain the distribution and excitation of TiO2 around VY CMa in order to clarify its role in dust formation. Methods: We analyse spectra and channel maps for TiO2 extracted from ALMA science verification data. Results: We detect 15 transitions of TiO2, and spatially resolve the emission for the first time. The maps demonstrate a highly clumpy, anisotropic outflow in which the TiO2 emission likely traces gas exposed to the stellar radiation field. An accelerating bipolar-like structure is found, oriented roughly east-west, of which the blue component runs into and breaks up around a solid continuum component. A distinct tail to the south-west is seen for some transitions, consistent with features seen in the optical and near-infrared. Conclusions: We find that a significant fraction of TiO2 remains in the gas phase outside the dust-formation zone and suggest that this species might play only a minor role in the dust-condensation process around extreme oxygen-rich evolved stars like VY CMa. Appendix A is available in electronic form at http://www.aanda.org

  15. Photocatalytic degradation of Rhodamine B dye using Fe doped TiO2 nanocomposites

    Science.gov (United States)

    Barkhade, Tejal; Banerjee, Indrani

    2018-05-01

    The unique properties of titanium dioxide (TiO2) such as high photo catalytic activity, high chemical stability and low toxicity have made it a suitable photocatalyst in recent decades. The effect of modification of TiO2 with doping of iron on its characteristics and photo catalytic efficiency was studied. The change in band gap energy of TiO2 nanoparticles after doping with Fe has been studied. Significant enhancement in photo catalytic property of TiO2 after Fe doping under light exposure conditions has been investigated. Acute exposure to non-biodegradable Rhodamine B resulted in many health problems like burning of eyes, skin irritation, nasal burning, and chest pain etc. Therefore, degradation of this dye is needed to save environment and animals. Considering the similar radius of Fe3+ and Ti4+ ions (respectively 0.64 Å and 0.68 Å), titanium position in the lattice of TiO2 can be replaced by iron cations easily. The undoped and Fe doped TiO2 nano composites were synthesized by sol-gel method, in which 1.0M% of Fe was doped with TiO2 and then the samples were characterized by using FE-SEM, UV-Visible diffuse spectroscopy, Raman Spectroscopy, and FTIR. Photo catalytic degradation of Rhodamine B dye experiment was carried out in visible light range. After 90 min time duration pink colour of dye turned colourless, indicating significant degradation rate with time.

  16. NOx photocatalytic degradation on gypsum plates modified by TiO2-N,C photocatalysts

    Directory of Open Access Journals (Sweden)

    Janus Magdalena

    2015-09-01

    Full Text Available In presented studies the photocatalytic decomposition of NOx on gypsum plates modified by TiO2-N,Cphotocatalysts were presented. The gypsum plates were obtained by addition of 10 or 20 wt.% of different types of titanium dioxide, such as: pure TiO2 and carbon and nitrogen co-modified TiO2 (TiO2-N,C to gypsum. TiO2-N,C photocatalysts were obtained by heating up the starting TiO2 (Grupa Azoty Zakłady Chemiczne Police S.A in the atmosphere of ammonia and carbon at the temperature: 100, 300 i 600ºC. Photocatalyst were characterized by FTIR/DRS, UVVis/DR, BET and XRD methods. Moreover the compressive strength tests of modified gypsum were also done. Photocatalytic activity of gypsum plates was done during NOx decomposition. The highest photocatalytic activity has gypsum with 20 wt.% addition of TiO2-N,C obtained at 300ºC.

  17. Facile synthesis of porous TiO_2 photocatalysts using waste sludge as the template

    International Nuclear Information System (INIS)

    Wang, Xiaopeng; Huang, Shouqiang; Zhu, Nanwen; Lou, Ziyang; Yuan, Haiping

    2015-01-01

    Graphical abstract: Waste sludge is introduced to synthesize the waste sludge templated TiO_2 photocatalyst with porous structure, which possesses better photocatalytic activity compared to pure TiO_2. - Highlights: • Waste sludge is introduced to synthesize the TiO_2 photocatalyst. • Waste sludge templated TiO_2 sample possesses porous structure. • Waste sludge templated TiO_2 sample exhibits high photocatalytic activity. - Abstract: A resource utilization method of waste sludge is present by the synthesis of waste sludge templated TiO_2 photocatalysts. The organic materials in waste sludge are used as the pore-forming agents, and the transition metals included in the remaining waste sludge through calcination (WSC) can serve as the dopants for the WSC-TiO_2 (WSCT) photocatalyst. The visible and UV–visible light driven photocatalytic activities of WSCT are much better compared to those of pure TiO_2 and WSC, and it is originated from the higher light absorption property and the efficient electron–hole pair separation provided by waste sludge.

  18. Probing Photocatalytic Characteristics of Sb-Doped TiO2 under Visible Light Irradiation

    Directory of Open Access Journals (Sweden)

    Lingjing Luo

    2014-01-01

    Full Text Available Sb-doped TiO2 nanoparticle with varied dopant concentrations was synthesized using titanium tetrachloride (TiCl4 and antimony chloride (SbCl3 as the precursors. The properties of Sb-doped TiO2 nanoparticles were characterized by X-ray diffraction (XRD, scanning electron microscope (SEM, fluorescence spectrophotometer, and Uv-vis spectrophotometer. The absorption edge of TiO2 nanoparticles could be extended to visible region after doping with antimony, in contrast to the UV absorption of pure TiO2. The results showed that the photocatalytic activity of Sb-doped TiO2 nanoparticles was much more active than pure TiO2. The 0.1% Sb-doped TiO2 nanoparticles demonstrated the best photocatalytic activity which was better than that of the Degussa P25 under visible light irradiation using terephthalic acid as fluorescent probe. The effects of Sb dopant on the photocatalytic activity and the involved mechanism were extensively investigated in this work as well.

  19. W-doped TiO2 photoanode for high performance perovskite solar cell

    International Nuclear Information System (INIS)

    Liu, Jinwang; Zhang, Jing; Yue, Guoqiang; Lu, Xingwei; Hu, Ziyang; Zhu, Yuejin

    2016-01-01

    Titanium dioxide (TiO 2 ) with dispersed W-doping shows its capability for efficient electron collection from perovskite to TiO 2 in perovskite solar cell. The conduction band (CB) of TiO 2 moves downward (positive shift) with increasing the tungsten (W) content, which enlarges the energy gap between the CB of TiO 2 and the perovskite. Thus, the efficiency of electron injection from perovskite to TiO 2 is increased. Due to the increased electron injection, W-doped TiO 2 (≤0.2% W content) enhances the short-circuit photocurrent (J sc ) of perovskite solar cell and improves the performance of perovskite solar cell. Perovskite solar cell with 0.1% W-doped photoanode obtains the highest power conversion efficiency (η = 10.6%), which shows enhancement by 13% in J sc and by 17% in η, as compared with the undoped TiO 2 perovskite solar cell.

  20. TiO2 nanoparticle biosynthesis and its physiological effect on mung bean (Vigna radiata L.

    Directory of Open Access Journals (Sweden)

    Ramesh Raliya

    2015-03-01

    Full Text Available TiO2 nanoparticle (NPs biosynthesis is a low cost, ecofriendly approach developed using the fungi Aspergillus flavus TFR 7. To determine whether TiO2 NPs is suitable for nutrient, we conducted a two part study; biosynthesis of TiO2 NP and evaluates their influence on mung bean. The characterized TiO2 NPs were foliar sprayed at 10 mgL−1 concentration on the leaves of 14 days old mung bean plants. A significant improvement was observed in shoot length (17.02%, root length (49.6%, root area (43%, root nodule (67.5%, chlorophyll content (46.4% and total soluble leaf protein (94% as a result of TiO2 NPs application. In the rhizosphere microbial population increased by 21.4–48.1% and activity of acid phosphatase (67.3%, alkaline phosphatase (72%, phytase (64% and dehydrogenase (108.7% enzyme was observed over control in six weeks old plants owing to application of TiO2 NPs. A possible mechanism has also been hypothesized for TiO2 NPs biosynthesis.

  1. Enhanced photocatalytic activity of wool-ball-like TiO2 microspheres on carbon fabric and FTO substrates

    Science.gov (United States)

    Zhang, Yu; Gu, Jian; Zhang, Mengqi

    2018-06-01

    The wool-ball-like TiO2 microspheres on carbon fabric (TiO2-CF) and FTO substrates (TiO2-FTO) have been synthesized by a facile hydrothermal method in alkali environment, using commercial TiO2 (P25) as precursors. The XRD results indicate that the as-prepared TiO2 have good crystallinity. And the SEM images show that the wool-ball-like TiO2 microspheres with a diameter of 2-3 μm are composed of TiO2 nanowires, which have a diameter of 50 nm. The photocatalytic behavior of the wool-ball-like TiO2 microspheres, TiO2-CF and TiO2-FTO under ultraviolet light was investigated by a pseudo first-order kinetic model, using methyl orange (MO) as pollutant. The wool-ball-like TiO2 microspheres obtained a degradation rate constant (Kap) of 6.91×10-3 min-1 . The Kap values of TiO2-FTO and TiO2-CF reach 13.97×10-3 min-1 and 11.80×10-3 min-1, which are 2.0 and 1.7 times higher than that of pristine wool-ball-like TiO2 microspheres due to the "sum effect" between TiO2 and substrates. This study offers a facile hydrothermal method to prepare wool-ball-like TiO2 microspheres on CF and FTO substrates, which will improve the recyclability of phtocatalysts and can be extended to other fields.

  2. Photocatalytic and microwave absorbing properties of polypyrrole/Fe-doped TiO2 composite by in situ polymerization method

    International Nuclear Information System (INIS)

    Li Qiaoling; Zhang Cunrui; Li Jianqiang

    2011-01-01

    Research highlights: → Polypyrrole/Fe-doped TiO 2 composite is prepared by in situ polymerization of pyrrole on the Fe-doped TiO 2 template. → The Fe-doped TiO 2 microbelts are prepared by sol-gel method using the absorbent cotton template for the first time. → Then the Fe-doped TiO 2 microbelts are used as template for the preparation of polypyrrole/Fe-doped TiO 2 composites. → The structure, morphology and properties of the composites are characterized with scanning electron microscope (SEM), IR, Net-work Analyzer. → A possible formation mechanism of Fe-doped TiO 2 microbelts and polypyrrole/Fe-doped TiO 2 composites has been proposed. → The effect of the mol ratio of pyrrole/Fe-doped TiO 2 on the photocatalysis properties and microwave loss properties of the composites is investigated. - Abstract: The Fe-doped TiO 2 microbelts were prepared by sol-gel method using the absorbent cotton template for the first time. Then the Fe-doped TiO 2 microbelts were used as templates for the preparation of polypyrrole/Fe-doped TiO 2 composites. Polypyrrole/Fe-doped TiO 2 composites were prepared by in situ polymerization of pyrrole on the Fe-doped TiO 2 template. The structure, morphology and properties of the composites were characterized with scanning electron microscope (SEM), FTIR, Net-work Analyzer. The possible formation mechanisms of Fe-doped TiO 2 microbelts and polypyrrole/Fe-doped TiO 2 composites have been proposed. The effect of the molar ratio of pyrrole/Fe-doped TiO 2 on the photocatalytic properties and microwave loss properties of the composites was investigated.

  3. RuO2-TiO2 mixed oxides prepared from the hydrolysis of the metal alkoxides

    International Nuclear Information System (INIS)

    Osman, Julian R.; Crayston, Joe A.; Pratt, Allin; Richens, David T.

    2008-01-01

    The hydrolysis of ruthenium alkoxide/titanium tetraethoxide mixtures to gels and powders containing 30-40 mol% Ru was investigated. Basic or neutral conditions led to powders consisting of 2-10 nm diameter crystalline RuO 2 nanoparticles embedded in a matrix of crystalline (anatase) and amorphous TiO 2 . Acid hydrolysis conditions gave gels containing smaller, amorphous RuO 2 nanoparticles (1-3 nm). In all samples the RuO 2 nanoparticles tended to clump into aggregates up to 0.5 μm across. Acid or neutral hydrolysis of ruthenium ethoxide gave samples which displayed lower surface Ru:Ti ratios as measured by XPS compared to the bulk (XRF), and also contained more low-valent Ru (as measured by XRF), probably due to incomplete hydrolysis of the precursors. These samples also contained more Ru metal after calcination (XRD). Calcination (450 deg. C) was accompanied by Ru-promoted combustion of organic material and led to crystalline (anatase) TiO 2 and Ti x Ru 1-x O 2 solid solution (rutile phase)

  4. Effect of TiO_2 Loading on Pt-Ru Catalysts During Alcohol Electrooxidation

    International Nuclear Information System (INIS)

    Hasa, Bjorn; Kalamaras, Evangelos; Papaioannou, Evangelos I.; Vakros, John; Sygellou, Labrini; Katsaounis, Alexandros

    2015-01-01

    Highlights: • TiO_2 can be used to modify Pt-Ru based electrodes for alcohol oxidation. • TiO_2 modified electrodes with lower amount of metals had higher active surface area than pure Pt-Ru electrodes. • TiO_2 modified electrodes showed comparable performance with pure Pt-Ru electrode both in a single cell and in a PEM fuel cell under alcohol fuelling. - Abstract: In this study, Pt-Ru based electrodes modified by TiO_2 were prepared by means of thermal decomposition of chloride and isopropoxide precursors on Ti substrates, characterised by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), X-ray Photoelectron Spectroscopy (XPS), electrochemical techniques and CO stripping and used as anodes for alcohol oxidation. The minimization of the metal loading without electrocatalytic activity losses was also explored. TiO_2 was chosen due to its chemical stability, low cost and excellent properties as substrate for metal dispersion. It was found that TiO_2 loading up to 50% results in a 3-fold increase of the Electrochemically Active Surface (EAS). This conclusion has been confirmed by CO stripping experiments. All samples have been evaluated during the electrochemical oxidation of methanol, ethanol and glycerol. In all cases, the Pt_2_5-Ru_2_5-(TiO_2)_5_0 electrode had better electrocatalytic activity than the pure Pt_5_0-Ru_5_0 anode. The best modified electrode, (Pt_2_5-Ru_2_5-(TiO_2)_5_0), was also evaluated as anode in a PEM fuel cell under methanol fuelling conditions. The observed higher performance of the TiO_2 modified electrodes was attributed to the enhanced Pt-Ru dispersion as well as the formation of smaller Pt and Ru particles.

  5. Adsorption and Recovery of Polyphenolic Flavonoids Using TiO_2-Functionalized Mesoporous Silica Nanoparticles

    International Nuclear Information System (INIS)

    Khan, M. Arif; Wallace, William T.; Islam, Syed Z.; Nagpure, Suraj; Strzalka, Joseph

    2017-01-01

    Exploiting specific interactions with titania (TiO_2) has been proposed for the separation and recovery of a broad range of biomolecules and natural products, including therapeutic polyphenolic flavonoids which are susceptible to degradation, such as quercetin. Functionalizing mesoporous silica with TiO_2 has many potential advantages over bulk and mesoporous TiO_2 as an adsorbent for natural products, including robust synthetic approaches leading to high surface area, stable separation platforms. Here, TiO_2 surface functionalized mesoporous silica nanoparticles (MSNPs) are synthesized and characterized as a function of TiO_2 content (up to 636 mg TiO2/g). The adsorption isotherms of two polyphenolic flavonoids, quercetin and rutin, were determined (0.05-10 mg/ml in ethanol), and a 100-fold increase in the adsorption capacity was observed relative to functionalized nonporous particles with similar TiO_2 surface coverage. An optimum extent of functionalization (approximately 440 mg TiO_2/g particles) is interpreted from characterization techniques including grazing incidence x-ray scattering (GIXS), high resolution transmission electron microscopy (HRTEM) and nitrogen adsorption, which examined the interplay between the extent of TiO_2 functionalization and the accessibility of the porous structures. The recovery of flavonoids is demonstrated using ligand displacement in ethanolic citric acid solution (20% w/v), in which greater than 90% recovery can be achieved in a multistep extraction process. The radical scavenging activity (RSA) of the recovered and particle-bound quercetin as measured by 2,2-diphenyl-1-picrylhydrazyl (DPPH) radical scavenging assay demonstrates greater than 80% retention of antioxidant activity by both particle-bound and recovered quercetin. In conclusion, these mesoporous titanosilicate materials can serve as a synthetic platform to isolate, recover, and potentially deliver degradation-sensitive natural products to biological systems.

  6. TiO2-BASED Composite Films for the Photodegradation of Oxytetracycline

    Science.gov (United States)

    Li, Hui; Guan, Ling-Xiao; Feng, Ji-Jun; Li, Fang; Yao, Ming-Ming

    2015-02-01

    The spread of the antibiotic oxytetracycline (OTC) has been thought as a threat to the safety of drinking water. In this paper, the photocatalytic activity of the nanocrystalline Fe/Ca co-doped TiO2-SiO2 composite film for the degradation of OTC was studied. The films were characterized by field emission scanning electron microscopy (FE-SEM) equipped with energy-dispersive spectroscopy (EDS), N2 adsorption/desorption isotherms, photoluminescence (PL) spectra, and UV-Vis diffraction reflectance absorption spectra (DRS). The FE-SEM results indicated that the Fe/Ca co-doped TiO2-SiO2 film was composed of smaller nanoparticles compared to pure TiO2 or TiO2-SiO2 film. The BET surface area results showed that the specific surface area of the pure TiO2, TiO2-SiO2 and Ca2+/Fe3+ co-doped TiO2-SiO2 is 118.3 m2g-1, 294.3 m2g-1 and 393.7 m2g-1, respectively. The DRS and PL spectra revealed that the Fe/Ca co-doped TiO2-SiO2 film had strong visible light adsorption and diminished electrons/holes recombination. Experimental results showed that the Fe/Ca co-doped TiO2-SiO2 film is effective in the degradation of OTC under both UV and visible light irradiation.

  7. Preparation, Characterization and Analysis of Fouling Mechanisms of TiO2- Embedded PVDF Membranes

    Directory of Open Access Journals (Sweden)

    Yoones Jafarzadeh

    2017-01-01

    Full Text Available Titanium dioxide (TiO2-embedded polyvinylidene fluoride (PVDF mixed matrix membranes were prepared through a nonsolvent induced phase separation (NIPS method. The structure of the membranes was characterized by FESEM, EDX, water drop contact angle measurement, pure water flux and mean pore radius analysis. The results showed that the prepared membranes had asymmetric structures with macro-voids and the presence of TiO2 nanoparticles increased the size of macro-voids. Moreover, pure water flux increased from 41 kg/m2h to 162 kg/m2h the content of TiO2 nanoparticles increased from 1 wt% to 5 wt% as embedded membrane. The contact angle dropped from 100° for 1 wt% TiO2- embedded membrane to 69° for 5 wt% TiO2-embedded membrane, showing that the hydrophilicity of membranes increased by addition of inorganic TiO2 nanoparticles. The fouling behavior oftheprepared mixed matrix membranes was studied in filtration process of 1% humic acid solution. The results showed that fouling resistance of the membranes increased with higher content of TiO2 nanoparticles. The results of classic fouling modeling of membranes showed that for 2 and 5 wt% TiO2-embedded membranes the best fit of the data occurred with the intermediate blockage model whereas cake formation model was the dominant mechanism for other membranes. Moreover, the analysis of fouling mechanisms by combined models showed that cake filtration-intermediate blockage model was in good agreement with the experimental data for all membranes. Finally, the results showed that the rejection of membranes increased with the addition of TiO2 nanoparticles, and then decreased.

  8. Synthesis and photocatalytic activity of mesoporous – (001) facets TiO_2 single crystals

    International Nuclear Information System (INIS)

    Dong, Yeshuo; Fei, Xuening; Zhou, Yongzhu

    2017-01-01

    Highlights: • The (001) facets of TiO_2 single crystals with mesoporous structure. • The (010) and (100) facets of TiO_2 single crystals were covered by the flower – shaped TiO_2 crystals. • This special structure could promote charge separation and provide more active sites, which will lead to a substantial increase in photocatalytic activity. - Abstract: In this work, the mesoporous – (001) facets TiO_2 single crystals have been successfully synthesized through a two-step solvothermal route without any template. Their structure and morphology were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), ultraviolet-visible (UV–vis) diffuse reflectance spectroscopy and energy dispersive X-ray spectrometer (EDX). Based on the different characteristics and atomic arrangements on each facet of anatase TiO_2 single crystals, we synthesized these mesoporous – (001) facets TiO_2 single crystals by controlling the interaction characteristics of hydrofluoric acid (HF) and isopropanol (i-PrOH) on the crystal facets. It can been seen that the (001) facets of these as-synthesized TiO_2 single crystals have a clear mesoporous structure through the SEM images and BET methods. Moreover, the other four facets were covered by the flower – shaped TiO_2 crystals with the generation of the mesoporous – (001) facets. This special and interesting morphology could promote charge separation and provide more active sites, which will lead to a substantial increase in photocatalytic activity. Moreover, it is more intuitive to reflect that the different crystal facets possess the different properties due to their atomic arrangement. Besides, according to the different synthetic routes, we proposed and discussed a plausible synthesis mechanism of these mesoporous – (001) facets TiO_2 single crystals.

  9. Preparation and Characterization of Nano-Sized TiO2@Chitosan for Bone Tissue Engineering

    Directory of Open Access Journals (Sweden)

    Lei JIANG

    2016-12-01

    Full Text Available Background: With the development of genetic engineering, it is urgent to find a vector with high transfection efficiency and good biocompatibility for genes. We considered combining nano-TiO2 with chitosan (CTS in order to tap their respective advantages to make a better new nanoparticle as gene vector.Methods: TiO2@CTS was prepared using microemulsion method. The physicochemical property of TiO2@CTS was measured by transmission electron microscopy (TEM and zeta potential. The safety and influence on MC3T3-E1 cells were detected by methyl thiazolyl tetrazolium (MTT, blood compatibility assay and flow cytometry.Results: TiO2@CTS was well prepared and it was safe to cells under concentration tests. TiO2@CTS particles had a fuzzy boundary with a particle size remaining in 20-30 nm. Besides, the results also showed that TiO2@CTS did better in cellular uptake than TiO2 at 2 h and 24 h, and had good biocompatibility. MTT assay proved that the MC3T3 cells remained good growth when treated with different concentrations of TiO2@CTS (2.5, 5, 10, 20, 40 and 80 μg/mL. Moreover, transfection assay in vitro and electrophoretic mobility shift assay illustrated the high transfection efficiency of TiO2@CTS.Conclusion: TiO2@CTS is a good choice to gene transfection, with good biocompatibility, and it also provides a new thought for the application of nanotechnology in the field of aveolar bone graft material.

  10. A self-cleaning coating based on commercial grade polyacrylic latex modified by TiO2/Ag-exchanged-zeolite-A nanocomposite

    Science.gov (United States)

    Nosrati, Rahimeh; Olad, Ali; Nofouzi, Katayoon

    2015-08-01

    The commercial grade polyacrylic latex was modified in order to prepare a self-cleaning coating. TiO2/Ag-exchanged-zeolite-A nanocomposite was prepared and used as additive in the matrix of polyacrylic latex to achieve a hydrophilic and photocatalytic coating. FTIR and UV-visible spectroscopy, X-ray diffraction patterns and FESEM were used to characterize the composition and structure of the nanocomposites and coatings. The acrylic coatings, were prepared by using of TiO2/Ag-exchanged-zeolite-A additive, had better UV and visible light absorption, hydrophilic, degradation of organic pollutants, stability in water and antimicrobial properties than pristine commercial grade polyacrylic latex coating. According to the results, the modified polyacrylic based coating containing 0.5 wt% of TiO2/Ag-exchanged-zeolite-A nanocomposite additive with TiO2 to Ag-exchanged-zeolite-A ratio of 1:2 was the best coating considering most of useful properties such as small band gap and low water contact angle. The water contact angle for unmodified polyacrylic latex coating was 68° which was decreased to less than 10° in modified coating after 24 h LED lamp illumination.

  11. Synthesis and characterization of Ag-doped TiO2 nanotubes on Ti-6Al-4V and Ti-6Al-7Nb alloy

    Science.gov (United States)

    Ulfah, Ika Maria; Bachtiar, Boy M.; Murnandityas, Arnita Rut; Slamet

    2018-05-01

    The present paper is focused on comparative behavior of nanotubes growth on Ti-6Al-4V and Ti-6Al-7Nb alloy using electrochemical anodization method. These alloys were anodized in electrolytes solution containing glycerol, water and 0.5wt.% of NH4F. Silver-doped TiO2 nanotubes were synthesized using photo-assisted deposition (PAD) at various Ag loading concentration in 0.05 M, 0.10 M, and 0.15 M. The phase composition and morphological characteristics were investigated by XRD and FESEM/EDX, respectively. The surface wettability was measured by contact angle meter. The results showed that TiO2 nanotubes can be grown on these surface alloys. XRD profiles revealed crystal formation of anatase, rutile and Ag on these surface alloys. According to FESEM images, the average nanotube diameter of Ti-6Al-4V alloy and Ti-6Al-7Nb alloy are 134 nm and 120 nm, respectively. EDX-Mapping analysis showed that Ag desposited over surface of TiO2 nanotubes. The surface wettability indicated hydrophilicity properties on Ti-4Al-4V alloy and Ti-6Al-7Nb alloy surface. This study may contribute to the development of silver-doped TiO2 nanotubes on Ti-6Al-4V alloy and Ti-6Al-7Nb alloy can be considered in various photocatalytic applications such as biomedical devicesdue to photocatalytic mechanism and antibacterial ability.

  12. Improved electron density through hetero-junction binary sensitized TiO2/ CdTe / D719 system as photoanode for dye sensitized solar cell

    Science.gov (United States)

    Pandey, A. K.; Ahmad, Muhammad Shakeel; Alizadeh, Mahdi; Rahim, Nasrudin Abd

    2018-07-01

    The combined effect of dual sensitization and hetero-junction symmetry has been investigated on the performance of TiO2 based dye sensitized solar cell. CdTe nanoparticles have been introduced in TiO2 matrix to function as sensitizer as well as act as hetero-junction between D719 dye and TiO2 nanoarchitecture. Four concentrations of CdTe i.e. 0.5 wt%, 2 wt%, 5 wt% and 8 wt% have been investigated. Morphological and compositional studies have been conducted using scanning electron microscope (SEM) and X-ray diffraction (XRD) respectively. Light absorption characteristics have been investigated by employing Uv-vis spectroscopy and the overall performance has been studied using solar simulator and electrochemical impedance spectroscopy (EIS). Performance has been found to be increased with the addition of CdTe due to high electron density and reduction in recombination reactions. An increase of 41.73% in incident photo conversion efficiency (IPCE) and 75.57% in short circuit current density (Jsc) have been recorded for the specimens containing 5 wt% CdTe compared to bare TiO2 based DSSCs. Further addition of CdTe leads to reduction in overall performance of DSSCs.

  13. Eosin-Y and N3-Dye sensitized solar cells (DSSCs) based on novel nanocoral TiO2: A comparative study

    International Nuclear Information System (INIS)

    Mali, Sawanta S.; Betty, C.A.; Bhosale, P.N.; Patil, P.S.

    2012-01-01

    Highlights: ► Synthesis of novel TiO 2 nanocorals by hydrothermal route. ► Comparative study of Eosin-Y and N3-Dyes. ► The efficiency of N3-Dye is 66% improved to that of Eosin-Y. ► The highest solar energy conversion efficiency 2.37% was observed for N3-Dye loaded DSSCs. - Abstract: Titanium oxide (TiO 2 ) nanocorals containing nanopolyps have been synthesized by a cost effective hydrothermal route directly on fluorine doped tin oxide (FTO) coated conducting glass substrates. The morphological features and physical properties of TiO 2 films were investigated by field-emission scanning electron microscopy, high resolution transmission electron microscopy, X-ray diffraction, Fourier transform Raman spectroscopy, room temperature photoluminescence spectroscopy and X-ray photoelectron spectroscopy. The surface morphology revealed the formation of TiO 2 corals having nanosized (30–40 nm) polyps. Further, we have studied its dye sensitized solar cell performance by using Eosin-Y and N3-Dye. The results indicate that the photoconversion efficiency of N3-Dye is 66% compared to that of Eosin-Y. The highest solar energy conversion efficiency of 2.37% was observed for N3-Dye loaded DSSCs.

  14. Investigating the solubility and cytocompatibility of CaO-Na2 O-SiO2 /TiO2 bioactive glasses.

    Science.gov (United States)

    Wren, Anthony W; Coughlan, Aisling; Smith, Courtney M; Hudson, Sarah P; Laffir, Fathima R; Towler, Mark R

    2015-02-01

    This study aims to investigate the solubility of a series of titanium (TiO2 )-containing bioactive glasses and their subsequent effect on cell viability. Five glasses were synthesized in the composition range SiO2 -Na2 O-CaO with 5 mol % of increments TiO2 substituted for SiO2 . Glass solubility was investigated with respect to (1) exposed surface area, (2) particle size, (3) incubation time, and (4) compositional effects. Ion release profiles showed that sodium (Na(+) ) presented high release rates after 1 day and were unchanged between 7 and 14 days. Calcium (Ca(2+) ) release presented a significant change at each time period and was also composition dependent, where a reduction in Ca(2+) release is observed with an increase in TiO2 concentration. Silica (Si(4+) ) release did not present any clear trends while no titanium (Ti(4+) ) was released. Cell numbers were found to increase up to 44%, compared to the growing control population, with a reduction in particle size and with the inclusion of TiO2 in the glass composition. © 2014 Wiley Periodicals, Inc.

  15. Study of Dye-Sensitized Solar Cells by Scanning Electron Micrograph Observation and Thickness Optimization of Porous TiO2 Electrodes

    Directory of Open Access Journals (Sweden)

    Seigo Ito

    2009-01-01

    Full Text Available In order to improve the photoenergy conversion efficiency of dye-sensitized solar cells (DSCs, it is important to optimize their porous TiO2 electrodes. This paper examines the surface and cross-sectional views of the electrodes using scanning electron micrography. Two types of samples for cross-sectional viewing were prepared by mechanically breaking the substrate and by using an Ar-ion etching beam. The former displays the surface of the TiO2 particles and the latter shows the cross-section of the TiO2 particles. We found interesting surface and cross-sectional structures in the scattering layer containing the 400 nm diameter particles, which have an angular and horned shape. The influence of TiO2 particle size and the thickness of the nanocrystalline-TiO2 electrode in DSCs using four kinds of sensitizing dyes (D149, K19, N719 and Z907 and two kinds of electrolytes (acetonitrile-based and ionic-liquid electrolytes are discussed in regards to conversion efficiency, which this paper aims to optimize.

  16. Liquid phase deposition of WO3/TiO2 heterojunction films with high photoelectrocatalytic activity under visible light irradiation

    International Nuclear Information System (INIS)

    Zhang, Man; Yang, Changzhu; Pu, Wenhong; Tan, Yuanbin; Yang, Kun; Zhang, Jingdong

    2014-01-01

    Highlights: • Liquid phase deposition is developed for preparing WO 3 /TiO 2 heterojunction films. • TiO 2 film provides an excellent platform for WO 3 deposition. • WO 3 expands the absorption band edge of TiO 2 film to visible light region. • WO 3 /TiO 2 heterojunction film shows high photoelectrocatalytic activity. - ABSTRACT: The heterojunction films of WO 3 /TiO 2 were prepared by liquid phase deposition (LPD) method via two-step processes. The scanning electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopic analysis indicated that flower-like WO 3 film was successfully deposited on TiO 2 film with the LPD processes. The TiO 2 film provided an excellent platform for WO 3 deposition while WO 3 obviously expanded the absorption of TiO 2 film to visible light. As the result, the heterojunction film of WO 3 /TiO 2 exhibited higher photocurrent response to visible light illumination than pure TiO 2 or WO 3 film. The photoelectrocatalytic (PEC) activity of WO 3 /TiO 2 film was evaluated by degrading Rhodamin B (RhB) and 4-chlorophenol (4-CP) under visible light irradiation. The results showed that the LPD WO 3 /TiO 2 film possessed high PEC activity for efficient removal of various refractory organic pollutants

  17. Application of nitrogen-doped TiO2 nano-tubes in dye-sensitized solar cells

    DEFF Research Database (Denmark)

    Tran, Vy Anh; Thinh Troung, Trieu; Pham Phan, Thu Anh

    2017-01-01

    Our research aimed to improve the overall energy conversion efficiency of DSCs by applying nitrogen-doped TiO2 nano-tubes (N-TNT) for the preparation of DSCs photo-anodes. The none-doped TiO2 nano-tubes (TNTs) were synthesized by alkaline hydrothermal treatment of Degussa P25 TiO2 particles in 10...

  18. Synthesis and characterization of cerium containing iron phosphate based glass-ceramics

    Science.gov (United States)

    Deng, Yi; Liao, Qilong; Wang, Fu; Zhu, Hanzhen

    2018-02-01

    The structure and properties of xCeO2-(100-x)(40Fe2O3-60P2O5), where x = 0, 2, 4, 6 and 8 mol%, glass-ceramics prepared by melting and slow cooling method have been investigated by using X-ray diffraction (XRD), scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR), differential thermal analysis (DTA) and the Product Consistency Test (PCT). The results show that the 40Fe2O3-60P2O5 sample is homogeneously amorphous and the sample containing 2 mol% CeO2 has a small amount of FePO4 phase embedded. For the sample containing up to 4 mol% CeO2, monazite CePO4 and a small amount of FePO4 appear. Spectra analysis show that the structure networks of the glass-ceramics mainly consist of orthophosphate, along with pyrophosphate and a small amount of metaphosphate units. Moreover, the leaching rates of Fe and Ce are about 3.5 × 10-5 g m-2 d-1 and 5.0 × 10-5 g m-2 d-1 respectively after immersion in deionized water at 90 °C for 56 days, indicating their good chemical durability. The conclusions imply that the prepared method may be a promising process to immobilize nuclear waste into glass-ceramic matrix.

  19. Development and Application of TiO2 Nanoparticles Coupled with Silver Halide

    Directory of Open Access Journals (Sweden)

    Xiaojia Wan

    2014-01-01

    Full Text Available Titanium dioxide (TiO2 is proposed to be effective photocatalyst for wastewater treatment, air purification, and self-cleaning ability, because of its strong oxidation and superhydrophilicity. In order to conquer the limits of TiO2, a variety of methods have been used. This paper presents a critical review of novel research and achievements in the modification of TiO2 nanoparticles with silver halide (AgX, X=Cl, Br, I, which aims at enhancing the visible light absorption and photosensitivity. Herein we study the synthesis, physical and chemical properties, and the mechanism of this composite photocatalyst.

  20. TiO2-Anatase Nanowire Dispersed Composite Electrode for Dye-Sensitized Solar Cells

    International Nuclear Information System (INIS)

    Asagoe, K; Suzuki, Y; Ngamsinlapasathian, S; Yoshikawa, S

    2007-01-01

    TiO 2 anatase nanowires have been prepared by a hydrothermal process followed by post-heat treatment in air. TiO 2 nanoparticle/TiO 2 nanowire composite electrodes were prepared for dye-sensitized solar cells (DSC) in order to improve light-to-electricity conversion efficiency. The TiO 2 NP/TiO 2 NW composite cells showed higher DSC performance than ordinary nanoparticle cells and fully nanowire cells: efficiency (η = 6.53 % for DSC with 10% nanowire, whereas 5.59% for 0% nanowire, and 2.42% for 100% nanowire