Sample records for thallium alloys

  1. IRIS Toxicological Review of Thallium and Compounds ... (United States)

    Thallium compounds are used in the semiconductor industry, the manufacture of optic lenses and low-melting glass, low-temperature thermometers, alloys, electronic devices, mercury lamps, fireworks, and imitation germs, and clinically as an imaging agent in the diagnosis of certain tumors. EPA's assessment of noncancer health effects and carcinogenic potential of thallium compounds was last prepared and added to the IRIS database between 1988 and 1990. The IRIS program is preparing an assessment that will incorporate current health effects information available for thallium and compounds, and current risk assessment methods. The IRIS assessment for thallium compounds will consist of a Toxicological Review and IRIS Summary. The Toxicological Review is a critical review of the physiochemical and toxicokinetic properties of a chemical, and its toxicity in humans and experimental systems. The assessment will present reference values for the noncancer effects of thallium compounds (RfD and Rfc), and a cancer assessment. The Toxicological Review and IRIS Summary have been subject to Agency review, Interagency review, and external scientific peer review. The final product will reflect the Agency opinion on the overall toxicity of thallium and compounds. EPA is undertaking an Integrated Risk Information System (IRIS) health assessment for thallium and compounds. IRIS is an EPA database containing Agency scientific positions on potential adverse human health effec

  2. Extraction separation of thallium (III) from thallium (I) with n-octylaniline. (United States)

    Shilimkar, Tulshidas N; Anuse, Mansing A; Patil, Kesharsingh J


    A novel method is developed for the extraction separation of thallium(III) from salicylate medium with n-octylaniline dissolved in toluene as an extractant. The optimum conditions have been determined by making a critical study of weak acid concentration, extractant concentration, period of equilibration and effect of solvent on the equilibria. The thallium (III) from the pregnant organic phase is stripped with acetate buffer solution (pH 4.7) and determined complexometrically with EDTA. The method affords the sequential separation of thallium(III) from thallium(I) and also commonly associated metal ions such as Al(III), Ga(III), In(III), Fe(III), Bi(III), Sb(III) and Pb(II). It is used for analysis of synthetic mixtures of associated metal ions and alloys. The method is highly selective, simple and reproducible. The reaction takes place at room temperature and requires 15-20 min for extraction and determination of thallium(III).

  3. IRIS Toxicological Review of Thallium and Compounds (External Review Draft) (United States)

    Thallium compounds are used in the semiconductor industry, the manufacture of optic lenses and low-melting glass, low-temperature thermometers, alloys, electronic devices, mercury lamps, fireworks, and imitation germs, and clinically as an imaging agent in the diagnosis of certai...

  4. Sodium dithionite as a selective demasking agent for the complexometric determination of thallium

    Directory of Open Access Journals (Sweden)



    Full Text Available Sodium dithionite is proposed as a new demasking agent for the rapid and selective complexometric determination of thallium(III. In the presence of diverse metal ions, thallium (III was first complexed with excess EDTA and the surplus EDTAwas then titrated with a standard zinc sulphate solution at pH 5–6 (hexamine buffer using Xylenol Orange as the indicator. The EDTAequivalent to thallium was then released selectively with sodium dithionite and back titrated with a standard zinc sulphate solution as before. Reproducible and accurate results were obtained in the range 4–100 mg of thallium with a relative error of ±27 % and a coefficient of variation (n = 6 of not more than 0.30 %. The effects of various diverse ions were studied. The method was applied to the determination of thallium in its complexes and in alloys.

  5. Extracorporeal treatment for thallium poisoning

    DEFF Research Database (Denmark)

    Ghannoum, Marc; Nolin, Thomas D; Goldfarb, David S


    The EXtracorporeal TReatments In Poisoning (EXTRIP) workgroup was formed to provide recommendations on the use of extracorporeal treatment (ECTR) in poisoning. To test and validate its methods, the workgroup reviewed data for thallium (Tl)....

  6. Thermodynamic Study of Tl6SBr4 Compound and Some Regularities in Thermodynamic Properties of Thallium Chalcohalides

    Directory of Open Access Journals (Sweden)

    Dunya Mahammad Babanly


    Full Text Available The solid-phase diagram of the Tl-TlBr-S system was clarified and the fundamental thermodynamic properties of Tl6SBr4 compound were studied on the basis of electromotive force (EMF measurements of concentration cells relative to a thallium electrode. The EMF results were used to calculate the relative partial thermodynamic functions of thallium in alloys and the standard integral thermodynamic functions (-ΔfG0, -ΔfH0, and S0298 of Tl6SBr4 compound. All data regarding thermodynamic properties of thallium chalcogen-halides are generalized and comparatively analyzed. Consequently, certain regularities between thermodynamic functions of thallium chalcogen-halides and their binary constituents as well as degree of ionization (DI of chemical bonding were revealed.

  7. Usefulness of Thallium Scan for Differential Diagnosis of Breast Mass

    Energy Technology Data Exchange (ETDEWEB)

    Bae, Sang Kyun; Yum, Ha Yong; Lee, Chung Han; Choi, Kyung Hyun [Kosin University College of Medicine, Pusan (Korea, Republic of)


    The purpose of this study is to evaluate thallium scanning as a potential test in differentiating malignant from benign lesions of breast. Thirty-one female patients underwent thallium scan of the breast. After intravenous injection of 74-111 MBq(2-3 mCi)of thallium-201, anterior and lateral images were obtained. We compared thallium scans with pathological results. Of 11 patients with breast cancers, 10 cases (90.9%) were detected using thallium scan. Thallium scan obtained in one patient who had breast cancer but received several cycles of chemotherapy did not show thallium uptake. The smallest detectable cancer was 1.5 cm in diameter. In contrast, there is no thallium accumulation in breasts of 17 of 20 patients with benign disease (85%), Three cases of 13 fibrocystic disease show thallium uptake in their breast. In conclusion, thallium scan is an effective test in differentiating benign from malignant lesion.

  8. Thallium contamination of water in Canada

    Energy Technology Data Exchange (ETDEWEB)

    Cheam, V. [National Water Research Institute Branch, Burlington, ON (Canada). Aquatic Ecosystems Protection Research Branch


    A highly sensitive instrument, a Laser-Excited Atomic Fluorescence Spectrometer, has been developed to study thallium contamination in some important Canadian ecosystems from the Arctic (containing very low thallium concentration) to coal-related industries across Canada and even to the study of thallium toxicity in an invertebrate, Hyalella azteca. Overall, the data indicate that the coal power plants and mines contain higher thallium concentrations than the other ecosystems studied, and the eastern region has the highest Tl concentrations compared to other regions. The range of thallium concentration in ng/L for the Arctic snow and ice was between not detected and 8.4, for the Great Lakes waters 0.9 to 48, for pore waters 0.1 to 213, for western coal power plants and mines 0.1 to 1326, for central coal power plants 1.2 to 175, for eastern coal power plants and mines 0.2 to 23605, and for miscellaneous sites across Canada not detected to 4390 ng/L. Some of these high concentrations and those high ones reported in industrial wastewaters exceeded the chronic toxicity endpoints for Hyalella azteca mortality, growth and reproduction, and thus can cause serious distress to the environment. All data were integrated into a map of thallium distribution, the first one in Canada. Natural background level of thallium for the Arctic was estimated to be 0.02 to 0.03 pg/g.

  9. Repeat thallium-201 SPECT in cerebral lymphoma. (United States)

    Borggreve, F; Dierckx, R A; Crols, R; Mathijs, R; Appel, B; Vandevivere, J; Mariën, P; Martin, J J; De Deyn, P P


    The authors report on the contribution of Thallium-201 brain SPECT in the diagnosis and follow-up of a non-immunosuppressed patient, presenting with primary cerebral lymphoma. The tumoral process was at first not diagnosed on CT-scan, but Thallium-201 SPECT suggested a tumoral invasion. During corticosteroid treatment the tumor volume on CT-scan decreased, while on Thallium-201 SPECT there was an enhancement of the accumulation and an increasing tumor to non-tumor ratio. These scintigraphical findings more closely reflected the clinical course and the postmortem results.

  10. Thallium poisoning from maliciously contaminated food. (United States)

    Meggs, W J; Hoffman, R S; Shih, R D; Weisman, R S; Goldfrank, L R


    Four young adults presented two days after one of them had received marzipan balls packaged in a box from an expensive candy manufacturer. Two ate one candy ball, while two others shared a third. The next day, variable gastrointestinal symptoms developed. On the third day, two patients developed painful paresthesiae of the hands and feet, an early but nonspecific clinical marker of thallium poisoning. A tentative diagnosis of thallium poisoning was made based on symptoms, and treatment was initiated. The remaining candies were radiographed. Metallic densities in the candies supported the diagnosis, and atomic absorption spectroscopy was used to quantitate thallium content. Each candy contained a potentially fatal dose. Five to seven days later, hypertension and tachycardia developed in the two patients who had ingested an entire candy. All patients developed alopecia but recovered without overt neurologic or other sequelae. While the diagnosis of thallium poisoning is often delayed until alopecia develops, an early diagnosis favors an effective treatment strategy.

  11. Thallium in mineral resources extracted in Poland

    Directory of Open Access Journals (Sweden)

    Bojakowska I.


    Full Text Available Thallium concentrations in primary mineral commodities extracted in Poland and processed in high temperatures were determined by ICP-MS method. Samples of hard and brown coal, copper-silver and zinclead ores, argillaceous and calcareous rocks of different genesis and age were analyzed. The highest thallium concentrations occur in the zinc-lead ores, the average content being of 52.1 mg/kg. The copper ores contain in average 1.4 mg/kg of thallium. Hard coals from the Upper Silesian Coal Basin display higher thallium content than those exploited in the Lublin Coal Basin. Brown coals from Turow deposit distinguish by much higher values, 0.7 mg/kg Tl, than those from huge Bełchatów and smaller Konin-Turek region deposits. Average thallium concentrations in clays used for ceramic materials are lower than 1 mg/kg, except of Mio-Pliocene Slowiany deposit. The average content of thallium in the studied limestone and dolomite raw materials for cement, lime, and metallurgical flux, and refractories is very low in comparison to the average amounts in the world carbonate rocks.

  12. Complexometric determination of thallium(III using ethanethiol as a selective masking agent

    Directory of Open Access Journals (Sweden)

    Karthikeyan J.


    Full Text Available A simple and selective complexometric method for the determination of thallium in presence of other metal ions is proposed based on the selective masking ability of ethanethiol towards thallium(III. Thallium present in a given sample solution is first complexed with a known excess of EDTA and the surplus EDTA is titrated with standard zinc sulphate solution at pH 5-6(hexamine using xylenol orange as the indicator. A 0.3% aqueous solution of ethanethiol is then added to displace EDTA from the Tl(III-EDTA complex. The released EDTA is titrated with standard zinc sulphate solution as before. Reproducible and accurate results are obtained for 3.70 mg to 74.07 mg of Tl (III with relative error less than ? 0.44% and coefficient of variation not more than 0.27%. The interference of various ions was studied and the method was used for the analysis of thallium in its synthetic alloy mixtures and also in complexes.

  13. Examining of Thallium in Cigarette Smokers. (United States)

    Ghaderi, Amir; NasehGhafoori, Payam; Rasouli-Azad, Morad; Sehat, Mojtaba; Mehrzad, Fateme; Nekuei, Mina; Aaseth, Jan; Banafshe, Hamid Reza; Mehrpour, Omid


    Smoking is one of the sources of thallium which is considered as a toxic heavy metal. The aim of this study was to determine urinary thallium levels and related variables in smokers, compared to a control group. The study was conducted on 56 participants who had smoked continuously during the year before they were referred to Kashan Smoking Cessation Clinic. Fifty-three nonsmokers who were family members or friends of the smokers were selected as the control group. Urinary thallium was measured in both groups (n = 109) using atomic absorption spectrophotometry. The mean value (with SD) for urinary thallium in the smokers (10.16 ± 1.82 μg/L) was significantly higher than in the control group (2.39 ± 0.63 μg/L). There was a significant relationship between smoking duration and urinary thallium levels (P = 0.003). In a subgroup of smokers who was addicted to opium and opium residues (n = 9), the mean level of thallium (37.5 ± 13.09 μg/L) was significantly higher than in the other smokers (4.93 ± 4.45; P = 0.001). Multiple regression analysis showed opioid abuse, insomnia, and chronic obstructive pulmonary disease (COPD), together were strong predictors of urinary thallium levels in smokers. There was no significant difference in thallium level in hookah smokers (P = 0.299) or in those with COPD compared to other smokers (P = 0.375). Urinary thallium levels of smokers with clinical signs of depression, sleep disorders, memory loss, and sweating were higher than those of smokers without these signs. Since thallium, as other toxic metals is accumulated in the body, and cigarette smoking also involves carcinogenic exposures and health hazards for passively exposed people, the need for cigarette control policies is emphasized.

  14. Thallium-201 scintigraphy in unstable angina pectoris

    Energy Technology Data Exchange (ETDEWEB)

    Wackers, F.J.T.; Lie, K.I.; Liem, K.L.; Sokole, E.B.; Samson, G.; Van Der Schoot, J.B.; Durrer, D.


    Thallium-201 scintigraphy was performed during the pain free period in 98 patients with unstable angina. Scintiscans were positive in 39 patients, questionable in 27 patients and normal in 32 patients. Eighty-one patients responded favorably to treatment (group I). Seventeen patients had complicated courses (group II) and despite maximal treatment with propranolol either developed infarction (six patients) or continued to have angina necessitating coronary surgery (11 patients). In group I during the pain free period 26 of 81 patients had positive thallium-201 scans, whereas 20 patients had an abnormal ECG at that time; during angina 18 patients had transient ECG changes. In group II during the pain free period 13 of 17 patients had positive scans, whereas two patients had abnormal ECG at that time; during angina 12 patients showed transient ECG changes. The sensitivity to recognize group II was 76% for thallium-201 scintigraphy, 11% for ECG during the pain free period; 70% for ECG during angina; 94% for the combination of either positive scans or abnormal ECG. Thus, positive thallium-201 scans occur in patients with unstable angina, positive scans can be obtained during the pain free period, thallium-201 scans are more frequently positive in patients with complicated course.

  15. Thallium-201 uptake in a benign thymoma

    Energy Technology Data Exchange (ETDEWEB)

    Campeau, R.J.; Ey, E.H.; Varma, D.G.


    A 68-year-old woman was admitted with atypical angina. A chest radiograph showed an anterior mediastinal mass that was confirmed on CT. The mass was relatively avascular and separate from the heart and great vessels. She underwent stress thallium testing that demonstrated no exercise-induced ischemia; however, an abnormal focus of thallium activity was present in the anterior mediastinum on stress and redistribution images. Cardiac catheterization demonstrated a normal left ventriculogram, coronary arteries and thoracic aorta. Subsequent surgery and pathologic examination revealed the mass to be a benign thymoma arising in the right lobe of the thymus gland.

  16. Endogenous thiols enhance thallium toxicity

    Energy Technology Data Exchange (ETDEWEB)

    Montes, Sergio; Rios, Camilo [Instituto Nacional de Neurologia y Neurocirugia, ' ' Manuel Velasco Suarez' ' , Departamento de Neuroquimica, Mexico, D.F (Mexico); Soriano, Luz; Monroy-Noyola, Antonio [Universidad Autonoma del Estado de Morelos, Laboratorio de Neuroproteccion, Facultad de Farmacia, Cuernavaca, Morelos (Mexico)


    Either L-methionine (L-met) or L-cysteine (L-cys), given alone and in combination with Prussian blue (PB) was characterized as treatment against acute thallium (Tl) toxicity in rats. Animals were intoxicated with 32 mg/kg Tl acetate corresponding to rat LD{sub 50}. Antidotal treatments were administered during 4 days, as follows: (1) vehicle, (2) L-met 100 mg/kg i.p. twice a day, (3) L-cys 100 mg/kg i.p. twice a day, (4) PB 50 mg/kg oral, twice a day, (5) L-met + PB and (6) L-cys + PB. Mortality was as follows: control 50%; L-met 80%; L-cys 80%; PB 20%; L-met + PB 90% and L-cys + PB 100%. In a different experiment, using 16 mg/kg of Tl, tissue levels of this metal were analyzed. PB treatment statistically diminished Tl content in body organs and brain regions (P < 0.01). Whereas, separate treatments of L-met and L-cys failed to decrease Tl content in organs and brain regions; while its administration in combination with PB (L-met + PB and L-cys + PB groups) lowered Tl levels in body organs in the same extent as PB group. Results indicate that L-met and L-cys administered alone or in combination with PB should not be considered suitable treatments against acute Tl toxic effects because this strategy failed to prevent mortality and Tl accumulation in brain. (orig.)

  17. Thallium in fractions of soil formed on floodplain terraces. (United States)

    Jakubowska, Monika; Pasieczna, Anna; Zembrzuski, Wlodzimierz; Swit, Zbigniew; Lukaszewski, Zenon


    Two soils formed on the floodplain terrace of a rivulet flowing through the zinc-lead ore exploration area polluted with thallium and one soil from a floodplain terrace of the reference area were investigated in terms of thallium distribution between soil fractions. Such type of soil is formed on river floodplain terraces next to the main river channel and its composition records the history of river pollution. A sequential extraction of soil according to the BCR protocol was performed with an additional initial stage of extraction with water. Apart from labile thallium, thallium entrapped in the residual parent matter was also determined. Thallium was determined by flow-injection differential-pulse anodic stripping voltammetry. In all three cases, the major fraction is thallium entrapped in parent matter. Top soil from the polluted area contains 49.3% thallium entrapped in the residual parent matter, the bottom soil contains 41% while the reference soil contains 80% in this fraction. The major part of labile thallium is located in the reducible fraction (27.7% of total thallium in the top soil, 27% in the bottom soil and 12.4% of the reference soil). Second in terms of significance is the fraction of oxidizable thallium. The top soil contains 12% of total thallium concentration, the bottom soil contains 19% of total concentration, while the reference soil contains 4.1% of total concentration. The acid soluble/exchangeable fraction of thallium has almost the same significance as the oxidizable fraction. The top soil contains 10.4% of the total concentration, while the bottom soil contains 12% of the total concentration. Water soluble thallium concentration is very small. Comparison of the top and the bottom soil show that thallium has not been transported from the river channel onto the floodplain terrace over a long period.

  18. Characteristics of photoconductivity in thallium monosulfide single ...

    Indian Academy of Sciences (India)

    journal of. March 2007 physics pp. 467–479. Characteristics of photoconductivity in thallium monosulfide single crystals. I M ASHRAF, H A ELSHAIKH and A M BADR. Physics Department ... pendencies of carrier lifetime on light intensity, applied voltage and temperature are also ..... 14, 797 (1935) (in Japanese). [10] A T ...

  19. Thallium bromide iodide crystal acoustic anisotropy examination. (United States)

    Mantsevich, S N


    Thallium bromide iodide crystal also known as KRS-5 is the well known material used in far infrared radiation applications for optical windows and lenses fabrication. The main advantage of this material is the transparency in wide band of wavelengths from 0.53 to 50μm. Despite such advantages as transparency and large acousto-optic figure of merit values, KRS-5 is rarely used in acousto-optics. Nevertheless this material seems to be promising for far infrared acousto-optic applications. The acoustic and acousto-optic properties of KRS-5 needed for the full use in optoelectronics are not well understood to date. In this paper the detailed examination of thallium bromide iodide crystal acoustic properties is presented. Copyright © 2016 Elsevier B.V. All rights reserved.

  20. Thallium and its contents in Remata carbonate rocks

    Directory of Open Access Journals (Sweden)

    Kondelová Marcela


    Full Text Available The article presents at first the list of thallium own minerals and its isomorphic content in other minerals, especially in Slovakian ore deposits. This trace element was found in numerous dolomite-rock samples from Remata massif near Handlová. An interesting level of Tl content was analyzed in nonsilicified rocks; the highest content of Tl (and Ag are along the E – W line of disturbance. The presence of thallium in some limonitic aggregates in close Kremnica-gold deposit indicate any continuous relation. Some similarities to type gold deposits Carlin ( USA are discussed, even if no gold and discrete thallium phases were in Remata determined yet.

  1. Tracing thallium contamination in soils using isotopes (United States)

    Vaněk, Aleš; Grösslová, Zuzana; Mihaljevič, Martin; Ettler, Vojtěch; Trubač, Jakub; Teper, Leslaw; Cabala, Jerzy; Rohovec, Jan; Penížek, Vít; Zádorová, Tereza; Pavlů, Lenka; Holubík, Ondřej; Drábek, Ondřej; Němeček, Karel; Houška, Jakub; Ash, Christopher


    We report the thallium (Tl) isotope record in moderately contaminated soils, which have been historically affected by emissions from coal-fired power plants. Our findings clearly demonstrate that Tl of anthropogenic (high-temperature) origin with light isotope composition was deposited onto the studied soils, where heavier Tl (ɛ205Tl -1) naturally occurs. The results show a positive linear relationship (R2 = 0.71) between 1/Tl and the isotope record, as determined for all the soils and bedrocks, also indicative of binary Tl mixing between two dominant reservoirs. We also identified significant Tl isotope variations within the products from coal combustion and thermo-desorption experiments with local Tl-rich coal pyrite. Bottom ash exhibited the heaviest Tl isotope composition (ɛ205Tl 0), followed by fly ash (ɛ205Tl between -2.5 and -2.8) and volatile Tl fractions (ɛ205Tl between -6.2 and -10.3), suggesting partial Tl isotope fractionations. Despite the evident role of soil processes in the isotope redistribution, we demonstrate that Tl contamination can be traced in soils, and propose that the isotope data represent a possible tool to aid our understanding of post-depositional Tl dynamics in surface environments for the future. This research was supported by the Czech Science Foundation (grant no. 14-01866S and 17-03211S).

  2. Catalytic properties of Thallium-containing mesoporous silicas

    Directory of Open Access Journals (Sweden)

    A. Baradji


    Full Text Available The benzylation of benzene by benzyl chloride over a series of Thallium-containing mesoporous silicas with different Tl contents has been investigated. These materials (Tl-HMS-n have been characterized by chemical analysis, N2 adsorption/desorption isotherm and X-ray diffraction (XRD. The mesoporous Thallium-containing materials showed both high activity and high selectivity for the benzylation of benzene. More interesting is the observation that these catalysts are always active and selective for large molecules like naphthenic compounds such as methoxynaphthalene.

  3. A comparison of the clinical relevance of thallium201 and ...

    African Journals Online (AJOL)

    Thallium-201 is at present the radiotracer of choice for the clinical evaluation of myocardial blood flow. Although different technetium-99m-isonitrile agents have been synthesised recently, only 99mTc-melhoxyisobutyl-isonitrile (99mTc_MIBI) has proved to hold promise for clinical implementation. The myocardial distribution ...

  4. Een bepalingsmethode voor thallium in regenwater met behulp van voltammetrie

    NARCIS (Netherlands)

    Struijs; J.; Wolfs; P.M.; Esseveld; F.G.van


    In dit rapport wordt een bepalingmethode beschreven voor thallium in het nanogram/liter-gebied, waarbij gebruik wordt gemaakt van differentiele pulse-anodic stripping voltammetry (DPASV) aan de dunne kwikfilm. Met deze techniek blijkt het mogelijk om de concentratie van dit element rechtstreeks

  5. Band-Structure of Thallium by the LMTO Method

    DEFF Research Database (Denmark)

    Holtham, P. M.; Jan, J. P.; Skriver, Hans Lomholt


    The relativistic band structure of thallium has been calculated using the linear muffin-tin orbital (LMTO) method. The positions and extents of the bands were found to follow the Wigner-Seitz rule approximately, and the origin of the dispersion of the bands was established from the canonical s...

  6. A Simple and Rapid Complexometric Determination of Thallium(III ...

    African Journals Online (AJOL)

    A simple, rapid and selective complexometric method is proposed for the determination of thallium(III), using mercaptoethane(EtSH) as demasking agent. The sample solution containing Tl(III) is first complexed with excess EDTA and the surplus EDTA is removed by titration at pH 5–6 with zinc sulphate solution using ...

  7. Selective Thallium (I Ion Sensor Based on Functionalised ZnO Nanorods

    Directory of Open Access Journals (Sweden)

    Z. H. Ibupoto


    Full Text Available Well controlled in length and highly aligned ZnO nanorods were grown on the gold-coated glass substrate by hydrothermal growth method. ZnO nanorods were functionalised with selective thallium (I ion ionophore dibenzyldiaza-18-crown-6 (DBzDA18C6. The thallium ion sensor showed wide linear potentiometric response to thallium (I ion concentrations ( M to  M with high sensitivity of 36.87 ± 1.49 mV/decade. Moreover, thallium (I ion demonstrated fast response time of less than 5 s, high selectivity, reproducibility, storage stability, and negligible response to common interferents. The proposed thallium (I ion-sensor electrode was also used as an indicator electrode in the potentiometric titration, and it has shown good stoichiometric response for the determination of thallium (I ion.

  8. A Simple and Rapid Complexometric Determination of Thallium(III ...

    African Journals Online (AJOL)



    Oct 8, 2005 ... surplus EDTA is removed by titration at pH 5–6 with zinc sulphate solution using xylenol orange as indicator. ... Reproducible and accurate results are obtained in the concentration range 4–80 mg of thallium with a relative error ≤ ±0.6% .... soluble and stable 1:1 complex with Tl(I) so formed.22 This was.

  9. Thallium in the hydrosphere of south west England

    Energy Technology Data Exchange (ETDEWEB)

    Law, Sin [School of Geography, Earth and Environmental Sciences, University of Plymouth, Drake Circus, Plymouth PL4 8AA (United Kingdom); Turner, Andrew, E-mail: [School of Geography, Earth and Environmental Sciences, University of Plymouth, Drake Circus, Plymouth PL4 8AA (United Kingdom)


    Thallium is a highly toxic metal whose environmental concentrations, distributions and behaviour are not well understood. In the present study we measure the concentrations of Tl in filtered and unfiltered samples of rain, tap, river, estuarine and waste waters collected from south west England. Dissolved Tl was lowest (<20 ng L{sup -1}) in tap water, rain water, treated sewage and landfill effluents, estuarine waters, and rivers draining catchments of sandstones and shales. Concentrations up to about 450 ng L{sup -1} were observed in rivers whose catchments are partly mineralized and where metal mining was historically important, and the highest concentration ({approx}1400 ng L{sup -1}) was measured in water abstracted directly from an abandoned mine. Compared with other trace metals measured (e.g. As, Cd, Co, Cr, Cu, Ni, Pb, Zn), Tl has a low affinity for suspended particles and undergoes little removal by conventional (hydroxide precipitation) treatment of mine water. - Highlights: > Thallium concentrations have been measured in natural and waste waters from south west England. > Dissolved concentrations spanned three orders of magnitude and were highest in water from an abandoned mine. > Inputs associated with historical metal mine workings are the most important to the regional hydrosphere. - Concentrations of dissolved thallium in waters of south west England span two orders of magnitude and are greatest in water from an abandoned mine.

  10. [Efficiency of hemoperfusion on clearing thallium based on atomic absorption spectrometry]. (United States)

    Tian, Tian; Wang, Yongan; Nie, Zhiyong; Wang, Jiao; Peng, Xiaobo; Yuan, Ye; Li, Wanhua; Qiu, Zewu; Xue, Yanping; Xiong, Yiru


    To determine thallium in whole blood by atomic absorption detection method, and to investigate the eliminating effect of hemoperfusion (HP) for thallium in blood. The blood of Beagle dogs which had not exposed to thallium before were obtained for preparation of thallium nitrate ( TlNO3 )-containing solution in three concentrations according to the conversion formula based on animal weight and volume of blood. HP was performed in the simulated in vivo environment. The content of TlNO3 in blood of the next group was determined on the amount of TlNO3 for the last HP of the former dose group. Thallium quantity in different samples was measured with atomic absorption spectrometer blood samples before and after HP. Finally, the thallium concentration in blood was analyzed statistically. Thallium concentrations showed a good linear relationship in the range of 0-200 μg/L (r = 0.998 4). The intra-day precision (RSD) was lower than 4.913%, the intra-day recovery rate was 96.2%-111.9%; the inter-day precision (RSD) was lower than 7.502%, the inter-day recovery rate was 89.6%-105.2%. The concentration of thallium in blood was significantly reduced after HP per time in high, middle, and low dose groups [(453.43 ± 27.80) mg/L to (56.09 ± 14.44) mg/L in high dose group, F = 8.820, P = 0.003; (64.51 ± 13.60) mg/L to (3.19 ± 0.23) mg/L in middle dose group, F = 36.312, P = 0.000; (5.40 ± 0.98) mg/L to (0.38 ± 0.25) mg/L in low dose group, F = 46.240, P = 0.000 ]. The adsorption rate of four times of HP in high, middle and low dose group were (87.63 ± 2.48 )%, (95.06 ± 1.54 )% and (92.76 ± 4.87)%, respectively, without significant difference (F = 4.231, P = 0.070). The method for measuring thallium was established, and it shows a very stable, simple, sensitive for determination of thallium. HP can effectively remove thallium from blood. Thallium concentration can be reduced by 90% after four times of HP. HP is also effective even when thallium concentration is not high.

  11. Left ventricular dilatation and pulmonary thallium uptake after single-photon emission computer tomography using thallium-201 during adenosine-induced coronary hyperemia

    Energy Technology Data Exchange (ETDEWEB)

    Iskandrian, A.S.; Heo, J.; Nguyen, T.; Lyons, E.; Paugh, E. (Philadelphia Heart Institute, PA (USA))


    This study examined the implications of left ventricular (LV) dilatation and increased pulmonary thallium uptake during adenosine-induced coronary hyperemia. The lung-to-heart thallium ratio in the initial images was significantly higher in patients with coronary artery disease (CAD) than normal subjects; 0.48 +/- 0.16 in 3-vessel disease (n = 16), 0.43 +/- 0.10 in 2-vessel disease (n = 20), 0.43 +/- 0.08 in 1-vessel disease (n = 16) and 0.36 +/- 0.05 in normal subjects (n = 7) (p less than 0.001, 0.09 and 0.06, respectively). There was a significant correlation between the severity and the extent of the perfusion abnormality (determined from the polar maps) and the lung-to-heart thallium ratio (r = 0.51 and 0.52, respectively, p less than 0.0002). There was also a significant correlation between lung thallium washout and lung-to-heart thallium ratio (r = 0.42, p = 0.0009) and peak heart rate (r = -0.49, p less than 0.0001). The LV dilatation was mostly due to an increase in cavity dimension (30% increase) and to a lesser extent (6% increase) due to increase in LV size. (The cavity dimensions were measured from the short-axis slices at the midventricular level in the initial and delayed images). The dilation was seen in patients with CAD but not in the normal subjects. These changes correlated with the extent and severity of the thallium perfusion abnormality. Thus, adenosine-induced coronary hyperemia may cause LV dilation and increased lung thallium uptake on the basis of subendocardial ischemia.

  12. Early detection of restenosis after successful percutaneous transluminal coronary angioplasty by exercise-redistribution Thallium scintigraphy

    NARCIS (Netherlands)

    W. Wijns (William); P.W.J.C. Serruys (Patrick); J.H.C. Reiber (Johan); P.J. de Feyter (Pim); M.J.B.M. van den Brand (Marcel); M.L. Simoons (Maarten); P.G. Hugenholtz (Paul)


    textabstractThe value of exercise testing and thallium scintigraphy in predicting recurrence of angina pectoris and restenosis after a primary successful transluminal coronary angioplasty (PTCA) was prospectively evaluated. In 89 patients, a symptom-limited exercise electrocardiogram (ECG) and

  13. Oral zinc sulphate in treatment of patients with thallium poisoning: A clinical therapeutic trial

    Directory of Open Access Journals (Sweden)

    Ahmed A. Al-Mohammadi


    Full Text Available Thallium poisoning is usually associated with typical dermatological features simulating that of zinc deficiency. The aim of this study was to evaluate the role of oral zinc sulphate in the treatment of patients with thallium poisoning.Materials and methods: This clinical therapeutic trial study was conducted in Departments of Dermatology of Baghdad and Basrah Teaching Hospitals from February 2008 - February 2010, where a total of 37 patients with thallium poisoning were enrolled.A detailed history was taken from all patients and complete clinical examination was performed. All patients received zinc sulphate in a dose of 5 mg/kg three times a day few days before confirming the diagnosis of thallium poisoning. Thallium in urine had been measured using the colorimetric method and was positive in all patients. After confirming the diagnosis of thallium poisoning, thallium antidotes Prussian blue was given to 32 patients.Results: Age range of 37 patients was 5-33 (24±5.3 years. The dermatological findings were mainly: anagen hair loss affected the scalp and limbs. Also, dusky ecchymotic red dermatitis like rash was observed on the face and dorsum of hands and legs, while neurological manifestations were mainly of peripheral neuropathy, were reported in 21 (55% patients. All patients but two responded promptly to a trial of zinc sulphate within few days.Conclusion: Oral Zinc sulphate appears to be an effective and safe treatment for thallium poisoning particularly for skin and hair features and in reducing its lethal progression and complications. J Clin Exp Invest 2011;2(2:133-7

  14. Fate of Thallium(I) in Reverse Osmosis and Chlorinated Water Matrices (United States)


    THALLIUM(I) IN REVERSE OSMOSIS AND CHLORINATED WATER MATRICES ECBC-TR-1127 Approved for public release; distribution is unlimited...3. DATES COVERED (From - To) Apr 2010 - Dec 2011 4. TITLE AND SUBTITLE Fate of Thallium(I) in Reverse Osmosis and Chlorinated Water Matrices... osmosis (RO) and RO water with added chlorine (RO-Cl) was measured using inductively coupled plasma optical emission spectroscopy (ICP-OES) for a period of

  15. Thallium in the hydrosphere of south west England. (United States)

    Law, Sin; Turner, Andrew


    Thallium is a highly toxic metal whose environmental concentrations, distributions and behaviour are not well understood. In the present study we measure the concentrations of Tl in filtered and unfiltered samples of rain, tap, river, estuarine and waste waters collected from south west England. Dissolved Tl was lowest (<20 ng L(-1)) in tap water, rain water, treated sewage and landfill effluents, estuarine waters, and rivers draining catchments of sandstones and shales. Concentrations up to about 450 ng L(-1) were observed in rivers whose catchments are partly mineralized and where metal mining was historically important, and the highest concentration (~1400 ng L(-1)) was measured in water abstracted directly from an abandoned mine. Compared with other trace metals measured (e.g. As, Cd, Co, Cr, Cu, Ni, Pb, Zn), Tl has a low affinity for suspended particles and undergoes little removal by conventional (hydroxide precipitation) treatment of mine water. Copyright © 2011 Elsevier Ltd. All rights reserved.

  16. Qualitative evaluation of coronary flow during anesthetic induction using thallium-201 perfusion scans

    Energy Technology Data Exchange (ETDEWEB)

    Kleinman, B.; Henkin, R.E.; Glisson, S.N.; el-Etr, A.A.; Bakhos, M.; Sullivan, H.J.; Montoya, A.; Pifarre, R.


    Qualitative distribution of coronary flow using thallium-201 perfusion scans immediately postintubation was studied in 22 patients scheduled for elective coronary artery bypass surgery. Ten patients received a thiopental (4 mg/kg) and halothane induction. Twelve patients received a fentanyl (100 micrograms/kg) induction. Baseline thallium-201 perfusion scans were performed 24 h prior to surgery. These scans were compared with the scans performed postintubation. A thallium-positive scan was accepted as evidence of relative hypoperfusion. Baseline hemodynamic and ECG data were obtained prior to induction of anesthesia. These data were compared with the data obtained postintubation. Ten patients developed postintubation thallium-perfusion scan defects (thallium-positive scan), even though there was no statistical difference between their baseline hemodynamics and hemodynamics at the time of intubation. There was no difference in the incidence of thallium-positive scans between those patients anesthetized by fentanyl and those patients anesthetized with thiopental-halothane. The authors conclude that relative hypoperfusion, and possibly ischemia, occurred in 45% of patients studied, despite stable hemodynamics, and that the incidence of these events was the same with two different anesthetic techniques.

  17. Comparison of thallium deposition with segmental perfusion in pigs with chronic hibernating myocardium. (United States)

    Baldwa, Sunil; Rana, Muzamil; Canty, John M; Fallavollita, James A


    Viable, chronically dysfunctional myocardium with reduced resting flow (or hibernating myocardium) is an important prognostic factor in ischemic heart disease. Although thallium-201 imaging is frequently used to assess myocardial viability in patients with ischemic cardiomyopathy, there are limited data regarding its deposition in hibernating myocardium, and this data suggest that thallium retention may be supernormal compared with control myocardium. Accordingly, pigs (n=7) were chronically instrumented with a 1.5 mm Delrin stenosis on the proximal left anterior descending coronary artery (LAD) to produce hibernating myocardium. Four months later, severe anteroapical hypokinesis was documented with contrast ventriculography (wall motion score, 0.7+/-0.8; normal=3), and microsphere measurements confirmed reduced resting flow (LAD subendocardium, 0.78+/-0.34 vs. 0.96+/-0.24 ml.min(-1).g(-1) in remote; P<0.001). Absolute deposition of thallium-201 and insulin-stimulated [18F]-2 fluoro-2-deoxyglucose (FDG) were assessed over 1 h and compared with resting flow (n=704 samples). Thallium-201 deposition was only weakly correlated with perfusion (r2=0.20; P<0.001) and was more homogeneously distributed (relative dispersion, 0.12+/-0.03 vs. 0.29+/-0.10 for microsphere flow; P<0.01). Thus after 1 h relative thallium-201 (subendocardium LAD/remote, 0.96+/-0.16) overestimated relative perfusion (0.78+/-0.32; P<0.0001) and underestimated the relative reduction in flow. Viability was confirmed by both histology and preserved FDG uptake. We conclude that under resting conditions, thallium-201 redistribution in hibernating myocardium is nearly complete within 1 h, with similar deposition to remote myocardium despite regional differences in flow. These data suggest that in this time frame thallium-201 deposition may not discriminate hibernating myocardium from dysfunction myocardium with normal resting flow. Since hibernating myocardium has been associated with a worse prognosis

  18. Thallium uptake and biological behaviour in childhood brain tumours

    Energy Technology Data Exchange (ETDEWEB)

    Bernard, E.J.; Howman-Giles, R.; Kellie, S.; Uren, R.F. [Royal Alexandra Hospital for Children, Sydney, NSW (Australia)


    Full text: The histopathological grade and radiological appearance of the diverse cerebral neoplasms in childhood frequently poorly reflect their biological behaviour. We examined thallium accumulation prior to treatment (and in several cases, at intervals there after) in 13 children to determine its usefulness as a tumour marker. 23 SPECT studies were acquired 20 minutes after the injection of 1-3 mCi of {sup 201}TI. Thallium index (TI), the ratio of counts in tumour/normal brain, was calculated. No uptake was seen in two patients (pts) with a Grade 1 cerebellar astrocytomas (disease free at 4/12 f/u). Three pts with medulloblastomas were studied. One pt showed intense uptake (Tl =12). His tumour (proliferative antigen stain Ki67 = 50%) recurred early after debulking surgery (Tl +ve prior to CT or MRI changes). The second pt was imaged at relapse (Ki67 = 60%) and showed intense uptake, Tl = 17. The third pt showed lower level uptake (Tl = 2), Ki67 = 5%, and is disease-free at 5/12 (as per {sup 201}TI and MRI). One pt with a Grade 1 brainstem glioma showed Tl = 5 and has progressed rapidly despite low grade histology. Four pts with chiasmatic-hypothalamic gliomas have been studied. Although these neoplasms are usually low grade histologically, their growth properties vary greatly. Two pts with Tl<2.5 have been conservatively managed because of slow tumour growth. The other two pts have Tl>3.5 and have required aggressive treatment for rapid disease progression. One pt with a large pilocytic astrocytoma of the optic chiasm showed Tl = 9.5. Active treatment was not undertaken. One pt with a pineal germ cell tumour showed avid {sup 201}TI uptake (Tl not performed) and has had two normal studies, and is clinically well, since BMT. Avid {sup 201}TI uptake also seen in one pt with cerebral neuroblastoma. (Died at 8/12 after Dx.) Thus, {sup 201}TI accumulates in histologically diverse paediatric neoplasms. The Tl appears to reflect biological behaviour in the limited

  19. Evaluation of muscular lesions in connective tissue diseases: thallium 201 muscular scans

    Energy Technology Data Exchange (ETDEWEB)

    Guillet, G.; Guillet, J.; Sanciaume, C.; Maleville, J.; Geniaux, M.; Morin, P.


    We performed thallium 201 muscle scans to assess muscular involvement in 40 patients with different connective tissue diseases (7 with dermatomyositis, 7 with systemic lupus erythematosus, 12 with progressive systemic scleroderma, 2 with calcinosis, Raynaud's phenomenon, esophageal involvement, sclerodactyly, and telangiectasia (CREST) syndrome, 3 with monomelic scleroderma, 6 with morphea, and 3 with Raynaud's disease). Only 12 of these patients complained of fatigability and/or myalgia. Electromyography was performed and serum levels of muscle enzymes were measured in all patients. Comparison of thallium 201 exercise recording with the other tests revealed that scan sensitivity is greater than electromyographic and serum muscle enzymes levels. Thallium 201 scans showed abnormal findings in 32 patients and revealed subclinical lesions in 18 patients, while electromyography findings were abnormal in 25 of these 32 patients. Serum enzyme levels were raised in only 8 patients. Thallium 201 scanning proved to be a useful guide for modifying therapy when laboratory data were conflicting. It was useful to evaluate treatment efficacy. Because our data indicate a 100% positive predictive value, we believe that thallium 201 scanning should be advised for severe systemic connective tissue diseases with discordant test results.

  20. Exercise-induced thallium-201 myocardial perfusion defects in angina pectoris without significant coronary artery stenosis

    Energy Technology Data Exchange (ETDEWEB)

    Nakazato, Masayasu; Maruoka, Yuji; Sunagawa, Osahiko; Kinjo, Kunihiko; Tomori, Masayuki; Fukiyama, Koshiro (Ryukyu Univ., Nishihara, Okinawa (Japan). School of Medicine)


    We performed exercise thallium-201 myocardial scintigraphy in 32 patients with angina pectoris to study the incidence of perfusion defects, who had no significant organic stenosis on coronary angiography. None of them had myocardial infarction or cardiomyopathy. Thallium-201 myocardial scintigraphy and 12-lead ECG recording were performed during supine bicycle ergometer exercise. Perfusion defects in thallium-201 scintigrams in SPECT images were assessed during visual analysis by two observers. In the coronary angiograms obtained during intravenous infusion of nitroglycerin, the luminal diameter of 75% stenosis or less in the AHA classification was regarded as an insignificant organic stenosis. Myocardial perfusion defects in the thallium-201 scintigrams were detected in eight (25%) of the 32 patients. Six of these eight patients had variant angina documented during spontaneous attacks with ST elevations in standard 12-lead ECGs. Perfusion defects were demonstrated at the inferior or infero-posterior regions in six patients, one of whom had concomitant anteroseptal defect. The defects were not always accompanied by chest pain. All but one patient demonstrating inferior or inferoposterior defects showed ST depression in leads II, III and aV{sub F} on their ECGs, corresponding to inferior wall ischemia. The exception was a case with right bundle branch block. Thus, 25% of the patients with angina pectoris, who had no evidence of significant organic stenosis on their coronary angiograms, exhibited exercise-induced perfusion defects in their thallium-201 scintigrams. Coronary spasms might have caused myocardial ischemia in these patients. (author).

  1. Advanced crystal growth techniques for thallium bromide semiconductor radiation detectors (United States)

    Datta, Amlan; Becla, Piotr; Guguschev, Christo; Motakef, Shariar


    Thallium Bromide (TlBr) is a promising room-temperature radiation detector candidate with excellent charge transport properties. Currently, Travelling Molten Zone (TMZ) technique is widely used for growth of semiconductor-grade TlBr crystals. However, there are several challenges associated with this type of crystal growth process including lower yield, high thermal stress, and low crystal uniformity. To overcome these shortcomings of the current technique, several different crystal growth techniques have been implemented in this study. These include: Vertical Bridgman (VB), Physical Vapor Transport (PVT), Edge-defined Film-fed Growth (EFG), and Czochralski Growth (Cz). Techniques based on melt pulling (EFG and Cz) were demonstrated for the first time for semiconductor grade TlBr material. The viability of each process along with the associated challenges for TlBr growth has been discussed. The purity of the TlBr crystals along with its crystalline and electronic properties were analyzed and correlated with the growth techniques. Uncorrected 662 keV energy resolutions around 2% were obtained from 5 mm x 5 mm x 10 mm TlBr devices with virtual Frisch-grid configuration.

  2. Thallium distribution in sediments from the Pearl river basin, China

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Juan [Guangzhou University, Key Laboratory of Waters Safety and Protection in the Pearl River Delta, Ministry of Education, Guangzhou (China); Forschungszentrum Dresden-Rossendorf (FZD), Institute of Radiochemistry, Research Site Leipzig, Leipzig (Germany); Wang, Jin; Chen, Yongheng [Guangzhou University, Key Laboratory of Waters Safety and Protection in the Pearl River Delta, Ministry of Education, Guangzhou (China); Qi, Jianying [Department of Environmental Science and Engineering, Guangzhou University, Guangzhou (China); Lippold, Holger [Forschungszentrum Dresden-Rossendorf (FZD), Institute of Radiochemistry, Research Site Leipzig, Leipzig (Germany); Wang, Chunlin [Guangdong Provincial Academy of Environmental Science, Guangzhou (China)


    Thallium (Tl) is a rare element of high toxicity. Sediments sampled in three representative locations near industries utilizing Tl-containing raw materials from the Pearl River Basin, China were analyzed for their total Tl contents and the Tl contents in four sequentially extracted fractions (i.e., weak acid exchangeable, reducible, oxidizable, and residual fraction). The results reveal that the total Tl contents (1.25-19.1 {mu}g/g) in the studied sediments were slightly high to quite high compared with those in the Chinese background sediments. This indicates the apparent Tl contamination of the investigated sediments. However, with respect to the chemical fractions, Tl is mainly associated with the residual fraction (>60%) of the sediments, especially of those from the mining area of Tl-bearing pyrite minerals, indicating the relatively low mobility, and low bioavailability of Tl in these sediments. This obviously contrasts with the previous findings that Tl is mainly entrapped in the first three labile fractions of the contaminated samples. Possible reasons were given for the dominating association of Tl with the residual fraction (>95%) of the mining area sediments. The significant role of certain K-containing silicates or minerals of these sediments on retaining Tl in the residual fraction, discovered by this study, provides a special field of research opportunity for the Tl-containing wastewater treatment. (Copyright copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  3. [Graphite furnace atomic absorption spectrometry for determination of thallium in blood]. (United States)

    Zhang, Q L; Gao, G


    Colloidal palladium was used as chemical modifier in the determination of blood thallium by graphite furnace atomic absorption spectrometry. Blood samples were precipitated with 5% (V/V)nitric acid, and then determined by GFAAS with colloidal palladium used as a chemical modifier. 0.2% (W/V)sodium chloride was added in the standard series to improve the matrix matching between standard solution and sample. The detection limit was 0.2 μg/L. The correlation coefficient was 0.9991. The recoveries were between 93.9% to 101.5%.The relative standard deviations were between 1.8% to 2.7%.The certified reference material of whole blood thallium was determined and the result was within the reference range Conclusion: The method is accurate, simple and sensitive, and it can meet the needs of detection thallium in blood entirely.

  4. Myocardial perfusion defect on thallium-201 imaging in patients with chronic obstructive pulmonary disease

    Energy Technology Data Exchange (ETDEWEB)

    Mehrotra, P.P.; Weaver, Y.J.; Higginbotham, E.A.


    Six patients with angina pectoris had reversible perfusion defects on stress and redistribution thallium imaging. Three patients had a positive electrocardiographic response to exercise. No significant coronary artery lesions were seen on coronary arteriography in any of the six patients. All had mild to moderate hypoxemia at rest and physiologic evidence of chronic obstructive pulmonary disease as defined by the decrease in the ratio of forced expiratory volume at 1 second to forced vital capacity (FEV1/FVC X 100) or decrease in the forced midexpiratory flow rate (FEF25-75), or both. None had clinical findings suggestive of any of the reported causes of positive thallium scans in patients with normal coronary arteriograms. Cellular dysfunction produced by hypoxemia affecting the uptake of thallium seems to be the most likely mechanism of this abnormality.

  5. Early and delayed thallium-201 scintigraphy in thyroid nodules: the relationship between early thallium-201 uptake and perfusion

    Energy Technology Data Exchange (ETDEWEB)

    Derebek, E. [Dept. of Nuclear Medicine, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Biberoglu, S. [Dept. of Internal Medicine, Div. of Endocrinology, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Kut, O. [Dept. of Nuclear Medicine, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Yesil, S. [Dept. of Internal Medicine, Div. of Endocrinology, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Saydam, S. [Dept. of Surgery, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Yilmaz, M. [Dept. of Nuclear Medicine, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Yenici, O. [Dept. of Nuclear Medicine, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Igci, E. [Dept. of Radiology, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Gokce, O. [Dept. of Surgery, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Canda, S. [Dept. of Pathology, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Bueyuekgebiz, A. [Dept. of Pediatrics, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Dogan, A.S. [Dept. of Nuclear Medicine, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey); Durak, H. [Dept. of Nuclear Medicine, Dokuz Eylul Univ., School of Medicine, Izmir (Turkey)


    Seventy-six patients with tyroid nodules were studied. Initially, 75 MBq of thallium-201 was injected. The thyroid gland was imaged 15 min (early) and 3 h (delayed) after the injection. Thereafter, 185 MBq technetium-99m pertechnetate was injected. Immediately after the injection, a 1-min perfusion image was acquired, followed by an image at 20 min. Increased early and delayed {sup 201}Tl uptake compared with the contralateral thyroid tissue was adopted as the criterion for malignancy. Sensitivity, specificity and negative predictive values were found to be 85%, 64% and 78%, respectively, in operated patients, but these values were 86%, 87% and 95%, respectively, in the whole group, including patients followed with fine-needle aspiration biopsy. With the purpose of investigating the relationship between perfusion and early {sup 201}Tl uptake, bot perfusion and early images were graded comparing nodular activity with contralateral thyroid activity. There was a poor correlation between perfusion and {sup 201}Tl uptake. The correlation was even worse in hyperactive nodules. It is concluded that early and delayed {sup 201}Tl imaging should not be used in the differential diagnosis of cold nodules and that early {sup 201}Tl uptake seems to be more closely related to factors other than perfusion. (orig.)

  6. Overlapping toxic effect of long term thallium exposure on white mustard (Sinapis alba L.) photosynthetic activity. (United States)

    Mazur, Radosław; Sadowska, Monika; Kowalewska, Łucja; Abratowska, Agnieszka; Kalaji, Hazem M; Mostowska, Agnieszka; Garstka, Maciej; Krasnodębska-Ostręga, Beata


    Heavy metal exposure affect plant productivity by interfering, directly and indirectly, with photosynthetic reactions. The toxic effect of heavy metals on photosynthetic reactions has been reported in wide-ranging studies, however there is paucity of data in the literature concerning thallium (Tl) toxicity. Thallium is ubiquitous natural trace element and is considered the most toxic of heavy metals; however, some plant species, such as white mustard (Sinapis alba L.) are able to accumulate thallium at very high concentrations. In this study we identified the main sites of the photosynthetic process inhibited either directly or indirectly by thallium, and elucidated possible detoxification mechanisms in S. alba. We studied the toxicity of thallium in white mustard (S. alba) growing plants and demonstrated that tolerance of plants to thallium (the root test) decreased with the increasing Tl(I) ions concentration in culture media. The root growth of plants exposed to Tl at 100 μg L(-1) for 4 weeks was similar to that in control plants, while in plants grown with Tl at 1,000 μg L(-1) root growth was strongly inhibited. In leaves, toxic effect became gradually visible in response to increasing concentration of Tl (100 - 1,000 μg L(-1)) with discoloration spreading around main vascular bundles of the leaf blade; whereas leaf margins remained green. Subsequent structural analyses using chlorophyll fluorescence, microscopy, and pigment and protein analysis have revealed different effects of varying Tl concentrations on leaf tissue. At lower concentration partial rearrangement of the photosynthetic complexes was observed without significant changes in the chloroplast structure and the pigment and protein levels. At higher concentrations, the decrease of PSI and PSII quantum yields and massive oxidation of pigments was observed in discolored leaf areas, which contained high amount of Tl. Substantial decline of the photosystem core proteins and disorder of the

  7. Stable room-temperature thallium bromide semiconductor radiation detectors (United States)

    Datta, A.; Fiala, J.; Becla, P.; Motakef, Shariar


    Thallium bromide (TlBr) is a highly efficient ionic semiconductor with excellent radiation detection properties. However, at room temperature, TlBr devices polarize under an applied electric field. This phenomenon not only degrades the charge collection efficiency of the detectors but also promotes chemical reaction of the metal electrodes with bromine, resulting in an unstable electric field and premature failure of the device. This drawback has been crippling the TlBr semiconductor radiation detector technology over the past few decades. In this exhaustive study, this polarization phenomenon has been counteracted using innovative bias polarity switching schemes. Here the highly mobile Br- species, with an estimated electro-diffusion velocity of 10-8 cm/s, face opposing electro-migration forces during every polarity switch. This minimizes the device polarization and availability of Br- ions near the metal electrode. Our results indicate that it is possible to achieve longer device lifetimes spanning more than 17 000 h (five years of 8 × 7 operation) for planar and pixelated radiation detectors using this technique. On the other hand, at constant bias, 2500 h is the longest reported lifetime with most devices less than 1000 h. After testing several biasing switching schemes, it is concluded that the critical bias switching frequency at an applied bias of 1000 V/cm is about 17 μHz. Using this groundbreaking result, it will now be possible to deploy this highly efficient room temperature semiconductor material for field applications in homeland security, medical imaging, and physics research.

  8. Thallium pollution in China: A geo-environmental perspective. (United States)

    Xiao, Tangfu; Yang, Fei; Li, Shehong; Zheng, Baoshan; Ning, Zengping


    It is well known that thallium (Tl) is a non-essential and toxic metal to human health, but less is known about the geo-environmentally-induced Tl pollution and its associated health impacts. High concentrations of Tl that are primarily associated with the epithermal metallogenesis of sulfide minerals have the potential of producing Tl pollution in the environment, which has been recognized as an emerging pollutant in China. This paper aims to review the research progress in China on Tl pollution in terms of the source, mobility, transportation pathway, and health exposure of Tl and to address the environmental concerns on Tl pollution in a geo-environmental perspective. Tl associated with the epithermal metallogenesis of sulfide minerals has been documented to disperse readily and accumulate through the geo-environmental processes of soil enrichment, water transportation and food crop growth beyond a mineralized zone. The enrichments of Tl in local soil, water, and crops may result in Tl pollution and consequent adverse health effects, e.g. chronic Tl poisoning. Investigation of the baseline Tl in the geo-environment, proper land use and health-related environmental planning and regulation are critical to prevent the Tl pollution. Examination of the human urinary Tl concentration is a quick approach to identify exposure of Tl pollution to humans. The experiences of Tl pollution in China can provide important lessons for many other regions in the world with similar geo-environmental contexts because of the high mobility and toxicity of Tl. Copyright © 2011 Elsevier B.V. All rights reserved.

  9. Stable room-temperature thallium bromide semiconductor radiation detectors

    Directory of Open Access Journals (Sweden)

    A. Datta


    Full Text Available Thallium bromide (TlBr is a highly efficient ionic semiconductor with excellent radiation detection properties. However, at room temperature, TlBr devices polarize under an applied electric field. This phenomenon not only degrades the charge collection efficiency of the detectors but also promotes chemical reaction of the metal electrodes with bromine, resulting in an unstable electric field and premature failure of the device. This drawback has been crippling the TlBr semiconductor radiation detector technology over the past few decades. In this exhaustive study, this polarization phenomenon has been counteracted using innovative bias polarity switching schemes. Here the highly mobile Br− species, with an estimated electro-diffusion velocity of 10−8 cm/s, face opposing electro-migration forces during every polarity switch. This minimizes the device polarization and availability of Br− ions near the metal electrode. Our results indicate that it is possible to achieve longer device lifetimes spanning more than 17 000 h (five years of 8 × 7 operation for planar and pixelated radiation detectors using this technique. On the other hand, at constant bias, 2500 h is the longest reported lifetime with most devices less than 1000 h. After testing several biasing switching schemes, it is concluded that the critical bias switching frequency at an applied bias of 1000 V/cm is about 17 μHz. Using this groundbreaking result, it will now be possible to deploy this highly efficient room temperature semiconductor material for field applications in homeland security, medical imaging, and physics research.

  10. Medical geology of arsenic, selenium and thallium in China. (United States)

    Li, Shehong; Xiao, Tangfu; Zheng, Baoshan


    Arsenic (As), selenium (Se) and thallium (Tl) are three trace metals (metalloids) of high concern in China because deficiency or excess expose can cause a range of endemic diseases, such as endemic arsenism, selenosis, Keshan disease (KD), Kashin-Beck disease (KBD) and thallotoxicosis. These specific endemic diseases were attributable for overabundance or deficiency (mainly referring to selenium) of these three elements in the local environment as a result of natural geochemical processes and/or anthropologic activities. The geochemistry and human health impacts of these three trace elements have been intensively studied since the 1970s in China, in terms of geochemical sources, distribution, transportation, health impact pathways, and prevention/remediation measures. Endemic arsenism in China are induced from the exposures of high As in either drinking water or domestic combustion of As-rich coals. Both endemic selenium deficiency and selenosis occurred in China. The KD and KBD were related to the deficiency of Se in the low-Se geological belt with Se contents in soil less than 0.125mg/kg stretching from northeast to southwest of China. Endemic selenosis occurred in areas with high Se concentrations in soils derived from the Se-enriched black carbonaceous siliceous rocks, carbonaceous shale and slate. Endemic Tl poisoning occurred in southwestern China due to Tl contamination in local drinking water and vegetables surrounding the Tl-rich sulfide mineralized areas. Some measures have been taken to control and remedy the endemic diseases with significant effects in reducing health risk and damage of As, Se and Tl. However, the states of the endemic diseases of As, Se and Tl in China are still serious in some areas, and substantial research efforts regarding the health impacts of these elements are further required. This paper reviews the progress of medical geology of As, Se and Tl in China, and provides with some outlooks for future research directions. Copyright

  11. New CZT cardiac cameras and myocardial perfusion imaging with thallium 201; Nouvelles cameras cardiaques a semi-conducteur cadmium -zinc- telluride (CZT) et scintigraphies myocardiques au thallium 201

    Energy Technology Data Exchange (ETDEWEB)

    Songy, B. [Service de medecine et imagerie nucleaire, centre cardiologique du Nord (CCN), 93 - Saint-Denis (France)


    Myocardial perfusion imaging is widely used for management of coronary artery disease. However, it suffers from technical limitations. New cardiac cameras using CZT detectors are now available and increase spatial (x2) and energy (x2) resolutions and photons sensitivity (x5). We describe here the General Electric Discovery NM 530c new camera and summarize the validation studies with technetium agents and with thallium 201, protocols to reduce doses, ultrafast protocols and perspectives offered with this new technology. (author)

  12. Genotoxic and mutagenic effects of the diagnostic use of thallium-201 in nuclear medicine

    Energy Technology Data Exchange (ETDEWEB)

    Kelsey, K.T. (Harvard School of Public Health, Boston, MA (United States)); Donohoe, K.J. (Beth Israel Hospital, Boston, MA (United States). Div. of Nuclear Medicine); Baxter, Barbara; Memisoglu, Asli; Little, J.B.; Caggana, Michele; Liber, H.L. (Harvard School of Public Health, Boston, MA (United States))


    In order to investigate possible mutagenetic effects of in vivo exposure to low levels of ionizing radiation used in nuclear medicine, the authors examined hypoxanthine guanine phosphoribosyl transferase (hprt) mutant fraction (MF) and chromosome aberration (CA) frequency in 24 nuclear medicine patients before and after injection of thallium-201. The mean MF of the thallium-201-exposed cohort was 5.2{+-}4.4 x 10{sup -6} before injection exposure. No significant difference in MF was observed 24 h later. In 11 patients who were studied on a 3rd occasion, 30 days after thallium-201 exposure, there was again no significant difference in post-exposure as compared with the pre-exposure MF. The frequency of CA in peripheral blood lymphocytes was not significantly different, comparing pre- and 24h to 1 month post-radionuclide exposure . Thus, thallium-201 exposure was not associated with significant elevations in MF or CA frequency in lymphocytes of exposed individuals. (author). 40 refs.; 3 tabs.

  13. Systematics of c-axis Phonons in the Thallium- and Bismuth-Based Cuprate Superconductors

    NARCIS (Netherlands)

    Tsvetkov, A. A; Dulic, D.; Marel, D. van der; Damascelli, A.; Kaljushnaia, G. A.; Gorina, J. I.; Senturina, N. N.; Kolesnikov, N. N.; Ren, Z. F.; Wang, J. H.; Menovsky, A. A.; Palstra, T. T. M.


    Published in: Phys. Rev. B 60 (1999) 13196 Citing articles (CrossRef) citations recorded in [Science Citation Index] Abstract: We present grazing incidence reflectivity measurements in the far infrared region at temperatures above and below Tc for a series of thallium (Tl2Ba2CuO6, Tl2Ba2CaCu2O8) and

  14. Dipyridamole-thallium-201 tomography documenting improved myocardial perfusion with therapy in Kawasaki disease

    Energy Technology Data Exchange (ETDEWEB)

    Nienaber, C.A.; Spielmann, R.P.; Hausdorf, G.


    Thallium-201 tomographic perfusion studies after pharmacologic vasodilation were performed in seven children (aged 2 years 8 months to 8 years 7 months), 3 to 20 months after the acute stage of the disease. In all patients coronary aneurysms were seen on cross-sectional echocardiograms. The scintigrams of six children showed no significant regional reduction of myocardial thallium-201 uptake. These children had remained asymptomatic in the follow-up period after the acute inflammatory stage of Kawasaki disease. Persistent and transient thallium defects were present in one child with acute posterolateral myocardial infarction; obstruction of two coronary vessels supplying the defect zones was confirmed by contrast angiography. After 8 months of treatment a follow-up nuclear scan showed marked reduction in the size of the defect and almost complete abolishment of the ischemic reaction. Thus tomographic thallium-201 perfusion scintigraphy in conjunction with vasodilation stress is useful to assess myocardial perfusion in children with Kawasaki disease and demonstrates marked improvement in regional perfusion after adequate medical therapy.

  15. Thallium-201: Autoradiography in pigmented mice and melanin-binding in vitro

    Energy Technology Data Exchange (ETDEWEB)

    Tjaelve, H.; Nilsson, M.; Larsson, B. (Uppsala Univ. (Sweden))


    Autoradiography with /sup 201/Tl/sup +/ in C57Bl mice showed a strong labelling of the eye melanin and of pigmented hair follicles. An analysis of the affinity of thallium for pigment from cow eyes indicated a binding to three groups of sites and showed a marked sensitivity to the addition of H/sup +/-ions. The results are consistent with the conception that a binding of thallium occurs to the free carboxyl groups of the melanin and that the structure of the polymer has a marked influence on the affinity. Similar results have previously been obtained with other cations. There was no indication that the strong in vivo affinity of thallium to melanin is due to a more firm binding than for other cations which do not localize on melanin in vivo. Instead, the ability of cations to pass the melanocyte membranes and reach the melanin granules is probably decisive for whether a melanin-binding will take place in vivo. Toxic effects on the eye and epilation are symptoms of thallium intoxication which may be related to its melanin-binding. The fate of /sup 201/Tl/sup +/ in some other tissues is also described and discussed.

  16. Laser-assisted decay and optical spectroscopy studies of neutron-deficient thallium isotopes

    CERN Document Server

    Van Beveren, Céline; Huyse, Mark

    The neutron-deficient thallium isotopes with one proton less than the Z = 82 shell closure, are situated in an interesting region of the nuclear chart, notorious for intruder states and shape coexistence. Shape coexistence is the remarkable phenomenon in which two or more distinct types of deformation occur at low energy in the same atomic nucleus. Shape coexistence has been studied intensively, experimentally as well as theoretically in different nuclei in the light-lead region and the isomerism in the thallium isotopes was among the first indications of this phenomenon. Different shapes, whose structure has been linked to specific proton orbitals above and below the Z = 82 shell closure, are present at low energy in the neutron-deficient odd-mass thallium nuclei. In the odd-odd nuclei, the coupling of an unpaired proton and unpaired neutron gives rise to multiplets of low-lying states from which some can be isomeric. Since thallium has one proton missing in the major proton shell, and when approaching neutr...

  17. Clinical features and applications of thallium-201. With reference to scintigraphy

    Energy Technology Data Exchange (ETDEWEB)

    Fujii, Tadashige


    Thallium-201 is not only used widely in myocardial imaging but also has a great potential in other various nuclear medicine imaging studies. This paper presents clinical features and applications of thallium-201, focusing on clinical trials with thallium-201 at the Shinshu University School of Medicine. Thallium-201 myocardial scintigraphy offers information on (1) ventricular position and morphology, (2) hypertrophy or dilatation of the left ventricle, (3) hypertrophy or dilatation of the right ventricle, (4) site and extent of myocardial ischemia and infarct, (5) myocardial blood flow, (6) pulmonary congestion or interstitial pulmonary edema, and (7) pericardial effusion. It can be used in the following evaluation or diagnosis: (1) acute or old myocardial infarction, (2) angina pectoris, (3) treatment strategy or prognosis of ischemic heart disease, (4) treatment strategy or observation of bypass graft or drug therapy, (5) hypertrophic or dilated idiopathic cardiomyopathy, (6) myocardial lesions induced by sarcoidosis, collagen disease, and neuro-muscular disease, (7) ventricular hypertrophy and pulmonary edema, and (9) pericarditis, pericardial effusion, and systolic pericarditis associated with underlying disease. The significance of tumor, liver, bone marrow scintigraphies is also referred to. (Namekawa, K) 69 refs.

  18. Optimised thallium precipitation in a waste water treatment system of the flue gas desulphurisation; Optimierte Thalliumabscheidung einer RAA

    Energy Technology Data Exchange (ETDEWEB)

    Ritzerfeld, Guenter [RWE Power AG, Bergheim (Germany); Birngruber, Ingolf [RWE Power AG, Hamm (Germany); Muelder, Thomas [RWE Power AG, Ibbenbueren (Germany)


    When co-combusting substitute fuels in power plants, the element Thallium should be checked in the drain of the waste water treatment system of flue gas desulphurisation. In 2005 Thallium-concentrations exceeding the limit value were determined for the first time as a consequence of the modified analysis of the supervisory authority. The previous lower Thallium concentrations with graphite tube-atomic absorption spectrometry were caused by the high chloride concentration in RAA waste water. The RAA operating mode was checked and changed. Equipment-related weak spots were detected and corrected. (orig.)

  19. Comparison of Polythionates as Precursors for the Formation of Thallium Sulfide Layers

    Directory of Open Access Journals (Sweden)

    Vitalijus JANICKIS


    Full Text Available The processes of obtaining layers of thallium, sulfides, TlxSy, by the sorption-diffusion method on polyamide 6 using solutions of lower polythionates - sodium trithionate and tetrathionate, Na2S3O6, Na2S4O6, potassium pentathionate, K2S5O6, and of dodecathionic acid, H2S12O6, as precursors of sulfur are compared. The concentration of sorbed sulfur increases with increasing the duration of treatment, the concentration and temperature of precursor solution. It rather significantly also depends on the nature - sulfurity of polythionate, i. e. on the number of sulfur atoms in the polythionate anion: effectiveness of sulfurization using solutions of dodecathionic acid is significantly higher than that of lower polythionates. Thallium sulfide layers are formed on the surface of polyamide after the treatment of sulfurized polymer with Tl(I salt solution. The concentration of thallium in the layer increases with the increase of initial sulfurization duration and in case of H2S12O6 solution used - on the temperature of this process. The results of X-ray diffraction analysis confirmed the formation of thallium sulfide layers in the surface of polyamide 6. The phase composition of layer changes depending on the conditions of initial treatment in a H2S12O6 solution. Five thallium sulfide phases, two forms of TlS, Tl2S2, Tl4S3 and Tl2S5 were identified in the composition of the layers treated for different time with a solution of dodecathionic acid at the temperature of 20 °C and 30 °C and then with Tl(I salt solution by X-ray diffraction but the maxima of TlS and Tl2S5 phases predominate in the diffractograms.

  20. A calixarene-based ion-selective electrode for thallium(I) detection

    Energy Technology Data Exchange (ETDEWEB)

    Chester, Ryan [Nanochemistry Research Institute, Department of Chemistry, Curtin University, GPO Box U1987, Perth, Western Australia 6845 (Australia); Sohail, Manzar [Faculty of Science, Health, Education and Engineering, University of the Sunshine Coast, Locked Bag 4, Maroochydore DC, Queensland 4556 (Australia); Ogden, Mark I.; Mocerino, Mauro [Nanochemistry Research Institute, Department of Chemistry, Curtin University, GPO Box U1987, Perth, Western Australia 6845 (Australia); Pretsch, Ernö [ETH Zürich, Institute of Biogeochemistry and Pollutant Dynamics (IBP), Universitätstrasse 16, CH-8092, Zürich (Switzerland); De Marco, Roland, E-mail: [Nanochemistry Research Institute, Department of Chemistry, Curtin University, GPO Box U1987, Perth, Western Australia 6845 (Australia); Faculty of Science, Health, Education and Engineering, University of the Sunshine Coast, Locked Bag 4, Maroochydore DC, Queensland 4556 (Australia)


    Highlights: • Tuning of metal binding cavities in thallium(I) calixarene ionophores. • Novel calixarene-based ionophores with improved selectivity for thallium(I). • Sandwich membrane characterization of thallium(I) binding in novel calixarenes. • Improved selectivity and sensitivity with novel thallium(I) calixarene ionophores. • Solid contact ion-selective electrodes for novel thallium(I) calixarene ionophores. - Abstract: Three new calixarene Tl{sup +} ionophores have been utilized in Tl{sup +} ion-selective electrodes (ISEs) yielding Nernstian response in the concentration range of 10{sup −2}–10{sup −6} M TlNO{sub 3} with a non-optimized filling solution in a conventional liquid contact ISE configuration. The complex formation constants (log β{sub IL}) for two of the calixarene derivatives with thallium(I) (i.e. 6.44 and 5.85) were measured using the sandwich membrane technique, with the other ionophore immeasurable due to eventual precipitation of the ionophore during these long-term experiments. Furthermore, the unbiased selectivity coefficients for these ionophores displayed excellent selectivity against Zn{sup 2+}, Ca{sup 2+}, Ba{sup 2+}, Cu{sup 2+}, Cd{sup 2+} and Al{sup 3+} with moderate selectivity against Pb{sup 2+}, Li{sup +}, Na{sup +}, H{sup +}, K{sup +}, NH{sub 4}{sup +} and Cs{sup +}, noting that silver was the only significant interferent with these calixarene-based ionophores. When optimizing the filling solution in a liquid contact ISE, it was possible to achieve a lower limit of detection of approximately 8 nM according to the IUPAC definition. Last, the new ionophores were also evaluated in four solid-contact (SC) designs leading to Nernstian response, with the best response noted with a SC electrode utilizing a gold substrate, a poly(3-octylthiophene) (POT) ion-to-electron transducer and a poly(methyl methacrylate)–poly(decyl methacrylate) (PMMA–PDMA) co-polymer membrane. This electrode exhibited a slope of 58.4 mV decade

  1. Thallium Flux Assay for Measuring the Activity of Monovalent Cation Channels and Transporters. (United States)

    Weaver, C David


    Monovalent cation channels are critically important for physiological processes ranging from the control of neuronal excitability to the maintenance of solute balance. Mutations in these channels are associated with a multiplicity of diseases and monovalent cation channel-modulating drugs are used as therapeutics. Techniques that allow the measurement of the activity of these ion channels are useful for exploring their many biological roles as well as enabling the discovery and characterization of ion channel modulators for the purposes of drug discovery. Although there are numerous techniques for measuring the activity of monovalent cation channels, the thallium flux assay technique is a widely used fluorescence-based approach. Described herein is a method for using the thallium-flux technique for detecting and quantifying the activity of small-molecule potassium channel modulators in 384-well plates.

  2. Comparative studies on right ventricular pressure and volume overloading by thallium-201 myocardial scintigraphy

    Energy Technology Data Exchange (ETDEWEB)

    Owada, K.; Tsukahara, Y.; Kijima, M.; Miyazaki, Y.; Ono, K. (Fukushima Medical Coll. (Japan))


    Thallium-201 myocardial scintigraphy was performed in 44 patients with various heart diseases including mitral stenosis, atrial septal defect, primary pulmonary hypertension, and left atrial myxoma. The morphological findings of right ventricular (RV) free wall on the scintigram and RV/IVS (interventricular septum) uptake ratio of the images obtained from the left anterior oblique projection were studied in the patients with RV pressure or volume overloading.

  3. Tunable frequency-stabilization of UV laser using a Hallow-Cathode Lamp of atomic thallium

    CERN Document Server

    Chen, Tzu-Ling; Shy, Jow-Tsong; Liu, Yi-Wei


    A frequency-stabilized ultraviolet laser system, locked to the thallium resonant transition of 377.5 nm, was demonstrated using a novel bichromatic spectroscopy technique for tuning the zero-crossing laser-lock point. The atomic thallium system is a promising candidate in atomic parity violation and permanent electric dipole moment experiments, and its 377.5 nm 6P1/2->7S1/2 transition is important for thallium laser cooling and trapping experiment. The pressure shift, owing to the high pressure bu?er gas of the hollow-cathode lamp, was observed using an atomic beam resonance as reference. Such a shift was corrected by adjusting the peak ratio of the two Doppler-free saturation pro?les resulted from two pumping beams with a 130 MHz frequency di?erence. The resulted frequency stability of the ultraviolet laser is ?0.5 MHz at 0.1 sec integration time. This scheme is compact and versatile for stabilizing UV laser systems, which acquire a sub-MHz stability and frequency tunability.

  4. Detection of human collateral circulation by vasodilation-thallium-201 tomography

    Energy Technology Data Exchange (ETDEWEB)

    Nienaber, C.A.; Salge, D.; Spielmann, R.P.; Montz, R.; Bleifeld, W. (University Hospital Eppendorf, Hamburg (Germany, F.R.))


    Coronary arteriolar vasodilation may provoke redistribution of flow to collateral-dependent jeopardized myocardium. To assess the physiologic significance of collaterals, 80 consecutive post-infarction patients (age 58 +/- 8 years) underwent vasodilation-redistribution thallium-201 tomographic imaging after administration of 0.56 mg of intravenous dipyridamole/kg body weight. Circumferential profile analysis of thallium-201 uptake and redistribution in representative left ventricular tomograms provided quantitative assessment of transient and fixed defects and separation between periinfarctional and distant inducible hypoperfusion. Tomographic perfusion data were correlated to wall motion and collateral circulation between distinct anatomic perfusion territories. Patients were grouped according to presence (59%) or absence (41%) of angiographically visible collateral channels to jeopardized myocardium. In the presence of collaterals, distant reversible defects were larger than in absence of collaterals (p less than 0.05); the extent of combined periinfarctional and distant redistribution was also larger in collateralized patients (p less than 0.025), whereas the size of the persistent perfusion defect was similar in both groups. By prospective analysis the tomographic perfusion pattern of combined periinfarctional and distant redistribution revealed a sensitivity of 85% and a specificity of 78% for the detection of significant collateral circulation in this group of patients. Thus, using the exhausted flow reserve as a diagnostic tool, vasodilation-thallium-201 tomography has the potential to identify and quantitate collateralized myocardium in post-infarction patients and may guide diagnostic and therapeutic decision-making.

  5. [Characterization of kale (Brassica oberacea var acephala) under thallium stress by in situ attenuated total reflection FTIR]. (United States)

    Yao, Yan; Zhang, Ping; Wang, Zhen-Chun; Chen, Yong-Heng


    The experiment was designed based on consumption of carbon dioxide through the photosynthesis of Brassica oberacea var acephala leaf, and the photosynthesis of kale leaf under thallium stress was investigated by in situ attenuated total reflection FTIR (in situ ATR-FTIR). The ATR-FTIR showed that the absorption peaks of leaves had no obvious difference between plants growing in thallium stress soil and plants growing in non-thallium pollution soil, and the strong peaks at 3,380 cm(-1) could be assigned to the absorption of water, carbohydrate, protein or amide; the strong peaks at 2,916 and 2,850 cm(-1) assigned to the absorption of carbohydrate or aliphatic compound; the peaks at 1,640 cm(-1) assigned to the absorption of water. However, as detected by the in situ ATR-FTIR, the double peaks (negative peaks) at 2,360 and 2,340 cm(-1) that are assigned to the absorption of CO2 appeared and became high gradually. It was showed that kale was carrying photosynthesis. At the same time, the carbon dioxide consumption speed of leaf under thallium stress was obviously larger than that of the blank It was expressed that photosynthesis under thallium stress was stronger than the blank All these represented that kale had certain tolerance to the heavy metal thallium. Meanwhile, the carbon dioxide consumption of grown-up leaf was more than that of young leaf whether or not under thallium stress. It was also indicated that the intensity of photosynthesis in grown-up leaf is higher than that in young leaf.

  6. Thallium and manganese complexes involved in the luminescence emission of potassium-bearing aluminosilicates

    Energy Technology Data Exchange (ETDEWEB)

    Gomez-Gonzalez, Miguel A., E-mail: [Museo Nacional de Ciencias Naturales, CSIC, Jose Gutierrez Abascal 2, Madrid E-28006 (Spain); Garcia-Guinea, Javier, E-mail: [Museo Nacional de Ciencias Naturales, CSIC, Jose Gutierrez Abascal 2, Madrid E-28006 (Spain); Garrido, Fernando, E-mail: [Museo Nacional de Ciencias Naturales, CSIC, Jose Gutierrez Abascal 2, Madrid E-28006 (Spain); Townsend, Peter D., E-mail: [School of Science and Technology, University of Sussex, Brighton BN1 9QH (United Kingdom); Marco, Jose-Francisco, E-mail: [Instituto de Química-Física Rocasolano, CSIC, Calle Serrano 119, Madrid E-28006 (Spain)


    The luminescence emission at 285 nm in natural K-feldspar has been studied by Russian groups and associated with thallium ions in structural positions of K{sup +} sites as artificially thallium-doped feldspars display the same emission band. Here attention is focussed on spectra of CL emission bands centered near 285 and 560 nm from paragenetic adularia, moscovite and quartz micro-inclusions. With accesorial thallium they show clear resemblances to each other. Associated sedimentary and hydrothermal aluminosilicate samples collected from Guadalix (Madrid, Spain) were analyzed with a wide range of experimental techniques including Environmental Scanning Electron Microscopy (ESEM) with an attached X-Ray Energy-Dispersive Spectrometer (EDS) and a cathodoluminescence probe (CL) and Electron Probe Microanalysis (EPMA), X-Ray Fluorescence Spectrometry (XRF), Inductively Coupled Plasma-Optical Emission Spectrometry (ICP-OES), Differential and Thermogravimetric Analyses (DTA-TG), radioluminescence (RL), Mössbauer spectroscopy and X-Ray Photoelectron Spectrometry (XPS). The luminescence emission bands at 285 and 560 nm seem to be associated with hydrous thallium–manganese complexes bonded to potassium-bearing aluminosilicates since various minerals such as K-feldspar, moscovite and quartz micro-inclusions display similar CL spectra, accesorial thallium and hydroxyl groups. The presence of iron introduces a brown color which is attributed to submicroscopic iron oxides detectable in the optical and chemical microanalysis, but this does not contribute to the luminescence emission. The XPS Mn 2p spectrum of the adularia sample at room temperature is composed of a spin–orbit doublet plus clear shake-up satellite structure ∼4 eV above the main photoemision lines and is consistent with Mn{sup 2+} in good agreement with the observed luminescence emission at 560 nm for aluminosilicates produced by a {sup 4}T1({sup 4}G)→{sup 6}A1({sup 6}S) transition in tetrahedrally

  7. Diagnostic value of 123I-phenylpentadecanoic acid (IPPA) metabolic and thallium 201 perfusion imaging in stable coronary artery disease. (United States)

    Walamies, M; Turjanmaa, V; Koskinen, M; Uusitalo, A


    The diagnostic value of 123I-phenylpentadecanoic acid (IPPA) metabolic cardiac imaging was studied in a group (n = 29) of patients with angiographically confirmed CAD using single photon emission computed tomography (SPECT). A symptom-limited exercise test was first done with IPPA, and 2 days later with thallium. Medications were not withheld during testing. Fourteen healthy control subjects participated in parallel IPPA and 15 in thallium tests. Data acquisition and output were comparable in the two imaging modalities. By testing various relatively simple criteria for abnormality we found that the semiquantitative interpretation was more accurate than the visual readings. The best compromise of accuracy with the scored criteria consisted of a sensitivity of 86% and a specificity of 86%, obtained with IPPA polar tomograms (mild exercise defect) and a sensitivity of 86% and a specificity of 80% obtained with thallium (regionally decreased washout). With visual interpretation alone, a sensitivity of 83% and a specificity of 71% was detected with IPPA (mild exercise defect) and 72% and 73%, respectively, with thallium (partial reversibility). The sensitivity of the exercise ECG alone was 62%. The results of this study imply that IPPA imaging could be a rational, uncomplicated clinical method for non-invasive diagnosis of CAD. The diagnostic ability of IPPA is at least as good as that of thallium, and it is possible to use them in succession.

  8. Dilatation of the left ventricular cavity on dipyridamole thallium-201 imaging: A new marker of triple-vessel disease

    Energy Technology Data Exchange (ETDEWEB)

    Takeishi, Y.; Tono-oka, I.; Ikeda, K.; Komatani, A.; Tsuiki, K.; Yasui, S. (Yamagata Univ. School of Medicine (Japan))


    To investigate the significance and mechanism of dilatation of the left ventricular cavity on dipyridamole thallium-201 imaging, we performed both dipyridamole thallium-201 imaging and dipyridamole radionuclide angiography on 83 patients with known angiograms. The dipyridamole/delayed ratio of the left ventricular dimension from the thallium-201 image was defined as the left ventricular dilatation ratio (LVDR). An LVDR greater than the mean + two standard deviations in patients without coronary artery disease was defined as abnormal. Twenty-two of 83 patients showed an abnormal LVDR, and 18 of the 22 patients (82%) had triple-vessel disease. By defect and washout analysis, the sensitivity and specificity for correctly identifying the patients as having triple-vessel disease was 72% and 76%, respectively, whereas LVDR had a sensitivity of 72% and a specificity of 93%. When LVDR was used in combination with the defect and washout criteria, sensitivity increased to 84% without a loss of specificity. In those 22 patients with abnormal LVDRs, end-diastolic volume measured by radionuclide angiography did not change after dipyridamole infusion. Dilatation of the left ventricular cavity on dipyridamole thallium-201 imaging reflected relative subendocardial hypoperfusion induced by dipyridamole rather than actual chamber enlargement. The LVDR was moderately sensitive and highly specific for triple-vessel disease and provided complementary information to dipyridamole thallium-201 imaging.

  9. VANADIUM ALLOYS (United States)

    Smith, K.F.; Van Thyne, R.J.


    This patent deals with vanadium based ternary alloys useful as fuel element jackets. According to the invention the ternary vanadium alloys, prepared in an arc furnace, contain from 2.5 to 15% by weight titanium and from 0.5 to 10% by weight niobium. Characteristics of these alloys are good thermal conductivity, low neutron capture cross section, good corrosion resistance, good welding and fabricating properties, low expansion coefficient, and high strength.

  10. A preliminary investigation and evaluation of the thallium environmental impacts of the unmined Xiangquan thallium-only deposit in Hexian, China (United States)

    Zhou, Taofa; Fan, Yu; Yuan, Feng; Cooke, David; Zhang, Xin; Li, Liangjun


    The Xiangquan Thallium-only deposit in Hexian, east China is a newly found near-surface and unmined shallow-seated thallium deposit. The 250t Tl deposit is hosted in Lower Ordovician Lunshan Group as lenticular and confined by northeast F1, F2 faults. The metallic minerals are dominated by pyrite, more than 95% Tl occurs in pyrite as tiny individual grains or as ‘‘invisible thallium”. Tl and other trace elements pollution in ecosystems such as soils, surface and ground waters and water sediments, plants and crops, and animal and human beings in Xiangquan near the Tl ore deposit have been investigated and evaluated. Results show that Tl as well as As and Sb in ecosystems in Xiangquan around the deposit have enriched, they came from Tl-pyrite in the ore bodies and in the parent rocks of weathered soils on top of the ore bodies and went into the nearby ecosystems through weathering, leaching and dissolving. In 2 km2 around the Xiaolongwang Mountain where the Tl ore deposit seated, soils, vegetables, crops have been polluted or heavily polluted by Tl, As and Sb. Farmlands near the ore body are not fit to grow vegetables and crops. Thermal Spring water in Xiangquan town and pond water close to the Tl deposit are not potable. Tl also enriches in human hair and urinate of villagers who live close to the Tl deposit. Even through the Tl-only deposit has put clear environmental impacts on the local environment and ecosystems around it, no serious consequences of Tl pollution have so far taken place due to unmining of the Tl deposit as well as the screen effect of the silicficious breccia cap on top of it. All this work adds new knowledge to understand Tl behavior in unmined Tl deposit, and also benefit to the local environmental protection and the future mineral resources exploration.

  11. {sup 201}Thallium SPECT, accuracy in astrocytoma diagnosis and treatment evaluation

    Energy Technology Data Exchange (ETDEWEB)

    Kaellen, K


    The aims of the studies included in this thesis were: - to investigate the reliability of {sup 201}Thallium single photon emission computed tomography. Tl SPECT for preoperative diagnosis and histological staging of malignant astrocytomas in comparison with CT; - to develop a method for quantification of cerebral thallium uptake, and to evaluate the quantitative measurement in comparison with CT, for astrocytoma treatment follow-up purposes; - to compare quantitative Tl SPECT and proton magnetic resonance spectroscopy (H-MRS) with conventional MR imagingfor astrocytoma monitoring, and to evaluate associations between change of morphological tumour characteristics during treatment and changes of cerebral thallium uptake and metabolic ratios. Results and conclusions: - High TI-index, calculated as a ratio comparing tumour uptake to uptake in the contralateral hemisphere, is an indicator of highly malignant astrocytoma. Differentiation between the high-grade astrocytomas, the low-grade astrocytomas, and infectious lesions is only partial, with an overlap of Tl-indexes between these groups. High-grade astrocytomas that do not show contrast enhancement on CT, and astrocytomas with central necrosis and moderate ring-enhancement, tend to be underestimated when evaluated by Tl-index calculation. Tl SPECT is not a reliable method for non-invasive tumour staging among the group of highly malignant astrocytomas. - Quantification of cerebral TI-uptake, defining the volume of viable tumour tissue, is a new method for astrocytoma chemotherapy monitoring. Results suggest that the method provides prognostic information, and information of treatment efficacy, at an earlier stage than CT. - We did not find a higher accuracy of quantitative Tl SPECT than of MR for monitoring purposes and our results indicated that treatment induced MR changes were interrelated with TI-uptake variations. - Multi-voxel H-MRS was difficult to apply for astrocytoma treatment monitoring, due to the

  12. A Novel Ion - selective Polymeric Membrane Sensor for Determining Thallium(I) With High Selectivity (United States)

    Kassim, Anuar; Rezayi, Majid; Ahmadzadeh, Saeid; Rounaghi, Gholamhossein; Mohajeri, Masoomeh; Azah Yusof, Noor; Tee, Tan Wee; Yook Heng, Lee; Halim Abdullah, Abd


    Thallium is a toxic metal that introduced into the environment mainly as a waste from the production of zinc, cadmium, and lead and by combustion of coal. Thallium causes gastrointestinal irritation and nerve damage when people are exposed to it for relatively short period of time. For long term, thallium has the potential to cause the following effects: change in blood chemistry, damage to liver, kidney, intestinal and testicular tissue, and hair loss. In this work a membrane was prepared by use of 4'-nitrobenzo -18-crown-6 (4'NB18C6) as an ion carrier, polyvinylchloride (PVC) as a matrix, and diocthylphetalate (DOP) as a plasticizer for making an ion selective electrode for measurement of Tl+ cation in solutions. The amount of 4'-nitrobenzo-18C6 and polyvinylchloride were optimized in the preparation of the membrane. The response of the electrode was Nernstian within the concentration range 1.0 × 10-8 to 1.0 × 10-1M. This sensor displays a drift in Nernstian response for this cation with increasing the amount of ionophore and decreasing the amount of polyvinylchloride.The results of potentiometric measurements showed that, this electrode also responses to Cu2+ Ni2+ and Pb2+ cations, but the electrode has a wider dynamic range and a lower detection limit to Tl+ cation. The effects of various parameters such as pH, different cations interferences, effect of the amount of ionophore and polyvinylchloride and time on response of the coated ion selective electrode were investigated. Finally the constructed electrode was used in complexometric and precipitation titrations of Tl+ cation with EDTA and KBr, respectively. The response of the fabricated electrode at concentration range from 1.0 × 10-8 to 1.0 × 10-1M is linear with a Nernstian slope of 57.27 mV.

  13. Oxidative stress and DNA damage in broad bean (Vicia faba L.) seedlings induced by thallium. (United States)

    Radić, Sandra; Cvjetko, Petra; Glavas, Katarina; Roje, Vibor; Pevalek-Kozlina, Branka; Pavlica, Mirjana


    Thallium (Tl) is a metal of great toxicological concern because it is highly toxic to all living organisms through mechanisms that are yet poorly understood. Since Tl is accumulated by important crops, the present study aimed to analyze the biological effects induced by bioaccumulation of Tl in broad bean (Vicia faba L.) as well as the plant's antioxidative defense mechanisms usually activated by heavy metals. Thallium toxicity was related to production of reactive oxygen species in leaves and roots of broad bean seedlings following short-term (72 h) exposure to thallium (I) acetate (0, 0.5, 1, 5, and 10 mg/L) by evaluating DNA damage and oxidative stress parameters as well as antioxidative response. The possible antagonistic effect of potassium (K) was tested by combined treatment with 5 mg/L of Tl (Tl+) and 10 mg/L of potassium (K+) acetate. Accumulation of Tl+ in roots was 50 to 250 times higher than in broad bean shoots and was accompanied by increase in dry weight and proline. Despite responsive antioxidative defense (increased activities of superoxide dismutase, ascorbate peroxidase, and pyrogallol peroxidase), Tl+ caused oxidative damage to lipids and proteins as evaluated by malondialdehyde and carbonyl group levels, and induced DNA strand breaks. Combined treatment caused no oxidative alternations to lipids and proteins though it induced DNA damage. The difference in Tl-induced genotoxicity following both acellular and cellular exposure implies indirect DNA damage. Results obtained indicate that oxidative stress is involved in the mechanism of Tl toxicity and that the tolerance of broad bean to Tl is achieved, at least in part, through the increased activity of antioxidant enzymes.

  14. Thallium Intoxication Treated with Long-Term Hemodialysis, Forced Diuresis and Prussian Blue

    DEFF Research Database (Denmark)

    Larsen, Elfinn; Solgaard, Per Bent; Freund, L. Gade


    A 56 yr old woman, who ingested 2 g of thallium sulfate, was successfully treated with long-term hemodialysis for 200 h during 10 days, combined with forced diuresis and Prussian blue. The effect of the artificial kidney dialysis was determined by repeated analysis of the Tl concentration...... in the dialysis bath and in blood samples. During the 1st 120 h of hemodialysis, 143 mg of Tl was eliminated via the artificial kidney and 110 mg via the urinary tract. The present case of acute Tl intoxication is the 1st in which long-term hemodialysis has been used in the acute phase...

  15. Experimental excitation functions of deuteron induced reactions on natural thallium up to 50 MeV

    Energy Technology Data Exchange (ETDEWEB)

    Adam Rebeles, R., E-mail: [Cyclotron Laboratory, Vrije Universiteit Brussel, B-1090 Brussels (Belgium); Van den Winkel, P.; Hermanne, A. [Cyclotron Laboratory, Vrije Universiteit Brussel, B-1090 Brussels (Belgium); Tarkanyi, F.; Takacs, S. [Institute of Nuclear Research of the Hungarian Academy of Sciences, Debrecen H-4026 (Hungary)


    Excitation functions of deuteron induced reactions on natural thallium leading to the formation of {sup 204m,203m2+m1+g,202m,201m+g,200}Pb and {sup 202,201m+g,200m+g}Tl isotopes were determined up to 50 MeV. The cross sections were measured by an activation technique using stacked foil irradiation. The excitation functions of the investigated reactions are compared with data reported in literature and also with the theoretical results of TALYS nuclear reaction code. From the measured cross section data, the thick target yield for the medical interesting {sup 203}Pb isotope is calculated.

  16. Application of Hyphenated Techniques in Speciation Analysis of Arsenic, Antimony, and Thallium (United States)

    Michalski, Rajmund; Szopa, Sebastian; Jabłońska, Magdalena; Łyko, Aleksandra


    Due to the fact that metals and metalloids have a strong impact on the environment, the methods of their determination and speciation have received special attention in recent years. Arsenic, antimony, and thallium are important examples of such toxic elements. Their speciation is especially important in the environmental and biomedical fields because of their toxicity, bioavailability, and reactivity. Recently, speciation analytics has been playing a unique role in the studies of biogeochemical cycles of chemical compounds, determination of toxicity and ecotoxicity of selected elements, quality control of food products, control of medicines and pharmaceutical products, technological process control, research on the impact of technological installation on the environment, examination of occupational exposure, and clinical analysis. Conventional methods are usually labor intensive, time consuming, and susceptible to interferences. The hyphenated techniques, in which separation method is coupled with multidimensional detectors, have become useful alternatives. The main advantages of those techniques consist in extremely low detection and quantification limits, insignificant interference, influence as well as high precision and repeatability of the determinations. In view of their importance, the present work overviews and discusses different hyphenated techniques used for arsenic, antimony, and thallium species analysis, in different clinical, environmental and food matrices. PMID:22654649

  17. Evaluation of myocardial abnormalities in collagen diseases by thallium-201 myocardial scintigraphy

    Energy Technology Data Exchange (ETDEWEB)

    Yamano, Shigeru; Kagoshima, Tadashi; Sugihara, Kiyotaka (Nara Medical Univ., Kashihara (Japan)) (and others)


    This study was performed to evaluate myocardial abnormalities in patients with collagen diseases by exercise and rest thallium-201 myocardial scintigrams. A total of 65 patients without ischemic ECG changes, consisting of 18 with systemic lupus erythematosus (SLE), 18 with polymyositis (PM), 8 with progressive systemic sclerosis (PSS), and 21 with Sjoegren's syndrome (SjS), was enrolled in this study. Reversible exercise-induced defects scintigraphically suggesting myocardial ischemia were noted in 8 cases of SLE, 4 cases of PM, 4 cases of PSS, and 3 cases of SjS. Nineteen patients had exercise-induced defects and underwent cardiac catheterization, 8 of whom had normal coronary angiograms. Fixed hypoperfusion areas were observed in one case of SLE, 6 cases of PM and 3 cases of SjS. Rest thallium-201 myocardial scintigram disclosed hypoperfusion areas which were not induced by exercise in 2 cases of SLE, 3 cases of PM, one case of PSS and 5 cases of SjS. Echocardiogram showed no significant differences in ejection fraction and % fractional shortening between the disease groups and healthy control group. These findings suggest that patients with collagen diseases have abnormalities of coronary circulation at the level of the intramural vasculature before cardiac function impairment, myocardial fibrosis and functional abnormalities at the cell membrane. (author).

  18. Follow-up Thallium-201 scintigraphy after mantle field radiotherapy for Hodgkin's disease

    Energy Technology Data Exchange (ETDEWEB)

    Pierga, J.Y.; Girinski, T.; Henry-Amar, M. (Institut Gustave Roussy, Villejuif (France)); Maunoury, C.; Valette, H.; Tchernia, G.; Desgrez, A. (Centre Hospitalier de Bicetre, Le Kremlin-Bicetre (France)); Socie, G. (Institut Gustave Roussy, Villejuif (France) Hopital St Louis, Paris (France)); Cosset, J.M. (Institut Gustave Roussy, Villejuif (France) Institut Curie, Paris (France))


    Assessment of the long-term cardiac effects of mediastinal radiotherapy for Hodgkin's disease, by Thallium scintigraphy. 32 patients (14 males and 18 females) who underwent mantle field radiotherapy for Hodgkin's disease were included in this study. Twenty patients received 4 fractions of 2.5 Gy per week and 12, five fraction of 2 Gy per week, delivered on alternate days. All the patients, except three, performed exercise testing electrocardiogram and Thallium-201 tomoscintigraphy. The average time interval from completion of treatment to the study was 7 years (range 3--13 years). No patients had clinical symptoms of cardiac disease. Mean age at the time of the study was 35 years (range 23--48 years). Two electrocardiograms revealed left bundle branch block and the patients were excluded from the study. Only one out of 27 exercise electrocardiograms was abnormal in a patient with mitral valve prolapse, who was also excluded from the study. Twenty-six scintigraphies were evaluable. Twenty-two (85%) were clearly abnormal with partial or complete redistribution on delayed images. The anterior region was affected in 19 of these cases (86%). Four explorations were undoubtedly normal. Coronary angiography was not performed for ethical reasons in these asymptomatic patients. Despite possible false positive tests, the high rate of abnormality (85%) in this small series is striking. These preliminary data justify larger studies and a close long-term follow-up of these patients. 24 refs., 1 fig., 2 tabs.

  19. Thallium occurrence and partitioning in soils and sediments affected by mining activities in Madrid province (Spain)

    Energy Technology Data Exchange (ETDEWEB)

    Gomez-Gonzalez, M.A.; Garcia-Guinea, J. [National Museum of Natural Sciences, CSIC, Jose Gutierrez Abascal 2, 28006 Madrid (Spain); Laborda, F. [Group of Analytical Spectroscopy and Sensors Group, Institute of Environmental Sciences, University of Zaragoza, Pedro Cerbuna 12, 50009 Zaragoza (Spain); Garrido, F., E-mail: [National Museum of Natural Sciences, CSIC, Jose Gutierrez Abascal 2, 28006 Madrid (Spain)


    Thallium (Tl) and its compounds are toxic to biota even at low concentrations but little is known about Tl concentration and speciation in soils. An understanding of the source, mobility, and dispersion of Tl is necessary to evaluate the environmental impact of Tl pollution cases. In this paper, we examine the Tl source and dispersion in two areas affected by abandoned mine facilities whose residues remain dumped on-site affecting to soils and sediments of natural water courses near Madrid city (Spain). Total Tl contents and partitioning in soil solid phases as determined by means of a sequential extraction procedure were also examined in soils along the riverbeds of an ephemeral and a permanent streams collecting water runoff and drainage from the mines wastes. Lastly, electronic microscopy and cathodoluminescence probe are used as a suitable technique for Tl elemental detection on thallium-bearing phases. Tl was found mainly bound to quartz and alumino-phyllosilicates in both rocks and examined soils. Besides, Tl was also frequently found associated to organic particles and diatom frustules in all samples from both mine scenarios. These biogenic silicates may regulate the transfer of Tl into the soil-water system. - Highlights: • Abandoned mine residues are Tl sources in soils of Madrid catchment area. • Tl was associated to quartz and aluminosilicates in both rocks and soils. • Tl was frequently found associated to organic particles and diatom frustules. • Cathodoluminescence is a suitable technique for Tl detection on soils and rocks.

  20. [Detecting Thallium in Water Samples using Dispersive Liquid Phase Microextraction-Graphite Furnace Atomic Absorption Spectroscopy]. (United States)

    Zhu, Jing; Li, Yan; Zheng, Bo; Tang, Wei; Chen, Xiao; Zou, Xiao-li


    To develope a method of solvent demulsification dispersive liquid phase microextraction (SD-DLPME) based on ion association reaction coupled with graphite furnace atomic absorption spectroscopy (GFAAS) for detecting thallium in water samples. Methods Thallium ion in water samples was oxidized to Tl(III) with bromine water, which reacted with Cl- to form TlCl4-. The ionic associated compound with trioctylamine was obtained and extracted. DLPME was completed with ethanol as dispersive solvent. The separation of aqueous and organic phase was achieved by injecting into demulsification solvent without centrifugation. The extractant was collected and injected into GFAAS for analysis. With palladium colloid as matrix modifier, a two step drying and ashing temperature programming process was applied for high precision and sensitivity. The linear range was 0.05-2.0 microg/L, with a detection limit of 0.011 microg/L. The relative standard derivation (RSD) for detecting Tl in spiked water sample was 9.9%. The spiked recoveries of water samples ranged from 94.0% to 103.0%. The method is simple, sensitive and suitable for batch analysis of Tl in water samples.

  1. The learning machine in quantitative chemical analysis : Part I. Anodic Stripping Voltammetry of Cadmium, Lead and Thallium

    NARCIS (Netherlands)

    Bos, M.; Jasink, G.


    The linear learning machine method was applied to the determination of cadmium, lead and thallium down to 10-8 M by anodic stripping voltammetry at a hanging mercury drop electrode. With a total of three trained multicategory classifiers, concentrations of Cd, Pb and Tl could be predicted with an

  2. Thallium chloride 201Tl combined with single photon emission computed tomography (SPECT) in the evaluation of vestibular schwannoma growth

    DEFF Research Database (Denmark)

    Charabi, Samih Ahmed; Lassen, N A; Thomsen, J


    Thallium chloride 201Tl combined with SPECT was performed in a series of 29 patients with neuroradiological evidence of vestibular schwannoma (VS). The relative tumor uptake (U) and relative tumor concentration (C) of the radiotracer 201Tl was determined, and the cerebellum served as a reference...

  3. BRAZING ALLOYS (United States)

    Donnelly, R.G.; Gilliland, R.G.; Slaughter, G.M.


    A brazing alloy is described which, in the molten state, is characterized by excellent wettability and flowability and is capable of forming a corrosion-resistant brazed joint. At least one component of said joint is graphite and the other component is a corrosion-resistant refractory metal. The brazing alloy consists essentially of 40 to 90 wt % of gold, 5 to 35 wt% of nickel, and 1 to 45 wt% of tantalum. (AEC)

  4. Bis(2-mercapto-1-R-imidazolyl)hydroborato complexes of aluminium, gallium, indium and thallium: compounds possessing gallium-gallium bonds and a trivalent thallium alkyl. (United States)

    Yurkerwich, Kevin; Coleman, Fergal; Parkin, Gerard


    The reactions of bis(mercaptoimidazolyl)hydroborato derivatives [Bm(R)]M' (R = Me, Bu(t); M' = Li, Na, Tl) with MX(3) trihalides of aluminium, gallium and indium yield both 1:1 and 2:1 complexes of the types [Bm(R)]MX(2) and [Bm(R)](2)MX, respectively. Structurally characterized examples of the [Bm(R)]MX(2) series include [Bm(Me)]AlCl(2), [Bm(Me)]GaI(2), [Bm(Me)]InI(2), [Bm(Bu(t))]AlCl(2) and [Bm(Bu(t))]GaX(2) (X = Cl, Br, I), while structurally characterized examples of the [Bm(R)](2)MX series include [Bm(Bu(t))](2)InX (X = Cl, Br, I). In addition to the halide complexes, the trivalent dimethyl thallium complex [Bm(Bu(t))]TlMe(2) has been synthesized via the reaction of [Bm(Bu(t))]Tl with Me(2)TlCl. The reactions of [Bm(R)]M' with the monovalent halides, "GaI", InCl and InI, result in disproportionation. In the case of indium, the mononuclear complexes [Bm(Bu(t))](2)InI and [Bm(Bu(t))]InCl(kappa(2)-mim(Bu(t))) are obtained, whereas for gallium, dinuclear compounds that feature Ga-Ga bonds, namely [Bm(R)](GaI)(GaI)[Bm(R)] (R = Me, Bu(t)) have been isolated.

  5. Thallium stress testing does not predict cardiovascular risk in diabetic patients with end-stage renal disease undergoing cadaveric renal transplantation

    Energy Technology Data Exchange (ETDEWEB)

    Holley, J.L.; Fenton, R.A.; Arthur, R.S. (Univ. of Pittsburgh, PA (USA))


    This study assessed the usefulness of thallium stress testing as a predictor of perioperative cardiovascular risk in diabetic patients with end-stage renal disease undergoing cadaveric renal transplantation. Demographic factors influencing the exercise performance in these patients were also examined. The medical records of 189 consecutive patients with diabetic nephropathy who were evaluated for cadaveric renal transplantation were reviewed. Thallium stress testing was the initial examination of cardiovascular status in 141 patients. An adequate examination was one in which at least 70% of maximum heart rate was achieved. A thallium stress test was normal if there were no ST segment depressions on the electrocardiogram and no perfusion abnormalities on the thallium scan. Forty-four patients underwent cardiac catheterization as the initial evaluation (Group C) and four patients underwent transplantation without a formal cardiovascular evaluation (Group D). Sixty-four of the 141 patients undergoing thallium stress testing had an adequate and normal examination (Group A). The incidence of perioperative cardiac events in this group was 2%. Seventy-seven patients (Group B) had an abnormal (n = 41) or an inadequate (n = 36) thallium stress test and most (n = 61) then underwent coronary angiography. The use of beta-blockers was the only predictor of an abnormal or inadequate thallium stress test. Forty-three percent of patients with inadequate or abnormal thallium stress tests had significant coronary artery disease on cardiac catheterization. The perioperative risk of cardiac events was not different in Group A versus Groups B, C, and D combined. Survival of Group A and B patients was not different but was significantly longer than that of Group C patients.

  6. Evaluation of thallium-201 scanning for detection of latent coronary artery disease (United States)

    Johnson, P. C.; Leblanc, A.; Deboer, L.; Jhingran, S.


    The use of thallium imaging as a noninvasive method to accurately screen shuttle passengers for latent coronary artery disease was investigated. All radionuclide procedures were performed using an Anger type camera with a high resolution collimator. A minimum of 200,000 counts were collected for each image using a 20% window centered on the 69-83 keV X-rays. For the images obtained following injection with the patient at rest, the testing was begun 10 minutes after injection. Injections of TT during exercise were made at a point near the termination of the treadmill procedure as determined by either the appearance of ST segment changes on the electrocardiogram consistant with subendocardial ischemia, the appearance of angina-like chest pain in the patient or fatigue in the patient which required cessation of the test. The severity of heart disease was based on the medical history, physical exam, exercise electrocardiograms, chest X-rays and the coronary arteriogram.

  7. BaHg2Tl2. An unusual polar intermetallic phase with strong differentiation between the neighboring elements mercury and thallium. (United States)

    Dai, Jing-Cao; Gupta, Shalabh; Gourdon, Olivier; Kim, Hyun-Jeong; Corbett, John D


    High yields of the novel BaHg(2)Tl(2) are achieved from reactions of the appropriate cast alloys at approximately 400 degrees C. (Isotypic SrHg(2)Tl(2) also exists.) The tetragonal barium structure (P4(2)/mnm, a = 10.606 A, c = 5.159 A) was refined from both single-crystal X-ray and neutron powder diffraction data in order to ensure the atom site assignments although distances and calculated atom site population also support the results. The Hg and Tl network atoms are distinctive in their functions and bonding. Parallel chains of Hg hexagons and of Tl tetrahedra along c are constructed from polyhedra that share opposed like edges, and these are in turn interconnected by Hg-Tl bonds. Overall, the number of Tl-Tl bonds per cell exceeds the Hg-Hg type by 20:12, but these are approximately 1:2 each in bonding according to their average -ICOHP values (related to overlap populations). Barium is bound within a close 15-atom polyhedron, 12 atoms of which are the more electronegative Hg. LMTO-ASA calculations show that scalar relativistic effects are particularly important for Hg 5d-6s mixing in Hg-Hg and Hg-Tl bonding, whereas relatively separate Tl 6s and 6p states are more important in Tl-Tl interactions. The 6p states of Hg and Tl and 5d of Ba define a dominant conduction band around E(F), and the phase is metallic and Pauli-like paramagnetic. The thallium characteristics here are close to those in numerous alkali-metal-Tl cluster systems. Other active metal-mercury phases that have been studied theoretically are all distinctly electron-richer and more reduced, and without appreciable net 5d, 6s contributions to Hg-Hg bonding.

  8. Thallium Analysis in Environmental Samples by Inductively Coupled Plasma Mass Spectrometry; Analisis de Talio en Muestras Ambientales por Espectrometria de Masas con Fuente de Plasma de Acoplamiento Inductivo

    Energy Technology Data Exchange (ETDEWEB)

    Higueras, I.; Fernandez, M.; Conde, E.; Gajate, A.


    Due to its high toxicity, thallium has been considered by the US Environmental Protection Agency as one of the priority pollutants to be controlled. While being a highly toxic element, thallium has been studied to a much lesser degree than other toxic elements, mainly because thallium is often undetected by classical analytical methods. Thallium is a rare and dispersed element that occurs mainly in sulfur-containing ores. Thus, it is a potential pollutant to surrounding environment, if Tl-rich mineral and/or their industrial wastes are not properly disposed. In this work an Inductively Coupled Plasma Mass Spectrometry analytical procedure has been developed in order to determine thallium in environmental solid samples and its application to the study of this element as a potential pollutant associated with natural and anthropogenic activities. The analytical procedure has been validated by the use of appropriate reference materials, and through the isotope dilution technique as a primary method of measurement. Finally, the developed procedure has been applied to several samples from a mining area, as one of the scenarios where thallium it is likely to occur. (Author) 87 refs.

  9. A Case-Control Study of Prenatal Thallium Exposure and Low Birth Weight in China. (United States)

    Xia, Wei; Du, Xiaofu; Zheng, Tongzhang; Zhang, Bin; Li, Yuanyuan; Bassig, Bryan A; Zhou, Aifen; Wang, Youjie; Xiong, Chao; Li, Zhengkuan; Yao, Yuanxiang; Hu, Jie; Zhou, Yanqiu; Liu, Juan; Xue, Weiyan; Ma, Yue; Pan, Xinyun; Peng, Yang; Xu, Shunqing


    Thallium (Tl) is a highly toxic heavy metal widely present in the environment. Case reports have suggested that maternal exposure to high levels of Tl during pregnancy is associated with low birth weight (LBW), but epidemiological data are limited. This study was designed to evaluate whether prenatal Tl exposure is associated with an increased risk of LBW. This case-control study involving 816 study participants (204 LBW cases and 612 matched controls) was conducted in Hubei Province, China, in 2012-2014. Tl concentrations were measured in maternal urine collected at delivery, and associations with LBW were evaluated using conditional logistic regression. Higher maternal urinary Tl levels were significantly associated with increased risk of LBW [crude odds ratio (OR) = 1.52; 95% CI: 1.00, 2.30 for the highest vs. lowest tertile], and the association was similarly elevated after adjustment for potential confounders (adjusted OR = 1.90; 95% CI: 1.01, 3.58 for the highest vs. lowest tertile). Stratified analyses showed slightly higher risk estimates for LBW associated with higher Tl levels for mothers case-control study to investigate the association between prenatal Tl exposure and LBW. The results suggest that prenatal exposure to high levels of Tl may be associated with an increased risk of LBW. Xia W, Du X, Zheng T, Zhang B, Li Y, Bassig BA, Zhou A, Wang Y, Xiong C, Li Z, Yao Y, Hu J, Zhou Y, Liu J, Xue W, Ma Y, Pan X, Peng Y, Xu S. 2016. A case-control study of prenatal thallium exposure and low birth weight in China. Environ Health Perspect 124:164-169;

  10. Evaluation of myocardial abnormalities in patients with collagen diseases by thallium-201 myocardial scintigram

    Energy Technology Data Exchange (ETDEWEB)

    Yamano, Shigeru (Nara Medical Univ., Kashihara (Japan))


    This study was performed to evaluate myocardial lesions in patients with collagen diseases by rest and exercise thallium-201 myocardial scintigraphies. A total of 76 patients without ischemic ECG changes, consisting of 27 cases of systemic lupus erythematosus (SLE), 17 cases of polymyositis or dermatomyositis (PM[center dot]DM), 11 cases of progressive systemic sclerosis (PSS), and 21 cases of Sjoegren's syndrome (SjS), were enrolled in this study. Reversible exercise-induced defects suggesting myocardial ischemia were noted in 12 cases of SLE, 5 cases of PM[center dot]DM, 3 cases of PSS, and 3 cases of SjS. Of the 23 patients who had exercise-induced defects, 9 patients showed normal coronary angiograms by cardiac catheterization. Fixed hypoperfusion areas were observed in 5 cases of SLE, 6 cases of PM[center dot]DM, 4 cases of PSS and 3 cases of SjS. Rest thallium-201 myocardial scintigraphy disclosed hypoperfusion areas, which were not induced by exercise, in 1 case of SLE, 4 cases of PM[center dot]DM, 1 case of PSS and 5 cases of SjS. Endomyocardial biopsy was performed on 20 patients. Myocardial lesions in PM[center dot]DM and PSS were more severe and wide spread than in SLE. Ejection fraction and fractional shortening evaluated by echocardiography had no significant differences between each disease group and the healthy control group. These findings suggest that patients with collagen diseases show the presence of abnormalities of coronary circulation at the level of the intramyocardial vasculature in the stage before impairment of cardiac function, myocardial fibrosis and functional abnormalities of the cell membrane level that were not dependent on myocardial ischemia. (author).

  11. Development and Applications of Thallium isotopes: a new proxy tracking the extent of manganese oxide burial (United States)

    Owens, J. D.; Nielsen, S.; Ostrander, C.; Peterson, L. C.; Anbar, A. D.


    Thallium (Tl) isotopes are a new and potential powerful paleoredox proxy with the possibility to track bottom water oxygen conditions based on the burial flux of manganese oxides. Thallium has a residence time of ~20 thousand years, which is long enough to render modern oxic seawater conservative with respect to concentration and isotopes. The isotopic signature of Tl in the global ocean is driven mainly by two outputs (1) adsorption onto manganese oxides and (2) low temperature oceanic crust alteration. Importantly, the isotopic inputs of Tl are all nearly the same value; thus, the isotopic composition and flux of the outputs almost exclusively set the seawater signature. For relatively short term redox events it is reasonable to assume that the dominant isotope fractionation process is associated with manganese oxide precipitation because low temperature alteration is controlled by long-term average ocean crust production rates. We present a broad range of modern samples that span several open ocean profiles combined with water column and sediment profiles from the permanently anoxic basins of the Black Sea and Cariaco Basins. The open ocean shows no variation in depth profiles that encompass most of the major water masses in the Atlantic and Southern Oceans. The anoxic basins, however, reveal Tl isotope signatures closer to their inputs, which is likely due to basinal restriction. The authigenic fraction of organic-rich sediments from the Black Sea and Cariaco Basin capture the Tl isotope value of the overlying water column, which shows that Tl isotopes could be applied as a faithful deep time redox proxy. For the first time, we will present new data showing that Tl isotopes is tracking bottom water ocean oxygenation. We are applying this isotope system to ancient samples, testing the spatial and temporal variability of ocean oxygenation coinciding with major biogeochemical events.

  12. Electrical Resistance Alloys and Low-Expansion Alloys

    DEFF Research Database (Denmark)

    Kjer, Torben


    The article gives an overview of electrical resistance alloys and alloys with low thermal expansion. The electrical resistance alloys comprise resistance alloys, heating alloys and thermostat alloys. The low expansion alloys comprise alloys with very low expansion coefficients, alloys with very low...

  13. Thallium myocardial tomoscintigraphy: detection of ischemia during weaning from mechanical ventilation in patients with chronic obstructive pulmonary disease. Tomoscintigraphie myocardique au thallium: detection de l'ischemie provoquee par le sevrage de la ventilation assistee chez le bronchiteux chronique

    Energy Technology Data Exchange (ETDEWEB)

    Andre, L.; Valette, H.; Obama, S.; Archambaud, F.; Richard, C.; Teboul, J.L.; Hebert, J.L.; Auzepy, P.; Desgrez, A. (Hopital de Bicetre, 94 - Le Kremlin-Bicetre (FR))


    In order to evidence myocardial ischemia-leading to ventricular dysfunction-during weaning from mechanical ventilation in patients with chronic obstructive pulmonary disease, thallium myocardial tomography and gated blood pool studies were performed in 9 patients during mechanical ventilation and during weaning from mechanical ventilation. During the latter, results of gated blood pool studies showed a diffuse homogeneous left ventricular dysfunction. A fixed lower thallium uptake in the septum than in the lateral wall was found with the quantitative analysis of myocardial tomograms. Partial volume effect is likely the cause of this septal defect. The hypothesis of a diffuse ischemia cannot be excluded; but, without the absolute quantification of tomographic data, it cannot be proven.

  14. Studies of photon spectra from a thallium-204 foil source as an aid to dosimetry and shielding

    CERN Document Server

    Francis, T M


    Beta ray foil sources incorporating nuclides such as thallium-204, promethium-147 and strontium-90 plus yttrium-90 ar increasingly used in industrial devices such as thickness gauges. These sources are so constructed that they give rise to complex photon spectra containing low energy Bremsstrahlung and X-rays characteristic of the constructional materials. The energy response of practical monitoring instruments is such that they are likely to underestimate the dose due to such spectra unless they are calibrated using appropriate spectra. This report describes a series of measurements carried out on a commercially available thallium-204 foil source and five commonly used shielding materials. The measurements made with a NaI(T1) spectrometer have been corrected for instrumental distortions to obtain the photon spectra in air. These spectra are presented and have been used to compute dose in air with the help of published data on mass energy-absorption coefficients. Also included in the report are data derived f...

  15. Septal myocardial perfusion imaging with thallium-201 in the diagnosis of proximal left anterior descending coronary artery disease

    Energy Technology Data Exchange (ETDEWEB)

    Pichard, A.D.; Wiener, I.; Martinez, E.; Horowitz, S.; Patterson, R.; Meller, J.; Goldsmith, S.J.; Gorlin, R.; Herman, M.V.


    The use of myocardial perfusion imaging (MPI) to identify obstructive coronary disease of the left anterior descending coronary artery proximal to the first septal perforator (prox LAD) was studied in 60 patients. Perfusion of the septum and anteroapical areas with thallium-201 injected during exercise was compared to results of coronary arteriography. Septal MPI defect was found in 92.3% of patients with obstruction of the proximal LAD, 27.7% of patients with obstruction of LAD distal to first septal perforator, 0% in patients with obstructions involving right or circumflex arteries, and in 10.5% of patients without coronary disease. Anteroapical MPI defects were found with similar frequency in the three groups with obstructive coronary disease. Septal MPI defect had a sensitivity of 92.3% and specificity of 85.4% in the diagnosis of proximal LAD disease. Normal septal perfusion with thallium-201 virtually excluded proximal LAD disease.

  16. Usefulness of rest-redistribution thallium scan for the indication of PTCA in an interesting case with acute myocardial infarction

    Energy Technology Data Exchange (ETDEWEB)

    Chiba, Hiroshi; Nishimura, Tsunehiko; Mitani, Isao; Matsuo, Takeshi; Uehara, Toshiisa; Hayashida, Kohei; Sumiyoshi, Tetsuya; Haze, Kazuo


    A 72-year-old woman with acute myocardial infarction was received coronary thrombolytic therapy. After percutaneous transluminal coronary recanalization (PTCR), the stenosis of LAD became from 99 % to 90 %. Left ventriculogram showed dyskinesis of anterior wall in acute phase. After PTCR, she complained of postinfarctional angina. Thus, in order to evaluate the viability of anterior wall, serial thallium scintigraphy was performed at rest, which showed perfusion defect and redistribution of anterior wall. After percutaneous transluminal coronary angioplasty (PTCA), anterior wall motion became almost normal. The perfusion defect of anterior wall was also gradually disappeared. The serial thallium scintigraphy at rest is an useful method not only to evaluate the viability of myocardium in acute myocardial infarction, but also to follow the effect of PTCA.

  17. Orthodontic silver brazing alloys. (United States)

    Brockhurst, P J; Pham, H L


    Orthodontic silver brazing alloys suffer from the presence of cadmium, excessive flow temperatures, and crevice corrosion on stainless steel. Seven alloys were examined. Two alloys contained cadmium. The lowest flow temperature observed was 629 degrees C for a cadmium alloy and 651 degrees C for two cadmium free alloys. Three alloys had corrosion resistance superior to the other solders. Addition of low melting temperature elements gallium and indium reduced flow temperature in some cases but produced brittleness in the brazing alloy.

  18. Rearrangement of beta,gamma-unsaturated esters with thallium trinitrate: synthesis of indans bearing a beta-keto ester moiety

    Directory of Open Access Journals (Sweden)

    Silva Jr. Luiz F.


    Full Text Available The rearrangement of beta,gamma-unsaturated esters, such as 2-(3,4-dihydronaphthalen-1-yl-propionic acid ethyl ester, with thallium trinitrate (TTN in acetic acid leads to 3-indan-1-yl-2-methyl-3-oxo-propionic acid ethyl ester in good yield, through a ring contraction reaction. The new indans thus obtained feature a beta-keto ester moiety, which would be useful for further functionalization.

  19. Formic acid electrooxidation on thallium-decorated shape-controlled platinum nanoparticles: an improvement in electrocatalytic activity


    Busó-Rogero, Carlos; Perales-Rondón, Juan V.; Farias, Manuel J.S.; Vidal-Iglesias, Francisco J.; Solla-Gullón, José; Herrero, Enrique; Feliu, Juan M.


    Thallium modified shape-controlled Pt nanoparticles were prepared and their electrocatalytic activity towards formic acid electrooxidation was evaluated in 0.5 M sulfuric acid. The electrochemical and in situ FTIR spectroscopic results show a remarkable improvement in the electrocatalytic activity, especially in the low potential region (around 0.1–0.2 V vs. RHE). Cubic Pt nanoparticles modified with Tl were found to be more active than the octahedral Pt ones in the entire range of Tl coverag...

  20. Usefulness and limitations of thallium-201 myocardial scintigraphy in delineating location and size of prior myocardial infarction

    Energy Technology Data Exchange (ETDEWEB)

    Niess, G.S.; Logic, J.R.; Russell, R.O. Jr.; Rackley, C.E.; Rogers, W.J.


    Thirty-two patients were evaluated at a mean of 7 +- 2 months after infarction with a 12-lead ECG, resting /sup 201/Tl myocardial scintigram, biplane left ventriculogram, and coronary angiograms. From the left ventriculogram, asynergy was quantified as percent abnormally contracting segment (% ACS), the percent of end-diastolic circumference which was either akinetic or dyskinetic. Using a computerized planimetry system, we expressed /sup 201/Tl perfusion defects as a percentage of total potential thallium uptake. Of 21 patients with ECG evidence of prior transmural infarction, a /sup 201/Tl defect was present in 20, and angiographic asynergy was present in all 21. The site of prior infarction by ECG agreed with the /sup 201/T1 defect location in 24 of 32 patients and with site of angiographic asynergy in 23 of 32 patients. Scintigraphic defects were present in only four of 10 patients with ACS less than or equal to 6%, but scintigraphic defects were found in 20 of 22 patients with ACS > 6%. Thallium defect size correlated marginally with angiographic left ventricular ejection fraction but correlated closely with angiographic % ACS. Thallium defect size was similar among patients with one-, two-, or three-vessel coronary artery disease (greater than or equal to 70% stenosis), but thallium defect size was larger in patients with electrocardiographic evidence of transmural infarction or pulmonary capillary wedge pressure > 12 mm Hg. Thus, resting /sup 201/T1 myocardial scintigraphy is useful in localizing and quantifying the extent of prior myocardial infarction, but is insensitive to small infarcts (ACS < 6%).

  1. Determination of thallium at ultra-trace levels in water and biological samples using solid phase spectrophotometry. (United States)

    Amin, Alaa S; El-Sharjawy, Abdel-Azeem M; Kassem, Mohammed A


    A new simple, very sensitive, selective and accurate procedure for the determination of trace amounts of thallium(III) by solid-phase spectrophotometry (SPS) has been developed. The procedure is based on fixation of Tl(III) as quinalizarin ion associate on a styrene-divinylbenzene anion-exchange resin. The absorbance of resin sorbed Tl(III) ion associate is measured directly at 636 and 830 nm. Thallium(I) was determined by difference measurements after oxidation of Tl(I) to Tl(III) with bromine. Calibration is linear over the range 0.5-12.0 μg L(-1) of Tl(III) with relative standard deviation (RSD) of 1.40% (n=10). The detection and quantification limits are 150 and 495 ng L(-1) using 0.6 g of the exchanger. The molar absorptivity and Sandell sensitivity are also calculated and found to be 1.31×10(7) L mol(-1)cm(-1) and 0.00156 ng cm(-2), respectively. The proposed procedure has been successfully applied to determine thallium in water, urine and serum samples. Copyright © 2013 Elsevier B.V. All rights reserved.

  2. The efficient removal of thallium from sintering flue gas desulfurization wastewater in ferrous metallurgy using emulsion liquid membrane. (United States)

    Yang, Li; Xiao, Jiangping; Shen, Yi; Liu, Xian; Li, Wensong; Wang, Weiyan; Yang, Yunquan


    The removal of thallium ions in flue gas desulfurization wastewater from ferrous metallurgic industry was studied by emulsion liquid membrane (ELM) method using 2-ethylhexyl phosphoric acid-2-ethylhexyl ester (P507) as carrier, aviation kerosene (AK) as organic solvent, polyisobutylene succinimide (T154) as surfactant, polyisobutylene (PIB) as additive, and sulfuric acid as internal reagent. Some important influence parameters such as concentrations of carrier, surfactant and stripping agent, agitation speed, extraction time, volume ratios of feed solution to emulsion phase and internal phase to membrane phase, and their effects on the removal efficiency of Tl in the ELM process were investigated and optimized. Under the optimum operating conditions of 2% of carrier, 5% of surfactant, 0.5 M of stripping agent, 350 rpm of agitation speed, 12.5:1 of volume ratio of feed solution to emulsion phase, and 3:1 volume ratio of membrane to internal phase, the maximum extraction efficiency of thallium reached 99.76% within 15-min reaction time. The ICP-MS analysis indicated that the thallium concentration in treated wastewater was below 5 μg/L and could meet the emission standard demand for industrial wastewater enacted by the local government of Hunan province of China. Meanwhile, the extraction of impurity ions calcium and magnesium in the ELM system was investigated. The result showed that an acidic environment would be in favor of the removal of Tl from calcium and magnesium contained in wastewater. Graphical abstract ᅟ.

  3. Thallium isotopes in metallurgical wastes/contaminated soils: A novel tool to trace metal source and behavior. (United States)

    Vaněk, Aleš; Grösslová, Zuzana; Mihaljevič, Martin; Ettler, Vojtěch; Trubač, Jakub; Chrastný, Vladislav; Penížek, Vít; Teper, Leslaw; Cabala, Jerzy; Voegelin, Andreas; Zádorová, Tereza; Oborná, Vendula; Drábek, Ondřej; Holubík, Ondřej; Houška, Jakub; Pavlů, Lenka; Ash, Christopher


    Thallium (Tl) concentration and isotope data have been recorded for contaminated soils and a set of industrial wastes that were produced within different stages of Zn ore mining and metallurgical processing of Zn-rich materials. Despite large differences in Tl levels of the waste materials (1-500mgkg-1), generally small changes in ε205Tl values have been observed. However, isotopically lighter Tl was recorded in fly ash (ε205Tl∼-4.1) than in slag (ε205Tl∼-3.3), implying partial isotope fractionation during material processing. Thallium isotope compositions in the studied soils reflected the Tl contamination (ε205Tl∼-3.8), despite the fact that the major pollution period ended more than 30 years ago. Therefore, we assume that former industrial Tl inputs into soils, if significant, can potentially be traced using the isotope tracing method. We also suggest that the isotope redistributions occurred in some soil (subsurface) horizons, with Tl being isotopically heavier than the pollution source, due to specific sorption and/or precipitation processes, which complicates the discrimination of primary Tl. Thallium isotope analysis proved to be a promising tool to aid our understanding of Tl behavior within the smelting process, as well as its post-depositional dynamics in the environmental systems (soils). Copyright © 2017 Elsevier B.V. All rights reserved.

  4. Thallium-isotopic compositions of euxinic sediments as a proxy for global manganese-oxide burial (United States)

    Owens, Jeremy D.; Nielsen, Sune G.; Horner, Tristan J.; Ostrander, Chadlin M.; Peterson, Larry C.


    Thallium (Tl) isotopes are a new and potentially powerful paleoredox proxy that may track bottom water oxygen conditions based on the global burial flux of manganese oxides. Thallium has a residence time of ∼20 thousand years, which is longer than the ocean mixing time, and it has been inferred that modern oxic seawater is conservative with respect to both concentration and isotopes. Marine sources of Tl have nearly identical isotopic values. Therefore, the Tl sinks, adsorption onto manganese oxides and low temperature oceanic crust alteration (the dominant seawater output), are the primary controls of the seawater isotopic composition. For relatively short-term, ∼million years, redox events it is reasonable to assume that the dominant mechanism that alters the Tl isotopic composition of seawater is associated with manganese oxide burial because large variability in low temperature ocean crust alteration is controlled by long-term, multi-million years, average ocean crust production rates. This study presents new Tl isotope data for an open ocean transect in the South Atlantic, and depth transects for two euxinic basins (anoxic and free sulfide in the water column), the Cariaco Basin and Black Sea. The Tl isotopic signature of open ocean seawater in the South Atlantic was found to be homogeneous with ε205Tl = -6.0 ± 0.3 (±2 SD, n = 41) while oxic waters from Cariaco and the Black Sea are -5.6 and -2.2, respectively. Combined with existing data from the Pacific and Arctic Oceans, our Atlantic data establish the conservatism of Tl isotopes in the global ocean. In contrast, partially- and predominantly-restricted basins reveal Tl isotope differences that vary between open-ocean (-6) and continental material (-2) ε205Tl, scaling with the degree of restriction. Regardless of the differences between basins, Tl is quantitatively removed from their euxinic waters below the chemocline. The burial of Tl in euxinic sediments is estimated to be an order of magnitude

  5. Thallium isotopes as a potential tracer for the origin of cratonic eclogites (United States)

    Nielsen, Sune G.; Williams, Helen M.; Griffin, William L.; O'Reilly, Suzanne Y.; Pearson, Norman; Viljoen, Fanus


    Cratonic eclogites are inferred to originate either from subducted ocean crust or mantle melts accreted onto the roots of continents. These models have different implications for the growth of continents, but it is currently difficult to determine the origin of individual eclogite suites. Upper ocean crust altered at low temperatures and marine sediments both display high thallium (Tl) concentrations and strongly fractionated Tl isotope signatures relative to the ambient upper mantle. In this study we carry out the first examination of the suitability of Tl isotopes as a tracer for an ocean-crust origin of cratonic eclogites. We have analysed the Tl isotope composition of clinopyroxene and garnet in six eclogites from the Kaalvallei and Bellsbank kimberlite pipes in South Africa. Minerals were pre-cleaned with an HCl leaching technique and the leachates display variably light Tl isotope ratios. These most likely reflect low-temperature hydrothermal alteration occurring after eruption of the kimberlite that carried the eclogites to the surface. The leached mineral pairs all display identical Tl isotope ratios, strongly suggesting that the source of the analysed Tl is identical for each mineral pair. It is, however, not possible to exclude the possibility that the analysed Tl originates from kimberlitic material that was not removed by the cleaning procedure. Only one of the six samples exhibits a Tl isotope composition different from ambient mantle. Assuming that the Tl isotope signatures indeed represent the eclogite minerals and not any form of contamination, the Tl isotope composition in this sample is consistent with containing a minor component (low temperatures. Thallium isotopes may become one of the most sensitive indicators for the presence of low-T altered ocean crust because of the stark contrast in Tl concentration and isotopic composition between the mantle and altered ocean crust. In fact, no other chemical or isotopic tracer could have provided an

  6. Thallium-201 SPECT in the diagnosis of head and neck cancer. (United States)

    Valdés Olmos, R A; Balm, A J; Hilgers, F J; Koops, W; Loftus, B M; Tan, I B; Muller, S H; Hoefnagel, C A; Gregor, R T


    The accuracy of SPECT with 201Tl-chloride for the diagnosis of primary tumors, lymph node metastases and recurrences in head and neck cancer was evaluated for clinical applicability. SPECT images, obtained 60 min after administration of 150 MBq 201Tl-chloride, were compared with clinical, CT and/or MRI and histology results. In addition, whole-body images were obtained to detect distant metastases. In 79 patients studied for primary tumors (principally larynix, hypopharynx, oropharynx, nasopharynx and oral cavity), 201Tl SPECT correctly identified 69 of 73 (95% versus 88% for CT/MRI) histologically confirmed malignancies including 63 squamous-cell carcinomas. The method localized four occult naso- and oropharynx carcinomas not seen on CT/MRI and was correctly negative in two patients without tumor and in three of four patients with no confirmed primary tumor in the head and neck. With respect to regional spread, only patients who had cervical lymph node dissection were evaluated, and the findings were recorded per side of the neck. Thallium-201 SPECT correctly identified metastases in 31 of 36 neck dissections with proven lymph node involvement (86%), was correctly negative in nine and false-positive in one. Although the sensitivity of CT/MRI was clearly higher (97%), considerably more false-positive cases affected its accuracy (81% versus 87% for SPECT). In 30 patients investigated for recurrences, 201Tl SPECT correctly identified 27 of 29 microscopically confirmed tumor sites (93%) and was correctly negative in seven. Sensitivity of CT/MRI was lower (76%), and a greater number of false-positives (seven versus three for SPECT) further decreased its accuracy (64% versus 87% for SPECT). Distant metastases were detected in five patients. Thallium-201 SPECT appears to be an accurate method for the diagnosis of head and neck cancer. The method is particularly useful for detection of occult head and neck tumors and for assessing recurrences. It also may be of

  7. Thallium in spawn, juveniles, and adult common toads (Bufo bufo) living in the vicinity of a zinc-mining complex, Poland. (United States)

    Dmowski, Krzysztof; Rossa, Monika; Kowalska, Joanna; Krasnodębska-Ostręga, Beata


    A breeding population of the common toad Bufo bufo living in the vicinity of a Zn-Pb smelting works in Bukowno, Poland was studied for the presence of thallium. Tl concentration was measured in the bottom sediments of the spawning pond, in the laid eggs, in juveniles after metamorphosis, and in the selected tissues of the adult individuals. A very high concentration of Tl was detected in the spawn (13.97 ± 8.90 mg/kg d.w.). In 50% of the spawn samples, levels exceeded 20 mgTl/kg d.w. The issue of maternal transfer of thallium from females to oocytes is discussed. Due to a significant accumulation of thallium, spawn analysis can be used as a sensitive indicator of the presence of this element in the environment and may replace more invasive methods that involve the killing of adult animals. In those regions that are abundant in Zn-Pb ores, the spawn of amphibians may be a very important source of thallium contamination for predators. From among all tissues of the Bukowno adult toads, the livers have shown the highest accumulation of thallium (mean 3.98 mg/kg d.w. and maximum value--18.63). For as many as 96.5% of livers, concentrations exceeded 1.0 mgTl/kg d.w. which is treated as indicative of poisoning.

  8. In-situ pre-concentration through repeated sampling and pyrolysis for ultrasensitive determination of thallium in drinking water by electrothermal atomic absorption spectrometry. (United States)

    Liu, Liwei; Zheng, Huaili; Xu, Bincheng; Xiao, Lang; Chigan, Yong; Zhangluo, Yilan


    In this paper, a procedure for in-situ pre-concentration in graphite furnace by repeated sampling and pyrolysis is proposed for the determination of ultra-trace thallium in drinking water by graphite furnace atomic absorption spectrometry (GF-AAS). Without any other laborious enrichment processes that routinely result in analyte loss and contamination, thallium was directly concentrated in the graphite furnace automatically and subsequently subject to analysis. The effects of several key factors, such as the temperature for pyrolysis and atomization, the chemical modifier, and the repeated sampling times were investigated. Under the optimized conditions, a limit of detection of 0.01µgL -1 was obtained, which fulfilled thallium determination in drinking water by GB 5749-2006 regulated by China. Successful analysis of thallium in certified water samples and drinking water samples was demonstrated, with analytical results in good agreement with the certified values and those by inductively coupled plasma mass spectrometry (ICP-MS), respectively. Routine spike-recovery tests with randomly selected drinking water samples showed satisfactory results of 80-96%. The proposed method is simple and sensitive for screening of ultra-trace thallium in drinking water samples. Copyright © 2017. Published by Elsevier B.V.

  9. The ECG component of Thallium-201 exercise testing impacts on cardiac intervention rates

    Energy Technology Data Exchange (ETDEWEB)

    Deague, J.; Salehi, N.; Grigg, L.; Lichtenstein, M.; Better, N. [Royal Melbourne Hospital, Parkville, VIC (Australia). Departments of Nuclear Medicine and Cardiology


    Full text: Thallium exercise testing (Tlex) offers superior sensitivity and specificity to exercise electrocardiography (ECG), but the value of the ECG data in Tlex remains poorly studied. While a normal Tlex is associated with an excellent prognosis, patients with a positive Tlex have a higher cardiac event rate. We aimed to see if a negative ECG Component of the Tlex (ECGTl) was associated with an improved outcome compared with a positive ECGTl, in those patients with a reversible Tlex defect. We followed 100 consecutive patients retrospectively with a reversible defect on Tlex (50 with negative and 50 with positive ECGTI) for 12 months. The ECG was reviewed as positive (1mm ST depression 0.08 seconds after J point or >2mm if on digoxin or prior ECG changes), negative, equivocal or uninterpretable. We excluded patients with pharmacological testing, and those with equivocal or uninterpretable ECGs. End-points included angiography, cardiac interventions and cardiac event rate (CER) incorporating unstable angina, acute myocardial infarction, and cardiac death. In conclusion 24% of patients with reversible defects on Tlex who had a negative ECGTI still proceeded to PTCA or CABG. Those with a positive ECGTI had a higher incidence of angiography and cardiac revascularisation, but this difference was only evident in patients with mild to moderate reversibility

  10. Redox-controlled release dynamics of thallium in periodically flooded arable soil. (United States)

    Antić-Mladenović, Svetlana; Frohne, Tina; Kresović, Mirjana; Stärk, Hans-Joachim; Savić, Dubravka; Ličina, Vlado; Rinklebe, Jörg


    To our knowledge, this is the first work to mechanistically study the impact of the redox potential (E H ) and principal factors, such as pH, iron (Fe), manganese (Mn), dissolved organic carbon (DOC), dissolved inorganic carbon (DIC), chlorides (Cl - ) and sulfates (SO 4 2- ), on the release dynamics of thallium (Tl) in periodically flooded soil. We simulated flooding using an automated biogeochemical microcosm system that allows for systematical control of pre-defined redox windows. The E H value was increased mechanistically at intervals of approximately 100 mV from reducing (-211 mV) to oxidizing (475 mV) conditions. Soluble Tl levels (0.02-0.28 μg L -1 ) increased significantly with increases in E H (r = 0.80, p soils along with a determination of the Tl species and monitoring of the Tl content in plants to achieve more detailed insight into soluble Tl behavior. Copyright © 2017 Elsevier Ltd. All rights reserved.


    Directory of Open Access Journals (Sweden)

    Arif Gökhan BAŞARAN


    Full Text Available Determination of larval growth rate of and forensic analysis of the age of Calliphoridae larvae on a corpse are useful evidence in legal investigations for the estimation of exact death time and time duration after death; post mortem interval. However many factors, such as temperature, tissue type and contamination of drugs and toxins, effect larval development of blow fly larvae and consequently theestimation of post mortem interval. The present study examined the larval growth rate of a forensically important blow fly species, Lucilia sericata Meigen 1826 in different concentrations (0,12; 0,25; 0,50; 1 and 2 μg/g of toxic heavy metal Thallium under controlled laboratory conditions. Body length and weight, death ratio of larvae and pupa between experimental and control groups were compared. Results demonstrated that the development rate of larvae between uncontaminated and contaminated diets varies significantly. In short, they molted later, reached maximum length more slowly and sometimesproduced significantly smaller pupae in contaminated food source. These results emphasized that the importance of determining the contamination rate of toxins in tissue for the forensic entomologist,while using development rates from standard curves based on larvae fed non-contaminated mediums.

  12. Value of transient dilation of the left ventricular cavity on stress thallium scintigraphy

    Energy Technology Data Exchange (ETDEWEB)

    Sugihara, Hiroki; Shiga, Kouji; Umamoto, Ikuo (Kyoto Prefectural Univ. of Medicine (Japan)) (and others)


    This study was undertaken to evaluate the value of transient dilation of the left ventricular cavity on stress thallium scintigraphy in 80 patients with ischemic heart disease (IHD) and 50 with hypertrophic cardiomyopathy (HCM). Twenty persons without either coronary artery stenosis or heart disease were served as controls. Areas surrounded by maximum count points on the line of each 10deg on the short axis slice through the mid-cavity of the left ventricle were obtained at 10 minutes and at 3 hours after exercise. Transient dilation index (TDI) was obtained by dividing the area on early image by that on delayed image. TDI was significantly higher in patients with two or three vessel disease in the IHD group than the control group. High TDI was observed in 8% for one vessel disease, 40% for two vessel disease, and 80% for three vessel disease, contributing to the detection of multivessel IHD. In the HCM group of 80 patients, 24 (48%) had high TDI which was frequently associated with a history of chest pain and positive ECG findings at exercise. When these 24 HCM patients underwent exercise blood pool scintiscanning, left ventricular enddiastolic volume was similar before and at 10 minutes after exercise. These findings suggest that transient dilation of the left ventricular cavity after exercise may reflect subendocardial ischemia in both IHD and HCM. TDI would become a useful indicator for transient dilation of the left ventricular cavity. (N.K.).

  13. Clinicopathologic correlation study of thallium-201 myocardial scintigraphy in diagnosis of myocardial infarction

    Energy Technology Data Exchange (ETDEWEB)

    Chida, Kouji; Sugiura, Masaya; Ohkawa, Shin-ichiro


    In a series of 1,000 consecutive autopsy cases, we evaluated the clinical utility of thallium-201 (Tl-201) myocardial scintigraphy and electrocardiography (ECG) in 101 patients who had been studied while alive. Fifty-five cases had myocardial infarctions (MI) at autopsy. The Tl-201 scintigram and ECG in diagnosis of MI showed sensitivities of 68 % and 60 %, specificities of 87 % and 83 %, and diagnostic accuracies of 76 % and 70 %, respectively. The sensitivity of the Tl-201 scintigram was 70 % in anterior MI, 80 % in postero-inferior MI, 25 % in lateral and subendocardial infarction. The sensitivity was 88 % for large massive MI, but was low in scattered (50 %) or middle-sized MI (17 %). The diagnostic limit of the resolution of Tl-201 scintigrams was 4.5 cm in long diameter. All 8 cases with MI of less than 4 cm could not be diagnosed with the technique. There were 48 cases of large MI (more than 5 cm), but 8 cases could not be diagnosed by scintigraphy because of non-transmural or scattered MI. A comparison of the Tl-201 scintigram and ECG showed that 27 cases out of 60 cases were diagnosed by both methods, 14 only by the Tl-201 scintigram, 9 only by ECG and 10 by neither method.

  14. Evaluation of myocardial damage in Duchenne's muscular dystrophy with thallium-201 myocardial SPECT

    Energy Technology Data Exchange (ETDEWEB)

    Tamura, Takuhisa; Shibuya, Noritoshi (Kawatana National Hospital, Nagasaki (Japan)); Hashiba, Kunitake; Oku, Yasuhiko; Mori, Hideki; Yano, Katsusuke


    Myocardial damage and cardiopulmonary functions in patients with Duchenne's muscular dystrophy (DMD) were assessed using thallium-201 myocardial single-photon emission computed tomography (SPECT) and technetium-99m multigated radionuclide angiography. Twenty-five patients with DMD were divided into 4 groups according to percent of perfusion defect (%PD) calculated by the bull's-eye method and age. PD was detected in 24 (96.0%) of 25 patients with DMD, and it spread from the left ventricular lateral wall to the anterior wall and/or interventricular septum. PD was detected even in a 6-year-old DMD boy. Patients in Group I (%PD[>=]10% and age<15 years old) were shown to have a higher risk of left-sided heart failure without respiratory failure. Patients in Group II (%PD[>=]10 and age[>=]15) showed decreased pulmonary function and worsened arterial blood gas values as compared with Group IV (%PD<10 and age[>=]15). There was no significant difference in cardiac function among the 4 groups. It is postulated that myocardial damage in Group II patients is dependent primarily on a deficiency of dystrophin and on chronic respiratory failure, and that some of them are at risk of cardiopulmonary failure. It is concluded that myocardial SPECT is useful for the early diagnosis of myocardial damage and evaluation of cardiopulmonary function in DMD patients. (author).

  15. Role of relativity in high-pressure phase transitions of thallium. (United States)

    Kotmool, Komsilp; Chakraborty, Sudip; Bovornratanaraks, Thiti; Ahuja, Rajeev


    We demonstrate the relativistic effects in high-pressure phase transitions of heavy element thallium. The known first phase transition from h.c.p. to f.c.c. is initially investigated by various relativistic levels and exchange-correlation functionals as implemented in FPLO method, as well as scalar relativistic scheme within PAW formalism. The electronic structure calculations are interpreted from the perspective of energetic stability and electronic density of states. The full relativistic scheme (FR) within L(S)DA performs to be the scheme that resembles mostly with experimental results with a transition pressure of 3 GPa. The s-p hybridization and the valence-core overlapping of 6s and 5d states are the primary reasons behind the f.c.c. phase occurrence. A recent proposed phase, i.e., a body-centered tetragonal (b.c.t.) phase, is confirmed with a small distortion from the f.c.c. phase. We have also predicted a reversible b.c.t. → f.c.c. phase transition at 800 GPa. This finding has been suggested that almost all the III-A elements (Ga, In and Tl) exhibit the b.c.t. → f.c.c. phase transition at extremely high pressure.

  16. High thallium concentrations in soils from sites of historical Ag, Pb, and Zn mining in western Małopolska (S Poland

    Directory of Open Access Journals (Sweden)

    Woch M. W.


    Full Text Available The aim of this study was to assess thallium concentration in topsoil originating from sites of historical mining of Ag, Pb and Zn in western Małopolska (S Poland. Soil samples were collected from 63 sites, sieved, ground and digested in hot HClO4. Thallium concentration was measured with an atomic absorption spectrometer. Thallium concentrations averaged 20.84 mg kg-1 and varied from 4.42 to 49.82 mg kg-1. In all studied soils they exceeded values typical for uncontaminated soils (0.02 to 2.8 mg Tl kg-1. This indicates that Tl contamination may threaten the environment and public health. Routine monitoring of Tl contamination in southern Poland is required.

  17. Preconcentration of thallium(III) with 2,6-bis( N-phenyl carbamoyl) pyridine on microcrystalline naphthalene prior to its trace determination in human serum spectrophotometrically (United States)

    Rezaei, B.; Meghdadi, S.; Majidi, N.


    A novel, simple, sensitive and effective method has been developed for preconcentration of thallium on 2,6-bis( N-phenyl carbamoyl)pyridine-naphthalene adsorbent in the pH range 5.0-10.0, prior to its spectrophotometric determination, based on the oxidation of bromopyrogallol red at λ = 518 nm. This method makes it possible to quantitize thallium in the range of 3.0 × 10 -9 to 1.0 × 10 -5 M, with a detection limit (S/N = 3) of 1.2 × 10 -9 M. This procedure has been successfully applied to determine the ultra trace levels of thallium in the environmental and biological samples, free from the interference of some diverse ions. The precision, expressed as relative standard deviation of three measurements is better than 4.17%.

  18. Biphasic thallium 201 SPECT-imaging for the noninvasive diagnosis of myocardial perfusion abnormalities in a child with Kawasaki disease--a case report

    Energy Technology Data Exchange (ETDEWEB)

    Hausdorf, G.; Nienaber, C.A.; Spielman, R.P.


    The mucocutaneous lymph node syndrome (Kawasaki disease) is of increasing importance for the pediatric cardiologist, for coronary aneurysms with the potential of thrombosis and subsequent stenosis can develop in the course of the disease. The authors report a 2 1/2-year-old female child in whom, fourteen months after the acute phase of Kawasaki disease, myocardial infarction occurred. Biphasic thallium 201 SPECT-imaging using dipyridamole depicted anterior wall ischemia and inferolateral infarction. This case demonstrates that noninvasive vasodilation-redistribution thallium 201 SPECT-imaging has the potential to predict reversible myocardial perfusion defects and myocardial necrosis, even in small infants with Kawasaki disease.

  19. Influence of the Dirac-Hartree-Fock starting potential on the parity-nonconserving electric-dipole-transition amplitudes in cesium and thallium (United States)

    Perger, W. F.; Das, B. P.


    The parity-nonconserving electric-dipole-transition amplitudes for the 6s1/2-7s1/2 transition in cesium and the 6p1/2-7p1/2 transition in thallium have been calculated by the Dirac-Hartree-Fock method. The effects of using different Dirac-Hartree-Fock atomic core potentials are examined and the transition amplitudes for both the length and velocity gauges are given. It is found that the parity-nonconserving transition amplitudes exhibit a greater dependence on the starting potential for thallium than for cesium.

  20. Assessment of myocardial viability by dynamic tomographic iodine 123 iodophenylpentadecanoic acid imaging: comparison with rest-redistribution thallium 201 imaging. (United States)

    Iskandrian, A S; Powers, J; Cave, V; Wasserleben, V; Cassell, D; Heo, J


    This study examined the ability of dynamic 123I-labeled iodophenylpentadecanoic acid (IPPA) imaging to detect myocardial viability in patients with left ventricular (LV) dysfunction caused by coronary artery disease. Serial 180-degree single-photon emission computed tomographic (SPECT) images (five sets, 8 minutes each) were obtained starting 4 minutes after injection of 2 to 6 mCi 123I at rest in 21 patients with LV dysfunction (ejection fraction [EF] 34% +/- 11%). The segmental uptake was compared with that of rest-redistribution 201Tl images (20 segments/study). The number of perfusion defects (reversible and fixed) was similar by IPPA and thallium (11 +/- 5 vs 10 +/- 5 segments/patient; difference not significant). There was agreement between IPPA and thallium for presence or absence (kappa = 0.78 +/- 0.03) and nature (reversible, mild fixed, or severe fixed) of perfusion defects (kappa = 0.54 +/- 0.04). However, there were more reversible IPPA defects than reversible thallium defects (7 +/- 4 vs 3 +/- 4 segments/patient; p = 0.001). In 14 patients the EF (by gated pool imaging) improved after coronary revascularization from 33% +/- 11% to 39% +/- 12% (p = 0.002). The number of reversible IPPA defects was greater in the seven patients who had improvement in EF than in the patients without such improvement (10 +/- 4 vs 5 +/- 4 segments/patient; p = 0.075). 123I-labeled IPPA SPECT imaging is a promising new technique for assessment of viability. Reversible defects predict recovery of LV dysfunction after coronary revascularization.

  1. Self-propagating high-temperature synthesis (SHS) and microwave-assisted combustion synthesis (MACS) of the thallium superconducting phases (United States)

    Bayya, S. S.; Snyder, R. L.


    This paper explores the speed of reaction as a parameter to minimizing thallium loss. Self-propagating high-temperature synthesis (SHS) and microwave-assisted combustion synthesis (MACS) were developed for the synthesis of Tl-2212 and Tl-2223 superconductors using Cu metal powder as a fuel. A kitchen microwave oven was used to carry out MACS reactions. The samples were reacted for few seconds and led to the formation of the superconducting phases. Further explorations and modifications in the processing could lead to the formation of single phases by MACS.

  2. Tracking along-arc sediment inputs to the Aleutian arc using thallium isotopes (United States)

    Nielsen, Sune G.; Yogodzinski, Gene; Prytulak, Julie; Plank, Terry; Kay, Suzanne M.; Kay, Robert W.; Blusztajn, Jerzy; Owens, Jeremy D.; Auro, Maureen; Kading, Tristan


    Sediment transport from the subducted slab to the mantle wedge is an important process in understanding the chemical and physical conditions of arc magma generation. The Aleutian arc offers an excellent opportunity to study sediment transport processes because the subducted sediment flux varies systematically along strike (Kelemen et al., 2003) and many lavas exhibit unambiguous signatures of sediment addition to the sub-arc mantle (Morris et al., 1990). However, the exact sediment contribution to Aleutian lavas and how these sediments are transported from the slab to the surface are still debated. Thallium (Tl) isotope ratios have great potential to distinguish sediment fluxes in subduction zones because pelagic sediments and low-temperature altered oceanic crust are highly enriched in Tl and display heavy and light Tl isotope compositions, respectively, compared with the upper mantle and continental crust. Here, we investigate the Tl isotope composition of lavas covering almost the entire Aleutian arc a well as sediments outboard of both the eastern (DSDP Sites 178 and 183) and central (ODP Hole 886C) portions of the arc. Sediment Tl isotope compositions change systematically from lighter in the Eastern to heavier in the Central Aleutians reflecting a larger proportion of pelagic sediments when distal from the North American continent. Lavas in the Eastern and Central Aleutians mirror this systematic change to heavier Tl isotope compositions to the west, which shows that the subducted sediment composition is directly translated to the arc east of Kanaga Island. Moreover, quantitative mixing models of Tl and Pb, Sr and Nd isotopes reveal that bulk sediment transfer of ∼0.6-1.0% by weight in the Eastern Aleutians and ∼0.2-0.6% by weight in the Central Aleutians can account for all four isotope systems. Bulk mixing models, however, require that fractionation of trace element ratios like Ce/Pb, Cs/Tl, and Sr/Nd in the Central and Eastern Aleutians occurs after

  3. Controls on thallium uptake during hydrothermal alteration of the upper ocean crust (United States)

    Coggon, Rosalind M.; Rehkämper, Mark; Atteck, Charlotte; Teagle, Damon A. H.; Alt, Jeffrey C.; Cooper, Matthew J.


    Hydrothermal circulation is a fundamental component of global biogeochemical cycles. However, the magnitude of the high temperature axial hydrothermal fluid flux remains disputed, and the lower temperature ridge flank fluid flux is difficult to quantify. Thallium (Tl) isotopes behave differently in axial compared to ridge flank systems, with Tl near-quantitatively stripped from the intrusive crust by high temperature hydrothermal reactions, but added to the lavas during low temperature reaction with seawater. This contrasting behavior provides a unique approach to determine the fluid fluxes associated with axial and ridge flank environments. Unfortunately, our understanding of the Tl isotopic mass balance is hindered by poor knowledge of the mineralogical, physical and chemical controls on Tl-uptake by the ocean crust. Here we use analyses of basaltic volcanic upper crust from Integrated Ocean Drilling Program Hole U1301B on the Juan de Fuca Ridge flank, combined with published analyses of dredged seafloor basalts and upper crustal basalts from Holes 504B and 896A, to investigate the controls on Tl-uptake by mid-ocean ridge basalts and evaluate when in the evolution of the ridge flank hydrothermal system Tl-uptake occurs. Seafloor basalts indicate an association between basaltic uptake of Tl from cold seawater and uptake of Cs and Rb, which are known to partition into K-rich phases. Although there is no clear relationship between Tl and K contents of seafloor basalts, the data do not rule out the incorporation of at least some Tl into the same minerals as the alkali elements. In contrast, we find no relationship between the Tl content and either the abundance of secondary phyllosilicate minerals, or the K, Cs or Rb contents in upper crustal basalts. We conclude that the uptake of Tl and alkali elements during hydrothermal alteration of the upper crust involves different processes and/or mineral phases compared to those that govern seafloor weathering. Furthermore

  4. Chemistry and phase evolution during roasting of toxic thallium-bearing pyrite. (United States)

    Lopez-Arce, Paula; Garcia-Guinea, Javier; Garrido, Fernando


    In the frame of a research project on microscopic distribution and speciation of geogenic thallium (Tl) from contaminated mine soils, Tl-bearing pyrite ore samples from Riotinto mining district (Huelva, SW Spain) were experimentally fired to simulate a roasting process. Concentration and volatility behavior of Tl and other toxic heavy metals was determined by quantitative ICP-MS, whereas semi-quantitative mineral phase transitions were identified by in situ thermo X-Ray Diffraction (HT-XRD) and Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM-EDS) analyses after each firing temperature. Sample with initial highest amount of quartz (higher Si content), lowest quantity of pyrite and traces of jarosite (lower S content) developed hematite and concentrated Tl (from 10 up to 72 mg kg-1) after roasting at 900 °C in an oxidizing atmosphere. However, samples with lower or absent quartz content and higher pyrite amount mainly developed magnetite, accumulating Tl between 400 and 500 °C and releasing Tl from 700 up to 900 °C (from 10-29 mg kg-1 down to 4-1 mg kg-1). These results show the varied accumulative, or volatile, behaviors of one of the most toxic elements for life and environment, in which oxidation of Tl-bearing Fe sulfides produce Fe oxides wastes with or without Tl. The initial chemistry and mineralogy of pyrite ores should be taken into account in coal-fired power stations, cement or sulfuric acid production industry involving pyrite roasting processes, and steel, brick or paint industries, which use iron ore from roasted pyrite ash, where large amounts of Tl entail significant environmental pollution. Copyright © 2017 Elsevier Ltd. All rights reserved.

  5. Measurement of the parity nonconserving neutral weak interaction in atomic thallium

    Energy Technology Data Exchange (ETDEWEB)

    Bucksbaum, P.H.


    This thesis describes an experiment to measure parity nonconservation in atomic thallium. A frequency doubled, flashlamp pumped tunable dye laser is used to excite the 6P/sub 1/2/(F = 0) ..-->.. 7P/sub 1/2/(F = 1) transition at 292.7 nm, with circularly polarized light. An electrostatic field E of 100 to 300 V/cm causes this transition to occur via Stark induced electric dipole. Two field free transitions may also occur: a highly forbidden magnetic dipole M, and a parity nonconserving electric dipole epsilon/sub P/. The latter is presumed to be due to the presence of a weak neutral current interaction between the 6p valence electron and the nucleus, as predicted by gauge theories which unite the electromagnetic and weak interactions. Both M and epsilon/sub P/ interfere with the Stark amplitude ..beta..E to produce a polarization of the 7P/sub 1/2/ state. This is measured with a circularly polarized infrared laser beam probe, tuned to the 7P/sub 1/2/ ..-->.. 8S/sub 1/2/ transition. This selectively excites m/sub F/ = +1 or -1 components of the 7P/sub 1/2/ state, and the polarization is seen as an asymmetry in 8S ..-->.. 6P/sub 3/2/ fluorescence when the probe helicity is reversed. The polarization due to M is M/ = -2M/(BETAE). It is used to calibrate the analyzing efficiency. The polarization due to epsilon/sub P/ is P/ = 2i epsilon/sub P//(..beta..E), and can be distinguished from M/ by its properties under reversal of the 292.7 nm photon helicity and reversal of the laser direction. A preliminary measurement yielded a parity violation in agreement with the gauge theory of Weinberg and Salam.

  6. MRI and thallium-201 SPECT in the prediction of survival in glioma

    Energy Technology Data Exchange (ETDEWEB)

    Vos, Maaike J. [VU University Medical Center, Department of Neurology, Amsterdam (Netherlands); Medical Center Haaglanden, Department of Neurology, PO Box 432, The Hague (Netherlands); Berkhof, Johannes [VU University Medical Center, Department of Epidemiology and Biostatistics, Amsterdam (Netherlands); Hoekstra, Otto S. [VU University Medical Center, Department of Nuclear Medicine and PET Research, Amsterdam (Netherlands); Bosma, Ingeborg; Sizoo, Eefje M.; Heimans, Jan J.; Reijneveld, Jaap C.; Postma, Tjeerd J. [VU University Medical Center, Department of Neurology, Amsterdam (Netherlands); Sanchez, Esther [VU University Medical Center, Department of Radiology, Amsterdam (Netherlands); Lagerwaard, Frank J. [VU University Medical Center, Department of Radiation Oncology, Amsterdam (Netherlands); Buter, Jan [VU University Medical Center, Department of Medical Oncology, Amsterdam (Netherlands); Noske, David P. [VU University Medical Center, Department of Neurosurgery and Neuro-Oncology Research Group, Amsterdam (Netherlands)


    This paper aims to study the value of MRI and Thallium 201 ({sup 201}Tl) single-photon emission computed tomography (SPECT) in the prediction of overall survival (OS) in glioma patients treated with temozolomide (TMZ) and to evaluate timing of radiological follow-up. We included patients treated with TMZ chemoradiotherapy for newly diagnosed glioblastoma multiforme (GBM) and with TMZ for recurrent glioma. MRIs and {sup 201}Tl SPECTs were obtained at regular intervals. The value of both imaging modalities in predicting OS was examined using Cox regression analyses. Altogether, 138 MRIs and 113 {sup 201}Tl SPECTs in 46 patients were performed. Both imaging modalities were strongly related to OS (P {<=} 0.02). In newly diagnosed GBM patients, the last follow-up MRI (i.e., after six adjuvant TMZ courses) and SPECT (i.e., after three adjuvant TMZ courses) were the strongest predictors of OS (P = 0.01). In recurrent glioma patients, baseline measurements appeared to be the most predictive of OS (P < 0.01). The addition of one imaging modality to the other did not contribute to the prediction of OS. Both MRI and {sup 201}Tl SPECT are valuable in the prediction of OS. It is adequate to restrict to one of both modalities in the radiological follow-up during treatment. In the primary GBM setting, MRI after six adjuvant TMZ courses contributes significantly to the prediction of survival. In the recurrent glioma setting, baseline MRI appears to be a powerful predictor of survival, whereas follow-up MRIs during TMZ seem to be of little additional value. (orig.)

  7. Synthesis, calorimetric, structural and conductivity studies in a new thallium selenate tellurate adduct compound

    Energy Technology Data Exchange (ETDEWEB)

    Ktari, L. [Laboratoire de l' Etat Solide (LES), Faculte des Sciences de Sfax, 3000 Sfax (Tunisia); Abdelhedi, M. [Laboratoire de l' Etat Solide (LES), Faculte des Sciences de Sfax, 3000 Sfax (Tunisia); Laboratoire Leon Brouillon LLB, CEA Saclay, 91191 Gif-Sur-Yvette Cedex (France); Bouhlel, N. [Laboratoire de l' Etat Solide (LES), Faculte des Sciences de Sfax, 3000 Sfax (Tunisia); Dammak, M., E-mail: [Laboratoire de l' Etat Solide (LES), Faculte des Sciences de Sfax, 3000 Sfax (Tunisia); Cousson, A. [Laboratoire Leon Brouillon LLB, CEA Saclay, 91191 Gif-Sur-Yvette Cedex (France)


    The crystal structure of the thallium selenate tellurate Tl{sub 2}SeO{sub 4}.Te(OH){sub 6} (TlSeTe) was determined by X-ray diffraction method. The title compound crystallizes in the monoclinic system with P2{sub 1}/c space group. The following parameters are: a = 12.358(3) A; b = 7.231(1) A; c = 11.986(2) A; {beta} = 111.092(2){sup o}; Z = 4. The structure can be regarded as being built of isolated TeO{sub 6} octahedra and SeO{sub 4} tetrahedra. The Tl{sup +} cations are intercalated between these kinds of polyhedra. The main feature of this structure is the coexistence of two different and independent anions (SeO{sub 4}{sup 2-} and TeO{sub 6}{sup 6-}) in the same unit cell. The structure is stable due to O-H...O hydrogen bonds which link tetrahedral and octahedral groups. Crystals of Tl{sub 2}SeO{sub 4}.Te(OH){sub 6} undergo three endothermal transitions at 373, 395 and 437 K. These transitions are detected by DSC and analyzed by dielectric measurements with impedance spectroscopy. The evolution of conductivity versus temperature showed the presence of a protonic conduction phase transition at 437 K. The phase transition at 373 K can be related to a structural phase transition, whereas the one at 395 K is ascribed as likely due to a ferroelectric-paraelectric phase transition.

  8. Electrochemical properties of modified copper-thallium hexacyanoferrate electrode in the presence of different univalent cations

    Energy Technology Data Exchange (ETDEWEB)

    Rutkowska, Iwona A.; Stroka, Jadwiga [Department of Chemistry, University of Warsaw, Pasteura 1, PL-02-093 Warsaw (Poland); Galus, Zbigniew [Department of Chemistry, University of Warsaw, Pasteura 1, PL-02-093 Warsaw (Poland)], E-mail:


    The preparation of copper(II) hexacyanoferrate (CuHCF) films on the surface of gold electrodes as well as their characterization in solutions of various alkali metal and NH{sub 4}{sup +} cations and in the presence of thallium(I) are described. The electrochemical quartz crystal microbalance and cyclic voltammetric techniques were used. In 0.50 M lithium nitrate, even at submillimolar concentration of Tl(I), the formal potential of CuHCF was shifted to more positive values. At higher Tl(I) concentrations, the formal potential of the CuHCF redox reaction changed linearly with the logarithm of Tl(I) concentration (in the 0.50 M solution of lithium or another alkali metal nitrate). From such dependencies, selectivity coefficients K{sub Tl/M} were calculated, and they show that the CuHCF film on the gold electrode interacts preferentially with Tl(I). High affinity of Tl(I) to copper hexacyanoferrate, that was observed in the presence of alkali metal cations, was explained by relatively strong donor-acceptor interactions of Tl(I) ions with nitrogen in CN groups of the CuHCF film. It was also shown for simple M{sub 4}[Fe(CN){sub 6}] metal ferrocyanate salts (where M = Li{sup +}, Na{sup +}, K{sup +}, Rb{sup +}, Cs{sup +} and Tl{sup +}) that there is a preferential interaction of Tl{sup +} with CN group consistent with formation of a Tl-NC-Fe bridge.

  9. Quantitative evaluation of thallium-201 myocardial scintigram in coronary artery diseases

    Energy Technology Data Exchange (ETDEWEB)

    Mikada, Ken-etsu (Akita Univ. (Japan). School of Medicine)


    Quantitative indices from circumferential profile curves of thallium-201 ([sup 201]Tl) myocardial scintigram were evaluated for diagnostic utility in coronary artery diseases (CAD). Myocardial [sup 201]Tl scintigrams with single photon emission computed tomography (SPECT) were obtained 5 minutes (early) and 4 hours (delayed) after exercise in 20 normal subjects and 66 cases of CAD, of which 20 were angina pectoris without myocardial infarction (AP), 14 were subendocardial infarction (non-QMI) and 32 were Q-wave infarction (QMI). Tl counts, %Tl uptake and washout ratio (WR) were measured in 81 segments (9 apical segments of the slice from the longitudinal axis and all 72 segments of two slices from the short axis). A mean early defect (MED), a mean delayed defect (MDD), a mean delta washout rate (MDR), and a [Sigma] delayed defect ([Sigma]DD) were calculated from the areas which were below the two standard deviations of the mean %Tl uptake in normal subjects. A mean filling-in (MFI) was calculated from the difference of the %Tl uptake between early and delayed curves in each patient. In patients with CAD, the MED and MFI were higher, but MDW was lower with a more severe coronary stenosis, indicating that these indices were useful to detect myocardial hypo-perfuion. In severely stenotic regions, the MDD was higher in QMI than in AP and non-QMI, indicating that the ratio of infarct to the myocardium in the region was higher in QMI. In QMI, [Sigma]DD correlated well (r=0.723) with Total Wall Motion Scores with two-dimentional echocardiography which was directly related with infarct size. Further, MED, MFI and MDW were improved after aortocoronary bypass only in patients with patent graft. It is concluded that this quantitative evaluation with [sup 201]Tl-SPECT can provide an objective and quantitative estimate of regional myocardial ischemia and infarct. (author).

  10. Thallium-201 for cardiac stress tests: residual radioactivity worries patients and security. (United States)

    Geraci, Matthew J; Brown, Norman; Murray, David


    A 47-year-old man presented to the Emergency Department (ED) in duress and stated he was "highly radioactive." There were no reports of nuclear disasters, spills, or mishaps in the local area. This report discusses the potential for thallium-201 (Tl-201) patients to activate passive radiation alarms days to weeks after nuclear stress tests, even while shielded inside industrial vehicles away from sensors. Characteristics of Tl-201, as used for medical imaging, are described. This patient was twice detained by Homeland Security Agents and searched after he activated radiation detectors at a seaport security checkpoint. Security agents deemed him not to be a threat, but they expressed concern regarding his health and level of personal radioactivity. The patient was subsequently barred from his job and sent to the hospital. Tl-201 is a widely used radioisotope for medical imaging. The radioactive half-life of Tl-201 is 73.1h, however, reported periods of extended personal radiation have been seen as far out as 61 days post-administration. This case describes an anxious, but otherwise asymptomatic patient presenting to the ED with detection of low-level personal radiation. Documentation should be provided to and carried by individuals receiving radionuclides for a minimum of five to six half-lives of the longest-lasting isotope provided. Patients receiving Tl-201 should understand the potential for security issues; reducing probable tense moments, confusion, and anxiety to themselves, their employers, security officials, and ED staff. Copyright © 2012 Elsevier Inc. All rights reserved.

  11. Usefulness of thallium-201 SPECT in the evaluation of tumor natures in intracranial meningiomas

    Energy Technology Data Exchange (ETDEWEB)

    Takeda, Tetsuji; Nakano, Takahiro; Asano, Kenichiroh; Shimamura, Norihito; Ohkuma, Hiroki [Hirosaki University Graduate School of Medicine, Department of Neurosurgery, Hirosaki (Japan)


    Although intracranial meningiomas are regarded as benign tumors, some of them behave clinically as malignant tumors. Past reports suggest that MIB 1 and vascular endothelial growth factor (VEGF) in postoperative tumor specimens correlate with the aggressive nature of tumors, but preoperative prediction of such a nature is more useful for therapeutic planning for the tumor. The purpose of this study was to assess the usefulness of preoperative thallium-201 chloride single-photon emission computed tomography (Tl SPECT) to evaluate biological behavior in intracranial meningiomas. Tl SPECT was performed on 39 patients with intracranial meningioma and Tl uptake indices were calculated. The difference in the Tl uptake index between atypical meningiomas and other pathological types of meningioma was evaluated. Moreover, correlation of Tl uptake indices with the MIB1 labeling index was estimated. Tl uptake indices were also compared between VEGF strongly positive and weakly positive meningiomas. The delayed index of atypical meningioma was significantly higher than that of the other pathological types (p = 0.036). Significant correlation was found between the Tl uptake index in the delayed image and MIB1 labeling index (p < 0.0001, R{sup 2} = 0.36). Moreover, VEGF strongly positive meningiomas exhibited a significantly higher Tl uptake index compared to VEGF weakly positive meningiomas in both the early image and the delayed image (p = 0.029, 0.023, respectively). Tl uptake index may be a possible preoperative surrogate marker of MIB1 and VEGF that is useful in detecting aggressive natures in intracranial meningiomas. (orig.)

  12. Effective removal of trace thallium from surface water by nanosized manganese dioxide enhanced quartz sand filtration. (United States)

    Huangfu, Xiaoliu; Ma, Chengxue; Ma, Jun; He, Qiang; Yang, Chun; Zhou, Jian; Jiang, Jin; Wang, Yaan


    Thallium (Tl) has drawn wide concern due to its high toxicity even at extremely low concentrations, as well as its tendency for significant accumulation in the human body and other organisms. The need to develop effective strategies for trace Tl removal from drinking water is urgent. In this study, the removal of trace Tl (0.5 μg L -1 ) by conventional quartz sand filtration enhanced by nanosized manganese dioxide (nMnO 2 ) has been investigated using typical surface water obtained from northeast China. The results indicate that nMnO 2 enhanced quartz sand filtration could remove trace Tl(I) and Tl(III) efficiently through the adsorption of Tl onto nMnO 2 added to a water matrix and onto nMnO 2 attached on quartz sand surfaces. Tl(III)-HA complexes might be responsible for higher residual Tl(III) in the effluent compared to residual Tl(I). Competitive Ca 2+ cations inhibit Tl removal to a certain extent because the Ca 2+ ions will occupy the Tl adsorption site on nMnO 2 . Moreover, high concentrations of HA (10 mgTOC L -1 ), which notably complexes with and dissolves nMnO 2 (more than 78%), resulted in higher residual Tl(I) and Tl(III). Tl(III)-HA complexes might also enhance Tl(III) penetration to a certain extent. Additionally, a higher pH level could enhance the removal of trace Tl from surface water. Finally, a slight increase of residual Tl was observed after backwash, followed by the reduction of the Tl concentration in the effluent to a "steady" state again. The knowledge obtained here may provide a potential strategy for drinking water treatment plants threatened by trace Tl. Copyright © 2017. Published by Elsevier Ltd.

  13. Reduced left ventricular cavitary activity ("black hole sign") in thallium-201 SPECT perfusion images of anteroapical transmural myocardial infarction. (United States)

    Civelek, A C; Shafique, I; Brinker, J A; Durski, K; Weiss, J L; Links, J M; Natarajan, T K; Ozguven, M A; Wagner, H N


    Apparently reduced left ventricular (LV) cavitary thallium activity in both planar and tomographic perfusion images has been previously observed by these and other investigators. With single-photon emission computerized tomography, we have clinically noted that this "black hole sign" was associated with an aneurysm in the setting of a transmural anterior or anteroapical perfusion defect. We have now prospectively studied the etiology and predictive value of this sign in 84 consecutive patients with an anterior, anteroapical transmural perfusion defect. Of the 84 patients, 49 had both LV aneurysm (confirmed by contrast ventriculography, echocardiography or gated blood pool studies) and a black hole sign. Only 1 patient with an aneurysm did not have the black hole sign, and 2 without aneurysm did. Thus, it is concluded that this sign is highly accurate in diagnosing LV aneurysm. Because thallium-201 single-photon emission computerized tomography imaging is often performed as one of the first diagnostic tests soon after myocardial infarction, this has important clinical management implications.

  14. The analysis of thallium in geological materials by radiochemical neutron activation and x-ray fluorescence spectrometry: a comparison

    Energy Technology Data Exchange (ETDEWEB)

    McGoldrick, P.J.; Robinson, P. [Tasmania Univ., Sandy Bay, TAS (Australia)


    Carrier-based radiochemical neutron activation (RNAA) is a precise and accurate technique for the analysis of Tl in geological materials. For about a decade, until the mid-80s, a procedure modified from Keays et al. (1974) was used at the University of Melbourne to analyse for Tl in a wide variety of geological materials. Samples of powdered rock weighing several hundred milligrams each were irradiated in HIFAR for between 12 hours and 1 week, and subsequently fused with a sodium hydroxide - sodium peroxide mixture and several milligrams of inactive Tl carrier. Following acid digestion of the fusion mixture anion exchange resin was used to separate Tl from the major radioactive rock constituents. The Tl was then stripped from the resin and purified as thallium iodide and a yield measured gravimetrically. Activity from {sup 204}Tl (a {beta}-emitter with a 3 8 year half-life) was measured and Tl determined by reference to pure chemical standards irradiated and processed along with the unkowns. Detection limits for the longer irradiations were about one part per billion. Precision was monitored by repeat analyses of `internal standard` rocks and was estimated to be about five to ten percent (one standard deviation). On the other hand, X-ray fluorescence spectrometry (XRF) was seen as an excellent cost-effective alternative for thallium analysis in geological samples, down to 1 ppm. 6 refs. 1 tab., 1 fig.

  15. Pentoxifylline (Trental) does not inhibit dipyridamole-induced coronary hyperemia: Implications for dipyridamole-thallium-201 myocardial imaging

    Energy Technology Data Exchange (ETDEWEB)

    Brown, K.A.; Slinker, B.K. (Univ. of Vermont College of Medicine, Burlington (USA))


    Dipyridamole-thallium-201 imaging is often performed in patients unable to exercise because of peripheral vascular disease. Many of these patients are taking pentoxifylline (Trental), a methylxanthine derivative which may improve intermittent claudication. Whether pentoxifylline inhibits dipyridamole-induced coronary hyperemia like other methylxanthines such as theophylline and should be stopped prior to dipyridamole-thallium-201 imaging is unknown. Therefore, we studied the hyperemic response to dipyridamole in seven open-chest anesthetized dogs after pretreatment with either pentoxifylline (0, 7.5, or 15 mg/kg i.v.) or theophylline (3 mg/kg i.v.). Baseline circumflex coronary blood flows did not differ significantly among treatment groups. Dipyridamole significantly increased coronary blood flow before and after 7.5 or 15 mm/kg i.v. pentoxifylline (p less than 0.002). Neither dose of pentoxifylline significantly decreased the dipyridamole-induced hyperemia, while peak coronary blood flow was significantly lower after theophylline (p less than 0.01). We conclude that pentoxyifylline does not inhibit dipyridamole-induced coronary hyperemia even at high doses.

  16. Thallium-201 scintigraphy after dipyridamole infusion with low-level exercise. III Clinical significance and additional diagnostic value of ST segment depression and angina pectoris during the test

    NARCIS (Netherlands)

    G-J. Laarman (GertJan); P.W.J.C. Serruys (Patrick); J.F. Verzijlbergen (Fred); C.A.P.L. Ascoop (Carl); J. Azar


    textabstractIntravenous dipyridamole thallium testing is a useful alternative procedure for assessing coronary artery disease (CAD) in patients who are unable to perform maximal exercise tests. Ischaemic ST segment depression and angina pectoris are frequently observed during the test, in particular

  17. Indium-111 antimyosin antibody imaging and thallium-201 imaging. A comparative myocardial scintigraphic study using single-photon emission computed tomography in patients with myocarditis and dilated cardiomyopathy

    Energy Technology Data Exchange (ETDEWEB)

    Yamada, Takehiko; Matsumori, Akira; Nohara, Ryuji; Konishi, Junji; Sasayama, Shigetake [Kyoto Univ. (Japan). Faculty of Medicine; Tamaki, Nagara


    Indium-111 antimyosin antibody imaging (a tracer of myocardial necrosis) and thallium-201 imaging (a tracer of myocardial perfusion) were compared in patients with myocarditis and dilated cardiomyopathy. The distribution of each tracer and antimyosin/thallium-201 overlapping were evaluated with single-photon emission computed tomography (SPECT). Scintigraphic data were classified into 5 patterns according to the distribution of both images and were compared with histologic findings of endomyocardial biopsy: AM-D, intense and diffuse antimyosin uptake and no perfusion abnormality (active myocarditis); AM-L, localized antimyosin uptake and no perfusion abnormality (active myocarditis); HM, no antimyosin uptake with or without perfusion abnormality (healed myocarditis); DCM-NH, diffuse antimyosin uptake and inhomogeneous thallium-201 uptake (dilated cardiomyopathy); DCM-PD, diffuse or localized antimyosin uptake and myocardial perfusion defect(s) (dilated cardiomyopathy). Patients with dilated-phase hypertrophic cardiomyopathy were frequently found in the DCM-PD group. Taken together, comparative antimyosin/thallium-201 SPECT images are useful for evaluating the activity of myocarditis and ongoing myocardial damage even in areas with no perfusion in patients with dilated cardiomyopathy. (author)

  18. Thallium-201 myocardial scintigraphy in patients with normal coronary arteries and normal left ventriculogram. Comparison with hemodynamic, metabolic and morphologic findings

    Energy Technology Data Exchange (ETDEWEB)

    Loesse, B.; Kuhn, H.; Rafflenbeul, D.; Kroenert, H.; Hort, W.; Feinendegen, L.E.; Loogen, F.


    36 consecutive patients with chest pain and/or severe ventricular dysrhythmias, but normal coronary arteries and normal left ventriculogram, underwent thallium-201 myocardial imaging at rest and during exercise. The myocardial scintigram was abnormal in 27 patients (group A) and normal in only 9 patients (group B).

  19. Preconcentration of thallium (I) by single drop microextraction with electrothermal atomic absorption spectroscopy detection using dicyclohexano-18-crown-6 as extractant system. (United States)

    Chamsaz, Mahmoud; Arbab-Zavar, Mohammad Hossien; Darroudi, Abolfazl; Salehi, Thiery


    A simple single drop liquid-phase microextraction (SDME) technique, combined with electrothermal atomic absorption spectroscopy (ETAAS) is developed both to preconcentrate and determine thallium (I) ions in aqueous solutions. The ions were transferred from 10.0 ml of aqueous sample (donor phase) containing 0.5 ml of 1% picric acid as the ion-pair agent into a 3 microl microdrop of nitrobenzene (acceptor phase) containing dicyclohexano-18-crown-6 as the complexing agent. The latter will help to improve the extraction efficiency of the analyte. After the ions have been extracted, the acceptor drop was directly injected into a graphite furnace for thallium (I) determination. Several parameters such as the extracting solvent, extraction time, temperature, concentration of picric acid and crown ether, drop volume and stirring rate were examined. Under the optimized experimental conditions, the detection limit (L.O.D.) was 0.7 ng ml(-1). The relative standard deviation for five replicate analysis of 10 ng ml(-1) of thallium (I) was 5.1%. The calibration curve was linear in the range of 3-22 ng ml(-1). The results for determination of thallium in reference material, spiked tap water and seawater demonstrated the accuracy, recovery and applicability of the presented method. The enrichment factor was 50.

  20. Synthesis and application of a novel nanostructured ion-imprinted polymer for the preconcentration and determination of thallium(I) ions in water samples

    Energy Technology Data Exchange (ETDEWEB)

    Fayazi, M., E-mail: [Young Researchers and Elite Club, Kerman Branch, Islamic Azad University, Kerman (Iran, Islamic Republic of); Ghanei-Motlagh, M. [Young Researchers and Elite Club, Kerman Branch, Islamic Azad University, Kerman (Iran, Islamic Republic of); Taher, M.A. [Department of Chemistry, Faculty of Sciences, Shahid Bahonar University of Kerman, Kerman (Iran, Islamic Republic of); Ghanei-Motlagh, R. [Department of Pathobiology, Faculty of Veterinary Medicine, Ferdowsi University of Mashhad, Mashhad (Iran, Islamic Republic of); Salavati, M.R. [Department of Chemistry, Faculty of Science, Ferdowsi University of Mashhad, Mashhad (Iran, Islamic Republic of)


    Highlights: • A novel nanostructured thallium(I)-imprinted polymer was evaluated for trace detection of Tl(I). • The prepared sorbent displayed rapid extraction rate, high sensitivity and good reproducibility. • The proposed methodology was applied for quantification of Tl(I) in different water samples. - Abstract: A novel synthesized nanostructured ion-imprinted polymer (IIP) was investigated for the determination of trace amount of thallium(I). For this purpose, the thallium(I) IIP particles were synthesized using methacrylic acid (MAA) as the functional monomer, ethylene glycol dimethacrylate (EGDMA) as the cross-linker, methyl-2-[2-(2-2-[2-(methoxycarbonyl) phenoxy] ethoxyethoxy) ethoxy] benzoate as the chelating agent and 2,2-azobisisobutyronitrile (AIBN) as the initiator. The prepared IIP particles were characterized by field emission scanning electron microscopy (FE-SEM), Fourier transform infrared spectroscopy (FT-IR) and thermo gravimetric analysis (TGA). Various experimental factors such as pH, the amount of IIP particles, sorption and desorption time, sample volume, elution condition, and potentially interfering ions systematically examined. Under the optimum conditions, a sensitive response to Tl(I) within a wide concentration range (0.05–18 μg L{sup −1}) was achieved. The limit of detection (LOD, 3S{sub b}/m) was 6.3 ng L{sup −1}. The maximum adsorption capacity of the novel imprinted adsorbent for Tl(I) was calculated to be 18.3 mg g{sup −1}. The relative standard deviation (RSD) for eight replicate detections of 0.1 μg L{sup −1} of thallium(I) was found to be 4.0%. An enrichment factor (EF) of 100 was obtained by this method. The proposed technique was successfully applied to monitoring thallium in different water samples and the certified reference material.

  1. L-Tyrosine immobilized on multiwalled carbon nanotubes: A new substrate for thallium separation and speciation using stabilized temperature platform furnace-electrothermal atomic absorption spectrometry

    Energy Technology Data Exchange (ETDEWEB)

    Pacheco, Pablo H.; Gil, Raul A. [Departamento de Quimica Analitica, Facultad de Quimica, Bioquimica y Farmacia, Universidad Nacional de San Luis, Chacabuco y Pedernera, P.O. Box 375, 5700 San Luis (Argentina); Instituto de Quimica de San Luis (INQUISAL-CONICET), Chacabuco y Pedernera, CP 5700, San Luis (Argentina); Smichowski, Patricia, E-mail: [Consejo Nacional de Investigaciones Cientificas y Tecnicas (CONICET), Rivadavia 1917, CP C1033 AAJ, Ciudad de Buenos Aires (Argentina); Comision Nacional de Energia Atomica, Gerencia Quimica, Av. Gral. Paz 1499, B1650KNA San Martin (Argentina); Polla, Griselda [Comision Nacional de Energia Atomica, Gerencia de Investigacion y Aplicaciones, Av.Gral. Paz 1499, B1650KNA San Martin (Argentina); Martinez, Luis D., E-mail: [Departamento de Quimica Analitica, Facultad de Quimica, Bioquimica y Farmacia, Universidad Nacional de San Luis, Chacabuco y Pedernera, P.O. Box 375, 5700 San Luis (Argentina); Instituto de Quimica de San Luis (INQUISAL-CONICET), Chacabuco y Pedernera, CP 5700, San Luis (Argentina)


    An approach for the separation and determination of inorganic thallium species is described. A new sorbent, L-tyrosine-carbon nanotubes (L-tyr-CNTs), was used and applied to the analysis of tap water samples. At pH 5.0, L-tyr was selective only towards Tl(III), while total thallium was determined directly by stabilized temperature platform furnace-electrothermal atomic absorption spectrometry (STPF-ETAAS). The Tl(III) specie, which was retained by L-tyrosine, was quantitatively eluted from the column with 10% of nitric acid. An on-line breakthrough curve was used to determine the column capacity, which resulted to be 9.00 {mu}mol of Tl(III) g{sup -1} of L-tyr-CNTs with a molar ratio of 0.14 (moles of Tl bound to moles of L-tyr at pH 5). Transient peak areas revealed that Tl stripping from the column occurred instantaneously. Effects of sample flow rate, concentration and flow rate of the eluent, and interfering ions on the recovery of the analyte were systematically investigated. The detection limit for the determination of total thallium (3{sigma}) by STPF-ETAAS was 150 ng L{sup -1}. The detection limit (3{sigma}) for Tl(III) employing the separation system was 3 ng L{sup -1}, with an enrichment factor of 40. The precision of the method expressed as the relative standard deviation (RSD) resulted to be 3.4%. The proposed method was applied to the speciation and determination of inorganic thallium in tap water samples. The found concentrations were in the range of 0.88-0.91 {mu}g L{sup -1} of Tl(III), and 3.69-3.91 {mu}g L{sup -1} of total thallium.

  2. Tracing subducted sediment inputs to the Ryukyu arc-Okinawa Trough system: Evidence from thallium isotopes (United States)

    Shu, Yunchao; Nielsen, Sune G.; Zeng, Zhigang; Shinjo, Ryuichi; Blusztajn, Jerzy; Wang, Xiaoyuan; Chen, Shuai


    Sediments are actively subducted in virtually every arc worldwide. However, quantifying their contributions to arc lavas and thereby establishing budgets of how sediments participate in slab-mantle interaction is challenging. In this contribution we use thallium (Tl) abundances and isotopic compositions of lavas from the Ryukyu arc (including south Kyushu) and its back-arc basin, Okinawa Trough, to investigate the influence of sediments from arc to back-arc. We also present extensive geochemical data for sediments and altered oceanic crust (AOC) outboard of the northern (DSDP Sites 296, 442B, 443 and 444) and central (DSDP Sites 294 and 295) part of the Ryukyu arc. The Tl isotopic compositions of sediments change systematically from lighter outboard of northern Ryukyu arc to heavier outboard of central Ryukyu arc. The feature reflects the dominance of terrigenous material and pelagic sedimentation outboard of the northern and central Ryukyu arc, respectively. Central and northern sections of Ryukyu arc and Okinawa Trough display larger range of Tl isotopic variation than southern section, which is consistent with more pelagic provenance for sediments outboard of central and northern Ryukyu arcs than that of expected sediments outboard of southern Ryukyu arc. Identical Tl, Sr, Nd and Pb isotope variations are found when comparing arc and back arc lavas, which indicates that sediments fluxes also account for the Tl isotopic variations in the Okinawa Trough lavas. Two-end-member mixing models of Tl with Pb, Sr and Nd isotopes require sediment inputs ofsediment end members predict very similar sediment fluxes when using Tl, Sr, Nd and Pb isotopes, which indicates that fractionation of these elements must have happened after mixing between mantle and sediments. This conclusion is corroborated by model calculations of mixing between sediment melts with fractionated Sr/Nd ratios and mantle wedge, which show that no arc lava plot on such mixing lines. Thus bulk sediment

  3. Comparison of arbutamine stress and treadmill exercise thallium-201 SPECT: Hemodynamics, safety profile and diagnostic accuracy

    Energy Technology Data Exchange (ETDEWEB)

    Kiat, H.; Berman, D.S. [Cedars-Sinai Medical Centre, Los Angeles, California, LA (United States)


    Full text: Arbutamine (ARB), a new pharmacologic stress agent with enhanced chronotropic property compared to dobutamine, was compared with treadmill (TM) exercise testing (Ex) in a multicenter study using thallium-201 (Tl) SPECT. Of the total of 184 patients who underwent ARB, 69 also had TM stress and quantitative coronary angiography. Fifty-eight patients with a low pretest likelihood of CAD also underwent ARB study for evaluation of test specificity (normalcy rate). Tl scans were scored by a central laboratory using a 20 segment (seg)/scan visual analysis (5 point system: 0=normal, 4-absent uptake). Maximum heart rate (HR) by ARB and Ex was 122 vs 141 bpm (p<0.05). Mean %HR change from baseline was similar (79% vs 82%, respectively, p=ns). Maximum systolic BP for ARB and Ex was 173 vs 175 mmHg, and mean % change from baseline was 24% vs 28% (p=ns). Sensitivity for detecting CAD (270% stenosis) by ARB Tl was 94% and 97% by Ex Tl (p=ns). Stress Tl SPECT segmental agreement for presence of defect between ARB and Ex was 92% (kappa=0.8, p<0.001). Exact segmental stress Tl score (0-4 grading) agreement was 83 % (kappa=0.7, p<0.001). Among 346 segs with stress defects by both ARB and Ex defect reversibility agreement was 86% (kappa=0.7, p<0.001). The normalcy rate for ARB TI-SPECT among patients with a low likelihood of CAD was 90%. Adverse events were mostly mild (tremor: 23%, flushing: 10%, headache: 10%, paraesthesia: 8%, dizziness: 8%, hot flushes: 4%). Arrhythimia of clinical concern occurred in 8% (10/122) of ARB patients who had cardiac catheterisation and in 1.4% (1/69) of patients who had stress Tl. Of all 184 patients with ARB stress, ARB was discontinued due to arrhythmia in 7(5%) and 1 patient had IV Metoprolol for frequent ventricular couplets. Sustained arrhythmias were not observed

  4. Thallium Isotopes Tracking Mn-Oxide Burial - A Proxy for Deoxygenation During Oceanic Anoxic Event 2 (United States)

    Ostrander, C.; Owens, J. D.; Nielsen, S.


    Thallium (Tl) is proving to be a useful paleoredox proxy given that the Tl isotope composition of seawater is highly dependent on the magnitude of manganese (Mn) oxide burial in the ocean. In turn, Mn oxides require oxygen at the sediment-water interface to precipitate, linking the Tl isotope cycle to ocean oxygenation. Currently, the marine residence time of Tl is ~20kyrs and the Tl isotope composition of seawater is invariant, which suggests Tl isotopes could be a global tracer of marine Mn-oxide burial. Importantly, recent research suggests sediments deposited under a euxinic water column faithfully record the Tl isotope value of the overlying oxic water column (e.g. Black Sea and Cariaco Basin). Therefore, analysis of organic-rich black shales may prove useful in evaluating the seawater Tl isotope composition of past oceans and, hence, large-scale burial of Mn-oxides and the extent of bottom water ocean oxygenation. A logical test for this proxy is during the well-studied Cenomanian-Turonian boundary event termed Oceanic Anoxic Event 2 (OAE-2) at ~94 Ma. It is known that the global extent of anoxia and euxinia increased during this event, however, to what extent global bottom water deoxygenation occured is unconstrained. If deep water deoxygenation occurred, it would be hypothesized that Mn-oxide precipitation would decrease, resulting in a positive Tl isotope excursion during OAE-2. We have analyzed the Tl isotope composition of organic-rich black shales from Site 1258 of the Ocean Drilling Program (ODP) spanning the period before, during, and after OAE-2. Based on Fe redox proxies, the entire section is euxinic and thus no Mn-oxides are present (i.e. no local redox changes). Before the event, Tl isotope compositions are similar or slightly heavier than modern seawater values. Just prior to the onset of OAE-2, a positive shift occurs and is maintained until recovery, slightly before the termination of the event. The shift to heavier values and subsequent

  5. Geochemical translocation of thallium in the sediments from the North River, China (United States)

    Liu, J.


    Thallium (Tl) is a highly toxic rare heavy metal. As a sulphophile element, it usually occurs in numerous sulphide minerals (such as pyrite, galena, sphlerite). Guangdong north region, known as the hometown of nonferrous metals, has abundant containing Tl mineral resources. Numerous industrial activities, such as mining, smelting, and electroplating are also flourishing. In 2010, a serious Tl pollution in the North River (a major river in the Northern Guangdong Province) shocked the society. The Tl pollution in water appeared to be under control after that incident. But in fact, even if the wastewater discharge of pollution sources has been controlled, the potential risk of heavy metal pollution in the sediments of the North River still exists, for the metals are easy to precipitate and accumulate into sediment from water. So far, Tl pollution in sediments has been studied to a very limited extent. In this paper, we investigated the content and vertical distribution characteristics of Tl and some other related heavy metals in a typical sediment profile from the North River by using inductively coupled plasma mass spectrometry (ICP-MS). Then the Pb isotopic compositions in the sediments were measured by using multi-inductively coupled plasma mass spectrometry (MC-ICP-MS). Several sediments from typical layers were also subjected to sequential extraction procedure for investigating the geochemical fractions of Tl. The risk of Tl and other metal pollution was finally assessed by calculating geo-accumulation indexes (Igeo) and potential ecological risk. The results showed that: (1) Tl concentrations range 1.03 mg/kg to 3.13 mg/kg with a mean of 1.89 mg/kg, three times higher than that in local background soil; (2) Tl content generally increased with depth with some fluctuations and significant correlations were found between Tl and Pb, Zn, Cd, Cu, and Ni; (3) About 46 % to 70 % in sediment cores were resided in the residual fraction; (4) Igeo showed that the studied

  6. Source and distribution of sedimentary thallium in the Bohai Sea: Implications for hydrodynamic forces and anthropogenic impact (United States)

    Hu, Ningjing; Liu, Jihua; Shi, Xuefa


    Source and distribution of sedimentary thallium in the Bohai Sea: Implications for hydrodynamic forces and anthropogenic impact Hu Ningjing, Liu Jihua, Shi Xuefa First Institute of Oceanography, State Oceanic Administration, Qingdao 266061, China Thallium (Tl), a non-essential and highly toxic trace metal, is listed as priority toxic pollutant by the United States Environmental Protection Agency (USEPA) (Keith and Telliard, 1979). However, its geochemical cycling in aquatic environment has received far less attention than that of many other trace metals. This has been attributed to relatively little commercial interest in Tl and, until recently, problems inherent in its detection at environmental concentrations (Meeravali and Jiang, 2008). In this study, we investigated the sources, distribution and fate of Tl in surface sediments of the Bohai Sea (BS), China, based on the datasets of total Tl and chemical speciation of Tl of 408 surface sediment samples in the total entire BS. The enrichment factors and chemical speciation of Tl indicated that Tl in BS was dominated by natural Tl, although anthropogenic Tl contamination was observed in the Liuguhe River mouth; the mud deposits are the sinks of Tl and the regional currents and tide systems play a key role on the accumulation of Tl in BS. The distribution of Tl consistent with that of MnO and Fe2O3 as well as the level of Fe-Mn fraction is relatively high, indicating MnO and Fe2O3 influence the geochemical behaviors of Tl in the BS. Although the positive correlation between Tl and TOC is observed for the samples in the BS, however, level of Tl in oxidizable faction could be neglected, suggesting TOC might not be a major factor affecting the concentration of Tl in BS. The low proportion of Tl in the non-residual fraction dominated by the Fe-Mn oxides suggested that the labile Tl was controlled by the Fe-Mn oxides and Tl has a low bioavailability and a minor potential threat to biota in BS. Acknowledgements: this work

  7. Rhenium alloying of tungsten heavy alloys

    Energy Technology Data Exchange (ETDEWEB)

    Bose, A.; Jerman, G.; German, R.M.


    Alloying experiments have been performed using rhenium additions to a classic 90 mass% tungsten heavy alloy. The mixed powder system was liquid phase sintered to full density at 1500/sup 0/C in 60 min. The rhenium modified alloys exhibited a smaller grain size, higher hardness, higher strength, and lower ductility than the unalloyed system. For an alloy with a composition of 84W-6Re-8Ni-2Fe, the sintered density was 17,4 Mg/m/sup 3/ with a yield strength of 815 MPa, tensile strength of 1180 MPa, and elongation to failure of 13%. This property combination results from the aggregate effects of grain size reduction and solid solution hardening due to rhenium. In the unalloyed system these properties require post-sintering swaging and aging; thus, alloying with rhenium is most attractive for applications where netshaping is desired, such as by powder injection molding. (orig.).

  8. Rhenium alloying of tungsten heavy alloys

    Energy Technology Data Exchange (ETDEWEB)

    German, R.M.; Bose, A.; Jerman, G.


    Alloying experiments were performed using rhenium additions to a classic 90 mass % tungsten heavy alloy. The mixed-powder system was liquid phase sintered to full density at 1500 C in 60 min The rhenium-modified alloys exhibited a smaller grain size, higher hardness, higher strength, and lower ductility than the unalloyed system. For an alloy with a composition of 84W-6Re-8Ni-2Fe, the sintered density was 17, 4 Mg/m{sup 3} with a yield strength of 815 MPa, tensile strength of 1180 MPa, and elongation to failure of 13%. This property combination results from the aggregate effects of grain size reduction and solid solution hardening due to rhenium. In the unalloyed system these properties require post-sintering swaging and aging; thus, alloying with rhenium is most attractive for applications where net shaping is desired, such as by powder injection molding.

  9. Nickel alloys development-Inconel alloys development

    Energy Technology Data Exchange (ETDEWEB)

    Park, Yong Soo; Uhm, Tae Sik; Kim, Taek Jun; Jeon, Yu Taek; Chang, Hyun Young [Yonsei University, Seoul (Korea, Republic of); Kim, Young Sik [Andong National University, Andon (Korea, Republic of)


    This report dealt with the evaluation of Alloy 600 and alloy 690 of steam= generator materials. The experimental alloys were divided into two groups. ; Seamless tubings made by different ingot, and Mo-modified alloys. Thermal treatment had no influenced on the anodic polarization resistance in some caustic solution, but improved stress corrosion resistance by CERT. The effect of SO{sub 4}{sup =} ions reduced markedly caustic SCC resistance. The corrosion mode by 70 days and 120 days C-ring tests revealed the intergranular corrosion instead of stress corrosion cracking. Mo addition on the corrosion resistance of Alloy 690M showed beneficial effect in neutral and acidic solutions, but a little effect in caustic solutions. However, the caustic stress corrosion resistance was improved by the addition of molybdenum. 27 refs., 84 figs., 5 tabs. (author)

  10. Fractionation and Mobility of Thallium in Volcanic Ashes after Eruption of Eyjafjallajökull (2010) in Iceland. (United States)

    Karbowska, Bozena; Zembrzuski, Wlodzimierz


    Volcanic ash contains thallium (Tl), which is highly toxic to the biosphere. The aim of this study was to determine the Tl concentration in fractions of volcanic ash samples originating from the Eyjafjallajökull volcano. A sequential extraction scheme allowed for a study of element migration in the environment. Differential pulse anodic stripping voltammetry using a flow measuring system was selected as the analytical method to determine Tl content. The highest average content of Tl in volcanic ash was determined in the fraction entrapped in the aluminosilicate matrix (0.329 µg g(-1)), followed by the oxidizable fraction (0.173 µg g(-1)). The lowest content of Tl was found in the water soluble fraction (0.001 µg g(-1)); however, this fraction is important due to the fact that Tl redistribution among all the fractions occurs through the aqueous phase.

  11. High strength alloys

    Energy Technology Data Exchange (ETDEWEB)

    Maziasz, Phillip James; Shingledecker, John Paul; Santella, Michael Leonard; Schneibel, Joachim Hugo; Sikka, Vinod Kumar; Vinegar, Harold J.; John, Randy Carl; Kim, Dong Sub


    High strength metal alloys are described herein. At least one composition of a metal alloy includes chromium, nickel, copper, manganese, silicon, niobium, tungsten and iron. System, methods, and heaters that include the high strength metal alloys are described herein. At least one heater system may include a canister at least partially made from material containing at least one of the metal alloys. At least one system for heating a subterranean formation may include a tublar that is at least partially made from a material containing at least one of the metal alloys.

  12. High strength alloys

    Energy Technology Data Exchange (ETDEWEB)

    Maziasz, Phillip James [Oak Ridge, TN; Shingledecker, John Paul [Knoxville, TN; Santella, Michael Leonard [Knoxville, TN; Schneibel, Joachim Hugo [Knoxville, TN; Sikka, Vinod Kumar [Oak Ridge, TN; Vinegar, Harold J [Bellaire, TX; John, Randy Carl [Houston, TX; Kim, Dong Sub [Sugar Land, TX


    High strength metal alloys are described herein. At least one composition of a metal alloy includes chromium, nickel, copper, manganese, silicon, niobium, tungsten and iron. System, methods, and heaters that include the high strength metal alloys are described herein. At least one heater system may include a canister at least partially made from material containing at least one of the metal alloys. At least one system for heating a subterranean formation may include a tubular that is at least partially made from a material containing at least one of the metal alloys.

  13. Creep Resistant Zinc Alloy

    Energy Technology Data Exchange (ETDEWEB)

    Frank E. Goodwin


    This report covers the development of Hot Chamber Die Castable Zinc Alloys with High Creep Strengths. This project commenced in 2000, with the primary objective of developing a hot chamber zinc die-casting alloy, capable of satisfactory service at 140 C. The core objectives of the development program were to: (1) fill in missing alloy data areas and develop a more complete empirical model of the influence of alloy composition on creep strength and other selected properties, and (2) based on the results from this model, examine promising alloy composition areas, for further development and for meeting the property combination targets, with the view to designing an optimized alloy composition. The target properties identified by ILZRO for an improved creep resistant zinc die-casting alloy were identified as follows: (1) temperature capability of 1470 C; (2) creep stress of 31 MPa (4500 psi); (3) exposure time of 1000 hours; and (4) maximum creep elongation under these conditions of 1%. The project was broadly divided into three tasks: (1) Task 1--General and Modeling, covering Experimental design of a first batch of alloys, alloy preparation and characterization. (2) Task 2--Refinement and Optimization, covering Experimental design of a second batch of alloys. (3) Task 3--Creep Testing and Technology transfer, covering the finalization of testing and the transfer of technology to the Zinc industry should have at least one improved alloy result from this work.

  14. Biocompatibility of dental alloys

    Energy Technology Data Exchange (ETDEWEB)

    Braemer, W. [Heraeus Kulzer GmbH and Co. KG, Hanau (Germany)


    Modern dental alloys have been used for 50 years to produce prosthetic dental restorations. Generally, the crowns and frames of a prosthesis are prepared in dental alloys, and then veneered by feldspar ceramics or composites. In use, the alloys are exposed to the corrosive influence of saliva and bacteria. Metallic dental materials can be classified as precious and non-precious alloys. Precious alloys consist of gold, platinum, and small amounts of non-precious components such as copper, tin, or zinc. The non-precious alloys are based on either nickel or cobalt, alloyed with chrome, molybdenum, manganese, etc. Titanium is used as Grade 2 quality for dental purposes. As well as the dental casting alloys, high purity electroplated gold (99.8 wt.-%) is used in dental technology. This review discusses the corrosion behavior of metallic dental materials with saliva in ''in vitro'' tests and the influence of alloy components on bacteria (Lactobacillus casei and Streptococcus mutans). The test results show that alloys with high gold content, cobalt-based alloys, titanium, and electroplated gold are suitable for use as dental materials. (orig.)

  15. Determination of gold, indium, tellurium and thallium in the same sample digest of geological materials by atomic-absorption spectroscopy and two-step solvent extraction (United States)

    Hubert, A.E.; Chao, T.T.


    A rock, soil, or stream-sediment sample is decomposed with hydrofluoric acid, aqua regia, and hydrobromic acid-bromine solution. Gold, thallium, indium and tellurium are separated and concentrated from the sample digest by a two-step MIBK extraction at two concentrations of hydrobromic add. Gold and thallium are first extracted from 0.1M hydrobromic acid medium, then indium and tellurium are extracted from 3M hydrobromic acid in the presence of ascorbic acid to eliminate iron interference. The elements are then determined by flame atomic-absorption spectrophotometry. The two-step solvent extraction can also be used in conjunction with electrothermal atomic-absorption methods to lower the detection limits for all four metals in geological materials. ?? 1985.

  16. Catalyst Alloys Processing (United States)

    Tan, Xincai


    Catalysts are one of the key materials used for diamond formation at high pressures. Several such catalyst products have been developed and applied in China and around the world. The catalyst alloy most widely used in China is Ni70Mn25Co5 developed at Changsha Research Institute of Mining and Metallurgy. In this article, detailed techniques for manufacturing such a typical catalyst alloy will be reviewed. The characteristics of the alloy will be described. Detailed processing of the alloy will be presented, including remelting and casting, hot rolling, annealing, surface treatment, cold rolling, blanking, finishing, packaging, and waste treatment. An example use of the catalyst alloy will also be given. Industrial experience shows that for the catalyst alloy products, a vacuum induction remelt furnace can be used for remelting, a metal mold can be used for casting, hot and cold rolling can be used for forming, and acid pickling can be used for metal surface cleaning.

  17. Low activation ferritic alloys (United States)

    Gelles, D.S.; Ghoniem, N.M.; Powell, R.W.


    Low activation ferritic alloys, specifically bainitic and martensitic stainless steels, are described for use in the production of structural components for nuclear fusion reactors. They are designed specifically to achieve low activation characteristics suitable for efficient waste disposal. The alloys essentially exclude molybdenum, nickel, nitrogen and niobium. Strength is achieved by substituting vanadium, tungsten, and/or tantalum in place of the usual molybdenum content in such alloys.

  18. Comparison of glucose-insulin-thallium-201 infusion single photon emission computed tomography (SPECT), stress-redistribution-reinjection thallium-201 SPECT and low dose dobutamine echocardiography for prediction of reversible dysfunction

    Energy Technology Data Exchange (ETDEWEB)

    Sakamoto, Hiroki; Kondo, Makoto; Motohiro, Masayuki; Usami, Satoru [Shimada Municipal Hospital, Shizuoka (Japan)


    The usefulness of glucose-insulin-thallium-201 (GI-Tl) infusion single photon emission computed tomography (SPECT) in predicting reversible dysfunction has not been evaluated, so the present study recruited 20 patients with regional ischemic dysfunction for investigation. All patients underwent GI-Tl SPECT, post-stress Tl reinjection imaging and low dose dobutamine echocardiography. The diagnostic accuracy of these 3 techniques in predicting functional recovery was evaluated by receiver operating characteristic (ROC) analysis. In segments with functional recovery, regional Tl activities of GI-Tl SPECT were significantly higher than those of reinjection imaging (p<0.05), although there were no significant differences in segments without recovery. The area under the ROC curve for GI-Tl SPECT (0.75{+-}0.06) was greater than that for reinjection imaging (0.68{+-}0.07). The optimal cutoff values to identify viable myocardium were considered to be 55% of peak activity for GI-Tl SPECT and 50% for reinjection imaging. At this cutoff point, the sensitivity and specificity for detection of functional recovery were, respectively, 85% and 61% for GI-Tl SPECT, and 73% and 61% for reinjection imaging. Dobutamine echocardiography had the same sensitivity (85%), but lower specificity (48%) than GI-Tl SPECT. Continuous infusion of GI-Tl solution enhances regional Tl uptake compared with conventional post-stress reinjection imaging. This study suggests that GI-Tl SPECT is superior to reinjection imaging and dobutamine echocardiography in predicting functional recovery after ischemic left ventricular dysfunction. (author)

  19. Copper-tantalum alloy (United States)

    Schmidt, Frederick A.; Verhoeven, John D.; Gibson, Edwin D.


    A tantalum-copper alloy can be made by preparing a consumable electrode consisting of an elongated copper billet containing at least two spaced apart tantalum rods extending longitudinally the length of the billet. The electrode is placed in a dc arc furnace and melted under conditions which co-melt the copper and tantalum to form the alloy.

  20. Ultrahigh temperature intermetallic alloys

    Energy Technology Data Exchange (ETDEWEB)

    Brady, M.P.; Zhu, J.H.; Liu, C.T.; Tortorelli, P.F.; Wright, J.L.; Carmichael, C.A.; Walker, L.R. [Oak Ridge National Lab., TN (United States). Metals and Ceramics Div.


    A new family of Cr-Cr{sub 2}X based alloys with fabricability, mechanical properties, and oxidation resistance superior to previously developed Cr-Cr{sub 2}Nb and Cr-Cr{sub 2}Zr based alloys has been identified. The new alloys can be arc-melted/cast without cracking, and exhibit excellent room temperature and high-temperature tensile strengths. Preliminary evaluation of oxidation behavior at 1100 C in air indicates that the new Cr-Cr{sub 2}X based alloys form an adherent chromia-based scale. Under similar conditions, Cr-Cr{sub 2}Nb and Cr-Cr{sub 2}Zr based alloys suffer from extensive scale spallation.

  1. Detection and dosimetry of gamma ray emitted from thallium-201 and technetium-99m based on chemiluminescence technique

    Energy Technology Data Exchange (ETDEWEB)

    Shourian, Mostafa [Laboratory of Microanalysis, Institute of Biochemistry and Biophysics, University of Tehran, P.O. Box 13145-1384, Tehran (Iran, Islamic Republic of); Tavakoli, Hassan, E-mail: [Faculty of Medicine, Department of Physiology and Biophysics, Faculty of Medicine, Baqiyatollah University of Medical Sciences, P.O. Box 19395-6558, Tehran (Iran, Islamic Republic of); Ghourchian, Hedayatollah, E-mail: [Laboratory of Microanalysis, Institute of Biochemistry and Biophysics, University of Tehran, P.O. Box 13145-1384, Tehran (Iran, Islamic Republic of); Rafiee-Pour, Hossain-Ali [Laboratory of Microanalysis, Institute of Biochemistry and Biophysics, University of Tehran, P.O. Box 13145-1384, Tehran (Iran, Islamic Republic of)


    This report describes the detection and dosimetry of gamma ray emitted from Thallium-201 ({sup 201}Tl) and Technetium-99m ({sup 99m}Tc) based on chemiluminescence technique. H{sub 2}O{sub 2} produced by two gamma emitter radioisotopes of {sup 201}Tl and {sup 99m}Tc were quantitatively measured by chemiluminescence method. Upon producing H{sub 2}O{sub 2} in a luminol alkaline solution, in the presence of diperiodatocuprate, as catalyst a chemical reaction was accrued and consequently the emitted light was measured. The determined H{sub 2}O{sub 2} concentration was correlated with the gamma ray detection and dosimetry. The sensitivity of chemiluminescence technique for {sup 201}Tl and {sup 99m}Tc dosimetry was determined to be 0.20 and 0.08 MBq/l (Mega Becquerel per liter) respectively (R.S.D. = %5, N = 3). The plotted calibration curves showed detection limits of 3.24 and 1.76 MBq/l for {sup 201}Tl and {sup 99m}Tc, respectively.

  2. Myocardial infarction diagnosis with body surface potential mapping, electrocardiography, vectorcardiography and thallium-201 scintigraphy: a correlative study with left ventriculography. (United States)

    Ackaoui, A; Nadeau, R; Sestier, F; Savard, P; Primeau, R; Lemieux, R; Descary, M C


    In 35 subjects with typical or atypical angina and/or documented myocardial infarction (MI), body surface potential maps (BSPMs), ECG, VCG and rest Thallium-201 (T1-201) have been compared to left ventriculography (LVG). BSPMs were recorded with 26 ECGs, and BSPM abnormalities for MI cases were considered to be areas of normally positive potentials that have become negative. Subjects with MI were classified according to the segmental localization and degree of asynergy on LVG. Moderate anterolateral and apical asynergy were found to correlate with BSPM diagnosis of anterolateral MI and ischemia, severe anterolateral and apical asynergy with BSPM diagnosis of anterolateral MI and ischemia, and moderate diaphragmatic and/or posterobasal asynergy with BSPM diagnosis of posterior MI. Simultaneous anterior and posterior asynergy were found for BSPM diagnosis of anterior with posterior MI. Subjects with no LVG asynergy had normal BSPMs. BSPM diagnosis had the highest correlation coefficient with the LVG diagnosis (r = 0.88). ECG and VCG showed similar results with r = 0.65 and 0.71 respectively, while T1-201 had r = 0.55. The examination of our BSPMs, as well as the ECG, VCG and T1-201, did not permit to detect apical damage in presence of anterior MI, and posterobasal damage in the presence of inferoposterior MI. It is concluded that BSPMs are slightly superior to ECG and VCG for diagnosis of MI.

  3. Thallium release from acid mine drainages: Speciation in river and tap water from Valdicastello mining district (northwest Tuscany). (United States)

    Campanella, Beatrice; Casiot, Corinne; Onor, Massimo; Perotti, Martina; Petrini, Riccardo; Bramanti, Emilia


    In this work we present an advantageous method for the simultaneous separation and detection of Tl(I) and Tl(III) species through ion chromatography coupled with on-line inductively coupled plasma - mass spectrometry. Chromatographic separation between Tl(III) and Tl(I) was achieved in less than two minutes. The method was validated by recovery experiments on real samples, and by comparing the sum of the concentrations of individual Tl species with total thallium values obtained from continuous flow ICP-MS. The experimental procedure offers an accurate, sensitive and interference-free method for Tl speciation at trace levels in environmental samples. This allowed us to investigate the Tl speciation in acid mine drainages (AMD), surface waters and springs in a mining catchment in Valdicastello Carducci (Tuscany, Italy), where severe Tl contamination ad been evidenced previously. This study shows for the first time that Tl(III), in addition to Tl(I), is present in considerable amounts in water samples affected by acid mining outflow, raising the question of the origin of this thermodynamically unstable species. Copyright © 2017 Elsevier B.V. All rights reserved.

  4. Brazing dissimilar aluminum alloys (United States)

    Dalalian, H.


    Dip-brazing process joins aluminum castings to aluminum sheet made from different aluminum alloy. Process includes careful cleaning, surface preparation, and temperature control. It causes minimum distortion of parts.

  5. Thallium in spawn, juveniles, and adult common toads (Bufo bufo) living in the vicinity of a zinc-mining complex, Poland


    Dmowski, Krzysztof; Rossa, Monika; Kowalska, Joanna; Krasnodębska-Ostręga, Beata


    A breeding population of the common toad Bufo bufo living in the vicinity of a Zn-Pb smelting works in Bukowno, Poland was studied for the presence of thallium. Tl concentration was measured in the bottom sediments of the spawning pond, in the laid eggs, in juveniles after metamorphosis, and in the selected tissues of the adult individuals. A very high concentration of Tl was detected in the spawn (13.97 ± 8.90 mg/kg d.w.). In 50 % of the spawn samples, levels exceeded 20 mgTl/kg d.w. The iss...

  6. Machining of titanium alloys

    CERN Document Server


    This book presents a collection of examples illustrating the resent research advances in the machining of titanium alloys. These materials have excellent strength and fracture toughness as well as low density and good corrosion resistance; however, machinability is still poor due to their low thermal conductivity and high chemical reactivity with cutting tool materials. This book presents solutions to enhance machinability in titanium-based alloys and serves as a useful reference to professionals and researchers in aerospace, automotive and biomedical fields.

  7. Pareto-optimal alloys

    DEFF Research Database (Denmark)

    Bligaard, Thomas; Johannesson, Gisli Holmar; Ruban, Andrei


    and the cost. In this letter we present a database consisting of the lattice parameters, bulk moduli, and heats of formation for over 64 000 ordered metallic alloys, which has been established by direct first-principles density-functional-theory calculations. Furthermore, we use a concept from economic theory......, the Pareto-optimal set, to determine optimal alloy solutions for the compromise between low compressibility, high stability, and cost....

  8. Effects of potassium channel opener on the kinetics of thallium-201 in in-vitro and in-vivo

    Energy Technology Data Exchange (ETDEWEB)

    Lee, J.; Kim, E. J.; Ahn, B. C.; Chae, S. C.; Lee, K. B. [College of Medicine, Kyungpook National Univ., Taegu (Korea, Republic of); Kim, C. K. [Mt. Sinai Medical School, New York (United States)


    Potassium channel opener (K-opener) opens membrane ATP-sensitive K{sup +}-channel and induces and increase in potassium efflux from cells. K-openers are powerful smooth muscle relaxants and currently used as antihypertensive, antianginal drugs or bronchodilators in clinic. Pharmacologic potency of newly synthesized K-opener is being evaluated with efflux capacity of preincubated Rb-83 from the isolated aortic vascular tissue preparation. Thallium has similar characteristics to those of rubidium and potassium in vivo. To evaluate the effect of pinacidil (a potent K-opener) on Tl-201 biokinetics, we have performed uptake/washout studies in cultured myocytes, and mice biodistribution study. Primary culture of spontaneous contracting myocytes was undertake from hearts of newborn Sprague-Dawley rat. Different concentration of pinacidil (100nM or 10uM) was co-incubated with Tl-201 in HBSS buffer to evaluate its effect on cellular uptake, or challenged to myocyte preparations pre-incubated with Tl-201 for washout study. Pinacidil was injected into mice simultaneous or 10-min after Tl-201 injection, and organ uptake and whole body retention ratio was measured using gamma counter or dose calibrator. Co-incubation of pinacidil with Tl-201 resulted in a decrease in Tl uptake into myocytes by 1.6 - 2.5 times, and an increase in washout by 1.6 - 3.1 times. Pinacidil injection resulted in mild decrease in blood, heart and liver uptake in mice, bur renal uptake was markedly decreased in a dose dependent manner. These results suggest that the pinacidil Tl-201 kinetics and may potentially affect the interpretation of Tl-201 myocardial imaging.

  9. Functional Significance of Angiographic Collaterals in Patients with Totally Occluded Right Coronary Artery: Intracoronary Thallium-201 Scintigraphy

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Do Yun; Lee, Jong Doo; Cho, Seung Yun; Shim, Won Heum; Ha, Jong Won; Kim, Han Soo; Kwon, Hyuk Moon; Jang, Yang Soo; Chung, Nam Sik; Kim, Sung Soon [Yonsei University College of Medicine, Seoul (Korea, Republic of); Park, Chang Yun; Kim, Young Soo [Inje University College of Medicine, Seoul (Korea, Republic of)


    To compare the myocardial viability in patients suffering from total occlusion of the right coronary artery (RCA) with the angiographic collaterals, intracoronary injection of Thallium-201 (T1-201) was done to 14 coronary artery disease (CAD) patients (pts) with total occlusion of RCA and into four normal subjects for control. All 14 CAD pts had Grade 2 or 3 collateral circulations. There were 14 male and 4 females, and their ages ranged from 31 to 70 years. In nine pts, T1-201 was injected into left main coronary artery (LCA) (300 approx 350 mu Ci) to evaluate the myocardial viability of RCA territory through collateral circulations. The remaining five pts received T1-201 into RCA (200-250 mu Ci) because two had intraarterial bridging collaterals and three had previous successful PTCA. Planar and SPECT myocardial perfusion images were obtained 30 minutes, and four to five hours after T1-201 reinjection. Intravenous T1-201 reinjection (six pts) or {sup 99m}Tc-MIBI (two pts) were also performed in eight CAD pts. Intracoronary myocardial perfusion images were compared with intravenous T1-201(IV T1-201) images, EGG, and ventriculography. Intracoronary TI-201 images proved to be superior to that of IV T1-201 due to better myocardial to background uptake ratio and more effective in the detection of viable tissue. We also found that perfusion defects were smaller on intracoronary T1-201 images than those on the IV T1-201. All of the 14 CAD pts had either mostly viable myocardium (seven pts) or large area of T1-201 perfusion (seven pts) in RCA territory, however ventriculographic wall motion and ECG did not correlate well with intracoronary myocardial perfusion images. In conclusion, total RCA occlusion patients with well developed collateral circulation had large area of viable myocardial in the corresponding territory.

  10. Disease stage classification in hypertrophic cardiomyopathy by dual analysis of iodine-123-labeled metaiodobenzylguanidine and thallium-201 myocardial scintigraphies

    Energy Technology Data Exchange (ETDEWEB)

    Hiasa, Go [Ehime Univ., Matsuyama (Japan). School of Medicine


    Many patients with hypertrophic cardiomyopathy (HCM) gradually changes from typical myocardial hypertrophy to dilated cardiomyopathy-like features. However, it is difficult to estimate the disease stage in HCM. To determine the disease stage, dual analysis of iodine-123-labeled metaiodobenzylguanidine ({sup 123}I-MIBG) and thallium-201 ({sup 201}Tl) myocardial scintigraphies were performed in 108 HCM patients. According to the scintigraphic distribution patterns, patients were divided into three groups. Group A (n=15): normal distributions of both {sup 123}I-MIBG and {sup 201}Tl, group B (n=71): normal {sup 201}Tl and low {sup 123}I-MIBG patterns, group C (n=22): low distributions of both scintigraphies. The decrease in {sup 201}Tl uptake was observed in only group C. Concerning {sup 123}I-MIBG, heart-to-mediastinum ratio (H/M) and washout rate (WOR) had good correlations with left ventricular systolic functions. H/M was decreased and WOR was increased in order of C, B and A groups. Left ventricular diastolic function reflected by isovolumic relaxation time was longer in group B than in group A. Attenuated left ventricular hypertrophy, enlarged left ventricular volumes, impaired left ventricular functions and serious clinical symptoms were observed in only group C. Myocardial sympathetic abnormalities in group B may be mainly due to myocardial hypertrophy, and those in group C may be due to myocardial injury. Dual analysis of {sup 123}I-MIBG and {sup 201}Tl scintigraphies may be useful to classify disease stages of HCM. (author)

  11. New quaternary thallium indium germanium selenide TlInGe2Se6: Crystal and electronic structure (United States)

    Khyzhun, O. Y.; Parasyuk, O. V.; Tsisar, O. V.; Piskach, L. V.; Myronchuk, G. L.; Levytskyy, V. O.; Babizhetskyy, V. S.


    Crystal structure of a novel quaternary thallium indium germanium selenide TlInGe2Se6 was investigated by means of powder X-ray diffraction method. It was determined that the compound crystallizes in the trigonal space group R3 with the unit cell parameters a = 10.1798(2) Å, c = 9.2872(3) Å. The relationship with similar structures was discussed. The as-synthesized TlInGe2Se6 ingot was tested with X-ray photoelectron spectroscopy (XPS) and X-ray emission spectroscopy (XES). In particular, the XPS valence-band and core-level spectra were recorded for initial and Ar+ ion-bombarded surfaces of the sample under consideration. The XPS data allow for statement that the TlInGe2Se6 surface is rigid with respect to Ar+ ion-bombardment. Particularly, Ar+ ion-bombardment (3.0 keV, 5 min duration, ion current density fixed at 14 μA/cm2) did not cause substantial modifications of stoichiometry in topmost surface layers. Furthermore, comparison on a common energy scale of the XES Se Kβ2 and Ge Kβ2 bands and the XPS valence-band spectrum reveals that the principal contributions of the Se 4p and Ge 4p states occur in the upper and central portions of the valence band of TlInGe2Se6, respectively, with also their substantial contributions in other portions of the band. The bandgap energy of TlInGe2Se6 at the level of αg=103 cm-1 is equal to 2.38 eV at room temperature.

  12. Synthesis, Characterization and Antibacterial Studies of N-(Benzothiazol-2-yl-4-chlorobenzenesulphonamide and Its Neodymium(III and Thallium(III Complexes

    Directory of Open Access Journals (Sweden)

    Lawrence Nnamdi Obasi


    Full Text Available N-(Benzothiazol-2-yl-4-chlorobenzenesulphonamide (NBTCS was synthesized by condensation reaction of 4-chlorobenzenesulphonyl chloride and 2-aminobenzothiazole in acetone under reflux. Neodymium(III and thallium(III complexes of the ligand were also synthesized. Both ligand and metal complexes were characterized using UV-Vis, IR, 1H- and 13C-NMR spectroscopies, elemental analysis and molar conductance measurement. IR studies revealed that the ligand is tridentate and coordinates to the metal ions through nitrogen and oxygen atoms of the sulphonamide group and nitrogen atom attached to benzothiazole ring. The neodymium(III complex displays a coordination number of eight while thallium(III complex displays a coordination number of six. The ligand and its complexes were screened in vitro for their antibacterial activities against Escherichia coli strains (E. coli 6 and E. coli 13, Proteus species, Staphylococcus aureus and Pseudomonas aeruginosa using the agar well diffusion technique. The synthesized compounds were found to be more active against the microorganisms screened relative to ciprofloxacin, gentamicin and co-trimoxazole.

  13. Comparative study of body surface isopotential map, left ventriculogram and thallium-201 myocardial scintigram in patients with old lateral myocardial infarction

    Energy Technology Data Exchange (ETDEWEB)

    Matsumoto, Naoyuki


    In 16 patients with old lateral myocardial infarction, body surface isopotential maps and 12 lead electrocardiograms were compared with left ventriculographic findings. In addition 8 of these subjects were performed thallium-201 myocardial scintigraphy in order to determine the location and extent of myocardial necrosis. Common 12 lead electrocardiographic findings of the subjects were initial Q waves more than 30 msec and inverted T waves in only aVL lead. The patients were classified into 4 groups according to the location and extent of ventricular wall motion abnormalities group I (6 cases) showed hypokinesis in the anterior segment, group II (5 cases): akinesis in the anterior segment and hypokinesis in the seg. 6, group III (4 cases): hypokinesis in the anterior segment and seg. 7, group IV (1 case): hypokinesis in the anterior segment and seg. 4, 7. And each of the 4 groups demonstrated characteristic findings of surface isopotential maps. Group II with coexisting hypokinesis in the seg. 6 showed surface isopotential maps additional pattern of anterior myocardial infarction, and group III with coexisting hypokinesis in the seg. 7 showed additional patterns of posterior myocardial infarction. The classification according to the abnormality of ventricular wall motion was also conformed with the thallium-201 myocardial scintigraphic findings except one case. These results suggest that body surface isopotential map is more useful than the 12 lead electrocardiogram in detecting the location and extent of left ventricular wall motion abnormality in patients with old lateral myocardial infarction. (author) 53 refs.

  14. Serial thallium-201 imaging at rest in patients with unstable and stable angina pectoris: relationship of myocardial perfusion at rest to presenting clinical syndrome

    Energy Technology Data Exchange (ETDEWEB)

    Brown, K.A.; Okada, R.D.; Boucher, C.A.; Phillips, H.R.; Strauss, H.W.; Pohost, G.M.


    In order to determine whether there are differences in myocardial perfusion at rest among patients with various unstable and stable angina syndromes, serial thallium-201 imaging was performed at rest in 19 patients presenting with rapidly worsening exertional angina (unstable angina, group A), 12 patients with rest angina alone without exertional symptoms (unstable angina, group B), and 34 patients with chronic stable angina. No patient had an episode of angina within 4 hours of study. Nineteen of 19 (100%) patients in group A demonstrated transient defects compared to only 3 of 12 (25%) patients in group B (p less than 0.0001) and 4 of 34 (12%) stable angina patients (p less than 0.0001). The majority of zones demonstrating transient defects in group A were associated with hypokinesis of the corresponding left ventriculogram segment without associated ECG evidence of previous infarction. There were no significant differences in the frequency of persistent thallium defects, severity of angiographic coronary artery disease, or frequency of regional wall motion abnormalities of myocardial segments supplied by stenotic coronary arteries among the three groups of patients. Transient defects have been shown to reflect reduction in regional coronary blood flow to viable myocardium. Therefore, we conclude that regional resting hypoperfusion of viable myocardium is far more common in patients with exertional unstable angina symptoms than in patients with rest angina alone or chronic stable angina.

  15. Impact toughness of laser alloyed aluminium AA1200 alloys

    CSIR Research Space (South Africa)

    Mabhali, Luyolo AB


    Full Text Available Laser surface alloying of aluminium AA1200 was performed with a 4kW Nd:YAG laser and impact resistance of the alloys was investigated. The alloying powders were a mixture of Ni, Ti and SiC in different proportions. Surfaces reinforced...


    Directory of Open Access Journals (Sweden)

    Berat Barıs BULDUM


    Full Text Available Magnesium is the lightest structural metal. Magnesium alloys have a hexagonal lattice structure, which affects the fundamental properties of these alloys. Plastic deformation of the hexagonal lattice is more complicated than in cubic latticed metals like aluminum, copper and steel. Magnesium alloy developments have traditionally been driven by industry requirements for lightweight materials to operate under increasingly demanding conditions. Magnesium alloys have always been attractive to designers due to their low density, only two thirds that of aluminium and its alloys [1]. The element and its alloys take a big part of modern industry needs. Especially nowadays magnesium alloys are used in automotive and mechanical (trains and wagons manufacture, because of its lightness and other features. Magnesium and magnesium alloys are the easiest of all metals to machine, allowing machining operations at extremely high speed. All standard machining operations such as turning, drilling, milling, are commonly performed on magnesium parts.

  17. Structural thermodynamics of alloys

    CERN Document Server

    Manenc, Jack


    Technical progress has for a very long time been directly dependent on progress in metallurgy, which is itself connected with improvements in the technology of alloys. Metals are most frequently used in the form of alloys for several reasons: the quantity of pure metal in its native state in the earth's crust is very limited; pure metals must be extracted from ores which are themselves impure. Finally, the methods of treatment used lead more easily to alloys than to pure metals. The most typical case is that of iron, where a pure ore may be found, but which is the starting point for cast iron or steel, alloys of iron and carbon. In addition, the properties of alloys are in general superior to those of pure metals and modem metallurgy consists of controlling these properties so as to make them conform to the requirements of the design office. Whilst the engineer was formerly compelled to adapt his designs and constructions to the materials available, such as wood, stone, bronze, iron, cast iron and ordinary st...



    Berat Barıs BULDUM; Aydın SIK; Iskender OZKUL


    Magnesium is the lightest structural metal. Magnesium alloys have a hexagonal lattice structure, which affects the fundamental properties of these alloys. Plastic deformation of the hexagonal lattice is more complicated than in cubic latticed metals like aluminum, copper and steel. Magnesium alloy developments have traditionally been driven by industry requirements for lightweight materials to operate under increasingly demanding conditions. Magnesium alloys have always been attra...

  19. De-alloyed platinum nanoparticles (United States)

    Strasser, Peter [Houston, TX; Koh, Shirlaine [Houston, TX; Mani, Prasanna [Houston, TX; Ratndeep, Srivastava [Houston, TX


    A method of producing de-alloyed nanoparticles. In an embodiment, the method comprises admixing metal precursors, freeze-drying, annealing, and de-alloying the nanoparticles in situ. Further, in an embodiment de-alloyed nanoparticle formed by the method, wherein the nanoparticle further comprises a core-shell arrangement. The nanoparticle is suitable for electrocatalytic processes and devices.

  20. Silumins alloy crystallization

    Directory of Open Access Journals (Sweden)

    S. Pietrowski


    Full Text Available This paper presents the results of research, by ATD method, of hypo-, near- and hyperutectic silumins crystallization containing the following alloying additives: Mg, Ni, Cu, Cr, Mo, W, V. It has been shown that, depending on their concentration may crystallize pre-eutectic or eutectic multicomponent phases containing these alloy additives. It has been revealed that any subsequent crystallizable phase nucleate and grows near the liquid/former crystallized phase interface. In multiphases compound also falls the silicon, resulting in a reduction in its quantity and the fragmentation in the eutectic mixture. As a result, it gets a high hardness of silumins in terms of 110-220HB.

  1. Advanced ordered intermetallic alloy deployment

    Energy Technology Data Exchange (ETDEWEB)

    Liu, C.T.; Maziasz, P.J.; Easton, D.S. [Oak Ridge National Lab., TN (United States)


    The need for high-strength, high-temperature, and light-weight materials for structural applications has generated a great deal of interest in ordered intermetallic alloys, particularly in {gamma}-based titanium aluminides {gamma}-based TiAl alloys offer an attractive mix of low density ({approximately}4g/cm{sup 3}), good creep resistance, and high-temperature strength and oxidation resistance. For rotating or high-speed components. TiAl also has a high damping coefficient which minimizes vibrations and noise. These alloys generally contain two phases. {alpha}{sub 2} (DO{sub 19} structure) and {gamma} (L 1{sub 0}), at temperatures below 1120{degrees}C, the euticoid temperature. The mechanical properties of TiAl-based alloys are sensitive to both alloy compositions and microstructure. Depending on heat-treatment and thermomechanical processing, microstructures with near equiaxed {gamma}, a duplex structure (a mix of the {gamma} and {alpha}{sub 2} phases) can be developed in TiAl alloys containing 45 to 50 at. % Al. The major concern for structural use of TiAl alloys is their low ductility and poor fracture resistance at ambient temperatures. The purpose of this project is to improve the fracture toughness of TiAl-based alloys by controlling alloy composition, microstructure and thermomechanical treatment. This work is expected to lead to the development of TiAl alloys with significantly improved fracture toughness and tensile ductility for structural use.

  2. Syndrome of diminished vasodilator reserve of the coronary microcirculation (microvascular angina or syndrome X): Diagnosis by combined atrial pacing and thallium 201 imaging--a case report

    Energy Technology Data Exchange (ETDEWEB)

    Magarian, G.J.; Palac, R.; Reinhart, S. (Veterans Administration Medical Center, Portland, OR (USA))


    Patients with angina-like chest pain without evidence of epicardial coronary artery disease or coronary arterial vasospasm are becoming increasingly recognized. These are often related to noncardiac causes including esophageal, musculoskeletal, and hyperventilatory or panic states. However, recently a subgroup of such patients are being recognized as having true myocardial ischemia and chest pain on the basis of diminished coronary microvascular vasodilatory reserve (microvascular ischemia or Syndrome X). The authors describe such a patient who was found to have replication of anginal pain associated with a reversible ischemic defect on thallium 201 imaging during atrial pacing, suggesting ischemia in this myocardial segment. Resolution of angina and ST segment electrocardiographic changes of ischemia occurred with cessation of pacing. We believe this is the first report of a patient with this form of myocardial ischemia diagnosed by this method and should be considered in patients with anginal chest pain after significant coronary artery disease and coronary vasospasm have been excluded.

  3. Determination of perfusion defect area in experimental myocardial infarction. A comparison between 201-thallium and sup 99m Tc methoxy-isobutyl-isonitril (MIBI)

    Energy Technology Data Exchange (ETDEWEB)

    Mueller, K.D.; Rohmann, S.; Bahavar, H.; Grebe, S.F.; Schaper, W.; Schlepper, M. (Kerckhoff-Klinik, Bad Nauheim (Germany))


    To assess the accuracy of two myocardial perfusion markers in quantifying defect size, the left anterior descending coronary artery (LAD) was occluded in 13 porcine hearts. Fourty minutes later 55 MBq {sup 201}TI and 370 MBq {sup 99m}Tc-MIBI were simultaneously injected i.v. in 10 animals. After injection and in vivo double nuclide SPECT acquisition, the risk area was demarcated with fluorescein (FI) dye in 5 animals. The in vitro defect area determined by {sup 201}TI was significant larger (15.8 {+-} 27%) than those of {sup 99m}Tc-MIBI, while FI compared to Tc showed no statistical difference. Thus, in a pig model Tc-MIBI was more accurate with ex vivo imaging. With SPECT thallium imaging defect size was overestimated. In vivo there was a distinct trend with Tc-MIBI studies to underestimate the defect size up to 16%. (orig.).

  4. High thallium content in rocks associated with Au-As-Hg-Tl and coal mineralization and its adverse environmental potential in SW Guizhou, China

    Energy Technology Data Exchange (ETDEWEB)

    Xiao, T.F.; Guha, J.; Boyle, D. [Chinese Academy of Science, Guiyang (China)


    This study is focused on high concentrations of Tl in rocks in SW Guizhou, China, that are related to several widely scattered disseminated gold-mercury-arsenic and coal deposits, and a primary Tl deposit within an Au-As-Hg-Tl metallogenic belt of the Huijiabao anticline. The Tl, Hg and As in the Lanmuchang Hg-Tl deposit area are associated with the abundant occurrence of sulfide minerals such as lorandite, realgar, orpiment and cinnabar. Concentrations of Tl range from 100 to 35 000 ppm in sulfide ores, and 39-490 ppm in host rocks. The enrichment of Au, Tl, Hg, As, and Sb in the Yanshang gold mineralized area reflects the occurrence of Au mineralization and its mineral assemblage of Tl-Hg-As-Sb sulfides. Thallium ranges from 0.22 to 16 ppm in Au ores and host rocks. Thallium in coals is enriched up to 46 ppm within the Au-As-Hg-TI metallogenic belt, and is derived from the regional Au-As-Hg-Tl mineralization. Mercury and As show a similar distribution to Tl with high concentrations in sulfide ores, coals and host rocks. Human populations living near and downstream of Tl deposits and Tl-bearing ore deposits are susceptible to Tl contamination because of its high toxicity and high uptake rate by crops. The dispersion of Tl, Hg and As associated with the primary mineralization of Au-As-Hg-TI can be traced through physical erosion and chemical weathering, producing secondary dispersion into sods, groundwater and surface water and crops. Mining activities compound the natural processes, readily dispersing Tl into the surface environment.

  5. Functional significance of myocardial perfusion defects induced by dipyridamole using thallium-201 single-photon emission computed tomography and two-dimensional echocardiography

    Energy Technology Data Exchange (ETDEWEB)

    Jain, A.; Suarez, J.; Mahmarian, J.J.; Zoghbi, W.A.; Quinones, M.A.; Verani, M.S. (Baylor College of Medicine, Houston, TX (USA))


    The mechanisms responsible for inhomogeneous myocardial blood flow after oral administration of a large dose (300 mg) of dipyridamole were assessed in 27 patients with serial thallium-201 single-photon emission computed tomography (SPECT) and simultaneous 2-dimensional echocardiograms. Myocardial tomographic images were obtained 50 minutes and 3 to 4 hours after administration of dipyridamole. Two-dimensional echocardiograms were recorded at baseline and then every 15 minutes for 60 minutes. Dipyridamole caused only a mild reduction in blood pressure (from 129 +/- 18 to 126 +/- 16 mm Hg) and a mild increase in heart rate (from 69 +/- 15 to 73 +/- 4 beats/min). Sixteen patients had perfusion defects after dipyridamole by SPECT, which underwent partial or total filling-in. Fourteen of these patients (87.5%) had either a new abnormality or further deterioration of a preexisting wall motion abnormality by 2-dimensional echocardiography, and thus were considered to have developed transient ischemia during dipyridamole administration. Ten of 11 patients (91%) with normal perfusion or fixed defects by SPECT had no further deterioration in wall motion after oral dipyridamole, and were thus considered to have no evidence of myocardial ischemia. In conclusion, most patients with transient thallium-201 defects after dipyridamole develop transient worsening of resting wall motion by 2-dimensional echocardiography, suggestive of true myocardial ischemia. Because myocardial oxygen demand, as indicated by the heart rate-blood pressure product, did not change significantly, the mechanism of myocardial ischemia in these patients is likely to be diminished regional blood flow related to a subendocardial steal induced by dipyridamole.

  6. Magnesium-lithium casting alloys (United States)

    Latenko, V. P.; Silchenko, T. V.; Tikhonov, V. A.; Maltsev, V. P.; Korablin, V. P.


    The strength properties of magnesium-lithium alloys at room, low, and high temperatures are investigated. It is found that the alloys may have practical application at ambient temperatures up to 100 C, that negative temperatures have a favorable influence on the alloy strength, and that cyclic temperature variations have practically no effect on the strength characteristics. The influence of chemical coatings on corrosion resistance of the MgLi alloys is examined. Several facilities based on pressure casting machines, low-pressure casting machines, and magnetodynamic pumps were designed for producing MgLi alloy castings. Results were obtained for MgLi alloys reinforced with fibers having a volumetric content of 15%.

  7. Two phase titanium aluminide alloy

    Energy Technology Data Exchange (ETDEWEB)

    Deevi, Seetharama C. (Midlothian, VA); Liu, C. T. (Oak Ridge, TN)


    A two-phase titanic aluminide alloy having a lamellar microstructure with little intercolony structures. The alloy can include fine particles such as boride particles at colony boundaries and/or grain boundary equiaxed structures. The alloy can include alloying additions such as .ltoreq.10 at % W, Nb and/or Mo. The alloy can be free of Cr, V, Mn, Cu and/or Ni and can include, in atomic %, 45 to 55% Ti, 40 to 50% Al, 1 to 5% Nb, 0.3 to 2% W, up to 1% Mo and 0.1 to 0.3% B. In weight %, the alloy can include 57 to 60% Ti, 30 to 32% Al, 4 to 9% Nb, up to 2% Mo, 2 to 8% W and 0.02 to 0.08% B.

  8. Materials data handbook, Inconel alloy 718 (United States)

    Sessler, J.; Weiss, V.


    Materials data handbook on Inconel alloy 718 includes data on the properties of the alloy at cryogenic, ambient, and elevated temperatures and other pertinent engineering information required for the design and fabrication of components and equipment utilizing this alloy.

  9. Nanoscale Alloying in Electrocatalysts

    Directory of Open Access Journals (Sweden)

    Shiyao Shan


    Full Text Available In electrochemical energy conversion and storage, existing catalysts often contain a high percentage of noble metals such as Pt and Pd. In order to develop low-cost electrocatalysts, one of the effective strategies involves alloying noble metals with other transition metals. This strategy promises not only significant reduction of noble metals but also the tunability for enhanced catalytic activity and stability in comparison with conventional catalysts. In this report, some of the recent approaches to developing alloy catalysts for electrocatalytic oxygen reduction reaction in fuel cells will be highlighted. Selected examples will be also discussed to highlight insights into the structural and electrocatalytic properties of nanoalloy catalysts, which have implications for the design of low-cost, active, and durable catalysts for electrochemical energy production and conversion reactions.

  10. Ultralight Magnesium-Lithium Alloys


    A. Białobrzeski; K. Saja; Hubner, K.


    The article gives basic information on the chief constituents of Mg-Li alloys and on their expected properties. A schematic representation and technical performance of a pilot stand for melting and pouring of reactive ultralight magnesium-based alloys have been presented. The preliminary data regarding the manufactured magnesium alloys with about 2-3 % Li and about 10 % Li have been given in the form of microstructures and chemical compositions.

  11. Titanium alloys for aerospace applications

    Energy Technology Data Exchange (ETDEWEB)

    Peters, M.; Leyens, C. [DLR-German Aerospace Center, D-51170 Koeln (Germany); Kumpfert, J. [Airbus Industrie, F-31707 Blagnac (France); Ward, C.H. [US Air Force Research Laboratory, London NW1 5TH (United Kingdom)


    There is probably no other material more closely related to aerospace than titanium and its alloys. With a density of 4.5 g/cm{sup 3}, titanium alloys are only about half as heavy as steel or Ni-based superalloys, yielding an excellent strength-to-weight ratio. Furthermore, they have exceptional corrosion resistance. The use of titanium alloys in the aerospace sector will be highlighted including airframe, engine, helicopter, and space applications. (Abstract Copyright [2003], Wiley Periodicals, Inc.)

  12. Alloy catalyst material

    DEFF Research Database (Denmark)


    The present invention relates to a novel alloy catalyst material for use in the synthesis of hydrogen peroxide from oxygen and hydrogen, or from oxygen and water. The present invention also relates to a cathode and an electrochemical cell comprising the novel catalyst material, and the process use...... of the novel catalyst material for synthesising hydrogen peroxide from oxygen and hydrogen, or from oxygen and water....

  13. Aluminum alloy impact sparkling

    Directory of Open Access Journals (Sweden)

    M. Dudyk


    Full Text Available The cast machine parts are widely used in many branches of industry. A very important issue is gaining the appropriate knowledge relating to the application of castings in places of explosion risks including but not limited to mining, chemical industry and rescue works. A possibility of explosion risks occurrence following the impact sparkling of the cast metal parts is still not solved problem in scientific research. In relation to this issue, in this article, the results of the study are presented, and relating to the tendency to impact sparkling of the aluminium alloys used in machine building. On the grounds of the results obtained, it was demonstrated that the registered impact sparkles bunches of feathers from the analyzed alloys: AlSi7Mg, (AK7; AlSi9Mg, (AK9; AlSi6Cu4, (AK64 and AlSi11, (AK11 show significant differences between each other. The quantitative analysis of the temperature distribution and nuclei surface area performed on the example of the alloy AK9 (subjected to defined period of corrosion allows for the statement that they are dangerous in conditions of explosion risk. Following this fact, designers and users of machine parts made from these materials should not use them in conditions where the explosive mixtures occur.


    Coffinberry, A.S.


    A low melting point plutonium alloy useful as fuel is a homogeneous liquid metal fueled nuclear reactor is described. Vessels of tungsten or tantalum are useful to contain the alloy which consists essentially of from 10 to 30 atomic per cent copper and the balance plutonium and cerium. with the plutontum not in excess of 50 atomic per cent.

  15. Shape memory alloy based motor

    Indian Academy of Sciences (India) Keywords. Shape Memory Alloy (SMA); poly phase; rotary actuator; torque; ripple. Abstract. Design and characterization of a new shape memory alloy wire based Poly Phase Motor has been reported in this paper. The motor can be used either in stepping mode or ...

  16. Mo-Si alloy development

    Energy Technology Data Exchange (ETDEWEB)

    Liu, C.T.; Heatherly, L.; Wright, J.L. [Oak Ridge National Lab., TN (United States)


    The objective of this task is to develop new-generation corrosion-resistant Mo-Si intermetallic alloys as hot components in advanced fossil energy conversion and combustion systems. The initial effort is devoted to Mo{sub 5}-Si{sub 3}-base (MSB) alloys containing boron additions. Three MSB alloys based on Mo-10.5Si-1.1B (wt %), weighing 1500 g were prepared by hot pressing of elemental and alloy powders at temperatures to 1600{degrees}C in vacuum. Microporosities and glassy-phase (probably silicate phases) formations are identified as the major concerns for preparation of MSB alloys by powder metallurgy. Suggestions are made to alleviate the problems of material processing.

  17. Nickel alloys and high-alloyed special stainless steels. Properties, manufacturing, applications. 4. compl. rev. ed.

    Energy Technology Data Exchange (ETDEWEB)

    Heubner, Ulrich; Kloewer, Jutta; Alves, Helena; Behrens, Rainer; Schindler, Claudius; Wahl, Volker; Wolf, Martin


    This book contains the following eight topics: 1. Nickel alloys and high-alloy special stainless steels - Material overview and metallurgical principles (U. Heubner); 2. Corrosion resistance of nickel alloys and high-alloy special stainless steels (U. Heubner); 3. Welding of nickel alloys and high-alloy special stainless steels (T. Hoffmann, M. Wolf); 4. High-temperature materials for industrial plant construction (J. Kloewer); 5. Nickel alloys and high-alloy special stainless steels as hot roll clad composites-a cost-effective alternative (C. Schindler); 6. Selected examples of the use of nickel alloys and high-alloy special stainless steels in chemical plants (H. Alves); 7. The use of nickel alloys and stainless steels in environmental engineering (V. Wahl); 8: Nickel alloys and high-alloy special stainless steels for the oil and gas industry (R. Behrens).

  18. Stress Corrosion Cracking of Certain Aluminum Alloys (United States)

    Hasse, K. R.; Dorward, R. C.


    SC resistance of new high-strength alloys tested. Research report describes progress in continuing investigation of stress corrosion (SC) cracking of some aluminum alloys. Objective of program is comparing SC behavior of newer high-strength alloys with established SC-resistant alloy.

  19. Effects of Potassium-Channel Opener on Thallium-201 Kinetics: In-vitro Study in Rat Myocyte Preparations and In-vivo Mice Biodistribution Study

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jae Tae; Kim, Eun Ji; Ahn, Byeong Cheol; Son, Kang Kyun; Lee, Kyu Bo [Kyungpook National University School of Medicine, Taegu (Korea, Republic of); Ha, Jeoung Hee [Youngnam University Medical School, Taegu (Korea, Republic of); Kim, Chun Ki [Mt. Sinai School of Medicine, New York (United States)


    Potassium channel opener (K-opener) opens ATP-sensitive K{sup +}-channel located at membrane and induces potassium efflux from cytosol, resulting in intracellular hyperpolarization. Newly synthesized K-opener is currently examined for pharmacologic potency by means of rubidium release test from smooth muscle strip preincubated with Rb-86. Since in-vive behavior of thallium is similar to that of rubidium, we hypothesized that K-opener can alter T1-201 kinetics in vivo. This study was prepared to investigate the effects of pinacidil (one of potent K-openers) on the T1-201 uptake and clearance in cultured myocyte, and in-vivo biodistribution in mice. Spontaneous contracting myocytes were prepared to imitate in-vivo condition from 20 hearts of 3-5 days old Sprague-Dawley rat and cultured for 3-5 days before use (5 X 105 cells/ml). Pinacidil was dissolved in 10% DMSO solution at a final concentration of 100nM or 10uM and was co-incubated with T1-201 in HBSS buffer for 20-min to evaluate its effect on cellular T1-uptake, or challenged to cell preparation pre-incubated with T1-201 for washout study. Two, 40 or 100 mg of pinacidil was injected intravenously into ICR mice at 10 min after 5 muCi T1-201 injection, and organ uptake and whole body retention rate were measured at different time points. Co-incubation of pinacidil with T1-201 resulted in a decrease in T1-201 uptake into cultured myocyte by 1.6 to 2.5 times, depending on pinacidil concentration and activity of T1-201 used. Pinacidil enhanced T1-201 washout by 1.6-3.1 times from myocyte preparations pre-incubated with T1-201. Pinacidil treatment appears to be resulted in mild decreases in blood and liver activity in normal mice, in contrast, renal and cardiac uptake were mildly decreased in a dose dependent manner. Whole body retention ratios of T1-201 were lower at 24 hour after injection with 100 mg of pinacidil than control. These results suggest that treatment with K-opener may affect the interpretation of T1

  20. Heat storage in alloy transformations (United States)

    Birchenall, C. E.


    The feasibility of using metal alloys as thermal energy storage media was investigated. The elements selected as candidate media were limited to aluminum, copper, magnesium, silicon, zinc, calcium, and phosphorus on the basis of low cost and latent heat of transformation. Several new eutectic alloys and ternary intermetallic phases were determined. A new method employing X-ray absorption techniques was developed to determine the coefficients of thermal expansion of both the solid and liquid phases and the volume change during phase transformation. The method and apparatus are discussed and the experimental results are presented for aluminum and two aluminum-eutectic alloys. Candidate materials were evaluated to determine suitable materials for containment of the metal alloys. Graphite was used to contain the alloys during the volume change measurements. Silicon carbide was identified as a promising containment material and surface-coated iron alloys were also evaluated. System considerations that are pertinent if alloy eutectics are used as thermal energy storage media are discussed. Potential applications to solar receivers and industrial furnaces are illustrated schematically.

  1. Determination of particle mass deposition according to Bergerhoff; Performance characteristics of the measurement of particle mass deposition and its portions of lead, cadmium, zinc and thallium. Bestimmung des Staubniederschlags nach Bergerhoff; Verfahrenskenngroessen fuer die Messung des Staubniederschlags und seiner Anteile an Blei, Cadmium, Zink und Thallium

    Energy Technology Data Exchange (ETDEWEB)

    Gehrig, R. (Eidgenoessische Materialpruefungs- und Forschungsanstalt, Duebendorf (Switzerland). Abt. fuer Luftfremdstoffe); Faesi, C. (Eidgenoessische Materialpruefungs- und Forschungsanstalt, Duebendorf (Switzerland). Abt. fuer Luftfremdstoffe); Hofer, P. (Eidgenoessische Materialpruefungs- und Forschungsanstalt, Duebendorf (Switzerland). Abt. fuer Luftfremdstoffe)


    The requirements concerning quality assurance have increased considerably in the field of immission control. Well founded values for detection limits and confidence limits have to be given. Based on the statistical analysis of long term data series of deposition measurements of particle mass (Berghoff method), lead, cadmium, zinc and thallium performance characteristics were established for very differently polluted sites. The resulting detection limits as well as confidence limits are low enough for a reliable control of the respective immission limit values. It is further shown that the use of plastic buckets instead of the glass buckets required by the VDI guideline or the addition of a protecting agent to avoid freezing does not affect the measurements significantly. (orig.)

  2. Magnesium alloying - some metallurgical aspects

    Energy Technology Data Exchange (ETDEWEB)

    Pekgueleryuez, M.Oe. [Inst. of Magnesium Technology (ITM), Quebec, PQ (Canada); Avedesian, M.M. [Inst. of Magnesium Technology (ITM), Quebec, PQ (Canada)


    The incentive for alloy development is the need for new materials with a combination of better performance properties at lower cost. Over the past 45 years the development of new Mg alloys has lagged steel, aluminum, copper, zinc and other metals. The reasons for the slow development of Mg alloys since the 1920`s may have been the real and perceived short comings of Mg which has limited the wide acceptance of the metal by the various industries. In addition the advent of high performance plastics has put new competitive pressure on magnesium. Upon a close look, it can be seen that Mg does not possess a full alloy spectrum; there are really three to four major commercial alloy systems such as Mg-Al-Zn, Mg-Al, Mg-Zn and Mg-Rare Earths. In 1990 most magnesium usage for structural applications was in diecasting (36 kt) and 90% of this was in one alloy, AZ91D. This shows that Mg has not yet fully realized its potential as a structural metal. The 1990`s may, however, generate a long term driving force for magnesium alloy development due to the fact that industries such as the transport industry are faced more than ever with weight reduction objectives. They are driven to use light weight metals and will continue to do so in the future. Magnesium which is the lightest structural metal offers an attractive solution and the interest in the metal is increasing rapidly. This paper attempts to address the major problems of magnesium alloys with the view of identifying opportunities for cost-competitive ways of eliminating the problems of magnesium via alloy and microstructural design. A basic understanding of the fundamental mechanisms affecting strength and creep of Mg is also presented. (orig.)

  3. Dendritic Alloy Solidification Experiment (DASE) (United States)

    Beckermann, C.; Karma, A.; Steinbach, I.; deGroh, H. C., III


    A space experiment, and supporting ground-based research, is proposed to study the microstructural evolution in free dendritic growth from a supercooled melt of the transparent model alloy succinonitrile-acetone (SCN-ACE). The research is relevant to equiaxed solidification of metal alloy castings. The microgravity experiment will establish a benchmark for testing of equiaxed dendritic growth theories, scaling laws, and models in the presence of purely diffusive, coupled heat and solute transport, without the complicating influences of melt convection. The specific objectives are to: determine the selection of the dendrite tip operating state, i.e. the growth velocity and tip radius, for free dendritic growth of succinonitrile-acetone alloys; determine the growth morphology and sidebranching behavior for freely grown alloy dendrites; determine the effects of the thermal/solutal interactions in the growth of an assemblage of equiaxed alloy crystals; determine the effects of melt convection on the free growth of alloy dendrites; measure the surface tension anisotropy strength of succinon itrile -acetone alloys establish a theoretical and modeling framework for the experiments. Microgravity experiments on equiaxed dendritic growth of alloy dendrites have not been performed in the past. The proposed experiment builds on the Isothermal Dendritic Growth Experiment (IDGE) of Glicksman and coworkers, which focused on the steady growth of a single crystal from pure supercooled melts (succinonitrile and pivalic acid). It also extends the Equiaxed Dendritic Solidification Experiment (EDSE) of the present investigators, which is concerned with the interactions and transients arising in the growth of an assemblage of equiaxed crystals (succinonitrile). However, these experiments with pure substances are not able to address the issues related to coupled heat and solute transport in growth of alloy dendrites.

  4. Laser surface alloying on aluminum and its alloys: A review (United States)

    Chi, Yiming; Gu, Guochao; Yu, Huijun; Chen, Chuanzhong


    Aluminum and its alloys have been widely used in aerospace, automotive and transportation industries owing to their excellent properties such as high specific strength, good ductility and light weight. Surface modification is of crucial importance to the surface properties of aluminum and its alloys since high coefficient of friction, wear characteristics and low hardness have limited their long term performance. Laser surface alloying is one of the most effective methods of producing proper microstructure by means of non-equilibrium solidification which results from rapid heating and cooling. In this paper, the influence of different processing parameters, such as laser power and scanning velocity is discussed. The developments of various material systems including ceramics, metals or alloys, and metal matrix composites (MMCs) are reviewed. The microstructure, hardness, wear properties and other behaviors of laser treated layer are analyzed. Besides, the existing problems during laser surface treatment and the corresponding solutions are elucidated and the future developments are predicted.

  5. Alloying and Casting Furnace for Shape Memory Alloys Project (United States)

    National Aeronautics and Space Administration — The concept in the proposed project is to create a melting, alloying and casting furnace for the processing titanium based SMA using cold crucible techniques. The...

  6. Laser surface alloying of aluminium-transition metal alloys

    Directory of Open Access Journals (Sweden)

    Almeida, A.


    Full Text Available Laser surface alloying has been used as a tool to produce hard and corrosion resistant Al-transition metal (TM alloys. Cr and Mo are particularly interesting alloying elements to produce stable highstrength alloys because they present low diffusion coefficients and solid solubility in Al. To produce Al-TM surface alloys a two-step laser process was developed: firstly, the material is alloyed using low scanning speed and secondly, the microstructure is modified by a refinement step. This process was used in the production of Al-Cr, Al-Mo and Al-Nb surface alloys by alloying Cr, Mo or Nb powder into an Al and 7175 Al alloy substrate using a CO2 laser. This paper presents a review of the work that has been developed at Instituto Superior Tecnico on laser alloying of Al-TM alloys, over the last years.

    En el presente trabajo se estudia la aleación superficial mediante láser de aluminio con metales de transición. El cromo y el molibdeno son particularmente interesantes porque producen aleaciones de alta resistencia y por el bajo coeficiente de difusión y solución sólida en aluminio. Para producir estas aleaciones se ha seguido un procedimiento desarrollado en dos partes. En primer lugar, el material se alea usando una baja velocidad de procesado y en segundo lugar la estructura se modifica mediante un refinamiento posterior. Este procedimiento se ha empleado en la producción de aleaciones Al-Cr, Al-Mo y Al-Nb mediante aleación con láser de CO2 de polvos de Cr, Mo o Nb en aluminio y la aleación 7175. Este trabajo es una revisión del desarrollado en el Instituto Superior Técnico de Lisboa en los últimos años.

  7. Preparation, Characterization, and In Vivo Pharmacoscintigraphy Evaluation of an Intestinal Release Delivery System of Prussian Blue for Decorporation of Cesium and Thallium

    Directory of Open Access Journals (Sweden)

    Nidhi Sandal


    Full Text Available Background. Prussian blue (PB, ferric hexacyanoferrate is approved by US-FDA for internal decorporation of Cesium-137 (137Cs and Thallium-201 (201Tl. Aim. Since PB is a costly drug, pH-dependent oral delivery system of PB was developed using calcium alginate matrix system. Methods. Alginate (Alg beads containing PB were optimized by gelation of sodium alginate with calcium ions and effect of varying polymer concentration on encapsulation efficiency and release profile was investigated. Scanning electron microscopy (SEM was carried out to study surface morphology. Adsorption efficacy of Alg-PB beads for 201Tl was evaluated and compared with native PB. In vivo pH-dependent release of the formulation was studied in humans using gamma scintigraphy. Results. Encapsulation efficiencies of Alg-PB beads with 0.5, 1.0, 1.5, and 2.0% polymer solution were 99.9, 91, 92, and 93%, respectively. SEM and particle size analysis revealed differences between formulations in their appearance and size distribution. No drug release was seen in acidic media (pH of 1-2 while complete release was observed at pH of 6.8. Dissolution data was fitted to various mathematical models and beads were found to follow Hixson-Crowell mechanism of release. The pH-dependent release of beads was confirmed in vivo by pharmacoscintigraphy in humans.

  8. Replacement of a photomultiplier tube in a 2-inch thallium-doped sodium iodide gamma spectrometer with silicon photomultipliers and a light guide

    Directory of Open Access Journals (Sweden)

    Chankyu Kim


    Full Text Available The thallium-doped sodium iodide [NaI(Tl] scintillation detector is preferred as a gamma spectrometer in many fields because of its general advantages. A silicon photomultiplier (SiPM has recently been developed and its application area has been expanded as an alternative to photomultiplier tubes (PMTs. It has merits such as a low operating voltage, compact size, cheap production cost, and magnetic resonance compatibility. In this study, an array of SiPMs is used to develop an NaI(Tl gamma spectrometer. To maintain detection efficiency, a commercial NaI(Tl 2′ × 2′ scintillator is used, and a light guide is used for the transport and collection of generated photons from the scintillator to the SiPMs without loss. The test light guides were fabricated with polymethyl methacrylate and reflective materials. The gamma spectrometer systems were set up and included light guides. Through a series of measurements, the characteristics of the light guides and the proposed gamma spectrometer were evaluated. Simulation of the light collection was accomplished using the DETECT 97 code (A. Levin, E. Hoskinson, and C. Moison, University of Michigan, USA to analyze the measurement results. The system, which included SiPMs and the light guide, achieved 14.11% full width at half maximum energy resolution at 662 keV.

  9. Myocardial scintigraphy with iodine-123 phenylpentadecanoic acid and thallium-201 in patients with coronary artery disease: a comparative dual-isotope study. (United States)

    Zimmermann, R; Rauch, B; Kapp, M; Bubeck, B; Neumann, F J; Seitz, F; Stokstad, P; Mall, G; Tillmanns, H; Kübler, W


    To characterise the clinical usefulness of serial myocardial scintigraphy with iodine-123 phenylpentadecanoic acid (IPPA) in comparison with thallium-201, dual-isotope investigations were performed in 41 patients with angiographically documented coronary artery disease. Both tracers were administered simultaneously during symptom-limited ergometry. Planar scintigrams were acquired immediately after stress, and delayed imaging was performed after 1 h for IPPA and 4 h for 201Tl. Scintigrams were evaluated both qualitatively and quantitatively using a newly developed algorithm for automated image superposition. Initial myocardial uptake of both tracers was closely correlated (r = 0.75, p or = 75% (IP-PA: 70.0%, 201Tl: 66.3%, P = NS) with identical specificity (69.8%). The number of persistent defects, however, was significantly higher with IPPA (P = 0.021), suggesting that visual analysis of serial IPPA scintigrams may overestimate the presence of myocardial scar tissue. On the other hand, previous Q wave myocardial infarction was associated with a decreased regional IPPA clearance (29% +/- 11% vs 44% +/- 11% in normal myocardium, P IPPA is essentially as sensitive as scintigraphy with 201Tl for the detection of stress-induced perfusion abnormalities. Quantitative analysis of myocardial IPPA kinetics, however, is required for the evaluation of tissue viability.

  10. Dynamic low dose I-123-iodophenylpentadecanoic acid metabolic cardiac imaging; Comparison to myocardial biopsy and reinjection SPECT thallium in ischemic cardiomyopathy and cardiac transplantation

    Energy Technology Data Exchange (ETDEWEB)

    Murray, G.L.; Magill, H.L. [Baptist Memorial Hospital (United States); Schad, N.C.


    Recognition of stunned and hibernating myocardium is essential in this era of cardiac revascularization. Positron emission tomography (PET) accurately identifies viability but is costly and unavailable to most patients. Dynamic low dose I-123-iodophenylpentadecanoic acid (IPPA) metabolic cardiac imaging is a potentially cost-effective alternative to PET. Using transmural myocardial biopsies obtained during coronary bypass surgery as the viability gold standard, resting IPPA imaging agreed with 39/43 (91%) biopsies, with a sensitivity for viability of 33/36(92%) and a specificity of 6/7 (86%) in patients with severe ischemic cardiomyopathy. Eighty percent of IPPA viable, infarcted segments improved wall motion postoperatively. Furthermore, when compared to reinjection thallium (SPECT-Tl) scans after myocardial infarction, there was IPPA-Tl concordance in 27/35 (77%)(Kappa=0.536, p=0.0003). Similar to PET, IPPA demonstrated more viability than SPECT-Tl, 26/35 (74%) vs. 18/35 (51%)(p=0.047). Finally, when compared to transvenous endomyocardial biopsy for detecting rejection following cardiac transplantation, IPPA sensitivity for {>=}Grade II rejection was 100%, and IPPA screening assessment for the necessity of biopsy could result in a 31% cost-savings. Therefore, IPPA metabolic cardiac imaging is a safe, inexpensive technique with a promising future. (author).

  11. Myocardial scintigraphy with iodine-123 phenylpentadecanoic acid and thallium-201 in patients with coronary artery disease: A comparative dual-isotope study

    Energy Technology Data Exchange (ETDEWEB)

    Zimmermann, R.; Rauch, B.; Kapp, M.; Neumann, F.J.; Seitz, F.; Kuebler, W. (Heidelberg Univ. (Germany). Dept. of Cardiology); Bubeck, B. (Heidelberg Univ. (Germany). Dept. of Nuclear Medicine); Mall, G. (Heidelberg Univ. (Germany). Dept. of Pathology); Tillmanns, H. (Giessen Univ. (Germany). Dept. of Cardiology); Stokstad, P.


    To characterise the clinical usefulness of serial myocardial scintigraphy with iodine-123 phenylpentadecanoic acid (IPPA) in comparison with thallium-201, dual-isotope investigations were performed in 41 patients with angiographically documented coronary artery disease. Both tracers were adminstered simultaneously during symptom-limited ergometry. Planar scintigrams were acquired immediately after stress, and delayed imaging was performed after 1 h for IPPA and 4 h for {sup 201}Tl. Scintigrams were evaluated both qualitatively and quantitatively using a newly developed algorithm for automated image superposition. Initial myocardial uptake of both tracers was closely correlated (r=0.75, p<0.001). Both tracers also revealed a similar sensitivity for the identification of individual coronary artery stenoses {>=}75% (IPPA: 70%, {sup 201}Tl: 66.3%, P=NS) with identical specificity (69.8%). The number of persistent defects, however, was significantly higher with IPPA (P=0.021), suggesting that visual analysis of serial IPPA scintigrams may overestimate the presence of myocardial scar tissue. On the other hand, previous Q wave myocardial infarction was associated with a decreased regional IPPA clearance (29%{+-}11% vs 44%{+-}11% in normal myocardium, P<0.05). The data indicate that serial myocardial scintigraphy with IPPA is essentially as sensitive as scintigraphy with {sup 201}Tl for the detection of stress-induced perfusion abnormalities. Quantitative analysis of myocardial IPPA kinetics, however, is required for the evaluation of tissue viability. (orig.).

  12. Myocardial viability assessment with dynamic low-dose iodine-123-iodophenylpentadecanoic acid metabolic imaging: comparison with myocardial biopsy and reinjection SPECT thallium after myocardial infarction. (United States)

    Murray, G L; Schad, N C; Magill, H L; Vander Zwaag, R


    Aggressive cardiac revascularization requires recognition of stunned and hibernating myocardium, and cost considerations may well govern the technique used. Dynamic low-dose (1 mCi) [123I]iodophenylpentadecanoic acid (IPPA) metabolic imaging is a potential alternative to PET using either 18FDG or 15O-water. Resting IPPA images were obtained from patients with severe ischemic cardiomyopathy, and transmural myocardial biopsies were obtained during coronary bypass surgery to confirm viability. Thirty-nine of 43 (91%) biopsies confirmed the results of the IPPA images with a sensitivity for viability of 33/36 (92%) and a specificity of 6/7 (86%). Postoperatively, wall motion improved in 80% of IPPA-viable, dysfunctional segments. Furthermore, when compared to reinjection thallium (SPECT-TI) scans after myocardial infarction, IPPA-SPECT-TI concordance occurred in 27/35 (77%) (K = 0.536, p = 0.0003). Similar to PET, IPPA demonstrated more viability than SPECT-TI, 26/35 (74%) versus 18/35 (51%) (p = 0.047). Metabolic IPPA cardiac viability imaging is a safe, inexpensive technique that may be a useful alternative to PET.

  13. Identification and Decay Studies of New, Neutron-Rich Isotopes of Bismuth, Lead and Thallium by means of a Pulsed Release Element Selective Method

    CERN Multimedia

    Mills, A; Kugler, E; Van duppen, P L E; Lettry, J


    % IS354 \\\\ \\\\ It is proposed to produce, identify and investigate at ISOLDE new, neutron-rich isotopes of bismuth, lead and thallium at the mass numbers A=215 to A=218. A recently tested operation mode of the PS Booster-ISOLDE complex, taking an advantage of the unique pulsed proton beam structure, will be used together with a ThC target in order to increase the selectivity. The decay properties of new nuclides will be studied by means of $\\beta$-, $\\gamma$- and X- ray spectroscopy methods. The expected information on the $\\beta$-half-lives and excited states will be used for testing and developing the nuclear structure models ``south-east'' of $^{208}$Pb, and will provide input data for the description of the r-process path at very heavy nuclei. The proposed study of the yields and the decay properties of those heavy nuclei produced in the spallation of $^{232}$Th by a 1~GeV proton beam contributes also the data necessary for the simulations of a hybrid accelerator-reactor system.

  14. Thallium contamination in arable soils and vegetables around a steel plant-A newly-found significant source of Tl pollution in South China. (United States)

    Liu, Juan; Luo, Xuwen; Wang, Jin; Xiao, Tangfu; Chen, Diyun; Sheng, Guodong; Yin, Meiling; Lippold, Holger; Wang, Chunlin; Chen, Yongheng


    Thallium (Tl) is a highly toxic rare element. Severe Tl poisoning can cause neurological brain damage or even death. The present study was designed to investigate contents of Tl and other associated heavy metals in arable soils and twelve common vegetables cultivated around a steel plant in South China, a newly-found initiator of Tl pollution. Potential health risks of these metals to exposed population via consumption of vegetables were examined by calculating hazard quotients (HQ). The soils showed a significant contamination with Tl at a mean concentration of 1.34 mg/kg. The Tl levels in most vegetables (such as leaf lettuce, chard and pak choy) surpassed the maximum permissible level (0.5 mg/kg) according to the environmental quality standards for food in Germany. Vegetables like leaf lettuce, chard, pak choy, romaine lettuce and Indian beans all exhibited bioconcentration factors (BCF) and transfer factors (TF) for Tl higher than 1, indicating a hyperaccumulation of Tl in these plants. Although the elevated Tl levels in the vegetables at present will not immediately pose significant non-carcinogenic health risks to residents, it highlights the necessity of a permanent monitoring of Tl contamination in the steel-making areas. Copyright © 2017 Elsevier Ltd. All rights reserved.

  15. Thallium-201 is comparable to technetium-99m-sestamibi for estimating cardiac function in patients with abnormal myocardial perfusion imaging

    Directory of Open Access Journals (Sweden)

    Ming-Che Wu


    Full Text Available We analyzed the left-ventricular functional data obtained by cardiac-gated single-photon emission computed tomography myocardial perfusion imaging (MPI with thallium-201 (Tl-201 and technetium-99m-sestamibi (MIBI protocols in different groups of patients, and compared the data between Tl-201 and MIBI. Two hundred and seventy-two patients undergoing dipyridamole stress/redistribution Tl-201 MPI and 563 patients undergoing 1-day rest/dipyridamole stress MIBI MPI were included. Higher mean stress ejection fraction (EF, rest EF, and change in EF (ΔEF were noticed in the normal MPI groups by both Tl-201 and MIBI protocols. Higher mean EF was observed in the females with normal MPI results despite their higher mean age. Comparisons between the Tl-201 and MIBI groups suggested a significant difference in all functional parameters, except for the rest end diastolic volume/end systolic volume and ΔEF between groups with negative MPI results. For the positive MPI groups, there was no significant difference in all parameters, except for the change in end diastolic volume and change in end systolic volume after stress between both protocols. The Tl-201 provides comparable left-ventricular functional data to MIBI cardiac-gated single-photon emission computed tomography in patients with positive MPI results, and may therefore be undertaken routinely for incremental functional information that is especially valuable to this patient group.

  16. Usefulness of thallium-201 myocardial scintigraphy during hyperventilation and accelerated exercise test in patients with vasospastic angina and nearly normal coronary artery

    Energy Technology Data Exchange (ETDEWEB)

    Sueda, Shozo; Mineoi, Kazuaki; Kondou, Tadashi [Takanoko Hospital, Matsuyama, Ehime (Japan)] [and others


    The usefulness of thallium-201 ({sup 201}Tl) myocardial scintigraphy was studied in 109 patients with vasospastic angina who had nearly normal coronary arteries (degree of stenosis <50%). Coronary spasm was confirmed by pharmacologic agents in all 109 patients from January 1991 to June 1996. The appearance rate of visual redistribution on {sup 201}Tl myocardial scintigraphy was compared between four groups, 34 patients performing graded bicycle ergometer exercise starting at a work load of 50 W with increments of 25 W every 3 min (Ergo(3) group), 14 patients performing hyperventilation for 5 min (HV(5) group), 31 patients performing bicycle ergometer exercise with increments of 25 W every 1 min after 5 min hyperventilation (HV(5)+Ergo(1) group), and 30 patients at rest (Rest group). The value of the visual redistribution rate on {sup 201}Tl myocardial scintigrams in the HV(5)+Ergo(l) group (65%) was higher than that in the patients of other groups (Ergo(3) 41%, HV(5) 43%, Rest 33%). However, there were no significant differences between the four groups. Stress {sup 201}Tl imaging after hyperventilation and accelerated exercise is useful to disclose ischemic evidence in about two thirds of patients with vasospastic angina and nearly normal coronary arteries, whereas about 40% of patients had visual redistribution on {sup 201}Tl myocardial scintigrams by performing standard procedures. (author)

  17. On-line preconcentration of ultra-trace thallium(I in water samples with titanium dioxide nanoparticles and determination by graphite furnace atomic absorption spectrometry

    Directory of Open Access Journals (Sweden)

    Saeid Asadpour


    Full Text Available A new method has been developed for the determination of Tl(I based on simultaneous sorption and preconcentration with a microcolumn packed with TiO2 nanoparticle with a high specific surface area prepared by Sonochemical synthesis prior to its determination by graphite furnace atomic absorption spectrometry (GFAAS. The optimum experimental parameters for preconcentration of thallium, such as elution condition, pH, and sample volume and flow rate have been investigated. Tl(I can be quantitatively retained by TiO2 nanoparticles at pH 9.0, then eluted completely with 1.0 mol L−1 HCl. The adsorption capacity of TiO2 nanoparticles for Tl(I was found to be 25 mg g−1. Also detection limit, precision (RSD, n = 8 and enrichment factor for Tl(I were 87 ng L−1, 6.4% and 100, respectively. The method has been applied for the determination of trace amounts of Tl(I in some environmental water samples with satisfactory results.

  18. Thallium-201 single photon emission computed tomography (SPECT) in patients with Duchenne's progressive muscular dystrophy. A histopathologic correlation study

    Energy Technology Data Exchange (ETDEWEB)

    Nishimura, Toru; Yanagisawa, Atsuo; Sakata, Konomi; Shimoyama, Katsuya; Yoshino, Hideaki; Ishikawa, Kyozo [Kyorin Univ., Mitaka, Tokyo (Japan). School of Medicine; Sakata, Hitomi; Ishihara, Tadayuki


    The pathomorphologic mechanism responsible for abnormal perfusion imaging during thallium-201 myocardial single photon emission computed tomography ({sup 201}Tl-SPECT) in patients with Duchenne's progressive muscular dystrophy (DMD) was investigated. Hearts from 7 patients with DMD were evaluated histopathologically at autopsy and the results correlated with findings on initial and delayed resting {sup 201}Tl-SPECT images. The location of segments with perfusion defects correlated with the histopathologically abnormal segments in the hearts. Both the extent and degree of myocardial fibrosis were severe, especially in the posterolateral segment of the left ventricle. Severe transmural fibrosis and severe fatty infiltration were common in segments with perfusion defects. In areas of redistribution, the degree of fibrosis appeared to be greater than in areas of normal perfusion; and intermuscular edema was prominent. Thus, the degree and extent of perfusion defects detected by {sup 201}Tl-SPECT were compatible with the histopathology. The presence of the redistribution phenomenon may indicate ongoing fibrosis. Initial and delayed resting {sup 201}Tl-SPECT images can predict the site and progress of myocardial degeneration in patients with DMD. (author)

  19. Development of magnesium diecasting alloys

    Energy Technology Data Exchange (ETDEWEB)

    King, J.F. (Magnesium Elektron, Manchester (United Kingdom))


    Although there are many fascinating aspects of the development of magnesium diecasting alloys, the volume potential of the automotive industry has always had a major influence on justifying the significant R and D expenditure necessary for this task. Apart from a review of the history of magnesium diecasting alloy development, I would therefore like to focus this presentation on aspects of development specifically relevant to current automotive requirements. (orig.)

  20. Wettability of magnesium based alloys (United States)

    Ornelas, Victor Manuel

    The premise of this project was to determine the wettability behavior of Mg-based alloys using three different liquids. Contact angle measurements were carried out along with utilizing the Zisman method for obtaining values for the critical surface tension. Adhesion energy values were also found through the use of the Young-Dupre equation. This project utilized the Mg-based alloy Mg-2Zn-2Gd with supplemented alpha-Minimum Essential Medium (MEM), Phosphate Buffer Saline solution (PBS), and distilled water. These three liquids are commonly used in cell cultivation and protein adsorption studies. Supplemented alpha-MEM consisted of alpha-MEM, fetal bovine serum, and penicillin-streptomycin. Mg-2Zn-2Gd was used because of observed superior mechanical properties and better corrosion resistance as compared to conventional Mg-alloys. These attractive properties have made it possible for this alloy to be used in biomedical devices within the human body. However, the successful use of this alloy system in the human body requires knowledge in the response of protein adsorption on the alloy surface. Protein adsorption depends on many parameters, but one of the most important factors is the wettability behavior at the surface.

  1. Microstructural studies on Alloy 693

    Energy Technology Data Exchange (ETDEWEB)

    Halder, R.; Dutta, R.S. [Materials Science Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India); Sengupta, P., E-mail: [Materials Science Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India); Samajdar, I. [Dept. of Metall. Engg. and Mater. Sci., Indian Institute of Technology Bombay, Mumbai 400 072 (India); Dey, G.K. [Materials Science Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India)


    Superalloy 693, is a newly identified ‘high-temperature corrosion resistant alloy’. Present study focuses on microstructure and mechanical properties of the alloy prepared by double ‘vacuum melting’ route. In general, the alloy contains ordered Ni{sub 3}Al precipitates distributed within austenitic matrix. M{sub 6}C primary carbide, M{sub 23}C{sub 6} type secondary carbide and NbC particles are also found to be present. Heat treatment of the alloy at 1373 K for 30 min followed by water quenching (WQ) brings about a microstructure that is free from secondary carbides and Ni{sub 3}Al type precipitates but contains primary carbides. Tensile property of Alloy 693 materials was measured with as received and solution annealed (1323 K, 60 min, WQ) and (1373 K, 30 min, WQ) conditions. Yield strength, ultimate tensile strength (UTS) and hardness of the alloy are found to drop with annealing. It is noted that in annealed condition, considerable cold working of the alloy can be performed.

  2. Ni{sub 3}Al aluminide alloys

    Energy Technology Data Exchange (ETDEWEB)

    Liu, C.T.


    This paper provides a brief review of the recent progress in research and development of Ni{sub 3}Al and its alloys. Emphasis has been placed on understanding low ductility and brittle fracture of Ni{sub 3}Al alloys at ambient and elevated temperatures. Recent studies have resulted in identifying both intrinsic and extrinsic factors governing the fracture behavior of Ni{sub 3}Al alloys. Parallel efforts on alloy design using physical metallurgy principles have led to properties for structural use. Industrial interest in these alloys is high, and examples of industrial involvement in processing and utilization of these alloys are briefly mentioned.

  3. Effect of alloy elements on the anti-corrosion properties of low alloy ...

    Indian Academy of Sciences (India)

    Home; Journals; Bulletin of Materials Science; Volume 23; Issue 3. Effect of alloy elements on the anti-corrosion properties of low alloy steel ... Effect of alloy elements on corrosion of low alloy steel was studied under simulated offshore conditions. The results showed that the elements Cu, P, Mo, W, V had evident effect on ...

  4. Iodine-123 phenylpentadecanoic acid and single photon emission computed tomography in identifying left ventricular regional metabolic abnormalities in patients with coronary heart disease: comparison with thallium-201 myocardial tomography. (United States)

    Hansen, C L; Corbett, J R; Pippin, J J; Jansen, D E; Kulkarni, P V; Ugolini, V; Henderson, E; Akers, M; Buja, L M; Parkey, R W


    Iodine-123 phenylpentadecanoic acid (IPPA) is a synthetic long chain fatty acid with myocardial kinetics similar to palmitate. Two hypotheses were tested in this study. The first hypothesis was that IPPA imaging with single photon emission computed tomography (SPECT) is useful in the identification of patients with coronary artery disease. Fourteen normal volunteers (aged 27 +/- 2 years) and 33 patients (aged 54 +/- 11 years) with stable symptomatic coronary artery disease and at least one major coronary artery with luminal diameter narrowing greater than or equal to 70% were studied with symptom-limited maximal exercise testing. The IPPA (6 to 8 mCi) was injected 1 min before the termination of exercise, and tomographic imaging was performed beginning at 9 min and repeated at 40 min after the injection of IPPA. Nine of the normal volunteers and 13 of the patients had a second examination performed at rest on another day. Using the limits of normal as 2 SD from the normal mean values, 27 of the 33 patients with coronary artery disease demonstrated abnormalities in either the initial distribution or the clearance of IPPA, or both. Nineteen of the 33 patients had a maximal variation of activity distribution of greater than or equal to 25% on the 9 min IPPA images. Twenty-two of the 33 patients had a maximal variation in IPPA washout greater than 17% and 17 had a washout rate less than or equal to 2%. There was good agreement between the location of significant coronary artery stenoses and abnormalities in the initial distribution and clearance of IPPA. The second hypothesis tested was that IPPA imaging is as or more sensitive and, therefore, complementary to thallium-201 imaging in the identification of exercise-induced ischemia in patients. Twenty-five of the 33 patients underwent both thallium-201 and IPPA tomographic imaging after symptom-limited maximal exercise testing. The amount of exercise performed by each patient during both studies was similar. Twenty

  5. High strength forgeable tantalum base alloy (United States)

    Buckman, R. W., Jr.


    Increasing tungsten content of tantalum base alloy to 12-15% level will improve high temperature creep properties of existing tantalum base alloys while retaining their excellent fabrication and welding characteristics.

  6. Compensative alloying of Cr-Si low-alloyed steels

    Energy Technology Data Exchange (ETDEWEB)

    Lunika, M., E-mail: [Institute of Applied Physics, National Academy of Science of Ukraine, 58, Petropavlovskaja Str., 40030 Sumy (Ukraine)


    The principle of choosing alloy elements in order to suppress the embrittlement of solid solution strengthening is proposed. In the case of Cr-Si low-alloyed steels, the effects of compensative alloying are studied. The ultimate tensile strength and impact toughness of Cr-Si steels microalloyed with Mo, V, and Ti are determined to prove the aspects. The structure of these steels is studied using optical and transmission electron microscopy techniques after applying the optimum heat treatment. The kinetics of phase transformation after quenching and tempering have been examined by means of measurements of specific electrical resistance and magnetic parameters. It is shown that at the Si-content of about 1 wt% high values of tensile strength and impact toughness are simultaneously obtained. It is established by calculations that, for the indicated steel, long-range distortions of the crystal lattice become close to zero at the Si-content of about 1 wt%.

  7. Luminescent one- and two-dimensional extended structures and a loosely associated dimer based on platinum(II)-thallium(I) backbones. (United States)

    Forniés, Juan; García, Ana; Lalinde, Elena; Moreno, M Teresa


    Neutralization reactions between (NBu4)2[ trans-Pt(C 6F5)2(CN)2] 1 and (NBu4)2[cis-Pt(C6F5)2(CN)2] 2 with TlPF 6 have been carried out, and the resulting structures of [trans,trans,trans-Tl2{Pt(C6F5)2(CN)2}.(CH3COCH3) ] n [4.(CH3COCH3)2] n and {Tl[Tl{cis-Pt(C6F5)2(CN)2}].(H2O)} n [5.(H2O)] n have been determined by X-ray crystallography. Remarkably, the change from trans to cis geometry on the platinum substrate causes a significant decrease in the Pt(II)...Tl(I) metallophilic interaction. Thus, the platinum center in the trans fragment easily connects with two Tl(I) ions forming a distorted pseudo-octahedron PtTl2, which generates a final two-dimensional layered structure by secondary additional intermolecular Tl(I)...N(CN) interactions. However, the [cis-Pt(C6F5)2(CN)2] (2-) fragment interacts strongly with just one Tl center leading to an extended helical [-Pt-Tl-Pt-Tl-] n(n-) chain. In this case, the second thallium center neutralizes the anionic chain mainly through Tl...N(CN) ( intra) and Tl...F(C 6F 5) (intra and inter)actions. The reaction of TlPF 6 with the monoanionic fragment (NBu4)[cis-Pt(C6F5)2(CN)(PPh2C[triple bond]CPh)] 3 yields the discrete associated dimer [Tl{cis-Pt(C6F5)2(CN)(PPh2C[triple bond]CPh)}] 2 [ 6] 2. Dimer [ 6] 2 could be described as two square pyramids with the thallium atoms in the apical positions, connected through Tl...N(cyano) interactions. The final heteropolynuclear Pt-Tl complexes, except 4 at room temperature, show bright emission in the solid state when irradiated with UV-vis radiation, in contrast to the precursors 1 and 3, which are not luminescent. This difference indicates that the emissions in 4- 6 are presumably related to the interaction between the metal centers. The Pt-Tl bonding interactions and, consequently, the emissive properties are lost in solution at room temperature, as shown by the conductivity and NMR measurements. However, variable-concentration luminescence measurements in glassy acetonitrile solutions

  8. Thermomechanical behavior of comercial yellow gold alloy

    Directory of Open Access Journals (Sweden)

    Miloš G. Djordjević


    Full Text Available With the development of science and technology, in the late 19th century, began the research and application of new alloys for making jewelry. By adding different amounts of Cu and Ag alloy of Au, as well as adding some new elements (Zn, alloys were obtained with different color spectrum (from red to yellow and different technological and metallurgical characteristics. This paper aims to show thermomechanical behavior of commercial yellow Au alloys for making jewelry.

  9. Nickel aluminide alloys with improved weldability (United States)

    Santella, M.L.; Goodwin, G.M.


    Weldable nickel aluminide alloys which are essentially free, if not entirely free, of weld hot cracking are provided by employing zirconium concentrations in these alloys of greater than 2.6 wt. % or sufficient to provide a substantial presence of Ni--Zr eutectic phase in the weld so as to prevent weld hot cracking. Weld filler metals formed from these so modified nickel aluminide alloys provide for crack-free welds in previously known nickel aluminide alloys. 5 figs.

  10. Microstructural and technological optimisation of magnesium alloys


    Facchinelli, Nicola


    Magnesium is one of the most abundance element in nature, and it's characterised by a lower density than aluminium. These characteristics confer great potential to magnesium alloys, which are so used for specialised applications, like for military purposes and in the aerospace industry. While some magnesium alloys, including the AM60B alloy, are historically associated to high pressure die casting, for such applications the magnesium alloy components are usually produced by the gravity castin...

  11. New Theoretical Technique for Alloy Design (United States)

    Ferrante, John


    During the last 2 years, there has been a breakthrough in alloy design at the NASA Lewis Research Center. A new semi-empirical theoretical technique for alloys, the BFS Theory (Bozzolo, Ferrante, and Smith), has been used to design alloys on a computer. BFS was used, along with Monte Carlo techniques, to predict the phases of ternary alloys of NiAl with Ti or Cr additions. High concentrations of each additive were used to demonstrate the resulting structures.

  12. Simultaneous dual myocardial imaging with iodine-123-[beta]-methyl iodophenyl-pentadecanoic acid (BMIPP) and thallium-201 in patients with coronary heart disease

    Energy Technology Data Exchange (ETDEWEB)

    Tawarahara, Kei; Kurata, Chinori; Taguchi, Takahisa; Aoshima, Shigeyuki; Okayama, Kenichi; Kobayashi, Akira; Yamazaki, Noboru; Kaneko, Masao (Hamamatsu Univ. School of Medicine, Shizuoka (Japan))


    To assess the clinical value of simultaneous dual myocardial imaging with iodine-123-[beta]-methyl-iodophenyl-pentadecanoic acid ([sup 123]I-BMIPP) and thallium-201 ([sup 201]TL), myocardial imaging was performed at rest and during execise in seven patients with coronary heart disease. When [sup 123]I-BMIPP and [sup 201]Tl images were compared, the initial exercise and resting images agreed 87% and 64%, respectively. In the initial resting images, the regional uptake of [sup 123]I-BMIPP was frequently less than that of [sup 201]Tl. The incidence of exercise-induced reversible defects by [sup 201]Tl in the Tl>BMIPP regions was significantly higher than that in the Tl=BMIPP regions (57% vs 4%, p<0.01) and the incidence of coronary narrowing of more than 90% in the Tl>BMIPP regions was also significantly higher than that in the Tl=BMIPP regions (91% vs 38%, p<0.01). In addition, this disparity (Tl>BMIPP) was found more frequently in regions with abnormal wall motion than in regions with normal wall motion (hypokinetic regions; 68%, severe hypokinetic or akinetic regions; 50%, vs normokinetic regions; 4%, p<0.01). In contrast, the uptake of [sup 123]I-BMIPP correlated closely with that of [sup 201]Tl in normal myocardium and the uptake of both [sup 123]I-BMIPP and [sup 201]Tl was severely reduced in myocardium with severe ischemia during exercise and prior infarction. These results indicate that dual myocardial imaging with [sup 123]I-BMIPP and [sup 201]Tl may provide a unique means of identifying patients with metabolically disturbed myocardium, such as hibernating and stunned myocardium. (author).

  13. Imaging of brain tumors in AIDS patients by means of dual-isotope thallium-201 and technetium-99m sestamibi single-photon emission tomography

    Energy Technology Data Exchange (ETDEWEB)

    De La Pena, R.C.; Ketonen, L.; Villanueva-Meyer, J. [Dept. of Radiology, Univ. of Texas, Galveston (United States)


    Our aim was to evaluate the use of dual-isotope thallium-201 (Tl) and technetium-99m sestamibi (sestamibi) simultaneous acquisition in brain single-photon emission tomography (SPET) for the differentiation between brain lymphoma and benign central nervous system (CNS) lesions in AIDS patients. Thirty-six consecutive patients with enhancing mass lesions on magnetic resonance (MR) imaging were included in the study. SPET of the brain was performed to obtain simultaneous Tl and sestamibi images. Regions-of-interest were drawn around the lesion and on the contralateral side to calculate uptake ratios. The final diagnosis was reached by pathologic findings in 17 patients and clinical and/or MR follow-up in 19 patients. Of the 36 patients, 11 had brain lymphoma, 1 glioblastoma multiforme, 15 toxoplasmosis and 9 other benign CNS lesions. Correlation between SPET and the final diagnosis revealed in 10 true-positive, 23 true-negative, 1 false-positive and 2 false-negative studies. All patients with toxoplasmosis had negative scans. A patient with a purulent infection had positive scans. Tl and sestamibi scans were concordant in every lesion. The same lesions that took up Tl were also visualized with sestamibi. However, sestamibi scans showed higher lesion-to-normal tissue uptake ratios (3.7{+-}1.8) compared with those of Tl (2.3{+-}0.8, P<0.002). Simultaneous acquisition of Tl and sestamibi can help differentiate CNS lymphoma from benign brain lesions in AIDS patients. (orig.) With 2 figs., 2 tabs., 34 refs.

  14. Technetium-99m pyrophosphate/thallium-201 dual-isotope SPECT imaging predicts reperfusion injury in patients with acute myocardial infarction after reperfusion

    Energy Technology Data Exchange (ETDEWEB)

    Akutsu, Yasushi; Kaneko, Kyouichi; Kodama, Yusuke; Li, Hui-Ling; Nishimura, Hideki; Hamazaki, Yuji; Kobayashi, Youichi [Showa University School of Medicine, Division of Cardiology, Department of Medicine, Tokyo (Japan); Suyama, Jumpei; Shinozuka, Akira; Gokan, Takehiko [Showa University School of Medicine, Department of Radiology, Tokyo (Japan)


    Microcirculatory failure after reperfusion is clinically indicated to cause reperfusion injury whereas excessive intracellular calcium ion overload is experimentally proved as a key mechanism of reperfusion injury. We hypothesized that technetium-99m ({sup 99m}Tc) pyrophosphate (Tc-PYP) uptake in injured but viable infarct-related myocardium with preserved myocardial perfusion after reperfusion estimated by thallium-201 ({sup 201}Tl) uptake would be associated with final functional recovery. Dual-isotope Tc-PYP/{sup 201}Tl single-photon emission computed tomography (SPECT) was performed 2 days after successful reperfusion therapy in patients with first acute myocardial infarction, and 50 patients (63 {+-} 13 years old, female 22%) with preserved {sup 201}Tl uptakes of {>=}50% in reperfused myocardium was followed for 1 month. Tc-PYP uptake was assessed as the heart-to-sternum (H/S) ratio. Two-dimensional echocardiography was also performed 2 days and 1 month after reperfusion to evaluate functional recovery. High Tc-PYP uptake, defined as the H/S ratio {>=}0.81, was predictive of chronic phase no functional recovery (73.7% in 14 of 19 patients with high uptake vs 16.1% in five of 31 patients without those, p < 0.0001). After adjustment for potential confounding variables, including electrocardiographic persistent ST segment elevation at 1 h after reperfusion, high Tc-PYP uptake remained independently predictive of no functional recovery with odds ratio of 8.7 (95% confidential interval = 2 to 38.7; p = 0.005). High Tc-PYP uptake in reperfused but viable infarct-related myocardium was a powerful predictor of no functional recovery, which may reflect excessive intracellular calcium ion overload caused by reperfusion injury. Tc-PYP/{sup 201}Tl dual-isotope SPECT imaging can provide prognostic information after reperfusion. (orig.)

  15. Nano-sized Superlattice Clusters Created by Oxygen Ordering in Mechanically Alloyed Fe Alloys


    Yong-Jie Hu; Jing Li; Kristopher A. Darling; William Y. Wang; VanLeeuwen, Brian K.; Xuan L Liu; Kecskes, Laszlo J.; Dickey, Elizabeth C.; Zi-Kui Liu


    Creating and maintaining precipitates coherent with the host matrix, under service conditions is one of the most effective approaches for successful development of alloys for high temperature applications; prominent examples include Ni- and Co-based superalloys and Al alloys. While ferritic alloys are among the most important structural engineering alloys in our society, no reliable coherent precipitates stable at high temperatures have been found for these alloys. Here we report discovery of...


    Moore, R.H.


    A process is given for preparing uranium--aluminum alloys from a solution of uranium halide in an about equimolar molten alkali metal halide-- aluminum halide mixture and excess aluminum. The uranium halide is reduced and the uranium is alloyed with the excess aluminum. The alloy and salt are separated from each other. (AEC)

  17. Corrosion Behaviour of New Zr Alloys

    DEFF Research Database (Denmark)

    Tolksdorf, E.


    Corrosion studies have indicated that the most promising replacements for Zicaloy-2 are ZrCrFe, ZrVFe and probably ZrNbTa, provided they are in their optimized condition. These alloys are conventionally manufactured alloys. An internally oxidized ZrMgO alloy is even superior, from the corrosion...

  18. [Microbiological corrosion of aluminum alloys]. (United States)

    Smirnov, V F; Belov, D V; Sokolova, T N; Kuzina, O V; Kartashov, V R


    Biological corrosion of ADO quality aluminum and aluminum-based construction materials (alloys V65, D16, and D16T) was studied. Thirteen microscopic fungus species and six bacterial species proved to be able to attack aluminum and its alloys. It was found that biocorrosion of metals by microscopic fungi and bacteria was mediated by certain exometabolites. Experiments on biocorrosion of the materials by the microscopic fungus Alternaria alternata, the most active biodegrader, demonstrated that the micromycete attack started with the appearance of exudate with pH 8-9 on end faces of the samples.

  19. Dendritic solidification in binary alloys (United States)

    Chopra, M. A.; Glicksman, M. E.; Singh, N. B.


    Alloys generally solidify dendritically, and associated with that is the microsegregation of impurities. Pure metals also solidify in dendritic form as 'thermal' dendrites, which actually segregate the system's enthalpy. In this investigation, small additions of solute to succinonitrile have been studied and dendritic growth observed in a supercooled melt. This free dendritic growth-mode is similar to that experienced by equiaxed dendrites found in alloy castings. Observations of these free dendrites include measurement of velocity and tip radius of the dendrites at different supercoolings and solute concentrations.


    African Journals Online (AJOL)


    Abstract. Ti-Mo alloy containing Nb and Sn were arc melted and composition analyzed by EDX. The XRD analysis indicates that the crystal structure and mechanical properties are sensitive to Sn concentration. A combination of Sn and Nb elements in synergy hindered formation athermal ω phase and significantly.

  1. An introduction to surface alloying of metals

    CERN Document Server

    Hosmani, Santosh S; Goyal, Rajendra Kumar


    An Introduction to Surface Alloying of Metals aims to serve as a primer to the basic aspects of surface alloying of metals. The book serves to elucidate fundamentals of surface modification and their engineering applications. The book starts with basics of surface alloying and goes on to cover key surface alloying methods, such as carburizing, nitriding, chromizing, duplex treatment, and the characterization of surface layers. The book will prove useful to students at both the undergraduate and graduate levels, as also to researchers and practitioners looking for a quick introduction to surface alloying.


    Gilliland, R.G.; Patriarca, P.; Slaughter, G.M.; Williams, L.C.


    A new and improved ternary alloy is described which is of particular utility in braze-bonding parts made of a refractory metal selected from Group IV, V, and VI of the periodic table and alloys containing said metal as a predominating alloying ingredient. The brazing alloy contains, by weight, 40 to 50 per cent zirconium, 40 to 50 per cent titanium, and the balance beryllium in amounts ranging from 1 to 20 per cent, said alloy having a melting point in the range 950 to 1400 deg C. (AEC)

  3. Assessment of Co-Ga alloys magnetostriction (United States)

    Bormio-Nunes, Cristina; Boccia, Daniel Lourenço Rodrigues; Fulop, Guilherme Origo; Sato-Turtelli, Reiko


    The magnetostriction of Co-Ga alloys: Co-14Ga, Co-24Ga and Co-33Ga (atomic), is studied at room temperature for the first time. All three alloys are ferromagnetic. Co-14Ga microstructure is biphasic, a mixture of ε (hcp) and α (fcc) phases. Co-24Ga presents three phases ε, α and β (ordered bcc) and Co-33Ga is single β phase alloy. It was found that all three alloys present negative saturation magnetostriction λs. The most interesting material for applications would be the alloy Co-33Ga since the magnetostriction saturates for a small field.

  4. Optical Characterization of AlAsSb Digital Alloy and Random Alloy on GaSb

    Directory of Open Access Journals (Sweden)

    Bor-Chau Juang


    Full Text Available III-(As, Sb alloys are building blocks for various advanced optoelectronic devices, but the growth of their ternary or quaternary materials are commonly limited by spontaneous formation of clusters and phase separations during alloying. Recently, digital alloy growth by molecular beam epitaxy has been widely adopted in preference to conventional random alloy growth because of the extra degree of control offered by the ordered alloying. In this article, we provide a comparative study of the optical characteristics of AlAsSb alloys grown lattice-matched to GaSb using both techniques. The sample grown by digital alloy technique showed stronger photoluminescence intensity, narrower peak linewidth, and larger carrier activation energy than the random alloy technique, indicating an improved optical quality with lower density of non-radiative recombination centers. In addition, a relatively long carrier lifetime was observed from the digital alloy sample, consistent with the results obtained from the photoluminescence study.

  5. Aeronautical Industry Requirements for Titanium Alloys (United States)

    Bran, D. T.; Elefterie, C. F.; Ghiban, B.


    The project presents the requirements imposed for aviation components made from Titanium based alloys. A significant portion of the aircraft pylons are manufactured from Titanium alloys. Strength, weight, and reliability are the primary factors to consider in aircraft structures. These factors determine the requirements to be met by any material used to construct or repair the aircraft. Many forces and structural stresses act on an aircraft when it is flying and when it is static and this thesis describes environmental factors, conditions of external aggression, mechanical characteristics and loadings that must be satisfied simultaneously by a Ti-based alloy, compared to other classes of aviation alloys (as egg. Inconel super alloys, Aluminum alloys).For this alloy class, the requirements are regarding strength to weight ratio, reliability, corrosion resistance, thermal expansion and so on. These characteristics additionally continue to provide new opportunities for advanced manufacturing methods.

  6. Aqueous recovery of actinides from aluminum alloys

    Energy Technology Data Exchange (ETDEWEB)

    Gray, J.H.; Chostner, D.F.; Gray, L.W.


    Early in the 1980's, a joint Rocky Flats/Savannah River program was established to recover actinides from scraps and residues generated during Rocky Flats purification operations. The initial program involved pyrochemical treatment of Molten Salt Extraction (MSE) chloride salts and Electrorefining (ER) anode heel metal to form aluminum alloys suitable for aqueous processing at Savannah River. Recently Rocky Flats has expressed interest in expanding the aluminum alloy program to include treatment of chloride salt residues from a modified Molten Salt Extraction process and from the Electrorefining purification operations. Samples of the current aluminum alloy buttons were prepared at Rocky Flats and sent to Savannah River Laboratory for flowsheet development and characterization of the alloys. A summary of the scrub alloy-anode heel alloy program will be presented along with recent results from aqueous dissolution studies of the new aluminum alloys. 2 figs., 4 tabs.

  7. [Fatigue properties of dental alloys. 12% Au-Pd-Ag alloy and type III gold alloy]. (United States)

    Kato, H


    Usually the mechanical properties of dental alloys are determined from the values obtained through static tests of their tensile strength, hardness, etc. Generally, high tensile strength and ductility are preferred. However, when small stresses within proportional limits are applied repeatedly (even though not amounting to destructive forces in static tests), they may cause rupture in the alloy or, at least, cause it to lose its original mechanical properties. This phenomenon is called metal fatigue. It is estimated that the intraoral stress loads received by dental restorations during mastication or during insertion and removal of appliances are repeated more than 3 x 10(5) times/year. From this standpoint, it may be more appropriate to estimate the fracture strength of such dental alloys based on the fatigue properties of the restorative materials used for clasps, bars, and fixed bridges. For this reason, it is necessary to obtain data through fatigue tests on the fatigue strength and the fatigue endurance limits of dental alloys, and it is important to find a correlation between these data and the static data on tensile strengths and ductility obtained by tensile tests. Two alloys are used in these experiments. Both wrought specimens and cast specimens of 12% Au-Pd-Ag and Type III gold alloy were prepared for the fatigue tests. The size of the rectangular wrought specimens was 3 x 4 x 110 mm. The 12% Au-Pd-Ag alloy was heated to 800 degrees C for 15 minutes, quenched, and reheated to 400 degrees C for 20 minutes and quenched again according to the manufacturer's instructions for heat treatment. The Type III gold alloy was heated to 700 degrees C for 10 minutes, quenched, and reheated to 350 degrees C for 20 minutes and quenched again. The cylindrical cast specimens were 60 mm long and 2 mm in diameter. They were invested by conventional methods and cast in a centrifugal casting machine, Thermotrol Model 2500. The four point bending test for the wrought specimen

  8. Nickel, cobalt, and their alloys

    CERN Document Server


    This book is a comprehensive guide to the compositions, properties, processing, performance, and applications of nickel, cobalt, and their alloys. It includes all of the essential information contained in the ASM Handbook series, as well as new or updated coverage in many areas in the nickel, cobalt, and related industries.

  9. Hydrostatic extrusion of magnesium alloys

    NARCIS (Netherlands)

    Sillekens, W.H.; Bohlen, J.


    This chapter deals with the capabilities and limitations of the hydrostatic extrusion process for the manufacturing of magnesium alloy sections. Firstly, the process basics for the hydrostatic extrusion of materials in general and of magnesium in particular are introduced. Next, some recent research

  10. Relative value of thallium-201 and iodine-131 scans in the detection of recurrence or distant metastasis of well differentiated thyroid carcinoma. (United States)

    Lin, J D; Kao, P F; Weng, H F; Lu, W T; Huang, M J


    Radioactive iodine (131I) has been found to be more sensitive and more specific than thallium-201 for the detection of distant metastases and thyroid remnants in the neck in cases of well-differentiated thyroid carcinoma. 201Tl has been deemed particularly useful in localizing metastases or recurrence in patients with a negative 131I scan and abnormal levels of serum thyroglobulin (Tg). This study aimed to: (1) determine the value of 201Tl imaging in localizing metastases or recurrence in patients with well-differentiated thyroid carcinoma, and (2) evaluate the false-positive and false-negative results of 131I and 201Tl scintigraphy. Sixty-two thyroid remnant ablated patients who underwent simultaneous postoperative 201Tl and 131I scans and and serum Tg determinations were evaluated. Fifty patients had papillary thyroid carcinomas and 12 had follicular thyroid carcinomas. 201Tl imaging was performed before the 131I studies. Of the 62 patients who underwent 201Tl imaging studies, 24 were found to have positive results, with local recurrence or distant metastases. Patients with positive results in the 201Tl imaging studies tended to be older, were mor often male, had higher Tg levels and had a higher recurrence rate. Of these 24 patients, ten had negative diagnostic or therapeutic 131I scans. Concurrently, serum Tg levels were less than 5 ng/ml in five of these ten patients. Three patients were deemed false positive by 201Tl scans; one had a parotid tumour, one a periodontal abscess and one lung metastasis. Among the 38 patients with negative 201Tl scans, 11 had positive findings on 131I scans. Three had distant metastases: two with lung metastases and one with bone metastases. Patients with false-positive results on 131I scans included those with biliary tract stones, ovarian cysts, and breast secretion. Of the 27 patients with negative 201Tl and 131I scans, 15 had elevated serum Tg levels. Among these, local recurrence followed by lung metastases was manifested in

  11. MRI and thallium features of pigmented villonodular synovitis and giant cell tumours of tendon sheaths: a retrospective single centre study of imaging and literature review. (United States)

    Lynskey, Samuel J; Pianta, Marcus J


    The purpose of this study was to characterize the MRI and thallium-201 ((201)TI) scintigraphy attributes of pigmented villonodular synovitis (PVNS) and giant cell tumours of tendon sheaths (GCTTS). The epidemiology of these uncommon lesions was also assessed and less commonly encountered pathology reported on including multifocality, necrosis and concurrent malignancy. A retrospective single centre review of MRI and (201)TI scintigraphy findings for 83 surgically proven or biopsy-proven consecutive cases of PVNS was undertaken. Radiological findings including lesion size, (201)TI uptake (as a marker of metabolic activity), location, extent and patient demographics were correlated with biopsy and surgical specimen histology. Typical appearances are described, as well as less common imaging manifestations. The study period encompassed all patients presenting or referred to a tertiary bone and soft-tissue tumour referral centre with PVNS or GCTTS between 1 January 2007 and the 1 December 2013. Lesions occur most commonly around the knee joint in the fourth decade of life, with younger patients showing a tendency to occur in the hip. Features of PVNS and GTTS include bone erosion, ligamentous and cartilage replacement, muscle infiltration and multifocality. MR signal characteristics were variable but post-contrast enhancement was near-universal. 14 of 83 cases showed no uptake of (201)TI and revealed a statistically significant smaller average axial dimension of 19.8 mm than lesions displaying active (201)TI uptake of 36.4 mm, p = 0.016. Four lesions demonstrated central necrosis on gross histology, two of each from both the (201)TI-avid and (201)TI-non-avid groups. MR is the imaging modality of choice when considering the diagnosis of these uncommon tumours. (201)TI scintigraphy as a marker of metabolic activity further adds minimal value although small lesions can appear to lack (201)TI avidity. This article depicts typical imaging findings of PVNS/GCTTS and

  12. Relative value of thallium-201 and iodine-131 scans in the detection of recurrence or distant metastasis of well differentiated thyroid carcinoma

    Energy Technology Data Exchange (ETDEWEB)

    Lin Jen-Der; Weng Hsiao-Fen; Lu Wen-Tsoung [Division of Endocrinology and Metabolism, Chang Gung Memorial Hospital (Taiwan, Province of China); Kao Pan-Fu; Huang Miau-Ju [Department of Nuclear Medicine, Chang Gung Memorial Hospital, Taiwan (Taiwan, Province of China)


    Radioactive iodine ({sup 131}I) has been found to be more sensitive and more specific than thallium-201 for the detection of distant metastases and thyroid remnants in the neck in cases of well-differentiated thyroid carcinoma. {sup 201}Tl has been deemed particularly useful in localizing metastases or recurrence in patients with a negative {sup 131}I scan and abnormal levels of serum thyroglobulin (Tg). This study aimed to: (1) determine the value of {sup 201}Tl imaging in localizing metastases or recurrence in patients with well-differentiated thyroid carcinoma, and (2) evaluate the false-positive and false-negative results of {sup 131}I and {sup 201}Tl scintigraphy. Sixty-two thyroid remnant ablated patients who underwent simultaneous postoperative {sup 201}Tl and {sup 131}I scans and and serum Tg determinations were evaluated. Fifty patients had papillary thyroid carcinomas and 12 had follicular thyroid carcinomas. {sup 201}Tl imaging was performed before the {sup 131}I studies. Of the 62 patients who underwent {sup 201}Tl imaging studies, 24 were found to have positive results, with local recurrence or distant metastases. Patients with positive results in the {sup 201}Tl imaging studies tended to be older, were mor often male, had higher Tg levels and had a higher recurrence rate. Of these 24 patients, ten had negative diagnostic or therapeutic {sup 131}I scans. Concurrently, serum Tg levels were less than 5 ng/ml in five of these ten patients. Three patients were deemed false positive by {sup 201}Tl scans; one had a parotid tumour, one a periodontal abscess and one lung metastasis. Among the 38 patients with negative {sup 201}Tl scans, 11 had positive findings on {sup 131}I scans. Three had distant metastases: two with lung metastases and one with bone metastases. Patients with false-positive results on {sup 131}I scans included those with biliary tract stones, ovarian cysts, and breast secretion. Of the 27 patients with negative {sup 201}Tl and {sup 131}I

  13. Effects of adenosine and a selective A2A adenosine receptor agonist on hemodynamic and thallium-201 and technetium-99m-sestaMIBI biodistribution and kinetics. (United States)

    Mekkaoui, Choukri; Jadbabaie, Farid; Dione, Donald P; Meoli, David F; Purushothaman, Kailasnath; Belardinelli, Luiz; Sinusas, Albert J


    The purpose of this study was to compare a selective A(2A) adenosine receptor agonist (regadenoson) with adenosine in clinically relevant canine models with regard to effects on hemodynamics and thallium-201 ((201)Tl) and technetium-99m ((99m)Tc)-sestaMIBI biodistribution and kinetics. The clinical application of vasodilator stress for perfusion imaging requires consideration of the effects of these vasodilating agents on systemic hemodynamics, coronary flow, and radiotracer uptake and clearance kinetics. Sequential imaging and arterial blood sampling was performed on control, anesthetized closed-chest canines (n = 7) to evaluate radiotracer biodistribution and kinetics after either a bolus administration of regadenoson (2.5 microg/kg) or 4.5-min infusion of adenosine (280 microg/kg). The effects of regadenoson on coronary flow and myocardial radiotracer uptake were then evaluated in an open-chest canine model of a critical stenosis (n = 7). Results from ex vivo single-photon emission computed tomography were compared with tissue well-counting. The use of regadenoson compared favorably with adenosine in regard to the duration and magnitude of the hemodynamic effects and the effect on (201)Tl and (99m)Tc-sestaMIBI biodistribution and kinetics. The arterial blood clearance half-time was significantly faster for (99m)Tc-sestaMIBI (regadenoson: 1.4 +/- 0.03 min; adenosine: 1.5 +/- 0.08 min) than for (201)Tl (regadenoson: 2.5 +/- 0.16 min, p adenosine: 2.7 +/- 0.04 min, p regadenoson stress was significantly greater than the relative perfusion defect with (99m)Tc-sestaMIBI (0.69 +/- 0.03%, p regadenoson produced a hyperemic response comparable to a standard infusion of adenosine. The biodistribution and clearance of both (201)Tl and (99m)Tc-sestaMIBI during regadenoson were similar to adenosine vasodilation. Ex vivo perfusion images under the most ideal conditions permitted detection of a critical stenosis, although (201)Tl offered significant advantages over (99m

  14. Comparison of 8-frame and 16-frame thallium-201 gated myocardial perfusion SPECT for determining left ventricular systolic and diastolic parameters. (United States)

    Kurisu, Satoshi; Sumimoto, Yoji; Ikenaga, Hiroki; Watanabe, Noriaki; Ishibashi, Ken; Dohi, Yoshihiro; Fukuda, Yukihiro; Kihara, Yasuki


    The myocardial perfusion single photon emission computed tomography synchronized with the electrocardiogram (gated SPECT) has been widely used for the assessment of left ventricular (LV) systolic and diastolic functions using Quantitative gated SPECT. The aim of this study was to compare the effects of 8-frame and 16-frame thallium-201 (Tl-201) gated SPECT for determining LV systolic and diastolic parameters. The study population included 42 patients with suspected coronary artery disease who underwent gated SPECT by clinical indication. LV systolic and diastolic parameters were assessed on 8-frame and 16-frame gated SPECT. There were good correlations in end-diastolic volume (r = 0.99, p < 0.001), end-systolic volume (ESV) (r = 0.97, p < 0.001) and ejection fraction (EF) (r = 0.95, p < 0.001) between 8-frame and 16-frame gated SPECT. Bland-Altman plot showed a significant negative slope of -0.08 in EDV indicating a larger difference for larger EDV. Eight-frame gated SPECT overestimated ESV by 2.3 ml, and underestimated EF by -4.2% than 16-frame gated SPECT. There were good correlations in peak filling rate (PFR) (r = 0.87, p < 0.001), one third mean filling rate (r = 0.87, p < 0.001) and time to PFR (r = 0.61, p < 0.001) between 8-frame and 16-frame gated SPECT. Eight-frame gated SPECT underestimated PFR by -0.22 than 16-frame gated SPECT. Eight-frame gated SPECT estimated as much MFR/3 and TPFR as 16-frame gated SPECT. According to the data, the study suggested that 8-frame Tl-201 gated SPECT could underestimate systolic and/or diastolic parameter when compared with 16-frame gated SPECT.


    Directory of Open Access Journals (Sweden)

    A. G. Slutsky


    Full Text Available Motor is one of most important part of automobile determine its economical effectiveness of usage. On the other hand, sleeves, pistons and rings are crucible parts as they determine the service life of a motor. These parts are producing in big scale – dozens of millions pieces. Increase of cylinder sleeves physical-mechanical properties results in prolongation of motor service life and improvement of motor’s characteristics. Nowadays low alloyed cast irons with perlite structure are used to manufacture motor’s sleeves. For alloying purposes such traditional elements as Cr, Ni, Cu, and V are applied. But it is interesting to use molybdenum for cast iron alloying. It is known that alloying of alloys allows considerable increasing of consumption properties of castings. But in spite of advantages of alloys alloying the increase of molybdenum containing iron-carbon alloys production is restricted by economical reasons – high cost of alloying additions. Expenditures on alloying additions can be reduced by the application cheap secondary alloys in the charge. So, the present paper is devoted to investigation of alloying peculiarities during the treatment of ferrous alloys with molybdenum applying different initial materials.

  16. The Examination of the Aluminum Alloy 7017 as a Replacement for the Aluminum Alloy 7039 in Lightweight Armor Systems (United States)


    Aluminum Alloy 7017 as a Replacement for the Aluminum ...2016 US Army Research Laboratory The Examination of the Aluminum Alloy 7017 as a Replacement for the Aluminum Alloy 7039 in Lightweight Armor... Aluminum Alloy 7017 as a Replacement for the Aluminum Alloy 7039 in Lightweight Armor Systems 5a. CONTRACT NUMBER 5b. GRANT NUMBER 5c.

  17. Status of Testing and Characterization of CMS Alloy 617 and Alloy 230

    Energy Technology Data Exchange (ETDEWEB)

    Ren, Weiju [ORNL; Santella, Michael L [ORNL; Battiste, Rick [ORNL; Terry, Totemeier [Idaho National Laboratory (INL); Denis, Clark [Idaho National Laboratory (INL)


    Status and progress in testing and characterizing CMS Alloy 617 and Alloy 230 tasks in FY06 at ORNL and INL are described. ORNL research has focused on CMS Alloy 617 development and creep and tensile properties of both alloys. In addition to refurbishing facilities to conduct tests, a significant amount of creep and tensile data on Alloy 230, worth several years of research funds and time, has been located and collected from private enterprise. INL research has focused on the creep-fatigue behavior of standard chemistry Alloy 617 base metal and fusion weldments. Creep-fatigue tests have been performed in air, vacuum, and purified Ar environments at 800 and 1000 C. Initial characterization and high-temperature joining work has also been performed on Alloy 230 and CCA Alloy 617 in preparation for creep-fatigue testing.

  18. Effects of segregation of primary alloying elements on the creep response in magnesium alloys

    DEFF Research Database (Denmark)

    Huang, Y.D.; Dieringa, H.; Hort, N.


    The segregation of primary alloying elements deteriorates the high temperature creep resistance of magnesium alloys. Annealing at high temperatures alleviating their segregations can improve the creep resistance. Present investigation on the effect of segregation of primary alloying elements...... on the creep response may provide some useful information about how to improve the creep resistance of magnesium alloys in the future. (c) 2008 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved....

  19. The Influence of Novel Alloying Additions on the Performance of Magnesium Alloy AZ31B (United States)


    alloys are based on a rather small group of alloying elements, there are often limited differences between them in properties (strength, corrosion...the first year of the project. 2. Introduction To date, the majority of Mg alloys have used a rather small group of alloying elements (such as...and subsequently processed using Equal Channel Angular Extrusion ( ECAE ) in an attempt to obtain ultra-fine-grained samples. Detailed evaluation of

  20. Bulk amorphous Mg-based alloys

    DEFF Research Database (Denmark)

    Pryds, Nini


    and a low glass transition temperature. The alloys were prepared by using a relatively simple technique, i.e. rapid cooling of the melt in a copper wedge mould. The essential structural changes that are achieved by going from the amorphous to the crystalline state through the supercooled liquid state...... are discussed in this paper. On the basis of these measurements phase diagrams of the different systems were constructed. Finally, it is demonstrated that when pressing the bulk amorphous alloy onto a metallic dies at temperatures within the supercooled liquid region, the alloy faithfully replicates the surface......The present paper describes the preparation and properties of bulk amorphous quarternary Mg-based alloys and the influence of additional elements on the ability of the alloy to form bulk amorphous. The main goal is to find a Mg-based alloy system which shows both high strength to weight ratio...

  1. Theory of Random Anisotropic Magnetic Alloys

    DEFF Research Database (Denmark)

    Lindgård, Per-Anker


    A mean-field-crystal-field theory is developed for random, multicomponent, anisotropic magnetic alloys. It is specially applicable to rare-earth alloys. A discussion is given of multicritical points and phase transitions between various states characterized by order parameters with different...... spatial directions or different ordering wave vectors. Theoretical predictions based on known parameters for the phase diagrams and magnetic moments for the binary rare-earth alloys of Tb, Dy, Ho, and Er, Tb-Tm, Nd-Pr, and pure double-hcp Nd agree qualitatively with the experimental observations....... Quantitative agreement can be obtained by increasing the interaction between different alloy elements, in particular for alloys with very different axial anisotropy, e.g., Tb-Tm. A model system consisting of a singlet-singlet and singlet-doublet alloy is discussed in detail. A simple procedure to include...

  2. Magnetism of quaternary Heusler alloys

    Energy Technology Data Exchange (ETDEWEB)

    Kudrnovsky, Josef; Drchal, Vaclav [Institute of Physics, AS CR, Prague (Czech Republic); Bose, Shyamal [Brock University, St. Catharines (Canada); Turek, Ilja [Institute of Physics of Materials, AS CR, Brno (Czech Republic)


    The electronic properties, exchange interactions, finite-temperature magnetism and transport properties of random Ni{sub 2}MnSn quaternary Heusler alloys doped with Cu- and Pd-atoms are studied theoretically by means of first-principles calculations over the entire concentration range. While the magnetic moments are only weakly dependent on the alloy composition, the Curie temperatures exhibit strongly non-linear behavior with respect to Cu-doping in contrast with an almost linear concentration dependence in the case of Pd-doping. The residual resistivity obey the Nordheim rule while the dominating contribution to the temperature-dependent resistivity is due to thermodynamical fluctuations originating from the spin-disorder, which, according to our calculations, can be described reasonably well via the disordered local moments model. The present parameter-free theory agrees qualitatively and also reasonably well quantitatively with all available experiments.

  3. Digital Alloy Absorber for Photodetectors (United States)

    Hill, Cory J. (Inventor); Ting, David Z. (Inventor); Gunapala, Sarath D. (Inventor)


    In order to increase the spectral response range and improve the mobility of the photo-generated carriers (e.g. in an nBn photodetector), a digital alloy absorber may be employed by embedding one (or fraction thereof) to several monolayers of a semiconductor material (insert layers) periodically into a different host semiconductor material of the absorber layer. The semiconductor material of the insert layer and the host semiconductor materials may have lattice constants that are substantially mismatched. For example, this may performed by periodically embedding monolayers of InSb into an InAsSb host as the absorption region to extend the cutoff wavelength of InAsSb photodetectors, such as InAsSb based nBn devices. The described technique allows for simultaneous control of alloy composition and net strain, which are both key parameters for the photodetector operation.


    Moore, R.H.


    BS>A process is given for preparing alloys of aluminum with plutonium, uranium, and/or thorium by chlorinating actinide oxide dissolved in molten alkali metal chloride with hydrochloric acid, chlorine, and/or phosgene, adding aluminum metal, and passing air and/or water vapor through the mass. Actinide metal is formed and alloyed with the aluminum. After cooling to solidification, the alloy is separated from the salt. (AEC)

  5. Aspects of precipitation in alloy Inconel 718


    Azadian, Saied


    A study was made of the microstructure of the Ni-base alloy Inconel 718 with emphasis on the precipitation and stability of intermetallic phases as affected by heat treatments. In addition the effect of the precipitation on selected mechanical properties namely hardness, creep notch sensitivity and hot ductlity were investigated. The materials studied were a spray-formed version and three wrought versions of the alloy. The spray-formed version of the alloy was of interest since it exhibited a...

  6. Research and Development on Titanium Alloys (United States)


    61 No. 733 LWE: ec/mk/ma September 14, 1949 13ATTK- LLE MESMORIAL INSTITUTE DEPARTMENT OF THE AIR FORCE HEADOUARTERS AERONAUTICAL SYSTEMS CENTER (AFMC...period reported, titanium binary alloys of germanium and nickel vere studied, as venl as tltanium-molybdenum and titanium- manganese ternary alloys. Carbon...September 18, 1949, titanium binary alloys of germanium and nickel were studied. Also investigated were titanium-molybdenum and titanium-manganese ternary

  7. Low-Gold-Content Brazing Alloys (United States)

    Brennan, A.; Mckown, R. D.


    Two new alloys for brazing at 1,760 degrees to 1,850 degrees F are stronger and have better gap-filling capability. Alloys have lower gold content than other gold brazes for their temperature range and therefore are far less expensive. They are produced in wire, foil, and powder and are excellent for brazing at temperatures where no suitable alloys existed--especially for step brazing copper.

  8. Alloy nanoparticle synthesis using ionizing radiation (United States)

    Nenoff, Tina M [Sandia Park, NM; Powers, Dana A [Albuquerque, NM; Zhang, Zhenyuan [Durham, NC


    A method of forming stable nanoparticles comprising substantially uniform alloys of metals. A high dose of ionizing radiation is used to generate high concentrations of solvated electrons and optionally radical reducing species that rapidly reduce a mixture of metal ion source species to form alloy nanoparticles. The method can make uniform alloy nanoparticles from normally immiscible metals by overcoming the thermodynamic limitations that would preferentially produce core-shell nanoparticles.

  9. Advanced powder metallurgy aluminum alloys and composites (United States)

    Lisagor, W. B.; Stein, B. A.


    The differences between powder and ingot metallurgy processing of aluminum alloys are outlined. The potential payoff in the use of advanced powder metallurgy (PM) aluminum alloys in future transport aircraft is indicated. The national program to bring this technology to commercial fruition and the NASA Langley Research Center role in this program are briefly outlined. Some initial results of research in 2000-series PM alloys and composites that highlight the property improvements possible are given.

  10. Deformation Driven Alloying and Transformation (United States)


    1991;15:317. [69] Watson A, Hayes F. J Alloys Compd 2001;320:199. [70] Ohtake M, Nonaka Y, Futamoto M. IEEE Trans Magn 2012;48:1589. [71] Heinrich B...Hahn H, Averback R, Bellon P. Phys.Rev. B 2012;86:144302. [77] Bellon P, Averback RS. Phys. Rev. Lett. 1995;74:1819. 28 [78] Takeuchi A, Inoue

  11. Brazing Alloys Indicate Turbomachinery Temperatures (United States)

    Schlaff, J. W.


    Foils serve as consumable thermometers. Stainless-steel tab with circular window holds brazing-foil sample in place. Tab tacked to object to be tested with capacitive-discharge spot welder operating in range 10 + 1 joules. After measurements, tabs and samples chiseled off, leaving tested object fairly well intact. Technique used on objects made of alloys with iron, nickel, or cobalt as principal ingredients.

  12. Electrodeposition of engineering alloy coatings

    DEFF Research Database (Denmark)

    Christoffersen, Lasse

    Nickel based electrodeposited alloys were investigated with respect to their deposition process, heat treatment, hardness, corrosion resistance and combined wear-corrosion resistance. The investigated alloys were Ni-B, Ni-P and Ni-W, which are not fully developed for industrial utilisation...... are written in brackets). Temperature and especially pH influenced the cathodic efficiency of the electrodeposition processes for Ni-W and Ni-P. Mass balance problems of the development alloy processes are identified.Heat treatment for one hour at approx. 350°C, 400°C and 600°C of electrodeposited Ni-B, Ni......-P and Ni-W, respectively, resulted in hardness values of approx. 1000 HV0.1 in the case of Ni-P(6), approx. 1100 HV0.1 in the case of Ni-W(40-53) and approx. 1300 HV0.1 in the case of Ni-B(5). Cracks, which emerged during electrodeposition and heat treatment, were observed on Ni-W and Ni-B.The corrosion...

  13. Pack cementation coatings for alloys

    Energy Technology Data Exchange (ETDEWEB)

    He, Yi-Rong; Zheng, Minhui; Rapp, R.A. [Ohio State Univ., Columbus, OH (United States)


    The halide-activated pack cementation process was modified to produce a Ge-doped silicide diffusion coating on a Cr-Cr{sub 2}Nb alloy in a single processing step. The morphology and composition of the coating depended both on the composition of the pack and on the composition and microstructure of the substrate. Higher Ge content in the pack suppressed the formation of CrSi{sub 2} and reduced the growth kinetics of the coating. Ge was not homogeneously distributed in the coatings. In cyclic and isothermal oxidation in air at 700 and 1050{degrees}C, the Ge-doped silicide coating protected the Cr-Nb alloys from significant oxidation by the formation of a Ge-doped silica film. The codeposition and diffusion of aluminum and chromium into low alloy steel have been achieved using elemental Al and Cr powders and a two-step pack cementation process. Sequential process treatments at 925{degrees}C and 1150{degrees}C yield dense and uniform ferrite coatings, whose compositions are close to either Fe{sub 3}Al or else FeAl plus a lower Cr content, when processed under different conditions. The higher content of Al in the coatings was predicted by thermodynamic calculations of equilibrium in the gas phase. The effect of the particle size of the metal powders on the surface composition of the coating has been studied for various combinations of Al and Cr powders.

  14. Mechanically alloyed aluminum metal matrix composites (United States)

    Hashiguchi, Don; Tricker, David; Tarrant, Andrew


    Aluminum alloys reinforced with ceramic particles produce a low density metal matrix composite (MMC) with enhanced mechanical and physical properties including relatively high modulus and vibration loss. This paper will outline the capability through Powder Metallurgy processing techniques made by mechanical alloying (MA). MA enables production of MMC's with micron to submicron mean particulate reinforcement size which increases mechanical properties in comparison to larger reinforcement particle size. Smaller reinforcement particles also result in a material that fits well within established value streams enabling conventional post consolidation metalworking and machining methods. The microstructure and properties of MMC's mechanical alloyed with base aluminum alloys 6061B and 2124A will be presented.

  15. Titanium alloys Russian aircraft and aerospace applications

    CERN Document Server

    Moiseyev, Valentin N


    This text offers previously elusive information on state-of-the-art Russian metallurgic technology of titanium alloys. It details their physical, mechanical, and technological properties, as well as treatments and applications in various branches of modern industry, particularly aircraft and aerospace construction. Titanium Alloys: Russian Aircraft and Aerospace Applications addresses all facets of titanium alloys in aerospace and aviation technology, including specific applications, fundamentals, composition, and properties of commercial alloys. It is useful for all students and researchers interested in the investigation and applications of titanium.

  16. Casting Characteristics of Aluminum Die Casting Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Makhlouf M. Makhlouf; Diran Apelian


    The research program investigates the casting characteristics of selected aluminum die casting alloys. Specifically, the alloys' tendencies towards die soldering and sludge formation, and the alloys' fluidity and machinability are evaluated. It was found that: When the Fe and Mn contents of the alloy are low; caution has to be taken against possible die soldering. When the alloy has a high sludge factor, particularly a high level of Fe, measures must be taken to prevent the formation of large hardspots. For this kind of alloy, the Fe content should be kept at its lowest allowable level and the Mn content should be at its highest possible level. If there are problems in die filling, measures other than changing the alloy chemistry need to be considered first. In terms of alloy chemistry, the elements that form high temperature compounds must be kept at their lowest allowable levels. The alloys should not have machining problems when appropriate machining techniques and machining parameters are used.

  17. Barocaloric effect in metamagnetic shape memory alloys

    Energy Technology Data Exchange (ETDEWEB)

    Manosa, Lluis; Stern-Taulats, Enric; Planes, Antoni [Facultat de Fisica, Departament d' Estructura i Constituents de la Materia, Universitat de Barcelona (Spain); Lloveras, Pol; Barrio, Maria; Tamarit, Josep-Lluis [Departament de Fisica i Enginyeria Nuclear, ETSEIB, Universitat Politecnica de Catalunya, Barcelona (Spain); Emre, Baris [Faculty of Engineering, Department of Engineering Physics, Ankara University (Turkey); Yuece, Suheyla [Department of Physics, Science and Literature Faculty, Ondokuz Mayis University, Samsun (Turkey); Fabbrici, Simone [MIST E-R Laboratory, Bologna (Italy); IMEM-CNR, Parma (Italy); Albertini, Franca [IMEM-CNR, Parma (Italy)


    We report on calorimetric measurements under hydrostatic pressure in a series of composition related metamagnetic shape memory alloys. We show that metamagnetic shape memory alloys exhibit a barocaloric effect whose magnitude compares well to the magnetocaloric effect exhibited by this kind of alloys. While in metamagnetic alloys the magnetocaloric effect is inverse, the barocaloric effect has been found to be conventional. The values obtained for the pressure-induced entropy changes at moderate pressures are in the range of those reported for giant caloric materials. (copyright 2014 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  18. Thermally activated martensite formation in ferrous alloys

    DEFF Research Database (Denmark)

    Villa, Matteo; Somers, Marcel A. J.


    Magnetometry was applied to investigate the formation of α/α´martensite in 13ferrous alloys during immersion in boiling nitrogen and during re-heating to room temperature at controlled heating rates in the range 0.0083-0.83 K s-1. Data showsthat in 3 of the alloys, those that form {5 5 7}γ...... martensite, no martensite developsduring cooling. For all investigated alloys, irrespective of the type of martensiteforming, thermally activated martensite develops during heating. The activationenergy for thermally activated martensite formation is in the range 8‒27 kJ mol-1and increases with the fraction...... of interstitial solutes in the alloy...

  19. Preparation of superconducting Nb-Zr alloys

    Energy Technology Data Exchange (ETDEWEB)

    Drapala, J.; Kuchar, L. (Vysoka Skola Banska, Ostrava (Czechoslovakia). Katedra Nezeleznych Kovu a Jaderne Metalurgie)


    Superconducting Nb-Zr alloy with a zirconium content of up to 3 wt.% was prepared by a combination of arc and electron zone melting. First, the Nb-Zr master alloy with 1 wt.% Zr was prepared in a horizontal arc furnace under an argon atmosphere. This master alloy was remelted several times to achieve the highest possible homogeneity of samples. The Nb-Zr ingot was then remelted through two zone passes on equipment for high-vacuum electron zone melting. Samples were taken of the Nb-Zr alloy and a metallographic analysis was made.

  20. Yield and excitation function measurements of some nuclear reactions on natural thallium induced by protons leading to the production of medical radioisotopes {sup 201}Tl and {sup 203}Pb

    Energy Technology Data Exchange (ETDEWEB)

    Al-Saleh, F.S.; Al-Harbi, A.A. [Girls College of Education, Riyadh (Saudi Arabia). Physics Dept.; Azzam, A. [Nuclear Research Center, Cairo (Egypt). Nuclear Physics Dept.


    Excitation functions for {sup 201}Pb, {sup 202m}Pb, {sup 203}Pb and {sup 204m}Pb radionuclides which are formed via proton induced reactions with natural thallium target have been measured from their respective threshold (E{sub thr}) to 27.5 MeV using activation technique. Natural copper foils were used to monitor the cyclotron beam. The integral yields (MBq/{mu}A h) of the produced radionuclides were calculated from the measured excitation functions. The optimum proton energy range for the production of {sup 203}Pb with low amount of impurities is (16-10 MeV) after 5 h of EOB. The experimental cross-sections for {sup nat}Tl(p,xn) reactions were compared with the cross-sections recommended by the IAEA and with earlier published data when it was possible. (orig.)

  1. Investigations on the optimization of phase and alloy compositions of Al-Cu-Si-Mg alloys

    Energy Technology Data Exchange (ETDEWEB)

    Eskin, D.G. (A.A. Baikov Inst. of Metallurgy, Russian Academy of Sciences, Moscow (Russia))


    The effect of the supersaturated solid solution composition on the phase composition of aging products in Al - (4 mass%) Cu-Si-Mg alloys has been investigated in a broad compositional range. The diagram of distribution of phase regions has been constructed for the Al-Cu (4 mass%)-Si-Mg alloys after aging at 170degC for 20 h. With cast and deformed alloys, it has been shown exemplarily that the best complex of mechanical properties is associated with alloy compositions ensuring the precipitation of [Theta]' and [beta]'' phases. The composition of cast Al - Si - Cu - Mg alloys has been optimized. (orig.).

  2. Bond Strength of Gold Alloys Laser Welded to Cobalt-Chromium Alloy


    Watanabe, Ikuya; Wallace, Cameron


    The objective of this study was to investigate the joint properties between cast gold alloys and Co-Cr alloy laser-welded by Nd:YAG laser. Cast plates were fabricated from three types of gold alloys (Type IV, Type II and low-gold) and a Co-Cr alloy. Each gold alloy was laser-welded to Co-Cr using a dental laser-welding machine. Homogeneously-welded and non-welded control specimens were also prepared. Tensile testing was conducted and data were statistically analyzed using ANOVA. The homogeneo...

  3. Data set for diffusion coefficients of alloying elements in dilute Mg alloys from first-principles

    Directory of Open Access Journals (Sweden)

    Bi-Cheng Zhou


    Full Text Available Diffusion coefficients of alloying elements in Mg are critical for the development of new Mg alloys for lightweight applications. Here we present the data set of the temperature-dependent dilute tracer diffusion coefficients for 47 substitutional alloying elements in hexagonal closed packed (hcp Mg calculated from first-principles calculations based on density functional theory (DFT by combining transition state theory and an 8-frequency model. Benchmark for the DFT calculations and systematic comparison with experimental diffusion data are also presented. The data set refers to “Diffusion coefficients of alloying elements in dilute Mg alloys: A comprehensive first-principles study” by Zhou et al. [1].

  4. Development of a Brazing Alloy for the Mechanically Alloyed High Temperature Sheet Material INCOLOY Alloy MA 956. (United States)


    OF CONTENTS Section Pge 1. INTRODUCTION AND PW)GRAM E OBJECTIVE 7 2. ALLOYING APROACH AND RATIONALE 9 2.1 Approach 9 2.2 Selection of Suitable Alloy...At the time of writing this final summary report only limited success has been achieved by Allied Chemicals but it is reported as follows so that the

  5. Role of alloying elements in adhesive transfer and friction of copper-base alloys (United States)

    Buckley, D. H.


    Sliding friction experiments were conducted in a vacuum with binary-copper alloy riders sliding against a conventional bearing-steel surface with normal residual oxides present. The binary alloys contained 1 atomic percent of various alloying elements. Auger spectroscopy analysis was used to monitor the adhesive transfer of the copper alloys to the bearing-steel surface. A relation was found to exist between adhesive transfer and the reaction potential and free energy of formation of the alloying element in the copper. The more chemically active the element and the more stable its oxide, the greater was the adhesive transfer and wear of the copper alloy. Transfer occurred in all the alloys except copper-gold after relatively few (25) passes across the steel surface.

  6. Bond strength of gold alloys laser welded to cobalt-chromium alloy. (United States)

    Watanabe, Ikuya; Wallace, Cameron


    The objective of this study was to investigate the joint properties between cast gold alloys and Co-Cr alloy laser-welded by Nd:YAG laser. Cast plates were fabricated from three types of gold alloys (Type IV, Type II and low-gold) and a Co-Cr alloy. Each gold alloy was laser-welded to Co-Cr using a dental laser-welding machine. Homogeneously-welded and non-welded control specimens were also prepared. Tensile testing was conducted and data were statistically analyzed using ANOVA. The homogeneously-welded groups showed inferior fracture load compared to corresponding control groups, except for Co-Cr. In the specimens welded heterogeneously to Co-Cr, Type IV was the greatest, followed by low-gold and Type II. There was no statistical difference (Palloys tested, the Type IV gold alloy was the most suitable alloy for laser-welding to Co-Cr.

  7. The role of the alloy matrix in the creep behavior of particle-strengthened alloys (United States)

    Ajaja, O.; Howson, T. E.; Purushothaman, S.; Tien, J. K.


    The strengthening microstructural features in heat-resistant super-alloys are oxide dispersoids and/or gamma-prime precipitates. The role of the strength of the alloy matrix in the creep resistance of these alloys is considered. An evaluation was made of experimental data on oxide-dispersion- and/or precipitation-strengthened nickel-based alloys with various levels of matrix solid solution strengthening; a generalized expression for creep rates which separates the matrix contributions from the particle contributions to the resisting stress and creep strength of these alloys was derived. It is concluded that the major role of the alloy matrix in the creep behavior of these alloys is in determining the apparent stress dependence of the creep rates.

  8. Alloys of clathrate allotropes for rechargeable batteries (United States)

    Chan, Candace K; Miller, Michael A; Chan, Kwai S


    The present disclosure is directed at an electrode for a battery wherein the electrode comprises clathrate alloys of silicon, germanium or tin. In method form, the present disclosure is directed at methods of forming clathrate alloys of silicon, germanium or tin which methods lead to the formation of empty cage structures suitable for use as electrodes in rechargeable type batteries.

  9. Heat storage in alloy transformations. Final report

    Energy Technology Data Exchange (ETDEWEB)

    Birchenall, C E; Gueceri, S I; Farkas, D; Labdon, M B; Nagaswami, N; Pregger, B


    A study conducted to determine the feasibility of using metal alloys as thermal energy storage media is described. The study had the following major elements: (1) the identification of congruently transforming alloys and thermochemical property measurements, (2) the development of a precise and convenient method for measuring volume change during phase transformation and thermal expansion coefficients, (3) the development of a numerical modeling routine for calculating heat flow in cylindrical heat exchangers containing phase-change materials, and (4) the identification of materials that could be used to contain the metal alloys. The elements selected as candidate media were limited to aluminum, copper, magnesium, silicon, zinc, calcium, and phosphorus on the basis of low cost and latent heat of transformation. Several new eutectic alloys and ternary intermetallic phases have been determined. A new method employing x-ray absorption techniques was developed to determine the coefficients of thermal expansion of both the solid and liquid phases and the volume change during phase transformation from data that are obtained during one continuous experimental test. The method and apparatus are discussed and the experimental results are presented. The development of the numerical modeling method is presented and results are discussed for both salt and metal alloy phase-change media. Candidate materials were evaluated to determine suitable materials for containment of the metal alloys. Graphite was used to contain the alloys during the volume change measurements. Silicon carbide has been identified as a promising containment material and surface-coated iron alloys were considered.

  10. Materials data handbook: Aluminum alloy 2219 (United States)

    Muraca, R. F.; Whittick, J. S.


    A summary of the materials property information for aluminum 2219 alloy is presented. The scope of the information includes physical and mechanical properties at cryogenic, ambient, and elevated temperatures. Information on material procurement, metallurgy of the alloy, corrosion, environmental effects, fabrication, and joining techniques is developed.

  11. Materials data handbook: Aluminum alloy 5456 (United States)

    Muraca, R. F.; Whittick, J. S.


    A summary of the materials property information for aluminum alloy 5456 is presented. The scope of the information includes physical and mechanical property data at cryogenic, ambient, and elevated temperatures. Information on material procurement, metallurgy of the alloy, corrosion, environmental effects, fabrication, and joining techniques is developed.

  12. Materials data handbook: Aluminum alloy 6061 (United States)

    Muraca, R. F.; Whittick, J. S.


    A summary of the materials property information for aluminum alloy 6061 is presented. The scope of the information includes physical and mechanical properties of the alloy at cryogenic, ambient, and elevated temperatures. Information on material procurement, metallurgy, corrosion, environmental effects, fabrication, and joining techniques is developed.

  13. Tantalum modified ferritic iron base alloys (United States)

    Oldrieve, R. E.; Blankenship, C. P. (Inventor)


    Strong ferritic alloys of the Fe-CR-Al type containing 0.4% to 2% tantalum were developed. These alloys have improved fabricability without sacrificing high temperature strength and oxidation resistance in the 800 C (1475 F) to 1040 C (1900 F) range.

  14. Materials data handbook: Inconel alloy 718 (United States)

    Muraca, R. F.; Whittick, J. S.


    A summary of the materials property information for Inconel alloy 718 is presented. The scope of the information includes physical and mechanical properties at cryogenic, ambient, and elevated temperatures. Information on material procurement, metallurgy of the alloy, corrosion, environmental effects, fabrication, and joining techniques is developed.

  15. Development of high performance ODS alloys

    Energy Technology Data Exchange (ETDEWEB)

    Shao, Lin; Gao, Fei; Garner, Frank


    This project aims to capitalize on insights developed from recent high-dose self-ion irradiation experiments in order to develop and test the next generation of optimized ODS alloys needed to meet the nuclear community's need for high strength, radiation-tolerant cladding and core components, especially with enhanced resistance to void swelling. Two of these insights are that ferrite grains swell earlier than tempered martensite grains, and oxide dispersions currently produced only in ferrite grains require a high level of uniformity and stability to be successful. An additional insight is that ODS particle stability is dependent on as-yet unidentified compositional combinations of dispersoid and alloy matrix, such as dispersoids are stable in MA957 to doses greater than 200 dpa but dissolve in MA956 at doses less than 200 dpa. These findings focus attention on candidate next-generation alloys which address these concerns. Collaboration with two Japanese groups provides this project with two sets of first-round candidate alloys that have already undergone extensive development and testing for unirradiated properties, but have not yet been evaluated for their irradiation performance. The first set of candidate alloys are dual phase (ferrite + martensite) ODS alloys with oxide particles uniformly distributed in both ferrite and martensite phases. The second set of candidate alloys are ODS alloys containing non-standard dispersoid compositions with controllable oxide particle sizes, phases and interfaces.

  16. Aluminum alloy nanosecond vs femtosecond laser marking

    Indian Academy of Sciences (India)

    aluminum alloy, a vastly used material base within several industry fields. For the novelty impact, femtolaser mark- ing has ... The modern industry, in order to preserve, protect, promote and enhance the value of their activities, use .... the laser beam; therefore, the freshly formed clusters of li- quid alloy microspheres have the ...

  17. Titanium and titanium alloys: fundamentals and applications

    National Research Council Canada - National Science Library

    Leyens, C; Peters, M


    ... number of titanium alloys have paved the way for light metals to vastly expand into many industrial applications. Titanium and its alloys stand out primarily due to their high specific strength and excellent corrosion resistance, at just half the weight of steels and Ni-based superalloys. This explains their early success in the aerospace and the...

  18. Methods for Electrodepositing Composition-Modulated Alloys

    DEFF Research Database (Denmark)

    Leisner, Peter; Nielsen, Christian Bergenstof; Tang, Peter Torben


    Materials exhibiting unique mechanical, physical and chemical properties can be obtained by combining thin layers of different metals or alloys forming a multilayered structure. Two general techniques exist for electrodepositing composition-modulated alloy (CMA) materials; dual-bath and single...

  19. Atomic displacements in bcc dilute alloys

    Indian Academy of Sciences (India)

    Keywords. Atomic displacements; crystal defects; crystalline solids. PACS Nos 63.43.j; 63.43.Dq; 61.66.Dk; 61.72.Ji. 1. Introduction. The transition metal dilute alloys are studied for their unique properties such as high strength ...... Even the recent techniques like EXAFS are inadequate for bcc alloys because in the EXAFS ...

  20. Inventory of alloy composition, microstructures and mechanical ...

    African Journals Online (AJOL)

    The mechanical test results show that crankshaft possesses high strength, toughness and hardness and it is case hardened alloy steel while camshaft displays excellent resistance to wear, high brittleness and it is alloy cast Iron. Results also reveal that connecting rod possesses high strength and toughness and it is ...

  1. Improving mechanical properties of aluminium alloy through ...

    African Journals Online (AJOL)

    This paper investigates the microstructure and mechanical properties of aluminum alloy (Al-Si-Fe) reinforced with coconut shell-ash particulate. The aluminium (Al-Si-Fe) alloy composite was produced by a double-stir casting process at a speed of 700 rpm for 10 and 5 minutes at first and second stirring respectively.


    Directory of Open Access Journals (Sweden)

    T.P. Pavlenko


    Full Text Available The paper reviews and analyzes properties of amorphous alloys for the purpose of their application in magnetic systems of electrical apparatus instead of high-permeability electric steels. The studies have shown a possibility of utilizing these alloys in the magnetic structure of a current transformer in the pulsed voltage stabilizer of an automated circuit-breaker semiconductor release.

  3. Progress in High-Entropy Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Gao, Michael C


    Strictly speaking, high-entropy alloys (HEAs) refer to single-phase, solid-solution alloys with multiprincipal elements in an equal or a near-equal molar ratio whose configurational entropy is tremendously high. This special topic was organized to reflect the focus and diversity of HEA research topics in the community.

  4. R-HPDC of magnesium alloys

    CSIR Research Space (South Africa)

    Curle, UA


    Full Text Available liquid segregation is observed in the as-cast microstructure for all three alloys. Minor alloy additions of Mn, in composition specifications, results in the formation of Al8Mn5 intermetallic phase particles dispersed throughout the microstructure. All...


    NARCIS (Netherlands)


    Resistivity measurements on liquid Rb-In and Cs-In alloys provide evidence for compound formation at a composition of 50% In. The discussion is based on existing electronic structure calculations for solid alloys of Li and Na with Ga, In and Tl. Several possible models for describing liquid

  6. [Corrosion resistance of Ti-Cu alloy]. (United States)

    Song, Yu-Xuan; Wang, Shi-Ming


    to investigate the corrosion behavior of Ti-Cu alloy in 0.9%NaCl solution and in acidified 0.9%NaCl solution. the microstructure of Ti-Cu alloys were characterized by means of X-ray diffraction (XRD). The electrochemical behavior of Ti-Cu alloy in two solutions (namely 0.9%NaCl solution and acidified 0.9%NaCl solution) was tested. Commercial pure Ti and 316L stainless steel were used as control. Ti-Cu alloys were composed by α-Ti and Ti(2)Cu intermetallic compound. After 3500 s immersion, the open circuit potential (OCP) values of pure Ti, Ti-5Cu alloy and Ti-10Cu alloy in 0.9% NaCl solution were -188, -181 and -173 mV, respectively. In 0.9% NaCl solution with lactic acid added, the OCP values were -143, -158 and -109 mV, respectively. In potentiodynamic polarization tests, the passive current densities of pure Ti and Ti-5Cu alloys were about 20 µA/cm(2). However, 316L stainless steel experienced pitting corrosion. it was possible to establish the following relation for their corrosion resistances: pure Ti≈Ti-5Cu > Ti-10Cu > 316L stainless steel. The addition of lactic acid in the solution did not compromise the corrosion resistance of Ti-Cu alloys.

  7. The interaction of hydrogen with metal alloys (United States)

    Danford, M. D.; Montano, J. W.


    Hydrogen diffusion coefficients were measured for several alloys, and these were determined to be about the same at 25 C for all alloys investigated. The relation of structure, both metallurgical and crystallographic, to the observed hydrogen distribution on charging was investigated, as well as the role of hydride formation in the hydrogen resistance of metal alloys. An attempt was made to correlate the structures and compositions of metal alloys as well as other parameters with the ratios of their notched tensile strengths in hydrogen to that in helium, R(H2/He), which are believed to represent a measure of their hydrogen resistance. Evidence supports the belief that hydrogen permeability and hydrogen resistance are increased by smaller grain sizes for a given alloy composition.

  8. A Study of Tungsten-Technetium Alloys (United States)

    Maltz, J. W.


    Technetium is a sister element to rhenium and has many properties that are similar to rhenium. It is predicted that technetium will have about the same effects on tungsten as rhenium in regard to increase in workability, lowered ductile to brittle transition temperature, and improved ductility. The objectives of the current work are to recover technetium from fission product wastes at Hanford Atomic Products Operation and reduce to purified metal; prepare W-Tc alloys containing up to 50 atomic% Tc; fabricate the alloy ingots to sheet stock, assessing the effect of technetium on workability; and perform metallurgical and mechanical properties evaluation of the fabricated alloys. Previous reports have described the separation and purification of 800 g of technetium metal powder, melting of technetium and W-Tc alloys, and some initial observation of the alloy material.

  9. Long - range foundry Al composite alloys

    Directory of Open Access Journals (Sweden)

    A. D. Mekhtiev


    Full Text Available The technology of obtaining nanostructural composite aluminum alloys consists in the plasma injection of refractory nanometric particles with simultaneous two-plane magnetic dynamic mixing of the melt. Particularly important in obtaining composite aluminum matrix alloys is the provision of the introduced particles wettability with the matrix melt for forming stable adhesive bonds. Nanostructured powder components can be considered not only to be a starting product for producing nanostructural composite aluminum alloys but as an independent commerce product. Nanostructural composite metal matrix alloys make one of the most prospective structural materials of the future, and liquid-phase technologies of their obtaining are the most competitive in producing products of nanostructural composite aluminum alloys in the industrial scale.

  10. Internal chlorination of Ni-Cr alloys

    Energy Technology Data Exchange (ETDEWEB)

    Berztiss, D.; Hennesen, K.; Grabke, H.J. [Max-Planck-Institut fuer Eisenforschung GmbH, Duesseldorf (Germany)


    In contrast to internal oxidation, sulfidation and carburization, very little information is available regarding internal chlorination, especially diffusion of chlorine in metallic alloys. This paper describes results of experiments on Ni-Cr alloys (<10 wt% Cr) exposed in an atmosphere containing radioactive HCl. The diffusion of chlorine in the alloy can be determined by measurement of residual {beta}-activity from the sample surface. Successively thin layers (0.5-10 {mu}m) of the alloy were removed by lapping and the surface activity was measured to obtain a depth profile. Both single and polycrystalline materials were tested. Through this work it should be determined if there is in fact solubility and diffusion of chlorine in Ni-based alloys as some authors have proposed or if the ingress of chlorine is mainly a grain boundary phenomenon. (orig.)

  11. Corrosion resistance improvement of titanium base alloys

    Directory of Open Access Journals (Sweden)

    Mihai V. Popa


    Full Text Available The corrosion resistance of the new Ti-6Al-4V-1Zr alloy in comparison with ternary Ti-6Al-4V alloy in Ringer-Brown solution and artificial Carter-Brugirard saliva of different pH values was studied. In Ringer-Brown solution, the new alloy presented an improvement of all electrochemical parameters due to the alloying with Zr; also, impedance spectra revealed better protective properties of its passive layer. In Carter-Brugirard artificial saliva, an increase of the passive film thickness was proved. Fluoride ions had a slight negative influence on the corrosion and ion release rates, without to affect the very good stability of the new Ti-6Al-4V-1Zr alloy.

  12. Magnesium and related low alloys

    Energy Technology Data Exchange (ETDEWEB)

    Bernard, J.; Caillat, R.; Darras, R. [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires


    In the first part the authors examine the comparative corrosion of commercial magnesium, of a magnesium-zirconium alloy (0,4 per cent {<=} Zr {<=} 0,7 per cent) of a ternary magnesium-zinc-zirconium alloy (0,8 per cent {<=} Zn {<=} 1,2 per cent) and of english 'Magnox type' alloys, in dry carbon dioxide-free air, in damp carbon dioxide-free air, and in dry and damp carbon dioxide, at temperatures from 300 to 600 deg. C. In the second part the structural stability of these materials is studied after annealings, of 10 to 1000 hours at 300 to 450 deg. C. Variations in grain after these heat treatments and mechanical stretching properties at room temperature are presented. Finally various creep rate and life time diagrams are given for these materials, for temperatures ranging from 300 to 450 deg. C. (author) [French] Dans une premiere partie les auteurs etudient la corrosion comparee du magnesium commercial, d'un alliage magnesium-zirconium (0,4 pour cent {<=} Zr {<=} 0,7 pour cent), d'un alliage ternaire magnesium-zinc-zirconium (0,8 pour cent {<=} Zn {<=} 1,2 pour cent), et d'alliages anglais 'type Magnox', dans l'air sec decarbonate, l'air humide decarbonate, le gaz carbonique sec et humide a des temperatures de 300 a 600 deg. C. Dans une seconde partie, est etudiee la stabilite structurale de ces materiaux apres des recuits de 300 a 450 deg. C, et de 10 a 1000 heures. Sont presentees les variations, apres ces traitements thermiques, de la grosseur du grain, et des caracteristiques mecaniques de traction a la temperature ambiante. Enfin, quelques diagrammes de vitesse de fluage et de durees de vie sont presentes sur ces materiaux pour des temperatures variant entre 300 et 450 deg. C. (auteur)

  13. Machine Casting of Ferrous Alloys (United States)


    1976 g DTIC 8 AELECTEI% UJ %AUG2 31985|| —J mjfr %M ^ B rra M B5 8 23 151 l-TT-WFtf.^ viH »<.wil»t«^lvi»wmrgT1i^^V\\’.-’\\’.^VA’ ,T...Slurry Producer . . 13 4. Laboratory Casting Machine 15 IV. STRUCTURE, SEGREGATION, HOMOGENIZATION HEAT TREATMENT , AND MECHANICAL PROPERTIES OF...RHEOCAST ALLOYS 18 1. Effect of Process Variables on Structure 18 2. Segregation, Homogenization Heat Treatment and Mechanical Properties 22 V

  14. Braze alloy spreading on steel (United States)

    Siewert, T. A.; Heine, R. W.; Lagally, M. G.


    Scanning electron microscopy (SEM) and Auger electron microscopy (AEM) were employed to observe elemental surface decomposition resulting from the brazing of a copper-treated steel. Two types of steel were used for the study, stainless steel (treated with a eutectic silver-copper alloy), and low-carbon steel (treated with pure copper). Attention is given to oxygen partial pressure during the processes; a low enough pressure (8 x 10 to the -5th torr) was found to totally inhibit the spreading of the filler material at a fixed heating cycle. With both types of steel, copper treatment enhanced even spreading at a decreased temperature.

  15. A novel method of aluminum-gadolinium master alloy production (United States)

    Maksimtsev, Konstantin; Krylosov, Andrey; Polovov, Ilya; Zhilyakov, Arkadiy; Belikov, Sergey; Volkovich, Vladimir; Rebrin, Oleg


    A new method for manufacturing aluminum-gadolinium master alloy was designed. It is based on an exchange reaction between metallic aluminum and gadolinium fluoride. The structure on the synthesized alloys with different gadolinium content was investigated. Al and Al3Gd were the main phases present in the alloys. Mechanical and thermophysical properties of the master-alloys obtained were measured.

  16. Crystallographic attributes of a shape-memory alloy


    Bhattacharya, Kaushik


    Shape-memory Alloys are attractive for many potential applications. In an attempt to provide ideas and guidelines for the development of new shape-memory alloys, this paper reports on a series of investigations that examine the reasons in the crystallography that make (i) shape-memory alloys special amongst martensites and (ii) Nickel-Titanium special among shape-memory alloys.

  17. Recent research and developments on wrought magnesium alloys

    Directory of Open Access Journals (Sweden)

    Sihang You


    Full Text Available Wrought magnesium alloys attract special interests as lightweight structural material due to their homogeneous microstructure and enhanced mechanical properties compared to as-cast alloys. In this contribution, recent research and developments on wrought magnesium alloys are reviewed from the viewpoint of the alloy design, focusing on Mg-Al, Mg-Zn and Mg-rare earth (RE systems. The effects of different alloying elements on the microstructure and mechanical properties are described considering their strengthening mechanisms, e.g. grain refinement, precipitation and texture hardening effect. Finally, the new alloy design and also the future research of wrought magnesium alloys to improve their mechanical properties are discussed.

  18. Aeronautical requirements for Inconel 718 alloy (United States)

    Elefterie, C. F.; Guragata, C.; Bran, D.; Ghiban, B.


    The project goal is to present the requirements imposed by aviation components made from super alloys based on Nickel. A significant portion of fasteners, locking lugs, blade retainers and inserts are manufactured from Alloy 718. The thesis describes environmental factors (corrosion), conditions of external aggression (salt air, intense heat, heavy industrial pollution, high condensation, high pressure), mechanical characteristics (tensile strength, yield strength and fatigue resistance) and loadings (tensions, compression loads) that must be satisfied simultaneously by Ni-based super alloy, compared to other classes of aviation alloys (as egg. Titanium alloys, Aluminum alloys). For this alloy the requirements are strength durability, damage tolerance, fail safety and so on. The corrosion can be an issue, but the fatigue under high-magnitude cyclic tensile loading it’s what limits the lifetime of the airframe. Also, the excellent malleability and weldability characteristics of the 718 system make the material physical properties tolerant of manufacturing processes. These characteristics additionally continue to provide new opportunities for advanced manufacturing methods.

  19. Vapor phase lubrication of high temperature alloys

    Energy Technology Data Exchange (ETDEWEB)

    Hanyaloglu, B.F.; Graham, E.E.; Oreskovic, T.; Hajj, C.G. [Cleveland State Univ., OH (United States)


    In a previous study, it was found that when a nickel-based superalloy IN750 was heated to high temperatures, a passive layer of aluminum oxide formed on the surface, preventing vapor phase lubrication. In this study, two nickel-chrome-iron alloys and a nickel-copper alloy were studied for high temperature lubrication to see if these alloys, which contained small amounts of aluminum, would exhibit similar behavior. It was found that under static conditions, all three alloys formed a lubricious nodular coating when exposed to a vapor of aryl phosphate. Under dynamic sliding conditions at 500{degrees}C, these alloys were successfully lubricated with a coefficient of friction of 0.1 and no detectable wear. In order to explain these results, a direct correlation between successful vapor phase lubrication and the composition of the alloys containing aluminum has been proposed. If the ratio of copper/aluminum or iron/aluminum is greater that 100 vapor phase, lubrication will be successful. If the ratio is less than 10, a passive aluminum oxide layer will prevent vapor phase lubrication. By selecting alloys with a high iron or copper content, vapor phase lubrication can provide excellent lubrication at high temperatures. 14 refs., 11 figs., 1 tab.

  20. Indium Helps Strengthen Al/Cu/Li Alloy (United States)

    Blackburn, Linda B.; Starke, Edgar A., Jr.


    Experiments on Al/Cu/Li alloys focus specifically on strengthening effects of minor additions of In and Cd. Indium-bearing alloy combines low density with ability to achieve high strength through heat treatment alone. Tensile tests on peak-aged specimens indicated that alloy achieved yield strength approximately 15 percent higher than baseline alloy. Alloy highly suitable for processing to produce parts of nearly net shape, with particular applications in aircraft and aerospace vehicles.

  1. Fatigue Characteristics of Selected Light Metal Alloys

    Directory of Open Access Journals (Sweden)

    Cieśla M.


    Full Text Available The paper addresses results of fatigue testing of light metal alloys used in the automotive as well as aerospace and aviation industries, among others. The material subject to testing comprised hot-worked rods made of the AZ31 alloy, the Ti-6Al-4V two-phase titanium alloy and the 2017A (T451 aluminium alloy. Both low- and high-cycle fatigue tests were conducted at room temperature on the cycle asymmetry ratio of R=-1. The low-cycle fatigue tests were performed using the MTS-810 machine on two levels of total strain, i.e.Δεc= 1.0% and 1.2%. The high-cycle fatigue tests, on the other hand, were performed using a machine from VEB Werkstoffprufmaschinen-Leipzig under conditions of rotary bending. Based on the results thus obtained, one could develop fatigue life characteristics of the materials examined (expressed as the number of cycles until failure of sample Nf as well as characteristics of cyclic material strain σa=f(N under the conditions of low-cycle fatigue testing. The Ti-6Al-4V titanium alloy was found to be characterised by the highest value of fatigue life Nf, both in lowand high-cycle tests. The lowest fatigue life, on the other hand, was established for the aluminium alloys examined. Under the high-cycle fatigue tests, the life of the 2017A aluminium and the AZ31 magnesium alloy studied was determined by the value of stress amplitude σa. With the stress exceeding 150 MPa, it was the aluminium alloy which displayed higher fatigue life, whereas the magnesium alloy proved better on lower stress.

  2. Grain refining technique of AM60B alloy by Al-Ti-B master alloy

    Directory of Open Access Journals (Sweden)

    Chen Tijun


    Full Text Available The effects of grain refining parameters on grain size of AM60B magnesium alloy have been investigated using an Al-5Ti-1B master alloy as refiner; and an appropriate refining technique has been developed. The results indicate that the Al-Ti-B master alloy is an effective grain refiner for AM60B alloy and the grain size can be decreased from 348 μm to 76 μm. Raising the addition temperature or the pouring temperature is beneficial for grain refinement; while for the addition amount and holding time, there is an optimal value. The appropriate grain refining technique is that 0.3% Al-Ti-B master alloy is added at 780 ℃ and then the melt is held for 30 min before pouring. The above phenomena can be explained by the refining mechanisms that have been proposed from the related studies on Al and Mg alloys and theoretical analysis.

  3. Cast bulk glassy alloys: fabrication, alloy development and properties

    Directory of Open Access Journals (Sweden)

    Qingsheng Zhang


    Full Text Available Metallic glasses represent an interesting group of materials as they possess outstanding physical, chemical and mechanical properties compared to their crystalline counterparts. Currently, with well designed compositions it is possible to cast liquid alloys into the glassy state at low critical cooling rates from 100 K•s-1 to 1 K•s-1 and in large critical sample sizes up to several centimeters, which significantly enhances the promise for possible applications as advanced engineering materials. This paper reviews the development of (ZrCu-based bulk metallic glasses with large sizes by copper mold casting and their unique properties. Additionally, the ex-situ and in-situ second phases reinforced BMG composites with large plasticity are also presented.

  4. Current assisted superplastic forming of titanium alloy

    Directory of Open Access Journals (Sweden)

    Wang Guofeng


    Full Text Available Current assisted superplastic forming combines electric heating technology and superplastic forming technology, and can overcome some shortcomings of traditional superplastic forming effectively, such as slow heating rate, large energy loss, low production efficiency, etc. Since formability of titanium alloy at room temperature is poor, current assisted superplastic forming is suitable for titanium alloy. This paper mainly introduces the application of current assisted superplastic forming in the field of titanium alloy, including forming technology of double-hemisphere structure and bellows.

  5. Graded coatings for metallic implant alloys

    Energy Technology Data Exchange (ETDEWEB)

    Saiz, Eduardo; Tomsia, Antoni P.; Fujino, Shigeru; Gomez-Vega, Jose M.


    Graded glass and glass-hydroxyapatite coatings on Ti-based and Co-Cr alloys have been prepared using a simple enameling technique. The composition of the glasses has been tailored to match the thermal expansion of the alloys. By controlling the firing time, and temperature, it has been possible to control the reactivity between the glass and the alloy and to fabricate coatings (25 to 150 mu m thick) with excellent adhesion to the substrate, resistant to corrosion and able to precipitate hydroxyapatite during in vitro tests in simulated body fluid.

  6. New alloys to conserve critical elements (United States)

    Stephens, J. R.


    Based on availability of domestic reserves, chromium is one of the most critical elements within the U.S. metal industry. New alloys having reduced chromium contents which offer potential as substitutes for higher chromium containing alloys currently in use are being investigated. This paper focuses primarily on modified Type 304 stainless steels having one-third less chromium, but maintaining comparable oxidation and corrosion properties to that of type 304 stainless steel, the largest single use of chromium. Substitutes for chromium in these modified Type 304 stainless steel alloys include silicon and aluminum plus molybdenum.

  7. Stress corrosion cracking of titanium alloys (United States)

    Statler, G. R.; Spretnak, J. W.; Beck, F. H.; Fontana, M. G.


    The effect of hydrogen on the properties of metals, including titanium and its alloys, was investigated. The basic theories of stress corrosion of titanium alloys are reviewed along with the literature concerned with the effect of absorbed hydrogen on the mechanical properties of metals. Finally, the basic modes of metal fracture and their importance to this study is considered. The experimental work was designed to determine the effects of hydrogen concentration on the critical strain at which plastic instability along pure shear directions occurs. The materials used were titanium alloys Ti-8Al-lMo-lV and Ti-5Al-2.5Sn.

  8. Development of Lightweight Titanium Base Alloys (United States)


    as base alloy compositions. After the program began, the gamma-Ti-35A1 alloy was added. The principal thrust was to add significant amounts of Be to...creepresistance at high temperatures. A secondary thrust of this program was to add Li arid Mg to the base alloys in sufficient concentrations to decrease overall...selected al!oy samples were determined by using the Archimedes technique with water at 23°C; these densities are compared with densities of tne

  9. Magnetization curve modelling of soft magnetic alloys

    Energy Technology Data Exchange (ETDEWEB)

    Meszaros, I, E-mail: [Department of Materials Science and Engineering, Budapest University of Technology and Economics, Bertalan L. street 7., Budapest, H-1111 (Hungary)


    In this paper we present an application of the so called hyperbolic model of magnetization. The model was modified and it was applied for nine different soft magnetic alloys. The tested samples were electro-technical steels (FeSi alloys) and a permalloy (FeNi alloy) with strongly different magnetic properties. Among them there are top, medium and definitely poor quality soft magnetic materials as well. Their minor hysteresis loops and normal magnetization curves were measured by alternating current measurement. The hyperbolic model of magnetization was applied for the experimental normal magnetization curves. It was proved that the applied model is excellent for describing mathematically the experimental magnetization curves.

  10. Influence of the selected alloy additions on limiting the phase formation in Cu-Zn alloys

    Directory of Open Access Journals (Sweden)

    J. Kozana


    Full Text Available Influence of the selected alloy additions into copper and zinc alloys was investigated in order to find out the possibility of limiting the precipitation of unfavourable phase . The observation of microstructures and strength tests were performed. The results of metallographic and strength investigations indicate positive influence of small amounts of nickel, cobalt or tellurium. The precise determination of the influence of the selected alloy additions on limiting the gamma phase formation will be the subject of further examinations.

  11. HAYNES 244 alloy – a new 760 ∘C capable low thermal expansion alloy


    Fahrmann Michael G.; Srivastava S. Krishna; Pike Lee M.


    HAYNES® 244TM alloy is a new 760∘C capable, high strength low thermal expansion (CTE) alloy. Its nominal chemical composition in weight percent is Ni – 8 Cr – 22.5 Mo – 6 W. Recently, a first mill-scale heat of 244 alloy was melted by Haynes International, and processed to various product forms such as re-forge billet, plate, and sheet. This paper presents key attributes of this new alloy (CTE, strength, low-cycle fatigue performance, oxidation resistance, thermal stability) as they pertain t...

  12. HAYNES 244 alloy – a new 760 ∘C capable low thermal expansion alloy

    Directory of Open Access Journals (Sweden)

    Fahrmann Michael G.


    Full Text Available HAYNES® 244TM alloy is a new 760∘C capable, high strength low thermal expansion (CTE alloy. Its nominal chemical composition in weight percent is Ni – 8 Cr – 22.5 Mo – 6 W. Recently, a first mill-scale heat of 244 alloy was melted by Haynes International, and processed to various product forms such as re-forge billet, plate, and sheet. This paper presents key attributes of this new alloy (CTE, strength, low-cycle fatigue performance, oxidation resistance, thermal stability as they pertain to the intended use in rings and seals of advanced gas turbines.

  13. Wear resistance of alloy вт-22 with non-ferrous alloys at reverse

    Directory of Open Access Journals (Sweden)

    А.М. Хімко


    Full Text Available  The article presents the results of tests of non hardened titanium alloy ВТ-22 with aviation non-ferrous alloys in reverse sliding friction. The main objective of the work is the selection of the optimum combination of materials depending on changes in loading conditions. Study of alloy ВТ-22 wear resistance was carried out in pairs with БрОФ-10-1, БрБ2, БрАЖ-9-4, ВТ-22, МЛ5, Д16Т, 7Х21ГАН5Ш and 95Х18Ш. The dependencies of the materials wear at pressures 10, 20 and 30 Mpa we determined. The linear nature of titanium alloy wear curves indicates that the change in the wear mechanism occurs gradually. The histograms of non-ferrous materials wear and the total wear of the friction pair are presented. It is established that the bronze БрАЖ-9-4 is the most preferable material for contact with non hardened titanium alloy ВТ-22, the least wear among the tested materials. The established coefficients of the titanium alloy ВТ-22 friction in pair with aviation structural non-ferrous alloys are presented. The results of research will be relevant for the engineering industry, where non hardened titanium alloy ВТ-22 in pair with non-ferrous alloys is applied.

  14. Effect of the selected alloying on Ni-Mn-Ga alloys

    Energy Technology Data Exchange (ETDEWEB)

    Soederberg, O.; Koho, K.; Sammi, T.; Liu, X.W.; Sozinov, A.; Lanska, N.; Lindroos, V.K


    The aim of the present study was to investigate the possibilities of changing some characteristics of ternary Ni-Mn-Ga alloys by alloying. Therefore, five quaternary materials were prepared from the same polycrystalline Ni-Mn-Ga master ternary alloy with about 2 at.% additions of Bi, Pb, Si, Sn and Zn. The transformation temperatures and Curie points of the annealed materials were determined with DSC and magnetic susceptibility measurements. The crystal structures of the alloys were determined with the X-ray diffraction. In alloys with Si and Sn phase transformations were retarded to very low temperatures or outside the observable temperature region (below 113 K). With Si alloying a clear premartensitic softening was present. Bi, Pb and Zn doping preserved the original monoclinic crystal structure of the master alloy with slight lattice parameter changes. Bi increased slightly the phase transformation temperatures and decreased the Curie point, while in the two others phase transformations were shifted little lower and Curie temperature to higher temperatures. The intermartensitic transformation present in the ternary alloy was either totally retarded or diminished to a large extent in all of the doped alloys.

  15. Incology alloy 908 data handbook

    Energy Technology Data Exchange (ETDEWEB)

    Toma, L.S.; Steeves, M.M. [Massachusetts Institute of Technology, Cambridge, MA (United States); Reed, R.P. [Cryogenic Materials Inc., Boulder, CO (United States)


    This handbook is a compilation of all available properties of Incoloy alloy 908 as of March, 1994. Data included in this paper cover mechanical, elastic, thermal and magnetic characteristics. The mechanical properties include tensile, fracture toughness, fatigue, and stress-rupture for both the base metal and related weld filler metals. Elastic properties listed are Young`s, shear and bulk moduli and Poisson`s ratio. Thermal expansion, thermal conductivity and specific heat and magnetization are also reported. Data presented are summarized in the main body and presented in detail in the supplements. Areas of ongoing research are briefly described, and topics for future research are suggested. The data have been compiled to assist in the design of large-scale superconducting magnets for fusion reactors.

  16. Silver-hafnium braze alloy (United States)

    Stephens, Jr., John J.; Hosking, F. Michael; Yost, Frederick G.


    A binary allow braze composition has been prepared and used in a bonded article of ceramic-ceramic and ceramic-metal materials. The braze composition comprises greater than approximately 95 wt % silver, greater than approximately 2 wt % hafnium and less than approximately 4.1 wt % hafnium, and less than approximately 0.2 wt % trace elements. The binary braze alloy is used to join a ceramic material to another ceramic material or a ceramic material, such as alumina, quartz, aluminum nitride, silicon nitride, silicon carbide, and mullite, to a metal material, such as iron-based metals, cobalt-based metals, nickel-based metals, molybdenum-based metals, tungsten-based metals, niobium-based metals, and tantalum-based metals. A hermetic bonded article is obtained with a strength greater than 10,000 psi.

  17. Phase diagrams for surface alloys

    DEFF Research Database (Denmark)

    Christensen, Asbjørn; Ruban, Andrei; Stoltze, Per


    of the heat of segregation from the bulk and the sign of the excess interactions between the atoms in the surface (the surface mixing energy). We also consider the more complicated cases a with ordered surface phases, nonpseudomorphic overlayers, second layer segregation, and multilayers. The discussion......We discuss surface alloy phases and their stability based on surface phase diagrams constructed from the surface energy as a function of the surface composition. We show that in the simplest cases of pseudomorphic overlayers there are four generic classes of systems, characterized by the sign...... is based on density-functional calculations using the coherent-potential approximation and on effective-medium theory. We give self-consistent density-functional results for the segregation energy and surface mixing energy for all combinations of the transition and noble metals. Finally we discuss...

  18. Copper Alloy For High-Temperature Uses (United States)

    Dreshfield, Robert L.; Ellis, David L.; Michal, Gary


    Alloy of Cu/8Cr/4Nb (numbers indicate parts by atom percent) improved over older high-temperature copper-based alloys in that it offers enhanced high temperature strength, resistance to creep, and ductility while retaining most of thermal conductivity of pure copper; in addition, alloy does not become embrittled upon exposure to hydrogen at temperatures as high as 705 degrees C. Designed for use in presence of high heat fluxes and active cooling; for example, in heat exchangers in advanced aircraft and spacecraft engines, and other high-temperature applications in which there is need for such material. High conductivity and hardness of alloy exploited in welding electrodes and in high-voltage and high-current switches and other applications in which wear poses design problem.

  19. Theory of Rare-Earth Alloys

    DEFF Research Database (Denmark)

    Lindgård, Per-Anker


    A mean-field random alloy theory combined with a simple calculation of the exchange interaction J(c,Q) is shown to quantitatively account for the phase diagrams for alloys of rare-earth metals with Y, Lu, Sc, and other rare-earth metals. A concentration-dependent J(c,Q) explains the empirical 2...... to account for all alloys except the Sc based. The exceptional behavior of the Sc alloys is due to a low density of states for Sc. A brief discussion is given of the effect on the mean-field results of changes in volume or c/a ratio and of critical fluctuations. Since the physical mechanisms of these ideal...


    Directory of Open Access Journals (Sweden)

    V. Ju. Stetsenko


    Full Text Available It is shown that antifriction aluminium-silicon alloy is perspective material for change of the parts of heavy and expensive bronze in different frictional units of machines and mechanisms.

  1. NASA-427: A New Aluminum Alloy (United States)

    Nabors, Sammy A.


    NASA's Marshall Space Flight Center researchers have developed a new, stronger aluminum alloy, ideal for cast aluminum products that have powder or paint-baked thermal coatings. With advanced mechanical properties, the NASA-427 alloy shows greater tensile strength and increased ductility, providing substantial improvement in impact toughness. In addition, this alloy improves the thermal coating process by decreasing the time required for heat treatment. With improvements in both strength and processing time, use of the alloy provides reduced materials and production costs, lower product weight, and better product performance. The superior properties of NASA-427 can benefit many industries, including automotive, where it is particularly well-suited for use in aluminum wheels.

  2. Development of creep resistant magnesium diecasting alloys

    Energy Technology Data Exchange (ETDEWEB)

    Pekguleryuz, M.O. [Noranda Technol. Center, Que. (Canada)


    The most economic use of magnesium in the automotive industry presently is in diecast applications because of the high productivity of the diecasting process that upsets the relatively high cost of the magnesium metal. The current commercial magnesium alloys developed for diecasting applications fall into two classes. The first group is based on the Mg-Al system and the Mg-Al-Zn systems. These alloys have been developed for good room temperature strength and/or ductility but do not exhibit good creep resistance. The second group of alloys has been developed for improved elevated-temperature performance and are based on the Mg-Al-RE and Mg-Al-Si systems. These second group alloys offer either borderline improvement in creep resistance (Mg-Al-Si) or have cost or other disadvantages despite the good creep resistance (Mg- Al-RE).

  3. Solid solution lithium alloy cermet anodes (United States)

    Richardson, Thomas J.


    A metal-ceramic composite ("cermet") has been produced by a chemical reaction between a lithium compound and another metal. The cermet has advantageous physical properties, high surface area relative to lithium metal or its alloys, and is easily formed into a desired shape. An example is the formation of a lithium-magnesium nitride cermet by reaction of lithium nitride with magnesium. The reaction results in magnesium nitride grains coated with a layer of lithium. The nitride is inert when used in a battery. It supports the metal in a high surface area form, while stabilizing the electrode with respect to dendrite formation. By using an excess of magnesium metal in the reaction process, a cermet of magnesium nitride is produced, coated with a lithium-magnesium alloy of any desired composition. This alloy inhibits dendrite formation by causing lithium deposited on its surface to diffuse under a chemical potential into the bulk of the alloy.

  4. Room temperature creep in metals and alloys

    Energy Technology Data Exchange (ETDEWEB)

    Deibler, Lisa Anne [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Materials Characterization and Performance


    Time dependent deformation in the form of creep and stress relaxation is not often considered a factor when designing structural alloy parts for use at room temperature. However, creep and stress relaxation do occur at room temperature (0.09-0.21 Tm for alloys in this report) in structural alloys. This report will summarize the available literature on room temperature creep, present creep data collected on various structural alloys, and finally compare the acquired data to equations used in the literature to model creep behavior. Based on evidence from the literature and fitting of various equations, the mechanism which causes room temperature creep is found to include dislocation generation as well as exhaustion.

  5. Study of fluoride corrosion of nickel alloys (United States)

    Gunther, W. H.; Steindler, M. J.


    Report contains the results of an investigation of the corrosion resistance of nickel and nickel alloys exposed to fluorine, uranium hexafluoride, and volatile fission product fluorides at high temperatures. Survey of the unclassified literature on the subject is included.


    Directory of Open Access Journals (Sweden)

    Eva Mazancová


    Full Text Available Stacking fault energy of high manganese alloys (marked as TWIP and TRIPLEX is an important parameter determining deformation mechanism type realized in above mentioned alloys. Stacking fault energy level can be asserted with a gliding of partial and/or full dislocations, b gliding mechanism and twinning deformation process in connection with increasing of fracture deformation level (deformation elongation and with increasing of simultaneously realized work hardening proces., c gliding mechanism and deformation induced e-martensite formation. In contribution calculated stacking fault energies are presented for various chemical compositions of high manganese alloys. Stacking fault energy dependences on manganese, carbon, iron and alluminium contents are presented. Results are confronted with some accessible papers.The aim of work is to deepen knowledge of presented data. The TWIP and TRIPLEX alloys can be held for promissing new automotive materials.

  7. Shape Memory Alloy Rock Splitters (SMARS) (United States)

    Benafan, Othmane (Inventor); Noebe, Ronald D. (Inventor)


    Shape memory alloys (SMAs) may be used for static rock splitting. The SMAs may be used as high-energy multifunctional materials, which have a unique ability to recover large deformations and generate high stresses in response to thermal loads.

  8. Hydrogen treatment of titanium based alloys (United States)

    Losertová, M.; Hartmann, M.; Schindler, I.; Drápala, J.


    The positive effect of the hydrogen on hot deformation behaviour at 700 and 750 °C was investigated after thermal hydrogen treatment of Ti6Al4V and Ti26Nb alloys. Comparing the results obtained for the non-hydrogenated and hydrogenated specimens of both alloys, it was found that the hydrogen content as high as 1325 wt. ppm has an obvious benefit effect on high temperature deformation behaviour in the Ti6Al4V alloy by stabilizing beta phase and lowering thermal deformation resistance. In the case of Ti26Nb alloy the hydrogen content of 2572 wt. ppm suppressed stress instabilities during hot compression but slightly increased thermal deformation resistance. The microstructure study was performed before and after the isothermal compression tests on the specimens in hydrogenated as well as in non-hydrogenated condition. The hydrogen amounts in the specimens were measured by means of an analyser LECO RH600.

  9. Simulation and Modeling in High Entropy Alloys (United States)

    Toda-Caraballo, I.; Wróbel, J. S.; Nguyen-Manh, D.; Pérez, P.; Rivera-Díaz-del-Castillo, P. E. J.


    High entropy alloys (HEAs) is a fascinating field of research, with an increasing number of new alloys discovered. This would hardly be conceivable without the aid of materials modeling and computational alloy design to investigate the immense compositional space. The simplicity of the microstructure achieved contrasts with the enormous complexity of its composition, which, in turn, increases the variety of property behavior observed. Simulation and modeling techniques are of paramount importance in the understanding of such material performance. There are numerous examples of how different models have explained the observed experimental results; yet, there are theories and approaches developed for conventional alloys, where the presence of one element is predominant, that need to be adapted or re-developed. In this paper, we review of the current state of the art of the modeling techniques applied to explain HEAs properties, identifying the potential new areas of research to improve the predictability of these techniques.

  10. Alloy solution hardening with solute pairs (United States)

    Mitchell, John W.


    Solution hardened alloys are formed by using at least two solutes which form associated solute pairs in the solvent metal lattice. Copper containing equal atomic percentages of aluminum and palladium is an example.

  11. Stress-corrosion cracking of titanium alloys. (United States)

    Blackburn, M. J.; Feeney, J. A.; Beck, T. R.


    In the light of research material published up to May 1970, the current understanding of the experimental variables involved in the stress-corrosion cracking (SCC) behavior of titanium and its alloys is reviewed. Following a brief summary of the metallurgy and electrochemistry of titanium alloys, the mechanical, electrochemical, and metallurgical parameters influencing SCC behavior are explored with emphasis on crack growth kinetics. Macro- and microfeatures of fractures are examined, and it is shown that many transgranular SCC failures exhibit morphological and crystallographic features similar to mechanical cleavage failures. Current SCC models are reviewed with respect to their ability to explain the observed SCC behavior of titanium and its alloys. Possible methods for eliminating or minimizing stress corrosion hazards in titanium or titanium alloy components are described.

  12. Surface Phases in Binary Liquid Metal Alloys


    Tostmann, Holger; DiMasi, Elaine; Shpyrko, Oleg G.; Ocko, Ben M.; Pershan, Peter S.; Deutsch, Moshe


    Surface sensitive x-ray scattering techniques with atomic scale resolution are employed to investigate the microscopic structure of the surface of three classes of liquid binary alloys: (i) Surface segregation in partly miscible binary alloys as predicted by the Gibbs adsorption rule is investigated for Ga-In. The first layer consists of a supercooled In monolayer and the bulk composition is reached after about two atomic diameters. (ii) The Ga-Bi system displays a wetting transition at a cha...

  13. Internal gettering by metal alloy clusters (United States)

    Buonassisi, Anthony; Heuer, Matthias; Istratov, Andrei A.; Pickett, Matthew D.; Marcus, Mathew A.; Weber, Eicke R.


    The present invention relates to the internal gettering of impurities in semiconductors by metal alloy clusters. In particular, intermetallic clusters are formed within silicon, such clusters containing two or more transition metal species. Such clusters have melting temperatures below that of the host material and are shown to be particularly effective in gettering impurities within the silicon and collecting them into isolated, less harmful locations. Novel compositions for some of the metal alloy clusters are also described.

  14. Degassing of Aluminum Alloys Using Ultrasonic Vibration

    Energy Technology Data Exchange (ETDEWEB)

    Meek, T. T.; Han, Q.; Xu, H.


    The research was intended to lead to a better fundamental understanding of the effect of ultrasonic energy on the degassing of liquid metals and to develop practical approaches for the ultrasonic degassing of alloys. The goals of the project described here were to evaluate core principles, establish a quantitative basis for the ultrasonic degassing of aluminum alloy melts, and demonstrate the application of ultrsaonic processing during ingot casting and foundry shape casting.

  15. Reduction Expansion Synthesis for Magnetic Alloy Powders (United States)


    12 Figure 6. RES Particle Size Distribution Iron-Nickel alloy. .....................................14 Figure 7. Copper Particles a...diameter was less than 150 nm. Finally, it was suggested that the RES technique can be adapted for additional alloys, as well as graphene ...expand RES to wider applications. In [18], RES was used to reduce graphite oxide in order to produce graphene sheets. This study demonstrates the

  16. Titanium and titanium alloys fundamentals and applications

    CERN Document Server

    Peters, Manfred


    This handbook is an excellent reference for materials scientists and engineers needing to gain more knowledge about these engineering materials. Following introductory chapters on the fundamental materials properties of titanium, readers will find comprehensive descriptions of the development, processing and properties of modern titanium alloys. There then follows detailed discussion of the applications of titanium and its alloys in aerospace, medicine, energy and automotive technology.

  17. Phonon broadening in high entropy alloys (United States)

    Körmann, Fritz; Ikeda, Yuji; Grabowski, Blazej; Sluiter, Marcel H. F.


    Refractory high entropy alloys feature outstanding properties making them a promising materials class for next-generation high-temperature applications. At high temperatures, materials properties are strongly affected by lattice vibrations (phonons). Phonons critically influence thermal stability, thermodynamic and elastic properties, as well as thermal conductivity. In contrast to perfect crystals and ordered alloys, the inherently present mass and force constant fluctuations in multi-component random alloys (high entropy alloys) can induce significant phonon scattering and broadening. Despite their importance, phonon scattering and broadening have so far only scarcely been investigated for high entropy alloys. We tackle this challenge from a theoretical perspective and employ ab initio calculations to systematically study the impact of force constant and mass fluctuations on the phonon spectral functions of 12 body-centered cubic random alloys, from binaries up to 5-component high entropy alloys, addressing the key question of how chemical complexity impacts phonons. We find that it is crucial to include both mass and force constant fluctuations. If one or the other is neglected, qualitatively wrong results can be obtained such as artificial phonon band gaps. We analyze how the results obtained for the phonons translate into thermodynamically integrated quantities, specifically the vibrational entropy. Changes in the vibrational entropy with increasing the number of elements can be as large as changes in the configurational entropy and are thus important for phase stability considerations. The set of studied alloys includes MoTa, MoTaNb, MoTaNbW, MoTaNbWV, VW, VWNb, VWTa, VWNbTa, VTaNbTi, VWNbTaTi, HfZrNb, HfMoTaTiZr.

  18. Oxidation of alloys for advanced steam turbines

    Energy Technology Data Exchange (ETDEWEB)

    Holcomb, Gordon R.; Covino, Bernard S., Jr.; Bullard, Sophie J.; Ziomek-Moroz, M.; Alman, David E.


    Ultra supercritical (USC) power plants offer the promise of higher efficiencies and lower emissions. Current goals of the U.S. Department of Energy’s Advanced Power Systems Initiatives include coal generation at 60% efficiency, which would require steam temperatures of up to 760°C. This research examines the steamside oxidation of advanced alloys for use in USC systems, with emphasis placed on alloys for high- and intermediate-pressure turbine sections.

  19. Research and Development on Titanium Alloys (United States)


    are being prepared by the Norton Company for evaluation. Titanium boride , tantalum boride , zirconium boride , tungsten boride , and molybdenum boride ...alloying additionO will be ex- tended. 9 Ternary alloys of manganese and carbon, manganese and vanadium, and molybdenum and tungsten, prepared by...graphite crucibles lined with tantalum carbide and turgsten boride as refractories for molten titanium,. Melts were prepared In crucibles made of zirconium

  20. Ternary alloy nanocatalysts for hydrogen evolution reaction

    Indian Academy of Sciences (India)

    Cu–Fe–Ni ternary alloys (size ∼55–80 nm) with varying compositions viz. CuFeNi (A1), CuFe2Ni (A2) and CuFeNi2 (A3) were successfully synthesized using microemulsion. It is to be noted that synthesis of nanocrystallineternary alloys with precise composition is a big challenge which can be overcome by choosing an ...

  1. Fracture & Fatigue Characteristics in Titanium Alloys. (United States)


    Part III is directed at characterizing internal fatigue crack initiation sites in an a/s alloy. Part I includes a systematic study of the effect of sub...electrochemically polished or shot peened. Prior to fatigue testing, the surface residual stresses were measured in the longitudinal direction using x-ray...alloy) attests to the validity of the phase boundary positions. 7 C/3871A/cb 1 Rockwell International Scince Center SC5227.1FR The compositions of the

  2. Progress in Preparation and Research of High Entropy Alloys

    Directory of Open Access Journals (Sweden)

    CHEN Yong-xing


    Full Text Available The current high entropy alloys' studies are most in block, powder, coating, film and other areas. There are few studies of high entropy alloys in other areas and they are lack of unified classification. According to the current high entropy alloys' research situation, The paper has focused on the classification on all kinds of high entropy alloys having been researched, introduced the selecting principle of elements, summarized the preparation methods, reviewed the research institutions, research methods and research contents of high entropy alloys, prospected the application prospect of high entropy alloys, put forward a series of scientific problems of high entropy alloys, including less research on mechanism, incomplete performance research, unsystematic thermal stability study, preparation process parameters to be optimized, lightweight high entropy alloys' design, the expansion on the research field, etc, and the solutions have been given. Those have certain guiding significance for the expansion of the application of high entropy alloys subjects in the future research direction.

  3. Die casting for high performance - focus on alloy development

    Energy Technology Data Exchange (ETDEWEB)

    Bakke, P.; Westengen, H. [Hydro Aluminium a.s., Magnesium Competence Centre, PO Box 2560, N-Porsgrunn (Norway)


    Development of magnesium die casting alloys is the art of combining a thorough understanding of thermodynamic aspects of alloy composition and phase formation with the solidification kinetics as experienced in the die casting process. The microstructures obtained will determine The Alloy Property profile, which must be in line with the targeted application requirements. Successful development of an industrial alloy means that also The Diecasting Performance profile as well as the Alloy Production and Recycling profile must be fulfilled. In the present paper, a summary of current alloy development efforts will be given. Results from alloy development work by Hydro Magnesium will be presented, focusing mainly on creep resistant alloys. Specifically, alloys within the Mg-Al-RE system are highlighted. (Abstract Copyright [2003], Wiley Periodicals, Inc.)

  4. Development of Advanced Alloys using Fullerenes (United States)

    Sims, J.; Wasz, M.; O'Brien, J.; Callahan, D. L.; Barrera, E. V.


    Development of advanced alloys using fullerenes is currently underway to produce materials for use in the extravehicular mobility unit (EMU). These materials will be directed toward commercial usages as they are continually developed. Fullerenes (of which the most common is C(sub 60)) are lightweight, nanometer size, hollow molecules of carbon which can be dispersed in conventional alloy systems to enhance strength and reduce weight. In this research, fullerene interaction with aluminum is investigated and a fullerene-reinforced aluminum alloy is being developed for possible use on the EMU. The samples were manufactured using standard commercial approaches including powder metallurgy and casting. Alloys have been processed having 1.3, 4.0 and 8.0 volume fractions of fullerenes. It has been observed that fullerene dispersion is related to the processing approach and that they are stable for the processing conditions used in this research. Emphasis will be given to differential thermal analysis and wavelength dispersive analysis of the processed alloys. These two techniques are particularly useful in determining the condition of the fullerenes during and after processing. Some discussion will be given as to electrical properties of fullerene-reinforced materials. Although the aluminum and other advanced alloys with fullerenes are being developed for NASA and the EMU, the properties of these materials will be of interest for commercial applications where specific Dual-Use will be given.

  5. Capacity retention in hydrogen storage alloys (United States)

    Anani, A.; Visintin, A.; Srinivasan, S.; Appleby, A. J.; Reilly, J. J.; Johnson, J. R.


    Results of our examination of the properties of several candidate materials for hydrogen storage electrodes and their relation to the decrease in H-storage capacity upon open-circuit storage over time are reported. In some of the alloy samples examined to date, only about 10 percent of the hydrogen capacity was lost upon storage for 20 days, while in others, this number was as high as 30 percent for the same period of time. This loss in capacity is attributed to two separate mechanisms: (1) hydrogen desorbed from the electrode due to pressure differences between the cell and the electrode sample; and (2) chemical and/or electrochemical degradation of the alloy electrode upon exposure to the cell environment. The former process is a direct consequence of the equilibrium dissociation pressure of the hydride alloy phase and the partial pressure of hydrogen in the hydride phase in equilibrium with that in the electrolyte environment, while the latter is related to the stability of the alloy phase in the cell environment. Comparison of the equilibrium gas-phase dissociation pressures of these alloys indicate that reversible loss of hydrogen capacity is higher in alloys with P(eqm) greater than 1 atm than in those with P(eqm) less than 1 atm.

  6. Nickel-base alloys for severe environments

    Energy Technology Data Exchange (ETDEWEB)

    Wilson, R.K.; Flower, H.L. [Inco Alloys International Inc., Huntington, WV (United States); Hack, G.A.J. [Inco Alloys Ltd., Hereford (United Kingdom); Isobe, S. [Daido Steel Co. Ltd., Nagoya (Japan)


    Inconel alloys MA754 and MA758 are nickel-base, oxide dispersion-strengthened superalloys made by mechanical alloying. The simple nickel-chromium matrix, when combined with the strengthening effect of the yttrium oxide dispersoid during mechanical alloys, provides excellent creep properties, resistance to thermal fatigue, and surface stability suitable for operation without protective coatings. Gas turbine engine components are primary applications for alloy MA754, but this aerospace alloy has been applied in many other products that operate in severe conditions, and alloy MA758 was developed specifically for aggressive, elevated temperature industrial environments. Billets for large bar and plate are typically consolidated by hot isostatic pressing (HIP), because this technology allows production of forms suitable for a variety of industrial components. Material consolidated by HIP and conventionally worked by extrusion and hot rolling generally exhibits properties that are more isotropic than those of material consolidated by extrusion. However, the degree of anisotropy depends strongly on the specific processing of the consolidated billet. This article describes production of new mill shapes from HIP billets, and reviews current and potential applications such as skid rails for high-temperature walking-beam furnaces, heat treating furnace parts, equipment for handling molten glass, and furnace tubes.

  7. New Stainless Steel Alloys for Low Temperature Surface Hardening?

    DEFF Research Database (Denmark)

    Christiansen, Thomas Lundin; Dahl, Kristian Vinter; Somers, Marcel A. J.


    The present contribution showcases the possibility for developing new surface hardenable stainless steels containing strong nitride/carbide forming elements (SNCFE). Nitriding of the commercial alloys, austenitic A286, and ferritic AISI 409 illustrates the beneficial effect of having SNCFE present...... in the stainless steel alloys. The presented computational approach for alloy design enables “screening” of hundreds of thousands hypothetical alloy systems by use of Thermo-Calc. Promising compositions for new stainless steel alloys can be selected based on imposed criteria, i.e. facilitating easy selection...... of candidate alloys designed for low temperature surface hardening....

  8. Comparison of the Oxidation Rates of Some New Copper Alloys (United States)

    Ogbuji, Linus U. J. Thomas; Humphrey, Donald L.


    Copper alloys were studied for oxidation resistance and mechanisms between 550 and 700 C, in reduced-oxygen environments expected in rocket engines, and their oxidation behaviors compared to that of pure copper. They included two dispersion-strengthened alloys (precipitation-strengthened and oxide-dispersion strengthened, respectively) and one solution-strengthened alloy. In all cases the main reaction was oxidation of Cu into Cu2O and CuO. The dispersion-strengthened alloys were superior to both Cu and the solution-strengthened alloy in oxidation resistance. However, factors retarding oxidation rates seemed to be different for the two dispersion-strengthened alloys.

  9. First principles analysis of hydrogen chemisorption on Pd-Re alloyed overlayers and alloyed surfaces

    DEFF Research Database (Denmark)

    Pallassana, Venkataraman; Neurock, Matthew; Hansen, Lars Bruno


    Gradient corrected periodic density functional theory (DFT-GGA) slab calculations were used to examine the chemisorption of atomic hydrogen on various Pd-Re alloyed overlayers and uniformly alloyed surfaces. Adsorption was examined at 33% surface coverage, where atomic hydrogen preferred the thre...

  10. Microstructure and magnetic properties of mechanically alloyed FeSiBAlNi (Nb) high entropy alloys (United States)

    Wang, Jian; Zheng, Zhou; Xu, Jing; Wang, Yan


    In this paper, the effects of milling duration and composition on the microstructure and magnetic properties of equi-atomic FeSiBAlNi and FeSiBAlNiNb high entropy alloys during mechanical alloying have been investigated using X-ray diffraction, differential scanning calorimetry, scanning electron microscopy, transmission electron microscopy and alternating gradient magnetometry. The amorphous high entropy alloys have been successfully fabricated using the mechanical alloying method. The results show that the Nb addition prolongs the milling time for the formation of the fully FeSiBAlNi amorphous phase and decreases the glass forming ability. However, FeSiBAlNiNb amorphous high entropy alloy has the higher thermal stability and heat resisting properties. Moreover, the as-milled FeSiBAlNi(Nb) powders are soft-magnetic materials indicated by their low coercivity. The saturation magnetization of the as-milled FeSiBAlNi(Nb) powders decreases with prolonging of the milling time and shows the lowest value when the amorphous high entropy alloys are formed. It suggests that the as-milled products with solid solution phases show the better soft-magnetic properties than those with fully amorphous phases. The Nb addition does not improve the soft-magnetic properties of the FeSiBAlNi high entropy alloys. Rather, both amorphous high entropy alloys have similar soft-magnetic properties after a long milling time.


    DEFF Research Database (Denmark)


    An electroplating method of forming platings of nickel, cobalt, nickel alloys or cobalt alloys with reduced stresses in an electrodepositing bath of the type: Watt's bath, chloride bath or a combination thereof, by employing pulse plating with periodic reverse pulse and a sulfonated naphthalene...... additive. This method makes it possible to deposit nickel, cobalt, nickel or cobalt platings without internal stresses....

  12. Effect of alloy elements on the anti-corrosion properties of low alloy ...

    Indian Academy of Sciences (India)


    Abstract. Effect of alloy elements on corrosion of low alloy steel was studied under simulated offshore condi- tions. The results showed that the elements Cu, P, Mo, W, V had evident effect on corrosion resistance in the atmosphere zone; Cu, P, V, Mo in the splash zone and Cr, Al, Mo in the submerged zone. Keywords.

  13. Nano-sized Superlattice Clusters Created by Oxygen Ordering in Mechanically Alloyed Fe Alloys (United States)

    Hu, Yong-Jie; Li, Jing; Darling, Kristopher A.; Wang, William Y.; VanLeeuwen, Brian K.; Liu, Xuan L.; Kecskes, Laszlo J.; Dickey, Elizabeth C.; Liu, Zi-Kui


    Creating and maintaining precipitates coherent with the host matrix, under service conditions is one of the most effective approaches for successful development of alloys for high temperature applications; prominent examples include Ni- and Co-based superalloys and Al alloys. While ferritic alloys are among the most important structural engineering alloys in our society, no reliable coherent precipitates stable at high temperatures have been found for these alloys. Here we report discovery of a new, nano-sized superlattice (NSS) phase in ball-milled Fe alloys, which maintains coherency with the BCC matrix up to at least 913 °C. Different from other precipitates in ferritic alloys, this NSS phase is created by oxygen-ordering in the BCC Fe matrix. It is proposed that this phase has a chemistry of Fe3O and a D03 crystal structure and becomes more stable with the addition of Zr. These nano-sized coherent precipitates effectively double the strength of the BCC matrix above that provided by grain size reduction alone. This discovery provides a new opportunity for developing high-strength ferritic alloys for high temperature applications. PMID:26134420

  14. Study on microstructure and properties of Mg-alloy surface alloying layer fabricated by EPC

    Directory of Open Access Journals (Sweden)

    Chen Dongfeng


    Full Text Available AZ91D surface alloying was investigated through evaporative pattern casting (EPC technology. Aluminum powder (0.074 to 0.104 mm was used as the alloying element in the experiment. An alloying coating with excellent properties was fabricated, which mainly consisted of adhesive, co-solvent, suspending agent and other ingredients according to desired proportion. Mg-alloy melt was poured under certain temperature and the degree of negative pressure. The microstructure of the surface layer was examined by means of scanning electron microscopy. It has been found that a large volume fraction of network new phases were formed on the Mg-alloy surface, the thickness of the alloying surface layer increased with the alloying coating increasing from 0.3 mm to 0.5 mm, and the microstructure became compact. Energy dispersive X-ray (EDX analysis was used to determine the chemical composition of the new phases. It showed that the new phases mainly consist of β-Mg17Al12, in addition to a small quantity of inter-metallic compounds and oxides. A micro-hardness test and a corrosion experiment to simulate the effect of sea water were performed. The result indicated that the highest micro-hardness of the surface reaches three times that of the matrix. The corrosion rate of alloying samples declines to about a fifth of that of the as-cast AZ91D specimen.

  15. Corrosion and wear protective composition modulated alloy coatings based on ternary Ni-P-X alloys

    DEFF Research Database (Denmark)

    Leisner, P.; Benzon, M. E.; Christoffersen, Lasse


    Scattered reporting in the litterature describes a number of ternary Ni-P-X alloyes (where X can be Co, Cr, Cu, Mo, Pd, Re or W) with promising corrosin and wear protective performance. Based on a systematic study of Ni-P-X alloys it is the intention to produce coatings with improved corrosion...

  16. Hot workability of magnesium alloys (United States)

    Mwembela, Aaron Absalom

    For the alloy AZ91 (Mg-9.OAl-0.7Zn-0.13Mn) die cast specimens were subjected to torsion testing at 150, 180, 240, 300, 420 and 450°C at 0.05 0.5 and 5.0 s--1 The as-cast specimens exhibited hot shortness at 360°C and above; however in that domain, after prior thermomechanical processing (TMP) at 300°C, they showed much improved properties (which were reported along with as-cast properties at 300°C and below). For AZ31-Mn (Mg-3.2Al-1-1Zn-0.34Mn), AZ31 (Mg-2-8Al-0-88Zn-0.01Mn), AZ63 (Mg-5-5Al-2.7Zn-0.34Mn) and ZK60 (Mg-5.7Zn-0.65Zr-O-O1A]), the specimens were subjected to hot torsion testing in the range 180 to 450°C and 0.01, 0.1, and 1.0 s--1. In the temperature range below 300°C flow curves rise to a peak with failure occurring immediately thereafter. Above 300°C the flow curves exhibited a peak and a gradual decline towards steady state. The temperature and strain rate dependence of the strength is described by a sinh-Arrhenius equation with QHW between 125 and 144 kJ/mol; this indicates control by climb in comparison with creep in the range 200--400°C. The alloy strength and activation energy declined in the order AZ63, AZ31-Mn AZ91, AZ31 and ZK60, while ductility increased with decreasing strength. In working of Mg alloys from 150 to 450°C, the flow curves harden to a peak and work soften to a steady state regime above 300°C. At temperatures below 300°C, twinning is observed initially to bring grains into more suitable slip orientations. At high T a substructure develops due to basal and prismatic slip, Forming cells of augmented misorientation first near the grain boundaries and later towards the grain cores. Near the peak, new grains appear along the old boundaries (mantle) as a result of dynamic recrystallization DRX but not in the core of the initial grains. As T rises, the new grains are larger and the mantle broader, enhanced DRX results in higher ductility. At intermediate T, shear bands form through alignment of mantle zones resulting in

  17. Catalytic properties of Ni-Zn alloy prepared by mechanical alloying for steam reforming from methanol (United States)

    Park, Jeshin; Kim, Wonbaek; Suh, Changyoul; Kim, Sangbae


    Amorphous Zn65Ni35 alloy, the composition of which lies between β1-NiZn and γ-NiZn phases, was prepared by mechanical alloying for 200 hours. The alloy was heat treated at various temperatures and leached in NaOH solution in an effort to enhance the catalytic properties for hydrogen production from methanol. X-ray diffraction study revealed that the amorphous phase crystallized during the heat treatment to the equilibrium β1-NiZn and γ-NiZn phases. It was found that Zn65Ni35 alloy leached after heat treatment at 928 K showed the highest catalytic activity for steam reforming of methanol. It is believed that the enhanced catalytic activity of the Zn65Ni35 alloy heat treated at 928 K is due to the dispersed Ni particles on β1-ZnNi matrix which was formed during leaching of the γ-Zn21Ni5 phase.

  18. Method for producing La/Ce/MM/Y base alloys, resulting alloys and battery electrodes (United States)

    Gschneidner, Jr., Karl A.; Schmidt, Frederick A.


    A carbothermic reduction method is provided for reducing a La-, Ce-, MM-, and/or Y-containing oxide in the presence of carbon and a source of a reactant element comprising Si, Ge, Sn, Pb, As, Sb, Bi, and/or P to form an intermediate alloy material including a majority of La, Ce, MM, and/or Y and a minor amount of the reactant element. The intermediate material is useful as a master alloy for in making negative electrode materials for a metal hydride battery, as hydrogen storage alloys, as master alloy additive for addition to a melt of commercial Mg and Al alloys, steels, cast irons, and superalloys; or in reducing Sm.sub.2O.sub.3 to Sm metal for use in Sm--Co permanent magnets.

  19. Development of Creep Resistant Mg-Al-Sr Alloys (United States)

    Pekguleryuz, Mihriban O.; Baril, Eric

    There have been attempts since in the 70's to develop creep resistant magnesium diecasting alloys for automotive applications such as automatic-transmission case and engine components. The earliest die casting alloys developed as a result of these activities were the Mg-Al- RE and Mg-Al-Si systems (AE and AS alloys). The shortcomings of these two alloy systems related to high cost or borderline properties have led to renewed activity in the 90's in the development of magnesium alloys with improved elevaied-temperature properties. This paper presents the development of a new family of creep-resistant Mg alloys based on the Mg-Al-Sr system. Creep resistance, the tensile yield strength and the bolt-load-retention of these alloys at 150°C and 175°C show improvement over Mg-Al-RE and Mg-Al-Si system. The microstructure of the alloys is characterized by Al-Sr-(Mg) containing intermetallic second phases. The absence of the Mg17Al12 phase in the microstructure, either creep-induced or as-cast, is one of the factors that contribute to improved creep-resistance of these alloys over the Mg-Al based diecasting alloys. Furthermore, the alloys exhibit better salt-spray corrosion resistance (0.09-0.15mg/cm2/day) than other commercial magnesium diecasting alloys such as AM60B, AS41, AE42 and the aluminum diecasting alloy A380.

  20. Experimental titanium alloys for dental applications. (United States)

    Faria, Adriana C L; Rodrigues, Renata C S; Rosa, Adalberto L; Ribeiro, Ricardo F


    Although the use of titanium has increased, casting difficulties limit routine use. The purpose of the present study was to compare the mechanical properties and biocompatibility of the experimental titanium alloys titanium-5-zirconium, titanium-5-tantalum, and titanium-5-tantalum-5-zirconium (in wt%) with those of commercially pure titanium. Specimens of titanium alloys and commercially pure titanium were cast by using plasma. Their modulus of elasticity and ultimate tensile strength were determined in a universal testing machine. Biocompatibility was evaluated with SCC9 cells. In periods of 1, 4, 7, 10, and 14 days, cell proliferation was evaluated by the (3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide) tetrazolium reduction assay, and cell viability was evaluated in the 7-day period. Cell morphology was evaluated at 2, 12, and 24 hours. Modulus of elasticity, ultimate tensile strength, and cell viability were analyzed by 1-way ANOVA and the Bonferroni test; cell proliferation data were compared by 2-way ANOVA (alloy versus time) and by the Bonferroni test; and the cell morphology data were analyzed by split-plot design. All statistical tests were performed at the 95% confidence level (Ptantalum presented the lowest modulus of elasticity and ultimate tensile strength, whereas titanium-5-zirconium and titanium-5-tantalum-5-zirconium were statistically similar to commercially pure titanium. Cell proliferation and viability were not affected by any alloy being similar to those observed for commercially pure titanium. No noticeably differences were found in the morphology of cells cultured on any alloy and commercially pure titanium. Experimental alloys, especially titanium-5-zirconium and titanium-5-tantalum-5-zirconium, presented promising mechanical results for future studies and clinical applications. In addition, these alloys, evaluated by cell proliferation, viability, and morphology, were found to be biocompatible in vitro. Copyright © 2014

  1. Significance of exercise-induced ST segment depression in patients with myocardial infarction involving the left circumflex artery. Evaluation by exercise thallium-201 myocardial single photon emission computed tomography

    Energy Technology Data Exchange (ETDEWEB)

    Koitabashi, Norimichi; Toyama, Takuji; Hoshizaki, Hiroshi [Gunma Prefectural Cardiovascular Center, Maebashi (Japan)] [and others


    The significance of exercise-induced ST segment depression in patients with left circumflex artery involvement was investigated by comparing exercise electrocardiography with exercise thallium-201 single photon emission computed tomography (Tl-SPECT) and the wall motion estimated by left ventriculography. Tl-SPECT and exercise electrocardiography were simultaneously performed in 51 patients with left circumflex artery involvement (angina pectoris 30, myocardial infarction 21). In patients with myocardial infarction, exercise-induced ST depression was frequently found in the V{sub 2}, V{sub 3} and V{sub 4} leads. In patients with angina pectoris, ST depression was frequently found in the II, III, aV{sub F}, V{sub 5} and V{sub 6} leads. There was no obvious difference in the leads of ST depression in patients with myocardial infarction with ischemia and without ischemia on Tl-SPECT images. In patients with myocardial infarction, the lateral wall motion of the infarcted area evaluated by left ventriculography was more significantly impaired in the patients with ST depression than without ST depression (p<0.01). Exercise-induced ST depression in the precordial leads possibly reflects wall motion abnormality rather than ischemia in the lateral infarcted myocardium. (author)

  2. Surface Features of Nanocrystalline Alloys

    Directory of Open Access Journals (Sweden)

    Marcel Miglierini


    Full Text Available Nanocrystalline alloys are prepared by controlled annealing of metallic glass precursors. The latter are obtained by rapid quenching of a melt on a rotating wheel. This process leads to structural deviation of the produced ribbons’ surfaces. Structural features of as-quenched and thermally annealed 57Fe81Mo8Cu1B10 ribbons were studied employing Conversion Electron Mössbauer Spectrometry (CEMS and Conversion X-ray Mössbauer Spectrometry (CXMS. Enrichment of the alloy’s composition in 57Fe helped in identification of surface crystallites that were formed even during the production process. Magnetite and bcc-Fe were found at the wheel side of the as-quenched ribbons whereas only bcc-Fe nanocrystals were uncovered at the opposite air side. Accelerated formation of bcc-Fe was observed in this side of the ribbons after annealing. The relative content of magnetite at the wheel side was almost stable in near surface areas (CEMS and in more deep subsurface regions (CXMS. It vanished completely after annealing at 550 °C. No magnetite was observed at the air side of the ribbons regardless the annealing temperature and/or depth of the scanned regions.

  3. Bismuth alloy potting seals aluminum connector in cryogenic application (United States)

    Flower, J. F.; Stafford, R. L.


    Bismuth alloy potting seals feedthrough electrical connector for instrumentation within a pressurized vessel filled with cryogenic liquids. The seal combines the transformation of high-bismuth content alloys with the thermal contraction of an external aluminum tube.

  4. Assessment of Al-Li Alloys for Cryotanks (United States)

    Babel, Henry W.; Bozich, William; Farahmand, Bob; DeJesus, Ron; Sankaran, K. K.; Schwab, Dave; Tarkanian, Mike; Funk, Joan G. (Technical Monitor)


    This viewgraph presentation provides information on steps undertaken to determine the suitability of Aluminum and Lithium alloys in cryogenic tank construction. Major characteristics are offered for several different candidate alloys including reliability, weldability, flammability, and required thicknesses.

  5. The Origin of the Name "Onion's Fusible Alloy" (United States)

    Jensen, William B.


    In response to a reader query, this article traces the history of fusible alloys, including Newton's metal, D'Arcet's metal, Rose's metal, Onion's fusible alloy, and Wood's metal. (Contains 1 table and 1 figure.)

  6. Impact and modal analysis for different alloy wheel compositions (United States)

    Suman, Shwetabh; Abhimanyu Abrol, J.; Ravi, K.


    Wheels are an important component in the vehicle. The strength of the Alloy wheel rim is an important property of the Alloy wheel, which plays an important part in determining the overall performance of the vehicle, the structural integrity of the rim and the life of the Alloy wheel rim. With the advent of new Alloy wheel materials, new options are available to replace the conventional Aluminium Alloy wheels with new ones. The new Alloy wheel rim material and design need to be tested virtually for optimizing the appropriate design and material and the optimised wheel in virtual mode can be tested experimentally for the performance in real-time conditions before they can be used in the vehicles. The work in this project includes doing the impact and modal analysis for different alloy wheel compositions. From the results obtained, the optimum alloy wheel is suggested, which can be considered with further experimental validation.


    Directory of Open Access Journals (Sweden)

    О. V. Diachenko


    Full Text Available The paper is devoted to investigations on influence of laser treatment regimes of gas-thermal and adhesive coatings from self-fluxing powders on iron basis and after melting with modifying plaster on their roughness and phase composition. One of mathematical planning methods that is a complete factor experiment method has been used for investigation of parameters’ influence on micro-geometry of coatings. The executed investigations have made it possible to observe a general regularity which does not depend on a type of alloying plaster: while increasing speed of laser beam relatively to treated part, beam diameter value of Ra parameter is becoming less. Decrease in height of surface irregularities in case of increasing laser beam speed is related with intensification of evaporation processes. An increase in beam diameter diminishes Ra parameter of the surface. This is due to the fact that decrease in power density occurs at high rate of beam defocusing. Overlapping coefficient does not exert a pronounced effect on Ra parameter of fused coatings. While increasing the speed of laser beam relatively to the part structure is transferred from dendrite into supersaturated one with carbide and boride precipitations. It has been established that technological parameters of laser treatment and particularly speed of laser beam influence on coating composition. While increasing the speed up to v5 = 5 × 10–3 m/s amount of chromium has become larger by 1.5-fold that resulted in increase of micro-hardness of the coating from 9.5–10.1 GPa up to 11.04–15.50 GPa.

  8. Electromigration testing of Al alloy films (United States)

    Ghate, P. B.


    A search for reliability improvement of Al film interconnections has led to the introduction of Al-Alloy films such as Al-Cu, Al-Cu-Si and so on. This report describes the results of an in-depth study of Al, Al-Cu (2 wt % Cu) and Al-Cu-Si (2 wt % Cu - 1% Si) film interconnections and Silicon/Al-Alloy film contacts as they impact reliability of integrated circuits. Resistivity, microstructure and composition of Al-Alloy films vacuum deposited from an induction heated source (IN-Source) and dc magnetron sputter deposition techniques have been investigated and it is concluded that IN-Source and dc magnetron sputter deposition techniques are equally capable of producing Al, Al-Cu (2 wt %) and Al-Cu-Si (2 wt % Cu - 1% Si) films of comparable compositions, resistivity and microstructure. Chemical analysis X-ray fluorescence electron microprobe, scanning and transmission electron microscopy and ion microprobe have been employed for Al-Alloy film characterization. Availability of automated dc magnetron sputter (M-S) deposition equipment was a primary factor in the selection of magnetron sputter deposited Al-Alloy films for electromigration testing.

  9. Precision forging technology for aluminum alloy (United States)

    Deng, Lei; Wang, Xinyun; Jin, Junsong; Xia, Juchen


    Aluminum alloy is a preferred metal material for lightweight part manufacturing in aerospace, automobile, and weapon industries due to its good physical properties, such as low density, high specific strength, and good corrosion resistance. However, during forging processes, underfilling, folding, broken streamline, crack, coarse grain, and other macro- or microdefects are easily generated because of the deformation characteristics of aluminum alloys, including narrow forgeable temperature region, fast heat dissipation to dies, strong adhesion, high strain rate sensitivity, and large flow resistance. Thus, it is seriously restricted for the forged part to obtain precision shape and enhanced property. In this paper, progresses in precision forging technologies of aluminum alloy parts were reviewed. Several advanced precision forging technologies have been developed, including closed die forging, isothermal die forging, local loading forging, metal flow forging with relief cavity, auxiliary force or vibration loading, casting-forging hybrid forming, and stamping-forging hybrid forming. High-precision aluminum alloy parts can be realized by controlling the forging processes and parameters or combining precision forging technologies with other forming technologies. The development of these technologies is beneficial to promote the application of aluminum alloys in manufacturing of lightweight parts.

  10. Amorphous Alloy Surpasses Steel and Titanium (United States)


    In the same way that the inventions of steel in the 1800s and plastic in the 1900s sparked revolutions for industry, a new class of amorphous alloys is poised to redefine materials science as we know it in the 21st century. Welcome to the 3rd Revolution, otherwise known as the era of Liquidmetal(R) alloys, where metals behave similar to plastics but possess more than twice the strength of high performance titanium. Liquidmetal alloys were conceived in 1992, as a result of a project funded by the California Institute of Technology (CalTech), NASA, and the U.S. Department of Energy, to study the fundamentals of metallic alloys in an undercooled liquid state, for the development of new aerospace materials. Furthermore, NASA's Marshall Space Flight Center contributed to the development of the alloys by subjecting the materials to testing in its Electrostatic Levitator, a special instrument that is capable of suspending an object in midair so that researchers can heat and cool it in a containerless environment free from contaminants that could otherwise spoil the experiment.

  11. [Superplastic forming of titanium alloy denture base]. (United States)

    Okuno, O; Nakano, T; Hamanaka, H; Miura, I; Ito, M; Ai, M; Okada, M


    Ti-6Al-4V alloy has both excellent biocompatibility and superior mechanical properties. This Ti-6Al-4V can be deformed greatly and easily at the superplastic temperature of 800 degrees C to 900 degrees C. The superplastic forming of Ti-6Al-4V was made to apply to fabrication of denture base. Almost the same procedure as for dental casting mold was employed in producing the superplastic forming die by the improved phosphate bonded investment. In the pressure vessel of heat resistant alloy, Ti-6Al-4V plate was formed superplastically on the die by argon gas pressure at 850 degrees C. The fit of superplactic forming Ti-6Al-4V denture base was better than that of casting Co-Cr alloy denture bases. The Ti-6Al-4V alloy might react a little with the die. Because micro Vikers hardness of the cross-section did not go up too much near the surfaces. Even just after being formed, the surfaces were much smoother than that of Co-Cr alloy casting. The tensile strength and yield strength of superplastic forming Ti-6Al-4V were higher than those of Co-Cr castings. The elongation was about 10%. These results show that superplastic forming of Ti-6Al-4V would be suitable for a denture base.

  12. The effect of remelting various combinations of new and used cobalt-chromium alloy on the mechanical properties and microstructure of the alloy

    Directory of Open Access Journals (Sweden)

    Sharad Gupta


    Conclusion: Repeated remelting of base metal alloy for dental casting without addition of new alloy can affect the mechanical properties of the alloy. Microstructure analysis shows deterioration upon remelting. However, the addition of 25% and 50% (by weight of new alloy to the remelted alloy can bring about improvement both in mechanical properties and in microstructure.

  13. Microstructure and Aging of Powder-Metallurgy Al Alloys (United States)

    Blackburn, L. B.


    Report describes experimental study of thermal responses and aging behaviors of three new aluminum alloys. Alloys produced from rapidly solidified powders and contain 3.20 to 5.15 percent copper, 0.24 to 1.73 percent magnesium, 0.08 to 0.92 percent iron, and smaller amounts of manganese, nickel, titanium, silicon, and zinc. Peak hardness achieved at lower aging temperatures than with standard ingot-metallurgy alloys. Alloys of interest for automobile, aircraft, and aerospace applications.

  14. Effective and Environmentally Friendly Nickel Coating on the Magnesium Alloy


    Ivana Škugor Rončević; Mirjana Metikoš-Huković; Marijo Buzuk; Nives Vladislavić


    The low density and good mechanical properties make magnesium and its alloys attractive construction materials in the electronics, automotive, and aerospace industry, together with application in medicine due to their biocompatibility. Magnesium AZ91D alloy is an alloy with a high content of aluminum, whose mechanical properties overshadow the low corrosion resistance caused by the composition of the alloy and the existence of two phases: α magnesium matrix and β magnesium aluminum intermetal...

  15. [Metallurgical differentiation of cobalt-chromium alloys for implants]. (United States)

    Holzwarth, U; Thomas, P; Kachler, W; Göske, J; Schuh, A


    Cobalt Chromium alloys are used in cemented total hip or knee arthroplasty as well as in metal-on-metal bearings in total hip arthroplasty. An increasing number of publications report about (allergic) reactions to wear particles of Cobalt Chromium alloys. Reactions to nickel are more frequent in comparison to Cobalt or Chromium particles. It is well known that different kinds of Cobalt Chromium alloys contain different amounts of alloying elements; nevertheless. The aim of the current work was to compare the different Cobalt Chromium alloys according to ASTM F or ISO standards in respect to the different alloying elements. Co28Cr6Mo casting alloys according to ASTM F 75 or ISO 5832-4 as well as forging alloy types according to ASTM F 799 and ISO 5832 such as Co20Cr15W10Ni, Co35Ni20Cr, Fe40Co20Cr10Ni, Co20Cr20Ni, and Co28Cr6Mo were analyzed in respect to their element content of Co, Cr, Ni, Mo, Fe, W, and Mn. In 1935 the Cobalt based alloy "Vitallium" Co30Cr5Mo basically used in the aircraft industry was introduced into medicine. The chemical composition of this alloy based on Cobalt showed 30 wt.% Chromium and 5 wt.% Molybdenum. The differentiation using alloy names showed no Nickel information in single alloy names. The information given about different alloys can lead to an unprecise evaluation of histopathological findings in respect to alloys or alloying constituents. Therefore, implant manufacturers should give the exact information about the alloys used and adhere to European law, Euronorm 93/42/EWG.

  16. Excessively High Vapor Pressure of Al-based Amorphous Alloys


    Jeong, Jae; Lee, Sung; Jeon, Je-Beom; Kim, Suk


    Aluminum-based amorphous alloys exhibited an abnormally high vapor pressure at their approximate glass transition temperatures. The vapor pressure was confirmed by the formation of Al nanocrystallites from condensation, which was attributed to weight loss of the amorphous alloys. The amount of weight loss varied with the amorphous alloy compositions and was inversely proportional to their glass-forming ability. The vapor pressure of the amorphous alloys around 573 K was close to the va...

  17. Microstructures and properties of aluminum die casting alloys

    Energy Technology Data Exchange (ETDEWEB)

    M. M. Makhlouf; D. Apelian; L. Wang


    This document provides descriptions of the microstructure of different aluminum die casting alloys and to relate the various microstructures to the alloy chemistry. It relates the microstructures of the alloys to their main engineering properties such as ultimate tensile strength, yield strength, elongation, fatigue life, impact resistance, wear resistance, hardness, thermal conductivity and electrical conductivity. Finally, it serves as a reference source for aluminum die casting alloys.


    Directory of Open Access Journals (Sweden)

    A. V. Alifanov


    Full Text Available The alloys of Fe-Cr-Ni-C system for the purpose of development the economic alloy paramagnetic (not magnetic steels are investigated. A series of alloys are melted for this purpose, deformation is carried out and a structural state was studied.The area for the selection of the chemical composition of the economic alloy steels with stable paramagnetic properties is defined.

  19. Microstructure of Cast Ni-Cr-Al-C Alloy


    Cios G.; Bała P.; Stępień M.; Górecki K.


    Nickel based alloys, especially nickel based superalloys have gained the advantage over other alloys in the field of high temperature applications, and thus become irreplaceable at high temperature creep and aggressive corrosion environments, such as jet engines and steam turbines. However, the wear resistance of these alloys is insufficient at high temperatures. This work describes a microstructure of a new cast alloy. The microstructure consists of γ matrix strengthened by γ’ fine precipita...

  20. Development and Processing Improvement of Aerospace Aluminum Alloys-Development of AL-Cu-Mg-Ag Alloy (2139) (United States)

    Cho, Alex; Lisagor, W. Barry; Bales, Thomas T.


    This final report supplement in presentation format describes a comprehensive multi-tasked contract study to continue the development of the silver bearing alloy now registered as aluminum alloy 2139 by the Aluminum Association. Two commercial scale ingots were processed into nominal plate gauges of two, four and six inches, and were extensively characterized in terms of metallurgical and crystallographic structure, and resulting mechanical properties. This report includes comparisons of the property combinations for this alloy and 2XXX and 7XXX alloys more widely used in high performance applications. Alloy 2139 shows dramatic improvement in all combinations of properties, moreover, the properties of this alloy are retained in all gauge thicknesses, contrary to typical reductions observed in thicker gauges of the other alloys in the comparison. The advancements achieved in this study are expected to result in rapid, widespread use of this alloy in a broad range of ground based, aircraft, and spacecraft applications.

  1. Microstructure and mechanical properties of laser treated aluminium alloys

    NARCIS (Netherlands)

    deHosson, JTM; vanOtterloo, LDM; Noordhuis, J; Mazumder, J; Conde, O; Villar, R; Steen, W


    Al-Cu alloys and an Al-Cu-Mg alloy, Al 2024-T3, were exposed to laser treatments at various scan velocities. In this paper the microstructural features and mechanical properties are reported. As far as the mechanical property of the Al-Cu-Mg alloy is concerned a striking observation is a minimum in

  2. Thixomolded magnesium alloys: Strategic product innovation in automobiles (United States)

    D'Errico, F.; Rivolta, B.; Gerosa, R.; Perricone, G.


    The research on magnesium alloys for structural lightweight applications is today at an embryonic stage, but these alloys offer great potential. Thixomolding of magnesium alloys for automotive applications is promising since the process can be used to manufacture net-shape parts cost-effectively and with high reliability and repeatability.

  3. Lead and lead-based alloys as waste matrix materials

    Energy Technology Data Exchange (ETDEWEB)

    Arustamov, A.E.; Ojovan, M.I.; Kachalov, M.B.


    Metals and alloys with relatively low melting temperatures such as lead and lead-based alloys are considered in Russia as prospective matrices for encapsulation of spent nuclear fuel in containers in preparation for final disposal in underground repositories. Now lead and lead-based alloys are being used for conditioning spent sealed radioactive sources at radioactive waste disposal facilities.

  4. Fatigue Analysis of Magnesium Alloys Components for Car Industry (United States)

    Marsavina, Liviu; Rusu, Lucian; Șerban, Dan Andrei; Negru, Radu Marcel; Cernescu, Anghel


    The use of magnesium alloys in the automotive industry increased in the last decade because of their low weight and relative good mechanical properties. However, the variable loading conditions require a good fatigue behavior. This paper summaries the fatigue properties of magnesium alloys and presents new fatigue curve results for die cast AM50 magnesium alloy.

  5. Sulfuric Acid Corrosion of Low Sb - Pb Battery Alloys | Ntukogu ...

    African Journals Online (AJOL)

    The corrosion properties of low Sb - Pb alloys developed for maintenance free motive power industrial batteries was studied by a bare grid constant current method and compared to those of the conventional Pb- 6% Sb alloy. Low Sb-Pb alloys with Se and As grain refiners were found to have higher corrosion rates than the ...

  6. Effects and mechanisms of grain refinement in aluminium alloys

    Indian Academy of Sciences (India)

    Grain refinement plays a crucial role in improving characteristics and properties of cast and wrought aluminium alloys. Generally Al–Ti and Al–Ti–B master alloys are added to the aluminium alloys to grain refine the solidified product. The mechanism of grain refinement is of considerable controversy in the scientific literature ...

  7. Friction factor of CP aluminium and aluminium–zinc alloys

    Indian Academy of Sciences (India)

    Friction factor has been determined for CP aluminium and aluminium–zinc alloys using ring compression test at different temperatures from 303 K to 773 K. It is found that CP aluminium exhibits sticking whereas Al–Zn alloys do not exhibit sticking at elevated temperatures. Hot working of Al–Zn alloy is easier than that of CP ...

  8. Residual stress state in titanium alloy remelted using GTAW method

    Directory of Open Access Journals (Sweden)

    A. Dudek


    Full Text Available Test materials comprised two-phase titanium alloy Ti6Al4V (Grade5. The surface of the tested alloy was remelted by means of TIG welding method using variable current-voltage parameters. The investigations aimed to determine surface geometry and residual stresses in the remelted surface layer in the investigated alloy.

  9. Friction factor of CP aluminium and aluminium–zinc alloys

    Indian Academy of Sciences (India)

    zinc alloys using ring compression test at different temperatures from 303 K to 773 K. It is found that CP aluminium exhibits stick- ing whereas Al–Zn alloys do not exhibit sticking at elevated temperatures. Hot working of Al–Zn alloy is easier.

  10. 21 CFR 872.3060 - Noble metal alloy. (United States)


    ... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Noble metal alloy. 872.3060 Section 872.3060 Food... DEVICES DENTAL DEVICES Prosthetic Devices § 872.3060 Noble metal alloy. (a) Identification. A noble metal alloy is a device composed primarily of noble metals, such as gold, palladium, platinum, or silver, that...

  11. 21 CFR 872.3710 - Base metal alloy. (United States)


    ... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Base metal alloy. 872.3710 Section 872.3710 Food... DEVICES DENTAL DEVICES Prosthetic Devices § 872.3710 Base metal alloy. (a) Identification. A base metal alloy is a device composed primarily of base metals, such as nickel, chromium, or cobalt, that is...

  12. Nanostructured Platinum Alloys for Use as Catalyst Materials (United States)

    Hays, Charles C. (Inventor); Narayan, Sri R. (Inventor)


    A series of binary and ternary Pt-alloys, that promote the important reactions for catalysis at an alloy surface; oxygen reduction, hydrogen oxidation, and hydrogen and oxygen evolution. The first two of these reactions are essential when applying the alloy for use in a PEMFC.

  13. Nitriding of super alloys for enhancing physical properties (United States)

    Purohit, A.


    The invention teaches the improvement of certain super alloys by exposing the alloy to an atmosphere of elemental nitrogen at elevated temperatures in excess of 750/sup 0/C but less than 1150/sup 0/C for an extended duration, viz., by nitriding the surface of the alloy, to establish barrier nitrides of the order of 25 to 100 micrometers thickness. These barrier

  14. 21 CFR 872.3080 - Mercury and alloy dispenser. (United States)


    ... 21 Food and Drugs 8 2010-04-01 2010-04-01 false Mercury and alloy dispenser. 872.3080 Section 872...) MEDICAL DEVICES DENTAL DEVICES Prosthetic Devices § 872.3080 Mercury and alloy dispenser. (a) Identification. A mercury and alloy dispenser is a device with a spring-activated valve intended to measure and...

  15. Effects and mechanisms of grain refinement in aluminium alloys

    Indian Academy of Sciences (India)


    Abstract. Grain refinement plays a crucial role in improving characteristics and properties of cast and wrought aluminium alloys. Generally Al–Ti and Al–Ti–B master alloys are added to the aluminium alloys to grain refine the solidified product. The mechanism of grain refinement is of considerable controversy in the scientific ...

  16. Preferential dissolution behaviour in Ni–Cr dental cast alloy

    Indian Academy of Sciences (India)


    Ni–Cr–Mo; dental cast alloy; microstructure; corrosion; cyclic polarization. 1. Introduction. Co and Ni based alloys are widely used in dental skeletal structures and orthopedic implants such as screws, pins and plates (Wataha 2000). The advantages of these alloys include low cost of casting, matching thermal expansion.


    The paper describes work, done in 1957-58, in the course of the development of the high-temperature (HT) Ti alloy currently termed BT9(VT9). requirements for the new alloy specified the development of a Ti alloy for forging billets and stamping blanks which at 500 degrees centigrade

  18. Mechanical evaluation of cerebral aneurysm clip scissoring phenomenon: comparison of titanium alloy and cobalt alloy. (United States)

    Tsutsumi, Keiji; Horiuchi, Tetsuyoshi; Hongo, Kazuhiro


    Cerebral aneurysm clip blades crossing during surgery is well known as scissoring. Scissoring might cause rupture of the aneurysm due to laceration of its neck. Although aneurysm clip scissoring is well known, there have been few reports describing the details of this phenomenon. Quasi-scissoring phenomenon was introduced mechanically by rotating the clip head attached to a silicone sheet. The anti-scissoring torque during the twist of the blades was measured by changing the depth and the opening width. The closing force was also evaluated. Sugita straight clips of titanium alloy and cobalt alloy were used in the present study. In both materials, the anti-scissoring torque and the closing force were bigger 3 mm in thickness than 1 mm. The initial closing forces and the anti-scissoring torque values at each rotation angles were increased in proportion to depth. Closing forces of titanium alloy clip were slightly higher than those of cobalt alloy clip. By contrast, anti-scissoring torque values of cobalt alloy clip were bigger than those of titanium alloy clip in all conditions. In condition of 3 mm in thickness and 3 mm in depth, anti-scissoring torque vales of titanium alloy clip decreased suddenly when an angle surpassed 70 degrees. Aneurysm clip scissoring phenomenon tends to occur when clipping the aneurysm neck only with blade tips. Based on the results of this experiment, titanium alloy clip is more prone to scissoring than cobalt alloy clip under the condition that the wide blade separation distance and the shallow blade length.

  19. Welding of gamma titanium aluminide alloys (United States)

    Smashey, Russell W. (Inventor); Kelly, Thomas J. (Inventor); Snyder, John H. (Inventor); Sheranko, Ronald L. (Inventor)


    An article made of a gamma titanium aluminide alloy is welded, as for example in the weld repair of surface cracks, by removing foreign matter from the area to be welded, first stress relieving the article, cooling the entire article to a welding temperature of from about F. to about F., welding a preselected region in an inert atmosphere at the welding temperature, and second stress relieving the article. Welding is preferably accomplished by striking an arc in the preselected region so as to locally melt the alloy in the preselected region, providing a filler metal having the same composition as the gamma titanium aluminide alloy of the article, and feeding the filler metal into the arc so that the filler metal is melted and fused with the article to form a weldment upon solidification.

  20. [Copper and copper alloys. Technology updates]. (United States)

    Loconsolo, V; Crespi, M


    The correlations between copper and copper alloys and human health have been the subject of some recent and extensive scientific researches. The voluntary risks evaluation, which anticipated the EU REACH Directive application, has shown that copper is a "safe" product for human health and for environment. In addition, it could be of great help thanks to its antibacterial properties. Copper tube can contribute in a relevant way to the prevention of water systems pollution by Legionella. Also the spreading of nosocomial infections is significantly contrasted by the use of copper and copper alloys for the production of articles intended for being frequently touched by people. The Environmental Protection Agency of the United States has in fact "registered" as antibacterial over 350 of copper alloys.

  1. Study on Explosive Forming of Aluminum Alloy

    Directory of Open Access Journals (Sweden)

    H Iyama


    Full Text Available Now, the aluminum alloy is often used as auto parts, for example, body, engine. For example, there are the body, a cylinder block, a piston, a connecting rod, interior, exterior parts, etc. These are practical used the characteristic of a light and strong aluminum alloy efficiently. However, although an aluminum alloy is lighter than steel, the elongation is smaller than that. Therefore, in press forming, some problems often occur. We have proposed use of explosive forming, in order to solve this problem. In the explosive forming, since a blank is formed at high speed, a strain rate effect becomes large and it can be made the elongation is larger. Then, in order to clarify this feature, we carried out experimental research and numerical analysis. In this paper, these contents will be discussed.

  2. Joining Techniques for Ferritic ODS Alloys

    Energy Technology Data Exchange (ETDEWEB)

    V.G. Krishnardula; V.G. Krishnardula; D.E. Clark; T.C. Totemeier


    This report presents results of research on advanced joining techniques for ferritic oxide-dispersion strengthened alloys MA956 and PM2000. The joining techniques studied were resistance pressure welding (also known as pressure forge welding), transient liquid phase bonding, and diffusion bonding. All techniques were shown to produce sound joints in fine-grained, unrecrystallized alloys. Post-bond heat treatment to produce a coarse-grained, recrystallized microstructure resulted in grain growth across the bondline for transient liquid phase and diffusion bonds, giving microstructures essentially identical to that of the parent alloy in the recrystallized condition. The effects of bond orientation, boron interlayer thickness, and bonding parameters are discussed for transient liquid phase and diffusion bonding. The report concludes with a brief discussion of ODS joining techniques and their applicability to GEN IV reactor systems.

  3. Magnesium Diecasting Alloys for High Temperature Applications (United States)

    Pekguleryuz, Mihriban O.; Kaya, A. Arslan

    New growth area for automotive use of magnesium is powertrain applications such as the transmission case and engine block. These applications see service conditions in the temperature range of 150-200C under 50-70 MPa of tensile and compressive loads. In addition, metallurgical stability, fatigue resistance, corrosion resistance and castability requirements need to be met. A decade of research and development has resulted in a number of creep- resistant magnesium alloys that are potential candidates for elevated-temperature automotive applications. These alloys are mostly based on rare-earth and alkaline earth element additions to magnesium. This paper gives an overview of the various magnesium alloy systems for use in elevated-temperature applications.

  4. Sputtered Clusters from Niobium-Vanadium Alloys

    DEFF Research Database (Denmark)

    Schou, Jørgen; Hofer, W. O.


    A series of Nb&z.sbnd;V alloys have been irradiated by 6 keV argon ions. Homonuclear and heteronuclear clusters emitted from these alloys have been studied by means of post-ionization and/or secondary ion mass spectrometry. The intensity of clusters of atomic masses up to approximately 300 amu...... was related to the concentrations of Nb and V in the alloys. In addition, the behaviour of polyatomic cluster yields as a function of partial oxygen pressure was studied. At partial pressures larger than approximately 10 6Torr, the yields decreased with increasing partial pressures. By inclusion of the post......-ionized neutrals, the total secondary particle intensity was increased by a factor of 1.5 for clusters up to atomic masses of around 200 amu. Scanning electron microscopy revealed a varied surface topography with large differences from grain to grain for irradiated samples exposed for doses larger than 1018 atoms...

  5. Friction Stir Welding of Steel Alloys (United States)

    Ding, R. Jeffrey; Munafo, Paul M. (Technical Monitor)


    The friction stir welding process has been developed primarily for the welding of aluminum alloys. Other higher melting allows such, as steels are much more difficult to join. Special attention must be given to pin tool material selection and welding techniques. This paper addresses the joining of steels and other high melting point materials using the friction stir welding process. Pin tool material and welding parameters will be presented. Mechanical properties of weldments will also be presented. Significance: There are many applications for the friction stir welding process other than low melting aluminum alloys. The FSW process can be expanded for use with high melting alloys in the pressure vessel, railroad and ship building industries.

  6. Rapid solidification of Nb-base alloys (United States)

    Gokhale, A. B.; Javed, K. R.; Abbaschian, G. J.; Lewis, R. E.


    New Nb-base alloys are of interest for aerospace structural applications at high temperatures, viz, 800 to 1650 C. Fundamental information regarding the effects of rapid solidification in achieving greatly refined microstructures, extended solid solubility, suppression of embrittling equilibrium phases, and formation of new phases is desired in a number of Nb-X alloys. The microstructures and selected properties of Nb-Si and other Nb-base alloys are presented for materials both rapidly quenched from the equilibrium liquidus and rapidly solidified following deep supercooling. Electromagnetic levitation was used to achieve melting and supercooling in a containerless inert gas environment. A variety of solidification conditions were employed including splatting or drop casting of supercooled samples. The morphology and composition of phases formed are discussed in terms of both solidification history and bulk composition.

  7. Seacoast stress corrosion cracking of aluminum alloys (United States)

    Humphries, T. S.; Nelson, E. E.


    The stress corrosion cracking resistance of high strength, wrought aluminum alloys in a seacoast atmosphere was investigated and the results were compared with those obtained in laboratory tests. Round tensile specimens taken from the short transverse grain direction of aluminum plate and stressed up to 100 percent of their yield strengths were exposed to the seacoast and to alternate immersion in salt water and synthetic seawater. Maximum exposure periods of one year at the seacoast, 0.3 or 0.7 of a month for alternate immersion in salt water, and three months for synthetic seawater were indicated for aluminum alloys to avoid false indications of stress corrosion cracking failure resulting from pitting. Correlation of the results was very good among the three test media using the selected exposure periods. It is concluded that either of the laboratory test media is suitable for evaluating the stress corrosion cracking performance of aluminum alloys in seacoast atmosphere.

  8. Cast Aluminum Alloy for High Temperature Applications (United States)

    Lee, Jonathan A.


    Originally developed by NASA as high performance piston alloys to meet U.S. automotive legislation requiring low exhaust emission, the novel NASA alloys now offer dramatic increase in tensile strength for many other applications at elevated temperatures from 450 F (232 C) to about 750 F (400 C). It is an ideal low cost material for cast automotive components such as pistons, cylinder heads, cylinder liners, connecting rods, turbo chargers, impellers, actuators, brake calipers and rotors. It can be very economically produced from conventional permanent mold, sand casting or investment casting, with silicon content ranging from 6% to 18%. At high silicon levels, the alloy exhibits excellent dimensional stability, surface hardness and wear resistant properties.

  9. High-strength iron aluminide alloys

    Energy Technology Data Exchange (ETDEWEB)

    McKamey, C.G.; Maziasz, P.J.


    Past studies have shown that binary Fe{sub 3}Al possesses low creep-rupture strength compared to many other alloys, with creep-rupture lives of less than 5 h being reported for tests conducted at 593{degrees}C and 207 MPa. The combination of poor creep resistance and low room-temperature tensile ductility due to a susceptibility to environmentally-induced dynamic hydrogen embrittlement has limited use of these alloys for structural applications despite their excellent corrosion properties. With regard to the ductility problem, alloy development efforts have produced significant improvements, with ductilities of 10-20% and tensile yield strengths as high as 500 MPa being reported. Likewise, initial improvements in creep resistance have been realized through small additions of Mo, Nb, and Zr.

  10. Irradiation creep of vanadium-base alloys

    Energy Technology Data Exchange (ETDEWEB)

    Tsai, H.; Billone, M.C.; Strain, R.V.; Smith, D.L. [Argonne National Lab., IL (United States); Matsui, H. [Tohoku Univ. (Japan)


    A study of irradiation creep in vanadium-base alloys is underway with experiments in the Advanced Test Reactor (ATR) and the High Flux Isotope Reactor (HFIR) in the United States. Test specimens are thin-wall sealed tubes with internal pressure loading. The results from the initial ATR irradiation at low temperature (200--300 C) to a neutron damage level of 4.7 dpa show creep rates ranging from {approx}0 to 1.2 {times} 10{sup {minus}5}/dpa/MPa for a 500-kg heat of V-4Cr-4Ti alloy. These rates were generally lower than reported from a previous experiment in BR-10. Because both the attained neutron damage levels and the creep strains were low in the present study, however, these creep rates should be regarded as only preliminary. Substantially more testing is required before a data base on irradiation creep of vanadium alloys can be developed and used with confidence.

  11. Effect of alloy recasting on the color of opaque porcelain applied on different dental alloy systems. (United States)

    Yilmaz, Burak; Ozcelik, Tuncer B; Johnston, William M; Kurtulmus-Yilmaz, Sevcan; Company, Andrea M


    The effect of different proportions of recast dental alloys on the color of overlying opaque porcelain (OP) is unknown. The purpose of this study was to compare the color of OP applied on 2 different proportions (50% and 100%) of recast alloys with the color of commercially available shade tabs of OP. Six different metal alloy systems (2 base: Metalloy CC, Cr-Co [B-MCC]; Heraenium NA, Ni-Cr [B-HNA]; 3 noble: Cerapall 2, Pd-Au [N-CP2]; Triumph, Pd-Ag [N-T]; V-Deltaloy, Au-Pd [N-VD]; and 1 high-noble: V-Gnathos Plus, Au-Pt [HN-GP]) were selected for the fabrication of disk-shaped specimens (10 mm in diameter, 1 mm in thickness). Each alloy was divided into 2 subgroups: 50% new alloy with 50% recast alloy (n=3) and 100% recast alloy (n=3). OP (B1) was applied (0.1 mm) to all specimens. The color coordinates (L*, a*, b*) of each specimen and the corresponding commercially available OP shade tab (control) were measured with a spectroradiometer, and color differences between specimens and control group were calculated. Data were statistically analyzed (2-way ANOVA, Ryan-Einot-Gabriel-Welsch multiple range test, α=.05). For each alloy, ΔL*(L(control)(-)L(recastalloy)) values for the 2 subgroups were not statistically different from each other. The Δa* and Δb* of different proportions of N-CP2, B-HNA, N-VD, and HN-GP were not statistically different within the alloys. However, the a* values of 100% recast N-T and B-MCC were significantly closer to the a* values of the control group, and the b* values of 50% recast B-MCC were significantly closer to the b* values of the control group (Pvalues for different proportions of alloys were not statistically different. However, color differences did not meet the criterion of clinical acceptability (ΔE=3.46). According to the results of this study, the different proportions (50% and 100%) of recast alloys used have similar effects on the color of OP. Differences between the final color of OP on the recast alloys used and the

  12. Effects of alloy composition in alleviating embrittlement problems associated with the tantalum alloy T-111 (United States)

    Stephens, J. R.


    The causes of aging embrittlement in T-111 (Ta-8W-2Hf) and the effects of alloy modification were investigated. Results showed that T-111 contains a critical combination of tungsten and hafnium that leads to loss of ductility at -196 C after aging near 1040 C. This appears to occur because tungsten enhances hafnium segregation to grain boundaries and this also leads to increased susceptibility to hydrogen embrittlement. Aging embrittlement was not observed in tantalum alloys with reduced tungsten or hafnium contents; however, most of the alloys studied have lower strengths than T-111 and exhibit susceptibility to hydrogen embrittlement.

  13. Non-alloyed Ni3Al based alloys – preparation and evaluation of mechanical properties

    Directory of Open Access Journals (Sweden)

    J. Malcharcziková


    Full Text Available The paper reports on the fabrication and mechanical properties of Ni3Al based alloy, which represents the most frequently used basic composition of nickel based intermetallic alloys for high temperature applications. The structure of the alloy was controlled through directional solidification. The samples had a multi-phase microstructure. The directionally solidified specimens were subjected to tensile tests with concurrent measurement of acoustic emission (AE. The specimens exhibited considerable room temperature ductility before fracture. During tensile testing an intensive AE was observed.

  14. Formation and characterization of Al–Ti–Nb alloys by electron-beam surface alloying

    Energy Technology Data Exchange (ETDEWEB)

    Valkov, S., E-mail: [Institute of Electronics, Bulgarian Academy of Science, 72 Tzarigradsko Chaussee blvd., 1784 Sofia (Bulgaria); Petrov, P. [Institute of Electronics, Bulgarian Academy of Science, 72 Tzarigradsko Chaussee blvd., 1784 Sofia (Bulgaria); Lazarova, R. [Institute of Metal Science, Equipment and Technologies with Hydro and Aerodynamics Center, Bulgarian Academy of Science, 67 Shipchenski Prohod blvd., 1574 Sofia (Bulgaria); Bezdushnyi, R. [Department of Solid State Physics and Microelectronics, Faculty of Physics, Sofia University “St. Kliment Ohridsky”, 1164 Sofia (Bulgaria); Dechev, D. [Institute of Electronics, Bulgarian Academy of Science, 72 Tzarigradsko Chaussee blvd., 1784 Sofia (Bulgaria)


    Highlights: • Al–Ti–Nb surface alloys have been successfully obtained by electron-beam surface alloying technology. • The alloys consist of (Ti,Nb)Al{sub 3} fractions, distributed in the biphasic structure of (Ti,Nb)Al{sub 3} particles dispersed in α-Al. • The alloying speed does not affect the lattice parameters of (Ti,Nb)Al{sub 3} and, does not form additional stresses, strains etc. • It was found that lower velocity of the specimen motion during the alloying process develops more homogeneous structures. • The measured hardness of (Ti,Nb)Al{sub 3} compound reaches 775 HV[kg/cm{sup 2}] which is much greater than the values of NbAl{sub 3}. - Abstract: The combination of attractive mechanical properties, light weight and resistance to corrosion makes Ti-Al based alloys applicable in many industrial branches, like aircraft and automotive industries etc. It is known that the incorporation of Nb improves the high temperature performance and mechanical properties. In the present study on Al substrate Ti and Nb layers were deposited by DC (Direct Current) magnetron sputtering, followed by electron-beam alloying with scanning electron beam. It was chosen two speeds of the specimen motion during the alloying process: V{sub 1} = 0.5 cm/s and V{sub 2} = 1 cm/s. The alloying process was realized in circular sweep mode in order to maintain the melt pool further. The obtained results demonstrate a formation of (Ti,Nb)Al{sub 3} fractions randomly distributed in biphasic structure of intermetallic (Ti,Nb)Al{sub 3} particles, dispersed in α-Al solid solution. The evaluated (Ti,Nb)Al{sub 3} lattice parameters are independent of the speed of the specimen motion and therefore the alloying speed does not affect the lattice parameters and thus, does not form additional residual stresses, strains etc. It was found that lower velocity of the specimen motion during the alloying process develops more homogeneous structures. The metallographic analyses demonstrate a

  15. Magnesium alloy AZ63A reinforcement by alloying with gallium and using high-disperse ZrO2 particles

    Directory of Open Access Journals (Sweden)

    J. Khokhlova


    Full Text Available The aim of this work was to obtain an experimental magnesium alloy by remelting standard AZ63A alloy with addition of gallium ligatures and ZrO2 particles. This allowed reinforcement of alloy and increase its hardness and Young's modulus. The chemical analysis of this alloy shows two types of structures which are evenly distributed in volume. Thus we can conclude that reinforcing effect is the result of formation of intermetallic phase Mg5-Ga2.

  16. Fast LIBS Identification of Aluminum Alloys

    Directory of Open Access Journals (Sweden)

    Tawfik W.


    Full Text Available Laser-induced breakdown spectroscopy (LIBS has been applied to analysis aluminum alloy targets. The plasma is generated by focusing a 300 mJ pulsed Nd: YAG laser on the target in air at atmospheric pressure. Such plasma emission spectrum was collected using a one-meter length wide band fused-silica optical fiber connected to a portable Echelle spectrometer with intensified CCD camera. Spectroscopic analysis of plasma evolution of laser produced plasmas has been characterized in terms of their spectra, electron density and electron temperature assuming the LTE and optically thin plasma conditions. The LIBS spectrum was optimized for high S/N ratio especially for trace elements. The electron temperature and density were determined using the emission intensity and stark broadening, respectively, of selected aluminum spectral lines. The values of these parameters were found to change with the aluminum alloy matrix, i.e. they could be used as a fingerprint character to distinguish between different aluminum alloy matrices using only one major element (aluminum without needing to analysis the rest of elements in the matrix. Moreover, It was found that the values of T e and N e decrease with increasing the trace elements concentrations in the aluminum alloy samples. The obtained results indicate that it is possible to improve the exploitation of LIBS in the remote on-line industrial monitoring application, by following up only the values of T e and N e for aluminum in aluminum alloys as a marker for the correct alloying using an optical fiber probe.

  17. Ultraprecision microelectroforming of metals and metal alloys (United States)

    Loewe, Holger; Ehrfeld, Wolfgang; Diebel, Joerg


    In recent years, microsystem technology and its growing importance for actuators, sensors, optics and microfluidics, only to name a few, have gained a lot of attention. Specific applications demand fabrication techniques allowing a fast and reliable replication of microstructure products in a variety of materials. An important technique for replication processes of microstructures in many applications of microsystem technology are microelectroforming processes, generating a variety of metals and metal alloys with tailored characteristics. Here, new results in the development of alloys for specific applications as well as their applications are reported: (1) Newly developed alloys: Nickel-iron alloys enable the production of soft magnetic microstructures e.g. for specific applications in microactuators. Nickel-cobalt and Nickel-tungsten alloys have been employed for the manufacture of microstructured tools with excellent mechanical properties regarding wear and mechanical durability. These tools have been applied to hot-embossing and injection molding processes successfully. (2) Microelectroforming within the frame of the LIGA technique allows the manufacturing of extremely precise electrodes with various cross-sections and heights for (mu) - electro discharge machining. The combination of these techniques enables the production of microstructures from non- electrodepositable materials, like stainless steel e.g. for large scale replication processes. (3) The precision of microelectroforming enables the replication of structured surfaces on a nanoscale for molecular microelectronics or special applications. The new types of alloys reported here significantly enlarge the applicability of microelectroforming processes for tool fabrication or direct use. Moreover combining this process with other microstructuring processes like injection molding or (mu) -EDM techniques generates a powerful tool for microsystem technology.

  18. Creep behavior of Zr-Nb alloys

    Energy Technology Data Exchange (ETDEWEB)

    Suh, Yong Chan; Kim, Young Suk; Cheong, Yong Mu; Kwon, Sang Chul; Kim, Sung Soo; Choo, Ki Nam [Korea Atomic Energy Research Institute, Taejeon (Korea)


    The creep characteristics of Zirconium alloy is affected by several parameters. Out-reactor creep increases both with an increasing amount of Nb, Sn and S contained in alpha-Zr and decreases with the increasing volume of alpha-Zr. Especially, the creep of Zr-2.5Nb alloy depends on the solubility of Nb in alpha-Zr, which is associated with the decomposition of beta-Zr. Since Zr of the hcp structure is strongly anisotropic, it shows the characteristics of texture and results in the anisotropy of creep. Due to the circumferential texture of Zr-2.5%Nb alloy (CANDU Pressure tube), the longitudinal slip is easier than the circumferential one, resulting in the high creep rate. The irradiation creep also increases with increasing neutron fluence. The neutron irradiation increases the strength of the zirconium alloys but decreases their creep strength. In contrast to the out-reactor creep, the irradiation creep is little sensitive to temperature, resulting in the lower activation energy. The most important factor to affect the in-reactor and out-reactor creep of niobium containing alloys seems to be the solution hardening by Nb or Sn which is soluble in alpha-zirconium and the texture as well. Irradiation growth is the mechanism which is caused only by the irradiation. It becomes saturated at lower fluence than the critical fluence but beyond it, shows the break-away growth. The onset of accelerated irradiation growth corresponds with the c-dislocation loop formation, though its mechanism needs better understanding. Generally, the irradiation growth of Zr-Nb alloys increases with an increase in fluence, cold working, dislocation, density and temperature, and with a decrease in the grain size. 141 refs., 59 figs., 10 tabs. (Author)

  19. The influence of the pure metal components of four different casting alloys on the electrochemical properties of the alloys. (United States)

    Tuna, Süleyman H; Pekmez, Nuran Ozçiçek; Keyf, Filiz; Canli, Fulya


    The aim of this study was to investigate the influence of the pure metal components of the four different casting alloys on the corrosion behaviors of these alloys tested. Potentiodynamic polarization tests were carried out on four different types of casting alloys and their pure metals at 37 degrees C in an artificial saliva solution. The ions released from the alloys into the solutions during the polarization test were also determined quantitatively using inductively coupled plasma-mass spectrometry (ICP-MS). Ni-Cr (M1) and Co-Cr (M2) alloys had a more homogenous structure than palladium based (M3) and gold based (M4) alloys in terms of the pitting potentials of the casting alloys and those of the pure metals composing the alloys. The total ion concentration released from M3 and M4 was less than from M1 and M2. This may be because M3 and M4 alloys contained noble metals. It was also found that the noble metals in the M3 and M4 samples decreased the current density in the anodic branch of the potentiodynamic polarization curves. In other words, noble metals contributed positively to dental materials. Corrosion resistance of the casting alloys can be affected by the pure metals they are composed of. Au and Pd based noble alloys dissolved less than Ni-Cr and Co-Cr based alloys.

  20. The effect of alloying additives on structure and properties of cast Al-Cu-Si-Mg alloys

    Energy Technology Data Exchange (ETDEWEB)

    Eskin, D.G. [Russian Academy of Sciences, Moscow (Russian Federation). Baikov Inst. of Metall.


    The effect of base and additive alloying elements on the structure and properties of cast Al-Cu-Si-Mg alloys was studied. The mechanical properties at room and elevated temperatures were shown to correlate well with the composition of a supersaturated solid solution and the structure of cast alloys. (orig.)

  1. Mechanical Properties of Aluminum-alloy Rivets (United States)

    Brueggeman, Wm C


    The development of metal construction for aircraft has created a need for accurate and detailed information regarding the strength of riveted joints in aluminum-alloy structures. To obtain this information the National Bureau of Standards in cooperation with the National Advisory Committee for Aeronautics is investigating the strength of riveted joints in aluminum alloys. The strength of riveted joints may be influenced by the form of the head, the ratio of the rivet diameter to the sheet thickness, the driving stress, and other factors. This note gives the results of tests to develop the riveting technique for test specimens and to determine the effects of these factors.

  2. Amorphous Alloy: Promising Precursor to Form Nanoflowerpot

    Directory of Open Access Journals (Sweden)

    Guo Lan


    Full Text Available Nanoporous copper is fabricated by dealloying the amorphous Ti2Cu alloy in 0.03 M HF electrolyte. The pore and ligament sizes of the nanoporous copper can be readily tailored by controlling the dealloying time. The as-prepared nanoporous copper provides fine and uniform nanoflowerpots to grow highly dispersed Au nanoflowers. The blooming Au nanoflowers in the nanoporous copper flowerpots exhibit both high catalytic activity and stability towards the oxidation of glucose, indicating that the amorphous alloys are ideal precursors to form nanoflowerpot which can grow functional nanoflowers.

  3. Pulse reversal plating of nickel alloys

    DEFF Research Database (Denmark)

    Tang, Peter Torben


    Pulse plating has previously been reported to improve the properties of nickel and nickel alloy deposits. Typically, focus has been on properties such as grain size, hardness and smoothness. When pulse plating is to be utilised for microtechnologies such as microelectromechanical systems (MEMS......), internal stress and material distribution are even more important. With baths based upon nickel chloride, and nickel and cobalt chlorides, pulse reversal plating of both pure nickel and nickel-cobalt alloys has been used to fabricate tools for microinjection moulding. Pulse reversal plating of ternary soft...

  4. New developments in rapidly solidified magnesium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Das, S.K. [Allied-Signal, Inc., Morristown, NJ (United States); Chang, C.F. [Allied-Signal, Inc., Morristown, NJ (United States); Raybould, D. [Allied-Signal, Inc., Morristown, NJ (United States); King, J.F. [Magnesium Elektron Ltd., Manchester (United Kingdom); Thistlethwaite, S. [Magnesium Elektron Ltd., Manchester (United Kingdom)


    In the present paper, we will examine the new developments in the rapidly solidified Mg-Al-Zn-Nd (EA55RS) alloy. We shall first briefly review the process scale-up currently employed for producing rapidly solidified magnesium alloys in large quantities, and then discuss the effect of billet size and processing parameters on the mechanical properties of various mill product forms such as extrusions and sheets. The superplastic behavior of EA55RS extrusions and rolled sheets are also discussed. Finally, some results on magnesium metal-matrix composites using rapidly solidified EA55RS matrix powders and SiC particulates are presented. (orig.)

  5. Corrosion resistant alloys for flue gas desulphurisation

    Energy Technology Data Exchange (ETDEWEB)

    Asphahani; Nickerson, J.L. (Haynes International (United States)); Storey, I.J. (Haynes International (United Kingdom))

    Since the mid-seventies, more than 140 field tests have been conducted on several corrosion-resistant alloys in a multitude of flue gas desulphurisation units. In addition, during the eighties, over 30 utilities have installed Hastelloy alloys in the most corrosive conditions in wet scrubbing systems. This article discusses the results from field tests and the experience gained from several installations. The cost effectiveness of thinsheet metallic lining is addressed and the issues of quality control/reliability are reviewed. (6 figures, 5 tables, 7 references). (Author)

  6. Transparent Analogs for Alloy Phase Studies (United States)

    Frazier, D. O.; Smith, James E., Jr.


    Report describes experiments to add information to data base supporting use of transparent, partially miscible liquids and solids as analogs in studies of alloy solidification. Behavior of these materials observed directly while they undergo liquid/liquid and liquid/solid phase transformations. Light-scattering techniques used to determine phase boundaries. Transparent analogs allow observation of both solidification patterns and processes leading to those patterns, whereas metal alloys require tedious post-solidification metallographic analyses because processes not generally observed. Experiments with transparent substances safer and cheaper since conducted at much lower temperatures.

  7. Thermal expansion: Metallic elements and alloys. [Handbook (United States)

    Touloukian, Y. S.; Kirby, R. K.; Taylor, R. E.; Desai, P. D.


    The introductory sections of the work are devoted to the theory of thermal expansion of solids and to methods for the measurement of the linear thermal expansion of solids (X-ray methods, high speed methods, interferometry, push-rod dilatometry, etc.). The bulk of the work is devoted to numerical data on the thermal linear expansion of all the metallic elements, a large number of intermetallics, and a large number of binary alloy systems and multiple alloy systems. A comprehensive bibliography is provided along with an index to the materials examined.

  8. Nodular Corrosion Characteristics of Zirconium Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Hyun Gil; Jeong, Y. H.; Park, S. Y.; Lee, D. J


    This study was reported the effect of the nodular corrosion on the nuclear reactor environmental along with metallurgical influence, also suggested experimental scheme related to evaluate nodular corrosion characteristics of Zr-1 Nb alloy. Remedial strategies against the nodular corrosion should firstly develop plan to assess the effect of the water quality condition (Oxygen, Hydrogen) as well as the boiling on the nodular corrosion, secondarily establish plan to control heat treatment process to keep a good resistance on nodular corrosion in Zr-1Nb alloy as former western reactor did.

  9. Model for magnetic-nonmagnetic binary alloys

    Energy Technology Data Exchange (ETDEWEB)

    Razafimandimby, H. [Departement de Physique, Universite de Toliara, 601 Toliara (Madagascar); Randrianasoloharisoa, D. [LPMR, Universite d' Antananarivo (Madagascar); Rakotomahevitra, A. [Departement des Sciences Exactes, Universite de Mahajanga, BP 155 (Madagascar); Parlebas, J.C. [IPCMS, UMR 7504 CNRS-Universite Louis Pasteur, 23 rue du Loess, BP 43, 67034 Strasbourg (France)


    An extension of a mean-field approximation (MFA) developed within standard basis operators (SBO) is used to study magnetism in magnetic-nonmagnetic binary alloys. The Curie temperature is calculated from the free energy within the framework of the present approach. The calculated results are in fair agreement with the theoretical results of other research groups for the same problem but utilizing other methods. Finally, the case of NiPt alloys is briefly examined as an example test for the comparison with experiment. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  10. Magnetic susceptibility of Dirac fermions, Bi-Sb alloys, interacting Bloch fermions, dilute nonmagnetic alloys, and Kondo alloys

    Energy Technology Data Exchange (ETDEWEB)

    Buot, Felix A., E-mail: [Computational Materials Science Center, George Mason University, Fairfax, VA 22030 (United States); TCSE Center, Spintronics Group, Physics Department, University of San Carlos, Talamban, Cebu 6000 (Philippines); C& LB Research Institute, Carmen, Cebu 6005 (Philippines); Otadoy, Roland E.S.; Rivero, Karla B. [TCSE Center, Spintronics Group, Physics Department, University of San Carlos, Talamban, Cebu 6000 (Philippines)


    Wide ranging interest in Dirac Hamiltonian is due to the emergence of novel materials, namely, graphene, topological insulators and superconductors, the newly-discovered Weyl semimetals, and still actively-sought after Majorana fermions in real materials. We give a brief review of the relativistic Dirac quantum mechanics and its impact in the developments of modern physics. The quantum band dynamics of Dirac Hamiltonian is crucial in resolving the giant diamagnetism of bismuth and Bi-Sb alloys. Quantitative agreement of the theory with the experiments on Bi-Sb alloys has been achieved, and physically meaningful contributions to the diamagnetism has been identified. We also treat relativistic Dirac fermion as an interband dynamics in uniform magnetic fields. For the interacting Bloch electrons, the role of translation symmetry for calculating the magnetic susceptibility avoids any approximation to second order in the field. The expressions for magnetic susceptibility of dilute nonmagnetic alloys give a firm theoretical foundation of the empirical formulas used in fitting experimental results. The unified treatment of all the above calculations is based on the lattice Weyl-Wigner formulation of discrete phase-space quantum mechanics. For completeness, the magnetic susceptibility of Kondo alloys is also given since Dirac fermions in conduction band and magnetic impurities exhibit Kondo effect.

  11. Heat-Resistance of the Powder Cobalt Alloys Reinforced by Niobium or Titanium Carbide


    Cherepova, T.S.; Dmitrieva, G.P.; V.K. Nosenko


    The characteristics of heat-resistance of powder cobalt alloys at 1100 °C were investigated. These alloys were developed for the protection of workers banding shelves GTE blades from wear. The alloys were prepared by hot pressing powders of cobalt, chromium, aluminum, iron and niobium or titanium carbides. The values of heat resistance alloys containing carbides between 30 and 70% (vol.) depend on the type made of carbide alloys: alloys with titanium carbide superior in heat-resistant alloy o...

  12. The recasting effects on the high gold dental alloy properties

    Directory of Open Access Journals (Sweden)

    Maksimović V.M.


    Full Text Available Noble dental alloys are often reused in dental practice by recasting. The aim of this study was to determine if repeated casting of high gold dental alloys has a detrimental effect on alloy microstructure, type of porosity, structure and microhardness. Results showed that recasting procedure had a strong effect on the change of alloy porosity type. It was also found that alloy microhardness increased with the increase of the number of recasting cycles. At the same time the grain growth and changes of the solid solution phases in the microstructure were observed. [Projekat Ministarstva nauke Republike Srbije, br. III 45012

  13. Challenges for research and development of new aluminum alloys

    Directory of Open Access Journals (Sweden)

    D. Vojtĕch


    Full Text Available Modern trends in research and development of new aluminum alloys are characterized in the present work. Although conventional wrought and casting Al-based alloys show good specific strength, as compared to steels or Ti-based alloys, there is still a potential for significant improvement of their performance. It consists in application of new alloying elements, mainly transition metals, and uncommon processing routes, for example powder metallurgy. By this way, qualitatively new materials with ultra high strength and excellent thermal stability can be developed. However, there are many questions to be answered before new alloys can be competitive to conventional Al-based materials.

  14. Cadmium free lead alloy for reusable radiotherapy shielding. (United States)

    Blackwell, C R; Amundson, K D


    A low melting point cadmium free fusible lead alloy suitable for custom radiotherapy shielding blocks is described. The alloy, referred to here as Alloy-203, differs in composition from the more common Lipowitz's metal (Cerrobend) by being cadmium free, having a slightly higher lead content and a 203 degrees F melting temperature. Attenuation properties have been studied for 4-18 MV X-rays. Alloy-203 has lower transmission than Lipowitz's metal, primarily due to the higher content of lead and bismuth. Daily use for the past 2 years at Mayo Clinic has not indicated any major problems associated with the use of this cadmium free alloy for custom shield fabrication.

  15. A review on hot tearing of magnesium alloys

    Directory of Open Access Journals (Sweden)

    Jiangfeng Song


    Full Text Available Hot tearing is often a major casting defect in magnesium alloys and has a significant impact on the quality of their casting products. Hot tearing of magnesium alloys is a complex solidification phenomenon which is still not fully understood, it is of great importance to investigate the hot tearing behaviour of magnesium alloys. This review attempts to summarize the investigations on hot tearing of magnesium alloys over the past decades. The hot tearing criteria including recently developed Kou's criterion are summarized and compared. The numeric simulation and assessing methods of hot tearing, factors influencing hot tearing, and hot tearing susceptibility (HTS of magnesium alloys are discussed.

  16. Effects of Grain Refining Additions to Aluminum Alloys (United States)

    Gennone, R. J.; Coyle, F. T.; Farrior, G. M.

    An efficient method of controlling the grain-size of commercial aluminum alloys is by continuous additions of grain-refining agents in the form of master-alloy rod which is fed automatically into the launder during casting. The simultaneous addition of titanium and boron in a single rod is more efficient and more economical than separate additions. Response of various alloys to grain refining may be determined using the laboratory test described. Effects of these additions on 6063 alloy are presented; preliminary results on other commercial alloys are included.

  17. Vanadium-base alloys for fusion reactor applications

    Energy Technology Data Exchange (ETDEWEB)

    Smith, D.L.; Loomis, B.A.; Diercks, D.R.


    Vanadium-base alloys offer potentially significant advantages over other candidate alloys as a structural material for fusion reactor first wall/blanket applications. Although the data base is more limited than that for the other leading candidate structural materials, viz., austenitic and ferritic steels, vanadium-base alloys exhibit several properties that make them particularly attractive for the fusion reactor environment. This paper presents a review of the structural material requirements, a summary of the materials data base for selected vanadium-base alloys, and a comparison of projected performance characteristics compared to other candidate alloys. Also, critical research and development (R and D) needs are defined.

  18. The effect of alloying on the ordering processes in near-alpha titanium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Popov, Artemiy, E-mail: [Ural Federal University named after the first President of Russia B.N. Yeltsin, 19 Mira Street, Ekaterinburg 620002 (Russian Federation); Rossina, Natalya [Ural Federal University named after the first President of Russia B.N. Yeltsin, 19 Mira Street, Ekaterinburg 620002 (Russian Federation); Popova, Maria, E-mail: [Ural Federal University named after the first President of Russia B.N. Yeltsin, 19 Mira Street, Ekaterinburg 620002 (Russian Federation)


    The substructure of near-alpha Ti–Al–Sn–Zr–Mo–Si alloys containing up to 12.5 at% aluminum was studied by transmission electron microscopy (TEM). It was shown that long-range order sections are formed at aging temperatures up to 500 °C in alloys, high in aluminum, and the ordered phase is formed by the nucleation and growth mechanism at 700 °C aging temperatures. Causes of changing the phase transformation mechanism have been discussed, and the relationship between the structure and properties of alloys, depending on modes of heat treatment has been analyzed. Also the influence of aluminides and silicides precipitation on the mechanical alloy properties after aging was examined. It was shown that the aluminide formation led to a slight hardening and a significant viscosity decrease. The silicide particles formation reduced the heat resistance properties, due to the depletion of the solid solution by silicon.

  19. Corrosion behavior of friction stir welded AZ31B Mg alloy - Al6063 alloy joint

    Directory of Open Access Journals (Sweden)

    B. Ratna Sunil


    Full Text Available In the present work, AZ31B Mg alloy and Al6063 alloy-rolled sheets were successfully joined by friction stir welding. Microstructural studies revealed a sound joint with good mechanical mixing of both the alloys at the nugget zone. Corrosion performance of the joint was assessed by immersing in 3.5% NaCl solution for different intervals of time and the corrosion rate was calculated. The joint has undergone severe corrosion attack compared with both the base materials (AZ31B and Al6063 alloys. The predominant corrosion mechanism behind the high corrosion rate of the joint was found to be high galvanic corrosion. From the results, it can be suggested that the severe corrosion of dissimilar Mg–Al joints must be considered as a valid input while designing structures intended to work in corroding environment.

  20. Magnesium alloys as implant materials--principles of property design for Mg-RE alloys. (United States)

    Hort, N; Huang, Y; Fechner, D; Störmer, M; Blawert, C; Witte, F; Vogt, C; Drücker, H; Willumeit, R; Kainer, K U; Feyerabend, F


    Magnesium alloys have attracted increasing interest in the past years due to their potential as implant materials. This interest is based on the fact that magnesium and its alloys are degradable during their time of service in the human body. Moreover magnesium alloys offer a property profile that is very close or even similar to that of human bone. The chemical composition triggers the resulting microstructure and features of degradation. In addition, the entire manufacturing route has an influence on the morphology of the microstructure after processing. Therefore the composition and the manufacturing route have to be chosen carefully with regard to the requirements of an application. This paper discusses the influence of composition and heat treatments on the microstructure, mechanical properties and corrosion behaviour of cast Mg-Gd alloys. Recommendations are given for the design of future degradable magnesium based implant materials. Copyright (c) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  1. Characteristics of 14Cr-ODS ferritic alloy fabricated by mechanically alloying and microwave sintering

    Energy Technology Data Exchange (ETDEWEB)

    Zhenhua, Yao [State Key Laboratory of Materia Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Weihao, Xiong, E-mail: [State Key Laboratory of Materia Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Bin, Huang; Qingqing, Yang [State Key Laboratory of Materia Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074 (China); Jiang, Jianjun [School of Optical and Electronic Information, Huazhong University of Science and Technology, Wuhan 430074 (China)


    14Cr-ODS ferritic alloys were fabricated by microwave sintering and conventional vacuum sintering. The results showed that the sintering time could be reduced and the sintering temperature could be decreased effectively by adoption of microwave sintering. The tensile strength of the alloy microwave sintered at 1250 °C and the alloy vacuum sintered at 1350 °C were 691.4 MPa and 521.5 MPa respectively. The superior strength of microwave sintered one would be attributed to finer grain size, which was resulted from the shorter sintering time and lower sintering temperature. The elongation of microwave sintered alloy was worse than that of the vacuum sintering one. Nano-oxide precipitates were dispersed homogeneously in the Fe-based matrix, and their size was mostly ranged from several nm to more than 20 nm.

  2. Alloying effect of copper concentration on the localized corrosion of aluminum alloy for heat exchanger tube (United States)

    Hong, Min-Sung; Park, In-Jun; Kim, Jung-Gu


    This study examined the alloying effect of Cu content on the localized corrosion properties of Al alloy in synthetic acid rain containing 200 ppm of Cl- ion. In aluminum alloy tubes, a small amount of Cu is contained as the additive to improve the mechanical strength or as the impurity. The Cu-containing intermetallic compound, Al2Cu can cause galvanic corrosion because it has more noble potential than Al matrix. Therefore aluminum tube could be penetrated by localized corrosion attack. The results were obtained from electrochemical test, scanning electron microscopy, and time of flight secondary ion mass spectrometry (ToF-SIMS) mapping. Severe localized corrosion was occurred on the Al-0.03 wt% Cu alloy. The negative effect of Cu on the pitting corrosion was attributed to the presence of the Al2Cu precipitates.

  3. Dispersoid reinforced alloy powder and method of making

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, Iver E.; Terpstra, Robert L.


    A method of making dispersion-strengthened alloy particles involves melting an alloy having a corrosion and/or oxidation resistance-imparting alloying element, a dispersoid-forming element, and a matrix metal wherein the dispersoid-forming element exhibits a greater tendency to react with a reactive species acquired from an atomizing gas than does the alloying element. The melted alloy is atomized with the atomizing gas including the reactive species to form atomized particles so that the reactive species is (a) dissolved in solid solution to a depth below the surface of atomized particles and/or (b) reacted with the dispersoid-forming element to form dispersoids in the atomized particles to a depth below the surface of said atomized particles. The atomized alloy particles are solidified as solidified alloy particles or as a solidified deposit of alloy particles. Bodies made from the dispersion strengthened alloy particles, deposit thereof, exhibit enhanced fatigue and creep resistance and reduced wear as well as enhanced corrosion and/or oxidation resistance at high temperatures by virtue of the presence of the corrosion and/or oxidation resistance imparting alloying element in solid solution in the particle alloy matrix.

  4. Microstructure and mechanical properties of Mg-Zn-Ag alloys

    Energy Technology Data Exchange (ETDEWEB)

    Park, S.C.; Lim, J.D. [Materials Research Team, R and D Div., Hyundai Motor Co. and Kia Motors Corp., Kyunggi-do (Korea); Eliezer, D. [Dept. of Materials Engineering, Ben-Gurion Univ. of the Negev, Beer-Sheva (Israel); Shin, K.S. [School of Materials Science and Engineering, Seoul National Univ. (Korea); CAAM, POSTECH, Pohang (Korea)


    The majority of Mg components currently in use in the automotive and electronic industries are produced by conventional casting processes. However, there is a strong need to develop new high strength wrought alloys for wide-spread application of Mg alloys in near future. In the present study, new Mg-Zn-Ag alloys were developed and characterized. In order to evaluate the effects of Ag addition on the mechanical properties of the extruded Mg-Zn alloys, the age hardening response and mechanical properties were examined with different amounts of alloying element. The microstructures of the specimens were examined with optical microscopy and transmission electron microscopy. The grain sizes of the alloys in as-extruded condition were markedly reduced with the addition of Ag. The hardness was found to increase more rapidly in the alloys with double aging treatment compared to those with single aging treatment. The peak hardness was also found to be higher in the alloys with double aging treatment. In all heat treatment conditions, the hardness of the Mg-Zn-Ag alloys were found to be higher than those of the Mg-Zn alloys. The addition of Ag to the Mg-Zn alloys increased the tensile strength with a small decrease in tensile elongation in the peak double aging condition. (orig.)

  5. Dispersoid reinforced alloy powder and method of making

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, Iver E.; Terpstra, Robert L.


    A method of making dispersion-strengthened alloy particles involves melting an alloy having a corrosion and/or oxidation resistance-imparting alloying element, a dispersoid-forming element, and a matrix metal wherein the dispersoid-forming element exhibits a greater tendency to react with a reactive species acquired from an atomizing gas than does the alloying element. The melted alloy is atomized with the atomizing gas including the reactive species to form atomized particles so that the reactive species is (a) dissolved in solid solution to a depth below the surface of atomized particles and/or (b) reacted with the dispersoid-forming element to form dispersoids in the atomized particles to a depth below the surface of said atomized particles. The atomized alloy particles are solidified as solidified alloy particles or as a solidified deposit of alloy particles. Bodies made from the dispersion strengthened alloy particles, deposit thereof, exhibit enhanced fatigue and creep resistance and reduced wear as well as enhanced corrosion and/or oxidation resistance at high temperatures by virtue of the presence of the corrosion and/or oxidation resistance imparting alloying element in solid solution in the particle alloy matrix.

  6. Development of the advanced nuclear materials -Development of Inconel alloys-

    Energy Technology Data Exchange (ETDEWEB)

    Kuk, Il Hyun; Chang, Jin Sung; Lee, Chang Kyu; Park, Soon Dong; Kim, Woo Kon; Jeong, Man Kyo; Woo, Yoon Myung; Han, Chang Hee [Korea Atomic Energy Research Institute, Taejon (Korea, Republic of)


    The performance and the integrity of the steam generator U-tubes directly affects the efficiency and economics of nuclear power plant because they are closely interrelated with the maintenance and repair. Also the steam generator U-tubes have been one of world-wide hot issues in nuclear power plants for long time because of their continuing corrosion-related degradation. Right after stress corrosion cracking of Alloy 600 tubes are reported at primary side, in which the environment is believed to be tightly controlled all the time, in mid 80`s, alloy 690 has started to replace alloy 600. Alloy 690 is basically same with alloy 600 except more Cr content. Firstly minor elements in alloy 690 (C, B, N, Y, Mo) were added or controlled to improve hot workability and corrosion resistance. It would be much more desirable if the mechanism or basic understanding of the degradation phenomena of steam generator U-tubes in operation conditions can be illuminated through the alloy modification research. Alloy 600 tubes which were preproduced in cooperation with Sammi Special Steel were evaluated, being compared with imported one. Also alloy 600 and alloy 690 tubes were produced from Inconel 600 and 690 INCO- forged bar. These will be closely evaluated with purely Korean-made alloy 600 and 690 tubes. 22 tabs., 93 figs., 14 refs. (Author).

  7. Grain Refinement of Permanent Mold Cast Copper Base Alloys

    Energy Technology Data Exchange (ETDEWEB)

    M.Sadayappan; J.P.Thomson; M.Elboujdaini; G.Ping Gu; M. Sahoo


    Grain refinement is a well established process for many cast and wrought alloys. The mechanical properties of various alloys could be enhanced by reducing the grain size. Refinement is also known to improve casting characteristics such as fluidity and hot tearing. Grain refinement of copper-base alloys is not widely used, especially in sand casting process. However, in permanent mold casting of copper alloys it is now common to use grain refinement to counteract the problem of severe hot tearing which also improves the pressure tightness of plumbing components. The mechanism of grain refinement in copper-base alloys is not well understood. The issues to be studied include the effect of minor alloy additions on the microstructure, their interaction with the grain refiner, effect of cooling rate, and loss of grain refinement (fading). In this investigation, efforts were made to explore and understand grain refinement of copper alloys, especially in permanent mold casting conditions.

  8. Heat resistant magnesium alloys for automotive powertrain applications

    Energy Technology Data Exchange (ETDEWEB)

    Anyanwu, I.A.; Gokan, Y.; Nozawa, S.; Kamado, S.; Kojima, Y. [Dept. of Mechanical Engineering, Nagaoka Univ. of Technology, Nagaoka, Niigata (Japan); Takeda, S.; Ishida, T. [Ahresty Corp., Magnesium Products Mfg. Div., Tochigi (Japan)


    The suitability of new Mg-Zn-Al-Ca-RE alloys for automotive power train applications are evaluated. Zinc and aluminum contents of the alloys were systematically varied in order to determine alloys with a combination of good diecasting characteristics and high heat resistance. Addition of large amounts of zinc to the alloys results in the formation of intermetallic compounds that crystallize at lower temperatures relative to the matrix, and consequently, fluidity is improved, but hot tearing occurs during diecasting. However, one of the new alloys, Mg-0.5%Zn-6%Al-1%Ca-3%RE alloy is found to exhibit good diecastability and comparable heat resistance with the conventional aluminum alloy, ADC12 that is currently used for diecasting of automotive powertrain parts. (orig.)

  9. Casting Characteristics of High Cerium Content Aluminum Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Weiss, D; Rios, O R; Sims, Z C; McCall, S K; Ott, R T


    This paper compares the castability of the near eutectic aluminum-cerium alloy system to the aluminum-silicon and aluminum-copper systems. The alloys are compared based on die filling capability, feeding characteristics and tendency to hot tear in both sand cast and permanent mold applications. The castability ranking of the binary Al–Ce systems is as good as the aluminum-silicon system with some deterioration as additional alloying elements are added. In alloy systems that use cerium in combination with common aluminum alloying elements such as silicon, magnesium and/or copper, the casting characteristics are generally better than the aluminum-copper system. In general, production systems for melting, de-gassing and other processing of aluminum-silicon or aluminum-copper alloys can be used without modification for conventional casting of aluminum-cerium alloys.

  10. In vitro and in vivo studies on biodegradable magnesium alloy

    Directory of Open Access Journals (Sweden)

    Lida Hou


    Full Text Available The microstructure, mechanical property, electrochemical behavior and biocompatibility of magnesium alloy (BioDe MSM™ were studied in the present work. The experimental results demonstrated that grain refining induced by extrusion improves the alloy strength significantly from 162 MPa for the as-cast alloy to 241 MPa for the as-extruded one. The anticorrosion properties of the as-extruded alloy also increased. Furthermore, the hemolysis ratio was decreased from 4.7% for the as-cast alloy to 2.9% for the as-extruded one, both below 5%. BioDe MSM™ alloy shows good biocompatibility after being implanted into the dorsal muscle and the femoral shaft of the New Zealand rabbit, respectively, and there are no abnormalities after short-term implantation. In vivo observation indicated that the corrosion rate of this alloy varies with different implantation positions, with higher degradation rate in the femur than in the muscle.

  11. Effects of surface poisons on the oxidation of binary alloys

    Energy Technology Data Exchange (ETDEWEB)

    Hagan, P.S.; Polizzotti, R.S.; Luckman, G.


    A system of reaction-diffusion equations describing the oxidation of binary alloys in environments containing small amounts of surface poisons is analyzed. These poisons reduce the oxygen flux into the alloy, which causes the alloy to oxidize in two stages.During the initial stage, the oxidation reaction occurs in a stationary boundary layer at the alloy surface. Consequently, a thin zone containing a very high concentration of the metal oxide is created at the alloy surface. During the second stage, the oxidation reaction occurs in a moving boundary layer. This leads to a Stefan problem, which is analyzed by using asymptotic and numerical techniques. By comparing the solutions to those of alloys in unpoisoned environments, it is concluded that surface poisons can lead to the formation of protective external oxide scales in alloys which would not normally form such scales. 11 references.

  12. Development of Lead-Free Copper Alloy-Graphite Castings

    Energy Technology Data Exchange (ETDEWEB)

    Rohatgi, P.K. [Univ. of Wisconsin-Milwaukee (US)


    In this project, graphite is used as a substitute for lead in order to maintain the machinability of plumbing components at the level of leaded brass. Graphite dispersed in Cu alloy was observed to impart good machinability and reduce the sizes of chips during machining of plumbing components in a manner similar to lead. Copper alloys containing dispersed graphite particles could be successfully cast in several plumbing fixtures which exhibited acceptable corrosion rate, solderability, platability, and pressure tightness. The power consumption for machining of composites was also lower than that of the matrix alloy. In addition, centrifugally cast copper alloy cylinders containing graphite particles were successfully made. These cylinders can therefore be used for bearing applications, as substitutes for lead-containing copper alloys. The results indicate that copper graphite alloys developed under this DOE project have a great potential to substitute for lead copper alloys in both plumbing and bearing applications.

  13. Biaxial Thermal Creep of Alloy 617 and Alloy 230 for VHTR Applications

    Energy Technology Data Exchange (ETDEWEB)

    Mo, Kun; Lv, Wei; Tung, Hsiao-Ming; Yun, Di; Miao, Yinbin; Lan, Kuan-Che; Stubbins, James F.


    In this study, we employed pressurized creep tubes to investigate the biaxial thermal creep behavior of Inconel 617 (alloy 617) and Haynes 230 (alloy 230). Both alloys are considered to he the primary candidate structural materials for very high-temperature reactors (VITITRs) due to their exceptional high-temperature mechanical properties. The current creep experiments were conducted at 900 degrees C for the effective stress range of 15-35 MPa. For both alloys, complete creep strain development with primary, secondary, and tertiary regimes was observed in all the studied conditions. Tertiary creep was found to he dominant over the entire creep lives of both alloys. With increasing applied creep stress, the fraction of the secondary creep regime decreases. The nucleation, diffusion, and coarsening of creep voids and carbides on grain boundaries were found to be the main reasons for the limited secondary regime and were also found to be the major causes of creep fracture. The creep curves computed using the adjusted creep equation of the form epsilon= cosh 1(1 rt) + P-sigma ntm agree well with the experimental results for both alloys at die temperatures of 850-950 degrees C.

  14. Effect of mechanical alloying on FeCrC reinforced Ni alloys

    Energy Technology Data Exchange (ETDEWEB)

    Yilmaz, S. Osman [Univ. of Namik Kemal, Tekirdag (Turkey); Teker, Tanju [Adiyaman Univ. (Turkey). Dept. of Metallurgical and Materials Engineering; Demir, Fatih [Batman Univ. (Turkey)


    Mechanical alloying (MA) is a powder metallurgy processing technique involving cold welding, fracturing and rewelding of powder particles in a high-energy ball mill. In the present study, the intermetallic matrix composites (IMCs) of Ni-Al reinforced by M{sub 7}C{sub 3} were produced by powder metallurgical routes via solid state reaction of Ni, Al and M{sub 7}C{sub 3} particulates by mechanical alloying processes. Ni, Al and M{sub 7}C{sub 3} powders having 100 μm were mixed, mechanical alloyed and the compacts were combusted in a furnace. The mechanically alloyed (MAed) powders were investigated by X-ray diffraction (XRD), microhardness measurement, optic microscopy (OM), scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS). The presence of the carbides depressed the formation of unwanted NiAl intermetallic phases. The mechanical alloyed M{sub 7}C{sub 3} particles were unstable and decomposed partially within the matrix during alloying and sintering, and the morphology of the composites changed with the dissolution ratio of M{sub 7}C{sub 3} and sintering temperature.

  15. Effect of Al alloying on the martensitic temperature in Ti-Ta shape memory alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ferrari, Alberto; Rogal, Jutta; Drautz, Ralf [Interdisciplinary Centre for Advanced Materials Simulation, Ruhr-Universitaet Bochum (Germany)


    Ti-Ta-based alloys are promising candidates as high temperature shape memory alloys (HTSMAs) for actuators and superelastic applications. The shape memory mechanism involves a martensitic transformation between the low-temperature α'' phase (orthorhombic) and the high-temperature β phase (body-centered cubic). In order to prevent the degradation of the shape memory effect, Ti-Ta needs to be alloyed with further elements. However, this often reduces the martensitic temperature M{sub s}, which is usually strongly composition dependent. The aim of this work is to analyze how the addition of a third element to Ti-Ta alloys affects M{sub s} by means of electronic structure calculations. In particular, it will be investigated how alloying Al to Ti-Ta alters the relative stability of the α'' and β phases. This understanding will help to identify new alloy compositions featuring both a stable shape memory effect and elevated transformation temperatures.

  16. Alloy development and mechanical properties of nickel aluminide (Ni sub 3 Al) alloys

    Energy Technology Data Exchange (ETDEWEB)

    Liu, C.T.; Sikka, V.K.; Horton, J.A.; Lee, E.H.


    This report summarizes recent alloy development of nickel aluminides for structural applications. Boron-doped Ni{sub 3}Al showed severe embrittlement when tested in oxidizing environments above 300{degrees}C. The embrittlement is due to a dynamic effect, which can be alleviated by alloying with 8 at. % Cr. The chromium-modified aluminide alloys possess a good combination of strength and ductility for use at temperatures to 1000{degrees}C. The hot ductility and fabricability of the aluminide alloys can be substantially improved by reducing the zirconium content to below 0.35 at. %. Material processing of large aluminide heats has been demonstrated by both conventional and innovative techniques. Mechanical properties of the aluminide alloys were characterized at temperatures to 1200{degrees}C. Grain size, which is the main difference between the materials produced by the various processing techniques, is the major metallurgical parameter that strongly influences the mechanical properties of the aluminide alloys. 35 refs., 20 figs., 11 tabs.

  17. Magnetic field-induced solvothermal synthesis of one-dimensional assemblies of Ni-Co alloy microstructures

    National Research Council Canada - National Science Library

    Hu, Ming Jun; Lin, Bin; Yu, Shu Hong


    One-dimensional magnetic Ni-Co alloy microwires with different microstructures and differently shaped building blocks including spherical particles, multilayer stacked alloy plates, and alloy flowers...

  18. Diagnostic value of thallium-201 myocardial perfusion IQ-SPECT without and with computed tomography-based attenuation correction to predict clinically significant and insignificant fractional flow reserve: A single-center prospective study. (United States)

    Tanaka, Haruki; Takahashi, Teruyuki; Ohashi, Norihiko; Tanaka, Koichi; Okada, Takenori; Kihara, Yasuki


    The aim of this study was to clarify the predictive value of fractional flow reserve (FFR) determined by myocardial perfusion imaging (MPI) using thallium (Tl)-201 IQ-SPECT without and with computed tomography-based attenuation correction (CT-AC) for patients with stable coronary artery disease (CAD).We assessed 212 angiographically identified diseased vessels using adenosine-stress Tl-201 MPI-IQ-SPECT/CT in 84 consecutive, prospectively identified patients with stable CAD. We compared the FFR in 136 of the 212 diseased vessels using visual semiquantitative interpretations of corresponding territories on MPI-IQ-SPECT images without and with CT-AC.FFR inversely correlated most accurately with regional summed difference scores (rSDS) in images without and with CT-AC (r = -0.584 and r = -0.568, respectively, both P < .001). Receiver-operating characteristics analyses using rSDS revealed an optimal FFR cut-off of <0.80 without and with CT-AC. Although the diagnostic accuracy of FFR <0.80 did not significantly differ, FFR ≥0.82 was significantly more accurate with, than without CT-AC. Regions with rSDS ≥2 without or with CT-AC predicted FFR <0.80, and those with rSDS ≤1 without and with CT-AC predicted FFR ≥0.81, with 73% and 83% sensitivity, 84% and 67% specificity, and 79% and 75% accuracy, respectively.Although limited by the sample size and the single-center design, these findings showed that the IQ-SPECT system can predict FFR at an optimal cut-off of <0.80, and we propose a novel application of CT-AC to MPI-IQ-SPECT for predicting clinically significant and insignificant FFR even in nonobese patients. Copyright © 2017 The Authors. Published by Wolters Kluwer Health, Inc. All rights reserved.

  19. Dual myocardial single photon emission computed tomography (SPECT) using thallium-201 and I-123-{beta}-methyl-i-pentadecanoic acid in patients with Duchenne's progressive muscular dystrophy

    Energy Technology Data Exchange (ETDEWEB)

    Shimoyama, Katsuya [Kyorin Univ., Mitaka, Tokyo (Japan). School of Medicine


    Dual single photon emission computed tomography (SPECT) was performed in 31 patients with Duchenne's progressive muscular dystrophy (DMD) using {sup 123}I-{beta}-methyl pentadecanoic acid (BMIPP) for myocardial fatty acid metabolism and {sup 201}thallium (Tl)-chloride for myocardial perfusion. The left ventricle was divided into 9 segments, and accumulation of the radiotracers was assessed visually for each segment to calculate defect score for each tracer. There was some degree of decrease in myocardial accumulation of both tracers in all DMD patients. Reduced accumulation was most common at the apex (BMIPP: 67%, Tl: 63%), followed by the posterior wall, lateral wall, and anterior wall. On the other hand, reduced accumulation was less common at the septum. BMIPP showed a higher accumulation than Tl in all segments but the septum. When BMIPP defect score was larger than Tl defect score, BMIPP defect score tended to increase during 4 years follow-up (p<0.042). However, when Tl defect score was larger than BMIPP defect score, an increase in Tl defect score was slight. A significant negative correlation was found between the sum of the BMIPP and Tl defect scores and the left ventricular ejection fraction (LVEF) (r=0.66, p<0.0001). According to the histo-pathological study of two autopsied hearts, severe myocardial fibrosis was seen in segments with fixed perfusion defect. In addition, the mismatched segments of BMIPP defect score > Tl defect score revealed a slight fibrosis or normal myocardium. It can be concluded that the dual SPECT myocardial scintigraphy using BMIPP and Tl provides accurate information about disease progression of the heart in patients with DMD by detecting abnormalities of the myocardial metabolism of each substance, thereby enabling the assessment of left ventricular function. (author)

  20. Reduction in Defect Content of ODS Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ritherdon, J


    The work detailed within this report is a continuation of earlier work carried out under contract number 1DX-SY382V. The earlier work comprises a literature review of the sources and types of defects found principally in Fe-based ODS alloys as well as experimental work designed to identify defects in the prototype ODS-Fe{sub 3}Al alloy, deduce their origins and to recommend methods of defect reduction. The present work is an extension of the experimental work already reported and concentrates on means of reduction of defects already identified rather than the search for new defect types. This report also includes results gathered during powder separation trials, conducted by the University of Groningen, Netherlands and coordinated by the University of Liverpool, involving the separation of different metallic powders in terms of their differing densities. The scope and objectives of the present work were laid out in the technical proposal ''Reduction in Defect Content in ODS Alloys-III''. All the work proposed in the ''Statement of Work'' section of the technical proposal has been carried out and all work extra to the ''Statement of Work'' falls within the context of an ODS-Fe{sub 3}Al alloy of improved overall quality and potential creep performance in the consolidated form. The outturn of the experimental work performed is reported in the following sections.

  1. High temperature alloy chloridation at 850 C

    Energy Technology Data Exchange (ETDEWEB)

    Chevalier, S.; Bekaddour, A. [Laboratoire de Recherches sur la Reactivite des Solides, UMR 5613 CNRS, Universite de Bourgogne, 9 avenue Alain Savary, 21078 Dijon (France); Ched' Homme, S. [DTM/SRPU/LPPU, CEA Valduc, 21120 Is-sur-Tille (France); Amilain-Basset, K.; Buisson, L. [Interface Caracterisation des Materiaux, Universite de Bourgogne, 21078 Dijon (France)


    The resistance of eight alloys against chloridation was tested at 850 C in Ar/Cl{sub 2} (2.5% Cl{sub 2}) for 15 min. Pre-oxidation treatments were performed for 1 h and 8 h at 850 C in order to produce a thin, adherent and protective oxide scale able to improve the chloridation behaviour of the tested materials. The chloridised sample morphologies were compared to the morphologies observed on the non pre-oxidised samples. The alloys containing a large amount of iron did not exhibit any chloridation resistance, even after pre-oxidation, and were severely damaged. The nickel based alloys gave interesting results but were also attacked by chloride, probably by the ''active oxidation'' mechanism. The duration of the pre-oxidation treatment plays an important role, since the 8 h pre-oxidation appears more beneficial than the 1 h pre-oxidation, to delay the chloridation, probably because of the best quality of the oxide layer grown during 8 h. For the nickel based materials, the effects of chloride appear less severe than for the iron-based alloys, but are not stopped. The ''active oxidation'' mechanism is proposed to be responsible for the degradation of the tested materials. (Abstract Copyright [2007], Wiley Periodicals, Inc.)

  2. Discontinuous precipitation in copper base alloys

    Indian Academy of Sciences (India)


    Abstract. Discontinuous precipitation (DP) is associated with grain boundary migration in the wake of which alternate plates of the precipitate and the depleted matrix form. Some copper base alloys show DP while others do not. In this paper the misfit strain parameter, η, has been calculated and predicted that if.

  3. Zirconium modified nickel-copper alloy (United States)

    Whittenberger, J. D. (Inventor)


    An improved material for use in a catalytic reactor which reduces nitrogen oxide from internal combustion engines is in the form of a zirconium-modified, precipitation-strengthened nickel-copper alloy. This material has a nominal composition of Ni-30 Cu-0.2 Zr and is characterized by improved high temperature mechanical properties.

  4. Dendritic Solidification in a Copper Nickel Alloy


    DÜNDAR, Sacit


    The distribution of nickel in dendrite arms and in interdendritic regions of copper-10% nickel alloy solidified under production conditions designed to provide 4 different cooling rates was investigated. The results indicate that at different rates of solidification undercooling, diffusion and convection mechanisms affect the microsegregation of nickel and copper in the cast materials to various extents.

  5. Materials data handbook on Inconel Alloy 718 (United States)

    Muraca, R. F.; Whittick, J. S.


    Handbook is divided into twelve chapters. Scope of information presented includes physical- and mechanical-property data at cryogenic, ambient, and elevated temperatures. This is supplemented with useful information in such areas as material procurement, metallurgy of alloy, corrosion, environmental effect, fabrication, and joining techniques. Design data are presented, as available.

  6. In vivo effects of dental casting alloys

    Czech Academy of Sciences Publication Activity Database

    Venclíková, Z.; Benada, Oldřich; Bártová, J.; Joska, L.; Mrklas, L.; Procházková, J.; Stejskal, V.D.M.; Podzimek, Š.


    Roč. 27, č. 1 (2006), s. 25-32 ISSN 0172-780X R&D Projects: GA MZd NK7437 Institutional research plan: CEZ:AV0Z50200510 Keywords : dental alloys * metals * gingiva Subject RIV: EE - Microbiology, Virology Impact factor: 0.924, year: 2006

  7. Laser polishing of additive manufactured Ti alloys (United States)

    Ma, C. P.; Guan, Y. C.; Zhou, W.


    Laser-based additive manufacturing has attracted much attention as a promising 3D printing method for metallic components in recent years. However, surface roughness of additive manufactured components has been considered as a challenge to achieve high performance. In this work, we demonstrate the capability of fiber laser in polishing rough surface of additive manufactured Ti-based alloys as Ti-6Al-4V and TC11. Both as-received surface and laser-polished surfaces as well as cross-section subsurfaces were analyzed carefully by White-Light Interference, Confocal Microscope, Focus Ion Beam, Scanning Electron Microscopy, Energy Dispersive Spectrometer, and X-ray Diffraction. Results revealed that as-received Ti-based alloys with surface roughness more than 5 μm could be reduce to less than 1 μm through laser polishing process. Moreover, microstructure, microhardness and wear resistance of laser-polished zone was investigated in order to examine the thermal effect of laser polishing processing on the substrate of additive manufactured Ti alloys. This proof-of-concept process has the potential to effectively improve the surface roughness of additive manufactured metallic alloy by local polishing method without damage to the substrate.

  8. Deformation heterogeneity in cellular Al alloys

    Energy Technology Data Exchange (ETDEWEB)

    Bastawros, A.-F. [Iowa State Univ., Ames, IA (United States). Dept. of Aerospace Engineering and Mechanics; Evans, A.G. [Princeton Univ., NJ (United States). Materials Inst.


    Cell ellipticity and non-planar membranes are thought to be dominant degradation factors of cellular metals. The mechanisms operating at the cell/membrane level in both closed and open cell Al alloys have been established by following the evolution of deformation with cell-level resolution using digital image correlation analysis. (orig.)

  9. Nickel-titanium alloys: a systematic review

    Directory of Open Access Journals (Sweden)

    Marcelo do Amaral Ferreira


    Full Text Available OBJECTIVE: A systematic review on nickel-titanium wires was performed. The strategy was focused on Entrez-PubMed-OLDMEDLINE, Scopus and BioMed Central from 1963 to 2008. METHODS: Papers in English and French describing the behavior of these wires and laboratorial methods to identify crystalline transformation were considered. A total of 29 papers were selected. RESULTS: Nickel-titanium wires show exceptional features in terms of elasticity and shape memory effects. However, clinical applications request a deeper knowledge of these properties in order to allow the professional to use them in a rational manner. In addition, the necessary information regarding each alloy often does not correspond to the information given by the manufacturer. Many alloys called "superelastic" do not present this effect; they just behave as less stiff alloys, with a larger springback if compared to the stainless steel wires. CONCLUSIONS: Laboratory tests are the only means to observe the real behavior of these materials, including temperature transition range (TTR and applied tensions. However, it is also possible to determine in which TTR these alloys change the crystalline structure.

  10. Structure of Liquid Na-K Alloys

    NARCIS (Netherlands)

    Alblas, B.P.; Lugt, W. van der; Valk, H.J.L. van der; Hosson, J.Th.M. De; Dijk, C. van


    X-ray and neutron diffraction data are presented for a number of liquid Na-K alloys covering the whole composition range. Additionally, for the composition 50 at.% Na - 50 at.% K, a computer experiment in molecular dynamics has been carried out. An attempt is made to analyze the results in terms of

  11. Cytotoxicity of titanium and titanium alloying elements. (United States)

    Li, Y; Wong, C; Xiong, J; Hodgson, P; Wen, C


    It is commonly accepted that titanium and the titanium alloying elements of tantalum, niobium, zirconium, molybdenum, tin, and silicon are biocompatible. However, our research in the development of new titanium alloys for biomedical applications indicated that some titanium alloys containing molybdenum, niobium, and silicon produced by powder metallurgy show a certain degree of cytotoxicity. We hypothesized that the cytotoxicity is linked to the ion release from the metals. To prove this hypothesis, we assessed the cytotoxicity of titanium and titanium alloying elements in both forms of powder and bulk, using osteoblast-like SaOS(2) cells. Results indicated that the metal powders of titanium, niobium, molybdenum, and silicon are cytotoxic, and the bulk metals of silicon and molybdenum also showed cytotoxicity. Meanwhile, we established that the safe ion concentrations (below which the ion concentration is non-toxic) are 8.5, 15.5, 172.0, and 37,000.0 microg/L for molybdenum, titanium, niobium, and silicon, respectively.

  12. Hydrogenation properties of Mg-Al alloys

    DEFF Research Database (Denmark)

    Andreasen, Anders


    . Further, it is found that the kinetics of hydrogenation, as well dehydrogenation, may be significantly improved by alloying compared to pure Mg. The expense of these improvements of the hydrogenation/dehydrogenation properties is a lower gravimetric hydrogen density in the hydrogenated product, (C) 2008...

  13. Gold-nickel-titanium brazing alloy (United States)

    Mizuhara, Howard


    A brazing alloy in accordance with this invention has the following composition, by weight: 91 to 99% gold, 0.5 to 7% nickel; 0.10 to 2% titanium. Alternatively, with palladium present, the composition is as follows, by weight: 83 to 96% gold; 3 to 10% palladium; 0.5 to 5% nickel; 0.10 to 2% titanium.

  14. Discontinuous precipitation in copper base alloys

    Indian Academy of Sciences (India)

    Discontinuous precipitation (DP) is associated with grain boundary migration in the wake of which alternate plates of the precipitate and the depleted matrix form. Some copper base alloys show DP while others do not. In this paper the misfit strain parameter, , has been calculated and predicted that if 100 > ± 0.1, DP is ...

  15. Microstructure Development during Solidification of Aluminium Alloys

    NARCIS (Netherlands)

    Ruvalcaba Jimenez, D.G.


    This Thesis demonstrates studies on microstructure development during the solidification of aluminium alloys. New insights of structure development are presented here. Experimental techniques such as quenching and in-situ High-brilliance X-ray microscopy were utilized to study the microstructure

  16. Shape memory alloys – characterization techniques

    Indian Academy of Sciences (India)

    A space-rotating platform is designed and fabricated, using an actuator of shape memory spring, for obtaining controlled rotations. The efficiency and the reliability of this actuator has been tested, over a million thermal cycles. Keywords. Shape memory alloys; characterization techniques; austenitic phase; martensitic phase;.

  17. Corrosion of carbon-alloyed iron aluminides

    Indian Academy of Sciences (India)


    Corrosion of carbon-alloyed iron aluminides. M SEN, R BALASUBRAMANIAM* and A V RAMESH KUMAR†. Department of Materials and Metallurgical Engineering, Indian Institute of Technology, Kanpur 208 016, India. †Defence Materials Stores and Research Development Establishment, Kanpur 208 013, India.

  18. Biocompatibility of nickel and cobalt dental alloys. (United States)

    Grimaudo, N J


    Allergies related to dentistry generally constitute delayed hypersensitivity reactions to specific dental materials. Although true allergic hypersensitivity to dental materials is rare, certain products have definite allergenic properties. This review presents a comparative evaluation of the biocompatibility of nickel-chromium, nickel-chromium-beryllium, and cobalt-chromium alloys.

  19. Antiferromagnetism in chromium alloy single crystals

    DEFF Research Database (Denmark)

    Bjerrum Møller, Hans; Trego, A.L.; Mackintosh, A.R.


    The antiferromagnetism of single crystals of dilute alloys of V, Mn and Re in Cr has been studied at 95°K and 300°K by neutron diffraction. The addition of V causes the diffraction peaks to decrease in intensity and move away from (100), while Mn and Re cause them to increase and approach (100) s...

  20. Localized Corrosion of Alloy 22 -Fabrication Effects-

    Energy Technology Data Exchange (ETDEWEB)

    Rebak, R B


    This report deals with the impact of fabrication processes on the localized corrosion behavior of Alloy 22 (N06022). The four fabrication processes that were analyzed are: (1) Surface stress mitigation of final closure weld, (2) Manufacturing of the mockup container, (3) Black annealing of the container and (4) Use of different heats of Alloy 22 for container fabrication. Immersion and Electrochemical tests performed in the laboratory are generally aggressive and do not represent actual repository environments in Yucca Mountain. For example, to determine the intergranular attack in the heat affected zone of a weldment, tests are conducted in boiling acidic and oxidizing solutions according to ASTM standards. These solutions are used to compare the behavior of differently treated metallic coupons. Similarly for electrochemical tests many times pure sodium chloride or calcium chloride solutions are used. Pure chloride solutions are not representative of the repository environment. (1) Surface Stress Mitigation: When metallic plates are welded, for example using the Gas Tungsten Arc Welding (GTAW) method, residual tensile stresses may develop in the vicinity of the weld seam. Processes such as Low Plasticity Burnishing (LPB) and Laser Shock Peening (LSP) could be applied locally to eliminate the residual stresses produced by welding. In this study, Alloy 22 plates were welded and then the above-mentioned surface treatments were applied to eliminate the residual tensile stresses. The aim of the current study was to comparatively test the corrosion behavior of as-welded (ASW) plates with the corrosion behavior of plates with stress mitigated surfaces. Immersion and electrochemical tests were performed. Results from both immersion and electrochemical corrosion tests show that the corrosion resistance of the mitigated plates was not affected by the surface treatments applied. (2) Behavior of Specimens from a Mockup container: Alloy 22 has been extensively tested for