Fabrication of titanium dioxide nanotube arrays using organic electrolytes

Science.gov (United States)

Yoriya, Sorachon

This dissertation focuses on fabrication and improvement of morphological features of TiO2 nanotube arrays in the selected organic electrolytes including dimethyl sulfoxide (DMSO; see Chapter 4) and diethylene glycol (DEG; see Chapter 5). Using a polar dimethyl sulfoxide containing hydrofluoric acid, the vertically oriented TiO2 nanotube arrays with well controlled morphologies, i.e. tube lengths ranging from few microns up to 101 microm, pore diameters from 100 nm to 150 nm, and wall thicknesses from 15 nm to 50 nm were achieved. Various anodization variables including fluoride ion concentration, voltage, anodization time, water content, and reuse of the anodized electrolyte could be manipulated under proper conditions to control the nanotube array morphology. Anodization current behaviors associated with evolution of nanotube length were analyzed in order to clarify and better understand the formation mechanism of nanotubes grown in the organic electrolytes. Typically observed for DMSO electrolyte, the behavior that anodization current density gradually decreases with time is a reflection of a constant growth rate of nanotube arrays. Large fluctuation of anodization current was significantly observed probably due to the large change in electrolyte properties during anodization, when anodizing in high conductivity electrolytes such as using high HF concentration and reusing the anodized electrolyte as a second time. It is believed that the electrolyte properties such as conductivity and polarity play important role in affecting ion solvation and interactions in the solution consequently determining the formation of oxide film. Fabrication of the TiO2 nanotube array films was extended to study in the more viscous diethylene glycol (DEG) electrolyte. The arrayed nanotubes achieved from DEG electrolytes containing either HF or NH4 F are fully separated, freely self-standing structure with open pores and a wide variation of tube-to-tube spacing ranging from

Layered growth of aligned carbon nanotube arrays by pyrolysis

International Nuclear Information System (INIS)

Zhang Hongrui; Liang Erjun; Ding Pei; Chao Mingju

2003-01-01

Based on the study of reaction temperature and duration of the growth of aligned carbon nanotube arrays, layered aligned multi-wall carbon nanotube (MWNT) films grown directly around a reaction quartz tube in an Ar/H 2 atmosphere by pyrolysis of ferrocene in xylene in a suitable reaction furnace with the help of cobalt powder. The scanning electron microscope and transmission electron microscope images indicated that the obtained arrays were composed of many separated layers with MWNTs. The reaction temperature significantly influenced the alignment of the MWNTs, and an appropriate reaction temperature range for growth was 800-900 deg. C. The diameter of the carbon nanotube increased from 46 to 75 nm with the growth temperature. Besides temperature, the reaction duration influenced the length of the well-aligned carbon nanotubes. There was no significant relation between the growth time and the diameter of the carbon nanotubes in the array

Nanoindentation study of the mechanical behavior of TiO2 nanotube arrays

International Nuclear Information System (INIS)

Xu, Y. N.; Wang, M. C.; Oloyede, A.; Bell, J. M.; Yan, C.; Liu, M. N.

2015-01-01

Titanium dioxide (TiO 2 ) nanotube arrays are attracting increasing attention for use in solar cells, lithium-ion batteries, and biomedical implants. To take full advantage of their unique physical properties, such arrays need to maintain adequate mechanical integrity in applications. However, the mechanical performance of TiO 2 nanotube arrays is not well understood. In this work, we investigate the deformation and failure of TiO 2 nanotube arrays using the nanoindentation technique. We found that the load–displacement response of the arrays strongly depends on the indentation depth and indenter shape. Substrate-independent elastic modulus and hardness can be obtained when the indentation depth is less than 2.5% of the array height. The deformation mechanisms of TiO 2 nanotube arrays by Berkovich and conical indenters are closely associated with the densification of TiO 2 nanotubes under compression. A theoretical model for deformation of the arrays under a large-radius conical indenter is also proposed

Composite of TiN nanoparticles and few-walled carbon nanotubes and its application to the electrocatalytic oxygen reduction reaction

KAUST Repository

Isogai, Shunsuke; Ohnishi, Ryohji; Katayama, Masao; Kubota, Jun; Kim, Dongyoung; Noda, Suguru; Cha, Dong Kyu; Takanabe, Kazuhiro; Domen, Kazunari

2011-01-01

Nanoparticles meet nanotubes! Direct synthesis of TiN nanoparticles in a three-dimensional network of few-walled carbon nanotubes (FWCNTs) was achieved by using mesoporous graphitic carbon nitride (C 3N 4) as both a hard template and a nitrogen

Double-walled ZrO{sub 2} nanotube array. Preparation and enhanced photocatalytic activity

Energy Technology Data Exchange (ETDEWEB)

Xue, Chaorui; Hu, Shengliang; Chang, Qing; Wang, Yanzhong [School of Materials Science and Engineering, North University of China, Taiyuan (China); Yang, Jinlong [School of Materials Science and Engineering, North University of China, Taiyuan (China); School of Materials Science and Engineering, Tsinghua University, Beijing (China)

2017-11-15

This work demonstrates the formation of self-ordered double-walled ZrO{sub 2} nanotube array via electrochemical anodization in glycerol-based electrolyte. Compared with its counterpart of single-walled ZrO{sub 2} nanotube array, the tube wall of double-walled ZrO{sub 2} nanotube split into outer and inner layers for the decomposition of glycerol during anodization process. Moreover, the double-walled structure showed its advantage of achieving improved utilization of light and higher specific surface area of nanotube array. Due to the unique double-walled structure, the double-walled ZrO{sub 2} nanotube array exhibited better photocatalytic activity than the single-walled ZrO{sub 2} nanotube array. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Multiwall carbon nanotube microcavity arrays

Energy Technology Data Exchange (ETDEWEB)

Ahmed, Rajib; Butt, Haider, E-mail: h.butt@bham.ac.uk [Nanotechnology Laboratory, School of Mechanical Engineering, University of Birmingham, Birmingham B15 2TT (United Kingdom); Rifat, Ahmmed A. [Integrated Lightwave Research Group, Department of Electrical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur 50603 (Malaysia); Yetisen, Ali K.; Yun, Seok Hyun [Harvard Medical School and Wellman Center for Photomedicine, Massachusetts General Hospital, 65 Landsdowne Street, Cambridge, Massachusetts 02139 (United States); Harvard-MIT Division of Health Sciences and Technology, Massachusetts Institute of Technology, Cambridge, Massachusetts 02139 (United States); Dai, Qing [National Center for Nanoscience and Technology, Beijing 100190 (China)

2016-03-21

Periodic highly dense multi-wall carbon nanotube (MWCNT) arrays can act as photonic materials exhibiting band gaps in the visible regime and beyond terahertz range. MWCNT arrays in square arrangement for nanoscale lattice constants can be configured as a microcavity with predictable resonance frequencies. Here, computational analyses of compact square microcavities (≈0.8 × 0.8 μm{sup 2}) in MWCNT arrays were demonstrated to obtain enhanced quality factors (≈170–180) and narrow-band resonance peaks. Cavity resonances were rationally designed and optimized (nanotube geometry and cavity size) with finite element method. Series (1 × 2 and 1 × 3) and parallel (2 × 1 and 3 × 1) combinations of microcavities were modeled and resonance modes were analyzed. Higher order MWCNT microcavities showed enhanced resonance modes, which were red shifted with increasing Q-factors. Parallel microcavity geometries were also optimized to obtain narrow-band tunable filtering in low-loss communication windows (810, 1336, and 1558 nm). Compact series and parallel MWCNT microcavity arrays may have applications in optical filters and miniaturized optical communication devices.

Hierarchical TiN nanoparticles-assembled nanopillars for flexible supercapacitors with high volumetric capacitance.

Science.gov (United States)

Qin, Ping; Li, Xingxing; Gao, Biao; Fu, Jijiang; Xia, Lu; Zhang, Xuming; Huo, Kaifu; Shen, Wenli; Chu, Paul K

2018-05-10

Titanium nitride (TiN) is an attractive electrode material in fast charging/discharging supercapacitors because of its excellent conductivity. However, the low capacitance and mechanical brittleness of TiN restricts its further application in flexible supercapacitors with high energy density. Thus, it is still a challenge to rationally design TiN electrodes with both high electrochemical and mechanical properties. Herein, the hierarchical TiN nanoparticles-assembled nanopillars (H-TiN NPs) array as binder free electrodes were obtained by nitriding of hierarchical titanium dioxide (TiO2) nanopillars, which was produced by a simple hydrothermal treatment of anodic TiO2 nanotubes (NTs) array in water. The porous TiN nanoparticles connected to each other to form ordered nanopillar arrays, effectively providing larger specific surface area and more active sites for charge storage. The H-TiN NPs delivered a high volumetric capacitance of 120 F cm-3 at 0.83 A cm-3, which is better than that of TiN NTs arrays (69 F cm-3 at 0.83 A cm-3). After assembling into all-solid-state devices, the H-TiN NPs based supercapacitors exhibited outstanding volumetric capacitance of 5.9 F cm-3 at 0.02 A cm-3 and a high energy density of 0.53 mW h cm-3. Our results reveal a new strategy to optimize the supercapacitive performance of metal nitrides.

Vertically aligned carbon nanotubes for microelectrode arrays applications.

Science.gov (United States)

Castro Smirnov, J R; Jover, Eric; Amade, Roger; Gabriel, Gemma; Villa, Rosa; Bertran, Enric

2012-09-01

In this work a methodology to fabricate carbon nanotube based electrodes using plasma enhanced chemical vapour deposition has been explored and defined. The final integrated microelectrode based devices should present specific properties that make them suitable for microelectrode arrays applications. The methodology studied has been focused on the preparation of highly regular and dense vertically aligned carbon nanotube (VACNT) mat compatible with the standard lithography used for microelectrode arrays technology.

Influence of anodization parameters on the morphology of TiO 2 nanotube arrays

Science.gov (United States)

Omidvar, Hamid; Goodarzi, Saba; Seif, Ahmad; Azadmehr, Amir R.

2011-07-01

TiO 2 nanotube arrays can be fabricated by electrochemical anodization in organic and inorganic electrolytes. Morphology of these nanotube arrays changes when anodization parameters such as applied voltage, type of electrolyte, time and temperature are varied. Nanotube arrays fabricated by anodization of commercial titanium in electrolytes containing NH 4F solution and either sulfuric or phosphoric acid were studied at room temperature; time of anodization was kept constant. Applied voltage, fluoride ion concentration, and acid concentrations were varied and their influences on TiO 2 nanotubes were investigated. The current density of anodizing was recorded by computer controlled digital multimeter. The surface morphology (top-view) of nanotube arrays were observed by SEM. The nanotube arrays in this study have inner diameters in range of 40-80 nm.

Aligned Carbon Nanotubes Array by DC Glow Plasma Etching for Supercapacitor

Directory of Open Access Journals (Sweden)

Yongfeng Luo

2013-01-01

Full Text Available To open the end of carbon nanotubes and make these ends connect with functional carboxyl group, aligned carbon nanotubes (CNTs arrays was etched by DC glow oxygen-argon plasma. With these open-ended carbon nanotubes array as electrode materials to build supercapacitor, we found that the capacity (32.2 F/g increased significantly than that of pure carbon nanotubes (6.7 F/g.

Mo-Co catalyst nanoparticles: Comparative study between TiN and Si surfaces for single-walled carbon nanotube growth

Energy Technology Data Exchange (ETDEWEB)

Morant, C., E-mail: c.morant@uam.es [Departamento de Fisica Aplicada, C-XII, Universidad Autonoma de Madrid, Cantoblanco, 28049 Madrid (Spain); Campo, T. [Departamento de Fisica Aplicada, C-XII, Universidad Autonoma de Madrid, Cantoblanco, 28049 Madrid (Spain); Marquez, F. [School of Science and Technology, University of Turabo, 00778-PR (United States); Domingo, C. [Instituto de Estructura de la Materia, CSIC, Serrano 123, 28006 Madrid (Spain); Sanz, J.M.; Elizalde, E. [Departamento de Fisica Aplicada, C-XII, Universidad Autonoma de Madrid, Cantoblanco, 28049 Madrid (Spain)

2012-06-01

Highly pure single-walled carbon nanotubes (SWNT) were synthesized by alcohol catalytic chemical vapor deposition on silicon substrates partially covered by a thin layer of TiN. The TiN coating selectively prevented the growth of carbon nanotubes. Field emission scanning electron microscopy and Raman spectroscopy revealed the formation of high purity vertically aligned SWNT in the Si region. X-ray Photoelectron Spectroscopy and Atomic Force Microscopy indicated that Co nanoparticles are present on the Si regions, and not on the TiN regions. This clearly explains the obtained experimental results: the SWNT only grow where the Co is presented as nanoparticles, i.e. on the Si regions. - Highlights: Black-Right-Pointing-Pointer Single-wall carbon nanotubes (SWNT) ontained by catalytic chemical vapor-deposition. Black-Right-Pointing-Pointer Substrate/Co-Mo catalyst behaviour plays a key role in the SWNT growth. Black-Right-Pointing-Pointer Co nanoparticles (the effective catalyst) have been only observed on the Si region. Black-Right-Pointing-Pointer High purity SWNT were spatially confined in specific locations (Si regions). Black-Right-Pointing-Pointer TiN-coated surfaces, adjacent to a Si oxide region, prevent the growth of SWNT.

Physicochemical characteristics and droplet impact dynamics of superhydrophobic carbon nanotube arrays.

Science.gov (United States)

Aria, Adrianus I; Gharib, Morteza

2014-06-17

The physicochemical and droplet impact dynamics of superhydrophobic carbon nanotube arrays are investigated. These superhydrophobic arrays are fabricated simply by exposing the as-grown carbon nanotube arrays to a vacuum annealing treatment at a moderate temperature. This treatment, which allows a significant removal of oxygen adsorbates, leads to a dramatic change in wettability of the arrays, from mildly hydrophobic to superhydrophobic. Such change in wettability is also accompanied by a substantial change in surface charge and electrochemical properties. Here, the droplet impact dynamics are characterized in terms of critical Weber number, coefficient of restitution, spreading factor, and contact time. Based on these characteristics, it is found that superhydrophobic carbon nanotube arrays are among the best water-repellent surfaces ever reported. The results presented herein may pave a way for the utilization of superhydrophobic carbon nanotube arrays in numerous industrial and practical applications, including inkjet printing, direct injection engines, steam turbines, and microelectronic fabrication.

Nanoindentation study of the mechanical behavior of TiO{sub 2} nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Xu, Y. N.; Wang, M. C.; Oloyede, A.; Bell, J. M.; Yan, C., E-mail: c2.yan@qut.edu.au [School of Chemistry, Physics and Mechanical Engineering, Science and Engineering Faculty, Queensland University of Technology (QUT), Brisbane, Queensland 4001 (Australia); Liu, M. N. [i-Lab, Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Science, Suzhou (China)

2015-10-14

Titanium dioxide (TiO{sub 2}) nanotube arrays are attracting increasing attention for use in solar cells, lithium-ion batteries, and biomedical implants. To take full advantage of their unique physical properties, such arrays need to maintain adequate mechanical integrity in applications. However, the mechanical performance of TiO{sub 2} nanotube arrays is not well understood. In this work, we investigate the deformation and failure of TiO{sub 2} nanotube arrays using the nanoindentation technique. We found that the load–displacement response of the arrays strongly depends on the indentation depth and indenter shape. Substrate-independent elastic modulus and hardness can be obtained when the indentation depth is less than 2.5% of the array height. The deformation mechanisms of TiO{sub 2} nanotube arrays by Berkovich and conical indenters are closely associated with the densification of TiO{sub 2} nanotubes under compression. A theoretical model for deformation of the arrays under a large-radius conical indenter is also proposed.

Photoelectrocatalytic properties of Ag nanoparticles loaded TiO2 nanotube arrays prepared by pulse current deposition

International Nuclear Information System (INIS)

Xie Kunpeng; Sun Lan; Wang Chenglin; Lai Yuekun; Wang Mengye; Chen Hongbo; Lin Changjian

2010-01-01

A pulse current deposition technique was adopted to construct highly dispersed Ag nanoparticles on TiO 2 nanotube arrays which were prepared by the electrochemical anodization. The morphology, crystallinity, elemental composition, and UV-vis absorption of Ag/TiO 2 nanotube arrays were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and diffuse reflectance spectra (DRS). In particular, the photoelectrochemical properties and photoelectrocatalytic activity under UV light irradiation and the photocatalytic activity under visible light irradiation for newly synthesized Ag/TiO 2 nanotube arrays were investigated. The maximum incident photon to charge carrier efficiency (IPCE) value of Ag/TiO 2 nanotube arrays was 51%, much higher than that of pure TiO 2 nanotube arrays. Ag/TiO 2 nanotube arrays exhibited higher photocatalytic activities than the pure TiO 2 nanotube arrays under both UV and visible light irradiation. The photoelectrocatalytic activity of Ag/TiO 2 nanotube arrays under UV light irradiation was 1.6-fold enhancement compared with pure TiO 2 nanotube arrays. This approach can be used in synthesizing various metal-loaded nanotube arrays materials.

Ordered metal nanotube arrays fabricated by PVD.

Science.gov (United States)

Marquez, F; Morant, C; Campo, T; Sanz, J M; Elizalde, E

2010-02-01

In this work we report a simple method to fabricate ordered arrays of metal nanotubes. This method is based on the deposition of a metal by PVD onto an anodized aluminum oxide (AAO) template. The dimensions of the synthesized nanotubes depend both on the AAO template and on the deposited metal. In fact, it is observed that the aspect ratios of the nanotubes clearly depend significantly on the metal, ranging from 0.6 (Fe) to at least 3 (Zr).

Biophotofuel cell anode containing self-organized titanium dioxide nanotube array

Energy Technology Data Exchange (ETDEWEB)

Gan, Yong X., E-mail: yong.gan@utoledo.edu [Mechanical, Industrial and Manufacturing Engineering, College of Engineering, University of Toledo, 2801 W Bancroft Street, Toledo, OH 43606 (United States); Gan, Bo J. [Ottawa Hills High School, 2532 Evergreen Road, Toledo, OH 43606 (United States); Su Lusheng [Mechanical, Industrial and Manufacturing Engineering, College of Engineering, University of Toledo, 2801 W Bancroft Street, Toledo, OH 43606 (United States)

2011-09-15

Graphical abstract: Highlights: {center_dot} A photoactive anode containing highly ordered TiO{sub 2} nanotube array was made and the formation mechanism of self-organized TiO{sub 2} nanotube array on Ti was revealed. {center_dot} Effect of electrolyte concentration and voltage on the size distribution of the nanotubes was investigated. {center_dot} Self-organized TiO{sub 2} nanotube array anode possesses good photo-catalytic behavior of biomass decomposition under ultraviolet (UV) radiation. {center_dot} The fuel cell generates electricity and hydrogen via photoelectrochemical decomposition of ethanol, apple vinegar, sugar and tissue paper. - Abstract: We made a biophotofuel cell consisting of a titanium dioxide nanotube array photosensitive anode for biomass decomposition, and a low-hydrogen overpotential metal, Pt, as the cathode for hydrogen production. The titanium dioxide nanotubes (TiO{sub 2} NTs) were prepared via electrochemical oxidation of pure Ti in NaF solutions. Scanning electron microscopy was used to analyze the morphology of the nanotubes. The average diameter, wall thickness and length of the as-prepared TiO{sub 2} NTs were 88 {+-} 16 nm, 10 {+-} 2 nm and 491 {+-} 56 nm, respectively. Such dimensions are affected by the NaF concentration and the applied voltage during processing. Higher NaF concentrations result in the formation of longer and thicker nanotubes. The higher the voltage is, the thicker the nanotubes. The photosensitive anode made from the highly ordered TiO{sub 2} NTs has good photo-catalytic property, as can be seen from the test results of ethanol, apple vinegar, sugar and tissue paper decomposition under ultraviolet (UV) radiation. It is concluded that the biophotofuel cell with the TiO{sub 2} nanotube photoanode and a Pt cathode can generate electricity, hydrogen and clean water depending on the pH value and the oxygen presence in the solutions.

Electrochemical properties of Ti3+ doped Ag-Ti nanotube arrays coated with hydroxyapatite

Science.gov (United States)

Zhang, Hangzhou; Shi, Xiaoguo; Tian, Ang; Wang, Li; Liu, Chuangwei

2018-04-01

Ag-Ti nanotube array was prepared by simple anodic oxidation method and uniform hydroxyapatite were electrochemically deposited on the nanotubes, and then characterized by SEM, XRD, XPS and EIS. In order to investigate the influence of Ti3+ on the electrochemical deposition of hydroxyapatite on the nanotubes, the Ag-Ti nanotube array self-doped with Ti3+ was prepared by one step reduction method. The experiment results revealed that the Ti3+ can promote the grow rate of hydroxyapatite coatings on nanotube surface. The hydroxyapatite coated Ag-Ti nanotube arrays with Ti3+ exhibit excellent stability and higher corrosion resistance. Moreover, the compact and dense hydroxyapatite coating can also prevent the Ag atom erosion from the Ag-Ti nanotube.

MnO{sub 2} nanotube and nanowire arrays by electrochemical deposition for supercapacitors

Energy Technology Data Exchange (ETDEWEB)

Xia, Hui; Feng, Jinkui; Wang, Hailong; Lai, Man On; Lu, Li [Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, Singapore 117576 (Singapore)

2010-07-01

Highly ordered MnO{sub 2} nanotube and nanowire arrays are successfully synthesized via a electrochemical deposition technique using porous alumina templates. The morphologies and microstructures of the MnO{sub 2} nanotube and nanowire arrays are investigated by field emission scanning electron microscopy and transmission electron microscopy. Electrochemical characterization demonstrates that the MnO{sub 2} nanotube array electrode has superior capacitive behaviour to that of the MnO{sub 2} nanowire array electrode. In addition to high specific capacitance, the MnO{sub 2} nanotube array electrode also exhibits good rate capability and good cycling stability, which makes it promising candidate for supercapacitors. (author)

Anodic Fabrication of Ti-Ni-O Nanotube Arrays on Shape Memory Alloy

Directory of Open Access Journals (Sweden)

Qiang Liu

2014-04-01

Full Text Available Surface modification with oxide nanostructures is one of the efficient ways to improve physical or biomedical properties of shape memory alloys. This work reports a fabrication of highly ordered Ti-Ni-O nanotube arrays on Ti-Ni alloy substrates through pulse anodization in glycerol-based electrolytes. The effects of anodization parameters and the annealing process on the microstructures and surface morphology of Ti-Ni-O were studied using scanning electron microscope and Raman spectroscopy. The electrolyte type greatly affected the formation of nanotube arrays. A formation of anatase phase was found with the Ti-Ni-O nanotube arrays annealed at 450 °C. The oxide nanotubes could be crystallized to rutile phase after annealing treatment at 650 °C. The Ti-Ni-O nanotube arrays demonstrated an excellent thermal stability by keeping their nanotubular structures up to 650 °C.

A Palladium-Tin Modified Microband Electrode Array for Nitrate Determination

Directory of Open Access Journals (Sweden)

Yexiang Fu

2015-09-01

Full Text Available A microband electrode array modified with palladium-tin bimetallic composite has been developed for nitrate determination. The microband electrode array was fabricated by Micro Electro-Mechanical System (MEMS technique. Palladium and tin were electrodeposited successively on the electrode, forming a double-layer structure. The effect of the Pd-Sn composite was investigated and its enhancement of catalytic activity and lifetime was revealed. The Pd-Sn modified electrode showed good linearity (R2 = 0.998 from 1 mg/L to 20 mg/L for nitrate determination with a sensitivity of 398 μA/(mg∙L−1∙cm2. The electrode exhibited a satisfying analytical performance after 60 days of storage, indicating a long lifetime. Good repeatability was also displayed by the Pd-Sn modified electrodes. The results provided an option for nitrate determination in water.

Inherent-opening-controlled pattern formation in carbon nanotube arrays

International Nuclear Information System (INIS)

Huang Xiao; Zhou, Jijie J; Sansom, Elijah; Gharib, Morteza; Haur, Sow Chorng

2007-01-01

We have introduced inherent openings into densely packed carbon nanotube arrays to study self-organized pattern formation when the arrays undergo a wetting-dewetting treatment from nanotube tips. These inherent openings, made of circular or elongated hollows in nanotube mats, serve as dewetting centres, from where liquid recedes from. As the dewetting centres initiate dry zones and the dry zones expand, surrounding nanotubes are pulled away from the dewetting centres by liquid surface tension. Among short nanotubes, the self-organized patterns are consistent with the shape of the inherent openings, i.e. slender openings lead to elongated trench-like structures, and circular holes result in relatively round nest-like arrangements. Nanotubes in a relatively high mat are more connected, like in an elastic body, than those in a short mat. Small cracks often initialize themselves in a relatively high mat, along two or more adjacent round openings; each of the cracks evolves into a trench as liquid dries up. Self-organized pattern control with inherent openings needs to initiate the dewetting process above the nanotube tips. If there is no liquid on top, inherent openings barely enlarge themselves after the wetting-dewetting treatment

Indium tin oxide-rod/single walled carbon nanotube based transparent electrodes for ultraviolet light-emitting diodes

International Nuclear Information System (INIS)

Yun, Min Ju; Kim, Hee-Dong; Kim, Kyeong Heon; Sung, Hwan Jun; Park, Sang Young; An, Ho-Myoung; Kim, Tae Geun

2013-01-01

In this paper, we report a transparent conductive oxide electrode scheme working for ultraviolet light-emitting diodes based on indium tin oxide (ITO)-rod and a single walled carbon nanotube (SWCNT) layer. We prepared four samples with ITO-rod, SWCNT/ITO-rod, ITO-rod/SWCNT, and SWCNT/ITO-rod/SWCNT structures for comparison. As a result, the sample with SWCNT/ITO-rod/SWCNT structures showed the highest transmittance over 90% at 280 nm and the highest Ohmic behavior (with sheet resistance of 5.33 kΩ/□) in the current–voltage characteristic curves. - Highlights: • Transparent conductive oxide (TCO) electrodes are proposed for UV light-emitting diodes. • These TCO electrodes are based on evaporated indium tin oxide (ITO)-rods. • Single walled carbon nanotube (SWCNT) layers are used as a current spreading layer. • The proposed TCO electrode structures show more than 90% transmittance at 280 nm

Embedded arrays of vertically aligned carbon nanotube carpets and methods for making them

Science.gov (United States)

Kim, Myung Jong; Nicholas, Nolan Walker; Kittrell, W. Carter; Schmidt, Howard K.

2015-06-30

According to some embodiments, the present invention provides a system and method for supporting a carbon nanotube array that involve an entangled carbon nanotube mat integral with the array, where the mat is embedded in an embedding material. The embedding material may be depositable on a carbon nanotube. A depositable material may be metallic or nonmetallic. The embedding material may be an adhesive material. The adhesive material may optionally be mixed with a metal powder. The embedding material may be supported by a substrate or self-supportive. The embedding material may be conductive or nonconductive. The system and method provide superior mechanical and, when applicable, electrical, contact between the carbon nanotubes in the array and the embedding material. The optional use of a conductive material for the embedding material provides a mechanism useful for integration of carbon nanotube arrays into electronic devices.

Piezoelectric Nanotube Array for Broadband High-Frequency Ultrasonic Transducer.

Science.gov (United States)

Liew, Weng Heng; Yao, Kui; Chen, Shuting; Tay, Francis Eng Hock

2018-03-01

Piezoelectric materials are vital in determining ultrasonic transducer and imaging performance as they offer the function for conversion between mechanical and electrical energy. Ultrasonic transducers with high-frequency operation suffer from performance degradation and fabrication difficulty of the demanded piezoelectric materials. Hence, we propose 1-D polymeric piezoelectric nanostructure with controlled nanoscale features to overcome the technical limitations of high-frequency ultrasonic transducers. For the first time, we demonstrate the integration of a well-aligned piezoelectric nanotube array to produce a high-frequency ultrasonic transducer with outstanding performance. We find that nanoconfinement-induced polarization orientation and unique nanotube structure lead to significantly improved piezoelectric and ultrasonic transducing performance over the conventional piezoelectric thin film. A large bandwidth, 126% (-6 dB), is achieved at high center frequency, 108 MHz. Transmission sensitivity of nanotube array is found to be 46% higher than that of the monolithic thin film transducer attributed to the improved electromechanical coupling effectiveness and impedance match. We further demonstrate high-resolution scanning, ultrasonic imaging, and photoacoustic imaging using the obtained nanotube array transducers, which is valuable for biomedical imaging applications in the future.

Real-time imaging of vertically aligned carbon nanotube array growth kinetics

International Nuclear Information System (INIS)

Puretzky, A A; Eres, G; Rouleau, C M; Ivanov, I N; Geohegan, D B

2008-01-01

In situ time-lapse photography and laser irradiation are applied to understand unusual coordinated growth kinetics of vertically aligned carbon nanotube arrays including pauses in growth, retraction, and local equilibration in length. A model is presented which explains the measured kinetics and determines the conditions for diffusion-limited growth. Laser irradiation of the growing nanotube arrays is first used to prove that the nanotubes grow from catalyst particles at their bases, and then increase their growth rate and terminal lengths

Magnetization Reversal Mechanism for CoFeB Ferromagnetic Nanotube Arrays

International Nuclear Information System (INIS)

Hai-Rui, Liu; Qing-Feng, Lu; Shamaila, S.; Jun-Yang, Chen; Sharif, R.; Xiu-Feng, Han

2009-01-01

CoFeB nanotube arrays are fabricated in anodic aluminum oxide (AAO) membranes and track etched polycarbonate (PCTE) membranes by using an electrochemical method, and their magnetic properties are investigated by vibrating sample magnetometry. The coercivity H c and remanent squareness S Q of these CoFeB nanotube arrays are derived from hysteresis loops as a function of angle between the field and tube axis. The H c (θ) curves for CoFeB nanotube arrays in AAO and PCTE membranes show M-type variation, while they change shape from M to mountain-type as the tube length increases. However, the overall easy axis perpendicular to tube axis does not change with tube length. The different angular dependences are attributed to different magnetization reversal mechanisms. (condensed matter: electronicstructure, electrical, magnetic, and opticalproperties)

TiO2 nanotube formation by Ti film anodization and their transport properties for dye-sensitized solar cells

NARCIS (Netherlands)

Iraj, M.; Kolahdouz, M.; Asl-Soleimani, E.; Esmaeili, E.; Kolahdouz Esfahani, Z.

2016-01-01

In this paper, we present the synthesis of TiO2 nanotube (NT) arrays formed by anodization of Ti film deposited on a fluorine-doped tin oxide-coated glass substrate by direct current magnetron sputtering. NH4F/ethylene glycol electrolyte was used to demonstrate the growth of stable nanotubes at room

Room temperature synthesis of indium tin oxide nanotubes with high precision wall thickness by electroless deposition

Directory of Open Access Journals (Sweden)

Mario Boehme

2011-02-01

Full Text Available Conductive nanotubes consisting of indium tin oxide (ITO were fabricated by electroless deposition using ion track etched polycarbonate templates. To produce nanotubes (NTs with thin walls and small surface roughness, the tubes were generated by a multi-step procedure under aqueous conditions. The approach reported below yields open end nanotubes with well defined outer diameter and wall thickness. In the past, zinc oxide films were mostly preferred and were synthesized using electroless deposition based on aqueous solutions. All these methods previously developed, are not adaptable in the case of ITO nanotubes, even with modifications. In the present work, therefore, we investigated the necessary conditions for the growth of ITO-NTs to achieve a wall thickness of around 10 nm. In addition, the effects of pH and reductive concentrations for the formation of ITO-NTs are also discussed.

Self-assembled ordered carbon-nanotube arrays and membranes.

Energy Technology Data Exchange (ETDEWEB)

Overmyer, Donald L.; Siegal, Michael P.; Yelton, William Graham

2004-11-01

Imagine free-standing flexible membranes with highly-aligned arrays of carbon nanotubes (CNTs) running through their thickness. Perhaps with both ends of the CNTs open for highly controlled nanofiltration? Or CNTs at heights uniformly above a polymer membrane for a flexible array of nanoelectrodes or field-emitters? How about CNT films with incredible amounts of accessible surface area for analyte adsorption? These self-assembled crystalline nanotubes consist of multiple layers of graphene sheets rolled into concentric cylinders. Tube diameters (3-300 nm), inner-bore diameters (2-15 nm), and lengths (nanometers - microns) are controlled to tailor physical, mechanical, and chemical properties. We proposed to explore growth and characterize nanotube arrays to help determine their exciting functionality for Sandia applications. Thermal chemical vapor deposition growth in a furnace nucleates from a metal catalyst. Ordered arrays grow using templates from self-assembled hexagonal arrays of nanopores in anodized-aluminum oxide. Polymeric-binders can mechanically hold the CNTs in place for polishing, lift-off, and membrane formation. The stiffness, electrical and thermal conductivities of CNTs make them ideally suited for a wide-variety of possible applications. Large-area, highly-accessible gas-adsorbing carbon surfaces, superb cold-cathode field-emission, and unique nanoscale geometries can lead to advanced microsensors using analyte adsorption, arrays of functionalized nanoelectrodes for enhanced electrochemical detection of biological/explosive compounds, or mass-ionizers for gas-phase detection. Materials studies involving membrane formation may lead to exciting breakthroughs in nanofiltration/nanochromatography for the separation of chemical and biological agents. With controlled nanofilter sizes, ultrafiltration will be viable to separate and preconcentrate viruses and many strains of bacteria for 'down-stream' analysis.

Visible Light Photoelectrochemical Properties of N-Doped TiO2 Nanorod Arrays from TiN

Directory of Open Access Journals (Sweden)

Zheng Xie

2013-01-01

Full Text Available N-doped TiO2 nanorod arrays (NRAs were prepared by annealing the TiN nanorod arrays (NRAs which were deposited by using oblique angle deposition (OAD technique. The TiN NRAs were annealed at 330°C for different times (5, 15, 30, 60, and 120 min. The band gaps of annealed TiN NRAs (i.e., N-doped TiO2 NRAs show a significant variance with annealing time, and can be controlled readily by varying annealing time. All of the N-doped TiO2 NRAs exhibit an enhancement in photocurrent intensity in visible light compared with that of pure TiO2 and TiN, and the one annealed for 15 min shows the maximum photocurrent intensity owning to the optimal N dopant concentration. The results show that the N-doped TiO2 NRAs, of which the band gap can be tuned easily, are a very promising material for application in photocatalysis.

Preparation of FeS2 nanotube arrays based on layer-by-layer assembly and their photoelectrochemical properties

International Nuclear Information System (INIS)

Wang, Mudan; Xue, Dongpeng; Qin, Haiying; Zhang, Lei; Ling, Guoping; Liu, Jiabin; Fang, Youtong; Meng, Liang

2016-01-01

Graphical abstract: - Highlights: • Amorphous Fe 2 O 3 nanotube arrays are prepared via layer-by-layer assembly. • Pyrite FeS 2 nanotube arrays are obtained by sulfurizing Fe 2 O 3 nanotube arrays. • Various electrochemical properties are characterized. • A comparison between FeS 2 nanotube and nanoparticle films is conducted. • Nanotube arrays show enhanced corrosion resistance and photoresponse. - Abstract: Well-aligned one-dimensional iron pyrite FeS 2 nanotube arrays have been fabricated via layer-by-layer assembly technique on ZnO nanorod arrays in combination with subsequent sulfurization. The as-prepared products were confirmed to be pure phase pyrite FeS 2 with Fe/S ratio approaching 1/2. Typical nanotube structure was observed for the FeS 2 with average outer diameter of 150 ± 20 nm and wall thickness of 50 ± 5 nm. Comparisons of photoelectrochemical properties between FeS 2 nanotubes and FeS 2 nanoparticles were conducted. Tafel polarization curves and electrochemical impedance spectroscopy indicate that FeS 2 nanotubes possess high corrosion resistance and electrochemical stability. The J–V curves show that the photocurrent at 1.0 V for FeS 2 nanotubes is more than five times larger than that of FeS 2 nanoparticles, indicating enhanced photoresponse and rapid charge transfer performances of 1-D nanotube structure. The enhanced photoelectrochemical properties mainly benefit from the unique architecture features of nanotube array structure.

Capacitive performance of molybdenum nitride/titanium nitride nanotube array for supercapacitor

Energy Technology Data Exchange (ETDEWEB)

Xie, Yibing, E-mail: ybxie@seu.edu.cn; Tian, Fang

2017-01-15

Highlights: • MoN{sub x}/TiN NTA is fully converted from MoO{sub 2}/TiO{sub 2} NTA by one-step nitridation process. • MoN{sub x}/TiN NTA is used as feasible electrode material of high-performance supercapacitor. • MoN{sub x}/TiN NTA shows high capacitance, rate capability and cycling stability. - Abstract: Molybdenum nitride (MoN{sub x}) depositing on titanium nitride nanotube array (TiN NTA) was designed as MoN{sub x}/TiN NTA for supercapacitor electrode material. MoN{sub x}/TiN NTA was fabricated by electrodepositing molybdenum oxide onto titanium dioxide NTA and one-step nitridation treatment in ammonia. MoN{sub x}/TiN NTA involved top-surface layer of MoN{sub x} nanoparticles and underlying layer of TiN NTA, which contributed to electric double layer capacitance in aqueous lithium-ion electrolyte solution. The specific capacitance was increased from 69.05 mF cm{sup −2} for TiN NTA to 121.50 mF cm{sup −2} for MoN{sub x}/TiN NTA at 0.3 mA cm{sup −2}, presenting the improved capacitance performance. MoN{sub x} exhibited the capacitance of 174.83 F g{sup −1} at 1.5 A g{sup −1} and slightly declined to 109.13 F g{sup −1} at 30 A g{sup −1}, presenting high rate capability. MoN{sub x}/TiN NTA exhibited the capacitance retention ratio of 93.8% at 3.0 mA cm{sup −2} after 1000 cycles, presenting high cycling stability. MoN{sub x}/TiN NTA could act as a promising electrode material of supercapacitor.

ZnO nanorod–templated well-aligned ZrO2 nanotube arrays for fibroblast adhesion and proliferation

International Nuclear Information System (INIS)

Lu, Zhisong; Hu, Weihua; Ming Li, Chang; Zhu, Zhihong; Liu, Jinping

2014-01-01

Cellular responses to porous tubular structures have recently been investigated in highly ordered ZrO 2 nanotube arrays fabricated with anodization. However, the potential applications of the nanotube arrays are hindered by instrument requirements and substrate limitations, as well as by the complicated processes needed for synthesis. In this work, ZrO 2 nanotube arrays were synthesized by in situ hydrolysis of zirconium propoxide with a zinc oxide nanorod array–based template. Fibroblast cells were able to grow on the nanotube array surface with produced elongated filopodia. Studies of the capability of cell growth and the expression of adhesion- and proliferation-related genes reveal that ZrO 2 nanotube arrays may provide a better environment for cell adhesion and growth than a flat titanium surface. These findings not only provide fundamental insight into cell response to nanostructures but also provide an opportunity to use a unique approach to fabricate ZrO 2 nanotube array structures for potential implant applications. (papers)

Composite of TiN nanoparticles and few-walled carbon nanotubes and its application to the electrocatalytic oxygen reduction reaction

KAUST Repository

Isogai, Shunsuke

2011-11-30

Nanoparticles meet nanotubes! Direct synthesis of TiN nanoparticles in a three-dimensional network of few-walled carbon nanotubes (FWCNTs) was achieved by using mesoporous graphitic carbon nitride (C 3N 4) as both a hard template and a nitrogen source. The TiN/FWCNT composite showed high performance for the oxygen reduction reaction in acidic media. © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Amorphous and crystalline TiO2 nanotube arrays for enhanced Li-ion intercalation properties.

Science.gov (United States)

Guan, Dongsheng; Cai, Chuan; Wang, Ying

2011-04-01

We have employed a simple process of anodizing Ti foils to prepare TiO2 nanotube arrays which show enhanced electrochemical properties for applications as Li-ion battery electrode materials. The lengths and pore diameters of TiO2 nanotubes can be finely tuned by varying voltage, electrolyte composition, or anodization time. The as-prepared nanotubes are amorphous and can be converted into anatase nanotubes with heat treatment at 480 degrees C. Rutile crystallites emerge in the anatase nanotube when the annealing temperature is increased to 580 degrees C, resulting in TiO2 nanotubes of mixed phases. The morphological features of nanotubes remain unchanged after annealing. Li-ion insertion performance has been studied for amorphous and crystalline TiO2 nanotube arrays. Amorphous nanotubes with a length of 3.0 microm and an outer diameter of 125 nm deliver a capacity of 91.2 microA h cm(-2) at a current density of 400 microA cm(-2), while those with a length of 25 microm and an outer diameter of 158 nm display a capacity of 533 microA h cm-2. When the 3-microm long nanotubes become crystalline, they deliver lower capacities: the anatase nanotubes and nanotubes of mixed phases show capacities of 53.8 microA h cm-2 and 63.1 microA h cm(-2), respectively at the same current density. The amorphous nanotubes show excellent capacity retention ability over 50 cycles. The cycled nanotubes show little change in morphology compared to the nanotubes before electrochemical cycling. All the TiO2 nanotubes demonstrate higher capacities than amorphous TiO2 compact layer reported in literature. The amorphous TiO2 nanotubes with a length of 1.9 microm exhibit a capacity five times higher than that of TiO2 compact layer even when the nanotube array is cycled at a current density 80 times higher than that for the compact layer. These results suggest that anodic TiO2 nanotube arrays are promising electrode materials for rechargeable Li-ion batteries.

High-efficiency perovskite solar cells based on anatase TiO{sub 2} nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Huang, Yan, E-mail: huangyan@ecust.edu.cn [School of Chemistry and Molecular Engineering, East China University of Science & Technology, Shanghai 200237 (China); Department of Chemical and Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Wu, Jiamin; Gao, Di [Department of Chemical and Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States)

2016-01-01

Perovskite solar cells (PSCs) based on one-dimensional anatase TiO{sub 2} nanotube arrays were prepared by using a two-step deposition method to fill the arrays of TiO{sub 2} nanotubes in different lengths with perovskite. The photovoltaic performance of PSCs was found to be significantly dependent on the length of the TiO{sub 2} nanotubes, and the power conversion efficiency decreased as the length of the TiO{sub 2} nanotubes increased from ~ 0.40 μm to ~ 0.65 and then to ~ 0.93 μm. The PSC fabricated with ~ 0.40 μm-long anatase TiO{sub 2} nanotube arrays yielded a power conversion efficiency of 11.3% and a fill factor of 0.68 under illumination of 100 mW/cm{sup 2} AM 1.5G simulated sunlight, which is significantly higher than previously reported solar cells based on 1-D TiO{sub 2} nanostructures. Incident photon-to-current efficiency and electrochemical impedance spectroscopy measurements indicated that longer TiO{sub 2} nanotubes led to higher recombination losses of charge carriers, possibly due to poor filling of the nanotube arrays with perovskite. - Highlights: • 1D anatase TiO{sub 2} nanotubes were used to fabricate perovskite solar cells. • The best efficiency of 11.3% was achieved with ~ 0.40 μm-long TiO{sub 2} nanotubes. • The efficiency of the devices decreased with increasing TiO{sub 2} nanotube lengths.

Visible diffraction from quasi-crystalline arrays of carbon nanotubes

Science.gov (United States)

Butler, Timothy P.; Butt, Haider; Wilkinson, Timothy D.; Amaratunga, Gehan A. J.

2015-08-01

Large area arrays of vertically-aligned carbon nanotubes (VACNTs) are patterned in a quasi-crystalline Penrose tile arrangement through electron beam lithography definition of Ni catalyst dots and subsequent nanotube growth by plasma-enhanced chemical vapour deposition. When illuminated with a 532 nm laser beam high-quality and remarkable diffraction patterns are seen. The diffraction is well matched to theoretical calculations which assume apertures to be present at the location of the VACNTs for transmitted light. The results show that VACNTs act as diffractive elements in reflection and can be used as spatially phased arrays for producing tailored diffraction patterns.

Preparation and elementary research on electrocatalytic hydrogen evolution of highly ordered titanium dioxide nanotube arrays

International Nuclear Information System (INIS)

Wu Qinglong; Liao Junsheng; Bai Yun

2010-01-01

Well ordered and uniform titanium dioxide nanotube arrays were fabricated by anodiaing process from a bath containing 1% NaF, 1mol/L Na 2 SO 4 , 0.5 mol/L H 2 SO 4 at room temperature. Surface morphology of titanium dioxide nanotube arrays were observed with SEM. The formation process of titanium dioxide nanotube arrays was suggested by current-time transient. Its catalytic hydrogen evolution behavior was studied by electrochemical measurements in a 5%(mass fraction) H 2 SO 4 solution. The results showed that the titanium dioxide nanotube arrays on titanium had better hydrogen evolution activity and trace palladium lead to the maximum electrocatalytic activity of hydrogen production. (authors)

Investigation on the Photoelectrocatalytic Activity of Well-Aligned TiO2 Nanotube Arrays

Directory of Open Access Journals (Sweden)

Xiaomeng Wu

2012-01-01

Full Text Available Well-aligned TiO2 nanotube arrays were fabricated by anodizing Ti foil in viscous F− containing organic electrolytes, and the crystal structure and morphology of the TiO2 nanotube array were characterized and analyzed by XRD, SEM, and TEM, respectively. The photocatalytic activity of the TiO2 nanotube arrays was evaluated in the photocatalytic (PC and photoelectrocatalytic (PEC degradation of methylene blue (MB dye in different supporting solutions. The excellent performance of ca. 97% for color removal was reached after 90 min in the PEC process compared to that of PC process which indicates that a certain external potential bias favors the promotion of the electrode reaction rate on TiO2 nanotube array when it is under illumination. In addition, it is found that PEC process conducted in supporting solutions with low pH and containing Cl− is also beneficial to accelerate the degradation rate of MB.

Dipolar interaction in arrays of magnetic nanotubes

International Nuclear Information System (INIS)

Velázquez-Galván, Y; Martínez-Huerta, J M; Encinas, A; De La Torre Medina, J; Danlée, Y; Piraux, L

2014-01-01

The dipolar interaction field in arrays of nickel nanotubes has been investigated on the basis of expressions derived from the effective demagnetizing field of the assembly as well as magnetometry measurements. The model incorporates explicitly the wall thickness and aspect ratio, as well as the spatial order of the nanotubes. The model and experiment show that the interaction field in nanotubes is smaller than that in solid nanowires due to the packing fraction reduction in tubes related to their inner cavity. Finally, good agreement between the model and experiment is found for the variation of the interaction field as a function of the tube wall thickness. (paper)

Visible light photoelectrocatalysis with salicylic acid-modified TiO2 nanotube array electrode for p-nitrophenol degradation

International Nuclear Information System (INIS)

Wang Xin; Zhao Huimin; Quan Xie; Zhao Yazhi; Chen Shuo

2009-01-01

This research focused on immersion method synthesis of visible light active salicylic acid (SA)-modified TiO 2 nanotube array electrode and its photoelectrocatalytic (PEC) activity. The SA-modified TiO 2 nanotube array electrode was synthesized by immersing in SA solution with an anodized TiO 2 nanotube array electrode. Scanning electron microscope (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), infrared spectroscopy (IR), UV-vis diffuse reflectance spectrum (DRS), and Surface photovoltage (SPV) were used to characterize this electrode. It was found that SA-modified TiO 2 nanotube array electrode absorbed well into visible region and exhibited enhanced visible light PEC activity on the degradation of p-nitrophenol (PNP). The degradation efficiencies increased from 63 to 100% under UV light, and 79-100% under visible light (λ > 400 nm), compared with TiO 2 nanotube array electrode. The enhanced PEC activity of SA-modified TiO 2 nanotube array electrode was attributed to the amount of surface hydroxyl groups introduced by SA-modification and the extension of absorption wavelength range.

The detection of improvised nonmilitary peroxide based explosives using a titania nanotube array sensor

International Nuclear Information System (INIS)

Banerjee, Subarna; Mohapatra, Susanta K; Misra, Mano; Mishra, Indu B

2009-01-01

There is a critical need to develop an efficient, reliable and highly selective sensor for the detection of improvised nonmilitary explosives. This paper describes the utilization of functionalized titania nanotube arrays for sensing improvised organic peroxide explosives such as triacetone triperoxide (TATP). TATP forms complexes with titania nanotube arrays (prepared by anodization and sensitized with zinc ions) and thus affects the electron state of the nanosensing device, which is signaled as a change in current of the overall nanotube material. The response is rapid and a signal of five to eight orders of magnitude is observed. These nanotube array sensors can be used as hand-held miniaturized devices as well as large scale portable units for military and homeland security applications.

The detection of improvised nonmilitary peroxide based explosives using a titania nanotube array sensor.

Science.gov (United States)

Banerjee, Subarna; Mohapatra, Susanta K; Misra, Mano; Mishra, Indu B

2009-02-18

There is a critical need to develop an efficient, reliable and highly selective sensor for the detection of improvised nonmilitary explosives. This paper describes the utilization of functionalized titania nanotube arrays for sensing improvised organic peroxide explosives such as triacetone triperoxide (TATP). TATP forms complexes with titania nanotube arrays (prepared by anodization and sensitized with zinc ions) and thus affects the electron state of the nanosensing device, which is signaled as a change in current of the overall nanotube material. The response is rapid and a signal of five to eight orders of magnitude is observed. These nanotube array sensors can be used as hand-held miniaturized devices as well as large scale portable units for military and homeland security applications.

Guided proliferation and bone-forming functionality on highly ordered large diameter TiO2 nanotube arrays

International Nuclear Information System (INIS)

Zhang, Ruopeng; Wu, Hongliu; Ni, Jiahua; Zhao, Changli; Chen, Yifan; Zheng, Chengjunyi; Zhang, Xiaonong

2015-01-01

The significantly enhanced osteoblast adhesion, proliferation and alkaline phosphatase (ALP) activity were observed on TiO 2 nanotube surface in recent studies in which the scale of nanotube diameter was restricted under 100 nm. In this paper, a series of highly ordered TiO 2 nanotube arrays with larger diameters ranging from 150 nm to 470 nm were fabricated via high voltage anodization. The behaviors of MC3T3-E1 cells in response to the diameter-controlled TiO 2 nanotubes were investigated. A contrast between the trend of proliferation and the trend of cell elongation was observed. The highest cell elongation (nearly 10:1) and the lowest cell number were observed on the TiO 2 nanotube arrays with 150 nm diameter. While, the lowest cell elongation and highest cell number were achieved on the TiO 2 nanotube arrays with 470 nm diameter. Furthermore, the ALP activity peaked on the 150 nm diameter TiO 2 nanotube arrays and decreased dramatically with the increase of nanotube diameter. Thus a narrow range of diameter (100–200 nm) that could induce the greatest bone-forming activity is determined. It is expected that more delicate design of orthopedic implant with regional abduction of cell proliferation or bone forming could be achieved by controlling the diameter of TiO 2 nanotubes. - Highlights: • Improved anodization methods leading to more ordered large diameter TiO 2 nanotubes • Significantly enhanced ALP activity was observed on 150 nm diameter TiO 2 nanotubes. • The highest cell density was observed on 470 nm diameter TiO 2 nanotube arrays. • Similar cell response was observed on the amorphous and anatase phased nanotube surface

Fabrication of DNA nanotubes with an array of exterior magnetic nanoparticles.

Science.gov (United States)

Rafati, Adele; Zarrabi, Ali; Gill, Pooria

2017-10-01

Described here a methodology for arraying of magnetic nanoparticles (MNPs) on the surface of DNA nanotubes (DNTs). Positioning of magnetic nanoparticles at exterior surface of DNTs were shaped after self-assembling of oligonucleotide staples within an M13mp18 DNA scaffold via an origami process. The staples were partially labeled with biotin to be arrayed at the surface of DNTs. Gel retardation assay of the DNTs carrying magnetic nanoparticles indicated a reversely behavioral electrophoretic movement in comparison to the nanotubes have been demonstrated previously. Also, high resolution transmission electron microscopy confirmed positioning magnetic nanoparticles at the exterior surface of DNTs, correctly. Ultrastructural characteristics of these DNA nanotubes using atomic force microscopy demonstrated topographic heights on their surfaces formed through positioning of magnetic nanoparticles outside the tubules. This nanoarchitecture would be potential for multiple arraying of nanoparticles that those be useful as functionalized chimeric nanocarriers for developing novel nanodrugs and nanobiosensors. Copyright © 2017. Published by Elsevier B.V.

Investigation of Conversion CO2 to Fuel by TiN nanotube-Cu nanoparticle

Directory of Open Access Journals (Sweden)

Leila Mahdavian

2017-01-01

Full Text Available The CO and CO2 effects are global warming, acid rain, limit visibility, decreases UV radiation; yellow/black color over cities and so on. In this study, convention of CO2 and H2O to CH4 and O2 near TiN- nanotube with Cu-nanoparticle calculated by Density Functional Theory (DFT methods. We have studied the structural, total energy, thermodynamic properties of these systems at room temperature. All the geometry optimization structures were carried out using GAMESS program package under Linux. DFT optimized their intermediates and transient states. The results have shown a sensitivity enhancement in resistance and capacitance when CO2 and H2O are converted to CH4 and O2. TiN-nanotube used photo-catalytic reactivity for the reduction of CO2 with H2O to form CH4 and O2 at 298K. The calculations are done in state them between of three TiN-nanotubes near Cu-nanoparticle.The calculation shown which heat reaction formation (∆H is endothermic for this reaction. This reaction needs to sun, photo active or other energy in the presence of visible light for doing.

Highly stable palladium-loaded TiO{sub 2} nanotube array electrode for the electrocatalytic hydrodehalogenation of polychlorinated biphenyls

Energy Technology Data Exchange (ETDEWEB)

Cui, Chunyue; Wu, Juan; Xin, Yanjun [Qingdao Agricultural University, Qingdao (China); Han, Yanhe [Beijing Institute of Petrochemical Technology, Beijing (China)

2015-06-15

Palladized TiO{sub 2} nanotube array electrode was prepared for the electrocatalytic hydrodehalogenation (HDH) of 2,4,5-trichlorobiphenyl (2,4,5-PCB). The TiO{sub 2} nanotube array electrode was successfully fabricated by anodic oxidation method, and Pd was loaded onto the TiO{sub 2} nanotubes by electrochemical deposition. The morphology and structure of the nanotube array electrodes with and without Pd catalysts were evaluated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The results showed that the diameters and lengths of the TiO{sub 2} nanotubes were 30-50 nm and 200-400 nm, respectively. The particle size of the Pd was about 12 nm. Electrocatalytic HDH of 2,4,5-PCB with the Pd/TiO{sub 2} nanotube array electrode was performed in H-cell reactor. Under a constant potential of -1.0 V, the HDH efficiency of 2,4,5-PCB was 90% and the biphenyl yield was 83% (15% current efficiency) within 180min at the Pd/TiO{sub 2} nanotube array electrode. Compared with the Pd/Ti electrode, the Pd/TiO{sub 2} nanotube array electrode exhibited higher HDH efficiency and stability. Additionally, the effect of the primary HDH factors was also investigated.

Thermal conductivity of vertically aligned carbon nanotube arrays: Growth conditions and tube inhomogeneity

Energy Technology Data Exchange (ETDEWEB)

Bauer, Matthew L.; Pham, Quang N.; Saltonstall, Christopher B.; Norris, Pamela M. [Department of Mechanical and Aerospace Engineering, University of Virginia, Charlottesville, Virginia 22904-4746 (United States)

2014-10-13

The thermal conductivity of vertically aligned carbon nanotube arrays (VACNTAs) grown on silicon dioxide substrates via chemical vapor deposition is measured using a 3ω technique. For each sample, the VACNTA layer and substrate are pressed to a heating line at varying pressures to extract the sample's thermophysical properties. The nanotubes' structure is observed via transmission electron microscopy and Raman spectroscopy. The presence of hydrogen and water vapor in the fabrication process is tuned to observe the effect on measured thermal properties. The presence of iron catalyst particles within the individual nanotubes prevents the array from achieving the overall thermal conductivity anticipated based on reported measurements of individual nanotubes and the packing density.

Growth of vertically aligned arrays of carbon nanotubes for high field emission

International Nuclear Information System (INIS)

Kim, D.; Lim, S.H.; Guilley, A.J.; Cojocaru, C.S.; Bouree, J.E.; Vila, L.; Ryu, J.H.; Park, K.C.; Jang, J.

2008-01-01

Vertically aligned multi-walled carbon nanotubes have been grown on Ni-coated silicon substrates, by using either direct current diode or triode plasma-enhanced chemical vapor deposition at low temperature (around 620 deg. C). Acetylene gas has been used as the carbon source while ammonia and hydrogen have been used for etching. However densely packed (∼ 10 9 cm -2 ) CNTs were obtained when the pressure was ∼ 100 Pa. The alignment of nanotubes is a necessary, but not a sufficient condition in order to get an efficient electron emission: the growth of nanotubes should be controlled along regular arrays, in order to minimize the electrostatic interactions between them. So a three dimensional numerical simulation has been developed to calculate the local electric field in the vicinity of the tips for a finite square array of nanotubes and thus to calculate the maximum of the electron emission current density as a function of the spacing between nanotubes. Finally the triode plasma-enhanced process combined with pre-patterned catalyst films (using different lithography techniques) has been chosen in order to grow regular arrays of aligned CNTs with different pitches in the micrometer range. The comparison between the experimental and the simulation data permits to define the most efficient CNT-based electron field emitters

Aligned carbon nanotube webs as a replacement for indium tin oxide in organic solar cells

International Nuclear Information System (INIS)

Sears, Kallista; Fanchini, Giovanni; Watkins, Scott E.; Huynh, Chi P.; Hawkins, Stephen C.

2013-01-01

Bulk heterojunction solar cells were fabricated with flexible webs of aligned multiwalled carbon nanotubes (MWNTs). These webs were drawn from a forest of MWNTs and placed directly onto the device substrate to form the hole collecting electrode. Devices were fabricated on glass substrates with one or two MWNT web layers to study the trade-off between transparency and resistivity on device performance. Devices with two web layers performed better with a fill factor of 0.47 and a device power conversion efficiency of 1.66% due to their higher conductivity. Flexible devices on Mylar substrates were also demonstrated with an efficiency of 1.2% indicating the potential of MWNT webs as a flexible alternative to the more conventional indium tin oxide. - Highlights: ► Drawable carbon nanotube webs were used as an anode in bulk heterojunction cells. ► One and two layers of carbon nanotube webs were compared. ► A thick active layer of ∼ 530 nm was needed to avoid shunting through nanotubes. ► Two layers of web gave the better efficiency of 1.6%. ► Flexible devices on Mylar were demonstrated with 1.2% efficiency

Aligned carbon nanotube webs as a replacement for indium tin oxide in organic solar cells

Energy Technology Data Exchange (ETDEWEB)

Sears, Kallista, E-mail: kallista.sears@csiro.au; Fanchini, Giovanni; Watkins, Scott E.; Huynh, Chi P.; Hawkins, Stephen C.

2013-03-01

Bulk heterojunction solar cells were fabricated with flexible webs of aligned multiwalled carbon nanotubes (MWNTs). These webs were drawn from a forest of MWNTs and placed directly onto the device substrate to form the hole collecting electrode. Devices were fabricated on glass substrates with one or two MWNT web layers to study the trade-off between transparency and resistivity on device performance. Devices with two web layers performed better with a fill factor of 0.47 and a device power conversion efficiency of 1.66% due to their higher conductivity. Flexible devices on Mylar substrates were also demonstrated with an efficiency of 1.2% indicating the potential of MWNT webs as a flexible alternative to the more conventional indium tin oxide. - Highlights: ► Drawable carbon nanotube webs were used as an anode in bulk heterojunction cells. ► One and two layers of carbon nanotube webs were compared. ► A thick active layer of ∼ 530 nm was needed to avoid shunting through nanotubes. ► Two layers of web gave the better efficiency of 1.6%. ► Flexible devices on Mylar were demonstrated with 1.2% efficiency.

Copper-encapsulated vertically aligned carbon nanotube arrays.

Science.gov (United States)

Stano, Kelly L; Chapla, Rachel; Carroll, Murphy; Nowak, Joshua; McCord, Marian; Bradford, Philip D

2013-11-13

A new procedure is described for the fabrication of vertically aligned carbon nanotubes (VACNTs) that are decorated, and even completely encapsulated, by a dense network of copper nanoparticles. The process involves the conformal deposition of pyrolytic carbon (Py-C) to stabilize the aligned carbon-nanotube structure during processing. The stabilized arrays are mildly functionalized using oxygen plasma treatment to improve wettability, and they are then infiltrated with an aqueous, supersaturated Cu salt solution. Once dried, the salt forms a stabilizing crystal network throughout the array. After calcination and H2 reduction, Cu nanoparticles are left decorating the CNT surfaces. Studies were carried out to determine the optimal processing parameters to maximize Cu content in the composite. These included the duration of Py-C deposition and system process pressure as well as the implementation of subsequent and multiple Cu salt solution infiltrations. The optimized procedure yielded a nanoscale hybrid material where the anisotropic alignment from the VACNT array was preserved, and the mass of the stabilized arrays was increased by over 24-fold because of the addition of Cu. The procedure has been adapted for other Cu salts and can also be used for other metal salts altogether, including Ni, Co, Fe, and Ag. The resulting composite is ideally suited for application in thermal management devices because of its low density, mechanical integrity, and potentially high thermal conductivity. Additionally, further processing of the material via pressing and sintering can yield consolidated, dense bulk composites.

Novel iron oxide nanotube arrays as high-performance anodes for lithium ion batteries

Science.gov (United States)

Zhong, Yuan; Fan, Huiqing; Chang, Ling; Shao, Haibo; Wang, Jianming; Zhang, Jianqing; Cao, Chu-nan

2015-11-01

Nanostructured iron oxides can be promising anode materials for lithium ion batteries (LIBs). However, improvement on the rate capability and/or electrochemical cycling stability of iron oxide anode materials remains a key challenge because of their poor electrical conductivities and large volume expansion during cycling. Herein, the vertically aligned arrays of one-dimensional (1D) iron oxide nanotubes with 5.8 wt% carbon have been fabricated by a novel surfactant-free self-corrosion process and subsequent thermal treatment. The as-fabricated nanotube array electrode delivers a reversible capacity of 932 mAh g-1 after 50 charge-discharge cycles at a current of 0.6 A g-1. The electrode still shows a reversible capacity of 610 mAh g-1 even at a very high rate (8.0 A g-1), demonstrating its prominent rate capability. Furthermore, the nanotube array electrode also exhibits the excellent electrochemical cycling stability with a reversible capacity of 880 mAh g-1 after 500 cycles at a current of 4 A g-1. The nanotube array electrode with superior lithium storage performance reveals the promising potential as a high-performance anode for LIBs.

Biochips Containing Arrays of Carbon-Nanotube Electrodes

Science.gov (United States)

Li, Jun; Meyyappan, M.; Koehne, Jessica; Cassell, Alan; Chen, Hua

2008-01-01

Biochips containing arrays of nanoelectrodes based on multiwalled carbon nanotubes (MWCNTs) are being developed as means of ultrasensitive electrochemical detection of specific deoxyribonucleic acid (DNA) and messenger ribonucleic acid (mRNA) biomarkers for purposes of medical diagnosis and bioenvironmental monitoring. In mass production, these biochips could be relatively inexpensive (hence, disposable). These biochips would be integrated with computer-controlled microfluidic and microelectronic devices in automated hand-held and bench-top instruments that could be used to perform rapid in vitro genetic analyses with simplified preparation of samples. Carbon nanotubes are attractive for use as nanoelectrodes for detection of biomolecules because of their nanoscale dimensions and their chemical properties.

Determination of the effective Young's modulus of vertically aligned carbon nanotube arrays: a simple nanotube-based varactor

International Nuclear Information System (INIS)

Olofsson, Niklas; Eriksson, Anders; Ek-Weis, Johan; Campbell, Eleanor E B; Idda, Tonio

2009-01-01

The electromechanical properties of arrays of vertically aligned multiwalled carbon nanotubes were studied in a parallel plate capacitor geometry. The electrostatic actuation was visualized using both optical microscopy and scanning electron microscopy, and highly reproducible behaviour was achieved for actuation voltages below the pull-in voltage. The walls of vertically aligned carbon nanotubes behave as solid cohesive units. The effective Young's modulus for the carbon nanotube arrays was determined by comparing the actuation results with the results of electrostatic simulations and was found to be exceptionally low, of the order of 1-10 MPa. The capacitance change and Q-factor were determined by measuring the frequency dependence of the radio-frequency transmission. Capacitance changes of over 20% and Q-factors in the range 100-10 were achieved for a frequency range of 0.2-1.5 GHz.

Fringing-field dielectrophoretic assembly of ultrahigh-density semiconducting nanotube arrays with a self-limited pitch

Science.gov (United States)

Cao, Qing; Han, Shu-Jen; Tulevski, George S.

2014-09-01

One key challenge of realizing practical high-performance electronic devices based on single-walled carbon nanotubes is to produce electronically pure nanotube arrays with both a minuscule and uniform inter-tube pitch for sufficient device-packing density and homogeneity. Here we develop a method in which the alternating voltage-fringing electric field formed between surface microelectrodes and the substrate is utilized to assemble semiconducting nanotubes into well-aligned, ultrahigh-density and submonolayered arrays, with a consistent pitch as small as 21±6 nm determined by a self-limiting mechanism, based on the unique field focusing and screening effects of the fringing field. Field-effect transistors based on such nanotube arrays exhibit record high device transconductance (>50 μS μm-1) and decent on current per nanotube (~1 μA per tube) together with high on/off ratios at a drain bias of -1 V.

Chemical Vapor Identification by Plasma Treated Thick Film Tin Oxide Gas Sensor Array and Pattern Recognition

Directory of Open Access Journals (Sweden)

J. K. Srivastava

2011-02-01

Full Text Available Present study deals the class recognition potential of a four element plasma treated thick film tin oxide gas sensor array exposed with volatile organic compounds (VOCs. Methanol, Ethanol and Acetone are selected as target VOCs and exposed on sensor array at different concentration in range from 100-1000 ppm. Sensor array consist of four tin oxide sensors doped with 1-4 % PbO concentrations were fabricated by thick film technology and then treated with oxygen plasma for 5-10 minute durations. Sensor signal is analyzed by principal component analysis (PCA for visual classification of VOCs. Further output of PCA is used as input for classification of VOCs by four pattern classification techniques as: linear discriminant analysis (LDA, k-nearest neighbor (KNN, back propagation neural network (BPNN and support vector machine (SVM. All the four classifier results 100 % correct classification rate of VOCs by response analysis of sensor array treated with plasma for 5 minute.

Uniform, dense arrays of vertically aligned, large-diameter single-walled carbon nanotubes.

Science.gov (United States)

Han, Zhao Jun; Ostrikov, Kostya

2012-04-04

Precisely controlled reactive chemical vapor synthesis of highly uniform, dense arrays of vertically aligned single-walled carbon nanotubes (SWCNTs) using tailored trilayered Fe/Al(2)O(3)/SiO(2) catalyst is demonstrated. More than 90% population of thick nanotubes (>3 nm in diameter) can be produced by tailoring the thickness and microstructure of the secondary catalyst supporting SiO(2) layer, which is commonly overlooked. The proposed model based on the atomic force microanalysis suggests that this tailoring leads to uniform and dense arrays of relatively large Fe catalyst nanoparticles on which the thick SWCNTs nucleate, while small nanotubes and amorphous carbon are effectively etched away. Our results resolve a persistent issue of selective (while avoiding multiwalled nanotubes and other carbon nanostructures) synthesis of thick vertically aligned SWCNTs whose easily switchable thickness-dependent electronic properties enable advanced applications in nanoelectronic, energy, drug delivery, and membrane technologies.

Structure and dye-sensitized solar cell application of TiO2 nanotube arrays fabricated by the anodic oxidation method

Science.gov (United States)

Ok, Seon-Yeong; Cho, Kwon-Koo; Kim, Ki-Won; Ryu, Kwang-Sun

2010-05-01

Well-ordered TiO2 nanotube arrays were fabricated by the potentiostatic anodic oxidation method using pure Ti foil as a working electrode and ethylene glycol solution as an electrolyte with the small addition of NH4F and H2O. The influence of anodization temperature and time on the morphology and formation of TiO2 nanotube arrays was examined. The TiO2 nanotube arrays were applied as a photoelectrode to dye-sensitized solar cells. Regardless of anodizing temperature and time, the average diameter and wall thickness of TiO2 nanotube arrays show a similar value, whereas the length increases with decreasing reaction temperature. The conversion efficiency is very low, which is due to a morphology breaking of the TiO2 nanotube arrays in the manufacturing process of a photoelectrode.

Improved electrochemical performances of CuO nanotube array prepared via electrodeposition as anode for lithium ion battery

Energy Technology Data Exchange (ETDEWEB)

Xiao, Anguo, E-mail: hixiaoanguo@126.com; Zhou, Shibiao; Zuo, Chenggang; Zhuan, Yongbing; Ding, Xiang

2015-10-15

Graphical abstract: CuO nanotube array electrodes prepared by electrodeposition method exhibit an excellent lithium ion storage ability as anode of Li-ion battery. - Highlights: • CuO nanotube arrays are synthesized by an electrodeposition method. • CuO nanotube shows a high-rate performance. • CuO nanotube shows an excellent cycling performance. - Abstract: We report a facile strategy to prepared CuO nanotube arrays directly grown on Cu plate through the electrodeposition method. The as-prepared CuO nanotubes show a quasi-cylinder nanostructure with internal diameters of ca. ∼100 nm, external diameters of ca. ∼120 nm, and average length of ∼3 μm. As an anode for lithium ion batteries, the electrochemical properties of the CuO nanotube arrays are investigated by cyclic voltammetry (CV) and galvanostatic charge/discharge tests. Due to the unique nanotube nanostructure, the as-prepared CuO electrodes exhibit good rate performance (550 mAh g{sup −1} at 0.1 C and 464 mAh g{sup −1} at 1 C) and cycling performance (581 mAh g{sup −1} at 0.1 C and 538 mAh g{sup −1} at 0.5 C)

Graphene quantum dots-carbon nanotube hybrid arrays for supercapacitors

Science.gov (United States)

Hu, Yue; Zhao, Yang; Lu, Gewu; Chen, Nan; Zhang, Zhipan; Li, Hui; Shao, Huibo; Qu, Liangti

2013-05-01

Graphene quantum dots (GQDs) have been successfully deposited onto aligned carbon nanotubes (CNTs) by a benign electrochemical method and the capacitive properties of the as-formed GQD/CNT hybrid arrays were evaluated in symmetrical supercapacitors. It was found that supercapacitors fabricated from GQD/CNT hybrid arrays exhibited a high capacitance of 44 mF cm-2, representing a more than 200% improvement over that of bare CNT electrodes.

Synthesis of Fe2O3/TiO2 nanorod-nanotube arrays by filling TiO2 nanotubes with Fe

International Nuclear Information System (INIS)

Mohapatra, Susanta K; Banerjee, Subarna; Misra, Mano

2008-01-01

Synthesis of hematite (α-Fe 2 O 3 ) nanostructures on a titania (TiO 2 ) nanotubular template is carried out using a pulsed electrodeposition technique. The TiO 2 nanotubes are prepared by the sonoelectrochemical anodization method and are filled with iron (Fe) by pulsed electrodeposition. The Fe/TiO 2 composite is then annealed in an O 2 atmosphere to convert it to Fe 2 O 3 /TiO 2 nanorod-nanotube arrays. The length of the Fe 2 O 3 inside the TiO 2 nanotubes can be tuned from 50 to 550 nm by changing the deposition time. The composite material is characterized by scanning electron microscopy, transmission electron microscopy and diffuse reflectance ultraviolet-visible studies to confirm the formation of one-dimensional Fe 2 O 3 /TiO 2 nanorod-nanotube arrays. The present approach can be used for designing variable one-dimensional metal oxide heterostructures

A novel method for the fabrication of a high-density carbon nanotube microelectrode array

Directory of Open Access Journals (Sweden)

Adam Khalifa

2015-09-01

Full Text Available We present a novel method for fabricating a high-density carbon nanotube microelectrode array (MEA chip. Vertically aligned carbon nanotubes (VACNTs were synthesized by microwave plasma-enhanced chemical vapor deposition and thermal chemical vapor deposition. The device was characterized using electrochemical experiments such as cyclic voltammetry, impedance spectroscopy and potential transient measurements. Through-silicon vias (TSVs were fabricated and partially filled with polycrystalline silicon to allow electrical connection from the high-density electrodes to a stimulator microchip. In response to the demand for higher resolution implants, we have developed a unique process to obtain a high-density electrode array by making the microelectrodes smaller in size and designing new ways of routing the electrodes to current sources. Keywords: Microelectrode array, Neural implant, Carbon nanotubes, Through-silicon via interconnects, Microfabrication

Fast fabrication of long TiO2 nanotube array with high photoelectrochemical property on flexible stainless steel.

Science.gov (United States)

Tao, Jie; Wu, Tao; Gao, Peng

2012-03-01

Oriented highly ordered long TiO2 nanotube array films with nanopore structure and high photoelectrochemical property were fabricated on flexible stainless steel substrate (50 microm) by anodization treatment of titanium thin films in a short time. The samples were characterized by means of field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD) and photoelectrochemical methods, respectively. The results showed that Ti films deposited at the condition of 0.7 Pa Ar pressure and 96 W sputtering power at room temperature was uniform and dense with good homogeneity and high crystallinity. The voltage and the anodization time both played significant roles in the formation of TiO2 nanopore-nanotube array film. The optimal voltage was 60 V and the anodization time is less than 30 min by anodizing Ti films in ethylene glycerol containing 0.5% (w) NH4F and 3% (w) H2O. The growth rate of TiO2 nanotube array was as high as 340 nm/min. Moreover, the photocurrent-potential curves, photocurrent response curves and electrochemical impedance spectra results indicated that the TiO2 nanotube array film with the nanoporous structure exhibited a better photo-response ability and photoelectrochemical performance than the ordinary TiO2 nanotube array film. The reason is that the nanoporous structure on the surface of the nanotube array can separate the photo electron-hole pairs more efficiently and completely than the tubular structure.

Inkjet printed ambipolar transistors and inverters based on carbon nanotube/zinc tin oxide heterostructures

International Nuclear Information System (INIS)

Kim, Bongjun; Jang, Seonpil; Dodabalapur, Ananth; Geier, Michael L.; Prabhumirashi, Pradyumna L.; Hersam, Mark C.

2014-01-01

We report ambipolar field-effect transistors (FETs) consisting of inkjet printed semiconductor bilayer heterostructures utilizing semiconducting single-walled carbon nanotubes (SWCNTs) and amorphous zinc tin oxide (ZTO). The bilayer structure allows for electron transport to occur principally in the amorphous oxide layer and hole transport to occur exclusively in the SWCNT layer. This results in balanced electron and hole mobilities exceeding 2 cm 2 V −1 s −1 at low operating voltages ( 10). This work provides a pathway for realizing solution processable, inkjet printable, large area electronic devices, and systems based on SWCNT-amorphous oxide heterostructures

Structure and dye-sensitized solar cell application of TiO{sub 2} nanotube arrays fabricated by the anodic oxidation method

Energy Technology Data Exchange (ETDEWEB)

Ok, Seon-Yeong; Cho, Kwon-Koo; Kim, Ki-Won [School of Material Science and Engineering, ERI and i-cube center, Gyeongsang National University, 900 Gazwadong, Jinju, Gyeongnam 660-701 (Korea, Republic of); Ryu, Kwang-Sun, E-mail: kkcho66@gnu.ac.k [Department of Chemistry, University of Ulsan, Ulsan, 680-749 (Korea, Republic of)

2010-05-01

Well-ordered TiO{sub 2} nanotube arrays were fabricated by the potentiostatic anodic oxidation method using pure Ti foil as a working electrode and ethylene glycol solution as an electrolyte with the small addition of NH{sub 4}F and H{sub 2}O. The influence of anodization temperature and time on the morphology and formation of TiO{sub 2} nanotube arrays was examined. The TiO{sub 2} nanotube arrays were applied as a photoelectrode to dye-sensitized solar cells. Regardless of anodizing temperature and time, the average diameter and wall thickness of TiO{sub 2} nanotube arrays show a similar value, whereas the length increases with decreasing reaction temperature. The conversion efficiency is very low, which is due to a morphology breaking of the TiO{sub 2} nanotube arrays in the manufacturing process of a photoelectrode.

Coated carbon nanotube array electrodes

Science.gov (United States)

Ren, Zhifeng [Newton, MA; Wen, Jian [Newton, MA; Chen, Jinghua [Chestnut Hill, MA; Huang, Zhongping [Belmont, MA; Wang, Dezhi [Wellesley, MA

2008-10-28

The present invention provides conductive carbon nanotube (CNT) electrode materials comprising aligned CNT substrates coated with an electrically conducting polymer, and the fabrication of electrodes for use in high performance electrical energy storage devices. In particular, the present invention provides conductive CNTs electrode material whose electrical properties render them especially suitable for use in high efficiency rechargeable batteries. The present invention also provides methods for obtaining surface modified conductive CNT electrode materials comprising an array of individual linear, aligned CNTs having a uniform surface coating of an electrically conductive polymer such as polypyrrole, and their use in electrical energy storage devices.

Anodic Fabrication of Ti-Nb-Zr-O Nanotube Arrays

Directory of Open Access Journals (Sweden)

Qiang Liu

2014-01-01

Full Text Available Highly ordered Ti-Nb-Zr-O nanotube arrays were fabricated through pulse anodic oxidation of Ti-Nb-Zr alloy in 1 M NaH2PO4 containing 0.5 wt% HF electrolytes. The effect of anodization parameters and Zr content on the microstructure and composition of Ti-Nb-Zr-O nanotubes was investigated using a scanning electron microscope equipped with energy dispersive X-ray analysis. It was found that length of the Ti-Nb-Zr-O nanotubes increased with increase of Zr contents. The diameter and the length of Ti-Nb-Zr-O nanotubes could be controlled by pulse voltage. XRD analysis of Ti-Nb-Zr-O samples annealed at 500°C in air indicated that the (101 diffraction peaks shifted from 25.78° to 25.05° for annealed Ti-Nb-Zr-O samples with different Zr contents because of larger lattice parameter of Ti-Nb-Zr-O compared to that of undoped TiO2.

Fabrication of doped TiO2 nanotube array films with enhanced photo-catalytic activity

Science.gov (United States)

Peighambardoust, Naeimeh-Sadat; Khameneh-asl, Shahin; Khademi, Adib

2018-01-01

In the present work, we investigate the N and Fe-doped TiO2 nanotube array film prepared by treating TiO2 nanotube array film with ammonia solution and anodizing in Fe(NO3)3 solution respectively. This method avoided the use of hazardous ammonia gas, or laborious ion implantation process. N and Fe-doped TiO2 nanotube arrays (TiO2 NTs) were prepared by electrochemical anodization process in 0.5 wt % HF aqueous solution. The anodization was performed at the conditions of 20 V and 20 min, Followed by a wet immersion in NH3.H2O (1M) for N-doping for 2 hr and annealing post-treatment at 450 °C. The morphology and structure of the nanotube films were characterized by field emission scanning electron microscope (FESEM) and EDX. UV-vis. illumination test were done to observe photo-enhanced catalysis. The effect of different annealing temperature on the structure and photo-absorption property of the TiO2-TNTs was investigated. The results showed that N-TNTs nanotubes exhibited higher photocatalytic activity compared whit the Fe-doped and pure TNTs, because doping N promoted the separation of the photogenerated electrons and holes.

Laser-assisted simultaneous transfer and patterning of vertically aligned carbon nanotube arrays on polymer substrates for flexible devices.

Science.gov (United States)

In, Jung Bin; Lee, Daeho; Fornasiero, Francesco; Noy, Aleksandr; Grigoropoulos, Costas P

2012-09-25

We demonstrate a laser-assisted dry transfer technique for assembling patterns of vertically aligned carbon nanotube arrays on a flexible polymeric substrate. A laser beam is applied to the interface of a nanotube array and a polycarbonate sheet in contact with one another. The absorbed laser heat promotes nanotube adhesion to the polymer in the irradiated regions and enables selective pattern transfer. A combination of the thermal transfer mechanism with rapid direct writing capability of focused laser beam irradiation allows us to achieve simultaneous material transfer and direct micropatterning in a single processing step. Furthermore, we demonstrate that malleability of the nanotube arrays transferred onto a flexible substrate enables post-transfer tailoring of electric conductance by collapsing the aligned nanotubes in different directions. This work suggests that the laser-assisted transfer technique provides an efficient route to using vertically aligned nanotubes as conductive elements in flexible device applications.

In situ synthesis of oriented NiS nanotube arrays on FTO as high-performance counter electrode for dye-sensitized solar cells

Energy Technology Data Exchange (ETDEWEB)

Li, Yan, E-mail: liyan-nwnu@163.com [Key Laboratory of Atomic and Molecular Physics & Functional Materials of Gansu Province, College of Physics and Electronic Engineering, Northwest Normal University, Lanzhou, 730070 (China); Chang, Yin [Key Laboratory of Atomic and Molecular Physics & Functional Materials of Gansu Province, College of Physics and Electronic Engineering, Northwest Normal University, Lanzhou, 730070 (China); Zhao, Yun [Laboratory of Clean Energy Chemistry and Materials, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000 (China); Wang, Jian; Wang, Cheng-wei [Key Laboratory of Atomic and Molecular Physics & Functional Materials of Gansu Province, College of Physics and Electronic Engineering, Northwest Normal University, Lanzhou, 730070 (China)

2016-09-15

Oriented nickel sulfide (NiS) nanotube arrays were successfully in-situ fabricated on conductive glass substrate and used directly as counter electrode for dye-sensitized solar cells without any post-processing. Compared with Pt counter electrode, for the beneficial effect of electronic transport along the axial direction through the arrays to the substrate, oriented NiS nanotube arrays exhibit both higher electrocatalytic activity for I{sub 3}{sup −} reduction and better electrochemical stability, resulting in a significantly improved power conversion efficiency of 9.8%. Such in-situ grown oriented sulfide semiconductor nanotube arrays is expected to lead a new class structure of composites for highly efficient cathode materials. - Highlights: • In-situ synthesis strategy was proposed to construct oriented NiS nanotube arrays. • Such oriented tube nanostructure benefits the electronic transport along the axial direction of the arrays. • As CE of DSSCs, NiS nanotube arrays exhibit both higher efficiency (9.8%) and electrochemical stability than Pt.

Laser-Assisted Simultaneous Transfer and Patterning of Vertically Aligned Carbon Nanotube Arrays on Polymer Substrates for Flexible Devices

KAUST Repository

In, Jung Bin; Lee, Daeho; Fornasiero, Francesco; Noy, Aleksandr; Grigoropoulos, Costas P.

2012-01-01

We demonstrate a laser-assisted dry transfer technique for assembling patterns of vertically aligned carbon nanotube arrays on a flexible polymeric substrate. A laser beam is applied to the interface of a nanotube array and a polycarbonate sheet

Self-Assembled TiO2 Nanotube Arrays with U-Shaped Profile by Controlling Anodization Temperature

Directory of Open Access Journals (Sweden)

Jingfei Chen

2010-01-01

Full Text Available TiO2 nanotube arrays with uniform diameter from top to bottom were fabricated. The synthesizing approach is based on the investigation of the influence of electrolyte temperature on the tube diameter. We found that the inner diameter of the tubes increased with the electrolyte temperature. Accordingly, we improved the tube profile from the general V shape to U shape by raising the electrolyte temperature gradually. This is a simple and fast approach to fabricate uniform TiO2 nanotubes in diameter. The improved TiO2 nanotube arrays may show better properties and have broad potential applications.

Laser-Assisted Simultaneous Transfer and Patterning of Vertically Aligned Carbon Nanotube Arrays on Polymer Substrates for Flexible Devices

KAUST Repository

In, Jung Bin

2012-09-25

We demonstrate a laser-assisted dry transfer technique for assembling patterns of vertically aligned carbon nanotube arrays on a flexible polymeric substrate. A laser beam is applied to the interface of a nanotube array and a polycarbonate sheet in contact with one another. The absorbed laser heat promotes nanotube adhesion to the polymer in the irradiated regions and enables selective pattern transfer. A combination of the thermal transfer mechanism with rapid direct writing capability of focused laser beam irradiation allows us to achieve simultaneous material transfer and direct micropatterning in a single processing step. Furthermore, we demonstrate that malleability of the nanotube arrays transferred onto a flexible substrate enables post-transfer tailoring of electric conductance by collapsing the aligned nanotubes in different directions. This work suggests that the laser-assisted transfer technique provides an efficient route to using vertically aligned nanotubes as conductive elements in flexible device applications. © 2012 American Chemical Society.

Preparation and characterization of SiO2:Sm3+ nanotube arrays with 1.06 μm laser antireflective property

International Nuclear Information System (INIS)

Tan, Wei-min; Huang, Ning; Wang, Li-jun; Song, Tian-shun; Lu, Chun-hua; Wang, Liu-fang; Zhang, Jun-zhi

2013-01-01

SiO 2 : Sm 3+ nanotube arrays with excellent antireflective property at 1.06 μm were synthesized by a template-assisted sol–gel process. The molecular structure, morphology and optical properties of the fabricated SiO 2 :Sm 3+ nanotube arrays were investigated by a Fourier transform infrared spectroscope (FTIR), a Scanning electron microscope (SEM), and a spectro-fluorometer, respectively. The experimental results demonstrate that the SiO 2 :Sm 3+ nanotube arrays were formed via the AAO membrane during the sol–gel process. The remarkable antireflective characteristic of about 0.166% at 1.06 μm was attributed to the drastic decrease of effective refraction index which enhances the matching effect between air and substrate. As well as the absorption performance of Sm3+ at 1.06 μm which consumes the energies of incident light. - Graphical abstract: Directional aligned SiO 2 :Sm 3+ nanotube arrays were synthesized in AAO template by sol–gel process, and the antiflective performance of arrays is prominent comparing to the blank AAO template. Highlights: ► SiO 2 :Sm 3+ nanotube arrays are synthesized by a template-assisted sol–gel process. ► SiO 2 :Sm 3+ nanotube arrays have remarkable antireflective properties at 1.06 μm. ► The subwavelength structure results in a decrease of effective refraction index. ► The absorption performance of Sm 3+ at 1.06 μm consume the energies of incident light

Polyaniline nanowire array encapsulated in titania nanotubes as a superior electrode for supercapacitors

Science.gov (United States)

Xie, Keyu; Li, Jie; Lai, Yanqing; Zhang, Zhi'an; Liu, Yexiang; Zhang, Guoge; Huang, Haitao

2011-05-01

Conducting polymer with 1D nanostructure exhibits excellent electrochemical performances but a poor cyclability that limits its use in supercapacitors. In this work, a novel composite electrode made of polyaniline nanowire-titania nanotube array was synthesized via a simple and inexpensive electrochemical route by electropolymerizing aniline onto an anodized titania nanotube array. The specific capacitance was as high as 732 F g-1 at 1 A g-1, which remained at 543 F g-1 when the current density was increased by 20 times. 74% of the maximum energy density (36.6 Wh kg-1) was maintained even at a high power density of 6000 W kg-1. An excellent long cycle life of the electrode was observed with a retention of ~86% of the initial specific capacitance after 2000 cycles. The good electrochemical performance was attributed to the unique microstructure of the electrode with disordered PANI nanowire arrays encapsulated inside the TiO2 nanotubes, providing high surface area, fast diffusion path for ions and long-term cycle stability. Such a nanocomposite electrode is attractive for supercapacitor applications.

Electrochemically synthesized visible light absorbing vertically aligned N-doped TiO2 nanotube array films

International Nuclear Information System (INIS)

Antony, Rajini P.; Mathews, Tom; Ajikumar, P.K.; Krishna, D. Nandagopala; Dash, S.; Tyagi, A.K.

2012-01-01

Graphical abstract: Display Omitted Highlights: ► Single step electrochemical synthesis of N-doped TiO 2 nanotube array films. ► Effective substitutional N-doping achieved. ► Different N-concentrations were achieved by varying the N-precursor concentration in the electrolyte. ► Visible light absorption observed at high N-doping. -- Abstract: Visible light absorbing vertically aligned N-doped anatase nanotube array thin films were synthesized by anodizing Ti foils in ethylene glycol + NH 4 F + water mixture containing urea as nitrogen source. Different nitrogen concentrations were achieved by varying the urea content in the electrolyte. The structure, morphology, composition and optical band gap of the nanotube arrays were determined by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy (XPS) and diffuse reflectance spectroscopy, respectively. The substitution of O 2− ions by N 3− ions in the anion sublattice as well as the formulae of the doped samples was confirmed from the results of XPS. The optical band gap of the nanotube arrays was found to decrease with N-concentration. The sample with the highest concentration corresponding to the formula TiO 1.83 N 0.14 showed two regions in the Tauc's plot indicating the presence of interband states.

Exploring hierarchical FeS2/C composite nanotubes arrays as advanced cathode for lithium ion batteries

Science.gov (United States)

Pan, G. X.; Cao, F.; Xia, X. H.; Zhang, Y. J.

2016-11-01

Rational construction of advanced FeS2 cathode is one of research hotspots, and of great importance for developing high-performance lithium ion batteries (LIBs). Herein we report a facile hydrolysis-sulfurization method for fabrication of FeS2/C nanotubes arrays with the help of sacrificial Co2(OH)2CO3 nanowires template and glucose carbonization. Self-supported FeS2/C nanotubes consist of interconnected nanoburrs of 5-20 nm, and show hierarchical porous structure. The FeS2/C nanotubes arrays are demonstrated with enhanced cycling life and noticeable high-rate capability with capacities ranging from 735 mAh g-1 at 0.25 C to 482 mAh g-1 at 1.5 C, superior to those FeS2 counterparts in the literature. The composite nanotubes arrays architecture plays positive roles in the electrochemical enhancement due to combined advantages of large electrode-electrolyte contact area, good strain accommodation, improved electrical conductivity, and enhanced structural stability.

Efficient Photocatalytic Degradation of Rhodamine B Dye by Aligned Arrays of Self-Assembled Hydrogen Titanate Nanotubes

Directory of Open Access Journals (Sweden)

Sriparna Chatterjee

2014-01-01

Full Text Available We show that an aligned array of hydrothermally grown, multiwalled hydrogen titanate (H2Ti3O7 nanotubes—anchored to both faces of a metallic Ti foil—acts as an efficient photocatalyst. We studied the degradation of rhodamine B dye in the presence of the nanostructured photocatalyst under UV irradiation, by monitoring the optical absorption of the dye. Rhodamine B was chosen as a representative—and particularly harmful—industrial pollutant dye. The inner and outer diameters of the H2Ti3O7 nanotubes were 5 nm and 10 nm, respectively. The nanotube array catalyst is recyclable and structurally stable. Most importantly, it shows comparable or higher photodecomposition rate constant than those of both H2Ti3O7 nanotube powder and P-25 (Degussa. The enhanced photocatalytic performance may be ascribed to the nanotube array having a superhydrophilic surface with a high accessible surface area.

Hot spot dynamics in carbon nanotube array devices.

Science.gov (United States)

Engel, Michael; Steiner, Mathias; Seo, Jung-Woo T; Hersam, Mark C; Avouris, Phaedon

2015-03-11

We report on the dynamics of spatial temperature distributions in aligned semiconducting carbon nanotube array devices with submicrometer channel lengths. By using high-resolution optical microscopy in combination with electrical transport measurements, we observe under steady state bias conditions the emergence of time-variable, local temperature maxima with dimensions below 300 nm, and temperatures above 400 K. On the basis of time domain cross-correlation analysis, we investigate how the intensity fluctuations of the thermal radiation patterns are correlated with the overall device current. The analysis reveals the interdependence of electrical current fluctuations and time-variable hot spot formation that limits the overall device performance and, ultimately, may cause device degradation. The findings have implications for the future development of carbon nanotube-based technologies.

Highly aligned carbon nanotube arrays fabricated by bias sputtering

International Nuclear Information System (INIS)

Hayashi, Nobuyuki; Honda, Shin-ichi; Tsuji, Keita; Lee, Kuei-Yi; Ikuno, Takashi; Fujimoto, Keiichi; Ohkura, Shigeharu; Katayama, Mitsuhiro; Oura, Kenjiro; Hirao, Takashi

2003-01-01

Vertically aligned carbon nanotube (CNT) arrays have been successfully grown on Si substrates by dc bias sputtering. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observations revealed that the resultant arrays consisted of dense CNTs with diameters of 40-60 nm and lengths of 300-400 nm. The CNTs were found to have a bamboo-like structure at the end of which metallic nanoparticle was formed, indicating tip growth mechanism. The energy enhancement of carbon particles is a key factor for synthesis of CNTs using dc bias sputtering system

Facile fabrication of organic/inorganic nanotube heterojunction arrays for enhanced photoelectrochemical water splitting

Science.gov (United States)

Chen, Yingzhi; Li, Aoxiang; Yue, Xiaoqi; Wang, Lu-Ning; Huang, Zheng-Hong; Kang, Feiyu; Volinsky, Alex A.

2016-07-01

Organic/inorganic heterojunction photoanodes are appealing for making concurrent use of the highly photoactive organic semiconductors, and the efficient dielectric screening provided by their inorganic counterparts. In the present work, organic/inorganic nanotube heterojunction arrays composed of TiO2 nanotube arrays and a semiconducting N,N-(dicyclohexyl) perylene-3,4,9,10-tetracarboxylic diimide (PDi) layer were fabricated for photoelectrochemical water splitting. In this arrayed architecture, a PDi layer with a tunable thickness was coated on anodic TiO2 nanotube arrays by physical vapor deposition, which is advantageous for the formation of a uniform layer and an adequate interface contact between PDi and TiO2. The obtained PDi/TiO2 junction exhibited broadened visible light absorption, and an effective interface for enhanced photogenerated electron-hole separation, which is supported by the reduced charge transfer resistance and prolonged excitation lifetime via impedance spectroscopy analysis and fluorescence emission decay investigations. Consequently, such a heterojunction photoanode was photoresponsive to a wide visible light region of 400-600 nm, and thus demonstrated a highly enhanced photocurrent density at 1.23 V vs. a reversible hydrogen electrode. Additionally, the durability of such a photoanode can be guaranteed after long-time illumination because of the geometrical restraint imposed by the PDi aggregates. These results pave the way to discover new organic/inorganic assemblies for high-performance photoelectric applications and device integration.Organic/inorganic heterojunction photoanodes are appealing for making concurrent use of the highly photoactive organic semiconductors, and the efficient dielectric screening provided by their inorganic counterparts. In the present work, organic/inorganic nanotube heterojunction arrays composed of TiO2 nanotube arrays and a semiconducting N,N-(dicyclohexyl) perylene-3,4,9,10-tetracarboxylic diimide (PDi

Nanoparticle fractionation using an aligned carbon nanotube array

Energy Technology Data Exchange (ETDEWEB)

Lim Xiaodai [NUS Graduate School for Integrative Sciences and Engineering (NGS), Centre for Life Sciences (CeLS), 05-01, 28 Medical Drive, 117456 (Singapore); Xu Hairuo; Chin, Wee Shong [Department of Chemistry, Faculty of Science, National University of Singapore, 3 Science Drive 3, 117543 (Singapore); Nicole Chew, Yi Hui; Phua, Yi Hui [Dunman High School, 10 Tanjong Rhu Road, 436895 (Singapore); Sie, Edbert Jarvis; Sum, Tze Chien [Division of Physics and Applied Physics, School of Physical and Mathematical Sciences, Nanyang Technological University, 637371 (Singapore); Chia, Guo Hao; Sow, Chorng-Haur, E-mail: chmcws@nus.edu.sg, E-mail: physowch@nus.edu.sg [Department of Physics, Blk S12, Faculty of Science, National University of Singapore, 2 Science Drive 3, 117542 (Singapore)

2010-07-23

A technique utilizing the capillary assisted sieving capability of carbon nanotubes (CNTs) to achieve fractionation of nanoparticles of small size distribution is presented. By dipping aligned CNT arrays into a solution comprising different sized quantum dots (QDs), size-selective gradient decoration of QDs onto CNTs is achieved. The fractionating capability of CNTs is also demonstrated for poly-dispersed manganese doped zinc sulfide nanoparticles and QDs of varying sizes and chemical compositions, which we attribute to the size-selective sieving effect of CNTs. By controlling the terminating point for the flow of QDs across the CNT array, a QD size specific CNT/QD hybrid structure is achieved.

A visible-light-driven composite photocatalyst of TiO2 nanotube arrays and graphene quantum dots

Directory of Open Access Journals (Sweden)

Donald K. L. Chan

2014-05-01

Full Text Available TiO2 nanotube arrays are well-known efficient UV-driven photocatalysts. The incorporation of graphene quantum dots could extend the photo-response of the nanotubes to the visible-light range. Graphene quantum dot-sensitized TiO2 nanotube arrays were synthesized by covalently coupling these two materials. The product was characterized by Fourier-transform infrared spectrometry (FTIR, scanning electron microscopy (SEM, transmission electron microscopy (TEM, X-ray diffraction (XRD, thermogravimetric analysis (TGA and UV–vis absorption spectroscopy. The product exhibited high photocatalytic performance in the photodegradation of methylene blue and enhanced photocurrent under visible light irradiation.

Integrated high-efficiency Pt/carbon nanotube arrays for PEM fuel cells

Energy Technology Data Exchange (ETDEWEB)

Zhang, Weimin; Minett, Andrew I.; Zhao, Jie; Razal, Joselito M.; Wallace, Gordon G.; Romeo, Tony; Chen, Jun [Intelligent Polymer Research Institute, AIIM Facility, Innovation Campus, University of Wollongong, NSW 2522 (Australia); Gao, Mei [Division of Materials Science and Engineering, CSIRO, Bayview Ave, Clayton, VIC 3168 (Australia)

2011-07-15

A facile strategy to deposit Pt nanoparticles with various metal-loading densities on vertically aligned carbon nanotube (ACNT) arrays as electrocatalysts for proton exchange membrane (PEM) fuel cells is described. The deposition is achieved by electrostatic adsorption of the Pt precursor on the positively charged polyelectrolyte functionalized ACNT arrays and subsequent reduction by L-ascorbic acid. The application of the aligned electrocatalysts in fuel cells is realized by transferring from a quartz substrate to nafion membrane using a hot-press procedure to fabricate the membrane electrode assembly (MEA). It is shown that the MEA with vertically aligned structured electrocatalysts provides better Pt utilization than that with Pt on conventional carbon nanotubes or carbon black, resulting in higher fuel cell performance. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Characteristics of N-doped TiO{sub 2} nanotube arrays by N{sub 2}-plasma for visible light-driven photocatalysis

Energy Technology Data Exchange (ETDEWEB)

Liu Xu [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China); Liu Zhongqing, E-mail: 301zql@vip.sina.com [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China); Zheng Jian; Yan Xin; Li Dandan; Chen Si [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China); Chu Wei, E-mail: chuwei1965_scu@yahoo.com [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China)

2011-10-13

Highlights: > A new pathway is provided to prepare N-doped TiO2 nanotube arrays using N{sub 2}-plasma treatment. > N{sub 2}-plasma treatment did not wreck the structure of nanotube arrays. > Nitrogen doping promoted the phase transition to rutile phase at low annealing temperatures > Nitrogen doping narrow band gap of TiO{sub 2} and improve the photocatalytic activity of samples. - Abstract: N-doped TiO{sub 2} nanotube arrays were prepared by electrochemical anode oxidation of Ti foil followed by treatment with N{sub 2}-plasma and subsequent annealed under Ar atmosphere. The morphologies, composition and optical properties of N-doped TiO{sub 2} nanotube arrays were characterized using field-emission scanning electron microscope (FE-SEM), transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction spectrometer (XRD), Photoluminescence (PL) and UV-vis diffusion reflection spectroscopy (UV-vis DRS). Methylene blue (MB) solution was utilized as the degradation model to evaluate the photocatalytic activity of the samples under visible light irradiation. The results suggested N{sub 2}-plasma treatment created doping of nitrogen onto the surface of photoelectrodes successfully and the N-doped TiO{sub 2} nanotube arrays display a significantly enhancement of the photocatalytic activity comparing with the pure TiO{sub 2} nanotube arrays under the visible light irradiation.

WIMP detection and slow ion dynamics in carbon nanotube arrays

International Nuclear Information System (INIS)

Cavoto, G.; Cirillo, E.N.M.; Cocina, F.; Ferretti, J.; Polosa, A.D.

2016-01-01

Large arrays of aligned carbon nanotubes (CNTs), open at one end, could be used as target material for the directional detection of weakly interacting dark matter particles (WIMPs). As a result of a WIMP elastic scattering on a CNT, a carbon ion might be injected in the body of the array and propagate through multiple collisions within the lattice. The ion may eventually emerge from the surface with open end CNTs, provided that its longitudinal momentum is large enough to compensate energy losses and its transverse momentum approaches the channeling conditions in a single CNT. Therefore, the angle formed between the WIMP wind apparent orientation and the direction of parallel carbon nanotube axes must be properly chosen. We focus on very low ion recoil kinetic energies, related to low mass WIMPs (∼ 11 GeV) where most of the existing experiments have low sensitivity. Relying on some exact results on two-dimensional lattices of circular obstacles, we study the low energy ion motion in the transverse plane with respect to CNT directions. New constraints are obtained on how to devise the CNT arrays to maximize the target channeling efficiency. (orig.)

WIMP detection and slow ion dynamics in carbon nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Cavoto, G. [INFN Sezione di Roma, Rome (Italy); Cirillo, E.N.M. [Sapienza Universita di Roma, Dipartimento SBAI, Rome (Italy); Cocina, F. [Sapienza Universita di Roma, Dipartimento di Fisica, Rome (Italy); Ferretti, J. [Sapienza Universita di Roma, Dipartimento di Fisica (Italy); INFN Sezione di Roma, Rome (Italy); Polosa, A.D. [Sapienza Universita di Roma, Dipartimento di Fisica (Italy); CERN, Theory Division, Geneva (Switzerland); INFN Sezione di Roma, Rome (Italy)

2016-06-15

Large arrays of aligned carbon nanotubes (CNTs), open at one end, could be used as target material for the directional detection of weakly interacting dark matter particles (WIMPs). As a result of a WIMP elastic scattering on a CNT, a carbon ion might be injected in the body of the array and propagate through multiple collisions within the lattice. The ion may eventually emerge from the surface with open end CNTs, provided that its longitudinal momentum is large enough to compensate energy losses and its transverse momentum approaches the channeling conditions in a single CNT. Therefore, the angle formed between the WIMP wind apparent orientation and the direction of parallel carbon nanotube axes must be properly chosen. We focus on very low ion recoil kinetic energies, related to low mass WIMPs (∼ 11 GeV) where most of the existing experiments have low sensitivity. Relying on some exact results on two-dimensional lattices of circular obstacles, we study the low energy ion motion in the transverse plane with respect to CNT directions. New constraints are obtained on how to devise the CNT arrays to maximize the target channeling efficiency. (orig.)

WIMP detection and slow ion dynamics in carbon nanotube arrays.

Science.gov (United States)

Cavoto, G; Cirillo, E N M; Cocina, F; Ferretti, J; Polosa, A D

2016-01-01

Large arrays of aligned carbon nanotubes (CNTs), open at one end, could be used as target material for the directional detection of weakly interacting dark matter particles (WIMPs). As a result of a WIMP elastic scattering on a CNT, a carbon ion might be injected in the body of the array and propagate through multiple collisions within the lattice. The ion may eventually emerge from the surface with open end CNTs, provided that its longitudinal momentum is large enough to compensate energy losses and its transverse momentum approaches the channeling conditions in a single CNT. Therefore, the angle formed between the WIMP wind apparent orientation and the direction of parallel carbon nanotube axes must be properly chosen. We focus on very low ion recoil kinetic energies, related to low mass WIMPs ([Formula: see text] GeV) where most of the existing experiments have low sensitivity. Relying on some exact results on two-dimensional lattices of circular obstacles, we study the low energy ion motion in the transverse plane with respect to CNT directions. New constraints are obtained on how to devise the CNT arrays to maximize the target channeling efficiency.

Synthesis and photocatalytic properties of Sn-doped TiO{sub 2} nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Tu Yafang; Huang Shengyou [Department of Physics, Wuhan University, Wuhan 430072 (China); Sang Jianping, E-mail: jpsang@acc-lab.whu.edu.c [Department of Physics, Wuhan University, Wuhan 430072 (China); Department of Physics, Jianghan University, Wuhan 430056 (China); Zou Xianwu [Department of Physics, Wuhan University, Wuhan 430072 (China)

2009-08-12

TiO{sub 2} nanotube arrays doped by Sn up to 12 at% have been prepared using template-based liquid phase deposition method. Their morphologies, structures and optical properties have been investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV-vis absorption spectroscopy and photoluminescence spectroscopy. The photocatalytic properties of the samples were evaluated with the degradation of methylene blue under UV irradiation. The result shows that doping an appropriate amount of Sn can effectively improve the photocatalytic activity of TiO{sub 2} nanotube arrays, and the optimum dopant amount is found to be 5.6 at% in our experiments.

Large-scale aligned silicon carbonitride nanotube arrays: Synthesis, characterization, and field emission property

International Nuclear Information System (INIS)

Liao, L.; Xu, Z.; Liu, K. H.; Wang, W. L.; Liu, S.; Bai, X. D.; Wang, E. G.; Li, J. C.; Liu, C.

2007-01-01

Large-scale aligned silicon carbonitride (SiCN) nanotube arrays have been synthesized by microwave-plasma-assisted chemical vapor deposition using SiH 4 , CH 4 , and N 2 as precursors. The three elements of Si, C, and N are chemically bonded with each other and the nanotube composition can be adjusted by varying the SiH 4 concentration, as revealed by electron energy loss spectroscopy and x-ray photoelectron spectroscopy. The evolution of microstructure of the SiCN nanotubes with different Si concentrations was characterized by high-resolution transmission electron microscopy and Raman spectroscopy. The dependence of field emission characteristics of the SiCN nanotubes on the composition has been investigated. With the increasing Si concentration, the SiCN nanotube exhibits more favorable oxidation resistance, which suggests that SiCN nanotube is a promising candidate as stable field emitter

Preparation of Fe-doped TiO{sub 2} nanotube arrays and their photocatalytic activities under visible light

Energy Technology Data Exchange (ETDEWEB)

Tu, Ya-Fang; Huang, Sheng-You [Department of Physics, Wuhan University, Wuhan 430072 (China); Sang, Jian-Ping, E-mail: jpsang@acc-lab.whu.edu.cn [Department of Physics, Wuhan University, Wuhan 430072 (China); Department of Physics, Jianghan University, Wuhan 430056 (China); Zou, Xian-Wu [Department of Physics, Wuhan University, Wuhan 430072 (China)

2010-02-15

Fe-doped TiO{sub 2} nanotube arrays have been prepared by the template-based liquid phase deposition method. Their morphologies, structures and optical properties were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction and UV-vis absorption spectroscopy. Their photocatalytic activities were evaluated by the degradation of methylene blue under visible light. The UV-vis absorption spectra of the Fe-doped TiO{sub 2} nanotube arrays showed a red shift and an enhancement of the absorption in the visible region compared to the undoped sample. The Fe-doped TiO{sub 2} nanotube arrays exhibited good photocatalytic activities under visible light irradiation, and the optimum dopant amount was found to be 5.9 at% in our experiments.

Fabrication and structural characterization of highly ordered titania nanotube arrays

Science.gov (United States)

Shi, Hongtao; Ordonez, Rosita

Titanium (Ti) dioxide nanotubes have drawn much attention in the past decade due to the fact that titania is an extremely versatile material with a variety of technological applications. Anodizing Ti in different electrolytes has proved to be quite successful so far in creating the nanotubes, however, their degree of order is still not nearly as good as nanoporous anodic alumina. In this work, we first deposit a thin layer of aluminum (Al) onto electropolished Ti substrates, using thermal evaporation. Such an Al layer is then anodized in 0.3 M oxalic acid, forming an ordered nanoporous alumina mask on top of Ti. Afterwards, the anodization of Ti is accomplished at 20 V in solutions containing 1 M NaH2PO4 and 0.5% HF or H2SO4, which results in the creation of ordered titania nanotube arrays. The inner pore diameter of the nanotubes can be tuned from ~50 nm to ~75 nm, depending on the anodization voltage applied to Al or Ti. X-ray diffractometry shows the as-grown titania nanotubes are amorphous. Samples annealed at different temperatures in ambient atmosphere will be also reported.

WIMP detection and slow ion dynamics in carbon nanotube arrays

CERN Document Server

Cavoto, G.; Cocina, F.; Ferretti, J.; Polosa, A.D.

2016-06-24

Large arrays of aligned carbon nanotubes (CNTs), open at one end, could be used as target material for the directional detection of weakly interacting dark matter particles (WIMPs). As a result of a WIMP elastic scattering on a CNT, a carbon ion might be injected in the body of the array and propagate through multiple collisions within the lattice. The ion may eventually emerge from the surface with open end CNTs, provided that its longitudinal momentum is large enough to compensate energy losses and its transverse momentum approaches the channeling conditions in a single CNT. Therefore, the angle formed between the WIMP wind apparent orientation and the direction of parallel carbon nanotube axes must be properly chosen. We focus on very low ion recoil kinetic energies, related to low mass WIMPs (~ 10 GeV) where most of the existing experiments have low sensitivity. Relying on some exact results on two-dimensional lattices of circular obstacles, we study the low energy ion motion in the transverse plane with ...

Dye-sensitized solar cells employing doubly or singly open-ended TiO2 nanotube arrays: structural geometry and charge transport.

Science.gov (United States)

Choi, Jongmin; Song, Seulki; Kang, Gyeongho; Park, Taiho

2014-09-10

We systematically investigated the charge transport properties of doubly or singly open-ended TiO2 nanotube arrays (DNT and SNT, respectively) for their utility as electrodes in dye-sensitized solar cells (DSCs). The SNT or DNT arrays were transferred in a bottom-up (B-up) or top-up (T-up) configuration onto a fluorine-doped tin oxide (FTO) substrate onto which had been deposited a 2 μm thick TiO2 nanoparticle (NP) interlayer. This process yielded four types of DSCs prepared with SNTs (B-up or T-up) or DNT (B-up or T-up). The photovoltaic performances of these DSCs were analyzed by measuring the dependence of the charge transport on the DSC geometry. High resolution scanning electron microscopy techniques were used to characterize the electrode cross sections, and electrochemical impedance spectroscopy was used to characterize the electrical connection at the interface between the NT array and the TiO2 NP interlayer. We examined the effects of decorating the DNT or SNT arrays with small NPs (sNP@DNT and sNP@SNT, respectively) in an effort to increase the extent of dye loading. The DNT arrays decorated with small NPs performed better than the decorated SNT arrays, most likely because the Ti(OH)4 precursor solution flowed freely into the array through the open ends of the NTs in the DNT case but not in the SNT case. The sNP@DNT-based DSC exhibited a better PCE (10%) compared to the sNP@SNT-based DSCs (6.8%) because the electrolyte solution flow was not restricted, direct electron transport though the NT arrays was possible, the electrical connection at the interface between the NT array and the TiO2 NP interlayer was good, and the array provided efficient light harvesting.

Ag2S/CdS/TiO2 Nanotube Array Films with High Photocurrent Density by Spotting Sample Method

OpenAIRE

Sun, Hong; Zhao, Peini; Zhang, Fanjun; Liu, Yuliang; Hao, Jingcheng

2015-01-01

Ag2S/CdS/TiO2 hybrid nanotube array films (Ag2S/CdS/TNTs) were prepared by selectively depositing a narrow-gap semiconductor—Ag2S (0.9 eV) quantum dots (QDs)—in the local domain of the CdS/TiO2 nanotube array films by spotting sample method (SSM). The improvement of sunlight absorption ability and photocurrent density of titanium dioxide (TiO2) nanotube array films (TNTs) which were obtained by anodic oxidation method was realized because of modifying semiconductor QDs. The CdS/TNTs, Ag2S/TNT...

Formation of tin-tin oxide core–shell nanoparticles in the composite SnO{sub 2−x}/nitrogen-doped carbon nanotubes by pulsed ion beam irradiation

Energy Technology Data Exchange (ETDEWEB)

Korusenko, P.M., E-mail: korusenko@obisp.oscsbras.ru [Omsk Scientific Center, Siberian Branch of the Russian Academy of Sciences, Karl Marx avenue 15, 644040 Omsk (Russian Federation); Nesov, S.N.; Bolotov, V.V.; Povoroznyuk, S.N. [Omsk Scientific Center, Siberian Branch of the Russian Academy of Sciences, Karl Marx avenue 15, 644040 Omsk (Russian Federation); Pushkarev, A.I. [National Research Tomsk Polytechnic University, Lenin Ave. 2a, 634028 Tomsk (Russian Federation); Ivlev, K.E. [Omsk Scientific Center, Siberian Branch of the Russian Academy of Sciences, Karl Marx avenue 15, 644040 Omsk (Russian Federation); Smirnov, D.A. [St. Petersburg State University, Lieutenant Shmidt Emb. 11, 198504 St. Petersburg (Russian Federation); Institute of Solid State Physics, Dresden University of Technology, D-01069 Dresden (Germany)

2017-03-01

Highlights: • Original method the formation of core–shell structures by pulsed ion beam is proposed. • The composite SnO{sub 2−x}/N-MWCNTs was irradiated by pulsed ion beam. • Morphology and electronic structure of the irradiated composite were characterized. • The formation of Sn−SnO{sub x} core–shell nanoparticles after irradiation was observed. - Abstract: The complex methods of transmission electron microscopy, energy dispersive X-ray analysis, and X-ray photoelectron spectroscopy were used to investigate the changes in the morphology, phase composition, and electronic structure of the composite SnO{sub 2−x}/nitrogen-doped multiwalled carbon nanotubes (SnO{sub 2−x}/N-MWCNTs) irradiated with the pulsed ion beam of nanosecond duration. The irradiation of the composite SnO{sub 2−x}/N-MWCNTs leads to the formation of nanoparticles with the core–shell structure on the surface of CNTs with a sharp interfacial boundary. It has been established that the “core” is a metal tin (Sn{sup 0}) with a typical size of 5–35 nm, and the “shell” is a thin amorphous layer (2–6 nm) consisting of nonstoichiometric tin oxide with a low oxygen content. The “core–shell” structure Sn−SnO{sub x} is formed due to the process of heating and evaporation of SnO{sub 2−x} under the effect of the ion beam, followed by vapor deposition on the surface of carbon nanotubes.

Synthesis of highly-ordered TiO2 nanotube arrays with tunable sizes

Science.gov (United States)

Wang, Xian; Zha, Chenyang; Ji, Cheng; Zhang, Xiaoyan; Shen, Liming; Wang, Yifeng; Gupta, Arunava; Yoriya, Sorachon; Bao, Ningzhong

2014-09-01

Vertically-oriented one-dimensional TiO2 nanotube (TNT) arrays have been fabricated by anodic oxidation using different electrolyte solvents, including ethylene glycol (EG), diethylene glycol (DEG), and dimethyl sulfoxide (DMSO), in the presence of hydrofluoric acid (HF) or ammonium fluoride (NH4F). The influence of synthetic conditions, including the nature of the electrolyte and anodization voltage, on nanotube microstructure has been systematically investigated. Highly-ordered TNTs with tube length of ˜0.5-26.7 μm, inner diameter of ˜13-201 nm, and outer diameter of ˜28-250 nm have been obtained. The conversion of as-prepared TNT arrays from amorphous phase to crystalline structure has been achieved by a post-synthetic annealing at 500 °C for 3 h in oxygen ambient. The TNT arrays with tunable sizes and structures are attractive for use as electrode materials in fabrication of thin film solar cells and highly active photocatalysts.

Synthesis of highly-ordered TiO2 nanotube arrays with tunable sizes

International Nuclear Information System (INIS)

Wang, Xian; Zha, Chenyang; Ji, Cheng; Zhang, Xiaoyan; Shen, Liming; Wang, Yifeng; Bao, Ningzhong; Gupta, Arunava; Yoriya, Sorachon

2014-01-01

Vertically-oriented one-dimensional TiO 2 nanotube (TNT) arrays have been fabricated by anodic oxidation using different electrolyte solvents, including ethylene glycol (EG), diethylene glycol (DEG), and dimethyl sulfoxide (DMSO), in the presence of hydrofluoric acid (HF) or ammonium fluoride (NH 4 F). The influence of synthetic conditions, including the nature of the electrolyte and anodization voltage, on nanotube microstructure has been systematically investigated. Highly-ordered TNTs with tube length of ∼0.5–26.7 μm, inner diameter of ∼13–201 nm, and outer diameter of ∼28–250 nm have been obtained. The conversion of as-prepared TNT arrays from amorphous phase to crystalline structure has been achieved by a post-synthetic annealing at 500 °C for 3 h in oxygen ambient. The TNT arrays with tunable sizes and structures are attractive for use as electrode materials in fabrication of thin film solar cells and highly active photocatalysts. (paper)

Effect of Source, Surfactant, and Deposition Process on Electronic Properties of Nanotube Arrays

Directory of Open Access Journals (Sweden)

Dheeraj Jain

2011-01-01

Full Text Available The electronic properties of arrays of carbon nanotubes from several different sources differing in the manufacturing process used with a variety of average properties such as length, diameter, and chirality are studied. We used several common surfactants to disperse each of these nanotubes and then deposited them on Si wafers from their aqueous solutions using dielectrophoresis. Transport measurements were performed to compare and determine the effect of different surfactants, deposition processes, and synthesis processes on nanotubes synthesized using CVD, CoMoCAT, laser ablation, and HiPCO.

Magnetic behaviour of arrays of Ni nanowires by electrodeposition into self-aligned titania nanotubes

International Nuclear Information System (INIS)

Prida, V.M.; Hernandez-Velez, M.; Cervera, M.; Pirota, K.; Sanz, R.; Navas, D.; Asenjo, A.; Aranda, P.; Ruiz-Hitzky, E.; Batallan, F.; Vazquez, M.; Hernando, B.; Menendez, A.; Bordel, N.; Pereiro, R.

2005-01-01

Arrays of Ni nanowires electrodeposited into self-aligned and randomly disordered titania nanotube arrays grown by anodization process are investigated by X-ray diffraction, SEM, rf-GDOES and VSM magnetometry. The titania nanotube outer diameter is about 160 nm, wall thickness ranging from 60 to 70 nm and 300 nm in depth. The so-obtained Ni nanowires reach above 100 nm diameter and 240 nm length, giving rise to coercive fields of 98 and 200 Oe in the perpendicular or parallel to the nanowires axis hysteresis loops, respectively. The formation of magnetic vortex domain states is also discussed

Vertically Aligned Carbon Nanotube Array (VANTA Biosensor for MEMS Lab-on-a-Chip

Directory of Open Access Journals (Sweden)

Luke JOSEPH

2009-10-01

Full Text Available We describe the fabrication, functionalization and characterization of vertically aligned carbon nanotube arrays (VANTAs for biological sensor applications. This structure is created using a standard MEMS process and chemical vapor deposition (CVD multi-walled carbon nanotube (MWNT post-processing. The device is well suited for full integration into microfluidic lab-on-a-chip solutions. Included is a spectroscopic characterization of the galvanostatic impedance of the device, as well as scanning electron microscopy (SEM images of the pre- and post- functionalized device. Interferometric 3D profiling and X-ray spectroscopy were also used to check process assumptions. The work presented validates that this approach is an ideal candidate for low-cost, high-throughput manufacturing of biochemical sensors. Unlike previously published work [1, 2] using SWNT, the use of MWNT arrays allows functionalization over the entirety of the nanotubes. This approach maintains low baseline impedance and increases the surface area leveraging inherent benefits of the VANTA.

Enhanced Photocatalytic Properties of Ag-Loaded N-Doped Tio2 Nanotube Arrays

Directory of Open Access Journals (Sweden)

Gao Dawei

2018-03-01

Full Text Available Highly ordered TiO2 nanotube (TiO2 NT arrays were prepared by anodic oxidizing method on the surface of the Ti substrate. Nitrogen-doped TiO2 nanotube (N-TiO2 NT arrays were carried out by ammonia solution immersion, and Ag nanoparticles loaded N-doped TiO2 nanotube (Ag/N-TiO2 NT arrays were obtained by successive ionic layer adsorption and reaction (SILAR technique. The samples were characterized by the X-ray diffraction (XRD, X-ray photoelectron spectroscopy (XPS, field emission scanning electron microscopy (FESEM, high-resolution transmission electron microscopy (HRTEM, photoluminescence (PL emission spectra, ultraviolet–visible (UV–vis diffuse reflectance spectroscopy (DRS. The result indicated that the diameter and wall thickness of the TiO2 NT are 100–120 and 20–30 nm, respectively. Moreover, the morphology and structure of the highly ordered TiO2 NTs were not affected by N-doping. Furthermore, Ag nanoparticles were evenly deposited on the surface of TiO2 NTs in the form of elemental silver. Finally, the photocatalytic activity of Ag/N-TiO2 NTs was evaluated by degradation of methyl orange (MO under visible-light irradiation. The Ag/N-TiO2 NTs exhibited enhanced photocatalytic properties, which could reach 95% after 90-min irradiation.

Interaction of a two-dimensional electromagnetic breather with an electron inhomogeneity in an array of carbon nanotubes

International Nuclear Information System (INIS)

Zhukov, Alexander V.; Bouffanais, Roland; Fedorov, E. G.; Belonenko, Mikhail B.

2014-01-01

Propagation of ultrashort laser pulses through various nano-objects has recently became an attractive topic for both theoretical and experimental studies due to its promising perspectives in a variety of problems of modern nanoelectronics. Here, we study the propagation of extremely short two-dimensional bipolar electromagnetic pulses in a heterogeneous array of semiconductor carbon nanotubes. Heterogeneity is defined as a region of enhanced electron density. The electromagnetic field in an array of nanotubes is described by Maxwell's equations, reduced to a multidimensional wave equation. Our numerical analysis shows the possibility of stable propagation of an electromagnetic pulse in a heterogeneous array of nanotubes. Furthermore, we establish that, depending on its speed of propagation, the pulse can pass through the area of increased electron concentration or be reflected therefrom.

Drying induced upright sliding and reorganization of carbon nanotube arrays

International Nuclear Information System (INIS)

Li Qingwen; De Paula, Raymond; Zhang Xiefei; Zheng Lianxi; Arendt, Paul N; Mueller, Fred M; Zhu, Y T; Tu Yi

2006-01-01

Driven by capillary force, wet carbon nanotube (CNT) arrays have been found to reorganize into cellular structures upon drying. During the reorganization process, individual CNTs are firmly attached to the substrate and have to lie down on the substrate at cell bottoms, forming closed cells. Here we demonstrate that by modifying catalyst structures, the adhesion of CNTs to the substrate can be weakened. Upon drying such CNT arrays, CNTs may slide away from their original sites on the surface and self-assemble into cellular patterns with bottoms open. It is also found that the sliding distance of CNTs increases with array height, and drying millimetre tall arrays leads to the sliding of CNTs over a few hundred micrometres and the eventual self-assembly into discrete islands. By introducing regular vacancies in CNT arrays, CNTs may be manipulated into different patterns

Single-layer graphene-TiO{sub 2} nanotubes array heterojunction for ultraviolet photodetector application

Energy Technology Data Exchange (ETDEWEB)

Zhang, Deng-Yue [School of Material Sciences and Engineering, Hefei University of Technology, Hefei, Anhui 230009 (China); Ge, Cai-Wang [School of Electronic Science and Applied Physics, Hefei University of Technology, Hefei, Anhui 230009 (China); Wang, Jiu-Zhen [School of Material Sciences and Engineering, Hefei University of Technology, Hefei, Anhui 230009 (China); Zhang, Teng-Fei [School of Electronic Science and Applied Physics, Hefei University of Technology, Hefei, Anhui 230009 (China); Wu, Yu-Cheng, E-mail: ycwu@hfut.edu.cn [School of Material Sciences and Engineering, Hefei University of Technology, Hefei, Anhui 230009 (China); Liang, Feng-Xia, E-mail: fxliang@hfut.edu.cn [School of Material Sciences and Engineering, Hefei University of Technology, Hefei, Anhui 230009 (China)

2016-11-30

Highlights: • Heterostructures comprised of a single-layer graphene and TiO{sub 2} nanotube arrays were constructed for ultraviolet detection. • The electrical properties of the fabricated heterostructures were dependent on the annealing atmospheres. • The effect of anodic TiO{sub 2} nanotube length on the performance of the photodetector were investigated. - Abstract: In this work, we reported on the fabrication of a single-layer graphene (SLG)-TiO{sub 2} nanotube arrays (NTs) heterostructures ultraviolet photodetector (UVPD) by transferring chemical vapor deposition derived MLG on the surface of anodic TiO{sub 2}NTs array. Through varying the annealing atmosphere and anodization time in the TiO{sub 2} synthesis procedure, the electronic and optoelectronic properties of the as-fabricated Schottky junction UVPD were studied. It was revealed that the anodic TiO{sub 2}NTs annealed in air showed a better rectifying behavior and was highly sensitive to UV light irradiation. Further investigation found that the device performance of the UVPD can be readily modulated by the anodization time, and the anodic TiO{sub 2}NTs with a medium tube length of 9.6 μm exhibits the highest device performance. These results demonstrated that the present SLG-TiO{sub 2}NTs array hetero-junction UVPD will be highly promising for fabricating high-performance optoelectronic device and system in the future.

Polyoxometalate-modified TiO2 nanotube arrays photoanode materials for enhanced dye-sensitized solar cells

Science.gov (United States)

Liu, Ran; Sun, Zhixia; Zhang, Yuzhuo; Xu, Lin; Li, Na

2017-10-01

In this work, we prepared for the first time the TiO2 nanotube arrays (TNAs) photoanode with polyoxometalate(POMs)-modified TiO2 electron-transport layer for improving the performance of zinc phthalocyanine(ZnPc)-sensitized solar cells. The as-prepared POMs/TNAs/ZnPc composite photoanode exhibited higher photovoltaic performances than the TNAs/ZnPc photoanode, so that the power conversion efficiency of the solar cell device based on the POMs/TNAs/ZnPc photoanode displayed a notable improvement of 45%. These results indicated that the POMs play a key role in reducing charge recombination in phthalocyanine-sensitized solar cells, together with TiO2 nanotube arrays being helpful for electron transport. The mechanism of the performance improvement was demonstrated by the measurements of electrochemical impedance spectra and open-circuit voltage decay curves. Although the resulting performance is still below that of the state-of-the-art dye-sensitized solar cells, this study presents a new insight into improving the power conversion efficiency of phthalocyanine-sensitized solar cells via polyoxometalate-modified TiO2 nanotube arrays photoanode.

Surface-restrained growth of vertically aligned carbon nanotube arrays with excellent thermal transport performance.

Science.gov (United States)

Ping, Linquan; Hou, Peng-Xiang; Liu, Chang; Li, Jincheng; Zhao, Yang; Zhang, Feng; Ma, Chaoqun; Tai, Kaiping; Cong, Hongtao; Cheng, Hui-Ming

2017-06-22

A vertically aligned carbon nanotube (VACNT) array is a promising candidate for a high-performance thermal interface material in high-power microprocessors due to its excellent thermal transport property. However, its rough and entangled free tips always cause poor interfacial contact, which results in serious contact resistance dominating the total thermal resistance. Here, we employed a thin carbon cover to restrain the disorderly growth of the free tips of a VACNT array. As a result, all the free tips are seamlessly connected by this thin carbon cover and the top surface of the array is smoothed. This unique structure guarantees the participation of all the carbon nanotubes in the array in the heat transport. Consequently the VACNT array grown on a Cu substrate shows a record low thermal resistance of 0.8 mm 2 K W -1 including the two-sided contact resistances, which is 4 times lower than the best result previously reported. Remarkably, the VACNT array can be easily peeled away from the Cu substrate and act as a thermal pad with excellent flexibility, adhesive ability and heat transport capability. As a result the CNT array with a thin carbon cover shows great potential for use as a high-performance flexible thermal interface material.

P25 nanoparticles decorated on titania nanotubes arrays as effective drug delivery system for ibuprofen

Energy Technology Data Exchange (ETDEWEB)

Wang, Zhang; Xie, Chunlin; Luo, Fei; Li, Ping; Xiao, Xiufeng, E-mail: xfxiao@fjnu.edu.cn

2015-01-01

Highlights: • P25 nanoparticles decorated on titania nanotube arrays were prepared by hydrothermal treatment. • P25 nanoparticles were conducive to improve the loading effect of ibuprofen into nanotube arrays. • The diameters of the decorated nanotubes were decrease markedly which led to an effective and prolonged drug release. - Abstract: In this study, uniformly distributed layer of P25 nanoparticles (NPs) decorated on titania (TiO{sub 2}) nanotubes (TNTs) arrays was prepared in a teflon-lined stainless steel autoclave by the hydrothermal treatment. To investigate the influence of the P25 concentration, different concentrations of P25 NPs were added into the solution to obtain the optimal decorative effect. TNTs decorated with P25 (TNTs–P25) and TNTs without P25 decorated on its surface were loaded with ibuprofen (IBU) via vacuum drying and its release properties were investigated. The samples were characterized by field emission scanning electron microscopy, X-ray diffraction, and Fourier transform infrared spectroscopy. The results indicated that P25 NPs were successfully decorated on the surface of TNTs by hydrothermal method and the optimal concentration was found to be 7.5 × 10{sup −4} M. P25 NPs decorated on TNTs led to a significant increase in the specific surface area of TNTs which was conducive to improve the loading effect of IBU. Importantly, the diameters of the decorated nanotubes were reduced to 100 ± 10 nm and the increase in roughness led to an effective and prolonged drug release.

Nanomanipulation of 2 inch wafer fabrication of vertically aligned carbon nanotube arrays by nanoimprint lithography

DEFF Research Database (Denmark)

Bu, Ian Y. Y.; Eichhorn, Volkmar; Carlson, Kenneth

2011-01-01

Carbon nanotube (CNT) arrays are typically defined by electron beam lithography (EBL), and hence limited to small areas due to the low throughput. To obtain wafer‐scale fabrication we propose large area thermal nanoimprint lithography (NIL). A 2‐inch stamp master is defined using EBL for subsequent......, efficient production of wafer‐scale/larger arrays of CNTs has been achieved. The CNTs have been deposited by wafer‐scale plasma enhanced chemical vapour deposition (PECVD) of C2H2/NH3. Substrates containing such nanotubes have been used to automate nanorobotic manipulation sequences of individual CNTs...

Modelling clustering of vertically aligned carbon nanotube arrays.

Science.gov (United States)

Schaber, Clemens F; Filippov, Alexander E; Heinlein, Thorsten; Schneider, Jörg J; Gorb, Stanislav N

2015-08-06

Previous research demonstrated that arrays of vertically aligned carbon nanotubes (VACNTs) exhibit strong frictional properties. Experiments indicated a strong decrease of the friction coefficient from the first to the second sliding cycle in repetitive measurements on the same VACNT spot, but stable values in consecutive cycles. VACNTs form clusters under shear applied during friction tests, and self-organization stabilizes the mechanical properties of the arrays. With increasing load in the range between 300 µN and 4 mN applied normally to the array surface during friction tests the size of the clusters increases, while the coefficient of friction decreases. To better understand the experimentally obtained results, we formulated and numerically studied a minimalistic model, which reproduces the main features of the system with a minimum of adjustable parameters. We calculate the van der Waals forces between the spherical friction probe and bunches of the arrays using the well-known Morse potential function to predict the number of clusters, their size, instantaneous and mean friction forces and the behaviour of the VACNTs during consecutive sliding cycles and at different normal loads. The data obtained by the model calculations coincide very well with the experimental data and can help in adapting VACNT arrays for biomimetic applications.

Transmission properties of terahertz waves through asymmetric rectangular aperture arrays on carbon nanotube films

Directory of Open Access Journals (Sweden)

Yue Wang

2016-04-01

Full Text Available Transmission spectra of terahertz waves through a two-dimensional array of asymmetric rectangular apertures on super-aligned multi-walled carbon nanotube films were obtained experimentally. In this way, the anisotropic transmission phenomena of carbon nanotube films were observed. For a terahertz wave polarization parallel to the orientation of the carbon nanotubes and along the aperture short axis, sharp resonances were observed and the resonance frequencies coincided well with the surface plasmon polariton theory. In addition, the minima of the transmission spectra were in agreement with the location predicted by the theory of Wood’s anomalies. Furthermore, it was found that the resonance profiles through the carbon nanotube films could be well described by the Fano model.

Optical properties of TiO2 nanotube arrays fabricated by the electrochemical anodization method

International Nuclear Information System (INIS)

Ly, Ngoc Tai; Nguyen, Van Chien; Dao, Thi Hoa; Hoang To, Le Hong; Pham, Duy Long; Do, Hung Manh; Vu, Dinh Lam; Le, Van Hong

2014-01-01

Perpendicularly self-aligned TiO 2 nanotube samples of size of 3 × 5 cm 2 were fabricated by the electrochemical anodization method using a solution containing NH 4 F. Influences of the technological conditions such as NH 4 F concentration and anodization voltage were studied. It was found that NH 4 F concentration in the solution and anodization voltage significantly affect the diameter and length of a TiO 2 nanotube. The diameter and the length of a TiO 2 nanotube were observed and estimated by using scanning electron microscopy. It has shown that the largest diameter and the longest length of about 80 nm and 20 μm, respectively, were obtained for the sample anodized in a solution containing 0.4% of NH 4 F, under a voltage of 48 V. Photoluminescence spectra excited by laser lights having wavelengths of 325 and 442 nm (having energies higher and lower than the band gap energy of TiO 2 ) was recorded at room temperature for the TiO 2 nanotube arrays. An abnormal luminescence result was observed. It is experimental evidence that the manufactured TiO 2 nanotube array is an expected material for hydrogen splitting from water by photochemical effect under sunlight as well as for the nano solar cells. (paper)

Photocatalytic methane decomposition over vertically aligned transparent TiO2 nanotube arrays

DEFF Research Database (Denmark)

In, Su-il; Nielsen, Morten Godtfred; Vesborg, Peter Christian Kjærgaard

2011-01-01

Vertically aligned transparent TiO2 nanotube arrays grown by the one-step anodic oxidation technique (on non-conductive supports such as Pyrex) and their photocatalytic performance for methane decomposition in a single-pass micro-fabricated reactor under UV light....

Inkjet printed ambipolar transistors and inverters based on carbon nanotube/zinc tin oxide heterostructures

Energy Technology Data Exchange (ETDEWEB)

Kim, Bongjun; Jang, Seonpil; Dodabalapur, Ananth, E-mail: ananth.dodabalapur@engr.utexas.edu [Microelectronics Research Center, The University of Texas at Austin, Austin, Texas 78758 (United States); Department of Electrical and Computer Engineering, The University of Texas at Austin, Austin, Texas 78712 (United States); Geier, Michael L.; Prabhumirashi, Pradyumna L. [Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois 60208 (United States); Hersam, Mark C. [Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois 60208 (United States); Department of Chemistry, Northwestern University, Evanston, Illinois 60208 (United States); Department of Medicine, Northwestern University, Evanston, Illinois 60208 (United States)

2014-02-10

We report ambipolar field-effect transistors (FETs) consisting of inkjet printed semiconductor bilayer heterostructures utilizing semiconducting single-walled carbon nanotubes (SWCNTs) and amorphous zinc tin oxide (ZTO). The bilayer structure allows for electron transport to occur principally in the amorphous oxide layer and hole transport to occur exclusively in the SWCNT layer. This results in balanced electron and hole mobilities exceeding 2 cm{sup 2} V{sup −1} s{sup −1} at low operating voltages (<5 V) in air. We further show that the SWCNT-ZTO hybrid ambipolar FETs can be integrated into functional inverter circuits that display high peak gain (>10). This work provides a pathway for realizing solution processable, inkjet printable, large area electronic devices, and systems based on SWCNT-amorphous oxide heterostructures.

Investigation of the influence of geometric parameters of carbon nanotube arrays on their adhesion properties

Science.gov (United States)

Il’ina, M. V.; Konshin, A. A.; Il’in, O. I.; Rudyk, N. N.; Fedotov, A. A.; Ageev, O. A.

2018-03-01

The results of experimental studies of adhesion of carbon nanotube (CNT) arrays with different geometric parameters and orientations using atomic-force microscopy are presented. The adhesion values of CNT arrays were determined, which were from 82 to 1315 nN depending on the parameters of the array. As a result, it was established that the adhesion of a CNT array increases with an increase in branching and disorientation of the array, as well as with the growth of the aspect ratio of CNTs in the array.

Fabrication of Arrays of Metal and Metal Oxide Nanotubes by Shadow Evaporation

NARCIS (Netherlands)

Dickey, Michael D.; Weiss, Emily A.; Smythe, Elizabeth J.; Chiechi, Ryan C.; Capasso, Federico; Whitesides, George M.

2008-01-01

This paper describes a simple technique for fabricating uniform arrays of metal and metal oxide nanotubes with controlled heights and diameters. The technique involves depositing material onto an anodized aluminum oxide (AAO) membrane template using a collimated electron beam evaporation source. The

Effect of alignment on adsorption characteristics of self-oriented multi-walled carbon nanotube arrays

International Nuclear Information System (INIS)

Zilli, D; Bonelli, P R; Cukierman, A L

2006-01-01

The adsorption characteristics of self-oriented multi-walled carbon nanotube (MWCNT) arrays are examined from N 2 (-196 deg. C) adsorption measurements. The arrays were synthesized in a laboratory by in situ chemical vapour deposition of iron or cobalt phthalocyanines at 880 and 950 deg. C, under otherwise constant conditions, in an attempt to obtain different morphological structures. For both precursors, increasing the temperature leads to MWCNT arrays with lower Brunauer-Emmett-Teller (BET) surface area and total pore volume, though the effect is more pronounced for those arising from the iron-based compound. Despite this, precursor yields of individual nanotubes of larger diameter, higher BET area and total pore volume characterize the resulting arrays compared to those arising from cobalt phthalocyanine for the same temperatures. As evidenced by SEM and TEM images, the arrays synthesized from iron phthalocyanine at 880 deg. C show better vertical alignment and denser structures than those obtained from this compound at 950 deg. C, and also from cobalt phthalocyanine at both temperatures. Further ultrasonication of the arrays produced from the iron compound brings about a significant reduction in their adsorption capacity, attributable to the pronounced disarrangement of the resulting structures. The present results demonstrate that the alignment of MWCNT arrays plays a crucial role in their N 2 adsorption characteristics

Interface feature characterization and Schottky interfacial layer confirmation of TiO{sub 2} nanotube array film

Energy Technology Data Exchange (ETDEWEB)

Li, Hongchao [State Key Laboratory of Powder Metallurgy, Central South University, 410083 Changsha (China); Chongyi Zhangyuan Tungsten Industry Corporation Limited, 341300 Ganzhou (China); Tang, Ningxin; Yang, Hongzhi; Leng, Xian [State Key Laboratory of Powder Metallurgy, Central South University, 410083 Changsha (China); Zou, Jianpeng, E-mail: zoujp@csu.edu.cn [State Key Laboratory of Powder Metallurgy, Central South University, 410083 Changsha (China)

2015-11-15

Highlights: • Interfacial fusion of TiO{sub 2} nanotube film increases with annealing temperature. • Interface bonding force of the film increases with annealing temperature. • We report the forth stage of nanofibers formation in the growing mechanism. • TiO{sub 2} nanotubes grow from Schottky interface layer rather than from Ti substrate. • Schottky interface layer's thickness of 35–45 nm is half the diameter of nanotube. - Abstract: We report here characterization of the interfacial microstructure and properties of titanium dioxide (TiO{sub 2}) nanotube array films fabricated by anodization. Field effect scanning electron microscopy (FESEM), X-ray diffraction (XRD), nanoindentation, atomic force microscopy (AFM), selected area electron diffraction (SAED), and high-resolution transmission electron microscopy (HRTEM) were used to characterize the interface of the film. With increasing annealing temperature from 200 °C to 800 °C, the interfacial fusion between the film and the Ti substrate increased. The phase transformation of the TiO{sub 2} nanotube film from amorphous to anatase to rutile took place gradually; as the phase transformation progressed, the force needed to break the film increased. The growth of TiO{sub 2} nanotube arrays occurs in four stages: barrier layer formation, penetrating micropore formation, regular nanotube formation, and nanofiber formation. The TiO{sub 2} nanotubes grow from the Schottky interface layer rather than from the Ti substrate. The Schottky interface layer's thickness of 35–45 nm was identified as half the diameter of the corresponding nanotube, which shows good agreement to the Schottky interface layer growth model. The TiO{sub 2} nanotube film was amorphous and the Ti substrate was highly crystallized with many dislocation walls.

Sol-gel auto-combustion synthesis of hydroxyapatite nanotubes array in porous alumina template

International Nuclear Information System (INIS)

Yuan Yuan; Liu Changsheng; Zhang Yuan; Shan Xiaoqian

2008-01-01

In this paper, an array of highly ordered hydroxyapatite (HAP) nanotubes was synthesized by sol-gel auto-combustion method with porous anodic aluminum oxide (AAO) template for the first time. Based on thermogravimetry (DTA/TG), Fourier transform infrared (FTIR) and X-ray diffraction (XRD), the dried gel, derived from the sol solution with Ca(NO 3 ) 2 .4H 2 O and PO(CH 3 O) 3 as precursors and ethylene glycol as the polymeric matrix, exhibited a typical self-propagating combustion behavior at low temperature, directly resulting in hexagonal crystalline HAP materials. The resultant HAP arrays fabricated from the above sol-gel in the AAO template were uniformly distributed, highly ordered nanotubes with uniform length and diameter according to the observations of scanning electron microscopy (SEM) and transmission electron microscope (TEM). The electron diffraction (ED), XRD and X-ray photoelectron spectroscopy (XPS) survey proved the formation of HAP phase with polycrystalline structure in the AAO template. Based on these results, a potential mechanism of 'an auto-combustion from dried gel to nanoparticles and a subsequent in situ reaction from nanoparticles to nanotubes' was proposed

Effects of carbon nanotube arrays on nucleate pool boiling

OpenAIRE

Ujereh, Sebastine; Fisher, Timothy; Mudawar, Issam

2007-01-01

Experiments were performed to assess the impact coating silicon and copper substrates with nanotubes (CNTs) have on pool boiling performance. Different CNT array densities and area coverages were tested on 1.27 1.27 mm2 samples in FC-72. The CNT preparation techniques used provided strong adherence of CNTs to both substrate materials. Very small contact angle enabled deep penetration of FC-72 liquid inside surface cavities of smooth uncoated silicon surfaces, requiring unusually high surface...

Enhancement in photo-electrochemical efficiency by reducing recombination rate in branched TiO2 nanotube array on functionalizing with ZnO micro crystals

Science.gov (United States)

Boda, Muzaffar Ahmad; Ashraf Shah, Mohammad

2018-06-01

In this study, branched TiO2 nanotube array were fabricated through electrochemical anodization process at constant voltage using third generation electrolyte. On account of morphological advantage, these nanotubes shows significant enhancement in photo-electrochemical property than compact or conventional titania nanotube array. However, their photo-electrochemical efficiency intensifies on coating with ZnO micro-crystals. ZnO coated branched TiO2 nanotube array shows a photocurrent density of 27.8 mA cm‑2 which is 1.55 times the photocurrent density (17.2 mA cm‑2) shown by bare branched titania nanotubes. The significant enhancement in photocurrent density shown by the resulting ZnO/TiO2 hybrid structure is attributed to suppression in electron–hole recombination phenomenon by offering smooth pathway to photo generated excitons on account of staggered band edge positions in individual semiconductors.

Propagation of three-dimensional bipolar ultrashort electromagnetic pulses in an inhomogeneous array of carbon nanotubes

Science.gov (United States)

Fedorov, Eduard G.; Zhukov, Alexander V.; Bouffanais, Roland; Timashkov, Alexander P.; Malomed, Boris A.; Leblond, Hervé; Mihalache, Dumitru; Rosanov, Nikolay N.; Belonenko, Mikhail B.

2018-04-01

We study the propagation of three-dimensional (3D) bipolar ultrashort electromagnetic pulses in an inhomogeneous array of semiconductor carbon nanotubes. The heterogeneity is represented by a planar region with an increased concentration of conduction electrons. The evolution of the electromagnetic field and electron concentration in the sample are governed by the Maxwell's equations and continuity equation. In particular, nonuniformity of the electromagnetic field along the axis of the nanotubes is taken into account. We demonstrate that depending on values of the parameters of the electromagnetic pulse approaching the region with the higher electron concentration, the pulse is either reflected from the region or passes it. Specifically, our simulations demonstrate that after interacting with the higher-concentration area, the pulse can propagate steadily, without significant spreading. The possibility of such ultrashort electromagnetic pulses propagating in arrays of carbon nanotubes over distances significantly exceeding characteristic dimensions of the pulses makes it possible to consider them as 3D solitons.

Double-sided anodic titania nanotube arrays: a lopsided growth process.

Science.gov (United States)

Sun, Lidong; Zhang, Sam; Sun, Xiao Wei; Wang, Xiaoyan; Cai, Yanli

2010-12-07

In the past decade, the pore diameter of anodic titania nanotubes was reported to be influenced by a number of factors in organic electrolyte, for example, applied potential, working distance, water content, and temperature. All these were closely related to potential drop in the organic electrolyte. In this work, the essential role of electric field originating from the potential drop was directly revealed for the first time using a simple two-electrode anodizing method. Anodic titania nanotube arrays were grown simultaneously at both sides of a titanium foil, with tube length being longer at the front side than that at the back side. This lopsided growth was attributed to the higher ionic flux induced by electric field at the front side. Accordingly, the nanotube length was further tailored to be comparable at both sides by modulating the electric field. These results are promising to be used in parallel configuration dye-sensitized solar cells, water splitting, and gas sensors, as a result of high surface area produced by the double-sided architecture.

Ti/TiO 2 nanotube array electrode as a new sensor to ...

Indian Academy of Sciences (India)

The Ti/TiO2 nanotube array (Ti-NTA) electrode was prepared by anodizing of the Ti foil ... and the pH=3.0 and =1.0 V (vs. reference electrode) were determined as the ... It was found that the photocurrent of EG was linearly dependent on the ...

Using Ag-embedded TiO{sub 2} nanotubes array as recyclable SERS substrate

Energy Technology Data Exchange (ETDEWEB)

Ling, Yunhan, E-mail: yhling@mail.tsinghua.edu.cn [Lab of Advanced Materials, School of Materials Science & Engineering, Tsinghua University, Beijing 100084 (China); Zhuo, Yuqing; Huang, Liang [Lab of Advanced Materials, School of Materials Science & Engineering, Tsinghua University, Beijing 100084 (China); Mao, Duolu [School of Physical and Electronic Information Engineering, Qinghai Nationalities University, Xining, Qinghai 810007 (China)

2016-12-01

Highlights: • Ag embedded nanoparticles inside nanotube have better SERS enhancement than surface cap. • Ag NPs reconstruction via self-migration with UV and humidity control. • Self-cleaning effects both on organic molecule photo-oxidation as well as Ag ions photo-reduction. - Abstract: A simple strategy for synthesizing Ag-loaded TiO{sub 2} nanotube film for use as multifunctional photocatalyst and recyclable surface-enhanced Raman scattering (SERS) substrate is introduced. Highly aligned TiO{sub 2} nanotube arrays (TNTA) prepared via electrochemical anodization were used as a 3D rough host for silver nanoparticles. Ag deposits were sputtered in a vacuum, and it was found that their morphologies were mainly influenced by the diameters of nanotubes and the UV irradiation induced aging process, especially the self-migration of silver along the tubular wall. SERS and the self-cleaning effect were observed using Rhodamine 6G (R6G) as the probe molecule. The results showed that narrow nanotube and silver nanoparticles embedment contributed significantly to both the phenomenal SERS and recyclability.

Control of neuronal network organization by chemical surface functionalization of multi-walled carbon nanotube arrays

International Nuclear Information System (INIS)

Liu Jie; Bibari, Olivier; Marchand, Gilles; Benabid, Alim-Louis; Sauter-Starace, Fabien; Appaix, Florence; De Waard, Michel

2011-01-01

Carbon nanotube substrates are promising candidates for biological applications and devices. Interfacing of these carbon nanotubes with neurons can be controlled by chemical modifications. In this study, we investigated how chemical surface functionalization of multi-walled carbon nanotube arrays (MWNT-A) influences neuronal adhesion and network organization. Functionalization of MWNT-A dramatically modifies the length of neurite fascicles, cluster inter-connection success rate, and the percentage of neurites that escape from the clusters. We propose that chemical functionalization represents a method of choice for developing applications in which neuronal patterning on MWNT-A substrates is required.

Control of neuronal network organization by chemical surface functionalization of multi-walled carbon nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Liu Jie; Bibari, Olivier; Marchand, Gilles; Benabid, Alim-Louis; Sauter-Starace, Fabien [CEA, LETI-Minatec, 17 Rue des Martyrs, 38054 Grenoble Cedex 9 (France); Appaix, Florence; De Waard, Michel, E-mail: fabien.sauter@cea.fr, E-mail: michel.dewaard@ujf-grenoble.fr [Inserm U836, Grenoble Institute of Neuroscience, Site Sante la Tronche, Batiment Edmond J Safra, Chemin Fortune Ferrini, BP170, 38042 Grenoble Cedex 09 (France)

2011-05-13

Carbon nanotube substrates are promising candidates for biological applications and devices. Interfacing of these carbon nanotubes with neurons can be controlled by chemical modifications. In this study, we investigated how chemical surface functionalization of multi-walled carbon nanotube arrays (MWNT-A) influences neuronal adhesion and network organization. Functionalization of MWNT-A dramatically modifies the length of neurite fascicles, cluster inter-connection success rate, and the percentage of neurites that escape from the clusters. We propose that chemical functionalization represents a method of choice for developing applications in which neuronal patterning on MWNT-A substrates is required.

Visible-light-driven photoelectrochemical and photocatalytic performances of Cr-doped SrTiO3/TiO2 heterostructured nanotube arrays.

Science.gov (United States)

Jiao, Zhengbo; Chen, Tao; Xiong, Jinyan; Wang, Teng; Lu, Gongxuan; Ye, Jinhua; Bi, Yingpu

2013-01-01

Well-aligned TiO2 nanotube arrays have become of increasing significance because of their unique highly ordered array structure, high specific surface area, unidirectional charge transfer and transportation features. However, their poor visible light utilization as well as the high recombination rate of photoexcited electron-hole pairs greatly limited their practical applications. Herein, we demonstrate the fabrication of visible-light-responsive heterostructured Cr-doped SrTiO3/TiO2 nanotube arrays by a simple hydrothermal method, which facilitate efficient charge separation and thus improve the photoelectrochemical as well as photocatalytic performances.

INFLUENCE OF IONIZING IRRADIATION ON THE PARAMETERS OF ZN NANOTUBES ARRAYS FOR DESIGN OF FLEXIBLE ELECTRONICS ELEMENTS

Directory of Open Access Journals (Sweden)

D. B. Kadyrzhanov

2018-01-01

Full Text Available The aim of the study is establishing the possibility of using Zn nanotube arrays as a basis for design compact and lightweight elements of flexible electronics, including operating under influence of ionizing irradiation.The paper presents the results of the synthesis of Zn nanotubes obtained by electrochemical deposition in the pores of polymer matrices and the study of their structural and electrophysical properties after directional modification by ionizing radiation with different doses. Using the methods of scanning electron microscopy, X-ray diffraction and energy dispersive analysis, the structure of nanotubes having a polycrystalline structure and completely consisting of zinc was studied and it was demonstrated that irradiation with Ar8+ ions with a dose from 1 × 109 to 5 × 1011 ion/cm2 and energy 1.75 MeV/nucleon has an effect on the crystal structure of nanotubes.At high doses, localized highly defect zones arise, leading to a critical change in the structure and physical properties of the nanotubes, respectively. It is shown that the consequence of the modification of the crystal structure is a change in the electrical conductivity of nanotubes: at low doses the electrical conductivity increases, but when the threshold value is reached, it sharply decreases. The change in the crystal structure and the corresponding changes in the conductive properties of Zn nanotubes due to irradiation determine the mechanism of ionizing radiation influence on nanomaterials and determine the possibility of using Zn nanotubes arrays as a basis for creating compact and lightweight elements of flexible electronics.

Fabrication of polyaniline/graphene/titania nanotube arrays nanocomposite and their application in supercapacitors

International Nuclear Information System (INIS)

Huang, Hua; Gan, Mengyu; Ma, Li; Yu, Lei; Hu, Haifeng; Yang, Fangfang; Li, Yanjun; Ge, Chengqiang

2015-01-01

Highlights: • The PANI/graphene/TiO 2 nanotube arrays were fabricated firstly. • The composite shows a high specific capacitance and superior rate capability. • A high capacity retention rate of 91% after 1000 cycles can be achieved. • The composite possesses a novel three-dimensional (3D) highly ordered nanostructure. • TiO 2 NTs enhance the adhesion between PANI and substrate. - Abstract: Polyaniline/graphene/titania nanotube arrays (PGTNs) nanocomposite as a supercapacitor electrode is fabricated by in-situ polymerization for the first time. Herein, the PGTNs possesses a novel three-dimensional (3D) highly ordered hybrid nanostructure consisting of coaxial polyaniline (PANI)/TiO 2 nanotube arrays and graphene coated with PANI on the surface of TiO 2 in some degree. The synthesized three-dimensional PGTNs is characterized by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and Raman spectroscopy, and its electrochemical performance is measured by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and galvanostatic charge/discharge. The maximum specific capacitance of PGTNs is as high as 933 F g −1 at current density of 0.75 A g −1 and the specific capacitance retains 91% of the initial after constant charge–discharge 1000 cycles. The improved electrochemical performance is due to the 3D nanostructure, which effectively prevents the mechanical deformation during the fast charge/discharge process and favors the diffusion of the electrolyte ions into the inner region of active materials. The composite electrode material is very promising for the next generation of high-performance electrochemical supercapacitors

In-vitro bioactivity and electrochemical behavior of polyaniline encapsulated titania nanotube arrays for biomedical applications

Science.gov (United States)

Agilan, P.; Rajendran, N.

2018-05-01

Titania nanotube arrays (TNTA) have attracted increasing attention due to their outstanding properties and potential applications in biomedical field. Fabrication of titania nanotubes on titanium surface enhances the biocompatibility. Polyaniline (PANI) is one of the best conducting polymers with remarkable corrosion resistance and reasonable biocompatibility. In this work, the corrosion resistance and biocompatibility of polyaniline encapsulated TiO2 nanotubes for orthopaedic applications were investigated. The vertically oriented, highly ordered TiO2 nanotubes were fabricated on titanium by electrochemical anodization process using fluoride containing electrolytes. The anodization parameters viz., voltage, pH, time and electrolyte concentration were optimized to get orderly arranged TNTA. Further, the conducting polymer PANI was encapsulated on TNTA by electropolymerization process to enhance the corrosion resistance. The nanostructure of the fabricated TNTA and polyaniline encapsulated titania nanotube arrays (PANI-TNTA) were investigated by HR SEM analysis. The formed phases and functional groups were find using XRD, ATR-FTIR. The hydrophilic surface of TNTA and PANI-TNTA was identified by water contact angle studies. The corrosion behavior of specimens was evaluated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization studies. In-vitro immersion studies were carried out in simulated body fluid solution (Hanks' solution) to evaluate the bioactivity of the TNTA and PANI-TNTA. The surface morphological studies revealed the formation of PANI on the TNTA surface. Formation of hydroxyapatite (HAp) on the surfaces of TNTA and PANI-TNTA enhanced the bioactivity and corrosion resistance.

Sensitivity, selectivity and stability of tin oxide nanostructures on large area arrays of microhotplates

Science.gov (United States)

Panchapakesan, Balaji; Cavicchi, Richard; Semancik, Steve; DeVoe, Don L.

2006-01-01

In this paper, the sensitivity, stability and selectivity of nanoparticle engineered tin oxide (SnO2) are reported, for microhotplate chemical sensing applications. 16 Å of metals such as nickel, cobalt, iron, copper and silver were selectively evaporated onto each column of the microhotplate array. Following evaporation, the microhotplates were heated to 500 °C and SnO2 was deposited on top of the microhotplates using a self-aligned chemical vapour deposition process. Scanning electron microscopy characterization revealed control of SnO2 nanostructures in the range of 20-121 nm. Gas sensing in seven different hydrocarbons revealed that metal nanoparticles that helped in producing faster nucleation of SnO2 resulted in smaller grain size and higher sensitivity. Sensitivity as a function of concentration and grain size is addressed for tin oxide nanostructures. Smaller grain sizes resulted in higher sensitivity of tin oxide nanostructures. Temperature programmed sensing of the devices yielded shape differences in the response between air and methanol, illustrating selectivity. Spiderweb plots were used to monitor the materials programmed selectivity. The shape differences between different gases in spiderweb plots illustrate materials selectivity as a powerful mapping approach for monitoring selectivity in various gases. Continuous monitoring in 80 ppm methanol yielded stable sensor response for more than 200 h. This comprehensive study illustrates the use of a nanoparticle engineering approach for sensitive, selective and stable gas sensing applications.

Force sensitive carbon nanotube arrays for biologically inspired airflow sensing

International Nuclear Information System (INIS)

Maschmann, Matthew R; Ehlert, Gregory J; Baur, Jeffery W; Dickinson, Ben

2012-01-01

The compressive electromechanical response of aligned carbon nanotube (CNT) arrays is evaluated for use as an artificial hair sensor (AHS) transduction element. CNT arrays with heights of 12, 75, and 225 µm are examined. The quasi-static and dynamic sensitivity to force, response time, and signal drift are examined within the range of applied stresses predicted by a mechanical model applicable to the conceptual CNT array-based AHS (0–1 kPa). Each array is highly sensitive to compressive loading, with a maximum observed gauge factor of 114. The arrays demonstrate a repeatable response to dynamic cycling after a break-in period of approximately 50 cycles. Utilizing a four-wire measurement electrode configuration, the change in contact resistance between the array and the electrodes is observed to dominate the electromechanical response of the arrays. The response time of the CNT arrays is of the order of 10 ms. When the arrays are subjected to constant stress, mechanical creep is observed that results in a signal drift that generally diminishes the responsiveness of the arrays, particularly at stress approaching 1 kPa. The results of this study serve as a preliminary proof of concept for utilizing CNT arrays as a transduction mechanism for a proposed artificial hair sensor. Such a low profile and light-weight flow sensor is expected to have application in a number of applications including navigation and state awareness of small air vehicles, similar in function to natural hair cell receptors utilized by insects and bats. (paper)

Force sensitive carbon nanotube arrays for biologically inspired airflow sensing

Science.gov (United States)

Maschmann, Matthew R.; Dickinson, Ben; Ehlert, Gregory J.; Baur, Jeffery W.

2012-09-01

The compressive electromechanical response of aligned carbon nanotube (CNT) arrays is evaluated for use as an artificial hair sensor (AHS) transduction element. CNT arrays with heights of 12, 75, and 225 µm are examined. The quasi-static and dynamic sensitivity to force, response time, and signal drift are examined within the range of applied stresses predicted by a mechanical model applicable to the conceptual CNT array-based AHS (0-1 kPa). Each array is highly sensitive to compressive loading, with a maximum observed gauge factor of 114. The arrays demonstrate a repeatable response to dynamic cycling after a break-in period of approximately 50 cycles. Utilizing a four-wire measurement electrode configuration, the change in contact resistance between the array and the electrodes is observed to dominate the electromechanical response of the arrays. The response time of the CNT arrays is of the order of 10 ms. When the arrays are subjected to constant stress, mechanical creep is observed that results in a signal drift that generally diminishes the responsiveness of the arrays, particularly at stress approaching 1 kPa. The results of this study serve as a preliminary proof of concept for utilizing CNT arrays as a transduction mechanism for a proposed artificial hair sensor. Such a low profile and light-weight flow sensor is expected to have application in a number of applications including navigation and state awareness of small air vehicles, similar in function to natural hair cell receptors utilized by insects and bats.

Highly efficient photoelectrochemical performance of SrTiO{sub 3}/TiO{sub 2} heterojunction nanotube array thin film

Energy Technology Data Exchange (ETDEWEB)

Zhang Yan [Qingdao University, School of Chemistry, Chemical Engineering and Environments (China); Bu Yuyu [Chinese Academy of Sciences, National Engineering Center of Marine Corrosion Protection, Institute of Oceanology (China); Yu Jianqiang, E-mail: yjq@licp.cas.cn; Li Ping [Qingdao University, School of Chemistry, Chemical Engineering and Environments (China)

2013-06-15

SrTiO{sub 3}-TiO{sub 2} heterojunction thin-film nanotube arrays (SNTs, the average inner diameter is about 50 nm) was fabricated via electrochemical anodization followed by a hydrothermal treatment. The photo-to-current conversion properties and the photoelectrochemical performance for cathodic protection of carbon steel in 0.5 M of sodium chloride solution under white light illumination were investigated. The results showed that the highly ordered nanotube arrays could provide very excellent cathodic protection for carbon steel under white light irradiation.

Fabrication of polyaniline/graphene/titania nanotube arrays nanocomposite and their application in supercapacitors

Energy Technology Data Exchange (ETDEWEB)

Huang, Hua; Gan, Mengyu; Ma, Li, E-mail: mlsys607@126.com; Yu, Lei; Hu, Haifeng; Yang, Fangfang; Li, Yanjun; Ge, Chengqiang

2015-05-05

Highlights: • The PANI/graphene/TiO{sub 2} nanotube arrays were fabricated firstly. • The composite shows a high specific capacitance and superior rate capability. • A high capacity retention rate of 91% after 1000 cycles can be achieved. • The composite possesses a novel three-dimensional (3D) highly ordered nanostructure. • TiO{sub 2} NTs enhance the adhesion between PANI and substrate. - Abstract: Polyaniline/graphene/titania nanotube arrays (PGTNs) nanocomposite as a supercapacitor electrode is fabricated by in-situ polymerization for the first time. Herein, the PGTNs possesses a novel three-dimensional (3D) highly ordered hybrid nanostructure consisting of coaxial polyaniline (PANI)/TiO{sub 2} nanotube arrays and graphene coated with PANI on the surface of TiO{sub 2} in some degree. The synthesized three-dimensional PGTNs is characterized by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and Raman spectroscopy, and its electrochemical performance is measured by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and galvanostatic charge/discharge. The maximum specific capacitance of PGTNs is as high as 933 F g{sup −1} at current density of 0.75 A g{sup −1} and the specific capacitance retains 91% of the initial after constant charge–discharge 1000 cycles. The improved electrochemical performance is due to the 3D nanostructure, which effectively prevents the mechanical deformation during the fast charge/discharge process and favors the diffusion of the electrolyte ions into the inner region of active materials. The composite electrode material is very promising for the next generation of high-performance electrochemical supercapacitors.

Electrooxidation of ethanol on novel multi-walled carbon nanotube supported platinum-antimony tin oxide nanoparticle catalysts

Energy Technology Data Exchange (ETDEWEB)

Guo, Dao-Jun [School of Chemistry and Chemical Engineering, The Key Laboratory of Life-Organic Analysis, Qufu Normal University, Qufu, Shandong 273165 (China)

2011-01-15

We synthesize the new Pt based catalyst for direct ethanol fuel cells using novel multi-walled carbon nanotubes supported platinum-antimony tin oxide (Pt-ATO/MWCNT) nanoparticle as new catalyst support for the first time. The structure of Pt-ATO/MWCNT catalyst is characterized by transmission electron micrograph (TEM) and X-ray diffraction (XRD). The electrocatalytic properties of Pt-ATO/MWCNT catalyst for ethanol electrooxidation reactions are investigated by cyclic voltammetry (CV) and chronoamperometric experiments in acidic medium. The electrocatalytic activity for ethanol electrooxidation reaction shows that high carbon monoxide tolerance and good stability of Pt-ATO/MWCNT catalyst compared with Pt-SnO{sub 2}/MWCNT and commercial Pt/C are observed. These results imply that Pt-ATO/MWCNT catalyst has promising potential applications in direct alcohol fuel cells. (author)

Vertically aligned carbon nanotube field emitter arrays with Ohmic base contact to silicon by Fe-catalyzed chemical vapor deposition

NARCIS (Netherlands)

Morassutto, M.; Tiggelaar, Roald M.; Smithers, M.A.; Smithers, M.A.; Gardeniers, Johannes G.E.

2016-01-01

Abstract In this study, dense arrays of aligned carbon nanotubes are obtained by thermal catalytic chemical vapor deposition, using Fe catalyst dispersed on a thin Ta layer. Alignment of the carbon nanotubes depends on the original Fe layer thickness from which the catalyst dispersion is obtained by

Direct electrodeposition of gold nanotube arrays of rough and porous wall by cyclic voltammetry and its applications of simultaneous determination of ascorbic acid and uric acid

International Nuclear Information System (INIS)

Yang Guangming; Li Ling; Jiang Jinhe; Yang Yunhui

2012-01-01

Gold nanotube arrays of rough and porous wall has been synthesized by direct electrodeposition with cyclic voltammetry utilizing anodic aluminum oxide template (AAO) and polycarbonate membrane (PC) during short time (only 3 min and 2 min, respectively). The mechanism of the direct electrodeposition of gold nanotube arrays by cyclic voltammetry (CV) has been discussed. The morphological characterizations of the gold nanotube arrays have been investigated by scanning electron microscopy (SEM). A simultaneous determination of ascorbic acid (AA) and uric acid (UA) by differential pulse voltammetry (DPV) was constructed by attaching gold nanotube arrays (using AAO) onto the surface of a glassy carbon electrode (GCE). The electrochemical behavior of AA and UA at this modified electrode has been studied by CV and differential pulse voltammetry (DPV). The sensor offers an excellent response for AA and UA and the linear response range for AA and UA were 1.02 × 10 −7 –5.23 × 10 −4 mol L −1 and 1.43 × 10 −7 –4.64 × 10 −4 mol L −1 , the detection limits were 1.12 × 10 −8 mol L −1 and 2.24 × 10 −8 mol L −1 , respectively. This sensor shows good regeneration, stability and selectivity and has been used for the determination of AA and UA in real human urine and serum samples with satisfied results. - Graphical abstract: The schematic diagram of formation of Au nanotube arrays (a) and the stepwise procedure of the sensor (b). Highlights: ► Gold nanotubes array has been synthesized by cyclic voltammetry. ► The mechanism of deposition of gold nanotube has been discussed. ► A determination of ascorbic acid and uric acid was constructed by gold array. ► A satisfied determination of samples can be obtained by this sensor.

Synthesis and Investigation of Millimeter-Scale Vertically Aligned Boron Nitride Nanotube Arrays

Science.gov (United States)

Tay, Roland; Li, Hongling; Tsang, Siu Hon; Jing, Lin; Tan, Dunlin; Teo, Edwin Hang Tong

Boron nitride nanotubes (BNNTs) have shown potential in a wide range of applications due to their superior properties such as exceptionally high mechanical strength, excellent chemical and thermal stabilities. However, previously reported methods to date only produced BNNTs with limited length/density and insufficient yield at high temperatures. Here we present a facile and effective two-step synthesis route involving template-assisted chemical vapor deposition at a relatively low temperature of 900 degree C and subsequent annealing process to fabricate vertically aligned (VA) BN coated carbon nanotube (VA-BN/CNT) and VA-BNNT arrays. By using this method, we achieve the longest VA-BN/CNTs and VA-BNNTs to date with lengths of over millimeters (exceeding two orders of magnitude longer than the previously reported length of VA-BNNTs). In addition, the morphology, chemical composition and microstructure of the resulting products, as well as the mechanism of coating process are systematically investigated. This versatile BN coating technique and the synthesis of millimeter-scale BN/CNT and BNNT arrays pave a way for new applications especially where the aligned geometry of the NTs is essential such as for field-emission, interconnects and thermal management.

Glucose biosensor based on glucose oxidase immobilized on unhybridized titanium dioxide nanotube arrays

International Nuclear Information System (INIS)

Wang, Wei; Xie, Yibing; Du, Hongxiu; Xia, Chi; Wang, Yong; Tian, Fang

2014-01-01

A glucose biosensor has been fabricated by immobilizing glucose oxidase (GOx) on unhybridized titanium dioxide nanotube arrays using an optimized cross-linking technique. The TiO 2 nanotube arrays were synthesized directly on a titanium substrate by anodic oxidation. The structure and morphology of electrode material were characterized by X-ray diffraction and scanning electron microscopy. The electrochemical performances of the glucose biosensor were conducted by cyclic voltammetry and chronoamperometry measurements. It gives a linear response to glucose in the 0.05 to 0.65 mM concentration range, with a correlation coefficient of 0.9981, a sensitivity of 199.6 μA mM −1 cm −2 , and a detection limit as low as 3.8 µM. This glucose biosensor exhibited high selectivity for glucose determination in the presence of ascorbic acid, sucrose and other common interfering substances. This glucose biosensor also performed good reproducibility and long-time storage stability. This optimized cross-linking technique could open a new avenue for other enzyme biosensors fabrication. (author)

Tin-oxide-coated single-walled carbon nanotube bundles supporting platinum electrocatalysts for direct ethanol fuel cells

International Nuclear Information System (INIS)

Hsu, Ryan S; Higgins, Drew; Chen Zhongwei

2010-01-01

Novel tin-oxide (SnO 2 )-coated single-walled carbon nanotube (SWNT) bundles supporting platinum (Pt) electrocatalysts for ethanol oxidation were developed for direct ethanol fuel cells. SnO 2 -coated SWNT (SnO 2 -SWNT) bundles were synthesized by a simple chemical-solution route. SnO 2 -SWNT bundles supporting Pt (Pt/SnO 2 -SWNTs) electrocatalysts and SWNT-supported Pt (Pt/SWNT) electrocatalysts were prepared by an ethylene glycol reduction method. The catalysts were physically characterized using TGA, XRD and TEM and electrochemically evaluated through cyclic voltammetry experiments. The Pt/SnO 2 -SWNTs showed greatly enhanced electrocatalytic activity for ethanol oxidation in acid medium, compared to the Pt/SWNT. The optimal SnO 2 loading of Pt/SnO 2 -SWNT catalysts with respect to specific catalytic activity for ethanol oxidation was also investigated.

Tin-oxide-coated single-walled carbon nanotube bundles supporting platinum electrocatalysts for direct ethanol fuel cells.

Science.gov (United States)

Hsu, Ryan S; Higgins, Drew; Chen, Zhongwei

2010-04-23

Novel tin-oxide (SnO(2))-coated single-walled carbon nanotube (SWNT) bundles supporting platinum (Pt) electrocatalysts for ethanol oxidation were developed for direct ethanol fuel cells. SnO(2)-coated SWNT (SnO(2)-SWNT) bundles were synthesized by a simple chemical-solution route. SnO(2)-SWNT bundles supporting Pt (Pt/SnO(2)-SWNTs) electrocatalysts and SWNT-supported Pt (Pt/SWNT) electrocatalysts were prepared by an ethylene glycol reduction method. The catalysts were physically characterized using TGA, XRD and TEM and electrochemically evaluated through cyclic voltammetry experiments. The Pt/SnO(2)-SWNTs showed greatly enhanced electrocatalytic activity for ethanol oxidation in acid medium, compared to the Pt/SWNT. The optimal SnO(2) loading of Pt/SnO(2)-SWNT catalysts with respect to specific catalytic activity for ethanol oxidation was also investigated.

Direct electrodeposition of gold nanotube arrays of rough and porous wall by cyclic voltammetry and its applications of simultaneous determination of ascorbic acid and uric acid

Energy Technology Data Exchange (ETDEWEB)

Yang Guangming, E-mail: yangguangmingbs@126.com [Department of Resources and Environment, Baoshan University, Baoshan 678000 (China); Ling, Li [Department of Resources and Environment, Baoshan University, Baoshan 678000 (China); Jinhe, Jiang; Yunhui, Yang [College of Chemistry and Chemical Engineering, Yunnan Normal University, Kunming 650092 (China)

2012-08-01

Gold nanotube arrays of rough and porous wall has been synthesized by direct electrodeposition with cyclic voltammetry utilizing anodic aluminum oxide template (AAO) and polycarbonate membrane (PC) during short time (only 3 min and 2 min, respectively). The mechanism of the direct electrodeposition of gold nanotube arrays by cyclic voltammetry (CV) has been discussed. The morphological characterizations of the gold nanotube arrays have been investigated by scanning electron microscopy (SEM). A simultaneous determination of ascorbic acid (AA) and uric acid (UA) by differential pulse voltammetry (DPV) was constructed by attaching gold nanotube arrays (using AAO) onto the surface of a glassy carbon electrode (GCE). The electrochemical behavior of AA and UA at this modified electrode has been studied by CV and differential pulse voltammetry (DPV). The sensor offers an excellent response for AA and UA and the linear response range for AA and UA were 1.02 Multiplication-Sign 10{sup -7}-5.23 Multiplication-Sign 10{sup -4} mol L{sup -1} and 1.43 Multiplication-Sign 10{sup -7}-4.64 Multiplication-Sign 10{sup -4} mol L{sup -1}, the detection limits were 1.12 Multiplication-Sign 10{sup -8} mol L{sup -1} and 2.24 Multiplication-Sign 10{sup -8} mol L{sup -1}, respectively. This sensor shows good regeneration, stability and selectivity and has been used for the determination of AA and UA in real human urine and serum samples with satisfied results. - Graphical abstract: The schematic diagram of formation of Au nanotube arrays (a) and the stepwise procedure of the sensor (b). Highlights: Black-Right-Pointing-Pointer Gold nanotubes array has been synthesized by cyclic voltammetry. Black-Right-Pointing-Pointer The mechanism of deposition of gold nanotube has been discussed. Black-Right-Pointing-Pointer A determination of ascorbic acid and uric acid was constructed by gold array. Black-Right-Pointing-Pointer A satisfied determination of samples can be obtained by this sensor.

Dysprosium-Catalyzed Growth of Single-Walled Carbon Nanotube Arrays on Substrates

Directory of Open Access Journals (Sweden)

Qian Yong

2009-01-01

Full Text Available Abstract In this letter, we report that dysprosium is an effective catalyst for single-walled carbon nanotubes (SWNTs growth via a chemical vapor deposition (CVD process for the first time. Horizontally superlong well-oriented SWNT arrays on SiO2/Si wafer can be fabricated by EtOH-CVD under suitable conditions. The structure and properties are characterized by scanning electron microscopy, transition electron microscopy, Raman spectroscopy and atomic force microscopy. The results show that the SWNTs from dysprosium have better structural uniformity and better conductivity with fewer defects. This rare earth metal provides not only an alternative catalyst for SWNTs growth, but also a possible method to generate high percentage of superlong semiconducting SWNT arrays for various applications of nanoelectronic device.

Room temperature alcohol sensing by oxygen vacancy controlled TiO2 nanotube array

International Nuclear Information System (INIS)

Hazra, A.; Dutta, K.; Bhowmik, B.; Bhattacharyya, P.; Chattopadhyay, P. P.

2014-01-01

Oxygen vacancy (OV) controlled TiO 2 nanotubes, having diameters of 50–70 nm and lengths of 200–250 nm, were synthesized by electrochemical anodization in the mixed electrolyte comprising NH 4 F and ethylene glycol with selective H 2 O content. The structural evolution of TiO 2 nanoforms has been studied by field emission scanning electron microscopy. Variation in the formation of OVs with the variation of the structure of TiO 2 nanoforms has been evaluated by photoluminescence and X-ray photoelectron spectroscopy. The sensor characteristics were correlated to the variation of the amount of induced OVs in the nanotubes. The efficient room temperature sensing achieved by the control of OVs of TiO 2 nanotube array has paved the way for developing fast responding alcohol sensor with corresponding response magnitude of 60.2%, 45.3%, and 36.5% towards methanol, ethanol, and 2-propanol, respectively.

Spectroscopic and nonlinear photophysical characterization of organic octupolar-compounds supported by anodic-alumina nanotube-arrays

International Nuclear Information System (INIS)

Morales-Saavedra, O.G.; Ontiveros-Barrera, F.G.; Hennrich, G.; Mata-Zamora, M.E.; Rodriguez-Rosales, A.A.; Banuelos, J.G.

2011-01-01

Highlights: → Preparation of organic-inorganic nanostructured hybrid materials. → Insertion of octupolar compounds in alumina nanotube arrays. → Linear and nonlinear photophysical characterization of solid-state hybrid structures. → Fabrication of photonic materials. - Abstract: Amorphous anodic alumina membranes (AAM) comprising highly ordered nanometric porous arrays (porous anodic aluminas: PAA) with 1D-nanotube dimensions of ∼75 nm in diameter and 45 microns in depth were successfully prepared and used as nanostructured host networks for different functionalized octupolar chromophores (named here Oct-(n)). Atomic force microscopy (AFM) studies performed on the developed hybrid systems confirmed a homogeneous insertion of these organic molecules into the PAA nanotube-arrays. Samples with high structural quality were selected for several photophysical characterizations: Comprehensive X-ray diffraction (XRD) and optical spectroscopic characterizations performed according to UV-vis absorption, photoluminescent (PL) and Raman measurements revealed the structural and optical performance of these molecules within the PAA-confinement. Since the implemented optical chromophores were specifically functionalized for nonlinear optical (NLO) applications, the obtained Oct-(n)/PAA-based amorphous hybrids were also characterized according to cubic NLO-techniques such as third harmonic generation (THG) and the Z-Scan method. PAA-confined octupolar chromophores have shown interesting linear and NLO optical properties which have not yet been intensively investigated in bulk hybrid systems; hence, the obtained hybrid nanostructures represent a promising field of investigation in the route to functional octupolar-based materials, where different self-assembled molecular structures may be formed, giving rise to enhanced linear and NLO-properties.

Photoelectrochemical oxidation of ibuprofen via Cu_2O-doped TiO_2 nanotube arrays

International Nuclear Information System (INIS)

Sun, Qiannan; Peng, Yen-Ping; Chen, Hanlin; Chang, Ken-Lin; Qiu, Yang-Neng; Lai, Shiau-Wu

2016-01-01

Highlights: • A p–n junction material was synthesized to enhance photocatalytic ability. • Cu_2O-doped TiO_2 nanotube arrays works as a photoanode in a PEC system. • Recombination of photo-generated holes and electrons were greatly reduced. • Synergetic effect was quantified in PEC degradation. • Recombination of photogenerated holes and electrons was greatly enhanced. - Abstract: A p–n junction based Cu_2O-doped TiO_2 nanotube arrays (Cu_2O-TNAs) were synthesized and used as a working anode in a photoelectrochemical (PEC) system. The results revealed that the Cu_2O-TNAs were dominated by the anatase phase and responded significantly to visible light. XPS analyses indicated that with an amount of 24.79% Cu doping into the structure, the band gap of Cu_2O-TNAs was greatly reduced. SEM images revealed that the supported TiO_2 nanotubes had diameters of approximately 80 nm and lengths of about 2.63 μm. Upon doping with Cu_2O, the TiO_2 nanotubes maintained their structural integrity, exhibiting no significant morphological change, favoring PEC applications. Under illumination, the photocurrent from Cu_2O/TNAs was 2.4 times larger than that from TNAs, implying that doping with Cu_2O significantly improved electron mobility by reducing the rate of recombination of electron-hole pairs. The EIS and Bode plot revealed that the estimated electron lifetimes, τ_e_l, of TNAs and Cu_2O/TNAs were 6.91 and 26.26 ms, respectively. The efficiencies of degradation of Ibuprofen by photoelectrochemical, photocatalytic (PC), electrochemical (EC) and photolytic (P) methods were measured.

Enhancement of hole injection and electroluminescence by ordered Ag nanodot array on indium tin oxide anode in organic light emitting diode

Energy Technology Data Exchange (ETDEWEB)

Jung, Mi, E-mail: jmnano00@gmail.com, E-mail: Dockha@kist.re.kr [Sensor System Research Center, Korea Institute of Science and Technology, Seoul 136-791 (Korea, Republic of); School of Mechanical Systems Engineering, Kookmin University, Seoul 136-702 (Korea, Republic of); Mo Yoon, Dang; Kim, Miyoung [Korea Printed Electronics Center, Korea Electronics Technology Institute, Jeollabuk-do, 561-844 (Korea, Republic of); Kim, Chulki; Lee, Taikjin; Hun Kim, Jae; Lee, Seok; Woo, Deokha, E-mail: jmnano00@gmail.com, E-mail: Dockha@kist.re.kr [Sensor System Research Center, Korea Institute of Science and Technology, Seoul 136-791 (Korea, Republic of); Lim, Si-Hyung [School of Mechanical Systems Engineering, Kookmin University, Seoul 136-702 (Korea, Republic of)

2014-07-07

We report the enhancement of hole injection and electroluminescence (EL) in an organic light emitting diode (OLED) with an ordered Ag nanodot array on indium-tin-oxide (ITO) anode. Until now, most researches have focused on the improved performance of OLEDs by plasmonic effects of metal nanoparticles due to the difficulty in fabricating metal nanodot arrays. A well-ordered Ag nanodot array is fabricated on the ITO anode of OLED using the nanoporous alumina as an evaporation mask. The OLED device with Ag nanodot arrays on the ITO anode shows higher current density and EL enhancement than the one without any nano-structure. These results suggest that the Ag nanodot array with the plasmonic effect has potential as one of attractive approaches to enhance the hole injection and EL in the application of the OLEDs.

Surface-conduction electron-emitter characteristics and fabrication based on vertically aligned carbon nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Shih, Yi-Ting [Graduate Institute of Electro-Optical Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan (China); Li, Kuan-Wei [Department of Electronic and Computer Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan (China); Honda, Shin-ichi [Graduate School of Engineering, University of Hyogo, 2167 Shosha, Himeji, Hyogo 671-2280 (Japan); Lin, Pao-Hung; Huang, Ying-Sheng [Graduate Institute of Electro-Optical Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan (China); Department of Electronic and Computer Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan (China); Lee, Kuei-Yi, E-mail: kylee@mail.ntust.edu.tw [Graduate Institute of Electro-Optical Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan (China); Department of Electronic and Computer Engineering, National Taiwan University of Science and Technology, No. 43, Section 4, Keelung Road, Taipei 10607, Taiwan (China)

2017-06-01

Graphical abstract: The pattern design provides a new structure of surface-conduction electron-emitter display (SED). Delta-star shaped vertically aligned CNT (VACNT) arrays with 20o tips can simultaneously provide three emitters to bombard the sides of equilateral triangles pattern of VACNT, which produces numerous secondary electrons and enhance the SED efficiency. - Highlights: • The carbon nanotube (CNT) has replaced palladium oxide (PdO) as the electrode material for surface-conduction electron-emitter (SCE) applications. • The vertically aligned CNT (VACNT) arrays with 20° tips of the delta-star arrangement are used as cathodes that easily emit electrons. The cathode pattern simultaneously provides three emitters to bombard the sides of equilateral triangles pattern of VACNT. • The VACNT arrays were covered with magnesium oxide (MgO) nanostructures to promote the surface-conduction electron-emitter display (SED) efficiency (η). • The η was stably maintained in the 75–85% range. The proposed design provides a facile new method for developing SED applications. - Abstract: The carbon nanotube (CNT) has replaced palladium oxide (PdO) as the electrode material for surface-conduction electron-emitter (SCE) applications. Vertically aligned CNT arrays with a delta-star arrangement were patterned and synthesized onto a quartz substrate using photolithography and thermal chemical vapor deposition. Delta-star shaped VACNT arrays with 20° tips are used as cathodes that easily emit electrons because of their high electrical field gradient. In order to improve the field emission and secondary electrons (SEs) in SCE applications, magnesium oxide (MgO) nanostructures were coated onto the VACNT arrays to promote the surface-conduction electron-emitter display (SED) efficiency (η). According to the definition of η in SCE applications, in this study, the η was stably maintained in the 75–85% range. The proposed design provides a facile new method for

Extremely Black Vertically Aligned Carbon Nanotube Arrays for Solar Steam Generation.

Science.gov (United States)

Yin, Zhe; Wang, Huimin; Jian, Muqiang; Li, Yanshen; Xia, Kailun; Zhang, Mingchao; Wang, Chunya; Wang, Qi; Ma, Ming; Zheng, Quan-Shui; Zhang, Yingying

2017-08-30

The unique structure of a vertically aligned carbon nanotube (VACNT) array makes it behave most similarly to a blackbody. It is reported that the optical absorptivity of an extremely black VACNT array is about 0.98-0.99 over a large spectral range of 200 nm-200 μm, inspiring us to explore the performance of VACNT arrays in solar energy harvesting. In this work, we report the highly efficient steam generation simply by laminating a layer of VACNT array on the surface of water to harvest solar energy. It is found that under solar illumination the temperature of upper water can significantly increase with obvious water steam generated, indicating the efficient solar energy harvesting and local temperature rise by the thin layer of VACNTs. We found that the evaporation rate of water assisted by VACNT arrays is 10 times that of bare water, which is the highest ratio for solar-thermal-steam generation ever reported. Remarkably, the solar thermal conversion efficiency reached 90%. The excellent performance could be ascribed to the strong optical absorption and local temperature rise induced by the VACNT layer, as well as the ultrafast water transport through the VACNT layer due to the frictionless wall of CNTs. Based on the above, we further demonstrated the application of VACNT arrays in solar-driven desalination.

Low-cost silver capped polystyrene nanotube arrays as super-hydrophobic substrates for SERS applications.

Science.gov (United States)

Lovera, Pierre; Creedon, Niamh; Alatawi, Hanan; Mitchell, Micki; Burke, Micheal; Quinn, Aidan J; O'Riordan, Alan

2014-05-02

In this paper, we describe the fabrication, simulation and characterization of dense arrays of freestanding silver capped polystyrene nanotubes, and demonstrate their suitability for surface enhanced Raman scattering (SERS) applications. Substrates are fabricated in a rapid, low-cost and scalable way by melt wetting of polystyrene (PS) in an anodized alumina (AAO) template, followed by silver evaporation. Scanning electron microscopy reveals that substrates are composed of a dense array of freestanding polystyrene nanotubes topped by silver nanocaps. SERS characterization of the substrates, employing a monolayer of 4-aminothiophenol (4-ABT) as a model molecule, exhibits an enhancement factor of ∼1.6 × 10(6), in agreement with 3D finite difference time domain simulations. Contact angle measurements of the substrates revealed super-hydrophobic properties, allowing pre-concentration of target analyte into a small volume. These super-hydrophobic properties of the samples are taken advantage of for sensitive detection of the organic pollutant crystal violet, with detection down to ∼400 ppt in a 2 μl aliquot demonstrated.

Low-cost silver capped polystyrene nanotube arrays as super-hydrophobic substrates for SERS applications

International Nuclear Information System (INIS)

Lovera, Pierre; Creedon, Niamh; Alatawi, Hanan; Mitchell, Micki; Burke, Micheal; Quinn, Aidan J; O’Riordan, Alan

2014-01-01

In this paper, we describe the fabrication, simulation and characterization of dense arrays of freestanding silver capped polystyrene nanotubes, and demonstrate their suitability for surface enhanced Raman scattering (SERS) applications. Substrates are fabricated in a rapid, low-cost and scalable way by melt wetting of polystyrene (PS) in an anodized alumina (AAO) template, followed by silver evaporation. Scanning electron microscopy reveals that substrates are composed of a dense array of freestanding polystyrene nanotubes topped by silver nanocaps. SERS characterization of the substrates, employing a monolayer of 4-aminothiophenol (4-ABT) as a model molecule, exhibits an enhancement factor of ∼1.6 × 10 6 , in agreement with 3D finite difference time domain simulations. Contact angle measurements of the substrates revealed super-hydrophobic properties, allowing pre-concentration of target analyte into a small volume. These super-hydrophobic properties of the samples are taken advantage of for sensitive detection of the organic pollutant crystal violet, with detection down to ∼400 ppt in a 2 μl aliquot demonstrated. (paper)

Dye-Sensitized Solar Cells Based on TiO_2 Nanotube and Shelled Arrayed Structures

International Nuclear Information System (INIS)

Zhang, Jie; Kusumawati, Yuly; Pauporté, Thierry

2016-01-01

Anatase TiO_2 nanostructure arrays were synthetized starting from a template made of self-standing ZnO NWs prepared by an electrodeposition technique. By controlling the liquid phase deposition step, the obtained structures could be varied from free-standing nanotube (NT) arrays with controlled morphology to hierarchical spiky radiating core-shell rods. The nanotubes were made of assembled nanocrystals with an average size of 7–8 nm. The structures were investigated as n-type layers in DSSCs. The efficiency was enhanced for the core-shell layer and by starting with longer initial ZnO NW templates. The limitation of the cell efficiency was shown related to the specific surface area and dye loading. The cell functioning was in-depth investigated by electrochemical impedance spectroscopy over a large applied voltage range and compared to a cell based on a nanoparticle TO_2 mesoporous layer. A slow recombination rate was found. The enhancement of electron transport with nanocrystallite size explained the conductivity results. We also found that the prepared structures presented a high charge collection efficiency.

Multidirectional flexible force sensors based on confined, self-adjusting carbon nanotube arrays

Science.gov (United States)

Lee, J.-I.; Pyo, Soonjae; Kim, Min-Ook; Kim, Jongbaeg

2018-02-01

We demonstrate a highly sensitive force sensor based on self-adjusting carbon nanotube (CNT) arrays. Aligned CNT arrays are directly synthesized on silicon microstructures by a space-confined growth technique which enables a facile self-adjusting contact. To afford flexibility and softness, the patterned microstructures with the integrated CNTs are embedded in polydimethylsiloxane structures. The sensing mechanism is based on variations in the contact resistance between the facing CNT arrays under the applied force. By finite element analysis, proper dimensions and positions for each component are determined. Further, high sensitivities up to 15.05%/mN of the proposed sensors were confirmed experimentally. Multidirectional sensing capability could also be achieved by designing multiple sets of sensing elements in a single sensor. The sensors show long-term operational stability, owing to the unique properties of the constituent CNTs, such as outstanding mechanical durability and elasticity.

Multifunctional Material Structures Based on Laser-Etched Carbon Nanotube Arrays

Directory of Open Access Journals (Sweden)

Aline Emplit

2014-09-01

Full Text Available High-power electronics in the transportation and aerospace sectors need size and weight reduction. Multifunctional and multistructured materials are currently being developed to couple electromagnetic (EM and thermal properties, i.e., shielding against electromagnetic impulsions, and thermal management across the thermal interface material (TIM. In this work, we investigate laser-machined patterned carbon nanotube (CNT micro-brushes as an alternative to metallic structures for driving simultaneously EM and heat propagation. The thermal and electromagnetic response of the CNT array is expected to be sensitive to the micro-structured pattern etched in the CNT brush.

Morphological evolution of TiO2 nanotube arrays with lotus-root-shaped nanostructure

Science.gov (United States)

Yu, Dongliang; Song, Ye; Zhu, Xufei; Yang, Ruiquan; Han, Aijun

2013-07-01

TiO2 nanotube arrays (TNAs) with lotus-root-shaped nanostructure have been fabricated by a modified two-step electrochemical anodization method. In the present work, different morphologies formed under different anodizing voltages are investigated in detail by field-emission scanning electron microscope. The results show that the concaves left by the first-step anodization can guide the uniform growth of TNAs in some degree as the second-step anodizing voltage is the same with that in the first step, however, when lower voltages are adopted in the second-step anodization, no guidance can be achieved, and different morphological TNAs with lotus-root-shaped nanostructure are fabricated. And we find that the nanotube diameters are directly proportional to the applied voltage in the second-step anodization. Furthermore, a possible mechanism for the growth of the TiO2 nanotubes with the special morphology is proposed for the first time, which depends on both the oxygen bubble mold and the viscous flow of the barrier oxide from the pore base to the pore wall.

Room temperature alcohol sensing by oxygen vacancy controlled TiO{sub 2} nanotube array

Energy Technology Data Exchange (ETDEWEB)

Hazra, A.; Dutta, K.; Bhowmik, B.; Bhattacharyya, P., E-mail: pb-etc-besu@yahoo.com [Nano-Thin Films and Solid State Gas Sensor Devices Laboratory, Department of Electronics and Telecommunication Engineering, Indian Institute of Engineering Science and Technology (IIEST), Shibpur, Howrah (India); Chattopadhyay, P. P. [Department of Metallurgy and Materials Engineering, Indian Institute of Engineering Science and Technology (IIEST), Shibpur, Howrah (India)

2014-08-25

Oxygen vacancy (OV) controlled TiO{sub 2} nanotubes, having diameters of 50–70 nm and lengths of 200–250 nm, were synthesized by electrochemical anodization in the mixed electrolyte comprising NH{sub 4}F and ethylene glycol with selective H{sub 2}O content. The structural evolution of TiO{sub 2} nanoforms has been studied by field emission scanning electron microscopy. Variation in the formation of OVs with the variation of the structure of TiO{sub 2} nanoforms has been evaluated by photoluminescence and X-ray photoelectron spectroscopy. The sensor characteristics were correlated to the variation of the amount of induced OVs in the nanotubes. The efficient room temperature sensing achieved by the control of OVs of TiO{sub 2} nanotube array has paved the way for developing fast responding alcohol sensor with corresponding response magnitude of 60.2%, 45.3%, and 36.5% towards methanol, ethanol, and 2-propanol, respectively.

Fabrication of nickel hydroxide electrodes with open-ended hexagonal nanotube arrays for high capacitance supercapacitors.

Science.gov (United States)

Wu, Mao-Sung; Huang, Kuo-Chih

2011-11-28

A nickel hydroxide electrode with open-ended hexagonal nanotube arrays, prepared by hydrolysis of nickel chloride in the presence of hexagonal ZnO nanorods, shows a very high capacitance of 1328 F g(-1) at a discharge current density of 1 A g(-1) due to the significantly improved ion transport.

Gold nanoparticle arrays directly grown on nanostructured indium tin oxide electrodes: Characterization and electroanalytical application

International Nuclear Information System (INIS)

Zhang Jingdong; Oyama, Munetaka

2005-01-01

This work describes an improved seed-mediated growth approach for the direct attachment and growth of mono-dispersed gold nanoparticles on nanostructured indium tin oxide (ITO) surfaces. It was demonstrated that, when the seeding procedure of our previously reported seed-mediated growth process on an ITO surface was modified, the density of gold nanospheres directly grown on the surface could be highly improved, while the emergence of nanorods was restrained. By field emission scanning electron microscopy (FE-SEM) and cyclic voltammetry, the growth of gold nanoparticles with increasing growth time on the defect sites of nanostructured ITO surface was monitored. Using a [Fe(China) 6 ] 3- /[Fe(China) 6 ] 4- redox probe, the increasingly facile heterogeneous electron transfer kinetics resulting from the deposition and growth of gold nanoparticle arrays was observed. The as-prepared gold nanoparticle arrays exhibited high catalytic activity toward the electrooxidation of nitric oxide, which could provide electroanalytical application for nitric oxide sensing

Decorating Mg/Fe oxide nanotubes with nitrogen-doped carbon nanotubes

Energy Technology Data Exchange (ETDEWEB)

Cao Yong, E-mail: caoyangel@126.com [Institute of Environment and Municipal Engineering, North China Institute of Water Conservancy and Hydroelectric Power, Zhengzhou 450011 (China); Jiao Qingze, E-mail: jiaoqz@bit.edu.cn [School of Chemical Engineering and the Environment, Beijing Institute of Technology, Beijing 100081 (China); Zhao Yun [School of Chemical Engineering and the Environment, Beijing Institute of Technology, Beijing 100081 (China); Dong Yingchao [Materials and Surface Science Institute (MSSI), University of Limerick, Limerick (Ireland)

2011-09-22

Graphical abstract: Highlights: > Mg/Fe oxide nanotubes arrayed parallel to each other were prepared by an AAO template method. > The Mg/Fe oxide nanotubes decorated with CN{sub x} were realized by CVD of ethylenediamine on the outer surface of oxide nanotubes. > The magnetic properties of Mg/Fe oxide nanotubes were highly improved after being decorated. - Abstract: Mg/Fe oxide nanotubes decorated with nitrogen-doped carbon nanotubes (CN{sub x}) were fabricated by catalytic chemical vapor deposition of ethylenediamine on the outer surface of oxide nanotubes. Mg/Fe oxide nanotubes were prepared using a 3:1 molar precursor solution of Mg(NO{sub 3}){sub 2} and Fe(NO{sub 3}){sub 3} and anodic aluminum oxide as the substrate. The obtained samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and vibrating sample magnetometer (VSM). The XRD pattern shows that the oxide nanotubes are made up of MgO and Fe{sub 2}O{sub 3}. TEM and SEM observations indicate the oxide nanotubes are arrayed roughly parallel to each other, and the outer surface of oxide nanotubes are decorated with CN{sub x}. XPS results show the nitrogen-doped level in CN{sub x} is about 7.3 at.%. Magnetic measurements with VSM demonstrate the saturated magnetization, remanence and coercivity of oxide nanotubes are obvious improved after being decorated with CN{sub x}.

Rational control on floating catalysts for the growth of carbon nanotube assemblies: From vertically aligned carbon nanotube arrays to carbon nanotube films

International Nuclear Information System (INIS)

Chen, Hongyuan; Chen, Minghai; Zhang, Yongyi; Li, Qingwen

2015-01-01

Graphical abstract: - Highlights: • Floating catalyst CVD for the growth of CNT films and arrays was investigated. • The structure of CNT array grown in floating catalyst CVD was revealed. • Temperature was proved as a key for the growth of different CNT assemblies. • The increase of growth temperature induced the growth of single-walled CNT film. - Abstract: Floating catalyst chemical vapor deposition (FCCVD) has been widely used for the growth of various carbon nanotube (CNT) macrostructures, mainly including vertically aligned CNT (VACNT) arrays and none-woven CNT films. However, it is still unclear for the reason why these CNT macrostructures with largely different morphologies were received via the similar method. In this research, it revealed that the growth temperature largely affected the nucleation status of floating catalysts and thus controlled the morphologies of CNT macrostructures from VACNT arrays to none-woven CNT films. In low temperatures (below 800 °C), VACNTs were grown by bottom-up mechanism with several CNTs, but not one individual from bottom to up along the array height direction. Furthermore, VACNT arrays were only grown on some substrates that can induce iron atoms aggregating to catalyst particles with a suitable size. When increasing the growth temperature higher than 800 °C, more catalyst particles were nucleated in the gas flow, which induced the formation of none-woven CNT films composed of thin CNTs (single-walled CNTs and double-walled CNTs). This research was significative for understanding CNT growth mechanism via FCCVD process and the synthesis of different CNT macrostructures by this strategy.

Rational control on floating catalysts for the growth of carbon nanotube assemblies: From vertically aligned carbon nanotube arrays to carbon nanotube films

Energy Technology Data Exchange (ETDEWEB)

Chen, Hongyuan; Chen, Minghai, E-mail: mhchen2008@sinano.ac.cn; Zhang, Yongyi; Li, Qingwen

2015-10-30

Graphical abstract: - Highlights: • Floating catalyst CVD for the growth of CNT films and arrays was investigated. • The structure of CNT array grown in floating catalyst CVD was revealed. • Temperature was proved as a key for the growth of different CNT assemblies. • The increase of growth temperature induced the growth of single-walled CNT film. - Abstract: Floating catalyst chemical vapor deposition (FCCVD) has been widely used for the growth of various carbon nanotube (CNT) macrostructures, mainly including vertically aligned CNT (VACNT) arrays and none-woven CNT films. However, it is still unclear for the reason why these CNT macrostructures with largely different morphologies were received via the similar method. In this research, it revealed that the growth temperature largely affected the nucleation status of floating catalysts and thus controlled the morphologies of CNT macrostructures from VACNT arrays to none-woven CNT films. In low temperatures (below 800 °C), VACNTs were grown by bottom-up mechanism with several CNTs, but not one individual from bottom to up along the array height direction. Furthermore, VACNT arrays were only grown on some substrates that can induce iron atoms aggregating to catalyst particles with a suitable size. When increasing the growth temperature higher than 800 °C, more catalyst particles were nucleated in the gas flow, which induced the formation of none-woven CNT films composed of thin CNTs (single-walled CNTs and double-walled CNTs). This research was significative for understanding CNT growth mechanism via FCCVD process and the synthesis of different CNT macrostructures by this strategy.

Direct electrodeposition of highly ordered gold nanotube arrays for use in non-enzymatic amperometric sensing of glucose

International Nuclear Information System (INIS)

Tian, Taolei; Dong, Junping; Xu, Jiaqiang

2016-01-01

The authors describe vertically aligned gold nanotube arrays (Au-NTAs) and gold nanowire arrays (Au-NWAs) that were directly grown in alumina oxide templates by galvanostatic deposition. The morphology of the gold arrays can be controlled by adjusting the pH value of the plating bath. Scanning electron microscopy shows the nanoarrays to be highly ordered (with an average length of around 2 μm), and the opening width of the gold nanotube arrays to be uniform (with diameters of around 50 nm). The electrocatalytic activities of the Au-NTAs and Au-NWAs deposited on a glassy carbon electrode toward glucose oxidation were compared by cyclic voltammetry and amperometry at pH 7.2. The Au-NTAs yield higher amperometric currents. The respective glucose sensor, when operated at a working potential of 0.25 V (vs. SCE), exhibits a linear range that extends from 5 μM to 16.4 mM concentrations of glucose, a sensitivity of 44.2 μA mM"−"1 cm"−"2, and a detection limit of 2.1 μM (at an S/N ratio of 3). The excellent sensing performance is attributed to the large surface area and the fast electron transfer rate for the one-dimensional gold nanoarrays (author)

En route to controlled catalytic CVD synthesis of densely packed and vertically aligned nitrogen-doped carbon nanotube arrays

Directory of Open Access Journals (Sweden)

Slawomir Boncel

2014-03-01

Full Text Available The catalytic chemical vapour deposition (c-CVD technique was applied in the synthesis of vertically aligned arrays of nitrogen-doped carbon nanotubes (N-CNTs. A mixture of toluene (main carbon source, pyrazine (1,4-diazine, nitrogen source and ferrocene (catalyst precursor was used as the injection feedstock. To optimize conditions for growing the most dense and aligned N-CNT arrays, we investigated the influence of key parameters, i.e., growth temperature (660, 760 and 860 °C, composition of the feedstock and time of growth, on morphology and properties of N-CNTs. The presence of nitrogen species in the hot zone of the quartz reactor decreased the growth rate of N-CNTs down to about one twentieth compared to the growth rate of multi-wall CNTs (MWCNTs. As revealed by electron microscopy studies (SEM, TEM, the individual N-CNTs (half as thick as MWCNTs grown under the optimal conditions were characterized by a superior straightness of the outer walls, which translated into a high alignment of dense nanotube arrays, i.e., 5 × 108 nanotubes per mm2 (100 times more than for MWCNTs grown in the absence of nitrogen precursor. In turn, the internal crystallographic order of the N-CNTs was found to be of a ‘bamboo’-like or ‘membrane’-like (multi-compartmental structure morphology. The nitrogen content in the nanotube products, which ranged from 0.0 to 3.0 wt %, was controlled through the concentration of pyrazine in the feedstock. Moreover, as revealed by Raman/FT-IR spectroscopy, the incorporation of nitrogen atoms into the nanotube walls was found to be proportional to the number of deviations from the sp2-hybridisation of graphene C-atoms. As studied by XRD, the temperature and the [pyrazine]/[ferrocene] ratio in the feedstock affected the composition of the catalyst particles, and hence changed the growth mechanism of individual N-CNTs into a ‘mixed base-and-tip’ (primarily of the base-type type as compared to the purely �

En route to controlled catalytic CVD synthesis of densely packed and vertically aligned nitrogen-doped carbon nanotube arrays.

Science.gov (United States)

Boncel, Slawomir; Pattinson, Sebastian W; Geiser, Valérie; Shaffer, Milo S P; Koziol, Krzysztof K K

2014-01-01

The catalytic chemical vapour deposition (c-CVD) technique was applied in the synthesis of vertically aligned arrays of nitrogen-doped carbon nanotubes (N-CNTs). A mixture of toluene (main carbon source), pyrazine (1,4-diazine, nitrogen source) and ferrocene (catalyst precursor) was used as the injection feedstock. To optimize conditions for growing the most dense and aligned N-CNT arrays, we investigated the influence of key parameters, i.e., growth temperature (660, 760 and 860 °C), composition of the feedstock and time of growth, on morphology and properties of N-CNTs. The presence of nitrogen species in the hot zone of the quartz reactor decreased the growth rate of N-CNTs down to about one twentieth compared to the growth rate of multi-wall CNTs (MWCNTs). As revealed by electron microscopy studies (SEM, TEM), the individual N-CNTs (half as thick as MWCNTs) grown under the optimal conditions were characterized by a superior straightness of the outer walls, which translated into a high alignment of dense nanotube arrays, i.e., 5 × 10(8) nanotubes per mm(2) (100 times more than for MWCNTs grown in the absence of nitrogen precursor). In turn, the internal crystallographic order of the N-CNTs was found to be of a 'bamboo'-like or 'membrane'-like (multi-compartmental structure) morphology. The nitrogen content in the nanotube products, which ranged from 0.0 to 3.0 wt %, was controlled through the concentration of pyrazine in the feedstock. Moreover, as revealed by Raman/FT-IR spectroscopy, the incorporation of nitrogen atoms into the nanotube walls was found to be proportional to the number of deviations from the sp(2)-hybridisation of graphene C-atoms. As studied by XRD, the temperature and the [pyrazine]/[ferrocene] ratio in the feedstock affected the composition of the catalyst particles, and hence changed the growth mechanism of individual N-CNTs into a 'mixed base-and-tip' (primarily of the base-type) type as compared to the purely 'base'-type for undoped

Controllable 3D architectures of aligned carbon nanotube arrays by multi-step processes

Science.gov (United States)

Huang, Shaoming

2003-06-01

An effective way to fabricate large area three-dimensional (3D) aligned CNTs pattern based on pyrolysis of iron(II) phthalocyanine (FePc) by two-step processes is reported. The controllable generation of different lengths and selective growth of the aligned CNT arrays on metal-patterned (e.g., Ag and Au) substrate are the bases for generating such 3D aligned CNTs architectures. By controlling experimental conditions 3D aligned CNT arrays with different lengths/densities and morphologies/structures as well as multi-layered architectures can be fabricated in large scale by multi-step pyrolysis of FePc. These 3D architectures could have interesting properties and be applied for developing novel nanotube-based devices.

Highly efficient biosensors by using well-ordered ZnO/ZnS core/shell nanotube arrays

Science.gov (United States)

Tarish, Samar; Xu, Yang; Wang, Zhijie; Mate, Faten; Al-Haddad, Ahmed; Wang, Wenxin; Lei, Yong

2017-10-01

We have studied the fabrication of highly efficient glucose sensors using well-ordered heterogeneous ZnO/ZnS core/shell nanotube arrays (CSNAs). The modified electrodes exhibit a superior electrochemical response towards ferrocyanide/ferricyanide and in glucose sensing. Further, the fabricated glucose biosensor exhibited good performance over an acceptable linear range from 2.39 × 10-5 to 2.66 × 10-4 mM, with a sensitivity of 188.34 mA mM-1 cm-2, which is higher than that of the ZnO nanotube array counterpart. A low limit of detection was realized (24 μM), which is good compared with electrodes based on conventional structures. In addition, the enhanced direct electrochemistry of glucose oxidase indicates the fast electron transfer of ZnO/ZnS CSNA electrodes, with a heterogeneous electron transfer rate constant (K s) of 1.69 s-1. The fast electron transfer is attributed to the high conductivity of the modified electrodes. The presented ZnS shell can facilitate the construction of future sensors and enhance the ZnO surface in a biological environment.

Surface modification of indium tin oxide films by amino ion implantation for the attachment of multi-wall carbon nanotubes

International Nuclear Information System (INIS)

Jiao Jiao; Liu Chenyao; Chen Qunxia; Li Shuoqi; Hu Jingbo; Li Qilong

2010-01-01

Amino ion implantation was carried out at the energy of 80 keV with fluence of 5 x 10 15 ions cm -2 for indium tin oxide film (ITO) coated glass, and the existence of amino group on the ITO surface was verified by X-ray photoelectron spectroscopy analysis and Fourier transform infrared spectra. Scanning electron microscopy images show that multi-wall carbon nanotubes (MWCNTs) directly attached to the amino ion implanted ITO (NH 2 /ITO) surface homogeneously and stably. The resulting MWCNTs-attached NH 2 /ITO (MWCNTs/NH 2 /ITO) substrate can be used as electrode material. Cyclic voltammetry results indicate that the MWCNTs/NH 2 /ITO electrode shows excellent electrochemical properties and obvious electrocatalytic activity towards uric acid, thus this material is expected to have potential in electrochemical analysis and biosensors.

Enhanced field emission properties of vertically aligned double-walled carbon nanotube arrays

International Nuclear Information System (INIS)

Chen, Guohai; Shin, Dong Hoon; Lee, Cheol Jin; Iwasaki, Takayuki; Kawarada, Hiroshi

2008-01-01

Vertically aligned double-walled carbon nanotube (VA-DWCNT) arrays were synthesized by point-arc microwave plasma chemical vapor deposition on Cr/n-Si and SiO 2 /n-Si substrates. The outer tube diameters of VA-DWCNTs are in the range of 2.5-3.8 nm, and the average interlayer spacing is approximately 0.42 nm. The field emission properties of these VA-DWCNTs were studied. It was found that a VA-DWCNT array grown on a Cr/n-Si substrate had better field emission properties as compared with a VA-DWCNT array grown on a SiO 2 /n-Si substrate and randomly oriented DWCNTs, showing a turn-on field of about 0.85 V μm -1 at the emission current density of 0.1 μA cm -2 and a threshold field of 1.67 V μm -1 at the emission current density of 1.0 mA cm -2 . The better field emission performance of the VA-DWCNT array was mainly attributed to the vertical alignment of DWCNTs on the Cr/n-Si substrate and the low contact resistance between CNTs and the Cr/n-Si substrate

Solution-processed single-wall carbon nanotube transistor arrays for wearable display backplanes

Directory of Open Access Journals (Sweden)

Byeong-Cheol Kang

2018-01-01

Full Text Available In this paper, we demonstrate solution-processed single-wall carbon nanotube thin-film transistor (SWCNT-TFT arrays with polymeric gate dielectrics on the polymeric substrates for wearable display backplanes, which can be directly attached to the human body. The optimized SWCNT-TFTs without any buffer layer on flexible substrates exhibit a linear field-effect mobility of 1.5cm2/V-s and a threshold voltage of around 0V. The statistical plot of the key device metrics extracted from 35 SWCNT-TFTs which were fabricated in different batches at different times conclusively support that we successfully demonstrated high-performance solution-processed SWCNT-TFT arrays which demand excellent uniformity in the device performance. We also investigate the operational stability of wearable SWCNT-TFT arrays against an applied strain of up to 40%, which is the essential for a harsh degree of strain on human body. We believe that the demonstration of flexible SWCNT-TFT arrays which were fabricated by all solution-process except the deposition of metal electrodes at process temperature below 130oC can open up new routes for wearable display backplanes.

Fabrication of 3D interconnected porous TiO{sub 2} nanotubes templated by poly(vinyl chloride-g-4-vinyl pyridine) for dye-sensitized solar cells

Energy Technology Data Exchange (ETDEWEB)

Koh, Joo Hwan; Koh, Jong Kwan; Seo, Jin Ah; Kim, Jong Hak [Department of Chemical and Biomolecular Engineering, Yonsei University, 262 Seongsanno, Seodaemun-gu, Seoul 120-749 (Korea, Republic of); Shin, Jong-Shik, E-mail: jonghak@yonsei.ac.kr [Department of Biotechnology, Yonsei University, 262 Seongsanno, Seodaemun-gu, Seoul 120-749 (Korea, Republic of)

2011-09-07

Porous TiO{sub 2} nanotube arrays with three-dimensional (3D) interconnectivity were prepared using a sol-gel process assisted by poly(vinyl chloride-graft-4-vinyl pyridine), PVC-g-P4VP graft copolymer and a ZnO nanorod template. A 7 {mu}m long ZnO nanorod array was grown from the fluorine-doped tin oxide (FTO) glass via a liquid phase deposition method. The TiO{sub 2} sol-gel solution templated by the PVC-g-P4VP graft copolymer produced a random 3D interconnection between the adjacent ZnO nanorods during spin coating. Upon etching of ZnO, TiO{sub 2} nanotubes consisting of 10-15 nm nanoparticles were generated, as confirmed by wide-angle x-ray scattering (WAXS), energy-filtering transmission electron microscopy (EF-TEM) and field-emission scanning electron microscopy (FE-SEM). The ordered and interconnected nanotube architecture showed an enhanced light scattering effect and increased penetration of polymer electrolytes in dye-sensitized solar cells (DSSC). The energy conversion efficiency reached 1.82% for liquid electrolyte, and 1.46% for low molecular weight (M{sub w}) and 0.74% for high M{sub w} polymer electrolytes.

Fabrication of Vertically Aligned Carbon Nanotube or Zinc Oxide Nanorod Arrays for Optical Diffraction Gratings.

Science.gov (United States)

Kim, Jeong; Kim, Sun Il; Cho, Seong-Ho; Hwang, Sungwoo; Lee, Young Hee; Hur, Jaehyun

2015-11-01

We report on new fabrication methods for a transparent, hierarchical, and patterned electrode comprised of either carbon nanotubes or zinc oxide nanorods. Vertically aligned carbon nanotubes or zinc oxide nanorod arrays were fabricated by either chemical vapor deposition or hydrothermal growth, in combination with photolithography. A transparent conductive graphene layer or zinc oxide seed layer was employed as the transparent electrode. On the patterned surface defined using photoresist, the vertically grown carbon nanotubes or zinc oxides could produce a concentrated electric field under applied DC voltage. This periodic electric field was used to align liquid crystal molecules in localized areas within the optical cell, effectively modulating the refractive index. Depending on the material and morphology of these patterned electrodes, the diffraction efficiency presented different behavior. From this study, we established the relationship between the hierarchical structure of the different electrodes and their efficiency for modulating the refractive index. We believe that this study will pave a new path for future optoelectronic applications.

Influence of sol–gel parameters in the fabrication of ferromagnetic La2/3Ca1/3MnO3 nanotube arrays

International Nuclear Information System (INIS)

Kumaresavanji, M.; Sousa, C.T.; Apolinario, A.; Lopes, A.M.L.; Araujo, J.P.

2015-01-01

Graphical abstract: - Highlights: • La 2/3 Ca 1/3 MnO 3 nanotube arrays were fabricated by the alumina template assisted sol–gel method. • By varying molarity, viscosity and pH values of sol–gels, their influence was studied. • Sol–gel with 0.8 M, 29 mPa s and 4 pH is found to be suitable for the fabrication of nanotubes. • Such condition can also be applicable to the fabrication of other multicomponent oxide materials. - Abstract: Highly ordered La 2/3 Ca 1/3 MnO 3 nanotube arrays have been synthesized by porous anodic alumina template assisted sol–gel method. Precursor sol–gels with different molar concentration, viscosity and pH values have been used in the fabrication process in order to find the suitable conditions for the fabrication of such multi component oxides. Diverse characterizations such as scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD) were done to verify the structural and morphological behavior of as prepared nanotubes. Magnetic properties were also characterized with respect to temperature and field. Based on the obtained results, a possible nanotubes formation mechanism has been discussed. Depends on the percentage of nanopore filling and the morphology of nanotubes, the sol–gel parameters such as molarity, viscosity and pH have been determined as the key factors in the fabrication of nanostructured manganites which can also be applicable to the fabrication process of other multicomponent nanostructured materials

Fabrication of CdS/H-TiO2 Nanotube Arrays and Their Application for the Degradation of Methyl Orange in Aqueous Solutions

Directory of Open Access Journals (Sweden)

Xiaosong Zhou

2014-01-01

Full Text Available The fabrication and characterization of heterogeneous structures based on CdS and self-doped TiO2 nanotube arrays (H-TNTs are reported for the first time. CdS was conformally deposited onto TiO2 nanotube arrays (TNTs using a simple method of electrochemical atomic layer deposition. The as-prepared samples were characterized by scanning electron microscopy (SEM, X-ray photoelectron spectroscopy (XPS, UV-Vis diffusion reflection spectroscopy (UV-Vis DRS, and photoluminescence spectroscopy (PL techniques. Compared with pure TNTs, CdS/H-TNTs exhibit enhanced photoelectrochemical properties and photocatalytic activity under visible light. Self-doping introduces oxygen vacancies and Ti3+ species, and the electrochemical deposition technique promotes the deposition of CdS onto TiO2 nanotube walls, forming a heterojunction compact structure and resulting in decrease in photocatalytic activity under visible light.

Morphological evolution of TiO{sub 2} nanotube arrays with lotus-root-shaped nanostructure

Energy Technology Data Exchange (ETDEWEB)

Yu, Dongliang; Song, Ye; Zhu, Xufei, E-mail: zhuxufei.njust@163.com; Yang, Ruiquan; Han, Aijun

2013-07-01

TiO{sub 2} nanotube arrays (TNAs) with lotus-root-shaped nanostructure have been fabricated by a modified two-step electrochemical anodization method. In the present work, different morphologies formed under different anodizing voltages are investigated in detail by field-emission scanning electron microscope. The results show that the concaves left by the first-step anodization can guide the uniform growth of TNAs in some degree as the second-step anodizing voltage is the same with that in the first step, however, when lower voltages are adopted in the second-step anodization, no guidance can be achieved, and different morphological TNAs with lotus-root-shaped nanostructure are fabricated. And we find that the nanotube diameters are directly proportional to the applied voltage in the second-step anodization. Furthermore, a possible mechanism for the growth of the TiO{sub 2} nanotubes with the special morphology is proposed for the first time, which depends on both the oxygen bubble mold and the viscous flow of the barrier oxide from the pore base to the pore wall.

A Robust and Low-Complexity Gas Recognition Technique for On-Chip Tin-Oxide Gas Sensor Array

Directory of Open Access Journals (Sweden)

Farid Flitti

2008-01-01

Full Text Available Gas recognition is a new emerging research area with many civil, military, and industrial applications. The success of any gas recognition system depends on its computational complexity and its robustness. In this work, we propose a new low-complexity recognition method which is tested and successfully validated for tin-oxide gas sensor array chip. The recognition system is based on a vector angle similarity measure between the query gas and the representatives of the different gas classes. The latter are obtained using a clustering algorithm based on the same measure within the training data set. Experimented results on our in-house gas sensors array show more than 98% of correct recognition. The robustness of the proposed method is tested by recognizing gas measurements with simulated drift. Less than 1% of performance degradation is noted at the worst case scenario which represents a significant improvement when compared to the current state-of-the-art.

Oriented nanotube electrodes for lithium ion batteries and supercapacitors

Science.gov (United States)

Frank, Arthur J.; Zhu, Kai; Wang, Qing

2013-03-05

An electrode having an oriented array of multiple nanotubes is disclosed. Individual nanotubes have a lengthwise inner pore defined by interior tube walls which extends at least partially through the length of the nanotube. The nanotubes of the array may be oriented according to any identifiable pattern. Also disclosed is a device featuring an electrode and methods of fabrication.

Nanotube cathodes.

Energy Technology Data Exchange (ETDEWEB)

Overmyer, Donald L.; Lockner, Thomas Ramsbeck; Siegal, Michael P.; Miller, Paul Albert

2006-11-01

Carbon nanotubes have shown promise for applications in many diverse areas of technology. In this report we describe our efforts to develop high-current cathodes from a variety of nanotubes deposited under a variety of conditions. Our goal was to develop a one-inch-diameter cathode capable of emitting 10 amperes of electron current for one second with an applied potential of 50 kV. This combination of current and pulse duration significantly exceeds previously reported nanotube-cathode performance. This project was planned for two years duration. In the first year, we tested the electron-emission characteristics of nanotube arrays fabricated under a variety of conditions. In the second year, we planned to select the best processing conditions, to fabricate larger cathode samples, and to test them on a high-power relativistic electron beam generator. In the first year, much effort was made to control nanotube arrays in terms of nanotube diameter and average spacing apart. When the project began, we believed that nanotubes approximately 10 nm in diameter would yield sufficient electron emission properties, based on the work of others in the field. Therefore, much of our focus was placed on measured field emission from such nanotubes grown on a variety of metallized surfaces and with varying average spacing between individual nanotubes. We easily reproduced the field emission properties typically measured by others from multi-wall carbon nanotube arrays. Interestingly, we did this without having the helpful vertical alignment to enhance emission; our nanotubes were randomly oriented. The good emission was most likely possible due to the improved crystallinity, and therefore, electrical conductivity, of our nanotubes compared to those in the literature. However, toward the end of the project, we learned that while these 10-nm-diameter CNTs had superior crystalline structure to the work of others studying field emission from multi-wall CNT arrays, these nanotubes still

Nanotube cathodes

International Nuclear Information System (INIS)

Overmyer, Donald L.; Lockner, Thomas Ramsbeck; Siegal, Michael P.; Miller, Paul Albert

2006-01-01

Carbon nanotubes have shown promise for applications in many diverse areas of technology. In this report we describe our efforts to develop high-current cathodes from a variety of nanotubes deposited under a variety of conditions. Our goal was to develop a one-inch-diameter cathode capable of emitting 10 amperes of electron current for one second with an applied potential of 50 kV. This combination of current and pulse duration significantly exceeds previously reported nanotube-cathode performance. This project was planned for two years duration. In the first year, we tested the electron-emission characteristics of nanotube arrays fabricated under a variety of conditions. In the second year, we planned to select the best processing conditions, to fabricate larger cathode samples, and to test them on a high-power relativistic electron beam generator. In the first year, much effort was made to control nanotube arrays in terms of nanotube diameter and average spacing apart. When the project began, we believed that nanotubes approximately 10 nm in diameter would yield sufficient electron emission properties, based on the work of others in the field. Therefore, much of our focus was placed on measured field emission from such nanotubes grown on a variety of metallized surfaces and with varying average spacing between individual nanotubes. We easily reproduced the field emission properties typically measured by others from multi-wall carbon nanotube arrays. Interestingly, we did this without having the helpful vertical alignment to enhance emission; our nanotubes were randomly oriented. The good emission was most likely possible due to the improved crystallinity, and therefore, electrical conductivity, of our nanotubes compared to those in the literature. However, toward the end of the project, we learned that while these 10-nm-diameter CNTs had superior crystalline structure to the work of others studying field emission from multi-wall CNT arrays, these nanotubes still

Cyclic voltammetric study of tin hexacyanoferrate for aqueous battery applications

Directory of Open Access Journals (Sweden)

Denys Gromadskyi

2016-09-01

Full Text Available A hybrid composite containing 65 mass % of tin hexacyanoferrate mixed with 35 mass % of carbon nanotubes has been synthesized and its electrochemical behavior as a negative electrode in alkali metal-ion batteries has been studied in 1 mol L-1 aqueous solution of sodium sulfate. The specific capacity of pure tin hexacyanoferrate is 58 mAh g-1, whereas the specific capacity normalized per total electrode mass of the composite studied reaches 34 mAh g-1. The estimated maximal specific power of an aqueous alkali-metal ion battery with a tin hexacyanoferrate electrode is ca. 3.6 kW kg-1 being comparable to characteristics of industrial electric double-layer capacitors. The maximal specific energy accumulated by this battery may reach 25.6 Wh kg-1 at least three times exceeding the specific energy for supercapacitors.

Photoelectric Properties of Silicon Nanocrystals/P3HT Bulk-Heterojunction Ordered in Titanium Dioxide Nanotube Arrays

Directory of Open Access Journals (Sweden)

Švrček Vladimir

2009-01-01

Full Text Available Abstract A silicon nanocrystals (Si-ncs conjugated-polymer-based bulk-heterojunction represents a promising approach for low-cost hybrid solar cells. In this contribution, the bulk-heterojunction is based on Si-ncs prepared by electrochemical etching and poly(3-hexylthiophene (P3HT polymer. Photoelectric properties in parallel and vertical device-like configuration were investigated. Electronic interaction between the polymer and surfactant-free Si-ncs is achieved. Temperature-dependent photoluminescence and transport properties were studied and the ratio between the photo- and dark-conductivity of 1.7 was achieved at ambient conditions. Furthermore the porous titanium dioxide (TiO2 nanotubes’ template was used for vertical order of photosensitive Si-ncs/P3HT-based blend. The anodization of titanium foil in ethylene glycol-based electrolyte containing fluoride ions and subsequent thermal annealing were used to prepare anatase TiO2nanotube arrays. The arrays with nanotube inner diameter of 90 and 50 nm were used for vertical ordering of the Si-ncs/P3HT bulk-heterojunction.

Electrodeposition synthesis of MnO{sub 2}/TiO{sub 2} nanotube arrays nanocomposites and their visible light photocatalytic activity

Energy Technology Data Exchange (ETDEWEB)

Xu, Xuyao [School of Chemistry Science and Technology, and Institute of Physical Chemistry, Zhanjiang Normal University, Zhanjiang 524048 (China); Zhou, Xiaosong, E-mail: zxs801213@163.com [School of Chemistry Science and Technology, and Institute of Physical Chemistry, Zhanjiang Normal University, Zhanjiang 524048 (China); Li, Xiaoyu, E-mail: lixiaoyu@iga.ac.cn [Key Laboratory of Wetland Ecology and Environment, Northeast Institute of Geography and Agroecology, Chinese Academy of Science, Changchun 130012 (China); Yang, Fei [The State Key Laboratory of Resources and Environmental Information System, Institute of Geographic Sciences and Natural Resources Research of Chinese Academy of Sciences, 11A, Datun Road, Chaoyang District, Beijing 100101 (China); Jin, Bei; Xu, Tan; Li, Guosheng; Li, Manyi [School of Chemistry Science and Technology, and Institute of Physical Chemistry, Zhanjiang Normal University, Zhanjiang 524048 (China)

2014-11-15

Highlights: • MnO{sub 2}/TiO{sub 2} nanotube arrays nanocomposites are prepared by electrodeposition. • MnO{sub 2}/TiO{sub 2} exhibits high visible light photocatalytic activity. • The results of XRD show the depositions are attributed to α-MnO{sub 2}. • A photocatalytic mechanism is discussed under visible light irradiation. - Abstract: MnO{sub 2}/TiO{sub 2} nanotube arrays nanocomposite photocatalysts have been synthesized through an electrodeposition method. X-ray powder diffraction analysis and X-ray photoelectron spectroscopy measurements reveal that the products of electrodeposition method are MnO{sub 2}. Scanning electron microscopy measurements suggest that the depositions are deposited on the surface or internal of the nanotube. UV–vis light absorbance spectra demonstrate the excellent adsorption properties of MnO{sub 2}/TiO{sub 2} over the whole region of visible light, which enables this novel photocatalytic material to possess remarkable activity in the photocatalytic degradation of acid Orange II under visible light radiation. Moreover, a possible photocatalytic mechanism is discussed.

1D goes 2D: A Berezinskii-Kosterlitz-Thouless transition in superconducting arrays of 4-Angstrom carbon nanotubes

KAUST Repository

Wang, Zhe

2010-10-01

We report superconducting resistive transition characteristics for array(s) of coupled 4-Angstrom single wall carbon nanotubes embedded in aluminophosphate-five zeolite. The transition was observed to initiate at 15 K with a slow resistance decrease switching to a sharp, order of magnitude drop between 7.5 and 6.0 K with strong (anisotropic) magnetic field dependence. Both the sharp resistance drop and its attendant nonlinear IV characteristics are consistent with the manifestations of a Berezinskii-Kosterlitz-Thouless transition that establishes quasi long range order in the plane transverse to the c-axis of the nanotubes, leading to an inhomogeneous system comprising 3D superconducting regions connected by weak links. Global coherence is established at below 5 K with the appearance of a well-defined supercurrent gap/low resistance region at 2 K. © 2010 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effects of Titanium Oxide Nanotube Arrays with Different Lengths on the Characteristics of Dye-Sensitized Solar Cells

Directory of Open Access Journals (Sweden)

Chin-Guo Kuo

2013-01-01

Full Text Available The self-aligned highly ordered TiO2 nanotube (TNT arrays were fabricated by potentiostatic anodization of Ti foil, and we found that the TNT-array length and diameter were dependent on the electrolyte (NH4F concentration in ethylene glycol and anodization time. The characteristics of the fabricated TNT arrays were characterized by XRD pattern, FESEM, and absorption spectrum. As the electrolyte NH4F concentration in the presence of H2O (2 vol% with anodization was changed from 0.25 to 0.75 wt% and the anodization period was increased from 1 to 5 h, the TNT-array length was changed from 9.55 to 30.2 μm and the TNT-array diameter also increased. As NH4F concentration was 0.5 wt%, the prepared TNT arrays were also used to fabricate the dye-sensitized solar cells (DSSCs. We would show that the measured photovoltaic performance of the DSSCs was dependent on the TNT-array length.

Photoelectrochemical oxidation of ibuprofen via Cu{sub 2}O-doped TiO{sub 2} nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Sun, Qiannan [College of Environment and Energy, South China University of Technology, Guangzhou (China); Peng, Yen-Ping, E-mail: yppeng@thu.edu.tw [Department of Environmental Science and Engineering, Tunghai University, Taichung, Taiwan (China); Chen, Hanlin [College of Environment and Energy, South China University of Technology, Guangzhou (China); Chang, Ken-Lin [School of Environmental Science and Engineering and Institute of Environmental Health and Pollution Control, Guangdong University of Technology, Guangzhou, 51006 China (China); Qiu, Yang-Neng; Lai, Shiau-Wu [Department of Environmental Science and Engineering, Tunghai University, Taichung, Taiwan (China)

2016-12-05

Highlights: • A p–n junction material was synthesized to enhance photocatalytic ability. • Cu{sub 2}O-doped TiO{sub 2} nanotube arrays works as a photoanode in a PEC system. • Recombination of photo-generated holes and electrons were greatly reduced. • Synergetic effect was quantified in PEC degradation. • Recombination of photogenerated holes and electrons was greatly enhanced. - Abstract: A p–n junction based Cu{sub 2}O-doped TiO{sub 2} nanotube arrays (Cu{sub 2}O-TNAs) were synthesized and used as a working anode in a photoelectrochemical (PEC) system. The results revealed that the Cu{sub 2}O-TNAs were dominated by the anatase phase and responded significantly to visible light. XPS analyses indicated that with an amount of 24.79% Cu doping into the structure, the band gap of Cu{sub 2}O-TNAs was greatly reduced. SEM images revealed that the supported TiO{sub 2} nanotubes had diameters of approximately 80 nm and lengths of about 2.63 μm. Upon doping with Cu{sub 2}O, the TiO{sub 2} nanotubes maintained their structural integrity, exhibiting no significant morphological change, favoring PEC applications. Under illumination, the photocurrent from Cu{sub 2}O/TNAs was 2.4 times larger than that from TNAs, implying that doping with Cu{sub 2}O significantly improved electron mobility by reducing the rate of recombination of electron-hole pairs. The EIS and Bode plot revealed that the estimated electron lifetimes, τ{sub el}, of TNAs and Cu{sub 2}O/TNAs were 6.91 and 26.26 ms, respectively. The efficiencies of degradation of Ibuprofen by photoelectrochemical, photocatalytic (PC), electrochemical (EC) and photolytic (P) methods were measured.

Direct current injection and thermocapillary flow for purification of aligned arrays of single-walled carbon nanotubes

Energy Technology Data Exchange (ETDEWEB)

Xie, Xu; Islam, Ahmad E.; Seabron, Eric; Dunham, Simon N.; Du, Frank; Lin, Jonathan; Wilson, William L.; Rogers, John A., E-mail: jrogers@illinois.edu [Department of Materials Science and Engineering, Frederick Seitz Materials Research Laboratory, University of Illinois at Urbana-Champaign, Urbana, Illinois 61801 (United States); Wahab, Muhammad A.; Alam, Muhammad A. [School of Electrical and Computer Engineering, Purdue University, West Lafayette, Indiana 47907 (United States); Li, Yuhang [Institute of Solid Mechanics, Beihang University, Beijing 100191 (China); Tomic, Bojan [Department of Electrical Engineering, University of Illinois at Urbana-Champaign, Urbana, Illinois 61801 (United States); Huang, Jiyuan [Department of Physics, University of Illinois at Urbana-Champaign, Urbana, Illinois 61801 (United States); Burns, Branden [Department of Physics, Purdue University, West Lafayette, Indiana 47907 (United States); Song, Jizhou [Department of Engineering Mechanics and Soft Matter Research Center, Zhejiang University, Hangzhou 310027 (China); Huang, Yonggang [Department of Civil and Environmental Engineering, Department of Mechanical Engineering, Center for Engineering and Health, and Skin Disease Research Center, Northwestern University, Evanston, Illinois 60208 (United States)

2015-04-07

Aligned arrays of semiconducting single-walled carbon nanotubes (s-SWNTs) represent ideal configurations for use of this class of material in high performance electronics. Development of means for removing the metallic SWNTs (m-SWNTs) in as-grown arrays represents an essential challenge. Here, we introduce a simple scheme that achieves this type of purification using direct, selective current injection through interdigitated electrodes into the m-SWNTs, to allow their complete removal using processes of thermocapillarity and dry etching. Experiments and numerical simulations establish the fundamental aspects that lead to selectivity in this process, thereby setting design rules for optimization. Single-step purification of arrays that include thousands of SWNTs demonstrates the effectiveness and simplicity of the procedures. The result is a practical route to large-area aligned arrays of purely s-SWNTs with low-cost experimental setups.

Direct current injection and thermocapillary flow for purification of aligned arrays of single-walled carbon nanotubes

International Nuclear Information System (INIS)

Xie, Xu; Islam, Ahmad E.; Seabron, Eric; Dunham, Simon N.; Du, Frank; Lin, Jonathan; Wilson, William L.; Rogers, John A.; Wahab, Muhammad A.; Alam, Muhammad A.; Li, Yuhang; Tomic, Bojan; Huang, Jiyuan; Burns, Branden; Song, Jizhou; Huang, Yonggang

2015-01-01

Aligned arrays of semiconducting single-walled carbon nanotubes (s-SWNTs) represent ideal configurations for use of this class of material in high performance electronics. Development of means for removing the metallic SWNTs (m-SWNTs) in as-grown arrays represents an essential challenge. Here, we introduce a simple scheme that achieves this type of purification using direct, selective current injection through interdigitated electrodes into the m-SWNTs, to allow their complete removal using processes of thermocapillarity and dry etching. Experiments and numerical simulations establish the fundamental aspects that lead to selectivity in this process, thereby setting design rules for optimization. Single-step purification of arrays that include thousands of SWNTs demonstrates the effectiveness and simplicity of the procedures. The result is a practical route to large-area aligned arrays of purely s-SWNTs with low-cost experimental setups

Fabrication and photoelectrochemical properties of ZnS/Au/TiO2 nanotube array films.

Science.gov (United States)

Zhu, Yan-Feng; Zhang, Juan; Xu, Lu; Guo, Ya; Wang, Xiao-Ping; Du, Rong-Gui; Lin, Chang-Jian

2013-03-21

A highly ordered TiO(2) nanotube array film was fabricated by an anodic oxidation method. The film was modified by Au nanoparticles (NPs) formed by a deposition-precipitation technique and was covered with a thin ZnS shell prepared by a successive ionic layer adsorption and reaction (SILAR) method. The photoelectrochemical properties of the prepared ZnS/Au/TiO(2) composite film were evaluated by incident photon-to-current conversion efficiency (IPCE), and photopotential and electrochemical impedance spectroscopy (EIS) measurements under white light illumination. The results indicated that the Au NPs could expand the light sensitivity range of the film and suppress the electron-hole recombination, and the ZnS shell could inhibit the leakage of photogenerated electrons from the surface of Au NPs to the ZnS/electrolyte interface. When the 403 stainless steel in a 0.5 M NaCl solution was coupled to the ZnS/Au/TiO(2) nanotube film photoanode under illumination, its potential decreased by 400 mV, showing that the composite film had a better photocathodic protection effect on the steel than that of a pure TiO(2) nanotube film.

On-Chip Sorting of Long Semiconducting Carbon Nanotubes for Multiple Transistors along an Identical Array.

Science.gov (United States)

Otsuka, Keigo; Inoue, Taiki; Maeda, Etsuo; Kometani, Reo; Chiashi, Shohei; Maruyama, Shigeo

2017-11-28

Ballistic transport and sub-10 nm channel lengths have been achieved in transistors containing one single-walled carbon nanotube (SWNT). To fill the gap between single-tube transistors and high-performance logic circuits for the replacement of silicon, large-area, high-density, and purely semiconducting (s-) SWNT arrays are highly desired. Here we demonstrate the fabrication of multiple transistors along a purely semiconducting SWNT array via an on-chip purification method. Water- and polymer-assisted burning from site-controlled nanogaps is developed for the reliable full-length removal of metallic SWNTs with the damage to s-SWNTs minimized even in high-density arrays. All the transistors with various channel lengths show large on-state current and excellent switching behavior in the off-state. Since our method potentially provides pure s-SWNT arrays over a large area with negligible damage, numerous transistors with arbitrary dimensions could be fabricated using a conventional semiconductor process, leading to SWNT-based logic, high-speed communication, and other next-generation electronic devices.

Fabrication of transparent TiO2 nanotube-based photoanodes for CdS/CdTe quantum co-sensitized solar cells

Science.gov (United States)

Gualdrón-Reyes, A. F.; Cárdenas-Arenas, A.; Martínez, C. A.; Kouznetsov, V. V.; Meléndez, A. M.

2017-01-01

In order to fabricate a solar cell, ordered TiO2 nanotube (TNT) arrays were prepared by double anodization. TNT arrays with variable lengths were obtained by changing the duration of the anodizing process of up to 3h. TNT membranes were transferred to indium tin oxide substrates and attached with a B-TiO2 sol. TNT photoanode with the best photoelectrochemical performance was sensitized with CdS by SILAR method. On other hand, CdTe quantum dots prepared via colloidal synthesis were deposited on TNT photoanodes for 2h, 4h and 6h. In addition, TNT/CdS was loaded with CdTe quantum dots for 4 h. Morphology and chemical modification of TiO2 were characterized by FESEM and XPS, while their photoelectrochemical performance was measured by open-circuit photopotential and photovoltammetry under visible light. TiO2 nanotubes grown during 2.5h showed the highest photocurrent due to presence of Ti3+ donor states by N and F co-doping, increasing the number of photogenerated electrons transported to back collector. TNT/CdS/CdTe photoanode reach the highest conversion efficiency under AM 1.5G simulated solar illumination.

Preparation of Janus Particles and Alternating Current Electrokinetic Measurements with a Rapidly Fabricated Indium Tin Oxide Electrode Array.

Science.gov (United States)

Chen, Yu-Liang; Jiang, Hong-Ren

2017-06-23

This article provides a simple method to prepare partially or fully coated metallic particles and to perform the rapid fabrication of electrode arrays, which can facilitate electrical experiments in microfluidic devices. Janus particles are asymmetric particles that contain two different surface properties on their two sides. To prepare Janus particles, a monolayer of silica particles is prepared by a drying process. Gold (Au) is deposited on one side of each particle using a sputtering device. The fully coated metallic particles are completed after the second coating process. To analyze the electrical surface properties of Janus particles, alternating current (AC) electrokinetic measurements, such as dielectrophoresis (DEP) and electrorotation (EROT)- which require specifically designed electrode arrays in the experimental device- are performed. However, traditional methods to fabricate electrode arrays, such as the photolithographic technique, require a series of complicated procedures. Here, we introduce a flexible method to fabricate a designed electrode array. An indium tin oxide (ITO) glass is patterned by a fiber laser marking machine (1,064 nm, 20 W, 90 to 120 ns pulse-width, and 20 to 80 kHz pulse repetition frequency) to create a four-phase electrode array. To generate the four-phase electric field, the electrodes are connected to a 2-channel function generator and to two invertors. The phase shift between the adjacent electrodes is set at either 90° (for EROT) or 180° (for DEP). Representative results of AC electrokinetic measurements with a four-phase ITO electrode array are presented.

TiO2 Nanotubes on Transparent Substrates: Control of Film Microstructure and Photoelectrochemical Water Splitting Performance

Directory of Open Access Journals (Sweden)

Matus Zelny

2018-01-01

Full Text Available Transfer of semiconductor thin films on transparent and or flexible substrates is a highly desirable process to enable photonic, catalytic, and sensing technologies. A promising approach to fabricate nanostructured TiO2 films on transparent substrates is self-ordering by anodizing of thin metal films on fluorine-doped tin oxide (FTO. Here, we report pulsed direct current (DC magnetron sputtering for the deposition of titanium thin films on conductive glass substrates at temperatures ranging from room temperature to 450 °C. We describe in detail the influence that deposition temperature has on mechanical, adhesion and microstructural properties of titanium film, as well as on the corresponding TiO2 nanotube array obtained after anodization and annealing. Finally, we measure the photoelectrochemical water splitting activity of different TiO2 nanotube samples showing that the film deposited at 150 °C has much higher activity correlating well with the lower crystallite size and the higher degree of self-organization observed in comparison with the nanotubes obtained at different temperatures. Importantly, the film showing higher water splitting activity does not have the best adhesion on glass substrate, highlighting an important trade-off for future optimization.

Organic vapor discrimination with chemiresistor arrays of temperature modulated tin-oxide nanowires and thiolate-monolayer-protected gold nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Scholten, K; Bohrer, F I; Dattoli, E; Lu, W; Zellers, E T, E-mail: ezellers@umich.edu [Center for Wireless Integrated Microsystems, University of Michigan, Ann Arbor, MI 48109-2122 (United States)

2011-03-25

This paper explores the discrimination of organic vapors with arrays of chemiresistors (CRs) employing interface layers of tin-oxide nanowires (NWs) and thiolate-monolayer-protected gold nanoparticles (MPNs). The former devices use contact-printed mats of NWs on micro-hotplate membranes to bridge a pair of metal electrodes. Oxidation at the NW surface causes changes in charge transport, the temperature dependence of which differs among different vapors, permitting vapor discrimination. The latter devices use solvent cast films of MPNs on interdigital electrodes operated at room temperature. Sorption into the organic monolayers causes changes in film tunneling resistance that differ among different vapors and MPN structures, permitting vapor discrimination. Here, we compare the performance and assess the 'complementarity' of these two types of sensors. Calibrated responses from an NW CR operated at two different temperatures and from a set of four different MPN CRs were generated for three test vapors: n-hexane, toluene, and nitromethane. This pooled data set was then analyzed using principal components regression classification models with varying degrees of random error superimposed on the responses via Monte Carlo simulation in order to estimate the rates of recognition/discrimination for arrays comprising different combinations of sensors. Results indicate that the diversity of most of the dual MPN-CR arrays exceeds that of the dual NW-CR array. Additionally, in assessing all possible arrays of 4-6 CR sensors, the recognition rates of the hybrid arrays (i.e. MPN + NW) were no better than that of the 4-sensor array containing only MPN CRs.

Using a cut-paste method to prepare a carbon nanotube fur electrode

International Nuclear Information System (INIS)

Zhang, H; Cao, G P; Yang, Y S

2007-01-01

We describe and realize an aligned carbon nanotube array based 'carbon nanotube fur (CNTF)' electrode. We removed an 800 μm long aligned carbon nanotube array from the silica substrate, and then pasted the array on a nickel foam current collector to obtain a CNTF electrode. CNTF's characteristics and electrochemical properties were studied systemically in this paper. The cut-paste method is simple, and does not damage the microstructure of the aligned carbon nanotube array. The CNTF electrode obtained a specific capacitance of 14.1 F g -1 and excellent rate capability

Substrate morphology induced self-organization into carbon nanotube arrays, ropes, and agglomerates.

Science.gov (United States)

Huang, Jia-Qi; Zhang, Qiang; Xu, Guang-Hui; Qian, Wei-Zhong; Wei, Fei

2008-10-29

In this paper, hydrophobic carbon nanotube (CNT) arrays, ropes, and agglomerates were synthesized through self-organization on quartz substrates with different micro-structures under the same growth condition. On a flat substrate, a uniform woven structure was formed which resulted in a synchronous growth into an array. When the substrate with 10 µm round concaves distributed on the surface was adopted, the woven structure was sporadic and a CNT cluster was grown in the concave. With further growth, CNT ropes were self-organized. Subsequently, when the substrate consisting of irregular ∼100 nm gaps was used, the initial woven structure was high density, thus resulting in the formation of CNT agglomerates. Study results showed that CNT arrays grown on the flat substrate were of the highest purity and had a contact angle of 153.8 ± 0.9°. Thus, the self-organization behavior among CNTs was in situ modulated by different substrate morphology without further treatments. This provides us with an additional understanding of the self-organization of CNTs during growth, as well as strategies for the controllable synthesis of CNTs with fixed properties.

Substrate morphology induced self-organization into carbon nanotube arrays, ropes, and agglomerates

International Nuclear Information System (INIS)

Huang Jiaqi; Zhang Qiang; Xu Guanghui; Qian Weizhong; Wei Fei

2008-01-01

In this paper, hydrophobic carbon nanotube (CNT) arrays, ropes, and agglomerates were synthesized through self-organization on quartz substrates with different micro-structures under the same growth condition. On a flat substrate, a uniform woven structure was formed which resulted in a synchronous growth into an array. When the substrate with 10 μm round concaves distributed on the surface was adopted, the woven structure was sporadic and a CNT cluster was grown in the concave. With further growth, CNT ropes were self-organized. Subsequently, when the substrate consisting of irregular ∼100 nm gaps was used, the initial woven structure was high density, thus resulting in the formation of CNT agglomerates. Study results showed that CNT arrays grown on the flat substrate were of the highest purity and had a contact angle of 153.8 ± 0.9 0 . Thus, the self-organization behavior among CNTs was in situ modulated by different substrate morphology without further treatments. This provides us with an additional understanding of the self-organization of CNTs during growth, as well as strategies for the controllable synthesis of CNTs with fixed properties.

Photoelectrochemical performance of cadmium sulfide quantum dots modified titania nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Xie, Yibing, E-mail: ybxie@seu.edu.cn

2016-01-01

The cadmium sulfide quantum dots modified titania nanotube arrays (CdS QDs/TiO{sub 2} NTAs) were prepared through a sequential sonication-assisted chemical bath deposition (CBD) process. The morphology and microstructure of CdS QDs/TiO{sub 2} NTAs were characterized using scanning electron microscopy, transmission electron microscopy, X-ray diffraction spectroscopy, energy-dispersive X-ray spectroscopy, Raman spectroscopy and UV–vis diffuse reflectance spectroscopy. The photoelectrochemical performance of CdS QDs/TiO{sub 2} NTAs was investigated under solar light illumination. The affecting parameters were studied including the nanotube length of TiO{sub 2} NTAs, CBD cycles of CdS QDs and the annealing treatment of CdS QDs/TiO{sub 2} NTAs. CdS QDs synthesized through 8 CBD cycles could uniformly cover on the tube walls of TiO{sub 2} NTAs to form unique CdS QDs/TiO{sub 2} NTAs with an open pore mouth. The appropriate annealing treatment at 400 °C for 60 min in N{sub 2} atmosphere could improve the crystallinity of CdS QDs, and accordingly enhance the photovoltaic properties of CdS QDs/TiO{sub 2} NTAs. Significantly, the nanotube length was the predominant factor affecting photoelectrochemical performance of CdS QDs/TiO{sub 2} NTAs. The unannealed CdS QDs/TiO{sub 2} NTAs with an optimal nanotube length of 12 μm achieved a short-circuit photocurrent density of 4.37 mA cm{sup −2}, an open circuit photovoltage of 1.10 V and a top photoconversion efficiency of 3.56%. Comparatively, the annealed CdS QDs/TiO{sub 2} NTAs with an optimal nanotube length of 4 μm achieved a short-circuit photocurrent density of 6.31 mA cm{sup −2}, an open circuit photovoltage of 1.23 V and a top photoconversion efficiency of 4.18%. The suitable modification of crystalline CdS QDs could well improve the photoelectrochemical performance of TiO{sub 2} NTAs photoanode. - Highlights: • CdS QDs are uniformly loaded into short and long TiO{sub 2} NTAs to form CdS QDs/TiO{sub 2} NTAs. �

A one-step technique to prepare aligned arrays of carbon nanotubes

Energy Technology Data Exchange (ETDEWEB)

Mahanandia, Pitamber [Department of Physics, Indian Institute of Science, Bangalore 560012 (India); Nanda, Karuna Kar [Materials Research Centre, Indian Institute of Science, Bangalore 560012 (India)], E-mail: pitam@physics.iisc.ernet.in

2008-04-16

A simple effective pyrolysis technique has been developed to synthesize aligned arrays of multi-walled carbon nanotubes (MWCNTs) without using any carrier gas in a single-stage furnace at 700 deg. C. This technique eliminates nearly the entire complex and expensive machinery associated with other extensively used methods for preparation of CNTs such as chemical vapour deposition (CVD) and pyrolysis. Carbon source materials such as xylene, cyclohexane, camphor, hexane, toluene, pyridine and benzene have been pyrolyzed separately with the catalyst source material ferrocene to obtain aligned arrays of MWCNTs. The synthesized CNTs have been characterized by scanning electron microscopy (SEM), x-ray diffraction (XRD), transmission electron microscopy (TEM), thermogravimetric analysis (TGA) and Raman spectroscopy. In this technique, the need for the tedious and time-consuming preparation of metal catalysts and continuously fed carbon source material containing carrier gas can be avoided. This method is a single-step process where not many parameters are required to be monitored in order to prepare aligned MWCNTs. For the production of CNTs, the technique has great advantages such as low cost and easy operation.

Ni nanotube array-based electrodes by electrochemical alloying and de-alloying for efficient water splitting.

Science.gov (United States)

Teng, Xue; Wang, Jianying; Ji, Lvlv; Lv, Yaokang; Chen, Zuofeng

2018-05-17

The design of cost-efficient earth-abundant catalysts with superior performance for the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) is extremely important for future renewable energy production. Herein, we report a facile strategy for constructing Ni nanotube arrays (NTAs) on a Ni foam (NF) substrate through cathodic deposition of NiCu alloy followed by anodic stripping of metallic Cu. Based on Ni NTAs, the as-prepared NiSe2 NTA electrode by NiSe2 electrodeposition and the NiFeOx NTA electrode by dipping in Fe3+ solution exhibit excellent HER and OER performance in alkaline conditions. In these systems, Ni NTAs act as a binder-free multifunctional inner layer to support the electrocatalysts, offer a large specific surface area and serve as a fast electron transport pathway. Moreover, an alkaline electrolyzer has been constructed using NiFeOx NTAs as the anode and NiSe2 NTAs as the cathode, which only demands a cell voltage of 1.78 V to deliver a water-splitting current density of 500 mA cm-2, and demonstrates remarkable stability during long-term electrolysis. This work provides an attractive method for the design and fabrication of nanotube array-based catalyst electrodes for highly efficient water-splitting.

Preparation and photoluminescence properties of Tm{sup 3+}-doped ZrO{sub 2} nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Wang, Mingli [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China); Zhao, Jianling, E-mail: hebutzhaoj@126.com [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China); Xu, Rongqing [Tianjin Zhonghuan Advanced Material & Technology Co., LTD, Tianjin 300384 (China); Fu, Ning [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China); Wang, Xixin, E-mail: xixinwang@126.com [School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130 (China)

2016-07-25

Tm{sup 3+}-doped ZrO{sub 2} nanotube arrays were prepared by anodization of a Zr–Tm alloy (3 at.% Tm) obtained by a powder metallurgical method. The morphologies, structures, elemental valence, and photoluminescence properties were characterized by using scanning electron microscope, X-ray diffractometer, X-ray photoelectron spectrometer and photoluminescence analyser, respectively. Results show that preparing conditions and annealing temperatures have significant effects on the crystalline structure and photoluminescence performance. The sample TmZNT-Org prepared in formamide + glycerol organic solution is mainly monoclinic phase and the sample TmZNT-Aq prepared in aqueous solution is mainly tetragonal phase. The sample TmZNT-Org had the strongest photoluminescence peak when annealed at 800 °C, whereas both TmZNT-Aq samples annealed at 600 °C and 800 °C had the strongest photoluminescence peak. The monoclinic phase was conductive to the emission at 454 nm while the tetragonal phase was conductive to the emission at 460 nm. - Highlights: • Tm{sup 3+}-doped ZrO{sub 2} nanotube arrays were prepared by anodization of a Zr-Tm alloy. • Crystal structure had remarkable effects on the photoluminescence properties. • The monoclinic phase was conductive to the emission at 454 nm. • The tetragonal phase was conductive to the emission at 460 nm.

Three-dimensional electrodes for dye-sensitized solar cells: synthesis of indium-tin-oxide nanowire arrays and ITO/TiO2 core-shell nanowire arrays by electrophoretic deposition

International Nuclear Information System (INIS)

Wang, H-W; Ting, C-F; Hung, M-K; Chiou, C-H; Liu, Y-L; Liu Zongwen; Ratinac, Kyle R; Ringer, Simon P

2009-01-01

Dye-sensitized solar cells (DSSCs) show promise as a cheaper alternative to silicon-based photovoltaics for specialized applications, provided conversion efficiency can be maximized and production costs minimized. This study demonstrates that arrays of nanowires can be formed by wet-chemical methods for use as three-dimensional (3D) electrodes in DSSCs, thereby improving photoelectric conversion efficiency. Two approaches were employed to create the arrays of ITO (indium-tin-oxide) nanowires or arrays of ITO/TiO 2 core-shell nanowires; both methods were based on electrophoretic deposition (EPD) within a polycarbonate template. The 3D electrodes for solar cells were constructed by using a doctor-blade for coating TiO 2 layers onto the ITO or ITO/TiO 2 nanowire arrays. A photoelectric conversion efficiency as high as 4.3% was achieved in the DSSCs made from ITO nanowires; this performance was better than that of ITO/TiO 2 core-shell nanowires or pristine TiO 2 films. Cyclic voltammetry confirmed that the reaction current was significantly enhanced when a 3D ITO-nanowire electrode was used. Better separation of charge carriers and improved charge transport, due to the enlarged interfacial area, are thought to be the major advantages of using 3D nanowire electrodes for the optimization of DSSCs.

A Porous Perchlorate-Doped Polypyrrole Nanocoating on Nickel Nanotube Arrays for Stable Wide-Potential-Window Supercapacitors.

Science.gov (United States)

Chen, Gao-Feng; Li, Xian-Xia; Zhang, Li-Yi; Li, Nan; Ma, Tian Yi; Liu, Zhao-Qing

2016-09-01

A bottom-up synthetic strategy is developed to fabricate a highly porous wave-superposed perchlorate-doped polypyrrole nanocoating on nickel nanotube arrays. The delicate nanostructure and the unique surface chemistry synergistically endow the obtained electrode with revealable pseudocapacitance, large operating potential window, and excellent cycling stability, which are highly promising for both asymmetric and symmetric supercapacitors. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

In situ growth of NiCo2S4 nanotube arrays on Ni foam for supercapacitors: Maximizing utilization efficiency at high mass loading to achieve ultrahigh areal pseudocapacitance

Science.gov (United States)

Chen, Haichao; Jiang, Jianjun; Zhang, Li; Xia, Dandan; Zhao, Yuandong; Guo, Danqing; Qi, Tong; Wan, Houzhao

2014-05-01

Self-standing NiCo2S4 nanotube arrays have been in situ grown on Ni foam by the anion-exchange reaction and directly used as the electrode for supercapacitors. The NiCo2S4 nanotube in the arrays effectively reduces the inactive material and increases the electroactive surface area because of the ultrathin wall, which is quite competent to achieve high utilization efficiency at high electroactive materials mass loading. The NiCo2S4 nanotube arrays hybrid electrode exhibits an ultrahigh specific capacitance of 14.39 F cm-2 at 5 mA cm-2 with excellent rate performance (67.7% retention for current increases 30 times) and cycling stability (92% retention after 5000 cycles) at a high mass loading of 6 mg cm-2. High areal capacitance (4.68 F cm-2 at 10 mA cm-2), high energy density (31.5 Wh kg-1 at 156.6 W kg-1) and high power density (2348.5 W kg-1 at 16.6 Wh kg-1) can be achieved by assembling asymmetric supercapacitor with reduced graphene oxide at a total active material mass loading as high as 49.5 mg. This work demonstrates that NiCo2S4 nanotube arrays structure is a superior electroactive material for high-performance supercapacitors even at a mass loading of potential application-specific scale.

Exploring aligned-carbon-nanotubes@polyaniline arrays on household Al as supercapacitors.

Science.gov (United States)

Huang, Fan; Lou, Fengliu; Chen, De

2012-05-01

Herein, we demonstrate a new approach towards the construction of supercapacitors consisting of carbon nanotubes (CNTs) and conducting polymers (ECPs) with high specific power, high specific energy, and stable cycling performance through a 3D design of a thin film of polyaniline (PANI) on an aligned small carbon nanotube (ACNT) array on household Al foils. The thin-film strategy is used to fully exploit the specific capacitance of PANI, and obtain regular pores, strong interaction between PANI and CNTs, and reduced electrical resistance for the electrodes. A facile process is developed to fabricate a highly flexible supercapacitor using this binder-free composite on household Al foil as the current collector. It exhibits high specific energy of 18.9 Wh kg(-1) , high maximum specific power of 11.3 kW kg(-1) of the active material in an aqueous electrolyte at 1.0 A g(-1) , and excellent rate performance and cycling stability. A high specific energy of 72.4 Wh kg(-1) , a high maximum specific power of 24.9 kW kg(-1) , and a good cycling performance of the active material are obtained in an organic electrolyte. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effect of density variation and non-covalent functionalization on the compressive behavior of carbon nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Misra, A [Instrumentation and Applied Physics, Indian Institute of Science, Bangalore, 560012 (India); Raney, J R; Craig, A E; Daraio, C, E-mail: daraio@caltech.edu [Engineering and Applied Science, California Institute of Technology, Pasadena, CA 91125 (United States)

2011-10-21

Arrays of aligned carbon nanotubes (CNTs) have been proposed for different applications, including electrochemical energy storage and shock-absorbing materials. Understanding their mechanical response, in relation to their structural characteristics, is important for tailoring the synthesis method to the different operational conditions of the material. In this paper, we grow vertically aligned CNT arrays using a thermal chemical vapor deposition system, and we study the effects of precursor flow on the structural and mechanical properties of the CNT arrays. We show that the CNT growth process is inhomogeneous along the direction of the precursor flow, resulting in varying bulk density at different points on the growth substrate. We also study the effects of non-covalent functionalization of the CNTs after growth, using surfactant and nanoparticles, to vary the effective bulk density and structural arrangement of the arrays. We find that the stiffness and peak stress of the materials increase approximately linearly with increasing bulk density.

Effects of TiN coating on the corrosion of nanostructured Ti-30Ta-xZr alloys for dental implants

Science.gov (United States)

Kim, Won-Gi; Choe, Han-Cheol

2012-01-01

Electrochemical characteristics of a titanium nitride (TiN)-coated/nanotube-formed Ti-Ta-Zr alloy for biomaterials have been researched by using the magnetic sputter and electrochemical methods. Ti-30Ta-xZr (x = 3, 7 and 15 wt%) alloys were prepared by arc melting and heat treated for 24 h at 1000 °C in an argon atmosphere and then water quenching. The formation of oxide nanotubes was achieved by anodizing a Ti-30Ta-xZr alloy in H3PO4 electrolytes containing small amounts of fluoride ions at room temperature. Anodization was carried out using a scanning potentiostat, and all experiments were conducted at room temperature. The microstructure and morphology of nanotube arrays were characterized by optical microscopy (OM), field emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD). The TiN coatings were obtained by the radio-frequency (RF) magnetron sputtering technique. The depositions were performed from pure Ti targets on Ti-30Ta-xZr alloys substrates. The corrosion properties of the specimens were examined using potentiodynamic test in a 0.9% NaCl solution by using potentiostat. The microstructures of Ti-30Ta-xZr alloys were changed from an equiaxed to a needle-like structure with increasing Zr content. The interspace between the nanotubes was approximately 20, 80 and 200 nm for Zr contents of 3, 7 and 15 wt%, respectively. The corrosion resistance of the TiN-coated on the anodized Ti-30Ta-xZr alloys was higher than that of the untreated Ti alloys, indicating a better protective effect.

Synthesis and optical characterization of carbon nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Rahman, Md. Mahfuzur, E-mail: mrahman@masdar.ac.ae [Institute Centre for Energy (iEnergy), Mechanical and Materials Engineering Department, Masdar Institute of Science and Technology (MIST), P.O. Box 54224, Abu Dhabi (United Arab Emirates); Younes, Hammad [Institute Centre for Energy (iEnergy), Mechanical and Materials Engineering Department, Masdar Institute of Science and Technology (MIST), P.O. Box 54224, Abu Dhabi (United Arab Emirates); Ni, George [Department of Mechanical Engineering, Massachusetts Institute of Technology, 77 Massachusetts Ave, Cambridge, MA 02139 (United States); Zhang, TieJun [Institute Centre for Energy (iEnergy), Mechanical and Materials Engineering Department, Masdar Institute of Science and Technology (MIST), P.O. Box 54224, Abu Dhabi (United Arab Emirates); Al Ghaferi, Amal, E-mail: aalghaferi@masdar.ac.ae [Institute Centre for Energy (iEnergy), Mechanical and Materials Engineering Department, Masdar Institute of Science and Technology (MIST), P.O. Box 54224, Abu Dhabi (United Arab Emirates)

2016-05-15

Highlights: • Controlling metallicity and vertical alignment of CNT forest by changing hydrogen catalyst annealing time and growth pressure. • Verifying metallicity using Raman spectroscopy of top CNT layer. • Optical characterization of CNT forest using UV–vis–NIR spectrophotometer. - Abstract: Catalyst annealing time and growth pressure play a crucial role in the chiral selective and high-efficiency growth of single-walled carbon nanotubes (SWCNTs) during low pressure chemical vapor deposition (LPCVD). We achieved a high growth rates for SWCNTs and a change the chiral distribution towards metallic (n, m) increasing the catalyst annealing time in hydrogen. A strong correlation is revealed between the catalyst annealing time at lower growth pressures and the shape of the G band, which indicates the metallic or semiconducting nature of the SWCNT and predict the chirality distribution. Under a 15 min annealing time and 10 mbar of growth pressure, the bottom of the G band is broadened with a sharp G{sup −} peak, and the G-band exhibited asymmetrical Breit–Wigner–Fano (BWF) shape. In addition, the growth of SWCNTs with smaller diameters and rich in metallic character is confirmed by the shift of the G-band to a smaller Raman frequency. Homogeneity and vertical alignment of as-grown SWCNT arrays are optically studied using UV/vis/NIR Spectrophotometer. Wavelength-independent and low reflectance resulted from the growth of uniform arrays of SWCNTs. Because of their tunable electronic and optical properties, selective growth of SWCNTs promises great application potential, particularly in electronics and solar industries.

Observation of high Tc one dimensional superconductivity in 4 angstrom carbon nanotube arrays

KAUST Repository

Zhang, Bing; Liu, Yang; Chen, Qihong; Lai, Zhiping; Sheng, Ping

2017-01-01

The only known approach to fabricate large, uniform arrays of 4-Å single wall carbon nanotubes (SWNTs) is by using zeolite crystals as the template, in which the nanotubes are formed by chemical vapor deposition inside the linear channels of the AlPO-5 (AFI for short) zeolite. However, up to now the pore filling factor has been very low, as evidenced by the weight percentage of carbon in thermal gravimetric analysis (TGA) measurements. In this work, we show that by using a new, micro-platelet AFI crystals as the template, combined with the use of a new CVD process, we can increase the TGA result to 22.5wt%, which translates to a pore filling factor of 91%. We have observed one dimensional (1D) superconductivity in such samples. The temperature dependence of resistance shows a smooth decreasing trend below 60 K, and the differential resistance displays a gap that disappears above the 1D superconducting initiation temperature. The observed behaviour is shown to agree very well with the theoretical predictions of 1D superconductivity.

Observation of high Tc one dimensional superconductivity in 4 angstrom carbon nanotube arrays

KAUST Repository

Zhang, Bing

2017-02-14

The only known approach to fabricate large, uniform arrays of 4-Å single wall carbon nanotubes (SWNTs) is by using zeolite crystals as the template, in which the nanotubes are formed by chemical vapor deposition inside the linear channels of the AlPO-5 (AFI for short) zeolite. However, up to now the pore filling factor has been very low, as evidenced by the weight percentage of carbon in thermal gravimetric analysis (TGA) measurements. In this work, we show that by using a new, micro-platelet AFI crystals as the template, combined with the use of a new CVD process, we can increase the TGA result to 22.5wt%, which translates to a pore filling factor of 91%. We have observed one dimensional (1D) superconductivity in such samples. The temperature dependence of resistance shows a smooth decreasing trend below 60 K, and the differential resistance displays a gap that disappears above the 1D superconducting initiation temperature. The observed behaviour is shown to agree very well with the theoretical predictions of 1D superconductivity.

Synthesis and enhanced photoelectrocatalytic activity of p–n junction Co3O4/TiO2 nanotube arrays

International Nuclear Information System (INIS)

Dai Gaopeng; Liu Suqin; Liang Ying; Luo Tianxiong

2013-01-01

Highlights: ► Co 3 O 4 /TiO 2 nanotube arrays (NTs) were prepared by an impregnating–deposition–decompostion method treatment. ► Co 3 O 4 /TiO 2 NTs exhibit high photoelectrocatalytic (PEC) activity. ► The high PEC activity was attribute to the formation of p–n junction between Co 3 O 4 and TiO 2 . - Abstract: Co 3 O 4 /TiO 2 nanotube arrays (NTs) were prepared by depositing Co 3 O 4 nanoparticles (NPs) on the tube wall of the self-organized TiO 2 NTs using an impregnating–deposition–decompostion method. The prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and UV–vis absorption spectroscopy. The photoelectrocatalytic (PEC) activity is evaluated by degradation of methyl orange (MO) aqueous solution. The prepared Co 3 O 4 /TiO 2 NTs exhibit much higher PEC activity than TiO 2 NTs due to the p–n junction formed between Co 3 O 4 and TiO 2 .

ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays

Science.gov (United States)

Meško, Marcel; Ou, Qiongrong; Matsuda, Takafumi; Ishikawa, Tomokazu; Veis, Martin; Antoš, Roman; Ogino, Akihisa; Nagatsu, Masaaki

2009-06-01

We report on ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays. We observed a significant reduction of the internal multiple light scattering phenomena, which are characteristic for ZnO micropowders. The microsized grains of the commercially available ZnO:Zn (P 15) were reduced to the nanometre scale by pulsed laser ablation at an oxygen ambient pressure of 10 kPa. Our investigations show no crystalline change and no shift of the broad green emission peak at 500 nm for the ZnO nanopowder. For the application in field emission displays, we demonstrate the possibility of achieving cathodoluminescence with a fine pitch size of 100 µm of the patterned pixels without requiring additional electron beam focusing and without a black matrix. Moreover, the presented results show the feasibility of employing ZnO nanopowder as a detection material for the phosphorus screen method, which is able to localize emission sites of carbon nanotube films and arrays with an accuracy comparable to scanning anode field emission microscopy.

ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays

International Nuclear Information System (INIS)

Mesko, Marcel; Ou Qiongrong; Matsuda, Takafumi; Ishikawa, Tomokazu; Ogino, Akihisa; Nagatsu, Masaaki; Veis, Martin; Antos, Roman

2009-01-01

We report on ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays. We observed a significant reduction of the internal multiple light scattering phenomena, which are characteristic for ZnO micropowders. The microsized grains of the commercially available ZnO:Zn (P 15) were reduced to the nanometre scale by pulsed laser ablation at an oxygen ambient pressure of 10 kPa. Our investigations show no crystalline change and no shift of the broad green emission peak at 500 nm for the ZnO nanopowder. For the application in field emission displays, we demonstrate the possibility of achieving cathodoluminescence with a fine pitch size of 100 μm of the patterned pixels without requiring additional electron beam focusing and without a black matrix. Moreover, the presented results show the feasibility of employing ZnO nanopowder as a detection material for the phosphorus screen method, which is able to localize emission sites of carbon nanotube films and arrays with an accuracy comparable to scanning anode field emission microscopy.

Ag2S/CdS/TiO2 Nanotube Array Films with High Photocurrent Density by Spotting Sample Method.

Science.gov (United States)

Sun, Hong; Zhao, Peini; Zhang, Fanjun; Liu, Yuliang; Hao, Jingcheng

2015-12-01

Ag2S/CdS/TiO2 hybrid nanotube array films (Ag2S/CdS/TNTs) were prepared by selectively depositing a narrow-gap semiconductor-Ag2S (0.9 eV) quantum dots (QDs)-in the local domain of the CdS/TiO2 nanotube array films by spotting sample method (SSM). The improvement of sunlight absorption ability and photocurrent density of titanium dioxide (TiO2) nanotube array films (TNTs) which were obtained by anodic oxidation method was realized because of modifying semiconductor QDs. The CdS/TNTs, Ag2S/TNTs, and Ag2S/CdS/TNTs fabricated by uniformly depositing the QDs into the TNTs via the successive ionic layer adsorption and reaction (SILAR) method were synthesized, respectively. The X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectrum (XPS) results demonstrated that the Ag2S/CdS/TNTs prepared by SSM and other films were successfully prepared. In comparison with the four films of TNTs, CdS/TNTs, Ag2S/TNTs, and Ag2S/CdS/TNTs by SILAR, the Ag2S/CdS/TNTs prepared by SSM showed much better absorption capability and the highest photocurrent density in UV-vis range (320~800 nm). The cycles of local deposition have great influence on their photoelectric properties. The photocurrent density of Ag2S/CdS/TNTs by SSM with optimum deposition cycles of 6 was about 37 times that of TNTs without modification, demonstrating their great prospective applications in solar energy utilization fields.

Aligned carbon nanotube array functionalization for enhanced atomic layer deposition of platinum electrocatalysts

Energy Technology Data Exchange (ETDEWEB)

Dameron, Arrelaine A., E-mail: arrelaine.dameron@nrel.gov [National Renewable Energy Laboratory, 1617 Cole Blvd Golden, Golden, CO 80401 (United States); Pylypenko, Svitlana; Bult, Justin B.; Neyerlin, K.C.; Engtrakul, Chaiwat; Bochert, Christopher; Leong, G. Jeremy; Frisco, Sarah L.; Simpson, Lin; Dinh, Huyen N.; Pivovar, Bryan [National Renewable Energy Laboratory, 1617 Cole Blvd Golden, Golden, CO 80401 (United States)

2012-04-15

Uniform metal deposition onto high surface area supports is a key challenge of developing successful efficient catalyst materials. Atomic layer deposition (ALD) circumvents permeation difficulties, but relies on gas-surface reactions to initiate growth. Our work demonstrates that modified surfaces within vertically aligned carbon nanotube (CNT) arrays, from plasma and molecular precursor treatments, can lead to improved catalyst deposition. Gas phase functionalization influences the number of ALD nucleation sites and the onset of ALD growth and, in turn, affects the uniformity of the coating along the length of the CNTs within the aligned arrays. The induced chemical changes for each functionalization route are identified by X-ray photoelectron and Raman spectroscopies. The most effective functionalization routes increase the prevalence of oxygen moieties at defect sites on the carbon surfaces. The striking effects of the functionalization are demonstrated with ALD Pt growth as a function of surface treatment and ALD cycles examined by electron microscopy of the arrays and the individual CNTs. Finally, we demonstrate applicability of these materials as fuel cell electrocatalysts and show that surface functionalization affects their performance towards oxygen reduction reaction.

Tin

Science.gov (United States)

Kamilli, Robert J.; Kimball, Bryn E.; Carlin, James F.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

2017-12-19

Tin (Sn) is one of the first metals to be used by humans. Almost without exception, tin is used as an alloy. Because of its hardening effect on copper, tin was used in bronze implements as early as 3500 B.C. The major uses of tin today are for cans and containers, construction materials, transportation materials, and solder. The predominant ore mineral of tin, by far, is cassiterite (SnO2).In 2015, the world’s total estimated mine production of tin was 289,000 metric tons of contained tin. Total world reserves at the end of 2016 were estimated to be 4,700,000 metric tons. China held about 24 percent of the world’s tin reserves and accounted for 38 percent of the world’s 2015 production of tin.The proportion of scrap used in tin production is between 10 and 25 percent. Unlike many metals, tin recycling is relatively efficient, and the fraction of tin in discarded products that get recycled is greater than 50 percent.Only about 20 percent of the world’s identified tin resources occur as primary hydrothermal hard-rock veins, or lodes. These lodes contain predominantly high-temperature minerals and almost invariably occur in close association with silicic, peraluminous granites. About 80 percent of the world’s identified tin resources occur as unconsolidated secondary or placer deposits in riverbeds and valleys or on the sea floor. The largest concentration of both onshore and offshore placers is in the extensive tin belt of Southeast Asia, which stretches from China in the north, through Thailand, Burma (also referred to as Myanmar), and Malaysia, to the islands of Indonesia in the south. Furthermore, tin placers are almost always found closely allied to the granites from which they originate. Other countries with significant tin resources are Australia, Bolivia, and Brazil.Most hydrothermal tin deposits belong to what can be thought of as a superclass of porphyry-greisen deposits. The hydrothermal tin deposits are all characterized by a close spatial

Optical properties of ordered vertical arrays of multi-walled carbon nanotubes from FDTD simulations.

Science.gov (United States)

Bao, Hua; Ruan, Xiulin; Fisher, Timothy S

2010-03-15

A finite-difference time-domain (FDTD) method is used to model thermal radiative properties of vertical arrays of multi-walled carbon nanotubes (MWCNT). Individual CNTs are treated as solid circular cylinders with an effective dielectric tensor. Consistent with experiments, the results confirm that CNT arrays are highly absorptive. Compared with the commonly used Maxwell-Garnett theory, the FDTD calculations generally predict larger reflectance and absorbance, and smaller transmittance, which are attributed to the diffraction and scattering within the cylinder array structure. The effects of volume fraction, tube length, tube distance, and incident angle on radiative properties are investigated systematically. Low volume fraction and long tubes are more favorable to achieve low reflectance and high absorbance. For a fixed volume fraction and finite tube length, larger periodicity results in larger reflectance and absorbance. The angular dependence studies reveal an optimum incident angle at which the reflectance can be minimized. The results also suggest that an even darker material could be achieved by using CNTs with good alignment on the top surface.

Fabrication, Modification, and Emerging Applications of TiO2 Nanotube Arrays by Electrochemical Synthesis: A Review

Directory of Open Access Journals (Sweden)

Jian-Ying Huang

2013-01-01

Full Text Available Titania nanotube arrays (TNAs as a hot nanomaterial have a unique highly ordered array structure and good mechanical and chemical stability, as well as excellent anticorrosion, biocompatible, and photocatalytic performance. It has been fabricated by a facile electrochemical anodization in electrolytes containing small amounts of fluoric ions. In combination with our research work, we review the recent progress of the new research achievements of TNAs on the preparation processes, forming mechanism, and modification. In addition, we will review the potential and significant applications in the photocatalytic degradation of pollutants, solar cells, water splitting, and other aspects. Finally, the existing problems and further prospects of this renascent and rapidly developing field are also briefly addressed and discussed.

Aligned Carbon Nanotube Arrays Bonded to Solid Graphite Substrates: Thermal Analysis for Future Device Cooling Applications

Directory of Open Access Journals (Sweden)

Betty T. Quinton

2018-05-01

Full Text Available Carbon nanotubes (CNTs are known for high thermal conductivity and have potential use as nano-radiators or heat exchangers. This paper focuses on the thermal performance of carpet-like arrays of vertically aligned CNTs on solid graphite substrates with the idea of investigating their behavior as a function of carpet dimensions and predicting their performance as thermal interface material (TIM for electronic device cooling. Vertically aligned CNTs were grown on highly oriented pyrolytic graphite (HOPG substrate, which creates a robust and durable all-carbon hierarchical structure. The multi-layer thermal analysis approach using Netzsch laser flash analysis system was used to evaluate their performance as a function of carpet height, from which their thermal properties can be determined. It was seen that the thermal resistance of the CNT array varies linearly with CNT carpet height, providing a unique way of decoupling the properties of the CNT carpet from its interface. This data was used to estimate the thermal conductivity of individual multi-walled nanotube strands in this carpet, which was about 35 W/m-K. The influence of CNT carpet parameters (aerial density, diameter, and length on thermal resistance of the CNT carpet and its potential advantages and limitations as an integrated TIM are discussed.

Enhanced graphitization of c-CVD grown multi-wall carbon nanotube arrays assisted by removal of encapsulated iron-based phases under thermal treatment in argon

International Nuclear Information System (INIS)

Boncel, Slawomir; Koziol, Krzysztof K.K.

2014-01-01

Graphical abstract: - Highlights: • Annealing of the c-CVD MWCNT arrays toward complete removal of iron nanoparticles. • The ICP-AES protocol established for quantitative analysis of Fe-content in MWCNTs. • The vertical alignment from the as-grown MWCNT arrays found intact after annealing. • A route to decrease number of defects/imperfections in the MWCNT graphene walls. • A foundation for commercial purification of c-CVD derived MWCNTs. - Abstract: The effect of annealing on multi-walled carbon nanotube (MWCNT) arrays grown via catalytic Chemical Vapour Deposition (c-CVD) was studied. The treatment enabled to decrease number of defects/imperfections in the graphene walls of MWCNTs’, which was reflected in Raman spectroscopy by reduction of the I D /I G ratio by 27%. Moreover, the vertical alignment from the as-synthesized nanotube arrays was found intact after annealing. Not only graphitization of the nanotube walls occurred under annealing, but the amount of metal iron-based catalyst residues (interfering with numerous physicochemical properties, and hence applications of MWCNTs) was reduced from 9.00 wt.% (for pristine MWCNTs) to 0.02 wt.% as detected by Inductively Coupled Plasma Atomic Emission Spectroscopy (ICP-AES). This value, established by a new analytical protocol, is the lowest recorded by now for purified c-CVD MWCNTs and, due to operating under atmospheric pressure, medium temperature regime (as for annealing processes), reasonable time-scale and metal residue non-specificity, it could lay the foundation for commercial purification of c-CVD derived MWCNTs

Synthesis and magnetotransport studies of CrO2 films grown on TiO2 nanotube arrays by chemical vapor deposition

Science.gov (United States)

Wang, Xiaoling; Zhang, Caiping; Wang, Lu; Lin, Tao; Wen, Gehui

2018-04-01

The CrO2 films have been prepared on the TiO2 nanotube array template via atmospheric pressure chemical vapor deposition method. And the growth procedure was studied. In the beginning of the deposition process, the CrO2 grows on the cross section of the TiO2 nanotubes wall, forms a nanonet-like layer. And the grain size of CrO2 is very small. With the increase of the deposition time, the grain size of CrO2 also increases, and the nanonet-like layer changes into porous film. With the further increase of the deposition time, all the nanotubes are covered by CrO2 grains and the surface structure becomes polycrystalline film. The average grain size on the surface of the CrO2 films deposited for 1 h, 2 h and 5 h is about 190 nm, 300 nm and 470 nm. The X-ray diffraction pattern reveals that the rutile CrO2 film has been synthesized on the TiO2 nanotube array template. The CrO2 films show large magnetoresistance (MR) at low temperature, which should originate from spin-dependent tunneling through grain boundaries between CrO2 grains. And the tunneling mechanism of the CrO2 films can be well described by the fluctuation-induced tunneling (FIT) model. The CrO2 film deposited for 2 h shows insulator behavior from 5 k to 300 K, but the CrO2 film deposited for 5 h shows insulator-metal transition around 140 K. The reason is briefly discussed.

Nano-engineering of three-dimensional core/shell nanotube arrays for high performance supercapacitors

Science.gov (United States)

Grote, Fabian; Wen, Liaoyong; Lei, Yong

2014-06-01

Large-scale arrays of core/shell nanostructures are highly desirable to enhance the performance of supercapacitors. Here we demonstrate an innovative template-based fabrication technique with high structural controllability, which is capable of synthesizing well-ordered three-dimensional arrays of SnO2/MnO2 core/shell nanotubes for electrochemical energy storage in supercapacitor applications. The SnO2 core is fabricated by atomic layer deposition and provides a highly electrical conductive matrix. Subsequently a thin MnO2 shell is coated by electrochemical deposition onto the SnO2 core, which guarantees a short ion diffusion length within the shell. The core/shell structure shows an excellent electrochemical performance with a high specific capacitance of 910 F g-1 at 1 A g-1 and a good rate capability of remaining 217 F g-1 at 50 A g-1. These results shall pave the way to realize aqueous based asymmetric supercapacitors with high specific power and high specific energy.

Far infrared thermal detectors for laser radiometry using a carbon nanotube array

Energy Technology Data Exchange (ETDEWEB)

Lehman, John H.; Lee, Bob; Grossman, Erich N.

2011-07-20

We present a description of a 1.5 mm long, vertically aligned carbon nanotube array (VANTA) on a thermopile and separately on a pyroelectric detector. Three VANTA samples, having average lengths of 40 {mu}m, 150 {mu}m, and 1.5 mm were evaluated with respect to reflectance at a laser wavelength of 394 {mu}m(760 GHz), and we found that the reflectance decreases substantially with increasing tube length, ranging from 0.38 to 0.23 to 0.01, respectively. The responsivity of the thermopile by electrical heating (98.4 mA/W) was equal to that by optical heating (98.0 mA/W) within the uncertainty of the measurement. We analyzed the frequency response and temporal response and found a thermal decay period of 500 ms, which is consistent with the specific heat of comparable VANTAs in the literature. The extremely low (0.01) reflectance of the 1.5 mm VANTAs and the fact that the array is readily transferable to the detector's surface is, to our knowledge, unprecedented.

Rate-independent dissipation and loading direction effects in compressed carbon nanotube arrays

International Nuclear Information System (INIS)

Raney, J R; Fraternali, F; Daraio, C

2013-01-01

Arrays of nominally-aligned carbon nanotubes (CNTs) under compression deform locally via buckling, exhibit a foam-like, dissipative response, and can often recover most of their original height. We synthesize millimeter-scale CNT arrays and report the results of compression experiments at different strain rates, from 10 −4 to 10 −1 s −1 , and for multiple compressive cycles to different strains. We observe that the stress–strain response proceeds independently of the strain rate for all tests, but that it is highly dependent on loading history. Additionally, we examine the effect of loading direction on the mechanical response of the system. The mechanical behavior is modeled using a multiscale series of bistable springs. This model captures the rate independence of the constitutive response, the local deformation, and the history-dependent effects. We develop here a macroscopic formulation of the model to represent a continuum limit of the mesoscale elements developed previously. Utilizing the model and our experimental observations we discuss various possible physical mechanisms contributing to the system’s dissipative response. (paper)

Design of Pd/PANI/Pd sandwich-structured nanotube array catalysts with special shape effects and synergistic effects for ethanol electrooxidation.

Science.gov (United States)

Wang, An-Liang; Xu, Han; Feng, Jin-Xian; Ding, Liang-Xin; Tong, Ye-Xiang; Li, Gao-Ren

2013-07-24

Low cost, high activity, and long-term durability are the main requirements for commercializing fuel cell electrocatalysts. Despite tremendous efforts, developing non-Pt anode electrocatalysts with high activity and long-term durability at low cost remains a significant technical challenge. Here we report a new type of hybrid Pd/PANI/Pd sandwich-structured nanotube array (SNTA) to exploit shape effects and synergistic effects of Pd-PANI composites for the oxidation of small organic molecules for direct alcohol fuel cells. These synthesized Pd/PANI/Pd SNTAs exhibit significantly improved electrocatalytic activity and durability compared with Pd NTAs and commercial Pd/C catalysts. The unique SNTAs provide fast transport and short diffusion paths for electroactive species and high utilization rate of catalysts. Besides the merits of nanotube arrays, the improved electrocatalytic activity and durability are especially attributed to the special Pd/PANI/Pd sandwich-like nanostructures, which results in electron delocalization between Pd d orbitals and PANI π-conjugated ligands and in electron transfer from Pd to PANI.

Thin randomly aligned hierarchical carbon nanotube arrays as ultrablack metamaterials

Science.gov (United States)

De Nicola, Francesco; Hines, Peter; De Crescenzi, Maurizio; Motta, Nunzio

2017-07-01

Ultrablack metamaterials are artificial materials able to harvest all the incident light regardless of wavelength, angle, or polarization. Here, we show the ultrablack properties of randomly aligned hierarchical carbon nanotube arrays with thicknesses below 200 nm. The thin coatings are realized by solution processing and dry-transfer deposition on different substrates. The hierarchical surface morphology of the coatings is biomimetic and provides a large effective area that improves the film optical absorption. Also, such a morphology is responsible for the moth-eye effect, which leads to the omnidirectional and polarization-independent suppression of optical reflection. The films exhibit an emissivity up to 99.36% typical of an ideal black body, resulting in the thinnest ultrablack metamaterial ever reported. Such a material may be exploited for thermal, optical, and optoelectronic devices such as heat sinks, optical shields, solar cells, light and thermal sensors, and light-emitting diodes.

Effects of interfaces on nano-friction of vertically aligned multi-walled carbon nanotube arrays

International Nuclear Information System (INIS)

Lou, J.; Kim, K.-S.

2008-01-01

Sliding friction properties of vertically aligned multi-walled carbon nanotube (VAMWNT) arrays have been investigated in current study in a quantitative manner. The VAMWNT arrays have been fabricated on an anodic aluminum oxide template by chemical vapor deposition at 650 deg. C. Friction force was measured in air by a modified atomic force microscopy (AFM) cantilever-bead assembly with 15 μm diameter borosilicate sphere attached to the end of the regular AFM cantilever. Quantitative measurements were achieved by using a novel in situ calibration methods recently developed based on diamagnetic levitation [Q. Li, K.-S. Kim, A. Rydberg, Rev. Sci. Instrum. 77 (2006) 065105-1-13]. The effects of different interfaces were studied using both cantilever-bead assembly coated with and without Al thin layer coatings. A reverse stick-slip behavior was observed in the current system as compared to the normal stick-slip behavior found in the literature

Carbon Nanotube Arrays for Intracellular Delivery and Biological Applications

Science.gov (United States)

Golshadi, Masoud

Introducing nucleic acids into mammalian cells is a crucial step to elucidate biochemical pathways, modify gene expression in immortalized cells, primary cells, and stem cells, and intoduces new approaches for clinical diagnostics and therapeutics. Current gene transfer technologies, including lipofection, electroporation, and viral delivery, have enabled break-through advances in basic and translational science to enable derivation and programming of embryonic stem cells, advanced gene editing using CRISPR (Clustered regularly interspaced short palindromic repeats), and development of targeted anti-tumor therapy using chimeric antigen receptors in T-cells (CAR-T). Despite these successes, current transfection technologies are time consuming and limited by the inefficient introduction of test molecules into large populations of target cells, and the cytotoxicity of the techniques. Moreover, many cell types cannot be consistently transfected by lipofection or electroporation (stem cells, T-cells) and viral delivery has limitations to the size of experimental DNA that can be packaged. In this dissertation, a novel coverslip-like platform consisting of an array of aligned hollow carbon nanotubes (CNTs) embedded in a sacrificial template is developed that enhances gene transfer capabilities, including high efficiency, low toxicity, in an expanded range of target cells, with the potential to transfer mixed combinations of protein and nucleic acids. The CNT array devices are fabricated by a scalable template-based manufacturing method using commercially available membranes, eliminating the need for nano-assembly. High efficient transfection has been demonstrated by delivering various cargos (nanoparticles, dye and plasmid DNA) into populations of cells, achieving 85% efficiency of plasmid DNA delivery into immortalized cells. Moreover, the CNT-mediated transfection of stem cells shows 3 times higher efficiency compared to current lipofection methods. Evaluating the cell

Electrochemical biosensing based on polypyrrole/titania nanotube hybrid

Energy Technology Data Exchange (ETDEWEB)

Xie, Yibing, E-mail: ybxie@seu.edu.cn; Zhao, Ye

2013-12-01

The glucose oxidase (GOD) modified polypyrrole/titania nanotube enzyme electrode is fabricated for electrochemical biosensing application. The titania nanotube array is grown directly on a titanium substrate through an anodic oxidation process. A thin film of polypyrrole is coated onto titania nanotube array to form polypyrrole/titania nanotube hybrid through a normal pulse voltammetry process. GOD-polypyrrole/titania nanotube enzyme electrode is prepared by the covalent immobilization of GOD onto polypyrrole/titania nanotube hybrid via the cross-linker of glutaraldehyde. The morphology and microstructure of nanotube electrodes are characterized by field emission scanning electron microscopy and Fourier transform infrared analysis. The biosensing properties of this nanotube enzyme electrode have been investigated by means of cyclic voltammetry and chronoamperometry. The hydrophilic polypyrrole/titania nanotube hybrid provides highly accessible nanochannels for GOD encapsulation, presenting good enzymatic affinity. As-formed GOD-polypyrrole/titania nanotube enzyme electrode well conducts bioelectrocatalytic oxidation of glucose, exhibiting a good biosensing performance with a high sensitivity, low detection limit and wide linear detection range. - Graphical abstract: The schematic diagram presents the fabrication of glucose oxidase modified polypyrrole/titania (GOD-PPy/TiO{sub 2}) nanotube enzyme electrode for biosensing application. - Highlights: • Hydrophilic polypyrrole/titania nanotube hybrid is well used as biosensing substrate. • Polypyrrole promotes GOD immobilization on titania nanotubes via glutaraldehyde. • GOD-polypyrrole/titania enzyme electrode shows good bioelectrocatalytic reactivity.

Electrochemical biosensing based on polypyrrole/titania nanotube hybrid

International Nuclear Information System (INIS)

Xie, Yibing; Zhao, Ye

2013-01-01

The glucose oxidase (GOD) modified polypyrrole/titania nanotube enzyme electrode is fabricated for electrochemical biosensing application. The titania nanotube array is grown directly on a titanium substrate through an anodic oxidation process. A thin film of polypyrrole is coated onto titania nanotube array to form polypyrrole/titania nanotube hybrid through a normal pulse voltammetry process. GOD-polypyrrole/titania nanotube enzyme electrode is prepared by the covalent immobilization of GOD onto polypyrrole/titania nanotube hybrid via the cross-linker of glutaraldehyde. The morphology and microstructure of nanotube electrodes are characterized by field emission scanning electron microscopy and Fourier transform infrared analysis. The biosensing properties of this nanotube enzyme electrode have been investigated by means of cyclic voltammetry and chronoamperometry. The hydrophilic polypyrrole/titania nanotube hybrid provides highly accessible nanochannels for GOD encapsulation, presenting good enzymatic affinity. As-formed GOD-polypyrrole/titania nanotube enzyme electrode well conducts bioelectrocatalytic oxidation of glucose, exhibiting a good biosensing performance with a high sensitivity, low detection limit and wide linear detection range. - Graphical abstract: The schematic diagram presents the fabrication of glucose oxidase modified polypyrrole/titania (GOD-PPy/TiO 2 ) nanotube enzyme electrode for biosensing application. - Highlights: • Hydrophilic polypyrrole/titania nanotube hybrid is well used as biosensing substrate. • Polypyrrole promotes GOD immobilization on titania nanotubes via glutaraldehyde. • GOD-polypyrrole/titania enzyme electrode shows good bioelectrocatalytic reactivity

Electrophoretic deposition and field emission properties of patterned carbon nanotubes

International Nuclear Information System (INIS)

Zhao Haifeng; Song Hang; Li Zhiming; Yuan Guang; Jin Yixin

2005-01-01

Patterned carbon nanotubes on silicon substrates were obtained using electrophoretic method. The carbon nanotubes migrated towards the patterned silicon electrode in the electrophoresis suspension under the applied voltage. The carbon nanotubes arrays adhered well on the silicon substrates. The surface images of carbon nanotubes were observed by scanning electron microscopy. The field emission properties of the patterned carbon nanotubes were tested in a diode structure under a vacuum pressure below 5 x 10 -4 Pa. The measured emission area was about 1.0 mm 2 . The emission current density up to 30 mA/cm 2 at an electric field of 8 V/μm has been obtained. The deposition of patterned carbon nanotubes by electrophoresis is an alternative method to prepare field emission arrays

Enhanced graphitization of c-CVD grown multi-wall carbon nanotube arrays assisted by removal of encapsulated iron-based phases under thermal treatment in argon

Energy Technology Data Exchange (ETDEWEB)

Boncel, Slawomir, E-mail: slawomir.boncel@polsl.pl [Department of Organic Chemistry, Biochemistry and Biotechnology, Silesian University of Technology, Krzywoustego 4, 44-100 Gliwice (Poland); Koziol, Krzysztof K.K., E-mail: kk292@cam.ac.uk [Department of Materials Science and Metallurgy, University of Cambridge, 27 Charles Babbage Road, CB3 0FS Cambridge (United Kingdom)

2014-05-01

Graphical abstract: - Highlights: • Annealing of the c-CVD MWCNT arrays toward complete removal of iron nanoparticles. • The ICP-AES protocol established for quantitative analysis of Fe-content in MWCNTs. • The vertical alignment from the as-grown MWCNT arrays found intact after annealing. • A route to decrease number of defects/imperfections in the MWCNT graphene walls. • A foundation for commercial purification of c-CVD derived MWCNTs. - Abstract: The effect of annealing on multi-walled carbon nanotube (MWCNT) arrays grown via catalytic Chemical Vapour Deposition (c-CVD) was studied. The treatment enabled to decrease number of defects/imperfections in the graphene walls of MWCNTs’, which was reflected in Raman spectroscopy by reduction of the I{sub D}/I{sub G} ratio by 27%. Moreover, the vertical alignment from the as-synthesized nanotube arrays was found intact after annealing. Not only graphitization of the nanotube walls occurred under annealing, but the amount of metal iron-based catalyst residues (interfering with numerous physicochemical properties, and hence applications of MWCNTs) was reduced from 9.00 wt.% (for pristine MWCNTs) to 0.02 wt.% as detected by Inductively Coupled Plasma Atomic Emission Spectroscopy (ICP-AES). This value, established by a new analytical protocol, is the lowest recorded by now for purified c-CVD MWCNTs and, due to operating under atmospheric pressure, medium temperature regime (as for annealing processes), reasonable time-scale and metal residue non-specificity, it could lay the foundation for commercial purification of c-CVD derived MWCNTs.

SERS activity of Au nanoparticles coated on an array of carbon nanotube nested into silicon nanoporous pillar

International Nuclear Information System (INIS)

Jiang Weifen; Zhang Yanfeng; Wang Yusheng; Xu Lei; Li Xinjian

2011-01-01

A novel composite structure, Au nanoparticles coated on a nest-shaped array of carbon nanotube nested into a silicon nanoporous pillar array (Au/NACNT/Si-NPA), was fabricated for surface-enhanced Raman scattering (SERS). The morphology of the Au/NACNT/Si-NPA composite structure was characterized with the aid of scanning electron microscopy, X-ray diffraction instrumentation and Transmission electron microscopy. Compared with SERS of rhodamine 6G (R6G) adsorbed on SERS-active Au substrate reported, the SERS signals of R6G adsorbed on these gold nanoparticles were obviously improved. This was attributed to the enlarged specific surface area for adsorption of target molecules brought by the nest-shaped CNTs structure.

Conformal atomic layer deposition of alumina on millimeter tall, vertically-aligned carbon nanotube arrays.

Science.gov (United States)

Stano, Kelly L; Carroll, Murphy; Padbury, Richard; McCord, Marian; Jur, Jesse S; Bradford, Philip D

2014-11-12

Atomic layer deposition (ALD) can be used to coat high aspect ratio and high surface area substrates with conformal and precisely controlled thin films. Vertically aligned arrays of multiwalled carbon nanotubes (MWCNTs) with lengths up to 1.5 mm were conformally coated with alumina from base to tip. The nucleation and growth behaviors of Al2O3 ALD precursors on the MWCNTs were studied as a function of CNT surface chemistry. CNT surfaces were modified through a series of post-treatments including pyrolytic carbon deposition, high temperature thermal annealing, and oxygen plasma functionalization. Conformal coatings were achieved where post-treatments resulted in increased defect density as well as the extent of functionalization, as characterized by X-ray photoelectron spectroscopy and Raman spectroscopy. Using thermogravimetric analysis, it was determined that MWCNTs treated with pyrolytic carbon and plasma functionalization prior to ALD coating were more stable to thermal oxidation than pristine ALD coated samples. Functionalized and ALD coated arrays had a compressive modulus more than two times higher than a pristine array coated for the same number of cycles. Cross-sectional energy dispersive X-ray spectroscopy confirmed that Al2O3 could be uniformly deposited through the entire thickness of the vertically aligned MWCNT array by manipulating sample orientation and mounting techniques. Following the ALD coating, the MWCNT arrays demonstrated hydrophilic wetting behavior and also exhibited foam-like recovery following compressive strain.

Drug-eluting Ti wires with titania nanotube arrays for bone fixation and reduced bone infection

Science.gov (United States)

Gulati, Karan; Aw, Moom Sinn; Losic, Dusan

2011-10-01

Current bone fixation technology which uses stainless steel wires known as Kirschner wires for fracture fixing often causes infection and reduced skeletal load resulting in implant failure. Creating new wires with drug-eluting properties to locally deliver drugs is an appealing approach to address some of these problems. This study presents the use of titanium [Ti] wires with titania nanotube [TNT] arrays formed with a drug delivery capability to design alternative bone fixation tools for orthopaedic applications. A titania layer with an array of nanotube structures was synthesised on the surface of a Ti wire by electrochemical anodisation and loaded with antibiotic (gentamicin) used as a model of bone anti-bacterial drug. Successful fabrication of TNT structures with pore diameters of approximately 170 nm and length of 70 μm is demonstrated for the first time in the form of wires. The drug release characteristics of TNT-Ti wires were evaluated, showing a two-phase release, with a burst release (37%) and a slow release with zero-order kinetics over 11 days. These results confirmed our system's ability to be applied as a drug-eluting tool for orthopaedic applications. The established biocompatibility of TNT structures, closer modulus of elasticity to natural bones and possible inclusion of desired drugs, proteins or growth factors make this system a promising alternative to replace conventional bone implants to prevent bone infection and to be used for targeted treatment of bone cancer, osteomyelitis and other orthopaedic diseases.

Effect of gold nanoparticle attached multi-walled carbon nanotube-layered indium tin oxide in monitoring the effect of paracetamol on the release of epinephrine

International Nuclear Information System (INIS)

Goyal, Rajendra N.; Rana, Anoop Raj Singh; Aziz, Md. Abdul; Oyama, Munetaka

2011-01-01

A gold nanoparticle attached multi-walled carbon nanotube-layered indium tin oxide (AuNP/MWNT/ITO) electrode has been used for monitoring the effect of paracetamol (PAR) on the release of epinephrine (EPI) in human urine. The modified electrode shows an excellent electrocatalytic activity for the oxidation of EPI and PAR with acceleration of electron transfer rate as compared to MWNT/ITO and AuNP/ITO. An apparent shift of the oxidative potential towards less positive potential with a marked increase in peak currents is observed in square wave voltammetry at AuNP/MWNT/ITO electrode. The calibration curves for the simultaneous determination of PAR and EPI showed an excellent linear response, ranging from 5.0 x 10 -9 mol L -1 to 80.0 x 10 -9 mol L -1 for both the compounds. The detection limits for the simultaneous determination of PAR and EPI were found to be 46 x 10 -10 mol L -1 and 42 x 10 -10 mol L -1 respectively. The proposed method has been successfully applied for the simultaneous determination of PAR and EPI in human urine. It is observed that gold nanoparticles attached with multi-wall carbon nanotube catalyze the oxidation of EPI and PAR.

Effect of gold nanoparticle attached multi-walled carbon nanotube-layered indium tin oxide in monitoring the effect of paracetamol on the release of epinephrine

Energy Technology Data Exchange (ETDEWEB)

Goyal, Rajendra N., E-mail: rngcyfcy@iitr.ernet.in [Department of Chemistry, Indian Institute of Technology Roorkee, Roorkee 247667 (India); Rana, Anoop Raj Singh [Department of Chemistry, Indian Institute of Technology Roorkee, Roorkee 247667 (India); Aziz, Md. Abdul; Oyama, Munetaka [Department of Materials Chemistry, Graduate School of Engineering, Kyoto University, Nishikyo-ku, Kyoto 615-8520 (Japan)

2011-05-05

A gold nanoparticle attached multi-walled carbon nanotube-layered indium tin oxide (AuNP/MWNT/ITO) electrode has been used for monitoring the effect of paracetamol (PAR) on the release of epinephrine (EPI) in human urine. The modified electrode shows an excellent electrocatalytic activity for the oxidation of EPI and PAR with acceleration of electron transfer rate as compared to MWNT/ITO and AuNP/ITO. An apparent shift of the oxidative potential towards less positive potential with a marked increase in peak currents is observed in square wave voltammetry at AuNP/MWNT/ITO electrode. The calibration curves for the simultaneous determination of PAR and EPI showed an excellent linear response, ranging from 5.0 x 10{sup -9} mol L{sup -1} to 80.0 x 10{sup -9} mol L{sup -1} for both the compounds. The detection limits for the simultaneous determination of PAR and EPI were found to be 46 x 10{sup -10} mol L{sup -1} and 42 x 10{sup -10} mol L{sup -1} respectively. The proposed method has been successfully applied for the simultaneous determination of PAR and EPI in human urine. It is observed that gold nanoparticles attached with multi-wall carbon nanotube catalyze the oxidation of EPI and PAR.

Electrical device fabrication from nanotube formations

Science.gov (United States)

Nicholas, Nolan Walker; Kittrell, W. Carter; Kim, Myung Jong; Schmidt, Howard K.

2013-03-12

A method for forming nanotube electrical devices, arrays of nanotube electrical devices, and device structures and arrays of device structures formed by the methods. Various methods of the present invention allow creation of semiconducting and/or conducting devices from readily grown SWNT carpets rather than requiring the preparation of a patterned growth channel and takes advantage of the self-controlling nature of these carpet heights to ensure a known and controlled channel length for reliable electronic properties as compared to the prior methods.

Field emission from optimized structure of carbon nanotube field emitter array

International Nuclear Information System (INIS)

Chouhan, V.; Noguchi, T.; Kato, S.

2016-01-01

The authors report a detail study on the emission properties of field emitter array (FEA) of micro-circular emitters of multiwall carbon nanotubes (CNTs). The FEAs were fabricated on patterned substrates prepared with an array of circular titanium (Ti) islands on titanium nitride coated tantalum substrates. CNTs were rooted into these Ti islands to prepare an array of circular emitters. The circular emitters were prepared in different diameters and pitches in order to optimize their structure for acquiring a high emission current. The pitch was varied from 0 to 600 μm, while a diameter of circular emitters was kept constant to be 50 μm in order to optimize a pitch. For diameter optimization, a diameter was changed from 50 to 200 μm while keeping a constant edge-to-edge distance of 150 μm between the circular emitters. The FEA with a diameter of 50 μm and a pitch of 120 μm was found to be the best to achieve an emission current of 47 mA corresponding to an effective current density of 30.5 A/cm"2 at 7 V/μm. The excellent emission current was attributed to good quality of CNT rooting into the substrate and optimized FEA structure, which provided a high electric field on a whole circular emitter of 50 μm and the best combination of the strong edge effect and CNT coverage. The experimental results were confirmed with computer simulation.

Field emission from optimized structure of carbon nanotube field emitter array

Energy Technology Data Exchange (ETDEWEB)

Chouhan, V., E-mail: vchouhan@post.kek.jp, E-mail: vijaychouhan84@gmail.com [School of High Energy Accelerator, The Graduate University for Advanced Studies, Tsukuba 305-0801 (Japan); Noguchi, T. [High Energy Accelerator Research Organization (KEK), Tsukuba 305-0801 (Japan); Kato, S. [School of High Energy Accelerator, The Graduate University for Advanced Studies, Tsukuba 305-0801 (Japan); High Energy Accelerator Research Organization (KEK), Tsukuba 305-0801 (Japan)

2016-04-07

The authors report a detail study on the emission properties of field emitter array (FEA) of micro-circular emitters of multiwall carbon nanotubes (CNTs). The FEAs were fabricated on patterned substrates prepared with an array of circular titanium (Ti) islands on titanium nitride coated tantalum substrates. CNTs were rooted into these Ti islands to prepare an array of circular emitters. The circular emitters were prepared in different diameters and pitches in order to optimize their structure for acquiring a high emission current. The pitch was varied from 0 to 600 μm, while a diameter of circular emitters was kept constant to be 50 μm in order to optimize a pitch. For diameter optimization, a diameter was changed from 50 to 200 μm while keeping a constant edge-to-edge distance of 150 μm between the circular emitters. The FEA with a diameter of 50 μm and a pitch of 120 μm was found to be the best to achieve an emission current of 47 mA corresponding to an effective current density of 30.5 A/cm{sup 2} at 7 V/μm. The excellent emission current was attributed to good quality of CNT rooting into the substrate and optimized FEA structure, which provided a high electric field on a whole circular emitter of 50 μm and the best combination of the strong edge effect and CNT coverage. The experimental results were confirmed with computer simulation.

Wafer-Level Patterned and Aligned Polymer Nanowire/Micro- and Nanotube Arrays on any Substrate

KAUST Repository

Morber, Jenny Ruth

2009-05-25

A study was conducted to fabricate wafer-level patterned and aligned polymer nanowire (PNW), micro- and nanotube arrays (PNT), which were created by exposing the polymer material to plasma etching. The approach for producing wafer-level aligned PNWs involved a one-step inductively coupled plasma (ICP) reactive ion etching process. The polymer nanowire array was fabricated in an ICP reactive ion milling chamber with a pressure of 10mTorr. Argon (Ar), O 2, and CF4 gases were released into the chamber as etchants at flow rates of 15 sccm, 10 sccm, and 40 sccm. Inert gasses, such as Ar-form positive ions were incorporated to serve as a physical component to assist in the material degradation process. One power source (400 W) was used to generate dense plasma from the input gases, while another power source applied a voltage of approximately 600V to accelerate the plasma toward the substrate.

Vertically Aligned Carbon Nanotube Arrays as Efficient Supports for Faradaic Capacitive Electrodes

Science.gov (United States)

Oguntoye, Moses; Holleran, Mary-Kate; Roberts, Katherine; Pesika, Noshir

Supercapacitors are notable for their ability to deliver energy at higher power (compared to batteries) and store energy at higher density (compared to capacitors) as well as exhibit a long cycle life. In our efforts to further the development of supercapacitors, our focus is on using vertically aligned carbon nanotubes (VACNT) as supports for faradaic capacitive electrode materials. The objective is to develop electrodes functioning in an inexpensive aqueous environment with small potential windows, that store energy at a higher density than carbon materials alone. We describe the different approaches explored to overcome the challenges of non-uniform deposition, poor wetting and array collapse. Materials that are electrochemically anchored to VACNT supports include NiCo2O4, VOx, Fe2O3 and Co-Mn mixed oxides. In each case, the specific capacitance obtained using the VACNT arrays as supports is significantly more than that obtained by direct deposition onto current collectors or by using VACNT alone. The ease of VACNT growth and the degree of coating control achievable using electrodeposition means there is much potential in exploring them as supports for capacitive electrode materials.

MoSe2 modified TiO2 nanotube arrays with superior photoelectrochemical performance

Science.gov (United States)

Zhang, Yaping; Zhu, Haifeng; Yu, Lianqing; He, Jiandong; Huang, Chengxing

2018-04-01

TiO2 nanotube arrays (TNTs) are first prepared by anodization Ti foils in ethylene glycol electrolyte. Then, MoSe2 deposites electrochemically on TNTs. The as-synthesized MoSe2/TiO2 composite has a much higher photocurrent density of 1.07 mA cm‑2 at 0 V than pure TNTs of 0.38 mA cm‑2, which suggests that the MoSe2/TiO2 composite film has optimum photoelectrocatalysis properties. The electron transport resistances of the MoSe2/TiO2 decreases to half of pure TiO2, at 295.6 ohm/cm2. Both photocurrent-time and Mott-Schottky plots indicate MoSe2 a p-type semiconductor characteristics. MoSe2/TiO2 composite can achieve a maximum 5 orders of magnitude enhancement in carrier density (4.650 × 1027 cm‑3) than that of pure TiO2 arrays. It can be attributed to p-n heterojunction formed between MoSe2 and TiO2, and the composite can be potentially applied in photoelectrochemical, photocatalysis fields.

Nanotubes based neutron generator for calibration of neutrino and dark matter detectors

Science.gov (United States)

Chepurnov, A. S.; Ionidi, V. Y.; Kirsanov, M. A.; Kitsyuk, E. P.; Klenin, A. A.; Kubankin, A. S.; Oleinik, A. N.; Pavlov, A. A.; Shchagin, A. V.

2017-12-01

The compact 2.45 MeV fast neutron generator with a reduced supply voltage for calibration of low-background neutrino and dark matter detectors was tested. The generator is based on an array of carbon nanotubes. Neutron generation is carried out by applying a high voltage in the range of +10 to + 25 kV to a nanotube array, which cause an ionization of deuterium molecules with the following acceleration of ions in the direction of the grounded target covered by a deuterated polyethylene film. The d(d,n)3He nuclear reaction happens as the result of ions collisions with the target. The dependences of the neutron yield as functions of the applied voltage were obtained for two different types of carbon nanotubes array. It is shown that the type of nanotubes array does not influence significantly on the neutron yield.

Preparation of CuInS{sub 2}/TiO{sub 2} nanotube heterojunction arrays electrode and investigation of its photoelectrochemical properties

Energy Technology Data Exchange (ETDEWEB)

Li, Tingting [School of Environmental Science and Technology, State Key Laboratory of Fine Chemical, Key Laboratory of Industrial Ecology and Environmental Engineering of Ministry of Education, Dalian University of Technology, Dalian 116024, Liaoning (China); College of Civil Engineering and Architecture, Liaoning Technical University, Fuxin 123000 (China); Li, Xinyong, E-mail: xyli@dlut.edu.cn [School of Environmental Science and Technology, State Key Laboratory of Fine Chemical, Key Laboratory of Industrial Ecology and Environmental Engineering of Ministry of Education, Dalian University of Technology, Dalian 116024, Liaoning (China); Zhao, Qidong; Teng, Wei [School of Environmental Science and Technology, State Key Laboratory of Fine Chemical, Key Laboratory of Industrial Ecology and Environmental Engineering of Ministry of Education, Dalian University of Technology, Dalian 116024, Liaoning (China)

2014-11-15

Graphical abstract: Schematic illustration of the synthesis steps of CuInS{sub 2}/TiO{sub 2} heterojunction arrays electrode. - Highlights: • CuInS{sub 2}/TiO{sub 2} nanotube heterojunction arrays electrode was successfully fabricated via a modified SILAR method. • Morphology, chemical compositions and the photoelectrochemical properties were studied. • The formed heterojunction structure is demonstrated as n–n type heterojunction. - Abstract: CuInS{sub 2}/TiO{sub 2} nanotube heterojunction arrays electrode was synthesized via a modified successive ionic layer adsorption and reaction (SILAR) method. The morphology, crystalline structure and chemical composition of the composite electrode were characterized with field-emission scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray photoelectron spectra (XPS), respectively. The optical properties were investigated by UV–vis diffusion reflection spectra (DRS) and photoluminescence (PL) spectra as well as the photoelectrochemical measurements. Significantly enhanced photoelectrochemical properties of CuInS{sub 2}/TiO{sub 2} NTs electrode were observed under visible light irradiation, which could be attributed to the high absorption coefficient of CuInS{sub 2} in visible region and the heterostructure formed between CuInS{sub 2} and TiO{sub 2}.

Combination of Polymer Technology and Carbon Nanotube Array for the Development of an Effective Drug Delivery System at Cellular Level

Directory of Open Access Journals (Sweden)

Riggio Cristina

2009-01-01

Full Text Available Abstract In this article, a carbon nanotube (CNT array-based system combined with a polymer thin film is proposed as an effective drug release device directly at cellular level. The polymeric film embedded in the CNT array is described and characterized in terms of release kinetics, while in vitro assays on PC12 cell line have been performed in order to assess the efficiency and functionality of the entrapped agent (neural growth factor, NGF. PC12 cell differentiation, following incubation on the CNT array embedding the alginate delivery film, demonstrated the effectiveness of the proposed solution. The achieved results indicate that polymeric technology could be efficiently embedded in CNT array acting as drug delivery system at cellular level. The implication of this study opens several perspectives in particular in the field of neurointerfaces, combining several functions into a single platform.

Rapid synthesis of tin oxide decorated carbon nanotube nanocomposities as anode materials for lithium-ion batteries

International Nuclear Information System (INIS)

Lin, Jeng-Yu; Chou, Ming-Hung; Kuo, Yi-Chen

2014-01-01

Highlights: • SnO 2 –CNTs nanocomposite was synthesized by microwave-assisted hydrothermal route. • Adding glucose assisted SnO 2 nanoclusters uniformly grow on the surfaces of CNTs. • SnO 2 –CNTs nanocomposite shows improved electrochemical properties. -- Abstract: In this study, the tin oxide decorated carbon nanotubes (SnO 2 –CNTs) nanocomposites have been successfully synthesized using an ultrafast and environmentally friendly microwave-assisted hydrothermal method. According to X-ray diffraction pattern, field emission scanning electron microscopy and transmission electron microscopy, the SnO 2 nanoclusters can directly grow on the surfaces of CNTs with uniform coverage along the longitudinal axis by using glucose as a binding agent. The electrochemical properties of the SnO 2 –CNTs nanocomposite electrode have been further characterized by galvanostatic discharge/charge cycling tests, cyclic voltammetry and electrochemical impedance spectroscopy. Results demonstrate that the SnO 2 –CNTs nanocomposite electrode exhibited a superior reversible discharge capacity, cycling stability and rate capability as an anode material for Li-ion batteries compared to the pristine SnO 2 electrode. Such synergic improvements can be attributed to combining the SnO 2 nanoclusters onto the conductive CNTs matrix by taking advantage of the relatively high specific capacity of SnO 2 nanoclusters and the excellent cycling capability of the CNTs

Controlled Growth of Carbon Nanotubes on Micropatterned Au/Cr Composite Film and Field Emission from Their Arrays

Science.gov (United States)

Kamide, Koichi; Araki, Hisashi; Yoshino, Katsumi

2003-12-01

Carbon nanotube (CNT) arrays with a controlled density are prepared on a micropatterned Au/Cr composite film formed on a quartz glass plate by pyrolysis of Ni-phthalocyanine at 800°C. It is clarified from characteristic X-ray analyses for those samples that a catalytic Ni nanoparticle is not contained within the base of the whisker-like CNT in contrast to that of the bamboo-like CNT, suggesting that the growth process of the present novel CNT is incompatible with that of the bamboo-like CNT. In the Au/Cr composite film, both the Cr atomic content of approximately 30% and the presence of the Ni catalyst devoid of a particle-like shape are important factors for the growth of CNTs. Field emission from the novel CNT arrays exhibits a lower turn-on voltage and a higher current density compared with that from the bamboo-like arrays formed on a quartz plate.

Metal oxide nanorod arrays on monolithic substrates

Energy Technology Data Exchange (ETDEWEB)

Gao, Pu-Xian; Guo, Yanbing; Ren, Zheng

2018-01-02

A metal oxide nanorod array structure according to embodiments disclosed herein includes a monolithic substrate having a surface and multiple channels, an interface layer bonded to the surface of the substrate, and a metal oxide nanorod array coupled to the substrate surface via the interface layer. The metal oxide can include ceria, zinc oxide, tin oxide, alumina, zirconia, cobalt oxide, and gallium oxide. The substrate can include a glass substrate, a plastic substrate, a silicon substrate, a ceramic monolith, and a stainless steel monolith. The ceramic can include cordierite, alumina, tin oxide, and titania. The nanorod array structure can include a perovskite shell, such as a lanthanum-based transition metal oxide, or a metal oxide shell, such as ceria, zinc oxide, tin oxide, alumina, zirconia, cobalt oxide, and gallium oxide, or a coating of metal particles, such as platinum, gold, palladium, rhodium, and ruthenium, over each metal oxide nanorod. Structures can be bonded to the surface of a substrate and resist erosion if exposed to high velocity flow rates.

Impact of the atomic layer deposition precursors diffusion on solid-state carbon nanotube based supercapacitors performances

International Nuclear Information System (INIS)

Fiorentino, Giuseppe; Vollebregt, Sten; Ishihara, Ryoichi; Sarro, Pasqualina M; Tichelaar, F D

2015-01-01

A study on the impact of atomic layer deposition (ALD) precursors diffusion on the performance of solid-state miniaturized nanostructure capacitor array is presented. Three-dimensional nanostructured capacitor array based on double conformal coating of multiwalled carbon nanotubes (MWCNTs) bundles is realized using ALD to deposit Al 2 O 3 as dielectric layer and TiN as high aspect-ratio conformal counter-electrode on 2 μm long MWCNT bundles. The devices have a small footprint (from 100 μm 2 to 2500 μm 2 ) and are realized using an IC wafer-scale manufacturing process with high reproducibility (≤0.3E-12F deviation). To evaluate the enhancement of the electrode surface, the measured capacitance values are compared to a lumped circuital model. The observed discrepancies are explained with a partial coating of the CNT, that determine a limited use of the available electrode surface area. To analyze the CNT coating effectiveness, the ALD precursors diffusions inside the CNT bundle is studied using a Knudsen diffusion mechanism. (paper)

Impact of the atomic layer deposition precursors diffusion on solid-state carbon nanotube based supercapacitors performances

Science.gov (United States)

Fiorentino, Giuseppe; Vollebregt, Sten; Tichelaar, F. D.; Ishihara, Ryoichi; Sarro, Pasqualina M.

2015-02-01

A study on the impact of atomic layer deposition (ALD) precursors diffusion on the performance of solid-state miniaturized nanostructure capacitor array is presented. Three-dimensional nanostructured capacitor array based on double conformal coating of multiwalled carbon nanotubes (MWCNTs) bundles is realized using ALD to deposit Al2O3 as dielectric layer and TiN as high aspect-ratio conformal counter-electrode on 2 μm long MWCNT bundles. The devices have a small footprint (from 100 μm2 to 2500 μm2) and are realized using an IC wafer-scale manufacturing process with high reproducibility (≤0.3E-12F deviation). To evaluate the enhancement of the electrode surface, the measured capacitance values are compared to a lumped circuital model. The observed discrepancies are explained with a partial coating of the CNT, that determine a limited use of the available electrode surface area. To analyze the CNT coating effectiveness, the ALD precursors diffusions inside the CNT bundle is studied using a Knudsen diffusion mechanism.

Investigating the antifungal activity of TiO{sub 2} nanoparticles deposited on branched carbon nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Darbari, S; Abdi, Y; Haghighi, N [Nano-Physics Research Laboratory, Department of Physics, University of Tehran, Tehran (Iran, Islamic Republic of); Haghighi, F [Department of Medical Mycology, School of Medical Sciences, Tarbiat Modares University, Tehran (Iran, Islamic Republic of); Mohajerzadeh, S, E-mail: y.abdi@ut.ac.ir [Thin Film Laboratory, ECE Department, University of Tehran, Tehran (Iran, Islamic Republic of)

2011-06-22

Branched carbon nanotube (CNT) arrays were synthesized by plasma-enhanced chemical vapour deposition on a silicon substrate. Ni was used as the catalyst and played an important role in the realization of branches in vertically aligned nanotubes. TiO{sub 2} nanoparticles on the branched CNTs were produced by atmospheric pressure chemical vapour deposition followed by a 500 {sup 0}C annealing step. Transmission and scanning electron microscopic techniques were used to study the morphology of the TiO{sub 2}/branched CNT structures while x-ray diffraction and Raman spectroscopy were used to verify the characteristics of the prepared nanostructures. Their antifungal effect on Candida albicans biofilms under visible light was investigated and compared with the activity of TiO{sub 2}/CNT arrays and thin films of TiO{sub 2}. The TiO{sub 2}/branched CNTs showed a highly improved photocatalytic antifungal activity in comparison with the TiO{sub 2}/CNTs and TiO{sub 2} film. The excellent visible light-induced photocatalytic antifungal activity of the TiO{sub 2}/branched CNTs was attributed to the generation of electron-hole pairs by visible light excitation with a low recombination rate, in addition to the high surface area provided for the interaction between the cells and the nanostructures. Scanning electron microscopy was used to observe the resulting morphological changes in the cell body of the biofilms existing on the antifungal samples.

Fabrication of uniformly dispersed Ag nanoparticles loaded TiO{sub 2} nanotube arrays for enhancing photoelectrochemical and photocatalytic performances under visible light irradiation

Energy Technology Data Exchange (ETDEWEB)

Yi, Junhui; Zhang, Shengsen; Wang, Hongjuan; Yu, Hao; Peng, Feng, E-mail: cefpeng@scut.edu.cn

2014-12-15

Graphical abstract: Uniformly dispersed Ag nanoparticles (NPs) were successfully loaded on both the outer and inner surface of the TiO{sub 2} nanotube arrays (NTs) through a simple polyol method, which exhibited the enhanced photoelectrochemical and photocatalytic performances under visible-light irradiation due to the more effective separation of photo-generated electron–hole pairs and faster interfacial charge transfer. - Highlights: • Highly dispersed Ag nanoparticles (NPs) are successfully prepared by polyol method. • Ag NPs are uniformly loaded on the surface of the TiO{sub 2} nanotube arrays (NTs). • Ag/TiO{sub 2}-NTs exhibit the enhanced photocatalytic activity under visible-light. • The enhanced photocurrent is explained by electrochemical impedance spectroscopy. - Abstract: Uniformly dispersed Ag nanoparticles (NPs) were successfully loaded on both the outer and inner surface of the TiO{sub 2} nanotube arrays (NTs) through a simple polyol method. The as-prepared Ag/TiO{sub 2}-NTs were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and UV–vis diffusion reflectance spectroscopy. Photoelectrochemical behaviors were investigated via photocurrent response and electrochemical impedance spectroscopy (EIS). Photocatalytic activity of Ag/TiO{sub 2}-NTs was evaluated by degradation of acid orange II under visible light irradiation. The results showed that photocatalytic efficiency of Ag/TiO{sub 2}-NTs is more than 5 times higher than that of pure TiO{sub 2} NTs. Comparing with the electrochemical deposition method, the photocatalytic activity of Ag/TiO{sub 2}-NTs prepared by polyol method has been obviously increased.

Hydrolysis of bis(dimethylamido)tin to tin (II) oxyhydroxide and its selective transformation into tin (II) or tin (IV) oxide

KAUST Repository

Khanderi, Jayaprakash; Shi, Lei; Rothenberger, Alexander

2015-01-01

Sn6O4(OH)4, a hydrolysis product of Sn(NMe2)2, is transformed to tin (II) or tin (IV) oxide by solid and solution phase processing. Tin (II) oxide is formed by heating Sn6O4(OH)4 at ≤200 °C in air or under inert atmosphere. Tin (IV) oxide

Carbon treated self-ordered TiO{sub 2} nanotube arrays with enhanced lithium-ion intercalation performance

Energy Technology Data Exchange (ETDEWEB)

Kim, Hyun Sik [Energy Material Group, Lotte Chemical, 115, Gajeongbuk-ro, Yuseong-gu, Daejeon 305-726 (Korea, Republic of); Yu, Seung-Ho; Sung, Yung-Eun [School of Chemical and Biological Engineering and Research Center for Energy Conversion and Storage, Seoul National University, San 56-1, Sillim-dong, Gwanak-gu, Seoul 151-744 (Korea, Republic of); Kang, Soon Hyung, E-mail: skang@jnu.ac.kr [Department of Chemical Education, Chonnam National University, Gwangju 500-757 (Korea, Republic of)

2014-06-01

Highlights: • C-doped TONT was prepared by anodization, followed by acetylene treatment. • C-doped TONT exhibited the superior cycle performance and electrochemical kinetics. • It was attributed from the enhanced electrical conductivity from carbon doping. - Abstract: Vertically aligned TiO{sub 2} nanotube (TONT) arrays on titanium substrate developed by facile electrochemical anodization in an aqueous solution of 0.5 M Na{sub 2}SO{sub 4}, 0.5 M H{sub 3}PO{sub 4}, 0.2 M sodium citrate, and 0.5 wt% NaF were prepared having a pore diameter and thickness of 100 nm and 1.2 μm, respectively. The undoped (u-doped) TONT arrays possessing an anatase phase were again annealed at 500 °C under a mixed gas flux of nitrogen (N{sub 2}) and acetylene (C{sub 2}H{sub 2}), to induce the enhancement of electrical conductivity. It was designated as carbon-doped (c-doped) TONT arrays. Undoped and c-doped TONT arrays were compared using various characterization tools, including X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), and X-ray photoelectron spectroscopy (XPS). Furthermore, based on several electrochemical tests (galvanostatic charge/discharge tests, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS)), it was observed that c-doped TONT arrays revealed improved charge/discharge capacity, cycle stability, and rate capability, due to the enhanced electrical conductivity of c-doped TONT arrays.

Fabrication and electrical properties of single wall carbon nanotube channel and graphene electrode based transistors arrays

Energy Technology Data Exchange (ETDEWEB)

Seo, M.; Kim, H.; Kim, Y. H.; Yun, H.; McAllister, K.; Lee, S. W., E-mail: leesw@konkuk.ac.kr [Division of Quantum Phases and Devices, School of Physics, Konkuk University, Seoul 143-701 (Korea, Republic of); Na, J.; Kim, G. T. [School of Electrical Engineering, Korea University, Seoul 136-701 (Korea, Republic of); Lee, B. J.; Kim, J. J.; Jeong, G. H. [Department of Nano Applied Engineering, Kangwon National University, Kangwon-do 200-701 (Korea, Republic of); Lee, I.; Kim, K. S. [Department of Physics and Graphene Research Institute, Sejong University, Seoul 143-747 (Korea, Republic of)

2015-07-20

A transistor structure composed of an individual single-walled carbon nanotube (SWNT) channel with a graphene electrode was demonstrated. The integrated arrays of transistor devices were prepared by transferring patterned graphene electrode patterns on top of the aligned SWNT along one direction. Both single and multi layer graphene were used for the electrode materials; typical p-type transistor and Schottky diode behavior were observed, respectively. Based on our fabrication method and device performances, several issues are suggested and discussed to improve the device reliability and finally to realize all carbon based future electronic systems.

Synthesis and Growth Mechanism of Ni Nanotubes and Nanowires

Directory of Open Access Journals (Sweden)

Wang Yiqian

2009-01-01

Full Text Available Abstract Highly ordered Ni nanotube and nanowire arrays were fabricated via electrodeposition. The Ni microstructures and the process of the formation were investigated using conventional and high-resolution transmission electron microscope. Herein, we demonstrated the systematic fabrication of Ni nanotube and nanowire arrays and proposed an original growth mechanism. With the different deposition time, nanotubes or nanowires can be obtained. Tubular nanostructures can be obtained at short time, while nanowires take longer time to form. This formation mechanism is applicable to design and synthesize other metal nanostructures and even compound nanostuctures via template-based electrodeposition.

Near-field radiation between graphene-covered carbon nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Zhang, Richard Z.; Liu, Xianglei; Zhang, Zhuomin M., E-mail: zhuomin.zhang@me.gatech.edu [George W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States)

2015-05-15

It has been shown that at small separation distances, thermal radiation between hyperbolic metamaterials is enhanced over blackbodies. This theoretical study considers near-field radiation when graphene is covered on the surfaces of two semi-infinite vertically aligned carbon nanotube (VACNT) arrays separated by a sub-micron vacuum gap. Doped graphene is found to improve photon tunneling in a broad hyperbolic frequency range, due to the interaction with graphene-graphene surface plasmon polaritons (SPP). In order to elucidate the SPP resonance between graphene on hyperbolic substrates, vacuum-suspended graphene sheets separated by similar gap distances are compared. Increasing the Fermi energy through doping shifts the spectral heat flux peak toward higher frequencies. Although the presence of graphene on VACNT does not offer huge near-field heat flux enhancement over uncovered VACNT, this study identifies conditions (i.e., gap distance and doping level) that best utilize graphene to augment near-field radiation. Through the investigation of spatial Poynting vectors, heavily doped graphene is found to increase penetration depths in hyperbolic modes and the result is sensitive to the frequency regime. This study may have an impact on designing carbon-based vacuum thermophotovoltaics and thermal switches.

Lithium storage study on MoO3-grafted TiO2 nanotube arrays

Directory of Open Access Journals (Sweden)

Tauseef Anwar

2016-03-01

Full Text Available Abstract Titanium dioxide nanotube arrays (TNAs were fabricated via anodic ionization. Porous MoO3 was grafted on TNAs with the help of hydrothermal method. Scanning electron microscopy and X-ray powder diffraction was utilized for the confirmation of one dimensional morphology and phase identification. The porous MoO3 nanoflake-grafted TNAs (MoO3/TNAs electrode was used as anode material in lithium ion battery (LIB and it was found that the areal specific capacity of MoO3/TNAs (~797 µAh cm−2 was three times higher than those of anatase TNAs (~287 µAh cm−2 and porous MoO3 (~234 µAh cm−2 at 50 µA cm−2.

Effect of hydrophilicity of carbon nanotube arrays on the release rate and activity of recombinant human bone morphogenetic protein-2

Energy Technology Data Exchange (ETDEWEB)

Han Zhaojun; Ostrikov, Kostya [Plasma Nanoscience Centre Australia (PNCA), CSIRO Materials Science and Engineering, Lindfield, New South Wales 2070 (Australia); Tan, Cher Ming; Tay, Beng Kang [School of Electrical and Electronic Engineering, Nanyang Technological University, 639798 (Singapore); Peel, Sean A F, E-mail: zhaojun.han@csiro.au [Department of Dentistry, University of Toronto, Toronto, ON, M5G 1G6 (Canada)

2011-07-22

Novel nanostructures such as vertically aligned carbon nanotube (CNT) arrays have received increasing interest as drug delivery carriers. In the present study, two CNT arrays with extreme surface wettabilities are fabricated and their effects on the release of recombinant human bone morphogenetic protein-2 (rhBMP-2) are investigated. It is found that the superhydrophilic arrays retained a larger amount of rhBMP-2 than the superhydrophobic ones. Further use of a poloxamer diffusion layer delayed the initial burst and resulted in a greater total amount of rhBMP-2 released from both surfaces. In addition, rhBMP-2 bound to the superhydrophilic CNT arrays remained bioactive while they denatured on the superhydrophobic surfaces. These results are related to the combined effects of rhBMP-2 molecules interacting with poloxamer and the surface, which could be essential in the development of advanced carriers with tailored surface functionalities.

Quasi-ballistic carbon nanotube array transistors with current density exceeding Si and GaAs

Science.gov (United States)

Brady, Gerald J.; Way, Austin J.; Safron, Nathaniel S.; Evensen, Harold T.; Gopalan, Padma; Arnold, Michael S.

2016-01-01

Carbon nanotubes (CNTs) are tantalizing candidates for semiconductor electronics because of their exceptional charge transport properties and one-dimensional electrostatics. Ballistic transport approaching the quantum conductance limit of 2G0 = 4e2/h has been achieved in field-effect transistors (FETs) containing one CNT. However, constraints in CNT sorting, processing, alignment, and contacts give rise to nonidealities when CNTs are implemented in densely packed parallel arrays such as those needed for technology, resulting in a conductance per CNT far from 2G0. The consequence has been that, whereas CNTs are ultimately expected to yield FETs that are more conductive than conventional semiconductors, CNTs, instead, have underperformed channel materials, such as Si, by sixfold or more. We report quasi-ballistic CNT array FETs at a density of 47 CNTs μm−1, fabricated through a combination of CNT purification, solution-based assembly, and CNT treatment. The conductance is as high as 0.46 G0 per CNT. In parallel, the conductance of the arrays reaches 1.7 mS μm−1, which is seven times higher than the previous state-of-the-art CNT array FETs made by other methods. The saturated on-state current density is as high as 900 μA μm−1 and is similar to or exceeds that of Si FETs when compared at and equivalent gate oxide thickness and at the same off-state current density. The on-state current density exceeds that of GaAs FETs as well. This breakthrough in CNT array performance is a critical advance toward the exploitation of CNTs in logic, high-speed communications, and other semiconductor electronics technologies. PMID:27617293

The relationship between critical current and microstructure of internal tin wire

International Nuclear Information System (INIS)

Dietderich, D.R.; Hassenzahl, W.V.; Morris, J.W. Jr.

1986-01-01

Prior work on internal tin wire has shown that an increase in critical current results when the Nb 3 Sn reaction temperatures (650-730 0 C) are preceded by low temperature diffusion heat treatments that distribute the tin. These heat treatments produce a more uniform tin distribution through the niobium filament array before substantial Nb 3 Sn formation has occurred. Heat treatments as long as 19 days have been proposed as the optimal heat treatment for the conductor. However, it is possible to substantially reduce the low temperature heat treatment time while retaining the same high critical current. The success of shortened heat treatments may be interpreted on the basis of the Cu-Sn reaction, diffusion kinetics and the Nb 3 Sn growth kinetics

A practical dimensionless equation for the thermal conductivity of carbon nanotubes and CNT arrays

Directory of Open Access Journals (Sweden)

Qiang Chen

2014-05-01

Full Text Available Experimental results reported in the last decade on the thermal conductivity of carbon nanotubes (CNTs have shown a fairly divergent behavior. An underlying intrinsic consistency was believed to exist in spite of the divergence in the thermal conductivity data of various CNTs. A dimenisonless equation that describes the temperature dependence of thermal conductivity was derived by introducing reduced forms relative to a chosen reference point. This equation can serve as a practical approximation to characterize the conductivity of individual CNT with different structural parameters as well as bulk CNT arrays with different bundle configurations. Comparison of predictions by the equation and historical measurements showed good agreements within their uncertainties.

Carbon nanotube diameter selection by pretreatment of metal catalysts on surfaces

Science.gov (United States)

Hauge, Robert H [Houston, TX; Xu, Ya-Qiong [Houston, TX; Shan, Hongwei [Houston, TX; Nicholas, Nolan Walker [South Charleston, WV; Kim, Myung Jong [Houston, TX; Schmidt, Howard K [Cypress, TX; Kittrell, W Carter [Houston, TX

2012-02-28

A new and useful nanotube growth substrate conditioning processes is herein disclosed that allows the growth of vertical arrays of carbon nanotubes where the average diameter of the nanotubes can be selected and/or controlled as compared to the prior art.

Multi-walled carbon nano-tubes for energy storage and production applications

International Nuclear Information System (INIS)

Andrews, R.; Jacques, D.; Likpa, S.; Qian, D.; Rantell, T.; Anthony, J.

2005-01-01

Full text of publication follows: Since their discovery, carbon nano-tubes have been proposed as candidate materials for a broad range of applications, including high strength composites, molecular electronics, and energy storage. In many cases, nano-tubes have been proposed to replace traditional carbon materials, such as activated carbons in energy storage devices. In other cases, novel applications have been proposed, such as the use of carbon nano-tube arrays in photovoltaic devices. The use of multi-walled carbon nano-tubes in energy storage devices has generated great interest due to their high inherent conductivity, layered structure, and high surface area per volume compared to traditional graphitic materials. However as produced nano-tubes do not possess ideal properties, and exhibit only modest charge storage. We have explored the charge storage abilities of nano-tubes with varying morphologies (fullerenic versus stacked cones), nano-tubes containing N or B dopants, as well as various post-treatments of the nano-tubes. The use of nano-tubes in charge storage devices will be described, as well as modification of the nano-tube surfaces or morphology to improve this performance. The synthesis of nano-tubes with several differing hetero-atom dopants will also be described, as well as the effect of heat treatment on these structures. One of the most significant problems in organic photovoltaics is the typically low charge-carrier mobility in organic thin films which, coupled with short exciton diffusion lengths, means that photo-generated charge-carrier pairs are more likely to re-combine than reach an electrode to generate current. Two organic systems with high charge-carrier mobilities are carbon nano-tubes (here, MWNTs) and acene-based organic semiconductors. We believe that blended devices based on MWNTs and organic semiconductors could lead to the next class of efficient, flexible and inexpensive organic photovoltaic systems. We have developed methods to

Production and characterization of a novel carbon nanotube/titanium nitride nanocomposite

Science.gov (United States)

Baddour, Carole Emilie; Das, Kaushik; Vengallatore, Srikar; Meunier, Jean-Luc

2016-12-01

A novel titanium nitride (TiN)/carbon nanotube (CNT) nanocomposite is produced with the purpose to mechanically, structurally and chemically stabilize a ‘felt-like’ CNT growth structure. The CNTs are grown on stainless steel (SS) 304 by chemical vapor deposition using the direct growth method previously developed, which does not require the use of an additional catalyst precursor. The TiN coating is achieved by physical vapor deposition and is shown here to generate a nanocomposite with a porous three-dimensional architecture. The contact stiffness is evaluated using nanoindentation, and wetting properties of the TiN/CNT nanocomposites are determined from contact angle measurements. An increase in contact stiffness and effective elastic modulus with TiN coating time was observed. The TiN coating on the non-wetting CNT felt results in a wetting nanocomposite surface. The wetting property is found to be a function of the TiN coating thickness on the CNT structure.

Fabrication of a gas sensor array with micro-wells for VOCs gas sensing based on polymer/carbon nanotube thin films

Science.gov (United States)

Xie, Guangzhong; Xie, Tao; Zhu, Tao; Jiang, Yadong; Tai, Huiling

2014-08-01

In this paper, gas sensor array with micro-well was designed and prepared by Micro Electro-Mechanical Systems (MEMS) technology. The micro-well and interdigital electrodes of sensor array were prepared using photolithography process, reactive ion etching (RIE) process, wet etching and conventional vacuum evaporation. In the manufacture process of the gas sensor array, KOH wet etching process was mainly discussed. The optimum etching processing parameters were as follows: 30 wt% KOH solution at 80 °C, a cooling back-flow device and a magnetic stirrer. The multi-walled carbon nanotubes (MWCNTs)-polyethyleneoxide (PEO) and MWNTs-Polyvinylpyrrolidone (PVP) composite films were utilized as sensitive layers to test gas-sensing properties. Response performances of MWCNTs- PEO and MWNTs-PVP composite films to toluene vapor and methanol vapor at room temperature were investigated. The results revealed that the sensor array showed a larger sensitivity to toluene vapor than to methanol vapor. In addition, the sensing mechanisms were studied as well.

Design of hybrid two-dimensional and three-dimensional nanostructured arrays for electronic and sensing applications

Science.gov (United States)

Ko, Hyunhyub

This dissertation presents the design of organic/inorganic hybrid 2D and 3D nanostructured arrays via controlled assembly of nanoscale building blocks. Two representative nanoscale building blocks such as carbon nanotubes (one-dimension) and metal nanoparticles (zero-dimension) are the core materials for the study of solution-based assembly of nanostructured arrays. The electrical, mechanical, and optical properties of the assembled nanostructure arrays have been investigated for future device applications. We successfully demonstrated the prospective use of assembled nanostructure arrays for electronic and sensing applications by designing flexible carbon nanotube nanomembranes as mechanical sensors, highly-oriented carbon nanotubes arrays for thin-film transistors, and gold nanoparticle arrays for SERS chemical sensors. In first section, we fabricated highly ordered carbon nanotube (CNT) arrays by tilted drop-casting or dip-coating of CNT solution on silicon substrates functionalized with micropatterned self-assembled monolayers. We further exploited the electronic performance of thin-film transistors based on highly-oriented, densely packed CNT micropatterns and showed that the carrier mobility is largely improved compared to randomly oriented CNTs. The prospective use of Raman-active CNTs for potential mechanical sensors has been investigated by studying the mechano-optical properties of flexible carbon nanotube nanomembranes, which contain freely-suspended carbon nanotube array encapsulated into ultrathin (optical waveguide properties of nano-canals. We demonstrated the ability of this SERS substrate for trace level sensing of nitroaromatic explosives by detecting down to 100 zeptogram (˜330 molecules) of DNT.

A Facile Method for Loading CeO2 Nanoparticles on Anodic TiO2 Nanotube Arrays.

Science.gov (United States)

Liao, Yulong; Yuan, Botao; Zhang, Dainan; Wang, Xiaoyi; Li, Yuanxun; Wen, Qiye; Zhang, Huaiwu; Zhong, Zhiyong

2018-04-03

In this paper, a facile method was proposed to load CeO 2 nanoparticles (NPs) on anodic TiO 2 nanotube (NT) arrays, which leads to a formation of CeO 2 /TiO 2 heterojunctions. Highly ordered anatase phase TiO 2 NT arrays were fabricated by using anodic oxidation method, then these individual TiO 2 NTs were used as tiny "nano-containers" to load a small amount of Ce(NO 3 ) 3 solutions. The loaded anodic TiO 2 NTs were baked and heated to a high temperature of 450 °C, under which the Ce(NO 3 ) 3 would be thermally decomposed inside those nano-containers. After the thermal decomposition of Ce(NO 3 ) 3 , cubic crystal CeO 2 NPs were obtained and successfully loaded into the anodic TiO 2 NT arrays. The prepared CeO 2 /TiO 2 heterojunction structures were characterized by a variety of analytical technologies, including XRD, SEM, and Raman spectra. This study provides a facile approach to prepare CeO 2 /TiO 2 films, which could be very useful for environmental and energy-related areas.

Fabrication of Au nanoparticle/double-walled carbon nanotube film/TiO{sub 2} nanotube array/Ti heterojunctions with low resistance state for broadband photodetectors

Energy Technology Data Exchange (ETDEWEB)

Chen, Yan [School of Mathematics and Physics, Mianyang Teachers’ College (Mianyang Normal University), Mianyang 621000 (China); Zhang, Guowei; Dong, Zhanmin [Department of Physics and State Key Lab of Low-Dimensional Quantum Physics, Tsinghua University, Beijing100084 (China); Wei, Jinquan [Key Laboratory for Advanced Materials Processing Technology of Education Ministry, School of Materials Science and Engineering, Tsinghua University, Beijing100084 (China); Zhu, Jia-Lin [Department of Physics and State Key Lab of Low-Dimensional Quantum Physics, Tsinghua University, Beijing100084 (China); Sun, Jia-Lin, E-mail: jlsun@tsinghua.edu.cn [Department of Physics and State Key Lab of Low-Dimensional Quantum Physics, Tsinghua University, Beijing100084 (China); Collaborative Innovation Center of Quantum Matter, Beijing (China)

2017-03-01

A broadband photodetector based on Au nanoparticle/double-walled carbon nanotube film/TiO{sub 2} nanotube array /Ti multilayer heterojunction structures has been fabricated. A pre-electroforming process at a voltage bias of 35 V was used to switch the photodetector from a high resistance state to a low resistance state. At a voltage bias of 1 V under 532-nm laser illumination in air, the photoresponsivity of the device reached 15.41 mA W{sup −1}, which is enhanced by approximately 1.91 times when compared with that of device before deposition of Au nanoparticles. In addition, in a vacuum under a voltage bias of 1 V, the photoresponsivity of the device reached 23.29 mA W{sup −1} and 6.85 mA W{sup −1} at 532 nm and 1064 nm, respectively. The surface plasmon polaritons of the Au nanoparticles allowed extension of the sensitivity of the photosensitive regions into the mid-infrared range. The experimental results show that the device photoresponsivity reached 2.26 mA W{sup −1} at a voltage bias of 1 V under 10.6-µm laser illumination in air.

Titania nanotube arrays surface-modified with ZnO for enhanced photocatalytic applications

Energy Technology Data Exchange (ETDEWEB)

Nageri, Manoj; Kalarivalappil, Vijila; Vijayan, Baiju K.; Kumar, Viswanathan, E-mail: vkumar10@yahoo.co.in

2016-05-15

Highlights: • Heterostructures of TNA/ZnO synthesised through potentiostatic anodisation followed by hydrothermal method. • Evaluation of morphological features of the heterostructure with hydrothermal processing time. • Correlation of photocatalytic activity of the hetrostructure with its morphology and surface texture. - Abstract: Well ordered titanium dioxide nanotube arrays (TNA) of average diameter 129 nm and wall thickness of 25 nm were fabricated through potentiostatic anodisation of titanium (Ti) metal substrates. Such TNA were subsequently surface-modified with various amounts of zinc oxide (ZnO) nanopowders using hydrothermal technique to obtain heterogeneous TNA/ZnO nanostructures. The crystalline phase and surface microstructure of the heterostructures were determined by X-ray diffraction, Raman spectroscopy and scanning electron microscopy respectively. The morphology of the heterostructures strongly depended on the hydrothermal conditions employed. The photocatalytic activity of the heterostructures have also been investigated and correlated with their surface morphology and texture.

Synthesis of Large Arrays of Well-Aligned Carbon Nanotubes on Glass

Energy Technology Data Exchange (ETDEWEB)

Bush, P. Siegal, M.P.; Huang, Z.P.; Provencio, P.N.; Ren, Z.F.; Wang, J.H.; Xu, J.W.

1998-11-10

Free-standing aligned carbon nanotubes have previously been grown above 7000C on mesoporous silica embedded with iron nanoparticles. Here, carbon nanotubes aligned over areas up to several square centimeters were grown on nickel-coated glass below 666oC by plasma-enhanced hot filament chemical vapor deposition. Acetylene (C2H2) gas was used as the carbon source and ammonia (NH3) gas was used as a catalyst and dilution gas. Nanotubes with controllable diameters from 20 to 400 nanometers and lengths from 0.1 to 50 micrometers were obtained. Using this method, large panels of aligned carbon nanotubes can be made under conditions that are suitable for device fabrication.

Flow-Regulated Growth of Titanium Dioxide (TiO2 ) Nanotubes in Microfluidics.

Science.gov (United States)

Fan, Rong; Chen, Xinye; Wang, Zihao; Custer, David; Wan, Jiandi

2017-08-01

Electrochemical anodization of titanium (Ti) in a static, bulk condition is used widely to fabricate self-organized TiO 2 nanotube arrays. Such bulk approaches, however, require extended anodization times to obtain long TiO 2 nanotubes and produce only vertically aligned nanotubes. To date, it remains challenging to develop effective strategies to grow long TiO 2 nanotubes in a short period of time, and to control the nanotube orientation. Here, it is shown that the anodic growth of TiO 2 nanotubes is significantly enhanced (≈16-20 times faster) under flow conditions in microfluidics. Flow not only controls the diameter, length, and crystal orientations of TiO 2 nanotubes, but also regulates the spatial distribution of nanotubes inside microfluidic devices. Strikingly, when a Ti thin film is deposited on silicon substrates and anodized in microfluidics, both vertically and horizontally aligned (relative to the bottom substrate) TiO 2 nanotubes can be produced. The results demonstrate previously unidentified roles of flow in the regulation of growth of TiO 2 nanotubes, and provide powerful approaches to effectively grow long, oriented TiO 2 nanotubes, and construct hierarchical TiO 2 nanotube arrays on silicon-based materials. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Femtosecond laser modification of an array of vertically aligned carbon nanotubes intercalated with Fe phase nanoparticles.

Science.gov (United States)

Labunov, Vladimir; Prudnikava, Alena; Bushuk, Serguei; Filatov, Serguei; Shulitski, Boris; Tay, Beng Kang; Shaman, Yury; Basaev, Alexander

2013-09-03

Femtosecond lasers (FSL) are playing an increasingly important role in materials research, characterization, and modification. Due to an extremely short pulse width, interactions of FSL irradiation with solid surfaces attract special interest, and a number of unusual phenomena resulted in the formation of new materials are expected. Here, we report on a new nanostructure observed after the interaction of FSL irradiation with arrays of vertically aligned carbon nanotubes (CNTs) intercalated with iron phase catalyst nanoparticles. It was revealed that the FSL laser ablation transforms the topmost layer of CNT array into iron phase nanospheres (40 to 680 nm in diameter) located at the tip of the CNT bundles of conical shape. Besides, the smaller nanospheres (10 to 30 nm in diameter) are found to be beaded at the sides of these bundles. Some of the larger nanospheres are encapsulated into carbon shells, which sometime are found to contain CNTs. The mechanism of creation of such nanostructures is proposed.

Facile Synthesis of Highly Aligned Multiwalled Carbon Nanotubes from Polymer Precursors

Directory of Open Access Journals (Sweden)

Catherine Y. Han

2009-01-01

Full Text Available We report a facile one-step approach which involves no flammable gas, no catalyst, and no in situ polymerization for the preparation of well-aligned carbon nanotube array. A polymer precursor is placed on top of an anodized aluminum oxide (AAO membrane containing regular nanopore arrays, and slow heating under Ar flow allows the molten polymer to wet the template through adhesive force. The polymer spread into the nanopores of the template to form polymer nanotubes. Upon carbonization the resulting multi-walled carbon nanotubes duplicate the nanopores morphology precisely. The process is demonstrated for 230, 50, and 20 nm pore membranes. The synthesized carbon nanotubes are characterized with scanning/transmission electron microscopies, Raman spectroscopy, and resistive measurements. Convenient functionalization of the nanotubes with this method is demonstrated through premixing CoPt nanoparticles in the polymer precursors.

Facile synthesis of highly aligned multiwalled carbon nanotubes from polymer precursors.

Energy Technology Data Exchange (ETDEWEB)

Han, C. Y.; Xiao, Z.-L.; Wang, H. H.; Lin, X.-M.; Trasobares, S.; Cook, R. E.; Richard J. Daley Coll.; Northern Illinois Univ.; Univ. de Cadiz

2009-01-01

We report a facile one-step approach which involves no flammable gas, no catalyst, and no in situ polymerization for the preparation of well-aligned carbon nanotube array. A polymer precursor is placed on top of an anodized aluminum oxide (AAO) membrane containing regular nanopore arrays, and slow heating under Ar flow allows the molten polymer to wet the template through adhesive force. The polymer spread into the nanopores of the template to form polymer nanotubes. Upon carbonization the resulting multi-walled carbon nanotubes duplicate the nanopores morphology precisely. The process is demonstrated for 230, 50, and 20 nm pore membranes. The synthesized carbon nanotubes are characterized with scanning/transmission electron microscopies, Raman spectroscopy, and resistive measurements. Convenient functionalization of the nanotubes with this method is demonstrated through premixing CoPt nanoparticles in the polymer precursors.

Effect of the geometry of the anodized titania nanotube array on the performance of dye-sensitized solar cells.

Science.gov (United States)

Sun, Lidong; Zhang, Sam; Sun, Xiaowei; He, Xiaodong

2010-07-01

Highly ordered TiO2 nanotube arrays are superior photoanodes for dye-sensitized solar cells (DSSCs) due to reduced intertube connections, vectorial electron transport, suppressed electron recombination, and enhanced light scattering. Performance of the cells is greatly affected by tube geometry, such as wall thickness, length, inner diameter and intertube spacing. In this paper, effect of geometry on the photovoltaic characteristics of DSSCs is reviewed. The nanotube wall has to be thick enough for a space charge layer to form for faster electron transportation and reduced recombination. When the tube wall is too thin to support the space charge layer, electron transport in the nanotubes will be hindered and reduced to that similar in a typical nanoparticle photoanode, and recombination will easily take place. Length of the nanotubes also plays a role: longer tube length is desired because of more dye loading, however, tube length longer than the electron diffusion length results in low collecting efficiency, which in turn, results in low short-circuit current density and thus low overall conversion efficiency. The tube inner diameter (pore size) affects the conversion efficiency through effective surface area, i.e., larger pore size gives rise to smaller surface area for dye adsorption, which results in low short-circuit current density under the same light soaking. Another issue that may seriously affect the conversion efficiency is whether each of the tube stands alone (free from connecting to the neighboring tubes) to facilitate infiltration of dye and fully use the outer surface area.

High-performance and renewable supercapacitors based on TiO2 nanotube array electrodes treated by an electrochemical doping approach

International Nuclear Information System (INIS)

Wu, Hui; Li, Dongdong; Zhu, Xufei; Yang, Chunyan; Liu, Dongfang; Chen, Xiaoyuan; Song, Ye; Lu, Linfeng

2014-01-01

Although one-dimensional anodic TiO 2 nanotube arrays have shown promise as supercapacitor electrode materials, their poor electronic conductivity embarrasses the practical applications. Here, we develop a simple electrochemical doping method to significantly improve the electronic conductivity and the electrochemical performances of TiO 2 nanotube electrodes. These TiO 2 nanotube electrodes treated by the electrochemical hydrogenation doping (TiO 2 -H) exhibit a very high average specific capacitance of 20.08 mF cm −2 at a current density of 0.05 mA cm −2 , ∼20 times more than the pristine TiO 2 nanotube electrodes. The improved electrochemical performances can be attributed to ultrahigh conductivity of TiO 2 -H due to the introduction of interstitial hydrogen ions and oxygen vacancies by the doping. The supercapacitor device assembled by the doped electrodes delivers a specific capacitance of 5.42 mF cm −2 and power density of 27.66 mW cm −2 , on average, at the current density of 0.05 mA cm −2 . The device also shows an outstanding rate capability with 60% specific capacitance retained when the current density increases from 0.05 to 4.00 mA cm −2 . More interestingly, the electrochemical performances of the supercapacitor after cycling can be recovered by the same doping process. This strategy boosts the performances of the supercapacitor, especially cycling stability

Fabrication and photocatalytic activity of high-efficiency visible-light-responsive photocatalyst ZnTe/TiO2 nanotube arrays

International Nuclear Information System (INIS)

Liu Yutang; Zhang Xilin; Liu Ronghua; Yang Renbin; Liu Chengbin; Cai Qingyun

2011-01-01

A new ZnTe modified TiO 2 nanotube (NT) array catalyst was prepared by pulse potential electrodeposition of ZnTe nanoparticles (NPs) onto TiO 2 NT arrays, and its application for photocatalytic degradation of anthracene-9-carboxylic acid (9-AnCOOH) was investigated. The even distribution of ZnTe NPs was well-proportionately grown on the top surface of the TiO 2 NT while without clogging the tube entrances. Compared with the unmodified TiO 2 NT, the ZnTe modified TiO 2 NT (ZnTe/TiO 2 NT) showed significantly enhanced photocatalytic activity towards 9-AnCOOH under simulated solar light. After 70 min of irradiation, 9-AnCOOH was degraded with the removal ratio of 45% on the bare TiO 2 NT, much lower than 80%, 90%, and 100% on the ZnTe/TiO 2 NT with the ZnTe NPs prepared under the pulsed 'on' potentials of -0.8, -1.0, and -2.0 V, respectively. The increased photodegradation efficiency mainly results from the improved photocurrent density as results of enhanced visible-light absorption and decreased hole-electron recombination due to the presence of narrow-band-gap p-type semiconductor ZnTe. -- Graphical abstract: Surface-view SEM images of ZnTe/TiO 2 NT prepared under -2.0 V, and the inset is the corresponding enlarged drawings. Display Omitted Research highlights: → A new method to deposit chalcogenides of transition metals on the TiO 2 nanotubes. → The even distribution of ZnTe nanoparticles was well-proportionedly grown onto TiO 2 NT arrays. → ZnTe/TiO 2 NT showed remarkably increased photocurrent density. → ZnTe/TiO 2 NT showed good photocatalytic performance. → The prepared new catalyst has a promising application in practical systems.

The Surface Interface Characteristics of Vertically Aligned Carbon Nanotube and Graphitic Carbon Fiber Arrays Grown by Thermal and Plasma Enhanced Chemical Vapor Deposition

Science.gov (United States)

Delzeit, Lance; Nguyen, Cattien; Li, Jun; Han, Jie; Meyyappan, M.

2002-01-01

The development of nano-arrays for sensors and devices requires the growth of arrays with the proper characteristics. One such application is the growth of vertically aligned carbon nanotubes (CNTs) and graphitic carbon fibers (GCFs) for the chemical attachment of probe molecules. The effectiveness of such an array is dependent not only upon the effectiveness of the probe and the interface between that probe and the array, but also the array and the underlaying substrate. If that array is a growth of vertically aligned CNTs or GCFs then the attachment of that array to the surface is of the utmost importance. This attachment provides the mechanical stability and durability of the array, as well as, the electrical properties of that array. If the detection is to be acquired through an electrical measurement, then the appropriate resistance between the array and the surface need to be fabricated into the device. I will present data on CNTs and GCFs grown from both thermal and plasma enhanced chemical vapor deposition. The focus will be on the characteristics of the metal film from which the CNTs and GCFs are grown and the changes that occur due to changes within the growth process.

Broadband Light Collection Efficiency Enhancement of Carbon Nanotube Excitons Coupled to Metallo-Dielectric Antenna Arrays

Energy Technology Data Exchange (ETDEWEB)

Shayan, Kamran [Department; Rabut, Claire [Department; Kong, Xiaoqing [Department; Li, Xiangzhi [Department; Luo, Yue [Department; Mistry, Kevin S. [National Renewable; Blackburn, Jeffrey L. [National Renewable; Lee, Stephanie S. [Department; Strauf, Stefan [Department

2017-11-09

The realization of on-chip quantum networks ideally requires lossless interfaces between photons and solid-state quantum emitters. We propose and demonstrate on-chip arrays of metallo-dielectric antennas (MDA) that are tailored toward efficient and broadband light collection from individual embedded carbon nanotube quantum emitters by trapping air gaps on chip that form cavity modes. Scalable implementation is realized by employing polymer layer dry-transfer techniques that avoid solvent incompatibility issues, as well as a planar design that avoids solid-immersion lenses. Cryogenic measurements demonstrate 7-fold enhanced exciton intensity when compared to emitters located on bare wafers, corresponding to a light collection efficiency (LCE) up to 92% in the best case (average LCE of 69%) into a narrow output cone of +/-15 degrees that enables a priori fiber-to-chip butt coupling. The demonstrated MDA arrays are directly compatible with other quantum systems, particularly 2D materials, toward enabling efficient on-chip quantum light sources or spin-photon interfaces requiring unity light collection, both at cryogenic or room temperature.

Remote and direct plasma regions for low-temperature growth of carbon nanotubes on glass substrates for display applications

International Nuclear Information System (INIS)

Tabatabaei, M K; Ghafouri fard, H; Koohsorkhi, J; Khatami, S; Mohajerzadeh, S

2011-01-01

A novel method for growing carbon nanotubes (CNTs) on glass substrates is introduced in this study. A two-stage plasma was used to achieve low-temperature and vertically aligned CNTs. Ni deposited on indium tin oxide/glass substrate was used as the catalyst and hydrogen and acetylene were used as gas feeds. In this investigation a new technique was developed to grow vertically aligned CNTs at temperatures below 400 deg. C while CNT growth by plasma-enhanced chemical vapour deposition required high temperatures. Low-temperature growth of vertically aligned CNTs was suitable for the fabrication of micro-lens and self-oriented displays on glass substrates. Also, we have reported a new configuration for CNT-based display by means of controlling the refractive index of liquid crystal around the CNT by applying a proper voltage to the top and bottom array.

Self-organized TiO{sub 2} nanotubes in mixed organic-inorganic electrolytes and their photoelectrochemical performance

Energy Technology Data Exchange (ETDEWEB)

Lai Yuekun [State Key Laboratory for Physical Chemistry of Solid Surfaces, and Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005 (China); School of Materials Science and Engineering, Nanyang Technological University, 50 Nanyang Avenue, Singapore 639798 (Singapore); Zhuang Huifang; Sun Lan [State Key Laboratory for Physical Chemistry of Solid Surfaces, and Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005 (China); Chen Zhong [School of Materials Science and Engineering, Nanyang Technological University, 50 Nanyang Avenue, Singapore 639798 (Singapore); Lin Changjian [State Key Laboratory for Physical Chemistry of Solid Surfaces, and Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005 (China)], E-mail: cjlin@xmu.edu.cn

2009-11-01

The formation of self-organized TiO{sub 2} nanotube array films by electrochemical anodizing titanium foils was investigated in a developed organic-inorganic mixed electrolyte. It was found that the structure and morphology of the TiO{sub 2} nanotube layer were greatly dependent upon the electrolyte composition, anodizing potential and time. Under the optimized electrolyte composition and electrochemical conditions, a controllable, well-ordered TiO{sub 2} nanotube array layer could be fabricated in a short time. The diameters of the as-prepared TiO{sub 2} nanotubes could be adjusted from 20 to 150 nm, and the thickness could be adjusted from a few hundred nanometers to several micrometers. The photoresponse and the photocatalytic activity of the highly ordered TiO{sub 2} nanotube array films were also examined. The nanotube array film with a thickness of about 2.5 {mu}m had the highest incident photon to photocurrent conversion efficiency (IPCE) (34.3%) at the 350 nm wavelength, and had better charge transfer ability under UV light illumination. The photocatalytic experimental results indicated that the 450 deg. C annealing samples have the highest photodegradation efficiency for methyl orange pollutant.

Tailoring the Electrochemical Properties of Carbon Nanotube Modified Indium Tin Oxide via in Situ Grafting of Aryl Diazonium.

Science.gov (United States)

Hicks, Jacqueline M; Wong, Zhi Yi; Scurr, David J; Silman, Nigel; Jackson, Simon K; Mendes, Paula M; Aylott, Jonathan W; Rawson, Frankie J

2017-05-23

Our ability to tailor the electronic properties of surfaces by nanomodification is paramount for various applications, including development of sensing, fuel cell, and solar technologies. Moreover, in order to improve the rational design of conducting surfaces, an improved understanding of structure/function relationships of nanomodifications and effect they have on the underlying electronic properties is required. Herein, we report on the tuning and optimization of the electrochemical properties of indium tin oxide (ITO) functionalized with single-walled carbon nanotubes (SWCNTs). This was achieved by controlling in situ grafting of aryl amine diazonium films on the nanoscale which were used to covalently tether SWCNTs. The structure/function relationship of these nanomodifications on the electronic properties of ITO was elucidated via time-of-flight secondary ion mass spectrometry and electrochemical and physical characterization techniques which has led to new mechanistic insights into the in situ grafting of diazonium. We discovered that the connecting bond is a nitro group which is covalently linked to a carbon on the aryl amine. The increased understanding of the surface chemistry gained through these studies enabled us to fabricate surfaces with optimized electron transfer kinetics. The knowledge gained from these studies allows for the rational design and tuning of the electronic properties of ITO-based conducting surfaces important for development of various electronic applications.

Synthesis and optimization of tin dioxide/functionalized multi-walled carbon nanotube composites as anode in lithium-ion battery

Energy Technology Data Exchange (ETDEWEB)

Xu, Xiao-Bing; Geng, Hong-Zhang, E-mail: genghz@tjpu.edu.cn; Meng, Yan; Ding, Er-Xiong; Wang, Yan; Zhang, Ze-Chen; Wang, Wen-Yi

2015-03-01

In this paper, nanocomposite electrodes for rechargeable Lithium-ion battery composed of tin dioxide (SnO{sub 2}) and multi-walled carbon nanotubes (MWCNTs) were prepared using the chemical deposition method with a subsequent sintering process. The as-prepared hybrids were characterized by thermal gravimetric analysis, Fourier transform infrared spectroscopy, X-ray diffraction and transmission electron microscopy. The results showed that the size of pure SnO{sub 2} particles was ∼5 nm and hybrids presented a uniform dispersion of SnO{sub 2} nanoparticles on the surfaces of the MWCNTs. The electrochemical properties of the composites were researched through a cyclic voltammetry and a galvanostatic charge–discharge test. It was found that the electrochemical performance of the composite was strongly dependent on the content of MWCNTs in the composites. The SnO{sub 2}/MWCNT composite with 18.40 wt% MWCNTs gave the best performance, exhibiting a relatively higher reversible capacity of 475 mAh g{sup −1} and an extended capacity retention of 65% even after 30 cycles at a current density of 78.2 mA g{sup −1}. - Highlights: • SnO{sub 2}/MWCNT nanocomposites were prepared using chemical deposition method. • SnO{sub 2} nanoparticles presented a uniformly dispersion on the surfaces of MWCNTs. • SnO{sub 2}/MWCNT composite anode exhibited high reversible capacity for rechargeable Li-ion battery.

Synthesis and optimization of tin dioxide/functionalized multi-walled carbon nanotube composites as anode in lithium-ion battery

International Nuclear Information System (INIS)

Xu, Xiao-Bing; Geng, Hong-Zhang; Meng, Yan; Ding, Er-Xiong; Wang, Yan; Zhang, Ze-Chen; Wang, Wen-Yi

2015-01-01

In this paper, nanocomposite electrodes for rechargeable Lithium-ion battery composed of tin dioxide (SnO 2 ) and multi-walled carbon nanotubes (MWCNTs) were prepared using the chemical deposition method with a subsequent sintering process. The as-prepared hybrids were characterized by thermal gravimetric analysis, Fourier transform infrared spectroscopy, X-ray diffraction and transmission electron microscopy. The results showed that the size of pure SnO 2 particles was ∼5 nm and hybrids presented a uniform dispersion of SnO 2 nanoparticles on the surfaces of the MWCNTs. The electrochemical properties of the composites were researched through a cyclic voltammetry and a galvanostatic charge–discharge test. It was found that the electrochemical performance of the composite was strongly dependent on the content of MWCNTs in the composites. The SnO 2 /MWCNT composite with 18.40 wt% MWCNTs gave the best performance, exhibiting a relatively higher reversible capacity of 475 mAh g −1 and an extended capacity retention of 65% even after 30 cycles at a current density of 78.2 mA g −1 . - Highlights: • SnO 2 /MWCNT nanocomposites were prepared using chemical deposition method. • SnO 2 nanoparticles presented a uniformly dispersion on the surfaces of MWCNTs. • SnO 2 /MWCNT composite anode exhibited high reversible capacity for rechargeable Li-ion battery

Polymeric Electrolyte Membrane Photoelectrochemical (PEM-PEC Cell with a Web of Titania Nanotube Arrays as Photoanode and Gaseous Reactants

Directory of Open Access Journals (Sweden)

Tsampas M.N.

2017-01-01

Photoanodes of titania nanotube arrays, TNTAs, were developed, for the first time, on a Ti-web of microfiber substrates, by electrochemical anodization. The performance of TNTAs/Ti-web photoanodes were evaluated in both gaseous and liquid reactants. Due to the presence of reliable reference electrode in gas phase direct comparison of the results was possible. Gas phase operation with He or Air as carrier gases and only 2.5% of water content exhibits very promising photoefficiency in comparison with conventional PEC cells.

Anatase TiO2 nanotube arrays and titania films on titanium mesh for photocatalytic NOx removal and water cleaning

Czech Academy of Sciences Publication Activity Database

Motola, M.; Satrapinskyy, L.; Roch, T.; Šubrt, Jan; Kupčík, Jaroslav; Klementová, Mariana; Jakubičková, M.; Peterka, F.; Plesch, G.

2017-01-01

Roč. 287, JUN (2017), s. 59-64 ISSN 0920-5861. [European meeting on Solar Chemistry and Photocatalysis: Environmental Applications (SPEA) /9./. Strasbourg, 13.06.2016-17.06.2016] R&D Projects: GA ČR(CZ) GA14-20744S; GA MŠk(CZ) 7AMB14SK178 Institutional support: RVO:61388980 Keywords : Titanium mesh * Anatase nanotubes array * Liquid state deposition * NOx removal * Photocatalysis Subject RIV: CA - Inorganic Chemistry OBOR OECD: Inorganic and nuclear chemistry Impact factor: 4.636, year: 2016

Sacrificial template method of fabricating a nanotube

Science.gov (United States)

Yang, Peidong [Berkeley, CA; He, Rongrui [Berkeley, CA; Goldberger, Joshua [Berkeley, CA; Fan, Rong [El Cerrito, CA; Wu, Yi-Ying [Albany, CA; Li, Deyu [Albany, CA; Majumdar, Arun [Orinda, CA

2007-05-01

Methods of fabricating uniform nanotubes are described in which nanotubes were synthesized as sheaths over nanowire templates, such as using a chemical vapor deposition process. For example, single-crystalline zinc oxide (ZnO) nanowires are utilized as templates over which gallium nitride (GaN) is epitaxially grown. The ZnO templates are then removed, such as by thermal reduction and evaporation. The completed single-crystalline GaN nanotubes preferably have inner diameters ranging from 30 nm to 200 nm, and wall thicknesses between 5 and 50 nm. Transmission electron microscopy studies show that the resultant nanotubes are single-crystalline with a wurtzite structure, and are oriented along the direction. The present invention exemplifies single-crystalline nanotubes of materials with a non-layered crystal structure. Similar "epitaxial-casting" approaches could be used to produce arrays and single-crystalline nanotubes of other solid materials and semiconductors. Furthermore, the fabrication of multi-sheath nanotubes are described as well as nanotubes having multiple longitudinal segments.

Photoelectrocatalytic degradation of atrazine by boron-fluorine co-doped TiO2 nanotube arrays.

Science.gov (United States)

Wang, He-Xuan; Zhu, Li-Nan; Guo, Fu-Qiao

2018-06-23

Atrazine, one of the most widespread herbicides in the world, is considered as an environmental estrogen and has potential carcinogenicity. In this study, atrazine was degraded on boron-fluorine co-doped TiO 2 nanotube arrays (B, F-TiO 2 NTAs), which had similar morphology with the pristine TiO 2 NTAs. The structure and morphology of TiO 2 nanotube samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), and UV-visible diffuse reflectance spectroscopy (DRS). It showed that the decoration of fluorine and boron made both the absorption in the visible region enhanced and the band edge absorption shifted. The efficiency of atrazine degradation by B, F-TiO 2 NTAs through photoelectrocatalysis was investigated by current, solution pH, and electrolyte concentration, respectively. The atrazine removal rate reached 76% through photoelectrocatalytic reaction by B, F-TiO 2 NTAs, which was 46% higher than that under the photocatalysis process. Moreover, the maximum degradation rate was achieved at pH of 6 in 0.01 M of Na 2 SO 4 electrolyte solution under a current of 0.02 A and visible light for 2 h in the presence of B, F-TiO 2 NTAs. These results showed that B, F-TiO 2 NTAs exhibit remarkable photoelectrocatalytic activity in degradation of atrazine.

Fabrication of an artificial nanosucker device with a large area nanotube array of metallic glass.

Science.gov (United States)

Chen, Wei-Ting; Manivannan, Karthikeyan; Yu, Chia-Chi; Chu, Jinn P; Chen, Jem-Kun

2018-01-18

The concurrent attachment and detachment movements of geckos on virtually any type of surface via their foot pads have inspired us to develop a thermal device with numerous arrangements of a multi-layer thin film together with electrodes that can help modify the temperature of the surface via application of a voltage. A sequential fabrication process was employed on a large-scale integration to generate well-defined contact hole arrays of photoresist for use as templates on the electrode-based device. The photoresist templates were then subjected to sputter deposition of the metallic glass Zr 55 Cu 30 Al 10 Ni 5 . Consequently, a metallic glass nanotube (MGNT) array having a nominal wall thickness of 100 nm was obtained after removal of the photoresist template. When a water droplet was placed on the MGNT array, close nanochambers of metallic glass were formed. By applying voltage, the surface was heated to increase the pressure inside the nanochambers; this generated an expanding force that raised the droplet; thus, the static water contact angle (SWCA) was increased. In contrast, a sucking force was generated during surface cooling, which decreased the SWCA. Our fabrication strategy exploits the MGNT array surface as nanosuckers, which can mimic the climbing aptitude of geckos as they attach to (>10 N m -2 ) and detach from (0.26 N m -2 ) surfaces at 0.5 and 3 V of applied voltage, respectively. Thus, the climbing aptitude of geckos can be mimicked by employing the processing strategy presented herein for the development of artificial foot pads.

Preparation of Sb2S3 nanocrystals modified TiO2 dendritic structure with nanotubes for hybrid solar cell

Science.gov (United States)

Li, Yingpin; Wei, Yanan; Feng, Kangning; Hao, Yanzhong; Pei, Juan; Sun, Bao

2018-06-01

Array of TiO2 dendritic structure with nanotubes was constructed on transparent conductive fluorine-doped tin oxide glass (FTO) with titanium potassium oxalate as titanium source. Sb2S3 nanocrystals were successfully deposited on the TiO2 substrate via spin-coating method. Furthermore, TiO2/Sb2S3/P3HT/PEDOT:PSS composite film was prepared by successively spin-coating P3HT and PEDOT:PSS on TiO2/Sb2S3. It was demonstrated that the modification of TiO2 dendritic structure with Sb2S3 could enhance the light absorption in the visible region. The champion hybrid solar cell assembled by TiO2/Sb2S3/P3HT/PEDOT:PSS composite film achieved a power conversion efficiency (PCE) of 1.56%.

Self-ordering anodized nanotubes: Enhancing the performance by surface plasmon for dye-sensitized solar cell

International Nuclear Information System (INIS)

Agarwala, S.; Ho, G.W.

2012-01-01

In the present work, electrochemical anodization has been used to prepare uniform TiO 2 nanotube array photoelectrode. The average internal diameter, tube length and wall thickness of the optimized morphology is ∼180 nm, 14 μm and 10 nm, respectively. It was found that the tube diameter increases with the anodization voltage. Diffraction data reveals that the nanotubes consist solely of anatase phase. Back illuminated geometry of dye-sensitized solar cell (DSSC), with nanotubes grown at 60 V for 2 h, gave a cell performance of 4.5%. TiO 2 nanotubes are loaded with silver (Ag) nanoparticles synthesized by a hydrothermal route. The Ag particle size is controlled resulting in solar conversion efficiency to increase by 22%. The DSSC based on TiO 2 nanotube with Ag nanoparticles shows power conversion efficiency of 5.5%. Detailed characterization are performed, presented and discussed. - Graphical abstract: Enhanced solar conversion efficiency of dye-sensitized solar cells by decorating TiO 2 nanotube array with Ag nanoparticles. Highlights: ► Uniform array of TiO 2 nanotubes synthesized via electrochemical anodization. ► Back illuminated DSSC gave a cell performance of 4.5%. ► TiO 2 nanotubes are loaded with Ag nanoparticles, which increased the power conversion efficiency to 5.5%.

Confinement of hydrogen at high pressure in carbon nanotubes

Science.gov (United States)

Lassila, David H [Aptos, CA; Bonner, Brian P [Livermore, CA

2011-12-13

A high pressure hydrogen confinement apparatus according to one embodiment includes carbon nanotubes capped at one or both ends thereof with a hydrogen-permeable membrane to enable the high pressure confinement of hydrogen and release of the hydrogen therethrough. A hydrogen confinement apparatus according to another embodiment includes an array of multi-walled carbon nanotubes each having first and second ends, the second ends being capped with palladium (Pd) to enable the high pressure confinement of hydrogen and release of the hydrogen therethrough as a function of palladium temperature, wherein the array of carbon nanotubes is capable of storing hydrogen gas at a pressure of at least 1 GPa for greater than 24 hours. Additional apparatuses and methods are also presented.

Investigation on the influence of pH on structure and photoelectrochemical properties of CdSe electrolytically deposited into TiO2 nanotube arrays

International Nuclear Information System (INIS)

Xue, Jinbo; Shen, Qianqian; Yang, Fei; Liang, Wei; Liu, Xuguang

2014-01-01

Highlights: • There-dimensional CdSe-TiO 2 multijunction was fabricated by electrochemical method. • CdSe nanoparticles had a good bonding with the walls of TiO 2 nanotube. • pH value played an important role in the quality of CdSe-TiO 2 interfaces. - Abstract: In this work, we fabricated CdSe/TiO 2 nanotube arrays (NTAs) by electrochemical method. In electrodeposition, the pH value of the electrolyte played an important role in formation of CdSe nanoparticles. As the pH value decreased, more CdSe deposited on TiO 2 NTAs. Scanning electron microscopy and transmission electron microscopy characterization shows that the CdSe nanoparticles were uniformly deposited on and into TiO 2 nanotubes when the pH value was 3, and this structure fully utilized the three-dimensional (3D) space of TiO 2 nanotubes to form 3D multijunction heterostructures. According to the photoelectrochemical test, the CdSe/TiO 2 NTAs sample prepared at pH = 3 exhibited maximum photocurrent and open circuit potential. This is because that the deposited CdSe nanoparticles had better bond with the walls of TiO 2 nanotube than the samples deposited at other pH values, which facilitated the propagation and kinetic separation of photogenerated charges

Carbon nanotube fiber spun from wetted ribbon

Science.gov (United States)

Zhu, Yuntian T; Arendt, Paul; Zhang, Xiefei; Li, Qingwen; Fu, Lei; Zheng, Lianxi

2014-04-29

A fiber of carbon nanotubes was prepared by a wet-spinning method involving drawing carbon nanotubes away from a substantially aligned, supported array of carbon nanotubes to form a ribbon, wetting the ribbon with a liquid, and spinning a fiber from the wetted ribbon. The liquid can be a polymer solution and after forming the fiber, the polymer can be cured. The resulting fiber has a higher tensile strength and higher conductivity compared to dry-spun fibers and to wet-spun fibers prepared by other methods.

Parameter optimization for Ag-coated TiO2 nanotube arrays as recyclable SERS substrates

Science.gov (United States)

Sun, Yuyang; Yang, Lulu; Liao, Fan; Dang, Qian; Shao, Mingwang

2018-06-01

The Ag-coated titanium dioxide nanotube arrays (Ag-coated TNTs) are obtained via the deposition of Ag nanoparticles on the two-step anodized TNTs. The wall thickness of TNTs is modulated via finite difference time domain simulation to get the favorable electromagnetic field for surface enhanced Raman scattering (SERS). Ag-coated TNTs with optimal wall thickness of 20 nm were employed as the SERS substrates to detect 2-mercaptobenzoxazole, which show superior detection sensitivity and uniformity. In addition, due to the photocatalysis of TNTs, the SERS substrates could clean themselves and be repeatedly used by photo-degradation of target molecules under the ultra-violet irradiation. The Ag-coated TNTs are a kind of bifunctional SERS substrates which can produce high-quality SERS signals and reuse to reduce the cost.

Field emission from carbon nanotube bundle arrays grown on self-aligned ZnO nanorods

International Nuclear Information System (INIS)

Li Chun; Fang Guojia; Yuan Longyan; Liu Nishuang; Ai Lei; Xiang Qi; Zhao Dongshan; Pan Chunxu; Zhao Xingzhong

2007-01-01

The field emission (FE) properties of carbon nanotube (CNT) bundle arrays grown on vertically self-aligned ZnO nanorods (ZNRs) are reported. The ZNRs were first synthesized on ZnO-seed-coated Si substrate by the vapour phase transport method, and then the radically grown CNTs were grown directly on the surface of the ZNRs from ethanol flames. The CNT/ZNR composite showed a turn-on field of 1.5 V μm -1 (at 0.1 μA cm -2 ), a threshold field of 4.5 V μm -1 (at 1 mA cm -2 ) and a stable emission current with fluctuations of 5%, demonstrating significantly enhanced FE of ZNRs due to the low work function and high aspect ratio of the CNTs, and large surface-to-volume ratio of the underlying ZNRs

Solar fuel production in a novel polymeric electrolyte membrane photoelectrochemical (PEM-PEC) cell with a web of titania nanotube arrays as photoanode and gaseous reactants

NARCIS (Netherlands)

Stoll, T.; Zafeiropoulos, G.; Tsampas, M. N.

2016-01-01

A novel photoelectrochemical (PEC) cell design is proposed and investigated for H-2 production with gaseous reactants. The core of the cell is a membrane electrode assembly (MEA) that consists of a TiO2 nanotube arrays photoanode, a Pt/C cathode, a Pt/C reference electrode and a proton conducting

Surface passivation function of indium-tin-oxide-based nanorod structural sensors

International Nuclear Information System (INIS)

Lin, Tzu-Shun; Lee, Ching-Ting; Lee, Hisn-Ying; Lin, Chih-Chien

2012-01-01

Employing self-shadowing traits of an oblique-angle electron-beam deposition system, various indium tin oxide (ITO) nanorod arrays were deposited on a silicon substrate and used as extended-gate field-effect-transistor (EGFET) pH sensors. The length and morphology of the deposited ITO nanorod arrays could be changed and controlled under different deposition conditions. The ITO nanorod structural EGFET pH sensors exhibited high sensing performances owing to the larger sensing surface area. The sensitivity of the pH sensors with 150-nm-length ITO nanorod arrays was 53.96 mV/pH. By using the photoelectrochemical treatment of the ITO nanorod arrays, the sensitivity of the pH sensors with 150-nm-length passivated ITO nanorod arrays was improved to 57.21 mV/pH.

Performance of dye-sensitized solar cells with various carbon nanotube counter electrodes

International Nuclear Information System (INIS)

Zhang, D.; Li, X.; Chen, S.; Sun, Z.; Huang, S.; Yin, X.J.

2011-01-01

Double-wall carbon nanotubes (DWCNTs), single-wall carbon nanotubes (SWCNTs), and multi-wall carbon nanotubes (MWCNTs) were investigated as an alternative for platinum in counter-electrodes for dye-sensitized solar cells. The counter-electrodes were prepared on fluorine-doped tin oxide glass substrates by the screen printing technique from pastes of carbon nanotubes and organic binder. The solar cells were assembled from carbon nanotubes counter-electrodes and screen printed anodes made from titanium dioxide. The cells produced with DWCNTs, SWCNTs or MWCNTs have overall conversion efficiencies of 8.0%, 7.6% and 7.1%, respectively. Electrochemical impedance spectroscopy measurements revealed that DWCNTs displayed the highest catalytic activity for the reduction of tri-iodide ions. The large surface area and superior chemical stability of the DWCNTs facilitated the electron-transfer kinetics at the interface between counter-electrode and electrolyte and yielded the lowest transfer resistance, thereby improving the photovoltaic activity. A short-term stability test at moderate conditions confirmed the robustness of solar cells based on the use of DWCNTs, SWCNTs or MWCNTs. (author)

Porosimetry and packing morphology of vertically-aligned carbon nanotube arrays via impedance spectroscopy.

Science.gov (United States)

Mutha, Heena K; Lu, Yuan; Stein, Itai; Cho, H Jeremy; Suss, Matthew; Laoui, Tahar; Thompson, Carl; Wardle, Brian; Wang, Evelyn

2016-12-13

Vertically aligned one-dimensional nanostructure arrays are promising in many applications such as electrochemical systems, solar cells, and electronics, taking advantage of high surface area per unit volume, nanometer length scale packing, and alignment leading to high conductivity. However, many devices need to optimize arrays for device performance by selecting an appropriate morphology. Developing a simple, non-invasive tool for understanding the role of pore volume distribution and interspacing would aid in the optimization of nanostructure morphologies in electrodes. In this work, we combined electrochemical impedance spectroscopy (EIS) with capacitance measurements and porous electrode theory to conduct in situ porosimetry of vertically-aligned carbon nanotubes (VA-CNTs) non-destructively. We utilized the EIS measurements with a pore size distribution model to quantify the average and dispersion of inter-CNT spacing (Γ), stochastically, in carpets that were mechanically densified from 1.7 × 1010 tubes/cm2 to 4.5 × 1011 tubes/cm2. Our analysis predicts that the inter-CNT spacing ranges from over 100 ± 50 nm in sparse carpets to sub 10 ± 5 nm in packed carpets. Our results suggest that waviness of CNTs leads to variations in the inter-CNT spacing, which can be significant in sparse carpets. This methodology can be used to predict the performance of many nanostructured devices, including supercapacitors, batteries, solar cells, and semiconductor electronics. Copyright 2016 IOP Publishing Ltd.

Stationary chest tomosynthesis using a carbon nanotube x-ray source array: a feasibility study

International Nuclear Information System (INIS)

Shan, Jing; Lee, Yueh Z; Lu, Jianping; Zhou, Otto; Tucker, Andrew W; Heath, Michael D; Wang, Xiaohui; Foos, David H

2015-01-01

Chest tomosynthesis is a low-dose, quasi-3D imaging modality that has been demonstrated to improve the detection sensitivity for small lung nodules, compared to 2D chest radiography. The purpose of this study is to investigate the feasibility and system requirements of stationary chest tomosynthesis (s-DCT) using a spatially distributed carbon nanotube (CNT) x-ray source array, where the projection images are collected by electronically activating individual x-ray focal spots in the source array without mechanical motion of the x-ray source, detector, or the patient. A bench-top system was constructed using an existing CNT field emission source array and a flat panel detector. The tube output, beam quality, focal spot size, system in-plane and in-depth resolution were characterized. Tomosynthesis slices of an anthropomorphic chest phantom were reconstructed for image quality assessment. All 75 CNT sources in the source array were shown to operate reliably at 80 kVp and 5 mA tube current. Source-to-source consistency in the tube current and focal spot size was observed. The incident air kerma reading per mAs was measured as 74.47 uGy mAs −1 at 100 cm. The first half value layer of the beam was 3 mm aluminum. An average focal spot size of 2.5  ×  0.5 mm was measured. The system MTF was measured to be 1.7 cycles mm −1 along the scanning direction, and 3.4 cycles mm −1 perpendicular to the scanning direction. As the angular coverage of 11.6°–34°, the full width at half maximum of the artifact spread function improved greatly from 9.5 to 5.2 mm. The reconstructed tomosynthesis slices clearly show airways and pulmonary vascular structures in the anthropomorphic lung phantom. The results show the CNT source array is capable of generating sufficient dose for chest tomosynthesis imaging. The results obtained so far suggest an s-DCT using a distributed CNT x-ray source array is feasible. (paper)

Ultrasound enhanced release of therapeutics from drug-releasing implants based on titania nanotube arrays.

Science.gov (United States)

Aw, Moom Sinn; Losic, Dusan

2013-02-25

A non-invasive and external stimulus-driven local drug delivery system (DDS) based on titania nanotube (TNT) arrays loaded with drug encapsulated polymeric micelles as drug carriers and ultrasound generator is described. Ultrasound waves (USW) generated by a pulsating sonication probe (Sonotrode) in phosphate buffered saline (PBS) at pH 7.2 as the medium for transmitting pressure waves, were used to release drug-loaded nano-carriers from the TNT arrays. It was demonstrated that a very rapid release in pulsatile mode can be achieved, controlled by several parameters on the ultrasonic generator. This includes pulse length, time, amplitude and power intensity. By optimization of these parameters, an immediate drug-micelles release of 100% that spans a desirable time of 5-50 min was achieved. It was shown that stimulated release can be generated and reproduced at any time throughout the TNT-Ti implant life, suggesting considerable potential of this approach as a feasible and tunable ultrasound-mediated drug delivery system in situ via drug-releasing implants. It is expected that this concept can be translated from an in vitro to in vivo regime for therapeutic applications using drug-releasing implants in orthopedic and coronary stents. Crown Copyright © 2013. Published by Elsevier B.V. All rights reserved.

Co(OH)2/RGO/NiO sandwich-structured nanotube arrays with special surface and synergistic effects as high-performance positive electrodes for asymmetric supercapacitors

Science.gov (United States)

Xu, Han; Zhang, Chi; Zhou, Wen; Li, Gao-Ren

2015-10-01

High power density, high energy density and excellent cycling stability are the main requirements for high-performance supercapacitors (SCs) that will be widely used for portable consumer electronics and hybrid electric vehicles. Here we investigate novel types of hybrid Co(OH)2/reduced graphene oxide (RGO)/NiO sandwich-structured nanotube arrays (SNTAs) as positive electrodes for asymmetric supercapacitors (ASCs). The synthesized Co(OH)2/RGO/NiO SNTAs exhibit a significantly improved specific capacity (~1470 F g-1 at 5 mV s-1) and excellent cycling stability with ~98% Csp retention after 10 000 cycles because of the fast transport and short diffusion paths for electroactive species, the high utilization rate of electrode materials, and special synergistic effects among Co(OH)2, RGO, and NiO. The high-performance ASCs are assembled using Co(OH)2/RGO/NiO SNTAs as positive electrodes and active carbon (AC) as negative electrodes, and they exhibit a high energy density (115 Wh kg-1), a high power density (27.5 kW kg-1) and an excellent cycling stability (less 5% Csp loss after 10 000 cycles). This study shows an important breakthrough in the design and fabrication of multi-walled hybrid nanotube arrays as positive electrodes for ASCs.High power density, high energy density and excellent cycling stability are the main requirements for high-performance supercapacitors (SCs) that will be widely used for portable consumer electronics and hybrid electric vehicles. Here we investigate novel types of hybrid Co(OH)2/reduced graphene oxide (RGO)/NiO sandwich-structured nanotube arrays (SNTAs) as positive electrodes for asymmetric supercapacitors (ASCs). The synthesized Co(OH)2/RGO/NiO SNTAs exhibit a significantly improved specific capacity (~1470 F g-1 at 5 mV s-1) and excellent cycling stability with ~98% Csp retention after 10 000 cycles because of the fast transport and short diffusion paths for electroactive species, the high utilization rate of electrode materials, and

Polypyrrole/titanium oxide nanotube arrays composites as an active material for supercapacitors.

Science.gov (United States)

Kim, Min Seok; Park, Jong Hyeok

2011-05-01

The authors present the first reported use of vertically oriented titanium oxide nanotube/polypyrrole (PPy) nanocomposites to increase the specific capacitance of TiO2 based energy storage devices. To increase their electrical storage capacity, titanium oxide nanotubes were coated with PPy and their morphologies were characterized. The incorporation of PPy increased the specific capacitance of the titanium oxide nanotube based supercapacitor system, due to their increased surface area and additional pseudo-capacitance.

Production of vertical arrays of small diameter single-walled carbon nanotubes

Science.gov (United States)

Hauge, Robert H; Xu, Ya-Qiong

2013-08-13

A hot filament chemical vapor deposition method has been developed to grow at least one vertical single-walled carbon nanotube (SWNT). In general, various embodiments of the present invention disclose novel processes for growing and/or producing enhanced nanotube carpets with decreased diameters as compared to the prior art.

Self-ordering anodized nanotubes: Enhancing the performance by surface plasmon for dye-sensitized solar cell

Energy Technology Data Exchange (ETDEWEB)

Agarwala, S., E-mail: agarwala.shweta@gmail.com [Department of Electrical and Computer Engineering, National University of Singapore, 4 Engineering Drive, Singapore 117576 (Singapore); Ho, G.W. [Department of Electrical and Computer Engineering, National University of Singapore, 4 Engineering Drive, Singapore 117576 (Singapore)

2012-05-15

In the present work, electrochemical anodization has been used to prepare uniform TiO{sub 2} nanotube array photoelectrode. The average internal diameter, tube length and wall thickness of the optimized morphology is {approx}180 nm, 14 {mu}m and 10 nm, respectively. It was found that the tube diameter increases with the anodization voltage. Diffraction data reveals that the nanotubes consist solely of anatase phase. Back illuminated geometry of dye-sensitized solar cell (DSSC), with nanotubes grown at 60 V for 2 h, gave a cell performance of 4.5%. TiO{sub 2} nanotubes are loaded with silver (Ag) nanoparticles synthesized by a hydrothermal route. The Ag particle size is controlled resulting in solar conversion efficiency to increase by 22%. The DSSC based on TiO{sub 2} nanotube with Ag nanoparticles shows power conversion efficiency of 5.5%. Detailed characterization are performed, presented and discussed. - Graphical abstract: Enhanced solar conversion efficiency of dye-sensitized solar cells by decorating TiO{sub 2} nanotube array with Ag nanoparticles. Highlights: Black-Right-Pointing-Pointer Uniform array of TiO{sub 2} nanotubes synthesized via electrochemical anodization. Black-Right-Pointing-Pointer Back illuminated DSSC gave a cell performance of 4.5%. Black-Right-Pointing-Pointer TiO{sub 2} nanotubes are loaded with Ag nanoparticles, which increased the power conversion efficiency to 5.5%.

Functional nanostructured titanium nitride films obtained by sputtering magnetron

International Nuclear Information System (INIS)

Sanchez, O.; Hernandez-Velez, M.; Navas, D.; Auger, M.A.; Baldonedo, J.L.; Sanz, R.; Pirota, K.R.; Vazquez, M.

2006-01-01

Development of new methods in the formation of hollow structures, in particular, nanotubes and nanocages are currently generating a great interest as a consequence of the growing relevance of these nanostructures on many technological fields, ranging from optoelectronics to biotechnology. In this work, we report the formation of titanium nitride (TiN) nanotubes and nanohills via reactive sputtering magnetron processes. Anodic Alumina Membranes (AAM) were used as template substrates to grow the TiN nanostructures. The AAM were obtained through electrochemical anodization processes by using oxalic acid solutions as electrolytes. The nanotubes were produced at temperatures below 100 deg. C, and using a pure titanium (99.995%) sputtering target and nitrogen as reactive gas. The obtained TiN thin films showed surface morphologies adjusted to pore diameter and interpore distance of the substrates, as well as ordered arrays of nanotubes or nanohills depending on the sputtering and template conditions. High Resolution Scanning Electron Microscopy (HRSEM) was used to elucidate both the surface order and morphology of the different grown nanostructures. The crystalline structure of the samples was examined using X-ray Diffraction (XRD) patterns and their qualitative chemical composition by using X-ray Energy Dispersive Spectroscopy (XEDS) in a scanning electron microscopy

Bifacial dye-sensitized solar cells based on vertically oriented TiO2 nanotube arrays

International Nuclear Information System (INIS)

Liu Zhaoyue; Misra, Mano

2010-01-01

In this work we describe a novel bifacial design concept for dye-sensitized solar cells (DSCs). Bifacial DSCs are fabricated with ruthenium complex chemisorbed double-sided TiO 2 nanotube arrays on a Ti metal substrate, in combination with two electron-collecting counter electrodes. Our investigation shows that the present bifacial DSCs have similar conversion efficiencies when illuminated from either their front or rear side, and a summated output power when illuminated on both sides. Furthermore, this type of bifacial DSC is also able to summate the output power of each side when working at an 'unsymmetrical' mode, in which much different output powers are generated by the front and rear sides. Therefore, this bifacial design concept exhibits a promising potential to reduce the cost of solar electricity when DSCs are operated at a location where a high albedo radiation is available.

Investigation of anodic TiO2 nanotube composition with high spatial resolution AES and ToF SIMS

Science.gov (United States)

Dronov, Alexey; Gavrilin, Ilya; Kirilenko, Elena; Dronova, Daria; Gavrilov, Sergey

2018-03-01

High resolution Scanning Auger Electron Spectroscopy (AES) and Time-of-Flight Secondary Ion Mass-Spectrometry (ToF SIMS) were used to investigate structure and elemental composition variation of both across an array of TiO2 nanotubes (NTs) and single tube of an array. The TiO2 NT array was grown by anodic oxidation of Ti foil in fluorine-containing ethylene glycol electrolyte. It was found that the studied anodic TiO2 nanotubes have a layered structure with rather sharp interfaces. The differences in AES depth profiling results of a single tube with the focused primary electron beam (point analysis) and over an area of 75 μm in diameter of a nanotube array with the defocused primary electron beam are discussed. Depth profiling by ToF SIMS was carried out over approximately the same size of a nanotube array to determine possible ionic fragments in the structure. The analysis results show that the combination of both mentioned methods is useful for a detailed analysis of nanostructures with complex morphology and multi-layered nature.

Flexible symmetric supercapacitors based on vertical TiO2 and carbon nanotubes

Science.gov (United States)

Chien, C. J.; Chang, Pai-Chun; Lu, Jia G.

2010-03-01

Highly conducting and porous carbon nanotubes are widely used as electrodes in double-layer-effect supercapacitors. In this presentation, vertical TiO2 nanotube array is fabricated by anodization process and used as supercapacitor electrode utilizing its compact density, high surface area and porous structure. By spin coating carbon nanotube networks on vertical TiO2 nanotube array as electrodes with 1M H2SO4 electrolyte in between, the specific capacitance can be enhanced by 30% compared to using pure carbon nanotube network alone because of the combination of double layer effect and redox reaction from metal oxide materials. Based on cyclic voltammetry and galvanostatic charge-discharge measurements, this type of hybrid electrode has proven to be suitable for high performance supercapacitor application and maintain desirable cycling stability. The electrochemical impedance spectroscopy technique shows that the electrode has good electrical conductivity. Furthermore, we will discuss the prospect of extending this energy storage approach in flexible electronics.

Effect of TiO2 nanotube length and lateral tubular spacing on ...

Indian Academy of Sciences (India)

Abstract. The main objective of this study is to show the effect of TiO2 nanotube length, diameter and intertubular ... formation of nanotube arrays spread uniformly over a large area. ... 36, 48 and 72 h at an applied voltage of 40 V. The anodized ... and phase analysis for the obtained nanotubes were done .... Using an extra-.

Laser Processing of Carbon Nanotube Transparent Conducting Films

Science.gov (United States)

Mann, Andrew

Transparent conducting films, or TCFs, are 2D electrical conductors with the ability to transmit light. Because of this, they are used in many popular electronics including smart phones, tablets, solar panels, and televisions. The most common material used as a TCF is indium tin oxide, or ITO. Although ITO has great electrical and optical characteristics, it is expensive, brittle, and difficult to pattern. These limitations have led researchers toward other materials for the next generation of displays and touch panels. The most promising material for next generation TCFs is carbon nanotubes, or CNTs. CNTs are cylindrical tubes of carbon no more than a few atoms thick. They have different electrical and optical properties depending on their atomic structure, and are extremely strong. As an electrode, they conduct electricity through an array of randomly dispersed tubes. The array is highly transparent because of gaps between the tubes, and size and optical properties of the CNTs. Many research groups have tried making CNT TCFs with opto-electric properties similar to ITO but have difficultly achieving high conductivity. This is partly attributed to impurities from fabrication and a mix of different tube types, but is mainly caused by low junction conductivity. In functionalized nanotubes, junction conductivity is impaired by covalently bonded molecules added to the sidewalls of the tubes. The addition of this molecule, known as functionalization, is designed to facilitate CNT dispersion in a solvent by adding properties of the molecule to the CNTs. While necessary for a good solution, functionalization decreases the conductivity in the CNT array by creating defects in the tube's structures and preventing direct inter-carbon bonding. This research investigates removing the functional coating (after tube deposition) by laser processing. Laser light is able to preferentially heat the CNTs because of their optical and electrical properties. Through local conduction

Carbon nanotube transistors scaled to a 40-nanometer footprint.

Science.gov (United States)

Cao, Qing; Tersoff, Jerry; Farmer, Damon B; Zhu, Yu; Han, Shu-Jen

2017-06-30

The International Technology Roadmap for Semiconductors challenges the device research community to reduce the transistor footprint containing all components to 40 nanometers within the next decade. We report on a p-channel transistor scaled to such an extremely small dimension. Built on one semiconducting carbon nanotube, it occupies less than half the space of leading silicon technologies, while delivering a significantly higher pitch-normalized current density-above 0.9 milliampere per micrometer at a low supply voltage of 0.5 volts with a subthreshold swing of 85 millivolts per decade. Furthermore, we show transistors with the same small footprint built on actual high-density arrays of such nanotubes that deliver higher current than that of the best-competing silicon devices under the same overdrive, without any normalization. We achieve this using low-resistance end-bonded contacts, a high-purity semiconducting carbon nanotube source, and self-assembly to pack nanotubes into full surface-coverage aligned arrays. Copyright © 2017 The Authors, some rights reserved; exclusive licensee American Association for the Advancement of Science. No claim to original U.S. Government Works.

Crystallization Behavior of Poly(ethylene oxide) in Vertically Aligned Carbon Nanotube Array.

Science.gov (United States)

Sheng, Jiadong; Zhou, Shenglin; Yang, Zhaohui; Zhang, Xiaohua

2018-03-27

We investigate the effect of the presence of vertically aligned multiwalled carbon nanotubes (CNTs) on the orientation of poly(ethylene oxide) (PEO) lamellae and PEO crystallinity. The high alignment of carbon nanotubes acting as templates probably governs the orientation of PEO lamellae. This templating effect might result in the lamella planes of PEO crystals oriented along a direction parallel to the long axis of the nanotubes. The presence of aligned carbon nanotubes also gives rise to the decreases in PEO crystallinity, crystallization temperature, and melting temperature due to the perturbation of carbon nanotubes to the crystallization of PEO. These effects have significant implications for controlling the orientation of PEO lamellae and decreasing the crystallinity of PEO and thickness of PEO lamellae, which have significant impacts on ion transport in PEO/CNT composite and the capacitive performance of PEO/CNT composite. Both the decreased PEO crystallinity and the orientation of PEO lamellae along the long axes of vertically aligned CNTs give rise to the decrease in the charge transfer resistance, which is associated with the improvements in the ion transport and capacitive performance of PEO/CNT composite.

A photoelectrochemical study of CdS modified TiO2 nanotube arrays as photoanodes for cathodic protection of stainless steel

International Nuclear Information System (INIS)

L, Jing; Lin Changjian; Li Juntao; Lin Zequan

2011-01-01

An electrodeposited CdS nanoparticles-modified highly-ordered TiO 2 nanotube arrays (CdS-TNs) photoelectrode and its performance of photocathodic protection are reported. The self-organized TiO 2 nanotube arrays are fabricated by electrochemical anodization in an organic-inorganic mixed electrolyte and sensitized with CdS nanoparticles by electrodeposition via a single-step direct current. The morphology, crystalline phase, and composition of the CdS-TNs films were characterized systematically by scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and ultraviolet-visible (UV-Vis) spectroscopy, respectively. The photoelectrochemical performances of the CdS-TNs film under illumination and dark conditions in 0.5 M NaCl solution were evaluated through the electrochemical measurements. It is indicated that the TNs incorporated by CdS effectively harvest solar light in the UV as well as the visible light (up to 480 nm) region. It is supposed that the high photoelectro-response activity of the CdS-TNs is attributed to the increased efficiency of charge separation and transport of electrons. The electrode potentials of 304 stainless steel coupled with the CdS-TNs is found to be negatively shifted for about 246 mV and 215 mV under UV and white light irradiation, respectively, which can be remained for 24 h even in darkness. It is implied that the CdS-TNs are able to effectively function a photogenerated cathodic protection for metals both under the UV and visible light illumination.

TiN nanoparticles on CNT-graphene hybrid support as noble-metal-free counter electrode for quantum-dot-sensitized solar cells.

Science.gov (United States)

Youn, Duck Hyun; Seol, Minsu; Kim, Jae Young; Jang, Ji-Wook; Choi, Youngwoo; Yong, Kijung; Lee, Jae Sung

2013-02-01

The development of an efficient noble-metal-free counter electrode is crucial for possible applications of quantum-dot-sensitized solar cells (QDSSCs). Herein, we present TiN nanoparticles on a carbon nanotube (CNT)-graphene hybrid support as a noble-metal-free counter electrode for QDSSCs employing a polysulfide electrolyte. The resulting TiN/CNT-graphene possesses an extremely high surface roughness, a good metal-support interaction, and less aggregation relative to unsupported TiN; it also has superior solar power conversion efficiency (4.13 %) when applying a metal mask, which is much higher than that of the state-of-the-art Au electrode (3.35 %). Based on electrochemical impedance spectroscopy measurements, the enhancement is ascribed to a synergistic effect between TiN nanoparticles and the CNT-graphene hybrid, the roles of which are to provide active sites for the reduction of polysulfide ions and electron pathways to TiN nanoparticles, respectively. The combination of graphene and CNTs leads to a favorable morphology that prevents stacking of graphene or bundling of CNTs, which maximizes the contact of the support with TiN nanoparticles and improves electron-transfer capability relative to either carbon material alone. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Carbon Micronymphaea: Graphene on Vertically Aligned Carbon Nanotubes

Directory of Open Access Journals (Sweden)

Jong Won Choi

2013-01-01

Full Text Available This paper describes the morphology of carbon nanomaterials such as carbon nanotube (CNT, graphene, and their hybrid structure under various operating conditions during a one-step synthesis via plasma-enhanced chemical vapor deposition (PECVD. We focus on the synthetic aspects of carbon hybrid material composed of heteroepitaxially grown graphene on top of a vertical array of carbon nanotubes, called carbon micronymphaea. We characterize the structural features of this unique nanocomposite by uses of electron microscopy and micro-Raman spectroscopy. We observe carbon nanofibers, poorly aligned and well-aligned vertical arrays of CNT sequentially as the growth temperature increases, while we always discover the carbon hybrids, called carbon micronymphaea, at specific cooling rate of 15°C/s, which is optimal for the carbon precipitation from the Ni nanoparticles in this study. We expect one-pot synthesized graphene-on-nanotube hybrid structure poses great potential for applications that demand ultrahigh surface-to-volume ratios with intact graphitic nature and directional electronic and thermal transports.

Robust non-carbon titanium nitride nanotubes supported Pt catalyst with enhanced catalytic activity and durability for methanol oxidation reaction

International Nuclear Information System (INIS)

Xiao, Yonghao; Zhan, Guohe; Fu, Zhenggao; Pan, Zhanchang; Xiao, Chumin; Wu, Shoukun; Chen, Chun; Hu, Guanghui; Wei, Zhigang

2014-01-01

By the combination of solvothermal alcoholysis and post-nitriding method, titanium nitride nanotubes (TiN NTs), with high surface area, hollow and interior porous structure are prepared successfully and used at a support for Pt nanoparticles. The TiN NTs supported Pt (Pt/TiN NTs) catalyst displays enhanced activity and durability towards methanol oxidation reaction (MOR) compared with the commercial Pt/C (E-TEK) catalyst. X ray diffraction (XRD), nitrogen adsorption/desorption, transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) measurements are performed to investigate the physicochemical properties of the synthesized catalyst. SEM and TEM images reveal that the wall of the TiN NTs is porous and Pt nanoparticles supported on the dendritic TiN nanocrystals exhibit small size and good dispersion. Effects of inherent corrosion-resistant, tubular and porous nanostructures and electron transfer due to the strong metal–support interactions of TiN NTs contribute to the enhanced catalytic activity and stability of Pt/TiN NTs towards the MOR

Controlled Directional Growth of TiO2 Nanotubes

DEFF Research Database (Denmark)

In, Su-il; Hou, Yidong; Abrams, Billie

2010-01-01

We demonstrate how the anodization direction and growth rate of vertically aligned, highly ordered TiO2 nanotube (NT) arrays can be controlled and manipulated by the local concentration of O-2 in the electrolyte. This leads to the growth of highly active TiO2 NT arrays directly on nonconducting s...

Angular dependent anisotropic terahertz response of vertically aligned multi-walled carbon nanotube arrays with spatial dispersion

Science.gov (United States)

Zhou, Yixuan; Yiwen, E.; Xu, Xinlong; Li, Weilong; Wang, Huan; Zhu, Lipeng; Bai, Jintao; Ren, Zhaoyu; Wang, Li

2016-12-01

Spatial dispersion effect of aligned carbon nanotubes (CNTs) in the terahertz (THz) region has significance for both theoretical and applied consideration due to the unique intrinsically anisotropic physical properties of CNTs. Herein, we report the angular dependent reflection of p-polarized THz wave from vertically aligned multi-walled CNT arrays in both experiment and theory. The spectra indicate that the reflection depends on the film thickness of vertically aligned CNTs, the incident angle, and the frequency. The calculation model is based on the spatial dispersion effect of aligned CNTs and performed with effective impedance method and the Maxwell-Garnett approximation. The results fit well with the experiment when the thickness of CNT film is thin, which reveals a coherent superposition mechanism of the CNT surface reflection and CNTs/Si interface reflection. For thick CNT films, the CNTs/Si interface response determines the reflection at small incident angles, while the CNTs surface effect dominates at large incident angles. This work investigates the spatial dispersion effect of vertically aligned CNT arrays in the THz region, and paves a way for potential anisotropic THz applications based on CNTs with oblique incidence requirements.

Self-assembly graphitic carbon nitride quantum dots anchored on TiO_2 nanotube arrays: An efficient heterojunction for pollutants degradation under solar light

International Nuclear Information System (INIS)

Su, Jingyang; Zhu, Lin; Geng, Ping; Chen, Guohua

2016-01-01

Highlights: • Carbon nitride quantum dots (CNQDs) were decorated onto TiO_2 nanotube arrays (NTAs). • The CNQDs/TiO_2 NTAs exhibits much improved photoelectrochemical activity. • The heterojunction displays efficient removal efficiencies for RhB and phenol. • Pollutants degradation mechanism over CNQDs/TiO_2 NTAs was clarified. - Abstract: In this study, an efficient heterojunction was constructed by anchoring graphitic carbon nitride quantum dots onto TiO_2 nanotube arrays through hydrothermal reaction strategy. The prepared graphitic carbon nitride quantum dots, which were prepared by solid-thermal reaction and sequential dialysis process, act as a sensitizer to enhance light absorption. Furthermore, it was demonstrated that the charge transfer and separation in the formed heterojunction were significantly improved compared with pristine TiO_2. The prepared heterojunction was used as a photoanode, exhibiting much improved photoelectrochemical capability and excellent photo-stability under solar light illumination. The photoelectrocatalytic activities of prepared heterojunction were demonstrated by degradation of RhB and phenol in aqueous solution. The kinetic constants of RhB and phenol degradation using prepared photoelectrode are 2.4 times and 4.9 times higher than those of pristine TiO_2, respectively. Moreover, hydroxyl radicals are demonstrated to be dominant active radicals during the pollutants degradation.

Studies on Cementation of Tin on Copper and Tin Stripping from Copper Substrate

Directory of Open Access Journals (Sweden)

Rudnik E.

2016-06-01

Full Text Available Cementation of tin on copper in acid chloride-thiourea solutions leads to the formation of porous layers with a thickness dependent on the immersion time. The process occurs via Sn(II-Cu(I mechanism. Chemical stripping of tin was carried out in alkaline and acid solutions in the presence of oxidizing agents. It resulted in the dissolution of metallic tin, but refractory Cu3Sn phase remained on the copper surface. Electrochemical tin stripping allows complete tin removal from the copper substrate, but porosity and complex phase composition of the tin coating do not allow monitoring the process in unambiguous way.

TIN-X

DEFF Research Database (Denmark)

Cannon, Daniel C; Yang, Jeremy J; Mathias, Stephen L

2017-01-01

between proteins and diseases, based on text mining data processed from scientific literature. In the current implementation, TIN-X supports exploration of data for G-protein coupled receptors, kinases, ion channels, and nuclear receptors. TIN-X supports browsing and navigating across proteins......Motivation: The increasing amount of peer-reviewed manuscripts requires the development of specific mining tools to facilitate the visual exploration of evidence linking diseases and proteins. Results: We developed TIN-X, the Target Importance and Novelty eXplorer, to visualize the association...

Bacterial Stress and Osteoblast Responses on Graphene Oxide-Hydroxyapatite Electrodeposited on Titanium Dioxide Nanotube Arrays

Directory of Open Access Journals (Sweden)

Yardnapar Parcharoen

2017-01-01

Full Text Available To develop bone implant material with excellent antibacterial and biocompatible properties, nanotubular titanium surface was coated with hydroxyapatite (HA and graphene oxide (GO. Layer-by-layer deposition was achieved by coating HA on an anodic-grown titanium dioxide nanotube array (ATi with electrolytic deposition, followed by coating with GO using anodic-electrophoretic deposition. The antibacterial activity against both Gram-negative (Escherichia coli and Gram-positive (Staphylococcus aureus bacteria was determined based on the percentage of surviving bacteria and the amount of ribonucleic acid (RNA leakage and correlated with membrane disruption. The oxidative stress induced in both strains of bacteria by GO was determined by cyclic voltammetry and is discussed. Importantly, the antibacterial GO coatings on HA-ATi were not cytotoxic to preosteoblasts and promoted osteoblast proliferation after 5 days and calcium deposition after 21 days in standard cell culture conditions.

Growth of nanotubes and chemical sensor applications

Science.gov (United States)

Hone, James; Kim, Philip; Huang, X. M. H.; Chandra, B.; Caldwell, R.; Small, J.; Hong, B. H.; Someya, T.; Huang, L.; O'Brien, S.; Nuckolls, Colin P.

2004-12-01

We have used a number of methods to grow long aligned single-walled carbon nanotubes. Geometries include individual long tubes, dense parallel arrays, and long freely suspended nanotubes. We have fabricated a variety of devices for applications such as multiprobe resistance measurement and high-current field effect transistors. In addition, we have measured conductance of single-walled semiconducting carbon nanotubes in field-effect transistor geometry and investigated the device response to water and alcoholic vapors. We observe significant changes in FET drain current when the device is exposed to various kinds of different solvent. These responses are reversible and reproducible over many cycles of vapor exposure. Our experiments demonstrate that carbon nanotube FETs are sensitive to a wide range of solvent vapors at concentrations in the ppm range.

A novel voltammetric sensor based on carbon nanotubes and nanoparticles of antimony tin oxide for the determination of ractopamine

Energy Technology Data Exchange (ETDEWEB)

Baytak, Aysegul Kutluay; Teker, Tugce; Duzmen, Sehriban; Aslanoglu, Mehmet, E-mail: maslanoglu@harran.edu.tr

2016-02-01

An electrochemical sensor was prepared by the modification of a glassy carbon electrode (GCE) with carbon nanotubes (CNTs) and nanoparticles of antimony tin oxide (ATO). The surface layer was characterized by scanning electron microscopy (SEM), energy dispersive X-ray diffraction method (EDX) and ATR FT-IR spectroscopy. The proposed electrode was assessed in respect to the electro-oxidation of ractopamine. Compared with a bare GCE and a GCE electrode modified with CNTs, the ATONPs/CNTs/GCE exhibited a great catalytic activity towards the oxidation of ractopamine with a well-defined anodic peak at 600 mV. The current response was linear with the concentration of ractopamine over the range from 10 to 240 nM with a detection limit of 3.3 nM. The proposed electrode enabled the selective determination of ractopamine in the presence of high concentrations of ascorbic acid (AA), dopamine (DA) and uric acid (UA). The proposed electrode was successfully applied for the determination of ractopamine in feed and urine samples. The sensitive and selective determination of ractopamine makes the developed method of great interest for monitoring its therapeutic use and doping control purposes. - Highlights: • A novel voltammetric sensor was prepared using nanoparticles of ATO and CNTs. • The ATONPs/CNTs/GCE has greatly improved the voltammetry of ractopamine. • The proposed electrode enabled a detection limit of 3.3 nM. • AA, DA and UA did not interfere with the selective detection of ractopamine. • Measurements were precise and accurate.

A novel voltammetric sensor based on carbon nanotubes and nanoparticles of antimony tin oxide for the determination of ractopamine

International Nuclear Information System (INIS)

Baytak, Aysegul Kutluay; Teker, Tugce; Duzmen, Sehriban; Aslanoglu, Mehmet

2016-01-01

An electrochemical sensor was prepared by the modification of a glassy carbon electrode (GCE) with carbon nanotubes (CNTs) and nanoparticles of antimony tin oxide (ATO). The surface layer was characterized by scanning electron microscopy (SEM), energy dispersive X-ray diffraction method (EDX) and ATR FT-IR spectroscopy. The proposed electrode was assessed in respect to the electro-oxidation of ractopamine. Compared with a bare GCE and a GCE electrode modified with CNTs, the ATONPs/CNTs/GCE exhibited a great catalytic activity towards the oxidation of ractopamine with a well-defined anodic peak at 600 mV. The current response was linear with the concentration of ractopamine over the range from 10 to 240 nM with a detection limit of 3.3 nM. The proposed electrode enabled the selective determination of ractopamine in the presence of high concentrations of ascorbic acid (AA), dopamine (DA) and uric acid (UA). The proposed electrode was successfully applied for the determination of ractopamine in feed and urine samples. The sensitive and selective determination of ractopamine makes the developed method of great interest for monitoring its therapeutic use and doping control purposes. - Highlights: • A novel voltammetric sensor was prepared using nanoparticles of ATO and CNTs. • The ATONPs/CNTs/GCE has greatly improved the voltammetry of ractopamine. • The proposed electrode enabled a detection limit of 3.3 nM. • AA, DA and UA did not interfere with the selective detection of ractopamine. • Measurements were precise and accurate.

Synthesis of carbon nanotube-TiO2 nanotubular material for reversible hydrogen storage

International Nuclear Information System (INIS)

Mishra, Amrita; Banerjee, Subarna; Mohapatra, Susanta K; Graeve, Olivia A; Misra, Mano

2008-01-01

A material consisting of multi-walled carbon nanotubes (MWCNTs) and larger titania (TiO 2 ) nanotube arrays has been produced and found to be efficient for reversible hydrogen (H 2 ) storage. The TiO 2 nanotube arrays (diameter ∼60 nm and length ∼2-3 μm) are grown on a Ti substrate, and MWCNTs a few μm in length and ∼30-60 nm in diameter are grown inside these TiO 2 nanotubes using chemical vapor deposition with cobalt as a catalyst. The resulting material has been used in H 2 storage experiments based on a volumetric method using the pressure, composition, and temperature relationship of the storage media. This material can store up to 2.5 wt% of H 2 at 77 K under 25 bar with more than 90% reversibility.

Synthesis of carbon nanotube-TiO(2) nanotubular material for reversible hydrogen storage.

Science.gov (United States)

Mishra, Amrita; Banerjee, Subarna; Mohapatra, Susanta K; Graeve, Olivia A; Misra, Mano

2008-11-05

A material consisting of multi-walled carbon nanotubes (MWCNTs) and larger titania (TiO(2)) nanotube arrays has been produced and found to be efficient for reversible hydrogen (H(2)) storage. The TiO(2) nanotube arrays (diameter ∼60 nm and length ∼2-3 µm) are grown on a Ti substrate, and MWCNTs a few µm in length and ∼30-60 nm in diameter are grown inside these TiO(2) nanotubes using chemical vapor deposition with cobalt as a catalyst. The resulting material has been used in H(2) storage experiments based on a volumetric method using the pressure, composition, and temperature relationship of the storage media. This material can store up to 2.5 wt% of H(2) at 77 K under 25 bar with more than 90% reversibility.

Tin Oxide Nanorod Array-Based Electrochemical Hydrogen Peroxide Biosensor

Directory of Open Access Journals (Sweden)

Liu Jinping

2010-01-01

Full Text Available Abstract SnO2 nanorod array grown directly on alloy substrate has been employed as the working electrode of H2O2 biosensor. Single-crystalline SnO2 nanorods provide not only low isoelectric point and enough void spaces for facile horseradish peroxidase (HRP immobilization but also numerous conductive channels for electron transport to and from current collector; thus, leading to direct electrochemistry of HRP. The nanorod array-based biosensor demonstrates high H2O2 sensing performance in terms of excellent sensitivity (379 μA mM−1 cm−2, low detection limit (0.2 μM and high selectivity with the apparent Michaelis–Menten constant estimated to be as small as 33.9 μM. Our work further demonstrates the advantages of ordered array architecture in electrochemical device application and sheds light on the construction of other high-performance enzymatic biosensors.

Diameter modulation of vertically aligned single-walled carbon nanotubes.

Science.gov (United States)

Xiang, Rong; Einarsson, Erik; Murakami, Yoichi; Shiomi, Junichiro; Chiashi, Shohei; Tang, Zikang; Maruyama, Shigeo

2012-08-28

We demonstrate wide-range diameter modulation of vertically aligned single-walled carbon nanotubes (SWNTs) using a wet chemistry prepared catalyst. In order to ensure compatibility to electronic applications, the current minimum mean diameter of 2 nm for vertically aligned SWNTs is challenged. The mean diameter is decreased to about 1.4 nm by reducing Co catalyst concentrations to 1/100 or by increasing Mo catalyst concentrations by five times. We also propose a novel spectral analysis method that allows one to distinguish absorbance contributions from the upper, middle, and lower parts of a nanotube array. We use this method to quantitatively characterize the slight diameter change observed along the array height. On the basis of further investigation of the array and catalyst particles, we conclude that catalyst aggregation-rather than Ostwald ripening-dominates the growth of metal particles.

On the electrochemistry of tin oxide coated tin electrodes in lithium-ion batteries

International Nuclear Information System (INIS)

Böhme, Solveig; Edström, Kristina; Nyholm, Leif

2015-01-01

As tin based electrodes are of significant interest in the development of improved lithium-ion batteries it is important to understand the associated electrochemical reactions. In this work it is shown that the electrochemical behavior of SnO_2 coated tin electrodes can be described based on the SnO_2 and SnO conversion reactions, the lithium tin alloy formation and the oxidation of tin generating SnF_2. The CV, XPS and SEM data, obtained for electrodeposited tin crystals on gold substrates, demonstrates that the capacity loss often observed for SnO_2 is caused by the reformed SnO_2 layer serving as a passivating layer protecting the remaining tin. Capacities corresponding up to about 80 % of the initial SnO_2 capacity could, however, be obtained by cycling to 3.5 V vs. Li"+/Li. It is also shown that the oxidation of the lithium tin alloy is hindered by the rate of the diffusion of lithium through a layer of tin with increasing thickness and that the irreversible oxidation of tin to SnF_2 at potentials larger than 2.8 V vs. Li"+/Li is due to the fact that SnF_2 is formed below the SnO_2 layer. This improved electrochemical understanding of the SnO_2/Sn system should be valuable in the development of tin based electrodes for lithium-ion batteries.

Single walled carbon nanotubes functionally adsorbed to biopolymers for use as chemical sensors

Science.gov (United States)

Johnson, Jr., Alan T.; Gelperin, Alan [Princeton, NJ; Staii, Cristian [Madison, WI

2011-07-12

Chemical field effect sensors comprising nanotube field effect devices having biopolymers such as single stranded DNA functionally adsorbed to the nanotubes are provided. Also included are arrays comprising the sensors and methods of using the devices to detect volatile compounds.

Investigation of Chirality Selection Mechanism of Single-Walled Carbon Nanotube

Science.gov (United States)

2015-07-17

Final 3. DATES COVERED (From - To) 01-June-2014 to 31-May-2015 4. TITLE AND SUBTITLE Investigation of Chirality Selection Mechanism of...of two significant mechanistic aspects of carbon nanotube (CNT) array growth under chemical vapor deposition conditions: chirality selectivity and...affected by the morphological evolution of catalyst particles. 15. SUBJECT TERMS Carbon Nanotubes, Chirality , Processing, Catalysis

A photoelectrochemical study of CdS modified TiO{sub 2} nanotube arrays as photoanodes for cathodic protection of stainless steel

Energy Technology Data Exchange (ETDEWEB)

L, Jing; Lin Changjian, E-mail: cjlin@xmu.edu.cn; Li Juntao; Lin Zequan

2011-06-01

An electrodeposited CdS nanoparticles-modified highly-ordered TiO{sub 2} nanotube arrays (CdS-TNs) photoelectrode and its performance of photocathodic protection are reported. The self-organized TiO{sub 2} nanotube arrays are fabricated by electrochemical anodization in an organic-inorganic mixed electrolyte and sensitized with CdS nanoparticles by electrodeposition via a single-step direct current. The morphology, crystalline phase, and composition of the CdS-TNs films were characterized systematically by scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and ultraviolet-visible (UV-Vis) spectroscopy, respectively. The photoelectrochemical performances of the CdS-TNs film under illumination and dark conditions in 0.5 M NaCl solution were evaluated through the electrochemical measurements. It is indicated that the TNs incorporated by CdS effectively harvest solar light in the UV as well as the visible light (up to 480 nm) region. It is supposed that the high photoelectro-response activity of the CdS-TNs is attributed to the increased efficiency of charge separation and transport of electrons. The electrode potentials of 304 stainless steel coupled with the CdS-TNs is found to be negatively shifted for about 246 mV and 215 mV under UV and white light irradiation, respectively, which can be remained for 24 h even in darkness. It is implied that the CdS-TNs are able to effectively function a photogenerated cathodic protection for metals both under the UV and visible light illumination.

Determination of material constants of vertically aligned carbon nanotube structures in compressions

International Nuclear Information System (INIS)

Li, Yupeng; Kang, Junmo; Choi, Jae-Boong; Nam, Jae-Do; Suhr, Jonghwan

2015-01-01

Different chemical vapour deposition (CVD) fabrication conditions lead to a wide range of variation in the microstructure and morphologies of carbon nanotubes (CNTs), which actually determine the compressive mechanical properties of CNTs. However, the underlying relationship between the structure/morphology and mechanical properties of CNTs is not fully understood. In this study, we characterized and compared the structural and morphological properties of three kinds of vertically aligned carbon nanotube (VACNT) arrays from different CVD fabrication methods and performed monotonic compressive tests for each VACNT array. The compressive stress–strain responses and plastic deformation were first compared and analyzed with nanotube buckling behaviours. To quantify the compressive properties of the VACNT arrays, a strain density energy function was used to determine their intrinsic material constants. Then, the structural and morphological effects on the quantified material constants of the VACNTs were statistically investigated and analogized to cellular materials with an open-cell model. The statistical analysis shows that density, defect degree, and the moment of inertia of the CNTs are key factors in the improvement of the compressive mechanical properties of VACNT arrays. This approach could allow a model-driven CNT synthesis for engineering their mechanical behaviours. (paper)

Optimization of photoelectrochemical water splitting performance on hierarchical TiO 2 nanotube arrays

KAUST Repository

Zhang, Z.

2012-02-10

In this paper, we show that by varying the voltages during two-step anodization the morphology of the hierarchical top-layer/bottom-tube TiO 2 (TiO 2 NTs) can be finely tuned between nanoring/nanotube, nanopore/nanotube, and nanohole-nanocave/nanotube morphologies. This allows us to optimize the photoelectrochemical (PEC) water splitting performance on the hierarchical TiO 2 NTs. The optimized photocurrent density and photoconversion efficiency in this study, occurring on the nanopore/nanotube TiO 2 NTs, were 1.59 mA cm -2 at 1.23 V vs. RHE and 0.84% respectively, which are the highest values ever reported on pristine TiO 2 materials under illumination of AM 1.5G. Our findings contribute to further improvement of the energy conversion efficiency of TiO 2-based devices.

Optimization of photoelectrochemical water splitting performance on hierarchical TiO 2 nanotube arrays

KAUST Repository

Zhang, Z.; Wang, Peng

2012-01-01

In this paper, we show that by varying the voltages during two-step anodization the morphology of the hierarchical top-layer/bottom-tube TiO 2 (TiO 2 NTs) can be finely tuned between nanoring/nanotube, nanopore/nanotube, and nanohole-nanocave/nanotube morphologies. This allows us to optimize the photoelectrochemical (PEC) water splitting performance on the hierarchical TiO 2 NTs. The optimized photocurrent density and photoconversion efficiency in this study, occurring on the nanopore/nanotube TiO 2 NTs, were 1.59 mA cm -2 at 1.23 V vs. RHE and 0.84% respectively, which are the highest values ever reported on pristine TiO 2 materials under illumination of AM 1.5G. Our findings contribute to further improvement of the energy conversion efficiency of TiO 2-based devices.

Co(OH)2/RGO/NiO sandwich-structured nanotube arrays with special surface and synergistic effects as high-performance positive electrodes for asymmetric supercapacitors.

Science.gov (United States)

Xu, Han; Zhang, Chi; Zhou, Wen; Li, Gao-Ren

2015-10-28

High power density, high energy density and excellent cycling stability are the main requirements for high-performance supercapacitors (SCs) that will be widely used for portable consumer electronics and hybrid electric vehicles. Here we investigate novel types of hybrid Co(OH)2/reduced graphene oxide (RGO)/NiO sandwich-structured nanotube arrays (SNTAs) as positive electrodes for asymmetric supercapacitors (ASCs). The synthesized Co(OH)2/RGO/NiO SNTAs exhibit a significantly improved specific capacity (∼1470 F g(-1) at 5 mV s(-1)) and excellent cycling stability with ∼98% Csp retention after 10 000 cycles because of the fast transport and short diffusion paths for electroactive species, the high utilization rate of electrode materials, and special synergistic effects among Co(OH)2, RGO, and NiO. The high-performance ASCs are assembled using Co(OH)2/RGO/NiO SNTAs as positive electrodes and active carbon (AC) as negative electrodes, and they exhibit a high energy density (115 Wh kg(-1)), a high power density (27.5 kW kg(-1)) and an excellent cycling stability (less 5% Csp loss after 10 000 cycles). This study shows an important breakthrough in the design and fabrication of multi-walled hybrid nanotube arrays as positive electrodes for ASCs.

Single walled carbon nanotubes with functionally adsorbed biopolymers for use as chemical sensors

Science.gov (United States)

Johnson, Jr., Alan T

2013-12-17

Chemical field effect sensors comprising nanotube field effect devices having biopolymers such as single stranded DNA or RNA functionally adsorbed to the nanotubes are provided. Also included are arrays comprising the sensors and methods of using the devices to detect volatile compounds.

Preparation, characterization and simulation studies of carbon nanotube electrodes for electrochemical energy storage

Energy Technology Data Exchange (ETDEWEB)

Meissner, Frank; Endler, Ingolf [Fraunhofer-Institut fuer Keramische Technologien und Systeme (IKTS), Dresden (Germany); Lorrmann, Henning [Fraunhofer-Institut fuer Silicatforschung (ISC), Wuerzburg (Germany); Pastewka, Lars [Fraunhofer-Institut fuer Werkstoffmechanik (IWM), Freiburg im Breisgau (Germany)

2010-07-01

Chemical Vapor Deposition (CVD) was employed to synthesize multiwalled carbon nanotubes (MWCNT) on different carrier materials for electrode applications. In the field of electrochemical energy storage it is essential to grow MWCNT on conducting substrates. For this reason titanium nitride (TiN) layers as well as a copper foil were used as substrates. The MWCNT grown on TiN layers show diameters of about 20 nm and lengths up to 13 {mu}m. In the case of copper foil substrates a remarkably higher nanotube diameter of several tens of nanometers was found. First electrochemical characterization via cyclic voltammetry shows the potential of MWCNT as electrodes for energy storage applications. The CNT were measured in an organic carbonate electrolyte vs. a lithium counter electrode with various scan rates. Until now the preliminary investigations by cyclic voltammetry for electrodes consisting of aligned MWCNT on TiN showed a capacity of around 130 F g{sup -1} in the range of 1 - 3 V vs. Li/Li{sup +}. In support of the experiments we construct a one dimensional Poisson-Nernst-Planck (PNP) continuum model that has been shown to yield agreement with corresponding molecular dynamics simulations to model ion transport into these types of electrodes. Our simulations show that first the ions accumulate at the tips of the tubes because the inner volume of the electrodes is initially field-free. A homogeneous charge distribution is then established through diffusion. The PNP model is used to compute cyclic voltammograms which show qualitative agreement with the experiments. (orig.)

Pd-MnO2 nanoparticles/TiO2 nanotube arrays (NTAs) photo-electrodes photo-catalytic properties and their ability of degrading Rhodamine B under visible light.

Science.gov (United States)

Thabit, Mohamed; Liu, Huiling; Zhang, Jian; Wang, Bing

2017-10-01

Pd-MnO 2 /TiO 2 nanotube arrays (NTAs) photo-electrodes were successfully fabricated via anodization and electro deposition subsequently; the obtained Pd-MnO 2 /TiO 2 NTAs photo electrodes were analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD) and characterized accordingly. Moreover, the light harvesting and absorption properties were investigated via ultraviolet-visible diffuse reflectance spectrum (DRS); photo degradation efficiency was investigated via analyzing the photo catalytic degradation of Rhodamine B under visible illumination (xenon light). The performed analyses illustrated that Pd-MnO 2 codoped particles were successfully deposited onto the surface of the TiO 2 nanotube arrays; DRS results showed significant improvement in visible light absorption which was between 400 and 700nm. Finally, the photo catalytic degradation efficiency results of the designated organic pollutant (Rhodamine B) illustrated a superior photocatalytic (PC) efficiency of approximately 95% compared to the bare TiO 2 NTAs, which only exhibited a photo catalytic degradation efficiency of approximately 61%, thus it indicated the significant enhancement of the light absorption properties of fabricated photo electrodes and their yield of OH radicals. Copyright © 2017. Published by Elsevier B.V.

Array of titanium dioxide nanostructures for solar energy utilization

Science.gov (United States)

Qiu, Xiaofeng; Parans Paranthaman, Mariappan; Chi, Miaofang; Ivanov, Ilia N; Zhang, Zhenyu

2014-12-30

An array of titanium dioxide nanostructures for solar energy utilization includes a plurality of nanotubes, each nanotube including an outer layer coaxial with an inner layer, where the inner layer comprises p-type titanium dioxide and the outer layer comprises n-type titanium dioxide. An interface between the inner layer and the outer layer defines a p-n junction.

Evaluation of the shear force of single cancer cells by vertically aligned carbon nanotubes suitable for metastasis diagnosis.

Science.gov (United States)

Abdolahad, M; Mohajerzadeh, S; Janmaleki, M; Taghinejad, H; Taghinejad, M

2013-03-01

Vertically aligned carbon nanotube (VACNT) arrays have been demonstrated as probes for rapid quantifying of cancer cell deformability with high resolution. Through entrapment of various cancer cells on CNT arrays, the deflections of the nanotubes during cell deformation were used to derive the lateral cell shear force using a large deflection mode method. It is observed that VACNT beams act as sensitive and flexible agents, which transfer the shear force of cells trapped on them by an observable deflection. The metastatic cancer cells have significant deformable structures leading to a further cell traction force (CTF) than primary cancerous one on CNT arrays. The elasticity of different cells could be compared by their CTF measurement on CNT arrays. This study presents a nanotube-based methodology for quantifying the single cell mechanical behavior, which could be useful for understanding the metastatic behavior of cells.

Selective growth of carbon nanotube on silicon substrates

Institute of Scientific and Technical Information of China (English)

ZOU Xiao-ping; H. ABE; T. SHIMIZU; A. ANDO; H. TOKUMOT; ZHU Shen-ming; ZHOU Hao-shen

2006-01-01

The carbon nanotube (CNT) growth of iron oxide-deposited trench-patterns and the locally-ordered CNT arrays on silicon substrate were achieved by simple thermal chemical vapor deposition(STCVD) of ethanol vapor. The CNTs were uniformly synthesized with good selectivity on trench-patterned silicon substrates. This fabrication process is compatible with currently used semiconductor-processing technologies,and the carbon-nanotube fabrication process can be widely applied for the development of electronic devices using carbon-nanotube field emitters as cold cathodes and can revolutionize the area of field-emitting electronic devices. The site-selective growth of CNT from an iron oxide nanoparticle catalyst patterned were also achieved by drying-mediated self-assembly technique. The present method offers a simple and cost-effective method to grow carbon nanotubes with self-assembled patterns.

Synthesis and structural determination of twisted MoS2 nanotubes

International Nuclear Information System (INIS)

Santiago, P.; Schabes-Retchkiman, P.; Ascencio, J.A.; Mendoza, D.; Perez-Alvarez, M.; Espinosa, A.; Reza-SanGerman, C.; Camacho-Bragado, G.A.; Jose-Yacaman, M.

2004-01-01

In the present work we report the synthesis of MoS 2 nanotubes with diameters greater than 10 nm using a template method. The length and properties of these nanotubes are a direct result of the preparation method. High-resolution transmission electron microscopy is used to study the structure of these highly curved entities. Molecular dynamics simulations of MoS 2 nanotubes reveal that one of the stable forms of the nanotubes is a twisted one. The twisting of the nanotubes produces a characteristic contrast in the images, which is also studied using simulation methods. The analysis of the local contrast close to the perpendicular orientation shows geometrical arrays of dots in domain-like structures, which are demonstrated to be a product of the atomic overlapping of irregular curvatures in the nanotubes. The configuration of some of the experimentally obtained nanotubes is demonstrated to be twisted with a behavior suggesting partial plasticity. (orig.)

Metal-modified and vertically aligned carbon nanotube sensors array for landfill gas monitoring applications.

Science.gov (United States)

Penza, M; Rossi, R; Alvisi, M; Serra, E

2010-03-12

Vertically aligned carbon nanotube (CNT) layers were synthesized on Fe-coated low-cost alumina substrates using radio-frequency plasma enhanced chemical vapour deposition (RF-PECVD) technology. A miniaturized CNT-based gas sensor array was developed for monitoring landfill gas (LFG) at a temperature of 150 degrees C. The sensor array was composed of 4 sensing elements with unmodified CNT, and CNT loaded with 5 nm nominally thick sputtered nanoclusters of platinum (Pt), ruthenium (Ru) and silver (Ag). Chemical analysis of multicomponent gas mixtures constituted of CO(2), CH(4), H(2), NH(3), CO and NO(2) has been performed by the array sensor responses and pattern recognition based on principal component analysis (PCA). The PCA results demonstrate that the metal-decorated and vertically aligned CNT sensor array is able to discriminate the NO(2) presence in the multicomponent mixture LFG. The NO(2) gas detection in the mixture LFG was proved to be very sensitive, e.g.: the CNT:Ru sensor shows a relative change in the resistance of 1.50% and 0.55% for NO(2) concentrations of 3.3 ppm and 330 ppb dispersed in the LFG, respectively, with a wide NO(2) gas concentration range measured from 0.33 to 3.3 ppm, at the sensor temperature of 150 degrees C. The morphology and structure of the CNT networks have been characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectroscopy. A forest-like nanostructure of vertically aligned CNT bundles in the multi-walled form appeared with a height of about 10 microm and a single-tube diameter varying in the range of 5-35 nm. The intensity ratio of the Raman spectroscopy D-peak and G-peak indicates the presence of disorder and defects in the CNT networks. The size of the metal (Pt, Ru, Ag) nanoclusters decorating the CNT top surface varies in the range of 5-50 nm. Functional characterization based on electrical charge transfer sensing mechanisms in the metal-modified CNT-chemoresistor array

Mechanochemical treatment of amorphous carbon from brown sphagnum moss for the preparation of carbon nanotubes

International Nuclear Information System (INIS)

Onishchenko, D.V.

2013-01-01

Under consideration is the mechanism of multiwalled nanotubes formation during mechanical activation of amorphous carbon synthesized by pyrolysis of sphagnum moss. The formation of nanotubes has been shown to take place in the array of carbon particles. A complex study of the sorption characteristics of carbon nanotubes has been carried out. The dependence of the sorption capacity of carbon nanotubes on their storage time, as well as the effect of the process parameters of nanotubes formation on their ability for oxidative modification, is represented. (authors)

Enhanced field emission properties of tilted graphene nanoribbons on aggregated TiO{sub 2} nanotube arrays

Energy Technology Data Exchange (ETDEWEB)

Hung, Shang-Chao, E-mail: schung99@gmail.com [Department of Information Technology & Communication, Shih Chien University Kaohsiung Campus, Neimen, Kaohsiung 845, Taiwan (China); Chen, Yu-Jyun [Graduate Institute of Electro-Optical Engineering & Department of Electronic Engineering, National Taiwan University of Science and Technology, Taipei 106, Taiwan (China)

2016-07-15

Highlights: • Graphene nanoribbons (GNBs) slanted on aggregate TiO{sub 2} nanotube (A-TNTs) as field-emitters. • Turn-on electric field and field enhancement factor β are dependent on the substrate morphology. • Various quantities of GNRs are deposited on top of A-TNTs (GNRs/A-TNTs) with different morphologies. • With an increase of GNBs compositions, the specimens' turn-on electric field is reduced to 2.8 V/μm. • The field enhancement factor increased rapidly to about 1964 with the addition of GNRs. - Abstract: Graphene nanoribbons (GNRs) slanted on aggregate TiO{sub 2} nanotube arrays (A-TNTs) with various compositions as field-emitters are reported. The morphology, crystalline structure, and composition of the as-obtained specimens were characterized by field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD) and Raman spectrometry. The dependence of the turn-on electric field and the field enhancement factor β on substrate morphology was studied. An increase of GNRs reduces the specimens’ turn-on electric field to 2.8 V/μm and the field enhancement factor increased rapidly to about 1964 with the addition of GNRs. Results show a strong dependence of the field emission on GNR composition aligned with the gradient on the top of the A-TNT substrate. Enhanced FE properties of the modified TNTs can be mainly attributed to their improved electrical properties and rougher surface morphology.

Bottom-up approach for carbon nanotube interconnects

International Nuclear Information System (INIS)

Li Jun; Ye Qi; Cassell, Alan; Ng, Hou Tee; Stevens, Ramsey; Han Jie; Meyyappan, M.

2003-01-01

We report a bottom-up approach to integrate multiwalled carbon nanotubes (MWNTs) into multilevel interconnects in silicon integrated-circuit manufacturing. MWNTs are grown vertically from patterned catalyst spots using plasma-enhanced chemical vapor deposition. We demonstrate the capability to grow aligned structures ranging from a single tube to forest-like arrays at desired locations. SiO 2 is deposited to encapsulate each nanotube and the substrate, followed by a mechanical polishing process for planarization. MWNTs retain their integrity and demonstrate electrical properties consistent with their original structure

Logic circuits based on individual semiconducting and metallic carbon-nanotube devices

International Nuclear Information System (INIS)

Ryu, Hyeyeon; Kaelblein, Daniel; Ante, Frederik; Zschieschang, Ute; Kern, Klaus; Klauk, Hagen; Weitz, R Thomas; Schmidt, Oliver G

2010-01-01

Nanoscale transistors employing an individual semiconducting carbon nanotube as the channel hold great potential for logic circuits with large integration densities that can be manufactured on glass or plastic substrates. Carbon nanotubes are usually produced as a mixture of semiconducting and metallic nanotubes. Since only semiconducting nanotubes yield transistors, the metallic nanotubes are typically not utilized. However, integrated circuits often require not only transistors, but also resistive load devices. Here we show that many of the metallic carbon nanotubes that are deposited on the substrate along with the semiconducting nanotubes can be conveniently utilized as load resistors with favorable characteristics for the design of integrated circuits. We also demonstrate the fabrication of arrays of transistors and resistors, each based on an individual semiconducting or metallic carbon nanotube, and their integration on glass substrates into logic circuits with switching frequencies of up to 500 kHz using a custom-designed metal interconnect layer.

A High Current Density Low Cost Niobium 3 Tin Titanium Doped Conductor Utilizing A Novel Internal Tin Process

International Nuclear Information System (INIS)

Bruce A Zeitlin

2005-01-01

An internal tin conductor has been developed using a Mono Element Internal Tin (MEIT) with an integral Nb barrier surrounding the Nb filaments. High current densities of 3000 A/mm2+ at 12 T and 1800 A/mm2 at 15 T have been achieved in conductors as small as 0.152 mm with the use of Nb7.5Ta filaments and Ti in the Sn core. In contrast, conductors with pure Nb and Ti in the Sn achieved 2700 A/mm2 at 12 T. Two internal fins, developed and patented on the project, were introduced into the filament array and reduced the effective filament diameter (Deff) by 38%. Additional fins will further reduce Deff The conductor was produced from 152.4 mm diameter billets to produce wire as small as 0.152 mm. The process promises be scaleable to 304 mm diameter billets yielding wire of 0.304 mm diameter. The MEIT process wire was easy to draw with relatively few breaks. The cost of this conductor in large production quantities based on the cost model presented could meet the 1.5 $/kilo amp meter(KAM) target of the HEP community

Comparative assessment of gastrointestinal irritant potency in man of tin(II) chloride and tin migrated from packaging.

Science.gov (United States)

Boogaard, Peter J; Boisset, Michel; Blunden, Steve; Davies, Scot; Ong, Teng Jin; Taverne, Jean-Pierre

2003-12-01

Tin is present in low concentrations in most canned foods and beverages, the highest levels being found in products packaged in unlacquered or partially lacquered tinplate cans. A limited number of case-reports of acute gastrointestinal disorders after consumption of food containing 100-500 mg/kg tin have been reported, but these reports suffer many insufficiencies. Controlled clinical studies on acute effects of tin migrated from packaging suggest a threshold concentration for adverse effects (AEs) of >730 mg/kg. Two separate randomised, single-centre, double-blind, crossover studies, enabling comparison of the tolerability of tin added as tin(II) chloride at concentrations of soup in 24 volunteers (Study 2) were carried out. Distribution studies were conducted to get insight in the acute AEs of low molecular weight (clear dose-response relationship was only observed when tin was added as tin(II) chloride in tomato juice. No clinically significant AEs were reported in Study 2 and comparison of the incidence of tin-related AEs showed no difference between the dose levels (including control). Tin species of low molecular weight in supernatant represented 31-32% of total tin in canned tomato soup versus 56-61% in juice freshly spiked with tin(II) chloride. Differences in the incidence of AEs following administration of tomato juice with 161 and 264 mg of tin per kg and tomato soup with 201 and 267 mg of tin per kg likely results from differences in the concentration of low molecular weight tin species and in the nature of tin complexes formed. The results of this work demonstrate that tin levels up to 267 mg/kg in canned food cause no AEs in healthy adults and support the currently proposed tin levels of 200 mg/kg and 250 mg/kg for canned beverages and canned foods, respectively, as safe levels for adults in the general population.

TiO2 Nanotubes: Recent Advances in Synthesis and Gas Sensing Properties

Directory of Open Access Journals (Sweden)

Giorgio Sberveglieri

2013-10-01

Full Text Available Synthesis—particularly by electrochemical anodization-, growth mechanism and chemical sensing properties of pure, doped and mixed titania tubular arrays are reviewed. The first part deals on how anodization parameters affect the size, shape and morphology of titania nanotubes. In the second part fabrication of sensing devices based on titania nanotubes is presented, together with their most notable gas sensing performances. Doping largely improves conductivity and enhances gas sensing performances of TiO2 nanotubes

Nanomolecular gas sensor architectures based on functionalized carbon nanotubes for vapor detection

Science.gov (United States)

Hines, Deon; Zhang, Henan; Rümmeli, Mark H.; Adebimpe, David; Akins, Daniel L.

2015-05-01

There is enormous interest in detection of simple & complex odors by mean of electronic instrumentation. Specifically, our work focuses on creating derivatized-nanotube-based "electronic noses" for the detection and identification of gases, and other materials. We have grafted single-walled carbon nanotubes (SWNTs) with an array of electron-donating and electron withdrawing moieties and have characterized some of the physicochemical properties of the modified nanotubes. Gas sensing elements have been fabricated by spin coating the functionalized nanotubes onto interdigitated electrodes (IDE's), creating an array of sensors. Each element in the sensor array can contain a different functionalized matrix. This facilitates the construction of chemical sensor arrays with high selectivity and sensitivity; a methodology that mimics the mammalian olfactory system. Exposure of these coated IDEs to organic vapors and the successful classification of the data obtained under DC monitoring, indicate that the system can function as gas sensors of high repeatability and selectivity for a wide range of common analytes. Since the detection of explosive materials is also of concern in this research, our next phase focuses on explosives such as, TNT, RDX, and Triacetone Triperoxide (TATP). Sensor data from individual detection are assessed on their own individual merits, after which they are amalgamated and reclassified to present each vapor as unique data point on a 2-dimensional map and with minimum loss of information. This approach can assist the nation's need for a technology to defeat IEDs through the use of methods that detect unique chemical signatures associated with explosive molecules and byproducts.

Hydrolysis of bis(dimethylamido)tin to tin (II) oxyhydroxide and its selective transformation into tin (II) or tin (IV) oxide

KAUST Repository

Khanderi, Jayaprakash

2015-03-01

Sn6O4(OH)4, a hydrolysis product of Sn(NMe2)2, is transformed to tin (II) or tin (IV) oxide by solid and solution phase processing. Tin (II) oxide is formed by heating Sn6O4(OH)4 at ≤200 °C in air or under inert atmosphere. Tin (IV) oxide nanoparticles are formed in the presence of a carboxylic acid and base in air at room temperature. IR spectroscopy, Raman spectroscopy, thermogravimetry (coupled with infrared spectroscopy), powder X-ray diffraction, high temperature X-ray diffraction, scanning electron and transmission electron microscopy are used for the characterization of Sn6O4(OH)4 and the investigation of its selective decomposition into SnO or SnO2. Spectroscopic and X-ray diffraction results indicate that SnO is formed by the removal of water from crystalline Sn6O4(OH)4. SEM shows octahedral morphology of the Sn6O4(OH)4, SnO and SnO2 with particle size from 400 nm-2 μm during solid state conversion. Solution phase transformation of Sn6O4(OH)4 to SnO2 occurs in the presence of potassium glutarate and oxygen. SnO2 particles are 15-20 nm in size.

Electrochemical synthesis of self-organized TiO2 crystalline nanotubes without annealing

Science.gov (United States)

Giorgi, Leonardo; Dikonimos, Theodoros; Giorgi, Rossella; Buonocore, Francesco; Faggio, Giuliana; Messina, Giacomo; Lisi, Nicola

2018-03-01

This work demonstrates that upon anodic polarization in an aqueous fluoride-containing electrolyte, TiO2 nanotube array films can be formed with a well-defined crystalline phase, rather than an amorphous one. The crystalline phase was obtained avoiding any high temperature annealing. We studied the formation of nanotubes in an HF/H2O medium and the development of crystalline grains on the nanotube wall, and we found a facile way to achieve crystalline TiO2 nanotube arrays through a one-step anodization. The crystallinity of the film was influenced by the synthesis parameters, and the optimization of the electrolyte composition and anodization conditions (applied voltage and time) were carried out. For comparison purposes, crystalline anatase TiO2 nanotubes were also prepared by thermal treatment of amorphous nanotubes grown in an organic bath (ethylene glycol/NH4F/H2O). The morphology and the crystallinity of the nanotubes were studied by field emission gun-scanning electron microscopy (FEG-SEM) and Raman spectroscopy, whereas the electrochemical and semiconducting properties were analyzed by means of linear sweep voltammetry, impedance spectroscopy, and Mott-Schottky plots. X-ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS) allowed us to determine the surface composition and the electronic structure of the samples and to correlate them with the electrochemical data. The optimal conditions to achieve a crystalline phase with high donor concentration are defined.

Batch fabrication of carbon nanotube bearings

International Nuclear Information System (INIS)

Subramanian, A; Dong, L X; Tharian, J; Sennhauser, U; Nelson, B J

2007-01-01

Relative displacements between the atomically smooth, nested shells in multiwalled carbon nanotubes (MWNTs) can be used as a robust nanoscale motion enabling mechanism. Here, we report on a novel method suited for structuring large arrays of MWNTs into such nanobearings in a parallel fashion. By creating MWNT nanostructures with nearly identical electrical circuit resistance and heat transport conditions, uniform Joule heating across the array is used to simultaneously engineer the shell geometry via electric breakdown. The biasing approach used optimizes process metrics such as yield and cycle-time. We also present the parallel and piecewise shell engineering at different segments of a single nanotube to construct multiple, but independent, high density bearings. We anticipate this method for constructing electromechanical building blocks to be a fundamental unit process for manufacturing future nanoelectromechanical systems (NEMS) with sophisticated architectures and to drive several nanoscale transduction applications such as GHz-oscillators, shuttles, memories, syringes and actuators

Heterostructured ZnFe2O4/Fe2TiO5/TiO2 Composite Nanotube Arrays with an Improved Photocatalysis Degradation Efficiency Under Simulated Sunlight Irradiation

Science.gov (United States)

Xiong, Kun; Wang, Kunzhou; Chen, Lin; Wang, Xinqing; Fan, Qingbo; Courtois, Jérémie; Liu, Yuliang; Tuo, Xianguo; Yan, Minhao

2018-03-01

To improve the visible light absorption and photocatalytic activity of titanium dioxide nanotube arrays (TONTAs), ZnFe2O4 (ZFO) nanocrystals were perfused into pristine TONTA pipelines using a novel bias voltage-assisted perfusion method. ZFO nanocrystals were well anchored on the inner walls of the pristine TONTAs when the ZFO suspensions (0.025 mg mL-1) were kept under a 60 V bias voltage for 1 h. After annealing at 750 °C for 2 h, the heterostructured ZFO/Fe2TiO5 (FTO)/TiO2 composite nanotube arrays were successfully obtained. Furthermore, Fe3+ was reduced to Fe2+ when solid solution reactions occurred at the interface of ZFO and the pristine TONTAs. Introducing ZFO significantly enhanced the visible light absorption of the ZFO/FTO/TONTAs relative to that of the annealed TONTAs. The coexistence of type I and staggered type II band alignment in the ZFO/FTO/TONTAs facilitated the separation of photogenerated electrons and holes, thereby improving the efficiency of the ZFO/FTO/TONTAs for photocatalytic degradation of methylene blue when irradiated with simulated sunlight. [Figure not available: see fulltext.

T-gate aligned nanotube radio frequency transistors and circuits with superior performance.

Science.gov (United States)

Che, Yuchi; Lin, Yung-Chen; Kim, Pyojae; Zhou, Chongwu

2013-05-28

In this paper, we applied self-aligned T-gate design to aligned carbon nanotube array transistors and achieved an extrinsic current-gain cutoff frequency (ft) of 25 GHz, which is the best on-chip performance for nanotube radio frequency (RF) transistors reported to date. Meanwhile, an intrinsic current-gain cutoff frequency up to 102 GHz is obtained, comparable to the best value reported for nanotube RF transistors. Armed with the excellent extrinsic RF performance, we performed both single-tone and two-tone measurements for aligned nanotube transistors at a frequency up to 8 GHz. Furthermore, we utilized T-gate aligned nanotube transistors to construct mixing and frequency doubling analog circuits operated in gigahertz frequency regime. Our results confirm the great potential of nanotube-based circuit applications and indicate that nanotube transistors are promising building blocks in high-frequency electronics.

Combined antenna and localized plasmon resonance in Raman scattering from random arrays of silver-coated, vertically aligned multiwalled carbon nanotubes.

Science.gov (United States)

Dawson, P; Duenas, J A; Boyle, M G; Doherty, M D; Bell, S E J; Kern, A M; Martin, O J F; Teh, A-S; Teo, K B K; Milne, W I

2011-02-09

The electric field enhancement associated with detailed structure within novel optical antenna nanostructures is modeled using the surface integral equation technique in the context of surface-enhanced Raman scattering (SERS). The antennae comprise random arrays of vertically aligned, multiwalled carbon nanotubes dressed with highly granular Ag. Different types of "hot-spot" underpinning the SERS are identified, but contrasting characteristics are revealed. Those at the outer edges of the Ag grains are antenna driven with field enhancement amplified in antenna antinodes while intergrain hotspots are largely independent of antenna activity. Hot-spots between the tops of antennae leaning towards each other also appear to benefit from antenna amplification.

Fabrication of PANI/C-TiO2 Composite Nanotube Arrays Electrode for Supercapacitor

Directory of Open Access Journals (Sweden)

Chengcheng Zhang

2015-01-01

Full Text Available Polyaniline/carbon doped TiO2 composite nanotube arrays (PANI/C-TiO2 NTAs have been prepared successfully by electrodepositing PANI in C-TiO2 NTAs which were prepared by directly annealing the as-anodized TiO2 NTAs under Ar atmosphere. The organic residual in the TiO2 NTAs during the process of anodization acts as carbon source and is carbonized in Ar atmosphere to manufacture the C-TiO2 NTAs. The specific capacitance of the PANI/C-TiO2 electrode is 120.8 mF cm−2 at a current density of 0.1 mA cm−2 and remains 104.3 mF cm−2 at a current density of 2 mA cm−2 with the calculated rate performance of 86.3%. After 5000 times of charge-discharge cycling at a current density of 0.2 mA cm−2, the specific capacitance retains 88.7% compared to the first cycle. All these outstanding performances of the as-prepared PANI/C-TiO2 NTAs indicate it will be a promising electrode for supercapacitor.

Performance assessments of vertically aligned carbon nanotubes multi-electrode arrays using Cath.a-differentiated (CAD) cells

Science.gov (United States)

Jeong, Du Won; Jung, Jongjin; Kim, Gook Hwa; Yang, Cheol-Soo; Kim, Ju Jin; Jung, Sang Don; Lee, Jeong-O.

2015-08-01

In this work, Cath.a-differentiated (CAD) cells were used in place of primary neuronal cells to assess the performance of vertically aligned carbon nanotubes (VACNTs) multi-electrode arrays (MEA). To fabricate high-performance MEA, VACNTs were directly grown on graphene/Pt electrodes via plasma enhanced chemical deposition technique. Here, graphene served as an intermediate layer lowering contact resistance between VACNTs and Pt electrode. In order to lower the electrode impedance and to enhance the cell adhesion, VACNTs-MEAs were treated with UV-ozone for 20 min. Impedance of VACNTs electrode at 1 kHz frequency exhibits a reasonable value (110 kΩ) for extracellular signal recording, and the signal to noise ratio the is good enough to measure low signal amplitude (15.7). Spontaneous firing events from CAD cells were successfully measured with VACNTs MEAs that were also found to be surprisingly robust toward the biological interactions.

Performance assessments of vertically aligned carbon nanotubes multi-electrode arrays using Cath.a-differentiated (CAD) cells

International Nuclear Information System (INIS)

Jeong, Du Won; Jin Kim, Ju; Jung, Jongjin; Yang, Cheol-Soo; Lee, Jeong-O; Hwa Kim, Gook; Don Jung, Sang

2015-01-01

In this work, Cath.a-differentiated (CAD) cells were used in place of primary neuronal cells to assess the performance of vertically aligned carbon nanotubes (VACNTs) multi-electrode arrays (MEA). To fabricate high-performance MEA, VACNTs were directly grown on graphene/Pt electrodes via plasma enhanced chemical deposition technique. Here, graphene served as an intermediate layer lowering contact resistance between VACNTs and Pt electrode. In order to lower the electrode impedance and to enhance the cell adhesion, VACNTs-MEAs were treated with UV–ozone for 20 min. Impedance of VACNTs electrode at 1 kHz frequency exhibits a reasonable value (110 kΩ) for extracellular signal recording, and the signal to noise ratio the is good enough to measure low signal amplitude (15.7). Spontaneous firing events from CAD cells were successfully measured with VACNTs MEAs that were also found to be surprisingly robust toward the biological interactions. (paper)

Template directed synthesis of plasmonic gold nanotubes with tunable IR absorbance.

Science.gov (United States)

Bridges, Colin R; Schon, Tyler B; DiCarmine, Paul M; Seferos, Dwight S

2013-04-01

A nearly parallel array of pores can be produced by anodizing aluminum foils in acidic environments. Applications of anodic aluminum oxide (AAO) membranes have been under development since the 1990's and have become a common method to template the synthesis of high aspect ratio nanostructures, mostly by electrochemical growth or pore-wetting. Recently, these membranes have become commercially available in a wide range of pore sizes and densities, leading to an extensive library of functional nanostructures being synthesized from AAO membranes. These include composite nanorods, nanowires and nanotubes made of metals, inorganic materials or polymers. Nanoporous membranes have been used to synthesize nanoparticle and nanotube arrays that perform well as refractive index sensors, plasmonic biosensors, or surface enhanced Raman spectroscopy (SERS) substrates, as well as a wide range of other fields such as photo-thermal heating, permselective transport, catalysis, microfluidics, and electrochemical sensing. Here, we report a novel procedure to prepare gold nanotubes in AAO membranes. Hollow nanostructures have potential application in plasmonic and SERS sensing, and we anticipate these gold nanotubes will allow for high sensitivity and strong plasmon signals, arising from decreased material dampening.

As-grown vertically aligned amorphous TiO2 nanotube arrays as high-rate Li-based micro-battery anodes with improved long-term performance

International Nuclear Information System (INIS)

Lamberti, Andrea; Garino, Nadia; Sacco, Adriano; Bianco, Stefano; Chiodoni, Angelica; Gerbaldi, Claudio

2015-01-01

Highlights: • Amorphous TiO 2 nanotube (NT) arrays are fabricated by fast and facile anodic oxidation. • Near-theoretical initial specific capacity and remarkable rate capability. • Very long-term cycling stability (>2000 cycles) at a very high C-rate. • High surface area and improved interfacial characteristics for fast diffusion kinetics. • NTs show promising prospects in storage devices conceived for high power applications. - Abstract: Vertically oriented arrays of high surface area TiO 2 nanotubes (NTs) are fabricated by the fast and facile anodic oxidation of a titanium foil. The formation of well-defined one-dimensional nanotubular carpets is assessed by means of morphological Field Emission Scanning Electron Microscopy characterisation, while X-ray diffraction analysis and Transmission Electron Microscopy imaging confirm the amorphous nature of the samples. The electrochemical response evaluated in lab-scale lithium cells is highly satisfying with near-theoretical initial specific capacity and remarkable rate capability, noteworthy in the absence of binders and conductive agents, which would affect the overall energy density. A specific capacity exceeding 200 mAh g −1 is observed at very high 24 C and approx. 80 mAh g −1 are retained even at very high 96 C rate, thus accounting for the promising prospects in storage devices conceived for high power applications. Moreover, the NTs can perform with good cycling stability and capacity retention approaching 50% of the initial value after very long-term operation along with improved durability (> 2000 cycles)

Au Nanoparticles Decorated TiO2 Nanotube Arrays as a Recyclable Sensor for Photoenhanced Electrochemical Detection of Bisphenol A.

Science.gov (United States)

Hu, Liangsheng; Fong, Chi-Chun; Zhang, Xuming; Chan, Leo Lai; Lam, Paul K S; Chu, Paul K; Wong, Kwok-Yin; Yang, Mengsu

2016-04-19

A photorefreshable and photoenhanced electrochemical sensing platform for bisphenol A (BPA) detection based on Au nanoparticles (NPs) decorated carbon doped TiO2 nanotube arrays (TiO2/Au NTAs) is described. The TiO2/Au NTAs were prepared by quick annealing of anodized nanotubes in argon, followed by controllable electrodeposition of Au NPs. The decoration of Au NPs not only improved photoelectrochemical behavior but also enhanced electrocatalytic activities of the resulted hybrid NTAs. Meanwhile, the high photocatalytic activity of the NTAs allowed the electrode to be readily renewed without damaging the microstructures and surface states after a short UV treatment. The electrochemical detection of BPA on TiO2/Au NTAs electrode was significantly improved under UV irradiation as the electrode could provide fresh reaction surface continuously and the further increased photocurrent resulting from the improved separation efficiency of the photogenerated electron-hole pairs derived from the consumption of holes by BPA. The results showed that the refreshable TiO2/Au NTAs electrode is a promising sensor for long-term BPA monitoring with the detection limit (S/N = 3) of 6.2 nM and the sensitivity of 2.8 μA·μM(-1)·cm(-2).

Miniaturized pH Sensors Based on Zinc Oxide Nanotubes/Nanorods

Directory of Open Access Journals (Sweden)

Magnus Willander

2009-11-01

Full Text Available ZnO nanotubes and nanorods grown on gold thin film were used to create pH sensor devices. The developed ZnO nanotube and nanorod pH sensors display good reproducibility, repeatability and long-term stability and exhibit a pH-dependent electrochemical potential difference versus an Ag/AgCl reference electrode over a large dynamic pH range. We found the ZnO nanotubes provide sensitivity as high as twice that of the ZnO nanorods, which can be ascribed to the fact that small dimensional ZnO nanotubes have a higher level of surface and subsurface oxygen vacancies and provide a larger effective surface area with higher surface-to-volume ratio as compared to ZnO nanorods, thus affording the ZnO nanotube pH sensor a higher sensitivity. Experimental results indicate ZnO nanotubes can be used in pH sensor applications with improved performance. Moreover, the ZnO nanotube arrays may find potential application as a novel material for measurements of intracellular biochemical species within single living cells.

Multimodal Electrothermal Silicon Microgrippers for Nanotube Manipulation

DEFF Research Database (Denmark)

Nordström Andersen, Karin; Petersen, Dirch Hjorth; Carlson, Kenneth

2009-01-01

Microgrippers that are able to manipulate nanoobjects reproducibly are key components in 3-D nanomanipulation systems. We present here a monolithic electrothermal microgripper prepared by silicon microfabrication, and demonstrate pick-and-place of an as-grown carbon nanotube from a 2-D array onto...

Evolution of nanomechanical properties and crystallinity of individual titanium dioxide nanotube resonators

KAUST Repository

Stassi, Stefano

2017-12-29

Herein a complete characterization of single TiO2 nanotube resonator was reported for the first time. The modal vibration response analysis allows a non-invasive indirect evaluation of the mechanical properties of the TiO2 nanotube. The effect of post-grown thermal treatments on nanotube mechanical properties was investigated and carefully correlated to the chemico-physical parameters evolution. The Young\\'s modulus of TiO2 nanotube linearly rises from 57 GPa up to 105 GPa for annealing at 600°C depending on the compositional and crystallographic evolution of the nanostructure. Considering the growing interest in single nanostructure devices, the reported findings allow a deeper understanding of the properties of individual titanium dioxide nanotubes extrapolated from their standard arrayed architecture.

Carbon Nanotube Bolometer for Absolute FTIR Spectroscopy

Science.gov (United States)

Woods, Solomon; Neira, Jorge; Tomlin, Nathan; Lehman, John

We have developed and calibrated planar electrical-substitution bolometers which employ absorbers made from vertically-aligned carbon nanotube arrays. The nearly complete absorption of light by the carbon nanotubes from the visible range to the far-infrared can be exploited to enable a device with read-out in native units equivalent to optical power. Operated at cryogenic temperatures near 4 K, these infrared detectors are designed to have time constant near 10 ms and a noise floor of about 10 pW. Built upon a micro-machined silicon platform, each device has an integrated heater and thermometer, either a carbon nanotube thermistor or superconducting transition edge sensor, for temperature control. We are optimizing temperature-controlled measurement techniques to enable high resolution spectral calibrations using these devices with a Fourier-transform spectrometer.

International strategic minerals inventory summary report; tin

Science.gov (United States)

Sutphin, D.M.; Sabin, A.E.; Reed, B.L.

1990-01-01

The International Strategic Minerals Inventory tin inventory contains records for 56 major tin deposits and districts in 21 countries. These countries accounted for 98 percent of the 10 million metric tons of tin produced in the period 1934-87. Tin is a good alloying metal and is generally nontoxic, and its chief uses are as tinplate for tin cans and as solder in electronics. The 56 locations consist of 39 lode deposits and 17 placers and contain almost 7.5 million metric tons of tin in identified economic resources (R1E) and another 1.5 million metric tons of tin in other resource categories. Most of these resources are in major deposits that have been known for over a hundred years. Lode deposits account for 44 percent of the R1E and 87 percent of the resources in other categories. Placer deposits make up the remainder. Low-income and middle-income countries, including Bolivia and Brazil and countries along the Southeast Asian Tin Belt such as Malaysia, Thailand, and Indonesia account for 91 percent of the R1E resources of tin and for 61 percent of resources in other categories. The United States has less than 0.05 percent of the world's tin R1E in major deposits. Available data suggest that the Soviet Union may have about 4 percent of resources in this category. The industrial market economy countries of the United States, Japan, Federal Republic of Germany, and the United Kingdom are major consumers of tin, whereas the major tin-producing countries generally consume little tin. The Soviet Union and China are both major producers and consumers of tin. At the end of World War II, the four largest tin-producing countries (Bolivia, the Belgian Congo (Zaire), Nigeria, and Malaysia) produced over 80 percent of the world's tin. In 1986, the portion of production from the four largest producers (Malaysia, Brazil, Soviet Union, Indonesia) declined to about 55 percent, while the price of tin rose from about $1,500 to $18,000 per metric ton. In response to tin shortages

Preparations, Properties, and Applications of Periodic Nano Arrays using Anodized Aluminum Oxide and Di-block Copolymer

Science.gov (United States)

Noh, Kunbae

2011-12-01

Self-ordered arrangements observed in various materials systems such as anodic aluminum oxide, polystyrene nanoparticles, and block copolymer are of great interest in terms of providing new opportunities in nanofabrication field where lithographic techniques are broadly used in general. Investigations on self-assembled nano arrays to understand how to obtain periodic nano arrays in an efficient yet inexpensive way, and how to realize advanced material and device systems thereof, can lead to significant impacts on science and technology for many forefront device applications. In this thesis, various aspects of periodic nano-arrays have been discussed including novel preparations, properties and applications of anodized aluminum oxide (AAO) and PS-b-P4VP (S4VP) di-block copolymer self-assembly. First, long-range ordered AAO arrays have been demonstrated. Nanoimprint lithography (NIL) process allowed a faithful pattern transfer of the imprint mold pattern onto Al thin film, and interesting self-healing and pattern tripling phenomena were observed, which could be applicable towards fabrication of the NIL master mold having highly dense pattern over large area, useful for fabrication of a large-area substrate for predictable positioning of arrayed devices. Second, S4VP diblock copolymer self-assembly and S4VP directed AAO self-assembly have been demonstrated in the Al thin film on Si substrate. Such a novel combination of two dissimilar self-assembly techniques demonstrated a potential as a versatile tool for nanopatterning formation on a Si substrate, capable of being integrated into Si process technology. As exemplary applications, vertically aligned Ni nanowires have been synthesized into an S4VP-guided AAO membrane on a Si substrate in addition to anti-dot structured [Co/Pd]n magnetic multilayer using S4VP self assembly. Third, a highly hexagonally ordered, vertically parallel aluminum oxide nanotube array was successfully fabricated via hard anodization technique

A carbon nanotube immunosensor for Salmonella

Science.gov (United States)

Lerner, Mitchell B.; Goldsmith, Brett R.; McMillon, Ronald; Dailey, Jennifer; Pillai, Shreekumar; Singh, Shree R.; Johnson, A. T. Charlie

2011-12-01

Antibody-functionalized carbon nanotube devices have been suggested for use as bacterial detectors for monitoring of food purity in transit from the farm to the kitchen. Here we report progress towards that goal by demonstrating specific detection of Salmonella in complex nutrient broth solutions using nanotube transistors functionalized with covalently-bound anti-Salmonella antibodies. The small size of the active device region makes them compatible with integration in large-scale arrays. We find that the on-state current of the transistor is sensitive specifically to the Salmonella concentration and saturates at low concentration (Salmonella and other bacteria types, with no sign of saturation even at much larger concentrations (108 cfu/ml).

Vertically Aligned Co9 S8 Nanotube Arrays onto Graphene Papers as High-Performance Flexible Electrodes for Supercapacitors.

Science.gov (United States)

Xiong, Dongbin; Li, Xifei; Bai, Zhimin; Li, Jianwei; Han, Yan; Li, Dejun

2018-02-16

Paper-like electrodes are emerging as a new category of advanced electrodes for flexible supercapacitors (SCs). Graphene, a promising two-dimensional material with high conductivity, can be easily processed into papers. Here, we report a rational design of flexible architecture with Co 9 S 8 nanotube arrays (NAs) grown onto graphene paper (GP) via a facile two-step hydrothermal method. When employed as flexible free-standing electrode for SCs, the proposed architectured Co 9 S 8 /GPs exhibits superior electrochemical performance with ultrahigh capacitance and outstanding rate capability (469 F g -1 at 10 A g -1 ). These results demonstrate that the new nanostructured Co 9 S 8 /GPs can be potentially applied in high performance flexible supercapacitors. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Gamma radiation effects in vertically aligned carbon nanotubes

OpenAIRE

Lubkowski, Grzegorz; Kuhnhenn, Jochen; Suhrke, Michael; Weinand, Udo; Endler, Ingolf; Meißner, Frank; Richter, Sylvia

2011-01-01

This paper describes an experimental study of gamma radiation effects in low-density arrays of vertically aligned carbon nanotubes. These arrays are characterized by excellent anti-reflective and absorbing properties for wavelengths from UV to IR, which makes them an interesting option for stray light control in optical space applications. Gamma irradiation equivalent to an estimated surface lifetime exposition in geostationary orbit does not affect the reflectivity of the structures. First h...

A three-dimensional microelectrode array composed of vertically aligned ultra-dense carbon nanotube networks

Science.gov (United States)

Nick, C.; Yadav, S.; Joshi, R.; Schneider, J. J.; Thielemann, C.

2015-07-01

Electrodes based on carbon nanotubes are a promising approach to manufacture highly sensitive sensors with a low limit of signal detection and a high signal-to-noise ratio. This is achieved by dramatically increasing the electrochemical active surface area without increasing the overall geometrical dimensions. Typically, carbon nanotube electrodes are nearly planar and composed of randomly distributed carbon nanotube networks having a limited surface gain for a specific geometrical surface area. To overcome this limitation, we have introduced vertically aligned carbon nanotube (VACNT) networks as electrodes, which are arranged in a microelectrode pattern of 60 single electrodes. Each microelectrode features a very high aspect ratio of more than 300 and thus a dramatically increased surface area. These microelectrodes composed of VACNT networks display dramatically decreased impedance over the entire frequency range compared to planar microelectrodes caused by the enormous capacity increase. This is experimentally verified by electrochemical impedance spectroscopy and cyclic voltammetry.

A facile one-step synthesis of Mn{sub 3}O{sub 4} nanoparticles-decorated TiO{sub 2} nanotube arrays as high performance electrode for supercapacitors

Energy Technology Data Exchange (ETDEWEB)

Zhang, Jianfang [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); Wang, Yan [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); Key Laboratory of Advance Functional Materials and Devices of Anhui Province, Hefei 230009 (China); Qin, Yongqiang, E-mail: albon@hfut.edu.cn [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); Key Laboratory of Advance Functional Materials and Devices of Anhui Province, Hefei 230009 (China); Yu, Cuiping [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); Cui, Lihua [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); School of Materials Science and Engineering, Beifang University of Nationalities, Yinchuan 750021 (China); Shu, Xia [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); Cui, Jiewu; Zheng, Hongmei; Zhang, Yong [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); Key Laboratory of Advance Functional Materials and Devices of Anhui Province, Hefei 230009 (China); Wu, Yucheng, E-mail: ycwu@hfut.edu.cn [School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009 (China); Key Laboratory of Advance Functional Materials and Devices of Anhui Province, Hefei 230009 (China)

2017-02-15

Via a facile one-step chemical bath deposition route, homogeneously dispersed Mn{sub 3}O{sub 4} nanoparticles have been successfully deposited onto the inner surface of TiO{sub 2} nanotube arrays (TNAs). The content and size of Mn{sub 3}O{sub 4} can be controlled by changing the deposition time. Field emission scanning electron microscopy and transmission electron microscopy analysis reveal the morphologies structures of Mn{sub 3}O{sub 4}/TNAs composites. The crystal-line structures are characterized by the X-ray diffraction patterns and Raman spectra. X-ray photoelectron spectroscopy further confirms the valence states of the sample elements. The electrochemical properties of Mn{sub 3}O{sub 4}/TNAs electrodes are systematically investigated by the combine use of cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance spectroscopy. The resulting Mn{sub 3}O{sub 4}/TNAs electrode prepared by deposition time of 3 h shows the highest specific capacitance of 570 F g{sup −1} at a current density of 1 A g{sup −1}. And it also shows an excellent long-term cycling stability at a current density of 5 A g{sup −1}, which remaining 91.8% of the initial capacitance after 2000 cycles. Thus this kind of Mn{sub 3}O{sub 4} nanoparticles decorated TNAs may be considered as an alternative promising candidate for high performance supercapacitor electrodes. - Graphical abstract: Mn{sub 3}O{sub 4} nanoparticles have been uniformly deposited onto the inner surfaces of TiO{sub 2} nanotube arrays through a facile one-step chemical bath deposition method. As electrodes for supercapacitors, they exhibit a relatively high specific capacity and excellent cycling stability. - Highlights: • Mn{sub 3}O{sub 4} nanoparticles have been deposited onto TiO{sub 2} nanotube arrays by chemical bath deposition. • The Mn{sub 3}O{sub 4}/TNAs exhibits a highest specific capacitance of 570 F g{sup –1} at a current density of 1 A g{sup –1}. • The Mn{sub 3}O{sub 4}/TNAs

An innovative approach to synthesize highly-ordered TiO2 nanotubes.

Science.gov (United States)

Isimjan, Tayirjan T; Yang, D Q; Rohani, Sohrab; Ray, Ajay K

2011-02-01

An innovative route to prepare highly-ordered and dimensionally controlled TiO2 nanotubes has been proposed using a mild sonication method. The nanotube arrays were prepared by the anodization of titanium in an electrolyte containing 3% NH4F and 5% H2O in glycerol. It is demonstrated that the TiO2 nanostructures has two layers: the top layer is TiO2 nanowire and underneath is well-ordered TiO2 nanotubes. The top layer can easily fall off and form nanowires bundles by implementing a mild sonication after a short annealing time. We found that the dimensions of the TiO2 nanotubes were only dependent on the anodizing condition. The proposed technique may be extended to fabricate reproducible well-ordered TiO2 nanotubes with large area on other metals.

Langmuir-Blodgett assembly of visible light responsive TiO{sub 2} nanotube arrays/graphene oxide heterostructure

Energy Technology Data Exchange (ETDEWEB)

Chen, Ying; Gao, Hongyan; Wei, Danming; Dong, Xinju; Cao, Yan, E-mail: yan.cao@wku.edu

2017-01-15

Highlights: • First to report a heterostructure of TNA with GO prepared by LB assembly. • Much better photocurrent (32 μAcm{sup −2}) of TNA-GO, contrasting to TNA (12 μAcm{sup −2}). • Schottky junction formed between TNA and GO enhanced the photocurrent. • GO on TNA improved the hydrophilicity of TNA-GO. - Abstract: The hybrid nanocomposites of titanium dioxide (TiO{sub 2}) with graphene oxide (GO) have recently garnered much attention as electronic devices, energy conversion devices, photocatalysts and other applications. In this study, Langmuir-Blodgett (LB) assembly method was firstly reported to prepare a TiO{sub 2} nanotube arrays (TNA)-GO heterostructure. The as-prepared TNA-GO sample was characterized by X-ray diffraction, Raman spectra, scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy. The promising characteristics of this TNA-GO material, the inexpensive, nontoxic and highly visible-light responsiveness, may raise the potential uses in many, various photocatalytic applications.

Ag-bridged Ag{sub 2}O nanowire network/TiO{sub 2} nanotube array p–n heterojunction as a highly efficient and stable visible light photocatalyst

Energy Technology Data Exchange (ETDEWEB)

Liu, Chengbin, E-mail: chem_cbliu@hnu.edu.cn [Key Laboratory of Jiangxi Province for Persistent Pollutants Control and Resources Recycle, Nanchang Hangkong University, Nanchang 330063 (China); State Key Laboratory of Chemo/Biosensing and Chemometrics, Hunan University, Changsha 410082 (China); Cao, Chenghao [State Key Laboratory of Chemo/Biosensing and Chemometrics, Hunan University, Changsha 410082 (China); Luo, Xubiao [Key Laboratory of Jiangxi Province for Persistent Pollutants Control and Resources Recycle, Nanchang Hangkong University, Nanchang 330063 (China); Luo, Shenglian [Key Laboratory of Jiangxi Province for Persistent Pollutants Control and Resources Recycle, Nanchang Hangkong University, Nanchang 330063 (China); State Key Laboratory of Chemo/Biosensing and Chemometrics, Hunan University, Changsha 410082 (China)

2015-03-21

Graphical abstract: A unique Ag-bridged Ag{sub 2}O nanowire network/TiO{sub 2} nanotube array p–n heterojunction was fabricated by simple electrochemical method. The heterostructures exhibit high photocatalytic activity and excellent recycling performance. - Highlights: • Ag-bridged Ag{sub 2}O nanowire network self-stability structure. • Ag{sub 2}O nanowire network/TiO{sub 2} nanotube p–n heterojunction. • High visible light photocatalytic activity. • Highly stable recycling performance. - Abstract: A unique Ag-bridged Ag{sub 2}O nanowire network/TiO{sub 2} nanotube array p–n heterojunction (Ag–Ag{sub 2}O/TiO{sub 2} NT) was fabricated by simple electrochemical method. Ag nanoparticles were firstly electrochemically deposited onto the surface of TiO{sub 2} NT and then were partly oxidized to Ag{sub 2}O nanowires while the rest of Ag mother nanoparticles were located at the junctions of Ag{sub 2}O nanowire network. The Ag–Ag{sub 2}O/TiO{sub 2} NT heterostructure exhibited strong visible-light response, effective separation of photogenerated carriers, and high adsorption capacity. The integration of Ag–Ag{sub 2}O self-stability structure and p–n heterojunction permitted high and stable photocatalytic activity of Ag–Ag{sub 2}O/TiO{sub 2} NT heterostructure photocatalyst. Under 140-min visible light irradiation, the photocatalytic removal efficiency of both dye acid orange 7 (AO7) and industrial chemical p-nitrophenol (PNP) over Ag–Ag{sub 2}O/TiO{sub 2} NT reached nearly 100% much higher than 17% for AO7 or 13% for PNP over bare TiO{sub 2} NT. After 5 successive cycles under 600-min simulated solar light irradiation, Ag–Ag{sub 2}O/TiO{sub 2} NT remained highly stable photocatalytic activity.

Length Dependent Foam-Like Mechanical Response of Axially Indented Vertically Oriented Carbon Nanotube Arrays

Science.gov (United States)

2011-01-01

Sands T, Xu X, Fisher T. Dendrimer -assisted controlled growth of carbon nanotubes for enhanced thermal interface conductance. Nanotechnology 2007;18...surfaces. Rev Sci Instrum 2006;77(9):095105-1–3. [11] Allaoui A, Hoa S, Evesque P, Bai J. Electronic transport in carbon nanotube tangles under compression

High resolution stationary digital breast tomosynthesis using distributed carbon nanotube x-ray source array.

Science.gov (United States)

Qian, Xin; Tucker, Andrew; Gidcumb, Emily; Shan, Jing; Yang, Guang; Calderon-Colon, Xiomara; Sultana, Shabana; Lu, Jianping; Zhou, Otto; Spronk, Derrek; Sprenger, Frank; Zhang, Yiheng; Kennedy, Don; Farbizio, Tom; Jing, Zhenxue

2012-04-01

The purpose of this study is to investigate the feasibility of increasing the system spatial resolution and scanning speed of Hologic Selenia Dimensions digital breast tomosynthesis (DBT) scanner by replacing the rotating mammography x-ray tube with a specially designed carbon nanotube (CNT) x-ray source array, which generates all the projection images needed for tomosynthesis reconstruction by electronically activating individual x-ray sources without any mechanical motion. The stationary digital breast tomosynthesis (s-DBT) design aims to (i) increase the system spatial resolution by eliminating image blurring due to x-ray tube motion and (ii) reduce the scanning time. Low spatial resolution and long scanning time are the two main technical limitations of current DBT technology. A CNT x-ray source array was designed and evaluated against a set of targeted system performance parameters. Simulations were performed to determine the maximum anode heat load at the desired focal spot size and to design the electron focusing optics. Field emission current from CNT cathode was measured for an extended period of time to determine the stable life time of CNT cathode for an expected clinical operation scenario. The source array was manufactured, tested, and integrated with a Selenia scanner. An electronic control unit was developed to interface the source array with the detection system and to scan and regulate x-ray beams. The performance of the s-DBT system was evaluated using physical phantoms. The spatially distributed CNT x-ray source array comprised 31 individually addressable x-ray sources covering a 30 angular span with 1 pitch and an isotropic focal spot size of 0.6 mm at full width at half-maximum. Stable operation at 28 kV(peak) anode voltage and 38 mA tube current was demonstrated with extended lifetime and good source-to-source consistency. For the standard imaging protocol of 15 views over 14, 100 mAs dose, and 2 × 2 detector binning, the projection

Chemistry of tin compounds and environment

International Nuclear Information System (INIS)

Ali, S.; Mazhar, M.; Mahmood, S.; Bhatti, M.H.; Chaudhary, M.A.

1997-01-01

Of the large volume of tin compounds reported in the literature, possible only 100 are commercially important. Tin compounds are a wide variety of purposes such as catalysts, stabilizers for many materials including polymer, biocidal agents, bactericides, insecticides, fungicides, wood preservatives, acaricides and anti fouling agents in paints, anticancer and antitumour agents, ceramic opacifiers, as textile additives, in metal finishing operations, as food additives and in electro conductive coating. All these applications make the environment much exposed to tin contamination. The application of organotin compounds as biocides account for about 30% of total tin consumption suggesting that the main environmental effects are likely to originate from this sector. Diorgano tins and mono-organo tins are used mainly in plastic industry which is the next big source for environmental pollution. In this presentation all environmental aspects of the use of tin compounds and the recommended preventive measures are discussed. (author)

Effect of ZnS layers on optical properties of prepared CdS/TiO{sub 2} nanotube arrays for photocatalyst

Energy Technology Data Exchange (ETDEWEB)

Zhang, Miao; Gong, Zezhou; Tao, Jiajia; Wang, Xingzhi; Wang, Zhuang; Yang, Lei; He, Gang [Anhui University, School of Physics and Material Science (China); Lv, Jianguo [Hefei Normal University, School of Electronic and Information Engineering (China); Wang, Peihong; Ding, Zongling [Anhui University, School of Physics and Material Science (China); Chen, Xiaoshuang [Chinese Academy of Sciences, National Laboratory for Infrared Physics, Shanghai Institute of Technical Physics (China); Sun, Zhaoqi, E-mail: szq@ahu.edu.cn [Anhui University, School of Physics and Material Science (China)

2017-03-15

The TiO{sub 2} nanotube arrays (TiO{sub 2} NTAs) prepared by re-oxidation were chosen as basement. The NTAs prepared through re-oxidation show smoother surface and more uniform tube mouth on large scale compared with the first as-grown one. We use successive ionic layer adsorption and reaction method to deposit quantum dots (ZnS and CdS) onto the sample successively. The findings reveal that two kinds of quantum dots (∼10 nm) distribute regularly and the nanotube mouth is open. From the UV–Vis absorption spectrum of samples, the red shift occurs after the sedimentation of the two quantum dots, which proves that the double modification can expand the absorption to 650 nm. Among all specimens, the sample produced by co-deposition has the highest speed of catalytic efficiency of 90.7% compared with bare TiO{sub 2} NTAs (52.9%) and just CdS QDs sensitized sample (65.8%). In the test of photocatalysis durability, the decay percentages of CdS/TiO{sub 2} NTAs and ZnS/CdS/TiO{sub 2} NTAs were 35.8 and 48.4%, respectively, which means that the ZnS passivation layer plays a crucial role in enhancing photocatalytic activities.

Hydrothermal solid-gas route to TiO2 nanoparticles/nanotube arrays for high-performance supercapacitors

Science.gov (United States)

Fan, Haowen; Zhang, He; Luo, Xiaolei; Liao, Maoying; Zhu, Xufei; Ma, Jing; Song, Ye

2017-07-01

Although TiO2 nanotube arrays (TNTAs) have shown great promise as supercapacitor materials, their specific capacitances are still not comparable with some typical materials. Here, TiO2 nanoparticles (NPs)/TNTAs hybrid structure has been derived from the anodized TNTAs by a facile hydrothermal solid-gas method (HSGM), which can avoid cracking or curling of the TNTAs from Ti substrate. The obtained NPs/TNTAs hybrid structure can exhibit a ∼4.90 times increase in surface area and a ∼5.49 times increase in areal specific capacitance compared to the TNTAs without HSGM treatment. Besides, the argon-atmosphere annealing can offer improved areal capacitance and cycling stability relative to the air-atmosphere annealing. The hydrothermal vapor pressure is a key factor for controlling microscopic morphologies of TNTAs, the morphology transformations of TNTAs during the HSGM treatment can be accelerated under enhanced vapor pressures. The highest areal capacitance of HSGM-treated TNTAs is up to 76.12 mF cm-2 at 0.5 mA cm-2, well above that of any TiO2 materials reported to date.

Synthesising highly reactive tin oxide using Tin(II2- ethylhexanoate polynucleation as precursor

Directory of Open Access Journals (Sweden)

Alejandra Montenegro Hernández

2009-01-01

Full Text Available Tin oxide is a widely used compound in technological applications, particularity as a catalyst, gas sensor and in making varistors, transparent conductors, electrocatalytic electrodes and photovoltaic cells. An ethylhexanoate tin salt, a carboxylic acid and poly-esterification were used for synthesising highly reactive tin oxide in the present study. Synthesis was controlled by Fourier transform infrared (FTIR spectroscopy and recording changes in viscosity. The tin oxide characteristics so obtained were determined using FTIR spectroscopy, X-ray diffraction (XRD and scanning electron microscopy (SEM. The SnO2 dust synthesised and heat-treated at 550°C yielded high density aggregates, having greater than 50 μm particle size. This result demonstrates the high reactivity of the ceramic powders synthesised here.

Measuring the sustainability of tin in China.

Science.gov (United States)

Yang, Congren; Tan, Quanyin; Zeng, Xianlai; Zhang, Yuping; Wang, Zhishi; Li, Jinhui

2018-09-01

Tin is a component of many items used in daily activities, including solder in consumer electronics, tin can containing food and beverages, polyvinyl chloride stabilizers in construction products, catalysts in industrial processes, etc. China is the largest producer and consumer of refined tin, and more than 60% of this refined tin is applied in the electronics sector as solder. China is the leader in global economic growth; simultaneously, China is also a major producer and consumer of electrical and electronic equipment (EEE). Thus, future tin supply and demand in China are forecasted, based on the gross domestic product per capita and the average consumption of refined tin in past five years. Current tin reserves and identified resources in China can meet the future two decades of mine production, but import of tin will also be critical for China's future tin consumption. However, there will be a lot of uncertainty for import of tin from other countries. At the same time, virgin mining of geological ores is a process of high energy consumption and destruction of the natural environment. Hence recycling tin from Sn-bearing secondary resources like tailings and waste electrical and electronic equipment (WEEE) can not only address the shortage of tin mineral resources, but also save energy and protect the ecological environment. Copyright © 2018 Elsevier B.V. All rights reserved.

Nonhomogeneous morphology and the elastic modulus of aligned carbon nanotube films

International Nuclear Information System (INIS)

Won, Yoonjin; Gao, Yuan; Kenny, Thomas W; Goodson, Kenneth E; Guzman de Villoria, Roberto; Wardle, Brian L; Xiang, Rong; Maruyama, Shigeo

2015-01-01

Carbon nanotube (CNT) arrays offer the potential to develop nanostructured materials that leverage their outstanding physical properties. Vertically aligned carbon nanotubes (VACNTs), also named CNT forests, CNT arrays, or CNT turfs, can provide high heat conductivity and sufficient mechanical compliance to accommodate thermal expansion mismatch for use as thermal interface materials (TIMs). This paper reports measurements of the in-plane moduli of vertically aligned, single-walled CNT (SWCNT) and multi-walled CNT (MWCNT) films. The mechanical response of these films is related to the nonhomogeneous morphology of the grown nanotubes, such as entangled nanotubes of a top crust layer, aligned CNTs in the middle region, and CNTs in the bottom layer. To investigate how the entanglements govern the overall mechanical moduli of CNT films, we remove the crust layer consisting of CNT entanglements by etching the CNT films from the top. A microfabricated cantilever technique shows that crust removal reduces the resulting moduli of the etched SWCNT films by as much as 40%, whereas the moduli of the etched MWCNT films do not change significantly, suggesting a minimal crust effect on the film modulus for thick MWCNT films (>90 μm). This improved understanding will allow us to engineer the mechanical moduli of CNT films for TIMs or packaging applications. (paper)

Nonhomogeneous morphology and the elastic modulus of aligned carbon nanotube films

Science.gov (United States)

Won, Yoonjin; Gao, Yuan; Guzman de Villoria, Roberto; Wardle, Brian L.; Xiang, Rong; Maruyama, Shigeo; Kenny, Thomas W.; Goodson, Kenneth E.

2015-11-01

Carbon nanotube (CNT) arrays offer the potential to develop nanostructured materials that leverage their outstanding physical properties. Vertically aligned carbon nanotubes (VACNTs), also named CNT forests, CNT arrays, or CNT turfs, can provide high heat conductivity and sufficient mechanical compliance to accommodate thermal expansion mismatch for use as thermal interface materials (TIMs). This paper reports measurements of the in-plane moduli of vertically aligned, single-walled CNT (SWCNT) and multi-walled CNT (MWCNT) films. The mechanical response of these films is related to the nonhomogeneous morphology of the grown nanotubes, such as entangled nanotubes of a top crust layer, aligned CNTs in the middle region, and CNTs in the bottom layer. To investigate how the entanglements govern the overall mechanical moduli of CNT films, we remove the crust layer consisting of CNT entanglements by etching the CNT films from the top. A microfabricated cantilever technique shows that crust removal reduces the resulting moduli of the etched SWCNT films by as much as 40%, whereas the moduli of the etched MWCNT films do not change significantly, suggesting a minimal crust effect on the film modulus for thick MWCNT films (>90 μm). This improved understanding will allow us to engineer the mechanical moduli of CNT films for TIMs or packaging applications.

Efficient photocatalytic degradation of gaseous N,N-dimethylformamide in tannery waste gas using doubly open-ended Ag/TiO2 nanotube array membranes

Science.gov (United States)

Zhao, Yang; Ma, Lin; Chang, Wenkai; Huang, Zhiding; Feng, Xugen; Qi, Xiaoxia; Li, Zenghe

2018-06-01

Gaseous N,N-dimethylformamide (DMF), typical volatile organic compound exhausted from manufacturing factories, may damage the health of workers under long-term exposure even at low levels. The defined geometry, porous surface and highly ordered channels make the free-standing anodic TiO2 nanotube (TiNT) arrays particularly suitable for applications of practical air purification by flow-through photocatalysis. In the present work, crystallized doubly open-ended Ag/TiNT array membranes were designed and prepared by employing a lift-off process based on an anodization-annealing-anodization-etching sequence, followed by uniform Ag nanoparticles decoration. For the photocatalytic degradation of gaseous DMF at low concentration levels close to that found in realistic pollutant air, an analytical methodology for the monitoring and determination of degradation process was developed based on the coupling of headspace sampling with gas chromatography mass spectrometry (HS-GC-MS). The doubly open-ended Ag/TiNT arrays exhibited higher removal efficiency of gaseous DMF from air compared with conventional bottom-closed Ag/TiNT arrays and pure bottomless TiNT arrays. These results indicated that the photocatalytic properties of TiNT arrays were improved with the open-bottom morphology and the Ag nanoparticles decoration. Based on the analysis with GC-MS and high performance ion chromatography (HPIC), it was found that demethylation is the main pathway of DMF degradation in photocatalytic reactions. Furthermore, decontamination of actual polluted tannery waste gas collected in leather factory proved that the photocatalysis on doubly open-ended Ag/TiNT array membrane is an efficient way and a promising application to treat air contaminated by DMF despite the complexity of various volatile organic compounds.

Field Emission of ITO-Coated Vertically Aligned Nanowire Array.

KAUST Repository

Lee, Changhwa

2010-04-29

An indium tin oxide (ITO)-coated vertically aligned nanowire array is fabricated, and the field emission characteristics of the nanowire array are investigated. An array of vertically aligned nanowires is considered an ideal structure for a field emitter because of its parallel orientation to the applied electric field. In this letter, a vertically aligned nanowire array is fabricated by modified conventional UV lithography and coated with 0.1-μm-thick ITO. The turn-on electric field intensity is about 2.0 V/μm, and the field enhancement factor, β, is approximately 3,078 when the gap for field emission is 0.6 μm, as measured with a nanomanipulator in a scanning electron microscope.

Field Emission of ITO-Coated Vertically Aligned Nanowire Array.

KAUST Repository

Lee, Changhwa; Lee, Seokwoo; Lee, Seung S

2010-01-01

An indium tin oxide (ITO)-coated vertically aligned nanowire array is fabricated, and the field emission characteristics of the nanowire array are investigated. An array of vertically aligned nanowires is considered an ideal structure for a field emitter because of its parallel orientation to the applied electric field. In this letter, a vertically aligned nanowire array is fabricated by modified conventional UV lithography and coated with 0.1-μm-thick ITO. The turn-on electric field intensity is about 2.0 V/μm, and the field enhancement factor, β, is approximately 3,078 when the gap for field emission is 0.6 μm, as measured with a nanomanipulator in a scanning electron microscope.

Nanoscale Optimization and Statistical Modeling of Photoelectrochemical Water Splitting Efficiency of N-Doped TiO2 Nanotubes

KAUST Repository

Isimjan, Tayirjan T.

2014-12-19

Highly ordered nitrogen-doped titanium dioxide (N-doped TiO2) nanotube array films with enhanced photo-electrochemical water splitting efficiency (PCE) for hydrogen generation were fabricated by electrochemical anodization, followed by annealing in a nitrogen atmosphere. Morphology, structure and composition of the N-doped TiO2 nanotube array films were investigated by FE-SEM, XPS, UV-Vis and XRD. The effect of annealing temperature, heating rate and annealing time on the morphology, structure, and photo-electrochemical property of the N-doped TiO2 nanotube array films were investigated. A design of experiments method was applied in order to minimize the number of experiments and obtain a statistical model for this system. From the modelling results, optimum values for the influential factors were obtained in order to achieve the maximum PCE. The optimized experiment resulted in 7.42 % PCE which was within 95 % confidence interval of the predicted value by the model. © 2014 Springer Science+Business Media.

Microwave synthesis and characterisation of tin dioxide (SnO2) coated multi-walled carbon nanotubes

CSIR Research Space (South Africa)

Motshekga, S

2010-09-01

Full Text Available an attractive material for application in solar cells, field effect transistors, catalysis and gas-sensing1-3. Nanostructured composite materials of carbon nanotubes and metal oxides promise superior performance over conventional approaches due to the ability...

Development of a Carbon Nanotube-Based Touchscreen Capable of Multi-Touch and Multi-Force Sensing

OpenAIRE

Kim, Wonhyo; Oh, Haekwan; Kwak, Yeonhwa; Park, Kwangbum; Ju, Byeong-Kwon; Kim, Kunnyun

2015-01-01

A force sensing touchscreen, which detects touch point and touch force simultaneously by sensing a change in electric capacitance, was designed and fabricated. It was made with single-walled carbon nanotubes (SWCNTs) which have better mechanical and chemical characteristics than the indium-tin-oxide transparent electrodes used in most contemporary touchscreen devices. The SWCNTs, with a transmittance of about 85% and electric conductivity of 400 Ω per square; were coated and patterned on glas...

InAs/Si Hetero-Junction Nanotube Tunnel Transistors

KAUST Repository

Hanna, Amir; Fahad, Hossain M.; Hussain, Muhammad Mustafa

2015-01-01

Hetero-structure tunnel junctions in non-planar gate-all-around nanowire (GAA NW) tunnel FETs (TFETs) have shown significant enhancement in ‘ON’ state tunnel current over their all-silicon counterpart. Here we show the unique concept of nanotube TFET in a hetero-structure configuration that is capable of much higher drive current as opposed to that of GAA NW TFETs.Through the use of inner/outer core-shell gates, a single III-V hetero-structured nanotube TFET leverages physically larger tunneling area while achieving higher driver current (ION) and saving real estates by eliminating arraying requirement. Numerical simulations has shown that a 10 nm thin nanotube TFET with a 100 nm core gate has a 5×normalized output current compared to a 10 nm diameter GAA NW TFET.

InAs/Si Hetero-Junction Nanotube Tunnel Transistors

KAUST Repository

Hanna, Amir

2015-04-29

Hetero-structure tunnel junctions in non-planar gate-all-around nanowire (GAA NW) tunnel FETs (TFETs) have shown significant enhancement in ‘ON’ state tunnel current over their all-silicon counterpart. Here we show the unique concept of nanotube TFET in a hetero-structure configuration that is capable of much higher drive current as opposed to that of GAA NW TFETs.Through the use of inner/outer core-shell gates, a single III-V hetero-structured nanotube TFET leverages physically larger tunneling area while achieving higher driver current (ION) and saving real estates by eliminating arraying requirement. Numerical simulations has shown that a 10 nm thin nanotube TFET with a 100 nm core gate has a 5×normalized output current compared to a 10 nm diameter GAA NW TFET.

Interfacial Engineered Polyaniline/Sulfur-doped TiO2 Nanotube Arrays for Ultralong Cycle Lifetime Fiber-Shaped, Solid-State Supercapacitors.

Science.gov (United States)

Li, Chun; Wang, Zhuanpei; Li, Shengwen; Cheng, Jianli; Zhang, Yanning; Zhou, Jingwen; Yang, Dan; Tong, Dong-Ge; Wang, Bin

2018-05-04

Fiber-shaped supercapacitors (FSCs) have great potential in wearable electronics applications. However, the limited specific surface area and inadequate structural stability caused by the weak interfacial interactions of the electrodes result in relatively low specific capacitance and unsatisfactory cycle lifetime. Herein, solid-state FSCs with high energy density and ultralong cycle lifetime based on polyaniline (PANI)/sulfur-doped TiO2 nanotubes array (PANI/S-TiO2) are fabricated by interfacial engineering. The experimental results and ab initio calculations reveal that S doping can effectively promote the conductivity of titania nanotubes and increase the binding energy of PANI anchored on the electrode surface, leading to much stronger binding of PANI on the surface of the electrode and excellent electrode structure stability. As a result, the FSCs using the PANI/S-TiO2 electrodes deliver a high specific capacitance of 91.9 mF cm-2, a capacitance retention of 93.78% after 12,000 charge/discharge cycles, and an areal energy density of 3.2 µWh cm-2, respectively. Meanwhile, the all-solid-state FSC device retains its excellent flexibility and stable electrochemical capacitance even after bending 150 cycles. The enhanced performances of FSCs could be attributed to the large surface area, short ion diffusion path, high electrical conductivity and engineered interfacial interaction of the rationally designed electrodes.

Carbon Nanotube Paper-Based Electroanalytical Devices

Directory of Open Access Journals (Sweden)

Youngmi Koo

2016-04-01

Full Text Available Here, we report on carbon nanotube paper-based electroanalytical devices. A highly aligned-carbon nanotube (HA-CNT array, grown using chemical vapor deposition (CVD, was processed to form bi-layered paper with an integrated cellulose-based Origami-chip as the electroanalytical device. We used an inverse-ordered fabrication method from a thick carbon nanotube (CNT sheet to a thin CNT sheet. A 200-layered HA-CNT sheet and a 100-layered HA-CNT sheet are explored as a working electrode. The device was fabricated using the following methods: (1 cellulose-based paper was patterned using a wax printer, (2 electrical connection was made using a silver ink-based circuit printer, and (3 three electrodes were stacked on a 2D Origami cell. Electrochemical behavior was evaluated using electrochemical impedance spectroscopy (EIS and cyclic voltammetry (CV. We believe that this platform could attract a great deal of interest for use in various chemical and biomedical applications.

Microstructure and pseudocapacitive properties of electrodes constructed of oriented NiO-TiO2 nanotube arrays.

Science.gov (United States)

Kim, Jae-Hun; Zhu, Kai; Yan, Yanfa; Perkins, Craig L; Frank, Arthur J

2010-10-13

We report on the synthesis and electrochemical properties of oriented NiO-TiO(2) nanotube (NT) arrays as electrodes for supercapacitors. The morphology of the films prepared by electrochemically anodizing Ni-Ti alloy foils was characterized by scanning and transmission electron microscopies, X-ray diffraction, and photoelectron spectroscopies. The morphology, crystal structure, and composition of the NT films were found to depend on the preparation conditions (anodization voltage and postgrowth annealing temperature). Annealing the as-grown NT arrays to a temperature of 600 °C transformed them from an amorphous phase to a mixture of crystalline rock salt NiO and rutile TiO(2). Changes in the morphology and crystal structure strongly influenced the electrochemical properties of the NT electrodes. Electrodes composed of NT films annealed at 600 °C displayed pseudocapacitor (redox-capacitor) behavior, including rapid charge/discharge kinetics and stable long-term cycling performance. At similar film thicknesses and surface areas, the NT-based electrodes showed a higher rate capability than the randomly packed nanoparticle-based electrodes. Even at the highest scan rate (500 mV/s), the capacitance of the NT electrodes was not much smaller (within 12%) than the capacitance measured at the slowest scan rate (5 mV/s). The faster charge/discharge kinetics of NT electrodes at high scan rates is attributed to the more ordered NT film architecture, which is expected to facilitate electron and ion transport during the charge-discharge reactions.

Decoration of TiO_2 nanotube arrays by graphitic-C_3N_4 quantum dots with improved photoelectrocatalytic performance

International Nuclear Information System (INIS)

Sun, Bo; Lu, Na; Su, Yan; Yu, Hongtao; Meng, Xiangyu; Gao, Zhanming

2017-01-01

Highlights: • TiO_2 nanotube arrays/graphitic-C_3N_4 quantum dots heterojunction was prepared via a facile dipping method. • The optimized dipping duration and concentration of heterojunction were investigated. • The prepared heterojunction extends optical absorption and reduces the recombination of charge carriers. • The photocurrent generated by the optimal g-C_3N_4 QDs/TNTAs photoanode is 4.3 times that of pristine TNTAs. • 98.6% of phenol is degraded in 120 min and the degradation rate is 4.9 times as great as that of pristine TNTAs. - Abstract: In this paper, we present a novel method to improve the photoelectrocatalytic (PEC) property of TiO_2 nanotube arrays (TNTAs) by way of decorating it with visible-light-respond graphitic-C_3N_4 quantum dots (g-C_3N_4 QDs). The g-C_3N_4 QDs/TNTAs heterojunction is successfully prepared using a facile dipping method. The optimal condition of preparing g-C_3N_4 QDs/TNTAs heterojunction is found as 60 min of dipping duration and 0.2 mg mL"−"1 of g-C_3N_4 QDs dipping solution. The fabricated g-C_3N_4 QDs/TNTAs heterojunction shows improved PEC activity comparing to TNTAs due to its better separation capability of photo-generated charges and wider optical absorption. And the photocurrent generated by the optimal g-C_3N_4 QDs/TNTAs photoanode is 4.3 times than that of pristine TNTAs. Besides, the g-C_3N_4 QDs/TNTAs heterojunction also exhibits superior PEC activities in degradation of phenol. 98.6% of phenol is successfully degraded in 120 min and the pseudo-first-order kinetic constant of phenol degradation is 4.9 times as great as that of pristine TNTAs. This work indicates that the g-C_3N_4 QDs/TNTAs heterojunction is expected to be a promising nanomaterial for pollutant degradation and further application in solar energy conversion.

Origin of enhancement in Raman scattering from Ag-dressed carbon-nanotube antennas : experiment and modelling

NARCIS (Netherlands)

Raziman, T.V.; Duenas, J.A.; Milne, W.I.; Martin, O.J.F.; Dawson, P.

2018-01-01

The D- and G-band Raman signals from random arrays of vertically aligned, multi-walled carbon nanotubes are significantly enhanced (up to ∼14×) while the signal from the underlying Si substrate is simultaneously attenuated (up to ∼6×) when the nanotubes are dressed, either capped or coated, with Ag.

Low-temperature Synthesis of Tin(II) Oxide From Tin(II) ketoacidoximate Precursor