  1. Enhanced photoelectrochemical and photocatalytic activity of WO3-surface modified TiO2 thin film

    Science.gov (United States)

    Qamar, Mohammad; Drmosh, Qasem; Ahmed, Muhammad I.; Qamaruddin, Muhammad; Yamani, Zain H.

    2015-02-01

    Development of nanostructured photocatalysts for harnessing solar energy in energy-efficient and environmentally benign way remains an important area of research. Pure and WO3-surface modified thin films of TiO2 were prepared by magnetron sputtering on indium tin oxide glass, and photoelectrochemical and photocatalytic activities of these films were studied. TiO2 particles were <50 nm, while deposited WO3 particles were <20 nm in size. An enhancement in the photocurrent was observed when the TiO2 surface was modified WO3 nanoparticles. Effect of potential, WO3 amount, and radiations of different wavelengths on the photoelectrochemical activity of TiO2 electrodes was investigated. Photocatalytic activity of TiO2 and WO3-modified TiO2 for the decolorization of methyl orange was tested.

  2. Fabrication and Film Qualification of Sr Modified Pb(Ca) TiO3 Thin Films

    International Nuclear Information System (INIS)

    Naw Hla Myat San; Khin Aye Thwe; Than Than Win; Yin Maung Maung; Ko Ko Kyaw Soe

    2011-12-01

    Strontium and calcium - modified lead titanate (Pb0.7 Ca0.15 Sr0.15 ) TiO3 (PCST)thin films were prepared by using spin coating technique. Phase transition of PCST was interpreted by means of Er-T characteristics. Process temperature dependence on micro-structure of PCST film was studied. Charge conduction mechanism of PCST thin film was also investigated for film qualification.

  3. Photocatalytic decomposition of diclofenac potassium using silver-modified TiO2 thin films

    International Nuclear Information System (INIS)

    Cavalheiro, A.A.; Bruno, J.C.; Saeki, M.J.; Valente, J.P.S.; Florentino, A.O.

    2008-01-01

    The effects of silver insertion on the TiO 2 photocatalytic activity for the degradation of diclofenac potassium were reported here. Techniques such as X-ray diffraction, scanning electron microscopy and UV-Vis spectroscopy were used to comprehend the relation between structure and properties of the silver-modified TiO 2 thin films obtained by the sol-gel method. The lattice parameters and the crystallinity of TiO 2 anatase phase were affected by inserted silver, and the film thickness increased about 4 nm for each 1 wt.% of silver inserted. The degradation of diclofenac potassium and by-products reached an efficiency of 4.6 mg C W -1 when the material was modified with silver. Although the first step of degradation involves only the photochemical process related to the loss of the chlorine and hydrogen atoms. This cyclization reaction leads to the formation of intermediate, which degradation is facilitated by the modified material

  4. Photocatalytic decomposition of diclofenac potassium using silver-modified TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Cavalheiro, A.A. [Depto de Quimica - Instituto de Biociencias - UNESP, Distrito de Rubiao Junior, s/n, Zip Code 18.618-000, P.O. Box 510, Botucatu, SP (Brazil)], E-mail: albecava@bol.com.br; Bruno, J.C.; Saeki, M.J.; Valente, J.P.S.; Florentino, A.O. [Depto de Quimica - Instituto de Biociencias - UNESP, Distrito de Rubiao Junior, s/n, Zip Code 18.618-000, P.O. Box 510, Botucatu, SP (Brazil)

    2008-07-31

    The effects of silver insertion on the TiO{sub 2} photocatalytic activity for the degradation of diclofenac potassium were reported here. Techniques such as X-ray diffraction, scanning electron microscopy and UV-Vis spectroscopy were used to comprehend the relation between structure and properties of the silver-modified TiO{sub 2} thin films obtained by the sol-gel method. The lattice parameters and the crystallinity of TiO{sub 2} anatase phase were affected by inserted silver, and the film thickness increased about 4 nm for each 1 wt.% of silver inserted. The degradation of diclofenac potassium and by-products reached an efficiency of 4.6 mg{sub C} W{sup -1} when the material was modified with silver. Although the first step of degradation involves only the photochemical process related to the loss of the chlorine and hydrogen atoms. This cyclization reaction leads to the formation of intermediate, which degradation is facilitated by the modified material.

  5. Characterization and electrochemical studies of Nafion/nano-TiO2 film modified electrodes

    International Nuclear Information System (INIS)

    Yuan Shuai; Hu Shengshui

    2004-01-01

    A nano-TiO 2 film from stable aqueous dispersion has been modified on a glassy carbon electrode (GCE), and was characterized by scanning electron microscopy (SEM) and surface-enhanced Raman spectroscopy (SERS). This nanostructured film exhibits an ability to improve the electron-transfer rate between electrode and dopamine (DA), and electrocatalyze the redox of DA. The electrocatalytical behavior of DA was examined by cyclic voltammetry (CV). Combined with Nafion, the bilayer-modified electrode (N/T/GCE) gives a sensitive voltammetric response of DA regardless of excess ascorbic acid (AA). Electrochemical impedance spectroscopy (EIS) at a fixed potential was performed at variously treated GCEs. The mechanism of the electrode reaction of DA at N/T/GCE and the equivalent circuits of different GCEs have been proposed

  6. Preparation of Oleyl Phosphate-Modified TiO2/Poly(methyl methacrylate Hybrid Thin Films for Investigation of Their Optical Properties

    Directory of Open Access Journals (Sweden)

    Masato Fujita

    2015-01-01

    Full Text Available TiO2 nanoparticles (NPs modified with oleyl phosphate were synthesized through stable Ti–O–P bonds and were utilized to prepare poly(methyl methacrylate- (PMMA- based hybrid thin films via the ex situ route for investigation of their optical properties. After surface modification of TiO2 NPs with oleyl phosphate, IR and 13C CP/MAS NMR spectroscopy showed the presence of oleyl groups. The solid-state 31P MAS NMR spectrum of the product revealed that the signal due to oleyl phosphate (OP shifted upon reaction, indicating formation of covalent Ti–O–P bonds. The modified TiO2 NPs could be homogeneously dispersed in toluene, and the median size was 16.1 nm, which is likely to be sufficient to suppress Rayleigh scattering effectively. The TEM images of TiO2/PMMA hybrid thin films also showed a homogeneous dispersion of TiO2 NPs, and they exhibited excellent optical transparency even though the TiO2 content was 20 vol%. The refractive indices of the OP-modified TiO2/PMMA hybrid thin films changed higher with increases in TiO2 volume fraction, and the hybrid thin film with 20 vol% of TiO2 showed the highest refractive index (n = 1.86.

  7. Studies on Gas Sensing Performance of Pure and Surface Modified SrTiO3 Thick Film Resistors

    Directory of Open Access Journals (Sweden)

    V. B. Gaikwad

    2009-08-01

    Full Text Available Strontium Titanate (SrTiO3 (ST was prepared mechanochemically from Sr(OH2 and TiO2. XRD confirms the Perovskite phase of material. Thick films of ST were prepared by screen-printing technique. The gas sensing performances of thick films were tested for various gases. It showed maximum sensitivity to CO gas at 350 oC for 100 ppm gas concentration. To improve the sensitivity and selectivity of the film towards a particular gas, ST thick films were surface modified by dipping them in a solution of nano copper for different intervals of time. These surface modified ST films showed larger sensitivity to H2S gas (100 ppm at 300 oC than pure ST film. A systematic study, of sensing performance of the sensor, indicates the key role-played by the nano copper species on the surface .The sensitivity, selectivity, response and recovery time of the sensor were measured and presented.

  8. TiO2 Films Modified with Au Nanoclusters as Self-Cleaning Surfaces under Visible Light

    Directory of Open Access Journals (Sweden)

    Ting-Wei Liao

    2018-01-01

    Full Text Available In this study, we applied cluster beam deposition (CBD as a new approach for fabricating efficient plasmon-based photocatalytic materials. Au nanoclusters (AuNCs produced in the gas phase were deposited on TiO2 P25-coated silicon wafers with coverage ranging from 2 to 8 atomic monolayer (ML equivalents. Scanning Electron Microscopy (SEM images of the AuNCs modified TiO2 P25 films show that the surface is uniformly covered by the AuNCs that remain isolated at low coverage (2 ML, 4 ML and aggregate at higher coverage (8 ML. A clear relationship between AuNCs coverage and photocatalytic activity towards stearic acid photo-oxidation was measured, both under ultraviolet and green light illumination. TiO2 P25 covered with 4 ML AuNCs showed the best stearic acid photo-oxidation performance under green light illumination (Formal Quantum Efficiency 1.6 × 10−6 over a period of 93 h. These results demonstrate the large potential of gas-phase AuNCs beam deposition technology for the fabrication of visible light active plasmonic photocatalysts.

  9. Comparative study of the anchorage and the catalytic properties of nanoporous TiO2 films modified with ruthenium (II) and rhenium (I) carbonyl complexes

    Science.gov (United States)

    Oyarzún, Diego P.; Chardon-Noblat, Sylvie; Linarez Pérez, Omar E.; López Teijelo, Manuel; Zúñiga, César; Zarate, Ximena; Shott, Eduardo; Carreño, Alexander; Arratia-Perez, Ramiro

    2018-02-01

    In this article we study the anchoring of cis-[Ru(bpyC4pyr)(CO)2(CH3CN)2]2+, cis-[Ru(bpy)2(CO)2]2+ and cis-[Ru(bpyac)(CO)2Cl2], onto nanoporous TiO2 employing electropolymerization, electrostatic interaction and chemical bonding. Also, the [Re(bpyac)(CO)3Cl] rhenium(I) complex for chemical anchorage was analyzed. The characterization of TiO2/Ru(II) and TiO2/Re(I) nanocomposite films was performed by field emission scanning electron microscopy (FESEM), electron dispersive X-ray spectroscopy (EDS) and Raman spectroscopy. In addition, for the more stable nanocomposites obtained, the catalytic properties (solar energy conversion and CO2 reduction) were evaluated. The efficiency improvement in redox process derived from the (photo)electrochemical evidence indicates that modified nanoporous TiO2 structures enhance the rate of charge transfer reactions.

  10. Characterization of n-TiO2 thin films modified with silver nanoparticles

    International Nuclear Information System (INIS)

    Cueto, L.F.; Sanchez-Cervantes, E.M.

    2010-01-01

    Carbon dioxide accumulation in the atmosphere has gained much attention and has reopened many research lines that initiated two or three decades ago. Electrochemical reduction represents one of the most discussed methods, especially where semiconductor and metal-semiconductor cathodes are used to achieve CO 2 transformation into higher-energy products. In the present work, the influence of silver nanoparticles upon CO 2 reduction on n-TiO 2 cathodes in aqueous media is presented. Silver nanoparticles with an average diameter of 250nm were deposited on n-TiO 2 surfaces by the electrochemical Double-Pulse Potential method. A Grazing-Incidence X-Ray Diffraction structural analysis is presented showing the presence of metallic silver, while Atomic Force Microscopy shows surface roughness and particle size before and after surface modification. These measurements were confirmed by Scanning-Electron Microscopy acquainting for the formation of metal particles on the n-TiO 2 surface. Enhancement of CO 2 reduction by the presence of silver on cathodes is shown by cyclic voltammetry. (author)

  11. Effect of metal ion dopants on photochemical properties of anatase TiO{sub 2} films synthesized by a modified sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Yuan Zhangfu [Multi-Phase Reaction Laboratory, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 10080 (China)]. E-mail: yuanzhf@home.ipe.ac.cn; Zhang Junling [Multi-Phase Reaction Laboratory, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 10080 (China); Graduate University of Chinese Academy of Sciences, Beijing 100049 (China); Li Bin [Multi-Phase Reaction Laboratory, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 10080 (China); Graduate University of Chinese Academy of Sciences, Beijing 100049 (China); Li Jianqiang [Multi-Phase Reaction Laboratory, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 10080 (China)

    2007-06-25

    Anatase TiO{sub 2} films were successfully synthesized by a modified sol-gel method wherein peroxo titanic acid solution was derived from TiCl{sub 4}/ethanol/water solution at room temperature. The as-prepared films were further surface-doped by photodeposited Fe{sub 2}O{sub 3} and Cr{sub 2}O{sub 3} to improve its physicochemical properties. The phase and structure of the films were investigated by X-ray diffraction, scanning electron microscopy and X-ray photoelectron spectroscopy. The physicochemical properties of the films were also measured. The results show that both hydrophilicity and photocatalytic activity of the films were remarkably improved by doping transition metal ion Fe{sup 3+}. In case of Cr{sup 3+} doped films, hydrophilicity was also significantly enhanced but photocatalytic activity for methyl orange under UV irradiation was still comparable with the undoped films.

  12. Modification of oxide films by ion implantation: TiO2-films modified by Ti+ and O+ as example

    International Nuclear Information System (INIS)

    Schultze, J.W.; Elfenthal, L.; Leitner, K.; Meyer, O.

    1988-01-01

    Oxide films can be modified by ion implantation. Changes in the electrochemical properties of the films are due to the deposition profile of the implanted ion, ie doping and stoichiometric changes, as well as to the radiation damage. The latter is due to the formation of Frenkel defects and at high concentrations to a complete amorphization of the oxide film. TiOsub(x)-films with 1 + - and O + -ions into anodic oxide films on titanium. The electrode capacity shows always the behaviour of an n-type semiconductor with an almost constant flatband potential but a strong maximum donor concentration at about 3% Ti + concentration. Oxygen implantation, on the other hand, causes a small increase of donor concentration only at high concentration of O + . Electron transfer reactions show strong modifications of the electronic behaviour of the oxide film with a maximum again at 3% titanium. Photocurrent spectra prove the increasing amorphization and show interband states 2.6 eV above the VB or below the CB. During repassivation measurements at various potentials different defects formed by Ti + - and O + -implantation become mobile. A tentative model of the band structure is constructed which takes into account the interband states due to localised Ti + - and O + -ions. The modification of ion implanted oxide films is compared with the effects of other preparation techniques. (author)

  13. Near Infrared Lateral Photovoltaic Effect in LaTiO3 Films

    Directory of Open Access Journals (Sweden)

    Wujun Jin

    2013-01-01

    Full Text Available We have reported on the lateral photovoltaic effect of LaTiO3 films epitaxially grown on (100 SrTiO3 substrates. Under illumination of continuous 1064 nm laser beam on the LaTiO3 film through SrTiO3 substrate, the open-circuit photovoltage depended linearly on the illuminated position. The photosensitivity can be modified by bias current. These results indicated that the LaTiO3 films give rise to a potentially photoelectronic device for near infrared position-sensitive detection.

  14. Silver film on nanocrystalline TiO{sub 2} support: Photocatalytic and antimicrobial ability

    Energy Technology Data Exchange (ETDEWEB)

    Vukoje, Ivana D., E-mail: ivanav@vinca.rs [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, 11000 Belgrade (Serbia); Tomašević-Ilić, Tijana D., E-mail: tommashev@gmail.com [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, 11000 Belgrade (Serbia); Zarubica, Aleksandra R., E-mail: zarubica2000@yahoo.com [Department of Chemistry, Faculty of Science and Mathematics, University of Niš, Višegradska 33, 18000 Niš (Serbia); Dimitrijević, Suzana, E-mail: suzana@tmf.bg.ac.rs [Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade (Serbia); Budimir, Milica D., E-mail: mickbudimir@gmail.com [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, 11000 Belgrade (Serbia); Vranješ, Mila R., E-mail: mila@vinca.rs [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, 11000 Belgrade (Serbia); Šaponjić, Zoran V., E-mail: saponjic@vinca.rs [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, 11000 Belgrade (Serbia); Nedeljković, Jovan M., E-mail: jovned@vinca.rs [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, 11000 Belgrade (Serbia)

    2014-12-15

    Highlights: • Simple photocatalytic rout for deposition of Ag on nanocrystalline TiO{sub 2} films. • High antibactericidal efficiency of deposited Ag on TiO{sub 2} support. • Improved photocatalytic performance of TiO{sub 2} films in the presence of deposited Ag. - Abstract: Nanocrystalline TiO{sub 2} films were prepared on glass slides by the dip coating technique using colloidal solutions consisting of 4.5 nm particles as a precursor. Photoirradiation of nanocrystalline TiO{sub 2} film modified with alanine that covalently binds to the surface of TiO{sub 2} and at the same time chelate silver ions induced formation of metallic silver film. Optical and morphological properties of thin silver films on nanocrystalline TiO{sub 2} support were studied by absorption spectroscopy and atomic force microscopy. Improvement of photocatalytic performance of nanocrystalline TiO{sub 2} films after deposition of silver was observed in degradation reaction of crystal violet. Antimicrobial ability of deposited silver films on nanocrystalline TiO{sub 2} support was tested in dark as a function of time against Escherichia coli, Staphylococcus aureus, and Candida albicans. The silver films ensured maximum cells reduction of both bacteria, while the fungi reduction reached satisfactory 98.45% after 24 h of contact.

  15. Nonstoichiometry of Epitaxial FeTiO(3+delta) Films

    Science.gov (United States)

    2003-01-01

    nonstoichiometry of the FeTiO3 +8 films was probably produced by cation vacancies and disarrangement of Fe3+ and Ti4 ions, which randomly occupied both interstitial...and substitutional sites of the FeTiO 3 related structure. INTRODUCTION Solid solutions of ot-Fe20 3- FeTiO3 (hematite-ilmenite) series are known to...tried to confirm preparation conditions of stoichiometric FeTiO 3 films. According to a literature on bulk crystal growth of FeTiO3 [5], very low oxygen

  16. Effects of TiO{sub 2} buffer layer on the photoelectrochemical properties of TiO{sub 2} Nano rods grown by modified chemical bath deposition method

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Tae-hyun; Ha, Jin-wook; Ryu, Hyukhyun [Inje University, Gimhae (Korea, Republic of); Lee, Won-Jae [Dong-Eui University, Busan (Korea, Republic of)

    2015-08-15

    In this study, we grew TiO{sub 2} nano rods on TiO{sub 2}-film buffered FTO substrate using modified chemical bath deposition (M-CBD). The TiO{sub 2} buffer layer was grown by spin coating method with different RPM (revolutions per minute) values and deposition cycles. We investigated the effects of the RPM values and the deposition cycles on the morphological, structural and photoelectrochemical properties of TiO{sub 2} nano rods. In this work, we have also found that the morphological and structural properties of TiO{sub 2} nano rods affected the photoelectrochemical properties of TiO{sub 2} nano rods. And the maximum photocurrent density of 0.34 mA/cm{sup 2} at 0.6V (vs.SCE) was obtained from the buffer layer deposition process condition of 4,000 RPM and two-times buffer layer depositions.

  17. Photocatalytically active Au/TiO2 films deposited by two-step spray pyrolysis

    International Nuclear Information System (INIS)

    Balashev, Konstantin; Georgiev, Petar; Simeonova, Sylvia; Stambolova, Irina; Blaskov, Vladimir; Vassilev, Sasho; Eliyas, Alexander

    2016-01-01

    Nanocrystalline TiO 2 and surface gold-modified films (Au/TiO 2 ) are obtained by two step spray pyrolysis process. Titanium tetrachloride (TiCl 4 ) was used as inorganic titanium precursor. The Au nanoparticles were deposited on the surface of sprayed TiO 2 films, obtained by the classical Turkevich method. The AFM analyses have revealed that the roughness of Au/TiO 2 is twice lower than that of the reference titania film. Some globular species are visible on the surface, which could be either individual Au nanoparticles or Au nanoparticles’ agglomerates embedded into the TiO 2 film. The photocatalytic activity in the oxidative degradation of Reactive Black 5 dye under visible light of the Au/TiO 2 films was estimated in a semi-batch reactor. Surface gold modified TiO 2 films revealed higher photocatalytic efficiency than the reference sample. Key words: Au nanoparticles, photocatalysis, azo dye, titania, nanosized

  18. TiO2 and Cu/TiO2 Thin Films Prepared by SPT

    Directory of Open Access Journals (Sweden)

    S. S. Roy

    2015-12-01

    Full Text Available Titanium oxide (TiO2 and copper (Cu doped titanium oxide (Cu/TiO2 thin films have been prepared by spray pyrolysis technique. Titanium chloride (TiCl4 and copper acetate (Cu(CH3COO2.H2O were used as source of Ti and Cu. The doping concentration of Cu was varied from 1-10 wt. %. The X-ray diffraction studies show that TiO2 thin films are tetragonal structure and Cu/TiO2 thin films implies CuO has present with monoclinic structure. The optical properties of the TiO2 thin films have been investigated as a function of Cu-doping level. The optical transmission of the thin films was found to increase from 88 % to 94 % with the addition of Cu up to 8 % and then decreases for higher percentage of Cu doping. The optical band gap (Eg for pure TiO2 thin film is found to be 3.40 eV. Due to Cu doping, the band gap is shifted to lower energies and then increases further with increasing the concentration of Cu. The refractive index of the TiO2 thin films is found to be 2.58 and the variation of refractive index is observed due to Cu doped. The room temperature resistivity of the films decreases with increasing Cu doping and is found to be 27.50 - 23.76 W·cm. It is evident from the present study that the Cu doping promoted the thin film morphology and thereby it is aspect for various applications.

  19. Influence of the Porosity of the TiO2 Film on the Performance of the Perovskite Solar Cell

    Directory of Open Access Journals (Sweden)

    Xiaodan Sun

    2017-01-01

    Full Text Available The structure of mesoporous TiO2 (mp-TiO2 films is crucial to the performance of mesoporous perovskite solar cells (PSCs. In this study, we fabricated highly porous mp-TiO2 films by doping polystyrene (PS spheres in TiO2 paste. The composition of the perovskite films was effectively improved by modifying the mass fraction of the PS spheres in the TiO2 paste. Due to the high porosity of the mp-TiO2 film, PbI2 and CH3NH3I could sufficiently infiltrate into the network of the mp-TiO2 film, which ensured a more complete transformation to CH3NH3PbI3. The surface morphology of the mp-TiO2 film and the photoelectric performance of the perovskite solar cells were investigated. The results showed that an increase in the porosity of the mp-TiO2 film resulted in an improvement in the performance of the PSCs. The best device with the optimized mass fraction of 1.0 wt% PS in TiO2 paste exhibited an efficiency of 12.69%, which is 25% higher than the efficiency of the PSCs without PS spheres.

  20. Optical properties of SrTiO3 films

    International Nuclear Information System (INIS)

    Agasiyev, A.A.; Magerramov, E.M.; Mammadov, M.Z.; Sarmasov, S.M.

    2010-01-01

    The spectrums of optical absorption of amorphous and single crystalline films SrTiO 3 at temperatures : 105 K, 300 K, 400 K are investigated. The temperature dependences of slope absorption edge, forbidden gap and characteristic constant of Urbah rule are obtained. The forbidden gap of single crystalline film SrTiO 3 and average shift shift of absorption edge degree are defined. It is established that edge of optical absorption of SrTiO 3 film is obeyed to Urbah rule and the absorption in the investigated region is caused by the transition of electron interacting with phonon

  1. Chemically synthesized TiO2 and PANI/TiO2 thin films for ethanol sensing applications

    Science.gov (United States)

    Gawri, Isha; Ridhi, R.; Singh, K. P.; Tripathi, S. K.

    2018-02-01

    Ethanol sensing properties of chemically synthesized titanium dioxide (TiO2) and polyaniline/titanium dioxide nanocomposites (PANI/TiO2) had been performed at room temperature. In-situ oxidative polymerization process had been employed with aniline as a monomer in presence of anatase titanium dioxide nanoparticles. The prepared samples were structurally and morphologically characterized by x-ray diffraction, fourier transform infrared spectra, high resolution-transmission electron microscopy and field emission-scanning electron microscopy. The crystallinity of PANI/TiO2 nanocomposite was revealed by XRD and FTIR spectra confirmed the presence of chemical bonding between the polymer chains and metal oxide nanoparticles. HR-TEM micrographs depicted that TiO2 particles were embedded in polymer matrix, which provides an advantage over pure TiO2 nanoparticles in efficient adsorption of vapours. These images also revealed that the TiO2 nanoparticles were irregular in shape with size around 17 nm. FE-SEM studies revealed that in the porous structure of PANI/TiO2 film, the intercalation of TiO2 in PANI chains provides an advantage over pure TiO2 film for uniform interaction with ethanol vapors. The sensitivity values of prepared samples were examined towards ethanol vapours at room temperature. The PANI/TiO2 nanocomposite exhibited better sensing response and faster response-recovery examined at different ethanol concentrations ranging from 5 ppm to 20 ppm in comparison to pure TiO2 nanoparticles. The increase in vapour sensing of PANI/TiO2 sensing film as compared to pure TiO2 film had been explained in detail with the help of gas sensing mechanism of TiO2 and PANI/TiO2. This provides strong evidence that gas sensing properties of TiO2 had been considerably improved and enhanced with the addition of polymer matrix.

  2. Dopamine/TiO{sub 2} hybrid thin films prepared by the liquid phase deposition method

    Energy Technology Data Exchange (ETDEWEB)

    Gutierrez-Tauste, David [Departament de Quimica, Universitat Autonoma de Barcelona, Campus UAB, Edifici Cn, 08290 Cerdanyola del Valles, Barcelona (Spain)], E-mail: davidg@qf.uab.es; Domenech, Xavier [Departament de Quimica, Universitat Autonoma de Barcelona, Campus UAB, Edifici Cn, 08290 Cerdanyola del Valles, Barcelona (Spain); Domingo, Concepcion [Instituto de Ciencia de Materiales (CSIC), Campus UAB, 08290 Cerdanyola del Valles, Barcelona (Spain); Ayllon, Jose A. [Departament de Quimica, Universitat Autonoma de Barcelona, Campus UAB, Edifici Cn, 08290 Cerdanyola del Valles, Barcelona (Spain)

    2008-04-30

    Liquid phase deposition method is applied to one-step production of a hybrid material composed by dopamine(DA) and TiO{sub 2} anatase. An optimized amount of the enediol derivative is added to a fluoride titania precursor aqueous solution in order to entrap this modifier within the growing TiO{sub 2}, yielding a DA/TiO{sub 2} nanocomposite material. Uniform, well-adhered and brown-colored thin films are deposited on indium tin oxide covered glass substrate. The DA/TiO{sub 2} hybrid material has been characterized by infrared spectroscopy, electronic microscopy, X-ray diffraction and UV-vis spectroscopy. The formation of the hybrid material seems to be reasonably explained by linkage of different TiO{sub 2} nanocrystallites taking advantage of both enediol and amine groups of DA.

  3. Au-TiO2/Chit modified sensor for electrochemical detection of trace organophosphates insecticides.

    Science.gov (United States)

    Qu, Yunhe; Min, Hong; Wei, Yinyin; Xiao, Fei; Shi, Guoyue; Li, Xiaohua; Jin, Litong

    2008-08-15

    In this paper, Au-TiO2/Chit modified electrode was prepared with Au-TiO2 nanocomposite (Au-TiO2) and Chitosan (Chit) as a conjunct. The Au-TiO2 nanocomposite and the films were characterized by electrochemical and spectroscopy methods. A set of experimental conditions was also optimized for the film's fabrication. The electrochemical and electrocatalytic behaviors of Au-TiO2/Chit modified electrode to trace organophosphates (OPs) insecticides such as parathion were discussed in this work. By differential pulse voltammetry (DPV) measurement, the current responses of Au-TiO2/Chit modified electrode were linear with parathion concentration ranging from 1.0 ng/ml to 7.0 x 10(3)ng/ml with the detection limit of 0.5 ng/ml. In order to evaluate the performance of the detection system, we also examined the real samples successfully in this work. It exhibited a sensitive, rapid and easy-to-use method for the fast determination of trace OPs insecticides.

  4. TiO2 thin-films on polymer substrates and their photocatalytic activity

    International Nuclear Information System (INIS)

    Yang, Jae-Hun; Han, Yang-Su; Choy, Jin-Ho

    2006-01-01

    We have developed dip-coating process for TiO 2 -thin film on polymer substrates (acrylonitrile-butadiene-styrene polymer: ABS, polystyrene: PS). At first, a monodispersed and transparent TiO 2 nano-sol solution was prepared by the controlled hydrolysis of titanium iso-propoxide in the presence of acetylacetone and nitric acid catalyst at 80 deg. C. Powder X-ray diffraction patterns of the dried particles are indicative of crystalline TiO 2 with anatase-type structure. According to the XRD and transmission electron microscopy (TEM) studies, the mean particle size was estimated to be ca. 5 nm. The transparent thin films on ABS and PS substrates were fabricated by dip-coating process by changing the processing variables, such as the number of dip-coating and TiO 2 concentration in nano-sol solution. Scanning electron microscopic (SEM) analysis for the thin film samples reveals that the acetylacetone-modified TiO 2 nano-sol particles are effective for enhancing the interfacial adherence between films and polymeric substrates compared to the unmodified one. Photocatalytic degradation of methylene blue (MB) on the TiO 2 thin-films has also been systematically investigated

  5. Nanocrystalline TiO2 Composite Films for the Photodegradation of Formaldehyde and Oxytetracycline under Visible Light Irradiation

    Directory of Open Access Journals (Sweden)

    Min Wei

    2017-06-01

    Full Text Available In order to effectively photodegradate organic pollutants, ZnO composite and Co-B codoped TiO2 films were successfully deposited on glass substrates via a modified sol-gel method and a controllable dip-coating technique. Combining with UV–Vis diffuse reflectance spectroscopy (DRS and photoluminescence spectra (PL analyses, the multi-modification could not only extend the optical response of TiO2 to visible light region but also decrease the recombination rate of electron-hole pairs. XRD results revealed that the multi-modified TiO2 film had an anatase-brookite biphase heterostructure. FE-SEM results indicated that the multi-modified TiO2 film without cracks was composed of smaller round-like nanoparticles compared to pure TiO2. BET surface area results showed that the specific surface area of pure TiO2 and the multi-modified TiO2 sample was 47.8 and 115.8 m2/g, respectively. By degradation of formaldehyde and oxytetracycline, experimental results showed that the multi-modified TiO2 film had excellent photodegradation performance under visible light irradiation.

  6. Graphene Oxide-TiO2 Nanocomposite Films for Electron Transport Applications

    Science.gov (United States)

    Saleem, Abida; Ullah, Naveed; Khursheed, Kamran; Iqbal, Tahir; Shah, Saqlain A.; Asjad, Muhammad; Sarwar, Nazim; Saleem, Murtaza; Arshad, Muhammad

    2018-03-01

    Graphene oxide-titanium dioxide (GO-TiO2) nanocomposite thin films were prepared for application as the window layer of perovskite solar cells. Graphene oxide (GO) was prepared by a modified Hummer's method, and titanium dioxide (TiO2) nanoparticles were synthesized by hydrothermal solution method. Thin films of GO-TiO2 nanocomposite were prepared with different wt.% of GO by spin coating on indium tin oxide (ITO) substrate followed by annealing at 150°C. X-ray diffraction analysis revealed rutile phase of TiO2 nanostructures. The bandgap of the pure TiO2 thin film was found to be 3.5 eV, reducing to 2.9 eV for the GO-TiO2 nanocomposites with a red-shift towards higher wavelength. Furthermore, thermal postannealing at 400°C improved the transparency in the visible region and decreased the sheet resistance. Morphological and elemental analysis was performed by scanning electron microscopy and energy-dispersive x-ray spectroscopy, respectively. The current-voltage characteristic of the GO-TiO2 nanocomposites indicated Ohmic contact with the ITO substrate. The chemical composition of the as-synthesized GO-TiO2 nanocomposites was investigated by x-ray photoelectron spectroscopy (XPS). The results presented herein demonstrate a new, low-temperature solution-processing approach to obtain rGO-TiO2 composite material for use as the electron transport layer of perovskite solar cells.

  7. SURFACE MODIFICATION OF SEMICONDUCTOR THIN FILM OF TiO2 ON GRAPHITE SUBSTRATE BY Cu-ELECTRODEPOSITION

    Directory of Open Access Journals (Sweden)

    Fitria Rahmawati

    2010-06-01

    Full Text Available Surface modification of graphite/TiO2 has been done by mean of Cu electrodeposition. This research aims to study the effect of Cu electrodeposition on photocatalytic enhancing of TiO2. Electrodeposition has been done using CuSO4 0,4 M as the electrolyte at controlled current. The XRD pattern of modified TiO2 thin film on graphite substrate exhibited new peaks at 2θ= 43-44o and 2θ= 50-51o that have been identified as Cu with crystal cubic system, face-centered crystal lattice and crystallite size of 26-30 nm. CTABr still remains in the material as impurities. Meanwhile, based on morphological analysis, Cu particles are dissipated in the pore of thin film. Graphite/TiO2/Cu has higher photoconversion efficiency than graphite/TiO2.   Keywords: semiconductor, graphite/TiO2, Cu electrodeposition

  8. Visible light active TiO2 films prepared by electron beam deposition of noble metals

    International Nuclear Information System (INIS)

    Hou Xinggang; Ma Jun; Liu Andong; Li Dejun; Huang Meidong; Deng Xiangyun

    2010-01-01

    TiO 2 films prepared by sol-gel method were modified by electron beam deposition of noble metals (Pt, Pd, and Ag). Effects of noble metals on the chemical and surface characteristics of the films were studied using XPS, TEM and UV-Vis spectroscopy techniques. Photocatalytic activity of modified TiO 2 films was evaluated by studying the degradation of methyl orange dye solution under visible light UV irradiation. The result of TEM reveals that most of the surface area of TiO 2 is covered by tiny particles of noble metals with diameter less than 1 nm. Broad red shift of UV-Visible absorption band of modified photocatalysts was observed. The catalytic degradation of methyl orange in aqueous solutions under visible light illumination demonstrates a significant enhancement of photocatalytic activity of these films compared with the un-loaded films. The photocatalytic efficiency of modified TiO 2 films by this method is affected by the concentration of impregnating solution.

  9. The microstructure and wettability of the TiO{sub x} films synthesized by reactive DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lin Zeng [School of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004 (China); State Key Laboratory of Plastic Forming Simulation and Die and Mould Technology Wuhan, Hubei 430074 (China)], E-mail: linzengsy@gmail.com; Liu Kun; Zhang Yichen; Yue Xiangji; Song Guiqiu [School of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004 (China); Ba Dechun [School of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004 (China)], E-mail: dechunba@yahoo.com

    2009-01-25

    Different chemical state of titanium oxide films were deposited on commercially pure Ti (CP Ti) by reactive DC magnetron sputtering under different oxygen flow rates to examine a possibility of their applications to endovascular stents. The chemical composition and crystal structure of the obtained films were analyzed by XPS and XRD, respectively. In dependence on the deposition parameters employed, the obtained films demonstrated different mixture of anatase TiO{sub 2}, Ti{sub 2}O{sub 3}, TiO and Ti. The wettability of the films was measured by the water contact angle variation. By formation of titanium oxide film on CP Ti, contact angle was decreased. In order to modify and control the surface wettability, the resultant TiO{sub x} films were etched subsequently by different plasma. The wettability was influenced by etched process according to the decreased contact angle values of etched TiO{sub x} film. Furthermore, TiO{sub x} films became highly hydrophilic by ultraviolet (UV) irradiation, and returned to the initial relatively hydrophobic state by visible-light (VIS) irradiation. The wettability of the TiO{sub x} film was enabled to convert between hydrophilic and hydrophobic reversibly by alternative UV and VIS irradiation. By adjusting deposition parameter and further modification process, the wettability of the TiO{sub x} films can be changed freely in the range of 0-90 deg.

  10. Photodegradation properties and optics of Ag/TiO2 films

    International Nuclear Information System (INIS)

    Tirado G, S.; Valenzuela Z, M. A.

    2016-10-01

    In the thin semiconductor films of Ag/TiO 2 the topographic properties were recorded by atomic force microscopy and the main parameters of roughness were determined; the optical properties were also recorded when determining their transmittance degree, their refractive indexes, their thickness and the bandwidth of the semiconductor Eg, both for pure TiO 2 films and the modified Ag/TiO 2 films with various layers of the Ag catalyst. The Ag/TiO 2 films that were grown by sol-gel and repeated immersion, chemical technique that has been used in the development of thin film technology, were carried out in photo catalysis, when are used in photo degradation of methyl orange at an aqueous concentration of 14 ppm, once they are characterized with several techniques required to be able to explain the possible photo catalytic reactions at the solid-aqueous interface, when irradiated with UV; with the possible application in water treatment. The photoluminescence spectra of the prepared Ag/TiO 2 samples are reported, which resulted in a green emission, characteristic of the visible, in addition to emissions in the UV range. (Author)

  11. Photodegradation properties and optics of Ag/TiO{sub 2} films; Propiedades de fotodegradacion y opticas de peliculas Ag/TiO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Tirado G, S. [IPN, Escuela Superior de Fisica y Matematicas, San Pedro Zacatenco, 07738 Ciudad de Mexico (Mexico); Valenzuela Z, M. A., E-mail: tirado@esfm.ipn.mx [IPN, Escuela Superior de Ingenieria Quimica e Industrias Extractivas, Laboratorio de Catalisis y Materiales, San Pedro Zacatenco, 07738 Ciudad de Mexico (Mexico)

    2016-10-15

    In the thin semiconductor films of Ag/TiO{sub 2} the topographic properties were recorded by atomic force microscopy and the main parameters of roughness were determined; the optical properties were also recorded when determining their transmittance degree, their refractive indexes, their thickness and the bandwidth of the semiconductor Eg, both for pure TiO{sub 2} films and the modified Ag/TiO{sub 2} films with various layers of the Ag catalyst. The Ag/TiO{sub 2} films that were grown by sol-gel and repeated immersion, chemical technique that has been used in the development of thin film technology, were carried out in photo catalysis, when are used in photo degradation of methyl orange at an aqueous concentration of 14 ppm, once they are characterized with several techniques required to be able to explain the possible photo catalytic reactions at the solid-aqueous interface, when irradiated with UV; with the possible application in water treatment. The photoluminescence spectra of the prepared Ag/TiO{sub 2} samples are reported, which resulted in a green emission, characteristic of the visible, in addition to emissions in the UV range. (Author)

  12. Tuning thermal conductivity in homoepitaxial SrTiO{sub 3} films via defects

    Energy Technology Data Exchange (ETDEWEB)

    Brooks, Charles M. [Department of Materials Science and Engineering, Cornell University, Ithaca, New York 14853-1501 (United States); Department of Materials Science and Engineering, Pennsylvania State University, University Park, Pennsylvania 16802 (United States); Wilson, Richard B.; Cahill, David G. [Department of Materials Science and Engineering and Materials Research Laboratory, University of Illinois, Urbana, Illinois 61801 (United States); Schäfer, Anna; Schubert, Jürgen [Peter Grünberg Institute (PGI9-IT), JARA-Fundamentals of Future Information Technology, Research Centre Jülich, D-52425 Jülich (Germany); Mundy, Julia A.; Holtz, Megan E. [School of Applied and Engineering Physics, Cornell University, Ithaca, New York 14853 (United States); Muller, David A. [School of Applied and Engineering Physics, Cornell University, Ithaca, New York 14853 (United States); Kavli Institute at Cornell for Nanoscale Science, Ithaca, New York 14853 (United States); Schlom, Darrell G. [Department of Materials Science and Engineering, Cornell University, Ithaca, New York 14853-1501 (United States); Kavli Institute at Cornell for Nanoscale Science, Ithaca, New York 14853 (United States)

    2015-08-03

    We demonstrate the ability to tune the thermal conductivity of homoepitaxial SrTiO{sub 3} films deposited by reactive molecular-beam epitaxy by varying growth temperature, oxidation environment, and cation stoichiometry. Both point defects and planar defects decrease the longitudinal thermal conductivity (k{sub 33}), with the greatest decrease in films of the same composition observed for films containing planar defects oriented perpendicular to the direction of heat flow. The longitudinal thermal conductivity can be modified by as much as 80%—from 11.5 W m{sup −1}K{sup −1} for stoichiometric homoepitaxial SrTiO{sub 3} to 2 W m{sup −1}K{sup −1} for strontium-rich homoepitaxial Sr{sub 1+δ}TiO{sub x} films—by incorporating (SrO){sub 2} Ruddlesden-Popper planar defects.

  13. Ag2S/CdS/TiO2 Nanotube Array Films with High Photocurrent Density by Spotting Sample Method

    OpenAIRE

    Sun, Hong; Zhao, Peini; Zhang, Fanjun; Liu, Yuliang; Hao, Jingcheng

    2015-01-01

    Ag2S/CdS/TiO2 hybrid nanotube array films (Ag2S/CdS/TNTs) were prepared by selectively depositing a narrow-gap semiconductor—Ag2S (0.9 eV) quantum dots (QDs)—in the local domain of the CdS/TiO2 nanotube array films by spotting sample method (SSM). The improvement of sunlight absorption ability and photocurrent density of titanium dioxide (TiO2) nanotube array films (TNTs) which were obtained by anodic oxidation method was realized because of modifying semiconductor QDs. The CdS/TNTs, Ag2S/TNT...

  14. Resistivity behavior of optimized PbTiO3 thin films prepared by spin coating method

    Science.gov (United States)

    Nurbaya, Z.; Wahid, M. H.; Rozana, M. D.; Alrokayan, S. A. H.; Khan, H. A.; Rusop, M.

    2018-05-01

    Th is study presents the resistivity behavior of PbTiO3 thin films which were prepared towards metal-insulator-metal capacitor device fabrication. The PbTiO3 thin films were prepared through sol-gel spin coating method that involved various deposition parameters that is (1) different molar concentration of PbTiO3 solutions, (2) various additional PbAc-content in PbTiO3 solutions, and (3) various annealing temperature on PbTiO3 thin films. Hence, an electrical measurement of current versus voltage was done to determine the resistivity behavior of PbTiO3 thin films.

  15. Enhanced Optical and Electrical Properties of TiO_2 Buffered IGZO/TiO_2 Bi-Layered Films

    International Nuclear Information System (INIS)

    Moon, Hyun-Joo; Kim, Daeil

    2016-01-01

    In and Ga doped ZnO (IGZO, 100-nm thick) thin films were deposited by radio frequency magnetron sputtering without intentional substrate heating on a bare glass substrate and a TiO_2-deposited glass substrate to determine the effect of the thickness of a thin TiO_2 buffer layer on the structural, optical, and electrical properties of the films. The thicknesses of the TiO_2 buffer layers were 5, 10 and 15 nm, respectively. As-deposited IGZO films with a 10 nm-thick TiO_2 buffer layer had an average optical transmittance of 85.0% with lower resistivity (1.83×10-2 Ω cm) than that of IGZO single layer films. The figure of merit (FOM) reached a maximum of 1.44×10-4 Ω-1 for IGZO/10 nm-thick TiO_2 bi-layered films, which is higher than the FOM of 6.85×10-5 Ω-1 for IGZO single layer films. Because a higher FOM value indicates better quality transparent conducting oxide (TCO) films, the IGZO/10 nm-thick TiO_2 bi-layered films are likely to perform better in TCO applications than IGZO single layer films.

  16. Fabrication and photoelectrochemical properties of ZnS/Au/TiO2 nanotube array films.

    Science.gov (United States)

    Zhu, Yan-Feng; Zhang, Juan; Xu, Lu; Guo, Ya; Wang, Xiao-Ping; Du, Rong-Gui; Lin, Chang-Jian

    2013-03-21

    A highly ordered TiO(2) nanotube array film was fabricated by an anodic oxidation method. The film was modified by Au nanoparticles (NPs) formed by a deposition-precipitation technique and was covered with a thin ZnS shell prepared by a successive ionic layer adsorption and reaction (SILAR) method. The photoelectrochemical properties of the prepared ZnS/Au/TiO(2) composite film were evaluated by incident photon-to-current conversion efficiency (IPCE), and photopotential and electrochemical impedance spectroscopy (EIS) measurements under white light illumination. The results indicated that the Au NPs could expand the light sensitivity range of the film and suppress the electron-hole recombination, and the ZnS shell could inhibit the leakage of photogenerated electrons from the surface of Au NPs to the ZnS/electrolyte interface. When the 403 stainless steel in a 0.5 M NaCl solution was coupled to the ZnS/Au/TiO(2) nanotube film photoanode under illumination, its potential decreased by 400 mV, showing that the composite film had a better photocathodic protection effect on the steel than that of a pure TiO(2) nanotube film.

  17. Characterization of n-TiO{sub 2} thin films modified with silver nanoparticles; Caracterizacion de peliculas delgadas de n-TiO{sub 2} modificadas con nanoparticulas de plata

    Energy Technology Data Exchange (ETDEWEB)

    Cueto, L.F. [Universidad Autonoma de Nuevo Leon, Monterrey, N.L. (Mexico). Dept. de Biotecnologia e Ingenieria de Alimentos; Sanchez-Cervantes, E.M. [Universidad Autonoma de Nuevo Leon, San Nicolas de los Garza, N.L. (Mexico). Facultad de Ciencias Quimicas. Lab. de Vidrio

    2010-07-01

    Carbon dioxide accumulation in the atmosphere has gained much attention and has reopened many research lines that initiated two or three decades ago. Electrochemical reduction represents one of the most discussed methods, especially where semiconductor and metal-semiconductor cathodes are used to achieve CO{sub 2} transformation into higher-energy products. In the present work, the influence of silver nanoparticles upon CO{sub 2} reduction on n-TiO{sub 2} cathodes in aqueous media is presented. Silver nanoparticles with an average diameter of 250nm were deposited on n-TiO{sub 2} surfaces by the electrochemical Double-Pulse Potential method. A Grazing-Incidence X-Ray Diffraction structural analysis is presented showing the presence of metallic silver, while Atomic Force Microscopy shows surface roughness and particle size before and after surface modification. These measurements were confirmed by Scanning-Electron Microscopy acquainting for the formation of metal particles on the n-TiO{sub 2} surface. Enhancement of CO{sub 2} reduction by the presence of silver on cathodes is shown by cyclic voltammetry. (author)

  18. Resistive switching in TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Lin

    2011-10-26

    The continuing improved performance of the digital electronic devices requires new memory technologies which should be inexpensively fabricated for higher integration capacity, faster operation, and low power consumption. Resistive random access memory has great potential to become the front runner as the non volatile memory technology. The resistance states stored in such cell can remain for long time and can be read out none-destructively by a very small electrical pulse. In this work the typically two terminal memory cells containing a thin TiO{sub 2} layer are studied. Polycrystalline TiO{sub 2} thin films are deposited with atomic layer deposition and magnetron reactive sputtering processes, which are both physically and electrically characterized. The resistive switching cells are constructed in a metal/TiO{sub 2}/metal structure. Electroforming process initiate the cell from the beginning good insulator to a real memory cell to program the resistive states. Multilevel resistive bipolar switching controlled by current compliance is the common characteristic observed in these cells, which is potentially to be used as so called multi-bit memory cells to improve the memory capacity. With different top electrodes of Pt, Cu, Ag the resistive switching behaviors are studied. The switching behaviors are different depending on the top metal such as the minimum current compliance, the endurance of the programmed resistance states and the morphology change during the switching. The temperature dependence of different resistance states are investigated. A reduction of the activation energy and their possible conduction mechanisms is discussed on the base of the basic current conduction models. It is found that the resistance state transfers from semiconductor to metallic property with the reducing resistances. The calculated temperature coefficients of their metallic states on the Cu/TiO{sub 2}/Pt and Ag/TiO{sub 2}/Pt are very close to the reported literature data

  19. Superhydrophilicity of TiO2 nano thin films

    International Nuclear Information System (INIS)

    Mohammadizadeh, M.R.; Ashkarran, A.A.

    2007-01-01

    Full text: Among the several oxide semiconductors, titanium dioxide has a more helpful role in our environmental purification due to its photocatalytic activity, photo-induced superhydrophilicity, and as a result of them non-toxicity, self cleaning, and antifogging effects. After the discovery of superhydrophilicity of titanium dioxide in 1997, several researches have been performed due to its nature and useful applications. The superhydrophilicity property of the surface allows water to spread completely across the surface rather than remains as droplets, thus making the surface antifog and easy-to-clean. The distinction of photo-induced catalytic and hydrophilicity properties of TiO 2 thin films has been accepted although, the origin of hydrophilicity property has not been recognized completely yet. TiO 2 thin films on soda lime glass were prepared by the sol-gel method and spin coating process. The calcination temperature was changed from 100 to 550 C. XRD patterns show increasing the content of polycrystalline anatase phase with increasing the calcination temperature. The AFM results indicate granular morphology of the films, which particle size changes from 22 to 166 nm by increasing the calcination temperature. The RBS, EDX and Raman spectroscopy of the films show the ratio of Ti:O∼0.5, and diffusion of sodium ions from substrate into the layer, by increasing the calcination temperature. The UV/Vis. spectroscopy of the films indicates a red shift by increasing the calcination temperature. The contact angle meter experiment shows that superhydrophilicity of the films depends on the formation of anatase crystal structure and diffused sodium content from substrate to the layer. The best hydrophilicity property was observed at 450 C calcination temperature, where the film is converted to a superhydrophilic surface after 10 minutes under 2mW/cm 2 UV irradiation. TiO 2 thin film on Si(111), Si(100), and quartz substrates needs less time to be converted to

  20. TiO2 and SiC nanostructured films, organized CNT structures

    Indian Academy of Sciences (India)

    sized nanostructured TiO2 films through hydrolysis of titanium tetra-isopropoxide. (TTIP) [9 ... structured TiO2 as a photocatalyst is as follows [15]:. TiO2(ns) ... The deposited films were easily detached from the silica tube and subjected to. SEM.

  1. Hydrogen-bonding effects on film structure and photoelectrochemical properties of porphyrin and fullerene composites on nanostructured TiO 2 electrodes

    NARCIS (Netherlands)

    Kira, Aiko; Tanaka, Masanobu; Umeyama, Tomokazu; Matano, Yoshihiro; Yoshimoto, Naoki; Zhang, Yi; Ye, Shen; Lehtivuori, Heli; Tkachenko, Nikolai V.; Lemmetyinen, Helge; Imahori, Hiroshi

    2007-01-01

    Hydrogen-bonding effects on film structures and photophysical, photoelectrochemical, and photovoltaic properties have been examined in mixed films of porphyrin and fullerene composites with and without hydrogen bonding on nanostructured TiO2 electrodes. The nanostructured TiO2 electrodes modified

  2. Layer-by-layer assembled TiO2 films with high ultraviolet light-shielding property

    International Nuclear Information System (INIS)

    Li, Xiaozhou; Wang, Lin; Pei, Yuxin; Jiang, Jinqiang

    2014-01-01

    Ultraviolet (UV) B is hazardous to human, plants and animals. With the rapid growth of ozone holes over the earth, the exploration of optical materials that can cut off harmful UV radiation is important. In this work, fusiform TiO 2 nanoparticles were synthesized by a hydrothermal synthesis method. The thin films assembled with TiO 2 nanoparticles and oppositely charged polyelectrolytes were fabricated via a layer-by-layer assembly method. The fabrication of poly(ethylene imine) (PEI)/TiO 2 multilayer films was verified by ultraviolet–visible spectra measurements, scanning electron microscopy and atomic force microscopy. The as-prepared PEI/TiO 2 multilayer films can effectively absorb harmful UVB light and filter off visible light. Most importantly, the PEI/TiO 2 films can be deposited directly on various kinds of hydrophilic substrates such as quartz, glass, silicon and hydrophobic substrates such as polystyrene, polypropylene, polyethylene and polymethyl methacrylate when the hydrophilic substrates were modified to obtain a hydrophilic surface. - Highlights: • PEI/TiO 2 films were fabricated via a layer-by-layer self-assembly method. • The films could effectively absorb harmful UVB light and filter off visible light. • The films could deposit directly on either hydrophilic or hydrophobic substrates

  3. Layer-by-layer assembled TiO{sub 2} films with high ultraviolet light-shielding property

    Energy Technology Data Exchange (ETDEWEB)

    Li, Xiaozhou [College of Science, Northwest A and F University, Yangling, Shaanxi 712100 (China); Wang, Lin, E-mail: wanglin0317@nwsuaf.edu.cn [College of Science, Northwest A and F University, Yangling, Shaanxi 712100 (China); Pei, Yuxin [College of Science, Northwest A and F University, Yangling, Shaanxi 712100 (China); Jiang, Jinqiang [State Key Lab of Applied Surface and Colloid Chemistry, College of Chemistry and Chemical Engineering, Shaanxi Normal University, Xi' an 710062 (China)

    2014-11-28

    Ultraviolet (UV) B is hazardous to human, plants and animals. With the rapid growth of ozone holes over the earth, the exploration of optical materials that can cut off harmful UV radiation is important. In this work, fusiform TiO{sub 2} nanoparticles were synthesized by a hydrothermal synthesis method. The thin films assembled with TiO{sub 2} nanoparticles and oppositely charged polyelectrolytes were fabricated via a layer-by-layer assembly method. The fabrication of poly(ethylene imine) (PEI)/TiO{sub 2} multilayer films was verified by ultraviolet–visible spectra measurements, scanning electron microscopy and atomic force microscopy. The as-prepared PEI/TiO{sub 2} multilayer films can effectively absorb harmful UVB light and filter off visible light. Most importantly, the PEI/TiO{sub 2} films can be deposited directly on various kinds of hydrophilic substrates such as quartz, glass, silicon and hydrophobic substrates such as polystyrene, polypropylene, polyethylene and polymethyl methacrylate when the hydrophilic substrates were modified to obtain a hydrophilic surface. - Highlights: • PEI/TiO{sub 2} films were fabricated via a layer-by-layer self-assembly method. • The films could effectively absorb harmful UVB light and filter off visible light. • The films could deposit directly on either hydrophilic or hydrophobic substrates.

  4. Optical band gap and magnetic properties of unstrained EuTiO3 films

    International Nuclear Information System (INIS)

    Lee, J. H.; Ke, X.; Schiffer, P.; Podraza, N. J.; Kourkoutis, L. Fitting; Fennie, C. J.; Muller, D. A.; Heeg, T.; Schlom, D. G.; Roeckerath, M.; Schubert, J.; Freeland, J. W.

    2009-01-01

    Phase-pure, stoichiometric, unstrained, epitaxial (001)-oriented EuTiO 3 thin films have been grown on (001) SrTiO 3 substrates by reactive molecular-beam epitaxy. Magnetization measurements show antiferromagnetic behavior with T N =5.5 K, similar to bulk EuTiO 3 . Spectroscopic ellipsometry measurements reveal that EuTiO 3 films have a direct optical band gap of 0.93±0.07 eV.

  5. Octahedral tilt independent magnetism in confined GdTiO3 films

    Science.gov (United States)

    Need, R. F.; Isaac, B. J.; Kirby, B. J.; Borchers, J. A.; Stemmer, S.; Wilson, Stephen D.

    2018-03-01

    Low temperature polarized neutron reflectometry measurements are presented, exploring the evolution of ferrimagnetism in thin GdTiO3 films embedded within a SrTiO3 matrix. In GdTiO3 films thinner than ˜4 nm, the TiO6 octahedral tilts endemic to GdTiO3 coherently relax toward the undistorted, cubic phase of SrTiO3. Our measurements indicate that the ferrimagnetic state within the GdTiO3 layers survives as these TiO6 octahedral tilts are suppressed. Furthermore, our data suggest that layers of suppressed magnetization (i.e., magnetic dead layers) develop within the GdTiO3 layer at each GdTiO3/SrTiO3 interface and explain the apparent magnetization suppression observed in thin GdTiO3 films when using volume-averaged techniques. Our data show that the low temperature magnetic moment inherent to the core GdTiO3 layers is only weakly impacted as the octahedral tilt angles are suppressed by more than 50% and the t2 g bandwidth is dramatically renormalized.

  6. Surface engineering of Ti-O films by photochemical immobilization of gelatin

    International Nuclear Information System (INIS)

    Weng, Y.J.; Ren, J.R.; Huang, N.; Wang, J.; Chen, J.Y.; Leng, Y.X.; Liu, H.Q.

    2008-01-01

    Crystalline Ti-O films were prepared by unbalanced magnetron sputtering and the structure was confirmed by XRD. An organic layer of 3-aminopropylphosphonic acid (APP) was first introduced on the Ti-O films by self-assembling. The stability of the APP on Ti-O films was confirmed by XPS and FTIR analysis. Simultaneously, azido group was introduced in gelatin molecule to act as photoreactive point. The derivated gelatin was spin-coated onto the self-assembled layer and immobilized by UV irradiating. Chemical patterned surface was obtained by using a photomask when irradiating and confirmed by sirius red staining and surface profile analysis. Measured by surface profilometer, the thickness of the immobilized gelatin was about 5-20 nm. The adhering of human endothelial EVC304 cells on APP modified surface was enhanced in the cell culture test. Moreover, the adherence and growth of cells were prior on gelatin-immobilized region visually seen on the patterned surface. This result indicated gelatin-immobilized Ti-O surface can serve as a biocompatible biomaterial for endothelialization

  7. Influence of operating parameters on surface properties of RF glow discharge oxygen plasma treated TiO{sub 2}/PET film for biomedical application

    Energy Technology Data Exchange (ETDEWEB)

    Pandiyaraj, K. Navaneetha, E-mail: dr.knpr@gmail.com [Surface Engineering Laboratory, Department of Physics, Sri Shakthi Institute of Engineering and Technology, L and T by pass, Chinniyam Palayam (post), Coimbatore 641062 (India); Deshmukh, R.R. [Department of Physics, Institute of Chemical Technology, Matunga, Mumbai 400 019 (India); Mahendiran, R. [Surface Engineering Laboratory, Department of Physics, Sri Shakthi Institute of Engineering and Technology, L and T by pass, Chinniyam Palayam (post), Coimbatore 641062 (India); Su, Pi-G [Department of Chemistry, Chinese Culture University, Taipei 111, Taiwan (China); Yassitepe, Emre; Shah, Ismat [Department of Physics and Astronomy, Department of Materials Science and Engineering, University of Delaware, 208 Dupont Hall, Newark (United States); Perni, Stefano [School of Pharmacy and Pharmaceutical Sciences, Cardiff University, Cardiff (United Kingdom); Prokopovich, Polina [School of Pharmacy and Pharmaceutical Sciences, Cardiff University, Cardiff (United Kingdom); Institute of Medical Engineering and Medical Physics, School of Engineering, Cardiff University (United Kingdom); Nadagouda, Mallikarjuna N., E-mail: Nadagouda.Mallikarjuna@epamail.epa.gov [The U.S. Environmental Protection Agency, ORD, NRMRL, WSWRD, 26W. Martin Luther King Drive, Cincinnati, OH 45268 (United States)

    2014-03-01

    In this paper, a thin transparent titania (TiO{sub 2}) film was coated on the surface of flexible poly(ethylene terephthalate) (PET) film using the sol–gel method. The surface properties of the obtained TiO{sub 2}/PET film were further improved by RF glow discharge oxygen plasma as a function of exposure time and discharge power. The changes in hydrophilicity of TiO{sub 2}/PET films were analyzed by contact angle measurements and surface energy. The influence of plasma on the surface of the TiO{sub 2}/PET films was analyzed by atomic force microscopy (AFM) as well as the change in chemical state and composition that were investigated by X-ray photo electron spectroscopy (XPS). The cytotoxicity of the TiO{sub 2}/PET films was analyzed using human osteoblast cells and the bacterial eradication behaviors of TiO{sub 2}/PET films were also evaluated against Staphylococcus bacteria. It was found that the surface roughness and incorporation of oxygen containing polar functional groups of the plasma treated TiO{sub 2}/PET films increased substantially as compared to the untreated one. Moreover the increased concentration of Ti{sup 3+} on the surface of plasma treated TiO{sub 2}/PET films was due to the transformation of chemical states (Ti{sup 4+} → Ti{sup 3+}). These morphological and chemical changes are responsible for enhanced hydrophilicity of the TiO{sub 2}/PET films. Furthermore, the plasma treated TiO{sub 2}/PET film exhibited no citotoxicity against osteoblast cells and antibacterial activity against Staphylococcus bacteria which can find application in manufacturing of biomedical devices. - Graphical abstract: Mechanism of plasma treatment on the surface of TiO{sub 2}/PET films. - Highlights: • Investigated the surface properties of TiO{sub 2}/PET films modified by O{sub 2} plasma • Studied the effect of operating parameters on surface properties of TiO{sub 2}/PET films • Mechanism of the plasma treatment on TiO{sub 2}/PET was clearly investigated.

  8. Growth of BaTiO3-PVDF composite thick films by using aerosol deposition

    Science.gov (United States)

    Cho, Sung Hwan; Yoon, Young Joon

    2016-01-01

    Barium titanate (BaTiO3)-polyvinylidene fluoride (PVDF) composite thick films were grown by using aerosol deposition at room temperature with BaTiO3 and PVDF powders. To produce a uniform composition in ceramic and polymer composite films, which show a substantial difference in specific gravity, we used PVDF-coated BaTiO3 powders as the starting materials. An examination of the microstructure confirmed that the BaTiO3 were well distributed in the PVDF matrix in the form of a 0 - 3 compound. The crystallite size in the BaTiO3-PVDF composite thick films was 5 ˜ 50 times higher than that in pure BaTiO3 thick films. PVDF plays a role in suppressing the fragmentation of BaTiO3 powder during the aerosol deposition process and in controlling the relative permittivity.

  9. A pH sensor based on the TiO{sub 2} nanotube array modified Ti electrode

    Energy Technology Data Exchange (ETDEWEB)

    Zhao Rongrong; Xu Meizhu [Ministry of Education Key Laboratory of Analysis and Detection for Food Safety, Fujian Provincial Key Laboratory of Analysis and Detection for Food Safety, Department of Chemistry, Fuzhou University, 523 Gongye Road, Fuzhou 350002, Fujian (China); Wang Jian, E-mail: jwang@fzu.edu.c [Ministry of Education Key Laboratory of Analysis and Detection for Food Safety, Fujian Provincial Key Laboratory of Analysis and Detection for Food Safety, Department of Chemistry, Fuzhou University, 523 Gongye Road, Fuzhou 350002, Fujian (China); Chen Guonan, E-mail: guonanchen@126.co [Ministry of Education Key Laboratory of Analysis and Detection for Food Safety, Fujian Provincial Key Laboratory of Analysis and Detection for Food Safety, Department of Chemistry, Fuzhou University, 523 Gongye Road, Fuzhou 350002, Fujian (China)

    2010-08-01

    In this paper, a novel solid state pH sensor was fabricated by anodization of titanium substrate electrode. The relationship between pH sensitivity and hydrophilicity or surface morphology of TiO{sub 2} film was investigated. Amorphous TiO{sub 2} nanotube has better pH response than anatase TiO{sub 2} nanotube. After being irradiated by ultraviolet light (UV), the potential response of the electrode modified by amorphous TiO{sub 2} nanotube was close to Nernst equation (59 mV/pH). SEM, XRD, and XPS were used to characterize electrodes. Possible mechanism was discussed by analyzing surface hydroxyl groups, crystal structure and hydrophilicity of the electrodes. The electrode has been used to detect some kinds of soft drinks and shows good response.

  10. Microporous TiO2-WO3/TiO2 films with visible-light photocatalytic activity synthesized by micro arc oxidation and DC magnetron sputtering

    International Nuclear Information System (INIS)

    Wu, Kee-Rong; Hung, Chung-Hsuang; Yeh, Chung-Wei; Wu, Jiing-Kae

    2012-01-01

    Highlights: ► A simple MAO is used to prepare porous WO 3 /TiO 2 layer on Ti sheet as a visible-light enabled catalyst. ► The photocatalytic activity of the WO 3 /TiO 2 is enhanced by sputtering over an N,C-TiO 2 layer. ► This is ascribed to the synergetic effect of hybrid sample prepared by two-step method. - Abstract: This study reports the preparation of microporous TiO 2 -WO 3 /TiO 2 films with a high surface area using a two-step approach. A porous WO 3 /TiO 2 template was synthesized by oxidizing a titanium sheet using a micro arc oxidation (MAO) process. This sheet was subsequently overlaid with a visible light (Vis)-enabled TiO 2 (N,C-TiO 2 ) film, which was deposited by codoping nitrogen (N) and carbon (C) ions into a TiO 2 lattice using direct current magnetron sputtering. The resulting microporous TiO 2 -WO 3 /TiO 2 film with a 0.38-μm-thick N,C-TiO 2 top-layer exhibited high photocatalytic activity in methylene blue (MB) degradation among samples under ultraviolet (UV) and Vis irradiation. This is attributable to the synergetic effect of two-step preparation method, which provides a highly porous microstructure and the well-crystallized N,C-TiO 2 top-layer. This is because a higher surface area with high crystallinity favors the adsorption of more MB molecules and more photocatalytic active areas. Thus, the microporous TiO 2 -WO 3 /TiO 2 film has promising applications in the photocatalytic degradation of dye solution under UV and Vis irradiation. These results imply that the microporous WO 3 /TiO 2 can be used as a template of hybrid electrode because it enables rapid fabrication.

  11. Electrochemical Behavior of TiO2 Nanoparticle Doped WO3 Thin Films

    Directory of Open Access Journals (Sweden)

    Suvarna R. Bathe

    2014-01-01

    Full Text Available Nanoparticle TiO2 doped WO3 thin films by pulsed spray pyrolysis technique have been studied on fluorine tin doped (FTO and glass substrate. XRD shows amorphous nature for undoped and anatase phase of TiO2 having (101 plane for nanoparticle TiO2 doped WO3 thin film. SEM shows microfibrous reticulated porous network for WO3 with 600 nm fiber diameter and nanocrystalline having size 40 nm for TiO2 nanoparticle doped WO3 thin film. TiO2 nanoparticle doped WO3 thin film shows ~95% reversibility due to may be attributed to nanocrystalline nature of the film, which helpful for charge insertion and deinsertion process. The diffusion coefficient for TiO2 nanoparticle doped WO3 film is less than undoped WO3.

  12. Annealing of TiO2 Films Deposited on Si by Irradiating Nitrogen Ion Beams

    International Nuclear Information System (INIS)

    Yokota, Katsuhiro; Yano, Yoshinori; Miyashita, Fumiyoshi

    2006-01-01

    Thin TiO2 films were deposited on Si at a temperature of 600 deg. C by an ion beam assisted deposition (IBAD) method. The TiO2 films were annealed for 30 min in Ar at temperatures below 700 deg. C. The as-deposited TiO2 films had high permittivities such 200 εo and consisted of crystallites that were not preferentially oriented to the c-axis but had an expanded c-axis. On the annealed TiO2 films, permittivities became lower with increasing annealing temperature, and crystallites were oriented preferentially to the (110) plane

  13. Synthesis of nanocrystalline TiO2 thin films by liquid phase ...

    Indian Academy of Sciences (India)

    WINTEC

    goes degradation efficiently in presence of TiO2 thin films by exposing its aqueous solution to .... Figure 6. Photodegradation of IGOR organic dye by a. bare TiO2 thin film and b. ... Meng L-J and Dos Santos M P 1993 Thin Solid Films 226 22.

  14. Tailoring the wettability of nanocrystalline TiO 2 films

    Science.gov (United States)

    Liang, Qiyu; Chen, Yan; Fan, Yuzun; Hu, Yong; Wu, Yuedong; Zhao, Ziqiang; Meng, Qingbo

    2012-01-01

    The water contact angle (WCA) of nanocrystalline TiO2 films was adjusted by fluoroalkylsilane (FAS) modification and photocatalytic lithography. FAS modification made the surface hydrophobic with the WCA up to ∼156°, while ultraviolet (UV) irradiation changed surface to hydrophilic with the WCA down to ∼0°. Both the hydrophobicity and hydrophilicity were enhanced by surface roughness. The wettability can be tailored by varying the concentration of FAS solution and soaking time, as well as the UV light intensity and irradiation time. Additionally, with the help of photomasks, hydrophobic-hydrophilic micropatterns can be fabricated and manifested via area-selective deposition of polystyrene particles.

  15. Visible light active TiO{sub 2} films prepared by electron beam deposition of noble metals

    Energy Technology Data Exchange (ETDEWEB)

    Hou Xinggang, E-mail: hou226@163.co [Department of Physics, Tianjin Normal University, Tianjin 300387 (China); Ma Jun [Department of Physics, Tianjin Normal University, Tianjin 300387 (China); Liu Andong [Key Laboratory of Beam Technology and Material Modification of Ministry of Education, Beijing Normal University, Beijing 100875 (China); Li Dejun; Huang Meidong; Deng Xiangyun [Department of Physics, Tianjin Normal University, Tianjin 300387 (China)

    2010-03-15

    TiO{sub 2} films prepared by sol-gel method were modified by electron beam deposition of noble metals (Pt, Pd, and Ag). Effects of noble metals on the chemical and surface characteristics of the films were studied using XPS, TEM and UV-Vis spectroscopy techniques. Photocatalytic activity of modified TiO{sub 2} films was evaluated by studying the degradation of methyl orange dye solution under visible light UV irradiation. The result of TEM reveals that most of the surface area of TiO{sub 2} is covered by tiny particles of noble metals with diameter less than 1 nm. Broad red shift of UV-Visible absorption band of modified photocatalysts was observed. The catalytic degradation of methyl orange in aqueous solutions under visible light illumination demonstrates a significant enhancement of photocatalytic activity of these films compared with the un-loaded films. The photocatalytic efficiency of modified TiO{sub 2} films by this method is affected by the concentration of impregnating solution.

  16. The influence of metal interlayers on the structural and optical properties of nano-crystalline TiO 2 films

    KAUST Repository

    Yang, Yong

    2012-03-01

    TiO 2-M-TiO 2 (M = W, Co and Ag) multilayer films have been deposited on glass substrates using reactive magnetron sputtering, then annealed in air for 2 h at 500°C. The structure, surface morphology and optical properties of the films have been studied using X-ray diffraction, Raman spectroscopy, atomic force microscopy and UV-vis spectroscopy. The TiO 2-W-TiO 2 and TiO 2-Co-TiO 2 films showed crystalline phases, whereas the TiO 2-Ag-TiO 2 films remained in the amorphous state. The crystallization temperature for the TiO 2-M-TiO 2 films decreased significantly compared with pure TiO 2 film deposited on quartz. Detailed analysis of the Raman spectra suggested that the crystallization of TiO 2-M-TiO 2 films was associated with the large structural deformation imposed by the oxidation of intermediate metal layers. Moreover, the optical band gap of the films narrowed due to the appearance of impurity levels as the metal ions migrated into the TiO 2 matrix. These results indicate that the insertion of intermediate metal layers provides a feasible access to improve the structural and optical properties of anatase TiO 2 films, leading to promising applications in the field of photocatalysis. © 2011 Elsevier B.V. All rights reserved.

  17. Optical Properties and Surface Morphology of Nano-composite PMMA: TiO2 Thin Films

    International Nuclear Information System (INIS)

    Lyly Nyl Ismail; Ahmad Fairoz Aziz; Habibah Zulkefle

    2011-01-01

    There are two nano-composite PMMA: TiO 2 solutions were prepared in this research. First solution is nano-composite PMMA commercially available TiO 2 nanopowder and the second solution is nano-composite PMMA with self-prepared TiO 2 powder. The self-prepared TiO 2 powder is obtained by preparing the TiO 2 sol-gel. Solvo thermal method were used to dry the TiO 2 sol-gel and obtained TiO 2 crystal. Ball millers were used to grind the TiO 2 crystal in order to obtained nano sized powder. Triton-X was used as surfactant to stabilizer the composite between PMMA: TiO 2 . Besides comparing the nano-composite solution, we also studied the effect of the thin films thickness on the optical properties and surface morphology of the thin films. The thin films were deposited by sol-gel spin coating method on glass substrates. The optical properties and surface characterization were measured with UV-VIS spectrometer equipment and atomic force microscopy (AFM). The result showed that nano-composite PMMA with self prepared TiO 2 give high optical transparency than nano-composite PMMA with commercially available TiO 2 nano powder. The results also indicate as the thickness is increased the optical transparency are decreased. Both AFM images showed that the agglomerations of TiO 2 particles are occurred on the thin films and the surface roughness is increased when the thickness is increased. High agglomeration particles exist in the AFM images for nano-composite PMMA: TiO 2 with TiO 2 nano powder compare to the other nano-composite solution. (author)

  18. Relationship between nano/micro structure and physical properties of TiO2-sodium caseinate composite films.

    Science.gov (United States)

    Montes-de-Oca-Ávalos, Juan Manuel; Altamura, Davide; Candal, Roberto Jorge; Scattarella, Francesco; Siliqi, Dritan; Giannini, Cinzia; Herrera, María Lidia

    2018-03-01

    Films obtained by casting, starting from conventional emulsions (CE), nanoemulsions (NE) or their gels, which led to different structures, with the aim of explore the relationship between structure and physical properties, were prepared. Sodium caseinate was used as the matrix, glycerol as plasticizer, glucono-delta-lactone as acidulant to form the gels, and TiO 2 nanoparticles as reinforcement to improve physical behavior. Structural characterization was performed by SAXS and WAXS (Small and Wide Angle X-ray Scattering, respectively), combined with confocal and scanning electron microscopy. The results demonstrate that the incorporation of the lipid phase does not notably modify the mechanical properties of the films compared to solution films. Films from NE were more stable against oil release than those from CE. Incorporation of TiO 2 improved mechanical properties as measured by dynamical mechanical analysis (DMA) and uniaxial tensile tests. TiO 2 macroscopic spatial distribution homogeneity and the nanostructure character of NE films were confirmed by mapping the q-dependent scattering intensity in scanning SAXS experiments. SAXS microscopies indicated a higher intrinsic homogeneity of NE films compared to CE films, independently of the TiO 2 load. NE-films containing structures with smaller and more homogeneously distributed building blocks showed greater potential for food applications than the films prepared from sodium caseinate solutions, which are the best known films. Copyright © 2017 Elsevier Ltd. All rights reserved.

  19. Preparation and characterization of nanocrystalline porous TiO2/WO3 composite thin films

    International Nuclear Information System (INIS)

    Hsu, C.-S.; Lin, C.-K.; Chan, C.-C.; Chang, C.-C.; Tsay, C.-Y.

    2006-01-01

    TiO 2 materials possessing not only photocatalytic but also electrochromic properties have attracted many research and development interests. Though WO 3 exhibits excellent electrochromic properties, the much higher cost and water-sensitivity of WO 3 as compared with the TiO 2 may restrict the practical application of WO 3 materials. In the present study, the feasibility of preparing nanocrystalline porous TiO 2 /WO 3 composite thin films was investigated. Precursors of sols TiO 2 and/or WO 3 and polystyrene microspheres were used to prepare nanocrystalline pure TiO 2 , WO 3 , and composite TiO 2 /WO 3 thin films by spin coating. The spin-coated thin films were amorphous and, after heat treating at a temperature of 500 o C, nanocrystalline TiO 2 , TiO 2 /WO 3 , and WO 3 thin films with or without pores were prepared successfully. The heat-treated thin films were colorless and coloration-bleaching phenomena can be observed during cyclic voltammetry tests. The heat-treated thin films exhibited good reversible electrochromic behavior while the porous TiO 2 /WO 3 composite film exhibited improved electrochromic properties

  20. Preparation and Application of Immobilized Surfactant-Modified PANi-CNT/TiO2 under Visible-Light Irradiation

    Directory of Open Access Journals (Sweden)

    Ching Yuan

    2017-07-01

    Full Text Available Hydrothermally and sol-gel-synthesized immobilized surfactant-modified polyaniline-carbon nanotubes/TiO2 (PANi-CNT/TiO2 photocatalysts were prepared and their application in the degradation of diethyl phthalate (DEP under visible light at 410 nm was investigated in this sturdy. To improve the dispersion of nanoparticles and the transfer of electrons, the TiO2 surface was modified with both sodium dodecyl sulfate (SDS and functionalized carbon nanotubes (CNT-COOH and CNT-COCl. With the addition of PANi, which was increased from 1%–5%, the adsorption edge of the prepared photocatalysts shifted to 442 nm. The SDS linked the PANi polymers to achieve a thickness of coating of the film of up to 314–400 nm and 1301–1600 nm for sol-gel hydrolysis and hydrothermally-synthesized photocatalysts, respectively. An appropriate film thickness would extend the transfer path of the electrons and inhibit the recombination of the electrons and the electron-holes. The photo-degradation performance of DEP by the hydrothermally-synthesized photocatalysts was better than those by sol-gel hydrolysis. The results revealed that the hydroxyl radicals were the key oxidant in the degradation of DEP using hydrothermally-synthesized PANi-CNT/TiO2 photocatalysts. The morphology and functional groups of the raw materials of photocatalysts were characterized and a comparison of photocatalytic activity with other TiO2-based photocatalysts was also provided.

  1. Microstructural properties of BaTiO3 ceramics and thin films

    International Nuclear Information System (INIS)

    Fundora C, A.; Portelles, J.J.; Siqueiros, J.M.

    2000-01-01

    A microstructural study of BaTiO 3 ceramics obtained by the conventional ceramic method is presented. Targets were produced to grow BaTiO 3 thin films by pulsed laser deposition on Pt/Ti/Si (100) substrates. X-ray diffraction, Auger Electron Spectroscopy, X-ray Photon Spectroscopy and Scanning Electron Microscopy were used to study the properties of the BaTiO 3 ceramic samples and thin films, as deposited and after an annealing process. (Author)

  2. Synthesis and characterization of thin films of Pd/TiO2 with possible applications in photo catalysis

    International Nuclear Information System (INIS)

    Tirado G, S.; Valenzuela Z, M. A.

    2015-10-01

    In this paper the synthesis and study of thin films of titanium oxide is reported, as well as those that were surface modified with palladium nanoparticles Pd/TiO 2 . First, the TiO 2 films are grown on substrates of soda-lime glass using chemical sol-gel route and the repeated immersion procedure. The salt precursor titanium oxy-acetylacetonate to 0.2 M, in the solvent 2-methoxyethanol and monoethanolamine was used as stabilizer. The number of used immersions gave an average thickness estimate for these films of 172.8 nm. Second, the series of Pd/TiO 2 films surface modified were obtained from a solution of palladium nitrate dehydrate at low concentration, with the same procedure. The films grown TiO 2 and those surface-modified films were characterized in its structure by X-ray diffraction, morphology by scanning electron microscopy, the topography with atomic force microscopy, optical properties by UV-Vis, among others. Photoluminescence properties and/or possible applications in photo catalysis are reported in this paper. (Author)

  3. Two steps hydrothermal growth and characterisations of BaTiO3 films composed of nanowires

    Science.gov (United States)

    Zawawi, Che Zaheerah Najeehah Che Mohd; Salleh, Shahril; Oon Jew, Lee; Tufail Chaudhary, Kashif; Helmi, Mohamad; Safwan Aziz, Muhammad; Haider, Zuhaib; Ali, Jalil

    2018-05-01

    Barium titanate (BaTiO3) films composed of nanowires have gained considerable research interest due to their lead-free composition and strong energy conversion efficiency. BaTiO3 films can be developed with a simple two steps hydrothermal reactions, which are low cost effective. In this research, BaTiO3 films were fabricated on titanium foil through two steps hydrothermal method namely, the growth of TiO2 and followed by BaTiO3 films. The structural evolutions and the dielectric properties of the films were investigated as well. The structural evolutions of titanium dioxide (TiO2) and BaTiO3 nanowires were characterized using X-ray diffraction and scanning electron microscopy. First step of hydrothermal reaction, TiO2 nanowires were prepared in varied temperatures of 160 °C, 200 °C and 250 °C respectively. Second step of hydrothermal reaction was performed to produce a layer of BaTiO3 films.

  4. Stable Water Oxidation in Acid Using Manganese-Modified TiO2 Protective Coatings.

    Science.gov (United States)

    Siddiqi, Georges; Luo, Zhenya; Xie, Yujun; Pan, Zhenhua; Zhu, Qianhong; Röhr, Jason A; Cha, Judy J; Hu, Shu

    2018-06-06

    Accomplishing acid-stable water oxidation is a critical matter for achieving both long-lasting water-splitting devices and other fuel-forming electro- and photocatalytic processes. Because water oxidation releases protons into the local electrolytic environment, it becomes increasingly acidic during device operation, which leads to corrosion of the photoactive component and hence loss in device performance and lifetime. In this work, we show that thin films of manganese-modified titania, (Ti,Mn)O x , topped with an iridium catalyst, can be used in a coating stabilization scheme for acid-stable water oxidation. We achieved a device lifetime of more than 100 h in pH = 0 acid. We successfully grew (Ti,Mn)O x coatings with uniform elemental distributions over a wide range of manganese compositions using atomic layer deposition (ALD), and using X-ray photoelectron spectroscopy, we show that (Ti,Mn)O x films grown in this manner give rise to closer-to-valence-band Fermi levels, which can be further tuned with annealing. In contrast to the normally n-type or intrinsic TiO 2 coatings, annealed (Ti,Mn)O x films can make direct charge transfer to a Fe(CN) 6 3-/4- redox couple dissolved in aqueous electrolytes. Using the Fe(CN) 6 3-/4- redox, we further demonstrated anodic charge transfer through the (Ti,Mn)O x films to high work function metals, such as iridium and gold, which is not previously possible with ALD-grown TiO 2 . We correlated changes in the crystallinity (amorphous to rutile TiO 2 ) and oxidation state (2+ to 3+) of the annealed (Ti,Mn)O x films to their hole conductivity and electrochemical stability in acid. Finally, by combining (Ti,Mn)O x coatings with iridium, an acid-stable water-oxidation anode, using acid-sensitive conductive fluorine-doped tin oxides, was achieved.

  5. Surface nanostructuring of TiO2 thin films by ion beam irradiation

    International Nuclear Information System (INIS)

    Romero-Gomez, P.; Palmero, A.; Yubero, F.; Vinnichenko, M.; Kolitsch, A.; Gonzalez-Elipe, A.R.

    2009-01-01

    This work reports a procedure to modify the surface nanostructure of TiO 2 anatase thin films through ion beam irradiation with energies in the keV range. Irradiation with N + ions leads to the formation of a layer with voids at a depth similar to the ion-projected range. By setting the ion-projected range a few tens of nanometers below the surface of the film, well-ordered nanorods appear aligned with the angle of incidence of the ion beam. Slightly different results were obtained by using heavier (S + ) and lighter (B + ) ions under similar conditions

  6. Photo-induced wettability of TiO{sub 2} film with Au buffer layer

    Energy Technology Data Exchange (ETDEWEB)

    Purkayastha, Debarun Dhar; Sangani, L. D. Varma; Krishna, M. Ghanashyam [School of Physics, University of Hyderabad, Hyderabad-500046 (India); Madhurima, V., E-mail: madhurima.v@gmail.com [Department of Physics, Central University of Tamil Nadu, Thiruvarur-610004 (India)

    2014-04-24

    The effect of thickness of Au buffer layer (15-25 nm) between TiO{sub 2} film and substrate on the wettability of TiO{sub 2} films is reported. TiO{sub 2} films grown on Au buffer layer have a higher contact angle of 96-;100° as compared to 47.6o for the film grown without buffer layer. The transition from hydrophobicity to hydrophilicity under UV irradiation occurs within 10 min. for the buffer layered films whereas it is almost 30 min. for the film grown without buffer layer. The enhanced photo induced hydrophilicity is shown to be surface energy driven.

  7. Hydrothermal growth of highly textured BaTiO3 films composed of nanowires

    International Nuclear Information System (INIS)

    Zhou Zhi; Tang Haixiong; Sodano, Henry A; Lin Yirong

    2013-01-01

    Textured barium titanate (BaTiO 3 ) films are attracting immense research interest due to their lead-free composition and excellent piezoelectric and dielectric properties. Most synthesis methods for these films require a high temperature, leading to the formation of a secondary phase and an overall decrease in the electrical properties of the ceramic. In order to alleviate these issues, a novel fabrication method is introduced by transferring oriented rutile TiO 2 nanowires to a textured BaTiO 3 film at temperatures below 160 °C. The microstructure and thickness of the fabricated BaTiO 3 films were characterized by scanning electron microscopy, and the crystal structure and degree of orientation were evaluated by x-ray diffraction patterns using the Lotgering method. It is shown that the thickness of the BaTiO 3 film can be controlled by the length of TiO 2 nanowire array template, and the degree of orientation of the textured BaTiO 3 films is highly dependent on the film thickness; the crystallographic orientation has been measured to reach up to 87%. The relative dielectric constant (ε r = 1300) and ferroelectric properties (P r = 2.7 μC cm −2 , E c = 4.0 kV mm −1 ) of the textured BaTiO 3 films were also characterized to demonstrate their potential application in sensors, random access memory, and micro-electromechanical systems. (paper)

  8. Photocatalytic properties of porous TiO2/Ag thin films

    International Nuclear Information System (INIS)

    Chang, C.-C.; Chen, J.-Y.; Hsu, T.-L.; Lin, C.-K.; Chan, C.-C.

    2008-01-01

    In this study, nanocrystalline TiO 2 /Ag composite thin films were prepared by a sol-gel spin-coating technique. By introducing polystyrene (PS) spheres into the precursor solution, porous TiO 2 /Ag thin films were prepared after calcination at a temperature of 500 deg. C for 4 h. Three different sizes (50, 200, and 400 nm) of PS spheres were used to prepare porous TiO 2 films. The as-prepared TiO 2 and TiO 2 /Ag thin films were characterized by X-ray diffractometry (XRD) and by scanning electron microscopy to reveal structural and morphological differences. In addition, the photocatalytic properties of these films were investigated by degrading methylene blue under UV irradiation. When PS spheres of different sizes were introduced after calcination, the as-prepared TiO 2 films exhibited different porous structures. XRD results showed that all TiO 2 /Ag films exhibited a major anatase phase. The photodegradation of porous TiO 2 thin films prepared with 200 nm PS spheres and doped with 1 mol% Ag exhibited the best photocatalytic efficiency where ∼ 100% methylene blue was decomposed within 8 h under UV exposure

  9. Intrinsic Photocatalytic Assessment of Reactively Sputtered TiO2 Films

    NARCIS (Netherlands)

    Rafieian Boroujeni, Damon; Driessen, Rick Theodorus; Driessen, Rick T.; Ogieglo, Wojciech; Lammertink, Rob G.H.

    2015-01-01

    Thin TiO2 films were prepared by DC magnetron reactive sputtering at different oxygen partial pressures. Depending on the oxygen partial pressure during sputtering, a transition from metallic Ti to TiO2 was identified by spectroscopic ellipsometry. The crystalline nature of the film developed during

  10. Transparent EuTiO3 films: a possible two-dimensional magneto-optical device

    Science.gov (United States)

    Bussmann-Holder, Annette; Roleder, Krystian; Stuhlhofer, Benjamin; Logvenov, Gennady; Lazar, Iwona; Soszyński, Andrzej; Koperski, Janusz; Simon, Arndt; Köhler, Jürgen

    2017-01-01

    The magneto-optical activity of high quality transparent thin films of insulating EuTiO3 (ETO) deposited on a thin SrTiO3 (STO) substrate, both being non-magnetic materials, are demonstrated to be a versatile tool for light modulation. The operating temperature is close to room temperature and allows for multiple device engineering. By using small magnetic fields birefringence of the samples can be switched off and on. Similarly, rotation of the sample in the field can modify its birefringence Δn. In addition, Δn can be increased by a factor of 4 in very modest fields with simultaneously enhancing the operating temperature by almost 100 K.

  11. Synthesis of the lithium metatitanate, Li2TiO3, by the modified combustion method

    International Nuclear Information System (INIS)

    Cruz, D.; Bulbulian, S.; Pfeiffer, H.

    2005-01-01

    A modified combustion method to obtain Li 2 TiO 3 it was used, a compound to be used in fusion reactors like tritium generator material. To obtain Li 2 TiO 3 were proven different molar ratios of lithium hydroxide (LiOH), titanium oxide (TiO 2 ) and urea (CO(NH 2 ) 2 ), as well as different heating temperatures (550, 650 and 750 C). The characterization of the products it was carried out using X-ray diffraction, Scanning electron microscopy and Thermal gravimetric analysis. The sample prepared with a molar ratio Li: Ti: urea = 2.75: 1: 3 was the one that presented as only product the Li 2 TiO 3 . The particle size and the morphology found in the Li 2 TiO 3 , showed similar particle size and morphology to the TiO 2 used as precursor. (Author)

  12. Hydrothermal fabrication of Ni{sub 3}S{sub 2}/TiO{sub 2} nanotube composite films on Ni anode and application in photoassisted water electrolysis

    Energy Technology Data Exchange (ETDEWEB)

    He, Hongbo; Chen, Aiping, E-mail: apchen@ecust.edu.cn; Lv, Hui; Dong, Haijun; Chang, Ming; Li, Chunzhong

    2013-10-15

    Highlights: •Ni{sub 3}S{sub 2}/TiO{sub 2} nanotube photocatalysts were synthesized on Ni by hydrothermal method. •Structure of Ni{sub 3}S{sub 2} wrapped by TiO{sub 2} nanotubes improves remarkably stability of Ni{sub 3}S{sub 2}. •Ni{sub 3}S{sub 2}/TiO{sub 2} film on Ni has better H{sub 2} production performance than TiO{sub 2}-modified anode. -- Abstract: Nanostructured films of rhombohedral Ni{sub 3}S{sub 2} were hydrothermally synthesized on Ni and TiO{sub 2} nanotube layer, as substrates. A possible mechanism is proposed to explain the formation of rhombohedral Ni{sub 3}S{sub 2} nanostructures. The results of UV–vis spectrophotometric studies indicate that optical absorption spectrum of Ni{sub 3}S{sub 2}/TiO{sub 2} nanotube composites could be extended to the visible region. As-synthesized Ni{sub 3}S{sub 2}/TiO{sub 2} nanotube composite films on Ni substrate had better (by about 40%) hydrogen production performance under the visible light irradiation, in comparison with the Ni anode modified by TiO{sub 2} nanotubes.

  13. Deposition of Au/TiO2 film by pulsed laser

    International Nuclear Information System (INIS)

    Zhao Chongjun; Zhao Quanzhong; Zhao Qitao; Qiu Jianrong; Zhu Congshan

    2006-01-01

    Au nanoparticles, which were photoreduced by a Nd:YAG laser in HAuCl 4 solution containing TiO 2 colloid and accompanied by the TiO 2 particles, were deposited on the substrate surface. The film consisting of Au/TiO 2 particles was characterized by the absorption spectra, scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. The adhesion between the film and substrate was evaluated by using adhesive tape test. It was found that the presence of TiO 2 dramatically enhanced the adhesion strength between the film and the substrate, as well as the deposition rate of film. The mechanism for the deposition of Au/TiO 2 film was also discussed

  14. Preparation of anatase TiO2 thin films by vacuum arc plasma evaporation

    International Nuclear Information System (INIS)

    Miyata, Toshihiro; Tsukada, Satoshi; Minami, Tadatsugu

    2006-01-01

    Anatase titanium dioxide (TiO 2 ) thin films with high photocatalytic activity have been prepared with deposition rates as high as 16 nm/min by a newly developed vacuum arc plasma evaporation (VAPE) method using sintered TiO 2 pellets as the source material. Highly transparent TiO 2 thin films prepared at substrate temperatures from room temperature to 400 deg. C exhibited photocatalytic activity, regardless whether oxygen (O 2 ) gas was introduced during the VAPE deposition. The highest photocatalytic activity and photo-induced hydrophilicity were obtained in anatase TiO 2 thin films prepared at 300 deg. C, which correlated to the best crystallinity of the films, as evidenced from X-ray diffraction. In addition, a transparent and conductive anatase TiO 2 thin film with a resistivity of 2.6 x 10 -1 Ω cm was prepared at a substrate temperature of 400 deg. C without the introduction of O 2 gas

  15. Photocatalytic self-cleaning cotton fabrics with platinum (IV) chloride modified TiO{sub 2} and N-TiO{sub 2} coatings

    Energy Technology Data Exchange (ETDEWEB)

    Long, Mingce, E-mail: long_mc@sjtu.edu.cn [School of Environmental Science and Engineering, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai, 200240 (China); Key Laboratory for Thin Film and Microfabrication of the Ministry of Education, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai, 200240 (China); Zheng, Longhui; Tan, Beihui [School of Environmental Science and Engineering, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai, 200240 (China); Shu, Heping [Xiaoxi New Materials Science and Technology (Shanghai) Co. Ltd., 655 Cangyuan Road, Shanghai, 200240 (China)

    2016-11-15

    Highlights: • Platinum (IV) chloride modified TiO{sub 2} and N-TiO{sub 2} nanosols are synthesized. • Pt-TiO{sub 2} coatings display enhanced performance in the degradation of MO and stains. • Surface attached PtCl{sub 6}{sup 2−} enable visible light activity of TiO{sub 2} coated cotton fabric. - Abstract: To enable photocatalytic self-cleaning cotton fabrics working under visible light irradiation, platinum (IV) chloride modified TiO{sub 2} (Pt-TiO{sub 2}) and N-TiO{sub 2} (Pt-N-TiO{sub 2}) nanosols are synthesized through a low temperature precipitation-peptization method. According to the characterizations of XRD, DRS and TEM, all nanoparticles are anatase nanocrystallites in the sizes of less than 10 nm, while N-TiO{sub 2} nanoparticles have better crystallization and smaller sizes. However, the cotton fabrics functionalized with Pt-TiO{sub 2} display significantly enhanced photocatalytic activity for methyl orange degradation and coffee stain removal under both solar simulator and visible light irradiation, while the performance of that coatings of Pt-N-TiO{sub 2} is poor. Further XRF and XPS results indicate that surface species on N-TiO{sub 2} block the adsorption of PtCl{sub 6}{sup 2−} anions, whereas these anions strongly attach on the surface of TiO{sub 2} nanoparticles, and accordingly enable functionalized cotton fabrics efficient visible light driven activities based on a mechanism of charge transfer from ligand to metal (CTLM) excitation.

  16. High photocatalytic degradation activity of the polyvinyl chloride (PVC)-vitamin C (VC)-TiO{sub 2} nano-composite film

    Energy Technology Data Exchange (ETDEWEB)

    Yang Changjun; Gong Chuqing; Peng Tianyou [College of Chemistry and Molecular Sciences, Wuhan University, Wuhan 430072 (China); Deng Kejian [Key Laboratory of Catalysis and Materials Science of the State Ethnic Affairs Commission and Ministry of Education, South-Central University for Nationalities, Wuhan 430074 (China); Zan Ling, E-mail: irlab@whu.edu.cn [College of Chemistry and Molecular Sciences, Wuhan University, Wuhan 430072 (China)

    2010-06-15

    A novel photodegradable polyvinyl chloride (PVC)-vitamin C (VC)-TiO{sub 2} nano-composite film was prepared by embedding VC modified nano-TiO{sub 2} photocatalyst into the commercial PVC plastic. The solid-phase photocatalytic degradation behavior of PVC-VC-TiO{sub 2} nano-composite film under UV light irradiation was investigated and compared with those of the PVC-TiO{sub 2} film and the pure PVC film, with the aid of UV-Vis spectroscopy, scanning electron microscopy (SEM), weight loss monitoring, and X-ray diffraction spectra (XRD). The results show that PVC-VC-TiO{sub 2} nano-composite film has a high photocatalytic activity; the photocatalytic degradation rate of it is two times higher than that of PVC-TiO{sub 2} film and fifteen times higher than that of pure PVC film. The optimal mass ratio of VC to TiO{sub 2} is found to be 0.5. The mechanism of enhancing photocatalytic activity is attributed to the formation of a Ti{sup IV}-VC charge-transfer complex with five-member chelate ring structure and a rapid photogenerated charge separation is thus achieved.

  17. High photocatalytic degradation activity of the polyvinyl chloride (PVC)-vitamin C (VC)-TiO2 nano-composite film

    International Nuclear Information System (INIS)

    Yang Changjun; Gong Chuqing; Peng Tianyou; Deng Kejian; Zan Ling

    2010-01-01

    A novel photodegradable polyvinyl chloride (PVC)-vitamin C (VC)-TiO 2 nano-composite film was prepared by embedding VC modified nano-TiO 2 photocatalyst into the commercial PVC plastic. The solid-phase photocatalytic degradation behavior of PVC-VC-TiO 2 nano-composite film under UV light irradiation was investigated and compared with those of the PVC-TiO 2 film and the pure PVC film, with the aid of UV-Vis spectroscopy, scanning electron microscopy (SEM), weight loss monitoring, and X-ray diffraction spectra (XRD). The results show that PVC-VC-TiO 2 nano-composite film has a high photocatalytic activity; the photocatalytic degradation rate of it is two times higher than that of PVC-TiO 2 film and fifteen times higher than that of pure PVC film. The optimal mass ratio of VC to TiO 2 is found to be 0.5. The mechanism of enhancing photocatalytic activity is attributed to the formation of a Ti IV -VC charge-transfer complex with five-member chelate ring structure and a rapid photogenerated charge separation is thus achieved.

  18. Liquid phase deposition of WO3/TiO2 heterojunction films with high photoelectrocatalytic activity under visible light irradiation

    International Nuclear Information System (INIS)

    Zhang, Man; Yang, Changzhu; Pu, Wenhong; Tan, Yuanbin; Yang, Kun; Zhang, Jingdong

    2014-01-01

    Highlights: • Liquid phase deposition is developed for preparing WO 3 /TiO 2 heterojunction films. • TiO 2 film provides an excellent platform for WO 3 deposition. • WO 3 expands the absorption band edge of TiO 2 film to visible light region. • WO 3 /TiO 2 heterojunction film shows high photoelectrocatalytic activity. - ABSTRACT: The heterojunction films of WO 3 /TiO 2 were prepared by liquid phase deposition (LPD) method via two-step processes. The scanning electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopic analysis indicated that flower-like WO 3 film was successfully deposited on TiO 2 film with the LPD processes. The TiO 2 film provided an excellent platform for WO 3 deposition while WO 3 obviously expanded the absorption of TiO 2 film to visible light. As the result, the heterojunction film of WO 3 /TiO 2 exhibited higher photocurrent response to visible light illumination than pure TiO 2 or WO 3 film. The photoelectrocatalytic (PEC) activity of WO 3 /TiO 2 film was evaluated by degrading Rhodamin B (RhB) and 4-chlorophenol (4-CP) under visible light irradiation. The results showed that the LPD WO 3 /TiO 2 film possessed high PEC activity for efficient removal of various refractory organic pollutants

  19. Enhancement of open-circuit voltage on organic photovoltaic devices by Al-doped TiO{sub 2} modifying layer produced by sol–gel method

    Energy Technology Data Exchange (ETDEWEB)

    Valaski, R.; Arantes, C.; Senna, C.A.; Carôzo, Victor; Achete, C.A. [Materials Metrology Division, Instituto Nacional de Metrologia, Qualidade e Tecnologia, Xerém, Duque de Caxias 25250-020, RJ (Brazil); Cremona, M., E-mail: cremona@fis.puc-rio.br [Materials Metrology Division, Instituto Nacional de Metrologia, Qualidade e Tecnologia, Xerém, Duque de Caxias 25250-020, RJ (Brazil); Physics Department, Pontifícia Universidade Católica do Rio de Janeiro, Rio de Janeiro 22453-970, RJ (Brazil)

    2014-12-01

    Sol–gel method has shown several advantages for oxide synthesis, such as lower cost production, coating large areas, lower processing temperatures and ease insertion of doping materials. Therefore, it is attractive for production of intermediate and electrode modifying layers in organic optoelectronic devices. Herein, spin-coated aluminum-doped titanium dioxide (AlTiO{sub 2}) thin films were produced by sol–gel method onto glass and fluorine-doped tin oxide (FTO) substrates, using different Al-dopant concentrations and post-done annealing temperatures. Electrical measurements were performed in order to investigate the improvement of the TiO{sub 2} resistivity. Additionally, structural, compositional, morphological, optical and electrical properties of the optimal AlTiO{sub 2} modifying layers onto FTO substrates were probed by different techniques, and compared with those obtained from the undoped thin films produced under similar conditions. Organic photovoltaic devices (OPVs) with the structure FTO/AlTiO{sub 2}(30 nm)/C{sub 60}(50 nm)/CuPc(50 nm)/Al with an Al concentration of 0.03 M in AlTiO{sub 2} layer were produced. The insertion of AlTiO{sub 2} thin films improved the short-circuit current density (J{sub sc}) as well as the open circuit voltage (V{sub oc}) in comparison with non-modified electrode FTO based devices. This behavior is discussed in terms of induced interface phenomena as dipole formation induced by Al. - Highlights: • Easy and cheap solution-process for AlTiO{sub 2} modification of FTO electrode for OPVs • Electrical, structural and optical characterization of TiO{sub 2} layers with Al-dopant • Improvement of Voc and Jsc of inverted OPVs with AlTiO{sub 2} modified electrode.

  20. Enhancement of open-circuit voltage on organic photovoltaic devices by Al-doped TiO2 modifying layer produced by sol–gel method

    International Nuclear Information System (INIS)

    Valaski, R.; Arantes, C.; Senna, C.A.; Carôzo, Victor; Achete, C.A.; Cremona, M.

    2014-01-01

    Sol–gel method has shown several advantages for oxide synthesis, such as lower cost production, coating large areas, lower processing temperatures and ease insertion of doping materials. Therefore, it is attractive for production of intermediate and electrode modifying layers in organic optoelectronic devices. Herein, spin-coated aluminum-doped titanium dioxide (AlTiO 2 ) thin films were produced by sol–gel method onto glass and fluorine-doped tin oxide (FTO) substrates, using different Al-dopant concentrations and post-done annealing temperatures. Electrical measurements were performed in order to investigate the improvement of the TiO 2 resistivity. Additionally, structural, compositional, morphological, optical and electrical properties of the optimal AlTiO 2 modifying layers onto FTO substrates were probed by different techniques, and compared with those obtained from the undoped thin films produced under similar conditions. Organic photovoltaic devices (OPVs) with the structure FTO/AlTiO 2 (30 nm)/C 60 (50 nm)/CuPc(50 nm)/Al with an Al concentration of 0.03 M in AlTiO 2 layer were produced. The insertion of AlTiO 2 thin films improved the short-circuit current density (J sc ) as well as the open circuit voltage (V oc ) in comparison with non-modified electrode FTO based devices. This behavior is discussed in terms of induced interface phenomena as dipole formation induced by Al. - Highlights: • Easy and cheap solution-process for AlTiO 2 modification of FTO electrode for OPVs • Electrical, structural and optical characterization of TiO 2 layers with Al-dopant • Improvement of Voc and Jsc of inverted OPVs with AlTiO 2 modified electrode

  1. Preparation of Pb(Zr, Ti)O3 Thin Films by Plasma-Assisted Sputtering

    Science.gov (United States)

    Hioki, Tsuyoshi; Akiyama, Masahiko; Ueda, Tomomasa; Onozuka, Yutaka; Suzuki, Kouji

    1999-09-01

    A novel plasma-assisted RF magnetron sputtering system with an immersed coil antenna between a target and a substrate was applied for preparing Pb(Zr, Ti)O3 (PZT) thin films. The antenna enabled the generation of inductively coupled plasma (ICP) independently of the target RF source. The plasma assisted by the antenna resulted in the changes of ion fluxes and these energy distributions irradiating to the substrate. The crystalline phase of the deposited PZT thin films was occupied by the perovskite phase depending on the antenna power. In addition, a high deposition rate, modified uniformity of film thickness, and a dense film structure with large columnar grains were obtained as a result of effects of the assisted plasma. The application of the plasma-assisted sputtering method may enable the preparation of PZT thin films that haveexcellent properties.

  2. Influence factors of photocatalytic activity of the filter media modified by TiO2

    Directory of Open Access Journals (Sweden)

    Shen Rongyan

    2014-01-01

    Full Text Available The gangue filter media was modified by the titanium dioxide (TiO2 through the liquid phase deposition method. Some influence factors of photocatalytic activity were investigated, including the mole ratio of initial solution, the water bath temperature, the deposition time, the calcination temperature, and the heat preservation time of calcination. The morphology of the film was examined by SEM, EDS, and crystallite structure by X-Ray Diffraction (XRD. The SEM, EDS, and XRD data showed that new TiO2 crystal was found in the modified filter media. And the specific surface area of the modified filter media greatly increased. By the orthogonal experiment, the optimum parameters of modification were (NH42TiF6:H3BO3=1:2, water bath temperature of 80ºC, deposition time of 5h, calcination temperature of 500ºC, and 1h heat preservation time of calcination. Under above conditions, the heavy nitrogen wastewater of 1589.94 mg/L COD and 18750 times chroma was treated by the modified filter media. After 1h catalytic reaction, the decolorization rate and COD removal rate reached 65.89% and 47.87%, respectively.

  3. Existence, release, and antibacterial actions of silver nanoparticles on Ag–PIII TiO2 films with different nanotopographies

    Directory of Open Access Journals (Sweden)

    Li J

    2014-07-01

    Full Text Available Jinhua Li, Yuqin Qiao, Hongqin Zhu, Fanhao Meng, Xuanyong Liu State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, People’s Republic of China Abstract: Nanotopographical TiOfilms (including nanorod, nanotip, and nanowire topographies were successfully fabricated on the metallic Ti surface via hydrothermal treatment and then underwent Ag plasma immersion ion implantation to incorporate Ag with TiO2. The surface morphology, phase component, and chemical composition before and after Ag–PIII were characterized. In view of the potential clinical applications, both Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus were used to estimate their antimicrobial effect. The nanostructured TiOfilms on a Ti surface exhibit a better bacteriostatic effect on both microbes compared to the pristine Ti. The nanotopographies of the TiOfilms affect the nucleation, growth, and distribution of Ag nanoparticles in the films during Ag–PIII process. The Ag nanoparticles are completely embedded into the nanorod film while partially exposed out of the nanotip and nanowire films, which account for the significant differences in the release behaviors of Ag ions in vitro. However, no significant difference exists in their antimicrobial activity against both microbes. The antimicrobial actions of the Ag@TiO2 system described here consist of two methods – the contact-killing action and the release-killing action. Nevertheless, based on the observed results, the contact-killing action should be regarded as the main method to destroy microbes for all the Ag plasma-modified TiO2 nanofilms. This study provides insight to optimize the surface design of Ti-based implants to acquire more effective antimicrobial surfaces to meet clinical applications. Keywords: silver, nanoparticles, titania, nanostructure, antibacterial, plasma

  4. Development and characterization of the kefiran-whey protein isolate-TiO2 nanocomposite films.

    Science.gov (United States)

    Zolfi, Mohsen; Khodaiyan, Faramarz; Mousavi, Mohammad; Hashemi, Maryam

    2014-04-01

    Biodegradable kefiran-whey protein isolate (WPI)-titanium dioxide (TiO2) blend films were developed and characterized as a function of incorporating amount of TiO2 nanoparticles (1, 3 and 5% wt.). Results showed that the water vapor permeability, moisture content, moisture absorption and water solubility decreased by increasing the nano-TiO2 content. Mechanical tests revealed the plasticizing effect of TiO2 nanoparticles on the kefiran-WPI-TiO2 film. Addition of TiO2 nanoparticles to kefiran-WPI films significantly decreased tensile strength and Young's modulus, while increased its elongation at break. Differential scanning calorimetry data indicated that the glass transition temperature significantly changed by adding nano-TiO2. X-ray diffraction analysis also demonstrated that crystal type in kefiran-WPI was not affected by incorporation of TiO2 nanoparticles. A uniform distribution at 1 and 3% wt. loading levels of TiO2 nanoparticles was observed using scanning electron microscopy (SEM) micrographs. Copyright © 2014 Elsevier B.V. All rights reserved.

  5. Enhancement of photoelectric catalytic activity of TiO2 film via Polyaniline hybridization

    International Nuclear Information System (INIS)

    Wang Yajun; Xu Jing; Zong Weizheng; Zhu Yongfa

    2011-01-01

    A Polyaniline (PANI)/TiO 2 film coated on titanium foil was successfully prepared using the sol-gel method followed by a facile chemisorption. Compared with pristine TiO 2 , the photocatalytic (PC) and photoelectrocatalytic (PEC) degradation rates of 2,4-dichlorophenol (2,4-DCP) with the PANI/TiO 2 film were enhanced by 22.2% and 57.5%, respectively. 2,4-DCP can be mineralized more effectively in the presence of PANI/TiO 2 film. The best PEC degradation efficiency of 2,4-DCP with the PANI/TiO 2 film was acquired at an external potential of 1.5 V with a layer of 1 nm thick PANI. The PANI/TiO 2 film was characterized by Raman spectra, Fourier transform infrared spectra (FT-IR), Auger electron spectroscopy (AES), and electrochemical analysis. These results indicated that there was a chemical interaction on the interface of PANI and TiO 2 . This interaction may be of significance to promote the migration efficiency of carriers and induce a synergetic effect to enhance the PC and PEC activities. - Graphical abstract: The effect of PANI content on 2,4-DCP degradation with initial concentration of 50 mg/L, external potential=1.5 V. Inset: degradation rate constants of various PANI/TiO 2 films. Highlights: → Polyaniline/TiO 2 film was prepared using the sol-gel method followed by chemisorption. → Photoelectrocatalytic degradation rate of 2,4-dichlorophenol was enhanced by 57.5%. → The modification of Polyaniline to TiO 2 film caused a rapid charge separation. → Best degradation efficiency was acquired at 1.5 V with 1 nm thick PANI.

  6. Structural, morphological and optical properties of thermal annealed TiO thin films

    International Nuclear Information System (INIS)

    Zribi, M.; Kanzari, M.; Rezig, B.

    2008-01-01

    Structural, morphological and optical properties of TiO thin films grown by single source thermal evaporation method were studied. The films were annealed from 300 to 520 deg. C in air after evaporation. Qualitative film analysis was performed with X-ray diffraction, atomic force microscopy and optical transmittance and reflectance spectra. A correlation was established between the optical properties, surface roughness and growth morphology of the evaporated TiO thin films. The X-ray diffraction spectra indicated the presence of the TiO 2 phase for the annealing temperature above 400 deg. C

  7. Fabrication, characterization and photocatalytic properties of Ag nanoparticles modified TiO2 NTs

    International Nuclear Information System (INIS)

    Wang Qingyao; Yang Xiuchun; Liu Dan; Zhao Jianfu

    2012-01-01

    photocatalytic results showed that the Ag nanoparticle modified TiO 2 NTs largely enhanced the photocatalytic degradation of methyl orange under ultraviolet light irradiation.

  8. Fabrication, characterization and photocatalytic properties of Ag nanoparticles modified TiO{sub 2} NTs

    Energy Technology Data Exchange (ETDEWEB)

    Wang Qingyao [School of Materials Science and Engineering, Tongji University, Shanghai 201804 (China); Yang Xiuchun, E-mail: yangxc@tongji.edu.cn [School of Materials Science and Engineering, Tongji University, Shanghai 201804 (China); Liu Dan; Zhao Jianfu [School of Materials Science and Engineering, Tongji University, Shanghai 201804 (China)

    2012-06-25

    the SILAR process does not damage the ordered tubular structure. A possible formation mechanism of Ag/TiO{sub 2} NTs has also been proposed. The photocatalytic results showed that the Ag nanoparticle modified TiO{sub 2} NTs largely enhanced the photocatalytic degradation of methyl orange under ultraviolet light irradiation.

  9. Azo dyes decomposition on new nitrogen-modified anatase TiO2 with high adsorptivity

    International Nuclear Information System (INIS)

    Janus, M.; Choina, J.; Morawski, A.W.

    2009-01-01

    New vis active photocatalyst was obtained by the modification of commercial anatase TiO 2 (Police, Poland) in pressure reactor in an ammonia water atmosphere at 100 o C for 4 h. The photocatalytic activity of new material was tested during three azo dyes decomposition: monoazo (Reactive Read), diazo (Reactive Black) and poliazodye (Direct Green). Obtained photocatalyst had new bands at 1430-1440 cm -1 attributed to the bending vibrations of NH 4 + and at 1535 cm -1 associated with NH 2 groups or NO 2 and NO. UV-vis/DR spectra of photocatalyst had also insignificant decrease in visible region. Fluorescence technique was used for studying the amount of hydroxyl radicals produced on TiO 2 surface during visible light irradiation. The hydroxyl radicals produced react with coumarin present in the solution to form 7-hydroxycoumarin which has fluorescent capacity. Photocatalytic activity of modified TiO 2 was compared with commercial titanium dioxide P25 (Degussa, Germany). The photocatalytic activity of TiO 2 /N was higher than that of unmodified material and P25 under visible light irradiation. The ability for dye adsorption (Reactive Red) on photocatalyst surface was also tested. Unmodified TiO 2 and P25 has isotherm of adsorption by Freundlich model, and nitrogen-modified TiO 2 by Langmuir model. The presence of nitrogen at the surface of TiO 2 significantly increased adsorption capacity of TiO 2 as well as OH· radicals formation under visible radiation.

  10. Pt Catalyst Supported within TiO2 Mesoporous Films for Oxygen Reduction Reaction

    International Nuclear Information System (INIS)

    Huang, Dekang; Zhang, Bingyan; Bai, Jie; Zhang, Yibo; Wittstock, Gunther; Wang, Mingkui; Shen, Yan

    2014-01-01

    In this study, dispersed Pt nanoparticles into mesoporous TiO 2 thin films are fabricated by a facile electrochemical deposition method as electro-catalysts for oxygen reduction reaction. The mesoporous TiO 2 thin films coated on the fluorine-doped tin oxide glass by screen printing allow a facile transport of reactants and products. The structural properties of the resulted Pt/TiO 2 electrode are evaluated by field emission scanning electron microscopy, energy dispersive X-ray spectrometry, X-ray diffraction, and X-ray photoelectron spectroscopy. Cyclic voltammetry measurements are performed to study the electrochemical properties of the Pt/TiO 2 electrode. Further study demonstrates the stability of the Pt catalyst supported within TiO 2 mesoporous films for the oxygen reduction reaction

  11. Antimicrobial and Barrier Properties of Bovine Gelatin Films Reinforced by Nano TiO2

    Directory of Open Access Journals (Sweden)

    R. Nassiri

    2013-11-01

    Full Text Available The effects of nano titanium dioxide incorporation were investigated on the water vaporpermeability, oxygen permeability, and antimicrobial properties of bovine gelatin films. The nano TiO2 (TiO2-N was homogenized by sonication and incorporated into bovine gelatin solutions at different concentrations(e.g. 1, 2, 3, and 5% w/w of dried gelatin. The permeability of the films to water vapor and oxygen wassignificantly decreased by incorporating of low concentration TiO2-N to gelatin solutions. TiO2-N gelatin filmsshowed an excellent antimicrobial activity against Staphylococcus aureus and Escherichia coli. Theseproperties suggest that TiO2-N has the potential as filler in gelatin-based films for using as an active packagingmaterials in pharmaceutical and food packaging industries.

  12. Synthesis of TiO2-doped SiO2 composite films and its applications

    Indian Academy of Sciences (India)

    Wintec

    structure of the titanium oxide species in the TiO2-doped SiO2 composite films and the photocatalytic reactiv- ity in order to ... gaku D-max γA diffractometer with graphite mono- chromized ... FT–IR absorption spectra of TiO2-doped SiO2 com-.

  13. Preparation and antibacterial activity of Ag–TiO 2 composite film by ...

    Indian Academy of Sciences (India)

    From these analyses, it was found that silver ions were trapped in TiO2 matrix and their reduction could be achieved at 600°C annealing temperature. The antibacterial activity against S. aureus and . coli has been studied applying the so called antibacterial-drop test. The Ag–TiO2 thin films exhibited a high antibacterial ...

  14. MoSe2 modified TiO2 nanotube arrays with superior photoelectrochemical performance

    Science.gov (United States)

    Zhang, Yaping; Zhu, Haifeng; Yu, Lianqing; He, Jiandong; Huang, Chengxing

    2018-04-01

    TiO2 nanotube arrays (TNTs) are first prepared by anodization Ti foils in ethylene glycol electrolyte. Then, MoSe2 deposites electrochemically on TNTs. The as-synthesized MoSe2/TiO2 composite has a much higher photocurrent density of 1.07 mA cm‑2 at 0 V than pure TNTs of 0.38 mA cm‑2, which suggests that the MoSe2/TiO2 composite film has optimum photoelectrocatalysis properties. The electron transport resistances of the MoSe2/TiO2 decreases to half of pure TiO2, at 295.6 ohm/cm2. Both photocurrent-time and Mott-Schottky plots indicate MoSe2 a p-type semiconductor characteristics. MoSe2/TiO2 composite can achieve a maximum 5 orders of magnitude enhancement in carrier density (4.650 × 1027 cm‑3) than that of pure TiO2 arrays. It can be attributed to p-n heterojunction formed between MoSe2 and TiO2, and the composite can be potentially applied in photoelectrochemical, photocatalysis fields.

  15. In situ modification of cell-culture scaffolds by photocatalysis of visible-light-responsive TiO2 film

    Science.gov (United States)

    Kono, Sho; Furusawa, Kohei; Kurotobi, Atsushi; Hattori, Kohei; Yamamoto, Hideaki; Hirano-Iwata, Ayumi; Tanii, Takashi

    2018-02-01

    We propose a novel process to modify the cell affinity of scaffolds in a cell-culture environment using the photocatalytic activity of visible-light (VL)-responsive TiO2. The proposed process is the improved version of our previous demonstration in which ultraviolet (UV)-responsive TiO2 was utilized. In that demonstration, we showed that cell-repellent molecules on TiO2 were decomposed and replaced with cell-permissive molecules upon UV exposure in the medium where cells are being cultured. However, UV irradiation involves taking the risk of inducing damage to the cells. In this work, a TiO2 film was sputter-deposited on a quartz coverslip at 640 °C without O2 gas injection to create a rutile structure containing oxygen defects, which is known to exhibit photocatalytic activity upon VL exposure. We show that the cell adhesion site and migration area can be controlled with the photocatalytic activity of the VL-responsive TiO2 film, while the cellular oxidative stress is reduced markedly by the substitution of VL for UV.

  16. Effect of TiCl4 treatment on the refractive index of nanoporous TiO2 films

    Science.gov (United States)

    Lee, Jeeyoung; Lee, Myeongkyu

    2015-12-01

    We investigate the effect of TiCl4 treatment on the refractive index of a nanoporous TiO2 film. A nanoparticulate TiO2 film prepared on a glass substrate was immersed in a TiCl4 aqueous solution. The subsequent reaction of TiCl4 with H2O produces TiO2 and thus modifies the density and the refractive index of the film. With increasing TiCl4 concentration, the refractive index initially increased and then declined after being maximized (n = 2.02 at 633 nm) at 0.08 M concentration. A refractive index change as large as 0.45 could be obtained with the TiCl4 treatment, making it possible to achieve diffraction efficiency exceeding 80% in a diffraction grating-embedded TiO2 film. For high TiCl4 concentrations of 0.32 M and 0.64 M, the refractive index remained nearly unchanged. This was attributed to the limited permeability of high-viscosity TiCl4 solutions into the nanoporous films. The measured pore size distributions were in good agreement with the results of a diffraction analysis and refractive index measurement.

  17. Synthesis and characterization of thin films of Pd/TiO{sub 2} with possible applications in photo catalysis; Sintesis y caracterizacion de peliculas delgadas de Pd/TiO{sub 2} con posibles aplicaciones en fotocatalisis

    Energy Technology Data Exchange (ETDEWEB)

    Tirado G, S. [IPN, Escuela Superior de Fisica y Matematicas, U. P. Adolfo Lopez Mateos Edif. 9, San Pedro Zacatenco, 07738 Mexico D. F. (Mexico); Valenzuela Z, M. A., E-mail: tirado@esfm.ipn.mx [IPN, Escuela Superior de Ingenieria Quimica e Industrias Extractivas, Laboratorio de Catalisis y Materiales, U. P. Adolfo Lopez Mateos Edif. 8, San Pedro Zacatenco, 07738 Mexico D. F. (Mexico)

    2015-10-15

    In this paper the synthesis and study of thin films of titanium oxide is reported, as well as those that were surface modified with palladium nanoparticles Pd/TiO{sub 2}. First, the TiO{sub 2} films are grown on substrates of soda-lime glass using chemical sol-gel route and the repeated immersion procedure. The salt precursor titanium oxy-acetylacetonate to 0.2 M, in the solvent 2-methoxyethanol and monoethanolamine was used as stabilizer. The number of used immersions gave an average thickness estimate for these films of 172.8 nm. Second, the series of Pd/TiO{sub 2} films surface modified were obtained from a solution of palladium nitrate dehydrate at low concentration, with the same procedure. The films grown TiO{sub 2} and those surface-modified films were characterized in its structure by X-ray diffraction, morphology by scanning electron microscopy, the topography with atomic force microscopy, optical properties by UV-Vis, among others. Photoluminescence properties and/or possible applications in photo catalysis are reported in this paper. (Author)

  18. Photocatalytic properties of nanocrystalline TiO2 thin film with Ag additions

    International Nuclear Information System (INIS)

    Chang, C.-C.; Lin, C.-K.; Chan, C.-C.; Hsu, C.-S.; Chen, C.-Y.

    2006-01-01

    In the present study, nanocrystalline TiO 2 /Ag composite thin films were prepared by a sol-gel spin coating technique. While, by introducing polystyrene (PS) microspheres, porous TiO 2 /Ag films were obtained after calcining at a temperature of 500 o C. The as-prepared TiO 2 and TiO 2 /Ag thin films were characterized by X-ray diffractometry, and scanning electron microscopy to reveal the structural and morphological differences. In addition, the photocatalytic properties of these films were investigated by degrading methylene blue under UV irradiation. After 500 o C calcination, the microstructure of PS-TiO 2 film without Ag addition exhibited a sponge-like microstructure while significant sintering effect was noticed with Ag additions and the films exhibited a porous microstructure. Meanwhile, coalescence of nanocrystalline anatase-phase TiO 2 can be observed with respect to the sharpening of XRD diffraction peaks. The photodegradation of porous TiO 2 doped with 1 mol% Ag exhibited the best photocatalytic efficiency where 72% methylene blue can be decomposed after UV exposure for 12 h

  19. Photoelectrocatalytic Degradation of Organic Pollutants in Aqueous Solution Using a Pt-TiO2 Film

    Directory of Open Access Journals (Sweden)

    Chun He

    2009-01-01

    Full Text Available A series of Pt-TiO2 films with nanocrystaline structure was prepared by a procedure of photodeposition and subsequent dip-coating. The Pt-TiO2 films were characterized by X-ray diffraction, scanning electronic microscope, electrochemical characterization to examine the surface structure, chemical composition, and the photoelectrochemical properties. The photocatalytic activity of the Pt-TiO2 films was evaluated in the photocatalytic (PC and photoelectrocatalytic (PEC degradation of formic acid in aqueous solution. Compared with a TiO2 film, the efficiency of formic acid degradation using the Pt-TiO2 films was significantly higher in both the PC and PEC processes. The enhancement is attributed to the action of Pt deposits on the TiO2 surface, which play a key role by attracting conduction band photoelectrons. In the PEC process, the anodic bias externally applied on the illuminated Pt-TiO2 films can further drive away the accumulated photoelectrons from the metal deposits and promote a process of interfacial charge transfer.

  20. Enhancement of photocatalytic degradation of polyethylene plastic with CuPc modified TiO2 photocatalyst under solar light irradiation

    International Nuclear Information System (INIS)

    Zhao Xu; Li Zongwei; Chen Yi; Shi Liyi; Zhu Yongfa

    2008-01-01

    Solid-phase photocatalytic degradation of polyethylene (PE) plastic, one of the most common commercial plastic, over copper phthalocyanine (CuPc) modified TiO 2 (TiO 2 /CuPc) photocatalyst was investigated in the ambient air under solar light irradiation. Higher PE weight loss rate, greater texture change; more amount of generated CO 2 , which is the main product of the photocatalytic degradation of the composite PEC plastic can be achieved in the system of PE-(TiO 2 /CuPc) in comparison with PE-TiO 2 system. The CuPc promoted charge separation of TiO 2 and enhanced the photocatalytic degradation of PE based on the analysis of surface photovoltage spectroscopy (SPS). During the photodegradation of PE plastic, the reactive oxygen species generated on TiO 2 or TiO 2 /CuPc particle surfaces play important roles. The present study demonstrates that the combination of polymer plastic with TiO 2 /CuPc composite photocatalyst in the form of thin film is a practical and useful way to photodegrade plastic contaminants under solar light irradiation

  1. High Transparent and Conductive TiO2/Ag/TiO2 Multilayer Electrode Films Deposited on Sapphire Substrate

    Science.gov (United States)

    Loka, Chadrasekhar; Moon, Sung Whan; Choi, YiSik; Lee, Kee-Sun

    2018-03-01

    Transparent conducting oxides attract intense interests due to its diverse industrial applications. In this study, we report sapphire substrate-based TiO2/Ag/TiO2 (TAT) multilayer structure of indium-free transparent conductive multilayer coatings. The TAT thin films were deposited at room temperature on sapphire substrates and a rigorous analysis has been presented on the electrical and optical properties of the films as a function of Ag thickness. The optical and electrical properties were mainly controlled by the Ag mid-layer thickness of the TAT tri-layer. The TAT films showed high luminous transmittance 84% at 550 nm along with noteworthy low electrical resistance 3.65 × 10-5 Ω-cm and sheet resistance of 3.77 Ω/square, which is better are than those of amorphous ITO films and any sapphire-based dielectric/metal/dielectric multilayer stack. The carrier concentration of the films was increased with respect to Ag thickness. We obtained highest Hackke's figure of merit 43.97 × 10-3 Ω-1 from the TAT multilayer thin film with a 16 nm thick Ag mid-layer.

  2. NOx photocatalytic degradation on gypsum plates modified by TiO2-N,C photocatalysts

    Directory of Open Access Journals (Sweden)

    Janus Magdalena

    2015-09-01

    Full Text Available In presented studies the photocatalytic decomposition of NOx on gypsum plates modified by TiO2-N,Cphotocatalysts were presented. The gypsum plates were obtained by addition of 10 or 20 wt.% of different types of titanium dioxide, such as: pure TiO2 and carbon and nitrogen co-modified TiO2 (TiO2-N,C to gypsum. TiO2-N,C photocatalysts were obtained by heating up the starting TiO2 (Grupa Azoty Zakłady Chemiczne Police S.A in the atmosphere of ammonia and carbon at the temperature: 100, 300 i 600ºC. Photocatalyst were characterized by FTIR/DRS, UVVis/DR, BET and XRD methods. Moreover the compressive strength tests of modified gypsum were also done. Photocatalytic activity of gypsum plates was done during NOx decomposition. The highest photocatalytic activity has gypsum with 20 wt.% addition of TiO2-N,C obtained at 300ºC.

  3. Antimicrobial Activity of TiO2 Nanoparticle-Coated Film for Potential Food Packaging Applications

    Directory of Open Access Journals (Sweden)

    Siti Hajar Othman

    2014-01-01

    Full Text Available Recent uses of titanium dioxide (TiO2 have involved various applications which include the food industry. This study aims to develop TiO2 nanoparticle-coated film for potential food packaging applications due to the photocatalytic antimicrobial property of TiO2. The TiO2 nanoparticles with varying concentrations (0–0.11 g/ 100 mL organic solvent were coated on food packaging film, particularly low density polyethylene (LDPE film. The antimicrobial activity of the films was investigated by their capability to inactivate Escherichia coli (E. coli in an actual food packaging application test under various conditions, including types of light (fluorescent and ultraviolet (UV and the length of time the film was exposed to light (one–three days. The antimicrobial activity of the TiO2 nanoparticle-coated films exposed under both types of lighting was found to increase with an increase in the TiO2 nanoparticle concentration and the light exposure time. It was also found that the antimicrobial activity of the films exposed under UV light was higher than that under fluorescent light. The developed film has the potential to be used as a food packaging film that can extend the shelf life, maintain the quality, and assure the safety of food.

  4. Effect of chemisorbed surface species on the photocatalytic activity of TiO2 nanoparticulate films

    International Nuclear Information System (INIS)

    Cao Yaan; Yang Wensheng; Chen Yongmei; Du Hui; Yue, Polock

    2004-01-01

    TiO 2 sols prepared in acidic and basic medium were deposited into films by a spin coating method. Photodegradation experiments showed that photocatalytic activity of the films prepared from acidic sol was much higher than that from basic sol. It is identified that there are more chemisorbed species of CO 2 on the surface of the TiO 2 films from the basic sol than on the surface of the TiO 2 films from the acidic sol. The chemisorbed species of CO 2 reduce the concentration of active species such as hydroxyl group and bridging oxygen on surface of the TiO 2 film and contribute to the formation of surface electron traps in the band gap which are detrimental to charge separation, thus lowering the photocatalytic activity

  5. Enhanced Optical and Electrical Properties of TiO{sub 2} Buffered IGZO/TiO{sub 2} Bi-Layered Films

    Energy Technology Data Exchange (ETDEWEB)

    Moon, Hyun-Joo; Kim, Daeil [University of Ulsan, Ulsan (Korea, Republic of)

    2016-08-15

    In and Ga doped ZnO (IGZO, 100-nm thick) thin films were deposited by radio frequency magnetron sputtering without intentional substrate heating on a bare glass substrate and a TiO{sub 2}-deposited glass substrate to determine the effect of the thickness of a thin TiO{sub 2} buffer layer on the structural, optical, and electrical properties of the films. The thicknesses of the TiO{sub 2} buffer layers were 5, 10 and 15 nm, respectively. As-deposited IGZO films with a 10 nm-thick TiO{sub 2} buffer layer had an average optical transmittance of 85.0% with lower resistivity (1.83×10-2 Ω cm) than that of IGZO single layer films. The figure of merit (FOM) reached a maximum of 1.44×10-4 Ω-1 for IGZO/10 nm-thick TiO{sub 2} bi-layered films, which is higher than the FOM of 6.85×10-5 Ω-1 for IGZO single layer films. Because a higher FOM value indicates better quality transparent conducting oxide (TCO) films, the IGZO/10 nm-thick TiO{sub 2} bi-layered films are likely to perform better in TCO applications than IGZO single layer films.

  6. Biocompatibility and Surface Properties of TiO2 Thin Films Deposited by DC Magnetron Sputtering

    Science.gov (United States)

    López-Huerta, Francisco; Cervantes, Blanca; González, Octavio; Hernández-Torres, Julián; García-González, Leandro; Vega, Rosario; Herrera-May, Agustín L.; Soto, Enrique

    2014-01-01

    We present the study of the biocompatibility and surface properties of titanium dioxide (TiO2) thin films deposited by direct current magnetron sputtering. These films are deposited on a quartz substrate at room temperature and annealed with different temperatures (100, 300, 500, 800 and 1100 °C). The biocompatibility of the TiO2 thin films is analyzed using primary cultures of dorsal root ganglion (DRG) of Wistar rats, whose neurons are incubated on the TiO2 thin films and on a control substrate during 18 to 24 h. These neurons are activated by electrical stimuli and its ionic currents and action potential activity recorded. Through X-ray diffraction (XRD), the surface of TiO2 thin films showed a good quality, homogeneity and roughness. The XRD results showed the anatase to rutile phase transition in TiO2 thin films at temperatures between 500 and 1100 °C. This phase had a grain size from 15 to 38 nm, which allowed a suitable structural and crystal phase stability of the TiO2 thin films for low and high temperature. The biocompatibility experiments of these films indicated that they were appropriated for culture of living neurons which displayed normal electrical behavior. PMID:28788667

  7. Production and Characterization of (004) Oriented Single Anatase TiO2 Films

    Science.gov (United States)

    Atay, Ferhunde; Akyuz, Idris; Cergel, Muge Soyleyici; Erdogan, Banu

    2018-02-01

    Highly (004) oriented anatase TiO2 films have been successfully obtained by an inexpensive ultrasonic spray pyrolysis technique at low substrate temperatures and without additional annealing. X-ray diffraction analysis, ultraviolet-visible spectroscopy and field emission scanning electron microscopy were used to analyze the structural, optical and surface properties of the films. By using the less reported TiCl4 solution, the optical band gap values falling into the visible region (between 2.70 eV and 2.92 eV) have been obtained for all films. Spectroscopic ellipsometry technique has been used to determine the dispersive refractive index and extinction coefficient of TiO2 films. Possible electrical conduction mechanisms in TiO2 films have been examined using temperature dependent conductivity measurements in the temperature range of 78-300 K. At room temperature, electrical resistivity values of TiO2 films change between 1.68 × 104 Ω cm and 5.88 × 104 Ω cm. Considering the analyzed parameters with respect to substrate temperature, this work refers to the properties of anatase TiO2 films that are strongly correlated to the growth direction, namely (004). As a result, (004) oriented anatase TiO2 films with appropriate optical band gap values are promising materials for technological applications, especially for photocatalysts.

  8. Enhanced electrochromic properties of TiO2 nanoporous film prepared based on an assistance of polyethylene glycol

    Science.gov (United States)

    Xu, Shunjian; Luo, Xiaorui; Xiao, Zonghu; Luo, Yongping; Zhong, Wei; Ou, Hui; Li, Yinshuai

    2017-01-01

    Polyethylene glycol (PEG) was employed as pore-forming agent to prepare TiO2 nanoporous film based on spin-coating a TiO2 nanoparticle mixed paste on fluorine doped tin oxide (FTO) glass. The electrochromic and optical properties of the obtained TiO2 film were investigated by cyclic voltammetry (CV), chronoamperometry (CA) and UV-Vis spectrophotometer. The results show that the PEG in the mixed paste endows the TiO2 film with well-developed porous structure and improves the uniformity of the TiO2 film, which are helpful for the rapid intercalation and extraction of lithium ions within the TiO2 film and the strengthening of the diffuse reflection of visible light in the TiO2 film. As a result, the TiO2 film derived from the mixed paste with PEG displays higher electrochemical activity and more excellent electrochromic performances compared with the TiO2 film derived from the mixed paste without PEG. The switching times of coloration/bleaching are respectively 10.16/5.65 and 12.77/6.13 s for the TiO2 films with PEG and without PEG. The maximum value of the optical contrast of the TiO2 film with PEG is 21.2% while that of the optical contrast of the TiO2 film without PEG is 14.9%. Furthermore, the TiO2 film with PEG has better stability of the colored state than the TiO2 film without PEG.

  9. TiO2-BASED Composite Films for the Photodegradation of Oxytetracycline

    Science.gov (United States)

    Li, Hui; Guan, Ling-Xiao; Feng, Ji-Jun; Li, Fang; Yao, Ming-Ming

    2015-02-01

    The spread of the antibiotic oxytetracycline (OTC) has been thought as a threat to the safety of drinking water. In this paper, the photocatalytic activity of the nanocrystalline Fe/Ca co-doped TiO2-SiO2 composite film for the degradation of OTC was studied. The films were characterized by field emission scanning electron microscopy (FE-SEM) equipped with energy-dispersive spectroscopy (EDS), N2 adsorption/desorption isotherms, photoluminescence (PL) spectra, and UV-Vis diffraction reflectance absorption spectra (DRS). The FE-SEM results indicated that the Fe/Ca co-doped TiO2-SiO2 film was composed of smaller nanoparticles compared to pure TiO2 or TiO2-SiO2 film. The BET surface area results showed that the specific surface area of the pure TiO2, TiO2-SiO2 and Ca2+/Fe3+ co-doped TiO2-SiO2 is 118.3 m2g-1, 294.3 m2g-1 and 393.7 m2g-1, respectively. The DRS and PL spectra revealed that the Fe/Ca co-doped TiO2-SiO2 film had strong visible light adsorption and diminished electrons/holes recombination. Experimental results showed that the Fe/Ca co-doped TiO2-SiO2 film is effective in the degradation of OTC under both UV and visible light irradiation.

  10. SAXS Studies of TiO2 Nanoparticles in Polymer Electrolytes and in Nanostructured Films

    Directory of Open Access Journals (Sweden)

    Sigrid Bernstorff

    2010-11-01

    Full Text Available Polymer electrolytes as nanostructured materials are very attractive components for batteries and opto-electronic devices. (PEO8ZnCl2 polymer electrolytes were prepared from PEO and ZnCl2. The nanocomposites (PEO8ZnCl2/TiO2 themselves contained TiO2 nanograins. In this work, the influence of the TiO2 nanograins on the morphology and ionic conductivity of the nanocomposite was systematically studied by transmission small-angle X-ray scattering (SAXS simultaneously recorded with wide-angle X-ray diffraction (WAXD and differential scanning calorimetry (DSC at the synchrotron ELETTRA. Films containing nanosized grains of titanium dioxide (TiO2 are widely used in the research of optical and photovoltaic devices. The TiO2 films, prepared by chemical vapor deposition and e-beam epitaxy, were annealed in hydrogen atmospheres in the temperature range between 20 °C and 900 °C in order to study anatase-rutile phase transition at 740 °C. Also, grazing-incidence small angle X-ray scattering (GISAXS spectra for each TiO2 film were measured in reflection geometry at different grazing incident angles. Environmentally friendly galvanic cells, as well as solar cells of the second generation, are to be constructed with TiO2 film as working electrode, and nanocomposite polymer as electrolyte.

  11. Strong out-of-plane magnetic anisotropy in ion irradiated anatase TiO2 thin films

    Directory of Open Access Journals (Sweden)

    M. Stiller

    2016-12-01

    Full Text Available The temperature and field dependence of the magnetization of epitaxial, undoped anatase TiO2 thin films on SrTiO3 substrates was investigated. Low-energy ion irradiation was used to modify the surface of the films within a few nanometers, yet with high enough energy to produce oxygen and titanium vacancies. The as-prepared thin film shows ferromagnetism which increases after irradiation with low-energy ions. An optimal and clear magnetic anisotropy was observed after the first irradiation, opposite to the expected form anisotropy. Taking into account the experimental parameters, titanium vacancies as di-Frenkel pairs appear to be responsible for the enhanced ferromagnetism and the strong anisotropy observed in our films. The magnetic impurities concentrations was measured by particle-induced X-ray emission with ppm resolution. They are ruled out as a source of the observed ferromagnetism before and after irradiation.

  12. Improvement of β-phase crystal formation in a BaTiO3-modified PVDF membrane

    Science.gov (United States)

    Lin, SHEN; Lei, GONG; Shuhua, CHEN; Shiping, ZHAN; Cheng, ZHANG; Tao, SHAO

    2018-04-01

    In this paper, low temperature plasma is used to modify the surface of barium titanate (BaTiO3) nanoparticles in order to enhance the interfacial compatibility between ferroelectric poly(vinylidene fluoride) (PVDF) and BaTiO3 nanoparticles. The results demonstrate that oxygenic groups are successfully attached to the BaTiO3 surface, and the quantity of the functional groups increases with the treatment voltage. Furthermore, the effect of modified BaTiO3 nanoparticles on the morphology and crystal structure of the PVDF/BaTiO3 membrane is investigated. The results reveal that the dispersion of BaTiO3 nanoparticles in the PVDF matrix was greatly improved due to the modification of the BaTiO3 nanoparticles by air plasma. It is worth noting that the formation of a β-phase in a PVDF/modified BaTiO3 membrane is observably promoted, which results from the strong interaction between PVDF chains and oxygenic groups fixed on the BaTiO3 surface and the better dispersion of BaTiO3 nanoparticles in the PVDF matrix. Besides, the PVDF/modified BaTiO3 membrane at the treatment voltage of 24 kV exhibits a lower water contact angle (≈68.4°) compared with the unmodified one (≈86.7°). Meanwhile, the dielectric constant of PVDF/BaTiO3 nanocomposites increases with the increase of working voltage.

  13. The properties of transparent TiO2 films for Schottky photodetector

    Directory of Open Access Journals (Sweden)

    Sung-Ho Park

    2017-08-01

    Full Text Available In this data, the properties of transparent TiO2 film for Schottky photodetector are presented for the research article, entitled as “High-performing transparent photodetectors based on Schottky contacts” (Patel et al., 2017 [1]. The transparent photoelectric device was demonstrated by using various Schottky metals, such as Cu, Mo and Ni. This article mainly shows the optical transmittance of the Ni-transparent Schottky photodetector, analyzed by the energy dispersive spectroscopy and interfacial TEM images for transparency to observe the interface between NiO and TiO2 film. The observation and analyses clearly show that no pinhole formation in the TiO2 film by Ni diffusion. The rapid thermal process is an effective way to form the quality TiO2 film formation without degradation, such as pinholes (Qiu et al., 2015 [2]. This thermal process may apply to form functional metal oxide layers for solar cells and photodetectors.

  14. Atom beam sputtered Ag-TiO{sub 2} plasmonic nanocomposite thin films for photocatalytic applications

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Jaspal; Sahu, Kavita [School of Basic and Applied Sciences, Guru Gobind Singh Indraprastha University, Dwarka, NewDelhi 110078 (India); Pandey, A. [Solid State Physics Laboratory, Defence Research and Development Organization, Timarpur, Delhi 110054 (India); Kumar, Mohit [Institute of Physics, Sachivalaya Marg, Bhubaneswar, Odisha 751005 (India); Ghosh, Tapas; Satpati, B. [Saha Institute of Nuclear Physics, HBNI, 1/AF, Bidhannagar, Kolkata 700064 (India); Som, T.; Varma, S. [Institute of Physics, Sachivalaya Marg, Bhubaneswar, Odisha 751005 (India); Avasthi, D.K. [Amity Institute of Nanotechnology, Noida 201313, Uttar Pradesh (India); Mohapatra, Satyabrata, E-mail: smiuac@gmail.com [School of Basic and Applied Sciences, Guru Gobind Singh Indraprastha University, Dwarka, NewDelhi 110078 (India)

    2017-07-31

    The development of nanocomposite coatings with highly enhanced photocatalytic activity is important for photocatalytic purification of water and air. We report on the synthesis of Ag-TiO{sub 2} nanocomposite thin films with highly enhanced photocatalytic activity by atom beam co-sputtering technique. The effects of Ag concentration on the structural, morphological, optical, plasmonic and photocatalytic properties of the nanocomposite thin films were investigated. UV–visible DRS studies revealed the presence of surface plasmon resonance (SPR) peak characteristic of Ag nanoparticles together with the excitonic absorption peak originating from TiO{sub 2} nanoparticles in the nanocomposites. XRD studies showed that the nanocomposite thin films consist of Ag nanoparticles and rutile TiO{sub 2} nanoparticles. The synthesized Ag-TiO{sub 2} nanocomposite thin films with 5 at% Ag were found to exhibit highly enhanced photocatalytic activity for sun light driven photocatalytic degradation of methylene blue in water, indicating their potential application in water purification.

  15. Cellulose Acetate/N-TiO2 Biocomposite Flexible Films with Enhanced Solar Photochromic Properties

    Science.gov (United States)

    Radhika, T.; Anju, K. R.; Silpa, M. S.; Ramalingam, R. Jothi; Al-Lohedan, Hamad A.

    2017-07-01

    Flexible cellulose acetate/N-TiO2 nanocomposite films containing various concentrations of nanosized N-TiO2 and an intelligent methylene blue ink have been prepared by solution casting. The hydrothermally prepared nitrogen-doped titania (N-TiO2) and the films were characterized in detail. The photochromic properties of the prepared films were investigated under ultraviolet (UV), visible light, and simulated solar irradiation by UV-Vis spectrophotometry. Upon irradiation, the films exhibited rapid photochromic response that was reversible at room temperature. Films with higher content of nano N-TiO2 showed enhanced decoloration/recoloration under all irradiation conditions, with fast decoloration/recoloration under simulated solar irradiation. These results suggest that the amount of nano N-TiO2 in the composite, the concentration of methylene blue, and the solvent greatly influence the photochromic properties of the films. Such flexible and transparent cellulose acetate/N-TiO2 films with enhanced decoloration/recoloration properties under solar irradiation are promising smart materials for use in photoreversible printed electronics applications.

  16. Microstructural properties of BaTiO{sub 3} ceramics and thin films

    Energy Technology Data Exchange (ETDEWEB)

    Fundora C, A.; Portelles, J.J.; Siqueiros, J.M. [Posgrado en Fisica de Materiales, Centro de Investigacion Cientifica y de Educacion Superior de Ensenada. Apartado Postal 2861, 22800 Ensenada, Baja California (Mexico)

    2000-07-01

    A microstructural study of BaTiO{sub 3} ceramics obtained by the conventional ceramic method is presented. Targets were produced to grow BaTiO{sub 3} thin films by pulsed laser deposition on Pt/Ti/Si (100) substrates. X-ray diffraction, Auger Electron Spectroscopy, X-ray Photon Spectroscopy and Scanning Electron Microscopy were used to study the properties of the BaTiO{sub 3} ceramic samples and thin films, as deposited and after an annealing process. (Author)

  17. CO2 Plasma-Treated TiO2 Film as an Effective Electron Transport Layer for High-Performance Planar Perovskite Solar Cells.

    Science.gov (United States)

    Wang, Kang; Zhao, Wenjing; Liu, Jia; Niu, Jinzhi; Liu, Yucheng; Ren, Xiaodong; Feng, Jiangshan; Liu, Zhike; Sun, Jie; Wang, Dapeng; Liu, Shengzhong Frank

    2017-10-04

    Perovskite solar cells (PSCs) have received great attention because of their excellent photovoltaic properties especially for the comparable efficiency to silicon solar cells. The electron transport layer (ETL) is regarded as a crucial medium in transporting electrons and blocking holes for PSCs. In this study, CO 2 plasma generated by plasma-enhanced chemical vapor deposition (PECVD) was introduced to modify the TiO 2 ETL. The results indicated that the CO 2 plasma-treated compact TiO 2 layer exhibited better surface hydrophilicity, higher conductivity, and lower bulk defect state density in comparison with the pristine TiO 2 film. The quality of the stoichiometric TiO 2 structure was improved, and the concentration of oxygen-deficiency-induced defect sites was reduced significantly after CO 2 plasma treatment for 90 s. The PSCs with the TiO 2 film treated by CO 2 plasma for 90 s exhibited simultaneously improved short-circuit current (J SC ) and fill factor. As a result, the PSC-based TiO 2 ETL with CO 2 plasma treatment affords a power conversion efficiency of 15.39%, outperforming that based on pristine TiO 2 (13.54%). These results indicate that the plasma treatment by the PECVD method is an effective approach to modify the ETL for high-performance planar PSCs.

  18. Pulsed Laser Deposition of BaTiO3 Thin Films on Different Substrates

    Directory of Open Access Journals (Sweden)

    Yaodong Yang

    2010-01-01

    Full Text Available We have studied the deposition of BaTiO3 (BTO thin films on various substrates. Three representative substrates were selected from different types of material systems: (i SrTiO3 single crystals as a typical oxide, (ii Si wafers as a semiconductor, and (iii Ni foils as a magnetostrictive metal. We have compared the ferroelectric properties of BTO thin films obtained by pulsed laser deposition on these diverse substrates.

  19. Effects of LP-MOCVD prepared TiO2 thin films on the in vitro behavior of gingival fibroblasts

    International Nuclear Information System (INIS)

    Cimpean, Anisoara; Popescu, Simona; Ciofrangeanu, Cristina M.; Gleizes, Alain N.

    2011-01-01

    We report on the in vitro response of human gingival fibroblasts (HGF-1 cell line) to various thin films of titanium dioxide (TiO 2 ) deposited on titanium (Ti) substrates by low pressure metal-organic chemical vapor deposition (LP-MOCVD). The aim was to study the influence of film structural parameters on the cell behavior comparatively with a native-oxide covered titanium specimen, this objective being topical and interesting for materials applications in implantology. HGF-1 cells were cultured on three LP-MOCVD prepared thin films of TiO 2 differentiated by their thickness, roughness, transversal morphology, allotropic composition and wettability, and on a native-oxide covered Ti substrate. Besides traditional tests of cell viability and morphology, the biocompatibility of these materials was evaluated by fibronectin immunostaining, assessment of cell proliferation status and the zymographic evaluation of gelatinolytic activities specific to matrix metalloproteinases secreted by cells grown in contact with studied specimens. The analyzed surfaces proved to influence fibronectin fibril assembly, cell proliferation and capacity to degrade extracellular matrix without considerably affecting cell viability and morphology. The MOCVD of TiO 2 proved effective in positively modifying titanium surface for medical applications. Surface properties playing a crucial role for cell behavior were the wettability and, secondarily, the roughness, HGF-1 cells preferring a moderately rough and wettable TiO 2 coating.

  20. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    OpenAIRE

    Rafieian Boroujeni, Damon; Ogieglo, Wojciech; Savenije, Tom; Lammertink, Rob G.H.

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx

  1. Photo-oxidative degradation of TiO{sub 2}/polypropylene films

    Energy Technology Data Exchange (ETDEWEB)

    García-Montelongo, X.L. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Martínez-de la Cruz, A., E-mail: azael70@yahoo.com.mx [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Vázquez-Rodríguez, S. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Torres-Martínez, Leticia M. [Facultad de Ingeniería Civil, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico)

    2014-03-01

    Graphical abstract: - Highlights: • Photo-oxidative degradation of polypropylene is accelerated by TiO{sub 2} incorporation. • Weight loss, FTIR, SEM and GPC shown high degree of degradation of polypropylene. • A mechanism of the photo-degradation of polypropylene by TiO{sub 2} is proposed. - Abstract: Photo-oxidative degradation of polypropylene films with TiO{sub 2} nanoparticles incorporated was studied in a chamber of weathering with Xenon lamps as irradiation source. TiO{sub 2} powder with crystalline structure of anatase was synthesized by thermal treatments at 400 and 500 °C starting from a precursor material obtained by sol–gel method. Composites of TiO{sub 2}/polypropylene were prepared with 0.1, 0.5 and 1.0 wt% of TiO{sub 2}. The mixture of components was performed using a twin screw extruder, the resulting material was pelletized by mechanical fragmenting and then hot-pressed in order to form polypropylene films with TiO{sub 2} dispersed homogeneously. Photo-oxidative degradation process was followed by visual inspection, weight loss of films, scanning electron microscopy (SEM), infrared spectroscopy with Fourier transformed (FTIR), and gel permeation chromatography (GPC)

  2. Thiourea-Modified TiO2 Nanorods with Enhanced Photocatalytic Activity

    Directory of Open Access Journals (Sweden)

    Xiaofeng Wu

    2016-02-01

    Full Text Available Semiconductor TiO2 photocatalysis has attracted much attention due to its potential application in solving the problems of environmental pollution. In this paper, thiourea (CH4N2S modified anatase TiO2 nanorods were fabricated by calcination of the mixture of TiO2 nanorods and thiourea at 600 °C for 2 h. It was found that only N element was doped into the lattice of TiO2 nanorods. With increasing the weight ratio of thiourea to TiO2 (R from 0 to 8, the light-harvesting ability of the photocatalyst steady increases. Both the crystallization and photocatalytic activity of TiO2 nanorods increase first and then decrease with increase in R value, and R2 sample showed the highest crystallization and photocatalytic activity in degradation of Brilliant Red X3B (X3B and Rhodamine B (RhB dyes under visible light irradiation (λ > 420 nm. The increased visible-light photocatalytic activity of the prepared N-doped TiO2 nanorods is due to the synergistic effects of the enhanced crystallization, improved light-harvesting ability and reduced recombination rate of photo-generated electron-hole pairs. Note that the enhanced visible photocatalytic activity of N-doped nanorods is not based on the scarification of their UV photocatalytic activity.

  3. Polymer Photovoltaic Cell Using TiO2/G-PEDOT Nanocomplex Film as Electrode

    Directory of Open Access Journals (Sweden)

    F. X. Xie

    2008-01-01

    Full Text Available Using TiO2/G-PEDOT (PEDOT/PSS doped with glycerol nanocomplex film as a substitute for metal electrode in organic photovoltaic cell is described. Indium tin oxide (ITO worked as cathode and TiO2/G-PEDOT nanocomplex works as anode. The thickness of TiO2 layer in nanocomplex greatly affects the act of this nonmetallic electrode of the device. To enhance its performance, this inverted organic photovoltaic cell uses another TiO2 layer as electron selective layer contacted to ITO coated glass substrates. All films made by solution processing techniques are coated on the transparent substrate (glass with a conducting film ITO. The efficiency of this solar cell is compared with the conventional device using Al as electrode.

  4. Self-Organized Ni Nanocrystal Embedded in BaTiO3 Epitaxial Film

    Directory of Open Access Journals (Sweden)

    Ge FF

    2010-01-01

    Full Text Available Abstract Ni nanocrystals (NCs were embedded in BaTiO3 epitaxial films using the laser molecular beam epitaxy. The processes involving the self-organization of Ni NCs and the epitaxial growth of BaTiO3 were discussed. With the in situ monitoring of reflection high-energy electron diffraction, the nanocomposite films were engineered controllably by the fine alternation of the self-organization of Ni NCs and the epitaxial growth of BaTiO3. The transmission electron microscopy and the X-ray diffraction characterization confirmed that the composite film consists of the Ni NCs layers alternating with the (001/(100-oriented epitaxial BaTiO3 separation layers.

  5. Surface functionalization of cyclic olefin copolymer (COC) with evaporated TiO{sub 2} thin film

    Energy Technology Data Exchange (ETDEWEB)

    El Fissi, Lamia, E-mail: lamia.elfissi@uclouvain.be [ICTEAM Institute, Université catholique du Louvain, place de Levant 3, 1348 Louvain-la-Neuve (Belgium); Vandormael, Denis [SIRRIS Liege Science Park, 4102 Seraing (Belgium); Houssiau, Laurent [Research Centre in Physics of Matter and Radiation (PMR), University of Namur, Rue de Bruxelles 61, B-5000 Namur (Belgium); Francis, Laurent A. [ICTEAM Institute, Université catholique du Louvain, place de Levant 3, 1348 Louvain-la-Neuve (Belgium)

    2016-02-15

    Highlights: • TiO{sub 2}/COC (cyclic olefin copolymer) hybrid material for BioMEMS applications. • Thin layer of TiO{sub 2} was deposed on cyclic olefin copolymer using physical vapor deposition (PVD) technique. • The coating possess the highest level of adhesion with an excellent morphology of the hybrid material (TiO{sub 2}/COC). - Abstract: Cyclic olefin copolymer (COC) is a new class of thermoplastic polymers used for a variety of applications ranging from bio-sensing to optics. However, the hydrophobicity of native COC hampers the further development and application of this material [1]. In this work, we report the structural, morphological, and optical properties of the TiO{sub 2}/COC hybrid material, which provides a desirable substrate for optical devices and subsequent surface modifications. The TiO{sub 2} film on COC substrate was deposited by the evaporation method, and it was characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), profilometry and atomic force microscope (AFM). Using an UV-vis spectrophotometer, we found that the transmittance of the TiO{sub 2}/COC hybrid material in the visible domain reached 80%. The TiO{sub 2}/COC hybrid appeared to be stable in most of the assessed polar solvents and acid/basic solutions. The new TiO{sub 2}/COC hybrid material and the robust fabrication method are expected to enable a variety of BioMEMS applications.

  6. Thermoelectric properties of conducting polyaniline/BaTiO3 nanoparticle composite films

    Science.gov (United States)

    Anno, H.; Yamaguchi, K.; Nakabayashi, T.; Kurokawa, H.; Akagi, F.; Hojo, M.; Toshima, N.

    2011-05-01

    Conducting polyaniline (PANI)/BaTiO3 nanoparticle composite films with different molar ratio values R=1, 5, 10, and 100 have been prepared on a quartz substrate by casting the m-cresol solution of PANI, (±)-10-camphorsulfonic acid (CSA) and BaTiO3 nanoparticle with an average diameter of about 20 nm. The CSA-doped PANI/BaTiO3 composite films were characterized by x-ray diffraction, Fourier transform infrared spectroscopy, and UV-Vis transmission spectroscopy. The Seebeck coefficient and the electrical conductivity of the films with different R values, together with CSA-doped PANI films, were measured in the temperature range from room temperature to ~400 K. The relation between the Seebeck coefficient and the electrical conductivity in the composite films are discussed from a comparison of them with those of CSA-doped PANI films and other PANI composite films.

  7. Photocatalysis and characterization of the gel-derived TiO{sub 2} and P-TiO{sub 2} transparent thin films

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Hsuan-Fu, E-mail: hfyu@mail.tku.edu.tw [Department of Chemical and Materials Engineering, Ceramic Materials Laboratory, Tamkang University, Taipei 25137, Taiwan (China); Energy and Opto-Electronic Materials Research Center, Tamkang University, Taipei 25137, Taiwan (China); Wang, Chang-Wen [Department of Chemical and Materials Engineering, Ceramic Materials Laboratory, Tamkang University, Taipei 25137, Taiwan (China)

    2011-07-29

    The gel-derived TiO{sub 2} and P-TiO{sub 2} transparent films coated on fused-SiO{sub 2} substrates were prepared using a spin-coating technique. Effects of phosphorus dopants and calcination temperature on crystal structure, crystallite size, microstructure, light transmittance and photocatalytic activity of the films were investigated. By introducing P atoms to Ti-O framework, the growth of anatase crystallites was hindered and the crystal structure of anatase-TiO{sub 2} could withstand temperature up to 900 deg. C. The photocatalytic activities of the prepared films were characterized using the characteristic time constant ({tau}) for the photocatalytic reaction. The titania film with a smaller {tau} value possesses a higher photocatalytic ability. After exposing to 365-nm UV light for 12 h, the P-TiO{sub 2} films calcined between 600 deg. C and 900 deg. C can photocatalytically decomposed {>=} 84 mol% of the methylene blue in water with corresponding {tau} {<=} 7.1 h, which were better than the pure TiO{sub 2} films prepared at the same calcination temperature.

  8. Multi-Layered TiO2 Films towards Enhancement of Escherichia coli Inactivation

    Directory of Open Access Journals (Sweden)

    Sorachon Yoriya

    2016-09-01

    Full Text Available Crystalline TiO2 has shown its great photocatalytic properties in bacterial inactivation. This work presents a design fabrication of low-cost, layered TiO2 films assembled reactors and a study of their performance for a better understanding to elucidate the photocatalytic effect on inactivation of E. coli in water. The ability to reduce the number of bacteria in water samples for the layered TiO2 composing reactors has been investigated as a function of time, while varying the parameters of light sources, initial concentration of bacteria, and ratios of TiO2 film area and volume of water. Herein, the layered TiO2 films have been fabricated on the glass plates by thermal spray coating prior to screen printing, allowing a good adhesion of the films. Surface topology and crystallographic phase of TiO2 for the screen-printed active layer have been characterized, resulting in the ratio of anatase:rutile being 80:20. Under exposure to sunlight and a given condition employed in this study, the optimized film area:water volume of 1:2.62 has shown a significant ability to reduce the E. coli cells in water samples. The ratio of surface area of photocatalytic active base to volume of water medium is believed to play a predominant role facilitating the cells inactivation. The kinetic rate of inactivation and its behavior are also described in terms of adsorption of reaction species at different contact times.

  9. The Comparative PDT Experiment of the Inactivation of HL60 on Modified TiO2 Nanoparticles

    Directory of Open Access Journals (Sweden)

    Kaiqi Lu

    2015-01-01

    Full Text Available Four samples of modified titanium dioxide (TiO2, Fe/TiO2 (2 wt%, Fe/TiO2 (5 wt%, and 5-ALA/TiO2, were experimented in photodynamic therapy (PDT on leukemia cells HL60, performing promising photocatalytic inactivation effect. Fe/TiO2 and 5-ALA/TiO2 were synthesized in methods of precipitation and ultrasonic methods, respectively. X-ray diffraction spectra and UV-Vis spectra were studied for the samples’ crystalline phase and redshift of absorption peak. Further, FTIR spectra and Raman spectra were obtained to examine the combination of 5-aminolevulinic (5-ALA and TiO2 nanoparticles. The toxicity of these four kinds of nanoparticles was studied through darkroom experiments. And based on the concentration which caused the same toxic effect (90% on HL60, PDT experiments of TiO2, Fe/TiO2 (2%, Fe/TiO2 (5%, and ALA/TiO2 were done, resulting in the fact that the photokilling efficiency was 69.7%, 71.6%, 72%, and 80.6%, respectively. Scanning electron microscope (SEM images of the samples were also taken to study the morphology of HL60 cells before and after PDT, resulting in the fact the activation of the modified TiO2 from PDT was the main cause of cell apoptosis.

  10. Study on Gas Sensing Performance of TiO2 Screen Printed Thick Films

    Directory of Open Access Journals (Sweden)

    C. G. DIGHAVKAR

    2009-02-01

    Full Text Available Titanium dioxide (TiO2 thick films were prepared on alumina substrate by using screen printing technique. After preparation, the films were fired at temperature range 600 -1000 ºC for two hour. Morphological, compositional and structural properties of the film samples were performed by means of several techniques, including scanning electron microscopy (SEM, Energy dispersive spectroscopy (EDS, X-ray diffraction techniques. We explore the various gases to study the sensing performance of the TiO2 thick films. The maximum response was reported to film fired at 800 0C for LPG gas at 350 0C operating temperature.

  11. Synthesis of Ag-TiO2 composite nano thin film for antimicrobial application

    Science.gov (United States)

    Yu, Binyu; Leung, Kar Man; Guo, Qiuquan; Lau, Woon Ming; Yang, Jun

    2011-03-01

    TiO2 photocatalysts have been found to kill cancer cells, bacteria and viruses under mild UV illumination, which offers numerous potential applications. On the other hand, Ag has long been proved as a good antibacterial material as well. The advantage of Ag-TiO2 nanocomposite is to expand the nanomaterial's antibacterial function to a broader range of working conditions. In this study neat TiO2 and Ag-TiO2 composite nanofilms were successfully prepared on silicon wafer via the sol-gel method by the spin-coating technique. The as-prepared composite Ag-TiO2 and TiO2 films with different silver content were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), x-ray diffraction (XRD) and x-ray photoelectron spectroscopy (XPS) to determine the topologies, microstructures and chemical compositions, respectively. It was found that the silver nanoparticles were uniformly distributed and strongly attached to the mesoporous TiO2 matrix. The morphology of the composite film could be controlled by simply tuning the molar ratio of the silver nitrate aqueous solution. XPS results confirmed that the Ag was in the Ag0 state. The antimicrobial effect of the synthesized nanofilms was carried out against gram-negative bacteria (Escherichia coli ATCC 29425) by using an 8 W UV lamp with a constant relative intensity of 0.6 mW cm - 2 and in the dark respectively. The synthesized Ag-TiO2 thin films showed enhanced bactericidal activities compared to the neat TiO2 nanofilm both in the dark and under UV illumination.

  12. Synthesis of Ag-TiO2 composite nano thin film for antimicrobial application

    International Nuclear Information System (INIS)

    Yu Binyu; Guo Qiuquan; Yang Jun; Leung, Kar Man; Lau, Woon Ming

    2011-01-01

    TiO 2 photocatalysts have been found to kill cancer cells, bacteria and viruses under mild UV illumination, which offers numerous potential applications. On the other hand, Ag has long been proved as a good antibacterial material as well. The advantage of Ag-TiO 2 nanocomposite is to expand the nanomaterial's antibacterial function to a broader range of working conditions. In this study neat TiO 2 and Ag-TiO 2 composite nanofilms were successfully prepared on silicon wafer via the sol-gel method by the spin-coating technique. The as-prepared composite Ag-TiO 2 and TiO 2 films with different silver content were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), x-ray diffraction (XRD) and x-ray photoelectron spectroscopy (XPS) to determine the topologies, microstructures and chemical compositions, respectively. It was found that the silver nanoparticles were uniformly distributed and strongly attached to the mesoporous TiO 2 matrix. The morphology of the composite film could be controlled by simply tuning the molar ratio of the silver nitrate aqueous solution. XPS results confirmed that the Ag was in the Ag 0 state. The antimicrobial effect of the synthesized nanofilms was carried out against gram-negative bacteria (Escherichia coli ATCC 29425) by using an 8 W UV lamp with a constant relative intensity of 0.6 mW cm -2 and in the dark respectively. The synthesized Ag-TiO 2 thin films showed enhanced bactericidal activities compared to the neat TiO 2 nanofilm both in the dark and under UV illumination.

  13. Synthesis of Ag-TiO{sub 2} composite nano thin film for antimicrobial application

    Energy Technology Data Exchange (ETDEWEB)

    Yu Binyu; Guo Qiuquan; Yang Jun [Biomedical Engineering Graduate Program, University of Western Ontario, London, ON, N6A 5B9 (Canada); Leung, Kar Man [Department of Mechanical and Materials Engineering, University of Western Ontario, London, ON, N6A 5B9 (Canada); Lau, Woon Ming [Surface Science Western, University of Western Ontario, London, ON, N6A 5B9 (Canada)

    2011-03-18

    TiO{sub 2} photocatalysts have been found to kill cancer cells, bacteria and viruses under mild UV illumination, which offers numerous potential applications. On the other hand, Ag has long been proved as a good antibacterial material as well. The advantage of Ag-TiO{sub 2} nanocomposite is to expand the nanomaterial's antibacterial function to a broader range of working conditions. In this study neat TiO{sub 2} and Ag-TiO{sub 2} composite nanofilms were successfully prepared on silicon wafer via the sol-gel method by the spin-coating technique. The as-prepared composite Ag-TiO{sub 2} and TiO{sub 2} films with different silver content were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), x-ray diffraction (XRD) and x-ray photoelectron spectroscopy (XPS) to determine the topologies, microstructures and chemical compositions, respectively. It was found that the silver nanoparticles were uniformly distributed and strongly attached to the mesoporous TiO{sub 2} matrix. The morphology of the composite film could be controlled by simply tuning the molar ratio of the silver nitrate aqueous solution. XPS results confirmed that the Ag was in the Ag{sup 0} state. The antimicrobial effect of the synthesized nanofilms was carried out against gram-negative bacteria (Escherichia coli ATCC 29425) by using an 8 W UV lamp with a constant relative intensity of 0.6 mW cm{sup -2} and in the dark respectively. The synthesized Ag-TiO{sub 2} thin films showed enhanced bactericidal activities compared to the neat TiO{sub 2} nanofilm both in the dark and under UV illumination.

  14. Single-Nanoparticle Photoelectrochemistry at a Nanoparticulate TiO2 -Filmed Ultramicroelectrode.

    Science.gov (United States)

    Peng, Yue-Yi; Ma, Hui; Ma, Wei; Long, Yi-Tao; Tian, He

    2018-03-26

    An ultrasensitive photoelectrochemical method for achieving real-time detection of single nanoparticle collision events is presented. Using a micrometer-thick nanoparticulate TiO 2 -filmed Au ultra-microelectrode (TiO 2 @Au UME), a sub-millisecond photocurrent transient was observed for an individual N719-tagged TiO 2 (N719@TiO 2 ) nanoparticle and is due to the instantaneous collision process. Owing to a trap-limited electron diffusion process as the rate-limiting step, a random three-dimensional diffusion model was developed to simulate electron transport dynamics in TiO 2 film. The combination of theoretical simulation and high-resolution photocurrent measurement allow electron-transfer information of a single N719@TiO 2 nanoparticle to be quantified at single-molecule accuracy and the electron diffusivity and the electron-collection efficiency of TiO 2 @Au UME to be estimated. This method provides a test for studies of photoinduced electron transfer at the single-nanoparticle level. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  15. Zirconium doped TiO{sub 2} thin films deposited by chemical spray pyrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Juma, A. [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Department of Physics and Astronomy, Botswana International University of Science and Technology, Private bag 16, Palapye (Botswana); Oja Acik, I., E-mail: ilona.oja@ttu.ee [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Oluwabi, A.T.; Mere, A. [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Mikli, V.; Danilson, M. [Chair of Semiconductor Materials Technology, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Krunks, M. [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia)

    2016-11-30

    Highlights: • Mean crystallite size of TiO{sub 2}:Zr film decreases with increasing [Zr] in the solution. • Zr doping supresses the anatase to rutile transformation process in TiO{sub 2} films. • Band gap of TiO{sub 2}:Zr film is 3.4 eV irrespective of the annealing temperature. - Abstract: Chemical spray pyrolysis (CSP) is a flexible deposition technique that allows for mixing of the precursor solutions in different proportions suitable for doping thin films. The CSP method was used to dope TiO{sub 2} thin films with Zr by adding zirconium(IV) acetylacetonate into a solution of titanium(IV) isopropoxide in ethanol stabilized by acetylacetone at [Zr]/[Ti] of 0, 5, 10 and 20 at%. The Zr-doped TiO{sub 2} thin films were uniform and homogeneous showing much smaller grains than the undoped TiO{sub 2} films. Zr stabilized the anatase phase to temperatures above 800 °C depending on Zr concentration in the spray solution. The concentration of Zr determined by XPS was 6.4 at% for the thin film deposited from the 20 at% solution. According to AFM studies, Zr doping decreased the root mean square roughness of TiO{sub 2} film from 5.9 to 1.1 nm. An XRD study of samples with the highest Zr amount showed the ZrTiO{sub 4} phase started forming after annealing at 800 °C. The optical band gap for TiO{sub 2} decreased from 3.3 eV to 3.0 eV after annealing at 800 °C but for the TiO{sub 2}:Zr(20) film it remained at 3.4 eV. The dielectric constant increased by more than four times with Zr-doping and this was associated with the change in the bond formations caused by substitution of Ti by Zr in the lattice.

  16. Surface properties of UV irradiated PC–TiO{sub 2} nanocomposite film

    Energy Technology Data Exchange (ETDEWEB)

    Jaleh, B., E-mail: bkjaleh@yahoo.com; Shahbazi, N.

    2014-09-15

    Highlights: • Production of PC–TiO{sub 2} nanocomposite films. • Fully characterization of PC–TiO{sub 2} nanocomposite films. • Influence of UV irradiation on surface properties and hardness of PC–TiO{sub 2} nanocomposite film. - Abstract: In this work, polycarbonate–TiO{sub 2} nanocomposite films were prepared with two different percentages. The structure of samples were studied by X-ray diffraction. Thermal stability of the nanocomposites was studied by thermogravimetric analysis (TGA). The polycarbonate and polycarbonate–TiO{sub 2} nanocomposite films were exposed by UV light at different irradiation times. The effects of UV irradiation on the surface properties of samples have been studied by different characterization techniques, viz. scanning electron microscopy (SEM), FTIR spectroscopy, X-ray photoelectron spectroscopy (XPS), contact angle measurement and Vickers microhardness tester. Hydrophilicity and surface energy of UV treated samples varied depending on UV irradiation time. TGA curves showed that nanocomposite films have higher resistance to thermal degradation compared to polycarbonate. XPS analysis shows that surface of samples become more oxidized due to UV irradiation. For nanocomposite film, the smallest contact angle was observed in association with the longest UV irradiation time. The contact angle significantly decreased from 90° to 12° after 15 h of UV irradiation. It is observed that the hardness of the nanocomposite films increases after UV irradiation.

  17. Nitrogen and europium doped TiO2 anodized films with applications in photocatalysis

    International Nuclear Information System (INIS)

    Chi, Choong-Soo; Choi, Jinwook; Jeong, Yongsoo; Lee, Oh Yeon; Oh, Han-Jun

    2011-01-01

    Micro-arc oxidation method is a useful process for mesoporous titanium dioxide films. In order to improve the photocatalytic activity of the TiO 2 film, N-Eu co-doped titania catalyst was synthesized by micro-arc oxidation in the H 2 SO 4 /Eu(NO 3 ) 3 mixture solution. The specific surface area and the roughness of the anodic titania film fabricated in the H 2 SO 4 /Eu(NO 3 ) 3 electrolyte, were increased compared to that of the anodic TiO 2 film prepared in H 2 SO 4 solution. The absorbance response of N-Eu titania film shows a higher adsorption onset toward visible light region, and the incorporated N and Eu ions during anodization as a dopant in the anodic TiO 2 film significantly enhanced the photocatalytic activity for dye degradation. After dye decomposition test for 3 h, dye removal rates for the anodic TiO 2 film were 60.7% and 90.1% for the N-Eu doped titania film. The improvement of the photocatalytic activity was ascribed to the synergistic effects of the surface enlargement and the new electronic state of the TiO 2 band gap by N and Eu co-doping.

  18. Visible-light photocatalytic activity of nitrided TiO2 thin films

    International Nuclear Information System (INIS)

    Camps, Enrique; Escobar-Alarcon, L.; Camacho-Lopez, Marco Antonio; Casados, Dora A. Solis

    2010-01-01

    TiO 2 thin films have been applied in UV-light photocatalysis. Nevertheless visible-light photocatalytic activity would make this material more attractive for applications. In this work we present results on the modification of titanium oxide (anatase) sol-gel thin films, via a nitriding process using a microwave plasma source. After the treatment in the nitrogen plasma, the nitrogen content in the TiO 2 films varied in the range from 14 up to 28 at%. The titanium oxide films and the nitrided ones were characterized by XPS, micro-Raman spectroscopy and UV-vis spectroscopy. Photocatalytic activity tests were done using a Methylene Blue dye solution, and as catalyst TiO 2 and nitrided TiO 2 films. The irradiation of films was carried out with a lamp with emission in the visible (without UV). The results showed that the nitrided TiO 2 films had photocatalytic activity, while the unnitrided films did not.

  19. A chemical route to room-temperature synthesis of nanocrystalline TiO2 thin films

    International Nuclear Information System (INIS)

    Pathan, Habib M.; Kim, Woo Young; Jung, Kwang-Deog; Joo, Oh-Shim

    2005-01-01

    A lot of methods are developed for the deposition of TiO 2 thin films; however, in each of these methods as-deposited films are amorphous and need further heat treatment at high temperature. In the present article, a chemical bath deposition (CBD) method was used for the preparation of TiO 2 thin films. We investigated nanocrystalline TiO 2 thin films using CBD at room temperature onto glass and ITO coated glass substrate. The films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and high-resolution transmission electron microscopy (HRTEM) techniques. The chemically synthesized films were nanocrystalline and composed of crystal grains of 2-3 nm

  20. Nucleation control and inhibition of BaTiO3 films using hydrothermal-electrochemical method

    International Nuclear Information System (INIS)

    Escobar, Ivan; Silva, Carmen; Silva, Eric; Vargas, Tomas; Fuenzalida, Victor

    1999-01-01

    The microstructure of BaTiO 3 films on titanium by the hydrothermal-electrochemical method was investigated using a three electrode high pressure electrochemical cell in a 0.2 M Ba(OH) 2 electrolyte at 150 0 C. The spontaneous initial linked to pure hydrothermal BaTiO 3 formation can be inhibited by cathodically protecting titanium electrode since its immersion in the electrolyte. The application of initial nucleation pulses of varying the cathodic potentials affected the grain size of the deposit. It is suggested that the formation of a titanium oxide layers is a necessary step previous to the nucleation of BaTiO 3

  1. Epitaxial growth of SrTiO3 thin film on Si by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Zhou, X. Y.; Miao, J.; Dai, J. Y.; Chan, H. L. W.; Choy, C. L.; Wang, Y.; Li, Q.

    2007-01-01

    SrTiO 3 thin films have been deposited on Si (001) wafers by laser molecular beam epitaxy using an ultrathin Sr layer as the template. X-ray diffraction measurements indicated that SrTiO 3 was well crystallized and epitaxially aligned with Si. Cross-sectional observations in a transmission electron microscope revealed that the SrTiO 3 /Si interface was sharp, smooth, and fully crystallized. The thickness of the Sr template was found to be a critical factor that influenced the quality of SrTiO 3 and the interfacial structure. Electrical measurements revealed that the SrTiO 3 film was highly resistive

  2. Changes in the microbiological and chemical characteristics of white bread during storage in paper packages modified with Ag/TiO2-SiO2, Ag/N-TiO2 or Au/TiO2.

    Science.gov (United States)

    Peter, Anca; Mihaly-Cozmuta, Leonard; Mihaly-Cozmuta, Anca; Nicula, Camelia; Ziemkowska, Wanda; Basiak, Dariusz; Danciu, Virginia; Vulpoi, Adriana; Baia, Lucian; Falup, Anca; Craciun, Grigore; Ciric, Alexandru; Begea, Mihaela; Kiss, Claudia; Vatuiu, Daniela

    2016-04-15

    Microbiological and chemical characteristics of white bread during storage in paper-packages modified with Ag/TiO2-SiO2, Ag/N-TiO2 or Au/TiO2 were investigated. The whiteness and the water retention of the modified packages were slightly superior to those exhibited by the reference sample, as the color of the composite was lighter. The water retention was very good especially for the Ag/TiO2-SiO2-paper. These improvements can be associated with the high specific surface area and with the low agglomeration tendency of Ag nanoparticles in comparison with the Au ones. The preservation activity of the composites for the bread storage is positively influenced by photoactivity and presence of nano-Ag. Packages Ag/TiO2-SiO2-paper and Ag/N-TiO2-paper can find their applicability for extending the shelf life of bread by 2 days as compared with the unmodified paper-package. No influence of the Au/TiO2 on the extending the shelf life of bread was observed. Copyright © 2015 Elsevier Ltd. All rights reserved.

  3. Sol-Gel TiO2 thin films sensitized with the mulberry pigment cyanidin

    Directory of Open Access Journals (Sweden)

    Emerson Henrique de Faria

    2007-12-01

    Full Text Available TiO2 films have various applications, among them solar cells and photodegradation of pollutants. In this study, we investigated TiO2 films functionalized with the organic dye cyanidin extracted from black mulberry (Morus nigra. The TiO2 was functionalized by the sol-gel method and the film was deposited on glass substrates by dip-coating. Our aim was to investigate the interaction between the semiconductor and the dye, as well as the influence of the velocity and number of deposits on the characteristics of the film. Using ultraviolet-visible spectroscopy, we observed a shift from the maximum absorption band at 545 nm for the dye’s ethanol solution to 595 nm for the film, indicating interaction of the cyanidin with the TiO2. The absorption spectra in the infrared region of the functionalized TiO2 particles showed bands characteristic of the oxide and indicated their interaction with the dye. Using profilometry and m-line techniques, we found that the films presented thicknesses in the order of 100 nm. A SEM analysis confirmed the high density of the films.

  4. Photocatalytic Reduction of CO2 to Methane on Pt/TiO2 Nanosheet Porous Film

    Directory of Open Access Journals (Sweden)

    Li Qiu-ye

    2014-01-01

    Full Text Available Anatase TiO2 nanosheet porous films were prepared by calcination of the orthorhombic titanic acid films at 400°C. They showed an excellent photocatalytic activity for CO2 photoreduction to methane, which should be related to their special porous structure and large Brunauer-Emmett-Teller (BET surface area. In order to further improve the photocatalytic activity, Pt nanoparticles were loaded uniformly with the average size of 3-4 nm on TiO2 porous films by the photoreduction method. It was found that the loading of Pt expanded the light absorption ability of the porous film and improved the transformation efficiency of CO2 to methane. The conversion yield of CO2 to methane on Pt/TiO2 film reached 20.51 ppm/h·cm2. The Pt/TiO2 nanosheet porous film was characterized by means of X-ray diffraction (XRD, scanning electron microscopy (SEM, transmission electron microscope (TEM, and ultraviolet-visible light diffuse reflectance spectra (UV-vis DRS. Moreover, the transient photocurrent-time curves showed that the Pt/TiO2 nanosheet porous film exhibited higher photocurrent, indicating that the higher separation efficiency of the photogenerated charge carriers was achieved.

  5. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    NARCIS (Netherlands)

    Rafieian Boroujeni, Damon; Ogieglo, Wojciech; Savenije, Tom; Lammertink, Rob G.H.

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to

  6. Dye sensitized solar cell applications of CdTiO{sub 3}–TiO{sub 2} composite thin films deposited from single molecular complex

    Energy Technology Data Exchange (ETDEWEB)

    Ehsan, Muhammad Ali [Nanotechnology and Catalysis Centre (NANOCAT), University of Malaya, Lembah Pantai, 50603 Kuala Lumpur (Malaysia); Khaledi, Hamid [Department of Chemistry, Faculty of Science, University of Malaya, Lembah Pantai, 50603 Kuala Lumpur (Malaysia); Pandikumar, Alagarsamy; Huang, Nay Ming [Department of Physics, Faculty of Science, University of Malaya, Lembah Pantai, 50603 Kuala Lumpur (Malaysia); Arifin, Zainudin [Department of Chemistry, Faculty of Science, University of Malaya, Lembah Pantai, 50603 Kuala Lumpur (Malaysia); Mazhar, Muhammad, E-mail: mazhar42pk@yahoo.com [Department of Chemistry, Faculty of Science, University of Malaya, Lembah Pantai, 50603 Kuala Lumpur (Malaysia)

    2015-10-15

    A heterobimetallic complex [Cd{sub 2}Ti{sub 4}(μ-O){sub 6}(TFA){sub 8}(THF){sub 6}]·1.5THF (1) (TFA=trifluoroacetato, THF=tetrahydrofuran) comprising of Cd:Ti (1:2) ratio was synthesized by a chemical reaction of cadmium (II) acetate with titanium (IV) isopropoxide and triflouroacetic acid in THF. The stoichiometry of (1) was recognized by single crystal X-ray diffraction, spectroscopic and elemental analyses. Thermal studies revealed that (1) neatly decomposes at 450 °C to furnish 1:1 ratio of cadmium titanate:titania composite oxides material. The thin films of CdTiO{sub 3}–TiO{sub 2} composite oxides were deposited at 550 °C on fluorine doped tin oxide coated conducting glass substrate in air ambient. The micro-structure, crystallinity, phase identification and chemical composition of microspherical architectured CdTiO{sub 3}–TiO{sub 2} composite thin film have been determined by scanning electron microscopy, X-ray diffraction, Raman spectroscopy and energy dispersive X-ray analysis. The scope of composite thin film having band gap of 3.1 eV was explored as photoanode for dye-sensitized solar cell application. - Graphical abstarct: Microspherical designed CdTiO{sub 3}–TiO{sub 2} composite oxides photoanode film has been fabricated from single source precursor [Cd{sub 2}Ti{sub 4}(μ-O){sub 6}(TFA){sub 8}(THF){sub 6}]·1.5THF via aerosol assisted chemical vapor deposition technique for dye sensitized solar cell application. - Highlights: • Synthesis and characterization of a heterobimetallic Cd–Ti complex. • Fabrication of CdTiO{sub 3}–TiO{sub 2} thin film photoelectrode. • Application as dye sensitized photoanode for solar application.

  7. Hydrogenated TiO{sub 2} film for enhancing photovoltaic properties of solar cells and self-sensitized effect

    Energy Technology Data Exchange (ETDEWEB)

    He, Hongcai; Yang, Kui; Wang, Ning, E-mail: ning-wang@uestc.edu.cn; Luo, Feifei; Chen, Haijun [State Key Laboratory of Electronic Thin Films and Integrated Devices and School of Microelectronics and Solid-State Electronics, University of Electronic Science and Technology of China, Chengdu 610054 (China)

    2013-12-07

    Hydrogenated TiO{sub 2} film was obtained by annealing TiO{sub 2} film at 350 °C for 2 h with hydrogen, and TiO{sub 2} films were prepared by screen printing on fluorine-doped tin oxide glass. Structural characterization by X-ray diffraction and electron microscopy did not show obvious difference between hydrogenated TiO{sub 2} film and pristine TiO{sub 2} film. Through optical and electrochemical characterization, the hydrogenated TiO{sub 2} film showed enhanced absorption and narrowed band gap, as well as reduced TiO{sub 2} surface impedance and dark current. As a result, an obviously enhanced photovoltaic effect was observed in the solar cell with hydrogenated TiO{sub 2} as photoanode without adding any dye due to the self-sensitized effect of hydrogenated TiO{sub 2} film, which excited electrons injecting internal conduction band of TiO{sub 2} to generate more photocurrent.

  8. Phase-controlled preparation of TiO{sub 2} films and micro(nano)spheres by low-temperature chemical bath deposition

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Mingsong, E-mail: wangms@mail.ujs.edu.cn [School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013 (China); Li, Qihui; Yu, Haiyan [School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013 (China); Hur, Seung Hyun [Department of Chemical Engineering, University of Ulsan, Ulsan 680-749 (Korea, Republic of); Kim, Eui Jung, E-mail: ejkim@ulsan.ac.kr [Department of Chemical Engineering, University of Ulsan, Ulsan 680-749 (Korea, Republic of)

    2013-11-25

    Highlights: •Simultaneously preparation of TiO{sub 2} films and sphere-like precipitates by low-temperature chemical bath deposition. •The same building blocks observed in the films and precipitates. •Cluster-by-cluster attachment is succeeded by the ion-by-ion growth. •Phase-controlled growth of TiO{sub 2} by the effects of solvent or fluorine ion. -- Abstract: TiO{sub 2} films and micro(nano)spheres have been simultaneously prepared by means of low-temperature chemical bath deposition (CBD). The films and precipitates are found to be constructed of the same building blocks regardless of the bath conditions. Thin nanosheets of ca. 20 nm in thickness serve as the building blocks of rutile TiO{sub 2} grown in an acidic bath. They aggregate to form spheres to reduce the surface energy of the precipitates, while in the films they grow into discrete crystallites on the seeded substrate. Fine control over the crystalline phase of TiO{sub 2} is achieved by replacing some water with ethanol or the addition of NH{sub 4}F. A gradual transition from rutile to anatase is observed as the ethanol and NH{sub 4}F contents are increased. Moreover, the crystallite size of TiO{sub 2} is significantly reduced and there exists monodisperse nanoparticles and aggregate microspheres in the products modified with ethanol and NH{sub 4}F, respectively. This size-dependent phase transition is consistent with previous theoretical and thermodynamic studies. The facile tune of the TiO{sub 2} phase by low-temperature CBD method may be useful to improve the performance of TiO{sub 2} for its various applications.

  9. Temperature dependence of gas sensing behaviour of TiO2 doped PANI composite thin films

    Science.gov (United States)

    Srivastava, Subodh; Sharma, S. S.; Sharma, Preetam; Sharma, Vinay; Rajura, Rajveer Singh; Singh, M.; Vijay, Y. K.

    2014-04-01

    In the present work we have reported the effect of temperature on the gas sensing properties of TiO2 doped PANI composite thin film based chemiresistor type gas sensors for hydrogen gas sensing application. PANI and TiO2 doped PANI composite were synthesized by in situ chemical oxidative polymerization of aniline at low temperature. The electrical properties of these composite thin films were characterized by I-V measurements as function of temperature. The I-V measurement revealed that conductivity of composite thin films increased as the temperature increased. The changes in resistance of the composite thin film sensor were utilized for detection of hydrogen gas. It was observed that at room temperature TiO2 doped PANI composite sensor shows higher response value and showed unstable behavior as the temperature increased. The surface morphology of these composite thin films has also been characterized by scanning electron microscopy (SEM) measurement.

  10. Effect of Sr doping on LaTiO3 thin films

    International Nuclear Information System (INIS)

    Vilquin, B.; Kanki, T.; Yanagida, T.; Tanaka, H.; Kawai, T.

    2005-01-01

    We report on the electric properties of La 1-x Sr x TiO 3 (0 ≤ x ≤ 0.5) thin films fabricated by pulsed laser deposition method. Crystallographic measurement of the thin films showed the epitaxial c-axis perovskite structure. The electric property of LaTiO 3 thin film, which is a typical Mott insulative material in bulk, showed insulative behaviour, while the Sr-doped films showed metallic conduction suffering electron-electron scattering. Below x = 0.1, the major carrier type was identified to be hole, and switched to electron with further increasing Sr-doping above x = 0.15. In fact, the switching from p-type to n-type for La 1-x Sr x TiO 3 thin films is first demonstrated in this study. The transition suggests that effective Coulomb gap vanishes due to over-additional Sr doping

  11. Electrophoretic deposition of nanocrystalline TiO2 films on Ti substrates for use in flexible dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Tan Weiwei; Yin Xiong; Zhou Xiaowen; Zhang Jingbo; Xiao Xurui; Lin Yuan

    2009-01-01

    Nanocrystalline TiO 2 films were prepared on flexible Ti-metal sheets by electrophoretic deposition followed by chemical treatment with tetra-n-butyl titanate (TBT) and sintering at 450 deg. C. X-ray diffraction (XRD) analysis indicates that TBT treatment led to the formation of additional anatase TiO 2 , which plays an important role in improving the interconnection between TiO 2 particles, as well as the adherence of the film to the substrate, and in modifying the surface properties of the nanocrystalline particles. The effect of TBT treatment on the electron transport in the nanocrystalline films was studied by intensity-modulated photocurrent spectroscopy (IMPS). An increase in the conversion efficiency was obtained for the dye-sensitized solar cells with TBT-treated nanocrystalline TiO 2 films. The cell performance was further optimized by designing nanocrystalline TiO 2 films with a double-layer structure composed of a light-scattering layer and a transparent layer. The light-scattering effect of the double-layer nanocrystalline films was evaluated by diffuse reflectance spectra. Employing the double-layer nanocrystalline films as the photoelectrodes resulted in a significant improvement in the incident photo-to-current conversion efficiency of the corresponding cells due to enhanced solar absorption by light scattering. A high conversion efficiency of 6.33% was measured under illumination with 100 mW cm -2 (AM 1.5) simulated sunlight.

  12. The Photocatalytic Activity and Compact Layer Characteristics of TiO2 Films Prepared Using Radio Frequency Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    H. C. Chang

    2014-01-01

    Full Text Available TiO2 compact layers are used in dye-sensitized solar cells (DSSCs to prevent charge recombination between the electrolyte and the transparent conductive substrate (indium tin oxide, ITO; fluorine-doped tin oxide, FTO. Thin TiO2 compact layers are deposited onto ITO/glass by means of radio frequency (rf magnetron sputtering, using deposition parameters that ensure greater photocatalytic activity and increased DSSC conversion efficiency. The photoinduced decomposition of methylene blue (MB and the photoinduced hydrophilicity of the TiO2 thin films are also investigated. The photocatalytic performance characteristics for the deposition of TiO2 films are improved by using the Grey-Taguchi method. The average transmittance in the visible region exceeds 85% for all samples. The XRD patterns of the TiO2 films, for sol-gel with spin coating of porous TiO2/TiO2 compact/ITO/glass, show a good crystalline structure. In contrast, without the TiO2 compact layer (only porous TiO2, the peak intensity of the anatase (101 plane in the XRD patterns for the TiO2 film has a lower value, which demonstrates inferior crystalline quality. With a TiO2 compact layer to prevent charge recombination, a higher short-circuit current density is obtained. The DSSC with the FTO/glass and Pt counter electrode demonstrates the energy conversion efficiency increased.

  13. Influence of substrate temperature and silver-doping on the structural and optical properties of TiO_2 films

    International Nuclear Information System (INIS)

    Fischer, Dieter

    2016-01-01

    Evaporation of titanium together with activated oxygen is used to grow TiO_2 films and simultaneously with silver to grow Ag–TiO_2 films (5 at.% Ag) onto sapphire substrates at three different substrate temperatures: − 190, 30, and 200 °C. The obtained films were characterized by X-ray powder diffraction, Raman, X-ray photoelectron, ultraviolet–visible spectroscopy, and transmission electron microscope investigations. The properties of TiO_2 films varied with the substrate temperature. Amorphous, transparent TiO_2 films were grown at − 190 °C and opaque, polycrystalline films at 200 °C, respectively. Surprisingly, at room temperature black, amorphous TiO_2 films are obtained which transform at 350 °C into a mixture of the anatase and brookite polymorph. In the amorphous state of the TiO_2 films a predefined rutile arrangement is suggested by Raman investigations, and the contraction of the lattice constant c of anatase phases (tetragonal, space group I 4_1/amd) depending on the substrate temperature is experimentally observed. The silver-doped TiO_2 films deposited at − 190 and 30 °C contain Ag-particles with 2 nm in size inside the TiO_2 matrix, which after annealing segregate under increasing particle sizes. The silver-doping stabilizes the anatase polymorph and yields to reduced titanium species in the films especially during deposition at 30 °C. The Ag–TiO_2 films deposited at − 190 °C are transparent up to 350 °C. In the undoped as well as silver-doped TiO_2 films the rutile polymorph is directly formed at 200 °C as main phase. - Highlights: • At room temperature black, amorphous TiO_2 films are obtained. • A predefined rutile arrangement is suggested in amorphous TiO_2 films. • Annealed TiO_2 films crystallize to a mixture of the anatase and brookite polymorph. • In TiO_2 and Ag-doped TiO_2 films the rutile polymorph is directly formed at 200 °C. • Ag-doped TiO_2 films stabilize the anatase polymorph and reduced titanium

  14. Characterization of ultra-thin TiO2 films grown on Mo(112)

    International Nuclear Information System (INIS)

    Kumar, D.; Chen, M.S.; Goodman, D.W.

    2006-01-01

    Ultra-thin TiO 2 films were grown on a Mo(112) substrate by stepwise vapor depositing of Ti onto the sample surface followed by oxidation at 850 K. X-ray photoelectron spectroscopy showed that the Ti 2p peak position shifts from lower to higher binding energy with an increase in the Ti coverage from sub- to multilayer. The Ti 2p peak of a TiO 2 film with more than a monolayer coverage can be resolved into two peaks, one at 458.1 eV corresponding to the first layer, where Ti atoms bind to the substrate Mo atoms through Ti-O-Mo linkages, and a second feature at 458.8 eV corresponding to multilayer TiO 2 where the Ti atoms are connected via Ti-O-Ti linkages. Based on these assignments, the single Ti 2p 3/2 peak at 455.75 eV observed for the Mo(112)-(8 x 2)-TiO x monolayer film can be assigned to Ti 3+ , consistent with our previous results obtained with high-resolution electron energy loss spectroscopy

  15. Cisplatin Loaded Hyaluronic Acid Modified TiO2 Nanoparticles for Neoadjuvant Chemotherapy of Ovarian Cancer

    Directory of Open Access Journals (Sweden)

    Enling Liu

    2015-01-01

    Full Text Available Novel tumor-targeting titanium dioxide (TiO2 nanoparticles modified with hyaluronic acid (HA were developed to explore the feasibility of exploiting the pH-responsive drug release property of TiO2 and the tumor-targeting ability of HA to construct a tumor-targeting cisplatin (CDDP delivery system (HA-TiO2 for potential neoadjuvant chemotherapy of ovarian cancer. The experimental results indicated that CDDP release from the HA-TiO2 nanoparticles was significantly accelerated by decreasing pH from 7.4 to 5.0, which is of particular benefit to cancer therapy. CDDP-loaded HA-TiO2 nanoparticles increased the accumulation of CDDP in A2780 ovarian cancer cells via HA-mediated endocytosis and exhibited superior anticancer activity in vitro. In vivo real-time imaging assay revealed that HA-TiO2 nanoparticles possessed preferable tumor-targeting ability which might potentially minimize the toxic side effects of CDDP in clinical application.

  16. Acetone sensors based on TiO{sub 2} nanocrystals modified with tungsten oxide species

    Energy Technology Data Exchange (ETDEWEB)

    Epifani, Mauro, E-mail: mauro.epifani@le.imm.cnr.it [Consiglio Nazionale delle Ricerche – Istituto per la Microelettronica e Microsistemi (CNR-IMM), via Monteroni c/o Campus Universitario, I-73100, Lecce (Italy); Comini, Elisabetta [SENSOR Lab, Department of Information Engineering, Brescia University and CNR-INO, via Valotti, 9, 25133 Brescia (Italy); Díaz, Raül [Electrochemical Processes Unit, IMDEA Energy Institute, Avda. Ramón de la Sagra, 3 28935 Móstoles (Spain); Genç, Aziz [Metallurgy and Materials Engineering Department, Faculty of Engineering, Bartin University, 74100, Bartin (Turkey); Andreu, Teresa [Catalonia Institute for Energy Research- (IREC), Jardíns de les Dones de Negre, 1, E-08930 Sant Adrià del Besos, Barcelona, CAT (Spain); Siciliano, Pietro [Consiglio Nazionale delle Ricerche – Istituto per la Microelettronica e Microsistemi (CNR-IMM), via Monteroni c/o Campus Universitario, I-73100, Lecce (Italy); Morante, Joan R. [Catalonia Institute for Energy Research- (IREC), Jardíns de les Dones de Negre, 1, E-08930 Sant Adrià del Besos, Barcelona, CAT (Spain); Departament d' Electrònica, Universitat de Barcelona, C./ Martí i Franquès 1, E-08028 Barcelona (Spain)

    2016-04-25

    TiO{sub 2} nanocrystals were prepared by sol–gel/solvothermal processing and modified by the addition of W precursor before the solvothermal step. The W: Ti nominal atomic ratio (R{sub W}) was fixed to 0.16 and 0.64. Surface modification of TiO{sub 2} occurred for R{sub W} = 0.16 while for R{sub W} = 0.64 nanocomposites with WO{sub 3} nanocrystals were obtained after heat-treatment at 500 °C. Pure TiO{sub 2} proved to be very poorly performing in acetone sensing in all the operating conditions. Instead, the addition of both W concentrations largely enhanced the sensor response. It ranged over two orders of magnitude of conductance variation for all the tested concentrations at as low as 200 °C operating temperature. The results showed that it is possible to enhance the performance of an otherwise almost inactive oxide like TiO{sub 2} by proper combination with another more active oxide like WO{sub 3}. - Highlights: • Sensing architecture are synthesized, combining WO{sub 3} and of TiO{sub 2} nanocrystals. • Surface layers of W oxides or heterojunctions of TiO{sub 2} and WO{sub 3} are obtained. • Simple TiO{sub 2} surface modification by W oxides boosts the TiO{sub 2} acetone response. • High responses even at 200 °C show catalytic effect of WO{sub 3} addition.

  17. Photoconductivity studies on amorphous and crystalline TiO{sub 2} films doped with gold nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Valverde-Aguilar, G.; Garcia-Macedo, J.A. [Universidad Nacional Autonoma de Mexico, Departamento de Estado Solido, Instituto de Fisica, Mexico D.F. (Mexico); Renteria-Tapia, V. [Universidad de Guadalajara, Centro Universitario de los Valles, Departamento de Ciencias Naturales y Exactas, Ameca, Jalisco (Mexico); Aguilar-Franco, M. [Universidad Nacional Autonoma de Mexico, Departamento de Fisica Quimica, Instituto de Fisica, Mexico D.F. (Mexico)

    2011-06-15

    In this work, amorphous and crystalline TiO{sub 2} films were synthesized by the sol-gel process at room temperature. The TiO{sub 2} films were doped with gold nanoparticles. The films were spin-coated on glass wafers. The crystalline samples were annealed at 100 C for 30 minutes and sintered at 520 C for 2 h. All films were characterized using X-ray diffraction, transmission electronic microscopy and UV-Vis absorption spectroscopy. Two crystalline phases, anatase and rutile, were formed in the matrix TiO{sub 2} and TiO{sub 2}/Au. An absorption peak was located at 570 nm (amorphous) and 645 nm (anatase). Photoconductivity studies were performed on these films. The experimental data were fitted with straight lines at darkness and under illumination at 515 nm and 645 nm. This indicates an ohmic behavior. Crystalline TiO{sub 2}/Au films are more photoconductive than the amorphous ones. (orig.)

  18. Rutile TiO2 thin films grown by reactive high power impulse magnetron sputtering

    International Nuclear Information System (INIS)

    Agnarsson, B.; Magnus, F.; Tryggvason, T.K.; Ingason, A.S.; Leosson, K.; Olafsson, S.; Gudmundsson, J.T.

    2013-01-01

    Thin TiO 2 films were grown on Si(001) substrates by reactive dc magnetron sputtering (dcMS) and high power impulse magnetron sputtering (HiPIMS) at temperatures ranging from 300 to 700 °C. Optical and structural properties of films were compared both before and after post-annealing using scanning electron microscopy, low angle X-ray reflection (XRR), grazing incidence X-ray diffractometry and spectroscopic ellipsometry. Both dcMS- and HiPIMS-grown films reveal polycrystalline rutile TiO 2 , even prior to post-annealing. The HiPIMS-grown films exhibit significantly larger grains compared to that of dcMC-grown films, approaching 100% of the film thickness for films grown at 700 °C. In addition, the XRR surface roughness of HiPIMS-grown films was significantly lower than that of dcMS-grown films over the whole temperature range 300–700 °C. Dispersion curves could only be obtained for the HiPIMS-grown films, which were shown to have a refractive index in the range of 2.7–2.85 at 500 nm. The results show that thin, rutile TiO 2 films, with high refractive index, can be obtained by HiPIMS at relatively low growth temperatures, without post-annealing. Furthermore, these films are smoother and show better optical characteristics than their dcMS-grown counterparts. - Highlights: • We demonstrate growth of rutile TiO 2 on Si (111) by high power impulse magnetron sputtering. • The films exhibit significantly larger grains than dc magnetron sputtered filmsTiO 2 films with high refractive index are obtained without post-growth annealing

  19. Correlation of Photocatalysis and Photoluminescence Effect in Relation to the Surface Properties of TiO2:Tb Thin Films

    Directory of Open Access Journals (Sweden)

    Damian Wojcieszak

    2013-01-01

    Full Text Available In this paper structural, optical, photoluminescence, and photocatalytic properties of TiO2 and TiO2:(2.6 at. % Tb thin films have been compared. Thin films were prepared by high-energy reactive magnetron sputtering process, which enables obtaining highly nanocrystalline rutile structure of deposited films. Crystallites sizes were 8.7 nm and 6.6 nm for TiO2 and TiO2:Tb, respectively. Surface of prepared thin films was homogenous with small roughness of ca. 7.2 and 2.1 nm in case of TiO2 and TiO2:Tb samples, respectively. Optical properties measurements have shown that the incorporation of Tb into TiO2 matrix has not changed significantly the thin films transparency. It also enables obtaining photoluminescence effect in wide range from 350 to 800 nm, what is unique phenomenon in case of TiO2 with rutile structure. Moreover, it has been found that the incorporation of 2.6 at. % of Tb has increased the photocatalytic activity more than two times as compared to undoped TiO2. Additionally, for the first time in the current state of the art, the relationship between photoluminescence effect, photocatalytic activity, and surface properties of TiO2:Tb thin films has been theoretically explained.

  20. Atomic force microscopy study of TiO2 sol-gel films thermally treated under NH3 atmosphere

    International Nuclear Information System (INIS)

    Trapalis, C.; Todorova, N.; Anastasescu, M.; Anastasescu, C.; Stoica, M.; Gartner, M.; Zaharescu, M.; Stoica, T.

    2009-01-01

    Multilayered TiO 2 films were obtained by sol-gel and dipping deposition on quartz substrate followed by thermal treatment under NH 3 atmosphere. In an attempt to understand the close relationship between microstructural characteristics and the synthesis parameters, a systematic research of the structure and the morphology of NH 3 modified TiO 2 sol-gel films by XRD and Atomic Force Microscopy is reported. The surface morphology has been evaluated in terms of grains size, fractal dimension and surface roughness. For each surface, it was found a self-similar behavior (with mean fractal dimension in the range of 2.67-3.00) related to an optimum morphology favorable to maintain a nano-size distribution of the grains. The root mean square (RMS) roughness of the samples was found to be in the range of 0.72-6.02 nm.

  1. Study of band gap reduction of TiO{sub 2} thin films with variation in GO contents and use of TiO{sub 2}/Graphene composite in hybrid solar cell

    Energy Technology Data Exchange (ETDEWEB)

    Saleem, Hareema, E-mail: hareemasaleem@gmail.com; Habib, Amir

    2016-09-15

    We have successfully designed a hybrid solar cell for improved performance of the P3HT based photovoltaic devices by using TiO{sub 2}/Graphene composites. There has been significant improvement in IV characteristics of organic solar cells prepared by this method. The TiO{sub 2}/Graphene composites act as electron collectors in active layer along with P3HT: PCBM in inverted organic photovoltaic devices. The energy bandgap was prominently reduced from 3.00 eV to 2.71 eV as confirmed by cyclic voltametery (CV) and UV–Vis spectroscopy. We have separately synthesized the TiO{sub 2} nanoparticles of size range (15 nm–22 nm) through condensed refluxed sol gel method in which titanium isopropoxide was taken as precursor. Modified Hummer's Method was used for the oxidation of graphite flakes into graphene oxide (GO) using KMnO{sub 4} as an oxidizing agent. TiO{sub 2}/Graphene composites were prepared by the subsequent sonication and heating processes. We have rigorously characterized the sample through various characterization tools. Scanning electron microscopy (SEM) results of TiO{sub 2}/Graphene films reveal the homogenous distribution of graphene nanosheets among the homogenously distributed titanium nanoparticles. X-ray diffraction (XRD) has shown the pure anatase phase peaks of TiO{sub 2} nanoparticles and oxidation of graphite at 11.8°. Fourier transform infrared spectroscopy (FTIR) has been used to study the vibrating modes. The chemical bonding Ti−O−C resulted to enhance the electron transport in obtained TiO{sub 2}/Graphene composite films. UV–Vis spectroscopy has expressed the oxidation peaks of graphite around 216 nm and all composite films were observed in visible region. The significant reduction in band gap and improved performance of hybrid solar cell using TiO{sub 2}/Graphene composite as electron collector in active layer, is attributed to getting better economical power conversion efficiency solar cell. - Highlights: • Reduction of

  2. Enhanced Magnetization of Cobalt Defect Clusters Embedded in TiO2-δ Films.

    Science.gov (United States)

    Cortie, David L; Khaydukov, Yury; Keller, Thomas; Sprouster, David J; Hughes, Jacob S; Sullivan, James P; Wang, Xiaolin L; Le Brun, Anton P; Bertinshaw, Joel; Callori, Sara J; Aughterson, Robert; James, Michael; Evans, Peter J; Triani, Gerry; Klose, Frank

    2017-03-15

    High magnetizations are desirable for spintronic devices that operate by manipulating electronic states using built-in magnetic fields. However, the magnetic moment in promising dilute magnetic oxide nanocomposites is very low, typically corresponding to only fractions of a Bohr magneton for each dopant atom. In this study, we report a large magnetization formed by ion implantation of Co into amorphous TiO 2-δ films, producing an inhomogeneous magnetic moment, with certain regions producing over 2.5 μ B per Co, depending on the local dopant concentration. Polarized neutron reflectometry was used to depth-profile the magnetization in the Co:TiO 2-δ nanocomposites, thus confirming the pivotal role of the cobalt dopant profile inside the titania layer. X-ray photoemission spectra demonstrate the dominant electronic state of the implanted species is Co 0 , with a minor fraction of Co 2+ . The detected magnetizations have seldom been reported before and lie near the upper limit set by Hund's rules for Co 0 , which is unusual because the transition metal's magnetic moment is usually reduced in a symmetric 3D crystal-field environment. Low-energy positron annihilation lifetime spectroscopy indicates that defect structures within the titania layer are strongly modified by the implanted Co. We propose that a clustering motif is promoted by the affinity of the positively charged implanted species to occupy microvoids native to the amorphous host. This provides a seed for subsequent doping and nucleation of nanoclusters within an unusual local environment.

  3. Synthesis and characterization of Ag doped TiO{sub 2} heterojunction films and their photocatalytic performances

    Energy Technology Data Exchange (ETDEWEB)

    Demirci, Selim, E-mail: selim.demirci@marmara.edu.tr [Marmara University, Department of Metallurgical and Materials Engineering, Kadiköy, 34722 Istanbul (Turkey); Dikici, Tuncay [Izmir Katip Celebi University, Department of Materials Science and Engineering, Cigli, 35620 Izmir (Turkey); Yurddaskal, Metin [Department of Metallurgical and Materials Engineering, Dokuz Eylul University, 35390 Izmir (Turkey); Center for Fabrication and Application of Electronic Materials, Dokuz Eylul University, 35390 Izmir (Turkey); Gultekin, Serdar [Department of Nanoscience and Nanoengineering, Dokuz Eylul University, 35390 İzmir (Turkey); Experimental Science Applications and Research Center, Celal Bayar University, 45140 Manisa (Turkey); Toparli, Mustafa; Celik, Erdal [Department of Metallurgical and Materials Engineering, Dokuz Eylul University, 35390 Izmir (Turkey); Department of Nanoscience and Nanoengineering, Dokuz Eylul University, 35390 İzmir (Turkey); Center for Fabrication and Application of Electronic Materials, Dokuz Eylul University, 35390 Izmir (Turkey)

    2016-12-30

    Highlights: • Ag doped TiO{sub 2} films were successfully synthesized by sol–gel spin coating method. • Ag in TiO{sub 2} lattice enters in intermediate states to decrease TiO{sub 2} bandgap energy. • Ag dopants increase the photoactivity and superhydrophilicity. • The degradation kinetics of methylene blue was studied. • The 0.7 mol% of Ag was found to be the optimum concentration. - Abstract: In this study, undoped and silver (Ag) doped titanium dioxide (TiO{sub 2}) films were successfully synthesized by sol-gel spin coating technique on the Si substrates. Photocatalytic activities of the TiO{sub 2} films with different Ag content were investigated for the degradation of methylene blue (MB) under UV light irradiation. The crystal phase structure, surface morphology, chemical and optical properties of Ag-doped TiO{sub 2} films were characterized using an X-ray diffractometer (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), UV–vis spectrophotometer, and FTIR spectrophotometer. The results showed that the Ag-doped TiO{sub 2} films calcined at 500 °C had the crystalline anatase phases and the surface morphologies with some cracks. Ag substitution into TiO{sub 2} matrix enhanced the photocatalytic activity of TiO{sub 2} films under UV light irradiation as compared to the undoped TiO{sub 2} film. Furthermore, the results indicated that the 0.7% Ag doped TiO{sub 2} film exhibited a superior photocatalytic activity than that of undoped and other Ag-doped TiO{sub 2} films. This study demonstrated the potential of an application of Ag doped films to efficiently treat dissolved organic contaminants in water.

  4. Synthesis and characterization of anatase-TiO2 thin films

    International Nuclear Information System (INIS)

    Sankapal, B.R.; Lux-Steiner, M.Ch.; Ennaoui, A.

    2005-01-01

    A new and effective method for the preparation of nanocrystalline TiO 2 (anatase) thin films is presented. This method is based on the use of peroxo-titanium complex as a single precursor. Post-annealing treatment is necessary to convert the deposited amorphous film into TiO 2 (anatase) phase. The films obtained are uniform, compact and free of pinholes. A wide range of techniques are used for characterization, namely X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), transmission electron microscopy (TEM), energy-dispersive X-ray analysis (EDAX) and UV-Vis-NIR spectrophotometer. Glass, indium-doped tin oxide (ITO) and quartz are used as substrates. TiO 2 (anatase) phase with (1 0 1) preferred orientation is obtained for the films. Byproduct (collected powder) consists of the same crystal structure. The optical measurement reveals the indirect bandgap of 3.2 eV

  5. Synthesis and characterization of anatase-TiO 2 thin films

    Science.gov (United States)

    Sankapal, B. R.; Lux-Steiner, M. Ch.; Ennaoui, A.

    2005-01-01

    A new and effective method for the preparation of nanocrystalline TiO 2 (anatase) thin films is presented. This method is based on the use of peroxo-titanium complex as a single precursor. Post-annealing treatment is necessary to convert the deposited amorphous film into TiO 2 (anatase) phase. The films obtained are uniform, compact and free of pinholes. A wide range of techniques are used for characterization, namely X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), transmission electron microscopy (TEM), energy-dispersive X-ray analysis (EDAX) and UV-Vis-NIR spectrophotometer. Glass, indium-doped tin oxide (ITO) and quartz are used as substrates. TiO 2 (anatase) phase with (1 0 1) preferred orientation is obtained for the films. Byproduct (collected powder) consists of the same crystal structure. The optical measurement reveals the indirect bandgap of 3.2 eV.

  6. Synthesis and characterization of anatase-TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Sankapal, B.R.; Lux-Steiner, M.Ch.; Ennaoui, A

    2005-01-15

    A new and effective method for the preparation of nanocrystalline TiO{sub 2} (anatase) thin films is presented. This method is based on the use of peroxo-titanium complex as a single precursor. Post-annealing treatment is necessary to convert the deposited amorphous film into TiO{sub 2} (anatase) phase. The films obtained are uniform, compact and free of pinholes. A wide range of techniques are used for characterization, namely X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), transmission electron microscopy (TEM), energy-dispersive X-ray analysis (EDAX) and UV-Vis-NIR spectrophotometer. Glass, indium-doped tin oxide (ITO) and quartz are used as substrates. TiO{sub 2} (anatase) phase with (1 0 1) preferred orientation is obtained for the films. Byproduct (collected powder) consists of the same crystal structure. The optical measurement reveals the indirect bandgap of 3.2 eV.

  7. Magnetism in spin-coated pristine TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Hassini, Awatef [IUT de Blois, 3 place Jean Jaures, C.S. 2903, 41029 Blois (France); Sakai, Joe [Laboratoire LEMA, UMR 6157 CNRS/CEA, Universite Francois Rabelais, Parc de Grandmont, 37200 Tours (France); Lopez, Josep Santiso [Institut de Ciencia de Materials de Barcelona, CSIC, Campus UAB, Bellaterra 08193 (Spain); Nguyen Hoa Hong [Laboratoire LEMA, UMR 6157 CNRS/CEA, Universite Francois Rabelais, Parc de Grandmont, 37200 Tours (France)], E-mail: nguyen.hoahong@univ-tours.fr

    2008-04-28

    Spin coated pristine TiO{sub 2} thin films show magnetic behaviors that are similar to those of pulsed laser ablated TiO{sub 2} thin films that were reported previously. It seems that in this kind of material, ferromagnetism (FM) is indeed intrinsic, and it can be achieved by various deposition techniques. The fact that oxygen annealing degrades the magnetic moment implies that the observed magnetism is likely due to defects or/and oxygen vacancies. Moreover, thick films that were deposited under the same growth conditions have the magnetic ordering degraded enormously. It is found that as for FM in undoped TiO{sub 2} films made by the chemical solution deposition, not only do defects/oxygen vacancies play a role, but also the confinement effects seem to be important.

  8. Raman spectra of TiO2 thin films deposited electrochemically and by spray pyrolysis

    International Nuclear Information System (INIS)

    Shishiyanu, S.; Vartic, V.; Shishiyanu, T.; Stratan, Gh.; Rusu, E.; Zarrelli, M.; Giordano, M.

    2013-01-01

    In this paper we present our experimental results concerning the fabrication of TiO 2 thin films by spray pyrolysis and electrochemical deposition method onto different substrates - Corning glass, Si and optical fibers. The surface morphology of the TiO 2 thin films have been investigated by Atomic Force Microscopy. Raman shift spectra measurements have been done for the optical characterization of the fabricated titania thin films. The post-growth rapid photothermal processing (RPP) at temperatures of 100-800 degrees Celsius for 1-3 min have been applied. Our experimental results prove that by the application of post-growth RPP is possible to essentially improve the crystallinity of the deposited TiO 2 films. (authors)

  9. Preparation of anatase TiO{sub 2} thin films by vacuum arc plasma evaporation

    Energy Technology Data Exchange (ETDEWEB)

    Miyata, Toshihiro [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan)]. E-mail: tmiyata@neptune.kanazawa-it.ac.jp; Tsukada, Satoshi [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan); Minami, Tadatsugu [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan)

    2006-02-01

    Anatase titanium dioxide (TiO{sub 2}) thin films with high photocatalytic activity have been prepared with deposition rates as high as 16 nm/min by a newly developed vacuum arc plasma evaporation (VAPE) method using sintered TiO{sub 2} pellets as the source material. Highly transparent TiO{sub 2} thin films prepared at substrate temperatures from room temperature to 400 deg. C exhibited photocatalytic activity, regardless whether oxygen (O{sub 2}) gas was introduced during the VAPE deposition. The highest photocatalytic activity and photo-induced hydrophilicity were obtained in anatase TiO{sub 2} thin films prepared at 300 deg. C, which correlated to the best crystallinity of the films, as evidenced from X-ray diffraction. In addition, a transparent and conductive anatase TiO{sub 2} thin film with a resistivity of 2.6 x 10{sup -1} {omega} cm was prepared at a substrate temperature of 400 deg. C without the introduction of O{sub 2} gas.

  10. The TiO2 Refraction Film for CsI Scintillator

    OpenAIRE

    C. C. Chen; C. W. Hun; C. J. Wang; C. Y. Chen; J. S. Lin; K. J. Huang

    2015-01-01

    Cesium iodide (CsI) melt was injected into anodic aluminum oxide (AAO) template and was solidified to CsI column. The controllable AAO channel size (10~500 nm) can makes CsI column size from 10 to 500 nm in diameter. In order to have a shorter light irradiate from each singe CsI column top to bottom the AAO template was coated a TiO2 nano-film. The TiO2 film acts a refraction film and makes X-ray has a shorter irradiation path in the CsI crystal making a stronger the photo-electron signal. Wh...

  11. Measurement of the extinction of sputtered TiO/sub 2/ films

    Energy Technology Data Exchange (ETDEWEB)

    Welsch, E; Lieder, G; Walther, H G; Hacker, E

    1982-05-28

    In this paper a method for separate measurement of the extinction of optical thin films is presented. The method combines a laser calorimetric technique and a light-scattering goniophotometer. As an example, the spectral extinction properties of r.f. reactively sputtered TiO/sub 2/ films were measured. Under certain conditions absorption indices of 10/sup -5/ or less can be achieved. Thus light scattering, rather than absorption, is the dominant optical loss mechanism in sputtered TiO/sub 2/ films.

  12. Preparation of Sb2S3 nanocrystals modified TiO2 dendritic structure with nanotubes for hybrid solar cell

    Science.gov (United States)

    Li, Yingpin; Wei, Yanan; Feng, Kangning; Hao, Yanzhong; Pei, Juan; Sun, Bao

    2018-06-01

    Array of TiO2 dendritic structure with nanotubes was constructed on transparent conductive fluorine-doped tin oxide glass (FTO) with titanium potassium oxalate as titanium source. Sb2S3 nanocrystals were successfully deposited on the TiO2 substrate via spin-coating method. Furthermore, TiO2/Sb2S3/P3HT/PEDOT:PSS composite film was prepared by successively spin-coating P3HT and PEDOT:PSS on TiO2/Sb2S3. It was demonstrated that the modification of TiO2 dendritic structure with Sb2S3 could enhance the light absorption in the visible region. The champion hybrid solar cell assembled by TiO2/Sb2S3/P3HT/PEDOT:PSS composite film achieved a power conversion efficiency (PCE) of 1.56%.

  13. Spray pyrolysed Ru:TiO2 thin film electrodes prepared for electrochemical supercapacitor

    Science.gov (United States)

    Fugare, B. Y.; Thakur, A. V.; Kore, R. M.; Lokhande, B. J.

    2018-04-01

    Ru doped TiO2 thin films are prepared by using 0.06 M aqueous solution of potassium titanium oxalate (pto), and 0.005 M aqueous solution of ruthenium tri chloride (RuCl3) precursors. The deposition was carried on stainless steel (SS) by using well known ultrasonic spray pyrolysis technique (USPT) at 723° K by maintaining the spray rate 12 cc/min and compressed air flow rate 10 Lmin-1. Prepared Ru:TiO2 thin films were characterized by structurally, morphologically and electrochemically. Deposited RuO2 shows amorphous structure and TiO2 shows tetragonal crystal structure with rutile as prominent phase at very low decomposition temperature. SEM micrographs of RuO2 exhibits porous, interconnected, spherical grains type morphology and TiO2 shows porous, nanorods and nanoplates like morphology and also Ru doped TiO2 shows porous, spherical, granular and nanorods type morphology. The electrochemical cyclic voltammetery shows mixed capacitive behavior. The achieved highest value of specific capacitance 2692 F/g was Ru doped TiO2 electrode in 0.5 M H2SO4.

  14. Methylene blue photocatalytic mineralization under visible irradiation on TiO{sub 2} thin films doped with chromium

    Energy Technology Data Exchange (ETDEWEB)

    Diaz-Uribe, Carlos; Vallejo, William, E-mail: williamvallejo@mail.uniatlantico.edu.co; Ramos, Wilkendry

    2014-11-15

    Graphical abstract: - Highlights: • We used an easy and inexpensive technique to dope thin films of TiO{sub 2}. • We proved that hydroxyl radicals were generated under visible light irradiation by Cr:TiO{sub 2}. • We used a Haber–Weiss reaction through Cr:TiO{sub 2} catalyst to improve the photo-mineralization process. - Abstract: We studied changes in structural, optical and photocatalytic properties of TiO{sub 2} thin films due to doping process with chromium. Powders of undoped TiO{sub 2} and chromium-doped TiO{sub 2} (Cr:TiO{sub 2}) were synthesized by sol–gel method and, thin films were deposited by doctor blade method. The properties of the thin films were studied by X-ray diffraction (XRD), infrared spectroscopy (IR) and diffuse reflectance. The XRD patterns indicated that doping process changed the crystalline phases radio of TiO{sub 2} thin films, furthermore, the optical analysis showed that band gap value of Cr:TiO{sub 2} thin films was 31% fewer than undoped TiO{sub 2} thin films. Along, Langmuir–Hinshelwood model was used to obtain kinetic information of the photo-mineralization process; results indicated that photocatalytic activity of Cr:TiO{sub 2} thin films were four times better than undoped TiO{sub 2} thin films; finally the synergic effect was tested by addition of the H{sub 2}O{sub 2}, photocatalytic yield was improved from 26% to 61% when methylene blue photo-mineralization was assisted with slightly amount of H{sub 2}O{sub 2}.

  15. Photoelectrochemical Performances and Potential Applications of TiO2 Nanotube Arrays Modified with Ag and Pt Nanoparticles

    International Nuclear Information System (INIS)

    Xu, Guangqing; Liu, Haipeng; Wang, Jinwen; Lv, Jun; Zheng, Zhixiang; Wu, Yucheng

    2014-01-01

    TiO 2 nanotube arrays (NTAs) modified with Ag (Ag/TiO 2 ) and Pt (Pt/TiO 2 ) nanoparticles were fabricated by anodic oxidation combined with photoreduction and hydrothermal methods, respectively. Structures, element components and morphologies of TiO 2 , Ag/TiO 2 and Pt/TiO 2 NTAs were measured by X-ray diffraction diffractometer, X-ray photoelectron spectroscopy, scanning electron microscope and transmission electron microscope. The photoeletrochemical performances of TiO 2 , Pt/TiO 2 and Ag/TiO 2 NTAs were characterized by cyclic voltammetry and amperometry in phosphate buffer solution in absence and presence of glucose. Modifications of Ag and Pt nanoparticles play different roles in the photoelectrochemical process and have different potential applications. Ag nanoparticles decrease the photocurrent in buffer solution but increase the photocurrent response to organic compounds, which is fit for electrochemical detection of organic compounds due to the low background photocurrent and high photocurrent response. Ag/TiO 2 NTAs achieve the best detection performance with sensitivity of 0.152 μA/μM and detection limit of 0.53 μM. On the contrary, Pt nanoparticles can enhance the photocurrent of TiO 2 NTAs in buffer solution but decrease the photocurrent response to organic compounds, which are benefit for photocatalytic water splitting but not for photoelectrochemical detection

  16. Investigations of structural, morphological and optical properties of Cu:ZnO/TiO2/ZnO and Cu:TiO2/ZnO/TiO2 thin films prepared by spray pyrolysis technique

    Directory of Open Access Journals (Sweden)

    M.I. Khan

    Full Text Available The aim of this research work is presented a comparison study of Cu:ZnO/TiO2/ZnO (Cu:ZTZ and Cu:TiO2/ZnO/TiO2 (Cu:TZT thin films deposited by spray pyrolysis technique on FTO substrates. After deposition, these films are annealed at 500 °C. XRD confirms the anatase phase of TiO2 and Hexagonal wurtzite phase of ZnO. SEM shows that Cu:TZT has more porous surface than Cu:ZTZ and also the root mean square (RMS roughness of Cu:TZT film is 48.96 and Cu:ZTZ film is 32.69. The calculated optical band gaps of Cu:TZT and Cu:ZTZ thin films are 2.65 eV and 2.6 eV respectively, measured by UV–Vis spectrophotometer. This work provides an environment friendly and low cost use of an abundant material for highly efficient dye sensitized solar cells (DSSCs. Keywords: Multilayer films, ZnO, TiO2, Cu

  17. Modification of physicochemical and thermal properties of starch films by incorporation of TiO2 nanoparticles.

    Science.gov (United States)

    Oleyaei, Seyed Amir; Zahedi, Younes; Ghanbarzadeh, Babak; Moayedi, Ali Akbar

    2016-08-01

    In this research, potato starch and TiO2 nanoparticles (0.5, 1 and 2wt%) films were developed. Influences of different concentrations of TiO2 on the functional properties of nanocomposite films (water-related properties, mechanical characteristics, and UV transmittance) were investigated. XRD, FTIR, and DSC analyses were used to characterize the morphology and thermal properties of the films. The results revealed that TiO2 nanoparticles dramatically decreased the values of water-related properties (water vapor permeability: 11-34%; water solubility: 1.88-9.26%; moisture uptake: 2.15-11.18%). Incorporation of TiO2 led to a slight increment of contact angle and tensile strength, and a decrease in elongation at break of the films. TiO2 successfully blocked more than 90% of UV light, while opacity and white index of the films were enhanced. Glass transition temperature and melting point of the films were positively affected by the addition of TiO2 nanoparticles. The result of XRD study exhibited that due to a limited agglomeration of TiO2 nanoparticles, the mean crystal size of TiO2 increased. Formation of new hydrogen bonds between the hydroxyl groups of starch and nanoparticles was confirmed by FTIR spectroscopy. In conclusion, TiO2 nanoparticles improved the functional properties of potato starch film and extended the potential for food packaging applications. Copyright © 2016 Elsevier B.V. All rights reserved.

  18. Sn4+-Doped TiO2 Nanorod Array Film with Enhanced Visible Light ...

    Indian Academy of Sciences (India)

    61

    specific surface area of flat film than nano-powder would lead to the decrease of its .... doped TiO2 NAFs were acquired with EDS spectrometer fitted on the microscopy. ... The morphologies of films were obtained by the SEM measurement.

  19. Preparation and antibacterial activity of Ag–TiO2 composite film by ...

    Indian Academy of Sciences (India)

    WINTEC

    The stability of the Ag–TiO2 films was tested in a weather chamber (Atlas ... test. The antibacterial activity of the film after weathering was then compared to the one before weathering. 3. Results .... form the electron-cavity, the cavities oxidize the OH. – and ... in pharmaceutical and medical device factories, where the bacteria ...

  20. Preparation and Properties of Nano Dy/TiO2 Films Supported on High Silica Fiber

    Directory of Open Access Journals (Sweden)

    HUANG Feng-ping

    2017-07-01

    Full Text Available In order to improve the photocatalytic degradation performance and stability of nano TiO2, Dy doped TiO2 supported on high silica glass fiber was prepared by microwave-sol method combined with dip-coating method. The samples were analyzed by XRD,SEM,PL,EDS,XPS and other equipments for phase composition of films,surface topography, surface elements and the stability of films. And the effects of pretreatment solution and coating method on the high-silica fiber film were investigated.In addition, the photocatalytic performance of the sample has been investigated by degrading methylene blue. The results show that the catalytic stability of Dy doping TiO2 nanofilms supported on high silica glass fiber can be improved and the degradation of methyl orange can reach 94% in 30min after 5 times of coating treatment.

  1. Magnetic and structural study of Cu-doped TiO2 thin films

    International Nuclear Information System (INIS)

    Torres, C.E. Rodriguez; Golmar, F.; Cabrera, A.F.; Errico, L.; Navarro, A.M. Mudarra; Renteria, M.; Sanchez, F.H.; Duhalde, S.

    2007-01-01

    Transparent pure and Cu-doped (2.5, 5 and 10 at.%) anatase TiO 2 thin films were grown by pulsed laser deposition technique on LaAlO 3 substrates. The samples were structurally characterized by X-ray absorption spectroscopy and X-ray diffraction. The magnetic properties were measured using a SQUID. All films have a FM-like behaviour. In the case of the Cu-doped samples, the magnetic cycles are almost independent of the Cu concentration. Cu atoms are forming CuO and/or substituting Ti in TiO 2 . The thermal treatment in air promotes the CuO segregation. Since CuO is antiferromagnetic, the magnetic signals present in the films could be assigned to Cu substitutionally replacing cations in TiO 2

  2. Magnetic and structural study of Cu-doped TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Torres, C.E. Rodriguez [Dpto de Fisica-IFLP, Fac. Cs. Exactas, Universidad Nacional de La Plata-CONICET, CC 67, 1900 La Plata (Argentina)], E-mail: torres@fisica.unlp.edu.ar; Golmar, F. [Laboratorio de Ablacion Laser, Facultad de Ingenieria, Universidad de Buenos Aires, Paseo Colon 850, 1063 Buenos Aires (Argentina); Cabrera, A.F.; Errico, L.; Navarro, A.M. Mudarra; Renteria, M.; Sanchez, F.H. [Dpto de Fisica-IFLP, Fac. Cs. Exactas, Universidad Nacional de La Plata-CONICET, CC 67, 1900 La Plata (Argentina); Duhalde, S. [Laboratorio de Ablacion Laser, Facultad de Ingenieria, Universidad de Buenos Aires, Paseo Colon 850, 1063 Buenos Aires (Argentina)

    2007-10-31

    Transparent pure and Cu-doped (2.5, 5 and 10 at.%) anatase TiO{sub 2} thin films were grown by pulsed laser deposition technique on LaAlO{sub 3} substrates. The samples were structurally characterized by X-ray absorption spectroscopy and X-ray diffraction. The magnetic properties were measured using a SQUID. All films have a FM-like behaviour. In the case of the Cu-doped samples, the magnetic cycles are almost independent of the Cu concentration. Cu atoms are forming CuO and/or substituting Ti in TiO{sub 2}. The thermal treatment in air promotes the CuO segregation. Since CuO is antiferromagnetic, the magnetic signals present in the films could be assigned to Cu substitutionally replacing cations in TiO{sub 2}.

  3. Physics properties of TiO_2 films produced by dip-coating technique

    International Nuclear Information System (INIS)

    Teloeken, A.C.; Alves, A.K.; Berutti, F.A.; Tabarelli, A.; Bergmann, C.P.

    2014-01-01

    The use of titanium dioxide (TiO_2) as a photocatalyst to produce hydrogen has been of great interest because of their chemical stability, low cost and non-toxicity. TiO_2 occurs in three different crystal forms: rutile, anatase and brokita. Among these, the anatase phase generally exhibits the best photocatalytic behavior, while the rutile phase is the most stable. Among the various techniques of deposition, dip-coating technique produces films with good photocatalytic properties, using simple and inexpensive equipment. In this work TiO_2 films were obtained by dip-coating. The films were characterized using X-ray diffraction, scanning electron microscopy, profilometry, contact angle measurements and photocurrent. The microstructure and physical properties were evaluated in relation of the temperature and the addition of an additive. (author)

  4. Structural transformations of TiO{sub 2} films with deposition temperature and electrical properties of nanostructure n-TiO{sub 2}/p-Si heterojunction diode

    Energy Technology Data Exchange (ETDEWEB)

    Aksoy, Seval; Caglar, Yasemin, E-mail: yasemincaglar@anadolu.edu.tr

    2014-11-15

    Highlights: • Titanium oxide (TiO{sub 2}) films have been deposited on p-Si substrates by sol gel spin coating technique. • The effect of deposition temperatures on structural and morphological properties of TiO{sub 2} films. • The electrical parameters of nanostructure n-TiO{sub 2}/p-Si heterojunction diode such as n, R{sub s} and ϕ{sub b} were investigated. - Abstract: Titanium oxide (TiO{sub 2}) films have been deposited on p-Si substrates by sol–gel method using spin coating technique. Structural and morphological properties were studied as a function of deposition temperatures by X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). The deposition temperatures were chosen from 700 °C to 1100 °C. Crystallization of the anatase phase and its transformation to the rutile phase were observed at 700 °C and 800 °C, respectively. The fabrication of nanostructure n-TiO{sub 2}/p-Si heterojunction diode was formed by using T7 film deposited at 700 °C. The electrical parameters such as barrier height (ϕ{sub b}) and ideality factor (n) of nanostructure n-TiO{sub 2}/p-Si heterojunction diode were investigated by using I–V measurements and observed to be 0.58 eV and 5.39, respectively. Also, the values of ϕ{sub b} and series resistance (R{sub s}) were determined by using Cheung’s and Norde methods. From the I–V measurements taken at room temperature, the space charge limited (SCLC) mechanism was determined at the low voltage region. The obtained results showed that n-TiO{sub 2}/p-Si heterojunction diode is a good candidate for the applications of semiconductor electronic devices.

  5. Modifying TiO{sub 2} surface architecture by oxygen plasma to increase dye sensitized solar cell efficiency

    Energy Technology Data Exchange (ETDEWEB)

    Rajmohan, Gayathri Devi [Institute for Frontier Materials, Deakin University, Geelong Waurn Ponds, Victoria 3216 (Australia); Dai, Xiujuan J., E-mail: jane.dai@deakin.edu.au [Institute for Frontier Materials, Deakin University, Geelong Waurn Ponds, Victoria 3216 (Australia); Tsuzuki, Takuya; Lamb, Peter R. [Institute for Frontier Materials, Deakin University, Geelong Waurn Ponds, Victoria 3216 (Australia); Plessis, Johan du [School of Applied Sciences, RMIT University, GPO Box 2476 V, Melbourne, Victoria 3001 (Australia); Huang, Fuzhi; Cheng, Yi-Bing [Department of Materials Engineering, Monash University, Melbourne, Victoria 3800 (Australia)

    2013-10-31

    Oxygen plasma treatment of TiO{sub 2} films has been used to improve the efficiency of dye sensitized solar cells. Both a commercial TiO{sub 2} sample and a TiO{sub 2} thin film synthesized by a sol-gel technique were treated using a custom built inductively coupled plasma apparatus. X-ray photoelectron spectroscopy revealed that oxygen-plasma treatment increased the number of oxygen functional groups (hydroxyl groups) and introduced some Ti{sup 3+} species on the surface of TiO{sub 2}. A sample solar cell with plasma treated TiO{sub 2} showed an overall solar-to-electricity conversion efficiency of 4.3%, about a 13% increase over untreated TiO{sub 2}. The photon conversion efficiency for the plasma treated TiO{sub 2} was 34% higher than untreated TiO{sub 2}. This enhanced cell-performance is partly due to increased dye adsorption from an increase in surface oxygen functional groups and also may be partly due to Ti{sup 3+} states on the surface of TiO{sub 2}. - Highlights: • Oxygen plasma is used to generate hydroxyl groups on the surface of TiO{sub 2} • Parallel study was conducted using a spin coated TiO{sub 2} and a Commercial TiO{sub 2} film. • The plasma functionalization caused increased dye uptake. • Some species in Ti{sup 3+} state are also generated after oxygen plasma. • Dye sensitised solar cell with functionalised electrode showed improved efficiency.

  6. Temperature dependent optical characterization of Ni-TiO2 thin films as potential photocatalytic material

    Science.gov (United States)

    De, Rajnarayan; Haque, S. Maidul; Tripathi, S.; Rao, K. Divakar; Singh, Ranveer; Som, T.; Sahoo, N. K.

    2017-09-01

    Along with other transition metal doped titanium dioxide materials, Ni-TiO2 is considered to be one of the most efficient materials for catalytic applications due to its suitable energy band positions in the electronic structure. The present manuscript explores the possibility of improving the photocatalytic activity of RF magnetron sputtered Ni-TiO2 films upon heat treatment. Optical, structural and morphological and photocatalytic properties of the films have been investigated in detail for as deposited and heat treated samples. Evolution of refractive index (RI) and total film thickness as estimated from spectroscopic ellipsometry characterization are found to be in agreement with the trend in density and total film thickness estimated from grazing incidence X-ray reflectivity measurement. Interestingly, the evolution of these macroscopic properties were found to be correlated with the corresponding microstructural modifications realized in terms of anatase to rutile phase transformation and appearance of a secondary phase namely NiTiO3 at high temperature. Corresponding morphological properties of the films were also found to be temperature dependent which leads to modifications in the grain structure. An appreciable reduction of optical band gap from 2.9 to 2.5 eV of Ni-TiO2 thin films was also observed as a result of post deposition heat treatment. Testing of photocatalytic activity of the films performed under UV illumination demonstrates heat treatment under atmospheric ambience to be an effective means to enhance the photocatalytic efficiency of transition metal doped titania samples.

  7. QCM gas sensor characterization of ALD-grown very thin TiO2 films

    Science.gov (United States)

    Boyadjiev, S.; Georgieva, V.; Vergov, L.; Szilágyi, I. M.

    2018-03-01

    The paper presents a technology for preparation and characterization of titanium dioxide (TiO2) thin films suitable for gas sensor applications. Applying atomic layer deposition (ALD), very thin TiO2 films were deposited on quartz resonators, and their gas sensing properties were studied using the quartz crystal microbalance (QCM) method. The TiO2 thin films were grown using Ti(iOPr)4 and water as precursors. The surface of the films was observed by scanning electron microscopy (SEM), coupled with energy dispersive X-ray analysis (EDX) used for a composition study. The research was focused on the gas-sensing properties of the films. Films of 10-nm thickness were deposited on quartz resonators with Au electrodes and the QCMs were used to build highly sensitive gas sensors, which were tested for detecting NO2. Although very thin, these ALD-grown TiO2 films were sensitive to NO2 already at room temperature and could register as low concentrations as 50 ppm, while the sorption was fully reversible, and the sensors could be fully recovered. With the technology presented, the manufacturing of gas sensors is simple, fast and cost-effective, and suitable for energy-effective portable equipment for real-time environmental monitoring of NO2.

  8. Drug loading of nanoporous TiO2 films

    International Nuclear Information System (INIS)

    Ayon, Arturo A; Cantu, Michael; Chava, Kalpana; Agrawal, C Mauli; Feldman, Marc D; Johnson, Dave; Patel, Devang; Marton, Denes; Shi, Emily

    2006-01-01

    The loading of therapeutic amounts of drug on a nanoporous TiO 2 surface is described. This novel drug-loading scheme on a biocompatible surface, when employed on medical implants, will benefit patients who require the deployment of drug-eluting implants. Anticoagulants, analgesics and antibiotics can be considered on the associated implants for drug delivery during the time of maximal pain or risk for patients undergoing orthopedic procedures. Therefore, this scheme will maximize the chances of patient recovery. (communication)

  9. Processing and thin film formation of TiO{sub 2}-Pt nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Es-Souni, M.; Kartopu, G.; Habouti, S.; Piorra, A.; Solterbeck, C.H. [Institute for Materials and Surface Technology, Kiel University of Applied Sciences, Grenzstr. 3, 24149 Kiel (Germany); Es-Souni, Mar.; Brandies, H.F. [Faculty of Dentistry, Christian-Albrecht University, Kiel (Germany)

    2008-02-15

    Thin films of TiO{sub 2}-Pt nanocomposites containing 4 at% Pt have been processed via spin-coating. Film characterization involved XRD, Raman as well as XPS and scanning surface potential microscopy (SSPM). After annealing at 500 C the thin films consisted of nanocrystalline anatase and a few nm Pt nanoclusters. Annealing at 600 C resulted in the formation of a high volume fraction of rutile, {proportional_to}70%, and a coarsening of the microstructure, including Pt nanoparticles which attained a mean particle size of up to 11 nm. These results contrasted with those of pure TiO{sub 2} films obtained at 600 C which showed only a limited amount of rutile formation, namely 9%. Raman spectra of Pt-containing samples exhibited a fluorescence emission, as background to the Raman features, which was attributed to photoinduced luminescence from Pt nanoparticles supported by their surface plasmon resonance. Emission intensity being much higher in 600 C film indicated a difference between the two films in terms of the (Pt) particle size and crystallinity, in agreement with the XRD results. XPS investigations revealed different oxidation states of Pt at the surface and in the film interior. The spectra suggested a slight oxidation of Pt at the surface while mainly metallic Pt was revealed in the film interior. The morphology and distribution of the Pt nanoparticles in the films annealed at 600 C were investigated using SSPM. Discrete Pt nanoparticles, mainly distributed in the vicinity of TiO{sub 2} grain boundaries were revealed. Nanocomposite film formation, Pt distribution and morphology are explained in terms of the limited solubility of Pt in the TiO{sub 2} lattice and its higher surface energy in comparison to that of TiO{sub 2}. Both effects are believed to lead to the formation of Pt nanoparticles at the (anatase or rutile) grain boundaries. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  10. Charge transfer in photorechargeable composite films of TiO2 and polyaniline

    Science.gov (United States)

    Nomiyama, Teruaki; Sasabe, Kenichi; Sakamoto, Kenta; Horie, Yuji

    2015-07-01

    A photorechargeable battery (PRB) is a photovoltaic device having an energy storage function in a single cell. The photoactive electrode of PRB is a bilayer film consisting of bare porous TiO2 and a TiO2-polyaniline (PANi) mixture that work as a photovoltaic current generator and an electrochemical energy storage by ion dedoping, respectively. To study the charge transfer between TiO2 and PANi, the photorechargeable quantum efficiency QE ([electron count on discharge]/[incident photon count on photocharge]) was measured by varying the thickness LS of the TiO2-PANi mixture. The quantum efficiency QEuv for UV photons had a maximum of ˜7% at LS ˜ 7 µm. The time constant τTP for the charge transfer was about 10-1 s, which was longer ten times or more than the lifetime of excited electrons within TiO2. These facts reveal that the main rate-limiting factor in the photocharging process is the charge transfer between TiO2 and PANi.

  11. Origin of visible-light sensitivity in N-doped TiO2 films

    International Nuclear Information System (INIS)

    Nakano, Yoshitaka; Morikawa, Takeshi; Ohwaki, Takeshi; Taga, Yasunori

    2007-01-01

    We report on visible-light sensitivity in N-doped TiO 2 (TiO 2 :N) films that were deposited on n + -GaN/Al 2 O 3 substrates by reactive magnetron sputtering and subsequently crystallized by annealing at 550 deg. C in flowing N 2 gas. The N-doping concentration was ∼8.8%, as determined by X-ray photoelectron spectroscopy measurements. From transmission electron microscopic observations and optical absorption measurements, yellow-colored TiO 2 :N samples showed an enhanced granular structure and strong absorption in the visible-light region. Photoelectron spectroscopy in air measurements showed a noticeable decrease in ionization energy of TiO 2 by the N doping. Deep-level optical spectroscopy measurements revealed two characteristic deep levels located at ∼1.18 and ∼2.48 eV below the conduction band. The 1.18 eV level is probably attributable to the O vacancy state and can be active as an efficient generation-recombination center. The pronounced 2.48 eV band is newly introduced by the N doping and contributes to band-gap narrowing of TiO 2 by mixing with the O 2p valence band. Therefore, this localized intraband is probably one origin of visible-light sensitivity in TiO 2 :N

  12. Fabrication of doped TiO2 nanotube array films with enhanced photo-catalytic activity

    Science.gov (United States)

    Peighambardoust, Naeimeh-Sadat; Khameneh-asl, Shahin; Khademi, Adib

    2018-01-01

    In the present work, we investigate the N and Fe-doped TiO2 nanotube array film prepared by treating TiO2 nanotube array film with ammonia solution and anodizing in Fe(NO3)3 solution respectively. This method avoided the use of hazardous ammonia gas, or laborious ion implantation process. N and Fe-doped TiO2 nanotube arrays (TiO2 NTs) were prepared by electrochemical anodization process in 0.5 wt % HF aqueous solution. The anodization was performed at the conditions of 20 V and 20 min, Followed by a wet immersion in NH3.H2O (1M) for N-doping for 2 hr and annealing post-treatment at 450 °C. The morphology and structure of the nanotube films were characterized by field emission scanning electron microscope (FESEM) and EDX. UV-vis. illumination test were done to observe photo-enhanced catalysis. The effect of different annealing temperature on the structure and photo-absorption property of the TiO2-TNTs was investigated. The results showed that N-TNTs nanotubes exhibited higher photocatalytic activity compared whit the Fe-doped and pure TNTs, because doping N promoted the separation of the photogenerated electrons and holes.

  13. Optical, structural and photocatalysis properties of Cu-doped TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bensouici, F., E-mail: fbensouici@yahoo.fr [Department of Physics, URMPE Unite, UMBB University, 35000 Boumerdes (Algeria); Bououdina, M.; Dakhel, A.A. [Department of Physics, College of Science, University of Bahrain, PO Box 32038 (Bahrain); Tala-Ighil, R.; Tounane, M.; Iratni, A. [Department of Physics, URMPE Unite, UMBB University, 35000 Boumerdes (Algeria); Souier, T. [Department of Physics, College of Science, Sultan Qaboos University, PO Box 36 (Oman); Liu, S.; Cai, W. [Key laboratory of Materials Physics, Anhui Key Laboratory of Nanomaterials and Technology, Center for Environmental and Energy Nanomaterials, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031 (China)

    2017-02-15

    Highlights: • A simple chemical route to obtain thin layers of Cu doped TiO{sub 2}. • Detailed structure analysis was carried out by Rietveld refinements. • Forming the CuO phase decreases the efficiency photocatalysis of TiO{sub 2}. - Abstract: Pure and Cu{sup +2} doped TiO{sub 2} thin films have been successfully deposited onto glass substrate by sol–gel dip-coating. The films were annealed at 450 °C for 1 h and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM-EDX), atomic force microscopy (AFM), UV–vis spectrophotometer and photocatalytic degradation of methylene blue. XRD confirmed the presence of two phases at higher Cu concentration; TiO{sub 2} anatase and CuO. AFM analysis showed that the surface roughness increases within increasing Cu content as well as the presence of large aggregates at higher Cu content. SEM observations confirmed the granular structure of the films, and EDX analysis revealed a low solubility limit (effective doping) of Cu into TiO{sub 2} lattice. It was found that the optical band gap energy decreases with increasing Cu content. At constant irradiation time, the photo-degradation of methylene blue rate decreased with increasing concentration of Cu{sup +2}.

  14. Synthesis and characterization of polythiophene-modified TiO2 ...

    Indian Academy of Sciences (India)

    prospects and has attracted much attention for its many advantages such as ... the ground state of the polymer located in the semiconduc- tor energy gap into an .... in figure 1(c) that the polythiophene modified TiO2 nanotube arrays still keep ...

  15. Asymmetric photoelectric property of transparent TiO2 nanotube films loaded with Au nanoparticles

    International Nuclear Information System (INIS)

    Wang, Hui; Liang, Wei; Liu, Yiming; Zhang, Wanggang; Zhou, Diaoyu; Wen, Jing

    2016-01-01

    Highlights: • Highly transparent films of TiO 2 nanotube arrays were directly fabricated on FTO glasses. • Semitransparent TNT-Au composite films were obtained and exhibited excellent photoelectrocatalytic ability. • Back-side of TNT-Au composite films was firstly irradiated and tested to compare with front-side of films. - Abstract: Semitransparent composite films of Au loaded TiO 2 nanotubes (TNT-Au) were prepared by sputtering Au nanoparticles on highly transparent TiO 2 nanotubes films, which were fabricated directly on FTO glasses by anodizing the Ti film sputtered on the FTO glasses. Compared with pure TNT films, the prepared TNT-Au films possessed excellent absorption ability and high photocurrent response and improved photocatalytic activity under visible-light irradiation. It could be concluded that Au nanoparticles played important roles in improving the photoelectrochemical performance of TNT-Au films. Moreover, in this work, both sides of TNT-Au films were researched and compared owing to theirs semitransparency. It was firstly found that the photoelectric activity of TNT-Au composite films with back-side illumination was obviously superior to front-side illumination.

  16. Asymmetric photoelectric property of transparent TiO{sub 2} nanotube films loaded with Au nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hui [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024 (China); College of Applied Science, Taiyuan University of Science and Technology, Taiyuan, Shanxi 030024 (China); Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, Shanxi 030024 (China); Liang, Wei, E-mail: 986903124@qq.com [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024 (China); Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, Shanxi 030024 (China); Liu, Yiming; Zhang, Wanggang; Zhou, Diaoyu; Wen, Jing [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan, Shanxi 030024 (China); Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan, Shanxi 030024 (China)

    2016-11-15

    Highlights: • Highly transparent films of TiO{sub 2} nanotube arrays were directly fabricated on FTO glasses. • Semitransparent TNT-Au composite films were obtained and exhibited excellent photoelectrocatalytic ability. • Back-side of TNT-Au composite films was firstly irradiated and tested to compare with front-side of films. - Abstract: Semitransparent composite films of Au loaded TiO{sub 2} nanotubes (TNT-Au) were prepared by sputtering Au nanoparticles on highly transparent TiO{sub 2} nanotubes films, which were fabricated directly on FTO glasses by anodizing the Ti film sputtered on the FTO glasses. Compared with pure TNT films, the prepared TNT-Au films possessed excellent absorption ability and high photocurrent response and improved photocatalytic activity under visible-light irradiation. It could be concluded that Au nanoparticles played important roles in improving the photoelectrochemical performance of TNT-Au films. Moreover, in this work, both sides of TNT-Au films were researched and compared owing to theirs semitransparency. It was firstly found that the photoelectric activity of TNT-Au composite films with back-side illumination was obviously superior to front-side illumination.

  17. Enhanced visible light photocatalytic performance of polyaniline modified mesoporous single crystal TiO{sub 2} microsphere

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Yaocheng [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Tang, Lin, E-mail: tanglin@hnu.edu.cn [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Zeng, Guangming, E-mail: zgming@hnu.edu.cn [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Dong, Haoran; Yan, Ming; Wang, Jingjing [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Hu, Wei [College of Physics and Microelectronics Science, Hunan University, Changsha, 410082 (China); Wang, Jiajia; Zhou, Yaoyu; Tang, Jing [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China)

    2016-11-30

    Highlights: • The mesoporous single crystal microsphere of PANI/MS-TiO{sub 2} improved the light absorption. • The mesoporous structure of MS-TiO{sub 2} can increase the loading amount of PANI. • The synergistic effect between PANI and MS-TiO{sub 2} promoted the separation of charges. • Improved photocatalysis was achieved via PANI modified mesoporous single crystal TiO{sub 2} microsphere. - Abstract: Polyaniline (PANI) modified mesoporous single crystal TiO{sub 2} microsphere (PANI/MS-TiO{sub 2}) with excellent photocatalytic activity was successfully prepared by a simple method of solution evaporation and chemisorption. The X-ray diffraction characterization demonstrated that the whole MS-TiO{sub 2} kept the crystal type of anatase. The nitrogen adsorption-desorption characterization coupled with scanning electron microscopy indicated that the MS-TiO{sub 2} possessed a unique mesoporous structure with high specific surface area, which resulted in the increased load of PANI on the surface of MS-TiO{sub 2} and multiple light reflection in the photocatalyst. The UV–vis diffuse reflectance spectra confirmed that PANI/MS-TiO{sub 2} presented more absorption ability in the visible light range than that of the pristine MS-TiO{sub 2}. The transient photocurrent responses and electrochemical impedance spectroscopy (EIS) indicated the high photo responses and fast photogenerated charge separation efficiency of PANI/MS-TiO{sub 2}. The photocatalytic activity of the PANI/MS-TiO{sub 2} was evaluated by the photodegradation of RhB and MB under visible light irradiation. MS-TiO{sub 2} photocatalyst with different molar ration of PANI had been prepared, and the results showed that the optimal photocatalyst (PANI/MS-TiO{sub 2} (1:40)) exhibited the highest photocatalytic efficiency which is nearly three times as great as that of pristine MS-TiO{sub 2} for the degradation of the RhB and MB under visible light irradiation. The remarkable performance of the PANI/MS-TiO

  18. Graphene Modified TiO2 Composite Photocatalysts: Mechanism, Progress and Perspective

    Science.gov (United States)

    Tang, Bo; Chen, Haiqun; Peng, Haoping; Wang, Zhengwei; Huang, Weiqiu

    2018-01-01

    Graphene modified TiO2 composite photocatalysts have drawn increasing attention because of their high performance. Some significant advancements have been achieved with the continuous research, such as the corresponding photocatalytic mechanism that has been revealed. Specific influencing factors have been discovered and potential optimizing methods are proposed. The latest developments in graphene assisted TiO2 composite photocatalysts are abstracted and discussed. Based on the primary reasons behind the observed phenomena of these composite photocatalysts, probable development directions and further optimizing strategies are presented. Moreover, several novel detective technologies—beyond the decomposition test—which can be used to judge the photocatalytic performances of the resulting photocatalysts are listed and analyzed. Although some objectives have been achieved, new challenges still exist and hinder the widespread application of graphene-TiO2 composite photocatalysts, which deserves further study. PMID:29439545

  19. Magnetic properties of co-modified Fe,N-TiO2 nanocomposites

    Directory of Open Access Journals (Sweden)

    Zolnierkiewicz Grzegorz

    2015-01-01

    Full Text Available Iron and nitrogen co-modified titanium dioxide nanocomposites, nFe,N-TiO2 (where n = 1, 5 and 10 wt% of Fe, were investigated by detailed dc susceptibility and magnetization measurements. Different kinds of magnetic interactions were evidenced depending essentially on iron loading of TiO2. The coexistence of superparamagnetic, paramagnetic and ferromagnetic phases was identified at high temperatures. Strong antiferromagnetic interactions were observed below 50 K, where some part of the nanocomposite entered into a long range antiferromagnetic ordering. Antiferromagnetic interactions were attributed to the magnetic agglomerates of iron-based and trivalent iron ions in FeTiO3 phase,whereas ferromagnetic interactions stemmed from the F-center mediated bound magnetic polarons.

  20. Transparent nanostructured Fe-doped TiO2 thin films prepared by ultrasonic assisted spray pyrolysis technique

    Science.gov (United States)

    Rasoulnezhad, Hossein; Hosseinzadeh, Ghader; Ghasemian, Naser; Hosseinzadeh, Reza; Homayoun Keihan, Amir

    2018-05-01

    Nanostructured TiO2 and Fe-doped TiO2 thin films with high transparency were deposited on glass substrate through ultrasonic-assisted spray pyrolysis technique and were used in the visible light photocatalytic degradation of MB dye. The resulting thin films were characterized by scanning electron microscopy (SEM), Raman spectroscopy, photoluminescence spectroscopy, x-ray diffraction (XRD), and UV-visible absorption spectroscopy techniques. Based on Raman spectroscopy results, both of the TiO2 and Fe-doped TiO2 films have anatase crystal structure, however, because of the insertion of Fe in the structure of TiO2 some point defects and oxygen vacancies are formed in the Fe-doped TiO2 thin film. Presence of Fe in the structure of TiO2 decreases the band gap energy of TiO2 and also reduces the electron–hole recombination rate. Decreasing of the electron–hole recombination rate and band gap energy result in the enhancement of the visible light photocatalytic activity of the Fe-doped TiO2 thin film.

  1. Hierarchical porous TiO{sub 2} thin films by soft and dual templating

    Energy Technology Data Exchange (ETDEWEB)

    Henrist, Catherine, E-mail: catherine.henrist@ulg.ac.be [University of Liege, Department of Chemistry, GREENMAT-LCIS, B6 Sart Tilman, Liege 4000 (Belgium); University of Liege, Center for Applied Technology in Microscopy (CATmu), B6 Sart Tilman, Liege 4000 (Belgium); Dewalque, Jennifer [University of Liege, Department of Chemistry, GREENMAT-LCIS, B6 Sart Tilman, Liege 4000 (Belgium); Cloots, Rudi [University of Liege, Department of Chemistry, GREENMAT-LCIS, B6 Sart Tilman, Liege 4000 (Belgium); University of Liege, Center for Applied Technology in Microscopy (CATmu), B6 Sart Tilman, Liege 4000 (Belgium); Vertruyen, Bénédicte; Jonlet, Jonathan; Colson, Pierre [University of Liege, Department of Chemistry, GREENMAT-LCIS, B6 Sart Tilman, Liege 4000 (Belgium)

    2013-07-31

    Hierarchical porous structures, with different pore sizes, including pores larger than 10 nm, constitute an important field of research for many applications such as selective molecule detection, catalysis, dye-sensitized solar cells, nanobiotechnology and nanomedecine. However, increasing the pore size logically results in the decrease of specific surface. There is a need to quantify and predict the resulting porosity and specific surface. We have prepared hierarchical porous TiO{sub 2} thin films either by surfactant templating (soft) or dual surfactant/nanospheres templating (soft/hard). They all show narrow, bimodal distribution of pores. Soft templating route uses a modified sol–gel procedure by adding a swelling agent (polypropylene glycol) to a precursor solution containing Ti alkoxide and block-copolymer surfactant. This scheme leads to very thin films showing high specific surface and bimodal porosity with diameters of 10 nm and 54 nm. Dual templating route combines a precursor solution made of Ti alkoxide and block-copolymer surfactant with polystyrene (PS) nanospheres (diam. 250 nm) in a one-pot simple process. This gives thicker films with a bimodal distribution of pores (8 nm and 165-200 nm). The introduction of PS nanospheres in the surfactant–Ti system does not interfere with the soft templating process and results in a macroporosity with a pore diameter 20–30% smaller than the original beads diameter. The dye loading of hierarchical films is compared to pure surfactant-templated TiO{sub 2} films and shows a relative decrease of 29% for soft templating and 43% for dual templating. The microstructure of bimodal porous films is characterized by several techniques such as transmission and scanning electron microscopy, X-ray diffraction, profilometry and ellipsometry. Finally, a geometrical model is proposed and validated for each system, based on the agreement between calculated specific surfaces and experimental dye loading with N719 dye

  2. Impact of symmetry on the ferroelectric properties of CaTiO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Biegalski, Michael D.; Qiao, Liang [Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Gu, Yijia; Chen, Long-Qing [Department of Materials Science and Engineering, Pennsylvania State University, University Park, Pennsylvania 16801 (United States); Mehta, Apurva [Stanford Synchrotron Lightsource SLAC National Accelerator Laboratory, Menlo Park, California 94025 (United States); He, Qian; Borisevich, Albina [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Takamura, Yayoi, E-mail: ytakamura@ucdavis.edu [Department of Chemical Engineering and Materials Science, University of California Davis, Davis, California 95616 (United States)

    2015-04-20

    Epitaxial strain is a powerful tool to induce functional properties such as ferroelectricity in thin films of materials that do not possess ferroelectricity in bulk form. In this work, a ferroelectric state was stabilized in thin films of the incipient ferroelectric, CaTiO{sub 3}, through the careful control of the biaxial strain state and TiO{sub 6} octahedral rotations. Detailed structural characterization was carried out by synchrotron x-ray diffraction and scanning transmission electron microscopy. CaTiO{sub 3} films grown on La{sub 0.18}Sr{sub 0.82}Al{sub 0.59}Ta{sub 0.41}O{sub 3} (LSAT) and NdGaO{sub 3} (NGO) substrates experienced a 1.1% biaxial strain state but differed in their octahedral tilt structures. A suppression of the out-of-plane rotations of the TiO{sub 6} octahedral in films grown on LSAT substrates resulted in a robust ferroelectric I4 mm phase with remnant polarization ∼5 μC/cm{sup 2} at 10 K and T{sub c} near 140 K. In contrast, films grown on NGO substrates with significant octahedral tilting showed reduced polarization and T{sub c}. These results highlight the key role played by symmetry in controlling the ferroelectric properties of perovskite oxide thin films.

  3. The influence of metal interlayers on the structural and optical properties of nano-crystalline TiO 2 films

    KAUST Repository

    Yang, Yong; Zhang, Qiang; Zhang, Bei; Mi, Wenbo; Chen, Long; Li, Lin; Zhao, Chao; Diallo, Elhadj; Zhang, Xixiang

    2012-01-01

    TiO 2-M-TiO 2 (M = W, Co and Ag) multilayer films have been deposited on glass substrates using reactive magnetron sputtering, then annealed in air for 2 h at 500°C. The structure, surface morphology and optical properties of the films have been

  4. Structural and vibrational investigations of Nb-doped TiO2 thin films

    International Nuclear Information System (INIS)

    Uyanga, E.; Gibaud, A.; Daniel, P.; Sangaa, D.; Sevjidsuren, G.; Altantsog, P.; Beuvier, T.; Lee, Chih Hao; Balagurov, A.M.

    2014-01-01

    Highlights: • We studied the evolutions of structure for TiO 2 thin film as changes with Nb doping and temperatures. • Up to 800 °C, the grain size of Nb 0.1 Ti 0.9 O 2 is smaller than for pure TiO 2 because doped Nb hinders the growth of the TiO 2 grains. • There was no formation of the rutile phase at high temperature. • Nb doped TiO 2 films have high electron densities at 400–700 °C. • Nb dope extends the absorbance spectra of TiO 2 which leads to the band gap reduce. - Abstract: Acid-catalyzed sol–gel and spin-coating methods were used to prepare Nb-doped TiO 2 thin film. In this work, we studied the effect of niobium doping on the structure, surface, and absorption properties of TiO 2 by energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), X-ray reflectometry (XRR), X-ray photoelectron spectroscopy (XPS), Raman, and UV–vis absorption spectroscopy at various annealing temperatures. EDX spectra show that the Nb:Ti atomic ratios of the niobium-doped titania films are in good agreement with the nominal values (5 and 10%). XPS results suggest that charge compensation is achieved by the formation of Ti vacancies. Specific niobium phases are not observed, thus confirming that niobium is well incorporated into the titania crystal lattice. Thin films are amorphous at room temperature and the formation of anatase phase appeared at an annealing temperature close to 400 °C. The rutile phase was not observed even at 900 °C (XRD and Raman spectroscopy). Grain sizes and electron densities increased when the temperature was raised. Nb-doped films have higher electron densities and lower grain sizes due to niobium doping. Grain size inhibition can be explained by lattice stress induced by the incorporation of larger Nb 5+ ions into the lattice. The band gap energy of indirect transition of the TiO 2 thin films was calculated to be about 3.03 eV. After niobium doping, it decreased to 2.40 eV

  5. Improvement of epoxy resin properties by incorporation of TiO2 nanoparticles surface modified with gallic acid esters

    International Nuclear Information System (INIS)

    Radoman, Tijana S.; Džunuzović, Jasna V.; Jeremić, Katarina B.; Grgur, Branimir N.; Miličević, Dejan S.; Popović, Ivanka G.; Džunuzović, Enis S.

    2014-01-01

    Highlights: • Nanocomposites of epoxy resin and TiO 2 nanoparticles surface modified with gallates. • The T g of epoxy resin was increased by incorporation of surface modified TiO 2 . • WVTR of epoxy resin decreased in the presence of surface modified TiO 2 nanoparticles. • WVTR of nanocomposites was reduced with increasing gallates hydrophobic chain length. • Modified TiO 2 nanoparticles react as oxygen scavengers, inhibiting steel corrosion. - Abstract: Epoxy resin/titanium dioxide (epoxy/TiO 2 ) nanocomposites were obtained by incorporation of TiO 2 nanoparticles surface modified with gallic acid esters in epoxy resin. TiO 2 nanoparticles were obtained by acid catalyzed hydrolysis of titanium isopropoxide and their structural characterization was performed by X-ray diffraction and transmission electron microscopy. Three gallic acid esters, having different hydrophobic part, were used for surface modification of the synthesized TiO 2 nanoparticles: propyl, hexyl and lauryl gallate. The gallate chemisorption onto surface of TiO 2 nanoparticles was confirmed by Fourier transform infrared and ultraviolet–visible spectroscopy, while the amount of surface-bonded gallates was determined using thermogravimetric analysis. The influence of the surface modified TiO 2 nanoparticles, as well as the length of hydrophobic part of the gallate used for surface modification of TiO 2 nanoparticles, on glass transition temperature, barrier, dielectric and anticorrosive properties of epoxy resin was investigated by differential scanning calorimetry, water vapor transmission test, dielectric spectroscopy, electrochemical impedance spectroscopy and polarization measurements. Incorporation of surface modified TiO 2 nanoparticles in epoxy resin caused increase of glass transition temperature and decrease of the water vapor permeability of epoxy resin. The water vapor transmission rate of epoxy/TiO 2 nanocomposites was reduced with increasing hydrophobic part chain length of

  6. Synthesis and electronic properties of Fe2TiO5 epitaxial thin films

    Science.gov (United States)

    Osada, Motoki; Nishio, Kazunori; Hwang, Harold Y.; Hikita, Yasuyuki

    2018-05-01

    We investigate the growth phase diagram of pseudobrookite Fe2TiO5 epitaxial thin films on LaAlO3 (001) substrates using pulsed laser deposition. Control of the oxygen partial pressure and temperature during deposition enabled selective stabilization of (100)- and (230)-oriented films. In this regime, we find an optical gap of 2.1 eV and room temperature resistivity in the range of 20-80 Ω cm, which are significantly lower than α-Fe2O3, making Fe2TiO5 potentially an ideal inexpensive visible-light harvesting semiconductor. These results provide a basis to incorporate Fe2TiO5 in oxide heterostructures for photocatalytic and photoelectrochemical applications.

  7. Characterization of TiO2 Thin Films on Glass Substrate Growth Using DC Sputtering Technique

    International Nuclear Information System (INIS)

    Agus Santoso; Tjipto Sujitno; Sayono

    2002-01-01

    It has been fabricated and characterization a TiO 2 thin films deposited on glass substrate using DC sputtering technique. Fabrication of TiO 2 thin films were carried out at electrode voltage 4 kV, sputtering current 5 mA, vacuum pressure 5 x 10 -4 torr, deposition time 150 minutes, and temperature of the substrate were varied from 150 -350 o C, while as a gas sputter was argon. The results was tested their micro structure using SEM, and crystal structure using XRD and found that the crystal structure of TiO 2 powder before deposited on glass substrate was rutile and anatase with orientation (110) and (200) for anatase and (100) and (111) rutile structure. While the crystal structure which deposited at temperature 150 o C and deposition time 2.5 hours was anatase with orientation (001) and (200). (author)

  8. Synthesis and characterization of C-doped TiO{sub 2} thin films for visible-light-induced photocatalytic degradation of methyl orange

    Energy Technology Data Exchange (ETDEWEB)

    Hassan, Mohamed Elfatih; Cong, Longchao; Liu, Guanglong, E-mail: liugl@mail.hzau.edu.cn; Zhu, Duanwei; Cai, Jianbo

    2014-03-01

    Graphical abstract: - Highlights: • C-TiO{sub 2} thin films were successfully synthesized by modified sol–gel method based on the self-assembly technique. • Tween 80, one kind of hydrocarbon surfactants, was used as template and carbon precursor. • A thorough material characterization was performed to determine the effect of calcination time on the structural and optical properties of the synthesized catalyst films. - Abstract: C-TiO{sub 2} thin films were synthesized by a modified sol–gel route based on the self-assembly technique exploiting Tween80 (T80) as a pore directing agent and carbon source. The effect of calcination time on the photocatalytic activity of C-doped TiO{sub 2} catalyst was studied. The samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier transforms infrared (FTIR), UV–vis diffuse reflectance spectroscopy, and photoluminescence spectra (PL). The XRD results showed that C-TiO{sub 2} sample calcined at 400 °C for various times exhibited anatase phase and no other crystal phase was identified. C-TiO{sub 2} exhibited a shift in an absorption edge of samples in the visible region than that of conventional or reference TiO{sub 2}. The XPS results showed an existence of C in the TiO{sub 2} catalysts and C might be existed as C-O-Ti group. Moreover, the C-TiO{sub 2} thin film calcined at 400 °C for 30 min showed the lowest PL intensity due to a decrease in the recombination rate of photogenerated electrons and holes under UV light irradiation. Also the photocatalytic activity of synthesized catalyst was evaluated by decomposition of methyl orange (MO) under visible light irradiation. The results showed that the optimum preparations of C-TiO{sub 2} thin films were found to be under calcination temperature of 400, calcination time of 30 min, and with preparation 9 layers film.

  9. A short literature survey on iron and cobalt ion doped TiO2 thin films and photocatalytic activity of these films against fungi

    International Nuclear Information System (INIS)

    Tatlıdil, İlknur; Bacaksız, Emin; Buruk, Celal Kurtuluş; Breen, Chris; Sökmen, Münevver

    2012-01-01

    Highlights: ► Co or Fe doped TiO 2 thin films were prepared by sol–gel method. ► We obtained lower E g values for Fe-doped and Co-TiO 2 thin films. ► Doping greatly affected the size and shape of the TiO 2 nanoparticles. ► Photocatalytic killing effect of the doped TiO 2 thin films on C. albicans and A. niger was significantly higher than undoped TiO 2 thin film for short exposure periods. - Abstract: In this study, a short recent literature survey which concentrated on the usage of Fe 3+ or Co 2+ ion doped TiO 2 thin films and suspensions were summarized. Additionally, a sol–gel method was used for preparation of the 2% Co or Fe doped TiO 2 thin films. The surface of the prepared materials was characterised using scanning-electron microscopy (SEM) combined with energy dispersive X-ray (EDX) analysis and band gap of the films were calculated from the transmission measurements that were taken over the range of 190 and 1100 nm. The E g value was 3.40 eV for the pure TiO 2 , 3.00 eV for the Fe-doped TiO 2 film and 3.25 eV for Co-TiO 2 thin film. Iron or cobalt doping at lower concentration produce more uniformed particles and doping greatly affected the size and shape of the TiO 2 nanoparticles. Photocatalytic killing effect of the 2% Co doped TiO 2 thin film on Candida albicans was significantly higher than Fe doped TiO 2 thin film for short and long exposure periods. Doped thin films were more effective on Aspergillus niger for short exposure periods.

  10. Surface plasmon resonance caused by gold nanoparticles formed on sprayed TiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Oja Acik, I., E-mail: ilona.oja@ttu.ee [Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Dolgov, L. [Institute of Physics, University of Tartu, Riia 142, 51014 Tartu (Estonia); Krunks, M.; Mere, A.; Mikli, V. [Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Pikker, S.; Loot, A.; Sildos, I. [Institute of Physics, University of Tartu, Riia 142, 51014 Tartu (Estonia)

    2014-02-28

    Titania films covered by gold nanoparticles are prepared by combination of spray pyrolysis and spin-coating methods. Proposed combination of techniques is prospective for photovoltaic coatings with plasmonic properties. The prepared TiO{sub 2} films with Au nanoparticles demonstrate variation in size of the gold nanocrystallites from 36 to 56 nm depending on the concentration of the HAuCl{sub 4}∙ 3H{sub 2}O solution and plasmonic light extinction in the spectral range of 600–650 nm. It is shown that gold nanocrystallites enhance Raman scattering from the underlying thin TiO{sub 2} film. - Highlights: • TiO{sub 2} thin films with Au-nanoparticles were produced by chemical solution methods. • The size and shape of Au-nanoparticles are controlled by the [HAuCl{sub 4}∙ 3H{sub 2}O]. • Plasmon light extinction was tuned from 600 to 650 nm by changing [HAuCl{sub 4}∙ 3H{sub 2}O]. • Raman scattering intensity of TiO{sub 2} films is enhanced by the Au-nanoparticles.

  11. Room temperature growth of nanocrystalline anatase TiO2 thin films by dc magnetron sputtering

    International Nuclear Information System (INIS)

    Singh, Preetam; Kaur, Davinder

    2010-01-01

    We report, the structural and optical properties of nanocrystalline anatase TiO 2 thin films grown on glass substrate by dc magnetron sputtering at room temperature. The influence of sputtering power and pressure over crystallinity and surface morphology of the films were investigated. It was observed that increase in sputtering power activates the TiO 2 film growth from relative lower surface free energy to higher surface free energy. XRD pattern revealed the change in preferred orientation from (1 0 1) to (0 0 4) with increase in sputtering power, which is accounted for different surface energy associated with different planes. Microstructure of the films also changes from cauliflower type to columnar type structures with increase in sputtering power. FESEM images of films grown at low pressure and low sputtering power showed typical cauliflower like structure. The optical measurement revealed the systematic variation of the optical constants with deposition parameters. The films are highly transparent with transmission higher than 90% with sharp ultraviolet cut off. The transmittance of these films was found to be influenced by the surface roughness and film thickness. The optical band gap was found to decrease with increase in the sputtering power and pressure. The refractive index of the films was found to vary in the range of 2.50-2.24 with increase in sputtering pressure or sputtering power, resulting in the possibility of producing TiO 2 films for device applications with different refractive index, by changing the deposition parameters.

  12. Cytotoxicity Evaluation of Anatase and Rutile TiO2 Thin Films on CHO-K1 Cells in Vitro

    Directory of Open Access Journals (Sweden)

    Blanca Cervantes

    2016-07-01

    Full Text Available Cytotoxicity of titanium dioxide (TiO2 thin films on Chinese hamster ovary (CHO-K1 cells was evaluated after 24, 48 and 72 h of culture. The TiO2 thin films were deposited using direct current magnetron sputtering. These films were post-deposition annealed at different temperatures (300, 500 and 800 °C toward the anatase to rutile phase transformation. The root-mean-square (RMS surface roughness of TiO2 films went from 2.8 to 8.08 nm when the annealing temperature was increased from 300 to 800 °C. Field emission scanning electron microscopy (FESEM results showed that the TiO2 films’ thickness values fell within the nanometer range (290–310 nm. Based on the results of the tetrazolium dye and trypan blue assays, we found that TiO2 thin films showed no cytotoxicity after the aforementioned culture times at which cell viability was greater than 98%. Independently of the annealing temperature of the TiO2 thin films, the number of CHO-K1 cells on the control substrate and on all TiO2 thin films was greater after 48 or 72 h than it was after 24 h; the highest cell survival rate was observed in TiO2 films annealed at 800 °C. These results indicate that TiO2 thin films do not affect mitochondrial function and proliferation of CHO-K1 cells, and back up the use of TiO2 thin films in biomedical science.

  13. Cytotoxicity Evaluation of Anatase and Rutile TiO2 Thin Films on CHO-K1 Cells in Vitro

    Science.gov (United States)

    Cervantes, Blanca; López-Huerta, Francisco; Vega, Rosario; Hernández-Torres, Julián; García-González, Leandro; Salceda, Emilio; Herrera-May, Agustín L.; Soto, Enrique

    2016-01-01

    Cytotoxicity of titanium dioxide (TiO2) thin films on Chinese hamster ovary (CHO-K1) cells was evaluated after 24, 48 and 72 h of culture. The TiO2 thin films were deposited using direct current magnetron sputtering. These films were post-deposition annealed at different temperatures (300, 500 and 800 °C) toward the anatase to rutile phase transformation. The root-mean-square (RMS) surface roughness of TiO2 films went from 2.8 to 8.08 nm when the annealing temperature was increased from 300 to 800 °C. Field emission scanning electron microscopy (FESEM) results showed that the TiO2 films’ thickness values fell within the nanometer range (290–310 nm). Based on the results of the tetrazolium dye and trypan blue assays, we found that TiO2 thin films showed no cytotoxicity after the aforementioned culture times at which cell viability was greater than 98%. Independently of the annealing temperature of the TiO2 thin films, the number of CHO-K1 cells on the control substrate and on all TiO2 thin films was greater after 48 or 72 h than it was after 24 h; the highest cell survival rate was observed in TiO2 films annealed at 800 °C. These results indicate that TiO2 thin films do not affect mitochondrial function and proliferation of CHO-K1 cells, and back up the use of TiO2 thin films in biomedical science. PMID:28773740

  14. Detection of nicotine based on molecularly imprinted TiO{sub 2}-modified electrodes

    Energy Technology Data Exchange (ETDEWEB)

    Wu, C.-T.; Chen, P.-Y.; Chen, J.-G.; Suryanarayanan, Vembu [Department of Chemical Engineering, National Taiwan University, Taipei 10617, Taiwan (China); Ho, K.-C. [Department of Chemical Engineering, National Taiwan University, Taipei 10617, Taiwan (China); Institute of Polymer Science and Engineering, National Taiwan University, Taipei 10617, Taiwan (China)], E-mail: kcho@ntu.edu.tw

    2009-02-02

    Amperometric detection of nicotine (NIC) was carried out on a titanium dioxide (TiO{sub 2})/poly(3,4-ethylenedioxythiophene) (PEDOT)-modified electrode by a molecular imprinting technique. In order to improve the conductivity of the substrate, PEDOT was coated onto the sintered electrode by in situ electrochemical polymerization of the monomer. The sensing potential of the NIC-imprinted TiO{sub 2} electrode (ITO/TiO{sub 2}[NIC]/PEDOT) in a phosphate-buffered saline (PBS) solution (pH 7.4) containing 0.1 M KCl was determined to be 0.88 V (vs. Ag/AgCl/saturated KCl). The linear detection range for NIC oxidation on the so-called ITO/TiO{sub 2}[NIC]/PEDOT electrode was 0-5 mM, with a sensitivity and limit of detection of 31.35 {mu}A mM{sup -1} cm{sup -2} and 4.9 {mu}M, respectively. When comparing with the performance of the non-imprinted one, the sensitivity ratio was about 1.24. The sensitivity enhancement was attributed to the increase in the electroactive area of the imprinted electrode. The at-rest stability of the ITO/TiO{sub 2}[NIC]/PEDOT electrode was tested over a period of 3 days. The current response remained about 85% of its initial value at the end of 2 days. The ITO/TiO{sub 2}[NIC]/PEDOT electrode showed reasonably good selectivity in distinguishing NIC from its major interferent, (-)-cotinine (COT). Moreover, scanning electrochemical microscopy (SECM) was employed to elucidate the surface morphology of the imprinted and non-imprinted electrodes using Fe(CN){sub 6}{sup 3-}/Fe(CN){sub 6}{sup 4-} as a redox probe on a platinum tip. The imprinted electrode was further characterized by scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR)

  15. Surface Structure and Photocatalytic Activity of Nano-TiO2 Thin Film

    Science.gov (United States)

    Controlled titanium dioxide (TiO2) thin films were deposited on stainless steel surfaces using flame aerosol synthetic technique, which is a one-step coating process, that doesn’t require further calcination. Solid state characterization of the coatings was conducted by different...

  16. ALD TiO2 thin film as dielectric for Al/p-Si Schottky diode

    Indian Academy of Sciences (India)

    Abstract. Electrical analysis of Al/p-Si Schottky diode with titanium dioxide (TiO2) thin film was performed at ..... This work was partially supported by The Management Unit of Scientific Research Project of Bozok University and Hitit. University.

  17. Polarization retention loss in PbTiO3 ferroelectric films due to leakage currents

    NARCIS (Netherlands)

    Morelli, A.; Venkatesan, Sriram; Palasantzas, G.; Kooi, B. J.; De Hosson, J. Th. M.

    2007-01-01

    The relationship between retention loss in single crystal PbTiO3 ferroelectric thin films and leakage currents is demonstrated by piezoresponse and conductive atomic force microscopy measurements. It was found that the polarization reversal in the absence of an electric field followed a stretched

  18. Nanocrystalline Pt-doped TiO2 thin films prepared by spray pyrolysis ...

    Indian Academy of Sciences (India)

    Administrator

    Spray pyrolysis techniques; TiO2 thin films; hydrogen gas response. 1. Introduction ... tion is necessary during the production, storage and use of hydrogen. It is also ..... ient, and 'green': it may be used to large scale industrial application for ...

  19. Dynamic nonlinearity in epitaxial BaTiO.sub.3./sub. films

    Czech Academy of Sciences Publication Activity Database

    Tyunina, Marina; Savinov, Maxim

    2016-01-01

    Roč. 94, č. 5 (2016), 1-6, č. článku 054109. ISSN 2469-9950 R&D Projects: GA ČR GA15-15123S Institutional support: RVO:68378271 Keywords : dynamic nonlinearity * epitaxial * BaTiO 3 films Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.836, year: 2016

  20. Synthesis of nanocrystalline TiO 2 thin films by liquid phase ...

    Indian Academy of Sciences (India)

    A transparent, high purity titanium dioxide thin film composed of densely packed nanometer sized grains has been successfully deposited on a glass substrate at 30°C from an aqueous solution of TiO2–HF with the addition of boric acid as a scavenger by liquid phase deposition technique. From X-ray diffraction ...

  1. Performance of Erbium-doped TiO2 thin film grown by physical vapor deposition technique

    Science.gov (United States)

    Lahiri, Rini; Ghosh, Anupam; Dwivedi, Shyam Murli Manohar Dhar; Chakrabartty, Shubhro; Chinnamuthu, P.; Mondal, Aniruddha

    2017-09-01

    Undoped and Erbium-doped TiO2 thin films (Er:TiO2 TFs) were fabricated on the n-type Si substrate using physical vapour deposition technique. Field emission scanning electron microscope showed the morphological change in the structure of Er:TiO2 TF as compared to undoped sample. Energy dispersive X-ray spectroscopy (EDX) confirmed the Er doping in the TiO2 thin film (TF). The XRD and Raman spectrum showed the presence of anatase phase TiO2 and Er2O3 in the Er:TiO2 TF. The Raman scattering depicted additional number of vibrational modes for Er:TiO2 TF due to the presence of Er as compared to the undoped TiO2 TF. The UV-Vis absorption measurement showed that Er:TiO2 TF had approximately 1.2 times more absorption over the undoped TiO2 TF in the range of 300-400 nm. The main band transition, i.e., the transition between the oxygen (2p) state and the Ti (3d) state was obtained at 3.0 eV for undoped TiO2 and at 3.2 eV for Er:TiO2 TF, respectively. The photo responsivity measurement was done on both the detectors, where Er:TiO2 TF detector showed better detectivity ( D *), noise equivalent power and temporal response as compared to undoped detector under ultra-violet illumination.

  2. Morphological study of electrophoretically deposited TiO2 film for DSSC application

    Science.gov (United States)

    Patel, Alkesh B.; Patel, K. D.; Soni, S. S.; Sonigara, K. K.

    2018-05-01

    In the immerging field of eco-friendly and low cost photovoltaic devices, dye sensitized solar cell (DSSC) [1] has been investigated as promising alternative to the conventional silicon-based solar cells. In the DSSC device, photoanode is crucial component that take charge of holding sensitizer on it and inject the electrons from the sensitizer to current collector. Nanoporous TiO2 is the most relevant candidate for the preparation of photoanode in DSSCs. Surface properties, morphology, porosity and thickness of TiO2 film as well as preparation technique determine the performance of device. In the present work we have report the study of an effect of nanoporous anatase titanium dioxide (TiO2) film thickness on DSSC performance. Photoanode TiO2 (P25) film was deposited on conducting substrate by electrophoresis technique (EPD) and film thickness was controlled during deposition by applying different current density for a constant time interval. Thickness and surface morphology of prepared films was studied by SEM and transmittance analysis. The same set of photoanode was utilized in DSSC devices using metal free organic dye sensitizer to evaluate the photovoltaic performance. Devices were characterized through Current-Voltage (I-V) characteristic, electrochemical impedance spectroscopy (EIS) and open circuit voltage decay curves. Dependency of device performance corresponding to TiO2 film thickness is investigated through the lifetime kinetics of electron charge transfer mechanism trough impedance fitting. It is concluded that appropriate thickness along with uniformity and porosity are required to align the dye molecules to respond efficiently the incident light photons.

  3. Low Loss Sol-Gel TiO2 Thin Films for Waveguiding Applications

    Directory of Open Access Journals (Sweden)

    Alexis Fischer

    2013-03-01

    Full Text Available TiO2 thin films were synthesized by sol-gel process: titanium tetraisopropoxide (TTIP was dissolved in isopropanol, and then hydrolyzed by adding a water/isopropanol mixture with a controlled hydrolysis ratio. The as prepared sol was deposited by “dip-coating” on a glass substrate with a controlled withdrawal speed. The obtained films were annealed at 350 and 500 °C (2 h. The morphological properties of the prepared films were analyzed by Scanning Electron Microscopy (SEM and Atomic Force Microscopy (AFM. The optical waveguiding properties of TiO2 films were investigated for both annealing temperature using m-lines spectroscopy. The refractive indices and the film thickness were determined from the measured effective indices. The results show that the synthesized planar waveguides are multimodes and demonstrate low propagation losses of 0.5 and 0.8 dB/cm for annealing temperature 350 and 500 °C, respectively.

  4. Photocatalytic sterilization of TiO2 films coated on Al fiber

    International Nuclear Information System (INIS)

    Luo Li; Miao Lei; Tanemura, Sakae; Tanemura, Masaki

    2008-01-01

    Photocatalytic TiO 2 films were coated on Al fiber by sol-gel dip-coating method, and then annealed. The crystal structure and morphology of the films were performed by XRD, TEM and SEM. Photocatalytic sterilization of the films was investigated in O 2 atmosphere through purifying the aqueous solution with facultative aerobe (Bacillus cereus), aerobe (Pseudomonas aeruginosa) and anaerobe (Staphylococcus aureus, Enterococcus faecalis and Escherichia coli). In the presence of O 2 , it benefits to generate O 2 · - and ·OH at the first stage of the photocatalytic reaction, while the excess O 2 restrains the anaerobe from reproducing and accelerates the reproducing for the aerobe at the second stage of reaction. As a result, it was found that the crystal of TiO 2 films is anatase phase and the films have excellent sterilization effect against facultative aerobe and anaerobe. Nevertheless, it only decreased the bioactivity against aerobe in a short time

  5. Surface modification of porous nanocrystalline TiO2 films for dye-sensitized solar cell application by various gas plasmas

    International Nuclear Information System (INIS)

    Kim, Youngsoo; Yoon, Chang-Ho; Kim, Kang-Jin; Lee, Yeonhee

    2007-01-01

    Titanium dioxide (TiO 2 ) film for dye-sensitized solar cells (DSSCs) has surface defects such as oxygen vacancies created during the annealing process. The authors used a plasma treatment technique to reduce defects on TiO 2 surfaces. They investigated the influence of different gas plasma treatments of TiO 2 film on the photoelectric performance of DSSC. Short-circuit photocurrent density (J sc ), open-circuit photovoltage (V oc ), and the amount of adsorbed dye for DSSCs were measured. As a result, the solar-to-electricity conversion efficiencies of the O 2 - and N 2 -treated cells increased by 15%-20% compared to untreated cells. On the other hand, solar energy conversion efficiency of CF 4 -plasma treated cells decreased drastically. The increased amount of adsorbed dye on the TiO 2 film was measured by time-of-flight secondary ion mass spectrometry. TiO 2 surfaces modified by plasma treatment were characterized using analytical instruments such as x-ray photoelectron spectroscopy and near-edge x-ray absorption fine structure

  6. Structural study of TiO2-based transparent conducting films

    International Nuclear Information System (INIS)

    Hitosugi, T.; Yamada, N.; Nakao, S.; Hatabayashi, K.; Shimada, T.; Hasegawa, T.

    2008-01-01

    We have investigated microscopic structures of sputter and pulsed laser deposited (PLD) anatase Nb-doped TiO 2 transparent conducting films, and discuss what causes the degradation of resistivity in sputter-deposited films. Cross-sectional transmission electron microscope and polarized optical microscope images show inhomogeneous intragrain structures and small grains of ∼10 μm in sputter-deposited films. From comparison with PLD films, these results suggest that homogeneous film growth is the important factor to obtain highly conducting sputter-deposited film

  7. Photodegradative properties of TiO{sub 2} films prepared by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Justicia, I.; Ayllon, J.A.; Figueras, A. [Consejo Superior de Investigaciones Cientificas, Barcelona (Spain). Inst. de Ciencia de Materiales; Battiston, G.A.; Gerbasi, R. [Consejo Superior de Investigaciones Cientificas, Barcelona (Spain). Inst. de Ciencia de Materiales; Ist. di Chimica e Tecnologie Inorganiche e dei Materiali Avanzati del CNR, Padova (Italy)

    2001-08-01

    TiO{sub 2} is a well-known photocatalyst for the air-oxydation of organic compounds. This paper deals with the preparation of TiO{sub 2} layers by MOCVD. The photodegradation rate has been studied in the presence of aqueous suspensions (methylene blue) as a function of the film thickness, roughness and crystallite preferred orientation. These results are compared with aqueous suspensions of Degussa P-25 powders. Deposits obtained on fused quartz showed a higher photodegradation rate than those prepared on glass, while Degussa powders exhibited an intermediate value. (orig.)

  8. Nanoimprinted distributed feedback lasers comprising TiO2 thin films

    DEFF Research Database (Denmark)

    Vannahme, Christoph; Smith, Cameron; Leung, Michael C.

    2013-01-01

    Design guidelines for optimizing the sensing performance of nanoimprinted second order distributed feedback dye lasers are presented. The guidelines are verified by experiments and simulations. The lasers, fabricated by UV-nanoimprint lithography into Pyrromethene doped Ormocomp thin films on glass......, have their sensor sensitivity enhanced by a factor of up to five via the evaporation of a titanium dioxide (TiO2) waveguiding layer. The influence of the TiO2 layer thickness on the device sensitivity is analyzed with a simple model that accurately predicts experimentally measured wavelength shifts...

  9. Low-temperature sputtering of crystalline TiO2 films

    International Nuclear Information System (INIS)

    Musil, J.; Herman, D.; Sicha, J.

    2006-01-01

    This article reports on the investigation of reactive magnetron sputtering of transparent, crystalline titanium dioxide films. The aim of this investigation is to determine a minimum substrate surface temperature T surf necessary to form crystalline TiO 2 films with anatase structure. Films were prepared by dc pulsed reactive magnetron sputtering using a dual magnetron operating in bipolar mode and equipped with Ti(99.5) and ceramic Ti 5 O 9 targets. The films were deposited on unheated glass substrates and their structure was characterized by x-ray diffraction and surface morphology by atomic force microscopy. Special attention is devoted to the measurement of T surf using thermostrips pasted to the glass substrate. It was found that (1) T surf is considerably higher (approximately by 100 deg. C or more) than the substrate temperature T s measured by the thermocouple incorporated into the substrate holder and (2) T surf strongly depends on the substrate-to-target distance d s-t , the magnetron target power loading, and the thermal conductivity of the target and its cooling. The main result of this study is the finding that (1) the crystallization of sputtered TiO 2 films depends not only on T surf but also on the total pressure p T of sputtering gas (Ar+O 2 ), partial pressure of oxygen p O 2 , the film deposition rate a D , and the film thickness h (2) crystalline TiO 2 films with well developed anatase structure can be formed at T surf =160 deg. C and low values of a D ≅5 nm/min (3) the crystalline structure of TiO 2 film gradually changes from (i) anatase through (ii) anatase+rutile mixture, and (iii) pure rutile to x-ray amorphous structure at T surf =160 deg. C and p T =0.75 Pa when p O 2 decreases and a D increases above 5 nm/min, and (4) crystallinity of the TiO 2 films decreases with decreasing h and T surf . Interrelationships between the structure of TiO 2 film, its roughness, T surf , and a D are discussed in detail. Trends of next development are

  10. Enhanced Magnetization of Cobalt Defect Clusters Embedded in TiO_2_-_δ Films

    International Nuclear Information System (INIS)

    Cortie, David L.; Khaydukov, Yury; Max Planck Society, Garching

    2017-01-01

    High magnetizations are desirable for spintronic devices that operate by manipulating electronic states using built-in magnetic fields. However, the magnetic moment in promising dilute magnetic oxide nanocomposites is very low, typically corresponding to only fractions of a Bohr magneton for each dopant atom. In this study, we report a large magnetization formed by ion implantation of Co into amorphous TiO_2_-_δ films, producing an inhomogeneous magnetic moment, with certain regions producing over 2.5 μ_B per Co, depending on the local dopant concentration. Polarized neutron reflectometry was used to depth-profile the magnetization in the Co:TiO_2_-_δ nanocomposites, thus confirming the pivotal role of the cobalt dopant profile inside the titania layer. X-ray photoemission spectra demonstrate the dominant electronic state of the implanted species is Co"0, with a minor fraction of Co"2"+. The detected magnetizations have seldom been reported before and lie near the upper limit set by Hund’s rules for Co"0, which is unusual because the transition metal’s magnetic moment is usually reduced in a symmetric 3D crystal-field environment. Low-energy positron annihilation lifetime spectroscopy indicates that defect structures within the titania layer are strongly modified by the implanted Co. We propose that a clustering motif is promoted by the affinity of the positively charged implanted species to occupy microvoids native to the amorphous host. This provides a seed for subsequent doping and nucleation of nanoclusters within an unusual local environment.

  11. Photolithographically Patterned TiO2 Films for Electrolyte-Gated Transistors.

    Science.gov (United States)

    Valitova, Irina; Kumar, Prajwal; Meng, Xiang; Soavi, Francesca; Santato, Clara; Cicoira, Fabio

    2016-06-15

    Metal oxides constitute a class of materials whose properties cover the entire range from insulators to semiconductors to metals. Most metal oxides are abundant and accessible at moderate cost. Metal oxides are widely investigated as channel materials in transistors, including electrolyte-gated transistors, where the charge carrier density can be modulated by orders of magnitude upon application of relatively low electrical bias (2 V). Electrolyte gating offers the opportunity to envisage new applications in flexible and printed electronics as well as to improve our current understanding of fundamental processes in electronic materials, e.g. insulator/metal transitions. In this work, we employ photolithographically patterned TiO2 films as channels for electrolyte-gated transistors. TiO2 stands out for its biocompatibility and wide use in sensing, electrochromics, photovoltaics and photocatalysis. We fabricated TiO2 electrolyte-gated transistors using an original unconventional parylene-based patterning technique. By using a combination of electrochemical and charge carrier transport measurements we demonstrated that patterning improves the performance of electrolyte-gated TiO2 transistors with respect to their unpatterned counterparts. Patterned electrolyte-gated (EG) TiO2 transistors show threshold voltages of about 0.9 V, ON/OFF ratios as high as 1 × 10(5), and electron mobility above 1 cm(2)/(V s).

  12. Visible photoenhanced current-voltage characteristics of Au : TiO2 nanocomposite thin films as photoanodes

    International Nuclear Information System (INIS)

    Naseri, N; Amiri, M; Moshfegh, A Z

    2010-01-01

    In this investigation, the effect of annealing temperature and concentration of gold nanoparticles on the photoelectrochemical properties of sol-gel deposited Au : TiO 2 nanocomposite thin films is studied. Various gold concentrations have been added to the TiO 2 thin films and their properties are compared. All the deposited samples are annealed at different temperatures. The optical density spectra of the films show the formation of gold nanoparticles in the films. The optical bandgap energy of the Au : TiO 2 films decreases with increasing Au concentration. The crystalline structure of the nanocomposite films is studied by x-ray diffractometry indicating the formation of gold nanocrystals in the anatase TiO 2 nanocrystalline thin films. X-ray photoelectron spectroscopy reveals that the presence of gold in the metallic state and the formation of TiO 2 are stoichiometric. The photoelectrochemical properties of the Au : TiO 2 samples are characterized using a compartment cell containing H 2 SO 4 and KOH as cathodic and anodic electrolytes, respectively. It is found that the addition of Au nanoparticles in TiO 2 films enhances the photoresponse of the layer and the addition of gold nanocrystals with an optimum value of 5 mol% resulted in the highest photoelectrochemical activity. Moreover, the photoresponse of the samples is also enhanced with an increase in the annealing temperature.

  13. Electrochemical fabrication of TiO2 nanoparticles/[BMIM]BF4 ionic liquid hybrid film electrode and its application in determination of p-acetaminophen

    International Nuclear Information System (INIS)

    Wang, Bin; Li, Yuan; Qin, Xianjing; Zhan, Guoqing; Ma, Ming; Li, Chunya

    2012-01-01

    A water soluble ionic liquid, 1‐butyl‐3‐methylimidazolium tetrafluoroborate ([BMIM]BF 4 ), was incorporated into TiO 2 nanoparticles to fabricate a hybrid film modified glassy carbon electrode (nano‐TiO 2 /[BMIM]BF 4 /GCE) through electrochemical deposition in a tetrabutyltitanate sol solution containing [BMIM]BF 4 . The obtained nano‐TiO 2 /[BMIM]BF 4 /GCEs were characterized scanning electronic microscopy (SEM) and X‐ray photoelectron spectroscopy (XPS). Electrochemical behaviors of p‐acetaminophen at the nano‐TiO 2 /[BMIM]BF 4 /GCEs were thoroughly investigated. Compared to the redox reaction of p‐acetaminophen using an unmodified electrode under the same conditions, a new reduction peak was observed clearly at 0.26 V with the modified electrode. In addition, the peak potential for the oxidation of p‐acetaminophen was found to shift negatively about 90 mV and the current response increased significantly. These changes indicate that the nano‐TiO 2 /[BMIM]BF 4 hybrid film can improve the redox reactions of p‐acetaminophen in aqueous medium. Under optimum conditions, a linear relationship was obtained for the p‐acetaminophen solutions with concentration in the range from 5.0 × 10 −8 to 5.0 × 10 −5 M. The estimated detection limit was 1.0 × 10 −8 M (S/N = 3). The newly developed method was applied for the determination of p-acetaminophen in urine samples. - Highlights: ► Nano-TiO 2 /[BMIM]BF 4 hybrid film electrode was fabricated with electrodeposition. ► Voltammetric behavior of p-acetaminophen at the obtained electrode was investigated. ► The hybrid film electrode shows good electrocatalytic response to p-acetaminophen. ► p-acetaminophen in urine samples was successfully determined.

  14. Highly efficient photoelectrochemical performance of SrTiO{sub 3}/TiO{sub 2} heterojunction nanotube array thin film

    Energy Technology Data Exchange (ETDEWEB)

    Zhang Yan [Qingdao University, School of Chemistry, Chemical Engineering and Environments (China); Bu Yuyu [Chinese Academy of Sciences, National Engineering Center of Marine Corrosion Protection, Institute of Oceanology (China); Yu Jianqiang, E-mail: yjq@licp.cas.cn; Li Ping [Qingdao University, School of Chemistry, Chemical Engineering and Environments (China)

    2013-06-15

    SrTiO{sub 3}-TiO{sub 2} heterojunction thin-film nanotube arrays (SNTs, the average inner diameter is about 50 nm) was fabricated via electrochemical anodization followed by a hydrothermal treatment. The photo-to-current conversion properties and the photoelectrochemical performance for cathodic protection of carbon steel in 0.5 M of sodium chloride solution under white light illumination were investigated. The results showed that the highly ordered nanotube arrays could provide very excellent cathodic protection for carbon steel under white light irradiation.

  15. Characterization of dispersion of a nano composites PP/TiO2 non modified

    International Nuclear Information System (INIS)

    Soares, Igor L.; Tavares, Maria I.B.; Silva, Vanessa A. da; Legramanti, Cintia; Luetkmeyer, Leandro

    2011-01-01

    Polymeric nano composites are composite materials where an inorganic particle, which has a dimension in the nanometer range, is dispersed in a polymer matrix. Nano composites, using polypropylene (PP) as matrix polymer and titanium dioxide (TiO 2 ) as filler, have great versatility in marketing applications, this factor is inherent in the PP and the inherent ability photo degraded TiO 2 particles. This combination can lead to a widely used material and a degradation time after discharge reduced, there by becoming, a residue of low environmental impact. This study aimed to evaluate the dispersion and particle distribution of TiO 2 , non modified, in PP matrix, using the process of preparation by melt extrusion pathway and characterization of the materials obtained: on the molecular dynamics, using low field NMR solid state, measures the relaxation time spin-network (T 1 H); morphology using XRD technique, and thermal analysis technique with the TGA of pure PP and nano composites PP/TiO 2 . (author)

  16. Synthesis of photosensitive nanograined TiO2 thin films by SILAR method

    International Nuclear Information System (INIS)

    Patil, U.M.; Gurav, K.V.; Joo, Oh-Shim; Lokhande, C.D.

    2009-01-01

    Nanocrystalline TiO 2 thin films are deposited by simple successive ionic layer adsorption and reaction (SILAR) method on glass and fluorine-doped tin oxide (FTO)-coated glass substrate from aqueous solution. The as-deposited films are heat treated at 673 K for 2 h in air. The change in structural, morphological and optical properties are studied by means of X-ray diffraction (XRD), selected area electron diffraction (SAED), scanning electron microscopy (SEM), Fourier transform infrared (FTIR), transmission electron microscopy (TEM) and UV-vis-NIR spectrophotometer. The results show that the SILAR method allows the formation of anatase, nanocrystalline, and porous TiO 2 thin films. The heat-treated film showed conversion efficiency of 0.047% in photoelectrochemical cell with 1 M NaOH electrolyte.

  17. Oxygen tracer studies of ferroelectric fatigue in Pb(Zr,Ti)O3 thin films

    International Nuclear Information System (INIS)

    Schloss, Lawrence F.; McIntyre, Paul C.; Hendrix, Bryan C.; Bilodeau, Steven M.; Roeder, Jeffrey F.; Gilbert, Stephen R.

    2002-01-01

    Long-range oxygen motion has been observed in Pt/Pb(Zr,Ti)O 3 /Ir thin-film structures after electrical fatigue cycling at room temperature. Through an exchange anneal, isotopic 18 O was incorporated as a tracer into bare Pb(Zr,Ti)O 3 (PZT) films, allowing secondary ion mass spectrometry measurements of the tracer profile evolution as a function of the number of polarization reversals. Observation of 18 O tracer redistribution during voltage cycling, which is presumably mediated by oxygen vacancy motion, was found to be strongly dependent upon the thermal history of the film. However, there was no strong correlation between the extent of 18 O tracer redistribution and the extent of polarization suppression induced by voltage cycling. Our results suggest that oxygen vacancy motion plays, at most, a secondary role in ferroelectric fatigue of PZT thin films

  18. Nano structured TiO2 thin films by polymeric precursor method

    International Nuclear Information System (INIS)

    Stroppa, Daniel Grando; Giraldi, Tania Regina; Leite, Edson Roberto; Varela, Jose Arana; Longo, Elson

    2008-01-01

    This work focuses in optimizing setup for obtaining TiO 2 thin films by polymeric precursor route due to its advantages on stoichiometric and morphological control. Precursor stoichiometry, synthesis pH, solids concentration and rotation speed at deposition were optimized evaluating thin films morphology and thickness. Thermogravimetry and NMR were applied for precursor's characterization and AFM, XRD and ellipsometry for thin films evaluation. Results showed successful attainment of homogeneous nanocrystalline anatase TiO 2 thin films with outstanding control over morphological characteristics, mean grain size of 17 nm, packing densities between 57 and 75%, estimated surface areas of 90 m 2 /g and monolayers thickness within 20 and 128 nm. (author)

  19. Preparation and characterization of TiO[sub 2]/Sb thin films for solar energy applications

    Energy Technology Data Exchange (ETDEWEB)

    Badawy, W.A. (Dept. of Chemistry, Cairo Univ., Giza (Egypt))

    1993-01-01

    Pure and antimony-incorporated TiO[sub 2] thin films were prepared using a spray-CVD method. The method allows for convenient incorporation of foreign atoms into the oxide matrix during film growth. The foreign atoms in the oxide film affects both the photovoltaic and photoelectrochemical properties of the n-Si/oxide heterojunction. The characteristics of the prepared oxide films were affected significantly by the presence of antimony on the oxide matrix. The increased conductivity of the Sb-containing oxide layers is reflected in the improved photovoltaic properties of the prepared n-Si/TiO[sub 2]-Sb heterojunctions, e.g. fill factor and solar conversion efficiency. The photoelectrochemical properties of the prepared devices revealed that the charge transfer step at the oxide/electrolyte interface leads to a deterioration of the cell quality. However, this drawback has been offset by the improved properties of the heterojunction. (orig.)

  20. Study of the structural and electrical behavior of Bi(Mg,TiO3 modified (Ba,CaTiO3 ceramics

    Directory of Open Access Journals (Sweden)

    Md. Kashif Shamim

    2016-12-01

    Full Text Available The ability of BaTiO3 to form solid solutions with different dopants (both iso- and aliovalent makes it versatile for various applications. In the present study, (Ba,CaTiO3 (BCT is modified with Bi(MgTiO3 (BMT in search for new lead-free ferroelectric material and improve their properties. For this purpose, BCT acts as a main base material and BMT acts as a modifier to fabricate a multifunctional material. In this study, we report the structural and electrical properties of lead free piezo-ceramics (1−x(Ba0.8Ca0.2TiO3–xBi(Mg0.5Ti0.5O3 with x=0.2, 0.4, 0.5 prepared by solid-state sintering technique. Single perovskite phase with tetragonal structure is obtained for all the compositions, which is reconfirmed by the Raman Spectroscopic study. Dielectric study confirm the temperature stable behavior of the dielectric permittivity values above 300∘C. The dielectric constant value decreases with increase in BMT doping content. Impedance Spectroscopic study confirms non-Debye type dielectric relaxation in the specimen. The Nyquist plot and conductivity studies show the negative temperature coefficient of resistance behavior (NTCR of the samples.

  1. Ag2S/CdS/TiO2 Nanotube Array Films with High Photocurrent Density by Spotting Sample Method.

    Science.gov (United States)

    Sun, Hong; Zhao, Peini; Zhang, Fanjun; Liu, Yuliang; Hao, Jingcheng

    2015-12-01

    Ag2S/CdS/TiO2 hybrid nanotube array films (Ag2S/CdS/TNTs) were prepared by selectively depositing a narrow-gap semiconductor-Ag2S (0.9 eV) quantum dots (QDs)-in the local domain of the CdS/TiO2 nanotube array films by spotting sample method (SSM). The improvement of sunlight absorption ability and photocurrent density of titanium dioxide (TiO2) nanotube array films (TNTs) which were obtained by anodic oxidation method was realized because of modifying semiconductor QDs. The CdS/TNTs, Ag2S/TNTs, and Ag2S/CdS/TNTs fabricated by uniformly depositing the QDs into the TNTs via the successive ionic layer adsorption and reaction (SILAR) method were synthesized, respectively. The X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectrum (XPS) results demonstrated that the Ag2S/CdS/TNTs prepared by SSM and other films were successfully prepared. In comparison with the four films of TNTs, CdS/TNTs, Ag2S/TNTs, and Ag2S/CdS/TNTs by SILAR, the Ag2S/CdS/TNTs prepared by SSM showed much better absorption capability and the highest photocurrent density in UV-vis range (320~800 nm). The cycles of local deposition have great influence on their photoelectric properties. The photocurrent density of Ag2S/CdS/TNTs by SSM with optimum deposition cycles of 6 was about 37 times that of TNTs without modification, demonstrating their great prospective applications in solar energy utilization fields.

  2. Structural and electrical characteristics of ZrO2-TiO2 thin films by sol-gel method

    International Nuclear Information System (INIS)

    Hsu, Cheng-Hsing; Tseng, Ching-Fang; Lai, Chun-Hung; Tung, Hsin-Han; Lin, Shih-Yao

    2010-01-01

    In this paper, we investigated electrical properties and microstructures of ZrTiO 4 (ZrO 2 -TiO 2 ) thin films prepared by the sol-gel method on ITO substrates at different annealing temperatures. All films exhibited ZrTiO 4 (1 1 1) and (1 0 1) orientations perpendicular to the substrate surface, and the grain size increased with increase in the annealing temperature. A low leakage current density of 2.06 x 10 -6 A/cm 2 was obtained for the prepared films. Considering the primary memory switching behavior of ZrTiO 4 , ReRAM based on ZrTiO 4 shows promise for future nonvolatile memory applications.

  3. Magnetic and ferroelectric properties of Fe doped SrTiO{sub 3-{delta}} films

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, A Sendil; Suresh, P; Srinath, S [School of Physics, University of Hyderabad, Hyderabad, 500 046 (India); Kumar, M Mahesh; Post, M L [Institute for Chemical Process and Environmental Technology, National Research Council of Canada, Ottawa, ON, K1A 0R6 (Canada); Srikanth, H [Materials Physics Laboratory, Department of Physics, University of South Florida, Tampa, Florida, 33620 (United States); Sahner, Kathy; Moos, Ralf, E-mail: sssp@uohyd.ernet.i [Functional Materials, University of Bayreuth, 95447, Bayreuth (Germany)

    2010-01-01

    Recent interest in SrTiO{sub 3} stems from its wide applicability in microwave devices based on the tunable characteristics of dielectric constant in the microwave frequency range. It is obvious that for any such application, SrTiO{sub 3} should have a ferroelectric Curie temperature (T{sub C}) close to room temperature or higher. By inducing strains by chemical substitutions, it was possible to obtain T{sub C} as high as 200{sup 0}C in SrTiO{sub 3} modified with Fe{sup 4+}. Hysteresis loops obtained confirms the presence of ferroelectric domains. Two apparent transitions, one at {approx}200 {sup 0}C and another {approx}300 {sup 0}C were seen in {epsilon}', which are replicated as sharp drops in resistivity curves. These temperatures far exceed the T{sub C}s reported in the literature till now and could open new avenues for innumerable other applications for SrTiO{sub 3}. The magnetic properties of Fe doped SrTiO{sub 3} are also investigated. Low doping of Fe exhibits simple antiferromagnetic behaviour.

  4. Multiphase nanodomains in a strained BaTiO3 film on a GdScO3 substrate

    Science.gov (United States)

    Kobayashi, Shunsuke; Inoue, Kazutoshi; Kato, Takeharu; Ikuhara, Yuichi; Yamamoto, Takahisa

    2018-02-01

    Controlling the crystal structure of ferroelectric materials via epitaxial strain, which is a well-known technique in strain engineering, can lead to the formation of unique domain structures generating non-intrinsic phenomena such as electronic conductivity, photovoltages, and enhanced piezoelectric characteristics. Strained BaTiO3 films are promising ferroelectric materials as theoretical modeling predicts that different domain morphologies can introduce additional properties not observed in conventional BaTiO3 ceramics. To rationally design materials for practical application, a thorough understanding of the formation mechanisms and stabilities of different domain structures in strained BaTiO3 films is required. However, there have been very few experimental reports on this topic, and details about the domain structures in strained BaTiO3 films are currently lacking. In this paper, we report multiphase nanodomains in a strained BaTiO3 film deposited on an orthorhombic GdScO3 substrate. The phase-transition behavior of the strained BaTiO3 film reveals that it contains multiple phases at room temperature; the film first undergoes a phase-transition upon heating at around 550 K, and then a paraelectric phase forms at temperatures above 690 K. A picometer-scale analysis of the Ti ion displacements, using an advanced scanning transmission electron microscopy technique, is used to characterize the complex multiphase nanodomains, providing useful insights into the control of domain structures in BaTiO3 films by applying epitaxial strain.

  5. High-Quality Fe-doped TiO2 films with Superior Visible-Light Performance

    DEFF Research Database (Denmark)

    Su, Ren; Bechstein, Ralf; Kibsgaard, Jakob

    2012-01-01

    We report on high-quality polycrystalline Fe-doped TiO2 (Fe–TiO2) porous films synthesized via one-step electrochemical oxidation. We demonstrate that delicate properties such as the impurity concentration and the microstructure that strongly influence the performance of the material for photovol...

  6. Photocathodic Protection of 304 Stainless Steel by Bi2S3/TiO2 Nanotube Films Under Visible Light.

    Science.gov (United States)

    Li, Hong; Wang, Xiutong; Wei, Qinyi; Hou, Baorong

    2017-12-01

    We report the preparation of TiO 2 nanotubes coupled with a narrow bandgap semiconductor, i.e., Bi 2 S 3 , to improve the photocathodic protection property of TiO 2 for metals under visible light. Bi 2 S 3 /TiO 2 nanotube films were successfully synthesized using the successive ionic layer adsorption and reaction (SILAR) method. The morphology and structure of the composite films were studied by scanning electron microscopy and X-ray diffraction, respectively. UV-visible diffuse reflectance spectra were recorded to analyze the optical absorption property of the composite films. In addition, the influence of Bi 2 S 3 deposition cycles on the photoelectrochemical and photocathodic protection properties of the composite films was also studied. Results revealed that the heterostructure comprised crystalline anatase TiO 2 and orthorhombic Bi 2 S 3 and exhibited a high visible light response. The photocurrent density of Bi 2 S 3 /TiO 2 was significantly higher than that of pure TiO 2 under visible light. The sensitization of Bi 2 S 3 enhanced the separation efficiency of the photogenerated charges and photocathodic protection properties of TiO 2 . The Bi 2 S 3 /TiO 2 nanotubes prepared by SILAR deposition with 20 cycles exhibited the optimal photogenerated cathodic protection performance on the 304 stainless steel under visible light.

  7. Photocathodic Protection of 304 Stainless Steel by Bi2S3/TiO2 Nanotube Films Under Visible Light

    Science.gov (United States)

    Li, Hong; Wang, Xiutong; Wei, Qinyi; Hou, Baorong

    2017-01-01

    We report the preparation of TiO2 nanotubes coupled with a narrow bandgap semiconductor, i.e., Bi2S3, to improve the photocathodic protection property of TiO2 for metals under visible light. Bi2S3/TiO2 nanotube films were successfully synthesized using the successive ionic layer adsorption and reaction (SILAR) method. The morphology and structure of the composite films were studied by scanning electron microscopy and X-ray diffraction, respectively. UV-visible diffuse reflectance spectra were recorded to analyze the optical absorption property of the composite films. In addition, the influence of Bi2S3 deposition cycles on the photoelectrochemical and photocathodic protection properties of the composite films was also studied. Results revealed that the heterostructure comprised crystalline anatase TiO2 and orthorhombic Bi2S3 and exhibited a high visible light response. The photocurrent density of Bi2S3/TiO2 was significantly higher than that of pure TiO2 under visible light. The sensitization of Bi2S3 enhanced the separation efficiency of the photogenerated charges and photocathodic protection properties of TiO2. The Bi2S3/TiO2 nanotubes prepared by SILAR deposition with 20 cycles exhibited the optimal photogenerated cathodic protection performance on the 304 stainless steel under visible light.

  8. Study on plasma pre-functionalized PVC film grafted with TiO2/PVP to improve blood compatible and antibacterial properties

    International Nuclear Information System (INIS)

    Suganya, Arjunan; Shanmugavelayutham, Gurusamy; Rodríguez, Carmen Serra

    2017-01-01

    Research into the design of new biopolymers/polymer functionalized with nanoparticles is of tremendous interest to the medical sector, particularly with regard to blood-contacting devices. In this present study, a steady blood compatible and active antibacterial coating was fabricated by the grafting of titanium dioxide (TiO 2 )/polyvinylpyyrolidone (PVP) onto a polyvinyl chloride (PVC) film surface via the direct-current glow discharge plasma method. To enhance the chemical interaction between TiO 2 /PVP and PVC, the surfaces of the PVC films were functionalized by different plasmas (air, argon, and oxygen) before coating. In this study, the plasma parameters were varied, such as treatment time of about 5–20 min for a constant power of 100 W, potential 300 V, and a constant gas pressure of 2 Pa for air, argon, and oxygen gas environment. Then, the different plasma treatments on the PVC films, TiO 2 /PVP were grafted using a simple dip-coating method. In addition, the TiO 2 /PVP-grafted PVC films were characterized by contact angle, attenuated total reflectance Fourier transform infrared spectroscopy, field-emission scanning electron microscope, and x-ray photo electron spectroscopy. Importantly, TiO 2 /PVP is grafted onto the PVC surface due to the plasma-based retained functionality and demonstrates adhesive efficiency, which was observed by XPS. The bio-stability of the TiO 2 /PVP-modified PVC film was evaluated by in vitro platelet activation analysis and protein adsorption analysis. Then, the antibacterial properties were evaluated by the agar diffusion method against Escherichia coli . The result reveals that the grafting of TiO 2 /PVP was slightly higher for the 15 min oxygen plasma-functionalized PVC, which significantly decreases the platelet adhesion and protein adsorption. Moreover, the antibacterial properties of the 15 min oxygen plasma-functionalized PVC with TiO 2 /PVP-grafted film is also greatly improved compared with an air- and argon

  9. Reactive Coevaporation Synthesis and Characterization of SrTiO3 Thin Films

    Science.gov (United States)

    Yamaguchi, Hiromu; Matsubara, Shogo; Miyasaka, Yoichi

    1991-09-01

    SrTiO3 thin films were prepared by the reactive coevaporation method, where the Ti and Sr metals were evaporated in oxygen ambient with an E-gun and K-cell, respectively. A uniform depth profile in composition was achieved by altering the Ti evaporation rate according to the Sr evaporation rate change. A typical dielectric constant of 170 was measured on films of 75 nm in thickness. The in-situ annealing in oxygen plasma reduced the leakage current.

  10. Photocatalytic activity and interfacial carrier transfer of Ag-TiO2 nanoparticle films

    International Nuclear Information System (INIS)

    Xin Baifu; Ren Zhiyu; Hu Haiyuan; Zhang Xiangyu; Dong Chunlei; Shi Keying; Jing Liqiang; Fu Honggang

    2005-01-01

    The electrodes of Ag-TiO 2 with different Ag content are prepared by a modified sol-gel method. The photochemical properties of Ag-TiO 2 with different Ag content are characterized by surface photovoltage spectroscopy (SPS). The results show that the SPS intensity decreased with increasing Ag contents. This demonstrates that the doping Ag plays the roles trapping photoinduced electrons, which inhibiting the recombination of photoinduced electrons and holes. The photoelectrochemical properties of Ag-TiO 2 electrodes with different Ag content are performed by electrochemical impedance spectroscopy (EIS) under high-pressure mercury lamp (160 W) illuminating, and photocatalytic degradation of RhB are studied at the same time. The experimental results indicate that the process of charge transfer is a controlled-step of photocatalytic reaction. The SPS intensity and the electrical impedance values of EIS equivalent circuits are contrary to photocatalytic degradation ratio of RhB

  11. Crystal Structure And Optical Properties Of TiO2 Thin Films Prepared By Reactive RF Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Goto S.

    2015-06-01

    Full Text Available In sputtering deposition process of TiO2, metal Ti or sintered TiO2 target is used as deposition source. In this study, we have compared the characteristic of target materials. When TiO2 target was used, stoichiometric TiO2 films was deposited under the Ar atmosphere containing 1.0% of oxygen. The highest sputtering rate under this atmosphere was 3.9nm/min at 3.4W/cm2. But, sintered TiO2 target is fragile and cannot endure higher density of input power than 3.4W/cm2. On the other hand, Ti target needs higher oxygen concentration (8% in sputtering gas atmosphere for obtaining rutile/anatase. Even though Ti target can be input twice power density of 7.9W/cm2, the highest deposition rate for Ti target was 1.4/nm, which was ~35% of the highest rate for TiO2 target. Then we have study out the composite target consisting of Ti plate and TiO2 chips. Using the composite target, stoichiometric TiO2 films were prepared in the rate of 9.6nm/min at 6.8 W/cm2 under the atmosphere of Ar/2.5%O2. Furthermore, we have found that the TiO2 films obtained from the composite target consisted of about 100% anatase, whereas TiO2 films obtained from other target have rutile dominant structure. The optical band gap energy of the film is determined by using the Tauc plot. The calculated band gap energies for the films deposited by Ti target and composite target were 2.95 and 3.24eV, which are equivalent to that of rutile and anatase structure, respectively.

  12. Undoped TiO2 and nitrogen-doped TiO2 thin films deposited by atomic layer deposition on planar and architectured surfaces for photovoltaic applications

    International Nuclear Information System (INIS)

    Tian, Liang; Soum-Glaude, Adurey; Volpi, Fabien; Salvo, Luc; Berthomé, Grégory; Coindeau, Stéphane; Mantoux, Arnaud; Boichot, Raphaël; Lay, Sabine; Brizé, Virginie; Blanquet, Elisabeth; Giusti, Gaël; Bellet, Daniel

    2015-01-01

    Undoped and nitrogen doped TiO 2 thin films were deposited by atomic layer deposition on planar substrates. Deposition on 3D-architecture substrates made of metallic foams was also investigated to propose architectured photovoltaic stack fabrication. All the films were deposited at 265 °C and nitrogen incorporation was achieved by using titanium isopropoxide, NH 3 and/or N 2 O as precursors. The maximum nitrogen incorporation level obtained in this study was 2.9 at. %, resulting in films exhibiting a resistivity of 115 Ω cm (+/−10 Ω cm) combined with an average total transmittance of 60% in the 400–1000 nm wavelength range. Eventually, TiO 2 thin films were deposited on the 3D metallic foam template

  13. Improved photoelectrochemical detection of mercury (II) with a TiO2-modified composite photoelectrode

    International Nuclear Information System (INIS)

    Chamier, Jessica; Crouch, Andrew M.

    2012-01-01

    Highlights: • We have determined that a PANI–RS modified photoelectrode behaved as a photoanode in the presence of Hg 2+ . • The photoresponse of the ITO/TiO 2 /PANI–RS photoelectrode was equivalent to the amount of Hg 2+ in solution. • The linear range for photoelectrochemical detection of Hg 2+ was 10–200 μg L −1 Hg 2+ with a LOQ of 4 μg L −1 . • We determined that the pH independence of ITO/TiO 2 /PANI–RS photoelectrode was limit by the TiO 2 layer to between pH 6 and 7. - Abstract: The spectrophotometric change of a mercury (II) (Hg 2+ ) selective small molecule chemosensor has been successfully converted into a photovoltaic response upon ligating Hg 2+ . The photon excitation was followed by charge separation facilitated by TiO 2 and polyaniline (PANI), resulting in an electron transfer to an electrical back contact. The photoresponse of the Hg 2+ selective chromophore was converted to an electron current equivalent to the amount of Hg 2+ in solution. The favourable properties of a Hg 2+ sensitive chemosensor was combined with the semiconductor capabilities of TiO 2 to construct a sensor that is capable of generating a current in the presence of Hg 2+ under illumination. A composite of the fluorescent chemosensor rhodamine 6G hydrozone derivative (RS) and PANI was immobilized on indium tin oxide (ITO) plates coated with TiO 2 and subjected to photovoltammetric measurements. The photovoltammetric responses of the coated layers were investigated to determine the sensitivity and selectivity of the immobilized sensor to Hg 2+ in the presence of background ions. The photo-response increased linearly with increasing Hg 2+ concentration from 10 to 200 μg L −1 with a limit of quantification (LOQ) of 4 μg L −1 . The pH independence for the photoresponse was limited by the TiO 2 layer and was optimal between pH 6 and 7.

  14. Improved photoelectrochemical detection of mercury (II) with a TiO{sub 2}-modified composite photoelectrode

    Energy Technology Data Exchange (ETDEWEB)

    Chamier, Jessica [Department of Chemistry and Polymer Science, University of Stellenbosch, Matieland X1, Stellenbosch 7602 (South Africa); Council for Scientific and Industrial Research, Natural Resources and the Environment, P.O. Box 320, Stellenbosch 7599 (South Africa); Crouch, Andrew M., E-mail: andrew.crouch@wits.ac.za [Institute of Molecular Sciences, Faculty of Science, University of the Witwatersrand, Private Bag 3, Wits, 2050, Johannesburg (South Africa)

    2012-01-16

    Highlights: Bullet We have determined that a PANI-RS modified photoelectrode behaved as a photoanode in the presence of Hg{sup 2+}. Bullet The photoresponse of the ITO/TiO{sub 2}/PANI-RS photoelectrode was equivalent to the amount of Hg{sup 2+} in solution. Bullet The linear range for photoelectrochemical detection of Hg{sup 2+} was 10-200 {mu}g L{sup -1} Hg{sup 2+} with a LOQ of 4 {mu}g L{sup -1}. Bullet We determined that the pH independence of ITO/TiO{sub 2}/PANI-RS photoelectrode was limit by the TiO{sub 2} layer to between pH 6 and 7. - Abstract: The spectrophotometric change of a mercury (II) (Hg{sup 2+}) selective small molecule chemosensor has been successfully converted into a photovoltaic response upon ligating Hg{sup 2+}. The photon excitation was followed by charge separation facilitated by TiO{sub 2} and polyaniline (PANI), resulting in an electron transfer to an electrical back contact. The photoresponse of the Hg{sup 2+} selective chromophore was converted to an electron current equivalent to the amount of Hg{sup 2+} in solution. The favourable properties of a Hg{sup 2+} sensitive chemosensor was combined with the semiconductor capabilities of TiO{sub 2} to construct a sensor that is capable of generating a current in the presence of Hg{sup 2+} under illumination. A composite of the fluorescent chemosensor rhodamine 6G hydrozone derivative (RS) and PANI was immobilized on indium tin oxide (ITO) plates coated with TiO{sub 2} and subjected to photovoltammetric measurements. The photovoltammetric responses of the coated layers were investigated to determine the sensitivity and selectivity of the immobilized sensor to Hg{sup 2+} in the presence of background ions. The photo-response increased linearly with increasing Hg{sup 2+} concentration from 10 to 200 {mu}g L{sup -1} with a limit of quantification (LOQ) of 4 {mu}g L{sup -1}. The pH independence for the photoresponse was limited by the TiO{sub 2} layer and was optimal between pH 6 and 7.

  15. Study on the enhanced adsorption properties of lysozyme on polyacrylic acid modified TiO2 nano-adsorbents

    Science.gov (United States)

    Liu, Yufeng; Jin, Zu; Meng, Hao; Zhang, Xia

    2018-01-01

    The adsorption and immobilization of enzymes onto solid carriers has been focused on due to their many advantages, such as improved stability against a thermal or organic solvent and a good cycle usability. TiO2 nanoparticles is one of excellent nano-adsorbents owing to its excellent biocompatibility, non-inflammatory, and abundant surface hydroxyl groups, which are convenient to be combined with various functional groups. In this paper polyacrylic acid (PAA) modified TiO2 nanoparticles were synthesized through an in situ light-induced polymerization of acrylic acid on the surface of TiO2 nanoparticles. The structure and surface physicochemical properties of the PAA/TiO2 nanoparticles were characterized by TEM, XRD, FT-IR, Zeta potential measurements and TG-DSC. The experimental results showed that the isoelectric point of PAA/TiO2 significantly reduced to 1.82 compared with that of pure TiO2 nanoparticles (6.08). In the adsorption tests of lysozyme (Lyz), the PAA/TiO2 nanoparticles displayed enhanced adsorption activity compared with pristine TiO2. The maximum adsorption capacity of PAA/TiO2 for Lyz was 225.9 mg g-1 under the optimum conditions where the initial concentration of Lyz was 300 mg ml-1, the addition amount of PAA/TiO2 was 6.4 mg, the adsorption time was 30 min and the pH value was 7.0. The sodium dodecyl sulfate (SDS, 0.5%) presented the best efficiency (76.86%) in the removal of adsorbed Lyz, and the PAA/TiO2 nanoparticles showed excellent adsorption stability based on five cyclic adsorption-desorption tests. The fitting calculation results of the adsorption isotherm and the thermodynamics indicated the adsorption was an exothermic, entropy increasing, spontaneous and monomolecular layer adsorption process.

  16. A practical demonstration of water disinfection using TiO2 films and sunlight.

    Science.gov (United States)

    Gelover, Silvia; Gómez, Luis A; Reyes, Karina; Teresa Leal, Ma

    2006-10-01

    The scope of this study is the assessment of the efficiency of solar disinfection by heterogeneous photocatalysis with sol-gel immobilized (titanium dioxide) TiO2 films over glass cylinders. The solar disinfection process known as SODIS was considered as a reference. Spring water naturally polluted with coliform bacteria was exposed to sunlight in plastic bottles with and without TiO2 over simple solar collectors and the disinfection effectiveness was measured. Total and fecal coliforms quantification was performed by means of the chromogenic substrate method in order to obtain the efficiency of each disinfection treatment. The disinfection with TiO2 was more efficient than the SODIS process, inactivating total coliforms as well as fecal coliforms. On a sunny day (more than 1000 W m(-2) irradiance), it took the disinfection with immobilized TiO2 15 min of irradiation to inactivate the fecal coliforms to make them undetectable. For inactivation of total coliforms, 30 min was required, so that in less than half the time it takes SODIS, the treated water complies with the microbial standards for drinking water in Mexico. Another important part of this study has been to determine the bacterial regrowth in water after the disinfection processes were tested. After SODIS, bacterial regrowth of coliforms was observed. In contrast, when using the TiO2 catalyst, coliforms regrowth was not detected, neither for total nor for fecal coliforms. The disinfection process using TiO2 kept treated water free of coliforms at least for seven days after sun irradiation. This demonstration opens the possibility of application of this simple method in rural areas of developing countries.

  17. Photocatalytic Activity of TiO2 Thin Films Obtained by the Sputtering RF in Wastewater

    Science.gov (United States)

    Cardona Bedoya, Jairo Armando; Sanchez Velandia, Wilmer Asmed; Delgado Rosero, Miguel Iban; Florido Cuellar, Alex Enrique; Zelaya Angel, Orlando; Mendoza Alvarez, Julio G.

    2011-03-01

    The photocatalytic activity of Ti O2 thin films in wastewater, under an UV irradiation, is studied. The films were prepared on corning glass substrates by the sputtering RF technique. We present evidence on the photocatalytic degradation, carried out by advanced oxidation processes (AOPs) in domestic wastewater pretreated with UASB (upflow anaerobic sludge blanket) reactors. Ti O2 films were illuminated with ultraviolet light during a time of 4 hours (λ ≅ 264 nm). We could see the effect of degraded operation in the absorbance measurement using UV-VIS spectrophotometry. The results show an increased rate of degradation of the wastewater by 30% compared to the values reflected biologically treated wastewater by anaerobic reactors.

  18. Influence of annealing temperature and organic dyes as sensitizers on sol–gel derived TiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Rani, Mamta; Abbas, Saeed J.; Tripathi, S.K., E-mail: surya@pu.ac.in

    2014-09-15

    Highlights: • Preparation of rice shaped TiO{sub 2} nanorods with anatase structure by sol–gel method. • Effect of post deposition annealing on structural properties of TiO{sub 2} is studied. • Unlike individual dye, absorption of Cocktail dye with TiO{sub 2} nanorods is broader. • Cocktail dye sensitized TiO{sub 2} film has more photosensitivity than EY, RB, AO. • Increase in photosensitivity up to optimum temperature is due to hole passivation. - Abstract: Five different organic dyes and reported cocktail dye composed of these dyes are used as sensitizer for titanium dioxide (TiO{sub 2}). Rice shaped (TiO{sub 2}) nanorods are prepared by using sol–gel method. The films annealed at 673 K and above are crystalline with anatase structure. The effect of post annealing temperature is studied on various structural parameters. Cocktail dye shows broader absorption with TiO{sub 2} nanorods in visible region compared with five dyes. Maximum photosensitivity is obtained with RhB dye, followed by FGF and cocktail dye sensitized TiO{sub 2} films. Increase in photosensitivity is due to passivating some hole traps on the surface up to some optimum temperature, above which photosensitivity decreases due to a higher photo activation energy compared to dark conductivity in low temperature region and also may be due to damage of the dye molecule. This work may prove its worth for understanding the electron transport in dye sensitized nanodevices.

  19. Silver loaded WO{sub 3-x}/TiO{sub 2} composite multifunctional thin films

    Energy Technology Data Exchange (ETDEWEB)

    Dunnill, Charles W.; Noimark, Sacha; Parkin, Ivan P., E-mail: I.P.Parkin@ucl.ac.uk

    2012-06-30

    Multifunctional WO{sub 3-x}-TiO{sub 2} composite thin films have been prepared by sol-gel synthesis and shown to be good visible light photocatalysts whilst retaining a desirable underlying blue colouration. The WO{sub 3-x}-TiO{sub 2} composite thin films were further enhanced using silver nanoparticles synthesised in-situ on the surface from the photo-degradation of silver nitrate solution. Thin films were characterised using X-ray diffraction, Raman, Scanning electron microscopy and UV-visible spectroscopy and shown to photo degrade stearic acid, using white light {lambda} = 420-800 nm. - Highlights: Black-Right-Pointing-Pointer WO{sub 3-X} TiO{sub 2} composite thin films were synthesised by sol-gel methods. Black-Right-Pointing-Pointer Blue tinted glass is desirable for the value added glass industry. Black-Right-Pointing-Pointer Silver nanoparticle island formation enhances the activity of the films. Black-Right-Pointing-Pointer Blue tinted 'value added' coated glass is now possible.

  20. Silver loaded WO3−x/TiO2 composite multifunctional thin films

    International Nuclear Information System (INIS)

    Dunnill, Charles W.; Noimark, Sacha; Parkin, Ivan P.

    2012-01-01

    Multifunctional WO 3−x –TiO 2 composite thin films have been prepared by sol–gel synthesis and shown to be good visible light photocatalysts whilst retaining a desirable underlying blue colouration. The WO 3−x –TiO 2 composite thin films were further enhanced using silver nanoparticles synthesised in-situ on the surface from the photo-degradation of silver nitrate solution. Thin films were characterised using X-ray diffraction, Raman, Scanning electron microscopy and UV–visible spectroscopy and shown to photo degrade stearic acid, using white light λ = 420–800 nm. - Highlights: ► WO 3−X TiO 2 composite thin films were synthesised by sol–gel methods. ► Blue tinted glass is desirable for the value added glass industry. ► Silver nanoparticle island formation enhances the activity of the films. ► Blue tinted “value added” coated glass is now possible.

  1. Photoactive TiO2 Films Formation by Drain Coating for Endosulfan Degradation

    Directory of Open Access Journals (Sweden)

    Natalia Tapia-Orozco

    2013-01-01

    Full Text Available Heterogeneous photocatalysis is an advanced oxidation process in which a photoactive catalyst, such as TiO2, is attached to a support to produce free radical species known as reactive oxygen species (ROS that can be used to break down toxic organic compounds. In this study, the draining time, annealing temperature, and draining/annealing cycles for TiO2 films grown by the drain coating method were evaluated using a 23 factorial experimental design to determine the photoactivity of the films via endosulfan degradation. The TiO2 films prepared with a large number of draining/annealing cycles at high temperatures enhanced (P>0.05 endosulfan degradation and superoxide radical generation after 30 minutes of illumination with UV light. We demonstrated a negative correlation (R2=0.69; P>0.01 between endosulfan degradation and superoxide radical generation. The endosulfan degradation rates were the highest at 30 minutes with the F6 film. In addition, films prepared using conditions F1, F4, and F8 underwent an adsorption/desorption process. The kinetic reaction constants, Kapp (min−1, were 0.0101, 0.0080, 0.0055, 0.0048, and 0.0035 for F6, F2, F5, F3, and F1, respectively. The endosulfan metabolites alcohol, ether, and lactone were detected and quantified at varying levels in all photocatalytic assays.

  2. Fabrication of TiO2/PU Superhydrophobic Film by Nanoparticle Assisted Cast Micromolding Process.

    Science.gov (United States)

    Li, Jie; Zheng, Jianyong; Zhang, Jing; Feng, Jie

    2016-06-01

    Lotus-like surfaces have attracted great attentions in recent years for their wide applications in water repellency, anti-fog and self-cleaning. This paper introduced a novel process, nanoparticle assisted cast micromolding, to create polymer film with superhydrophobic surface. Briefly, waterborne polyurethane (WPU) sol and nano TiO2/WPU sol were each cast onto the featured surfaces of the poly(dimethylsiloxane) (PDMS) stamps replicated from fresh lotus leaves. After being dried and peeled off from the stamps, PU and TiO2/WPU replica films were created respectively. To the former, only high hydrophobic property was observed with static water contact angle (WCA) at 142.5 degrees. While to the later, superhydrophobic property was obtained with WCA more than 150 degrees and slide angle less than 3 degrees. Scanning electron microscopy (SEM) imaging showed that the PU replica film only had the micro-papillas and the TiO2/PU replica film not only had micro papillas but also had a large number of nano structures distributed on and between the micro-papillas. Such nano and micro hierarchical structures were very similar with those on the natural lotus leaf surface, thus was the main reason for causing superhydrophobic property. Although an elastic PDMS stamp from lotus leaf was used in herein process, hard molds may also be used in theory. This study supplied an alternative technique for large scale production of polymeric films with superhydrophobic.

  3. Rutile TiO{sub 2} active-channel thin-film transistor using rapid thermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Sung-Jin; Heo, Kwan-Jun; Yoo, Su-Chang; Choi, Seong-Gon [Chungbuk National University, Cheongju (Korea, Republic of); Chang, Seung-Wook [Samsung Display, Co., Ltd., Suwon (Korea, Republic of)

    2014-10-15

    TiO{sub 2} active-channel thin-film transistors (TFTs), in which the bottom-gate top-contact architecture was prepared with atomic layer deposition grown TiO{sub 2} as the semiconducting layer, were fabricated and then investigated based on key process parameters, such as the rapid thermal annealing (RTA) temperature. Structural analyses suggested that TiO{sub 2} films annealed at temperatures above 500 .deg. C changed from an amorphous to a rutile phase. The TFT with a TiO{sub 2} semiconductor annealed at 600 .deg. C exhibited strongly-saturated output characteristics, a much higher on/off current ratio of 4.3 x 10{sup 5}, and an electron mobility of 0.014 cm{sup 2}/Vs. Moreover, the potential for manipulating TiO{sub 2}-based TFTs with RTA methodology was demonstrated through the realization of a simple resistive-load inverter.

  4. Dielectric and piezoelectric properties of lead-free (Bi,Na)TiO3-based thin films

    Science.gov (United States)

    Abazari, M.; Safari, A.; Bharadwaja, S. S. N.; Trolier-McKinstry, S.

    2010-02-01

    Dielectric and piezoelectric properties of morphotropic phase boundary (Bi,Na)TiO3-(Bi,K)TiO3-BaTiO3 epitaxial thin films deposited on SrRuO3 coated SrTiO3 substrates were reported. Thin films of 350 nm thickness exhibited small signal dielectric permittivity and loss tangent values of 750 and 0.15, respectively, at 1 kHz. Ferroelectric hysteresis measurements indicated a remanent polarization value of 30 μC/cm2 with a coercive field of 85-100 kV/cm. The thin film transverse piezoelectric coefficient (e31,f) of these films after poling at 600 kV/cm was found to be -2.2 C/m2. The results indicate that these BNT-based thin films are a potential candidate for lead-free piezoelectric devices.

  5. Enhanced Water Splitting by Fe2O3-TiO2-FTO Photoanode with Modified Energy Band Structure

    Directory of Open Access Journals (Sweden)

    Eul Noh

    2013-01-01

    Full Text Available The effect of TiO2 layer applied to the conventional Fe2O3/FTO photoanode to improve the photoelectrochemical performance was assessed from the viewpoint of the microstructure and energy band structure. Regardless of the location of the TiO2 layer in the photoanodes, that is, Fe2O3/TiO2/FTO or TiO2/Fe2O3/FTO, high performance was obtained when α-Fe2O3 and H-TiNT/anatase-TiO2 phases existed in the constituent Fe2O3 and TiO2 layers after optimized heat treatments. The presence of the Fe2O3 nanoparticles with high uniformity in the each layer of the Fe2O3/TiO2/FTO photoanode achieved by a simple dipping process seemed to positively affect the performance improvement by modifying the energy band structure to a more favorable one for efficient electrons transfer. Our current study suggests that the application of the TiO2 interlayer, together with α-Fe2O3 nanoparticles present in the each constituent layers, could significantly contribute to the performance improvement of the conventional Fe2O3 photoanode.

  6. Influence of interface layer on optical properties of sub-20 nm-thick TiO2 films

    Science.gov (United States)

    Shi, Yue-Jie; Zhang, Rong-Jun; Li, Da-Hai; Zhan, Yi-Qiang; Lu, Hong-Liang; Jiang, An-Quan; Chen, Xin; Liu, Juan; Zheng, Yu-Xiang; Wang, Song-You; Chen, Liang-Yao

    2018-02-01

    The sub-20 nm ultrathin titanium dioxide (TiO2) films with tunable thickness were deposited on Si substrates by atomic layer deposition (ALD). The structural and optical properties were acquired by transmission electron microscopy, atomic force microscopy and spectroscopic ellipsometry. Afterwards, a constructive and effective method of analyzing interfaces by applying two different optical models consisting of air/TiO2/Ti x Si y O2/Si and air/effective TiO2 layer/Si, respectively, was proposed to investigate the influence of interface layer (IL) on the analysis of optical constants and the determination of band gap of TiO2 ultrathin films. It was found that two factors including optical constants and changing components of the nonstoichiometric IL could contribute to the extent of the influence. Furthermore, the investigated TiO2 ultrathin films of 600 ALD cycles were selected and then annealed at the temperature range of 400-900 °C by rapid thermal annealing. Thicker IL and phase transition cause the variation of optical properties of TiO2 films after annealing and a shorter electron relaxation time reveals the strengthened electron-electron and electron-phonon interactions in the TiO2 ultrathin films at high temperature. The as-obtained results in this paper will play a role in other studies of high dielectric constants materials grown on Si substrates and in the applications of next generation metal-oxide-semiconductor devices.

  7. Configuration and local elastic interaction of ferroelectric domains and misfit dislocation in PbTiO3/SrTiO3 epitaxial thin films

    Directory of Open Access Journals (Sweden)

    Takanori Kiguchi, Kenta Aoyagi, Yoshitaka Ehara, Hiroshi Funakubo, Tomoaki Yamada, Noritaka Usami and Toyohiko J Konno

    2011-01-01

    Full Text Available We have studied the strain field around the 90° domains and misfit dislocations in PbTiO3/SrTiO3 (001 epitaxial thin films, at the nanoscale, using the geometric phase analysis (GPA combined with high-resolution transmission electron microscopy (HRTEM and high-angle annular dark field––scanning transmission electron microscopy (HAADF-STEM. The films typically contain a combination of a/c-mixed domains and misfit dislocations. The PbTiO3 layer was composed from the two types of the a-domain (90° domain: a typical a/c-mixed domain configuration where a-domains are 20–30 nm wide and nano sized domains with a width of about 3 nm. In the latter case, the nano sized a-domain does not contact the film/substrate interface; it remains far from the interface and stems from the misfit dislocation. Strain maps obtained from the GPA of HRTEM images show the elastic interaction between the a-domain and the dislocations. The normal strain field and lattice rotation match each other between them. Strain maps reveal that the a-domain nucleation takes place at the misfit dislocation. The lattice rotation around the misfit dislocation triggers the nucleation of the a-domain; the normal strains around the misfit dislocation relax the residual strain in a-domain; then, the a-domain growth takes place, accompanying the introduction of the additional dislocation perpendicular to the misfit dislocation and the dissociation of the dislocations into two pairs of partial dislocations with an APB, which is the bottom boundary of the a-domain. The novel mechanism of the nucleation and growth of 90° domain in PbTiO3/SrTiO3 epitaxial system has been proposed based on above the results.

  8. Improvement of the epoxy coating properties by incorporation of polyaniline surface treated TiO2 nanoparticles previously modified with vitamin B6

    OpenAIRE

    Radoman, Tijana S.; Džunuzović, Jasna V.; Grgur, Branimir; Gvozdenović, Milica M.; Jugović, Branimir; Miličević, Dejan S.; Džunuzović, Enis S.

    2016-01-01

    Novel TiO2-PANI core-shell nanocomposite, prepared by in situ oxidative polymerization of aniline in the presence of TiO2 nanoparticles surface modified with vitamin B6, was used to reinforce epoxy resin. The size of prepared TiO2 nanoparticles and TiO2-PANI nanocomposite were determined by a transmission electron microscopy (TEM). The surface modification of TiO2 nanoparticles was confirmed by FTIR and UV–vis spectroscopy, while the morphology of PANI and TiO2-PANI nanocomposite was investig...

  9. High Photocatalytic Performance of Two Types of Graphene Modified TiO2 Composite Photocatalysts

    Science.gov (United States)

    Zhang, Jun; Li, Sen; Tang, Bo; Wang, Zhengwei; Ji, Guojian; Huang, Weiqiu; Wang, Jinping

    2017-07-01

    High quality and naturally continuous structure of three-dimensional graphene network (3DGN) endow it a promising candidate to modify TiO2. Although the resulting composite photocatalysts display outstanding performances, the lacking of active sites of the 3DGN not only goes against a close contact between the graphene basal plane and TiO2 nanoparticles (weaken electron transport ability) but also limits the efficient adsorption of pollutant molecules. Similar with surface functional groups of the reduced graphene oxide (RGO) nanosheets, surface defects of the 3DGN can act as the adsorption sites. However, the defect density of the 3DGN is difficult to control (a strict cool rate of substrate and a strict flow of precursor gas are necessary) because of its growth approach (chemical vapor deposition method). In this study, to give full play to the functions of graphene, the RGO nanosheets and 3DGN co-modified TiO2 composite photocatalysts are prepared. After optimizing the mass fraction of the RGO nanosheets in the composite photocatalyst, the resulting chemical adsorption ability and yields of strong oxidizing free radicals increase significantly, indicating the synergy of the RGO nanosheets and 3DGN.

  10. Facile synthesis of tunable carbon modified mesoporous TiO{sub 2} for visible light photocatalytic application

    Energy Technology Data Exchange (ETDEWEB)

    Wei, Xiao-Na; Wang, Hui-Long, E-mail: hlwang@dlut.edu.cn; Wang, Xin-Kui; Jiang, Wen-Feng

    2017-08-01

    Highlights: • Combined hydrothermal-calcination steps were used to prepare mesoporous C-TiO{sub 2}. • Polyacrylate was employed as the carbon source. • XPS revealed the interstitial carbon modifying mode through carbonate-like species. • C-TiO{sub 2} exhibited visible light activity towards dinitro butyl phenol degradation. - Abstract: In this paper, we describe a simple and novel approach for preparing tunable carbon-modified mesoporous TiO{sub 2} photocatalysts by combining the in-situ carbonization of PAA-Ti/TiO{sub 2}, hydrothermal reaction process and post-calcination treatment. The synthesized carbon-modified mesoporous TiO{sub 2} powders were of high crystallinity, large specific surface area and good visible light response. The carbon species were formed by the carbonization of polyacrylate (PAA). The presence of carbonates was subsequently confirmed by the XPS spectra, which significantly narrow down the band gap of TiO{sub 2}. The organic group in polyacrylate served as the carbon source and carbon resulted from in-situ carbonization treatment could help to inhibit the excessive growth of TiO{sub 2} grain and enlarge the pore structure of TiO{sub 2}. The amount of carbon species could be feasibly modulated by adjusting the post-calcination temperature and the surface area of the photocatalyst was enlarged further after the partial removal of carbon species. The carbon-modified mesoporous TiO{sub 2} powders exhibit excellent reproducibility and photocatalytic performance under visible light irradiation.

  11. Structure and photocatalytic activity studies of TiO2-supported over Ce-modified Al-MCM-41

    International Nuclear Information System (INIS)

    Krishna Reddy, Jakkidi; Durgakumari, Valluri; Subrahmanyam, Machiraju; Sreedhar, Bojja

    2009-01-01

    Ce-Al-MCM-41, TiO 2 /Al-MCM-41 and TiO 2 /Ce-Al-MCM-41 materials with varying contents of Ce (by impregnation) and TiO 2 loaded (by solid-state dispersion) on Al-MCM-41 support are prepared. The Ce modified and TiO 2 loaded composite systems are characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV-vis diffuse reflectance spectra (DRS) and X-ray photoelectron spectroscopy (XPS) techniques. The DRS and XPS of low Ce content (0.2-0.5 wt.%) modified Al-MCM-41 samples are showing more characteristic of Ce 3+ species wherein cerium in interaction with Al-MCM-41 and that of high Ce (0.8, 3.0 wt.%) content modified samples are showing the characteristic of both Ce 4+ and Ce 3+ species. A series of Ce-modified Al-MCM-41 and TiO 2 loaded composite catalysts are evaluated for photocatalytic degradation of phenol under UV irradiation. Low Ce content in Ce 3+ state on Al-MCM-41 is showing good photoactivity in comparison with high Ce content samples and pure ceria. The composite TiO 2 /Ce-Al-MCM-41 is showing enhanced degradation activity due decreased rate of electron-hole recombination on TiO 2 surface by the redox properties of cerium. The photocatalyst TiO 2 /Ce-Al-MCM-41 with an optimum of 10 wt.% TiO 2 and 0.3 wt.% Ce is showing maximum phenol degradation activity. The possible mechanism of phenol degradation on the composite photocatalyst is proposed.

  12. Preparation of TiO2-based nanotubes/nanoparticles composite thin film electrodes for their electron transport properties

    International Nuclear Information System (INIS)

    Zhao, Wanyu; Fu, Wuyou; Chen, Jingkuo; Li, Huayang; Bala, Hari; Wang, Xiaodong; Sun, Guang; Cao, Jianliang; Zhang, Zhanying

    2015-01-01

    The composite thin film electrodes were prepared with one-dimensional (1D) TiO 2 -B nanotubes (NTs) and zero-dimensional TiO 2 nanoparticles (NPs) based on different weight ratios. The electron transport properties of the NTs/NPs composite thin film electrodes applied for dye-sensitized solar cells had been investigated systematically. The results indicated that although the amount of dye adsorption decreased slightly, the devices with the NTs/NPs composite thin film electrodes could obtain higher open-circuit voltage and overall conversion efficiency compared to devices with pure TiO 2 NPs electrodes by rational tuning the weight ratio of TiO 2 -B NTs and TiO 2 NPs. When the weight ratio of TiO 2 -B NTs in the NTs/NPs composite thin film electrodes increased, the density of states and recombination rate decreased. The 1D structure of TiO 2 -B NTs can provide direct paths for electron transport, resulting in higher electron lifetime, electron diffusion coefficient and electron diffusion length. The composite thin film electrodes possess the merits of the rapid electron transport of TiO 2 -B NTs and the high surface area of TiO 2 NPs, which has great applied potential in the field of photovoltaic devices. - Highlights: • The composite thin film electrodes (CTFEs) were prepared with nanotubes and nanoparticles. • The CTFEs possess the rapid electron transport and high surface area. • The CTFEs exhibit lower recombination rate and longer electron life time. • The CTFEs have great applied potential in the field of photovoltaic devices

  13. Enhanced photoelectrochemical properties of F-containing TiO2 sphere thin film induced by its novel hierarchical structure

    International Nuclear Information System (INIS)

    Dong Xiang; Tao Jie; Li Yingying; Zhu Hong

    2009-01-01

    The novel nanostructured F-containing TiO 2 (F-TiO 2 ) sphere was directly synthesized on the surface of Ti foil in the solution of NH 4 F and HCl by one-step hydrothermal approach under low-temperature condition. The samples were characterized respectively by means of field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The results showed that the F-TiO 2 sphere was hierarchical structure, which composed of porous octahedron crystals with one truncated cone, leading to a football-like morphology. XPS results indicated that F - anions were just physically adsorbed on the surface of TiO 2 microspheres. The studies on the optical properties of the F-TiO 2 were carried out by UV-vis light absorption spectrum. The surface fluorination of the spheres, the unique nanostructure induced accessible macropores or mesopores, and the increased light-harvesting abilities were crucial for the high photoelectrochemical activity of the synthesized F-TiO 2 sphere for water-splitting. The photocurrent density of the F-TiO 2 sphere thin film was more than two times than that of the P25 thin film. Meanwhile, a formation mechanism was briefly proposed. This approach could provide a facile method to synthesize F-TiO 2 microsphere with a special morphology and hierarchical structure in large scale.

  14. Superior environment resistance of quartz crystal microbalance with anatase TiO2/ZnO nanorod composite films

    International Nuclear Information System (INIS)

    Qiang, Wei; Wei, Li; Shaodan, Wang; Yu, Bai

    2015-01-01

    Graphical abstract: ZnO nanorod array being prepared by an in situ method on the QCM coated with Au film via hydrothermal process and surface modification with coated TiO 2 by sol–gel methods to form a superhydrophobic TiO 2 /ZnO composite film the anatase TiO 2 /ZnO nanorod composite film with a sharp, pencil-like structure exhibiting excellent superhydrophobicity (water contact angle of 155°), non-sticking water properties, and an autonomous cleaning property under UV irradiation. The anatase TiO 2 /ZnO nanorod composite film facilitates the precise measurement and extended lifetime of the QCM for the detection of organic gas molecules. - Highlights: • This work combines, for the first time, the advantage of the TiO 2 /ZnO composite film on photocatalysis and reversible super-hydrophobic and super-hydrophilic transition, and puts forward a solution to satisfy weatherability of quartz crystal microbalance in long-term application. • The anatase TiO 2 /ZnO nanorod composite film with pencil structure exhibit excellent super-hydrophobicity (water contact angle can reach 155°), no-sticking water properties and self-cleaning property under UV irradiation. • The photocatalysis and reversible super-hydrophobic and super-hydrophilic transition of the TiO 2 /ZnO nanorod composite film is stable in long-term application. - Abstract: The precise measurement of quartz crystal microbalance (QCM) in the detection and weighing of organic gas molecules is achieved due to excellent superhydrophobicity of a deposited film composite. Photocatalysis is utilized as a method for the self-cleaning of organic molecules on the QCM for extended long-term stability in the precision of the instrument. In this paper, ZnO nanorod array is prepared via in situ methods on the QCM coated with Au film via hydrothermal process. Subsequently, a TiO 2 /ZnO composite film is synthesized by surface modification with TiO 2 via sol–gel methods. Results show the anatase TiO 2 /ZnO nanorod

  15. Defect engineering of SrTiO3 thin films for resistive switching applications

    International Nuclear Information System (INIS)

    Wicklein, Sebastian

    2013-01-01

    As a matter of fact, the importance of (transition) metal oxides for modern applications in the field of energy and information technology (IT) for e.g. novel energy storage systems and solid state electronic devices is increasing. Previous studies discovered the importance of defects in an oxide for their functionality and emphasized the impact of stoichiometry on the oxide performance. A new field of interest of the memory technology sector is the so-called resistive switching phenomena where a voltage stimulus causes a thin oxide (≤10 nm) to change its resistance state from a high resistance state to a low resistance state and back. So called resistive RAM (ReRAM or RRAM) are deemed to be the future replacement (2015) for contemporary FLASH memory technology due to its extremely low energy consumption, its very fast read/write time (ns) and its possible node size 3 was used as an oxide model material and was deposited by pulsed laser deposition (PLD) onto doped and undoped SrTiO 3 single crystals to investigate the formation of defects as a function of the process parameters. By combining structural and chemical thin film analysis with detailed PLD plume diagnostics and modeling of the laser plume dynamics, it was possible to elucidate the different physical mechanisms determining the stoichiometry of SrTiO 3 during PLD. Deviations between thin film and target stoichiometry are basically a result of two effects, namely, incongruent ablation and preferential scattering of lighter ablated species during their motion towards the substrate in the O 2 background gas. It is shown that the SrTiO 3 system reacts to a non-stoichiometry with the systematic incorporation of titanium and strontium vacancies which could be detected by positron annihilation lifetime spectroscopy. The role of extrinsic dopands such as Fe is shown to have more complicated effects on the SrTiO 3 system than portrayed by theoretical considerations. The effect of defects on the resistive

  16. Electrical properties of (1 0 0)-predominant BaTiO3 films derived from alkoxide solutions of two concentrations

    International Nuclear Information System (INIS)

    Guo Yiping; Suzuki, Kazuyuki; Nishizawa, Kaori; Miki, Takeshi; Kato, Kazumi

    2006-01-01

    Lead-free piezoelectric films with thickness larger than 1 μm integrated on silicon substrates have been receiving considerable attention because of environmental concerns and their potential applications in microelectromechanical systems. We demonstrate that, by chemical solution deposition, it is possible to process (1 0 0)-predominant 1 μm BaTiO 3 films on LaNiO 3 /Pt/TiO x /SiO 2 /Si substrates using thinner high-crystallinity columnar BaTiO 3 films as buffer layers. We point out that this kind of buffer layer prepared with a lower concentration solution on the surface of an LaNiO 3 /Pt electrode is effective in enhancing the crystallinity and orientation degree of final BaTiO 3 films prepared with a higher concentration solution. The 1 μm BaTiO 3 films show good dielectric and insulating characteristics against an applied field, and the conduction current shows Schottky emission behavior at modest voltage and space-charge-limited behavior at higher voltage. We also demonstrate that the (1 0 0)-predominant 1 μm BaTiO 3 films have excellent piezoelectric properties: piezoelectric coefficients d 33 higher than 50 pm/V have been determined for the bare films using atomic force microscopy, which are comparable to those of Pb(Zr,Ti)O 3 films. These results indicate that the (1 0 0)-predominant BaTiO 3 films should be promising candidates for microelectromechanical systems applications

  17. Preparation of mesoporous CdS-containing TiO{sub 2} film and enhanced visible light photocatalytic property

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Yanmei; Wang, Renliang, E-mail: rlwang@tsmc.edu.cn; Zhang, Wenping; Ge, Haiyan; Wang, Xiaopeng; Li, Li

    2015-01-15

    Highlights: • Well-dispersed distribution of CdS nanoparticles inside of TiO{sub 2} mesoporous structures was fabricated. • The sensitization of CdS nanoparticles significantly extends the response of TiO{sub 2} mesoporous film in the visible region. • An improved visible light photocatalytic activity was observed by the CdS–MTF. - Abstract: Mesoporous TiO{sub 2} films containing CdS nanocrystals were successfully fabricated by a two-step process of successive ionic layer adsorption and reaction (SILAR) technique and a solvothermal method followed by annealing. The distribution of CdS nanoparticles in the inner structures of the TiO{sub 2} mesoporous films is confirmed by field emission scanning electron microscope. The CdS modification of the mesoporous films results in an increase in the visible light adsorption, and exhibits more excellent photocatalytic degradation of methyl orange (MO) under visible light irradiation.

  18. Chromium doped TiO2 sputtered thin films synthesis, physical investigations and applications

    CERN Document Server

    Hajjaji, Anouar; Gaidi, Mounir; Bessais, Brahim; El Khakani, My Ali

    2014-01-01

    This book presents co-sputtered processes ways to produce chrome doped TiO2 thin films onto various substrates such as quartz, silicon and porous silicon. Emphasis is given on the link between the experimental preparation and physical characterization in terms of Cr content. Moreover, the structural, optical and optoelectronic investigations are emphasized throughout. The book explores the potencial applications of devices based on Cr doped TiO2 thin films as gas sensors and in photocatalysis and in the photovoltaic industry. Also, this book provides extensive leads into research literature, and each chapter contains details which aim to develop awareness of the subject and the methods used. The content presented here will be useful for graduate students as well as researchers in materials science, physics, chemistry and engineering.

  19. Photoelectrocatalytic Degradation of Sodium Oxalate by TiO2/Ti Thin Film Electrode

    Directory of Open Access Journals (Sweden)

    Chen-Yu Chang

    2012-01-01

    Full Text Available The photocatalytically active TiO2 thin film was deposited on the titanium substrate plate by chemical vapor deposition (CVD method, and the photoelectrocatalytic degradation of sodium oxalate was investigated by TiO2 thin film reactor prepared in this study with additional electric potential at 365 nm irradiation. The batch system was chosen in this experiment, and the controlled parameters were pH, different supporting electrolytes, applied additional potential, and different electrolyte solutions that were examined and discussed. The experimental results revealed that the additional applied potential in photocatalytic reaction could prohibit recombination of electron/hole pairs, but the photoelectrocatalytic effect was decreased when the applied electric potential was over 0.25 V. Among the electrolyte solutions added, sodium sulfate improved the photoelectrocatalytic effect most significantly. At last, the better photoelectrocatalytic degradation of sodium oxalate occurred at pH 3 when comparing the pH influence.

  20. Aggregate formation of eosin-Y adsorbed on nanocrystalline TiO2 films

    Science.gov (United States)

    Yaguchi, Kaori; Furube, Akihiro; Katoh, Ryuzi

    2012-11-01

    We have studied the adsorption of eosin-Y on nanocrystalline TiO2 films with two different solvents namely acetonitrile (ACN) and ethanol (EtOH). A Langmuir-type adsorption isotherm was observed with ACN. In contrast, a Freundlich-type adsorption isotherm was observed with EtOH, suggesting that EtOH molecules co-adsorbed on TiO2 surface. Absorption spectra of the dye adsorbed films clearly show aggregate formation at high concentrations of dye in the solutions. From the analysis of the spectra, we conclude that head-to-tail type aggregates are observed with ACN, whereas various types of aggregates, including H-type and head-to-tail type aggregates, are observed with EtOH.

  1. Nanoscale self-recovery of resistive switching in Ar+ irradiated TiO2-x films

    Science.gov (United States)

    Barman, A.; Saini, C. P.; Sarkar, P. K.; Das, D.; Dhar, S.; Singh, M.; Sinha, A. K.; Kanjilal, D.; Gupta, M.; Phase, D. M.; Kanjilal, A.

    2017-11-01

    Nanoscale evidence of self-recovery in resistive switching (RS) behavior was found in TiO2-x film by conductive atomic force microscopy when exposed to Ar+-ions above a threshold fluence of 1  ×  1016 ions cm-2. This revealed an evolution and gradual disappearance of bipolar RS-loops, followed by reappearance with increasing number of voltage sweep. This was discussed in the realm of oxygen vacancy (OV) driven formation, dissolution and reformation of conducting filaments. The presence of OVs in ion-beam irradiated TiO2-x films was evidenced by decreasing trend of work function in scanning-Kelvin probe microscopy, and was further verified by x-ray absorption near edge spectroscopy at Ti and O-K edges.

  2. Solar photocatalytic activity of TiO2 modified with WO3 on the degradation of an organophosphorus pesticide

    International Nuclear Information System (INIS)

    Ramos-Delgado, N.A.; Gracia-Pinilla, M.A.; Maya-Treviño, L.; Hinojosa-Reyes, L.; Guzman-Mar, J.L.; Hernández-Ramírez, A.

    2013-01-01

    Highlights: • TiO 2 and WO 3 /TiO 2 (2 and 5%) were tested in the photocatalytic malathion degradation. • The use of solar radiation in the photocatalytic degradation process was evaluated. • Modified catalyst showed greater photocatalytic activity than pure TiO 2 . • The mineralization rate was improved when WO 3 content on TiO 2 was 2%. -- Abstract: In this study, the solar photocatalytic activity (SPA) of WO 3 /TiO 2 photocatalysts synthesized by the sol–gel method with two different percentages of WO 3 (2 and 5%wt) was evaluated using malathion as a model contaminant. For comparative purpose bare TiO 2 was also prepared by sol–gel process. The powders were characterized by X-ray diffraction (XRD), Raman spectroscopy, diffuse reflectance UV–vis spectroscopy (DRUV–vis), specific surface area by the BET method (SSA BET ), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM) and scanning transmission electron microscopy with a high annular angle dark field detector (STEM-HAADF). The XRD, Raman, HRTEM and STEM-HAADF analyses indicated that WO 3 was present as a monoclinic crystalline phase with nanometric cluster sizes (1.1 ± 0.1 nm for 2% WO 3 /TiO 2 and 1.35 ± 0.3 nm for 5% WO 3 /TiO 2 ) and uniformly dispersed on the surface of TiO 2 . The particle size of the materials was 19.4 ± 3.3 nm and 25.6 ± 3 nm for 2% and 5% WO 3 /TiO 2 , respectively. The SPA was evaluated on the degradation of commercial malathion pesticide using natural solar light. The 2% WO 3 /TiO 2 photocatalyst exhibited the best photocatalytic activity achieving 76% of total organic carbon (TOC) abatement after 300 min compared to the 5% WO 3 /TiO 2 and bare TiO 2 photocatalysts, which achieved 28 and 47% mineralization, respectively. Finally, experiments were performed to assess 2% WO 3 /TiO 2 catalyst activity on repeated uses; after several successive cycles its photocatalytic activity was retained showing long-term stability

  3. Annealing effect on the structural, morphological and electrical properties of TiO2/ZnO bilayer thin films

    Science.gov (United States)

    Khan, M. I.; Imran, S.; Shahnawaz; Saleem, Muhammad; Ur Rehman, Saif

    2018-03-01

    The effect of annealing temperature on the structural, morphological and electrical properties of TiO2/ZnO (TZ) thin films has been observed. Bilayer thin films of TiO2/ZnO are deposited on FTO glass substrate by spray pyrolysis method. After deposition, these films are annealed at 573 K, 723 K and 873 K. XRD shows that TiO2 is present in anatase phase only and ZnO is present in hexagonal phase. No other phases of TiO2 and ZnO are present. Also, there is no evidence of other compounds like Zn-Ti etc. It also shows that the average grain size of TiO2/ZnO films is increased by increasing annealing temperature. AFM (Atomic force microscope) showed that the average roughness of TiO2/ZnO films is decreased at temperature 573-723 K and then increased at 873 K. The calculated average sheet resistivity of thin films annealed at 573 K, 723 K and 873 K is 152.28 × 102, 75.29 × 102 and 63.34 × 102 ohm-m respectively. This decrease in sheet resistivity might be due to the increment of electron concentration with increasing thickness and the temperature of thin films.

  4. Preparation of TiO2 thin films from autoclaved sol containing needle-like anatase crystals

    International Nuclear Information System (INIS)

    Ge Lei; Xu Mingxia; Fang Haibo; Sun Ming

    2006-01-01

    A new inorganic sol-gel method was introduced in this paper to prepare TiO 2 thin films. The autoclaved sol with needle-like anatase crystals was synthesized using titanyl sulfate (TiOSO 4 ) and peroxide (H 2 O 2 ) as starting materials. The transparent anatase TiO 2 thin films were prepared on glass slides from the autoclaved sol by sol-gel dip-coating method. A wide range of techniques such as Fourier transform infrared transmission spectra (FT-IR), X-ray diffraction (XRD), thermogravimetry-differential thermal analysis (TG-DTA), scanning electron microscopes, X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible spectrum were applied to characterize the autoclaved sol and TiO 2 thin films. The results indicate that the autoclaved sol is flavescent, semitransparent and stable at room temperature. The anatase crystals of TiO 2 films connect together to form net-like structure after calcined and the films become uniform with increasing heating temperature. The surface of the TiO 2 films contain not only Ti and O elements, but also a small amount of N and Na elements diffused from substrates during heat treatment. The TiO 2 films are transparent and their maximal light transmittances exceed 80% under visible light region

  5. Low-temperature liquid phase deposited TiO{sub 2} films on stainless steel for photogenerated cathodic protection applications

    Energy Technology Data Exchange (ETDEWEB)

    Lei, C.X.; Zhou, H. [College of Materials, Xiamen University, Xiamen 361005 (China); Feng, Z.D., E-mail: zdfeng@xmu.edu.cn [College of Materials, Xiamen University, Xiamen 361005 (China); Zhu, Y.F.; Du, R.G. [College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005 (China)

    2011-06-01

    The low-temperature synthesis of anatase TiO{sub 2} films was an imperative requirement for their application to corrosion prevention of metals. In this paper, a liquid phase deposition (LPD) technique was developed to prepare TiO{sub 2} films on SUS304 stainless steel (304SS) at a relatively low temperature (80 deg. C). The as-prepared films were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy and X-ray photon spectroscopy (XPS). It was observed that a dense and crack-free anatase TiO{sub 2} film with a thickness about 300 nm was obtained. The film contained some fluorine and nitrogen elements, and the amounts of these impurities were greatly decreased upon calcination. Under the white light illumination, the electrode potential of TiO{sub 2} coated 304SS rapidly shifted to a more negative direction. Moreover, the photopotential of TiO{sub 2}/304SS electrode showed more negative values with increased film thickness. In conclusion, the photogenerated cathodic protection of 304SS was achieved by the low-temperature LPD-derived TiO{sub 2} film.

  6. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Damon Rafieian

    2015-09-01

    Full Text Available We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx<2, obtained by sputtering at relatively low oxygen concentration, formed rutile upon annealing in air, whereas stoichiometric films formed anatase. This route therefore presents a formation route for rutile films via lower (<500 °C temperature pathways. The dynamics of the annealing process were followed by in situ ellipsometry, showing the optical properties transformation. The final crystal structures were identified by XRD. The anatase film obtained by this deposition method displayed high carriers mobility as measured by time-resolved microwave conductance. This also confirms the high photocatalytic activity of the anatase films.

  7. Mesoporous films of TiO2 as efficient photocatalysts for the purification of water

    Czech Academy of Sciences Publication Activity Database

    Rathouský, Jiří; Kalousek, Vít; Kolář, Michal; Jirkovský, Jaromír

    2011-01-01

    Roč. 10, č. 3 (2011), s. 419-424 ISSN 1474-905X R&D Projects: GA ČR GA104/08/0435; GA ČR GD203/08/H032; GA MŠk 1M0577 Institutional research plan: CEZ:AV0Z40400503 Keywords : TiO2 * mesoporous films * photocatalyst Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 2.584, year: 2011

  8. Strain-controlled optical absorption in epitaxial ferroelectric BaTiO.sub.3./sub. films

    Czech Academy of Sciences Publication Activity Database

    Chernova, Ekaterina; Pacherová, Oliva; Chvostová, Dagmar; Dejneka, Alexandr; Kocourek, Tomáš; Jelínek, Miroslav; Tyunina, Marina

    2015-01-01

    Roč. 106, č. 19 (2015), "192903-1"-"192903-4" ISSN 0003-6951 R&D Projects: GA ČR GA15-13778S; GA ČR GA15-15123S Institutional support: RVO:68378271 Keywords : thin-films * polarization * evolution * SrTiO 3 Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.142, year: 2015

  9. PLD prepared bioactive BaTiO.sub.3./sub. films on TiNb implants

    Czech Academy of Sciences Publication Activity Database

    Jelínek, Miroslav; Vaněk, Přemysl; Tolde, Z.; Buixaderas, Elena; Kocourek, Tomáš; Studnička, Václav; Drahokoupil, Jan; Petzelt, Jan; Remsa, Jan; Tyunina, Marina

    2017-01-01

    Roč. 70, Jan (2017), s. 334-339 ISSN 0928-4931 R&D Projects: GA ČR(CZ) GA15-05864S; GA ČR(CZ) GA15-01558S Institutional support: RVO:68378271 Keywords : BaTiO 3 * thin films * pld * implants * TiNb * ferroelectricity Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.)

  10. Novel Synthesis of the TiO2(B) Multilayer Templated Films

    Czech Academy of Sciences Publication Activity Database

    Procházka, Jan; Kavan, Ladislav; Zukalová, Markéta; Frank, Otakar; Kalbáč, Martin; Zukal, Arnošt; Klementová, Mariana; Carbone, D.; Graetzel, M.

    2009-01-01

    Roč. 21, č. 8 (2009), s. 1457-1464 ISSN 0897-4756 R&D Projects: GA MŠk LC510; GA AV ČR IAA400400804; GA AV ČR KAN200100801; GA AV ČR KAN100500652 Institutional research plan: CEZ:AV0Z40400503; CEZ:AV0Z40320502 Keywords : TiO2(B) * synthesis * films Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 5.368, year: 2009

  11. Electric-field-induced monoclinic phase in (Ba,Sr)TiO3 thin film

    International Nuclear Information System (INIS)

    Anokhin, A. S.; Yuzyuk, Yu. I.; Golovko, Yu. I.; Mukhortov, V. M.; El Marssi, M.

    2011-01-01

    We have studied electric-field-induced symmetry lowering in the tetragonal (001)-oriented heteroepitaxial (Ba 0.8 Sr 0.2 )TiO 3 thin film deposited on (001)MgO substrate. Polarized micro-Raman spectra were recorded from the film area in between two planar electrodes deposited on the film surface. Presence of c domains with polarization normal to the substrate was confirmed from polarized Raman study under zero field, while splitting and hardening of the E(TO) soft mode and polarization changes in the Raman spectra suggest monoclinic symmetry under external electric field.

  12. Thin nanostructured crystalline TiO{sub 2} films and their applications in solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Cheng Yajun

    2007-06-15

    Research on thin nanostructured crystalline TiO{sub 2} films has attracted considerable interests because of their intriguing physical properties and potential applications in photovoltaics. Nanostructured TiO{sub 2} film plays an important role in the TiO{sub 2} based dye-sensitized solar cells because they act as a substrate for the adsorption of dye molecules and a matrix for the transportation of electrons as well. Thus they can influence the solar cell performance significantly. Consequently, the control of the morphology including the shape, size and size distribution of the TiO{sub 2} nanostructures is critical to tune and optimize the performance of the solar cells. To control the TiO{sub 2} morphology, a strategy using amphiphilic block copolymer as templating agent coupled with sol-gel chemistry has been applied. Especially, a good-poor solvent pair induced phase separation process has been developed to guide the microphase separation behavior of the block copolymers. The amphiphilic block copolymers used include polystyrene-block-poly (ethylene oxide) (PS-b-PEO), poly (methyl methacrylate)-block-poly (ethylene oxide) (PMMA-b-PEO), and poly (ethylene oxide)-block-polystyrene-block-poly (ethylene oxide) (PEO-b-PS-b-PEO). The block copolymer undergoes a good-poor-solvent pair induced phase separation in a mixed solution of 1, 4-dioxane or N, N-dimethyl formamide (DMF), concentrated hydrochloric acid (HCl) and Titanium tetraisopropoxide (TTIP). Specifically, in the system of PS-b-PEO, a morphology phase diagram of the inorganic-copolymer composite films was mapped by adjusting the weight fractions among 1, 4-dioxane, HCl, and TTIP in solution. The amorphous TiO{sub 2} within the titania-block copolymer composite films was crystallized by calcination at temperatures above 400 C, where the organic block copolymer was simultaneously burned away. This strategy is further extended to other amphiphilic block copolymers of PMMA-b-PEO and PEO-b-PS-b-PEO, where the

  13. Photocatalytic degradation of Lissamine Green B dye by using nanostructured sol–gel TiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Ćurković, Lidija, E-mail: lcurkov@fsb.hr [Faculty of Mechanical Engineering and Naval Architecture, University of Zagreb, Ivana Lučića 5, 10000 Zagreb (Croatia); Ljubas, Davor [Faculty of Mechanical Engineering and Naval Architecture, University of Zagreb, Ivana Lučića 5, 10000 Zagreb (Croatia); Šegota, Suzana [Ruđer Bošković Institute, Bijenička 54, 10000 Zagreb (Croatia); Bačić, Ivana [Forensic Science Centre Ivan Vučetić, Ministry of the Interior, Ilica 335, Zagreb (Croatia)

    2014-08-01

    Highlights: • Nanostructured photocatalytic TiO{sub 2} films were prepared by sol–gel methods. • The addition of PEG to the TiO{sub 2} film changes the surface morphology and roughness parameters. • The addition of PEG to the initial sols increases photocatalytic properties of TiO{sub 2}. • LGB water solution could be decolourised within 2 h. • The influence of photolysis and adsorption on the LGB removal from the solution is negligible. - Abstract: Nanostructured sol–gel TiO{sub 2} films were prepared on a glass substrate by means of the dip-coating technique with titanium tetraisopropoxide as a precursor. TiO{sub 2} sols were synthesized with and without the addition of polyethylene glycol (PEG) as a structure-directing agent. The synthesized sol–gel TiO{sub 2} were characterized by XRD, AFM, FTIR and Micro-Raman spectroscopy. The photocatalytic activity of the films was evaluated by the photocatalytic degradation of Lissamine Green B (LGB) dye (dissolved in water) as a model pollutant with the predominant irradiation wavelength of 365 nm (UV-A). It was found that the addition of PEG to the initial sol affects the surface morphology and the photocatalytic properties of prepared sol–gel TiO{sub 2} films. AFM analysis confirmed the presence of nanostructured sol–gel titania films on the glass substrate. Roughness parameters (R{sub a}, R{sub q}, and Z{sub max}) of the sol–gel TiO{sub 2} film with the addition of PEG are higher than the parameters of the sol–gel TiO{sub 2} film without the addition of PEG. The TiO{sub 2} film prepared with the addition of PEG has a higher surface density (a larger active surface area) and better photocatalytic activity in the degradation of the LGB dye solution than the TiO{sub 2} film prepared without the addition of PEG.

  14. Influence of crystallinity on CO gas sensing for TiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Seeley, Zachary Mark [School of Mechanical and Materials Engineering, Washington State University, Pullman, WA 99164-2920 (United States); Bandyopadhyay, Amit [School of Mechanical and Materials Engineering, Washington State University, Pullman, WA 99164-2920 (United States)], E-mail: amitband@wsu.edu; Bose, Susmita [School of Mechanical and Materials Engineering, Washington State University, Pullman, WA 99164-2920 (United States)

    2009-08-15

    In the present research, carbon monoxide (CO) gas sensing response was studied for TiO{sub 2} thick films calcined and sintered between 700 and 900 deg. C. Crystalline phase, crystallite size, surface area, particle size, and amorphous content were measured for the calcined powder. Crystallinity of the powder was found to affect sensing response significantly towards CO. Anatase phase of TiO{sub 2} thick film was stable up to 900 deg. C however, as calcination temperature increased from 700 to 900 deg. C, surface area and amorphous phase content decreased. Films calcined and sintered at 700 deg. C showed a lower response towards CO than those calcined at 800 deg. C. Upon increasing the calcination temperature further, particle growth and reduced surface area hindered the sensing response. A calcination temperature of 800 deg. C was necessary to achieve sufficient order in the crystal structure leading to more efficient adsorption and desorption of oxygen ions on the surface of TiO{sub 2}.

  15. TiO{sub 2} and TiO{sub 2}-SiO{sub 2} thin films and powders by one-step soft-solution method: Synthesis and characterizations

    Energy Technology Data Exchange (ETDEWEB)

    Ennaoui, A.; Sankapal, B.R.; Skryshevsky, V.; Lux-Steiner, M.Ch. [Division Solar Energy Research, Department Heterogeneous Material Systems, Hahn-Meitner-Institut, Glienicker Strasse 100, 14109 Berlin (Germany)

    2006-06-15

    Simple soft-solution method has been developed to synthesize films and powders of TiO{sub 2} and mixed TiO{sub 2}-SiO{sub 2} at relatively low temperatures. This method is simple and inexpensive. Furthermore, reactor can be designed for large-scale applications as well as to produce large quantities of composite powders in a single step. For the preparation of TiO{sub 2}, we used aqueous acidic medium containing TiOSO{sub 4} and H{sub 2}O{sub 2}, which results in a peroxo-titanium precursor while colloidal SiO{sub 2} has been added to the precursor for the formation of TiO{sub 2}-SiO{sub 2}. Post annealing at 500{sup o}C is necessary to have anatase structure. Resulting films and powders were characterized by different techniques. TiO{sub 2} (anatase) phase with (101) preferred orientation has been obtained. Also in TiO{sub 2}-SiO{sub 2} mixed films and powders, TiO{sub 2} (anatase) phase was found. Fourier transform infrared spectroscopy (FTIR) results for TiO{sub 2} and mixed TiO{sub 2}-SiO{sub 2} films have been presented and discussed. The method developed in this paper allowed obtaining compact and homogeneous TiO{sub 2} films. These compact films are highly photoactive when TiO{sub 2} is used as photo anode in an photoelectrochemical cell. Nanoporous morphology is obtained when SiO{sub 2} colloids are added into the solution. (author)

  16. N, Fe and WO3 modified TiO2 for degradation of formaldehyde

    International Nuclear Information System (INIS)

    Tong Haixia; Zhao Li; Li Dan; Zhang Xiongfei

    2011-01-01

    Graphical abstract: The undoped TiO 2 powder (T(0)) shows strong photoabsorption only at wavelengths shorter than 400 nm, and while Fe 3+ and N-doped TiO 2 nanoparticles show photoabsorption in visible region and the absorption edge shifts to a longer wavelength. WO 3 compounding also benefits the photoabsorption in visible region. Display Omitted Highlights: → The preparation of the catalysts co-doped by Fe, N and compounded by WO 3 . → The obvious sculptured 'pattern' of the catalysts doped by Fe in the SEM images. → Strengthened photoabsorption to visible light of the modified catalysts from UV-DRS analysis. - Abstract: Butyltitanate, ethanol and glacial acetic acid were chosen as titanium source, solvent and chelating agent, respectively, via a sol-gel method combined impregnation method to prepare N, Fe co-doped and WO 3 compounded photocatalyst TiO 2 powder. The synthesized products were characterized by X-ray diffraction (XRD), diffuse reflectance UV-Vis spectra (UV-DRS), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Photocatalytic degradation of formaldehyde was employed to investigate the catalytic activity. The results show that the degradation rate is 77.61% in 180 min under UV light irradiation when the concentration of N is fixed on, and the optimum proportioning ratio of n(Fe):n(W):n(Ti) is 0.5:2:100.

  17. Preparation of Porous F-WO3/TiO2 Films with Visible-Light Photocatalytic Activity by Microarc Oxidation

    OpenAIRE

    Yeh, Chung-Wei; Wu, Kee-Rong; Hung, Chung-Hsuang; Chang, Hao-Cheng; Hsu, Chuan-Jen

    2012-01-01

    Porous F-WO3/TiO2 (mTiO2) films are prepared on titanium sheet substrates using microarc oxidation (MAO) technique. The X-ray diffraction patterns show that visible-light (Vis) enabling mTiO2 films with a very high content of anatase TiO2 and high loading of WO3 are successfully synthesized at a low applied voltage of 300 V using electrolyte contenting NaF and Na2WO4 without subsequent heat treatment. The cross-sectional transmission electron microscopy micrograph reveals that the mTiO2 films...

  18. TiO2 coated SnO2 nanosheet films for dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Cai Fengshi; Yuan Zhihao; Duan Yueqing; Bie Lijian

    2011-01-01

    TiO 2 -coated SnO 2 nanosheet (TiO 2 -SnO 2 NS) films about 300 nm in thickness were fabricated on fluorine-doped tin oxide glass by a two-step process with facile solution-grown approach and subsequent hydrolysis of TiCl 4 aqueous solution. The as-prepared TiO 2 -SnO 2 NSs were characterized by scanning electron microscopy and X-ray diffraction. The performances of the dye-sensitized solar cells (DSCs) with TiO 2 -SnO 2 NSs were analyzed by current-voltage measurements and electrochemical impedance spectroscopy. Experimental results show that the introduction of TiO 2 -SnO 2 NSs can provide an efficient electron transition channel along the SnO 2 nanosheets, increase the short current density, and finally improve the conversion efficiency for the DSCs from 4.52 to 5.71%.

  19. Fabrication of assembled ZnO/TiO2 heterojunction thin film transistors using solution processing technique

    Science.gov (United States)

    Liau, Leo Chau-Kuang; Lin, Yun-Guo

    2015-01-01

    Ceramic-based metal-oxide-semiconductor (MOS) field-effect thin film transistors (TFTs), which were assembled by ZnO and TiO2 heterojunction films coated using solution processing technique, were fabricated and characterized. The fabrication of the device began with the preparation of ZnO and TiO2 films by spin coating. The ZnO and TiO2 films that were stacked together and annealed at 450 °C were characterized as a p-n junction diode. Two types of the devices, p-channel and n-channel TFTs, were produced using different assemblies of ZnO and TiO2 films. Results show that the p-channel TFTs (p-TFTs) and n-channel TFTs (n-TFTs) using the assemblies of ZnO and TiO2 films were demonstrated by source-drain current vs. drain voltage (IDS-VDS) measurements. Several electronic properties of the p- and n- TFTs, such as threshold voltage (Vth), on-off ratio, channel mobility, and subthreshold swing (SS), were determined by current-voltage (I-V) data analysis. The ZnO/TiO2-based TFTs can be produced using solution processing technique and an assembly approach.

  20. Structure and Properties of La2O3-TiO2 Nanocomposite Films for Biomedical Applications

    Science.gov (United States)

    Zhang, Lin; Sun, Zhi-Hua; Yu, Feng-Mei; Chen, Hong-Bin

    2011-01-01

    The hemocompatibility of La2O3-doped TiO2 films with different concentration prepared by radio frequency (RF) sputtering was studied. The microstructures and blood compatibility of TiO2 films were investigated by scan electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and UV-visible optical absorption spectroscopy, respectively. With the increasing of the La2O3 concentrations, the TiO2 films become smooth, and the grain size becomes smaller. Meanwhile, the band gap of the samples increases from 2.85 to 3.3 eV with increasing of the La2O3 content in TiO2 films from 0 to 3.64%. La2O3-doped TiO2 films exhibit n-type semiconductor properties due to the existence of Ti2+ and Ti3+. The mechanism of hemocompatibility of TiO2 film doped with La2O3 was analyzed and discussed. PMID:22162671

  1. Visible light photoelectrocatalysis with salicylic acid-modified TiO2 nanotube array electrode for p-nitrophenol degradation

    International Nuclear Information System (INIS)

    Wang Xin; Zhao Huimin; Quan Xie; Zhao Yazhi; Chen Shuo

    2009-01-01

    This research focused on immersion method synthesis of visible light active salicylic acid (SA)-modified TiO 2 nanotube array electrode and its photoelectrocatalytic (PEC) activity. The SA-modified TiO 2 nanotube array electrode was synthesized by immersing in SA solution with an anodized TiO 2 nanotube array electrode. Scanning electron microscope (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), infrared spectroscopy (IR), UV-vis diffuse reflectance spectrum (DRS), and Surface photovoltage (SPV) were used to characterize this electrode. It was found that SA-modified TiO 2 nanotube array electrode absorbed well into visible region and exhibited enhanced visible light PEC activity on the degradation of p-nitrophenol (PNP). The degradation efficiencies increased from 63 to 100% under UV light, and 79-100% under visible light (λ > 400 nm), compared with TiO 2 nanotube array electrode. The enhanced PEC activity of SA-modified TiO 2 nanotube array electrode was attributed to the amount of surface hydroxyl groups introduced by SA-modification and the extension of absorption wavelength range.

  2. Fabrication and characterization of nanostructured anatase TiO{sub 2} films prepared by electrochemical anodization and their photocatalytic properties

    Energy Technology Data Exchange (ETDEWEB)

    Yurddaskal, Metin [Dokuz Eylul University, The Graduate School of Natural and Applied Sciences, Buca 35390, Izmir (Turkey); Dokuz Eylul University, Center for Fabrication and Applications of Electronic Materials (EMUM), Buca, 35390, Izmir (Turkey); Dikici, Tuncay, E-mail: tuncay.dikici@ikc.edu.tr [Dokuz Eylul University, The Graduate School of Natural and Applied Sciences, Buca 35390, Izmir (Turkey); Izmir Katip Celebi University, Department of Materials Science and Engineering, Cigli 35620, Izmir (Turkey); Yildirim, Serdar [Dokuz Eylul University, The Graduate School of Natural and Applied Sciences, Buca 35390, Izmir (Turkey); Dokuz Eylul University, Center for Fabrication and Applications of Electronic Materials (EMUM), Buca, 35390, Izmir (Turkey); Yurddaskal, Melis [Celal Bayar University, Department of Mechanical Engineering, Muradiye, 45140 Manisa (Turkey); Toparli, Mustafa; Celik, Erdal [Dokuz Eylul University, Center for Fabrication and Applications of Electronic Materials (EMUM), Buca, 35390, Izmir (Turkey); Dokuz Eylul University, Department of Metallurgical and Materials Engineering, Buca 35390, Izmir (Turkey)

    2015-12-05

    In this study, nanostructured anatase titanium dioxide (TiO{sub 2}) films were fabricated by electrochemical anodization of titanium first, and then annealed at 500 °C for 2 h. Effect of electrolyte concentration, anodization time and electrolyte temperature on the surface morphology of the resulting TiO{sub 2} thin films were investigated. The phase structures, surface morphology and chemical composition were analyzed using X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). The photocatalytic activity tests of the samples were evaluated by the degradation of aqueous methylene blue (MB) solutions under UV light illumination for different periods of time. The results showed that the structure of nanostructured TiO{sub 2} films depended strongly on the anodization parameters. It was found that there were micro-scale pores (<10 μm) and nano-scale pores (diameter in the range from 40 to 70 nm) on the anodized titanium surfaces. This study indicated that structures, surface morphology, and surface area of the nanostructured anatase TiO{sub 2} films played an important role on their photocatalytic performance. The results clearly proved that nanostructured anatase TiO{sub 2} film prepared with optimum process parameters resulted in enhancement of the photocatalytic activity. - Highlights: • TiO{sub 2} thin films were prepared on titanium substrates by electrochemical anodization at 30 V. • Effect of various anodization parameters on the photocatalytic activity of titanium was investigated. • Micro- and nanoscale TiO{sub 2} pores formed on the titanium by anodizing. • Surface morphology of the TiO{sub 2} films plays an important role on the photocatalytic performance. • The sample anodized for 240 min showed the highest photocatalytic activity.

  3. Hydrothermal growth of double-layer TiO{sub 2} nanostructure film for quantum dot sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Feng Shuanglong; Yang Junyou, E-mail: jyyang@mail.hust.edu.cn; Liu Ming; Zhu Hu; Zhang Jiansheng; Li Gen; Peng Jiangying; Liu Qiongzhen

    2012-01-31

    A double-layer (DL) film with a TiO{sub 2} nanosheet-layer on a layer of TiO{sub 2} nanorod-array, was synthesized on a transparent conductive fluorine-doped tin oxide substrate by a two-step hydrothermal method. Starting from the precursors of NaSeSO{sub 3}, CdSO{sub 4} and the complex of N(CH{sub 2}COOK){sub 3}, CdSe quantum dots (QDs) were grown on the DL-TiO{sub 2} substrate by chemical bath deposition method. The samples were characterized by X-ray diffraction, Scanning electron microscopy, Energy dispersion spectroscopy, and their optical scattering property was measured by light reflection spectrometry. Some CdSe QDs sensitized DL-TiO{sub 2} films serve as the photoanodes, were assembled into solar cell devices and their photovoltaic performance were also characterized. The short circuit current and open-circuit voltage of the solar cells range from 0.75 to 4.05 mA/cm{sup 2} and 0.20 - 0.42 V under the illumination of one sun (AM1.5, 100 mW/cm{sup 2}), respectively. The photocurrent density of the DL-TiO{sub 2} film is five times higher than that of a bare TiO{sub 2} nanorod array photoelectrode cell. - Highlights: Black-Right-Pointing-Pointer A two-step hydrothermal deposition method was used to deposit TiO{sub 2} films. Black-Right-Pointing-Pointer Double-layer TiO{sub 2} films were synthesized on transparent FTO substrate. Black-Right-Pointing-Pointer The bi-functional character of the electrode were confirmed. Black-Right-Pointing-Pointer Photocurrent density of DL-film electrode was enhanced 5 times than a single film.

  4. Effect of laser irradiation on the structural, morphological and electrical properties of polycrystalline TiO2 thin films

    Directory of Open Access Journals (Sweden)

    M.I. Khan

    Full Text Available TiO2 thin film is deposited on glass substrate by sol-gel dip coating technique. After deposition, films were irradiated by continuous wave (CW diode laser at an angle of 45°. XRD shows both the anatase and brookite phases of TiO2. Nano particles of regular and control sizes are appeared in SEM micrographs. Therefore, shape and size of nano particles can be control by using Laser irradiation. The average sheet resistivity of TiO2 thin film irradiated by 0, 2, 4 and 6 min are 6.72 × 105, 5.32 × 105, 3.44 × 105 and 4.95 × 105 (ohm-m respectively, according to four point probe. Keywords: TiO2, Diode laser, XRD, SEM

  5. Preparation of mesoporous Ag-containing TiO{sub 2} heterojunction film and its photocatalytic property

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Q. Y., E-mail: wangqingyao0532@163.com [Ludong University, School of Chemistry and Materials Science (China); Qiao, J. L. [Jilin Agricultural University, College of Horticulture (China); Cui, X. Y. [Mudanjiang Medical University, School of Public Health (China); Zhong, J. S. [Hangzhou Dianzi University, College of Materials and Environmental Engineering (China); Xu, Y. B.; Zhang, S. H.; Zhang, Q. H.; Chang, P.; Li, M.; Zhang, C.; Gao, S. M., E-mail: gaosm@ustc.edu [Ludong University, School of Chemistry and Materials Science (China)

    2015-03-15

    Mesoporous Ag/TiO{sub 2} heterojunction films (Ag-MTHF) with enhanced photocatalytic activity were synthesized by a three-step approach including an electrochemical anodization technique followed by successive ionic layer adsorption and reaction (SILAR) and solvothermal methods. The distribution of Ag nanoparticles on the inner structure of the mesoporous TiO{sub 2} film was confirmed by field emission scanning electron (FE-SEM) and transmission electron microscopes (TEM). The formation progress of the novel mesoporous Ag/TiO{sub 2} nanojunction film with Ag average diameter of 17 nm was illuminated. The formed nanojunction between Ag and TiO{sub 2} nanoparticles largely enhanced the photocatalytic degradation of methyl orangey (MO), and the corresponding mechanism was proposed.

  6. Study of the photophysical properties of composite film assembled of porphyrin and TiO{sub 2} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Feng, X -S; Kang, S -Z; Liu, H -G; Mu, J [Shandong Univ., Jinan (China). Key Lab. for Colloid and Interface Chem. of Education Ministry

    1999-09-08

    In this paper, the formation, structure, and photophysical properties of functional mixed film of 5,10,15,20-tetra-4-(2-decanoic acid)phenyl porphyrin (TDPP) with TiO{sub 2} nanoparticles formed from the 2D sol-gel process of tetrabutoxyltitanium (TBT) at the air/water interface is reported. The composite multilayer films were assembled by transferring the mixed monolayer onto quartz plates. The diameter distribution and crystallinity of TiO{sub 2} particles were estimated by TEM observation and electron diffraction. The sensitization of TDPP upon TiO{sub 2} nanoparticles was confirmed by the spectral changes of UV-visible absorption and fluorescence of TDPP in the composite films. Furthermore the photosensitization greatly affected the photocatalytic activity of TiO{sub 2} particles with respect to the degradation of methylene blue (MO). (orig.)

  7. Fluorescence imaging technology (FI) for high-throughput screening of selenide-modified nano-TiO2 catalysts.

    Science.gov (United States)

    Wang, Liping; Lee, Jianchao; Zhang, Meijuan; Duan, Qiannan; Zhang, Jiarui; Qi, Hailang

    2016-02-18

    A high-throughput screening (HTS) method based on fluorescence imaging (FI) was implemented to evaluate the catalytic performance of selenide-modified nano-TiO2. Chemical ink-jet printing (IJP) technology was reformed to fabricate a catalyst library comprising 1405 (Ni(a)Cu(b)Cd(c)Ce(d)In(e)Y(f))Se(x)/TiO2 (M6Se/Ti) composite photocatalysts. Nineteen M6Se/Tis were screened out from the 1405 candidates efficiently.

  8. Low-temperature preparation of rutile-type TiO2 thin films for optical coatings by aluminum doping

    Science.gov (United States)

    Ishii, Akihiro; Kobayashi, Kosei; Oikawa, Itaru; Kamegawa, Atsunori; Imura, Masaaki; Kanai, Toshimasa; Takamura, Hitoshi

    2017-08-01

    A rutile-type TiO2 thin film with a high refractive index (n), a low extinction coefficient (k) and small surface roughness (Ra) is required for use in a variety of optical coatings to improve the controllability of the reflection spectrum. In this study, Al-doped TiO2 thin films were prepared by pulsed laser deposition, and the effects of Al doping on their phases, optical properties, surface roughness and nanoscale microstructure, including Al distribution, were investigated. By doping 5 and 10 mol%Al, rutile-type TiO2 was successfully prepared under a PO2 of 0.5 Pa at 350-600 °C. The nanoscale phase separation in the Al-doped TiO2 thin films plays an important role in the formation of the rutile phase. The 10 mol%Al-doped rutile-type TiO2 thin film deposited at 350 °C showed excellent optical properties of n ≈ 3.05, k ≈ 0.01 (at λ = 400 nm) and negligible surface roughness, at Ra ≈ 0.8 nm. The advantages of the superior optical properties and small surface roughness of the 10 mol%Al-doped TiO2 thin film were confirmed by fabricating a ten-layered dielectric mirror.

  9. Rapid fabrication of mesoporous TiO2 thin films by pulsed fibre laser for dye sensitized solar cells

    Science.gov (United States)

    Hadi, Aseel; Alhabradi, Mansour; Chen, Qian; Liu, Hong; Guo, Wei; Curioni, Michele; Cernik, Robert; Liu, Zhu

    2018-01-01

    In this paper we demonstrate for the first time that a fibre laser with a wavelength of 1070 nm and a pulse width of milliseconds can be applied to generate mesoporous nanocrystalline (nc) TiO2 thin films on ITO coated glass in ambient atmosphere, by complete vaporisation of organic binder and inter-connection of TiO2 nanoparticles, without thermally damaging the ITO layer and the glass substrate. The fabrication of the mesoporous TiO2 thin films was achieved by stationary laser beam irradiation of 1 min. The dye sensitized solar cell (DSSC) with the laser-sintered TiO2 photoanode reached higher power conversion efficiency (PCE) of 3.20% for the TiO2 film thickness of 6 μm compared with 2.99% for the furnace-sintered. Electrochemical impedance spectroscopy studies revealed that the laser sintering under the optimised condition effectively decreased charge transfer resistance and increased electron lifetime of the TiO2 thin films. The use of the fibre laser with over 40% wall-plug efficiency offers an economically-feasible, industrial viable solution to the major challenge of rapid fabrication of large scale, mass production of mesoporous metal oxide thin film based solar energy systems, potentially for perovskite and monolithic tandem solar cells, in the future.

  10. In situ scanning tunneling microscopy study of Ca-modified rutile TiO2(110 in bulk water

    Directory of Open Access Journals (Sweden)

    Giulia Serrano

    2015-02-01

    Full Text Available Despite the rising technological interest in the use of calcium-modified TiO2 surfaces in biomedical implants, the Ca/TiO2 interface has not been studied in an aqueous environment. This investigation is the first report on the use of in situ scanning tunneling microscopy (STM to study calcium-modified rutile TiO2(110 surfaces immersed in high purity water. The TiO2 surface was prepared under ultrahigh vacuum (UHV with repeated sputtering/annealing cycles. Low energy electron diffraction (LEED analysis shows a pattern typical for the surface segregation of calcium, which is present as an impurity on the TiO2 bulk. In situ STM images of the surface in bulk water exhibit one-dimensional rows of segregated calcium regularly aligned with the [001] crystal direction. The in situ-characterized morphology and structure of this Ca-modified TiO2 surface are discussed and compared with UHV-STM results from the literature. Prolonged immersion (two days in the liquid leads to degradation of the overlayer, resulting in a disordered surface. X-ray photoelectron spectroscopy, performed after immersion in water, confirms the presence of calcium.

  11. Manipulating the ferroelectric polarization state of BaTiO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Datta, S.; Rioult, M.; Stanescu, D.; Magnan, H.; Barbier, A., E-mail: antoine.barbier@cea.fr

    2016-05-31

    Controlling the ferroelectric polarization at macroscopic or microscopic levels is crucial in the framework of the development of ferroelectric materials used in yet challenging photo-electrochemical (PEC) cells and spintronic applications. We report here on polarization methods allowing to electrically polarize prototypical samples of BaTiO{sub 3} (001) films. Epitaxial single crystalline layers were grown up to a thickness of 25 nm by atomic oxygen assisted molecular beam epitaxy on 1 at.% Nb doped SrTiO{sub 3} (001) single crystals. The samples were both microscopically and macroscopically polarized using Piezoresponse Force Microscopy and electrochemical poling in an electrolyte respectively. In addition we demonstrate the possibility to retrieve a quasi-native mixed ferroelectric polarization state after annealing. These polarization methods may be applied to many other ferroelectric thin films. - Highlights: • Ferroelectricity of BaTiO{sub 3} layers can be micro- and macroscopically controlled. • Microscopic ferroelectric domains are defined with piezoresponse force microscopy. • Poling in a LiClO{sub 4} electrolyte is a macroscopic poling method. • Air annealing above the Curie temperature “resets” the polarization state.

  12. Thin TiO2 films deposited by implantation and sputtering in RF inductively coupled plasmas

    International Nuclear Information System (INIS)

    Valencia-Alvarado, R; López-Callejas, R; Barocio, S R; Mercado-Cabrera, A; Peña-Eguiluz, R; Muñoz-Castro, A E; Rodríguez-Méndez, B G; De la Piedad-Beneitez, A; De la Rosa-Vázquez, J M

    2012-01-01

    The achievement of titanium dioxide (TiO 2 ) thin films in the rutile crystalline phase is reported. The samples result from the implantation of oxygen ions of Ti in argon/oxygen plasma generated by inductively coupled RF at a commercial 13.56 MHz frequency. Simultaneously, a sputtering process is conducted on the titanium target in order to produce TiO 2 thin films in the anatase phase over silicon and glass substrates. Both implantation and sputtering processes shared the same 500 W plasma with the target, polarized between 0 and -3 kV. The substrates were placed between 2 and 3 cm from the target, this distance being found to be determinant of the TiO 2 deposition rate. The rutile phase in the target was obtained at temperatures in the order of 680 degrees C and the anatase (unbiased) one at about 300 degrees C without any auxiliary heating. The crystalline phases were characterized by x ray diffraction and Raman spectroscopy. The morphology and average roughness were established by means of scanning electronic and atomic force microscopy, whereas the reaction products generated during the oxidation process were analyzed by mass spectrometry. Finally, the stoichiometric composition was measured by means of X-ray photoelectron spectroscopy.

  13. Cystamine immobilization on TiO2 film surfaces and the influence on inhibition of collagen-induced platelet activation

    International Nuclear Information System (INIS)

    Zhou Yujuan; Weng Yajun; Zhang Liping; Jing Fengjuan; Huang Nan; Chen Junying

    2011-01-01

    Poor haemocompatibility is a main issue of artificial cardiovascular materials in clinical application. Nitric oxide (NO), produced by vascular endothelial cells, is a well known inhibitor of platelet adhesion and activation. Thus, NO-releasing biomaterials are beneficial for improving haemocompatibility of blood-contacting biomedical devices. In this paper, a novel method was developed for enhancement of haemocompatibility by exploiting endogenous NO donors. TiO 2 films were firstly synthesized on Si (1 0 0) wafers via unbalanced magnetron sputtering technology, and then polydopamine was grafted on TiO 2 films and used as a linker for further immobilization of cystamine. The obtained surfaces were characterized by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) analysis. NO generation is evaluated by saville-griess reagents, and it shows that cystamine immobilized samples are able to catalytically generate NO by decomposing endogenous S-nitrosothiols (RSNO). In vitro platelet adhesion results reveal that cystamine modified surfaces can inhibit collagen-induced platelet activation. ELISA analysis reveals that cGMP in platelets obviously increases on cystamine immobilized surface, which suggests the reducing of platelet activation is through NO/cGMP signal channel. It can be concluded that cystamine immobilized surface shows better blood compatibility by catalyzing NO release from the endogenous NO donor. It may be a promising method for improvement of haemocompatibility of blood-contacting implants.

  14. Synthesis of Ag ion-implanted TiO{sub 2} thin films for antibacterial application and photocatalytic performance

    Energy Technology Data Exchange (ETDEWEB)

    Hou, Xinggang, E-mail: hou226@mail.tjnu.edu.cn [Department of Physics, Tianjin Normal University, Tianjin 300387 (China); Ma, Huiyan; Liu, Feng; Deng, Jianhua; Ai, Yukai; Zhao, Xinlei; Mao, Dong; Li, Dejun [Department of Physics, Tianjin Normal University, Tianjin 300387 (China); Liao, Bin [Key Laboratory of Beam Technology and Material Modification of Ministry of Education, Beijing Normal University, Beijing 100875 (China)

    2015-12-15

    Highlights: • Implanted TiO{sub 2} films with excellent antibacterial and photocatalytic ability was prepared. • Bactericidal effect of released Ag ions was confirmed using VC as radical scavenger. • Excitation of TiO{sub 2} to visible region is attributed to subtitutional Ag. • Synergetic effect of Ag{sup 3+} and Ag{sup +} accounts for the enhanced ability of TiO{sub 2}. - Abstract: TiO{sub 2} thin films were deposited by spin coating method. Silver ions were implanted into the films using a Metal Vapor Vacuum Arc implanter. The antibacterial ability of implanted films was tested using Escherichia coli removal under fluorescent irradiation and in the dark. The concentration of E. coli was evaluated by plating technique. The photocatalytic efficiency of the implanted films was studied by degradation of methyl orange under fluorescent illumination. The surface free energy of the implanted TiO{sub 2} films was calculated by contact angle testing. Vitamin C was used as radical scavengers to explore the antibacterial mechanism of the films. The results supported the model that both generation of reactive oxygen species and release of silver ions played critical roles in the toxic effect of implanted films against E. coli. XPS experimental results demonstrated that a portion of the Ag(Ag{sup 3+}) ions were doped into the crystalline lattice of TiO{sub 2}. As demonstrated by density functional theory calculations, the impurity energy level of subtitutional Ag was responsible for enhanced absorption of visible light. Ag ion-implanted TiO{sub 2} films with excellent antibacterial efficiency against bacteria and decomposed ability against organic pollutants could be potent bactericidal surface in moist environment.

  15. TiO2 thin film growth using the MOCVD method

    Directory of Open Access Journals (Sweden)

    Bernardi M.I.B.

    2001-01-01

    Full Text Available Titanium oxide (TiO2 thin films were obtained using the MOCVD method. In this report we discuss the properties of a film, produced using a ordinary deposition apparatus, as a function of the deposition time, with constant deposition temperature (90 °C, oxygen flow (7,0 L/min and substrate temperature (400 °C. The films were characterized by X-ray diffraction (XRD, scanning electron microscopy (SEM, atomic force microscopy (AFM and visible and ultra-violet region spectroscopy (UV-Vis. The films deposited on Si (100 substrates showed the anatase polycrystalline phase, while the films grown on glass substrates showed no crystallinity. Film thickness increased with deposition time as expected, while the transmittance varied from 72 to 91% and the refractive index remained close to 2.6.

  16. Tensile properties of latex paint films with TiO2 pigment

    Science.gov (United States)

    Hagan, Eric W. S.; Charalambides, Maria N.; Young, Christina T.; Learner, Thomas J. S.; Hackney, Stephen

    2009-05-01

    The tensile properties of latex paint films containing TiO2 pigment were studied with respect to temperature, strain-rate and moisture content. The purpose of performing these experiments was to assist museums in defining safe conditions for modern paintings held in collections. The glass transition temperature of latex paint binders is in close proximity to ambient temperature, resulting in high strain-rate dependence in typical exposure environments. Time dependence of modulus and failure strain is discussed in the context of time-temperature superposition, which was used to extend the experimental time scale. Nonlinear viscoelastic material models are also presented, which incorporate a Prony series with the Ogden or Neo-Hookean hyperelastic function for different TiO2 concentrations.

  17. Synthesis, characterization and application of Co doped TiO2 multilayer thin films

    Science.gov (United States)

    Khan, M. I.

    2018-06-01

    To use the visible portion of solar light, 2% cobalt doped TiO2 (Co: TiO2) multilayer thin films having 1, 2, 3 and 4 stacked layers have been deposited on FTO substrates using spray pyrolysis technique. XRD results show that 1 and 2 layers of films have anatase phase. Brookite phase has been appeared at the 3 and 4 layered films. The average grain size of 1, 2, 3 and 4 layers of films are 14.4, 23.5, 29.7 and 33.6 nm respectively. UV-Vis results show that 4th layer film has high absorption in the visible region. The calculated Eg of 1, 2, 3 and 4 layers is 3.54, 3.42, 3.30 and 3.03 eV respectively. The calculated average sheet resistivity of 1, 2, 3 and 4 layers of films is 7.68 × 104, 4.54 × 104, 8.85 × 103 and 7.95 × 102 (ohm-m) respectively, according to four point probe technique. Solar simulator results show that highest solar conversion efficiency (5.6%) has been obtained by using 3 stacked layers photoanode. This new structure in the form of stack layers provides a way to improve the efficiency of optoelectronic devices.

  18. Polythiophene thin films electrochemically deposited on sol-gel based TiO2 for photovoltaic applications

    International Nuclear Information System (INIS)

    Valaski, R.; Yamamoto, N.A.D.; Canestraro, C.D.; Micaroni, L.; Mello, R.M.Q.; Quirino, W.G.; Legani, C.; Achete, C.A.; Roman, L.S.; Cremona, M.

    2010-01-01

    In this work, the influence of titanium dioxide (TiO 2 ) thin films on the efficiency of organic photovoltaic devices based on electrochemically synthesized polythiophene (PT) was investigated. TiO 2 films were produced by sol-gel methods with controlled thickness. The best TiO 2 annealing condition was determined through the investigation of the temperature influence on the electron charge mobility and resistivity in a range between 723 K and 923 K. The PT films were produced by chronoamperometric method in a 3-electrode cell under a controlled atmosphere. High quality PT films were produced onto 40 nm thick TiO 2 layer previously deposited onto fluorine doped tin oxide (FTO) substrate. The morphology of PT films grown on both substrates and its strong influence on the device performance and PT minimum thickness were also investigated. The maximum external quantum efficiency (IPCE) reached was 9% under monochromatic irradiation (λ = 610 nm; 1 W/m 2 ) that is three orders of magnitude higher than that presented by PT-homolayer devices with similar PT thickness. In addition, the open-circuit voltage (V oc ) was about 700 mV and the short-circuit current density (J sc ) was 0.03 A/m 2 (λ = 610 nm; 7 W/m 2 ). However, as for the PT-homolayer also the TiO 2 /PT based devices are characterized by antibatic response when illuminated through FTO. Finally, the Fill Factor (FF) of these devices is low (25%), indicating that the series resistance (R s ), which is strongly dependent of the PT thickness, is too large. This large R s value is compensated by TiO 2 /PT interface morphology and by FTO/TiO 2 and TiO 2 /PT interface phenomena producing preferential paths in which the internal electrical field is higher, improving the device efficiency.

  19. Tuning the Phase and Microstructural Properties of TiO2 Films Through Pulsed Laser Deposition and Exploring Their Role as Buffer Layers for Conductive Films

    Science.gov (United States)

    Agarwal, S.; Haseman, M. S.; Leedy, K. D.; Winarski, D. J.; Saadatkia, P.; Doyle, E.; Zhang, L.; Dang, T.; Vasilyev, V. S.; Selim, F. A.

    2018-04-01

    Titanium oxide (TiO2) is a semiconducting oxide of increasing interest due to its chemical and thermal stability and broad applicability. In this study, thin films of TiO2 were deposited by pulsed laser deposition on sapphire and silicon substrates under various growth conditions, and characterized by x-ray diffraction (XRD), atomic force microscopy (AFM), optical absorption spectroscopy and Hall-effect measurements. XRD patterns revealed that a sapphire substrate is more suitable for the formation of the rutile phase in TiO2, while a silicon substrate yields a pure anatase phase, even at high-temperature growth. AFM images showed that the rutile TiO2 films grown at 805°C on a sapphire substrate have a smoother surface than anatase films grown at 620°C. Optical absorption spectra confirmed the band gap energy of 3.08 eV for the rutile phase and 3.29 eV for the anatase phase. All the deposited films exhibited the usual high resistivity of TiO2; however, when employed as a buffer layer, anatase TiO2 deposited on sapphire significantly improves the conductivity of indium gallium zinc oxide thin films. The study illustrates how to control the formation of TiO2 phases and reveals another interesting application for TiO2 as a buffer layer for transparent conducting oxides.

  20. Enhanced antifouling behaviours of polyvinylidene fluoride membrane modified through blending with nano-TiO2/polyethylene glycol mixture

    International Nuclear Information System (INIS)

    Zhang, Jie; Wang, Zhiwei; Zhang, Xingran; Zheng, Xiang; Wu, Zhichao

    2015-01-01

    Graphical abstract: - Highlights: • Nano-TiO 2 /polyethylene glycol (PEG) mixture was used to modify PVDF membranes. • The steric hindrance effects of PEG enabled the dispersion of nanoparticles. • The energy barrier between SMP and modified membranes was increased. • The modification by nano-TiO 2 /PEG well improved the anti-fouling ability. - Abstract: Titanium dioxide (TiO 2 ) nanoparticles/polyethylene glycol (PEG) mixture was used to modify polyvinylidene fluoride (PVDF) membranes aiming to improve their antifouling ability. The use of PEG could improve the dispersion of nanoparticles thanks to steric hindrance effects. Test results showed that compared to the original PVDF membrane, the modified membranes had higher hydrophilicity and lower negative Zeta potential, facilitating membrane fouling control. The extended Derjaguin-Landau-Verwey-Overbeek (XDLVO) analysis indicated that the addition of TiO 2 nanoparticles improved their electron donor monopolarity, i.e., enhanced electron-donating ability. The interaction energy barrier between soluble microbial products (SMP) and membrane surfaces was also improved, indicating that anti-fouling ability of the modified membrane was elevated. The optimal dosage of nano-TiO 2 was found to be 0.15%, and further increase of dosage resulted in the aggregation of nanoparticles which consequently impaired the modification efficiency. Quartz crystal microbalance with dissipation (QCM-D) monitoring and SMP filtration tests confirmed the antifouling ability of the modified membrane

  1. Enhanced antifouling behaviours of polyvinylidene fluoride membrane modified through blending with nano-TiO{sub 2}/polyethylene glycol mixture

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Jie [State Key Laboratory of Pollution Control and Resource Reuse, School of Environmental Science and Engineering, Tongji University, Shanghai, 200092 (China); Wang, Zhiwei, E-mail: zwwang@tongji.edu.cn [State Key Laboratory of Pollution Control and Resource Reuse, School of Environmental Science and Engineering, Tongji University, Shanghai, 200092 (China); Zhang, Xingran [State Key Laboratory of Pollution Control and Resource Reuse, School of Environmental Science and Engineering, Tongji University, Shanghai, 200092 (China); Zheng, Xiang, E-mail: zhengxiang7825@163.com [School of Environment and Natural Resources, Renmin University of China, Beijing, 100872 (China); Wu, Zhichao [State Key Laboratory of Pollution Control and Resource Reuse, School of Environmental Science and Engineering, Tongji University, Shanghai, 200092 (China)

    2015-08-01

    Graphical abstract: - Highlights: • Nano-TiO{sub 2}/polyethylene glycol (PEG) mixture was used to modify PVDF membranes. • The steric hindrance effects of PEG enabled the dispersion of nanoparticles. • The energy barrier between SMP and modified membranes was increased. • The modification by nano-TiO{sub 2}/PEG well improved the anti-fouling ability. - Abstract: Titanium dioxide (TiO{sub 2}) nanoparticles/polyethylene glycol (PEG) mixture was used to modify polyvinylidene fluoride (PVDF) membranes aiming to improve their antifouling ability. The use of PEG could improve the dispersion of nanoparticles thanks to steric hindrance effects. Test results showed that compared to the original PVDF membrane, the modified membranes had higher hydrophilicity and lower negative Zeta potential, facilitating membrane fouling control. The extended Derjaguin-Landau-Verwey-Overbeek (XDLVO) analysis indicated that the addition of TiO{sub 2} nanoparticles improved their electron donor monopolarity, i.e., enhanced electron-donating ability. The interaction energy barrier between soluble microbial products (SMP) and membrane surfaces was also improved, indicating that anti-fouling ability of the modified membrane was elevated. The optimal dosage of nano-TiO{sub 2} was found to be 0.15%, and further increase of dosage resulted in the aggregation of nanoparticles which consequently impaired the modification efficiency. Quartz crystal microbalance with dissipation (QCM-D) monitoring and SMP filtration tests confirmed the antifouling ability of the modified membrane.

  2. Interface feature characterization and Schottky interfacial layer confirmation of TiO{sub 2} nanotube array film

    Energy Technology Data Exchange (ETDEWEB)

    Li, Hongchao [State Key Laboratory of Powder Metallurgy, Central South University, 410083 Changsha (China); Chongyi Zhangyuan Tungsten Industry Corporation Limited, 341300 Ganzhou (China); Tang, Ningxin; Yang, Hongzhi; Leng, Xian [State Key Laboratory of Powder Metallurgy, Central South University, 410083 Changsha (China); Zou, Jianpeng, E-mail: zoujp@csu.edu.cn [State Key Laboratory of Powder Metallurgy, Central South University, 410083 Changsha (China)

    2015-11-15

    Highlights: • Interfacial fusion of TiO{sub 2} nanotube film increases with annealing temperature. • Interface bonding force of the film increases with annealing temperature. • We report the forth stage of nanofibers formation in the growing mechanism. • TiO{sub 2} nanotubes grow from Schottky interface layer rather than from Ti substrate. • Schottky interface layer's thickness of 35–45 nm is half the diameter of nanotube. - Abstract: We report here characterization of the interfacial microstructure and properties of titanium dioxide (TiO{sub 2}) nanotube array films fabricated by anodization. Field effect scanning electron microscopy (FESEM), X-ray diffraction (XRD), nanoindentation, atomic force microscopy (AFM), selected area electron diffraction (SAED), and high-resolution transmission electron microscopy (HRTEM) were used to characterize the interface of the film. With increasing annealing temperature from 200 °C to 800 °C, the interfacial fusion between the film and the Ti substrate increased. The phase transformation of the TiO{sub 2} nanotube film from amorphous to anatase to rutile took place gradually; as the phase transformation progressed, the force needed to break the film increased. The growth of TiO{sub 2} nanotube arrays occurs in four stages: barrier layer formation, penetrating micropore formation, regular nanotube formation, and nanofiber formation. The TiO{sub 2} nanotubes grow from the Schottky interface layer rather than from the Ti substrate. The Schottky interface layer's thickness of 35–45 nm was identified as half the diameter of the corresponding nanotube, which shows good agreement to the Schottky interface layer growth model. The TiO{sub 2} nanotube film was amorphous and the Ti substrate was highly crystallized with many dislocation walls.

  3. Excimer laser assisted re-oxidation of BaTiO3 thin films on Ni metal foils

    International Nuclear Information System (INIS)

    Bharadwaja, S. S. N.; Ko, S. W.; Qu, W.; Clark, T.; Rajashekhar, A.; Motyka, M.; Podraza, N.; Randall, C. A.; Trolier-McKinstry, S.

    2016-01-01

    Excimer laser assisted re-oxidation for reduced, crystallized BaTiO 3 thin films on Ni-foils was investigated. It was found that the BaTiO 3 can be re-oxidized at an oxygen partial pressure of ∼50 mTorr and substrate temperature of 350 °C without forming a NiO x interface layer between the film and base metal foil. The dielectric permittivity of re-oxidized films was >1000 with loss tangent values <2% at 100 Hz, 30 mV rms excitation signal. Electron Energy Loss Spectroscopy indicated that BaTiO 3 thin films can be re-oxidized to an oxygen stoichiometry close to ∼3 (e.g., stoichiometric). High resolution cross sectional transmission electron microscopy showed no evidence of NiO x formation between the BaTiO 3 and the Ni foil upon excimer laser re-oxidation. Spectroscopic ellipsometry studies on laser re-oxidized [001] C and [111] C BaTiO 3 single crystals indicate that the re-oxidation of BaTiO 3 single crystals is augmented by photo-excitation of the ozone, as well as laser pulse induced temperature and local stress gradients

  4. Novel Flexible Transparent Conductive Films with Enhanced Chemical and Electromechanical Sustainability: TiO2 Nanosheet-Ag Nanowire Hybrid.

    Science.gov (United States)

    Sohn, Hiesang; Kim, Seyun; Shin, Weonho; Lee, Jong Min; Lee, Hyangsook; Yun, Dong-Jin; Moon, Kyoung-Seok; Han, In Taek; Kwak, Chan; Hwang, Seong-Ju

    2018-01-24

    Flexible transparent conductive films (TCFs) of TiO 2 nanosheet (TiO 2 NS) and silver nanowire (Ag NW) network hybrid were prepared through a simple and scalable solution-based process. The as-formed TiO 2 NS-Ag NW hybrid TCF shows a high optical transmittance (TT: 97% (90.2% including plastic substrate)) and low sheet resistance (R s : 40 Ω/sq). In addition, the TiO 2 NS-Ag NW hybrid TCF exhibits a long-time chemical/aging and electromechanical stability. As for the chemical/aging stability, the hybrid TCF of Ag NW and TiO 2 NS reveals a retained initial conductivity (ΔR s /R s 4000%) or RuO 2 NS-Ag NW hybrid (ΔR s /R s > 200%). As corroborated by the density functional theory simulation, the superb chemical stability of TiO 2 NS-Ag NW hybrid is attributable to the unique role of TiO 2 NS as a barrier, which prevents Ag NW's chemical corrosion via the attenuated adsorption of sulfidation molecules (H 2 S) on TiO 2 NS. With respect to the electromechanical stability, in contrast to Ag NWs (ΔR/R 0 ∼ 152.9%), our hybrid TCF shows a limited increment of fractional resistivity (ΔR/R 0 ∼ 14.4%) after 200 000 cycles of the 1R bending test (strain: 6.7%) owing to mechanically welded Ag NW networks by TiO 2 NS. Overall, our unique hybrid of TiO 2 NS and Ag NW exhibits excellent electrical/optical properties and reliable chemical/electromechanical stabilities.

  5. Defect engineering of SrTiO{sub 3} thin films for resistive switching applications

    Energy Technology Data Exchange (ETDEWEB)

    Wicklein, Sebastian

    2013-11-19

    As a matter of fact, the importance of (transition) metal oxides for modern applications in the field of energy and information technology (IT) for e.g. novel energy storage systems and solid state electronic devices is increasing. Previous studies discovered the importance of defects in an oxide for their functionality and emphasized the impact of stoichiometry on the oxide performance. A new field of interest of the memory technology sector is the so-called resistive switching phenomena where a voltage stimulus causes a thin oxide (≤10 nm) to change its resistance state from a high resistance state to a low resistance state and back. So called resistive RAM (ReRAM or RRAM) are deemed to be the future replacement (2015) for contemporary FLASH memory technology due to its extremely low energy consumption, its very fast read/write time (ns) and its possible node size <10 nm. A key challenge for the investigation of oxides and their electronic properties is the management and controlled incorporation of defects in the thin film oxide. Within this work, SrTiO{sub 3} was used as an oxide model material and was deposited by pulsed laser deposition (PLD) onto doped and undoped SrTiO{sub 3} single crystals to investigate the formation of defects as a function of the process parameters. By combining structural and chemical thin film analysis with detailed PLD plume diagnostics and modeling of the laser plume dynamics, it was possible to elucidate the different physical mechanisms determining the stoichiometry of SrTiO{sub 3} during PLD. Deviations between thin film and target stoichiometry are basically a result of two effects, namely, incongruent ablation and preferential scattering of lighter ablated species during their motion towards the substrate in the O{sub 2} background gas. It is shown that the SrTiO{sub 3} system reacts to a non-stoichiometry with the systematic incorporation of titanium and strontium vacancies which could be detected by positron annihilation

  6. A short literature survey on iron and cobalt ion doped TiO{sub 2} thin films and photocatalytic activity of these films against fungi

    Energy Technology Data Exchange (ETDEWEB)

    Tatl Latin-Small-Letter-Dotless-I dil, Ilknur [Department of Chemistry, Faculty of Science, Karadeniz Technical University, 61080 Trabzon (Turkey); Bacaks Latin-Small-Letter-Dotless-I z, Emin [Department of Physics, Faculty of Science, Karadeniz Technical University, 61080 Trabzon (Turkey); Buruk, Celal Kurtulus [Department of Microbiology, Faculty of Medicine, Karadeniz Technical University, 61080 Trabzon (Turkey); Breen, Chris [Materials and Engineering Research Institution, Sheffield Hallam University, Sheffield S1 1WB (United Kingdom); Soekmen, Muenevver, E-mail: msokmen@ktu.edu.tr [Department of Chemistry, Faculty of Science, Karadeniz Technical University, 61080 Trabzon (Turkey)

    2012-03-15

    Highlights: Black-Right-Pointing-Pointer Co or Fe doped TiO{sub 2} thin films were prepared by sol-gel method. Black-Right-Pointing-Pointer We obtained lower E{sub g} values for Fe-doped and Co-TiO{sub 2} thin films. Black-Right-Pointing-Pointer Doping greatly affected the size and shape of the TiO{sub 2} nanoparticles. Black-Right-Pointing-Pointer Photocatalytic killing effect of the doped TiO{sub 2} thin films on C. albicans and A. niger was significantly higher than undoped TiO{sub 2} thin film for short exposure periods. - Abstract: In this study, a short recent literature survey which concentrated on the usage of Fe{sup 3+} or Co{sup 2+} ion doped TiO{sub 2} thin films and suspensions were summarized. Additionally, a sol-gel method was used for preparation of the 2% Co or Fe doped TiO{sub 2} thin films. The surface of the prepared materials was characterised using scanning-electron microscopy (SEM) combined with energy dispersive X-ray (EDX) analysis and band gap of the films were calculated from the transmission measurements that were taken over the range of 190 and 1100 nm. The E{sub g} value was 3.40 eV for the pure TiO{sub 2}, 3.00 eV for the Fe-doped TiO{sub 2} film and 3.25 eV for Co-TiO{sub 2} thin film. Iron or cobalt doping at lower concentration produce more uniformed particles and doping greatly affected the size and shape of the TiO{sub 2} nanoparticles. Photocatalytic killing effect of the 2% Co doped TiO{sub 2} thin film on Candida albicans was significantly higher than Fe doped TiO{sub 2} thin film for short and long exposure periods. Doped thin films were more effective on Aspergillus niger for short exposure periods.

  7. Fabrication of La-doped TiO2 Film Electrode and investigation of its electrocatalytic activity for furfural reduction

    International Nuclear Information System (INIS)

    Wang, Fengwu; Xu, Mai; Wei, Lin; Wei, Yijun; Hu, Yunhu; Fang, Wenyan; Zhu, Chuan Gao

    2015-01-01

    Lanthanum trivalent ions (La 3+ ) doped nano-TiO 2 film electrode was prepared by the sol–gel method. The prepared electrode was characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS) and cyclic voltammetry (CV). The electrocatalytic properties of the roughened TiO 2 film electrode towards the electrocatalytic reduction of furfural to furfural alcohol were evaluated by CV and preparative electrolysis experiments. The results of the optimum molar ratio of La: Ti was 0.005:1. Experimental evidence was presented that the La nano-TiO 2 electrode exhibited higher electrocatalytic activity for the reduction of furfural than the undoped nano-TiO 2 electrode in N,N-dimethylformamide medium. Bulk electrolysis studies were also carried out for the reduction of furfural and the product was confirmed by NMR

  8. Quantum size effects in TiO2 thin films grown by atomic layer deposition

    Directory of Open Access Journals (Sweden)

    Massimo Tallarida

    2014-01-01

    Full Text Available We study the atomic layer deposition of TiO2 by means of X-ray absorption spectroscopy. The Ti precursor, titanium isopropoxide, was used in combination with H2O on Si/SiO2 substrates that were heated at 200 °C. The low growth rate (0.15 Å/cycle and the in situ characterization permitted to follow changes in the electronic structure of TiO2 in the sub-nanometer range, which are influenced by quantum size effects. The modified electronic properties may play an important role in charge carrier transport and separation, and increase the efficiency of energy conversion systems.

  9. Ceramic thick film humidity sensor based on MgTiO3 + LiF

    International Nuclear Information System (INIS)

    Kassas, Ahmad; Bernard, Jérôme; Lelièvre, Céline; Besq, Anthony; Guhel, Yannick; Houivet, David; Boudart, Bertrand; Lakiss, Hassan; Hamieh, Tayssir

    2013-01-01

    Graphical abstract: - Highlights: • The fabricated sensor based on MgTiO 3 + LiF materials used the spin coating technology. • The response time is 70 s to detect variation between 5 and 95% relative humidity. • The addition of Scleroglucan controls the viscosity and decreases the roughness of thick film surface. • This humidity sensor is a promising, low-cost, high-quality, reliable ceramic films, that is highly sensitive to humidity. - Abstract: The feasibility of humidity sensor, consisting of a thick layer of MgTiO 3 /LiF materials on alumina substrate, was studied. The thermal analysis TGA-DTGA and dilatometric analysis worked out to confirm the sintering temperature. An experimental plan was applied to describe the effects of different parameters in the development of the thick film sensor. Structural and microstructural characterizations of the developed thick film were made. Rheological study with different amounts of a thickener (scleroglucan “sclg”), showing the behavior variation, as a function of sclg weight % was illustrated and rapprochement with the results of thickness variation as a function of angular velocity applied in the spin coater. The electrical and dielectric measurements confirmed the sensitivity of the elaborated thick film against moisture, along with low response time

  10. Ceramic thick film humidity sensor based on MgTiO{sub 3} + LiF

    Energy Technology Data Exchange (ETDEWEB)

    Kassas, Ahmad, E-mail: a.kassas.mcema@ul.edu.lb [Faculty of Agricultural Engineering and Veterinary Medicine, Laboratory of Materials, Catalysis, Environment and Analytical Methods (MCEMA), Faculty of Sciences and Doctoral School of Sciences and Technology (EDST), Lebanese University, Hariri Campus, Hadath, Beirut (Lebanon); Laboratoire Universitaire des Sciences Appliquées de Cherbourg (LUSAC), 50130 Cherbourg-Octeville (France); Bernard, Jérôme; Lelièvre, Céline; Besq, Anthony; Guhel, Yannick; Houivet, David; Boudart, Bertrand [Laboratoire Universitaire des Sciences Appliquées de Cherbourg (LUSAC), 50130 Cherbourg-Octeville (France); Lakiss, Hassan [Faculty of Agricultural Engineering and Veterinary Medicine, Laboratory of Materials, Catalysis, Environment and Analytical Methods (MCEMA), Faculty of Sciences and Doctoral School of Sciences and Technology (EDST), Lebanese University, Hariri Campus, Hadath, Beirut (Lebanon); Faculty of Engineering, Section III, Hariri Campus, Hadath, Beirut (Lebanon); Hamieh, Tayssir [Faculty of Agricultural Engineering and Veterinary Medicine, Laboratory of Materials, Catalysis, Environment and Analytical Methods (MCEMA), Faculty of Sciences and Doctoral School of Sciences and Technology (EDST), Lebanese University, Hariri Campus, Hadath, Beirut (Lebanon)

    2013-10-15

    Graphical abstract: - Highlights: • The fabricated sensor based on MgTiO{sub 3} + LiF materials used the spin coating technology. • The response time is 70 s to detect variation between 5 and 95% relative humidity. • The addition of Scleroglucan controls the viscosity and decreases the roughness of thick film surface. • This humidity sensor is a promising, low-cost, high-quality, reliable ceramic films, that is highly sensitive to humidity. - Abstract: The feasibility of humidity sensor, consisting of a thick layer of MgTiO{sub 3}/LiF materials on alumina substrate, was studied. The thermal analysis TGA-DTGA and dilatometric analysis worked out to confirm the sintering temperature. An experimental plan was applied to describe the effects of different parameters in the development of the thick film sensor. Structural and microstructural characterizations of the developed thick film were made. Rheological study with different amounts of a thickener (scleroglucan “sclg”), showing the behavior variation, as a function of sclg weight % was illustrated and rapprochement with the results of thickness variation as a function of angular velocity applied in the spin coater. The electrical and dielectric measurements confirmed the sensitivity of the elaborated thick film against moisture, along with low response time.

  11. Azo dyes decomposition on new nitrogen-modified anatase TiO{sub 2} with high adsorptivity

    Energy Technology Data Exchange (ETDEWEB)

    Janus, M., E-mail: mjanus@ps.pl [Szczecin University of Technology, Department of Sanitary Engineering, al. Piastow 50, 70-310 Szczecin (Poland); Szczecin University of Technology, Institute of Chemical and Environment Engineering, Department of Water Technology and Environment Engineering, ul. Pulaskiego 10, 70-322 Szczecin (Poland); Choina, J.; Morawski, A.W. [Szczecin University of Technology, Institute of Chemical and Environment Engineering, Department of Water Technology and Environment Engineering, ul. Pulaskiego 10, 70-322 Szczecin (Poland)

    2009-07-15

    New vis active photocatalyst was obtained by the modification of commercial anatase TiO{sub 2} (Police, Poland) in pressure reactor in an ammonia water atmosphere at 100 {sup o}C for 4 h. The photocatalytic activity of new material was tested during three azo dyes decomposition: monoazo (Reactive Read), diazo (Reactive Black) and poliazodye (Direct Green). Obtained photocatalyst had new bands at 1430-1440 cm{sup -1} attributed to the bending vibrations of NH{sub 4}{sup +} and at 1535 cm{sup -1} associated with NH{sub 2} groups or NO{sub 2} and NO. UV-vis/DR spectra of photocatalyst had also insignificant decrease in visible region. Fluorescence technique was used for studying the amount of hydroxyl radicals produced on TiO{sub 2} surface during visible light irradiation. The hydroxyl radicals produced react with coumarin present in the solution to form 7-hydroxycoumarin which has fluorescent capacity. Photocatalytic activity of modified TiO{sub 2} was compared with commercial titanium dioxide P25 (Degussa, Germany). The photocatalytic activity of TiO{sub 2}/N was higher than that of unmodified material and P25 under visible light irradiation. The ability for dye adsorption (Reactive Red) on photocatalyst surface was also tested. Unmodified TiO{sub 2} and P25 has isotherm of adsorption by Freundlich model, and nitrogen-modified TiO{sub 2} by Langmuir model. The presence of nitrogen at the surface of TiO{sub 2} significantly increased adsorption capacity of TiO{sub 2} as well as OH{center_dot} radicals formation under visible radiation.

  12. Influence of Substrate Biasing on (Ba,Sr)TiO3 Films Prepared by Electron Cyclotron Resonance Plasma Sputtering

    Science.gov (United States)

    Matsumoto, Takeshi; Niino, Atsushi; Ohtsu, Yasunori; Misawa, Tatsuya; Yonesu, Akira; Fujita, Hiroharu; Miyake, Shoji

    2004-03-01

    (Ba,Sr)TiO3 (BST) films were deposited by electron cyclotron resonance (ECR) plasma sputtering with mirror confinement. DC bias voltage was applied to Pt/Ti/SiO2/Si substrates during deposition to vary the intensity of bombardment of energetic ions and to modify film properties. BST films deposited on the substrates at floating potential (approximately +20 V) were found to be amorphous, while films deposited on +40 V-biased substrates were crystalline in spite of a low substrate temperature below 648 K. In addition, atomic diffusion, which causes deterioration in the electrical properties of the films, was hardly observed in the crystallized films deposited with +40 V bias perhaps due to the low substrate temperature. Plasma diagnoses revealed that application of a positive bias to the substrate reduced the energy of ion bombardment and increased the density of excited neutral particles, which was assumed to result in the promotion of chemical reactions during deposition and the crystallization of BST films at a low temperature.

  13. TiO 2 Thin Films Prepared via Adsorptive Self-Assembly for Self-Cleaning Applications

    KAUST Repository

    Xi, Baojuan

    2012-02-22

    Low-cost controllable solution-based processes for preparation of titanium oxide (TiO 2) thin films are highly desirable, because of many important applications of this oxide in catalytic decomposition of volatile organic compounds, advanced oxidation processes for wastewater and bactericidal treatments, self-cleaning window glass for green intelligent buildings, dye-sensitized solar cells, solid-state semiconductor metal-oxide solar cells, self-cleaning glass for photovoltaic devices, and general heterogeneous photocatalysis for fine chemicals etc. In this work, we develop a solution-based adsorptive self-assembly approach to fabricate anatase TiO 2 thin films on different glass substrates such as simple plane glass and patterned glass at variable compositions (normal soda lime glass or solar-grade borofloat glass). By tuning the number of process cycles (i.e., adsorption-then-heating) of TiO 2 colloidal suspension, we could facilely prepare large-area TiO 2 films at a desired thickness and with uniform crystallite morphology. Moreover, our as-prepared nanostructured TiO 2 thin films on glass substrates do not cause deterioration in optical transmission of glass; instead, they improve optical performance of commercial solar cells over a wide range of incident angles of light. Our as-prepared anatase TiO 2 thin films also display superhydrophilicity and excellent photocatalytic activity for self-cleaning application. For example, our investigation of photocatalytic degradation of methyl orange indicates that these thin films are indeed highly effective, in comparison to other commercial TiO 2 thin films under identical testing conditions. © 2012 American Chemical Society.

  14. In vitro corrosion behavior of Ti-O film deposited on fluoride-treated Mg-Zn-Y-Nd alloy

    Energy Technology Data Exchange (ETDEWEB)

    Hou, S.S.; Zhang, R.R. [Materials Research Center, School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450002 (China); Guan, S.K., E-mail: skguan@zzu.edu.cn [Materials Research Center, School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450002 (China); Ren, C.X.; Gao, J.H.; Lu, Q.B.; Cui, X.Z. [Materials Research Center, School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450002 (China)

    2012-02-01

    In this paper, a new composite coating was fabricated on magnesium alloy by a two-step approach, to improve the corrosion resistance and biocompatibility of Mg-Zn-Y-Nd alloy. First, fluoride conversion layer was synthesized on magnesium alloy surface by immersion treatment in hydrofluoric acid and then, Ti-O film was deposited on the preceding fluoride layer by magnetron sputtering. FE-SEM images revealed a smooth and uniform surface consisting of aggregated nano-particles with average size of 100 nm, and a total coating thickness of {approx}1.5 {mu}m, including an outer Ti-O film of {approx}250 nm. The surface EDS and XRD data indicated that the composite coating was mainly composed of crystalline magnesium fluoride (MgF{sub 2}), and non-crystalline Ti-O. Potentiodynamic polarization tests revealed that the composite coated sample have a corrosion potential (E{sub corr}) of -1.60 V and a corrosion current density (I{sub corr}) of 0.17 {mu}A/cm{sup 2}, which improved by 100 mV and reduced by two orders of magnitude, compared with the sample only coated by Ti-O. EIS results showed a polarization resistance of 3.98 k{Omega} cm{sup 2} for the Ti-O coated sample and 0.42 k{Omega} cm{sup 2} for the composite coated sample, giving an improvement of about 100 times. After 72 h immersion in SBF, widespread damage and deep corrosion holes were observed on the Ti-O coated sample surface, while the integrity of composite coating remained well after 7 d. In brief, the data suggested that single Ti-O film on degradable magnesium alloys was apt to become failure prematurely in corrosion environment. Ti-O film deposited on fluoride-treated magnesium alloys might potentially meet the requirements for future clinical magnesium alloy stent application.

  15. In vitro corrosion behavior of Ti-O film deposited on fluoride-treated Mg-Zn-Y-Nd alloy

    International Nuclear Information System (INIS)

    Hou, S.S.; Zhang, R.R.; Guan, S.K.; Ren, C.X.; Gao, J.H.; Lu, Q.B.; Cui, X.Z.

    2012-01-01

    In this paper, a new composite coating was fabricated on magnesium alloy by a two-step approach, to improve the corrosion resistance and biocompatibility of Mg-Zn-Y-Nd alloy. First, fluoride conversion layer was synthesized on magnesium alloy surface by immersion treatment in hydrofluoric acid and then, Ti-O film was deposited on the preceding fluoride layer by magnetron sputtering. FE-SEM images revealed a smooth and uniform surface consisting of aggregated nano-particles with average size of 100 nm, and a total coating thickness of ∼1.5 μm, including an outer Ti-O film of ∼250 nm. The surface EDS and XRD data indicated that the composite coating was mainly composed of crystalline magnesium fluoride (MgF 2 ), and non-crystalline Ti-O. Potentiodynamic polarization tests revealed that the composite coated sample have a corrosion potential (E corr ) of -1.60 V and a corrosion current density (I corr ) of 0.17 μA/cm 2 , which improved by 100 mV and reduced by two orders of magnitude, compared with the sample only coated by Ti-O. EIS results showed a polarization resistance of 3.98 kΩ cm 2 for the Ti-O coated sample and 0.42 kΩ cm 2 for the composite coated sample, giving an improvement of about 100 times. After 72 h immersion in SBF, widespread damage and deep corrosion holes were observed on the Ti-O coated sample surface, while the integrity of composite coating remained well after 7 d. In brief, the data suggested that single Ti-O film on degradable magnesium alloys was apt to become failure prematurely in corrosion environment. Ti-O film deposited on fluoride-treated magnesium alloys might potentially meet the requirements for future clinical magnesium alloy stent application.

  16. Metal-to-Insulator Transition in Anatase TiO2 Thin Films Induced by Growth Rate Modulation

    International Nuclear Information System (INIS)

    Tachikawa, Takashi

    2012-01-01

    We demonstrate control of the carrier density of single phase anatase TiO 2 thin films by nearly two orders of magnitude by modulating the growth kinetics during pulsed laser deposition, under fixed thermodynamic conditions. The resistivity and the intensity of the photoluminescence spectra of these TiO 2 samples, both of which correlate with the number of oxygen vacancies, are shown to depend strongly on the growth rate. A quantitative model is used to explain the carrier density changes.

  17. Highly-efficient photocatalytic degradation of methylene blue by PoPD-modified TiO 2 nanocomposites due to photosensitization-synergetic effect of TiO2 with PoPD.

    Science.gov (United States)

    Yang, Chuanxi; Dong, Wenping; Cui, Guanwei; Zhao, Yingqiang; Shi, Xifeng; Xia, Xinyuan; Tang, Bo; Wang, Weiliang

    2017-06-21

    Poly-o-phenylenediamine modified TiO 2 nanocomposites were successfully synthesized via an 'in situ' oxidative polymerization method. The modified nanocomposites were characterized by BET, XRD, TEM, FT-IR, TGA, XPS, EA and UV-Vis DRS. The photocatalytic degradation of methylene blue was chosen as a model reaction to evaluate the photocatalytic activities of TiO 2 and PoPD/TiO 2 . The results indicated that PoPD/TiO 2 nanocomposites exhibited good photocatalytic activity and stability. The photocatalytic activity of PoPD/TiO 2 increased as the initial pH increased because of electrostatic adsorption between the photocatalyst and MB as well as the generation of ·OH, whereas it exhibited an earlier increasing and later decreasing trend as the concentration of the photocatalyst increased owing to the absorption of visible light. The photocatalytic stability of the PoPD/TiO 2 nanocomposite was dependent on the stability of its structure. Based on radical trapping experiments and ESR measurements, the origin of oxidizing ability of PoPD/TiO 2 nanocomposites on photocatalytic degradation of MB was proposed, which taking into account of ·OH and ·O 2 - were the first and second important ROS, respectively. The possible photocatalytic mechanism and photocatalytic activity enhanced mechanism has been proposed, taking into account the photosensitization effect and synergetic effect of TiO 2 with PoPD.

  18. Enhancement of polarization property of silane-modified BaTiO3 nanoparticles and its effect in increasing dielectric property of epoxy/BaTiO3 nanocomposites

    Directory of Open Access Journals (Sweden)

    Thi Tuyet Mai Phan

    2016-03-01

    Full Text Available The surface modification of synthesized nano-BaTiO3 particles was carried out using γ-aminopropyl trimethoxy silane (γ-APS in an ethanol/water solution. The modified particles were characterized by FTIR, TGA, surface charge analysis, and by dielectric constant measurement. The silane molecules were attached to the surface of BaTiO3 particles through SiOBaTiO3 bonds. The γ-APS grafted on BaTiO3 made the dielectric constant of the particles increase at frequencies ≥0.3 kHz in a wide range of temperature (25 °C–140 °C, due to the presence of NH2 groups. The dependence of the polarization vs. electrical field was measured in order to elucidate the dielectric behavior of the silane treated BaTiO3 in comparison to untreated BaTiO3. The nanocomposite based on epoxy resin containing BaTiO3 nanoparticles untreated and treated with γ-APS was also prepared and characterized. The results indicated that the γ-APS-modified BaTiO3 surfaces significantly enhanced the dielectric property of the nanocomposite.

  19. Ion beam modification of TiO2 films prepared by Cat-CVD for solar cell

    International Nuclear Information System (INIS)

    Narita, Tomoki; Iida, Tamio; Ogawa, Shunsuke; Mizuno, Kouichi; So, Jisung; Kondo, Akihiro; Yoshida, Norimitsu; Itoh, Takashi; Nonomura, Shuichi; Tanaka, Yasuhito

    2008-01-01

    The effects of nitrogen ion bombardment on TiO 2 films prepared by the Cat-CVD method have been studied to improve the optical and electrical properties of the material for use in Si thin film solar cells. The refractive index n and the dark conductivity of the TiO 2 film increased with irradiation time. The refractive index n of the TiO 2 film was changed from 2.1 to 2.4 and the electrical conductivity was improved from 3.4 x 10 -2 to 1.2 x 10 -1 S/cm by the irradiation. These results are due to the formation of Ti-N bonds and oxygen vacancies in the film

  20. Co3O4/TiO2 films obtained by laser ablation and sol-gel for the reaction of oxygen liberation in alkaline medium

    International Nuclear Information System (INIS)

    Perez A, J.; Fernandez V, S. M.; Escobar A, L.; Jimenez B, J.

    2008-01-01

    The laser ablation technique known as Pulsed Laser Deposition (PLD) is used for obtaining thin films of TiO 2 /SnO 2 , which was later modified with Co 3 O 4 by PLD or by sol-gel technique. The films were characterized by X-ray diffraction, ultraviolet Vis and Raman spectroscopies, scanning electron microscopy and energy analysis of the dispersed X-rays produced by Auger decay. The anatase phase with particles of nano metric size was obtained by depositing the titanium dioxide in argon atmosphere. The Co 3 O 4 films obtained by PLD on the TiO 2 showed the same morphology. The electrocatalytic activity of the films that were used as photo anodes for the reaction of oxygen liberation was carried out in the darkness, with environment light and the light emitted by a xenon lamp. The current density was higher for films of Co 3 O 4 /TiO 2 /SnO 2 obtained by PLD that for cobalt dioxide of mixed valence obtained by sol-gel. (Author)

  1. Effect of electrode type in the resistive switching behaviour of TiO2 thin films

    International Nuclear Information System (INIS)

    Hernández-Rodríguez, E; Zapata-Torres, M; Márquez-Herrera, A; Zaleta-Alejandre, E; Meléndez-Lira, M; Cruz, W de la

    2013-01-01

    The influence of the electrode/active layer on the electric-field-induced resistance-switching phenomena of TiO 2 -based metal-oxide-metal devices (MOM) is studied. TiO 2 active layers were fabricated by the reactive rf-sputtering technique and devices were made by sandwiching between several metal electrodes. Three different MOM devices were made, according with the junction type formed between the electrode and the TiO 2 active layer, those where Ohmic-Ohmic, Ohmic-Schottky and Schottky-Schottky. The junction type was tested by electrical I-V measurements. It was found that MOM devices made with the Ohmic-Ohmic combination did not show any resistive switching behaviour in contrast with devices made with Ohmic-Schottky and Schottky-Schottky combinations. From a detailed analysis of the I-V curves it was found that transport characteristics are Ohmic for the low-resistance state for all the contacts combinations of the MOM devices, whereas in the high-resistance state it depends on contact combinations and can be identified as Ohmic, Schottky and Poole-Frenkel type. These conduction mechanisms in the low- and high-resistance states suggest that formation and rupture of conducting filaments through the film oxide is the mechanism responsible for the resistance switching.

  2. Effect of deposition temperature of TiO2 on the piezoelectric property of PbTiO3 film grown by PbO gas phase reaction sputtering

    International Nuclear Information System (INIS)

    Kim, Jiyoon; Kim, Yunseok; Park, Moonkyu; No, Kwangsoo; Hong, Seungbum; Buehlmann, Simon; Kim, Yong Kwan

    2010-01-01

    A 17 nm thick PbTiO 3 (PTO) films were fabricated via PbO gas phase reaction with TiO 2 starting layer in a sputtering chamber. The influence of deposition temperature of TiO 2 on the piezoelectric properties of PTO thin films was investigated. The remnant piezoresponse of PTO films nonlinearly increased as a function of TiO 2 deposition temperature, which is correlated with the increase in average grain diameter of PTO film. As grain size increases, the restriction on remnant piezoresponse imposed by the grain boundary via coupling between local strain and polarization becomes less pronounced, which results in the increase in remnant piezoresponse. Furthermore, we found that the vertical shift in piezoresponse hysteresis loops is closely related to the residual stress state. A strong correlation between the negative vertical shift and the residual tensile stress reveals that residual stress on the resulting PTO film contributed to the asymmetric piezoelectric property.

  3. Controllable nitrogen doping in as deposited TiO{sub 2} film and its effect on post deposition annealing

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Shaoren; Devloo-Casier, Kilian; Devulder, Wouter; Dendooven, Jolien; Deduytsche, Davy; Detavernier, Christophe, E-mail: Christophe.Detavernier@ugent.be [Department of Solid State Sciences, Ghent University, Krijgslaan 281/S1, B-9000 Gent (Belgium); Verbruggen, Sammy W. [Department of Bio-Engineering Sciences, University of Antwerp, Groenenborgerlaan 171, B-2020 Antwerp, Belgium and Center for Surface Chemistry and Catalysis, KU Leuven, Kasteelpark Arenberg 23, B-3001 Heverlee (Belgium); Lenaerts, Silvia [Department of Bio-Engineering Sciences, University of Antwerp, Groenenborgerlaan 171, B-2020 Antwerp (Belgium); Martens, Johan A. [Center for Surface Chemistry and Catalysis, KU Leuven, Kasteelpark Arenberg 23, B-3001 Heverlee (Belgium); Van den Berghe, Sven [SCK-CEN, Boeretang 200, B-2400 Mol (Belgium)

    2014-01-15

    In order to narrow the band gap of TiO{sub 2}, nitrogen doping by combining thermal atomic layer deposition (TALD) of TiO{sub 2} and plasma enhanced atomic layer deposition (PEALD) of TiN has been implemented. By altering the ratio between TALD TiO{sub 2} and PEALD TiN, the as synthesized TiO{sub x}N{sub y} films showed different band gaps (from 1.91 eV to 3.14 eV). In situ x-ray diffraction characterization showed that the crystallization behavior of these films changed after nitrogen doping. After annealing in helium, nitrogen doped TiO{sub 2} films crystallized into rutile phase while for the samples annealed in air a preferential growth of the anatase TiO{sub 2} along (001) orientation was observed. Photocatalytic tests of the degradation of stearic acid were done to evaluate the effect of N doping on the photocatalytic activity.

  4. Effective Carbon Dioxide Photoreduction over Metals (Fe-, Co-, Ni-, and Cu- Incorporated TiO2/Basalt Fiber Films

    Directory of Open Access Journals (Sweden)

    Jeong Yeon Do

    2016-01-01

    Full Text Available Mineralogical basalt fibers as a complementary adsorbent were introduced to improve the adsorption of CO2 over the surfaces of photocatalysts. TiO2 photocatalysts (M-TiO2 incorporated with 5.0 mol.% 3d-transition metals (Fe, Co, Ni, and Cu were prepared using a solvothermal method and mixed with basalt fibers for applications to CO2 photoreduction. The resulting 5.0 mol.% M-TiO2 powders were characterized by X-ray diffraction, scanning electron microscopy, ultraviolet-visible spectroscopy, photoluminescence, Brunauer, Emmett, and Teller surface area, and CO2-temperature-programmed desorption. A paste composed of two materials was coated and fixed on a Pyrex plate by a thermal treatment. The 5.0 mol.% M-TiO2/basalt fiber films increased the adsorption of CO2 significantly, indicating superior photocatalytic behavior compared to pure TiO2 and basalt fiber films, and produced 158~360 μmol gcat-1 L−1 CH4 gases after an 8 h reaction. In particular, the best performance was observed over the 5.0 mol.% Co-TiO2/basalt fiber film. These results were attributed to the effective CO2 gas adsorption and inhibition of photogenerated electron-hole pair recombination.

  5. An impact of the copper additive on photocatalytic and bactericidal properties of TiO2 thin films

    Directory of Open Access Journals (Sweden)

    Wojcieszak Damian

    2017-07-01

    Full Text Available The biological and photocatalytic activity of TiO2 and TiO2:Cu in relation to their structure, surface topography, wettability and optical properties of the thin films was investigated. Thin-film coatings were prepared by magnetron sputtering method in oxygen plasma with use of metallic targets (Ti and Ti-Cu. The results of structural studies revealed that addition of Cu into titania matrix (during the deposition process resulted in obtaining of an amorphous film, while in case of undoped TiO2, presence of nanocrystalline anatase (with crystallites size of 20 nm was found. Moreover, an addition of cooper had also an effect on surface diversification and decrease of its hydrophilicity. The roughness of TiO2:Cu film was 25 % lower (0.6 nm as-compared to titania (0.8 nm. These modifications of TiO2:Cu had an impact on the decrease of its photocatalytic activity, probably as a result of the active surface area decrease. Antibacterial and antifungal properties of the thin films against bacteria (Enterococcus hirae, Staphylococcus aureus, Bacillus subtilis, Escherichia coli and yeast (Candida albicans were also examined. For the purpose of this work the method dedicated for the evaluation of antimicrobial properties of thin films was developed. It was revealed that Cu-additive has a positive impact on neutralization of microorganisms.

  6. Synthesis and photocatalytic properties of porous TiO2 films prepared by ODA/sol-gel method

    International Nuclear Information System (INIS)

    Zhang Wenjie; Bai Jiawei

    2012-01-01

    Porous TiO 2 films were deposited on SiO 2 pre-coated glass-slides by sol-gel method using octadecylamine (ODA) as template. The amount of ODA in the sol played an important role on the physicochemical properties and photocatalytic performance of the TiO 2 films. The films prepared at different conditions were all composed of anatase titanium dioxide crystals, and TiO 2 crystalline size got larger with increasing ODA amount. The maximum specific surface area of 41.5 m 2 /g was obtained for TiO 2 powders prepared from titanium sol containing 2.0 g ODA. Methyl orange degradation rate was enhanced along with increasing ODA amount and reached the maximal value at 2.0 g addition of ODA. After 40 min of UV-light irradiation, methyl orange degradation rate reached 30.5% on the porous film, which was about 10% higher than that on the smooth film. Porous TiO 2 film showed almost constant activity with slight decrease from 30.5% to 28.5% after 4 times of recycles.

  7. Optical and photoelectrochemical studies on Ag{sub 2}O/TiO{sub 2} double-layer thin films

    Energy Technology Data Exchange (ETDEWEB)

    Li, Chuan, E-mail: cli10@yahoo.com [Department of Biomedical Engineering, National Yang Ming University, Taipei, Taiwan 11221 (China); Department of Mechanical Engineering, National Central University, Jhongli, Taoyuan, Taiwan 32001 (China); Hsieh, J.H. [Department of Materials Engineering, Ming Chi University of Technology, Taishan, Taipei, Taiwan 24301 (China); Cheng, J.C. [Department of Electronic Engineering, National Taipei University of Technology, Taipei, Taiwan 10608 (China); Huang, C.C. [Department of Biomedical Engineering, National Yang Ming University, Taipei, Taiwan 11221 (China)

    2014-11-03

    When two different oxides films stacked together, if the absorption (upper) layer has both its conduction and valence bands more negatively lower than that of the layer underneath, then the photo-excited electrons can be forwarded to the underneath layer to become an effect of energy storage. Recent studies discovered that the double-layers of Cu{sub 2}O/TiO{sub 2} films possess such capacity. In order to investigate this specific phenomenon, we use a DC magnetron reactive sputtering to deposit a double-layer of Ag{sub 2}O/TiO{sub 2} films on glass substrate. The film thicknesses of the double-layer are 300 nm and 200 nm respectively. X-Ray diffraction (XRD), scanning electron microscope (SEM) and UV–VIS–NIR photospectrometer and photoluminance tests were used to study the structure, morphology, optical absorption and band gaps of the stacked films. From XRD and SEM, we can confirm the microstructures of each layer. The UV–VIS–NIR spectrum revealed that the optical absorption of Ag{sub 2}O/TiO{sub 2} fell in between the single film of Ag{sub 2}O and TiO{sub 2}. Further, two band gaps were estimated for Ag{sub 2}O/TiO{sub 2} films based on the Beer-Lambert law and Tauc plot. Photoluminance and photoelectrochemical tests indicated that delayed emission by electron-hole recombination and photoelectrical current was effectively support the mechanism of electrons transfer from Ag{sub 2}O to TiO{sub 2} at Ag{sub 2}O/TiO{sub 2} interface in the double-layer films. - Highlights: • A double-layer of Ag{sub 2}O/TiO{sub 2} films was deposited on glass substrate by sputtering. • XRD confirms the nanocrystalline structures of the stack deposited films. • UV–VIS–NIR spectroscopy shows the enhanced of optical absorption in Ag{sub 2}O/TiO{sub 2}. • Photoluminance and photoelectrochemical tests show electron-hole separation effect.

  8. Hydrogen irradiation on TiO{sub 2} nano-thin films

    Energy Technology Data Exchange (ETDEWEB)

    Heidari, Sh.; Mohammadizadeh, M.R. [University of Tehran, Superconductivity Research Laboratory (SRL), Department of Physics, Tehran (Iran, Islamic Republic of); Mahjour-Shafiei, M. [University of Tehran, Department of Physics, Tehran (Iran, Islamic Republic of); Larijani, M.M.; Malek, M. [Science and Technology Research Institute, Agricultural, Medical and Industrial Research School, Karaj (Iran, Islamic Republic of)

    2015-10-15

    Titanium dioxide thin films were coated on soda-lime glass substrates using spray pyrolysis method with a thickness of 152 ± 10 nm. The films were irradiated with hydrogen ions at room temperature at various beam energies and fluences. Optimized incident beam energy and beam fluence were obtained to improve photocatalytic and hydrophilicity properties of TiO{sub 2} thin films by narrowing the band gap. Samples were characterized by scanning electron microscopy to study the surface morphology and by UV-Vis absorption spectroscopy to measure the band gap. The optical band gap of H-doped anatase TiO{sub 2} thin films irradiated with hydrogen beam with energies of 2 and 4 keV and a fluence of 10{sup 15} ions/cm{sup 2} was narrowed from 3.34 eV (before irradiation) to 3.04 and 2.92 eV (after irradiation), respectively. The irradiated sample with energy of 4 keV with a fluence of 10{sup 15} ions/cm{sup 2} has the best improvement. This is attributed to the contraction of the band gap and to the increase in surface active site. Furthermore, it was observed that photocatalytic and hydrophilicity properties of this sample were improved, as well. (orig.)

  9. Perturbation of the Electron Transport Mechanism by Proton Intercalation in Nanoporous TiO2 Films

    Energy Technology Data Exchange (ETDEWEB)

    Halverson, A. F.; Zhu, K.; Erslev, P. T.; Kim, J. Y.; Neale, N. R.; Frank, A. J.

    2012-04-11

    This study addresses a long-standing controversy about the electron-transport mechanism in porous metal oxide semiconductor films that are commonly used in dye-sensitized solar cells and related systems. We investigated, by temperature-dependent time-of-flight measurements, the influence of proton intercalation on the electron-transport properties of nanoporous TiO{sub 2} films exposed to an ethanol electrolyte containing different percentages of water (0-10%). These measurements revealed that increasing the water content in the electrolyte led to increased proton intercalation into the TiO{sub 2} films, slower transport, and a dramatic change in the dependence of the thermal activation energy (E{sub a}) of the electron diffusion coefficient on the photogenerated electron density in the films. Random walk simulations based on a microscopic model incorporating exponential conduction band tail (CBT) trap states combined with a proton-induced shallow trap level with a long residence time accounted for the observed effects of proton intercalation on E{sub a}. Application of this model to the experimental results explains the conditions under which E{sub a} dependence on the photoelectron density is consistent with multiple trapping in exponential CBT states and under which it appears at variance with this model.

  10. Increased photocatalytic activity induced by TiO2/Pt/SnO2 heterostructured films

    Science.gov (United States)

    Testoni, Glaucio O.; Amoresi, Rafael A. C.; Lustosa, Glauco M. M. M.; Costa, João P. C.; Nogueira, Marcelo V.; Ruiz, Miguel; Zaghete, Maria A.; Perazolli, Leinig A.

    2018-02-01

    In this work, a high photocatalytic activity was attained by intercalating a Pt layer between SnO2 and TiO2 semiconductors, which yielded a TiO2/Pt/SnO2 - type heterostructure used in the discoloration of blue methylene (MB) solution. The porous films and platinum layer were obtained by electrophoretic deposition and DC Sputtering, respectively, and were both characterized morphologically and structurally by FE-SEM and XRD. The films with the Pt interlayer were evaluated by photocatalytic activity through exposure to UV light. An increase in efficiency of 22% was obtained for these films compared to those without platinum deposition. Studies on the reutilization of the films pointed out high efficiency and recovery of the photocatalyst, rendering the methodology favorable for the construction of fixed bed photocatalytic reactors. A proposal associated with the mechanism is discussed in this work in terms of the difference in Schottky barrier between the semiconductors and the electrons transfer and trapping cycle. These are fundamental factors for boosting photocatalytic efficiency.

  11. Preparation of anatase TiO{sub 2} thin film by low temperature annealing as an electron transport layer in inverted polymer solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Noh, Hongche [Department of Chemical Engineering, Hanyang University, Seoul 133-791 (Korea, Republic of); Oh, Seong-Geun, E-mail: seongoh@hanyang.ac.kr [Department of Chemical Engineering, Hanyang University, Seoul 133-791 (Korea, Republic of); Im, Seung Soon, E-mail: imss007@hanyang.ac.kr [Department of Organic and Nano Engineering, Hanyang University, Seoul 133-791 (Korea, Republic of)

    2015-04-01

    Highlights: • Anatase thin film of TiO{sub 2} was prepared by low temperature annealing. • Anatase TiO{sub 2} colloidal solution was obtained from amorphous form through solvothermal process. • Anatase TiO{sub 2} colloidal solution was used to prepare thin film on ITO glass. • Polymer solar cell fabricated on anatase TiO{sub 2} thin film showed 2.6% of PCE. - Abstract: To prepare the anatase TiO{sub 2} thin films on ITO glass, amorphous TiO{sub 2} colloidal solution was synthesized through the simple sol-gel method by using titanium (IV) isopropoxide as a precursor. This amorphous TiO{sub 2} colloidal solution was spread on ITO glass by spin-coating, then treated at 450 °C to obtain anatase TiO{sub 2} film (for device A). For other TiO{sub 2} films, amorphous TiO{sub 2} colloidal solution was treated through solvothermal process at 180 °C to obtain anatase TiO{sub 2} colloidal solution. This anatase TiO{sub 2} colloidal solution was spread on ITO glass by spin coating, and then annealed at 200 °C (for device B) and 130 °C (for device C), respectively. The average particle size of amorphous TiO{sub 2} colloidal solution was about 1.0 nm and that of anatase TiO{sub 2} colloidal solution was 10 nm. The thickness of TiO{sub 2} films was about 15 nm for all cases. When inverted polymer solar cells were fabricated by using these TiO{sub 2} films as an electron transport layer, the device C showed the highest PCE (2.6%) due to the lack of defect, uniformness and high light absorbance of TiO{sub 2} films. The result of this study can be applied for the preparation of inverted polymer solar cell using TiO{sub 2} films as a buffer layer at low temperature on plastic substrate by roll-to roll process.

  12. Adhesion and inactivation of Gram-negative and Gram-positive bacteria on photoreactive TiO2/polymer and Ag-TiO2/polymer nanohybrid films

    Science.gov (United States)

    Tallósy, Szabolcs Péter; Janovák, László; Nagy, Elisabeth; Deák, Ágota; Juhász, Ádám; Csapó, Edit; Buzás, Norbert; Dékány, Imre

    2016-05-01

    The aim of this study was to develop photoreactive surface coatings, possessing antibacterial properties and can be activated under visible light illumination (λmax = 405 nm) using LED-light source. The photocatalytically active titanium dioxide (TiO2) was functionalized with silver nanoparticles (Ag NPs) and immobilized in polyacrylate based nanohybrid thin film in order to facilitate visible light activity (λAg/TiO2,max = 500 nm). First, the photocatalytic activity was modelled by following ethanol vapor degradation. The plasmonic functionalization resulted in 15% enhancement of the activity compared to pure TiO2. The photoreactive antimicrobial (5 log reduction of cfu in 2 h) surface coatings are able to inactivate clinically relevant pathogen strains (methicillin resistant Staphylococcus aureus, Escherichia coli, Pseudomonas aeruginosa) within short time (60-120 min) due to the formed and quantified reactive oxygen species (ROS). The existence of electrostatic interactions between the negatively charged bacteria (from -0.89 to -3.19 μeq/109 cfu) and positively charged photocatalyst particles (in the range of +0.38 and +12.3 meq/100 g) was also proven by charge titration measurements. The surface inactivation of the bacteria and the photocatalytic degradation of the cell wall component were also confirmed by fluorescence and transmission electron microscopic observations, respectively. According to the results an effective sterilizing system and prevention strategy can be developed and carried out against dangerous microorganisms in health care.

  13. Visible light assisted photodecolorization of eosin-Y in aqueous solution using hesperidin modified TiO2 nanoparticles

    Science.gov (United States)

    Vignesh, K.; Suganthi, A.; Rajarajan, M.; Sakthivadivel, R.

    2012-03-01

    Hesperidin a flavanoid, modified TiO2 nanoparticles (Hes-TiO2) was synthesized to improve the visible light driven photocatalytic performance of TiO2. The synthesized nanoparticles were characterized by UV-visible diffuse reflectance spectroscopy (UV-vis-DRS), FT-IR, powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photocatalytic activity of Hes-TiO2 was investigated based on the decolorization of eosin-Y under visible light irradiation. Hes-TiO2 showed high efficiency for the decolorization of eosin-Y. The influences of various reaction parameters like effect of pH, catalyst dosage and initial dye concentration on the photocatalytic efficiency were investigated. The adsorption of eosin-Y on Hes-TiO2 was found favorable by the Langmuir approach. The removal percentage of chemical oxygen demand (COD) was determined to evaluate the mineralization of eosin-Y during photodecolorization. Based on the intermediates obtained in the GC-MS spectroscopic technique, a probable degradation mechanism has been proposed.

  14. Visible light assisted photodecolorization of eosin-Y in aqueous solution using hesperidin modified TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Vignesh, K.; Suganthi, A.; Rajarajan, M.; Sakthivadivel, R.

    2012-01-01

    Hesperidin a flavanoid, modified TiO 2 nanoparticles (Hes-TiO 2 ) was synthesized to improve the visible light driven photocatalytic performance of TiO 2 . The synthesized nanoparticles were characterized by UV-visible diffuse reflectance spectroscopy (UV-vis-DRS), FT-IR, powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photocatalytic activity of Hes-TiO 2 was investigated based on the decolorization of eosin-Y under visible light irradiation. Hes-TiO 2 showed high efficiency for the decolorization of eosin-Y. The influences of various reaction parameters like effect of pH, catalyst dosage and initial dye concentration on the photocatalytic efficiency were investigated. The adsorption of eosin-Y on Hes-TiO 2 was found favorable by the Langmuir approach. The removal percentage of chemical oxygen demand (COD) was determined to evaluate the mineralization of eosin-Y during photodecolorization. Based on the intermediates obtained in the GC-MS spectroscopic technique, a probable degradation mechanism has been proposed.

  15. Visible light assisted photodecolorization of eosin-Y in aqueous solution using hesperidin modified TiO{sub 2} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Vignesh, K. [P.G. and Research Department of Chemistry, Thiagarajar College, Madurai, Tamilnadu 625009 (India); Suganthi, A., E-mail: suganthiphd09@gmail.com [P.G. and Research Department of Chemistry, Thiagarajar College, Madurai, Tamilnadu 625009 (India); Rajarajan, M., E-mail: rajarajan_1962@yahoo.com [Department of Chemistry, C.P.A. College, Bodinayakanur, Tamilnadu 626513 (India); Sakthivadivel, R. [P.G. and Research Department of Chemistry, Thiagarajar College, Madurai, Tamilnadu 625009 (India)

    2012-03-01

    Hesperidin a flavanoid, modified TiO{sub 2} nanoparticles (Hes-TiO{sub 2}) was synthesized to improve the visible light driven photocatalytic performance of TiO{sub 2}. The synthesized nanoparticles were characterized by UV-visible diffuse reflectance spectroscopy (UV-vis-DRS), FT-IR, powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The photocatalytic activity of Hes-TiO{sub 2} was investigated based on the decolorization of eosin-Y under visible light irradiation. Hes-TiO{sub 2} showed high efficiency for the decolorization of eosin-Y. The influences of various reaction parameters like effect of pH, catalyst dosage and initial dye concentration on the photocatalytic efficiency were investigated. The adsorption of eosin-Y on Hes-TiO{sub 2} was found favorable by the Langmuir approach. The removal percentage of chemical oxygen demand (COD) was determined to evaluate the mineralization of eosin-Y during photodecolorization. Based on the intermediates obtained in the GC-MS spectroscopic technique, a probable degradation mechanism has been proposed.

  16. Ferroelectric properties of Pb(Zr,Ti)O3 films under ion-beam induced strain

    Science.gov (United States)

    Lee, Jung-Kun; Nastasi, Michael

    2012-11-01

    The influence of an ion-beam induced biaxial stress on the ferroelectric and dielectric properties of Pb(Zr,Ti)O3 (PZT) films is investigated using the ion beam process as a novel approach to control external stress. Tensile stress is observed to decrease the polarization, permittivity, and ferroelectric fatigue resistance of the PZT films whose structure is monoclinic. However, a compressive stress increases all of them in monoclinic PZT films. The dependence of the permittivity on stress is found not to follow the phenomenological theory relating external forces to intrinsic properties of ferroelectric materials. Changes in the ferroelectric and dielectric properties indicate that the application of a biaxial stress modulates both extrinsic and intrinsic properties of PZT films. Different degrees of dielectric non-linearity suggests the density and mobility of non-180o domain walls, and the domain switching can be controlled by an applied biaxial stress and thereby influence the ferroelectric and dielectric properties.

  17. Combined sonochemical/CVD method for preparation of nanostructured carbon-doped TiO{sub 2} thin film

    Energy Technology Data Exchange (ETDEWEB)

    Rasoulnezhad, Hossein [Semiconductor Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of); Kavei, Ghassem, E-mail: kaveighassem@gmail.com [Semiconductor Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of); Ahmadi, Kamran [Semiconductor Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of); Rahimipour, Mohammad Reza [Ceramic Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of)

    2017-06-30

    Highlights: • Combination of sonochemical and CVD methods for preparation of nanostructured carbon-doped TiO{sub 2} thin film on glass substrate, for the first time. • High transparency, monodispersity and homogeneity of the prepared thin films. • Preparation of the carbon-doped TiO{sub 2} thin films with nanorod and nanosphere morphologies. - Abstract: The present work reports the successful synthesis of the nanostructured carbon-doped TiO{sub 2} thin films on glass substrate by combination of chemical vapor deposition (CVD) and ultrasonic methods, for the first time. In this method the ultrasound waves act as nebulizer for converting of sonochemically prepared TiO{sub 2} sol to the mist particles. These mist particles were thermally decomposed in subsequent CVD chamber at 320 °C to produce the carbon-doped TiO{sub 2} thin films. The obtained thin films were characterized by means of X-ray Diffraction (XRD), Raman spectroscopy, diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and scanning electron microscopy (SEM) techniques. The results show that the prepared thin films have anatase crystal structure and nanorod morphology, which calcination of them at 800 °C results in the conversion of nanorods to nanoparticles. In addition, the prepared samples have high transparency, monodispersity and homogeneity. The presence of the carbon element in the structure of the thin films causes the narrowing of the band-gap energy of TiO{sub 2} to about 2.8 eV, which results in the improvement of visible light absorption capabilities of the thin film.

  18. Photocatalytic activity of tin-doped TiO{sub 2} film deposited via aerosol assisted chemical vapor deposition

    Energy Technology Data Exchange (ETDEWEB)

    Chua, Chin Sheng, E-mail: cschua@simtech.a-star.edu.sg [School of Electrical and Electronic Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 (Singapore); Singapore Institute of Manufacturing Technology, 71 Nanyang Drive, 638075 (Singapore); Tan, Ooi Kiang; Tse, Man Siu [School of Electrical and Electronic Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 (Singapore); Ding, Xingzhao [Singapore Institute of Manufacturing Technology, 71 Nanyang Drive, 638075 (Singapore)

    2013-10-01

    Tin-doped TiO{sub 2} films are deposited via aerosol assisted chemical vapor deposition using a precursor mixture composing of titanium tetraisopropoxide and tetrabutyl tin. The amount of tin doping in the deposited films is controlled by the volume % concentration ratio of tetrabutyl tin over titanium tetraisopropoxide in the mixed precursor solution. X-ray diffraction analysis results reveal that the as-deposited films are composed of pure anatase TiO{sub 2} phase. Red-shift in the absorbance spectra is observed attributed to the introduction of Sn{sup 4+} band states below the conduction band of TiO{sub 2}. The effect of tin doping on the photocatalytic property of TiO{sub 2} films is studied through the degradation of stearic acid under UV light illumination. It is found that there is a 10% enhancement on the degradation rate of stearic acid for the film with 3.8% tin doping in comparison with pure TiO{sub 2} film. This improvement of photocatalytic performance with tin incorporation could be ascribed to the reduction of electron-hole recombination rate through charge separation and an increased amount of OH radicals which are crucial for the degradation of stearic acid. Further increase in tin doping results in the formation of recombination site and large anatase grains, which leads to a decrease in the degradation rate. - Highlights: ► Deposition of tin-doped TiO{sub 2} film via aerosol assisted chemical vapor deposition ► Deposited anatase films show red-shifted in UV–vis spectrum with tin-dopants. ► Photoactivity improves at low tin concentration but reduces at higher concentration. ► Improvement in photoactivity due to bandgap narrowing from Sn{sup 4+} band states ► Maximum photoactivity achieved occurs for films with 3.8% tin doping.

  19. Properties of TiO{sub 2} thin films deposited by rf reactive magnetron sputtering on biased substrates

    Energy Technology Data Exchange (ETDEWEB)

    Nezar, Sawsen, E-mail: snezar@cdta.dz [Equipe Plasma & Applications, Division des Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées, Cité du 20 Aout 1956, Baba Hassen, Alger (Algeria); Laboratoire des phénomènes de transfert, génie chimique, Faculté de Génie des procèdes, USTHB, BP 32 El-alia, Bab Ezzouar, Alger (Algeria); Saoula, Nadia [Equipe Plasma & Applications, Division des Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées, Cité du 20 Aout 1956, Baba Hassen, Alger (Algeria); Sali, Samira [Centre de Recherche en Technologie des Semi-conducteurs pour l’Energétique (CRTSE Algiers) (Algeria); Faiz, Mohammed; Mekki, Mogtaba [Physics Department, King Fahd University of Petroleum and Minerals, Dhahran (Saudi Arabia); Laoufi, Nadia Aïcha [Laboratoire des phénomènes de transfert, génie chimique, Faculté de Génie des procèdes, USTHB, BP 32 El-alia, Bab Ezzouar, Alger (Algeria); Tabet, Nouar [Qatar Environment and Energy Research Institute, Hamad Bin Khalifa University (HBKU), Doha (Qatar)

    2017-02-15

    Highlights: • TiO{sub 2} thin films were deposited on negatively biased substrates by rf magnetron sputtering technique. • The bias favors the formation of TiO{sub 2} crystalline phase. • The roughness of the films increases and the grain size decreases as the bias voltage is varied between (0 and −100 V). • XPS reveals the presence of adsorbed humidity of the surface and Ti{sup 4+} oxidation state in the as prepared samples. - Abstract: TiO{sub 2} thin films are of paramount importance due to their pervasive applications. In contrast to previous published works where the substrate was heated at high temperatures to obtain TiO{sub 2} crystalline phase, we show in this study that it is possible to deposit crystalline TiO{sub 2} thin films on biased and unbiased substrate at room temperature using reactive rf magnetron sputtering. The bias voltage was varied from 0 V to −100 V. The deposited films were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), UV–vis spectroscopy, Raman spectroscopy, X-ray Photoelectron Spectroscopy (XPS) and atomic force microscopy (AFM). The average crystallite size was estimated using x-ray diffraction. The results showed that the application of negative bias affects the surface roughness of the films and favors the formation of the rutile phase. The root mean square roughness (R{sub rms}), the average grain size and the optical band gap of the films decreased as the substrate bias voltage was varied from 0 to −100 V. The UV–visible transmittance spectra showed that the films were transparent in the visible range and absorb strongly in the UV range. This study shows that biasing the substrate could be a promising and effective alternative to deposit TiO{sub 2} crystallized thin films of engineered properties at room temperature.

  20. Microstructure of Homoepitaxial SrTiO3 Films Deposited by Laser Ablation

    International Nuclear Information System (INIS)

    Tse, Y Y; Jackson, T J; Koutsonas, Y; Passerieux, G; Jones, I P

    2006-01-01

    Homoepitaxial strontium titanate thin films have been grown by pulsed laser deposition on (001) SrTiO 3 (STO) substrates with pulse rates ranging from 0.15 Hz to 100 Hz. The microstructure of the as-deposited films has been characterised by cross-sectional transmission electron microscopy. It is found that the growth mode and microstructure of the films are strongly influenced by the intervals between the laser pulses. Films have homogeneous microstructure under a critical thickness, above which the film breaks into toothlike columns. The growth is unstable against the formation of low angle boundaries which result in the formation of grains elongated in the direction of film growth. These become toothlike structures and the size of the tooth depends on the pulse rate and the growth time. The diffusion of point defects in films grown over a long time can lead instead to the development of elongated vacancy clusters directed normal to the film-vacuum interface. All films grow with a high density of point defects which may be related to deviation from the stoichiometry of the ceramic ablation target. Microanalysis suggests that there is strontium loss in the film, which causes defect formation inside the STO films

  1. Epitaxial c-axis oriented BaTiO{sub 3} thin films on SrTiO{sub 3}-buffered Si(001) by atomic layer deposition

    Energy Technology Data Exchange (ETDEWEB)

    Ngo, Thong Q.; McDaniel, Martin D.; Ekerdt, John G., E-mail: ekerdt@che.utexas.edu [Department of Chemical Engineering, The University of Texas at Austin, Austin, Texas 78712 (United States); Posadas, Agham B.; Demkov, Alexander A. [Department of Physics, The University of Texas at Austin, Austin, Texas 78712 (United States); Hu, Chengqing; Yu, Edward T. [Department of Electrical Engineering, The University of Texas at Austin, Austin, Texas 78712 (United States); Bruley, John [IBM Research Division, Yorktown Heights, New York 10593 (United States)

    2014-02-24

    Atomic layer deposition (ALD) of epitaxial c-axis oriented BaTiO{sub 3} (BTO) on Si(001) using a thin (1.6 nm) buffer layer of SrTiO{sub 3} (STO) grown by molecular beam epitaxy is reported. The ALD growth of crystalline BTO films at 225  °C used barium bis(triisopropylcyclopentadienyl), titanium tetraisopropoxide, and water as co-reactants. X-ray diffraction (XRD) reveals a high degree of crystallinity and c-axis orientation of as-deposited BTO films. Crystallinity is improved after vacuum annealing at 600  °C. Two-dimensional XRD confirms the tetragonal structure and orientation of 7–20-nm thick films. The effect of the annealing process on the BTO structure is discussed. A clean STO/Si interface is found using in-situ X-ray photoelectron spectroscopy and confirmed by cross-sectional scanning transmission electron microscopy. The capacitance-voltage characteristics of 7–20 nm-thick BTO films are examined and show an effective dielectric constant of ∼660 for the heterostructure.

  2. Epitaxial c-axis oriented BaTiO3 thin films on SrTiO3-buffered Si(001) by atomic layer deposition

    International Nuclear Information System (INIS)

    Ngo, Thong Q.; McDaniel, Martin D.; Ekerdt, John G.; Posadas, Agham B.; Demkov, Alexander A.; Hu, Chengqing; Yu, Edward T.; Bruley, John

    2014-01-01

    Atomic layer deposition (ALD) of epitaxial c-axis oriented BaTiO 3 (BTO) on Si(001) using a thin (1.6 nm) buffer layer of SrTiO 3 (STO) grown by molecular beam epitaxy is reported. The ALD growth of crystalline BTO films at 225  °C used barium bis(triisopropylcyclopentadienyl), titanium tetraisopropoxide, and water as co-reactants. X-ray diffraction (XRD) reveals a high degree of crystallinity and c-axis orientation of as-deposited BTO films. Crystallinity is improved after vacuum annealing at 600  °C. Two-dimensional XRD confirms the tetragonal structure and orientation of 7–20-nm thick films. The effect of the annealing process on the BTO structure is discussed. A clean STO/Si interface is found using in-situ X-ray photoelectron spectroscopy and confirmed by cross-sectional scanning transmission electron microscopy. The capacitance-voltage characteristics of 7–20 nm-thick BTO films are examined and show an effective dielectric constant of ∼660 for the heterostructure

  3. Photoelectrochemical hydrogen production from water/methanol decomposition using Ag/TiO{sub 2} nanocomposite thin films

    Energy Technology Data Exchange (ETDEWEB)

    Alenzi, Naser; Ehlig-Economides, Christine [Harold Vance Department of Petroleum Engineering, Texas A and M University, College Station, TX 77843 (United States); Liao, Wei-Ssu; Cremer, Paul S. [Department of Chemistry, Texas A and M University, College Station, TX 77843 (United States); Sanchez-Torres, Viviana; Cheng, Zhengdong [Artie McFerrin Department of Chemical Engineering, Texas A and M University, College Station, TX 77843 (United States); Wood, Thomas K. [Artie McFerrin Department of Chemical Engineering, Texas A and M University, College Station, TX 77843 (United States); Department of Biology, Texas A and M University, College Station, TX 77843-3258 (United States); Zachry Department of Civil and Environmental Engineering, Texas A and M University, College Station, TX 77843 3136 (United States)

    2010-11-15

    Though less frequently studied for solar-hydrogen production, films are more convenient to use than powders and can be easily recycled. Anatase TiO{sub 2} films decorated with Ag nanoparticles are synthesized by a rapid, simple, and inexpensive method. They are used to cleave water to produce H{sub 2} under UV light in the presence of methanol as a hole scavenger. A simple and sensitive method is established here to monitor the time course of hydrogen production for ultralow amounts of TiO{sub 2}. The average hydrogen production rate of Ag/TiO{sub 2} anatase films is 147.9 {+-} 35.5 {mu}mol/h/g. Without silver, it decreases dramatically to 4.65 {+-} 0.39 {mu}mol/h/g for anatase TiO{sub 2} films and to 0.46 {+-} 0.66 {mu}mol/h/g for amorphous TiO{sub 2} films fabricated at room temperature. Our method can be used as a high through-put screening process in search of high efficiency heterogeneous photocatalysts for solar-hydrogen production from water-splitting. (author)

  4. Uniform thin films of TiO2 nanoparticles deposited by matrix-assisted pulsed laser evaporation

    International Nuclear Information System (INIS)

    Caricato, A.P.; Manera, M.G.; Martino, M.; Rella, R.; Romano, F.; Spadavecchia, J.; Tunno, T.; Valerini, D.

    2007-01-01

    We report morphological and optical properties of a colloidal TiO 2 nanoparticle film, deposited on a quartz substrate by using the Matrix-Assisted Pulsed Laser Evaporation (MAPLE) technique. Atomic Force Microscopy demonstrated that a good uniformity of the deposition can be obtained. The presence of agglomerates with dimensions of about 1 μm in size was noticed. Form UV-vis transmission spectra, recorded in the 200-800 nm range, the optical constants and the energy gap were determined besides the film thickness. The optical constants resulted in agreement with the values reported in literature for TiO 2 nanoparticle thin films

  5. Photo-induced hydrophilicity of TiO2-xNx thin films on PET plates

    International Nuclear Information System (INIS)

    Chou, H.-Y.; Lee, E.-K.; You, J.-W.; Yu, S.-S.

    2007-01-01

    TiO 2-x N x thin films were deposited on PET (polyethylene terephthalate) plates by sputtering a TiN target in a N 2 /O 2 plasma and without heating. X-ray photoemission spectroscopy (XPS) was used to investigate the N 1s, Ti 2p core levels and the nitrogen composition in the TiO 2-x N x films. The results indicate that Ti-O-N bonds are formed in the thin films. Two nitrogen states, substitution and interstitial nitrogen atoms, were attributed to peaks at 396 and 399 eV, respectively. It was observed that the nitrogen atoms occupy both the substitutive and interstitial sites in respective of the nitrogen content in the thin films. UV-VIS absorption spectroscopy of PET coated thin films shows a significant shift of the absorption edge to lower energy in the visible-light region. UV and visible-light irradiation are used to activate PET coated thin films for the development of hydrophilicity. The photo-induced surface wettability conversion reaction of the thin films has been investigated by means of water contact angle measurement. PET plates coated with TiO 2-x N x thin films are found to exhibit lower water contact angle than non-coated plates when the surface is illuminated with UV and visible light. The effects of nitrogen doping on photo-generated hydrophilicity of the thin films are investigated in this work

  6. Effect of TiO{sub 2} nanopatterns on the performance of hydrogenated amorphous silicon thin-film solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Oh, Joon-Ho [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Yang, Ji-Hwan; Lim, Koeng Su [Department of Electrical Engineering, Korea Advanced Institute of Science and Technology, Daejeon 305-701 (Korea, Republic of); Han, Kang-Soo; Kim, Yang-Doo; Lee, Heon; Song, Jun-Hyuk [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Kim, Kyoung-Kook [Department of Nano-Optical Engineering, Korea Polytechnic University, Gyeonggi 429-793 (Korea, Republic of); Seong, Tae-Yeon, E-mail: tyseong@korea.ac.kr [Department of Materials Science and Engineering, Korea University, Seoul 136-713 (Korea, Republic of)

    2012-07-31

    We investigate how TiO{sub 2} nanopatterns formed onto ZnO:Al (AZO) films affect the performance of hydrogenated amorphous silicon (a-Si:H) solar cells. Scanning electron microscopy results show that the dome-shaped TiO{sub 2} nanopatterns (300 nm in diameter) having a period of 500 nm are formed onto AZO films and vary from 60 to 180 nm in height. Haze factor increases with an increase in the height of the nanopatterns in the wavelength region below 530 nm. Short circuit current density also increases with an increase in the height of the nanopatterns. As the nanopatterns increases in height, the fill factor of the cells slightly increases, reaches maximum (0.64) at 100 nm, and then decreases. Measurements show that a-Si:H solar cells fabricated with 100 nm-high TiO{sub 2} nanopatterns exhibit the highest conversion efficiency (6.34%) among the solar cells with the nanopatterns and flat AZO sample. - Highlights: Black-Right-Pointing-Pointer We investigated the height effect of TiO{sub 2} nanopatterns on the a-Si:H solar cells. Black-Right-Pointing-Pointer Light scattering and anti-reflection were introduced by TiO{sub 2} nanopatterns. Black-Right-Pointing-Pointer a-Si:H Solar cells with the 100 nm-high TiO{sub 2} nanopatterns showed highest efficiency.

  7. Hybrid Solar Cell with TiO2 Film: BBOT Polymer and Copper Phthalocyanine as Sensitizer

    Directory of Open Access Journals (Sweden)

    Saptadip Saha

    2016-01-01

    Full Text Available An organic-inorganic hybrid solar cell was fabricated using Titanium dioxide (TiO2: 2,5-bis(5-tert-butyl-2-benzoxazolyl thiophene (BBOT film and Copper Phthalocyanine (CuPc as a sensitizer. BBOT was used in photodetector in other reported research works, but as per best of our knowledge, it was not implemented in solar cells till date. The blend of TiO2: BBOT blend was used to fabricate the film on ITO-coated glass and further a thin layer of CuPc was coated on the film. This was acted as photoanode and another ITO coated glass with a platinum coating was used as a counter electrode (cathode. An optimal blend of acetonitrile (solvent (50-100%, 1,3-dimethylimidazolium iodide (10-25%, iodine (2.5-10% and lithium iodide, pyridine derivative and thiocyanate was used as electrolytes in the hybrid solar cell. The different structural, optical and electrical characteristics were measured. The Hybrid solar cell showed a maximum conversion efficiency of 6.51%.

  8. Growth of TiO2 Thin Film on Various Substrates using RF Magnetron Sputtering

    International Nuclear Information System (INIS)

    Ali, Riyaz Ahmad Mohamed; Nayan, Nafarizal

    2011-01-01

    The conductivity of Titanium Dioxide (TiO 2 ) thin film fabricated using Radio Frequency (RF) Magnetron Sputtering on Silicon (Si), Indium doped--Tin Oxide (ITO) and microscope glass (M) substrates is presented in this paper. The dependant of thin film thickness and type of substrate been discussed. TiO 2 was deposited using Ti target in Ar+O 2 (45:10) mixture at 250 W for 45, 60, 75, 90, 105 and 120 minute. Resultant thickness varies from 295 nm to 724 nm with deposition rate 6.4 nm/min. On the other hand, resistivity, Rs value for ITO substrate is between 5.72x10 -7 to 1.54x10 -6 Ω.m, Si substrate range is between 3.52x10 -6 to 1.76x10 -5 Ω.m and M substrate range is between 99 to 332 Ω.m. The value of resistivity increases with the thickness of the thin film.

  9. Structural Properties of Nanoparticles TiO2/PVA Polymeric Films

    Directory of Open Access Journals (Sweden)

    Samara A. Madhloom

    2018-04-01

    Full Text Available In this research, X-ray diffraction of the powder (PVA polymer, titanium dioxide with two parti-cle sizes and (TiO2 (15.7 nm/PVA and TiO2 (45.7 nm/PVA films have been studied,the amount of polymer is (0.5 g and (0.01g from each particle sizes of nanoparticles will be used. Casting method is used to prepare homogeneous films on glass petri dishes. All parameters ac-counted for the X-ray diffraction; full width half maximum (FWHM, Miller indices (hkl, size of crystalline (D, Specific Surface Area (S and Dislocation Density (δ. The nature of the structural of materials and films will be investigated. The XRD pattern of PVA polymer has semi-crystalline nature and the titanium dioxide with two particle sizes have crystalline structure; ana-tase type. While the mixture between these materials led to appearing some crystalline peaks into XRD pattern of PVA polymer

  10. Giant piezoelectric voltage coefficient in grain-oriented modified PbTiO3 material.

    Science.gov (United States)

    Yan, Yongke; Zhou, Jie E; Maurya, Deepam; Wang, Yu U; Priya, Shashank

    2016-10-11

    A rapid surge in the research on piezoelectric sensors is occurring with the arrival of the Internet of Things. Single-phase oxide piezoelectric materials with giant piezoelectric voltage coefficient (g, induced voltage under applied stress) and high Curie temperature (T c ) are crucial towards providing desired performance for sensing, especially under harsh environmental conditions. Here, we report a grain-oriented (with 95% texture) modified PbTiO 3 ceramic that has a high T c (364 °C) and an extremely large g 33 (115 × 10 -3  Vm N -1 ) in comparison with other known single-phase oxide materials. Our results reveal that self-polarization due to grain orientation along the spontaneous polarization direction plays an important role in achieving large piezoelectric response in a domain motion-confined material. The phase field simulations confirm that the large piezoelectric voltage coefficient g 33 originates from maximized piezoelectric strain coefficient d 33 and minimized dielectric permittivity ɛ 33 in [001]-textured PbTiO 3 ceramics where domain wall motions are absent.

  11. TiO2-anatase modified by carbon as the photo catalyst under visible light

    International Nuclear Information System (INIS)

    Morawski, A.W.; Janus, M.; Tryba, B.; Kalucki, K.; Tryba, B.; Inagaki, M.

    2006-01-01

    The photo-catalytic oxidation of phenol in water under a visible light over anatase-type titanium dioxide (Tytanpol A11, Poland), modified by carbon deposited via n-hexane carbonization, was investigated. The catalysts, which had small (0-0.2 mass%) and high (0.69-0.85 mass%) contents of carbon showed a little lower catalytic photo-activity than pristine TiO 2 . However, the catalyst with high content of carbon (0.85 mass%) gave almost 14-times lower turbidity in the phenol solution after the photo-catalyst sedimentation. These two factors depend on the carbon content and have an influence on the 'practical efficiency' of the catalysts. The 'practical efficiency' of the catalyst under visible light, calculated from these two factors, was therefore 14-times higher for the catalyst containing 0.85 mass% carbon (whereas for UV radiation, it was found to be lower - 0.2 mass% -; this is the result of a previous work). The surface modification of the catalyst with 0.85% carbon seemed to be stable under visible light. The deposition of carbon on TiO 2 by carbonization of n-hexane was supposed to lead to obtain the catalyst, which could be easily used in a water-treatment system under visible light. (authors)

  12. Formation of TiO2 domains in Poly (9-vinylcarbazole) thin film by hydrolysis-condensation of a metal alkoxide

    International Nuclear Information System (INIS)

    Barlier, V.; Bounor-Legare, V.; Alcouffe, P.; Boiteux, G.; Davenas, J.

    2007-01-01

    New organic-inorganic hybrid thin films based on Poly (9-vinylcarbazole) (P9VK) and Dioxide titanium (TiO 2 ) bulk-heterojunction were obtained by a hydrolysis-condensation (H-C) process of titanium (IV) isopropoxide in thin film. The TiO 2 distribution in the film was investigated by scanning electron microscopy. The results indicated that homogeneous TiO 2 particles around 100 nm were formed on the surface of the polymer thin film. Photoluminescence spectroscopy has been used to study the charge transfer efficiency in the photoactive layer and results were compared with a simplest elaboration route, the dispersion of TiO 2 anatase in a P9VK solution before spin coating. Results showed that TiO 2 elaborated by H-C exhibits a competitive quenching effect with TiO 2 anatase

  13. A first-principles study of phase transitions in ultrathin films of BaTiO 3

    Indian Academy of Sciences (India)

    We determine the effects of film thickness, epitaxial strain and the nature of electrodes on ferroelectric phase transitions in ultrathin films of BaTiO3 using a first-principles effective Hamiltonian in classical molecular dynamics simulations. We present results for polarization and dielectric properties as a function of temperature ...

  14. Piezoelectric properties of PbTiO(3) thin films characterized with piezoresponse force and high resolution transmission electron microscopy

    NARCIS (Netherlands)

    Morelli, A.; Venkatesan, Sriram; Kooi, B. J.; Palasantzas, G.; De Hosson, J. Th. M.

    2009-01-01

    In this paper we investigate the piezoelectric properties of PbTiO(3) thin films grown by pulsed laser deposition with piezoresponse force microscopy and transmission electron microscopy. The as-grown films exhibit an upward polarization, inhomogeneous distribution of piezoelectric characteristics

  15. Plasmonic metamaterial-based chemical converted graphene/TiO2/Ag thin films by a simple spray pyrolysis technique

    Science.gov (United States)

    Kumar, Promod; Swart, H. C.

    2018-04-01

    Graphene based hybrid nanostructures have received special attention in both the scientific and technological development due to their unique physicochemical behavior, which make them attractive in various applications such as, batteries, supercapacitors, fuel cells, solar cells, photovoltaic devices and bio-sensors. In the present study, the role of plasmonic metamaterials in light trapping photovoltaics for inorganic semiconducting materials by a simple and low cost spray pyrolysis technique has been studied. The plasmonic metamaterials thin film has been fabricated by depositing chemically converted graphene (CCG) onto TiO2-Ag nanoparticles which has a low resistivity and a low electron-hole recombination probability. The localized surface plasmon resonance at the metal-dielectric interface for the Ag nanoparticles has been observed at 403 nm after depositing chemical converted graphene (CCG) on the TiO2-Ag thin film. The results suggest that the stacking order of the CCG/TiO2/Ag plasmonic metamaterials samples did not change the band gap of TiO2 while it changed the conductivity of the film. Thus the diffusion of the noble metals in the glass and TiO2 matrices based thin films can trap the light of a particular wavelength by mean of plasmonic resonance and may be useful for superior photovoltaic and optoelectronic applications.

  16. Phase transformation synthesis of TiO2/CdS heterojunction film with high visible-light photoelectrochemical activity

    Science.gov (United States)

    Liu, Canjun; Yang, Yahui; Li, Jie; Chen, Shu

    2018-06-01

    CdS/TiO2 heterojunction film used as a photoanode has attracted much attention in the past few years due to its good visible light photocatalytic activity. However, CdS/TiO2 films prepared by conventional methods (successive ionic layer adsorption and reaction, chemical bath deposition and electrodeposition) show numerous grain boundaries in the CdS layer and an imperfect contact at the heterojunction interface. In this study, we designed a phase transformation method to fabricate CdS/TiO2 nanorod heterojunction films. The characterization results showed that the CdS layer with fewer grain boundaries was conformally coated on the TiO2 nanorod surface and the formation mechanism has been explained in this manuscript. Moreover, the prepared CdS/TiO2 films show a high photocatalytic activity and the photocurrent density is as high as 9.65 mA cm‑2 at 0.80 V versus RHE. It may be attributed to fewer grain boundaries and a compact heterojunction contact, which can effectively improve charge separation and transportation.

  17. Influence of Nd-Doping on Photocatalytic Properties of TiO2 Nanoparticles and Thin Film Coatings

    Directory of Open Access Journals (Sweden)

    Damian Wojcieszak

    2014-01-01

    Full Text Available Structural, optical, and photocatalytic properties of TiO2 and TiO2:Nd nanopowders and thin films composed of those materials have been compared. Titania nanoparticles with 1, 3, and 6 at. % of Nd-dopant were synthesized by sol-gel method. Additionally, thin films with the same material composition were prepared with the aid of spin-coating method. The analysis of structural investigations revealed that all as-prepared nanopowders were nanocrystalline and had TiO2-anatase structure. The average size of crystallites was ca. 4-5 nm and the correlation between the amount of neodymium and the size of TiO2 crystallites was observed. It was shown that the dopant content influenced the agglomeration of the nanoparticles. The results of photocatalytic decomposition of MO showed that doping with Nd (especially in the amount of 3 at. % increased self-cleaning activity of the prepared titania nanopowder. Similar effect was received in case of the thin films, but the decomposition rate was lower due to their smaller active surface area. However, the as-prepared TiO2:Nd photocatalyst in the form of thin films or nanopowders seems to be a very attractive material for various applications.

  18. Passivation of pigment-grade TiO2 particles by nanothick atomic layer deposited SiO2 films

    International Nuclear Information System (INIS)

    King, David M; Liang Xinhua; Weimer, Alan W; Burton, Beau B; Akhtar, M Kamal

    2008-01-01

    Pigment-grade TiO 2 particles were passivated using nanothick insulating films fabricated by atomic layer deposition (ALD). Conformal SiO 2 and Al 2 O 3 layers were coated onto anatase and rutile powders in a fluidized bed reactor. SiO 2 films were deposited using tris-dimethylaminosilane (TDMAS) and H 2 O 2 at 500 deg. C. Trimethylaluminum and water were used as precursors for Al 2 O 3 ALD at 177 deg. C. The photocatalytic activity of anatase pigment-grade TiO 2 was decreased by 98% after the deposition of 2 nm SiO 2 films. H 2 SO 4 digest tests were performed to exhibit the pinhole-free nature of the coatings and the TiO 2 digest rate was 40 times faster for uncoated TiO 2 than SiO 2 coated over a 24 h period. Mass spectrometry was used to monitor reaction progress and allowed for dosing time optimization. These results demonstrate that the TDMAS-H 2 O 2 chemistry can deposit high quality, fully dense SiO 2 films on high radius of curvature substrates. Particle ALD is a viable passivation method for pigment-grade TiO 2 particles

  19. Deposition of SrTiO3 films by electrophoresis with thickness and particle size control

    International Nuclear Information System (INIS)

    Junior, W.D.M.; Pena, A.F.V.; Souza, A.E.; Santos, G.T.A.; Teixeira, S.R.; Senos, A.M.R.; Longo, E.

    2012-01-01

    The SrTiO3 (ST) is a material that exhibits semiconducting characteristics and interesting electrical properties. In room temperature has a structure of high cubic symmetry. The size of the crystallites of this material directly influences this symmetry, changing its network parameters. ST nanoparticles are obtained by hydrothermal method assisted by microwave (MAH). ST films are prepared by electrophoretic deposition (EPD). Approximately 1 g of the powder is dissolved in 100 ml of acetone and 1.5 ml of triethanolamine. The stainless steel substrates are arranged horizontally in the solution. The depositions are performed for 1-10 min and subjected to a potential difference of 20-100 V. The films were characterized by x-ray diffraction (XRD) and atomic force microscopy (AFM). The characterizations show that it is possible to control both the thickness and size of the crystallites of the film depending on the deposition parameters adopted. (author)

  20. Giant Polarization Rotation in BiFeO3/SrTiO3 Thin Films.

    Science.gov (United States)

    Langner, M. C.; Chu, Y. H.; Martin, L. M.; Gajek, M.; Ramesh, R.; Orenstein, J.

    2008-03-01

    We use optical second harmonic generation to probe dynamics of the ferroelectric polarization in (111) oriented BiFeO3 thin films grown on SrTiO3 substrates. The second harmonic response indicates 3m point group symmetry and is consistent with a spontaneous polarization normal to the surface of the film. We measure large changes in amplitude and lowering of symmetry, consistent with polarization rotation, when modest electric fields are applied in the plane of the film. At room temperature the rotation is an order of magnitude larger than expected from reported values of the dielectric constant and increases further (as 1/T) as temperature is lowered. We propose a substrate interaction model to explain these results.

  1. Elaboration of TiO2 films by PECVD for use in photocatalysis

    International Nuclear Information System (INIS)

    Di Lalla, N; Lasorsa, C; Pineda Ramos, P

    2012-01-01

    We present the first results in the production of films of titanium dioxide (TiO 2 ) deposited by Plasma enhanced chemical vapor deposition (PECVD). The films are destined for use in photocatalysis for water treatment. The deposits were made on glass from titanium isopropoxide as precursor (Ti[OCH(CH 3 ) 2 ]4) and a controlled flow of O 2 . The films were grown at room temperature and 300 o C to compare properties. The characterization of the deposits was performed using scanning electron microscopy, UV-visible transmittance and infrared absorbance. The deposits were obtained with very good adhesion to substrates showing energy values of band gap of 2.83 eV

  2. Efficient degradation of H2S over transition metal modified TiO2 under VUV irradiation: Performance and mechanism

    Science.gov (United States)

    Liu, Gaoyuan; Ji, Jian; Hu, Peng; Lin, Sixin; Huang, Haibao

    2018-03-01

    Odor pollution causes great harm to the atmospheric environment and human health. H2S, as an odor gas, is highly toxic and corrosive and thus requires removal efficiently. In this study, TiO2 catalysts modified by transition metals including Mn, Cu, Ni and Co, were prepared using a modified sol-gelatin method and tested under UV-PCO or VUV-PCO process. H2S degradation was great enhanced in VUV-PCO compared with conventional UV-PCO. Among the catalysts, 1 wt% Mn-TiO2 showed the highest removal efficiency of 89.9%, which is 30 times higher than that under 254 nm UV irradiation. Residual ozone in the outlet can be completely eliminated by Mn-TiO2. Photocatalytic oxidation, photolysis and ozone-assisted catalytic oxidation all involved in the VUV-PCO process and their contribution were determined by H2S removal efficiency.

  3. Removal of U(VI) from aqueous solution using TiO{sub 2} modified β-zeolite

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Peng; Yuan, Ni; Xiong, Wei; Wu, Hanyu; Pan, Duoqiang; Wu, Wangsuo [Lanzhou Univ. (China). Radiochemistry and Nuclear Environment Laboratory; Ministry of Education, Lanzhou (China). Key Laboratory of Special Function Materials and Structure Design

    2017-07-01

    β-Zeolite was synthesized and modified with TiO{sub 2}. The synthesized materials were characterized and used for removal of U(VI) from aqueous solutions. The influences of pH, contact time and temperature on U(VI) adsorption onto modified β-zeolite by TiO{sub 2} were studied by batch technique, and XPS was employed to analysed the experimental data. The dynamic process showed that the adsorption of U(VI) onto TiO{sub 2}/β-zeolite matched the pseudo-second-order kinetics model, and the adsorption of U(VI) were significantly dependent on pH values. Through simulating the adsorption isotherms by Langmuir, Freundlich and Dubini-Radushkevich (D-R) models, it could be seen, respectively that the adsorption patterns of U(VI) onto TiO{sub 2}/β-zeolite were mainly controlled by surface complexation, and the adsorption processes were endothermic and spontaneous. The modification of β-zeolite by TiO{sub 2} it shows a novel material for the removing of U(VI) from water environment for industrialized application.

  4. Properties of reactively radio frequency-magnetron sputtered (Zr,Sn)TiO4 dielectric films

    International Nuclear Information System (INIS)

    Huang, C.-L.; Hsu, C.-H.

    2004-01-01

    Zirconium tin titanium oxide doped 1 wt % ZnO thin films on n-type Si substrate were deposited by rf magnetron sputtering at a fixed rf power of 350 W with various argon-oxygen (Ar/O 2 ) mixture and different substrate temperatures. Electrical properties and microstructures of ZnO-doped (Zr 0.8 Sn 0.2 )TiO 4 thin films prepared by rf magnetron sputtering on n-type Si(100) substrates at different Ar/O 2 ratios and substrate temperatures have been investigated. The surface structural and morphological characteristics analyzed by x-ray diffraction, scanning electron microscopy, and atomic force microscope were sensitive to the deposition conditions, such as Ar/O 2 ratio (100/0-80/20) and substrate temperature (350 deg. C-450 deg. C). The selected-area diffraction pattern showed that the deposited films exhibited a polycrystalline microstructure. All films exhibited ZST (111) orientation perpendicular to the substrate surface and the grain size as well as the deposition rate of the films increased with the increase of both the Ar partial pressure and the substrate temperature. At a Ar/O 2 ratio of 100/0, rf power level of 350 W and substrate temperature of 450 deg. C, the Zr 0.8 Sn 0.2 TiO 4 films with 6.44 μm thickness possess a dielectric constant of 42 (at 10 MHz), a dissipation factor of 0.065 (at 10 MHz), and a leakage current density of 2x10 -7 A/cm 2 at an electrical field of 1 kV/cm

  5. Preparation of TiO{sub 2} films by layer-by-layer assembly and their application in solar cell

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, L. [School of Chemistry and Chemical Engineering, Anhui University, Hefei 230039 (China); Anhui Key Laboratory of Spin Electron and Nanomaterials (Cultivating Base), Suzhou University, Suzhou 234000 (China); Xie, A.J. [School of Chemistry and Chemical Engineering, Anhui University, Hefei 230039 (China); Shen, Y.H., E-mail: s_yuhua@163.co [School of Chemistry and Chemical Engineering, Anhui University, Hefei 230039 (China); Li, S.K. [School of Chemistry and Chemical Engineering, Anhui University, Hefei 230039 (China)

    2010-09-03

    Polyacrylate sodium (PAAS)/titania (TiO{sub 2}) multilayers have been fabricated through the electrostatic layer-by-layer assembly technique. The composite films display an excellent photovoltaic performance after sintering and sensitization by cyanine dye (CD), which can be applied in dye-sensitized solar cells. The properties of PAAS/TiO{sub 2} multilayers are investigated by ultraviolet-visible spectroscopy (UV-vis), X-ray photoelectron spectroscopy (XPS), X-ray diffraction analysis (XRD), Thermogravimetric analysis (TGA), and photovoltaic measurements. The results indicate that the thermal stability of the PAAS has a direct influence on the performance of dye-sensitized solar cells. The energy conversion efficiency of approximately 1.29% was obtained for dye-sensitized solar cell with TiO{sub 2}/PAAS (40 bilayers) as precursor film. In addition, the composite films also show a good self-cleaning property for photocatalytic degradation of methylene blue.

  6. Effect of laser irradiation on the structural, morphological and electrical properties of polycrystalline TiO2 thin films

    Science.gov (United States)

    Khan, M. I.; Ali, Asghar

    TiO2 thin film is deposited on glass substrate by sol-gel dip coating technique. After deposition, films were irradiated by continuous wave (CW) diode laser at an angle of 45°. XRD shows both the anatase and brookite phases of TiO2. Nano particles of regular and control sizes are appeared in SEM micrographs. Therefore, shape and size of nano particles can be control by using Laser irradiation. The average sheet resistivity of TiO2 thin film irradiated by 0, 2, 4 and 6 min are 6.72 × 105, 5.32 × 105, 3.44 × 105 and 4.95 × 105 (ohm-m) respectively, according to four point probe.

  7. Preparation of hydrogenated-TiO2/Ti double layered thin films by water vapor plasma treatment

    International Nuclear Information System (INIS)

    Pranevicius, L.L.; Milcius, D.; Tuckute, S.; Gedvilas, K.

    2012-01-01

    Highlights: ► We investigated reaction of water plasma with nanocrystalline TiO 2 films. ► Simultaneous oxidation and hydrogenation of Ti was observed during plasma treatment. ► Water plasma treatment forms hydrogenated nanocrystalline TiO 2 in the shallow surface. - Abstract: We have investigated the structural and compositional variations in 200–500 nm thick Ti films deposited by magnetron sputter-deposition technique and treated in water vapor plasma at different processing powers. It was found that the upper layer of treated film with the thickness of 110 nm was changed into the black hydrogenated-TiO 2 with around 16 nm sized nanocystals during 10 min for dissipated power 200 W at room temperature. Analysis of the experimental results is used to obtain insights into the effects of water layer adsorbed on hydrophilic oxidized titanium surfaces exposed to plasma radiation.

  8. Properties of TiO2-based transparent conducting oxide thin films on GaN(0001) surfaces

    International Nuclear Information System (INIS)

    Kasai, J.; Nakao, S.; Yamada, N.; Hitosugi, T.; Moriyama, M.; Goshonoo, K.; Hoang, N. L. H.; Hasegawa, T.

    2010-01-01

    Anatase Nb-doped TiO 2 transparent conducting oxide has been formed on GaN(0001) surfaces using a sputtering method. Amorphous films deposited at room temperature were annealed at a substrate temperature of 500 deg. C in vacuum to form single-phase anatase films. Films with a thickness of 170 nm exhibited a resistivity of 8x10 -4 Ω cm with absorptance less than 5% at a wavelength of 460 nm. Furthermore, the refractive index of the Nb-doped TiO 2 was well matched to that of GaN. These findings indicate that Nb-doped TiO 2 is a promising material for use as transparent electrodes in GaN-based light emitting diodes (LEDs), particularly since reflection at the electrode/GaN boundary can be suppressed, enhancing the external quantum efficiency of blue LEDs.

  9. The effect of bulk/surface defects ratio change on the photocatalysis of TiO_2 nanosheet film

    International Nuclear Information System (INIS)

    Wang, Fangfang; Ge, Wenna; Shen, Tong; Ye, Bangjiao; Fu, Zhengping; Lu, Yalin

    2017-01-01

    Highlights: • The defect behaviors of TiO_2 nanosheet array films were studied by positron annihilation spectroscopy. • Different bulk/surface defect ratios were realized by annealing at different temperature. • It was concluded that bulk defects are mainly Ti"3"+ vacancy defects. • The separation efficiency of photogenerated electrons and holes could be significantly improved by optimizing the bulk/surface defects ratio. - Abstract: The photocatalysis behavior of TiO_2 nanosheet array films was studied, in which the ratio of bulk/surface defects were adjusted by annealing at different temperature. Combining positron annihilation spectroscopy, EPR and XPS, we concluded that the bulk defects belonged to Ti"3"+ related vacancy defects. The results show that the separation efficiency of photogenerated electrons and holes could be significantly improved by optimizing the bulk/surface defects ratio of TiO_2 nanosheet films, and in turn enhancing the photocatalysis behaviors.

  10. The effect of bulk/surface defects ratio change on the photocatalysis of TiO{sub 2} nanosheet film

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Fangfang [CAS Key Laboratory of Materials for Energy Conversion, Department of Materials Science and Engineering, University of Science and Technology of China, Hefei 230026 (China); Ge, Wenna [State Key Laboratory of Particle Detection and Electronics, University of Science and Technology of China, Hefei 230026 (China); Department of Modern Physics, University of Science and Technology of China, Hefei 230026 (China); Shen, Tong [CAS Key Laboratory of Materials for Energy Conversion, Department of Materials Science and Engineering, University of Science and Technology of China, Hefei 230026 (China); Ye, Bangjiao [State Key Laboratory of Particle Detection and Electronics, University of Science and Technology of China, Hefei 230026 (China); Department of Modern Physics, University of Science and Technology of China, Hefei 230026 (China); Fu, Zhengping, E-mail: fuzp@ustc.edu.cn [CAS Key Laboratory of Materials for Energy Conversion, Department of Materials Science and Engineering, University of Science and Technology of China, Hefei 230026 (China); Lu, Yalin, E-mail: yllu@ustc.edu.cn [CAS Key Laboratory of Materials for Energy Conversion, Department of Materials Science and Engineering, University of Science and Technology of China, Hefei 230026 (China); Synergetic Innovation Center of Quantum Information & Stop Quantum Physics, University of Science and Technology of China, Hefei 230026 (China); National Synchrotron Radiation Laboratory, University of Science and Technology of China, Hefei 230026, Anhui (China)

    2017-07-15

    Highlights: • The defect behaviors of TiO{sub 2} nanosheet array films were studied by positron annihilation spectroscopy. • Different bulk/surface defect ratios were realized by annealing at different temperature. • It was concluded that bulk defects are mainly Ti{sup 3+} vacancy defects. • The separation efficiency of photogenerated electrons and holes could be significantly improved by optimizing the bulk/surface defects ratio. - Abstract: The photocatalysis behavior of TiO{sub 2} nanosheet array films was studied, in which the ratio of bulk/surface defects were adjusted by annealing at different temperature. Combining positron annihilation spectroscopy, EPR and XPS, we concluded that the bulk defects belonged to Ti{sup 3+} related vacancy defects. The results show that the separation efficiency of photogenerated electrons and holes could be significantly improved by optimizing the bulk/surface defects ratio of TiO{sub 2} nanosheet films, and in turn enhancing the photocatalysis behaviors.

  11. Photoanode of Dye-Sensitized Solar Cells Based on a ZnO/TiO2 Composite Film

    Directory of Open Access Journals (Sweden)

    Lu-Ting Yan

    2012-01-01

    Full Text Available A photoanode of dye-sensitized solar cells based on a ZnO/TiO2 composite film was fabricated on a transparent conductive glass substrate using different techniques including electrophoretic deposition, screen printing, and colloidal spray coating. The ZnOs used in the composite film were ZnO tetrapods prepared via thermal evaporation and ZnO nanorods obtained via hydrothermal growth. The structural and morphological characterizations of the thin composite films were carried out using scanning electron microscope (SEM. The best power conversion was 1.87%, which corresponds to the laminated TiO2/ZnO/TiO2 structure prepared via screen printing.

  12. Colloidal nanocrystal ZnO- and TiO2-modified electrodes sensitized with chlorophyll a and carotenoids: a photoelectrochemical study

    International Nuclear Information System (INIS)

    Petrella, Andrea; Cosma, Pinalysa; Lucia Curri, M.; Rochira, Sergio; Agostiano, Angela

    2011-01-01

    Heterostructures formed of films of organic-capped ZnO and TiO 2 nanocrystals (both with the size of ca. 6 nm) and photosynthetic pigments were prepared and characterized. The surface of optically transparent electrodes (Indium Tin Oxide) was modified with nanocrystals and prepared by colloidal synthetic routes. The nanostructured electrodes were sensitized by a mixture of chlorophyll a and carotenoids. The characterization of the hybrid structures, carried out by means of steady-state optical measurements, demonstrated such class of dyes able to extend the photoresponse of the large band-gap semiconductors. The charge-transfer processes between the components of the heterojunction were investigated, and photoelectrochemical measurements taken on the sensitized ZnO and TiO 2 nanocrystals electrodes elucidated the photoactivity of the heterojunctions as a function of the dyes and of the red–ox mediator used in solution. The effect of methyl viologen as different red–ox mediator was also evaluated in order to show its effect on the heterojunction photoactivity. The overall results contributed to describe the photoelectrochemical potential of the investigated heterojunctions, highlighting a higher response of the dye-sensitized ZnO nanocrystals, and then provided the TiO 2 -modified counterparts.

  13. Electrical properties of resistive switches based on Ba1-χSrχTiO3 thin films prepared by RF co-sputtering

    International Nuclear Information System (INIS)

    Marquez H, A.; Hernandez R, E.; Zapata T, M.; Guillen R, J.; Cruz, M. P.; Calzadilla A, O.; Melendez L, M.

    2010-01-01

    In this work, was proposed the use of Ba 1-χ Sr χ TiO 3 (0≤x≤1) thin films for the construction of metal-insulator-metal heterostructures; and their great potential for the development of non-volatile resistance memories (ReRAM) is shown. The deposition of Ba 1-χ Sr χ TiO 3 thin films was done by the RF co-sputtering technique using two magnetron sputtering cathodes with BaTiO 3 and SrTiO 3 targets. The chemical composition (x parameter) in the deposited Ba 1-χ Sr χ TiO 3 thin films was varied through the RF powder applied to the targets. The constructed metal-insulator-metal heterostructures were Al/Ba 1-χ Sr χ TiO 3 /nichrome. The I-V measurements of the heterostructures showed that their hysteretic characteristics change depending on the Ba/Sr ratio of the Ba 1-χ Sr χ TiO 3 thin films; the Ba/Sr ratio was determined by employing the energy dispersive spectroscopy; Sem micrographs showed that Ba 1-χ Sr χ TiO 3 thin films were uniform without cracks or pinholes. Additionally, the analysis of the X-ray diffraction results indicated the substitutional incorporation of Sr into the BaTiO 3 lattice and the obtainment of crystalline films for the entire range of the x values. (Author)

  14. A Humidity Sensor Based on Nb-doped Nanoporous TiO2 Thin Film

    Directory of Open Access Journals (Sweden)

    Mansoor Anbia

    2011-11-01

    Full Text Available The humidity sensing properties of the sensor fabricated from Nb-doped nanoporous TiO2 by screen-printing on the alumina substrate with Ag-Pd interdigital electrodes have been investigated. The nanoporous thin film has been prepared by sol-gel technique. The product has been characterized by X-ray diffraction and scanning electron microscopy to analyze the structure and its morphology. It is found that the impedance of this sensor changes more than four orders of magnitude in the relative humidity (RH range of 11–95 % at 25 °C. The response and recovery time of the sensor are about 19 and 25 s, respectively, during the RH variation from 11 to 95 %. The sensor shows high humidity sensitivity, rapid response and recovery, prominent stability, good repeatability and narrow hysteresis loop. These results indicate that Nb-doped nanoporous TiO2 thin films have a great potential for humidity sensing applications in room temperature operations.

  15. Analyses of surface coloration on TiO2 film irradiated with excimer laser

    International Nuclear Information System (INIS)

    Zheng, H.Y.; Qian, H.X.; Zhou, W.

    2008-01-01

    TiO 2 film of around 850 nm in thickness was deposited on a soda-lime glass by PVD sputtering and irradiated using one pulse of krypton-fluorine (KrF) excimer laser (wavelength of 248 nm and pulse duration of 25 ns) with varying fluence. The color of the irradiated area became darker with increasing laser fluence. Irradiated surfaces were characterized using optical microscopy, scanning electron microscopy, Raman spectroscopy and atomic force microscopy. Surface undergoes thermal annealing at low laser fluence of 400 and 590 mJ/cm 2 . Microcracks at medium laser fluence of 1000 mJ/cm 2 are attributed to surface melting and solidification. Hydrodynamic ablation is proposed to explain the formation of micropores and networks at higher laser fluence of 1100 and 1200 mJ/cm 2 . The darkening effect is explained in terms of trapping of light in the surface defects formed rather than anatase to rutile phase transformation as reported by others. Controlled darkening of TiO 2 film might be used for adjustable filters

  16. Ferroelectric BaTiO3 thin films on Ti substrate fabricated using pulsed-laser deposition.

    Science.gov (United States)

    He, J; Jiang, J C; Liu, J; Collins, G; Chen, C L; Lin, B; Giurgiutiu, V; Guo, R Y; Bhalla, A; Meletis, E I

    2010-09-01

    We report on the fabrication of ferroelectric BaTiO3 thin films on titanium substrates using pulsed laser deposition and their microstructures and properties. Electron microscopy studies reveal that BaTiO3 films are composed of crystalline assemblage of nanopillars with average cross sections from 100 nm to 200 nm. The BaTiO3 films have good interface structures and strong adhesion with respect to Ti substrates by forming a rutile TiO2 intermediate layer with a gradient microstructure. The room temperature ferroelectric polarization measurements show that the as-deposited BTO films possess nearly the same spontaneous polarization as the bulk BTO ceramics indicating formation of ferroelectric domains in the films. Successful fabrication of such ferroelectric films on Ti has significant importance for the development of new applications such as structural health monitoring spanning from aerospace to civil infrastructure. The work can be extended to integrate other ferroelectric oxide films with various promising properties to monitor the structural health of materials.

  17. Effects of RGD immobilization on light-induced cell sheet detachment from TiO{sub 2} nanodots films

    Energy Technology Data Exchange (ETDEWEB)

    Cheng, Kui; Wang, Tiantian [School of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou 310027 (China); Yu, Mengliu [The Affiliated Stomatologic Hospital, Zhejiang University, Hangzhou 310003 (China); The First Affiliated Hospital of Medical College, Zhejiang University, Hangzhou, 310003 (China); Wan, Hongping [School of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou 310027 (China); Lin, Jun [The First Affiliated Hospital of Medical College, Zhejiang University, Hangzhou, 310003 (China); Weng, Wenjian, E-mail: wengwj@zju.edu.cn [School of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou 310027 (China); The Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai 200050 (China); Wang, Huiming, E-mail: hmwang1960@hotmail.com [The Affiliated Stomatologic Hospital, Zhejiang University, Hangzhou 310003 (China); The First Affiliated Hospital of Medical College, Zhejiang University, Hangzhou, 310003 (China)

    2016-06-01

    Light-induced cell detachment is reported to be a safe and effective cell sheet harvest method. In the present study, the effects of arginine–glycine–aspartic acid (RGD) immobilization on cell growth, cell sheet construction and cell harvest through light illumination are investigated. RGD was first immobilized on TiO{sub 2} nanodots films through simple physical adsorption, and then mouse pre-osteoblastic MC3T3-E1 cells were seeded on the films. It was found that RGD immobilization promoted cell adhesion and proliferation. It was also observed that cells cultured on RGD immobilized films showed relatively high level of pan-cadherin. Cells harvested with ultraviolet illumination (365 nm) showed good viability on both RGD immobilized and unmodified TiO{sub 2} nanodot films. Single cell detachment assay showed that cells detached more quickly on RGD immobilized TiO{sub 2} nanodot films. That could be ascribed to the RGD release after UV365 illumination. The current study demonstrated that RGD immobilization could effectively improve both the cellular responses and light-induced cell harvest. - Highlights: • RGD immobilization on TiO{sub 2} nanodots film favors light-induced cell sheet detachment. • Physically adsorbed RGD detaches from the film through ultraviolet illumination. • RGD detachment promotes cells and cell sheets detachment.

  18. Synthesis and characterization of multilayered BaTiO3/NiFe2O4 thin films

    Directory of Open Access Journals (Sweden)

    Branimir Bajac

    2013-03-01

    Full Text Available Presented research was focused on the fabrication of multiferroic thin film structures, composed of ferrielectric barium titanate perovskite phase and magnetostrictive nickel ferrite spinel phase. The applicability of different, solution based, deposition techniques (film growth from solution, dip coating and spin coating for thefabrication of multilayered BaTiO3 /NiFe2O4 thin films was investigated. It was shown that only spin coating produces films of desired nanostructure, thickness and smooth and crackfree surfaces.

  19. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    OpenAIRE

    Rafieian, Damon; Ogieglo, Wojciech; Savenije, T.J.; Lammertink, Rob G H

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx), obtained by sputtering at relatively low oxygen concentration, formed rutile upon annealing in air, ...

  20. Influence of different TiO2 blocking films on the photovoltaic performance of perovskite solar cells

    Science.gov (United States)

    Zhang, Chenxi; Luo, Yudan; Chen, Xiaohong; Ou-Yang, Wei; Chen, Yiwei; Sun, Zhuo; Huang, Sumei

    2016-12-01

    Organolead trihalide perovskite materials have been successfully used as light absorbers in efficient photovoltaic (PV) cells. Cell structures based on mesoscopic metal oxides and planar heterojunctions have already demonstrated very impressive and brisk advances, holding great potential to grow into a mature PV technology. High power conversion efficiency (PCE) values have been obtained from the mesoscopic configuration in which a few hundred nano-meter thick mesoporous scaffold (e.g. TiO2 or Al2O3) infiltrated by perovskite absorber was sandwiched between the electron and hole transport layers. A uniform and compact hole-blocking layer is necessary for high efficient perovskite-based thin film solar cells. In this study, we investigated the characteristics of TiO2 compact layer using various methods and its effects on the PV performance of perovskite solar cells. TiO2 compact layer was prepared by a sol-gel method based on titanium isopropoxide and HCl, spin-coating of titanium diisopropoxide bis (acetylacetonate), screen-printing of Dyesol's bocking layer titania paste, and a chemical bath deposition (CBD) technique via hydrolysis of TiCl4, respectively. The morphological and micro-structural properties of the formed compact TiO2 layers were characterized by scanning electronic microscopy and X-ray diffraction. The analyses of devices performance characteristics showed that surface morphologies of TiO2 compact films played a critical role in affecting the efficiencies. The nanocrystalline TiO2 film deposited via the CBD route acts as the most efficient hole-blocking layer and achieves the best performance in perovskite solar cells. The CBD-based TiO2 compact and dense layer offers a small series resistance and a large recombination resistance inside the device, and makes it possible to achieve a high power conversion efficiency of 12.80%.

  1. SILAR BiOI-Sensitized TiO2 Films for Visible-Light Photocatalytic Degradation of Rhodamine B and 4-Chlorophenol.

    Science.gov (United States)

    Odling, Gylen; Robertson, Neil

    2017-04-05

    BiOI nanoplates were deposited upon a film of TiO 2 nanoparticles derived from a commercial source using a simple room temperature sequential ionic layer adsorption and reaction (SILAR) method. X-ray diffraction, X-ray photoelectron spectroscopy and electron microscopies have been used to confirm the crystal phase, chemical states of key elements and morphology of the BiOI nanoplate-TiO 2 composites. Using both valence band X-ray photoelectron spectroscopy and UV/Vis diffuse reflectance measurements the band structure of the composites is determined to be that of a type II heterojunction. Through initial screening of the photocatalytic activity of the SILAR-modified films it was determined that five SILAR cycles are optimal in the photocatalytic degradation of rhodamine B. The visible-light sensitisation effect of BiOI was then proven by examination of the photocatalytic degradation of the colourless organic pollutant 4-chlorophenol, showing a large enhancement over an equivalent TiO 2 film. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  2. Preparation of sensitive and recyclable porous Ag/TiO{sub 2} composite films for SERS detection

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Zhengyi; Yu, Jiajie; Yang, Jingying; Lv, Xiang; Wang, Tianhe, E-mail: thwang56@126.com

    2015-12-30

    Graphical abstract: - Highlights: • A new but simple method of fabricating robust TiO{sub 2} films on glass. • AgNPs were deposited on the surface of TiO{sub 2} films with the assistance of UV irradiation. • Substrates with high SERS sensitivity and excellent recyclability. - Abstract: Porous Ag/TiO{sub 2} composite films were prepared by spin coating of titania on normal glass slides and subsequent photochemical deposition of silver nanoparticles (AgNPs). The films were characterized by XRD and FESEM to reveal micro structural and morphological differences between films obtained under varied conditions. The SERS properties of these films were investigated using aqueous crystal violet (CV) as probe molecules. The results indicate that the content of polyethylene glycol (PEG) and photo-reduction time had significant influences on both the microstructure and SERS performance of Ag/TiO{sub 2} films. The highest SERS sensitivity that allowed as low as 10{sup −10} M aqueous CV to be detected, was achieved with the PEG/(C{sub 4}H{sub 9}O){sub 4}Ti molar ratio being 0.08% and with 30 min of UV irradiation. With this film a linear relationship was established through experiment between SERS intensity and CV concentration from 10{sup −10} to 10{sup −5} M, which could be used as a calibration curve for CV concentration measurement. In addition, the film could be reused as a SERS substrate for up to four times without significantly losing SERS sensitivity if a simple regeneration was followed. It is visualized that the Ag/TiO{sub 2} film on glass has potentials for being developed into a practical SERS substrate with high sensitivity and good reusability.

  3. Hollow TiO2 modified reduced graphene oxide microspheres encapsulating hemoglobin for a mediator-free biosensor.

    Science.gov (United States)

    Liu, Hui; Guo, Kai; Duan, Congyue; Dong, Xiaonan; Gao, Jiaojiao

    2017-01-15

    Hollow TiO 2 modified reduced graphene oxide microspheres (hollow TiO 2 -rGO microspheres or H-TiO 2 -rGO MS) have been synthesized and then be used to immobilize hemoglobin (Hb) to fabricate a mediator-free biosensor. The morphology and structure of hollow TiO 2 -rGO microspheres were characterized by scanning electron microscopy, transmission electronic microscopy and X-ray diffraction. Results of spectroscopy and electrochemistry tests revealed that hollow TiO 2 -rGO microsphere is an excellent immobilization matrix with biocompatibility for redox protein, affording good protein bioactivity and stability. The hollow TiO 2 -rGO microspheres with special structure and component enhance the immobilization efficiency of proteins and facilitate the direct electron transfer, which result in the better H 2 O 2 detection performance-the wide linear range of 0.1-360μM for H 2 O 2 (sensitivity of 417.6 μA mM -1 cm -2 ) and the extremely low detection limit of 10nM for H 2 O 2 . Moreover, the hollow microsphere can provide a protective microenvironment for Hb to make the as-prepared biosensor improve long-term stability. The as-prepared biosensor retains 95.4% of the initial response to H 2 O 2 after 60-d storage. Hence, this work suggests that if can be fabricated a mediator-free biosensor, hollow TiO 2 -rGO microspheres will find wide potential applications in environmental analysis and biomedical detection. Copyright © 2016 Elsevier B.V. All rights reserved.

  4. Incorporation of N in TiO{sub 2} films grown by DC-reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Serio, S. [CEFITEC, Departamento de Fisica, Faculdade de Ciencias e Tecnologia da Universidade Nova de Lisboa, 2829-516 Caparica (Portugal); Melo Jorge, M.E. [CCMM, Departamento de Quimica e Bioquimica, Faculdade de Ciencias da Universidade de Lisboa, Campo Grande C8, 1749-016 Lisboa (Portugal); Nunes, Y. [CEFITEC, Departamento de Fisica, Faculdade de Ciencias e Tecnologia da Universidade Nova de Lisboa, 2829-516 Caparica (Portugal); Barradas, N.P. [Instituto Tecnologico e Nuclear and CFNUL, E.N. 10, Sacavem 2686-953 (Portugal); Alves, E., E-mail: ealves@itn.pt [Instituto Tecnologico e Nuclear and CFNUL, E.N. 10, Sacavem 2686-953 (Portugal); Munnik, F. [Helmholtz-Zentrum Dresden-Rossendorf (Germany)

    2012-02-15

    Photocatalytic properties of TiO{sub 2} are expected to play an important role on emerging technologies based on OH radicals to destroy harmful nonbiodegradable organic and inorganic contaminants in water. The drawback is the wide band gap of TiO{sub 2} (3.2 eV) limiting its use to the UV part of electromagnetic spectrum under sunlight. Therefore, modifications of TiO{sub 2} are needed to tune the gap in order to allow an efficient use of the entire solar spectrum. One possibility is N-doping of TiO{sub 2} to make the photocatalytic activity possible under visible light and more suitable for water treatment. In our study nitrogen-doped TiO{sub 2} (TiO{sub 2-x}N{sub x}) films were deposited by DC-reactive magnetron sputtering using a dual-magnetron co-deposition apparatus on unheated glass and silicon substrates using a pure titanium target. The depth profile of nitrogen was measured with heavy ion elastic recoil detection analysis combined with Rutherford backscattering spectrometry (RBS) and correlated with the optical and structural properties obtained by UV-VIS spectroscopy and X-ray diffraction (XRD).

  5. Diamagnetism to ferromagnetism in Sr-substituted epitaxial BaTiO{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Singamaneni, Srinivasa Rao, E-mail: ssingam@ncsu.edu; Prater, John T. [Materials Science Division, Army Research Office, Research Triangle Park, North Carolina 27709 (United States); Department of Materials Science and Engineering, North Carolina State University, Raleigh, North Carolina 27695 (United States); Punugupati, Sandhyarani; Narayan, Jagdish [Department of Materials Science and Engineering, North Carolina State University, Raleigh, North Carolina 27695 (United States)

    2016-04-04

    We report on the ferromagnetic-like behavior in otherwise diamagnetic BaTiO{sub 3} (BTO) thin films upon doping with non-magnetic element Sr having the composition Ba{sub 0.4}Sr{sub 0.6}TiO{sub 3} (BST). The epitaxial integration of BST (∼800 nm) thick films on Si (100) substrate was achieved using MgO (40 nm) and TiN (20 nm) as buffer layers to prepare BST/MgO/TiN/Si (100) heterostructure by pulsed laser deposition. The c-axis oriented and cube-on-cube epitaxial BST is formed on Si (100) as evidenced by the in-plane and out-of-plane X-ray diffraction. All the deposited films are relaxed through domain matching epitaxy paradigm as observed from X-ray diffraction pattern and A{sub 1}TO{sub 3} mode (at 521.27 cm{sup −1}) of Raman spectra. As-deposited BST thin films reveal ferromagnetic-like properties, which persist up to 400 K. The magnetization decreases two-fold upon oxygen annealing. In contrast, as-deposited un-doped BTO films show diamagnetism. Electron spin resonance measurements reveal no evidence of external magnetic impurities. XRD and X-ray photoelectron spectroscopy spectra show significant changes influenced by Sr doping in BTO. The ferromagnetic-like behavior in BST could be due to the trapped electron donors from oxygen vacancies resulting from Sr-doping.

  6. Structural, Electrical and Optical Properties of TiO2 Thin Film Deposited on the Nano Porous Silicon Template

    Science.gov (United States)

    Bahar, Mahmood; Dermani, Ensieh Khalili

    The porous silicon (PSi), which is produced by the electrochemical etching, has been used as a substrate for the growth of the titanium oxide (TiO2) thin films. By using the EBPVD method, TiO2 thin films have been deposited on the surface of the PSi substrate. TiO2/PSi layers were annealed at the temperature of 400∘C, 500∘C and 600∘C for different tests. The morphology and structures of layers were investigated by the scanning electron microscopy (SEM) and X-ray diffraction (XRD). The current-voltage characteristic curves of samples and the ideality factor of heterojunction were studied. The results showed that the electrical properties of the samples change with increase in the annealing temperature. The optical properties of the prepared samples were investigated by using UV-Vis and photoluminescence (PL) spectroscopy. Green light emission of the PSi combined with the blue light and violet-blue emission obtained from the TiO2/PSi PL spectra. The results showed that the optical band gap energy of the PSi has increased from 1.86eV to 2.93eV due to the deposition of TiO2 thin film.

  7. TiO2 nanoparticle thin film deposition by matrix assisted pulsed laser evaporation for sensing applications

    International Nuclear Information System (INIS)

    Caricato, A.P.; Capone, S.; Ciccarella, G.; Martino, M.; Rella, R.; Romano, F.; Spadavecchia, J.; Taurino, A.; Tunno, T.; Valerini, D.

    2007-01-01

    The MAPLE technique has been used for the deposition of nanostructured titania (TiO 2 ) nanoparticles thin films to be used for gas sensors applications. An aqueous solution of TiO 2 nanoparticles, synthesised by a novel chemical route, was frozen at liquid nitrogen temperature and irradiated with a pulsed ArF excimer laser in a vacuum chamber. A uniform distribution of TiO 2 nanoparticles with an average size of about 10 nm was deposited on Si and interdigitated Al 2 O 3 substrates as demonstrated by high resolution scanning electron microscopy-field emission gun inspection (SEM-FEG). Energy dispersive X-ray (EDX) analysis revealed the presence of only the titanium and oxygen signals and FTIR (Fourier transform infra-red) revealed the TiO 2 characteristic composition and bond. A comparison with a spin coated thin film obtained from the same solution of TiO 2 nanoparticles is reported. The sensing properties of the films deposited on interdigitated substrates were investigated, too

  8. Study on fabrication of TiO{sub 2} thin films by spin – coating and their optical properties

    Energy Technology Data Exchange (ETDEWEB)

    Zharvan, Vicran, E-mail: vicran.zharvan@gmail.com; Daniyati, Risqa; Nur Ichzan, A.S.; Yudoyono, Gatut; Darminto, E-mail: darminto@physics.its.ac.id [Department of Physics, Institut Teknologi Sepuluh Nopember (ITS), Kampus ITS Sukolilo, Surabaya 60111 (Indonesia)

    2016-03-11

    Study on fabrication of TiO{sub 2} thin films and their optical properties in UV-VIS spectrum has been conducted. TiO{sub 2} nanopowders were prepared by co-precipitation method with varying mixing duration for 5, 10 and 25 hours using TiCl{sub 3} as precursor. The as-synthesized TiO{sub 2} phase is anatase having crystalline size of 14.25 nm, 13.75 nm and 12.62, respectively for the corresponding mixing duration. Thin films of TiO{sub 2} were fabricated by spin coating method and then checked by XRD diffractometer and UV-Vis Spectrophotometer to examine their structure and band gap energy. The prepared films also contain anatase phase of TiO{sub 2} with respective band gap of 3.70 eV, 3.74 eV and 3.76 eV, depending on the powders and their treatment.

  9. Photocatalytic activity of bipolar pulsed magnetron sputter deposited TiO{sub 2}/TiWO{sub x} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Weng, Ko-Wei; Hu, Chung-Hsuan; Hua, Li-Yu; Lee, Chin-Tan [Department of Electronic Engineering, National Quemoy University, 1 Daxue Road, Jinning Township, Kinmen 89250, Taiwan, ROC (China); Zhao, Yu-Xiang [Department of Computer Science and Information Engineering, National Quemoy University, Taiwan, ROC (China); Chang, Julian; Yang, Shu-Yi [Department of Applied English, National Quemoy University, Taiwan, ROC (China); Han, Sheng, E-mail: shenghan@nutc.edu.tw [Center for General Education, National Taichung University of Science and Technology, 129 San-min Road, Section 3, Taichung 40401, Taiwan, ROC (China)

    2016-08-15

    Highlights: • TiO{sub 2}/TiWO{sub x} films were fabricated by a bipolar pulsed magnetron sputtering apparatus. • Titanium oxide being sputtered tungsten enhanced the highly oriented of TiO{sub 2} (1 0 1) plane of the specimen assemblies. • The mechanism WO{sub 3}(h{sup +}, e{sup −})/TiO{sub 2}(h{sup +}, e{sup −}) → WO{sub 3}(e{sup −})/TiO{sub 2}(h{sup +}) shows the higher hydrophilicity and lower contact angle. - Abstract: Titanium oxide films were formed by sputtering and then TiWO{sub x} films were deposited by bipolar pulsed magnetron sputtering with pure titanium and tungsten metal targets. The sputtering of titanium oxide with tungsten enhanced the orientation of the TiO{sub 2} (1 0 1) plane of the specimen assemblies. The main varying parameter was the tungsten pulse power. Titanium oxide sputtered with tungsten using a pulsing power of 50 W exhibited a superior hydrophilic property, and a contact angle of 13.1°. This fabrication conditions maximized the photocatalytic decomposition of methylene blue solution. The mechanism by which the titanium oxide was sputtered with tungsten involves the photogeneration of holes and electron traps, inhibiting the hole–electron recombination, enhancing hydrophilicity and reducing the contact angle.

  10. The effect of bulk/surface defects ratio change on the photocatalysis of TiO2 nanosheet film

    Science.gov (United States)

    Wang, Fangfang; Ge, Wenna; Shen, Tong; Ye, Bangjiao; Fu, Zhengping; Lu, Yalin

    2017-07-01

    The photocatalysis behavior of TiO2 nanosheet array films was studied, in which the ratio of bulk/surface defects were adjusted by annealing at different temperature. Combining positron annihilation spectroscopy, EPR and XPS, we concluded that the bulk defects belonged to Ti3+ related vacancy defects. The results show that the separation efficiency of photogenerated electrons and holes could be significantly improved by optimizing the bulk/surface defects ratio of TiO2 nanosheet films, and in turn enhancing the photocatalysis behaviors.

  11. Transparent TiO2 nanowire networks via wet corrosion of Ti thin films for dye-sensitized solar cells

    Science.gov (United States)

    Shin, Eunhye; Jin, Saera; Hong, Jongin

    2017-09-01

    Transparent TiO2 nanowire networks were prepared by corrosion of Ti thin films on F-doped SnO2 glass substrates in an alkaline (potassium hydroxide: KOH) solution. The formation of the porous TiO2 nanostructures from the Ti thin films was thoroughly investigated. Dye-sensitized solar cells with a photoanode of 1.2-μm-thick nanowire networks exhibit an average optical transmittance of 40% in the visible light region and a power conversion efficiency of 1.0% under one sun illumination.

  12. Annealing dependence of residual stress and optical properties of TiO2 thin film deposited by different deposition methods.

    Science.gov (United States)

    Chen, Hsi-Chao; Lee, Kuan-Shiang; Lee, Cheng-Chung

    2008-05-01

    Titanium oxide (TiO(2)) thin films were prepared by different deposition methods. The methods were E-gun evaporation with ion-assisted deposition (IAD), radio-frequency (RF) ion-beam sputtering, and direct current (DC) magnetron sputtering. Residual stress was released after annealing the films deposited by RF ion-beam or DC magnetron sputtering but not evaporation, and the extinction coefficient varied significantly. The surface roughness of the evaporated films exceeded that of both sputtered films. At the annealing temperature of 300 degrees C, anatase crystallization occurred in evaporated film but not in the RF ion-beam or DC magnetron-sputtered films. TiO(2) films deposited by sputtering were generally more stable during annealing than those deposited by evaporation.

  13. Study on epoxy/BaTiO3 composite embedded capacitor films (ECFs) for organic substrate applications

    International Nuclear Information System (INIS)

    Cho, Sung-Dong; Lee, Joo-Yeon; Hyun, Jin-Gul; Paik, Kyung-Wook

    2004-01-01

    Embedded capacitor films (ECFs) were newly designed for high dielectric constant and low capacitance tolerance (less than ±5%) embedded capacitor fabrication for organic substrates. ECFs are transferable and B-stage films which can be coated on a releasing film. In terms of materials formulation, ECFs are composed of high dielectric constant BaTiO 3 (BT) powder, specially formulated epoxy resin, and latent curing agent. And in terms of coating process, a roll coating method is used for obtaining film thickness uniformity in a large area. Differential scanning calorimeter (DSC) thermal analysis was conducted to determine the optimum amount of curing agent, curing temperature, and curing time. Changes in the dielectric constant of epoxy/BaTiO 3 composite ECFs with BT particle sizes and contents were investigated. Dielectric constant of 90 was obtained using two different size BaTiO 3 powders mixture. Typically, capacitors of 12 μm thick film with 8 nF/cm 2 with less than ±5% capacitance tolerance and low leakage current (less than 10 -7 A/cm 2 at 10 V) were successfully demonstrated on PCBs using epoxy/BaTiO 3 composite embedded capacitor films

  14. Photocatalytic properties of P25-doped TiO2 composite film synthesized via sol-gel method on cement substrate.

    Science.gov (United States)

    Guo, Xiang; Rao, Lei; Wang, Peifang; Wang, Chao; Ao, Yanhui; Jiang, Tao; Wang, Wanzhong

    2018-04-01

    TiO 2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface water, we herein examined the preparation of a P25-TiO 2 composite film on a cement substrate via a sol-gel method. In this case, Rhodamine B (RhB) was employed as the target organic pollutant. The self-generated TiO 2 film and the P25-TiO 2 composite film were characterized by X-ray diffraction (XRD), N 2 adsorption/desorption measurements, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and diffuse reflectance spectroscopy (DRS). The photodegradation efficiencies of the two films were studied by RhB removal in water under UV (ultraviolet) irradiation. Over 4day exposure, the P25-TiO 2 composite film exhibited higher photocatalytic performance than the self-generated TiO 2 film. The photodegradation rate indicated that the efficiency of the P25-TiO 2 composite film was enhanced by the addition of the rutile phase Degussa P25 powder. As such, cooperation between the anatase TiO 2 and rutile P25 nanoparticles was beneficial for separation of the photo-induced electrons and holes. In addition, the influence of P25 doping on the P25-TiO 2 composite films was evaluated. We found that up to a certain saturation point, increased doping enhanced the photodegradation ability of the composite film. Thus, we herein demonstrated that the doping of P25 powders is a simple but effective strategy to prepare a P25-TiO 2 composite film on a cement substrate, and the resulting film exhibits excellent removal efficiency in the degradation of organic pollutants. Copyright © 2017. Published by Elsevier B.V.

  15. Production of TiO2 films with bactericidal properties deposited on paper substrate

    Energy Technology Data Exchange (ETDEWEB)

    Lisboa, A.J.T.; Vasconcelos, J.S.; Vasconcelos, A.C.S.; Vasconcelos, N.S.L.S.; Rangel, J.H.G.; Oliveira, M.M.O. [Universidade Federal do Maranha (UFMA), MA (Brazil); Longo, E.; Varela, J. A. [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), SP (Brazil)

    2014-07-01

    The main objective of this work was to obtain anatase-phase titanium oxide films deposited on paper substrates, using the polymeric precursor (Pechini) method. The oxide was mixed with a polyvinyl alcohol (PVA) solution and deposited on a paper substrate. The samples were then characterized by X-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM), and energy dispersive spectroscopy (EDS), to check their surface phase. Bactericidal assays using Staphylococcus aureus and Escherichia coli bacteria for the anatase TiO2 film deposited on paper substrate indicated that the method was efficient, since the bacteria were eliminated after a given exposure time. However, the method proved to be more efficient when exposing samples contaminated with E. coli to UV irradiation for 30 and 45 min and then to sunlight for 90 min, since this resulted in the elimination of all the bacteria. (author)

  16. Production of TiO2 films with bactericidal properties deposited on paper substrate

    International Nuclear Information System (INIS)

    Lisboa, A.J.T.; Vasconcelos, J.S.; Vasconcelos, A.C.S.; Vasconcelos, N.S.L.S.; Rangel, J.H.G.; Oliveira, M.M.O.; Longo, E.; Varela, J. A.

    2014-01-01

    The main objective of this work was to obtain anatase-phase titanium oxide films deposited on paper substrates, using the polymeric precursor (Pechini) method. The oxide was mixed with a polyvinyl alcohol (PVA) solution and deposited on a paper substrate. The samples were then characterized by X-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM), and energy dispersive spectroscopy (EDS), to check their surface phase. Bactericidal assays using Staphylococcus aureus and Escherichia coli bacteria for the anatase TiO2 film deposited on paper substrate indicated that the method was efficient, since the bacteria were eliminated after a given exposure time. However, the method proved to be more efficient when exposing samples contaminated with E. coli to UV irradiation for 30 and 45 min and then to sunlight for 90 min, since this resulted in the elimination of all the bacteria. (author)

  17. Epitaxial Pb(Zr,Ti)O3 thin films for a MEMS application

    International Nuclear Information System (INIS)

    Nguyen, Minh D; Vu, Hung N; Blank, Dave H A; Rijnders, Guus

    2011-01-01

    This research presents the deposition and device fabrication of epitaxial Pb(Zr,Ti)O 3 (PZT) thin films for applications in microelectromechanical systems (MEMS). A piezoelectric micro-membrane is described as an example. Using the pulsed laser deposition (PLD) technique and the MEMS microfabrication process, the piezo-membranes with diameters ranging from 200 to 500 μm were obtained. The displacement of piezo-membranes increased from 5.1 to 17.5 nm V −1 with a piezoelectric-membrane diameter in the range of 200–500 μm. Furthermore, the effect of PZT film-thickness on the mechanical properties has been investigated. By using the conductive-oxide SrRuO 3 (SRO) layers as the electrodes, the degradation of both ferroelectric and piezoelectric properties is prevented up to 10 10 switching cycles

  18. Effects of modified TiO{sub 2} photoanode on the photoelectrochemical properties of dye sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Shengli, E-mail: luvictory@hotmail.com [School of Biological and Chemical Engineering, Zhejiang University of Science and Technology, Hangzhou 310023 (China); Sun, Sam-Shajing [Ph.D. Program in Materials Science and Engineering and Center for Materials Research, Norfolk State University, Norfolk, VA 23504 (United States); Geng, Rui [School of Biological and Chemical Engineering, Zhejiang University of Science and Technology, Hangzhou 310023 (China); College of Chemical Engineering and Materials Science, Zhejiang University of Technology, Hangzhou 310000 (China); Gao, Jianrong [College of Chemical Engineering and Materials Science, Zhejiang University of Technology, Hangzhou 310000 (China)

    2015-08-31

    The study of nanoporous TiO{sub 2} electrodes modified by magnesium and manganese acetates in dye sensitized solar cells was reported. The formation and composition of modified electrodes were characterized by X-ray photoelectron spectroscopy and X-ray diffraction, revealing that MgO and Mn(OH)O were formed after magnesium acetate and manganese acetate treatments. Sunlight absorbance was also enhanced after such modification as supported by UV–vis spectra. The effects of modification include the increase of the dye adsorption, open-circuit voltage, short-circuit current density, and photoelectric conversion efficiency of the fabricated devices. The mechanisms of electron transfer, charge recombination, and electron lifetime were investigated by dark current and electrochemical impedance spectroscopy. - Highlights: • A simple dip coating process was used to modify the TiO{sub 2} electrode surface. • The loaded dye was increased and the lifetime of electrons in TiO{sub 2} was extended. • DSSC efficiency of 5.3% based on magnesium acetate modified TiO{sub 2} was obtained.

  19. Effects of filtered cathodic vacuum arc deposition (FCVAD) conditions on photovoltaic TiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Aramwit, C. [Plasma and Beam Physics Research Facility, Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Intarasiri, S. [Science and Technology Research Institute, Chiang Mai University, Chiang Mai 50200 (Thailand); Thailand Center of Excellence in Physics, Commission on Higher Education, 328 Si Ayutthaya Road, Bangkok 10400 (Thailand); Bootkul, D. [Thailand Center of Excellence in Physics, Commission on Higher Education, 328 Si Ayutthaya Road, Bangkok 10400 (Thailand); Department of General Science, Faculty of Science, Srinakharinwirot University, Bangkok 10110 (Thailand); Tippawan, U. [Plasma and Beam Physics Research Facility, Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Thailand Center of Excellence in Physics, Commission on Higher Education, 328 Si Ayutthaya Road, Bangkok 10400 (Thailand); Supsermpol, B.; Seanphinit, N. [Department of General Science, Faculty of Science, Srinakharinwirot University, Bangkok 10110 (Thailand); Western Digital Thailand Co. Ltd., Ayutthaya 13160 (Thailand); Ruangkul, W. [Thailand Center of Excellence in Physics, Commission on Higher Education, 328 Si Ayutthaya Road, Bangkok 10400 (Thailand); Yu, L.D., E-mail: yuld@thep-center.org [Plasma and Beam Physics Research Facility, Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Thailand Center of Excellence in Physics, Commission on Higher Education, 328 Si Ayutthaya Road, Bangkok 10400 (Thailand)

    2014-08-15

    Highlights: • Titanium dioxide films were synthesized using the FCVAD technique. • Various FCVAD conditions were tested. • The TiO{sub 2} films were characterized. • The FCVAD condition effects on the film characteristics were studied. • The O{sub 2} pressure had the most important effect on the film quality. - Abstract: Titanium dioxide (TiO{sub 2}) films for photovoltaic applications were synthesized using filtered cathodic vacuum arc deposition (FCVAD) technique. Various deposition conditions were tested for an optimal film formation. The conditions included the oxygen (O{sub 2}) pressure which was varied from a base pressure 10{sup −5} to 10{sup −4}, 10{sup −3}, 10{sup −2} and 10{sup −1} Torr, sample holder bias varied using 0 or −250 V, deposition time varied from 10, 20 to 30 min, and deposition distance varied from 1 to 3 cm. The deposited films were also annealed and compared with unannealed ones. The films under various conditions were characterized using optical microscopy, scanning electron microscopy (SEM), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS) and Raman spectroscopy techniques. The film transparency increased and thickness decreased to a nanoscale with increasing of the O{sub 2} pressure. The transparent deposited films contained stoichiometric titanium and oxygen under the medium O{sub 2} pressure. The as-deposited films were TiO{sub 2} containing some rutile but no anatase which needed annealing to form.

  20. TiO2 film/Cu2O microgrid heterojunction with photocatalytic activity under solar light irradiation.

    Science.gov (United States)

    Zhang, Junying; Zhu, Hailing; Zheng, Shukai; Pan, Feng; Wang, Tianmin

    2009-10-01

    Coupling a narrow-band-gap semiconductor with TiO(2) is an effective method to produce photocatalysts that work under UV-vis light irradiation. Usually photocatalytic coupled-semiconductors exist mainly as powders, and photocatalytic activity is only favored when a small loading amount of narrow-band-gap semiconductor is used. Here we propose a heavy-loading photocatalyst configuration in which 51% of the surface of the TiO(2) film is covered by a Cu(2)O microgrid. The coupled system shows higher photocatalytic activity under solar light irradiation than TiO(2) and Cu(2)O films. This improved performance is due to the efficient charge transfer between the two phases and the similar opportunity each has to be exposed to irradiation and adsorbates.

  1. Investigations on the synthesis, optical and electrical properties of TiO{sub 2} thin films by Chemical Bath Deposition (CBD) method

    Energy Technology Data Exchange (ETDEWEB)

    Govindasamy, Geetha [Bharathiar University, Coimbatore (India); Murugasen, Priya [Department of Physics, Saveetha Engineering College (India); Sagadevan, Suresh [Department of Physics, AMET University, Chennai (India)

    2016-03-15

    Titanium dioxide (TiO{sub 2} ) thin films were prepared by Chemical Bath Deposition (CBD) method. The X-ray diffraction (XRD) analysis was used to examine the structure and to determine the crystallite size of TiO{sub 2} thin film. The surface morphology of the film was studied using Scanning Electron Microscopy (SEM).The optical properties were studied using the UV-Visible and photoluminescence (PL) spectrum. Optical constants such as band gap, refractive index, extinction coefficient and electric susceptibility were determined. The FTIR spectrum revealed the strong presence of TiO{sub 2} . The dielectric properties of TiO{sub 2} thin films were studied for different frequencies and different temperatures. The AC electrical conductivity test revealed that the conduction depended both on the frequency and the temperature. Photoconductivity study was carried out in order to ascertain the positive photoconductivity of the TiO{sub 2} thin films. (author)

  2. Effect of iron doping on structural and optical properties of TiO2 thin film by sol–gel routed spin coating technique

    Directory of Open Access Journals (Sweden)

    Stephen Lourduraj

    2017-08-01

    Full Text Available Thin films of iron (Fe-doped titanium dioxide (Fe:TiO2 were prepared by sol–gel spin coating technique and further calcined at 450∘C. The structural and optical properties of Fe-doped TiO2 thin films were investigated by X-ray diffraction (XRD, scanning electron microscopy (SEM, ultraviolet–visible spectroscopy (UV–vis and atomic force microscopic (AFM techniques. The XRD results confirm the nanostructured TiO2 thin films having crystalline nature with anatase phase. The characterization results show that the calcined thin films having high crystallinity and the effect of iron substitution lead to decreased crystallinity. The SEM investigations of Fe-doped TiO2 films also gave evidence that the films were continuous spherical shaped particles with a nanometric range of grain size and film was porous in nature. AFM analysis establishes that the uniformity of the TiO2 thin film with average roughness values. The optical measurements show that the films having high transparency in the visible region and the optical band gap energy of Fe-doped TiO2 film with iron (Fe decrease with increase in iron content. These important requirements for the Fe:TiO2 films are to be used as window layers in solar cells.

  3. Preparation of β-Li{sub 2}TiO{sub 3} pebbles by a modified indirect wet chemistry method

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Cheng-Long, E-mail: johnyucl@aliyun.com [School of Materials Science and Engineering, Shaanxi University of Science & Technology, Xi’an 710021 (China); Research Laboratory of Hydrothermal Chemistry, Faculty of Science, The Kochi University, Kochi 780-8520 (Japan); Wang, Fei; Zhang, Ai-Lin; Gao, Dan-Peng; Cao, Shu-Yao [School of Materials Science and Engineering, Shaanxi University of Science & Technology, Xi’an 710021 (China); Guo, Ying-Yan [College of Resources and Environment, Shaanxi University of Science & Technology, Xi’an 710021 (China); Hui, Huai-Bin [School of Materials Science and Engineering, Shaanxi University of Science & Technology, Xi’an 710021 (China); Technology Research Institute, Technical Center at Dongfeng Commercial Vehicle Company Limited, Wuhan 430056 (China); Hao, Xin [School of Management, Shaanxi University of Science & Technology, Xi’an 710021 (China); Wang, Dao-Yi [School of Materials Science and Engineering, Shaanxi University of Science & Technology, Xi’an 710021 (China); Yanagisawa, Kazumichi [Research Laboratory of Hydrothermal Chemistry, Faculty of Science, The Kochi University, Kochi 780-8520 (Japan)

    2015-12-15

    Graphical abstract: β-Li{sub 2}TiO{sub 3} pebbles with about 1.56 mm in diameter, a better sphericity of 1.02 and relative sintered density of 95.8%T.D. are successfully fabricated when sintered at 1100 °C for 6 h in ambient conditions. - Highlights: • β-Li{sub 2}TiO{sub 3} powders via hydrothermal method are used as raw materials. • A mixture of the acetone and carbon tetrachloride bath is used. • The wet gel pebbles can be fabricated at room temperature. - Abstract: β-Li{sub 2}TiO{sub 3} pebbles were fabricated by a modified indirect wet chemistry method. The first feature lies in that β-Li{sub 2}TiO{sub 3} powders via hydrothermal method were used as raw materials. The second one lies in that a mixture of the acetone and carbon tetrachloride was used for formation and aging of the pebbles at room temperature. The phase identification of the β-Li{sub 2}TiO{sub 3} sintered pebbles was conducted by the X-ray Diffraction analysis. The morphology of the sintered β-Li{sub 2}TiO{sub 3} pebbles was observed by Field Emission Scanning Electron Microscope. The experimental results show that the β-Li{sub 2}TiO{sub 3} pebbles with about 1.56 mm in diameter, a better sphericity of 1.02 and relative sintered density of 95.8%T.D. are successfully fabricated when sintered at 1100 °C for 6 h in ambient conditions. The grains in the pebbles are polyhedral brick-shaped, and homogeneous in size distribution. The morphology evolution and relative density of the β-Li{sub 2}TiO{sub 3} pebbles are governed by the sintering temperature, between 1050 °C and 1150 °C. More homogeneous in grain size, less porosity, and higher densification of the β-Li{sub 2}TiO{sub 3} pebbles can be obtained at 1100 °C.

  4. Preparation of silver-modified TiO2 via microwave-assisted method and its photocatalytic activity for toluene degradation

    International Nuclear Information System (INIS)

    Li Xiaobin; Wang Linling; Lu Xiaohua

    2010-01-01

    Silver-modified TiO 2 (Ag-TiO 2 ) with various Ag/Ti molar ratios were prepared by the microwave-assisted method and characterized by X-ray diffraction (XRD), transmission electron microscope (TEM) and UV-vis diffuse reflectance spectroscopy (UV-vis-DRS). Compared with the hydrothermal method, Ag-TiO 2 of small crystallite size and high crystallinity can be obtained by the microwave-assisted preparation method. When the Ag/Ti molar ratio increased from 0 to 2%, the doping of Ag promoted the phase transformation and inhibited the growth of anatase crystallite. The absorption edge of Ag-TiO 2 shifted to longer wavelength, and the band gap energy of Ag-TiO 2 decreased. However, after increasing the molar ratio Ag/Ti further from 2 to 4%, the anatase content, the crystallite size and the band gap energy of Ag-TiO 2 only increased slightly. In photodegradation gaseous toluene, the photocatalytic activity of Ag-TiO 2 increased with the increase of Ag/Ti molar ratio from 0 to 1%, but declined with the further increase to 2%. The optimal Ag/Ti molar ratio for photocatalytic activity of Ag-TiO 2 was found as 1%, with the content of anatase, rutile and brookite of 71.1, 14.5 and 14.4%, respectively. Compared with TiO 2 , Ag-TiO 2 exhibited a better photostability in toluene degradation.

  5. CdSxSe1−x alloyed quantum dots-sensitized solar cells based on different architectures of anodic oxidation TiO2 film

    International Nuclear Information System (INIS)

    Li, Zhen; Yu, Libo; Liu, Yingbo; Sun, Shuqing

    2014-01-01

    Nanostructured TiO 2 translucent films with different architectures including TiO 2 nanotube (NT), TiO 2 nanowire (NW), and TiO 2 nanowire/nanotube (NW/NT) have been produced by second electrochemical oxidization of TiO 2 NT with diameter around 90–110 nm via modulation of applied voltage. These TiO 2 architectures are sensitized with CdS x Se 1−x alloyed quantum dots (QDs) in sizes of around 3–5 nm aiming to tune the response of the photoelectrochemical properties in the visible region. One-step hydrothermal method facilitates the deposition of CdS x Se 1−x QDs onto TiO 2 films. These CdS x Se 1−x QDs exhibit a tunable range of light absorption with changing the feed molar ratio of S:Se in precursor solution, and inject electrons into TiO 2 films upon excitation with visible light, enabling their application as photosensitizers in sensitized solar cells. Power conversion efficiency (PCE) of 2.00, 1.72, and 1.06 % are achieved with CdS x Se 1−x (obtained with S:Se = 0:4) alloyed QDs sensitized solar cells based on TiO 2 NW/NT, TiO 2 NW, and TiO 2 NT architectures, respectively. The significant enhancement of power conversion efficiency obtained with the CdS x Se 1−x /TiO 2 NW/NT solar cell can be attributed to the extended absorption of light region tuned by CdS x Se 1−x alloyed QDs and enlarged deposition of QDs and efficient electrons transport provided by TiO 2 NW/NT architecture

  6. Multi-modal TiO2-LaFeO3 composite films with high photocatalytic activity and hydrophilicity

    International Nuclear Information System (INIS)

    Gao Kun; Li Shudan

    2012-01-01

    In this paper, a series of multi-modal TiO 2 -LaFeO 3 composite films have been successfully synthesized through a two-step method. The resultant films were characterized in detail by several testing techniques, such as X-ray diffraction (XRD), ultraviolet-visible diffuse reflection spectrum (UV-vis DRS), photoluminescence spectrum (PL), surface photovoltage spectroscopy (SPS) and water contact angle measurements. The photocatalytic activity of different films was evaluated for degrading Methylene Blue (MB) aqueous solution. Hydrophilicity of the obtained TiO 2 -LaFeO 3 composite films was also investigated. The results show that TL film and LT film exhibited superior photocatalytic activity and hydrophilicity.

  7. Preparation and characterization of novel nanocomposite films formed from silk fibroin and nano-TiO2.

    Science.gov (United States)

    Feng, Xin-Xing; Zhang, Li-Li; Chen, Jian-Yong; Guo, Yu-Hai; Zhang, Hua-Peng; Jia, Chang-Ian

    2007-01-30

    This paper describes the synthesis and characterization of new regenerated silk fibroin (SF)/nano-TiO(2) composite films. The preparation method, based on the sol-gel technique using butyl titanate as oxide precursor, could avoid reagglomeration of the prepared nanoparticles. Samples were characterized mainly by X-ray diffraction (XRD), ultra-violet (UV) spectroscopy, atomic force microscopy (AFM), Fourier transform infrared (FT-IR) spectroscopy, and thermogravimetric analysis (TGA). The UV and AFM results indicated that TiO(2) nanoparticles could be well dispersed inside the SF film, and the size of TiO(2) was about 80nm. The XRD and FT-IR analysis implied that the formation of nano-TiO(2) particles may induce the conformational transition of silk fibroin to a typical Silk II structure partly with the increasing of crystallinity in the composite films. Compared to the pure SF films, the mechanical and thermal properties of composite films were improved, and the solubility in water was decreased due to the conformational transition of silk fibroin to Silk II structure.

  8. Double layer films based on TiO{sub 2} and NiO{sub x} for gas detection

    Energy Technology Data Exchange (ETDEWEB)

    Kosc, I., E-mail: ivan.kosc@stuba.sk [Institute of Electronics and Photonics, Slovak University of Technology, Bratislava (Slovakia); Hotovy, I. [Institute of Electronics and Photonics, Slovak University of Technology, Bratislava (Slovakia); Roch, T.; Plecenik, T.; Gregor, M. [Faculty of Mathematics, Physics and Informatics, Comenius University, Bratislava (Slovakia); Predanocy, M. [Institute of Electronics and Photonics, Slovak University of Technology, Bratislava (Slovakia); Cehlarova, M.; Kus, P.; Plecenik, A. [Faculty of Mathematics, Physics and Informatics, Comenius University, Bratislava (Slovakia)

    2014-09-01

    Highlights: • Double layer films based on TiO{sub 2} and NiO{sub x} for gas detection were studied. • Structural, compositional and morphological properties were investigated. • XPS spectra of TiO{sub 2} and NiO{sub x} were identified. • P- and n-type of response to hydrogen were presented. • Inversion of conductivity response type was confirmed. - Abstract: Double layer films based on TiO{sub 2} and NiO{sub x} for gas detection were studied. Two layouts with opposite position of functional films were deposited via DC magnetron sputtering method and annealed at 600 °C. The compositional, structural, morphological, electrical and gas sensing parameters were investigated. The depth profiles and the chemical state of the thin films elements were explored by X-ray photoelectron spectroscopy (XPS). Differences between the surface and subsurface NiO{sub x} were confirmed. In this way the formation of surface oxides and subsurface metallic Ni were observed. The structural changes and polycrystalline character were noticed by X-ray diffraction (XRD). The atomic force microscopy (AFM) revealed nanocrystalline character of the examined surfaces (both layouts). Different position of TiO{sub 2} and NiO{sub x} functional films brought difference in the type of response to reducing gas. Moreover, inversion of response type due to different H{sub 2} concentrations was confirmed.

  9. Preparation and optical properties of gold-dispersed BaTiO3 thin films

    Energy Technology Data Exchange (ETDEWEB)

    Kineri, T; Mori, M [TDK Corp., Tokyo (Japan). R and D Center; Kadono, K; Sakaguchi, T; Miya, M; Wakabayashi, H [Osaka National Research Inst., Osaka (Japan); Tsuchiya, T [Science Univ. of Tokyo, Tokyo (Japan). Faculty of Industrial Science and Technology

    1993-12-01

    Recently, metal or semiconductor-doped glasses were widely studied because of their large resonant third-order nonlinearity. These glasses are utilized in an optical information field as all optical logic devices in the future. The gold-doped glass films or thin layers have a large third-order nonlinear susceptibility [chi] and are prepared by r.f. sputtering method, etc. The optical properties, particularly the refractive index or dielectric constant of the matrix, are very important for the optical nonlinearity of these materials. In this study, gold-dispersed BaTiO3 thin films and gold-dispersed SiO2 thin films are prepared using r.f. magnetron sputtering method, and the optical properties of the films are compared. The [chi] of the films are measured and the effect of the matrix of the films on [chi] is investigated. The headings in the paper are: Introduction, Experimental procedure, Results, Discussion, and Conclusion. 13 refs., 9 figs.

  10. Electrochemical and spectroelectrochemical characterization of different mesoporous TiO2 film electrodes for the immobilization of Cytochrome c

    Science.gov (United States)

    Katsiaounis, Stavros; Tiflidis, Christina; Tsekoura, Christina; Topoglidis, Emmanuel

    2018-03-01

    In this work three different mesoporous TiO2 film electrodes were prepared and used for the immobilization of Cytochrome c (Cyt-c). Films prepared via a standard sol-gel route (SG-films) were compared with commercially available benchmark nanotitania materials, namely P25 Degussa (P25-films) and Dyesol nanopaste (Dyesol films). Their properties, film deposition characteristics and their abilities to adsorb protein molecules in a stable and functional way were examined. We investigated whether it is possible, rather than preparing TiO2 films using multistep, lengthy and not always reproducible sol-gel procedures, to use commercially available nanotitania materials and produce reproducible films faster that exhibit all the properties that make TiO2 films ideal for protein immobilization. Although these materials are formulated primarily for dye-sensitized solar cell applications, in this study we found out that protein immobilization is facile and remarkably stable on all of them. We also investigated their electrochemical properties by using cyclic voltammetry and spectroelectrochemistry and found out that not only direct reduction of Fe(III)-heme to Fe(II)-heme of immobilized Cyt-c was possible on all films but that the adsorbed protein remained electroactive.

  11. Influence of Pore Size on the Optical and Electrical Properties of Screen Printed TiO2 Thin Films

    Directory of Open Access Journals (Sweden)

    Dinfa Luka Domtau

    2016-01-01

    Full Text Available Influence of pore size on the optical and electrical properties of TiO2 thin films was studied. TiO2 thin films with different weight percentages (wt% of carbon black were deposited by screen printing method on fluorine doped tin oxide (FTO coated on glass substrate. Carbon black decomposed on annealing and artificial pores were created in the films. All the films were 3.2 µm thick as measured by a surface profiler. UV-VIS-NIR spectrophotometer was used to study transmittance and reflectance spectra of the films in the photon wavelength of 300–900 nm while absorbance was studied in the range of 350–900 nm. Band gaps and refractive index of the films were studied using the spectra. Reflectance, absorbance, and refractive index were found to increase with concentrations of carbon black. There was no significant variation in band gaps of films with change in carbon black concentrations. Transmittance reduced as the concentration of carbon black in TiO2 increased (i.e., increase in pore size. Currents and voltages (I-V characteristics of the films were measured by a 4-point probe. Resistivity (ρ and conductivity (σ of the films were computed from the I-V values. It was observed that resistivity increased with carbon black concentrations while conductivity decreased as the pore size of the films increased.

  12. Room temperature growth of nanocrystalline anatase TiO{sub 2} thin films by dc magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Preetam, E-mail: preetamphy@gmail.co [Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology, Indian Institute of Technology Roorkee, Roorkee 247667 (India); Kaur, Davinder [Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology, Indian Institute of Technology Roorkee, Roorkee 247667 (India)

    2010-03-01

    We report, the structural and optical properties of nanocrystalline anatase TiO{sub 2} thin films grown on glass substrate by dc magnetron sputtering at room temperature. The influence of sputtering power and pressure over crystallinity and surface morphology of the films were investigated. It was observed that increase in sputtering power activates the TiO{sub 2} film growth from relative lower surface free energy to higher surface free energy. XRD pattern revealed the change in preferred orientation from (1 0 1) to (0 0 4) with increase in sputtering power, which is accounted for different surface energy associated with different planes. Microstructure of the films also changes from cauliflower type to columnar type structures with increase in sputtering power. FESEM images of films grown at low pressure and low sputtering power showed typical cauliflower like structure. The optical measurement revealed the systematic variation of the optical constants with deposition parameters. The films are highly transparent with transmission higher than 90% with sharp ultraviolet cut off. The transmittance of these films was found to be influenced by the surface roughness and film thickness. The optical band gap was found to decrease with increase in the sputtering power and pressure. The refractive index of the films was found to vary in the range of 2.50-2.24 with increase in sputtering pressure or sputtering power, resulting in the possibility of producing TiO{sub 2} films for device applications with different refractive index, by changing the deposition parameters.

  13. Preparation and characterization of photocatalytic performance of hierarchical heterogeneous nanostructured ZnO/TiO2 films made by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Le Phuc Quy; Vu Thi Hanh Thu

    2013-01-01

    With the aim to enhance photocatalytic properties and anti-Ecoli bacteria abilities of TiO 2 thin films; hierarchical heterogeneous nanostructured ZnO/TiO 2 (HN s ) films were deposited by DC magnetron sputtering. The obtained results showed that both the photocatalytic performance and anti-Ecoli bacteria ability of HN s films exhibited enhancement in comparison with standard TiO 2 films. This enhancement was explained due to the reduction of the electron - hole recombination and the red shift of absorption edge of the HNs films. (author)

  14. Influence of Nb dopant on the structural and optical properties of nanocrystalline TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Kaleji, Behzad Koozegar, E-mail: bkaleji@yahoo.com [Department of Materials Engineering, Faculty of Engineering, Tarbiat Modares University, P.O. Box:14115-143, Tehran (Iran, Islamic Republic of); Sarraf-Mamoory, Rasoul, E-mail: rsarrafm@modares.ac.ir [Department of Materials Engineering, Faculty of Engineering, Tarbiat Modares University, P.O. Box:14115-143, Tehran (Iran, Islamic Republic of); Fujishima, Akira [Photo-catalyst Group, Kanagawa Academy of Science and Technology, KSP East 412, 3-2-1 Sakado, Takatsu-ku, Kawasaki, Kanagawa 213-0012 (Japan)

    2012-01-16

    Highlights: Black-Right-Pointing-Pointer We coated Nb-doped TiO{sub 2} films on glazed porcelain via sol-gel dip coating method. Black-Right-Pointing-Pointer We examined coatings by degradation of MB solution and optical light transmittance. Black-Right-Pointing-Pointer Coatings show enhanced photo-catalytic activity in 1 mol% Nb. Black-Right-Pointing-Pointer Nb doping inhibited the grain growth, and which are found to inhibit the anatase to rutile phase transformation. - Abstract: In this study, preparation of Nb-doped (0-20 mol% Nb) TiO{sub 2} dip-coated thin films on glazed porcelain substrates via sol-gel process has been investigated. The effects of Nb on the structural, optical, and photo-catalytic properties of applied thin films have been studied by X-ray diffraction, Raman spectroscopy, and scanning electron microscopy. Surface topography and surface chemical state of thin films was examined by atomic force microscope and X-ray photoelectron spectroscopy. XRD and Raman study showed that the Nb doping inhibited the grain growth. The photo-catalytic activity of the film was tested on degradation of methylene blue. Best photo-catalytic activity of Nb-doped TiO{sub 2} thin films were measured in the TiO{sub 2}-1 mol% Nb sample. The average optical transmittance of about 47% in the visible range and the band gap of films became wider with increasing Nb doping concentration. The Nb{sup 5+} dopant presented substitutional Ti{sup 4+} into TiO{sub 2} lattice.

  15. Electrical characteristics of SrTiO{sub 3}/Al{sub 2}O{sub 3} laminated film capacitors

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Yong; Yao, Manwen, E-mail: yaomw@tongji.edu.cn; Chen, Jianwen; Xu, Kaien; Yao, Xi [Functional Materials Research Laboratory, School of Materials Science and Engineering, Tongji University, Shanghai 200092 (China)

    2016-07-07

    The electrical characteristics of SrTiO{sub 3}/Al{sub 2}O{sub 3} (160 nm up/90 nm down) laminated film capacitors using the sol-gel process have been investigated. SrTiO{sub 3} is a promising and extensively studied high-K dielectric material, but its leakage current property is poor. SrTiO{sub 3}/Al{sub 2}O{sub 3} laminated films can effectively suppress the demerits of pure SrTiO{sub 3} films under low electric field, but the leakage current value reaches to 0.1 A/cm{sup 2} at higher electric field (>160 MV/m). In this study, a new approach was applied to reduce the leakage current and improve the dielectric strength of SrTiO{sub 3}/Al{sub 2}O{sub 3} laminated films. Compared to laminated films with Au top electrodes, dielectric strength of laminated films with Al top electrodes improves from 205 MV/m to 322 MV/m, simultaneously the leakage current maintains the same order of magnitude (10{sup −4} A/cm{sup 2}) until the breakdown occurs. The above electrical characteristics are attributed to the anodic oxidation reaction in origin, which can repair the defects of laminated films at higher electric field. The anodic oxidation reactions have been confirmed by the corresponding XPS measurement and the cross sectional HRTEM analysis. This work provides a new approach to fabricate dielectrics with high dielectric strength and low leakage current.

  16. modified BiFeO3–BaTiO3

    Indian Academy of Sciences (India)

    based perovskite structures lead- free BiFeO3–BaTiO3 solid solutions are popularly studied due to the high Curie temperature (TC). It was reported that the BiFeO3–BaTiO3 system possessed high piezoelectric. ∗. Author for correspondence ...

  17. Assembly of CdSe onto mesoporous TiO{sub 2} films induced by a self-assembled monolayer for quantum dot-sensitized solar cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Chong, Lai-Wan; Chien, Huei-Ting; Lee, Yuh-Lang [Department of Chemical Engineering, National Cheng Kung University, No. 1 University Road, Tainan 70101 (China)

    2010-08-01

    A self-assembled monolayer (SAM) of 3-mercaptopropyl-trimethyoxysilane (MPTMS) is pre-assembled onto a mesoporous TiO{sub 2} film and is used as a surface-modified layer to induce the growth of CdSe QDs in the successive ionic layer adsorption and reaction (SILAR) process. Due to the specific interaction of the terminal thiol groups to CdSe, the MPTMS SAM is found to increase the nucleation and growth rates of CdSe in the SILAR process, leading to a well covering and higher uniform CdSe layer which has a superior ability, compared with the electrode without MPTMS, in inhibiting the charge recombination at the electrode/electrolyte interface. Furthermore, the performance of the CdSe-sensitized TiO{sub 2} electrode can further be improved by an additional heat annealing after film deposition, attributable to a better interfacial connection between CdSe and TiO{sub 2}, as well as a better connection among CdSe QDs. The CdSe-sensitized solar cell prepared by the present strategy can achieve an energy conversion efficiency of 2.65% under the illumination of one sun (AM 1.5, 100 mW cm{sup -2}). (author)

  18. Optimization of nanocomposite Au/TiO2 thin films towards LSPR optical-sensing

    Science.gov (United States)

    Rodrigues, M. S.; Costa, D.; Domingues, R. P.; Apreutesei, M.; Pedrosa, P.; Martin, N.; Correlo, V. M.; Reis, R. L.; Alves, E.; Barradas, N. P.; Sampaio, P.; Borges, J.; Vaz, F.

    2018-04-01

    Nanomaterials based on Localized Surface Plasmon Resonance (LSPR) phenomena are revealing to be an important solution for several applications, namely those of optical biosensing. The main reasons are mostly related to their high sensitivity, with label-free detection, and to the simplified optical systems that can be implemented. For the present work, the optical sensing capabilities were tailored by optimizing LSPR absorption bands of nanocomposite Au/TiO2 thin films. These were grown by reactive DC magnetron sputtering. The main deposition parameters changed were the number of Au pellets placed in the Ti target, the deposition time, and DC current applied to the Ti-Au target. Furthermore, the Au NPs clustering, a key feature to have biosensing responses, was induced by several post-deposition in-air annealing treatments at different temperatures, and investigated via SEM analysis. Results showed that the Au/TiO2 thin films with a relatively low thickness (∼100 nm), revealing concentrations of Au close to 13 at.%, and annealed at temperatures above 600 °C, had the most well-defined LSPR absorption band and thus, the most promising characteristics to be explored as optical sensors. The NPs formation studies revealed an incomplete aggregation at 300 and 500 ⁰C and well-defined spheroidal NPs for higher temperatures. Plasma treatment with Ar led to a gradual blue-shift of the LSPR absorption band, which demonstrates the sensitivity of the films to changes in the dielectric environment surrounding the NPs (essential for optical sensing applications) and the exposure of the Au nanoparticles (crucial for a higher sensitivity).

  19. Adsorption of carbon dioxide on TEPA-modified TiO_2/titanate composite nano-rods

    International Nuclear Information System (INIS)

    Kapica-Kozar, Joanna; Michalkiewicz, Beata; Wrobel, Rafal J.; Mozia, Sylwia; Pirog, Ewa; Usiak-Nejman, Ewelina K.; Serafin, Jaroslaw; Morawski, Antoni W.; Narkiewicz, Urszula

    2017-01-01

    A titanate-TiO_2 composite was obtained through hydrothermal treatment of TiO_2 in KOH solution. The presence of a titanate phase was confirmed by X-ray diffraction (XRD), whereas scanning electron microscopy (SEM) measurements showed the porous nano-rod structure of the material. The obtained nano-rods were treated with tetra-ethylene-pentamine (TEPA). Such synthesized sorbents were applied for CO_2 removal. The CO_2 capacity under a pressure of 1 bar and at 80 C was 0.47, 0.34, and 3.11 mmol.g"-"1 for the starting TiO_2, the titanate-TiO_2 composite and the TEPA-titanate-TiO_2 composite (27.4 wt% of TEPA), respectively. The experimental isotherms of CO_2 were analysed using the Langmuir, Freundlich, Sips, Toth, Unilan, Redlich-Peterson, Radke-Prausnitz, Dubinin-Radushkevich, Temkin and Pyzhev, and Jovanovich models. The error sums of squares (SSR) function was used to test the fit of the models. The analysis revealed that the Sips isotherm is the best-fitting model for the CO_2 adsorption on the starting TiO_2, whereas the Freundlich equation should be used to describe the CO_2 adsorption isotherm on the titanate-TiO_2 composite. The CO_2 adsorption on the TEPA-modified sorbents was proposed to be described using the Sips isotherm for physical sorption and the modified Sips model for chemical sorption. The calculated isosteric heat of adsorption was found to be E46 kJ mol"-"1, which is about two times higher than the heat of CO_2 absorption in liquid TEPA reported in the literature (i.e. E85 kJ.mol"-"1). Therefore, it was concluded that the TEPA-titanate-TiO_2 composite is an attractive alternative for liquid amines due to the lower energy of regeneration in the sorption-desorption process. The material was proved to be stable during multiple sorption-desorption cycles. Moreover, its thermal stability up to 150 C was confirmed by thermogravimetric analysis (TGA). All these features make it a promising alternative for sorbents based on liquid amines. (authors)

  20. Preparation of Porous F-WO3/TiO2 Films with Visible-Light Photocatalytic Activity by Microarc Oxidation

    Directory of Open Access Journals (Sweden)

    Chung-Wei Yeh

    2012-01-01

    Full Text Available Porous F-WO3/TiO2 (mTiO2 films are prepared on titanium sheet substrates using microarc oxidation (MAO technique. The X-ray diffraction patterns show that visible-light (Vis enabling mTiO2 films with a very high content of anatase TiO2 and high loading of WO3 are successfully synthesized at a low applied voltage of 300 V using electrolyte contenting NaF and Na2WO4 without subsequent heat treatment. The cross-sectional transmission electron microscopy micrograph reveals that the mTiO2 films feature porous networks connected by many micron pores. The diffused reflection spectrum displays broad absorbance across the UV-Vis regions and a significant red shift in the band gap energy (∼2.23 eV for the mTiO2 film. Owing to the high specific surface area from the porous microstructure, the mTiO2 film shows a 61% and 50% rate increase in the photocatalytic dye degradation, as compared with the N,C-codoped TiO2 films under UV and Vis irradiation, respectively.

  1. Degradation of paracetamol by advance oxidation processes using modified reticulated vitreous carbon electrodes with TiO(2) and CuO/TiO(2)/Al(2)O(3).

    Science.gov (United States)

    Arredondo Valdez, H C; García Jiménez, G; Gutiérrez Granados, S; Ponce de León, C

    2012-11-01

    The degradation of paracetamol in aqueous solutions in the presence of hydrogen peroxide was carried out by photochemistry, electrolysis and photoelectrolysis using modified 100 pores per inch reticulated vitreous carbon electrodes. The electrodes were coated with catalysts such as TiO(2) and CuO/TiO(2)/Al(2)O(3) by electrophoresis followed by heat treatment. The results of the electrolysis with bare reticulated vitreous carbon electrodes show that 90% paracetamol degradation occurs in 4 h at 1.3 V vs. SCE, forming intermediates such as benzoquinone and carboxylic acids followed by their complete mineralisation. When the electrolysis was carried out with the modified electrodes such as TiO(2)/RVC, 90% degradation was achieved in 2 h while with CuO/TiO(2)/Al(2)O(3)/RVC, 98% degradation took only 1 h. The degradation was also carried out in the presence of UV reaching 95% degradation with TiO(2)/RVC/UV and 99% with CuO/TiO(2)/Al(2)O(3)/RVC/UV in 1 h. The reactions were followed by spectroscopy UV-Vis, HPLC and total organic carbon analysis. These studies show that the degradation of paracetamol follows a pseudo-first order reaction kinetics. Copyright © 2012 Elsevier Ltd. All rights reserved.

  2. Hydrothermal–galvanic couple synthesis of directionally oriented BaTiO3 thin films on TiN-coated substrates

    International Nuclear Information System (INIS)

    Yang, Chia-Jung; Tsai, Di-You; Chan, Pei-Hsuan; Wu, Chu-Tsun; Lu, Fu-Hsing

    2013-01-01

    BaTiO 3 films were synthesized on TiN-coated Si substrate below 100 °C by a hydrothermal–galvanic couple technique in barium contained alkaline solutions. X-ray diffraction and electron backscatter diffraction results show that the BaTiO 3 thin films were directionally oriented grown on the TiN/Si substrates, i.e., (111) BaTiO 3 over (111) TiN. The surface morphologies revealed that BaTiO 3 nucleated and grew over the TiN surface with a single layer. From kinetic analyses, the growth rates of BaTiO 3 films prepared by the hydrothermal–galvanic couple technique were faster than a hydrothermal method. The galvanic effects were confirmed by investigating the induced currents and energies. The galvanic currents were generated and controlled by both the dissolution of TiN and the formation of BaTiO 3 . The output electric energies increased rapidly with the reaction time and leveled off at the full coverage of BaTiO 3 . - Highlights: • Cubic BaTiO 3 films are synthesized by a hydrothermal–galvanic couple method (HT–GC). • Growth rates of BaTiO 3 films made by HT–GC are faster than a hydrothermal method. • BaTiO 3 films are directionally oriented grown on the TiN/Si substrates. • Galvanic currents are controlled by dissolution of TiN and formation of BaTiO 3

  3. TiO2 nanotube formation by Ti film anodization and their transport properties for dye-sensitized solar cells

    NARCIS (Netherlands)

    Iraj, M.; Kolahdouz, M.; Asl-Soleimani, E.; Esmaeili, E.; Kolahdouz Esfahani, Z.

    2016-01-01

    In this paper, we present the synthesis of TiO2 nanotube (NT) arrays formed by anodization of Ti film deposited on a fluorine-doped tin oxide-coated glass substrate by direct current magnetron sputtering. NH4F/ethylene glycol electrolyte was used to demonstrate the growth of stable nanotubes at room

  4. Effect of TiO2/Al2O3 film coated diamond abrasive particles by sol-gel technique

    Science.gov (United States)

    Hu, Weida; Wan, Long; Liu, Xiaopan; Li, Qiang; Wang, Zhiqi

    2011-04-01

    The diamond abrasive particles were coated with the TiO2/Al2O3 film by the sol-gel technique. Compared with the uncoated diamonds, the TiO2/Al2O3 film was excellent material for the protection of the diamonds. The results showed that the incipient oxidation temperature of the TiO2/Al2O3 film coated diamonds in air atmosphere was 775 °C, which was higher 175 °C than that of the uncoated diamonds. And the coated diamonds also had better the diamond's single particle compressive strength and the impact toughness than that of uncoated diamonds after sintering at 750 °C. For the vitrified bond grinding wheels, replacing the uncoated diamonds with the TiO2/Al2O3 film coated diamonds, the volume expansion of the grinding wheels decreased from 6.2% to 3.4%, the porosity decreased from 35.7% to 25.7%, the hardness increased from 61.2HRC to 66.5HRC and the grinding ratio of the vitrified bond grinding wheels to carbide alloy (YG8) increased from 11.5 to 19.1.

  5. Design and fabrication of ZnO/TiO2-based thin-film inverter circuits using solution processing techniques

    International Nuclear Information System (INIS)

    Liau, Leo Chau-Kuang; Kuo, Juo-Wei; Chiang, Hsin-Ni

    2012-01-01

    Novel and cost-effective ceramic-based thin-film inverter circuits, based on two layers of TiO 2 and ZnO films to construct junction field-effect transistors (FETs), were designed and fabricated by solution coating techniques. The double layers of the sol–gel ZnO and TiO 2 films were coated and characterized as a diode according to the current–voltage performance. Two types of FETs, the p-channel (p-FET) and the n-channel (n-FET) devices, were produced using different coating sequences of ZnO and TiO 2 layers. Both of the transistor performances were evaluated by analyzing the source–drain current versus voltage (I ds –V ds ) data with the control of the gate voltage (V g ). The ZnO/TiO 2 -based inverter circuits, such as the complementary-FET device, were further fabricated using the integration of the p-FET and the n-FET. The voltage transfer characteristics of the inverters were estimated by the tests of the input voltage (V in ) versus the output voltage (V out ) for the thin-film inverter circuits. (paper)

  6. Photocatalytic and photoelectrochemical properties of sol–gel TiO2 films of controlled thickness and porosity

    Czech Academy of Sciences Publication Activity Database

    Krýsa, J.; Baudyš, M.; Zlámal, M.; Krýsová, Hana; Morozová, Magdalena; Klusoň, Petr

    2014-01-01

    Roč. 230, JUL 2014 (2014), s. 2-7 ISSN 0920-5861 Institutional support: RVO:61388955 ; RVO:67985858 Keywords : TiO2 film * Sol-gel * Thickness Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 3.893, year: 2014

  7. Spin Speed and Duration Dependence of TiO2 Thin Films pH Sensing Behavior

    Directory of Open Access Journals (Sweden)

    Muhammad AlHadi Zulkefle

    2016-01-01

    Full Text Available Titanium dioxide (TiO2 thin films were applied as the sensing membrane of an extended-gate field-effect transistor (EGFET pH sensor. TiO2 thin films were deposited by spin coating method and the influences of the spin speed and spin duration on the pH sensing behavior of TiO2 thin films were investigated. The spin coated TiO2 thin films were connected to commercial metal-oxide-semiconductor field-effect transistor (MOSFET to form the extended gates and the MOSFET was integrated in a readout interfacing circuit to complete the EGFET pH sensor system. For the spin speed parameter investigation, the highest sensitivity was obtained for the sample spun at 3000 rpm at a fixed spinning time of 60 s, which was 60.3 mV/pH. The sensitivity was further improved to achieve 68 mV/pH with good linearity of 0.9943 when the spin time was 75 s at the speed of 3000 rpm.

  8. Polyoxometalate-modified TiO2 nanotube arrays photoanode materials for enhanced dye-sensitized solar cells

    Science.gov (United States)

    Liu, Ran; Sun, Zhixia; Zhang, Yuzhuo; Xu, Lin; Li, Na

    2017-10-01

    In this work, we prepared for the first time the TiO2 nanotube arrays (TNAs) photoanode with polyoxometalate(POMs)-modified TiO2 electron-transport layer for improving the performance of zinc phthalocyanine(ZnPc)-sensitized solar cells. The as-prepared POMs/TNAs/ZnPc composite photoanode exhibited higher photovoltaic performances than the TNAs/ZnPc photoanode, so that the power conversion efficiency of the solar cell device based on the POMs/TNAs/ZnPc photoanode displayed a notable improvement of 45%. These results indicated that the POMs play a key role in reducing charge recombination in phthalocyanine-sensitized solar cells, together with TiO2 nanotube arrays being helpful for electron transport. The mechanism of the performance improvement was demonstrated by the measurements of electrochemical impedance spectra and open-circuit voltage decay curves. Although the resulting performance is still below that of the state-of-the-art dye-sensitized solar cells, this study presents a new insight into improving the power conversion efficiency of phthalocyanine-sensitized solar cells via polyoxometalate-modified TiO2 nanotube arrays photoanode.

  9. Influence of Nb content on the structural and optical properties of anatase TiO{sub 2} polycrystalline thin film by e-beam technique

    Energy Technology Data Exchange (ETDEWEB)

    Shah, A., E-mail: attaullah77@yahoo.com; Mahmood, Arshad; Aziz, Uzma; Rashid, Rashad; Raza, Qaiser; Ali, Zahid

    2016-09-01

    In this paper, we report the structural and optical properties of Nb-doped TiO{sub 2} thin films deposited by e-beam evaporation technique. After post annealing in air at 500 °C for 1 h, the samples were characterized by various techniques such as X-ray diffraction (XRD), Raman spectroscopy, UV–Vis spectrophotometry and spectroscopic Ellipsometer. Both XRD and Raman analyses indicate that the films were crystallized into the polycrystalline anatase TiO{sub 2} structure. However it was observed that the crystallinity of the films decreases with the addition of Nb atoms and tends to become amorphous at 20% Nb content in TiO{sub 2} film. Moreover, no new phases such as Nb{sub 2}O{sub 5}, NbO{sub 2} or Nb metal were observed. The band gap energy was found to decrease with the increasing of Nb concentration which was verified by ellipsometric study. Ellipsomtric measurements also indicate that refractive index (n) of the films decreases while extinction coefficient (k) increases with the increasing of Nb content. All these analyses elucidate that the incorporation of Nb atom into TiO{sub 2} may tune the structural and optical properties of TiO{sub 2} thin films. - Highlights: • The addition of Nb into TiO{sub 2} film has strongly influenced its physical properties. • Anatase polycrystalline Nb:TiO{sub 2} films were grown up to 15% Nb content. • The film becomes an amorphous at 20% Nb doping. • Band gap energy of TiO{sub 2} film was decreased with increasing of Nb content in the film. • The Optical constants (n, k) of Nb:TiO{sub 2} film were varied as a function of Nb content.

  10. Metal-to-Insulator Transition in Anatase TiO2 Thin Films Induced by Growth Rate Modulation

    Energy Technology Data Exchange (ETDEWEB)

    Tachikawa, T; Minohara, M.; Nakanishi, Y.; Hikita, Y.; Yoshita, M.; Akiyama, H.; Bell, C.; Hwang, H.Y.

    2012-06-21

    We demonstrate control of the carrier density of single phase anatase TiO{sub 2} thin films by nearly two orders of magnitude by modulating the growth kinetics during pulsed laser deposition, under fixed thermodynamic conditions. The resistivity and the intensity of the photoluminescence spectra of these TiO{sub 2} samples, both of which correlate with the number of oxygen vacancies, are shown to depend strongly on the growth rate. A quantitative model is used to explain the carrier density changes.

  11. RBS analysis of substoichiometric TiO{sub 2}-anatase thin films for visible-light photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Ager, F.J. [Depto. Fisica Aplicada I, Escuela Universitaria Politecnica, Universidad de Sevilla, C. Virgen de Africa 7, E-41011 Sevilla (Spain) and Centro Nacional de Aceleradores, Av. Thomas A. Edison, E-41092 Sevilla (Spain)]. E-mail: fjager@us.es; Justicia, I. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Gerbasi, R. [Istituto di Chimica Inorganica e delle Superficie, Corso Stati Uniti 4, I-35127 Padova (Italy); Battiston, G.A. [Istituto di Chimica Inorganica e delle Superficie, Corso Stati Uniti 4, I-35127 Padova (Italy); McSporran, N. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Figueras, A. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); CFATA-UNAM, Juriquilla, Queretaro, C.P. 76230 Queretaro (Mexico)

    2006-08-15

    The anatase phase of TiO{sub 2} is the most promising photocatalyst for organic pollutants degradation. However, due to the large anatase band gap energy the possibility of using visible sunlight as energy source for the photocalatysis activation is ruled out and ultraviolet (UV) radiation with a wave length below the critical limit is thus required. Inducing defects in the anatase crystalline structure in the form of oxygen substoichiometry may theoretically reduce this large band gap energy. This paper focuses on the determination of the stoichiometry of TiO{sub 2} thin films and its influence on the photodegradation properties.

  12. Enhanced photoelectrochemical and photocatalytic behaviors of MFe2O4 (M = Ni, Co, Zn and Sr) modified TiO2 nanorod arrays

    Science.gov (United States)

    Gao, Xin; Liu, Xiangxuan; Zhu, Zuoming; Wang, Xuanjun; Xie, Zheng

    2016-07-01

    Modified TiO2 nanomaterials are considered to be promising in energy conversion and ferrites modification may be one of the most efficient modifications. In this research, various ferrites, incorporated with various cations (MFe2O4, M = Ni, Co, Zn, and Sr), are utilized to modify the well aligned TiO2 nanorod arrays (NRAs), which is synthesized by hydrothermal method. It is found that all MFe2O4/TiO2 NRAs show obvious red shift into the visible light region compared with the TiO2 NRAs. In particular, NiFe2O4 modification is demonstrated to be the best way to enhance the photoelectrochemical and photocatalytic activity of TiO2 NRAs. Furthermore, the separation and transfer of charge carriers after MFe2O4 modification are clarified by electrochemical impedance spectroscopy measurements. Finally, the underlying mechanism accounting for the enhanced photocatalytic activity of MFe2O4/TiO2 NRAs is proposed. Through comparison among different transition metals modified TiO2 with the same synthesis process and under the same evaluating condition, this work may provide new insight in designing modified TiO2 nanomaterials as visible light active photocatalysts.

  13. CdS/TiO{sub 2} nanocomposite film and its enhanced photoelectric responses to dry air and formaldehyde induced by visible light at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Zou, Zhijun, E-mail: zjzou@xynu.edu.cn [Key Laboratory of Advanced Micro/Nano Functional Materials, Department of Physics and Electronic Engineering, Xinyang Normal University, Xinyang 464000 (China); State Key Laboratory of Material Processing and Die & Mould Technology, Nanomaterials and Smart Sensors Research Laboratory, Department of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China); Qiu, Yang [Key Laboratory of Advanced Micro/Nano Functional Materials, Department of Physics and Electronic Engineering, Xinyang Normal University, Xinyang 464000 (China); Xie, Changsheng [State Key Laboratory of Material Processing and Die & Mould Technology, Nanomaterials and Smart Sensors Research Laboratory, Department of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China); Xu, Jingjing; Luo, Yongsong; Wang, Chunlei; Yan, Hailong [Key Laboratory of Advanced Micro/Nano Functional Materials, Department of Physics and Electronic Engineering, Xinyang Normal University, Xinyang 464000 (China)

    2015-10-05

    Highlights: • Photoelectric responses of TiO{sub 2} and CdS/TiO{sub 2} to dry air and formaldehyde were tested. • In contrary to TiO{sub 2}, photoelectric response of CdS/TiO{sub 2} obviously increased. • CdS/TiO{sub 2} nanocomposite device exhibits excellent stability to formaldehyde. • CdS/TiO{sub 2} may be a promising material for developing high performance sensor. - Abstract: Photoelectric responses of pure TiO{sub 2} and CdS/TiO{sub 2} nanocomposite devices to dry air and formaldehyde under visible light irradiation at room temperature were investigated in this work. The pure TiO{sub 2} film was firstly prepared by screen printing and CdS/TiO{sub 2} nanocomposite film by the subsequent SILAR process. XRD, FE-SEM, HR-TEM and UV–vis DRS analysis were employed to examine the fundamental characteristics of as-prepared samples. Photoelectric responses of pure TiO{sub 2} device displayed that no obvious photocurrent was observed upon turning the visible light on either in dry air or in formaldehyde. But in contrary to pure TiO{sub 2} device, the photoelectric response of CdS/TiO{sub 2} nanocomposite device has been obviously enhanced. It is the adding of CdS, which works as a sensitizer, that accounts for the enhanced response and makes the CdS/TiO{sub 2} device sensitive to the visible light. Moreover, the CdS/TiO{sub 2} nanocomposite device exhibits excellent stability to formaldehyde. The present work does not only shed light on the photoelectric gas sensing properties of TiO{sub 2} and CdS/TiO{sub 2}, but also suggests that the CdS/TiO{sub 2} nanocomposite may be a promising material for fabricating visible-light-induced photoelectric gas sensors working at room temperature.

  14. Compliant ferroelastic domains in epitaxial Pb(Zr,Ti)O{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Feigl, L.; McGilly, L. J.; Sandu, C. S.; Setter, N. [Ceramics Laboratory, EPFL - Swiss Federal Institute of Technology, Lausanne CH-1015 (Switzerland)

    2014-04-28

    Ordered patterns of highly compliant ferroelastic domains have been created by use of tensile strained epitaxial Pb(Zr,Ti)O{sub 3} thin films, of very low defect density, grown on DyScO{sub 3} substrates. The effect of 180° switching on well-ordered a/c 90° domain patterns is investigated by a combination of transmission electron microscopy, piezoelectric force microscopy, and X-ray diffraction. It is shown that ferroelastic a-domains, having an in-plane polarization, can be created and completely removed on a local level by an out-of-plane electric field. The modifications of the ferroelastic domain pattern can be controlled by varying the parameters used during switching with a piezoresponse force microscope to produce the desired arrangement.

  15. Band-gap narrowing of TiO2 films induced by N-doping

    International Nuclear Information System (INIS)

    Nakano, Y.; Morikawa, T.; Ohwaki, T.; Taga, Y.

    2006-01-01

    N-doped TiO 2 films were deposited on n + -GaN/Al 2 O 3 substrates by reactive magnetron sputtering and subsequently crystallized by annealing at 550 o C in flowing N 2 gas. The N-doping concentration was ∼8.8%, as determined from X-ray photoelectron spectroscopy measurements. Deep-level optical spectroscopy measurements revealed two characteristic deep levels located at 1.18 and 2.48 eV below the conduction band. The 1.18 eV level is probably attributable to the O vacancy state and can be active as an efficient generation-recombination center. Additionally, the 2.48 eV band is newly introduced by the N-doping and contributes to band-gap narrowing by mixing with the O 2p valence band

  16. Tuning the resistive switching properties of TiO2-x films

    Science.gov (United States)

    Ghenzi, N.; Rozenberg, M. J.; Llopis, R.; Levy, P.; Hueso, L. E.; Stoliar, P.

    2015-03-01

    We study the electrical characteristics of TiO2-x-based resistive switching devices fabricated with different oxygen/argon flow ratio during the oxide thin film sputtering deposition. Upon minute changes in this fabrication parameter, three qualitatively different device characteristics were accessed in the same system, namely, standard bipolar resistive switching, electroforming-free devices, and devices with multi-step breakdown. We propose that small variations in the oxygen/ argon flow ratio result in relevant changes of the oxygen vacancy concentration, which is the key parameter determining the resistive switching behavior. The coexistence of percolative or non-percolative conductive filaments is also discussed. Finally, the hypothesis is verified by means of the temperature dependence of the devices in low resistance state.

  17. Deep-level optical spectroscopy investigation of N-doped TiO2 films

    International Nuclear Information System (INIS)

    Nakano, Yoshitaka; Morikawa, Takeshi; Ohwaki, Takeshi; Taga, Yasunori

    2005-01-01

    N-doped TiO 2 films were deposited on n + -GaN/Al 2 O 3 substrates by reactive magnetron sputtering and subsequently crystallized by annealing at 550 deg. C in flowing N 2 gas. The N-doping concentration was ∼8.8%, as determined from x-ray photoelectron spectroscopy measurements. Deep-level optical spectroscopy measurements revealed two characteristic deep levels located at ∼1.18 and ∼2.48 eV below the conduction band. The 1.18 eV level is probably attributable to the O vacancy state and can be active as an efficient generation-recombination center. Additionally, the 2.48 eV band is newly introduced by the N doping and contributes to band-gap narrowing by mixing with the O 2p valence band

  18. X-ray photoelectron spectroscopy characterization of composite TiO{sub 2}-poly(vinylidenefluoride) films synthesised for applications in pesticide photocatalytic degradation

    Energy Technology Data Exchange (ETDEWEB)

    Losito, I.; Amorisco, A.; Palmisano, F.; Zambonin, P.G

    2005-02-15

    X-ray photoelectron spectroscopy (XPS) was adopted for the analytical characterization of composite titanium dioxide-poly(vinylidenefluoride) (TiO{sub 2}-PVDF) films developed for applications in the photocatalytic degradation of pollutants. The composites were deposited on glass substrates by casting or spin coating from TiO{sub 2}-PVDF suspensions in dimethylformamide (DMF). XPS data on the TiO{sub 2}-PVDF surface composition were used to optimize preparation conditions (composition of the TiO{sub 2}/PVDF suspension, deposition technique) in terms of titanium dioxide surface amount and film stability. The use of spin-coating deposition and the increase of TiO{sub 2} amount in the DMF suspensions were found to improve the titanium surface content, although high TiO{sub 2}/PVDF ratios led to film instability. PVDF-TiO{sub 2} films were also used in preliminary photocatalytic degradation tests on isoproturon, a phenylurea herbicide, under solar UV irradiation; the results were compared to direct photolysis to evaluate the catalytic efficiency of immobilized TiO{sub 2} and the role played by the PVDF film during the degradation process.

  19. XAS study of the local environment of impurities in doped TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Rodriguez Torres, C.E. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina)]. E-mail: torres@fisica.unlp.edu.ar; Cabrera, A.F. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina); Errico, L.A. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina); Duhalde, S. [Lab. de Ablacion Laser, FI-UBA (Argentina); Renteria, M. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina); Golmar, F. [Lab. de Ablacion Laser, FI-UBA (Argentina); Sanchez, F.H. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina)

    2007-09-01

    In this work, we present an X-ray absorption spectroscopy (XAS) characterization of the local environment of the impurity in room temperature ferromagnetic (RTF) anatase TiO{sub 2} thin films doped with Co, Ni, Cu, or Zn, deposited on LaAlO{sub 3} substrate by pulsed laser deposition (PLD). It was found that there is a considerable amount of impurity atoms substituting Ti in TiO{sub 2} anatase, although the presence of metal transition monoxide clusters can not be discarded. From our results, we infer that the observed RT ferromagnetism of the samples could be assigned to the metal transition atoms replacing Ti in TiO{sub 2} anatase.

  20. The directed preparation of TiO2 nanotubes film on FTO substrate via hydrothermal method for gas sensing application

    Directory of Open Access Journals (Sweden)

    Pham Van Viet

    2016-04-01

    Full Text Available In this research, we directly synthesized TiO2 nanotubes film on Fluorine doped Tin oxide (FTO substrate via hydrothermal method from commercial TiO2 in NaOH solution at 135 ℃ for 24 hours. The samples were characterized by X-ray diffraction (XRD pattern, field emission scanning electron microscopy (FESEM and transmitting electron microscopy (TEM. The average diameter of TiO2 nanotubes (TNTs is about 10–12 nm and their length is about a few hundred nanometers. The sensitivity ability of TNTs increases as the gas concentration increases and developing to the highest sensitivity of TNTs is 2.4 at 700 ppm of the ethanol concentration. The same as the gas concentration, the sensitivity of TNTs increases when the temperature increases. Besides, the sensitivity of samples at 250 ℃ is doubled compared to samples determined at 100 ℃.

  1. Photoelectrochemical properties of TiO2 Nanotube Arrays Modified with BiOCl nanosheets

    International Nuclear Information System (INIS)

    Liu, Haipeng; Xu, Guangqing; Wang, Jinwen; Lv, Jun; Zheng, Zhixiang; Wu, Yucheng

    2014-01-01

    Highlights: • BiOCl were deposited on TiO2 NTAs by sequential chemical bath deposition. • BiOCl can decrease background photocurrent and increase current response. • High sensitivity BiOCl/TiO2 is due to the direct oxidation of organics on BiOCl. - Abstract: BiOCl nanosheets were deposited on anodized TiO 2 nanotube arrays (NTAs) by sequential chemical bath deposition method to get BiOCl/TiO 2 NTAs for photoelectrochemical detection of organic compounds (represented by glucose). The structures, elemental components and morphologies of TiO 2 and BiOCl/TiO 2 NTAs were characterized by using X-ray diffraction diffractometer, scanning electron microscope and transmission electron microscope. The photoelectrochemical behaviors of TiO 2 and BiOCl/TiO 2 NTAs in the buffer and glucose solutions were measured by cyclic votammetry and amperometry with different optical powers. The modification of BiOCl nanosheets on TiO 2 NTAs decreases the photocurrents of TiO 2 NTAs in the buffer solution and increases the current response to glucose. Both of the background photocurrent decrease and current response increase are benefit for photoelectrochemical detection of organic compounds. When glucose was used as the target organic compound, the optimized BiOCl/TiO 2 NTAs sensor achieved a sensitivity of 0.327 μA/μM (0.417 μA·cm −2 ·μM −1 ), linear range from 0 to 1300 μM and calculated detection limit of 5.7 μM. Mechanisms of BiOCl modification were studied by measuring the optical absorption and hydroxyl radical HO· productivity. The transfer of holes from TiO 2 to BiOCl and the direct oxidation of organic compounds on BiOCl nanosheets led to the decrease of background photocurrent (lower reaction rate of water splitting on BiOCl nanosheets) and the increase of current response to organic compounds (higher reaction rate of direct oxidation of organic compounds)

  2. Ultrasonic force microscopy on poly(vinyl alcohol)/SrTiO3 nano-perovskites hybrid films

    International Nuclear Information System (INIS)

    Marino, Salvatore; Joshi, Girish M.; Lusuardi, Angelo; Cuberes, M. Teresa

    2014-01-01

    Atomic Force Microscopy (AFM) and Ultrasonic Force Microscopy (UFM) have been applied to the characterization of composite samples formed by SrTiO 3 (STO) nanoparticles (NPs) and polyvinyl alcohol (PVA). The morphological features of the STO NPs were much better resolved using UFM than contact-mode AFM topogr