  1. Formation of hydroxyl radicals and kinetic study of 2-chlorophenol photocatalytic oxidation using C-doped TiO2, N-doped TiO2, and C,N Co-doped TiO2 under visible light.

    Science.gov (United States)

    Ananpattarachai, Jirapat; Seraphin, Supapan; Kajitvichyanukul, Puangrat

    2016-02-01

    This work reports on synthesis, characterization, adsorption ability, formation rate of hydroxyl radicals (OH(•)), photocatalytic oxidation kinetics, and mineralization ability of C-doped titanium dioxide (TiO2), N-doped TiO2, and C,N co-doped TiO2 prepared by the sol-gel method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and UV-visible spectroscopy were used to analyze the titania. The rate of formation of OH(•) for each type of titania was determined, and the OH-index was calculated. The kinetics of as-synthesized TiO2 catalysts in photocatalytic oxidation of 2-chlorophenol (2-CP) under visible light irradiation were evaluated. Results revealed that nitrogen was incorporated into the lattice of titania with the structure of O-Ti-N linkages in N-doped TiO2 and C,N co-doped TiO2. Carbon was joined to the Ti-O-C bond in the C-doped TiO2 and C,N co-doped TiO2. The 2-CP adsorption ability of C,N co-doped TiO2 and C-doped TiO2 originated from a layer composed of a complex carbonaceous mixture at the surface of TiO2. C,N co-doped TiO2 had highest formation rate of OH(•) and photocatalytic activity due to a synergistic effect of carbon and nitrogen co-doping. The order of photocatalytic activity per unit surface area was the same as that of the formation rate of OH(•) unit surface area in the following order: C,N co-doped TiO2 > C-doped TiO2 > N-doped TiO2 > undoped TiO2.

  2. Photocatalysis with chromium-doped TiO2: Bulk and surface doping

    KAUST Repository

    Ould-Chikh, Samy

    2014-04-15

    The photocatalytic properties of TiO2 modified by chromium are usually found to depend strongly on the preparation method. To clarify this problem, two series of chromium-doped titania with a chromium content of up to 1.56 wt % have been prepared under hydrothermal conditions: the first series (Cr:TiO2) is intended to dope the bulk of TiO2, whereas the second series (Cr/TiO2) is intended to load the surface of TiO2 with Cr. The catalytic properties have been compared in the photocatalytic oxidation of formic acid. Characterization data provides evidence that in the Cr/TiO2 catalysts chromium is located on the surface of TiO2 as amorphous CrOOH clusters. In contrast, in the Cr:TiO 2 series, chromium is mostly dissolved in the titania lattice, although a minor part is still present on the surface. Photocatalytic tests show that both series of chromium-doped titania demonstrate visible-light-driven photo-oxidation activity. Surface-doped Cr/TiO2 solids appear to be more efficient photocatalysts than the bulk-doped Cr:TiO2 counterparts. It\\'s classified! The photocatalytic properties of TiO2 modified by chromium depend strongly on the preparation method. To clarify this problem, two types of modified titania are discussed: one with CrIII doped in the bulk and one with CrOOH clusters on the TiO2 surface (see picture). Both series show visible-light-driven photo-oxidation activity. However, surface modification appears to be a more efficient strategy. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. Ag- and Cu-doped multifunctional bioactive nanostructured TiCaPCON films

    Energy Technology Data Exchange (ETDEWEB)

    Shtansky, D.V., E-mail: shtansky@shs.misis.ru [National University of Science and Technology “MISIS”, Leninsky prospekt 4, Moscow 119049 (Russian Federation); Batenina, I.V.; Kiryukhantsev-Korneev, Ph.V.; Sheveyko, A.N.; Kuptsov, K.A. [National University of Science and Technology “MISIS”, Leninsky prospekt 4, Moscow 119049 (Russian Federation); Zhitnyak, I.Y.; Anisimova, N.Yu.; Gloushankova, N.A. [N.N. Blokhin Russian Cancer Research Center of RAMS, Kashirskoe shosse 24, Moscow 115478 (Russian Federation)

    2013-11-15

    A key property of multicomponent bioactive nanostructured Ti(C,N)-based films doped with Ca, P, and O (TiCaPCON) that can be improved further is their antibacterial effect that should be achieved without compromising the implant bioactivity and biocompatibility. The present work is focused on the study of structure, chemical, mechanical, tribological, and biological properties of Ag- and Cu-doped TiCaPCON films. The films with Ag (0.4–4 at.%) and Cu (13 at.%) contents were obtained by simultaneous sputtering of a TiC{sub 0.5}–Ca{sub 3}(PO{sub 4}){sub 2} target and either an Ag or a Cu target. The film structure was studied using X-ray diffraction, transmission and scanning electron microscopy, energy dispersive X-ray spectroscopy, glow discharge optical emission spectroscopy, and Raman-shift and IR spectroscopy. The films were characterized in terms of their hardness, elastic modulus, dynamic impact resistance, friction coefficient and wear rate (both in air and normal saline), surface wettability, electrochemical behavior and Ag or Cu ion release in normal saline. Particular attention was paid to the influence of inorganic bactericides (Ag and Cu ions) on the bactericidal activity against unicellular yeast fungus Saccharomyces cerevisiae and gram-positive bacteria Lactobacillus acidophilus, as well as on the attachment, spreading, actin cytoskeleton organization, focal adhesions, and early stages of osteoblastic cell differentiation. The obtained results show that the Ag-doped films are more suitable for the protection of metallic surfaces against bacterial infection compared with their Cu-doped counterpart. In particular, an excellent combination of mechanical, tribological, and biological properties makes Ag-doped TiCaPCON film with 1.2 at.% of Ag very attractive material for bioengineering and modification of load-bearing metal implant surfaces.

  4. Improving the conductance of ZnO thin film doping with Ti by using a cathodic vacuum arc deposition process

    International Nuclear Information System (INIS)

    Wu, Chun-Sen; Lin, Bor-Tsuen; Jean, Ming-Der

    2011-01-01

    The Ti-doped ZnO films compared to un-doped ZnO films were deposited onto Corning XG glass substrates by using a cathodic vacuum arc deposition process in a mixture of oxygen and argon gases. The structural, electrical and optical properties of un-doped and Ti-doped ZnO films have been investigated. When the Ti target power is about 750 W, the incorporation of titanium atoms into zinc oxide films is obviously effective. Additionally, the resistivity of un-doped ZnO films is high and reduces to a value of 3.48 x 10 -3 Ω-cm when Ti is incorporated. The Ti doped in the ZnO films gave rise to the improvement of the conductivity of the films obviously. The Ti-doped ZnO films have > 85% transmittance in a range of 400-700 nm.

  5. Mechanical properties and biocompatibility of the sputtered Ti doped hydroxyapatite.

    Science.gov (United States)

    Vladescu, A; Padmanabhan, S C; Ak Azem, F; Braic, M; Titorencu, I; Birlik, I; Morris, M A; Braic, V

    2016-10-01

    The hydroxyapatite enriched with Ti were prepared as possible candidates for biomedical applications especially for implantable devices that are in direct contact to the bone. The hydroxyapatites with different Ti content were prepared by RF magnetron sputtering on Ti-6Al-4V alloy using pure hydroxyapatite and TiO2 targets. The content of Ti was modified by changing the RF power fed on TiO2 target. The XPS and FTIR analyses revealed the presence of hydroxyapatite structure. The hardness and elastic modulus of the hydroxyapatite were increased by Ti addition. After 5 days of culture, the cell viability of the Ti-6Al-4V was enhanced by depositing with undoped or doped hydroxyapatite. The Ti additions led to an increase in cell viability of hydroxyapatite, after 5 days of culture. The electron microscopy showed the presence of more cells on the surface of Ti-enriched hydroxyapatite than those observed on the surface of the uncoated alloys or undoped hydroxyapatite. Copyright © 2016 Elsevier Ltd. All rights reserved.

  6. Physical and chemical characterization of Ag-doped Ti coatings produced by magnetron sputtering of modular targets

    International Nuclear Information System (INIS)

    Schmitz, Tobias; Warmuth, Franziska; Werner, Ewald; Hertl, Cornelia; Groll, Jürgen; Gbureck, Uwe; Moseke, Claus

    2014-01-01

    Silver-doped Ti films were produced using a single magnetron sputtering source equipped with a titanium target containing implemented silver modules under variation of bias voltage and substrate temperature. The Ti(Ag) films were characterized regarding their morphology, contact angle, phase composition, silver content and distribution as well as the elution of Ag + ions into cell media. SEM and AFM pictures showed that substrate heating during film deposition supported the formation of even and dense surface layers with small roughness values, an effect that could even be enforced, when a substrate bias voltage was applied instead. The deposition of both Ti and Ag was confirmed by X-ray diffraction. ICP-MS and EDX showed a clear correlation between the applied sputtering parameters and the silver content of the coatings. Surface-sensitive XPS measurements revealed that higher substrate temperatures led to an accumulation of Ag in the near-surface region, while the application of a bias voltage had the opposite effect. Additional elution measurements using ICP-MS showed that the release kinetics depended on the amount of silver located at the film surface and hence could be tailored by variation of the sputter parameters. - Highlights: • Modular targets were used to deposit Ti(Ag) films. • Ag-content is adjustable by bias voltage, sputtering power and substrate temperature. • Coating parameters significantly change film morphology and roughness. • A critical parameter for Ag release is the fraction of silver on the film surface

  7. Visible Light Photoelectrochemical Properties of N-Doped TiO2 Nanorod Arrays from TiN

    Directory of Open Access Journals (Sweden)

    Zheng Xie

    2013-01-01

    Full Text Available N-doped TiO2 nanorod arrays (NRAs were prepared by annealing the TiN nanorod arrays (NRAs which were deposited by using oblique angle deposition (OAD technique. The TiN NRAs were annealed at 330°C for different times (5, 15, 30, 60, and 120 min. The band gaps of annealed TiN NRAs (i.e., N-doped TiO2 NRAs show a significant variance with annealing time, and can be controlled readily by varying annealing time. All of the N-doped TiO2 NRAs exhibit an enhancement in photocurrent intensity in visible light compared with that of pure TiO2 and TiN, and the one annealed for 15 min shows the maximum photocurrent intensity owning to the optimal N dopant concentration. The results show that the N-doped TiO2 NRAs, of which the band gap can be tuned easily, are a very promising material for application in photocatalysis.

  8. Structure, microstructure and photoluminescence of nanocrystalline Ti-doped gahnite

    International Nuclear Information System (INIS)

    Vrankić, M.; Gržeta, B.; Mandić, V.; Tkalčec, E.; Milošević, S.; Čeh, M.; Rakvin, B.

    2012-01-01

    Highlights: ► Ti-doped gahnite samples with 0–11.6 at.% Ti were synthesized for the first time. ► The samples had crystallite size of 16.6–20.5 nm and lattice strain of 0.07–0.26%. ► Titanium entered the gahnite structure as Ti 4+ , substituting for octahedral Al 3+ . ► Ti-doped gahnite showed the UV absorption and blue emission under UV excitation. - Abstract: A series of Ti-doped ZnAl 2 O 4 (gahnite) samples with doping levels of 0, 1.8, 3.8, 5.4 and 11.6 at.% Ti in relation to Al were prepared by a sol–gel technique. The samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), EPR spectroscopy, UV–vis reflectance spectroscopy and photoluminescence (PL) studies. Diffraction patterns indicated that all samples were nanocrystalline, with a spinel-type structure, space group Fd3 ¯ m. Titanium doping of gahnite caused an increase of unit-cell parameter and diffraction line broadening. The structure of samples was refined by the Rietveld method, simultaneously with the analysis of diffraction line broadening. TEM investigations confirmed that samples had spinel-type structure, and showed that samples contained evenly shaped particles of about 20 nm in size. Ti-doped samples exhibited strong absorption at wavelength exc = 308 nm.

  9. Transformation from Al3BC phase to doped TiB2 or TiC particles in Al–Ti melts

    International Nuclear Information System (INIS)

    Tian, Wenjie; Li, Pengting; Gao, Tong; Nie, Jinfeng; Liu, Xiangfa

    2013-01-01

    Highlights: ► The reaction of phase Al 3 BC with Ti was investigated. ► The transformation leads to the formation of C-doped TiB 2 and B-doped TiC. ► The doped particles show macroporous and lamellar morphologies. ► A model was proposed to illustrate the transformation mechanism. ► Grain refinement performance of the Al–5Ti–0.8B–0.2C on A356 alloy is excellent. -- Abstract: An Al–8B–2C master alloy was added into Al–Ti melts to study the reaction of Al 3 BC phase with Ti. As a result, a new Al–5Ti–0.8B–0.2C master alloy was fabricated. The microstructures were studied by field emission scanning electron microscope (FESEM), X-ray diffraction (XRD) and transmission electron microscope (TEM). The analysis indicates that C-doped TiB 2 and B-doped TiC which show macroporous and lamellar morphologies are transformed from Al 3 BC. The transformation mechanism is also discussed in this work. Furthermore, the grain refinement performance of the Al–5Ti–0.8B–0.2C on A356 alloy was investigated

  10. Ti-doped hydrogenated diamond like carbon coating deposited by hybrid physical vapor deposition and plasma enhanced chemical vapor deposition

    Science.gov (United States)

    Lee, Na Rae; Sle Jun, Yee; Moon, Kyoung Il; Sunyong Lee, Caroline

    2017-03-01

    Diamond-like carbon films containing titanium and hydrogen (Ti-doped DLC:H) were synthesized using a hybrid technique based on physical vapor deposition (PVD) and plasma enhanced chemical vapor deposition (PECVD). The film was deposited under a mixture of argon (Ar) and acetylene gas (C2H2). The amount of Ti in the Ti-doped DLC:H film was controlled by varying the DC power of the Ti sputtering target ranging from 0 to 240 W. The composition, microstructure, mechanical and chemical properties of Ti-doped DLC:H films with varying Ti concentrations, were investigated using Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), nano indentation, a ball-on-disk tribometer, a four-point probe system and dynamic anodic testing. As a result, the optimum composition of Ti in Ti-doped DLC:H film using our hybrid method was found to be a Ti content of 18 at. %, having superior electrical conductivity and high corrosion resistance, suitable for bipolar plates. Its hardness value was measured to be 25.6 GPa with a low friction factor.

  11. Structural, optical and ferromagnetic properties of Cr doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Choudhury, Biswajit; Choudhury, Amarjyoti

    2013-01-01

    Graphical abstract: Doping of Cr 3+ distorts the lattice of TiO 2 , generate oxygen vacancies and create d-band states in the mid band gap of TiO 2 . Incorporation of Cr 3+ also imparts magnetism in non-magnetic TiO 2 by undergoing coupling with the neighboring oxygen vacancies. -- Highlights: • Incorporation of Cr 3+ increases the concentration of oxygen vacancies in TiO 2 nanoparticles. • Doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ into TiO 2 . • Pure and doped TiO 2 nanoparticles contain emission peaks related to oxygen vacancies. • Pure TiO 2 shows diamagnetism while Cr doped TiO 2 shows ferromagnetism. • The ferromagnetism is due to the interaction of Cr 3+ ions via oxygen vacancies. -- Abstract: Cr doped TiO 2 nanoparticles are prepared with three different concentrations of chromium, 1.5%, 3.0% and 4.5 mol% respectively. Doping decreases the crystallinity and increases the width of the X-ray diffraction peak. The Raman active E g peak of TiO 2 nanoparticles become asymmetric and shifted to higher energy on doping of 4.5% chromium. Electron paramagnetic resonance spectra reveal the presence of Cr 3+ in the host TiO 2 matrix. The absorption spectra of Cr doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ in octahedral coordination. Most of the visible emission peaks are due to the electrons trapped in the oxygen vacancy centers. Undoped TiO 2 nanoparticles show diamagnetism at room temperature while all chromium doped samples show ferromagnetism. The magnetization of the doped samples increases at 1.5% and 3.0% and decreases at 4.5%. The ferromagnetism arises owing to the interaction of the neighboring Cr 3+ ions via oxygen vacancies. The decrease of magnetization at the highest doping is possibly due to the antiferromagnetic interactions of Cr 3+ pairs or due to Cr 3+ -O 2− -Cr 3+ superexchange interaction in the lattice

  12. Electrochemical reduction induced self-doping of Ti3+ for efficient water splitting performance on TiO2 based photoelectrodes

    KAUST Repository

    Zhang, Zhonghai

    2013-01-01

    Hetero-element doping (e.g., N, F, C) of TiO2 is inevitably accompanied by significantly increased structural defects due to the dopants\\' nature being foreign impurities. Very recently, in situ self-doping with homo-species (e.g., Ti3+) has been emerging as a rational solution to enhance TiO2 photoactivity within both UV and visible light regions. Herein we demonstrate that conventional electrochemical reduction is indeed a facile and effective strategy to induce in situ self-doping of Ti3+ into TiO2 and the self-doped TiO2 photoelectrodes showed remarkably improved and very stable water splitting performance. In this study, hierarchical TiO2 nanotube arrays (TiO2 NTs) were chosen as TiO2 substrates and then electrochemically reduced under varying conditions to produce Ti3+ self-doped TiO2 NTs (ECR-TiO2 NTs). The optimized saturation photocurrent density and photoconversion efficiency on the ECR-TiO2 NTs under simulated AM 1.5G illumination were identified to be 2.8 mA cm-2 at 1.23 V vs. RHE and 1.27% respectively, which are the highest values ever reported for TiO 2 based photoelectrodes. The electrochemical impedance spectra measurement confirms that the electrochemical induced Ti3+ self-doping improved the electrical conductivity of the ECR-TiO2 NTs. The versatility and effectiveness of the electrochemical reduction method for Ti3+ self-doping in P25 based TiO2 was also examined and confirmed. This journal is © 2013 the Owner Societies.

  13. Electrochemical Behavior of TiO2 Nanoparticle Doped WO3 Thin Films

    Directory of Open Access Journals (Sweden)

    Suvarna R. Bathe

    2014-01-01

    Full Text Available Nanoparticle TiO2 doped WO3 thin films by pulsed spray pyrolysis technique have been studied on fluorine tin doped (FTO and glass substrate. XRD shows amorphous nature for undoped and anatase phase of TiO2 having (101 plane for nanoparticle TiO2 doped WO3 thin film. SEM shows microfibrous reticulated porous network for WO3 with 600 nm fiber diameter and nanocrystalline having size 40 nm for TiO2 nanoparticle doped WO3 thin film. TiO2 nanoparticle doped WO3 thin film shows ~95% reversibility due to may be attributed to nanocrystalline nature of the film, which helpful for charge insertion and deinsertion process. The diffusion coefficient for TiO2 nanoparticle doped WO3 film is less than undoped WO3.

  14. Synthesis and photocatalytic activity of graphene based doped TiO2 nanocomposites

    International Nuclear Information System (INIS)

    Gu, Yongji; Xing, Mingyang; Zhang, Jinlong

    2014-01-01

    Graphical abstract: - Highlights: • Graphene based doped TiO 2 nanocomposites were prepared. • The intimate contact between doped TiO 2 and graphene is achieved simultaneously. • These nanocomposites showed higher photocatalytic activity than TiO 2 and doped TiO 2 . • Photocatalytic mechanism was explained thoroughly. - Abstract: The nanocomposites of reduced graphene oxide based nitrogen doped TiO 2 (N–TiO 2 –RGO) and reduced graphene oxide based nitrogen and vanadium co-doped TiO 2 (N, V–TiO 2 –RGO) were prepared via a facile hydrothermal reaction of graphene oxide and TiO 2 in a water solvent. In this hydrothermal treatment, the reduction of graphene oxide and the intimate contact between nitrogen doped TiO 2 (N–TiO 2 ) or nitrogen and vanadium co-doped TiO 2 (N,V–TiO 2 ) and the RGO sheet is achieved simultaneously. Both N–TiO 2 –RGO and N,V–TiO 2 –RGO nanocomposites exhibit much higher visible light photocatalytic activity than N–TiO 2 and N,V–TiO 2 , and the order of visible light photocatalytic activity is N,V–TiO 2 –RGO > N–TiO 2 –RGO > N,V–TiO 2 > N–TiO 2 > TiO 2 . According to the characterization, the enhanced photocatalytic activity of the nanocomposites is attributed to reasons, such as enhancement of adsorption of pollutants, light absorption intensity, minimizing the recombination of photoinduced electrons and holes and more excited states of these nanocomposites under visible light irradiation. Overall, this work provides a more marked contrast of graphene based semiconductor nanocomposites and a more comprehensive explanation of the mechanism

  15. The influence of Ti doping and annealing on Ce_2Ti_2O_7 flash memory devices

    International Nuclear Information System (INIS)

    Kao, Chyuan Haur; Chen, Su Zhien; Luo, Yang; Chiu, Wang Ting; Chiu, Shih Wei; Chen, I Chien; Lin, Chan-Yu; Chen, Hsiang

    2017-01-01

    Highlights: • Ce_2Ti_2O_7 flash memories have been fabricated. • Material quality can be improved by annealing. • The memory performance can be enhanced by Ti doping. • Ti doping and annealing can reinforce crystallization. - Abstract: In this research, a CeO_2 film with Ti doping was used as a trapping layer in metal oxide high-K-oxide-Si (MOHOS)-type memory devices. Since incorporation of Ti atoms into the film could fix dangling bonds and defects, the Ce_2Ti_2O_7 trapping layer with annealing treatment could have a larger memory window and a faster programming/erasing speed. To confirm the origin, multiple material analyses indicate that annealing at an appropriate temperature and Ti doping could enhance crystallization. The Ce_2Ti_2O_7-based memory device is promising for future industrial flash memory applications.

  16. The Formation of Lithiated Ti-Doped α-Fe2O3 Nanocrystalline Particles by Mechanical Milling of Ti-Doped Lithium Spinel Ferrite

    International Nuclear Information System (INIS)

    Widatallah, H. M.; Gismelseed, A. M.; Bouziane, K.; Berry, F. J.; Al Rawas, A. D.; Al-Omari, I. A.; Yousif, A. A.; Elzain, M. E.

    2004-01-01

    The milling of spinel-related Ti-doped Li 0.5 Fe 2.5 O 4 for different times is studied with XRD, Moessbauer spectroscopy and magnetic measurements. Milling converts the material to Li-Ti-doped α-Fe 2 O 3 nanocrystalline particles via an intermediate γ-LiFeO 2 -related phase. The role played by the dopant Ti-ion in the process is emphasized.

  17. Characterization and Comparison of Photocatalytic Activity Silver Ion doped on TiO2(TiO2/Ag+) and Silver Ion doped on Black TiO2(Black TiO2/Ag+)

    Science.gov (United States)

    Kim, Jin Yi; Sim, Ho Hyung; Song, Sinae; Noh, Yeoung Ah; Lee, Hong Woon; Taik Kim, Hee

    2018-03-01

    Titanium dioxide (TiO2) is one of the representative ceramic materials containing photocatalyst, optic and antibacterial activity. The hydroxyl radical in TiO2 applies to the intensive oxidizing agent, hence TiO2 is suitable to use photocatalytic materials. Black TiO2was prepared through reduction of amorphous TiO2 conducting under H2 which leads to color changes. Its black color is proven that absorbs 100% light across the whole-visible light, drawing enhancement of photocatalytic property. In this study, we aimed to compare the photocatalytic activity of silver ion doped on TiO2(TiO2/Ag+) and silver ion doped on black TiO2(black TiO2/Ag+) under visible light range. TiO2/Ag+ was fabricated following steps. 1) TiO2 was synthesized by a sol-gel method from Titanium tetraisopropoxide (TTIP). 2) Then AgNO3 was added during an aging process step for silver ion doping on the surface of TiO2. Moreover, Black TiO2/Ag+ was obtained same as TiO2/Ag+ except for calcination under H2. The samples were characterized X-ray diffraction (XRD), UV-visible reflectance (UV-vis DRS), and Methylene Blue degradation test. XRD analysis confirmed morphology of TiO2. The band gap of black TiO2/Ag+ was confirmed (2.6 eV) through UV-vis DRS, which was lower than TiO2/Ag+ (2.9 eV). The photocatalytic effect was conducted by methylene blue degradation test. It demonstrated that black TiO2/Ag+ had a photocatalytic effect under UV light also visible light.

  18. Effect of substrate roughness and working pressure on photocatalyst of N-doped TiOx films prepared by reactive sputtering with air

    International Nuclear Information System (INIS)

    Lee, Seon-Hong; Yamasue, Eiji; Okumura, Hideyuki; Ishihara, Keiichi N.

    2015-01-01

    Highlights: • Effect of substrate roughness and working pressure on the physical properties and the photocatalytic properties of the N-doped TiO x films are investigated. • Surface roughness of glass substrate has little influence on the film properties, but significant influence on the photocatalytic ability. • Working pressure has little influence on the produced phases and the atomic bonding configurations, but significant influence on the atomic concentration of the N-doped TiO x film. • High photocatalysis of N-doped TiO x film requires the permissible range of the N doping concentration which shows the interstitial complex N doping states in TiO 2 . - Abstract: N-doped TiO x films on the glass substrate were prepared by radio-frequency (RF) magnetron reactive sputtering of Ti target in a mixed gas of argon and dry air. The effect of substrate roughness and working pressure on the physical properties and the photocatalytic properties of the N-doped TiO x films was investigated. The surface roughness of glass substrate has little influence on the film properties such as produced phases, lattice parameters, introduced nitrogen contents, and atomic bonding configurations, but significant influence on the surface roughness of film resulting in the variation of the photocatalytic ability. The working pressure has little influence on the produced phases and the atomic bonding configurations, but significant influence on the atomic concentration of the N-doped TiO x film, resulting in the large variation of optical, structural, and photocatalytic properties. It is suggested that the high photocatalysis of N-doped TiO x film requires a certain range of the N doping concentration which shows the interstitial complex N doping states in TiO 2

  19. Synthesis and Photocatalytic Activity of Mo-Doped TiO2 Nanoparticles

    Directory of Open Access Journals (Sweden)

    Ji-guo Huang

    2015-01-01

    Full Text Available The undoped and Mo-doped TiO2 nanoparticles were synthesized by sol-gel method. The as-prepared samples were characterized by X-ray diffraction (XRD, diffuse reflectance UV-visible absorption spectra (UV-vis DRS, X-ray photoelectron spectra (XPS, and transmission electron microscopy (TEM. The photocatalytic activity was evaluated by photocatalytic degradation of methylene blue under irradiation of a 500 W xenon lamp and natural solar light outdoor. Effects of calcination temperatures and Mo doping amounts on crystal phase, crystallite size, lattice distortion, and optical properties were investigated. The results showed that most of Mo6+ took the place of Ti4+ in the crystal lattice of TiO2, which inhibited the growth of crystallite size, suppressed the transformation from anatase to rutile, and led to lattice distortion of TiO2. Mo doping narrowed the band gap (from 3.05 eV of TiO2 to 2.73 eV of TiMo0.02O and efficiently increased the optical absorption in visible region. Mo doping was shown to be an efficient method for degradation of methylene blue under visible light, especially under solar light. When the calcination temperature was 550°C and the Mo doping amount was 2.0%, the Mo-doped TiO2 sample exhibited the highest photocatalytic activity.

  20. Structural, morphological, optical and photocatalytic investigation of Ag-doped TiO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Kundu, Virender Singh; Tanwar, Amit [Department of Electronic Science, Kurukshetra University, Kurukshetra-136119 (India); Singh, Davender, E-mail: Davender-kadian@rediffmail.com; Maan, A. S. [Departments of Physics, Maharshi Dayanand University, Rohtak-124001 (India)

    2016-05-06

    The pure and Ag-doped TiO{sub 2} nanoparticles were prepared by using Titanium isoproxide (TTIP), silver nitrate sodium hydroxide and sodium hydroxide. The calcined nanoparticles at 400°C were characterized by means of X-ray diffraction (XRD). XRD analyses reveal that the nanoparticles of various doping concentration were having anatase phase. The particle size was calculated by Scherrer formula and was found 11.08 nm for pure TiO{sub 2} and 8.86 nm for 6 mol % Ag doped TiO{sub 2}. The morphology and nature of nanoparticles was analyzed by using scanning electron microscope (SEM), the optical absorption spectra of pure TiO{sub 2} and Ag-doped TiO{sub 2} nanoparticles showed that absorption edge increases towards longer wavelength from 390 nm (pure) to 450 nm (doped), also band gap energy calculated from Tauc’s plot decrease from 3.20eV to 2.92eV with increase in doing. The measurement of photocatalytic properties of pure TiO{sub 2} and Ag-doped TiO{sub 2} nanoparticles showed that Ag-doped TiO{sub 2} degrades MB dye more efficiently than pure TiO{sub 2}.

  1. Structural and vibrational investigations of Nb-doped TiO2 thin films

    International Nuclear Information System (INIS)

    Uyanga, E.; Gibaud, A.; Daniel, P.; Sangaa, D.; Sevjidsuren, G.; Altantsog, P.; Beuvier, T.; Lee, Chih Hao; Balagurov, A.M.

    2014-01-01

    Highlights: • We studied the evolutions of structure for TiO 2 thin film as changes with Nb doping and temperatures. • Up to 800 °C, the grain size of Nb 0.1 Ti 0.9 O 2 is smaller than for pure TiO 2 because doped Nb hinders the growth of the TiO 2 grains. • There was no formation of the rutile phase at high temperature. • Nb doped TiO 2 films have high electron densities at 400–700 °C. • Nb dope extends the absorbance spectra of TiO 2 which leads to the band gap reduce. - Abstract: Acid-catalyzed sol–gel and spin-coating methods were used to prepare Nb-doped TiO 2 thin film. In this work, we studied the effect of niobium doping on the structure, surface, and absorption properties of TiO 2 by energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), X-ray reflectometry (XRR), X-ray photoelectron spectroscopy (XPS), Raman, and UV–vis absorption spectroscopy at various annealing temperatures. EDX spectra show that the Nb:Ti atomic ratios of the niobium-doped titania films are in good agreement with the nominal values (5 and 10%). XPS results suggest that charge compensation is achieved by the formation of Ti vacancies. Specific niobium phases are not observed, thus confirming that niobium is well incorporated into the titania crystal lattice. Thin films are amorphous at room temperature and the formation of anatase phase appeared at an annealing temperature close to 400 °C. The rutile phase was not observed even at 900 °C (XRD and Raman spectroscopy). Grain sizes and electron densities increased when the temperature was raised. Nb-doped films have higher electron densities and lower grain sizes due to niobium doping. Grain size inhibition can be explained by lattice stress induced by the incorporation of larger Nb 5+ ions into the lattice. The band gap energy of indirect transition of the TiO 2 thin films was calculated to be about 3.03 eV. After niobium doping, it decreased to 2.40 eV

  2. Photocatalytic activity of Fe-doped CaTiO₃ under UV-visible light.

    Science.gov (United States)

    Yang, He; Han, Chong; Xue, Xiangxin

    2014-07-01

    The photocatalytic degradation of methylene blue (MB) over Fe-doped CaTiO₃ under UV-visible light was investigated. The as-prepared samples were characterized using X-ray diffraction (XRD), scanning electron microscope (SEM) equipped with an energy dispersive spectrometer (EDS) system, Fourier transform infrared spectra (FT-IR), and UV-visible diffuse reflectance spectroscopy (DRS). The results show that the doping with Fe significantly promoted the light absorption ability of CaTiO₃ in the visible light region. The Fe-doped CaTiO₃ exhibited higher photocatalytic activity than CaTiO₃ for the degradation of MB. However, the photocatalytic activity of the Fe-doped CaTiO₃ was greatly influenced by the calcination temperature during the preparation process. The Fe-doped CaTiO₃ prepared at 500°C exhibited the best photocatalytic activity, with degradation of almost 100% MB (10ppm) under UV-visible light for 180 min. Copyright © 2014. Published by Elsevier B.V.

  3. Probing Photocatalytic Characteristics of Sb-Doped TiO2 under Visible Light Irradiation

    Directory of Open Access Journals (Sweden)

    Lingjing Luo

    2014-01-01

    Full Text Available Sb-doped TiO2 nanoparticle with varied dopant concentrations was synthesized using titanium tetrachloride (TiCl4 and antimony chloride (SbCl3 as the precursors. The properties of Sb-doped TiO2 nanoparticles were characterized by X-ray diffraction (XRD, scanning electron microscope (SEM, fluorescence spectrophotometer, and Uv-vis spectrophotometer. The absorption edge of TiO2 nanoparticles could be extended to visible region after doping with antimony, in contrast to the UV absorption of pure TiO2. The results showed that the photocatalytic activity of Sb-doped TiO2 nanoparticles was much more active than pure TiO2. The 0.1% Sb-doped TiO2 nanoparticles demonstrated the best photocatalytic activity which was better than that of the Degussa P25 under visible light irradiation using terephthalic acid as fluorescent probe. The effects of Sb dopant on the photocatalytic activity and the involved mechanism were extensively investigated in this work as well.

  4. The Formation of Lithiated Ti-Doped {alpha}-Fe{sub 2}O{sub 3} Nanocrystalline Particles by Mechanical Milling of Ti-Doped Lithium Spinel Ferrite

    Energy Technology Data Exchange (ETDEWEB)

    Widatallah, H. M., E-mail: hisham@ictp.trieste.it [Khartoum University, Department of Physics (Sudan); Gismelseed, A. M.; Bouziane, K. [Sultan Qaboos University, Department of Physics (Oman); Berry, F. J. [Open University, Department of Chemistry (United Kingdom); Al Rawas, A. D.; Al-Omari, I. A.; Yousif, A. A.; Elzain, M. E. [Sultan Qaboos University, Department of Physics (Oman)

    2004-12-15

    The milling of spinel-related Ti-doped Li{sub 0.5}Fe{sub 2.5}O{sub 4} for different times is studied with XRD, Moessbauer spectroscopy and magnetic measurements. Milling converts the material to Li-Ti-doped {alpha}-Fe{sub 2}O{sub 3} nanocrystalline particles via an intermediate {gamma}-LiFeO{sub 2}-related phase. The role played by the dopant Ti-ion in the process is emphasized.

  5. Synthesis and electrochemical properties of Ti-doped DLC films by a hybrid PVD/PECVD process

    Science.gov (United States)

    Jo, Yeong Ju; Zhang, Teng Fei; Son, Myoung Jun; Kim, Kwang Ho

    2018-03-01

    Low electrical conductivity and poor adhesion to metallic substrates are the main drawbacks of diamond-like carbon (DLC) films when used in electrode applications. In this study, Ti-doped DLC films with various Ti contents were synthesized on metal Ti substrates by a hybrid PVD/PECVD process, where PECVD was used for deposition of DLC films and PVD was used for Ti doping. The effects of the Ti doping ratio on the microstructure, adhesion strength, and electrical and electrochemical properties of the DLC films were systematically investigated. An increase in the Ti content led to increased surface roughness and a higher sp2/sp3 ratio of the Ti-DLC films. Ti atoms existed as amorphous-phase Ti carbide when the Ti doping ratio was less than 2.8 at.%, while the nanocrystalline TiC phase was formed in DLC films when the Ti doping ratio was exceeded 4.0 at.%. The adhesion strength, electrical resistivity, electrochemical activity and reversibility of the DLC films were greatly improved by Ti doping. The influence of Ti doping ratio on the electrical and electrochemical properties of the DLC films were also investigated and the best performance was obtained at a Ti content of 2.8 at.%.

  6. Facile synthesis of the Ti3+ self-doped TiO2-graphene nanosheet composites with enhanced photocatalysis.

    Science.gov (United States)

    Qiu, Bocheng; Zhou, Yi; Ma, Yunfei; Yang, Xiaolong; Sheng, Weiqin; Xing, Mingyang; Zhang, Jinlong

    2015-02-26

    This study developed a facile approach for preparing Ti(3+) self-doped TiO2-graphene photocatalyst by a one-step vacuum activation technology involved a relative lower temperature, which could be activated by the visible light owing to the synergistic effect among Ti(3+) doping, some new intersurface bonds generation and graphene oxide reduction. Compared with the traditional methods, the vacuum activation involves a low temperature and low-costing, which can achieve the reduction of GO, the self doping of Ti(3+) in TiO2 and the loading of TiO2 nanoparticles on GR surface at the same time. These resulting TiO2-graphene composites show the high photodegradation rate of MO, high hydrogen evolution activity and excellent IPCE in the visible light irradiation. The facile vacuum activation method can provide an effective and practical approach to improve the performance of TiO2-graphene and other metal oxides-graphene towards their practical photocatalytic applications.

  7. Morphology and thermal stability of Ti-doped copper nitride films

    International Nuclear Information System (INIS)

    Fan Xiaoyan; Wu Zhiguo; Li Huajun; Geng Baisong; Li Chun; Yan Pengxun

    2007-01-01

    A weakly Ti-doped copper nitride (Cu 3 N) film was prepared by cylindrical magnetron sputtering. The XPS results indicate that Ti atoms do not substitute for the Cu atoms but probably locate at the grain boundaries. The columnar grains size is about half of that of the undoped Cu 3 N film and the surface is smoother. For weakly Ti-doped Cu 3 N films, a dense layer appears on top of the columnar crystals. The RMS of the Cu film formed by annealing of the weakly Ti-doped Cu 3 N film is more than twice larger than that of the film before annealing. Compared with the undoped Cu 3 N film, it possesses fine thermal stability both in vacuum and in atmosphere

  8. Blue photoluminescence in Ti-doped alkaline-earth stannates

    International Nuclear Information System (INIS)

    Yamashita, Takahiro; Ueda, Kazushige

    2007-01-01

    Blue photoluminescence properties of Ti-doped alkaline-earth stannates, A 2 (Sn 1- x Ti x )O 4 (A=Ca, Sr, Ba) (x=0.005-0.15), were examined at room temperature. These stannates showed intense broad emission bands peaking at 445 nm for Ca 2 SnO 4 , at 410 nm for Sr 2 SnO 4 , and at 425 nm for Ba 2 SnO 4 under UV excitation. Emission intensities were relatively insensitive to Ti concentration and no sharp concentration quenching was observed. Mixing alkaline-earth ions in the crystal structures did not increase the emission intensities in the A 2 (Sn 1- x Ti x )O 4 system. The excitation spectra of these stannates exhibited broad bands just below the fundamental absorption edges, implying that luminescence centers do not consist of the component elements in the host materials. It was suggested that the isolated TiO 6 complexes are possible luminescence centers in these materials, as previously proposed in other Ti-doped stannates such as Mg 2 SnO 4 and Y 2 Sn 2 O 7 . - Graphical abstract: Blue photoluminescence properties of Ti-doped alkaline-earth stannates, A 2 (Sn 1- x Ti x )O 4 (A=Ca, Sr, Ba) (x=0.005-0.15), were examined at room temperature. These stannates showed intense broad emission bands peaking at 445 nm for Ca 2 SnO 4 , at 410 nm for Sr 2 SnO 4 , and at 425 nm for Ba 2 SnO 4 under UV excitation

  9. The influence of Ti doping and annealing on Ce{sub 2}Ti{sub 2}O{sub 7} flash memory devices

    Energy Technology Data Exchange (ETDEWEB)

    Kao, Chyuan Haur [Department of Electronic Engineering, Chang Gung University, No. 259, Wenhua 1st Rd., Guishan Dist., Taoyuan City 33302, Taiwan, ROC (China); Kidney Research Center, Department of Nephrology, Chang Gung Memorial Hospital, Chang Gung University, College of Medicine, Taoyuan, Taiwan, ROC (China); Department of Electronic Engineering, Ming Chi University of Technology, Taiwan, ROC (China); Chen, Su Zhien [Department of Electronic Engineering, Chang Gung University, No. 259, Wenhua 1st Rd., Guishan Dist., Taoyuan City 33302, Taiwan, ROC (China); Kidney Research Center, Department of Nephrology, Chang Gung Memorial Hospital, Chang Gung University, College of Medicine, Taoyuan, Taiwan, ROC (China); Luo, Yang; Chiu, Wang Ting; Chiu, Shih Wei; Chen, I Chien [Department of Applied Materials and Optoelectronic Engineering, National Chi Nan University, No. 1, University Rd., Puli, Nantou Country 54561, Taiwan, ROC (China); Lin, Chan-Yu [Kidney Research Center, Department of Nephrology, Chang Gung Memorial Hospital, Chang Gung University, College of Medicine, Taoyuan, Taiwan, ROC (China); Chen, Hsiang, E-mail: hchen@ncnu.edu.tw [Department of Applied Materials and Optoelectronic Engineering, National Chi Nan University, No. 1, University Rd., Puli, Nantou Country 54561, Taiwan, ROC (China)

    2017-02-28

    Highlights: • Ce{sub 2}Ti{sub 2}O{sub 7} flash memories have been fabricated. • Material quality can be improved by annealing. • The memory performance can be enhanced by Ti doping. • Ti doping and annealing can reinforce crystallization. - Abstract: In this research, a CeO{sub 2} film with Ti doping was used as a trapping layer in metal oxide high-K-oxide-Si (MOHOS)-type memory devices. Since incorporation of Ti atoms into the film could fix dangling bonds and defects, the Ce{sub 2}Ti{sub 2}O{sub 7} trapping layer with annealing treatment could have a larger memory window and a faster programming/erasing speed. To confirm the origin, multiple material analyses indicate that annealing at an appropriate temperature and Ti doping could enhance crystallization. The Ce{sub 2}Ti{sub 2}O{sub 7}-based memory device is promising for future industrial flash memory applications.

  10. Effects of donor doping and acceptor doping on rutile TiO2 particles for photocatalytic O2 evolution by water oxidation

    Science.gov (United States)

    Amano, Fumiaki; Tosaki, Ryosuke; Sato, Kyosuke; Higuchi, Yamato

    2018-02-01

    Crystalline defects of photocatalyst particles may be considered to be the recombination center of photoexcited electrons and holes. In this study, we investigated the photocatalytic activity of cation-doped rutile TiO2 photocatalysts for O2 evolution from an aqueous silver nitrate solution under ultraviolet light irradiation. The photocatalytic activity of rutile TiO2 was enhanced by donor doping of Ta5+ and Nb5+ with a valence higher than that of Ti4+, regardless of increased density of electrons and Ti3+ species (an electron trapped in Ti4+ sites). Conversely, acceptor doping of lower valence cations such as In3+ and Ga3+ decreased photocatalytic activity for O2 evolution by water oxidation. The doping of equal valence cations such as Sn4+ and Ge4+ hardly changed the activity of non-doped TiO2. This study demonstrates that Ti3+ species, which is a crystalline defect, enhanced the photocatalytic activity of semiconductor oxides, for example rutile TiO2 with large crystalline size.

  11. Photocatalytic and microwave absorbing properties of polypyrrole/Fe-doped TiO2 composite by in situ polymerization method

    International Nuclear Information System (INIS)

    Li Qiaoling; Zhang Cunrui; Li Jianqiang

    2011-01-01

    Research highlights: → Polypyrrole/Fe-doped TiO 2 composite is prepared by in situ polymerization of pyrrole on the Fe-doped TiO 2 template. → The Fe-doped TiO 2 microbelts are prepared by sol-gel method using the absorbent cotton template for the first time. → Then the Fe-doped TiO 2 microbelts are used as template for the preparation of polypyrrole/Fe-doped TiO 2 composites. → The structure, morphology and properties of the composites are characterized with scanning electron microscope (SEM), IR, Net-work Analyzer. → A possible formation mechanism of Fe-doped TiO 2 microbelts and polypyrrole/Fe-doped TiO 2 composites has been proposed. → The effect of the mol ratio of pyrrole/Fe-doped TiO 2 on the photocatalysis properties and microwave loss properties of the composites is investigated. - Abstract: The Fe-doped TiO 2 microbelts were prepared by sol-gel method using the absorbent cotton template for the first time. Then the Fe-doped TiO 2 microbelts were used as templates for the preparation of polypyrrole/Fe-doped TiO 2 composites. Polypyrrole/Fe-doped TiO 2 composites were prepared by in situ polymerization of pyrrole on the Fe-doped TiO 2 template. The structure, morphology and properties of the composites were characterized with scanning electron microscope (SEM), FTIR, Net-work Analyzer. The possible formation mechanisms of Fe-doped TiO 2 microbelts and polypyrrole/Fe-doped TiO 2 composites have been proposed. The effect of the molar ratio of pyrrole/Fe-doped TiO 2 on the photocatalytic properties and microwave loss properties of the composites was investigated.

  12. Tuning the morphology, stability and photocatalytic activity of TiO2 nanocrystal colloids by tungsten doping

    International Nuclear Information System (INIS)

    Xu, Haiping; Liao, Jianhua; Yuan, Shuai; Zhao, Yin; Zhang, Meihong; Wang, Zhuyi; Shi, Liyi

    2014-01-01

    Graphical abstract: - Highlights: • W 6+ -doped TiO 2 nanocrystal colloids were prepared by hydrothermal methods. • The properties of TiO 2 nanocrystal colloids can be tuned by tungsten doping. • W 6+ -doped TiO 2 nanocrystal colloids show higher stability and dispersity. • W 6+ -doped TiO 2 nanocrystal colloids show higher photocatalytic activity. - Abstract: The effects of tungsten doping on the morphology, stability and photocatalytic activity of TiO 2 nanocrystal colloids were investigated. The nanostructure, chemical state of Ti, W, O, and the properties of tungsten doped TiO 2 samples were investigated carefully by TEM, XRD, XPS, UV–vis, PL and photocatalytic degradation experiments. And the structure–activity relationship was discussed according to the analysis and measurement results. The analysis results reveal that the morphology, zeta potential and photocatalytic activity of TiO 2 nanocrystals can be easily tuned by changing the tungsten doping concentration. The tungsten doped TiO 2 colloid combines the characters of high dispersity and high photocatalytic activity

  13. Hydrothermal synthesis of Fe-doped TiO2 nanostructure photocatalyst

    International Nuclear Information System (INIS)

    Nguyen, Van Nghia; Nguyen, Ngoc Khoa Truong; Nguyen, Phi Hung

    2011-01-01

    Fe-doped TiO 2 catalyst was prepared by the hydrothermal method. The resulting nanopowders were characterized by x-ray diffraction, transmission electron microscopy and Raman and UV-visible spectroscopies. The photocatalytic activity of the Fe-doped TiO 2 was tested by decomposition of methylene orange with a concentration of 10 mg l −1 in aqueous solution. The obtained results showed that methylene orange was significantly degraded after irradiation for 90 min under a halogen lamp and sunlight. The doping effect on the photocatalytic activity of the iron-doped catalyst samples are discussed

  14. Tailoring luminescence properties of TiO2 nanoparticles by Mn doping

    International Nuclear Information System (INIS)

    Choudhury, B.; Choudhury, A.

    2013-01-01

    TiO 2 nanoparticles are doped with three different concentrations of Mn, 2%, 4% and 6% respectively. Absorption edge of TiO 2 is shifted from UV to visible region on amplification of Mn content. Room temperature photoluminescence spectra, excited at 320 nm, exhibit band edge and visible emission peaks associated with self trapped excitons, oxygen defects, etc. Doping of Mn increases the width and decreases the intensity of the UV emission peak. Potential fluctuations of impurities increase the width and auger type non-radiative recombination decreases the intensity of the UV emission peak. The intensity ratio of the UV to defect emission band decreases on doping, indicating degradation of structural quality. Excitation of pure and doped nanoparticles at 390 nm results in Mn 2+ emission peaks at 525 nm and 585 nm respectively. Photoluminescence excitation spectra also indicate the presence of Mn 2+ in the crystalline environment of TiO 2 . The oxygen defects and Mn related impurities act as efficient trap centers and increases the lifetime of the charge carriers. -- Highlights: ► Doping of Mn increases the d-spacing of TiO 2 nanoparticles. ► Characteristic d–d electronic transition of Mn 2+ is observed in the absorption spectra. ► Doping of Mn quenches the UV and visible emission peaks of TiO 2 . ► Photoexcitation at 390 nm generates emission peaks of Mn 2+

  15. Dopant concentration dependent magnetism of Cu-doped TiO{sub 2} nanocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Anitha, B.; Khadar, M. Abdul, E-mail: mabdulkhadar@rediffmail.com [University of Kerala, Centre for Nanoscience and Nanotechnology (India)

    2016-06-15

    Undoped and Cu-doped nanocrystals of TiO{sub 2} having the size range of 8–11 nm were synthesized by peroxide gel method. XRD analysis using Rietveld refinement confirmed anatase phase with a small percentage of rutile content for undoped TiO{sub 2} nanocrystals while a pure anatase phase with preferential growth along [004] direction was observed for nanocrystals of Cu-doped TiO{sub 2}. Variation in the intensity ratios of the XRD peaks of the doped samples compared to that of the undoped sample offered an evidence for the substitutional incorporation of Cu ions in the TiO{sub 2} lattice. The preferential growth of the nanocrystals along the [004] direction was verified using HRTEM analysis. Cu doping extended the optical absorption edge of TiO{sub 2} nanocrystals to the visible spectral region and caused a blue shift and broadening of the E{sub g} (1) Raman active mode of anatase TiO{sub 2}. Undoped TiO{sub 2} sample showed a weak ferromagnetism superimposed on a diamagnetic background while Cu-doped TiO{sub 2} samples exhibited a weak ferromagnetism in the low-field region with a paramagnetic component in the high-field region. The magnetic moment exhibited by the doped samples is interpreted as the resultant of a weak ferromagnetic moment in the low-field region arising from the presence of defects near the surface of TiO{sub 2} nanoparticles or from the interaction of the substituted Cu ions with the oxygen vacancies, and the paramagnetic contribution from the increased Cu dopant concentration near the surface of the particles arising from self-purification mechanism.

  16. Copper doping enhanced the oxidative stress-mediated cytotoxicity of TiO2 nanoparticles in A549 cells.

    Science.gov (United States)

    Ahmad, J; Siddiqui, M A; Akhtar, M J; Alhadlaq, H A; Alshamsan, A; Khan, S T; Wahab, R; Al-Khedhairy, A A; Al-Salim, A; Musarrat, J; Saquib, Q; Fareed, M; Ahamed, M

    2018-05-01

    Physicochemical properties of titanium dioxide nanoparticles (TiO 2 NPs) can be tuned by doping with metals or nonmetals. Copper (Cu) doping improved the photocatalytic behavior of TiO 2 NPs that can be applied in various fields such as environmental remediation and nanomedicine. However, interaction of Cu-doped TiO 2 NPs with human cells is scarce. This study was designed to explore the role of Cu doping in cytotoxic response of TiO 2 NPs in human lung epithelial (A549) cells. Characterization data demonstrated the presence of both TiO 2 and Cu in Cu-doped TiO 2 NPs with high-quality lattice fringes without any distortion. The size of Cu-doped TiO 2 NPs (24 nm) was lower than pure TiO 2 NPs (30 nm). Biological results showed that both pure and Cu-doped TiO 2 NPs induced cytotoxicity and oxidative stress in a dose-dependent manner. Low mitochondrial membrane potential and higher caspase-3 enzyme (apoptotic markers) activity were also observed in A549 cells exposed to pure and Cu-doped TiO 2 NPs. We further observed that cytotoxicity caused by Cu-doped TiO 2 NPs was higher than pure TiO 2 NPs. Moreover, antioxidant N-acetyl cysteine effectively prevented the reactive oxygen species generation, glutathione depletion, and cell viability reduction caused by Cu-doped TiO 2 NPs. This is the first report showing that Cu-doped TiO 2 NPs induced cytotoxicity and oxidative stress in A549 cells. This study warranted further research to explore the role of Cu doping in toxicity mechanisms of TiO 2 NPs.

  17. One-step preparation and photocatalytic performance of vanadium doped TiO2 coatings

    International Nuclear Information System (INIS)

    Vasilić, R.; Stojadinović, S.; Radić, N.; Stefanov, P.; Dohčević-Mitrović, Z.; Grbić, B.

    2015-01-01

    In this paper, we have investigated one-step preparation of vanadium doped TiO 2 coatings formed by plasma electrolytic oxidation (PEO) of titanium in electrolyte containing 10 g/L Na 3 PO 4 ·12H 2 O + 0.5 g/L NH 4 VO 3 . The morphology, phase structure, and elemental composition of the formed coatings were characterized by atomic force microscopy (AFM), x-ray diffraction (XRD), and x-ray photoelectron spectroscopy (XPS) techniques. Ultraviolet–visible diffuse reflectance spectroscopy (UV–Vis DRS) was employed to evaluate the band gap energy of obtained coatings. Vanadium doped TiO 2 coatings are partly crystallized and mainly composed of anatase phase TiO 2 , with up to about 2 wt% of vanadium present in the surface layer of the oxide. The valence band photoelectron spectra and UV–Vis DRS showed that vanadium doped TiO 2 coatings exhibit notable red shift with respect to the pure TiO 2 coatings. The photocatalytic activity was evaluated by monitoring the degradation of methyl orange under simulated sunlight conditions. Photocatalytic activity of vanadium doped TiO 2 coatings increases with PEO time. Prolonged PEO times result in higher roughness of obtained coatings, thus increasing surface area available for methyl orange degradation. Vanadium doped TiO 2 coatings obtained after 180 s of PEO time exhibit the best photocatalytic activity and about 67% of methyl orange is degraded after 12 h of irradiation under simulated sunlight. - Highlights: • One-step preparation of V-doped TiO 2 coatings in 10 g/L Na 3 PO 4 ·12H 2 O + 0.5 g/L NH 4 VO 3 . • Properties of obtained coatings strongly depend on microdischarge characteristics. • Band gap of V-doped TiO 2 coatings is shifted towards red side of the spectrum. • V-doped TiO 2 coatings have better photocatalytic activity than pure TiO 2 . • After 12 h of simulated sunlight irradiation, 67% of methyl orange was decomposed

  18. Enhanced supercapacitor performances using C-doped porous TiO{sub 2} electrodes

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Juanrong [School of Environment and Safety Engineering, Jiangsu University, Zhenjiang 212013 (China); Qiu, Fengxian, E-mail: fxqiuchem@163.com [School of Chemistry and Chemical Engineering, Jiangsu University, Zhenjiang 212013 (China); Zhang, Ying [School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013 (China); Liang, Jianzheng [School of Environment and Safety Engineering, Jiangsu University, Zhenjiang 212013 (China); Zhu, Huijun, E-mail: H.Zhu@cranfieldac.uk [School of Energy, Environmental Technology and Agrifood, Cranfield University, Bedfordshire MK43 0AL (United Kingdom); Cao, Shunsheng [School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013 (China)

    2015-11-30

    Graphical abstract: - Highlights: • A facile, cost-effective strategy was reported to prepare porous anatase TiO{sub 2} materials. • C-doped porous TiO{sub 2} (C/TiO{sub 2}) was in situ synthesized without the addition of carbon precursors. • C/TiO{sub 2} manifested an enhanced capacitance than the commercial P25. - Abstract: Considerable efforts have been paid to develop electrochemical capacitors with energy storage capability in order to meet the demands of multifunctional electronics. Here we report a facile method to fabricate C-doped porous anatase TiO{sub 2}. This technique involves the preparation of monodisperse cationic polystyrene nanoparticles (CPN), following sequential deposition of tetrabutylorthotitanate (TBT), and directly carbonizing of CPN. Interestingly, during the process of carbonizing CPN, a phase transition of TiO{sub 2} will be happened and whist C-doped porous anatase TiO{sub 2} is in situ formed. When this porous C-doped TiO{sub 2} is used as electrode material to prepare electrochemical capacitor, it manifests a higher capacitance than the commercial P25, effectively broadening it potential for many practical applications.

  19. Density functional theory calculations on the adsorption of formaldehyde and other harmful gases on pure, Ti-doped, or N-doped graphene sheets

    International Nuclear Information System (INIS)

    Zhang, Hong-ping; Luo, Xue-gang; Lin, Xiao-yang; Lu, Xiong; Leng, Yang; Song, Hong-tao

    2013-01-01

    Understanding the interaction mechanisms of CO, NO, SO 2 , and HCHO with graphene are important in developing graphene-based sensors for gas detection and removal. In this study, the effects of doped Ti or N atom on the interaction of these gases with graphene were investigated by density functional theory calculations. Analyses of adsorption energy, electron density difference, and density of states indicated that the doped Ti atom could greatly improve the interaction of gas molecules with graphene. The Ti-doped graphene sheet demonstrated selective gas absorption. The order of interaction between the gas molecules and the Ti-doped graphene sheet was as follows: SO 2 > NO > HCHO > CO. By contrast, the N-doped graphene sheet did not exhibit apparent selective gas absorption. These results imply that the Ti-doped graphene sheet is more effective than the N-doped graphene sheet in detecting and removing gas molecules because of its high selectivity.

  20. Density functional theory calculations on the adsorption of formaldehyde and other harmful gases on pure, Ti-doped, or N-doped graphene sheets

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Hong-ping, E-mail: zhp1006@126.com [Engineering Research Center of Biomass Materials, Ministry of Education, School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang, Sichuan 621010 (China); Luo, Xue-gang, E-mail: lxg@swust.edu.cn [Engineering Research Center of Biomass Materials, Ministry of Education, School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang, Sichuan 621010 (China); Lin, Xiao-yang, E-mail: xylin-2004@163.com [Engineering Research Center of Biomass Materials, Ministry of Education, School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang, Sichuan 621010 (China); Lu, Xiong, E-mail: luxiong_2004@163.com [Key Laboratory of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031, Sichuan (China); Leng, Yang, E-mail: meleng@ust.hk [Department of Mechanical Engineering, Hong Kong University of Science and Technology, Kowloon, Hong Kong (China); Song, Hong-tao, E-mail: yinyishushengsht@163.com [Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang 621900 (China)

    2013-10-15

    Understanding the interaction mechanisms of CO, NO, SO{sub 2}, and HCHO with graphene are important in developing graphene-based sensors for gas detection and removal. In this study, the effects of doped Ti or N atom on the interaction of these gases with graphene were investigated by density functional theory calculations. Analyses of adsorption energy, electron density difference, and density of states indicated that the doped Ti atom could greatly improve the interaction of gas molecules with graphene. The Ti-doped graphene sheet demonstrated selective gas absorption. The order of interaction between the gas molecules and the Ti-doped graphene sheet was as follows: SO{sub 2} > NO > HCHO > CO. By contrast, the N-doped graphene sheet did not exhibit apparent selective gas absorption. These results imply that the Ti-doped graphene sheet is more effective than the N-doped graphene sheet in detecting and removing gas molecules because of its high selectivity.

  1. W-doped TiO2 photoanode for high performance perovskite solar cell

    International Nuclear Information System (INIS)

    Liu, Jinwang; Zhang, Jing; Yue, Guoqiang; Lu, Xingwei; Hu, Ziyang; Zhu, Yuejin

    2016-01-01

    Titanium dioxide (TiO 2 ) with dispersed W-doping shows its capability for efficient electron collection from perovskite to TiO 2 in perovskite solar cell. The conduction band (CB) of TiO 2 moves downward (positive shift) with increasing the tungsten (W) content, which enlarges the energy gap between the CB of TiO 2 and the perovskite. Thus, the efficiency of electron injection from perovskite to TiO 2 is increased. Due to the increased electron injection, W-doped TiO 2 (≤0.2% W content) enhances the short-circuit photocurrent (J sc ) of perovskite solar cell and improves the performance of perovskite solar cell. Perovskite solar cell with 0.1% W-doped photoanode obtains the highest power conversion efficiency (η = 10.6%), which shows enhancement by 13% in J sc and by 17% in η, as compared with the undoped TiO 2 perovskite solar cell.

  2. Ti-doped isotropic graphite: A promising armour material for plasma-facing components

    Science.gov (United States)

    García-Rosales, C.; López-Galilea, I.; Ordás, N.; Adelhelm, C.; Balden, M.; Pintsuk, G.; Grattarola, M.; Gualco, C.

    2009-04-01

    Finely dispersed Ti-doped isotropic graphites with 4 at.% Ti have been manufactured using synthetic mesophase pitch 'AR' as raw material. These new materials show a thermal conductivity at room temperature of ˜200 W/mK and flexural strength close to 100 MPa. Measurement of the total erosion yield by deuterium bombardment at ion energies and sample temperatures for which pure carbon shows maximum values, resulted in a reduction of at least a factor of 4, mainly due to dopant enrichment at the surface caused by preferential erosion of carbon. In addition, ITER relevant thermal shock loads were applied with an energetic electron beam at the JUDITH facility. The results demonstrated a significantly improved performance of Ti-doped graphite compared to pure graphite. Finally, Ti-doped graphite was successfully brazed to a CuCrZr block using a Mo interlayer. These results let assume that Ti-doped graphite can be a promising armour material for divertor plasma-facing components.

  3. Ti-doped isotropic graphite: A promising armour material for plasma-facing components

    Energy Technology Data Exchange (ETDEWEB)

    Garcia-Rosales, C. [CEIT and Tecnun (University of Navarra), Paseo de Manuel Lardizabal, 15, E-20018 San Sebastian (Spain)], E-mail: cgrosales@ceit.es; Lopez-Galilea, I.; Ordas, N. [CEIT and Tecnun (University of Navarra), Paseo de Manuel Lardizabal, 15, E-20018 San Sebastian (Spain); Adelhelm, C.; Balden, M. [Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, D-85748 Garching (Germany); Pintsuk, G. [Forschungszentrum Juelich GmbH, EURATOM Association, D-52425 Juelich (Germany); Grattarola, M.; Gualco, C. [Ansaldo Ricerche S.p.A., I-16152 Genoa (Italy)

    2009-04-30

    Finely dispersed Ti-doped isotropic graphites with 4 at.% Ti have been manufactured using synthetic mesophase pitch 'AR' as raw material. These new materials show a thermal conductivity at room temperature of {approx}200 W/mK and flexural strength close to 100 MPa. Measurement of the total erosion yield by deuterium bombardment at ion energies and sample temperatures for which pure carbon shows maximum values, resulted in a reduction of at least a factor of 4, mainly due to dopant enrichment at the surface caused by preferential erosion of carbon. In addition, ITER relevant thermal shock loads were applied with an energetic electron beam at the JUDITH facility. The results demonstrated a significantly improved performance of Ti-doped graphite compared to pure graphite. Finally, Ti-doped graphite was successfully brazed to a CuCrZr block using a Mo interlayer. These results let assume that Ti-doped graphite can be a promising armour material for divertor plasma-facing components.

  4. Ti-doped isotropic graphite: A promising armour material for plasma-facing components

    International Nuclear Information System (INIS)

    Garcia-Rosales, C.; Lopez-Galilea, I.; Ordas, N.; Adelhelm, C.; Balden, M.; Pintsuk, G.; Grattarola, M.; Gualco, C.

    2009-01-01

    Finely dispersed Ti-doped isotropic graphites with 4 at.% Ti have been manufactured using synthetic mesophase pitch 'AR' as raw material. These new materials show a thermal conductivity at room temperature of ∼200 W/mK and flexural strength close to 100 MPa. Measurement of the total erosion yield by deuterium bombardment at ion energies and sample temperatures for which pure carbon shows maximum values, resulted in a reduction of at least a factor of 4, mainly due to dopant enrichment at the surface caused by preferential erosion of carbon. In addition, ITER relevant thermal shock loads were applied with an energetic electron beam at the JUDITH facility. The results demonstrated a significantly improved performance of Ti-doped graphite compared to pure graphite. Finally, Ti-doped graphite was successfully brazed to a CuCrZr block using a Mo interlayer. These results let assume that Ti-doped graphite can be a promising armour material for divertor plasma-facing components.

  5. Enhancement of tributyltin degradation under natural light by N-doped TiO2 photocatalyst

    International Nuclear Information System (INIS)

    Bangkedphol, S.; Keenan, H.E.; Davidson, C.M.; Sakultantimetha, A.; Sirisaksoontorn, W.; Songsasen, A.

    2010-01-01

    Photo-degradation of tributyltin (TBT) has been enhanced by TiO 2 nanoparticles doped with nitrogen (N-doped TiO 2 ). The N-doped catalyst was prepared by a sol-gel reaction of titanium (IV) tetraisopropoxide with 25% ammonia solution and calcined at various temperatures from 300 to 600 deg. C. X-ray diffraction results showed that N-doped TiO 2 remained amorphous at 300 deg. C. At 400 deg. C the anatase phase occurred then transformed to the rutile phase at 600 deg. C. The crystallite size calculated from Scherrer's equation was in the range of 16-51 nm which depended on the calcination temperature. N-doped TiO 2 calcined at 400 deg. C which contained 0.054% nitrogen, demonstrated the highest photocatalytic degradation of TBT at 28% in 3 h under natural light when compared with undoped TiO 2 and commercial photocatalyst, P25-TiO 2 which gave 14.8 and 18% conversion, respectively.

  6. Thermoelectric Properties of the Yttrium-Doped Ceramic Oxide SrTiO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Khan, Tamal Tahsin; Ur, Soon-Chul [Korea National University of Transportation, Chungju (Korea, Republic of)

    2017-01-15

    The doping dependence of the thermoelectric figure of merit, ZT, of the ceramic oxide SrTiO{sub 3} at high temperature has been studied. In this study, yttrium was used as the doping element. A conventional solid-state reaction method was used for the preparation of Y-doped SrTiO{sub 3}. The doping level in SrTiO{sub 3} was controlled to be in the doping range of 2 - 10 mole%. Almost all the yttrium atoms incorporated into the SrTiO{sub 3} provided charge carriers, as was observed by using X-ray diffraction pattern. The relative densities of all the samples varied from 98.53% to 99.45%. The thermoelectric properties, including the electrical conductivity σ, Seebeck coefficient S, thermal conductivity k, and the figure of merit, ZT, were investigated at medium temperatures. The ZT value showed an obvious doping level dependence, in which a value as high as 0.18 is realized at 773 K for a doping of 8 mole%.

  7. Photocatalytic activity of TiO2 doped with boron and vanadium

    International Nuclear Information System (INIS)

    Bettinelli, M.; Dallacasa, V.; Falcomer, D.; Fornasiero, P.; Gombac, V.; Montini, T.; Romano, L.; Speghini, A.

    2007-01-01

    Boron (B)- and vanadium (V)-doped TiO 2 photocatalysts were synthesized using modified sol-gel reaction processes and characterized by X-ray diffraction (XRD), Raman spectroscopy and N 2 physisorption (BET). The photocatalytic activities were evaluated by monitoring the degradation of methylene blue (MB). The results showed that the materials possess high surface area. The addition of B favored the transformation of anatase to rutile, while in the presence of V, anatase was the only phase detected. The MB degradation on V-doped TiO 2 was significantly affected by the preparation method. In fact while the presence of V in the bulk did not influence strongly the photoreactivity under visible irradiation, an increase of surface V doping lead to improved photodegradation of MB. The degradation of MB dye indicated that the photocatalytic activities of TiO 2 increased as the boron doping increased, with high conversion efficiency for 9 mol% B doping

  8. Comparative study of (N, Fe) doped TiO{sub 2} photocatalysts

    Energy Technology Data Exchange (ETDEWEB)

    Larumbe, S., E-mail: silvia.larumbe@unavarra.es [Departamento Física, Universidad Pública de Navarra, Campus de Arrosadia, 31006 Pamplona (Spain); Monge, M. [Departamento de Química, Universidad de la Rioja, Centro de Investigación en Síntesis Química (CISQ), Complejo Científico Tecnológico, 26006 Logroño (Spain); Gómez-Polo, C. [Departamento Física, Universidad Pública de Navarra, Campus de Arrosadia, 31006 Pamplona (Spain)

    2015-02-01

    Highlights: • Fe, N doped TiO{sub 2} nanoparticles were synthesized by sol–gel. • The nitrogen content controlled the mean size of nanoparticles and afterwards the modification of cell parameters with respect the undoped sample. • Both doping elements induced the increase of the anatase-rutile transition temperature. • A red-shift is observed in the absorption spectra with the introduction of both elements. • An improvement of photocatalytic activity is observed with the introduction of nitrogen under UV and Visible light. However for higher concentrations a decrease in kinetic constants was observed as consequence of the oxygen vacancies acting as recombination centers. On the contrary, a deterioration of photocatalytic efficiency is found for the Fe doped samples. • A correlation between magnetic behavior and photocatalytic activity was found. - Abstract: The effect of N and Fe doping on the structural, optical, photocatalytic and magnetic properties of TiO{sub 2} nanoparticles is analyzed. Undoped, N and Fe doped TiO{sub 2} nanoparticles were synthesized by sol–gel method. Titanium tetraisopropoxide (TTIP) was used as the alkoxyde precursor and iron (III) nitrate and urea were the employed precursors to obtain Fe and N doped TiO{sub 2} nanoparticles, respectively. Differential Scanning Calorimetry (DSC) and Thermogravimetrical Analysis (TGA) enabled the analysis of the thermal decomposition process and the final calcination temperature. X-Ray Diffraction patterns of the calcined nanoparticles displayed a monophasic anatase structure in all the samples with mean crystallite diameter around 4–6 nm. The introduction of Fe or N induced a red-shift in the absorption spectra. Such a red-shift is characterized by a decrease in the band-gap energy and the occurrence of an absorption (Urbach) tail in the visible region. Finally, the photocatalytic efficiency was evaluated under UV and Visible light, obtaining an improvement of the kinetic constants in

  9. Improved visible-light photocatalytic activity of TiO2 co-doped with copper and iodine

    Science.gov (United States)

    Dorraj, Masoumeh; Goh, Boon Tong; Sairi, Nor Asrina; Woi, Pei Meng; Basirun, Wan Jefrey

    2018-05-01

    Cu-I-co-doped TiO2 photocatalysts active to visible light absorption were prepared by hydrothermal method and calcined at various temperatures (350 °C, 450 °C, and 550 °C). The co-doped powders at 350 °C displayed the highest experimental Brunauer-Emmett-Teller surface area and lowest photoluminescence intensity, which demonstrated that a decrease in electron-hole recombination process. The synthesis of co-doped TiO2 was performed at this optimized temperature. In the co-doped sample, the Cu2+ doped TiO2 lattice created a major "red-shift" in the absorption edge due to the presence of the 3d Cu states, whereas the amount of red-shift from the I5+ doping in the TiO2 lattice was minor. Interestingly, the presence of Cu2+ species also boosted the reduction of I5+ ions to the lower multi-valance state I- in the TiO2 lattice by trapping the photogenerated electrons, which resulted in effective separation of the photogenerated charges. The Cu-I-co-doped TiO2 was able to degrade methyl orange dye under visible-light irradiation with improved photocatalytic activity compared with the single metal-doped TiO2 and pure TiO2 because of the strong visible light absorption and effective separation of photogenerated charges caused by the synergistic effects of Cu and I co-dopants.

  10. Preparation and Photocatalytic Activity of Nitrogen-doped Nano TiO2/Tourmaline Composites

    Directory of Open Access Journals (Sweden)

    LIU Xin-wei

    2016-06-01

    Full Text Available Using Ti(OC4H94 as precursor, CO(NH22 as nitrogen source, tourmaline as support, the nitrogen-doped nano TiO2/tourmaline composites were synthesized by sol-gel method with ultrasound assisted.The structure and performance of composites were characterized by XRD, FT-IR, UV-Vis DRS, SEM, EDS.The effects of calcining temperature, nitrogen-doped content, tourmaline amount, catalyst system on the photocatalytic activity of nitrogen-doped nano TiO2/tourmaline composites were studied.The results show that the photocatalytic activity of nitrogen-doped nano TiO2/tourmaline composites calcined under 500℃, the nitrogen doped amount of 5% (mole fraction, tourmaline added in an amount of 10% (mass fraction, catalyst dosage of 3g/L, under 500W UV light irradiation conditions, the photocatalytic degradation effect of TNT(10mg/L is the best, and has a good recycling performance.

  11. Electrochemical properties of Ti3+ doped Ag-Ti nanotube arrays coated with hydroxyapatite

    Science.gov (United States)

    Zhang, Hangzhou; Shi, Xiaoguo; Tian, Ang; Wang, Li; Liu, Chuangwei

    2018-04-01

    Ag-Ti nanotube array was prepared by simple anodic oxidation method and uniform hydroxyapatite were electrochemically deposited on the nanotubes, and then characterized by SEM, XRD, XPS and EIS. In order to investigate the influence of Ti3+ on the electrochemical deposition of hydroxyapatite on the nanotubes, the Ag-Ti nanotube array self-doped with Ti3+ was prepared by one step reduction method. The experiment results revealed that the Ti3+ can promote the grow rate of hydroxyapatite coatings on nanotube surface. The hydroxyapatite coated Ag-Ti nanotube arrays with Ti3+ exhibit excellent stability and higher corrosion resistance. Moreover, the compact and dense hydroxyapatite coating can also prevent the Ag atom erosion from the Ag-Ti nanotube.

  12. Electrochemical reduction induced self-doping of Ti3+ for efficient water splitting performance on TiO2 based photoelectrodes

    KAUST Repository

    Zhang, Zhonghai; Hedhili, Mohamed N.; Zhu, Haibo; Wang, Peng

    2013-01-01

    Hetero-element doping (e.g., N, F, C) of TiO2 is inevitably accompanied by significantly increased structural defects due to the dopants' nature being foreign impurities. Very recently, in situ self-doping with homo-species (e.g., Ti3+) has been

  13. Optical spectroscopy of rare earth ion-doped TiO2 nanophosphors.

    Science.gov (United States)

    Chen, Xueyuan; Luo, Wenqin

    2010-03-01

    Trivalent rare-earth (RE3+) ion-doped TiO2 nanophosphors belong to one kind of novel optical materials and have attracted increasing attention. The luminescence properties of different RE3+ ions in various TiO2 nanomaterials have been reviewed. Much attention is paid to our recent progresses on the luminescence properties of RE3+ (RE = Eu, Er, Sm, Nd) ions in anatase TiO2 nanoparticles prepared by a sol-gel-solvothermal method. Using Eu3+ as a sensitive optical probe, three significantly different luminescence centers of Eu3+ in TiO2 nanoparticles were detected by means of site-selective spectroscopy at 10 K. Based on the crystal-field (CF) splitting of Eu3+ at each site, C2v and D2 symmetries were proposed for Eu3+ incorporated at two lattice sites. A structural model for the formation of multiple sites was proposed based on the optical behaviors of Eu3+ at different sites. Similar multi-site luminescence was observed in Sm(3+)- or Nd(3+)-doped TiO2 nanoparticles. In Eu(3+)-doped TiO2 nanoparticles, only weak energy transfer from the TiO2 host to the Eu3+ ions was observed at 10 K due to the mismatch of energy between the TiO2 band-gap and the Eu3+ excited states. On the contrary, efficient host-sensitized luminescences were realized in Sm(3+)- or Nd(3+)-doped anatase TiO2 nanoparticles due to the match of energy between TiO2 band-gap and the Sm3+ and Nd3+ excited states. The excitation spectra of both Sm(3+)- and Nd(3+)-doped samples exhibit a dominant broad peak centered at approximately 340 nm, which is associated with the band-gap of TiO2, indicating that sensitized emission is much more efficient than direct excitation of the Sm3+ and Nd3+ ions. Single lattice site emission of Er3+ in TiO2 nanocrystals can be achieved by modifying the experimental conditions. Upon excitation by a Ti: sapphire laser at 978 nm, intense green upconverted luminescence was observed. The characteristic emission of Er3+ ions was obtained both in the ultraviolet-visible (UV-vis) and

  14. Zirconium doped TiO{sub 2} thin films deposited by chemical spray pyrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Juma, A. [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Department of Physics and Astronomy, Botswana International University of Science and Technology, Private bag 16, Palapye (Botswana); Oja Acik, I., E-mail: ilona.oja@ttu.ee [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Oluwabi, A.T.; Mere, A. [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Mikli, V.; Danilson, M. [Chair of Semiconductor Materials Technology, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Krunks, M. [Laboratory of Thin Film Chemical Technologies, Department of Materials Science, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia)

    2016-11-30

    Highlights: • Mean crystallite size of TiO{sub 2}:Zr film decreases with increasing [Zr] in the solution. • Zr doping supresses the anatase to rutile transformation process in TiO{sub 2} films. • Band gap of TiO{sub 2}:Zr film is 3.4 eV irrespective of the annealing temperature. - Abstract: Chemical spray pyrolysis (CSP) is a flexible deposition technique that allows for mixing of the precursor solutions in different proportions suitable for doping thin films. The CSP method was used to dope TiO{sub 2} thin films with Zr by adding zirconium(IV) acetylacetonate into a solution of titanium(IV) isopropoxide in ethanol stabilized by acetylacetone at [Zr]/[Ti] of 0, 5, 10 and 20 at%. The Zr-doped TiO{sub 2} thin films were uniform and homogeneous showing much smaller grains than the undoped TiO{sub 2} films. Zr stabilized the anatase phase to temperatures above 800 °C depending on Zr concentration in the spray solution. The concentration of Zr determined by XPS was 6.4 at% for the thin film deposited from the 20 at% solution. According to AFM studies, Zr doping decreased the root mean square roughness of TiO{sub 2} film from 5.9 to 1.1 nm. An XRD study of samples with the highest Zr amount showed the ZrTiO{sub 4} phase started forming after annealing at 800 °C. The optical band gap for TiO{sub 2} decreased from 3.3 eV to 3.0 eV after annealing at 800 °C but for the TiO{sub 2}:Zr(20) film it remained at 3.4 eV. The dielectric constant increased by more than four times with Zr-doping and this was associated with the change in the bond formations caused by substitution of Ti by Zr in the lattice.

  15. Active Ti Species in TiCl3-Doped NaAlH4. Mechanism for Catalyst Deactivation

    NARCIS (Netherlands)

    Balde, C.P.; Stil, H.A.; van der Eerden, A.M.J.; de Jong, K.P.; Bitter, J.H.

    2007-01-01

    The nature of the active Ti species in TiCl3-doped NaAlH4, a promising hydrogen storage material, was studied as a function of the desorption temperature with Ti K-edge extended X-ray absorption fine structure (EXAFS) spectroscopy, Ti K-edge X-ray absorption near-edge structure (XANES) spectroscopy,

  16. Y-doping TiO2 nanorod arrays for efficient perovskite solar cells

    Science.gov (United States)

    Deng, Xinlian; Wang, Yanqing; Cui, Zhendong; Li, Long; Shi, Chengwu

    2018-05-01

    To improve the electron transportation in TiO2 nanorod arrays and charge separation in the interface of TiO2/perovskite, Y-doping TiO2 nanorod arrays with the length of 200 nm, diameter of 11 nm and areal density of 1050 μm-2 were successfully prepared by the hydrothermal method and the influence of Y/Ti molar ratios of 0%, 3%, 5% in the hydrothermal grown solutions on the growth of TiO2 nanorod arrays was investigated. The results revealed that the appropriate Y/Ti molar ratios can increase the areal density of the corresponding TiO2 nanorod arrays and improve the charge separation in the interface of the TiO2/perovskite. The Y-doping TiO2 nanorod array perovskite solar cells with the Y/Ti molar ratio of 3% exhibited a photoelectric conversion efficiency (PCE) of 18.11% along with an open-circuit voltage (Voc) of 1.06 V, short-circuit photocurrent density (Jsc) of 22.50 mA cm-2 and fill factor (FF) of 76.16%, while the un-doping TiO2 nanorod array perovskite solar cells gave a PCE of 16.42% along with Voc of 1.04 V, Jsc of 21.66 mA cm-2 and FF of 72.97%.

  17. Influence of VB group doped TiO2 on photovoltaic performance of dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Liu, Jia; Duan, Yandong; Zhou, Xiaowen; Lin, Yuan

    2013-01-01

    Dye-sensitized solar cell with V B group (vanadium (V), niobium (Nb) and tantalum (Ta)) doped TiO 2 prepared by hydrothermal method shows a higher photovoltaic efficiency compared with the undoped TiO 2 . All the V B doping shift the flat band potential positively and increase the doping density which is investigated by Mott–Schottky plot. The positive shift of flat band potential improves the driving force of injecting electron from the LUMO of dye to the conduction band of TiO 2 and the photocurrent. On the other hand, the increase of doping density accelerates transfer rate of electrons in TiO 2 than the un-doped, which is confirmed by intensity-modulated photocurrent. V-, Nb-, Ta-doped TiO 2 exhibited photovoltaic performance with 7.80%, 8.33%, 8.18%, respectively, compared with that of the cells based on pure TiO 2 (7.42%).

  18. Photocatalytic degradation of Rhodamine B dye using Fe doped TiO2 nanocomposites

    Science.gov (United States)

    Barkhade, Tejal; Banerjee, Indrani

    2018-05-01

    The unique properties of titanium dioxide (TiO2) such as high photo catalytic activity, high chemical stability and low toxicity have made it a suitable photocatalyst in recent decades. The effect of modification of TiO2 with doping of iron on its characteristics and photo catalytic efficiency was studied. The change in band gap energy of TiO2 nanoparticles after doping with Fe has been studied. Significant enhancement in photo catalytic property of TiO2 after Fe doping under light exposure conditions has been investigated. Acute exposure to non-biodegradable Rhodamine B resulted in many health problems like burning of eyes, skin irritation, nasal burning, and chest pain etc. Therefore, degradation of this dye is needed to save environment and animals. Considering the similar radius of Fe3+ and Ti4+ ions (respectively 0.64 Å and 0.68 Å), titanium position in the lattice of TiO2 can be replaced by iron cations easily. The undoped and Fe doped TiO2 nano composites were synthesized by sol-gel method, in which 1.0M% of Fe was doped with TiO2 and then the samples were characterized by using FE-SEM, UV-Visible diffuse spectroscopy, Raman Spectroscopy, and FTIR. Photo catalytic degradation of Rhodamine B dye experiment was carried out in visible light range. After 90 min time duration pink colour of dye turned colourless, indicating significant degradation rate with time.

  19. XRD analysis of undoped and Fe doped TiO2 nanoparticles by Williamson Hall method

    International Nuclear Information System (INIS)

    Bharti, Bandna; Barman, P. B.; Kumar, Rajesh

    2015-01-01

    Undoped and Fe doped titanium dioxide (TiO 2 ) nanoparticles were synthesized by sol-gel method at room temperature. The synthesized samples were annealed at 500°C. For structural analysis, the prepared samples were characterized by X-ray diffraction (XRD). The crystallite size of TiO 2 and Fe doped TiO 2 nanoparticles were calculated by Scherer’s formula, and was found to be 15 nm and 11 nm, respectively. Reduction in crystallite size of TiO 2 with Fe doping was observed. The anatase phase of Fe-doped TiO 2 nanoparticles was also confirmed by X-ray diffraction. By using Williamson-Hall method, lattice strain and crystallite size were also calculated. Williamson–Hall plot indicates the presence of compressive strain for TiO 2 and tensile strain for Fe-TiO 2 nanoparticles annealed at 500°C

  20. Improved optical response and photocatalysis for N-doped titanium oxide (TiO2) films prepared by oxidation of TiN

    International Nuclear Information System (INIS)

    Wan, L.; Li, J.F.; Feng, J.Y.; Sun, W.; Mao, Z.Q.

    2007-01-01

    In order to improve the photocatalytic activity, N-doped titanium oxide (TiO 2 ) films were obtained by thermal oxidation of TiN films, which were prepared on Ti substrates by ion beam assisted deposition (IBAD). The dominating rutile TiO 2 phase was found in films after thermal oxidation. According to the results of X-ray photoelectron spectroscopy (XPS), the residual N atoms occupied O-atom sites in TiO 2 lattice to form Ti-O-N bonds. UV-vis spectra revealed the N-doped TiO 2 film had a red shift of absorption edge. The maximum red shift was assigned to the sample annealed at 750 deg. C, with an onset wavelength at 600 nm. The onset wavelength corresponded to the photon energy of 2.05 eV, which was nearly 1.0 eV below the band gap of pure rutile TiO 2 . The effect of nitrogen was responsible for the enhancement of photoactivity of N-doped TiO 2 films in the range of visible light

  1. Synthesis of nano-TiO2 photocatalysts with tunable Fe doping concentration from Ti-bearing tailings

    Science.gov (United States)

    Sui, Yulei; Liu, Qingxia; Jiang, Tao; Guo, Yufeng

    2018-01-01

    In this work, highly pure nano-TiO2 photocatalysts with varying Fe doping concentration were successfully synthesized from low-cost Ti-bearing tailings by an acidolysis-hydrothermal route. The effects of H2SO4 concentration, leaching temperature, acid/tailings ratio and leaching time on the recovery of TiO2 from the tailings were investigated. Synthesized samples were characterized by XRD, TEM, EDS, XPS, and UV-vis spectroscopy. The results showed that the material prepared is characteristic anatase with the average size of 20 nm and the Fe doping concentration in the synthesized nano-TiO2 is tunable. The photocatalytic activity of synthesized nano-TiO2 photocatalyst was also evaluated by the photodegradation of Rhodamine B under visible light and UV light irradiation. Our study demonstrates a low-cost approach to synthesize highly efficient and visible light responsive catalysts.

  2. Decoupling the Lattice Distortion and Charge Doping Effects on the Phase Transition Behavior of VO2 by Titanium (Ti4+) Doping

    Science.gov (United States)

    Wu, Yanfei; Fan, Lele; Liu, Qinghua; Chen, Shi; Huang, Weifeng; Chen, Feihu; Liao, Guangming; Zou, Chongwen; Wu, Ziyu

    2015-01-01

    The mechanism for regulating the critical temperature (TC) of metal-insulator transition (MIT) in ions-doped VO2 systems is still a matter of debate, in particular, the unclear roles of lattice distortion and charge doping effects. To rule out the charge doping effect on the regulation of TC, we investigated Ti4+-doped VO2 (TixV1-xO2) system. It was observed that the TC of TixV1-xO2 samples first slightly decreased and then increased with increasing Ti concentration. X-ray absorption fine structure (XAFS) spectroscopy was used to explore the electronic states and local lattice structures around both Ti and V atoms in TixV1-xO2 samples. Our results revealed the local structure evolution from the initial anatase to the rutile-like structure around the Ti dopants. Furthermore, the host monoclinic VO2 lattice, specifically, the VO6 octahedra would be subtly distorted by Ti doping. The distortion of VO6 octahedra and the variation of TC showed almost the similar trend, confirming the direct effect of local structural perturbations on the phase transition behavior. By comparing other ion-doping systems, we point out that the charge doping is more effective than the lattice distortion in modulating the MIT behavior of VO2 materials. PMID:25950809

  3. One-step preparation and photocatalytic performance of vanadium doped TiO{sub 2} coatings

    Energy Technology Data Exchange (ETDEWEB)

    Vasilić, R., E-mail: rastko.vasilic@ff.bg.ac.rs [University of Belgrade, Faculty of Physics, Studentski trg 12-16, 11000 Belgrade (Serbia); Stojadinović, S. [University of Belgrade, Faculty of Physics, Studentski trg 12-16, 11000 Belgrade (Serbia); Radić, N. [University of Belgrade, Institute of Chemistry, Technology and Metallurgy, Department of Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Stefanov, P. [Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev Str., Block 11, Sofia 1113 (Bulgaria); Dohčević-Mitrović, Z. [University of Belgrade, Institute of Physics, Pregrevica 118, 11080 Belgrade (Serbia); Grbić, B. [University of Belgrade, Institute of Chemistry, Technology and Metallurgy, Department of Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia)

    2015-02-01

    In this paper, we have investigated one-step preparation of vanadium doped TiO{sub 2} coatings formed by plasma electrolytic oxidation (PEO) of titanium in electrolyte containing 10 g/L Na{sub 3}PO{sub 4}·12H{sub 2}O + 0.5 g/L NH{sub 4}VO{sub 3}. The morphology, phase structure, and elemental composition of the formed coatings were characterized by atomic force microscopy (AFM), x-ray diffraction (XRD), and x-ray photoelectron spectroscopy (XPS) techniques. Ultraviolet–visible diffuse reflectance spectroscopy (UV–Vis DRS) was employed to evaluate the band gap energy of obtained coatings. Vanadium doped TiO{sub 2} coatings are partly crystallized and mainly composed of anatase phase TiO{sub 2}, with up to about 2 wt% of vanadium present in the surface layer of the oxide. The valence band photoelectron spectra and UV–Vis DRS showed that vanadium doped TiO{sub 2} coatings exhibit notable red shift with respect to the pure TiO{sub 2} coatings. The photocatalytic activity was evaluated by monitoring the degradation of methyl orange under simulated sunlight conditions. Photocatalytic activity of vanadium doped TiO{sub 2} coatings increases with PEO time. Prolonged PEO times result in higher roughness of obtained coatings, thus increasing surface area available for methyl orange degradation. Vanadium doped TiO{sub 2} coatings obtained after 180 s of PEO time exhibit the best photocatalytic activity and about 67% of methyl orange is degraded after 12 h of irradiation under simulated sunlight. - Highlights: • One-step preparation of V-doped TiO{sub 2} coatings in 10 g/L Na{sub 3}PO{sub 4}·12H{sub 2}O + 0.5 g/L NH{sub 4}VO{sub 3}. • Properties of obtained coatings strongly depend on microdischarge characteristics. • Band gap of V-doped TiO{sub 2} coatings is shifted towards red side of the spectrum. • V-doped TiO{sub 2} coatings have better photocatalytic activity than pure TiO{sub 2}. • After 12 h of simulated sunlight irradiation, 67% of

  4. Novel silver-doped NiTiO3: auto-combustion synthesis ...

    African Journals Online (AJOL)

    ... Ag-NiTiO3 film was directly deposited on top of the TiO2 prepared by electrophoresis deposition method. Furthermore, solar cell result indicates that an inexpensive solar cell could be developed by the synthesized Ag-NiTiO3 nanoparticles. Keywords: Ag-NiTiO3, sol-gel method, semiconductor, photovoltaic, doping ...

  5. Origin of visible-light sensitivity in N-doped TiO2 films

    International Nuclear Information System (INIS)

    Nakano, Yoshitaka; Morikawa, Takeshi; Ohwaki, Takeshi; Taga, Yasunori

    2007-01-01

    We report on visible-light sensitivity in N-doped TiO 2 (TiO 2 :N) films that were deposited on n + -GaN/Al 2 O 3 substrates by reactive magnetron sputtering and subsequently crystallized by annealing at 550 deg. C in flowing N 2 gas. The N-doping concentration was ∼8.8%, as determined by X-ray photoelectron spectroscopy measurements. From transmission electron microscopic observations and optical absorption measurements, yellow-colored TiO 2 :N samples showed an enhanced granular structure and strong absorption in the visible-light region. Photoelectron spectroscopy in air measurements showed a noticeable decrease in ionization energy of TiO 2 by the N doping. Deep-level optical spectroscopy measurements revealed two characteristic deep levels located at ∼1.18 and ∼2.48 eV below the conduction band. The 1.18 eV level is probably attributable to the O vacancy state and can be active as an efficient generation-recombination center. The pronounced 2.48 eV band is newly introduced by the N doping and contributes to band-gap narrowing of TiO 2 by mixing with the O 2p valence band. Therefore, this localized intraband is probably one origin of visible-light sensitivity in TiO 2 :N

  6. Photocatalytic Hydrogen or Oxygen Evolution from Water over S- or N-Doped TiO2 under Visible Light

    Directory of Open Access Journals (Sweden)

    Kazumoto Nishijima

    2008-01-01

    Full Text Available S- or N-doping of TiO2 powder having an anatase or rutile phase extended the photocatalytic activity for water oxidation and reduction under UV light and visible light irradiation. For the reduction of water, anatase-doped TiO2 showed higher level of activity than that of doped TiO2 having a rutile phase using ethanol as an electron donor. Furthermore, the activity level of S-doped TiO2 for hydrogen evolution was higher than that of N-doped TiO2 photocatalysts under visible light. Photocatalytic oxidation of water on doped TiO2 having a rutile phase proceeded with fairly high efficiency when Fe3+ ions were used as electron acceptors compared to that on doped TiO2 having an anatase phase. In addition, water splitting under visible light irradiation was achieved by construction of a Z-scheme photocatalysis system employing the doped TiO2 having anatase and rutile phases for H2 and O2 evolution and the I−/IO3− redox couple as an electron relay.

  7. Flux pinning behaviors of Ti and C co-doped MgB2 superconductors

    International Nuclear Information System (INIS)

    Yang, Y.; Zhao, D.; Shen, T.M.; Li, G.; Zhang, Y.; Feng, Y.; Cheng, C.H.; Zhang, Y.P.; Zhao, Y.

    2008-01-01

    Flux pinning behavior of carbon and titanium concurrently doped MgB 2 alloys has been studied by ac susceptibility and dc magnetization measurements. It is found that critical current density and irreversibility field of MgB 2 have been significantly improved by doping C and Ti concurrently, sharply contrasted to the situation of C-only-doped or Ti-only-doped MgB 2 samples. AC susceptibility measurement reveals that the dependence of the pinning potential on the dc applied field of Mg 0.95 Ti 0.05 B 1.95 C 0.05 has been determined to be U(B dc )∝B dc -1 compared to that of MgB 2 U(B dc )∝B dc -1.5 . As to the U(J) behavior, a relationship of U(J) ∝ J -0.17 is found fitting well for Mg 0.95 Ti 0.05 B 1.95 C 0.05 with respect to U(J) ∝ J -0.21 for MgB 2 . All the results reveal a strong enhancement of the high field pinning potential in C and Ti co-doped MgB 2

  8. Comparative assessment of the efficiency of Fe-doped TiO2 prepared by two doping methods and photocatalytic degradation of phenol in domestic water suspensions

    Directory of Open Access Journals (Sweden)

    Mst. Shamsun Nahar, Kiyoshi Hasegawa, Shigehiro Kagaya and Shigeyasu Kuroda

    2007-01-01

    Full Text Available Fe-doped TiO2 particles responding to visible light were synthesized by impregnation and calcination method using TiO2 particle and Ti element, respectively. The optical and the chemical properties were characterized by measuring the X-ray diffraction (XRD and UV–visible spectroscopy. The onset of absorption shifted to longer wavelengths on doping TiO2 by the calcination process, which showed a better response as compared to the impregnation method. The photocatalytic reactivity was evaluated by the degradation of phenol with impregnated Fe-doped (0.5% w/w in Fe and calcined Fe-doped (FexTi1−xO2, x=0.005 (Fe/Ti molar ratio TiO2 separately in distilled and tap water. The characterization results have confirmed the advanced possibility of correlation between photoactivity and the special property of sulfur-containing calcined Fe-doped TiO2. In case of the coagulation of the undoped A-I and the Fe-doped B-I, the photoactivity showed a decrease due to the presence of natural electrolytes and due to the high pH of tap water, whereas in the case of the coagulation of calcined Fe-doped TiO2 prepared from sulfides (FexTiS2, the photoactivity showed an increase. In this study, highest catalytic activity was found to be strongly dependent both on catalyst structure and on the type of water used.

  9. Investigation of the Optoelectronic Properties of Ti-doped Indium Tin Oxide Thin Film.

    Science.gov (United States)

    Pu, Nen-Wen; Liu, Wei-Sheng; Cheng, Huai-Ming; Hu, Hung-Chun; Hsieh, Wei-Ting; Yu, Hau-Wei; Liang, Shih-Chang

    2015-09-21

    : In this study, direct-current magnetron sputtering was used to fabricate Ti-doped indium tin oxide (ITO) thin films. The sputtering power during the 350-nm-thick thin-film production process was fixed at 100 W with substrate temperatures increasing from room temperature to 500 °C. The Ti-doped ITO thin films exhibited superior thin-film resistivity (1.5 × 10 - ⁴ Ω/cm), carrier concentration (4.1 × 10 21 cm - ³), carrier mobility (10 cm²/Vs), and mean visible-light transmittance (90%) at wavelengths of 400-800 nm at a deposition temperature of 400 °C. The superior carrier concentration of the Ti-doped ITO alloys (>10 21 cm - ³) with a high figure of merit (81.1 × 10 - ³ Ω - ¹) demonstrate the pronounced contribution of Ti doping, indicating their high suitability for application in optoelectronic devices.

  10. Enhancement of Perovskite Solar Cells Efficiency using N-Doped TiO2 Nanorod Arrays as Electron Transfer Layer.

    Science.gov (United States)

    Zhang, Zhen-Long; Li, Jun-Feng; Wang, Xiao-Li; Qin, Jian-Qiang; Shi, Wen-Jia; Liu, Yue-Feng; Gao, Hui-Ping; Mao, Yan-Li

    2017-12-01

    In this paper, N-doped TiO 2 (N-TiO 2 ) nanorod arrays were synthesized with hydrothermal method, and perovskite solar cells were fabricated using them as electron transfer layer. The solar cell performance was optimized by changing the N doping contents. The power conversion efficiency of solar cells based on N-TiO 2 with the N doping content of 1% (N/Ti, atomic ratio) has been achieved 11.1%, which was 14.7% higher than that of solar cells based on un-doped TiO 2 . To get an insight into the improvement, some investigations were performed. The structure was examined with X-ray powder diffraction (XRD), and morphology was examined by scanning electron microscopy (SEM). Energy dispersive spectrometer (EDS) and Tauc plot spectra indicated the incorporation of N in TiO 2 nanorods. Absorption spectra showed higher absorption of visible light for N-TiO 2 than un-doped TiO 2 . The N doping reduced the energy band gap from 3.03 to 2.74 eV. The photoluminescence (PL) and time-resolved photoluminescence (TRPL) spectra displayed the faster electron transfer from perovskite layer to N-TiO 2 than to un-doped TiO 2 . Electrochemical impedance spectroscopy (EIS) showed the smaller resistance of device based on N-TiO 2 than that on un-doped TiO 2 .

  11. Photocatalytic degradation of methyl orange with W-doped TiO2 synthesized by a hydrothermal method

    International Nuclear Information System (INIS)

    Tian Hua; Ma Junfeng; Li Kang; Li Jinjun

    2008-01-01

    Nanosized W-doped TiO 2 photocatalysts were synthesized by a simple hydrothermal method, and characterized by energy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD), transmission electron microscopy (TEM) and BET surface area analyzer. The photocatalytic activity of undoped TiO 2 and W-doped TiO 2 photocatalysts was evaluated by the photocatalytic oxidation degradation of methyl orange in aqueous solution. The results show that the photocatalytic activity of the W-doped TiO 2 photocatalyst is much higher than that of undoped TiO 2 , and the optimum percentage of W doped is 2.0 mol%. The enhanced photocatalytic activity of the doped photocatalyst may be attributed to the increase in the charge separation efficiency and the presence of surface acidity

  12. TiAl doping by vanadium: ab initio study

    International Nuclear Information System (INIS)

    Smirnova, E.A.; Isaev, Eh.I.; Vekilov, Yu.Kh.

    2004-01-01

    Tetragonality degree in TiAl and vanadium doping effect on it were studied using the methods of calculation based on approximation of coherent potential and ab initio pseudopotentials. It is shown that vanadium substitution for Ti sublattice atoms entails increase in tetragonality degree but with substitution of the atoms in aluminium sublattice the tetragonality of the TiAl:V alloy decreases and at the content of vanadium about 8 at. % the lattice becomes actually cubical. In its turn, it may result in increase in TiAl ductility, the alloy being brittle at low temperatures [ru

  13. Dielectric response and room temperature ferromagnetism in Cr doped anatase TiO2 nanoparticles

    Science.gov (United States)

    Naseem, Swaleha; Khan, Wasi; Khan, Shakeel; Husain, Shahid; Ahmad, Abid

    2018-02-01

    In the present work, nanocrystalline samples of Ti1-xCrxO2 (x = 0, 0.02, 0.04, 0.06 and 0.08) were synthesized in anatase phase through simple and cost effective acid modified sol gel method. The influence of Cr doping on thermal, microstructural, electrical and magnetic properties was investigated in TiO2 host matrix. The surface morphology has revealed less agglomeration and considerable reduction in particle size in case of Cr doped TiO2 as compared to undoped TiO2 nanoparticles (NPs). Energy dispersive x-ray spectroscopy (EDS), Raman and X-ray photoelectron spectroscopy (XPS) established high purity, appropriate stoichiometry and oxidation states of the compositions. The dielectric properties of the nanoparticles were altered by the doping concentration, applied frequency as well as temperature variation. The variation in dielectric constant (ε‧), dielectric loss (δ) and ac conductivity as a function of frequency and temperature at different doping concentration of Cr were interpreted in the light of Maxwell Wagner theory, space charge polarization mechanism and drift mobility of charge carriers. Both undoped and Cr doped TiO2 samples exhibit room temperature ferromagnetism (RTFM) that remarkably influenced by means of the Cr content. The significant enhancement in the magnetization was observed at 4% Cr doping. However, decrease in magnetization for higher doping signify antiferromagnetic interactions between Cr ions or superexchange mechanism. These results reveal that the oxygen vacancies play a crucial role to initiate the RTFM. Therefore, the present investigation suggests the potential applications of Cr doped TiO2 nanoparticles for spintronics application.

  14. Microwave-assisted self-doping of TiO2 photonic crystals for efficient photoelectrochemical water splitting

    KAUST Repository

    Zhang, Zhonghai

    2014-01-08

    In this article, we report that the combination of microwave heating and ethylene glycol, a mild reducing agent, can induce Ti3+ self-doping in TiO2. A hierarchical TiO2 nanotube array with the top layer serving as TiO2 photonic crystals (TiO2 NTPCs) was selected as the base photoelectrode. The self-doped TiO2 NTPCs demonstrated a 10-fold increase in visible-light photocurrent density compared to the nondoped one, and the optimized saturation photocurrent density under simulated AM 1.5G illumination was identified to be 2.5 mA cm-2 at 1.23 V versus reversible hydrogen electrode, which is comparable to the highest values ever reported for TiO2-based photoelectrodes. The significant enhancement of photoelectrochemical performance can be ascribed to the rational coupling of morphological and electronic features of the self-doped TiO 2 NTPCs: (1) the periodically morphological structure of the photonic crystal layer traps broadband visible light, (2) the electronic interband state induced from self-doping of Ti3+ can be excited in the visible-light region, and (3) the captured light by the photonic crystal layer is absorbed by the self-doped interbands. © 2013 American Chemical Society.

  15. Phosphorus doped TiO2 as oxygen sensor with low operating temperature and sensing mechanism

    International Nuclear Information System (INIS)

    Han, Zhizhong; Wang, Jiejie; Liao, Lan; Pan, Haibo; Shen, Shuifa; Chen, Jianzhong

    2013-01-01

    Nano-scale TiO 2 powders doped with phosphorus were prepared by sol–gel method. The characterization of the materials was performed by XRD, BET, FT-IR spectroscopy, Zeta potential measurement and XPS analysis. The results indicate that the phosphorus suppresses the crystal growth and phase transformation and, at the same time, increases the surface area and enhances the sensitivity and selectivity for the P-doped TiO 2 oxygen sensors. In this system, the operating temperature is low, only 116 °C, and the response time is short. The spectra of FT-IR and XPS show that the phosphorus dopant presents as the pentavalent-oxidation state in TiO 2 , further phosphorus can connect with Ti 4+ through the bond of Ti-O-P. The positive shifts of XPS peaks indicate that electron depleted layer of P-doped TiO 2 is narrowed compared with that of pure TiO 2 , and the results of Zeta potential illuminate that the density of surface charge carrier is intensified. The adsorptive active site and Lewis acid characteristics of the surface are reinforced by phosphorus doping, where phosphorus ions act as a new active site. Thus, the sensitivity of P-doped TiO 2 is improved, and the 5 mol% P-doped sample has the optimal oxygen sensing properties.

  16. Preparation and photoelectrocatalytic performance of N-doped TiO2/NaY zeolite membrane composite electrode material.

    Science.gov (United States)

    Cheng, Zhi-Lin; Han, Shuai

    2016-01-01

    A novel composite electrode material based on a N-doped TiO2-loaded NaY zeolite membrane (N-doped TiO2/NaY zeolite membrane) for photoelectrocatalysis was presented. X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible (UV-vis) and X-ray photoelectron spectroscopy (XPS) characterization techniques were used to analyze the structure of the N-doped TiO2/NaY zeolite membrane. The XRD and SEM results verified that the N-doped TiO2 nanoparticles with the size of ca. 20 nm have been successfully loaded on the porous stainless steel-supported NaY zeolite membrane. The UV-vis result showed that the N-doped TiO2/NaY zeolite membrane exhibited a more obvious red-shift than that of N-TiO2 nanoparticles. The XPS characterization revealed that the doping of N element into TiO2 was successfully achieved. The photoelectrocatalysis performance of the N-doped TiO2/NaY zeolite membrane composite electrode material was evaluated by phenol removal and also the effects of reaction conditions on the catalytic performance were investigated. Owing to exhibiting an excellent catalytic activity and good recycling stability, the N-doped TiO2/NaY zeolite membrane composite electrode material was of promising application for photoelectrocatalysis in wastewater treatment.

  17. Synergistic effects of F and Fe in co-doped TiO{sub 2} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Yufei, E-mail: zhang.yu.fei@stu.xjtu.edu.cn; Shen, Huiyuan; Liu, Yanhua, E-mail: yhliu@mail.xjtu.edu.cn [Xi’an Jiaotong University, Department of Building Environment and Services Engineering, School of Human Settlements and Civil Engineering (China)

    2016-03-15

    TiO{sub 2} photocatalysts co-doped with F and Fe were synthesized by a sol–gel method. Synergistic effects of F and Fe in the co-doped TiO{sub 2} were verified by NH{sub 3} decomposition, X-ray diffraction (XRD), scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS) and ultraviolet–visible (UV–Vis) absorption spectroscopy, and was analyzed by the simulation based on the density functional theory (DFT). The results from NH{sub 3} decomposition confirmed that the cooperation of F and Fe broadened the optical response of TiO{sub 2} to visible light region and also enhanced the photocatalytic activity of TiO{sub 2} under ultraviolet light. XRD patterns, SEM and HRTEM images showed that the co-doped samples were nanometric anatase with an average particle size of 25 nm. Co-doping with F and Fe inhibited the grain growth of TiO{sub 2} from anatase to rutile and resulted in a larger lattice defect. XPS analysis exhibited that the doped F and Fe atoms were into the TiO{sub 2} lattice. UV–Vis absorption spectra showed that its optical absorption edge was moved up to approximately 617 nm and its ultraviolet absorption was also enhanced. The DFT results indicated that the cooperation of Fe 3d and O 2p orbits narrowed the band gap of TiO{sub 2} and F 2p orbit widened the upper valence bands. The synergistic electron density around F and Fe in co-doped TiO{sub 2} was capable to enhance the photo-chemical stability of TiO{sub 2}.

  18. Synthesis and characterization of Ag doped TiO{sub 2} heterojunction films and their photocatalytic performances

    Energy Technology Data Exchange (ETDEWEB)

    Demirci, Selim, E-mail: selim.demirci@marmara.edu.tr [Marmara University, Department of Metallurgical and Materials Engineering, Kadiköy, 34722 Istanbul (Turkey); Dikici, Tuncay [Izmir Katip Celebi University, Department of Materials Science and Engineering, Cigli, 35620 Izmir (Turkey); Yurddaskal, Metin [Department of Metallurgical and Materials Engineering, Dokuz Eylul University, 35390 Izmir (Turkey); Center for Fabrication and Application of Electronic Materials, Dokuz Eylul University, 35390 Izmir (Turkey); Gultekin, Serdar [Department of Nanoscience and Nanoengineering, Dokuz Eylul University, 35390 İzmir (Turkey); Experimental Science Applications and Research Center, Celal Bayar University, 45140 Manisa (Turkey); Toparli, Mustafa; Celik, Erdal [Department of Metallurgical and Materials Engineering, Dokuz Eylul University, 35390 Izmir (Turkey); Department of Nanoscience and Nanoengineering, Dokuz Eylul University, 35390 İzmir (Turkey); Center for Fabrication and Application of Electronic Materials, Dokuz Eylul University, 35390 Izmir (Turkey)

    2016-12-30

    Highlights: • Ag doped TiO{sub 2} films were successfully synthesized by sol–gel spin coating method. • Ag in TiO{sub 2} lattice enters in intermediate states to decrease TiO{sub 2} bandgap energy. • Ag dopants increase the photoactivity and superhydrophilicity. • The degradation kinetics of methylene blue was studied. • The 0.7 mol% of Ag was found to be the optimum concentration. - Abstract: In this study, undoped and silver (Ag) doped titanium dioxide (TiO{sub 2}) films were successfully synthesized by sol-gel spin coating technique on the Si substrates. Photocatalytic activities of the TiO{sub 2} films with different Ag content were investigated for the degradation of methylene blue (MB) under UV light irradiation. The crystal phase structure, surface morphology, chemical and optical properties of Ag-doped TiO{sub 2} films were characterized using an X-ray diffractometer (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), UV–vis spectrophotometer, and FTIR spectrophotometer. The results showed that the Ag-doped TiO{sub 2} films calcined at 500 °C had the crystalline anatase phases and the surface morphologies with some cracks. Ag substitution into TiO{sub 2} matrix enhanced the photocatalytic activity of TiO{sub 2} films under UV light irradiation as compared to the undoped TiO{sub 2} film. Furthermore, the results indicated that the 0.7% Ag doped TiO{sub 2} film exhibited a superior photocatalytic activity than that of undoped and other Ag-doped TiO{sub 2} films. This study demonstrated the potential of an application of Ag doped films to efficiently treat dissolved organic contaminants in water.

  19. Highly Al-doped TiO2 nanoparticles produced by Ball Mill Method: structural and electronic characterization

    International Nuclear Information System (INIS)

    Santos, Desireé M. de los; Navas, Javier; Sánchez-Coronilla, Antonio; Alcántara, Rodrigo; Fernández-Lorenzo, Concha; Martín-Calleja, Joaquín

    2015-01-01

    Highlights: • Highly Al-doped TiO 2 nanoparticles were synthesized using a Ball Mill Method. • Al doping delayed anatase to rutile phase transformation. • Al doping allow controlling the structural and electronic properties of nanoparticles. - Abstract: This study presents an easy method for synthesizing highly doped TiO 2 nanoparticles. The Ball Mill method was used to synthesize pure and Al-doped titanium dioxide, with an atomic percentage up to 15.7 at.% Al/(Al + Ti). The samples were annealed at 773 K, 973 K and 1173 K, and characterized using ICP-AES, XRD, Raman spectroscopy, FT-IR, TG, STEM, XPS, and UV–vis spectroscopy. The effect of doping and the calcination temperature on the structure and properties of the nanoparticles were studied. The results show high levels of internal doping due to the substitution of Ti 4+ ions by Al 3+ in the TiO 2 lattice. Furthermore, anatase to rutile transformation occurs at higher temperatures when the percentage of doping increases. Therefore, Al doping allows us to control the structural and electronic properties of the nanoparticle synthesized. So, it is possible to obtain nanoparticles with anatase as predominant phase in a higher range of temperature

  20. Investigation of the Optoelectronic Properties of Ti-doped Indium Tin Oxide Thin Film

    Directory of Open Access Journals (Sweden)

    Nen-Wen Pu

    2015-09-01

    Full Text Available : In this study, direct-current magnetron sputtering was used to fabricate Ti-doped indium tin oxide (ITO thin films. The sputtering power during the 350-nm-thick thin-film production process was fixed at 100 W with substrate temperatures increasing from room temperature to 500 °C. The Ti-doped ITO thin films exhibited superior thin-film resistivity (1.5 × 10−4 Ω/cm, carrier concentration (4.1 × 1021 cm−3, carrier mobility (10 cm2/Vs, and mean visible-light transmittance (90% at wavelengths of 400–800 nm at a deposition temperature of 400 °C. The superior carrier concentration of the Ti-doped ITO alloys (>1021 cm−3 with a high figure of merit (81.1 × 10−3 Ω−1 demonstrate the pronounced contribution of Ti doping, indicating their high suitability for application in optoelectronic devices.

  1. Influence of silver doping on surface defect characteristics of TiO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Tripathi, S. K., E-mail: surya@pu.ac.in [Department of Physics, Center of Advanced Study in Physics, Panjab University, Chandigarh-160 014 (India); Rani, Mamta [Department of Physics, Center of Advanced Study in Physics, Panjab University, Chandigarh-160 014 (India); Department of Physics, DAV University Jalandhar, - 144 001, Punjab (India)

    2015-08-28

    In the present work, we proposed a novel silver doped TiO{sub 2} polyethylene conjugated films to improve the performance of DSSCs. Oxides nanoparticles dispersed in a semiconducting polymer form the active layer of a solar cell. Localized surface plasmon resonance effects associated with spatially dispersed silver (Ag) nanoparticles can be exploited to enhance the light-harvesting efficiency, the photocurrent density and the overall light-to electrical-energy-conversion efficiency of high-area DSSCs based TiO{sub 2} photoanodes. Silver doped titanium dioxide (TiO{sub 2}:Ag) is prepared by sol-gel technique and deposited on fluorine doped indium oxide (FTO) coated glass substrates by using doctor blade technique at 550°C from aqueous solutions of titanium butoxide and silver nitrate precursors. The effect of Ag doping on electrical properties of films is studied. The Ag-TiO{sub 2} films are about 548 times more photosensitive as compare to the pure TiO{sub 2} sample. The presence of metallic Ag nanoparticles and oxygen vacancy on the surface of TiO{sub 2} nanoparticles promotes the separation of photogenerated electron-hole pairs and thus enhances the photosensitivity. Photoconduction mechanism of all prepared samples is investigated by performing transient photoconductivity measurements on TiO{sub 2} and Ag-TiO{sub 2} films keeping intensity of light constant.

  2. Photocatalysis with chromium-doped TiO2: Bulk and surface doping

    KAUST Repository

    Ould-Chikh, Samy; Proux, Olivier; Afanasiev, Pavel V.; Khrouz, Lhoussain; Hedhili, Mohamed N.; Anjum, Dalaver H.; Harb, Moussab; Geantet, Christophe; Basset, Jean-Marie; Puzenat, Eric

    2014-01-01

    The photocatalytic properties of TiO2 modified by chromium are usually found to depend strongly on the preparation method. To clarify this problem, two series of chromium-doped titania with a chromium content of up to 1.56 wt % have been prepared

  3. Enhancement of tributyltin degradation under natural light by N-doped TiO{sub 2} photocatalyst

    Energy Technology Data Exchange (ETDEWEB)

    Bangkedphol, S., E-mail: sornnarin.bangkedphol@strath.ac.uk [David Livingstone Centre for Sustainability, Department of Civil Engineering, University of Strathclyde, Glasgow, Scotland G1 1XN (United Kingdom); Keenan, H.E. [David Livingstone Centre for Sustainability, Department of Civil Engineering, University of Strathclyde, Glasgow, Scotland G1 1XN (United Kingdom); Davidson, C.M. [WestCHEM, Department of Pure and Applied Chemistry, University of Strathclyde, Glasgow, Scotland G1 1XL (United Kingdom); Sakultantimetha, A. [David Livingstone Centre for Sustainability, Department of Civil Engineering, University of Strathclyde, Glasgow, Scotland G1 1XN (United Kingdom); Sirisaksoontorn, W.; Songsasen, A. [Department of Chemistry and Centre for Innovation in chemistry, Faculty of Science, Kasetsart University, Bangkok 10900 (Thailand)

    2010-12-15

    Photo-degradation of tributyltin (TBT) has been enhanced by TiO{sub 2} nanoparticles doped with nitrogen (N-doped TiO{sub 2}). The N-doped catalyst was prepared by a sol-gel reaction of titanium (IV) tetraisopropoxide with 25% ammonia solution and calcined at various temperatures from 300 to 600 deg. C. X-ray diffraction results showed that N-doped TiO{sub 2} remained amorphous at 300 deg. C. At 400 deg. C the anatase phase occurred then transformed to the rutile phase at 600 deg. C. The crystallite size calculated from Scherrer's equation was in the range of 16-51 nm which depended on the calcination temperature. N-doped TiO{sub 2} calcined at 400 deg. C which contained 0.054% nitrogen, demonstrated the highest photocatalytic degradation of TBT at 28% in 3 h under natural light when compared with undoped TiO{sub 2} and commercial photocatalyst, P25-TiO{sub 2} which gave 14.8 and 18% conversion, respectively.

  4. Hydrazine-based synergistic Ti(III)/N doping of surfactant-templated TiO{sub 2} thin films for enhanced visible light photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Islam, Syed Z.; Rankin, Stephen E., E-mail: srankin@engr.uky.edu

    2016-10-01

    This study reports the preparation of titanium (Ti{sup 3+}) and nitrogen co-doped cubic ordered mesoporous TiO{sub 2} thin films using N{sub 2}H{sub 4} treatment. The resulting co-doped TiO{sub 2} (Ti{sup 3+}-N-TiO{sub 2}) thin films show significant enhancements in visible light absorption and photocatalytic activity. Cubic ordered mesoporous TiO{sub 2} thin films were prepared via a sol-gel method with Pluronic F127 as the pore template. After brief calcination, the TiO{sub 2} films were dipped into hydrazine hydrate which acts both as a nitrogen source and as a reducing agent, followed by heating at low temperature (90 °C). The hydrazine treatment period was varied from 5 to 20 h to obtain different degrees of reduction and nitrogen doping. X-ray photoelectron spectroscopy (XPS) analyses and UV–vis absorbance spectra of Ti{sup 3+}-N-TiO{sub 2} films indicate that the incorporated N atoms and Ti{sup 3+} reduce the band gap of TiO{sub 2} and thus enhance the absorption of visible light. The corresponding visible light photocatalytic activity of Ti{sup 3+}-N-TiO{sub 2} films was determined from the photocatalytic degradation of methylene blue under visible light illumination (at 455 nm). The Ti{sup 3+}-N-TiO{sub 2} films prepared with 10 h of treatment show the optimum photocatalytic activity, with a pseudo-first order rate coefficient of 0.12 h{sup −1}, which is 3 times greater than that of undoped TiO{sub 2} films. Calcination temperature and time were varied prior to hydrazine treatment to confirm that a brief calcination at low temperature (10 min at 350 °C) gave the best photochemical activity. In photoelectrochemical water oxidation using a 455 nm LED, the Ti{sup 3+}-N-TiO{sub 2} films prepared with 10 h of N{sub 2}H{sub 4} treatment show about 4 times the photocurrent compared to undoped TiO{sub 2} films. The present study suggests that hydrazine induced doping is a promising approach to enable synergistic incorporation of N and Ti{sup 3+} into the

  5. Enhanced visible light photocatalytic degradation of methylene blue by F-doped TiO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Wei [Engineering Research Center for Nanophotonics and Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 (China); Liu, Xinjuan, E-mail: lxj669635@126.com [Shanghai Nanotechnlogy Promotion Center, Shanghai 200237 (China); Center for Coordination Bond and Electronic Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Pan, Likun, E-mail: lkpan@phy.ecnu.edu.cn [Engineering Research Center for Nanophotonics and Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 (China); Li, Jinliang; Liu, Junying [Engineering Research Center for Nanophotonics and Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 (China); Zhang, Jing; Li, Ping; Chen, Chen [Shanghai Nanotechnlogy Promotion Center, Shanghai 200237 (China); Sun, Zhuo [Engineering Research Center for Nanophotonics and Advanced Instrument, Ministry of Education, Department of Physics, East China Normal University, Shanghai 200062 (China)

    2014-11-15

    Graphical abstract: F-doped TiO2 is synthesized using a modified sol–gel method for visible photocatalytic degradation of MB with a high degradation rate of 91%. - Highlights: • F-doped TiO{sub 2} are synthesized using a modified sol–gel method. • The photocatalytic degradation of methylene blue by F-doped TiO{sub 2} is investigated. • A high methylene blue degradation rate of 91% is achieved under visible light irradiation. - Abstract: F-doped TiO{sub 2} (F-TiO{sub 2}) were successfully synthesized using a modified sol–gel method. The morphologies, structures, and photocatalytic performance in the degradation of methylene blue (MB) were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV–vis absorption spectroscopy, and electrochemical impedance spectra, respectively. The results show that F-TiO{sub 2} exhibits an enhanced photocatalytic performance in the degradation of MB with a maximum degradation rate of 91% under visible light irradiation as compared with pure TiO{sub 2} (32%). The excellent photocatalytic activity is due to the contribution from the increased visible light absorption, promoted separation of photo-generated electrons and holes as well as enhanced photocatalytic oxidizing species with the doping of F in TiO{sub 2}.

  6. Synthesis of Nd3+doped TiO2 nanoparticles and Its Optical Behaviour

    Directory of Open Access Journals (Sweden)

    Ezhil Arasi S.

    2017-04-01

    Full Text Available Pure and Rare earth ion doped TiO2 nanoparticles were synthesized by Sol-gel method. The synthesized TiO2 nanoparticles were characterized by X-ray diffraction, Raman spectroscopy, UV–Vis spectroscopy and photoluminescence emission spectra. From the UV-visible measurement, the absorption edge of Nd3+-TiO2 was shifted to a higher wavelength side with decreasing band gap. Photoluminescence emission studies reveal the energy transfer mechanism of Nd3+ doped TiO2 nanoparticles explain.

  7. Advanced LiTi2(PO4)3@N-doped carbon anode for aqueous lithium ion batteries

    International Nuclear Information System (INIS)

    He, Zhangxing; Jiang, Yingqiao; Meng, Wei; Zhu, Jing; Liu, Yang; Dai, Lei; Wang, Ling

    2016-01-01

    Highlights: • LiTi 2 (PO 4 ) 3 @N-doped carbon anode was prepared by in-situ coating approach for aqueous lithium ion batteries. • The well-proportioned N-doped carbon layer and loose nanoporous structure was obtained using urea as nitrogen source and pore former. • LiTi 2 (PO 4 ) 3 @N-doped carbon demonstrates excellent rate performance and good cycling stability. - Abstract: In this paper, LiTi 2 (PO 4 ) 3 @N-doped carbon anode has been synthesized by in situ carbon coating approach. The well-proportioned N-doped carbon layer and loose nanoporous structure was obtained by using urea as nitrogen source and pore former. LiTi 2 (PO 4 ) 3 @N-doped carbon as anode demonstrates much better rate capability than LiTi 2 (PO 4 ) 3 @carbon in ALIBs. The optimized anode delivers the discharge capacity of 93.7 mAh g −1 and 74.2 mAh g −1 at rates of 10C and 20C, 22.5 mAh g −1 and 50.0 mAh g −1 larger than that of LiTi 2 (PO 4 ) 3 @carbon. Moreover, LiTi 2 (PO 4 ) 3 @N-doped carbon exhibits excellent cycling performance with capacity retention of 84.3% at 5C after 1000 cycles. As verified, the well-proportioned N-doped carbon layer could reduce charge transfer resistance and improve electrical conductivity. The loose nanoporous structure could shorten pathway and facilitate diffusion for Li ion. Therefore, LiTi 2 (PO 4 ) 3 @N-doped carbon gets the superior electrochemical properties benefiting from those two characteristics.

  8. Preparation and spectroscopic characterization of visible light sensitized N doped TiO2 (rutile)

    International Nuclear Information System (INIS)

    Livraghi, S.; Czoska, A.M.; Paganini, M.C.; Giamello, E.

    2009-01-01

    Nitrogen doped TiO 2 represents one of the most promising material for photocatalitic degradation of environmental pollutants with visible light. However, at present, a great deal of activity is devoted to the anatase polymorph while few data about rutile are available. In the present paper we report an experimental characterization of N doped polycrystalline rutile TiO 2 prepared via sol-gel synthesis. Nitrogen doping does not affect the valence band to conduction band separation but, generates intra band gap localized states which are responsible of the on set of visible light absorption. The intra band gap states correspond to a nitrogen containing defect similar but not coincident with that recently reported for N doped anatase. - Graphical abstract: Nitrogen doped TiO 2 represents one of the most promising material for photocatalitic degradation of environmental pollutants with visible light. However, at present, a great deal of activity is devoted to the anatase polymorph while few data about rutile are available. In the present paper we report an experimental characterization of N doped polycrystalline rutile TiO 2 prepared via sol-gel synthesis

  9. C, N co-doped TiO_2/TiC_0_._7N_0_._3 composite coatings prepared from TiC_0_._7N_0_._3 powder using ball milling followed by oxidation

    International Nuclear Information System (INIS)

    Hao, Liang; Wang, Zhenwei; Zheng, Yaoqing; Li, Qianqian; Guan, Sujun; Zhao, Qian; Cheng, Lijun; Lu, Yun; Liu, Jizi

    2017-01-01

    Highlights: • TiO_2/TiC_0_._7N_0_._3 coatings were prepared by ball milling followed by oxidation. • In situ co-doping of C and N with simultaneous TiO_2 formation was observed. • Improved photocatalytic activity under UV/visible light was noticed. • Synergism in co-doping and heterojunction formation promoted carrier separation. - Abstract: Ball milling followed by heat oxidation was used to prepared C, N co-doped TiO_2 coatings on the surfaces of Al_2O_3 balls from TiC_0_._7N_0_._3 powder. The as-prepared coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible spectrophotometer (UV–vis). The results show that continuous TiC_0_._7N_0_._3 coatings were formed after ball milling. C, N co-doped TiO_2/TiC_0_._7N_0_._3 composite coatings were prepared after the direct oxidization of TiC_0_._7N_0_._3 coatings in the atmosphere. However, TiO_2 was hardly formed in the surface layer of TiC_0_._7N_0_._3 coatings within a depth less than 10 nm during the heat oxidation of TiC_0_._7N_0_._3 coatings in carbon powder. Meanwhile, the photocatalytic activity evaluation of these coatings was conducted under the irradiation of UV and visible light. All the coatings showed photocatalytic activity in the degradation of MB no matter under the irradiation of UV or visible light. The C, N co-doped TiO_2/TiC_0_._7N_0_._3 composite coatings showed the most excellent performance. The enhancement under visible light irradiation should attribute to the co-doping of carbon and nitrogen, which enhances the absorption of visible light. The improvement of photocatalytic activity under UV irradiation should attribute to the synergistic effect of C, N co-doping, the formation of rutile-anatase mixed phases and the TiO_2/TiC_0_._7N_0_._3 composite microstructure.

  10. Effect of zinc doping on the bandgap and photoluminescence of Zn2+-doped TiO2 nanowires

    Science.gov (United States)

    Loan, Trinh Thi; Huong, Vu Hoang; Tham, Vu Thi; Long, Nguyen Ngoc

    2018-03-01

    This study was focused on the effect of Zn2+ dopant concentration on the absorption edge and photoluminescence of anatase TiO2 nanowires synthesized by hydrothermal technique. For the undoped anatase TiO2 nanowires, the indirect band gap of 3.26 eV and the direct band gap of 3.58 eV are assigned to the indirect Γ3 → X1b and direct X2b → X1b transitions, respectively. The Zn2+-doping makes the absorption edge of TiO2:Zn2+ nanowires shift towards the lower energy side (red shift). On the other hand, the replacing Ti4+ ions with Zn2+ ions creates oxygen vacancies (VO) and shallow defects associated with VO. Just these defects are responsible for the enhanced luminescence of Zn2+-doped TiO2 nanowires.

  11. Co-doping TiO{sub 2} with boron and/or yttrium elements: Effects on antimicrobial activity

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Yuzheng [School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870 (China); Wu, Yusheng, E-mail: henanwys@sina.com [School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870 (China); Yang, He; Xue, Xiangxin; Liu, Zhihua [Institute of Metallurgical Resources and Environmental Engineering, Northeastern University, Shenyang 110819 (China)

    2016-09-15

    Highlights: • B-Y/TiO{sub 2} nano materials firstly applied to the fields of antibacterial materials. • Systems analysis the existence state of boron and yttrium ion in TiO{sub 2}. • Doping B and Y greatly strengthened the antibacterial activity of TiO{sub 2}. - Abstract: Pure TiO{sub 2}, boron and/or yttrium doped TiO{sub 2} nano-materials were synthesized by a sol–gel method and characterized by XRD, SEM, XPS and PL. XRD analysis indicates that, in the pure TiO{sub 2} and B single doped TiO{sub 2} (B-TiO{sub 2}) nano-materials calcinated at 700 °C, the presence of TiO{sub 2} is a mixture of anatase and rutile; in the Y single doped (Y-TiO{sub 2}), B and Y co-doped TiO{sub 2} nano-materials (B/Y-TiO{sub 2}), the presence of TiO{sub 2} is anatase. SEM image shows the prepared materials have a common round morphology and hexagonal plate morphology caused by the agglomeration of particles. Boron atoms are partially embedded into the TiO{sub 2} interstitial structure or incorporated into the TiO{sub 2} lattice through occupying the position of the oxygen atoms. The results of antimicrobial experiment show that B/Y-TiO{sub 2} material has a remarkable antimicrobial activity. Compared with the visible light irradiation, antimicrobial activity of B/Y-TiO{sub 2} in dark is significant poor.

  12. Study of Sn and Mg doping effects on TiO2/Ge stack structure by combinatorial synthesis

    Science.gov (United States)

    Nagata, Takahiro; Suzuki, Yoshihisa; Yamashita, Yoshiyuki; Ogura, Atsushi; Chikyow, Toyohiro

    2018-04-01

    The effects of Sn and Mg doping of a TiO2 film on a Ge substrate were investigated to improve leakage current properties and Ge diffusion into the TiO2 film. For systematic analysis, dopant-composition-spread TiO2 samples with dopant concentrations of up to 20.0 at. % were fabricated by RF sputtering and a combinatorial method. X-ray photoelectron spectroscopy revealed that the instability of Mg doping of TiO2 at dopant concentrations above 10.5 at. %. Both Sn and Mg dopants reduced Ge diffusion into TiO2. Sn doping enhanced the crystallization of the rutile phase, which is a high-dielectric-constant phase, although the Mg-doped TiO2 film indicated an amorphous structure. Sn-doping indicated systematic leakage current reduction with increasing dopant concentration. Doping at Sn concentrations higher than 16.8 at. % improved the leakage properties (˜10-7 A/cm2 at -3.0 V) and capacitance-voltage properties of metal-insulator-semiconductor (MIS) operation. The Sn doping of TiO2 may be useful for interface control and as a dielectric material for Ge-based MIS capacitors.

  13. Application of nitrogen-doped TiO2 nano-tubes in dye-sensitized solar cells

    DEFF Research Database (Denmark)

    Tran, Vy Anh; Thinh Troung, Trieu; Pham Phan, Thu Anh

    2017-01-01

    Our research aimed to improve the overall energy conversion efficiency of DSCs by applying nitrogen-doped TiO2 nano-tubes (N-TNT) for the preparation of DSCs photo-anodes. The none-doped TiO2 nano-tubes (TNTs) were synthesized by alkaline hydrothermal treatment of Degussa P25 TiO2 particles in 10...

  14. Application of nitrogen-doped TiO{sub 2} nano-tubes in dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Tran, Vy Anh; Truong, Trieu Thinh; Phan, Thu Anh Pham; Nguyen, Trang Ngoc [Faculty of Chemistry, University of Science, Vietnam National University, Ho Chi Minh City (Viet Nam); Huynh, Tuan Van [Faculty of Physics and Engineering Physics, University of Science, Vietnam National University, Ho Chi Minh City (Viet Nam); Agresti, Antonio; Pescetelli, Sara [CHOSE (Centre for Hybrid and Organic Solar Energy), Department of Electronic Engineering, University of Rome Tor Vergata (Italy); Le, Tien Khoa [Faculty of Chemistry, University of Science, Vietnam National University, Ho Chi Minh City (Viet Nam); Di Carlo, Aldo [CHOSE (Centre for Hybrid and Organic Solar Energy), Department of Electronic Engineering, University of Rome Tor Vergata (Italy); Lund, Torben [Department of Science and Environment, Roskilde University, DK-4000 (Denmark); Le, So-Nhu [Faculty of Chemistry, University of Science, Vietnam National University, Ho Chi Minh City (Viet Nam); Nguyen, Phuong Tuyet, E-mail: ngtuyetphuong@gmail.com [Faculty of Chemistry, University of Science, Vietnam National University, Ho Chi Minh City (Viet Nam)

    2017-03-31

    Highlights: • N-doped TiO{sub 2} nanotubes are synthesized by alkaline hydrothermal and reflux method. • Formation of TiO{sub 2} nanotube morphology and anatase phase is shown by TEM, XRD, Raman. • Coordination of NH{sub 4}{sup +} via Ti−O−NH{sub 4}{sup +} or H{sub 4}N{sup +}−Ti−O bonds is indicated by FT-IR and XPS. • Blocking effect of N-doped toward electron transfer on TiO{sub 2} anode is studied by CV. • N-doped TiO{sub 2} improved DSC performance up to 30–40% mainly due to an increase in J{sub sc}. - Abstract: Our research aimed to improve the overall energy conversion efficiency of DSCs by applying nitrogen-doped TiO{sub 2} nano-tubes (N-TNT) for the preparation of DSCs photo-anodes. The none-doped TiO{sub 2} nano-tubes (TNTs) were synthesized by alkaline hydrothermal treatment of Degussa P25 TiO{sub 2} particles in 10 M NaOH. The nano-tubes were N-doped by reflux in various concentrations of NH{sub 4}NO{sub 3}. The effects of nitrogen doping on the structure, morphology, and crystallography of N-TNT were analyzed by transmission electron microscopy (TEM), infrared spectroscopy (IR), Raman spectroscopy, and X-ray photoelectron spectra (XPS). DSCs fabricated with doped N-TNT and TNT was characterized by J-V measurements. Results showed that nitrogen doping significantly enhanced the efficiency of N-TNT cells, reaching the optimum value (η = 7.36%) with 2 M nitrogen dopant, compared to η = 4.75% of TNT cells. The high efficiency of the N-TNT cells was attributed to increased current density due to the reduction of dark current in the DSCs.

  15. Structural, optical, and magnetic properties of polycrystalline Co-doped TiO2 synthesized by solid-state method

    International Nuclear Information System (INIS)

    Bouaine, Abdelhamid; Schmerber, G.; Ihiawakrim, D.; Derory, A.

    2012-01-01

    Highlights: ► Influence of Co doping on the TiO 2 tetragonal structure. ► Decrease of the energy band gap after doping with Co atoms. ► Appearance of ferromagnetism in Co-doped TiO 2 diluted magnetic semiconductors. - Abstract: We have used a solid-state method to synthesize polycrystalline Co-doped TiO 2 diluted magnetic semiconductors (DMSs) with Co concentrations of 0, and 0.5 at.%. X-ray diffraction patterns reveal that Co doped TiO 2 crystallizes in the rutile tetragonal structure with no additional peaks. Transmission electron microscopy (TEM) did not indicate the presence of magnetic parasitic phases and confirmed that Co ions are uniformly distributed inside the samples. Optical absorbance measurements showed an energy band gap which decreases after doping with the Co atoms into the TiO 2 matrix. Magnetization measurements revealed a paramagnetic behavior for the as-prepared Co-doped TiO 2 and a ferromagnetic behavior for the same samples after annealed under a mixture of H 2 /N 2 atmosphere.

  16. Effect of Ce Doping on RGO-TiO2 Nanocomposite for High Photoelectrocatalytic Behavior

    Directory of Open Access Journals (Sweden)

    Md. Rakibul Hasan

    2014-01-01

    Full Text Available Ce doped RGO-TiO2 composite films on ITO substrates were prepared by sol-gel process using tetrabutyl titanate and reduced graphene oxide (RGO as the starting materials. The sample was designed for the photoelectrocatalytic applications. The obtained samples were characterized by X-ray diffraction, UV-vis absorption spectroscopy, scanning electron microscopy, and Fourier transformed infrared spectroscopy. The results showed that doping of Ce on RGO-TiO2 composite film inhibited the TiO2 anatase-rutile phase transformation. In this case, Ce atoms could serve as dispersion oxide and suppress the recombination of photoinduced electron-hole pairs. Besides, the change in absorbance from UV to visible region was observed in Ce doped RGO-TiO2 nanocomposite films. The Ce doped RGO-TiO2 composite film showed higher photoelectrochemical performance than that of RGO-TiO2 composite and pure TiO2 under solar simulator irradiation. The main reason might be attributed to the optimum content of Ce that could act as electrons acceptor to hinder the recombination loss and facilitate the better transportation for photoinduced charge carriers.

  17. Enhancing the photocatalytic activity of nanocrystalline TiO2 by co-doping with fluorine and yttrium

    International Nuclear Information System (INIS)

    Zhang, Huarong; Miao, Guashuai; Ma, Xingping; Wang, Bei; Zheng, Haiwu

    2014-01-01

    Highlights: • (F, Y)-codoped TiO 2 nanoparticles were prepared by a simple sol–gel method. • The highest photocatalytic activity (15 times of that over the pure TiO 2 ) was exhibited in the codoped TiO 2 with 0.05% Y doping level. • The Y doping induced oxygen vancancies played a duel role on the photocatalyic activity of the codoped TiO 2 . • The photocatalytic reactive oxygen species are critical to the photocatalytic degradation processes. - Abstract: Fluorine and yttrium codoped TiO 2 nanoparticles were prepared using a simple sol–gel method. The products were characterized with various spectroscopic and analytical techniques to determine their structural, morphological, optical absorption and photocatalytic properties. The results reveal that neither F nor Y doping causes obvious absorption edge shift in TiO 2 . Photoluminescence (PL) emission spectra present that the PL signal is enhanced, suggesting a decrease of photo-generated charge carrier separation efficiency, after the F or Y doping. The synergistic action by the F and Y doping leads to the highest photocatalytic activity for the degradation of methylene blue solution in the 0.05% (F, Y)-codoped sample (15 times of that over the pure TiO 2 ). With the increase of Y doping level, the photocatalytic performance in the codoped samples increases firstly and then decreases. The photocatalytic activity variations after the F and Y doping were interpreted by the formation of photocatalytic reactive oxygen species induced by the dopings

  18. Optical and electrochromic properties of sol-gel deposited Ti- doped vanadium oxide films

    International Nuclear Information System (INIS)

    Oezer, N.; Sabuncu, S.

    1997-01-01

    Because of the yellowish color, vanadium oxide films in the as deposited state is not as favorable as transparent coatings for most elector chromic devices. an interesting possibility to alter the yellowish colours is the doping with other non-absorbing metal oxides. Ti doped vanadium oxide films with various amounts of titanium were synthesized and investigated as transparent counter electrodes for electrochromic transmissive device application. Electrochromic titanium doped vanadium pentoxide (V sub 2 O 5) coatings were prepared by the sol-gel dip coating technique. The coating solutions were synthesized from vanadium tri(isopropoxide) precursors. X-ray diffraction (XRD) studies showed that the sol-gel deposited doped films heat treated at temperatures below 350 degree centigrade, were amorphous, whereas hose heat treated at higher temperatures were slight y crystalline. The optical and electrochemical properties of the Ti doped vanadium oxide films has been investigated in 0.1 m LiClO sub 4 propylene carbonate solution color changes by dropping were noted for all investigated films exhibits good electrochemical cycling (CV) measurements also showed that Ti doped V sub 2 O sub 5 films exhibits good electrochemical cycling reversibility, 'in situ' optical measurement revealed that those films exhibits good electrochemical cycling the spectra range 300 < lambda < 800 nm and change color between yellow and light green. The change in visible transmittance was 25 % for 5% Ti doped film. (author)

  19. Effect of lithium doping in BaTiO3 ceramics for vibration sensor application

    Science.gov (United States)

    Praveen, E.; Murugan, S.; Jayakumar, K.

    2018-04-01

    Phase pure undoped and Lithium doped BaTiO3 particles have been synthesized by high temperature solid-state reaction method. Substitution of Lithium at the Ba2+ site in BaTiO3 lattice has been investigated. The structural, vibrational, electrical and mechanical characterization have been carried out. The poled samples were used as a sensing element for the detection of mechanical oscillations and the presence of 80 Hz pulse in the output spectrum manifest the response of the sensor element to the applied mechanical stress. In comparison with pure BaTiO3 the sensitivity of Li doped BaTiO3 is 14 times greater than the pure BaTiO3. This confirms that Li doped BaTiO3 could be an efficient candidate for the functionalization of vibration sensors in space application.

  20. Effect of Sr doping on LaTiO3 thin films

    International Nuclear Information System (INIS)

    Vilquin, B.; Kanki, T.; Yanagida, T.; Tanaka, H.; Kawai, T.

    2005-01-01

    We report on the electric properties of La 1-x Sr x TiO 3 (0 ≤ x ≤ 0.5) thin films fabricated by pulsed laser deposition method. Crystallographic measurement of the thin films showed the epitaxial c-axis perovskite structure. The electric property of LaTiO 3 thin film, which is a typical Mott insulative material in bulk, showed insulative behaviour, while the Sr-doped films showed metallic conduction suffering electron-electron scattering. Below x = 0.1, the major carrier type was identified to be hole, and switched to electron with further increasing Sr-doping above x = 0.15. In fact, the switching from p-type to n-type for La 1-x Sr x TiO 3 thin films is first demonstrated in this study. The transition suggests that effective Coulomb gap vanishes due to over-additional Sr doping

  1. XAFS Studies of Fe Doped PhTiO3 Nanoparticles

    International Nuclear Information System (INIS)

    Shibata, Tomohiro; Chattopadhyay, Soma; Lin Bin; Palkar, V. R.

    2007-01-01

    Fe K and Ti K edge XAFS studies are reported on Fe doped PbTiO3 nanoparticles down to the 10 nm size. Fe forms Fe3+ ions and substitute for Ti4+ ions. For 18 nm nanoparticles, the Fe and Ti environment is found to be quite different. For PbFe0.5Ti0.5O3, locally the structure remains distorted from bulk to 10 nm size although the average structure changes

  2. NaF-assisted hydrothermal synthesis of Ti-doped hematite nanocubes with enhanced photoelectrochemical activity for water splitting

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Chong; Zhu, Zezhou; Wang, Sibo; Hou, Yidong, E-mail: ydhou@fzu.edu.cn

    2015-12-30

    Graphical abstract: An enhanced photoelectrochemical activity for water splitting was achieved over porous Ti-doped α-Fe{sub 2}O{sub 3} nanocubes. - Highlights: . • Ti-doped hematite nanocubes were successfully prepared by NaF-assisted hydrothermal deposition and subsequent annealing. • Ti-doped α-Fe{sub 2}O{sub 3} nanocubes showed an enhanced PEC activity with an IPCE of 25.2% at 340 nm at 1.23 V vs. RHE. • The enhanced activity of Ti-doped hematite nanocubes can be ascribed to high surface area and fast charge transportation. - Abstract: Ti-doped α-Fe{sub 2}O{sub 3} nanocubes on FTO substrate was prepared by hydrothermal deposition β-FeOOH onto FTO glass with a solution of FeCl{sub 3}, TiOCl{sub 2} and NaF, followed by an appropriate annealing. In comparison to Ti-doped α-Fe{sub 2}O{sub 3} nanorods Ti-doped α-Fe{sub 2}O{sub 3} nanocubes showed an enhanced photoelectrochemical activity for water splitting, with a remarkable IPCE of 25.2% at 340 nm at the potential of 1.23 V vs. RHE. The hematite films were studied in detail by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, UV–vis absorption spectroscopy and electrochemical impedance spectroscopy. On the basis of the obtained results, the improved performance of Ti-doped α-Fe{sub 2}O{sub 3} nanocubes can be ascribed to the porous structure, good electrical conductivity and fast charge transportation of hematite.

  3. Characteristics of nano Ti-doped SnO2 powders prepared by sol-gel method

    International Nuclear Information System (INIS)

    Liu, X.M.; Wu, S.L.; Chu, Paul K.; Zheng, J.; Li, S.L.

    2006-01-01

    Ti 4+ -doped SnO 2 nano-powders were prepared by the sol-gel process using tin tetrachloride and titanium tetrachloride as the starting materials. The crystallinity and purity of the powders were analyzed by X-ray diffraction (XRD) and the size and distribution of Ti 4+ -doped SnO 2 grains were studied using transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The results show that Ti 4+ has been successfully incorporated into the SnO 2 crystal lattice and the electrical conductivity of the doped materials improves significantly

  4. Transparent nanostructured Fe-doped TiO2 thin films prepared by ultrasonic assisted spray pyrolysis technique

    Science.gov (United States)

    Rasoulnezhad, Hossein; Hosseinzadeh, Ghader; Ghasemian, Naser; Hosseinzadeh, Reza; Homayoun Keihan, Amir

    2018-05-01

    Nanostructured TiO2 and Fe-doped TiO2 thin films with high transparency were deposited on glass substrate through ultrasonic-assisted spray pyrolysis technique and were used in the visible light photocatalytic degradation of MB dye. The resulting thin films were characterized by scanning electron microscopy (SEM), Raman spectroscopy, photoluminescence spectroscopy, x-ray diffraction (XRD), and UV-visible absorption spectroscopy techniques. Based on Raman spectroscopy results, both of the TiO2 and Fe-doped TiO2 films have anatase crystal structure, however, because of the insertion of Fe in the structure of TiO2 some point defects and oxygen vacancies are formed in the Fe-doped TiO2 thin film. Presence of Fe in the structure of TiO2 decreases the band gap energy of TiO2 and also reduces the electron–hole recombination rate. Decreasing of the electron–hole recombination rate and band gap energy result in the enhancement of the visible light photocatalytic activity of the Fe-doped TiO2 thin film.

  5. Effect of V-Nd co-doping on phase transformation and grain growth process of TiO2

    Science.gov (United States)

    Khatun, Nasima; Amin, Ruhul; Anita, Sen, Somaditya

    2018-05-01

    The pure and V-Nd co-doped TiO2 samples are prepared by the modified sol-gel process. The phase formation is confirmed by XRD spectrum. Phase transformation is delayed in V-Nd co-doped TiO2 (TVN) samples compared to pure TiO2. The particle size is comparatively small in TVN samples at both the temperature 450 °C and 900 °C. Hence the effect of Nd doping is dominated over V doping in both phase transformation and grain growth process of TiO2.

  6. Synthesis, Structural and Optical Properties of Co Doped TiO2 Nanocrystals by Sol-Gel Method

    Directory of Open Access Journals (Sweden)

    D.V. Sridevi

    2017-06-01

    Full Text Available A TiO2 nanoparticle doped with cobalt was synthesized by sol-gel technique employed at room temperature with appropriate reactants. In the present case, we used titanium tetra isoprotoxide (TTIP and 2–propanol as a common starting material and the obtained products were calcined at 450˚ C. From the Powder XRD data the particle size was calculated by Scherrer method. The FE-SEM analysis shows the morphology of cobalt doped TiO2 nanoparticles. The various functional groups of the samples were identified by Fourier transform spectroscopy (FT-IR. The UV-Vis-NIR spectra of cobalt doped TiO2 material shows two absorption peaks in the visible region related to d-d transitions of Co2+ in TiO2 lattice. Compared to un-doped TiO2 nanoparticles, the cobalt doped material show a red shift in the band gap.

  7. Fabrication of Ce/N co-doped TiO_2/diatomite granule catalyst and its improved visible-light-driven photoactivity

    International Nuclear Information System (INIS)

    Chen, Yan; Liu, Kuiren

    2017-01-01

    Highlights: • Ce/N co-doped TiO_2/diatomite granule (CNTD-G) was prepared via sol-gel method. • The optimal doping amount of Ce was determined. • The effects of impurity ions on photodegradation process were studied. • The intermediates generated during photodegradation process were deduced. • The mechanism of photodegradation process was proposed. - Abstract: Eliminating antibiotic remnants in aquatic environment has become one of the hottest topics among current research works. Thus, we prepared Ce, N co-doped TiO_2/diatomite granule (CNTD-G) catalyst to provide a new method. As one typical antibiotics, oxytetracycline (OTC) was selected as the target pollutant to be degradated under visible light irradiation. The carrier diatomite helped the spread of TiO_2 nanoparticles onto its surface, and inhibited their agglomeration. The synergy of Ce and N dopants highly improved the visible-light-driven photoactivity of TiO_2. The optimal doping amount and degradation conditions were determined. Besides, the effects of impurity ions were also investigated, including cations: Ca"2"+, Mg"2"+; or anions: NO_3"−, SO_4"2"− and PO_4"3"−. The intermediates generated during degradation process were studied, and the mechanism of the photodegradation process was proposed. CNTD-G could be easily collected from the reactor, and showed excellent recyclability.

  8. Effect of different processes and Ti/Zn molar ratios on the structure, morphology, and enhanced photoelectrochemical and photocatalytic performance of Ti3+ self-doped titanium-zinc hybrid oxides

    Science.gov (United States)

    Fu, Rongrong; Wang, Qingyao; Gao, Shanmin; Wang, Zeyan; Huang, Baibiao; Dai, Ying; Lu, Jun

    2015-07-01

    Ti3+ self-doped titanium-zinc hybrid oxides with different phase compositions and morphologies were successfully synthesized using Zn powder as the reductant and Zn source by a chemical-reduction precipitation method with subsequent thermal treatment. The fabricated Ti3+ self-doped TiO2(A)/TiO2(R), TiO2(A)/TiO2(R)/ZnTiO3, and TiO2(A)/ZnO heterojunctions were characterized by X-ray diffraction, transmission electron microscopy, high-resolution transmission electron microscopy, X-ray photoelectron spectroscopy, and UV-Vis diffuse reflectance spectroscopy. The effects of various Ti/Zn molar ratios and preparation processes on the structural, morphological, optical, photocurrent and photocatalytic properties of the resultant samples were investigated systematically. Results reveal that Ti3+ self-doping enhances the photoabsorption capability of titanium-zinc hybrid oxides in the visible-light region. Moreover, different processes and Ti/Zn molar ratios play great influences on the structure, morphology, optical, photocurrent and photocatalytic properties of the final products. Ti3+ self-doped titanium-zinc hybrid oxides exhibit excellent photocurrent and photocatalytic activity than pure TiO2 and ZnTiO3 under visible-light irradiation (λ ≥ 400 nm). The most active Ti3+ self-doped titanium-zinc hybrid oxides photoanode presents significantly improved water splitting performance. The synergistic effect between the Ti3+ self-doped and heterojunctions is responsible for the enhanced performance of these materials.

  9. Effect of Graphite Doped TiO_2 Nanoparticles on Smoke Degradation

    International Nuclear Information System (INIS)

    Roshasnorlyza Hazan; Mohamad Shahrizal Md Zain; Natrah Syafiqah Rosli

    2016-01-01

    Secondhand smoke affects in the same way as regular smoker. The best solution is to purify the air efficiently and effectively. In this study, we were successfully doped TiO_2 nanoparticle with graphite to accelerate the degradation of cigarette smoke. The graphite doped and undoped TiO_2 nanoparticles were prepared from synthetic rutile using alkaline fusion method and their photo catalytic activity were investigated under visible light irradiation. The photo catalytic activity of the TiO_2 nanoparticles was analyzed in terms of their particle size analysis, crystallization and optical band gap. TiO_2 nanoparticle act as photo catalyzer by utilization of light energy to excite electron-hole pairs in smoke degradation processes. With the aided from graphite in TiO_2 nanoparticles, the smoke degradation was accelerate up to 44.4 %. In this case, graphite helps to reduce optical band gap of TiO_2 nanoparticle, thus increasing excitation of electron from valence band to conduction band. (author)

  10. Photocatalytic degradation of methylene blue on Fe3+-doped TiO2 nanoparticles under visible light irradiation

    Institute of Scientific and Technical Information of China (English)

    SU Bitao; WANG Ke; BAI Jie; MU Hongmei; TONG Yongchun; MIN Shixiong; SHE Shixiong; LEI Ziqiang

    2007-01-01

    Fe3+-doped TiO2 composite nanoparticles with different doping amounts were successfully synthesized using sol-gel method and characterized by X-ray diffraction (XRD),transmission electron microscopy (TEM) and ultraviolet-visible spectroscopy (UV-Vis) diffuse reflectance spectra (DRS). The photocatalytic degradation of methylene blue was used as a model reaction to evaluate the photocatalytic activity of Fe3+/TiO2 nanoparticles under visible light irradia-tion. The influence of doping amount of Fe3+ (ω: 0.00%-3.00%) on photocatalytic activities of TiO2 was investigated.Results show that the size of Fe3+/TiO2 particles decreases with the increase of the amount of Fe3+ and their absorptionspectra are broaden and absorption intensities are also increased. Doping Fe3+ can control the conversion of TiO2 from anatase to rutile. The doping amount of Fe3+ remarkably affects the activity of the catalyst, and the optimum efficiency occurs at about the doping amount of 0.3%. The appropriate doping of Fe3+ can markedly increase the catalytic activity of TiO2 under visible light irradiation.

  11. Determination of photo-catalytic activity of un-doped and Mn-doped TiO2 anatase powders on acetaldehyde under UV and visible light

    International Nuclear Information System (INIS)

    Papadimitriou, Vassileios C.; Stefanopoulos, Vassileios G.; Romanias, Manolis N.; Papagiannakopoulos, Panos; Sambani, Kyriaki; Tudose, Valentin; Kiriakidis, George

    2011-01-01

    Titanium dioxide (TiO 2 ) photocatalytic powder materials doped with various levels of manganese (Mn) were synthesized to be used as additives to wall painting in combating indoor and outdoor air pollution. The heterogeneous photocatalytic degradation of gaseous acetaldehyde (CH 3 CHO) on Mn–TiO 2 surfaces under ultraviolet and visible (UV/Vis) irradiation was investigated, by employing the Photochemical Static Reactor coupled with Fourier-Transformed Infrared spectroscopy (PSR/FTIR) technique. Experiments were performed by exposing acetaldehyde (∼ 400 Pa) and synthetic air mixtures (∼ 1.01 × 10 5 Pa total pressure) on un-doped TiO 2 and doped with various levels of Mn (0.1–33% mole percentage) under UV and visible irradiation at room temperature. Photoactivation was initiated using either UV or visible light sources with known emission spectra. Initially, the photo-activity of CH 3 CHO under the above light sources, and the physical adsorption of CH 3 CHO on Mn–TiO 2 samples in the absence of light were determined prior to the photocatalytic experiments. The photocatalytic loss of CH 3 CHO on un-doped TiO 2 and Mn–TiO 2 samples in the absence and presence of UV or visible irradiation was measured over a long time period (≈ 60 min), to evaluate their relative photocatalytic activity. The gaseous photocatalytic end products were also determined using absorption FTIR spectroscopy. Carbon dioxide (CO 2 ) was identified as the main photocatalysis product. It was found that 0.1% Mn–TiO 2 samples resulted in the highest photocatalytic loss of CH 3 CHO under visible irradiation. This efficiency was drastically diminished at higher levels of Mn doping (1–33%). The CO 2 yields were the highest for 0.1% Mn–TiO 2 samples under UV irradiation, in agreement with the observed highest CH 3 CHO decomposition rates. It was demonstrated that low-level (0.1%) doping of TiO 2 with Mn results in a significant increase of their photocatalytic activity in the visible

  12. Characterization and improved solar light activity of vanadium doped TiO2/diatomite hybrid catalysts

    International Nuclear Information System (INIS)

    Wang, Bin; Zhang, Guangxin; Leng, Xue; Sun, Zhiming; Zheng, Shuilin

    2015-01-01

    Highlights: • V-doped TiO 2 /diatomite composite photocatalyst was synthesized. • The physiochemical property and solar light photoactivity were characterized. • The presence and influence of V ions in TiO 2 matrix was systematically analyzed. • The photocatalysis for Rhodamine B were studied under solar light illumination. - Abstract: V-doped TiO 2 /diatomite composite photocatalysts with different vanadium concentrations were synthesized by a modified sol–gel method. The diatomite was responsible for the well dispersion of TiO 2 nanoparticles on the matrix and consequently inhibited the agglomeration. V-TiO 2 /diatomite hybrids showed red shift in TiO 2 absorption edge with enhanced absorption intensity. Most importantly, the dopant energy levels were formed in the TiO 2 bandgap due to V 4+ ions substituted to Ti 4+ sites. The 0.5% V-TiO 2 /diatomite photocatalyst displayed narrower bandgap (2.95 eV) compared to undoped sample (3.13 eV) and other doped samples (3.05 eV) with higher doping concentration. The photocatalytic activities of V doped TiO 2 /diatomite samples for the degradation of Rhodamine B under stimulated solar light illumination were significantly improved compared with the undoped sample. In our case, V 4+ ions incorporated in TiO 2 lattice were responsible for increased visible-light absorption and electron transfer to oxygen molecules adsorbed on the surface of TiO 2 to produce superoxide radicals ·O 2 – , while V 5+ species presented on the surface of TiO 2 particles in the form of V 2 O 5 contributed to e – –h + separation. In addition, due to the combination of diatomite as support, this hybrid photocatalyst could be separated from solution quickly by natural settlement and exhibited good reusability

  13. Selective Oxidation Using Flame Aerosol Synthesized Iron and Vanadium-Doped Nano-TiO2

    Directory of Open Access Journals (Sweden)

    Zhong-Min Wang

    2011-01-01

    Full Text Available Selective photocatalytic oxidation of 1-phenyl ethanol to acetophenone using titanium dioxide (TiO2 raw and doped with Fe or V, prepared by flame aerosol deposition method, was investigated. The effects of metal doping on crystal phase and morphology of the synthesized nanostructured TiO2 were analyzed using XRD, TEM, Raman spectroscopy, and BET nitrogen adsorbed surface area measurement. The increase in the concentration of V and Fe reduced the crystalline structure and the anatase-to-rutile ratios of the synthesized TiO2. Synthesized TiO2 became fine amorphous powder as the Fe and V concentrations were increased to 3 and 5%, respectively. Doping V and Fe to TiO2 synthesized by the flame aerosol increased photocatalytic activity by 6 folds and 2.5 folds, respectively, compared to that of pure TiO2. It was found that an optimal doping concentration for Fe and V were 0.5% and 3%, respectively. The type and concentration of the metal dopants and the method used to add the dopant to the TiO2 are critical parameters for enhancing the activity of the resulting photocatalyst. The effects of solvents on the photocatalytic reaction were also investigated by using both water and acetonitrile as the reaction medium.

  14. Al2O3 doped TiO2 ceramic waste forms

    International Nuclear Information System (INIS)

    Uno, Masayoshi; Kinoshita, Hajime; Sakai, Etsuro; Ikeda, Akira; Matsumoto, Y.; Yamanaka, Shinsuke

    1999-01-01

    Melting of the mixture of Nd 2 O 3 , CeO 2 , SrO, TiO 2 and Al 2 O 3 at 1673 K for 1 hour produced one RE 2 Ti 3 O 9 phase compound. Differential Scanning Calorimetry (DSC) measurement showed that the melting temperature of this compound was 1646 K. Density of the alumina doped oxide was higher than that of the oxide obtained by the pressing and sintering without alumina. Vickers hardness of the oxide obtained by the pressing and sintering was 5.3 GPa and nearly same as that of glass waste. That of the alumina doped oxide was around 7 GPa. 7 days Soxhlet leach test (MCC-5) followed by Inductively Coupled Plasma Spectrometry (ICP) showed that normalized leaching rate of Ti for the oxide obtained by the pressing and sintering was 5.54 x 10 -3 kg/m 2 and that for the alumina doped oxide was 2.24 x 10 -3 kg/m 2 . The value of Sr for the pressed and sintered sample was 0.034 x 10 -3 kg/m 2 but that for alumina doped sample was below the detection limit (0.01 x 10 -3 kg/m 2 ). Al was not detected from the leachate of the alumina doped sample. (author)

  15. Facile synthesis and characterization of N-doped TiO2/C nanocomposites with enhanced visible-light photocatalytic performance

    Science.gov (United States)

    Jia, Tiekun; Fu, Fang; Yu, Dongsheng; Cao, Jianliang; Sun, Guang

    2018-02-01

    Ultrafine anatase N-doped TiO2 nanocrystals modified with carbon (denoted as N-doped TiO2/C) were successfully prepared via a facile and low-cost approach, using titanium tetrachloride, aqueous ammonia and urea as starting materials. The phase composition, surface chemical composition, morphological structure, electronic and optical properties of the as-prepared photocatalysts were well characterized and analyzed. On the basis of Raman spectral characterization combining with the results of X-ray photoelectron spectroscopy (XPS) and high resolution transmission electron microscopy (HRTEM), it could be concluded that N dopant ions were successfully introduced into TiO2 crystal lattice and carbon species were modified on the surface or between the nanoparticles to form N-doped TiO2/C nanocomposites. Compared with that of bare TiO2, the adsorption band edge of N-doped TiO2/C nanocomposites were found to have an evident red-shift toward visible light region, implying that the bandgap of N-doped TiO2/C nanocomposites is narrowed and the visible light absorption capacity is significantly enhanced due to N doping and carbon modification. The photoactivity of the as-prepared photocatalytsts was tested by the degradation of Rhodamine B (RhB) under visible light (λ > 420 nm), and the results showed that the N-doped TiO2/C nanocomposites exhibited much higher photodegradation rate than pure TiO2 and N-doped TiO2, which was mainly attributed to the synergistic effect of the enhanced light harvesting, augmented catalytic active sites and efficient separation of photogenerated electron-hole pairs.

  16. Morphology and structure of Ti-doped diamond films prepared by microwave plasma chemical vapor deposition

    Science.gov (United States)

    Liu, Xuejie; Lu, Pengfei; Wang, Hongchao; Ren, Yuan; Tan, Xin; Sun, Shiyang; Jia, Huiling

    2018-06-01

    Ti-doped diamond films were deposited through a microwave plasma chemical vapor deposition (MPCVD) system for the first time. The effects of the addition of Ti on the morphology, microstructure and quality of diamond films were systematically investigated. Secondary ion mass spectrometry results show that Ti can be added to diamond films through the MPCVD system using tetra n-butyl titanate as precursor. The spectra from X-ray diffraction, Raman spectroscopy, and X-ray photoelectron spectroscopy and the images from scanning electron microscopy of the deposited films indicate that the diamond phase clearly exists and dominates in Ti-doped diamond films. The amount of Ti added obviously influences film morphology and the preferred orientation of the crystals. Ti doping is beneficial to the second nucleation and the growth of the (1 1 0) faceted grains.

  17. Formation of Sol Gel Dried Droplets of Carbon Doped Titanium Dioxide (TiO2) at Low Temperature via Electrospraying

    Science.gov (United States)

    Halimi, S. U.; Hashib, S. Abd; Abu Bakar, N. F.; Ismail, S. N.; Nazli Naim, M.; Rahman, N. Abd; Krishnan, J.

    2018-05-01

    The high band gap energy of TiO2 and inconsistency in particles size has imposed a significant drawback on TiO2 applications. Dried droplets of carbon-doped TiO2 fine particles were produced by using electrospraying technique. The C-doped TiO2 particles were prepared by hydrolysis of titanium isopropoxide with the addition of carbon precursor followed by electrospraying the suspension in stable Taylor cone-jet mode. Coulomb fission of charged droplets from the electrospraying technique successfully transformed dispersed liquid C-doped TiO2 particles into solid. The deposited C-doped TiO2 droplets were collected on aluminium substrates placed at working distances of 10 to 20 cm from the tip of the electrospray needle. The collected C-doped TiO2 droplets were characterized by using FESEM, UV-Vis, FTIR and XRD. By increasing the working distance, the average droplets size of the deposited C-doped TiO2 was reduced from ±163.2 nm to ±147.56 nm. UV-Vis analysis showed a strong absorption in the visible-light region and about 93 nm red shift of the onset spectrum for C-doped TiO2. The red shift indicates an increase in photocatalytic efficiency by reducing the TiO2 band gap energy from 3.0 eV to 2.46 eV and shifting its activity to the visible-light region. FTIR analysis indicated the presence of Ti-C and C-O chemical bonding in the C-doped TiO2.

  18. Paramagnetic behavior of Co doped TiO{sub 2} nanocrystals controlled by self-purification mechanism

    Energy Technology Data Exchange (ETDEWEB)

    Anitha, B. [Centre for Nanoscience and Nanotechnology, University of Kerala, Kariavattom, Thiruvananthapuram 695 581 (India); Khadar, M. Abdul, E-mail: mabdulkhadar@rediffmail.com [Centre for Nanoscience and Nanotechnology, University of Kerala, Kariavattom, Thiruvananthapuram 695 581 (India); Banerjee, Alok [UGC-DAE Consortium for Scientific Research (CSR), Khandwa Road, Indore 452 001 (India)

    2016-07-15

    Doping in nanocrystals is a challenging process because of the self- purification mechanism which tends to segregate out the dopants resulting in a greater dopant concentration near the surface than at the interior of nanocrystals. In the present work nanocrystals of TiO{sub 2} doped with different atom % of Co were synthesized by peroxide gel method. XRD analysis confirmed the tetragonal anatase structure and HRTEM images showed the rod-like morphology of the samples. Raman modes of anatase phase of TiO{sub 2} along with weak intensity peaks of Co{sub 3}O{sub 4} for higher Co dopant concentrations were observed for the samples. EPR measurements revealed the presence of cobalt in +2 oxidation state in the TiO{sub 2} matrix. SQUID measurements indicated paramagnetic behavior of the Co doped TiO{sub 2} nanocrystals. The paramagnetic behavior is attributed to an increased concentration of Co{sup 2+} ions and an increased presence of Co{sub 3}O{sub 4} phase near the surface of the TiO{sub 2} nanocrystals due to self-purification mechanism. - Graphical abstract: Variation of the intensity ratios of XRD peaks as a function of atomic ratio of Co. Inset: variation of structure factor for (101) reflection as a function of atomic ratio of Co. Display Omitted - Highlights: • Co doped TiO{sub 2} nanocrystals were synthesized by peroxide gel method. • HRTEM images showed Co doped TiO{sub 2} nanocrystals to be rod-like. • EPR spectra showed +2 oxidation states for Co in the samples. • Co doped TiO{sub 2} nanocrystals showed paramagnetic behavior.

  19. Flux pinning behaviors of Ti and C co-doped MgB{sub 2} superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Y.; Zhao, D.; Shen, T.M.; Li, G.; Zhang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Feng, Y. [Northwest Institute for Nonferrous Metal Research, P.O. Box 51, Xian, Shaanxi 710016 (China); Western Superconductivity Technology Company, Xian (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); School of Materials Science and Engineering, University of New South Wales, Sydney 2052, NSW (Australia); Zhang, Y.P. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Zhao, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); School of Materials Science and Engineering, University of New South Wales, Sydney 2052, NSW (Australia)], E-mail: yzhao@swjtu.edu.cn

    2008-09-15

    Flux pinning behavior of carbon and titanium concurrently doped MgB{sub 2} alloys has been studied by ac susceptibility and dc magnetization measurements. It is found that critical current density and irreversibility field of MgB{sub 2} have been significantly improved by doping C and Ti concurrently, sharply contrasted to the situation of C-only-doped or Ti-only-doped MgB{sub 2} samples. AC susceptibility measurement reveals that the dependence of the pinning potential on the dc applied field of Mg{sub 0.95}Ti{sub 0.05}B{sub 1.95}C{sub 0.05} has been determined to be U(B{sub dc}){proportional_to}B{sub dc}{sup -1} compared to that of MgB{sub 2}U(B{sub dc}){proportional_to}B{sub dc}{sup -1.5}. As to the U(J) behavior, a relationship of U(J) {proportional_to} J{sup -0.17} is found fitting well for Mg{sub 0.95}Ti{sub 0.05}B{sub 1.95}C{sub 0.05} with respect to U(J) {proportional_to} J{sup -0.21} for MgB{sub 2}. All the results reveal a strong enhancement of the high field pinning potential in C and Ti co-doped MgB{sub 2}.

  20. Fabrication of doped TiO2 nanotube array films with enhanced photo-catalytic activity

    Science.gov (United States)

    Peighambardoust, Naeimeh-Sadat; Khameneh-asl, Shahin; Khademi, Adib

    2018-01-01

    In the present work, we investigate the N and Fe-doped TiO2 nanotube array film prepared by treating TiO2 nanotube array film with ammonia solution and anodizing in Fe(NO3)3 solution respectively. This method avoided the use of hazardous ammonia gas, or laborious ion implantation process. N and Fe-doped TiO2 nanotube arrays (TiO2 NTs) were prepared by electrochemical anodization process in 0.5 wt % HF aqueous solution. The anodization was performed at the conditions of 20 V and 20 min, Followed by a wet immersion in NH3.H2O (1M) for N-doping for 2 hr and annealing post-treatment at 450 °C. The morphology and structure of the nanotube films were characterized by field emission scanning electron microscope (FESEM) and EDX. UV-vis. illumination test were done to observe photo-enhanced catalysis. The effect of different annealing temperature on the structure and photo-absorption property of the TiO2-TNTs was investigated. The results showed that N-TNTs nanotubes exhibited higher photocatalytic activity compared whit the Fe-doped and pure TNTs, because doping N promoted the separation of the photogenerated electrons and holes.

  1. Preparation and photocatalytic activity of B, Y co-doped nanosized TiO_2 catalyst

    Institute of Scientific and Technical Information of China (English)

    石中亮; 刘富梅; 姚淑华

    2010-01-01

    The catalysts of un-doped, single-doped and co-doped titanium dioxide (TiO2) powders were prepared by sol-gel method with Ti(OC4H9)4 as a raw material. The photocatalytic decomposition of phenol in aqueous solution under UV light was used as a probe reaction to evaluate their photocatalytic activities. The effects of B, Y co-doping on the crystallite sizes, crystal pattern, surface composition, and optical property of the catalyst were investigated by thermogravimetric differential thermal analysis, X-ray d...

  2. Phase transformations in sputter-deposited W-doped TiO2 films during annealing in air

    International Nuclear Information System (INIS)

    Saladukhin, I. A.; Abadias, G.

    2013-01-01

    Pure and tungsten-doped TiO 2 films are characterized as amorphous in the as-deposited state by XRD. A crystallization of titanium dioxide occurs during their annealing in air. Depending on the tungsten and nitrogen doping level, anatase or rutile phase formation is observed. Both of these phases are thermally stable in all interval of the temperatures used during annealing. Phase composition and lattice parameter analysis indicates on the formation of substitutional Ti 1 -xW x O 2 films. N-doped Ti 0 .75W 0 .25O 2 film is more resistant against high-temperature oxidation as compared to Ti 0 .74W 0 .26O 2 film and, especially, as compared to Ti 0 .60W 0 .40O 2 film. (authors)

  3. The Effects of Doping Copper and Mesoporous Structure on Photocatalytic Properties of TiO2

    Directory of Open Access Journals (Sweden)

    Yang Wang

    2014-01-01

    Full Text Available This paper describes a system for the synthesis of Cu-doped mesoporous TiO2 nanoparticles by a hydrothermal method at relatively low temperatures. The technique used is to dope the as-prepared mesoporous TiO2 system with copper. In this method, the copper species with the form of Cu1+, which was attributed to the reduction effect of dehydroxylation and evidenced by X-ray photoelectron spectroscopy (XPS and X-ray diffraction (XRD, was well dispersed in the optimal concentration 1 wt.% Cu-doped mesoporous TiO2. In this as-prepared mesoporous TiO2 system, original particles with a size of approximately 20 nm are aggregated together to shapes of approximately 1100 nm, which resulted in the porous aggregate structure. More importantly, the enhancement of the photocatalytic activity was discussed as effects due to the formation of stable Cu(I and the mesoporous structure in the Cu-doped mesoporous TiO2. Among them, Cu-doped mesoporous TiO2 shows the highest degradation rate of methyl orange (MO. In addition, the effects of initial solution pH on degradation of MO had also been investigated. As a result, the optimum values of initial solution pH were found to be 3.

  4. Highly Al-doped TiO{sub 2} nanoparticles produced by Ball Mill Method: structural and electronic characterization

    Energy Technology Data Exchange (ETDEWEB)

    Santos, Desireé M. de los, E-mail: desire.delossantos@uca.es; Navas, Javier, E-mail: javier.navas@uca.es; Sánchez-Coronilla, Antonio; Alcántara, Rodrigo; Fernández-Lorenzo, Concha; Martín-Calleja, Joaquín

    2015-10-15

    Highlights: • Highly Al-doped TiO{sub 2} nanoparticles were synthesized using a Ball Mill Method. • Al doping delayed anatase to rutile phase transformation. • Al doping allow controlling the structural and electronic properties of nanoparticles. - Abstract: This study presents an easy method for synthesizing highly doped TiO{sub 2} nanoparticles. The Ball Mill method was used to synthesize pure and Al-doped titanium dioxide, with an atomic percentage up to 15.7 at.% Al/(Al + Ti). The samples were annealed at 773 K, 973 K and 1173 K, and characterized using ICP-AES, XRD, Raman spectroscopy, FT-IR, TG, STEM, XPS, and UV–vis spectroscopy. The effect of doping and the calcination temperature on the structure and properties of the nanoparticles were studied. The results show high levels of internal doping due to the substitution of Ti{sup 4+} ions by Al{sup 3+} in the TiO{sub 2} lattice. Furthermore, anatase to rutile transformation occurs at higher temperatures when the percentage of doping increases. Therefore, Al doping allows us to control the structural and electronic properties of the nanoparticle synthesized. So, it is possible to obtain nanoparticles with anatase as predominant phase in a higher range of temperature.

  5. Electrical and microstructural properties of CaTiO3-doped K1/2Na1 ...

    Indian Academy of Sciences (India)

    KNN) and CaTiO3- modified K1/2Na1/2NbO3 (CTO-KNN) systems, were investigated. Discs doped with 0 to 0.55% mol of CaTiO3 (CTO) were sintered at 1125°C for 2 h. Although minority phases were found in doped samples, CaTiO3 was not ...

  6. Antibacterial activity of single crystalline silver-doped anatase TiO{sub 2} nanowire arrays

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xiangyu, E-mail: zhangxiangyu@tyut.edu.cn; Li, Meng; He, Xiaojing; Hang, Ruiqiang; Huang, Xiaobo; Wang, Yueyue; Yao, Xiaohong; Tang, Bin, E-mail: tangbin@tyut.edu.cn

    2016-05-30

    Graphical abstract: The silver-doped TiO{sub 2} nanowire arrays on titanium foil substrate were synthesized via a two-step process. It includes: deposition of AgTi films on titanium foil by magnetron sputtering; preparation of AgNW arrays on AgTi films via alkali (NaOH) hydrothermal treatment and ion-exchange with HCl, followed by calcinations. - Highlights: • Ag-doped TiO{sub 2} nanowire arrays have been prepared by a duplex-treatment. • The duplex-treatment consisted of magnetron sputtering and hydrothermal growth. • Ag-doped nanowire arrays show excellent antibacterial activity against E. coli. - Abstract: Well-ordered, one-dimensional silver-doped anatase TiO{sub 2} nanowire (AgNW) arrays have been prepared through a hydrothermal growth process on the sputtering-deposited AgTi layers. Electron microscope analyses reveal that the as-synthesized AgNW arrays exhibit a single crystalline phase with highly uniform morphologies, diameters ranging from 85 to 95 nm, and lengths of about 11 μm. Silver is found to be doped into TiO{sub 2} nanowire evenly and mainly exists in the zerovalent state. The AgNW arrays show excellent efficient antibacterial activity against Escherichia coli (E. coli), and all of the bacteria can be killed within 1 h. Additionally, the AgNW arrays can still kill E. coli after immersion for 60 days, suggesting the long-term antibacterial property. The technique reported here is environmental friendly for formation of silver-containing nanostructure without using any toxic organic solvents.

  7. Fabrication of Ce/N co-doped TiO{sub 2}/diatomite granule catalyst and its improved visible-light-driven photoactivity

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yan; Liu, Kuiren, E-mail: liukr@smm.neu.edu.cn

    2017-02-15

    Highlights: • Ce/N co-doped TiO{sub 2}/diatomite granule (CNTD-G) was prepared via sol-gel method. • The optimal doping amount of Ce was determined. • The effects of impurity ions on photodegradation process were studied. • The intermediates generated during photodegradation process were deduced. • The mechanism of photodegradation process was proposed. - Abstract: Eliminating antibiotic remnants in aquatic environment has become one of the hottest topics among current research works. Thus, we prepared Ce, N co-doped TiO{sub 2}/diatomite granule (CNTD-G) catalyst to provide a new method. As one typical antibiotics, oxytetracycline (OTC) was selected as the target pollutant to be degradated under visible light irradiation. The carrier diatomite helped the spread of TiO{sub 2} nanoparticles onto its surface, and inhibited their agglomeration. The synergy of Ce and N dopants highly improved the visible-light-driven photoactivity of TiO{sub 2}. The optimal doping amount and degradation conditions were determined. Besides, the effects of impurity ions were also investigated, including cations: Ca{sup 2+}, Mg{sup 2+}; or anions: NO{sub 3}{sup −}, SO{sub 4}{sup 2−} and PO{sub 4}{sup 3−}. The intermediates generated during degradation process were studied, and the mechanism of the photodegradation process was proposed. CNTD-G could be easily collected from the reactor, and showed excellent recyclability.

  8. Influences of Mg Doping on the Electrochemical Performance of TiO2 Nanodots Based Biosensor Electrodes

    Directory of Open Access Journals (Sweden)

    M. S. H. Al-Furjan

    2014-01-01

    Full Text Available Electrochemical biosensors are essential for health monitors to help in diagnosis and detection of diseases. Enzyme adsorptions on biosensor electrodes and direct electron transfer between them have been recognized as key factors to affect biosensor performance. TiO2 has a good protein adsorption ability and facilitates having more enzyme adsorption and better electron transfer. In this work, Mg ions are introduced into TiO2 nanodots in order to further improve electrode performance because Mg ions are considered to have good affinity with proteins or enzymes. Mg doped TiO2 nanodots on Ti substrates were prepared by spin-coating and calcining. The effects of Mg doping on the nanodots morphology and performance of the electrodes were investigated. The density and size of TiO2 nanodots were obviously changed with Mg doping. The sensitivity of 2% Mg doped TiO2 nanodots based biosensor electrode increased to 1377.64 from 897.8 µA mM−1 cm−2 and its KMapp decreases to 0.83 from 1.27 mM, implying that the enzyme achieves higher catalytic efficiency due to better affinity of the enzyme with the Mg doped TiO2. The present work could provide an alternative to improve biosensor performances.

  9. Synthesis of TiO2-doped SiO2 composite films and its applications

    Indian Academy of Sciences (India)

    Wintec

    structure of the titanium oxide species in the TiO2-doped SiO2 composite films and the photocatalytic reactiv- ity in order to ... gaku D-max γA diffractometer with graphite mono- chromized ... FT–IR absorption spectra of TiO2-doped SiO2 com-.

  10. Impedance spectroscopy of Li2CO3 doped (Ba,Sr)TiO3 ceramic

    Science.gov (United States)

    Ham, Yong-Su; Koh, Jung-Hyuk

    2013-02-01

    (BaxSr1-x)TiO3-based ceramic has been considered as one of the most important electronic materials widely employed in microwave passive device applications. Many researches have been performed to lower the high sintering temperature, by adding various dopants such as B2O3, La2O3, etc. In our previous study, by adding Li2CO3 to (Ba0.5,Sr0.5)TiO3 ceramics, the sintering temperature of Li2CO3 doped (Ba0.5,Sr0.5)TiO3 ceramics decreased from 1350 to 900 °C. This study observed the crystalline structure and electrical properties of Li2CO3 doped (Ba0.5,Sr0.5)TiO3 ceramics. In scanning the crystalline structure of Li2CO3 doped (Ba0.5,Sr0.5)TiO3 ceramics, no pyro phase was observed by X-ray diffraction analysis. To investigate the electrical properties of Li2CO3 doped (Ba0.5,Sr0.5)TiO3 ceramics, real and imaginary parts of the impedances were analyzed. Complex impedance data were measured from 100 Hz to 1 MHz at various temperature ranges.

  11. Facile preparation of Ti{sup 3+} self-doped TiO{sub 2} nanosheets with dominant {0 0 1} facets using zinc powder as reductant

    Energy Technology Data Exchange (ETDEWEB)

    Si, Lingling; Huang, Ze’ai; Lv, Kangle, E-mail: lvkangle@mail.scuec.edu.cn; Tang, Dingguo; Yang, Changjun

    2014-07-15

    Highlights: • Ti{sup 3+}-doped high-energy TiO{sub 2} nanosheets was prepared using zinc powder as reductant. • Effects of Zn on morphology and BET surface areas of TiO{sub 2} nanosheets is negligible. • Zn powder resulted in the formation of Ti{sup 3+} self-doped anatase TiO{sub 2} nanosheets. • Ti{sup 3+} self-doped TiO{sub 2} nanosheets showed enhanced visible-light photoactivity. - Abstract: Ti{sup 3+} self-doped TiO{sub 2} nanosheets with dominant {0 0 1} facets for excellent visible-light photocatalytic activity were prepared by a facile one-pot hydrothermal reaction strategy using tetrabutyl titanate (TBT) as titanium source, hydrofluoric acid (HF) as structure-directing agent and zinc powder (Zn) as reductant. The synthesized catalysts were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectra (XPS), diffuse reflectance spectrum (DRS) and nitrogen adsorption–desorption isotherms. The photocatalytic activity of the photocatalyst was evaluated by measure the formation rate of photo-induced hydroxyl radicals (·OH) under visible-light irradiation (λ = 420 ± 10 nm) using coumarin as a probe. It was found that the presence of zinc shows little effect on the morphology, phase structure, BET surface areas and pore structure. However, the addition of Zn powder resulted in the formation of Ti{sup 3+} self-doped anatase TiO{sub 2} nanosheets with dominant {0 0 1} facets, which is responsible for the enhanced visible-light photocatalytic activity. The sample prepared with zinc/TBT molar ratio of 0.3 showed the highest visible-light photocatalytic activity, which is 1.9 times higher than that of commercial P25 TiO{sub 2}.

  12. Structural, optical, and magnetic properties of polycrystalline Co-doped TiO{sub 2} synthesized by solid-state method

    Energy Technology Data Exchange (ETDEWEB)

    Bouaine, Abdelhamid, E-mail: abdelhamidfethi@yahoo.fr [Laboratoire d' Etude des Materiaux (LEM), Departement de Physique, Faculte des Sciences Exactes et des Sciences de la Nature et de la vie, Universite de Jijel, cite Oued-Aissa, B.P 98, Jijel 18000 (Algeria); Institut de Physique et Chimie des Materiaux de Strasbourg (IPCMS), UMR 7504 CNRS - UdS, 23 rue du Loess, B.P. 43, 67034 Strasbourg Cedex 2 (France); Schmerber, G.; Ihiawakrim, D.; Derory, A. [Institut de Physique et Chimie des Materiaux de Strasbourg (IPCMS), UMR 7504 CNRS - UdS, 23 rue du Loess, B.P. 43, 67034 Strasbourg Cedex 2 (France)

    2012-11-01

    Highlights: Black-Right-Pointing-Pointer Influence of Co doping on the TiO{sub 2} tetragonal structure. Black-Right-Pointing-Pointer Decrease of the energy band gap after doping with Co atoms. Black-Right-Pointing-Pointer Appearance of ferromagnetism in Co-doped TiO{sub 2} diluted magnetic semiconductors. - Abstract: We have used a solid-state method to synthesize polycrystalline Co-doped TiO{sub 2} diluted magnetic semiconductors (DMSs) with Co concentrations of 0, and 0.5 at.%. X-ray diffraction patterns reveal that Co doped TiO{sub 2} crystallizes in the rutile tetragonal structure with no additional peaks. Transmission electron microscopy (TEM) did not indicate the presence of magnetic parasitic phases and confirmed that Co ions are uniformly distributed inside the samples. Optical absorbance measurements showed an energy band gap which decreases after doping with the Co atoms into the TiO{sub 2} matrix. Magnetization measurements revealed a paramagnetic behavior for the as-prepared Co-doped TiO{sub 2} and a ferromagnetic behavior for the same samples after annealed under a mixture of H{sub 2}/N{sub 2} atmosphere.

  13. Photocatalytic properties of P25-doped TiO2 composite film synthesized via sol-gel method on cement substrate.

    Science.gov (United States)

    Guo, Xiang; Rao, Lei; Wang, Peifang; Wang, Chao; Ao, Yanhui; Jiang, Tao; Wang, Wanzhong

    2018-04-01

    TiO 2 films have received increasing attention for the removal of organic pollutants via photocatalysis. To develop a simple and effective method for improving the photodegradation efficiency of pollutants in surface water, we herein examined the preparation of a P25-TiO 2 composite film on a cement substrate via a sol-gel method. In this case, Rhodamine B (RhB) was employed as the target organic pollutant. The self-generated TiO 2 film and the P25-TiO 2 composite film were characterized by X-ray diffraction (XRD), N 2 adsorption/desorption measurements, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and diffuse reflectance spectroscopy (DRS). The photodegradation efficiencies of the two films were studied by RhB removal in water under UV (ultraviolet) irradiation. Over 4day exposure, the P25-TiO 2 composite film exhibited higher photocatalytic performance than the self-generated TiO 2 film. The photodegradation rate indicated that the efficiency of the P25-TiO 2 composite film was enhanced by the addition of the rutile phase Degussa P25 powder. As such, cooperation between the anatase TiO 2 and rutile P25 nanoparticles was beneficial for separation of the photo-induced electrons and holes. In addition, the influence of P25 doping on the P25-TiO 2 composite films was evaluated. We found that up to a certain saturation point, increased doping enhanced the photodegradation ability of the composite film. Thus, we herein demonstrated that the doping of P25 powders is a simple but effective strategy to prepare a P25-TiO 2 composite film on a cement substrate, and the resulting film exhibits excellent removal efficiency in the degradation of organic pollutants. Copyright © 2017. Published by Elsevier B.V.

  14. Low temperature fabrication of V-doped TiO2 nanoparticles, structure and photocatalytic studies

    International Nuclear Information System (INIS)

    Liu Baoshun; Wang Xuelai; Cai Guofa; Wen Liping; Song Yanbao; Zhao Xiujian

    2009-01-01

    V-doped TiO 2 nanoparticles were synthesized at low temperature and characterized by X-ray diffraction (XRD), Raman spectroscopy (RS), transmission electron microscopy (TEM), Brunauer-Emmet-Teller (BET), X-ray photoelectron spectroscopy (XPS), UV-vis spectroscopy, and photoluminescence (PL) spectroscopy, respectively. It is found the nanoparticle shape changed from needle, to short stick and then to cubic with the increase of doped V concentration, which was also accompanied by the improvement of crystallinity. The specific surface area (S BET ) decreased with increasing V content. It is confirmed that V ions can be doped in TiO 2 by substituting Ti 4+ ions, which suppressed the CB → VB and surface recombination of photoinduced electrons and holes, and a relation was found between the PL spectra and the UV photocatalytic activity. There was an optimum V content for the V-doped TiO 2 to present the best UV-light induced photoactivity, but they were visible-inactive. At last, the effect of the doping V as trapping centers on photocatalysis was investigated in detail, and used to explain the difference between the photocatalysis under the illumination of UV light and visible light.

  15. Inverted organic solar cells with solvothermal synthesized vanadium-doped TiO2 thin films as efficient electron transport layer

    Institute of Scientific and Technical Information of China (English)

    Mehdi Ahmadi; Sajjad Rashidi Dafeh; Samaneh Ghazanfarpour; Mohammad Khanzadeh

    2017-01-01

    We investigated the effects of using different thicknesses of pure and vanadium-doped thin films of TiO2 as the electron transport layer in the inverted configuration of organic photovoltaic cells based on poly (3-hexylthiophene) P3HT:[6-6] phenyl-(6) butyric acid methyl ester (PCBM).1% vanadium-doped TiO2 nanoparticles were synthesized via the solvothermal method.Crystalline structure,morphology,and optical properties of pure and vanadium-doped TiO2 thin films were studied by different techniques such as x-ray diffraction,scanning electron microscopy,transmittance electron microscopy,and UV-visible transmission spectrum.The doctor blade method which is compatible with roll-2-roll printing was used for deposition of pure and vanadium-doped TiO2 thin films with thicknesses of 30 nm and 60 nm.The final results revealed that the best thickness of TiO2 thin films for our fabricated cells was 30 nm.The cell with vanadium-doped TiO2 thin film showed slightly higher power conversion efficiency and great Jsc of 10.7 mA/cm2 compared with its pure counterpart.In the cells using 60 nm pure and vanadium-doped TiO2 layers,the cell using the doped layer showed much higher efficiency.It is remarkable that the extemal quantum efficiency of vanadium-doped TiO2 thin film was better in all wavelengths.

  16. Study on mechanism of photocatalytic performance of La-doped TiO2/Ti photoelectrodes by theoretical and experimental methods

    International Nuclear Information System (INIS)

    Xin Yanjun; Liu Huiling

    2011-01-01

    TiO 2 photoelectrodes with various nanostructures have been successfully prepared by the anodization method. The morphology, microstructure and optical properties of as-prepared photoelectrodes were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), ultraviolet/visible light diffuse reflectance spectra (UV/vis/DRS), surface photovoltage spectroscopy (SPS) and photocurrent. The electronic structure and optical properties of La doped/undoped TiO 2 photoelectrodes with different crystal structures were calculated by the density function theory. The photocatalytic and photoelectrocatalytic activities of as-prepared photoelectrodes were evaluated. The results showed that the anodization potentials played a crucial role in the surface morphology and microstructure. Both results of theoretical calculations and experimental tests demonstrated that La-doped photoelectrodes were more sensitive to light than undoped one. The difference of photoelectrodes performance was ascribed to the crystal configuration, impurity energy levels and long-range orientation moving of photogenerated carriers. - Graphical abstract: Photophysical chemistry processes in as-prepared TiO 2 photoelectrodes. Overall scheme of TiO 2 photoelectrodes: (A) movement of photoelectrons and holes without bias potentials; (B) movement of photoelectrons and holes at applied bias potentials; (a) and (b) were the transmission of photogenerated electrons and holes of local enlargement of (A) (black open circle): (a) photoelectrons movement in P-TiO 2 photoelectrodes and La-TiO 2 photoelectrodes, the red dot line denotes the top of valence band (VB) and the bottom of conduction band (CB) of pure photoelectrodes; (b) photoelectrons movement in P-160 and La-160 TiO 2 photoelectrodes (mixed crystal phase). The number refers to as follows: (1) transmission process of photoelectrons and holes; (2) recombination process of photoelectrons and holes. Arrows represent the moving direction of

  17. Magnetic and structural study of Cu-doped TiO2 thin films

    International Nuclear Information System (INIS)

    Torres, C.E. Rodriguez; Golmar, F.; Cabrera, A.F.; Errico, L.; Navarro, A.M. Mudarra; Renteria, M.; Sanchez, F.H.; Duhalde, S.

    2007-01-01

    Transparent pure and Cu-doped (2.5, 5 and 10 at.%) anatase TiO 2 thin films were grown by pulsed laser deposition technique on LaAlO 3 substrates. The samples were structurally characterized by X-ray absorption spectroscopy and X-ray diffraction. The magnetic properties were measured using a SQUID. All films have a FM-like behaviour. In the case of the Cu-doped samples, the magnetic cycles are almost independent of the Cu concentration. Cu atoms are forming CuO and/or substituting Ti in TiO 2 . The thermal treatment in air promotes the CuO segregation. Since CuO is antiferromagnetic, the magnetic signals present in the films could be assigned to Cu substitutionally replacing cations in TiO 2

  18. Preparation of Fluorine-Doped TiO2 Photocatalysts with Controlled Crystalline Structure

    Directory of Open Access Journals (Sweden)

    N. Todorova

    2008-01-01

    Full Text Available Nanocrystalline F-doped TiO2 powders were prepared by sol-gel route. The thermal behavior of the powders was recorded by DTA/TG technique. The crystalline phase of the fluorinated TiO2 powders was determined by X-ray diffraction technique. It was demonstrated that F-doping using CF3COOH favors the formation of rutile along with anatase phase even at low temperature. Moreover, the rutile's phase content increases with the increase of the quantity of the fluorine precursor in the starting solution. The surface area of the powders and the pore size distribution were studied by N2 adsorption-desorption using BET and BJH methods. X-ray photoelectron spectroscopy (XPS revealed that the fluorine is presented in the TiO2 powders mainly as metal fluoride in quantities ∼16 at %. The F-doped TiO2 showed a red-shift absorption in UV-vis region which was attributed to the increased content of rutile phase in the powders. The powders exhibited enhanced photocatalytic activity in decomposition of acetone.

  19. Synthesis of Br-doped TiO{sub 2} hollow spheres with enhanced photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Qianqian; Zhu, Shengli, E-mail: slzhu@tju.edu.cn; Liang, Yanqin; Cui, Zhenduo; Yang, Xianjin [Tianjin University, School of Materials Science and Engineering (China); Liang, Chunyong [Hebei University of Technology, Research Institute for Energy Equipment Materials (China); Inoue, Akihisa [Tianjin University, School of Materials Science and Engineering (China)

    2017-02-15

    The Br-doped hollow TiO{sub 2} photocatalysts were prepared by a simple hydrothermal process on the carbon sphere template following with calcination at 400 °C. The structure and properties of photocatalysts were characterized by X-ray diffraction, Raman spectrum, scanning electron microscope, transmission electron microscopy, N{sub 2} desorption–adsorption, UV–Vis spectroscopy, and X-ray photoelectron spectroscopy. The TiO{sub 2} hollow spheres are in diameter of 500 nm with shell thickness of 50 nm. The shell is composed of small anatase nanoparticles with size of about 10 nm. The TiO{sub 2} hollow spheres exhibit high crystalline and high surface area of 89.208 m{sup 2}/g. With increasing content of Br doping, the band gap of TiO{sub 2} hollow spheres decreased from 2.85 to 1.75 eV. The formation of impurity band in the band gap would narrow the band gap and result in the red shift of absorption edge from 395 to 517 nm, which further enhances the photocatalytic activity. The appropriate Br doping improves the photocatlytic activity significantly. The TiO{sub 2} hollow spheres with 1.55% Br doping (0.5Br-TiO{sub 2}) exhibit the highest photocatalytic activity under full light. More than 98% of RhB, MO, and MB can be photodegraded using 0.5Br-TiO{sub 2} with concentration of 10 mg/L in 40, 30, and 30 min, respectively. The degradation rate of Br-doped photocatalysts was 40% faster than undoped ones.

  20. Characterization and improved solar light activity of vanadium doped TiO2/diatomite hybrid catalysts.

    Science.gov (United States)

    Wang, Bin; Zhang, Guangxin; Leng, Xue; Sun, Zhiming; Zheng, Shuilin

    2015-03-21

    V-doped TiO2/diatomite composite photocatalysts with different vanadium concentrations were synthesized by a modified sol-gel method. The diatomite was responsible for the well dispersion of TiO2 nanoparticles on the matrix and consequently inhibited the agglomeration. V-TiO2/diatomite hybrids showed red shift in TiO2 absorption edge with enhanced absorption intensity. Most importantly, the dopant energy levels were formed in the TiO2 bandgap due to V(4+) ions substituted to Ti(4+) sites. The 0.5% V-TiO2/diatomite photocatalyst displayed narrower bandgap (2.95 eV) compared to undoped sample (3.13 eV) and other doped samples (3.05 eV) with higher doping concentration. The photocatalytic activities of V doped TiO2/diatomite samples for the degradation of Rhodamine B under stimulated solar light illumination were significantly improved compared with the undoped sample. In our case, V(4+) ions incorporated in TiO2 lattice were responsible for increased visible-light absorption and electron transfer to oxygen molecules adsorbed on the surface of TiO2 to produce superoxide radicals ˙O2(-), while V(5+) species presented on the surface of TiO2 particles in the form of V2O5 contributed to e(-)-h(+) separation. In addition, due to the combination of diatomite as support, this hybrid photocatalyst could be separated from solution quickly by natural settlement and exhibited good reusability. Copyright © 2014 Elsevier B.V. All rights reserved.

  1. Mo-doped Gray Anatase TiO2: Lattice Expansion for Enhanced Sodium Storage

    International Nuclear Information System (INIS)

    Liao, Hanxiao; Xie, Lingling; Zhang, Yan; Qiu, Xiaoqing; Li, Simin; Huang, Zhaodong; Hou, Hongshuai; Ji, Xiaobo

    2016-01-01

    Gray-colored Mo 6+ -doped anatase TiO 2 is prepared uniformly with particle size of 10–20 nm, and is firstly employed as anode material in sodium-ion batteries (SIBs), presenting excellent electrochemical performances. It delivered reversible specific capacities of 231.8 mAh g −1 at 0.1 C (33.5 mA g −1 ) after 100 cycles and 108.3 mAh g −1 at 5 C (1.68 A g −1 ), comparing to 170.5 mAh g −1 at 0.1 C and only 41.7 mAh g −1 at 5C for the bare TiO 2 . The improved electrochemical performances might be beneficial from the doping of Mo 6+ , which can effectively enhance the conductivity of TiO 2 resulting from induced conduction band electrons, interstitial oxygen defects and vacancies. In addition, the doping can also lead to the lattice expansion, which can facilitate the diffusion of Na + . In combination with natural abundance and environmental benignity, Mo 6+ -doped TiO 2 can be expected to be utilized as an anode material for enhanced sodium storage.

  2. Heat treatment effect on the physical properties of cobalt doped TiO{sub 2} sol–gel materials

    Energy Technology Data Exchange (ETDEWEB)

    Samet, L., E-mail: lolwasamet@gmail.com [Institut Préparatoires aux Etudes d' Ingénieurs d' El-Manar, Université Tunis El Manar, Campus Universitaire, 2092 El Manar (Tunisia); Laboratoire de Photovoltaique de Semi-conducteur et de Nanostructure, Centre de Recherches et des Technologies de l' Energie, Technopole borj cedria, Bp 95, hammamm lif 2050 (Tunisia); Ben Nasseur, J.; Chtourou, R. [Laboratoire de Photovoltaique de Semi-conducteur et de Nanostructure, Centre de Recherches et des Technologies de l' Energie, Technopole borj cedria, Bp 95, hammamm lif 2050 (Tunisia); March, K.; Stephan, O. [Laboratoire de Physique des Solides, UMR 8502 CNRS - Université Paris-Sud, Bât 510, 91405 Orsay cedex (France)

    2013-11-15

    Cobalt doped and undoped TiO{sub 2} powders have been prepared by sol–gel technique and annealed at temperatures ranging from 400 °C to 1000 °C. The effects of annealing temperature on the structural, morphological and optical properties have been characterized by X-ray diffraction, transmission electron microscopy, electron energy-loss spectroscopy and diffuse reflectance spectroscopy. For all doped samples there is a general reduction of the band gap energy, in comparison with undoped samples prepared in the same conditions. More specifically, experimental results indicate that cobalt doping, occurring as Co{sup 2+} ion insertion into the TiO{sub 2} (Ti{sup 4+}) host lattice, inhibits the growth of the crystallites and delays the phase transformation from anatase to rutile. Moreover, at high temperature, a secondary phase (CoTiO{sub 3}) is found to coexist with highly crystalline rutile. These structural characteristics are discussed in relation with the observed general trends for the optical properties. - Highlights: • Cobalt doped and undoped TiO{sub 2} powders have been prepared by sol–gel route. • Doping makes the band gap narrower. • Doping delays the phase transformation from anatase to rutile. • Doping inhibits the growth of the crystallites. • At high annealing temperature a CoTiO{sub 3} phase coexists with highly crystalline rutile.

  3. Preparation and characterization of doped TiO2 nanofibers by coaxial electrospining combined with sol–gel process

    International Nuclear Information System (INIS)

    Tong, Haixia; Tao, Xican; Wu, Daoxin; Zhang, Xiongfei; Li, Dan; Zhang, Ling

    2014-01-01

    Graphical abstract: The surface of the precursor of Fe/TiO 2 nanofibers are smoother than that of Fe /TiO 2 nanofibers. After calcined at 500 °C, the tubers on the surface of the nanofibers become more obvious, and which also provides a direct proof for the dopant of Fe element. -- Highlights: • N, Fe, and W doped TiO 2 nanofibers have been fabricated by coaxial electrospining. • The dopant has obvious influences on the surface topographies and crystal structures. • Fe doping can make remarkable topography changes and easy formation of rutile TiO 2 . • The maximum doping amount of W in TiO 2 nanofibers is less than 10% under 500 °C. -- Abstract: N, Fe, and W doped TiO 2 nanofibers were fabricated by coaxial electrospining and directly annealing polyvinylpyrrolidone (PVP)/Tetrabutyl titanate (TBT) composite nanofibers. The crystal structure, morphology, and surface composition of the doped TiO 2 nanofibers were investigated by the X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) respectively. The results show that the dopants have different influence on the surface topographies, the crystal structures and the transformation of anatase to rutile of TiO 2 nanofibers. Fe dopant promotes bigger influence on topographies, phase transformation and crystallite growth of TiO 2 nanofibers than that of either N or W dopant

  4. A novel single-step synthesis of N-doped TiO2 via a sonochemical method

    International Nuclear Information System (INIS)

    Wang, Xi-Kui; Wang, Chen; Guo, Wei-Lin; Wang, Jin-Gang

    2011-01-01

    Graphical abstract: The N-doped anatase TiO 2 nanoparticles were synthesized by sonochemical method. The as-prepared sample is characterized by XRD, TEM, XPS and UV-Vis DRS. The photocatalytic activity of the photocatalyst was evaluated by the photodegradation of an azo dye direct sky blue 5B. Highlights: → A novel singal-step sonochemical synthesis method for the preparation of anatase N-doped TiO 2 nanocrystalline at low temperature has been devoleped. → The as-prepared sample is characterized by XRD, TEM, XPS and UV-Vis DRS. → The photodegradation of azo dye direct sky blue 5 showed that the N-doped TiO 2 catalyst is of high visible-light photocatalytic activity. -- Abstract: A novel single-step synthetic method for the preparation of anatase N-doped TiO 2 nanocrystalline at low temperature has been devoleped. The N-doped anatase TiO 2 nanoparticles were synthesized by sonication of the solution of tetraisopropyl titanium and urea in water and isopropyl alcohol at 80 o C for 150 min. The as-prepared sample was characterized by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy and UV-vis absorption spectrum. The product structure depends on the reaction temperature and reaction time. The photocatalytic activity of the as-prepared photocatalyst was evaluated via the photodegradation of an azo dye direct sky blue 5B. The results show that the N-doped TiO 2 nanocrystalline prepared via sonication exhibit an excellent photocatalytic activity under UV light and simulated sunlight.

  5. Synthesis and characterization of TiO2 photocatalyst doped by transition metal ions (Fe3+, Cr3+ and V5+)

    International Nuclear Information System (INIS)

    Tuan Vu, Anh; Linh Bui, Thi Hai; Cuong Tran, Manh; Phuong Dang, Tuyet; Hoa Tran, Thi Kim; Tuan Nguyen, Quoc

    2010-01-01

    Nano TiO 2 was synthesized by the hydrothermal method. The sample was doped with transition metal ions (V, Cr and Fe) and non-metal (N). Doped TiO 2 samples were characterized by x-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM) and UV-Vis diffuse reflectance spectroscopy (UV-Vis). Photocatalytic activity in the mineralization of xylene (vapor phase), methylene blue and active dyer PR (liquid phase) was tested. In comparison with non-doped TiO 2 , V-, Cr-, Fe-doped TiO 2 and N-doped TiO 2 samples exhibited much higher photocatalytic activity using visible light instead of UV

  6. Controllable nitrogen doping in as deposited TiO{sub 2} film and its effect on post deposition annealing

    Energy Technology Data Exchange (ETDEWEB)

    Deng, Shaoren; Devloo-Casier, Kilian; Devulder, Wouter; Dendooven, Jolien; Deduytsche, Davy; Detavernier, Christophe, E-mail: Christophe.Detavernier@ugent.be [Department of Solid State Sciences, Ghent University, Krijgslaan 281/S1, B-9000 Gent (Belgium); Verbruggen, Sammy W. [Department of Bio-Engineering Sciences, University of Antwerp, Groenenborgerlaan 171, B-2020 Antwerp, Belgium and Center for Surface Chemistry and Catalysis, KU Leuven, Kasteelpark Arenberg 23, B-3001 Heverlee (Belgium); Lenaerts, Silvia [Department of Bio-Engineering Sciences, University of Antwerp, Groenenborgerlaan 171, B-2020 Antwerp (Belgium); Martens, Johan A. [Center for Surface Chemistry and Catalysis, KU Leuven, Kasteelpark Arenberg 23, B-3001 Heverlee (Belgium); Van den Berghe, Sven [SCK-CEN, Boeretang 200, B-2400 Mol (Belgium)

    2014-01-15

    In order to narrow the band gap of TiO{sub 2}, nitrogen doping by combining thermal atomic layer deposition (TALD) of TiO{sub 2} and plasma enhanced atomic layer deposition (PEALD) of TiN has been implemented. By altering the ratio between TALD TiO{sub 2} and PEALD TiN, the as synthesized TiO{sub x}N{sub y} films showed different band gaps (from 1.91 eV to 3.14 eV). In situ x-ray diffraction characterization showed that the crystallization behavior of these films changed after nitrogen doping. After annealing in helium, nitrogen doped TiO{sub 2} films crystallized into rutile phase while for the samples annealed in air a preferential growth of the anatase TiO{sub 2} along (001) orientation was observed. Photocatalytic tests of the degradation of stearic acid were done to evaluate the effect of N doping on the photocatalytic activity.

  7. Concurrent doping effect of Ti and nano-diamond on flux pinning of MgB2

    International Nuclear Information System (INIS)

    Zhao, Y.; Ke, C.; Cheng, C.H.; Feng, Y.; Yang, Y.; Munroe, P.

    2010-01-01

    Nano-diamond and titanium concurrently doped MgB 2 nanocomposites have been prepared by solid state reaction method. The effects of carbon and Ti concurrent doping on J c -H behavior and pinning force scaling features of MgB 2 have been investigated. Although T c was slightly depressed, J c of MgB 2 have been significantly improved by the nano-diamond doping, especially in the high field region. In the mean time, the J c value in low field region is sustained though concurrent Ti doping. Microstructure analysis reveals that when nano-diamond was concurrently doped with titanium in MgB 2 , a unique nanocomposite in which TiB 2 forms a thin layer surrounding MgB 2 grains whereas nano-diamond particles were wrapped inside the MgB 2 grains. Besides, nano-diamond doping results in a high density stress field in the MgB 2 samples, which may take responsibility for the Δκ pinning behavior in the carbon-doped MgB 2 system.

  8. Low-temperature preparation of rutile-type TiO2 thin films for optical coatings by aluminum doping

    Science.gov (United States)

    Ishii, Akihiro; Kobayashi, Kosei; Oikawa, Itaru; Kamegawa, Atsunori; Imura, Masaaki; Kanai, Toshimasa; Takamura, Hitoshi

    2017-08-01

    A rutile-type TiO2 thin film with a high refractive index (n), a low extinction coefficient (k) and small surface roughness (Ra) is required for use in a variety of optical coatings to improve the controllability of the reflection spectrum. In this study, Al-doped TiO2 thin films were prepared by pulsed laser deposition, and the effects of Al doping on their phases, optical properties, surface roughness and nanoscale microstructure, including Al distribution, were investigated. By doping 5 and 10 mol%Al, rutile-type TiO2 was successfully prepared under a PO2 of 0.5 Pa at 350-600 °C. The nanoscale phase separation in the Al-doped TiO2 thin films plays an important role in the formation of the rutile phase. The 10 mol%Al-doped rutile-type TiO2 thin film deposited at 350 °C showed excellent optical properties of n ≈ 3.05, k ≈ 0.01 (at λ = 400 nm) and negligible surface roughness, at Ra ≈ 0.8 nm. The advantages of the superior optical properties and small surface roughness of the 10 mol%Al-doped TiO2 thin film were confirmed by fabricating a ten-layered dielectric mirror.

  9. Synthesis of Nano-Ilmenite (FeTiO3) doped TiO2/Ti Electrode for Photoelectrocatalytic System

    Science.gov (United States)

    Hikmawati; Watoni, A. H.; Wibowo, D.; Maulidiyah; Nurdin, M.

    2017-11-01

    Ilmenite (FeTiO3) doped on Ti and TiO2/Ti electrodes were successfully prepared by using the sol-gel method. The structure, morphology, and optical properties of FeTiO3 are characterized by XRD, UV-Vis DRS, and SEM. The FeTiO3 and TiO2 greatly affect the photoelectrocatalysis performance characterized by Linear Sweep Voltammetry (LSV) and Cyclic Voltammetry (CV). The characterization result shows a band gap of FeTiO3 is 2.94 eV. XRD data showed that FeTiO3 formed at 2θ were 35.1° (110), 49.9° (024), and 61.2° (214). The morphology of FeTiO3/Ti and FeTiO3.TiO2/Ti using SEM shows that the formation of FeTiO3 thin layer signifies the Liquid Phase Deposition method effectively in the coating process. Photoelectrochemical (PEC) test showed that FeTiO3.TiO2/Ti electrode was highly oxidation responsive under visible light compared to the FeTiO3/Ti electrodes i.e. 7.87×10-4 A and 9.87×10-5 A. Degradation test of FeTiO3/Ti and FeTiO3.TiO2/Ti electrodes on titan yellow showed that the percentages of degradation with photoelectrocatalysis at 0.5 mg/L were 41% and 43%, respectively.

  10. Fabrication and electrical investigations of Pb-doped BaTiO_3 ceramics

    International Nuclear Information System (INIS)

    Sareecha, N.; Shah, W.A.; Maqsood, A.; Anis-ur-Rehman, M.; Latif Mirza, M.

    2017-01-01

    Electrical properties of Pb doped BaTiO_3; PBT are investigated in the wide range of temperatures (40–700 °C) at 1 kHz frequency. PBT ceramics were fabricated through solid state sintering method. Pre fired BaTiO_3 prepared with Ba/Ti molar ratio of 0.98 was doped with PbCO_3 (<1 mole %). XRD patterns indicated perovskite phase with tetragonal structures (P4mm). Morphological studies (SEM) revealed grain development with increasing lead contents. With lead doping and its variation, Curie temperature (T_C) was shifted from 120 to 200 °C with broad dielectric constant peaks and dielectric anomalies with relaxor behavior were observed. Resistivity decreased with increasing temperature, all specimens showed semiconductor behavior with negative temperature coefficient of resistivity (NTCR) characteristics. Mobility of electrons increased with thermal activation due to hopping of charge carriers from one site to another. Ohmic conductivities and associated activation energies were evaluated by impedance spectroscopy. Conductivity followed the Arrhenius law with E_a = 1.187–1.169 eV which can be attributed to the ionic conduction owning to doubly ionized oxygen vacancies. Well-defined hysteresis P-E loops measured at room temperature depicted ferroelectric properties of the materials. - Graphical abstract: Temperature dependence of dielectric constant (Ɛ′) and resistivity (ρ) for pure and Pb-doped BaTiO_3 ceramics at 1 k Hz frequency. - Highlights: • Pb-doped BaTiO_3ceramics were fabricated through solid state sintering. • Electrical properties were studied at the temperatures 40–700 °C at 1 kHz. • Specimens showed negative temperature coefficient of resistivity characteristics. • Conductivity followed the Arrhenius law with E_a = 1.187–1.169 eV. • Ionic conduction was supposed to be responsible for conduction process.

  11. Investigation of semi-insulating InP co-doped with Ti and various acceptors for use in X-ray detection

    International Nuclear Information System (INIS)

    Zdansky, K.; Gorodynskyy, V.; Kozak, H.; Pekarek, L.

    2005-01-01

    Semi-insulating InP single crystals co-doped with Zn and Ti and co-doped with Ti and Mn were grown by Czochralski technique. Wafers of these crystals were annealed for a long time at a high temperature and cooled slowly. The samples were characterized by temperature dependent resistivity and Hall coefficient measurements. The binding energies of Ti in semi-insulating InP co-doped with Ti and Zn and co-doped with Ti and Mn were found to differ which shows that Ti may occupy different sites in InP. The curves of Hall coefficient vs. reciprocal temperature deviate from straight lines at low temperatures due to electron and hole mixed conductance. The value of resistivity of the annealed semi-insulating InP co-doped with Ti and Mn reaches high resistivity at a reduced temperature easily achievable by thermo-electric devices which could make this material useable in X-ray detection. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  12. Structure and high photocatalytic activity of (N, Ta)-doped TiO{sub 2} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Le, N. T. H.; Lam, V. D.; Manh, D. H.; Hong, L. V. [Institute of Materials Science, Vietnam Academy of Science and Technology, 18-Hoang Quoc Viet, Hanoi (Viet Nam); Thanh, T. D., E-mail: thanhxraylab@yahoo.com, E-mail: scyu@cbnu.ac.kr [Institute of Materials Science, Vietnam Academy of Science and Technology, 18-Hoang Quoc Viet, Hanoi (Viet Nam); Department of Physics, Chungbuk National University, Cheongju 28644 (Korea, Republic of); Pham, V.-T. [Center for Quantum Electronics, Institute of Physics, Vietnam Academy of Science and Technology, Hanoi (Viet Nam); Synchrotron SOLEIL, L' Orme des Merisiers, Boîte Postale, 48, 91192 Gif-sur-Yvette Cedex (France); Phan, T. L.; Yu, S. C., E-mail: thanhxraylab@yahoo.com, E-mail: scyu@cbnu.ac.kr [Department of Physics, Chungbuk National University, Cheongju 28644 (Korea, Republic of); Anh, T. X. [Center for Quantum Electronics, Institute of Physics, Vietnam Academy of Science and Technology, Hanoi (Viet Nam); Le, T. K. C. [Institut des Sciences Moleculaires d' Orsay, CNRS, Univ Paris-Sud, 91405 Orsay Cedex (France); Thammajak, N. [Synchrotron Light Research Institute, 111 University Avenue, Muang, Nakhon Ratchasima 30000 (Thailand)

    2016-10-14

    A hydrothermal method was used to prepare three nano-crystalline samples of TiO{sub 2} (S1), N-doped TiO{sub 2} (S2), and (N, Ta)-codoped TiO{sub 2} (S3) with average crystallite sizes (D) of 13–25 nm. X-ray diffraction studies confirmed a single phase of the samples with a tetragonal/anatase structure. A slight increase in the lattice parameters was observed when N and/or Ta dopants were doped into the TiO{sub 2} host lattice. Detailed analyses of extended X-ray absorption spectra indicated that N- and/or Ta-doping into TiO{sub 2} nanoparticles influenced the co-ordination number and radial distance (R) of Ti ions in the anatase structure. Concerning their absorption spectra, (N, Ta)-doping narrowed the band gap (E{sub g}) of TiO{sub 2} from 3.03 eV for S1 through 2.94 eV for S2 to 2.85 eV for S3. Such results revealed the applicability of these nanoparticles in the photocatalytic field working in the ultraviolet (UV)-visible region. Among these, photocatalytic activity of S3 was the strongest. By using S3 as a catalyst powder, the degradation efficiency of methylene blue solution was about 99% and 93% after irradiation of UV-visible light for 75 min and visible-light for 180 min, respectively.

  13. Electrochemical characterization and redox behavior of Nb-doped SrTiO3

    DEFF Research Database (Denmark)

    Blennow Tullmar, Peter; Kammer Hansen, Kent; Wallenberg, L. Reine

    2009-01-01

    Sr-vacancy compensated Nb-doped SrTiO3 with the nominal composition Sr0.94Ti0.9Nb0.1O3 has been evaluated as a solid oxide fuel cell (SOFC) anode material in terms of redox stability and electrochemical properties. Sr0.94Ti0.9Nb0.1O3 has been synthesized with a recently developed modified glycine......-nitrate process. The phase purity and redox behavior have been analyzed with XRD and TGA. The electrochemical properties of Sr0.94Ti0.9Nb0.1O3 and a composite electrode of Sr0.94Ti0.9Nb0.1O3/YSZ have been investigated by electrochemical impedance spectroscopy (EIS) on cone shaped electrodes and on electrodes...... in a symmetrical cell configuration. The experiments indicated that the Nb-doped SrTiO3 electrodes were redox stable and showed a potential ability to be used as a part of a SOFC anode. The electrochemical activity appeared to be governed by the concentration of defect species (especially Ti3+ and V-0...

  14. Room temperature one-step synthesis of microarrays of N-doped flower-like anatase TiO2 composed of well-defined multilayer nanoflakes by Ti anodization

    Science.gov (United States)

    Wang, Chenglin; Wang, Mengye; Xie, Kunpeng; Wu, Qi; Sun, Lan; Lin, Zhiqun; Lin, Changjian

    2011-07-01

    Microarrays of N-doped flower-like TiO2 composed of well-defined multilayer nanoflakes were synthesized at room temperature by electrochemical anodization of Ti in NH4F aqueous solution. The TiO2 flowers were of good anatase crystallinity. The effects of anodizing time, applied voltage and NH4F concentration on the flower-like morphology were systematically examined. It was found that the morphologies of the anodized Ti were related to the anodizing time and NH4F concentration. The size and density of the TiO2 flowers could be tuned by changing the applied voltage. The obtained N-doped flower-like TiO2 microarrays exhibited intense absorption in wavelengths ranging from 320 to 800 nm. Under both UV and visible light irradiation, the photocatalytic activity of the N-doped flower-like TiO2 microarrays in the oxidation of methyl orange showed a significant increase compared with that of commercial P25 TiO2 film.

  15. Rapid Synthesis and Formation Mechanism of Core-Shell-Structured La-Doped SrTiO3 with a Nb-Doped Shell

    Directory of Open Access Journals (Sweden)

    Nam-Hee Park

    2015-07-01

    Full Text Available To provide a convenient and practical synthesis process for metal ion doping on the surface of nanoparticles in an assembled nanostructure, core-shell-structured La-doped SrTiO3 nanocubes with a Nb-doped surface layer were synthesized via a rapid synthesis combining a rapid sol-precipitation and hydrothermal process. The La-doped SrTiO3 nanocubes were formed at room temperature by a rapid dissolution of NaOH pellets during the rapid sol-precipitation process, and the Nb-doped surface (shell along with Nb-rich edges formed on the core nanocubes via the hydrothermal process. The formation mechanism of the core-shell-structured nanocubes and their shape evolution as a function of the Nb doping level were investigated. The synthesized core-shell-structured nanocubes could be arranged face-to-face on a SiO2/Si substrate by a slow evaporation process, and this nanostructured 10 μm thick thin film showed a smooth surface.

  16. Microstructural and dielectrical characterization of Ho doped BaTiO3 ceramics

    Directory of Open Access Journals (Sweden)

    Marjanović Miloš

    2014-01-01

    Full Text Available The Ho doped BaTiO3 ceramics, with different Ho2O3 content, ranging from 0.01 to 1.0 wt % Ho, were investigated regarding their microstructural and dielectric characteristics. Doped BaTiO3 were prepared using conventional solid state reaction and sintered at 1380°C for four hours. SEM analysis of Ho/BaTiO3 doped ceramics showed that the low doped samples exhibit mainly fairly uniform and homogeneous microstructure with the grain size ranged from 20-40 μm. In the samples with the higher dopant concentration the abnormal grain growth is inhibited and the grain size ranged between 2-10 μm. Measurements of dielectric properties were carried out as a function of temperature up to 180 °C at different frequencies. The samples doped with 0.01wt % of Ho, exhibit the high value of dielectric permittivity (εr = 2160 at room temperature. A nearly flat permittivity-response was obtained in specimens with higher additive content. Using a Curie-Weiss law and modified Curie-Weiss law the Curie constant (C, Curie temperature (Tc and a critical exponent of nonlinearity (g were calculated. The Curie temperature of doped samples were ranged from 128 to 130°C. The Curie constant for all series of samples decrease with increase of dopant concentration and the lowest values were observed on samples doped with 0.01 wt % of holmium. [Projekat Ministarstva nauke Republike Srbije, br. OI 172057: Directed synthesis, structure and properties of multifunctional materials i br. TR 32026

  17. Synthesis and characterization of Ag-doped TiO2 nanotubes on Ti-6Al-4V and Ti-6Al-7Nb alloy

    Science.gov (United States)

    Ulfah, Ika Maria; Bachtiar, Boy M.; Murnandityas, Arnita Rut; Slamet

    2018-05-01

    The present paper is focused on comparative behavior of nanotubes growth on Ti-6Al-4V and Ti-6Al-7Nb alloy using electrochemical anodization method. These alloys were anodized in electrolytes solution containing glycerol, water and 0.5wt.% of NH4F. Silver-doped TiO2 nanotubes were synthesized using photo-assisted deposition (PAD) at various Ag loading concentration in 0.05 M, 0.10 M, and 0.15 M. The phase composition and morphological characteristics were investigated by XRD and FESEM/EDX, respectively. The surface wettability was measured by contact angle meter. The results showed that TiO2 nanotubes can be grown on these surface alloys. XRD profiles revealed crystal formation of anatase, rutile and Ag on these surface alloys. According to FESEM images, the average nanotube diameter of Ti-6Al-4V alloy and Ti-6Al-7Nb alloy are 134 nm and 120 nm, respectively. EDX-Mapping analysis showed that Ag desposited over surface of TiO2 nanotubes. The surface wettability indicated hydrophilicity properties on Ti-4Al-4V alloy and Ti-6Al-7Nb alloy surface. This study may contribute to the development of silver-doped TiO2 nanotubes on Ti-6Al-4V alloy and Ti-6Al-7Nb alloy can be considered in various photocatalytic applications such as biomedical devicesdue to photocatalytic mechanism and antibacterial ability.

  18. Mn-doped CdS quantum dots sensitized hierarchical TiO2 flower-rod for solar cell application

    International Nuclear Information System (INIS)

    Yu, Libo; Li, Zhen; Liu, Yingbo; Cheng, Fa; Sun, Shuqing

    2014-01-01

    A double-layered TiO 2 film which three dimensional (3D) flowers grown on highly ordered self-assembled one dimensional (1D) TiO 2 nanorods was synthesized directly on transparent fluorine-doped tin oxide (FTO) conducting glass substrate by a facile hydrothermal method and was applied as photoanode in Mn-doped CdS quantum dots sensitized solar cells (QDSSCs). The 3D TiO 2 flowers with the increased surface areas can adsorb more QDs, which increased the absorption of light; meanwhile 1D TiO 2 nanorods beneath the flowers offered a direct electrical pathway for photogenerated electrons, accelerating the electron transfer rate. A typical type II band alignment which can effectively separate photogenerated excitons and reduce recombination of electrons and holes was constructed by Mn-doped CdS QDs and TiO 2 flower-rod. The incident photon-to-current conversion efficiency (IPCE) of the Mn-doped CdS/TiO 2 flower-rod solar cell reached to 40% with the polysulfide electrolyte filled in the solar cell. The power conversion efficiency (PCE) of 1.09% was obtained with the Mn-doped CdS/TiO 2 flower-rod solar cell under one sun illumination (AM 1.5G, 100 mW/cm 2 ), which is 105.7% higher than that of the CdS/TiO 2 nanorod solar cell (0.53%).

  19. Toxicological aspects of photocatalytic degradation of selected xenobiotics with nano-sized Mn-doped TiO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Ozmen, Murat, E-mail: murat.ozmen@inonu.edu.tr [Inonu University, Faculty of Science, Department of Biology, Malatya (Turkey); Güngördü, Abbas [Inonu University, Faculty of Science, Department of Biology, Malatya (Turkey); Erdemoglu, Sema [Inonu University, Faculty of Science, Department of Chemistry, Malatya (Turkey); Ozmen, Nesrin [Inonu University, Faculty of Education, Department of Science Teaching Program, Malatya (Turkey); Asilturk, Meltem [Akdeniz University, Department of Materials Science and Engineering, Antalya (Turkey)

    2015-08-15

    Highlights: • Undoped and Mn-doped TiO{sub 2} nanoparticles were synthesized and characterized. • The photocatalytic efficiency of the photocatalysts was evaluated for BPA and ATZ. • Toxicity of photocatalysts and photocatalytic by-products were determined. • Mn-doped TiO{sub 2} nanoparticles did not cause significant lethality on X. laevis. • Degradation of BPA caused a significant reduction of lethal effects. - Abstract: The toxic effects of two selected xenobiotics, bisphenol A (BPA) and atrazine (ATZ), were evaluated after photocatalytic degradation using nano-sized, Mn-doped TiO{sub 2}. Undoped and Mn-doped TiO{sub 2} nanoparticles were synthesized. The samples were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), UV–vis-diffuse reflectance spectra (DRS), X-ray fluorescence spectroscopy (XRF), and BET surface area. The photocatalytic efficiency of the undoped and Mn-doped TiO{sub 2} was evaluated for BPA and ATZ. The toxicity of the synthesized photocatalysts and photocatalytic by-products of BPA and ATZ was determined using frog embryos and tadpoles, zebrafish embryos, and bioluminescent bacteria. Possible toxic effects were also evaluated using selected enzyme biomarkers. The results showed that Mn-doped TiO{sub 2} nanoparticles did not cause significant lethality in Xenopus laevis embryos and tadpoles, but nonfiltered samples caused lethality in zebrafish. Furthermore, Mn-doping of TiO{sub 2} increased the photocatalytic degradation capability of nanoparticles, and it successfully degraded BPA and AZT, but degradation of AZT caused an increase of the lethal effects on both tadpoles and fish embryos. Degradation of BPA caused a significant reduction of lethal effects, especially after 2–4 h of degradation. However, biochemical assays showed that both Mn-doped TiO{sub 2} and the degradation by-products caused a significant change of selected biomarkers on X. laevis tadpoles; thus, the ecological risks of Mn-doped

  20. Effect of N_2 flow rate on the properties of N doped TiO_2 films deposited by DC coupled RF magnetron sputtering

    International Nuclear Information System (INIS)

    Peng, Shou; Yang, Yong; Li, Gang; Jiang, Jiwen; Jin, Kewu; Yao, TingTing; Zhang, Kuanxiang; Cao, Xin; Wang, Yun; Xu, Genbao

    2016-01-01

    N doped TiO_2 films were deposited on glass substrates at room temperature using DC coupled RF magnetron sputtering with a TiO_2 ceramic target. The influences of N_2 flow rate on the deposition rate, crystal structure, chemical composition and band gap of the deposited films were investigated by Optical profiler, X-ray diffraction, X-ray photoelectron spectroscope and ultraviolet-visible spectrophotometer. The film growth rate gradually decreased with increasing N_2 flow rate. As N_2 flow rate increased, the crystallization of the films deteriorated, and the films tended to form amorphous structure. XPS analysis revealed that N dopant atoms were added at the substitutional sites into TiO_2 lattice structure. FE-SEM results showed that the grain size of the film decreased and the crystallinity degraded as N_2 flow rate increases. In addition, N doping caused an obvious red shift in the optical absorption edge. - Highlights: • N doped TiO_2 films were deposited by DC coupled RF magnetron reactive sputtering. • As N_2 flow rate increases, the crystallization of the deposited films degrades. • The higher N_2 flow rate is beneficial to form more substituted N in the film. • N doping causes an obvious red shift in the absorption wavelength.

  1. Influence of nitrogen dopants on N-doped TiO2 electrodes and their applications in dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Guo Wei; Shen Yihua; Boschloo, Gerrit; Hagfeldt, Anders; Ma Tingli

    2011-01-01

    Highlights: → Three different types of nanocrystalline N-doped TiO 2 synthesized by several nitrogen dopants. → N-doped DSCs achieves a high conversion efficiency of 8.32%. → Ammonia acts as good nitrogen dopants. → Enhanced photocurrent of ca. 36% in N-doped DSCs. → Less charge are needed to get a high open-circuit voltage in N-doped films. - Abstract: Three different types of nanocrystalline, N-doped TiO 2 electrodes were synthesized using several nitrogen dopants through wet methods. The obtained nanocrystalline, N-doped TiO 2 electrodes possessed different crystallite sizes, surface areas, and N-doping amounts. Characterizations were performed to reveal the nitrogen-doping processes for the wet methods using ammonia, urea, and triethylamine as the nitrogen dopants. Additionally, a high conversion efficiency of 8.32% was achieved by the dye-sensitized solar cells, based on the N-doped TiO 2 electrodes. For instance, in comparison with the commercial P25 (5.76%) and pure anatase TiO 2 electrodes (7.14%), significant improvements (44% and 17%, respectively) in the efficiencies were obtained. The findings also indicated that the ammonia nitrogen dopant was more efficient than other two nitrogen dopants. The electron transports, electron lifetimes, and charge recombination in the dye-sensitized N-doped TiO 2 solar cells also differed from those in the pure TiO 2 -based dye-sensitized solar cells (DSCs). Specifically, an enhanced photocurrent of ca. 36% in N-doped DSCs resulted from the synergistic effects of the high dye uptake and the efficient electron transport. Moreover, the relationship between charge and voltage revealed that less charge was needed to get a high open-circuit voltage in the N-doping films.

  2. The effects of antimony doping on the surface structure of rutile TiO2(110)

    International Nuclear Information System (INIS)

    Bechstein, Ralf; Schuette, Jens; Kuehnle, Angelika; Kitta, Mitsunori; Onishi, Hiroshi

    2009-01-01

    Titanium dioxide represents a very important wide bandgap photocatalyst that is known to be sensitized to visible light by transition metal doping. Antimony doping has been demonstrated to provide photocatalytic activity when codoped with chromium at an optimum dopant ratio [Sb]/[Cr] of about 1.5. Here, the role of antimony doping on the surface structure of rutile TiO 2 (110) is studied using non-contact atomic force microscopy (NC-AFM) under ultra-high vacuum conditions. At first glance, the surface structure of antimony-doped TiO 2 (110) resembles the structure of pristine TiO 2 (110). However, in contrast to what is found in pristine TiO 2 (110), a dense layer of protruding features is observed upon antimony doping, which is tentatively ascribed to antimony-rich clusters. Moreover, homogeneously distributed holes are found on the surface, which differ in depth and shape depending on the preparation conditions. Holes with depths ranging from a few up to more than a hundred monatomic steps are observed. These holes are explained by surface segregation of antimony during annealing, as the ionic radius of Sb 3+ is considerably larger than the ionic radius of Ti 4+ . Our finding provides an indication of why an antimony concentration larger than the optimum ratio results in decreased photocatalytic activity. Moreover, controlling annealing temperature seems to constitute a promising strategy for creating nanosized holes on TiO 2 surfaces.

  3. Sulphur doped nanoparticles of TiO2

    Czech Academy of Sciences Publication Activity Database

    Szatmáry, Lórant; Bakardjieva, Snejana; Šubrt, Jan; Bezdička, Petr; Jirkovský, Jaromír; Bastl, Zdeněk; Brezová, V.; Korenko, M.

    2011-01-01

    Roč. 161, č. 1 (2011), s. 23-28 ISSN 0920-5861 R&D Projects: GA MŠk 1M0577 Institutional research plan: CEZ:AV0Z40400503; CEZ:AV0Z40320502 Keywords : photocatalyst * S-doped TiO2 * Thiourea Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 3.407, year: 2011

  4. High photocatalytic activity of hierarchical SiO2@C-doped TiO2 hollow spheres in UV and visible light towards degradation of rhodamine B.

    Science.gov (United States)

    Zhang, Ying; Chen, Juanrong; Hua, Li; Li, Songjun; Zhang, Xuanxuan; Sheng, Weichen; Cao, Shunsheng

    2017-10-15

    Ongoing research activities are targeted to explore high photocatalytic activity of TiO 2 -based photocatalysts for the degradation of environmental contaminants under UV and visible light irradiation. In this work, we devise a facile, cost-effective technique to in situ synthesize hierarchical SiO 2 @C-doped TiO 2 (SCT) hollow spheres for the first time. This strategy mainly contains the preparation of monodisperse cationic polystyrene spheres (CPS), sequential deposition of inner SiO 2 , the preparation of the sandwich-like CPS@SiO 2 @CPS particles, and formation of outer TiO 2 . After the one-step removal of CPS templates by calcination at 450°C, hierarchical SiO 2 @C-doped TiO 2 hollow spheres are in situ prepared. The morphology, hierarchical structure, and properties of SCT photocatalyst were characterized by TEM. SEM, STEM Mapping, BET, XRD, UV-vis spectroscopy, and XPS. Results strongly confirm the carbon doping in the outer TiO 2 lattice of SCT hollow spheres. When the as-synthesized SCT hollow spheres were employed as a photocatalyst for the degradation of Rhodamine B under visible-light and ultraviolet irradiation, the SCT photocatalyst exhibits a higher photocatalytic activity than commercial P25, effectively overcoming the limitations of poorer UV activity for many previous reported TiO 2 -based photocatalysts due to doping. Copyright © 2017 Elsevier B.V. All rights reserved.

  5. Hydrogen storage properties of the Zintl phase alloy SrAl{sub 2} doped with TiF{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Zhu Yunfeng, E-mail: yfzhu@njut.edu.c [College of Materials Science and Engineering, Nanjing University of Technology, 5 Xinmofan Road, Nanjing 210009 (China); Zhang Wei; Liu Zhibing; Li Liquan [College of Materials Science and Engineering, Nanjing University of Technology, 5 Xinmofan Road, Nanjing 210009 (China)

    2010-03-04

    In this paper, the structural and hydrogenation characteristics of TiF{sub 3}-doped Zintl phase alloy SrAl{sub 2} were studied by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and hydrogenation measurements. The results show that the hydrogenation kinetics of the Zintl phase alloy SrAl{sub 2} is improved greatly after doping with TiF{sub 3}. By adjusting the doping amount and ball milling time, the optimal doping conditions were obtained. The catalytic mechanism of TiF{sub 3} for the hydrogenation of SrAl{sub 2} was also investigated. SrAl{sub 2} does not react with TiF{sub 3} during the ball milling process. However, it reacts with TiF{sub 3} to form SrAl{sub 2}H{sub 2}, SrF{sub 2}, SrAl{sub 4} and Ti during the hydrogenation process, among which Ti plays an important role in the hydrogenation kinetics of SrAl{sub 2}.

  6. Fabrication of Ce/N co-doped TiO2/diatomite granule catalyst and its improved visible-light-driven photoactivity.

    Science.gov (United States)

    Chen, Yan; Liu, Kuiren

    2017-02-15

    Eliminating antibiotic remnants in aquatic environment has become one of the hottest topics among current research works. Thus, we prepared Ce, N co-doped TiO 2 /diatomite granule (CNTD-G) catalyst to provide a new method. As one typical antibiotics, oxytetracycline (OTC) was selected as the target pollutant to be degradated under visible light irradiation. The carrier diatomite helped the spread of TiO 2 nanoparticles onto its surface, and inhibited their agglomeration. The synergy of Ce and N dopants highly improved the visible-light-driven photoactivity of TiO 2 . The optimal doping amount and degradation conditions were determined. Besides, the effects of impurity ions were also investigated, including cations: Ca 2+ , Mg 2+ ; or anions: NO 3 - , SO 4 2- and PO 4 3- . The intermediates generated during degradation process were studied, and the mechanism of the photodegradation process was proposed. CNTD-G could be easily collected from the reactor, and showed excellent recyclability. Copyright © 2016 Elsevier B.V. All rights reserved.

  7. Interplay of dopants and defects in making Cu doped TiO{sub 2} nanoparticle a ferromagnetic semiconductor

    Energy Technology Data Exchange (ETDEWEB)

    Choudhury, Biswajit, E-mail: biswa.tezu@gmail.com [Department of Physics, Tezpur University, Napaam 784028, Assam (India); Choudhury, Amarjyoti [Department of Physics, Tezpur University, Napaam 784028, Assam (India); Borah, Debajit [Department of Chemical Engineering, Indian Institute of Technology Guwahati, Guwahati 781039, Assam (India)

    2015-10-15

    Here we have studied the role of oxygen defects and Cu dopants on ferromagnetism in Cu doped TiO{sub 2} nanoparticles with nominal Cu concentration of 2%, 4% and 6 mol%. Electron paramagnetic resonance (EPR) spectra analysis reveals the presence of Cu{sup 2+} in the distorted octahedral coordination of TiO{sub 2}. Cu d-states undergo strong p-d coupling with the valence band O 2p state of TiO{sub 2} resulting the extended absorption hump in the visible region. Photoluminescence results reveal the presence of oxygen defect related emission peaks in Cu doped TiO{sub 2}. Room temperature ferromagnetism is observed in all the Cu doped TiO{sub 2} nanoparticles. Saturation magnetization is the highest at 4 mol% and then there is a decrease in magnetization at 6 mol%. Ferromagnetism completely disappears on calcinations of 4% Cu doped TiO{sub 2} in air at 450 °C for 8 h. It is speculated that both oxygen vacancies and Cu d-states are involved in the room temperature ferromagnetism. Spin polarization occurs by the formation of bound magnetic polaron between electrons in Cu{sup 2+}d-states and the unpaired spins in oxygen vacancies. Presence of Cu{sup 2+}-Cu{sup 2+}d-d exchange interaction and Cu{sup 2+}-O{sup 2−}-Cu{sup 2+} antiferromagnetic superexchange interactions might have resulted in the reduction in magnetization at 6 mol% Cu. - Graphical abstract: Ferromagnetism in Cu doped TiO{sub 2} requires presence of both Cu dopant and oxygen vacancies. - Highlights: • Cu doped TiO{sub 2} nanoparticle displays room temperature ferromagnetism. • Ferromagnetism requires presence of both Cu and oxygen vacancies. • Antiferromagnetic interaction persists at high Cu dopant concentration. • Paramagnetism appears on air annealing of the doped system for longer period.

  8. Surface modification of sol–gel synthesized TiO{sub 2} nanoparticles induced by La-doping

    Energy Technology Data Exchange (ETDEWEB)

    Grujić-Brojčin, M., E-mail: myramyra@ipb.ac.rs [Institute of Physics, University of Belgrade, Pregrevica 118, 11080 Belgrade (Serbia); Armaković, S. [Department of Chemistry, Biochemistry and Environmental Protection, Faculty of Sciences, University of Novi Sad, Trg D. Obradovića 3, 21000 Novi Sad (Serbia); Tomić, N. [Institute of Physics, University of Belgrade, Pregrevica 118, 11080 Belgrade (Serbia); Abramović, B. [Department of Chemistry, Biochemistry and Environmental Protection, Faculty of Sciences, University of Novi Sad, Trg D. Obradovića 3, 21000 Novi Sad (Serbia); Golubović, A.; Stojadinović, B. [Institute of Physics, University of Belgrade, Pregrevica 118, 11080 Belgrade (Serbia); Kremenović, A. [Faculty of Mining and Geology, Laboratory for Crystallography, University of Belgrade, Đušina 7, 11000 Belgrade (Serbia); Babić, B. [Institute of Nuclear Sciences “Vinča”, University of Belgrade, 11001 Belgrade (Serbia); Dohčević-Mitrović, Z.; Šćepanović, M. [Institute of Physics, University of Belgrade, Pregrevica 118, 11080 Belgrade (Serbia)

    2014-02-15

    The influence of La-doping in the range of 0.5–6.0 mol% on structural and morphological properties of TiO{sub 2} nanopowders synthesized by sol–gel routine has been investigated by XRPD, AFM, EDS and BET measurements, as well as Raman spectroscopy. The XRPD and Raman measurements have revealed the anatase phase as dominant in all nanopowders, with crystallite size decreasing from ∼ 15 nm in pure TiO{sub 2} to ∼ 12 nm in La-doped samples. The BET data suggest that all samples are fully mesoporous, with mean pore diameters in the range of ∼ 6–8 nm. The specific surface area and the complexity of pore structure are greater in doped samples than in pure TiO{sub 2} sample. The spectroscopic ellipsometry has apparently shown that the band gap has been gradually increased with the increase of La content. The STM and STS techniques have been used successfully to evaluate the surface morphology and electronic properties of La-doped nanopowders. All investigated properties have been related to photocatalytic activity, tested in degradation of a metoprolol tartrate salt (0.05 mM), and induced by UV-radiation. All doped samples showed increased photocatalytic activity compared to pure TiO{sub 2}, among which the 0.65 mol% La-doped sample appeared to be the most efficient. - Highlights: • Effects of La-doping on structural, morphological and electronic properties of TiO{sub 2} nanopowders. • Surface morphology and electronic properties of La-doped nanopowders evaluated by STM/STS. • Spectroscopic ellipsometry shown gradual increase of bandgap with the increase of La content. • Photocatalytic activity of samples was tested in degradation of MET under UV light.

  9. Synergistic Effect of Fluorinated and N Doped TiO2 Nanoparticles Leading to Different Microstructure and Enhanced Photocatalytic Bacterial Inactivation

    Directory of Open Access Journals (Sweden)

    Irena Milosevic

    2017-11-01

    Full Text Available This work focuses on the development of a facile and scalable wet milling method followed by heat treatment to prepare fluorinated and/or N-doped TiO2 nanopowders with improved photocatalytic properties under visible light. The structural and electronic properties of doped particles were investigated by various techniques. The successful doping of TiO2 was confirmed by X-ray photoelectron spectroscopy (XPS, and the atoms appeared to be mainly located in interstitial positions for N whereas the fluorination is located at the TiO2 surface. The formation of intragap states was found to be responsible for the band gap narrowing leading to the faster bacterial inactivation dynamics observed for the fluorinated and N doped TiO2 particles compared to N-doped TiO2. This was attributed to a synergistic effect. The results presented in this study confirmed the suitability of the preparation approach for the large-scale production of cost-efficient doped TiO2 for effective bacterial inactivation.

  10. Photonic, and photocatalytic behavior of TiO{sub 2} mediated by Fe, CO, Ni, N doping and co-doping

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jia [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan (China); Zhao, Y.F. [Institute of Coordination Bond Metrology and Engineering, School of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Wang, T., E-mail: twang@zju.edu.cn [College of Electrical Engineering, Zhejiang University (China); Li, H., E-mail: Lihui02@tyut.edu.cn [College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan (China); Li, C., E-mail: canli1983@gmail.com [Institute of Coordination Bond Metrology and Engineering, School of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China)

    2015-12-01

    Fe, Co, Ni, or N addition could modulate the photonic and catalytic responses of TiO{sub 2} for photocatalysts applications. Their morphologies, structures, compositions and photocatalytic performance in the degradation of methylene blue were characterized by scanning electron microscopy, X-ray diffraction, UV–vis absorption spectroscopy, Raman spectra and X-ray photoelectron spectroscopy. The results showed that dopants affect the electronic transition energies by changing the optical band gap and the impurity absorption peaks of the specimens. Especially, co-doping enhances the visible-light photocatalytic activity of TiO{sub 2} by 4–10 times that of pure TiO{sub 2}, and the Co and N co-doping derives 10-fold photocatalytic activity.

  11. Effect of Nb-doped TiO{sub 2} on nanocomposited aligned ZnO nanorod/TiO{sub 2}:Nb for dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Saurdi, I., E-mail: saurdy788@gmail.com; Ishak, A. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM),40450 Shah Alam, Selangor (Malaysia); UiTM Sarawak Kampus Kota Samarahan Jalan Meranek, Sarawak (Malaysia); Shafura, A. K.; Azhar, N. E. A.; Mamat, M. H. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM),40450 Shah Alam, Selangor (Malaysia); Malek, M. F.; Rusop, M. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM),40450 Shah Alam, Selangor (Malaysia); NANO-SciTech Centre (NST), (Centre for Nano-Science and Nano-Technology), Institute of Science, Universiti Teknologi MARA - UiTM, 40450 Shah Alam, Selangor (Malaysia); Alrokayan, A. H. Salman; Khan, Haseeb A. [Department of Biochemistry, College of Science, Bldg. 5, King Saud University (KSU) P.O: 2455 Riyadh 1145 (Saudi Arabia)

    2016-07-06

    The Nb-doped TiO{sub 2} films were deposited on glass substrate at different Nb concentrations of 0 at.%, 1 at.%, 3 at.%, 5 at.% and 7 at.%, respectively and their electrical and structural properties were investigated. Subsequently, the Nb-doped TiO{sub 2} films were deposited on top of aligned ZnO Nanorod on ITO glass substrates using spin coating technique. The nanocomposited aligned ZnO nanorod/Nb-doped TiO{sub 2} (TiO{sub 2}:Nb) were coated with different Nb concentrations of 0 at.%, 1 at.%, 3 at.%, 5 at.% and 7 at.%, respectively. The Dye-sensitized solar cells were fabricated from the nanocomposited aligned ZnO nanorod/TiO{sub 2}:Nb photoanodes and their effects on the performance of the DSSCs were investigated. From the solar simulator measurement of DSSC the solar energy conversion efficiency (η) of 5.376% under AM 1.5 was obtained for the ZnO nanorod/TiO{sub 2}:Nb-5at.%.

  12. Characterization and improved solar light activity of vanadium doped TiO{sub 2}/diatomite hybrid catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Bin, E-mail: b.wang6@uq.edu.au [School of Chemical and Environmental Engineering, China University of Mining & Technology, Beijing 100083 (China); School of Chemistry and Molecular Biosciences, The University of Queensland, Brisbane, Qld 4072 (Australia); Zhang, Guangxin, E-mail: z111@163.com [School of Chemical and Environmental Engineering, China University of Mining & Technology, Beijing 100083 (China); Leng, Xue, E-mail: xue.leng@uq.net.au [School of Chemistry and Molecular Biosciences, The University of Queensland, Brisbane, Qld 4072 (Australia); Sun, Zhiming, E-mail: zhiming.baxia@163.com [School of Chemical and Environmental Engineering, China University of Mining & Technology, Beijing 100083 (China); Zheng, Shuilin, E-mail: shuilinzheng8@gmail.com [School of Chemical and Environmental Engineering, China University of Mining & Technology, Beijing 100083 (China)

    2015-03-21

    Highlights: • V-doped TiO{sub 2}/diatomite composite photocatalyst was synthesized. • The physiochemical property and solar light photoactivity were characterized. • The presence and influence of V ions in TiO{sub 2} matrix was systematically analyzed. • The photocatalysis for Rhodamine B were studied under solar light illumination. - Abstract: V-doped TiO{sub 2}/diatomite composite photocatalysts with different vanadium concentrations were synthesized by a modified sol–gel method. The diatomite was responsible for the well dispersion of TiO{sub 2} nanoparticles on the matrix and consequently inhibited the agglomeration. V-TiO{sub 2}/diatomite hybrids showed red shift in TiO{sub 2} absorption edge with enhanced absorption intensity. Most importantly, the dopant energy levels were formed in the TiO{sub 2} bandgap due to V{sup 4+} ions substituted to Ti{sup 4+} sites. The 0.5% V-TiO{sub 2}/diatomite photocatalyst displayed narrower bandgap (2.95 eV) compared to undoped sample (3.13 eV) and other doped samples (3.05 eV) with higher doping concentration. The photocatalytic activities of V doped TiO{sub 2}/diatomite samples for the degradation of Rhodamine B under stimulated solar light illumination were significantly improved compared with the undoped sample. In our case, V{sup 4+} ions incorporated in TiO{sub 2} lattice were responsible for increased visible-light absorption and electron transfer to oxygen molecules adsorbed on the surface of TiO{sub 2} to produce superoxide radicals ·O{sub 2}{sup –}, while V{sup 5+} species presented on the surface of TiO{sub 2} particles in the form of V{sub 2}O{sub 5} contributed to e{sup –}–h{sup +} separation. In addition, due to the combination of diatomite as support, this hybrid photocatalyst could be separated from solution quickly by natural settlement and exhibited good reusability.

  13. Facile fabrication of Si-doped TiO2 nanotubes photoanode for enhanced photoelectrochemical hydrogen generation

    Science.gov (United States)

    Dong, Zhenbiao; Ding, Dongyan; Li, Ting; Ning, Congqin

    2018-04-01

    Photoelectrochemical (PEC) water splitting based doping modified one dimensional (1D) titanium dioxide (TiO2) nanostructures provide an efficient method for hydrogen generation. Here we first successfully fabricated 1D Si-doped TiO2 (Ti-Si-O) nanotube arrays through anodizing Ti-Si alloys with different Si amount, and reported the PEC properties for water splitting. The Ti-Si-O nanotube arrays fabricated on Ti-5 wt.% Si alloy and annealed at 600 °C possess higher PEC activity, yielding a higher photocurrent density of 0.83 mA/cm2 at 0 V vs. Ag/AgCl. The maximum photoconversion efficiency was 0.54%, which was 2.7 times the photoconversion efficiency of undoped TiO2.

  14. Synthesis, characterization, and analysis of enhanced photocatalytic activity of Zr-doped TiO2 nanostructured powders under UV light

    Science.gov (United States)

    Sekhar, M. Chandra; Purusottam Reddy, B.; Mallikarjuna, K.; Shanmugam, Gnanendra; Ahn, Chang-Hoi; Park, Si-Hyun

    2018-01-01

    Zr-doped and pure TiO2 nanoparticles (NPs) were synthesized using a simple inexpensive sol-gel method. X-ray powder diffractometry and Fourier transform infrared spectrometry revealed the presence of anatase-phase TiO2 NPs. Scanning electron microscopy and transmission electron microscopy revealed that the average nanocrystalline size of approximately 15 nm. The photocatalytic activities of these materials were evaluated using Rhodamine B (Rh B) as an organic contaminant. The photocatalytic activity of pure and Zr-doped TiO2 NPs (with at% 4, 8, 12 and 16) was measured in terms of the degradation of Rh B under UV light. The antibacterial activities of pure and Zr-doped (with 8 at%) TiO2 NPs were evaluated against Bacillus subtillis, Escherichia coli, and Pseudomonas aeruginosa. A maximum inhibition zone (19 mm) was observed for pure TiO2 NPs, against Bacillus subtillis and Pseudomonas aeruginosa, while Zr-doped TiO2 (8 at%) exhibited a lesser inhibition zone (18 mm) against the same Bacillus subtillis and Pseudomonas aeruginosa (18 mm). However, Zr-doped TiO2 (8 at%) NPs exhibited a greater inhibition zone against Escherichia coli (17 mm), while the activity of pure TiO2 NPs against Escherichia coli (15 mm) was retarded. Thus, pure TiO2 NPs and Zr-doped TiO2 (8 at%) NPs have competent activities and can be used as antibacterial agents against different bacteria.

  15. A short literature survey on iron and cobalt ion doped TiO2 thin films and photocatalytic activity of these films against fungi

    International Nuclear Information System (INIS)

    Tatlıdil, İlknur; Bacaksız, Emin; Buruk, Celal Kurtuluş; Breen, Chris; Sökmen, Münevver

    2012-01-01

    Highlights: ► Co or Fe doped TiO 2 thin films were prepared by sol–gel method. ► We obtained lower E g values for Fe-doped and Co-TiO 2 thin films. ► Doping greatly affected the size and shape of the TiO 2 nanoparticles. ► Photocatalytic killing effect of the doped TiO 2 thin films on C. albicans and A. niger was significantly higher than undoped TiO 2 thin film for short exposure periods. - Abstract: In this study, a short recent literature survey which concentrated on the usage of Fe 3+ or Co 2+ ion doped TiO 2 thin films and suspensions were summarized. Additionally, a sol–gel method was used for preparation of the 2% Co or Fe doped TiO 2 thin films. The surface of the prepared materials was characterised using scanning-electron microscopy (SEM) combined with energy dispersive X-ray (EDX) analysis and band gap of the films were calculated from the transmission measurements that were taken over the range of 190 and 1100 nm. The E g value was 3.40 eV for the pure TiO 2 , 3.00 eV for the Fe-doped TiO 2 film and 3.25 eV for Co-TiO 2 thin film. Iron or cobalt doping at lower concentration produce more uniformed particles and doping greatly affected the size and shape of the TiO 2 nanoparticles. Photocatalytic killing effect of the 2% Co doped TiO 2 thin film on Candida albicans was significantly higher than Fe doped TiO 2 thin film for short and long exposure periods. Doped thin films were more effective on Aspergillus niger for short exposure periods.

  16. Visible active nanocrystalline N-doped anatase TiO{sub 2} particles for photocatalytic mineralization studies

    Energy Technology Data Exchange (ETDEWEB)

    Barkul, R.P. [Department of Chemistry, Dr. Babasaheb Ambedkar Marathwada University, Aurangabad, Sub–campus Osmanabad, 413 501, MS (India); Koli, V.B.; Shewale, V.B. [Department of Chemistry, Shivaji University, Kolhapur, 416 004, MS (India); Patil, M.K. [Department of Chemistry, Dr. Babasaheb Ambedkar Marathwada University, Aurangabad, Sub–campus Osmanabad, 413 501, MS (India); Delekar, S.D., E-mail: sddelekar7@rediffmail.com [Department of Chemistry, Dr. Babasaheb Ambedkar Marathwada University, Aurangabad, Sub–campus Osmanabad, 413 501, MS (India); Department of Chemistry, Shivaji University, Kolhapur, 416 004, MS (India); Department of Chemistry and Biochemistry, Florida State University, Tallahassee, 30306-4390, FL (United States)

    2016-04-15

    Nitrogen-doped TiO{sub 2} nanoparticles (N–TiO{sub 2} NPs) with anatase phase were synthesized by sol–gel method using a single precursor containing titanium (IV) terbutoxide, glacial acetic acid, sodium dodecyl sulphate, ammonia, and urea. X-ray diffraction (XRD) reveals the nanocrystalline nature with anatase phase of all the samples. The particle size of all samples was found in the range of 5–12 nm using transmission electron microscopy (TEM). UV–visible absorption measurements examined that the optical band gap of the doped samples decrease with increase in dopant concentration from 0.0 to 7.0 mol%. Field-emission scanning electron microscopy (FESEM) with energy dispersive atomic X-ray (EDAX) spectroscopy was employed to analyse the morphology and chemical composition of these N–TiO{sub 2} NPs. The photocatalytic activity of bare/doped TiO{sub 2} samples was demonstrated for the degradation of Rhodamine B (RhB) dye under direct sunlight irradiation. The photocatalytic degradation was monitored by measuring the kinetic parameters based on UV–visible spectroscopy as well as the chemical oxygen demand (COD) during the course of the reaction. The effect of dye concentration and pH of the solution on the photocatalytic degradation reaction in the presence of colloidal bare/doped TiO{sub 2} were also studied. The N–TiO{sub 2} catalyst, with a nitrogen concentration of 7.0 mol%, showed the highest activity for photocatalytic mineralization of dye at acidic or alkaline medium than neutral condition under solar light irradiation directly. - Highlights: • Nitrogen doped TiO{sub 2} nanoparticles where synthesized by using simple sol–gel method at room temperature. • N–TiO{sub 2} nanoparticles shows red shift. • Hydroxylation on the surface of TiO{sub 2} increase with increasing nitrogen concentration. • In presence of sunlight N–TiO{sub 2} shows enhancement in degradation of RhB dye.

  17. Highly Efficient Low-Temperature N-Doped TiO2 Catalysts for Visible Light Photocatalytic Applications

    Science.gov (United States)

    Mahy, Julien G.; Cerfontaine, Vincent; Devred, François; Gaigneaux, Eric M.; Heinrichs, Benoît; Lambert, Stéphanie D.

    2018-01-01

    In this paper, TiO2 prepared with an aqueous sol-gel synthesis by peptization process is doped with nitrogen precursor to extend its activity towards the visible region. Three N-precursors are used: urea, ethylenediamine and triethylamine. Different molar N/Ti ratios are tested and the synthesis is adapted for each dopant. For urea- and trimethylamine-doped samples, anatase-brookite TiO2 nanoparticles of 6–8 nm are formed, with a specific surface area between 200 and 275 m2·g−1. In ethylenediamine-doped samples, the formation of rutile phase is observed, and TiO2 nanoparticles of 6–8 nm with a specific surface area between 185 and 240 m2·g−1 are obtained. X-ray photoelectron spectroscopy (XPS) and diffuse reflectance measurements show the incorporation of nitrogen in TiO2 materials through Ti–O–N bonds allowing light absorption in the visible region. Photocatalytic tests on the remediation of water polluted with p-nitrophenol show a marked improvement for all doped catalysts under visible light. The optimum doping, taking into account cost, activity and ease of synthesis, is up-scaled to a volume of 5 L and compared to commercial Degussa P25 material. This up-scaled sample shows similar properties compared to the lab-scale sample, i.e., a photoactivity 4 times higher than commercial P25. PMID:29642626

  18. Photocatalytic degradation of p,p'-DDT under UV and visible light using interstitial N-doped TiO₂.

    Science.gov (United States)

    Ananpattarachai, Jirapat; Kajitvichyanukul, Puangrat

    2015-01-01

    1,1,1-trichloro-2,2-bis(p-chlorophenyl)ethane (or p,p'-DDT) is one of the most persistent pesticides. It is resistant to breakdown in nature and cause the water contamination problem. In this work, a major objective was to demonstrate the application of N-doped TiO2 in degradation and mineralization of the p,p'-DDT under UV and visible light in aqueous solution. The N-doped TiO2 nanopowders were prepared by a simple modified sol-gel procedure using diethanolamine (DEA) as a nitrogen source. The catalyst characteristics were investigated using XRD, SEM, TEM, and XPS. The adsorption and photocatalytic oxidation of p,p'-DDT using the synthesized N-doped TiO2 under UV and visible light were conducted in a batch photocatalytic experiment. The kinetics and p,p'-DDT degradation performance of the N-doped TiO2 were evaluated. Results show that the N-doped TiO2 can degrade p,p'-DDT effectively under both UV and visible lights. The rate constant of the p,p'-DDT degradation under UV light was only 0.0121 min(-1), whereas the rate constant of the p,p'-DDT degradation under visible light was 0.1282 min(-1). Under visible light, the 100% degradation of p,p'-DDT were obtained from N-doped TiO2 catalyst. The reaction rate of p,p'-DDT degradation using N-doped TiO2 under visible light was sixfold higher than that under UV light. According to Langmuir-Hinshelwood model, the adsorption equilibrium constant (K) for the N-doped TiO2 under visible light was 0.03078 L mg(-1), and the apparent reaction rate constant (k) was 1.3941 mg L(-1)-min. Major intermediates detected during the p,p'-DDT degradation were p,p'-DDE, o,p'-DDE, p,p'-DDD and p,p'-DDD. Results from this work can be applied further for the breakdown of p,p'-DDT molecule in the real contaminated water using this technology.

  19. Corrosion protection of AISI 1018 steel using Co-doped TiO_2/polypyrrole nanocomposites in 3.5% NaCl solution

    International Nuclear Information System (INIS)

    Ladan, Magaji; Basirun, Wan Jeffrey; Kazi, Salim Newaz; Rahman, Fariza Abdul

    2017-01-01

    A polypyrrole nanocomposites (PPy NTCs) have been effectively synthesized in the presence of TiO_2 and Co-doped TiO_2 nanoparticles (NPs) by an in situ chemical oxidative polymerization. Field Emission Scanning Electron Microscopy and Transmission Electron Microscopy revealed a tube shape structure of the PPy. The TEM results confirmed that the nanocomposite size of Co-doped TiO_2/PPy NTCs was smaller than TiO_2/PPy NTCs thereby increasing the interaction between the PPy nanotube and the AISI steel surface. The corrosion performance of the coatings was evaluated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization measurements in 3.5% NaCl solution. The EIS results show that the log |Z| of AISI 1018 coated with Co-doped TiO_2/PPy NTCs and TiO_2/PPy NTCs reached about 8.2 and 6.0 respectively after 30 days of exposure in 3.5% NaCl solution. This is likely due to the increased surface area of the PPy synthesized in the presence of Co-doped TiO_2 NPs. The EIS results are confirmed by the potentiodynamic polarization and open circuit potential values of the Co-doped TiO_2/PPy which indicated little changes between 1 and 30 days of exposure which confirms the protection ability of this coating. . It is evident that the presence of Co-doped TiO_2 NPs can enhance the resistance against corrosion at the steel/electrolyte interface. - Highlights: • Polymerization of pyrrole monomer in the presence of Co-doped TiO_2 decreases the size of the polypyrrole nanotube (PPy NT). • The corrosion protection increases with the increase in PPy NT dispersion. • The corrosion resistance of steel coated with Co-doped TiO_2/PPy NTCs is considerably higher. • TiO_2/PPy with Co doping reduces the charge transfer across the electrolyte/AISI 1018 steel interface.

  20. Electronic properties and surface reactivity of SrO-terminated SrTiO3 and SrO-terminated iron-doped SrTiO3.

    Science.gov (United States)

    Staykov, Aleksandar; Tellez, Helena; Druce, John; Wu, Ji; Ishihara, Tatsumi; Kilner, John

    2018-01-01

    Surface reactivity and near-surface electronic properties of SrO-terminated SrTiO 3 and iron doped SrTiO 3 were studied with first principle methods. We have investigated the density of states (DOS) of bulk SrTiO 3 and compared it to DOS of iron-doped SrTiO 3 with different oxidation states of iron corresponding to varying oxygen vacancy content within the bulk material. The obtained bulk DOS was compared to near-surface DOS, i.e. surface states, for both SrO-terminated surface of SrTiO 3 and iron-doped SrTiO 3 . Electron density plots and electron density distribution through the entire slab models were investigated in order to understand the origin of surface electrons that can participate in oxygen reduction reaction. Furthermore, we have compared oxygen reduction reactions at elevated temperatures for SrO surfaces with and without oxygen vacancies. Our calculations demonstrate that the conduction band, which is formed mainly by the d-states of Ti, and Fe-induced states within the band gap of SrTiO 3 , are accessible only on TiO 2 terminated SrTiO 3 surface while the SrO-terminated surface introduces a tunneling barrier for the electrons populating the conductance band. First principle molecular dynamics demonstrated that at elevated temperatures the surface oxygen vacancies are essential for the oxygen reduction reaction.

  1. Enhanced visible light photocatalytic properties of Fe-doped TiO2 nanorod clusters and monodispersed nanoparticles

    International Nuclear Information System (INIS)

    Liu, Y.; Wei, J.H.; Xiong, R.; Pan, C.X.; Shi, J.

    2011-01-01

    In order to get photocatalysts with desired morphologies and enhanced visible light responses, the Fe-doped TiO 2 nanorod clusters and monodispersed nanoparticles were prepared by modified hydrothermal and solvothermal method, respectively. The microstructures and morphologies of TiO 2 crystals can be controlled by restraining the hydrolytic reaction rates. The Fe-doped photocatalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV-vis absorption spectroscopy (UV-vis), N 2 adsorption-desorption measurement (BET), and photoluminescence spectroscopy (PL). The refinements of the microstructures and morphologies result in the enhancement of the specific surface areas. The Fe 3+ -dopants in TiO 2 lattices not only lead to the significantly extending of the optical responses from UV to visible region but also diminish the recombination rates of the electrons and holes. The photocatalytic activities were evaluated by photocatalytic decomposition of formaldehyde in air under visible light illumination. Compared with P25 (TiO 2 ) and N-doped TiO 2 nanoparticles, the Fe-doped photocatalysts show high photocatalytic activities under visible light.

  2. Fabrication and characterization of perovskite-type solar cells with Nb-doped TiO{sub 2} layers

    Energy Technology Data Exchange (ETDEWEB)

    Saito, Jo; Oku, Takeo, E-mail: oku@mat.usp.ac.jp; Suzuki, Atsushi; Akiyama, Tsuyoshi [The University of Shiga Prefecture, Hikone, Shiga 522-8533 (Japan)

    2016-02-01

    Organic-inorganic hybrid heterojunction solar cells containing perovskite CH{sub 3}NH{sub 3}PbI{sub 3} using Nb-doped TiO{sub 2} as an electron-transporting layer were fabricated and characterized. Nb-doped TiO{sub 2} layer showed an improvement of the short-circuit current density and power conversion efficiency using Ti{sub 0.95}Nb{sub 0.05}O{sub 2}.

  3. Effect of Mo and Ti doping concentration on the structural and optical properties of ZnS nanoparticles

    Science.gov (United States)

    Naz, Hina; Ali, Rai Nauman; Zhu, Xingqun; Xiang, Bin

    2018-06-01

    In this paper, we report the effect of single phase Mo and Ti doping concentration on the structural and optical properties of the ZnS nanoparticles. The structural and optical properties of the as-synthesized samples have been examined by x-ray diffraction, transmission electron microscopy (TEM), UV-visible near infrared absorption spectroscopy and x-ray photoelectron spectroscopy. TEM characterizations reveal a variation in the doped ZnS nanoparticle size distribution by utilizing different dopants of Mo and Ti. In absorption spectra, a clear red shift of 14 nm is observed with increasing Mo concentration as compared to pure ZnS nanoparticles, while by increasing Ti doping concentration, blue shift of 14 nm is obtained. Moreover, it demonstrates that the value of energy band gap decreases from 4.03 eV to 3.89 eV in case of Mo doping. However, the value of energy band gap have shown a remarkable increase from 4.11 eV to 4.27 eV with increasing Ti doping concentration. Our results provide a new pathway to understand the effect of Mo and Ti doping concentrations on the structural and optical properties of ZnS nanoparticles as it could be the key to tune the properties for future optoelectronic devices.

  4. C, N co-doped TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite coatings prepared from TiC{sub 0.7}N{sub 0.3} powder using ball milling followed by oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Hao, Liang, E-mail: haoliang@tust.edu.cn [Tianjin Key Lab of Integrated Design and On-line Monitoring for Light Industry & Food Machinery and Equipment, Tianjin (China); College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Wang, Zhenwei, E-mail: 1004329228@qq.com [School of Naval Architecture and Ocean Engineering, Harbin Institute of Technology, Weihai, No. 2, Wenhua West Road, Weihai 264209 (China); Zheng, Yaoqing, E-mail: 13612177268@163.com [College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Li, Qianqian, E-mail: 1482471595@qq.com [College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Guan, Sujun, E-mail: sujunguan1221@gmail.com [College of Mechanical Engineering & Graduate School, Chiba University, 1-33, Yayoi-cho, Inage-ku, Chiba 263-8522 (Japan); Zhao, Qian, E-mail: zhaoqian@tust.edu.cn [Tianjin Key Lab of Integrated Design and On-line Monitoring for Light Industry & Food Machinery and Equipment, Tianjin (China); College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Cheng, Lijun, E-mail: chenglijun@tust.edu.cn [Tianjin Key Lab of Integrated Design and On-line Monitoring for Light Industry & Food Machinery and Equipment, Tianjin (China); College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Lu, Yun, E-mail: luyun@faculty.chiba-u.jp [College of Mechanical Engineering & Graduate School, Chiba University, 1-33, Yayoi-cho, Inage-ku, Chiba 263-8522 (Japan); Liu, Jizi, E-mail: jzliu@njust.edu.cn [Herbert Gleiter Institute of Nanoscience, Nanjing University of Science and Technology, No. 200, Xiaolingwei Street, Nanjing 210094 (China)

    2017-01-01

    Highlights: • TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} coatings were prepared by ball milling followed by oxidation. • In situ co-doping of C and N with simultaneous TiO{sub 2} formation was observed. • Improved photocatalytic activity under UV/visible light was noticed. • Synergism in co-doping and heterojunction formation promoted carrier separation. - Abstract: Ball milling followed by heat oxidation was used to prepared C, N co-doped TiO{sub 2} coatings on the surfaces of Al{sub 2}O{sub 3} balls from TiC{sub 0.7}N{sub 0.3} powder. The as-prepared coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible spectrophotometer (UV–vis). The results show that continuous TiC{sub 0.7}N{sub 0.3} coatings were formed after ball milling. C, N co-doped TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite coatings were prepared after the direct oxidization of TiC{sub 0.7}N{sub 0.3} coatings in the atmosphere. However, TiO{sub 2} was hardly formed in the surface layer of TiC{sub 0.7}N{sub 0.3} coatings within a depth less than 10 nm during the heat oxidation of TiC{sub 0.7}N{sub 0.3} coatings in carbon powder. Meanwhile, the photocatalytic activity evaluation of these coatings was conducted under the irradiation of UV and visible light. All the coatings showed photocatalytic activity in the degradation of MB no matter under the irradiation of UV or visible light. The C, N co-doped TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite coatings showed the most excellent performance. The enhancement under visible light irradiation should attribute to the co-doping of carbon and nitrogen, which enhances the absorption of visible light. The improvement of photocatalytic activity under UV irradiation should attribute to the synergistic effect of C, N co-doping, the formation of rutile-anatase mixed phases and the TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite microstructure.

  5. Effect of Metal (Mn, Ti) Doping on NCA Cathode Materials for Lithium Ion Batteries

    OpenAIRE

    Wan, Dao Yong; Fan, Zhi Yu; Dong, Yong Xiang; Baasanjav, Erdenebayar; Jun, Hang-Bae; Jin, Bo; Jin, En Mei; Jeong, Sang Mun

    2018-01-01

    NCA (LiNi0.85Co0.10Al0.05-x MxO2, M=Mn or Ti, x < 0.01) cathode materials are prepared by a hydrothermal reaction at 170°C and doped with Mn and Ti to improve their electrochemical properties. The crystalline phases and morphologies of various NCA cathode materials are characterized by XRD, FE-SEM, and particle size distribution analysis. The CV, EIS, and galvanostatic charge/discharge test are employed to determine the electrochemical properties of the cathode materials. Mn and Ti doping res...

  6. Concurrent doping effect of Ti and nano-diamond on flux pinning of MgB{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Y., E-mail: yzhao@swjtu.edu.c [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wales, Sydney, 2052 NSW (Australia); Ke, C. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Cheng, C.H. [Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wales, Sydney, 2052 NSW (Australia); Feng, Y. [Northwest Institute for Nonferrous Metal Research, P.O. Box 51, Xian, Shaanxi 710016 (China); Western Superconductivity Technology Company, Xian (China); Yang, Y. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Munroe, P. [Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wales, Sydney, 2052 NSW (Australia)

    2010-11-01

    Nano-diamond and titanium concurrently doped MgB{sub 2} nanocomposites have been prepared by solid state reaction method. The effects of carbon and Ti concurrent doping on J{sub c}-H behavior and pinning force scaling features of MgB{sub 2} have been investigated. Although T{sub c} was slightly depressed, J{sub c} of MgB{sub 2} have been significantly improved by the nano-diamond doping, especially in the high field region. In the mean time, the J{sub c} value in low field region is sustained though concurrent Ti doping. Microstructure analysis reveals that when nano-diamond was concurrently doped with titanium in MgB{sub 2}, a unique nanocomposite in which TiB{sub 2} forms a thin layer surrounding MgB{sub 2} grains whereas nano-diamond particles were wrapped inside the MgB{sub 2} grains. Besides, nano-diamond doping results in a high density stress field in the MgB{sub 2} samples, which may take responsibility for the {Delta}{kappa} pinning behavior in the carbon-doped MgB{sub 2} system.

  7. Photocatalytic performance of Cu-doped TiO2 nanofibers treated by the hydrothermal synthesis and air-thermal treatment

    Science.gov (United States)

    Wu, Ming-Chung; Wu, Po-Yeh; Lin, Ting-Han; Lin, Tz-Feng

    2018-02-01

    Series of transition metal-doped TiO2 (metal/TiO2) is prepared by combining the hydrothermal synthesis and air-thermal treatment without any reduction process. The selected transition metal precursors, including Ag, Au, Co, Cr, Cu, Fe, Ni, Pd, Pt, Y, and Zn, were individually doped into TiO2 nanofibers to evaluate the photocatalytic degradation activity and photocatalytic hydrogen generation. Consider the photocatalytic performance of these synthesized metal/TiO2 under UV-A irradiation, copper doped TiO2 nanofibers (Cu/TiO2 NFs) was chosen for further study due to its extraordinary reactivity. Systematical studies were spread to optimize the doping concentration and the calcination condition for much higher photocatalytic activity Cu/TiO2 NFs. In the photocatalytic degradation test, 0.5 mol%-Cu/TiO2 NFs calcined at 650 °C exhibits the highest activity, which is even higher than commercial TiO2-AEROXIDE® TiO2 P25 under UV-A irradiation. The synthesized 0.5 mol%-Cu/TiO2-650 NFs also have the capability in the photocatalytic hydrogen production. The hydrogen evolution rates are 200 μmol/g·h under UV-A irradiation and 280 μmol/g·h under UV-B irradiation. The density of state calculated by CASTEP for Cu/TiO2 indicates that Cu doping contributes to the states near valence band edge and narrows the band gap. The disclosed process in this study is industrial safe, convenient and cost-effective. We further produce a significant amount of TiO2-based catalysts without any hydrogen reduction treatment.

  8. Evaluation of surface energy state distribution and bulk defect concentration in DSSC photoanodes based on Sn, Fe, and Cu doped TiO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Ako, Rajour Tanyi [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara (Brunei Darussalam); Ekanayake, Piyaisiri, E-mail: piyasiri.ekanayake@ubd.edu.bn [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara (Brunei Darussalam); Young, David James [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara (Brunei Darussalam); Institute of Materials Research and Engineering (IMRE), Agency for Science, Technology and Research -A*STAR, 3 Research Link, 117602 (Singapore); Faculty of Science, Health, Education and Engineering, University of the Sunshine Coast, Locked Bag 4, Maroochydore DC, Queensland, 4558 (Australia); Hobley, Jonathan [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara (Brunei Darussalam); Chellappan, Vijila [Institute of Materials Research and Engineering (IMRE), Agency for Science, Technology and Research - A*STAR, 3 Research Link, 117602 (Singapore); Tan, Ai Ling [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara (Brunei Darussalam); Gorelik, Sergey; Subramanian, Gomathy Sandhya [Institute of Materials Research and Engineering (IMRE), Agency for Science, Technology and Research - A*STAR, 3 Research Link, 117602 (Singapore); Lim, Chee Ming [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara (Brunei Darussalam)

    2015-10-01

    Graphical abstract: - Highlights: • The structural, optical and optoelectronic properties of 1 mol.% Fe, Sn and Cu doped TiO{sub 2} have been compared. • Transient lifetimes for pure TiO{sub 2} and Sn doped TiO{sub 2} were considerably shorter than Fe and Cu doped TiO{sub 2}. • A good correlation between the bulk defects and transient decay for the doped TiO{sub 2} powders was observed. • Photon to current conversion efficiency of DSSC based on the metal doped TiO{sub 2} were in order Sn-TiO{sub 2} > Cu-TiO{sub 2} > Pure >> Fe-TiO{sub 2}. • DSSC based on Fe doped photoanodes is limited by a high concentration of surface free holes observed at 433 nm. - Abstract: Electron transfer dynamics in the oxide layers of the working electrodes in both dye-sensitized solar cells and photocatalysts greatly influences their performance. A proper understanding of the distribution of surface and bulk energy states on/in these oxide layers can provide insights into the associated electron transfer processes. Metal ions like Iron (Fe), Copper (Cu) and Tin (Sn) doped onto TiO{sub 2} have shown enhanced photoactivity in these processes. In this work, the structural, optical and transient properties of Fe, Cu and Sn doped TiO{sub 2} nanocrystalline powders have been investigated and compared using EDX, Raman spectroscopy, X-ray Photoelectron spectroscopy (XPS), and Transient Absorption spectroscopy (TAS). Surface free energy states distributions were probed using Electrochemical Impedance spectroscopy (EIS) on Dye Sensitized Solar Cells (DSSC) based on the doped TiO{sub 2} photoanodes. Raman and XPS Ti2p{sub 3/2} peak shifts and broadening showed that the concentration of defects were in the order: Cu doped TiO{sub 2} > Fe doped TiO{sub 2} > Sn doped TiO{sub 2} > pure TiO{sub 2}. Nanosecond laser flash photolysis of Fe and Cu doped TiO{sub 2} indicated slower transient decay kinetics than that of Sn doped TiO{sub 2} or pure TiO{sub 2}. A broad absorption peak and fast

  9. Tailoring the piezoelectric and relaxor properties of (Bi1/2 Na1/2) TiO3- BaTiO3 via zirconium doping

    DEFF Research Database (Denmark)

    Glaum, Julia; Simons, Hugh; Acosta, Matias

    2013-01-01

    This article details the influence of zirconium doping on the piezoelectric properties and relaxor characteristics of 94(Bi1/2Na1/2)TiO3-6Ba(ZrxTi1-x)O3 (BNT-6BZT) bulk ceramics. Neutron diffraction measurements of BNT-6BZT doped with 0%-15% Zr revealed an electric-field-induced transition...

  10. Comparing Cr, and N only doping with (Cr,N)-codoping for enhancing visible light reactivity of TiO2

    International Nuclear Information System (INIS)

    Li, Yuan; Wang, Wei; Qiu, Xiaofeng; Meyer, Harry M. III; Paranthaman, Mariappan Parans; Eres, Gyula; Zhang, Zhenyu; Gu, Baohua

    2011-01-01

    The photoreactivity of titania (TiO2) nanoclusters with varying levels of N or Cr-doping, or (Cr,N)-codoping, was systematically investigated using photodegradation of methyl orange in aqueous suspensions. The shifting of the TiO2 absorption edge into the visible spectral region that is primarily attributable to band gap narrowing was found to be a reliable metric for estimating the photoreactivity of the doped nanoclusters. Compared to the weak response with undoped and N-doped TiO2, Cr-doping and (Cr, N)-codoping were found to significantly enhance photodegradation of methyl orange under visible light. The initial reaction rates increase from about 0 to above 1.6 10-2 min-1 when the doping concentration of Cr in TiO2 increases from 0 to 5%. In stark contrast, under UV irradiation, doping is not only ineffective but detrimental to the photoreactivity, and all doping including N or Cr only and (Cr, N)-codoping were found to reduce photoreactivity.

  11. Simple method of preparing nitrogen - doped nanosized TiO2 powders of high photocatalytic activity under visible light

    International Nuclear Information System (INIS)

    Nguyen Van Hung; Dang Thi Thanh Le

    2014-01-01

    Nitrogen-doped nanosized TiO 2 powders were prepared by a simple thermal treatment method of the mixture of titanium dioxide and urea. The prepared products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV-Vis diffuse reflectance spectra (UV-Vis-DRS) and Fourier transform infrared (FT-IR) spectroscopy. The results showed that the crystal structure of N-TiO 2 was a mixture of anatase and rutile phases, and the average particle size was 31 nm calculated from XRD results. The UV-vis spectra indicate an increase in absorption of visible light when compared to undoped TiO 2 . The photocatalytic activity of nitrogen-doped TiO 2 powder was evaluated by the decomposition of methylene blue under visible light irradiation. And it was found that nitrogen-doped TiO 2 powders exhibited much higher photocatalytic activity than undoped TiO 2 . Moreover, the study also showed that, the doping N atoms improve the growth of the TiO 2 crystal and phase transformation. (author)

  12. Fabrication and electrical investigations of Pb-doped BaTiO{sub 3} ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Sareecha, N., E-mail: nsareecha@hotmail.com [Laboratory of Physical Chemistry, Department of Chemistry, Islamia University of Bahawalpur (Pakistan); Shah, W.A. [Glass and Ceramics Research Centre, PCSIR Laboratories Complex, Ferozpur Road, Lahore 54600 (Pakistan); Maqsood, A. [Nano Scale Physics Laboratory, Department of Physics, Air University, PAF Complex E-9, Islamabad (Pakistan); Anis-ur-Rehman, M. [Applied Thermal Physics Laboratory, COMSATS Institute of Information and Technology, Park Road, Islamabad 44000 (Pakistan); Latif Mirza, M. [Laboratory of Physical Chemistry, Department of Chemistry, Islamia University of Bahawalpur (Pakistan)

    2017-06-01

    Electrical properties of Pb doped BaTiO{sub 3}; PBT are investigated in the wide range of temperatures (40–700 °C) at 1 kHz frequency. PBT ceramics were fabricated through solid state sintering method. Pre fired BaTiO{sub 3} prepared with Ba/Ti molar ratio of 0.98 was doped with PbCO{sub 3} (<1 mole %). XRD patterns indicated perovskite phase with tetragonal structures (P4mm). Morphological studies (SEM) revealed grain development with increasing lead contents. With lead doping and its variation, Curie temperature (T{sub C}) was shifted from 120 to 200 °C with broad dielectric constant peaks and dielectric anomalies with relaxor behavior were observed. Resistivity decreased with increasing temperature, all specimens showed semiconductor behavior with negative temperature coefficient of resistivity (NTCR) characteristics. Mobility of electrons increased with thermal activation due to hopping of charge carriers from one site to another. Ohmic conductivities and associated activation energies were evaluated by impedance spectroscopy. Conductivity followed the Arrhenius law with E{sub a} = 1.187–1.169 eV which can be attributed to the ionic conduction owning to doubly ionized oxygen vacancies. Well-defined hysteresis P-E loops measured at room temperature depicted ferroelectric properties of the materials. - Graphical abstract: Temperature dependence of dielectric constant (Ɛ′) and resistivity (ρ) for pure and Pb-doped BaTiO{sub 3} ceramics at 1 k Hz frequency. - Highlights: • Pb-doped BaTiO{sub 3}ceramics were fabricated through solid state sintering. • Electrical properties were studied at the temperatures 40–700 °C at 1 kHz. • Specimens showed negative temperature coefficient of resistivity characteristics. • Conductivity followed the Arrhenius law with E{sub a} = 1.187–1.169 eV. • Ionic conduction was supposed to be responsible for conduction process.

  13. Enhanced Charge Extraction of Li-Doped TiO₂ for Efficient Thermal-Evaporated Sb₂S₃ Thin Film Solar Cells.

    Science.gov (United States)

    Lan, Chunfeng; Luo, Jingting; Lan, Huabin; Fan, Bo; Peng, Huanxin; Zhao, Jun; Sun, Huibin; Zheng, Zhuanghao; Liang, Guangxing; Fan, Ping

    2018-02-28

    We provided a new method to improve the efficiency of Sb₂S₃ thin film solar cells. The TiO₂ electron transport layers were doped by lithium to improve their charge extraction properties for the thermal-evaporated Sb₂S₃ solar cells. The Mott-Schottky curves suggested a change of energy band and faster charge transport in the Li-doped TiO₂ films. Compared with the undoped TiO₂, Li-doped mesoporous TiO₂ dramatically improved the photo-voltaic performance of the thermal-evaporated Sb₂S₃ thin film solar cells, with the average power conversion efficiency ( PCE ) increasing from 1.79% to 4.03%, as well as the improved open-voltage ( V oc ), short-circuit current ( J sc ) and fill factors. The best device based on Li-doped TiO₂ achieved a power conversion efficiency up to 4.42% as well as a V oc of 0.645 V, which are the highest values among the reported thermal-evaporated Sb₂S₃ solar cells. This study showed that Li-doping on TiO₂ can effectively enhance the charge extraction properties of electron transport layers, offering a new strategy to improve the efficiency of Sb₂S₃-based solar cells.

  14. Synthesis of two-dimensional nanowall of Cu-Doped TiO2 and its application as photoanode in DSSCs

    Science.gov (United States)

    Dahlan, Dahyunir; Md Saad, Siti Khatijah; Berli, Ade Usra; Bajili, Abdil; Umar, Akrajas Ali

    2017-07-01

    Two-dimensional nanowall of Cu-doped TiO2 (CuTNW) has been prepared in this work to study the role of Cu doping on its photoactivity properties and its photovoltaic performance as photoanode in a dye-sensitized solar cell (DSSC). TiO2 nanowall with five Cu ion doping, i.e. 6.25, 12.5, 25.0, 50.0 and 100.0 mM, were prepared via a liquid-phase deposition method using ammoniumhexafluorotitanate and hexamethylenetetramine as the reagents with a growth temperature of 90 °C. The X-Ray Diffraction (XRD), X-ray energy dispersion (EDX) and diffuse optical reflectance spectroscopy analysis results confirmed the successfulness of the Cu doping process in the TiO2 nanowall and effective modification on the photoactivity of the TiO2 nanowall. We found that the power conversion efficiency of the DSSC utilizing TiO2 nanowall as photoanode can be enhanced up to 2 times, i.e. from 0.2% to 0.44%, when the TiO2 nanowall doped with Cu ion. The nanostructure preparation, device fabrication and the mechanism for the device performance enhancement will be discussed.

  15. PAMAM templated N,Pt co-doped TiO2 for visible light photodegradation of brilliant black.

    Science.gov (United States)

    Nzaba, Sarre Kadia Myra; Ntsendwana, Bulelwa; Mamba, Bhekie Brilliance; Kuvarega, Alex Tawanda

    2018-05-01

    This study examined the photocatalytic degradation of an azo dye brilliant black (BB) using non-metal/metal co-doped TiO 2 . N,Pt co-doped TiO 2 photocatalysts were prepared by a modified sol-gel method using amine-terminated polyamidoamine dendrimer generation 0 (PG0) as a template and source of nitrogen. Structural, morphological, and textural properties were evaluated using scanning electron microscopy coupled to energy-dispersive X-ray spectroscopy (SEM/EDX), high-resolution transmission electron microscopy (HRTEM), X-ray diffraction spectroscopy (XRD), X-ray photoelectron spectroscopy (XPS), thermal gravimetric analysis (TGA), Fourier transform infrared (FTIR), Raman spectroscopy (RS), photoluminescence (PL) and ultra-violet/visible spectroscopy (UV-Vis). The synthesized photocatalysts exhibited lower band gap energies as compared to the Degussa P-25, revealing a red shift in band gap towards the visible light absorption region. Photocatalytic activity of N,Pt co-doped TiO 2 was measured by the reaction of photocatalytic degradation of BB dye. Enhanced photodegradation efficiency of BB was achieved after 180-min reaction time with an initial concentration of 50 ppm. This was attributed to the rod-like shape of the materials, larger surface area, and enhanced absorption of visible light induced by N,Pt co-doping. The N,Pt co-doped TiO 2 also exhibited pseudo-first-order kinetic behavior with half-life and rate constant of 0.37 and 0.01984 min -1 , respectively. The mechanism of the photodegradation of BB under the visible light irradiation was proposed. The obtained results prove that co-doping of TiO 2 with N and Pt contributed to the enhanced photocatalytic performances of TiO 2 for visible light-induced photodegradation of organic contaminants for environmental remediation. Therefore, this work provides a new approach to the synthesis of PAMAM templated N,Pt co-doped TiO 2 for visible light photodegradation of brilliant black.

  16. Preparation and characterization of doped TiO{sub 2} nanofibers by coaxial electrospining combined with sol–gel process

    Energy Technology Data Exchange (ETDEWEB)

    Tong, Haixia, E-mail: tonghaixia@126.com; Tao, Xican; Wu, Daoxin; Zhang, Xiongfei; Li, Dan; Zhang, Ling

    2014-02-15

    Graphical abstract: The surface of the precursor of Fe/TiO{sub 2} nanofibers are smoother than that of Fe /TiO{sub 2} nanofibers. After calcined at 500 °C, the tubers on the surface of the nanofibers become more obvious, and which also provides a direct proof for the dopant of Fe element. -- Highlights: • N, Fe, and W doped TiO{sub 2} nanofibers have been fabricated by coaxial electrospining. • The dopant has obvious influences on the surface topographies and crystal structures. • Fe doping can make remarkable topography changes and easy formation of rutile TiO{sub 2}. • The maximum doping amount of W in TiO{sub 2} nanofibers is less than 10% under 500 °C. -- Abstract: N, Fe, and W doped TiO{sub 2} nanofibers were fabricated by coaxial electrospining and directly annealing polyvinylpyrrolidone (PVP)/Tetrabutyl titanate (TBT) composite nanofibers. The crystal structure, morphology, and surface composition of the doped TiO{sub 2} nanofibers were investigated by the X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) respectively. The results show that the dopants have different influence on the surface topographies, the crystal structures and the transformation of anatase to rutile of TiO{sub 2} nanofibers. Fe dopant promotes bigger influence on topographies, phase transformation and crystallite growth of TiO{sub 2} nanofibers than that of either N or W dopant.

  17. Nitrogen and europium doped TiO2 anodized films with applications in photocatalysis

    International Nuclear Information System (INIS)

    Chi, Choong-Soo; Choi, Jinwook; Jeong, Yongsoo; Lee, Oh Yeon; Oh, Han-Jun

    2011-01-01

    Micro-arc oxidation method is a useful process for mesoporous titanium dioxide films. In order to improve the photocatalytic activity of the TiO 2 film, N-Eu co-doped titania catalyst was synthesized by micro-arc oxidation in the H 2 SO 4 /Eu(NO 3 ) 3 mixture solution. The specific surface area and the roughness of the anodic titania film fabricated in the H 2 SO 4 /Eu(NO 3 ) 3 electrolyte, were increased compared to that of the anodic TiO 2 film prepared in H 2 SO 4 solution. The absorbance response of N-Eu titania film shows a higher adsorption onset toward visible light region, and the incorporated N and Eu ions during anodization as a dopant in the anodic TiO 2 film significantly enhanced the photocatalytic activity for dye degradation. After dye decomposition test for 3 h, dye removal rates for the anodic TiO 2 film were 60.7% and 90.1% for the N-Eu doped titania film. The improvement of the photocatalytic activity was ascribed to the synergistic effects of the surface enlargement and the new electronic state of the TiO 2 band gap by N and Eu co-doping.

  18. The effects of antimony doping on the surface structure of rutile TiO{sub 2}(110)

    Energy Technology Data Exchange (ETDEWEB)

    Bechstein, Ralf; Schuette, Jens; Kuehnle, Angelika [Fachbereich Physik, Universitaet Osnabrueck, Barbarastrasse 7, D-49076 Osnabrueck (Germany); Kitta, Mitsunori; Onishi, Hiroshi [Department of Chemistry, Kobe University, Rokko-dai, Nada-ku, Kobe 657-8501 (Japan)], E-mail: kuehnle@uos.de

    2009-07-01

    Titanium dioxide represents a very important wide bandgap photocatalyst that is known to be sensitized to visible light by transition metal doping. Antimony doping has been demonstrated to provide photocatalytic activity when codoped with chromium at an optimum dopant ratio [Sb]/[Cr] of about 1.5. Here, the role of antimony doping on the surface structure of rutile TiO{sub 2}(110) is studied using non-contact atomic force microscopy (NC-AFM) under ultra-high vacuum conditions. At first glance, the surface structure of antimony-doped TiO{sub 2}(110) resembles the structure of pristine TiO{sub 2}(110). However, in contrast to what is found in pristine TiO{sub 2}(110), a dense layer of protruding features is observed upon antimony doping, which is tentatively ascribed to antimony-rich clusters. Moreover, homogeneously distributed holes are found on the surface, which differ in depth and shape depending on the preparation conditions. Holes with depths ranging from a few up to more than a hundred monatomic steps are observed. These holes are explained by surface segregation of antimony during annealing, as the ionic radius of Sb{sup 3+} is considerably larger than the ionic radius of Ti{sup 4+}. Our finding provides an indication of why an antimony concentration larger than the optimum ratio results in decreased photocatalytic activity. Moreover, controlling annealing temperature seems to constitute a promising strategy for creating nanosized holes on TiO{sub 2} surfaces.

  19. Magnetic and structural study of Cu-doped TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Torres, C.E. Rodriguez [Dpto de Fisica-IFLP, Fac. Cs. Exactas, Universidad Nacional de La Plata-CONICET, CC 67, 1900 La Plata (Argentina)], E-mail: torres@fisica.unlp.edu.ar; Golmar, F. [Laboratorio de Ablacion Laser, Facultad de Ingenieria, Universidad de Buenos Aires, Paseo Colon 850, 1063 Buenos Aires (Argentina); Cabrera, A.F.; Errico, L.; Navarro, A.M. Mudarra; Renteria, M.; Sanchez, F.H. [Dpto de Fisica-IFLP, Fac. Cs. Exactas, Universidad Nacional de La Plata-CONICET, CC 67, 1900 La Plata (Argentina); Duhalde, S. [Laboratorio de Ablacion Laser, Facultad de Ingenieria, Universidad de Buenos Aires, Paseo Colon 850, 1063 Buenos Aires (Argentina)

    2007-10-31

    Transparent pure and Cu-doped (2.5, 5 and 10 at.%) anatase TiO{sub 2} thin films were grown by pulsed laser deposition technique on LaAlO{sub 3} substrates. The samples were structurally characterized by X-ray absorption spectroscopy and X-ray diffraction. The magnetic properties were measured using a SQUID. All films have a FM-like behaviour. In the case of the Cu-doped samples, the magnetic cycles are almost independent of the Cu concentration. Cu atoms are forming CuO and/or substituting Ti in TiO{sub 2}. The thermal treatment in air promotes the CuO segregation. Since CuO is antiferromagnetic, the magnetic signals present in the films could be assigned to Cu substitutionally replacing cations in TiO{sub 2}.

  20. Methylene blue photocatalytic mineralization under visible irradiation on TiO{sub 2} thin films doped with chromium

    Energy Technology Data Exchange (ETDEWEB)

    Diaz-Uribe, Carlos; Vallejo, William, E-mail: williamvallejo@mail.uniatlantico.edu.co; Ramos, Wilkendry

    2014-11-15

    Graphical abstract: - Highlights: • We used an easy and inexpensive technique to dope thin films of TiO{sub 2}. • We proved that hydroxyl radicals were generated under visible light irradiation by Cr:TiO{sub 2}. • We used a Haber–Weiss reaction through Cr:TiO{sub 2} catalyst to improve the photo-mineralization process. - Abstract: We studied changes in structural, optical and photocatalytic properties of TiO{sub 2} thin films due to doping process with chromium. Powders of undoped TiO{sub 2} and chromium-doped TiO{sub 2} (Cr:TiO{sub 2}) were synthesized by sol–gel method and, thin films were deposited by doctor blade method. The properties of the thin films were studied by X-ray diffraction (XRD), infrared spectroscopy (IR) and diffuse reflectance. The XRD patterns indicated that doping process changed the crystalline phases radio of TiO{sub 2} thin films, furthermore, the optical analysis showed that band gap value of Cr:TiO{sub 2} thin films was 31% fewer than undoped TiO{sub 2} thin films. Along, Langmuir–Hinshelwood model was used to obtain kinetic information of the photo-mineralization process; results indicated that photocatalytic activity of Cr:TiO{sub 2} thin films were four times better than undoped TiO{sub 2} thin films; finally the synergic effect was tested by addition of the H{sub 2}O{sub 2}, photocatalytic yield was improved from 26% to 61% when methylene blue photo-mineralization was assisted with slightly amount of H{sub 2}O{sub 2}.

  1. Synergistic effect of Ti and F co-doping on dehydrogenation properties of MgH2 from first-principles calculations

    International Nuclear Information System (INIS)

    Zhang, J.; Huang, Y.N.; Mao, C.; Peng, P.

    2012-01-01

    Highlights: ► The co-incorporation of Ti and F into MgH 2 lattice is energetically favorable. ► The incorporated Ti and F in MgH 2 preferably generate TiH 2 and MgF 2 , respectively. ► The synergistic effect of Ti and F is superior to that of pure Ti. ► The weakened interactions of Mg–H explain enhanced dehydrogenation properties. - Abstract: The energetic and electronic properties of MgH 2 co-doped with Ti and F are investigated using first-principles calculations based on density functional theory. The calculation results show that incorporation of Ti combined with F atoms into MgH 2 lattice is energetically favorable relative to single incorporation of Ti atom. After dehydrogenation, the co-doped Ti and F in MgH 2 preferably generate TiH 2 and MgF 2 , respectively. Comparatively, the combined effect of Ti and F in improving the dehydrogenation properties of MgH 2 is superior to that of pure Ti. These results provide a reasonable explanation for experimental observations. Analysis of electronic structures suggests the enhanced dehydrogenation properties of doped MgH 2 can be attributed to the weakened bonding interactions between Mg and H due to foreign species doping.

  2. Ge{sup 4+} doped TiO{sub 2} for stoichiometric degradation of warfare agents

    Energy Technology Data Exchange (ETDEWEB)

    Stengl, Vaclav, E-mail: stengl@iic.cas.cz [Department of Solid State Chemistry, Institute of Inorganic Chemistry AS CR v.v.i., 250 68 Rez (Czech Republic); Grygar, Tomas Matys [Department of Solid State Chemistry, Institute of Inorganic Chemistry AS CR v.v.i., 250 68 Rez (Czech Republic); Oplustil, Frantisek; Nemec, Tomas [Military Technical Institute of Protection Brno, Veslarska 230, 628 00 Brno (Czech Republic)

    2012-08-15

    Highlights: Black-Right-Pointing-Pointer We prepared nanodisperse Ge{sup 4+} doped titania by a novel synthesis method. Black-Right-Pointing-Pointer Synthesis does not involve organic solvents, organometallics nor thermal processes. Black-Right-Pointing-Pointer The prepared materials are efficient in removal of chemical warfare agents. Black-Right-Pointing-Pointer Ge{sup 4+} doping improves rate of removal of soman and agent VX by TiO{sub 2}. - Abstract: Germanium doped TiO{sub 2} was prepared by homogeneous hydrolysis of aqueous solutions of GeCl{sub 4} and TiOSO{sub 4} with urea. The synthesized samples were characterized by X-ray diffraction, scanning electron microscopy, EDS analysis, specific surface area (BET) and porosity determination (BJH). Ge{sup 4+} doping increases surface area and content of amorphous phase in prepared samples. These oxides were used in an experimental evaluation of their reactivity with chemical warfare agent, sulphur mustard, soman and agent VX. Ge{sup 4+} doping worsens sulphur mustard degradation and improves soman and agent VX degradation. The best degree of removal (degradation), 100% of soman, 99% of agent VX and 95% of sulphur mustard, is achieved with sample with 2 wt.% of germanium.

  3. Fibroblast responses and antibacterial activity of Cu and Zn co-doped TiO2 for percutaneous implants

    Science.gov (United States)

    Zhang, Lan; Guo, Jiaqi; Yan, Ting; Han, Yong

    2018-03-01

    In order to enhance skin integration and antibacterial activity of Ti percutaneous implants, microporous TiO2 coatings co-doped with different doses of Cu2+ and Zn2+ were directly fabricated on Ti via micro-arc oxidation (MAO). The structures of coatings were investigated; the behaviors of fibroblasts (L-929) as well as the response of Staphylococcus aureus (S. aureus) were evaluated. During the MAO process, a large number of micro-arc discharges forming on Ti performed as penetrating channels; O2-, Ca2+, Zn2+, Cu2+ and PO43- delivered via the channels, giving rise to the formation of doped TiO2. Surface characteristics including phase component, topography, surface roughness and wettability were almost the same for different coatings, whereas, the amount of Cu doped in TiO2 decreased with the increased Zn amount. Compared with Cu single-doped TiO2 (0.77 Wt% Cu), the co-doped with appropriate amounts of Cu and Zn, for example, 0.55 Wt% Cu and 2.53 Wt% Zn, further improved proliferation of L-929, facilitated fibroblasts to switch to fibrotic phenotype, and enhanced synthesis of collagen I as well as the extracellular collagen secretion; the antibacterial properties including contact-killing and release-killing were also enhanced. By analyzing the relationship of Cu/Zn amount in TiO2 and the behaviors of L-929 and S. aureus, it can be deduced that when the doped Zn is in a low dose (<1.79 Wt%), the behaviors of L-929 and S. aureus are sensitive to the reduced amount of Cu2+, whereas, Zn2+ plays a key role in accelerating fibroblast functions and reducing S. aureus when its dose obviously increases from 2.63 to 6.47 Wt%.

  4. Synthesis, structure and total conductivity of A-site doped LaTiO3−δ perovskites

    International Nuclear Information System (INIS)

    Bradha, M.; Hussain, S.; Chakravarty, Sujay; Amarendra, G.; Ashok, Anuradha

    2015-01-01

    Highlights: • A-site divalent alkaline earth metal doped LaTiO 3−δ perovskites were synthesised by sol–gel method. • Structural studies revealed no change in crystal symmetry but change in cell dimensions after doping. • After doping divalent cations in A-site, an enhancement in total conductivity was observed in LaTiO 3−δ . • Temperature dependent electrical property was observed in all synthesised perovskites. - Abstract: Oxygen deficient perovskites LaTiO 3−δ and La 0.8 A 0.2 TiO 3−δ (A = Ba, Sr, Ca) were synthesized by sol–gel method. The effect of divalent dopants on microstructure is investigated in detail using X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The oxidation states of La 3+ and Ti 3+ ions have been deduced using X-ray Photoelectron Spectroscopy (XPS). Impedance spectroscopy was used to analyze the total conductivity, an increase in conductivity was observed after doping in the A-site with divalent cations Ba, Ca and Sr. Among the investigated perovskites La 0.8 Ca 0.2 TiO 3−δ exhibited the maximum conductivity of 1.22 × 10 −2 S/cm in air atmosphere at 650 °C

  5. Investigation of structural and optical properties of CaTiO3 powders doped with Mg2+ and Eu3+ ions

    International Nuclear Information System (INIS)

    Oliveira, Larissa H.; Savioli, Julia; Moura, Ana P. de; Nogueira, Içamira C.; Li, Maximo S.; Longo, Elson; Varela, José A.; Rosa, Ieda L.V.

    2015-01-01

    In this work, CaTiO 3 powders doped with Mg 2+ ions and CaTiO 3 powders co-doped with Mg 2+ and Eu 3+ ions were prepared by the polymeric precursor method (PPM). These powders were characterized by different characterization techniques to study the influence of Mg 2+ doping as well as Mg 2+ and Eu 3+ co-doping in structural and optical properties of CaTiO 3 perovskite-type structure. The Rietveld refinement and Micro-Raman analyses suggested the substitution Mg 2+ and Eu 3+ ions in the A-site of CaTiO 3 perovskite. The influence of Mg 2+ doping can be detected by the displacement of calcium and oxygen atomic positions when compared to the non-doped CaTiO 3 powder. When Eu 3+ ions are added to the A-site of this perovskite the excess of positive charge can be compensated by the formation of calcium vacancies. Luminescence data showed that Ca 1-x Mg x TiO 3 and Ca 1x Mg x/2 Eu 2y/3 TiO 3 powders are potential materials for fabrication of lighting devices based on near-UV and blue LED using an excitation wavelength of 397 and/or 450 nm. - Highlights: • CaTiO 3 co-doped with Mg 2+ and Eu 3+ were obtained by the Polymeric Precursor Method. • Incorporation of Mg 2+ and Eu 3+ ions in the CaTiO 3 lattice. • Enhancement of the Eu 3+ photoluminescence

  6. Recyclable UV and visible light photocatalytically active amorphous TiO2 doped with M (III) ions (M = Cr and Fe)

    International Nuclear Information System (INIS)

    Buddee, Supat; Wongnawa, Sumpun; Sirimahachai, Uraiwan; Puetpaibool, Walailak

    2011-01-01

    Research highlights: → The low photocatalytic activity of amorphous TiO2 was enhanced by doping with Cr(III) or Fe(III) ions. → The doped catalysts performed close to P25 under UV light and better with visible light. → The doped catalysts can be recycled. - Abstract: Samples of amorphous TiO 2 doped with Cr(III) and Fe(III), designated as Cr-TiO 2 and Fe-TiO 2 , were prepared via modified impregnation method. The resulting products were characterized by X-ray diffraction, scanning electron microscopy, specific surface area by the Brunauer, Emmett and Teller method, UV-vis absorption and diffuse reflectance spectroscopy, and electron spin resonance spectroscopy. Experimental results revealed that the concentrations of dopants under studied, from 0.05 to 0.2 mol%, had no effect on the phase of products. The band gap energies shifted from 3.28 eV in the undoped amorphous TiO 2 to 2.50 eV and 2.86 eV for Fe-TiO 2 and Cr-TiO 2 , respectively. The doped amorphous TiO 2 showed photocatalytic activities under both UV and visible light with optimal results at 0.1 mol% dopants. Under UV irradiation, the 0.1 mol% doped samples decolorized methylene blue solutions to the same extent as the commercial TiO 2 samples (P25 and anatase) in 5 h. Under visible light, the doped samples decolorized dye solutions in 12 h while the commercial ones were much less active. The used catalysts can be recycled many times without any special treatment.

  7. N-doped TiO2 photo-catalyst for the degradation of 1,2-dichloroethane under fluorescent light

    International Nuclear Information System (INIS)

    Lin, Yi-Hsing; Chiu, Tang-Chun; Hsueh, Hsin-Ta; Chu, Hsin

    2011-01-01

    The photo-catalytic degradation of 1,2-dichloroethane (1, 2-DCE) using nitrogen-doped TiO 2 photo-catalysts under fluorescent light irradiation was investigated. Highly pure TiO 2 and nitrogen-doped TiO 2 were prepared by a sol-gel method and characterized by thermo-gravimetric/differential-thermal analysis (TG/DTA), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared (FTIR) spectroscopy. The results indicate that the photo-catalysts were mainly nano-size with an anatase-phase structure. The degradation reaction of 1,2-DCE was operated under visible-light irradiation, and the photo-catalytic oxidation was conducted in a batch photo-reactor with various nitrogen doping ratios (N/Ti = 0-25 mol%). The relative humidity (RH) was controlled at 0-20% and the oxygen concentration was controlled at 0-21%. The photo-degradation with nitrogen-doped TiO 2 showed superior photo-catalytic activity compared to that for pure TiO 2 . TiO 2 doped with 15 mol% nitrogen exhibited the best photo-catalytic efficiency under the tested conditions. The products from the 1,2-DCE photo-catalytic oxidation were CO 2 and water; the by-products included dichloromethane, methyl chloride, ethyl chloride, carbon monoxide, and hydrogen chloride. The reaction pathway of 1,2-DCE indicates that oxygen molecules are the major factor that causes the degradation of 1,2-DCE in the gas phase.

  8. Room temperature one-step synthesis of microarrays of N-doped flower-like anatase TiO{sub 2} composed of well-defined multilayer nanoflakes by Ti anodization

    Energy Technology Data Exchange (ETDEWEB)

    Wang Chenglin; Wang Mengye; Xie Kunpeng; Wu Qi; Sun Lan; Lin Changjian [Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005 (China); Lin Zhiqun, E-mail: sunlan@xmu.edu.cn, E-mail: cjlin@xmu.edu.cn [Department of Materials Science and Engineering, Iowa State University, Ames, IA 50011 (United States)

    2011-07-29

    Microarrays of N-doped flower-like TiO{sub 2} composed of well-defined multilayer nanoflakes were synthesized at room temperature by electrochemical anodization of Ti in NH{sub 4}F aqueous solution. The TiO{sub 2} flowers were of good anatase crystallinity. The effects of anodizing time, applied voltage and NH{sub 4}F concentration on the flower-like morphology were systematically examined. It was found that the morphologies of the anodized Ti were related to the anodizing time and NH{sub 4}F concentration. The size and density of the TiO{sub 2} flowers could be tuned by changing the applied voltage. The obtained N-doped flower-like TiO{sub 2} microarrays exhibited intense absorption in wavelengths ranging from 320 to 800 nm. Under both UV and visible light irradiation, the photocatalytic activity of the N-doped flower-like TiO{sub 2} microarrays in the oxidation of methyl orange showed a significant increase compared with that of commercial P25 TiO{sub 2} film.

  9. Mild solution-processed metal-doped TiO2 compact layers for hysteresis-less and performance-enhanced perovskite solar cells

    Science.gov (United States)

    Liang, Chao; Li, Pengwei; Zhang, Yiqiang; Gu, Hao; Cai, Qingbin; Liu, Xiaotao; Wang, Jiefei; Wen, Hua; Shao, Guosheng

    2017-12-01

    TiO2 is extensively used as electron-transporting material on perovskite solar cells (PSCs). However, traditional TiO2 processing method needs high annealing temperature (>450 °C) and pure TiO2 suffers from low electrical mobility and poor conductivity. In this study, a general one-pot solution-processed method is devised to grow uniform crystallized metal-doped TiO2 thin film as large as 15 × 15 cm2. The doping process can be controlled effectively via a series of doping precursors from niobium (V), tin (IV), tantalum (V) to tungsten (VI) chloride. As far as we know, this is so far the lowest processing temperature for metal-doped TiO2 compact layers, as low as 70 °C. The overall performance of PSCs employing the metal-doped TiO2 layers is significantly improved in term of hysteresis effect, short circuit current, open-circuit voltage, fill factor, power conversion efficiency, and device stability. With the insertion of metal ions into TiO2 lattice, the corresponding CH3NH3PbI3 PSC leads to a ∼25% improved PCE of over 16% under irradiance of 100 mW cm-2 AM1.5G sunlight, compared with control device. The results indicate that this mild solution-processed metal-doped TiO2 is an effective industry-scale way for fabricating hysteresis-less and high-performance PSCs.

  10. Enhanced photocatalytic activity for H2 evolution under irradiation of UV-vis light by Au-modified nitrogen-doped TiO2.

    Science.gov (United States)

    Zhao, Weirong; Ai, Zhuyu; Dai, Jiusong; Zhang, Meng

    2014-01-01

    Photocatalytic water splitting for hydrogen evolution is a potential way to solve many energy and environmental issues. Developing visible-light-active photocatalysts to efficiently utilize sunlight and finding proper ways to improve photocatalytic activity for H2 evolution have always been hot topics for research. This study attempts to expand the use of sunlight and to enhance the photocatalytic activity of TiO2 by N doping and Au loading. Au/N-doped TiO2 photocatalysts were synthesized and successfully used for photocatalytic water splitting for H2 evolution under irradiation of UV and UV-vis light, respectively. The samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV-vis diffuse reflectance spectroscopy (DRS), photoluminescence spectroscopy (PL), and photoelectrochemical characterizations. DRS displayed an extension of light absorption into the visible region by doping of N and depositing with Au, respectively. PL analysis indicated electron-hole recombination due to N doping and an efficient inhibition of electron-hole recombination due to the loaded Au particles. Under the irradiation of UV light, the photocatalytic hydrogen production rate of the as-synthesized samples followed the order Au/TiO2 > Au/N-doped TiO2 > TiO2 > N-doped TiO2. While under irradiation of UV-vis light, the N-TiO2 and Au/N-TiO2 samples show higher H2 evolution than their corresponding nitrogen-free samples (TiO2 and Au/TiO2). This inconsistent result could be attributed to the doping of N and the surface plasmonic resonance (SPR) effect of Au particles extending the visible light absorption. The photoelectrochemical characterizations further indicated the enhancement of the visible light response of Au/N-doped TiO2. Comparative studies have shown that a combination of nitrogen doping and Au loading enhanced the visible light response of TiO2 and increased the utilization of solar energy, greatly

  11. Enhanced photocatalytic activity for H2 evolution under irradiation of UV-vis light by Au-modified nitrogen-doped TiO2.

    Directory of Open Access Journals (Sweden)

    Weirong Zhao

    Full Text Available BACKGROUND PURPOSE: Photocatalytic water splitting for hydrogen evolution is a potential way to solve many energy and environmental issues. Developing visible-light-active photocatalysts to efficiently utilize sunlight and finding proper ways to improve photocatalytic activity for H2 evolution have always been hot topics for research. This study attempts to expand the use of sunlight and to enhance the photocatalytic activity of TiO2 by N doping and Au loading. METHODS: Au/N-doped TiO2 photocatalysts were synthesized and successfully used for photocatalytic water splitting for H2 evolution under irradiation of UV and UV-vis light, respectively. The samples were characterized using X-ray diffraction (XRD, transmission electron microscopy (TEM, X-ray photoelectron spectroscopy (XPS, UV-vis diffuse reflectance spectroscopy (DRS, photoluminescence spectroscopy (PL, and photoelectrochemical characterizations. RESULTS: DRS displayed an extension of light absorption into the visible region by doping of N and depositing with Au, respectively. PL analysis indicated electron-hole recombination due to N doping and an efficient inhibition of electron-hole recombination due to the loaded Au particles. Under the irradiation of UV light, the photocatalytic hydrogen production rate of the as-synthesized samples followed the order Au/TiO2 > Au/N-doped TiO2 > TiO2 > N-doped TiO2. While under irradiation of UV-vis light, the N-TiO2 and Au/N-TiO2 samples show higher H2 evolution than their corresponding nitrogen-free samples (TiO2 and Au/TiO2. This inconsistent result could be attributed to the doping of N and the surface plasmonic resonance (SPR effect of Au particles extending the visible light absorption. The photoelectrochemical characterizations further indicated the enhancement of the visible light response of Au/N-doped TiO2. CONCLUSION: Comparative studies have shown that a combination of nitrogen doping and Au loading enhanced the visible light response of

  12. Corrosion protection of AISI 1018 steel using Co-doped TiO{sub 2}/polypyrrole nanocomposites in 3.5% NaCl solution

    Energy Technology Data Exchange (ETDEWEB)

    Ladan, Magaji, E-mail: ladanmagaji@yahoo.com [Department of Chemistry, Faculty of Science, University of Malaya, Kuala Lumpur, 50603 (Malaysia); Department of Pure and Industrial Chemistry, Bayero University Kano (Nigeria); Basirun, Wan Jeffrey, E-mail: jeff@um.edu.my [Department of Chemistry, Faculty of Science, University of Malaya, Kuala Lumpur, 50603 (Malaysia); Institute of Nanotechnology and Catalysis (NanoCat), University of Malaya, Kuala Lumpur, 50603 (Malaysia); Kazi, Salim Newaz; Rahman, Fariza Abdul [Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur, 50603 (Malaysia)

    2017-05-01

    A polypyrrole nanocomposites (PPy NTCs) have been effectively synthesized in the presence of TiO{sub 2} and Co-doped TiO{sub 2} nanoparticles (NPs) by an in situ chemical oxidative polymerization. Field Emission Scanning Electron Microscopy and Transmission Electron Microscopy revealed a tube shape structure of the PPy. The TEM results confirmed that the nanocomposite size of Co-doped TiO{sub 2}/PPy NTCs was smaller than TiO{sub 2}/PPy NTCs thereby increasing the interaction between the PPy nanotube and the AISI steel surface. The corrosion performance of the coatings was evaluated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization measurements in 3.5% NaCl solution. The EIS results show that the log |Z| of AISI 1018 coated with Co-doped TiO{sub 2}/PPy NTCs and TiO{sub 2}/PPy NTCs reached about 8.2 and 6.0 respectively after 30 days of exposure in 3.5% NaCl solution. This is likely due to the increased surface area of the PPy synthesized in the presence of Co-doped TiO{sub 2} NPs. The EIS results are confirmed by the potentiodynamic polarization and open circuit potential values of the Co-doped TiO{sub 2}/PPy which indicated little changes between 1 and 30 days of exposure which confirms the protection ability of this coating. . It is evident that the presence of Co-doped TiO{sub 2} NPs can enhance the resistance against corrosion at the steel/electrolyte interface. - Highlights: • Polymerization of pyrrole monomer in the presence of Co-doped TiO{sub 2} decreases the size of the polypyrrole nanotube (PPy NT). • The corrosion protection increases with the increase in PPy NT dispersion. • The corrosion resistance of steel coated with Co-doped TiO{sub 2}/PPy NTCs is considerably higher. • TiO{sub 2}/PPy with Co doping reduces the charge transfer across the electrolyte/AISI 1018 steel interface.

  13. Characteristics of N-doped TiO{sub 2} nanotube arrays by N{sub 2}-plasma for visible light-driven photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Liu Xu [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China); Liu Zhongqing, E-mail: 301zql@vip.sina.com [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China); Zheng Jian; Yan Xin; Li Dandan; Chen Si [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China); Chu Wei, E-mail: chuwei1965_scu@yahoo.com [College of Chemical Engineering, Sichuan University, Chengdu 610065 (China)

    2011-10-13

    Highlights: > A new pathway is provided to prepare N-doped TiO2 nanotube arrays using N{sub 2}-plasma treatment. > N{sub 2}-plasma treatment did not wreck the structure of nanotube arrays. > Nitrogen doping promoted the phase transition to rutile phase at low annealing temperatures > Nitrogen doping narrow band gap of TiO{sub 2} and improve the photocatalytic activity of samples. - Abstract: N-doped TiO{sub 2} nanotube arrays were prepared by electrochemical anode oxidation of Ti foil followed by treatment with N{sub 2}-plasma and subsequent annealed under Ar atmosphere. The morphologies, composition and optical properties of N-doped TiO{sub 2} nanotube arrays were characterized using field-emission scanning electron microscope (FE-SEM), transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction spectrometer (XRD), Photoluminescence (PL) and UV-vis diffusion reflection spectroscopy (UV-vis DRS). Methylene blue (MB) solution was utilized as the degradation model to evaluate the photocatalytic activity of the samples under visible light irradiation. The results suggested N{sub 2}-plasma treatment created doping of nitrogen onto the surface of photoelectrodes successfully and the N-doped TiO{sub 2} nanotube arrays display a significantly enhancement of the photocatalytic activity comparing with the pure TiO{sub 2} nanotube arrays under the visible light irradiation.

  14. Role of Zn doping in oxidative stress mediated cytotoxicity of TiO2 nanoparticles in human breast cancer MCF-7 cells

    Science.gov (United States)

    Ahamed, Maqusood; Khan, M. A. Majeed; Akhtar, Mohd Javed; Alhadlaq, Hisham A.; Alshamsan, Aws

    2016-07-01

    We investigated the effect of Zn-doping on structural and optical properties as well as cellular response of TiO2 nanoparticles (NPs) in human breast cancer MCF-7 cells. A library of Zn-doped (1-10 at wt%) TiO2 NPs was prepared. Characterization data indicated that dopant Zn was incorporated into the lattice of host TiO2. The average particle size of TiO2 NPs was decreases (38 to 28 nm) while the band gap energy was increases (3.35 eV-3.85 eV) with increasing the amount of Zn-doping. Cellular data demonstrated that Zn-doped TiO2 NPs induced cytotoxicity (cell viability reduction, membrane damage and cell cycle arrest) and oxidative stress (reactive oxygen species generation & glutathione depletion) in MCF-7 cells and toxic intensity was increases with increasing the concentration of Zn-doping. Molecular data revealed that Zn-doped TiO2 NPs induced the down-regulation of super oxide dismutase gene while the up-regulation of heme oxygenase-1 gene in MCF-7 cells. Cytotoxicity induced by Zn-doped TiO2 NPs was efficiently prevented by N-acetyl-cysteine suggesting that oxidative stress might be the primarily cause of toxicity. In conclusion, our data indicated that Zn-doping decreases the particle size and increases the band gap energy as well the oxidative stress-mediated toxicity of TiO2 NPs in MCF-7 cells.

  15. Microwave-assisted self-doping of TiO2 photonic crystals for efficient photoelectrochemical water splitting

    KAUST Repository

    Zhang, Zhonghai; Yang, Xiulin; Hedhili, Mohamed N.; Ahmed, Elaf S.; Shi, Le; Wang, Peng

    2014-01-01

    In this article, we report that the combination of microwave heating and ethylene glycol, a mild reducing agent, can induce Ti3+ self-doping in TiO2. A hierarchical TiO2 nanotube array with the top layer serving as TiO2 photonic crystals (TiO2 NTPCs

  16. Photoluminescence studies on Eu doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Ningthoujam, R.S.; Sudarsan, V.; Vatsa, R.K.; Kadam, R.M.; Jagannath; Gupta, A.

    2009-01-01

    Eu 3+ doped TiO 2 nanoparticles were prepared by urea hydrolysis in ethylene glycol medium at low temperature of 150 deg. C. X-ray diffraction study showed that anatase phase of tetragonal structure was formed below 500 deg. C; and above this temperature, additional peaks due to rutile phase were also observed. From luminescence study, it was found that as prepared nanoparticles showed the enhanced luminescence intensity due to energy transfer from host to europium ions. However, photoluminescence from these nanoparticles was found to disappear when the samples were heated above 900 deg. C. We established the origin of the reduction in the luminescence intensity from Eu 3+ when doped in TiO 2 and heated at 900 deg. C. Based on detailed studies at different heat-treatment temperatures using techniques such as X-ray diffraction, X-ray photoelectron spectroscopy, electron paramagnetic resonance, Raman spectroscopy, and Moessbauer spectroscopy, it has been established that formation of Eu 2 Ti 2 O 7 phase, wherein Eu 3+ ions occupy high symmetric environment (D 3d ) and also reduced distance between Eu 3+ and Eu 3+ ions is responsible for the decrease/loss in the luminescence intensity.

  17. Multiwalled carbon nanotubes decorated with nitrogen, palladium co-doped TiO2 (MWCNT/N, Pd co-doped TiO2) for visible light photocatalytic degradation of Eosin Yellow in water

    Science.gov (United States)

    Kuvarega, Alex T.; Krause, Rui W. M.; Mamba, Bhekie B.

    2012-03-01

    Multiwalled carbon nanotube (MWCNT/N), Pd co-doped TiO2 nanocomposites were prepared by calcining the hydrolysis products of the reaction of titanium isopropoxide, Ti(OC3H7)4 containing multiwalled carbon nanotubes with aqueous ammonia. The prepared samples were characterised by Fourier transform infrared spectroscopy, Raman spectroscopy, thermogravimetric analysis, diffuse reflectance UV-Vis spectrophotometry (DRUV-Vis), XRD, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). DRUV-Vis analysis confirmed the red shift in the absorption edge at lower MWCNT percentages. SEM and TEM images showed the complete coverage of the MWCNTs with clusters of anatase TiO2 at low MWCNT percentages. Higher MWCNT levels led to their aggregation and consequently poor coverage by N, Pd co-doped TiO2. The photocatalytic activities of the nanocomposites were monitored by photodegradation of Eosin Yellow under simulated solar and visible light irradiation (λ > 450 nm). Irradiation with simulated solar radiation gave higher dye-degradation rates compared to visible radiation. The optimum MWCNT weight percentage in the composites was found to be 0.5. High degradation-rate constants of 3.42 × 10-2 and 5.18 × 10-3 min-1 were realised for the 0.5% MWCNT/N, Pd co-doped TiO2 composite, using simulated solar light and visible light, respectively.

  18. Preparation and Characterization of Mn/N Co-Doped TiO2 Loaded on Wood-Based Activated Carbon Fiber and Its Visible Light Photodegradation

    Directory of Open Access Journals (Sweden)

    Xiaojun Ma

    2015-09-01

    Full Text Available Using MnSO4·H2O as manganese source and urea as nitrogen source, Mn/N co-doped TiO2 loaded on wood-based activated carbon fiber (Mn/Ti-N-WACF was prepared by sol–gel method. Mn/Ti-N-WACF with different Mn doping contents was characterized by scanning electron microscopy, X-ray diffraction (XRD and X-ray photoelectron spectroscopies (XPS, and ultraviolet-visible spectrophotometer. Results showed that the loading rate of TiO2 in Mn/Ti-N-WACF was improved by Mn/N co-doping. After calcination at 450 °C, the degree of crystallinity of TiO2 was reduced due to Mn/N co-doption in the resulting Mn/Ti-N-WACF samples, but the TiO2 crystal phase was not changed. XPS spectra revealed that some Ti4+ ions from the TiO2 lattice of Mn/Ti-N-WACF system were substituted by doped Mn. Moreover, new bonds formed within N–Ti–N and Ti–N–O because of the doped N that substituted some oxygen atoms in the TiO2 lattice. Notably, the degradation rate of methylene blue for Mn/Ti-N-WACF was improved because of the co-doped Mn/N under visible-light irradiation.

  19. Microwave-Hydrothermal Synthesis and Characterization of High-Purity Nb Doped BaTiO3 Nanocrystals

    Directory of Open Access Journals (Sweden)

    A. Khanfekr

    2014-01-01

    Full Text Available The synthesis of Nb doped BaTiO3 has been investigated under Microwave-Hydrothermal (MH conditions in the temperature of 150°C for only 2 h using C16H36O4Ti, BaH2O2.8H2O and NbCl5 as Ba, Ti and  Nb sources, respectively.  Typical experiments performed on MH processing have not yet reported for Nb doped BaTiO3.  In the MH process, the formation of high purity nano tetragonal Nb-BaTiO3 was strongly enhanced. New hydrothermal method was used instead of the previous solid state reaction for the BaTiO3±Nb2O3 system. The new method uses high pressure to create nano dimension particles in a lower time and temperature. In case of the phase evolution studies, the XRD pattern measurements and Raman spectroscopy were performed. TEM and FE-SEM images were taken for the detailed analysis of the particle size, surface and morphology.  Synthesis of Nb doped BaTiO3 with the Microwave-hydrothermal provides an advantage of fast crystallization and reduced crystal size when compared to existing methods.

  20. Fabrication and photovoltaic performance of niobium doped TiO{sub 2} hierarchical microspheres with exposed {001} facets and high specific surface area

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Yongqiang; Ran, Huili [School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001 (China); State Centre for International Cooperation on Designer Low-Carbon and Environmental Materials, Zhengzhou University, Zhengzhou 450001 (China); Fan, Jiajie, E-mail: fanjiajie@zzu.edu.cn [School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001 (China); State Centre for International Cooperation on Designer Low-Carbon and Environmental Materials, Zhengzhou University, Zhengzhou 450001 (China); Zhang, Xiaoli; Mao, Jing [School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001 (China); State Centre for International Cooperation on Designer Low-Carbon and Environmental Materials, Zhengzhou University, Zhengzhou 450001 (China); Shao, Guosheng [School of Materials Science and Engineering, Zhengzhou University, Zhengzhou 450001 (China); State Centre for International Cooperation on Designer Low-Carbon and Environmental Materials, Zhengzhou University, Zhengzhou 450001 (China); Institute for Renewable Energy and Environmental Technologies, University of Bolton, Bolton BL3 5AB (United Kingdom)

    2017-07-15

    Highlights: • Nb-doped hierarchical TiO{sub 2} microsphere DSSCs show enhanced performance. • Nb{sup 5+} dopant replaces Ti{sup 4+} cation in TiO{sub 2} lattice. • Electrons transport was enhanced due to the down-shifted conduction band minimum. • Exposed (001) facets and high specific surface area allows high dye-loading. - Abstract: The niobium doped hierarchical anatase TiO{sub 2} microspheres, which are consist of a serried nano-thorns and plicate nano-ribbons with exposed {001} facets, were synthesized using hydrothermal method followed by heat treatment. The effects of niobium on the microstructures and photovoltaic performances of the dye-sensitized solar cells (DSSCs) were studied. The results revealed that Nb{sup 5+} doping replaces Ti{sup 4+} cations in TiO{sub 2} lattice, and the bandgap of the films varies with increasing Nb doping concentration because of the downshift of the conduction band minimum (CBM). The niobium-doped TiO{sub 2} DSSCs with moderate loadings show enhanced performance comparing with their pure TiO{sub 2} counterparts. Optimally, the conversion efficiency of the Nb-3.5 (Nb 3.5 mol%) DSSC is 4.99%. This is higher than that (4.39%) of pure TiO{sub 2} cells by 13.7%. This is due to the fact that the Nb-doped solar cells have increased the number of the photo-induced electrons because of their exposed (001) facets and higher specific surface area; and enhanced electrons collection and transport because of the downshifted CBM of the Nb-doped TiO{sub 2}. However, heavy Nb doping results in the decrease of the performance of the niobium-doped cells due to the excessive defects within the Nb-TiO{sub 2} samples resulting in enhanced charge recombination at defects.

  1. Blue to Yellow Photoluminescence Emission and Photocatalytic Activity of Nitrogen Doping in TiO2 Powders

    Directory of Open Access Journals (Sweden)

    Gabriela Byzynski

    2015-01-01

    Full Text Available The defects caused by doping are important for understanding the increased photocatalytic activities of TiO2:N in organic reactions and in the evaluation of OH radical production after doping. TiO2:N was therefore synthesized using a modified polymeric method and N doping was performed by calcination with urea. The resulting powders were characterized using field emission scanning electron microscopy, X-ray diffraction, diffuse reflectance spectroscopy, Raman spectroscopy, Fourier transformation infrared spectroscopy, and photoluminescence emission spectroscopy (PL. N doping did not alter the morphology of the nanoparticles, and the anatase phase predominated, with the retention of the rutile phase. The band gap values, superficial areas, and crystallite sizes of the powders decreased after doping. The PL results showed an additional energy level in the TiO2:N band gap structure as a result of TiO2 lattice defects caused by doping. At low N contents, the powders showed continuous emissions from the blue region to the yellow region and a high N content shifted the PL emissions to the red region. These results suggest that the use of these powders could increase the efficiencies of solar cells and water-splitting processes. The photocatalytic activity of the powders under UVC illumination was confirmed for different organic dye molecules. The OH radical production did not change extensively after doping, as shown by experiments with terephthalic acid, and higher photocatalytic efficiencies in Rhodamine-B degradation under UVC illumination were achieved using the doped samples.

  2. High rate capability of TiO{sub 2}/nitrogen-doped graphene nanocomposite as an anode material for lithium–ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Cai, Dandan; Li, Dongdong; Wang, Suqing [School of Chemistry and Chemical Engineering, South China University of Technology, Wushan Road, Guangzhou (China); Zhu, Xuefeng; Yang, Weishen [State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian (China); Zhang, Shanqing [Centre for Clean Environment and Energy, Environmental Futures Centre and Griffith School of Environment, Gold Coast Campus, Griffith University, QLD 4222 (Australia); Wang, Haihui, E-mail: hhwang@scut.edu.cn [School of Chemistry and Chemical Engineering, South China University of Technology, Wushan Road, Guangzhou (China)

    2013-06-05

    Highlights: ► TiO{sub 2}/N-doped graphene composite was synthesized by a gas/liquid interfacial method. ► The nanocomposite was used to fabricate lithium-ion batteries. ► Its electrochemical performance was evaluated for the first time. ► The anode material exhibits a good cycling performance and rate capability. -- Abstract: TiO{sub 2}/nitrogen-doped graphene nanocomposite was synthesized by a facile gas/liquid interface reaction. The structure and morphology of the sample were analyzed by X-ray diffraction analysis, X-ray photoelectron spectroscopy, scanning electron microscopy and transmission electron microscopy. The results indicate that nitrogen atoms were successfully doped into graphene sheets. The TiO{sub 2} nanoparticles (8–13 nm in size) were homogenously anchored on the nitrogen-doped graphene sheets through gas/liquid interface reaction. The as-prepared TiO{sub 2}/nitrogen-doped graphene nanocomposite shows a better electrochemical performance than the TiO{sub 2}/graphene nanocomposite and the bare TiO{sub 2} nanoparticles. TiO{sub 2}/nitrogen-doped graphene nanocomposite exhibits excellent cycling stability and shows high capacity of 136 mAh g{sup −1} (at a current density of 1000 mA g{sup −1}) after 80 cycles. More importantly, a high reversible capacity of 109 mAh g{sup −1} can still be obtained even at a super high current density of 5000 mA g{sup −1}. The superior electrochemical performance is attributed to the good electronic conductivity introduced by the nitrogen-doped graphene sheets and the positive synergistic effect between nitrogen-doped graphene sheets and TiO{sub 2} nanoparticles.

  3. In Situ Fluorine Doping of TiO2 Superstructures for Efficient Visible-Light Driven Hydrogen Generation.

    Science.gov (United States)

    Zhang, Peng; Tachikawa, Takashi; Fujitsuka, Mamoru; Majima, Tetsuro

    2016-03-21

    With the aid of breakthroughs in nanoscience and nanotechnology, it is imperative to develop metal oxide semiconductors through visible light-driven hydrogen generation. In this study, TiOF2 was incorporated as an n-type F-dopant source to TiO2 mesocrystals (TMCs) with visible-light absorption during the topotactic transformation. The crystal growth, structural change, and dynamic morphological evolution, from the initial intermediate NH4 TiOF3 to HTiOF3, TiOF2, and F-doped TMCs, were verified through in situ temperature-dependent techniques to elucidate the doping mechanism from intermediate TiOF2. The visible-light efficiencies of photocatalytic hydrogen were dependent on the contents of the dopant as compared with the pure TMC and a controled reference. Using femtosecond time-resolved diffuse reflectance spectroscopy, the charge-transfer dynamics were monitored to confirm the improvement of charge separation after doping. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  4. A short literature survey on iron and cobalt ion doped TiO{sub 2} thin films and photocatalytic activity of these films against fungi

    Energy Technology Data Exchange (ETDEWEB)

    Tatl Latin-Small-Letter-Dotless-I dil, Ilknur [Department of Chemistry, Faculty of Science, Karadeniz Technical University, 61080 Trabzon (Turkey); Bacaks Latin-Small-Letter-Dotless-I z, Emin [Department of Physics, Faculty of Science, Karadeniz Technical University, 61080 Trabzon (Turkey); Buruk, Celal Kurtulus [Department of Microbiology, Faculty of Medicine, Karadeniz Technical University, 61080 Trabzon (Turkey); Breen, Chris [Materials and Engineering Research Institution, Sheffield Hallam University, Sheffield S1 1WB (United Kingdom); Soekmen, Muenevver, E-mail: msokmen@ktu.edu.tr [Department of Chemistry, Faculty of Science, Karadeniz Technical University, 61080 Trabzon (Turkey)

    2012-03-15

    Highlights: Black-Right-Pointing-Pointer Co or Fe doped TiO{sub 2} thin films were prepared by sol-gel method. Black-Right-Pointing-Pointer We obtained lower E{sub g} values for Fe-doped and Co-TiO{sub 2} thin films. Black-Right-Pointing-Pointer Doping greatly affected the size and shape of the TiO{sub 2} nanoparticles. Black-Right-Pointing-Pointer Photocatalytic killing effect of the doped TiO{sub 2} thin films on C. albicans and A. niger was significantly higher than undoped TiO{sub 2} thin film for short exposure periods. - Abstract: In this study, a short recent literature survey which concentrated on the usage of Fe{sup 3+} or Co{sup 2+} ion doped TiO{sub 2} thin films and suspensions were summarized. Additionally, a sol-gel method was used for preparation of the 2% Co or Fe doped TiO{sub 2} thin films. The surface of the prepared materials was characterised using scanning-electron microscopy (SEM) combined with energy dispersive X-ray (EDX) analysis and band gap of the films were calculated from the transmission measurements that were taken over the range of 190 and 1100 nm. The E{sub g} value was 3.40 eV for the pure TiO{sub 2}, 3.00 eV for the Fe-doped TiO{sub 2} film and 3.25 eV for Co-TiO{sub 2} thin film. Iron or cobalt doping at lower concentration produce more uniformed particles and doping greatly affected the size and shape of the TiO{sub 2} nanoparticles. Photocatalytic killing effect of the 2% Co doped TiO{sub 2} thin film on Candida albicans was significantly higher than Fe doped TiO{sub 2} thin film for short and long exposure periods. Doped thin films were more effective on Aspergillus niger for short exposure periods.

  5. Properties of Sn-doped TiO2 nanotubes fabricated by anodization of co-sputtered Ti–Sn thin films

    International Nuclear Information System (INIS)

    Kyeremateng, Nana Amponsah; Hornebecq, Virginie; Knauth, Philippe; Djenizian, Thierry

    2012-01-01

    Self-organized Sn-doped TiO 2 nanotubes (nts) were fabricated for the first time, by anodization of co-sputtered Ti and Sn thin films. This nanostructured material was characterized by scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, UV–vis spectroscopy and transmission electron microscopy. Due to their remarkable properties, Sn-doped TiO 2 nts can find potential applications in Li-ion microbatteries, photovoltaics, and catalysis. Particularly, the electrochemical performance as an anode material for Li-ion microbatteries was evaluated in Li test cells. With current density of 70 μA cm −2 (1 C) and cut-off potential of 1 V, Sn-doped TiO 2 nts showed improved performance compared to simple TiO 2 nts, and differential capacity plots revealed that the material undergoes full electrochemical reaction as a Rutile-type TiO 2 .

  6. Preparation of Ni Doped ZnO-TiO2 Composites and Their Enhanced Photocatalytic Activity

    Directory of Open Access Journals (Sweden)

    Xiaowen Zou

    2014-01-01

    Full Text Available Herein, Ni doped ZnO-TiO2 composites were prepared by facile sol-gel approach and were characterized by X-ray diffraction (XRD, transmission electron microscopy (TEM, UV-visible diffuse reflectance spectroscopy (UV-Vis DRS, X-ray photoelectron spectroscopy (XPS, and photoluminescence spectroscopy (PL. The results indicated that the Ni ions can be incorporated into the lattice of TiO2 structure and replace Ti. The introduction of Ni expanded light absorption of TiO2 to visible region, increased amount of surface hydroxyl groups and physically adsorbed oxygen (as the electronic scavenges, and then enhanced separation rate of photogenerated carriers. The photodegradation test of reactive brilliant blue (KN-R under simulated solar light indicated that Ni doped ZnO-TiO2 composites have better photocatalytic activities, as compared to those of TiO2 and ZnO-TiO2.

  7. Structural, Optical, Morphological and Elemental Analysis on Sol-gel Synthesis of Ni Doped TiO2 Nanocrystallites

    Directory of Open Access Journals (Sweden)

    T. Sakthivel

    2017-06-01

    Full Text Available Pure and Ni doped titanium dioxide nanoparticles were successfully synthesized by sol-gel method and characterized usingXRD, UV-Visible, FTIR, FESEM and EDS techniques. XRD pattern confirms the formation of tetragonal TiO2. The absorbance spectra of pure and Ni doped TiO2 showed absorption spectrum at ultra-violet region due to electronic transition between bonding and anti-bonding orbital (π-π•. Bandgap energy of Ni doped TiO2 decreased to 2.5 eV when compared to pure TiO2 (3.39 eV. FESEM study reveals agglomerated spherical shaped morphology. The functional groups of the prepared samples were identified using FTIR spectroscopy and the elemental analysis was further supported with EDS analysis.

  8. Photocatalytic activity of tin-doped TiO{sub 2} film deposited via aerosol assisted chemical vapor deposition

    Energy Technology Data Exchange (ETDEWEB)

    Chua, Chin Sheng, E-mail: cschua@simtech.a-star.edu.sg [School of Electrical and Electronic Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 (Singapore); Singapore Institute of Manufacturing Technology, 71 Nanyang Drive, 638075 (Singapore); Tan, Ooi Kiang; Tse, Man Siu [School of Electrical and Electronic Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 (Singapore); Ding, Xingzhao [Singapore Institute of Manufacturing Technology, 71 Nanyang Drive, 638075 (Singapore)

    2013-10-01

    Tin-doped TiO{sub 2} films are deposited via aerosol assisted chemical vapor deposition using a precursor mixture composing of titanium tetraisopropoxide and tetrabutyl tin. The amount of tin doping in the deposited films is controlled by the volume % concentration ratio of tetrabutyl tin over titanium tetraisopropoxide in the mixed precursor solution. X-ray diffraction analysis results reveal that the as-deposited films are composed of pure anatase TiO{sub 2} phase. Red-shift in the absorbance spectra is observed attributed to the introduction of Sn{sup 4+} band states below the conduction band of TiO{sub 2}. The effect of tin doping on the photocatalytic property of TiO{sub 2} films is studied through the degradation of stearic acid under UV light illumination. It is found that there is a 10% enhancement on the degradation rate of stearic acid for the film with 3.8% tin doping in comparison with pure TiO{sub 2} film. This improvement of photocatalytic performance with tin incorporation could be ascribed to the reduction of electron-hole recombination rate through charge separation and an increased amount of OH radicals which are crucial for the degradation of stearic acid. Further increase in tin doping results in the formation of recombination site and large anatase grains, which leads to a decrease in the degradation rate. - Highlights: ► Deposition of tin-doped TiO{sub 2} film via aerosol assisted chemical vapor deposition ► Deposited anatase films show red-shifted in UV–vis spectrum with tin-dopants. ► Photoactivity improves at low tin concentration but reduces at higher concentration. ► Improvement in photoactivity due to bandgap narrowing from Sn{sup 4+} band states ► Maximum photoactivity achieved occurs for films with 3.8% tin doping.

  9. Photo catalytic degradation of nitrobenzene using nanocrystalline TiO2 photo catalyst doped with Zn ions

    International Nuclear Information System (INIS)

    Reynoso S, E. A.; Perez S, S.; Reyes C, A. P.; Castro R, C. L.; Felix N, R. M.; Lin H, S. W.; Paraguay D, F.; Alonso N, G.

    2013-01-01

    Photo catalysis is a method widely used in the degradation of organic pollutants of the environment. The development of new materials is very important to improve the photo catalytic properties and to find new applications for TiO 2 as a photo catalyst. In this article we reported the synthesis of a photo catalyst based on TiO 2 doped with Zn 2+ ions highly efficient in the degradation of nitrobenzene. The results of photo catalytic activity experiments showed that the Zn 2+ doped TiO 2 is more active that un-doped TiO 2 catalyst with an efficiency of 99% for the nitrobenzene degradation at 120 min with an apparent rate constant of 35 x 10 -3 min -1 . For the characterization of photo catalyst X-ray diffraction, transmission electron microscopy and Raman spectroscopy were used. (Author)

  10. Al-doped TiO{sub 2} mesoporous material supported Pd with enhanced catalytic activity for complete oxidation of ethanol

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Jing, E-mail: mlczjsls123@163.com; Mu, Wentao, E-mail: mwt15035687833@163.com; Su, Liqing, E-mail: suliqing0163@163.com; Li, Xingying, E-mail: lixingying0479@link.tyut.edu.cn; Guo, Yuyu, E-mail: guoyuyu0455@link.tyut.edu.cn; Zhang, Shen, E-mail: zhangshen0472@link.tyut.edu.cn; Li, Zhe, E-mail: lizhe@tyut.edu.cn

    2017-04-15

    Pd catalysts supported on Al-doped TiO{sub 2} mesoporous materials were evaluated in complete oxidation of ethanol. The catalysts synthesized by wet impregnation based on evaporation-induced self-assembly were characterized by X-ray diffraction, measurement of pore structure, XPS, FT-IR, temperature programmed reduction and TEM. Characteristic results showed that the aluminium was doped into the lattice of mesoporous anatase TiO{sub 2} to form Al-O-Ti defect structure. Catalytic results revealed that Al-doped catalysts were much more active than the pristine one, especially at low temperature (≤200 °C). This should be ascribed to the introduction of aluminium ions that suppressed the strong metal-support interaction and increased the active sites of Pd oxides, enhanced the stabilized anatase TiO{sub 2}, improved well dispersed high valence palladium species with high reducibility and enriched chemisorption oxygen. - Graphical abstract: Al-doped Pd/TiO{sub 2} exhibited optimal catalytic performance for ethanol oxidation and CO{sub 2} yield by the suppression of SMSI. - Highlights: • Palladium catalysts supported on Al-doped TiO{sub 2} mesoporous materials were studied. • The introduction of Al can enhance anatase stabilization and increase defect TiO{sub 2}. • The Pd/Al-TiO{sub 2} catalysts show higher ethanol conversion and CO{sub 2} yield than Pd/TiO{sub 2}. • The influence of Al on SMSI and catalytic performance were evaluated by TPR and XPS.

  11. Synthesis and characterization of Fe3+ doped TiO2 nanoparticles and films and their performance for photocurrent response under UV illumination

    International Nuclear Information System (INIS)

    Elghniji, Kais; Atyaoui, Atef; Livraghi, Stefano; Bousselmi, Latifa; Giamello, Elio; Ksibi, Mohamed

    2012-01-01

    Graphical abstract: Schematic diagram illustrating the charge transfer from excited TiO 2 to the different states of Fe 3+ ions; C B and V B refer to the energy levels of the conduction and valence bands of TiO 2 , respectively. Highlights: ► In this study we examine the Iron as catalyst precursor to synthesize the Fe 3+ doped TiO 2 nanoparticles. ► The Fe 3+ doped TiO 2 catalysts show the presence of a mixed phase of anatase. ► The iron is completely absent in the XRD pattern of the doped iron TiO 2 powder. ► The analysis of EPR result further confirms that Fe 3+ ion are successfully doped in the TiO 2 lattice by substituting Ti 4+ . ► Fe 3+ doping can efficiently separate the photo-generated electrons and holes. - Abstract: Undoped TiO 2 and Fe 3+ doped (0.1, 0.3, 0.6 and 1 wt.%) TiO 2 nanoparticles have been synthesized by the acid-catalyzed sol–gel method. Iron cations are introduced in the initial solution, before gelification, what promotes their lattice localization. The Fe 3+ doped TiO 2 films have been fabricated using a dip-coating technique. The effect of iron content on the crystalline structure, phase transformation and grain growth were determined by X-ray diffraction (XRD), Raman spectroscopy, UV–visible diffused reflectance spectroscopy (DRS) and Electron paramagnetic resonance (EPR) spectroscopy. It has demonstrated that all catalysts are composed of mixed-phase crystals of anatase and brookite with anatase as dominant phase. The crystallinity of the brookite and anatase phases decreased with increasing the iron content. The analysis of EPR result further confirms that Fe 3+ ion are successfully doped in the TiO 2 lattice by substituting Ti 4+ . It was demonstrated that Fe 3+ ion in the TiO 2 films plays a role as the intermediate for the efficient separation of photogenerated hole–electron pairs and increases the photocurrent response of the film under UV light irradiation. The maximum photocurrent is obtained on the Fe 3+ doped Ti

  12. Eco-friendly synthesis of TiO2, Au and Pt doped TiO2 nanoparticles for dye sensitized solar cell applications and evaluation of toxicity

    Science.gov (United States)

    Gopinath, K.; Kumaraguru, S.; Bhakyaraj, K.; Thirumal, S.; Arumugam, A.

    2016-04-01

    Driven by the demand of pure TiO2, Au and Pt doped TiO2 NPs were successfully synthesized using Terminalia arjuna bark extract. The eco-friendly synthesized NPs were characterized by UV-Vis-DRS, ATR-FT-IR, PL, XRD, Raman, SEM with EDX and TEM analysis. The synthesized NPs were investigation for dye sensitized solar cell applications. UV-Vis-Diffused Reflectance Spectra clearly showed that the expected TiO2 inter band absorption below 306 nm, incorporation of gold shows surface plasma resonant (SPR) near 555 nm and platinum incorporated TiO2 NPs shows absorbance at 460 nm. The energy conversion efficiency for Au doped TiO2 NPs when compared to pure and Pt doped TiO2 NPs. In addition to that, Au noble metal present TiO2 matrix and an improve open-circuit voltage (Voc) of DSSC. Synthesized NPs was evaluated into antibacterial and antifungal activities by disk diffusion method. It is observed that NPs have not shown any activities in all tested bacterial and fungal strains. In this eco-friendly synthesis method to provide non toxic and environmental friendly nanomaterials can be used for solar energy device application.

  13. Carbamazepine degradation using a N-doped TiO_2 coated photocatalytic membrane reactor: Influence of physical parameters

    International Nuclear Information System (INIS)

    Horovitz, Inna; Avisar, Dror; Baker, Mark A.; Grilli, Rossana; Lozzi, Luca; Di Camillo, Daniela; Mamane, Hadas

    2016-01-01

    Highlights: • UV–vis N-doped TiO_2 was deposited by sol-gel onto Al_2O_3 microfiltration membranes. • Coating decreased permeability by 50 and 12% for 200- and 800-nm Al_2O_3 membranes. • Flow through membrane results in higher reaction rates compared to flow on top. • Higher vis photocatalytic activity for N-doped TiO_2 vs. non-doped TiO_2 membranes. • Mass transfer is a critical parameter for the design of immobilized PMR. - Abstract: Commercial α-Al_2O_3 photocatalytic membranes with a pore size of 200 and 800-nm were coated with N-doped TiO_2 photocatalytic film using a sol-gel technique for concurrent bottom-up filtration and photocatalytic oxidation. X-ray diffraction confirmed that the deposited N-doped TiO_2 films are in the form of anatase with 78–84% coverage of the membrane surface. The concentration of N found by X-ray photoelectron spectroscopy was in the range of 0.3–0.9 atomic percentage. Membrane permeability after coating decreased by 50% and 12% for the 200- and 800-nm membrane substrates, respectively. The impact of operational parameters on the photocatalytic activity (PCA) of the N-doped TiO_2-coated membranes was examined in a laboratory flow cell based on degradation of the model micropollutant carbamazepine, using a solar simulator as the light source. The significant gap in degradation rate between flow through the membrane and flow on the surface of the membrane was attributed both to the hydraulic effect and in-pore PCA. N-doped TiO_2-coated membranes showed enhanced activity for UV wavelengths, in addition to activity under visible light. Experiments of PCA under varying flow rates concluded that the process is in the mass-transfer control regime. Carbamazepine removal rate increased with temperature, despite the decrease in dissolved oxygen concentration.

  14. Nb-doped rutile TiO₂: a potential anode material for Na-ion battery.

    Science.gov (United States)

    Usui, Hiroyuki; Yoshioka, Sho; Wasada, Kuniaki; Shimizu, Masahiro; Sakaguchi, Hiroki

    2015-04-01

    The electrochemical properties of the rutile-type TiO2 and Nb-doped TiO2 were investigated for the first time as Na-ion battery anodes. Ti(1-x)Nb(x)O2 thick-film electrodes without a binder and a conductive additive were prepared using a sol-gel method followed by a gas-deposition method. The TiO2 electrode showed reversible reactions of Na insertion/extraction accompanied by expansion/contraction of the TiO2 lattice. Among the Ti(1-x)Nb(x)O2 electrodes with x = 0-0.18, the Ti(0.94)Nb(0.06)O2 electrode exhibited the best cycling performance, with a reversible capacity of 160 mA h g(-1) at the 50th cycle. As the Li-ion battery anode, this electrode also attained an excellent rate capability, with a capacity of 120 mA h g(-1) even at the high current density of 16.75 A g(-1) (50C). The improvements in the performances are attributed to a 3 orders of magnitude higher electronic conductivity of Ti(0.94)Nb(0.06)O2 compared to that of TiO2. This offers the possibility of Nb-doped rutile TiO2 as a Na-ion battery anode as well as a Li-ion battery anode.

  15. Photocatalytic activity of Sulfer-doped TiO2 fiber under visible light illumination (Joint research)

    International Nuclear Information System (INIS)

    Takeyama, Akinori; Yamamoto, Shunya; Yoshikawa, Masahito; Hasegawa, Yoshio; Awatsu, Satoshi

    2007-03-01

    The Sol-Gel derived precursor fiber was annealed under hydrogen disulfeid (H 2 S) following oxygen atmosphere, Sulfur-doped TiO 2 fiber was obtained. Crystal structure of the fiber was identified as anatase phase of TiO 2 . The energy band gap of the fiber was narrower by about 0.06 eV than that of anatase, which showed that it could absorb visible light. The fiber contains about 0.58 atomic % of Sulfur, and they located at the oxygen lattice site of TiO 2 . Under visible light illumination, the fiber degraded Trichloroethylen (TCE) and produced carbon dioxide (CO 2 ). This shows Sulfur-doped TiO 2 fiber has the photocatalytic activity under visible light illumination. (author)

  16. A facile method to synthesize nitrogen and fluorine co-doped TiO2 nanoparticles by pyrolysis of (NH4)2TiF6

    International Nuclear Information System (INIS)

    Chen Daimei; Jiang Zhongyi; Geng Jiaqing; Zhu Juhong; Yang Dong

    2009-01-01

    The nitrogen and fluorine co-doped TiO 2 (N-F-TiO 2 ) nanoparticles of anatase crystalline structure were prepared by a facile method of (NH 4 ) 2 TiF 6 pyrolysis, and characterized by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and ultraviolet visible (UV-Vis) spectroscopy etc. With the increase of calcination temperature, (NH 4 ) 2 TiF 6 decomposed into TiOF 2 and NH 4 TiOF 3 at first, and then formed anatase-type TiO 2 with thin sheet morphology. H 3 BO 3 as oxygen source can promote the formation of anatase TiO 2 , but decrease the F content in the N-F-TiO 2 materials due to the formation of volatile BF 3 during the precursor decomposition. The photocatalytic activity of the obtained N-F-TiO 2 samples was evaluated by the methylene blue degradation under visible light, and all the samples exhibited much higher photocatalytic activity than P25. Moreover, the merits and disadvantages of this proposed method to prepare doped TiO 2 are discussed.

  17. Ultrasound assisted synthesis of iron doped TiO2 catalyst.

    Science.gov (United States)

    Ambati, Rohini; Gogate, Parag R

    2018-01-01

    The present work deals with synthesis of Fe (III) doped TiO 2 catalyst using the ultrasound assisted approach and conventional sol-gel approach with an objective of establishing the process intensification benefits. Effect of operating parameters such as Fe doping, type of solvent, solvent to precursor ratio and initial temperature has been investigated to get the best catalyst with minimum particle size. Comparison of the catalysts obtained using the conventional and ultrasound assisted approach under the optimized conditions has been performed using the characterization techniques like DLS, XRD, BET, SEM, EDS, TEM, FTIR and UV-Vis band gap analysis. It was established that catalyst synthesized by ultrasound assisted approach under optimized conditions of 0.4mol% doping, irradiation time of 60min, propan-2-ol as the solvent with the solvent to precursor ratio as 10 and initial temperature of 30°C was the best one with minimum particle size as 99nm and surface area as 49.41m 2 /g. SEM analysis, XRD analysis as well as the TEM analysis also confirmed the superiority of the catalyst obtained using ultrasound assisted approach as compared to the conventional approach. EDS analysis also confirmed the presence of 4.05mol% of Fe element in the sample of 0.4mol% iron doped TiO 2 . UV-Vis band gap results showed the reduction in band gap from 3.2eV to 2.9eV. Photocatalytic experiments performed to check the activity also confirmed that ultrasonically synthesized Fe doped TiO 2 catalyst resulted in a higher degradation of Acid Blue 80 as 38% while the conventionally synthesized catalyst resulted in a degradation of 31.1%. Overall, the work has clearly established importance of ultrasound in giving better catalyst characteristics as well as activity for degradation of the Acid Blue 80 dye. Copyright © 2017 Elsevier B.V. All rights reserved.

  18. Optical, structural and photocatalysis properties of Cu-doped TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bensouici, F., E-mail: fbensouici@yahoo.fr [Department of Physics, URMPE Unite, UMBB University, 35000 Boumerdes (Algeria); Bououdina, M.; Dakhel, A.A. [Department of Physics, College of Science, University of Bahrain, PO Box 32038 (Bahrain); Tala-Ighil, R.; Tounane, M.; Iratni, A. [Department of Physics, URMPE Unite, UMBB University, 35000 Boumerdes (Algeria); Souier, T. [Department of Physics, College of Science, Sultan Qaboos University, PO Box 36 (Oman); Liu, S.; Cai, W. [Key laboratory of Materials Physics, Anhui Key Laboratory of Nanomaterials and Technology, Center for Environmental and Energy Nanomaterials, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei 230031 (China)

    2017-02-15

    Highlights: • A simple chemical route to obtain thin layers of Cu doped TiO{sub 2}. • Detailed structure analysis was carried out by Rietveld refinements. • Forming the CuO phase decreases the efficiency photocatalysis of TiO{sub 2}. - Abstract: Pure and Cu{sup +2} doped TiO{sub 2} thin films have been successfully deposited onto glass substrate by sol–gel dip-coating. The films were annealed at 450 °C for 1 h and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM-EDX), atomic force microscopy (AFM), UV–vis spectrophotometer and photocatalytic degradation of methylene blue. XRD confirmed the presence of two phases at higher Cu concentration; TiO{sub 2} anatase and CuO. AFM analysis showed that the surface roughness increases within increasing Cu content as well as the presence of large aggregates at higher Cu content. SEM observations confirmed the granular structure of the films, and EDX analysis revealed a low solubility limit (effective doping) of Cu into TiO{sub 2} lattice. It was found that the optical band gap energy decreases with increasing Cu content. At constant irradiation time, the photo-degradation of methylene blue rate decreased with increasing concentration of Cu{sup +2}.

  19. Modeling and calculation of RKKY exchange coupling to explain Ti-vacancy-induced ferromagnetism in Ta-doped TiO2

    Science.gov (United States)

    Majidi, Muhammad Aziz; Bupu, Annamaria; Fauzi, Angga Dito

    2017-12-01

    We present a theoretical study on Ti-vacancy-induced ferromagnetism in anatase TiO2. A recent experimental study has revealed room temperature ferromagnetism in Ta-doped anatase TiO2thin films (Rusydi et al., 2012) [7]. Ta doping assists the formation of Ti vacancies which then induce the formation of localized magnetic moments around the Ti vacancies. As neighboring Ti vacancies are a few unit cells apart, the ferromagnetic order is suspected to be mediated by itinerant electrons. We propose that such an electron-mediated ferromagnetism is driven by Ruderman-Kittel-Kasuya-Yosida (RKKY) exchange interaction. To examine our hypothesis, we construct a tight-binding based model Hamiltonian for the anatase TiO2 system. We calculate the RKKY exchange coupling constant of TiO2 as a function of distance between local magnetic moments at various temperatures. We model the system by taking only the layer containing a unit of TiO2, at which the Ti vacancy is believed to form, as our effective two-dimensional unit cell. Our model incorporates the Hubbard repulsive interactions between electrons occupying Ti d orbitals treated within mean-field approximation. The density of states profile resulting from the model captures the relevant electronic properties of TiO2, such as the energy gap of 3.4 eV and the n-type character, which may be a measure of the adequacy of the model. The calculated RKKY coupling constant shows that the ferromagnetic coupling extends up to 3-4 unit cells and enhances slightly as temperature is increased from 0 to 400 K. These results support our hypothesis that the ferromagnetism of this system is driven by RKKY mechanism.

  20. Thermoelectric performance enhancement of SrTiO3 by Pr doping

    KAUST Repository

    Kahaly, M. Upadhyay; Schwingenschlö gl, Udo

    2014-01-01

    We investigate Pr doping at the Sr site as a possible route to enhance the thermoelectric behavior of SrTiO3-based materials, using first principles calculations in full-potential density functional theory. The effects of the Pr dopant on the local electronic structure and resulting transport properties are compared to common Nb doping. We demonstrate a substantial enhancement of the thermoelectric figure of merit and develop an explanation for the positive effects, which opens new ways for materials optimization by substitutional doping at the perovskite B site. © 2014 the Partner Organisations.

  1. Synthesis and characterization of Fe-doped TiO2 photocatalyst by the sol–gel method

    International Nuclear Information System (INIS)

    Luu, Cam Loc; Ho, Si Thoang; Nguyen, Quoc Tuan

    2010-01-01

    Thin layers of pure TiO 2 and TiO 2 doped by different amounts of Fe 2 O 3 have been prepared by the sol–gel method with tetraisopropyl orthotitanate and Fe(NO 3 ) 3 . Physico-chemical properties of catalysts were characterized by BET Adsorption, x-ray Diffraction (XRD), FE-SEM, as well as Raman and UV-Vis spectroscopy. The photocatalytic activity of the obtained materials was investigated in the reaction of complete oxidation of p-xylene in gas phase under the radiation of UV (λ=365 nm) and LED (λ=470 nm) lamps. It has been found that the particle size of all samples was distributed in the range 20–30 nm. The content of the rutile phase in Fe-doped TiO 2 samples varied in the range 6.8 to 41.8% depending on the Fe content. Iron oxide doped into TiO 2 enables the photon absorbing zone of TiO 2 to extend from UV towards visible waves as well as to reduce its band gap energy from 3.2 to 2.67 eV. Photocatalytic activities of the TiO 2 samples modified by Fe 3+ have been found to be higher than those of pure TiO 2 by about 2.5 times

  2. Optical and electrical properties of TiOPc doped Alq{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ramar, M.; Suman, C. K., E-mail: sumanck@nplindia.org; Tyagi, Priyanka; Srivastava, R. [CSIR-Network of Institutes for Solar Energy CSIR - National Physical Laboratory, Dr. K. S. Krishnan Marg, New Delhi -110012 (India)

    2015-06-24

    The Titanyl phthalocyanine (TiOPc) was doped in Tris (8-hydroxyquinolinato) aluminum (Alq3) with different concentration. The thin film of optimized doping concentration was studied extensively for optical and electrical properties. The optical properties, studied using ellipsometry, absorption and photoluminescence. The absorption peak of Alq{sub 3} and TiOPc was observed at 387 nm and 707 nm and the photo-luminescence intensity (PL) peak of doped thin film was observed at 517 nm. The DC and AC electrical properties of the thin film were studied by current density-voltage (J-V) characteristics and impedance over a frequency range of 100 Hz - 1 MHz. The electron mobility calculated from trap-free space-charge limited region (SCLC) is 0.17×10{sup −5} cm{sup 2}/Vs. The Cole-Cole plots shows that the TiOPc doped Alq{sub 3} thin film can be represented by a single parallel resistance R{sub P} and capacitance C{sub P} network with a series resistance R{sub S} (10 Ω). The value of R{sub P} and C{sub P} at zero bias was 1587 Ω and 2.568 nF respectively. The resistance R{sub P} decreases with applied bias whereas the capacitance C{sub P} remains almost constant.

  3. Double-doped TiO{sub 2} nanoparticles as an efficient visible-light-active photocatalyst and antibacterial agent under solar simulated light

    Energy Technology Data Exchange (ETDEWEB)

    Ashkarran, Ali Akbar, E-mail: ashkarran@umz.ac.ir [Department of Physics, Faculty of Basic Sciences, University of Mazandaran, Babolsar (Iran, Islamic Republic of); Hamidinezhad, Habib [Nano and Biotechnology Research Group, Faculty of Basic Sciences, University of Mazandaran, Babolsar (Iran, Islamic Republic of); Haddadi, Hedayat [Department of Chemistry, Faculty of Sciences, Shahrekord University, P.O. Box 115, Shahrekord (Iran, Islamic Republic of); Mahmoudi, Morteza [Department of Nanotechnology, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Nanotechnology Research Center, Faculty of Pharmacy, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of)

    2014-05-01

    Graphical abstract: Double doping introduces two different electronic states in the band gap of TiO{sub 2}, which increase the lifetime of the charge carriers and leads to narrower band gap and enhancement of the visible-light absorption. - Highlights: • Preparation of single and double doped TiO{sub 2} NPs using a simple sol–gel route. • Extension of light absorption spectrum toward the visible region. • Enhanced visible-light photo-induced activity and antibacterial property in double doped TiO{sub 2} NPs. - Abstract: Silver and nitrogen doped TiO{sub 2} nanoparticles (NPs) were synthesized via sol–gel method. The physicochemical properties of the achieved NPs were characterized by various methods including X-Ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and ultra violet–visible absorption spectroscopy (UV–vis). Both visible-light photocatalytic activity and antimicrobial properties were successfully demonstrated for the degradation of Rhodamine B (Rh. B.), as a model dye, and inactivation of Escherichia coli (E. coli), as a representative of microorganisms. The concentration of the employed dopant was optimized and the results revealed that the silver and nitrogen doped TiO{sub 2} NPs extended the light absorption spectrum toward the visible region and significantly enhanced the photodegradation of model dye and inactivation of bacteria under visible-light irradiation while double-doped TiO{sub 2} NPs exhibited highest photocatalytic and antibacterial activity compared with single doping. The significant enhancement in the photocatalytic activity and antibacterial properties of the double doped TiO{sub 2} NPs, under visible-light irradiation, can be attributed to the generation of two different electronic states acting as electron traps in TiO{sub 2} and responsible for narrowing the band gap of TiO{sub 2} and shifting its optical response from UV to the

  4. Visible light-responded C, N and S co-doped anatase TiO{sub 2} for photocatalytic reduction of Cr(VI)

    Energy Technology Data Exchange (ETDEWEB)

    Lei, X.F., E-mail: leixuefei69@163.com [School of Resources and Materials, Northeastern University at Qinhuangdao, Qinhuangdao 066004 (China); Institute of Metallurgical Resource and Environmental Engineering, Northeastern University, Shenyang 110819 (China); Liaoning Key Laboratory of Metallurgical Resource Recycling Science, Shenyang 110819 (China); Liaoning Engineering and Technology Research Center of Boron Resource, Comprehensive, Utilization, Shenyang 110819 (China); Liaoning Provincial Universities Key Laboratory of Boron Resource Ecological, Utilization, Technology and Boron Materials, Shenyang 110819 (China); Xue, X.X.; Yang, H. [Institute of Metallurgical Resource and Environmental Engineering, Northeastern University, Shenyang 110819 (China); Liaoning Key Laboratory of Metallurgical Resource Recycling Science, Shenyang 110819 (China); Liaoning Engineering and Technology Research Center of Boron Resource, Comprehensive, Utilization, Shenyang 110819 (China); Liaoning Provincial Universities Key Laboratory of Boron Resource Ecological, Utilization, Technology and Boron Materials, Shenyang 110819 (China); Chen, C.; Li, X.; Pei, J.X.; Niu, M.C.; Yang, Y.T.; Gao, X.Y. [School of Resources and Materials, Northeastern University at Qinhuangdao, Qinhuangdao 066004 (China)

    2015-10-15

    The (C, N and S) co-doped TiO{sub 2} (TH-TiO{sub 2}) samples were synthesized by a sol-gel method calcined at 500 °C, employing butyl titanate as the titanium source and thiourea as the dopant. The structures of TH-TiO{sub 2} samples were characterized by X-ray diffraction (XRD), Transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), UV–vis diffuse reflectance spectra (DRS), photoluminescence (PL) spectroscopy, Thermo gravimetry and differential thermal analysis (TG-DTA), Scanning electron microscopy (SEM) and nitrogen adsorption–desorption isotherms. The photocatalytic activities were checked through the photocatalytic reduction of Cr(VI) as a model compound under visible light irradiation. The results showed that the thiourea content played an important role on the microstructure and photocatalytic activity of the samples. According to XPS results, (C, N and S) atoms were successfully co-doped into the nanostructures of TH-TiO{sub 2} samples. TH-TiO{sub 2} samples with thiourea: Ti molar ratio of 1.5 exhibits higher photocatalytic activity than that of the other samples under visible light irradiation, which can be attributed to the synergic effect of the pure anatase structure, the higher light absorption characteristics in visible regions, separation efficiency of electron–hole pairs, the specific surface area and the optimum (C, N and S) content. - Graphical abstract: (C, N and S) co-doped TiO{sub 2} samples show good photocatalytic activity for Cr (VI) reduction under visible light irradiation. - Highlights: • (C, N and S) co-doping in TH-TiO{sub 2} samples can promote the formation of the pure anatase structure. • (C, N and S) atoms were successfully co-doped into the nanostructures of TH-TiO{sub 2} samples. • The band gap energy of TH-TiO{sub 2} samples reduced after (C, N and S) co-doping. • (C, N and S) co-doped TiO{sub 2} samples were effective for the photocatalytic reduction of Cr(VI) under visible light

  5. The Synergistic Effect of Nitrogen Dopant and Calcination Temperature on the Visible-Light-Induced Photoactivity of N-Doped TiO2

    Directory of Open Access Journals (Sweden)

    Yao-Tung Lin

    2013-01-01

    Full Text Available The synergistic effect of nitrogen content and calcinations temperature on the N-doped TiO2 catalysts prepared by sol-gel method was investigated. The phase and structure, chemical state, optical properties, and surface area/pore distribution of N-doped TiO2 were characterized using X-ray diffraction spectrometer, high-resolution transmission electron microscope, X-ray photoelectron spectroscopy, UV-vis diffusion reflectance spectroscopy, and Brunauer-Emmett-Teller specific surface area. Finding showed that the photocatalytic activity of N-doped TiO2 was greatly enhanced compared to pure TiO2 under visible irradiation. N dopants could retard the transformation from anatase to rutile phase. Namely, N-doping effect is attributed to the anatase phase stabilization. The results showed nitrogen atoms were incorporated into the interstitial positions of the TiO2 lattice. Ethylene was used to evaluate the photocatalytic activity of samples under visible-light illumination. The results suggested good anatase crystallization, smaller particle size, and larger surface are beneficial for photocatalytic activity of N-doped TiO2. The N-doped TiO2 catalyst prepared with ammonia to titanium isopropoxide molar ratio of 2.0 and calcinated at 400°C showed the best photocatalytic ability.

  6. Influence of substrate temperature and silver-doping on the structural and optical properties of TiO_2 films

    International Nuclear Information System (INIS)

    Fischer, Dieter

    2016-01-01

    Evaporation of titanium together with activated oxygen is used to grow TiO_2 films and simultaneously with silver to grow Ag–TiO_2 films (5 at.% Ag) onto sapphire substrates at three different substrate temperatures: − 190, 30, and 200 °C. The obtained films were characterized by X-ray powder diffraction, Raman, X-ray photoelectron, ultraviolet–visible spectroscopy, and transmission electron microscope investigations. The properties of TiO_2 films varied with the substrate temperature. Amorphous, transparent TiO_2 films were grown at − 190 °C and opaque, polycrystalline films at 200 °C, respectively. Surprisingly, at room temperature black, amorphous TiO_2 films are obtained which transform at 350 °C into a mixture of the anatase and brookite polymorph. In the amorphous state of the TiO_2 films a predefined rutile arrangement is suggested by Raman investigations, and the contraction of the lattice constant c of anatase phases (tetragonal, space group I 4_1/amd) depending on the substrate temperature is experimentally observed. The silver-doped TiO_2 films deposited at − 190 and 30 °C contain Ag-particles with 2 nm in size inside the TiO_2 matrix, which after annealing segregate under increasing particle sizes. The silver-doping stabilizes the anatase polymorph and yields to reduced titanium species in the films especially during deposition at 30 °C. The Ag–TiO_2 films deposited at − 190 °C are transparent up to 350 °C. In the undoped as well as silver-doped TiO_2 films the rutile polymorph is directly formed at 200 °C as main phase. - Highlights: • At room temperature black, amorphous TiO_2 films are obtained. • A predefined rutile arrangement is suggested in amorphous TiO_2 films. • Annealed TiO_2 films crystallize to a mixture of the anatase and brookite polymorph. • In TiO_2 and Ag-doped TiO_2 films the rutile polymorph is directly formed at 200 °C. • Ag-doped TiO_2 films stabilize the anatase polymorph and reduced titanium

  7. AlTiN layer effect on mechanical properties of Ti-doped diamond-like carbon composite coatings

    International Nuclear Information System (INIS)

    Pang Xiaolu; Yang Huisheng; Gao Kewei; Wang Yanbin; Volinsky, Alex A.

    2011-01-01

    Ti/Ti-doped diamond-like carbon (DLC) and Ti/AlTiN/Ti-DLC composite coatings were deposited by magnetron sputtering on W18Cr4V high speed steel substrates. The effect of the AlTiN support layer on the properties of these composite coatings was investigated through microstructure and mechanical properties characterization, including hardness, elastic modulus, coefficient of friction and wear properties measured by scanning electron microscopy, Raman spectroscopy, scratch and ball-on-disk friction tests. Ti and AlTiN interlayers have a columnar structure with 50-80 nm grains. The hardness and elastic modulus of Ti/Ti-DLC and Ti/AlTiN/Ti-DLC coatings is 25.9 ± 0.4, 222.2 ± 6.3 GPa and 19.3 ± 1, 205.6 ± 6.7 GPa, respectively. Adhesion of Ti-DLC, Ti/AlTiN/Ti-DLC and AlTiN/Ti-DLC coatings expressed as the critical lateral force is 26.5 N, 38.2 N, and 47.8 N, respectively. Substrate coefficient of friction without coatings is 0.44, and it is 0.1 for Ti/Ti-DLC and Ti/AlTiN/Ti-DLC coatings. Wear resistance of Ti/AlTiN/Ti-DLC composite coatings is much higher than Ti/Ti-DLC coatings based on the wear track width of 169.8 and 73.2 μm, respectively, for the same experimental conditions.

  8. Visible-Light-Active Titania Photocatalysts: The Case of N-Doped TiO2s—Properties and Some Fundamental Issues

    Directory of Open Access Journals (Sweden)

    Alexei V. Emeline

    2008-01-01

    Full Text Available This article briefly reviews some factors that have impacted heterogeneous photocatalysis with next generation TiO2 photocatalysts, along with some issues of current debate in the fundamental understanding of the science that underpins the field. Preparative methods and some characteristics features of N-doped TiO2 are presented and described briefly. At variance are experimental results and interpretations of X-ray photoelectron spectra (XPS with regard to assignments of N 1s binding energies in N-doped TiO2 systems. Relative to pristine nominally clean TiO2 with absorption edges at 3.2 eV (anatase and 3.0 eV (rutile, N-doped TiO2s display red-shifted absorption edges into the visible spectral region. Several workers have surmised that the (intrinsic band gap of TiO2 is narrowed by coupling dopant energy states with valence band (VB states, an inference based on DFT computations. With similar DFT computations, others concluded that red-shifted absorption edges originate from the presence of localized intragap dopant states above the upper level of the VB band. Recent analyses of absorption spectral features in the visible region for a large number of doped TiO2 specimens, however, have suggested a common origin owing to the strong similarities of the absorption features, and this regardless of the preparative methods and the nature of the dopants. The next generation of (doped TiO2 photocatalysts should enhance overall process photoefficiencies (in some cases, since doped TiO2s absorb a greater quantity of solar radiation. The fundamental science that underpins heterogeneous photocatalysis with the next generation of photocatalysts is a rich playing field ripe for further exploration.

  9. Highly efficient electrochemical degradation of perfluorooctanoic acid (PFOA) by F-doped Ti/SnO{sub 2} electrode

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Bo, E-mail: boyang@szu.edu.cn [Department of Environmental Engineering, College of Chemistry and Chemical Engineering, Shenzhen University, Shenzhen 518060 (China); School of Environment, POPs Research Center, Tsinghua University, Beijing 100084 (China); Jiang, Chaojin [Department of Environmental Engineering, College of Chemistry and Chemical Engineering, Shenzhen University, Shenzhen 518060 (China); Yu, Gang, E-mail: yg-den@tsinghua.edu.cn [School of Environment, POPs Research Center, Tsinghua University, Beijing 100084 (China); Zhuo, Qiongfang [South China Institute of Environmental Sciences, The Ministry of Environment Protection, Guangzhou 510655 (China); Deng, Shubo [School of Environment, POPs Research Center, Tsinghua University, Beijing 100084 (China); Wu, Jinhua [School of Environment and Energy, South China University of Technology, Guangzhou 510006 (China); Zhang, Hong [Department of Environmental Engineering, College of Chemistry and Chemical Engineering, Shenzhen University, Shenzhen 518060 (China)

    2015-12-15

    Highlights: • A novel SnO{sub 2} electrode is prepared by F doping instead of the traditional Sb doping. • SnF{sub 4} as single-source precursor is used to fabricate the long-life Ti/SnO{sub 2}–F anode. • F-doped Ti/SnO{sub 2} anode possesses high OEP and decomposition ability for PFOA. • Further mechanistic detail of PFOA degradation on Ti/SnO{sub 2}–F electrode is proposed. - Abstract: The novel F-doped Ti/SnO{sub 2} electrode prepared by SnF{sub 4} as the single-source precursor was used for electrochemical degradation of aqueous perfluorooctanoic acid (PFOA). Higher oxidation reactivity and significantly longer service life were achieved for Ti/SnO{sub 2}–F electrode than Ti/SnO{sub 2}–X (X = Cl, Br, I, or Sb) electrode, which could decomposed over 99% of PFOA (50 mL of 100 mg L{sup −1}) within 30-min electrolysis. The property of Ti/SnO{sub 2}–F electrode and its electrooxidation mechanism were investigated by XRD, SEM–EDX, EIS, LSV, and interfacial resistance measurements. We propose that the similar ionic radii of F and O as well as strong electronegativity of F caused its electrochemical stability with high oxygen evolution potential (OEP) and smooth surface to generate weakly adsorbed ·OH. The preparation conditions of electrode were also optimized including F doping amount, calcination temperature, and dip coating times, which revealed the formation process of electrode. Additionally, the major mineralization product, F{sup −}, and low concentration of shorter chain perfluorocarboxylic acids (PFCAs) were detected in solution. So the reaction pathway of PFOA electrooxidation was proposed by intermediate analysis. These results demonstrate that Ti/SnO{sub 2}–F electrode is promising for highly efficient treatment of PFOA in wastewater.

  10. Amorphous TiO2 doped with carbon for visible light photodegradation of rhodamine B and 4-chlorophenol

    International Nuclear Information System (INIS)

    Shao, Penghui; Tian, Jiayu; Zhao, Zhiwei; Shi, Wenxin; Gao, Shanshan; Cui, Fuyi

    2015-01-01

    Graphical abstract: - Highlights: • Amorphous TiO 2 doped with carbon is prepared as a visible photocatalyst. • RhB and 4-chlorophenol are decomposed effectively by carbon-doped amorphous TiO 2 . • The mechanism for visible light photocatalysis is discussed detailedly. - Abstract: Visible light photocatalytic activity of amorphous TiO 2 doped with carbon is prepared by a facile sol-gel route for the first time. The most active sample with mesostructure of amorphous phase, high surface area (273 m 2 g −1 ) and large pore volume (0.33 cm 3 g −1 ) is identified by X-ray diffractometer, Raman spectrometer, transmission electron microscope and N 2 adsorption–desorption isotherms. In addition, the most active sample is characterized by Fourier transform-infrared spectrometer, X-ray photoelectron spectrometer, UV–vis diffuse reflectance spectrometer and luminescence spectrometer. The results show that the most active sample with oxygenic groups has a narrower bandgap and lower recombination of electron–hole, due to the carbon doping and phase of amorphous. Effective photodegradation capability and stability of rhodamine B and colorless 4-chlorophenol are verified by photocatalytic tests under visible light irradiation. A possible mechanism of amorphous TiO 2 doped with carbon for visible light photocatalysis is proposed. The findings of this paper will provide new insights to design visible light-induced photocatalyst based on amorphous TiO 2 for organic removal

  11. Zr doping effect with low-cost solid-state reaction method to synthesize submicron Li4Ti5O12 anode material

    Science.gov (United States)

    Seo, Inseok; Lee, Cheul-Ro; Kim, Jae-Kwang

    2017-09-01

    To improve the electrochemical properties, fine Zr-doping Li4Ti5O12 anode materials for rechargeable lithium batteries with a uniform particle size distribution were synthesized by a modified solid-state reaction using fine Li2CO3 and TiO2 (anatase) powders as precursors with a Li:Ti molar ratio of 4:5. The use of fine Li2CO3 and TiO2 (anatase) powders as precursors prevented the formation of ZrO2 at 0.1 mol Zr-doping. XRD analysis revealed that the substitution of Zr for Ti leads to the increase of lattice parameters, allowing improved Li diffusion. The discharge capacity retention increased slightly with Zr-doping and the 0.1 mol Zr-doped Li4Ti5O12 electrode achieved 99% retention of discharge capacity.

  12. Compositionally modulated multilayer diamond-like carbon coatings with AlTiSi multi-doping by reactive high power impulse magnetron sputtering

    Science.gov (United States)

    Dai, Wei; Gao, Xiang; Liu, Jingmao; Kwon, Se-Hun; Wang, Qimin

    2017-12-01

    Diamond-like carbon (DLC) coatings with AlTiSi multi-doping were prepared by a reactive high power impulse magnetron sputtering with using a gas mixture of Ar and C2H2 as precursor. The composition, microstructure, compressive stress, and mechanical property of the as-deposited DLC coatings were studied systemically by using SEM, XPS, TEM, Raman spectrum, stress-tester, and nanoindentation as a function of the Ar fraction. The results show that the doping concentrations of the Al, Ti and Si atoms increased as the Ar fraction increased. The doped Ti and Si preferred to bond with C while the doped Al mainly existed in oxidation state without bonding with C. As the doping concentrations increased, TiC carbide nanocrystals were formed in the DLC matrix. The microstructure of coatings changed from an amorphous feature dominant AlTiSi-DLC to a carbide nanocomposite AlTiSi-DLC with TiC nanoparticles embedding. In addition, the coatings exhibited the compositionally modulated multilayer consisting of alternate Al-rich layer and Al-poor layer due to the rotation of the substrate holder and the diffusion behavior of the doped Al which tended to separate from C and diffuse towards the DLC matrix surface owing to its weak interactions with C. The periodic Al-rich layer can effectively release the compressive stress of the coatings. On the other hand, the hard TiC nanoparticles were conducive to the hardness of the coatings. Consequently, the DLC coatings with relatively low residual stress and high hardness could be acquired successfully through AlTiSi multi-doping. It is believed that the AlCrSi multi-doping may be a good way for improving the comprehensive properties of the DLC coatings. In addition, we believe that the DLC coatings with Al-rich multilayered structure have a high oxidation resistance, which allows the DLC coatings application in high temperature environment.

  13. Deposition barium titanate (BaTiO3) doped lanthanum with chemical solution deposition

    International Nuclear Information System (INIS)

    Iriani, Y.; Nurhadi, N.; Jamaludin, A.

    2016-01-01

    Deposition of Barium Titanate (BaTiO 3 ) thin films used Chemical Solution Deposition (CSD) method and prepared with spin coater. BaTiO 3 is doped with lanthanum, 1%, 2%, and 3%. The thermal process use annealing temperature 900°C and holding time for 3 hours. The result of characterization with x-ray diffraction (XRD) equipment show that the addition of La 3+ doped on Barium Titanate caused the change of angle diffraction.The result of refine with GSAS software shows that lanthanum have been included in the structure of BaTiO 3 . Increasing mol dopant La 3+ cause lattice parameter and crystal volume become smaller. Characterization result using Scanning Electron Microscopy (SEM) equipment show that grain size (grain size) become smaller with increasing mole dopant (x) La 3+ . The result of characterization using Sawyer Tower methods show that all the samples (Barium Titanante and Barium Titanate doped lanthanum) are ferroelectric material. Increasing of mole dopant La 3+ cause smaller coercive field and remanent polarization increases. (paper)

  14. Structural Characterization and Magnetic Properties of Undoped and Ti-Doped ZnO Nanoparticles Prepared by Modified Oxalate Route

    Directory of Open Access Journals (Sweden)

    Ekane Peter Etape

    2018-01-01

    Full Text Available Ti-doped zinc oxide and pure zinc oxide nanoparticles were synthesized by a modified oxalate route using Averrhoa carambola fruit juice as a natural source of oxalate. The characteristics of the precursors have been investigated by FTIR, TGA, and XRD. The results from the investigation revealed that the precursors are zinc oxalate and Ti-doped zinc oxalate which readily decompose at 450°C. The as-prepared precursors were calcined at 450°C for 4 hours, and the decomposition products have been characterized by XRD, SEM, EDX, and VSM. XRD results revealed crystallinity with hexagonal wurtzite structure, while the average grain size was found to be 26 nm for Ti-doped ZnO and 29 nm for ZnO, using calculations based on Debye-Scherrer equation. Furthermore, the morphological studies by SEM showed particle agglomeration, while the presence of Ti3+ in the zinc oxide lattice is indicated by EDS analysis. Finally the hysteresis loop from VSM results shows that Ti-doped ZnO exhibits ferromagnetism.

  15. Optical and structural properties of Mo-doped NiTiO{sub 3} materials synthesized via modified Pechini methods

    Energy Technology Data Exchange (ETDEWEB)

    Pham, Thanh-Truc; Kang, Sung Gu; Shin, Eun Woo, E-mail: ewshin@ulsan.ac.kr

    2017-07-31

    Highlights: • Mo-doped NiTiO{sub 3} materials were well prepared by a modified Pechini method. • Recombination rates of the materials were significantly inhibited by Mo doping. • Defect sites were generated by the substitution of Mo for Ni or Ti positions. • The generation of defect sites gradually decreased the grain sizes of the materials. • The surface areas of the materials were increased with decreasing the grain sizes. - Abstract: In this study, molybdenum (Mo)-doped nickel titanate (NiTiO{sub 3}) materials were successfully synthesized as a function of Mo content through a modified Pechini method followed by a solvothermal treatment process. Various characterization methods were employed to investigate the optical and structural properties of the materials. XRD patterns clearly showed that the NiTiO{sub 3} structure maintained a single phase with no observed crystalline structure transformations, even after the addition of 10 wt.% Mo. In the Raman spectra and XRD patterns, peak positions shifted with a change in Mo content, confirming that the NiTiO{sub 3} lattice was doped with Mo. On the other hand, Mo doping of NiTiO{sub 3} materials changed their optical properties. DRS-UV demonstrated that the addition of Mo increased photon absorption within the UV region. Relaxation processes were inhibited by Mo doping, which was evident in the PL spectra. Structural properties of the prepared materials were studied via FE-SEM and HR-TEM. The measured surface area increased proportionally with Mo content due to a reduction in grain size of the materials.

  16. Microstructure evolution and electrical characterization of Lanthanum doped Barium Titanate (BaTiO_3) ceramics

    International Nuclear Information System (INIS)

    Billah, Masum; Ahmed, A.; Rahman, Md. Miftaur; Mahbub, Rubbayat; Gafur, M. A.; Bashar, M. Shahriar

    2016-01-01

    In the current work, we investigated the structural and dielectric properties of Lanthanum oxide (La_2O_3) doped Barium Titanate (BaTiO_3) ceramics and established a correlation between them. Solid state sintering method was used to dope BaTiO_3 with 0.3, 0.5 and 0.7 mole% La_2O_3 under different sintering parameters. The raw materials used were La_2O_3 nano powder of ~80 nm grain size and 99.995% purity and BaTiO_3 nano powder of 100 nm grain size and 99.99% purity. Grain size distribution and morphology of fracture surface of sintered pellets were examined by Field Emission Scanning Electron Microscope and X-Ray Diffraction analysis was conducted to confirm the formation of desired crystal structure. The research result reveal that grain size and electrical properties of BaTiO_3 ceramic significantly enhanced for small amount of doping (up to 0.5 mole% La_2O_3) and then decreased with increasing doping concentration. Desired grain growth (0.80-1.3 µm) and high densification (<90% theoretical density) were found by proper combination of temperature, sintering parameters and doping concentration. We found the resultant stable value of dielectric constant was 10000-12000 at 100-300 Hz in the temperature range of 30°-50° C for 0.5 mole% La_2O_3 with corresponding shift of curie temperature around 30° C. So overall this research showed that proper La"3"+ concentration can control the grain size, increase density, lower curie temperature and hence significantly improve the electrical properties of BaTiO_3 ceramics.

  17. Direct Observation of Surface Potential Distribution in Insulation Resistance Degraded Acceptor-Doped BaTiO3 Multilayered Ceramic Capacitors

    Science.gov (United States)

    Hong, Kootak; Lee, Tae Hyung; Suh, Jun Min; Park, Jae-Sung; Kwon, Hyung-Soon; Choi, Jaeho; Jang, Ho Won

    2018-05-01

    Insulation resistance (IR) degradation in BaTiO3 is a key issue for developing miniaturized multilayer ceramic capacitors (MLCCs) with high capacity. Despite rapid progress in BaTiO3-based MLCCs, the mechanism of IR degradation is still controversial. In this study, we demonstrate the Al doping effect on IR degradation behavior of BaTiO3 MLCCs by electrical measurements and scanning Kelvin probe microscopy (SKPM). As the Al doping concentration in BaTiO3 increases, IR degradation of MLCCs seems to be suppressed from electrical characterization results. However, SKPM results reveal that the conductive regions near the cathode become lager with Al doping after IR degradation. The formation of conducting regions is attributed to the migration of oxygen vacancies, which is the origin of IR degradation in BaTiO3, in dielectric layers. These results imply that acceptor doping in BaTiO3 solely cannot suppress the IR degradation in MLCC even though less asymmetric IR characteristics and IR degradation in MLCCs with higher Al doping concentration are observed from electrical characterization. Our results strongly suggest that observing the surface potential distribution in IR degraded dielectric layers using SKPM is an effective method to unravel the mechanism of IR degradation in MLCCs.

  18. Enhanced separation efficiency of photoinduced charges for antimony-doped tin oxide (Sb-SnO{sub 2})/TiO{sub 2} heterojunction semiconductors with varied Sb doping concentration

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Zhen-Long [School of Physics and Electronics, Henan University, Kaifeng 475004 (China); Ma, Wen-Hai [School of Physical Education, Henan University, Kaifeng 475004 (China); Mao, Yan-Li, E-mail: ylmao1@163.com [School of Physics and Electronics, Henan University, Kaifeng 475004 (China); Institute for Computational Materials Science, Henan University, Kaifeng 475004 (China)

    2014-09-07

    In this paper, antimony-doped tin oxide (Sb-SnO{sub 2}) nanoparticles were synthesized with varied Sb doping concentration, and the Sb-SnO{sub 2}/TiO{sub 2} heterojunction semiconductors were prepared with Sb-SnO{sub 2} and TiO{sub 2}. The separation efficiency of photoinduced charges was characterized with surface photovoltage (SPV) technique. Compared with Sb-SnO{sub 2} and TiO{sub 2}, Sb-SnO{sub 2}/TiO{sub 2} presents an enhanced separation efficiency of photoinduced charges, and the SPV enhancements were estimated to be 1.40, 1.43, and 1.99 for Sb-SnO{sub 2}/TiO{sub 2} composed of Sb-SnO{sub 2} with the Sb doping concentration of 5%, 10%, and 15%, respectively. To understand the enhancement, the band structure of Sb-SnO{sub 2} and TiO{sub 2} in the heterojunction semiconductor was determined, and the conduction band offsets (CBO) between Sb-SnO{sub 2} and TiO{sub 2} were estimated to be 0.56, 0.64, and 0.98 eV for Sb-SnO{sub 2}/TiO{sub 2} composed of Sb-SnO{sub 2} with the Sb doping concentration of 5%, 10%, and 15%, respectively. These results indicate that the separation efficiency enhancement is resulting from the energy level matching, and the increase of enhancement is due to the rising of CBO.

  19. Synthesis of Non-uniformly Pr-doped SrTiO3 Ceramics and Their Thermoelectric Properties

    KAUST Repository

    Mehdizadeh Dehkordi, Arash; Bhattacharya, Sriparna; Darroudi, Taghi; Zeng, Xiaoyu; Alshareef, Husam N.; Tritt, Terry M.

    2015-01-01

    We demonstrate a novel synthesis strategy for the preparation of Pr-doped SrTiO3 ceramics via a combination of solid state reaction and spark plasma sintering techniques. Polycrystalline ceramics possessing a unique morphology can be achieved by optimizing the process parameters, particularly spark plasma sintering heating rate. The phase and morphology of the synthesized ceramics were investigated in detail using X-ray diffraction, scanning electron microcopy and energy-dispersive X-ray spectroscopy It was observed that the grains of these bulk Pr-doped SrTiO3 ceramics were enhanced with Pr-rich grain boundaries. Electronic and thermal transport properties were also investigated as a function of temperature and doping concentration Such a microstructure was found to give rise to improved thermoelectric properties. Specifically, it resulted in a significant improvement in carrier mobility and the thermoelectric power factor. Simultaneously, it also led to a marked reduction in the thermal conductivity. As a result, a significant improvement (> 30%) in the thermoelectric figure of merit was achieved for the whole temperature range over all previously reported maximum values for SrTiO3-based ceramics. This synthesis demonstrates the steps for the preparation of bulk polycrystalline ceramics of non-uniformly Pr-doped SrTiO3.

  20. Synthesis of Non-uniformly Pr-doped SrTiO3 Ceramics and Their Thermoelectric Properties

    KAUST Repository

    Mehdizadeh Dehkordi, Arash

    2015-08-15

    We demonstrate a novel synthesis strategy for the preparation of Pr-doped SrTiO3 ceramics via a combination of solid state reaction and spark plasma sintering techniques. Polycrystalline ceramics possessing a unique morphology can be achieved by optimizing the process parameters, particularly spark plasma sintering heating rate. The phase and morphology of the synthesized ceramics were investigated in detail using X-ray diffraction, scanning electron microcopy and energy-dispersive X-ray spectroscopy It was observed that the grains of these bulk Pr-doped SrTiO3 ceramics were enhanced with Pr-rich grain boundaries. Electronic and thermal transport properties were also investigated as a function of temperature and doping concentration Such a microstructure was found to give rise to improved thermoelectric properties. Specifically, it resulted in a significant improvement in carrier mobility and the thermoelectric power factor. Simultaneously, it also led to a marked reduction in the thermal conductivity. As a result, a significant improvement (> 30%) in the thermoelectric figure of merit was achieved for the whole temperature range over all previously reported maximum values for SrTiO3-based ceramics. This synthesis demonstrates the steps for the preparation of bulk polycrystalline ceramics of non-uniformly Pr-doped SrTiO3.

  1. Effect of N{sub 2} flow rate on the properties of N doped TiO{sub 2} films deposited by DC coupled RF magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Shou [State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430000 (China); State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); Yang, Yong, E-mail: 88087113@163.com [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); Li, Gang; Jiang, Jiwen; Jin, Kewu; Yao, TingTing; Zhang, Kuanxiang [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); Cao, Xin [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116000 (China); Wang, Yun; Xu, Genbao [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China)

    2016-09-05

    N doped TiO{sub 2} films were deposited on glass substrates at room temperature using DC coupled RF magnetron sputtering with a TiO{sub 2} ceramic target. The influences of N{sub 2} flow rate on the deposition rate, crystal structure, chemical composition and band gap of the deposited films were investigated by Optical profiler, X-ray diffraction, X-ray photoelectron spectroscope and ultraviolet-visible spectrophotometer. The film growth rate gradually decreased with increasing N{sub 2} flow rate. As N{sub 2} flow rate increased, the crystallization of the films deteriorated, and the films tended to form amorphous structure. XPS analysis revealed that N dopant atoms were added at the substitutional sites into TiO{sub 2} lattice structure. FE-SEM results showed that the grain size of the film decreased and the crystallinity degraded as N{sub 2} flow rate increases. In addition, N doping caused an obvious red shift in the optical absorption edge. - Highlights: • N doped TiO{sub 2} films were deposited by DC coupled RF magnetron reactive sputtering. • As N{sub 2} flow rate increases, the crystallization of the deposited films degrades. • The higher N{sub 2} flow rate is beneficial to form more substituted N in the film. • N doping causes an obvious red shift in the absorption wavelength.

  2. Multiwalled carbon nanotubes decorated with nitrogen, palladium co-doped TiO{sub 2} (MWCNT/N, Pd co-doped TiO{sub 2}) for visible light photocatalytic degradation of Eosin Yellow in water

    Energy Technology Data Exchange (ETDEWEB)

    Kuvarega, Alex T.; Krause, Rui W. M., E-mail: rkrause@uj.ac.za; Mamba, Bhekie B. [University of Johannesburg, Department of Applied Chemistry, UJ Center for Nanomaterials Science (South Africa)

    2012-03-15

    Multiwalled carbon nanotube (MWCNT/N), Pd co-doped TiO{sub 2} nanocomposites were prepared by calcining the hydrolysis products of the reaction of titanium isopropoxide, Ti(OC{sub 3}H{sub 7}){sub 4} containing multiwalled carbon nanotubes with aqueous ammonia. The prepared samples were characterised by Fourier transform infrared spectroscopy, Raman spectroscopy, thermogravimetric analysis, diffuse reflectance UV-Vis spectrophotometry (DRUV-Vis), XRD, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). DRUV-Vis analysis confirmed the red shift in the absorption edge at lower MWCNT percentages. SEM and TEM images showed the complete coverage of the MWCNTs with clusters of anatase TiO{sub 2} at low MWCNT percentages. Higher MWCNT levels led to their aggregation and consequently poor coverage by N, Pd co-doped TiO{sub 2}. The photocatalytic activities of the nanocomposites were monitored by photodegradation of Eosin Yellow under simulated solar and visible light irradiation ({lambda} > 450 nm). Irradiation with simulated solar radiation gave higher dye-degradation rates compared to visible radiation. The optimum MWCNT weight percentage in the composites was found to be 0.5. High degradation-rate constants of 3.42 Multiplication-Sign 10{sup -2} and 5.18 Multiplication-Sign 10{sup -3} min{sup -1} were realised for the 0.5% MWCNT/N, Pd co-doped TiO{sub 2} composite, using simulated solar light and visible light, respectively.

  3. Effects of Nb and Sr doping on crystal structure of epitaxial BaTiO3 thin films on MgO substrates

    International Nuclear Information System (INIS)

    Kim, Yongsam; Chen, Chunhua; Saiki, Atsushi; Wakiya, Naoki; Shinozaki, Kazuo; Mizutani, Nobuyasu

    2002-01-01

    Niobium (Nb) and strontium (Sr) doped barium titanate (BT) films were deposited by radio frequency (RF) magnetron sputtering with Nb and Sr doped BT ceramic targets, respectively. The effect of Nb and Sr doping on the crystal structure of epitaxial BaTiO 3 thin films on MgO substrates was investigated. The crystal structure of the films was examined using the reciprocal space mapping measurement. All the films exhibit a cube-on-cube relation with respect to the substrates. As the amount of doped Sr increased, both of the in-plane and out-of-plane lattice constants of Sr doped BT films slowly approached the BT bulk values. On the other hand, the lattice constants of Nb doped BT films were rapidly coming close to the bulk values. These indicated that the lattices of doped BT films were relaxed as the amount of doped elements increased. In addition, Nb doping had greater influence on the relaxation of the films than Sr doping for the same content of dopant. (author)

  4. Structural and electronic properties of Mg and Mg-Nb co-doped TiO2 (101) anatase surface

    International Nuclear Information System (INIS)

    Sasani, Alireza; Baktash, Ardeshir; Mirabbaszadeh, Kavoos; Khoshnevisan, Bahram

    2016-01-01

    Highlights: • Formation energy of Mg and Mg-Nb co-doped TiO_2 anatase surface (101) is studied. • Effect of Mg defect to the TiO_2 anatase (101) surface and bond length distribution of the surface is studied and it is shown that Mg defects tend to stay far from each other. • Effect of Mg and Nb to the bond length distribution of the surface studied and it is shown that these defects tend to stay close to each other. • Effects of Mg and Mg-Nb defects on DSSCs using TiO_2 anatase hosting these defects are studied. - Abstract: In this paper, by using density functional theory, Mg and Nb-Mg co-doping of TiO_2 anatase (101) surfaces are studied. By studying the formation energy of the defects and the bond length distribution of the surface, it is shown that Mg defects tend to stay as far as possible to induce least possible lattice distortion while Nb and Mg defects stay close to each other to cause less stress to the surface. By investigating band structure of the surface and changes stemmed from the defects, potential effects of Mg and Mg-Nb co-doping of TiO_2 surface on dye-sensitized solar cells are investigated. In this study, it is shown that the Nb-Mg co-doping could increase J_S_C of the surface while slightly decreasing V_O_C compared to Mg doped surface, which might result in an increase in efficiency of the DSSCs compared to Nb or Mg doped surfaces.

  5. Role of dopant concentration, crystal phase and particle size on microbial inactivation of Cu-doped TiO{sub 2} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Sahu, Manoranjan; Wu Bing; Zhu Liying; Jacobson, Craig; Wang Weining; Jones, Kristen; Goyal, Yogesh; Tang, Yinjie J; Biswas, Pratim, E-mail: pbiswas@wustl.edu [Department of Energy, Environmental and Chemical Engineering, Washington University in St Louis, St Louis, MO 63130 (United States)

    2011-10-14

    The properties of Cu-doped TiO{sub 2} nanoparticles (NPs) were independently controlled in a flame aerosol reactor by varying the molar feed ratios of the precursors, and by optimizing temperature and time history in the flame. The effect of the physico-chemical properties (dopant concentration, crystal phase and particle size) of Cu-doped TiO{sub 2} nanoparticles on inactivation of Mycobacterium smegmatis (a model pathogenic bacterium) was investigated under three light conditions (complete dark, fluorescent light and UV light). The survival rate of M. smegmatis (in a minimal salt medium for 2 h) exposed to the NPs varied depending on the light irradiation conditions as well as the dopant concentrations. In dark conditions, pristine TiO{sub 2} showed insignificant microbial inactivation, but inactivation increased with increasing dopant concentration. Under fluorescent light illumination, no significant effect was observed for TiO{sub 2}. However, when TiO{sub 2} was doped with copper, inactivation increased with dopant concentration, reaching more than 90% (>3 wt% dopant). Enhanced microbial inactivation by TiO{sub 2} NPs was observed only under UV light. When TiO{sub 2} NPs were doped with copper, their inactivation potential was promoted and the UV-resistant cells were reduced by over 99%. In addition, the microbial inactivation potential of NPs was also crystal-phase-and size-dependent under all three light conditions. A lower ratio of anatase phase and smaller sizes of Cu-doped TiO{sub 2} NPs resulted in decreased bacterial survival. The increased inactivation potential of doped TiO{sub 2} NPs is possibly due to both enhanced photocatalytic reactions and leached copper ions.

  6. Electrostatic analysis of n-doped SrTiO3 metal-insulator-semiconductor systems

    International Nuclear Information System (INIS)

    Kamerbeek, A. M.; Banerjee, T.; Hueting, R. J. E.

    2015-01-01

    Electron doped SrTiO 3 , a complex-oxide semiconductor, possesses novel electronic properties due to its strong temperature and electric-field dependent permittivity. Due to the high permittivity, metal/n-SrTiO 3 systems show reasonably strong rectification even when SrTiO 3 is degenerately doped. Our experiments show that the insertion of a sub nanometer layer of AlO x in between the metal and n-SrTiO 3 interface leads to a dramatic reduction of the Schottky barrier height (from around 0.90 V to 0.25 V). This reduces the interface resistivity by 4 orders of magnitude. The derived electrostatic analysis of the metal-insulator-semiconductor (n-SrTiO 3 ) system is consistent with this trend. When compared with a Si based MIS system, the change is much larger and mainly governed by the high permittivity of SrTiO 3 . The non-linear permittivity of n-SrTiO 3 leads to unconventional properties such as a temperature dependent surface potential non-existent for semiconductors with linear permittivity such as Si. This allows tuning of the interfacial band alignment, and consequently the Schottky barrier height, in a much more drastic way than in conventional semiconductors

  7. Characterization and photocatalytic performance evaluation of various metal ion-doped microstructured TiO2 under UV and visible light.

    Science.gov (United States)

    Sahoo, Chittaranjan; Gupta, Ashok K

    2015-01-01

    Commercially available microcrystalline TiO2 was doped with silver, ferrous and ferric ion (1.0 mol %) using silver nitrate, ferrous sulfate and ferric nitrate solutions following the liquid impregnation technology. The catalysts prepared were characterised by FESEM, XRD, FTIR, DRS, particle size and micropore analysis. The photocatalytic activity of the prepared catalysts was tested on the degradation of two model dyes, methylene blue (3,7-bis (Dimethylamino)-phenothiazin-5-ium chloride, a cationic thiazine dye) and methyl blue (disodium;4-[4-[[4-(4-sulfonatoanilino)phenyl]-[4-(4-sulfonatophenyl)azaniumylidenecyclohexa-2,5-dien-1-ylidene]methyl]anilino]benzene sulfonate, an anionic triphenyl methane dye) under irradiation by UV and visible light in a batch reactor. The efficiency of the photocatalysts under UV and visible light was compared to ascertain the light range for effective utilization. The catalysts were found to have the anatase crystalline structure and their particle size is in a range of 140-250 nm. In the case of Fe(2+) doped TiO2 and Fe(3+) doped TiO2, there was a greater shift in the optical absorption towards the visible range. Under UV light, Ag(+) doped TiO2 was the most efficient catalyst and the corresponding decolorization was more than 99% for both the dyes. Under visible light, Fe(3+) doped TiO2 was the most efficient photocatalyst with more than 96% and 90% decolorization for methylene blue and methyl blue, respectively. The kinetics of the reaction under both UV and visible light was investigated using the Langmuir-Hinshelwood pseudo-first-order kinetic model. Kinetic measurements confirmed that, Ag(+) doped TiO2 was most efficient in the UV range, while Fe(3+) doped TiO2 was most efficient in the visible range.

  8. High-Quality Fe-doped TiO2 films with Superior Visible-Light Performance

    DEFF Research Database (Denmark)

    Su, Ren; Bechstein, Ralf; Kibsgaard, Jakob

    2012-01-01

    We report on high-quality polycrystalline Fe-doped TiO2 (Fe–TiO2) porous films synthesized via one-step electrochemical oxidation. We demonstrate that delicate properties such as the impurity concentration and the microstructure that strongly influence the performance of the material for photovol...

  9. Room temperature magnetic and dielectric properties of cobalt doped CaCu3Ti4O12 ceramics

    Science.gov (United States)

    Mu, Chunhong; Song, Yuanqiang; Wang, Haibin; Wang, Xiaoning

    2015-05-01

    CaCu3Ti4-xCoxO12 (x = 0, 0.2, 0.4) ceramics were prepared by a conventional solid state reaction, and the effects of cobalt doping on the room temperature magnetic and dielectric properties were investigated. Both X-ray diffraction and energy dispersive X-ray spectroscopy confirmed the presence of Cu and Co rich phase at grain boundaries of Co-doped ceramics. Scanning electron microscopy micrographs of Co-doped samples showed a striking change from regular polyhedral particle type in pure CaCu3Ti4O12 (CCTO) to sheet-like grains with certain growth orientation. Undoped CaCu3Ti4O12 is well known for its colossal dielectric constant in a broad temperature and frequency range. The dielectric constant value was slightly changed by 5 at. % and 10 at. % Co doping, whereas the second relaxation process was clearly separated in low frequency region at room temperature. A multirelaxation mechanism was proposed to be the origin of the colossal dielectric constant. In addition, the permeability spectra measurements indicated Co-doped CCTO with good magnetic properties, showing the initial permeability (μ') as high as 5.5 and low magnetic loss (μ″ < 0.2) below 3 MHz. And the interesting ferromagnetic superexchange coupling in Co-doped CaCu3Ti4O12 was discussed.

  10. Effects of TiC doping on the upper critical field of MgB2 superconductors

    International Nuclear Information System (INIS)

    Yan, S.C.; Zhou, L.; Yan, G.; Lu, Y.F.

    2008-01-01

    TiC doped MgB 2 bulks were fabricated by two-step reaction method. The sample with a nominal compositions of Mg(B 0.95 (TiC) 0.05 ) 4 was first sintered at 1000 deg. C for 0.5 h. An appropriate amount of Mg was added to reach the stoichiometry of Mg(B 0.95 (TiC) 0.05 ) 2 , which was sintered at 750 deg. C for 2 h. The H c2 for the micro-TiC doped MgB 2 reached 12 T at 20 K. And J c is 5.3 x 10 4 A/cm 2 at 20 K and 1 T. The results indicate that the two-step reaction method could effectively introduce the carbon in TiC into the MgB 2 crystalline lattice, and therefore improve the upper critical field

  11. Zr-doped TiO{sub 2} supported on delaminated clay materials for solar photocatalytic treatment of emerging pollutants

    Energy Technology Data Exchange (ETDEWEB)

    Belver, C., E-mail: carolina.belver@uam.es; Bedia, J.; Rodriguez, J.J.

    2017-01-15

    Highlights: • Novel Zr-doped TiO{sub 2} delaminated clay materials were prepared by a sol-gel process. • Zr is incorporated into the anatase lattice. • Zr-TiO{sub 2} nanoparticles are homogenously distributed over the delaminated clay. • Zr doping enhances the photoactivity by reducing the band gap. • Degradation rates were favored at low concentrations and high radiation intensities. - Abstract: Solar light-active Zr-doped TiO{sub 2} nanoparticles were successfully immobilized on delaminated clay materials by a one-step sol-gel route. Fixing the amount of TiO{sub 2} at 65 wt.%, this work studies the influence of Zr loading (up to 2%) on the photocatalytic activity of the resulting Zr-doped TiO{sub 2}/clay materials. The structural characterization demonstrates that all samples were formed by a delaminated clay with nanostructured anatase assembled on its surface. The Zr dopant was successfully incorporated into the anatase lattice, resulting in a slight deformation of the anatase crystal and the reduction of the band gap. These materials exhibit high surface area with a disordered mesoporous structure formed by TiO{sub 2} particles (15–20 nm) supported on a delaminated clay. They were tested in the solar photodegradation of antipyrine, usually used as an analgesic drug and selected as an example of emerging pollutant. High degradation rates have been obtained at low antipyrine concentrations and high solar irradiation intensities with the Zr-doped TiO{sub 2}/clay catalyst, more effective than the undoped one. This work demonstrates the potential application of the synthesis method for preparing novel and efficient solar-light photocatalysts based on metal-doped anatase and a delaminated clay.

  12. Hydrogenation Properties of TiFe Doped with Zirconium

    Directory of Open Access Journals (Sweden)

    Catherine Gosselin

    2015-11-01

    Full Text Available The goal of this study was to optimize the activation behaviour of hydrogen storage alloy TiFe. We found that the addition of a small amount of Zr in TiFe alloy greatly reduces the hydrogenation activation time. Two different procedural synthesis methods were applied: co-melt, where the TiFe was melted and afterward re-melted with the addition of Zr, and single-melt, where Ti, Fe and Zr were melted together in one single operation. The co-melted sample absorbed hydrogen at its maximum capacity in less than three hours without any pre-treatment. The single-melted alloy absorbed its maximum capacity in less than seven hours, also without pre-treatment. The reason for discrepancies between co-melt and single-melt alloys was found to be the different microstructure. The effect of air exposure was also investigated. We found that the air-exposed samples had the same maximum capacity as the argon protected samples but with a slightly longer incubation time, which is probably due to the presence of a dense surface oxide layer. Scanning electron microscopy revealed the presence of a rich Zr intergranular phase in the TiFe matrix, which is responsible for the enhanced hydrogenation properties of these Zr-doped TiFe alloys.

  13. Electronic and magnetic properties of digitally Ti doped InP: A first principles study

    International Nuclear Information System (INIS)

    Rahman, Gul; Cho, Sunglae; Hong, Soon Cheol

    2008-01-01

    Using the full-potential linearized augmented plane wave method within the generalized gradient approximation, we study the electronic and the magnetic properties of digitally Ti doped InP. It is quite interesting that digitally Ti-doped InP system shows half metallic ferromagnetism even though both bulk zinc blende TiP and InP are paramagnetic. We also investigate the electronic and the magnetic properties as a function of spacer layer thickness. Their properties such as exchange coupling constant and atomic projected density of states are more or less independent of the InP thickness. Spin density contour maps indicate that the spin-polarization is confined within the TiP plane. The system may show a highly anisotropic property in spin-polarized transport. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  14. Magnetic and magnetoelectric properties of NdCrTiO5 revealed by systematically rare-earth doping

    Science.gov (United States)

    Li, Qing; Feng, Zhenjie; Cheng, Cheng; Wang, Bojie; Chu, Hao; Huang, Ping; Wang, Difei; Qian, Xiaolong; Yu, Chuan; Wang, Guohua; Deng, Dongmei; Jing, Chao; Cao, Shixun; Zhang, Jincang

    2018-01-01

    We have systematically synthesized polycrystalline samples of Nd0.9A0.1CrTiO5 (A = Pr, Nd, Gd, Dy, Er, Tm, and Yb), and have investigated their crystal structure, polarization and magnetic susceptibility. The polarization values of doped samples are suppressed comparing to pure NdCrTiO5 sample, which indicates that the polarization is highly dependence with the magnetic moments of doping ions. The TN of Cr-Cr in Nd0.9A0.1CrTiO5 are dominated by both the suppression effect caused by doped magnetic moment increment and the enhancement effect caused by c axis contracting. We conclude that the magnetic moments in the rare-earth Nd sites play an important role in the magnetoelectric effect in NdCrTiO5 family. The substitution effect discussion here can help us well understand the intrinsic mechanism and provide a possible guidance in exploring new magnetoelectric coupling systems.

  15. Synthesis, structure and total conductivity of A-site doped LaTiO{sub 3−δ} perovskites

    Energy Technology Data Exchange (ETDEWEB)

    Bradha, M. [Nanotech Research Facility, PSG Institute of Advanced Studies, Coimbatore 641 004, TN (India); Hussain, S.; Chakravarty, Sujay [UGC-DAE CSR, Kalpakkam Node, Kokilamedu 603 104, TN (India); Amarendra, G. [UGC-DAE CSR, Kalpakkam Node, Kokilamedu 603 104, TN (India); Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102, TN (India); Ashok, Anuradha, E-mail: anu.machina@gmail.com [Nanotech Research Facility, PSG Institute of Advanced Studies, Coimbatore 641 004, TN (India)

    2015-03-25

    Highlights: • A-site divalent alkaline earth metal doped LaTiO{sub 3−δ} perovskites were synthesised by sol–gel method. • Structural studies revealed no change in crystal symmetry but change in cell dimensions after doping. • After doping divalent cations in A-site, an enhancement in total conductivity was observed in LaTiO{sub 3−δ}. • Temperature dependent electrical property was observed in all synthesised perovskites. - Abstract: Oxygen deficient perovskites LaTiO{sub 3−δ} and La{sub 0.8}A{sub 0.2}TiO{sub 3−δ} (A = Ba, Sr, Ca) were synthesized by sol–gel method. The effect of divalent dopants on microstructure is investigated in detail using X-ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The oxidation states of La{sup 3+} and Ti{sup 3+} ions have been deduced using X-ray Photoelectron Spectroscopy (XPS). Impedance spectroscopy was used to analyze the total conductivity, an increase in conductivity was observed after doping in the A-site with divalent cations Ba, Ca and Sr. Among the investigated perovskites La{sub 0.8}Ca{sub 0.2}TiO{sub 3−δ} exhibited the maximum conductivity of 1.22 × 10{sup −2} S/cm in air atmosphere at 650 °C.

  16. Carbamazepine degradation using a N-doped TiO{sub 2} coated photocatalytic membrane reactor: Influence of physical parameters

    Energy Technology Data Exchange (ETDEWEB)

    Horovitz, Inna [School of Mechanical Engineering, Faculty of Engineering, Tel Aviv University, Tel Aviv 69978 (Israel); The Hydro-Chemistry Laboratory, Faculty of Geography and the Environment, Tel Aviv University, Tel Aviv 69978 (Israel); Avisar, Dror [The Hydro-Chemistry Laboratory, Faculty of Geography and the Environment, Tel Aviv University, Tel Aviv 69978 (Israel); Baker, Mark A.; Grilli, Rossana [The Surface Analysis Laboratory, Faculty of Engineering and Physical Sciences, University of Surrey, Guildford, Surrey, GU2 7XH (United Kingdom); Lozzi, Luca; Di Camillo, Daniela [Department of Physical and Chemical Sciences, University of L' Aquila, Via Vetoio, I-67100 L' Aquila (Italy); Mamane, Hadas, E-mail: hadasmg@post.tau.ac.il [School of Mechanical Engineering, Faculty of Engineering, Tel Aviv University, Tel Aviv 69978 (Israel)

    2016-06-05

    Highlights: • UV–vis N-doped TiO{sub 2} was deposited by sol-gel onto Al{sub 2}O{sub 3} microfiltration membranes. • Coating decreased permeability by 50 and 12% for 200- and 800-nm Al{sub 2}O{sub 3} membranes. • Flow through membrane results in higher reaction rates compared to flow on top. • Higher vis photocatalytic activity for N-doped TiO{sub 2} vs. non-doped TiO{sub 2} membranes. • Mass transfer is a critical parameter for the design of immobilized PMR. - Abstract: Commercial α-Al{sub 2}O{sub 3} photocatalytic membranes with a pore size of 200 and 800-nm were coated with N-doped TiO{sub 2} photocatalytic film using a sol-gel technique for concurrent bottom-up filtration and photocatalytic oxidation. X-ray diffraction confirmed that the deposited N-doped TiO{sub 2} films are in the form of anatase with 78–84% coverage of the membrane surface. The concentration of N found by X-ray photoelectron spectroscopy was in the range of 0.3–0.9 atomic percentage. Membrane permeability after coating decreased by 50% and 12% for the 200- and 800-nm membrane substrates, respectively. The impact of operational parameters on the photocatalytic activity (PCA) of the N-doped TiO{sub 2}-coated membranes was examined in a laboratory flow cell based on degradation of the model micropollutant carbamazepine, using a solar simulator as the light source. The significant gap in degradation rate between flow through the membrane and flow on the surface of the membrane was attributed both to the hydraulic effect and in-pore PCA. N-doped TiO{sub 2}-coated membranes showed enhanced activity for UV wavelengths, in addition to activity under visible light. Experiments of PCA under varying flow rates concluded that the process is in the mass-transfer control regime. Carbamazepine removal rate increased with temperature, despite the decrease in dissolved oxygen concentration.

  17. Visible Light Irradiation-Mediated Drug Elution Activity of Nitrogen-Doped TiO2 Nano tubes

    International Nuclear Information System (INIS)

    Oh, S.; Moon, K.S.; Bae, J.M.; Moon, J.H.; Jin, S.

    2013-01-01

    We have developed nitrogen-doped TiO 2 nano tubes showing photo catalytic activity in the visible light region and have investigated the triggered release of antibiotics from these nano tubes in response to remote visible light irradiation. Scanning electron microscopy (SEM) observations indicated that the structure of TiO 2 nano tubes was not destroyed on the conditions of 0.05 and 0.1 M diethanolamine treatment. The results of X-ray photoelectron spectroscopy (XPS) confirmed that nitrogen, in the forms of nitrite (TiO 2 ) and nitrogen monoxide (NO), had been incorporated into the TiO 2 nano tube surface. A drug-release test revealed that the antibiotic-loaded TiO 2 nano tubes showed sustained and prolonged drug elution with the help of polylactic acid. Visible light irradiation tests showed that the antibiotic release from nitrogen-doped nano tubes was significantly higher than that from pure TiO 2 nano tubes (ρ ≨ 0.05).

  18. Photoelectrochemical oxidation of ibuprofen via Cu_2O-doped TiO_2 nanotube arrays

    International Nuclear Information System (INIS)

    Sun, Qiannan; Peng, Yen-Ping; Chen, Hanlin; Chang, Ken-Lin; Qiu, Yang-Neng; Lai, Shiau-Wu

    2016-01-01

    Highlights: • A p–n junction material was synthesized to enhance photocatalytic ability. • Cu_2O-doped TiO_2 nanotube arrays works as a photoanode in a PEC system. • Recombination of photo-generated holes and electrons were greatly reduced. • Synergetic effect was quantified in PEC degradation. • Recombination of photogenerated holes and electrons was greatly enhanced. - Abstract: A p–n junction based Cu_2O-doped TiO_2 nanotube arrays (Cu_2O-TNAs) were synthesized and used as a working anode in a photoelectrochemical (PEC) system. The results revealed that the Cu_2O-TNAs were dominated by the anatase phase and responded significantly to visible light. XPS analyses indicated that with an amount of 24.79% Cu doping into the structure, the band gap of Cu_2O-TNAs was greatly reduced. SEM images revealed that the supported TiO_2 nanotubes had diameters of approximately 80 nm and lengths of about 2.63 μm. Upon doping with Cu_2O, the TiO_2 nanotubes maintained their structural integrity, exhibiting no significant morphological change, favoring PEC applications. Under illumination, the photocurrent from Cu_2O/TNAs was 2.4 times larger than that from TNAs, implying that doping with Cu_2O significantly improved electron mobility by reducing the rate of recombination of electron-hole pairs. The EIS and Bode plot revealed that the estimated electron lifetimes, τ_e_l, of TNAs and Cu_2O/TNAs were 6.91 and 26.26 ms, respectively. The efficiencies of degradation of Ibuprofen by photoelectrochemical, photocatalytic (PC), electrochemical (EC) and photolytic (P) methods were measured.

  19. Nb-doped TiO2 cathode catalysts for oxygen reduction reaction of polymer electrolyte fuel cells

    KAUST Repository

    Arashi, Takuya

    2014-09-01

    Nb-doped TiO2 particles were studied as electrocatalysts for the oxygen reduction reaction (ORR) under acidic conditions. The Nb-doped TiN nanoparticles were first synthesized by meso-porous C3N4 and then fully oxidized to Nb-doped TiO2 by immersing in 0.1 M H 2SO4 at 353 K for 24 h. Although the ORR activity of the as-obtained sample was low, a H2 treatment at relatively high temperature (1173 K) dramatically improved the ORR performance. An onset potential as high as 0.82 VRHE was measured. No degradation of the catalysts was observed during the oxidation-reduction cycles under the ORR condition for over 127 h. H2 treatment at temperatures above 1173 K caused the formation of a Ti4O7 phase, resulting in a decrease in ORR current. Elemental analysis indicated that the Nb-doped TiO 2 contained 25 wt% residual carbon. Calcination in air at 673 or 973 K eliminated the residual carbon in the catalyst, which was accompanied by a dramatic decrease in ORR activity. This post-calcination process may reduce the conductivity of the sample by filling the oxygen vacancies, and the carbon residue in the particle aggregates may enhance the electrocatalytic activity for ORR. The feasibility of using conductive oxide materials as electrocatalysts is discussed. © 2013 Elsevier B.V.

  20. Nb-doped TiO2 cathode catalysts for oxygen reduction reaction of polymer electrolyte fuel cells

    KAUST Repository

    Arashi, Takuya; Seo, Jeongsuk; Takanabe, Kazuhiro; Kubota, Jun; Domen, Kazunari

    2014-01-01

    Nb-doped TiO2 particles were studied as electrocatalysts for the oxygen reduction reaction (ORR) under acidic conditions. The Nb-doped TiN nanoparticles were first synthesized by meso-porous C3N4 and then fully oxidized to Nb-doped TiO2 by immersing in 0.1 M H 2SO4 at 353 K for 24 h. Although the ORR activity of the as-obtained sample was low, a H2 treatment at relatively high temperature (1173 K) dramatically improved the ORR performance. An onset potential as high as 0.82 VRHE was measured. No degradation of the catalysts was observed during the oxidation-reduction cycles under the ORR condition for over 127 h. H2 treatment at temperatures above 1173 K caused the formation of a Ti4O7 phase, resulting in a decrease in ORR current. Elemental analysis indicated that the Nb-doped TiO 2 contained 25 wt% residual carbon. Calcination in air at 673 or 973 K eliminated the residual carbon in the catalyst, which was accompanied by a dramatic decrease in ORR activity. This post-calcination process may reduce the conductivity of the sample by filling the oxygen vacancies, and the carbon residue in the particle aggregates may enhance the electrocatalytic activity for ORR. The feasibility of using conductive oxide materials as electrocatalysts is discussed. © 2013 Elsevier B.V.

  1. One-pot synthesis of polyaniline-doped in mesoporous TiO2 and its electrorheological behavior

    International Nuclear Information System (INIS)

    Wei Chuan; Zhu Yihua; Yang Xiaoling; Li Chunzhong

    2007-01-01

    A class of hybrid organic-inorganic composite for application in electrorheological (ER) fluid was prepared by using a simple one-pot method. Transmission electron microscopy (TEM) image shows that the synthesized material had a mesoporous structure. X-ray diffraction (XRD) further proves that the pore size is about 7.4 nm with an anatase TiO 2 framework. Fourier transform infrared (FT-IR) and nitrogen sorption curve reveal polyaniline (PANI) is doped in mesochannels. The ER behaviors of PANI/TiO 2 in silicone oil are invesigated with different doping degrees under different electric fields. The results obtained provide more insight into the role of proper doping in ER fluid

  2. Enhanced photocatalytic degradation of dye under visible light on mesoporous microspheres by defects in manganese- and nitrogen-co-doped TiO{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Feng, Lu; Jiang, Heng, E-mail: hjiang78@hotmail.com [Liaoning Shihua University, School of Chemistry and Materials Science (China); Zou, Mingming; Xiong, Fengqiang; Ganeshraja, Ayyakannu Sundaram; Pervaiz, Erum [Chinese Academy of Sciences, Dalian National Laboratory for Clean Energy, Dalian Institute of Chemical Physics (China); Liu, Yinan; Zou, Shunying [Dalian Environmental Protection Laboratory (China); Yang, Minghui, E-mail: myang@dicp.ac.cn [Chinese Academy of Sciences, Dalian National Laboratory for Clean Energy, Dalian Institute of Chemical Physics (China)

    2016-09-15

    Manganese- and nitrogen-co-doped mesoporous TiO{sub 2} microsphere photocatalysts are prepared by a simple sol–gel method with controllable sizes in the range of 400–500 nm and high surface area of 112 m{sup 2} g{sup −1}. Manganous acetate is the Mn source, and ammonia gas is the nitrogen source used. The dopants are found to be uniformly distributed in the TiO{sub 2} matrix. Interestingly, in (Mn,N)-co-doped TiO{sub 2}, we observe an effective indirect band gap of ~2.58 eV. (Mn,N)-co-doped mesoporous TiO{sub 2} microspheres show higher photocatalytic activity than Mn–TiO{sub 2} microspheres under visible light irradiation. Among the samples reported in this work, 0.2 at.% Mn doping and 500 °C 2-h nitriding condition give the highest photocatalytic activity. The observed photocatalytic activity in the (Mn,N)-co-doped TiO{sub 2} is attributed to the contribution from improved absorption due to trap levels of Mn, oxygen vacancies and N doping.Graphical AbstractManganese- and nitrogen-co-doped mesoporous TiO{sub 2} microspheres containing substitutional N, interstitial N and O vacancies show high visible light photocatalytic activity.

  3. Phosphorous-doped TiO2 nanoparticles: synthesis, characterization, and visible photocatalytic evaluation on sulfamethazine degradation.

    Science.gov (United States)

    Mendiola-Alvarez, Sandra Yadira; Hernández-Ramírez, Ma Aracely; Guzmán-Mar, Jorge Luis; Garza-Tovar, Lorena Leticia; Hinojosa-Reyes, Laura

    2018-05-24

    Mesoporous phosphorous-doped TiO 2 (TP) with different wt% of P (0.5, 1.0, and 1.5) was synthetized by microwave-assisted sol-gel method. The obtained materials were characterized by XRD with cell parameters refinement approach, Raman, BET-specific surface area analysis, SEM, ICP-OES, UV-Vis with diffuse reflectance, photoluminescence, FTIR, and XPS. The photocatalytic activity under visible light was evaluated on the degradation of sulfamethazine (SMTZ) at pH 8. The characterization of the phosphorous materials (TP) showed that incorporation of P in the lattice of TiO 2 stabilizes the anatase crystalline phase, even increasing the annealing temperature. The mesoporous P-doped materials showed higher surface area and lower average crystallite size, band gap, and particle size; besides, more intense bands attributed to O-H bond were observed by FTIR analysis compared with bare TiO 2 . The P was substitutionally incorporated in the TiO 2 lattice network as P 5+ replacing Ti 4+ to form Ti-O-P bonds and additionally present as PO 4 3-  on the TiO 2 surface. All these characteristics explain the observed superior photocatalytic activity on degradation (100%) and mineralization (32%) of SMTZ under visible radiation by TP catalysts, especially for P-doped TiO 2 1.0 wt% calcined at 450 °C (TP1.0-450). Ammonium, nitrate, and sulfate ions released during the photocatalytic degradation were quantified by ion chromatography; the nitrogen and sulfur mass balance evidenced the partial mineralization of this recalcitrant molecule.

  4. Electrochemically synthesized visible light absorbing vertically aligned N-doped TiO2 nanotube array films

    International Nuclear Information System (INIS)

    Antony, Rajini P.; Mathews, Tom; Ajikumar, P.K.; Krishna, D. Nandagopala; Dash, S.; Tyagi, A.K.

    2012-01-01

    Graphical abstract: Display Omitted Highlights: ► Single step electrochemical synthesis of N-doped TiO 2 nanotube array films. ► Effective substitutional N-doping achieved. ► Different N-concentrations were achieved by varying the N-precursor concentration in the electrolyte. ► Visible light absorption observed at high N-doping. -- Abstract: Visible light absorbing vertically aligned N-doped anatase nanotube array thin films were synthesized by anodizing Ti foils in ethylene glycol + NH 4 F + water mixture containing urea as nitrogen source. Different nitrogen concentrations were achieved by varying the urea content in the electrolyte. The structure, morphology, composition and optical band gap of the nanotube arrays were determined by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy (XPS) and diffuse reflectance spectroscopy, respectively. The substitution of O 2− ions by N 3− ions in the anion sublattice as well as the formulae of the doped samples was confirmed from the results of XPS. The optical band gap of the nanotube arrays was found to decrease with N-concentration. The sample with the highest concentration corresponding to the formula TiO 1.83 N 0.14 showed two regions in the Tauc's plot indicating the presence of interband states.

  5. Formation of Ti(III) and Ti(IV) states in Ti{sub 3}O{sub 5} nano- and microfibers obtained from hydrothermal annealing of C-doped TiO{sub 2} on Si

    Energy Technology Data Exchange (ETDEWEB)

    Stem, Nair, E-mail: nairstem@hotmail.com [Laboratório de Sistemas Integráveis (LSI), Escola Politécnica, Universidade de São Paulo, Av. Prof. Luciano Gualberto 158, 05508900 São Paulo, SP (Brazil); Souza, Michele L.; Araújo de Faria, Dalva Lúcia Araújo [Laboratório de Espectroscopia Molecular (LEM), Instituto de Química, Universidade de São Paulo, Av. Prof. Lineu Prestes 748, 05508900 São Paulo, SP (Brazil); Santos Filho, Sebastião G. dos [Laboratório de Sistemas Integráveis (LSI), Escola Politécnica, Universidade de São Paulo, Av. Prof. Luciano Gualberto 158, 05508900 São Paulo, SP (Brazil)

    2014-05-02

    In this work, it is investigated the formation of Ti(III) and Ti(IV) states at the surface and in the bulk of the Ti{sub 3}O{sub 5} material grown as meshes of nano- and micro-fibers obtained from hydrothermal annealing of C-doped TiO{sub 2} on Si. The topography and distribution of the fibers in the meshes were characterized by atomic force microscopy. When the fiber distribution was more compact, a higher photoluminescence signal at 850 nm (1.46 eV) was obtained, indicating the presence of a higher number of defects corresponding to the Ti(III) sites. From X-ray photoelectron spectroscopy, it was obtained a Ti(III)/Ti(IV) ratio much lower than the expected value for the Ti{sub 3}O{sub 5} phase (2 Ti(III): 1 Ti(IV)). The discrepancy was mainly attributed to the reaction of surface Ti(III) states of the Ti{sub 3}O{sub 5} fibers with water during the hydrothermal annealing, resulting in surface Ti(IV) with -OH radicals. On the other hand, X-ray photoelectron spectroscopy also indicated that substitutional and interstitial carbon atoms coexist, elemental carbon exists in the samples due to the co-deposition process and, as a result, the carbon inside of the TiO{sub 2} rutile lattice is acting as one of the precursors for the formation of Ti{sub 3}O{sub 5}. - Highlights: • Ti(III) states are detected inside of Ti{sub 3}O{sub 5} nano- and microfibers. • Ti(IV) states are predominantly detected on the surface of Ti{sub 3}O{sub 5} nano- and microfibers. • Photoluminescence at 850 nm for Ti{sub 3}O{sub 5} is due to defects associated to Ti(III). • Rutile possibly changes to C2/m Ti{sub 3}O{sub 5} during the hydrothermal annealing of C-doped TiO{sub 2}.

  6. Temperature dependence of gas sensing behaviour of TiO2 doped PANI composite thin films

    Science.gov (United States)

    Srivastava, Subodh; Sharma, S. S.; Sharma, Preetam; Sharma, Vinay; Rajura, Rajveer Singh; Singh, M.; Vijay, Y. K.

    2014-04-01

    In the present work we have reported the effect of temperature on the gas sensing properties of TiO2 doped PANI composite thin film based chemiresistor type gas sensors for hydrogen gas sensing application. PANI and TiO2 doped PANI composite were synthesized by in situ chemical oxidative polymerization of aniline at low temperature. The electrical properties of these composite thin films were characterized by I-V measurements as function of temperature. The I-V measurement revealed that conductivity of composite thin films increased as the temperature increased. The changes in resistance of the composite thin film sensor were utilized for detection of hydrogen gas. It was observed that at room temperature TiO2 doped PANI composite sensor shows higher response value and showed unstable behavior as the temperature increased. The surface morphology of these composite thin films has also been characterized by scanning electron microscopy (SEM) measurement.

  7. Solvothermal syntheses of Bi and Zn co-doped TiO_2 with enhanced electron-hole separation and efficient photodegradation of gaseous toluene under visible-light

    International Nuclear Information System (INIS)

    Li, Juan-Juan; Cai, Song-Cai; Xu, Zhen; Chen, Xi; Chen, Jin; Jia, Hong-Peng; Chen, Jing

    2017-01-01

    Highlights: • Bi-Zn co-doped TiO_2 catalysts were prepared by solvothermal route. • The incorporation of Bi doping into the TiO_2 generates intermediate energy levels. • Bi and Zn doping showed the enhanced absorption in visible-light region. • Zn dopant acts as a mediator of interfacial charge transfer. • TiBi_1_._9_%Zn_1_%O_2 exhibited high photocatalytic degradation for toluene. - Abstract: This study investigated the effects of Bi doped and Bi-Zn co-doped TiO_2 on photodegradation of gaseous toluene. The doped TiO_2 with various concentration of metal was prepared using the solvothermal route and characterized by SEM, XRD, Raman, BET, DRS, XPS, PL and EPR. Their photocatalytic activities under visible-light irradiation were drastically influenced by the dopant content. The results showed that moderate metal doping levels were obviously beneficial for the toluene degradation, while high doping levels suppressed the photocatalytic activity. The photocatalytic degradation of toluene over TiBi_1_._9_%O_2 and TiBi_1_._9_%Zn_1_%O_2 can reach to 51% and 93%, respectively, which are much higher than 25% of TiO_2. Bi doping into TiO_2 lattice generates new intermediate energy level of Bi below the CB edge of TiO_2. The electron excitation from the VB to Bi orbitals results in the decreased band gap, extended absorption of visible-light and thus enhances its photocatalytic efficiency. Zn doping not only further enhances the absorption in this visible-light region, but also Zn dopant exists as the form of ZnO crystallites located on the interfaces of TiO_2 agglomerates and acts as a mediator of interfacial charge transfer to suppress the electron-hole recombination. These synergistic effects are responsible for the enhanced photocatalytic performance.

  8. Structural and Visible-Near Infrared Optical Properties of Cr-Doped TiO2 for Colored Cool Pigments

    Science.gov (United States)

    Yuan, Le; Weng, Xiaolong; Zhou, Ming; Zhang, Qingyong; Deng, Longjiang

    2017-11-01

    Chromium-doped TiO2 pigments were synthesized via a solid-state reaction method and studied with X-ray diffraction, SEM, XPS, and UV-VIS-NIR reflectance spectroscopy. The incorporation of Cr3+ accelerates the transition from the anatase phase to the rutile phase and compresses the crystal lattice. Moreover, the particle morphology, energy gap, and reflectance spectrum of Cr-doped TiO2 pigments is affected by the crystal structure and doping concentration. For the rutile samples, some of the Cr3+ ions are oxidized to Cr4+ after sintering at a high temperature, which leads to a strong near-infrared absorption band due to the 3A2 → 3 T1 electric dipole-allowed transitions of Cr4+. And the decrease of the band gap causes an obvious redshift of the optical absorption edges as the doping concentration increases. Thus, the VIS and near-infrared average reflectance of the rutile Ti1 - x Cr x O2 sample decrease by 60.2 and 58%, respectively, when the Cr content increases to x = 0.0375. Meanwhile, the color changes to black brown. However, for the anatase Ti1 - x Cr x O2 pigments, only the VIS reflection spectrum is inhibited by forming some characteristic visible light absorption peaks of Cr3+. The morphology, band gap, and NIR reflectance are not significantly affected. Finally, a Cr-doped anatase TiO2 pigment with a brownish-yellow color and 90% near-infrared reflectance can be obtained.

  9. Chrystal structure properties of Al-doped Li{sub 4}Ti{sub 5}O{sub 12} synthesized by solid state reaction method

    Energy Technology Data Exchange (ETDEWEB)

    Sandi, Dianisa Khoirum, E-mail: dianisa875@gmail.com; Suryana, Risa, E-mail: rsuryana@staff.uns.ac.id [Department of Physics, Faculty of Mathematics and Natural Sciences, Sebelas Maret University (Indonesia); Priyono, Slamet, E-mail: slam013@lipi.go.id [Physics Research Center (P2F)-LIPI, Puspiptek Area, Serpong, Tangerang (Indonesia)

    2016-02-08

    This research aim is to analyze the effect of Aluminum (Al) doping in the structural properties of Al-doped Li{sub 4}Ti{sub 5}O{sub 12} as anode in lithium ion battery. Al-doped Li{sub 4}Ti{sub 5}O{sub 12} powders were synthesized by solid state reaction method. LiOH.H{sub 2}O, TiO{sub 2}, and Al{sub 2}O{sub 3} were raw materials. These materials were milled for 15 h, calcined at temperature of 750{sup o}C and sintered at temperature of 800{sup o}C. Mole percentage of doping Al (x) was varied at x=0; x=0.025; and x =0.05. Al-doped Li{sub 4}Ti{sub 5}O{sub 12} powders were synthesized by solid state reaction method. X-ray diffraction was employed to determine the structure of Li{sub 4}Ti{sub 5}O{sub 12}. The PDXL software was performed on the x-ray diffraction data to estimate the phase percentage, the lattice parameter, the unit cell volume, and the crystal density. Al-doped Li{sub 4}Ti{sub 5}O{sub 12} has cubic crystal structure. Al-doping at x=0 and x=0.025 does not change the phase as Li{sub 4}Ti{sub 5}O{sub 12} while at x=0.050 the phase changes to the LiTiAlO{sub 4}. The diffraction patterns show that the angle shifted to the right as the increase of x which indicated that Al substitute Ti site. Percentage of Li{sub 4}Ti{sub 5}O{sub 12} phase at x=0 and x=0.025 was 97.8% and 96.8%, respectively. However, the lattice parameters, the unit cell volume, and the crystal density does not change significantly at x=0; x=0.025; and x=0.050. Based on the percentage of Li{sub 4}Ti{sub 5}O{sub 12} phase, the Al-doped Li at x=0 and x=0.025 is promising as a lithium battery anode.

  10. Characterization and mechanism analysis of N doped TiO2 with visible light response and its enhanced visible activity

    International Nuclear Information System (INIS)

    Cheng Xiuwen; Yu Xiujuan; Xing Zipeng

    2012-01-01

    Nitrogen doped TiO 2 nanoparticles were synthesized through a hydrolysis-precipitation process using ammonia water as the doping species. The resulting materials were characterized by XRD, DRS, SPS, XPS and FT-IR. Further, the activity enhanced-mechanism was discussed in detail. XRD results showed that doping with nitrogen could effectively retard the phase transformation of TiO 2 from anatase to rutile and increase the anatase crystallinity. DRS and SPS results indicated that the light absorbance edge of nitrogen doped TiO 2 nanoparticle was obviously red-shifted to visible light region and the separation rates of photogenerated charge carriers were greatly improved, respectively. XPS and FT-IR analysis implied that the contents of surface hydroxyl groups were improved significantly and the VBM (valance bond maximum) of O2p was 2.3 eV. Under the visible light irradiation with 120 min, a 65.3% degradation rate of phenol could be achieved. The photocatalytic activity of nitrogen doped TiO 2 was 2.08 and 1.97 times than that of pure TiO 2 and P25 TiO 2 , respectively. The enhanced visible light activity was attributed to the well anatase crystallinity, small crystallite size, intense light absorbance edge in visible region, more content of surface hydroxyl groups and high separation efficiency of photogenerated charge carriers.

  11. Structural and photodegradation behaviors of Fe{sup 3+}-doping TiO{sub 2} thin films prepared by a sol–gel spin coating

    Energy Technology Data Exchange (ETDEWEB)

    Lin, Huey-Jiuan; Yang, Tien-Syh [Department of Materials Science and Engineering, National United University, 1 Lien-Da, Kung-Ching Li, Miao-Li 36003, Taiwan (China); Wang, Moo-Chin, E-mail: mcwang@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 80782, Taiwan (China); Hsi, Chi-Shiung, E-mail: chsi@nuu.edu.tw [Department of Materials Science and Engineering, National United University, 1 Lien-Da, Kung-Ching Li, Miao-Li 36003, Taiwan (China)

    2014-10-15

    Highlights: • Pure and various Fe{sup 3+}-doped TiO{sub 2} thin films have been successfully fabricated. • The phase of all thin films was single phase of anatase TiO{sub 2} when calcined at 823 K. • The crystallinity of TiO{sub 2} thin films decreased as Fe{sup 3+}-doping increased. • The photodegradation of each sample increased as the irradiation time increased. • The photodegradation increased as Fe{sup 3+}-doping increased at a fixed irradiation time. - Abstract: Pure and various Fe{sup 3+}-doping TiO{sub 2} thin films have been successfully fabricated on glass substrate prepared by a sol–gel spin coating route. The structural and photodegradation behavior of these films after calcined at various temperatures for 1 h were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) spectrum and degradation of 1.0 × 10{sup −5} M methylene blue solution. When all thin films after calcined at 823 K for 1 h, the crystalline phase are comprised only contained single phase of anatase TiO{sub 2}. The crystallinity of various Fe{sup 3+}-doping TiO{sub 2} thin films decreases with Fe{sup 3+}-doping concentration increased. The PL intensity of all thin films also decreases with Fe{sup 3+}-doping concentration increased. When all various Fe{sup 3+}-doping TiO{sub 2} thin films after calcined at 823 K for 1 h, the photodegradation of each sample increases with irradiation time increased. Moreover, the photodegradation also increases with Fe{sup 3+}-doping concentration increased when fixed at constant irradiation time.

  12. Major enhancement of the thermoelectric performance in Pr/Nb-doped SrTiO3 under strain

    KAUST Repository

    Amin, B.

    2013-07-16

    The electronic structure and thermoelectric properties of strained (biaxially and uniaxially) Sr0.95Pr0.05TiO3 and SrTi0.95Nb0.05O3 are investigated in the temperature range from 300 K to 1200 K. Substitutions of Pr at the Sr site and Nb at the Ti site generate n-type doping and thus improve the thermoelectric performance as compared to pristine SrTiO3. Further enhancement is achieved by the application of strain, for example, of the Seebeck coefficient by 21% for Sr0.95Pr0.05TiO3 and 10% for SrTi0.95Nb0.05O3 at room temperature in the case of 5% biaxial strain. At 1200 K, we predict figures of merit of 0.58 and 0.55 for 2.5% biaxially strained Sr0.95Pr0.05TiO3 and SrTi0.95Nb0.05O3 , respectively, which are the highest values reported for rare earth doped SrTiO3.

  13. Light up conversion effects in Erbium doped CaBi4Ti4O15 ceramics

    International Nuclear Information System (INIS)

    Bokolia, Renuka; Sreenivas, K.

    2013-01-01

    In recent years the rare earth doped bismuth layered structured ferroelectric (BLSF) compositions such as CaBi 4 Ti 4 O 15 , SrBi 4 Ti 4 O 15 and BaBi 4 Ti 4 O 15 ceramics have shown interesting light up-conversion emission effects. The observation of such novel effects has generated a lot of scientific interest, and there is a need to further improve their dielectric, piezoelectric and light up-conversion properties. In the present study, Erbium doped CaBi 4 Ti 4 O 15 (CBT), and SrBi 4 Ti 4 O 15 (SBT) ferroelectric ceramic have been prepared by the conventional solid state reaction method. Formation of single phase material is confirmed by X-Ray Diffraction (XRD), and changes occurring in the lattice parameters with Erbium dopant are analysed. Room temperature dielectric studies and ferroelectric studies will be discussed. (author)

  14. Linear and nonlinear optical studies of bare and copper doped TiO2 nanoparticles via sol gel technique

    Science.gov (United States)

    Rajamannan, B.; Mugundan, S.; Viruthagiri, G.; Praveen, P.; Shanmugam, N.

    2014-01-01

    In general, the nanoparticles of TiO2 may exist in the phases of anatase, rutile and brookite. In the present work, we used titanium terta iso propoxide and 2-propanol as a common starting material to prepare the precursors of bare and copper doped nanosized TiO2. Then the synthesized products were calcinated at 500 °C and after calcination the pure TiO2 nanoparticles in anatase phase were harvested. The crystallite sizes of bare and copper doped TiO2 nanoparticles were calculated from X-ray diffraction analysis. The existence of functional groups of the samples was identified by Fourier transform infrared spectroscopy. The optical properties of bare and doped samples were carried out using UV-DRS and photoluminescence measurements. The surface morphology and the element constitution of the copper doped TiO2 nanoparticles were studied by scanning electron microscope fitted with energy dispersive X-ray spectrometer arrangement. The nonlinear optical properties of the products were confirmed by Kurtz second harmonic generation (SHG) test and the output power generated by the nanoparticle was compared with that of potassium di hydrogen phosphate (KDP).

  15. The Synthesis of Eu3+ Doped with TiO2 Nano-Powder and Application as a Pesticide Sensor

    International Nuclear Information System (INIS)

    Yao, Fei; Sun, Yang; Tan, Chunlei; Wei, Song; Zhang, Xiaojuan; Hu, Xiaoyun; Fan, Jun

    2011-01-01

    Using tetrabutyl titanate as precursor, Eu 3+ doped TiO 2 nano-powder was prepared by sol-gel method, the nature of luminescence of nano-powder was studied. The interaction of chlorpyrifos with Eu 3+ doped TiO 2 was studied by absorption and fluorescence spectroscopy. The results indicated the fluorescence intensity of Eu 3+ doped TiO 2 was quenched by chlorpyrifos and the quenching rate constant (kq) was 1.24Χ10 11 L/mol·s according to the Stern-Volmer equation. The dynamics of photoinduced electron transfer from chlorpyrifos to conduction band of TiO 2 nanoparticle was observed and the mechanism of electron transfer had been confirmed by the calculation of free energy change (ΔG et ) by applying Rehm-Weller equation as well as energy level diagram. A new rapid method for detection of chlorpyrifos was established according to the fluorescence intensity of Eu 3+ doped TiO 2 was proportional to chlorpyrifos concentration. The range of detection was 5.0Χ10 -10 -2.5Χ10 -7 mol/L and the detection limit (3σ) was 3.2Χ10 -11 mol/L

  16. Structural and electronic properties of Mg and Mg-Nb co-doped TiO2 (101) anatase surface

    Energy Technology Data Exchange (ETDEWEB)

    Sasani, Alireza [Department of Science, Karaj Islamic Azad University, Karaj, Alborz, P.O. Box 31485-313 (Iran, Islamic Republic of); Baktash, Ardeshir [Institute of Nano Science and Nano Technology, University of Kashan, Kashan, P.O. Box 87317-51167 (Iran, Islamic Republic of); Mirabbaszadeh, Kavoos, E-mail: mirabbas@aut.ac.ir [Department of Energy Engineering and Physics, Amirkabir University of Technology, Tehran, P. O. Box 15875-4413 (Iran, Islamic Republic of); Khoshnevisan, Bahram [Institute of Nano Science and Nano Technology, University of Kashan, Kashan, P.O. Box 87317-51167 (Iran, Islamic Republic of)

    2016-10-30

    Highlights: • Formation energy of Mg and Mg-Nb co-doped TiO{sub 2} anatase surface (101) is studied. • Effect of Mg defect to the TiO{sub 2} anatase (101) surface and bond length distribution of the surface is studied and it is shown that Mg defects tend to stay far from each other. • Effect of Mg and Nb to the bond length distribution of the surface studied and it is shown that these defects tend to stay close to each other. • Effects of Mg and Mg-Nb defects on DSSCs using TiO{sub 2} anatase hosting these defects are studied. - Abstract: In this paper, by using density functional theory, Mg and Nb-Mg co-doping of TiO{sub 2} anatase (101) surfaces are studied. By studying the formation energy of the defects and the bond length distribution of the surface, it is shown that Mg defects tend to stay as far as possible to induce least possible lattice distortion while Nb and Mg defects stay close to each other to cause less stress to the surface. By investigating band structure of the surface and changes stemmed from the defects, potential effects of Mg and Mg-Nb co-doping of TiO{sub 2} surface on dye-sensitized solar cells are investigated. In this study, it is shown that the Nb-Mg co-doping could increase J{sub SC} of the surface while slightly decreasing V{sub OC} compared to Mg doped surface, which might result in an increase in efficiency of the DSSCs compared to Nb or Mg doped surfaces.

  17. Combined sonochemical/CVD method for preparation of nanostructured carbon-doped TiO{sub 2} thin film

    Energy Technology Data Exchange (ETDEWEB)

    Rasoulnezhad, Hossein [Semiconductor Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of); Kavei, Ghassem, E-mail: kaveighassem@gmail.com [Semiconductor Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of); Ahmadi, Kamran [Semiconductor Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of); Rahimipour, Mohammad Reza [Ceramic Department, Materials and Energy Research Center (MERC), Karaj (Iran, Islamic Republic of)

    2017-06-30

    Highlights: • Combination of sonochemical and CVD methods for preparation of nanostructured carbon-doped TiO{sub 2} thin film on glass substrate, for the first time. • High transparency, monodispersity and homogeneity of the prepared thin films. • Preparation of the carbon-doped TiO{sub 2} thin films with nanorod and nanosphere morphologies. - Abstract: The present work reports the successful synthesis of the nanostructured carbon-doped TiO{sub 2} thin films on glass substrate by combination of chemical vapor deposition (CVD) and ultrasonic methods, for the first time. In this method the ultrasound waves act as nebulizer for converting of sonochemically prepared TiO{sub 2} sol to the mist particles. These mist particles were thermally decomposed in subsequent CVD chamber at 320 °C to produce the carbon-doped TiO{sub 2} thin films. The obtained thin films were characterized by means of X-ray Diffraction (XRD), Raman spectroscopy, diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and scanning electron microscopy (SEM) techniques. The results show that the prepared thin films have anatase crystal structure and nanorod morphology, which calcination of them at 800 °C results in the conversion of nanorods to nanoparticles. In addition, the prepared samples have high transparency, monodispersity and homogeneity. The presence of the carbon element in the structure of the thin films causes the narrowing of the band-gap energy of TiO{sub 2} to about 2.8 eV, which results in the improvement of visible light absorption capabilities of the thin film.

  18. Photo catalytic degradation of nitrobenzene using nanocrystalline TiO{sub 2} photo catalyst doped with Zn ions

    Energy Technology Data Exchange (ETDEWEB)

    Reynoso S, E. A.; Perez S, S.; Reyes C, A. P.; Castro R, C. L.; Felix N, R. M.; Lin H, S. W. [Instituto Tecnologico de Tijuana, Centro de Graduados e Investigacion, Apdo. Postal 1166, 22000 Tijuana, Baja California (Mexico); Paraguay D, F. [Centro de Investigacion en Materiales Avanzados, Apdo. Postal 311109, Chihuahua (Mexico); Alonso N, G. [UNAM, Centro de Nanociencias y Nanotecnologia, Carretera Tijuana-Ensenada Km 107, Apdo. Postal 356, 22800 Ensenada, Baja California (Mexico)

    2013-07-01

    Photo catalysis is a method widely used in the degradation of organic pollutants of the environment. The development of new materials is very important to improve the photo catalytic properties and to find new applications for TiO{sub 2} as a photo catalyst. In this article we reported the synthesis of a photo catalyst based on TiO{sub 2} doped with Zn{sup 2+} ions highly efficient in the degradation of nitrobenzene. The results of photo catalytic activity experiments showed that the Zn{sup 2+} doped TiO{sub 2} is more active that un-doped TiO{sub 2} catalyst with an efficiency of 99% for the nitrobenzene degradation at 120 min with an apparent rate constant of 35 x 10{sup -3} min{sup -1}. For the characterization of photo catalyst X-ray diffraction, transmission electron microscopy and Raman spectroscopy were used. (Author)

  19. Anatase phase stability and doping concentration dependent refractivity in codoped transparent conducting TiO2 films

    International Nuclear Information System (INIS)

    Chen, T L; Furubayashi, Y; Hirose, Y; Hitosugi, T; Shimada, T; Hasegawa, T

    2007-01-01

    Nb 0.06 Sn x Ti 0.94-x O 2 (x ≤ 0.3) thin films were grown by a pulsed-laser deposition method with varying Sn concentration. Through a combinatorial technique, we find that Sn concentration can reach a maximum of about x = 0.3 while maintaining the stable anatase phase and epitaxy. A doping concentration dependence of the refractivity is revealed, in which refractivity reduction at a wavelength of λ = 500 nm is estimated to be 12.4% for Nb 0.06 Sn 0.3 Ti 0.64 O 2 thin film. Sn doping induced band-gap blue shift can be contributed to the mixing of extended Sn 5s orbitals with the conduction band of TiO 2 . Low resistivity on the order of 10 -4 Ω cm at room temperature and high internal transmittance of more than 95% in the visible light region are exhibited for Nb 0.06 Sn x Ti 0.94-x O 2 thin films (x ≤ 0.2). Optical and transport analyses demonstrate that doping Sn into Nb 0.06 Ti 0.94 O 2 can reduce the refractivity while maintaining low resistivity and high transparency

  20. Dye-sensitized solar cells based on Cr-doped TiO2 nanotube photoanodes

    Institute of Scientific and Technical Information of China (English)

    M.M.Momeni

    2017-01-01

    The effect of chromium doping on the photovoltaic efficiency of dye-sensitized solar cells (DSSCs) with anodized TiO2 nanotubes followed by an annealing process was investigated.Cr-doped TiO2 nanotubes (CrTNs) with different amounts of chromium were obtained by anodizing of titanium foils in a single-step process using potassium chromate as the chromium source.Film features were investigated by scanning electron microscopy (SEM),X-ray diffraction (XRD),energy-dispersive X-ray spectroscopy (EDX),and ultraviolet-visible (UV-Vis) spectroscopy.It is clearly seen that highly ordered TiO2 nanotubes are formed in an anodizing solution free of potassium chromate,and with a gradual increase in the potassium chromate concentration,these nanotube structures change to nanoporous and compact films without porosity.The photovoltaic efficiencies of fabricated DSSCs were characterized by a solar cell measurement system via the photocurrent-voltage (Ⅰ-Ⅴ) curves.It is found that the photovoltaic efficiency of DSSCs with CrTNsl sample is improved by more than three times compared to that of DSSCs with undoped TNs.The energy conversion efficiency increases from 1.05 % to 3.89 % by doping of chromium.

  1. Facile synthesis and enhanced visible light photocatalytic activity of N and Zr co-doped TiO2 nanostructures from nanotubular titanic acid precursors

    Science.gov (United States)

    Zhang, Min; Yu, Xinluan; Lu, Dandan; Yang, Jianjun

    2013-12-01

    Zr/N co-doped TiO2 nanostructures were successfully synthesized using nanotubular titanic acid (NTA) as precursors by a facile wet chemical route and subsequent calcination. These Zr/N-doped TiO2 nanostructures made by NTA precursors show significantly enhanced visible light absorption and much higher photocatalytic performance than the Zr/N-doped P25 TiO2 nanoparticles. Impacts of Zr/N co-doping on the morphologies, optical properties, and photocatalytic activities of the NTA precursor-based TiO2 were thoroughly investigated. The origin of the enhanced visible light photocatalytic activity is discussed in detail.

  2. Preparation of Fe-doped TiO{sub 2} nanotube arrays and their photocatalytic activities under visible light

    Energy Technology Data Exchange (ETDEWEB)

    Tu, Ya-Fang; Huang, Sheng-You [Department of Physics, Wuhan University, Wuhan 430072 (China); Sang, Jian-Ping, E-mail: jpsang@acc-lab.whu.edu.cn [Department of Physics, Wuhan University, Wuhan 430072 (China); Department of Physics, Jianghan University, Wuhan 430056 (China); Zou, Xian-Wu [Department of Physics, Wuhan University, Wuhan 430072 (China)

    2010-02-15

    Fe-doped TiO{sub 2} nanotube arrays have been prepared by the template-based liquid phase deposition method. Their morphologies, structures and optical properties were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction and UV-vis absorption spectroscopy. Their photocatalytic activities were evaluated by the degradation of methylene blue under visible light. The UV-vis absorption spectra of the Fe-doped TiO{sub 2} nanotube arrays showed a red shift and an enhancement of the absorption in the visible region compared to the undoped sample. The Fe-doped TiO{sub 2} nanotube arrays exhibited good photocatalytic activities under visible light irradiation, and the optimum dopant amount was found to be 5.9 at% in our experiments.

  3. Synthesis and photocatalytic properties of Sn-doped TiO{sub 2} nanotube arrays

    Energy Technology Data Exchange (ETDEWEB)

    Tu Yafang; Huang Shengyou [Department of Physics, Wuhan University, Wuhan 430072 (China); Sang Jianping, E-mail: jpsang@acc-lab.whu.edu.c [Department of Physics, Wuhan University, Wuhan 430072 (China); Department of Physics, Jianghan University, Wuhan 430056 (China); Zou Xianwu [Department of Physics, Wuhan University, Wuhan 430072 (China)

    2009-08-12

    TiO{sub 2} nanotube arrays doped by Sn up to 12 at% have been prepared using template-based liquid phase deposition method. Their morphologies, structures and optical properties have been investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV-vis absorption spectroscopy and photoluminescence spectroscopy. The photocatalytic properties of the samples were evaluated with the degradation of methylene blue under UV irradiation. The result shows that doping an appropriate amount of Sn can effectively improve the photocatalytic activity of TiO{sub 2} nanotube arrays, and the optimum dopant amount is found to be 5.6 at% in our experiments.

  4. Synthesis of Zn-doped TiO{sub 2} microspheres with enhanced photovoltaic performance and application for dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Zhang Yu [State Key Laboratory of Theoretical and Computational Chemistry, College of Chemistry, Jilin University, Changchun 130023 (China); Wang Lingling [State Key Laboratory of Theoretical and Computational Chemistry, College of Chemistry, Jilin University, Changchun 130023 (China); State Key Laboratory of Supramolecular Structure and Materials, College of Chemistry, Jilin University, Changchun 130012 (China); Liu Bingkun; Zhai Jiali; Fan Haimei; Wang Dejun; Lin Yanhong [State Key Laboratory of Theoretical and Computational Chemistry, College of Chemistry, Jilin University, Changchun 130023 (China); Xie Tengfeng, E-mail: xietf@jlu.edu.cn [State Key Laboratory of Theoretical and Computational Chemistry, College of Chemistry, Jilin University, Changchun 130023 (China)

    2011-07-15

    Highlights: > Near-monodisperse Zn-doped TiO{sub 2} microspheres have been synthesized. > The photovoltaic properties of the samples were examined by SPS, FISPS and TPV measurements. > Surface photovoltage results revealed Zn doping can promote charge transfer in TiO{sub 2} film electrode. - Abstract: Zn-doped TiO{sub 2} microspheres have been synthesized by introducing a trace amount of zinc nitrate hexahydrate to the reaction system. Scanning electron microscope (SEM), field-emission scanning electron microscope (FESEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) have been utilized to characterize the samples. Both surface photovoltage spectroscopy (SPS) technique based on lock-in amplifier and transient photovoltage (TPV) measurement reveal that the slight doping of Zn can promote the separation of photo-generated charges as well as restrain the recombination due to the strong interface built-in electric field and the decreasing of surface trap states. The photovoltaic parameters of dye-sensitized solar cells (DSSCs) based on Zn-doped TiO{sub 2} are significantly better, compared to that of a cell based on undoped TiO{sub 2}. The relation between the performance of DSSCs and their photovoltaic properties is also discussed.

  5. The interplay between dopants and oxygen vacancies in the magnetism of V-doped TiO2

    KAUST Repository

    Grau-Crespo, Ricardo

    2011-08-03

    Density functional theory calculations indicate that the incorporation of V into Ti lattice positions of rutile TiO2 leads to magnetic V 4 + species, but the extension and sign of the coupling between dopant moments confirm that ferromagnetic order cannot be reached via low-concentration doping in the non-defective oxide. Oxygen vacancies can introduce additional magnetic centres, and we show here that one of the effects of vanadium doping is to reduce the formation energies of these defects. In the presence of both V dopants and O vacancies all the spins tend to align with the same orientation. We conclude that V doping favours the ferromagnetic behaviour of TiO2 not only by introducing spins associated with the dopant centres but also by increasing the concentration of oxygen vacancies with respect to the pure oxide. © 2001 IOP Publishing Ltd.

  6. The interplay between dopants and oxygen vacancies in the magnetism of V-doped TiO2

    KAUST Repository

    Grau-Crespo, Ricardo; Schwingenschlö gl, Udo

    2011-01-01

    Density functional theory calculations indicate that the incorporation of V into Ti lattice positions of rutile TiO2 leads to magnetic V 4 + species, but the extension and sign of the coupling between dopant moments confirm that ferromagnetic order cannot be reached via low-concentration doping in the non-defective oxide. Oxygen vacancies can introduce additional magnetic centres, and we show here that one of the effects of vanadium doping is to reduce the formation energies of these defects. In the presence of both V dopants and O vacancies all the spins tend to align with the same orientation. We conclude that V doping favours the ferromagnetic behaviour of TiO2 not only by introducing spins associated with the dopant centres but also by increasing the concentration of oxygen vacancies with respect to the pure oxide. © 2001 IOP Publishing Ltd.

  7. Degradation of selected industrial dyes using Mg-doped TiO2 polyscales under natural sun light as an alternative driving energy

    Science.gov (United States)

    Shivaraju, H. P.; Midhun, G.; Anil Kumar, K. M.; Pallavi, S.; Pallavi, N.; Behzad, Shahmoradi

    2017-11-01

    Designing photocatalytic materials with modified functionalities for the utilization of renewable energy sources as an alternative driving energy has attracted much attention in the area of sustainable wastewater treatment applications. Catalyst-assisted advanced oxidation process is an emerging treatment technology for organic pollutants and toxicants in industrial wastewater. Preparation of visible-light-responsive photocatalyst such as Mg-doped TiO2 polyscales was carried out under mild sol-gel technique. Mg-doped TiO2 polyscales were characterized by powder XRD, SEM, FTIR, and optical and photocatalytic activity techniques. The Mg-doped TiO2 showed a mixed phase of anatase and rutile with an excellent crystallinity, structural elucidations, polyscales morphology, consequent shifting of bandgap energy and adequate photocatalytic activities under visible range of light. Mg-doped TiO2 polyscales were investigated for their efficiencies in the degradation of most commonly used industrial dyes in the real-time textile wastewater. Mg-doped TiO2 polyscales showed excellent photocatalytic degradation efficiency in both model industrial dyes (65-95%) and textile wastewater (92%) under natural sunlight as an alternative and renewable driving energy.

  8. Electrical properties of niobium doped Bi4Ti3O12-SrBi4Ti4O15 intergrowth ferroelectrics

    International Nuclear Information System (INIS)

    Parida, Geetanjali; Bera, J.

    2013-01-01

    Bismuth layer structured ferroelectrics (BLSFs) have attracted much attention because of their potential applications in non-volatile ferroelectric random access memories and high temperature piezoelectric. They are very attractive for these applications due to their fatigue free nature and environment friendly lead-free composition. BLSF crystal structure has layers of bismuth oxide and pseudo perovskite block stacked alternately along their c-direction, For commercial application, numerous efforts have been made to improve the electrical properties of BLSFs. Some effective approaches are: (i) doping at A-site, (ii) high valentcation doping at B-site and (iii) formation of intergrowth between different BLSFs. The intergrowth BLSFs are consist of regular stacking of one half the unit cell of m-member structure and one half the unit cell of (m+1) member BLSF structure along their c-axis. In this report, Nb-doped Bi 4 Ti 3 O 12 -SrBi 4 Ti 4 O 15 intergrowth ceramics have been prepared by modified oxalate route. XRD phase analysis confirmed the formation of single phase compound. Nb-doping does not affect the basic crystal structure of the intergrowth. SEM micrographs showed that the grain size of the ceramics decreases with Nb-doping. The temperature dependence of dielectric constant and losses was investigated in the temperature range 30 to 800℃ and frequency range 1 kHz to 1 MHz. With Nb-doping, the T c of the ferroelectrics reduces and peak permittivity increases. Doping also introduces small relaxor behaviour in the ferroelectrics. The dc conductivity of the ceramics decreases with doping. The remnant polarization (Pr) of the intergrowth ferroelectrics is increased with Nb doping. (author)

  9. Origin of the Enhanced Visible-Light Absorption in N-Doped Bulk Anatase TiO 2 from First-Principles Calculations

    KAUST Repository

    Harb, Moussab

    2011-10-06

    Extension of the absorption properties of TiO2 photocatalytic materials to the visible part of the solar spectrum is of major importance for energy and cleaning up applications. We carry out a systematic study of the N-doped anatase TiO2 material using spin-polarized density functional theory (DFT) and the range-separated hybrid HSE06 functional. The thermodynamic stability of competitive N-doped TiO2 structural configurations is studied as a function of the oxygen chemical potential and of various chemical doping agents: N2, (N2 + H2), NH3, N2H4. We show that the diamagnetic TiO (2-3x)N2x system corresponding to a separated substitutional N species (with 2-4% N impurities) and formation of one-half concentration of O vacancies (1-2 atom %) is an optimal configuration thermodynamically favored by NH3, N2H4, and (N2 + H2) chemical doping agents presenting a dual nitrating-reducing character. The simulated UV-vis absorption spectra using the perturbation theory (DFPT) approach demonstrates unambiguously that the diamagnetic TiO(2-3x)N2x system exhibits the enhanced optical absorption in N-doped TiO2 under visible-light irradiation. Electronic analysis further reveals a band gap narrowing of 0.6 eV induced by delocalized impurity states located at the top of the valence band of TiO 2. A fruitful comparison with experimental data is furnished. © 2011 American Chemical Society.

  10. Magnetic and ferroelectric properties of Fe doped SrTiO{sub 3-{delta}} films

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, A Sendil; Suresh, P; Srinath, S [School of Physics, University of Hyderabad, Hyderabad, 500 046 (India); Kumar, M Mahesh; Post, M L [Institute for Chemical Process and Environmental Technology, National Research Council of Canada, Ottawa, ON, K1A 0R6 (Canada); Srikanth, H [Materials Physics Laboratory, Department of Physics, University of South Florida, Tampa, Florida, 33620 (United States); Sahner, Kathy; Moos, Ralf, E-mail: sssp@uohyd.ernet.i [Functional Materials, University of Bayreuth, 95447, Bayreuth (Germany)

    2010-01-01

    Recent interest in SrTiO{sub 3} stems from its wide applicability in microwave devices based on the tunable characteristics of dielectric constant in the microwave frequency range. It is obvious that for any such application, SrTiO{sub 3} should have a ferroelectric Curie temperature (T{sub C}) close to room temperature or higher. By inducing strains by chemical substitutions, it was possible to obtain T{sub C} as high as 200{sup 0}C in SrTiO{sub 3} modified with Fe{sup 4+}. Hysteresis loops obtained confirms the presence of ferroelectric domains. Two apparent transitions, one at {approx}200 {sup 0}C and another {approx}300 {sup 0}C were seen in {epsilon}', which are replicated as sharp drops in resistivity curves. These temperatures far exceed the T{sub C}s reported in the literature till now and could open new avenues for innumerable other applications for SrTiO{sub 3}. The magnetic properties of Fe doped SrTiO{sub 3} are also investigated. Low doping of Fe exhibits simple antiferromagnetic behaviour.

  11. Nanoscale Optimization and Statistical Modeling of Photoelectrochemical Water Splitting Efficiency of N-Doped TiO2 Nanotubes

    KAUST Repository

    Isimjan, Tayirjan T.

    2014-12-19

    Highly ordered nitrogen-doped titanium dioxide (N-doped TiO2) nanotube array films with enhanced photo-electrochemical water splitting efficiency (PCE) for hydrogen generation were fabricated by electrochemical anodization, followed by annealing in a nitrogen atmosphere. Morphology, structure and composition of the N-doped TiO2 nanotube array films were investigated by FE-SEM, XPS, UV-Vis and XRD. The effect of annealing temperature, heating rate and annealing time on the morphology, structure, and photo-electrochemical property of the N-doped TiO2 nanotube array films were investigated. A design of experiments method was applied in order to minimize the number of experiments and obtain a statistical model for this system. From the modelling results, optimum values for the influential factors were obtained in order to achieve the maximum PCE. The optimized experiment resulted in 7.42 % PCE which was within 95 % confidence interval of the predicted value by the model. © 2014 Springer Science+Business Media.

  12. Effect of In-Doping on Electronic Structure and Optical Properties of Sr2TiO4

    International Nuclear Information System (INIS)

    Jiang-Ni, Yun; Zhi-Yong, Zhang; Jun-Feng, Yan; Fu-Chun, Zhang

    2009-01-01

    The effect of In doping on the electronic structure and optical properties of Sr 2 TiO 4 is investigated by a first-principles calculation of plane wave ultrasoft pseudopotentials based on density functional theory. The calculated results reveal that corner-shared TiO 6 octahedra dominate the main electronic properties of Sr 2 TiO 4 and the covalency of the Ti–O(1) bond in the ab plane is stronger than that of the Ti–O(2) bond along the c-axis. After In doping, there is a little lattice expansion in Sr 2 In 0.125 Ti 0.875 O 4 , and the interaction between the Ti–O bond near the impurity In atom is weakened. The binding energies of Sr 2 TiO 4 and Sr 2 In 0.125 Ti 0.875 O 4 , estimated from the electronic structure calculations indicate that the crystal structure of Sr 2 In 0.125 Ti 0.875 O 4 is still stable after doping, but its stability is lower than that of undoped Sr 2 TiO 4 . Moreover, the valence bands (VBs) of the Sr 2 In 0.125 Ti 0.875 O 4 , system consist of O 2p and In 4d states, and the mixing of O 2p and In 4d states makes the top VBs shift significantly to high energies, resulting in visible light absorption. The adsorption of visible light is of practical importance for the application of Sr 2 TiO 4 as a photocatalyst. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  13. Performance of Erbium-doped TiO2 thin film grown by physical vapor deposition technique

    Science.gov (United States)

    Lahiri, Rini; Ghosh, Anupam; Dwivedi, Shyam Murli Manohar Dhar; Chakrabartty, Shubhro; Chinnamuthu, P.; Mondal, Aniruddha

    2017-09-01

    Undoped and Erbium-doped TiO2 thin films (Er:TiO2 TFs) were fabricated on the n-type Si substrate using physical vapour deposition technique. Field emission scanning electron microscope showed the morphological change in the structure of Er:TiO2 TF as compared to undoped sample. Energy dispersive X-ray spectroscopy (EDX) confirmed the Er doping in the TiO2 thin film (TF). The XRD and Raman spectrum showed the presence of anatase phase TiO2 and Er2O3 in the Er:TiO2 TF. The Raman scattering depicted additional number of vibrational modes for Er:TiO2 TF due to the presence of Er as compared to the undoped TiO2 TF. The UV-Vis absorption measurement showed that Er:TiO2 TF had approximately 1.2 times more absorption over the undoped TiO2 TF in the range of 300-400 nm. The main band transition, i.e., the transition between the oxygen (2p) state and the Ti (3d) state was obtained at 3.0 eV for undoped TiO2 and at 3.2 eV for Er:TiO2 TF, respectively. The photo responsivity measurement was done on both the detectors, where Er:TiO2 TF detector showed better detectivity ( D *), noise equivalent power and temporal response as compared to undoped detector under ultra-violet illumination.

  14. Photocatalytic behaviors and structural characterization of nanocrystalline Fe-doped TiO2 synthesized by mechanical alloying

    International Nuclear Information System (INIS)

    Kim, Dong Hyun; Hong, Hyun Seon; Kim, Sun Jae; Song, Jae Sung; Lee, Kyung Sub

    2004-01-01

    Nanocrystalline Fe-doped TiO 2 powders were synthesized by mechanical alloying (MA) with varying Fe contents from 0 up to 4.8 wt.% to shift the absorption threshold into the visible light region. The photocatalytic feasibility of the Fe-doped TiO 2 powder was evaluated by quantifying the visible light absorption capacity using ultraviolet and visible (UV-Vis) spectroscopy and photoluminescence spectroscopy. Effects of Fe additions on the crystal structures and the morphologies of the Fe-doped powders were also investigated as a function of the doping content using transmission electron microscopy-electron diffraction pattern (TEM-EDP), X-ray diffraction (XRD) and energy dispersive X-ray (EDAX) and X-ray photoelectron spectroscopy (XPS). The UV-Vis study showed that the UV absorption for the Fe-doped powder moved to a longer wavelength (red shift) and the photoefficiency was enhanced. Based on the analysis of the photoluminescence spectra, the red shift was believed to be induced by localizing the dopant level near the valence band of TiO 2 . The UV-Vis absorption depended on the Fe concentration. TEM-EDP and XRD investigations showed that the Fe-doped powder had a rutile phase in which the added Fe atoms were dissolved. The rutile phase was composed of spherical particles and chestnut bur shaped particles, resulting in a larger surface area than the spherical P-25 powder

  15. Improvement of thermal shock resistance of isotropic graphite by ti-doping

    International Nuclear Information System (INIS)

    Lopez-Galilea, I.; Ordas, N.; Garcia-Rosales, C.; Lindig, S.

    2007-01-01

    Full text of publication follows: Carbon fiber reinforced carbon (CFC) is the present candidate material for the strike point area of the ITER divertor due to its ability to withstand excessive heat loads during ELMs and plasma disruptions. However, chemical erosion of carbon under hydrogen bombardment from the plasma involves serious disadvantages for this application (replacement and safety problems due to tritium co-deposition). In addition, the manufacturing process of present CFC candidate materials is long and complex resulting in high costs, and CFC materials are inherently anisotropic. Doping of carbon with small amounts (several at. %) of titanium has proved to be effective in reducing chemical erosion while maintaining or even improving the mechanical properties. furthermore, TiC as dopant contributes to increase significantly the thermal conductivity and consequently the thermal shock resistance, due to the catalytic effect of this carbide on the graphitization. The aim of this work is to improve substantially the thermal shock resistance of fine-grained isotropic graphite by doping it with small amounts of TiC, reducing at the same time the chemical erosion. By this way Ti-doped graphites could be competitive with present CFC candidate materials for next step fusion devices. To achieve this, a synthetic naphthalene-derived mesophase pitch named AR is used as carbon precursor; this raw material exhibits excellent graphitizability, high chemical purity and consistent quality. Due to the low viscosity at the softening point of AR, resulting in swelling during the carbonization treatment, it is necessary to modify the initial viscosity of AR by an adequate oxidative stabilization treatment. As dopant, TiC powder with 130 nm average particle size is added. The influence of several manufacturing parameters such as oxidative stabilization treatment, carbonization cycle, graphitization temperature and dwell time during graphitization have been investigated in

  16. Improvement of thermal shock resistance of isotropic graphite by ti-doping

    Energy Technology Data Exchange (ETDEWEB)

    Lopez-Galilea, I.; Ordas, N.; Garcia-Rosales, C. [Navarrra Univ., CEPT, San Sebastian (Spain); Lindig, S. [Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, Garching (Germany)

    2007-07-01

    Full text of publication follows: Carbon fiber reinforced carbon (CFC) is the present candidate material for the strike point area of the ITER divertor due to its ability to withstand excessive heat loads during ELMs and plasma disruptions. However, chemical erosion of carbon under hydrogen bombardment from the plasma involves serious disadvantages for this application (replacement and safety problems due to tritium co-deposition). In addition, the manufacturing process of present CFC candidate materials is long and complex resulting in high costs, and CFC materials are inherently anisotropic. Doping of carbon with small amounts (several at. %) of titanium has proved to be effective in reducing chemical erosion while maintaining or even improving the mechanical properties. furthermore, TiC as dopant contributes to increase significantly the thermal conductivity and consequently the thermal shock resistance, due to the catalytic effect of this carbide on the graphitization. The aim of this work is to improve substantially the thermal shock resistance of fine-grained isotropic graphite by doping it with small amounts of TiC, reducing at the same time the chemical erosion. By this way Ti-doped graphites could be competitive with present CFC candidate materials for next step fusion devices. To achieve this, a synthetic naphthalene-derived mesophase pitch named AR is used as carbon precursor; this raw material exhibits excellent graphitizability, high chemical purity and consistent quality. Due to the low viscosity at the softening point of AR, resulting in swelling during the carbonization treatment, it is necessary to modify the initial viscosity of AR by an adequate oxidative stabilization treatment. As dopant, TiC powder with 130 nm average particle size is added. The influence of several manufacturing parameters such as oxidative stabilization treatment, carbonization cycle, graphitization temperature and dwell time during graphitization have been investigated in

  17. Improved conversion efficiency of dye sensitized solar cell using Zn doped TiO_2-ZrO_2 nanocomposite

    International Nuclear Information System (INIS)

    Tomar, Laxmi J.; Bhatt, Piyush J.; Desai, Rahul K.; Chakrabarty, B. S.; Panchal, C. J.

    2016-01-01

    TiO_2-ZrO_2 and Zn doped TiO_2-ZrO_2 nanocomposites were prepared by hydrothermal method for dye sensitized solar cell (DSSC) application. The structural and optical properties were investigated by X –ray diffraction (XRD) and UV-Visible spectroscopy respectively. XRD results revealed the formation of material in nano size. The average crystallite size is 22.32 nm, 17.41 nm and 6.31 nm for TiO_2, TiO_2-ZrO_2 and Zn doped TiO_2-ZrO_2 nanocomposites respectively. The optical bandgap varies from 2.04 eV to 3.75 eV. Dye sensitized solar cells were fabricated using the prepared material. Pomegranate juice was used as a sensitizer and graphite coated conducting glass plate was used as counter electrode. The I – V characteristics were recorded to measure photo response of DSSC. Photovoltaic parameter like open circuit voltage, power conversion efficiency, and fill factor were evaluated for fabricated solar cell. The power conversion efficiency of DSSC fabricated with TiO_2, TiO_2-ZrO_2 and Zn doped TiO_2-ZrO_2 nanocomposites were found 0.71%, 1.97% and 4.58% respectively.

  18. Improved conversion efficiency of dye sensitized solar cell using Zn doped TiO2-ZrO2 nanocomposite

    Science.gov (United States)

    Tomar, Laxmi J.; Bhatt, Piyush J.; Desai, Rahul K.; Chakrabarty, B. S.; Panchal, C. J.

    2016-05-01

    TiO2-ZrO2 and Zn doped TiO2-ZrO2 nanocomposites were prepared by hydrothermal method for dye sensitized solar cell (DSSC) application. The structural and optical properties were investigated by X -ray diffraction (XRD) and UV-Visible spectroscopy respectively. XRD results revealed the formation of material in nano size. The average crystallite size is 22.32 nm, 17.41 nm and 6.31 nm for TiO2, TiO2-ZrO2 and Zn doped TiO2-ZrO2 nanocomposites respectively. The optical bandgap varies from 2.04 eV to 3.75 eV. Dye sensitized solar cells were fabricated using the prepared material. Pomegranate juice was used as a sensitizer and graphite coated conducting glass plate was used as counter electrode. The I - V characteristics were recorded to measure photo response of DSSC. Photovoltaic parameter like open circuit voltage, power conversion efficiency, and fill factor were evaluated for fabricated solar cell. The power conversion efficiency of DSSC fabricated with TiO2, TiO2-ZrO2 and Zn doped TiO2-ZrO2 nanocomposites were found 0.71%, 1.97% and 4.58% respectively.

  19. High-performance and renewable supercapacitors based on TiO2 nanotube array electrodes treated by an electrochemical doping approach

    International Nuclear Information System (INIS)

    Wu, Hui; Li, Dongdong; Zhu, Xufei; Yang, Chunyan; Liu, Dongfang; Chen, Xiaoyuan; Song, Ye; Lu, Linfeng

    2014-01-01

    Although one-dimensional anodic TiO 2 nanotube arrays have shown promise as supercapacitor electrode materials, their poor electronic conductivity embarrasses the practical applications. Here, we develop a simple electrochemical doping method to significantly improve the electronic conductivity and the electrochemical performances of TiO 2 nanotube electrodes. These TiO 2 nanotube electrodes treated by the electrochemical hydrogenation doping (TiO 2 -H) exhibit a very high average specific capacitance of 20.08 mF cm −2 at a current density of 0.05 mA cm −2 , ∼20 times more than the pristine TiO 2 nanotube electrodes. The improved electrochemical performances can be attributed to ultrahigh conductivity of TiO 2 -H due to the introduction of interstitial hydrogen ions and oxygen vacancies by the doping. The supercapacitor device assembled by the doped electrodes delivers a specific capacitance of 5.42 mF cm −2 and power density of 27.66 mW cm −2 , on average, at the current density of 0.05 mA cm −2 . The device also shows an outstanding rate capability with 60% specific capacitance retained when the current density increases from 0.05 to 4.00 mA cm −2 . More interestingly, the electrochemical performances of the supercapacitor after cycling can be recovered by the same doping process. This strategy boosts the performances of the supercapacitor, especially cycling stability

  20. Nitrogen induced ferromagnetism in Cobalt doped BaTiO3

    Directory of Open Access Journals (Sweden)

    Chandrima Mitra

    2012-09-01

    Full Text Available The electronic structure and magnetism of Cobalt doped BaTiO3 (BaTi1−xCoxO3 is investigated. Substitutional Nitrogen on an Oxygen site is found to play an important role in inducing net magnetic moments in the system. The presence of a Nitrogen atom as nearest neighbour to a Cobalt atom is crucial in producing spin splitting of both the Nitrogen and Cobalt states thereby introducing a net local magnetic moment. The introduction of Nitrogen is further found to enhance ferromagnetic interactions between Cobalt atoms.

  1. Mechanical Properties and Electronic Structure of N and Ta Doped TiC: A First-Principles Study

    International Nuclear Information System (INIS)

    Ma Shi-Qing; Liu Ying; Ye Jin-Wen; Wang Bin

    2014-01-01

    The first principles calculations based on density functional theory (DFT) are employed to investigate the mechanical properties and electronic structure of N and Ta doped TiC. The result shows that the co-doping of nitrogen and tantalum dilates the lattice constant and improves the stability of TiC. Nitrogen and tantalum can signiβcantly enhance the elastic constants and elastic moduli of TiC. The results of B/G and C 12 –C 44 indicate tantalum can markedly increase the ductility of TiC. The electronic structure is calculated to describe the bonding characteristic, which revealed the strong hybridization between C-p and Ta-d and between N-p and Ti-d. The hardnessis is estimated by a semi-empirical model that is based on the Mulliken overlap population and bond length. While the weakest bond takes determinative role of the hardness of materials, the addition of Ta sharply reduces the hardness of TiC. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  2. Low-cost fabrication of highly sensitive room temperature hydrogen sensor based on ordered mesoporous Co-doped TiO2 structure

    Science.gov (United States)

    Li, Zhong; Haidry, Azhar Ali; Wang, Tao; Yao, Zheng Jun

    2017-07-01

    The development of cost-effective gas sensors with improved sensing properties and minimum power consumption for room temperature hydrogen leakage monitoring is in increasing demand. In this context, this report focus on the facile fabrication of ordered mesoporous TiO2 via evaporation-induced self-assembly route. With the controlled doping threshold (3%Co-TiO2), the output resistance change to 1000 ppm H2 is ˜4.1 × 103 with the response time of 66 s. The sensor response exhibits power law dependence with an increase in the hydrogen concentration, where the power law coefficient was found not only specific to the kind of target gas but also related to temperature. Further, the effect of structure integrity with doping level and humidity on sensing characteristics is interpreted in terms of variation in surface potential eVS and depletion region w caused by the adsorption of molecular oxygen O2-.

  3. N, S co-doped-TiO{sub 2}/fly ash beads composite material and visible light photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Lv, Jun, E-mail: lvjun117@126.com; Sheng, Tong; Su, Lili; Xu, Guangqing; Wang, Dongmei; Zheng, Zhixiang; Wu, Yucheng, E-mail: ycwu@hfut.edu.cn

    2013-11-01

    Using TiCl{sub 4} as the titanium source, urea as the precipitating agent, nano-TiO{sub 2}/fly ash beads composite materials were prepared by hydrolysis-precipitation method. Using (NH{sub 2}){sub 2}CO and (NH{sub 2}){sub 2}SC as the N and S source respectively, N and S co-doped TiO{sub 2}/fly ash beads composite materials were prepared by grinding them together according to a certain proportion and calcined at 500 °C for 2 h. The composite materials were characterized by SEM, EDS, XPS, and UV–vis spectrophotometer methods. The UV–vis absorption spectra results show that the absorption edge of un-doped composites is 390 nm while that of doped composites red-shifts to 500 nm. The photocatalytic activity of composite materials was evaluated by degradation of methyl orange under visible light irradiation (halogen lamp, 250 W). The results showed that after irradiation for 1 h, degradation rate of N, S co-doped-TiO{sub 2}/fly ash beads composite material can reach 65%, while the degradation rate of un-doped sample and P25 were just 10% and 6%, respectively. The composite material also showed excellent recycling properties.

  4. Strain induced atomic structure at the Ir-doped LaAlO3/SrTiO3 interface.

    Science.gov (United States)

    Lee, M; Arras, R; Warot-Fonrose, B; Hungria, T; Lippmaa, M; Daimon, H; Casanove, M J

    2017-11-01

    The structure of Ir-doped LaAlO 3 /SrTiO 3 (001) interfaces was investigated on the atomic scale using probe-corrected transmission electron microscopy in high-angle annular dark-field scanning mode (HAADF-STEM) and electron energy loss spectroscopy (EELS), combined with first-principles calculations. We report the evolution of the strain state experimentally measured in a 5 unit-cell thick LaAlO 3 film as a function of the Ir concentration in the topmost SrTiO 3 layer. It is shown that the LaAlO 3 layers remain fully elastically strained up to 3% of Ir doping, whereas a higher doping level seems to promote strain relaxation through enhanced cationic interdiffusion. The observed differences between the energy loss near edge structure (ELNES) of Ti-L 2,3 and O-K edges at non-doped and Ir-doped interfaces are consistent with the location of the Ir dopants at the interface, up to 3% of Ir doping. These findings, supported by the results of density functional theory (DFT) calculations, provide strong evidence that the effect of dopant concentrations on the properties of this kind of interface should not be analyzed without obtaining essential information from the fine structural and chemical analysis of the grown structures.

  5. Fabrication of predominantly Mn4+ -doped TiO2 nanoparticles under equilibrium conditions and their application as visible-light photocatalyts.

    Science.gov (United States)

    Wang, Lijie; Fan, Jiajie; Cao, Zetan; Zheng, Yichao; Yao, Zhiqiang; Shao, Guosheng; Hu, Junhua

    2014-07-01

    The chemical state of a transition-metal dopant in TiO(2) can intrinsically determine the performance of the doped material in applications such as photocatalysis and photovoltaics. In this study, manganese-doped TiO2 is fabricated by a near-equilibrium process, in which the TiO(2) precursor powder precipitates from a hydrothermally obtained transparent mother solution. The doping level and subsequent thermal treatment influence the morphology and crystallization of the TiO(2) samples. FTIR spectroscopy and X-ray photoelectron spectroscopy analyses indicate that the manganese dopant is substitutionally incorporated by replacing Ti(4+) cations. The absorption band edge can be gradually shifted to 1.8 eV by increasing the nominal manganese content to 10 at %. Manganese atoms doped into the titanium lattice are associated with the dominant 4+ valence oxidation state, which introduces two curved, intermediate bands within the band gap and results in a significant enhancement in photoabsorption and the quantity of photogenerated hydroxyl radicals. Additionally, the high photocatalytic performance of manganese-doped TiO(2) is also attributed to the low oxygen content, owing to the equilibrium fabrication conditions. This work provides an important strategy to control the chemical and defect states of dopants by using an equilibrium fabrication process. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  6. The investigation of photo-induced chemiluminescence on Co2+-doped TiO2 nanoparticles and its analytical application.

    Science.gov (United States)

    Li, Guixin; Nan, Hongyan; Zheng, Xingwang

    2009-07-01

    A novel space- and time-resolved photo-induced chemiluminescence (PICL) analytical method was developed based on the photocatalysis of the Co2+-doped TiO2 nanoparticles. The PICL reaction procedure under the photocatalysis of Co2+-doped TiO2 nanoparticles was investigated using cyclic voltammetry and potentiometry. Meanwhile, the effect of the electrical double layer outside the Co2+-doped TiO2 nanoparticles on the PICL was investigated by contrasting with the Co2+-doped TiO2-SiO2 core-shell nanoparticles. Significantly, the CL intensity increased apparently and the time of the CL was prolonged in the presence of procaterol hydrochloride because the mechanism of the enhanced PICL reaction may be modified. The route of the PICL was changed due to the participation of the procaterol hydrochloride enriched at the surface of the Co2+-doped TiO2-SiO2 in the PICL reaction, which prolonged the time of the CL reaction and resulted in the long-term PICL. The analytical characteristics of the proposed in-situ PICL method were investigated using the procaterol hydrochloride as the model analyte. The investigation results showed that this new PICL analytical method offered higher sensitivity to the analysis of the procaterol hydrochloride and the PICL intensity was linear with the concentration of the procaterol hydrochloride in the range from ca. 2.0 x 10(-10) to 1.0 x 10(-8) g mL(-1).

  7. Enhanced carrier density in Nb-doped SrTiO3 thermoelectrics

    KAUST Repository

    Ozdogan, K.

    2012-03-08

    We study epitaxial SrTiO3 interfaced with Nb-doped SrTi1-x Nb x O3 (x = 0, 0.125, 0.25, 0.375, and 0.5) by full-potential density functional theory. From the electronic band structures obtained by our ab-initio calculations we determine the dependence of the induced metallicity on the Nb concentration. We obtain a monotonous increase of the carrier density with the Nb concentration. The results are confirmed by experiments for SrTi0.88Nb0.12O3 and SrTi0.8Nb0.2O3, demonstrating the predictive power and limitations of our theoretical approach. We also show that the Seebeck coefficient decreases monotonously with increasing temperature.

  8. Enhanced carrier density in Nb-doped SrTiO3 thermoelectrics

    KAUST Repository

    Ozdogan, K.; Upadhyay Kahaly, M.; Sarath Kumar, S. R.; Alshareef, Husam N.; Schwingenschlö gl, Udo

    2012-01-01

    We study epitaxial SrTiO3 interfaced with Nb-doped SrTi1-x Nb x O3 (x = 0, 0.125, 0.25, 0.375, and 0.5) by full-potential density functional theory. From the electronic band structures obtained by our ab-initio calculations we determine the dependence of the induced metallicity on the Nb concentration. We obtain a monotonous increase of the carrier density with the Nb concentration. The results are confirmed by experiments for SrTi0.88Nb0.12O3 and SrTi0.8Nb0.2O3, demonstrating the predictive power and limitations of our theoretical approach. We also show that the Seebeck coefficient decreases monotonously with increasing temperature.

  9. Structural Modification of Sol-Gel Synthesized V2O5 and TiO2 Thin Films with/without Erbium Doping

    Directory of Open Access Journals (Sweden)

    Fatma Pınar Gökdemir

    2014-01-01

    Full Text Available Comparative work of with/without erbium- (Er- doped vanadium pentoxide (V2O5 and titanium dioxide (TiO2 thin films were carried out via sol-gel technique by dissolving erbium (III nitrate pentahydrate (Er(NO33·5H2O in vanadium (V oxoisopropoxide (OV[OCH(CH32]3 and titanium (IV isopropoxide (Ti[OCH(CH32]4. Effect of Er doping was traced by Fourier transform IR (FTIR, thermogravimetric/differential thermal (TG/DTA, and photoluminescence measurements. UV-Vis transmission/absorption measurement indicated a blue shift upon Er doping in V2O5 film due to the softening of V=O bond while appearance of typical absorption peaks in Er-doped TiO2 film. Granule size of the films increased (reduced upon Er substitution on host material compared to undoped V2O5 and TiO2 films, respectively.

  10. Preparation of Ce- and La-Doped Li4Ti5O12 Nanosheets and Their Electrochemical Performance in Li Half Cell and Li4Ti5O12/LiFePO4 Full Cell Batteries

    Directory of Open Access Journals (Sweden)

    Meng Qin

    2017-06-01

    Full Text Available This work reports on the synthesis of rare earth-doped Li4Ti5O12 nanosheets with high electrochemical performance as anode material both in Li half and Li4Ti5O12/LiFePO4 full cell batteries. Through the combination of decreasing the particle size and doping by rare earth atoms (Ce and La, Ce and La doped Li4Ti5O12 nanosheets show the excellent electrochemical performance in terms of high specific capacity, good cycling stability and excellent rate performance in half cells. Notably, the Ce-doped Li4Ti5O12 shows good electrochemical performance as anode in a full cell which LiFePO4 was used as cathode. The superior electrochemical performance can be attributed to doping as well as the nanosized particle, which facilitates transportation of the lithium ion and electron transportation. This research shows that the rare earth doped Li4Ti5O12 nanosheets can be suitable as a high rate performance anode material in lithium-ion batteries.

  11. Preparation of Ce- and La-Doped Li4Ti5O12 Nanosheets and Their Electrochemical Performance in Li Half Cell and Li4Ti5O12/LiFePO4 Full Cell Batteries

    Science.gov (United States)

    Qin, Meng; Li, Yueming; Lv, Xiao-Jun

    2017-01-01

    This work reports on the synthesis of rare earth-doped Li4Ti5O12 nanosheets with high electrochemical performance as anode material both in Li half and Li4Ti5O12/LiFePO4 full cell batteries. Through the combination of decreasing the particle size and doping by rare earth atoms (Ce and La), Ce and La doped Li4Ti5O12 nanosheets show the excellent electrochemical performance in terms of high specific capacity, good cycling stability and excellent rate performance in half cells. Notably, the Ce-doped Li4Ti5O12 shows good electrochemical performance as anode in a full cell which LiFePO4 was used as cathode. The superior electrochemical performance can be attributed to doping as well as the nanosized particle, which facilitates transportation of the lithium ion and electron transportation. This research shows that the rare earth doped Li4Ti5O12 nanosheets can be suitable as a high rate performance anode material in lithium-ion batteries. PMID:28632167

  12. Enhanced Charge Extraction of Li-Doped TiO2 for Efficient Thermal-Evaporated Sb2S3 Thin Film Solar Cells

    Science.gov (United States)

    Lan, Chunfeng; Luo, Jingting; Lan, Huabin; Fan, Bo; Peng, Huanxin; Zhao, Jun; Sun, Huibin; Zheng, Zhuanghao; Liang, Guangxing; Fan, Ping

    2018-01-01

    We provided a new method to improve the efficiency of Sb2S3 thin film solar cells. The TiO2 electron transport layers were doped by lithium to improve their charge extraction properties for the thermal-evaporated Sb2S3 solar cells. The Mott-Schottky curves suggested a change of energy band and faster charge transport in the Li-doped TiO2 films. Compared with the undoped TiO2, Li-doped mesoporous TiO2 dramatically improved the photo-voltaic performance of the thermal-evaporated Sb2S3 thin film solar cells, with the average power conversion efficiency (PCE) increasing from 1.79% to 4.03%, as well as the improved open-voltage (Voc), short-circuit current (Jsc) and fill factors. The best device based on Li-doped TiO2 achieved a power conversion efficiency up to 4.42% as well as a Voc of 0.645 V, which are the highest values among the reported thermal-evaporated Sb2S3 solar cells. This study showed that Li-doping on TiO2 can effectively enhance the charge extraction properties of electron transport layers, offering a new strategy to improve the efficiency of Sb2S3-based solar cells. PMID:29495612

  13. Enhanced Charge Extraction of Li-Doped TiO2 for Efficient Thermal-Evaporated Sb2S3 Thin Film Solar Cells

    Directory of Open Access Journals (Sweden)

    Chunfeng Lan

    2018-02-01

    Full Text Available We provided a new method to improve the efficiency of Sb2S3 thin film solar cells. The TiO2 electron transport layers were doped by lithium to improve their charge extraction properties for the thermal-evaporated Sb2S3 solar cells. The Mott-Schottky curves suggested a change of energy band and faster charge transport in the Li-doped TiO2 films. Compared with the undoped TiO2, Li-doped mesoporous TiO2 dramatically improved the photo-voltaic performance of the thermal-evaporated Sb2S3 thin film solar cells, with the average power conversion efficiency (PCE increasing from 1.79% to 4.03%, as well as the improved open-voltage (Voc, short-circuit current (Jsc and fill factors. The best device based on Li-doped TiO2 achieved a power conversion efficiency up to 4.42% as well as a Voc of 0.645 V, which are the highest values among the reported thermal-evaporated Sb2S3 solar cells. This study showed that Li-doping on TiO2 can effectively enhance the charge extraction properties of electron transport layers, offering a new strategy to improve the efficiency of Sb2S3-based solar cells.

  14. Sulphur mustard degradation on zirconium doped Ti-Fe oxides

    Energy Technology Data Exchange (ETDEWEB)

    Stengl, Vaclav, E-mail: stengl@iic.cas.cz [Department of Solid State Chemistry, Institute of Inorganic Chemistry AS CR v.v.i 250 68 Husinec-Rez (Czech Republic); Grygar, Tomas Matys [Department of Solid State Chemistry, Institute of Inorganic Chemistry AS CR v.v.i 250 68 Husinec-Rez (Czech Republic); Oplustil, Frantisek; Nemec, Tomas [Military Technical Institute of Protection Brno Veslarska 230, 628 00 Brno (Czech Republic)

    2011-09-15

    Highlights: {yields} New stechiometric materials for sulphur mustard degradation. {yields} High degree of degradation, more then 95% h{sup -1}. {yields} One-pot synthesis procedure. - Abstract: Zirconium doped mixed nanodispersive oxides of Ti and Fe were prepared by homogeneous hydrolysis of sulphate salts with urea in aqueous solutions. Synthesized nanodispersive metal oxide hydroxides were characterised as the Brunauer-Emmett-Teller (BET) surface area and Barrett-Joiner-Halenda porosity (BJH), X-ray diffraction (XRD), infrared (IR) spectroscopy, scanning electron microscopy (SEM) with energy-dispersive X-ray (EDX) microanalysis, and acid-base titration. These oxides were taken for an experimental evaluation of their reactivity with sulphur mustard (chemical warfare agent HD or bis(2-chloroethyl)sulphide). The presence of Zr{sup 4+} dopant tends to increase both the surface area and the surface hydroxylation of the resulting doped oxides in such a manner that it can contribute to enabling the substrate adsorption at the oxide surface and thus accelerate the rate of degradation of warfare agents. The addition of Zr{sup 4+} to the hydrolysis of ferric sulphate with urea shifts the reaction route and promotes formation of goethite at the expense of ferrihydrite. We discovered that Zr{sup 4+} doped oxo-hydroxides of Ti and Fe exhibit a higher degradation activity towards sulphur mustard than any other yet reported reactive sorbents. The reaction rate constant of the slower parallel reaction of the most efficient reactive sorbents is increased with the increasing amount of surface base sites.

  15. Visible light induced electron transfer process over nitrogen doped TiO2 nanocrystals prepared by oxidation of titanium nitride

    International Nuclear Information System (INIS)

    Wu Zhongbiao; Dong Fan; Zhao Weirong; Guo Sen

    2008-01-01

    Nitrogen doped TiO 2 nanocrystals with anatase and rutile mixed phases were prepared by incomplete oxidation of titanium nitride at different temperatures. The as-prepared samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), core level X-ray photoelectron spectroscopy (CL XPS), valence band X-ray photoelectron spectroscopy (VB XPS), UV-vis diffuse reflectance spectra (UV-vis DRS), and visible light excited photoluminescence (PL). The photocatalytic activity was evaluated for photocatalytic degradation of toluene in gas phase under visible light irradiation. The visible light absorption and photoactivities of these nitrogen doped TiO 2 nanocrystals can be clearly attributed to the change of the additional electronic (N - ) states above the valence band of TiO 2 modified by N dopant as revealed by the VB XPS and visible light induced PL. A band gap structure model was established to explain the electron transfer process over nitrogen doped TiO 2 nanocrystals under visible light irradiation, which was consistent with the previous theoretical and experimental results. This model can also be applied to understand visible light induced photocatalysis over other nonmetal doped TiO 2

  16. Microstructure evolution and electrical characterization of Lanthanum doped Barium Titanate (BaTiO{sub 3}) ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Billah, Masum, E-mail: masum.buet09@gmail.com; Ahmed, A., E-mail: jhinukbuetmme@gmail.com; Rahman, Md. Miftaur, E-mail: miftaurrahman@mme.buet.ac.bd [Department of Materials & Metallurgical Engineering, Bangladesh University of Engineering and Technology, Dhaka-1000 (Bangladesh); Mahbub, Rubbayat, E-mail: rubayyatm@gce.buet.ac.bd [Department of Glass and Ceramic Engineering, Bangladesh University of Engineering and Technology, Dhaka-1000 (Bangladesh); Gafur, M. A., E-mail: d-r-magafur@bcsir.gov.bd [Bangladesh Council of Scientific & Industrial Research (BCSIR), Dhaka-1205 (Bangladesh); Bashar, M. Shahriar, E-mail: bashar@agni.com [Institute of Fuel Research & Development, Bangladesh Council of Scientific & Industrial Research (BCSIR), Dhaka-1205 (Bangladesh)

    2016-07-12

    In the current work, we investigated the structural and dielectric properties of Lanthanum oxide (La{sub 2}O{sub 3}) doped Barium Titanate (BaTiO{sub 3}) ceramics and established a correlation between them. Solid state sintering method was used to dope BaTiO{sub 3} with 0.3, 0.5 and 0.7 mole% La{sub 2}O{sub 3} under different sintering parameters. The raw materials used were La{sub 2}O{sub 3} nano powder of ~80 nm grain size and 99.995% purity and BaTiO{sub 3} nano powder of 100 nm grain size and 99.99% purity. Grain size distribution and morphology of fracture surface of sintered pellets were examined by Field Emission Scanning Electron Microscope and X-Ray Diffraction analysis was conducted to confirm the formation of desired crystal structure. The research result reveal that grain size and electrical properties of BaTiO{sub 3} ceramic significantly enhanced for small amount of doping (up to 0.5 mole% La{sub 2}O{sub 3}) and then decreased with increasing doping concentration. Desired grain growth (0.80-1.3 µm) and high densification (<90% theoretical density) were found by proper combination of temperature, sintering parameters and doping concentration. We found the resultant stable value of dielectric constant was 10000-12000 at 100-300 Hz in the temperature range of 30°-50° C for 0.5 mole% La{sub 2}O{sub 3} with corresponding shift of curie temperature around 30° C. So overall this research showed that proper La{sup 3+} concentration can control the grain size, increase density, lower curie temperature and hence significantly improve the electrical properties of BaTiO{sub 3} ceramics.

  17. Influence of Zr doping on structure and morphology of TiO2 nanorods prepared using hydrothermal method

    Science.gov (United States)

    Muslimin, Masliana; Jumali, Mohammad Hafizuddin; Tee, Tan Sin; Beng, Lee Hock; Hui, Tan Chun; Chin, Yap Chi

    2018-04-01

    The aim of this work is to investigate the effect of Zr doping on TiO2 nanostructure. TiO2 nanorods thin films with different Zr-doping concentrations (6 × 10-3 M, 13 × 10-3 M and 25 × 10-3 M) were successfully prepared using a simple hydrothermal method. The structural and morphological properties of the samples were evaluated using XRD and FESEM respectively. The XRD results revealed that the TiO2 in all samples stabilized as rutile phase. The FESEM micrographs confirmed that TiO2 exist as square like nanorods with blunt tips. Although the crystallographic nature remains unchanged, the introduction of Zr has altered the surface density, structure and morphology of TiO2 which subsequently will have significant effect on its properties.

  18. Solvothermal synthesis of carbon coated N-doped TiO{sub 2} nanostructures with enhanced visible light catalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Yan Xuemin, E-mail: yanzhangmm2002@163.com [College of Chemistry and Environmental Engineering, Yangtze University, Jingzhou 434023 (China); Kang Jialing; Gao Lin; Xiong Lin; Mei Ping [College of Chemistry and Environmental Engineering, Yangtze University, Jingzhou 434023 (China)

    2013-01-15

    Highlights: Black-Right-Pointing-Pointer Chitosan was used as carbon and nitrogen resource to modify TiO{sub 2} nanostructure. Black-Right-Pointing-Pointer Nanocomposites with mesostructure were obtained by one-step solvothermal method. Black-Right-Pointing-Pointer Carbon species were modified on the surface of TiO{sub 2}. Black-Right-Pointing-Pointer Nitrogen was doped into the anatase titania lattice. Black-Right-Pointing-Pointer CTS-TiO{sub 2} nanocomposites show superior visible light photocatalytic activity. - Abstract: Visible light-active carbon coated N-doped TiO{sub 2} nanostructures(CTS-TiO{sub 2}) were prepared by a facile one-step solvothermal method with chitosan as carbon and nitrogen resource at 180 Degree-Sign C. The as-prepared samples were characterized by transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), N{sub 2} adsorption-desorption analysis, X-ray photoelectron spectroscopy (XPS), and ultraviolet-visible (UV-vis) diffuse reflectance spectroscopy. The CTS-TiO{sub 2} nanocomposites possess anatase phase of nanocrystalline structure with average particle size of about 5-7 nm. A wormhole mesostructure can be observed in the CTS-TiO{sub 2} nanocomposites due to the constituent agglomerated of nanoparticles. It has been evidenced that the nitrogen was doped into the anatase titania lattice and the carbon species were modified on the surface of TiO{sub 2}. The photocatalytic activities of the as-prepared photocatalysts were measured by the degradation of methylene blue (MB) under visible light irradiation at {lambda} {>=} 400 nm. The results show that CTS-TiO{sub 2} nanostructures display a higher visible light photocatalytic activity than pure TiO{sub 2}, commercial P25 and C-coated TiO{sub 2} (C-TiO{sub 2}) photocatalysts. The higher photocatalytic activity could be attributed to the band-gap narrowed by N-doping and the accelerated separation of the photo-generated electrons

  19. Tm-doped TiO2 and Tm2Ti2O7 pyrochlore nanoparticles: enhancing the photocatalytic activity of rutile with a pyrochlore phase.

    Science.gov (United States)

    De Los Santos, Desiré M; Navas, Javier; Aguilar, Teresa; Sánchez-Coronilla, Antonio; Fernández-Lorenzo, Concha; Alcántara, Rodrigo; Piñero, Jose Carlos; Blanco, Ginesa; Martín-Calleja, Joaquín

    2015-01-01

    Tm-doped TiO2 nanoparticles were synthesized using a water-controlled hydrolysis reaction. Analysis was performed in order to determine the influence of the dopant concentration and annealing temperature on the phase, crystallinity, and electronic and optical properties of the resulting material. Various characterization techniques were utilized such as X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy and UV-vis spectroscopy. For the samples annealed at 773 and 973 K, anatase phase TiO2 was obtained, predominantly internally doped with Tm(3+). ICP-AES showed that a doping concentration of up to 5.8 atom % was obtained without reducing the crystallinity of the samples. The presence of Tm(3+) was confirmed by X-ray photoelectron spectroscopy and UV-vis spectroscopy: the incorporation of Tm(3+) was confirmed by the generation of new absorption bands that could be assigned to Tm(3+) transitions. Furthermore, when the samples were annealed at 1173 K, a pyrochlore phase (Tm2Ti2O7) mixed with TiO2 was obtained with a predominant rutile phase. The photodegradation of methylene blue showed that this pyrochlore phase enhanced the photocatalytic activity of the rutile phase.

  20. Synthesis of N and La co-doped TiO{sub 2}/AC photocatalyst by microwave irradiation for the photocatalytic degradation of naphthalene

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Dandan; Wu, Zhansheng, E-mail: wuzhans@126.com; Tian, Fei; Ye, Bang-Ce; Tong, Yanbin, E-mail: tongyanbin@sina.com

    2016-08-15

    La and N co-doped TiO{sub 2} nanoparticles supported on activated carbon (TiO{sub 2}/AC) were synthesized through a microwave-assisted sol–gel method for the synergistic removal of naphthalene solution by photocatalytic degradation. Results showed that the La and N ions were incorporated into the TiO{sub 2} framework in both the anatase and rutile phases of TiO{sub 2} for single doped and co-doped samples, which narrowed the band gap of TiO{sub 2} from 2.82 to 2.20 eV. The PL spectra of the samples showed a decrease in the recombination centers when N and La were introduced in TiO{sub 2}/AC. The 0.001La-N-TiO{sub 2}/AC photocatalyst exhibited the highest degradation efficiency of 93.5% for naphthalene under visible light within 120 min. This result was attributed to a synergistic effect involving the efficient inhibition of the recombination of photogenerated electrons and holes, the increase in surface hydroxyl, surface area, volume pores, and the increase of uptake in the visible light region. In addition, the high apparent rate constant indicated that La and N co-doping result in the increase of photoactivity. This study demonstrated the co-doped TiO{sub 2}/AC is a highly efficient photocatalyst for the removal of naphthalene. The results provided valuable information on the mechanism of naphthalene decomposition. - Highlights: • N, La codoped TiO{sub 2}/AC catalysts were synthesized by microwave-assisted. • N and La doping inhibit the recombination of photogenerated electrons and holes. • 0.001La-N-TiO{sub 2}/AC obtains photodegradation efficiency of 93.5% for naphthalene. • The photocatalysts possess good photochemical stability and reusability.

  1. Al2O3 doping of TiO2 electrodes and applications in dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Eom, Tae Sung; Kim, Kyung Hwan; Bark, Chung Wung; Choi, Hyung Wook

    2014-01-01

    Dye-sensitized solar cells (DSSCs) have been intensively studied since their discovery in 1991. DSSCs have been extensively researched over the past decades as cheaper alternatives to silicon solar cells due to their high energy-conversion efficiency and their low production cost. However, some problems need to be solved in order to enhance the efficiency of DSSCs. In particular, the electron recombination that occurs due to the contact between the transparent conductive oxide (TCO) and a redox electrolyte is one of the main limiting factors of efficiency. In this work, we report for the first time the improvement of the photovoltaic characteristics of DSSCs by doping TiO 2 with Al 2 O 3 . DSSCs were constructed using composite particles of Al 2 O 3 -doped TiO 2 and TiO 2 nanoparticles. The DSSCs using Al 2 O 3 showed the maximum conversion efficiency of 6.29% due to effective electron transport. DSSCs based on Al 2 O 3 -doped TiO 2 films showed better photovoltaic performance than cells fabricated with only TiO 2 nanoparticles. This result is attributed to the prevention of electron recombination between electrons in the TiO 2 conduction band with holes in the dye or the electrolyte. There mechanism is suggested based on impedance results, which indicated improved electron transport at the TiO 2 /dye/electrolyte interface.

  2. Phase evaluation of YSZ upon doping with Ta"5"+, Ti"4"+ and Ca"2"+ with combined Raman and XRD analysis

    International Nuclear Information System (INIS)

    Bhattacharya, A.; Shklover, V.; Wermelinger, T.

    2012-01-01

    To improve the phase stability of 7YSZ (7 wt%-Y_2O_3-doped ZrO_2), it has been doped with larger (Ca"2"+) and smaller (Ti"4"+ or Ta"5"+) ions. Complementary Raman and XRD studies of these stabilized systems have been performed. The tetragonal symmetry of the Ta"5"+-ion-doped YSZ sample and the Ti"4"+-doped YSZ sample, and the cubic symmetry of Ca"2"+-doped YSZ have been confirmed both by means of XRD and Raman analyses. Raman scattering measurements show shifts of characteristic peaks when the YSZ is doped with Ta"5"+, Ti"4"+ and Ca"2"+ cations. The peak shift increased with increasing dopant concentration in the ZrO_2 lattice. The Ta-doped YSZ sample heat-treated below 1500 C contained some YTaO_4 phase, which was confirmed by means of XRD as well as by Raman spectroscopy. The effect of Ca"2"+ ion doping on the Raman peak shift was much higher than that of Y"3"+ ion doping. In this work it has been highlighted that Raman spectroscopy is a useful tool complementing XRD, for qualitative comparison of the doping effect on the lattice parameters of ZrO_2.

  3. Effects of nitrogen and carbon doping on properties and photocatalytic activity of TiO2-In2O3 composite

    International Nuclear Information System (INIS)

    Wu, Chung-Hsin; Wu, Jui-Tai; Lai, Chih-Hao; Chung, Wei-Yang; Kuo, Chao-Yin; Hong, Pui-Kwan Andy

    2015-01-01

    TiO 2 -In 2 O 3 (Ti-In) was synthesized by the sol-gel method and the composite was further doped with nitrogen and carbon to create Ti-In-N and Ti-In-C, respectively. The dye C.I. Reactive Red 2 (RR2) was used a model compound to be subjected to various composites and measured for removal by photocatalytic degradation and adsorption. Ti-In-N possessed a larger mean diameter than Ti-In-C, while the latter possessed a greater anatase content and surface area than the former. After N or C doping, the spectra of corresponding Ti-In-N and Ti-In-C showed absorption edges at longer wavelengths than the parent Ti-In. Ti-N-O and Ti-O-C bonds were found in Ti-In-N and Ti-In-C composites, respectively. Ti-In-N was more effective for RR2 photodegradation than Ti-In-C, and the Ti-In-C removed more RR2 by adsorption than Ti-In-N

  4. Synthesis of S/Cr doped mesoporous TiO2 with high-active visible light degradation property via solid state reaction route

    International Nuclear Information System (INIS)

    Liu Shaoyou; Tang Qunli; Feng Qingge

    2011-01-01

    S/Cr doped mesoporous TiO 2 (S-TiO 2 , Cr-TiO 2 , S-Cr-TiO 2 ) were successfully synthesized via a simple, effective and environmental benign solid state reaction route. The low angle XRD patterns demonstrated that the resulting samples possess mesostructures. The further characterizations via N 2 adsorption-desorption and XPS showed that the typical S/Cr co-doped mesoporous TiO 2 (S-Cr-TiO 2 (5S-5Cr)) possesses mesopore with the high specific surface area of 118.4 m 2 /g and narrow pore size distribution, and both S and Cr have been incorporated into the lattice of TiO 2 with the amounts of 4.16% sulfur and 7.88% chromium, respectively. And Raman spectroscopy shows that the surface of S-Cr-TiO 2 (5S-5Cr) material possesses stretching vibrational peaks at ∼709, ∼793 cm -1 are assignable to the Ti-O-Cr, O-Cr (Ti)-OH bonds, respectively. Interestingly, the UV-vis displayed that the absorption regions of S/Cr doped mesoporous TiO 2 cover the visible light region. As for the series of S-Cr-TiO 2 samples, the absorption region even extends to near infrared region with strong adsorption. Moreover, compared with the pure titanium dioxide (P25-TiO 2 ), the photodegradation properties of bromocresol green (BCG) on the S/Cr doped mesoporous TiO 2 showed excellent photocatalytic properties under visible light irradiation. Within 50 min visible light irradiation, 82.6% of the initial BCG was degraded for the S-Cr-TiO 2 (6S-4Cr) photocatalyst.

  5. Local geometric and electronic structures and origin of magnetism in Co-doped BaTiO3 multiferroics

    Science.gov (United States)

    Phan, The-Long; Thang, P. D.; Ho, T. A.; Manh, T. V.; Thanh, Tran Dang; Lam, V. D.; Dang, N. T.; Yu, S. C.

    2015-05-01

    We have prepared polycrystalline samples BaTi1-xCoxO3 (x = 0-0.1) by solid-state reaction. X-ray diffraction and Raman-scattering studies reveal the phase separation in crystal structure as changing Co-doping content (x). The samples with x = 0-0.01 are single phase in a tetragonal structure. At higher doping contents (x > 0.01), there is the formation and development of a secondary hexagonal phase. Magnetization measurements at room temperature indicate a coexistence of paramagnetic and weak-ferromagnetic behaviors in BaTi1-xCoxO3 samples with x > 0, while pure BaTiO3 is diamagnetic. Both these properties increase with increasing x. Analyses of X-ray absorption spectra recorded from BaTi1-xCoxO3 for the Co and Ti K-edges indicate the presence of Co2+ and Co3+ ions. They locate in the Ti4+ site of the tetragonal and hexagonal BaTiO3 structures. Particularly, there is a shift of oxidation state from Co2+ to Co3+ when Co-doping content increases. We believe that the paramagnetic nature in BaTi1-xCoxO3 samples is due to isolated Co2+ and Co3+ centers. The addition of Co3+ ions enhances the paramagnetic behavior. Meanwhile, the origin of ferromagnetism is due to lattice defects, which is less influenced by the changes caused by the variation in concentration of Co2+ and Co3+ ions.

  6. Carbon wrapped and doped TiO{sub 2} mesoporous nanostructure with efficient visible-light photocatalysis for NO removal

    Energy Technology Data Exchange (ETDEWEB)

    He, Di; Li, Yongli, E-mail: lyl@bjut.edu.cn; Wang, Inshu, E-mail: wangjsh@bjut.edu.cn; Wu, Junshu; Yang, Yilong; An, Qier

    2017-01-01

    Highlights: • Carbon wrapped and doped mesoporous titanium dioxide nanocrystals were fabricated. • Meso/micropores are generated on TiO{sub 2} surface caused by eliminating of carbon precursor. • Absorption edge is extended to visible region owing to the carbon-doping. • About 71% of NO is removed under visible light irradiation even in absence of moisture. - Abstract: Carbon wrapped and doped mesoporous anatase TiO{sub 2} nanocrystals were prepared by a hydrothermal approach in acetic acid aqueous containing chitosan. A designed post-thermal treatment was employed to enhance the incorporation between carbon and TiO{sub 2}. After hydrothermal process, mesoporous anatase TiO{sub 2} formed with wrapped by a few layers of carbon shell. Here chitosan was used as not only the template for the formation of mesopores, but also the carbon source toward the carbon layers coating. Furthermore, chitosan provided doping element into TiO{sub 2} lattice and induced to form Ti−C bond which caused Ti(III) with oxygen vacancies. The Ti(III)-oxygen vacancy are partly responsible for visible-light response and high photocatalytic activity, which can accelerate electron transfer thus inhibit photogenerated charge recombination. The photocatalytic activity was evaluated using photo-oxidation of gaseous NO under visible light irradiation as the probe reaction. In the optimum result, 71% of NO with starting concentration at ppb level was photo-degraded. Our results also showed that the photogenerated electrons played a key role in photodegradation of NO, as a result, the environmental humidity level had a negligible effect on the photocatalysis.

  7. Synthesis, structural and optical properties of pure and rare-earth ion doped TiO{sub 2} nanowire arrays by a facile hydrothermal technique

    Energy Technology Data Exchange (ETDEWEB)

    Bandi, Vengala Rao; Raghavan, Chinnambedu Murugesan; Grandhe, Bhaskar kumar; Kim, Sang Su [Department of Physics, Changwon National University, Changwon 641-773 (Korea, Republic of); Jang, Kiwan, E-mail: kwjang@changwon.ac.kr [Department of Physics, Changwon National University, Changwon 641-773 (Korea, Republic of); Shin, Dong-Soo [Department of Chemistry, Changwon National University, Changwon 641-773 (Korea, Republic of); Yi, Soung-Soo [Department of Photonics, Silla University, Busan 617-736 (Korea, Republic of); Jeong, Jung-Hyun [Department of Physics, Pukyong National University, Busan 608-737 (Korea, Republic of)

    2013-11-29

    Single crystalline pure and rare-earth metal ions (Eu{sup 3+} and Ce{sup 3+}) doped TiO{sub 2} nanowire arrays were prepared on conductive fluorine doped indium tin oxide substrates by a facile hydrothermal method. Initially the conditions and parameters were optimized to prepare the high quality TiO{sub 2} nanowire arrays in the absence of organic additives. The average diameter and length of the TiO{sub 2} nanowire were found to be ∼ 30–50 nm and ∼ 0.5–1.5 μm, respectively. The formations of rutile phase structure in all the samples were confirmed by x-ray diffractometric analysis while the transmission electron microscopy confirms the single crystallinity and the maximum orientation of growth direction along [001] for the as-grown TiO{sub 2} nanowire. The optical properties of all the samples were analyzed using photoluminescence spectroscopy. The photocatalytic properties of the pure and doped TiO{sub 2} were investigated for the decomposition of organic toludine blue-O dye under ultraviolet irradiation. The result demonstrates that the Ce{sup 3+}: TiO{sub 2} decomposed almost 90% of the organic dye within 80 min. - Highlights: • Rare-earth (RE) doped TiO{sub 2} nanowire arrays were prepared by hydrothermal method • RE doping enhanced the growth rate of TiO{sub 2} nanowire arrays • The catalysts used to check their photocatalytic activity by toludine blue-O dye • RE doped TiO2 act as unprecedented photocatalyst for organic dye decomposition.

  8. Synthesis, characterization and visible light photocatalytic activity of Cr 3+ , Ce 3+ and N co-doped TiO 2 for the degradation of humic acid

    KAUST Repository

    Rashid, S. G.; Gondal, M. A.; Hameed, A.; Aslam, M.; Dastageer, M. A.; Yamani, Z. H.; Anjum, Dalaver H.

    2015-01-01

    The synthesis, characterization and photocatalytic activity of Cr3+ and Ce3+ co-doped TiON (N-doped TiO2) for the degradation of humic acid with exposure to visible light is reported. The synthesized bimetal (Cr3+ + Ce3+) modified TiON (Cr-Ce/TiON), with an evaluated bandgap of 2.1 eV, exhibited an enhanced spectral response in the visible region as compared to pure and Ce3+ doped TiON (Ce/TiON). The XRD analysis revealed the insertion of Cr3+ and Ce3+ in the crystal lattice along with Ti4+ and N that resulted in the formation of a strained TiON anatase structure with an average crystallite size of ∼10 nm. Raman analysis also supported the formation of stressed rigid structures after bimetal doping. HRTEM confirmed the homogeneous distribution of both the doped metallic components in the crystal lattice of TiON without the formation of surface oxides of either Cr3+ or Ce3+. Electron energy loss spectroscopy (EELS) analysis revealed no change in the oxidation of either Cr or Ce during the synthesis. The synthesized Cr-Ce/TiON catalyst exhibited appreciable photocatalytic activity for the degradation of humic acid on exposure to visible light. Additionally, a noticeable mineralization of carbon rich humic acid was also witnessed. The photocatalytic activity of the synthesized catalyst was compared with pristine and Ce3+ doped TiON. © The Royal Society of Chemistry 2015.

  9. Biocompatibility of Mg Ion Doped Hydroxyapatite Films on Ti-6Al-4V Surface by Electrochemical Deposition.

    Science.gov (United States)

    Lee, Kang; Choe, Han-Cheol

    2016-02-01

    In this study, we prepared magnesium (Mg) doped nano-phase hydroxyapatite (HAp) films on the TiO2 nano-network surface using electrochemical deposition method. Ti-6Al-4V ELI surface was anodized in 5 M NaOH solution at 0.3 A for 10 min. Nano-network TiO2 surface were formed by these anodization steps which acted as templates and anchorage for growth of the Mg doped HAp during subsequent pulsed electrochemical deposition process at 85 degrees C. The phase and morphologies of HAp deposits were influenced by the Mg ion concentration.

  10. Colossal Dielectric Behavior of Ga+Nb Co-Doped Rutile TiO2.

    Science.gov (United States)

    Dong, Wen; Hu, Wanbiao; Berlie, Adam; Lau, Kenny; Chen, Hua; Withers, Ray L; Liu, Yun

    2015-11-18

    Stimulated by the excellent colossal permittivity (CP) behavior achieved in In+Nb co-doped rutile TiO2, in this work we investigate the CP behavior of Ga and Nb co-doped rutile TiO2, i.e., (Ga(0.5)Nb(0.5))(x)Ti(1-x)O2, where Ga(3+) is from the same group as In(3+) but with a much smaller ionic radius. Colossal permittivity of up to 10(4)-10(5) with an acceptably low dielectric loss (tan δ = 0.05-0.1) over broad frequency/temperature ranges is obtained at x = 0.5% after systematic synthesis optimizations. Systematic structural, defect, and dielectric characterizations suggest that multiple polarization mechanisms exist in this system: defect dipoles at low temperature (∼10-40 K), polaronlike electron hopping/transport at higher temperatures, and a surface barrier layer capacitor effect. Together these mechanisms contribute to the overall dielectric properties, especially apparent observed CP. We believe that this work provides comprehensive guidance for the design of new CP materials.

  11. Solvothermal syntheses of Bi and Zn co-doped TiO{sub 2} with enhanced electron-hole separation and efficient photodegradation of gaseous toluene under visible-light

    Energy Technology Data Exchange (ETDEWEB)

    Li, Juan-Juan [Center for Excellence in Regional Atmospheric Environment, and Key Laboratory of Urban Pollutant Conversion, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); Cai, Song-Cai [Center for Excellence in Regional Atmospheric Environment, and Key Laboratory of Urban Pollutant Conversion, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); University of Chinese Academy of Sciences, Beijing, 100049 (China); Xu, Zhen [Center for Excellence in Regional Atmospheric Environment, and Key Laboratory of Urban Pollutant Conversion, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); Chen, Xi [Center for Excellence in Regional Atmospheric Environment, and Key Laboratory of Urban Pollutant Conversion, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); University of Chinese Academy of Sciences, Beijing, 100049 (China); Chen, Jin [Center for Excellence in Regional Atmospheric Environment, and Key Laboratory of Urban Pollutant Conversion, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); Jia, Hong-Peng, E-mail: hpjia@iue.ac.cn [Center for Excellence in Regional Atmospheric Environment, and Key Laboratory of Urban Pollutant Conversion, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); Chen, Jing, E-mail: jing.chen@fjirsm.ac.cn [State Key Laboratory of Structural Chemistry, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou 350002 (China)

    2017-03-05

    Highlights: • Bi-Zn co-doped TiO{sub 2} catalysts were prepared by solvothermal route. • The incorporation of Bi doping into the TiO{sub 2} generates intermediate energy levels. • Bi and Zn doping showed the enhanced absorption in visible-light region. • Zn dopant acts as a mediator of interfacial charge transfer. • TiBi{sub 1.9%}Zn{sub 1%}O{sub 2} exhibited high photocatalytic degradation for toluene. - Abstract: This study investigated the effects of Bi doped and Bi-Zn co-doped TiO{sub 2} on photodegradation of gaseous toluene. The doped TiO{sub 2} with various concentration of metal was prepared using the solvothermal route and characterized by SEM, XRD, Raman, BET, DRS, XPS, PL and EPR. Their photocatalytic activities under visible-light irradiation were drastically influenced by the dopant content. The results showed that moderate metal doping levels were obviously beneficial for the toluene degradation, while high doping levels suppressed the photocatalytic activity. The photocatalytic degradation of toluene over TiBi{sub 1.9%}O{sub 2} and TiBi{sub 1.9%}Zn{sub 1%}O{sub 2} can reach to 51% and 93%, respectively, which are much higher than 25% of TiO{sub 2}. Bi doping into TiO{sub 2} lattice generates new intermediate energy level of Bi below the CB edge of TiO{sub 2}. The electron excitation from the VB to Bi orbitals results in the decreased band gap, extended absorption of visible-light and thus enhances its photocatalytic efficiency. Zn doping not only further enhances the absorption in this visible-light region, but also Zn dopant exists as the form of ZnO crystallites located on the interfaces of TiO{sub 2} agglomerates and acts as a mediator of interfacial charge transfer to suppress the electron-hole recombination. These synergistic effects are responsible for the enhanced photocatalytic performance.

  12. The influence of alizarin and fluorescein on the photoactivity of Ni, Pt and Ru-doped TiO2 layers

    International Nuclear Information System (INIS)

    Rosu, Marcela-Corina; Suciu, Ramona-Crina; Lazar, Mihaela D.; Bratu, I.

    2013-01-01

    Highlights: ► The Ni, Pt, Ru-doped TiO 2 materials and sensitized with alizarin and fluorescein dyes were prepared by wet chemical route. ► The samples were characterized by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N 2 physisorption measurements. ► A combined influence of the dopants and dyes was observed, leading to a beneficial effect to TiO 2 photoactivity. -- Abstract: The doping with different metal ions and sensitization with organic compounds are two well known methods used to improve the photoactivity of TiO 2 . In this respect, the metallic ions-doped TiO 2 samples were prepared by embedding Ni, Pt and Ru ions into TiO 2 crystalline network and then, each sample was sensitized with alizarin and fluorescein dyes. The qualitative evaluation of prepared TiO 2 -based materials was made by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N 2 physisorption measurements. The optoelectronic properties investigated by UV–vis spectroscopy show that the optical response of Ni-doped TiO 2 layer shifts to visible. The X-ray spectra do not show peaks of nickel, platinum and ruthenium oxide crystals or pure metals. The FT/IR spectra proved the presence of dye molecules adsorbed on titania nanoparticles surface. These results demonstrated that the studied dopants and dyes have potential to promote modified TiO 2 -based materials as good candidates to be used in photolectrocatalytic processes

  13. Synthesis of PtSn nanostructured catalysts supported over TiO{sub 2} and Ce-doped TiO{sub 2} particles for the electro-oxidation of ethanol

    Energy Technology Data Exchange (ETDEWEB)

    Alvarez, A.E. [Instituto de Ingeniería Electroquímica y Corrosión (INIEC), CONICET, Universidad Nacional del Sur. Av. Alem 1253, Bahía Blanca B8000CPB (Argentina); Gravina, A.N. [Departamento de Química, INQUISUR, CONICET, Universidad Nacional del Sur, Av. Alem 1253, Bahía Blanca B8000CPB (Argentina); Sieben, J.M., E-mail: jmsieben@uns.edu.ar [Instituto de Ingeniería Electroquímica y Corrosión (INIEC), CONICET, Universidad Nacional del Sur. Av. Alem 1253, Bahía Blanca B8000CPB (Argentina); Messina, P.V. [Departamento de Química, INQUISUR, CONICET, Universidad Nacional del Sur, Av. Alem 1253, Bahía Blanca B8000CPB (Argentina); Duarte, M.M.E. [Instituto de Ingeniería Electroquímica y Corrosión (INIEC), CONICET, Universidad Nacional del Sur. Av. Alem 1253, Bahía Blanca B8000CPB (Argentina)

    2016-09-15

    Highlights: • PtSn particles supported on TiO2 and Ce-doped TiO2 were evaluated as catalysts for EOR. • PtSn/TiO2 showed better mass current and higher TON than PtSn/Ce–TiO2 materials. • The activity for EOR decreased markedly with increasing Ce content in the TiO2. - Abstract: PtSn/TiO2 and PtSn/Ce-doped TiO2 catalysts were synthesized and evaluated for ethanol electro-oxidation in acid media. Titanium dioxide and Ce-doped TiO2 nanoparticles were prepared by hydrothermal method followed by calcination at 923 K. Bimetallic PtSn catalysts supported on the oxide materials were synthesized by microwave assisted reduction in ethylene glycol (EG). The structural properties of the resulting materials were evaluated via TEM and XRD, and the compositions were assessed by EDX and ICP-AES analysis. PtSn nanoparticles of about 3–4 nm were deposited on TiO2 and Ce–TiO2 particles. It was found that the catalyst composition is scarcely influenced by the cerium content in the mixed oxides while the electrochemical surface area per unit mass decreases upon the incorporation of Ce in the anatase lattice. The electrochemical tests pointed out that the electrocatalytic activity for ethanol oxidation decreases markedly as the Ce content increases. The results indicate that the presence of cerium in the titanium dioxide crystalline network induces local structural and electronic modifications, thereby leading to a reduction of the crystallinity, surface conductivity and the amount of OH species adsorbed on the surface of the oxide support.

  14. Mesostructured niobium-doped titanium oxide-carbon (Nb-TiO2-C) composite as an anode for high-performance lithium-ion batteries

    Science.gov (United States)

    Hwang, Keebum; Sohn, Hiesang; Yoon, Songhun

    2018-02-01

    Mesostructured niobium (Nb)-doped TiO2-carbon (Nb-TiO2-C) composites are synthesized by a hydrothermal process for application as anode materials in Li-ion batteries. The composites have a hierarchical porous structure with the Nb-TiO2 nanoparticles homogenously distributed throughout the porous carbon matrix. The Nb content is controlled (0-10 wt%) to investigate its effect on the physico-chemical properties and electrochemical performance of the composite. While the crystalline/surface structure varied with the addition of Nb (d-spacing of TiO2: 0.34-0.36 nm), the morphology of the composite remained unaffected. The electrochemical performance (cycle stability and rate capability) of the Nb-TiO2-C composite anode with 1 wt% Nb doping improved significantly. First, a full cut-off potential (0-2.5 V vs. Li/Li+) of Nb-doped composite anode (1 wt%) provides a higher energy utilization than that of the un-doped TiO2-C anode. Second, Nb-TiO2-C composite anode (1 wt%) exhibits an excellent long-term cycle stability (100% capacity retention, 297 mAh/g at 0.5 C after 100 cycles and 221 mAh/g at 2 C after 500 cycles) and improved rate-capability (192 mAh/g at 5 C), respectively (1 C: 150 mA/g). The superior electrochemical performance of Nb-TiO2-C (1 wt%) could be attributed to the synergistic effect of improved electronic conductivity induced by optimal Nb doping (1 wt%) and lithium-ion penetration (high diffusion kinetics) through unique pore structures.

  15. Fe-N co-doped SiO2@TiO2 yolk-shell hollow nanospheres with enhanced visible light photocatalytic degradation

    Science.gov (United States)

    Wan, Hengcheng; Yao, Weitang; Zhu, Wenkun; Tang, Yi; Ge, Huilin; Shi, Xiaozhong; Duan, Tao

    2018-06-01

    SiO2@TiO2 yolk@shell hollow nanospheres (STNSs) is considered as an outstanding photocatalyst due to its tunable structure and composition. Based on this point, we present an unprecedentedly excellent photocatalytic property of STNSs toward tannic acid via a Fe-N co-doped strategy. Their morphologies, compositions, structure and properties are characterized. The Fe-N co-doped STNSs formed good hollow yolk@shell structure. The results show that the energy gap of the composites can be downgraded to 2.82 eV (pure TiO2 = 3.2 eV). Photocatalytic degradation of tannic acid (TA, 30 mg L-1) under visible light (380 nm TiO2 nanospheres, non-doped STNSs and N-doped STNSs, the Fe-N co-doped STNSs exhibits the highest activity, which can degrade 99.5% TA into CO2 and H2O in 80 min. The probable degradation mechanism of the composites is simultaneously proposed, the band gap of STNSs becomes narrow by co-doping Fe-N, so that the TiO2 shell can stimulate electrons under visible light exposure, generate the ions of radOH and radO2- with a strong oxidizing property. Therefore this approach works is much desired for radioactive organic wastewater photocatalytic degradation.

  16. Pr3+ doped biphasic TiO2 (rutile-brookite) nanorod arrays grown on activated carbon fibers: Hydrothermal synthesis and photocatalytic properties

    Science.gov (United States)

    Li, Min; Zhang, Xiaomei; Liu, Ying; Yang, Yi

    2018-05-01

    Praseodymium-doped biphasic TiO2 (rutile-brookite) nanorod arrays (Pr-TiO2 NRAs) were successfully prepared via a two-step hydrothermal reaction on activated carbon fibers (ACFs) which pre-coated with TiO2 nanoparticles at first step. The bicrystalline arrays grown on ACFs are primarily constructed by the well-aligned TiO2 nanorods growing along [0 0 1] direction, which were indicated by the results of SEM and XRD. The nanorods are uniform in diameter and length with about 250 nm and 2.5 μm. The composite photocatalyst with high specific surface area and well-aligned nanostructure are beneficial to enhance the adsorption capacity and even help to suppress electron-hole recombination effectively, which consequently revealed much better (2 times) catalytic performance than that of commercially available P25 TiO2 on methylene blue(MB) photodegradation. In addition, the existence of praseodymium in TiO2 gives rise to shift of absorption edge towards long wavelength, which was indicated by the results of UV-vis DRS. Photodegradation results reveal that Pr-doping significantly improves the activity of TiO2, which was 20% higher than that of undoped TiO2 NRAs for the photodegradation of MB in aqueous medium under visible light irradiation. Meanwhile, the doped amount of Pr had a tiny influence on the photocatalytic performance of the composites. In our experiment, 3% Pr-doped molar concentration was proven to be the relatively optimal dopant concentration for the doping of TiO2 NRAs. Moreover, the photocatalyst grown on ACFs substrates is favorable to reuse and photodegradation rate kept on 76% even after 4 times of reuse.

  17. Microcystin-LR removal from aqueous solutions using a magnetically separable N-doped TiO2 nanocomposite under visible light irradiation

    Science.gov (United States)

    The performance of magnetically separable N-doped TiO2 was found to be significantly improved when compared with a non-magnetic N-doped TiO2 for the aqueous removal of cyanotoxin Microcystin-LR. The observed enhanced photocatalytic activity may be related to the presence of ferri...

  18. Sn doped TiO{sub 2} nanotube with oxygen vacancy for highly efficient visible light photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Li, Jinliang; Xu, Xingtao [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, Shanghai Key Laboratory of Magnetic Resonance, School of Physics and Materials Science, Department of Physics, East China Normal University, Shanghai 200062 (China); Liu, Xinjuan [Institute of Coordination Bond Metrology and Engineering, College of Materials Science and Engineering, China Jiliang University, Hangzhou 310018 (China); Yu, Caiyan; Yan, Dong; Sun, Zhuo [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, Shanghai Key Laboratory of Magnetic Resonance, School of Physics and Materials Science, Department of Physics, East China Normal University, Shanghai 200062 (China); Pan, Likun, E-mail: lkpan@phy.ecnu.edu.cn [Engineering Research Center for Nanophotonics & Advanced Instrument, Ministry of Education, Shanghai Key Laboratory of Magnetic Resonance, School of Physics and Materials Science, Department of Physics, East China Normal University, Shanghai 200062 (China)

    2016-09-15

    Sn doped TiO{sub 2} nanotube with oxygen vacancy (V{sub o}-Sn−TiO{sub 2}) was successfully synthesized via a facile hydrothermal process and subsequent annealing in nitrogen atmosphere. The morphology, structure and photocatalytic performance of V{sub o}-Sn−TiO{sub 2} in the degradation of nitrobenzene were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy, UV–vis absorption spectroscopy, nitrogen adsorption-desorption and electrochemical impedance spectra, respectively. The inner diameter, outer diameter and specific surface area of V{sub o}-Sn−TiO{sub 2} are about 5 nm, 15 nm and 235.54 m{sup 2} g{sup −1}, respectively. The experimental results show that the V{sub o}-Sn−TiO{sub 2} exhibits excellent photocatalytic performance with a maximum degradation rate of 92% in 300 min for nitrobenzene and 94% in 100 min for Rhodamine B and corresponding mineralization rates of 68% and 70% under visible light irradiation. The improved photocatalytic performance is ascribed to the enhanced light absorption and specific surface area as well as the reduced electron-hole pair recombination with the presence of oxygen vacancy and Sn doping in the TiO{sub 2} nanotube. - Highlights: • Photocatalysis is an environmental-friendly technology for nitrobenzene removal. • Sn doped TiO{sub 2} nanotube with oxygen vacancy is fabricated for the first time. • It exhibits excellent photocatalytic performance in degradation of nitrobenzene. • A high degradation rate of 92% is achieved under visible light irradiation.

  19. Synthesis and characterization of Fe{sup 3+} doped TiO{sub 2} nanoparticles and films and their performance for photocurrent response under UV illumination

    Energy Technology Data Exchange (ETDEWEB)

    Elghniji, Kais [University of Sfax, Laboratoire Eau, Energie et Environnement (LR3E), Ecole Nationale d' Ingenieurs de Sfax, B.P. 1173, 3038 Sfax (Tunisia); Atyaoui, Atef [Centre de Recherches et des Technologies des Eaux, Technopole de Borj Cedria B.P. 273, 8020 Soliman (Tunisia); Livraghi, Stefano [Dipartimento di Chimica I.F.M and NIS, Universita degli Studi di Torino, Via P. Giuria, 7 10125 Torino (Italy); Bousselmi, Latifa [Centre de Recherches et des Technologies des Eaux, Technopole de Borj Cedria B.P. 273, 8020 Soliman (Tunisia); Giamello, Elio [Dipartimento di Chimica I.F.M and NIS, Universita degli Studi di Torino, Via P. Giuria, 7 10125 Torino (Italy); Ksibi, Mohamed, E-mail: Mohamed.Ksibi@tunet.tn [University of Sfax, Laboratoire Eau, Energie et Environnement (LR3E), Ecole Nationale d' Ingenieurs de Sfax, B.P. 1173, 3038 Sfax (Tunisia)

    2012-11-15

    Graphical abstract: Schematic diagram illustrating the charge transfer from excited TiO{sub 2} to the different states of Fe{sup 3+} ions; C{sub B} and V{sub B} refer to the energy levels of the conduction and valence bands of TiO{sub 2}, respectively. Highlights: Black-Right-Pointing-Pointer In this study we examine the Iron as catalyst precursor to synthesize the Fe{sup 3+} doped TiO{sub 2} nanoparticles. Black-Right-Pointing-Pointer The Fe{sup 3+} doped TiO{sub 2} catalysts show the presence of a mixed phase of anatase. Black-Right-Pointing-Pointer The iron is completely absent in the XRD pattern of the doped iron TiO{sub 2} powder. Black-Right-Pointing-Pointer The analysis of EPR result further confirms that Fe{sup 3+} ion are successfully doped in the TiO{sub 2} lattice by substituting Ti{sup 4+}. Black-Right-Pointing-Pointer Fe{sup 3+} doping can efficiently separate the photo-generated electrons and holes. - Abstract: Undoped TiO{sub 2} and Fe{sup 3+} doped (0.1, 0.3, 0.6 and 1 wt.%) TiO{sub 2} nanoparticles have been synthesized by the acid-catalyzed sol-gel method. Iron cations are introduced in the initial solution, before gelification, what promotes their lattice localization. The Fe{sup 3+} doped TiO{sub 2} films have been fabricated using a dip-coating technique. The effect of iron content on the crystalline structure, phase transformation and grain growth were determined by X-ray diffraction (XRD), Raman spectroscopy, UV-visible diffused reflectance spectroscopy (DRS) and Electron paramagnetic resonance (EPR) spectroscopy. It has demonstrated that all catalysts are composed of mixed-phase crystals of anatase and brookite with anatase as dominant phase. The crystallinity of the brookite and anatase phases decreased with increasing the iron content. The analysis of EPR result further confirms that Fe{sup 3+} ion are successfully doped in the TiO{sub 2} lattice by substituting Ti{sup 4+}. It was demonstrated that Fe{sup 3+} ion in the TiO{sub 2} films

  20. Nanoscale Optimization and Statistical Modeling of Photoelectrochemical Water Splitting Efficiency of N-Doped TiO2 Nanotubes

    KAUST Repository

    Isimjan, Tayirjan T.; Trifkovic, Milana; Abdullahi, Inusa; Rohani, Sohrab M F; Ray, Ajay

    2014-01-01

    Highly ordered nitrogen-doped titanium dioxide (N-doped TiO2) nanotube array films with enhanced photo-electrochemical water splitting efficiency (PCE) for hydrogen generation were fabricated by electrochemical anodization, followed by annealing

  1. Behaviour of Ti-doped CFCs under thermal fatigue tests

    Energy Technology Data Exchange (ETDEWEB)

    Centeno, A. [Instituto Nacional del Carbon (CSIC), Apdo. 73, 33080 Oviedo (Spain); Pintsuk, G.; Linke, J. [Forschungszentrum Juelich GmbH, EURATOM Association, 52425 Juelich (Germany); Gualco, C. [Ansaldo Energia, I-16152 Genoa (Italy); Blanco, C., E-mail: clara@incar.csic.es [Instituto Nacional del Carbon (CSIC), Apdo. 73, 33080 Oviedo (Spain); Santamaria, R.; Granda, M.; Menendez, R. [Instituto Nacional del Carbon (CSIC), Apdo. 73, 33080 Oviedo (Spain)

    2011-01-15

    In spite of the remarkable progress in the design of in-vessel components for the divertor of the first International Thermonuclear Experimental Reactor (ITER), a great effort is still put into the development of manufacturing technologies for carbon armour with improved properties. Newly developed 3D titanium-doped carbon fibre reinforced composites and their corresponding undoped counterparts were brazed to a CuCrZr heat sink to produce actively cooled flat tile mock-ups. By exposing the mock-ups to thermal fatigue tests in an electron beam test facility, the material behaviour and the brazing between the individual constituents in the mock-up was qualified. The mock-ups with titanium-doped CFCs exhibited a significantly improved thermal fatigue resistance compared with those undoped materials. The comparison of these mock-ups with those produced using pristine NB31, one of the reference materials as plasma facing material for ITER, showed almost identical results, indicating the high potential of Ti-doped CFCs due to their improved thermal shock resistance.

  2. Synthesis, Structural and Optical Properties of Co Doped TiO2 Nanocrystals by Sol-Gel Method

    OpenAIRE

    Sridevi , D.V ,; Ramesh , V; Sakthivel , T; Geetha , K ,; Ratchagar , V ,; Jagannathan , K ,; Rajarajan , K ,; Ramachadran , K ,

    2017-01-01

    International audience; A TiO2 nanoparticle doped with cobalt was synthesized by sol-gel technique employed at room temperature with appropriate reactants. In the present case, we used titanium tetra isoprotoxide (TTIP) and 2–propanol as a common starting material and the obtained products were calcined at 450˚C450˚450˚C. From the Powder XRD data the particle size was calculated by Scherrer method. The FE-SEM analysis shows the morphology of cobalt doped TiO2 nanoparticles. The various functi...

  3. Visible-light-driven photoelectrochemical and photocatalytic performances of Cr-doped SrTiO3/TiO2 heterostructured nanotube arrays.

    Science.gov (United States)

    Jiao, Zhengbo; Chen, Tao; Xiong, Jinyan; Wang, Teng; Lu, Gongxuan; Ye, Jinhua; Bi, Yingpu

    2013-01-01

    Well-aligned TiO2 nanotube arrays have become of increasing significance because of their unique highly ordered array structure, high specific surface area, unidirectional charge transfer and transportation features. However, their poor visible light utilization as well as the high recombination rate of photoexcited electron-hole pairs greatly limited their practical applications. Herein, we demonstrate the fabrication of visible-light-responsive heterostructured Cr-doped SrTiO3/TiO2 nanotube arrays by a simple hydrothermal method, which facilitate efficient charge separation and thus improve the photoelectrochemical as well as photocatalytic performances.

  4. Synergistic effect on the photocatalytic activity of N-doped TiO{sub 2} nanorods synthesised by novel route with exposed (110) facet

    Energy Technology Data Exchange (ETDEWEB)

    Bakar, Shahzad Abu, E-mail: shazad_158@yahoo.com [Department of Chemistry, Federal University of São Carlos, Rod. Washington Luiz, km 235, CEP: 13565-905 São Carlos, SP (Brazil); Embrapa CNPDIA, Rua XV de Novembro, 1452, 13560-970, São Carlos, SP (Brazil); Byzynski, Gabriela; Ribeiro, Caue [Embrapa CNPDIA, Rua XV de Novembro, 1452, 13560-970, São Carlos, SP (Brazil)

    2016-05-05

    This paper describes a facile route for the preparation of visible-light-active N-doped TiO{sub 2} nanorods arrays at low temperature by a template-free oxidant peroxide method (OPM) and crystallized under hydrothermal treatment. The samples were characterized for structural, morphological and optical properties by XPS, FE-SEM, HRTEM, XRD, Raman and UV–vis spectroscopy. XPS analysis revealed that N dopant atoms were mainly added at the interstitial sites into TiO{sub 2} lattice structure and few N atoms were present as substitutional sites of nitrogen atoms and/or at molecularly chemisorbed γ-N{sub 2} molecules. FE-SEM and HR-TEM analyses show that doping does not influenced the cylindrical architecture of the nanorods. However, N doping causes an obvious red shift in the band edge which increases visible region absorption. The photocatalytic activity of pristine and N-doped TiO{sub 2} photocatalysts was tested for the degradation of methyl orange (MO) under UV and visible light irradiation. The N-doped TiO{sub 2} photocatalysts showed an efficient photocatalytic activity for methyl orange degradation under UV and visible-light irradiation as compared to pristine TiO{sub 2}. Multiple cycles for the MO photodegradation were performed without a decrease in the photocatalytic activity. PEC studies showed that photocurrent densities of 8.2 μA cm{sup −2} and 7.0 μA cm{sup −2} were obtained under UV and visible-light illumination at a potential of 0.8 V. - Highlights: • The pristine and N-doped TiO{sub 2} nanorods were prepared and characterized for structural and optical properties. • As-prepared samples showed enhanced photocatalytic activity toward the photodegradation of MO dye. • Photo-electrochemical measurements were done to investigate N-doped TiO{sub 2} nanorods capability for water splitting.

  5. Microstructure and mechanical properties of Ti/Al co-doped DLC films: Dependence on sputtering current, source gas, and substrate bias

    International Nuclear Information System (INIS)

    Guo, Ting; Kong, Cuicui; Li, Xiaowei; Guo, Peng; Wang, Zhenyu; Wang, Aiying

    2017-01-01

    Highlights: • Ti/Al co-doped diamond-like carbon films were fabricated by a hybrid ion beam method. • Process parameters affected the structure and chemical state of co-doped Ti and Al. • The relation between microstructure and properties was investigated systematically. • The guidance to tailor the Ti/Al-DLC films with high performance was provided. - Abstract: Co-doping two metal elements into diamond-like carbon (DLC) films can reach the desirable combined properties, but the preparation and commercialized application of metal co-doped DLC films with well-defined structural properties are currently hindered by the non-comprehensive understanding of structural evolutions under different process parameters. Here, we fabricated the Ti/Al-DLC films using a unique hybrid ion beam system which enabled the independent control of metal content and carbon structure. The evolutions of microstructure, residual compressive stress and mechanical properties induced by the different process parameters including sputtering currents, C_2H_2 or CH_4 source gases and bias voltages were investigated systematically in order to perform in-depth analysis on the relation between the structure and properties in Ti/Al-DLC films. Results revealed that the variations of process parameters seriously affected the concentration and chemical bond state of co-doped Ti/Al atoms in amorphous carbon matrix or incident energies of C ions, which brought the complicated effect on amorphous carbon structures, accounting for the change of residual compressive stress, hardness and toughness. The present results provide the guidance for suitable, effective parameters selection to tailor the Ti/Al-DLC films with high performance for further applications.

  6. Microstructure and mechanical properties of Ti/Al co-doped DLC films: Dependence on sputtering current, source gas, and substrate bias

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Ting [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); School of Materials Science and Engineering, Shanghai University, Shanghai 200444 (China); Kong, Cuicui [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Ningbo University, Ningbo 315201 (China); Li, Xiaowei, E-mail: lixw@nimte.ac.cn [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Guo, Peng; Wang, Zhenyu [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Wang, Aiying, E-mail: aywang@nimte.ac.cn [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China)

    2017-07-15

    Highlights: • Ti/Al co-doped diamond-like carbon films were fabricated by a hybrid ion beam method. • Process parameters affected the structure and chemical state of co-doped Ti and Al. • The relation between microstructure and properties was investigated systematically. • The guidance to tailor the Ti/Al-DLC films with high performance was provided. - Abstract: Co-doping two metal elements into diamond-like carbon (DLC) films can reach the desirable combined properties, but the preparation and commercialized application of metal co-doped DLC films with well-defined structural properties are currently hindered by the non-comprehensive understanding of structural evolutions under different process parameters. Here, we fabricated the Ti/Al-DLC films using a unique hybrid ion beam system which enabled the independent control of metal content and carbon structure. The evolutions of microstructure, residual compressive stress and mechanical properties induced by the different process parameters including sputtering currents, C{sub 2}H{sub 2} or CH{sub 4} source gases and bias voltages were investigated systematically in order to perform in-depth analysis on the relation between the structure and properties in Ti/Al-DLC films. Results revealed that the variations of process parameters seriously affected the concentration and chemical bond state of co-doped Ti/Al atoms in amorphous carbon matrix or incident energies of C ions, which brought the complicated effect on amorphous carbon structures, accounting for the change of residual compressive stress, hardness and toughness. The present results provide the guidance for suitable, effective parameters selection to tailor the Ti/Al-DLC films with high performance for further applications.

  7. La modified TiO{sub 2} photoanode and its effect on DSSC performance: A comparative study of doping and surface treatment on deep and surface charge trapping

    Energy Technology Data Exchange (ETDEWEB)

    Ako, Rajour Tanyi [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara Brunei Darussalam (Brunei Darussalam); Ekanayake, Piyasiri, E-mail: piyasiri.ekanayake@ubd.edu.bn [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara Brunei Darussalam (Brunei Darussalam); Centre for Advanced Material and Energy Sciences (CAMES), Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara Brunei Darussalam (Brunei Darussalam); Tan, Ai Ling [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara Brunei Darussalam (Brunei Darussalam); Young, David James [Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, BE1410, Negara Brunei Darussalam (Brunei Darussalam); Faculty of Science, Health, Education and Engineering, University of the Sunshine Coast, Maroochydore DC, Queensland, 4558 (Australia); Institute of Materials Research and Engineering (IMRE), Agency for Science, Technology and Research - A*STAR, #08-03, 2 Fusionopolis Way, Innovis, 138634 (Singapore)

    2016-04-01

    The effect of Lanthanum ions (La{sup 3+}) on charge trapping in dye-sensitized solar cell (DSSC) photoanodes has been investigated with doped and surface-treated TiO{sub 2} nanoparticles. Doped nanoparticles consisting of 0.5 mol.% Mg and La co-doped TiO{sub 2}, 0.5 mol.% Mg doped TiO{sub 2} and pure TiO{sub 2} were synthesized by the sol gel method. Surface-treated nanoparticles of Mg doped TiO{sub 2} and pure TiO{sub 2} were prepared by ball milling in 0.05 M aqueous La{sup 3+} solution. All materials were analyzed by XRD, XPS and UV–Vis DRS. Cell performance, surface free energy state changes and electron injection efficiency of DSSCs based on these nanoparticles were evaluated using current –voltage measurements, EIS and Incident photon to current conversion efficiency. Doped materials had La and Mg ions incorporated into the TiO{sub 2} lattice, while no lattice changes were observed for the surface-treated materials. Less visible light was absorbed by treated oxides compared with doped oxide samples. The overall power conversion efficiencies (PCE) of DSSC photoanodes based on doped materials were twice those of photoanodes fabricated from treated nanoparticles. Doping establishes deep traps that reduce the recombination of electron–hole (e–h) pairs. Conversely, the presence of absorbed oxygen in treated materials enhances e–h recombination with electrolyte at surface trap sites. - Highlights: • DSSC performance is investigated using photoanodes of doped and La{sup 3+} surface treated TiO{sub 2}. • TiO{sub 2} and Mg–TiO{sub 2} treated with La{sup 3+} absorbed less visible light. • A high concentration of absorbed oxygen on surface treated oxides reduced band bending. • Increased surface free energy in the modified DSSC anodes is caused more by Mg{sup 2+} at Ti{sup 4+} than by La{sup 3+} at the surfaces. • Near surface charge traps due to La{sup 3+} treatment promotes e–h recombination.

  8. Anomalous enhancement of the thermoelectric figure of merit by V co-doping of Nb-SrTiO3

    KAUST Repository

    Ozdogan, K.

    2012-05-10

    The effect of V co-doping of Nb-SrTiO3 is studied by full-potential density functional theory. We obtain a stronger increase of the carrier density for V than for Nbdopants. While in Nb-SrTiO3 a high carrier density counteracts a high thermoelectric figure of merit, the trend is inverted by V co-doping. The mechanism leading to this behavior is explained in terms of a local spin-polarization introduced by the V ions. Our results indicate that magnetic co-doping can be a prominent tool for improving the thermoelectric figure of merit.

  9. Anomalous enhancement of the thermoelectric figure of merit by V co-doping of Nb-SrTiO3

    KAUST Repository

    Ozdogan, K.; Alshareef, Husam N.; Schwingenschlö gl, Udo; Upadhyay Kahaly, M.

    2012-01-01

    The effect of V co-doping of Nb-SrTiO3 is studied by full-potential density functional theory. We obtain a stronger increase of the carrier density for V than for Nbdopants. While in Nb-SrTiO3 a high carrier density counteracts a high thermoelectric figure of merit, the trend is inverted by V co-doping. The mechanism leading to this behavior is explained in terms of a local spin-polarization introduced by the V ions. Our results indicate that magnetic co-doping can be a prominent tool for improving the thermoelectric figure of merit.

  10. Electronic structure and visible light photocatalysis water splitting property of chromium-doped SrTiO3

    International Nuclear Information System (INIS)

    Liu, J.W.; Chen, G.; Li, Z.H.; Zhang, Z.G.

    2006-01-01

    Cr-doped SrTi 1- x Cr x O 3 (x=0.00, 0.02, 0.05, 0.10) powders, prepared by solvothermal method, were further characterized by ultraviolet-visible (UV-vis) absorption spectroscopy. The UV-vis spectra indicate that the SrTi 1- x Cr x O 3 powders can absorb not only UV light like pure SrTiO 3 powder but also the visible-light spectrum (λ>420 nm). The results of density functional theory (DFT) calculation illuminate that the visible-light absorption bands in the SrTi 1- x Cr x O 3 catalyst are attributed to the band transition from the Cr 3d to the Cr 3d+Ti 3d hybrid orbital. The photocatalytic activities of chromium-doped SrTiO 3 both under UV and visible light are increased with the increase in the amounts of chromium. -- Graphical abstract: SrTi 1- x Cr x O 3 powders, prepared by solvothermal method, can absorb not only UV light like pure SrTiO 3 powder but also the visible-light spectrum (λ>420 nm). The results of DFT calculation illuminate that the visible-light absorption bands in the SrTi 1- x Cr x O 3 catalyst are attributed to the band transition from the Cr 3d to the Cr 3d+Ti 3d hybrid orbital

  11. Preparation and characterization of Bi-doped TiO2 and its solar photocatalytic activity for the degradation of isoproturon herbicide

    International Nuclear Information System (INIS)

    Reddy, Police Anil Kumar; Srinivas, Basavaraju; Kala, Pruthu; Kumari, Valluri Durga; Subrahmanyam, Machiraju

    2011-01-01

    Highlights: → Visible active Bi-TiO 2 photocatalyst preparation and thorough charaterization. → Bi-TiO 2 shows high activity for isoproturon degradation under solar light irradiation. → The spectral response of TiO 2 shifts from UV to visible light region by Bi doping. → Bi 3+δ+ species are playing a vital role in minimizing e - /h + recombination. -- Abstract: Bi-doped TiO 2 catalyst was prepared by sol-gel method and was characterized by thermo gravimetric analysis (TGA), X-ray diffraction spectra (XRD), X-ray photo electronic spectroscopy (XPS), UV-Vis diffused reflectance spectra (DRS), photoluminescence spectra (PLS), transmission electron microscopy (TEM), energy dispersive analysis of X-rays (EDAX) and BET surface area. The photocatalytic activity of the catalysts were evaluated for the degradation of isoproturon herbicide under solar light irradiation. The UV-Visible DRS of Bi-doped TiO 2 showed red shift in optical absorption. The presence of Bi 3+δ+ species are playing a vital role in minimizing the electron hole recombination resulting higher activity compared to bare TiO 2 .

  12. N-Doped TiO₂-Coated Ceramic Membrane for Carbamazepine Degradation in Different Water Qualities.

    Science.gov (United States)

    Luster, Enbal; Avisar, Dror; Horovitz, Inna; Lozzi, Luca; Baker, Mark A; Grilli, Rossana; Mamane, Hadas

    2017-07-31

    The photocatalytic degradation of the model pollutant carbamazepine (CBZ) was investigated under simulated solar irradiation with an N-doped TiO₂-coated Al₂O₃ photocatalytic membrane, using different water types. The photocatalytic membrane combines photocatalysis and membrane filtration in a single step. The impact of each individual constituent such as acidity, alkalinity, dissolved organic matter (DOM), divalent cations (Mg 2+ and Ca 2+ ), and Cl - on the degradation of CBZ was examined. CBZ in water was efficiently degraded by an N-doped TiO₂-coated Al₂O₃ membrane. However, elements added to the water, which simulate the constituents of natural water, had an impact on the CBZ degradation. Water alkalinity inhibited CBZ degradation mostly due to increase in pH while radical scavenging by carbonate was more dominant at higher values (>200 mg/L as CaCO₃). A negative effect of Ca 2+ addition on photocatalytic degradation was found only in combination with phosphate buffer, probably caused by deposition of CaHPO₄ or CaHPO₄·2H₂O on the catalyst surface. The presence of Cl - and Mg 2+ ions had no effect on CBZ degradation. DOM significantly inhibited CBZ degradation for all tested background organic compounds. The photocatalytic activity of N-doped TiO₂-coated Al₂O₃ membranes gradually decreased after continuous use; however, it was successfully regenerated by 0.1% HCl chemical cleaning. Nevertheless, dissolution of metals like Al and Ti should be monitored following acid cleaning.

  13. Anatase phase stability and doping concentration dependent refractivity in codoped transparent conducting TiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Chen, T L [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan); Furubayashi, Y [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan); Hirose, Y [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan); Hitosugi, T [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan); Shimada, T [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan); Hasegawa, T [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan)

    2007-10-07

    Nb{sub 0.06}Sn{sub x}Ti{sub 0.94-x}O{sub 2} (x {<=} 0.3) thin films were grown by a pulsed-laser deposition method with varying Sn concentration. Through a combinatorial technique, we find that Sn concentration can reach a maximum of about x = 0.3 while maintaining the stable anatase phase and epitaxy. A doping concentration dependence of the refractivity is revealed, in which refractivity reduction at a wavelength of {lambda} = 500 nm is estimated to be 12.4% for Nb{sub 0.06}Sn{sub 0.3} Ti{sub 0.64}O{sub 2} thin film. Sn doping induced band-gap blue shift can be contributed to the mixing of extended Sn 5s orbitals with the conduction band of TiO{sub 2}. Low resistivity on the order of 10{sup -4} {omega} cm at room temperature and high internal transmittance of more than 95% in the visible light region are exhibited for Nb{sub 0.06}Sn{sub x} Ti{sub 0.94-x}O{sub 2} thin films (x {<=} 0.2). Optical and transport analyses demonstrate that doping Sn into Nb{sub 0.06} Ti{sub 0.94}O{sub 2} can reduce the refractivity while maintaining low resistivity and high transparency.

  14. Improvement of thermal shock resistance of isotropic graphite by Ti-doping

    International Nuclear Information System (INIS)

    Lopez-Galilea, I.; Ordas, N.; Garcia-Rosales, C.; Lindig, S.

    2009-01-01

    Ti-doped isotropic graphite is a promising candidate material for the strike point area of the ITER divertor due to its reduced chemical erosion by hydrogen bombardment and its high thermal shock resistance, mainly due the catalytic effect of TiC on the graphitization leading to an increase of thermal conductivity and to higher mechanical strength. Several manufacturing parameters such as oxidative stabilization treatment, carbonization cycle, graphitization temperature and dwell time during graphitization have been investigated in order to establish a relationship between these parameters and the final properties.

  15. Improvement of thermal shock resistance of isotropic graphite by Ti-doping

    Energy Technology Data Exchange (ETDEWEB)

    Lopez-Galilea, I. [Inmaculada Lopez-Galilea, CEIT and Tecnun (University of Navarra), Po de Manuel Lardizabal, 15 E-20018 San Sebastian (Spain)], E-mail: ilopez@ceit.es; Ordas, N.; Garcia-Rosales, C. [Inmaculada Lopez-Galilea, CEIT and Tecnun (University of Navarra), Po de Manuel Lardizabal, 15 E-20018 San Sebastian (Spain); Lindig, S. [Max-Planck-Institut fuer Plasmaphysik, EURATOM Association, D-85748 Garching (Germany)

    2009-04-30

    Ti-doped isotropic graphite is a promising candidate material for the strike point area of the ITER divertor due to its reduced chemical erosion by hydrogen bombardment and its high thermal shock resistance, mainly due the catalytic effect of TiC on the graphitization leading to an increase of thermal conductivity and to higher mechanical strength. Several manufacturing parameters such as oxidative stabilization treatment, carbonization cycle, graphitization temperature and dwell time during graphitization have been investigated in order to establish a relationship between these parameters and the final properties.

  16. Sol-gel synthesis, characterization and optical properties of mercury-doped TiO{sub 2} thin films deposited on ITO glass substrates

    Energy Technology Data Exchange (ETDEWEB)

    Mechiakh, R., E-mail: raouf_mechiakh@yahoo.fr [Departement de Medecine, Faculte de Medecine, Universite Hadj Lakhdar, Batna (Algeria); Laboratoire de Photovoltaique de Semi-conducteurs et de Nanostructures, Centre de Recherche des Sciences et Technologies de l' Energie, BP 95, Hammam-Lif 2050 (Tunisia); Ben Sedrine, N.; Chtourou, R. [Laboratoire de Photovoltaique de Semi-conducteurs et de Nanostructures, Centre de Recherche des Sciences et Technologies de l' Energie, BP 95, Hammam-Lif 2050 (Tunisia)

    2011-08-15

    The Hg-doped and undoped nano-crystalline TiO{sub 2} films on ITO glass substrates surface and polycrystalline powders were prepared by sol-gel dip coating technique. The crystal structure and surface morphology of TiO{sub 2} were characterized by means of X-ray diffractometer (XRD), atomic force microscope (AFM), spectrophotometer, Fourier-transform infrared (FTIR), and spectroscopic ellipsometry (SE). The results indicated that the powder of TiO{sub 2}, doped with 5% Hg in room temperature was only composed of the anatase phase whereas in the undoped powder exhibits an amorphous phase were present. After heat treatments of thin films, titanium oxide starts to crystallize at the annealing temperature 400 {sup o}C. The average crystallite size of the undoped TiO{sub 2} films was about 8.17 nm and was increased with Hg-doping in the TiO{sub 2} films. Moreover, the grains distributed more uniform and the surface roughness was greater in the Hg-doped TiO{sub 2} films than in the undoped one. Refractive index and porosity were calculated from the measured transmittance spectrum. The values of the index of refraction are in the range (1.95-2.49) and the porosity is in the range (47-2.8). The coefficient of transmission varies from 60 to 90%. SE study was used to determine the annealing temperature effect on the optical properties in the wavelength range from 0.25 to 2 {mu}m and the optical gap of the Hg-doped TiO{sub 2} thin films.

  17. A first principle simulation of competitive adsorption of SF6 decomposition components on nitrogen-doped anatase TiO2 (101) surface

    Science.gov (United States)

    Dong, Xingchen; Zhang, Xiaoxing; Cui, Hao; Zhang, Jun

    2017-11-01

    Gas insulated switchgear has been widely used in modern electric systems due to its significantly excellent performances such as compact structure and low land occupation as well as the security stability. However, inside defects caused during manufacture process can lead to partial discharge which might develop into serious insulation failure. Online monitoring method on basis of gas sensors is considered a promising way of detecting partial discharge for alarm ahead of time. Research has found that TiO2 nanotubes sensors show good response to SO2, SOF2, SO2F2, the decomposition components as a result of partial discharge. In order to investigate the gas-sensing mechanism of nitrogen-doped TiO2 prepared via plasma treatment methods to SO2, SOF2, and SO2F2, the adsorption structures of both three gas molecules and anatase TiO2 (101) surface were built, and DFT calculations were then carried out for calculation and analysis of adsorption parameters. Adsorption property comparison of anatase TiO2 (101) surface after nitrogen doping with Au doping and without doping shows that nitrogen doping can obviously enhance the adsorption energy for SO2 and SOF2 adsorption and no charge transfer for SO2F2 adsorption, further explaining the adsorption mechanism and doping influence of different doping elements.

  18. Enhanced Power Conversion Efficiency of Perovskite Solar Cells with an Up-Conversion Material of Er3+-Yb3+-Li+ Tri-doped TiO2.

    Science.gov (United States)

    Zhang, Zhenlong; Qin, Jianqiang; Shi, Wenjia; Liu, Yanyan; Zhang, Yan; Liu, Yuefeng; Gao, Huiping; Mao, Yanli

    2018-05-11

    In this paper, Er 3+ -Yb 3+ -Li + tri-doped TiO 2 (UC-TiO 2 ) was prepared by an addition of Li + to Er 3+ -Yb 3+ co-doped TiO 2 . The UC-TiO 2 presented an enhanced up-conversion emission compared with Er 3+ -Yb 3+ co-doped TiO 2 . The UC-TiO 2 was applied to the perovskite solar cells. The power conversion efficiency (PCE) of the solar cells without UC-TiO 2 was 14.0%, while the PCE of the solar cells with UC-TiO 2 was increased to 16.5%, which presented an increase of 19%. The results suggested that UC-TiO 2 is an effective up-conversion material. And this study provided a route to expand the spectral absorption of perovskite solar cells from visible light to near-infrared using up-conversion materials.

  19. Multifold polar states in Zn-doped Sr0.9Ba0.1TiO3 ceramics

    Science.gov (United States)

    Guo, Yan-Yan; Guo, Yun-Jun; Wei, Tong; Liu, Jun-Ming

    2015-12-01

    We investigate the effect of Zn doping on the dielectricity and ferroelectricity of a series of polycrystalline Sr0.9-xZnxBa0.1TiO3 (0.0% ≤ x ≤ 5.0%) ceramics. It is surprisingly observed that the Zn doping will produce the multifold polar states, i.e., the Zn-doped ceramic will convert a reduced polar state into an enhanced polar state, and eventually into a stabilized polar state with increasing the doping level x. It is revealed that in the background of quantum fluctuations, the competition between the Zn-doping-induced lattice contraction and the Ba-doping-induced lattice expansion is responsible for both the reduced polar state and the enhanced polar state coming into being. Also, the addition of the antiferrodistortive effect, which is the antipolar interaction originating from the opposite tilted-TiO6 octahedra rotation, represents the core physics behind the stabilized polar state. Project supported by the National Natural Science Foundation of China (Grant Nos. 11304158, 51431006, 51102277, and 11104118), the Scientific Research Foundation of Nanjing University of Posts and Telecommunications, China (Grant No. NY213020), and the Qing Lan Project of Jiangsu Province, China.

  20. A comparative study of the magnetization in transition metal ion doped CeO2, TiO2 and SnO2 nanoparticles

    Science.gov (United States)

    Apostolov, A. T.; Apostolova, I. N.; Wesselinowa, J. M.

    2018-05-01

    Using the microscopic s-d model taking into account anharmonic spin-phonon interactions we have studied the magnetic properties of Co and Cu ion doped CeO2 and TiO2 nanoparticles and compared them with those of SnO2. By Co-doping there is a maximum in the magnetization M(x) curve for all nanoparticles observed in the most transition metal doped ones. The s-d interaction plays an important role by the decrease of M at higher dopant concentration. We have discussed the magnetization in dependence of different model parameters. By small Cu-ion doping there are some differences. In CeO2M decreases with the Cu-concentration, whereas in TiO2 and SnO2M increases. For higher Cu dopant concentrations M(X) decreases in TiO2 nanoparticles. We obtain room temperature ferromagnetism also in Zn doped CeO2, TiO2 and SnO2 nanoparticles, i.e. in non-transition metal ion doped ones. The different behavior of M in Co and Cu doped nanoparticles is due to a combination effect of multivalent metal ions, oxygen vacancies, different radius of cation dopants, connection between lattice and magnetism, as well as competition between the s-d and d-d ferromagnetic or antiferromagnetic interactions.

  1. Synthesis and photoluminescence of Cr-, Ni-, Co-, and Ti-doped ZnSe nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Huy, Bui The [Anastro Laboratory, Department of Chemistry, Changwon National University, Changwon 641-773 (Korea, Republic of); Nhatrang Institute of Technology and Research Application, 2 Hungvuong, Nhatrang (Viet Nam); Seo, Min-Ho; Kumar, Avvaru Praveen [Anastro Laboratory, Department of Chemistry, Changwon National University, Changwon 641-773 (Korea, Republic of); Jeong, Hyuk [Department of Chemistry, Sookmyung Women’s University, Seoul 140-742 (Korea, Republic of); Lee, Yong-Ill, E-mail: yilee@changwon.ac.kr [Anastro Laboratory, Department of Chemistry, Changwon National University, Changwon 641-773 (Korea, Republic of)

    2014-03-05

    Highlights: • The chain length, structure of surfactants operated the size nanoparticles. • Ni{sup 2+}, Co{sup 2+}, Cr{sup 3+}, and Ti{sup 3+} did not create any new centers in the structure of ZnSe. • Doping may have influenced the nanoparticles size because of the Zn replacement. • The TM ions change in ligand field caused the influence on fluorescence intensity. -- Abstract: We developed a facile strategy to synthesize transition metal (TM; Ni, Cr, Co, and Ti)-doped ZnSe nanoparticles (NPs) in aqueous media using a chemical co-precipitation method. Co-precipitation was performed in the presence of one of four different surfactants, namely mercaptoacetic acid (MAA), 3-mercaptopropionic acid (MPA), thioglycerol (TGC), or (3-mercaptopropyl) trimethoxysilane (MPTMS). Surface morphology, chemical, and crystalline properties of the TM-doped ZnSe NPs were studied by transmission electron microscopy (TEM) and X-ray diffraction (XRD). Optical features were characterized by UV–visible and photoluminescence spectroscopies. The influence of various experimental parameters, including the amount of TM and the ratio of precursors, as well as different types of surfactants on the photoluminescence properties of TM-doped ZnSe NPs was investigated systematically. TM-doped ZnSe NPs were excited in the UV region and exhibited photoluminescence in the visible region. Intensity was affected by the concentration of the TM. The results showed that MPA had a stronger influence on photoluminescence than MAA, TGC, and MPTMS. The photoluminescence intensity of TM-doped ZnSe NPs was 30% higher than that of undoped ZnSe NPs.

  2. The influence of alizarin and fluorescein on the photoactivity of Ni, Pt and Ru-doped TiO{sub 2} layers

    Energy Technology Data Exchange (ETDEWEB)

    Rosu, Marcela-Corina, E-mail: marcela.rosu@itim-cj.ro [National Institute for Research and Development of Isotopic and Molecular Technologies, 65-103 Donath Street, 400293, Cluj-Napoca (Romania); Suciu, Ramona-Crina; Lazar, Mihaela D.; Bratu, I. [National Institute for Research and Development of Isotopic and Molecular Technologies, 65-103 Donath Street, 400293, Cluj-Napoca (Romania)

    2013-04-20

    Highlights: ► The Ni, Pt, Ru-doped TiO{sub 2} materials and sensitized with alizarin and fluorescein dyes were prepared by wet chemical route. ► The samples were characterized by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N{sub 2} physisorption measurements. ► A combined influence of the dopants and dyes was observed, leading to a beneficial effect to TiO{sub 2} photoactivity. -- Abstract: The doping with different metal ions and sensitization with organic compounds are two well known methods used to improve the photoactivity of TiO{sub 2}. In this respect, the metallic ions-doped TiO{sub 2} samples were prepared by embedding Ni, Pt and Ru ions into TiO{sub 2} crystalline network and then, each sample was sensitized with alizarin and fluorescein dyes. The qualitative evaluation of prepared TiO{sub 2}-based materials was made by: UV–vis spectroscopy, spectrofluorimetry, FT/IR spectroscopy and microscopy, X-ray diffraction and N{sub 2} physisorption measurements. The optoelectronic properties investigated by UV–vis spectroscopy show that the optical response of Ni-doped TiO{sub 2} layer shifts to visible. The X-ray spectra do not show peaks of nickel, platinum and ruthenium oxide crystals or pure metals. The FT/IR spectra proved the presence of dye molecules adsorbed on titania nanoparticles surface. These results demonstrated that the studied dopants and dyes have potential to promote modified TiO{sub 2}-based materials as good candidates to be used in photolectrocatalytic processes.

  3. Unconventional cells of TiO2 doped with erbium

    International Nuclear Information System (INIS)

    Ribeiro, P.C.; Campos, R.D.; Oliveira, A.S.; Wellen, R.; Diniz, V.C.S.; Costa, A.C.F.M. da

    2016-01-01

    The technology used in TiO_2 solar cells is in constant improvement, new configurations have been developed, aiming practicality and leading to efficiency increase of photovoltaic devices. This paper proposes a new technology for the production of solar cells in order to investigate a better utilization of solar spectrum of TiO2 doped with erbium (Er"3"+), proven by energetic conversion. The Ti_0_,_9Er_0_,_1O2 system was obtained by Pechini method. Nanoparticles have a crystallite size 65.30 nm and surface area 118.48 m"2/g. These characteristics are essential for the formation of the film to be deposited on the conductive glass substrate constituting the cell's photoelectrode. The other side of the cell is the platinum counter electrode. The cell will have the faces sealed by a thermoplastic and, finally the electrolyte will be inserted, then they will be electrically evaluated through energy efficiency and confronted with the literature data base. (author)

  4. Effect of Metal (Mn, Ti Doping on NCA Cathode Materials for Lithium Ion Batteries

    Directory of Open Access Journals (Sweden)

    Dao Yong Wan

    2018-01-01

    Full Text Available NCA (LiNi0.85Co0.10Al0.05-x MxO2, M=Mn or Ti, x < 0.01 cathode materials are prepared by a hydrothermal reaction at 170°C and doped with Mn and Ti to improve their electrochemical properties. The crystalline phases and morphologies of various NCA cathode materials are characterized by XRD, FE-SEM, and particle size distribution analysis. The CV, EIS, and galvanostatic charge/discharge test are employed to determine the electrochemical properties of the cathode materials. Mn and Ti doping resulted in cell volume expansion. This larger volume also improved the electrochemical properties of the cathode materials because Mn4+ and Ti4+ were introduced into the octahedral lattice space occupied by the Li-ions to expand the Li layer spacing and, thereby, improved the lithium diffusion kinetics. As a result, the NCA-Ti electrode exhibited superior performance with a high discharge capacity of 179.6 mAh g−1 after the first cycle, almost 23 mAh g−1 higher than that obtained with the undoped NCA electrode, and 166.7 mAh g−1 after 30 cycles. A good coulombic efficiency of 88.6% for the NCA-Ti electrode is observed based on calculations in the first charge and discharge capacities. In addition, the NCA-Ti cathode material exhibited the best cycling stability of 93% up to 30 cycles.

  5. Zr-doped TiO2 as a thermostabilizer in plasmon-enhanced dye-sensitized solar cells

    Science.gov (United States)

    Pasche, Anastasia; Grohe, Bernd; Mittler, Silvia; Charpentier, Paul A.

    2017-07-01

    Harvesting solar energy is a promising solution toward meeting the world's ever-growing energy demand. Dye-sensitized solar cells (DSSCs) are hybrid organic-inorganic solar cells with tremendous potential for commercial application, but they are plagued by inefficiency due to their poor sunlight absorption. Plasmonic silver nanoparticles (AgNPs) have been shown to enhance the absorptive properties of DSSCs, but their plasmonic resonance can cause thermal damage resulting in cell deterioration. Hence, the influence of Zr-doped TiO2 on the efficiency of plasmon-enhanced DSSCs was studied, showing that 5 mol.% Zr-doping of the photoactive TiO2 material can improve the photovoltaic performance of DSSCs by 44%. By examining three different DSSC designs, it became clear that the efficiency enhancing effect of Zr strongly depends on the proximity of the Zr-doped material to the plasmonic AgNPs.

  6. Significant enhancement in the photocatalytic activity of N, W co-doped TiO2 nanomaterials for promising environmental applications

    International Nuclear Information System (INIS)

    Thind, Sapanbir S; Wu Guosheng; Tian Min; Chen Aicheng

    2012-01-01

    In this work, a mesoporous N, W co-doped TiO 2 photocatalyst was synthesized via a one-step solution combustion method, which utilized urea as the nitrogen source and sodium tungstate as the tungsten source. The photocatalytic activity of the N, W co-doped TiO 2 photocatalyst was significantly enhanced by a facile UV pretreatment approach and was evaluated by measuring the rate of photodegradation of Rhodamine B under both UV and visible (λ > 420) light. Following the UV pretreatment, the UV photocatalytic activity of the N, W co-doped TiO 2 was doubled. In terms of visible light activity, the UV pretreatment resulted in an extraordinary >12 fold improvement. In order to gain insight into this substantial enhancement, the N, W co-doped TiO 2 photocatalysts were studied using x-ray diffraction, transmission electron microscopy, N 2 physisorption, UV–vis absorbance spectroscopy and x-ray photoelectron spectroscopy prior to and following the UV pretreatment. Our experimental results have revealed that this significant augmentation of photocatalytic activity may be attributed to several synergetic factors, including increase of the specific surface area, reduction of the band gap energy and the removal of carbon impurities. (paper)

  7. Photocatalytic characteristics of single phase Fe-doped anatase TiO2 nanoparticles sensitized with vitamin B12

    International Nuclear Information System (INIS)

    Gharagozlou, Mehrnaz; Bayati, R.

    2015-01-01

    Highlights: • Anatase TiO 2 /B 12 hybrid nanostructured catalyst was successfully synthesized by sol–gel technique. • The nanoparticle catalyst was doped with iron at several concentrations. • Nanoparticles were characterized in detail by XRD, Raman, TEM, EDS, and spectroscopy techniques. • The formation mechanism and role of point defects on photocatalytic properties were discussed. • A structure-property-processing correlation was established. - Abstract: We report a processing-structure-property correlation in B 12 -anatase titania hybrid catalysts doped with several concentrations of iron. Our results clearly show that low-level iron doping alters structure, defect content, and photocatalytic characteristics of TiO 2 . XRD and Raman studies revealed formation of a single-phase anatase TiO 2 where no iron based segregation in particular iron oxide, was detected. FT-IR spectra clearly confirmed sensitization of TiO 2 nanoparticles with vitamin B 12 . TEM micrographs and diffraction patterns confirmed crystallization of anatase nanoparticles with a radius of 15–20 nm. Both XRD and Raman signals showed a peak shift and a peak broadening which are surmised to originate from creation of point defects, namely oxygen vacancy and titanium interstitial. The doped samples revealed a narrower band gap as compared to undoped samples. Photocatalytic activity of the samples was assessed through measuring the decomposition rate of rhodamine B. It was found that sensitization with vitamin B 12 and Fe-doping significantly enhances the photocatalytic efficiency of the anatase nanoparticles. We also showed that there is an optimum Fe-doping level where the maximum photocatalytic activity is achieved. The boost of photocatalytic activity was qualitatively understood to originate from a more effective use of the light photons, formation of point defects, which enhance the charge separation, higher carrier mobility

  8. Preparation of Pd-loaded La-doped TiO{sub 2} nanotubes and investigation of their photocatalytic activity under visible light

    Energy Technology Data Exchange (ETDEWEB)

    Zong, Lanlan; Li, Qiuye, E-mail: qiuyeli@henu.edu.cn; Zhang, Jiwei; Wang, Xiaodong; Yang, Jianjun [Henan University, Key Laboratory for Special Functional Materials (China)

    2013-11-15

    Orthorhombic titanic acid nanotubes (TAN) have large BET surface area and small-diameter one-dimensional nanotubular morphology, so they can work as a good supporter and a precursor of TiO{sub 2}. However, in our former research, we found that calcination of TAN to anatase TiO{sub 2} would destroy the nanotubular structure and decrease the BET surface area sharply. In this work, we utilized the pillar effect of the foreign nanoparticles (La{sub 2}O{sub 3}) to keep the nanotubular morphology of TiO{sub 2}, and obtained the anatase TiO{sub 2} nanotubes with large BET surface area. For improving the photocatalytic activity, Pd nanoparticles were loaded as the electron traps on the surface of La-doped TiO{sub 2} by photo-deposition method. The photocatalysts were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, diffuse reflectance spectra, and N{sub 2} adsorption–desorption isotherms measurement. Their photocatalytic activities were evaluated by the removal of propylene under visible light irradiation (λ ≥ 420 nm). The results showed that the photocatalytic activity of Pd-loaded La-doped TiO{sub 2} nanotubes improved effectively compared with that of La-doped TiO{sub 2} and pure TiO{sub 2}.

  9. Composition and crystal structure of N doped TiO2 film deposited at different O2 flow rate by direct current sputtering.

    Science.gov (United States)

    Ding, Wanyu; Ju, Dongying; Chai, Weiping

    2011-06-01

    N doped Ti02 films were deposited by direct current pulse magnetron sputtering system at room temperature. The influence of 02 flow rate on the crystal structure of deposited films was studied by Stylus profilometer, X-ray photoelectron spectroscopy, and X-ray diffractometer. The results indicate that the 02 flow rate strongly controls the growth behavior and crystal structure of N doped Ti02 film. It is found that N element mainly exists as substitutional doped state and the chemical stiochiometry is near to TiO1.68±0.06N0.11±0.01 for all film samples. N doped Ti02 film deposited with 2 sccm (standard-state cubic centimeter per minute) 02 flow rate is amorphous structure with high growth rate, which contains both anatase phase and rutile phase crystal nucleuses. In this case, the film displays the mix-phase of anatase and rutile after annealing treatment. While N doped Ti02 film deposited with 12 cm(3)/min 02 flow rate displays anatase phase before and after annealing treatment. And it should be noticed that no TiN phase appears for all samples before and after annealing treatment. Copyright © 2011 The Research Centre for Eco-Environmental Sciences, Chinese Academy of Sciences. Published by Elsevier B.V. All rights reserved.

  10. Influence of rare-earth additives (La, Sm and Dy on the microstructure and dielectric properties of doped BaTiO3 ceramics

    Directory of Open Access Journals (Sweden)

    Paunović Vesna

    2010-01-01

    Full Text Available A series of La/Mn, Sm/Mn and Dy/Mn codoped BaTiO3 samples were prepared by the conventional solid state procedure with dopant concentrations ranging from 0.1 up to 2.0 at%. The specimens were sintered at 1320°C and 1350°C in an air atmosphere for two hours. The low doped samples demonstrated a mainly uniform and homogeneous microstructure with average grain sizes ranging from 0.3 μm to 5.0 μm. The appearance of secondary abnormal grains in the fine grain matrix and core-shell structure were observed in highly doped La/BaTiO3 and Dy/BaTiO3 sintered at 1350°C. The low doped samples, sintered at 1350°C, display a high value of dielectric permittivity at room temperature, 6800 for Sm/BaTiO3, 5900 for Dy/BaTiO3 and 3100 for La/BaTiO3. A nearly flat permittivity-response was obtained in specimens with 2.0 at% additive content. Using a modified Curie-Weiss law the Curie-like constant C⁄ and a critical exponent γ were calculated. The obtained values of γ pointed out the diffuse phase transformation in heavily doped BaTiO3 samples.

  11. A theoretical investigation of the interaction of Immucillin-A with N-doped TiO2 anatase nanoparticles: Applications to nanobiosensors and nanocarriers

    Directory of Open Access Journals (Sweden)

    Amirali Abbasi

    2017-02-01

    Full Text Available Objective(s: Adsorption of IMMUCILLIN-A (BCX4430 molecule on the pristine and N-doped TiO2 anatase nanoparticles were studied using the density functional theory (DFT calculations. The adsorption energy analysis indicated that TiO2+IMMUCILLIN-A complexes including OC-substituted TiO2 have higher adsorption energy than the complexes with OT substituted TiO2, thus providing more stable configurations. Methods: The structural properties including bond lengths, adsorption energies and bond angles were analysed. The electronic structure of the adsorption system were investigated in view of the density of states, molecular orbitals and Mulliken charge analysis.Results: The results show that, the interaction of IMMUCILLIN-A drug with N-doped TiO2 nanoparticles is more energetically favorable than the interaction with the pristine ones, suggesting that the N-doped nanoparticles can react with IMMUCILLIN-A drug more efficiently. The Mulliken charge analysis also suggests a charge transfer from IMMUCILLIN-A molecule to the TiO2 nanoparticle.Conclusions: Based on obtained results, it can be concluded that the N-doped TiO2 nanoparticle could be utilized as an efficient candidate for application as highly sensitive nanobiosensors and efficient nanocarriers for IMMUCILLIN-A drugs.

  12. Effect of iron doping on structural and optical properties of TiO2 thin film by sol–gel routed spin coating technique

    Directory of Open Access Journals (Sweden)

    Stephen Lourduraj

    2017-08-01

    Full Text Available Thin films of iron (Fe-doped titanium dioxide (Fe:TiO2 were prepared by sol–gel spin coating technique and further calcined at 450∘C. The structural and optical properties of Fe-doped TiO2 thin films were investigated by X-ray diffraction (XRD, scanning electron microscopy (SEM, ultraviolet–visible spectroscopy (UV–vis and atomic force microscopic (AFM techniques. The XRD results confirm the nanostructured TiO2 thin films having crystalline nature with anatase phase. The characterization results show that the calcined thin films having high crystallinity and the effect of iron substitution lead to decreased crystallinity. The SEM investigations of Fe-doped TiO2 films also gave evidence that the films were continuous spherical shaped particles with a nanometric range of grain size and film was porous in nature. AFM analysis establishes that the uniformity of the TiO2 thin film with average roughness values. The optical measurements show that the films having high transparency in the visible region and the optical band gap energy of Fe-doped TiO2 film with iron (Fe decrease with increase in iron content. These important requirements for the Fe:TiO2 films are to be used as window layers in solar cells.

  13. Vacancy identification in Co+ doped rutile TiO2 crystal with positron annihilation spectroscopy

    Science.gov (United States)

    Qin, X. B.; Zhang, P.; Liang, L. H.; Zhao, B. Z.; Yu, R. S.; Wang, B. Y.; Wu, W. M.

    2011-01-01

    Co-doped rutile TiO2 films were synthesized by ion implantation. Variable energy positron annihilation Doppler broadening spectroscopy and coincidence Doppler broadening measurements were performed for identification of the vacancies. A newly formed type of vacancy can be concluded by the S-W plot and the CDB results indicated that the oxygen vacancy (VO) complex Ti-Co-VO and/or Ti-VO are formed with Co ions implantation and the vacancy concentration is increased with increase of dopant dose.

  14. Synergistic Effects of Sm and C Co-Doped Mixed Phase Crystalline TiO2 for Visible Light Photocatalytic Activity

    Directory of Open Access Journals (Sweden)

    Fuchang Peng

    2017-02-01

    Full Text Available Mixed phase TiO2 nanoparticles with element doping by Sm and C were prepared via a facile sol-gel procedure. The UV-Vis light-diffuse reflectance spectroscopy analysis showed that the absorption region of co-doped TiO2 was shifted to the visible-light region, which was attributed to incorporation of samarium and carbon into the TiO2 lattice during high-temperature reaction. Samarium effectively decreased the anatase-rutile phase transformation. The grain size can be controlled by Sm doping to achieve a large specific surface area useful for the enhancement of photocatalytic activity. The photocatalytic activities under visible light irradiation were evaluated by photocatalytic degradation of methylene blue (MB. The degradation rate of MB over the Sm-C co-doped TiO2 sample was the best. Additionally, first-order apparent rate constants increased by about 4.3 times compared to that of commercial Degusssa P25 under the same experimental conditions. Using different types of scavengers, the results indicated that the electrons, holes, and •OH radicals are the main active species for the MB degradation. The high visible-light photocatalytic activity was attributed to low recombination of the photo-generated electrons and holes which originated from the synergistic effect of the co-doped ions and the heterostructure.

  15. A facile method to synthesize nitrogen and fluorine co-doped TiO{sub 2} nanoparticles by pyrolysis of (NH{sub 4}){sub 2}TiF{sub 6}

    Energy Technology Data Exchange (ETDEWEB)

    Chen Daimei; Jiang Zhongyi; Geng Jiaqing; Zhu Juhong; Yang Dong, E-mail: dyangdong@hotmail.co [Tianjin University, Key Laboratory for Green Chemical Technology, School of Chemical Engineering and Technology (China)

    2009-02-15

    The nitrogen and fluorine co-doped TiO{sub 2} (N-F-TiO{sub 2}) nanoparticles of anatase crystalline structure were prepared by a facile method of (NH{sub 4}){sub 2}TiF{sub 6} pyrolysis, and characterized by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and ultraviolet visible (UV-Vis) spectroscopy etc. With the increase of calcination temperature, (NH{sub 4}){sub 2}TiF{sub 6} decomposed into TiOF{sub 2} and NH{sub 4}TiOF{sub 3} at first, and then formed anatase-type TiO{sub 2} with thin sheet morphology. H{sub 3}BO{sub 3} as oxygen source can promote the formation of anatase TiO{sub 2}, but decrease the F content in the N-F-TiO{sub 2} materials due to the formation of volatile BF{sub 3} during the precursor decomposition. The photocatalytic activity of the obtained N-F-TiO{sub 2} samples was evaluated by the methylene blue degradation under visible light, and all the samples exhibited much higher photocatalytic activity than P25. Moreover, the merits and disadvantages of this proposed method to prepare doped TiO{sub 2} are discussed.

  16. Performance-Microstructure Relations in Ni/CGO Infiltrated Nb-doped SrTiO3 SOFC Anodes

    DEFF Research Database (Denmark)

    Ramos, Tania; Bernuy-Lopez, Carlos; Reddy Sudireddy, Bhaskar

    2012-01-01

    Nb-doped SrTiO3 solid oxide fuel cell (SOFC) anodes, infiltrated with CGO/Ni, were investigated by electrochemical impedance spectroscopy (EIS) and high resolution microscopy techniques, upon varying production and testing parameters. The electrochemical analysis involved a combination of distrib......Nb-doped SrTiO3 solid oxide fuel cell (SOFC) anodes, infiltrated with CGO/Ni, were investigated by electrochemical impedance spectroscopy (EIS) and high resolution microscopy techniques, upon varying production and testing parameters. The electrochemical analysis involved a combination...... of distribution of relaxation times (DRT) and complex non-linear least squares (CNLS) fitting routine. These electrodes were studied as singlephase or as composites with 8YSZ. Sr0.94Ti0.9Nb0.1O3-δ/ 10 vol.% 8YSZ composite infiltrated electrodes were the best overall performers, with enhanced performance stability...

  17. Chromium doped TiO2 sputtered thin films synthesis, physical investigations and applications

    CERN Document Server

    Hajjaji, Anouar; Gaidi, Mounir; Bessais, Brahim; El Khakani, My Ali

    2014-01-01

    This book presents co-sputtered processes ways to produce chrome doped TiO2 thin films onto various substrates such as quartz, silicon and porous silicon. Emphasis is given on the link between the experimental preparation and physical characterization in terms of Cr content. Moreover, the structural, optical and optoelectronic investigations are emphasized throughout. The book explores the potencial applications of devices based on Cr doped TiO2 thin films as gas sensors and in photocatalysis and in the photovoltaic industry. Also, this book provides extensive leads into research literature, and each chapter contains details which aim to develop awareness of the subject and the methods used. The content presented here will be useful for graduate students as well as researchers in materials science, physics, chemistry and engineering.

  18. Room temperature ferromagnetism and phonon properties of pure and doped TiO{sub 2} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Apostolova, I.N. [University of Forestry, Faculty of Forest Industry, 10, Kl. Ohridsky Blvd., 1756 Sofia (Bulgaria); Apostolov, A.T. [University of Architecture, Civil Engineering and Geodesy, Faculty of Hydrotechnics, Department of Physics, 1, Hristo Smirnenski Blvd., 1046 Sofia (Bulgaria); Bahoosh, S.G. [Max Planck Institute of Microstructure Physics, Weinberg 2, 06120 Halle (Germany); Wesselinowa, J.M., E-mail: julia@phys.uni-sofia.bg [University of Sofia, Department of Physics, 5, J. Bouchier Blvd., 1164 Sofia (Bulgaria)

    2014-03-15

    We have considered the origin of RTFM in TiO{sub 2} nanoparticles (NPs). Further we have studied the properties of the E{sub g1} phonon mode. The phonon frequency of anatase TiO{sub 2} NPs increases whereas in the case of rutile TiO{sub 2} NPs it decreases as the particle size decreases. The phonon damping is always enhanced in the nanosized materials. The hardening of the E{sub g1} mode and the softening of the E{sub g3} mode in anatase TiO{sub 2} NPs could be explained with the different anharmonic spin–phonon interaction constants of these modes. The doping effects with different transition metal ions on the E{sub g1} phonon mode are also discussed. - Highlights: • The origin of RTFM in TiO{sub 2} nanoparticles is investigated. • With decreasing of particle size the phonon frequency of anatase and rutile TiO{sub 2} NPs increases and decreases, respectively. • This could be explained with the different anharmonic spin–phonon interaction constants of these modes. • The phonon damping is always enhanced in the nanosized materials. • The doping effects with different transition metal ions on the E{sub g1} phonon mode are also discussed.

  19. Competing magnetic fluctuations in Sr3Ru2O7 probed by Ti doping

    DEFF Research Database (Denmark)

    Hooper, J.; Fang, M.H.; Zhou, M.

    2007-01-01

    We report the effect of nonmagnetic Ti4+ impurities on the electronic and magnetic properties of Sr3Ru2O7. Small amounts of Ti suppress the characteristic peak in magnetic susceptibility near 16 K and result in a sharp upturn in specific heat. The metamagnetic quantum phase transition and related...... anomalous features are quickly smeared out by small amounts of Ti. These results provide strong evidence for the existence of competing magnetic fluctuations in the ground state of Sr3Ru2O7. Ti doping suppresses the low-temperature antiferromagnetic interactions that arise from Fermi surface nesting...

  20. Photoelectrochemical oxidation of ibuprofen via Cu{sub 2}O-doped TiO{sub 2} nanotube arrays

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Qiannan [College of Environment and Energy, South China University of Technology, Guangzhou (China); Peng, Yen-Ping, E-mail: yppeng@thu.edu.tw [Department of Environmental Science and Engineering, Tunghai University, Taichung, Taiwan (China); Chen, Hanlin [College of Environment and Energy, South China University of Technology, Guangzhou (China); Chang, Ken-Lin [School of Environmental Science and Engineering and Institute of Environmental Health and Pollution Control, Guangdong University of Technology, Guangzhou, 51006 China (China); Qiu, Yang-Neng; Lai, Shiau-Wu [Department of Environmental Science and Engineering, Tunghai University, Taichung, Taiwan (China)

    2016-12-05

    Highlights: • A p–n junction material was synthesized to enhance photocatalytic ability. • Cu{sub 2}O-doped TiO{sub 2} nanotube arrays works as a photoanode in a PEC system. • Recombination of photo-generated holes and electrons were greatly reduced. • Synergetic effect was quantified in PEC degradation. • Recombination of photogenerated holes and electrons was greatly enhanced. - Abstract: A p–n junction based Cu{sub 2}O-doped TiO{sub 2} nanotube arrays (Cu{sub 2}O-TNAs) were synthesized and used as a working anode in a photoelectrochemical (PEC) system. The results revealed that the Cu{sub 2}O-TNAs were dominated by the anatase phase and responded significantly to visible light. XPS analyses indicated that with an amount of 24.79% Cu doping into the structure, the band gap of Cu{sub 2}O-TNAs was greatly reduced. SEM images revealed that the supported TiO{sub 2} nanotubes had diameters of approximately 80 nm and lengths of about 2.63 μm. Upon doping with Cu{sub 2}O, the TiO{sub 2} nanotubes maintained their structural integrity, exhibiting no significant morphological change, favoring PEC applications. Under illumination, the photocurrent from Cu{sub 2}O/TNAs was 2.4 times larger than that from TNAs, implying that doping with Cu{sub 2}O significantly improved electron mobility by reducing the rate of recombination of electron-hole pairs. The EIS and Bode plot revealed that the estimated electron lifetimes, τ{sub el}, of TNAs and Cu{sub 2}O/TNAs were 6.91 and 26.26 ms, respectively. The efficiencies of degradation of Ibuprofen by photoelectrochemical, photocatalytic (PC), electrochemical (EC) and photolytic (P) methods were measured.

  1. The Synthesis of Eu{sup 3+} Doped with TiO{sub 2} Nano-Powder and Application as a Pesticide Sensor

    Energy Technology Data Exchange (ETDEWEB)

    Yao, Fei; Sun, Yang; Tan, Chunlei; Wei, Song; Zhang, Xiaojuan; Hu, Xiaoyun; Fan, Jun [Northwest Univ., Xi' an (China)

    2011-12-15

    Using tetrabutyl titanate as precursor, Eu{sup 3+} doped TiO{sub 2} nano-powder was prepared by sol-gel method, the nature of luminescence of nano-powder was studied. The interaction of chlorpyrifos with Eu{sup 3+} doped TiO{sub 2} was studied by absorption and fluorescence spectroscopy. The results indicated the fluorescence intensity of Eu{sup 3+} doped TiO{sub 2} was quenched by chlorpyrifos and the quenching rate constant (kq) was 1.24Χ10{sup 11} L/mol·s according to the Stern-Volmer equation. The dynamics of photoinduced electron transfer from chlorpyrifos to conduction band of TiO{sub 2} nanoparticle was observed and the mechanism of electron transfer had been confirmed by the calculation of free energy change (ΔG{sub et}) by applying Rehm-Weller equation as well as energy level diagram. A new rapid method for detection of chlorpyrifos was established according to the fluorescence intensity of Eu{sup 3+} doped TiO{sub 2} was proportional to chlorpyrifos concentration. The range of detection was 5.0Χ10{sup -10}-2.5Χ10{sup -7}mol/L and the detection limit (3σ) was 3.2Χ10{sup -11} mol/L.

  2. The synergetic effect of V and Fe-co-doping in TiO{sub 2} studied from the DFT + U first-principle calculation

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Baoshun, E-mail: liubaoshun@126.com; Zhao, Xiujian

    2017-03-31

    Highlights: • The effect of Fe and V doping on TiO{sub 2} structure was studied with DFT + U calculation. • V and Fe co-doping affects the formation energies and electronic structure. • V and Fe co-doping causes the synergetic effect on the optical properties. - Abstract: Based on the density functional theory (DFT + U), a detailed study on the energetic, electronic, and optical properties of Fe-, V-, and Fe & V-co-doping anatase and rutile TiO{sub 2} was performed The synergetic effect of Fe & V bimetal co-doping on the optical absorption was discussed on electronic level. Two kinds of co-dopants were considered, which included edge-shared and corner-shared co-doping. It was shown that Fe and V atoms prefer to replace Ti atom in the O-rich contions than in the Ti-rich conditions. Co-doping in anatase reduces the formation energies in both cases, while the formation energies for rutile cannot be decreased. The Bader charge analysis indicates the +3 of Fe atom and +4 of V atom, and the obvious electron exchange between Fe and V atom in co-doping cases can be identified, which indicates the presence of synergetic effect induced by co-doping. The cooperation of Fe & V co-dopants was also supported by the result of projected density of states and spin charge density differences, as the hybridization of Fe3d with V3d orbitals was seen within the TiO{sub 2} forbidden band. Different from single-dopant systems, the V3d-Fe3d co-interaction leads to the formation of some spin mid-gap states, which have an obvious effect on the optical absorptions.

  3. Electrochromic Characteristics of Nitrogen-Doped Graphene/TiO2 Nanocomposite Electrodes

    International Nuclear Information System (INIS)

    Yang, Chien-Hsin; Chen, Shih-Ming; Wang, Tzong-Liu; Shieh, Yeong-Tarng

    2014-01-01

    Nitrogen-doped graphene (NDG)/titanium dioxide (TiO 2 ) nanoparticles were coated on indium-tin oxide (ITO) glass substrates to fabricate NDG-TiO 2 nanocomposite electrodes. 3-methylthiophene (3MT) was electrochemically deposited on the NDG-TiO 2 films to form poly(3-methylthiophene) (P3MT/NDG/TiO 2 ) composite electrochromic electrodes. The introduction of NDG and TiO 2 mesoporous films significantly increased the initial maximum optical contrast (ΔT%) to 70% as compared 41% of pure ITO electrodes, whereas the P3MT/NDG/TiO 2 composite electrodes enhanced the adhesion of P3MT polymers to the NDG/TiO 2 /ITO substrate, thereby increasing the long-term stability of the corresponding electrochromic devices. Experimental results reveal that P3MT/NDG/TiO 2 composite electrodes retained up to 90% of ΔT%, relative to 70% remaining ΔT% of pure ITO electrodes. This illustrates the enhanced long-term stability achieved through the introduction of a NDG-TiO 2 nanocomposite films in electrochromic devices. These devices demonstrated excellent response time characteristics and ΔT% value of 6 s and ca. of 70%, respectively. This work has shown that conductive polymer/NDG/TiO 2 composite electrodes are well suited to electrochromic devices for the promotion of performance and stability

  4. Preparation and characterization of N-I co-doped nanocrystal anatase TiO2 with enhanced photocatalytic activity under visible-light irradiation

    International Nuclear Information System (INIS)

    Zhou Liang; Deng Jian; Zhao Yubao; Liu Wanbing; An Lin; Chen Fei

    2009-01-01

    N-I co-doped TiO 2 nanoparticles were prepared by hydrolysis method, using ammonia and iodic acid as the doping sources and Ti(OBu) 4 as the titanium source. The prepared catalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR) and ultraviolet-visible diffuse reflection spectroscopy (UV-vis DRS). XRD spectra show that N-I-TiO 2 samples calcined at 673 K for 3 h are of anatase structure. XPS analysis of N-I-TiO 2 samples indicates that some N atoms replace O atoms in TiO 2 lattice, and I exist in I 7+ , I - and I 5+ chemical states in the samples. UV-vis DRS results reveal that N-I-TiO 2 had significant optical absorption in the region of 400-600 nm. The photocatalytic activity of catalysts was evaluated by monitoring the photocatalytic degradation of methyl orange (MO). Compared with P25 and mono-doped TiO 2 , N-I-TiO 2 powder shows higher photocatalytic activity under both visible-light (λ > 420 nm) and UV-vis light irradiation. Furthermore, N-I-TiO 2 also displays higher COD removal rate under UV-vis light irradiation.

  5. Combined embedding of N-doping and CaCO{sub 3} surface modification in the TiO{sub 2} photoelectrodes for dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Park, Su Kyung; Yun, Tae Kwan [Department of Chemistry, Keimyung University, Daegu 704-701 (Korea, Republic of); Bae, Jae Young, E-mail: jybae@kmu.ac.kr [Department of Chemistry, Keimyung University, Daegu 704-701 (Korea, Republic of); Won, Yong Sun, E-mail: yswon@pknu.ac.kr [Department of Chemical Engineering, Pukyong National University, Busan 608-739 (Korea, Republic of)

    2013-11-15

    A successive embedding of N-doping and CaCO{sub 3} surface modification was carried out in the TiO{sub 2} photoelectrodes for dye-sensitized solar cells (DSSCs). The combined effect was revealed with the great increase of the open-circuit voltage (V{sub oc}), short-circuit current (J{sub sc}), and photoelectric conversion efficiency (η) of the prepared cells; the efficiency (η) was improved from 5.42% of a commercial TiO{sub 2} photoelectrode to 7.47% of an unmodified N-doped electrode, and to 9.03% of a N-doped and CaCO{sub 3} surface modified electrode. An enhanced photoresponse in N-doped TiO{sub 2} nanoparticles generate more photo-excited electrons in adsorbed dye, as supported by measured UV–vis diffuse reflectance spectra and incident photon to current conversion efficiency (IPCE). A successive CaCO{sub 3} surface modification then form a barrier on the surface of N-doped TiO{sub 2} particles, suppressing charge recombination of photo-generated electrons from N-doped TiO{sub 2} to dye or electrolyte, and thus extending their life time in the electrode, as supported by electron impedance spectroscopy (EIS). Furthermore, the higher basicity of the CaCO{sub 3} modified TiO{sub 2} facilitates the dye adsorption, as supported by the direct measurement of the amount of adsorbed dye.

  6. Improved ferroelectric and pyroelectric properties of Pb-doped SrBi4Ti4O15 ceramics for high temperature applications

    International Nuclear Information System (INIS)

    Venkata Ramana, E.; Graça, M.P.F.; Valente, M.A.; Bhima Sankaram, T.

    2014-01-01

    Highlights: • Sr 1−x Pb x Bi 4 Ti 4 O 15 (SPBT, x = 0 − 0.4) ceramics were synthesized by soft chemical method. • X-ray diffraction analysis confirmed the formation of bismuth layered structure. • SEM images showed plate like grain morphology with random orientation of plate faces. • Pb-doping resulted in improved ferroelectricity of SrBi 4 Ti 4 O 15 ceramics. • Pb-doped SrBi 4 Ti 4 O 15 exhibited improved pyroelectric properties with high T C . -- Abstract: Ferroelectric properties of Pb-modified strontium bismuth titanate ceramics with chemical formula Sr 1−x Pb x Bi 4 Ti 4 O 15 (x = 0–0.4) were investigated. Polycrystalline ceramics were synthesized by soft chemical method to study the effect of Pb-doping on its physical properties. X-ray diffraction analysis revealed a bismuth layered structure for all the compounds. The doping resulted in an increased tetragonal strain and improved ferroelectric properties. Scanning electron microscope images showed plate like grain morphology with random orientation of platelets. The ferroelectric transition temperature of the ceramics increased systematically from 525 °C to 560 °C with the increase of doping concentration. The piezoelectric coefficient (d 33 ) of the ceramics was enhanced significantly with Pb doping, exhibiting a maximum value of 21.8 pC/N for 40 mol.% Pb-doped SBT. Pyroelectric studies carried out using the Byer–Roundy method indicated that the modified SBT ceramics are promising candidates for high temperature pyroelectric applications

  7. Microstructure and electric characteristics of AETiO3 (AE=Mg, Ca, Sr doped CaCu3Ti4O12 thin films prepared by the sol–gel method

    Directory of Open Access Journals (Sweden)

    Dong Xu

    2015-10-01

    Full Text Available This paper focuses on the effects of alkline-earth metal titante AETiO3 (AE=Mg, Ca, Sr doping on the microstructure and electric characteristics of CaCu3Ti4O12 thin films prepared by the sol–gel method. The results showed that the grain size of CCTO thin films could be increased by MgTiO3 doping. The movement of the grain boundaries was impeded by the second phases of CaTiO3 and SrTiO3 concentrating at grain boundaries in CaTiO3 and SrTiO3 doped CCTO thin films. Rapid ascent of dielectric constant could be observed in 0.1Mg TiO3 doped CCTO thin films, which was almost as three times high as pure CCTO thin film and the descent of the dielectric loss at low frequency could also be observed. In addition, the nonlinear coefficient (α, threshold voltage (VT and leakage current (IL of AETiO3 doped CCTO thin films (AE=Mg, Ca, Sr showed different variation with the increasing content of the MgTiO3, CaTiO3 and SrTiO3.

  8. New insights on the synthesis and electronic transport in bulk polycrystalline Pr-doped SrTiO3−δ

    International Nuclear Information System (INIS)

    Dehkordi, Arash Mehdizadeh; Bhattacharya, Sriparna; Darroudi, Taghi; Alshareef, Husam N.; Tritt, Terry M.

    2015-01-01

    Recently, we have reported a significant enhancement in the electronic and thermoelectric properties of bulk polycrystalline SrTiO 3 ceramics via praseodymium doping. This improvement was originated from the simultaneous enhancement in the thermoelectric power factor and reduction in thermal conductivity, which was contributed to the non-uniform distribution of Pr dopants. In order to further understand the underlying mechanism, we herein investigate the role of praseodymium doping source (Pr 2 O 3 versus Pr 6 O 11 ) on the synthesis and electronic transport in Pr-doped SrTiO 3 ceramics. It was observed that the high-temperature electronic transport properties are independent of the choice of praseodymium doping source for samples prepared following our synthesis strategy. Theoretical calculations were also performed in order to estimate the maximum achievable power factor and the corresponding optimal carrier concentration. The result suggests the possibility of further improvement of the power factor. This study should shed some light on the superior electronic transport in bulk polycrystalline Pr-doped SrTiO 3 ceramics and provide new insight on further improvement of the thermoelectric power factor

  9. New insights on the synthesis and electronic transport in bulk polycrystalline Pr-doped SrTiO3−δ

    KAUST Repository

    Dehkordi, Arash Mehdizadeh

    2015-02-07

    Recently, we have reported a significant enhancement in the electronic and thermoelectric properties of bulk polycrystalline SrTiO3 ceramics via praseodymium doping. This improvement was originated from the simultaneous enhancement in the thermoelectric power factor and reduction in thermal conductivity, which was contributed to the non-uniform distribution of Pr dopants. In order to further understand the underlying mechanism, we herein investigate the role of praseodymium doping source (Pr2O3 versus Pr6O11) on the synthesis and electronic transport in Pr-doped SrTiO3 ceramics. It was observed that the high-temperature electronic transport properties are independent of the choice of praseodymium doping source for samples prepared following our synthesis strategy. Theoretical calculations were also performed in order to estimate the maximum achievable power factor and the corresponding optimal carrier concentration. The result suggests the possibility of further improvement of the power factor. This study should shed some light on the superior electronic transport in bulk polycrystalline Pr-doped SrTiO3 ceramics and provide new insight on further improvement of the thermoelectric power factor.

  10. Novel three-dimensionally ordered macroporous Fe{sup 3+}-doped TiO{sub 2} photocatalysts for H{sub 2} production and degradation applications

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Xiaoqing; Xue, Chao; Yang, Bolun; Yang, Guidong, E-mail: guidongyang@xjtu.edu.cn

    2017-02-01

    Highlights: • 3DOM Fe{sup 3+}-doped TiO{sub 2} photocatalyst was prepared. • 3DOM structure showed high activity for decomposition of the RhB and the generation of H{sub 2}. • 3DOM structure provided interfacial reaction sites and optical absorption active sites. • The energy level from Fe{sup 3+} centers were existed in the band gap of TiO{sub 2}. • 3DOM structure promoted the separation of charge carriers. - Abstract: Novel three-dimensionally ordered macroporous (3DOM) Fe{sup 3+}-doped TiO{sub 2} photocatalysts were prepared using a colloidal crystal template method with low-cost raw material including ferric trichloride, isopropanol, tetrabutyl titanate and polymethyl methacrylate. The as-prepared 3DOM Fe{sup 3+}-doped TiO{sub 2} photocatalysts were characterized by various analytical techniques. TEM and SEM results showed that the obtained photocatalysts possess well-ordered macroporous structure in three dimensional orientations. As proved by XPS and EDX analysis that Fe{sup 3+} ions have been introduced TiO{sub 2} lattice and the doped Fe{sup 3+} ions can act as the electron acceptor/donor centers to significantly enhance the electron transfer from the bulk to surface of TiO{sub 2}, resulting in more electrons could take part in the oxygen reduction process thereby decreasing the recombination rate of photogenerated charges. Meanwhile, the 3DOM architecture with the feature of interfacial chemical reaction active sites and optical absorption active sites is remarkably favorable for the reactant transfer and light trapping in the photoreaction process. As a result, the 3DOM Fe{sup 3+}-doped TiO{sub 2} photocatalysts show the considerably higher photocatalytic activity for decomposition of the Rhodamine B (RhB) and the generation of hydrogen under visible light irradiation due to the synergistic effects of open, interconnected macroporous network and metal ion doping.

  11. Fabrication and characterization of polyvinyl alcohol/metal (Ca, Mg, Ti) doped zirconium phosphate nanocomposite films for scaffold-guided tissue engineering application

    International Nuclear Information System (INIS)

    Kalita, Himani; Pal, Pallabi; Dhara, Santanu; Pathak, Amita

    2017-01-01

    Nanocomposite films of polyvinyl alcohol (PVA) and zirconium phosphate (ZrP)/doped ZrP (doped with Ca, Mg, Ti) nanoparticles have been developed by solvent casting method to assess their potential as matrix material in scaffold-guided tissue engineering application. The prepared ZrP and doped ZrP nanoparticles as well as the nanocomposite films were characterized by various spectroscopic and microscopic techniques. Nanoindentation studies revealed improved nanomechanical properties in the PVA/doped ZrP nanocomposite films (highest for PVA/Ti doped ZrP: hardness = 262.4 MPa; elastic modulus = 5800 MPa) as compared to the PVA/ZrP and neat PVA films. In-vitro cell culture experiments carried out to access the cellular viability, attachment, proliferation, and migration on the substrates, using mouse fibroblast (3T3) cell lines, inferred enhanced bioactivity in the PVA/doped ZrP nanocomposite films (highest for PVA/Ca doped ZrP) in contrast to PVA/ZrP and neat PVA films. Controlled biodegradability as well as swelling behavior, superior bioactivity and improved mechanical properties of the PVA/doped ZrP nanocomposite films make them promising matrix materials for scaffold-guided tissue engineering application. - Highlights: • PVA/ZrP (undoped/doped with Ca, Mg and Ti) nanocomposite scaffolds were developed. • The nanocomposites were prepared via solvent casting method. • PVA/doped ZrP films exhibited enhanced mechanical properties than PVA/undoped ZrP. • Excellent bioactivity was observed in the PVA/doped ZrP films than PVA/undoped ZrP.

  12. Fabrication and characterization of polyvinyl alcohol/metal (Ca, Mg, Ti) doped zirconium phosphate nanocomposite films for scaffold-guided tissue engineering application

    Energy Technology Data Exchange (ETDEWEB)

    Kalita, Himani [Department of Chemistry, Indian Institute of Technology Kharagpur, West Bengal 721302 (India); Pal, Pallabi; Dhara, Santanu [School of Medical Science and Technology, Indian Institute of Technology Kharagpur, West Bengal 721302 (India); Pathak, Amita, E-mail: ami@chem.iitkgp.ernet.in [Department of Chemistry, Indian Institute of Technology Kharagpur, West Bengal 721302 (India)

    2017-02-01

    Nanocomposite films of polyvinyl alcohol (PVA) and zirconium phosphate (ZrP)/doped ZrP (doped with Ca, Mg, Ti) nanoparticles have been developed by solvent casting method to assess their potential as matrix material in scaffold-guided tissue engineering application. The prepared ZrP and doped ZrP nanoparticles as well as the nanocomposite films were characterized by various spectroscopic and microscopic techniques. Nanoindentation studies revealed improved nanomechanical properties in the PVA/doped ZrP nanocomposite films (highest for PVA/Ti doped ZrP: hardness = 262.4 MPa; elastic modulus = 5800 MPa) as compared to the PVA/ZrP and neat PVA films. In-vitro cell culture experiments carried out to access the cellular viability, attachment, proliferation, and migration on the substrates, using mouse fibroblast (3T3) cell lines, inferred enhanced bioactivity in the PVA/doped ZrP nanocomposite films (highest for PVA/Ca doped ZrP) in contrast to PVA/ZrP and neat PVA films. Controlled biodegradability as well as swelling behavior, superior bioactivity and improved mechanical properties of the PVA/doped ZrP nanocomposite films make them promising matrix materials for scaffold-guided tissue engineering application. - Highlights: • PVA/ZrP (undoped/doped with Ca, Mg and Ti) nanocomposite scaffolds were developed. • The nanocomposites were prepared via solvent casting method. • PVA/doped ZrP films exhibited enhanced mechanical properties than PVA/undoped ZrP. • Excellent bioactivity was observed in the PVA/doped ZrP films than PVA/undoped ZrP.

  13. Cooperative doping effects of Ti and nano-SiC on transport critical current density and grain connectivity of in situ MgB{sub 2} tapes

    Energy Technology Data Exchange (ETDEWEB)

    Pan, X.F., E-mail: PAN.Xifeng@nims.go.jp [National Institute for Materials Science, Superconducting Materials Research Center, 1-2-1, Sengen, Tsukuba, Ibaraki 305-0047 (Japan)] [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Chengdu 610031 (China); Matsumoto, A.; Kumakura, H. [National Institute for Materials Science, Superconducting Materials Research Center, 1-2-1, Sengen, Tsukuba, Ibaraki 305-0047 (Japan); Cheng, C.H.; Zhao, Y. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Chengdu 610031 (China)] [School of Materials Science and Engineering, University of New South Wales, Sydney 2052, NSW (Australia)

    2011-11-15

    We studied the cooperative doping effects of Ti and nano-SiC on transport J{sub c} and grain connectivity of MgB{sub 2} tape. Ti doping significantly weakens the current dependence of T{sub c} of MgB{sub 2} tapes at self-field, and does not change T{sub c} or slightly increases T{sub c}. Further Ti adding can enhance in-field J{sub c} performance of SiC doped MgB{sub 2} tapes by a factor of 50-100% at 4.2 K and 10 T. Ti addition improves the J{sub c} performance of undoped and SiC doped MgB{sub 2} by modifying their grains connection. By now, nano-SiC powder (20-30 nm) is still the most effective additive for improving upper critical field and critical current density of MgB{sub 2}-based superconducting materials. However, some decomposed carbon aggregates at grain boundaries and results in serious weak-links of MgB{sub 2} grains, and these weak-links limit the further improvement of critical current density, J{sub c} of MgB{sub 2}, especially at lower fields. Ti doping is reported to increase the compactness of MgB{sub 2}, and modify its intergranular coupling by forming ultrathin TiB{sub 2} layer at grain boundaries. In this work, we studied the cooperative doping effects of Ti and nano-SiC on transport J{sub c} and grain connectivity of MgB{sub 2} and the possibility to improve transport J{sub c} of SiC doped MgB{sub 2} by introducing Ti additive. The results suggest the Ti addition can obviously improve J{sub c} of MgB{sub 2} at lower fields and also enhance the J{sub c} of SiC doped MgB{sub 2} by improving their grain connectivity which shows serious intergranular weak-links.

  14. Facile Synthesis and Characterization of N-Doped TiO2 Photocatalyst and Its Visible-Light Activity for Photo-Oxidation of Ethylene

    Directory of Open Access Journals (Sweden)

    Yu-Hao Lin

    2015-01-01

    Full Text Available A facile wet chemical method was adopted for preparing highly photoactive nitrogen doped TiO2 (N-TiO2 powders with visible responsive capability, which could be achieved by the hydrolysis of titanium isopropoxide (TTIP in the ammonium hydroxide precursor solution in various concentrations and then calcined at different temperatures. The N-TiO2 powders were characterized, and the photocatalytic activity was evaluated for the photocatalytic oxidation of ethylene gas under visible light irradiation to optimize the synthesizing conditions of N-TiO2 catalyst. The N-TiO2 photocatalytic powders were calcined in a range of temperatures from 300 to 600°C and obviously found to have greater photocatalytic activities than commercial TiO2 P25. The strong absorption in the visible light region could be ascribed to good crystallization and adapted sinter temperature of as prepared sample. XPS test demonstrated that the N was doped into TiO2 lattice and made an interstitial formation (Ti-O-N, and N doping also retarded the phase transformation from anatase to rutile as well. The N-TiO2 catalyst prepared with 150 mL ammonium hydroxide added and calcined at 500°C showed the best photocatalytic activity. The experimental results also proved the enhanced photoactivity of N-TiO2 material depends on the synthesizing conditions.

  15. Enhanced Visible Light Photocatalytic Activity of V2O5 Cluster Modified N-Doped TiO2 for Degradation of Toluene in Air

    Directory of Open Access Journals (Sweden)

    Fan Dong

    2012-01-01

    Full Text Available V2O5 cluster-modified N-doped TiO2 (N-TiO2/V2O5 nanocomposites photocatalyst was prepared by a facile impregnation-calcination method. The effects of V2O5 cluster loading content on visible light photocatalytic activity of the as-prepared samples were investigated for degradation of toluene in air. The results showed that the visible light activity of N-doped TiO2 was significantly enhanced by loading V2O5 clusters. The optimal V2O5 loading content was found to be 0.5 wt.%, reaching a removal ratio of 52.4% and a rate constant of 0.027 min−1, far exceeding that of unmodified N-doped TiO2. The enhanced activity is due to the deposition of V2O5 clusters on the surface of N-doped TiO2. The conduction band (CB potential of V2O5 (0.48 eV is lower than the CB level of N-doped TiO2 (−0.19 V, which favors the photogenerated electron transfer from CB of N-doped TiO2 to V2O5 clusters. This function of V2O5 clusters helps promote the transfer and separation of photogenerated electrons and holes. The present work not only displays a feasible route for the utilization of low cost V2O5 clusters as a substitute for noble metals in enhancing the photocatalysis but also demonstrates a facile method for preparation of highly active composite photocatalyst for large-scale applications.

  16. Synthesis and electrochemical properties of Ti4+ doped Li3-xFe2-xTix(PO4)3/C cathode materials

    International Nuclear Information System (INIS)

    Liu Zhanqiang; Huang Fuqiang; Sun Junkang

    2011-01-01

    Highlights: → Li 3-x Fe 2-x Ti x (PO 4 ) 3 /C composite cathodes were prepared by ball-milling method. Ti-doping can improve the electrochemical property of Li 3 Fe 2 (PO 4 ) 3 . → The optimized doping level was found to be x = 0.2. → The second phase of LiTi 2 (PO 4 ) 3 will emerge if the doping level higher than 0.2. - Abstract: Li 3-x Fe 2-x Ti x (PO 4 ) 3 /C (x = 0-0.4) cathodes designed with Fe doped by Ti was studied. Both Li 3 Fe 2 (PO 4 ) 3 /C (x = 0) and Li 2.8 Fe 1.8 Ti 0.2 (PO 4 ) 3 /C (x = 0.2) possess two plateau potentials of Fe 3+ /Fe 2+ couple (around 2.8 V and 2.7 V vs. Li + /Li) upon discharge observed from galvanostatic charge/discharge and cyclic voltammetry. Li 2.8 Fe 1.8 Ti 0.2 (PO 4 ) 3 /C has higher reversibility and better capacity retention than that of the undoped Li 3 Fe 2 (PO 4 ) 3 /C. A much higher specific capacity of 122.3 mAh/g was obtained at C/20 in the first cycle, approaching the theoretical capacity of 128 mAh/g, and a capacity of 100.1 mAh/g was held at C/2 after the 20th cycle.

  17. Nb and Ta layer doping effects on the interfacial energetics and electronic properties of LaAlO3/SrTiO3 heterostructure: first-principles analysis.

    Science.gov (United States)

    Nazir, Safdar; Behtash, Maziar; Cheng, Jianli; Luo, Jian; Yang, Kesong

    2016-01-28

    The two-dimensional electron gas (2DEG) formed at the n-type (LaO)(+1)/(TiO2)(0) interface in the polar/nonpolar LaAlO3/SrTiO3 (LAO/STO) heterostructure (HS) has emerged as a prominent research area because of its great potential for nanoelectronic applications. Due to its practical implementation in devices, desired physical properties such as high charge carrier density and mobility are vital. In this respect, 4d and 5d transition metal doping near the interfacial region is expected to tailor electronic properties of the LAO/STO HS system effectively. Herein, we studied Nb and Ta-doping effects on the energetics, electronic structure, interfacial charge carrier density, magnetic moment, and the charge confinements of the 2DEG at the n-type (LaO)(+1)/(TiO2)(0) interface of LAO/STO HS using first-principles density functional theory calculations. We found that the substitutional doping of Nb(Ta) at Ti [Nb(Ta)@Ti] and Al [Nb(Ta)@Al] sites is energetically more favorable than that at La [Nb(Ta)@La] and Sr [Nb(Ta)@Sr] sites, and under appropriate thermodynamic conditions, the changes in the interfacial energy of HS systems upon Nb(Ta)@Ti and Nb(Ta)@Al doping are negative, implying that the formation of these structures is energetically favored. Our calculations also showed that Nb(Ta)@Ti and Nb(Ta)@Al doping significantly improve the interfacial charge carrier density with respect to that of the undoped system, which is because the Nb(Ta) dopant introduces excess free electrons into the system, and these free electrons reside mainly on the Nb(Ta) ions and interfacial Ti ions. Hence, along with the Ti 3d orbitals, the Nb 4d and Ta 5d orbitals also contribute to the interfacial metallic states; accordingly, the magnetic moments on the interfacial Ti ions increase significantly. As expected, the Nb@Al and Ta@Al doped LAO/STO HS systems show higher interfacial charge carrier density than the undoped and other doped systems. In contrast, Nb@Ti and Ta@Ti doped systems may

  18. Magnetic and Mössbauer studies of pure and Ti-doped YFeO _3 nanocrystalline particles prepared by mechanical milling and subsequent sintering

    International Nuclear Information System (INIS)

    Khalifa, N. O.; Widatallah, H. M.; Gismelseed, A. M.; Al-Mabsali, F. N.; Sofin, R. G. S.; Pekala, M.

    2016-01-01

    Single-phased nanocrystalline particles of pure and 10 % Ti "4"+-doped perovskite-related YFeO _3were prepared via mechanosynthesis at 450"∘C. This temperature is ∼150–350 "∘C lower than those at which the materials, in bulk form, are normally prepared. Rietveld refinements of the X-ray diffraction patterns reveal that the dopant Ti "4"+ ions prefer interstitial octahedral sites in the orthorhombic crystal lattice rather than those originally occupied by the expelled Fe "3"+ ions. Magnetic measurements show canted antiferromagnetism in both types of nanoparticles. Doping with Ti "4"+ lowers the Néel temperature of the YFeO _3 nanoparticles from ∼ 586 K to ∼ 521 K. The Ti "4"+-doped YFeO _3 nanoparticles exhibit enhanced magnetization and coercivity but less magnetic hyperfine fields relative to the un-doped nanoparticles. The "5"7Fe Mössbauer spectra show ∼ 15 % of the YFeO _3 nanoparticles and ∼22 of Ti "4"+-doped YFeO _3 ones to be superparamagnetic with blocking temperatures < 78 K. The broadened magnetic components in the "5"7Fe Mössbauer spectra suggest size-dependent hyperfine magnetic fields at the "5"7Fe nuclear sites and were associated with collective magnetic excitations. The "5"7Fe Mössbauer spectra show the local environments of the Fe "3"+ ions in the superparamagnetic nanoparticles to be more sensitive to the presence of the Ti "4"+ ions relative to those in the larger magnetic nanoparticles.

  19. The magnetic characterization of Fe doped TiO{sub 2} semiconducting oxide nanoparticles synthesized by sol–gel method

    Energy Technology Data Exchange (ETDEWEB)

    Yeganeh, M., E-mail: mahboubeh.yeganeh@yahoo.co.uk [Department of Physics, Kosar University of Bojnord, P.O. Box 94104455 (Iran, Islamic Republic of); Shahtahmasebi, N.; Kompany, A. [Department of Physics, Ferdowsi University of Mashhad (Iran, Islamic Republic of); Karimipour, M. [Department of Physics, Vali-e-Asr University of Rafsanjan (Iran, Islamic Republic of); Razavi, F. [Department of Physics, Brock University (Canada); Nasralla, N.H.S. [Electron Microscope and Thin Film Department, Physics Division, 33 El Buhouth st., Dokki, 12622 Giza (Egypt); Šiller, L. [School of Chemical Engineering and Advanced Materials, Newcastle University, NE1 7RU (United Kingdom)

    2017-04-15

    In this work Fe doped TiO{sub 2} nanoparticles were synthesized at different Fe/Ti molar ratio from 1% to 5% by sol-gel technique. The post annealing of the samples was carried out at T=400, 600, and 800 °C. HRTEM of the samples revealed that the mean size of the nanoparticles increases from about 8 nm to about 100 nm as the annealing temperature increased. SQUID magnetometry of 1% and 5% Fe doped TiO{sub 2} has shown mixed ferromagnetic and paramagnetic phases within the crystal while ferromagnetic order with T{sub c} about 350 K was only observed in 5% Fe:TiO{sub 2} sample annealed at T=800 °C. The oxygen vacancy mediated ferromagnetic (FM) interaction could be responsible for the observed FM.

  20. Improved conversion efficiency of dye sensitized solar cell using Zn doped TiO{sub 2}-ZrO{sub 2} nanocomposite

    Energy Technology Data Exchange (ETDEWEB)

    Tomar, Laxmi J., E-mail: laxmi-tomar86@yahoo.com; Bhatt, Piyush J.; Desai, Rahul K.; Chakrabarty, B. S.; Panchal, C. J. [Department of Applied Physics, Faculty of Technology and Engineering, The M. S. University of Baroda, Vadodara, India-390003 (India)

    2016-05-23

    TiO{sub 2}-ZrO{sub 2} and Zn doped TiO{sub 2}-ZrO{sub 2} nanocomposites were prepared by hydrothermal method for dye sensitized solar cell (DSSC) application. The structural and optical properties were investigated by X –ray diffraction (XRD) and UV-Visible spectroscopy respectively. XRD results revealed the formation of material in nano size. The average crystallite size is 22.32 nm, 17.41 nm and 6.31 nm for TiO{sub 2}, TiO{sub 2}-ZrO{sub 2} and Zn doped TiO{sub 2}-ZrO{sub 2} nanocomposites respectively. The optical bandgap varies from 2.04 eV to 3.75 eV. Dye sensitized solar cells were fabricated using the prepared material. Pomegranate juice was used as a sensitizer and graphite coated conducting glass plate was used as counter electrode. The I – V characteristics were recorded to measure photo response of DSSC. Photovoltaic parameter like open circuit voltage, power conversion efficiency, and fill factor were evaluated for fabricated solar cell. The power conversion efficiency of DSSC fabricated with TiO{sub 2}, TiO{sub 2}-ZrO{sub 2} and Zn doped TiO{sub 2}-ZrO{sub 2} nanocomposites were found 0.71%, 1.97% and 4.58% respectively.

  1. Annealing-free synthesis of C-N co-doped TiO{sub 2} hierarchical spheres by using amine agents via microwave-assisted solvothermal method and their photocatalytic activities

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Yu-Chun, E-mail: yuchunwu@mail.ncku.edu.tw; Ju, Lung-Shen

    2014-08-01

    Highlights: • The synthesis method for C-N co-doped TiO{sub 2} hierarchical spheres is proposed. • Microwave-assisted solvothermal method is applied. • C and N are doped into TiO{sub 2} via a direct chelating reaction of amine compounds. • The photodegradation rate is eightfold higher than the commercial P25 powders. - Abstract: The annealing-free synthesis of C-N co-doped TiO{sub 2} hierarchical spheres is proposed in this study. C and N were doped into the TiO{sub 2} structure via a direct chelating process to the Ti-precursor by using different amine agents, including hexadecylamine (HDA), diethylamine (DEA), trimethylamine (TMA), and diethylenetriamine (DETA). C-N co-doped TiO{sub 2} spheres (300 nm to 500 nm) composed of nanoparticles approximately 11 nm to 13 nm in size were obtained via an efficient microwave-assisted solvothermal reaction at 190 °C for 60 min. The effects of C and N doping by using different amine compounds on the bandgap energy and photocatalytic performance of TiO{sub 2} were investigated. Among the amine compounds, DETA provided the highest chelating efficiency because it provides two primary amine groups, which resulted in the highest C and N doping concentrations and the largest degree of bandgap narrowing (2.77 eV); nevertheless, the high chelating ratio of C and N restrained the crystallization of TiO{sub 2} and considerably decreased its photocatalytic activity. The use of TMA produced optimal C and N doping concentrations, which effectively reduced the bandgap of TiO{sub 2} to 2.85 eV without affecting its crystallization. Its photodecomposition activity to rhodamine B was eightfold of that of commercial Degussa P25 powders under visible light irradiation.

  2. Cr3+ and Nb5+ co-doped Ti2Nb10O29 materials for high-performance lithium-ion storage

    Science.gov (United States)

    Yang, Chao; Yu, Shu; Ma, Yu; Lin, Chunfu; Xu, Zhihao; Zhao, Hua; Wu, Shunqing; Zheng, Peng; Zhu, Zi-Zhong; Li, Jianbao; Wang, Ning

    2017-08-01

    Ti2Nb10O29 is an advanced anode material for lithium-ion batteries due to its large specific capacity and high safety. However, its poor electronic/ionic conductivity significantly limits its rate capability. To tackle this issue, a Cr3+-Nb5+ co-doping is employed, and a series of CrxTi2-2xNb10+xO29 compounds are prepared. The co-doping does not change the Wadsley-Roth shear structure but increases the unit-cell volume and decreases the particle size. Due to the increased unit-cell volumes, the co-doped samples show increased Li+-ion diffusion coefficients. Experimental data and first-principle calculations reveal significantly increased electronic conductivities arising from the formation of impurity bands after the co-doping. The improvements of the electronic/ionic conductivities and the smaller particle sizes in the co-doped samples significantly contribute to improving their electrochemical properties. During the first cycle at 0.1 C, the optimized Cr0.6Ti0.8Nb10.6O29 sample delivers a large reversible capacity of 322 mAh g-1 with a large first-cycle Coulombic efficiency of 94.7%. At 10 C, it retains a large capacity of 206 mAh g-1, while that of Ti2Nb10O29 is only 80 mAh g-1. Furthermore, Cr0.6Ti0.8Nb10.6O29 shows high cyclic stability as demonstrated in over 500 cycles at 10 C with tiny capacity loss of only 0.01% per cycle.

  3. Surface energy effects on the stability of anatase and rutile nanocrystals: A predictive diagram for Nb_2O_5-doped-TiO_2

    International Nuclear Information System (INIS)

    Silva, Andre Luiz da; Hotza, Dachamir; Castro, Ricardo H.R.

    2017-01-01

    Highlights: • Anatase-rutile phase transition diagram was built for nano Nb_2O_5-doped-TiO_2. • Nb_2O_5-doping postpones the anatase-to-rutile transition. • The stability crossover for TiO_2 was 17.3 nm, for 2 mol% Nb_2O_5-doped-TiO_2 ∼30 nm. • The surface energy for Nb_2O_5-doped-TiO_2 decreases systematically with Nb concentration. - Abstract: Titanium dioxide nanoparticles are widely used for photocatalysis, and the relative fraction of titanium dioxide polymorph, i.e. anatase, rutile, or brookite, significantly affects the final performance. Even though conventional phase diagrams indicate a higher stability for the rutile polymorph, it is well established that nanosizes benefit the anatase phase due to its smaller surface energy. However, doping elements are expected to change this behavior, once changes in both surface and bulk energies may occur. Nb_2O_5 is commonly added to TiO_2 to allow property control. However, the effect of niobium on the relative stability of anatase and rutile phases is not well understood from the thermodynamic point of view. The objective of this work was to build a new predictive nanoscale phase diagram for Nb_2O_5-doped TiO_2. Water adsorption microcalorimetry and high temperature oxide melt solution were used to obtain the surface and bulk enthalpies. The phase diagram obtained shows the stable titania polymorph as a function of the composition and size.

  4. Optical and electrical properties of Ti(Cr)O_2:N thin films deposited by magnetron co-sputtering

    International Nuclear Information System (INIS)

    Kollbek, K.; Szkudlarek, A.; Marzec, M.M.; Lyson-Sypien, B.; Cecot, M.; Bernasik, A.; Radecka, M.; Zakrzewska, K.

    2016-01-01

    Graphical abstract: - Highlights: • Co-doped well-crystallized stoichiometric Ti(Cr)O_2:N thin films are deposited. • Magnetron sputtering of ceramic TiO_2 target is a new strategy for co-doping. • Bigger contribution from substitutionally incorporated nitrogen is seen in XPS. • Significant red shift of the fundamental absorption edge is obtained. - Abstract: The paper deals with TiO_2-based thin films, doped with Cr and N, obtained by magnetron co-sputtering from titanium dioxide ceramic and chromium targets in Ar + N_2 atmosphere. Co-doped samples of Ti(Cr)O_2:N are investigated from the point of view of morphological, crystallographic, optical, and electrical properties. Characterization techniques such as: X-ray diffraction, XRD, scanning electron microscopy, SEM, atomic force microscopy, AFM, Energy Dispersive X-ray spectroscopy, EDX, X-ray photoelectron spectroscopy, XPS, optical spectrophotometry as well as impedance spectroscopy are applied. XRD reveals TiO_2 and TiO_2:N thin films are well crystallized as opposed to those of TiO_2:Cr and Ti(Cr)O_2:N. XPS spectra confirm that co-doping has been successfully performed with the biggest contribution from the lower binding energy component of N 1s peak at 396 eV. SEM analysis indicates uniform and dense morphology without columnar growth. Comparison between the band gaps indicates a significant shift of the absorption edge towards visible range from 3.69 eV in the case of non-stoichiometric Ti(Cr)O_2_−_x:N to 2.78 eV in the case of stoichiometric Ti(Cr)O_2:N which should be attributed to the incorporation of both dopants at substitutional positions in TiO_2 lattice. Electrical conductivity of stoichiometric Ti(Cr)O_2:N increases in comparison to co-doped nonstoichiometric TiO_2_−_x thin film and reaches almost the same value as that of TiO_2 stoichiometric film.

  5. Defect types and room temperature ferromagnetism in N-doped rutile TiO2 single crystals

    Science.gov (United States)

    Qin, Xiu-Bo; Li, Dong-Xiang; Li, Rui-Qin; Zhang, Peng; Li, Yu-Xiao; Wang, Bao-Yi

    2014-06-01

    The magnetic properties and defect types of virgin and N-doped TiO2 single crystals are probed by superconducting quantum interference device (SQUID), X-ray photoelectron spectroscopy (XPS), and positron annihilation analysis (PAS). Upon N doping, a twofold enhancement of the saturation magnetization is observed. Apparently, this enhancement is not related to an increase in oxygen vacancy, rather to unpaired 3d electrons in Ti3+, arising from titanium vacancies and the replacement of O with N atoms in the rutile structure. The production of titanium vacancies can enhance the room temperature ferromagnetism (RTFM), and substitution of O with N is the onset of ferromagnetism by inducing relatively strong ferromagnetic ordering.

  6. Band-gap narrowing of TiO2 films induced by N-doping

    International Nuclear Information System (INIS)

    Nakano, Y.; Morikawa, T.; Ohwaki, T.; Taga, Y.

    2006-01-01

    N-doped TiO 2 films were deposited on n + -GaN/Al 2 O 3 substrates by reactive magnetron sputtering and subsequently crystallized by annealing at 550 o C in flowing N 2 gas. The N-doping concentration was ∼8.8%, as determined from X-ray photoelectron spectroscopy measurements. Deep-level optical spectroscopy measurements revealed two characteristic deep levels located at 1.18 and 2.48 eV below the conduction band. The 1.18 eV level is probably attributable to the O vacancy state and can be active as an efficient generation-recombination center. Additionally, the 2.48 eV band is newly introduced by the N-doping and contributes to band-gap narrowing by mixing with the O 2p valence band

  7. Major enhancement of the thermoelectric performance in Pr/Nb-doped SrTiO3 under strain

    KAUST Repository

    Amin, B.; Alshareef, Husam N.; Schwingenschlö gl, Udo; Singh, Nirpendra; Tritt, T. M.

    2013-01-01

    site generate n-type doping and thus improve the thermoelectric performance as compared to pristine SrTiO3. Further enhancement is achieved by the application of strain, for example, of the Seebeck coefficient by 21% for Sr0.95Pr0.05TiO3 and 10% for Sr

  8. A fast and effective method for N-doping TiO2 by post treatment with liquid ammonia: visible light photocatalysis

    International Nuclear Information System (INIS)

    Powell, Michael J.; Palgrave, Robert G.; Dunnill, Charles W.; Parkin, Ivan P.

    2014-01-01

    TiO 2 thin films prepared by sol–gel synthesis were N-doped by post treating with liquid ammonia and annealing at 500 °C. Characterisation by X-ray diffraction and Raman spectroscopy confirmed that the anatase crystal type was retained and present in all samples. Scanning electron microscopy showed that treatment with liquid ammonia had no significant effect on the film morphology. Functional testing under filtered while light conditions involving water contact angle, and the photo destruction of both Resazurin and Stearic acid showed the ammonia treated samples to be active visible light photocatalysts in contrast to the pure TiO 2 and the blank controls. X-ray Photoelectron Spectroscopy studies indicate the presence of interstitial nitrogen (N 1s = 400 eV) suggesting that the origin of the enhanced photocatalytic activity is most likely due to oxygen vacancies created by the interstitial nitrogen incorporation. This synthesis method utilises a simple, inexpensive and highly effective post treatment route to N-dope TiO 2 and produces visible light photocatalysts with potential applications in self-cleaning and healthcare environments. - Highlights: • Synthesis and characterisation of N-doped TiO 2 thin films • N-doping by a post treatment with liquid ammonia • Enhanced photocatalytic activity • Easy enhancement of current TiO 2 based technologies

  9. Sn4+-Doped TiO2 Nanorod Array Film with Enhanced Visible Light ...

    Indian Academy of Sciences (India)

    61

    specific surface area of flat film than nano-powder would lead to the decrease of its .... doped TiO2 NAFs were acquired with EDS spectrometer fitted on the microscopy. ... The morphologies of films were obtained by the SEM measurement.

  10. TiO2 and Cu/TiO2 Thin Films Prepared by SPT

    Directory of Open Access Journals (Sweden)

    S. S. Roy

    2015-12-01

    Full Text Available Titanium oxide (TiO2 and copper (Cu doped titanium oxide (Cu/TiO2 thin films have been prepared by spray pyrolysis technique. Titanium chloride (TiCl4 and copper acetate (Cu(CH3COO2.H2O were used as source of Ti and Cu. The doping concentration of Cu was varied from 1-10 wt. %. The X-ray diffraction studies show that TiO2 thin films are tetragonal structure and Cu/TiO2 thin films implies CuO has present with monoclinic structure. The optical properties of the TiO2 thin films have been investigated as a function of Cu-doping level. The optical transmission of the thin films was found to increase from 88 % to 94 % with the addition of Cu up to 8 % and then decreases for higher percentage of Cu doping. The optical band gap (Eg for pure TiO2 thin film is found to be 3.40 eV. Due to Cu doping, the band gap is shifted to lower energies and then increases further with increasing the concentration of Cu. The refractive index of the TiO2 thin films is found to be 2.58 and the variation of refractive index is observed due to Cu doped. The room temperature resistivity of the films decreases with increasing Cu doping and is found to be 27.50 - 23.76 W·cm. It is evident from the present study that the Cu doping promoted the thin film morphology and thereby it is aspect for various applications.

  11. Enhanced photovoltaic performance of a quantum dot-sensitized solar cell using a Nb-doped TiO2 electrode

    International Nuclear Information System (INIS)

    Jiang, Lei; You, Ting; Deng, Wei-Qiao

    2013-01-01

    In this work Nb-doped anatase TiO 2 nanocrystals are used as the photoanode of quantum-dot-sensitized solar cells. A solar cell with CdS/CdSe quantum dots co-sensitized 2.5 mol% Nb-doped anatase TiO 2 nanocrystals can achieve a photovoltaic conversion efficiency of 3.3%, which is almost twice as high as the 1.7% obtained by a cell based on undoped TiO 2 nanocrystals. The incident photon-to-current conversion efficiency can reach as high as 91%, which is a record for all quantum-dot-sensitized solar cells. Detailed analysis shows that such an enhancement is due to improved lifetime and diffusion length of electrons in the solar cell. (paper)

  12. Enhanced photovoltaic performance of a quantum dot-sensitized solar cell using a Nb-doped TiO2 electrode.

    Science.gov (United States)

    Jiang, Lei; You, Ting; Deng, Wei-Qiao

    2013-10-18

    In this work Nb-doped anatase TiO2 nanocrystals are used as the photoanode of quantum-dot-sensitized solar cells. A solar cell with CdS/CdSe quantum dots co-sensitized 2.5 mol% Nb-doped anatase TiO2 nanocrystals can achieve a photovoltaic conversion efficiency of 3.3%, which is almost twice as high as the 1.7% obtained by a cell based on undoped TiO2 nanocrystals. The incident photon-to-current conversion efficiency can reach as high as 91%, which is a record for all quantum-dot-sensitized solar cells. Detailed analysis shows that such an enhancement is due to improved lifetime and diffusion length of electrons in the solar cell.

  13. Lanthanide doped BaTiO{sub 3}−SrTiO{sub 3} solid-solution phosphors: Structure, optical spectroscopy and upconverted temperature sensing behavior

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Daqin, E-mail: dqchen@hdu.edu.cn; Xu, Wei; Zhou, Yang; Chen, Yan, E-mail: chenyan@hdu.edu.cn

    2016-08-15

    Lanthanide doped Ba{sub 1-x}Sr{sub x}TiO{sub 3} (x = 0–1) solid-solution phosphors were successfully prepared by a conventional solid-state reaction. Using Eu{sup 3+} dopants as the structural probe, the variation of {sup 5}D{sub 0} → {sup 7}F{sub 2}/{sup 5}D{sub 0} → {sup 7}F{sub 1} emission intensity ratio with increase of Eu{sup 3+} content and the excitation-wavelength-dependent luminescence in the Ba{sub 1-x}Sr{sub x}TiO{sub 3} sample were demonstrated to be originated from the different emission behaviors of Eu{sup 3+} in Ba{sup 2+}/Sr{sup 2+} site and Ti{sup 4+} site. Furthermore, upconversion luminescence for the Yb{sup 3+}/Er{sup 3+} co-doped Ba{sub 1-x}Sr{sub x}TiO{sub 3} samples were investigated, and it was found that the emission intensity of Yb{sup 3+}/Er{sup 3+}: Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} phosphor was about 5 and 2 times as high as those of Yb{sup 3+}/Er{sup 3+}: BaTiO{sub 3} and Yb{sup 3+}/Er{sup 3+}: SrTiO{sub 3} ones. Using the investigated Yb{sup 3+}/Er{sup 3+}: Ba{sub 0.5}Sr{sub 0.5}TiO{sub 3} solid-solution as the optical thermometric medium, the temperature sensitivity was determined to be 0.76% K{sup −1} at the temperature of 610 K based on the temperature-dependent fluorescence intensity ratio of the thermally coupled {sup 2}H{sub 11/2} and {sup 4}S{sub 3/2} emitting-states of Er{sup 3+}. - Highlights: • Lanthanide doped Ba{sub 1-x}Sr{sub x}TiO{sub 3} (x = 0–1) solid-solutions were fabricated. • Excitation-wavelength-dependent Eu{sup 3+} emissions were recorded. • Enhanced Er{sup 3+} luminescence was realized by partial substitution of Ba{sup 2+} by Sr{sup 2+}. • T-sensitive emissions of two Er{sup 3+} thermally coupled states were observed. • The upconversion phosphor exhibited a high sensitivity of 0.76% K{sup −1}.

  14. Vacancy-induced brittle to ductile transition of W-M co-doped Al3Ti (M=Si, Ge, Sn and Pb).

    Science.gov (United States)

    Zhu, Mingke; Wu, Ping; Li, Qiulin; Xu, Ben

    2017-10-25

    We investigated the effect of vacancy formation on brittle (D0 22 ) to ductile (L1 2 -like) transition in Al 3 Ti using DFT calculations. The well-known pseudogap on the density of states of Al 3 Ti migrates towards its Fermi level from far above, via a W - M co-doping strategy, where M is Si, Ge, Sn or Pb respectively. In particular, by a W - M co-doping the underline electronic structure of the pseudogap approaches an octahedral (L1 2 : t 2g , e g ) from the tetragonal (D0 22 : e g , b 2g , a 1g , b 1g ) crystal field. Our calculations demonstrated that (1) a W-doping is responsible for the close up of the energy gap between a 1g and b 1g so that they tend to merge into an e g symmetry, and (2) all M-doping lead to a narrower gap between e g and b 2g (moving towards a t 2g symmetry). Thus, a brittle to ductile transition in Al 3 Ti is possible by adopting this W - M co-doping strategy. We further recommend the use of W-Pb co-doped Al 3 Ti to replace the less anodic Al electrode in Al-battery, due to its improved ductility and high Al diffusivity. Finally this study opens a new field in physics to tailor mechanical properties by manipulating electron energy level(s) towards higher symmetry via vacancy optimization.

  15. Computational study of TiO2 Brookite (100), (010) and (210) surface doped with Ruthenium for application in Dye Sensitised Solar Cells

    Science.gov (United States)

    Dima, R. S.; Maluta, N. E.; Maphanga, R. R.; Sankaran, V.

    2017-10-01

    Titanium dioxide (TiO2) polymorphs are widely used in many energy-related applications due to their peculiar electronic and physicochemical properties. The electronic structures of brookite TiO2 surfaces doped with transition metal ruthenium have been investigated by ab initio band calculations based on the density functional theory with the planewave ultrasoft pseudopotential method. The generalized gradient approximation (GGA) was used in the scheme of Perdew-Burke-Ernzerhof (PBE) to describe the exchange-correlation functional. All calculations were carried out with CASTEP (Cambridge Sequential Total EnergyPackage) code in Materials Studio of Accelrys Inc. The surface structures of Ru doped TiO2 were constructed by cleaving the 1 × 1 × 1 optimized bulk structure of brookite TiO2. The results indicate that Ru doping can narrow the band gap of TiO2, leading to the improvement in the photoreactivity of TiO2, and simultaneously maintain strong redox potential. The theoretical calculations could provide meaningful guide to develop more active photocatalysts with visible light response.

  16. Stability of the Al/TiB2 interface and doping effects of Mg/Si

    Science.gov (United States)

    Deng, Chao; Xu, Ben; Wu, Ping; Li, Qiulin

    2017-12-01

    The Al/TiB2 interface is of significant importance in controlling the mechanical properties of Al-B4C composites and tuning the heterogeneous nucleation of Al/Si alloys in industry. Its stability and bonding conditions are critical for both purposes. In this paper, the interfacial energies were investigated by first-principles calculations, and the results support the reported grain refinement mechanisms in Al/Si alloys. Moreover, to improve the mechanical properties of the interface, Mg and Si were doped at the interface, and our simulations show that the two interfaces will both weaken after doping Mg/Si, thus the formation of TiB2 is inhibited. As a result, the processability of the Al-B4C composites may be improved. Our results provide a theoretical basis and guidance for practical applications.

  17. Pseudocapacitance of amorphous TiO2@nitrogen doped graphene composite for high rate lithium storage

    International Nuclear Information System (INIS)

    Li, Sheng; Xue, Pan; Lai, Chao; Qiu, Jingxia; Ling, Min; Zhang, Shanqing

    2015-01-01

    The high rate applications such as electric vehicles of the traditional lithium ion batteries (LIBs) are commonly limited by their insufficient electron conductivity and slow mass transport of lithium ions in bulk electrode materials. In order to address these issues, in this work, a simple and up-scalable wet-mechanochemical (wet-ball milling) route has been developed for fabrication of amorphous porous TiO 2 @nitrogen doped graphene (TiO 2 @N-G) nanocomposites. The amorphous phase, unique porous structure of TiO 2 and the surface defects from nitrogen doping to graphene planes have incurred surface controlled reactions, contributing pseudocapacitance to the total capacity of the battery. It plays a dominant role in producing outstanding high rate electrochemical performance, e.g., 182.7 mAh/g (at 3.36 A/g) after 100 cycles. The design and synthesis of electrode materials with enhanced conductivity and surface pseudocapacitance can be a promising way for high rate LIBs.

  18. Photocatalytic performance of Sn-doped and undoped TiO2 nanostructured thin films under UV and vis-lights

    International Nuclear Information System (INIS)

    Arpac, E.; Sayilkan, F.; Asiltuerk, M.; Tatar, P.; Kiraz, Nadir; Sayilkan, H.

    2007-01-01

    Sn-doped and undoped nano-TiO 2 particles have been synthesized by hydrotermal process without solvent at 200 deg. C in 1 h. Nanostructure-TiO 2 based thin films have been prepared on glass substrate by spin-coating technique. The structure, surface morphology and optical properties of the thin films and the particles have been investigated by element analysis and XRD, SEM, BET and UV-vis-NIR techniques. The photocatalytic performance of the films were tested for degradation of Malachite Green dye in solution under UV and vis-lights. The results showed that (a) hydrothermally synthesized nano-TiO 2 particles are fully anatase crystalline form and are easily dispersed in water, (b) the coated surfaces have nearly super-hydrophilic properties and (c) the doping of transition metal ion efficiently improved the photocatalytic performance of the TiO 2 thin film

  19. Effects of phosphorus-doping on energy band-gap, structural, surface, and photocatalytic characteristics of emulsion-based sol-gel derived TiO{sub 2} nano-powder

    Energy Technology Data Exchange (ETDEWEB)

    Ganesh, Ibram, E-mail: ibramganesh@arci.res.in

    2017-08-31

    Highlights: • Reported a novel route to synthesize high specific surface area P-doped TiO{sub 2} nano-powder photocatalysts. • Established methylene blue dye-sensitization mechanism of TiO{sub 2} photocatalyst. • Established the effects of methylene blue adsorption on the surface, structural and photocatalytic activity of P-doped TiO{sub 2}. • Established true quantum efficiency determination method for TiO{sub 2} photocatalysis. - Abstract: Different amounts of phosphorus (P)-doped TiO{sub 2} (PDT) nano-powders (P = 0–10 wt.%) were synthesized by following a new emulsion-based sol-gel (EBSG) route and calcined at 400 °C–800 °C for 6 h. These calcined PDT powders were then thoroughly characterized by means of XRD, XPS, SEM, FT-IR, FT-Raman, DRS, BET surface area, zeta-potential, cyclic-voltammetry and photocatalytic evaluation using methylene blue (MB) as a model-pollutant and established the effects of phosphorous doping on structural, surface, band-gap energy, and photocatalytic characteristics of TiO{sub 2} nano-powder formed in EBSG route. The characterization results suggest that the EBSG derived TiO{sub 2} nano-powder after calcination at 400 °C for 6 h is in the form of anatase phase when it was doped with <8 wt.% P, and it is in the amorphous state when doped with >8 wt.% P. Furthermore, these EBSG derived PDT powders own high negative zeta-potentials, high specific surface areas (up to >250 m{sup 2}/g), and suitable band-gap energies (<3.34 eV). Surprisingly, these PDT powders exhibit very high MB adsorption (up to 50%) from its aqueous 0.01 mM, 0.02 mM and 0.03 mM solutions during 30 min stirring in the dark, whereas, the commercial Degussa P-25 TiO{sub 2} nano-powder shows no adsorption. Among various photocatalysts investigated in this study, the 1 wt.% P-doped TiO{sub 2} nano-powder formed in EBSG route exhibited the highest photocatalytic activity for MB degradation reaction.

  20. A Ti-doped γ-Fe2O3/SDS nano-photocatalyst as an efficient adsorbent for removal of methylene blue from aqueous solutions.

    Science.gov (United States)

    Mirbagheri, Naghmeh Sadat; Sabbaghi, Samad

    2018-05-01

    Synthetic dyes are among the most important environmental pollutants in wastewaters. Consequently, elimination of the synthetic dyes from wastewaters using non-toxic materials and eco-friendly technologies has been of considerable interests. In this study, magnetically separable Ti-doped γ-Fe 2 O 3 photocatalysts were synthesized for the removal of methylene blue (MB) from a dye-contaminated aqueous solution (as a model of dye-polluted wastewaters). Compared to the pristine γ-Fe 2 O 3 , the 1.78 v% Ti-doped γ-Fe 2 O 3 significantly increased the adsorption of MB by 57% in the dark condition as a result of the improved BET surface area in this photocatalyst. Moreover, the contact time required for the photocatalytic degradation of MB by the 1.78 v% Ti-doped γ-Fe 2 O 3 decreased due to the higher concentration of charge carriers in this photocatalyst than that of the pristine γ-Fe 2 O 3 . The effect of different experimental parameters on the adsorption property and photocatalytic activity of the 1.78 v% Ti-doped γ-Fe 2 O 3 photocatalyst showed that the solution pH had a remarkable influence on the removal performance of this photocatalyst. Surface treatment of the 1.78 v% Ti-doped γ-Fe 2 O 3 with sodium dodecyl sulfate (SDS) resulted in the formation of a negatively charged Ti-doped γ-Fe 2 O 3 /SDS photocatalyst, which showed a higher tendency for the adsorption and removal of MB than the untreated photocatalyst. Moreover, the MB removal efficiency of this photocatalyst was among the best performances that have been reported for the γ-Fe 2 O 3 -based photocatalysts. The synthesized photocatalysts were characterized by various techniques, and a plausible mechanism for the removal of MB from aqueous solutions by the Ti-doped γ-Fe 2 O 3 /SDS photocatalyst was purposed. Copyright © 2018 Elsevier Ltd. All rights reserved.

  1. Preparation and characterization of Bi-doped TiO{sub 2} and its solar photocatalytic activity for the degradation of isoproturon herbicide

    Energy Technology Data Exchange (ETDEWEB)

    Reddy, Police Anil Kumar; Srinivas, Basavaraju; Kala, Pruthu; Kumari, Valluri Durga [Inorganic and Physical Chemistry Division, Indian Institute of Chemical Technology, Hyderabad, India 500607 (India); Subrahmanyam, Machiraju, E-mail: subrahmanyam@iict.res.in [Inorganic and Physical Chemistry Division, Indian Institute of Chemical Technology, Hyderabad, India 500607 (India)

    2011-11-15

    Highlights: {yields} Visible active Bi-TiO{sub 2} photocatalyst preparation and thorough charaterization. {yields} Bi-TiO{sub 2} shows high activity for isoproturon degradation under solar light irradiation. {yields} The spectral response of TiO{sub 2} shifts from UV to visible light region by Bi doping. {yields} Bi{sup 3+{delta}+} species are playing a vital role in minimizing e{sup -}/h{sup +} recombination. -- Abstract: Bi-doped TiO{sub 2} catalyst was prepared by sol-gel method and was characterized by thermo gravimetric analysis (TGA), X-ray diffraction spectra (XRD), X-ray photo electronic spectroscopy (XPS), UV-Vis diffused reflectance spectra (DRS), photoluminescence spectra (PLS), transmission electron microscopy (TEM), energy dispersive analysis of X-rays (EDAX) and BET surface area. The photocatalytic activity of the catalysts were evaluated for the degradation of isoproturon herbicide under solar light irradiation. The UV-Visible DRS of Bi-doped TiO{sub 2} showed red shift in optical absorption. The presence of Bi{sup 3+{delta}+} species are playing a vital role in minimizing the electron hole recombination resulting higher activity compared to bare TiO{sub 2}.

  2. Design of a novel dual Z-scheme photocatalytic system composited of Ag{sub 2}O modified Ti{sup 3+} self doped TiO{sub 2} nanocrystals with individual exposed (001) and (101) facets

    Energy Technology Data Exchange (ETDEWEB)

    Li, Mengyan; Liu, Hui, E-mail: liuhui@sust.edu.cn; Liu, Tingting; Qin, Yangxiao

    2017-02-15

    A novel dual Z-scheme photocatalytic system composited of Ag{sub 2}O nanocrystals modified Ti{sup 3+} self doped TiO{sub 2} nanocrystals with individual exposed (001) and (101) facets were successfully fabricated. In which, the Ti{sup 3+} self doped TiO{sub 2} nanocrystals with individual exposed (001) and (101) facets have been firstly prepared by a simple hydrothermal method, subsequently the as-prepared products were modified with Ag{sub 2}O nanocrystals through a sonochemical depositing process in order to build a novel dual Z-scheme photocatalytic system. The samples were carefully characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV–visible diffuse reflectance spectra (UV–vis DRS), and Brunauer-Emmett-Teller (BET). The photocatalytic activity toward degradation of Rhodamine B (Rh B) aqueous solution under stimulated solar light was investigated. The experimental results showed this new dual Z-scheme photocatalytic system possess an enhanced photocatalytic degradation activity compared to that similar surface heterojunction photocatalysts composed of Ti{sup 3+} self doped TiO{sub 2} nanocrystals with individual exposed (001) and (101) facets. This novel photocatalytic system presents a high charge-separation efficiency and strong redox ability. This study will help us to better understand the photocatalytic mechanism of semiconductor photocatalysts with exposed different facets, and provide a new insight into the design and fabrication of advanced photocatalytic materials. - Highlights: •A novel dual Z-scheme system was built by Ag{sub 2}O and facet exposed TiO{sub 2} nanocrystals. •The individual TiO{sub 2} nanocrystals exposed (001) and (101) facets respectively. •Ag{sub 2}O coupled with Ti{sup 3+} self doped TiO{sub 2} nanocrystals through a sonochemical process. •The as-prepared sample possesses a super photocatalytic activity.

  3. Theoretical study on the magnetic moments formation in Ta-doped anatase TiO2

    Science.gov (United States)

    Bupu, A.; Majidi, M. A.; Rusydi, A.

    2017-04-01

    We present a theoretical study on Ti-vacancy induced ferromagnetism in Ta-doped anatase TiO2. Experimental study of Ti1-x Ta x O2 thin film has shown that Ti-vacancies (assisted by Ta doping) induce the formation of localized magnetic moment around it, then, the observed ferromagnetism is caused by the alignment of localized magnetic moments through Ruderman-Kittel-Kasuya-Yosida (RKKY) interaction. In this study, we focus on the formation of the localized magnetic moments in this system. We hypothesize that on a unit cell, Ti-vacancy has caused four electrons from the surrounding oxygen atoms to become unpaired. These unpaired electrons then arrange themselves into a configuration with a non-zero net magnetic moment. To examine our hypothesis, we construct a Hamiltonian of the four unpaired electrons, incorporating the Coulomb intra- and inter-orbital interactions, in matrix form. Using a set of chosen parameter values, we diagonalize the Hamiltonian to get the eigenstates and eigenvalues, then, with the resulting eigenstates, we calculate the magnetic moment, μ, by obtaining the expectation value of the square of total spin operator. Our calculation results show that in the ground state, provided that the ratio of parameters satisfies some criterion, μ ≈ 4μ B , corresponding to the four electron spins being almost perfectly aligned, can be achieved. Further, as long as we keep the Coulomb intra-orbital interaction between 0.5 and 1 eV, we find that μ ≈ 4μ B is robust up to far above room temperature. Our results demonstrate that Ti vacancies in anatase TiO2 can form very stable localized magnetic moments.

  4. Optical and electrical properties of Ti(Cr)O{sub 2}:N thin films deposited by magnetron co-sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Kollbek, K., E-mail: kamila.kollbek@agh.edu.pl [Academic Centre for Materials and Nanotechnology, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland); Szkudlarek, A.; Marzec, M.M. [Academic Centre for Materials and Nanotechnology, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland); Lyson-Sypien, B.; Cecot, M. [Faculty of Computer Science, Electronics and Telecommunications, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland); Bernasik, A. [Academic Centre for Materials and Nanotechnology, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland); Faculty of Physics and Applied Computer Science, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland); Radecka, M. [Faculty of Materials Science and Ceramics, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland); Zakrzewska, K. [Faculty of Computer Science, Electronics and Telecommunications, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland)

    2016-09-01

    Graphical abstract: - Highlights: • Co-doped well-crystallized stoichiometric Ti(Cr)O{sub 2}:N thin films are deposited. • Magnetron sputtering of ceramic TiO{sub 2} target is a new strategy for co-doping. • Bigger contribution from substitutionally incorporated nitrogen is seen in XPS. • Significant red shift of the fundamental absorption edge is obtained. - Abstract: The paper deals with TiO{sub 2}-based thin films, doped with Cr and N, obtained by magnetron co-sputtering from titanium dioxide ceramic and chromium targets in Ar + N{sub 2} atmosphere. Co-doped samples of Ti(Cr)O{sub 2}:N are investigated from the point of view of morphological, crystallographic, optical, and electrical properties. Characterization techniques such as: X-ray diffraction, XRD, scanning electron microscopy, SEM, atomic force microscopy, AFM, Energy Dispersive X-ray spectroscopy, EDX, X-ray photoelectron spectroscopy, XPS, optical spectrophotometry as well as impedance spectroscopy are applied. XRD reveals TiO{sub 2} and TiO{sub 2}:N thin films are well crystallized as opposed to those of TiO{sub 2}:Cr and Ti(Cr)O{sub 2}:N. XPS spectra confirm that co-doping has been successfully performed with the biggest contribution from the lower binding energy component of N 1s peak at 396 eV. SEM analysis indicates uniform and dense morphology without columnar growth. Comparison between the band gaps indicates a significant shift of the absorption edge towards visible range from 3.69 eV in the case of non-stoichiometric Ti(Cr)O{sub 2−x}:N to 2.78 eV in the case of stoichiometric Ti(Cr)O{sub 2}:N which should be attributed to the incorporation of both dopants at substitutional positions in TiO{sub 2} lattice. Electrical conductivity of stoichiometric Ti(Cr)O{sub 2}:N increases in comparison to co-doped nonstoichiometric TiO{sub 2−x} thin film and reaches almost the same value as that of TiO{sub 2} stoichiometric film.

  5. Three-dimensional ruthenium-doped TiO 2 sea urchins for enhanced visible-light-responsive H 2 production

    Energy Technology Data Exchange (ETDEWEB)

    Nguyen-Phan, Thuy-Duong; Luo, Si; Vovchok, Dimitriy; Llorca, Jordi; Sallis, Shawn; Kattel, Shyam; Xu, Wenqian; Piper, Louis F. J.; Polyansky, Dmitry E.; Senanayake, Sanjaya D.; Stacchiola, Dario J.; Rodriguez, José A.

    2016-01-01

    Three-dimensional (3D) monodispersed sea urchin-like Ru-doped rutile TiO2 hierarchical architectures composed of radially aligned, densely-packed TiO2 nanorods have been successfully synthesized via an acid-hydrothermal method at low temperature without the assistance of any structure-directing agent and post annealing treatment. The addition of a minuscule concentration of ruthenium dopants remarkably catalyze the formation of the 3D urchin structure and drive the enhanced photocatalytic H2 production under visible light irradiation, not possible on undoped and bulk rutile TiO2. Increasing ruthenium doping dosage not only increases the surface area up to 166 m2 g-1 but also induces enhanced photo response in the regime of visible and near infrared light. The doping introduces defect impurity levels, i.e. oxygen vacancy and under-coordinated Ti3+, significantly below the conduction band of TiO2, and ruthenium species act as electron donors/acceptors that accelerate the photogenetated hole and electron transfer and efficiently suppress the rapid charge recombination, therefore improving the visible-light-driven activity.

  6. Structural and electrical properties of Barium Titanate (BaTiO3 and Neodymium doped BaTiO3 (Ba0.995Nd0.005TiO3

    Directory of Open Access Journals (Sweden)

    Tuan Sulong Tuan Amirah

    2017-01-01

    Full Text Available Barium titanate (BaTiO3 and Neodymium (Nd doped BaTiO3 with composition Ba0.995Nd0.005TiO3 were prepared using conventional solid state reaction method to study the dielectric properties of materials. Pure phase samples were found at final heating temperature of 1400°C for overnight. X-ray diffraction analysis reveals the changes in the lattice parameter and unit cell volume of the pure perovskite tetragonal structure with space group (P4mm. Electrical analysis is carried out to investigate the dielectric properties, conductivity behaviour and dielectric loss of BaTiO3 and Ba0.995Nd0.005TiO3. Ba0.995Nd0.005TiO3 have a broaden dielectric peaks with high permittivity of 8000 and reasonably low loss tan δ which is about 0.004 (1 kHz.

  7. Ammonia Gas Sensing Behavior of Tanninsulfonic Acid Doped Polyaniline-TiO2 Composite

    Directory of Open Access Journals (Sweden)

    Venu Gopal Bairi

    2015-10-01

    Full Text Available A highly active tannin doped polyaniline-TiO2 composite ammonia gas sensor was developed and the mechanism behind the gas sensing activity was reported for the first time. A tanninsulfonic acid doped polyaniline (TANIPANI-titanium dioxide nanocomposite was synthesized by an in situ polymerization of aniline in the presence of tanninsulfonic acid and titanium dioxide nanoparticles. X-ray diffraction and thermogravimetric analysis were utilized to determine the incorporation of TiO2 in TANIPANI matrix. UV-Visible and infrared spectroscopy studies provided information about the electronic interactions among tannin, polyaniline, and TiO2. Scanning electron microscopy (SEM along with energy dispersive X-ray spectroscopy (EDS and atomic force microscopy (AFM surface analysis techniques were used to investigate the metal oxide dispersions inside polyaniline matrix. Gas sensors were prepared by spin coating solutions of TANIPANI-TiO2 and TANIPANI composites onto glass slides. Sensors were tested at three different concentrations (20 ppm, 40 ppm, and 60 ppm of ammonia gas at ambient temperature conditions by measuring the changes in surface resistivity of the films with respect to time. Ammonia gas sensing plots are presented showing the response values, response times and recovery times. The TANIPANI-TiO2 composite exhibited better response and shorter recovery times when compared to TANIPANI control and other polyaniline composites that have been reported in the literature. For the first time a proposed mechanism of gas sensing basing on the polaron band localization and its effects on the gas sensing behavior of polyaniline are reported.

  8. Photocatalytic characteristics for the nanocrystalline TiO{sub 2} on the Ag-doped CaAl{sub 2}O{sub 4}:(Eu,Nd) phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jung-Sik, E-mail: jskim@uos.ac.kr; Sung, Hyun-Je; Kim, Bum-Joon

    2015-04-15

    Highlights: • The photocatalytic reactivity of the TiO{sub 2}-coated on the Ag-doped long-lasting phosphor (CaAl{sub 2}O{sub 4}:Eu{sup 2+},Nd{sup 3+}). • The photodecomposition of benzene gas under visible light irradiation. • The TiO{sub 2}-coated on the Ag-doped long-lasting phosphor showed much higher photocatalytic reactivity. • The light emitted from the long-lasting phosphors contributed to the photo generation of TiO{sub 2}. - Abstract: This study investigated the photocatalytic behavior of nanocrystalline TiO{sub 2} deposited on Ag-doped long-lasting phosphor (CaAl{sub 2}O{sub 4}:Eu{sup 2+},Nd{sup 3+}). The CaAl{sub 2}O{sub 4}:Eu{sup 2+},Nd{sup 3+} phosphor powders were prepared via conventional sintering using CaCO{sub 3}, Al{sub 2}O{sub 3}, Eu{sub 2}O{sub 3}, and Nd{sub 2}O{sub 3} as raw materials according to the appropriate molar ratios. Silver nanoparticles were loaded on the phosphor by mixing with an aqueous Ag-dispersion solution. Nanocrystalline TiO{sub 2} was deposited on Ag-doped CaAl{sub 2}O{sub 4}:Eu{sup 2+},Nd{sup 3+} powders via low-pressure chemical vapor deposition (LPCVD). The TiO{sub 2} coated on the phosphor was actively photo-reactive under irradiation with visible light and showed much faster benzene degradation than pure TiO{sub 2}, which is almost non-reactive. The coupling of TiO{sub 2} with phosphor may result in an energy band bending in the junction region, which then induces the TiO{sub 2} crystal at the interface to be photo-reactive under irradiation with visible light. In addition, the intermetallic compound of CaTiO{sub 3} that formed at the interface between TiO{sub 2} and the CaAl{sub 2}O{sub 4}:(Eu{sup 2+},Nd{sup 3+}) phosphor results in the formation of oxygen vacancies and additional electrons that promote the photodecomposition of benzene gas. The addition of Ag nanoparticles enhanced the photocatalytic reactivity of the TiO{sub 2}/CaAl{sub 2}O{sub 4}:Eu{sup 2+},Nd{sup 3+} phosphor. TiO{sub 2} on the Ag-doped

  9. N-Doped TiO2-Coated Ceramic Membrane for Carbamazepine Degradation in Different Water Qualities

    Science.gov (United States)

    Luster, Enbal; Avisar, Dror; Horovitz, Inna; Lozzi, Luca; Baker, Mark A.; Grilli, Rossana; Mamane, Hadas

    2017-01-01

    The photocatalytic degradation of the model pollutant carbamazepine (CBZ) was investigated under simulated solar irradiation with an N-doped TiO2-coated Al2O3 photocatalytic membrane, using different water types. The photocatalytic membrane combines photocatalysis and membrane filtration in a single step. The impact of each individual constituent such as acidity, alkalinity, dissolved organic matter (DOM), divalent cations (Mg2+ and Ca2+), and Cl− on the degradation of CBZ was examined. CBZ in water was efficiently degraded by an N-doped TiO2-coated Al2O3 membrane. However, elements added to the water, which simulate the constituents of natural water, had an impact on the CBZ degradation. Water alkalinity inhibited CBZ degradation mostly due to increase in pH while radical scavenging by carbonate was more dominant at higher values (>200 mg/L as CaCO3). A negative effect of Ca2+ addition on photocatalytic degradation was found only in combination with phosphate buffer, probably caused by deposition of CaHPO4 or CaHPO4·2H2O on the catalyst surface. The presence of Cl− and Mg2+ ions had no effect on CBZ degradation. DOM significantly inhibited CBZ degradation for all tested background organic compounds. The photocatalytic activity of N-doped TiO2-coated Al2O3 membranes gradually decreased after continuous use; however, it was successfully regenerated by 0.1% HCl chemical cleaning. Nevertheless, dissolution of metals like Al and Ti should be monitored following acid cleaning. PMID:28758982

  10. Effect of annealing on luminescence of Eu{sup 3+}- and Sm{sup 3+}-doped Mg{sub 2}TiO{sub 4} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Medić, Mina; Antić, Željka; Đorđević, Vesna [University of Belgrade, Vinča Institute of Nuclear Sciences, P.O. Box 522, 11001 Belgrade (Serbia); Ahrenkiel, Phillip S. [South Dakota School of Mines & Technology, Rapid City, SD (United States); Marinović-Cincović, Milena [University of Belgrade, Vinča Institute of Nuclear Sciences, P.O. Box 522, 11001 Belgrade (Serbia); Dramićanin, Miroslav D., E-mail: dramican@vinca.rs [University of Belgrade, Vinča Institute of Nuclear Sciences, P.O. Box 522, 11001 Belgrade (Serbia)

    2016-02-15

    This work explores the influence of annealing temperature on the structure and luminescence of 2 at% Eu{sup 3+} and 1 at% Sm{sup 3+}-doped Mg{sub 2}TiO{sub 4} nanopowders produced via Pechini-type polymerized complex route. Mg{sub 2}TiO{sub 4} samples were annealed at 7 different temperatures (400 °C, 450 °C, 500 °C, 550 °C, 600 °C, 650 °C and 700 °C) to determine the temperature range in which cubic inverse spinel structure is stable and to follow the changes of material luminescence properties. X-ray diffraction revealed that crystallization of both Eu{sup 3+} and Sm{sup 3+}-doped Mg{sub 2}TiO{sub 4} nanopowders starts at 400 °C, and that Sm{sup 3+} doped Mg{sub 2}TiO{sub 4} starts to decompose at 650 °C, while Eu{sup 3+} doped Mg{sub 2}TiO{sub 4} starts to decompose at 700 °C. Samples annealed at higher temperatures show higher crystallinity and larger crystallite size. Mg{sub 2}TiO{sub 4} powder annealed at 600 °C is composed of ~5 nm size nanoparticles agglomerated in micron-size and dense chunks. The emission spectra of nanoparticles are composed of emissions from defects in Mg{sub 2}TiO{sub 4} host and characteristic emissions of Eu{sup 3+} ({sup 5}D{sub 0}→{sup 7}F{sub J}) and Sm{sup 3+} ({sup 4}G{sub 5/2}→{sup 6}H{sub J}) ions. The stronger emission and longer emission decays are observed with samples annealed at high temperatures. In the case of the Eu{sup 3+} ions emission intensity increased one order of magnitude between samples annealed at 400 °C and 650 °C. - Highlights: • Mg{sub 2}TiO{sub 4} nanoparticles of 5–10 nm in size are prepared by polymerized complex route. • Emission spectra and decays of Eu{sup 3+} and Sm{sup 3+} doped Mg{sub 2}TiO{sub 4} nanoparticles are shown. • Eu{sup 3+}(Sm{sup 3+}) doped Mg{sub 2}TiO{sub 4} can be annealed at temperatures <700 °C (650 °C). • Emission intensity of nanoparticles increases with increase of annealing temperature.

  11. Deep-level optical spectroscopy investigation of N-doped TiO2 films

    International Nuclear Information System (INIS)

    Nakano, Yoshitaka; Morikawa, Takeshi; Ohwaki, Takeshi; Taga, Yasunori

    2005-01-01

    N-doped TiO 2 films were deposited on n + -GaN/Al 2 O 3 substrates by reactive magnetron sputtering and subsequently crystallized by annealing at 550 deg. C in flowing N 2 gas. The N-doping concentration was ∼8.8%, as determined from x-ray photoelectron spectroscopy measurements. Deep-level optical spectroscopy measurements revealed two characteristic deep levels located at ∼1.18 and ∼2.48 eV below the conduction band. The 1.18 eV level is probably attributable to the O vacancy state and can be active as an efficient generation-recombination center. Additionally, the 2.48 eV band is newly introduced by the N doping and contributes to band-gap narrowing by mixing with the O 2p valence band

  12. Oxygen nonstoichiometry and defects in Mn-doped Gd2Ti2O7+x

    International Nuclear Information System (INIS)

    Porat, O.; Tuller, H.L.

    1996-01-01

    The oxygen nonstoichiometry in Mn-doped Gd 2 Ti 2 O 7 , Gd 2 (Ti 0.975 Mn 0.025 ) 2 O 7+x , was measured electrochemically, as a function of temperature and oxygen partial pressure, with the aid of an oxygen titration cell. The analysis of the data shows that the defect equilibrium can be described by considering the dominant point defects to be neutral oxygen interstitials, doubly charged oxygen vacancies, and trivalent and quadrivalent Mn ions substituted in the Ti sites. The enthalpies for the formation of neutral oxygen interstitials and trivalent Mn are determined

  13. Photocatalytic characteristics of single phase Fe-doped anatase TiO{sub 2} nanoparticles sensitized with vitamin B{sub 12}

    Energy Technology Data Exchange (ETDEWEB)

    Gharagozlou, Mehrnaz, E-mail: gharagozlou@icrc.ac.ir [Department of Nanomaterials and Nanotechnology, Institute for Color Science and Technology, Tehran (Iran, Islamic Republic of); Bayati, R. [Intel Corporation, IMO-SC, SC2, Santa Clara, CA 95054 (United States)

    2015-01-15

    Highlights: • Anatase TiO{sub 2}/B{sub 12} hybrid nanostructured catalyst was successfully synthesized by sol–gel technique. • The nanoparticle catalyst was doped with iron at several concentrations. • Nanoparticles were characterized in detail by XRD, Raman, TEM, EDS, and spectroscopy techniques. • The formation mechanism and role of point defects on photocatalytic properties were discussed. • A structure-property-processing correlation was established. - Abstract: We report a processing-structure-property correlation in B{sub 12}-anatase titania hybrid catalysts doped with several concentrations of iron. Our results clearly show that low-level iron doping alters structure, defect content, and photocatalytic characteristics of TiO{sub 2}. XRD and Raman studies revealed formation of a single-phase anatase TiO{sub 2} where no iron based segregation in particular iron oxide, was detected. FT-IR spectra clearly confirmed sensitization of TiO{sub 2} nanoparticles with vitamin B{sub 12}. TEM micrographs and diffraction patterns confirmed crystallization of anatase nanoparticles with a radius of 15–20 nm. Both XRD and Raman signals showed a peak shift and a peak broadening which are surmised to originate from creation of point defects, namely oxygen vacancy and titanium interstitial. The doped samples revealed a narrower band gap as compared to undoped samples. Photocatalytic activity of the samples was assessed through measuring the decomposition rate of rhodamine B. It was found that sensitization with vitamin B{sub 12} and Fe-doping significantly enhances the photocatalytic efficiency of the anatase nanoparticles. We also showed that there is an optimum Fe-doping level where the maximum photocatalytic activity is achieved. The boost of photocatalytic activity was qualitatively understood to originate from a more effective use of the light photons, formation of point defects, which enhance the charge separation, higher carrier mobility.

  14. Influence of difference quantity La-doped TiO{sub 2} photoanodes on the performance of dye-sensitized solar cells: A strategy for choosing an appropriate doping quantity

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Zige; Li, Guoxiang; Cui, Zijian; Zhang, Kaiyue; Feng, Yaqing [School of Chemical Engineering and Technology, Tianjin University, Weijin Roard 92#, Tianjin 300072 (China); Collaborative Innovation Center of Chemical Science and Engineering, Weijin Roard 92#, Tianjin 300072 (China); Meng, Shuxian, E-mail: msxmail@tju.edu.cn [School of Chemical Engineering and Technology, Tianjin University, Weijin Roard 92#, Tianjin 300072 (China); Collaborative Innovation Center of Chemical Science and Engineering, Weijin Roard 92#, Tianjin 300072 (China)

    2016-05-15

    Facilitated by TiO{sub 2} particles adsorbing lanthanide ions in hydrosol, La-doped TiO{sub 2} was produced by a hydrothermal method. The structure, optical and photoluminescence properties of down-converting photoelectrode with the La{sup 3+} were characterized by X-ray (XRD), Scanning electron microscopy (SEM), Energy dispersive X-ray detector (EDX) and N{sub 2} adsorption-desorption isotherms measurement. The photoelectric conversion efficiency of dye-sensitized solar cells (DSSCs) fabricated with 0.05 g-La/TiO{sub 2} reached 7.02%, which gave an efficiency improved by 10.36% compared with that of cells fabricated from pure TiO{sub 2}. The improvement in efficiency was ascribed to more dyes adsorbed on the surface of TiO{sub 2}. - Graphical abstract: (a) J–V curves of La-doped photoelectrodes with different La(NO{sub 3}){sub 3}·6H{sub 2}O amounts; (b) the curves of efficiency changing with the amount of La(NO{sub 3}){sub 3}·6H{sub 2}O. The photoelectric conversion efficiency of dye-sensitized solar cells (DSSCs) fabricated with 0.05 g-La/TiO{sub 2} reached 7.02%, which gave an efficiency improved by 10.36% compared with that of cells fabricated from pure TiO{sub 2}.

  15. Stability and Electronic Properties of TiO2 Nanostructures With and Without B and N Doping

    DEFF Research Database (Denmark)

    Mowbray, Duncan; Martinez, Jose Ignacio; García Lastra, Juan Maria

    2009-01-01

    We address one of the main challenges to TiO2 photocatalysis, namely band gap narrowing, by combining nanostructural changes with doping. With this aim we compare TiO2’s electronic properties for small 0D clusters, 1D nanorods and nanotubes, 2D layers, and 3D surface and bulk phases using differe...

  16. A fast and effective method for N-doping TiO{sub 2} by post treatment with liquid ammonia: visible light photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Powell, Michael J.; Palgrave, Robert G.; Dunnill, Charles W.; Parkin, Ivan P.

    2014-07-01

    TiO{sub 2} thin films prepared by sol–gel synthesis were N-doped by post treating with liquid ammonia and annealing at 500 °C. Characterisation by X-ray diffraction and Raman spectroscopy confirmed that the anatase crystal type was retained and present in all samples. Scanning electron microscopy showed that treatment with liquid ammonia had no significant effect on the film morphology. Functional testing under filtered while light conditions involving water contact angle, and the photo destruction of both Resazurin and Stearic acid showed the ammonia treated samples to be active visible light photocatalysts in contrast to the pure TiO{sub 2} and the blank controls. X-ray Photoelectron Spectroscopy studies indicate the presence of interstitial nitrogen (N{sub 1s} = 400 eV) suggesting that the origin of the enhanced photocatalytic activity is most likely due to oxygen vacancies created by the interstitial nitrogen incorporation. This synthesis method utilises a simple, inexpensive and highly effective post treatment route to N-dope TiO{sub 2} and produces visible light photocatalysts with potential applications in self-cleaning and healthcare environments. - Highlights: • Synthesis and characterisation of N-doped TiO{sub 2} thin films • N-doping by a post treatment with liquid ammonia • Enhanced photocatalytic activity • Easy enhancement of current TiO{sub 2} based technologies.

  17. Research Update: Doping ZnO and TiO2 for solar cells

    Directory of Open Access Journals (Sweden)

    Robert L. Z. Hoye

    2013-12-01

    Full Text Available ZnO and TiO2 are two of the most commonly used n-type metal oxide semiconductors in new generation solar cells due to their abundance, low-cost, and stability. ZnO and TiO2 can be used as active layers, photoanodes, buffer layers, transparent conducting oxides, hole-blocking layers, and intermediate layers. Doping is essential to tailor the materials properties for each application. The dopants used and their impact in solar cells are reviewed. In addition, the advantages, disadvantages, and commercial potential of the various fabrication methods of these oxides are presented.

  18. Highly biocompatible TiO2:Gd3+ nano-contrast agent with enhanced longitudinal relaxivity for targeted cancer imaging

    Science.gov (United States)

    Chandran, Parwathy; Sasidharan, Abhilash; Ashokan, Anusha; Menon, Deepthy; Nair, Shantikumar; Koyakutty, Manzoor

    2011-10-01

    We report the development of a novel magnetic nano-contrast agent (nano-CA) based on Gd3+ doped amorphous TiO2 of size ~25 nm, exhibiting enhanced longitudinal relaxivity (r1) and magnetic resonance (MR) contrasting together with excellent biocompatibility. Quantitative T1 mapping of phantom samples using a 1.5 T clinical MR imaging system revealed that the amorphous phase of doped titania has the highest r1 relaxivity which is ~2.5 fold higher than the commercially used CA Magnevist™. The crystalline (anatase) samples formed by air annealing at 250 °C and 500 °C showed significant reduction in r1 values and MR contrast, which is attributed to the loss of proton-exchange contribution from the adsorbed water and atomic re-arrangement of Gd3+ ions in the crystalline host lattice. Nanotoxicity studies including cell viability, plasma membrane integrity, reactive oxygen stress and expression of pro-inflammatory cytokines, performed on human primary endothelial cells (HUVEC), human blood derived peripheral blood mononuclear cells (PBMC) and nasopharyngeal epidermoid carcinoma (KB) cell line showed excellent biocompatibility up to relatively higher doses of 200 μg ml-1. The potential of this nano-CA to cause hemolysis, platelet aggregation and plasma coagulation were studied using human peripheral blood samples and found no adverse effects, illustrating the possibility of the safe intravenous administration of these agents for human applications. Furthermore, the ability of these agents to specifically detect cancer cells by targeting molecular receptors on the cell membrane was demonstrated on folate receptor (FR) positive oral carcinoma (KB) cells, where the folic acid conjugated nano-CA showed receptor specific accumulation on cell membrane while leaving the normal fibroblast cells (L929) unstained. This study reveals that the Gd3+ doped amorphous TiO2 nanoparticles having enhanced magnetic resonance contrast and high biocompatibility is a promising candidate for

  19. A novel bifunctional Ni-doped TiO2 inverse opal with enhanced SERS performance and excellent photocatalytic activity

    Science.gov (United States)

    Li, Xuehong; Wu, Yun; Shen, Yuhua; Sun, Yan; Yang, Ying; Xie, Anjian

    2018-01-01

    Three-dimensional inverse opal photonic microarray (IOPM) structure exhibits good qualities in structural regularity and interconnectivity, such as high specific surface area, large pore volume, uniform pore size, and ordered periodic construction. Here, a novel nickel-doped titanium dioxide IOPM (Ni-TiO2 IOPM) was fabricated for the first time as a bifunctional material for the applications of surface-enhanced Raman scattering (SERS) substrate and photocatalyst. The Ni doping could change the defect concentration of the substrate to enhance the SERS effect, and could increase the light absorption of the substrate in visible region. The synergistic effect of Ni doping and the periodically ordered porous structure enhanced both SERS sensitivity and photocatalytic activity. As a SERS substrate, the Ni-TiO2 IOPM exhibited highly sensitive detection capability for 4-mercaptobenzoic acid (4-MBA) at a concentration as low as 1 × 10-11 M. Under simulated sunlight, about 95% of the methylene blue (MB) was degraded within 90 min when Ni-TiO2 IOPM was used as the photocatalytst. The Ni-TiO2 IOPM prepared in this work may be a promising bifunctional SERS substrate candidate for organic sewage detection and environment protection. In addition, the fabrication strategy can be extended to synthesize other nanomaterials with orderly and porous structure.

  20. Improved efficiency of dye-sensitized solar cells by doping of strontium aluminate phosphor in TiO2 photoelectrode

    Directory of Open Access Journals (Sweden)

    Hwangbo Seung

    2015-06-01

    Full Text Available SrAl2O4:Eu2+, Dy3+ phosphor was synthesized by chemical solution route to use as a dopant in TiO2 layer employed as a photoelectrode for down conversion of ultraviolet and near-ultraviolet to visible and near-infrared light in a dye-sensitized solar cell. Nano-crystalline structure of the SrAl2O4:Eu2+, Dy3+ powder was confirmed by X-ray diffraction analysis and field emission scanning electron microscopy. Monitored at 520 nm, SrAl2O4:Eu2+, Dy3+ phosphor showed emission peaks at 460 to 610 nm due to 4f6 4f7 transitions of Eu2+ ions. For the study, SrAl2O4:Eu2+, Dy3+ phosphor-doped TiO2 layer was deposited on fluorine-doped tin oxide coated glass by electrostatic spray deposition. The short circuit current, open circuit voltage, fill factor, and conversion efficiency of the cells were measured. Experimental results revealed that the device efficiency for the SrAl2O4:Eu2+, Dy3+ phosphor-doped TiO2 layer increased to 7.20 %, whereas that of the pure-TiO2 photoelectrode was 4.13 %.

  1. A Humidity Sensor Based on Nb-doped Nanoporous TiO2 Thin Film

    Directory of Open Access Journals (Sweden)

    Mansoor Anbia

    2011-11-01

    Full Text Available The humidity sensing properties of the sensor fabricated from Nb-doped nanoporous TiO2 by screen-printing on the alumina substrate with Ag-Pd interdigital electrodes have been investigated. The nanoporous thin film has been prepared by sol-gel technique. The product has been characterized by X-ray diffraction and scanning electron microscopy to analyze the structure and its morphology. It is found that the impedance of this sensor changes more than four orders of magnitude in the relative humidity (RH range of 11–95 % at 25 °C. The response and recovery time of the sensor are about 19 and 25 s, respectively, during the RH variation from 11 to 95 %. The sensor shows high humidity sensitivity, rapid response and recovery, prominent stability, good repeatability and narrow hysteresis loop. These results indicate that Nb-doped nanoporous TiO2 thin films have a great potential for humidity sensing applications in room temperature operations.

  2. Growth and characterization of nitrogen-doped TiO2 thin films prepared by reactive pulsed laser deposition

    International Nuclear Information System (INIS)

    Sauthier, G.; Ferrer, F.J.; Figueras, A.; Gyoergy, E.

    2010-01-01

    Nitrogen-doped titanium dioxide (TiO 2 ) thin films were grown on (001) SiO 2 substrates by reactive pulsed laser deposition. A KrF* excimer laser source (λ = 248 nm, τ FWHM ≅ 10 ns, ν = 10 Hz) was used for the irradiations of pressed powder targets composed by both anatase and rutile phase TiO 2 . The experiments were performed in a controlled reactive atmosphere consisting of oxygen or mixtures of oxygen and nitrogen gases. The obtained thin film crystal structure was investigated by X-ray diffraction, while their chemical composition as well as chemical bonding states between the elements were studied by X-ray photoelectron spectroscopy. An interrelation was found between nitrogen concentration, crystalline structure, bonding states between the elements, and the formation of titanium oxinitride compounds. Moreover, as a result of the nitrogen incorporation in the films a continuous red-shift of the optical absorption edge accompanied by absorption in the visible spectral range between 400 and 500 nm wavelength was observed.

  3. Magnetic and Mössbauer studies of pure and Ti-doped YFeO {sub 3} nanocrystalline particles prepared by mechanical milling and subsequent sintering

    Energy Technology Data Exchange (ETDEWEB)

    Khalifa, N. O. [University of Khartoum, Physics Department, Faculty of Science (Sudan); Widatallah, H. M., E-mail: hishammw@squ.edu.om; Gismelseed, A. M.; Al-Mabsali, F. N.; Sofin, R. G. S. [Sultan Qaboos University, Physics Department, College of Science (Oman); Pekala, M. [University of Warsaw, Chemistry Department (Poland)

    2016-12-15

    Single-phased nanocrystalline particles of pure and 10 % Ti {sup 4+}-doped perovskite-related YFeO {sub 3}were prepared via mechanosynthesis at 450{sup ∘}C. This temperature is ∼150–350 {sup ∘}C lower than those at which the materials, in bulk form, are normally prepared. Rietveld refinements of the X-ray diffraction patterns reveal that the dopant Ti {sup 4+} ions prefer interstitial octahedral sites in the orthorhombic crystal lattice rather than those originally occupied by the expelled Fe {sup 3+} ions. Magnetic measurements show canted antiferromagnetism in both types of nanoparticles. Doping with Ti {sup 4+} lowers the Néel temperature of the YFeO {sub 3} nanoparticles from ∼ 586 K to ∼ 521 K. The Ti {sup 4+}-doped YFeO {sub 3} nanoparticles exhibit enhanced magnetization and coercivity but less magnetic hyperfine fields relative to the un-doped nanoparticles. The {sup 57}Fe Mössbauer spectra show ∼ 15 % of the YFeO {sub 3} nanoparticles and ∼22 of Ti {sup 4+}-doped YFeO {sub 3} ones to be superparamagnetic with blocking temperatures < 78 K. The broadened magnetic components in the {sup 57}Fe Mössbauer spectra suggest size-dependent hyperfine magnetic fields at the {sup 57}Fe nuclear sites and were associated with collective magnetic excitations. The {sup 57}Fe Mössbauer spectra show the local environments of the Fe {sup 3+} ions in the superparamagnetic nanoparticles to be more sensitive to the presence of the Ti {sup 4+} ions relative to those in the larger magnetic nanoparticles.

  4. Investigation on the structural and nonlinear optical properties of Pt doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Rahulan, K. Mani; Padmanathan, N.; Vinitha, G.; Kanakam, Charles Christopher

    2013-01-01

    Graphical abstract: The open aperture Z-scan traces of Pt doped TiO 2 nanoparticles at different Pt concentrations were carried out at an irradiation wavelength of 532 nm. It was numerically found that, two photon absorption (TPA) type process gives the best fit to the obtained open aperture Z-scan data. The nonlinear transmission was found to be of third order as it fits to a two-photon absorption. The optical limiting performances of nanoparticles were greatly enhanced with increased volume ratio of Pt. Increasing particle size reduced the limiting threshold and enhanced the optical limiting performance. - Highlights: • Pt doped TiO 2 nanoparticles with different concentrations of Pt have been synthesized by sol–gel method. • The average fluorescence lifetime decreases as the volume fraction of Pt dopant increases. • The effects of Pt content on the optical limiting property were investigated by open aperture Z-scan measurements done at 532 nm using 5 ns laser pulses. • The values of the third-order nonlinearities of nanoparticles are interesting from the application point of view which could be used as a potential candidate for the application of nonlinear optical device. - Abstract: Pt doped TiO 2 nanoparticles with different concentrations of Pt were prepared by sol–gel method. X-ray diffraction (XRD) study reveals that the samples have a homogeneous anatase phase tetragonal system and the lattice parameter analysis indicates that Pt ions substitute into the lattice of TiO 2 . The addition of dopant increases the growth of TiO 2 grains, agglomerates them and shifts the absorption band of TiO 2 from ultraviolet to visible region. The incorporation of Pt in TiO 2 is also confirmed by fluorescence quenching and the fluorescence lifetime decreases as the volume fraction of Pt dopant increases. Open aperture Z-scan measurements done at 532 nm using 7 ns laser pulses show nonlinear absorption which arises from an effective two photon absorption process

  5. Review on dielectric properties of rare earth doped barium titanate

    International Nuclear Information System (INIS)

    Ismail, Fatin Adila; Osman, Rozana Aina Maulat; Idris, Mohd Sobri

    2016-01-01

    Rare earth doped Barium Titanate (BaTiO_3) were studied due to high permittivity, excellent electrical properties and have wide usage in various applications. This paper reviewed on the electrical properties of RE doped BaTiO_3 (RE: Lanthanum (La), Erbium (Er), Samarium (Sm), Neodymium (Nd), Cerium (Ce)), processing method, phase transition occurred and solid solution range for complete study. Most of the RE doped BaTiO_3 downshifted the Curie temperature (T_C). Transition temperature also known as Curie temperature, T_C where the ceramics had a transition from ferroelectric to a paraelectric phase. In this review, the dielectric constant of La-doped BaTiO_3, Er-doped BaTiO_3, Sm-doped BaTiO_3, Nd-doped BaTiO_3 and Ce-doped BaTiO_3 had been proved to increase and the transition temperature or also known as T_C also lowered down to room temperature as for all the RE doped BaTiO_3 except for Er-doped BaTiO_3.

  6. Al{sub 2}O{sub 3} doping of TiO{sub 2} electrodes and applications in dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Eom, Tae Sung; Kim, Kyung Hwan; Bark, Chung Wung; Choi, Hyung Wook [Gachon University, Seongnam (Korea, Republic of)

    2014-08-15

    Dye-sensitized solar cells (DSSCs) have been intensively studied since their discovery in 1991. DSSCs have been extensively researched over the past decades as cheaper alternatives to silicon solar cells due to their high energy-conversion efficiency and their low production cost. However, some problems need to be solved in order to enhance the efficiency of DSSCs. In particular, the electron recombination that occurs due to the contact between the transparent conductive oxide (TCO) and a redox electrolyte is one of the main limiting factors of efficiency. In this work, we report for the first time the improvement of the photovoltaic characteristics of DSSCs by doping TiO{sub 2} with Al{sub 2}O{sub 3}. DSSCs were constructed using composite particles of Al{sub 2}O{sub 3}-doped TiO{sub 2} and TiO{sub 2} nanoparticles. The DSSCs using Al{sub 2}O{sub 3} showed the maximum conversion efficiency of 6.29% due to effective electron transport. DSSCs based on Al{sub 2}O{sub 3}-doped TiO{sub 2} films showed better photovoltaic performance than cells fabricated with only TiO{sub 2} nanoparticles. This result is attributed to the prevention of electron recombination between electrons in the TiO{sub 2} conduction band with holes in the dye or the electrolyte. There mechanism is suggested based on impedance results, which indicated improved electron transport at the TiO{sub 2}/dye/electrolyte interface.

  7. Designed fabrication of fluorine-doped carbon coated mesoporous TiO2 hollow spheres for improved lithium storage

    International Nuclear Information System (INIS)

    Geng, Hongbo; Ming, Hai; Ge, Danhua; Zheng, Junwei; Gu, Hongwei

    2015-01-01

    Graphical abstract: Hollow TiO 2 with mesoporous shell (MHTO) was successfully fabricated by a novel and controllable route, followed by fluorine-doped carbon coating the MHTO (MHTO-C/F), with the aim of enhancing the conductivity and stability of structures. - Highlights: • Anatase TiO 2 hollow spheres with mesoporous shells (MHTO) was fabricated via a facile and controllable route, to improve the lithium ion mobility as well as the stability of the architecture. • Fluorine-doped carbon derived from polyvinylidene difluoride was further encapsulated onto TiO 2 hollow spheres to improve the conductivity. • The composites could provide excellent electrochemical performance, which was desirable for the application of TiO 2 as an anode material in lithium ion batteries. - Abstract: In this manuscript, we demonstrated a facile route for the controllable design of “Fluorine (F)-doped carbon” (C/F)-treated TiO 2 hollow spheres with mesoporous shells (MHTO-C/F). The fabrication of this distinct mesoporous hollow structures and the C/F coating could effectively improve the electrolyte permeability and architectural stability, as well as electrical conductivity and lithium ion mobility. As anticipated, MHTO-C/F has several remarkable electrochemical properties, such as a high specific reversible capacity of 252 mA h g −1 , outstanding cycling stability of more than 210 mA h g −1 after 100 cycles at 0.5 C, and good rate performance of around 123 mA h g −1 at 5 C (1 C = 168 mA g −1 ). These properties are highly beneficial for lithium storage

  8. Low temperature synthesis of iodine-doped TiO2 nanocrystallites with enhanced visible-induced photocatalytic activity

    International Nuclear Information System (INIS)

    Ma Yi; Fu Jiwen; Tao Xia; Li Xin; Chen Jianfeng

    2011-01-01

    Iodine-doped TiO 2 nanocrystallites (denoted as I-TNCs) were prepared via a newly developed triblock copolymer-mediated sol-gel method at a temperature of 393 K. I-doping, crystallization and the formation of porous structure have been simultaneously achieved. The obtained particles were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and UV-vis spectrophotometer. The results indicated that the as-prepared I-TNCs possessed a diameter of ca. 5 nm with anatase crystalline structure and a specific surface area of over 200 m 2 g -1 . The presence of iodine expanded the photoresponse in visible light range, and led to enrich in surface hydroxyl group on the TiO 2 surface. Compared with the commercial photocatalyst P25, the I-TNCs significantly enhanced the photocatalytic efficiency in the degradation of rhodamine B and 2,4-dichlorophenol, and the I-TNCs with 2.5 mol% doping ratio exhibited the best photocatalytic activity.

  9. Study of A-site doping of SrBi4Ti4O15 Bi-layered compounds using micro-Raman spectroscopy

    International Nuclear Information System (INIS)

    Hao, H.; Liu, H.X.; Cao, M.H.; Min, X.M.; Ouyang, S.X.

    2006-01-01

    The temperature-dependent Raman spectra of Mg- and La-doped SrBi 4 Ti 4 O 15 (SBT) were studied in the range 40-590 C. A quantum chemistry calculation was employed to estimate these two substitution states. It was found that A-site doping in this study not only caused multiplicative substitution states, but also the Raman spectra changed with the substitution amount. In a La-doped perovskite-like layer, La would occupy the Bi site when x>0.10 and the 314 and 550 cm -1 modes related to the rotating and tilting of the TiO 6 octahedron firstly became wide and then became sharp. With the increase of the substitution amount, both substitution states of Mg-doped SBT lead to the widening of 270 and 520 cm -1 peaks. (orig.)

  10. Study of A-site doping of SrBi4Ti4O15 Bi-layered compounds using micro-Raman spectroscopy

    Science.gov (United States)

    Hao, H.; Liu, H. X.; Cao, M. H.; Min, X. M.; Ouyang, S. X.

    2006-10-01

    The temperature-dependent Raman spectra of Mg- and La-doped SrBi4Ti4O15 (SBT) were studied in the range 40 590 °C. A quantum chemistry calculation was employed to estimate these two substitution states. It was found that A-site doping in this study not only caused multiplicative substitution states, but also the Raman spectra changed with the substitution amount. In a La-doped perovskite-like layer, La would occupy the Bi site when x>0.10 and the 314 and 550 cm-1 modes related to the rotating and tilting of the TiO6 octahedron firstly became wide and then became sharp. With the increase of the substitution amount, both substitution states of Mg-doped SBT lead to the widening of 270 and 520 cm-1 peaks.

  11. Structural evolution and electrical properties of BaTiO{sub 3} doped with Gd{sup 3+}

    Energy Technology Data Exchange (ETDEWEB)

    Hernandez Lara, Juan Pablo; Perez Labra, Miguel; Barrientos Hernandez, Francisco Raul, E-mail: miguelabra@hotmail.com [Autonomous University of Hidalgo (Mexico); Romero Serrano, Jose Antonio; Hernandez Ramirez, Aurelio [Metallurgy and Materials Department, ESIQIE-IPN, UPALM, Zacatenco (Mexico); Avila Davila, Erika Osiris [Mechanical Engineering Department, Technological Institute of Pachuca, Hidalgo (Mexico); Thangarasu, Pandiyan [Facultad de Quimica, UNAM, Mexico D.F. (Mexico)

    2017-03-15

    BaTiO{sub 3} doped with Gd{sup 3+} (Ba{sub 1-x}Gd{sub x}Ti{sub 1-x/4}O{sub 3}) was synthesized using the solid-state reaction method with x = 0.001, 0.003, 0.005, 0.01, 0.05, 0.1, 0.15, 0.20, 0.25, 0.30, and 0.35 Gd{sup 3+} (wt. %). The powders were decarbonated at 900 °C and sintered at 1400 °C for 8 hours. The tetragonality of the synthesized Gd{sup 3+}-doped BaTiO{sub 3} particles was analyzed. XRD patterns and Raman spectra revealed that the crystal phase of the obtained particles was predominately tetragonal BaTiO{sub 3}; the intensity of the Raman bands at 205 cm{sup -1}, 265 cm{sup -1}, and 304 cm{sup -1} decreased when Gd'3{sup +} was increased. A secondary phase (Gd{sub 2}Ti{sub 2}O{sub 7}) was found when the Gd{sup 3+} content was higher than 0.15 wt. %. The capacitance of the sintering pellets was measured at 1 kHz; these values were used to calculate the relative permittivity, the maximum permittivity values were recorded for the samples with x = 0.001, 0.005, and 0.1. (author)

  12. Microstructural changes of Y-doped V-4Cr-4Ti alloys after ion and neutron irradiation

    Directory of Open Access Journals (Sweden)

    H. Watanabe

    2016-12-01

    Full Text Available High-purity Y-doped V-4Cr-4Ti alloys (0.1–0.2wt. % Y, manufactured by the National Institute for Fusion Science (NIFS, were used for this study. Heavy-ion and fission-neutron irradiation was carried out at temperatures 673–873K. During the ion irradiation at 873K, the microstructure was controlled by the formation of Ti(C,O,N precipitates lying on the (100 plane. Y addition effectively suppressed the growth of Ti(C,O,N precipitates, especially at lower dose irradiation to up to 4 dpa. However, at higher dose levels (12.0 dpa, the number density was almost at the same levels irrespective of the presence of Y. After neutron irradiation at 873K, fine titanium oxides were also observed in all V alloys. However, smaller oxide sizes were observed in the Y-doped samples under the same irradiation conditions. The detailed analysis of EDS showed that the center of the Ti(C,O,N precipitates was mainly enriched by nitrogen. The results showed that the contribution of not only oxygen atoms picked up from the irradiation environment but also nitrogen atoms is essential to understand the microstructural evolution of V-4Cr-4Ti-Y alloys.

  13. Photocatalytic degradation of different chromophoric dyes in aqueous phase using La and Mo doped TiO{sub 2} hybrid carbon spheres

    Energy Technology Data Exchange (ETDEWEB)

    Raza, Waseem; Haque, M.M. [Department of Chemistry, Aligarh Muslim University, Aligarh 202002 (India); Muneer, M., E-mail: m.muneer.ch@amu.ac.in [Department of Chemistry, Aligarh Muslim University, Aligarh 202002 (India); Fleisch, M.; Hakki, A.; Bahnemann, D. [Institut fuer Technische Chemie, Leibniz Universität Hannover, Callinstrasse 3, D-30167 Hannover (Germany)

    2015-05-25

    Highlights: • La and Mo doped TiO{sub 2} hybrid carbon spheres have been synthesized using hydrothermal method. • The characterization of La and Mo doped TiO{sub 2} hybrid carbon spheres uniform morphology having anatase phase and good structural stability. • TiO{sub 2} hybrid carbon spheres with dopant concentration of 2.0% (La) and 1.5% (Mo) showed the highest photocatalytic activity as compared to the other dopant concentrations for the degradation of all the dyes under investigation. - Abstract: La and Mo-doped TiO{sub 2} coated carbon spheres have been synthesized using the hydrothermal method. The prepared materials were characterized by standard analytical techniques, X-ray diffraction (XRD), UV–Vis spectrophotometry, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX) and Raman spectroscopy. The XRD and Raman spectroscopic analysis showed that the particles are in anatase phase. The EDX and SEM images showed that La/Mo-doped TiO{sub 2} are present on the surface of the carbon spheres. The photocatalytic activity of the synthesized particles were tested by studying the degradation of three different chromophoric dyes, i.e., Acid Yellow 29 (azo dye), Coomassie Brilliant Blue G250 (triphenylmethane dye) and Acid Green 25 (anthraquinone dye) as a function of time on irradiation in aqueous suspension. TiO{sub 2} particle with dopant concentration of 2.0% La and 1.5% Mo showed the highest photocatalytic activity as compared to the other dopant concentrations for the degradation of all the dyes under investigation.

  14. Engineering the switching dynamics of TiO{sub x}-based RRAM with Al doping

    Energy Technology Data Exchange (ETDEWEB)

    Trapatseli, Maria, E-mail: mt3c13@soton.ac.uk; Khiat, Ali; Cortese, Simone; Serb, Alexantrou; Carta, Daniela; Prodromakis, Themistoklis [Nano Group, School of Electronics and Computer Science, University of Southampton, Southampton SO17 1BJ (United Kingdom)

    2016-07-14

    Titanium oxide (TiO{sub x}) has attracted a lot of attention as an active material for resistive random access memory (RRAM), due to its versatility and variety of possible crystal phases. Although existing RRAM materials have demonstrated impressive characteristics, like ultra-fast switching and high cycling endurance, this technology still encounters challenges like low yields, large variability of switching characteristics, and ultimately device failure. Electroforming has been often considered responsible for introducing irreversible damage to devices, with high switching voltages contributing to device degradation. In this paper, we have employed Al doping for tuning the resistive switching characteristics of titanium oxide RRAM. The resistive switching threshold voltages of undoped and Al-doped TiO{sub x} thin films were first assessed by conductive atomic force microscopy. The thin films were then transferred in RRAM devices and tested with voltage pulse sweeping, demonstrating that the Al-doped devices could on average form at lower potentials compared to the undoped ones and could support both analog and binary switching at potentials as low as 0.9 V. This work demonstrates a potential pathway for implementing low-power RRAM systems.

  15. Electric controlling of surface metal-insulator transition in the doped BaTiO3 film

    Directory of Open Access Journals (Sweden)

    Wei Xun

    2017-07-01

    Full Text Available Based on first-principles calculations, the BaTiO3(BTO film with local La-doping is studied. For a selected concentration and position of doping, the surface metal-insulator transition occurs under the applied electric field, and the domain appears near the surface for both bipolar states. Furthermore, for the insulated surface state, i.e., the downward polarization state in the doped film, the gradient bandgap structure is achieved, which favors the absorption of solar energy. Our investigation can provide an alternative avenue in modification of surface property and surface screening effect in polar materials.

  16. Low sintering temperature and high piezoelectric properties of Li-doped (Ba,Ca)(Ti,Zr)O3 lead-free ceramics

    International Nuclear Information System (INIS)

    Chen, Xiaoming; Ruan, Xuezheng; Zhao, Kunyun; He, Xueqing; Zeng, Jiangtao; Li, Yongsheng; Zheng, Liaoying; Park, Chul Hong; Li, Guorong

    2015-01-01

    Highlights: • Li-doped Ba 0.85 Ca 0.15 Ti 0.9 Zr 0.1 O 3 (BCZT) lead-free piezoceramics were prepared by the two-step synthesis and solid-state reaction method. • Their sintering temperature decreases from about 1540 °C down to about 1400 °C. • With the proper addition of Li, the densities and grain sizes of ceramics increase. • The ceramics not only have the characteristics of hard piezoceramics but also possesses the features of soft piezoceramics at low sintering temperature. - Abstract: Li-doped Ba 0.85 Ca 0.15 Ti 0.9 Zr 0.1 O 3 (BCZT) lead-free piezoelectric ceramics were prepared by the two-step synthesis and the solid-state reaction method. The density and grain size of ceramics sufficiently increases by Li-doped sintering aid, and their sintering temperature decreases from about 1540 °C down to about 1400 °C. X-ray diffraction reveals that the phase structure of Li-doped BCTZ ceramics is changed with the sintering temperature, which is consistent with their phase transition observed by the temperature-dependent dielectric curves. The well-poled Li-doped BCZT ceramics show a high piezoelectric constant d 33 (512 pC/N) and a planar electromechanical coupling factor k p (0.49), which have the characteristics of soft Pb(Zr,Ti)O 3 (PZT) piezoceramic, on the other hand, the mechanical quality factor Q m is about 190, which possesses the features of hard PZT piezoceramics. The enhanced properties of the Li-doped BCZT are explained by the combination of Li-doped effect and sintering effect on the microstructure and the phase transition around room temperature

  17. New insights on the synthesis and electronic transport in bulk polycrystalline Pr-doped SrTiO3−δ

    KAUST Repository

    Dehkordi, Arash Mehdizadeh; Bhattacharya, Sriparna; Darroudi, Taghi; Alshareef, Husam N.; Tritt, Terry M.

    2015-01-01

    versus Pr6O11) on the synthesis and electronic transport in Pr-doped SrTiO3 ceramics. It was observed that the high-temperature electronic transport properties are independent of the choice of praseodymium doping source for samples prepared following our

  18. Preparation of K-doped TiO{sub 2} nanostructures by wet corrosion and their sunlight-driven photocatalytic performance

    Energy Technology Data Exchange (ETDEWEB)

    Shin, Eunhye; Jin, Saera; Kim, Jiyoon; Chang, Sung-Jin [Department of Chemistry, Chung-Ang University, Seoul 06974 (Korea, Republic of); Jun, Byung-Hyuk [Neutron Science Division, Korea Atomic Energy Research Institute, Daejeon 34057 (Korea, Republic of); Park, Kwang-Won, E-mail: bryan.kwangwon.park@gmail.com [Department of Chemistry, Chung-Ang University, Seoul 06974 (Korea, Republic of); Hong, Jongin, E-mail: hongj@cau.ac.kr [Department of Chemistry, Chung-Ang University, Seoul 06974 (Korea, Republic of)

    2016-08-30

    Highlights: • Potassium-doped TiO{sub 2} nanowire networks were prepared by the corrosion reaction of Ti nanoparticles in an alkaline solution. • They were applied to sunlight-driven photocatalytic degradation of differently charged dye molecules. • The adsorption of the dye molecules on the photocatalyst surface is crucial for their sunlight-driven photodegradation. - Abstract: K-doped TiO{sub 2} nanowire networks were prepared by the corrosion reaction of Ti nanoparticles in an alkaline (potassium hydroxide: KOH) solution. The prepared nanostructures were characterized by scanning electron microscopy (SEM), Brunauer-Emmett-Teller (BET) analysis, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, X-ray diffraction (XRD) and photoluminescence (PL) spectra. Their sunlight-driven photocatalytic activity was also investigated with differently charged dye molecules, such as methylene blue, rhodamine B and methyl orange. The adsorption of the dye molecules on the photocatalyst surface would play a critical role in their selective photodegradation under sunlight illumination.

  19. Integrated photooxidative extractive deep desulfurization using metal doped TiO2 and eutectic based ionic liquid

    Science.gov (United States)

    Zaid, Hayyiratul Fatimah Mohd; Kait, Chong Fai; Mutalib, Mohamed Ibrahim Abdul

    2016-11-01

    A series of metal doped TiO2 namely Fe/TiO2, Cu/TiO2 and Cu-Fe/TiO2 were synthesized and characterized, to be used as a photocatalyst in the integrated photooxidative extractive deep desulfurization for model oil (dodecane) and diesel fuel. The order of the photocatalytic activity was Cu-Fe/TiO2 followed by Cu/TiO2 and then Fe/TiO2. Cu-Fe/TiO2 was an effective photocatalyst for sulfur conversion at ambient atmospheric pressure. Hydrogen peroxide was used as the source of oxidant and eutectic-based ionic liquid as the extractant. Sulfur conversion in model oil reached 100%. Removal of sulfur from model oil was done by two times extraction with a removal of 97.06% in the first run and 2.94% in the second run.

  20. Synthesis and photocatalytic activity of Eu3+-doped nanoparticulate TiO2 sols and thermal stability of the resulting xerogels

    International Nuclear Information System (INIS)

    Borlaf, Mario; Moreno, Rodrigo; Ortiz, Angel L.; Colomer, María T.

    2014-01-01

    The synthesis of nanoparticulate TiO 2 sols without and with Eu 3+ doping (1, 2, or 3 mol%) by the colloidal sol–gel method in aqueous media was investigated, with emphasis on the effect of the Eu 3+ doping on the peptization time and rheological properties of the sols. It was found that the addition of Eu 3+ increasingly retards the peptization process, and also results in sols with greater aggregate sizes which are therefore more viscous, although in all cases the distributions of aggregate sizes are unimodal and the flow behavior is Newtonian. The shifting of the isoelectric point of the sols toward greater pH with increasing Eu 3+ doping indicates that the aforementioned trends are due to the chemical adsorption of europium ionic complexes in the form of solvated species. Furthermore, the effect of Eu 3+ doping on the ultraviolet–visible spectrum and photocatalytic activity of the peptized sols was also explored. It was found that the Eu 3+ doping increasingly shifts slightly the absorption edge from the ultraviolet to the visible range, and that its effect on the photocatalytic activity is certainly complex because this is enhanced only if the Eu 3+ cations have some electronic transition (charge transfer transition or transitions between the ground state and the excited states) at the wavelength of the incident radiation, in which case the photocatalytic activity first increases with increasing Eu 3+ content and then decreases perhaps due to occurrence of Eu–Eu interactions or simply to the greater aggregation state. Finally, the influence of the Eu 3+ doping on the thermal stability of the nanoparticulate xerogels resulting from the drying of the peptized sols was also examined by X-ray thermo-diffractometry together with transmission electron microscopy, selected area electron diffractometry, and X-ray energy-dispersive spectrometry. It was found that although the xerogels crystallize all as anatase phase, this is increasingly more thermally stable

  1. Nitrogen and vanadium Co-doped TiO{sub 2} mesosponge layers for enhancement in visible photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Jiasong Zhong [College of Materials and Environmental Engineering, Hangzhou Dianzi University, Hangzhou, 310018 (China); Xu, Jinrong [Department of Mathematics and Physics, Anhui University of Architecture, Hefei, 230022 (China); Wang, Qingyao, E-mail: wangqingyao0532@163.com [School of Chemistry and Materials Science, Ludong University, Yantai, 264025 (China)

    2014-10-01

    Graphical abstract: - Highlights: • N and V co-doped TiO{sub 2} mesosponges were prepared by hydrothermal method. • The first-principle was used to investigate the novel porous materials. • N-V-TMSW had a remarkable visible absorption and photocatalytic activity. - Abstract: Novel N and V co-doped TiO{sub 2} mesosponge (N-V-TMSW) layers were successfully prepared by one-step hydrothermal treatment of TiO{sub 2} nanotube arrays, and the phase composition, morphology and optical property were characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Atomic force microscope (AFM), X-ray photoelectron spectroscopy (XPS) and UV–vis diffusion reflectance spectroscopy (DRS). The crystal structure and density of states were studied by means of the first-principle pseudo-potential plane wave. The results indicated that titanium ions and oxygen atoms in TiO{sub 2} were successfully substituted by vanadium ions and nitrogen atoms, respectively. The sample N-V0.1-TMSW showed a remarkable absorption in the visible light range of 400–600 nm and high visible photocatalytic activity.

  2. A Double Layer Sensing Electrode “BaTi(1-XRhxO3/Al-Doped TiO2” for NO2 Detection above 600 °C

    Directory of Open Access Journals (Sweden)

    Bilge Saruhan

    2016-04-01

    Full Text Available NO2 emission is mostly related to combustion processes, where gas temperatures exceed far beyond 500 °C. The detection of NO2 in combustion and exhaust gases at elevated temperatures requires sensors with high NO2 selectivity. The thermodynamic equilibrium for NO2/NO ≥ 500 °C lies on the NO side. High temperature stability of TiO2 makes it a promising material for elevated temperature towards CO, H2, and NO2. The doping of TiO2 with Al3+ (Al:TiO2 increases the sensitivity and selectivity of sensors to NO2 and results in a relatively low cross-sensitivity towards CO. The results indicate that NO2 exposure results in a resistance decrease of the sensors with the single Al:TiO2 layers at 600 °C, with a resistance increase at 800 °C. This alteration in the sensor response in the temperature range of 600 °C and 800 °C may be due to the mentioned thermodynamic equilibrium changes between NO and NO2. This work investigates the NO2-sensing behavior of duplex layers consisting of Al:TiO2 and BaTi(1-xRhxO3 catalysts in the temperature range of 600 °C and 900 °C. Al:TiO2 layers were deposited by reactive magnetron sputtering on interdigitated sensor platforms, while a catalytic layer, which was synthesized by wet chemistry in the form of BaTi(1-xRhxO3 powders, were screen-printed as thick layers on the Al:TiO2-layers. The use of Rh-incorporated BaTiO3 perovskite (BaTi(1-xRhxO3 as a catalytic filter stabilizes the sensor response of Al-doped TiO2 layers yielding more reliable sensor signal throughout the temperature range.

  3. XAS study of the local environment of impurities in doped TiO{sub 2} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Rodriguez Torres, C.E. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina)]. E-mail: torres@fisica.unlp.edu.ar; Cabrera, A.F. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina); Errico, L.A. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina); Duhalde, S. [Lab. de Ablacion Laser, FI-UBA (Argentina); Renteria, M. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina); Golmar, F. [Lab. de Ablacion Laser, FI-UBA (Argentina); Sanchez, F.H. [Departamento de Fisica e IFLP (CONICET), Facultad de Ciencias Exactas, Universidad Nacional de La Plata (Argentina)

    2007-09-01

    In this work, we present an X-ray absorption spectroscopy (XAS) characterization of the local environment of the impurity in room temperature ferromagnetic (RTF) anatase TiO{sub 2} thin films doped with Co, Ni, Cu, or Zn, deposited on LaAlO{sub 3} substrate by pulsed laser deposition (PLD). It was found that there is a considerable amount of impurity atoms substituting Ti in TiO{sub 2} anatase, although the presence of metal transition monoxide clusters can not be discarded. From our results, we infer that the observed RT ferromagnetism of the samples could be assigned to the metal transition atoms replacing Ti in TiO{sub 2} anatase.

  4. Investigation of the Influence of Ni Doping on the Structure and Hardness of Ti-Ni-C Coatings

    Directory of Open Access Journals (Sweden)

    J. Daniel

    2017-01-01

    Full Text Available Nanocomposite nc-TiC/a-C:H thin films exhibit unique combination of mechanical properties, high hardness, low friction, and wear. Selective doping by weak-carbide forming element can be used in order to specifically design the physical and chemical properties of nc-TiC/a-C:H coatings. In this paper we report on an effect of nickel addition on structure and hardness of the nc-TiC/a-C:H coatings. The effect of Ni alloying on the coating structure under conditions of DCMS and HiPIMS depositions was studied. The coating structure was correlated with the coating hardness. The grain size, the grain carbon vacancy concentration, and the mean grain separation were found to be the key parameters determining the coating hardness. Ni doping proved to have a significant effect on the coating microstructure which resulted in changes of the hardness of the deposited coatings.

  5. RBS and ion channeling studies of Ag-doped YBa2Cu3O7-δ targets and films

    International Nuclear Information System (INIS)

    Li Yupu; Liu, J.R.; Cui, X.T.; Chu, W.K.

    1998-01-01

    The location of Ag in Ag-doped YBa 2 Cu 3 O 7-δ (YBCO) films and other high-T c materials (such as Ag-doped BiSrCaCuO films and Ag-sheathed textured BiSrCaCuO wires) is a very important issue for improving high-T c materials. In this work, laser ablated and DC magnetron sputtered YBCO films on (100) LaAlO 3 and (100) SrTiO 3 were prepared from sintered Ag-YBCO composite targets (nominally containing 5 wt% Ag) and studied by Rutherford backscattering spectrometry (RBS) and ion channeling techniques using 2.0 MeV 4 He + and 7 Li + beams. We have found that the Ag-YBCO targets contain about 3 wt% Ag and most of the retained Ag atoms form some small size Ag precipitates with a typical size smaller than a few microns. We have demonstrated that in very good single crystalline YBCO films, the percentage of retained Ag in substitutional sites can be estimated by ion channeling technique. For example, we have found that about 1.2 wt% Ag atoms remain in the laser ablated Ag-doped films prepared from the Ag-YBCO target and about two-thirds of the retained Ag atoms occupy substitutional sites. The sputtered films contain less retained Ag atoms since the deposition temperature is higher and deposition time is longer than those for laser ablated films. (orig.)

  6. Thin Film growth and characterization of Ti doped ZnO by RF/DC magnetron sputtering

    KAUST Repository

    Baseer Haider, M.

    2015-01-01

    Thin film Ti doped ZnO (Ti-ZnO) film were grown on sapphire (0001) substrate by RF and DC magnetron sputtering. Films were grown at a substrate temperature of 250 °C with different Ti/Zn concentration. Surface chemical study of the samples was performed by X-ray photoelectron spectroscopy to determine the stoichiometry and Ti/Zn ratio for all samples. Surface morphology of the samples were studied by atomic force microscopy. X-ray diffraction was carried out to determine the crystallinity of the film. No secondary phases of TixOy was observed. We observed a slight increase in the lattice constant with the increase in Ti concentration in ZnO. No ferromagnetic signal was observed for any of the samples. However, some samples showed super-paramagnetic phase. © 2015 Materials Research Society.

  7. Microstructure and properties of duplex (Ti:N)-DLC/MAO coating on magnesium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Wei; Ke, Peiling [Ningbo Key Laboratory of Marine Protection Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Fang, Yong [Sir Run Run Shaw Hospital, School of Medicine, Zhe Jiang University, Zhejiang 310016 (China); Zheng, He [Ningbo Key Laboratory of Marine Protection Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Wang, Aiying, E-mail: aywang@nimte.ac.cn [Ningbo Key Laboratory of Marine Protection Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China)

    2013-04-01

    Ti and N co-doped diamond-like carbon ((Ti:N)-DLC) film was deposited on the MAO coated substrate using a hybrid beam deposition system, which consists of a DC magnetron sputtering of Ti target and a linear ion source (LIS) with C{sub 2}H{sub 2} and N{sub 2} precursor gas. The microstructure and properties of the duplex (Ti:N)-DLC/MAO coating were investigated. Results indicate that the (Ti:N)-DLC top film with TiN crystalline phase was formed. Ti and N co-doping resulted in the increasing I{sub D}/I{sub G} ratio. The significant improvement in the wear and corrosion resistance of duplex (Ti:N)-DLC/MAO coating was mainly attributed to the increased binding strength, lubrication characteristics and chemical inertness of (Ti:N)-DLC top film. The superior low-friction and anti-corrosion properties of duplex (Ti:N)-DLC/MAO coating make it a good candidate as protective coating on magnesium alloy.

  8. Fabrication and characterization of polyvinyl alcohol/metal (Ca, Mg, Ti) doped zirconium phosphate nanocomposite films for scaffold-guided tissue engineering application.

    Science.gov (United States)

    Kalita, Himani; Pal, Pallabi; Dhara, Santanu; Pathak, Amita

    2017-02-01

    Nanocomposite films of polyvinyl alcohol (PVA) and zirconium phosphate (ZrP)/doped ZrP (doped with Ca, Mg, Ti) nanoparticles have been developed by solvent casting method to assess their potential as matrix material in scaffold-guided tissue engineering application. The prepared ZrP and doped ZrP nanoparticles as well as the nanocomposite films were characterized by various spectroscopic and microscopic techniques. Nanoindentation studies revealed improved nanomechanical properties in the PVA/doped ZrP nanocomposite films (highest for PVA/Ti doped ZrP: hardness=262.4MPa; elastic modulus=5800MPa) as compared to the PVA/ZrP and neat PVA films. In-vitro cell culture experiments carried out to access the cellular viability, attachment, proliferation, and migration on the substrates, using mouse fibroblast (3T3) cell lines, inferred enhanced bioactivity in the PVA/doped ZrP nanocomposite films (highest for PVA/Ca doped ZrP) in contrast to PVA/ZrP and neat PVA films. Controlled biodegradability as well as swelling behavior, superior bioactivity and improved mechanical properties of the PVA/doped ZrP nanocomposite films make them promising matrix materials for scaffold-guided tissue engineering application. Copyright © 2016 Elsevier B.V. All rights reserved.

  9. P-doped strontium titanate grown using two target pulsed laser deposition for thin film solar cells

    Science.gov (United States)

    Man, Hamdi

    Thin-film solar cells made of Mg-doped SrTiO3 p-type absorbers are promising candidates for clean energy generation. This material shows p-type conductivity and also demonstrates reasonable absorption of light. In addition, p-type SrTiO3 can be deposited as thin films so that the cost can be lower than the competing methods. In this work, Mg-doped SrTiO3 (STO) thin-films were synthesized and analyzed in order to observe their potential to be employed as the base semiconductor in photovoltaic applications. Mg-doped STO thin-films were grown by using pulsed laser deposition (PLD) using a frequency quadrupled Yttrium Aluminum Garnet (YAG) laser and with a substrate that was heated by back surface absorption of infrared (IR) laser light. The samples were characterized using X-ray photoelectron spectroscopy (XPS) and it was observed that Mg atoms were doped successfully in the stoichiometry. Reflection high energy electron diffraction (RHEED) spectroscopy proved that the thin films were polycrystalline. Kelvin Probe work function measurements indicated that the work function of the films were 4.167 eV after annealing. UV/Vis Reflection spectroscopy showed that Mg-doped STO thin-films do not reflect significantly except in the ultraviolet region of the spectrum where the reflection percentage increased up to 80%. Self-doped STO thin-films, Indium Tin Oxide (ITO) thin films and stainless steel foil (SSF) were studied in order to observe their characteristics before employing them in Mg-doped STO based solar cells. Self-doped STO thin films were grown using PLD and the results showed that they are capable of serving as the n-type semiconductor in solar cell applications with oxygen vacancies in their structure and low reflectivity. Indium Tin Oxide thin-films grown by PLD system showed low 25-50 ?/square sheet resistance and very low reflection features. Finally, commercially available stainless steel foil substrates were excellent substrates for the inexpensive growth of

  10. N-doped hollow urchin-like anatase TiO2@C composite as a novel anode for Li-ion batteries

    Science.gov (United States)

    Xing, Yalan; Wang, Shengbin; Fang, Baizeng; Song, Ge; Wilkinson, David P.; Zhang, Shichao

    2018-05-01

    N-doped hollow urchin-like anatase TiO2 spheres (HUTSs) with carbon coating (HUTS@C) are prepared through a facile and scalable hydrothermal reaction followed by coating of polypyrrole and carbonization. The HUTS is composed of radially grown anatase nanorods and possesses an enhanced percentage of exposed {001} facets compared with P25 TiO2 nanoparticles. After the carbon coating, the HUTS@C retains the hollow nanostructure although covered with an N-doped carbon layer. As an anode for Li-ion batteries, the HUTS@C delivers a higher capacity of 165.1 mAh g-1 at 1C after 200 cycles and better rate capability (111.7 mAh g-1 at 10C) than the HUTS. Further electrochemical studies reveal that the HUTS@C has a better electrochemical reversibility, lower charge-transfer resistance, and higher Li-ion diffusion coefficient due to its unique nanosctructure including the hollow core, anatase phase of TiO2 microspheres with high exposed {001} facets and the N-doped carbon layer, which facilitates mass transport and enhances electrical conductivity.

  11. Microwave-assisted synthesis of C-doped TiO2 and ZnO hybrid nanostructured materials as quantum-dots sensitized solar cells

    Science.gov (United States)

    Rangel-Mendez, Jose R.; Matos, Juan; Cházaro-Ruiz, Luis F.; González-Castillo, Ana C.; Barrios-Yáñez, Guillermo

    2018-03-01

    The microwave-assisted solvothermal synthesis of C-doped TiO2 and ZnO hybrid materials was performed. Saccharose, titanium isopropoxide and zinc acetate were used as organic and inorganic sources for the synthesis. The influence of temperature and reaction time on the textural and optoelectronic properties of the hybrid materials was verified. Carbon quantum-dots of TiO2 and ZnO nanostructured spheres were obtained in a second pot by controlled calcination steps of the precursor hybrid materials. A carefully characterization by adsorption-desorption N2 isotherms, XRD, XPS, SEM, UV-vis/DR and electro- and photo-electrochemistry properties of the carbon quantum-dots TiO2 and ZnO spheres was performed. The photoelectrochemical activity of TiO2-C and ZnO-C films proved to be dependent on the conditions of synthesis. It was found a red-shift in the energy band gap of the semiconductors with values of 3.02 eV and 3.13 eV for the TiO2-C and ZnO-C, respectively, clearly lower than those on bare semiconductors, which is associated with the C-doping effect. From the photo-electrochemistry characterization of C-doped TiO2 and ZnO films can be concluded that the present materials have potential applications as photoelectrodes for quantum-dots sensitized solar cells.

  12. The Effect of TiO₂ Doped Photocatalytic Nano-Additives on the Hydration and Microstructure of Portland and High Alumina Cements.

    Science.gov (United States)

    Pérez-Nicolás, María; Navarro-Blasco, Íñigo; Fernández, José M; Alvarez, José Ignacio

    2017-10-14

    Mortars with two different binders (Portland cement (PC) and high alumina cement (HAC)) were modified upon the bulk incorporation of nano-structured photocatalytic additives (bare TiO₂, and TiO₂ doped with either iron (Fe-TiO₂) or vanadium (V-TiO₂)). Plastic and hardened state properties of these mortars were assessed in order to study the influence of these nano-additives. Water demand was increased, slightly by bare TiO₂ and Fe-TiO₂, and strongly by V-TiO₂, in agreement with the reduction of the particle size and the tendency to agglomerate. Isothermal calorimetry showed that hydration of the cementitious matrices was accelerated due to additional nucleation sites offered by the nano-additives. TiO₂ and doped TiO₂ did not show pozzolanic reactivity in the binding systems. Changes in the pore size distribution, mainly the filler effect of the nano-additives, accounted for the increase in compressive strengths measured for HAC mortars. A complex microstructure was seen in calcium aluminate cement mortars, strongly dependent on the curing conditions. Fe-TiO₂ was found to be homogeneously distributed whereas the tendency of V-TiO₂ to agglomerate was evidenced by elemental distribution maps. Water absorption capacity was not affected by the nano-additive incorporation in HAC mortars, which is a favourable feature for the application of these mortars.

  13. FTIR study of formic acid interaction with TiO2 and TiO2 doped with Pd and Cu in photocatalytic processes

    International Nuclear Information System (INIS)

    Arana, J.; Garriga i Cabo, C.; Dona-Rodriguez, J.M.; Gonzalez-Diaz, O.; Herrera-Melian, J.A.; Perez-Pena, J.

    2004-01-01

    In this study the different processes occurring on the TiO 2 and Pd and Cu doped TiO 2 surfaces during the photocatalytic formic acid degradation in the presence or absence of S 2 O 8 2- or H 2 O 2 have been investigated. FTIR studies have shown the relevance of the H-bounded hydroxyl groups. It has been observed that formate molecules interact simultaneously with the dopants and surfacial Ti atoms yielding an intermediate species which plays an important role in the phototacatalytic degradation mechanism. Also, it has been determined that Pd or Cu oxides may act as receptors or transmitters of the TiO 2 photogenerated electrons and thus modify the degradation mechanism. Different redox reactions have been proposed according to the obtained results

  14. Effect of heat treatment on the physical properties of bimetallic doped catalyst, Cu-Ni/TiO2

    International Nuclear Information System (INIS)

    Bashiri, Robabeh; Sufian, Suriati; Mohamed, Norani Muti; Kait, Chong Fai

    2015-01-01

    Post heat treatment is critical for the doped semiconductor oxide in order to improve its photocatalytic performance. Thus work had been carried out to understand the effect of different calcination temperature (400, 450 and 500°C) on the physical properties of nanosized Cu-Ni/TiO 2 Cu-Ni doped TiO 2 nanoparticles prepared using a combined method of sol-gel and hydrothermal. The treated samples were characterized using Raman spectroscopy, Brunauer–Emmett–teller (BET) measurement, high resolution transmission electron microscopy (HRTEM), field-emission scanning electron microscopy (FESEM), and diffuse reflectance UV-Vis spectroscopy (DR-UV-Vis). Raman analysis showed that all samples displayed anatase (101) phase of TiO 2 , which is in good agreement with the TEM results. BET data showed that all prepared Cu-Ni/TiO 2 with different calcination temperature are mesoporous. SEM images displayed spherical particles with typical size of about 15 to 20 nm. UV-Vis spectra illustrated that the absorbance edge of all prepared Cu-Ni/TiO 2 have extended to the visible region with bandgap energies (2-2.1 eV) less than the pure anatase TiO 2 (3.2 eV). Calcination temperature of 450°C is considered to be the optimum as it converts the synthesized Cu-Ni/TiO 2 sample to have smaller average particle size with higher surface area that lead to more absorbance in the visible region and lower bandgap energy

  15. Screened coulomb hybrid DFT study on electronic structure and optical properties of anionic and cationic Te-doped anatase TiO2

    KAUST Repository

    Harb, Moussab

    2013-06-27

    The origin of the enhanced visible-light optical absorption in Te-doped bulk anatase TiO2 is investigated in the framework of DFT and DFPT within HSE06 in order to ensure accurate electronic structure and optical transition predictions. Various oxidation states of Te species are considered based on their structural location in bulk TiO2. In fact, TiO (2-x)Tex (with isolated Te2- species at Te-Te distance of 8.28 Å), TiO2Tex (with isolated TeO 2- species at Te-Te distance of 8.28 Å), TiO2Te 2x (with two concomitant TeO2- species at Te-Te distance of 4.11 Å), and Ti(1-2x)O2Te2x (with two neighboring Te4+ species at nearest-neighbor Te-Te distance of 3.05 Å) show improved optical absorption responses in the visible range similarly as it is experimentally observed in Te-doped TiO2 powders. The optical absorption edges of TiO(2-x)Tex, TiO 2Tex, and TiO2Te2x are found to be red-shifted by 400 nm compared with undoped TiO2 whereas that of Ti(1-2x)O2Te2x is red-shifted by 150 nm. On the basis of calculated valence and conduction band edge positions of Te-doped TiO2, only TiO(2-x)Tex and Ti (1-2x)O2Te2x show suitable potentials for overall water splitting under visible-light irradiation. The electronic structure analysis revealed narrower band gaps of 1.12 and 1.17 eV with respect to undoped TiO2, respectively, resulting from the appearance of new occupied electronic states in the gap of TiO2. A delocalized nature of the gap states is found to be much more pronounced in TiO (2-x)Tex than that with Ti(1-2x)O 2Te2x due to the important contribution of numerous O 2p orbitals together with Te 5p orbitals. © 2013 American Chemical Society.

  16. Electron paramagnetic resonance investigations of Fe3+ doped layered TiInS2 and TiGaSe2 single crystals

    International Nuclear Information System (INIS)

    Faik, Mikailov; Bulat, Rameev; Sinan, Kazan; Bekir, Aktash; Faik, Mikailov; Bulat, Rameev

    2005-01-01

    Full text : TiInS 2 and TiGaSe 2 single crystals doped by paramagnetic Fe ions have been studied at room temperature by Electron Paramagnetic Resonance (EPR) technique. A fine structure of EPR spectra of paramagnetic Fe 3 + ions was observed. The spectra were interpreted to correspond to the transitions among spin multiplet which are splitted by the local ligand crystal field (CF) of orthorhombic symmetry. Four equivalent Fe 3 + centers have been observed in the EPR spectra and the local symmetry of crystal field at the Fe 3 + site and CF parameters were determined. It was established that symmetry axis of the axial component in the CF is making an angle of about 48 and 43 degree with the plane of layers of TiInS 2 and TiGaSe 2 crystals respectively. Experimental results indicate that the Fe ions substitute In (GA) at the center of InS 4 (GaSe 4 ) tetrahedrons, and the rhombic distortion of the CF is caused by the TI ions located in the trigonal cavities between the tethedral complexes

  17. Preparation and characterization of TiO2 and Si-doped octacalcium phosphate composite coatings on zirconia ceramics (Y-TZP) for dental implant applications

    Science.gov (United States)

    Bao, Lei; Liu, Jingxiao; Shi, Fei; Jiang, Yanyan; Liu, Guishan

    2014-01-01

    In order to prevent the low temperature degradation and improve the bioactivity of zirconia ceramic implants, TiO2 and Si-doped octacalcium phosphate composite coating was prepared on zirconia substrate. The preventive effect on low temperature degradation and surface morphology of the TiO2 layer were studied. Meanwhile, the structure and property changes of the bioactive coating after doping Si were discussed. The results indicate that the dense TiO2 layer, in spite of some microcracks, inhibited the direct contact of the water vapor with the sample's surface and thus prevented the low temperature degradation of zirconia substrates. The acceleration aging test shows that the ratio of the monoclinic phase transition decreased from 10% for the original zirconia substrate to 4% for the TiO2-coated substrate. As to the Si-doped octacalcium phosphate coating prepared by biomimetic method, the main phase composition of the coating was octacalcium phosphate. The morphology of the coating was lamellar-like, and the surface was uniform and continuous with no cracks being observed. It is suggested that Si was added into the coating both through substituting for PO43- and doping as NaSiO3.

  18. Carrier compensation mechanism in heavily Nb-doped anatase Ti{sub 1-x}Nb{sub x}O{sub 2+{delta}} epitaxial thin films

    Energy Technology Data Exchange (ETDEWEB)

    Nogawa, H; Chikamatsu, A; Hirose, Y; Hasegawa, T [Department of Chemistry, University of Tokyo, Tokyo 113-0033 (Japan); Nakao, S [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan); Kumigashira, H; Oshima, M, E-mail: chikamatsu@chem.s.u-tokyo.ac.jp [Department of Applied Chemistry, University of Tokyo, Tokyo 113-8656 (Japan)

    2011-09-14

    We investigated the electronic structures of anatase Ti{sub 1-x}Nb{sub x}O{sub 2+{delta}} (TNO) thin films as a function of Nb concentration x using photoemission spectroscopy (PES) measurements to elucidate the origin of the abrupt decrease in carrier activation in heavily Nb-doped regime. The existing intensity ratio of Nb{sup 5+} evaluated from Nb 3d core-level PES spectra maintained a constant value of {approx}0.8 at x = 0.06-0.3, implying that electron carriers generated by Nb doping are compensated by p-type defects. Ti 2p-3d and O1s-2p resonant PES measurements of x = 0.06-0.3 films revealed that the in-gap states positioned {approx}1 eV below the Fermi level (E{sub F}) have a mixed character of Ti 3d and O 2p orbitals, whereas the states at E{sub F} mainly have a Ti 3d nature. We proposed a carrier compensation mechanism that interstitial oxygen atoms strongly combined with surrounding Nb atoms kill conduction electrons in heavily Nb-doped anatase TiO{sub 2}.

  19. Origin of the Enhanced Visible-Light Absorption in N-Doped Bulk Anatase TiO 2 from First-Principles Calculations

    KAUST Repository

    Harb, Moussab; Sautet, P.; Raybaud, P.

    2011-01-01

    unambiguously that the diamagnetic TiO(2-3x)N2x system exhibits the enhanced optical absorption in N-doped TiO2 under visible-light irradiation. Electronic analysis further reveals a band gap narrowing of 0.6 eV induced by delocalized impurity states located

  20. Enhanced Photocatalytic Activity of La3+-Doped TiO2 Nanotubes with Full Wave-Band Absorption

    Science.gov (United States)

    Xia, Minghao; Huang, Lingling; Zhang, Yubo; Wang, Yongqian

    2018-06-01

    TiO2 nanotubes doped with La3+ were synthesized by anodic oxidation method and the photocatalytic activity was detected by photodegrading methylene blue. As-prepared samples improved the absorption of both ultraviolet light and visible light and have a great enhancement on the photocatalytic activity while contrasting with the pristine TiO2 nanotubes. A tentative mechanism for the enhancement of photocatalytic activity with full wave-band absorption is proposed.