Solid thin film materials for use in thin film charge-coupled devices

International Nuclear Information System (INIS)

Lynch, S.J.

1983-01-01

Solid thin films deposited by vacuum deposition were evaluated to ascertain their effectiveness for use in the manufacturing of charge-coupled devices (CCDs). Optical and electrical characteristics of tellurium and Bi 2 Te 3 solid thin films were obtained in order to design and to simulate successfully the operation of thin film (TF) CCDs. In this article some of the material differences between single-crystal material and the island-structured thin film used in TFCCDs are discussed. The electrical parameters were obtained and tabulated, e.g. the mobility, conductivity, dielectric constants, permittivity, lifetime of holes and electrons in the thin films and drift diffusion constants. The optical parameters were also measured and analyzed. After the design was complete, experimental TFCCDs were manufactured and were successfully operated utilizing the aforementioned solid thin films. (Auth.)

Protection of MoO3 high work function by organic thin film

International Nuclear Information System (INIS)

Wang, Chenggong; Irfan, Irfan; Gao, Yongli

2014-01-01

The effects of air exposure are investigated for molybdenum trioxide (MoO 3 ) covered with organic thin films using ultraviolet photoemission spectroscopy. It is found that the severe drop of the work function of MoO 3 by air exposure is substantially reduced by the organic thin films. Both CuPc and C 60 are used for the investigations. The results indicate that the MoO 3 surface can be passivated by approximately two monolayers of organic thin films against exposure to air

Optical properties of titanium trisulphide (TiS3) thin films

International Nuclear Information System (INIS)

Ferrer, I.J.; Ares, J.R.; Clamagirand, J.M.; Barawi, M.; Sánchez, C.

2013-01-01

Titanium trisulphide thin films have been grown on quartz substrates by sulphuration of electron-beam evaporated Ti layers (d ∼ 300 nm) in a vacuum sealed ampoule in the presence of sulphur powder at 550 °C for different periods of time (1 to 20 h). Thin films were characterized by X-ray diffraction, energy dispersive analyses of X-ray and scanning electron microscopy. Results demonstrate that films are composed by monoclinic titanium trisulphide. Films show n-type conductivity with a relatively high resistivity (ρ ∼ 4 ± 2 Ω·cm) and high values of the Seebeck coefficient (− 600 μV/K) at room temperature. Values of the optical absorption coefficient about α ∼ 10 5 cm −1 , determined from reflectance and transmittance measurements, have been obtained at photon energies hυ > 2 eV. The absorption coefficient dependence on the photon energy in the range of 1.6–3.0 eV hints the existence of a direct transition with an energy gap between 1.35 and 1.50 eV. By comparing these results with those obtained from bulk TiS 3 , a direct transition with lower energy is also found which could have been hidden due to the low value of the absorption coefficient in this energy range. - Highlights: ► Thin films of TiS 3 have been obtained by sulphuration of Ti layers. ► Optical properties of TiS 3 thin films have been determined. ► Optical energy gap of TiS 3 has been obtained. ► Optical properties of bulk TiS 3 have been measured and compared with those of films

Structural phototransformation of WO{sub 3} thin films detected by photoacoustic analysis

Energy Technology Data Exchange (ETDEWEB)

Pacheco, Argelia Perez, E-mail: ekargy@hotmail.com [Universidad Nacional Autonoma de Mexico, Laboratorio de Fotofisica y Peliculas Delgadas-CCADET, Ciudad Universitaria, Coyoacan, A.P. 70-186, C.P. 04510, Mexico, D.F. (Mexico); Montes de Oca, C. Oliva; Castaneda-Guzman, R.; Garcia, A. Esparza [Universidad Nacional Autonoma de Mexico, Laboratorio de Fotofisica y Peliculas Delgadas-CCADET, Ciudad Universitaria, Coyoacan, A.P. 70-186, C.P. 04510, Mexico, D.F. (Mexico)

2012-11-15

Highlights: Black-Right-Pointing-Pointer The phototransformation of WO{sub 3} thin films were studied by photoacoustic technique. Black-Right-Pointing-Pointer The phase transition in WO{sub 3} thin films was induced by laser irradiation fluence. Black-Right-Pointing-Pointer The onset and end of the phototransformation in the thin films was identified. Black-Right-Pointing-Pointer The ablation threshold for each sample was identified. - Abstract: The photoacoustic technique (PA) was used to detect the phase transformation from amorphous to crystalline state of tungsten oxide (WO{sub 3}) thin films induced by UV pulsed laser radiation at low energy (<1.5 mJ). The evolution of photoacoustic signal was studied by a correlation analysis, comparing successive signals at fluences ranging from 0 to 20 mJ/cm{sup 2}. In this interval, it was possible to observe structural changes and the ablation threshold in films due to incident laser fluence effect. Thin films of WO{sub 3} were deposited by DC reactive magnetron sputtering over glass substrates at different deposition times. The results obtained by correlation analysis were compared with Raman spectroscopy data.

Preparation and characterization of nanocrystalline porous TiO2/WO3 composite thin films

International Nuclear Information System (INIS)

Hsu, C.-S.; Lin, C.-K.; Chan, C.-C.; Chang, C.-C.; Tsay, C.-Y.

2006-01-01

TiO 2 materials possessing not only photocatalytic but also electrochromic properties have attracted many research and development interests. Though WO 3 exhibits excellent electrochromic properties, the much higher cost and water-sensitivity of WO 3 as compared with the TiO 2 may restrict the practical application of WO 3 materials. In the present study, the feasibility of preparing nanocrystalline porous TiO 2 /WO 3 composite thin films was investigated. Precursors of sols TiO 2 and/or WO 3 and polystyrene microspheres were used to prepare nanocrystalline pure TiO 2 , WO 3 , and composite TiO 2 /WO 3 thin films by spin coating. The spin-coated thin films were amorphous and, after heat treating at a temperature of 500 o C, nanocrystalline TiO 2 , TiO 2 /WO 3 , and WO 3 thin films with or without pores were prepared successfully. The heat-treated thin films were colorless and coloration-bleaching phenomena can be observed during cyclic voltammetry tests. The heat-treated thin films exhibited good reversible electrochromic behavior while the porous TiO 2 /WO 3 composite film exhibited improved electrochromic properties

Metal-insulator transition induced in CaVO{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Gu Man [Department of Physics, University of Virginia, 382 McCormick Rd., Charlottesville, Virginia 22904 (United States); Laverock, Jude; Chen, Bo; Smith, Kevin E. [Department of Physics, Boston University, 590 Commonwealth Avenue, Boston, Massachusetts 02215 (United States); Wolf, Stuart A. [Department of Physics, University of Virginia, 382 McCormick Rd., Charlottesville, Virginia 22904 (United States); Department of Materials Science and Engineering, University of Virginia, 395 McCormick Rd., Charlottesville, Virginia 22904 (United States); Lu Jiwei [Department of Materials Science and Engineering, University of Virginia, 395 McCormick Rd., Charlottesville, Virginia 22904 (United States)

2013-04-07

Stoichiometric CaVO{sub 3} (CVO) thin films of various thicknesses were grown on single crystal SrTiO{sub 3} (STO) (001) substrates using a pulsed electron-beam deposition technique. The CVO films were capped with a 2.5 nm STO layer. We observed a temperature driven metal-insulator transition (MIT) in CVO films with thicknesses below 4 nm that was not observed in either thick CVO films or STO films. The emergence of this MIT can be attributed to the reduction in effective bandwidth due to a crossover from a three-dimensional metal to a two-dimensional insulator. The insulating phase was only induced with a drive current below 0.1 {mu}A. X-ray absorption measurements indicated different electronic structures for thick and very thin films of CVO. Compared with the thick film ({approx}60 nm), thin films of CVO (2-4 nm) were more two-dimensional with the V charge state closer to V{sup 4+}.

SILAR deposited Bi2S3 thin film towards electrochemical supercapacitor

Science.gov (United States)

Raut, Shrikant S.; Dhobale, Jyotsna A.; Sankapal, Babasaheb R.

2017-03-01

Bi2S3 thin film electrode has been synthesized by simple and low cost successive ionic layer adsorption and reaction (SILAR) method on stainless steel (SS) substrate at room temperature. The formation of interconnected nanoparticles with nanoporous surface morphology has been achieved and which is favourable to the supercapacitor applications. Electrochemical supercapacitive performance of Bi2S3 thin film electrode has been performed through cyclic voltammetry, charge-discharge and stability studies in aqueous Na2SO4 electrolyte. The Bi2S3 thin film electrode exhibits the specific capacitance of 289 Fg-1 at 5 mVs-1 scan rate in 1 M Na2SO4 electrolyte.

Study of Sb2S3 thin films deposited by SILAR method

Science.gov (United States)

Deshpande, M. P.; Chauhan, Krishna; Patel, Kiran N.; Rajput, Piyush; Bhoi, Hiteshkumar R.; Chaki, S. H.

2018-05-01

In the present work, we deposited Sb2S3 thin films on glass slide by successive ionic layer adsorption and reaction (SILAR) technique with different time cycles. From EDAX, we could observe that the films were non-stoichiometric and contained few elements from glass slide. X-ray diffraction has shown that these films are orthorhombic in structure from where we have calculated the lattice parameter and crystallize size. SEM images shows that SILAR synthesized Sb2S3 thin films are homogenous and well distributed indicating the formation of uniform thin films at lower concentration. The room temperature Raman spectra of Sb2S3 thin films showed sharp peaks at 250 cm‑1 and 300 cm‑1 for all cases. Room temperature photoluminescence emission spectrum shows broad bands over 430–480 nm range with strong blue emission peak centered at same wavelength of 460 nm (2.70 eV) for all cases.

Improved photoelectrochemical performance of BiVO4/MoO3 heterostructure thin films

Science.gov (United States)

Kodan, Nisha; Mehta, B. R.

2018-05-01

Bismuth vanadate (BiVO4) and Molybdenum trioxide (MoO3) thin films have been prepared by RF sputtering technique. BiVO4 thin films were deposited on indium doped tin oxide (In: SnO2; ITO) substrates at room temperature and 80W applied rf power. The prepared BiVO4 thin films were further annealed at 450°C for 2 hours in air to obtain crystalline monoclinic phase and successively coated with MoO3 thin films deposited at 150W rf power and 400°C for 30 minutes. The effect of coupling BiVO4 and MoO3 on the structural, optical and photoelectrochemical (PEC) properties have been studied. Optical studies reveal that coupling of BiVO4 and MoO3 results in improvement of optical absorption in visible region of solar spectrum. PEC study shows approximate 3-fold and 38-fold increment in photocurrent values of BiVO4/MoO3 (0.38 mA/cm2) heterostructure thin film as compared to MoO3 (0.15 mA/cm2) and BiVO4 (10 µA/cm2) thin films at applied bias of 1 V vs Ag/AgCl in 0.5 M Na2SO4 (pH=7) electrolyte.

Characterization of MAPLE deposited WO3 thin films for electrochromic applications

Science.gov (United States)

Boyadjiev, S. I.; Stefan, N.; Szilágyi, I. M.; Mihailescu, N.; Visan, A.; Mihailescu, I. N.; Stan, G. E.; Besleaga, C.; Iliev, M. T.; Gesheva, K. A.

2017-01-01

Tungsten trioxide (WO3) is a widely studied material for electrochromic applications. The structure, morphology and optical properties of WO3 thin films, grown by matrix assisted pulsed laser evaporation (MAPLE) from monoclinic WO3 nano-sized particles, were investigated for their possible application as electrochromic layers. A KrF* excimer (λ=248 nm, ζFWHM=25 ns) laser source was used in all experiments. The MAPLE deposited WO3 thin films were studied by atomic force microscopy (AFM), grazing incidence X-ray diffraction (GIXRD) and Fourier transform infrared spectroscopy (FTIR). Cyclic voltammetry measurements were also performed, and the coloring and bleaching were observed. The morpho-structural investigations disclosed the synthesis of single-phase monoclinic WO3 films consisting of crystalline nano-grains embedded in an amorphous matrix. All thin films showed good electrochromic properties, thus validating application of the MAPLE deposition technique for the further development of electrochromic devices.

Characterization of MAPLE deposited WO3 thin films for electrochromic applications

International Nuclear Information System (INIS)

Boyadjiev, S I; Iliev, M T; Stefan, N; Mihailescu, N; Visan, A; Mihailescu, I N; Szilágyi, I M; Stan, G E; Besleaga, C; Gesheva, K A

2017-01-01

Tungsten trioxide (WO 3 ) is a widely studied material for electrochromic applications. The structure, morphology and optical properties of WO 3 thin films, grown by matrix assisted pulsed laser evaporation (MAPLE) from monoclinic WO 3 nano-sized particles, were investigated for their possible application as electrochromic layers. A KrF* excimer (λ=248 nm, ζ FWHM =25 ns) laser source was used in all experiments. The MAPLE deposited WO 3 thin films were studied by atomic force microscopy (AFM), grazing incidence X-ray diffraction (GIXRD) and Fourier transform infrared spectroscopy (FTIR). Cyclic voltammetry measurements were also performed, and the coloring and bleaching were observed. The morpho-structural investigations disclosed the synthesis of single-phase monoclinic WO 3 films consisting of crystalline nano-grains embedded in an amorphous matrix. All thin films showed good electrochromic properties, thus validating application of the MAPLE deposition technique for the further development of electrochromic devices. (paper)

Optical constants of CH3NH3PbBr3 perovskite thin films measured by spectroscopic ellipsometry

KAUST Repository

Alias, Mohd Sharizal; Dursun, Ibrahim; Saidaminov, Makhsud I.; Diallo, Elhadj Marwane; Mishra, Pawan; Ng, Tien Khee; Bakr, Osman; Ooi, Boon S.

2016-01-01

function) of CH3NH3PbBr3 perovskite thin films using spectroscopic ellipsometry. Due to the existence of voids, the refractive index of the thin films is around 8% less than the single crystals counterpart. The energy bandgap is around 2.309 eV as obtained

Optical properties of the c-axis oriented LiNbO{sub 3} thin film

Energy Technology Data Exchange (ETDEWEB)

Shandilya, Swati; Sharma, Anjali [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India); Tomar, Monika [Miranda House, University of Delhi, Delhi 110007 (India); Gupta, Vinay, E-mail: drguptavinay@gmail.com [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India)

2012-01-01

C-axis oriented Lithium Niobate (LiNbO{sub 3}) thin films have been deposited onto epitaxially matched (001) sapphire substrate using pulsed laser deposition technique. Structural and optical properties of the thin films have been studied using the X-ray diffraction (XRD) and UV-Visible spectroscopy respectively. Raman spectroscopy has been used to study the optical phonon modes and defects in the c-axis oriented LiNbO{sub 3} thin films. XRD analysis indicates the presence of stress in the as-grown LiNbO{sub 3} thin films and is attributed to the small lattice mismatch between LiNbO{sub 3} and sapphire. Refractive index (n = 2.13 at 640 nm) of the (006) LiNbO{sub 3} thin films was found to be slightly lower from the corresponding bulk value (n = 2.28). Various factors responsible for the deviation in the refractive index of (006) LiNbO{sub 3} thin films from the corresponding bulk value are discussed and the deviation is mainly attributed to the lattice contraction due to the presence of stress in deposited film.

Chemically deposited Sb{sub 2}S{sub 3} thin films for optical recording

Energy Technology Data Exchange (ETDEWEB)

Shaji, S; Arato, A; Castillo, G Alan; Palma, M I Mendivil; Roy, T K Das; Krishnan, B [Facultad de IngenierIa Mecanica y Electrica, Universidad Autonoma de Nuevo Leon, San Nicolas de los Garza, Nuevo Leon, C.P- 66450 (Mexico); O' Brien, J J; Liu, J, E-mail: bkrishnan@fime.uanl.m [Center for Nanoscience and Department of Chemistry and Biochemistry, University of Missouri-St. Louis, One Univ. Blvd., St. Louis, MO - 63121 (United States)

2010-02-24

Laser induced changes in the properties of Sb{sub 2}S{sub 3} thin films prepared by chemical bath deposition are described in this paper. Sb{sub 2}S{sub 3} thin films of thickness 550 nm were deposited from a solution containing SbCl{sub 3} and Na{sub 2}S{sub 2}O{sub 3} at 27 {sup 0}C for 5 h. These thin films were irradiated by a 532 nm continuous wave laser beam under different conditions at ambient atmosphere. X-ray diffraction analysis showed amorphous to polycrystalline transformation due to laser exposure of these thin films. Morphology and composition of these films were described. Optical properties of these films before and after laser irradiation were analysed. The optical band gap of the material was decreased due to laser induced crystallization. The results obtained confirm that there is further scope for developing this material as an optical recording media.

CuInS2 thin films obtained through the annealing of chemically deposited In2S3-CuS thin films

International Nuclear Information System (INIS)

Pena, Y.; Lugo, S.; Calixto-Rodriguez, M.; Vazquez, A.; Gomez, I.; Elizondo, P.

2011-01-01

In this work, we report the formation of CuInS 2 thin films on glass substrates by heating chemically deposited multilayers of copper sulfide (CuS) and indium sulfide (In 2 S 3 ) at 300 and 350 deg. C in nitrogen atmosphere at 10 Torr. CIS thin films were prepared by varying the CuS layer thickness in the multilayers with indium sulfide. The XRD analysis showed that the crystallographic structure of the CuInS 2 (JCPDS 27-0159) is present on the deposited films. From the optical analysis it was estimated the band gap value for the CIS film (1.49 eV). The electrical conductivity varies from 3 x 10 -8 to 3 Ω -1 cm -1 depending on the thickness of the CuS film. CIS films showed p-type conductivity.

Structural and optical properties of cobalt doped multiferroics BiFeO3 nanostructure thin films

Science.gov (United States)

Prasannakumara, R.; Naik, K. Gopalakrishna

2018-05-01

Bismuth ferrite (BiFeO3) and Cobalt doped BiFeO3 (BiFe1-XCoXO3) nanostructure thin films were deposited on glass substrates by the sol-gel spin coating method. The X-ray diffraction patterns (XRD) of the grown BiFeO3 and BiFe1-XCoXO3 nanostructure thin films showed distorted rhombohedral structure. The shifting of peaks to higher angles was observed in cobalt doped BiFeO3. The surface morphology of the BiFeO3 and BiFe1-XCoXO3 nanostructure thin films were studied using FESEM, an increase in grain size was observed as Co concentration increases. The thickness of the nanostructure thin films was examined using FESEM cross-section. The EDX studies confirmed the elemental composition of the grown BiFeO3 and BiFe1-XCoXO3 nanostructure thin films. The optical characterizations of the grown nanostructure thin films were carried out using FTIR, it confirms the existence of Fe-O and Bi-O bands and UV-Visible spectroscopy shows the increase in optical band gap of the BiFeO3 nanostructure thin films with Co doping by ploting Tauc plot.

Improved electrochromical properties of sol-gel WO3 thin films by doping gold nanocrystals

International Nuclear Information System (INIS)

Naseri, N.; Azimirad, R.; Akhavan, O.; Moshfegh, A.Z.

2010-01-01

In this investigation, the effect of gold nanocrystals on the electrochromical properties of sol-gel Au doped WO 3 thin films has been studied. The Au-WO 3 thin films were dip-coated on both glass and indium tin oxide coated conducting glass substrates with various gold concentrations of 0, 3.2 and 6.4 mol%. Optical properties of the samples were studied by UV-visible spectrophotometry in a range of 300-1100 nm. The optical density spectra of the films showed the formation of gold nanoparticles in the films. The optical bandgap energy of Au-WO 3 films decreased with increasing the Au concentration. Crystalline structure of the doped films was investigated by X-ray diffractometry, which indicated formation of gold nanocrystals in amorphous WO 3 thin films. X-ray photoelectron spectroscopy (XPS) was used to study the surface chemical composition of the samples. XPS analysis indicated the presence of gold in metallic state and the formation of stoichiometric WO 3 . The electrochromic properties of the Au-WO 3 samples were also characterized using lithium-based electrolyte. It was found that doping of Au nanocrystals in WO 3 thin films improved the coloration time of the layer. In addition, it was shown that variation of Au concentration led to color change in the colored state of the Au-WO 3 thin films.

Resistivity behavior of optimized PbTiO3 thin films prepared by spin coating method

Science.gov (United States)

Nurbaya, Z.; Wahid, M. H.; Rozana, M. D.; Alrokayan, S. A. H.; Khan, H. A.; Rusop, M.

2018-05-01

Th is study presents the resistivity behavior of PbTiO3 thin films which were prepared towards metal-insulator-metal capacitor device fabrication. The PbTiO3 thin films were prepared through sol-gel spin coating method that involved various deposition parameters that is (1) different molar concentration of PbTiO3 solutions, (2) various additional PbAc-content in PbTiO3 solutions, and (3) various annealing temperature on PbTiO3 thin films. Hence, an electrical measurement of current versus voltage was done to determine the resistivity behavior of PbTiO3 thin films.

Room temperature ferromagnetism in undoped and Ni doped In{sub 2}O{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Krishna, N. Sai; Kaleemulla, S., E-mail: skaleemulla@gmail.com; Rao, N. Madhusudhana; Krishnamoorthi, C.; Begam, M. Rigana [Thin Films Laboratory, School of Advanced Sciences, VIT University, Vellore – 632014 (India); Amarendra, G. [Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam – 603102 (India); UGC-DAE-CSR, Kalpakkam Node, Kokilamedu-603104 (India)

2015-06-24

Undoped and Ni (5 at.%) doped In{sub 2}O{sub 3} thin films were deposited on glass substrate using electron beam evaporation technique and Ni doped In{sub 2}O{sub 3} thin films were annealed at 450 oC. A systematic study was carried out on the structural, chemical and magnetic properties of the as deposited and annealed thin films. X-ray diffraction analysis revealed that all the films were cubic in structure and exhibied ferromagnetism at room temperature. The undoped In{sub 2}O{sub 3} thin films exhibited a saturation magnetization of 24.01 emu/cm3. Ni doped In{sub 2}O{sub 3} thin films annealed at 450 oC showed a saturation magnetization of 53.81 emu/cm3.

AC plasma induced modifications in Sb{sub 2}S{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Calixto-Rodriguez, M; Martinez, H [Instituto de Ciencias Fisicas, Universidad Nacional Autonoma de Mexico, Apartado Postal 48-3, 62210, Cuernavaca, Morelos (Mexico); Castillo, F [Instituto de Ciencias Nucleares, Universidad Nacional Autonoma de Mexico, Apartado Postal 70-543, 04510, Mexico D. F. (Mexico); Pena, Y [Universidad Autonoma de Nuevo Leon, Facultad de Ciencias Quimicas, Pedro de Alba s/n, Cd. Universitaria, San Nicolas de los Garza, N.L (Mexico); Sanchez-Juarez, A, E-mail: ciro@nucleares.unam.m [Centro de Investigacion en EnergIa, Universidad Nacional Autonoma de Mexico, Privada Xochicalco s/n Col. Centro, Temixco, Morelos, C.P. 62580 (Mexico)

2010-01-01

Sb{sub 2}S{sub 3} thin films, deposited by the chemical bath deposition method, were treated with N{sub 2} plasma at 3.0 Torr during several minutes. The as-prepared Sb{sub 2}S{sub 3} thin films and films treated with N{sub 2} plasma have been characterized using several techniques. X-ray diffraction studies have shown that plasma treatment induced recrystallization on the as-prepared Sb{sub 2}S{sub 3}thin films. The band gap values decreased from 2.37 to 1.82 eV after plasma treatment, and the electrical conductivity increased from 10{sup 9} to 10{sup 7} ({Omega}cm){sup -1} due to the annealing effect.

Thin-Film Transformation of NH4 PbI3 to CH3 NH3 PbI3 Perovskite: A Methylamine-Induced Conversion-Healing Process.

Science.gov (United States)

Zong, Yingxia; Zhou, Yuanyuan; Ju, Minggang; Garces, Hector F; Krause, Amanda R; Ji, Fuxiang; Cui, Guanglei; Zeng, Xiao Cheng; Padture, Nitin P; Pang, Shuping

2016-11-14

Methylamine-induced thin-film transformation at room-temperature is discovered, where a porous, rough, polycrystalline NH 4 PbI 3 non-perovskite thin film converts stepwise into a dense, ultrasmooth, textured CH 3 NH 3 PbI 3 perovskite thin film. Owing to the beneficial phase/structural development of the thin film, its photovoltaic properties undergo dramatic enhancement during this NH 4 PbI 3 -to-CH 3 NH 3 PbI 3 transformation process. The chemical origins of this transformation are studied at various length scales. © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Temperature behaviour of optical parameters in (Ag3AsS3)0.3(As2S3)0.7 thin films

Science.gov (United States)

Kutsyk, Mykhailo M.; Ráti, Yosyp Y.; Izai, Vitalii Y.; Makauz, Ivan I.; Studenyak, Ihor P.; Kökényesi, Sandor; Komada, Paweł; Zhailaubayev, Yerkin; Smailov, Nurzhigit

2015-12-01

(Ag3AsS3)0.3(As2S3)0.7 thin films were deposited onto a quartz substrate by rapid thermal evaporation. The optical transmission spectra of thin films were measured in the temperature range 77-300 K. It is shown that the absorption edge spectra are described by the Urbach rule. The temperature behaviour of absorption spectra was studied, the temperature dependences of energy position of absorption edge and Urbach energy were investigated. The influence of transition from three-dimensional glass to the two-dimensional thin film as well as influence of Ag3AsS3 introduction into As2S3 on the optical parameters of (Ag3AsS3)0.3(As2S3)0.7 were analysed. The spectral and temperature behaviour or refractive index for (Ag3AsS3)0.3(As2S3)0.7 thin film were studied.

Microstructural properties of BaTiO3 ceramics and thin films

International Nuclear Information System (INIS)

Fundora C, A.; Portelles, J.J.; Siqueiros, J.M.

2000-01-01

A microstructural study of BaTiO 3 ceramics obtained by the conventional ceramic method is presented. Targets were produced to grow BaTiO 3 thin films by pulsed laser deposition on Pt/Ti/Si (100) substrates. X-ray diffraction, Auger Electron Spectroscopy, X-ray Photon Spectroscopy and Scanning Electron Microscopy were used to study the properties of the BaTiO 3 ceramic samples and thin films, as deposited and after an annealing process. (Author)

Silver loaded WO3−x/TiO2 composite multifunctional thin films

International Nuclear Information System (INIS)

Dunnill, Charles W.; Noimark, Sacha; Parkin, Ivan P.

2012-01-01

Multifunctional WO 3−x –TiO 2 composite thin films have been prepared by sol–gel synthesis and shown to be good visible light photocatalysts whilst retaining a desirable underlying blue colouration. The WO 3−x –TiO 2 composite thin films were further enhanced using silver nanoparticles synthesised in-situ on the surface from the photo-degradation of silver nitrate solution. Thin films were characterised using X-ray diffraction, Raman, Scanning electron microscopy and UV–visible spectroscopy and shown to photo degrade stearic acid, using white light λ = 420–800 nm. - Highlights: ► WO 3−X TiO 2 composite thin films were synthesised by sol–gel methods. ► Blue tinted glass is desirable for the value added glass industry. ► Silver nanoparticle island formation enhances the activity of the films. ► Blue tinted “value added” coated glass is now possible.

Magnetic and electronic properties of SrMnO3 thin films

Science.gov (United States)

Mandal, Arup Kumar; Panchal, Gyanendra; Choudhary, R. J.; Phase, D. M.

2018-05-01

Single phase hexagonal bulk SrMnO3 (SMO) was prepared by solid state route and it was used for depositing thin films by pulsed laser deposition (PLD) technique on single crystalline (100) oriented SrTiO3 (STO) substrate. X-ray diffraction shows that the thin film is deposited in cubic SrMnO3 phase. From X-ray absorption at the Mn L edge we observed the mixed valency of Mn (Mn3+& Mn4+) due to strain induced by the lattice mismatching between SMO and STO. Due to this mixed valency of Mn ion in SMO film, the ferromagnetic nature is observed at lower temperature because of double exchange. After post annealing with very low oxygen partial pressure, magnetic and electronic property of SMO films are effectively modified.

Characterization of Alq3 thin films by a near-field microwave microprobe.

Science.gov (United States)

Hovsepyan, Artur; Lee, Huneung; Sargsyan, Tigran; Melikyan, Harutyun; Yoon, Youngwoon; Babajanyan, Arsen; Friedman, Barry; Lee, Kiejin

2008-09-01

We observed tris-8-hydroxyquinoline aluminum (Alq3) thin films dependence on substrate heating temperatures by using a near-field microwave microprobe (NFMM) and by optical absorption at wavelengths between 200 and 900 nm. The changes of absorption intensity at different substrate heating temperatures are correlated to the changes in the sheet resistance of Alq3 thin films.

Improvement of CH3NH3PbI3 thin film using the additive 1,8-diiodooctane for planar heterojunction perovskite cells

Science.gov (United States)

Abdulrahman, Solh; Wang, Chunhua; Cao, Chenghao; Zhang, Chujun; Yang, Junliang; Jiang, Li

2017-10-01

The thin-film quality is critical for obtaining high-performance perovskite solar cells (PSCs). The additive 1,8-diiodooctane (DIO) was used to control the morphology and structure of CH3NH3PbI3 perovskite thin films, and planar heterojunction (PHJ) PSCs with an architecture of ITO/PEDOT: PSS/CH3NH3PbI3/PCBM/Al was fabricated. It was found that the DIO played an important role on CH3NH3PbI3 thin-film quality and the performance of PHJ-PSCs. With the optimal volume ratio of 2%, the compact and uniform high-quality CH3NH3PbI3 thin films with enhanced crystallinity and less roughness were achieved, resulting in the great improvement of power conversion efficiency (PCE) from about 4.5% to over 9.0%. The research results indicate that the additive DIO is a simple and effective method to produce high-quality perovskite thin film and accordingly develop high-performance PHJ-PSCs.

Cu2SixSn1-xS3 Thin Films Prepared by Reactive Magnetron Sputtering For Low-Cost Thin Film Solar Cells

Science.gov (United States)

Yan, Chang; Liu, Fang-Yang; Lai, Yan-Qing; Li, Jie; Liu, Ye-Xiang

2011-10-01

We report the preparation of Cu2SixSn1-xS3 thin films for thin film solar cell absorbers using the reactive magnetron co-sputtering technique. Energy dispersive spectrometer and x-ray diffraction analyses indicate that Cu2Si1-xSnxS3 thin films can be synthesized successfully by partly substituting Si atoms for Sn atoms in the Cu2SnS3 lattice, leading to a shrinkage of the lattice, and, accordingly, by 2θ shifting to larger values. The blue shift of the Raman peak further confirms the formation of Cu2SixSn1-xS3. Environmental scanning electron microscope analyses reveal a polycrystalline and homogeneous morphology with a grain size of about 200-300 nm. Optical measurements indicate an optical absorption coefficient of higher than 104 cm-1 and an optical bandgap of 1.17±0.01 eV.

Magnetoelectric coupling effect in transition metal modified polycrystalline BiFeO3 thin films

International Nuclear Information System (INIS)

Sreenivas Puli, Venkata; Kumar Pradhan, Dhiren; Gollapudi, Sreenivasulu; Coondoo, Indrani; Panwar, Neeraj; Adireddy, Shiva; Chrisey, Douglas B.; Katiyar, Ram S.

2014-01-01

Rare-earth (Sm) and transition metal (Co) modified polycrystalline BiFeO 3 (BFO) thin films have been deposited on Pt/TiO 2 /SiO 2 /Si substrate successfully through pulsed laser deposition (PLD) technique. Piezoelectric, leakage current and temperature dependent dielectric and magnetic behaviour were investigated for the films. Typical “butterfly-shaped” loop were observed in BSFCO films with an effective piezoelectric constant (d 33 ) ∼94 pm/V at 0.6 MV/cm. High dielectric constant ∼900 and low dielectric loss ∼0.25 were observed at room temperature. M–H loops have shown relatively high saturation magnetization ∼35 emu/cm 3 at a maximum field of H ∼20 kOe. Enhanced magnetoelectric coupling response is observed under applied magnetic field. The multiferroic, piezoelectric, leakage current behaviours were explored. Such studies should be helpful in designing multiferroic materials based on BSFCO films. - Highlights: • Transition metal modified polycrystalline BiFeO 3 thin films prepared using PLD. • High ME-coupling response was observed in co-substituted BiFeO 3 thin films. • High magnetization ∼35 emu/cm 3 at a maximum field of H ∼20 kOe. • Low leakage current might be due to co-substitution in BiFeO 3 thin films. • A notable piezoelectric constant d 33 ∼94 pm/V was found in BiFeO 3 thin films

Dielectric properties of DC reactive magnetron sputtered Al2O3 thin films

International Nuclear Information System (INIS)

Prasanna, S.; Mohan Rao, G.; Jayakumar, S.; Kannan, M.D.; Ganesan, V.

2012-01-01

Alumina (Al 2 O 3 ) thin films were sputter deposited over well-cleaned glass and Si substrates by DC reactive magnetron sputtering under various oxygen gas pressures and sputtering powers. The composition of the films was analyzed by X-ray photoelectron spectroscopy and an optimal O/Al atomic ratio of 1.59 was obtained at a reactive gas pressure of 0.03 Pa and sputtering power of 70 W. X-ray diffraction results revealed that the films were amorphous until 550 °C. The surface morphology of the films was studied using scanning electron microscopy and the as-deposited films were found to be smooth. The topography of the as-deposited and annealed films was analyzed by atomic force microscopy and a progressive increase in the rms roughness of the films from 3.2 nm to 4.53 nm was also observed with increase in the annealing temperature. Al-Al 2 O 3 -Al thin film capacitors were then fabricated on glass substrates to study the effect of temperature and frequency on the dielectric property of the films. Temperature coefficient of capacitance, AC conductivity and activation energy were determined and the results are discussed. - Highlights: ► Al 2 O 3 thin films were deposited by DC reactive magnetron sputtering. ► The films were found to be amorphous up to annealing temperature of 550 C. ► An increase in rms roughness of the films was observed with annealing. ► Al-Al 2 O 3 -Al thin film capacitors were fabricated and dielectric constant was 7.5. ► The activation energy decreased with increase in frequency.

Effect of Annealing Temperature on Flowerlike Cu3BiS3 Thin Films Grown by Chemical Bath Deposition

Science.gov (United States)

Deshmukh, S. G.; Patel, S. J.; Patel, K. K.; Panchal, A. K.; Kheraj, Vipul

2017-10-01

For widespread application of thin-film photovoltaic solar cells, synthesis of inexpensive absorber material is essential. In this work, deposition of ternary Cu3BiS3 absorber material, which contains abundant and environmentally benign elements, was carried out on glass substrate. Flowerlike Cu3BiS3 thin films with nanoflakes as building block were formed on glass substrate by chemical bath deposition. These films were annealed at 573 K and 673 K in sulfur ambient for structural improvement. Their structure was characterized using Raman spectroscopy, as well as their surface morphological and optical properties. The x-ray diffraction profile of as-deposited Cu3BiS3 thin film revealed amorphous structure, which transformed to orthorhombic phase after annealing. The Raman spectrum exhibited a characteristic peak at 290 cm-1. Scanning electron microscopy of as-deposited Cu3BiS3 film confirmed formation of nanoflowers with diameter of around 1052 nm. Wettability testing of as-deposited Cu3BiS3 thin film demonstrated hydrophobic nature, which became hydrophilic after annealing. The measured ultraviolet-visible (UV-Vis) absorption spectra of the Cu3BiS3 thin films gave an absorption coefficient of 105 cm-1 and direct optical bandgap of about 1.42 eV after annealing treatment. Based on all these results, such Cu3BiS3 material may have potential applications in the photovoltaic field as an absorber layer.

Fe3O4 thin films sputter deposited from iron oxide targets

International Nuclear Information System (INIS)

Peng, Yingguo; Park, Chandro; Laughlin, David E.

2003-01-01

Fe 3 O 4 thin films have been directly sputter deposited from a target consisting of a mixture of Fe 3 O 4 and Fe 2 O 3 onto Si and glass substrates. The magnetic properties and microstructures of the films have been characterized and correlated. The columnar growth of the Fe 3 O 4 grains was found to be initialized from the substrate surface without any critical thickness. Substrate bias was found to be a very effective means of improving the crystal quality and magnetic properties of the thin films. The crystallographic defects revealed by high resolution transmission electron microscopy seem to be a characteristic of the films prepared by this method

Thickness control in electrophoretic deposition of WO3 nanofiber thin films for solar water splitting

International Nuclear Information System (INIS)

Fang, Yuanxing; Lee, Wei Cheat; Canciani, Giacomo E.; Draper, Thomas C.; Al-Bawi, Zainab F.; Bedi, Jasbir S.; Perry, Christopher C.; Chen, Qiao

2015-01-01

Graphical abstract: - Highlights: • A novel method combining electrospinning and electrophoretic deposition was established for the creation of nanostructured semiconductor thin films. • The created thin films displayed a high chemical stability with a controllable thickness. • The PEC water splitting performance of the thin films was optimized by fine-tuning the thickness of the films. • A maximum photoconversion efficiency was achieved by 18 μm nanofibrous thin films. - Abstract: Electrophoretic deposition (EPD) of ground electrospun WO 3 nanofibers was applied to create photoanodes with controlled morphology for the application of photoelectrochemical (PEC) water splitting. The correlations between deposition parameters and film thicknesses were investigated with theoretical models to precisely control the morphology of the nanostructured porous thin film. The photoconversion efficiency was further optimized as a function of film thickness. A maximum photoconversion efficiency of 0.924% from electrospun WO 3 nanofibers that EPD deposited on a substrate was achieved at a film thickness of 18 μm.

Dielectric and piezoelectric properties of lead-free (Bi,Na)TiO3-based thin films

Science.gov (United States)

Abazari, M.; Safari, A.; Bharadwaja, S. S. N.; Trolier-McKinstry, S.

2010-02-01

Dielectric and piezoelectric properties of morphotropic phase boundary (Bi,Na)TiO3-(Bi,K)TiO3-BaTiO3 epitaxial thin films deposited on SrRuO3 coated SrTiO3 substrates were reported. Thin films of 350 nm thickness exhibited small signal dielectric permittivity and loss tangent values of 750 and 0.15, respectively, at 1 kHz. Ferroelectric hysteresis measurements indicated a remanent polarization value of 30 μC/cm2 with a coercive field of 85-100 kV/cm. The thin film transverse piezoelectric coefficient (e31,f) of these films after poling at 600 kV/cm was found to be -2.2 C/m2. The results indicate that these BNT-based thin films are a potential candidate for lead-free piezoelectric devices.

Orientation control of chemical solution deposited LaNiO3 thin films

International Nuclear Information System (INIS)

Ueno, Kengo; Yamaguchi, Toshiaki; Sakamoto, Wataru; Yogo, Toshinobu; Kikuta, Koichi; Hirano, Shin-ichi

2005-01-01

High quality LaNiO 3 (LNO) thin films with preferred orientation could be synthesized on Pt/Ti/SiO 2 /Si substrates at 700 deg. C using the chemical solution deposition method. The homogeneous and stable LNO precursor solutions were prepared using lanthanum isopropoxide and nickel (II) acetylacetonate in a mixed solvent of absolute ethanol and 2-methoxyethanol. The oriented LNO thin films exhibit metallic electro-conduction, and their resistivity at room temperature is sufficiently low for making them an alternative electrode material for functional ceramic thin films

Modified chemical synthesis of porous α-Sm{sub 2}S{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Kumbhar, V.S.; Jagadale, A.D. [Thin Film Physics Laboratory, Department of Physics, Shivaji University, Kolhapur, (M.S.) 416004 (India); Gaikwad, N.S. [Rayat Shikshan Sanstha, Satara, (M.S.) 415 001 (India); Lokhande, C.D., E-mail: l_chandrakant@yahoo.com [Thin Film Physics Laboratory, Department of Physics, Shivaji University, Kolhapur, (M.S.) 416004 (India)

2014-08-15

Highlights: • A novel chemical route to prepare α-Sm{sub 2}S{sub 3} thin films. • A porous honeycomb like morphology of the α-Sm{sub 2}S{sub 3} thin film. • An application of α-Sm{sub 2}S{sub 3} thin film toward its supercapacitive behaviour. - Abstract: The paper reports synthesis of porous α-Sm{sub 2}S{sub 3} thin films using modified chemical synthesis, also known as successive ionic layer adsorption and reaction (SILAR) method. The X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), atomic force microscopy (AFM), wettability and ultraviolet–visible spectroscopy (UV–vis) techniques are used for the study of structural, elemental, morphological and optical properties of α-Sm{sub 2}S{sub 3} films. An orthorhombic crystal structure of α-Sm{sub 2}S{sub 3} is resulted from XRD study. The SEM and AFM observations showed highly porous α-Sm{sub 2}S{sub 3} film surface. An optical band gap of 2.50 eV is estimated from optical absorption spectrum. The porous α-Sm{sub 2}S{sub 3} thin film tuned for supercapacitive behaviour using cyclic voltammetry and galvanostatic charge discharge showed a specific capacitance and energy density of 294 Fg{sup –1} and 48.9 kW kg{sup –1}, respectively in 1 M LiClO{sub 4}–propylene carbonate electrolyte.

Oxygen vacancy induced room temperature ferromagnetism in (In1-xNix)2O3 thin films

Science.gov (United States)

Chakraborty, Deepannita; Kaleemulla, S.; Kuppan, M.; Rao, N. Madhusudhana; Krishnamoorthi, C.; Omkaram, I.; Reddy, D. Sreekantha; Rao, G. Venugopal

2018-05-01

Nickel doped indium oxide thin films (In1-xNix)2O3 at x = 0.00, 0.03, 0.05 and 0.07 were deposited onto glass substrates by electron beam evaporation technique. The deposited thin films were subjected to annealing in air at 250 °C, 350 °C and 450 °C for 2 h using high temperature furnace. A set of films were vacuum annealed at 450 °C to study the role of oxygen on magnetic properties of the (In1-xNix)2O3 thin films. The thin films were subjected to different characterization techniques to study their structural, chemical, surface, optical and magnetic properties. All the synthesized air annealed and vacuum annealed films exhibit body centered cubic structure without any secondary phases. No significant change in the diffraction peak position, either to lower or higher diffraction angles has been observed. The band gap of the films decreased from 3.73 eV to 3.63 eV with increase of annealing temperature from 250 °C to 450 °C, in the presence of air. From a slight decrease in strength of magnetization to a complete disappearance of hysteresis loop has been observed in pure In2O3 thin films with increasing the annealing temperature from 250 °C to 450 °C, in the presence of air. The (In1-xNix)2O3 thin films annealed under vacuum follow a trend of enhancement in the strength of magnetization to increase in temperature from 250 °C to 450 °C. The hysteresis loop does not disappear at 450 °C in (In1-xNix)2O3 thin films, as observed in the case of pure In2O3 thin films.

Conductivity of CH{sub 3}NH{sub 3}PbI{sub 3} thin film perovskite stored in ambient atmosphere

Energy Technology Data Exchange (ETDEWEB)

Gebremichael, Bizuneh, E-mail: bizunehme@gmail.com [Physics Department, Addis Ababa University, Addis Ababa, P.O. Box 1176 (Ethiopia); Alemu, Getachew [Physics Department, Addis Ababa University, Addis Ababa, P.O. Box 1176 (Ethiopia); Tessema Mola, Genene [School of Chemistry & Physics, University of KwaZulu-Nat al, Pietermaritzburg Campus, Private Bag X01, Scottsville 3209 (South Africa)

2017-06-01

Time dependent conductivity loss in CH{sub 3}NH{sub 3}PbI{sub 3} thin film perovskite stored in ambient atmosphere were studied based on electrical and optical measurements. Recent investigations on thin film perovskite solar cell suggest that in the steady state operation of the device, the V{sub oc} is unchanged by continuous illumination of light. Rather the reduction in the power conversion efficiency is caused by significant reduction of the short circuit current (J{sub sc}). In this paper, the effect of light on the optical absorption and electrical conductivity of the CH{sub 3}NH{sub 3}PbI{sub 3} thin film which is deposited on a glass substrate is investigated. The temperature dependent conductivity measurements indicated that the dominant conduction mechanism in the film perovskite is electronic rather than ionic.

Strain-Induced Ferromagnetism in Antiferromagnetic LuMnO3 Thin Films

Science.gov (United States)

White, J. S.; Bator, M.; Hu, Y.; Luetkens, H.; Stahn, J.; Capelli, S.; Das, S.; Döbeli, M.; Lippert, Th.; Malik, V. K.; Martynczuk, J.; Wokaun, A.; Kenzelmann, M.; Niedermayer, Ch.; Schneider, C. W.

2013-07-01

Single phase and strained LuMnO3 thin films are discovered to display coexisting ferromagnetic and antiferromagnetic orders. A large moment ferromagnetism (≈1μB), which is absent in bulk samples, is shown to display a magnetic moment distribution that is peaked at the highly strained substrate-film interface. We further show that the strain-induced ferromagnetism and the antiferromagnetic order are coupled via an exchange field, therefore demonstrating strained rare-earth manganite thin films as promising candidate systems for new multifunctional devices.

Multiferroic BiFeO{sub 3} thin films: Structural and magnetic characterization

Energy Technology Data Exchange (ETDEWEB)

Ali, Z. [Physics Department, Faculty of Science (Girls Branch), Al-Azhar University, Cairo (Egypt); Atta, A. [National Center for Radiation Research and Technology (NCRRT), Nasr City, Cairo (Egypt); Abbas, Y. [Physics Department, Faculty of Science, Suez Canal University, Ismailia (Egypt); Sedeek, K.; Adam, A.; Abdeltwab, E. [Physics Department, Faculty of Science (Girls Branch), Al-Azhar University, Cairo (Egypt)

2015-02-27

BiFeO{sub 3} (BFO) film has been deposited on indium tin oxide (ITO) substrate by a simple sol–gel spin-coating technique. The crystal phase composition, surface morphology, topography and magnetization measurements of the BFO thin film were investigated using grazing incidence X-ray diffraction (GIXRD), scanning electronic microscope (SEM), atomic force microscope and vibrating sample magnetometer, respectively. GIXRD analysis revealed that the film was fully crystallized and no impure phase was observed. Cross-section SEM results indicated that compact and homogeneous BFO thin film was deposited on ITO with a thickness of about 180 nm. Moreover, most of A and E-symmetry normal modes of R3c BFO were assigned by Raman spectroscopy. We report here that the pure phase BFO film shows ferromagnetism at room temperature with remarkably high saturation magnetization of 63 kA m{sup −1}. Our results are discussed mainly in correlation with the condition of processing technique and destruction of the spiral spin cycloid at interface layers and grain boundaries. - Highlights: • Multiferroic BiFeO{sub 3} (BFO) thin film was prepared by sol–gel spin-coating method. • BFO film w asdeposited on indium tin oxide substrate with a thickness of 180 nm. • The film exhibits pure rhombohedral perovskite structure. • High saturation magnetization was recorded for our film at room temperature.

Photoconductivity in BiFeO3 thin films

Science.gov (United States)

Basu, S. R.; Martin, L. W.; Chu, Y. H.; Gajek, M.; Ramesh, R.; Rai, R. C.; Xu, X.; Musfeldt, J. L.

2008-03-01

The optical properties of epitaxial BiFeO3 thin films have been characterized in the visible range. Variable temperature spectra show an absorption onset near 2.17eV, a direct gap (2.667±0.005eV at 300K), and charge transfer excitations at higher energy. Additionally, we report photoconductivity in BiFeO3 films under illumination from a 100mW /cm2 white light source. A direct correlation is observed between the magnitude of the photoconductivity and postgrowth cooling pressure. Dark conductivities increased by an order of magnitude when comparing films cooled in 760 and 0.1Torr. Large increases in photoconductivity are observed in light.

Superconducting thin films of YBa2Cu3O7-x

International Nuclear Information System (INIS)

Hudner, J.

1993-01-01

Thin films of the high temperature superconductor YBa 2 Cu 3 O 7-x (YBCO) are of significance in fundamental studies of oxide superconductors and for prospected electronic applications based on superconductors operating at liquid nitrogen temperatures (T= 77 K). Synthesis of YBCO thin films is complex and a large part of this thesis has been devoted to the elaboration of various techniques in forming YBCO thin films. A general observation was that synthesis of YBCO films exhibiting high zero-resistivity temperatures temperatures (T c ) ≥ 88 K and elevated critical current densities (J c ) ≥ 10 6 A/cm 2 at 77 K was possible under widely different conditions of film growth. For the BaF 2 -based method, various substrate materials were investigated. Among perovskite related substrates with low losses in the high frequency regime, LaA10 3 was found to yield YBCO films exhibiting the highest quality electrical properties. A study of YBCO film interaction with sapphire substrates was performed. It was suggested that the YBCO film on sapphire consists of weakly coupled superconducting grains. Compositional effects of Y, BA and Cu for MOCVD-YBCO films were examined with respect to morphology, structure, resistivity, as susceptibility and J c (T). High T c :s and J c :s were observed for an anomalous large compositional range of Cu in off-compositional YBCO films. This was shown to be related to the formation of Cu-rich precipitates embedded within a c-Axis oriented stoichiometric YBCO film matrix. Thermal critical current behavior at zero field in thin films of YBCO fabricated by various methods has been studied by three techniques: transport measurements on patterned microbridges, dc magnetization hysteresis loops using the Bean model and non-linear ac susceptibility analysis. Absolute critical current values obtained form the two former techniques when measured on the same YBCO film were observed to differ about a factor of two. The feasibility of non-linear ac

Photoluminescence in Spray Pyrolysis Deposited β-In2S3 Thin Films

Science.gov (United States)

Jayakrishnan, R.

2018-04-01

Spray pyrolysis deposited In2S3 thin films exhibit two prominent photoluminescent emissions. One of the emissions is green in color and centered at around ˜ 540 nm and the other is centered at around ˜ 690 nm and is red in color. The intensity of the green emission decreases when the films are subjected to annealing in air or vacuum. The intensity of red emission increases when films are air annealed and decreases when vacuum annealed. Vacuum annealing leads to an increase in work function whereas air annealing leads to a decrease in work function for this thin film system relative to the as deposited films indicating changes in space charge regions. Surface photovoltage analysis using a Kelvin probe leads to the conclusion that inversion of band bending occurs as a result of annealing. Correlating surface contact potential measurements using a Kelvin probe, x-ray photoelectron spectroscopy and photoluminescence, we conclude that the surface passivation plays a critical role in controlling the photoluminescence from the spray pyrolysis deposited for In2S3 thin films.

Synthesis and characterization of MoO3–WO3 composite thin films ...

Indian Academy of Sciences (India)

Abstract. In order to achieve high colouration efficiency, MoO3–WO3 composite thin films have been successfully deposited on sodium silicate glass and silicon wafer (111) at 30 ◦C by a very simple novel wet process known as liquid phase deposition. The deposited films were annealed at different temperatures and ...

Chemical solution deposition of CaCu3Ti4O12 thin film

Indian Academy of Sciences (India)

Administrator

CaCu3Ti4O12; thin film; chemical solution deposition; dielectric properties. 1. Introduction. The CaCu3Ti4O12. (CCTO) compound has recently attracted considerable ... and Kelvin probe force microscopy (Chung et al 2004). Intrinsic .... SEM images of CCTO thin films as a function of sintering temperature. silicon based ...

Magnetoelectric effect in Cr2O3 thin films

Science.gov (United States)

He, Xi; Wang, Yi; Sahoo, Sarbeswar; Binek, Christian

2008-03-01

Magnetoelectric materials experienced a recent revival as promising components of novel spintronic devices [1, 2, 3]. Since the magnetoelectric (ME) effect is relativistically small in traditional antiferromagnetic compounds like Cr2O3 (max. αzz 4ps/m ) and also cross- coupling between ferroic order parameters is typically small in the modern multiferroics, it is a challenge to electrically induce sufficient magnetization required for the envisioned device applications. A straightforward approach is to increase the electric field at constant voltage by reducing the thickness of the ME material to thin films of a few nm. Since magnetism is known to be affected by geometrical confinement thickness dependence of the ME effect in thin film Cr2O3 is expected. We grow (111) textured Cr2O3 films with various thicknesses below 500 nm and study the ME effect for various ME annealing conditions as a function of temperature with the help of Kerr-magnetometry. [1] P. Borisov et al. Phys. Rev. Lett. 94, 117203 (2005). [2] Ch. Binek, B.Doudin, J. Phys. Condens. Matter 17, L39 (2005). [3] R. Ramesh and Nicola A. Spaldin 2007 Nature Materials 6 21.

Silver loaded WO{sub 3-x}/TiO{sub 2} composite multifunctional thin films

Energy Technology Data Exchange (ETDEWEB)

Dunnill, Charles W.; Noimark, Sacha; Parkin, Ivan P., E-mail: I.P.Parkin@ucl.ac.uk

2012-06-30

Multifunctional WO{sub 3-x}-TiO{sub 2} composite thin films have been prepared by sol-gel synthesis and shown to be good visible light photocatalysts whilst retaining a desirable underlying blue colouration. The WO{sub 3-x}-TiO{sub 2} composite thin films were further enhanced using silver nanoparticles synthesised in-situ on the surface from the photo-degradation of silver nitrate solution. Thin films were characterised using X-ray diffraction, Raman, Scanning electron microscopy and UV-visible spectroscopy and shown to photo degrade stearic acid, using white light {lambda} = 420-800 nm. - Highlights: Black-Right-Pointing-Pointer WO{sub 3-X} TiO{sub 2} composite thin films were synthesised by sol-gel methods. Black-Right-Pointing-Pointer Blue tinted glass is desirable for the value added glass industry. Black-Right-Pointing-Pointer Silver nanoparticle island formation enhances the activity of the films. Black-Right-Pointing-Pointer Blue tinted 'value added' coated glass is now possible.

Growth and structure of thermally evaporated Bi{sub 2}Te{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Rogacheva, E.I., E-mail: rogacheva@kpi.kharkov.ua [National Technical University “Kharkov Polytechnic Institute”, 21 Frunze St., Kharkov 61002 (Ukraine); Budnik, A.V. [National Technical University “Kharkov Polytechnic Institute”, 21 Frunze St., Kharkov 61002 (Ukraine); Dobrotvorskaya, M.V.; Fedorov, A.G.; Krivonogov, S.I.; Mateychenko, P.V. [Institute for Single Crystals of NAS of Ukraine, 60 Lenin Prospect, Kharkov 61001 (Ukraine); Nashchekina, O.N.; Sipatov, A.Yu. [National Technical University “Kharkov Polytechnic Institute”, 21 Frunze St., Kharkov 61002 (Ukraine)

2016-08-01

The growth mechanism, microstructure, and crystal structure of the polycrystalline n-Bi{sub 2}Te{sub 3} thin films with thicknesses d = 15–350 nm, prepared by thermal evaporation in vacuum onto glass substrates, were studied. Bismuth telluride with Te excess was used as the initial material for the thin film preparation. The thin film characterization was performed using X-ray diffraction, X-ray photoelectron spectroscopy, energy-dispersive X-ray spectroscopy, scan electron microscopy, and electron force microscopy. It was established that the chemical composition of the prepared films corresponded rather well to the starting material composition and the films did not contain any phases apart from Bi{sub 2}Te{sub 3}. It was shown that the grain size and the film roughness increased with increasing film thickness. The preferential growth direction changed from [00l] to [015] under increasing d. The X-ray photoelectron spectroscopy studies showed that the thickness of the oxidized surface layer did not exceed 1.5–2.0 nm and practically did not change in the process of aging at room temperature, which is in agreement with the results reported earlier for single crystals. The obtained data show that using simple and inexpensive method of thermal evaporation in vacuum and appropriate technological parameters, one can grow n-Bi{sub 2}Te{sub 3} thin films of a sufficiently high quality. - Highlights: • The polycrystalline n-Bi{sub 2}Te{sub 3} thin films were grown thermal evaporation onto glass. • The growth mechanism and film structure were studied by different structure methods. • The grain size and film roughness increased with increasing film thickness. • The growth direction changes from [00l] to [015] under film thickness increasing. • The oxidized layer thickness (1–2 nm) did not change under aging at room temperature.

Electrochromism and photocatalysis in dendrite structured Ti:WO3 thin films grown by sputtering

Energy Technology Data Exchange (ETDEWEB)

Karuppasamy, A., E-mail: karuppasamy@psnacet.edu.in

2015-12-30

Graphical abstract: - Highlights: • Dendrite structured Ti doped WO{sub 3} (WTO) thin films are grown by co-sputtering. • Sputtering condition influences structure and surface morphology of WTO films. • Titanium doping and annealing lead to dendritic surface structures in WTO films. • Structural, optical, electrochromic and photocatalytic properties of WTO films. • Enhanced electrochromism and photocatalysis in dendrite structured WTO thin films. - Abstract: Titanium doped tungsten oxide (Ti:WO{sub 3}) thin films with dendrite surface structures were grown by co-sputtering titanium and tungsten in Ar + O{sub 2} atmosphere. Ti:WO{sub 3} thin films were deposited at oxygen flow rates corresponding to pressures in the range 1.0 × 10{sup −3}–5.0 × 10{sup −3} mbar. Argon flow rate and sputtering power densities for titanium (2 W/cm{sup 2}) and tungsten (3 W/cm{sup 2}) were kept constant. Ti:WO{sub 3} films deposited at an oxygen pressure of 5 × 10{sup −3} mbar are found to be better electrochromic and photocatalytic. They have high optical modulation (80% at λ = 550 nm), coloration efficiency (60 cm{sup 2}/C at λ = 550 nm), electron/ion storage and removal capacity (Qc: −22.01 mC/cm{sup 2}, Qa: 17.72 mC/cm{sup 2}), reversibility (80%) and methylene blue decomposition rate (−1.38 μmol/l d). The combined effects of titanium doping, dendrite surface structures and porosity leads to significant enhancement in the electrochromic and photocatalytic properties of Ti:WO{sub 3} films.

Electrochromism and photocatalysis in dendrite structured Ti:WO3 thin films grown by sputtering

International Nuclear Information System (INIS)

Karuppasamy, A.

2015-01-01

Graphical abstract: - Highlights: • Dendrite structured Ti doped WO 3 (WTO) thin films are grown by co-sputtering. • Sputtering condition influences structure and surface morphology of WTO films. • Titanium doping and annealing lead to dendritic surface structures in WTO films. • Structural, optical, electrochromic and photocatalytic properties of WTO films. • Enhanced electrochromism and photocatalysis in dendrite structured WTO thin films. - Abstract: Titanium doped tungsten oxide (Ti:WO 3 ) thin films with dendrite surface structures were grown by co-sputtering titanium and tungsten in Ar + O 2 atmosphere. Ti:WO 3 thin films were deposited at oxygen flow rates corresponding to pressures in the range 1.0 × 10 −3 –5.0 × 10 −3 mbar. Argon flow rate and sputtering power densities for titanium (2 W/cm 2 ) and tungsten (3 W/cm 2 ) were kept constant. Ti:WO 3 films deposited at an oxygen pressure of 5 × 10 −3 mbar are found to be better electrochromic and photocatalytic. They have high optical modulation (80% at λ = 550 nm), coloration efficiency (60 cm 2 /C at λ = 550 nm), electron/ion storage and removal capacity (Qc: −22.01 mC/cm 2 , Qa: 17.72 mC/cm 2 ), reversibility (80%) and methylene blue decomposition rate (−1.38 μmol/l d). The combined effects of titanium doping, dendrite surface structures and porosity leads to significant enhancement in the electrochromic and photocatalytic properties of Ti:WO 3 films.

Mechanism of Crystallization and Implications for Charge Transport in Poly(3-ethylhexylthiophene) Thin Films

KAUST Repository

Duong, Duc T.

2014-04-09

In this work, crystallization kinetics and aggregate growth of poly(3-ethylhexylthiophene) (P3EHT) thin films are studied as a function of film thickness. X-ray diffraction and optical absorption show that individual aggregates and crystallites grow anisotropically and mostly along only two packing directions: the alkyl stacking and the polymer chain backbone direction. Further, it is also determined that crystallization kinetics is limited by the reorganization of polymer chains and depends strongly on the film thickness and average molecular weight. Time-dependent, field-effect hole mobilities in thin films reveal a percolation threshold for both low and high molecular weight P3EHT. Structural analysis reveals that charge percolation requires bridged aggregates separated by a distance of ≈2-3 nm, which is on the order of the polymer persistence length. These results thus highlight the importance of tie molecules and inter-aggregate distance in supporting charge percolation in semiconducting polymer thin films. The study as a whole also demonstrates that P3EHT is an ideal model system for polythiophenes and should prove to be useful for future investigations into crystallization kinetics. Recrystallization kinetics and its relationship to charge transport in poly(3-ethylhexylthiophene) (P3EHT) thin films are investigated using a combination of grazing incidence X-ray diffraction, optical absorption, and field-effect transistor measurements. These results show that thin film crystallization kinetics is limited by polymer chain reorganization and that charge percolation depends strongly on the edge-to-edge distance between aggregates. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

CuInS{sub 2} thin films obtained through the annealing of chemically deposited In{sub 2}S{sub 3}-CuS thin films

Energy Technology Data Exchange (ETDEWEB)

Pena, Y., E-mail: yolapm@gmail.com [Facultad de Ciencias Quimicas, Universidad Autonoma de Nuevo Leon, Pedro de Alba S/N, Ciudad Universitaria, 66451, San Nicolas de los Garza, Nuevo Leon (Mexico); Lugo, S. [Facultad de Ciencias Quimicas, Universidad Autonoma de Nuevo Leon, Pedro de Alba S/N, Ciudad Universitaria, 66451, San Nicolas de los Garza, Nuevo Leon (Mexico); Calixto-Rodriguez, M. [Centro de Investigacion en Energia, Universidad Nacional Autonoma de Mexico, Privada Xochicalco S/N, Col Centro, 62580, Temixco, Morelos (Mexico); Vazquez, A.; Gomez, I.; Elizondo, P. [Facultad de Ciencias Quimicas, Universidad Autonoma de Nuevo Leon, Pedro de Alba S/N, Ciudad Universitaria, 66451, San Nicolas de los Garza, Nuevo Leon (Mexico)

2011-01-01

In this work, we report the formation of CuInS{sub 2} thin films on glass substrates by heating chemically deposited multilayers of copper sulfide (CuS) and indium sulfide (In{sub 2}S{sub 3}) at 300 and 350 deg. C in nitrogen atmosphere at 10 Torr. CIS thin films were prepared by varying the CuS layer thickness in the multilayers with indium sulfide. The XRD analysis showed that the crystallographic structure of the CuInS{sub 2} (JCPDS 27-0159) is present on the deposited films. From the optical analysis it was estimated the band gap value for the CIS film (1.49 eV). The electrical conductivity varies from 3 x 10{sup -8} to 3 {Omega}{sup -1} cm{sup -1} depending on the thickness of the CuS film. CIS films showed p-type conductivity.

Structural and magnetic properties of pure and Cu doped In{sub 2}O{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Krishna, N. Sai; Kaleemulla, S., E-mail: skaleemulla@gmail.com; Rao, N. Madhusudhana; Krishnamoorthi, C.; Begam, M. Rigana [Thin Films Laboratory, School of Advanced Sciences, VIT University, Vellore – 632014 (India); Amarendra, G. [Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam –603102 (India); UGC-DAE-CSR, Kalpakkam Node, Kokilamedu-603104 (India)

2015-06-24

Pure and Cu (7 at.%) doped In{sub 2}O{sub 3} thin films were prepared using an electron beam evaporation technique. A systematic study was carried out on the structural, chemical and magnetic properties of the thin films. X-ray diffraction analysis revealed that all the films were cubic in structure. The pure and Cu doped In{sub 2}O{sub 3} thin films showed ferromagnetism at room temperature. The Cu doped In{sub 2}O{sub 3} thin films showed the saturation magnetization, coercivity and retentivity of 38.71 emu/cm{sup 3}, 245 G and 5.54 emu/cm{sup 3}, respectively.

Magnetoelectric coupling effect in transition metal modified polycrystalline BiFeO{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Sreenivas Puli, Venkata, E-mail: pvsri123@gmail.com [Department of Physics and Engineering Physics, Tulane University, New Orleans, LA 70118 (United States); Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (United States); Kumar Pradhan, Dhiren [Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (United States); Gollapudi, Sreenivasulu [Department of Physics, Oakland University, Rochester, MI 48309-4401 (United States); Coondoo, Indrani [Department of Materials and Ceramic and CICECO, University of Aveiro, 3810-193 Aveiro (Portugal); Panwar, Neeraj [Department of Physics, Central University of Rajasthan, Bandar Sindri, Kishangarh 305801, Rajasthan (India); Adireddy, Shiva; Chrisey, Douglas B. [Department of Physics and Engineering Physics, Tulane University, New Orleans, LA 70118 (United States); Katiyar, Ram S. [Department of Physics and Institute of Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00936 (United States)

2014-11-15

Rare-earth (Sm) and transition metal (Co) modified polycrystalline BiFeO{sub 3} (BFO) thin films have been deposited on Pt/TiO{sub 2}/SiO{sub 2}/Si substrate successfully through pulsed laser deposition (PLD) technique. Piezoelectric, leakage current and temperature dependent dielectric and magnetic behaviour were investigated for the films. Typical “butterfly-shaped” loop were observed in BSFCO films with an effective piezoelectric constant (d{sub 33}) ∼94 pm/V at 0.6 MV/cm. High dielectric constant ∼900 and low dielectric loss ∼0.25 were observed at room temperature. M–H loops have shown relatively high saturation magnetization ∼35 emu/cm{sup 3} at a maximum field of H ∼20 kOe. Enhanced magnetoelectric coupling response is observed under applied magnetic field. The multiferroic, piezoelectric, leakage current behaviours were explored. Such studies should be helpful in designing multiferroic materials based on BSFCO films. - Highlights: • Transition metal modified polycrystalline BiFeO{sub 3} thin films prepared using PLD. • High ME-coupling response was observed in co-substituted BiFeO{sub 3} thin films. • High magnetization ∼35 emu/cm{sup 3} at a maximum field of H ∼20 kOe. • Low leakage current might be due to co-substitution in BiFeO{sub 3} thin films. • A notable piezoelectric constant d{sub 33} ∼94 pm/V was found in BiFeO{sub 3} thin films.

Thickness control in electrophoretic deposition of WO{sub 3} nanofiber thin films for solar water splitting

Energy Technology Data Exchange (ETDEWEB)

Fang, Yuanxing; Lee, Wei Cheat; Canciani, Giacomo E.; Draper, Thomas C.; Al-Bawi, Zainab F. [Department of Chemistry, School of Life Sciences, University of Sussex, Brighton BN1 9QJ (United Kingdom); Bedi, Jasbir S. [School of Public Health & Zoonoses, Guru Angad Dev Veterinary and Animal Sciences University, Ludhiana 141004 Punjab (India); Perry, Christopher C. [Division of Biochemistry, School of Medicine, Loma Linda University, Loma Linda, CA 92350 (United States); Chen, Qiao, E-mail: qiao.chen@sussex.ac.uk [Department of Chemistry, School of Life Sciences, University of Sussex, Brighton BN1 9QJ (United Kingdom)

2015-12-15

Graphical abstract: - Highlights: • A novel method combining electrospinning and electrophoretic deposition was established for the creation of nanostructured semiconductor thin films. • The created thin films displayed a high chemical stability with a controllable thickness. • The PEC water splitting performance of the thin films was optimized by fine-tuning the thickness of the films. • A maximum photoconversion efficiency was achieved by 18 μm nanofibrous thin films. - Abstract: Electrophoretic deposition (EPD) of ground electrospun WO{sub 3} nanofibers was applied to create photoanodes with controlled morphology for the application of photoelectrochemical (PEC) water splitting. The correlations between deposition parameters and film thicknesses were investigated with theoretical models to precisely control the morphology of the nanostructured porous thin film. The photoconversion efficiency was further optimized as a function of film thickness. A maximum photoconversion efficiency of 0.924% from electrospun WO{sub 3} nanofibers that EPD deposited on a substrate was achieved at a film thickness of 18 μm.

Microstructural properties of BaTiO{sub 3} ceramics and thin films

Energy Technology Data Exchange (ETDEWEB)

Fundora C, A.; Portelles, J.J.; Siqueiros, J.M. [Posgrado en Fisica de Materiales, Centro de Investigacion Cientifica y de Educacion Superior de Ensenada. Apartado Postal 2861, 22800 Ensenada, Baja California (Mexico)

2000-07-01

A microstructural study of BaTiO{sub 3} ceramics obtained by the conventional ceramic method is presented. Targets were produced to grow BaTiO{sub 3} thin films by pulsed laser deposition on Pt/Ti/Si (100) substrates. X-ray diffraction, Auger Electron Spectroscopy, X-ray Photon Spectroscopy and Scanning Electron Microscopy were used to study the properties of the BaTiO{sub 3} ceramic samples and thin films, as deposited and after an annealing process. (Author)

Preparation of YBa2Cu3O7-δ epitaxial thin films by pulsed ion-beam evaporation

International Nuclear Information System (INIS)

Sorasit, S.; Yoshida, G.; Suzuki, T.; Suematsu, H.; Jiang, W.; Yatsui, K.

2001-01-01

Thin films of YBa 2 Cu 3 O 7-δ (Y-123) grown epitaxially have been successfully deposited by ion-beam evaporation (IBE). The c-axis oriented YBa 2 Cu 3 O 7-δ thin films were successfully deposited on MgO and SrTiO 3 substrates. The Y-123 thin films which were prepared on the SrTiO 3 substrates were confirmed to be epitaxially grown, by X-ray diffraction analysis. The instantaneous deposition rate of the Y-123 thin films was estimated as high as 4 mm/s. (author)

Magneto-optical properties of BiFeO3 thin films using surface plasmon resonance technique

International Nuclear Information System (INIS)

Paliwal, Ayushi; Sharma, Anjali; Tomar, Monika; Gupta, Vinay

2014-01-01

Indigeneously assembled surface plasmon resonance (SPR) set up has been exploited to study the magnetic field dependent optical properties of BiFeO 3 thin films. BiFeO 3 thin films have been deposited onto gold (Au) coated glass prism by using pulsed laser deposition technique. The surface plasmon modes in prism/Au/BiFeO 3 /air structure have been excited in Kretschmann configuration at the interface of Au/BiFeO 3 thin films. The SPR reflectance curves obtained for prism/Au/BiFeO 3 /air structure were utilized to investigate the optical properties of BiFeO 3 thin films at optical frequency (λ=633 nm) as a function of applied magnetic field. SPR curves shows a continuous shift towards lower angles with increasing applied magnetic field, which indicate the promising application of ferromagnetic BiFeO 3 film as a magnetic field sensor. Complex dielectric constant of deposited BiFeO 3 film was determined by fitting the experimental SPR data with Fresnel's equations. The variation of complex dielectric constant and refractive index of BiFeO 3 film was studied with increase in magnetic field, and the sensitivity of magnetic field sensor was found to be about 0.52 RIU/T

Investigation of the optical property and structure of WO3 thin films with different sputtering depositions

Science.gov (United States)

Chen, Hsi-Chao; Jan, Der-Jun; Chen, Chien-Han; Huang, Kuo-Ting; Lo, Yen-Ming; Chen, Sheng-Hui

2011-09-01

The purpose of this research was to compare the optical properties and structure of tungsten oxide (WO3) thin films that was deposited by different sputtering depositions. WO3 thin films deposited by two different depositions of direct current (DC) magnetron sputtering and pulsed DC sputtering. A 99.95% WO3 target was used as the starting material for these depositions. These WO3 thin films were deposited on the ITO glass, PET and silicon substrate by different ratios of oxygen and argon. A shadow moiré interferometer would be introduced to measure the residual stress for PET substrate. RF magnetron sputtering had the large residual stress than the other's depositions. A Raman spectrum could exhibit the phase of oxidation of WO3 thin film by different depositions. At the ratio of oxygen and argon was about 1:1, and the WO3 thin films had the best oxidation. However, it was important at the change of the transmittance (ΔT = Tbleached - Tcolored) between the coloring and bleaching for the smart window. Therefore, we also found the WO3 thin films had the large variation of transmittance between the coloring and bleaching at the gas ratios of oxygen and argon of 1:1.

Tungsten oxide (WO3) thin films for application in advanced energy systems

International Nuclear Information System (INIS)

Gullapalli, S. K.; Vemuri, R. S.; Manciu, F. S.; Enriquez, J. L.; Ramana, C. V.

2010-01-01

Inherent processes in coal gasification plants produce hazardous hydrogen sulfide (H 2 S), which must be continuously and efficiently detected and removed before the fuel is used for power generation. An attempt has been made in this work to fabricate tungsten oxide (WO 3 ) thin films by radio-frequency reactive magnetron-sputter deposition. The impetus being the use of WO 3 films for H 2 S sensors in coal gasification plants. The effect of growth temperature, which is varied in the range of 30-500 deg. C, on the growth and microstructure of WO 3 thin films is investigated. Characterizations made using scanning electron microscopy (SEM) and x-ray diffraction (XRD) indicate that the effect of temperature is significant on the microstructure of WO 3 films. XRD and SEM results indicate that the WO 3 films grown at room temperature are amorphous, whereas films grown at higher temperatures are nanocrystalline. The average grain-size increases with increasing temperature. WO 3 films exhibit smooth morphology at growth temperatures ≤300 deg. C while relatively rough at >300 deg. C. The analyses indicate that the nanocrystalline WO 3 films grown at 100-300 deg. C could be the potential candidates for H 2 S sensor development for application in coal gasification systems.

Effect of Sb content on the thermoelectric properties of annealed CoSb_3 thin films deposited via RF co-sputtering

International Nuclear Information System (INIS)

Ahmed, Aziz; Han, Seungwoo

2017-01-01

Graphical abstract: The X-ray diffraction patterns and temperature dependence of the Seebeck coefficient of the annealed Co–Sb thin films. - Highlights: • CoSb_3 phase thin films were prepared using RF co sputtering method. • Thin film thermoelectric properties were hugely dependent on Sb content. • All thin films shows n-type conduction behavior at high temperatures. • The thin films with excess Sb possess the largest Seebeck coefficient. • The thin films with CoSb_2 phase possess the largest power factor. - Abstract: A series of CoSb_3 thin films with Sb contents in the range 70–79 at.% were deposited at room temperature via RF co-sputtering. The thin films were amorphous in the as-deposited state and annealed at 300 °C for 3 h to obtain crystalline samples. The annealed thin films were characterized using scanning electron microscopy and X-ray diffraction (XRD), and these data indicate that the films exhibited good crystallinity. The XRD patterns indicate single-phase CoSb_3 thin films in the Sb-rich samples. For the Sb-deficient samples, however, mixed-phase thin films consisting of CoSb_2 and CoSb_3 components were obtained. The electrical and thermoelectric properties were measured at temperatures up to 760 K and found to be highly sensitive to the phases that were present. We observed a change in the thermoelectric properties of the films from p-type at low temperatures to n-type at high temperatures, which indicates potential applications as n-type thermoelectric thin films. A large Seebeck coefficient and power factor was obtained for the single-phase CoSb_3 thin films. The CoSb_2 phase thin films were also found to possess a significant Seebeck coefficient, which coupled with the much smaller electrical resistivity, provided a larger power factor than the single-phase CoSb_3 thin films. We report maximum power factor of 7.92 mW/m K"2 for the CoSb_2-containing mixed phase thin film and 1.26 mW/m K"2 for the stoichiometric CoSb_3 thin film.

Evaluation of space environmental effects on metals and optical thin films on EOIM-3

Energy Technology Data Exchange (ETDEWEB)

Vaughn, J.A.; Linton, R.C.; Finckenor, M.M.; Kamenetzky, R.R.

1995-02-01

Metals and optical thin films exposed to the space environment on the Third Flight of the Evaluation of Oxygen Interactions with Materials (EOIM-3) payload, onboard Space Shuttle mission STS-46 were evaluated. The materials effects described in this paper include the effects of space exposure on various pure metals, optical thin films, and optical thin film metals. The changes induced by exposure to the space environment in the material properties were evaluated using bidirectional reflectance distribution function (BRDF), specular reflectance (250 nm to 2500 nm), ESCA, VUV reflectance (120 nm to 200 nm), ellipsometry, FTIR and optical properties. Using these analysis techniques gold optically thin film metal mirrors with nickel undercoats were observed to darken due to nickel diffusion through the gold to the surface. Also, thin film nickel mirrors formed nickel oxide due to exposure to both the atmosphere and space.

Evaluation of space environmental effects on metals and optical thin films on EOIM-3

Science.gov (United States)

Vaughn, Jason A.; Linton, Roger C.; Finckenor, Miria M.; Kamenetzky, Rachel R.

1995-01-01

Metals and optical thin films exposed to the space environment on the Third Flight of the Evaluation of Oxygen Interactions with Materials (EOIM-3) payload, onboard Space Shuttle mission STS-46 were evaluated. The materials effects described in this paper include the effects of space exposure on various pure metals, optical thin films, and optical thin film metals. The changes induced by exposure to the space environment in the material properties were evaluated using bidirectional reflectance distribution function (BRDF), specular reflectance (250 nm to 2500 nm), ESCA, VUV reflectance (120 nm to 200 nm), ellipsometry, FTIR and optical properties. Using these analysis techniques gold optically thin film metal mirrors with nickel undercoats were observed to darken due to nickel diffusion through the gold to the surface. Also, thin film nickel mirrors formed nickel oxide due to exposure to both the atmosphere and space.

Leakage current behavior in lead-free ferroelectric (K,Na)NbO3-LiTaO3-LiSbO3 thin films

Science.gov (United States)

Abazari, M.; Safari, A.

2010-12-01

Conduction mechanisms in epitaxial (001)-oriented pure and 1 mol % Mn-doped (K0.44,Na0.52,Li0.04)(Nb0.84,Ta0.1,Sb0.06)O3 (KNN-LT-LS) thin films on SrTiO3 substrate were investigated. Temperature dependence of leakage current density was measured as a function of applied electric field in the range of 200-380 K. It was shown that the different transport mechanisms dominate in pure and Mn-doped thin films. In pure (KNN-LT-LS) thin films, Poole-Frenkel emission was found to be responsible for the leakage, while Schottky emission was the dominant mechanism in Mn-doped thin films at higher electric fields. This is a remarkable yet clear indication of effect of 1 mol % Mn on the resistive behavior of such thin films.

Thin Film Microbatteries

International Nuclear Information System (INIS)

Dudney, Nancy J.

2008-01-01

aerosol spray coating, for one or more components of the battery. The active materials used for the thin film cathodes and anodes are familiar intercalation compounds, but the microstructures and often the cycling properties of the thin films may be quite distinct from those of battery electrodes formed from powders. The thin film cathodes are dense and homogeneous with no added phases such as binders or electrolytes. When deposited at ambient temperatures, the films of cathodes, such as LiCoO 2 , V 2 O 5 , LiMn 2 O4 , LiFePO 4 are amorphous or nanocrystalline. But even in this form, they often act as excellent cathodes with large specific capacities and good stability for hundreds to thousands of cycles. Annealing the cathode films at temperatures of 300 to 800 C may be used to induce crystallization and grain growth of the desired intercalation compound. Crystallizing the cathode film generally improves the Li chemical diffusivity in the electrode material, and hence the power delivered by the battery, by 1-2 orders of magnitude. The microstructure is also tailored by the deposition and heat treatment. Figure 3 shows a fracture edge of an annealed LiCoO 2 cathode film on an alumina substrate. The columnar microstructure, which is typical of a vapor deposited film, sinters at high temperatures leaving small fissures between the dense columns. Such crystalline films also may have a preferred crystallographic orientation. For LiCoO 2 films the crystallographic texture differs for films deposited by sputtering versus pulse laser ablation processes. To improve the manufacturability of the thin film batteries, it would be beneficial to eliminate or minimize the temperature or duration of the annealing step. Several efforts have lead to low temperature fabrication of thin film batteries on polyimide substrates, but the battery capacity and rate are lower than those treated at high temperatures. For the battery anode, many designs use a vapor-deposited metallic lithium film as

Neuromorphic transistor achieved by redox reaction of WO3 thin film

Science.gov (United States)

Tsuchiya, Takashi; Jayabalan, Manikandan; Kawamura, Kinya; Takayanagi, Makoto; Higuchi, Tohru; Jayavel, Ramasamy; Terabe, Kazuya

2018-04-01

An all-solid-state neuromorphic transistor composed of a WO3 thin film and a proton-conducting electrolyte was fabricated for application to next-generation information and communication technology including artificial neural networks. The drain current exhibited a 4-order-of-magnitude increment by redox reaction of the WO3 thin film owing to proton migration. Learning and forgetting characteristics were well tuned by the gate control of WO3 redox reactions owing to the separation of the current reading path and pulse application path in the transistor structure. This technique should lead to the development of versatile and low-power-consumption neuromorphic devices.

3D visualization of the internal nanostructure of polyamide thin films in RO membranes

KAUST Repository

Pacheco Oreamuno, Federico

2015-11-02

The front and back surfaces of fully aromatic polyamide thin films isolated from reverse osmosis (RO) membranes were characterized by TEM, SEM and AFM. The front surfaces were relatively rough showing polyamide protuberances of different sizes and shapes; the back surfaces were all consistently smoother with very similar granular textures formed by polyamide nodules of 20–50 nm. Occasional pore openings of approximately the same size as the nodules were observed on the back surfaces. Because traditional microscopic imaging techniques provide limited information about the internal morphology of the thin films, TEM tomography was used to create detailed 3D visualizations that allowed the examination of any section of the thin film volume. These tomograms confirmed the existence of numerous voids within the thin films and revealed structural characteristics that support the water permeance difference between brackish water (BWRO) and seawater (SWRO) RO membranes. Consistent with a higher water permeance, the thin film of the BWRO membrane ESPA3 contained relatively more voids and thinner sections of polyamide than the SWRO membrane SWC3. According to the tomograms, most voids originate near the back surface and many extend all the way to the front surface shaping the polyamide protuberances. Although it is possible for the internal voids to be connected to the outside through the pore openings on the back surface, it was verified that some of these voids comprise nanobubbles that are completely encapsulated by polyamide. TEM tomography is a powerful technique for investigating the internal nanostructure of polyamide thin films. A comprehensive knowledge of the nanostructural distribution of voids and polyamide sections within the thin film may lead to a better understanding of mass transport and rejection mechanisms in RO membranes.

3D visualization of the internal nanostructure of polyamide thin films in RO membranes

KAUST Repository

Pacheco Oreamuno, Federico; Sougrat, Rachid; Reinhard, Martin; Leckie, James O.; Pinnau, Ingo

2015-01-01

The front and back surfaces of fully aromatic polyamide thin films isolated from reverse osmosis (RO) membranes were characterized by TEM, SEM and AFM. The front surfaces were relatively rough showing polyamide protuberances of different sizes and shapes; the back surfaces were all consistently smoother with very similar granular textures formed by polyamide nodules of 20–50 nm. Occasional pore openings of approximately the same size as the nodules were observed on the back surfaces. Because traditional microscopic imaging techniques provide limited information about the internal morphology of the thin films, TEM tomography was used to create detailed 3D visualizations that allowed the examination of any section of the thin film volume. These tomograms confirmed the existence of numerous voids within the thin films and revealed structural characteristics that support the water permeance difference between brackish water (BWRO) and seawater (SWRO) RO membranes. Consistent with a higher water permeance, the thin film of the BWRO membrane ESPA3 contained relatively more voids and thinner sections of polyamide than the SWRO membrane SWC3. According to the tomograms, most voids originate near the back surface and many extend all the way to the front surface shaping the polyamide protuberances. Although it is possible for the internal voids to be connected to the outside through the pore openings on the back surface, it was verified that some of these voids comprise nanobubbles that are completely encapsulated by polyamide. TEM tomography is a powerful technique for investigating the internal nanostructure of polyamide thin films. A comprehensive knowledge of the nanostructural distribution of voids and polyamide sections within the thin film may lead to a better understanding of mass transport and rejection mechanisms in RO membranes.

Room temperature deposition of perpendicular magnetic anisotropic Co{sub 3}Pt thin films on glass substrate

Energy Technology Data Exchange (ETDEWEB)

Chen, Yu-Shen; Dai, Hong-Yu; Hsu, Yi-Wei [Department of Chemical Engineering and Materials Science, Yuan-Ze University, Chung-Li 32003, Taiwan (China); Ou, Sin-Liang, E-mail: slo@mail.dyu.edu.tw [Department of Materials Science and Engineering, Da-Yeh University, Changhua 51591, Taiwan (China); Chen, Shi-Wei [National Synchrotron Radiation Research Center (NSRRC), Hsinchu 300, Taiwan (China); Lu, Hsi-Chuan; Wang, Sea-Fue [Department of Materials and Mineral Resources Engineering, National Taipei University of Technology, Taipei 106, Taiwan (China); Sun, An-Cheng, E-mail: acsun@saturn.yzu.edu.tw [Department of Chemical Engineering and Materials Science, Yuan-Ze University, Chung-Li 32003, Taiwan (China)

2017-03-01

Co{sub 3}Pt alloy thin films were deposited on the glass substrate at room temperature (RT) and 300 °C, which showed high perpendicular magnetic anisotropy (PMA) and isotropy magnetic behaviors, respectively. Co{sub 3}Pt HCP (0002) planes grew along the substrate plane for the films deposited at RT. The easy axis [0001] was consequently vertical to the substrate surface and obtained the predominant PMA. Large magnetic domains and sharp boundary also supported high PMA in RT-deposited samples. On the other hand, the PMA was significantly decreased with increasing the deposition temperature from RT to 300 °C. Hard HCP(0002) and soft A1(111) co-existed in the film and the magnetic exchanged coupling between these two phases induced isotropy magnetic behavior. In addition, the various thicknesses (t) of the RT-deposited Co{sub 3}Pt films were deposited with different base pressures prior to sputtering. The Kerr rotation loops showed high PMA and out-of-plane squareness (S{sub ⊥}) of ~0.9 were found in low base pressure chamber. Within high base pressure chamber, Co{sub 3}Pt films just show magnetic isotropy behaviors. This study provides a fabrication method for the preparation of high PMA HCP-type Co{sub 3}Pt films on the glass substrate without any underlayer at RT. The results could be the base for future development of RT-deposited magnetic alloy thin film with high PMA. - Highlights: • Fabricated high perpendicular magnetic anisotropy Co{sub 3}Pt thin film on glass substrate. • Prepared HCP Co{sub 3}Pt thin film at room temperature. • The key to enhance the PMA of the Co{sub 3}Pt films. • Thinner film is good to fabricate PMA Co{sub 3}Pt thin films.

Investigation of water content in electrolyte solution on electrochromic properties of WO3 thin Films

Directory of Open Access Journals (Sweden)

Zahra Abadi

2017-05-01

Full Text Available Tungsten oxide thin films were prepared by a cathodic electrodeposition method at -0.450 mV in order to investigate how water content affects their electrochromic properties. FESEM images exhibit that WO3 thin films consist of 65 nm uniform grains. Thin Films were electrochemically investigated in 0.1M LiClO4 in propylene carbonate electrolyte with and without 5vol% water content by cyclic voltammetry and chronoamperometry. The results indicate that tungsten oxide thin films exhibit faster switching time between coloration and bleaching states and also higher coloration efficiency in hydrated electrolyte.  

Thin-film photovoltaic technology

Energy Technology Data Exchange (ETDEWEB)

Bhattacharya, R.N. [National Renewable Energy Laboratory, Golden, CO (United States)

2010-07-01

The high material and processing costs associated with single-crystal and polycrystalline silicon wafers that are commonly used in photovoltaic cells render these modules expensive. This presentation described thin-film solar cell technology as a promising alternative to silicon solar cell technology. Cadmium telluride (CdTe) thin films along with copper, indium, gallium, and selenium (CIGS) thin films have become the leaders in this field. Their large optical absorption coefficient can be attributed to a direct energy gap that allows the use of thin layers (1-2 {mu}m) of active material. The efficiency of thin-film solar cell devices based on CIGS is 20 per cent, compared to 16.7 per cent for thin-film solar cell devices based on CdTe. IBM recently reported an efficiency of 9.7 per cent for a new type of inorganic thin-film solar cell based on a Cu{sub 2}ZnSn(S, Se){sub 4} compound. The efficiency of an organic thin-film solar cell is 7.9 per cent. This presentation included a graph of PV device efficiencies and discussed technological advances in non-vacuum deposited, CIGS-based thin-film solar cells. 1 fig.

Dielectric properties of electron irradiated PbZrO 3 thin films

Indian Academy of Sciences (India)

The present paper deals with the study of the effects of electron (8 MeV) irradiation on the dielectric and ferroelectric properties of PbZrO3 thin films grown by sol–gel technique. The films were (0.62 m thick) subjected to electron irradiation using Microtron accelerator (delivered dose 80, 100, 120 kGy). The films were well ...

Photoelectrochemical properties of In{sub 2}Se{sub 3} thin films: Effect of substrate temperature

Energy Technology Data Exchange (ETDEWEB)

Yadav, Abhijit A., E-mail: aay_physics@yahoo.co.in [Thin Film Physics Laboratory, Department of Physics, Electronics and Photonics, Rajarshi Shahu Mahavidyalaya, Latur, M.S. 413512 (India); Salunke, S.D. [Department of Chemistry and Analytical Chemistry, Rajarshi Shahu Mahavidyalaya, Latur, M.S. 413512 (India)

2015-08-15

Highlights: • Photoelectrochemical properties of In{sub 2}Se{sub 3} thin films. • In{sub 2}Se{sub 3} films are of n-type with I{sub sc} and V{sub oc} of 1.05 mA/cm{sup 2} and 261 mV respectively. • Efficiency (η) and fill factor (FF) is found to be 0.71% and 0.51% respectively. • Performance of cell can motivate further studies concerning solar energy conversion. - Abstract: In{sub 2}Se{sub 3} thin films have been deposited onto fluorine doped tin oxide coated (FTO) glass substrates at various substrate temperatures by spray pyrolysis. The photoelectrochemical cell configurations were In{sub 2}Se{sub 3} thin film/1 M (NaOH + Na{sub 2}S + S)/C. From capacitance–voltage (C–V) and current–voltage (I–V) characteristics; it is concluded that In{sub 2}Se{sub 3} thin films are of n-type. The Fill factor (FF) and solar conversion efficiency (η) were calculated from photovoltaic power output characteristics. In this instance, the highest measured photocurrent density of 1.05 mA/cm{sup 2} and open circuit voltage of 261 mV is observed for film deposited at 350 °C resulting in maximum power conversion efficiency (η) and fill factor (FF) to be 0.71% and 0.51% respectively. Electrochemical impedance spectroscopy study shows that the In{sub 2}Se{sub 3} film deposited at 350 °C shows better performance in photoelectrochemical cell. The performance of indium selenide thin film observed in our work can motivate further studies concerning solar energy conversion.

Thin film processes II

CERN Document Server

Kern, Werner

1991-01-01

This sequel to the 1978 classic, Thin Film Processes, gives a clear, practical exposition of important thin film deposition and etching processes that have not yet been adequately reviewed. It discusses selected processes in tutorial overviews with implementation guide lines and an introduction to the literature. Though edited to stand alone, when taken together, Thin Film Processes II and its predecessor present a thorough grounding in modern thin film techniques.Key Features* Provides an all-new sequel to the 1978 classic, Thin Film Processes* Introduces new topics, and sever

Effect of Sb content on the thermoelectric properties of annealed CoSb{sub 3} thin films deposited via RF co-sputtering

Energy Technology Data Exchange (ETDEWEB)

Ahmed, Aziz, E-mail: aziz_ahmed@ust.ac.kr [Department of Nano-Mechatronics, Korea University of Science and Technology (UST), 217 Gajeong-ro, Yuseong-gu, Daejeon, 305-350 (Korea, Republic of); Department of Nano-Mechanics, Korea Institute of Machinery and Materials (KIMM), 156 Gajeongbuk-ro, Yuseong-gu, Daejeon, 305-343 (Korea, Republic of); Han, Seungwoo, E-mail: swhan@kimm.re.kr [Department of Nano-Mechatronics, Korea University of Science and Technology (UST), 217 Gajeong-ro, Yuseong-gu, Daejeon, 305-350 (Korea, Republic of); Department of Nano-Mechanics, Korea Institute of Machinery and Materials (KIMM), 156 Gajeongbuk-ro, Yuseong-gu, Daejeon, 305-343 (Korea, Republic of)

2017-06-30

Graphical abstract: The X-ray diffraction patterns and temperature dependence of the Seebeck coefficient of the annealed Co–Sb thin films. - Highlights: • CoSb{sub 3} phase thin films were prepared using RF co sputtering method. • Thin film thermoelectric properties were hugely dependent on Sb content. • All thin films shows n-type conduction behavior at high temperatures. • The thin films with excess Sb possess the largest Seebeck coefficient. • The thin films with CoSb{sub 2} phase possess the largest power factor. - Abstract: A series of CoSb{sub 3} thin films with Sb contents in the range 70–79 at.% were deposited at room temperature via RF co-sputtering. The thin films were amorphous in the as-deposited state and annealed at 300 °C for 3 h to obtain crystalline samples. The annealed thin films were characterized using scanning electron microscopy and X-ray diffraction (XRD), and these data indicate that the films exhibited good crystallinity. The XRD patterns indicate single-phase CoSb{sub 3} thin films in the Sb-rich samples. For the Sb-deficient samples, however, mixed-phase thin films consisting of CoSb{sub 2} and CoSb{sub 3} components were obtained. The electrical and thermoelectric properties were measured at temperatures up to 760 K and found to be highly sensitive to the phases that were present. We observed a change in the thermoelectric properties of the films from p-type at low temperatures to n-type at high temperatures, which indicates potential applications as n-type thermoelectric thin films. A large Seebeck coefficient and power factor was obtained for the single-phase CoSb{sub 3} thin films. The CoSb{sub 2} phase thin films were also found to possess a significant Seebeck coefficient, which coupled with the much smaller electrical resistivity, provided a larger power factor than the single-phase CoSb{sub 3} thin films. We report maximum power factor of 7.92 mW/m K{sup 2} for the CoSb{sub 2}-containing mixed phase thin film and 1

Pulsed Laser Deposition of BaTiO3 Thin Films on Different Substrates

Directory of Open Access Journals (Sweden)

Yaodong Yang

2010-01-01

Full Text Available We have studied the deposition of BaTiO3 (BTO thin films on various substrates. Three representative substrates were selected from different types of material systems: (i SrTiO3 single crystals as a typical oxide, (ii Si wafers as a semiconductor, and (iii Ni foils as a magnetostrictive metal. We have compared the ferroelectric properties of BTO thin films obtained by pulsed laser deposition on these diverse substrates.

Crystallized InBiS3 thin films with enhanced optoelectronic properties

Science.gov (United States)

Ali, N.; Hussain, Arshad; Ahmed, R.; Omar, M. Firdaus Bin; Sultan, M.; Fu, Yong Qing

2018-04-01

In this paper, a one-step thermal evaporation approach was used for fabrication of indium bismuth sulphide thin films, and the synergetic effects of co-evaporation of two sources (indium granules and Bi2S3 powders) were investigated using different characterization techniques. X-ray diffraction (XRD) analysis confirmed the crystalline orthorhombic structure for the post-annealed samples. Surface roughness and crystal size of the obtained film samples were increased with increasing annealing temperatures. Analysis using X-ray photoelectron spectroscopy showed the formation of the InBiS3 structure for the obtained films, which is also confirmed by the XRD results. The optical absorption coefficient value of the annealed samples was found to be in the order of 105 cm-1 in the visible region of the solar spectrum. The optical band gap energy and electrical resistivity of the fabricated samples were observed to decrease (from 2.2 to 1.3 eV, and from 0.3 to 0.01 Ω-cm, respectively) with increasing annealing temperatures (from 200 to 350 °C), indicating the suitability of the prepared InBiS3 thin films for solar cell applications.

Thin film bismuth iron oxides useful for piezoelectric devices

Science.gov (United States)

Zeches, Robert J.; Martin, Lane W.; Ramesh, Ramamoorthy

2016-05-31

The present invention provides for a composition comprising a thin film of BiFeO.sub.3 having a thickness ranging from 20 nm to 300 nm, a first electrode in contact with the BiFeO.sub.3 thin film, and a second electrode in contact with the BiFeO.sub.3 thin film; wherein the first and second electrodes are in electrical communication. The composition is free or essentially free of lead (Pb). The BFO thin film is has the piezoelectric property of changing its volume and/or shape when an electric field is applied to the BFO thin film.

Preparation of Pb(Zr, Ti)O3 Thin Films by Plasma-Assisted Sputtering

Science.gov (United States)

Hioki, Tsuyoshi; Akiyama, Masahiko; Ueda, Tomomasa; Onozuka, Yutaka; Suzuki, Kouji

1999-09-01

A novel plasma-assisted RF magnetron sputtering system with an immersed coil antenna between a target and a substrate was applied for preparing Pb(Zr, Ti)O3 (PZT) thin films. The antenna enabled the generation of inductively coupled plasma (ICP) independently of the target RF source. The plasma assisted by the antenna resulted in the changes of ion fluxes and these energy distributions irradiating to the substrate. The crystalline phase of the deposited PZT thin films was occupied by the perovskite phase depending on the antenna power. In addition, a high deposition rate, modified uniformity of film thickness, and a dense film structure with large columnar grains were obtained as a result of effects of the assisted plasma. The application of the plasma-assisted sputtering method may enable the preparation of PZT thin films that haveexcellent properties.

Infrared refractive index of thin YBa2Cu3O7 superconducting films

International Nuclear Information System (INIS)

Zhang, Z.M.; Choi, B.I.; Le, T.A.; Flik, M.I.; Siegal, M.P.; Phillips, J.M.

1992-01-01

This work investigates whether thin-film optics with a constant refractive index can be applied to high-T c superconducting thin films. The reflectance and transmittance of YBa 2 Cu 3 O 7 films on LaAlO 3 substrates are measured using a Fourier-transform infrared spectrometer at wavelengths from 1 to 100 μm at room temperature. The reflectance of these superconducting films at 10K in the wavelength region from 2.5 to 25 μm is measured using a cryogenic reflectance accessory. The film thickness varies from 10 to 200 nm. By modeling the frequency-dependent complex conductivity in the normal and superconducting states and applying electromagnetic-wave theory, the complex refractive index of YBa 2 Cu 3 O 7 films is obtained with a fitting technique. It is found that a thickness-independent refractive index can be applied even to a 25nm film, and average values of the spectral refractive index for film thicknesses between 25 and 200 nm are recommended for engineering applications

Growth and giant coercive field of spinel-structured Co3- x Mn x O4 thin films

Science.gov (United States)

Kwak, Yongsu; Song, Jonghyun; Koo, Taeyeong

2016-08-01

We grew epitaxial thin films of CoMn2O4 and Co2MnO4 on Nb-doped SrTiO3(011) and SrTiO3(001) single crystal substrates using pulsed laser deposition. The magnetic Curie temperature ( T c ) of the Co2MnO4 thin films was ~176 K, which is higher than that of the bulk whereas CoMn2O4 thin films exhibited a value of T c (~151 K) lower than that of the bulk. For the Co2MnO4 thin films, the M - H loop showed a coercive field of ~0.7 T at 10 K, similar to the value for the bulk. However, the M -H loop of the CoMn2O4(0 ll) thin film grown on a Nb-doped SrTiO3(011) substrate exhibited a coercive field of ~4.5 T at 30 K, which is significantly higher than those of the Co2MnO4 thin film and bulk. This giant coercive field, only observed for the CoMn2O4(0 ll) thin film, can be attributed to the shape anisotropy and strong spin-orbit coupling.

Diffusivity, solubility and thermodynamic modelling of diffusion growth of Ga"3"+-doped LiTaO_3 thin film for integrated optics

International Nuclear Information System (INIS)

Zhang, De-Long; Zhang, Qun; Zhang, Pei; Kang, Jian; Wong, Wing-Han; Yu, Dao-Yin

2016-01-01

Graphical abstract: Diffusion growth of Ga"3"+-doped LiTaO_3(LT) thin film was studied thermodynamically. Some Ga"3"+-doped LT thin films were grown on LT surface by in-diffusion of homogeneously coated Ga_2O_3 film at the temperature range of (1273 to 1473) K. The Ga"3"+ profile in the grown thin film was analyzed by secondary ion mass spectrometry. Form the measured Ga"3"+ profiles, some thermodynamic parameters were obtained. These include diffusivity, diffusion constant, chemical activation energy, solubility, solubility constant and enthalpy of solution. These parameters are crucial to design and growth of a Ga"3"+-doped LT thin film with desired Ga"3"+ profile for integrated optics application. A thermodynamic model is suggested for the growth and verified experimentally. - Highlights: • Diffusion growth of Ga"3"+-doped LiTaO_3 thin film were studied thermodynamically. • Diffusion constant is 1.41 · 10"−"6 m"2/s and activation energy is 237.2 kJ/mol. • Solubility constant is 22.9 · 10"2"6 ions/m"3 and enthalpy of solution is 28.9 kJ/mol. • Ga"3"+ dopant has small effect on LiTaO_3 refractive index. • Ga"3"+ growth can be described by a Fick-type equation with a constant diffusivity. - Abstract: A thermodynamic study was performed on diffusion growth of Ga"3"+-doped LiTaO_3(LT) thin film for integrated optics. Some Ga"3"+-doped LT thin films were grown on LT surface by in-diffusion of homogeneously coated Ga_2O_3 film at the temperature range of (1273 to 1473) K. After growth, the refractive indices at Ga"3"+-doped and un-doped surface parts were measured by prism coupling technique and Li composition there was evaluated from the measured refractive indices. The results show that Ga"3"+ dopant has small effect on the LT index. Li_2O out-diffusion is not measurable. The Ga"3"+ profile in the grown thin film was analysed by secondary ion mass spectrometry. It is found that the grown Ga"3"+ ions follow a complementary error function profile. A

Structure and magnetic properties of Fe doped In{sub 2}O{sub 3} thin films prepared by electron beam evaporation

Energy Technology Data Exchange (ETDEWEB)

Krishna, N. Sai; Kaleemulla, S., E-mail: skaleemulla@gmail.com; Rao, N. Madhusudhana; Krishnamoorthi, C.; Begam, M. Rigana [Thin Films Laboratory, School of Advanced Sciences, VIT University, Vellore – 632014 (India); Amarendra, G. [Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam – 603102 (India); UGC-DAE-CSR, Kalpakkam Node, Kokilamedu, Tamilnadu -603104 (India)

2015-06-24

Pure and Fe (7 at.%) doped In{sub 2}O{sub 3} thin films were grown onto the glass substrates by electron beam evaporation technique. The structural and magnetic properties of the pure and Fe doped In{sub 2}O{sub 3} thin films have been studied. The undoped and Fe doped In{sub 2}O{sub 3} thin films shown ferromagnetic property at room temperature. A magnetization of 24 emu/cm{sup 3} was observed for pure In{sub 2}O{sub 3} thin films. The magnetization of 38.23 emu/cm{sup 3} was observed for the Fe (7 at.%) doped In{sub 2}O{sub 3} thin films.

Influence of film thickness and Fe doping on LPG sensing properties of Mn3O4 thin film grown by SILAR method

Science.gov (United States)

Belkhedkar, M. R.; Ubale, A. U.

2018-05-01

Nanocrystalline Fe doped and undoped Mn3O4 thin films have been deposited by Successive Ionic Layer Adsorption and Reaction (SILAR) method onto glass substrates using MnCl2 and NaOH as cationic and anionic precursors. The grazing incidence X-ray diffraction (GIXRD) and field emission scanning electron microscopy (FESEM)) have been carried out to analyze structural and surface morphological properties of the films. The LPG sensing performance of Mn3O4thin films have been studied by varying temperature, concentration of LPG, thickness of the film and doping percentage of Fe. The LPG response of the Mn3O4thin films were found to be enhances with film thickness and decreases with increased Fe doping (0 to 8 wt. %) at 573 K temperature.

Preparation and optical properties of gold-dispersed BaTiO3 thin films

Energy Technology Data Exchange (ETDEWEB)

Kineri, T; Mori, M [TDK Corp., Tokyo (Japan). R and D Center; Kadono, K; Sakaguchi, T; Miya, M; Wakabayashi, H [Osaka National Research Inst., Osaka (Japan); Tsuchiya, T [Science Univ. of Tokyo, Tokyo (Japan). Faculty of Industrial Science and Technology

1993-12-01

Recently, metal or semiconductor-doped glasses were widely studied because of their large resonant third-order nonlinearity. These glasses are utilized in an optical information field as all optical logic devices in the future. The gold-doped glass films or thin layers have a large third-order nonlinear susceptibility [chi] and are prepared by r.f. sputtering method, etc. The optical properties, particularly the refractive index or dielectric constant of the matrix, are very important for the optical nonlinearity of these materials. In this study, gold-dispersed BaTiO3 thin films and gold-dispersed SiO2 thin films are prepared using r.f. magnetron sputtering method, and the optical properties of the films are compared. The [chi] of the films are measured and the effect of the matrix of the films on [chi] is investigated. The headings in the paper are: Introduction, Experimental procedure, Results, Discussion, and Conclusion. 13 refs., 9 figs.

Dielectric properties of DC reactive magnetron sputtered Al{sub 2}O{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Prasanna, S. [Thin Film Center, Department of Physics, PSG College of Technology, Coimbatore, 641 004 (India); Mohan Rao, G. [Department of Instrumentation, Indian Institute of Science (IISc), Bangalore, 560 012 (India); Jayakumar, S., E-mail: s_jayakumar_99@yahoo.com [Thin Film Center, Department of Physics, PSG College of Technology, Coimbatore, 641 004 (India); Kannan, M.D. [Thin Film Center, Department of Physics, PSG College of Technology, Coimbatore, 641 004 (India); Ganesan, V. [Low Temperature Lab, UGC-DAE Consortium for Scientific Research (CSR), Indore, 452 017 (India)

2012-01-31

Alumina (Al{sub 2}O{sub 3}) thin films were sputter deposited over well-cleaned glass and Si < 100 > substrates by DC reactive magnetron sputtering under various oxygen gas pressures and sputtering powers. The composition of the films was analyzed by X-ray photoelectron spectroscopy and an optimal O/Al atomic ratio of 1.59 was obtained at a reactive gas pressure of 0.03 Pa and sputtering power of 70 W. X-ray diffraction results revealed that the films were amorphous until 550 Degree-Sign C. The surface morphology of the films was studied using scanning electron microscopy and the as-deposited films were found to be smooth. The topography of the as-deposited and annealed films was analyzed by atomic force microscopy and a progressive increase in the rms roughness of the films from 3.2 nm to 4.53 nm was also observed with increase in the annealing temperature. Al-Al{sub 2}O{sub 3}-Al thin film capacitors were then fabricated on glass substrates to study the effect of temperature and frequency on the dielectric property of the films. Temperature coefficient of capacitance, AC conductivity and activation energy were determined and the results are discussed. - Highlights: Black-Right-Pointing-Pointer Al{sub 2}O{sub 3} thin films were deposited by DC reactive magnetron sputtering. Black-Right-Pointing-Pointer The films were found to be amorphous up to annealing temperature of 550 C. Black-Right-Pointing-Pointer An increase in rms roughness of the films was observed with annealing. Black-Right-Pointing-Pointer Al-Al{sub 2}O{sub 3}-Al thin film capacitors were fabricated and dielectric constant was 7.5. Black-Right-Pointing-Pointer The activation energy decreased with increase in frequency.

LPCVD homoepitaxy of Si doped β-Ga2O3 thin films on (010) and (001) substrates

Science.gov (United States)

Rafique, Subrina; Karim, Md Rezaul; Johnson, Jared M.; Hwang, Jinwoo; Zhao, Hongping

2018-01-01

This paper presents the homoepitaxy of Si-doped β-Ga2O3 thin films on semi-insulating (010) and (001) Ga2O3 substrates via low pressure chemical vapor deposition with a growth rate of ≥1 μm/h. Both high resolution scanning transmission electron microscopy and X-ray diffraction measurements demonstrated high crystalline quality homoepitaxial growth of these thin films. Atomic resolution STEM images of the as-grown β-Ga2O3 thin films on (010) and (001) substrates show high quality material without extended defects or dislocations. The charge carrier transport properties of the as-grown Si-doped β-Ga2O3 thin films were characterized by the temperature dependent Hall measurement using van der Pauw patterns. The room temperature carrier concentrations achieved for the (010) and (001) homoepitaxial thin films were ˜1.2 × 1018 cm-3 and ˜9.5 × 1017 cm-3 with mobilities of ˜72 cm2/V s and ˜42 cm2/V s, respectively.

Growth and structural properties of indium sesquitelluride (In2Te3) thin films

International Nuclear Information System (INIS)

Desai, R.R.; Lakshminarayana, D.; Patel, P.B.; Patel, P.K.; Panchal, C.J.

2005-01-01

Indium sesquitelluride (In 2 Te 3 ) compound was synthesized by mixing and melting the pure individual elements in stoichiometric proportions. The synthesized compound was utilized for the deposition of In 2 Te 3 thin films on glass and freshly cleaved NaCl substrates using flash evaporation technique. The structure of In 2 Te 3 thin films has been studied on the glass substrates by X-ray diffraction technique and on the cleavage faces of NaCl by electron diffraction technique. It was observed that the deposition from an ordered α-phase compound results in polycrystalline films on glass substrate at 473 K which are predominant α-phase and random β-phase compounds resulting in single crystal films on NaCl substrate at 523 K. Effect of source and substrate temperature on the composition of In 2 Te 3 was also studied

Optical and electrical properties of TiOPc doped Alq{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Ramar, M.; Suman, C. K., E-mail: sumanck@nplindia.org; Tyagi, Priyanka; Srivastava, R. [CSIR-Network of Institutes for Solar Energy CSIR - National Physical Laboratory, Dr. K. S. Krishnan Marg, New Delhi -110012 (India)

2015-06-24

The Titanyl phthalocyanine (TiOPc) was doped in Tris (8-hydroxyquinolinato) aluminum (Alq3) with different concentration. The thin film of optimized doping concentration was studied extensively for optical and electrical properties. The optical properties, studied using ellipsometry, absorption and photoluminescence. The absorption peak of Alq{sub 3} and TiOPc was observed at 387 nm and 707 nm and the photo-luminescence intensity (PL) peak of doped thin film was observed at 517 nm. The DC and AC electrical properties of the thin film were studied by current density-voltage (J-V) characteristics and impedance over a frequency range of 100 Hz - 1 MHz. The electron mobility calculated from trap-free space-charge limited region (SCLC) is 0.17×10{sup −5} cm{sup 2}/Vs. The Cole-Cole plots shows that the TiOPc doped Alq{sub 3} thin film can be represented by a single parallel resistance R{sub P} and capacitance C{sub P} network with a series resistance R{sub S} (10 Ω). The value of R{sub P} and C{sub P} at zero bias was 1587 Ω and 2.568 nF respectively. The resistance R{sub P} decreases with applied bias whereas the capacitance C{sub P} remains almost constant.

Structural and Optical Properties of Ultra-high Pure Hot Water Processed Ga2O3 Thin Film

Directory of Open Access Journals (Sweden)

Subramani SHANMUGAN

2016-05-01

Full Text Available Thin film based gas sensor is an advanced application of thin film especially Ga2O3 (GO thin film gas sensor is useful for high temperature gas sensor. The effect of moisture or environment on thin film properties has more influence on gas sensing properties. Radio Frequency sputtered Ga2O3 thin film was synthesized and processed in ultra-high pure hot water at 95 °C for different time durations. The structural properties were verified by the Xray Diffraction technique and the observed spectra revealed the formation of hydroxyl compound of Gallium (Gallium Oxide Dueterate – GOD on the surface of the thin film and evidenced for structural defects as an effect of moisture. Decreased crystallite size and increased dislocation density was showed the crystal defects of prepared film. From the Ultra Violet – Visible spectra, decreased optical transmittance was noticed for various processing time. The formation of needle like GOD was confirmed using Field Emission Secondary Electron Microscope (FESEM images.DOI: http://dx.doi.org/10.5755/j01.ms.22.2.7186

Liquid flow deposited spinel (Ni,Mn){sub 3}O{sub 4} thin films for microbolometer applications

Energy Technology Data Exchange (ETDEWEB)

Le, Duc Thang, E-mail: ducthang36@skku.edu [Intelligent Electronic Component Team, Electronic Materials Convergence Division, Korea Institute of Ceramic Engineering and Technology, Seoul 153-801 (Korea, Republic of); School of Advanced Materials Science & Engineering, Sungkyunkwan University, Suwon 440-746 (Korea, Republic of); Jeon, Chang Jun; Lee, Kui Woong; Jeong, Young Hun; Yun, Ji Sun [Intelligent Electronic Component Team, Electronic Materials Convergence Division, Korea Institute of Ceramic Engineering and Technology, Seoul 153-801 (Korea, Republic of); Yoon, Dae Ho, E-mail: dhyoon@skku.edu [School of Advanced Materials Science & Engineering, Sungkyunkwan University, Suwon 440-746 (Korea, Republic of); Cho, Jeong Ho, E-mail: goedc@kicet.re.kr [Intelligent Electronic Component Team, Electronic Materials Convergence Division, Korea Institute of Ceramic Engineering and Technology, Seoul 153-801 (Korea, Republic of)

2015-03-01

Highlights: • Highly quality (Ni,Mn){sub 3}O{sub 4} thin films were grown using liquid flow deposited (LFD) technique. • It is possible to deposit multi–component manganite–oxide thin films by LFD at low temperatures. • Nickel–manganite films showed a good negative temperature coefficient (NTC) characteristic. • Liquid flow deposited (Ni,Mn){sub 3}O{sub 4} thin films are very potential for microbolometer applications. - Abstract: A liquid flow deposition (LFD) technique was initially used for the fabrication of single-component Mn{sub 3}O{sub 4} thin films onto Si wafer substrates at a range of substrate temperatures of 30–80 °C, with the introduction of an oxidizing reagent (H{sub 2}O{sub 2}). As a result, solid thin films were well formed from an aqueous solution. An X-ray diffraction (XRD) analysis showed typical characteristics of hausmannite Mn{sub 3}O{sub 4} with a spinel tetragonal phase. Field-emission scanning electron microscopy (FE-SEM) observations revealed nano-sized grains arranged uniformly on a dense and smooth surface for all of the as-deposited films. On the other hand, the LFD method was then extended to prepare two-component nickel–manganite films according to the binary chemical composition of Ni{sub x}Mn{sub 3−x}O{sub 4} with x = 0.02–0.2. The as-grown nickel–manganite films showed a surface with a good quality with a spherical bead-like architecture when x ≤ 0.10, while a conversion from spherical grains into highly porous nanowalls in the microstructure was noted in films when x ≥ 0.12. These results signify that it is possible to fabricate various multi-component manganite-oxide thin films at a low temperature. In addition, the dependences of the room-temperature electrical resistivity (ρ) and the temperature coefficient of resistance (TCR) on the Ni substitution level (x) were investigated on films annealed at 400 °C.

Magneto-optical properties of BiFeO{sub 3} thin films using surface plasmon resonance technique

Energy Technology Data Exchange (ETDEWEB)

Paliwal, Ayushi; Sharma, Anjali [Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India); Tomar, Monika [Physics Department, Miranda House, University of Delhi, Delhi 110007 (India); Gupta, Vinay, E-mail: drguptavinay@gmail.com [Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India)

2014-09-01

Indigeneously assembled surface plasmon resonance (SPR) set up has been exploited to study the magnetic field dependent optical properties of BiFeO{sub 3} thin films. BiFeO{sub 3} thin films have been deposited onto gold (Au) coated glass prism by using pulsed laser deposition technique. The surface plasmon modes in prism/Au/BiFeO{sub 3}/air structure have been excited in Kretschmann configuration at the interface of Au/BiFeO{sub 3} thin films. The SPR reflectance curves obtained for prism/Au/BiFeO{sub 3}/air structure were utilized to investigate the optical properties of BiFeO{sub 3} thin films at optical frequency (λ=633 nm) as a function of applied magnetic field. SPR curves shows a continuous shift towards lower angles with increasing applied magnetic field, which indicate the promising application of ferromagnetic BiFeO{sub 3} film as a magnetic field sensor. Complex dielectric constant of deposited BiFeO{sub 3} film was determined by fitting the experimental SPR data with Fresnel's equations. The variation of complex dielectric constant and refractive index of BiFeO{sub 3} film was studied with increase in magnetic field, and the sensitivity of magnetic field sensor was found to be about 0.52 RIU/T.

Pyrolyzed thin film carbon

Science.gov (United States)

Tai, Yu-Chong (Inventor); Liger, Matthieu (Inventor); Harder, Theodore (Inventor); Konishi, Satoshi (Inventor); Miserendino, Scott (Inventor)

2010-01-01

A method of making carbon thin films comprises depositing a catalyst on a substrate, depositing a hydrocarbon in contact with the catalyst and pyrolyzing the hydrocarbon. A method of controlling a carbon thin film density comprises etching a cavity into a substrate, depositing a hydrocarbon into the cavity, and pyrolyzing the hydrocarbon while in the cavity to form a carbon thin film. Controlling a carbon thin film density is achieved by changing the volume of the cavity. Methods of making carbon containing patterned structures are also provided. Carbon thin films and carbon containing patterned structures can be used in NEMS, MEMS, liquid chromatography, and sensor devices.

Optimization of excess Bi doping to enhance ferroic orders of spin casted BiFeO3 thin film

International Nuclear Information System (INIS)

Gupta, Surbhi; Gupta, Vinay; Tomar, Monika; James, A. R.; Pal, Madhuparna; Guo, Ruyan; Bhalla, Amar

2014-01-01

Multiferroic Bismuth Ferrite (BiFeO 3 ) thin films with varying excess bismuth (Bi) concentration were grown by chemical solution deposition technique. Room temperature multiferroic properties (ferromagnetism, ferroelectricity, and piezoelectricity) of the deposited BiFeO 3 thin films have been studied. High resolution X-ray diffraction and Raman spectroscopy studies reveal that the dominant phases formed in the prepared samples change continuously from a mixture of BiFeO 3 and Fe 2 O 3 to pure BiFeO 3 phase and, subsequently, to a mixture of BiFeO 3 and Bi 2 O 3 with increase in the concentration of excess Bi from 0% to 15%. BiFeO 3 thin films having low content (0% and 2%) of excess Bi showed the traces of ferromagnetic phase (γ-Fe 2 O 3 ). Deterioration in ferroic properties of BiFeO 3 thin films is also observed when prepared with higher content (15%) of excess Bi. Single-phased BiFeO 3 thin film prepared with 5% excess Bi concentration exhibited the soft ferromagnetic hysteresis loops and ferroelectric characteristics with remnant polarization 4.2 μC/cm 2 and saturation magnetization 11.66 emu/g. The switching of fine spontaneous domains with applied dc bias has been observed using piezoresponse force microscopy in BiFeO 3 thin films having 5% excess Bi. The results are important to identify optimum excess Bi concentration needed for the formation of single phase BiFeO 3 thin films exhibiting the improved multiferroic properties.

Photovoltaic effect in transition metal modified polycrystalline BiFeO3 thin films

International Nuclear Information System (INIS)

Puli, Venkata Sreenivas; Chrisey, Douglas B; Pradhan, Dhiren Kumar; Katiyar, Rajesh Kumar; Misra, Pankaj; Scott, J F; Katiyar, Ram S; Coondoo, Indrani; Panwar, Neeraj

2014-01-01

We report photovoltaic (PV) effect in multiferroic Bi 0.9 Sm 0.1 Fe 0.95 Co 0.05 O 3 (BSFCO) thin films. Transition metal modified polycrystalline BiFeO 3 (BFO) thin films have been deposited on Pt/TiO 2 /SiO 2 /Si substrate successfully through pulsed laser deposition (PLD). PV response is observed under illumination both in sandwich and lateral electrode configurations. The open-circuit voltage (V oc ) and the short-circuit current density (J sc ) of the films in sandwich electrode configuration under illumination are measured to be 0.9 V and −0.051 µA cm −2 . Additionally, we report piezoresponse for BSFCO films, which confirms ferroelectric piezoelectric behaviour. (paper)

Structure and optical properties of thin As{sub 2}S{sub 3}-In{sub 2}S{sub 3} films

Energy Technology Data Exchange (ETDEWEB)

Todorov, R; Pirov, J; Petkov, K [Institute of Optical Materials and Technologies ' Acad. J. Malinowski' , Bulgarian Academy of Sciences, Acad. G. Bonchev Str., bl.109, 1113 Sofia (Bulgaria); Tsankov, D, E-mail: rossen@clf.bas.bg [Institute of Organic Chemistry with Centre of Phytochemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev St. bl.9, 1113 Sofia (Bulgaria)

2011-08-03

This paper deals with the optical properties of thin As{sub 2}S{sub 3}-In{sub 2}S{sub 3} films. The thin layers were deposited by thermal co-evaporation of As{sub 2}S{sub 3} and In{sub 2}S{sub 3}. The composition of the coatings was controlled by x-ray microanalysis; it was found to be close to the expected one. The refractive index n and optical band gap E{sub g}{sup opt} were calculated from the transmittance and reflectance spectra. The results showed that the refractive index of thin As-S films is not affected by the addition of 1 at% indium and it increases from 2.46 to 2.58 for thin film with 13 at% In. A decrease in the changes in the refractive index, {Delta}n, after exposure to light or annealing with addition of indium in arsenic sulfide is observed. To explain the influence of the indium on the photoinduced changes in the optical properties of thin As-S-In films, the glass structure was investigated by infrared spectroscopy. The calculated values of the optical constants were compared with those obtained from ellipsometric measurements.

Electrochemical synthesis of photoactive In/sub 2/Se/sub 3/ thin films

Energy Technology Data Exchange (ETDEWEB)

Herrero, J; Ortega, J

1987-12-01

In/sub 2/Se/sub 3/ thin films were grown by alternate electrodeposition of selenium and indium from separate baths onto titanium substrates with subsequent thermal annealing. The influence of annealing temperature on the properties of the obtained films was examined. The results of X-ray diffraction patterns led to the conclusion that films were ..beta..-phase when the temperature ranged between 300 and 500/sup 0/C. At 600/sup 0/C the thin film loses Se and the ratio Se/In decreases. Only photoanodic response, n-type thin films, was observed when the samples were tested in a photoelectrochemical cell with a sulfite/sulfate redox couple. Values of the photocurrent on the spectra response were increased when the annealing temperature was also increased, showing the best photocurrent values at 500/sup 0/C, and the films that were annealed at 600/sup 0/C showed no photoactivity. Spectral responses after chemical etching of the samples showed a significant increase of the photocurrent. Application of Gaertner-Butler's model to the interface semiconductor-electrolyte makes it possible to obtain the semiconductor energy gap, on samples heated at 500/sup 0/C, corresponding to a direct allowed band transition.

Dependence on film thickness of grain boundary low-field magnetoresistance in thin films of La0.7Ca0.3MnO3

International Nuclear Information System (INIS)

Todd, N. K.; Mathur, N. D.; Blamire, M. G.

2001-01-01

The magnetoresistance of grain boundaries in the perovskite manganites is being studied, both in polycrystalline materials, and thin films grown on bicrystal substrates, because of interest in low-field applications. In this article we show that epitaxial films grown on SrTiO 3 bicrystal substrates of 45 degree misorientation show magnetoresistance behavior which is strongly dependent on the thickness of the film. Thin films, e.g., 40 nm, can show a large low-field magnetoresistance at low temperatures, with very sharp switching between distinct high and low resistance states for fields applied in plane and parallel to the boundary. Thicker films show a more complex behavior of resistance as a function of field, and the dependence on the angle between the applied field and the grain boundary is altered. These changes in magnetoresistance behavior are linked to the variation in morphology of the films. Thin films are coherently strained, due to the mismatch with the substrate, and very smooth. Thicker films relax, with the formation of defects, and hence different micromagnetic behavior. [copyright] 2001 American Institute of Physics

thin films

Indian Academy of Sciences (India)

microscopy (SEM) studies, respectively. The Fourier transform ... Thin films; chemical synthesis; hydrous tin oxide; FTIR; electrical properties. 1. Introduction ... dehydrogenation of organic compounds (Hattori et al 1987). .... SEM images of (a) bare stainless steel and (b) SnO2:H2O thin film on stainless steel substrate at a ...

CVD growth and characterization of 3C-SiC thin films

Indian Academy of Sciences (India)

Unknown

Cubic silicon carbide (3C-SiC) thin films were grown on (100) and (111) Si substrates by CVD technique using ... of grown films were studied using optical microscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD) analysis and X-ray ... the oxide mask gets damaged (Edgar et al 1998). There- fore, lower ...

Investigation of growth, structural and electronic properties of V2O3 thin films on selected substrates

International Nuclear Information System (INIS)

Nateprov, Alexei

2006-08-01

The present work is devoted to the experimental study of the MI transition in V 2 O 3 thin films, grown on different substrates. The main goal of the work was to develop a technology of growth of V 2 O 3 thin films on substrates with different electrical and structural properties (diamond and LiNbO 3 ), designed for specific applications. The structural and electrical properties of the obtained films were characterized in detail with a special focus on their potential applications. The MIT of V 2 O 3 was investigated by SAW using first directly deposited V 2 O 3 thin film onto a LiNbO 3 substrate. (orig.)

Spray pyrolyzed Cu2SnS3 thin films for photovoltaic application

Science.gov (United States)

Patel, Biren; Waldiya, Manmohansingh; Pati, Ranjan K.; Mukhopadhyay, Indrajit; Ray, Abhijit

2018-05-01

We report the fabrication of Cu2SnS3 (CTS) thin films by a non-vacuum and low cost spray pyrolysis technique. Annealing of the as-deposited film in the sulphur atmosphere produces highly stoichiometric, granular and crystalline CTS phase. The CTS thin films shows direct optical band gap of 1.58 eV with high absorption coefficient of 105 cm-1. Hall measurement shows the carrier concentration of the order of 1021 cm-3 and a favourable resistivity of 10-3 Ω cm. A solar cell architecture of Glass/FTO/CTS/CdS/Al:ZnO/Al was fabricated and its current-voltage characteristic shows an open circuit voltage, short circuit current density and fill-factor of 12.6 mV, 20.2 µA/cm2 and 26% respectively. A further improvement in the solar cell parameters is underway.

Solid phase epitaxial growth of high mobility La:BaSnO_3 thin films co-doped with interstitial hydrogen

International Nuclear Information System (INIS)

Niedermeier, Christian A.; Rhode, Sneha; Fearn, Sarah; Moram, Michelle A.; Ide, Keisuke; Hiramatsu, Hidenori; Hosono, Hideo; Kamiya, Toshio

2016-01-01

This work presents the solid phase epitaxial growth of high mobility La:BaSnO_3 thin films on SrTiO_3 single crystal substrates by crystallization through thermal annealing of nanocrystalline thin films prepared by pulsed laser deposition at room temperature. The La:BaSnO_3 thin films show high epitaxial quality and Hall mobilities up to 26 ± 1 cm"2/Vs. Secondary ion mass spectroscopy is used to determine the La concentration profile in the La:BaSnO_3 thin films, and a 9%–16% La doping activation efficiency is obtained. An investigation of H doping to BaSnO_3 thin films is presented employing H plasma treatment at room temperature. Carrier concentrations in previously insulating BaSnO_3 thin films were increased to 3 × 10"1"9" cm"−"3 and in La:BaSnO_3 thin films from 6 × 10"1"9" cm"−"3 to 1.5 × 10"2"0" cm"−"3, supporting a theoretical prediction that interstitial H serves as an excellent n-type dopant. An analysis of the free electron absorption by infrared spectroscopy yields a small (H,La):BaSnO_3 electron effective mass of 0.27 ± 0.05 m_0 and an optical mobility of 26 ± 7 cm"2/Vs. As compared to La:BaSnO_3 single crystals, the smaller electron mobility in epitaxial thin films grown on SrTiO_3 substrates is ascribed to threading dislocations as observed in high resolution transmission electron micrographs.

Investigation of CaTiO3:Pr3+ thin films deposited by radiofrequency reactive magnetron sputtering for electroluminescence application

International Nuclear Information System (INIS)

Sarakha, L; Bousquet, A; Tomasella, E; Boutinaud, P; Mahiou, R

2010-01-01

In this report we successfully deposited thin films of CaTiO 3 :Pr 3+ by radiofrequency magnetron sputtering. The films were studied and we tried to understand the evolution of their optical and electrical properties. We noticed that the annealing temperature and the deposition pressures have an important influence on these properties. Thin films with good optical and electrical properties have been obtained. These films are transparent and are characterized by an intense red photoluminescence and a low fixed charge density. They are well dedicated for electroluminescence purposes.

Photoinduced hydrophobic surface of graphene oxide thin films

International Nuclear Information System (INIS)

Zhang Xiaoyan; Song Peng; Cui Xiaoli

2012-01-01

Graphene oxide (GO) thin films were deposited on transparent conducting oxide substrates and glass slides by spin coating method at room temperature. The wettability of GO thin films before and after ultraviolet (UV) irradiation was characterized with water contact angles, which increased from 27.3° to 57.6° after 3 h of irradiation, indicating a photo-induced hydrophobic surface. The UV–vis absorption spectra, Raman spectroscopy, X-ray photoelectron spectroscopy, and conductivity measurements of GO films before and after UV irradiation were taken to study the mechanism of photoinduced hydrophobic surface of GO thin films. It is demonstrated that the photoinduced hydrophobic surface is ascribed to the elimination of oxygen-containing functional groups on GO molecules. This work provides a simple strategy to control the wettability properties of GO thin films by UV irradiation. - Highlights: ► Photoinduced hydrophobic surface of graphene oxide thin films has been demonstrated. ► Elimination of oxygen-containing functional groups in graphene oxide achieved by UV irradiation. ► We provide novel strategy to control surface wettability of GO thin films by UV irradiation.

Epitaxial Pb(Mg1/3Nb2/3)O3 thin films synthesized by metal-organic chemical vapor deposition

International Nuclear Information System (INIS)

Bai, G. R.; Streiffer, S. K.; Baumann, P. K.; Auciello, O.; Ghosh, K.; Stemmer, S.; Munkholm, A.; Thompson, Carol; Rao, R. A.; Eom, C. B.

2000-01-01

Metal-organic chemical vapor deposition was used to prepare Pb(Mg 1/3 Nb 2/3 )O 3 (PMN) thin films on (001) SrTiO 3 and SrRuO 3 /SrTiO 3 substrates, using solid Mg β-diketonate as the Mg precursor. Parameters including the precursor ratio in the vapor phase, growth temperature, growth rate, and reaction pressure in the reactor chamber were varied in order to determine suitable growth conditions for producing phase-pure, epitaxial PMN films. A cube-on-cube orientation relationship between the thin film and the SrTiO 3 substrate was found, with a (001) rocking curve width of 0.1 degree sign , and in-plane rocking-curve width of 0.8 degree sign . The root-mean-square surface roughness of a 200-nm-thick film on SrTiO 3 was 2 to 3 nm as measured by scanning probe microscopy. The zero-bias dielectric constant and loss measured at room temperature and 10 kHz for a 200-nm-thick film on SrRuO 3 /SrTiO 3 were approximately 1100 and 2%, respectively. The remnant polarization for this film was 16 μC/cm 2 . (c) 2000 American Institute of Physics

Structural and optical properties of annealed and illuminated (Ag3AsS3)0.6(As2S3)0.4 thin films

Science.gov (United States)

Studenyak, I. P.; Neimet, Yu. Yu.; Rati, Y. Y.; Stanko, D.; Kranjčec, M.; Kökényesi, S.; Daróci, L.; Bohdan, R.

2014-11-01

(Ag3AsS3)0.6(As2S3)0.4 thin films were deposited upon a quartz substrate by rapid thermal evaporation. Structural studies of the as-deposited, annealed and illuminated films were performed using XRD, scanning electron and atomic force microscopies. Surfaces of all the films were found to be covered with Ag-rich crystalline micrometer sized cones. Thermal annealing leads to mechanical deformation of part of the cones and their detachment from the base film surface while the laser illumination leads to the new formations appearance on the surface of thin films. The spectroscopic studies of optical transmission spectra for as-deposited, annealed and illuminated thin films were carried out. The optical absorption spectra in the region of its exponential behaviour were analysed, the dispersion dependences of refractive index as well as their variation after annealing and illumination were investigated.

Photovoltaics: tests of thin-film technologies. 6 thin-film technologies in 3 different BIPV modes compared in a real outdoor performance test; PV-ThinFilmTest. 6 thin-film technologies in 3 different BIPV modes compared in a real outdoor performance test

Energy Technology Data Exchange (ETDEWEB)

Frei, R.; Meier, Ch.

2005-07-01

This final report for the Swiss Federal Office of Energy (SFOE) presents the results of a comparison made between six types of thin-film, building-integrated photovoltaic (BIPV) technologies used in three different modes of building-integration. More than 450 thin-film modules including amorphous silicon and CIS technologies were monitored. Each type of module was installed in three different modes: inclined (20{sup o}), flat with free back air flow, and flat with thermal back insulation. The performance of these commercially available thin-film BIPV systems was monitored using an extensive monitoring program. Additionally, three mono-crystalline PV arrays allowed direct comparison of the technologies. The results of the monitoring work are presented and further work to be done is discussed, including the monitoring of possible long-term degradation.

Optical, structural and electrochromic behavior studies on nanocomposite thin film of aniline, o-toluidine and WO3

Science.gov (United States)

Najafi-Ashtiani, Hamed; Bahari, Ali

2016-08-01

In the field of materials for electrochromic (EC) applications much attention was paid to the derivatives of aniline. We report on the optical, structural and electrochromic properties of electrochromic thin film based on composite of WO3 nanoparticles and copolymer of aniline and o-toluidine prepared by electrochemical polymerization method on fluorine doped tin oxide (FTO) coated glass. The thin film was studied by X-ray diffraction (XRD) and Fourier transforms infrared (FTIR) spectroscopy. The morphology of prepared thin film was characterized by field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM) and the thermal gravimetric analysis (TGA) as well. The optical spectra of nanocomposite thin film were characterized in the 200-900 nm wavelength range and EC properties of nanocomposite thin film were studied by cyclic voltammetry (CV). The calculation of optical band gaps of thin film exhibited that the thin film has directly allowed transition with the values of 2.63 eV on first region and 3.80 eV on second region. Dispersion parameters were calculated based on the single oscillator model. Finally, important parameters such as dispersion energy, oscillator energy and lattice dielectric constant were determined and compared with the data from other researchers. The nonlinear optical properties such as nonlinear optical susceptibility, nonlinear absorption coefficient and nonlinear refractive index were extracted. The obtained results of nanocomposite thin film can be useful for the optoelectronic applications.

Electrical transport in (103) YBa2Cu3O7-x thin films

International Nuclear Information System (INIS)

Divin, Yu.Ya.; Poppe, U.; Faley, M.I.; Soltner, H.; Seo, J.W.; Kabius, B.; Urban, K.

1993-01-01

We have studied the electrical and structural properties of (103) YBa 2 Cu 3 O 7-x thin films to estimate the applicability of these films as base electrodes of planar-type Josephson junctions. (orig.)

Structural characterization of PbTi03, Sm0.6Nd0.4NiO3 and NdMnO3 multifunctional Perovskite thin films

Directory of Open Access Journals (Sweden)

Rapenne L.

2012-06-01

Full Text Available Different multifunctional (PbTiO3, Sm0.6Nd0.4NiO3, NdMnO3 thin films were grown by metalorganic chemical vapor deposition (MOCVD technique on SrTiO3 and LaAlO3 substrates. TEM and X-ray diffraction measurements reveal that almost single crystalline thin films can be epitaxially grown on the top of substrates. The relationship between the crystallographic orientation of the films and those of the substrates were determined by reciprocal space mapping and TEM analyses. PbTi03 thin films appear to be under tensile or compressive strain according to the different mismatch of their cell parameter with those of the substrate. Relaxation mechanism as a function of the film thickness arises from coexistence of different type of domains and size and strain effect are analyzed. SmNiO3 thin films present diffuse scattering strikes and are less well organized when compared to PbTi03 thin films. Different domains are observed as well as an additional parasitic phase close to NiO. Its regular distribution can be associated to reduced transport properties. Preliminary observations on NdMnO3 thin films show that an amorphous phase is obtained during MOCVD that can be transformed in a single crystalline film by annealing. The films are under tensile or compressive strain according to the different mismatch of their cell parameter with those of the substrate. Magnetic properties are investigated.

Thermochemical hydrogen generation of indium oxide thin films

Directory of Open Access Journals (Sweden)

Taekyung Lim

2017-03-01

Full Text Available Development of alternative energy resources is an urgent requirement to alleviate current energy constraints. As such, hydrogen gas is gaining attention as a future alternative energy source to address existing issues related to limited energy resources and air pollution. In this study, hydrogen generation by a thermochemical water-splitting process using two types of In2O3 thin films was investigated. The two In2O3 thin films prepared by chemical vapor deposition (CVD and sputtering deposition systems contained different numbers of oxygen vacancies, which were directly related to hydrogen generation. The as-grown In2O3 thin film prepared by CVD generated a large amount of hydrogen because of its abundant oxygen vacancies, while that prepared by sputtering had few oxygen vacancies, resulting in low hydrogen generation. Increasing the temperature of the In2O3 thin film in the reaction chamber caused an increase in hydrogen generation. The oxygen-vacancy-rich In2O3 thin film is expected to provide a highly effective production of hydrogen as a sustainable and efficient energy source.

ESR and X-ray diffraction studies on thin films of poly-3-hexylthiophene: Molecular orientation and magnetic interactions

International Nuclear Information System (INIS)

Sugiyama, Keisuke; Kojima, Takashi; Fukuda, Hisashi; Yashiro, Hisashi; Matsuura, Toshihiko; Shimoyama, Yuhei

2008-01-01

Poly-3-hexylthiophene (P3HT) thin films were investigated by X-ray diffraction (XRD) and electron spin resonance (ESR) to reveal the film structure and molecular organization. The XRD data showed a diffraction pattern with a plane separation between the planes containing thiophene rings of 16.0 A. Comparison between the XRD patterns of powder and thin films of P3HT suggests that the main chains are folded on the substrate. Angular variation of the line position (g-value) of ESR spectra revealed that thiophene ring of P3HT orients along the substrate normal axis. The ESR linewidth varied by the angular rotation, indicating the one-dimensional spin-chain interactions in the P3HT thin films with a linear network of spin-chains. An organic thin-film transistor (OTFT) with P3HT film as a channel layer was then demonstrated. The P3HT films showed conducting characteristics with holes as carriers. The OTFTs indicated a field-effect mobility of 4.93 x 10 -3 cm 2 /Vs and an on/off ratio of 73 in the accumulation mode

Gasochromic performance of WO3-nanorod thin films fabricated with an ArF excimer laser

International Nuclear Information System (INIS)

Yaacob, M. H.; Ou, J. Z.; Wlodarski, W.; Kim, C. S.; Lee, J. Y.; Kim, Y. H.; Oh, C. M.; Dhakal, K. P.; Kim, J. Y.; Kang, J. H.

2012-01-01

Thin films with tungsten trioxide (WO 3 ) nanorods were fabricated by using an ArF pulsed laser deposition system. Because the ArF excimer laser operates at a very short wavelength of 193 nm, short enough to expect strong absorption of the photons in the semiconductor oxide targets, and because the clusters incoming to the substrates have high momentum, we could build thin films with good surface morphology. Highly homogeneous arrays of nanorods with sizes mostly in the range of 30 - 40 nm were observed. The absorbance response towards hydrogen (H 2 ) gas was investigated for a WO 3 film coated with 25-A-thick palladium (Pd). The Pd/WO 3 -nanorod thin films exhibited excellent gasochromic response when measured in the visible-NIR range (400 - 1000 nm). As low as 0.06% H 2 concentration was clearly sensed. A significant reversible absorbance change and fast recovery ( 2 at different concentrations.

Self-regulated growth of LaVO3 thin films by hybrid molecular beam epitaxy

International Nuclear Information System (INIS)

Zhang, Hai-Tian; Engel-Herbert, Roman; Dedon, Liv R.; Martin, Lane W.

2015-01-01

LaVO 3 thin films were grown on SrTiO 3 (001) by hybrid molecular beam epitaxy. A volatile metalorganic precursor, vanadium oxytriisopropoxide (VTIP), and elemental La were co-supplied in the presence of a molecular oxygen flux. By keeping the La flux fixed and varying the VTIP flux, stoichiometric LaVO 3 films were obtained for a range of cation flux ratios, indicating the presence of a self-regulated growth window. Films grown under stoichiometric conditions were found to have the largest lattice parameter, which decreased monotonically with increasing amounts of excess La or V. Energy dispersive X-ray spectroscopy and Rutherford backscattering measurements were carried out to confirm film compositions. Stoichiometric growth of complex vanadate thin films independent of cation flux ratios expands upon the previously reported self-regulated growth of perovskite titanates using hybrid molecular beam epitaxy, thus demonstrating the general applicability of this growth approach to other complex oxide materials, where a precise control over film stoichiometry is demanded by the application

The film thickness dependent thermal stability of Al{sub 2}O{sub 3}:Ag thin films as high-temperature solar selective absorbers

Energy Technology Data Exchange (ETDEWEB)

Xiao Xiudi; Xu Gang, E-mail: xiudixiao@163.com; Xiong Bin; Chen Deming; Miao Lei [Chinese Academy of Sciences, Key Laboratory of Renewable Energy and Gas Hydrates, Guangzhou Institute of Energy Conversion (China)

2012-03-15

The monolayer Al{sub 2}O{sub 3}:Ag thin films were prepared by magnetron sputtering. The microstructure and optical properties of thin film after annealing at 700 Degree-Sign C in air were characterized by transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and spectrophotometer. It revealed that the particle shape, size, and distribution across the film were greatly changed before and after annealing. The surface plasmon resonance absorption and thermal stability of the film were found to be strongly dependent on the film thickness, which was believed to be associated with the evolution process of particle diffusion, agglomeration, and evaporation during annealing at high temperature. When the film thickness was smaller than 90 nm, the film SPR absorption can be attenuated until extinct with increasing annealing time due to the evaporation of Ag particles. While the film thickness was larger than 120 nm, the absorption can keep constant even after annealing for 64 h due to the agglomeration of Ag particles. On the base of film thickness results, the multilayer Al{sub 2}O{sub 3}:Ag solar selective thin films were prepared and the thermal stability test illustrated that the solar selectivity of multilayer films with absorbing layer thickness larger than 120 nm did not degrade after annealing at 500 Degree-Sign C for 70 h in air. It can be concluded that film thickness is an important factor to control the thermal stability of Al{sub 2}O{sub 3}:Ag thin films as high-temperature solar selective absorbers.

Application-related properties of giant magnetostrictive thin films

International Nuclear Information System (INIS)

Lim, S.H.; Kim, H.J.; Na, S.M.; Suh, S.J.

2002-01-01

In an effort to facilitate the utilization of giant magnetostrictive thin films in microdevices, application-related properties of these thin films, which include induced anisotropy, residual stress and corrosion properties, are investigated. A large induced anisotropy with an energy of 6x10 4 J/m 3 is formed in field-sputtered amorphous Sm-Fe-B thin films, resulting in a large magnetostriction anisotropy. Two components of residual stress, intrinsic compressive stress and tensile stress due to the difference of the thermal expansion coefficients between the substrate and thin film, are identified. The variation of residual stress with fabrication parameter and annealing temperature, and its influence on mechanical bending and magnetic properties are examined. Better corrosion properties are observed in Sm-Fe thin films than in Tb-Fe. Corrosion properties of Tb-Fe thin films, however, are much improved with the introduction of nitrogen to the thin films without deteriorating magnetostrictive properties

Operating method of amorphous thin film semiconductor element

Energy Technology Data Exchange (ETDEWEB)

Mori, Koshiro; Ono, Masaharu; Hanabusa, Akira; Osawa, Michio; Arita, Takashi

1988-05-31

The existing technologies concerning amorphous thin film semiconductor elements are the technologies concerning the formation of either a thin film transistor or an amorphous Si solar cell on a substrate. In order to drive a thin film transistor for electronic equipment control by the output power of an amorphous Si solar cell, it has been obliged to drive the transistor weth an amorphous solar cell which was formed on a substrate different from that for the transistor. Accordingly, the space for the amorphous solar cell, which was formed on the different substrate, was additionally needed on the substrate for the thin film transistor. In order to solve the above problem, this invention proposes an operating method of an amorphous thin film semiconductor element that after forming an amorphous Si solar cell through lamination on the insulation coating film which covers the thin film transistor formed on the substrate, the thin film transistor is driven by the output power of this solar cell. The invention eliminates the above superfluous space and reduces the size of the amorphous thin film semiconductor element including the electric source. (3 figs)

Ceramic Composite Thin Films

Science.gov (United States)

Ruoff, Rodney S. (Inventor); Stankovich, Sasha (Inventor); Dikin, Dmitriy A. (Inventor); Nguyen, SonBinh T. (Inventor)

2013-01-01

A ceramic composite thin film or layer includes individual graphene oxide and/or electrically conductive graphene sheets dispersed in a ceramic (e.g. silica) matrix. The thin film or layer can be electrically conductive film or layer depending the amount of graphene sheets present. The composite films or layers are transparent, chemically inert and compatible with both glass and hydrophilic SiOx/silicon substrates. The composite film or layer can be produced by making a suspension of graphene oxide sheet fragments, introducing a silica-precursor or silica to the suspension to form a sol, depositing the sol on a substrate as thin film or layer, at least partially reducing the graphene oxide sheets to conductive graphene sheets, and thermally consolidating the thin film or layer to form a silica matrix in which the graphene oxide and/or graphene sheets are dispersed.

Preparation of SrIrO{sub 3} thin films by using metal-organic aerosol deposition technique

Energy Technology Data Exchange (ETDEWEB)

Esser, Sebastian; Schneider, Melanie; Moshnyaga, Vasily; Gegenwart, Philipp [1. Physikalisches Institut, Georg-August-Universitaet Goettingen (Germany)

2013-07-01

The interplay between spin-orbit coupling and electronic correlations could lead to interesting novel states in iridium oxide materials. We focus on the perovskite phase of SrIrO{sub 3} because Moon et al. [1] showed by using optical spectroscopy and first-principles calculations that the last member of the Ruddlesden-Popper series Sr{sub n+1}Ir{sub n}O{sub 3n+1} (n = ∞) is close to the Mott transition. By using metal-organic aerosol deposition technique we have grown SrIrO{sub 3} thin films on (111)-oriented SrTiO{sub 3} substrates. The cubic symmetry of the SrTiO{sub 3} substrate ensured that the SrIrO{sub 3} thin film grew in the monoclinic perovskite phase. The X-ray diffraction results suggest that SrIrO{sub 3} thin films in perovskite structure were obtained and these show out of plane epitaxy with monoclinic (002){sub m}-orientation. The temperature dependence of the electrical resistivity of these SrIrO{sub 3} thin films were investigated and metallic behavior was observed down to 50 K.

Preparation of Cu2Sn3S7 Thin-Film Using a Three-Step Bake-Sulfurization-Sintering Process and Film Characterization

Directory of Open Access Journals (Sweden)

Tai-Hsiang Lui

2015-01-01

Full Text Available Cu2Sn3S7 (CTS can be used as the light absorbing layer for thin-film solar cells due to its good optical properties. In this research, the powder, baking, sulfur, and sintering (PBSS process was used instead of vacuum sputtering or electrochemical preparation to form CTS. During sintering, Cu and Sn powders mixed in stoichiometric ratio were coated to form the thin-film precursor. It was sulfurized in a sulfur atmosphere to form CTS. The CTS film metallurgy mechanism was investigated. After sintering at 500°C, the thin film formed the Cu2Sn3S7 phase and no impurity phase, improving its energy band gap. The interface of CTS film is continuous and the formation of intermetallic compound layer can increase the carrier concentration and mobility. Therefore, PBSS process prepared CTS can potentially be used as a solar cell absorption layer.

The structure and magnetic properties of β-(Ga0.96Mn0.04)2O3 thin film

Science.gov (United States)

Huang, Yuanqi; Chen, Zhengwei; Zhang, Xiao; Wang, Xiaolong; Zhi, Yusong; Wu, Zhenping; Tang, Weihua

2018-05-01

High quality epitaxial single phase (Ga0.96Mn0.04)2O3 and Ga2O3 thin films have been prepared on sapphire substrates by using laser molecular beam epitaxy (L-MBE). X-ray diffraction results indicate that the thin films have the monoclinic structure with a ≤ft( {\\bar 201} \\right) preferable orientation. Room temperature (RT) ferromagnetism appears and the magnetic properties of β-(Ga0.96Mn0.04)2O3 thin film are enhanced compared with our previous works. Experiments as well as the first principle method are used to explain the role of Mn dopant on the structure and magnetic properties of the thin films. The ferromagnetic properties are explained based on the concentration of transition element and the defects in the thin films. Project supported by the National Natural Science Foundation of China (Nos. 11404029, 51572033, 51172208) and the Fund of State Key Laboratory of Information Photonics and Optical Communications (BUPT).

Effect of composition on properties of In2O3-Ga2O3 thin films

Science.gov (United States)

Demin, I. E.; Kozlov, A. G.

2017-06-01

The In2O3-Ga2O3 mixed oxide polycrystalline thin films with various ratios of components were obtained by pulsed laser deposition. The effect of films composition on surface morphology, electrophysical and gas sensing properties and energies of adsorption and desorption of combustible gases was studied. The films with50%In2O3-50%Ga2O3 composition showed maximum gas response (˜25 times) combined with minimum optimal working temperature (˜530 °C) as compared with the other films. The optical transmittance of the films in visible range was investigated. For 50%In2O3-50%Ga2O3 films, the transmittance is higher in comparison with the other films. The explanation of the dependency of films behaviors on their composition was presented.The In2O3-Ga2O3 films were assumed to have perspectives as gas sensing material for semiconducting gas sensors.

Thin films prepared from tungstate glass matrix

Energy Technology Data Exchange (ETDEWEB)

Montanari, B.; Ribeiro, S.J.L.; Messaddeq, Y. [Departamento de Quimica Geral e Inorganica, Instituto de Quimica, Sao Paulo State University-UNESP, CP 355, CEP 14800-900, Araraquara, SP (Brazil); Li, M.S. [Instituto de Fisica, USP, CP 369, CEP 13560-970, Sao Carlos, SP (Brazil); Poirier, G. [Departamento de Ciencias Exatas, UNIFAL-MG, CEP 37130-000, Alfenas-MG (Brazil)], E-mail: gael@unifal-mg.edu.br

2008-01-30

Vitreous samples containing high concentrations of WO{sub 3} (above 40% M) have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. These films were characterized by X-ray diffraction (XRD), perfilometry, X-ray energy dispersion spectroscopy (EDS), M-Lines and UV-vis absorption spectroscopy. In this work, experimental parameters were established to obtain stable thin films showing a chemical composition close to the glass precursor composition and with a high concentration of WO{sub 3}. These amorphous thin films of about 4 {mu}m in thickness exhibit a deep blue coloration but they can be bleached by thermal treatment near the glass transition temperature. Such bleached films show several guided modes in the visible region and have a high refractive index. Controlled crystallization was realized and thus it was possible to obtain WO{sub 3} microcrystals in the amorphous phase.

Resistive switching in polycrystalline YMnO3 thin films

Directory of Open Access Journals (Sweden)

A. Bogusz

2014-10-01

Full Text Available We report a unipolar, nonvolatile resistive switching in polycrystalline YMnO3 thin films grown by pulsed laser deposition and sandwiched between Au top and Ti/Pt bottom electrodes. The ratio of the resistance in the OFF and ON state is larger than 103. The observed phenomena can be attributed to the formation and rupture of conductive filaments within the multiferroic YMnO3 film. The generation of conductive paths under applied electric field is discussed in terms of the presence of grain boundaries and charged domain walls inherently formed in hexagonal YMnO3. Our findings suggest that engineering of the ferroelectric domains might be a promising route for designing and fabrication of novel resistive switching devices.

Stabilization and enhanced energy gap by Mg doping in ɛ-phase Ga2O3 thin films

Science.gov (United States)

Bi, Xiaoyu; Wu, Zhenping; Huang, Yuanqi; Tang, Weihua

2018-02-01

Mg-doped Ga2O3 thin films with different doping concentrations were deposited on sapphire substrates using laser molecular beam epitaxy (L-MBE) technique. X-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS) and ultraviolet-visible (UV-vis) absorption spectrum were used to characterize the crystal structure and optical properties of the as-grown films. Compared to pure Ga2O3 thin film, the Mg-doped thin films have transformed from the most stable β-phase into ɛ-phase. The absorption edge shifted to about 205 nm and the optical bandgap increased to ˜ 6 eV. These properties reveal that Mg-doped Ga2O3 films may have potential applications in the field of deep ultraviolet optoelectronic devices, such as deep ultraviolet photodetectors, short wavelength light emitting devices and so on.

Thickness dependent structural, optical and electrical properties of Se85In12Bi3 nanochalcogenide thin films

Science.gov (United States)

Tripathi, Ravi P.; Zulfequar, M.; Khan, Shamshad A.

2018-04-01

Our aim is to study the thickness dependent effects on structure, electrical and optical properties of Se85In12Bi3 nanochalcogenide thin films. Bulk alloy of Se85In12Bi3 was synthesized by melt-quenching technique. The amorphous as well as glassy nature of Se85In12Bi3 chalcogenide was confirmed by non-isothermal Differential Scanning Calorimetry (DSC) measurements. The nanochalcogenide thin films of thickness 30, 60 and 90 nm were prepared on glass/Si wafer substrate using Physical Vapour Condensation Technique (PVCT). From XRD studies it was found that thin films have amorphous texture. The surface morphology and particle size of films were studied by Field Emission Scanning Electron Microscope (FESEM). From optical studies, different optical parameters were estimated for Se85In12Bi3 thin films at different thickness. It was found that the absorption coefficient (α) and extinction coefficient (k) increases with photon energy and decreases with film thickness. The optical absorption process followed the rule of indirect transitions and optical band gap were found to be increase with film thickness. The value of Urbach energy (Et) and steepness parameter (σ) were also calculated for different film thickness. For electrical studies, dc-conductivity measurement was done at different temperature and activation energy (ΔEc) were determined and found to be increase with film thickness.

Chemical synthesis of Fe{sub 2}O{sub 3} thin films for supercapacitor application

Energy Technology Data Exchange (ETDEWEB)

Kulal, P.M.; Dubal, D.P.; Lokhande, C.D. [Holography and Material Research Laboratory, Department of Physics, Shivaji University, Kolhapur 416004, M.S. (India); Fulari, V.J., E-mail: vijayfulari@gmail.com [Holography and Material Research Laboratory, Department of Physics, Shivaji University, Kolhapur 416004, M.S. (India)

2011-02-03

Research highlights: > Simple chemical synthesis of Fe{sub 2}O{sub 3}. > Formation of amorphous and hydrous Fe{sub 2}O{sub 3}. > Potential candidate for supercapacitors. - Abstract: Fe{sub 2}O{sub 3} thin films have been prepared by novel chemical successive ionic layer adsorption and reaction (SILAR) method. Further these films were characterized for their structural, morphological and optical properties by means of X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectrum, scanning electron microscopy (SEM), wettability test and optical absorption studies. The XRD pattern showed that the Fe{sub 2}O{sub 3} films exhibit amorphous in nature. Formation of iron oxide compound was confirmed from FTIR studies. The optical absorption showed existence of direct optical band gap of energy 2.2 eV. Fe{sub 2}O{sub 3} film surface showed superhydrophilic nature with water contact angle less than 10{sup o}. The supercapacitive properties of Fe{sub 2}O{sub 3} thin film investigated in 1 M NaOH electrolyte showed supercapacitance of 178 F g{sup -1} at scan rate 5 mV/s.

Host thin films incorporating nanoparticles

Science.gov (United States)

Qureshi, Uzma

The focus of this research project was the investigation of the functional properties of thin films that incorporate a secondary nanoparticulate phase. In particular to assess if the secondary nanoparticulate material enhanced a functional property of the coating on glass. In order to achieve this, new thin film deposition methods were developed, namely use of nanopowder precursors, an aerosol assisted transport technique and an aerosol into atmospheric pressure chemical vapour deposition system. Aerosol assisted chemical vapour deposition (AACVD) was used to deposit 8 series of thin films on glass. Five different nanoparticles silver, gold, ceria, tungsten oxide and zinc oxide were tested and shown to successfully deposit thin films incorporating nanoparticles within a host matrix. Silver nanoparticles were synthesised and doped within a titania film by AACVD. This improved solar control properties. A unique aerosol assisted chemical vapour deposition (AACVD) into atmospheric pressure chemical vapour deposition (APCVD) system was used to deposit films of Au nanoparticles and thin films of gold nanoparticles incorporated within a host titania matrix. Incorporation of high refractive index contrast metal oxide particles within a host film altered the film colour. The key goal was to test the potential of nanopowder forms and transfer the suspended nanopowder via an aerosol to a substrate in order to deposit a thin film. Discrete tungsten oxide nanoparticles or ceria nanoparticles within a titanium dioxide thin film enhanced the self-cleaning and photo-induced super-hydrophilicity. The nanopowder precursor study was extended by deposition of zinc oxide thin films incorporating Au nanoparticles and also ZnO films deposited from a ZnO nanopowder precursor. Incorporation of Au nanoparticles within a VO: host matrix improved the thermochromic response, optical and colour properties. Composite VC/TiC and Au nanoparticle/V02/Ti02 thin films displayed three useful

Characterization of nanocrystalline cadmium telluride thin films ...

Indian Academy of Sciences (India)

Unknown

tion method, successive ionic layer adsorption and reaction (SILAR), are described. For deposition of CdTe thin films ... By conducting several trials optimization of the adsorption, reaction and rinsing time duration for CdTe thin film .... The electrical resistivity of CdTe films was studied in air. Figure 3 shows the variation of log ...

Optimization of excess Bi doping to enhance ferroic orders of spin casted BiFeO{sub 3} thin film

Energy Technology Data Exchange (ETDEWEB)

Gupta, Surbhi; Gupta, Vinay, E-mail: drguptavinay@gmail.com [Department of Physics and Astrophysics, University of Delhi, Delhi (India); Tomar, Monika [Department of Physics, Miranda Housea, University of Delhi, Delhi (India); James, A. R. [Defence Metallurgical Research Laboratory, Hyderabad (India); Pal, Madhuparna; Guo, Ruyan; Bhalla, Amar [Department of Electrical and Computer Engineering, College of Engineering, University of Texas at SanAntonio, San Antonio 78249 (United States)

2014-06-21

Multiferroic Bismuth Ferrite (BiFeO{sub 3}) thin films with varying excess bismuth (Bi) concentration were grown by chemical solution deposition technique. Room temperature multiferroic properties (ferromagnetism, ferroelectricity, and piezoelectricity) of the deposited BiFeO{sub 3} thin films have been studied. High resolution X-ray diffraction and Raman spectroscopy studies reveal that the dominant phases formed in the prepared samples change continuously from a mixture of BiFeO{sub 3} and Fe{sub 2}O{sub 3} to pure BiFeO{sub 3} phase and, subsequently, to a mixture of BiFeO{sub 3} and Bi{sub 2}O{sub 3} with increase in the concentration of excess Bi from 0% to 15%. BiFeO{sub 3} thin films having low content (0% and 2%) of excess Bi showed the traces of ferromagnetic phase (γ-Fe{sub 2}O{sub 3}). Deterioration in ferroic properties of BiFeO{sub 3} thin films is also observed when prepared with higher content (15%) of excess Bi. Single-phased BiFeO{sub 3} thin film prepared with 5% excess Bi concentration exhibited the soft ferromagnetic hysteresis loops and ferroelectric characteristics with remnant polarization 4.2 μC/cm{sup 2} and saturation magnetization 11.66 emu/g. The switching of fine spontaneous domains with applied dc bias has been observed using piezoresponse force microscopy in BiFeO{sub 3} thin films having 5% excess Bi. The results are important to identify optimum excess Bi concentration needed for the formation of single phase BiFeO{sub 3} thin films exhibiting the improved multiferroic properties.

Nb3Al thin film deposition for low-noise terahertz electronics

International Nuclear Information System (INIS)

Dochev, D; Pavolotsky, A B; Belitsky, V; Olofsson, H

2008-01-01

Higher energy gap superconducting materials were always interesting for low-noise mixer applications such as superconductor-insulator-superconductor tunnel junctions (SIS) and hot-electron bolometer (HEB) used in sub-millimeter and terahertz parts of electro-magnetic spectrum. Here, we report a novel approach for producing Nb 3 Al thin film by co-sputtering from two confocally arranged Nb and Al dc-magnetrons onto substrate heated up to 830 deg. C. Characterization of the deposited films revealed presence of the A15 phase and measured critical temperature was up to 15.7 K with the transition width 0.2-0.3 K for a 300 nm thick film. We measured the film critical magnetic field and studied influence of annealing on the film properties. We have investigated compositional depth profile of the deposited films by spectroscopy of reflected electrons

Gas Sensing Properties of Metal Doped WO3 Thin Film Sensors Prepared by Pulsed Laser Deposition and DC Sputtering Process

Science.gov (United States)

Bhuiyan, Md. Mosharraf Hossain; Ueda, Tsuyoshi; Ikegami, Tomoaki; Ebihara, Kenji

2006-10-01

Tungsten trioxide (WO3) thin films gas sensors were prepared by the KrF excimer pulsed laser deposition (PLD) method. The films were prepared on the quartz glass, silicon and also on the Al2O3 sensor substrates with platinum interdigitated electrodes. The effect of doping of the platinum (Pt), palladium (Pd) or gold (Au) on the WO3 thin film was also investigated. These metals were doped to the WO3 thin film by the DC sputtering process during the PLD. The substrate temperature and the oxygen pressure were 400 °C and 100 mTorr, respectively, during the deposition. The films were characterized by atomic force microscopy (AFM) and X-ray diffraction (XRD). The sensitivity of the prepared sensors to 60 ppm NO gas was examined using the two terminal resistance method in a chamber at atmospheric pressure and operating temperatures of 25-350 °C. The sensitivity of the WO3 thin films doped with Pt, Pd, or Au was found to be higher than that of the undoped WO3 thin film.

Novel chemical analysis for thin films

International Nuclear Information System (INIS)

Usui, Toshio; Kamei, Masayuki; Aoki, Yuji; Morishita, Tadataka; Tanaka, Shoji

1991-01-01

Scanning electron microscopy and total-reflection-angle X-ray spectroscopy (SEM-TRAXS) was applied for fluorescence X-ray analysis of 50A- and 125A-thick Au thin films on Si(100). The intensity of the AuM line (2.15 keV) emitted from the Au thin films varied as a function of the take-off angle (θ t ) with respect to the film surface; the intensity of AuM line from the 125A-thick Au thin film was 1.5 times as large as that of SiK α line (1.74 keV) emitted from the Si substrate when θ t = 0deg-3deg, in the vicinity of a critical angle for total external reflection of the AuM line at Si (0.81deg). In addition, the intensity of the AuM line emitted from the 50A-thick Au thin film was also sufficiently strong for chemical analysis. (author)

Substrate decoration for improvement of current-carrying capabilities of YBa2Cu3Ox thin films

International Nuclear Information System (INIS)

Khoryushin, Alexey V.; Mozhaev, Peter B.; Mozhaeva, Julia E.; Bdikin, Igor K.; Zhao, Yue; Andersen, Niels H.; Jacobsen, Claus S.; Hansen, Jørn Bindslev

2013-01-01

Highlights: ► Effects of substrate decoration on properties of YBCO thin films were studied. ► Y 2 O 3 nanoparticles, ultra-thin Y 2 O 3 and Y:ZrO 2 layers were used as decoration layer. ► Decoration improves j C (5 T and 50 K) up to 0.97 MA/cm 2 vs. 0.76 MA/cm 2 for a reference film. ► Ultra-thin layer of yttria and yttria nanoparticles have a similar effect on YBCO. ► Y 2 O 3 decoration results in power law coefficient α = 0.3 vs. α = 0.4 for a reference film. -- Abstract: The effects of substrate decoration with yttria and Y:ZrO 2 on the structural and electrical properties of the YBa 2 Cu 3 O x (YBCO) thin films are studied. The films were deposited on (LaAlO 3 ) 3 –(Sr 2 AlTaO 8 ) 7 substrates by pulsed laser deposition. Two different structures of decoration layer were applied, a template layer of nanoparticles and an uniform ultra-thin layer. Significant improvement of current-carrying capabilities was observed, especially at high external magnetic fields. Structural studies of these films reveal the presence of extended linear defects in the YBCO matrix. The formation of these structures is attributed to seeding of randomly oriented YBCO grains due to suppression of epitaxy in the very beginning of the deposition. The films of both kinds of decoration layers show nearly the same improvement of j C over the reference film at 77 and 50 K: j C (5T and 50 K) reaches 0.92 and 0.97 MA/cm 2 for uniform and template decoration layers. At 5 and 20 K the effect of template decoration layers is more beneficial: j C (5T and 20 K) values are 3.5 and 4.1 MA/cm 2 , j C (5T and 5 K) values are 6.4 and 7.9 MA/cm 2 , for uniform and template decoration layers, respectively

Indium Sulfide and Indium Oxide Thin Films Spin-Coated from Triethylammonium Indium Thioacetate Precursor for n-Channel Thin Film Transistor

Energy Technology Data Exchange (ETDEWEB)

Tung, Duy Dao; Jeong, Hyun Dam [Chonnam Natioal University, Gwangju (Korea, Republic of)

2014-09-15

The In{sub 2}S{sub 3} thin films of tetragonal structure and In{sub 2}O{sub 3} films of cubic structure were synthesized by a spin coating method from the organometallic compound precursor triethylammonium indium thioacetate ([(Et){sub 3}NH]+ [In(SCOCH{sub 3}){sub 4}]''-; TEA-InTAA). In order to determine the electron mobility of the spin-coated TEA-InTAA films, thin film transistors (TFTs) with an inverted structure using a gate dielectric of thermal oxide (SiO{sub 2}) was fabricated. These devices exhibited n-channel TFT characteristics with a field-effect electron mobility of 10.1 cm''2 V''-1s''-1 at a curing temperature of 500 o C, indicating that the semiconducting thin film material is applicable for use in low-cost, solution-processed printable electronics.

Critical behavior of ferromagnetic La0.7Sr0.3CoO3 thin films

International Nuclear Information System (INIS)

Schwarz, T.

2007-07-01

The present thesis concentrates on the critical behavior of ferromagnetic La 0.7 Sr 0.3 CoO 3 thin films (LSCO) close to the magnetic phase transition. The LSCO thin films were prepared by pulsed laser deposition and optimized with respect to their structural and magnetic properties. For the characterization of the structural and magnetic characteristics various methods were used. By means of X-ray diffraction and electron microscopy the crystallinity and microstructure of the epitaxial films were examined, respectively. The analysis of the chemical composition was accomplished by Rutherford backscattering and energy dispersive X-ray diffraction (EDX). Parallel to the investigations of the LSCO films a low-temperature measuring system for electrical measurements in magnetic fields up to 8 T in a temperature range from 1.5 K to 300 K was developed and built up including the necessary control and measuring software. The central point of this work was dedicated to the characterization of the magnetic characteristics of the LSCO films. In comparison, single crystals and polycrystalline bulk samples were also available. At these samples temperature-dependent and isothermal magnetization measurements were accomplished by a SQUID magnetometer. To determine the critical behavior of the samples the critical exponents of the susceptibility and the spontaneous magnetization in the proximity of the ferromagnetic phase transition were determined. For the exact determination of the critical exponents from the experimental data an evaluation routine in Matlab on basis of the Arrott representation method was used. In addition to the investigations of the critical behavior, electrical transportation measurements and neutron reflection measurements with spin-polarized neutrons were performed. The investigations of this work show that, in contrast to the critical behavior of single-crystal LSCO volume samples where a three-dimensional Heisenberg behavior could be observed, the

NMR characterization of thin films

Science.gov (United States)

Gerald II, Rex E.; Klingler, Robert J.; Rathke, Jerome W.; Diaz, Rocio; Vukovic, Lela

2010-06-15

A method, apparatus, and system for characterizing thin film materials. The method, apparatus, and system includes a container for receiving a starting material, applying a gravitational force, a magnetic force, and an electric force or combinations thereof to at least the starting material, forming a thin film material, sensing an NMR signal from the thin film material and analyzing the NMR signal to characterize the thin film of material.

NMR characterization of thin films

Science.gov (United States)

Gerald, II, Rex E.; Klingler, Robert J.; Rathke, Jerome W.; Diaz, Rocio; Vukovic, Lela

2008-11-25

A method, apparatus, and system for characterizing thin film materials. The method, apparatus, and system includes a container for receiving a starting material, applying a gravitational force, a magnetic force, and an electric force or combinations thereof to at least the starting material, forming a thin film material, sensing an NMR signal from the thin film material and analyzing the NMR signal to characterize the thin film of material.

Photoelectrochemical Performance Observed in Mn-Doped BiFeO3 Heterostructured Thin Films

Directory of Open Access Journals (Sweden)

Hao-Min Xu

2016-11-01

Full Text Available Pure BiFeO3 and heterostructured BiFeO3/BiFe0.95Mn0.05O3 (5% Mn-doped BiFeO3 thin films have been prepared by a chemical deposition method. The band structures and photosensitive properties of these films have been investigated elaborately. Pure BiFeO3 films showed stable and strong response to photo illumination (open circuit potential kept −0.18 V, short circuit photocurrent density was −0.023 mA·cm−2. By Mn doping, the energy band positions shifted, resulting in a smaller band gap of BiFe0.95Mn0.05O3 layer and an internal field being built in the BiFeO3/BiFe0.95Mn0.05O3 interface. BiFeO3/BiFe0.95Mn0.05O3 and BiFe0.95Mn0.05O3 thin films demonstrated poor photo activity compared with pure BiFeO3 films, which can be explained by the fact that Mn doping brought in a large amount of defects in the BiFe0.95Mn0.05O3 layers, causing higher carrier combination and correspondingly suppressing the photo response, and this negative influence was more considerable than the positive effects provided by the band modulation.

Characterization of nanostructured Mn3O4 thin films grown by SILAR method at room temperature

International Nuclear Information System (INIS)

Ubale, A.U.; Belkhedkar, M.R.; Sakhare, Y.S.; Singh, Arvind; Gurada, Chetan; Kothari, D.C.

2012-01-01

A novel successive ionic layer adsorption and reaction method has been successfully employed to grow nanostructured conducting nearly transparent thin films of Mn 3 O 4 on to glass substrates at room temperature using MnCl 2 and NaOH as cationic and anionic precursors. The structural and morphological characterizations of the as deposited Mn 3 O 4 films have been carried out by means of X-ray diffraction (XRD), Field Emission Scanning Electron Micrograph (FESEM), EDAX, Atomic Fore Microscopy (AFM) and Fourier Transform Infrared Spectrum (FTIR) analysis. The optical absorption and electrical resistivity measurements were carried out to investigate optical band gap and activation energy of Mn 3 O 4 films deposited by SILAR method. The optical band gap and activation energy of the as deposited film is found to be 2.70 and 0.14 eV respectively. The thermo-emf measurements of Mn 3 O 4 thin film confirm its p-type semiconducting nature. Highlights: ► Nanostructured Mn 3 O 4 thin film is prepared by SILAR method at room temperature. ► The film is nanocrystalline with orthorhombic structure of Mn 3 O 4 . ► The XRD, FTIR, FESEM, EDX and AFM characterization confirms nanocrystalline nature. ► Optical band gap, electrical resistivity and activation energy of film is reported. ► A thermo-emf measurement confirms p-type conductivity of Mn 3 O 4 films.

Photoluminescence properties of perovskite multilayer thin films

Energy Technology Data Exchange (ETDEWEB)

Macario, Leilane Roberta; Longo, Elson, E-mail: leilanemacario@gmail.com [Universidade Federal de Sao Carlos (UFSCar), SP (Brazil); Mazzo, Tatiana Martelli [Universidade Federal de Sao Paulo (UNIFESP), SP (Brazil); Bouquet, Valerie; Deputier, Stephanie; Ollivier, Sophie; Guilloux-Viry, Maryline [Universite de Rennes (France)

2016-07-01

Full text: The knowledge of the optical properties of thin films is important in many scientific, technological and industrial applications of thin films such as photoconductivity, solar energy, photography, and numerous other applications [1]. In this study, perovskite type oxides were grown by pulsed laser deposition [2] in order to obtain thin films with applicable optical properties. The LaNiO{sub 3} (LN), BaTiO{sub 3} (BT) and KNbO{sub 3} (KNb) targets were prepared by solid-state reaction. The X-ray Diffraction revealed the presence of the desired phases, containing the elements of interest in the targets and in the thin films that were produced. The LN, BT and KNb thin films were polycrystalline and the corresponding diffraction peaks were indexed in the with JCPDS cards n. 00-033-0711, n. 00-005-0626, and n. 00-009-0156, respectively. The multilayers films were polycrystalline. The majority of the micrographs obtained by scanning electron microscopy presented films with a thickness from 100 to 400 nm. The photoluminescent (PL) emission spectra of thin films show different broad bands that occupies large region of the visible spectrum, ranging from about 300-350 to 600-650 nm of the electromagnetic spectrum. The PL emission is associated with the order-disorder structural, even small structural changes can modify the interactions between electronic states. The structural disorder results in formation of new energy levels in the forbidden region. The proximity or distance of these new energy levels formed in relation to valence band and to the conduction band results in PL spectra located at higher or lower energies. These interactions change the electronic states which can be influenced by defects, particularly the interface defects between the layers of the thin films. The presence of defects results in changes in the broad band matrix intensity and in displacement of the PL emission maximum. (author)

Antisolvent-assisted powder engineering for controlled growth of hybrid CH3NH3PbI3 perovskite thin films

Directory of Open Access Journals (Sweden)

Yong Chan Choi

2017-02-01

Full Text Available We develop antisolvent-assisted powder engineering for the controlled growth of hybrid inorganic-organic CH3NH3PbI3 (MAPbI3 perovskite thin films. The powders, which are used as the precursors for solution processing, are synthesized by pouring a MAPbI3 precursor solution into various antisolvents, such as dichloromethane, chloroform, diethyl ether, and toluene. Two types of powders having different colors are obtained, depending on the antisolvent used. The choice of the antisolvent used for synthesizing the powders strongly influences not only the phases of the powders but also the morphology and structure of the thin films subsequently fabricated by solution processing. This, in turn, affects the photovoltaic performance.

Handbook of thin film technology

CERN Document Server

Frey, Hartmut

2015-01-01

“Handbook of Thin Film Technology” covers all aspects of coatings preparation, characterization and applications. Different deposition techniques based on vacuum and plasma processes are presented. Methods of surface and thin film analysis including coating thickness, structural, optical, electrical, mechanical and magnetic properties of films are detailed described. The several applications of thin coatings and a special chapter focusing on nanoparticle-based films can be found in this handbook. A complete reference for students and professionals interested in the science and technology of thin films.

Preparation and evaluation of Mn3GaN1-x thin films with controlled N compositions

Science.gov (United States)

Ishino, Sunao; So, Jongmin; Goto, Hirotaka; Hajiri, Tetsuya; Asano, Hidefumi

2018-05-01

Thin films of antiperovskite Mn3GaN1-x were grown on MgO (001) substrates by reactive magnetron sputtering, and their structural, magnetic, and magneto-optical properties were systematically investigated. It was found that the combination of the deposition rate and the N2 gas partial pressure could produce epitaxial films with a wide range of N composition (N-deficiency) and resulting c/a values (0.93 - 1.0). While the films with c/a = 0.992 - 1.0 were antiferromagnetic, the films with c/a = 0.93 - 0.989 showed perpendicular magnetic anisotropy (PMA) with the maximum PMA energy up to 1.5×106 erg/cm3. Systematic dependences of the energy spectra of the polar Kerr signals on the c/a ratio were observed, and the Kerr ellipticity was as large as 2.4 deg. at 1.9 eV for perpendicularly magnetized ferromagnetic thin films with c/a = 0.975. These results highlight that the tetragonal distortion plays an important role in magnetic and magneto-optical properties of Mn3GaN1-x thin films.

Preparation and characterization of Cu2SnS3 thin films by electrodeposition

Science.gov (United States)

Patel, Biren; Narasimman, R.; Pati, Ranjan K.; Mukhopadhyay, Indrajit; Ray, Abhijit

2018-05-01

Cu2SnS3 thin films were electrodeposited on F:SnO2/Glass substrates at room temperature by using aqueous solution. Copper and tin were first electrodeposited from single bath and post annealed in the presence of sulphur atmosphere to obtain the Cu2SnS3 phase. The Cu2SnS3 phase with preferred orientation along the (112) crystal direction grows to greater extent by the post annealing of the film. Raman analysis confirms the monoclinic crystal structure of Cu2SnS3 with principle mode of vibration as A1 (symmetric breathing mode) corresponding to the band at 291 cm-1. It also reveals the benign coexistence of orthorhombic Cu3SnS4 and Cu2SnS7 phases. Optical properties of the film show direct band gap of 1.25 eV with a high absorption coefficient of the order of 104 cm-1 in the visible region. Photo activity of the electrodeposited film was established in two electrode photoelectro-chemical cell, where an open circuit voltage of 91.6 mV and a short circuit current density of 10.6 µA/cm2 were recorded. Fabrication of Cu2SnS3 thin film heterojunction solar cell is underway.

Giant Polarization Rotation in BiFeO3/SrTiO3 Thin Films.

Science.gov (United States)

Langner, M. C.; Chu, Y. H.; Martin, L. M.; Gajek, M.; Ramesh, R.; Orenstein, J.

2008-03-01

We use optical second harmonic generation to probe dynamics of the ferroelectric polarization in (111) oriented BiFeO3 thin films grown on SrTiO3 substrates. The second harmonic response indicates 3m point group symmetry and is consistent with a spontaneous polarization normal to the surface of the film. We measure large changes in amplitude and lowering of symmetry, consistent with polarization rotation, when modest electric fields are applied in the plane of the film. At room temperature the rotation is an order of magnitude larger than expected from reported values of the dielectric constant and increases further (as 1/T) as temperature is lowered. We propose a substrate interaction model to explain these results.

YIG: Bi2O3 Nanocomposite Thin Films for Magnetooptic and Microwave Applications

Directory of Open Access Journals (Sweden)

M. Nur-E-Alam

2015-01-01

Full Text Available Y3Fe5O12-Bi2O3 composite thin films are deposited onto Gd3Ga5O12 (GGG substrates and their annealing crystallization regimes are optimized (in terms of both process temperatures and durations to obtain high-quality thin film layers possessing magnetic properties attractive for a range of technological applications. The amount of bismuth oxide content introduced into these nanocomposite-type films is controlled by adjusting the RF power densities applied to both Y3Fe5O12 and Bi2O3 sputtering targets during the cosputtering deposition processes. The measured material properties of oven-annealed YIG-Bi2O3 films indicate that cosputtering of YIG-Bi2O3 composites can provide the flexibility of application-specific YIG layers fabrication of interest for several existing, emerging, and also frontier technologies. Experimental results demonstrate large specific Faraday rotation (of more than 1°/µm at 532 nm, achieved simultaneously with low optical losses in the visible range and very narrow peak-to-peak ferromagnetic resonance linewidth of around ΔHpp= 6.1 Oe at 9.77 GHz.

Ultraviolet emitting (Y1-xGd x)2O3-δ thin films deposited by radio frequency magnetron sputtering; structure-property-thin film processing relationships

International Nuclear Information System (INIS)

Fowlkes, J.D.; Fitz-Gerald, J.M.; Rack, P.D.

2007-01-01

The effects that the oxygen partial pressure, substrate temperature and annealing temperature have on the cathodoluminescence (CL) efficiency of radio frequency magnetron sputter deposited Gd-doped Y 2 O 3 thin films is investigated. Furthermore these sputtering parameters are correlated to the degree of crystallinity, the phases present (cubic (α) versus monoclinic (β) Y 2 O 3 ), and the stoichiometry of the thin films. Films deposited at room temperature (RT) did not CL, however, the films were activated by a post-deposition anneal at 1273 K for 6 h. Films deposited at 873 K had a very low CL efficiency which was significantly enhanced by a post-deposition anneal. For RT deposited films the external CL efficiency increased with increasing oxygen partial pressure for the range studied, however the opposite trend was observed for the 873 K deposited films. Examination of the morphology and grain size of the high temperature deposited films revealed that the average grain size increased with decreasing partial pressure and the observed increase in the external CL efficiency was attributed to enhanced anomalous diffraction. An intrinsic CL efficiency term was determined to circumvent the effects of the enhanced anomalous diffraction, and the CL efficiency was correlated to the integrated intensity of the (222) of the cubic α-Y 2 O 3 phase

Stabilization and enhanced energy gap by Mg doping in ε-phase Ga2O3 thin films

Directory of Open Access Journals (Sweden)

Xiaoyu Bi

2018-02-01

Full Text Available Mg-doped Ga2O3 thin films with different doping concentrations were deposited on sapphire substrates using laser molecular beam epitaxy (L-MBE technique. X-ray diffraction (XRD, x-ray photoelectron spectroscopy (XPS and ultraviolet-visible (UV-vis absorption spectrum were used to characterize the crystal structure and optical properties of the as-grown films. Compared to pure Ga2O3 thin film, the Mg-doped thin films have transformed from the most stable β-phase into ε-phase. The absorption edge shifted to about 205 nm and the optical bandgap increased to ∼ 6 eV. These properties reveal that Mg-doped Ga2O3 films may have potential applications in the field of deep ultraviolet optoelectronic devices, such as deep ultraviolet photodetectors, short wavelength light emitting devices and so on.

Rare Earth Oxide Thin Films

CERN Document Server

Fanciulli, Marco

2007-01-01

Thin rare earth (RE) oxide films are emerging materials for microelectronic, nanoelectronic, and spintronic applications. The state-of-the-art of thin film deposition techniques as well as the structural, physical, chemical, and electrical properties of thin RE oxide films and of their interface with semiconducting substrates are discussed. The aim is to identify proper methodologies for the development of RE oxides thin films and to evaluate their effectiveness as innovative materials in different applications.

Thin-film solar cells

International Nuclear Information System (INIS)

Aberle, Armin G.

2009-01-01

The rapid progress that is being made with inorganic thin-film photovoltaic (PV) technologies, both in the laboratory and in industry, is reviewed. While amorphous silicon based PV modules have been around for more than 20 years, recent industrial developments include the first polycrystalline silicon thin-film solar cells on glass and the first tandem solar cells based on stacks of amorphous and microcrystalline silicon films ('micromorph cells'). Significant thin-film PV production levels are also being set up for cadmium telluride and copper indium diselenide.

Nanocomposite Thin Film of Poly(3-aminobenzoic acid and Multiwalled Carbon Nanotubes Fabricated through an Electrochemical Method

Directory of Open Access Journals (Sweden)

Paphawadee Netsuwan

2014-01-01

Full Text Available The composite thin films of poly(3-aminobenzoic acid (PABA and multiwalled carbon nanotubes (MWNTs are successfully fabricated through an electrochemical method. The composite mixtures containing 50 mM of 3-aminobenzoic acid with various concentrations of MWNTs (1.0, 2.5, 5.0, 7.5, and 10 mg/mL in 0.5 M H2SO4 were prepared and used in this study. Cyclic voltammetry (CV was used for fabrication and monitoring the electropolymerization of the composite thin films with potential range of 0 to 1100 mV for 5 cycles at scan rate of 20 mV/s on indium tin oxide- (ITO-coated glass substrate. UV-vis absorption spectroscopy, atomic force microscopy (AFM, and scanning electron microscopy (SEM techniques were employed to characterize the obtained composite thin films. It was found that MWNTs can enhance the peak current of CV traces of the PABA/MWNTs composite thin films without affecting the UV-vis absorption spectra. The surface morphology of the thin films can be studied using AFM and SEM techniques.

Photolithographically patterened thin-film multilayer devices of YBa2Cu3O7-x

International Nuclear Information System (INIS)

Kingston, J.J.; Wellstood, F.C.; Quan, D.; Clarke, J.

1990-09-01

We have fabricated thin-film YBa 2 Cu 3 O 7-x -SrTiO 3 -YBa 2 Cu 3 O 7-x multilayer interconnect structures in which each in situ laser-deposited film is independently patterned by photolithography. In particular, we have constructed the two key components necessary for a superconducting multilayer interconnect technology, crossovers and window contacts. As a further demonstration of the technology, we have fabricated a thin-film flux transformer, suitable for use with a Superconducting QUantum Interference Device (SQUID), that includes a ten-turn input coil with 6μm linewidth. Transport measurements showed that the critical temperature was 87K and the critical current was 135 μA at 82K. 7 refs., 6 figs

Growth of (100)-highly textured BaBiO{sub 3} thin films on silicon

Energy Technology Data Exchange (ETDEWEB)

Ferreyra, C. [GIyA and INN, CNEA, Av. Gral Paz 1499, 1650 San Martín, Buenos Aires (Argentina); Departamento de Física, Facultad Ciencias Exactas y Naturales, Universidad de Buenos Aires, Pabellón 1, Ciudad Universitaria, Buenos Aires (Argentina); Marchini, F. [Consejo Nacional de Investigaciones Científicas y Técnicas (CONICET) (Argentina); Departamento de Química Inorgánica, Analítica y Química-Física, INQUIMAE-CONICET, Facultad Ciencias Exactas y Naturales, Universidad de Buenos Aires, Pabellón 2, Ciudad Universitaria, Buenos Aires (Argentina); Granell, P. [INTI, CMNB, Av. Gral Paz 5445, B1650KNA San Martín, Buenos Aires (Argentina); Golmar, F. [Consejo Nacional de Investigaciones Científicas y Técnicas (CONICET) (Argentina); INTI, CMNB, Av. Gral Paz 5445, B1650KNA San Martín, Buenos Aires (Argentina); Escuela de Ciencia y Tecnología, UNSAM, Campus Miguelete, 1650 San Martín, Buenos Aires (Argentina); Albornoz, C. [GIyA and INN, CNEA, Av. Gral Paz 1499, 1650 San Martín, Buenos Aires (Argentina); and others

2016-08-01

We report on the growth and characterization of non-epitaxial but (100)-highly textured BaBiO{sub 3} thin films on silicon substrates. We have found the deposition conditions that optimize the texture, and show that the textured growth is favoured by the formation of a BaO layer at the first growth stages. X-ray diffraction Φ-scans, together with the observation that the same textured growth is found on films grown on Pt and SiO{sub 2} buffered Si, demonstrate the absence of epitaxy. Finally, we have shown that our (100)-oriented BaBiO{sub 3} films can be used as suitable buffers for the growth of textured heterostructures on silicon, which could facilitate the integration of potential devices with standard electronics. - Highlights: • BaBiO{sub 3} thin films were grown on Si substrates and characterized. • Films prepared using optimized conditions are highly textured in the (100) direction. • The absence of in-plane texture was demonstrated by X-ray diffraction. • Our films are suitable buffers for the growth of (100)-textured oxide heterostructures.

Process for forming thin film, heat treatment process of thin film sheet, and heat treatment apparatus therefor

International Nuclear Information System (INIS)

Watanabe, S.

1984-01-01

The invention provides a process for forming a magnetic thin film on a base film, a heat treatment process of a thin film sheet consisting of the base film and the magnetic thin film, and an apparatus for performing heat treatment of the thin film sheet. Tension applied to the thin film sheet is substantially equal to that applied to the base film when the magnetic thin film is formed thereon. Then, the thin film sheet is treated with heat. The thin film sheet is heated with a given temperature gradient to a reactive temperature at which heat shrinkage occurs, while the tension is being applied thereto. Thereafter, the thin film sheet to which the tension is still applied is cooled with substantially the same temperature gradient as applied in heating. The heat treatment apparatus has a film driving unit including a supply reel, a take-up reel, a drive source and guide rollers; a heating unit including heating plates, heater blocks and a temperature controller for heating the sheet to the reactive temperature; and a heat insulating unit including a thermostat and another temperature controller for maintaining the sheet at the nonreactive temperature which is slightly lower than the reactive temperature

Oxidation of ruthenium thin films using atomic oxygen

Energy Technology Data Exchange (ETDEWEB)

McCoy, A.P.; Bogan, J.; Brady, A.; Hughes, G.

2015-12-31

In this study, the use of atomic oxygen to oxidise ruthenium thin films is assessed. Atomic layer deposited (ALD) ruthenium thin films (~ 3 nm) were exposed to varying amounts of atomic oxygen and the results were compared to the impact of exposures to molecular oxygen. X-ray photoelectron spectroscopy studies reveal substantial oxidation of metallic ruthenium films to RuO{sub 2} at exposures as low as ~ 10{sup 2} L at 575 K when atomic oxygen was used. Higher exposures of molecular oxygen resulted in no metal oxidation highlighting the benefits of using atomic oxygen to form RuO{sub 2}. Additionally, the partial oxidation of these ruthenium films occurred at temperatures as low as 293 K (room temperature) in an atomic oxygen environment. - Highlights: • X-ray photoelectron spectroscopy study of the oxidation of Ru thin films • Oxidation of Ru thin films using atomic oxygen • Comparison between atomic oxygen and molecular oxygen treatments on Ru thin films • Fully oxidised RuO{sub 2} thin films formed with low exposures to atomic oxygen.

Preferential growth and enhanced dielectric properties of Ba0.7Sr0.3TiO3 thin films with preannealed Pt bottom electrode

International Nuclear Information System (INIS)

Zhu Xiaohong; Ren Yinjuan; Zhang Caiyun; Zhu Jiliang; Zhu Jianguo; Xiao Dingquan; Defaÿ, Emmanuel; Aïd, Marc

2013-01-01

Ba 0.7 Sr 0.3 TiO 3 (BST) thin films, about 100 nm in thickness, were prepared on unannealed and 700 °C-preannealed Pt bottom electrodes by the ion beam sputtering and post-deposition annealing method. It was found that the preannealed Pt layer has a more compact structure, making it not only a bottom electrode but also a good template for high-quality BST thin film growth. The BST films deposited on preannealed Pt bottom electrodes showed (0 0 l)-preferred orientation, dense and uniform microstructure with no intermediate phase formed at the film/electrode interface, and thus enhanced dielectric properties. As a result, the typical relative dielectric constant and tunability (under a dc electric field of 1 MV cm −1 ) reach 180 and 50.1%, respectively, for the BST thin films with preannealed Pt bottom electrodes, which are significantly higher than those (166 and 41.3%, respectively) for the BST thin films deposited on unannealed Pt bottom electrodes. (paper)

Preferential growth and enhanced dielectric properties of Ba0.7Sr0.3TiO3 thin films with preannealed Pt bottom electrode

Science.gov (United States)

Zhu, Xiaohong; Defaÿ, Emmanuel; Aïd, Marc; Ren, Yinjuan; Zhang, Caiyun; Zhu, Jiliang; Zhu, Jianguo; Xiao, Dingquan

2013-03-01

Ba0.7Sr0.3TiO3 (BST) thin films, about 100 nm in thickness, were prepared on unannealed and 700 °C-preannealed Pt bottom electrodes by the ion beam sputtering and post-deposition annealing method. It was found that the preannealed Pt layer has a more compact structure, making it not only a bottom electrode but also a good template for high-quality BST thin film growth. The BST films deposited on preannealed Pt bottom electrodes showed (0 0 l)-preferred orientation, dense and uniform microstructure with no intermediate phase formed at the film/electrode interface, and thus enhanced dielectric properties. As a result, the typical relative dielectric constant and tunability (under a dc electric field of 1 MV cm-1) reach 180 and 50.1%, respectively, for the BST thin films with preannealed Pt bottom electrodes, which are significantly higher than those (166 and 41.3%, respectively) for the BST thin films deposited on unannealed Pt bottom electrodes.

Ultra-thin zirconia films on Zr-alloys

Energy Technology Data Exchange (ETDEWEB)

Choi, Joong Il Jake; Mayr-Schmoelzer, Wernfried; Mittendorfer, Florian; Redinger, Josef; Diebold, Ulrike; Schmid, Michael [Institute of Applied Physics, Vienna University of Technology (Austria); Li, Hao; Rupprechter, Guenther [Institute of Materials Chemistry, Vienna University of Technology (Austria)

2014-07-01

Zirconia ultra-thin films have been prepared by oxidation of Pt{sub 3}Zr(0001) and showed a structure equivalent to (111) of cubic zirconia. Following previous work, we have prepared ultra-thin zirconia by oxidation of a different alloy, Pd{sub 3}Zr(0001), which resulted in a similar structure with a slightly different lattice parameter, 351.2 ±0.4 pm. Unlike the oxide on Pt{sub 3}Zr, where Zr of the oxide binds to Pt in the substrate, here the oxide binds to substrate Zr via oxygen. This causes stronger distortion of the oxide structure, i.e. a stronger buckling of Zr in the oxide. After additional oxidation of ZrO{sub 2}/Pt{sub 3}Zr, a different ultra-thin zirconia phase is observed. A preliminary structure model for this film is based on (113)-oriented cubic zirconia. 3D oxide clusters are also present after growing ultra-thin zirconia films. They occur at the step edges, and the density is higher on Pd{sub 3}Zr. These clusters also appear on terraces after additional oxidation. XPS reveals different core level shifts of the oxide films, bulk, and oxide clusters.

Bi-epitaxial YBa2Cu3Ox Thin Films on Tilted-axes NdGaO3 Substrates with CeO2 Seeding Layer

International Nuclear Information System (INIS)

Mozhaev, P B; Mozhaeva, J E; Jacobsen, C S; Hansen, J Bindslev; Bdikin, I K; Luzanov, V A; Kotelyanskii, I M; Zybtsev, S G

2006-01-01

Bi-epitaxial YBa 2 Cu 3 O x (YBCO) thin films with out-of-plane tilt angle in the range 18 - 27 0 were manufactured using pulsed laser deposition on NdGaO 3 tilted-axes substrates with CeO 2 seeding layers. The YBCO thin film orientation over the seeding layer depended on deposition conditions. Removal of the seeding layer from part of the substrate surface by ionbeam etching resulted in formation of a bi-epitaxial thin film with different c-axis orientation of two parts of the film. The bi-epitaxial film orientation and structure were studied using X-ray diffraction techniques, and surface morphology was observed with atomic force microscope (AFM). Photolithography and ion-beam etching techniques were used for patterning bi-epitaxial thin films. Electrical characterization of the obtained structures was performed

Ion beam-based characterization of multicomponent oxide thin films and thin film layered structures

International Nuclear Information System (INIS)

Krauss, A.R.; Rangaswamy, M.; Lin, Yuping; Gruen, D.M.; Schultz, J.A.; Schmidt, H.K.; Chang, R.P.H.

1992-01-01

Fabrication of thin film layered structures of multi-component materials such as high temperature superconductors, ferroelectric and electro-optic materials, and alloy semiconductors, and the development of hybrid materials requires understanding of film growth and interface properties. For High Temperature Superconductors, the superconducting coherence length is extremely short (5--15 Angstrom), and fabrication of reliable devices will require control of film properties at extremely sharp interfaces; it will be necessary to verify the integrity of thin layers and layered structure devices over thicknesses comparable to the atomic layer spacing. Analytical techniques which probe the first 1--2 atomic layers are therefore necessary for in-situ characterization of relevant thin film growth processes. However, most surface-analytical techniques are sensitive to a region within 10--40 Angstrom of the surface and are physically incompatible with thin film deposition and are typically restricted to ultra high vacuum conditions. A review of ion beam-based analytical methods for the characterization of thin film and multi-layered thin film structures incorporating layers of multicomponent oxides is presented. Particular attention will be paid to the use of time-of-flight techniques based on the use of 1- 15 key ion beams which show potential for use as nondestructive, real-time, in-situ surface diagnostics for the growth of multicomponent metal and metal oxide thin films

Epitaxial growth and magnetic properties of ultraviolet transparent Ga2O3/(Ga1-xFex)2O3 multilayer thin films.

Science.gov (United States)

Guo, Daoyou; An, Yuehua; Cui, Wei; Zhi, Yusong; Zhao, Xiaolong; Lei, Ming; Li, Linghong; Li, Peigang; Wu, Zhenping; Tang, Weihua

2016-04-28

Multilayer thin films based on the ferromagnetic and ultraviolet transparent semiconductors may be interesting because their magnetic/electronic/photonic properties can be manipulated by the high energy photons. Herein, the Ga2O3/(Ga1-xFex)2O3 multilayer epitaxial thin films were obtained by alternating depositing of wide band gap Ga2O3 layer and Fe ultrathin layer due to inter diffusion between two layers at high temperature using the laser molecular beam epitaxy technique. The multilayer films exhibits a preferred growth orientation of crystal plane, and the crystal lattice expands as Fe replaces Ga site. Fe ions with a mixed valence of Fe(2+) and Fe(3+) are stratified distributed in the film and exhibit obvious agglomerated areas. The multilayer films only show a sharp absorption edge at about 250 nm, indicating a high transparency for ultraviolet light. What's more, the Ga2O3/(Ga1-xFex)2O3 multilayer epitaxial thin films also exhibits room temperature ferromagnetism deriving from the Fe doping Ga2O3.

Thin Films in the Photovoltaic Industry

International Nuclear Information System (INIS)

Jaeger-Waldau, A.

2008-03-01

In the past years, the yearly world market growth rate for Photovoltaics was an average of more than 40%, which makes it one of the fastest growing industries at present. Business analysts predict the market volume to increase to 40 billion euros in 2010 and expect rising profit margins and lower prices for consumers at the same time. Today PV is still dominated by wafer based Crystalline Silicon Technology as the 'working horse' in the global market, but thin films are gaining market shares. For 2007 around 12% are expected. The current silicon shortage and high demand has kept prices higher than anticipated from the learning curve experience and has widened the windows of opportunities for thin film solar modules. Current production capacity estimates for thin films vary between 3 and 6 GW in 2010, representing a 20% market share for these technologies. Despite the higher growth rates for thin film technologies compared with the industry average, Thin Film Photovoltaic Technologies are still facing a number of challenges to maintain this growth and increase market shares. The four main topics which were discussed during the workshop were: Potential for cost reduction; Standardization; Recycling; Performance over the lifetime.

Solution-processed In2S3 buffer layer for chalcopyrite thin film solar cells

OpenAIRE

Wang Lan; Lin Xianzhong; Ennaoui Ahmed; Wolf Christian; Lux-Steiner Martha Ch.; Klenk Reiner

2016-01-01

We report a route to deposit In2S3 thin films from air-stable, low-cost molecular precursor inks for Cd-free buffer layers in chalcopyrite-based thin film solar cells. Different precursor compositions and processing conditions were studied to define a reproducible and robust process. By adjusting the ink properties, this method can be applied in different printing and coating techniques. Here we report on two techniques, namely spin-coating ...

Magnetoresistance Versus Oxygen Deficiency in Epi-stabilized SrRu1 - x Fe x O3 - δ Thin Films

Science.gov (United States)

Dash, Umasankar; Acharya, Susant Kumar; Lee, Bo Wha; Jung, Chang Uk

2017-03-01

Oxygen vacancies have a profound effect on the magnetic, electronic, and transport properties of transition metal oxide materials. Here, we studied the influence of oxygen vacancies on the magnetoresistance (MR) properties of SrRu1 - x Fe x O3 - δ epitaxial thin films ( x = 0.10, 0.20, and 0.30). For this purpose, we synthesized highly strained epitaxial SrRu1 - x Fe x O3 - δ thin films with atomically flat surfaces containing different amounts of oxygen vacancies using pulsed laser deposition. Without an applied magnetic field, the films with x = 0.10 and 0.20 showed a metal-insulator transition, while the x = 0.30 thin film showed insulating behavior over the entire temperature range of 2-300 K. Both Fe doping and the concentration of oxygen vacancies had large effects on the negative MR contributions. For the low Fe doping case of x = 0.10, in which both films exhibited metallic behavior, MR was more prominent in the film with fewer oxygen vacancies or equivalently a more metallic film. For semiconducting films, higher MR was observed for more semiconducting films having more oxygen vacancies. A relatively large negative MR ( 36.4%) was observed for the x = 0.30 thin film with a high concentration of oxygen vacancies ( δ = 0.12). The obtained results were compared with MR studies for a polycrystal of (Sr1 - x La x )(Ru1 - x Fe x )O3. These results highlight the crucial role of oxygen stoichiometry in determining the magneto-transport properties in SrRu1 - x Fe x O3 - δ thin films.

Impact of symmetry on the ferroelectric properties of CaTiO{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Biegalski, Michael D.; Qiao, Liang [Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Gu, Yijia; Chen, Long-Qing [Department of Materials Science and Engineering, Pennsylvania State University, University Park, Pennsylvania 16801 (United States); Mehta, Apurva [Stanford Synchrotron Lightsource SLAC National Accelerator Laboratory, Menlo Park, California 94025 (United States); He, Qian; Borisevich, Albina [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Takamura, Yayoi, E-mail: ytakamura@ucdavis.edu [Department of Chemical Engineering and Materials Science, University of California Davis, Davis, California 95616 (United States)

2015-04-20

Epitaxial strain is a powerful tool to induce functional properties such as ferroelectricity in thin films of materials that do not possess ferroelectricity in bulk form. In this work, a ferroelectric state was stabilized in thin films of the incipient ferroelectric, CaTiO{sub 3}, through the careful control of the biaxial strain state and TiO{sub 6} octahedral rotations. Detailed structural characterization was carried out by synchrotron x-ray diffraction and scanning transmission electron microscopy. CaTiO{sub 3} films grown on La{sub 0.18}Sr{sub 0.82}Al{sub 0.59}Ta{sub 0.41}O{sub 3} (LSAT) and NdGaO{sub 3} (NGO) substrates experienced a 1.1% biaxial strain state but differed in their octahedral tilt structures. A suppression of the out-of-plane rotations of the TiO{sub 6} octahedral in films grown on LSAT substrates resulted in a robust ferroelectric I4 mm phase with remnant polarization ∼5 μC/cm{sup 2} at 10 K and T{sub c} near 140 K. In contrast, films grown on NGO substrates with significant octahedral tilting showed reduced polarization and T{sub c}. These results highlight the key role played by symmetry in controlling the ferroelectric properties of perovskite oxide thin films.

Silicon-integrated thin-film structure for electro-optic applications

Science.gov (United States)

McKee, Rodney A.; Walker, Frederick Joseph

2000-01-01

A crystalline thin-film structure suited for use in any of an number of electro-optic applications, such as a phase modulator or a component of an interferometer, includes a semiconductor substrate of silicon and a ferroelectric, optically-clear thin film of the perovskite BaTiO.sub.3 overlying the surface of the silicon substrate. The BaTiO.sub.3 thin film is characterized in that substantially all of the dipole moments associated with the ferroelectric film are arranged substantially parallel to the surface of the substrate to enhance the electro-optic qualities of the film.

Synthesis and characterization of multilayered BaTiO3/NiFe2O4 thin films

Directory of Open Access Journals (Sweden)

Branimir Bajac

2013-03-01

Full Text Available Presented research was focused on the fabrication of multiferroic thin film structures, composed of ferrielectric barium titanate perovskite phase and magnetostrictive nickel ferrite spinel phase. The applicability of different, solution based, deposition techniques (film growth from solution, dip coating and spin coating for thefabrication of multilayered BaTiO3 /NiFe2O4 thin films was investigated. It was shown that only spin coating produces films of desired nanostructure, thickness and smooth and crackfree surfaces.

Catalytic EC′ reaction at a thin film modified electrode

International Nuclear Information System (INIS)

Gerbino, Leandro; Baruzzi, Ana M.; Iglesias, Rodrigo A.

2013-01-01

Numerical simulations of cyclic voltammograms corresponding to a catalytic EC′ reaction taking place at a thin film modified electrode are performed by way of finite difference method. Besides considering the chemical kinetic occurring inside the thin film, the model takes into account the different diffusion coefficients for each species at each of the involved phases, i.e. the thin film layer and bulk solution. The theoretical formulation is given in terms of dimensionless model parameters but a brief discussion of each of these parameters and their relationship to experimental variables is presented. Special emphasis is given to the use of working curve characteristics to quantify diffusion coefficient, homogeneous kinetic constant and thickness of the thin layer in a real system. Validation of the model is made by comparison of experimental results corresponding to the electron charge transfer of Ru(NH 3 ) 6 3+ /Ru(NH 3 ) 6 2+ hemi-couple at a thin film of a cross-linked chitosan film containing an immobilized redox dye

Nanometric thin film membranes manufactured on square meter scale: ultra-thin films for CO 2 capture

KAUST Repository

Yave, Wilfredo

2010-09-01

Miniaturization and manipulation of materials at nanometer scale are key challenges in nanoscience and nanotechnology. In membrane science and technology, the fabrication of ultra-thin polymer films (defect-free) on square meter scale with uniform thickness (<100 nm) is crucial. By using a tailor-made polymer and by controlling the nanofabrication conditions, we developed and manufactured defect-free ultra-thin film membranes with unmatched carbon dioxide permeances, i.e. >5 m3 (STP) m-2 h -1 bar-1. The permeances are extremely high, because the membranes are made from a CO2 philic polymer material and they are only a few tens of nanometers thin. Thus, these thin film membranes have potential application in the treatment of large gas streams under low pressure like, e.g., carbon dioxide separation from flue gas. © 2010 IOP Publishing Ltd.

Microstructure of epitaxial SrRuO 3 thin films on MgO substrates

Science.gov (United States)

Ai, Wan Yong; Zhu, Jun; Zhang, Ying; Li, Yan Rong; Liu, Xing Zhao; Wei, Xian Hua; Li, Jin Long; Zheng, Liang; Qin, Wen Feng; Liang, Zhu

2006-09-01

SrRuO 3 thin films have been grown on singular (1 0 0) MgO substrates using pulsed laser deposition (PLD) in 30 Pa oxygen ambient and at a temperature of 400-700 °C. Ex situ reflection high-energy electron diffraction (RHEED) as well as X-ray diffraction (XRD) θ/2 θ scan indicated that the films deposited above 650 °C were well crystallized though they had a rough surface as shown by atom force microscopy (AFM). XRD Φ scans revealed that these films were composed of all three different types of orientation domains, which was further confirmed by the RHEED patterns. The heteroepitaxial relationship between SrRuO 3 and MgO was found to be [1 1 0] SRO//[1 0 0] MgO and 45°-rotated cube-on-cube [0 0 1] SRO//[1 0 0] MgO. These domain structures and surface morphology are similar to that of ever-reported SrRuO 3 thin films deposited on the (0 0 1) LaAlO 3 substrates, and different from those deposited on (0 0 1) SrTiO 3 substrates that have an atomically flat surface and are composed of only the [1 1 0]-type domains. The reason for this difference was ascribed to the effect of lattice mismatch across the film/substrate interface. The room temperature resistivity of SrRuO 3 films fabricated at 700 °C was 300 μΩ cm. Therefore, epitaxial SrRuO 3 films on MgO substrate could serve as a promising candidate of electrode materials for the fabrication of ferroelectric or dielectric films.

Optical response of Cu3Ge thin films

OpenAIRE

Aboelfotoh, M. O.; Guizzetti, G.; Marabelli, F.; Pellegrino, Paolo; Sassella, A.

1996-01-01

We report an investigation on the optical properties of Cu3Ge thin films displaying very high conductivity, with thickness ranging from 200 to 2000 Å, deposited on Ge substrates. Reflectance, transmittance, and ellipsometric spectroscopy measurements were performed at room temperature in the 0.01-6.0, 0.01-0.6, and 1.4-5.0 eV energy range, respectively. The complex dielectric function, the optical conductivity, the energy-loss function, and the effective charge density were obtained over the ...

Structure and electrical properties of Pb(ZrxTi1-x)O3 deposited on textured Pt thin films

International Nuclear Information System (INIS)

Hong, Jongin; Song, Han Wook; Lee, Hee Chul; Lee, Won Jong; No, Kwangsoo

2001-01-01

The texturing of the bottom electrode plays a key role in the structure and electrical properties of Pb(Zr,Ti)O 3 (PZT) thin films. We fabricated Pt bottom electrodes having a different thickness on MgO single crystals at 600 o C by rf magnetron sputtering. As the thickness of platinum (Pt) thin film increased, the preferred orientation of Pt thin film changed from (200) to (111). PZT thin films were fabricated at 450 o C by electron cyclotron resonance-plasma enhanced metal organic chemical vapor deposition on the textured Pt thin films. The texturing of the bottom electrode caused drastic changes in the C--V characteristics, P--E characteristics, and fatigue characteristics of metal/ferroelectric material/metal (MFM) capacitors. The difference of the electrical properties between the PZT thin films having different texturing was discussed in terms-of the x--y alignment and the interface between electrode and PZT in MFM capacitors. copyright 2001 American Institute of Physics

Processing and properties of Pb(Mg(1/3)Nb(2/3))O3--PbTiO3 thin films by pulsed laser deposition

Science.gov (United States)

Tantigate, C.; Lee, J.; Safari, A.

1995-03-01

The objectives of this study were to prepare in situ Pb(Mg(1/3)Nb(2/3))O3 (PMN) and PMN-PT thin films by pulsed laser deposition and to investigate the electrical features of thin films for possible dynamic random access memory (DRAM) and microactuator applications. The impact of processing parameters such compositions, substrate temperature, and oxygen pressure on perovskite phase formation and dielectric characteristics were reported. It was found that the highest dielectric constant, measured at room temperature and 10 kHz, was attained from the PMN with 99% perovskite.

Metalorganic chemical vapor deposition of Er{sub 2}O{sub 3} thin films: Correlation between growth process and film properties

Energy Technology Data Exchange (ETDEWEB)

Giangregorio, Maria M. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM sez. Bari, Via Orabona 4, 70125 Bari (Italy)], E-mail: michelaria.giangregorio@ba.imip.cnr.it; Losurdo, Maria; Sacchetti, Alberto; Capezzuto, Pio; Bruno, Giovanni [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM sez. Bari, Via Orabona 4, 70125 Bari (Italy)

2009-02-27

Er{sub 2}O{sub 3} thin films have been grown by metalorganic chemical vapor deposition (MOCVD) at 600 deg. C on different substrates, including glass, Si (100) and sapphire (0001) using tris(isopropylcyclopentadienyl)erbium and O{sub 2}. The effects of growth parameters such as the substrate, the O{sub 2} plasma activation and the temperature of organometallic precursor injection, on the nucleation/growth kinetics and, consequently, on film properties have been investigated. Specifically, very smooth (111)-oriented Er{sub 2}O{sub 3} thin films (the root mean square roughness is 0.3 nm) are achieved on Si (100), {alpha}-Al{sub 2}O{sub 3} (0001) and amorphous glass by MOCVD. Growth under O{sub 2} remote plasma activation results in an increase in growth rate and in (100)-oriented Er{sub 2}O{sub 3} films with high refractive index and transparency in the visible photon energy range.

Physical properties of chemically deposited Bi{sub 2}S{sub 3} thin films using two post-deposition treatments

Energy Technology Data Exchange (ETDEWEB)

Moreno-García, H., E-mail: hamog@ier.unam.mx [Instituto de Ciencias Físicas, Laboratorio de espectroscopia, Universidad Nacional Autónoma de México, Apartado Postal 48-3, C.P. 62210 Cuernavaca, Morelos (Mexico); Messina, S. [Universidad Autónoma de Nayarit, Ciudad de la Cultura “Amado Nervo” S/N, C.P. 63155 Tepic, Nayarit (Mexico); Calixto-Rodriguez, M. [Universidad Tecnológica Emiliano Zapata del Estado de Morelos, Av. Universidad Tecnológica No. 1, C.P. 62760 Emiliano Zapata, Morelos (Mexico); Martínez, H. [Instituto de Ciencias Físicas, Laboratorio de espectroscopia, Universidad Nacional Autónoma de México, Apartado Postal 48-3, C.P. 62210 Cuernavaca, Morelos (Mexico)

2014-08-30

Highlights: • The post-deposition treatment by Ar plasma is a viable alternative to enhance the optical, electrical, morphological and structural properties of Bi{sub 2}S{sub 3} semiconductor thin films. • The plasma treatment avoids the loss in thickness of the chemically deposited Bi{sub 2}S{sub 3} thin films. • The E{sub g} values were 1.60 eV for the thermally annealed samples and 1.56 eV for the Ar plasma treated samples. • The highest value obtained for the electrical conductivity was 7.7 × 10{sup −2} (Ω cm){sup −1} in plasma treated samples. - Abstract: As-deposited bismuth sulfide (Bi{sub 2}S{sub 3}) thin films prepared by chemical bath deposition technique were treated with thermal annealed in air atmosphere and argon AC plasma. The as-deposited, thermally annealing and plasma treatment Bi{sub 2}S{sub 3} thin films have been characterized by X-ray diffraction (XRD) analysis, atomic force microscopy analysis (AFM), transmission, specular reflectance and electrical measurements. The structural, morphological, optical and electrical properties of the films are compared. The XRD analysis showed that both post-deposition treatments, transform the thin films from amorphous to a crystalline phase. The atomic force microscopy (AFM) measurement showed a reduction of roughness for the films treated in plasma. The energy band gap value of the as-prepared film was E{sub g} = 1.61 eV, while for the film thermally annealed was E{sub g} = 1.60 eV and E{sub g} = 1.56 eV for film treated with Plasma. The electrical conductivity under illumination of the as-prepared films was 3.6 × 10{sup −5} (Ω cm){sup −1}, whereas the conductivity value for the thermally annealed films was 2.0 × 10{sup −3} (Ω cm){sup −1} and for the plasma treated films the electrical conductivity increases up to 7.7 × 10{sup −2} (Ω cm){sup −1}.

Oxygen tracer studies of ferroelectric fatigue in Pb(Zr,Ti)O3 thin films

International Nuclear Information System (INIS)

Schloss, Lawrence F.; McIntyre, Paul C.; Hendrix, Bryan C.; Bilodeau, Steven M.; Roeder, Jeffrey F.; Gilbert, Stephen R.

2002-01-01

Long-range oxygen motion has been observed in Pt/Pb(Zr,Ti)O 3 /Ir thin-film structures after electrical fatigue cycling at room temperature. Through an exchange anneal, isotopic 18 O was incorporated as a tracer into bare Pb(Zr,Ti)O 3 (PZT) films, allowing secondary ion mass spectrometry measurements of the tracer profile evolution as a function of the number of polarization reversals. Observation of 18 O tracer redistribution during voltage cycling, which is presumably mediated by oxygen vacancy motion, was found to be strongly dependent upon the thermal history of the film. However, there was no strong correlation between the extent of 18 O tracer redistribution and the extent of polarization suppression induced by voltage cycling. Our results suggest that oxygen vacancy motion plays, at most, a secondary role in ferroelectric fatigue of PZT thin films

Growth of amorphous TeOx (2≤x≤3) thin film by radio frequency sputtering

International Nuclear Information System (INIS)

Dewan, Namrata; Gupta, Vinay; Sreenivas, K.; Katiyar, R. S.

2007-01-01

Thin films of Tellurium oxide TeO x over a wide range of x (2 to 3) were prepared by radio frequency diode sputtering at room temperature on corning glass and quartz substrate. The deposited films are amorphous in nature and IR spectroscopy reveals the formation of Te-O bond. X-ray photoelectron spectroscopy shows the variation in the stoichiometry of TeO x film from x=2 to 3 with an increase in oxygen percentage (25 to 100%) in processing sputtering gas composition. Raman spectroscopy depicts the formation of TeO 3 trigonal pyramid besides TeO 4 disphenoid in the amorphous TeO x film with increase in the value of x. The varying stoichiometry of TeO x thin film (x=2 to 3) was found to influence the optical, electrical, and elastic properties. The optical band gap of film increases from 3.8 to 4.2 eV with increasing x and is attributed to the decrease in density. The elastic constants (C 11 and C 44 ) of the deposited films are lower than the corresponding value reported for TeO 2 single crystal

Ferroelectric properties of NaNbO3-BaTiO3 thin films deposited on SrRuO3/(001)SrTiO3 substrate by pulsed laser deposition

International Nuclear Information System (INIS)

Yamazoe, Seiji; Oda, Shinya; Sakurai, Hiroyuki; Wada, Takahiro; Adachi, Hideaki

2009-01-01

(NaNbO 3 ) 1-x (BaTiO 3 ) x (NN-xBT) thin films with low BaTiO 3 (BT) concentrations x (x=0.05 and 0.10) were fabricated on SrRuO 3 /(001)SrTiO 3 (SRO)/(001)STO) substrate by pulsed laser deposition (PLD). X-ray diffraction pattern (XRD) and transmission electron diffraction pattern (TED) showed that NN-0.10BT thin film was epitaxially grown on SRO/(001)STO substrate with a crystallographic relationship of [001] NN-xBT parallel [001] STO . From reciprocal space maps, the lattice parameters of the out-of-plane direction of NN-xBT thin films became larger with an increase in BT concentration, although the lattice parameter of the in-plane was hardly changed by the BT concentration. The value of relative dielectric constant ε r of the NN-xBT thin films were increased with BT concentration. The ε r and the dielectric loss tanδ of NN-0.10BT were 1220 and 0.02 at 1 kHz, respectively. The P-E hysteresis loops of the NN-xBT thin films showed clear ferroelectricity. Although the value of remanent polarization P r decreased with the BT concentration, the behaviors of ε r , P r , and coercive electric field E c of the NN-xBT thin films against the BT concentration accorded with those of NN-xBT ceramics, in which NN-0.10BT ceramics exhibited the largest piezoelectric property. Therefore, the NN-0.10BT thin film is expected to show high piezoelectricity. (author)

Gasochromic performance of WO{sub 3}-nanorod thin films fabricated with an ArF excimer laser

Energy Technology Data Exchange (ETDEWEB)

Yaacob, M. H. [RMIT University, Melbourne (Australia); Universiti Putra Malaysia, Selangor (Malaysia); Ou, J. Z.; Wlodarski, W. [RMIT University, Melbourne (Australia); Kim, C. S.; Lee, J. Y. [KAIST, Daejon (Korea, Republic of); Kim, Y. H. [KIST, Seoul (Korea, Republic of); Oh, C. M.; Dhakal, K. P.; Kim, J. Y.; Kang, J. H. [University of Incheon, Incheon (Korea, Republic of)

2012-02-15

Thin films with tungsten trioxide (WO{sub 3}) nanorods were fabricated by using an ArF pulsed laser deposition system. Because the ArF excimer laser operates at a very short wavelength of 193 nm, short enough to expect strong absorption of the photons in the semiconductor oxide targets, and because the clusters incoming to the substrates have high momentum, we could build thin films with good surface morphology. Highly homogeneous arrays of nanorods with sizes mostly in the range of 30 - 40 nm were observed. The absorbance response towards hydrogen (H{sub 2}) gas was investigated for a WO{sub 3} film coated with 25-A-thick palladium (Pd). The Pd/WO{sub 3}-nanorod thin films exhibited excellent gasochromic response when measured in the visible-NIR range (400 - 1000 nm). As low as 0.06% H{sub 2} concentration was clearly sensed. A significant reversible absorbance change and fast recovery (<2 min) were observed when the films were exposed to H{sub 2} at different concentrations.

P-type CuxS thin films: Integration in a thin film transistor structure

International Nuclear Information System (INIS)

Nunes de Carvalho, C.; Parreira, P.; Lavareda, G.; Brogueira, P.; Amaral, A.

2013-01-01

Cu x S thin films, 80 nm thick, are deposited by vacuum thermal evaporation of sulfur-rich powder mixture, Cu 2 S:S (50:50 wt.%) with no intentional heating of the substrate. The process of deposition occurs at very low deposition rates (0.1–0.3 nm/s) to avoid the formation of Cu or S-rich films. The evolution of Cu x S films surface properties (morphology/roughness) under post deposition mild annealing in air at 270 °C and their integration in a thin film transistor (TFT) are the main objectives of this study. Accordingly, Scanning Electron Microscopy studies show Cu x S films with different surface morphologies, depending on the post deposition annealing conditions. For the shortest annealing time, the Cu x S films look to be constructed of grains with large dimension at the surface (approximately 100 nm) and consequently, irregular shape. For the longest annealing time, films with a fine-grained surface are found, with some randomly distributed large particles bound to this fine-grained surface. Atomic Force Microscopy results indicate an increase of the root-mean-square roughness of Cu x S surface with annealing time, from 13.6 up to 37.4 nm, for 255 and 345 s, respectively. The preliminary integration of Cu x S films in a TFT bottom-gate type structure allowed the study of the feasibility and compatibility of this material with the remaining stages of a TFT fabrication as well as the determination of the p-type characteristic of the Cu x S material. - Highlights: • Surface properties of annealed Cu x S films. • Variation of conductivity with annealing temperatures of Cu x S films. • Application of evaporated Cu x S films in a thin film transistor (TFT) structure. • Determination of Cu x S p-type characteristic from TFT behaviour

Pulsed Laser deposition of Al2O3 thin film on silicon

International Nuclear Information System (INIS)

Lamagna, A.; Duhalde, S.; Correra, L.; Nicoletti, S.

1998-01-01

Al 2 O 3 thin films were fabricated by pulsed laser deposition (PLD) on Si 3 N 4 /Si, to improve the thermal and electrical isolation of gas sensing devices. The microstructure of the films is analysed as a function of the deposition conditions (laser fluence, oxygen pressure, target-substrate distance and substrate temperature). X-ray analysis shows that only a sharp peak that coincides with the corundum (116) reflection can be observed in all the films. But, when they are annealed at temperatures above 1,200 degree centigrade, a change in the crystalline structure of some films occurs. The stoichiometry and morphology of the films with and without thermal treatment are compared using environmental scanning electron microscopy (SEM) and EDAX analysis. (Author) 14 refs

Mechanism of Crystallization and Implications for Charge Transport in Poly(3-ethylhexylthiophene) Thin Films

KAUST Repository

Duong, Duc T.; Ho, Victor; Shang, Zhengrong; Mollinger, Sonya; Mannsfeld, Stefan C.B.; Dacuñ a, Javier; Toney, Michael F.; Segalman, Rachel; Salleo, Alberto

2014-01-01

on the film thickness and average molecular weight. Time-dependent, field-effect hole mobilities in thin films reveal a percolation threshold for both low and high molecular weight P3EHT. Structural analysis reveals that charge percolation requires bridged

Persistent semi-metal-like nature of epitaxial perovskite CaIrO3 thin films

International Nuclear Information System (INIS)

Biswas, Abhijit; Jeong, Yoon Hee

2015-01-01

Strong spin-orbit coupled 5d transition metal based ABO 3 oxides, especially iridates, allow tuning parameters in the phase diagram and may demonstrate important functionalities, for example, by means of strain effects and symmetry-breaking, because of the interplay between the Coulomb interactions and strong spin-orbit coupling. Here, we have epitaxially stabilized high quality thin films of perovskite (Pv) CaIrO 3 . Film on the best lattice-matched substrate shows semi-metal-like characteristics. Intriguingly, imposing tensile or compressive strain on the film by altering the underlying lattice-mismatched substrates still maintains semi-metallicity with minute modification of the effective correlation as tensile (compressive) strain results in tiny increases (decreases) of the electronic bandwidth. In addition, magnetoresistance remains positive with a quadratic field dependence. This persistent semi-metal-like nature of Pv-CaIrO 3 thin films with minute changes in the effective correlation by strain may provide new wisdom into strong spin-orbit coupled 5d based oxide physics

Chemical solution deposition of CaCu 3 Ti 4 O 12 thin film

Indian Academy of Sciences (India)

CaCu3Ti4O12 (CCTO) thin film was successfully deposited on boron doped silica substrate by chemical solution deposition and rapid thermal processing. The phase and microstructure of the deposited films were studied as a function of sintering temperature, employing X-ray diffractometry and scanning electron ...

Highly polarized single-c-domain single-crystal Pb(Mn,Nb)O(3)-PZT thin films.

Science.gov (United States)

Wasa, Kiyotaka; Adachi, Hideaki; Nishida, Ken; Yamamoto, Takashi; Matsushima, Tomoaki; Kanno, Isaku; Kotera, Hidetoshi

2012-01-01

In-plane unstrained single-c-domain/single-crystal thin films of PZT-based ternary ferroelectric perovskite, ξPb(Mn,Nb)O3-(1 - ξ)PZT, were grown on SrRuO(3)/Pt/MgO substrates using magnetron sputtering followed by quenching. The sputtered unstrained thin films exhibit unique ferroelectric properties: high coercive field, Ec > 180 kV/cm, large remanent polarization, P(r) = 100 μC/cm(2), small relative dielectric constants, ε* = 100 to 150, high Curie temperature, Tc = ~600 °C, and bulk-like large transverse piezoelectric constants, e31,f = -12.0 C/m(2) for PZT(48/52) at ξ = 0.06. The unstrained thin films are an ideal structure to extract the bulk ferroelectric properties. Their micro-structures and ferroelectric properties are discussed in relation to the potential applications for piezoelectric MEMS. © 2012 IEEE

DC magnetron sputtering prepared Ag-C thin film anode for thin film lithium ion microbatteries

International Nuclear Information System (INIS)

Li, Y.; Tu, J.P.; Shi, D.Q.; Huang, X.H.; Wu, H.M.; Yuan, Y.F.; Zhao, X.B.

2007-01-01

An Ag-C thin film was prepared by DC magnetron co-sputtering, using pure silver and graphite as the targets. The microstructure and morphology of the deposited thin film were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Electrochemical performances of the Ag-C thin film anode were investigated by means of discharge/charge and cyclic voltammogram (CV) tests in model cells. The electrochemical impedance spectrum (EIS) characteristics and the chemical diffusion coefficient, D Li of the Ag-C thin film electrode at different discharging states were discussed. It was believed that the excellent cycling performance of the Ag-C electrode was ascribed to the good conductivity of silver and the volume stability of the thin film

Preparation of planar CH3NH3PbI3 thin films with controlled size using 1-ethyl-2-pyrrolidone as solvent

International Nuclear Information System (INIS)

Hao, Qiuyan; Chu, Yixia; Zheng, Xuerong; Liu, Zhenya; Liang, Liming; Qi, Jiakun; Zhang, Xin; Liu, Gang; Liu, Hui; Chen, Hongjian; Liu, Caichi

2016-01-01

Recently, planar perovskite solar cells based on CH 3 NH 3 PbI 3 have attracted many researcher's interest due to their unique advantages such as simple cell architecture, easy fabrication and potential multijunction construction comparing to the initial mesoporous structure. However, the preparation of planar perovskite films with high quality is still in challenge. In this paper, we developed a vapor-assisted solution process using a novel and green solvent of 1-Ethyl-2-pyrrolidone (NEP) instead of the traditional N, N-dimethylformamide (DMF) to construct a high-quality perovskite CH 3 NH 3 PbI 3 thin film with pure phase, high compactness, small surface roughness and controlled size. The phase evolution and growth mechanism of the perovskite films are also discussed. Utilizing the NEP of low volatility and moderate boiling point as solvent, we dried the PbI 2 -NEP precursor films at different temperature under vacuum and then obtained PbI 2 thin films with different crystalline degree from amorphous to highly crystalline. The perovskite films with crystal size ranged from hundreds of nanometers to several micrometers can be prepared by reacting the PbI 2 films of different crystalline degree with CH 3 NH 3 I vapor. Moreover, planar-structured solar cells combining the perovskite film with TiO 2 and spiro-OMeTAD as the electron and holes transporting layer achieves a power conversion efficiency of 10.2%. - Highlights: • A novel and green solvent of 1-Ethyl-2-pyrrolidone (NEP) was used to construct high-quality perovskite CH 3 NH 3 PbI 3 thin film. • The CH 3 NH 3 PbI 3 grain with different sizes ranged from hundreds of nanometers to several micrometers can be obtained. • Planar-structured perovskite CH 3 NH 3 PbI 3 solar cells using NEP as solvent achieves a power conversion efficiency of 10.2%.

Electrical transport properties of MoO3 thin films prepared by laser assisted evaporation

International Nuclear Information System (INIS)

Lopez-Carreno, L.D.; Pardo, A.; Zuluaga, M.; Torres, J.; Alfonso, J.E.; Cortes-Bracho, O.L.

2007-01-01

In the present paper the growth of MoO 3 thin films on common glass substrates are described. The films were prepared by evaporation of a MoO 3 target with a CO 2 laser (10.6 μm), operating in the continuous wave mode. The effect of substrate temperature on the crystallographic structure and electrical properties of MoO 3 thin films was studied. The chemical composition of the different species formed on the films surface was obtained by X-ray photoelectron spectroscopy (XPS) and the crystalline structure was studied with X-ray diffraction (XRD). The electrical conductivity of the films was determined using the standard four-points method. Conductivity of the films varied from de 10 -9 to 10 -5 (Ωcm) -1 in the 300-600 K temperature range. Arrhenius-type plots for the electrical conductivity indicate the presence of at least two different conduction mechanisms. The I-V characteristic curve shows an ohmic behavior only in the 4.5-60 V range. Outside this interval the I-V curve has a behavior described by a power law. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Temperature studies of optical parameters of (Ag3AsS3)0.6(As2S3)0.4 thin films prepared by rapid thermal evaporation and pulse laser deposition

Science.gov (United States)

Studenyak, I. P.; Kutsyk, M. M.; Buchuk, M. Yu.; Rati, Y. Y.; Neimet, Yu. Yu.; Izai, V. Yu.; Kökényesi, S.; Nemec, P.

2016-02-01

(Ag3AsS3)0.6(As2S3)0.4 thin films were deposited using rapid thermal evaporation (RTE) and pulse laser deposition (PLD) techniques. Ag-enriched micrometre-sized cones (RTE) and bubbles (PLD) were observed on the thin film surface. Optical transmission spectra of the thin films were studied in the temperature range 77-300 K. The Urbach behaviour of the optical absorption edge in the thin films due to strong electron-phonon interaction was observed, the main parameters of the Urbach absorption edge were determined. Temperature dependences of the energy position of the exponential absorption edge and the Urbach energy are well described in the Einstein model. Dispersion and temperature dependences of refractive indices were analysed; a non-linear increase of the refractive indices with temperature was revealed. Disordering processes in the thin films were studied and compared with bulk composites, the differences between the thin films prepared by RTE and PLD were analysed.

Modeling flux pinning in thin undoped and BazRo3-doped YBCO films

DEFF Research Database (Denmark)

Paturi, P.; Irjala, M.; Huhtinen, H.

2009-01-01

A simple model based on distributions of twin boundaries, dislocations, and BaZrO3 nanorods is presented to describe the Jc properties of undoped and BaZrO3 (BZO)-doped YBa2Cu3Ox thin films. The model accurately describes the shape of Jc(B,T) curves of the films, when the pinning site distributions...... are taken from distributions of twin spacings and BZO nanorods from transmission electron microscope images. Thus, assuming that the model can be used for prediction of the Jc properties, we conclude that for enhancement of undoped films more crystalline defects are needed and for doped films a dopant...

Co-sputtered ZnO:Si thin films as transparent conductive oxides

Energy Technology Data Exchange (ETDEWEB)

Faure, C. [CNRS, Univ. Bordeaux, ICMCB, UPR 9048, F33600 Pessac (France); Clatot, J. [LRCS, 33 Rue St Leu, F-80039 Amiens (France); Teule-Gay, L.; Campet, G. [CNRS, Univ. Bordeaux, ICMCB, UPR 9048, F33600 Pessac (France); Labrugere, C. [CeCaMA, Universite de Bordeaux, ICMCB, 87 avenue du Dr. A. Schweitzer, Pessac, F-33608 (France); Nistor, M. [National Institute for Lasers, Plasmas and Radiation Physics, L22, PO Box MG-36, 77125 Bucharest-Magurele (Romania); Rougier, A., E-mail: rougier@icmcb-bordeaux.cnrs.fr [CNRS, Univ. Bordeaux, ICMCB, UPR 9048, F33600 Pessac (France)

2012-12-01

Silicon doped Zinc Oxide thin films, so-called SZO, were deposited at room temperature on glass and plastic substrates by co-sputtering of ZnO and SiO{sub 2} targets. The influence of the SiO{sub 2} target power supply (from 30 to 75 W) on the SZO thin film composition and crystallinity is discussed. Si/Zn atomic ratio, determined by X-ray microprobe, increases from 1.2 to 8.2 at.%. For Si/Zn ratio equal and lower than 3.9%, SZO (S{sub 3.9}ZO) thin films exhibit the Wurzite structure with the (0 0 2) preferred orientation. Larger Si content leads to a decrease in crystallinity. With Si addition, the resistivity decreases down to 3.5 Multiplication-Sign 10{sup -3} Ohm-Sign {center_dot}cm for SZO thin film containing 3.9 at.% of Si prior to an increase. The mean transmittance of S{sub 3.9}ZO thin film on glass substrate approaches 80% (it is about 90% for the film itself) in the visible range (from 400 to 750 nm). Co-sputtered SZO thin films are suitable candidates for large area transparent conductive oxides. - Highlights: Black-Right-Pointing-Pointer Si doped ZnO thin films by co-sputtering of ZnO and SiO{sub 2} targets. Black-Right-Pointing-Pointer Minimum of resistivity for Si doped ZnO thin films containing 3.9% of Si. Black-Right-Pointing-Pointer Si and O environments by X-ray Photoelectron Spectroscopy.

Magnetron sputtered Cu{sub 3}N/NiTiCu shape memory thin film heterostructures for MEMS applications

Energy Technology Data Exchange (ETDEWEB)

Kaur, Navjot; Choudhary, Nitin [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India); Goyal, Rajendra N. [Indian Institute of Technology, Roorkee, Department of Chemistry (India); Viladkar, S. [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India); Matai, I.; Gopinath, P. [Indian Institute of Technology, Roorkee, Centre for Nanotechnology (India); Chockalingam, S. [Indian Institute of Technology, Guwahati, Department of Biotechnology (India); Kaur, Davinder, E-mail: dkaurfph@iitr.ernet.in [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India)

2013-03-15

In the present study, for the first time, Cu{sub 3}N/NiTiCu/Si heterostructures were successfully grown using magnetron sputtering technique. Nanocrystalline copper nitride (Cu{sub 3}N with thickness {approx}200 nm) thin films and copper nanodots were subsequently deposited on the surface of 2-{mu}m-thick NiTiCu shape memory thin films in order to improve the surface corrosion and nickel release properties of NiTiCu thin films. Interestingly, the phase transformation from martensite phase to austenite phase has been observed in Cu{sub 3}N/NiTiCu heterostructures with corresponding change in texture and surface morphology of top Cu{sub 3}N films. Field emission scanning electron microscopy and atomic force microscope images of the heterostructures reveals the formation of 20-nm-sized copper nanodots on NiTiCu surface at higher deposition temperature (450 Degree-Sign C) of Cu{sub 3}N. Cu{sub 3}N passivated NiTiCu films possess low corrosion current density with higher corrosion potential and, therefore, better corrosion resistance as compared to pure NiTiCu films. The concentration of Ni released from the Cu{sub 3}N/NiTiCu samples was observed to be much less than that of pure NiTiCu film. It can be reduced to the factor of about one-ninth after the surface passivation resulting in smooth, homogeneous and highly corrosion resistant surface. The antibacterial and cytotoxicity of pure and Cu{sub 3}N coated NiTiCu thin films were investigated through green fluorescent protein expressing E. coli bacteria and human embryonic kidney cells. The results show the strong antibacterial property and non cytotoxicity of Cu{sub 3}N/NiTiCu heterostructure. This work is of immense technological importance due to variety of BioMEMS applications.

Thickness-dependent piezoelectric behaviour and dielectric properties of lanthanum modified BiFeO3 thin films

Directory of Open Access Journals (Sweden)

Glenda Biasotto

2011-03-01

Full Text Available Bi0.85La0.15FeO3 (BLFO thin films were deposited on Pt(111/Ti/SiO2 /Si substrates by the soft chemical method. Films with thicknesses ranging from 140 to 280 nm were grown on platinum coated silicon substrates at 500°C for 2 hours. The X-ray diffraction analysis of BLFO films evidenced a hexagonal structure over the entire thickness range investigated. The grain size of the film changes as the number of the layers increases, indicating thickness dependence. It is found that the piezoelectric response is strongly influenced by the film thickness. It is shown that the properties of BiFeO3 thin films, such as lattice parameter, dielectric permittivity, piezoeletric coefficient etc., are functions of misfit strains.

Investigation of growth, structural and electronic properties of V{sub 2}O{sub 3} thin films on selected substrates

Energy Technology Data Exchange (ETDEWEB)

Nateprov, Alexei

2006-08-15

The present work is devoted to the experimental study of the MI transition in V{sub 2}O{sub 3} thin films, grown on different substrates. The main goal of the work was to develop a technology of growth of V{sub 2}O{sub 3} thin films on substrates with different electrical and structural properties (diamond and LiNbO{sub 3}), designed for specific applications. The structural and electrical properties of the obtained films were characterized in detail with a special focus on their potential applications. The MIT of V{sub 2}O{sub 3} was investigated by SAW using first directly deposited V{sub 2}O{sub 3} thin film onto a LiNbO{sub 3} substrate. (orig.)

Study on the Preparation and Properties of Colored Iron Oxide Thin Films

International Nuclear Information System (INIS)

Zhao Xianhui; Li Changhong; Liu Qiuping; He Junjing; Wang Hai; Liang Song; Duan Yandong; Liu Su

2013-01-01

Colored iron oxide thin films were prepared using Sol-gel technique. The raw materials were tetraethyl orthosilicate (TEOS), etoh ehanol (EtOH), iron nitrate, and de-ionized water. Various properties were measured and analysed, including the colour of thin films, surface topography, UV-Visible spectra, corrosion resistance and hydrophobicity. To understand how these properties influenced the structural and optical properties of Fe 2 O 3 thin films, Scanning Electron Microscope (SEM), UV Spectrophotometer and other facilities were employed. Many parameters influence the performance of thin films, such as film layers, added H 2 O content, and the amount of polydimethylsiloxane (PDMS). When the volume ratio of TEOS, EtOH and H 2 O was 15: 13: 1, the quality of Fe(NO 3 ) 3 ·9H 2 O was 6g, and pH value was 3, reddish and uniform Fe 2 O 3 thin films with excellent properties were produced. Obtained thin films possessed corrosion resistance in hydrochloric acid with pH=l and the absorption edge wavelength was ∼350.2nm. Different H 2 O contents could result in different morphologies of Fe 2 O 3 nanoparticles. When 1.5 ml PDMS was added into the Sol, thin films possessed hydrophobiliry without dropping. Coating with different layers, thin films appeared different morphologies. Meanwhile, with the increment of film layers, the absorbance increased gradually.

Growth and magnetic properties of multiferroic LaxBi1-xMnO3 thin films

Science.gov (United States)

Gajek, M.; Bibes, M.; Wyczisk, F.; Varela, M.; Fontcuberta, J.; Barthélémy, A.

2007-05-01

A comparative study of LaxBi1-xMnO3 thin films grown on SrTiO3 substrates is reported. It is shown that these films grow epitaxially in a narrow pressure-temperature range. A detailed structural and compositional characterization of the films is performed within the growth window. The structure and the magnetization of this system are investigated. We find a clear correlation between the magnetization and the unit-cell volume that we ascribe to Bi deficiency and the resultant introduction of a mixed valence on the Mn ions. On these grounds, we show that the reduced magnetization of LaxBi1-xMnO3 thin films compared to the bulk can be explained quantitatively by a simple model, taking into account the deviation from nominal composition and the Goodenough-Kanamori-Anderson rules of magnetic interactions.

Vacancy defects in epitaxial La0.7Sr0.3MnO3 thin films probed by a slow positron beam

International Nuclear Information System (INIS)

Jin, S W; Zhou, X Y; Wu, W B; Zhu, C F; Weng, H M; Wang, H Y; Zhang, X F; Ye, B J; Han, R D

2004-01-01

Vacancy defects in epitaxial La 0.7 Sr 0.3 MnO 3 (LSMO) thin films on LaAlO 3 substrates were detected using a variable energy positron beam. The line-shape S parameter of the epitaxial thin films deposited at different oxygen pressures was measured as a function of the implanting positron energy E. Our results show that the S parameter of the films changes non-monotonically with their deposition oxygen pressures. For the films deposited at lower oxygen pressures, the increase in S value in the films is attributed to the increase in oxygen vacancies and/or related defect-V O complexes, and for those deposited at higher oxygen pressures, the larger S parameter of the films is caused by the grain boundaries and/or metallic ion vacancies. The surface morphology of the films was also characterized to analyse the open volume defects in the LSMO films

Influence of γ-radiation doses on the properties of TeOx: (x=2-3) thin film

International Nuclear Information System (INIS)

Dewan, Namrata; Sreenivas, K.; Gupta, Vinay

2007-01-01

The influence of γ-ray doses (10-50 Gy) on the optical and electrical properties of radio-frequency sputtered tellurium dioxide (TeO x ) thin film was studied. The composition of the as-deposited TeO x films deposited under 25% oxygen and 100% oxygen in the sputtering gas mixture (Ar+O 2 ) was x=2 and 3, respectively. TeO 3 films were found to be highly sensitive to the γ-radiation doses and the value of optical band gap decrease from 4.18 to 3.56 eV with increasing radiation dose from 10 to 50 Gy. Current-voltage characteristics of the films showed an increase in the value of conductivity with increasing radiation doses. Monotonic decrease in the values of dielectric constant for the deposited films with increase in radiation dose was observed. The effect of γ-ray doses on the properties of TeO x film has been correlated with the rearrangement of the bipyramidal structure of amorphous TeO x thin film

Thin film metal-oxides

CERN Document Server

Ramanathan, Shriram

2009-01-01

Presents an account of the fundamental structure-property relations in oxide thin films. This title discusses the functional properties of thin film oxides in the context of applications in the electronics and renewable energy technologies.

Low-field tunnel-type magnetoresistance properties of polycrystalline and epitaxial La sub 0 sub . sub 6 sub 7 Sr sub 0 sub . sub 3 sub 3 MnO sub 3 thin films

CERN Document Server

Shim, I B; Choi, S Y

2000-01-01

The low-field tunnel-type magnetoresistance (TMB) properties of sol-gel derived polycrystalline and epitaxial La sub 0 sub . sub 6 sub 7 Sr sub 0 sub . sub 3 sub 3 MnO sub 3 (LSMO) thin films were investigated. The polycrystalline thin films were fabricated on Si (100) with a thermally oxidized SiO sub 2 layer while the epitaxial thin films were grown on LaAlO sub 3 (001) single-crystal substrates. The epitaxial thin films displayed both typical intrinsic colossal magnetoresistance (CMR) and abnormal extrinsic tunnel-type magnetoresistance behaviors. Tunnel-type MR ratio as high as 0.4% were observed in the polycrystalline thin films at a field of 120 Oe at room temperature (300 K) whereas the ratios were less than 0.1% for the epitaxial films in the same field range. The low-field tunnel-type MR of polycrystalline LSMO/SiO sub 2 ?Si (100) thin films originated from the behaviors of the grain-boundary properties.

Epitaxial growth and magnetic properties of ultraviolet transparent Ga2O3/(Ga1−xFex)2O3 multilayer thin films

Science.gov (United States)

Guo, Daoyou; An, Yuehua; Cui, Wei; Zhi, Yusong; Zhao, Xiaolong; Lei, Ming; Li, Linghong; Li, Peigang; Wu, Zhenping; Tang, Weihua

2016-01-01

Multilayer thin films based on the ferromagnetic and ultraviolet transparent semiconductors may be interesting because their magnetic/electronic/photonic properties can be manipulated by the high energy photons. Herein, the Ga2O3/(Ga1−xFex)2O3 multilayer epitaxial thin films were obtained by alternating depositing of wide band gap Ga2O3 layer and Fe ultrathin layer due to inter diffusion between two layers at high temperature using the laser molecular beam epitaxy technique. The multilayer films exhibits a preferred growth orientation of crystal plane, and the crystal lattice expands as Fe replaces Ga site. Fe ions with a mixed valence of Fe2+ and Fe3+ are stratified distributed in the film and exhibit obvious agglomerated areas. The multilayer films only show a sharp absorption edge at about 250 nm, indicating a high transparency for ultraviolet light. What’s more, the Ga2O3/(Ga1−xFex)2O3 multilayer epitaxial thin films also exhibits room temperature ferromagnetism deriving from the Fe doping Ga2O3. PMID:27121446

Electrical Transport and Magnetoresistance Properties of Tensile-Strained CaMnO3 Thin Films

Science.gov (United States)

Ullery, Dustin; Lawson, Bridget; Zimmerman, William; Neubauer, Samuel; Chaudhry, Adeel; Hart, Cacie; Yong, Grace; Smolyaninova, Vera; Kolagani, Rajeswari

We will present our studies of the electrical transport and magnetoresistance properties of tensile strained CaMnO3 thin films. We observe that the resistivity decreases significantly as the film thickness decreases which is opposite to what is observed in thin films of hole doped manganites. The decrease in resistivity is more pronounced in the films on (100) SrTiO3, with resistivity of the thinnest films being about 3 orders of magnitude lower than that of bulk CaMnO3. Structural changes accompanying resistivity changes cannot be fully explained as due to tensile strain, and indicate the presence of oxygen vacancies. These results also suggest a coupling between tensile strain and oxygen deficiency, consistent with predictions from models based on density functional theory calculations. We observe a change in resistance under the application of moderate magnetic field. Experiments are underway to understand the origin of the magnetoresistance and its possible relation to the tensile strain effects. We acknowledge support from: Towson Office of University Undergraduate Research, Fisher Endowment Grant and Undergraduate Research Grants from the Fisher College of Science and Mathematics, and Seed Funding Grant from the School of Emerging technologies.

Photo- and Electrochromic Properties of Activated Reactive Evaporated MoO3 Thin Films Grown on Flexible Substrates

Directory of Open Access Journals (Sweden)

K. Hari Krishna

2008-01-01

Full Text Available The molybdenum trioxide (MoO3 thin films were grown onto ITO-coated flexible Kapton substrates using plasma assisted activated reactive evaporation technique. The film depositions were carried out at constant glow power and oxygen partial pressures of 8 W and 1×10−3 Torr, respectively. The influence of substrate temperature on the microstructural and optical properties was investigated. The MoO3 thin films prepared at a substrate temperature of 523 K were found to be composed of uniformly distributed nanosized grains with an orthorhombic structure of α-MoO3. These nanocrystalline MoO3 thin films exhibited higher optical transmittance of about 80% in the visible region with an evaluated optical band gap of 3.29 eV. With the insertion of 12.5 mC/cm2, the films exhibited an optical modulation of 40% in the visible region with coloration efficiency of 22 cm2/C at the wavelength of 550 nm. The MoO3 films deposited at 523 K demonstrated better photochromic properties and showed highest color center concentration for the irradiation time of 30 minutes at 100 mW/cm2.

Photon up-converting (Yb,Er){sub 2}O{sub 3} thin films by atomic layer deposition

Energy Technology Data Exchange (ETDEWEB)

Tuomisto, Minnea [Department of Chemistry, University of Turku (Finland); Doctoral Programme in Physical and Chemical Sciences, University of Turku Graduate School (UTUGS), Turku (Finland); Giedraityte, Zivile; Karppinen, Maarit [Department of Chemistry and Materials Science, School of Chemical Engineering, Aalto University (Finland); Lastusaari, Mika [Department of Chemistry, University of Turku (Finland); Turku University Centre for Materials and Surfaces (MatSurf), Turku (Finland)

2017-06-15

We report up-converting (Yb,Er){sub 2}O{sub 3} thin films grown with the atomic layer deposition (ALD) technique. The films are crystalline and show a homogeneous morphology with a roughness less than 1 nm for 40 nm thick films. High-intensity near-infrared (NIR) to green and red two-photon up-conversion emission is obtained with 974 nm excitation through an absorption by Yb{sup 3+}, followed by a Yb{sup 3+}-Er{sup 3+} energy transfer and emission from Er{sup 3+}. The ALD technique promises to be excellent for producing up-converting films for many applications such as near-infrared radiation absorbing layers for solar cells and sensors in point-of-care biomedical diagnostics. Schematic picture of the ALD-grown (Yb,Er){sub 2}O{sub 3} thin film including the up-conversion emission spectra. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Thin films and nanomaterials

International Nuclear Information System (INIS)

Jayakumar, S.; Kannan, M.D.; Prasanna, S.

2012-01-01

The objective of this book is to disseminate the most recent research in Thin Films, Nanomaterials, Corrosion and Metallurgy presented at the International Conference on Advanced Materials (ICAM 2011) held in PSG College of Technology, Coimbatore, India during 12-16 December 2011. The book is a compilation of 113 chapters written by active researchers providing information and critical insights into the recent advancements that have taken place. Important new applications are possible today in the fields of microelectronics, opto-electronics, metallurgy and energy by the application of thin films on solid surfaces. Recent progress in high vacuum technology and new materials has a remarkable effect in thin film quality and cost. This has led to the development of new single or multi-layered thin film devices with diverse applications in a multitude of production areas, such as optics, thermal barrier coatings and wear protections, enhancing service life of tools and to protect materials against thermal and atmospheric influence. On the other hand, thin film process techniques and research are strongly related to the basic research activities in nano technology, an increasingly important field with countless opportunities for applications due to the emergence of new properties at the nanoscale level. Materials and structures that are designed and fabricated at the nano scale level, offer the potential to produce new devices and processes that may enhance efficiencies and reduce costs in many areas, as photovoltaic systems, hydrogen storage, fuel cells and solar thermal systems. In the book, the contributed papers are classified under two sections i) thin films and ii) nanomaterials. The thin film section includes single or multi layer conducting, insulating or semiconducting films synthesized by a wide variety of physical or chemical techniques and characterized or analyzed for different applications. The nanomaterials section deals with novel or exciting materials

New Method for Fabrication of Co3O4 Thin Film Sensors: Structural, Morphological and Optoelectronic Properties

Directory of Open Access Journals (Sweden)

Vikas PATIL

2011-05-01

Full Text Available Nanocrystalline Co3O4 thin films have been deposited by spin coating technique and then have been analyzed to test their application in NH3 gas-sensing technology. In particular, spectrophotometric and conductivity measurements have been performed in order to determine the optical and electrical properties of Co3O4 thin films. The structure and the morphology of such material have been investigated by X ray diffraction and Scanning electron microscopy. The X-ray diffraction studies confirmed that the films grown by this technique have good crystalline cubic spinel structure and present a random orientation. The morphology of the sol gel derived Co3O4 shows nanocrystalline grains with some overgrown clusters .The optical band gap has been determined from the absorption coefficient. We found that the optical band gap energy decreases from 2.58 eV to 2.07 eV with increasing annealing temperature between 400-700 oC. These mean that the optical quality of Co3O4 films is improved by annealing. The dc electrical conductivity of Co3O4 thin films were increased from 10-4 to 10-2(Ω cm-1 with increase in annealing temperature. The electron carrier concentration (n and mobility (μ of Co3O4 films annealed at 400-700 oC were estimated to be of the order of 2.4 to 4.5 x 1019 cm-3 and 5.2 to 7.0 x 10-5 cm2 V-1 s-1 respectively. It is observed that Co3O4 thin film annealing at 700 oC after deposition provide a smooth and flat texture suited for optoelectronic applications. Gas sensing properties showed that the Co3O4 films (at 700 oC were sensitive as well as fast in responding to NH3. A high sensitivity for ammonia indicates that the Co3O4 films are selective for this gas.

Nb{sub 3}Al thin film deposition for low-noise terahertz electronics

Energy Technology Data Exchange (ETDEWEB)

Dochev, D; Pavolotsky, A B; Belitsky, V; Olofsson, H [Group for Advanced Receiver Development and Onsala Space Observatory, Department of Radio- and Space Science, Chalmers University of Technology, SE 412 96 Gothenburg (Sweden)], E-mail: dimitar.dochev@chalmers.se

2008-02-01

Higher energy gap superconducting materials were always interesting for low-noise mixer applications such as superconductor-insulator-superconductor tunnel junctions (SIS) and hot-electron bolometer (HEB) used in sub-millimeter and terahertz parts of electro-magnetic spectrum. Here, we report a novel approach for producing Nb{sub 3}Al thin film by co-sputtering from two confocally arranged Nb and Al dc-magnetrons onto substrate heated up to 830 deg. C. Characterization of the deposited films revealed presence of the A15 phase and measured critical temperature was up to 15.7 K with the transition width 0.2-0.3 K for a 300 nm thick film. We measured the film critical magnetic field and studied influence of annealing on the film properties. We have investigated compositional depth profile of the deposited films by spectroscopy of reflected electrons.

Transport and magnetic properties of Ce-doped LaMnO3 thin films

International Nuclear Information System (INIS)

Yanagida, Takeshi; Kanki, Teruo; Vilquin, Bertrand; Tanaka, Hidekazu; Kawai, Tomoji

2005-01-01

Ce-doped LaMnO 3 epitaxial thin films were fabricated by a pulsed laser deposition method in consideration of thermodynamics. Oxygen- or argon-atmosphere post-annealed films showed a metal-insulator transition and ferromagnetic property, and the transition temperature T c was found to be significantly influenced by the post-annealing conditions at the T c ranging from 200 to 300 K. Moreover, the majority carriers within Ce-doped LaMnO 3 films were identified to be holes from Hall effect measurements

Polarization-tuned diode behaviour in multiferroic BiFeO3 thin films

KAUST Repository

Yao, Yingbang; Zhang, Bei; Chen, Long; Yang, Yang; Wang, Zhihong; Alshareef, Husam N.; Zhang, Xixiang

2012-01-01

Asymmetric rectifying I-V behaviour of multiferroic BiFeO3 (BFO) thin films grown on transparent ITO-coated glass was quantitatively studied as a function of ferroelectric polarization. Different polarized states were established by unipolar

Structural and photodegradation behaviors of Fe{sup 3+}-doping TiO{sub 2} thin films prepared by a sol–gel spin coating

Energy Technology Data Exchange (ETDEWEB)

Lin, Huey-Jiuan; Yang, Tien-Syh [Department of Materials Science and Engineering, National United University, 1 Lien-Da, Kung-Ching Li, Miao-Li 36003, Taiwan (China); Wang, Moo-Chin, E-mail: mcwang@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 80782, Taiwan (China); Hsi, Chi-Shiung, E-mail: chsi@nuu.edu.tw [Department of Materials Science and Engineering, National United University, 1 Lien-Da, Kung-Ching Li, Miao-Li 36003, Taiwan (China)

2014-10-15

Highlights: • Pure and various Fe{sup 3+}-doped TiO{sub 2} thin films have been successfully fabricated. • The phase of all thin films was single phase of anatase TiO{sub 2} when calcined at 823 K. • The crystallinity of TiO{sub 2} thin films decreased as Fe{sup 3+}-doping increased. • The photodegradation of each sample increased as the irradiation time increased. • The photodegradation increased as Fe{sup 3+}-doping increased at a fixed irradiation time. - Abstract: Pure and various Fe{sup 3+}-doping TiO{sub 2} thin films have been successfully fabricated on glass substrate prepared by a sol–gel spin coating route. The structural and photodegradation behavior of these films after calcined at various temperatures for 1 h were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), photoluminescence (PL) spectrum and degradation of 1.0 × 10{sup −5} M methylene blue solution. When all thin films after calcined at 823 K for 1 h, the crystalline phase are comprised only contained single phase of anatase TiO{sub 2}. The crystallinity of various Fe{sup 3+}-doping TiO{sub 2} thin films decreases with Fe{sup 3+}-doping concentration increased. The PL intensity of all thin films also decreases with Fe{sup 3+}-doping concentration increased. When all various Fe{sup 3+}-doping TiO{sub 2} thin films after calcined at 823 K for 1 h, the photodegradation of each sample increases with irradiation time increased. Moreover, the photodegradation also increases with Fe{sup 3+}-doping concentration increased when fixed at constant irradiation time.

Epitaxial La2/3Sr1/3MnO3 thin films with unconventional magnetic and electric properties near the Curie temperature

International Nuclear Information System (INIS)

Signorini, L.; Riva, M.; Cantoni, M.; Bertacco, R.; Ciccacci, F.

2006-01-01

We used Pulsed Laser Deposition (PLD) in oxidizing environment to epitaxially grow optimally doped manganite La 2/3 Sr 1/3 MnO 3 (LSMO) thin films over a (001) oriented SrTiO 3 substrate. Synthesized samples show good room temperature magnetic properties accompanied by a peculiar extension of the metallic conduction regime to temperatures higher than the Curie point. In this paper we present a study of the dependence of transport and magnetic properties of LSMO thin films on the oxygen pressure during PLD growth. We show how interaction of the growing films with O 2 molecules is fundamental for a correct synthesis and in which way it is possible to adjust PLD experimental parameters in order to tune LSMO thin film properties. The persistence of the metallic conduction regime above the Curie temperature indicates some minor changes of the electronic structure near the Fermi level, which is responsible for the half-metallic behavior of LSMO at low temperature. This feature is rather intriguing from the technological point of view, as it could pave the way to the increase of operating temperature of devices based on LSMO

Comparison of Y{sub 2}O{sub 3}:Bi{sup 3+} phosphor thin films fabricated by the spin coating and radio frequency magnetron techniques

Energy Technology Data Exchange (ETDEWEB)

Jafer, R.M.; Yousif, A. [Department of Physics, University of the Free State, P.O. Box 339, Bloemfontein ZA 9300 (South Africa); Department of Physics, Faculty of Education, University of Khartoum, P.O. Box 321, Postal Code 11115 Omdurman (Sudan); Kumar, Vinod [Department of Physics, University of the Free State, P.O. Box 339, Bloemfontein ZA 9300 (South Africa); Photovoltaic Laboratory, Centre for Energy Studies, Indian Institute of Technology Delhi, New Delhi 110016 (India); Pathak, Trilok Kumar [Department of Physics, University of the Free State, P.O. Box 339, Bloemfontein ZA 9300 (South Africa); Semiconductor Physics Lab, Department of Physics, Gurukula Kangri University, Haridwar (India); Purohit, L.P. [Semiconductor Physics Lab, Department of Physics, Gurukula Kangri University, Haridwar (India); Swart, H.C., E-mail: swarthc@ufs.ac.za [Department of Physics, University of the Free State, P.O. Box 339, Bloemfontein ZA 9300 (South Africa); Coetsee, E., E-mail: CoetseeE@ufs.ac.za [Department of Physics, University of the Free State, P.O. Box 339, Bloemfontein ZA 9300 (South Africa)

2016-09-15

The reactive radio-frequency (RF) magnetron sputtering and spin coating fabrication techniques were used to fabricate Y{sub 2−x}O{sub 3}:Bi{sub x=0.5%} phosphor thin films. The two techniques were analysed and compared as part of investigations being done on the application of down-conversion materials for a Si solar cell. The morphology, structural and optical properties of these thin films were investigated. The X-ray diffraction results of the thin films fabricated by both techniques showed cubic structures with different space groups. The optical properties showed different results because the Bi{sup 3+} ion is very sensitive towards its environment. The luminescence results for the thin film fabricated by the spin coating technique is very similar to the luminescence observed in the powder form. It showed three obvious emission bands in the blue and green regions centered at about 360, 410 and 495 nm. These emissions were related to the {sup 3}P{sub 1}–{sup 1}S{sub 0} transition of the Bi{sup 3+} ion situated in the two different sites of the Y{sub 2}O{sub 3} matrix with I a-3(206) space group. Whereas the thin film fabricated by the radio frequency magnetron technique showed a broad single emission band in the blue region centered at about 416 nm. This was assigned to the {sup 3}P{sub 1}–{sup 1}S{sub 0} transition of the Bi{sup 3+} ion situated in one of the Y{sub 2}O{sub 3} matrix's sites with a Fm-3 (225) space group. The spin coating fabrication technique is suggested to be the best technique to fabricate the Y{sub 2}O{sub 3}:Bi{sup 3+} phosphor thin films. - Highlights: • RF sputtering and spin coating were used to fabricate Y{sub 2−x}O{sub 3}:Bi{sub x=0.5%} phosphor thin films. • XRD results of the two films showed cubic structures with different space groups. • PL showed different emission for the Bi{sup 3+} ions in the two films. • Three emission bands in the blue and green regions centered at about 360, 410 and 495 nm. • RF

Epitaxial thin-film growth of Ruddlesden-Popper-type Ba3Zr2O7 from a BaZrO3 target by pulsed laser deposition

International Nuclear Information System (INIS)

Butt, Shariqa Hassan; Rafique, M.S.; Siraj, K.; Latif, A.; Afzal, Amina; Awan, M.S.; Bashir, Shazia; Iqbal, Nida

2016-01-01

Ruddlesden-Popper Ba 3 Zr 2 O 7 thin films have been synthesized via pulsed laser deposition (PLD) technique. The optimization of deposition parameters in PLD enables the formation of thin film of metastable Ba 3 Zr 2 O 7 phase from BaZrO 3 target. In order to see the post-annealing effects on the structural and optical properties, the deposited Ba 3 Zr 2 O 7 thin films were annealed at 500, 600 and 800 C. X-ray diffraction (XRD) reveals the formation of Ba 3 Zr 2 O 7 phase with tetragonal structure. The changes in the surface of the deposited films were analysed by FE-SEM and AFM. The thin film post-annealed at 500 C exhibited the best structural, optical and surface properties. Furthermore, the chemical states and chemical composition of the films were determined by X-ray photoelectron spectroscopy (XPS) near the surface. The XPS results show that Ba, Zr and O exist mainly in the form of Ba 3 Zr 2 O 7 Ruddlesden-Popper-type perovskite structure. (orig.)

Growth and physical properties of highly oriented La-doped (K,Na)NbO3 ferroelectric thin films

International Nuclear Information System (INIS)

Vendrell, X.; Raymond, O.; Ochoa, D.A.; García, J.E.; Mestres, L.

2015-01-01

Lead-free (K,Na)NbO 3 (KNN) and La doped (K,Na)NbO 3 (KNN-La) thin films are grown on SrTiO 3 substrates using the chemical solution deposition method. The effect of adding different amounts of Na and K excess (0–20 mol%) is investigated. The results confirm the necessity of adding 20 mol% excess amounts of Na and K precursor solutions in order to avoid the formation of the secondary phase, K 4 Nb 6 O 17 , as confirmed by X-ray diffraction and Raman spectroscopy. Moreover, when adding a 20 mol% of alkaline metal excess, the thin films are highly textured with out-of-plane preferential orientation in the [100] direction of the [100] orientation of the substrate. Doping with lanthanum results in a decrease of the leakage current density at low electric field, and an increase in the dielectric permittivity across the whole temperature range (80–380 K). Although the (100)-oriented KNN and KNN-La films exhibited rounded hysteresis loops, at low temperatures the films show the typical ferroelectric hysteresis loops. - Highlights: • (K 0.5 Na 0.5 )NbO 3 and [(K 0.5 Na 0.5 ) 0.985 La 0.005 ]NbO 3 thin films have been prepared. • The obtained thin films show an excellent (100) preferred orientation. • Doping with lanthanum results in a decrease of the leakage current density. • The dielectric properties are enhanced when doping with lanthanum

The Enhanced Formaldehyde-Sensing Properties of P3HT-ZnO Hybrid Thin Film OTFT Sensor and Further Insight into Its Stability

Directory of Open Access Journals (Sweden)

Huiling Tai

2015-01-01

Full Text Available A thin-film transistor (TFT having an organic–inorganic hybrid thin film combines the advantage of TFT sensors and the enhanced sensing performance of hybrid materials. In this work, poly(3-hexylthiophene (P3HT-zinc oxide (ZnO nanoparticles’ hybrid thin film was fabricated by a spraying process as the active layer of TFT for the employment of a room temperature operated formaldehyde (HCHO gas sensor. The effects of ZnO nanoparticles on morphological and compositional features, electronic and HCHO-sensing properties of P3HT-ZnO thin film were systematically investigated. The results showed that P3HT-ZnO hybrid thin film sensor exhibited considerable improvement of sensing response (more than two times and reversibility compared to the pristine P3HT film sensor. An accumulation p-n heterojunction mechanism model was developed to understand the mechanism of enhanced sensing properties by incorporation of ZnO nanoparticles. X-ray photoelectron spectroscope (XPS and atomic force microscopy (AFM characterizations were used to investigate the stability of the sensor in-depth, which reveals the performance deterioration was due to the changes of element composition and the chemical state of hybrid thin film surface induced by light and oxygen. Our study demonstrated that P3HT-ZnO hybrid thin film TFT sensor is beneficial in the advancement of novel room temperature HCHO sensing technology.

Piezoelectric MEMS: Ferroelectric thin films for MEMS applications

Science.gov (United States)

Kanno, Isaku

2018-04-01

In recent years, piezoelectric microelectromechanical systems (MEMS) have attracted attention as next-generation functional microdevices. Typical applications of piezoelectric MEMS are micropumps for inkjet heads or micro-gyrosensors, which are composed of piezoelectric Pb(Zr,Ti)O3 (PZT) thin films and have already been commercialized. In addition, piezoelectric vibration energy harvesters (PVEHs), which are regarded as one of the key devices for Internet of Things (IoT)-related technologies, are promising future applications of piezoelectric MEMS. Significant features of piezoelectric MEMS are their simple structure and high energy conversion efficiency between mechanical and electrical domains even on the microscale. The device performance strongly depends on the function of the piezoelectric thin films, especially on their transverse piezoelectric properties, indicating that the deposition of high-quality piezoelectric thin films is a crucial technology for piezoelectric MEMS. On the other hand, although the difficulty in measuring the precise piezoelectric coefficients of thin films is a serious obstacle in the research and development of piezoelectric thin films, a simple unimorph cantilever measurement method has been proposed to obtain precise values of the direct or converse transverse piezoelectric coefficient of thin films, and recently this method has become to be the standardized testing method. In this article, I will introduce fundamental technologies of piezoelectric thin films and related microdevices, especially focusing on the deposition of PZT thin films and evaluation methods for their transverse piezoelectric properties.

Influence of the vacuum interface on the charge distribution in V2O3 thin films

KAUST Repository

Schwingenschlögl, Udo

2009-09-22

The electronic structure of V2O3 thin films is studied by means of the augmented spherical wave method as based on density functional theory and the local density approximation. We establish that the effects of charge redistribution, induced by the vacuum interface, in such films are restricted to a very narrow surface layer of ≈15 Å thickness. As a consequence, charge redistribution can be ruled out as a source of the extraordinary thickness dependence of the metal–insulator transition observed in V2O3 thin films of ~100–1000 Å thickness.

A photoelectrochemical (PEC) study on graphene oxide based hematite thin films heterojunction (R-GO/Fe2O3)

Science.gov (United States)

Sharma, Poonam; Zachariah, Michael; Ehrman, Sheryl; Shrivastava, Rohit; Dass, Sahab; Satsangi, Vibha; Michael Zachariah, Sheryl Ehrman Collaboration; Rohit Shrivastava, Sahab Dass Collaboration; Vibha R Satsangi, Poonam Sharma Team

2013-03-01

Graphene has an excellent electronic conductivity, a high theoretical surface area of 2630 m2/g and excellent mechanical properties and, thus, is a promising component for high-performance electrode materials. Following this, GO has been used to modify the PEC response of photoactive material hematite thin films in PEC cell. A reduced graphene oxide/iron oxide (R-GO/Fe2O3) thin film structure has been successfully prepared on ITO by directly growing iron oxide particles on the thermally reduced graphene oxide sheets prepared from suspension of exfoliated graphene oxide. R-GO/Fe2O3 thin films were tested in PEC cell and offered ten times higher photocurrent density than pristine Fe2O3 thin film sample. XRD, SEM, EDS, UV-Vis, Mott-Schottky and Raman studies were carried out to study spectro-electrochemical properties. Enhanced PEC performance of these photoelectrodes was attributed to its porous morphology, improved conductivity upon favorable carrier transfer across the oxides interface.

Pulsed laser deposited KY3F10: Ho3+ thin films: Influence of target to substrate

CSIR Research Space (South Africa)

Debelo, NG

2017-04-01

Full Text Available The influence of target to substrate distance (dts) on the structural, morphological and photoluminescence (PL) properties of commercially obtained KY3F10 : Ho3+ phosphor thin films prepared by pulsed laser deposition is investigated for dts values...

Cation disorder and gas phase equilibrium in an YBa 2Cu 3O 7- x superconducting thin film

Science.gov (United States)

Shin, Dong Chan; Ki Park, Yong; Park, Jong-Chul; Kang, Suk-Joong L.; Yong Yoon, Duk

1997-02-01

YBa 2Cu 3O 7- x superconducting thin films have been grown by in situ off-axis rf sputtering with varying oxygen pressure, Ba/Y ratio in a target, and deposition temperature. With decreasing oxygen pressure, increasing Ba/Y ratio, increasing deposition temperature, the critical temperature of the thin films decreased and the c-axis length increased. The property change of films with the variation of deposition variables has been explained by a gas phase equilibrium of the oxidation reaction of Ba and Y. Applying Le Chatelier's principle to the oxidation reaction, we were able to predict the relation of deposition variables and the resultant properties of thin films; the prediction was in good agreement with the experimental results. From the relation between the three deposition variables and gas phase equilibrium, a 3-dimensional processing diagram was introduced. This diagram has shown that the optimum deposition condition of YBa 2Cu 3O 7- x thin films is not a fixed point but can be varied. The gas phase equilibrium can also be applied to the explanation of previous results that good quality films were obtained at low deposition temperature using active species, such as O, O 3, and O 2+.

Double switching hysteresis loop in a single layer Fe3Pt alloy thin films

International Nuclear Information System (INIS)

Nahid, M.A.I.; Suzuki, Takao

2008-01-01

The Fe 3 Pt alloy thin films were epitaxially grown on MgO(100) substrate by e-beam evaporation. The films were partially ordered at the substrate deposition temperature above 350 deg. C. These partially ordered films exhibit very large biaxial magnetic anisotropy constant in the order of 10 5 J/m 3 and produce double switching in the hysteresis loops. The difference of the switching field of these films can be up to about 3 x 10 5 A/m by tuning the angle of the applied field with respect to the easy axes. This double switching behavior stems from the large biaxial magnetic anisotropy of the films

Preparation and thermoelectric properties of RF co-sputtered CoSb{sub 3} skutteruddite thin films

Energy Technology Data Exchange (ETDEWEB)

Ahmed, Aziz [University of Science and Technology, Daejeon (Korea, Republic of); Han, Seungwoo [Korea Institute of Machinery and Materials, Daejeon (Korea, Republic of); University of Science and Technology, Daejeon (Korea, Republic of)

2014-11-15

Various skutterudites have been under investigation because of their potential application in thermoelectric materials and devices. These studies indicate that bulk materials with a skutterudite type structure show reasonable thermoelectric behaviors at elevated temperatures, which make them suitable for high-temperature thermoelectric applications. The results of thermoelectric-property measurements on skutterudite-phase CoSb{sub 3} thin films are presented in this study in order to extend the bulk material concept to micro-device applications by using thin film deposition technology. Thin films are deposited on oxidized silicon substrates by using the RF co-sputtering method. The film's composition is found to depend strongly on the deposition conditions. The temperature at which the deposited films transition from an amorphous state to a crystalline state has been reported to be about 153 .deg. C. Therefore, some experiments are performed with the substrate temperature kept at 200 .deg. C to obtain polycrystalline films. The crystal structure of the film is evaluated by using x-ray diffraction (XRD) measurements. Energy dispersive spectroscopy (EDS) is used to determine the film's composition whereas the surface morphology and the thickness are investigated and measured by using scanning electron microscopy (SEM). Finally, the thermoelectric properties, namely, the electrical resistivity and the Seebeck coefficient, are used to calculate the power factor of the deposited thin films and, their variations with temperature are measured. We report a maximum power factor of 0.41 mW/mK{sup 2} for the film deposited at a 200 .deg. C substrate temperature.

Microstructure and electric characteristics of AETiO3 (AE=Mg, Ca, Sr doped CaCu3Ti4O12 thin films prepared by the sol–gel method

Directory of Open Access Journals (Sweden)

Dong Xu

2015-10-01

Full Text Available This paper focuses on the effects of alkline-earth metal titante AETiO3 (AE=Mg, Ca, Sr doping on the microstructure and electric characteristics of CaCu3Ti4O12 thin films prepared by the sol–gel method. The results showed that the grain size of CCTO thin films could be increased by MgTiO3 doping. The movement of the grain boundaries was impeded by the second phases of CaTiO3 and SrTiO3 concentrating at grain boundaries in CaTiO3 and SrTiO3 doped CCTO thin films. Rapid ascent of dielectric constant could be observed in 0.1Mg TiO3 doped CCTO thin films, which was almost as three times high as pure CCTO thin film and the descent of the dielectric loss at low frequency could also be observed. In addition, the nonlinear coefficient (α, threshold voltage (VT and leakage current (IL of AETiO3 doped CCTO thin films (AE=Mg, Ca, Sr showed different variation with the increasing content of the MgTiO3, CaTiO3 and SrTiO3.

Effect of high energy ions on the electrical and morphological properties of Poly(3-Hexylthiophene) (P3HT) thin film

Science.gov (United States)

Sharma, Trupti; Singhal, R.; Vishnoi, R.; Sharma, G. D.; Biswas, S. K.

2018-05-01

The spin-coated thin films of Poly(3-Hexylthiophene) (P3HT) on the glass and Si (double side polished) substrates have been irradiated with 55 MeV Si+4 swift heavy ions (SHI) at fluences in the range from 1 × 1010 to 1 × 1012 ions/cm2. Structural modifications produced by energetic ions are observed by characterization of pristine and irradiated P3HT thin films. Different techniques like high-resolution X-ray diffraction (HR-XRD), micro-Raman spectroscopy and Fourier transform infrared spectroscopy (FTIR) were used to analyze the structural changes in the material. A significant increase in crystallinity and room temperature electrical conductivity of P3HT film has been detected on exposure to the heavy ions. The observed increase in the electrical conductivity with increased fluences is explained in the light of improved ordering of polymer chains after irradiation. Mott's variable range hopping model has been used to explain the conduction mechanism in the material in the temperature range of 230-350 K. The modification in surface properties also observed using AFM analysis and contact angle measurement. It is observed that nature of the P3HT thin films remains hydrophobic after irradiation.

Structural, compositional and optical properties of spin coated MoO3 thin film

Science.gov (United States)

Jain, Vishva; Shah, Dimple; Patel, K. D.; Zankat, Chetan

2018-05-01

The attraction towards the MoO3 thin film is due to its wide range of application base on its properties. Its application in the field of energy storage and conversion as a cathode material for rechargeable lithium ion battery, hole selective layer in solar cell and in pseudocapacitors makes it more attractive material. Taking in consideration, economical route and tailoring advantage of film formation we have used spin coating method for the synthesis of the film with Ammonium heptamolybdate (NH4)6Mo7O24 4H2O) and distilled water as the precursor and solvent respectively on the glass substrate. The method also provides the large area synthesis of the film which is beneficial for the commercial applications. The film was spin coated at 1600 rpm with 4 % weight per volume ratio. The film so formed was annealed at 300 °C for 3 hours. The structural investigation was done by the X-Ray diffraction technique which shows the thin film of polycrystalline type. The average crystallize size is about 50 nm. The composition of the film was studied with the help of EDAX. The optical properties were studied by the photoluminescence and UV Spectroscopy. The results from both the characterization are well matched with each other. Photoluminescence studies show band to band emission observed at 416 nm shown in the fig. 5. From UV spectroscopy, using transmission and absorption spectra we observed the band gap edge around 3 eV. This is in accordance with the photoluminescence result.

Investigation of Electrical, Optical and GaS Sensing properties Sol-Gel Derived WO3 Thin Films

International Nuclear Information System (INIS)

Dumludag, F.

2008-01-01

Tungsten oxide (WO 3 ) is a wide band gap n-type semiconductor. Thin films of WO 3 are considerable interest because of their potential applications in electrochromic devices, and gas sensors. In this work, WO 3 thin films were deposited on IDT (Interdigital electrodes) by a sol-gel dipping process. Precursor solution was prepared by dissolving of tungstic acid in ammonia. We investigated d.c. and a.c. (40 Hz-100 KHz) electrical properties of the films in the temperature range of 293K and 473K in vacuum ambient (10 - 2 mbar). We observed frequency dependent conductivity behavior at high frequencies. Absorption spectra of the film showed that a maximum absorption occurred at 330 nm. We also investigated the response of the films to vapors of the volatile organic compounds (acetone, chloroform, toluene, ethanol, ammonia) and water vapor. The films showed no sensitivity to the test gases at room temperature. Concentration of the vapors were controlled by mass flowmeters. All the measurement system was computerized

Phonon Drag in Thin Films, Cases of Bi2Te3 and ZnTe

Science.gov (United States)

Chi, Hang; Uher, Ctirad

2014-03-01

At low temperatures, in (semi-)conductors subjected to a thermal gradient, charge carriers (electrons and holes) are swept (dragged) by out-of-equilibrium phonons due to strong electron-phonon interaction, giving rise to a large contribution to the Seebeck coefficient called the phonon-drag effect. Such phenomenon was surprisingly observed in our recent transport study of highly mismatched alloys as potential thermoelectric materials: a significant phonon-drag thermopower reaching 1.5-2.5 mV/K was recorded for the first time in nitrogen-doped ZnTe epitaxial layers on GaAs (100). In thin films of Bi2Te3, we demonstrate a spectacular influence of substrate phonons on charge carriers. We show that one can control and tune the position and magnitude of the phonon-drag peak over a wide range of temperatures by depositing thin films on substrates with vastly different Debye temperatures. Our experiments also provide a way to study the nature of the phonon spectrum in thin films, which is rarely probed but clearly important for a complete understanding of thin film properties and the interplay of the substrate and films. This work is supported by the Center for Solar and Thermal Energy Conversion, an Energy Frontier Research Center funded by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences under Award Number DE-SC0000957.

Measurement of thermal conductance of La0.7Sr0.3MnO3 thin films deposited on SrTiO3 and MgO substrates

Science.gov (United States)

Aryan, A.; Guillet, B.; Routoure, J. M.; Fur, C.; Langlois, P.; Méchin, L.

2015-01-01

We present measurements of the thermal conductance of thin-film-on-substrate structures that could serve as thin film uncooled bolometers. Studied samples were 75 nm thick epitaxial La0.7Sr0.3MnO3 thin films deposited on SrTiO3 (0 0 1) and MgO (0 0 1) substrates patterned in square geometries of areas ranging from 50 μm × 50 μm to 200 μm × 200 μm. The model allows estimating thermal boundary conductance values at the interface between film and substrate of 0.28 ± 0.08 × 106 W K-1 m-2 for LSMO/STO (0 0 1) and 5.8 ± 3.0 × 106 W K-1 m-2 for LSMO/MgO (0 0 1) from measurements performed in the static regime. Analytical expressions of thermal conductance and thermal capacitance versus modulation frequency are compared to measurements of the elevation temperature due to absorbed incoming optical power. The overall good agreement found between measurements and model finally provides the possibility to calculate the bolometric response of thin film bolometers, thus predicting their frequency response for various geometries.

Thin film device applications

CERN Document Server

Kaur, Inderjeet

1983-01-01

Two-dimensional materials created ab initio by the process of condensation of atoms, molecules, or ions, called thin films, have unique properties significantly different from the corresponding bulk materials as a result of their physical dimensions, geometry, nonequilibrium microstructure, and metallurgy. Further, these characteristic features of thin films can be drasti­ cally modified and tailored to obtain the desired and required physical characteristics. These features form the basis of development of a host of extraordinary active and passive thin film device applications in the last two decades. On the one extreme, these applications are in the submicron dimensions in such areas as very large scale integration (VLSI), Josephson junction quantum interference devices, magnetic bubbles, and integrated optics. On the other extreme, large-area thin films are being used as selective coatings for solar thermal conversion, solar cells for photovoltaic conver­ sion, and protection and passivating layers. Ind...

Solution-processed In2S3 buffer layer for chalcopyrite thin film solar cells

Science.gov (United States)

Wang, Lan; Lin, Xianzhong; Ennaoui, Ahmed; Wolf, Christian; Lux-Steiner, Martha Ch.; Klenk, Reiner

2016-02-01

We report a route to deposit In2S3 thin films from air-stable, low-cost molecular precursor inks for Cd-free buffer layers in chalcopyrite-based thin film solar cells. Different precursor compositions and processing conditions were studied to define a reproducible and robust process. By adjusting the ink properties, this method can be applied in different printing and coating techniques. Here we report on two techniques, namely spin-coating and inkjet printing. Active area efficiencies of 12.8% and 12.2% have been achieved for In2S3-buffered solar cells respectively, matching the performance of CdS-buffered cells prepared with the same batch of absorbers.

Intermediate surface structure between step bunching and step flow in SrRuO3 thin film growth

Science.gov (United States)

Bertino, Giulia; Gura, Anna; Dawber, Matthew

We performed a systematic study of SrRuO3 thin films grown on TiO2 terminated SrTiO3 substrates using off-axis magnetron sputtering. We investigated the step bunching formation and the evolution of the SRO film morphology by varying the step size of the substrate, the growth temperature and the film thickness. The thin films were characterized using Atomic Force Microscopy and X-Ray Diffraction. We identified single and multiple step bunching and step flow growth regimes as a function of the growth parameters. Also, we clearly observe a stronger influence of the step size of the substrate on the evolution of the SRO film surface with respect to the other growth parameters. Remarkably, we observe the formation of a smooth, regular and uniform ``fish skin'' structure at the transition between one regime and another. We believe that the fish skin structure results from the merging of 2D flat islands predicted by previous models. The direct observation of this transition structure allows us to better understand how and when step bunching develops in the growth of SrRuO3 thin films.

Polarization enhancement and ferroelectric switching enabled by interacting magnetic structures in DyMnO3 thin films

KAUST Repository

Lu, Chengliang

2013-12-02

The mutual controls of ferroelectricity and magnetism are stepping towards practical applications proposed for quite a few promising devices in which multiferroic thin films are involved. Although ferroelectricity stemming from specific spiral spin ordering has been reported in highly distorted bulk perovskite manganites, the existence of magnetically induced ferroelectricity in the corresponding thin films remains an unresolved issue, which unfortunately halts this step. In this work, we report magnetically induced electric polarization and its remarkable response to magnetic field (an enhancement of ?800% upon a field of 2 Tesla at 2 K) in DyMnO3 thin films grown on Nb-SrTiO3 substrates. Accompanying with the large polarization enhancement, the ferroelectric coercivity corresponding to the magnetic chirality switching field is significantly increased. A picture based on coupled multicomponent magnetic structures is proposed to understand these features. Moreover, different magnetic anisotropy related to strain-suppressed GdFeO 3-type distortion and Jahn-Teller effect is identified in the films.

Structural, morphological, gas sensing and photocatalytic characterization of MoO3 and WO3 thin films prepared by the thermal vacuum evaporation technique

Science.gov (United States)

Arfaoui, A.; Touihri, S.; Mhamdi, A.; Labidi, A.; Manoubi, T.

2015-12-01

Thin films of molybdenum trioxide and tungsten trioxide were deposited on glass substrates using a simplified thermal evaporation under vacuum method monitored by heat treatment in flowing oxygen at 500 °C for 1 h. The structural and morphological properties of the films were investigated using X-ray diffraction, Raman spectroscopy, atomic force microscopy and scanning electron microscopy. The X-ray diffraction analysis shows that the films of MoO3 and WO3 were well crystallized in orthorhombic and monoclinic phase respectively with the crystallites preferentially oriented toward (2 0 0) direction parallel a-axis for both samples. In literature, we have shown in previous papers that structural and surface morphology of metal thin films play an important role in the gas detection mechanism. In this article, we have studied the response evolution of MoO3 and WO3 thin films sensors ethanol versus time, working temperature and the concentration of the ethanol. It was found that these films had high sensitivity to ethanol, which made them as a good candidate for the ethanol sensor. Finally, the photocatalytic activity of the samples was evaluated with respect to the degradation reaction of a wastewater containing methylene blue (MB) under UV-visible light irradiation. The molybdenum trioxide exhibits a higher degradation rate than the tungsten trioxide thin films under similar experimental conditions.

Biomimetic thin film synthesis

Energy Technology Data Exchange (ETDEWEB)

Graff, G.L.; Campbell, A.A.; Gordon, N.R.

1995-05-01

The purpose of this program is to develop a new process for forming thin film coatings and to demonstrate that the biomimetic thin film technology developed at PNL is useful for industrial applications. In the biomimetic process, mineral deposition from aqueous solution is controlled by organic functional groups attached to the underlying substrate surface. The coatings process is simple, benign, inexpensive, energy efficient, and particularly suited for temperature sensitive substrate materials (such as polymers). In addition, biomimetic thin films can be deposited uniformly on complex shaped and porous substrates providing a unique capability over more traditional line-of-sight methods.

Tuning of Transport and Magnetic Properties in Epitaxial LaMnO3+δ Thin Films

Directory of Open Access Journals (Sweden)

J. Chen

2014-01-01

Full Text Available The effect of compressive strain on the transport and magnetic properties of epitaxial LaMnO3+δ thin films has been investigated. It is found that the transport and magnetic properties of the LaMnO3+δ thin films grown on the LaAlO3 substrates can be tuned by the compressive strain through varying film thickness. And the insulator-metal transition, charge/orbital ordering transition, and paramagnetic-ferromagnetic transition are suppressed by the compressive strain. Consequently, the related electronic and magnetic transition temperatures decrease with an increase in the compressive strain. The present results can be explained by the strain-controlled lattice deformation and the consequent orbital occupation. It indicates that the lattice degree of freedom is crucial for understanding the transport and magnetic properties of the strongly correlated LaMnO3+δ.

Solution processible Cu{sub 2}SnS{sub 3} thin films for cost effective photovoltaics: Characterization

Energy Technology Data Exchange (ETDEWEB)

Dias, Sandra, E-mail: dias.sandra123@gmail.com; Murali, Banavoth; Krupanidhi, S.B.

2015-11-01

Thin films of Cu{sub 2}SnS{sub 3} (CTS) were deposited by the facile solution processed sol–gel route followed by a low-temperature annealing. The Cu–Sn-thiourea complex formation was analysed using Fourier Transform Infrared spectrophotometer (FTIR). The various phase transformations and the deposition temperature range for the initial precursor solution was determined using Thermogravimetric analysis (TGA) and Differential Scanning Calorimetry (DSC). X-Ray Diffraction (XRD) studies revealed the tetragonal phase formation of the CTS annealed films. Raman spectroscopy studies further confirmed the tetragonal phase formation and the absence of any deterioratory secondary phases. The morphological investigations and compositional analysis of the films were determined using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) respectively. Atomic Force Microscopy (AFM) was used to estimate the surface roughness of 1.3 nm. The absorption coefficient was found to be 10{sup 4} cm{sup −1} and bandgap 1.3 eV which qualifies CTS to be a potential candidate for photovoltaic applications. The refractive index, extinction coefficient and relative permittivity of the film were measured by Spectroscopic ellipsometry. Hall effect measurements, indicated the p type nature of the films with a hole concentration of 2 × 10{sup 18} cm{sup −3}, electrical conductivity of 9 S/cm and a hole mobility of 29 cm{sup 2}/V. The properties of CTS as deduced from the current study, present CTS as a potential absorber layer material for thin film solar cells. - Highlights: • Cu{sub 2}SnS{sub 3} thin films have been synthesized by spin coating of a precursor solution. • The Cu–Sn-thiourea complex precursor was analysed. • The structural, optical and electrical properties of the thin films were studied. • Totally 24 infra-red, 30 optical, 29 Raman and 30 hyper Raman modes are active. • Refractive index, extinction coefficient and relative

Morphology, structure, and electrical properties of YBa2Cu3Ox thin films on tilted NdGaO3 substrates, deposited by DC-sputtering

International Nuclear Information System (INIS)

Mozhaev, Peter B.; Kotelyanskii, Iosif M.; Luzanov, Valery A.; Mozhaeva, Julia E.; Donchev, Todor; Mateev, Emil; Nurgaliev, Timur; Bdikin, Igor K.; Narymbetov, Bakhyt Zh.

2005-01-01

Thin YBa 2 Cu 3 O x (YBCO) films were deposited using DC-sputtering technique on NdGaO 3 substrates, tilted from (1 1 0) orientation by 0-26 deg . The structure and surface quality of the substrates were carefully characterized to obtain reliable results of thin films deposition. Structural, morphological and electrical properties of the YBCO thin films show three different ranges of inclination angle: vicinal, intermediate and high. In the vicinal range the properties of the film are generally the same as of the standard films deposited on (1 1 0) NdGaO 3 substrate. An increase of the inclination angle to the intermediate range results in a significant improvement of morphology and structural quality of the film. Best electrical parameters are measured for the films of the intermediate range also. Probable reason for such behavior is simultaneous and regular seeding of the film in the joints of facets on the substrate surface. Further increase of inclination angle leads to step bunching and oxygen out-diffusion, destroying both structural and electrical perfection of the tilted-axes YBCO film

Effect of annealing time on morphological characteristics of Ba(Zr,Ti)O3 thin films

International Nuclear Information System (INIS)

Cavalcante, L.S.; Anicete-Santos, M.; Pontes, F.M.; Souza, I.A.; Santos, L.P.S.; Rosa, I.L.V.; Santos, M.R.M.C.; Santos-Junior, L.S.; Leite, E.R.; Longo, E.

2007-01-01

Ba(Zr 0.50 Ti 0.50 )O 3 thin films were prepared by the polymeric precursor method using the annealing low temperature of 300 o C for 8, 16, 24, 48, 96 and 192h in a furnace tube with oxygen atmosphere. The X-ray diffraction patterns revealed that the film annealed for 192 h presented some crystallographic planes (1bar 0bar 0) (1bar 1bar 0) and (2bar 0bar 0) in its crystalline lattice. Fourier transformed infrared presented the formation of metal-oxygen stretching at around 756cm -1 . The atomic force microscopy analysis presented the growth of granules in the Ba(Zr 0.50 Ti 0.50 )O 3 films annealed from 8 to 96h. The crystalline film annealed for 192h already presents grains in its perovskite structure. It evidenced a reduction in the thickness of the thin films with the increase of the annealing time

Indium sulfide thin films as window layer in chemically deposited solar cells

Energy Technology Data Exchange (ETDEWEB)

Lugo-Loredo, S. [Universidad Autónoma de Nuevo León, UANL, Fac. de Ciencias Químicas, Av. Universidad S/N Ciudad Universitaria San Nicolás de Los Garza Nuevo León, C.P. 66451 (Mexico); Peña-Méndez, Y., E-mail: yolapm@gmail.com [Universidad Autónoma de Nuevo León, UANL, Fac. de Ciencias Químicas, Av. Universidad S/N Ciudad Universitaria San Nicolás de Los Garza Nuevo León, C.P. 66451 (Mexico); Calixto-Rodriguez, M. [Universidad Tecnológica Emiliano Zapata del Estado de Morelos, Av. Universidad Tecnológica No. 1, C.P. 62760 Emiliano Zapata, Morelos (Mexico); Messina-Fernández, S. [Universidad Autónoma de Nayarit, Ciudad de la Cultura “Amado Nervo” S/N, C.P. 63190 Tepic, Nayarit (Mexico); Alvarez-Gallegos, A. [Universidad Autónoma del Estado de Morelos, Centro de Investigación en Ingeniería y Ciencias Aplicadas, Av. Universidad 1001, C.P. 62209, Cuernavaca Morelos (Mexico); Vázquez-Dimas, A.; Hernández-García, T. [Universidad Autónoma de Nuevo León, UANL, Fac. de Ciencias Químicas, Av. Universidad S/N Ciudad Universitaria San Nicolás de Los Garza Nuevo León, C.P. 66451 (Mexico)

2014-01-01

Indium sulfide (In{sub 2}S{sub 3}) thin films have been synthesized by chemical bath deposition technique onto glass substrates using In(NO{sub 3}){sub 3} as indium precursor and thioacetamide as sulfur source. X-ray diffraction studies have shown that the crystalline state of the as-prepared and the annealed films is β-In{sub 2}S{sub 3}. Optical band gap values between 2.27 and 2.41 eV were obtained for these films. The In{sub 2}S{sub 3} thin films are photosensitive with an electrical conductivity value in the range of 10{sup −3}–10{sup −7} (Ω cm){sup −1}, depending on the film preparation conditions. We have demonstrated that the In{sub 2}S{sub 3} thin films obtained in this work are suitable candidates to be used as window layer in thin film solar cells. These films were integrated in SnO{sub 2}:F/In{sub 2}S{sub 3}/Sb{sub 2}S{sub 3}/PbS/C–Ag solar cell structures, which showed an open circuit voltage of 630 mV and a short circuit current density of 0.6 mA/cm{sup 2}. - Highlights: • In{sub 2}S{sub 3} thin films were deposited using the Chemical Bath Deposition technique. • A direct energy band gap between 2.41 to 2.27 eV was evaluated for the In{sub 2}S{sub 3} films. • We made chemically deposited solar cells using the In{sub 2}S{sub 3} thin films.

Effect of preparation conditions on the properties of Cu3BiS3 thin films grown by a two - step process

Science.gov (United States)

Mesa, F.; Gordillo, G.

2009-05-01

Cu3BiS3 thin films were prepared on soda-lime glass substrates by co-evaporation of the precursors in a two-step process; for that, the metallic precursors were evaporated from a tungsten boat in presence of elemental sulfur evaporated from a tantalum effusion cell. The films were characterized by spectral transmittance, atomic force microscopy AFM and x-ray diffraction (XRD) measurements to investigate the effect of the growth conditions on the optical, morphological and structural properties. The results revealed that, independently of the deposition conditions, the films grow only in the orthorhombic Cu3BiS3 phase. It was also found that the Cu3BiS3 films present p-type conductivity, a high absorption coefficient (greater than 104 cm-1) and an energy band gap Eg of about 1.41 eV, indicating that this compound has good properties to perform as absorbent layer in thin film solar cells.

Preparation and characterization of poly(3,4-ethylenedioxythiophene)-poly(styrene sulfonate) composite thin films highly loaded with platinum nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Chang, Chao-Ching, E-mail: ccchang@tku.edu.tw [Department of Chemical and Materials Engineering, Tamkang University, No. 151, Yingzhuan Rd., Danshui Dist., New Taipei City 25137, Taiwan (China); Energy and Opto-Electronic Materials Research Center, Tamkang University, No. 151, Yingzhuan Rd., Danshui Dist., New Taipei City 25137, Taiwan (China); Jiang, Ming-Tai [Department of Chemical and Materials Engineering, Tamkang University, No. 151, Yingzhuan Rd., Danshui Dist., New Taipei City 25137, Taiwan (China); Chang, Chen-Liang; Lin, Cheng-Lan [Department of Chemical and Materials Engineering, Tamkang University, No. 151, Yingzhuan Rd., Danshui Dist., New Taipei City 25137, Taiwan (China); Energy and Opto-Electronic Materials Research Center, Tamkang University, No. 151, Yingzhuan Rd., Danshui Dist., New Taipei City 25137, Taiwan (China)

2011-06-15

Research highlights: {yields} Nano-sized and mono-dispersed Pt nanoparticles were synthesized by a polyol method. {yields} A thin film of PEDOT:PSS loaded with high concentration of Pt nanoparticles has been prepared. {yields} The PEDOT:PSS-Pt modified electrode has good potential to serve as a counter electrode in DSSC. - Abstract: In this work, we propose a simple and efficient, low-temperature ({approx}120 deg. C) process to prepare transparent thin films of poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) loaded with high concentration (up to 22.5 wt%) of platinum (Pt) nanoparticles. Firstly, an improved polyol method was modified to synthesize nano-sized ({approx}5 nm) and mono-dispersed Pt particles. These nanoparticles were incorporated into the matrix of PEDOT:PSS thin films via a spin coating/drying procedure. The electrochemical activities of the PEDOT:PSS thin film modified electrodes with respect to the I{sup -}/I{sub 3}{sup -} redox reactions were investigated. It was found that the modified electrode of PEDOT:PSS thin film containing 22.5 wt% Pt exhibited the electrochemical activity comparable to the conventional Pt thin film electrode, suggesting that this electrode has good potential to serve as a counter electrode in dye-sensitized solar cells.

Analysis of multiferroic properties in BiMnO3 thin films

International Nuclear Information System (INIS)

Grizalez, M; Mendoza, G A; Prieto, P

2009-01-01

Textured BiMnO 3 [111] thin films on SrTiO 3 (100) and Pt/TiO 2 /SiO 2 substrates were grown via r.f. magnetron sputtering (13.56 MHz). The XRD spectra confirmed a monoclinic structure and high-quality textured films for the BiMnO 3 films. The films grown on SrTiO 3 (100) showed higher crystalline quality than those developed on Pt/TiO 2 /SiO 2 . Through optimized oxygen pressure of 5x10 -2 mbar during the r.f. sputtering deposition, the crystalline orientation of the BiMnO 3 film was improved with respect to the previously reported value of 2x10 -1 mbar. The values of spontaneous polarization (P s ), remnant polarization (P r ), and coercive field (F c ) from ferroelectric hysteresis loops (P-E) at different temperatures were also obtained. Samples with higher crystalline order revealed better dielectric properties (high P s and P r values and a low F c ). For films on both types of substrates, the ferroelectric behavior was found to persist up to 400K. Measurements at higher temperatures were difficult to obtain given the increased conductivity of the films. Magnetic hysteresis loops from 5K to 120K were obtained for BiMnO 3 films grown on SrTiO 3 and Pt/TiO 2 /SiO 2 substrates. The results suggested that the coexistence of the magnetic and electric phases persists up to 120K.

Hall effect of K-doped superconducting thin films

Energy Technology Data Exchange (ETDEWEB)

Son, Eunseon; Lee, Nam Hoon; Kang, Won Nam [Dept. of physics, Sungkyunkwan University, Suwon (Korea, Republic of); Hwang, Tae Jong; Kim, Dong Ho [Dept. of physics, Yeungnam University, Gyeongsan(Korea, Republic of)

2013-09-15

We have studied Hall effect for potassium (K)-doped BaFe{sub 2}As{sub 2}superconducting thin films by analyzing the relation between the longitudinal resistivity (ρ{sub xy}) and the Hall resistivity (ρ{sub xy}). The thin films used in this study were fabricated on Al{sub O3} (000l) substrates by using an ex-situ pulsed laser deposition (PLD) technique under a high-vacuum condition of ∼10{sup -6} Torr. The samples showed the high superconducting transition temperatures (T{sub C}) of ∼40 K. The ρ{sub xx} and ρ{sub xy}the for K-doped BaFeAs{sub 2} thin films were measured by using a physical property measurement system (PPMS) with a temperature sweep (T-sweep) mode at an applied current density of 100 A/cm{sup 2} and at magnetic fields from 0 up to 9 T. We report the T-sweep results of the ρ{sub xx} and the ρ{sub xy} to investigate Hall scaling behavior on the basis of the relation of ρ{sub xy} = A(ρ{sub xy}){sup β}. The ρ{sub xx} values are 3.0 ± 0.2 in the c-axis-oriented K-doped BaFeAs{sub 2} thin films, whereas the thin films with various oriented-directions like a polycrystal showed slightly lower β than that of c-axis-oriented thin films. Interestingly, the β value is decreased with increasing magnetic fields.

YBa2Cu3O(7-x) based superconducting thin films by multitarget sputtering

International Nuclear Information System (INIS)

Bouteloup, E.; Mercey, B.; Poullain, G.; Brousse, T.; Murray, H.; Raveau, B.

1990-01-01

This paper reports a new technique to prepare superconducting YBa 2 Cu 3 O (7-x) thin films. The multitarget sputtering apparatus described below allows the simultaneous and reproducible production of numerous films with a metallic composition close to Y 17% Ba 33% Cu 50% . Superconducting films (R = 0) at 80 K have been produced on polycrystalline zirconia substrates after a high temperature annealing [fr

Ultrafast Magnetization Dynamics of SrRuO3 Thin Films

International Nuclear Information System (INIS)

Langner, Matthew C.

2009-01-01

Itinerant ferromagnet SrRuO3 has drawn interest from physicists due to its unusual transport and magnetic properties as well as from engineers due to its low resistivity and good lattice-matching to other oxide materials. The exact electronic structure remains a mystery, as well as details of the interactions between magnetic and electron transport properties. This thesis describes the use of time-resolved magneto-optical Kerr spectroscopy to study the ferromagnetic resonance of SrRuO3 thin films, where the ferromagnetic resonance is initiated by a sudden change in the easy axis direction in response to a pump pulse. The rotation of the easy axis is induced by laser heating, taking advantage of a temperature-dependent easy axis direction in SrRuO3 thin films. By measuring the change in temperature of the magnetic system in response to the laser pulse, we find that the specific heat is dominated by magnons up to unusually high temperature, ∼ 100 K, and thermal diffusion is limited by a boundary resistance between the film and the substrate that is not consistent with standard phonon reflection and scattering models. We observe a high FMR frequency, 250 GHz, and large Gilbert damping parameter, alpha ∼ 1, consistent with strong spin-orbit coupling. We observe a time-dependent change in the easy axis direction on a ps time-scale, and we find that parameters associated with the change in easy axis, as well as the damping parameter, have a non-monotonic temperature dependence similar to that observed in anomalous Hall measurements.

Fabrication and characterization of In2S3 thin films deposited by thermal evaporation technique

International Nuclear Information System (INIS)

Timoumi, A.; Bouzouita, H.; Kanzari, M.; Rezig, B.

2005-01-01

Indium sulphide, In 2 S 3 , thin films present an alternative to conventional CdS films as buffer layer for CIS-based thin film solar cells. The objective is to eliminate toxic cadmium for environmental reasons. Indium sulphide is synthesized and deposited by single source vacuum thermal evaporation method on glass substrates. The films are analyzed by X-ray diffraction (XRD) and spectrophotometric measurements. They have a good crystallinity, homogeneity and adhesion. The X-ray diffraction analysis confirmed the initial amorphous nature of the deposited InS film and phase transition into crystalline In 2 S 3 formed upon annealing at free air for 250 deg. C substrate temperature for 2 h. The optical constants of the deposited films were obtained from the analysis of the experimental recorded transmission and reflectance spectral data over the wavelength range of 300-1800 nm. We note that the films annealed at 250 deg. C for 2 h show a good homogeneity with 80% transmission. An analysis of the optical absorption data of the deposited films revealed an optical direct band gap energy in the range of 2.0-2.2 eV

Molecular dynamics simulation of Cu/Au thin films under temperature gradient

International Nuclear Information System (INIS)

Li, Qibin; Peng, Xianghe; Peng, Tiefeng; Tang, Qizhong; Zhang, Xiaomin; Huang, Cheng

2015-01-01

Graphical abstract: Heat transportation in the thin films. - Highlights: • The coherent lattice interface is found at thin films after annealing. • The vacancies are observed clearly in the deposit thin films. • The defect and component will influence the energy transportation in the coatings. • The vacancies and lattice mismatch can enlarge the mobility of atoms. • The phonon transportation in thin films has no apparent rule. - Abstract: Three modulation period thin films, 1.8 nm Cu/3.6 nm Au, 2.7 nm Cu/2.7 nm Au and 3.6 nm Cu/1.8 nm Au, are obtained from deposition method and ideal modeling based on lattice constant, to examine their structures and thermophysical characteristics under temperature gradient. The coherent lattice interface is found both at deposit and ideal thin films after annealing. Also, the vacancies are observed clearly in the deposit thin films. The defect and component of thin films will influence the energy transportation in the coatings. The vacancies and lattice mismatch can enlarge the mobility of atoms and result in the failure of coating under the thermal stress. The power spectrum of atoms’ movement has no apparent rule for phonon transportation in thin films. The results are helpful to reveal the micro-mechanism and provide reasonable basis for the failure of metallic coatings.

Molecular dynamics simulation of Cu/Au thin films under temperature gradient

Energy Technology Data Exchange (ETDEWEB)

Li, Qibin, E-mail: qibinli@cqu.edu.cn [College of Aerospace Engineering, Chongqing University, Chongqing 400030 (China); State Key Laboratory of Coal Mine Disaster Dynamics and Control, Chongqing University, Chongqing 400030 (China); Chongqing Key Laboratory of Heterogeneous Material Mechanics, Chongqing University, Chongqing 400030 (China); Peng, Xianghe [College of Aerospace Engineering, Chongqing University, Chongqing 400030 (China); State Key Laboratory of Coal Mine Disaster Dynamics and Control, Chongqing University, Chongqing 400030 (China); Peng, Tiefeng, E-mail: pengtiefeng@cqu.edu.cn [State Key Laboratory of Coal Mine Disaster Dynamics and Control, Chongqing University, Chongqing 400030 (China); Tang, Qizhong [College of Aerospace Engineering, Chongqing University, Chongqing 400030 (China); Zhang, Xiaomin [College of Aerospace Engineering, Chongqing University, Chongqing 400030 (China); Chongqing Key Laboratory of Heterogeneous Material Mechanics, Chongqing University, Chongqing 400030 (China); Huang, Cheng [College of Aerospace Engineering, Chongqing University, Chongqing 400030 (China)

2015-12-01

Graphical abstract: Heat transportation in the thin films. - Highlights: • The coherent lattice interface is found at thin films after annealing. • The vacancies are observed clearly in the deposit thin films. • The defect and component will influence the energy transportation in the coatings. • The vacancies and lattice mismatch can enlarge the mobility of atoms. • The phonon transportation in thin films has no apparent rule. - Abstract: Three modulation period thin films, 1.8 nm Cu/3.6 nm Au, 2.7 nm Cu/2.7 nm Au and 3.6 nm Cu/1.8 nm Au, are obtained from deposition method and ideal modeling based on lattice constant, to examine their structures and thermophysical characteristics under temperature gradient. The coherent lattice interface is found both at deposit and ideal thin films after annealing. Also, the vacancies are observed clearly in the deposit thin films. The defect and component of thin films will influence the energy transportation in the coatings. The vacancies and lattice mismatch can enlarge the mobility of atoms and result in the failure of coating under the thermal stress. The power spectrum of atoms’ movement has no apparent rule for phonon transportation in thin films. The results are helpful to reveal the micro-mechanism and provide reasonable basis for the failure of metallic coatings.

Persistent semi-metal-like nature of epitaxial perovskite CaIrO{sub 3} thin films

Energy Technology Data Exchange (ETDEWEB)

Biswas, Abhijit; Jeong, Yoon Hee, E-mail: yhj@postech.ac.kr [Department of Physics, POSTECH, Pohang 790-784 (Korea, Republic of)

2015-05-21

Strong spin-orbit coupled 5d transition metal based ABO{sub 3} oxides, especially iridates, allow tuning parameters in the phase diagram and may demonstrate important functionalities, for example, by means of strain effects and symmetry-breaking, because of the interplay between the Coulomb interactions and strong spin-orbit coupling. Here, we have epitaxially stabilized high quality thin films of perovskite (Pv) CaIrO{sub 3}. Film on the best lattice-matched substrate shows semi-metal-like characteristics. Intriguingly, imposing tensile or compressive strain on the film by altering the underlying lattice-mismatched substrates still maintains semi-metallicity with minute modification of the effective correlation as tensile (compressive) strain results in tiny increases (decreases) of the electronic bandwidth. In addition, magnetoresistance remains positive with a quadratic field dependence. This persistent semi-metal-like nature of Pv-CaIrO{sub 3} thin films with minute changes in the effective correlation by strain may provide new wisdom into strong spin-orbit coupled 5d based oxide physics.

Pulsed laser deposited Al-doped ZnO thin films for optical applications

Directory of Open Access Journals (Sweden)

Gurpreet Kaur

2015-02-01

Full Text Available Highly transparent and conducting Al-doped ZnO (Al:ZnO thin films were grown on glass substrates using pulsed laser deposition technique. The profound effect of film thickness on the structural, optical and electrical properties of Al:ZnO thin films was observed. The X-ray diffraction depicts c-axis, plane (002 oriented thin films with hexagonal wurtzite crystal structure. Al-doping in ZnO introduces a compressive stress in the films which increase with the film thickness. AFM images reveal the columnar grain formation with low surface roughness. The versatile optical properties of Al:ZnO thin films are important for applications such as transparent electromagnetic interference (EMI shielding materials and solar cells. The obtained optical band gap (3.2–3.08 eV was found to be less than pure ZnO (3.37 eV films. The lowering in the band gap in Al:ZnO thin films could be attributed to band edge bending phenomena. The photoluminescence spectra gives sharp visible emission peaks, enables Al:ZnO thin films for light emitting devices (LEDs applications. The current–voltage (I–V measurements show the ohmic behavior of the films with resistivity (ρ~10−3 Ω cm.

Thin Film Photovoltaic Partnership Project | Photovoltaic Research | NREL

Science.gov (United States)

Thin Film Photovoltaic Partnership Project Thin Film Photovoltaic Partnership Project NREL's Thin Film Photovoltaic (PV) Partnership Project led R&D on emerging thin-film solar technologies in the United States from 1994 to 2009. The project made many advances in thin-film PV technologies that allowed

Ga2O3-In2O3 thin films on sapphire substrates: Synthesis and ultraviolet photoconductivity

Science.gov (United States)

Muslimov, A. E.; Butashin, A. V.; Kolymagin, A. B.; Nabatov, B. V.; Kanevsky, V. M.

2017-11-01

The structure and electrical and optical properties of β-Ga2O3-In2O3 thin films on sapphire substrates with different orientations have been investigated. The samples have been prepared by annealing of gallium-indium metallic films on sapphire substrates in air at different gallium-to-indium ratios in the initial mixture. The photoconductivity of these structures in the solar-blind ultraviolet spectral region has been examined.

Thin Film & Deposition Systems (Windows)

Data.gov (United States)

Federal Laboratory Consortium — Coating Lab: Contains chambers for growing thin film window coatings. Plasma Applications Coating Lab: Contains chambers for growing thin film window coatings. Solar...

Antimicrobial effect of Al2O3, Ag and Al2O3/Ag thin films on Escherichia coli and Pseudomonas putida

International Nuclear Information System (INIS)

Angelov, O; Stoyanova, D; Ivanova, I; Todorova, S

2016-01-01

The influence of Al 2 O 3 , Ag and Al 2 O 3 /Ag thin films on bacterial growth of Gramnegative bacteria Pseudomonas putida and Escherichia coli is studied. The nanostructured thin films are deposited on glass substrates without intentional heating through r.f. magnetron sputtering in Ar atmosphere of Al 2 O 3 and Ag targets or through sequential sputtering of Al 2 O 3 and Ag targets, respectively. The individual Ag thin films (thickness 8 nm) have a weak bacteriostatic effect on Escherichia coli expressed as an extended adaptive phase of the bacteria up to 5 hours from the beginning of the experiment, but the final effect is only 10 times lower bacterial density than in the control. The individual Al 2 O 3 film (20 nm) has no antibacterial effect against two strains E. coli - industrial and pathogenic. The Al 2 O 3 /Ag bilayer films (Al 2 O 3 20 nm/Ag 8 nm) have strong bactericidal effect on Pseudomonas putida and demonstrate an effective time of disinfection for 2 hours. The individual films Al2O3 and Ag have not pronounced antibacterial effect on Pseudomonas putida . A synergistic effect of Al2O3/Ag bilayer films in formation of oxidative species on the surface in contact with the bacterial suspension could be a reason for their antimicrobial effect on E. coli and P. putida . (paper)

Nanoscale Control of Exchange Bias with BiFeO3 Thin Films

NARCIS (Netherlands)

Martin, Lane W.; Chu, Ying-Hao; Holcomb, Mikel B.; Huijben, Mark; Yu, Pu; Han, Shu-Jen; Lee, Donkoun; Wang, Shan X.; Ramesh, R.

2008-01-01

We demonstrate a direct correlation between the domain structure of multiferroic BiFeO3 thin films and exchange bias of Co0.9Fe0.1/BiFeO3 heterostructures. Two distinct types of interactions − an enhancement of the coercive field (exchange enhancement) and an enhancement of the coercive field

Purely hopping conduction in c-axis oriented LiNbO3 thin films

Science.gov (United States)

Shandilya, Swati; Tomar, Monika; Sreenivas, K.; Gupta, Vinay

2009-05-01

Dielectric constant and ac conductivity of highly c-axis oriented LiNbO3 thin film grown by pulsed laser deposition were studied in a metal-insulator-metal configuration over a wide temperature (200 to 450 K) and frequency (100 Hz to 1 MHz) range. The preferred oriented Al (1%) doped ZnO film with electrical conductivity 1.1×103 Ω-1 cm-1 was deposited for dual purpose: (1) to serve as nucleating center for LiNbO3 crystallites along preferred c-axis growth direction, and (2) to act as a suitable bottom electrode for electrical studies. The room temperature dc conductivity (σdc) of LiNbO3 film was about 5.34×10-10 Ω-1 cm-1 with activation energy ˜0.3 eV, indicating extrinsic conduction. The ac conductivity σac was found to be much higher in comparison to σdc in the low temperature region (300 K), σac shows a weak frequency dependence, whereas dielectric constant exhibits a strong frequency dispersion. The dielectric dispersion data has been discussed in the light of theoretical models based on Debye type mixed conduction and purely hopping conduction. The dominant conduction in c-axis oriented LiNbO3 thin film is attributed to the purely hopping where both σdc and σac arise due to same mechanism.

Effect of precursor concentration on physical properties of nebulized spray deposited In2S3 thin films

Directory of Open Access Journals (Sweden)

J. Raj Mohamed

2016-09-01

Full Text Available The present work investigates the effect of precursor concentration (mc on the structural, optical, morphological and electrical conductivity properties of In2S3 thin films grown on amorphous glass substrates by nebulized spray pyrolysis (NSP technique. The mixed phase of cubic and tetragonal structure of In2S3 thin films at higher concentration has been observed by X-ray diffraction pattern. The reduced strain by increasing the precursor concentration increased the average crystallite from 17.8 to 28.9 nm. The energy dispersive analysis by X-ray (EDAX studies confirmed the presence of In and S. The transmittance, optical direct band gap energy, Urbach energy and skin depth of In2S3 films have been analyzed by optical absorption spectra. The better conductivity and mobility noticed at mc = 0.15 M are explained by carrier concentration and crystallite. Better optical and electrical conductivity behaviour of In2S3 thin film sample proposes for effective solar cell fabrication.

Structure-property relations in sputter deposited epitaxial (1-x)Pb(Mg1/3Nb2/3)O3- xPbTiO3 thin films

Science.gov (United States)

Frederick, Joshua C.

Lead-based ferroelectric materials are of significant technological importance for sensing and actuation due to their high piezoelectric performance (i.e., the ability to convert an electrical signal to mechanical displacement, and vice versa). Traditionally, bulk ceramic or single crystals materials have filled these roles; however, emerging technologies stand to benefit by incorporating thin films to achieve miniaturization while maintaining high efficiency and sensitivity. Currently, chemical systems that have been well characterized in bulk form (e.g. Pb(Mg1/3Nb2/3)O3- xPbTiO3, or PMN-xPT) require further study to optimize both the chemistry and structure for deployment in thin film devices. Furthermore, the effect of internal electric fields is more significant at the length scales of thin films, resulting in self biases that require compensation to reveal their intrinsic dielectric response. To this end, the structure-property relations of epitaxial PMN-xPT films sputter deposited on a variety of substrates were investigated. Attention was paid to how the structure (i.e., strain state, crystal structure, domain configuration, and defects) gave rise to the ferroelectric, dielectric, and piezoelectric response. Three-dimensional visualization of the dielectric response as a simultaneous function of electric field and temperature revealed the true phase transition of the films, which was found to correspond to the strain state and defect concentration. A lead-buffered anneal process was implemented to enhance the ferroelectric and dielectric response of the films without altering their stoichiometry. It was discovered that PMN- xPT films could be domain-engineered to exhibit a mixed domain state through chemistry and substrate choice. Such films exhibited a monoclinic distortion similar to that of the bulk compositions near the morphotropic phase boundary. Finally, it was revealed that the piezoelectric response could be greatly enhanced by declamping the film

Valence control of cobalt oxide thin films by annealing atmosphere

International Nuclear Information System (INIS)

Wang Shijing; Zhang Boping; Zhao Cuihua; Li Songjie; Zhang Meixia; Yan Liping

2011-01-01

The cobalt oxide (CoO and Co 3 O 4 ) thin films were successfully prepared using a spin-coating technique by a chemical solution method with CH 3 OCH 2 CH 2 OH and Co(NO 3 ) 2 .6H 2 O as starting materials. The grayish cobalt oxide films had uniform crystalline grains with less than 50 nm in diameter. The phase structure is able to tailor by controlling the annealing atmosphere and temperature, in which Co 3 O 4 thin film was obtained by annealing in air at 300-600, and N 2 at 300, and transferred to CoO thin film by raising annealing temperature in N 2 . The fitted X-ray photoelectron spectroscopy (XPS) spectra of the Co2p electrons are distinguishable from different valence states of cobalt oxide especially for their satellite structure. The valence control of cobalt oxide thin films by annealing atmosphere contributes to the tailored optical absorption property.

Characterization of organic thin films

CERN Document Server

Ulman, Abraham; Evans, Charles A

2009-01-01

Thin films based upon organic materials are at the heart of much of the revolution in modern technology, from advanced electronics, to optics to sensors to biomedical engineering. This volume in the Materials Characterization series introduces the major common types of analysis used in characterizing of thin films and the various appropriate characterization technologies for each. Materials such as Langmuir-Blodgett films and self-assembled monolayers are first introduced, followed by analysis of surface properties and the various characterization technologies used for such. Readers will find detailed information on: -Various spectroscopic approaches to characterization of organic thin films, including infrared spectroscopy and Raman spectroscopy -X-Ray diffraction techniques, High Resolution EELS studies, and X-Ray Photoelectron Spectroscopy -Concise Summaries of major characterization technologies for organic thin films, including Auger Electron Spectroscopy, Dynamic Secondary Ion Mass Spectrometry, and Tra...

Piezoelectric characterization of Pb(Zr,Ti)O3 thin films deposited on metal foil substrates by dip coating

Science.gov (United States)

Hida, Hirotaka; Hamamura, Tomohiro; Nishi, Takahito; Tan, Goon; Umegaki, Toshihito; Kanno, Isaku

2017-10-01

We fabricated the piezoelectric bimorphs composed of Pb(Zr,Ti)O3 (PZT) thin films on metal foil substrates. To efficiently inexpensively manufacture piezoelectric bimorphs with high flexibility, 1.2-µm-thick PZT thin films were directly deposited on both surfaces of 10- and 20-µm-thick bare stainless-steel (SS) foil substrates by dip coating with a sol-gel solution. We confirmed that the PZT thin films deposited on the SS foil substrates at 500 °C or above have polycrystalline perovskite structures and the measured relative dielectric constant and dielectric loss were 323-420 and 0.12-0.17, respectively. The PZT bimorphs were demonstrated by comparing the displacements of the cantilever specimens driven by single- and double-side PZT thin films on the SS foil substrates under the same applied voltage. We characterized the piezoelectric properties of the PZT bimorphs and the calculated their piezoelectric coefficient |e 31,f| to be 0.3-0.7 C/m2.

Preparation of Pb(Zr, Ti)O3 Thin Films on Glass Substrates

Science.gov (United States)

Hioki, Tsuyoshi; Akiyama, Masahiko; Ueda, Tomomasa; Onozuka, Yutaka; Hara, Yujiro; Suzuki, Kouji

2000-09-01

Lead-zirconate-titanate (PZT) thin films were prepared on non-alkaline glass substrates widely used in liquid crystal display (LCD) devices, by plasma-assisted magnetron RF sputtering with an immersed coil. After preparation of the PZT thin film, the glass was available for use in LCD device processing. No mutual diffusion of the elements was recognized between the glass substrate and the bottom electrode. The PZT layer had a dense film structure with rectangular and columnar grains, and only its perovskite phase was crystalline. PZT thin films on a glass substrate had leakage current densities of about 10-8 A/cm2, acceptable hysteresis loop shapes with the remanent polarization (Pr) of 45 μC/cm2 and the coercive field (Ec) of 90 kV/cm. Ferroelectric properties on a glass substrate almost conform with those on a Si-based substrate.

Flexible thin film magnetoimpedance sensors

International Nuclear Information System (INIS)

Kurlyandskaya, G.V.; Fernández, E.; Svalov, A.; Burgoa Beitia, A.; García-Arribas, A.; Larrañaga, A.

2016-01-01

Magnetically soft thin film deposited onto polymer substrates is an attractive option for flexible electronics including magnetoimpedance (MI) applications. MI FeNi/Ti based thin film sensitive elements were designed and prepared using the sputtering technique by deposition onto rigid and flexible substrates at different deposition rates. Their structure, magnetic properties and MI were comparatively analyzed. The main structural features were sufficiently accurately reproduced in the case of deposition onto cyclo olefine polymer substrates compared to glass substrates for the same conditions. Although for the best condition (28 nm/min rate) of the deposition onto polymer a significant reduction of the MI field sensitivity was found satisfactory for sensor applications sensitivity: 45%/Oe was obtained for a frequency of 60 MHz. - Highlights: • [FeNi/Ti] 3 /Cu/[FeNi/Ti] 3 films were prepared by sputtering at different deposition rates. • Polymer substrates insure sufficiently accurate reproducibility of the film structure. • High deposition rate of 28 nm/min insures the highest values of the magnetoimpedance sensitivity. • Deposition onto polymer results in the satisfactory magnetoimpedance sensitivity of 45%/Oe.

Flexible thin film magnetoimpedance sensors

Energy Technology Data Exchange (ETDEWEB)

Kurlyandskaya, G.V., E-mail: galina@we.lc.ehu.es [Universidad del País Vasco, UPV/EHU, Departamento de Electricidad y Electrónica, P.O. Box 644, Bilbao 48080 (Spain); Ural Federal University, Laboratory of Magnetic sensoric, Lenin Ave. 51, 620083 Ekaterinburg (Russian Federation); Fernández, E. [BCMaterials UPV-EHU, Vizcaya Science and Technology Park, 48160 Derio (Spain); Svalov, A. [Universidad del País Vasco, UPV/EHU, Departamento de Electricidad y Electrónica, P.O. Box 644, Bilbao 48080 (Spain); Ural Federal University, Laboratory of Magnetic sensoric, Lenin Ave. 51, 620083 Ekaterinburg (Russian Federation); Burgoa Beitia, A. [Universidad del País Vasco, UPV/EHU, Departamento de Electricidad y Electrónica, P.O. Box 644, Bilbao 48080 (Spain); García-Arribas, A. [Universidad del País Vasco, UPV/EHU, Departamento de Electricidad y Electrónica, P.O. Box 644, Bilbao 48080 (Spain); BCMaterials UPV-EHU, Vizcaya Science and Technology Park, 48160 Derio (Spain); Larrañaga, A. [SGIker, Servicios Generales de Investigación, Universidad del País Vasco (UPV/EHU), 48080 Bilbao (Spain)

2016-10-01

Magnetically soft thin film deposited onto polymer substrates is an attractive option for flexible electronics including magnetoimpedance (MI) applications. MI FeNi/Ti based thin film sensitive elements were designed and prepared using the sputtering technique by deposition onto rigid and flexible substrates at different deposition rates. Their structure, magnetic properties and MI were comparatively analyzed. The main structural features were sufficiently accurately reproduced in the case of deposition onto cyclo olefine polymer substrates compared to glass substrates for the same conditions. Although for the best condition (28 nm/min rate) of the deposition onto polymer a significant reduction of the MI field sensitivity was found satisfactory for sensor applications sensitivity: 45%/Oe was obtained for a frequency of 60 MHz. - Highlights: • [FeNi/Ti]{sub 3}/Cu/[FeNi/Ti]{sub 3} films were prepared by sputtering at different deposition rates. • Polymer substrates insure sufficiently accurate reproducibility of the film structure. • High deposition rate of 28 nm/min insures the highest values of the magnetoimpedance sensitivity. • Deposition onto polymer results in the satisfactory magnetoimpedance sensitivity of 45%/Oe.

Room Temperature Tunable Multiferroic Properties in Sol-Gel-Derived Nanocrystalline Sr(Ti1−xFexO3−δ Thin Films

Directory of Open Access Journals (Sweden)

Yi-Guang Wang

2017-09-01

Full Text Available Sr(Ti1−xFexO3−δ (0 ≤ x ≤ 0.2 thin films were grown on Si(100 substrates with LaNiO3 buffer-layer by a sol-gel process. Influence of Fe substitution concentration on the structural, ferroelectric, and magnetic properties, as well as the leakage current behaviors of the Sr(Ti1−xFexO3−δ thin films, were investigated by using the X-ray diffractometer (XRD, atomic force microscopy (AFM, the ferroelectric test system, and the vibrating sample magnetometer (VSM. After substituting a small amount of Ti ion with Fe, highly enhanced ferroelectric properties were obtained successfully in SrTi0.9Ti0.1O3−δ thin films, with a double remanent polarization (2Pr of 1.56, 1.95, and 9.14 μC·cm−2, respectively, for the samples were annealed in air, oxygen, and nitrogen atmospheres. The leakage current densities of the Fe-doped SrTiO3 thin films are about 10−6–10−5 A·cm−2 at an applied electric field of 100 kV·cm−1, and the conduction mechanism of the thin film capacitors with various Fe concentrations has been analyzed. The ferromagnetic properties of the Sr(Ti1−xFexO3−δ thin films have been investigated, which can be correlated to the mixed valence ions and the effects of the grain boundary. The present results revealed the multiferroic nature of the Sr(Ti1−xFexO3−δ thin films. The effect of the annealing environment on the room temperature magnetic and ferroelectric properties of Sr(Ti0.9Fe0.1O3−δ thin films were also discussed in detail.