  1. Elastic properties of sub-stoichiometric nitrogen ion implanted silicon

    Energy Technology Data Exchange (ETDEWEB)

    Sarmanova, M.F., E-mail: marina.sarmanova@iom-leipzig.de [Leibniz Institute of Surface Modification, D-04318 Leipzig (Germany); Karl, H. [University Augsburg, Institute of Physics, D-86135 Augsburg (Germany); Mändl, S.; Hirsch, D. [Leibniz Institute of Surface Modification, D-04318 Leipzig (Germany); Mayr, S.G.; Rauschenbach, B. [Leibniz Institute of Surface Modification, D-04318 Leipzig (Germany); University Leipzig, Institute for Experimental Physics II, D-04103 Leipzig (Germany)

    2015-04-15

    Elastic properties of sub-stoichiometric nitrogen implanted silicon were measured with nanometer-resolution using contact resonance atomic force microscopy (CR-AFM) as function of ion fluence and post-annealing conditions. The determined range of indentation moduli was between 100 and 180 GPa depending on the annealing duration and nitrogen content. The high indentation moduli can be explained by formation of Si–N bonds, as verified by X-ray photoelectron spectroscopy.

  2. On the stability of sub-stoichiometric uranium oxides

    Science.gov (United States)

    Winer, K.; Colmenares, C. A.; Smith, R. L.; Wooten, F.

    1986-12-01

    The oxidation of clean, high-purity polycrystalline uranium metal surfaces for low exposures to dry oxygen was studied with AES and XPS in an attempt to substantiate claims for the formation of a stable UO surface phase at ambient temperatures. We found no evidence for such a surface phase and found instead that grossly sub-stoichiometric surface oxides were formed after sequential oxygen saturation and heating.

  3. Second-harmonic generation in substoichiometric silicon nitride layers

    Science.gov (United States)

    Pecora, Emanuele; Capretti, Antonio; Miano, Giovanni; Dal Negro, Luca

    2013-03-01

    Harmonic generation in optical circuits offers the possibility to integrate wavelength converters, light amplifiers, lasers, and multiple optical signal processing devices with electronic components. Bulk silicon has a negligible second-order nonlinear optical susceptibility owing to its crystal centrosymmetry. Silicon nitride has its place in the microelectronic industry as an insulator and chemical barrier. In this work, we propose to take advantage of silicon excess in silicon nitride to increase the Second Harmonic Generation (SHG) efficiency. Thin films have been grown by reactive magnetron sputtering and their nonlinear optical properties have been studied by femtosecond pumping over a wide range of excitation wavelengths, silicon nitride stoichiometry and thermal processes. We demonstrate SHG in the visible range (375 - 450 nm) using a tunable 150 fs Ti:sapphire laser, and we optimize the SH emission at a silicon excess of 46 at.% demonstrating a maximum SHG efficiency of 4x10-6 in optimized films. Polarization properties, generation efficiency, and the second order nonlinear optical susceptibility are measured for all the investigated samples and discussed in terms of an effective theoretical model. Our findings show that the large nonlinear optical response demonstrated in optimized Si-rich silicon nitride materials can be utilized for the engineering of nonlinear optical functions and devices on a Si chip.

  4. Triphenyl phosphine oxide as a substoichiometric radiochemical reagent: Determination of thallium

    International Nuclear Information System (INIS)

    Reddy, P.C.; Polaiah, B.; Rangamannar, B.

    1991-01-01

    A rapid radiochemical method has been developed for the determination of microgram amounts of thallium based on the substoichiometric extraction of its ocmplex with triphenylphosphine oxide into benzene from 6 M sulphuric acid. 10-90 μg of thallium was determined with an average error of 2.06%. The effect of diverse metal ions on the extraction was studied. (orig.)

  5. Etch-stop behavior of buried layers formed by substoichiometric nitrogen ion implantation into silicon

    International Nuclear Information System (INIS)

    Perez-Rodriguez, A.; Romano-Rodriguez, A.; Morante, J.R.; Acero, M.C. Esteve, J.; Montserrat, J.; El-Hassani, A.

    1996-01-01

    In this work the etch-stop behavior of buried layers formed by substoichiometric nitrogen ion implantation into silicon is studied as a function of the processing parameters, the implantation dose and temperature, and the presence of capping layers during implantation. Etching characteristics have been probed using tetramethylammonium hydroxide or KOH solutions for different times up to 6 h. Results show that, after annealing, the minimum dose required for the formation of an efficient etch-stop layer is about 4 x 10 17 cm -2 , for an implantation energy of 75 keV. This is defined as a layer with an efficient etch selectivity in relation to Si of s ≥ 100. For larger implantation doses efficient etch selectivities larger than 100 are obtained. However, for these doses a considerable density of pits is observed in the etch-stop layer. These are related to the presence of nitrogen poor Si regions in the buried layer after annealing, due to a partial separation of silicon and silicon nitride phases during the annealing process. The influence of this separation of phases as well as nitrogen gettering in the buried layer on the etch-stop behavior is discussed as a function of the processing parameters

  6. Substoichiometric cobalt oxide monolayer on Ir(100)-(1 x 1)

    International Nuclear Information System (INIS)

    Gubo, M; Ebensperger, C; Meyer, W; Hammer, L; Heinz, K

    2009-01-01

    A substoichiometric monolayer of cobalt oxide has been prepared by deposition and oxidation of slightly less than one monolayer of cobalt on the unreconstructed surface of Ir(100). The ultrathin film was investigated by scanning tunnelling microscopy (STM) and quantitative low-energy electron diffraction (LEED). The cobalt species of the film reside in or near hollow positions of the substrate with, however, unoccupied sites (vacancies) in a 3 x 3 arrangement. In the so-formed 3 x 3 supercell the oxide's oxygen species are both threefold and fourfold coordinated to cobalt, forming pyramids with a triangular and square cobalt basis, respectively. These pyramids are the building blocks of the oxide. Due to the reduced coordination as compared to the sixfold one in the bulk of rock-salt-type CoO, the Co-O bond lengths are smaller than in the latter. For the threefold coordination they compare very well with the bond length in oxygen terminated CoO(111) films investigated recently. The substoichiometric 3 x 3 oxide monolayer phase transforms to a stoichiometric c(10 x 2)-periodic oxide monolayer under oxygen exposure, in which, however, cobalt and oxygen species are in (111) orientation and so form a CoO(111) layer.

  7. Hot-wire substoichiometric tungsten oxide films deposited in hydrogen environment with n-type conductivity

    International Nuclear Information System (INIS)

    Kostis, I; Vasilopoulou, M; Giannakopoulos, K; Papadimitropoulos, G; Davazoglou, D; Michalas, L; Papaioannou, G; Konofaos, N; Iliadis, A A; Kennou, S

    2012-01-01

    Substoichiometric tungsten oxide nanostructured films were synthesized by a hot-wire deposition technique in hydrogen-rich environment and characterized for their structural and electrical properties. A semiconducting behaviour was identified, allowing n-type conductivity even at room temperature which is an important result since it is well known that fully stoichiometric tungsten trioxide is nearly an insulator. Current-voltage characteristics for various temperatures were measured for tungsten oxide/Si heterostructures and analysed using proper modelling. As a result, the conduction mechanism inside the films was identified and found to be of a dual nature, with variable range hopping being dominant at near room temperatures. The saturation current was found to be thermally activated and the activation energy was calculated at 0.40 eV and the grain boundaries barrier at 150 meV. From Hall measurements it was also revealed that the dominant carriers are electrons and a carrier concentration of about 10 14 cm -3 was estimated.

  8. Substoichiometric extraction of phosphorus

    International Nuclear Information System (INIS)

    Shigematsu, T.; Kudo, K.

    1981-01-01

    A study of the substoichiometric extraction of phosphorus is described. Phosphorus was extracted in the form of ternary compounds such as ammonium phosphomolybdate, 8-hydroxyquinolinium phosphomolybdate, tetraphenylarsonium phosphomolybdate and tri-n-octylamine phosphomolybdate. Consequently, phosphorus was extracted substoichiometrically by the addition of a substoichiometric amount of molybdenum for the four phosphomolybdate compounds. On the other hand, phosphorus could be separated substoichiometrically with a substoichiometric amount of tetraphenylarsonium chloride or tri-n-octylamine. Stoichiometric ratios of these ternary compounds obtained substoichiometrically were 1:12:3 for phosphorus, molybdenum and organic reagent. The applicability of these compounds to phosphorus determination is also discussed. (author)

  9. Buried oxide layer in silicon

    Science.gov (United States)

    Sadana, Devendra Kumar; Holland, Orin Wayne

    2001-01-01

    A process for forming Silicon-On-Insulator is described incorporating the steps of ion implantation of oxygen into a silicon substrate at elevated temperature, ion implanting oxygen at a temperature below 200.degree. C. at a lower dose to form an amorphous silicon layer, and annealing steps to form a mixture of defective single crystal silicon and polycrystalline silicon or polycrystalline silicon alone and then silicon oxide from the amorphous silicon layer to form a continuous silicon oxide layer below the surface of the silicon substrate to provide an isolated superficial layer of silicon. The invention overcomes the problem of buried isolated islands of silicon oxide forming a discontinuous buried oxide layer.

  10. Substoichiometric extraction of chromium

    International Nuclear Information System (INIS)

    Shigematsu, T.; Kudo, K.

    1980-01-01

    Substoichiometric extraction of chromium with tetraphenylarsonium chloride (TPACl), tri-n-octylamine (TNOA), diethylammonium diethyldithiocarbamate (DDDC) and ammonium pyrrolidinedithiocarbamate (APDC) was examined in detail. Chromium can be extracted substoichiometrically in a pH range, which is 1.1-2.6 for the TPACl compound, 0.6-2.3 for the TNOA compound, 5.1-6.4 for the DDDC chelate and 3.9-4.9 for the APDC chelate. Chromium in high-purity calcium carbonate, Orchard Leaves (NBS SRM-1571) and Brewers Yeast (NBS SRM-1569) was determined by neutron activation analysis combined with substoichiometric extraction by DDDC and APDC. The values of 2.0+-0.02 ppm and 2.6+-0.2 ppm were obtained for Brewers Yeast and Orchard Leaves, respectively. These values were in good agreement with those reported by NBS. The reaction mechanism and the reaction ratio between hexavalent chromium and dithiocarbamate are also discussed. (author)

  11. Phosphorus determination by various substoichiometric methods

    International Nuclear Information System (INIS)

    Shigematsu, Toshio; Kudo, Kiyoshi

    1981-01-01

    Various substoichiometric methods have been classified from a view point of the substoichiometric separation. Based upon the substoichiometric separation, phosphorus was determined substoichiometrically by a direct method, a method of carrier amount variation and a comparison method for the irradiated sample. The direct method was applied to the determination of phosphorus in orchard leaves (SRM-1571). The analytical value was 0.23 +- 0.01%. Phosphorus in orchard leaves and spinach (SRM-1570) was determined by an ordinary method which devided the sample into equal parts in the method of carrier amount variation. Analytical values of orchard leaves and spinach were 0.22 +- 0.02% and 0.56 +- 0.04%, respectively. Moreover, a new modification of the method of carrier amount variation was studied by the use of various standard samples such as red phosphorus, spinach and orchard leaves. These standard samples were also employed for the determination of phosphorus in orchard leaves and 0.21 +- 0.01% was obtained. All these results are in good agreement with the value reported by NBS. The comparison method was applied to the determination of phosphorus in a semiconductor silicon single crystal. As a result of the correction of 32 P activity induced by the secondary nuclear reaction of 30 Si, 7.9 ppb and 3.1 ppb were obtained for the phosphorus concentrations in the single crystal silicon. (author)

  12. Substoichiometric determination of phosphorus

    International Nuclear Information System (INIS)

    Shigematsu, T.; Kudo, K.

    1981-01-01

    Phosphorus in orchard leaves (NBS SRM-1571) and spinach (SRM-1570) was determined by various substoichiometric analytical methods such as the direct method, Gravshchenko's method and the method of carrier amount variation. All samples were labelled with 32 P radioisotope. The data obtained by the method of carrier amount variation were also treated by the method of least squares instead of De Voe's method. Phosphorus concentration in orchard leaves was 0.206+-0.011% by the direct method, 0.219+-0.011% by Gravshchenko's method, 0.211+-0.011% by the method of carrier amount variation and 0.207+-0.007% by the method of least squares, respectively. These values agree with the value reported by NBS (0.21+-0.01%). Furthermore, these concentrations obtained by various substoichiometric methods were compared with those by radioactivation reported in a previous paper. (author)

  13. Radiochemical determination of thallium by substoichiometric reduction

    International Nuclear Information System (INIS)

    Muralidhar, N.; Rangamannar, B.; Krishnan, V.R.

    1983-01-01

    A method was developed for the determination of thallium by substoichiometric reduction of Tl(III) with thiourea and separation of the two oxidation states by the extraction of the former into iso-amyl acetate. Thiourea reduces Tl(III) at room temperature quantitatively, with a 2:1 stoichiometry. 2-25 μg Tl can be determined by this method with a precision of 4%. (author)

  14. Substoichiometric neutron activation determination of gold

    International Nuclear Information System (INIS)

    Mitchell, J.W.; Riley, J.E. Jr.; Payne, V.

    1978-01-01

    A highly precise and selective method is described for the determination of traces of gold by substoichiometric extraction from hydrochloric acid with tri-n-octylphosphine sulfide in cyclohexane following thermal neutron activation. Fundamental aspects of the extraction system are discussed and results are reported for the determination of gold in an effluent from a recovery process containing a complexed species of gold and unknown amounts of cyanide, citrate, phosphate, potassium and sodium. Other constituents of the effluent stream include traces of the transition elements Co, Ni, Fe, Cu, Zn, Pb and Sn at concentrations less than 50 ppm. One hour was allowed for the Au 3+ carrier and the 198 Au complexed species in samples and standards to oxidize, exchange, and reach chemical equilibrium. Samples were then equilibrated by shaking with the organic phase for thirty min. The percentage extractions (%E) for the substoichiometric separation of gold from the effluent and from the corresponding comparison standards were monitored. The mean percentage extractions for the substoichiometric separations of carrier from the effluent, and its corresponding standard were 75.3 and 59.3, respectively. These data are estimated to be accurate within +-2.0%. (T.G.)

  15. Determination of phosphorus distribution in the region of a SiO2-Si interface by substoichiometric analysis

    International Nuclear Information System (INIS)

    Shigematsu, T.; Yonezawa, H.

    1994-01-01

    A simplified method for the substoichiometric analysis of phosphorus has been developed and applied to determine the concentration distribution of phosphorus in the region of a SiO 2 -Si interface in order to explain why phosphorus is lost from the ion-implanted silicon surface throughout the oxidation and oxide removal processes. It is revealed that phosphorus piles up on the SiO 2 side at the interface by the thermal oxidation of silicon surface and is removed with the oxide by wet etching and with the resulting silicon by RCA cleaning. This results in a total loss of ion-implanted phosphorus of 3.5%. (author) 11 refs.; 2 figs.; 3 tabs

  16. Thermodynamic Studies at Higher Temperatures of the Phase Relationships of Substoichiometric Plutonium and Uranium/Plutonium Oxides

    DEFF Research Database (Denmark)

    Sørensen, Ole Toft

    1976-01-01

    Partial molar thermodynamic quantities for oxygen in non-stoichiometric Pu and U/Pu oxides were determined by thermogravimetric measurements in CO/CO2 mixtures in the temperature range 900-1450°C. A detailed analysis of the thermodynamic data obtained, as well as data previously published...

  17. Characterization of platinum catalysts supported on substoichiometric oxides of Zr, Ti and Ce by the electric impedance spectroscopy

    International Nuclear Information System (INIS)

    Eder, D.

    2003-09-01

    Noble metal catalysts show enhanced catalytic activities towards hydrocarbon C-O bond reactions, when they are supported on reducible oxides (titania or ceria) compared to silica or alumina. Active sites on the surface of such species are probably electronic or structural defects which lower the bonding strength of adsorbed molecules and favor subsequent reactions at the triple phase boundary between the metal, the oxide and the atmosphere. On the other hand, a pre-treatment of these catalysts in hydrogen at higher temperatures leads to a reversed effect. Noble metal catalysts supported on reducible oxides suffer from the so called SMSI-effect ('strong metal support interaction'), when they are reduced at temperatures above 400 o C. The adsorption capacity for hydrogen and for carbon monoxide and the catalytic activity for hydrocarbon skeletal reactions are decreased, the reason for this is mostly agreed to be the reduction of the support. Aim of this work was to characterize the electronic structure of two reducible oxides (TiO 2 and CeO 2 ) as a support for noble metal catalysts and compare them to the non-reducible ZrO 2 . The formation of oxygen vacancies during a typical catalytic pre-treatment in hydrogen was studied quantitatively by the volumetric oxygen titration and by temperature controlled oxidation/Desorption (TPO, TPD), as well as qualitatively by Electron Paramagnetic Resonance (EPR) and Fourier Transformation Infrared Spectroscopy (FTIR). The materials used in this work were of polycrystalline type, their specific surface area was controlled by calcinations at different temperatures. The reduction was performed in flowing dry hydrogen with varied flow rates at different temperatures. In some experiments, a water vapour pressure of 6.1 mbar was added to the gas stream to study the influence of humidity on the formation of oxygen vacancies. The treatment in hydrogen at low temperatures leads to the formation of oxygen vacancies located at the surface

  18. Simulation of atomistic processes during silicon oxidation

    OpenAIRE

    Bongiorno, Angelo

    2003-01-01

    Silicon dioxide (SiO2) films grown on silicon monocrystal (Si) substrates form the gate oxides in current Si-based microelectronics devices. The understanding at the atomic scale of both the silicon oxidation process and the properties of the Si(100)-SiO2 interface is of significant importance in state-of-the-art silicon microelectronics manufacturing. These two topics are intimately coupled and are both addressed in this theoretical investigation mainly through first-principles calculations....

  19. Method of forming buried oxide layers in silicon

    Science.gov (United States)

    Sadana, Devendra Kumar; Holland, Orin Wayne

    2000-01-01

    A process for forming Silicon-On-Insulator is described incorporating the steps of ion implantation of oxygen into a silicon substrate at elevated temperature, ion implanting oxygen at a temperature below 200.degree. C. at a lower dose to form an amorphous silicon layer, and annealing steps to form a mixture of defective single crystal silicon and polycrystalline silicon or polycrystalline silicon alone and then silicon oxide from the amorphous silicon layer to form a continuous silicon oxide layer below the surface of the silicon substrate to provide an isolated superficial layer of silicon. The invention overcomes the problem of buried isolated islands of silicon oxide forming a discontinuous buried oxide layer.

  20. Photoluminescence and electrical properties of silicon oxide and silicon nitride superlattices containing silicon nanocrystals

    International Nuclear Information System (INIS)

    Shuleiko, D V; Ilin, A S

    2016-01-01

    Photoluminescence and electrical properties of superlattices with thin (1 to 5 nm) alternating silicon-rich silicon oxide or silicon-rich silicon nitride, and silicon oxide or silicon nitride layers containing silicon nanocrystals prepared by plasma-enhanced chemical vapor deposition with subsequent annealing were investigated. The entirely silicon oxide based superlattices demonstrated photoluminescence peak shift due to quantum confinement effect. Electrical measurements showed the hysteresis effect in the vicinity of zero voltage due to structural features of the superlattices from SiOa 93 /Si 3 N 4 and SiN 0 . 8 /Si 3 N 4 layers. The entirely silicon nitride based samples demonstrated resistive switching effect, comprising an abrupt conductivity change at about 5 to 6 V with current-voltage characteristic hysteresis. The samples also demonstrated efficient photoluminescence with maximum at ∼1.4 eV, due to exiton recombination in silicon nanocrystals. (paper)

  1. Substoichiometric determination of uranium in phosphate rock

    Energy Technology Data Exchange (ETDEWEB)

    Suzuki, N; Hanzawa, K; Imura, H

    1986-01-01

    The substoichiometric isotope dilution analysis for U(VI) in a synergic extraction system of an excess amount of a chelating agent hexafluoroacetylacetone (HHFA) and a substoichiometric amount of U(VI) can be precisely extracted, and U down to ppm levels can be accurately determined by the present method. This method was applied to the analysis of a phosphate rock.

  2. Fluorescence and thermoluminescence in silicon oxide films rich in silicon

    International Nuclear Information System (INIS)

    Berman M, D.; Piters, T. M.; Aceves M, M.; Berriel V, L. R.; Luna L, J. A.

    2009-10-01

    In this work we determined the fluorescence and thermoluminescence (TL) creation spectra of silicon rich oxide films (SRO) with three different silicon excesses. To study the TL of SRO, 550 nm of SRO film were deposited by Low Pressure Chemical Vapor Deposition technique on N-type silicon substrates with resistivity in the order of 3 to 5 Ω-cm with silicon excess controlled by the ratio of the gases used in the process, SRO films with Ro= 10, 20 and 30 (12-6% silicon excess) were obtained. Then, they were thermally treated in N 2 at high temperatures to diffuse and homogenize the silicon excess. In the fluorescence spectra two main emission regions are observed, one around 400 nm and one around 800 nm. TL creation spectra were determined by plotting the integrated TL intensity as function of the excitation wavelength. (Author)

  3. Redox substoichiometric isotope dilution analysis of metallic arsenic for antimony

    International Nuclear Information System (INIS)

    Kambara, Tomihisa; Yoshioka, Hiroe; Suzuki, Junsuke; Shibata, Yasue.

    1979-01-01

    In 1 M HCl solution Sb(III) reacts with N-benzoyl-N-phenylhydroxylamine (BPHA) to form a complex extractable into chloroform while the extraction of Sb(V) is negligible. The redox substoichiometric isotope dilution analysis based on this reaction was applied to the determination of antimony in metallic arsenic. After the dissolution of metallic arsenic, Sb(V) was separated from As(V) by a tribenzylamine extraction from 8 M HCl solution and the extracted Sb(V) was stripped into 0.5 M NaOH solution. Thereafter, all the Sb(V) were completely reduced to Sb(III) by bubbling SO 2 gas through 3 M HCl solution. As the substoichiometric reaction, the oxidation of Sb(III) to Sb(V) by a substoichiometric amount of potassium dichromate was used, followed by separation of these species by the BPHA extraction of Sb(III). The substoichiometric oxidation of Sb(III) was found to be quantitative over HCl concentration range from 0.8 to 1.2 M. The amount of antimony was determined by isotope dilution analysis using the method of carrier amount variation. By the present method the determination of as small as 0.36 μg antimony was accomplished with a good accuracy (relative error; 5.6%) and also the method was successfully applied to the determination of antimony in arsenic samples containing known amounts of Sb(III) and in metallic arsenic. The present method gives reliable results with the good accuracy and precision. (author)

  4. Formation of porous silicon oxide from substrate-bound silicon rich silicon oxide layers by continuous-wave laser irradiation

    Science.gov (United States)

    Wang, Nan; Fricke-Begemann, Th.; Peretzki, P.; Ihlemann, J.; Seibt, M.

    2018-03-01

    Silicon nanocrystals embedded in silicon oxide that show room temperature photoluminescence (PL) have great potential in silicon light emission applications. Nanocrystalline silicon particle formation by laser irradiation has the unique advantage of spatially controlled heating, which is compatible with modern silicon micro-fabrication technology. In this paper, we employ continuous wave laser irradiation to decompose substrate-bound silicon-rich silicon oxide films into crystalline silicon particles and silicon dioxide. The resulting microstructure is studied using transmission electron microscopy techniques with considerable emphasis on the formation and properties of laser damaged regions which typically quench room temperature PL from the nanoparticles. It is shown that such regions consist of an amorphous matrix with a composition similar to silicon dioxide which contains some nanometric silicon particles in addition to pores. A mechanism referred to as "selective silicon ablation" is proposed which consistently explains the experimental observations. Implications for the damage-free laser decomposition of silicon-rich silicon oxides and also for controlled production of porous silicon dioxide films are discussed.

  5. Subsurface oxidation for micropatterning silicon (SOMS).

    Science.gov (United States)

    Zhang, Feng; Sautter, Ken; Davis, Robert C; Linford, Matthew R

    2009-02-03

    Here we present a straightforward patterning technique for silicon: subsurface oxidation for micropatterning silicon (SOMS). In this method, a stencil mask is placed above a silicon surface. Radio-frequency plasma oxidation of the substrate creates a pattern of thicker oxide in the exposed regions. Etching with HF or KOH produces very shallow or much higher aspect ratio features on silicon, respectively, where patterning is confirmed by atomic force microscopy, scanning electron microscopy, and optical microscopy. The oxidation process itself is studied under a variety of reaction conditions, including higher and lower oxygen pressures (2 and 0.5 Torr), a variety of powers (50-400 W), different times and as a function of reagent purity (99.5 or 99.994% oxygen). SOMS can be easily executed in any normal chemistry laboratory with a plasma generator. Because of its simplicity, it may have industrial viability.

  6. High-density oxidized porous silicon

    International Nuclear Information System (INIS)

    Gharbi, Ahmed; Souifi, Abdelkader; Remaki, Boudjemaa; Halimaoui, Aomar; Bensahel, Daniel

    2012-01-01

    We have studied oxidized porous silicon (OPS) properties using Fourier transform infraRed (FTIR) spectroscopy and capacitance–voltage C–V measurements. We report the first experimental determination of the optimum porosity allowing the elaboration of high-density OPS insulators. This is an important contribution to the research of thick integrated electrical insulators on porous silicon based on an optimized process ensuring dielectric quality (complete oxidation) and mechanical and chemical reliability (no residual pores or silicon crystallites). Through the measurement of the refractive indexes of the porous silicon (PS) layer before and after oxidation, one can determine the structural composition of the OPS material in silicon, air and silica. We have experimentally demonstrated that a porosity approaching 56% of the as-prepared PS layer is required to ensure a complete oxidation of PS without residual silicon crystallites and with minimum porosity. The effective dielectric constant values of OPS materials determined from capacitance–voltage C–V measurements are discussed and compared to FTIR results predictions. (paper)

  7. Broadband dielectric spectroscopy of oxidized porous silicon

    International Nuclear Information System (INIS)

    Axelrod, Ekaterina; Urbach, Benayahu; Sa'ar, Amir; Feldman, Yuri

    2006-01-01

    Dielectric measurements accompanied by infrared absorption and photoluminescence (PL) spectroscopy were used to investigate the electrical and optical properties of oxidized porous silicon (PS). As opposed to non-oxidized PS, only high temperature relaxation processes could be resolved for oxidized PS. Two relaxation processes have been observed. The first process is related to dc-conductivity that dominates at high temperatures and low frequencies. After subtraction of dc-conductivity we could analyse a second high-temperature relaxation process that is related to interface polarization induced by charge carriers trapped at the host matrix-pore interfaces. We found that, while the main effect of the oxidation on the PL appears to be a size reduction in the silicon nanocrystals that gives rise to a blue shift of the PL spectrum, its main contribution to the dielectric properties turns out to be blocking of transport channels in the host tissue and activation of hopping conductivity between silicon nanocrystals

  8. Broadband dielectric spectroscopy of oxidized porous silicon

    Energy Technology Data Exchange (ETDEWEB)

    Axelrod, Ekaterina [Department of Applied Physics, Hebrew University of Jerusalem, Jerusalem, 91904 (Israel); Urbach, Benayahu [Racah Institute of Physics and the Center for Nanoscience and Nanotechnology, Hebrew University of Jerusalem, Jerusalem, 91904 (Israel); Sa' ar, Amir [Racah Institute of Physics and the Center for Nanoscience and Nanotechnology, Hebrew University of Jerusalem, Jerusalem, 91904 (Israel); Feldman, Yuri [Department of Applied Physics, Hebrew University of Jerusalem, Jerusalem, 91904 (Israel)

    2006-04-07

    Dielectric measurements accompanied by infrared absorption and photoluminescence (PL) spectroscopy were used to investigate the electrical and optical properties of oxidized porous silicon (PS). As opposed to non-oxidized PS, only high temperature relaxation processes could be resolved for oxidized PS. Two relaxation processes have been observed. The first process is related to dc-conductivity that dominates at high temperatures and low frequencies. After subtraction of dc-conductivity we could analyse a second high-temperature relaxation process that is related to interface polarization induced by charge carriers trapped at the host matrix-pore interfaces. We found that, while the main effect of the oxidation on the PL appears to be a size reduction in the silicon nanocrystals that gives rise to a blue shift of the PL spectrum, its main contribution to the dielectric properties turns out to be blocking of transport channels in the host tissue and activation of hopping conductivity between silicon nanocrystals.

  9. Thermal Oxidation of Structured Silicon Dioxide

    DEFF Research Database (Denmark)

    Christiansen, Thomas Lehrmann; Hansen, Ole; Jensen, Jørgen Arendt

    2014-01-01

    The topography of thermally oxidized, structured silicon dioxide is investigated through simulations, atomic force microscopy, and a proposed analytical model. A 357 nm thick oxide is structured by removing regions of the oxide in a masked etch with either reactive ion etching or hydrofluoric acid....... Subsequent thermal oxidation is performed in both dry and wet ambients in the temperature range 950◦C to 1100◦C growing a 205 ± 12 nm thick oxide in the etched mask windows. Lifting of the original oxide near the edge of the mask in the range 6 nm to 37 nm is seen with increased lifting for increasing...

  10. Compositional analysis of silicon oxide/silicon nitride thin films

    Directory of Open Access Journals (Sweden)

    Meziani Samir

    2016-06-01

    Full Text Available Hydrogen, amorphous silicon nitride (SiNx:H abbreviated SiNx films were grown on multicrystalline silicon (mc-Si substrate by plasma enhanced chemical vapour deposition (PECVD in parallel configuration using NH3/SiH4 gas mixtures. The mc-Si wafers were taken from the same column of Si cast ingot. After the deposition process, the layers were oxidized (thermal oxidation in dry oxygen ambient environment at 950 °C to get oxide/nitride (ON structure. Secondary ion mass spectroscopy (SIMS, Rutherford backscattering spectroscopy (RBS, Auger electron spectroscopy (AES and energy dispersive X-ray analysis (EDX were employed for analyzing quantitatively the chemical composition and stoichiometry in the oxide-nitride stacked films. The effect of annealing temperature on the chemical composition of ON structure has been investigated. Some species, O, N, Si were redistributed in this structure during the thermal oxidation of SiNx. Indeed, oxygen diffused to the nitride layer into Si2O2N during dry oxidation.

  11. Thermal oxidation of silicon with two oxidizing species

    International Nuclear Information System (INIS)

    Vild-Maior, A.A.; Filimon, S.

    1979-01-01

    A theoretical model for the thermal oxidation of silicon in wet oxygen is presented. It is shown that the presence of oxygen in the oxidation furnace has an important effect when the water temperature is not too high (less than about 65 deg C). The model is in good agreement with the experimental data. (author)

  12. Silicon heterojunction solar cell with passivated hole selective MoOx contact

    Science.gov (United States)

    Battaglia, Corsin; de Nicolás, Silvia Martín; De Wolf, Stefaan; Yin, Xingtian; Zheng, Maxwell; Ballif, Christophe; Javey, Ali

    2014-03-01

    We explore substoichiometric molybdenum trioxide (MoOx, x MoOx, we observe a substantial gain in photocurrent of 1.9 mA/cm2 in the ultraviolet and visible part of the solar spectrum, when compared to a p-type amorphous silicon emitter of a traditional silicon heterojunction cell. Our results emphasize the strong potential for oxides as carrier selective heterojunction partners to inorganic semiconductors.

  13. Cerium neodymium oxide solid solution synthesis as a potential analogue for substoichiometric AmO{sub 2} for radioisotope power systems

    Energy Technology Data Exchange (ETDEWEB)

    Watkinson, E.J., E-mail: ejw36@le.ac.uk [Department of Physics and Astronomy, University of Leicester, University Road, Leicester, LE1 7RH (United Kingdom); Ambrosi, R.M. [Department of Physics and Astronomy, University of Leicester, University Road, Leicester, LE1 7RH (United Kingdom); Williams, H.R. [Department of Engineering, University of Leicester, University Road, Leicester, LE1 7RH (United Kingdom); Sarsfield, M.J. [National Nuclear Laboratory, Central Laboratory, Sellafield, Seascale, Cumbria, CA20 1PG (United Kingdom); Stephenson, K. [European Space Agency, ESTEC TEC-EP, Keplerlaan 1, Noordwijk, 2201AZ (Netherlands); Weston, D.P. [Department of Engineering, University of Leicester, University Road, Leicester, LE1 7RH (United Kingdom); Marsh, N.; Haidon, C. [Department of Geology, University of Leicester, University Road, Leicester, LE1 7RH (United Kingdom)

    2017-04-01

    The European Space Agency (ESA) is sponsoring a research programme on the development of americium oxides for radioisotope generators and heater units. Cubic AmO{sub 2-(x/2)} with an O/Am ratio between 1.65 and 1.75 is a potentially suitable compound for pellet sintering. C-type (Ia-3) Ce{sub 1-x}Nd{sub x}O{sub 2-(x/2)} oxides with 0.5 < x < 0.7 could be used as a surrogate for some Ia-3 AmO{sub 2-(x/2)}. A new Ce{sub 1-x}Nd{sub x}O{sub 2-(x/2)} production process has been investigated where a nominally selected x value of 0.6 was targeted: Ce and Nd nitrates and oxalic acid were added drop-wise into a vessel, where they continuously reacted to create oxalate precipitates. The effect of temperature (25 °C, 60 °C) of the reactants (mixed at 250 revolutions per minute) on oxalate particle shape and size were investigated. Oxalates were calcined at 900 °C to produce oxide particles. Oxalate particle properties were characterised as these are expected to influence oxides particle properties and fuel pellet sintering. - Highlights: •A European radioisotope power systems fuel option is AmO{sub 2-(x/2)} i.e. AmO{sub 1.65} to AmO{sub 1.75} that stays cubic with temperature. •Superstructure (Ia-3) Ce{sub 1-x}Nd{sub x}O{sub 2-(x/2)} is proposed as a surrogate for some Ia-3 AmO{sub 2-(x/2)} phases. •Continuously precipitated oxalates were calcined to oxides. An x of 0.6 was targeted by the nitrate feeds’ molar ratio. •Powder X-ray diffraction and Raman spectroscopy confirmed Ia-3 Ce{sub 1-x}Nd{sub x}O{sub 2-(x/2)}. Samples had Nd/[Ce+Nd] ratios or x of 0.62. •Oxalate particles precipitated at 60 °C had larger modal sizes than those at 25 °C. Lath/plate-like particles were made.

  14. Substoichiometric method in the simple radiometric analysis

    International Nuclear Information System (INIS)

    Ikeda, N.; Noguchi, K.

    1979-01-01

    The substoichiometric method is applied to simple radiometric analysis. Two methods - the standard reagent method and the standard sample method - are proposed. The validity of the principle of the methods is verified experimentally in the determination of silver by the precipitation method, or of zinc by the ion-exchange or solvent-extraction method. The proposed methods are simple and rapid compared with the conventional superstoichiometric method. (author)

  15. Photoconduction in silicon rich oxide films

    Energy Technology Data Exchange (ETDEWEB)

    Luna-Lopez, J A; Carrillo-Lopez, J; Flores-Gracia, F J; Garcia-Salgado, G [CIDS-ICUAP, Benemerita Universidad Autonoma de Puebla. Ed. 103 D and C, col. San Manuel, Puebla, Pue. Mexico 72570 (Mexico); Aceves-Mijares, M; Morales-Sanchez, A, E-mail: jluna@buap.siu.m, E-mail: jluna@inaoep.m [INAOE, Luis Enrique Erro No. 1, Apdo. 51, Tonantzintla, Puebla, Mexico 72000 (Mexico)

    2009-05-01

    Photoconduction of silicon rich oxide (SRO) thin films were studied by current-voltage (I-V) measurements, where ultraviolet (UV) and white (Vis) light illumination were applied. SRO thin films were deposited by low pressure chemical vapour deposition (LPCVD) technique, using SiH{sub 4} (silane) and N{sub 2}O (nitrous oxide) as reactive gases at 700 {sup 0}. The gas flow ratio, Ro = [N{sub 2}O]/[SiH{sub 4}] was used to control the silicon excess. The thickness and refractive index of the SRO films were 72.0 nm, 75.5 nm, 59.1 nm, 73.4 nm and 1.7, 1.5, 1.46, 1.45, corresponding to R{sub o} = 10, 20, 30 and 50, respectively. These results were obtained by null ellipsometry. Si nanoparticles (Si-nps) and defects within SRO films permit to obtain interesting photoelectric properties as a high photocurrent and photoconduction. These effects strongly depend on the silicon excess, thickness and structure type. Two different structures (Al/SRO/Si and Al/SRO/SRO/Si metal-oxide-semiconductor (MOS)-like structures) were fabricated and used as devices. The photocurrent in these structures is dominated by the generation of carriers due to the incident photon energies ({approx}3.0-1.6 eV and 5 eV). These structures showed large photoconductive response at room temperature. Therefore, these structures have potential applications in optoelectronics devices.

  16. Electrochemical impedance spectroscopy of oxidized porous silicon

    Energy Technology Data Exchange (ETDEWEB)

    Mula, Guido, E-mail: guido.mula@unica.it [Dipartimento di Fisica, Università degli Studi di Cagliari, Cittadella Universitaria di Monserrato, S.P. 8 km 0.700, 09042 Cagliari (Italy); Tiddia, Maria V. [Dipartimento di Fisica, Università degli Studi di Cagliari, Cittadella Universitaria di Monserrato, S.P. 8 km 0.700, 09042 Cagliari (Italy); Ruffilli, Roberta [Nanochemistry, Istituto Italiano di Tecnologia, Via Morego 30, 16163 Genova (Italy); Falqui, Andrea [Nanochemistry, Istituto Italiano di Tecnologia, Via Morego 30, 16163 Genova (Italy); Dipartimento di Scienze Chimiche e Geologiche, Università degli Studi di Cagliari, Cittadella Universitaria di Monserrato, S.P. 8 km 0.700, 09042 Cagliari (Italy); Palmas, Simonetta; Mascia, Michele [Dipartimento di Ingegneria Meccanica Chimica e dei Materiali, Università degli Studi di Cagliari, Piazza d' Armi, 09126 Cagliari (Italy)

    2014-04-01

    We present a study of the electrochemical oxidation process of porous silicon. We analyze the effect of the layer thickness (1.25–22 μm) and of the applied current density (1.1–11.1 mA/cm{sup 2}, values calculated with reference to the external samples surface) on the oxidation process by comparing the galvanostatic electrochemical impedance spectroscopy (EIS) measurements and the optical specular reflectivity of the samples. The results of EIS were interpreted using an equivalent circuit to separate the contribution of different sample parts. A different behavior of the electrochemical oxidation process has been found for thin and thick samples: whereas for thin samples the oxidation process is univocally related to current density and thickness, for thicker samples this is no more true. Measurements by Energy Dispersive Spectroscopy using a Scanning Electron Microscopy confirmed that the inhomogeneity of the electrochemical oxidation process is increased by higher thicknesses and higher currents. A possible explanation is proposed to justify the different behavior of thin and thick samples during the electrochemical process. - Highlights: • A multidisciplinary approach on porous Si electrochemical oxidation is proposed. • Electrochemical, optical, and structural characterizations are used. • Layer thickness and oxidation current effects are shown. • An explanation of the observed behavior is proposed.

  17. Oxide film assisted dopant diffusion in silicon carbide

    Energy Technology Data Exchange (ETDEWEB)

    Tin, Chin-Che, E-mail: cctin@physics.auburn.ed [Department of Physics, Auburn University, Alabama 36849 (United States); Mendis, Suwan [Department of Physics, Auburn University, Alabama 36849 (United States); Chew, Kerlit [Department of Electrical and Electronic Engineering, Faculty of Engineering and Science, Universiti Tunku Abdul Rahman, Kuala Lumpur (Malaysia); Atabaev, Ilkham; Saliev, Tojiddin; Bakhranov, Erkin [Physical Technical Institute, Uzbek Academy of Sciences, 700084 Tashkent (Uzbekistan); Atabaev, Bakhtiyar [Institute of Electronics, Uzbek Academy of Sciences, 700125 Tashkent (Uzbekistan); Adedeji, Victor [Department of Chemistry, Geology and Physics, Elizabeth City State University, North Carolina 27909 (United States); Rusli [School of Electrical and Electronic Engineering, Nanyang Technological University (Singapore)

    2010-10-01

    A process is described to enhance the diffusion rate of impurities in silicon carbide so that doping by thermal diffusion can be done at lower temperatures. This process involves depositing a thin film consisting of an oxide of the impurity followed by annealing in an oxidizing ambient. The process uses the lower formation energy of silicon dioxide relative to that of the impurity-oxide to create vacancies in silicon carbide and to promote dissociation of the impurity-oxide. The impurity atoms then diffuse from the thin film into the near-surface region of silicon carbide.

  18. Oxide film assisted dopant diffusion in silicon carbide

    International Nuclear Information System (INIS)

    Tin, Chin-Che; Mendis, Suwan; Chew, Kerlit; Atabaev, Ilkham; Saliev, Tojiddin; Bakhranov, Erkin; Atabaev, Bakhtiyar; Adedeji, Victor; Rusli

    2010-01-01

    A process is described to enhance the diffusion rate of impurities in silicon carbide so that doping by thermal diffusion can be done at lower temperatures. This process involves depositing a thin film consisting of an oxide of the impurity followed by annealing in an oxidizing ambient. The process uses the lower formation energy of silicon dioxide relative to that of the impurity-oxide to create vacancies in silicon carbide and to promote dissociation of the impurity-oxide. The impurity atoms then diffuse from the thin film into the near-surface region of silicon carbide.

  19. Segregation of boron implanted into silicon on angular configurations of silicon/silicon dioxide oxidation interface

    CERN Document Server

    Tarnavskij, G A; Obrekht, M S

    2001-01-01

    One studies segregation of boron implanted into silicon when a wave (interface) of oxidation moves within it. There are four types of angular configurations of SiO sub 2 /Si oxidation interface, that is: direct and reverse shoulders, trench type cavities and a square. By means of computer-aided simulation one obtained and analyzed complex patterns of B concentration distribution within Si, SiO sub 2 domains and at SiO sub 2 /Si interface for all types of angular configurations of the oxidation interface

  20. Nano-ridge fabrication by local oxidation of silicon edges with silicon nitride as a mask

    NARCIS (Netherlands)

    Haneveld, J.; Berenschot, Johan W.; Maury, P.A.; Jansen, Henricus V.

    2005-01-01

    A method to fabricate nano-ridges over a full wafer is presented. The fabrication method uses local oxidation of silicon, with silicon nitride as a mask, and wet anisotropic etching of silicon. The realized structures are 7-20 nm wide, 40-100 nm high and centimeters long. All dimensions are easily

  1. Hydrothermal deposition and characterization of silicon oxide nanospheres

    International Nuclear Information System (INIS)

    Pei, L.Z.

    2008-01-01

    Silicon oxide nanospheres with the average diameter of about 100 nm have been synthesized by hydrothermal deposition process using silicon and silica as the starting materials. The silicon oxide nanospheres were characterized by field emission scanning electron microscopy (FESEM), energy dispersive X-ray spectrum (EDS), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM) and photoluminescence (PL) spectrum, respectively. The results show that large scale silicon oxide nanospheres with the uniform size are composed of Si and O showing the amorphous structure. Strong PL peak at 435 nm is observed demonstrating the good blue light emission property

  2. Redox substoichiometric determination of arsenic in biological materials by neutron activation analysis

    International Nuclear Information System (INIS)

    Kanda, Y.; Suzuki, N.

    1979-01-01

    Redox substoichiometry is proposed for an accurate and precise determination of arsenic. This method is based on the substoichiometric oxidation of trivalent arsenic to pentavalent with potassium bromate or ceric sulfate followed by the separation of these species by thionalide extraction of trivalent arsenic. It was applied to neutron activation analysis of arsenic in the NBS SRM Orchard Leaves and the Shark Powder. The results were obtained with and excellent accuracy and precision. (author)

  3. The oxidized porous silicon field emission array

    International Nuclear Information System (INIS)

    Smith, D.D.; Demroff, H.P.; Elliott, T.S.; Kasprowicz, T.B.; Lee, B.; Mazumdar, T.K.; McIntyre, P.M.; Pang, Y.; Trost, H.J.

    1993-01-01

    The goal of developing a highly efficient microwave power source has led the authors to investigate new methods of electron field emission. One method presently under consideration involves the use of oxidized porous silicon thin films. The authors have used this technology to fabricate the first working field emission arrays from this substance. This approach reduces the diameter of an individual emitter to the nanometer scale. Tests of the first samples are encouraging, with extracted electron currents to nearly 1 mA resulting from less than 20 V of pulsed DC gate voltage. Modulated emission at 5 MHz was also observed. Developments of a full-scale emission array capable of delivering an electron beam at 18 GHz of minimum density 100 A/cm 2 is in progress

  4. Passivating electron contact based on highly crystalline nanostructured silicon oxide layers for silicon solar cells

    Czech Academy of Sciences Publication Activity Database

    Stuckelberger, J.; Nogay, G.; Wyss, P.; Jeangros, Q.; Allebe, Ch.; Debrot, F.; Niquille, X.; Ledinský, Martin; Fejfar, Antonín; Despeisse, M.; Haug, F.J.; Löper, P.; Ballif, C.

    2016-01-01

    Roč. 158, Dec (2016), s. 2-10 ISSN 0927-0248 R&D Projects: GA MŠk LM2015087 Institutional support: RVO:68378271 Keywords : surface passivation * passivating contact * nanostructure * silicon oxide * nanocrystalline * microcrystalline * poly-silicon * crystallization * Raman * transmission line measurement Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 4.784, year: 2016

  5. Silicon oxide nanoimprint stamp fabrication by edge lithography reinforced with silicon nitride

    NARCIS (Netherlands)

    Zhao, Yiping; Berenschot, Johan W.; de Boer, Meint J.; Jansen, Henricus V.; Tas, Niels Roelof; Huskens, Jurriaan; Elwenspoek, Michael Curt

    2007-01-01

    The fabrication of silicon oxide nanoimprint stamp employing edge lithography in combination with silicon nitride deposition is presented. The fabrication process is based on conventional photolithography an weg etching methods. Nanoridges with width dimension of sub-20 nm were fabricated by edge

  6. Development of Doped Microcrystalline Silicon Oxide and its Application to Thin‑Film Silicon Solar Cells

    NARCIS (Netherlands)

    Lambertz, A.

    2015-01-01

    The aim of the present study is the development of doped microcrystalline silicon oxide (µc‑SiOx:H) alloys and its application in thin‑film silicon solar cells. The doped µc‑SiOx:H material was prepared from carbon dioxide (CO2), silane (SiH4), hydrogen (H2) gas mixtures using plasma enhanced

  7. Indium oxide/n-silicon heterojunction solar cells

    Science.gov (United States)

    Feng, Tom; Ghosh, Amal K.

    1982-12-28

    A high photo-conversion efficiency indium oxide/n-silicon heterojunction solar cell is spray deposited from a solution containing indium trichloride. The solar cell exhibits an Air Mass One solar conversion efficiency in excess of about 10%.

  8. Density of oxidation-induced stacking faults in damaged silicon

    NARCIS (Netherlands)

    Kuper, F.G.; Hosson, J.Th.M. De; Verwey, J.F.

    1986-01-01

    A model for the relation between density and length of oxidation-induced stacking faults on damaged silicon surfaces is proposed, based on interactions of stacking faults with dislocations and neighboring stacking faults. The model agrees with experiments.

  9. The influence of initial defects on mechanical stress and deformation distribution in oxidized silicon

    Directory of Open Access Journals (Sweden)

    Kulinich O. A.

    2008-10-01

    Full Text Available The near-surface silicon layers in silicon – dioxide silicon systems with modern methods of research are investigated. It is shown that these layers have compound structure and their parameters depend on oxidation and initial silicon parameters. It is shown the influence of initial defects on mechanical stress and deformation distribution in oxidized silicon.

  10. Oxidation of ultra low carbon and silicon bearing steels

    Energy Technology Data Exchange (ETDEWEB)

    Suarez, Lucia [CTM - Technologic Centre, Materials Technology Area, Manresa, Barcelona (Spain)], E-mail: lucia.suarez@ctm.com.es; Rodriguez-Calvillo, Pablo [CTM - Technologic Centre, Materials Technology Area, Manresa, Barcelona (Spain)], E-mail: pablo.rodriguez@ctm.com.es; Houbaert, Yvan [Department of Materials Science and Engineering, University of Ghent (Belgium)], E-mail: Yvan.Houbaert@UGent.be; Colas, Rafael [Facultad de Ingenieria Mecanica y Electrica, Universidad Autonoma de Nuevo Leon (Mexico)], E-mail: rcolas@mail.uanl.mx

    2010-06-15

    Oxidation tests were carried out in samples from an ultra low carbon and two silicon bearing steels to determine the distribution and morphology of the oxide species present. The ultra low carbon steel was oxidized for short periods of time within a chamber designed to obtain thin oxide layers by controlling the atmosphere, and for longer times in an electric furnace; the silicon steels were reheated only in the electric furnace. The chamber was constructed to study the behaviour encountered during the short period of time between descaling and rolling in modern continuous mills. It was found that the oxide layers formed on the samples reheated in the electric furnace were made of different oxide species. The specimens treated in the chamber had layers made almost exclusively of wustite. Selected oxide samples were studied by scanning electron microscopy to obtain electron backscattered diffraction patterns, which were used to identify the oxide species in the layer.

  11. Oxide layers for silicon detector protection against enviroment effects

    International Nuclear Information System (INIS)

    Bel'tsazh, E.; Brylovska, I.; Valerian, M.

    1986-01-01

    It is shown that for protection of silicon detectors of nuclear radiations oxide layers could be used. The layers are produced by electrochemical oxidation of silicon surface with the following low-temperature annealing. These layers have characteristics similar to those for oxide layers produced by treatment of silicon samples at elevated temperature in oxygen flow. To determine properties of oxide layers produced by electrochemical oxidation the α-particle back-scattering method and the method of volt-farad characteristics were used. Protection properties of such layers were checked on the surface-barrier detectors. It was shown that protection properties of such detectors were conserved during long storage at room temperature and during their storage under wet-bulb temperature. Detectors without protection layer have worsened their characteristics

  12. Catalytic oxidation of silicon by cesium ion bombardment

    International Nuclear Information System (INIS)

    Souzis, A.E.; Huang, H.; Carr, W.E.; Seidl, M.

    1991-01-01

    Results for room-temperature oxidation of silicon using cesium ion bombardment and low oxygen exposure are presented. Bombardment with cesium ions is shown to allow oxidation at O 2 pressures orders of magnitude smaller than with noble gas ion bombardment. Oxide layers of up to 30 A in thickness are grown with beam energies ranging from 20--2000 eV, O 2 pressures from 10 -9 to 10 -6 Torr, and total O 2 exposures of 10 0 to 10 4 L. Results are shown to be consistent with models indicating that initial oxidation of silicon is via dissociative chemisorption of O 2 , and that the low work function of the cesium- and oxygen-coated silicon plays the primary role in promoting the oxidation process

  13. Mechanical grooving of oxidized porous silicon to reduce the reflectivity of monocrystalline silicon solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Zarroug, A.; Dimassi, W.; Ouertani, R.; Ezzaouia, H. [Laboratoire de Photovoltaique, Centre des Recherches et des Technologies de l' Energie, BP. 95, Hammam-Lif 2050 (Tunisia)

    2012-10-15

    In this work, we are interested to use oxidized porous silicon (ox-PS) as a mask. So, we display the creating of a rough surface which enhances the absorption of incident light by solar cells and reduces the reflectivity of monocrystalline silicon (c-Si). It clearly can be seen that the mechanical grooving enables us to elaborate the texturing of monocrystalline silicon wafer. Results demonstrated that the application of a PS layer followed by a thermal treatment under O2 ambient easily gives us an oxide layer of uniform size which can vary from a nanometer to about ten microns. In addition, the Fourier transform infrared (FTIR) spectroscopy investigations of the PS layer illustrates the possibility to realize oxide layer as a mask for porous silicon. We found also that this simple and low cost method decreases the total reflectivity (copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  14. A review of oxide, silicon nitride, and silicon carbide brazing

    International Nuclear Information System (INIS)

    Santella, M.L.; Moorhead, A.J.

    1987-01-01

    There is growing interest in using ceramics for structural applications, many of which require the fabrication of components with complicated shapes. Normal ceramic processing methods restrict the shapes into which these materials can be produced, but ceramic joining technology can be used to overcome many of these limitations, and also offers the possibility for improving the reliability of ceramic components. One method of joining ceramics is by brazing. The metallic alloys used for bonding must wet and adhere to the ceramic surfaces without excessive reaction. Alumina, partially stabilized zirconia, and silicon nitride have high ionic character to their chemical bonds and are difficult to wet. Alloys for brazing these materials must be formulated to overcome this problem. Silicon carbide, which has some metallic characteristics, reacts excessively with many alloys, and forms joints of low mechanical strength. The brazing characteristics of these three types of ceramics, and residual stresses in ceramic-to-metal joints are briefly discussed

  15. Integration of functional complex oxide nanomaterials on silicon

    Directory of Open Access Journals (Sweden)

    Jose Manuel eVila-Fungueiriño

    2015-06-01

    Full Text Available The combination of standard wafer-scale semiconductor processing with the properties of functional oxides opens up to innovative and more efficient devices with high value applications that can be produced at large scale. This review uncovers the main strategies that are successfully used to monolithically integrate functional complex oxide thin films and nanostructures on silicon: the chemical solution deposition approach (CSD and the advanced physical vapor deposition techniques such as oxide molecular beam epitaxy (MBE. Special emphasis will be placed on complex oxide nanostructures epitaxially grown on silicon using the combination of CSD and MBE. Several examples will be exposed, with a particular stress on the control of interfaces and crystallization mechanisms on epitaxial perovskite oxide thin films, nanostructured quartz thin films, and octahedral molecular sieve nanowires. This review enlightens on the potential of complex oxide nanostructures and the combination of both chemical and physical elaboration techniques for novel oxide-based integrated devices.

  16. Use of porous silicon to minimize oxidation induced stacking fault defects in silicon

    International Nuclear Information System (INIS)

    Shieh, S.Y.; Evans, J.W.

    1992-01-01

    This paper presents methods for minimizing stacking fault defects, generated during oxidation of silicon, include damaging the back of the wafer or depositing poly-silicon on the back. In either case a highly defective structure is created and this is capable of gettering either self-interstitials or impurities which promote nucleation of stacking fault defects. A novel method of minimizing these defects is to form a patch of porous silicon on the back of the wafer by electrochemical etching. Annealing under inert gas prior to oxidation may then result in the necessary gettering. Experiments were carried out in which wafers were subjected to this treatment. Subsequent to oxidation, the wafers were etched to remove oxide and reveal defects. The regions of the wafer adjacent to the porous silicon patch were defect-free, whereas remote regions had defects. Deep level transient spectroscopy has been used to examine the gettering capability of porous silicon, and the paper discusses the mechanism by which the porous silicon getters

  17. Waveguiding properties of Er-implanted silicon-rich oxides

    International Nuclear Information System (INIS)

    Elliman, R.G.; Forcales, M.; Wilkinson, A.R.; Smith, N.J.

    2007-01-01

    The optical properties of erbium-doped silicon-rich silicon-oxide waveguides containing amorphous silicon nanoclusters and/or silicon nanocrystals are reported. Both amorphous nanoclusters and nanocrystals are shown to act as effective sensitizers for Er, with nanocrystals being more effective at low pump powers and nanoclusters being more effective at higher pump powers. All samples are shown to exhibit photo-induced absorption, as measured for a guided 1.5 μm probe beam while the waveguide was illuminated from above with a 477 nm pump beam. At a given pump power samples containing silicon nanocrystals exhibited greater attenuation than samples containing amorphous nanoclusters. The absorption is shown to be consistent with confined-carrier absorption due to photoexcited carriers in the nanocrystals and/or nanoclusters

  18. Carbon nanotube network-silicon oxide non-volatile switches.

    Science.gov (United States)

    Liao, Albert D; Araujo, Paulo T; Xu, Runjie; Dresselhaus, Mildred S

    2014-12-08

    The integration of carbon nanotubes with silicon is important for their incorporation into next-generation nano-electronics. Here we demonstrate a non-volatile switch that utilizes carbon nanotube networks to electrically contact a conductive nanocrystal silicon filament in silicon dioxide. We form this device by biasing a nanotube network until it physically breaks in vacuum, creating the conductive silicon filament connected across a small nano-gap. From Raman spectroscopy, we observe coalescence of nanotubes during breakdown, which stabilizes the system to form very small gaps in the network~15 nm. We report that carbon nanotubes themselves are involved in switching the device to a high resistive state. Calculations reveal that this switching event occurs at ~600 °C, the temperature associated with the oxidation of nanotubes. Therefore, we propose that, in switching to a resistive state, the nanotube oxidizes by extracting oxygen from the substrate.

  19. Oxidation under electron bombardment. A tool for studying the initial states of silicon oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Carriere, B.; Deville, J.P.; El Maachi, A.

    1987-06-01

    The exciting beam of an Auger electron spectrometer has been used to monitor the oxidation of silicon single crystals at room temperature and very low pressures of oxygen (approx. 10/sup -7/ Torr). This process allows us to build ultra-thin layers of silica on silicon (down to 30 A) but it is mostly used to investigate the mechanisms of the initial stages of oxidation. Auger spectra recorded continuously during the oxidation process provide information on (1) the nature of the silicon-oxygen chemical bonds which are interpreted through fine structure in the Auger peak, and (2) the kinetics of oxide formation which are deduced from curves of Auger signal versus time. An account is given of the contribution of these Auger studies to the description of the intermediate oxide layer during the reaction between silicon and oxygen and the influence of surface structural disorder, induced mainly by argon-ion bombardment, is discussed in terms of reactivity and oxide coverage.

  20. Oxidation of mullite-zirconia-alumina-silicon carbide composites

    International Nuclear Information System (INIS)

    Baudin, C.; Moya, J.S.

    1990-01-01

    This paper reports the isothermal oxidation of mullite-alumina-zirconia-silicon carbide composites obtained by reaction sintering studied in the temperature interval 800 degrees to 1400 degrees C. The kinetics of the oxidation process was related to the viscosity of the surface glassy layer as well as to the crystallization of the surface film. The oxidation kinetics was halted to T ≤ 1300 degrees C, presumably because of crystallization

  1. Oxidation kinetics of CVD silicon carbide and silicon nitride

    Science.gov (United States)

    Fox, Dennis S.

    1992-01-01

    The long-term oxidation behavior of pure, monolithic CVD SiC and Si3N4 is studied, and the isothermal oxidation kinetics of these two materials are obtained for the case of 100 hrs at 1200-1500 C in flowing oxygen. Estimates are made of lifetimes at the various temperatures investigated. Parabolic rate constants for SiC are within an order of magnitude of shorter exposure time values reported in the literature. The resulting silica scales are in the form of cristobalite, with cracks visible after exposure. The oxidation protection afforded by silica for these materials is adequate for long service times under isothermal conditions in 1-atm dry oxygen.

  2. Study of Silicon/silicon, Silicon/silicon Dioxide, and Metal-Oxide

    Science.gov (United States)

    Leung, To Chi

    A variable-energy positron beam is used to study Si/Si, Si/SiO_2, and metal-oxide -semiconductor (MOS) structures. The capability of depth resolution and the remarkable sensitivity to defects have made the positron annihilation technique a unique tool in detecting open-volume defects in the newly innovated low temperature (300^circC) molecular-beam-epitaxy (MBE) Si/Si. These two features of the positron beam have further shown its potential role in the study of the Si/SiO_2. Distinct annihilation characteristics has been observed at the interface and has been studied as a function of the sample growth conditions, annealing (in vacuum), and hydrogen exposure. The MOS structure provides an effective way to study the electrical properties of the Si/SiO_2 interface as a function of applied bias voltage. The annihilation characteristics show a large change as the device condition is changed from accumulation to inversion. The effect of forming gas (FG) anneal is studied using positron annihilation and the result is compared with capacitance-voltage (C -V) measurements. The reduction in the number of interface states is found correlated with the changes in the positron spectra. The present study shows the importance of the positron annihilation technique as a non-contact, non-destructive, and depth-sensitive characterization tool to study the Si-related systems, in particular, the Si/SiO_2 interface which is of crucial importance in semiconductor technology, and fundamental understanding of the defects responsible for degradation of the electrical properties.

  3. Structural and photoluminescent properties of a composite tantalum oxide and silicon nanocrystals embedded in a silicon oxide film

    International Nuclear Information System (INIS)

    Díaz-Becerril, T.; Herrera, V.; Morales, C.; García-Salgado, G.; Rosendo, E.; Coyopol, A.; Galeazzi, R.; Romano, R.; Nieto-Caballero, F.G.; Sarmiento, J.

    2017-01-01

    Tantalum oxide crystals encrusted in a silicon oxide matrix were synthesized by using a hot filament chemical vapor deposition system (HFCVD). A solid source composed by a mixture in different percentages of Ta 2 O 5 and silicon (Si) powders were used as reactants. The films were grown at 800 °C and 1000 °C under hydrogen ambient. The deposited films were characterized by X-ray photoelectron spectroscopy (XPS), high-resolution transmission electron microscopy (HRTEM) and photoluminescence (PL) at room temperature. From the XPS results it was confirmed the formation of a mixture of Tantalum oxide, silicon oxide and Si nanoparticles (Ta 2 O 5- SiO 2 -Si(nc)) as seen from the Si (2p) and Ta (4f) lines corresponding to Si + and Ta + states respectively. Ta 2 O 5 and Si nanocrystals (Si-NCs) embedded in the silicon oxide films were observed on HRTEM images which corroborate the XPS results. Finally the emission properties of the films exhibited a broad band from 400 to 850 nm caused by the independent PL properties of tantalum oxide and Si-NCs that compose the film. The intensity of the emissions was observed to be dependent on both temperature of deposition and the ratio Ta 2 O 5 /Si, used as initial reactants. Results from this work might supply useful data for the development of future light emitter devices.

  4. The silicon-silicon oxide multilayers utilization as intrinsic layer on pin solar cells

    International Nuclear Information System (INIS)

    Colder, H.; Marie, P.; Gourbilleau, F.

    2008-01-01

    Silicon nanostructures are promising candidate for the intrinsic layer on pin solar cells. In this work we report on new material: silicon-rich silicon oxide (SRSO) deposited by reactive magnetron sputtering of a pure silica target and an interesting structure: multilayers consisting of a stack of SRSO and pure silicon oxide layers. Two thicknesses of the SRSO sublayer, t SRSO , are studied 3 nm and 5 nm whereas the thickness of silica sublayer is maintaining at 3 nm. The presence of nanocrystallites of silicon, evidenced by X-Ray diffraction (XRD), leads to photoluminescence (PL) emission at room temperature due to the quantum confinement of the carriers. The PL peak shifts from 1.3 eV to 1.5 eV is correlated to the decreasing of t SRSO from 5 nm down to 3 nm. In the purpose of their potential utilization for i-layer, the optical properties are studied by absorption spectroscopy. The achievement a such structures at promising absorption properties. Moreover by favouring the carriers injection by the tunnel effect between silicon nanograins and silica sublayers, the multilayers seem to be interesting for solar cells

  5. Determination of zinc by substoichiometric extraction with malonic anilide

    International Nuclear Information System (INIS)

    Dutta, J.; Basu, S.

    1994-01-01

    A substoichiometric radiochemical extraction method has been developed for the determination of zinc employing a new chelating agent e.g. malonic anilide, dissolved in a mixed organic solvent, MIBK and ether (3:1). The reagent was synthesized and characterized in our laboratory. The method developed was utilized to determine the zinc content in few common vegetable samples. (orig.)

  6. Y-Ba-Cu-O superconducting film on oxidized silicon

    International Nuclear Information System (INIS)

    Gupta, R.P.; Khokle, W.S.; Dubey, R.C.; Singhal, S.; Nagpal, K.C.; Rao, G.S.T.; Jain, J.D.

    1988-01-01

    We report thick superconducting films of Y-Ba-Cu-O on oxidized silicon substrates. The critical temperatures for onset and zero resistance are 96 and 77 K, respectively. X-ray diffraction analysis predicts 1, 2, 3 composition and orthorhombic phase of the film

  7. Transparent conductive oxides for thin-film silicon solar cells

    NARCIS (Netherlands)

    Löffler, J.

    2005-01-01

    This thesis describes research on thin-film silicon solar cells with focus on the transparent conductive oxide (TCO) for such devices. In addition to the formation of a transparent and electrically conductive front electrode for the solar cell allowing photocurrent collection with low ohmic losses,

  8. RF Reactive Magnetron Sputter Deposition of Silicon Sub-Oxides

    NARCIS (Netherlands)

    Hattum, E.D. van

    2007-01-01

    RF reactive magnetron plasma sputter deposition of silicon sub oxide E.D. van Hattum Department of Physics and Astronomy, Faculty of Sciences, Utrecht University The work described in the thesis has been inspired and stimulated by the use of SiOx layers in the direct inductive printing technology,

  9. Study of oxide facing at silicone detectors of ionization detectors

    International Nuclear Information System (INIS)

    Kopestansky, J.; Tykva, R.

    1999-01-01

    Formation of oxide facing on silicone in discrete phases of technological preparation of detectors and interaction of gold (aluminium) steamed with SiO x layer were studied. The homogeneity of Au and Si) x layers and interface Au-SiO x and SiO x -Si were examined. The methods SIMS, and partially XPS, AES and RBS were used

  10. Fluorescence studies of Rhodamine 6G functionalized silicon oxide nanostructures

    International Nuclear Information System (INIS)

    Baumgaertel, Thomas; Borczyskowski, Christian von; Graaf, Harald

    2010-01-01

    Selective anchoring of optically active molecules on nanostructured surfaces is a promising step towards the creation of nanoscale devices with new functionalities. Recently we have demonstrated the electrostatic attachment of charged fluorescent molecules on silicon oxide nanostructures prepared by atomic force microscopy (AFM) nanolithography via local anodic oxidation (LAO) of dodecyl-terminated silicon. In this paper we report on our findings from a more detailed optical investigation of the bound dye Rhodamine 6G. High sensitivity optical wide field microscopy as well as confocal laser microscopy have been used to characterize the Rhodamine fluorescence emission. A highly interesting question concerns the interaction between an emitter close to a silicon surface because mechanisms such as energy transfer and fluorescence quenching will occur which are still not fully understood. Since the oxide thickness can be varied during preparation continuously from 1 to ∼ 5 nm, it is possible to investigate the fluorescence of the bound dye in close proximity to the underlying silicon. Using confocal laser microscopy we were also able to obtain optical spectra from the bound molecules. Together with the results from an analysis of their photochemical bleaching behaviour, we conjecture that some of the Rhodamine 6G molecules on the structure are interacting with the oxide, causing a spectral shift and differences in their photochemical properties.

  11. Effect of backbond oxidation on silicon nanocrystallites

    International Nuclear Information System (INIS)

    Ramos, L.E.; Furthmueller, J.; Bechstedt, F.

    2004-01-01

    We employ density functional calculations to study properties of Si nanocrystals after backbond oxidation in comparison to the ones passivated with hydrogen or hydroxyl. Structural parameters, pair excitation energies, quasiparticle gaps, and electrostatic potentials vary significantly in dependence on degree of oxidation and surface passivation. The variations are discussed within a quantum confinement picture. Blueshifts and redshifts observed in photoluminescence are related to the size of the Si nanocrystallite cores and the oxygen incorporation via passivation with group OH or oxidation

  12. Sub-stoichiometric isotope dilution analysis method for the determination of iodine in common salts using iodine-131 tracer

    International Nuclear Information System (INIS)

    Singh, Vivek; Garg, A.N.

    1994-01-01

    A sub-stoichiometric isotope dilution analysis (SIDA) method was developed for the determination of iodine in different brands of common salts. An aqueous salt solution containing 131 I tracer and NaI as carrier is oxidized by tartaric acid and KIO 3 and the liberated iodine is extracted with CCl 4 . To the extract an aqueous solution of AgNO 3 is added in substoichiometric amount to obtain a colloidal solution of AgI. On adding sodium thiosulfate solution, the NaI so formed passes into aqueous solution, which is then counted. Several different brands of salt were analysed. The method is especially suitable for the determination of microgram amounts of iodide in the presence of excess of chloride. (Author)

  13. Development of an oxidized porous silicon vacuum microtriode

    Energy Technology Data Exchange (ETDEWEB)

    Smith, II, Don Deewayne [Texas A & M Univ., College Station, TX (United States)

    1994-05-01

    In order to realize a high-power microwave amplifier design known as a gigatron, a gated field emission array must be developed that can deliver a high-intensity electron beam at gigahertz frequencies. No existing field emission device meets the requirements for a gigatron cathode. In the present work, a porous silicon-based approach is evaluated. The use of porous silicon reduces the size of a single emitter to the nanometer scale, and a true two-dimensional array geometry can be approached. A wide number of applications for such a device exist in various disciplines. Oxidized porous silicon vacuum diodes were first developed in 1990. No systematic study had been done to characterize the performance of these devices as a function of the process parameters. The author has done the first such study, fabricating diodes from p<100>, p<111>, and n<100> silicon substrates. Anodization current densities from 11 mA/cm2 to 151 mA/cm2 were used, and Fowler-Nordheim behavior was observed in over 80% of the samples. In order to effectively adapt this technology to mainstream vacuum microelectronic applications, a means of creating a gated triodic structure must be found. No previous attempts had successfully yielded such a device. The author has succeeded in utilizing a novel metallization method to fabricate the first operational oxidized porous silicon vacuum microtriodes, and results are encouraging.

  14. Oxidation Protection of Porous Reaction-Bonded Silicon Nitride

    Science.gov (United States)

    Fox, D. S.

    1994-01-01

    Oxidation kinetics of both as-fabricated and coated reaction-bonded silicon nitride (RBSN) were studied at 900 and 1000 C with thermogravimetry. Uncoated RBSN exhibited internal oxidation and parabolic kinetics. An amorphous Si-C-O coating provided the greatest degree of protection to oxygen, with a small linear weight loss observed. Linear weight gains were measured on samples with an amorphous Si-N-C coating. Chemically vapor deposited (CVD) Si3N4 coated RBSN exhibited parabolic kinetics, and the coating cracked severely. A continuous-SiC-fiber-reinforced RBSN composite was also coated with the Si-C-O material, but no substantial oxidation protection was observed.

  15. Demonstration of slot-waveguide structures on silicon nitride / silicon oxide platform.

    Science.gov (United States)

    Barrios, C A; Sánchez, B; Gylfason, K B; Griol, A; Sohlström, H; Holgado, M; Casquel, R

    2007-05-28

    We report on the first demonstration of guiding light in vertical slot-waveguides on silicon nitride/silicon oxide material system. Integrated ring resonators and Fabry-Perot cavities have been fabricated and characterized in order to determine optical features of the slot-waveguides. Group index behavior evidences guiding and confinement in the low-index slot region at O-band (1260-1370nm) telecommunication wavelengths. Propagation losses of <20 dB/cm have been measured for the transverse-electric mode of the slot-waveguides.

  16. Field oxide radiation damage measurements in silicon strip detectors

    Energy Technology Data Exchange (ETDEWEB)

    Laakso, M [Particle Detector Group, Fermilab, Batavia, IL (United States) Research Inst. for High Energy Physics (SEFT), Helsinki (Finland); Singh, P; Shepard, P F [Dept. of Physics and Astronomy, Univ. Pittsburgh, PA (United States)

    1993-04-01

    Surface radiation damage in planar processed silicon detectors is caused by radiation generated holes being trapped in the silicon dioxide layers on the detector wafer. We have studied charge trapping in thick (field) oxide layers on detector wafers by irradiating FOXFET biased strip detectors and MOS test capacitors. Special emphasis was put on studying how a negative bias voltage across the oxide during irradiation affects hole trapping. In addition to FOXFET biased detectors, negatively biased field oxide layers may exist on the n-side of double-sided strip detectors with field plate based n-strip separation. The results indicate that charge trapping occurred both close to the Si-SiO[sub 2] interface and in the bulk of the oxide. The charge trapped in the bulk was found to modify the electric field in the oxide in a way that leads to saturation in the amount of charge trapped in the bulk when the flatband/threshold voltage shift equals the voltage applied over the oxide during irradiation. After irradiation only charge trapped close to the interface is annealed by electrons tunneling to the oxide from the n-type bulk. (orig.).

  17. Oxidation and corrosion of silicon-based ceramics and composites

    International Nuclear Information System (INIS)

    Jacobson, N.S.; Fox, D.S.; Smialek, J.L.

    1997-01-01

    Silica scales exhibit slow growth rates and a low activation energy. Thus silica-protected materials are attractive high temperature structural materials for their potentially excellent oxidation resistance and well-documented high temperature strength. This review focuses on silicon carbide, silicon nitride, and composites of these materials. It is divided into four parts: (i) Fundamental oxidation mechanisms, (ii) Special properties of silica scales, (iii) Protective coatings, and (iv) Internal oxidation behavior of composites. While the fundamental oxidation mechanism of SiC is understood, there are still many questions regarding the oxidation mechanism of Si 3 N 4 . Silica scales exhibit many unique properties as compared to chromia and alumina. These include slower growth rates, SiO(g) formation, sensitivity to water vapor and impurities, and dissolution by basic molten salts. Protective coatings can limit the deleterious effects. The fourth area-internal oxidation of fibers and fiber coatings in composites-has limited the application of these novel materials. Strategies for understanding and limiting this internal oxidation are discussed. (orig.)

  18. Influence of sample oxidation on the nature of optical luminescence from porous silicon

    International Nuclear Information System (INIS)

    Coulthard, I.; Antel, W. J. Jr.; Freeland, J. W.; Sham, T. K.; Naftel, S. J.; Zhang, P.

    2000-01-01

    Site-selective luminescence experiments were performed upon porous-silicon samples exposed to varying degrees of oxidation. The source of different luminescence bands was determined to be due to either quantum confinement in nanocrystalline silicon or defective silicon oxide. Of particular interest is the defective silicon-oxide luminescence band found at 2.1 eV, which was found to frequently overlap with a luminescence band from nanocrystalline silicon. Some of the historical confusion and debate with regards to the source of luminescence from porous silicon can be attributed to this overlap. (c) 2000 American Institute of Physics

  19. Ultrathin Oxide Passivation Layer by Rapid Thermal Oxidation for the Silicon Heterojunction Solar Cell Applications

    Directory of Open Access Journals (Sweden)

    Youngseok Lee

    2012-01-01

    Full Text Available It is difficult to deposit extremely thin a-Si:H layer in heterojunction with intrinsic thin layer (HIT solar cell due to thermal damage and tough process control. This study aims to understand oxide passivation mechanism of silicon surface using rapid thermal oxidation (RTO process by examining surface effective lifetime and surface recombination velocity. The presence of thin insulating a-Si:H layer is the key to get high Voc by lowering the leakage current (I0 which improves the efficiency of HIT solar cell. The ultrathin thermal passivation silicon oxide (SiO2 layer was deposited by RTO system in the temperature range 500–950°C for 2 to 6 minutes. The thickness of the silicon oxide layer was affected by RTO annealing temperature and treatment time. The best value of surface recombination velocity was recorded for the sample treated at a temperature of 850°C for 6 minutes at O2 flow rate of 3 Lpm. A surface recombination velocity below 25 cm/s was obtained for the silicon oxide layer of 4 nm thickness. This ultrathin SiO2 layer was employed for the fabrication of HIT solar cell structure instead of a-Si:H, (i layer and the passivation and tunneling effects of the silicon oxide layer were exploited. The photocurrent was decreased with the increase of illumination intensity and SiO2 thickness.

  20. Structural and photoluminescent properties of a composite tantalum oxide and silicon nanocrystals embedded in a silicon oxide film

    Energy Technology Data Exchange (ETDEWEB)

    Díaz-Becerril, T., E-mail: tomas.diaz.be@gmail.com; Herrera, V.; Morales, C.; García-Salgado, G.; Rosendo, E.; Coyopol, A., E-mail: acoyopol@gmail.com; Galeazzi, R.; Romano, R.; Nieto-Caballero, F.G.; Sarmiento, J.

    2017-04-15

    Tantalum oxide crystals encrusted in a silicon oxide matrix were synthesized by using a hot filament chemical vapor deposition system (HFCVD). A solid source composed by a mixture in different percentages of Ta{sub 2}O{sub 5} and silicon (Si) powders were used as reactants. The films were grown at 800 °C and 1000 °C under hydrogen ambient. The deposited films were characterized by X-ray photoelectron spectroscopy (XPS), high-resolution transmission electron microscopy (HRTEM) and photoluminescence (PL) at room temperature. From the XPS results it was confirmed the formation of a mixture of Tantalum oxide, silicon oxide and Si nanoparticles (Ta{sub 2}O{sub 5-}SiO{sub 2}-Si(nc)) as seen from the Si (2p) and Ta (4f) lines corresponding to Si{sup +} and Ta{sup +} states respectively. Ta{sub 2}O{sub 5} and Si nanocrystals (Si-NCs) embedded in the silicon oxide films were observed on HRTEM images which corroborate the XPS results. Finally the emission properties of the films exhibited a broad band from 400 to 850 nm caused by the independent PL properties of tantalum oxide and Si-NCs that compose the film. The intensity of the emissions was observed to be dependent on both temperature of deposition and the ratio Ta{sub 2}O{sub 5}/Si, used as initial reactants. Results from this work might supply useful data for the development of future light emitter devices.

  1. Substoichiometric determination of selenium with potassium ethyl xanthate

    International Nuclear Information System (INIS)

    Chandrasekhar Reddy, P.; Polaiah, B.; Rangamannar, B.

    1989-01-01

    A substoichiometric radiochemical method was developed for the determination of selenium with potassium ethyl xanthate. The selenium ethyl xanthate complex formed was extracted into chloroform from borate buffer at pH 5. The effect of foreign ions on the extraction was studied. Microgram quantities of selenium could be conveniently determined with a fair degree of accuracy. The method was successfully applied for the determination of selenium content in food stuffs such as 'Jaggery' and 'Wheat powder'. (author) 4 refs.; 3 figs

  2. Defects and defect generation in oxide layer of ion implanted silicon-silicon dioxide structures

    CERN Document Server

    Baraban, A P

    2002-01-01

    One studies mechanism of generation of defects in Si-SiO sub 2 structure oxide layer as a result of implantation of argon ions with 130 keV energy and 10 sup 1 sup 3 - 3.2 x 10 sup 1 sup 7 cm sup - sup 2 doses. Si-SiO sub 2 structures are produced by thermal oxidation of silicon under 950 deg C temperature. Investigations were based on electroluminescence technique and on measuring of high-frequency volt-farad characteristics. Increase of implantation dose was determined to result in spreading of luminosity centres and in its maximum shifting closer to boundary with silicon. Ion implantation was shown, as well, to result in increase of density of surface states at Si-SiO sub 2 interface. One proposed model of defect generation resulting from Ar ion implantation into Si-SiO sub 2

  3. Substoichiometric determination of chromium by neutron activation analysis

    International Nuclear Information System (INIS)

    Kudo, K.; Shigematsu, T.; Kobayashi, K.

    1977-01-01

    A method of radioactivation analysis has been developed for the determination of chromium. It is based on the substoichiometric extraction of chromium diethyldithiocarbamate into methyl-isobutyl-ketone from acetate buffer solution in the presence of EDTA and potassium cyanide. A solution of NaDDC was prepared by dissolving an appropriate amount of GR grade salt in bidistelled water. The concentration of NaDDC was determined by substoichiometric isotope dilution method using 64 Cu or sup(114m)In tracer of known specific activity. The extraction of chromium is not influenced by the presence of EDTA or potassium cyanide while the extraction of chromium is inhibited in tartrate or citrate solution. All metal ions examined are extracted by NaDDC together with chromium and become to interfere for the substoichiometric extraction of chromium. This can be avoided, however, by the addition of EDTA except for copper and silver. The method has been applied for the determination of chromium in high-purity calcium carbonate and NBS glasses as standard reference materials. (T.G.)

  4. Study Trapped Charge Distribution in P-Channel Silicon-Oxide-Nitride-Oxide-Silicon Memory Device Using Dynamic Programming Scheme

    Science.gov (United States)

    Li, Fu-Hai; Chiu, Yung-Yueh; Lee, Yen-Hui; Chang, Ru-Wei; Yang, Bo-Jun; Sun, Wein-Town; Lee, Eric; Kuo, Chao-Wei; Shirota, Riichiro

    2013-04-01

    In this study, we precisely investigate the charge distribution in SiN layer by dynamic programming of channel hot hole induced hot electron injection (CHHIHE) in p-channel silicon-oxide-nitride-oxide-silicon (SONOS) memory device. In the dynamic programming scheme, gate voltage is increased as a staircase with fixed step amplitude, which can prohibits the injection of holes in SiN layer. Three-dimensional device simulation is calibrated and is compared with the measured programming characteristics. It is found, for the first time, that the hot electron injection point quickly traverses from drain to source side synchronizing to the expansion of charged area in SiN layer. As a result, the injected charges quickly spread over on the almost whole channel area uniformly during a short programming period, which will afford large tolerance against lateral trapped charge diffusion by baking.

  5. Substoichiometric IDA in determination of zinc present in some spices (Paper No. RA-14)

    Energy Technology Data Exchange (ETDEWEB)

    Vaidya, M M; Ray, M N

    1982-01-01

    Results of separation and determination of zinc present in four spices, viz. Coriander, King's cumin, Fennel and Fenugreek seeds by IDA are presented. It is observed that zinc could be estimated by substoichiometric extraction as dithiozonate followed by IDA, in spices. The substoichiometric extraction results at lower concentrations of zinc also, but better results are obtained by increasing the concentration of zinc. The substoichiometric IDA agrees fairly with the conventional chemical analysis.

  6. Optical characterization of nanocrystals in silicon rich oxide superlattices and porous silicon

    International Nuclear Information System (INIS)

    Agocs, E.; Petrik, P.; Milita, S.; Vanzetti, L.; Gardelis, S.; Nassiopoulou, A.G.; Pucker, G.; Balboni, R.; Fried, M.

    2011-01-01

    We propose to analyze ellipsometry data by using effective medium approximation (EMA) models. Thanks to EMA, having nanocrystalline reference dielectric functions and generalized critical point (GCP) model the physical parameters of two series of samples containing silicon nanocrystals, i.e. silicon rich oxide (SRO) superlattices and porous silicon layers (PSL), have been determined. The superlattices, consisting of ten SRO/SiO 2 layer pairs, have been prepared using plasma enhanced chemical vapor deposition. The porous silicon layers have been prepared using short monopulses of anodization current in the transition regime between porous silicon formation and electropolishing, in a mixture of hydrofluoric acid and ethanol. The optical modeling of both structures is similar. The effective dielectric function of the layer is calculated by EMA using nanocrystalline components (nc-Si and GCP) in a dielectric matrix (SRO) or voids (PSL). We discuss the two major problems occurring when modeling such structures: (1) the modeling of the vertically non-uniform layer structures (including the interface properties like nanoroughness at the layer boundaries) and (2) the parameterization of the dielectric function of nanocrystals. We used several techniques to reduce the large number of fit parameters of the GCP models. The obtained results are in good agreement with those obtained by X-ray diffraction and electron microscopy. We investigated the correlation of the broadening parameter and characteristic EMA components with the nanocrystal size and the sample preparation conditions, such as the annealing temperatures of the SRO superlattices and the anodization current density of the porous silicon samples. We found that the broadening parameter is a sensitive measure of the nanocrystallinity of the samples, even in cases, where the nanocrystals are too small to be visible for X-ray scattering. Major processes like sintering, phase separation, and intermixing have been

  7. Silicon heterojunction solar cells with novel fluorinated n-type nanocrystalline silicon oxide emitters on p-type crystalline silicon

    Science.gov (United States)

    Dhar, Sukanta; Mandal, Sourav; Das, Gourab; Mukhopadhyay, Sumita; Pratim Ray, Partha; Banerjee, Chandan; Barua, Asok Kumar

    2015-08-01

    A novel fluorinated phosphorus doped silicon oxide based nanocrystalline material have been used to prepare heterojunction solar cells on flat p-type crystalline silicon (c-Si) Czochralski (CZ) wafers. The n-type nc-SiO:F:H material were deposited by radio frequency plasma enhanced chemical vapor deposition. Deposited films were characterized in detail by using atomic force microscopy (AFM), high resolution transmission electron microscopy (HRTEM), Raman, fourier transform infrared spectroscopy (FTIR) and optoelectronics properties have been studied using temperature dependent conductivity measurement, Ellipsometry, UV-vis spectrum analysis etc. It is observed that the cell fabricated with fluorinated silicon oxide emitter showing higher initial efficiency (η = 15.64%, Jsc = 32.10 mA/cm2, Voc = 0.630 V, FF = 0.77) for 1 cm2 cell area compare to conventional n-a-Si:H emitter (14.73%) on flat c-Si wafer. These results indicate that n type nc-SiO:F:H material is a promising candidate for heterojunction solar cell on p-type crystalline wafers. The high Jsc value is associated with excellent quantum efficiencies at short wavelengths (<500 nm).

  8. Direct comparison of the electrical properties in metal/oxide/nitride/oxide/silicon and metal/aluminum oxide/nitride/oxide/silicon capacitors with equivalent oxide thicknesses

    Energy Technology Data Exchange (ETDEWEB)

    An, Ho-Myoung; Seo, Yu Jeong; Kim, Hee Dong; Kim, Kyoung Chan; Kim, Jong-Guk [School of Electrical Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Cho, Won-Ju; Koh, Jung-Hyuk [Department of Electronic Materials Engineering, Kwangwoon University, Seoul 139-701 (Korea, Republic of); Sung, Yun Mo [Department of Materials and Science Engineering, Korea University, Seoul 136-713 (Korea, Republic of); Kim, Tae Geun, E-mail: tgkim1@korea.ac.k [School of Electrical Engineering, Korea University, Seoul 136-713 (Korea, Republic of)

    2009-07-31

    We examine the electrical properties of metal/oxide/nitride/oxide/silicon (MONOS) capacitors with two different blocking oxides, SiO{sub 2} and Al{sub 2}O{sub 3}, under the influence of the same electric field. The thickness of the Al{sub 2}O{sub 3} layer is set to 150 A, which is electrically equivalent to a thickness of the SiO{sub 2} layer of 65 A, in the MONOS structure for this purpose. The capacitor with the Al{sub 2}O{sub 3} blocking layer shows a larger capacitance-voltage memory window of 8.6 V, lower program voltage of 7 V, faster program/erase speeds of 10 ms/1 {mu}s, lower leakage current of 100 pA and longer data retention than the one with the SiO{sub 2} blocking layer does. These improvements are attributed to the suppression of the carrier transport to the gate electrode afforded by the use of an Al{sub 2}O{sub 3} blocking layer physically thicker than the SiO{sub 2} one, as well as the effective charge-trapping by Al{sub 2}O{sub 3} at the deep energy levels in the nitride layer.

  9. Thermal processing and native oxidation of silicon nanoparticles

    International Nuclear Information System (INIS)

    Winters, Brandon J.; Holm, Jason; Roberts, Jeffrey T.

    2011-01-01

    In this study, Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and electron energy loss spectroscopy (EELS) were used to investigate in-air oxidation of silicon nanoparticles ca. 11 nm in diameter. Particle samples were prepared first by extracting them from an RF plasma synthesis reactor, and then heating them in an inert carrier gas stream. The resulting particles had varying surface hydrogen coverages and relative amounts of SiH x (x = 1, 2, and 3), depending on the temperature to which they had been heated. The particles were allowed to oxidize in-air for several weeks. FTIR, XPS, and EELS analyses that were performed during this period clearly establish that adsorbed hydrogen retards oxidation, although in complex ways. In particular, particles that have been heated to intermediate hydrogen coverages oxidize more slowly in air than do freshly generated particles that have a much higher hydrogen content. In addition, the loss of surface hydride species at high processing temperatures results in fast initial oxidation and the formation of a self-limiting oxide layer. Analogous measurements made on deuterium-covered particles show broadly similar behavior; i.e., that oxidation is the slowest at some intermediate coverage of adsorbed deuterium.

  10. Phase formation and stability in TiO{sub x} and ZrO{sub x} thin films. Extremely sub-stoichiometric functional oxides for electrical and TCO applications

    Energy Technology Data Exchange (ETDEWEB)

    Henning, Ralph A.; Leichtweiss, Thomas; Decker, Yannic; Janek, Juergen [Giessen Univ. (Germany). Inst. of Physical Chemistry; Dorow-Gerspach, Daniel; Schmidt, Ruediger; Wuttig, Matthias [RWTH Aachen Univ. (Germany). Inst. of Physics; Wolff, Niklas; Schuermann, Ulrich; Kienle, Lorenz [Kiel Univ. (Germany). Faculty of Engineering

    2017-03-01

    Most functional materials are thermodynamic equilibrium phases representing minima in the thermodynamic phase space. However, it is expected that many metastable phases with highly interesting properties also exist. Here, we report on a systematic approach to prepare thin-films of such non-equilibrium phases based on the gas phase deposition methods sputtering and pulsed laser deposition (PLD). Our synthetic strategy is to deposit a ''precursor phase'' which is amorphous or already a crystalline non-equilibrium phase. Subsequent heat treatment leads to the nucleation of crystalline phases which again may be metastable or stable compounds. In the present paper we focus on the binary systems Ti-O and Zr-O, both systems being widely applied and technologically relevant. Highly oxygen-deficient titanium oxide (TiO{sub 1.6}) and zirconium oxide (ZrO) films prepared by pulsed laser deposition at room temperature are optically absorbing and possess electronic conductivities in the range of 10 S/cm. Both materials are metastable in respect to both composition and structure. For TiO{sub 1.6} we find an amorphous matrix with embedded grains of cubic titanium monoxide (γ-TiO) directly after deposition. Upon annealing nanocrystalline grains of metallic Ti are formed in the amorphous matrix due to an internal solid-state disproportionation whereas the electrical conductivity of the films increases and comes close to metal-like conductivity (1000 S/cm) at about 450 C. Congruently, room temperature deposited ZrO films with an average composition of Zr:O= 1:1 contain small ZrO nanocrystals within an amorphous matrix. Heat treatment again leads to an internal disproportionation reaction whereas small crystals of Zr{sub 2}O and ZrO{sub 2} precipitate at temperatures as low as 75 C. Increasing the temperature then results in the crystallization of metastable tetragonal ZrO{sub 2} at about 400 C. Sputter deposition allows a subtler control of the oxygen partial

  11. Self-cleaning glass coating containing titanium oxide and silicon

    International Nuclear Information System (INIS)

    Araujo, A.O. de; Alves, A.K.; Berutti, F.A.; Bergmann, C.P.

    2009-01-01

    Using the electro spinning technique nano fibers of titanium oxide doped with silicon were synthesized. As precursor materials, titanium propoxide, silicon tetra propoxide and a solution of polyvinylpyrrolidone were used. The non-tissue material obtained was characterized by X-ray diffraction to determine the phase and crystallite size, BET method to determine the surface and SEM to analyze the microstructure of the fibers. After ultrasound dispersion of this material in ethanol, the glass coatings were made by dip-coating methodology. The influence of the removal velocity, the solution composition and the glass surface preparation were evaluated. The film was characterized by the contact angle of a water droplet in its surface. (author)

  12. Ion beam analysis of PECVD silicon oxide thin films

    International Nuclear Information System (INIS)

    Fernandez-Lima, F.; Rodriguez, J.A.; Pedrero, E.; Fonseca Filho, H.D.; Llovera, A.; Riera, M.; Dominguez, C.; Behar, M.; Zawislak, F.C.

    2006-01-01

    A study of ion beam analysis techniques of plasma enhanced chemical vapor deposited (PECVD) silicon oxide thin films (1 μm thick) obtained from silane (SiH 4 ) and nitrous oxide (N 2 O) is reported. The film, elemental composition and surface morphology were determined as function of the reactant gas flow ratio, R = [N 2 O]/[SiH 4 ] in the 22-110 range using the Rutherford backscattering spectrometry, nuclear reaction analysis and atomic force microscopy techniques. The density of the films was determined by combining the RBS and thickness measurements. All the experiments were done at a deposition temperature of 300 deg. C. In all the cases almost stoichiometric oxides were obtained being the impurity content function of R. It was also observed that physical properties such as density, surface roughness and shape factor increase with R in the studied interval

  13. Size modulation of nanocrystalline silicon embedded in amorphous silicon oxide by Cat-CVD

    International Nuclear Information System (INIS)

    Matsumoto, Y.; Godavarthi, S.; Ortega, M.; Sanchez, V.; Velumani, S.; Mallick, P.S.

    2011-01-01

    Different issues related to controlling size of nanocrystalline silicon (nc-Si) embedded in hydrogenated amorphous silicon oxide (a-SiO x :H) deposited by catalytic chemical vapor deposition (Cat-CVD) have been reported. Films were deposited using tantalum (Ta) and tungsten (W) filaments and it is observed that films deposited using tantalum filament resulted in good control on the properties. The parameters which can affect the size of nc-Si domains have been studied which include hydrogen flow rate, catalyst and substrate temperatures. The deposited samples are characterized by X-ray diffraction, HRTEM and micro-Raman spectroscopy, for determining the size of the deposited nc-Si. The crystallite formation starts for Ta-catalyst around the temperature of 1700 o C.

  14. Passivation mechanism in silicon heterojunction solar cells with intrinsic hydrogenated amorphous silicon oxide layers

    Science.gov (United States)

    Deligiannis, Dimitrios; van Vliet, Jeroen; Vasudevan, Ravi; van Swaaij, René A. C. M. M.; Zeman, Miro

    2017-02-01

    In this work, we use intrinsic hydrogenated amorphous silicon oxide layers (a-SiOx:H) with varying oxygen content (cO) but similar hydrogen content to passivate the crystalline silicon wafers. Using our deposition conditions, we obtain an effective lifetime (τeff) above 5 ms for cO ≤ 6 at. % for passivation layers with a thickness of 36 ± 2 nm. We subsequently reduce the thickness of the layers using an accurate wet etching method to ˜7 nm and deposit p- and n-type doped layers fabricating a device structure. After the deposition of the doped layers, τeff appears to be predominantly determined by the doped layers themselves and is less dependent on the cO of the a-SiOx:H layers. The results suggest that τeff is determined by the field-effect rather than by chemical passivation.

  15. Ultrathin Oxide Passivation Layer by Rapid Thermal Oxidation for the Silicon Heterojunction Solar Cell Applications

    OpenAIRE

    Lee, Youngseok; Oh, Woongkyo; Dao, Vinh Ai; Hussain, Shahzada Qamar; Yi, Junsin

    2012-01-01

    It is difficult to deposit extremely thin a-Si:H layer in heterojunction with intrinsic thin layer (HIT) solar cell due to thermal damage and tough process control. This study aims to understand oxide passivation mechanism of silicon surface using rapid thermal oxidation (RTO) process by examining surface effective lifetime and surface recombination velocity. The presence of thin insulating a-Si:H layer is the key to get high Voc by lowering the leakage current (I0) which improves the efficie...

  16. Wet-Chemical Preparation of Silicon Tunnel Oxides for Transparent Passivated Contacts in Crystalline Silicon Solar Cells.

    Science.gov (United States)

    Köhler, Malte; Pomaska, Manuel; Lentz, Florian; Finger, Friedhelm; Rau, Uwe; Ding, Kaining

    2018-05-02

    Transparent passivated contacts (TPCs) using a wide band gap microcrystalline silicon carbide (μc-SiC:H(n)), silicon tunnel oxide (SiO 2 ) stack are an alternative to amorphous silicon-based contacts for the front side of silicon heterojunction solar cells. In a systematic study of the μc-SiC:H(n)/SiO 2 /c-Si contact, we investigated selected wet-chemical oxidation methods for the formation of ultrathin SiO 2 , in order to passivate the silicon surface while ensuring a low contact resistivity. By tuning the SiO 2 properties, implied open-circuit voltages of 714 mV and contact resistivities of 32 mΩ cm 2 were achieved using μc-SiC:H(n)/SiO 2 /c-Si as transparent passivated contacts.

  17. Study of the processes of carbonization and oxidation of porous silicon by Raman and IR spectroscopy

    International Nuclear Information System (INIS)

    Vasin, A. V.; Okholin, P. N.; Verovsky, I. N.; Nazarov, A. N.; Lysenko, V. S.; Kholostov, K. I.; Bondarenko, V. P.; Ishikawa, Y.

    2011-01-01

    Porous silicon layers were produced by electrochemical etching of single-crystal silicon wafers with the resistivity 10 Ω cm in the aqueous-alcohol solution of hydrofluoric acid. Raman spectroscopy and infrared absorption spectroscopy are used to study the processes of interaction of porous silicon with undiluted acetylene at low temperatures and the processes of oxidation of carbonized porous silicon by water vapors. It is established that, even at the temperature 550°C, the silicon-carbon bonds are formed at the pore surface and the graphite-like carbon condensate emerges. It is shown that the carbon condensate inhibits oxidation of porous silicon by water vapors and contributes to quenching of white photoluminescence in the oxidized carbonized porous silicon nanocomposite layer.

  18. A model for the formation of lattice defects at silicon oxide precipitates in silicon

    International Nuclear Information System (INIS)

    Vanhellemont, J.; Gryse, O. de; Clauws, P.

    2003-01-01

    The critical size of silicon oxide precipitates and the formation of lattice defects by the precipitates are discussed. An expression is derived allowing estimation of self-interstitial emission by spherical precipitates as well as strain build-up during precipitate growth. The predictions are compared with published experimental data. A model for stacking fault nucleation at oxide precipitates is developed based on strain and self-interstitial accumulation during the thermal history of the wafer. During a low-temperature treatment high levels of strain develop. During subsequent high-temperature treatment, excess strain energy in the precipitate is released by self-interstitial emission leading to favourable conditions for stacking fault nucleation

  19. Toward Annealing-Stable Molybdenum-Oxide-Based Hole-Selective Contacts For Silicon Photovoltaics

    KAUST Repository

    Essig, Stephanie; Dré on, Julie; Rucavado, Esteban; Mews, Mathias; Koida, Takashi; Boccard, Mathieu; Werner, Jé ré mie; Geissbü hler, Jonas; Lö per, Philipp; Morales-Masis, Monica; Korte, Lars; De Wolf, Stefaan; Balllif, Christophe

    2018-01-01

    Molybdenum oxide (MoOX) combines a high work function with broadband optical transparency. Sandwiched between a hydrogenated intrinsic amorphous silicon passivation layer and a transparent conductive oxide, this material allows a highly efficient

  20. 22.5% efficient silicon heterojunction solar cell with molybdenum oxide hole collector

    Energy Technology Data Exchange (ETDEWEB)

    Geissbühler, Jonas, E-mail: jonas.geissbuehler@epfl.ch; Werner, Jérémie; Martin de Nicolas, Silvia; Hessler-Wyser, Aïcha; Tomasi, Andrea; Niesen, Bjoern; De Wolf, Stefaan [Photovoltaics and Thin Film Electronics Laboratory, Institute of Microengineering (IMT), École Polytechnique Fédérale de Lausanne (EPFL), Rue de la Maladière 71b, CH-2000 Neuchâtel (Switzerland); Barraud, Loris; Despeisse, Matthieu; Nicolay, Sylvain [CSEM PV-Center, Jaquet-Droz 1, CH-2000 Neuchâtel (Switzerland); Ballif, Christophe [Photovoltaics and Thin Film Electronics Laboratory, Institute of Microengineering (IMT), École Polytechnique Fédérale de Lausanne (EPFL), Rue de la Maladière 71b, CH-2000 Neuchâtel (Switzerland); CSEM PV-Center, Jaquet-Droz 1, CH-2000 Neuchâtel (Switzerland)

    2015-08-24

    Substituting the doped amorphous silicon films at the front of silicon heterojunction solar cells with wide-bandgap transition metal oxides can mitigate parasitic light absorption losses. This was recently proven by replacing p-type amorphous silicon with molybdenum oxide films. In this article, we evidence that annealing above 130 °C—often needed for the curing of printed metal contacts—detrimentally impacts hole collection of such devices. We circumvent this issue by using electrodeposited copper front metallization and demonstrate a silicon heterojunction solar cell with molybdenum oxide hole collector, featuring a fill factor value higher than 80% and certified energy conversion efficiency of 22.5%.

  1. 22.5% efficient silicon heterojunction solar cell with molybdenum oxide hole collector

    OpenAIRE

    Geissbühler Jonas; Werner Jérémie; Martin de Nicolas Silvia; Barraud Loris; Hessler-Wyser Aïcha; Despeisse Matthieu; Nicolay Sylvain; Tomasi Andrea; Niesen Bjoern; De Wolf Stefaan; Ballif Christophe

    2015-01-01

    Substituting the doped amorphous silicon films at the front of silicon heterojunction solar cells with wide bandgap transition metal oxides can mitigate parasitic light absorption losses. This was recently proven by replacing p type amorphous silicon with molybdenum oxide films. In this article we evidence that annealing above 130?°C—often needed for the curing of printed metal contacts—detrimentally impacts hole collection of such devices. We circumvent this issue by using electrodeposited c...

  2. The role of oxide interlayers in back reflector configurations for amorphous silicon solar cells

    NARCIS (Netherlands)

    Demontis, V.; Sanna, C.; Melskens, J.; Santbergen, R.; Smets, A.H.M.; Damiano, A.; Zeman, M.

    2013-01-01

    Thin oxide interlayers are commonly added to the back reflector of thin-film silicon solar cells to increase their current. To gain more insight in the enhancement mechanism, we tested different back reflector designs consisting of aluminium-doped zinc oxide (ZnO:Al) and/or hydrogenated silicon

  3. Charging effects during focused electron beam induced deposition of silicon oxide

    NARCIS (Netherlands)

    de Boer, Sanne K.; van Dorp, Willem F.; De Hosson, Jeff Th. M.

    2011-01-01

    This paper concentrates on focused electron beam induced deposition of silicon oxide. Silicon oxide pillars are written using 2, 4, 6, 8, 10-pentamethyl-cyclopenta-siloxane (PMCPS) as precursor. It is observed that branching of the pillar occurs above a minimum pillar height. The branching is

  4. Shrinking of silicon nanocrystals embedded in an amorphous silicon oxide matrix during rapid thermal annealing in a forming gas atmosphere

    Science.gov (United States)

    van Sebille, M.; Fusi, A.; Xie, L.; Ali, H.; van Swaaij, R. A. C. M. M.; Leifer, K.; Zeman, M.

    2016-09-01

    We report the effect of hydrogen on the crystallization process of silicon nanocrystals embedded in a silicon oxide matrix. We show that hydrogen gas during annealing leads to a lower sub-band gap absorption, indicating passivation of defects created during annealing. Samples annealed in pure nitrogen show expected trends according to crystallization theory. Samples annealed in forming gas, however, deviate from this trend. Their crystallinity decreases for increased annealing time. Furthermore, we observe a decrease in the mean nanocrystal size and the size distribution broadens, indicating that hydrogen causes a size reduction of the silicon nanocrystals.

  5. Strained silicon/silicon germanium heterojunction n-channel metal oxide semiconductor field effect transistors

    International Nuclear Information System (INIS)

    Olsen, Sarah H.

    2002-01-01

    Investigations into the performance of strained silicon/silicon-germanium (Si/SiGe) n-channel metal-oxide-semiconductor field effect transistors (MOSFETs) have been carried out. Theoretical predictions suggest that use of a strained Si/SiGe material system with advanced material properties compared with conventional silicon allows enhanced MOSFET device performance. This study has therefore investigated the practical feasibility of obtaining superior electrical performance using a Si/SiGe material system. The MOSFET devices consisted of a strained Si surface channel and were fabricated on relaxed SiGe material using a reduced thermal budget process in order to preserve the strain. Two batches of strained Si/SiGe devices fabricated on material grown by differing methods have been analysed and both showed good transistor action. A correlation of electrical and physical device data established that the electrical device behaviour was closely related to the SiGe material quality, which differed depending on growth technique. The cross-wafer variation in the electrical performance of the strained Si/SiGe devices was found to be a function of material quality, thus the viability of Si/SiGe MOSFET technology for commercial applications has been addressed. Of particular importance was the finding that large-scale 'cross-hatching' roughness associated with relaxed SiGe alloys led to degradation in the small-scale roughness at the gate oxide interface, which affects electrical device performance. The fabrication of strained Si MOSFET devices on high quality SiGe material thus enabled significant performance gains to be realised compared with conventional Si control devices. In contrast, the performance of devices fabricated on material with severe cross-hatching roughness was found to be diminished by the nanoscale oxide interface roughness. The effect of device processing on SiGe material with differing as-grown roughness has been carried out and compared with the reactions

  6. Tunnel Oxides Formed by Field-Induced Anodisation for Passivated Contacts of Silicon Solar Cells

    Directory of Open Access Journals (Sweden)

    Jingnan Tong

    2018-02-01

    Full Text Available Tunnel silicon oxides form a critical component for passivated contacts for silicon solar cells. They need to be sufficiently thin to allow carriers to tunnel through and to be uniform both in thickness and stoichiometry across the silicon wafer surface, to ensure uniform and low recombination velocities if high conversion efficiencies are to be achieved. This paper reports on the formation of ultra-thin silicon oxide layers by field-induced anodisation (FIA, a process that ensures uniform oxide thickness by passing the anodisation current perpendicularly through the wafer to the silicon surface that is anodised. Spectroscopical analyses show that the FIA oxides contain a lower fraction of Si-rich sub-oxides compared to wet-chemical oxides, resulting in lower recombination velocities at the silicon and oxide interface. This property along with its low temperature formation highlights the potential for FIA to be used to form low-cost tunnel oxide layers for passivated contacts of silicon solar cells.

  7. Surface and Core Electronic Structure of Oxidized Silicon Nanocrystals

    Directory of Open Access Journals (Sweden)

    Noor A. Nama

    2010-01-01

    Full Text Available Ab initio restricted Hartree-Fock method within the framework of large unit cell formalism is used to simulate silicon nanocrystals between 216 and 1000 atoms (1.6–2.65 nm in diameter that include Bravais and primitive cell multiples. The investigated properties include core and oxidized surface properties. Results revealed that electronic properties converge to some limit as the size of the nanocrystal increases. Increasing the size of the core of a nanocrystal resulted in an increase of the energy gap, valence band width, and cohesive energy. The lattice constant of the core and oxidized surface parts shows a decreasing trend as the nanocrystal increases in a size that converges to 5.28 Ǻ in a good agreement with the experiment. Surface and core convergence to the same lattice constant reflects good adherence of oxide layer at the surface. The core density of states shows highly degenerate states that split at the oxygenated (001-(1×1 surface due to symmetry breaking. The nanocrystal surface shows smaller gap and higher valence and conduction bands when compared to the core part, due to oxygen surface atoms and reduced structural symmetry. The smaller surface energy gap shows that energy gap of the nanocrystal is controlled by the surface part. Unlike the core part, the surface part shows a descending energy gap that proves its obedience to quantum confinement effects. Nanocrystal geometry proved to have some influence on all electronic properties including the energy gap.

  8. Suppression of interfacial voids formation during silane (SiH4)-based silicon oxide bonding with a thin silicon nitride capping layer

    Science.gov (United States)

    Lee, Kwang Hong; Bao, Shuyu; Wang, Yue; Fitzgerald, Eugene A.; Seng Tan, Chuan

    2018-01-01

    The material properties and bonding behavior of silane-based silicon oxide layers deposited by plasma-enhanced chemical vapor deposition were investigated. Fourier transform infrared spectroscopy was employed to determine the chemical composition of the silicon oxide films. The incorporation of hydroxyl (-OH) groups and moisture absorption demonstrates a strong correlation with the storage duration for both as-deposited and annealed silicon oxide films. It is observed that moisture absorption is prevalent in the silane-based silicon oxide film due to its porous nature. The incorporation of -OH groups and moisture absorption in the silicon oxide films increase with the storage time (even in clean-room environments) for both as-deposited and annealed silicon oxide films. Due to silanol condensation and silicon oxidation reactions that take place at the bonding interface and in the bulk silicon, hydrogen (a byproduct of these reactions) is released and diffused towards the bonding interface. The trapped hydrogen forms voids over time. Additionally, the absorbed moisture could evaporate during the post-bond annealing of the bonded wafer pair. As a consequence, defects, such as voids, form at the bonding interface. To address the problem, a thin silicon nitride capping film was deposited on the silicon oxide layer before bonding to serve as a diffusion barrier to prevent moisture absorption and incorporation of -OH groups from the ambient. This process results in defect-free bonded wafers.

  9. Viscous properties of aluminum oxide nanotubes and aluminium oxide nanoparticles - silicone oil suspensions

    Science.gov (United States)

    Thapa, Ram; French, Steven; Delgado, Adrian; Ramos, Carlos; Gutierrez, Jose; Chipara, Mircea; Lozano, Karen

    2010-03-01

    Electrorheological (ER) fluids consisting of γ-aluminum oxide nanotubes and γ-aluminum oxide nanoparticles dispersed within silicone oil were prepared. The relationship between shear stress and shear rate was measured and theoretically simulated by using an extended Bingham model for both the rheological and electrorheological features of these systems. Shear stress and viscosity showed a sharp increase for the aluminum oxide nanotubes suspensions subjected to applied electric fields whereas aluminum oxide nanoparticles suspensions showed a moderate change. It was found that the transition from liquid to solid state (mediated by the applied electric field) can be described by a power law and that for low applied voltages the relationship is almost linear.

  10. Study of an Amorphous Silicon Oxide Buffer Layer for p-Type Microcrystalline Silicon Oxide/n-Type Crystalline Silicon Heterojunction Solar Cells and Their Temperature Dependence

    Directory of Open Access Journals (Sweden)

    Taweewat Krajangsang

    2014-01-01

    Full Text Available Intrinsic hydrogenated amorphous silicon oxide (i-a-SiO:H films were used as front and rear buffer layers in crystalline silicon heterojunction (c-Si-HJ solar cells. The surface passivity and effective lifetime of these i-a-SiO:H films on an n-type silicon wafer were improved by increasing the CO2/SiH4 ratios in the films. Using i-a-SiO:H as the front and rear buffer layers in c-Si-HJ solar cells was investigated. The front i-a-SiO:H buffer layer thickness and the CO2/SiH4 ratio influenced the open-circuit voltage (Voc, fill factor (FF, and temperature coefficient (TC of the c-Si-HJ solar cells. The highest total area efficiency obtained was 18.5% (Voc=700 mV, Jsc=33.5 mA/cm2, and FF=0.79. The TC normalized for this c-Si-HJ solar cell efficiency was −0.301%/°C.

  11. Effect of porous silicon layer on the performance of Si/oxide photovoltaic and photoelectrochemical cells

    International Nuclear Information System (INIS)

    Badawy, Waheed A.

    2008-01-01

    Photovoltaic and photoelectrochemical systems were prepared by the formation of a thin porous film on silicon. The porous silicon layer was formed on the top of a clean oxide free silicon wafer surface by anodic etching in HF/H 2 O/C 2 H 5 OH mixture (2:1:1). The silicon was then covered by an oxide film (tin oxide, ITO or titanium oxide). The oxide films were prepared by the spray/pyrolysis technique which enables doping of the oxide film by different atoms like In, Ru or Sb during the spray process. Doping of SnO 2 or TiO 2 films with Ru atoms improves the surface characteristics of the oxide film which improves the solar conversion efficiency. The prepared solar cells are stable against environmental attack due to the presence of the stable oxide film. It gives relatively high short circuit currents (I sc ), due to the presence of the porous silicon layer, which leads to the recorded high conversion efficiency. Although the open-circuit potential (V oc ) and fill factor (FF) were not affected by the thickness of the porous silicon film, the short circuit current was found to be sensitive to this thickness. An optimum thickness of the porous film and also the oxide layer is required to optimize the solar cell efficiency. The results represent a promising system for the application of porous silicon layers in solar energy converters. The use of porous silicon instead of silicon single crystals in solar cell fabrication and the optimization of the solar conversion efficiency will lead to the reduction of the cost as an important factor and also the increase of the solar cell efficiency making use of the large area of the porous structures

  12. Formation of silicon carbide by laser ablation in graphene oxide-N-methyl-2-pyrrolidone suspension on silicon surface

    Science.gov (United States)

    Jaleh, Babak; Ghasemi, Samaneh; Torkamany, Mohammad Javad; Salehzadeh, Sadegh; Maleki, Farahnaz

    2018-01-01

    Laser ablation of a silicon wafer in graphene oxide-N-methyl-2-pyrrolidone (GO-NMP) suspension was carried out with a pulsed Nd:YAG laser (pulse duration = 250 ns, wavelength = 1064 nm). The surface of silicon wafer before and after laser ablation was studied using optical microscopy, scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX). The results showed that the ablation of silicon surface in liquid by pulsed laser was done by the process of melt expulsion under the influence of the confined plasma-induced pressure or shock wave trapped between the silicon wafer and the liquid. The X-ray diffraction‌ (XRD) pattern of Si wafer after laser ablation showed that 4H-SiC layer is formed on its surface. The formation of the above layer was also confirmed by Raman spectroscopy, and X-ray photoelectron spectroscopy‌ (XPS), as well as EDX was utilized. The reflectance of samples decreased with increasing pulse energy. Therefore, the morphological alteration and the formation of SiC layer at high energy increase absorption intensity in the UV‌-vis regions. Theoretical calculations confirm that the formation of silicon carbide from graphene oxide and silicon wafer is considerably endothermic. Development of new methods for increasing the reflectance without causing harmful effects is still an important issue for crystalline Si solar cells. By using the method described in this paper, the optical properties of solar cells can be improved.

  13. Functionalization of 2D macroporous silicon under the high-pressure oxidation

    Science.gov (United States)

    Karachevtseva, L.; Kartel, M.; Kladko, V.; Gudymenko, O.; Bo, Wang; Bratus, V.; Lytvynenko, O.; Onyshchenko, V.; Stronska, O.

    2018-03-01

    Addition functionalization after high-pressure oxidation of 2D macroporous silicon structures is evaluated. X-ray diffractometry indicates formation of orthorhombic SiO2 phase on macroporous silicon at oxide thickness of 800-1200 nm due to cylindrical symmetry of macropores and high thermal expansion coefficient of SiO2. Pb center concentration grows with the splitting energy of LO- and TO-phonons and SiO2 thickness in oxidized macroporous silicon structures. This increase EPR signal amplitude and GHz radiation absorption and is promising for development of high-frequency devices and electronically controlled elements.

  14. A parametric study of laser induced ablation-oxidation on porous silicon surfaces

    International Nuclear Information System (INIS)

    De Stefano, Luca; Rea, Ilaria; Nigro, M Arcangela; Della Corte, Francesco G; Rendina, Ivo

    2008-01-01

    We have investigated the laser induced ablation-oxidation process on porous silicon layers having different porosities and thicknesses by non-destructive optical techniques. In particular, the interaction between a low power blue light laser and the porous silicon surfaces has been characterized by variable angle spectroscopic ellipsometry and Fourier transform infrared spectroscopy. The oxidation profiles etched on the porous samples can be tuned as functions of the layer porosity and laser fluence. Oxide stripes of width less than 2 μm and with thicknesses between 100 nm and 5 μm have been produced, depending on the porosity of the porous silicon, by using a 40 x focusing objective

  15. The suitability of silicon carbide for photocatalytic water oxidation

    Science.gov (United States)

    Aslam, M.; Qamar, M. T.; Ahmed, Ikram; Rehman, Ateeq Ur; Ali, Shahid; Ismail, I. M. I.; Hameed, Abdul

    2018-04-01

    Silicon carbide (SiC), owing to its extraordinary chemical stability and refractory properties, is widely used in the manufacturing industry. Despite the semiconducting nature and morphology-tuned band gap, its efficacy as photocatalysts has not been thoroughly investigated. The current study reports the synthesis, characterization and the evaluation of the capability of silicon carbide for hydrogen generation from water splitting. The optical characterization of the as-synthesized powder exposed the formation of multi-wavelength absorbing entities in synthetic process. The structural analysis by XRD and the fine microstructure analysis by HRTEM revealed the cubic 3C-SiC (β-SiC) and hexagonal α-polymorphs (2H-SiC and 6H-SiC) as major and minor phases, respectively. The Mott-Schottky analysis verified the n-type nature of the material with the flat band potential of - 0.7 V. In the electrochemical evaluation, the sharp increase in the peak currents in various potential ranges, under illumination, revealed the plausible potential of the material for the oxidation of water and generation of hydrogen. The generation of hydrogen and oxygen, as a consequence of water splitting in the actual photocatalytic experiments, was observed and measured. A significant increase in the yield of hydrogen was noticed in the presence of methanol as h + scavenger, whereas a retarding effect was offered by the Fe3+ entities that served as e - scavengers. The combined effect of both methanol and Fe3+ ions in the photocatalytic process was also investigated. Besides hydrogen gas, the other evolved gasses such as methane and carbon monoxide were also measured to estimate the mechanism of the process.

  16. New transport phenomena probed by dielectric spectroscopy of oxidized and non-oxidized porous silicon

    Energy Technology Data Exchange (ETDEWEB)

    Urbach, B.; Axelrod, E.; Sa' ar, A. [Racah Institute of Physics and the Center for Nanoscience and Nanotechnology, the Hebrew University of Jerusalem, Jerusalem 91904 (Israel)

    2007-05-15

    Dielectric spectroscopy accompanied by infrared (IR) and photoluminescence (PL) spectroscopy have been utilized to reveal the correlation between transport, optical and structural properties of oxidized porous silicon (PS). Three relaxation processes at low-, mid- and high-temperatures were observed, including dc-conductivity at high-temperatures. Both the low-T relaxation and the dc conductivity were found to be thermally activated processes that involve tunneling and hopping in between the nanocrystals in oxidized PS. We have found that the dc-conductivity is limited by geometrical constrictions along the transport channels, which are not effected by the oxidation process and are characterized by activation energies of about {proportional_to}0.85 eV. The low-T relaxation process involves thermal activation followed by tunneling in between neighbor nanocrystals, with somewhat lower activation energies. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  17. Exploring the deposition of oxides on silicon for photovoltaic cells by pulsed laser deposition

    NARCIS (Netherlands)

    Doeswijk, L.M.; de Moor, Hugo H.C.; Rogalla, Horst; Blank, David H.A.

    2002-01-01

    Since most commercially available solar cells are still made from silicon, we are exploring the introduction of passivating qualities in oxides, with the potential to serve as an antireflection coating. Pulsed laser deposition (PLD) was used to deposit TiO2 and SrTiO3 coatings on silicon substrates.

  18. Laser direct writing of oxide structures on hydrogen-passivated silicon surfaces

    DEFF Research Database (Denmark)

    Müllenborn, Matthias; Birkelund, Karen; Grey, Francois

    1996-01-01

    on amorphous and crystalline silicon surfaces in order to determine the depassivation mechanism. The minimum linewidth achieved is about 450 nm using writing speeds of up to 100 mm/s. The process is fully compatible with local oxidation of silicon by scanning probe lithography. Wafer-scale patterns can...

  19. Method for forming indium oxide/n-silicon heterojunction solar cells

    Science.gov (United States)

    Feng, Tom; Ghosh, Amal K.

    1984-03-13

    A high photo-conversion efficiency indium oxide/n-silicon heterojunction solar cell is spray deposited from a solution containing indium trichloride. The solar cell exhibits an Air Mass One solar conversion efficiency in excess of about 10%.

  20. Synchrotron x-ray reflectivity study of oxidation/passivation of copper and silicon

    International Nuclear Information System (INIS)

    Chu, Y.; Nagy, Z.; Parkhutik, V.; You, H.

    1999-01-01

    Synchrotron x-ray-scattering technique studies of copper and silicon electrochemical interfaces are reported. These two examples illustrate the application of synchrotron x-ray techniques for oxidation, passivation, and dissolution of metals and semiconductors

  1. Synchrotron x-ray reflectivity study of oxidation/passivation of copper and silicon.

    Energy Technology Data Exchange (ETDEWEB)

    Chu, Y.; Nagy, Z.; Parkhutik, V.; You, H.

    1999-07-21

    Synchrotron x-ray-scattering technique studies of copper and silicon electrochemical interfaces are reported. These two examples illustrate the application of synchrotron x-ray techniques for oxidation, passivation, and dissolution of metals and semiconductors.

  2. Nitric oxide levels in the anterior chamber of vitrectomized eyes with silicon oil

    Directory of Open Access Journals (Sweden)

    Paulo Escarião

    2013-10-01

    Full Text Available PURPOSE: To investigate the nitric oxide levels in the anterior chamber of eyes who underwent pars plana vitrectomy (PPV with silicone oil. METHODS: Patients who underwent PPV with silicon oil injection, from february 2005 to august 2007, were selected. Nine patients (nine eyes participated in the study (five women and four men. Nitric oxide concentration was quantified after the aspiration of aqueous humor samples during the procedure of silicon oil removal. Data such as: oil emulsification; presence of oil in the anterior chamber; intraocular pressure and time with silicone oil were evaluated. Values of p <0.05 were considered to be statistically significant. RESULTS: A positive correlation between nitric oxide concentration and time with silicon oil in the vitreous cavity (r=0.799 was observed. The nitric oxide concentration was significantly higher (p=0.02 in patients with silicon oil more than 24 months (0.90µmol/ml ± 0.59, n=3 in the vitreous cavity comparing to patients with less than 24 months (0.19µmol/ml ± 0.10, n=6. CONCLUSION: A positive correlation linking silicone oil time in the vitreous cavity with the nitric oxide concentration in the anterior chamber was observed.

  3. Role of atomic layer deposited aluminum oxide as oxidation barrier for silicon based materials

    Energy Technology Data Exchange (ETDEWEB)

    Fiorentino, Giuseppe, E-mail: g.fiorentino@tudelft.nl; Morana, Bruno [Department of Microelectronic, Delft University of Technology, Feldmannweg 17, 2628 CT Delft (Netherlands); Forte, Salvatore [Department of Electronic, University of Naples Federico II, Piazzale Tecchio, 80125 Napoli (Italy); Sarro, Pasqualina Maria [Department of Microelectronic, Delft University of Technology, Feldmannweg 17, 2628 CT, Delft (Netherlands)

    2015-01-15

    In this paper, the authors study the protective effect against oxidation of a thin layer of atomic layer deposited (ALD) aluminum oxide (Al{sub 2}O{sub 3}). Nitrogen doped silicon carbide (poly-SiC:N) based microheaters coated with ALD Al{sub 2}O{sub 3} are used as test structure to investigate the barrier effect of the alumina layers to oxygen and water vapor at very high temperature (up to 1000 °C). Different device sets have been fabricated changing the doping levels, to evaluate possible interaction between the dopants and the alumina layer. The as-deposited alumina layer morphology has been evaluated by means of AFM analysis and compared to an annealed sample (8 h at 1000 °C) to estimate the change in the grain structure and the film density. The coated microheaters are subjected to very long oxidation time in dry and wet environment (up to 8 h at 900 and 1000 °C). By evaluating the electrical resistance variation between uncoated reference devices and the ALD coated devices, the oxide growth on the SiC is estimated. The results show that the ALD alumina coating completely prevents the oxidation of the SiC up to 900 °C in wet environment, while an oxide thickness reduction of 50% is observed at 1000 °C compared to uncoated devices.

  4. Etched ion tracks in silicon oxide and silicon oxynitride as charge injection or extraction channels for novel electronic structures

    International Nuclear Information System (INIS)

    Fink, D.; Petrov, A.V.; Hoppe, K.; Fahrner, W.R.; Papaleo, R.M.; Berdinsky, A.S.; Chandra, A.; Chemseddine, A.; Zrineh, A.; Biswas, A.; Faupel, F.; Chadderton, L.T.

    2004-01-01

    The impact of swift heavy ions onto silicon oxide and silicon oxynitride on silicon creates etchable tracks in these insulators. After their etching and filling-up with highly resistive matter, these nanometric pores can be used as charge extraction or injection paths towards the conducting channel in the underlying silicon. In this way, a novel family of electronic structures has been realized. The basic characteristics of these 'TEMPOS' (=tunable electronic material with pores in oxide on silicon) structures are summarized. Their functionality is determined by the type of insulator, the etch track diameters and lengths, their areal densities, the type of conducting matter embedded therein, and of course by the underlying semiconductor and the contact geometry. Depending on the TEMPOS preparation recipe and working point, the structures may resemble gatable resistors, condensors, diodes, transistors, photocells, or sensors, and they are therefore rather universally applicable in electronics. TEMPOS structures are often sensitive to temperature, light, humidity and organic gases. Also light-emitting TEMPOS structures have been produced. About 37 TEMPOS-based circuits such as thermosensors, photosensors, humidity and alcohol sensors, amplifiers, frequency multipliers, amplitude modulators, oscillators, flip-flops and many others have already been designed and successfully tested. Sometimes TEMPOS-based circuits are more compact than conventional electronics

  5. Electrical properties improvement of multicrystalline silicon solar cells using a combination of porous silicon and vanadium oxide treatment

    International Nuclear Information System (INIS)

    Derbali, L.; Ezzaouia, H.

    2013-01-01

    In this paper, we will report the enhancement of the conversion efficiency of multicrystalline silicon solar cells after coating the front surface with a porous silicon layer treated with vanadium oxide. The incorporation of vanadium oxide into the porous silicon (PS) structure, followed by a thermal treatment under oxygen ambient, leads to an important decrease of the surface reflectivity, a significant enhancement of the effective minority carrier lifetime (τ eff ) and a significant enhancement of the photoluminescence (PL) of the PS structure. We Obtained a noticeable increase of (τ eff ) from 3.11 μs to 134.74 μs and the surface recombination velocity (S eff ) have decreased from 8441 cm s −1 to 195 cm s −1 . The reflectivity spectra of obtained films, performed in the 300–1200 nm wavelength range, show an important decrease of the average reflectivity from 40% to 5%. We notice a significant improvement of the internal quantum efficiency (IQE) in the used multicrystalline silicon substrates. Results are analyzed and compared to those carried out on a reference (untreated) sample. The electrical properties of the treated silicon solar cells were improved noticeably as regard to the reference (untreated) sample.

  6. Alternative method for steam generation for thermal oxidation of silicon

    Science.gov (United States)

    Spiegelman, Jeffrey J.

    2010-02-01

    Thermal oxidation of silicon is an important process step in MEMS device fabrication. Thicker oxide layers are often used as structural components and can take days or weeks to grow, causing high gas costs, maintenance issues, and a process bottleneck. Pyrolytic steam, which is generated from hydrogen and oxygen combustion, was the default process, but has serious drawbacks: cost, safety, particles, permitting, reduced growth rate, rapid hydrogen consumption, component breakdown and limited steam flow rates. Results from data collected over a 24 month period by a MEMS manufacturer supports replacement of pyrolytic torches with RASIRC Steamer technology to reduce process cycle time and enable expansion previously limited by local hydrogen permitting. Data was gathered to determine whether Steamers can meet or exceed pyrolytic torch performance. The RASIRC Steamer uses de-ionized water as its steam source, eliminating dependence on hydrogen and oxygen. A non-porous hydrophilic membrane selectively allows water vapor to pass. All other molecules are greatly restricted, so contaminants in water such as dissolved gases, ions, total organic compounds (TOC), particles, and metals can be removed in the steam phase. The MEMS manufacturer improved growth rate by 7% over the growth range from 1μm to 3.5μm. Over a four month period, wafer uniformity, refractive index, wafer stress, and etch rate were tracked with no significant difference found. The elimination of hydrogen generated a four-month return on investment (ROI). Mean time between failure (MTBF) was increased from 3 weeks to 32 weeks based on three Steamers operating over eight months.

  7. Nafion/Silicon Oxide Composite Membrane for High Temperature Proton Exchange Membrane Fuel Cell

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    Nafion/Silicon oxide composite membranes were produced via in situ sol-gel reaction of tetraethylorthosilicate (TEOS) in Nafion membranes. The physicochemical properties of the membranes were studied by FT-IR, TG-DSC and tensile strength. The results show that the silicon oxide is compatible with the Nafion membrane and the thermo stability of Nafion/Silicon oxide composite membrane is higher than that of Nafion membrane. Furthermore, the tensile strength of Nafion/Silicon oxide composite membrane is similar to that of the Nafion membrane. The proton conductivity of Nafion/Silicon oxide composite membrane is higher than that of Nafion membrane. When the Nafion/Silicon oxide composite membrane was employed as an electrolyte in H2/O2 PEMFC, a higher current density value (1 000 mA/cm2 at 0.38 V) than that of the Nafion 1135 membrane (100 mA/cm2 at 0.04 V) was obtained at 110 ℃.

  8. About the optical properties of oxidized black silicon structures

    Science.gov (United States)

    Pincik, E.; Brunner, R.; Kobayashi, H.; Mikula, M.; Kučera, M.; Švec, P.; Greguš, J.; Vojtek, P.; Zábudlá, Z.; Imamura, K.; Zahoran, M.

    2017-02-01

    The paper deals with the optical and morphological properties of thermally oxidized black silicon (OBSi) nano-crystalline specimens produced by the surface structure chemical transfer method (SSCT). This method can produce a nano-crystalline Si black color layer on c-Si with a range of thickness of ∼50 nm to ∼300 nm by the contact of c-Si immersed in chemical solutions HF + H2O2 with a catalytic mesh. We present and discuss mainly the photoluminescence properties of both polished c-Si and OBSi structures, respectively. The similar photoluminescence (PL) behaviors recorded at liquid helium (6 K) and room temperatures on both polished crystalline Si and OBSi samples, respectively, indicate the similar origin of recorded luminescence light. As the positions of PL maxima of OBSi structures are mainly related to the size of Si nanocrystallites and SiO(x), we therefore suppose that the size of the dominant parts of the luminated OBSi nanostructure is pre-determined by the used polishing Si procedure, and/or the distribution function of the number of formed crystallites on their size is very similar. The blue shift of both PL spectra reaching almost value of 0.40 eV observed after the decrease of the sample temperature to 6 K we relate also with the change of the semiconductor band gap width.

  9. Process for depositing an oxide epitaxially onto a silicon substrate and structures prepared with the process

    Science.gov (United States)

    McKee, Rodney A.; Walker, Frederick J.

    1993-01-01

    A process and structure involving a silicon substrate utilizes an ultra high vacuum and molecular beam epitaxy (MBE) methods to grow an epitaxial oxide film upon a surface of the substrate. As the film is grown, the lattice of the compound formed at the silicon interface becomes stabilized, and a base layer comprised of an oxide having a sodium chloride-type lattice structure grows epitaxially upon the compound so as to cover the substrate surface. A perovskite may then be grown epitaxially upon the base layer to render a product which incorporates silicon, with its electronic capabilities, with a perovskite having technologically-significant properties of its own.

  10. Role of masking oxide on silicon in processes of defect generation at formation of SIMOX structures

    CERN Document Server

    Askinazi, A Y; Miloglyadova, L V

    2002-01-01

    One investigated into Si-SiO sub 2 structures formed by implantation of oxygen ions into silicon (SIMOX-technology) by means of techniques based on measuring of high-frequency volt-farad characteristics and by means of electroluminescence. One determined existence of electrically active centres and of luminescence centres in the formed oxide layer near boundary with silicon. One clarified the role SiO sub 2 masking layer in silicon in defect generation under formation of the masked oxide layer. One established dependence of concentration of electrically active and luminescence centres on thickness of masking layer

  11. Substoichiometric extraction of traces of gold and palladium

    International Nuclear Information System (INIS)

    Colonat, J.-F.

    1975-01-01

    Several systems for extracting palladium at concentrations ranging from 10 -4 to 10 -6 M/l were studied. Extraction by dithizone is limited by the transformation of the primary complex into a secondary complex which takes place at concentrations around 10 -6 M. This transformation has been demonstrated kinetically. Dimethylglyoxime is an interesting reagent in substoichiometry, in spite of its comparatively low extraction constant. Various complexes which are formed in a highly chlorinated medium have been proposed. Use of copper diethyldithiocarbamate is limited principally by its stability in presence of chlorine ions. The kinetic formation of palladium diethyldithiocarbamate has been studied with greater precision. A direct determination of 100μg of palladium in a copper matrix without preliminary separation has given results comparable in every way with those of other methods. In the case of gold (III) the constants of formation with the diethyldithiocarbamate ion have been determined by an iterative method of calculation, using the influence curves of interfering metals. Finally conditions for an automatization of the substoichiometric extraction, as well as its possibilities for gold determination in the range 200-20ppm, were proposed [fr

  12. Effect of additive gases and injection methods on chemical dry etching of silicon nitride, silicon oxynitride, and silicon oxide layers in F2 remote plasmas

    International Nuclear Information System (INIS)

    Yun, Y. B.; Park, S. M.; Kim, D. J.; Lee, N.-E.; Kim, K. S.; Bae, G. H.

    2007-01-01

    The authors investigated the effects of various additive gases and different injection methods on the chemical dry etching of silicon nitride, silicon oxynitride, and silicon oxide layers in F 2 remote plasmas. N 2 and N 2 +O 2 gases in the F 2 /Ar/N 2 and F 2 /Ar/N 2 /O 2 remote plasmas effectively increased the etch rate of the layers. The addition of direct-injected NO gas increased the etch rates most significantly. NO radicals generated by the addition of N 2 and N 2 +O 2 or direct-injected NO molecules contributed to the effective removal of nitrogen and oxygen in the silicon nitride and oxide layers, by forming N 2 O and NO 2 by-products, respectively, and thereby enhancing SiF 4 formation. As a result of the effective removal of the oxygen, nitrogen, and silicon atoms in the layers, the chemical dry etch rates were enhanced significantly. The process regime for the etch rate enhancement of the layers was extended at elevated temperature

  13. The effect of oxidation on the efficiency and spectrum of photoluminescence of porous silicon

    International Nuclear Information System (INIS)

    Bulakh, B. M.; Korsunska, N. E.; Khomenkova, L. Yu.; Staraya, T. R.; Sheinkman, M. K.

    2006-01-01

    The photoluminescence spectra of porous silicon and their temperature dependences and transformations on aging are studied. It is shown that the infrared band prevailing in the spectra of as-prepared samples is due to exciton recombination in silicon crystallites. On aging, a well-pronounced additional band is observed at shorter wavelengths of the spectra. It is assumed that this band is due to the recombination of carriers that are excited in silicon crystallites and recombine via some centers located in oxide. It is shown that the broad band commonly observable in oxidized porous silicon is a superposition of the above two bands. The dependences of the peak positions and integrated intensities of the bands on time and temperature are studied. The data on the distribution of oxide centers with depth in the porous layer are obtained

  14. 18O isotopic tracer studies of silicon oxidation in dry oxygen

    International Nuclear Information System (INIS)

    Han, C.J.

    1986-01-01

    Oxidation of silicon in dry oxygen has been an important process in the integrated circuit industry for making gate insulators on metal-oxide-semiconductory (MOS) devices. This work examines this process using isotopic tracers of oxygen to determine the transport mechanisms of oxygen through silicon dioxide. Oxides were grown sequentially using mass-16 and mass-18 oxygen gas sources to label the oxygen molecules from each step. The resulting oxides are analyzed using secondary ion mass spectrometry (SIMS). The results of these analyses suggest two oxidant species are present during the oxidation, each diffuses and oxidizes separately during the process. A model from this finding using a sum of two linear-parabolic growth rates, each representing the growth rate from one of the oxidants, describes the reported oxidation kinetics in the literature closely. A fit of this relationship reveals excellent fits to the data for oxide thicknesses ranging from 30 A to 1 μm and for temperatures ranging from 800 to 1200 0 C. The mass-18 oxygen tracers also enable a direct observation of the oxygen solubility in the silicon dioxide during a dry oxidation process. The SIMS profiles establish a maximum solubility for interstitial oxygen at 1000 0 C at 2 x 10 20 cm -3 . Furthermore, the mass-18 oxygen profiles show negligible network diffusion during an 1000 0 C oxidation

  15. Distribution of impurity elements in slag-silicon equilibria for oxidative refining of metallurgical silicon for solar cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Johnston, M.D.; Barati, M. [Department of Materials Science and Engineering, The University of Toronto, 184 College Street, Toronto, Ont. (Canada)

    2010-12-15

    The possibility of refining metallurgical grade silicon to a high-purity product for solar cell applications by the slagging of impurity elements was investigated. Distribution coefficients were determined for B, Ca, Mg, Fe, K and P between magnesia or alumina saturated Al{sub 2}O{sub 3}-CaO-MgO-SiO{sub 2} and Al{sub 2}O{sub 3}-BaO-SiO{sub 2} slags and silicon at 1500 C. The partitioning of the impurity elements between molten silicon and slag was examined in terms of basicity and oxygen potential of the slag, with particular focus on the behaviour of boron and phosphorus. The experimental results showed that both of these aspects of slag chemistry have a significant influence on the distribution coefficient of B and P. Increasing the oxygen potential by additions of silica was found to increase the distribution coefficients for both B and P. Increasing the basicity of the slag was not always effective in achieving high removal of these elements from silicon as excess amounts of basic oxides lower the activity of silica and consequently the oxygen potential. The extent of this effect is such that increasing basicity can lead to a decrease in distribution coefficient. Increasing lime in the slag increased distribution coefficients for B and P, but this counterbalancing effect was such that distributions were the lowest in barium-containing slags, despite barium oxide being the most basic of the fluxes used in this study. The highest removal efficiencies achieved were of the order of 80% and 90% for B and P, respectively. It was demonstrated that for the removal of B and P from metallurgical-grade silicon to solar-grade levels, a slag mass about 5 times the mass of silicon would be required. (author)

  16. Fabrication of a silicon oxide stamp by edge lithography reinforced with silicon nitride for nanoimprint lithography

    NARCIS (Netherlands)

    Zhao, Yiping; Berenschot, Johan W.; de Boer, M.; de Boer, Meint J.; Jansen, Henricus V.; Tas, Niels Roelof; Huskens, Jurriaan; Elwenspoek, Michael Curt

    2008-01-01

    The fabrication of a stamp reinforced with silicon nitride is presented for its use in nanoimprint lithography. The fabrication process is based on edge lithography using conventional optical lithography and wet anisotropic etching of 110 silicon wafers. SiO2 nano-ridges of 20 nm in width were

  17. Microstructure and oxidative degradation behavior of silicon carbide fiber Hi-Nicalon type S

    International Nuclear Information System (INIS)

    Takeda, M.; Urano, A.; Sakamoto, J.; Imai, Y.

    1998-01-01

    Polycarbosilane-derived SiC fibers, Nicalon, Hi-Nicalon, and Hi-Nicalon type S were exposed for 1 to 100 h at 1273-1773 K in air. Oxide layer growth and tensile strength change of these fibers were examined after the oxidation test. As a result, three types of SiC fibers decreased their strength as oxide layer thickness increased. Fracture origins were determined at near the oxide layer-fiber interface. Adhered fibers arised from softening of silicon oxide at high temperature were also observed. In this study, Hi-Nicalon type S showed better oxidation resistance than other polycarbosilane-derived SiC fibers after 1673 K or higher temperature exposure in air for 10 h. This result was explained by the poreless silicon oxide layer structure of Hi-Nicalon type S. (orig.)

  18. On the oxidation mechanism of microcrystalline silicon thin films studied by Fourier transform infrared spectroscopy

    NARCIS (Netherlands)

    Bronneberg, A. C.; Smets, A. H. M.; Creatore, M.; M. C. M. van de Sanden,

    2011-01-01

    Insight into the oxidation mechanism of microcrystalline silicon thin films has been obtained by means of Fourier transform infrared spectroscopy. The films were deposited by using the expanding thermal plasma and their oxidation upon air exposure was followed in time. Transmission spectra were

  19. Super-oxidation of silicon nanoclusters: magnetism and reactive oxygen species at the surface

    Energy Technology Data Exchange (ETDEWEB)

    Lepeshkin, Sergey; Baturin, Vladimir; Tikhonov, Evgeny; Matsko, Nikita; Uspenskii, Yurii; Naumova, Anastasia; Feya, Oleg; Schoonen, Martin A.; Oganov, Artem R.

    2016-01-01

    Oxidation of silicon nanoclusters depending on the temperature and oxygen pressure is explored from first principles using the evolutionary algorithm, and structural and thermodynamic analysis. From our calculations of 90 SinOm clusters we found that under normal conditions oxidation does not stop at the stoichiometric SiO2 composition, as it does in bulk silicon, but goes further placing extra oxygen atoms on the cluster surface. These extra atoms are responsible for light emission, relevant to reactive oxygen species and many of them are magnetic. We argue that the super-oxidation effect is size-independent and discuss its relevance to nanotechnology and miscellaneous applications, including biomedical ones.

  20. Fabrication of amorphous silicon nanoribbons by atomic force microscope tip-induced local oxidation for thin film device applications

    International Nuclear Information System (INIS)

    Pichon, L; Rogel, R; Demami, F

    2010-01-01

    We demonstrate the feasibility of induced local oxidation of amorphous silicon by atomic force microscopy. The resulting local oxide is used as a mask for the elaboration of a thin film silicon resistor. A thin amorphous silicon layer deposited on a glass substrate is locally oxidized following narrow continuous lines. The corresponding oxide line is then used as a mask during plasma etching of the amorphous layer leading to the formation of a nanoribbon. Such an amorphous silicon nanoribbon is used for the fabrication of the resistor

  1. Effect of yttrium on the oxide scale adherence of pre-oxidized silicon-containing heat-resistant alloy

    International Nuclear Information System (INIS)

    Yan Jingbo; Gao Yimin; Shen Yudi; Yang Fang; Yi Dawei; Ye Zhaozhong; Liang Long; Du Yingqian

    2011-01-01

    Highlights: → AE experiment shows yttrium has a beneficial effect on the pre-oxidized HP40 alloy. → Yttrium facilitates the formation of internal oxide after 10 h of oxidation. → Internal oxide changes the rupture behaviour of the oxide scale. → Twins form in the internal oxide and improve the binding strength of the scale. - Abstract: This paper investigates the effect of the rare earth element yttrium on the rupture behaviour of the oxide scale on the silicon-containing heat-resistant alloy during cooling. After 10 h of oxidation, yttrium is found to facilitate the formation of internal oxides (silica) at the scale-matrix interface. Due to the twinning observed by scanning transmission electron microscopy (STEM) in silica, the critical strain value for the scale failure can be dramatically improved, and the formation of cracks at the scale-matrix interface is inhibited.

  2. Effect of trichloroethylene enhancement on deposition rate of low-temperature silicon oxide films by silicone oil and ozone

    Science.gov (United States)

    Horita, Susumu; Jain, Puneet

    2017-08-01

    A low-temperature silcon oxide film was deposited at 160 to 220 °C using an atmospheric pressure CVD system with silicone oil vapor and ozone gases. It was found that the deposition rate is markedly increased by adding trichloroethylene (TCE) vapor, which is generated by bubbling TCE solution with N2 gas flow. The increase is more than 3 times that observed without TCE, and any contamination due to TCE is hardly observed in the deposited Si oxide films from Fourier transform infrared spectra.

  3. The oxidation of titanium nitride- and silicon nitride-coated stainless steel in carbon dioxide environments

    International Nuclear Information System (INIS)

    Mitchell, D.R.G.; Stott, F.H.

    1992-01-01

    A study has been undertaken into the effects of thin titanium nitride and silicon nitride coatings, deposited by physical vapour deposition and chemical vapour deposition processes, on the oxidation resistance of 321 stainless steel in a simulated advanced gas-cooled reactor carbon dioxide environment for long periods at 550 o C and 700 o C under thermal-cycling conditions. The uncoated steel contains sufficient chromium to develop a slow-growing chromium-rich oxide layer at these temperatures, particularly if the surfaces have been machine-abraded. Failure of this layer in service allows formation of less protective iron oxide-rich scales. The presence of a thin (3-4 μm) titanium nitride coating is not very effective in increasing the oxidation resistance since the ensuing titanium oxide scale is not a good barrier to diffusion. Even at 550 o C, iron oxide-rich nodules are able to develop following relatively rapid oxidation and breakdown of the coating. At 700 o C, the coated specimens oxidize at relatively similar rates to the uncoated steel. A thin silicon nitride coating gives improved oxidation resistance, with both the coating and its slow-growing oxide being relatively electrically insulating. The particular silicon nitride coating studied here was susceptible to spallation on thermal cycling, due to an inherently weak coating/substrate interface. (Author)

  4. Preparation of highly aligned silicon oxide nanowires with stable intensive photoluminescence

    International Nuclear Information System (INIS)

    Duraia, El-Shazly M.; Mansurov, Z.A.; Tokmolden, S.; Beall, Gary W.

    2010-01-01

    In this work we report the successful formation of highly aligned vertical silicon oxide nanowires. The source of silicon was from the substrate itself without any additional source of silicon. X-ray measurement demonstrated that our nanowires are amorphous. Photoluminescence measurements were conducted through 18 months and indicated that there is a very good intensive emission peaks near the violet regions. The FTIR measurements indicated the existence of peaks at 463, 604, 795 and a wide peak at 1111 cm -1 and this can be attributed to Si-O-Si and Si-O stretching vibrations. We also report the formation of the octopus-like silicon oxide nanowires and the growth mechanism of these structures was discussed.

  5. Preparation of highly aligned silicon oxide nanowires with stable intensive photoluminescence

    Energy Technology Data Exchange (ETDEWEB)

    Duraia, El-Shazly M., E-mail: duraia_physics@yahoo.co [Suez Canal University, Faculty of Science, Physics Department, Ismailia (Egypt); Al-Farabi Kazakh National University, Almaty (Kazakhstan); Institute of Physics and Technology, 11 Ibragimov Street, 050032 Almaty (Kazakhstan); Mansurov, Z.A. [Al-Farabi Kazakh National University, Almaty (Kazakhstan); Tokmolden, S. [Institute of Physics and Technology, 11 Ibragimov Street, 050032 Almaty (Kazakhstan); Beall, Gary W. [Texas State University-San Marcos, Department of Chemistry and Biochemistry, 601 University Dr., San Marcos, TX 78666 (United States)

    2010-02-15

    In this work we report the successful formation of highly aligned vertical silicon oxide nanowires. The source of silicon was from the substrate itself without any additional source of silicon. X-ray measurement demonstrated that our nanowires are amorphous. Photoluminescence measurements were conducted through 18 months and indicated that there is a very good intensive emission peaks near the violet regions. The FTIR measurements indicated the existence of peaks at 463, 604, 795 and a wide peak at 1111 cm{sup -1} and this can be attributed to Si-O-Si and Si-O stretching vibrations. We also report the formation of the octopus-like silicon oxide nanowires and the growth mechanism of these structures was discussed.

  6. Sponge-like reduced graphene oxide/silicon/carbon nanotube composites for lithium ion batteries

    Science.gov (United States)

    Fang, Menglu; Wang, Zhao; Chen, Xiaojun; Guan, Shiyou

    2018-04-01

    Three-dimensional sponge-like reduced graphene oxide/silicon/carbon nanotube composites were synthesized by one-step hydrothermal self-assembly using silicon nanoparticles, graphene oxide and amino modified carbon nanotubes to develop high-performance anode materials of lithium ion batteries. Scanning electron microscopy and transmission electron microscopy images show the structure of composites that Silicon nanoparticles are coated with reduced graphene oxide while amino modified carbon nanotubes wrap around the reduced graphene oxide in the composites. When applied to lithium ion battery, these composites exhibit high initial specific capacity of 2552 mA h/g at a current density of 0.05 A/g. In addition, reduced graphene oxide/silicon/carbon nanotube composites also have better cycle stability than bare Silicon nanoparticles electrode with the specific capacity of 1215 mA h/g after 100 cycles. The three-dimension sponge-like structure not only ensures the electrical conductivity but also buffers the huge volume change, which has broad potential application in the field of battery.

  7. Covalent Surface Modification of Silicon Oxides with Alcohols in Polar Aprotic Solvents.

    Science.gov (United States)

    Lee, Austin W H; Gates, Byron D

    2017-09-05

    Alcohol-based monolayers were successfully formed on the surfaces of silicon oxides through reactions performed in polar aprotic solvents. Monolayers prepared from alcohol-based reagents have been previously introduced as an alternative approach to covalently modify the surfaces of silicon oxides. These reagents are readily available, widely distributed, and are minimally susceptible to side reactions with ambient moisture. A limitation of using alcohol-based compounds is that previous reactions required relatively high temperatures in neat solutions, which can degrade some alcohol compounds or could lead to other unwanted side reactions during the formation of the monolayers. To overcome these challenges, we investigate the condensation reaction of alcohols on silicon oxides carried out in polar aprotic solvents. In particular, propylene carbonate has been identified as a polar aprotic solvent that is relatively nontoxic, readily accessible, and can facilitate the formation of alcohol-based monolayers. We have successfully demonstrated this approach for tuning the surface chemistry of silicon oxide surfaces with a variety of alcohol containing compounds. The strategy introduced in this research can be utilized to create silicon oxide surfaces with hydrophobic, oleophobic, or charged functionalities.

  8. Recovery of indium-tin-oxide/silicon heterojunction solar cells by thermal annealing

    OpenAIRE

    Morales Vilches, Ana Belén; Voz Sánchez, Cristóbal; Colina Brito, Mónica Alejandra; López Rodríguez, Gema; Martín García, Isidro; Ortega Villasclaras, Pablo Rafael; Orpella García, Alberto; Alcubilla González, Ramón

    2014-01-01

    The emitter of silicon heterojunction solar cells consists of very thin hydrogenated amorphous silicon layers deposited at low temperature. The high sheet resistance of this type of emitter requires a transparent conductive oxide layer, which also acts as an effective antireflection coating. The deposition of this front electrode, typically by Sputtering, involves a relatively high energy ion bombardment at the surface that could degrade the emitter quality. The work function of the tra...

  9. Stressing effects on the charge trapping of silicon oxynitride prepared by thermal oxidation of LPCVD Si-rich silicon nitride

    International Nuclear Information System (INIS)

    Choi, H.Y.; Wong, H.; Filip, V.; Sen, B.; Kok, C.W.; Chan, M.; Poon, M.C.

    2006-01-01

    It was recently found that the silicon oxynitride prepared by oxidation of silicon-rich silicon nitride (SRN) has several important features. The high nitrogen and extremely low hydrogen content of this material allows it to have a high dielectric constant and a low trap density. The present work investigates in further detail the electrical reliability of this kind of gate dielectric films by studying the charge trapping and interface state generation induced by constant current stressing. Capacitance-voltage (C-V) measurements indicate that for oxidation temperatures of 850 and 950 deg. C, the interface trap generation is minimal because of the high nitrogen content at the interface. At a higher oxidation temperature of 1050 deg. C, a large flatband shift is found for constant current stressing. This observation can be explained by the significant reduction of the nitrogen content and the phase separation effect at this temperature as found by X-ray photoelectron spectroscopy study. In addition to the high nitrogen content, the Si atoms at the interface exist in the form of random bonding to oxygen and nitrogen atoms for samples oxidized at 850 and 950 deg. C. This structure reduces the interface bonding constraint and results in the low interface trap density. For heavily oxidized samples the trace amount of interface nitrogen atoms exist in the form of a highly constraint SiN 4 phase and the interface oxynitride layer is a random mixture of SiO 4 and SiN 4 phases, which consequently reduces the reliability against high energy electron stressing

  10. High aspect ratio silicon nanomoulds for UV embossing fabricated by directional thermal oxidation using an oxidation mask

    International Nuclear Information System (INIS)

    Chen, L Q; Chan-Park, Mary B; Yan, Y H; Zhang Qing; Li, C M; Zhang Jun

    2007-01-01

    Nanomoulding is simple and economical but moulds with nanoscale features are usually prohibitively expensive to fabricate because nanolithographic techniques are mostly serial and time-consuming for large-area patterning. This paper describes a novel, simple and inexpensive parallel technique for fabricating nanoscale pattern moulds by silicon etching followed by thermal oxidation. The mask pattern can be made by direct photolithography or photolithography followed by metal overetching for submicron- and nanoscale features, respectively. To successfully make nanoscale channels having a post-oxidation cross-sectional shape similar to that of the original channel, an oxidation mask to promote unidirectional (specifically horizontal) oxide growth is found to be essential. A silicon nitride or metal mask layer prevents vertical oxidation of the Si directly beneath it. Without this mask, rectangular channels become smaller but are V-shaped after oxidation. By controlling the silicon etch depth and oxidation time, moulds with high aspect ratio channels having widths ranging from 500 to 50 nm and smaller can be obtained. The nanomould, when passivated with a Teflon-like layer, can be used for first-generation replication using ultraviolet (UV) nanoembossing and second-generation replication in other materials, such as polydimethylsiloxane (PDMS). The PDMS stamp, which was subsequently coated with Au, was used for transfer printing of Au electrodes with a 600 nm gap which will find applications in plastics nanoelectronics

  11. Designing high performance precursors for atomic layer deposition of silicon oxide

    Energy Technology Data Exchange (ETDEWEB)

    Mallikarjunan, Anupama, E-mail: mallika@airproducts.com; Chandra, Haripin; Xiao, Manchao; Lei, Xinjian; Pearlstein, Ronald M.; Bowen, Heather R.; O' Neill, Mark L. [Air Products and Chemicals, Inc., 1969 Palomar Oaks Way, Carlsbad, California 92011 (United States); Derecskei-Kovacs, Agnes [Air Products and Chemicals, Inc., 7201 Hamilton Blvd., Allentown, Pennsylvania 18195 (United States); Han, Bing [Air Products and Chemicals, Inc., 2 Dongsanhuan North Road, Chaoyang District, Beijing 100027 (China)

    2015-01-15

    Conformal and continuous silicon oxide films produced by atomic layer deposition (ALD) are enabling novel processing schemes and integrated device structures. The increasing drive toward lower temperature processing requires new precursors with even higher reactivity. The aminosilane family of precursors has advantages due to their reactive nature and relative ease of use. In this paper, the authors present the experimental results that reveal the uniqueness of the monoaminosilane structure [(R{sub 2}N)SiH{sub 3}] in providing ultralow temperature silicon oxide depositions. Disubstituted aminosilanes with primary amines such as in bis(t-butylamino)silane and with secondary amines such as in bis(diethylamino)silane were compared with a representative monoaminosilane: di-sec-butylaminosilane (DSBAS). DSBAS showed the highest growth per cycle in both thermal and plasma enhanced ALD. These findings show the importance of the arrangement of the precursor's organic groups in an ALD silicon oxide process.

  12. Electronic structure of indium-tungsten-oxide alloys and their energy band alignment at the heterojunction to crystalline silicon

    Science.gov (United States)

    Menzel, Dorothee; Mews, Mathias; Rech, Bernd; Korte, Lars

    2018-01-01

    The electronic structure of thermally co-evaporated indium-tungsten-oxide films is investigated. The stoichiometry is varied from pure tungsten oxide to pure indium oxide, and the band alignment at the indium-tungsten-oxide/crystalline silicon heterointerface is monitored. Using in-system photoelectron spectroscopy, optical spectroscopy, and surface photovoltage measurements, we show that the work function of indium-tungsten-oxide continuously decreases from 6.3 eV for tungsten oxide to 4.3 eV for indium oxide, with a concomitant decrease in the band bending at the hetero interface to crystalline silicon than indium oxide.

  13. The effect of oxidation on physical properties of porous silicon layers for optical applications

    Energy Technology Data Exchange (ETDEWEB)

    Pirasteh, Parasteh [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France); Charrier, Joel [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France)]. E-mail: joel.charrier@univ-rennes1.fr; Soltani, Ali [Institut d' Electronique, de Microemectronique et de Nanotechnologie, CNRS-UMR 8520, Cite Scientifique Avenue Poincare, BP 69, 59652 Villeneuve d' Ascq Cedex (France); Haesaert, Severine [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France); Haji, Lazhar [Laboratoire d' Optronique, CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT Tecnhopole Anticipa, 6 rue de Kerampont, BP 447, 22305 Lannion Cedex (France); Godon, Christine [Laboratoire de Physique Crystalline, Institut des Materiaux Jean Rouxel, 44322 Nantes Cedex 3 (France); Errien, Nicolas [Laboratoire de Physique Crystalline, Institut des Materiaux Jean Rouxel, 44322 Nantes Cedex 3 (France)

    2006-12-15

    In order to understand the optical loss mechanisms in porous silicon based waveguides, structural and optical studies have been performed. Scanning and transmission electron microscopic observations of porous silicon layers are obtained before and after an oxidation process at high temperature in wet O{sub 2}. Pore size and shape of heavily p-type doped Si wafers are estimated and correlated to the optical properties of the material before and after oxidation. The refractive index was measured and compared to that determined by the Bruggeman model.

  14. Lithium-storage Properties of Gallic Acid-Reduced Graphene Oxide and Silicon-Graphene Composites

    International Nuclear Information System (INIS)

    Xu, Binghui; Zhang, Jintao; Gu, Yi; Zhang, Zhi; Al Abdulla, Wael; Kumar, Nanjundan Ashok; Zhao, X.S.

    2016-01-01

    Graphene oxide (GO) was de-oxygenated using gallic acid under mild conditions to prepare reduced graphene oxide (RGO). The resultant RGO showed a lithium-ion storage capacity of 1280 mA h g −1 at a current density of 200 mA g −1 after 350 cycles when used as an anode for lithium ion batteries. The RGO was further used to stabilize silicon (Si) nanoparticles to prepare silicon-graphene composite electrode materials. Experimental results showed that a composite electrode prepared with a mass ratio of Si:GO = 1:2 exhibited the best lithium ion storage performance.

  15. Surface texture of single-crystal silicon oxidized under a thin V{sub 2}O{sub 5} layer

    Energy Technology Data Exchange (ETDEWEB)

    Nikitin, S. E., E-mail: nikitin@mail.ioffe.ru; Verbitskiy, V. N.; Nashchekin, A. V.; Trapeznikova, I. N.; Bobyl, A. V.; Terukova, E. E. [Russian Academy of Sciences, Ioffe Physical–Technical Institute (Russian Federation)

    2017-01-15

    The process of surface texturing of single-crystal silicon oxidized under a V{sub 2}O{sub 5} layer is studied. Intense silicon oxidation at the Si–V{sub 2}O{sub 5} interface begins at a temperature of 903 K which is 200 K below than upon silicon thermal oxidation in an oxygen atmosphere. A silicon dioxide layer 30–50 nm thick with SiO{sub 2} inclusions in silicon depth up to 400 nm is formed at the V{sub 2}O{sub 5}–Si interface. The diffusion coefficient of atomic oxygen through the silicon-dioxide layer at 903 K is determined (D ≥ 2 × 10{sup –15} cm{sup 2} s{sup –1}). A model of low-temperature silicon oxidation, based on atomic oxygen diffusion from V{sub 2}O{sub 5} through the SiO{sub 2} layer to silicon, and SiO{sub x} precipitate formation in silicon is proposed. After removing the V{sub 2}O{sub 5} and silicon-dioxide layers, texture is formed on the silicon surface, which intensely scatters light in the wavelength range of 300–550 nm and is important in the texturing of the front and rear surfaces of solar cells.

  16. Influence of post-annealing on the electrical properties of metal/oxide/silicon nitride/oxide/silicon capacitors for flash memories

    International Nuclear Information System (INIS)

    Kim, Hee Dong; An, Ho-Myoung; Kim, Kyoung Chan; Seo, Yu Jeong; Kim, Tae Geun

    2008-01-01

    We report the effect of post-annealing on the electrical properties of metal/oxide/silicon nitride/oxide/silicon (MONOS) capacitors. Four samples, namely as-deposited and annealed at 750, 850 and 950 °C for 30 s in nitrogen ambient by a rapid thermal process, were prepared and characterized for comparison. The best performance with the largest memory window of 4.4 V and the fastest program speed of 10 ms was observed for the sample annealed at 850 °C. In addition, the highest traps density of 6.84 × 10 18 cm −3 was observed with ideal trap distributions for the same sample by capacitance–voltage (C–V) measurement. These results indicate that the memory traps in the ONO structure can be engineered by post-annealing to improve the electrical properties of the MONOS device

  17. Transparent conducting oxide layers for thin film silicon solar cells

    NARCIS (Netherlands)

    Rath, J.K.; Liu, Y.; de Jong, M.M.; de Wild, J.; Schuttauf, J.A.; Brinza, M.; Schropp, R.E.I.

    2009-01-01

    Texture etching of ZnO:1%Al layers using diluted HCl solution provides excellent TCOs with crater type surface features for the front contact of superstrate type of thin film silicon solar cells. The texture etched ZnO:Al definitely gives superior performance than Asahi SnO2:F TCO in case of

  18. Spectroellipsometric detection of silicon substrate damage caused by radiofrequency sputtering of niobium oxide

    Science.gov (United States)

    Lohner, Tivadar; Serényi, Miklós; Szilágyi, Edit; Zolnai, Zsolt; Czigány, Zsolt; Khánh, Nguyen Quoc; Petrik, Péter; Fried, Miklós

    2017-11-01

    Substrate surface damage induced by deposition of metal atoms by radiofrequency (rf) sputtering or ion beam sputtering onto single-crystalline silicon (c-Si) surface has been characterized earlier by electrical measurements. The question arises whether it is possible to characterize surface damage using spectroscopic ellipsometry (SE). In our experiments niobium oxide layers were deposited by rf sputtering on c-Si substrates in gas mixture of oxygen and argon. Multiple angle of incidence spectroscopic ellipsometry measurements were performed, a four-layer optical model (surface roughness layer, niobium oxide layer, native silicon oxide layer and ion implantation-amorphized silicon [i-a-Si] layer on a c-Si substrate) was created in order to evaluate the spectra. The evaluations yielded thicknesses of several nm for the i-a-Si layer. Better agreement could be achieved between the measured and the generated spectra by inserting a mixed layer (with components of c-Si and i-a-Si applying the effective medium approximation) between the silicon oxide layer and the c-Si substrate. High depth resolution Rutherford backscattering (RBS) measurements were performed to investigate the interface disorder between the deposited niobium oxide layer and the c-Si substrate. Atomic resolution cross-sectional transmission electron microscopy investigation was applied to visualize the details of the damaged subsurface region of the substrate.

  19. Silicon heterojunction solar cell passivation in combination with nanocrystalline silicon oxide emitters

    NARCIS (Netherlands)

    Gatz, H.A.; Rath, J.K.; Verheijen, M.A.; Kessels, W.M.M.; Schropp, R.E.I.

    2016-01-01

    Silicon heterojunction solar cells (SHJ) are well known for their high efficiencies, enabled by their remarkably high open-circuit voltages (VOC). A key factor in achieving these values is a good passivation of the crystalline wafer interface. One of the restrictions during SHJ solar cell production

  20. Room temperature NO2-sensing properties of porous silicon/tungsten oxide nanorods composite

    International Nuclear Information System (INIS)

    Wei, Yulong; Hu, Ming; Wang, Dengfeng; Zhang, Weiyi; Qin, Yuxiang

    2015-01-01

    Highlights: • Porous silicon/WO 3 nanorods composite is synthesized via hydrothermal method. • The morphology of WO 3 nanorods depends on the amount of oxalic acid (pH value). • The sensor can detect ppb level NO 2 at room temperature. - Abstract: One-dimensional single crystalline WO 3 nanorods have been successfully synthesized onto the porous silicon substrates by a seed-induced hydrothermal method. The controlled morphology of porous silicon/tungsten oxide nanorods composite was obtained by using oxalic acid as an organic inducer. The reaction was carried out at 180 °C for 2 h. The influence of oxalic acid (pH value) on the morphology of porous silicon/tungsten oxide nanorods composite was investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The NO 2 -sensing properties of the sensor based on porous silicon/tungsten oxide nanorods composite were investigated at different temperatures ranging from room temperature (∼25 °C) to 300 °C. At room temperature, the sensor behaved as a typical p-type semiconductor and exhibited high gas response, good repeatability and excellent selectivity characteristics toward NO 2 gas due to its high specific surface area, special structure, and large amounts of oxygen vacancies

  1. Determination of traces of iridium with thiodibenzoylmethane by substoichiometric isotope dilution analysis

    International Nuclear Information System (INIS)

    Roebisch, G.; Bansse, W.; Ludwig, E.

    1980-01-01

    Iridium(III or IV) reacts with thiodibenzoylmethane on heating at pH 6 to form a 1:3 complex, which can be concentrated by extraction into chloroform. Based on this reaction, a reproducible, selective determination of iridium is achieved by means of substoichiometric isotope dilution analysis, based on 192 Ir. The linear range is 1-11 nmol of iridium. (Auth.)

  2. Fluorescence and thermoluminescence in silicon oxide films rich in silicon; Fluorescencia y termoluminiscencia en peliculas de oxido de silicio rico en silicio

    Energy Technology Data Exchange (ETDEWEB)

    Berman M, D.; Piters, T. M. [Centro de Investigacion en Fisica, Universidad de Sonora, Apdo. Postal 5-088, Hermosillo 83190, Sonora (Mexico); Aceves M, M.; Berriel V, L. R. [Instituto Nacional de Astrofisica, Optica y Electronica, Apdo. Postal 51, Puebla 72000, Puebla (Mexico); Luna L, J. A. [CIDS, Benemerita Universidad Autonoma de Puebla, Apdo. Postal 1651, Puebla 72000, Puebla (Mexico)

    2009-10-15

    In this work we determined the fluorescence and thermoluminescence (TL) creation spectra of silicon rich oxide films (SRO) with three different silicon excesses. To study the TL of SRO, 550 nm of SRO film were deposited by Low Pressure Chemical Vapor Deposition technique on N-type silicon substrates with resistivity in the order of 3 to 5 {omega}-cm with silicon excess controlled by the ratio of the gases used in the process, SRO films with Ro= 10, 20 and 30 (12-6% silicon excess) were obtained. Then, they were thermally treated in N{sub 2} at high temperatures to diffuse and homogenize the silicon excess. In the fluorescence spectra two main emission regions are observed, one around 400 nm and one around 800 nm. TL creation spectra were determined by plotting the integrated TL intensity as function of the excitation wavelength. (Author)

  3. Heterojunction Solar Cells Based on Silicon and Composite Films of Graphene Oxide and Carbon Nanotubes.

    Science.gov (United States)

    Yu, LePing; Tune, Daniel; Shearer, Cameron; Shapter, Joseph

    2015-09-07

    Graphene oxide (GO) sheets have been used as the surfactant to disperse single-walled carbon nanotubes (CNT) in water to prepare GO/CNT electrodes that are applied to silicon to form a heterojunction that can be used in solar cells. GO/CNT films with different ratios of the two components and with various thicknesses have been used as semitransparent electrodes, and the influence of both factors on the performance of the solar cell has been studied. The degradation rate of the GO/CNT-silicon devices under ambient conditions has also been explored. The influence of the film thickness on the device performance is related to the interplay of two competing factors, namely, sheet resistance and transmittance. CNTs help to improve the conductivity of the GO/CNT film, and GO is able to protect the silicon from oxidation in the atmosphere. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  4. Nanopatterning of Crystalline Silicon Using Anodized Aluminum Oxide Templates for Photovoltaics

    Science.gov (United States)

    Chao, Tsu-An

    A novel thin film anodized aluminum oxide templating process was developed and applied to make nanopatterns on crystalline silicon to enhance the optical properties of silicon. The thin film anodized aluminum oxide was created to improve the conventional thick aluminum templating method with the aim for potential large scale fabrication. A unique two-step anodizing method was introduced to create high quality nanopatterns and it was demonstrated that this process is superior over the original one-step approach. Optical characterization of the nanopatterned silicon showed up to 10% reduction in reflection in the short wavelength range. Scanning electron microscopy was also used to analyze the nanopatterned surface structure and it was found that interpore spacing and pore density can be tuned by changing the anodizing potential.

  5. Ellipsometry measurements of thickness of oxide and water layers on spherical and flat silicon surfaces

    International Nuclear Information System (INIS)

    Kenny, M.J.; Netterfield, R.; Wielunski, L.S.

    1998-01-01

    Full text: Ellipsometry has been used to measure the thickness of oxide layers on single crystal silicon surfaces, both flat and spherical and also to measure the extent of adsorption of moisture on the surface as a function of partial water vapour pressure. The measurements form part of an international collaborative project to make a precise determination of the Avogadro constant (ΔN A /N A -8 ) which will then be used to obtain an absolute definition of the kilogram, rather than one in terms of an artefact. Typically the native oxide layer on a cleaned silicon wafer is about 2 nm thick. On a polished sphere this oxide layer is typically 8 to 10 nm thick, the increased thickness being attributed to parameters related to the polishing process. Ellipsometry measurements on an 89 mm diameter polished silicon sphere at both VUW and CSIRO indicated a SiO 2 layer at 7 to 10 nm thick. It was observed that this thickness varied regularly. The crystal orientation of the sphere was determined using electron patterns generated from an electron microscope and the oxide layer was then measured through 180 arcs of great circles along (110) and (100) planes. It was observed that the thickness varied systematically with orientation. The minimum thickness was 7.4 nm at the axis (softest direction in silicon) and the greatest thickness was 9.5 nm at the axis (hardest direction in silicon). This is similar to an orientation dependent cubic pattern which has been observed to be superimposed on polished silicon spheres. At VUW, the sphere was placed in an evacuated bell jar and the ellipsometry signal was observed as the water vapour pressure was progressively increased up to saturation. The amount of water vapour adsorbed at saturation was one or two monolayers, indicating that the sphere does not wet

  6. Improved reaction sintered silicon nitride. [protective coatings to improve oxidation resistance

    Science.gov (United States)

    Baumgartner, H. R.

    1978-01-01

    Processing treatments were applied to as-nitrided reaction sintered silicon nitride (RSSN) with the purposes of improving strength after processing to above 350 MN/m2 and improving strength after oxidation exposure. The experimental approaches are divided into three broad classifications: sintering of surface-applied powders; impregnation of solution followed by further thermal processing; and infiltration of molten silicon and subsequent carburization or nitridation of the silicon. The impregnation of RSSN with solutions of aluminum nitrate and zirconyl chloride, followed by heating at 1400-1500 C in a nitrogen atmosphere containing silicon monoxide, improved RSSN strength and oxidation resistance. The room temperature bend strength of RSSN was increased nearly fifty percent above the untreated strength with mean absolute strengths up to 420 MN/m2. Strengths of treated samples that were measured after a 12 hour oxidation exposure in air were up to 90 percent of the original as-nitrided strength, as compared to retained strengths in the range of 35 to 60 percent for untreated RSSN after the same oxidation exposure.

  7. Recent progress in the development and understanding of silicon surface passivation by aluminum oxide for photovoltaics

    NARCIS (Netherlands)

    Dingemans, G.; Kessels, W.M.M.

    2010-01-01

    In the recent years, considerable progress has been made in the understanding of the unique silicon surface passivation properties of aluminum oxide (Al2O3) films including its underlying mechanisms. Containing a high fixed negative charge density located close to the Si interface, Al2O3 provides a

  8. Transmission Electron Microscopy Studies of Electron-Selective Titanium Oxide Contacts in Silicon Solar Cells

    KAUST Repository

    Ali, Haider; Yang, Xinbo; Weber, Klaus; Schoenfeld, Winston V.; Davis, Kristopher O.

    2017-01-01

    In this study, the cross-section of electron-selective titanium oxide (TiO2) contacts for n-type crystalline silicon solar cells were investigated by transmission electron microscopy. It was revealed that the excellent cell efficiency of 21

  9. Effects of Cl+ and F+ implantation of oxidation-induced stacking faults in silicon

    NARCIS (Netherlands)

    Xu, J.Y.; Bronsveld, P.M.; Boom, G.; Hosson, J.Th.M. De

    1984-01-01

    Three implantation effects were investigated in floating-zone-grown silicon: (a) the effect of Cl+ implantation resulting in the shrinkage of oxidation-induced stacking faults; (b) the effect of F+ implantation giving rise to defaulting of the 1/3 [111] Frank dislocations into 1/2[110] perfect

  10. Mechanical anomaly impact on metal-oxide-semiconductor capacitors on flexible silicon fabric

    KAUST Repository

    Ghoneim, Mohamed T.; Kutbee, Arwa T.; Ghodsi Nasseri, Seyed Faizelldin; Bersuker, G.; Hussain, Muhammad Mustafa

    2014-01-01

    We report the impact of mechanical anomaly on high-κ/metal-oxide-semiconductor capacitors built on flexible silicon (100) fabric. The mechanical tests include studying the effect of bending radius up to 5 mm minimum bending radius with respect

  11. Fabrication of disposable topographic silicon oxide from sawtoothed patterns: control of arrays of gold nanoparticles.

    Science.gov (United States)

    Cho, Heesook; Yoo, Hana; Park, Soojin

    2010-05-18

    Disposable topographic silicon oxide patterns were fabricated from polymeric replicas of sawtoothed glass surfaces, spin-coating of poly(dimethylsiloxane) (PDMS) thin films, and thermal annealing at certain temperature and followed by oxygen plasma treatment of the thin PDMS layer. A simple imprinting process was used to fabricate the replicated PDMS and PS patterns from sawtoothed glass surfaces. Next, thin layers of PDMS films having different thicknesses were spin-coated onto the sawtoothed PS surfaces and annealed at 60 degrees C to be drawn the PDMS into the valley of the sawtoothed PS surfaces, followed by oxygen plasma treatment to fabricate topographic silicon oxide patterns. By control of the thickness of PDMS layers, silicon oxide patterns having various line widths were fabricated. The silicon oxide topographic patterns were used to direct the self-assembly of polystyrene-block-poly(2-vinylpyridine) (PS-b-P2VP) block copolymer thin films via solvent annealing process. A highly ordered PS-b-P2VP micellar structure was used to let gold precursor complex with P2VP chains, and followed by oxygen plasma treatment. When the PS-b-P2VP thin films containing gold salts were exposed to oxygen plasma environments, gold salts were reduced to pure gold nanoparticles without changing high degree of lateral order, while polymers were completely degraded. As the width of trough and crest in topographic patterns increases, the number of gold arrays and size of gold nanoparticles are tuned. In the final step, the silicon oxide topographic patterns were selectively removed by wet etching process without changing the arrays of gold nanoparticles.

  12. Magnetic oxide heterostructures. EuO on cubic oxides and on silicon

    International Nuclear Information System (INIS)

    Caspers, Christian

    2013-01-01

    In the thesis at hand, we explore fundamental properties of ultrathin europium oxide (EuO) films. EuO is a model system of a localized 4f Heisenberg ferromagnet, in which the ferromagnetic coupling. provided a high crystalline quality. can be tuned by biaxial lattice strain. Moreover, the magnetic oxide EuO is perfectly suited as a spin-functional tunnel contact for silicon spintronics. However, up to now a challenging bulk and interface chemistry of EuO and Si has hampered a seamless integration into functional silicon heterostructures. In order to investigate fundamental aspects of the magnetic and electronic structure of ultrathin EuO, in the first part of this thesis, we synthesize EuO thin films on conductive YSZ substrates from bulklike thicknesses down to one nanometer by oxide molecular beam epitaxy (MBE). The EuO thin films are of textbook-like single-crystalline quality, and show bulk-like magnetic properties. We control the stoichiometry of buried EuO thin films by hard X-ray photoemission spectroscopy (HAXPES); even a 1 nm ultrathin EuO film exhibits no valence change or interface shifts. Furthermore, we conduct an advanced magnetic characterization by the magnetic circular dichroism (MCD) of Eu core-levels in photoemission, this gives us insight into the intra-atomic exchange coupling of EuO thin films. The MCD reveals large asymmetries of up to 49% in the well-resolved Eu 4d photoemission multiplet. Thus, ultrathin EuO coherently grown on conductive YSZ allows us to explore fundamental magnetic and electronic properties of a 4f magnetic oxide. Biaxial lateral strain applied to single-crystalline EuO is of fundamental interest, since it alters the electronic structure and magnetic coupling in a controlled way. We apply +4.2% tensile biaxial strain to EuO by epitaxial EuO/LaAlO 3 (100) heterostructures. EuO seamlessly adapts the lateral lattice parameter of LaAlO 3 , while the perpendicular parameter of EuO is the unchanged EuO bulk value, thus the

  13. High performance high-κ/metal gate complementary metal oxide semiconductor circuit element on flexible silicon

    KAUST Repository

    Sevilla, Galo T.

    2016-02-29

    Thinned silicon based complementary metal oxide semiconductor(CMOS)electronics can be physically flexible. To overcome challenges of limited thinning and damaging of devices originated from back grinding process, we show sequential reactive ion etching of silicon with the assistance from soft polymeric materials to efficiently achieve thinned (40 μm) and flexible (1.5 cm bending radius) silicon based functional CMOSinverters with high-κ/metal gate transistors. Notable advances through this study shows large area of silicon thinning with pre-fabricated high performance elements with ultra-large-scale-integration density (using 90 nm node technology) and then dicing of such large and thinned (seemingly fragile) pieces into smaller pieces using excimer laser. The impact of various mechanical bending and bending cycles show undeterred high performance of flexible siliconCMOSinverters. Future work will include transfer of diced silicon chips to destination site, interconnects, and packaging to obtain fully flexible electronic systems in CMOS compatible way.

  14. Coating of tips for electrochemical scanning tunneling microscopy by means of silicon, magnesium, and tungsten oxides

    Science.gov (United States)

    Salerno, Marco

    2010-09-01

    Different combinations of metal tips and oxide coatings have been tested for possible operation in electrochemical scanning tunneling microscopy. Silicon and magnesium oxides have been thermally evaporated onto gold and platinum-iridium tips, respectively. Two different thickness values have been explored for both materials, namely, 40 and 120 nm for silicon oxide and 20 and 60 nm for magnesium oxide. Alternatively, tungsten oxide has been grown on tungsten tips via electrochemical anodization. In the latter case, to seek optimal results we have varied the pH of the anodizing electrolyte between one and four. The oxide coated tips have been first inspected by means of scanning electron microscopy equipped with microanalysis to determine the morphological results of the coating. Second, the coated tips have been electrically characterized ex situ for stability in time by means of cyclic voltammetry in 1 M aqueous KCl supporting electrolyte, both bare and supplemented with K3[Fe(CN)6] complex at 10 mM concentration in milliQ water as an analyte. Only the tungsten oxide coated tungsten tips have shown stable electrical behavior in the electrolyte. For these tips, the uncoated metal area has been estimated from the electrical current levels, and they have been successfully tested by imaging a gold grating in situ, which provided stable results for several hours. The successful tungsten oxide coating obtained at pH=4 has been assigned to the WO3 form.

  15. Formation of silicon Oxide nano thickness on Si (III) with the assistance of Cs

    International Nuclear Information System (INIS)

    Bahari, A.; Bagheri, M.

    2006-01-01

    : The possibility of controlling the growth of a uniform ultra thin oxide on silicon via oxygen dosing at low temperatures, would be a great interest for the projected further development of nano electronics. One way to achieve this is to be able to control the conversion of chemically adsorbed oxygen and retained at room temperature into oxide during subsequent heating. Oxygen is chemisorbed at room temperature on Si(111) surface to saturation ( >100 L O 2 ), and the experimental chamber is then evacuated. This leaves adsorbed oxygen as atomically inserted on Si surface which sits on the back bonds. This surface is then used as a base for further processing which in one case consists of annealing to 600- 700 d eg C and subsequent exposures equivalent to the first step. This is repeated again. As the focus of this work, a series of experiments are done with adsorbed Cs, which assists in retaining oxygen and in transforming the adsorbed oxygen into oxide upon heating. It was found that the oxide formed on the surface at low coverage clusters. Without any external influence, the clusters may be made to coalesce upon further oxygen adsorption at room temperature, and annealing terminates as a continuous monolayer of amorphous oxide on top of a well-ordered silicon substrate. This configuration is inert to further uptake of oxygen. A higher oxide thickness could be obtained with Cs. Also in this case, the oxide growth saturates in an inert oxide Iayer

  16. The role of extra-atomic relaxation in determining Si2p binding energy shifts at silicon/silicon oxide interfaces

    International Nuclear Information System (INIS)

    Zhang, K.Z.; Greeley, J.N.; Banaszak Holl, M.M.; McFeely, F.R.

    1997-01-01

    The observed binding energy shift for silicon oxide films grown on crystalline silicon varies as a function of film thickness. The physical basis of this shift has previously been ascribed to a variety of initial state effects (Si endash O ring size, strain, stoichiometry, and crystallinity), final state effects (a variety of screening mechanisms), and extrinsic effects (charging). By constructing a structurally homogeneous silicon oxide film on silicon, initial state effects have been minimized and the magnitude of final state stabilization as a function of film thickness has been directly measured. In addition, questions regarding the charging of thin silicon oxide films on silicon have been addressed. From these studies, it is concluded that initial state effects play a negligible role in the thickness-dependent binding energy shift. For the first ∼30 Angstrom of oxide film, the thickness-dependent binding energy shift can be attributed to final state effects in the form of image charge induced stabilization. Beyond about 30 Angstrom, charging of the film occurs. copyright 1997 American Institute of Physics

  17. Oxidation Kinetics of Chemically Vapor-Deposited Silicon Carbide in Wet Oxygen

    Science.gov (United States)

    Opila, Elizabeth J.

    1994-01-01

    The oxidation kinetics of chemically vapor-deposited SiC in dry oxygen and wet oxygen (P(sub H2O) = 0.1 atm) at temperatures between 1200 C and 1400 C were monitored using thermogravimetric analysis. It was found that in a clean environment, 10% water vapor enhanced the oxidation kinetics of SiC only very slightly compared to rates found in dry oxygen. Oxidation kinetics were examined in terms of the Deal and Grove model for oxidation of silicon. It was found that in an environment containing even small amounts of impurities, such as high-purity Al2O3 reaction tubes containing 200 ppm Na, water vapor enhanced the transport of these impurities to the oxidation sample. Oxidation rates increased under these conditions presumably because of the formation of less protective sodium alumino-silicate scales.

  18. Anchoring of alkyl chain molecules on oxide surface using silicon alkoxide

    Energy Technology Data Exchange (ETDEWEB)

    Narita, Ayumi, E-mail: narita.ayumi@jaea.go.jp [Quantum Beam Science Directorate, Japan Atomic Energy Agency, Tokai-mura, Naka-gun, Ibaraki-ken 319-1195 (Japan); Graduate School of Science and Engineering, Ibaraki University, Bunnkyo, Mito-shi, Ibaraki-ken 310-8512 (Japan); Baba, Yuji; Sekiguchi, Tetsuhiro; Shimoyama, Iwao; Hirao, Norie [Quantum Beam Science Directorate, Japan Atomic Energy Agency, Tokai-mura, Naka-gun, Ibaraki-ken 319-1195 (Japan); Yaita, Tsuyoshi [Quantum Beam Science Directorate, Japan Atomic Energy Agency, Tokai-mura, Naka-gun, Ibaraki-ken 319-1195 (Japan); Graduate School of Science and Engineering, Ibaraki University, Bunnkyo, Mito-shi, Ibaraki-ken 310-8512 (Japan)

    2012-01-01

    Chemical states of the interfaces between octadecyl-triethoxy-silane (ODTS) molecules and sapphire surface were measured by X-ray photoelectron spectroscopy (XPS) and near edge X-ray absorption fine structure (NEXAFS) using synchrotron soft X-rays. The nearly self-assembled monolayer of ODTS was formed on the sapphire surface. For XPS and NEXAFS measurements, it was elucidated that the chemical bond between silicon alkoxide in ODTS and the surface was formed, and the alkane chain of ODTS locates upper side on the surface. As a result, it was elucidated that the silicon alkoxide is a good anchor for the immobilization of organic molecules on oxides.

  19. Participation of oxygen and carbon in formation of oxidation-induced stacking faults in monocrystalline silicon

    Directory of Open Access Journals (Sweden)

    Иван Федорович Червоный

    2015-11-01

    Full Text Available It is experimentally established, that density of oxidation-induced stacking faults (OISF in the boron doped monocrystalline silicon plates, that above, than it is more relation of oxygen atoms concentration to carbon atoms concentration in them.On research results of geometry of OISF rings in the different sections of single-crystal geometry of areas is reconstructed with their different closeness. At adjustment of the growing modes of single-crystals of silicon the increase of output of suitable product is observed

  20. Subattoampere current induced by single ions in silicon oxide layers of nonvolatile memory cells

    International Nuclear Information System (INIS)

    Cellere, G.; Paccagnella, A.; Larcher, L.; Visconti, A.; Bonanomi, M.

    2006-01-01

    A single ion impinging on a thin silicon dioxide layer generates a number of electron/hole pairs proportional to its linear energy transfer coefficient. Defects generated by recombination can act as a conductive path for electrons that cross the oxide barrier, thanks to a multitrap-assisted mechanism. We present data on the dependence of this phenomenon on the oxide thickness by using floating gate memory arrays. The tiny number of excess electrons stored in these devices allows for extremely high sensitivity, impossible with any direct measurement of oxide leakage current. Results are of particular interest for next generation devices

  1. Improved the Surface Roughness of Silicon Nanophotonic Devices by Thermal Oxidation Method

    Energy Technology Data Exchange (ETDEWEB)

    Shi Zujun; Shao Shiqian; Wang Yi, E-mail: ywangwnlo@mail.hust.edu.cn [Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, No. 1037, Luoyu Street, Wuhan 430074 (China)

    2011-02-01

    The transmission loss of the silicon-on-insulator (SOI) waveguide and the coupling loss of the SOI grating are determined to a large extent by the surface roughness. In order to obtain smaller loss, thermal oxidation is a good choice to reduce the surface roughness of the SOI waveguide and grating. Before the thermal oxidation, the root mean square of the surface roughness is over 11 nm. After the thermal oxidation, the SEM figure shows that the bottom of the grating is as smooth as quartz surface, while the AFM shows that the root mean square of the surface is less than 5 nm.

  2. Rate equation modelling of erbium luminescence dynamics in erbium-doped silicon-rich-silicon-oxide

    Energy Technology Data Exchange (ETDEWEB)

    Shah, Miraj, E-mail: m.shah@ee.ucl.ac.uk [Department of Electronic and Electrical Engineering, UCL, Torrington Place, London WC1E 7JE (United Kingdom); Wojdak, Maciej; Kenyon, Anthony J. [Department of Electronic and Electrical Engineering, UCL, Torrington Place, London WC1E 7JE (United Kingdom); Halsall, Matthew P.; Li, Hang; Crowe, Iain F. [Photon Science Institute and School of Electrical and Electronic Engineering, University of Manchester, Sackville St Building, Manchester M13 9PL (United Kingdom)

    2012-12-15

    Erbium doped silicon-rich silica offers broad band and very efficient excitation of erbium photoluminescence (PL) due to a sensitization effect attributed to silicon nanocrystals (Si-nc), which grow during thermal treatment. PL decay lifetime measurements of sensitised Er{sup 3+} ions are usually reported to be stretched or multi exponential, very different to those that are directly excited, which usually show a single exponential decay component. In this paper, we report on SiO{sub 2} thin films doped with Si-nc's and erbium. Time resolved PL measurements reveal two distinct 1.54 {mu}m Er decay components; a fast microsecond component, and a relatively long lifetime component (10 ms). We also study the structural properties of these samples through TEM measurements, and reveal the formation of Er clusters. We propose that these Er clusters are responsible for the fast {mu}s decay component, and we develop rate equation models that reproduce the experimental transient observations, and can explain some of the reported transient behaviour in previously published literature.

  3. The influence of oxidation properties on the electron emission characteristics of porous silicon

    Energy Technology Data Exchange (ETDEWEB)

    He, Li [Key Laboratory of Physical Electronics and Devices of the Ministry of Education, Xi’an Jiaotong University, Xi’an 710049 (China); Zhang, Xiaoning, E-mail: znn@mail.xjtu.edu.cn [Key Laboratory of Physical Electronics and Devices of the Ministry of Education, Xi’an Jiaotong University, Xi’an 710049 (China); Wang, Wenjiang [Key Laboratory of Physical Electronics and Devices of the Ministry of Education, Xi’an Jiaotong University, Xi’an 710049 (China); Wei, Haicheng [School of Electrical and Information Engineering, Beifang University of Nationalities, Yinchuan750021 (China)

    2016-09-30

    Highlights: • Evaluated the oxidation properties of porous silicon from semi-quantitative methods. • Discovered the relationship between oxidation properties and emission characteristics. • Revealed the micro-essence of the electron emission of the porous silicon. - Abstract: In order to investigate the influence of oxidation properties such as oxygen content and its distribution gradient on the electron emission characteristics of porous silicon (PS) emitters, emitters with PS thickness of 8 μm, 5 μm, and 3 μm were prepared and then oxidized by electrochemical oxidation (ECO) and ECO-RTO (rapid thermal oxidation) to get different oxidation properties. The experimental results indicated that the emission current density, efficiency, and stability of the PS emitters are mainly determined by oxidation properties. The higher oxygen content and the smaller oxygen distribution gradient in the PS layer, the larger emission current density and efficiency we noted. The most favorable results occurred for the PS emitter with the smallest oxygen distribution gradient and the highest level of oxygen content, with an emission current density of 212.25 μA/cm{sup 2} and efficiency of 59.21‰. Additionally, it also demonstrates that thick PS layer benefits to the emission stability due to its longer electron acceleration tunnel. The FN fitting plots indicated that the effective emission areas of PS emitters can be enlarged and electron emission thresholds is decreased because of the higher oxygen content and smaller distribution gradient, which were approved by the optical micrographs of top electrode of PS emitters before and after electron emission.

  4. The influence of oxidation properties on the electron emission characteristics of porous silicon

    International Nuclear Information System (INIS)

    He, Li; Zhang, Xiaoning; Wang, Wenjiang; Wei, Haicheng

    2016-01-01

    Highlights: • Evaluated the oxidation properties of porous silicon from semi-quantitative methods. • Discovered the relationship between oxidation properties and emission characteristics. • Revealed the micro-essence of the electron emission of the porous silicon. - Abstract: In order to investigate the influence of oxidation properties such as oxygen content and its distribution gradient on the electron emission characteristics of porous silicon (PS) emitters, emitters with PS thickness of 8 μm, 5 μm, and 3 μm were prepared and then oxidized by electrochemical oxidation (ECO) and ECO-RTO (rapid thermal oxidation) to get different oxidation properties. The experimental results indicated that the emission current density, efficiency, and stability of the PS emitters are mainly determined by oxidation properties. The higher oxygen content and the smaller oxygen distribution gradient in the PS layer, the larger emission current density and efficiency we noted. The most favorable results occurred for the PS emitter with the smallest oxygen distribution gradient and the highest level of oxygen content, with an emission current density of 212.25 μA/cm"2 and efficiency of 59.21‰. Additionally, it also demonstrates that thick PS layer benefits to the emission stability due to its longer electron acceleration tunnel. The FN fitting plots indicated that the effective emission areas of PS emitters can be enlarged and electron emission thresholds is decreased because of the higher oxygen content and smaller distribution gradient, which were approved by the optical micrographs of top electrode of PS emitters before and after electron emission.

  5. Substoichiometric extraction and quantification of cobalt with potassium salts of ethyl, propyl, butyl, pentyl and benzyl xanthates

    International Nuclear Information System (INIS)

    Chandrasekhar Reddy, P.; Rangamannar, B.; Prasad, K.S.S.

    1999-01-01

    A rapid and sensitive substoichiometric radiochemical procedure has been developed for the extraction of cobalt with potassium salts of ethyl, propyl, butyl, pentyl and benzyl xanthates. The relative extractabilities of the cobalt-xanthate complexes into chloroform and carbon tetrachloride were studied. Substoichiometric quantification methods were developed in each case and utilised to determine the cobalt content present in standard solutions as well as biological samples. (author)

  6. Oxidation-enhanced diffusion of boron in very low-energy N2+-implanted silicon

    Science.gov (United States)

    Skarlatos, D.; Tsamis, C.; Perego, M.; Fanciulli, M.

    2005-06-01

    In this article we study the interstitial injection during oxidation of very low-energy nitrogen-implanted silicon. Buried boron δ layers are used to monitor the interstitial supersaturation during the oxidation of nitrogen-implanted silicon. No difference in boron diffusivity enhancement was observed compared to dry oxidation of nonimplanted samples. This result is different from our experience from N2O oxynitridation study, during which a boron diffusivity enhancement of the order of 20% was observed, revealing the influence of interfacial nitrogen on interstitial kinetics. A possible explanation may be that implanted nitrogen acts as an excess interstitial sink in order to diffuse towards the surface via a non-Fickian mechanism. This work completes a wide study of oxidation of very low-energy nitrogen-implanted silicon related phenomena we performed within the last two years [D. Skarlatos, C. Tsamis, and D. Tsoukalas, J. Appl. Phys. 93, 1832 (2003); D. Skarlatos, E. Kapetanakis, P. Normand, C. Tsamis, M. Perego, S. Ferrari, M. Fanciulli, and D. Tsoukalas, J. Appl. Phys. 96, 300 (2004)].

  7. Characterization of Transition Metal Oxide/Silicon Heterojunctions for Solar Cell Applications

    Directory of Open Access Journals (Sweden)

    Luis G. Gerling

    2015-10-01

    Full Text Available During the last decade, transition metal oxides have been actively investigated as hole- and electron-selective materials in organic electronics due to their low-cost processing. In this study, four transition metal oxides (V2O5, MoO3, WO3, and ReO3 with high work functions (>5 eV were thermally evaporated as front p-type contacts in planar n-type crystalline silicon heterojunction solar cells. The concentration of oxygen vacancies in MoO3−x was found to be dependent on film thickness and redox conditions, as determined by X-ray Photoelectron Spectroscopy. Transfer length method measurements of oxide films deposited on glass yielded high sheet resistances (~109 Ω/sq, although lower values (~104 Ω/sq were measured for oxides deposited on silicon, indicating the presence of an inversion (hole rich layer. Of the four oxide/silicon solar cells, ReO3 was found to be unstable upon air exposure, while V2O5 achieved the highest open-circuit voltage (593 mV and conversion efficiency (12.7%, followed by MoO3 (581 mV, 12.6% and WO3 (570 mV, 11.8%. A short-circuit current gain of ~0.5 mA/cm2 was obtained when compared to a reference amorphous silicon contact, as expected from a wider energy bandgap. Overall, these results support the viability of a simplified solar cell design, processed at low temperature and without dopants.

  8. Microcrystalline silicon oxides for silicon-based solar cells: impact of the O/Si ratio on the electronic structure

    Science.gov (United States)

    Bär, M.; Starr, D. E.; Lambertz, A.; Holländer, B.; Alsmeier, J.-H.; Weinhardt, L.; Blum, M.; Gorgoi, M.; Yang, W.; Wilks, R. G.; Heske, C.

    2014-10-01

    Hydrogenated microcrystalline silicon oxide (μc-SiOx:H) layers are one alternative approach to ensure sufficient interlayer charge transport while maintaining high transparency and good passivation in Si-based solar cells. We have used a combination of complementary x-ray and electron spectroscopies to study the chemical and electronic structure of the (μc-SiOx:H) material system. With these techniques, we monitor the transition from a purely Si-based crystalline bonding network to a silicon oxide dominated environment, coinciding with a significant decrease of the material's conductivity. Most Si-based solar cell structures contain emitter/contact/passivation layers. Ideally, these layers fulfill their desired task (i.e., induce a sufficiently high internal electric field, ensure a good electric contact, and passivate the interfaces of the absorber) without absorbing light. Usually this leads to a trade-off in which a higher transparency can only be realized at the expense of the layer's ability to properly fulfill its task. One alternative approach is to use hydrogenated microcrystalline silicon oxide (μc-SiOx:H), a mixture of microcrystalline silicon and amorphous silicon (sub)oxide. The crystalline Si regions allow charge transport, while the oxide matrix maintains a high transparency. To date, it is still unclear how in detail the oxygen content influences the electronic structure of the μc-SiOx:H mixed phase material. To address this question, we have studied the chemical and electronic structure of the μc-SiOx:H (0 0.5, we observe a pronounced decrease of Si 3s - Si 3p hybridization in favor of Si 3p - O 2p hybridization in the upper valence band. This coincides with a significant increase of the material's resistivity, possibly indicating the breakdown of the conducting crystalline Si network. Silicon oxide layers with a thickness of several hundred nanometres were deposited in a PECVD (plasma-enhanced chemical vapor deposition) multi chamber system

  9. The effects of trichloroethane HCl and ion-implantation on the oxidation rate of silicon

    International Nuclear Information System (INIS)

    Ahmed, W.; Ahmed, E.

    1994-01-01

    The thermal oxidation of silicon was studied using a large-scale industrial oxidation system. The characteristics of the oxides resulting from pure hydrogen/oxygen (Hsub(2)/Osub(2)), trichloroethane/oxygen (TCA/Osub(2) and hydrogen chloride/oxygen (HCI/Osub(2)) mixtures are compared. Both HCI and TCA addition to oxygen produced an enhanced oxidation rate. The oxidation rate for TCA/Osub(2) was approximately 30-40% higher than for HCI/Osub(2) mixtures. A molar ratio of TCA/Osub(2) of 1% gives an optimum process for very-large-scale industrial (VLSI) applications. However, 3% HCI/Osub(2) gives comparable results to 1% TCA. In addition, boron and phosphorus implantation are observed to increase the oxidation rate. Phosphorus doping of the silicon yields a higher rate than boron-doped wafers. This behaviour is explained in terms of surface damage and chemistry. It appears that the overall mechanisms governing all these processes are similar. (8 figures, 22 references) (Author)

  10. Substoichiometric extraction of rubidium with Dibenzo-24-crown-8 into Xylene

    International Nuclear Information System (INIS)

    Bag, M.; Chattopadhyay, P.; Basu, S.

    2014-01-01

    Owing to immense applications of rubidium in varied fields, extraction and quantification of rubidium have gained great importance in recent years. Here, studies on substoichiometric extraction of rubidium by dibenzo-24-crown-8 into xylene using 86 Rb radiotracer are reported. The method has been optimized by pH of the medium, effects of diverse ions, etc, to explore its applicability in real samples

  11. High-stability transparent amorphous oxide TFT with a silicon-doped back-channel layer

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Hyoung-Rae; Park, Jea-Gun [Hanyang University, Seoul (Korea, Republic of)

    2014-10-15

    We significantly reduced various electrical instabilities of amorphous indium gallium zinc oxide thin-film transistors (TFTs) by using the co-deposition of silicon on an a-IGZO back channel. This process showed improved stability of the threshold voltage (V{sub th}) under high temperature and humidity and negative gate-bias illumination stress (NBIS) without any reduction of IDS. The enhanced stability was achieved with silicon, which has higher metal-oxide bonding strengths than gallium does. Additionally, SiO{sub x} distributed on the a-IGZO surface reduced the adsorption and the desorption of H{sub 2}O and O{sub 2}. This process is applicable to the TFT manufacturing process with a variable sputtering target.

  12. Selective tuning of high-Q silicon photonic crystal nanocavities via laser-assisted local oxidation.

    Science.gov (United States)

    Chen, Charlton J; Zheng, Jiangjun; Gu, Tingyi; McMillan, James F; Yu, Mingbin; Lo, Guo-Qiang; Kwong, Dim-Lee; Wong, Chee Wei

    2011-06-20

    We examine the cavity resonance tuning of high-Q silicon photonic crystal heterostructures by localized laser-assisted thermal oxidation using a 532 nm continuous wave laser focused to a 2.5 μm radius spot-size. The total shift is consistent with the parabolic rate law. A tuning range of up to 8.7 nm is achieved with ∼ 30 mW laser powers. Over this tuning range, the cavity Qs decreases from 3.2×10(5) to 1.2×10(5). Numerical simulations model the temperature distributions in the silicon photonic crystal membrane and the cavity resonance shift from oxidation.

  13. Complete coverage of reduced graphene oxide on silicon dioxide substrates

    International Nuclear Information System (INIS)

    Jingfeng Huang; Hu Chen; Yoong Alfred Tok Iing; Larisika, Melanie; Nowak, Christoph; Faulkner, Steve; Nimmo, Myra A.

    2014-01-01

    Reduced graphene oxide (RGO) has the advantage of an aqueous and industrial-scale production route. No other approaches can rival the RGO field effect transistor platform in terms of cost (oxide with ethanol, carbon islets are deposited preferentially at the edges of existing flakes. With a 2-h treatment, the standard deviation in electrical resistance of the treated chips can be reduced by 99.95%. Thus this process could enable RGO to be used in practical electronic devices. (special topic — international conference on nanoscience and technology, china 2013)

  14. Optical properties of uniformly sized silicon nanocrystals within a single silicon oxide layer

    Energy Technology Data Exchange (ETDEWEB)

    En Naciri, A., E-mail: aotmane.en-naciri@univ-lorraine.fr [Universite de Lorraine, LCP-A2MC, Institut Jean Barriol (France); Miska, P. [Universite de Lorraine, Institut Jean Lamour CNRS UMR 7198 (France); Keita, A.-S. [Max Planck Institute for Intelligent Systems (Germany); Battie, Y. [Universite de Lorraine, LCP-A2MC, Institut Jean Barriol (France); Rinnert, H.; Vergnat, M. [Universite de Lorraine, Institut Jean Lamour CNRS UMR 7198 (France)

    2013-04-15

    Silicon nanocrystals (Si-NC) with different sizes (2-6 nm) are synthesized by evaporation. The system is composed of a single Si-NC layer that is well controlled in size. The numerical modeling of such system, without a large size distribution, is suitable to perform easily the optical calculations. The nanocrystal size and confinement effects on the optical properties are determined by photoluminescence (PL) measurements, absorption in the UV visible range, and spectroscopic ellipsometry (SE). The optical constants and the bandgap energies are then extracted and analyzed. The dependence of the optical responses with the decrease of the size of the Si-NC occurs not only with a drastic reduction of the amplitudes of dielectric function but also by a significant expansion of the optical gap. This study supports the idea of a presence of a critical size of Si-NC for which the confinement effect becomes weak. The evolution of those bandgap energies are discussed in comparison with values reported in literature.

  15. Mechanical anomaly impact on metal-oxide-semiconductor capacitors on flexible silicon fabric

    KAUST Repository

    Ghoneim, Mohamed T.

    2014-06-09

    We report the impact of mechanical anomaly on high-κ/metal-oxide-semiconductor capacitors built on flexible silicon (100) fabric. The mechanical tests include studying the effect of bending radius up to 5 mm minimum bending radius with respect to breakdown voltage and leakage current of the devices. We also report the effect of continuous mechanical stress on the breakdown voltage over extended periods of times.

  16. Silicon oxide based high capacity anode materials for lithium ion batteries

    Science.gov (United States)

    Deng, Haixia; Han, Yongbong; Masarapu, Charan; Anguchamy, Yogesh Kumar; Lopez, Herman A.; Kumar, Sujeet

    2017-03-21

    Silicon oxide based materials, including composites with various electrical conductive compositions, are formulated into desirable anodes. The anodes can be effectively combined into lithium ion batteries with high capacity cathode materials. In some formulations, supplemental lithium can be used to stabilize cycling as well as to reduce effects of first cycle irreversible capacity loss. Batteries are described with surprisingly good cycling properties with good specific capacities with respect to both cathode active weights and anode active weights.

  17. Isothermal and cyclic oxidation resistance of pack siliconized Mo–Si–B alloy

    Energy Technology Data Exchange (ETDEWEB)

    Majumdar, Sanjib, E-mail: sanjib@barc.gov.in

    2017-08-31

    Highlights: • Pack-siliconizing of Mo–Si–B alloy improves its oxidation resistance at 750, 900 and 1400 °C. • A marginal weight change of the coated alloy is detected in isothermal and cyclic oxidation tests. • Kinetics of growth of protective SiO{sub 2} scale is much faster at 1400 °C. • Self-healing SiO{sub 2} is developed at the cracks formed in MoSi{sub 2} layer during cyclic oxidation tests. - Abstract: Oxidation behaviour of MoSi{sub 2} coated Mo–9Si–8B–0.75Y (at.%) alloy has been investigated at three critical temperatures including 750, 900 and 1400 °C in static air. Thermogravimetric analysis (TGA) data indicates a remarkable improvement in the oxidation resistance of the silicide coated alloy in both isothermal and cyclic oxidation tests. The cross-sectional scanning electron microscopy and energy dispersive spectroscopic analysis reveal the occurrence of internal oxidation particularly at the crack fronts formed in the outer MoSi{sub 2} layer during thermal cycling. The dominant oxidation mechanisms at 750–900 °C and 1400 °C are identified. Development of MoB inner layer further improves the oxidation resistance of the silicide coated alloy.

  18. Tuning of structural, light emission and wetting properties of nanostructured copper oxide-porous silicon matrix formed on electrochemically etched copper-coated silicon substrates

    Science.gov (United States)

    Naddaf, M.

    2017-01-01

    Matrices of copper oxide-porous silicon nanostructures have been formed by electrochemical etching of copper-coated silicon surfaces in HF-based solution at different etching times (5-15 min). Micro-Raman, X-ray diffraction and X-ray photoelectron spectroscopy results show that the nature of copper oxide in the matrix changes from single-phase copper (I) oxide (Cu2O) to single-phase copper (II) oxide (CuO) on increasing the etching time. This is accompanied with important variation in the content of carbon, carbon hydrides, carbonyl compounds and silicon oxide in the matrix. The matrix formed at the low etching time (5 min) exhibits a single broad "blue" room-temperature photoluminescence (PL) band. On increasing the etching time, the intensity of this band decreases and a much stronger "red" PL band emerges in the PL spectra. The relative intensity of this band with respect to the "blue" band significantly increases on increasing the etching time. The "blue" and "red" PL bands are attributed to Cu2O and porous silicon of the matrix, respectively. In addition, the water contact angle measurements reveal that the hydrophobicity of the matrix surface can be tuned from hydrophobic to superhydrophobic state by controlling the etching time.

  19. Influence of oxidation treatment on ballistic electron surface-emitting display of porous silicon

    International Nuclear Information System (INIS)

    Du, Wentao; Zhang, Xiaoning; Zhang, Yujuan; Wang, Wenjiang; Duan, Xiaotao

    2012-01-01

    Two groups of porous silicon (PS) samples are treated by rapid thermal oxidation (RTO) and electrochemical oxidation (ECO), respectively. Scanning electron microscopy images show that PS samples are segmented into two layers. Oxidized film layer is formed on the top surface of PS samples treated by RTO while at the bottom of PS samples treated by ECO. Both ECO and RTO treatment can make emission current density, diode current density, and emission efficiency of PS increase with the bias voltage increasing. The emission current density and the field emission enhancement factor β of PS sample treated by RTO are larger than that treated by ECO. The Fowler–Nordheim curves of RTO and ECO samples are linear which indicates that high electric field exists on the oxidized layer and field emission occurs whether PS is treated by RTO or ECO.

  20. High resolution medium energy ion scattering study of silicon oxidation and oxy nitridation

    International Nuclear Information System (INIS)

    Gusev, E.P.; Lu, H.C.; Garfunkel, E.; Gustafsson, T.

    1998-01-01

    Full text: Silicon oxide is likely to remain the material of choice for gate oxides in microelectronics for the foreseeable future. As device become ever smaller and faster, the thickness of these layers in commercial products is predicted to be less than 50 Angstroms in just a few years. An understanding of such devices will therefore likely to be based on microscopic concepts and should now be investigated by atomistic techniques. With medium energy ion scattering (MEIS) using an electrostatic energy analyzer, depth profiling of thin (<60 Angstroms) silicon oxide films on Si(100) with 3 - 5 Angstroms depth resolution in the near region has been done. The growth mechanism of thin oxide films on Si(100) has been studied, using sequential oxygen isotope exposures. It is found that the oxide films are stoichiometric to within approx. 10 Angstroms of the interface. It is also found that the oxidation reactions occur at the surface, in the transition region and at interface, with only the third region being included in the conventional (Deal-Grove) model for oxide formation. Nitrogen is sometimes added to gate oxides, as it has been found empirically that his improves some of the electrical properties. The role, location and even the amount of nitrogen that exists in such films are poorly understood, and represent interesting analytical challenges. MEIS data will be presented that address these questions, measured for a number of different processing conditions. We have recently demonstrated how to perform nitrogen nano-engineering in such ultrathin gate dielectrics, and these results will also be discussed

  1. Polyenergy ion beam synthesis of buried oxynitride layer in silicon

    Energy Technology Data Exchange (ETDEWEB)

    Barabanenkov, M.Yu. E-mail: barab@ipmt-hpm.ac.ru; Agafonov, Yu.A.; Mordkovich, V.N.; Pustovit, A.N.; Vyatkin, A.F.; Zinenko, V.I

    2000-11-01

    The efficiency of silicon oxynitride synthesis in silicon crystals implanted with substoichiometric doses of oxygen and nitrogen ions is investigated both experimentally and theoretically. Si crystals are implanted with oxygen and nitrogen ions with doses of 1.5 and 4.5x10{sup 17} cm{sup -2}, respectively, at fixed oxygen ion energy of 150 keV and nitrogen ion energies varied from 80 to 180 keV. The samples annealed at 1200 deg C for 2 h were analysed by secondary ion mass spectroscopy (SIMS). Theoretically, a `diffusion-alternative sinks' model is applied to the annealing stage of ion beam synthesis of a buried layer of a new phase in solids. It is shown that the maximum of the ternary phase production is attained when nitrogen ions are implanted deeper than oxygen ions. An explanation of this fact is given in terms of that (i) the segregation of oxygen and nitrogen species on the surface of oxide nuclei removes the kinetic restriction of nuclei growth, characteristic of oxide growth, at the expense of only oxygen atoms, and (ii) the higher the implantation energy the smoother the shape of ion range distribution in the target, which, in its turn, causes the predominance of the impurity sink over the impurity diffusion.

  2. Polyenergy ion beam synthesis of buried oxynitride layer in silicon

    International Nuclear Information System (INIS)

    Barabanenkov, M.Yu.; Agafonov, Yu.A.; Mordkovich, V.N.; Pustovit, A.N.; Vyatkin, A.F.; Zinenko, V.I.

    2000-01-01

    The efficiency of silicon oxynitride synthesis in silicon crystals implanted with substoichiometric doses of oxygen and nitrogen ions is investigated both experimentally and theoretically. Si crystals are implanted with oxygen and nitrogen ions with doses of 1.5 and 4.5x10 17 cm -2 , respectively, at fixed oxygen ion energy of 150 keV and nitrogen ion energies varied from 80 to 180 keV. The samples annealed at 1200 deg C for 2 h were analysed by secondary ion mass spectroscopy (SIMS). Theoretically, a `diffusion-alternative sinks' model is applied to the annealing stage of ion beam synthesis of a buried layer of a new phase in solids. It is shown that the maximum of the ternary phase production is attained when nitrogen ions are implanted deeper than oxygen ions. An explanation of this fact is given in terms of that (i) the segregation of oxygen and nitrogen species on the surface of oxide nuclei removes the kinetic restriction of nuclei growth, characteristic of oxide growth, at the expense of only oxygen atoms, and (ii) the higher the implantation energy the smoother the shape of ion range distribution in the target, which, in its turn, causes the predominance of the impurity sink over the impurity diffusion

  3. Temperature dependence of nickel oxide effect on the optoelectronic properties of porous silicon

    Energy Technology Data Exchange (ETDEWEB)

    Riahi, R., E-mail: riahirim01@gmail.com [Laboratory of Semiconductors, Nanostructures and Advanced Technology (LSNTA), Research and Technology Center of Energy, Tourist Road Soliman, BP 95, 2050 Hammam-Lif (Tunisia); Faculty of Sciences Tunis–El Manar University (Tunisia); Derbali, L. [Laboratory of Semiconductors, Nanostructures and Advanced Technology (LSNTA), Research and Technology Center of Energy, Tourist Road Soliman, BP 95, 2050 Hammam-Lif (Tunisia); Ouertani, B. [Laboratory of Semiconductors, Nanostructures and Advanced Technology (LSNTA), Research and Technology Center of Energy, Tourist Road Soliman, BP 95, 2050 Hammam-Lif (Tunisia); Higher Institute of Environment Science and Technology of Borj-Cedria (Tunisia); Ezzaouia, H. [Laboratory of Semiconductors, Nanostructures and Advanced Technology (LSNTA), Research and Technology Center of Energy, Tourist Road Soliman, BP 95, 2050 Hammam-Lif (Tunisia)

    2017-05-15

    Highlights: • The treatment of porous silicon (PS) with nickel oxide (NiO) decreases the reflectivity significantly. • FTIR analysis showed a substitution of Si−H bonds to Si−O−Si and Si−O−Ni after the thermal annealing. • Annealing the treated NiO/PS at 400 °C leads to a noticeable improvement of the photoluminescence (PL) intensity. • A blueshift was obtained in the PL spectra due to the decrease of silicon nanocrystallites size after exceeding 400 °C. - Abstract: This paper investigates the effect of Nickel oxide (NiO) on the structural and optical properties of porous silicon (PS). Our investigations showed an obvious improvement of porous silicon optoelectronique properties after coating the PS with NiO thin film as a passivating process. The as-prepared NiO/PS thin film was subjected to a thermal annealing to study the effect of temperature on the efficiency of this treatment. The deposition of NiO onto the porous silicon layer was performed using the spray pyrolysis method. The surface modification of the as-prepared NiO/PS samples was investigated after annealing at various temperatures, using an infrared furnace, ranging between 300 °C and 600 °C. The X-ray Diffraction results showed that obtained films show cubic structure with preferred (200) plane orientation. We found an obvious dependence of the PS nanocrystallites size (nc-Si) to the annealing temperature. Photoluminescence (PL) is directly related to the electronic structure and transitions. The characteristic change of the band gap with decrease in size of the nanostructures can be pointed out by the observed blue shift in the photoluminescence spectra. Nickel oxide treatment of Porous silicon led to a significant increase of photoluminescence with a resulting blue-shift at higher annealing temperature. The surface morphology was examined by scanning electron microscope (SEM), and FTIR spectroscopy was used to study the chemical composition of the films. Moreover, the total

  4. Temperature dependence of nickel oxide effect on the optoelectronic properties of porous silicon

    International Nuclear Information System (INIS)

    Riahi, R.; Derbali, L.; Ouertani, B.; Ezzaouia, H.

    2017-01-01

    Highlights: • The treatment of porous silicon (PS) with nickel oxide (NiO) decreases the reflectivity significantly. • FTIR analysis showed a substitution of Si−H bonds to Si−O−Si and Si−O−Ni after the thermal annealing. • Annealing the treated NiO/PS at 400 °C leads to a noticeable improvement of the photoluminescence (PL) intensity. • A blueshift was obtained in the PL spectra due to the decrease of silicon nanocrystallites size after exceeding 400 °C. - Abstract: This paper investigates the effect of Nickel oxide (NiO) on the structural and optical properties of porous silicon (PS). Our investigations showed an obvious improvement of porous silicon optoelectronique properties after coating the PS with NiO thin film as a passivating process. The as-prepared NiO/PS thin film was subjected to a thermal annealing to study the effect of temperature on the efficiency of this treatment. The deposition of NiO onto the porous silicon layer was performed using the spray pyrolysis method. The surface modification of the as-prepared NiO/PS samples was investigated after annealing at various temperatures, using an infrared furnace, ranging between 300 °C and 600 °C. The X-ray Diffraction results showed that obtained films show cubic structure with preferred (200) plane orientation. We found an obvious dependence of the PS nanocrystallites size (nc-Si) to the annealing temperature. Photoluminescence (PL) is directly related to the electronic structure and transitions. The characteristic change of the band gap with decrease in size of the nanostructures can be pointed out by the observed blue shift in the photoluminescence spectra. Nickel oxide treatment of Porous silicon led to a significant increase of photoluminescence with a resulting blue-shift at higher annealing temperature. The surface morphology was examined by scanning electron microscope (SEM), and FTIR spectroscopy was used to study the chemical composition of the films. Moreover, the total

  5. Enhancing the far-ultraviolet sensitivity of silicon complementary metal oxide semiconductor imaging arrays

    Science.gov (United States)

    Retherford, Kurt D.; Bai, Yibin; Ryu, Kevin K.; Gregory, James A.; Welander, Paul B.; Davis, Michael W.; Greathouse, Thomas K.; Winters, Gregory S.; Suntharalingam, Vyshnavi; Beletic, James W.

    2015-10-01

    We report our progress toward optimizing backside-illuminated silicon P-type intrinsic N-type complementary metal oxide semiconductor devices developed by Teledyne Imaging Sensors (TIS) for far-ultraviolet (UV) planetary science applications. This project was motivated by initial measurements at Southwest Research Institute of the far-UV responsivity of backside-illuminated silicon PIN photodiode test structures, which revealed a promising QE in the 100 to 200 nm range. Our effort to advance the capabilities of thinned silicon wafers capitalizes on recent innovations in molecular beam epitaxy (MBE) doping processes. Key achievements to date include the following: (1) representative silicon test wafers were fabricated by TIS, and set up for MBE processing at MIT Lincoln Laboratory; (2) preliminary far-UV detector QE simulation runs were completed to aid MBE layer design; (3) detector fabrication was completed through the pre-MBE step; and (4) initial testing of the MBE doping process was performed on monitoring wafers, with detailed quality assessments.

  6. Pyroelectricity of silicon-doped hafnium oxide thin films

    Science.gov (United States)

    Jachalke, Sven; Schenk, Tony; Park, Min Hyuk; Schroeder, Uwe; Mikolajick, Thomas; Stöcker, Hartmut; Mehner, Erik; Meyer, Dirk C.

    2018-04-01

    Ferroelectricity in hafnium oxide thin films is known to be induced by various doping elements and in solid-solution with zirconia. While a wealth of studies is focused on their basic ferroelectric properties and memory applications, thorough studies of the related pyroelectric properties and their application potential are only rarely found. This work investigates the impact of Si doping on the phase composition and ferro- as well as pyroelectric properties of thin film capacitors. Dynamic hysteresis measurements and the field-free Sharp-Garn method were used to correlate the reported orthorhombic phase fractions with the remanent polarization and pyroelectric coefficient. Maximum values of 8.21 µC cm-2 and -46.2 µC K-1 m-2 for remanent polarization and pyroelectric coefficient were found for a Si content of 2.0 at%, respectively. Moreover, temperature-dependent measurements reveal nearly constant values for the pyroelectric coefficient and remanent polarization over the temperature range of 0 ° C to 170 ° C , which make the material a promising candidate for IR sensor and energy conversion applications beyond the commonly discussed use in memory applications.

  7. The effect of thermal oxidation on the luminescence properties of nanostructured silicon.

    Science.gov (United States)

    Liu, Lijia; Sham, Tsun-Kong

    2012-08-06

    Herein is reported a detailed study of the luminescence properties of nanostructured Si using X-ray excited optical luminescence (XEOL) in combination with X-ray absorption near-edge structures (XANES). P-type Si nanowires synthesized via electroless chemical etching from Si wafers of different doping levels and porous Si synthesized using electrochemical method are examined under X-ray excitation across the Si K-, L(3,2) -, and O K-edges. It is found that while as-prepared Si nanostructures are weak light emitters, intense visible luminescence is observed from thermally oxidized Si nanowires and porous Si. The luminescence mechanism of Si upon oxidation is investigated by oxidizing nanostructured Si at different temperatures. Interestingly, the two luminescence bands observed show different response with the variation of absorption coefficient upon Si and O core-electron excitation in elemental silicon and silicon oxide. A correlation between luminescence properties and electronic structures is thus established. The implications of the finding are discussed in terms of the behavior of the oxygen deficient center (OCD) and non-bridging oxygen hole center (NBOHC). Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  8. Optimization of oxidation processes to improve crystalline silicon solar cell emitters

    Directory of Open Access Journals (Sweden)

    L. Shen

    2014-02-01

    Full Text Available Control of the oxidation process is one key issue in producing high-quality emitters for crystalline silicon solar cells. In this paper, the oxidation parameters of pre-oxidation time, oxygen concentration during pre-oxidation and pre-deposition and drive-in time were optimized by using orthogonal experiments. By analyzing experimental measurements of short-circuit current, open circuit voltage, series resistance and solar cell efficiency in solar cells with different sheet resistances which were produced by using different diffusion processes, we inferred that an emitter with a sheet resistance of approximately 70 Ω/□ performed best under the existing standard solar cell process. Further investigations were conducted on emitters with sheet resistances of approximately 70 Ω/□ that were obtained from different preparation processes. The results indicate that emitters with surface phosphorus concentrations between 4.96 × 1020 cm−3 and 7.78 × 1020 cm−3 and with junction depths between 0.46 μm and 0.55 μm possessed the best quality. With no extra processing, the final preparation of the crystalline silicon solar cell efficiency can reach 18.41%, which is an increase of 0.4%abs compared to conventional emitters with 50 Ω/□ sheet resistance.

  9. The kinetics and properties of thermal oxidation of silicon in TCA-O/sub 2/

    International Nuclear Information System (INIS)

    Ahmed, W.; Ahmed, E.

    1993-01-01

    The oxidation of silicon using dry O/sub 2/ is now well established as a key process for the fabrication of electronic devices in the semiconductor industry. However, this process is complicated by its sensitivity to impurities which reduce device yields. HCl can be added to O/sub 2/ to remove these impurities but due to its highly corrosive nature a safer and cleaner alternative such as trichloroethane (TCA) is desirable. In this paper, the thermal oxidation of silicon using a mixture of TCA-O/sub 2/ has been investigated in a large scale industrial system. The growth kinetics and the properties of these films have been studies and compared to oxides produced from dry 2. The addition of TCA generates HCl in situ, enhances the oxidation rate by approximately 54% nd improves the electrical properties. It was found that a 1 mol.% mixture gives the optimum process. An analysis of the data suggests that a liner parabolic growth model is applicable and provides a valuable insight into the physical phenomena governing this important process. (author)

  10. Fluorinated alkyne-derived monolayers on oxide-free silicon nanowires via one-step hydrosilylation

    International Nuclear Information System (INIS)

    Nguyen Minh, Quyen; Pujari, Sidharam P.; Wang, Bin; Wang, Zhanhua; Haick, Hossam; Zuilhof, Han; Rijn, Cees J.M. van

    2016-01-01

    Highlights: • Oxide-free H-terminated silicon nanowires undergo efficient surface modification by reaction with fluorinated 1-alkynes (HC≡C−(CH 2 ) 6 C 8 H 17−x F x ; x = 0–17). • These surface-modified Si NWs are chemically stable under range of conditions (including acid, base). • The surface coating yields efficient electrical passivation as demonstrated by a near-zero electrochemical activity of the surface. - Abstract: Passivation of oxide-free silicon nanowires (Si NWs) by the formation of high-quality fluorinated 1-hexadecyne-derived monolayers with varying fluorine content has been investigated. Alkyl chain monolayers (C 16 H 30−x F x ) with a varying number of fluorine substituents (x = 0, 1, 3, 9, 17) were attached onto hydrogen-terminated silicon (Si−H) surfaces with an effective one-step hydrosilylation. This surface chemistry gives well-defined monolayers on nanowires that have a cylindrical core–shell structure, as characterized by X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR) and static contact angle (SCA) analysis. The monolayers were stable under acidic and basic conditions, as well as under extreme conditions (such as UV exposure), and provide excellent surface passivation, which opens up applications in the fields of field effect transistors, optoelectronics and especially for disease diagnosis.

  11. Effect of rapid oxidation on optical and electrical properties of silicon nanowires obtained by chemical etching

    Science.gov (United States)

    Karyaoui, M.; Bardaoui, A.; Ben Rabha, M.; Harmand, J. C.; Amlouk, M.

    2012-05-01

    In the present work, we report the investigation of passivated silicon nanowires (SiNWs) having an average radius of 3.7 μm, obtained by chemical etching of p-type silicon (p-Si). The surface passivation of the SiNWs was performed through a rapid oxidation conducted under a controlled atmosphere at different temperatures and durations. The morphology of the SiNWs was examined using a scanning electron microscope (SEM) that revealed a wave-like structure of dense and vertically aligned one-dimensional silicon nanostructures. On the other hand, optical and electrical characterizations of the SiNWs were studied using a UV-Vis-NIR spectrometer, the Fourier transform infrared spectroscopy (FTIR) and I-V measurements. The reflectance of SiNWs has been dropped to approximately 2% in comparison to that of bare p-Si. This low reflectance slightly increased after carrying out the rapid thermal annealing. The observed behavior was attributed to the formation of a SiO2 layer, as confirmed by FTIR measurements. Finally, the electrical measurements have shown that the rapid oxidation, at certain conditions, contributes to the improvement of the electrical responses of the SiNWs, which can be of great interest for photovoltaic applications.

  12. Fluorinated alkyne-derived monolayers on oxide-free silicon nanowires via one-step hydrosilylation

    Energy Technology Data Exchange (ETDEWEB)

    Nguyen Minh, Quyen [Laboratory of Organic Chemistry, Wageningen University, Stippeneng 4, 6708 WE Wageningen (Netherlands); Nanosens, IJsselkade 7, 7201 HB Zutphen (Netherlands); Pujari, Sidharam P. [Laboratory of Organic Chemistry, Wageningen University, Stippeneng 4, 6708 WE Wageningen (Netherlands); Wang, Bin [The Department of Chemical Engineering and Russell Berrie Nanotechnology Institute, Technion – Israel Institute of Technology, Haifa 3200003 (Israel); Wang, Zhanhua [Laboratory of Organic Chemistry, Wageningen University, Stippeneng 4, 6708 WE Wageningen (Netherlands); Haick, Hossam [The Department of Chemical Engineering and Russell Berrie Nanotechnology Institute, Technion – Israel Institute of Technology, Haifa 3200003 (Israel); Zuilhof, Han [Laboratory of Organic Chemistry, Wageningen University, Stippeneng 4, 6708 WE Wageningen (Netherlands); Rijn, Cees J.M. van, E-mail: cees.vanrijn@wur.nl [Laboratory of Organic Chemistry, Wageningen University, Stippeneng 4, 6708 WE Wageningen (Netherlands)

    2016-11-30

    Highlights: • Oxide-free H-terminated silicon nanowires undergo efficient surface modification by reaction with fluorinated 1-alkynes (HC≡C−(CH{sub 2}){sub 6}C{sub 8}H{sub 17−x}F{sub x}; x = 0–17). • These surface-modified Si NWs are chemically stable under range of conditions (including acid, base). • The surface coating yields efficient electrical passivation as demonstrated by a near-zero electrochemical activity of the surface. - Abstract: Passivation of oxide-free silicon nanowires (Si NWs) by the formation of high-quality fluorinated 1-hexadecyne-derived monolayers with varying fluorine content has been investigated. Alkyl chain monolayers (C{sub 16}H{sub 30−x}F{sub x}) with a varying number of fluorine substituents (x = 0, 1, 3, 9, 17) were attached onto hydrogen-terminated silicon (Si−H) surfaces with an effective one-step hydrosilylation. This surface chemistry gives well-defined monolayers on nanowires that have a cylindrical core–shell structure, as characterized by X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR) and static contact angle (SCA) analysis. The monolayers were stable under acidic and basic conditions, as well as under extreme conditions (such as UV exposure), and provide excellent surface passivation, which opens up applications in the fields of field effect transistors, optoelectronics and especially for disease diagnosis.

  13. Self-limiting and complete oxidation of silicon nanostructures produced by laser ablation in water

    Energy Technology Data Exchange (ETDEWEB)

    Vaccaro, L.; Messina, F.; Camarda, P.; Gelardi, F. M.; Cannas, M., E-mail: marco.cannas@unipa.it [Dipartimento di Fisica e Chimica, Università di Palermo, Via Archirafi 36, I-90123 Palermo (Italy); Popescu, R.; Schneider, R.; Gerthsen, D. [Laboratory for Electron Microscopy, Karlsruhe Institute of Technology, Engesserstrasse 7, 76131 Karlsruhe (Germany)

    2016-07-14

    Oxidized Silicon nanomaterials produced by 1064 nm pulsed laser ablation in deionized water are investigated. High-resolution transmission electron microscopy coupled with energy dispersive X-ray spectroscopy allows to characterize the structural and chemical properties at a sub-nanometric scale. This analysis clarifies that laser ablation induces both self-limiting and complete oxidation processes which produce polycrystalline Si surrounded by a layer of SiO{sub 2} and amorphous fully oxidized SiO{sub 2}, respectively. These nanostructures exhibit a composite luminescence spectrum which is investigated by time-resolved spectroscopy with a tunable laser excitation. The origin of the observed luminescence bands agrees with the two structural typologies: Si nanocrystals emit a μs-decaying red band; defects of SiO{sub 2} give rise to a ns-decaying UV band and two overlapping blue bands with lifetime in the ns and ms timescale.

  14. Fabrication and evaluation of series-triple quantum dots by thermal oxidation of silicon nanowire

    International Nuclear Information System (INIS)

    Uchida, Takafumi; Jo, Mingyu; Tsurumaki-Fukuchi, Atsushi; Arita, Masashi; Takahashi, Yasuo; Fujiwara, Akira

    2015-01-01

    Series-connected triple quantum dots were fabricated by a simple two-step oxidation technique using the pattern-dependent oxidation of a silicon nanowire and an additional oxidation of the nanowire through the gap of the fine gates attached to the nanowire. The characteristics of multi-dot single-electron devices are obtained. The formation of each quantum dot beneath an attached gate is confirmed by analyzing the electrical characteristics and by evaluating the gate capacitances between all pairings of gates and quantum dots. Because the gate electrode is automatically attached to each dot, the device structure benefits from scalability. This technique promises integrability of multiple quantum dots with individual control gates

  15. Control of the optical properties of silicon and chromium mixed oxides deposited by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Vergara, L.; Galindo, R. Escobar; Martinez, R.; Sanchez, O.; Palacio, C.; Albella, J.M.

    2011-01-01

    The development of mixed-oxide thin films allows obtaining materials with better properties than those of the different binary oxides, which makes them suitable for a great number of applications in different fields, such as tribology, optics or microelectronics. In this paper we investigate the deposition of mixed chromium and silicon oxides deposited by reactive magnetron sputtering with a view to use them as optical coatings with an adjustable refractive index. These films have been characterized by means of Rutherford backscattering spectrometry, Auger electron spectroscopy, X-ray diffraction, scanning electron microscopy, Fourier-transform infrared spectroscopy and spectroscopic ellipsometry so as to determine how the deposition conditions influence the characteristics of the material. We have found that the deposition parameter whose influence determines the properties of the films to a greater extent is the amount of oxygen in the reactive sputtering gas.

  16. A highly sensitive and durable electrical sensor for liquid ethanol using thermally-oxidized mesoporous silicon

    Science.gov (United States)

    Harraz, Farid A.; Ismail, Adel A.; Al-Sayari, S. A.; Al-Hajry, A.; Al-Assiri, M. S.

    2016-12-01

    A capacitive detection of liquid ethanol using reactive, thermally oxidized films constructed from electrochemically synthesized porous silicon (PSi) is demonstrated. The sensor elements are fabricated as meso-PSi (pore sizes hydrophobic PSi surface exhibited almost a half sensitivity of the thermal oxide sensor. The response to water is achieved only at the oxidized surface and found to be ∼one quarter of the ethanol sensitivity, dependent on parameters such as vapor pressure and surface tension. The capacitance response retains ∼92% of its initial value after continuous nine cyclic runs and the sensors presumably keep long-term stability after three weeks storage, demonstrating excellent durability and storage stability. The observed behavior in current system is likely explained by the interface interaction due to dipole moment effect. The results suggest that the current sensor structure and design can be easily made to produce notably higher sensitivities for reversible detection of various analytes.

  17. Low-temperature atomic layer deposition of MoO{sub x} for silicon heterojunction solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Macco, B.; Vos, M.F.J.; Thissen, N.F.W.; Bol, A.A. [Department of Applied Physics, Eindhoven University of Technology, Eindhoven (Netherlands); Kessels, W.M.M. [Department of Applied Physics, Eindhoven University of Technology, Eindhoven (Netherlands); Solliance Solar Research, Eindhoven (Netherlands)

    2015-07-15

    The preparation of high-quality molybdenum oxide (MoO{sub x}) is demonstrated by plasma-enhanced atomic layer deposition (ALD) at substrate temperatures down to 50 C. The films are amorphous, slightly substoichiometric with respect to MoO{sub 3}, and free of other elements apart from hydrogen (<11 at%). The films have a high transparency in the visible region and their compatibility with a-Si:H passivation schemes is demonstrated. It is discussed that these aspects, in conjunction with the low processing temperature and the ability to deposit very thin conformal films, make this ALD process promising for the future application of MoO{sub x} in hole-selective contacts for silicon heterojunction solar cells. (copyright 2015 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  18. Pull-test adhesion measurements of diamondlike carbon films on silicon carbide, silicon nitride, aluminum oxide, and zirconium oxide

    International Nuclear Information System (INIS)

    Erck, R.A.; Nichols, F.A.; Dierks, J.F.

    1994-01-01

    Hydrogenated amorphous carbon or diamondlike carbon (DLC) films were formed by 400 eV methane (CH 4 ) ion bombardment of various smooth and rough ceramics, as well as ceramics coated with a layer of Si or Ti. Adhesion was measured by a bonded-pin method. Excellent adhesion was measured for smooth SiC and Si 3 N 4 , but adhesion of DLC to smooth Al 2 O 3 and ZrO 2 was negligible. The use of a Si bonding interlayer produced good adhesion to all the substrates, but a Ti layer was ineffective due to poor bonding between the DLC film and Ti. Bulk thermodynamic calculations are not directly applicable to bonding at the interface because the interface is two dimensional and the compositions of interfacial phases are generally not known. If the standard enthalpy ΔH degree for the reaction between CH 4 and the substrate material is calculated under the assumption that a carbide phase is produced, a relationship is seen between the reaction enthalpy and the relative adhesion. Large positive enthalpies are associated with poor adhesion; negative or small positive enthalpies are associated with good adhesion. This relation between enthalpy and adhesion was also observed for DLC deposited on Si. The lack of adhesion to the Ti was attributed to inadvertent formation of a surface oxide layer that rendered the enthalpy for the reaction with CH 4 positive

  19. Amorphous silicon oxide layers for surface passivation and contacting of heterostructure solar cells of amorphous and crystalline silicon; Amorphe Siliziumoxidschichten zur Oberflaechenpassivierung und Kontaktierung von Heterostruktur-Solarzellen aus amorphen und kristallinem Silizium

    Energy Technology Data Exchange (ETDEWEB)

    Einsele, Florian

    2010-02-05

    Atomic hydrogen plays a dominant role in the passivation of crystalline silicon surfaces by layers of amorphous silicon. In order to research into this role, this thesis presents the method of hydrogen effusion from thin amorphous films of silicon (a-Si:H) and silicon oxide (a-SiO{sub x}:H). The oxygen concentration of the sub-stoichiometric a-SiO{sub x}:H films ranges up to 10 at.-%. The effusion experiment yields information about the content and thermal stability of hydrogen and about the microstructure of the films. A mathematical description of the diffusion process of atomic hydrogen yields an analytical expression of the effusion rate R{sub E} depending on the linearly increasing temperature in the experiment. Fitting of the calculated effusion rates R{sub E} to measured effusion spectra yields the diffusion coefficient of atomic hydrogen in a-SiO{sub x}:H. With increasing oxygen concentration, the diffusion coefficient of hydrogen in the a-SiO{sub x}:H films decreases. This is attributed to an increasing Si-H bond energy due to back bonded oxygen, resulting in a higher stability of hydrogen in the films. This result is confirmed by an increasing thermal stability of the p-type c-Si passivation with a-SiO{sub x}:H of increasing oxygen concentrations up to 5 at.-%. The passivation reaches very low recombination velocities of S < 10 cm/s at the interface. However, for higher oxygen concentrations up to 10 at.-%, the passivation quality decreases significantly. Here, infrared spectroscopy of Si-H vibrational modes and hydrogen effusion show an increase of hydrogen-rich interconnected voids in the films. This microstructure results in a high amount of molecular hydrogen (H{sub 2}) in the layers, which is not suitable for the saturation of c-Si interface defects. Annealing of the films at temperatures around 400 C leads to a release of H{sub 2} from the voids, as a result of which Si-Si bonds in the material reconstruct. Subsequently, hydrogen migration in the

  20. Silicon improves seed germination and alleviates oxidative stress of bud seedlings in tomato under water deficit stress.

    Science.gov (United States)

    Shi, Yu; Zhang, Yi; Yao, Hejin; Wu, Jiawen; Sun, Hao; Gong, Haijun

    2014-05-01

    The beneficial effects of silicon on plant growth and development under drought have been widely reported. However, little information is available on the effects of silicon on seed germination under drought. In this work, the effects of exogenous silicon (0.5 mM) on the seed germination and tolerance performance of tomato (Solanum lycopersicum L.) bud seedlings under water deficit stress simulated by 10% (w/v) polyethylene glycol (PEG-6000) were investigated in four cultivars ('Jinpengchaoguan', 'Zhongza No.9', 'Houpi L402' and 'Oubao318'). The results showed that the seed germination percentage was notably decreased in the four cultivars under water stress, and it was significantly improved by added silicon. Compared with the non-silicon treatment, silicon addition increased the activities of superoxide dismutase (SOD) and catalase (CAT), and decreased the production of superoxide anion (O2·) and hydrogen peroxide (H2O2) in the radicles of bud seedlings under water stress. Addition of silicon decreased the total phenol concentrations in radicles under water stress, which might contribute to the decrease of peroxidase (POD) activity, as observed in the in vivo and in vitro experiments. The decrease of POD activity might contribute to a less accumulation of hydroxyl radical (·OH) under water stress. Silicon addition also decreased the concentrations of malondialdehyde (MDA) in the radicles under stress, indicating decreased lipid peroxidation. These results suggest that exogenous silicon could improve seed germination and alleviate oxidative stress to bud seedling of tomato by enhancing antioxidant defense. The positive effects of silicon observed in a silicon-excluder also suggest the active involvement of silicon in biochemical processes in plants. Copyright © 2014 Elsevier Masson SAS. All rights reserved.

  1. Pull-test adhesion measurements of diamondlike carbon films on silicon carbide, silicon nitride, aluminum oxide, and zirconium oxide

    Energy Technology Data Exchange (ETDEWEB)

    Erck, R.A.; Nichols, F.A. [Argonne National Lab., IL (United States); Dierks, J.F. [North Dakota State Univ., Fargo, ND (United States)

    1993-10-01

    Hydrogenated amorphous carbon films or diamondlike carbon (DLC) films were formed by ion-beam deposition of 400 eV methane (CH{sub 4}) ions on several smooth and rough ceramics, as well as on ceramics coated with a layer of Si and Ti. Adhesion was measured by the pin-pull method. Excellent adhesion was measured for smooth SiC and Si{sub 3}N{sub 4}, but adhesion of DLC to Al{sub 2}O{sub 3} and ZrO{sub 2} was negligible. The use of a Si bonding interlayer produced good adhesion to all the substrates, but a Ti layer was ineffective because bonding between the DLC film and Ti was poor. The presence of surface roughness appeared to greatly increase the measured adhesion in all cases. Bulk thermodynamic calculations are not directly applicable to bonding at the interface. If the standard enthalpy of formation for reaction between CH{sub 4} and substrate is calculated assumpting a carbide or carbon phase is produced, a relation is seen between reaction enthalpy and relative adhesion. Large positive enthalpies are associated with poor adhesion; negative or small positive enthalpies are associated with good adhesion. This relation between enthalpy and adhesion was also observed for DLC deposited on Si. Lack of adhesion to Ti was attributed to inadvertent formation of a surface oxide layer that rendered the enthalpy for reaction with CH{sub 4} strongly positive and similar in magnitude to that for Al{sub 2}O{sub 3} and ZrO{sub 2}.

  2. High-aspect-ratio, silicon oxide-enclosed pillar structures in microfluidic liquid chromatography.

    Science.gov (United States)

    Taylor, Lisa C; Lavrik, Nickolay V; Sepaniak, Michael J

    2010-11-15

    The present paper discusses the ability to separate chemical species using high-aspect-ratio, silicon oxide-enclosed pillar arrays. These miniaturized chromatographic systems require smaller sample volumes, experience less flow resistance, and generate superior separation efficiency over traditional packed bed liquid chromatographic columns, improvements controlled by the increased order and decreased pore size of the systems. In our distinctive fabrication sequence, plasma-enhanced chemical vapor deposition (PECVD) of silicon oxide is used to alter the surface and structural properties of the pillars for facile surface modification while improving the pillar mechanical stability and increasing surface area. The separation behavior of model compounds within our pillar systems indicated an unexpected hydrophobic-like separation mechanism. The effects of organic modifier, ionic concentration, and pressure-driven flow rate were studied. A decrease in the organic content of the mobile phase increased peak resolution while detrimentally effecting peak shape. A resolution of 4.7 (RSD = 3.7%) was obtained for nearly perfect Gaussian shaped peaks, exhibiting plate heights as low as 1.1 and 1.8 μm for fluorescein and sulforhodamine B, respectively. Contact angle measurements and DART mass spectrometry analysis indicate that our employed elastomeric soft bonding technique modifies pillar properties, creating a fortuitous stationary phase. This discovery provides evidence supporting the ability to easily functionalize PECVD oxide surfaces by gas-phase reactions.

  3. Toward Annealing-Stable Molybdenum-Oxide-Based Hole-Selective Contacts For Silicon Photovoltaics

    KAUST Repository

    Essig, Stephanie

    2018-02-21

    Molybdenum oxide (MoOX) combines a high work function with broadband optical transparency. Sandwiched between a hydrogenated intrinsic amorphous silicon passivation layer and a transparent conductive oxide, this material allows a highly efficient hole-selective front contact stack for crystalline silicon solar cells. However, hole extraction from the Si wafer and transport through this stack degrades upon annealing at 190 °C, which is needed to cure the screen-printed Ag metallization applied to typical Si solar cells. Here, we show that effusion of hydrogen from the adjacent layers is a likely cause for this degradation, highlighting the need for hydrogen-lean passivation layers when using such metal-oxide-based carrier-selective contacts. Pre-MoOX-deposition annealing of the passivating a-Si:H layer is shown to be a straightforward approach to manufacturing MoOX-based devices with high fill factors using screen-printed metallization cured at 190 °C.

  4. Thermal radiative near field transport between vanadium dioxide and silicon oxide across the metal insulator transition

    Energy Technology Data Exchange (ETDEWEB)

    Menges, F.; Spieser, M.; Riel, H.; Gotsmann, B., E-mail: bgo@zurich.ibm.com [IBM Research-Zurich, Säumerstrasse 4, CH-8803 Rüschlikon (Switzerland); Dittberner, M. [IBM Research-Zurich, Säumerstrasse 4, CH-8803 Rüschlikon (Switzerland); Photonics Laboratory, ETH Zurich, 8093 Zurich (Switzerland); Novotny, L. [Photonics Laboratory, ETH Zurich, 8093 Zurich (Switzerland); Passarello, D.; Parkin, S. S. P. [IBM Almaden Research Center, 650 Harry Road, San Jose, California 95120 (United States)

    2016-04-25

    The thermal radiative near field transport between vanadium dioxide and silicon oxide at submicron distances is expected to exhibit a strong dependence on the state of vanadium dioxide which undergoes a metal-insulator transition near room temperature. We report the measurement of near field thermal transport between a heated silicon oxide micro-sphere and a vanadium dioxide thin film on a titanium oxide (rutile) substrate. The temperatures of the 15 nm vanadium dioxide thin film varied to be below and above the metal-insulator-transition, and the sphere temperatures were varied in a range between 100 and 200 °C. The measurements were performed using a vacuum-based scanning thermal microscope with a cantilevered resistive thermal sensor. We observe a thermal conductivity per unit area between the sphere and the film with a distance dependence following a power law trend and a conductance contrast larger than 2 for the two different phase states of the film.

  5. Efficiency improvement of multicrystalline silicon solar cells after surface and grain boundaries passivation using vanadium oxide

    Energy Technology Data Exchange (ETDEWEB)

    Derbali, L., E-mail: rayan.slat@yahoo.fr [Photovoltaiec Laboratory, Research and Technology Center of Energy, Technopole de Borj-Cedria, BP 95, Hammam-Lif 2050 (Tunisia); Ezzaouia, H. [Photovoltaiec Laboratory, Research and Technology Center of Energy, Technopole de Borj-Cedria, BP 95, Hammam-Lif 2050 (Tunisia)

    2012-08-01

    Highlights: Black-Right-Pointing-Pointer Evaporation of vanadium pentoxide onto the front surface leads to reduce the surface reflectivity considerably. Black-Right-Pointing-Pointer An efficient surface passivation can be obtained after thermal treatment of obtained films. Black-Right-Pointing-Pointer Efficiency of the obtained solar cells has been improved noticeably after thermal treatment of deposited thin films. - Abstract: The aim of this work is to investigate the effect of vanadium oxide deposition onto the front surface of multicrystalline silicon (mc-Si) substrat, without any additional cost in the fabrication process and leading to an efficient surface and grain boundaries (GBs) passivation that have not been reported before. The lowest reflectance of mc-Si coated with vanadium oxide film of 9% was achieved by annealing the deposited film at 600 Degree-Sign C. Vanadium pentoxide (V{sub 2}O{sub 5}) were thermally evaporated onto the surface of mc-Si substrates, followed by a short annealing duration at a temperature ranging between 600 Degree-Sign C and 800 Degree-Sign C, under O{sub 2} atmosphere. The chemical composition of the films was analyzed by means of Fourier transform infrared spectroscopy (FTIR). Surface and cross-section morphology were determined by atomic force microscope (AFM) and a scanning electron microscope (SEM), respectively. The deposited vanadium oxide thin films make the possibility of combining in one processing step an antireflection coating deposition along with efficient surface state passivation, as compared to a reference wafer. Silicon solar cells based on untreated and treated mc-Si wafers were achieved. We showed that mc-silicon solar cells, subjected to the above treatment, have better short circuit currents and open-circuit voltages than those made from untreated wafers. Thus, the efficiency of obtained solar cells has been improved.

  6. Efficiency improvement of multicrystalline silicon solar cells after surface and grain boundaries passivation using vanadium oxide

    International Nuclear Information System (INIS)

    Derbali, L.; Ezzaouia, H.

    2012-01-01

    Highlights: ► Evaporation of vanadium pentoxide onto the front surface leads to reduce the surface reflectivity considerably. ► An efficient surface passivation can be obtained after thermal treatment of obtained films. ► Efficiency of the obtained solar cells has been improved noticeably after thermal treatment of deposited thin films. - Abstract: The aim of this work is to investigate the effect of vanadium oxide deposition onto the front surface of multicrystalline silicon (mc-Si) substrat, without any additional cost in the fabrication process and leading to an efficient surface and grain boundaries (GBs) passivation that have not been reported before. The lowest reflectance of mc-Si coated with vanadium oxide film of 9% was achieved by annealing the deposited film at 600 °C. Vanadium pentoxide (V 2 O 5 ) were thermally evaporated onto the surface of mc-Si substrates, followed by a short annealing duration at a temperature ranging between 600 °C and 800 °C, under O 2 atmosphere. The chemical composition of the films was analyzed by means of Fourier transform infrared spectroscopy (FTIR). Surface and cross-section morphology were determined by atomic force microscope (AFM) and a scanning electron microscope (SEM), respectively. The deposited vanadium oxide thin films make the possibility of combining in one processing step an antireflection coating deposition along with efficient surface state passivation, as compared to a reference wafer. Silicon solar cells based on untreated and treated mc-Si wafers were achieved. We showed that mc-silicon solar cells, subjected to the above treatment, have better short circuit currents and open-circuit voltages than those made from untreated wafers. Thus, the efficiency of obtained solar cells has been improved.

  7. Comparative substoichiometric extraction of zinc with potassium salts of ethyl, propyl, butyl, pentyl and benzyl xanthates

    International Nuclear Information System (INIS)

    Chandrasekhar Reddy, P.; Rangamannar, P.

    1995-01-01

    The comparative extractability of zinc with potassium salts of ethyl, propyl, butyl, pentyl, and benzyl xanthates from the pH range of 3.5-9.0 into chloroform has been studied, employing a sensitive and rapid substoichiometric radiochemical method. The extent of reproducibility was tested in each case. The effect of associated ions on the extraction was studied. The amount of zinc present in the standard solutions was determined employing each xanthate separately. The zinc content present in geological water samples in and around Tirupati was determined by the method developed and compared with the values obtained by Atomic Absorption Spectrophotometry. (author) 4 refs.; 3 figs.; 4 tabs

  8. Comparative substoichiometric extraction of cadmium with potassium salts of ethyl, propyl, butyl, pentyl and benzyl xanthates

    International Nuclear Information System (INIS)

    Chandrasekhar Reddy, P.; Rangamannar, B.

    1995-01-01

    A comparative study of the extractability of cadmium with potassium salts of ethyl, propyl, butyl, pentyl and benzyl xanthates into chloroform and a mixture of 1:4 pyridine and ethyl acetate from pH 1-7 buffers and sodium formate media, respectively, has been carried out employing an accurate and highly sensitive substoichiometric radiochemical method. The effect of foreign ions on the extractability was studied. The method developed was utilized for the determination of cadmium content in standard as well as in geological water samples. (author) 4 refs.; 5 figs.; 3 tabs

  9. Determination of gold by substoichiometric extraction with N-thioacetyl benzamide

    International Nuclear Information System (INIS)

    Madhumita Bag; Pabitra Chattopadhyay; Sukalyan Basu

    2011-01-01

    Estimation of gold has been successfully carried out by substoichiometric radiochemical solvent extraction method using a newly designed organic moiety, N-thioacetyl benzamide as extractant and chloroform as solvent at aqueous pH 4. The interference effects of different closely related diverse ions like Fe(III), Cu(II), Co(II), Zn(II), Ni(II) etc. were also critically studied. The validity of this method has been verified by the study of recovery of gold in mud samples. (author)

  10. Interface bonding in silicon oxide nanocontacts: interaction potentials and force measurements

    Science.gov (United States)

    Wierez-Kien, M.; Craciun, A. D.; Pinon, A. V.; Le Roux, S.; Gallani, J. L.; Rastei, M. V.

    2018-04-01

    The interface bonding between two silicon-oxide nanoscale surfaces has been studied as a function of atomic nature and size of contacting asperities. The binding forces obtained using various interaction potentials are compared with experimental force curves measured in vacuum with an atomic force microscope. In the limit of small nanocontacts (typically contact area which is altered by stretching speeds. The mean unbinding force is found to decrease as the contact spends time in the attractive regime. This contact weakening is featured by a negative aging coefficient which broadens and shifts the thermal-induced force distribution at low stretching speeds.

  11. Optical study of planar waveguides based on oxidized porous silicon impregnated with laser dyes

    Energy Technology Data Exchange (ETDEWEB)

    Chouket, A. [Unite de recherche de Spectroscopie Raman, Departement de Physique, Faculte des Sciences de Tunis, Elmanar 2092, Tunis (Tunisia); Charrier, J. [Laboratoire d' Optronique CNRS-UMR FOTON 6082, Universite de Rennes 1, ENSSAT-6 rue de Kerampont, BP 80518, 22305 Lannion Cedex (France); Elhouichet, H. [Unite de recherche de Spectroscopie Raman, Departement de Physique, Faculte des Sciences de Tunis, Elmanar 2092, Tunis (Tunisia)], E-mail: habib.elhouichet@fst.rnu.tn; Oueslati, M. [Unite de recherche de Spectroscopie Raman, Departement de Physique, Faculte des Sciences de Tunis, Elmanar 2092, Tunis (Tunisia)

    2009-05-15

    Oxidized porous silicon optical planar waveguides were elaborated and impregnated with rhodamine B and rhodamine 6G. The waveguiding, absorption, and photoluminescence properties of these impregnated waveguides were studied. Successful impregnation of the structure with laser dyes is shown from photoluminescence and reflectivity measurements. Furthermore, the reflectivity spectra prove the homogenous incorporation of both dye molecules inside the pores of the matrices. The refractive indices of waveguide layers were determined before and after dye impregnation to indicate the conservation of guiding conditions. The optical losses in the visible wavelengths are studied as a function of dye concentration. The dye absorption is the main reason for these losses.

  12. Electronic detection of surface plasmon polaritons by metal-oxide-silicon capacitor

    Directory of Open Access Journals (Sweden)

    Robert E. Peale

    2016-09-01

    Full Text Available An electronic detector of surface plasmon polaritons (SPPs is reported. SPPs optically excited on a metal surface using a prism coupler are detected by using a close-coupled metal-oxide-silicon (MOS capacitor. Incidence-angle dependence is explained by Fresnel transmittance calculations, which also are used to investigate the dependence of photo-response on structure dimensions. Electrodynamic simulations agree with theory and experiment and additionally provide spatial intensity distributions on and off the SPP excitation resonance. Experimental dependence of the photoresponse on substrate carrier type, carrier concentration, and back-contact biasing is qualitatively explained by simple theory of MOS capacitors.

  13. Atomic force microscopy-based repeated machining theory for nanochannels on silicon oxide surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Z.Q., E-mail: wangzhiqian@sia.cn [State Key Laboratory of Robotics, Shenyang Institute of Automation, CAS, Shenyang 110016 (China); Graduate University of the Chinese Academy of Sciences, Beijing 100049 (China); Jiao, N.D. [State Key Laboratory of Robotics, Shenyang Institute of Automation, CAS, Shenyang 110016 (China); Tung, S. [Department of Mechanical Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); Dong, Z.L. [State Key Laboratory of Robotics, Shenyang Institute of Automation, CAS, Shenyang 110016 (China)

    2011-02-01

    The atomic force microscopy (AFM)-based repeated nanomachining of nanochannels on silicon oxide surfaces is investigated both theoretically and experimentally. The relationships of the initial nanochannel depth vs. final nanochannel depth at a normal force are systematically studied. Using the derived theory and simulation results, the final nanochannel depth can be predicted easily. Meanwhile, if a nanochannel with an expected depth needs to be machined, a right normal force can be selected simply and easily in order to decrease the wear of the AFM tip. The theoretical analysis and simulation results can be effectively used for AFM-based fabrication of nanochannels.

  14. On the Origin of Light Emission in Silicon Rich Oxide Obtained by Low-Pressure Chemical Vapor Deposition

    OpenAIRE

    Aceves-Mijares, M.; González-Fernández, A. A.; López-Estopier, R.; Luna-López, A.; Berman-Mendoza, D.; Morales, A.; Falcony, C.; Domínguez, C.; Murphy-Arteaga, R.

    2012-01-01

    Silicon Rich Oxide (SRO) has been considered as a material to overcome the drawbacks of silicon to achieve optical functions. Various techniques can be used to produce it, including Low-Pressure Chemical Vapor Deposition (LPCVD). In this paper, a brief description of the studies carried out and discussions of the results obtained on electro-, cathode-, and photoluminescence properties of SRO prepared by LPCVD and annealed at 1,100°C are presented. The experimental results lead us to accept th...

  15. Fabrication of heterojunction solar cells by using microcrystalline hydrogenated silicon oxide film as an emitter

    International Nuclear Information System (INIS)

    Banerjee, Chandan; Sritharathikhun, Jaran; Konagai, Makoto; Yamada, Akira

    2008-01-01

    Wide gap, highly conducting n-type hydrogenated microcrystalline silicon oxide (μc-SiO : H) films were prepared by very high frequency plasma enhanced chemical vapour deposition at a very low substrate temperature (170 deg. C) as an alternative to amorphous silicon (a-Si : H) for use as an emitter layer of heterojunction solar cells. The optoelectronic properties of n-μc-SiO : H films prepared for the emitter layer are dark conductivity = 0.51 S cm -1 at 20 nm thin film, activation energy = 23 meV and E 04 = 2.3 eV. Czochralski-grown 380 μm thick p-type (1 0 0) oriented polished silicon wafers with a resistivity of 1-10 Ω cm were used for the fabrication of heterojunction solar cells. Photovoltaic parameters of the device were found to be V oc = 620 mV, J sc = 32.1 mA cm -2 , FF = 0.77, η = 15.32% (active area efficiency)

  16. ZnO transparent conductive oxide for thin film silicon solar cells

    Science.gov (United States)

    Söderström, T.; Dominé, D.; Feltrin, A.; Despeisse, M.; Meillaud, F.; Bugnon, G.; Boccard, M.; Cuony, P.; Haug, F.-J.; Faÿ, S.; Nicolay, S.; Ballif, C.

    2010-03-01

    There is general agreement that the future production of electric energy has to be renewable and sustainable in the long term. Photovoltaic (PV) is booming with more than 7GW produced in 2008 and will therefore play an important role in the future electricity supply mix. Currently, crystalline silicon (c-Si) dominates the market with a share of about 90%. Reducing the cost per watt peak and energy pay back time of PV was the major concern of the last decade and remains the main challenge today. For that, thin film silicon solar cells has a strong potential because it allies the strength of c-Si (i.e. durability, abundancy, non toxicity) together with reduced material usage, lower temperature processes and monolithic interconnection. One of the technological key points is the transparent conductive oxide (TCO) used for front contact, barrier layer or intermediate reflector. In this paper, we report on the versatility of ZnO grown by low pressure chemical vapor deposition (ZnO LP-CVD) and its application in thin film silicon solar cells. In particular, we focus on the transparency, the morphology of the textured surface and its effects on the light in-coupling for micromorph tandem cells in both the substrate (n-i-p) and superstrate (p-i-n) configurations. The stabilized efficiencies achieved in Neuchâtel are 11.2% and 9.8% for p-i-n (without ARC) and n-i-p (plastic substrate), respectively.

  17. Tribology study of reduced graphene oxide sheets on silicon substrate synthesized via covalent assembly.

    Science.gov (United States)

    Ou, Junfei; Wang, Jinqing; Liu, Sheng; Mu, Bo; Ren, Junfang; Wang, Honggang; Yang, Shengrong

    2010-10-19

    Reduced graphene oxide (RGO) sheets were covalently assembled onto silicon wafers via a multistep route based on the chemical adsorption and thermal reduction of graphene oxide (GO). The formation and microstructure of RGO were analyzed by X-ray photoelectron spectroscopy (XPS), attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy, Raman spectroscopy, and water contact angle (WCA) measurements. Characterization by atomic force microscopy (AFM) was performed to evaluate the morphology and microtribological behaviors of the samples. Macrotribological performance was tested on a ball-on-plate tribometer. Results show that the assembled RGO possesses good friction reduction and antiwear ability, properties ascribed to its intrinsic structure, that is, the covalent bonding to the substrate and self-lubricating property of RGO.

  18. Self-assisted GaAs nanowires with selectable number density on Silicon without oxide layer

    International Nuclear Information System (INIS)

    Bietti, S; Somaschini, C; Esposito, L; Sanguinetti, S; Frigeri, C; Fedorov, A; Geelhaar, L

    2014-01-01

    We present the growth of self-assisted GaAs nanowires (NWs) with selectable number density on bare Si(1 1 1), not covered by the silicon oxide. We determine the number density of the NWs by initially self-assembling GaAs islands on whose top a single NW is nucleated. The number density of the initial GaAs base islands can be tuned by droplet epitaxy and the same degree of control is then transferred to the NWs. This procedure is completely performed during a single growth in an ultra-high vacuum environment and requires neither an oxide layer covering the substrate, nor any pre-patterning technique. (paper)

  19. Effect of grain alignment on interface trap density of thermally oxidized aligned-crystalline silicon films

    Science.gov (United States)

    Choi, Woong; Lee, Jung-Kun; Findikoglu, Alp T.

    2006-12-01

    The authors report studies of the effect of grain alignment on interface trap density of thermally oxidized aligned-crystalline silicon (ACSi) films by means of capacitance-voltage (C-V) measurements. C-V curves were measured on metal-oxide-semiconductor (MOS) capacitors fabricated on ⟨001⟩-oriented ACSi films on polycrystalline substrates. From high-frequency C-V curves, the authors calculated a decrease of interface trap density from 2×1012to1×1011cm-2eV-1 as the grain mosaic spread in ACSi films improved from 13.7° to 6.5°. These results demonstrate the effectiveness of grain alignment as a process technique to achieve significantly enhanced performance in small-grained (⩽1μm ) polycrystalline Si MOS-type devices.

  20. Down-conversion luminescence from (Ce, Yb) co-doped oxygen-rich silicon oxides

    International Nuclear Information System (INIS)

    Heng, C. L.; Wang, T.; Su, W. Y.; Wu, H. C.; Yin, P. G.; Finstad, T. G.

    2016-01-01

    We have studied down-conversion photoluminescence (PL) from (Ce, Yb) co-doped “oxygen rich” silicon oxide films prepared by sputtering and annealing. The Ce"3"+ ∼510 nm PL is sensitive to the Ce concentration of the films and is much stronger for 3 at. % Ce than for 2 at. % Ce after annealing at 1200 °C. The PL emission and excitation spectroscopy results indicate that the excitation of Yb"3"+ is mainly through an energy transfer from Ce"3"+ to Yb"3"+, oxide defects also play a role in the excitation of Yb"3"+ after lower temperature (∼800 °C) annealing. The Ce"3"+ 510 nm photon excites mostly only one Yb"3"+ 980 nm photon. Temperature-dependent PL measurements suggest that the energy transfer from Ce"3"+ to Yb"3"+ is partly thermally activated.

  1. Charge separation technique for metal-oxide-silicon capacitors in the presence of hydrogen deactivated dopants

    International Nuclear Information System (INIS)

    Witczak, Steven C.; Winokur, Peter S.; Lacoe, Ronald C.; Mayer, Donald C.

    2000-01-01

    An improved charge separation technique for metal-oxide-silicon (MOS) capacitors is presented which accounts for the deactivation of substrate dopants by hydrogen at elevated irradiation temperatures or small irradiation biases. Using high-frequency capacitance-voltage (C-V) measurements, radiation-induced inversion voltage shifts are separated into components due to oxide trapped charge, interface traps and deactivated dopants, where the latter is computed from a reduction in Si capacitance. In the limit of no radiation-induced dopant deactivation, this approach reduces to the standard midgap charge separation technique used widely for the analysis of room-temperature irradiations. The technique is demonstrated on a p-type MOS capacitor irradiated with 60 Co γ-rays at 100 C and zero bias, where the dopant deactivation is significant

  2. The fabrication of highly ordered block copolymer micellar arrays: control of the separation distances of silicon oxide dots

    Science.gov (United States)

    Yoo, Hana; Park, Soojin

    2010-06-01

    We demonstrate the fabrication of highly ordered silicon oxide dotted arrays prepared from polydimethylsiloxane (PDMS) filled nanoporous block copolymer (BCP) films and the preparation of nanoporous, flexible Teflon or polyimide films. Polystyrene-block-poly(2-vinylpyridine) (PS-b-P2VP) films were annealed in toluene vapor to enhance the lateral order of micellar arrays and were subsequently immersed in alcohol to produce nano-sized pores, which can be used as templates for filling a thin layer of PDMS. When a thin layer of PDMS was spin-coated onto nanoporous BCP films and thermally annealed at a certain temperature, the PDMS was drawn into the pores by capillary action. PDMS filled BCP templates were exposed to oxygen plasma environments in order to fabricate silicon oxide dotted arrays. By addition of PS homopolymer to PS-b-P2VP copolymer, the separation distances of micellar arrays were tuned. As-prepared silicon oxide dotted arrays were used as a hard master for fabricating nanoporous Teflon or polyimide films by spin-coating polymer precursor solutions onto silicon patterns and peeling off. This simple process enables us to fabricate highly ordered nanoporous BCP templates, silicon oxide dots, and flexible nanoporous polymer patterns with feature size of sub-20 nm over 5 cm × 5 cm.

  3. The fabrication of highly ordered block copolymer micellar arrays: control of the separation distances of silicon oxide dots

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Hana; Park, Soojin, E-mail: spark@unist.ac.kr [Interdisciplinary School of Green Energy, Ulsan National Institute of Science and Technology, Banyeon-ri 100, Ulsan 689-798 (Korea, Republic of)

    2010-06-18

    We demonstrate the fabrication of highly ordered silicon oxide dotted arrays prepared from polydimethylsiloxane (PDMS) filled nanoporous block copolymer (BCP) films and the preparation of nanoporous, flexible Teflon or polyimide films. Polystyrene-block-poly(2-vinylpyridine) (PS-b-P2VP) films were annealed in toluene vapor to enhance the lateral order of micellar arrays and were subsequently immersed in alcohol to produce nano-sized pores, which can be used as templates for filling a thin layer of PDMS. When a thin layer of PDMS was spin-coated onto nanoporous BCP films and thermally annealed at a certain temperature, the PDMS was drawn into the pores by capillary action. PDMS filled BCP templates were exposed to oxygen plasma environments in order to fabricate silicon oxide dotted arrays. By addition of PS homopolymer to PS-b-P2VP copolymer, the separation distances of micellar arrays were tuned. As-prepared silicon oxide dotted arrays were used as a hard master for fabricating nanoporous Teflon or polyimide films by spin-coating polymer precursor solutions onto silicon patterns and peeling off. This simple process enables us to fabricate highly ordered nanoporous BCP templates, silicon oxide dots, and flexible nanoporous polymer patterns with feature size of sub-20 nm over 5 cm x 5 cm.

  4. Silicon carbide: A unique platform for metal-oxide-semiconductor physics

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Gang [Institute for Advanced Materials, Devices and Nanotechnology, Rutgers University, Piscataway, New Jersey 08854 (United States); Tuttle, Blair R. [Department of Physics and Astronomy, Vanderbilt University, Nashville, Tennessee 37235 (United States); Dhar, Sarit [Department of Physics, Auburn University, Auburn, Alabama 36849 (United States)

    2015-06-15

    A sustainable energy future requires power electronics that can enable significantly higher efficiencies in the generation, distribution, and usage of electrical energy. Silicon carbide (4H-SiC) is one of the most technologically advanced wide bandgap semiconductor that can outperform conventional silicon in terms of power handling, maximum operating temperature, and power conversion efficiency in power modules. While SiC Schottky diode is a mature technology, SiC power Metal Oxide Semiconductor Field Effect Transistors are relatively novel and there is large room for performance improvement. Specifically, major initiatives are under way to improve the inversion channel mobility and gate oxide stability in order to further reduce the on-resistance and enhance the gate reliability. Both problems relate to the defects near the SiO{sub 2}/SiC interface, which have been the focus of intensive studies for more than a decade. Here we review research on the SiC MOS physics and technology, including its brief history, the state-of-art, and the latest progress in this field. We focus on the two main scientific problems, namely, low channel mobility and bias temperature instability. The possible mechanisms behind these issues are discussed at the device physics level as well as the atomic scale, with the support of published physical analysis and theoretical studies results. Some of the most exciting recent progress in interface engineering for improving the channel mobility and fundamental understanding of channel transport is reviewed.

  5. Metal/silicon Interfaces and Their Oxidation Behavior - Photoemission Spectroscopy Analysis.

    Science.gov (United States)

    Yeh, Jyh-Jye

    Synchrotron radiation photoemission spectroscopy was used to study Ni/Si and Au/Si interface properties on the atomic scale at room temperature, after high temperature annealing and after oxygen exposures. Room temperature studies of metal/Si interfaces provide background for an understanding of the interface structure after elevated temperature annealing. Oxidation studies of Si surfaces covered with metal overlayers yield insight about the effect of metal atoms in the Si oxidation mechanisms and are useful in the identification of subtle differences in bonding relations between atoms at the metal/Si interfaces. Core level and valence band spectra with variable surface sensitivities were used to study the interactions between metal, Si, and oxygen for metal coverages and oxide thickness in the monolayer region. Interface morphology at the initial stage of metal/Si interface formation and after oxidation was modeled on the basis of the evolutions of metal and Si signals at different probing depths in the photoemission experiment. Both Ni/Si and Au/Si interfaces formed at room temperature have a diffusive region at the interface. This is composed of a layer of metal-Si alloy, formed by Si outdiffusion into the metal overlayer, above a layer of interstitial metal atoms in the Si substrate. Different atomic structures of these two regions at Ni/Si interface can account for the two different growth orientations of epitaxial Ni disilicides on the Si(111) surface after thermal annealing. Annealing the Au/Si interface at high temperature depletes all the Au atoms except for one monolayer of Au on the Si(111) surface. These phenomena are attributed to differences in the metal-Si chemical bonding relations associated with specific atomic structures. After oxygen exposures, both the Ni disilicide surface and Au covered Si surfaces (with different coverages and surface orderings) show silicon in higher oxidation states, in comparison to oxidized silicon on a clean surface

  6. Characterization of 10 μm thick porous silicon dioxide obtained by complex oxidation process for RF application

    International Nuclear Information System (INIS)

    Park, Jeong-Yong; Lee, Jong-Hyun

    2003-01-01

    This paper proposes a 10 μm thick oxide layer structure, which can be used as a substrate for RF circuits. The structure has been fabricated by anodic reaction and complex oxidation, which is a combined process of low temperature thermal oxidation (500 deg. C, for 1 h at H 2 O/O 2 ) and a rapid thermal oxidation (RTO) process (1050 deg. C, for 1 min). The electrical characteristics of oxidized porous silicon layer (OPSL) were almost the same as those of standard thermal silicon dioxide. The leakage current through the OPSL of 10 μm was about 100-500 pA in the range of 0-50 V. The average value of breakdown field was about 3.9 MV cm -1 . From the X-ray photo-electron spectroscopy (XPS) analysis, surface and internal oxide films of OPSL, prepared by complex process were confirmed to be completely oxidized and also the role of RTO process was important for the densification of porous silicon layer (PSL) oxidized at a lower temperature. For the RF-test of Si substrate with thick silicon dioxide layer, we have fabricated high performance passive devices such as coplanar waveguide (CPW) on OPSL substrate. The insertion loss of CPW on OPSL prepared by complex oxidation process was -0.39 dB at 4 GHz and similar to that of CPW on OPSL prepared by a temperature of 1050 deg. C (1 h at H 2 O/O 2 ). Also the return loss of CPW on OPSL prepared by complex oxidation process was -23 dB at 10 GHz, which is similar to that of CPW on OPSL prepared by high temperature

  7. Hydrogen incorporation and radiation induced dynamics in metal-oxide-silicon structures. A study using nuclear reaction analysis

    International Nuclear Information System (INIS)

    Briere, M.A.

    1993-07-01

    Resonant nuclear reaction analysis, using the 1 H( 15 N, αγ) 12 C reaction at 6.4 MeV, has been successfully applied to the investigation of hydrogen incorporation and radiation induced migration in metal-oxide-silicon structures. A preliminary study of the influence of processing parameters on the H content of thermal oxides, with and without gate material present, has been performed. It is found that the dominant source of hydrogen in Al gate devices and dry oxides is often contamination, likely in the form of adsorbed water vapor, formed upon exposure to room air after removal from the oxidation furnace. Concentrations of hydrogen in the bulk oxide as high as 3 10 20 cm -3 (Al gate), and as low as 1 10 18 cm -3 (poly Si-gate) have been observed. Hydrogen accumulation at the Si-SiO 2 interface has been reproducibly demonstrated for as-oxidized samples, as well as for oxides exposed to H 2 containing atmospheres during subsequent thermal processing. The migration of hydrogen, from the bulk oxide to the silicon-oxide interface during NRA, has been observed and intensively investigated. A direct correlation between the hydrogen content of the bulk oxide and the radiation generated oxide charges and interface states is presented. These data provide strong support for the important role of hydrogen in determining the radiation sensitivity of electronic devices. (orig.)

  8. Induced nano-scale self-formed metal-oxide interlayer in amorphous silicon tin oxide thin film transistors.

    Science.gov (United States)

    Liu, Xianzhe; Xu, Hua; Ning, Honglong; Lu, Kuankuan; Zhang, Hongke; Zhang, Xiaochen; Yao, Rihui; Fang, Zhiqiang; Lu, Xubing; Peng, Junbiao

    2018-03-07

    Amorphous Silicon-Tin-Oxide thin film transistors (a-STO TFTs) with Mo source/drain electrodes were fabricated. The introduction of a ~8 nm MoO x interlayer between Mo electrodes and a-STO improved the electron injection in a-STO TFT. Mo adjacent to the a-STO semiconductor mainly gets oxygen atoms from the oxygen-rich surface of a-STO film to form MoO x interlayer. The self-formed MoO x interlayer acting as an efficient interface modification layer could conduce to the stepwise internal transport barrier formation while blocking Mo atoms diffuse into a-STO layer, which would contribute to the formation of ohmic contact between Mo and a-STO film. It can effectively improve device performance, reduce cost and save energy for the realization of large-area display with high resolution in future.

  9. Novel Size and Surface Oxide Effects in Silicon Nanowires as Lithium Battery Anodes

    KAUST Repository

    McDowell, Matthew T.

    2011-09-14

    With its high specific capacity, silicon is a promising anode material for high-energy lithium-ion batteries, but volume expansion and fracture during lithium reaction have prevented implementation. Si nanostructures have shown resistance to fracture during cycling, but the critical effects of nanostructure size and native surface oxide on volume expansion and cycling performance are not understood. Here, we use an ex situ transmission electron microscopy technique to observe the same Si nanowires before and after lithiation and have discovered the impacts of size and surface oxide on volume expansion. For nanowires with native SiO2, the surface oxide can suppress the volume expansion during lithiation for nanowires with diameters <∼50 nm. Finite element modeling shows that the oxide layer can induce compressive hydrostatic stress that could act to limit the extent of lithiation. The understanding developed herein of how volume expansion and extent of lithiation can depend on nanomaterial structure is important for the improvement of Si-based anodes. © 2011 American Chemical Society.

  10. Iron oxide shell coating on nano silicon prepared from the sand for lithium-ion battery application

    Science.gov (United States)

    Furquan, Mohammad; Vijayalakshmi, S.; Mitra, Sagar

    2018-05-01

    Elemental silicon, due to its high specific capacity (4200 mAh g-1) and non-toxicity is expected to be an attractive anode material for Li-ion battery. But its huge expansion volume (> 300 %) during charging of battery, leads to pulverization and cracking in the silicon particles and causes sudden failure of the Li-ion battery. In this work, we have designed yolk-shell type morphology of silicon, prepared from carbon coated silicon nanoparticles soaked in aqueous solution of ferric nitrate and potassium hydroxide. The soaked silicon particles were dried and finally calcined at 800 °C for 30 minutes. The product obtained is deprived of carbon and has a kind of yolk-shell morphology of nano silicon with iron oxide coating (Si@Iron oxide). This material has been tested for half-cell lithium-ion battery configuration. The discharge capacity is found to be ≈ 600 mAh g-1 at a current rate of 1.0 A g-1 for 200 cycles. It has shown a stable performance as anode for Li-ion battery application.

  11. High performance multilayered nano-crystalline silicon/silicon-oxide light-emitting diodes on glass substrates

    Energy Technology Data Exchange (ETDEWEB)

    Darbari, S; Shahmohammadi, M; Mortazavi, M; Mohajerzadeh, S [Thin Film and Nano-Electronic Laboratory, School of ECE, University of Tehran, Tehran (Iran, Islamic Republic of); Abdi, Y [Nano-Physics Research Laboratory, Department of Physics, University of Tehran, Tehran (Iran, Islamic Republic of); Robertson, M; Morrison, T, E-mail: mohajer@ut.ac.ir [Department of Physics, Acadia University, Wolfville, NS (Canada)

    2011-09-16

    A low-temperature hydrogenation-assisted sequential deposition and crystallization technique is reported for the preparation of nano-scale silicon quantum dots suitable for light-emitting applications. Radio-frequency plasma-enhanced deposition was used to realize multiple layers of nano-crystalline silicon while reactive ion etching was employed to create nano-scale features. The physical characteristics of the films prepared using different plasma conditions were investigated using scanning electron microscopy, transmission electron microscopy, room temperature photoluminescence and infrared spectroscopy. The formation of multilayered structures improved the photon-emission properties as observed by photoluminescence and a thin layer of silicon oxy-nitride was then used for electrical isolation between adjacent silicon layers. The preparation of light-emitting diodes directly on glass substrates has been demonstrated and the electroluminescence spectrum has been measured.

  12. Electron-spin-resonance study of radiation-induced paramagnetic defects in oxides grown on (100) silicon substrates

    International Nuclear Information System (INIS)

    Kim, Y.Y.; Lenahan, P.M.

    1988-01-01

    We have used electron-spin resonance to investigate radiation-induced point defects in Si/SiO 2 structures with (100) silicon substrates. We find that the radiation-induced point defects are quite similar to defects generated in Si/SiO 2 structures grown on (111) silicon substrates. In both cases, an oxygen-deficient silicon center, the E' defect, appears to be responsible for trapped positive charge. In both cases trivalent silicon (P/sub b/ centers) defects are primarily responsible for radiation-induced interface states. In earlier electron-spin-resonance studies of unirradiated (100) substrate capacitors two types of P/sub b/ centers were observed; in oxides prepared in three different ways only one of these centers, the P/sub b/ 0 defect, is generated in large numbers by ionizing radiation

  13. On the Origin of Light Emission in Silicon Rich Oxide Obtained by Low-Pressure Chemical Vapor Deposition

    Directory of Open Access Journals (Sweden)

    M. Aceves-Mijares

    2012-01-01

    Full Text Available Silicon Rich Oxide (SRO has been considered as a material to overcome the drawbacks of silicon to achieve optical functions. Various techniques can be used to produce it, including Low-Pressure Chemical Vapor Deposition (LPCVD. In this paper, a brief description of the studies carried out and discussions of the results obtained on electro-, cathode-, and photoluminescence properties of SRO prepared by LPCVD and annealed at 1,100°C are presented. The experimental results lead us to accept that SRO emission properties are due to oxidation state nanoagglomerates rather than to nanocrystals. The emission mechanism is similar to Donor-Acceptor decay in semiconductors, and a wide emission spectrum, from 450 to 850 nm, has been observed. The results show that emission is a function of both silicon excess in the film and excitation energy. As a result different color emissions can be obtained by selecting the suitable excitation energy.

  14. Silicon oxynitride films deposited by reactive high power impulse magnetron sputtering using nitrous oxide as a single-source precursor

    Energy Technology Data Exchange (ETDEWEB)

    Hänninen, Tuomas, E-mail: tuoha@ifm.liu.se; Schmidt, Susann; Jensen, Jens; Hultman, Lars; Högberg, Hans [Thin Film Physics Division, Department of Physics, Chemistry, and Biology (IFM), Linköping University, Linköping SE-581 83 (Sweden)

    2015-09-15

    Silicon oxynitride thin films were synthesized by reactive high power impulse magnetron sputtering of silicon in argon/nitrous oxide plasmas. Nitrous oxide was employed as a single-source precursor supplying oxygen and nitrogen for the film growth. The films were characterized by elastic recoil detection analysis, x-ray photoelectron spectroscopy, x-ray diffraction, x-ray reflectivity, scanning electron microscopy, and spectroscopic ellipsometry. Results show that the films are silicon rich, amorphous, and exhibit a random chemical bonding structure. The optical properties with the refractive index and the extinction coefficient correlate with the film elemental composition, showing decreasing values with increasing film oxygen and nitrogen content. The total percentage of oxygen and nitrogen in the films is controlled by adjusting the gas flow ratio in the deposition processes. Furthermore, it is shown that the film oxygen-to-nitrogen ratio can be tailored by the high power impulse magnetron sputtering-specific parameters pulse frequency and energy per pulse.

  15. Effect of the temperature and dew point of the decarburization process on the oxide subscale of a 3% silicon steel

    Energy Technology Data Exchange (ETDEWEB)

    Cesar, Maria das Gracas M.M. E-mail: gracamelo@acesita.com.br; Mantel, Marc J

    2003-01-01

    The oxide subscale formed on the decarburization annealing of 3% Si-Fe was investigated using microscopy and spectroscopy techniques. It was found that the morphology as well as the molecular structure of the subscale are affected by temperature and dew point. The results suggest that there is an optimum level of internal oxidation and an optimum fayalite/silica ratio in the subscale to achieve a oriented grain silicon steel having a continuous and smooth ceramic film and low core loss.

  16. Characterization of Interface State in Silicon Carbide Metal Oxide Semiconductor Capacitors

    Science.gov (United States)

    Kao, Wei-Chieh

    Silicon carbide (SiC) has always been considered as an excellent material for high temperature and high power devices. Since SiC is the only compound semiconductor whose native oxide is silicon dioxide (SiO2), it puts SiC in a unique position. Although SiC metal oxide semiconductor (MOS) technology has made significant progress in recent years, there are still a number of issues to be overcome before more commercial SiC devices can enter the market. The prevailing issues surrounding SiC MOSFET devices are the low channel mobility, the low quality of the oxide layer and the high interface state density at the SiC/SiO2 interface. Consequently, there is a need for research to be performed in order to have a better understanding of the factors causing the poor SiC/SiO2 interface properties. In this work, we investigated the generation lifetime in SiC materials by using the pulsed metal oxide semiconductor (MOS) capacitor method and measured the interface state density distribution at the SiC/SiO2 interface by using the conductance measurement and the high-low frequency capacitance technique. These measurement techniques have been performed on n-type and p-type SiC MOS capacitors. In the course of our investigation, we observed fast interface states at semiconductor-dielectric interfaces in SiC MOS capacitors that underwent three different interface passivation processes, such states were detected in the nitrided samples but not observed in PSG-passivated samples. This result indicate that the lack of fast states at PSG-passivated interface is one of the main reasons for higher channel mobility in PSG MOSFETs. In addition, the effect of mobile ions in the oxide on the response time of interface states has been investigated. In the last chapter we propose additional methods of investigation that can help elucidate the origin of the particular interface states, enabling a more complete understanding of the SiC/SiO2 material system.

  17. On the growth of native oxides on hydrogen-terminated silicon surfaces in dark and under illumination with light

    NARCIS (Netherlands)

    Kovalgin, Alexeij Y.; Zinine, A.; Bankras, R.G.; Wormeester, Herbert; Poelsema, Bene; Schmitz, Jurriaan

    2006-01-01

    After a cleaning procedure, a silicon surface can be terminated by Si-OH groups which results in a high chemical activity. As it is accepted, after removing the wet-chemically grown oxide layer using an HF solution, the surface becomes terminated with Si-H groups. This results in a chemically stable

  18. Polycrystalline silicon ring resonator photodiodes in a bulk complementary metal-oxide-semiconductor process.

    Science.gov (United States)

    Mehta, Karan K; Orcutt, Jason S; Shainline, Jeffrey M; Tehar-Zahav, Ofer; Sternberg, Zvi; Meade, Roy; Popović, Miloš A; Ram, Rajeev J

    2014-02-15

    We present measurements on resonant photodetectors utilizing sub-bandgap absorption in polycrystalline silicon ring resonators, in which light is localized in the intrinsic region of a p+/p/i/n/n+ diode. The devices, operating both at λ=1280 and λ=1550  nm and fabricated in a complementary metal-oxide-semiconductor (CMOS) dynamic random-access memory emulation process, exhibit detection quantum efficiencies around 20% and few-gigahertz response bandwidths. We observe this performance at low reverse biases in the range of a few volts and in devices with dark currents below 50 pA at 10 V. These results demonstrate that such photodetector behavior, previously reported by Preston et al. [Opt. Lett. 36, 52 (2011)], is achievable in bulk CMOS processes, with significant improvements with respect to the previous work in quantum efficiency, dark current, linearity, bandwidth, and operating bias due to additional midlevel doping implants and different material deposition. The present work thus offers a robust realization of a fully CMOS-fabricated all-silicon photodetector functional across a wide wavelength range.

  19. Spike-Timing Dependent Plasticity in Unipolar Silicon Oxide RRAM Devices.

    Science.gov (United States)

    Zarudnyi, Konstantin; Mehonic, Adnan; Montesi, Luca; Buckwell, Mark; Hudziak, Stephen; Kenyon, Anthony J

    2018-01-01

    Resistance switching, or Resistive RAM (RRAM) devices show considerable potential for application in hardware spiking neural networks (neuro-inspired computing) by mimicking some of the behavior of biological synapses, and hence enabling non-von Neumann computer architectures. Spike-timing dependent plasticity (STDP) is one such behavior, and one example of several classes of plasticity that are being examined with the aim of finding suitable algorithms for application in many computing tasks such as coincidence detection, classification and image recognition. In previous work we have demonstrated that the neuromorphic capabilities of silicon-rich silicon oxide (SiO x ) resistance switching devices extend beyond plasticity to include thresholding, spiking, and integration. We previously demonstrated such behaviors in devices operated in the unipolar mode, opening up the question of whether we could add plasticity to the list of features exhibited by our devices. Here we demonstrate clear STDP in unipolar devices. Significantly, we show that the response of our devices is broadly similar to that of biological synapses. This work further reinforces the potential of simple two-terminal RRAM devices to mimic neuronal functionality in hardware spiking neural networks.

  20. Direct exchange between silicon nanocrystals and tunnel oxide traps under illumination on single electron photodetector

    Energy Technology Data Exchange (ETDEWEB)

    Chatbouri, S., E-mail: Samir.chatbouri@yahoo.com; Troudi, M.; Sghaier, N.; Kalboussi, A. [Avenue de I’environnement, Université de Monastir, Laboratoire de Micro électronique et Instrumentation (LR13ES12), Faculté des Sciences de Monastir (Tunisia); Aimez, V. [Université de Sherbrooke, Laboratoire Nanotechnologies et Nanosystémes (UMI-LN2 3463), Université de Sherbrooke—CNRS—INSA de Lyon-ECL-UJF-CPE Lyon, Institut Interdisciplinaire d’Innovation Technologique (Canada); Drouin, D. [Avenue de I’environnement, Université de Monastir, Laboratoire de Micro électronique et Instrumentation (LR13ES12), Faculté des Sciences de Monastir (Tunisia); Souifi, A. [Institut des Nanotechnologies de Lyon—site INSA de Lyon, UMR CNRS 5270 (France)

    2016-09-15

    In this paper we present the trapping of photogenerated charge carriers for 300 s resulted by their direct exchange under illumination between a few silicon nanocrystals (ncs-Si) embedded in an oxide tunnel layer (SiO{sub x} = 1.5) and the tunnel oxide traps levels for a single electron photodetector (photo-SET or nanopixel). At first place, the presence of a photocurrent limited in the inversion zone under illumination in the I–V curves confirms the creation of a pair electron/hole (e–h) at high energy. This photogenerated charge carriers can be trapped in the oxide. Using the capacitance-voltage under illumination (the photo-CV measurements) we show a hysteresis chargement limited in the inversion area, indicating that the photo-generated charge carriers are stored at traps levels at the interface and within ncs-Si. The direct exchange of the photogenerated charge carriers between the interface traps levels and the ncs-Si contributed on the photomemory effect for 300 s for our nanopixel at room temperature.

  1. Thermal oxidation effect on structural and optical properties of heavily doped phosphorus polycrystalline silicon films

    Energy Technology Data Exchange (ETDEWEB)

    Birouk, B.; Madi, D. [Universite de Jijel, Laboratoire d' Etudes et de Modelisation en Electrotechnique (LAMEL), Cite Ouled Aissa, BP 98, Jijel (Algeria)

    2011-08-15

    The study reported in this paper contributes to better understanding the thermal oxidation effect on structural and optical properties of polycrystalline silicon heavily in situ P-LPCVD films. The deposits, doped at levels 3 x 10{sup 19} and 1.6 x 10{sup 20} cm{sup -3}, have been elaborated from silane decomposition (400 mTorrs, 605 C) on monosilicon substrate oriented left angle 111 right angle. The thermal oxidation was performed at temperatures: 850 C during 1 hour, 1000, 1050, and 1100 C during 15 minutes. The XRD spectra analysis pointed out significant left angle 111 right angle texture evolution, while in the case of left angle 220 right angle and left angle 311 right angle textures, the intensities are practically invariant (variations fall in the uncertainty intervals). The optical characterizations showed that refractive index and absorption coefficient are very sensitive to the oxidation treatment, mainly when the doping level is not very high. We think that atomic oxygen acts as defects passivating agent leading to carriers' concentration increasing. Besides, the optical behavior is modeled in visible and near infrared, by a seven-term polynomial function n {sup 2}=f({lambda} {sup 2}), with alternate signs, instead of theoretically unlimited terms number from Drude's model. It has been shown that fitting parameters fall on Gaussian curves like they do in the theoretical model. (orig.)

  2. Hot-pressed silicon nitride with various lanthanide oxides as sintering additives

    Science.gov (United States)

    Ueno, K.; Toibana, Y.

    1984-01-01

    The effects of addition of various lanthanide oxides and their mixture with Y2O3 on the sintering of Si3N4 were investigated. The addition of simple and mixed lanthanide oxides promoted the densification of Si3N4 in hot-pressing at 1800 C under 300-400kg/ centimeters squared for 60 min. The crystallization of yttrium and lanthanide-silicon oxynitrides which was observed inn the sintered body containing yttrium-lanthanide mixed oxides as additives led to the formation of a highly refractory Si3N4 ceramic having a bending strength of 82 and 84 kg/millimeters squared at room temperature and 1300 C respectively. In a Y2O3+La2O3 system, a higher molar ratio of La2O3 to Y2O3 gave a higher hardness and strength at high temperatures. It was found that 90 min was an optimum sintering time for the highest strength.

  3. Surface State Capture Cross-Section at the Interface between Silicon and Hafnium Oxide

    Directory of Open Access Journals (Sweden)

    Fu-Chien Chiu

    2013-01-01

    Full Text Available The interfacial properties between silicon and hafnium oxide (HfO2 are explored by the gated-diode method and the subthreshold measurement. The density of interface-trapped charges, the current induced by surface defect centers, the surface recombination velocity, and the surface state capture cross-section are obtained in this work. Among the interfacial properties, the surface state capture cross-section is approximately constant even if the postdeposition annealing condition is changed. This effective capture cross-section of surface states is about 2.4 × 10−15 cm2, which may be an inherent nature in the HfO2/Si interface.

  4. Silicon oxide: a non-innocent surface for molecular electronics and nanoelectronics studies.

    Science.gov (United States)

    Yao, Jun; Zhong, Lin; Natelson, Douglas; Tour, James M

    2011-02-02

    Silicon oxide (SiO(x)) has been widely used in many electronic systems as a supportive and insulating medium. Here, we demonstrate various electrical phenomena such as resistive switching and related nonlinear conduction, current hysteresis, and negative differential resistance intrinsic to a thin layer of SiO(x). These behaviors can largely mimic numerous electrical phenomena observed in molecules and other nanomaterials, suggesting that substantial caution should be paid when studying conduction in electronic systems with SiO(x) as a component. The actual electrical phenomena can be the result of conduction from SiO(x) at a post soft-breakdown state and not the presumed molecular or nanomaterial component. These electrical properties and the underlying mechanisms are discussed in detail.

  5. Ultrathin silicon dioxide layers with a low leakage current density formed by chemical oxidation of Si

    Science.gov (United States)

    Asuha,; Kobayashi, Takuya; Maida, Osamu; Inoue, Morio; Takahashi, Masao; Todokoro, Yoshihiro; Kobayashi, Hikaru

    2002-10-01

    Chemical oxidation of Si by use of azeotrope of nitric acid and water can form 1.4-nm-thick silicon dioxide layers with a leakage current density as low as those of thermally grown SiO2 layers. The capacitance-voltage (C-V) curves for these ultrathin chemical SiO2 layers have been measured due to the low leakage current density. The leakage current density is further decreased to approx1/5 (cf. 0.4 A/cm2 at the forward gate bias of 1 V) by post-metallization annealing at 200 degC in hydrogen. Photoelectron spectroscopy and C-V measurements show that this decrease results from (i) increase in the energy discontinuity at the Si/SiO2 interface, and (ii) elimination of Si/SiO2 interface states and SiO2 gap states.

  6. Optical and electrical characteristics of zirconium oxide thin films deposited on silicon substrates by spray pyrolysis

    International Nuclear Information System (INIS)

    Aguilar-Frutis, M.; Araiza, J.J.; Falcony, C.; Garcia, M.

    2002-01-01

    The optical and electrical characteristics of zirconium oxide thin films deposited by spray pyrolysis on silicon substrates are reported. The films were deposited from a spraying solution of zirconium acetylacetonate in N,N-dimethylformamide using an ultrasonic mist generator on (100) Si substrates. The substrate temperature during deposition was in the range of 400 to 600 grad C. Deposition rates up to 16 A/sec were obtained depending on the spraying solution concentration and on the substrate temperature. A refraction index of the order of 2.0 was measured on these films by ellipsometry. The electrical characteristics of the films were determined from the capacitance and current versus voltage measurements. The addition of water mist during the spraying deposition process was also studied in the characteristics of the films. (Authors)

  7. Methods for oxygen/uranium ratio determination in substoichiometric uranium dioxide

    International Nuclear Information System (INIS)

    Baranov, V.G.; Godin, Yu.G.; S'edin, Yu.D.; Kosykh, V.G.; Nepryakhin, A.M.; Komarenko, F.F.; Kutyreva, G.A.

    1994-01-01

    Investigations are performed into a possibility to use the methods of thermal gravimetric analysis, gas chromatography, hydration-dehydration, and e.m.f. of high-temperature solid-electrode galvanic cell for determining O-U atomic ratio in UO 2-x . It is shown that the investigated methods have an analysis error of ± 0.001 O/U units. However, the e.m.f. method, which feature a high accuracy near stoichiometry can be applied only within the limits of UO 2-x homogeneity. A possibility is shown to expend the area of e.m.f. method application during the analysis of substoichiometric uranium dioxide. 9 refs.; 1 tab

  8. Plasma surface oxidation of 316L stainless steel for improving adhesion strength of silicone rubber coating to metal substrate

    Energy Technology Data Exchange (ETDEWEB)

    Latifi, Afrooz, E-mail: afroozlatifi@yahoo.com [Department of Biomaterials, Biomedical Engineering Faculty, Science and Research Branch, Islamic Azad University, Tehran (Iran, Islamic Republic of); Imani, Mohammad [Novel Drug Delivery Systems Dept., Iran Polymer and Petrochemical Institute, P.O. Box 14965/115, Tehran (Iran, Islamic Republic of); Khorasani, Mohammad Taghi [Biomaterials Dept., Iran Polymer and Petrochemical Institute, P.O. Box 14965/159, Tehran (Iran, Islamic Republic of); Daliri Joupari, Morteza [Animal and Marine Biotechnology Dept., National Institute of Genetic Engineering and Biotechnology, P.O. Box 14965/161, Tehran (Iran, Islamic Republic of)

    2014-11-30

    Highlights: • Stainless steel 316L was surface modified by plasma surface oxidation (PSO) and silicone rubber (SR) coating. • On the PSO substrates, concentration of oxide species was increased ca. 2.5 times comparing to non-PSO substrates. • The surface wettability was improved to 12.5°, in terms of water contact angle, after PSO. • Adhesion strength of SR coating on the PSO substrates was improved by more than two times comparing to non-PSO ones. • After pull-off test, the fractured area patterns for SR coating were dependent on the type of surface modifications received. - Abstract: Stainless steel 316L is one of the most widely used materials for fabricating of biomedical devices hence, improving its surface properties is still of great interest and challenging in biomaterial sciences. Plasma oxidation, in comparison to the conventional chemical or mechanical methods, is one of the most efficient methods recently used for surface treatment of biomaterials. Here, stainless steel specimens were surface oxidized by radio-frequency plasma irradiation operating at 34 MHz under pure oxygen atmosphere. Surface chemical composition of the samples was significantly changed after plasma oxidation by appearance of the chromium and iron oxides on the plasma-oxidized surface. A wettable surface, possessing high surface energy (83.19 mN m{sup −1}), was observed after plasma oxidation. Upon completion of the surface modification process, silicone rubber was spray coated on the plasma-treated stainless steel surface. Morphology of the silicone rubber coating was investigated by scanning electron microscopy (SEM). A uniform coating was formed on the oxidized surface with no delamination at polymer–metal interface. Pull-off tests showed the lowest adhesion strength of coating to substrate (0.12 MPa) for untreated specimens and the highest (0.89 MPa) for plasma-oxidized ones.

  9. Experimental studies of thorium ion implantation from pulse laser plasma into thin silicon oxide layers

    Science.gov (United States)

    Borisyuk, P. V.; Chubunova, E. V.; Lebedinskii, Yu Yu; Tkalya, E. V.; Vasilyev, O. S.; Yakovlev, V. P.; Strugovshchikov, E.; Mamedov, D.; Pishtshev, A.; Karazhanov, S. Zh

    2018-05-01

    We report the results of experimental studies related to implantation of thorium ions into thin silicon dioxide by pulsed plasma flux expansion. Thorium ions were generated by laser ablation from a metal target, and the ionic component of the laser plasma was accelerated in an electric field created by the potential difference (5, 10 and 15 kV) between the ablated target and a SiO2/Si (0 0 1) sample. The laser ablation system installed inside the vacuum chamber of the electron spectrometer was equipped with a YAG:Nd3  +  laser having a pulse energy of 100 mJ and time duration of 15 ns in the Q-switched regime. The depth profile of thorium atoms implanted into the 10 nm thick subsurface areas together with their chemical state as well as the band gap of the modified silicon oxide at different conditions of implantation processes were studied by means of x-ray photoelectron spectroscopy and reflected electron energy loss spectroscopy methods. Analysis of the chemical composition showed that the modified silicon oxide film contains complex thorium silicates. Depending on the local concentration of thorium atoms, the experimentally established band gaps were located in the range 6.0–9.0 eV. Theoretical studies of the optical properties of the SiO2 and ThO2 crystalline systems were performed by ab initio calculations within hybrid functional. The optical properties of the SiO2/ThO2 composite were interpreted on the basis of the Bruggeman effective medium approximation. A quantitative assessment of the yield of isomeric nuclei in ‘hot’ laser plasma at the early stages of expansion was performed. The estimates made with experimental results demonstrated that the laser implantation of thorium ions into the SiO2 matrix can be useful for further research of low-lying isomeric transitions in a 229Th isotope with energy of 7.8 +/- 0.5 eV.

  10. Influence of silicon on hot-dip aluminizing process and subsequent oxidation for preparing hydrogen/tritium permeation barrier

    Energy Technology Data Exchange (ETDEWEB)

    Han, Shilei; Li, Hualing; Wang, Shumao; Jiang, Lijun; Liu, Xiaopeng [Energy Materials and Technology Research Institute, General Research Institute for Nonferrous Metals, Beijing 100088 (China)

    2010-04-15

    The development of the International Thermonuclear Experimental Reactor (ITER) requires the production of a material capable of acting as a hydrogen/tritium permeation barrier on low activation steel. It is well known that thin alumina layer can reduce the hydrogen permeation rate by several orders of magnitude. A technology is introduced here to form a ductile Fe/Al intermetallic layer on the steel with an alumina over-layer. This technology, consisting of two main steps, hot-dip aluminizing (HDA) and subsequent oxidation behavior, seems to be a promising coating method to fulfill the required goals. According to the experiments that have been done in pure Al, the coatings were inhomogeneous and too thick. Additionally, a large number of cracks and porous band could be observed. In order to solve these problems, the element silicon was added to the aluminum melt with a nominal composition. The influence of silicon on the aluminizing and following oxidation process was investigated. With the addition of silicon into the aluminum melt, the coating became thinner and more homogeneous. The effort of the silicon on the oxidation behavior was observed as well concerning the suppression of porous band and cracks. (author)

  11. Complete suppression of boron transient-enhanced diffusion and oxidation-enhanced diffusion in silicon using localized substitutional carbon incorporation

    Science.gov (United States)

    Carroll, M. S.; Chang, C.-L.; Sturm, J. C.; Büyüklimanli, T.

    1998-12-01

    In this letter, we show the ability, through introduction of a thin Si1-x-yGexCy layer, to eliminate the enhancement of enhanced boron diffusion in silicon due to an oxidizing surface or ion implant damage. This reduction of diffusion is accomplished through a low-temperature-grown thin epitaxial Si1-x-yGexCy layer which completely filters out excess interstitials introduced by oxidation or ion implant damage. We also quantify the oxidation-enhanced diffusion (OED) and transient-enhanced diffusion (TED) dependence on substitutional carbon level, and further report both the observation of carbon TED and OED, and its dependence on carbon levels.

  12. Preparation of silicon carbide-supported vanadium oxide and its application of removing NO by ammonia

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Zi-Bo; Xu, Xu [Yangzhou University, College of Environmental Science and Engineering, Yangzhou, Jiangsu (China); Bai, Shu-Li [Wuyi University, College of Chemical and Environmental Engineering, Jiangmen, Guangdong (China); Guan, Yu-Jiang; Jiang, Sheng-Tao [Taizhou University, Environmental Engineering, Taizhou, Zhejiang (China)

    2017-03-15

    The aim of this work was to study the preparation of SiC-supported V{sub 2}O{sub 5} catalysts and the kinetics on selective catalytic reduction for NO with NH{sub 3} on the catalysts. Using incipient wetness impregnation methods, vanadium oxide was applied to silicon carbide to prepare a SiC-supported vanadium oxide. X-ray photoelectron spectroscopy analysis confirmed that V{sub 2}O{sub 5} existed in the prepared materials. Using the prepared materials as catalysts, selective catalytic reduction for NO by NH{sub 3} has been analyzed, and reaction kinetics on the catalysts was studied at 150-300 C. The obtained results showed that the reduction reaction on the catalysts is close to zero-order kinetics with respect to NH{sub 3}, first-order with respect to NO, and half-order to O{sub 2}. Apparent activation energy for the reduction reaction was found to be 38 kJ mol{sup -1}. The prepared materials are stable and reusable. (orig.)

  13. Oxidation behaviour of silicon-free tungsten alloys for use as the first wall material

    Science.gov (United States)

    Koch, F.; Brinkmann, J.; Lindig, S.; Mishra, T. P.; Linsmeier, Ch

    2011-12-01

    The use of self-passivating tungsten alloys as armour material of the first wall of a fusion power reactor may be advantageous concerning safety issues. In earlier studies good performance of the system W-Cr-Si was demonstrated. Thin films of such alloys showed a strongly reduced oxidation rate compared to pure tungsten. However, the formation of brittle tungsten silicides may be disadvantageous for the powder metallurgical production of bulk W-Cr-Si alloys if a good workability is needed. This paper shows the results of screening tests to identify suitable silicon-free alloys with distinguished self-passivation and a potentially good workability. Of all the tested systems W-Cr-Ti alloys showed the most promising results. The oxidation rate was even lower than the one of W-Cr-Si alloys, the reduction factor was about four orders of magnitude compared to pure tungsten. This performance could be conserved even if the content of alloying elements was reduced.

  14. Oxidation behaviour of silicon-free tungsten alloys for use as the first wall material

    International Nuclear Information System (INIS)

    Koch, F; Brinkmann, J; Lindig, S; Mishra, T P; Linsmeier, Ch

    2011-01-01

    The use of self-passivating tungsten alloys as armour material of the first wall of a fusion power reactor may be advantageous concerning safety issues. In earlier studies good performance of the system W-Cr-Si was demonstrated. Thin films of such alloys showed a strongly reduced oxidation rate compared to pure tungsten. However, the formation of brittle tungsten silicides may be disadvantageous for the powder metallurgical production of bulk W-Cr-Si alloys if a good workability is needed. This paper shows the results of screening tests to identify suitable silicon-free alloys with distinguished self-passivation and a potentially good workability. Of all the tested systems W-Cr-Ti alloys showed the most promising results. The oxidation rate was even lower than the one of W-Cr-Si alloys, the reduction factor was about four orders of magnitude compared to pure tungsten. This performance could be conserved even if the content of alloying elements was reduced.

  15. Gadolinium oxide coated fully depleted silicon-on-insulator transistors for thermal neutron dosimetry

    Energy Technology Data Exchange (ETDEWEB)

    Vitale, Steven A., E-mail: steven.vitale@ll.mit.edu; Gouker, Pascale M.

    2013-09-01

    Fully depleted silicon-on-insulator transistors coated with gadolinium oxide are shown to be effective thermal neutron dosimeters. The theoretical neutron detection efficiency is calculated to be higher for Gd{sub 2}O{sub 3} than for other practical converter materials. Proof-of-concept dosimeter devices were fabricated and tested during thermal neutron irradiation. The transistor current changes linearly with neutron dose, consistent with increasing positive charge in the SOI buried oxide layer generated by ionization from high energy {sup 157}Gd(n,γ){sup 158}Gd conversion electrons. The measured neutron sensitivity is approximately 1/6 the maximum theoretical value, possibly due to electron–hole recombination or conversion electron loss in interconnect wiring above the transistors. -- Highlights: • A novel Gd{sub 2}O{sub 3} coated FDSOI MOSFET thermal neutron dosimeter is presented. • Dosimeter can detect charges generated from {sup 157}Gd(n,γ){sup 158}Gd conversion electrons. • Measured neutron sensitivity is comparable to that calculated theoretically. • Dosimeter requires zero power during operation, enabling new application areas.

  16. Silicon effects on formation of EPO oxide coatings on aluminum alloys

    International Nuclear Information System (INIS)

    Wang, L.; Nie, X.

    2006-01-01

    Electrolytic plasma processes (EPP) can be used for cleaning, metal-coating, carburizing, nitriding, and oxidizing. Electrolytic plasma oxidizing (EPO) is an advanced technique to deposit thick and hard ceramic coatings on a number of aluminum alloys. However, the EPO treatment on Al-Si alloys with a high Si content has rarely been reported. In this research, an investigation was conducted to clarify the effects of silicon contents on the EPO coating formation, morphology, and composition. Cast hypereutectic 390 alloys (∼ 17% Si) and hypoeutectic 319 alloys (∼ 7% Si) were chosen as substrates. The coating morphology, composition, and microstructure of the EPO coatings on those substrates were investigated using scanning electron microscopy (SEM) with energy dispersive X-ray (EDX) analysis and X-ray diffraction (XRD). A stylus roughness tester was used for surface roughness measurement. It was found that the EPO process had four stages where each stage was corresponding to various coating surface morphology, composition, and phase structures, characterised by different coating growth mechanisms

  17. Effects of RF plasma treatment on spray-pyrolyzed copper oxide films on silicon substrates

    Science.gov (United States)

    Madera, Rozen Grace B.; Martinez, Melanie M.; Vasquez, Magdaleno R., Jr.

    2018-01-01

    The effects of radio-frequency (RF) argon (Ar) plasma treatment on the structural, morphological, electrical and compositional properties of the spray-pyrolyzed p-type copper oxide films on n-type (100) silicon (Si) substrates were investigated. The films were successfully synthesized using 0.3 M copper acetate monohydrate sprayed on precut Si substrates maintained at 350 °C. X-ray diffraction revealed cupric oxide (CuO) with a monoclinic structure. An apparent improvement in crystallinity was realized after Ar plasma treatment, attributed to the removal of residues contaminating the surface. Scanning electron microscope images showed agglomerated monoclinic grains and revealed a reduction in size upon plasma exposure induced by the sputtering effect. The current-voltage characteristics of CuO/Si showed a rectifying behavior after Ar plasma exposure with an increase in turn-on voltage. Four-point probe measurements revealed a decrease in sheet resistance after plasma irradiation. Fourier transform infrared spectral analyses also showed O-H and C-O bands on the films. This work was able to produce CuO thin films via spray pyrolysis on Si substrates and enhancement in their properties by applying postdeposition Ar plasma treatment.

  18. Treatment of transparent conductive oxides by laser processes for the development of Silicon photovoltaic cells

    International Nuclear Information System (INIS)

    Canteli Perez-Caballero, D.

    2015-01-01

    Transparent conductive oxides (TCOs) are heavily doped oxides with high transparency in the visible range of the spectrum and a very low sheet resistance, making them very attractive for applications in optoelectronic devices. TCOs are widely found in many different areas such as low emissivity windows, electric contacts in computers, televisions or portable devices, and, specially, in the photovoltaic (PV) industry. PV industry is mainly based on mono- and multicrystalline silicon, where TCOs are used as anti-reflective coatings, but the search for cheaper, alternative technologies has led to the development of thin film PV technologies, where TCOs are used as transparent contacts. With the maturation of the thin film PV industry, laser sources have become an essential tool, allowing the improvement of some industrial processes and the development of new ones. Because of the interest on a deeper understanding of the interaction processes between laser light and TCOs, the laser ablation of three of the most important TCOs has been studied in depth in the present work. (Author)

  19. Transparent conducting oxide contacts and textured metal back reflectors for thin film silicon solar cells

    Science.gov (United States)

    Franken, R. H.-J.

    2006-09-01

    With the growing population and the increasing environmental problems of the 'common' fossil and nuclear energy production, the need for clean and sustainable energy sources is evident. Solar energy conversion, such as in photovoltaic (PV) systems, can play a major role in the urgently needed energy transition in electricity production. At the present time PV module production is dominated by the crystalline wafer technology. Thin film silicon technology is an alternative solar energy technology that operates at lower efficiencies, however, it has several significant advantages, such as the possibility of deposition on cheap (flexible) substrates and the much smaller silicon material consumption. Because of the small thickness of the solar cells, light trapping schemes are needed in order to obtain enough light absorption and current generation. This thesis describes the research on thin film silicon solar cells with the focus on the optimization of the transparent conducting oxide (TCO) layers and textured metal Ag substrate layers for the use as enhanced light scattering back reflectors in n-i-p type of solar cells. First we analyzed ZnO:Al (TCO) layers deposited in an radio frequent (rf) magnetron deposition system equipped with a 7 inch target. We have focused on the improvement of the electrical properties without sacrificing the optical properties by increasing the mobility and decreasing the grain boundary density. Furthermore, we described some of the effects on light trapping of ZnO:Al enhanced back reflectors. The described effects are able to explain the observed experimental data. Furthermore, we present a relation between the surface morphology of the Ag back contact and the current enhancement in microcrystalline (muc-Si:H) solar cells. We show the importance of the lateral feature sizes of the Ag surface on the light scattering and introduce a method to characterize the quality of the back reflector by combining the vertical and lateral feature sizes

  20. Single-electron-occupation metal-oxide-semiconductor quantum dots formed from efficient poly-silicon gate layout

    Energy Technology Data Exchange (ETDEWEB)

    Carroll, Malcolm S.; rochette, sophie; Rudolph, Martin; Roy, A. -M.; Curry, Matthew Jon; Ten Eyck, Gregory A.; Manginell, Ronald P.; Wendt, Joel R.; Pluym, Tammy; Carr, Stephen M; Ward, Daniel Robert; Lilly, Michael; pioro-ladriere, michel

    2017-07-01

    We introduce a silicon metal-oxide-semiconductor quantum dot structure that achieves dot-reservoir tunnel coupling control without a dedicated barrier gate. The elementary structure consists of two accumulation gates separated spatially by a gap, one gate accumulating a reservoir and the other a quantum dot. Control of the tunnel rate between the dot and the reservoir across the gap is demonstrated in the single electron regime by varying the reservoir accumulation gate voltage while compensating with the dot accumulation gate voltage. The method is then applied to a quantum dot connected in series to source and drain reservoirs, enabling transport down to the single electron regime. Finally, tuning of the valley splitting with the dot accumulation gate voltage is observed. This split accumulation gate structure creates silicon quantum dots of similar characteristics to other realizations but with less electrodes, in a single gate stack subtractive fabrication process that is fully compatible with silicon foundry manufacturing.

  1. Detailed statistical contact angle analyses; "slow moving" drops on inclining silicon-oxide surfaces.

    Science.gov (United States)

    Schmitt, M; Groß, K; Grub, J; Heib, F

    2015-06-01

    Contact angle determination by sessile drop technique is essential to characterise surface properties in science and in industry. Different specific angles can be observed on every solid which are correlated with the advancing or the receding of the triple line. Different procedures and definitions for the determination of specific angles exist which are often not comprehensible or reproducible. Therefore one of the most important things in this area is to build standard, reproducible and valid methods for determining advancing/receding contact angles. This contribution introduces novel techniques to analyse dynamic contact angle measurements (sessile drop) in detail which are applicable for axisymmetric and non-axisymmetric drops. Not only the recently presented fit solution by sigmoid function and the independent analysis of the different parameters (inclination, contact angle, velocity of the triple point) but also the dependent analysis will be firstly explained in detail. These approaches lead to contact angle data and different access on specific contact angles which are independent from "user-skills" and subjectivity of the operator. As example the motion behaviour of droplets on flat silicon-oxide surfaces after different surface treatments is dynamically measured by sessile drop technique when inclining the sample plate. The triple points, the inclination angles, the downhill (advancing motion) and the uphill angles (receding motion) obtained by high-precision drop shape analysis are independently and dependently statistically analysed. Due to the small covered distance for the dependent analysis (contact angle determination. They are characterised by small deviations of the computed values. Additional to the detailed introduction of this novel analytical approaches plus fit solution special motion relations for the drop on inclined surfaces and detailed relations about the reactivity of the freshly cleaned silicon wafer surface resulting in acceleration

  2. Improvement of electron emission characteristics of porous silicon emitter by using cathode reduction and electrochemical oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Li, He; Wenjiang, Wang, E-mail: wwj@mail.xjtu.edu.cn; Xiaoning, Zhang

    2017-03-31

    Highlights: • An electron emitter based on porous silicon having the strong application potential was prepared in the studying. • A new simple and convenient post-treat technique was proposed to improve the electron emission properties of the PS emitter. • It demonstrated that the improving of the PS morphology and the oxygen distribution is very important to the PS emitter. - Abstract: A new simple and convenient post-treat technique combined the cathode reduction (CR) and electrochemical oxidation (ECO) was proposed to improve the electron emission properties of the surface-emitting cold cathodes based on the porous silicon (PS). It is demonstrated here that by introducing this new technique combined CR and ECO, the emission properties of the diode have been significantly improved than those as-prepared samples. The experimental results showed that the emission current densities and efficiencies of sample treated by CR were 62 μA/cm{sup 2} and 12.10‰, respectively, nearly 2 orders of magnitude higher than those of as-prepared sample. Furthermore, the CR-treated PS emitter shows higher repeatability and stability compared with the as-prepared PS emitter. The scanning electron microscope (SEM), atomic force microscope (AFM), energy dispersive spectrometer (EDS), furier transformed infrared (FTIR) spectroscopy results indicated that the improved mechanism is mainly due to the passivation of the PS, which not only improve the PS morphology by the passivation of the H{sup +} but also improve the uniformity of the oxygen content distribution in the whole PS layer. Therefore, the method combined the CR treatment and ECO is expected to be a valuable technique to enhance the electron emission characteristics of the PS emitter.

  3. Improvement of electron emission characteristics of porous silicon emitter by using cathode reduction and electrochemical oxidation

    International Nuclear Information System (INIS)

    Li, He; Wenjiang, Wang; Xiaoning, Zhang

    2017-01-01

    Highlights: • An electron emitter based on porous silicon having the strong application potential was prepared in the studying. • A new simple and convenient post-treat technique was proposed to improve the electron emission properties of the PS emitter. • It demonstrated that the improving of the PS morphology and the oxygen distribution is very important to the PS emitter. - Abstract: A new simple and convenient post-treat technique combined the cathode reduction (CR) and electrochemical oxidation (ECO) was proposed to improve the electron emission properties of the surface-emitting cold cathodes based on the porous silicon (PS). It is demonstrated here that by introducing this new technique combined CR and ECO, the emission properties of the diode have been significantly improved than those as-prepared samples. The experimental results showed that the emission current densities and efficiencies of sample treated by CR were 62 μA/cm"2 and 12.10‰, respectively, nearly 2 orders of magnitude higher than those of as-prepared sample. Furthermore, the CR-treated PS emitter shows higher repeatability and stability compared with the as-prepared PS emitter. The scanning electron microscope (SEM), atomic force microscope (AFM), energy dispersive spectrometer (EDS), furier transformed infrared (FTIR) spectroscopy results indicated that the improved mechanism is mainly due to the passivation of the PS, which not only improve the PS morphology by the passivation of the H"+ but also improve the uniformity of the oxygen content distribution in the whole PS layer. Therefore, the method combined the CR treatment and ECO is expected to be a valuable technique to enhance the electron emission characteristics of the PS emitter.

  4. Damage induced by high energy multiply charged oxygen ions in oxide coated silicon

    Energy Technology Data Exchange (ETDEWEB)

    Dhole, S.D. [Department of Physics, University of Pune, Pune 411 007 (India)]. E-mail: sanjay@physics.unipune.ernet.in; Dahiwale, S.S. [Department of Physics, University of Pune, Pune 411 007 (India); Kulkarni, V.R. [Department of Physics, University of Pune, Pune 411 007 (India); Bogle, K.A. [Department of Physics, University of Pune, Pune 411 007 (India); Shinde, N.S. [Ecotopia Science Institute, Division of Energy Science, Nagoya University, Nagoya (Japan); Bhoraskar, V.N. [Department of Physics, University of Pune, Pune 411 007 (India)

    2006-03-15

    P-type oxide coated silicon samples of resistivity 120 {omega} cm were irradiated with 60 MeV oxygen ions of fixed charge states 4{sup +}, 5{sup +}, 6{sup +} and 7{sup +} at an equal fluence of, {phi}, {approx}10{sup 13} ions/cm{sup 2}. The induced damage was estimated by Hall voltage, Hall coefficient, carrier concentration and lifetime of minority carriers. The results indicate that Hall voltage (V {sub H}) and Hall coefficient (R {sub H}) increases, while carrier concentration (n) decreases with the charge state of impinging oxygen ions. The V {sub H} increases from 22 mV to 76.5 mV at typical current of 0.5 mA, R {sub H} from 0.42 x 10{sup 5} cm{sup 3}/C to 2.16 x 10{sup 5} cm{sup 3}/C and n decreases from 9 x 10{sup 13} cm{sup -3} to 2.88 x 10{sup 13} cm{sup -3} for the different charge states. This fact is an evidence that the oxygen ions with an individual fixed charge state passing through very thin 40 A layer of silicon dioxide, induces significant damage at the SiO{sub 2}-Si interface through the mechanism of electronic stopping power. The lifetime of minority charge carriers, {tau} (bulk property), remains constant at around 6 {mu}s for all the charge states of the 60 MeV energy oxygen ion irradiated samples at a constant fluence of, {phi}, 10{sup 13} ions/cm{sup 2}.

  5. [Synergetic effects of silicon carbide and molecular sieve loaded catalyst on microwave assisted catalytic oxidation of toluene].

    Science.gov (United States)

    Wang, Xiao-Hui; Bo, Long-Li; Liu, Hai-Nan; Zhang, Hao; Sun, Jian-Yu; Yang, Li; Cai, Li-Dong

    2013-06-01

    Molecular sieve loaded catalyst was prepared by impregnation method, microwave-absorbing material silicon carbide and the catalyst were investigated for catalytic oxidation of toluene by microwave irradiation. Research work examined effects of silicon carbide and molecular sieve loading Cu-V catalyst's mixture ratio as well as mixed approach changes on degradation of toluene, and characteristics of catalyst were measured through scanning electron microscope, specific surface area test and X-ray diffraction analysis. The result showed that the fixed bed reactor had advantages of both thermal storage property and low-temperature catalytic oxidation when 20% silicon carbide was filled at the bottom of the reactor, and this could effectively improve the utilization of microwave energy as well as catalytic oxidation efficiency of toluene. Under microwave power of 75 W and 47 W, complete-combustion temperatures of molecular sieve loaded Cu-V catalyst and Cu-V-Ce catalyst to toluene were 325 degrees C and 160 degrees C, respectively. Characteristics of the catalysts showed that mixture of rare-earth element Ce increased the dispersion of active components in the surface of catalyst, micropore structure of catalyst effectively guaranteed high adsorption capacity for toluene, while amorphous phase of Cu and V oxides increased the activity of catalyst greatly.

  6. Microarc Oxidation of the High-Silicon Aluminum AK12D Alloy

    Directory of Open Access Journals (Sweden)

    S. K. Kiseleva

    2015-01-01

    Full Text Available The aim of work is to study how the high-silicon aluminum AK12D alloy microstructure and MAO-process modes influence on characteristics (microhardness, porosity and thickness of the oxide layer of formed surface layer.Experimental methods of study:1 MAO processing of AK12D alloy disc-shaped samples. MAO modes features are concentration of electrolyte components – soluble water glass Na2SiO3 and potassium hydroxide (KOH. The content of two components both the soluble water glass and the potassium hydroxide was changed at once, with their concentration ratio remaining constant;2 metallographic analysis of AK12D alloy structure using an optical microscope «Olympus GX51»;3 image analysis of the system "alloy AK12D - MAO - layer" using a scanning electron microscope «JEOL JSM 6490LV»;4 hardness evaluation of the MAO-layers using a micro-hardness tester «Struers Duramin».The porosity, microhardness and thickness of MAO-layer formed on samples with different initial structures are analyzed in detail. Attention is paid to the influence of MAO process modes on the quality layer.It has been proved that the MAO processing allows reaching quality coverage with high microhardness values of 1200-1300HV and thickness up to 114 μm on high-silicon aluminum alloy. It has been found that the initial microstructure of alloy greatly affects the thickness of the MAO - layer. The paper explains the observed effect using the physical principles of MAO process and the nature of silicon particles distribution in the billet volume.It has been shown that increasing concentration of sodium silicate and potassium hydroxide in the electrolyte results in thicker coating and high microhardness.It has been revealed that high microhardness is observed in the thicker MAO-layers.Conclusions:1 The microstructure of aluminum AK12D alloy and concentration of electrolyte components - liquid glass Na2SiO3 and potassium hydroxide affect the quality of coating resulted from MAO

  7. Tunnel oxide passivated contacts formed by ion implantation for applications in silicon solar cells

    International Nuclear Information System (INIS)

    Reichel, Christian; Feldmann, Frank; Müller, Ralph; Hermle, Martin; Glunz, Stefan W.; Reedy, Robert C.; Lee, Benjamin G.; Young, David L.; Stradins, Paul

    2015-01-01

    Passivated contacts (poly-Si/SiO x /c-Si) doped by shallow ion implantation are an appealing technology for high efficiency silicon solar cells, especially for interdigitated back contact (IBC) solar cells where a masked ion implantation facilitates their fabrication. This paper presents a study on tunnel oxide passivated contacts formed by low-energy ion implantation into amorphous silicon (a-Si) layers and examines the influence of the ion species (P, B, or BF 2 ), the ion implantation dose (5 × 10 14  cm −2 to 1 × 10 16  cm −2 ), and the subsequent high-temperature anneal (800 °C or 900 °C) on the passivation quality and junction characteristics using double-sided contacted silicon solar cells. Excellent passivation quality is achieved for n-type passivated contacts by P implantations into either intrinsic (undoped) or in-situ B-doped a-Si layers with implied open-circuit voltages (iV oc ) of 725 and 720 mV, respectively. For p-type passivated contacts, BF 2 implantations into intrinsic a-Si yield well passivated contacts and allow for iV oc of 690 mV, whereas implanted B gives poor passivation with iV oc of only 640 mV. While solar cells featuring in-situ B-doped selective hole contacts and selective electron contacts with P implanted into intrinsic a-Si layers achieved V oc of 690 mV and fill factor (FF) of 79.1%, selective hole contacts realized by BF 2 implantation into intrinsic a-Si suffer from drastically reduced FF which is caused by a non-Ohmic Schottky contact. Finally, implanting P into in-situ B-doped a-Si layers for the purpose of overcompensation (counterdoping) allowed for solar cells with V oc of 680 mV and FF of 80.4%, providing a simplified and promising fabrication process for IBC solar cells featuring passivated contacts

  8. Room temperature NO2 gas sensing of Au-loaded tungsten oxide nanowires/porous silicon hybrid structure

    International Nuclear Information System (INIS)

    Wang Deng-Feng; Liang Ji-Ran; Li Chang-Qing; Yan Wen-Jun; Hu Ming

    2016-01-01

    In this work, we report an enhanced nitrogen dioxide (NO 2 ) gas sensor based on tungsten oxide (WO 3 ) nanowires/porous silicon (PS) decorated with gold (Au) nanoparticles. Au-loaded WO 3 nanowires with diameters of 10 nm–25 nm and lengths of 300 nm–500 nm are fabricated by the sputtering method on a porous silicon substrate. The high-resolution transmission electron microscopy (HRTEM) micrographs show that Au nanoparticles are uniformly distributed on the surfaces of WO 3 nanowires. The effect of the Au nanoparticles on the NO 2 -sensing performance of WO 3 nanowires/porous silicon is investigated over a low concentration range of 0.2 ppm–5 ppm of NO 2 at room temperature (25 °C). It is found that the 10-Å Au-loaded WO 3 nanowires/porous silicon-based sensor possesses the highest gas response characteristic. The underlying mechanism of the enhanced sensing properties of the Au-loaded WO 3 nanowires/porous silicon is also discussed. (paper)

  9. Characterization of silicon-oxide interfaces and organic monolayers by IR-UV ellipsometry and FTIR spectroscopy

    Science.gov (United States)

    Hess, P.; Patzner, P.; Osipov, A. V.; Hu, Z. G.; Lingenfelser, D.; Prunici, P.; Schmohl, A.

    2006-08-01

    VUV-laser-induced oxidation of Si(111)-(1×1):H, Si(100):H, and a-Si:H at 157 nm (F II laser) in pure O II and pure H IIO atmospheres was studied between 30°C and 250°C. The oxidation process was monitored in real time by spectroscopic ellipsometry (NIR-UV) and FTIR spectroscopy. The ellipsometric measurements could be simulated with a three-layer model, providing detailed information on the variation of the suboxide interface with the nature of the silicon substrate surface. Besides the silicon-dioxide and suboxide layer, a dense, disordered, roughly monolayer thick silicon layer was included, as found previously by molecular dynamics calculations. The deviations from the classical Deal-Grove mechanism and the self-limited growth of the ultrathin dioxide layers (TMS) groups and n-alkylthiol monolayers on gold-coated silicon. The C-H stretching vibrations of the methylene and methyl groups could be identified by FTIR spectroscopy and IR ellipsometry.

  10. Electronic devices containing switchably conductive silicon oxides as a switching element and methods for production and use thereof

    Science.gov (United States)

    Tour, James M; Yao, Jun; Natelson, Douglas; Zhong, Lin; He, Tao

    2013-11-26

    In various embodiments, electronic devices containing switchably conductive silicon oxide as a switching element are described herein. The electronic devices are two-terminal devices containing a first electrical contact and a second electrical contact in which at least one of the first electrical contact or the second electrical contact is deposed on a substrate to define a gap region therebetween. A switching layer containing a switchably conductive silicon oxide resides in the the gap region between the first electical contact and the second electrical contact. The electronic devices exhibit hysteretic current versus voltage properties, enabling their use in switching and memory applications. Methods for configuring, operating and constructing the electronic devices are also presented herein.

  11. Zinc tin oxide as high-temperature stable recombination layer for mesoscopic perovskite/silicon monolithic tandem solar cells

    KAUST Repository

    Werner, Jérémie

    2016-12-05

    Perovskite/crystalline silicon tandem solar cells have the potential to reach efficiencies beyond those of silicon single-junction record devices. However, the high-temperature process of 500 °C needed for state-of-the-art mesoscopic perovskite cells has, so far, been limiting their implementation in monolithic tandem devices. Here, we demonstrate the applicability of zinc tin oxide as a recombination layer and show its electrical and optical stability at temperatures up to 500 °C. To prove the concept, we fabricate monolithic tandem cells with mesoscopic top cell with up to 16% efficiency. We then investigate the effect of zinc tin oxide layer thickness variation, showing a strong influence on the optical interference pattern within the tandem device. Finally, we discuss the perspective of mesoscopic perovskite cells for high-efficiency monolithic tandem solar cells. © 2016 Author(s)

  12. Porous silicon carbide and aluminum oxide with unidirectional open porosity as model target materials for radioisotope beam production

    CERN Document Server

    Czapski, M; Tardivat, C; Stora, T; Bouville, F; Leloup, J; Luis, R Fernandes; Augusto, R Santos

    2013-01-01

    New silicon carbide (SiC) and aluminum oxide (Al2O3) of a tailor-made microstructure were produced using the ice-templating technique, which permits controlled pore formation conditions within the material. These prototypes will serve to verify aging of the new advanced target materials under irradiation with proton beams. Before this, the evaluation of their mechanical integrity was made based on the energy deposition spectra produced by FLORA codes. (C) 2013 Elsevier B.V. All rights reserved.

  13. Porous silicon carbide and aluminum oxide with unidirectional open porosity as model target materials for radioisotope beam production

    Science.gov (United States)

    Czapski, M.; Stora, T.; Tardivat, C.; Deville, S.; Santos Augusto, R.; Leloup, J.; Bouville, F.; Fernandes Luis, R.

    2013-12-01

    New silicon carbide (SiC) and aluminum oxide (Al2O3) of a tailor-made microstructure were produced using the ice-templating technique, which permits controlled pore formation conditions within the material. These prototypes will serve to verify aging of the new advanced target materials under irradiation with proton beams. Before this, the evaluation of their mechanical integrity was made based on the energy deposition spectra produced by FLUKA codes.

  14. Effect of annealing on silicon heterojunction solar cells with textured ZnO:Al as transparent conductive oxide

    Directory of Open Access Journals (Sweden)

    Roca i Cabarrocas P.

    2012-07-01

    Full Text Available We report on silicon heterojunction solar cells using textured aluminum doped zinc oxide (ZnO:Al as a transparent conductive oxide (TCO instead of flat indium tin oxide. Double side silicon heterojunction solar cell were fabricated by radio frequency plasma enhanced chemical vapor deposition on high life time N-type float zone crystalline silicon wafers. On both sides of these cells we have deposited by radio frequency magnetron sputtering ZnO:Al layers of thickness ranging from 800 nm to 1400 nm. These TCO layers were then textured by dipping the samples in a 0.5% hydrochloric acid. External quantum efficiency as well as I-V under 1 sun illumination measurements showed an increase of the current for the cells using textured ZnO:Al. The cells were then annealed at 150 °C, 175 °C and 200 °C during 30 min in ambient atmosphere and characterized at each annealing step. The results show that annealing has no impact on the open circuit voltage of the devices but that up to a 175 °C it enhances their short circuit current, consistent with an overall enhancement of their spectral response. Our results suggest that ZnO:Al is a promising material to increase the short circuit current (Jsc while avoiding texturing the c-Si substrate.

  15. Preparation and properties of novel epoxy/graphene oxide nanosheets (GON) composites functionalized with flame retardant containing phosphorus and silicon

    International Nuclear Information System (INIS)

    Li, Kuo-Yi; Kuan, Chen-Feng; Kuan, Hsu-Chiang; Chen, Chia-Hsun; Shen, Ming-Yuan; Yang, Jia-Ming; Chiang, Chin-Lung

    2014-01-01

    2-(Diphenylphosphino)ethyltriethoxy silane (DPPES) was grafted onto the surface of graphene oxide nanosheets (GON) via a condensation reaction. X-ray photoelectron spectroscopy, X-ray diffractometry, Fourier transform infrared spectroscopy and Raman spectroscopy verify that DPPES did not only covalently bond to GON as a functionalization moiety, but partly restored its conjugated structure as a reducing agent. DPPES on graphene sheets oxide was observed by transmission electron microscopy, and contributed to the favorable dispersion of DPPES-GON in nonpolar toluene. Additionally, the flame retardancy and thermal stability of epoxy/DPPES-GON nanocomposites that contain various weight fractions of DPPES-GON were studied using the limiting oxygen index test, UL-94 test and by thermogravimetric analysis in nitrogen. The composites containing 10 wt% DPPES-GON can pass V-0 rating in UL-94 test. Adding 10 wt% DPPES-GON in epoxy greatly increased the char yield and LOI by 42% and 80%, respectively. Epoxy/DPPES-GON nanocomposites with phosphorus, silicon and graphene layer structures were found to exhibit much greater flame retardancy than neat epoxy. The synergistic effects among silicon, phosphorus and GON can improve the flame retardancy of epoxy resin. - Highlights: • Flame retardant was grafted on the surface of graphene oxide nanosheets (GON) by the condensation reaction. • The synergistic effect between silicon, phosphorus and GON improved the flame retardance of epoxy resin. • Epoxy composites have excellent flame retardance at low additive concentrations

  16. A time-pulsed positronium beam and a study of oxides on silicon using positrons

    International Nuclear Information System (INIS)

    Khatri, R.K.

    1993-01-01

    The studies on rare gas solid moderators were carried out with a 350 μCi 22 Na radioactive source. The corrected efficiency for neon moderator in conical geometrical configuration was as high as (1.4 ± 0.2)%. The conical configuration moderator performed better by a factor of (2.2 ± 0.2) than the cylindrical configuration. A time pulsed positron beam was built to carry out investigations on the positronium formation processes and positronium beam. This beam has the capability to store low energy e + in a magnetic bottle, with a magnetic bottle at one end and an electrostatic mirror at the other. These stored e + are then bunched to form a pulse with a buncher. The bunched beam had a FWHM of 17 nsec and contained 1 to 2 e + /pulse. A thin carbon foil of 50 angstrom thickness was used for positronium formation by process of charge exchange. Positronium Annihilation Spectroscopy (PAS) was utilized to carry out studies on the activation energy of hydrogen at the interface of oxide and silicon substrate and the effect of irradiation on the oxides in SiO 2 /Si(100) sample. The activation energy of hydrogen at the interface of SiO 2 /Si(100) samples with n- and p-type substrate was measured to be 2.60(6) eV and 2.47(6) eV respectively. The investigations of the samples irradiated with x-ray and γ-ray led to the first time identification of creation of E' centers with PAS

  17. Electronic properties and morphology of copper oxide/n-type silicon heterostructures

    Science.gov (United States)

    Lindberg, P. F.; Gorantla, S. M.; Gunnæs, A. E.; Svensson, B. G.; Monakhov, E. V.

    2017-08-01

    Silicon-based tandem heterojunction solar cells utilizing cuprous oxide (Cu2O) as the top absorber layer show promise for high-efficiency conversion and low production cost. In the present study, single phase Cu2O films have been realized on n-type Si substrates by reactive magnetron sputtering at 400 °C. The obtained Cu2O/Si heterostructures have subsequently been heat treated at temperatures in the 400-700 °C range in Ar flow and extensively characterized by x-ray diffraction (XRD) measurements, transmission electron microscopy (TEM) imaging and electrical techniques. The Cu2O/Si heterojunction exhibits a current rectification of ~5 orders of magnitude between forward and reverse bias voltages. High resolution cross-sectional TEM-images show the presence of a ~2 nm thick interfacial SiO2 layer between Cu2O and the Si substrate. Heat treatments below 550 °C result in gradual improvement of crystallinity, indicated by XRD. At and above 550 °C, partial phase transition to cupric oxide (CuO) occurs followed by a complete transition at 700 °C. No increase or decrease of the SiO2 layer is observed after the heat treatment at 550 °C. Finally, a thin Cu-silicide layer (Cu3Si) emerges below the SiO2 layer upon annealing at 550 °C. This silicide layer influences the lateral current and voltage distributions, as evidenced by an increasing effective area of the heterojunction diodes.

  18. Oxidation Properties of Nitrogen-Doped Silicon Films Deposited from Si2H6 and NH3

    Science.gov (United States)

    Scheid, Emmanuel; Boyer, Pierre; Samitier, Josep; Hassani, Ahmed

    1994-03-01

    Si2H6/NH3 gas mixture was employed to obtain, by low-pressure chemical vapor deposition (LPCVD) at low temperature, nitrogen-doped silicon (NIDOS) films with various N/Si ratios. Thermal oxide was grown in dry oxygen at 900°C and 1100°C on NIDOS films. The result indicates that the nitrogen content of NIDOS films, assessed by X-ray photoelectron spectroscopy (XPS) and Fourier transform infrared spectroscopy (FTIR), greatly influences their oxidation rate.

  19. Effect of deposition temperature on the bonding configurations and properties of fluorine doped silicon oxide film

    International Nuclear Information System (INIS)

    Lu, Wei-Lun; Kuo, Ting-Wei; Huang, Chun-Hsien; Wang, Na-Fu; Tsai, Yu-Zen; Wang, Ming-Wei; Hung, Chen-I.; Houng, Mau-Phon

    2011-01-01

    In our study, fluorine-doped silicon oxide (SiOF) films were prepared using a mixture of SiH 4 , N 2 O, and CF 4 in a conventional plasma enhanced chemical vapor deposition system at various deposition temperatures. Deposition behaviors are determined by the deposition temperature. Our results show that for temperatures below 300 deg. C the process is surface-reaction-limited controlled, but becomes diffusion-limited when the deposition temperature exceeds 300 deg. C. The surface topography images obtained using an atomic force microscope show that a large amount of free volume space was created in the film with a low temperature deposition. The optical microscope and secondary ion mass spectrometer analyses show that precipitates were produced at the near-surface at the deposition temperature of 150 deg. C with a higher fluorine concentration of 2.97 at.%. Our results show that the properties of the SiOF film are controlled not only by the free volume space but also by the fluorine concentration. An optimal SiOF film prepared at a temperature of 200 deg. C shows a low dielectric constant of 3.55, a leakage current of 1.21 x 10 -8 A/cm 2 at 1 MV/cm, and a fluorine concentration of 2.5 at.%.

  20. Demonstration of Synaptic Behaviors and Resistive Switching Characterizations by Proton Exchange Reactions in Silicon Oxide

    Science.gov (United States)

    Chang, Yao-Feng; Fowler, Burt; Chen, Ying-Chen; Zhou, Fei; Pan, Chih-Hung; Chang, Ting-Chang; Lee, Jack C.

    2016-02-01

    We realize a device with biological synaptic behaviors by integrating silicon oxide (SiOx) resistive switching memory with Si diodes. Minimal synaptic power consumption due to sneak-path current is achieved and the capability for spike-induced synaptic behaviors is demonstrated, representing critical milestones for the use of SiO2-based materials in future neuromorphic computing applications. Biological synaptic behaviors such as long-term potentiation (LTP), long-term depression (LTD) and spike-timing dependent plasticity (STDP) are demonstrated systematically using a comprehensive analysis of spike-induced waveforms, and represent interesting potential applications for SiOx-based resistive switching materials. The resistive switching SET transition is modeled as hydrogen (proton) release from (SiH)2 to generate the hydrogen bridge defect, and the RESET transition is modeled as an electrochemical reaction (proton capture) that re-forms (SiH)2. The experimental results suggest a simple, robust approach to realize programmable neuromorphic chips compatible with large-scale CMOS manufacturing technology.

  1. Quantitative differentiation of multiple virus in blood using nanoporous silicon oxide immunosensor and artificial neural network.

    Science.gov (United States)

    Chakraborty, W; Ray, R; Samanta, N; RoyChaudhuri, C

    2017-12-15

    In spite of the rapid developments in various nanosensor technologies, it still remains challenging to realize a reliable ultrasensitive electrical biosensing platform which will be able to detect multiple viruses in blood simultaneously with a fairly high reproducibility without using secondary labels. In this paper, we have reported quantitative differentiation of Hep-B and Hep-C viruses in blood using nanoporous silicon oxide immunosensor array and artificial neural network (ANN). The peak frequency output (f p ) from the steady state sensitivity characteristics and the first cut off frequency (f c ) from the transient characteristics have been considered as inputs to the multilayer ANN. Implementation of several classifier blocks in the ANN architecture and coupling them with both the sensor chips, functionalized with Hep-B and Hep-C antibodies have enabled the quantification of the viruses with an accuracy of around 95% in the range of 0.04fM-1pM and with an accuracy of around 90% beyond 1pM and within 25nM in blood serum. This is the most sensitive report on multiple virus quantification using label free method. Copyright © 2017 Elsevier B.V. All rights reserved.

  2. Silicon-doped hafnium oxide anti-ferroelectric thin films for energy storage

    Science.gov (United States)

    Ali, Faizan; Liu, Xiaohua; Zhou, Dayu; Yang, Xirui; Xu, Jin; Schenk, Tony; Müller, Johannes; Schroeder, Uwe; Cao, Fei; Dong, Xianlin

    2017-10-01

    Motivated by the development of ultracompact electronic devices as miniaturized energy autonomous systems, great research efforts have been expended in recent years to develop various types of nano-structural energy storage components. The electrostatic capacitors characterized by high power density are competitive; however, their implementation in practical devices is limited by the low intrinsic energy storage density (ESD) of linear dielectrics like Al2O3. In this work, a detailed experimental investigation of energy storage properties is presented for 10 nm thick silicon-doped hafnium oxide anti-ferroelectric thin films. Owing to high field induced polarization and slim double hysteresis, an extremely large ESD value of 61.2 J/cm3 is achieved at 4.5 MV/cm with a high efficiency of ˜65%. In addition, the ESD and the efficiency exhibit robust thermal stability in 210-400 K temperature range and an excellent endurance up to 109 times of charge/discharge cycling at a very high electric field of 4.0 MV/cm. The superior energy storage performance together with mature technology of integration into 3-D arrays suggests great promise for this recently discovered anti-ferroelectric material to replace the currently adopted Al2O3 in fabrication of nano-structural supercapacitors.

  3. Mesoporous silicon oxide films and their uses as templates in obtaining nanostructured conductive polymers

    Science.gov (United States)

    Salgado, R.; Arteaga, G. C.; Arias, J. M.

    2018-04-01

    Obtaining conductive polymers (CPs) for the manufacture of OLEDs, solar cells, electrochromic devices, sensors, etc., has been possible through the use of electrochemical techniques that allow obtaining films of controlled thickness with positive results in different applications. Current trends point towards the manufacture of nanomaterials, and therefore it is necessary to develop methods that allow obtaining CPs with nanostructured morphology. This is possible by using a porous template to allow the growth of the polymeric materials. However, prior and subsequent treatments are required to separate the material from the template so that it can be evaluated in the applications mentioned above. This is why mesoporous silicon oxide films (template) are essential for the synthesis of nanostructured polymers since both the template and the polymer are obtained on the electrode surface, and therefore it is not necessary to separate the material from the template. Thus, the material can be evaluated directly in the applications mentioned above. The dimensions of the resulting nanostructures will depend on the power, time and technique used for electropolymerization as well as the monomer and the surfactant of the mesoporous film.

  4. Transmission Electron Microscopy Studies of Electron-Selective Titanium Oxide Contacts in Silicon Solar Cells

    KAUST Repository

    Ali, Haider

    2017-08-15

    In this study, the cross-section of electron-selective titanium oxide (TiO2) contacts for n-type crystalline silicon solar cells were investigated by transmission electron microscopy. It was revealed that the excellent cell efficiency of 21.6% obtained on n-type cells, featuring SiO2/TiO2/Al rear contacts and after forming gas annealing (FGA) at 350°C, is due to strong surface passivation of SiO2/TiO2 stack as well as low contact resistivity at the Si/SiO2/TiO2 heterojunction. This can be attributed to the transformation of amorphous TiO2 to a conducting TiO2-x phase. Conversely, the low efficiency (9.8%) obtained on cells featuring an a-Si:H/TiO2/Al rear contact is due to severe degradation of passivation of the a-Si:H upon FGA.

  5. Oxidation protection and behavior of in-situ zirconium diboride–silicon carbide coating for carbon/carbon composites

    International Nuclear Information System (INIS)

    Li, Lu; Li, Hejun; Yin, Xuemin; Chu, Yanhui; Chen, Xi; Fu, Qiangang

    2015-01-01

    Highlights: • ZrB 2 –SiC coating was prepared on C/C composite by in-situ reaction. • A two-layered structure was obtained when the coating was oxidized at 1500 °C. • The formation and collapse of bubbles influenced the coating oxidation greatly. • The morphology evolution of oxide scale during oxidation was illuminated. - Abstract: To protect carbon/carbon (C/C) composites against oxidation, zirconium diboride–silicon carbide (ZrB 2 –SiC) coating was prepared by in-situ reaction using ZrC, B 4 C and Si as raw materials. The in-situ ZrB 2 –SiC coated C/C presented good oxidation resistance, whose weight loss was only 0.15% after isothermal oxidation at 1500 °C for 216 h. Microstructure evolution of coating at 1500 °C was studied, revealing a two-layered structure: (1) ZrO 2 (ZrSiO 4 ) embedded in SiO 2 -rich glass, and (2) unaffected ZrB 2 –SiC. The formation and collapse of bubbles influenced the coating oxidation greatly. A model based on the evolution of oxide scale was proposed to explain the failure mechanism of coating

  6. The reactive element effect of yttrium and yttrium silicon on high temperature oxidation of NiCrAl coating

    Science.gov (United States)

    Ramandhany, S.; Sugiarti, E.; Desiati, R. D.; Martides, E.; Junianto, E.; Prawara, B.; Sukarto, A.; Tjahjono, A.

    2018-03-01

    The microstructure formed on the bond coat affects the oxidation resistance, particularly the formation of a protective oxide layer. The adhesion of bond coat and TGO increased significantly by addition of reactive element. In the present work, the effect of yttrium and yttrium silicon as reactive element (RE) on NiCrAl coating was investigated. The NiCrAl (without RE) and NiCrAlX (X:Y or YSi) bond coating were deposited on Hastelloy C-276 substrate by High Velocity Oxygen Fuel (HVOF) method. Isothermal oxidation was carried out at 1000 °C for 100 hours. The results showed that the addition of RE could prevent the breakaway oxidation. Therefore, the coating with reactive element were more protective against high temperature oxidation. Furthermore, the oxidation rate of NiCrAlY coating was lower than NiCrAlYSi coating with the total mass change was ±2.394 mg/cm2 after 100 hours of oxidation. The thickness of oxide scale was approximately 1.18 μm consisting of duplex oxide scale of spinel NiCr2O4 in outer scale and protective α-Al2O3 in inner scale.

  7. Gelatin Template Synthesis of Aluminum Oxide and/or Silicon Oxide Containing Micro/Mesopores Using the Proteic Sol-Gel Method

    Directory of Open Access Journals (Sweden)

    Amanda Sayure Kasuya de Oliveira

    2017-01-01

    Full Text Available Aluminum oxide and/or silicon oxide-based supports were synthesized by proteic sol-gel method. The characterization was performed through the analysis of TG, XRD, FTIR, SEM, and N2 physisorption. The XRD diffractograms showed an amorphous material profile. TG results indicate the total liberation of the organic and inorganic material in the calcination temperature used, occurring in different mass loss range. This piece of information was reaffirmed by the FTIR spectra, which presented characteristic bands of gelatin structure before calcinations which disappear in the spectrum of the solid after calcinations, indicating the loss of organic matter from gelatin after heat treatment. The spectra exhibited M-O stretching vibration at low wavenumbers after calcinations related to metal oxides. The acquired images by SEM suggest the obtaining of a highly porous material with very different characteristics depending on the composition of the support. The N2 isotherms indicate the presence of a micro/mesoporous oxide with interesting textural properties, particularly for the supports containing aluminum and silicon oxide. The ethanol dehydration results showed greater selectivity to diethyl ether compared to ethylene. From the reaction data, the following order of acid strength was obtained: 2Si-Al > Si-2Al > Si-Al > Al, which is related to the Si-Al ratio.

  8. Effect of annealing and oxide layer thickness on doping profiles shape of ''through-oxide'' implanted P+ ions in textured silicon

    International Nuclear Information System (INIS)

    El-Dessouki, M.S.; Galloni, R.

    1987-10-01

    Phosphorous ions at energies of 60+100 KeV, and doses (4+5)x10 15 atom/cm 2 have been implanted randomly through SiO 2 layers into textured silicon crystals. The penetration profiles of the P + ions have been determined by means of differential sheet resistivity and Hall-effect, together with the anodic oxidation stripping technique. The effect of the oxide layer thickness, annealing temperature on the junction properties has been studied. The damage produced by implantation, has also been investigated using transmission electron microscope (TEM). From the mobility measurements of the free carriers as a function of depth through the junction, two minima have been observed in through oxide implanted samples. The one nearer to the Si-SiO 2 interface (at about 200A from the interface) was related to the damage produced by the recoil oxygen atoms from the oxide layer into silicon. The deeper minimum is lying at ∼ 0.2μm from the interface and was attributed to the damage produced by the implanted P + ions, which caused clusters and defect loops after annealing. This damage was observed through TEM photographs. The optimum conditions for producing shallow junction without losing much of the implanted P + ions through the oxide layer were estimated. (author). 22 refs, 7 figs, 1 tab

  9. Oxide-Free Bonding of III-V-Based Material on Silicon and Nano-Structuration of the Hybrid Waveguide for Advanced Optical Functions

    Directory of Open Access Journals (Sweden)

    Konstantinos Pantzas

    2015-10-01

    Full Text Available Oxide-free bonding of III-V-based materials for integrated optics is demonstrated on both planar Silicon (Si surfaces and nanostructured ones, using Silicon on Isolator (SOI or Si substrates. The hybrid interface is characterized electrically and mechanically. A hybrid InP-on-SOI waveguide, including a bi-periodic nano structuration of the silicon guiding layer is demonstrated to provide wavelength selective transmission. Such an oxide-free interface associated with the nanostructured design of the guiding geometry has great potential for both electrical and optical operation of improved hybrid devices.

  10. Porous silicon used as an oxide diffusion mask to produce a periodic micro doped n{sup ++}/n regions

    Energy Technology Data Exchange (ETDEWEB)

    Dimassi, Wissem; Jafel, Hayet; Lajnef, Mohamed; Ali Kanzari, M.; Bouaicha, Mongi; Bessais, Brahim; Ezzaouia, Hatem [Laboratoire de Photovoltaique, Centre de Recherche et des Technologies de l' Energie, PB: 95, Hammam Lif 2050 (Tunisia)

    2011-06-15

    The realization of screen-printed contacts on silicon solar cells requires highly doped regions under the fingers and lowly doped and thin ones between them. In this work, we present a low-cost approach to fabricate selective emitter (n{sup ++}/n doped silicon regions), using oxidized porous silicon (ox-PS) as a mask. Micro-periodic fingers were opened on the porous silicon layer using a micro groove machining process. Optimized phosphorous diffusion through the micro grooved ox-PS let us obtain n{sup ++} doped regions in opened zones and n doped large regions underneath the ox-PS layer. The dark I-V characteristics of the obtained device and Fourier transform infrared (FTIR) spectroscopy investigations of the PS layer show the possibility to use PS as a dielectric layer. The Light Beam Induced Current (LBIC) mapping of the realized device, confirm the presence of a micro periodic n{sup ++}/n type structure. (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  11. Structural and optical properties of silicon rich oxide films in graded-stoichiometric multilayers for optoelectronic devices

    Energy Technology Data Exchange (ETDEWEB)

    Palacios-Huerta, L.; Aceves-Mijares, M. [Electronics Department, INAOE, Apdo. 51, Puebla, Pue. 72000, México (Mexico); Cabañas-Tay, S. A.; Cardona-Castro, M. A.; Morales-Sánchez, A., E-mail: alfredo.morales@cimav.edu.mx [Centro de Investigación en Materiales Avanzados S.C., Unidad Monterrey-PIIT, Apodaca, NL 66628, México (Mexico); Domínguez-Horna, C. [Instituto de Microelectrónica de Barcelona, IMB-CNM (CSIC), Bellaterra 08193, Barcelona (Spain)

    2016-07-18

    Silicon nanocrystals (Si-ncs) are excellent candidates for the development of optoelectronic devices. Nevertheless, different strategies are still necessary to enhance their photo and electroluminescent properties by controlling their structural and compositional properties. In this work, the effect of the stoichiometry and structure on the optical properties of silicon rich oxide (SRO) films in a multilayered (ML) structure is studied. SRO MLs with silicon excess gradually increased towards the top and bottom and towards the center of the ML produced through the variation of the stoichiometry in each SRO layer were fabricated and confirmed by X-ray photoelectron spectroscopy. Si-ncs with three main sizes were observed by a transmission electron microscope, in agreement with the stoichiometric profile of each SRO layer. The presence of the three sized Si-ncs and some oxygen related defects enhances intense violet/blue and red photoluminescence (PL) bands. The SRO MLs were super-enriched with additional excess silicon by Si{sup +} implantation, which enhanced the PL intensity. Oxygen-related defects and small Si-ncs (<2 nm) are mostly generated during ion implantation enhancing the violet/blue band to become comparable to the red band. The structural, compositional, and luminescent characteristics of the multilayers are the result of the contribution of the individual characteristics of each layer.

  12. Low-temperature atomic layer deposition of MoOx for silicon heterojunction solar cells

    NARCIS (Netherlands)

    Macco, B.; Vos, M.; Thissen, N.F.W.; Bol, A.A.; Kessels, W.M.M.

    2015-01-01

    The preparation of high-quality molybdenum oxide (MoOx) is demonstrated by plasma-enhanced atomic layer deposition (ALD) at substrate temperatures down to 50 °C. The films are amorphous, slightly substoichiometric with respect to MoO3, and free of other elements apart from hydrogen (&11 at%). The

  13. Influence of silicon species on the transformation of green rust I(Cl-) in aqueous solution by oxidation

    International Nuclear Information System (INIS)

    Sahoo, Gadadhar; Fujieda, Shun; Shinoda, Kozo; Yamaguchi, Shinichi; Korosaki, Masao; Suzuki, Shigeru

    2011-01-01

    Highlights: → Addition of silicate species and silica to GRI(Cl - ) increased oxidation time. → The lepidocrocite particle size in silicate added case has been reduced significantly. → The influence of silicate was attributed to its adsorption on lepidocrocite. → Silicate also influenced GRI(Cl - ) transformation due to adsorption on it. - Abstract: X-ray diffraction (XRD) and solution analysis were used for characterizing the influence of different silicon species on oxidation of green rust (GRI(Cl - )) suspension. While addition of silicon to metallic iron enhanced the formation of β-FeOOH, GRI(Cl - ) in aqueous solution oxidized into lepidocrocite and oxidation was delayed in presence of silica and silicate species as noticed from potential, pH, and dissolved oxygen (DO) measurements. Transmission electron micrographs showed that the particle size of lepidocrocite was reduced due to silicate addition. The influence of silicate was attributed to its adsorption on GRI(Cl - ) and lepidocrocite particles as confirmed from ICP-AES analysis of supernatant solution.

  14. Magnetotransport investigations of the two-dimensional metallic state in silicon metal-oxid-semiconductor structures

    International Nuclear Information System (INIS)

    Prinz, A.

    2002-03-01

    For more than two decades it was the predominant view among the physical community that the every two-dimensional (2D) disordered electron system becomes insulating as the temperature approaches the absolute zero temperature (0 Kelvin or -273.15 o C). Two-dimensional means that the movement of the charge carriers is confined in one direction by a potential so that the carriers can move freely only perpendicular to the confinement. The most famous physical realization of a 2D system is the silicon metal-oxide-semiconductor field effect transistor (Si-MOSFET). It is one of the basic elements of most electronic devices in our daily life. The working principle is very simple. Charges are attracted to the semiconductor-oxide interface by an electric field applied between the metallic gate and the semiconductor, so that a 2D conductive channel is formed. The charge density can be adjusted by the voltage from zero up to 10 13 cm -2 . In 1994 Kravchenko and coworkers made a very important discovery. They studied high mobility Si-MOSFETs and found that for densities below a certain critical value, nc, the resistivity increases as the temperature is decreased below 2 K, whereas for densities above $n c $ the resistivity decreases unexpectedly. The transition from insulating to metallic behavior, known as metal-insulator transition (MIT), was obviously a contradiction to the commonly accepted theories which predict insulating behavior for any density. The insulating behavior is a consequence of the wave properties of electrons which leads to interference in disordered media and thus to enhanced backscattering. In the subsequent years, experimental studies were performed on a variety of 2D systems, which qualitatively showed a similar behavior. All the investigated samples had one thing in common. The interaction energy between the carriers was considerable higher than their mean kinetic energy due to their movement in the 2D plane. Since the electron-electron interaction was

  15. Statistical contact angle analyses; "slow moving" drops on a horizontal silicon-oxide surface.

    Science.gov (United States)

    Schmitt, M; Grub, J; Heib, F

    2015-06-01

    Sessile drop experiments on horizontal surfaces are commonly used to characterise surface properties in science and in industry. The advancing angle and the receding angle are measurable on every solid. Specially on horizontal surfaces even the notions themselves are critically questioned by some authors. Building a standard, reproducible and valid method of measuring and defining specific (advancing/receding) contact angles is an important challenge of surface science. Recently we have developed two/three approaches, by sigmoid fitting, by independent and by dependent statistical analyses, which are practicable for the determination of specific angles/slopes if inclining the sample surface. These approaches lead to contact angle data which are independent on "user-skills" and subjectivity of the operator which is also of urgent need to evaluate dynamic measurements of contact angles. We will show in this contribution that the slightly modified procedures are also applicable to find specific angles for experiments on horizontal surfaces. As an example droplets on a flat freshly cleaned silicon-oxide surface (wafer) are dynamically measured by sessile drop technique while the volume of the liquid is increased/decreased. The triple points, the time, the contact angles during the advancing and the receding of the drop obtained by high-precision drop shape analysis are statistically analysed. As stated in the previous contribution the procedure is called "slow movement" analysis due to the small covered distance and the dominance of data points with low velocity. Even smallest variations in velocity such as the minimal advancing motion during the withdrawing of the liquid are identifiable which confirms the flatness and the chemical homogeneity of the sample surface and the high sensitivity of the presented approaches. Copyright © 2014 Elsevier Inc. All rights reserved.

  16. Nitric oxide releasing silicone rubbers with improved blood compatibility: preparation, characterization, and in vivo evaluation.

    Science.gov (United States)

    Zhang, Huiping; Annich, Gail M; Miskulin, Judiann; Osterholzer, Kathryn; Merz, Scott I; Bartlett, Robert H; Meyerhoff, Mark E

    2002-03-01

    Nitric oxide (NO) releasing silicone rubbers (SR) are prepared via a three-step reaction scheme. A diamino triaminoalkyltrimethoxysilane crosslinker is used to vulcanize hydroxyl terminated polydimethylsiloxane (PDMS) in the presence of ambient moisture and a dibutyltin dilaurate catalyst so that the respective diamine triamine groups are covalently linked to the cured SR structure. These amine sites are then diazeniumdiolated, in situ, when the cured SR is reacted with NO at elevated pressure (80 psi). Although nitrite species are also formed during the NO addition reaction, in most cases the diazeniumdiolated polymer is the major product within the final SR matrix. Temperature appears to be the major driving force for the dissociation of the attached diazeniumdiolate moieties, whereas the presence of bulk water bathing the SR materials has only minimal effect on the observed NO release rate owing to the low water uptake of the SR matrices. The resulting SR films/coatings release NO at ambient or physiological temperature for up to 20 d with average fluxes of at least 4 x 10(10) mol x cm(-2) x min(-1) (coating thickness > or = 600 microm) over first 4 h, comparable to the NO fluxes observed from stimulated human endothelial cells. The NO loading and concomitant NO release flux of the SR material are readily adjustable by altering the diamine triamine loading and film/coating thickness. The new NO releasing SR materials are shown to exhibit improved thromboresistance in vivo, as demonstrated via reduced platelet activation on the surface of these polymers when used to coat the inner walls of SR tubings employed for extracorporeal circulation in a rabbit model.

  17. Permeation mechanisms of pulsed microwave plasma deposited silicon oxide films for food packaging applications

    International Nuclear Information System (INIS)

    Deilmann, Michael; Grabowski, Mirko; Theiss, Sebastian; Bibinov, Nikita; Awakowicz, Peter

    2008-01-01

    Silicon oxide barrier layers are deposited on polyethylene terephthalate as permeation barriers for food packaging applications by means of a low pressure microwave plasma. Hexamethyldisiloxane (HMDSO) and oxygen are used as process gases to deposit SiO x coatings via pulsed low pressure plasmas. The layer composition of the coating is investigated by Fourier transform infrared spectroscopy and energy dispersive x-ray spectroscopy to show correlations with barrier properties of the films. The oxygen permeation barrier is determined by the carrier gas method using an electrochemical detector. The transition from low to high barrier films is mapped by the transition from organic SiO x C y H z layers to quartz-like SiO 1.7 films containing silanol bound hydrogen. A residual permeation as low as J = 1 ± 0.3 cm 3 m -2 day -1 bar -1 is achieved, which is a good value for food packaging applications. Additionally, the activation energy E p of oxygen permeation is analysed and a strong increase from E p = 31.5 kJ mol -1 for SiO x C y H z -like coatings to E p = 53.7 kJ mol -1 for SiO 1.7 films is observed by increasing the oxygen dilution of HMDSO:O 2 plasma. The reason for the residual permeation of high barrier films is discussed and coating defects are visualized by capacitively coupled atomic oxygen plasma etching of coated substrates. A defect density of 3000 mm -2 is revealed

  18. Growth of High-Density Zinc Oxide Nanorods on Porous Silicon by Thermal Evaporation

    Directory of Open Access Journals (Sweden)

    Nurul Izni Rusli

    2012-12-01

    Full Text Available The formation of high-density zinc oxide (ZnO nanorods on porous silicon (PS substrates at growth temperatures of 600–1000 °C by a simple thermal evaporation of zinc (Zn powder in the presence of oxygen (O2 gas was systematically investigated. The high-density growth of ZnO nanorods with (0002 orientation over a large area was attributed to the rough surface of PS, which provides appropriate planes to promote deposition of Zn or ZnOx seeds as nucleation sites for the subsequent growth of ZnO nanorods. The geometrical morphologies of ZnO nanorods are determined by the ZnOx seed structures, i.e., cluster or layer structures. The flower-like hexagonal-faceted ZnO nanorods grown at 600 °C seem to be generated from the sparsely distributed ZnOx nanoclusters. Vertically aligned hexagonal-faceted ZnO nanorods grown at 800 °C may be inferred from the formation of dense arrays of ZnOx clusters. The formation of disordered ZnO nanorods formed at 1000 °C may due to the formation of a ZnOx seed layer. The growth mechanism involved has been described by a combination of self-catalyzed vapor-liquid-solid (VLS and vapor-solid (VS mechanism. The results suggest that for a more precise study on the growth of ZnO nanostructures involving the introduction of seeds, the initial seed structures must be taken into account given their significant effects.

  19. A photoemission study of the effectiveness of nickel, manganese, and cobalt based corrosion barriers for silicon photo-anodes during water oxidation

    Energy Technology Data Exchange (ETDEWEB)

    O' Connor, Robert; Bogan, Justin; McCoy, Anthony; Byrne, Conor; Hughes, Greg [School of Physical Sciences, Dublin City University, Dublin 9 (Ireland)

    2016-05-21

    Silicon is an attractive material for solar water splitting applications due to its abundance and its capacity to absorb a large fraction of incident solar radiation. However, it has not received as much attention as other materials due to its tendency to oxidize very quickly in aqueous environments, particularly when it is employed as the anode where it drives the oxygen evolution reaction. In recent years, several works have appeared in the literature examining the suitability of thin transition metal oxide films grown on top of the silicon to act as a corrosion barrier. The film should be transparent to solar radiation, allow hole transport from the silicon surface to the electrolyte, and stop the diffusion of oxygen from the electrolyte back to the silicon. In this work, we compare Mn-oxide, Co-oxide, and Ni-oxide thin films grown using physical vapor deposition in order to evaluate which material offers the best combination of photocurrent and corrosion protection. In addition to the electrochemical data, we also present a detailed before-and-after study of the surface chemistry of the films using x-ray photoelectron spectroscopy. This approach allows for a comprehensive analysis of the mechanisms by which the corrosion barriers protect the underlying silicon, and how they degrade during the water oxidation reaction.

  20. Synthesis of low-oxide blue luminescent alkyl-functionalized silicon nanoparticles with no nitrogen containing surfactant

    International Nuclear Information System (INIS)

    Thomas, Jason A.; Ashby, Shane P.; Huld, Frederik; Pennycook, Timothy J.; Chao, Yimin

    2015-01-01

    Of ever growing interest in the fields of physical chemistry and materials science, silicon nanoparticles show a great deal of potential. Methods for their synthesis are, however, often hazardous, expensive or otherwise impractical. In the literature, there is a safe, fast and cheap inverse micelle-based method for the production of alkyl-functionalized blue luminescent silicon nanoparticles, which nonetheless found limitations, due to undesirable Si-alkoxy and remaining Si–H functionalization. In the following work, these problems are addressed, whereby an optimisation of the reaction mechanism encourages more desirable capping, and the introduction of alcohol is replaced by the use of anhydrous copper (II) chloride. The resulting particles, when compared with their predecessors through a myriad of spectroscopic techniques, are shown to have greatly reduced levels of ‘undesirable’ capping, with a much lower surface oxide level; whilst also maintaining long-term air stability, strong photoluminescence and high yields

  1. Efficient Flame Detection and Early Warning Sensors on Combustible Materials Using Hierarchical Graphene Oxide/Silicone Coatings.

    Science.gov (United States)

    Wu, Qian; Gong, Li-Xiu; Li, Yang; Cao, Cheng-Fei; Tang, Long-Cheng; Wu, Lianbin; Zhao, Li; Zhang, Guo-Dong; Li, Shi-Neng; Gao, Jiefeng; Li, Yongjin; Mai, Yiu-Wing

    2018-01-23

    Design and development of smart sensors for rapid flame detection in postcombustion and early fire warning in precombustion situations are critically needed to improve the fire safety of combustible materials in many applications. Herein, we describe the fabrication of hierarchical coatings created by assembling a multilayered graphene oxide (GO)/silicone structure onto different combustible substrate materials. The resulting coatings exhibit distinct temperature-responsive electrical resistance change as efficient early warning sensors for detecting abnormal high environmental temperature, thus enabling fire prevention below the ignition temperature of combustible materials. After encountering a flame attack, we demonstrate extremely rapid flame detection response in 2-3 s and excellent flame self-extinguishing retardancy for the multilayered GO/silicone structure that can be synergistically transformed to a multiscale graphene/nanosilica protection layer. The hierarchical coatings developed are promising for fire prevention and protection applications in various critical fire risk and related perilous circumstances.

  2. Self-cleaning glass coating containing titanium oxide and silicon; Revestimentos autolimpantes para vidros contendo oxido de titanio e silicio

    Energy Technology Data Exchange (ETDEWEB)

    Araujo, A.O. de; Alves, A.K.; Berutti, F.A.; Bergmann, C.P. [Universidade Federal do Rio Grande do Sul (LACER/UFRGS), Porto Alegre, RS (Brazil). Lab. de Materiais Ceramicos

    2009-07-01

    Using the electro spinning technique nano fibers of titanium oxide doped with silicon were synthesized. As precursor materials, titanium propoxide, silicon tetra propoxide and a solution of polyvinylpyrrolidone were used. The non-tissue material obtained was characterized by X-ray diffraction to determine the phase and crystallite size, BET method to determine the surface and SEM to analyze the microstructure of the fibers. After ultrasound dispersion of this material in ethanol, the glass coatings were made by dip-coating methodology. The influence of the removal velocity, the solution composition and the glass surface preparation were evaluated. The film was characterized by the contact angle of a water droplet in its surface. (author)

  3. Sponge-like Si-SiO2 nanocomposite—Morphology studies of spinodally decomposed silicon-rich oxide

    Science.gov (United States)

    Friedrich, D.; Schmidt, B.; Heinig, K. H.; Liedke, B.; Mücklich, A.; Hübner, R.; Wolf, D.; Kölling, S.; Mikolajick, T.

    2013-09-01

    Sponge-like Si nanostructures embedded in SiO2 were fabricated by spinodal decomposition of sputter-deposited silicon-rich oxide with a stoichiometry close to that of silicon monoxide. After thermal treatment a mean feature size of about 3 nm was found in the phase-separated structure. The structure of the Si-SiO2 nanocomposite was investigated by energy-filtered transmission electron microscopy (EFTEM), EFTEM tomography, and atom probe tomography, which revealed a percolated Si morphology. It was shown that the percolation of the Si network in 3D can also be proven on the basis of 2D EFTEM images by comparison with 3D kinetic Monte Carlo simulations.

  4. Sponge-like Si-SiO2 nanocomposite—Morphology studies of spinodally decomposed silicon-rich oxide

    International Nuclear Information System (INIS)

    Friedrich, D.; Schmidt, B.; Heinig, K. H.; Liedke, B.; Mücklich, A.; Hübner, R.; Wolf, D.; Kölling, S.; Mikolajick, T.

    2013-01-01

    Sponge-like Si nanostructures embedded in SiO 2 were fabricated by spinodal decomposition of sputter-deposited silicon-rich oxide with a stoichiometry close to that of silicon monoxide. After thermal treatment a mean feature size of about 3 nm was found in the phase-separated structure. The structure of the Si-SiO 2 nanocomposite was investigated by energy-filtered transmission electron microscopy (EFTEM), EFTEM tomography, and atom probe tomography, which revealed a percolated Si morphology. It was shown that the percolation of the Si network in 3D can also be proven on the basis of 2D EFTEM images by comparison with 3D kinetic Monte Carlo simulations

  5. Synthesis of low-oxide blue luminescent alkyl-functionalized silicon nanoparticles with no nitrogen containing surfactant

    Energy Technology Data Exchange (ETDEWEB)

    Thomas, Jason A.; Ashby, Shane P.; Huld, Frederik [University of East Anglia, School of Chemistry (United Kingdom); Pennycook, Timothy J. [SuperSTEM Laboratory, STFC Daresbury Campus (United Kingdom); Chao, Yimin, E-mail: y.chao@uea.ac.uk [University of East Anglia, School of Chemistry (United Kingdom)

    2015-05-15

    Of ever growing interest in the fields of physical chemistry and materials science, silicon nanoparticles show a great deal of potential. Methods for their synthesis are, however, often hazardous, expensive or otherwise impractical. In the literature, there is a safe, fast and cheap inverse micelle-based method for the production of alkyl-functionalized blue luminescent silicon nanoparticles, which nonetheless found limitations, due to undesirable Si-alkoxy and remaining Si–H functionalization. In the following work, these problems are addressed, whereby an optimisation of the reaction mechanism encourages more desirable capping, and the introduction of alcohol is replaced by the use of anhydrous copper (II) chloride. The resulting particles, when compared with their predecessors through a myriad of spectroscopic techniques, are shown to have greatly reduced levels of ‘undesirable’ capping, with a much lower surface oxide level; whilst also maintaining long-term air stability, strong photoluminescence and high yields.

  6. Dielectric discontinuity at interfaces in the atomic-scale limit: permittivity of ultrathin oxide films on silicon.

    Science.gov (United States)

    Giustino, Feliciano; Umari, Paolo; Pasquarello, Alfredo

    2003-12-31

    Using a density-functional approach, we study the dielectric permittivity across interfaces at the atomic scale. Focusing on the static and high-frequency permittivities of SiO2 films on silicon, for oxide thicknesses from 12 A down to the atomic scale, we find a departure from bulk values in accord with experiment. A classical three-layer model accounts for the calculated permittivities and is supported by the microscopic polarization profile across the interface. The local screening varies on length scales corresponding to first-neighbor distances, indicating that the dielectric transition is governed by the chemical grading. Silicon-induced gap states are shown to play a minor role.

  7. Interaction at the silicon/transition metal oxide heterojunction interface and its effect on the photovoltaic performance.

    Science.gov (United States)

    Liang, Zhimin; Su, Mingze; Zhou, Yangyang; Gong, Li; Zhao, Chuanxi; Chen, Keqiu; Xie, Fangyan; Zhang, Weihong; Chen, Jian; Liu, Pengyi; Xie, Weiguang

    2015-11-07

    The interfacial reaction and energy level alignment at the Si/transition metal oxide (TMO, including MoO3-x, V2O5-x, WO3-x) heterojunction are systematically investigated. We confirm that the interfacial reaction appears during the thermal deposition of TMO, with the reaction extent increasing from MoO3-x, to V2O5-x, and to WO3-x. The reaction causes the surface oxidation of silicon for faster electron/hole recombination, and the reduction of TMO for effective hole collection. The photovoltaic performance of the Si/TMO heterojunction devices is affected by the interface reaction. MoO3-x are the best hole selecting materials that induce least surface oxidation but strongest reduction. Compared with H-passivation, methyl group passivation is an effective way to reduce the interface reaction and improve the interfacial energy level alignment for better electron and hole collection.

  8. Non-classical polycrystalline silicon thin-film transistor with embedded block-oxide for suppressing the short channel effect

    International Nuclear Information System (INIS)

    Lin, Jyi-Tsong; Huang, Kuo-Dong; Hu, Shu-Fen

    2008-01-01

    In this paper, a polycrystalline silicon (polysilicon) thin-film transistor with a block oxide enclosing body, BTFT, is fabricated and investigated. By utilizing the block-oxide structure of thin-film transistors, the BTFT is shown to suppress the short channel effect. This proposed structure is formed by burying self-aligned oxide spacers along the sidewalls of the source and drain junctions, which reduces the P–N junction area, thereby reducing the junction capacitance and leakage current. Measurements demonstrate that the BTFT eliminates the punch-through effect even down to gate lengths of 1.5 µm, whereas the conventional TFT suffers serious short channel effects at this gate length

  9. Substoichiometrically different mitotypes coexist in mitochondrial genomes of Brassica napus L.

    Directory of Open Access Journals (Sweden)

    Jianmei Chen

    Full Text Available Cytoplasmic male sterility (CMS has been identified in numerous plant species. Brassica napus CMS plants, such as Polima (pol, MI, and Shaan 2A, have been identified independently by different researchers with different materials in conventional breeding processes. How this kind of CMS emerges is unclear. Here, we report the mitochondrial genome sequence of the prevalent mitotype in the most widely used pol-CMS line, which has a length of 223,412 bp and encodes 34 proteins, 3 ribosomal RNAs, and 18 tRNAs, including two near identical copies of trnH. Of these 55 genes, 48 were found to be identical to their equivalents in the "nap" cytoplasm. The nap mitotype carries only one copy of trnH, and the sequences of five of the six remaining genes are highly similar to their equivalents in the pol mitotype. Forty-four open reading frames (ORFs with unknown function were detected, including two unique to the pol mitotype (orf122 and orf132. At least five rearrangement events are required to account for the structural differences between the pol and nap sequences. The CMS-related orf224 neighboring region (∼5 kb rearranged twice. PCR profiling based on mitotype-specific primer pairs showed that both mitotypes are present in B. napus cultivars. Quantitative PCR showed that the pol cytoplasm consists mainly of the pol mitotype, and the nap mitotype is the main genome of nap cytoplasm. Large variation in the copy number ratio of mitotypes was found, even among cultivars sharing the same cytoplasm. The coexistence of mitochondrial mitotypes and substoichiometric shifting can explain the emergence of CMS in B. napus.

  10. Strong and reversible modulation of carbon nanotube-silicon heterojunction solar cells by an interfacial oxide layer.

    Science.gov (United States)

    Jia, Yi; Cao, Anyuan; Kang, Feiyu; Li, Peixu; Gui, Xuchun; Zhang, Luhui; Shi, Enzheng; Wei, Jinquan; Wang, Kunlin; Zhu, Hongwei; Wu, Dehai

    2012-06-21

    Deposition of nanostructures such as carbon nanotubes on Si wafers to make heterojunction structures is a promising route toward high efficiency solar cells with reduced cost. Here, we show a significant enhancement in the cell characteristics and power conversion efficiency by growing a silicon oxide layer at the interface between the nanotube film and Si substrate. The cell efficiency increases steadily from 0.5% without interfacial oxide to 8.8% with an optimal oxide thickness of about 1 nm. This systematic study reveals that formation of an oxide layer switches charge transport from thermionic emission to a mixture of thermionic emission and tunneling and improves overall diode properties, which are critical factors for tailoring the cell behavior. By controlled formation and removal of interfacial oxide, we demonstrate oscillation of the cell parameters between two extreme states, where the cell efficiency can be reversibly altered by a factor of 500. Our results suggest that the oxide layer plays an important role in Si-based photovoltaics, and it might be utilized to tune the cell performance in various nanostructure-Si heterojunction structures.

  11. Surface Area, and Oxidation Effects on Nitridation Kinetics of Silicon Powder Compacts

    Science.gov (United States)

    Bhatt, R. T.; Palczer, A. R.

    1998-01-01

    Commercially available silicon powders were wet-attrition-milled from 2 to 48 hr to achieve surface areas (SA's) ranging from 1.3 to 70 sq m/g. The surface area effects on the nitridation kinetics of silicon powder compacts were determined at 1250 or 1350 C for 4 hr. In addition, the influence of nitridation environment, and preoxidation on nitridation kinetics of a silicon powder of high surface area (approximately equals 63 sq m/g) was investigated. As the surface area increased, so did the percentage nitridation after 4 hr in N2 at 1250 or 1350 C. Silicon powders of high surface area (greater than 40 sq m/g) can be nitrided to greater than 70% at 1250 C in 4 hr. The nitridation kinetics of the high-surface-area powder compacts were significantly delayed by preoxidation treatment. Conversely, the nitridation environment had no significant influence on the nitridation kinetics of the same powder. Impurities present in the starting powder, and those accumulated during attrition milling, appeared to react with the silica layer on the surface of silicon particles to form a molten silicate layer, which provided a path for rapid diffusion of nitrogen and enhanced the nitridation kinetics of high surface area silicon powder.

  12. Novel processing of bioglass ceramics from silicone resins containing micro- and nano-sized oxide particle fillers.

    Science.gov (United States)

    Fiocco, L; Bernardo, E; Colombo, P; Cacciotti, I; Bianco, A; Bellucci, D; Sola, A; Cannillo, V

    2014-08-01

    Highly porous scaffolds with composition similar to those of 45S5 and 58S bioglasses were successfully produced by an innovative processing method based on preceramic polymers containing micro- and nano-sized fillers. Silica from the decomposition of the silicone resins reacted with the oxides deriving from the fillers, yielding glass ceramic components after heating at 1000°C. Despite the limited mechanical strength, the obtained samples possessed suitable porous architecture and promising biocompatibility and bioactivity characteristics, as testified by preliminary in vitro tests. © 2013 Wiley Periodicals, Inc.

  13. Low-power bacteriorhodopsin-silicon n-channel metal-oxide field-effect transistor photoreceiver.

    Science.gov (United States)

    Shin, Jonghyun; Bhattacharya, Pallab; Yuan, Hao-Chih; Ma, Zhenqiang; Váró, György

    2007-03-01

    A bacteriorhodopsin (bR)-silicon n-channel metal-oxide field-effect transistor (NMOSFET) monolithically integrated photoreceiver is demonstrated. The bR film is selectively formed on an external gate electrode of the transistor by electrophoretic deposition. A modified biasing circuit is incorporated, which helps to match the resistance of the bR film to the input impedance of the NMOSFET and to shift the operating point of the transistor to coincide with the maximum gain. The photoreceiver exhibits a responsivity of 4.7 mA/W.

  14. Effects of keV electron irradiation on the avalanche-electron generation rates of three donors on oxidized silicon

    International Nuclear Information System (INIS)

    Sah, C.; Sun, J.Y.; Tzou, J.J.

    1983-01-01

    After keV electron beam irradiation of oxidized silicon, the avalanche-electron-injection generation rates and densities of the bulk compensating donor, the interface states, and the turnaround trap all increase. Heating at 200 0 C can anneal out these three donor-like traps, however, it cannot restore the generation rates back to their original and lower pre-keV electron irradiation values. The experimental results also indicate that all three traps may be related to the same mobile impurity species whose bonds are loosened by the keV electrons and then broken or released by the avalanche injected electrons

  15. Electrical analysis of high dielectric constant insulator and metal gate metal oxide semiconductor capacitors on flexible bulk mono-crystalline silicon

    KAUST Repository

    Ghoneim, Mohamed T.

    2015-06-01

    We report on the electrical study of high dielectric constant insulator and metal gate metal oxide semiconductor capacitors (MOSCAPs) on a flexible ultra-thin (25 μm) silicon fabric which is peeled off using a CMOS compatible process from a standard bulk mono-crystalline silicon substrate. A lifetime projection is extracted using statistical analysis of the ramping voltage (Vramp) breakdown and time dependent dielectric breakdown data. The obtained flexible MOSCAPs operational voltages satisfying the 10 years lifetime benchmark are compared to those of the control MOSCAPs, which are not peeled off from the silicon wafer. © 2014 IEEE.

  16. Oxidation of hydrogen-passivated silicon surfaces by scanning near-field optical lithography using uncoated and aluminum-coated fiber probes

    DEFF Research Database (Denmark)

    Madsen, Steen; Bozhevolnyi, Sergey I.; Birkelund, Karen

    1997-01-01

    Optically induced oxidation of hydrogen-passivated silicon surfaces using a scanning near-field optical microscope was achieved with both uncoated and aluminum-coated fiber probes. Line scans on amorphous silicon using uncoated fiber probes display a three-peak profile after etching in potassium...... hydroxide. Numerical simulations of the electromagnetic field around the probe-sample interaction region are used to explain the experimental observations. With an aluminum-coated fiber probe, lines of 35 nm in width were transferred into the amorphous silicon layer. (C) 1997 American Institute of Physics....

  17. Experimental study of nucleate pool boiling heat transfer of water on silicon oxide nanoparticle coated copper heating surface

    International Nuclear Information System (INIS)

    Das, Sudev; Kumar, D.S.; Bhaumik, Swapan

    2016-01-01

    Highlights: • EBPVD approach was employed for fabrication of well-ordered nanoparticle coated micro/nanostructure on metal surface. • Nucleate boiling heat transfer performance on nanoparticle coated micro/nanostructure surface was experimentally studied. • Stability of nanoparticle coated surface under boiling environment was systematically studied. • 58% enhancement of boiling heat transfer coefficient was found. • Present experimental results are validated with well known boiling correlations. - Abstract: Electron beam physical vapor deposition (EBPVD) coating approach was employed for fabrication of well-ordered of nanoparticle coated micronanostructures on metal surfaces. This paper reports the experimental study of augmentation of pool boiling heat transfer performance and stabilities of silicon oxide nanoparticle coated surfaces with water at atmospheric pressure. The surfaces were characterized with respect to dynamic contact angle, surface roughness, topography, and morphology. The results were found that there is a reduction of about 36% in the incipience superheat and 58% enhancement in heat transfer coefficient for silicon oxide coated surface over the untreated surface. This enhancement might be the reason of enhanced wettability, enhanced surface roughness and increased number of a small artificial cavity on a heating surface. The performance and stability of nanoparticle coated micro/nanostructure surfaces were examined and found that after three runs of experiment the heat transfer coefficient with heat flux almost remain constant.

  18. Ultra-thin silicon oxide layers on crystalline silicon wafers: Comparison of advanced oxidation techniques with respect to chemically abrupt SiO{sub 2}/Si interfaces with low defect densities

    Energy Technology Data Exchange (ETDEWEB)

    Stegemann, Bert, E-mail: bert.stegemann@htw-berlin.de [HTW Berlin - University of Applied Sciences, 12459 Berlin (Germany); Gad, Karim M. [University of Freiburg, Department of Microsystems Engineering - IMTEK, 79110 Freiburg (Germany); Balamou, Patrice [HTW Berlin - University of Applied Sciences, 12459 Berlin (Germany); Helmholtz Center Berlin for Materials and Energy (HZB), 12489 Berlin (Germany); Sixtensson, Daniel [Helmholtz Center Berlin for Materials and Energy (HZB), 12489 Berlin (Germany); Vössing, Daniel; Kasemann, Martin [University of Freiburg, Department of Microsystems Engineering - IMTEK, 79110 Freiburg (Germany); Angermann, Heike [Helmholtz Center Berlin for Materials and Energy (HZB), 12489 Berlin (Germany)

    2017-02-15

    Highlights: • Fabrication of ultrathin SiO{sub 2} tunnel layers on c-Si. • Correlation of electronic and chemical SiO{sub 2}/Si interface properties revealed by XPS/SPV. • Chemically abrupt SiO{sub 2}/Si interfaces generate less interface defect states considerable. - Abstract: Six advanced oxidation techniques were analyzed, evaluated and compared with respect to the preparation of high-quality ultra-thin oxide layers on crystalline silicon. The resulting electronic and chemical SiO{sub 2}/Si interface properties were determined by a combined x-ray photoemission (XPS) and surface photovoltage (SPV) investigation. Depending on the oxidation technique, chemically abrupt SiO{sub 2}/Si interfaces with low densities of interface states were fabricated on c-Si either at low temperatures, at short times, or in wet-chemical environment, resulting in each case in excellent interface passivation. Moreover, the beneficial effect of a subsequent forming gas annealing (FGA) step for the passivation of the SiO{sub 2}/Si interface of ultra-thin oxide layers has been proven. Chemically abrupt SiO{sub 2}/Si interfaces have been shown to generate less interface defect states.

  19. Growth and structure of rapid thermal silicon oxides and nitroxides studied by spectroellipsometry and Auger electron spectroscopy

    Science.gov (United States)

    Gonon, N.; Gagnaire, A.; Barbier, D.; Glachant, A.

    1994-11-01

    Rapid thermal oxidation of Czochralski-grown silicon in either O2 or N2O atmospheres have been studied using spectroellipsometry and Auger electron spectroscopy. Multiwavelength ellipsometric data were processed in order to separately derive the thickness and refractive indexes of rapid thermal dielectrics. Results revealed a significant increase of the mean refractive index as the film thickness falls below 20 nm for both O2 or N2O oxidant species. A multilayer structure including an about 0.3-nm-thick interfacial region of either SiO(x) or nitroxide in the case of O2 and N2O growth, respectively, followed by a densified SiO2 layer, was found to accurately fit the experimental data. The interfacial region together with the densified state of SiO2 close to the interface suggest a dielectric structure in agreement with the continuous random network model proposed for classical thermal oxides. Auger electron spectroscopy analysis confirmed the presence of noncrystalline Si-Si bonds in the interfacial region, mostly in the case of thin oxides grown in O2. It was speculated that the initial fast growth regime was due to a transient oxygen supersaturation in the interfacial region. Besides, the self-limiting growth in N2O was confirmed and explained in agreement with several recently published data, by the early formation of a very thin nitride or oxynitride membrane in the highly densified oxide beneath the interface. The beneficial effect of direct nitrogen incorporation by rapid thermal oxidation in N2O instead of O2 for the electrical behavior of metal-oxide-semiconductor capacitors is likely a better SiO2/Si lattice accommodation through the reduction of stresses and Si-Si bonds in the interfacial region of the dielectric.

  20. The effect of silicon content on high temperature oxidation of 80Ni-20Cr alloys

    International Nuclear Information System (INIS)

    Takei, Atsushi; Nii, Kazuyoshi

    1981-01-01

    The effect of Si content on the oxidation behavior of 80Ni-20Cr alloys has been studied in the cyclic oxidation in an air stream at 1373K. The addition of 1% and 5%Si to the alloy lowered the mass gain in oxidation, whereas the amount of spalling of oxide scale was increased with the addition of Si. The structure of oxide layers observed by microphotography, X-ray diffraction and electron probe microanalysis (EPMA) were different with the Si content of alloys. The oxide layer of the alloy with 1%Si consists of multi-layers, that is Ni oxide, Cr 2 O 3 and SiO 2 as the external oxide layer. The oxide layer remaining on the alloy with 5%Si, however, was made of a single oxide layer of Cr 2 O 3 containing small amounts of Si and Ni. In spite of the fact that the amount of Si in this alloy is larger than that of the alloy with 1%Si, the SiO 2 oxide layer was not observed at the oxide-alloy interface. It was found by EPMA that the concentration of Si in the oxidized 5%Si alloy substrate was increased in the vicinity of the surface, although Si in the 1%Si alloy was depleted. From the above results the internal oxidation of Si is assumed in the near-surface region of the 5%Si alloy. The internal oxidation of the 5%Si alloy was confirmed by an increase in hardness in the near-surface region. The difference in oxidation behavior between the 1%Si and 5%Si alloys can be understood under the assumption that the oxide layer formed of the 5%Si alloy contained much larger amounts of Ni and Si than that on the 1%Si alloy, and that this oxide layer tends to crack more easily, thus being less protective for the penetration of oxygen. (author)

  1. Atomic layer deposited ZnO:B as transparent conductive oxide for silicon heterojunction solar cells

    NARCIS (Netherlands)

    Gatz, H.A.; Koushik, D.; Rath, J.K.; Kessels, W.M.M.; Schropp, R.E.I.

    A key factor to improve the performance of silicon heterojunction solar cells (SHJ) is increasing their short circuit density (Jsc) by reducing the parasitic absorption of light in the front side of the cell. Therefore, we have investigated the replacement of the conventional sputtered ITO on the

  2. Recognition enhancement of oxidized and methyl-10-undecenoate functionalized porous silicon in gas phase photoluminescence sensing

    Czech Academy of Sciences Publication Activity Database

    Dian, J.; Vrkoslav, Vladimír; Jelínek, I.

    2010-01-01

    Roč. 147, - (2010), s. 406-410 ISSN 0925-4005 Institutional research plan: CEZ:AV0Z40550506 Keywords : porous silicon * photoluminescence * sensor * recognition enhancement Subject RIV: CC - Organic Chemistry Impact factor: 3.368, year: 2010

  3. High performance high-κ/metal gate complementary metal oxide semiconductor circuit element on flexible silicon

    KAUST Repository

    Sevilla, Galo T.; Almuslem, A. S.; Gumus, Abdurrahman; Hussain, Aftab M.; Hussain, Aftab M.; Cruz, Melvin; Hussain, Muhammad Mustafa

    2016-01-01

    shows large area of silicon thinning with pre-fabricated high performance elements with ultra-large-scale-integration density (using 90 nm node technology) and then dicing of such large and thinned (seemingly fragile) pieces into smaller pieces using

  4. Tunnel oxide passivated rear contact for large area n-type front junction silicon solar cells providing excellent carrier selectivity

    Directory of Open Access Journals (Sweden)

    Yuguo Tao

    2016-01-01

    Full Text Available Carrier-selective contact with low minority carrier recombination and efficient majority carrier transport is mandatory to eliminate metal-induced recombination for higher energy conversion efficiency for silicon (Si solar cells. In the present study, the carrier-selective contact consists of an ultra-thin tunnel oxide and a phosphorus-doped polycrystalline Si (poly-Si thin film formed by plasma enhanced chemical vapor deposition (PECVD and subsequent thermal crystallization. It is shown that the poly-Si film properties (doping level, crystallization and dopant activation anneal temperature are crucial for achieving excellent contact passivation quality. It is also demonstrated quantitatively that the tunnel oxide plays a critical role in this tunnel oxide passivated contact (TOPCON scheme to realize desired carrier selectivity. Presence of tunnel oxide increases the implied Voc (iVoc by ~ 125 mV. The iVoc value as high as 728 mV is achieved on symmetric structure with TOPCON on both sides. Large area (239 cm2 n-type Czochralski (Cz Si solar cells are fabricated with homogeneous implanted boron emitter and screen-printed contact on the front and TOPCON on the back, achieving 21.2% cell efficiency. Detailed analysis shows that the performance of these cells is mainly limited by boron emitter recombination on the front side.

  5. Stable Organic Monolayers on Oxide-Free Silicon/Germanium in a Supercritical Medium: A New Route to Molecular Electronics.

    Science.gov (United States)

    Puniredd, Sreenivasa Reddy; Jayaraman, Sundaramurthy; Yeong, Sai Hooi; Troadec, Cedric; Srinivasan, M P

    2013-05-02

    Oxide-free Si and Ge surfaces have been passivated and modified with organic molecules by forming covalent bonds between the surfaces and reactive end groups of linear alkanes and aromatic species using single-step deposition in supercritical carbon dioxide (SCCO2). The process is suitable for large-scale manufacturing due to short processing times, simplicity, and high resistance to oxidation. It also allows the formation of monolayers with varying reactive terminal groups, thus enabling formation of nanostructures engineered at the molecular level. Ballistic electron emission microscopy (BEEM) spectra performed on the organic monolayer on oxide-free silicon capped by a thin gold layer reveals for the first time an increase in transmission of the ballistic current through the interface of up to three times compared to a control device, in contrast to similar studies reported in the literature suggestive of oxide-free passivation in SCCO2. The SCCO2 process combined with the preliminary BEEM results opens up new avenues for interface engineering, leading to molecular electronic devices.

  6. Research status in ultra-precision machining of silicon carbide parts by oxidation-assisted polishing

    Directory of Open Access Journals (Sweden)

    Xinmin SHEN

    2016-10-01

    Full Text Available Oxidation-assisted polishing is an important machining method for obtaining SiC parts with high precision. Through plasma oxidation, thermal oxidation, and anodic oxidation, soft oxide can be obtained on the RS-SiC substrate. With the assistance of abrasive polishing to remove the oxide rapidly, the material removal rate can be increased and the surface quality can be improved. The research results indicate that the surface roughness root-mean-square (RMS and roughness-average (Ra can reach 0.626 nm and 0.480 nm by plasma oxidation-assisted polishing; in thermal oxidation-assisted polishing, the RMS and Ra can be 0.920 nm and 0.726 nm; in anodic oxidation, the calculated oxidation rate is 5.3 nm/s based on Deal-Grove model, and the RMS and Ra are 4.428 nm and 3.453 nm respectively in anodic oxidation-assisted polishing. The oxidation-assisted polishing can be propitious to improve the process level in machining RS-SiC, which would promote the application of SiC parts in optics and ceramics fields.

  7. Growth of light-emitting SiGe heterostructures on strained silicon-on-insulator substrates with a thin oxide layer

    Energy Technology Data Exchange (ETDEWEB)

    Baidakova, N. A., E-mail: banatale@ipmras.ru [Russian Academy of Sciences, Institute for Physics of Microstructures (Russian Federation); Bobrov, A. I. [University of Nizhny Novgorod (Russian Federation); Drozdov, M. N.; Novikov, A. V. [Russian Academy of Sciences, Institute for Physics of Microstructures (Russian Federation); Pavlov, D. A. [University of Nizhny Novgorod (Russian Federation); Shaleev, M. V.; Yunin, P. A.; Yurasov, D. V.; Krasilnik, Z. F. [Russian Academy of Sciences, Institute for Physics of Microstructures (Russian Federation)

    2015-08-15

    The possibility of using substrates based on “strained silicon on insulator” structures with a thin (25 nm) buried oxide layer for the growth of light-emitting SiGe structures is studied. It is shown that, in contrast to “strained silicon on insulator” substrates with a thick (hundreds of nanometers) oxide layer, the temperature stability of substrates with a thin oxide is much lower. Methods for the chemical and thermal cleaning of the surface of such substrates, which make it possible to both retain the elastic stresses in the thin Si layer on the oxide and provide cleaning of the surface from contaminating impurities, are perfecte. It is demonstrated that it is possible to use the method of molecular-beam epitaxy to grow light-emitting SiGe structures of high crystalline quality on such substrates.

  8. Efficient and Stable CsPbBr3 Quantum-Dot Powders Passivated and Encapsulated with a Mixed Silicon Nitride and Silicon Oxide Inorganic Polymer Matrix.

    Science.gov (United States)

    Yoon, Hee Chang; Lee, Soyoung; Song, Jae Kyu; Yang, Heesun; Do, Young Rag

    2018-04-11

    Despite the excellent optical features of fully inorganic cesium lead halide (CsPbX 3 ) perovskite quantum dots (PeQDs), their unstable nature has limited their use in various optoelectronic devices. To mitigate the instability issues of PeQDs, we demonstrate the roles of dual-silicon nitride and silicon oxide ligands of the polysilazane (PSZ) inorganic polymer to passivate the surface defects and form a barrier layer coated onto green CsPbBr 3 QDs to maintain the high photoluminescence quantum yield (PLQY) and improve the environmental stability. The mixed SiN x /SiN x O y /SiO y passivated and encapsulated CsPbBr 3 /PSZ core/shell composite can be prepared by a simple hydrolysis reaction involving the addition of adding PSZ as a precursor and a slight amount of water into a colloidal CsPbBr 3 QD solution. The degree of the moisture-induced hydrolysis reaction of PSZ can affect the compositional ratio of SiN x , SiN x O y , and SiO y liganded to the surfaces of the CsPbBr 3 QDs to optimize the PLQY and the stability of CsPbBr 3 /PSZ core/shell composite, which shows a high PLQY (∼81.7%) with improved thermal, photo, air, and humidity stability as well under coarse conditions where the performance of CsPbBr 3 QDs typically deteriorate. To evaluate the suitability of the application of the CsPbBr 3 /PSZ powder to down-converted white-light-emitting diodes (DC-WLEDs) as the backlight of a liquid crystal display (LCD), we fabricated an on-package type of tricolor-WLED by mixing the as-synthesized green CsPbBr 3 /PSZ composite powder with red K 2 SiF 6 :Mn 4+ phosphor powder and a poly(methyl methacrylate)-encapsulating binder and coating this mixed paste onto a cup-type blue LED. The fabricated WLED show high luminous efficacy of 138.6 lm/W (EQE = 51.4%) and a wide color gamut of 128% and 111% without and with color filters, respectively, at a correlated color temperature of 6762 K.

  9. Bis(tri-n-hexylsilyl oxide) silicon phthalocyanine: a unique additive in ternary bulk heterojunction organic photovoltaic devices.

    Science.gov (United States)

    Lessard, Benoît H; Dang, Jeremy D; Grant, Trevor M; Gao, Dong; Seferos, Dwight S; Bender, Timothy P

    2014-09-10

    Previous studies have shown that the use of bis(tri-n-hexylsilyl oxide) silicon phthalocyanine ((3HS)2-SiPc) as an additive in a P3HT:PC61BM cascade ternary bulk heterojunction organic photovoltaic (BHJ OPV) device results in an increase in the short circuit current (J(SC)) and efficiency (η(eff)) of up to 25% and 20%, respectively. The previous studies have attributed the increase in performance to the presence of (3HS)2-SiPc at the BHJ interface. In this study, we explored the molecular characteristics of (3HS)2-SiPc which makes it so effective in increasing the OPV device J(SC) and η(eff. Initially, we synthesized phthalocyanine-based additives using different core elements such as germanium and boron instead of silicon, each having similar frontier orbital energies compared to (3HS)2-SiPc and tested their effect on BHJ OPV device performance. We observed that addition of bis(tri-n-hexylsilyl oxide) germanium phthalocyanine ((3HS)2-GePc) or tri-n-hexylsilyl oxide boron subphthalocyanine (3HS-BsubPc) resulted in a nonstatistically significant increase in JSC and η(eff). Secondly, we kept the silicon phthalocyanine core and substituted the tri-n-hexylsilyl solubilizing groups with pentadecyl phenoxy groups and tested the resulting dye in a BHJ OPV. While an increase in JSC and η(eff) was observed at low (PDP)2-SiPc loadings, the increase was not as significant as (3HS)2-SiPc; therefore, (3HS)2-SiPc is a unique additive. During our study, we observed that (3HS)2-SiPc had an extraordinary tendency to crystallize compared to the other compounds in this study and our general experience. On the basis of this observation, we have offered a hypothesis that when (3HS)2-SiPc migrates to the P3HT:PC61BM interface the reason for its unique performance is not solely due to its frontier orbital energies but also might be due to a high driving force for crystallization.

  10. Structural and electrical characteristics of high-k/metal gate metal oxide semiconductor capacitors fabricated on flexible, semi-transparent silicon (100) fabric

    KAUST Repository

    Rojas, Jhonathan Prieto

    2013-02-12

    In pursuit of flexible computers with high performance devices, we demonstrate a generic process to fabricate 10 000 metal-oxide-semiconductor capacitors (MOSCAPs) with semiconductor industry\\'s most advanced high-k/metal gate stacks on widely used, inexpensive bulk silicon (100) wafers and then using a combination of iso-/anisotropic etching to release the top portion of the silicon with the already fabricated devices as a mechanically flexible (bending curvature of 133 m−1), optically semi-transparent silicon fabric (1.5 cm × 3 cm × 25 μm). The electrical characteristics show 3.7 nm effective oxide thickness, −0.2 V flat band voltage, and no hysteresis from the fabricated MOSCAPs.

  11. Structural and electrical characteristics of high-k/metal gate metal oxide semiconductor capacitors fabricated on flexible, semi-transparent silicon (100) fabric

    KAUST Repository

    Rojas, Jhonathan Prieto; Hussain, Muhammad Mustafa; Sevilla, Galo T.

    2013-01-01

    In pursuit of flexible computers with high performance devices, we demonstrate a generic process to fabricate 10 000 metal-oxide-semiconductor capacitors (MOSCAPs) with semiconductor industry's most advanced high-k/metal gate stacks on widely used, inexpensive bulk silicon (100) wafers and then using a combination of iso-/anisotropic etching to release the top portion of the silicon with the already fabricated devices as a mechanically flexible (bending curvature of 133 m−1), optically semi-transparent silicon fabric (1.5 cm × 3 cm × 25 μm). The electrical characteristics show 3.7 nm effective oxide thickness, −0.2 V flat band voltage, and no hysteresis from the fabricated MOSCAPs.

  12. White-emitting oxidized silicon nanocrystals: Discontinuity in spectral development with reducing size

    Czech Academy of Sciences Publication Activity Database

    Dohnalová, Kateřina; Ondič, Lukáš; Kůsová, Kateřina; Pelant, Ivan; Rehspringer, J.L.; Mafouana, R.-R.

    2010-01-01

    Roč. 107, č. 5 (2010), 053102/1-053102/6 ISSN 0021-8979 R&D Projects: GA AV ČR(CZ) IAA101120804; GA MŠk LC510; GA AV ČR KJB100100903; GA ČR GA202/07/0818 Institutional research plan: CEZ:AV0Z10100521 Keywords : silicon nanocrystals * luminescence * spectral shift Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.064, year: 2010

  13. Electrical analysis of high dielectric constant insulator and metal gate metal oxide semiconductor capacitors on flexible bulk mono-crystalline silicon

    KAUST Repository

    Ghoneim, Mohamed T.; Rojas, Jhonathan Prieto; Young, Chadwin D.; Bersuker, Gennadi; Hussain, Muhammad Mustafa

    2015-01-01

    We report on the electrical study of high dielectric constant insulator and metal gate metal oxide semiconductor capacitors (MOSCAPs) on a flexible ultra-thin (25 μm) silicon fabric which is peeled off using a CMOS compatible process from a standard

  14. High-temperature oxidation of silicide-aluminide layer on the TiAl6V4 alloy prepared by liquid-phase siliconizing

    Czech Academy of Sciences Publication Activity Database

    Kubatík, Tomáš František

    2016-01-01

    Roč. 50, č. 2 (2016), s. 257-261 ISSN 1580-2949 Institutional support: RVO:61389021 Keywords : TiAl6V4 * silicides * high-temperature oxidation * liquid-phase silicon izing Subject RIV: JG - Metallurgy Impact factor: 0.436, year: 2016

  15. Ultra-high temperature oxidation behavior of chemical vapor deposited silicon carbide layers

    International Nuclear Information System (INIS)

    Goto, Takashi

    2003-01-01

    The active oxidation, passive oxidation and bubble formation of CVD SiC were studied in O 2 and CO 2 at temperatures from 1650 to 2000 K. The active oxidation rates in O 2 increased with increasing oxygen partial pressure (P o2 ); however, those in CO 2 showed the maxima at specific P o2 . The passive oxidation kinetics in O 2 were either linear-parabolic or parabolic depending on temperature and P o2 , whereas that in CO 2 was always parabolic. The activation energies for the parabolic oxidation in O 2 and CO 2 were 210 and 150 kJ/mol, respectively, suggesting different rate-determining process between these atmospheres. The bubble formation was controlled by temperature and P o2 being independent of oxidant gas species. (author)

  16. Single-electron regime and Pauli spin blockade in a silicon metal-oxide-semiconductor double quantum dot

    Science.gov (United States)

    Rochette, Sophie; Ten Eyck, Gregory A.; Pluym, Tammy; Lilly, Michael P.; Carroll, Malcolm S.; Pioro-Ladrière, Michel

    2015-03-01

    Silicon quantum dots are promising candidates for quantum information processing as spin qubits with long coherence time. We present electrical transport measurements on a silicon metal-oxide-semiconductor (MOS) double quantum dot (DQD). First, Coulomb diamonds measurements demonstrate the one-electron regime at a relatively high temperature of 1.5 K. Then, the 8 mK stability diagram shows Pauli spin blockade with a large singlet-triplet separation of approximatively 0.40 meV, pointing towards a strong lifting of the valley degeneracy. Finally, numerical simulations indicate that by integrating a micro-magnet to those devices, we could achieve fast spin rotations of the order of 30 ns. Those results are part of the recent body of work demonstrating the potential of Si MOS DQD as reliable and long-lived spin qubits that could be ultimately integrated into modern electronic facilities. Sandia National Laboratories is a multi-program laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. DOE's National Nuclear Security Administration under Contract DE-AC04-94AL85000.

  17. Gas Permeation, Mechanical Behavior and Cytocompatibility of Ultrathin Pure and Doped Diamond-Like Carbon and Silicon Oxide Films

    Directory of Open Access Journals (Sweden)

    Juergen M. Lackner

    2013-12-01

    Full Text Available Protective ultra-thin barrier films gather increasing economic interest for controlling permeation and diffusion from the biological surrounding in implanted sensor and electronic devices in future medicine. Thus, the aim of this work was a benchmarking of the mechanical oxygen permeation barrier, cytocompatibility, and microbiological properties of inorganic ~25 nm thin films, deposited by vacuum deposition techniques on 50 µm thin polyetheretherketone (PEEK foils. Plasma-activated chemical vapor deposition (direct deposition from an ion source was applied to deposit pure and nitrogen doped diamond-like carbon films, while physical vapor deposition (magnetron sputtering in pulsed DC mode was used for the formation of silicon as well as titanium doped diamond-like carbon films. Silicon oxide films were deposited by radio frequency magnetron sputtering. The results indicate a strong influence of nanoporosity on the oxygen transmission rate for all coating types, while the low content of microporosity (particulates, etc. is shown to be of lesser importance. Due to the low thickness of the foil substrates, being easily bent, the toughness as a measure of tendency to film fracture together with the elasticity index of the thin films influence the oxygen barrier. All investigated coatings are non-pyrogenic, cause no cytotoxic effects and do not influence bacterial growth.

  18. Silicon (Si) alleviates cotton (Gossypium hirsutum L.) from zinc (Zn) toxicity stress by limiting Zn uptake and oxidative damage.

    Science.gov (United States)

    Anwaar, Shad Ali; Ali, Shafaqat; Ali, Skhawat; Ishaque, Wajid; Farid, Mujahid; Farooq, Muhammad Ahsan; Najeeb, Ullah; Abbas, Farhat; Sharif, Muhammad

    2015-03-01

    Silicon (Si) is as an important fertilizer element, which has been found effective in enhancing plant tolerance to variety of biotic and a-biotic stresses. This study investigates the Si potential to alleviate zinc (Zn) toxicity stress in cotton (Gossypium hirsutum L.). Cotton plants were grown in hydroponics and exposed to different Zn concentration, 0, 25, and 50 μM, alone and/or in combination with 1 mM Si. Incremental Zn concentration in growth media instigated the cellular oxidative damage that was evident from elevated levels of hydrogen peroxide (H2O2), electrolyte leakage, and malondialdehyde (MDA) and consequently inhibited cotton growth, biomass, chlorophyll pigments, and photosynthetic process. Application of Si significantly suppressed Zn accumulation in various plant parts, i.e., roots, stems, and leaves and thus promoted biomass, photosynthetic, growth parameters, and antioxidant enzymes activity of Zn-stressed as well unstressed plants. In addition, Si reduced the MDA and H2O2 production and electrolyte leakage suggesting its role in protecting cotton plants from Zn toxicity-induced oxidative damage. Thus, the study indicated that exogenous Si application could improve growth and development of cotton crop experiencing Zn toxicity stress by limiting Zn bioavailability and oxidative damage.

  19. Studies for the yttrium determination by activation analysis, in the presence of lanthanides. Application of the substoichiometric technique

    International Nuclear Information System (INIS)

    Silva, D.I.T. da.

    1978-01-01

    Some methods using extraction chromatography for the separation of yttrium from the lanthanide elements were applied. The separation of yttrium was studied, using di-(2 ethylhexyl) orthophosphoric acid as stationary phase, Kieselguhr as support and HNO 3 of concentration between 4,5 and 5,0 N as the mobile phase. In these conditions, about 50% of pure yttrium was obtained. The substoichiometric technique was applied to the determination of yttrium. The elements was partially complexed and the Y 3 + ions were separated from the complex (EDTA-Y) - by means of a cationic resin. The sensitivity, precision and accuracy which can be expected in the analytical results were studied. The possibility of the analysis of a sample containing 1 part per million of yttrium with an error just above 8% was demonstrated. It was also shown that, admitting an error of 10%, it is possible to determine 60 parts per billion of yttrium [pt

  20. Room temperature plasma oxidation: A new process for preparation of ultrathin layers of silicon oxide, and high dielectric constant materials

    International Nuclear Information System (INIS)

    Tinoco, J.C.; Estrada, M.; Baez, H.; Cerdeira, A.

    2006-01-01

    In this paper we present basic features and oxidation law of the room temperature plasma oxidation (RTPO), as a new process for preparation of less than 2 nm thick layers of SiO 2 , and high-k layers of TiO 2 . We show that oxidation rate follows a potential law dependence on oxidation time. The proportionality constant is function of pressure, plasma power, reagent gas and plasma density, while the exponent depends only on the reactive gas. These parameters are related to the physical phenomena occurring inside the plasma, during oxidation. Metal-Oxide-Semiconductor (MOS) capacitors fabricated with these layers are characterized by capacitance-voltage, current-voltage and current-voltage-temperature measurements. Less than 2.5 nm SiO 2 layers with surface roughness similar to thermal oxide films, surface state density below 3 x 10 11 cm -2 and current density in the expected range for each corresponding thickness, were obtained by RTPO in a parallel-plate reactor, at 180 mW/cm 2 and pressure range between 9.33 and 66.5 Pa (0.07 and 0.5 Torr) using O 2 and N 2 O as reactive gases. MOS capacitors with TiO 2 layers formed by RTPO of sputtered Ti layers are also characterized. Finally, MOS capacitors with stacked layers of TiO 2 over SiO 2 , both layers obtained by RTPO, were prepared and evaluated to determine the feasibility of the use of TiO 2 as a candidate for next technology nodes

  1. Low-temperature grown indium oxide nanowire-based antireflection coatings for multi-crystalline silicon solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Yu-Cian; Chen, Chih-Yao; Chen, I Chen [Institute of Materials Science and Engineering, National Central University, Taoyuan (China); Kuo, Cheng-Wen; Kuan, Ta-Ming; Yu, Cheng-Yeh [TSEC Corporation, Hsinchu (China)

    2016-08-15

    Light harvesting by indium oxide nanowires (InO NWs) as an antireflection layer on multi-crystalline silicon (mc-Si) solar cells has been investigated. The low-temperature growth of InO NWs was performed in electron cyclotron resonance (ECR) plasma with an O{sub 2}-Ar system using indium nanocrystals as seed particles via the self-catalyzed growth mechanism. The size-dependence of antireflection properties of InO NWs was studied. A considerable enhancement in short-circuit current (from 35.39 to 38.33 mA cm{sup -2}) without deterioration of other performance parameters is observed for mc-Si solar cells coated with InO NWs. (copyright 2016 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  2. Corrosion behavior of plasma sprayed hydroxyapatite and hydroxyapatite-silicon oxide coatings on AISI 304 for biomedical application

    International Nuclear Information System (INIS)

    Singh, Gurpreet; Singh, Hazoor; Sidhu, Buta Singh

    2013-01-01

    The objective of this study is to evaluate corrosion resistance of plasma sprayed hydroxyapatite (HA) and HA-silicon oxide (SiO 2 ) coated AISI 304 substrates. In HA-SiO 2 coatings, 10 wt% SiO 2 and 20 wt% SiO 2 was mixed with HA. The feedstock and coatings were characterized by X-ray diffraction and scanning electron microscopy/energy dispersive X-ray spectroscopy. The corrosion resistance was determined for the uncoated and coated samples. The corrosion resistance of the AISI 304 was found more after the deposition of the HA-SiO 2 coatings rather than HA coating and uncoated. All the coatings were crack free after 24 h dipping in Ringer's solution for electrochemical corrosion testing.

  3. Porous silicon carbide and aluminum oxide with unidirectional open porosity as model target materials for radioisotope beam production

    Energy Technology Data Exchange (ETDEWEB)

    Czapski, M., E-mail: michal.czapski@cern.ch [CERN, Genève 23 CH-1211 (Switzerland); Stora, T. [CERN, Genève 23 CH-1211 (Switzerland); Tardivat, C.; Deville, S. [Lab. de Synthèse et Fonctionnalisation des Céramiques, CNRS/Saint-Gobain, Av. Jauffret 84306 Cavaillon (France); Santos Augusto, R. [CERN, Genève 23 CH-1211 (Switzerland); Leloup, J.; Bouville, F. [Lab. de Synthèse et Fonctionnalisation des Céramiques, CNRS/Saint-Gobain, Av. Jauffret 84306 Cavaillon (France); Fernandes Luis, R. [Univ. Técnica de Lisboa Estrada Nacional 10, 2686-953 Sacavem, Loures (Portugal)

    2013-12-15

    Highlights: • SiC and Al{sub 2}O{sub 3} of uniaxial porosity were produced with ice-templating method. • The method allows controlled pore formation within the material. • Calculation of mechanical integrity under irradiation with protons was performed. • Generated thermal stresses should not exceed material’s strength. -- Abstract: New silicon carbide (SiC) and aluminum oxide (Al{sub 2}O{sub 3}) of a tailor-made microstructure were produced using the ice-templating technique, which permits controlled pore formation conditions within the material. These prototypes will serve to verify aging of the new advanced target materials under irradiation with proton beams. Before this, the evaluation of their mechanical integrity was made based on the energy deposition spectra produced by FLUKA codes.

  4. Comparative study on the deposition of silicon oxide permeation barrier coatings for polymers using hexamethyldisilazane (HMDSN) and hexamethyldisiloxane (HMDSO)

    Science.gov (United States)

    Mitschker, F.; Schücke, L.; Hoppe, Ch; Jaritz, M.; Dahlmann, R.; de los Arcos, T.; Hopmann, Ch; Grundmeier, G.; Awakowicz, P.

    2018-06-01

    The effect of the selection of hexamethyldisiloxane (HMDSO) and hexamethyldisilazane (HMDSN) as a precursor in a microwave driven low pressure plasma on the deposition of silicon oxide barrier coatings and silicon based organic interlayers on polyethylene terephthalate (PET) and polypropylene (PP) substrates is investigated. Mass spectrometry is used to quantify the absolute gas density and the degree of depletion of neutral precursor molecules under variation of oxygen admixture. On average, HMDSN shows a smaller density, a higher depletion and the production of smaller fragments. Subsequently, this is correlated with barrier performance and chemical structure as a function of barrier layer thickness and oxygen admixture on PET. For this purpose, the oxygen transmission rate (OTR) is measured and Fourier transformed infrared (FTIR) spectroscopy as well as x-ray photoelectron spectroscopy (XPS) is performed. HMDSN based coatings exhibit significantly higher barrier performances for high admixtures of oxygen (200 sccm). In comparison to HMDSO based processes, however, a higher supply of oxygen is necessary to achieve a sufficient degree of oxidation, cross-linking and, therefore, barrier performance. FTIR and XPS reveal a distinct carbon content for low oxygen admixtures (10 and 20 sccm) in case of HMDSN based coatings. The variation of interlayer thickness also reveals significantly higher OTR for HMDSO based coatings on PET and PP. Barrier performance of HMDSO based coatings improves with increasing interlayer thickness up to 10 nm for PET and PP. HMDSN based coatings exhibit a minimum of OTR without interlayer on PP and for 2 nm interlayer thickness on PET. Furthermore, HMDSN based coatings show distinctly higher bond strengths to the PP substrate.

  5. Encapsulation of sacrificial silicon containing particles for SH oxide ceramics via a boehmite precursor route

    NARCIS (Netherlands)

    Carabat, A.L.; Van der Zwaag, S.; Sloof, W.G.

    2013-01-01

    Easy crack propagation in oxide ceramic coatings limits their application in high temperature environment (e.g. such as engines and gas turbine components) [1]. In order to overcome this problem, incorporation of sacrificial particles into an oxide ceramic coating may be a viable option. Particles

  6. Forward-bias diode parameters, electronic noise, and photoresponse of graphene/silicon Schottky junctions with an interfacial native oxide layer

    Science.gov (United States)

    An, Yanbin; Behnam, Ashkan; Pop, Eric; Bosman, Gijs; Ural, Ant

    2015-09-01

    Metal-semiconductor Schottky junction devices composed of chemical vapor deposition grown monolayer graphene on p-type silicon substrates are fabricated and characterized. Important diode parameters, such as the Schottky barrier height, ideality factor, and series resistance, are extracted from forward bias current-voltage characteristics using a previously established method modified to take into account the interfacial native oxide layer present at the graphene/silicon junction. It is found that the ideality factor can be substantially increased by the presence of the interfacial oxide layer. Furthermore, low frequency noise of graphene/silicon Schottky junctions under both forward and reverse bias is characterized. The noise is found to be 1/f dominated and the shot noise contribution is found to be negligible. The dependence of the 1/f noise on the forward and reverse current is also investigated. Finally, the photoresponse of graphene/silicon Schottky junctions is studied. The devices exhibit a peak responsivity of around 0.13 A/W and an external quantum efficiency higher than 25%. From the photoresponse and noise measurements, the bandwidth is extracted to be ˜1 kHz and the normalized detectivity is calculated to be 1.2 ×109 cm Hz1/2 W-1. These results provide important insights for the future integration of graphene with silicon device technology.

  7. Study of thickness and uniformity of oxide passivation with DI-O3 on silicon substrate for electronic and photonic applications

    Science.gov (United States)

    Sharma, Mamta; Hazra, Purnima; Singh, Satyendra Kumar

    2018-05-01

    Since the beginning of semiconductor fabrication technology evolution, clean and passivated substrate surface is one of the prime requirements for fabrication of Electronic and optoelectronic device fabrication. However, as the scale of silicon circuits and device architectures are continuously decreased from micrometer to nanometer (from VLSI to ULSI technology), the cleaning methods to achieve better wafer surface qualities has raised research interests. The development of controlled and uniform silicon dioxide is the most effective and reliable way to achieve better wafer surface quality for fabrication of electronic devices. On the other hand, in order to meet the requirement of high environment safety/regulatory standards, the innovation of cleaning technology is also in demand. The controlled silicon dioxide layer formed by oxidant de-ionized ozonated water has better uniformity. As the uniformity of the controlled silicon dioxide layer is improved on the substrate, it enhances the performance of the devices. We can increase the thickness of oxide layer, by increasing the ozone time treatment. We reported first time to measurement of thickness of controlled silicon dioxide layer and obtained the uniform layer for same ozone time.

  8. Mass Transfer Coefficients and Bubble Sizes in Oxidative Ladle Refining of Silicon

    OpenAIRE

    Bjørnstad, Erlend Lunnan

    2016-01-01

    The mass transfer of [Al] and [Ca] between three synthetic SiO_{2}-CaO-Al_{2}O_{3} slags, and 8N silicon, has been investigated to find the overall mass transfer coefficient k_{i,t} for the individual species. Samples were kept at 1873K for 5, 10, 20, 30 and 180min before quenching. The metal phase was later analyzed by ICP-MS to view how the concentrations of impurities change with respect to time. This work then compares these results to industrial data gathered from ladles used for oxidati...

  9. Synthesis of microsphere silicon carbide/nanoneedle manganese oxide composites and their electrochemical properties as supercapacitors

    Science.gov (United States)

    Kim, Myeongjin; Yoo, Youngjae; Kim, Jooheon

    2014-11-01

    Synthesis of microsphere silicon carbide/nanoneedle MnO2 (SiC/N-MnO2) composites for use as high-performance materials in supercapacitors is reported herein. The synthesis procedure involves the initial treatment of silicon carbide (SiC) with hydrogen peroxide to obtain oxygen-containing functional groups to provide anchoring sites for connection of SiC and the MnO2 nanoneedles (N-MnO2). MnO2 nanoneedles are subsequently formed on the SiC surface. The morphology and microstructure of the as-prepared composites are characterized via X-ray diffractometry, field-emission scanning electron microscopy, thermogravimetric analysis, and X-ray photoelectron spectroscopy. The characterizations indicate that MnO2 nanoneedles are homogeneously formed on the SiC surface in the composite. The capacitive properties of the as-prepared SiC/N-MnO2 electrodes are evaluated using cyclic voltammetry, galvanostatic charge/discharge testing, and electrochemical impedance spectroscopy in a three-electrode experimental setup using a 1-M Na2SO4 aqueous solution as the electrolyte. The SiC/N-MnO2(5) electrode, for which the MnO2/SiC feed ratio is 5:1, displays a specific capacitance as high as 273.2 F g-1 at 10 mV s-1.

  10. Degradability and Clearance of Silicon, Organosilica, Silsesquioxane, Silica Mixed Oxide, and Mesoporous Silica Nanoparticles

    KAUST Repository

    Croissant, Jonas G.

    2017-01-13

    The biorelated degradability and clearance of siliceous nanomaterials have been questioned worldwide, since they are crucial prerequisites for the successful translation in clinics. Typically, the degradability and biocompatibility of mesoporous silica nanoparticles (MSNs) have been an ongoing discussion in research circles. The reason for such a concern is that approved pharmaceutical products must not accumulate in the human body, to prevent severe and unpredictable side-effects. Here, the biorelated degradability and clearance of silicon and silica nanoparticles (NPs) are comprehensively summarized. The influence of the size, morphology, surface area, pore size, and surface functional groups, to name a few, on the degradability of silicon and silica NPs is described. The noncovalent organic doping of silica and the covalent incorporation of either hydrolytically stable or redox- and enzymatically cleavable silsesquioxanes is then described for organosilica, bridged silsesquioxane (BS), and periodic mesoporous organosilica (PMO) NPs. Inorganically doped silica particles such as calcium-, iron-, manganese-, and zirconium-doped NPs, also have radically different hydrolytic stabilities. To conclude, the degradability and clearance timelines of various siliceous nanomaterials are compared and it is highlighted that researchers can select a specific nanomaterial in this large family according to the targeted applications and the required clearance kinetics.

  11. Novel Size and Surface Oxide Effects in Silicon Nanowires as Lithium Battery Anodes

    KAUST Repository

    McDowell, Matthew T.; Lee, Seok Woo; Ryu, Ill; Wu, Hui; Nix, William D.; Choi, Jang Wook; Cui, Yi

    2011-01-01

    . Finite element modeling shows that the oxide layer can induce compressive hydrostatic stress that could act to limit the extent of lithiation. The understanding developed herein of how volume expansion and extent of lithiation can depend on nanomaterial

  12. Enhanced electrochemical performance of sandwich-structured polyaniline-wrapped silicon oxide/carbon nanotubes for lithium-ion batteries

    Science.gov (United States)

    Liu, Hui; Zou, Yongjin; Huang, Liyan; Yin, Hao; Xi, Chengqiao; Chen, Xin; Shentu, Hongwei; Li, Chao; Zhang, Jingjing; Lv, ChunJu; Fan, Meiqiang

    2018-06-01

    Sandwich-structured carbon nanotubes, silicon oxide, and polyaniline (hereafter denoted as CNTs/SiOx/PANI) were prepared by combining a sol-gel method, magnesiothermic reduction at 250 °C, and chemical oxidative polymerization. The CNTs, SiOx and PANI in the composite was 16 wt%, 51 wt% and 33 wt%, respectively. The CNTs/SiOx/PANI electrodes exhibited excellent cycle and high-rate performance as anodes in Li-ion batteries, including charge/discharge capacities of 1156/1178 mAh g-1 after 60 cycles at 0.2 A g-1 current density and 728/725 mAh g-1 at 8 A g-1 current density. The improvement was due to the synergy between CNTs and PANI. The SiOx scattered on the CNTs core and coated by PANI improved its conductivity and accommodated the volume change during repeated lithiation/delithiation cycles. This simple synthesis provided a scalable route for the large-scale production of CNTs/SiOx/PANI nanostructures, with various applications such as in Li-ion batteries.

  13. Effect of charged deep states in hydrogenated amorphous silicon on the behavior of iron oxides nanoparticles deposited on its surface

    International Nuclear Information System (INIS)

    Gmucova, Katarina; Weis, Martin; Nadazdy, Vojtech; Capek, Ignac; Satka, Alexander; Chitu, Livia; Cirak, Julius; Majkova, Eva

    2008-01-01

    Langmuir-Blodgett technique has been used for the deposition of ordered two-dimensional arrays of iron oxides (Fe 3 O 4 /Fe 2 O 3 ) nanoparticles onto the photovoltaic hydrogenated amorphous silicon (a-Si:H) thin film. Electric field at the a-Si:H/iron oxides nanoparticles interface was directly in the electrochemical cell modified by light soaking and bias voltage (negative or positive) pretreatment resulting in the change of the dominant type of charged deep states in the a-Si:H layer. Induced reversible changes in the nanoparticle redox behavior have been observed. We suggest two possible explanations of the data obtained, both of them are needed to describe measured electrochemical signals. The first one consists in the electrocatalytical effect caused by the defect states (negatively or positively charged) in the a-Si:H layer. The second one consists in the possibility to manipulate the nanoparticle cores in the prepared structure immersed in aqueous solution via the laser irradiation under specific bias voltage. In this case, the nanoparticle cores are assumed to be covered with surface clusters of heterovalent complexes created onto the surface regions with prevailing ferrous or ferric valency. Immersed in the high viscosity surrounding composed of the wet organic nanoparticle envelope these cores are able to perform a field-assisted pivotal motion. The local electric field induced by the deep states in the a-Si:H layer stabilizes their 'orientation ordering' in an energetically favourable position

  14. Fabrication and characterization of a chemically oxidized-nanostructured porous silicon based biosensor implementing orienting protein A.

    Science.gov (United States)

    Naveas, Nelson; Hernandez-Montelongo, Jacobo; Pulido, Ruth; Torres-Costa, Vicente; Villanueva-Guerrero, Raúl; Predestinación García Ruiz, Josefa; Manso-Silván, Miguel

    2014-03-01

    Nanostructured porous silicon (PSi) elicits as a very attractive material for future biosensing systems due to its high surface area, biocompatibility and well-established fabrication methods. In order to engineer its performance as a biosensor transducer platform, the density of immunoglobulins properly immobilized and oriented onto the surface needs to be optimized. In this work we fabricated and characterized a novel biosensing system focusing on the improvement of the biofunctionalization cascade. The system consists on a chemically oxidized PSi platform derivatized with 3-aminopropyltriethoxysilane (APTS) that is coupled to Staphylococcus protein A (SpA). The chemical oxidation has previously demonstrated to enhance the biofunctionalization process and here "by implementing SpA" a molecularly oriented immunosensor is achieved. The biosensor system is characterized in terms of its chemical composition, wettability and optical reflectance. Finally, this system is successfully exploited to develop a biosensor for detecting asymmetric dimethylarginine (ADMA), an endogenous molecule involved in cardiovascular diseases. Therefore, this work is relevant from the point of view of design and optimization of the biomolecular immobilization cascade on PSi surfaces with the added value of contribution to the development of new assays for detecting ADMA with a view on prevention of cardiovascular diseases. Copyright © 2013 Elsevier B.V. All rights reserved.

  15. Graphene oxide-Ag nanoparticles-pyramidal silicon hybrid system for homogeneous, long-term stable and sensitive SERS activity

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Jia [School of Physics and Electronics, Shandong Normal University, Jinan 250014 (China); Xu, Shicai [Shandong Provincial Key Laboratory of Biophysics, College of Physics and Electronic Information, Dezhou University, Dezhou 253023 (China); Liu, Xiaoyun; Li, Zhe; Hu, Litao; Li, Zhen; Chen, Peixi; Ma, Yong [School of Physics and Electronics, Shandong Normal University, Jinan 250014 (China); Jiang, Shouzhen, E-mail: jiang_sz@126.com [School of Physics and Electronics, Shandong Normal University, Jinan 250014 (China); Shandong Provincial Key Laboratory of Optics and Photonic Device, Jinan 250014 (China); Ning, Tingyin [School of Physics and Electronics, Shandong Normal University, Jinan 250014 (China); Shandong Provincial Key Laboratory of Optics and Photonic Device, Jinan 250014 (China)

    2017-02-28

    Highlights: • We directly grown AgNPs on substrate by annealing method in the quartz tube. Compare with spin-coating Ag nanoparticles solution method, we got more uniform distribution of AgNPs and the AgNPs better adsorption on the substrate. • We use a simple and lost-cost method to obtain the pyramidal silicon (PSi). The PSi possessing well-separated pyramid arrays can make contribution to the homogeneity and sensitivity of the substrate. • In our work, graphene oxide (GO) film is uniformly deposited on AgNPs and PSi by using a spin-coating method. The GO films endow the hybrid system a good stability and enhance the homogeneity and sensitivity of the substrate. - Abstract: In our work, few layers graphene oxide (GO) were directly synthesized on Ag nanoparticles (AgNPs) by spin-coating method to fabricate a GO-AgNPs hybrid structure on a pyramidal silicon (PSi) substrate for surface-enhanced Raman scattering (SERS). The GO-AgNPs-PSi substrate showed excellent Raman enhancement effect, the minimum detected concentration for Rhodamine 6G (R6G) can reach 10{sup −12} M, which is one order of magnitude lower than the AgNPs-PSi substrate and two order of magnitude lower than the GO-AgNPs-flat-Si substrate. The linear fit calibration curve with error bars is presented and the value of R{sup 2} of 612 and 773 cm{sup −1} can reach 0.986 and 0.980, respectively. The excellent linear response between the Raman intensity and R6G concentrations prove that the prepared GO-AgNPs-PSi substrates can serve as good SERS substrate for molecule detection. The maximum deviations of SERS intensities from 20 positions of the GO-AgNPs-PSi substrate are less than 8%, revealing the high homogeneity of the SERS substrate. The excellent homogeneity of the enhanced Raman signals can be attributed to well-separated pyramid arrays of PSi, the uniform morphology of AgNPs and multi-functions of GO layer. Besides, the uniform GO film can effectively protect AgNPs from oxidation and endow

  16. Doping profile measurements in silicon using terahertz time domain spectroscopy (THz-TDS) via electrochemical anodic oxidation

    Science.gov (United States)

    Tulsyan, Gaurav

    Doping profiles are engineered to manipulate device properties and to determine electrical performances of microelectronic devices frequently. To support engineering studies afterward, essential information is usually required from physically characterized doping profiles. Secondary Ion Mass Spectrometry (SIMS), Spreading Resistance Profiling (SRP) and Electrochemical Capacitance Voltage (ECV) profiling are standard techniques for now to map profile. SIMS yields a chemical doping profile via ion sputtering process and owns a better resolution, whereas ECV and SRP produce an electrical doping profile detecting free carriers in microelectronic devices. The major difference between electrical and chemical doping profiles is at heavily doped regions greater than 1020 atoms/cm3. At the profile region over the solubility limit, inactive dopants induce a flat plateau and detected by electrical measurements only. Destructive techniques are usually designed as stand-alone systems to study impurities. For an in-situ process control purpose, non-contact methods, such as ellipsometry and non-contact capacitance voltage (CV) techniques are current under development. In this theses work, terahertz time domain spectroscopy (THz-TDS) is utilized to achieve electrical doping profile in both destructive and non-contact manners. In recent years the Terahertz group at Rochester Institute Technology developed several techniques that use terahertz pulses to non-destructively map doping profiles. In this thesis, we study a destructive but potentially higher resolution version of the terahertz based approach to map the profile of activated dopants and augment the non-destructive approaches already developed. The basic idea of the profile mapping approach developed in this MS thesis is to anodize, and thus oxidize to silicon dioxide, thin layers (down to below 10 nm) of the wafer with the doping profile to be mapped. Since the dopants atoms and any free carriers in the silicon oxide thin

  17. Electronic defect levels in continuous wave laser annealed silicon metal oxide semiconductor devices

    Science.gov (United States)

    Cervera, M.; Garcia, B. J.; Martinez, J.; Garrido, J.; Piqueras, J.

    1988-09-01

    The effect of laser treatment on the bulk and interface states of the Si-SiO2 structure has been investigated. The annealing was performed prior to the gate metallization using a continuous wave Ar+ laser. For low laser powers the interface state density seems to decrease slightly in comparison with untreated samples. However, for the highest irradiating laser powers a new bulk level at 0.41 eV above the valence band with concentrations up to 1015 cm-3 arises probably due to the electrical activation of the oxygen diluted in the Czochralski silicon. Later postmetallization annealings reduce the interface state density to values in the 1010 cm-2 eV-1 range but leave the concentration of the 0.41-eV center nearly unchanged.

  18. Diode behavior in ultra-thin low temperature ALD grown zinc-oxide on silicon

    Directory of Open Access Journals (Sweden)

    Nazek El-Atab

    2013-10-01

    Full Text Available A thin-film ZnO(n/Si(p+ heterojunction diode is demonstrated. The thin film ZnO layer is deposited by Atomic Layer Deposition (ALD at different temperatures on a p-type silicon substrate. Atomic force microscopy (AFM AC-in-Air method in addition to conductive AFM (CAFM were used for the characterization of ZnO layer and to measure the current-voltage characteristics. Forward and reverse bias n-p diode behavior with good rectification properties is achieved. The diode with ZnO grown at 80°C exhibited the highest on/off ratio with a turn-on voltage (VON ∼3.5 V. The measured breakdown voltage (VBR and electric field (EBR for this diode are 5.4 V and 3.86 MV/cm, respectively.

  19. Strengthening of oxidation resistant materials for gas turbine applications. [treatment of silicon ceramics for increased flexural strength and impact resistance

    Science.gov (United States)

    Kirchner, H. P.

    1974-01-01

    Silicon nitride and silicon carbide ceramics were treated to form compressive surface layers. On the silicon carbide, quenching and thermal exposure treatments were used, and on the silicon nitride, quenching, carburizing, and a combination of quenching and carburizing were used. In some cases substantial improvements in impact resistance and/or flexural strength were observed. The presence of compressive surface stresses was demonstrated by slotted rod tests.

  20. Vanadium oxide thin films deposited on silicon dioxide buffer layers by magnetron sputtering

    International Nuclear Information System (INIS)

    Chen Sihai; Ma Hong; Wang Shuangbao; Shen Nan; Xiao Jing; Zhou Hao; Zhao Xiaomei; Li Yi; Yi Xinjian

    2006-01-01

    Thin films made by vanadium oxide have been obtained by direct current magnetron sputtering method on SiO 2 buffer layers. A detailed electrical and structural characterization has been performed on the deposited films by four-point probe method and scanning electron microscopy (SEM). At room temperature, the four-point probe measurement result presents the resistance of the film to be 25 kU/sheet. The temperature coefficient of resistance is - 2.0%/K. SEM image indicates that the vanadium oxide exhibits a submicrostructure with lamella size ranging from 60 nm to 300 nm. A 32 x 32-element test microbolometer was fabricated based on the deposited thin film. The infrared response testing showed that the response was 200 mV. The obtained results allow us to conclude that the vanadium oxide thin films on SiO 2 buffer layers is suitable for uncooled focal plane arrays applications

  1. Silicon Qubits

    Energy Technology Data Exchange (ETDEWEB)

    Ladd, Thaddeus D. [HRL Laboratories, LLC, Malibu, CA (United States); Carroll, Malcolm S. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2018-02-28

    Silicon is a promising material candidate for qubits due to the combination of worldwide infrastructure in silicon microelectronics fabrication and the capability to drastically reduce decohering noise channels via chemical purification and isotopic enhancement. However, a variety of challenges in fabrication, control, and measurement leaves unclear the best strategy for fully realizing this material’s future potential. In this article, we survey three basic qubit types: those based on substitutional donors, on metal-oxide-semiconductor (MOS) structures, and on Si/SiGe heterostructures. We also discuss the multiple schema used to define and control Si qubits, which may exploit the manipulation and detection of a single electron charge, the state of a single electron spin, or the collective states of multiple spins. Far from being comprehensive, this article provides a brief orientation to the rapidly evolving field of silicon qubit technology and is intended as an approachable entry point for a researcher new to this field.

  2. Joining elements of silicon carbide

    International Nuclear Information System (INIS)

    Olson, B.A.

    1979-01-01

    A method of joining together at least two silicon carbide elements (e.g.in forming a heat exchanger) is described, comprising subjecting to sufficiently non-oxidizing atmosphere and sufficiently high temperature, material placed in space between the elements. The material consists of silicon carbide particles, carbon and/or a precursor of carbon, and silicon, such that it forms a joint joining together at least two silicon carbide elements. At least one of the elements may contain silicon. (author)

  3. Oxidation and creep behaviour of dense silicon nitride materials with different compositions

    International Nuclear Information System (INIS)

    Ernstberger, U.

    1985-09-01

    The study was intended to yield information on the oxidation and creep behaviour of Si 3 N 4 materials of different composition and microstructure, and produced by different processes. The experiments carried out in a vast temperature and load range showed that the chemical grain boundary composition is the key parameter affecting the materials' high-temperature properties. Significant correlations could be established between oxidation and creep behaviour on the one hand, and between microstructure and the behaviour on the other. (orig./IHOE) [de

  4. Oxidation of clean silicon surfaces studied by four-point probe surface conductance measurements

    DEFF Research Database (Denmark)

    Petersen, Christian Leth; Grey, Francois; Aono, M.

    1997-01-01

    We have investigated how the conductance of Si(100)-(2 x 1) and Si(111)-(7 x 7) surfaces change during exposure to molecular oxygen. A monotonic decrease in conductance is seen as the (100) surfaces oxidizes. In contract to a prior study, we propose that this change is caused by a decrease in sur...

  5. Small Punch Tests at Oxide Scales Surface of Structural Steel and Low Silicon Steel

    Czech Academy of Sciences Publication Activity Database

    Hrabovský, J.; Dobeš, Ferdinand; Horský, J.

    2014-01-01

    Roč. 82, 3-4 (2014), s. 297-310 ISSN 0030-770X Institutional support: RVO:68081723 Keywords : Small punch * Oxide scales * X-ray diffraction * Mechanical properties Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 1.140, year: 2014

  6. Tunable sustained intravitreal drug delivery system for daunorubicin using oxidized porous silicon.

    Science.gov (United States)

    Hou, Huiyuan; Nieto, Alejandra; Ma, Feiyan; Freeman, William R; Sailor, Michael J; Cheng, Lingyun

    2014-03-28

    Daunorubicin (DNR) is an effective inhibitor of an array of proteins involved in neovascularization, including VEGF and PDGF. These growth factors are directly related to retina scar formation in many devastating retinal diseases. Due to the short vitreous half-life and narrow therapeutic window, ocular application of DNR is limited. It has been shown that a porous silicon (pSi) based delivery system can extend DNR vitreous residence from a few days to 3months. In this study we investigated the feasibility of altering the pore size of the silicon particles to regulate the payload release. Modulation of the etching parameters allowed control of the nano-pore size from 15nm to 95nm. In vitro studies showed that degradation of pSiO2 increased with increasing pore size and the degradation of pSiO2 was approximately constant for a given particle type. The degradation of pSiO2 with 43nm pores was significantly greater than the other two particles with smaller pores, judged by observed and normalized mean Si concentration of the dissolution samples (44.2±8.9 vs 25.7±5.6 or 21.2±4.2μg/mL, pporous silicon dioxide with covalent loading of daunorubicin) with large pores (43nm) yielded a significantly higher DNR level than particles with 15 or 26nm pores (13.5±6.9ng/mL vs. 2.3±1.6ng/mL and 1.1±0.9ng/mL, p<0.0001). After two months of in vitro dynamic release, 54% of the pSiO2-CO2H:DNR particles still remained in the dissolution chamber by weight. In vivo drug release study demonstrated that free DNR in the vitreous at post-injection day 14 was 66.52ng/mL for 95nm pore size pSiO2-CO2H:DNR, 10.76ng/mL for 43nm pSiO2-CO2H:DNR, and only 1.05ng/mL for 15nm pSiO2-CO2H:DNR. Pore expansion from 15nm to 95nm led to a 63 fold increase of DNR release (p<0.0001) and a direct correlation between the pore size and the drug levels in the living eye vitreous was confirmed. The present study demonstrates the feasibility of regulating DNR release from pSiO2 covalently loaded with DNR by

  7. Superparamagnetic iron oxide nanoparticle attachment on array of micro test tubes and microbeakers formed on p-type silicon substrate for biosensor applications

    Directory of Open Access Journals (Sweden)

    Raja Sufi

    2011-01-01

    Full Text Available Abstract A uniformly distributed array of micro test tubes and microbeakers is formed on a p-type silicon substrate with tunable cross-section and distance of separation by anodic etching of the silicon wafer in N, N-dimethylformamide and hydrofluoric acid, which essentially leads to the formation of macroporous silicon templates. A reasonable control over the dimensions of the structures could be achieved by tailoring the formation parameters, primarily the wafer resistivity. For a micro test tube, the cross-section (i.e., the pore size as well as the distance of separation between two adjacent test tubes (i.e., inter-pore distance is typically approximately 1 μm, whereas, for a microbeaker the pore size exceeds 1.5 μm and the inter-pore distance could be less than 100 nm. We successfully synthesized superparamagnetic iron oxide nanoparticles (SPIONs, with average particle size approximately 20 nm and attached them on the porous silicon chip surface as well as on the pore walls. Such SPION-coated arrays of micro test tubes and microbeakers are potential candidates for biosensors because of the biocompatibility of both silicon and SPIONs. As acquisition of data via microarray is an essential attribute of high throughput bio-sensing, the proposed nanostructured array may be a promising step in this direction.

  8. Electrical and Optical Characterization of Sputtered Silicon Dioxide, Indium Tin Oxide, and Silicon Dioxide/Indium Tin Oxide Antireflection Coating on Single-Junction GaAs Solar Cells

    Directory of Open Access Journals (Sweden)

    Wen-Jeng Ho

    2017-06-01

    Full Text Available This study characterized the electrical and optical properties of single-junction GaAs solar cells coated with antireflective layers of silicon dioxide (SiO2, indium tin oxide (ITO, and a hybrid layer of SiO2/ITO applied using Radio frequency (RF sputtering. The conductivity and transparency of the ITO film were characterized prior to application on GaAs cells. Reverse saturation-current and ideality factor were used to evaluate the passivation performance of the various coatings on GaAs solar cells. Optical reflectance and external quantum efficiency response were used to evaluate the antireflective performance of the coatings. Photovoltaic current-voltage measurements were used to confirm the efficiency enhancement obtained by the presence of the anti-reflective coatings. The conversion efficiency of the GaAs cells with an ITO antireflective coating (23.52% exceeded that of cells with a SiO2 antireflective coating (21.92%. Due to lower series resistance and higher short-circuit current-density, the carrier collection of the GaAs cell with ITO coating exceeded that of the cell with a SiO2/ITO coating.

  9. The influence of silicon as a possible reactive element in the protection against high temperature oxidation of AISI 304 stainless steel

    International Nuclear Information System (INIS)

    Otero, E.; Perez, F.J.; Hierro, M.P.; Gomez, C.; Pedraza, F.; Segovia, J. L. de; Roman, E.

    1998-01-01

    The influence of silicon incorporated into the alloy by means of ion implantation of 1 x 10''15 ions/cm''2 at 150 keV on the protective scale development based upon Cr 1 ,3 Fe 0 ,7O 3 and manganese-enriched spinels, Mn 1 ,5Cr 1 .5O 4 after oxidation of an austenitic AISI 304 stainless steel at 1.173 K and atmospheric pressure of air for 144 h has been studied. The presence of small quantities of silicon at the outermost layers of the alloy promotes transport of chromium during the early stages of oxidation. Further, ion implantation seems to play a beneficial role against decarburization of the alloy. (Author) 8 refs

  10. Conformity and structure of titanium oxide films grown by atomic layer deposition on silicon substrates

    Energy Technology Data Exchange (ETDEWEB)

    Jogi, Indrek [University of Tartu, Institute of Experimental Physics and Technology, Taehe 4, 51010, Tartu (Estonia)], E-mail: indrek.jogi@ut.ee; Paers, Martti; Aarik, Jaan; Aidla, Aleks [University of Tartu, Institute of Physics, Riia 142, 51014, Tartu (Estonia); Laan, Matti [University of Tartu, Institute of Experimental Physics and Technology, Taehe 4, 51010, Tartu (Estonia); Sundqvist, Jonas; Oberbeck, Lars; Heitmann, Johannes [Qimonda Dresden GmbH and Co. OHG, Koenigsbruecker Strasse 180, 01099, Dresden (Germany); Kukli, Kaupo [University of Tartu, Institute of Experimental Physics and Technology, Taehe 4, 51010, Tartu (Estonia)

    2008-06-02

    Conformity and phase structure of atomic layer deposited TiO{sub 2} thin films grown on silicon substrates were studied. The films were grown using TiCl{sub 4} and Ti(OC{sub 2}H{sub 5}){sub 4} as titanium precursors in the temperature range from 125 to 500 {sup o}C. In all cases perfect conformal growth was achieved on patterned substrates with elliptical holes of 7.5 {mu}m depth and aspect ratio of about 1:40. Conformal growth was achieved with process parameters similar to those optimized for the growth on planar wafers. The dominant crystalline phase in the as-grown films was anatase, with some contribution from rutile at relatively higher temperatures. Annealing in the oxygen ambient resulted in (re)crystallization whereas the effect of annealing depended markedly on the precursors used in the deposition process. Compared to films grown from TiCl{sub 4}, the films grown from Ti(OC{sub 2}H{sub 5}){sub 4} were transformed into rutile in somewhat greater extent, whereas in terms of step coverage the films grown from Ti(OC{sub 2}H{sub 5}){sub 4} remained somewhat inferior compared to the films grown from TiCl{sub 4}.

  11. Sol-gel synthesis of magnesium oxide-silicon dioxide glass compositions

    Science.gov (United States)

    Bansal, Narottam P.

    1988-01-01

    MgO-SiO2 glasses containing up to 15 mol pct MgO, which could not have been prepared by the conventional glass melting method due to the presence of stable liquid-liquid immiscibility, were synthesized by the sol-gel technique. Clear and transparent gels were obtained from the hydrolysis and polycondensation of silicon tetraethoxide (TEOS) and magnesium nitrate hexahydrate when the water/TEOS mole ratio was four or more. The gelling time decreased with increase in magnesium content, water/TEOS ratio, and reaction temperature. Magnesium nitrate hexahydrate crystallized out of the gels containing 15 and 20 mol pct MgO on slow drying. This problem was partially alleviated by drying the gels quickly at higher temperatures. Monolithic gel samples were prepared using glycerol as the drying control additive. The gels were subjected to various thermal treatments and characterized by several methods. No organic groups could be detected in the glasses after heat treatments to approx. 800 C, but trace amounts of hydroxyl groups were still present. No crystalline phase was found from X-ray diffraction in the gel samples to approx. 890 C. At higher temperatures, alpha quartz precipitated out as the crystalline phase in gels containing up to 10 mol pct MgO. The overall activation energy for gel formation in 10MgO-90SiO2 (mol pct) system for water/TEOS mole ratio of 7.5 was calculated to be 58.7 kJ/mol.

  12. Effect of salinity and silicon application on oxidative damage of sorghum [sorghum bicolor (L.) moench.

    International Nuclear Information System (INIS)

    Kafi, M.; Nabati, J.; Masoumi, A.; Mehrgerdi, M.Z.

    2011-01-01

    Application of silicon (Si) to soil is considered as an alternative approach to alleviate salinity stress in crop plants. Therefore, a field experiment was conducted to investigate the effects of Si application [control (without Si), 1.44 and 1.92 g.kg /sup -1/ soil on membrane stability index (MSI), relative water content (RWC), leaf proline, soluble sugars, antioxidant activity, total phenols and dry matter accumulation of two sorghum (Sorghum bicolor) cultivars under three levels of salinity of irrigation water (5.2, 10.5 and 23.1 dS m/sup -1/ . The results showed that leaf proline content, activities of ascorbate peroxidase (APX) and glutathione reductase (GR), Na/sup +/ concentration significantly increased only at high level of salinity, while, RWC Si caused an and dry matter accumulation were significantly decreased at all salinity levels. Soil application of 1.44 g.kg/sup -1/ increase in the activities of APX, catalase (CAT), superoxide dismutase (SOD), peroxidase (PRO), glutathione reductase soil Si caused an increase in membrane stabilityindex, (GR), total antioxidant and total phenol contents and 1.92 g.kg/sup -1/ soluble sugar and total phenol contents, CAT, SOD and total antioxidant activity. Soluble sugars, total phenols, SOD and total antioxidant activity and dry matter accumulation in cv. Omidbakhsh were higher than those in cv. Sepideh. In conclusion, alleviation of salinity stress by exogenous application of Si was found to be associated partly with enhanced antioxidant activity. (author)

  13. Influence of Nano sized Silicon Oxide on the Luminescent Properties of Zn O Nanoparticles

    International Nuclear Information System (INIS)

    Shvalagin, V.; Grodziuk, G.; Kurmach, M.; Granchak, V.; Sarapulova, O.; Sherstiuk, V.

    2016-01-01

    For practical use of nano sized zinc oxide as the phosphor its luminescence quantum yields should be maximized. The aim of this work was to enhance luminescent properties of Zn O nanoparticles and obtain high-luminescent Zn O/SiO 2 composites using simpler approaches to colloidal synthesis. The luminescence intensity of zinc oxide nanoparticles was increased about 3 times by addition of silica nano crystals to the source solutions during the synthesis of Zn O nanoparticles. Then the quantum yield of luminescence of the obtained Zn O/SiO 2 composites is more than 30%. Such an impact of silica is suggested to be caused by the distribution of Zn O nano crystals on the surface of silica, which reduces the probability of separation of photo generated charges between the zinc oxide nanoparticles of different sizes, and as a consequence, there is a significant increase of the luminescence intensity of Zn O nanoparticles. This way of increasing nano-Zn O luminescence intensity facilitates its use in a variety of devices, including optical ultraviolet and visible screens, luminescent markers, antibacterial coatings, luminescent solar concentrators, luminescent inks for security printing, and food packaging with abilities of informing consumers about the quality and safety of the packaged product.

  14. Influence of Nanosized Silicon Oxide on the Luminescent Properties of ZnO Nanoparticles

    Directory of Open Access Journals (Sweden)

    Vitaliy Shvalagin

    2016-01-01

    Full Text Available For practical use of nanosized zinc oxide as the phosphor its luminescence quantum yields should be maximized. The aim of this work was to enhance luminescent properties of ZnO nanoparticles and obtain high-luminescent ZnO/SiO2 composites using simpler approaches to colloidal synthesis. The luminescence intensity of zinc oxide nanoparticles was increased about 3 times by addition of silica nanocrystals to the source solutions during the synthesis of ZnO nanoparticles. Then the quantum yield of luminescence of the obtained ZnO/SiO2 composites is more than 30%. Such an impact of silica is suggested to be caused by the distribution of ZnO nanocrystals on the surface of silica, which reduces the probability of separation of photogenerated charges between the zinc oxide nanoparticles of different sizes, and as a consequence, there is a significant increase of the luminescence intensity of ZnO nanoparticles. This way of increasing nano-ZnO luminescence intensity facilitates its use in a variety of devices, including optical ultraviolet and visible screens, luminescent markers, antibacterial coatings, luminescent solar concentrators, luminescent inks for security printing, and food packaging with abilities of informing consumers about the quality and safety of the packaged product.

  15. Determining the thickness of aliphatic alcohol monolayers covalently attached to silicon oxide surfaces using angle-resolved X-ray photoelectron spectroscopy

    Science.gov (United States)

    Lee, Austin W. H.; Kim, Dongho; Gates, Byron D.

    2018-04-01

    The thickness of alcohol based monolayers on silicon oxide surfaces were investigated using angle-resolved X-ray photoelectron spectroscopy (ARXPS). Advantages of using alcohols as building blocks for the formation of monolayers include their widespread availability, ease of handling, and stability against side reactions. Recent progress in microwave assisted reactions demonstrated the ease of forming uniform monolayers with alcohol based reagents. The studies shown herein provide a detailed investigation of the thickness of monolayers prepared from a series of aliphatic alcohols of different chain lengths. Monolayers of 1-butanol, 1-hexanol, 1-octanol, 1-decanol, and 1-dodecanol were each successfully formed through microwave assisted reactions and characterized by ARXPS techniques. The thickness of these monolayers consistently increased by ∼1.0 Å for every additional methylene (CH2) within the hydrocarbon chain of the reagents. Tilt angles of the molecules covalently attached to silicon oxide surfaces were estimated to be ∼35° for each type of reagent. These results were consistent with the observations reported for thiol based or silane based monolayers on either gold or silicon oxide surfaces, respectively. The results of this study also suggest that the alcohol based monolayers are uniform at a molecular level.

  16. Graphene oxide-Ag nanoparticles-pyramidal silicon hybrid system for homogeneous, long-term stable and sensitive SERS activity

    Science.gov (United States)

    Guo, Jia; Xu, Shicai; Liu, Xiaoyun; Li, Zhe; Hu, Litao; Li, Zhen; Chen, Peixi; Ma, Yong; Jiang, Shouzhen; Ning, Tingyin

    2017-02-01

    In our work, few layers graphene oxide (GO) were directly synthesized on Ag nanoparticles (AgNPs) by spin-coating method to fabricate a GO-AgNPs hybrid structure on a pyramidal silicon (PSi) substrate for surface-enhanced Raman scattering (SERS). The GO-AgNPs-PSi substrate showed excellent Raman enhancement effect, the minimum detected concentration for Rhodamine 6G (R6G) can reach 10-12 M, which is one order of magnitude lower than the AgNPs-PSi substrate and two order of magnitude lower than the GO-AgNPs-flat-Si substrate. The linear fit calibration curve with error bars is presented and the value of R2 of 612 and 773 cm-1 can reach 0.986 and 0.980, respectively. The excellent linear response between the Raman intensity and R6G concentrations prove that the prepared GO-AgNPs-PSi substrates can serve as good SERS substrate for molecule detection. The maximum deviations of SERS intensities from 20 positions of the GO-AgNPs-PSi substrate are less than 8%, revealing the high homogeneity of the SERS substrate. The excellent homogeneity of the enhanced Raman signals can be attributed to well-separated pyramid arrays of PSi, the uniform morphology of AgNPs and multi-functions of GO layer. Besides, the uniform GO film can effectively protect AgNPs from oxidation and endow the hybrid system a good stability and long lifetime. This GO-AgNPs-PSi substrate may provide a new way toward practical applications for the ultrasensitive and label-free SERS detection in areas of medicine, food safety and biotechnology.

  17. Enhanced NO2 sensing characteristics of Au modified porous silicon/thorn-sphere-like tungsten oxide composites

    Science.gov (United States)

    Yuan, Lin; Hu, Ming; Wei, Yulong; Ma, Wenfeng

    2016-12-01

    The thorn-sphere-like tungsten oxide (WO3) made up by 1D nanorods has been successfully synthesized through hydrothermal method on the Au-modified porous silicon (PS) substrates with seed-layer induction. By using XRD, EDS, FESEM and TEM techniques, we tested and verified that the crystal structure and morphology evolution of WO3 hierarchical nanostructure on the Au-modified PS strongly depend on the Au-sputtering time and hydrothermal reaction time. In addition, by comparing the NO2-sensing properties of the prepared products, we found that the 10 s-Au decorated PS/WO3-3 h (sputtering Au for 10 s and hydrothermal reaction for 3 h) composites sensor behaving as a typical p-type semiconductor and operating at room temperature (RT) exhibits high sensitivity and response characteristics even to ppb-level NO2, which makes this kind of sensor a competitive candidate for NO2-sensing applications. Moreover, the enhanced response may not only due to the high specific surface area but the Au nanoparticles acting as promoters for the spillover effect and forming metal-semiconductor heterojunctions with the PS and WO3. The transmission of electrons and holes in the heterogeneous interface generated among PS, WO3 and Au is proposed to illustrate the p-type response mechanism.

  18. Luminescent passive-oxidized silicon quantum dots as biological staining labels and their cytotoxicity effects at high concentration

    International Nuclear Information System (INIS)

    Fujioka, Kouki; Manabe, Noriyoshi; Hanada, Sanshiro; Hoshino, Akiyoshi; Yamamoto, Kenji; Hiruoka, Masaki; Sato, Keisuke; Hirakuri, Kenji; Miyasaka, Ryosuke; Tilley, Richard D; Manome, Yoshinobu

    2008-01-01

    Semiconductor quantum dots (QDs) hold some advantages over conventional organic fluorescent dyes. Due to these advantages, they are becoming increasingly popular in the field of bioimaging. However, recent work suggests that cadmium based QDs affect cellular activity. As a substitute for cadmium based QDs, we have developed photoluminescent stable silicon quantum dots (Si-QDs) with a passive-oxidation technique. Si-QDs (size: 6.5 ± 1.5 nm) emit green light, and they have been used as biological labels for living cell imaging. In order to determine the minimum concentration for cytotoxicity, we investigated the response of HeLa cells. We have shown that the toxicity of Si-QDs was not observed at 112 μg ml -1 and that Si-QDs were less toxic than CdSe-QDs at high concentration in mitochondrial assays and with lactate dehydrogenase (LDH) assays. Especially under UV exposure, Si-QDs were more than ten times safer than CdSe-QDs. We suggest that one mechanism for the cytotoxicity is that Si-QDs can generate oxygen radicals and these radicals are associated with membrane damages. This work has demonstrated the suitability of Si-QDs for bioimaging in lower concentration, and their cytotoxicity and one toxicity mechanism at high concentration

  19. Oxidation effects on the mechanical properties of SiC fiber-reinforced reaction-bonded silicon nitride matrix composites

    Science.gov (United States)

    Bhatt, Ramakrishna T.

    1989-01-01

    The room temperature mechanical properties of SiC fiber reinforced reaction bonded silicon nitride composites were measured after 100 hrs exposure at temperatures to 1400 C in nitrogen and oxygen environments. The composites consisted of approx. 30 vol percent uniaxially aligned 142 micron diameter SiC fibers in a reaction bonded Si3N4 matrix. The results indicate that composites heat treated in a nitrogen environment at temperatures to 1400 C showed deformation and fracture behavior equivalent to that of the as-fabricated composites. Also, the composites heat treated in an oxidizing environment beyond 400 C yielded significantly lower tensile strength values. Specifically in the temperature range from 600 to 1000 C, composites retained approx. 40 percent of their as-fabricated strength, and those heat treated in the temperatures from 1200 to 1400 C retained 70 percent. Nonetheless, for all oxygen heat treatment conditions, composite specimens displayed strain capability beyond the matrix fracture stress; a typical behavior of a tough composite.

  20. Microchannel-connected SU-8 honeycombs by single-step projection photolithography for positioning cells on silicon oxide nanopillar arrays

    International Nuclear Information System (INIS)

    Larramendy, Florian; Paul, Oliver; Blatche, Marie Charline; Mazenq, Laurent; Laborde, Adrian; Temple-Boyer, Pierre

    2015-01-01

    We report on the fabrication, functionalization and testing of SU-8 microstructures for cell culture and positioning over large areas. The microstructure consists of a honeycomb arrangement of cell containers interconnected by microchannels and centered on nanopillar arrays designed for promoting cell positioning. The containers have been dimensioned to trap single cells and, with a height of 50 µm, prevent cells from escaping. The structures are fabricated using a single ultraviolet photolithography exposure with focus depth in the lower part of the SU-8 resist. With optimized process parameters, microchannels of various aspect ratios are thus produced. The cell containers and microchannels serve for the organization of axonal growth between neurons. The roughly 2 µm-high and 500 nm-wide nanopillars are made of silicon oxide structured by deep reactive ion etching. In future work, beyond their cell positioning purpose, the nanopillars could be functionalized as sensors. The proof of concept of the novel microstructure for organized cell culture is given by the successful growth of interconnected PC12 cells. Promoted by the honeycomb geometry, a dense network of interconnections between the cells has formed and the intended intimate contact of cells with the nanopillar arrays was observed by scanning electron microscopy. This proves the potential of these new devices as tools for the controlled cell growth in an interconnected container system with well-defined 3D geometry. (paper)

  1. Optimizing Thermoelectric Properties of In Situ Plasma-Spray-Synthesized Sub-stoichiometric TiO2-x Deposits

    Science.gov (United States)

    Lee, Hwasoo; Seshadri, Ramachandran Chidambaram; Pala, Zdenek; Sampath, Sanjay

    2018-06-01

    In this article, an attempt has been made to relate the thermoelectric properties of thermal spray deposits of sub-stoichiometric titania to process-induced phase and microstructural variances. The TiO2-x deposits were formed through the in situ reaction of the TiO1.9 or TiO1.7 feedstock within the high-temperature plasma flame and manipulated via varying the amounts of hydrogen fed into in the thermal plasma. Changes in the flow rates of H2 in the plasma plume greatly affected the in-flight particle behavior and composition of the deposits. For reference, a high-velocity oxy-fuel spray torch was also used to deposit the two varieties of feedstocks. Refinements to the representation of the in-flight particle characteristics derived via single particle and ensemble diagnostic methods are proposed using the group parameters (melting index and kinetic energy). The results show that depending on the value of the melting index, there is an inverse proportional relationship between electrical conductivity and Seebeck coefficient, whereas thermal conductivity has a directly proportional relationship with the electrical conductivity. Retention of the original phase and reduced decomposition is beneficial to retain the high Seebeck coefficient or the high electrical conductivity in the TiO2 system.

  2. Low temperature oxidation of niobium alloy with silicon-aluminium coating

    International Nuclear Information System (INIS)

    Lazarev, Eh.M.; Sapozhnikova, L.V.; Shabanova, M.E.; Pod'yachev, V.N.; Kornilova, Z.I.

    1987-01-01

    Using the gravimetry methods heat resistance of niobium-titanium-aluminium alloy in the air and at 700 deg C in the initial state and when it is protected by silicide-aluminium coatings (with variable content of aluminium) is investigated. Using X-ray diffraction and micro X-ray diffraction analyses, mechanisms of the alloy oxidation and the coating protective effect are studied. The role of aluminium in the formation of coatings is analyzed and according to bend tests the plasticity of the coatings is evaluated

  3. New applications of meso-structured silicon oxides in bio-remediation

    International Nuclear Information System (INIS)

    Galarneau, A.

    2006-01-01

    In this work, has been developed a new enzymes encapsulation method by sol-gel synthesis, using natural phospho-lipids as surfactants and amines as co-surfactants to control both the polarity and porosity. The catalytic performances are superior to the classical and commercial sol-gel encapsulations because of the addition of the porosity control. This new synthesis method, easy to carry out, provides new very efficient bio-catalysts, for instance for the oxidation of polluting molecules contained in water or in organic media. (O.M.)

  4. Chiral lewis Acid catalysis in nitrile oxide cycloadditions.

    Science.gov (United States)

    Sibi, Mukund P; Itoh, Kennosuke; Jasperse, Craig P

    2004-05-05

    We describe examples of highly regio- and enantioselective nitrile oxide cycloadditions to unsaturated alkenes using substoichiometric amounts of a chiral Lewis acid. Pyrazolidinones proved to be effective achiral templates in the cycloadditions providing C-adducts typically in >30:1 selectivity and 80-99% ee. To avoid potential problems involving coordination of the Lewis acid by amine bases, we have devised a novel method for the generation of unstable nitrile oxides from hydroximinoyl chlorides using Amberlyst 21 as the base.

  5. Swift heavy ion induced de wetting of metal oxide thin films on silicon

    International Nuclear Information System (INIS)

    Bolse, T.; Paulus, H.; Bolse, W.

    2006-01-01

    We have observed that thin oxide coatings (NiO, Fe 2 O 3 ) tend to dewet their Si substrate when being bombarded with swift heavy ions (350-600 MeV Au ions) even though the irradiation was carried out about 80 K and hence, the films never reached their melting point. Scanning electron and atomic force microscopy reveal a surprising similarity of the dewetting morphologies with those observed for molten polymer films on Si, which have recently been reported by others [S. Herminghaus, K. Jakobs, K. Mecke, J. Bischof, A. Fery, M. Ibn-Elhaj, S. Schlagowsky, Science 282 (1998) 916; R. Seemann, S. Herminghaus, K. Jacobs, J. Phys.: Condens. Matter 13 (2001) 4925]. Like in that cases also here heterogeneous and homogeneous hole nucleation could be identified. Heterogeneous nucleation is less pronounced in Fe 2 O 3 /Si than in NiO/Si. The occurrence of spinodal-like dewetting cannot be detected unambiguously. The dewetting kinetics were determined by means of Rutherford backscattering spectroscopy and found to slightly differ for the two compounds. The dewetting kinetics as well as the final dewetting pattern strongly depend on the initial film thicknesses. No dewetting occurs for film thicknesses above about 150 nm, while for very small thicknesses below about 40 nm the film decays into nm-sized spherical droplets. At intermediate film thicknesses percolated networks of small oxide bridges are formed

  6. Formation and electrical characteristics of silicon dioxide layers by use of nitric acid oxidation method

    International Nuclear Information System (INIS)

    Imal, S.; Takahashi, M.; Matsuba, K.; Asuha; Ishikawa, Y.; Kobayashi, Hikaru

    2005-01-01

    SiO 2 /Si structure can be formed at low temperatures by use of nitric acid (HNO 3 ) oxidation of Si (NAOS) method. When Si wafers are immersed in ∼ 40 wt% HNO 3 solutions at 108 deg C, ∼ 1 nm SiO 2 layers are formed. The subsequent immersion in 68 wt% HNO 3 (i.e., azeotropic mixture of HNO 3 with water) at 121 deg C increases the SiO 2 thickness. The 3,5 nm-thick SiO 2 layers produced by this two-step NAOS method possess a considerably low leakage current density (e.g. 1 x 10 2 A/cmi 2 at the forward gate bias, V G , of 1.5 V), in spite of the low temperature oxidation, and further decreased (e.g., 8 x 10 4 A/cm 2 at V G = 1.5 V) by post-metallization annealing at 250 deg C in hydrogen atmosphere. In order to increase the SiO 2 thickness, a bias voltage is applied during the NAOS method. When 10 V is applied to Si with respect to a Pt counter electrode both immersed in 1 M HNO 3 solutions at 25 deg C, SiO 2 layers with 8 nm thickness can be formed for 1 h(Authors)

  7. Non-metallic dopant modulation of conductivity in substoichiometric tantalum pentoxide: A first-principles study

    Science.gov (United States)

    Bondi, Robert J.; Fox, Brian P.; Marinella, Matthew J.

    2017-06-01

    We apply density-functional theory calculations to predict dopant modulation of electrical conductivity (σo) for seven dopants (C, Si, Ge, H, F, N, and B) sampled at 18 quantum molecular dynamics configurations of five independent insertion sites into two (high/low) baseline references of σo in amorphous Ta2O5, where each reference contains a single, neutral O vacancy center (VO0). From this statistical population (n = 1260), we analyze defect levels, physical structure, and valence charge distributions to characterize nanoscale modification of the atomistic structure in local dopant neighborhoods. C is the most effective dopant at lowering Ta2Ox σo, while also exhibiting an amphoteric doping behavior by either donating or accepting charge depending on the host oxide matrix. Both B and F robustly increase Ta2Ox σo, although F does so through elimination of Ta high charge outliers, while B insertion conversely creates high charge O outliers through favorable BO3 group formation, especially in the low σo reference. While N applications to dope and passivate oxides are prevalent, we found that N exacerbates the stochasticity of σo we sought to mitigate; sensitivity to the N insertion site and some propensity to form N-O bond chemistries appear responsible. We use direct first-principles predictions of σo to explore feasible Ta2O5 dopants to engineer improved oxides with lower variance and greater repeatability to advance the manufacturability of resistive memory technologies.

  8. Positive and negative gain exceeding unity magnitude in silicon quantum well metal-oxide-semiconductor transistors

    Science.gov (United States)

    Hu, Gangyi; Wijesinghe, Udumbara; Naquin, Clint; Maggio, Ken; Edwards, H. L.; Lee, Mark

    2017-10-01

    Intrinsic gain (AV) measurements on Si quantum well (QW) n-channel metal-oxide-semiconductor (NMOS) transistors show that these devices can have |AV| > 1 in quantum transport negative transconductance (NTC) operation at room temperature. QW NMOS devices were fabricated using an industrial 45 nm technology node process incorporating ion implanted potential barriers to define a lateral QW in the conduction channel under the gate. While NTC at room temperature arising from transport through gate-controlled QW bound states has been previously established, it was unknown whether the quantum NTC mechanism could support gain magnitude exceeding unity. Bias conditions were found giving both positive and negative AV with |AV| > 1 at room temperature. This result means that QW NMOS devices could be useful in amplifier and oscillator applications.

  9. Growth of aluminum oxide on silicon carbide with an atomically sharp interface

    DEFF Research Database (Denmark)

    Silva, Ana Gomes; Pedersen, Kjeld; Li, Zheshen

    2017-01-01

    this system up to around 600 °C (all in ultrahigh vacuum). This converts all the SiO2 into a uniform layer of Al2O3 with an atomically sharp interface between the Al2O3 and the Si surface. In the present work, the same procedures are applied to form Al2O3 on a SiC film grown on top of Si (111). The results...... indicate that a similar process, resulting in a uniform layer of 1-2 nm of Al2O3 with an atomically sharp Al2O3/SiC interface, also works in this case.......The development of SiC wafers with properties suitable for electronic device fabrication is now well established commercially. A critical issue for developing metal-oxide-semiconductor field effect transistor devices of SiC is the choice of dielectric materials for surface passivation...

  10. Radiation resistant passivation of silicon solar cells

    International Nuclear Information System (INIS)

    Swanson, R.M.; Gan, J.Y.; Gruenbaum, P.E.

    1991-01-01

    This patent describes a silicon solar cell having improved stability when exposed to concentrated solar radiation. It comprises a body of silicon material having a major surface for receiving radiation, a plurality of p and n conductivity regions in the body for collecting electrons and holes created by impinging radiation, and a passivation layer on the major surface including a first layer of silicon oxide in contact with the body and a polycrystalline silicon layer on the first layer of silicon oxide

  11. Evolution of a Native Oxide Layer at the a-Si:H/c-Si Interface and Its Influence on a Silicon Heterojunction Solar Cell.

    Science.gov (United States)

    Liu, Wenzhu; Meng, Fanying; Zhang, Xiaoyu; Liu, Zhengxin

    2015-12-09

    The interface microstructure of a silicon heterojunction (SHJ) solar cell was investigated. We found an ultrathin native oxide layer (NOL) with a thickness of several angstroms was formed on the crystalline silicon (c-Si) surface in a very short time (∼30 s) after being etched by HF solution. Although the NOL had a loose structure with defects that are detrimental for surface passivation, it acted as a barrier to restrain the epitaxial growth of hydrogenated amorphous silicon (a-Si:H) during the plasma-enhanced chemical vapor deposition (PECVD). The microstructure change of the NOL during the PECVD deposition of a-Si:H layers with different conditions and under different H2 plasma treatments were systemically investigated in detail. When a brief H2 plasma was applied to treat the a-Si:H layer after the PECVD deposition, interstitial oxygen and small-size SiO2 precipitates were transformed to hydrogenated amorphous silicon suboxide alloy (a-SiO(x):H, x ∼ 1.5). In the meantime, the interface defect density was reduced by about 50%, and the parameters of the SHJ solar cell were improved due to the post H2 plasma treatment.

  12. Very high-cycle fatigue failure in micron-scale polycrystalline silicon films : Effects of environment and surface oxide thickness

    NARCIS (Netherlands)

    Alsem, D. H.; Boyce, B. L.; Stach, E. A.; De Hosson, J. Th. M.; Ritchie, R. O.

    2007-01-01

    Fatigue failure in micron-scale polycrystalline silicon structural films, a phenomenon that is not observed in bulk silicon, can severely impact the durability and reliability of microelectromechanical system devices. Despite several studies on the very high-cycle fatigue behavior of these films (up

  13. Dewetting of nickel oxide-films on silicon under swift heavy ion irradiation

    International Nuclear Information System (INIS)

    Bolse, Thunu; Elsanousi, Ammar; Paulus, Hartmut; Bolse, Wolfgang

    2006-01-01

    Dewetting, occurring when a thin film on a non-wettable substrate turns into its liquid state, has gained strong interest during the last decade, since it results in nano-scale, large-area covering pattern formation. Recently we found that swift heavy ion (SHI) irradiation of thin NiO films on Si substrates at 80 K results in similar dewetting pattern, although in this case the coating has never reached its melting point. Careful inspection of the SEM images clearly revealed that the same nucleation mechanisms as observed for molten polymer films on Si (heterogeneous and homogeneous nucleation) were active. AFM shows that the circular holes formed in the early stages of the dewetting process exhibit a high and asymmetric rim-structure. RBS analysis was used to measure the coverage of the surface by the oxide films and revealed that the holes grow at constant velocity. This, and the shape of the rims, indicate that the material removed from the substrate surface piles up by plastic deformation, which points at a balance of the capillary driving forces and the hindered material dissipation

  14. A Novel Fully Depleted Air AlN Silicon-on-Insulator Metal-Oxide-Semiconductor Field Effect Transistor

    International Nuclear Information System (INIS)

    Yuan, Yang; Yong, Gao; Peng-Liang, Gong

    2008-01-01

    A novel fully depleted air AlN silicon-on-insulator (SOI) metal-oxide-semiconductor field effect transistor (MOS-FET) is presented, which can eliminate the self-heating effect and solve the problem that the off-state current of SOI MOSFETs increases and the threshold voltage characteristics become worse when employing a high thermal conductivity material as a buried layer. The simulation results reveal that the lattice temperature in normal SOI devices is 75 K higher than the atmosphere temperature, while the lattice temperature is just 4K higher than the atmosphere temperature resulting in less severe self-heating effect in air AlN SOI MOSFETs and AlN SOI MOSFETs. The on-state current of air AlN SOI MOSFETs is similar to the AlN SOI structure, and improves 12.3% more than that of normal SOI MOSFETs. The off-state current of AlN SOI is 6.7 times of normal SOI MOSFETs, while the counterpart of air AlN SOI MOSFETs is lower than that of SOI MOSFETs by two orders of magnitude. The threshold voltage change of air AlN SOI MOSFETs with different drain voltage is much less than that of AlN SOI devices, when the drain voltage is biased at 0.8 V, this difference is 28mV, so the threshold voltage change induced by employing high thermal conductivity material is cured. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  15. Indium tin oxide thin-films prepared by vapor phase pyrolysis for efficient silicon based solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Simashkevich, Alexei, E-mail: alexeisimashkevich@hotmail.com [Institute of Applied Physics, 5 Academiei str., Chisinau, MD-2028, Republic of Moldova (Moldova, Republic of); Serban, Dormidont; Bruc, Leonid; Curmei, Nicolai [Institute of Applied Physics, 5 Academiei str., Chisinau, MD-2028, Republic of Moldova (Moldova, Republic of); Hinrichs, Volker [Institut für Heterogene Materialsysteme, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Lise-Meitner Campus, Hahn-Meitner-Platz 1, 14109 Berlin (Germany); Rusu, Marin [Institute of Applied Physics, 5 Academiei str., Chisinau, MD-2028, Republic of Moldova (Moldova, Republic of); Institut für Heterogene Materialsysteme, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Lise-Meitner Campus, Hahn-Meitner-Platz 1, 14109 Berlin (Germany)

    2016-07-01

    The vapor phase pyrolysis deposition method was developed for the preparation of indium tin oxide (ITO) thin films with thicknesses ranging between 300 and 400 nm with the sheet resistance of 10–15 Ω/sq. and the transparency in the visible region of the spectrum over 80%. The layers were deposited on the (100) surface of the n-type silicon wafers with the charge carriers concentration of ~ 10{sup 15} cm{sup −3}. The morphology of the ITO layers deposited on Si wafers with different surface morphologies, e.g., smooth (polished), rough (irregularly structured) and textured (by inversed pyramids) was investigated. The as-deposited ITO thin films consist of crystalline columns with the height of 300–400 nm and the width of 50–100 nm. Photovoltaic parameters of mono- and bifacial solar cells of Cu/ITO/SiO{sub 2}/n–n{sup +} Si/Cu prepared on Si (100) wafers with different surface structures were studied and compared. A maximum efficiency of 15.8% was achieved on monofacial solar cell devices with the textured Si surface. Bifacial photovoltaic devices from 100 μm thick Si wafers with the smooth surface have demonstrated efficiencies of 13.0% at frontal illumination and 10% at rear illumination. - Highlights: • ITO thin films prepared by vapor phase pyrolysis on Si (100) wafers with a smooth (polished), rough (irregularly structured) and textured (by inversed pyramids) surface. • Monofacial ITO/SiO2/n-n+Si solar cells with an efficiency of 15.8% prepared and bifacial PV devices with front- and rear-side efficiencies up to 13% demonstrated. • Comparative studies of photovoltaic properties of solar cells with different morphologies of the Si wafer surface presented.

  16. Low-temperature growth of well-aligned zinc oxide nanorod arrays on silicon substrate and their photocatalytic application

    Directory of Open Access Journals (Sweden)

    Azam A

    2014-04-01

    Full Text Available Ameer Azam,1 Saeed Salem Babkair21Center of Nanotechnology, King Abdulaziz University, Jeddah, Saudi Arabia; 2Center of Nanotechnology, Department of Physics, Faculty of Science, King Abdulaziz University, Jeddah, Saudi ArabiaAbstract: Well-aligned and single-crystalline zinc oxide (ZnO nanorod arrays were grown on silicon (Si substrate using a wet chemical route for the photodegradation of organic dyes. Structural analysis using X-ray diffraction, high-resolution transmission electron microscopy, and selected area electron diffraction confirmed the formation of ZnO nanorods grown preferentially oriented in the (001 direction and with a single phase nature with a wurtzite structure. Field emission scanning electron microscopy and transmission electron microscopy micrographs showed that the length and diameter of the well-aligned rods were about ~350–400 nm and ~80–90 nm, respectively. Raman scattering spectra of ZnO nanorod arrays revealed the characteristic E2 (high mode that is related to the vibration of oxygen atoms in the wurtzite ZnO. The photodegradation of methylene blue (MB using ZnO nanorod arrays was performed under ultraviolet light irradiation. The results of photodegradation showed that ZnO nanorod arrays were capable of degrading ~80% of MB within 60 minutes of irradiation, whereas ~92% of degradation was achieved in 120 minutes. Complete degradation of MB was observed after 270 minutes of irradiation time. Owing to enhanced photocatalytic degradation efficiency and low-temperature growth method, prepared ZnO nanorod arrays may open up the possibility for the successful utilization of ZnO nanorod arrays as a future photocatalyst for environmental remediation.Keywords: ZnO, nanorods, XRD, photodegradation

  17. Photocatalysis in the visible range of sub-stoichiometric anatase films prepared by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Justicia, I. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Garcia, G. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain)]. E-mail: gemma@icmab.es; Battiston, G.A. [ICIS/CNR, Corso Stati Uniti 4, 35127 Padova (Italy); Gerbasi, R. [ICIS/CNR, Corso Stati Uniti 4, 35127 Padova (Italy); Ager, F. [CNA/CSIC Parque Tecnologico Cartuja 93, Avda Thomas A, Edison, 41092 Sevilla (Spain); Guerra, M. [IIQAB/CSIC Jordi Girona, 18 08034 Barcelona (Spain); Caixach, J. [IIQAB/CSIC Jordi Girona, 18 08034 Barcelona (Spain); Pardo, J.A. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Rivera, J. [IIQAB/CSIC Jordi Girona, 18 08034 Barcelona (Spain); Figueras, A. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Instituto de Fisica, UNAM, Campus UNAM Juriquilla, 76230 Queretaro (Mexico)

    2005-08-25

    Anatase phase of titanium oxide is the most promising photocatalyst material for organic pollutant degradation. However, due to its large band gap energy (3.2 eV) it is not viable to use sunlight as an energy source for the photocatalysis activation, and so, ultraviolet (UV) radiation below the wavelength of 380 nm is required. This paper focuses on the experimental demonstration of the reduction of this large band gap energy by inducing defects in the anatase structure under the form of oxygen sub-stoichiometry. TiO{sub 2} thin films were prepared in a metal organic chemical vapour deposition (MOCVD) reactor. The samples stoichiometry was measured by the Rutherford backscattering spectrometry (RBS) technique. Optical characterisation was also performed and the photodegradation activity in the visible range was tested using nonylphenol, which is one of the most harmful pollutants present in waste waters.

  18. Self-assembly silicon/porous reduced graphene oxide composite film as a binder-free and flexible anode for lithium-ion batteries

    International Nuclear Information System (INIS)

    Tang, H.; Zhang, Y.J.; Xiong, Q.Q.; Cheng, J.D.; Zhang, Q.; Wang, X.L.; Gu, C.D.; Tu, J.P.

    2015-01-01

    A Si/porous reduced graphene oxide (rGO) composite film synthesized by evaporation and leavening method are developed as a high-performance anode material for lithium ion batteries. The porous structure as buffer base can effectively release the volume expansion of the silicon particles, increase the electrical conductivity and reduce the transfer resistance of Li ions. The Si/porous rGO composite film presents high specific capacity and good cycling stability (1261 mA h g −1 at 50 mA g −1 up to 70 cycles), as well as enhanced rate capability. This approach to prepare such a unique structure is a low-cost and facile route for the silicon-based anode materials

  19. Features of carrier tunneling between the silicon valence band and metal in devices based on the Al/high-K oxide/SiO_2/Si structure

    International Nuclear Information System (INIS)

    Vexler, M. I.; Grekhov, I. V.

    2016-01-01

    The features of electron tunneling from or into the silicon valence band in a metal–insulator–semiconductor system with the HfO_2(ZrO_2)/SiO_2 double-layer insulator are theoretically analyzed for different modes. It is demonstrated that the valence-band current plays a less important role in structures with HfO_2(ZrO_2)/SiO_2 than in structures containing only silicon dioxide. In the case of a very wide-gap high-K oxide ZrO_2, nonmonotonic behavior related to tunneling through the upper barrier is predicted for the valence-band–metal current component. The use of an insulator stack can offer certain advantages for some devices, including diodes, bipolar tunnel-emitter transistors, and resonant-tunneling diodes, along with the traditional use of high-K insulators in a field-effect transistor.

  20. Adsorbate-modified growth of ultrathin rare-earth oxide films on silicon and complementary studies of cerium oxide on ruthenium; Adsorbat-modifiziertes Wachstum ultraduenner Seltenerdoxid-Filme auf Silizium und komplementaere Studien von Ceroxid auf Ruthenium

    Energy Technology Data Exchange (ETDEWEB)

    Kaemena, Bjoern

    2013-11-27

    Rare-earth oxides (REOx) are extensively investigated due to their extraordinary physical and chemical properties, which essentially arise from the unfilled 4f electron shell, in order to reveal the nature of these exceptional properties and ultimately to utilize them for multiple technological applications. To maintain the exponential increase in integration density in CMOS technology, which is also known as Moore s law, there is a strong desire for ultrathin, well-ordered, epitaxial REOx layers with a precisely engineered interface, which is essential for reliable, ultrahigh-performance devices. So far this has been considerably impeded by RE-promoted silicon oxidation, leading to amorphous silicon oxide and RE silicon formation. By using complementary synchrotron radiation methods such as X-ray standing waves (XSW), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD), structural and spectroscopic information are inferred simultaneously from ultrathin ceria and lanthana films grown on chlorine, silver and gallium passivated silicon(111). In general, it is revealed that the chemical and structural composition of the interface and the crystallinity of ultrathin REOx layers on silicon can be precisely controlled by adsorbate-mediated growth. This might represent a crucial step towards a perfectly engineered interface, eventually allowing for the integration of REOx as high-k gate oxides in microelectronics. In catalysis inverse model catalysts are studied with the aim of getting an in-depth understanding of the basic principles of catalysis. These model systems are employed to study, e. g., the nature of active sites and the reaction pathways in complex catalytic converters. However, a lot remains unknown about the chemical activity and selectivity as a function of the growth mechanism, structure and morphology of these model systems. The powerful spectroscopic photoemission and low-energy electron microscope, which is able to reveal the surface

  1. Substoichiometric hydroxynonenylation of a single protein recapitulates whole-cell-stimulated antioxidant response.

    Science.gov (United States)

    Parvez, Saba; Fu, Yuan; Li, Jiayang; Long, Marcus J C; Lin, Hong-Yu; Lee, Dustin K; Hu, Gene S; Aye, Yimon

    2015-01-14

    Lipid-derived electrophiles (LDEs) that can directly modify proteins have emerged as important small-molecule cues in cellular decision-making. However, because these diffusible LDEs can modify many targets [e.g., >700 cysteines are modified by the well-known LDE 4-hydroxynonenal (HNE)], establishing the functional consequences of LDE modification on individual targets remains devilishly difficult. Whether LDE modifications on a single protein are biologically sufficient to activate discrete redox signaling response downstream also remains untested. Herein, using T-REX (targetable reactive electrophiles and oxidants), an approach aimed at selectively flipping a single redox switch in cells at a precise time, we show that a modest level (∼34%) of HNEylation on a single target is sufficient to elicit the pharmaceutically important antioxidant response element (ARE) activation, and the resultant strength of ARE induction recapitulates that observed from whole-cell electrophilic perturbation. These data provide the first evidence that single-target LDE modifications are important individual events in mammalian physiology.

  2. The intergranular segregation of boron in substoichiometric Ni/sub 3/Al

    Energy Technology Data Exchange (ETDEWEB)

    Choudhury, A.

    1987-12-01

    The intermetallic compound Ni/sub 3/Al offers promise as a material for high temperature applications. In addition to its unusual property of increasing strength with temperature (until approx.700/sup 0/C), it has excellent corrosion and oxidation resistance. Microalloying the alloy with boron has been shown to be dramatically effective in improving its inherent intergranular brittleness. This improvement results from the strong tendency of boron to segregate to the grain boundaries of Ni/sub 3/Al. This research deals with the study of the segregation behavior of boron. Auger electron spectroscopy was chosen as the technique adopted to study this segregation. The strong effect of segregant level on the grain boundary strength level can be controlled by thermal history variations and by variations in the level of solute in the bulk. Cathodic hydrogen charging was shown to be a potent tool in opening up other wise cohesive boundaries for analysis. The effective binding energy of boron at the grain boundaries of Ni/sub 3/Al was calculated from experimental data; it was found to vary between 0.2 and 0.45 eV. Kinetics of segregation have been investigated; the present set of kinetic studies were shown to be inadequate to find a diffusion coefficient and that temperatures lower than those studied here need to be used. As an associated investigation, a set of elemental standards were developed for the particular scanning Auger microprobe used in this study. 141 refs., 94 figs., 26 tabs.

  3. Dependences of deposition rate and OH content on concentration of added trichloroethylene in low-temperature silicon oxide films deposited using silicone oil and ozone gas

    Science.gov (United States)

    Horita, Susumu; Jain, Puneet

    2018-03-01

    We investigated the dependences of the deposition rate and residual OH content of SiO2 films on the concentration of trichloroethylene (TCE), which was added during deposition at low temperatures of 160-260 °C with the reactant gases of silicone oil (SO) and O3. The deposition rate depends on the TCE concentration and is minimum at a concentration of ˜0.4 mol/m3 at 200 °C. The result can be explained by surface and gas-phase reactions. Experimentally, we also revealed that the thickness profile is strongly affected by gas-phase reaction, in which the TCE vapor was blown directly onto the substrate surface, where it mixed with SO and O3. Furthermore, it was found that adding TCE vapor reduces residual OH content in the SiO2 film deposited at 200 °C because TCE enhances the dehydration reaction.

  4. Memory characteristics of silicon nitride with silicon nanocrystals as a charge trapping layer of nonvolatile memory devices

    International Nuclear Information System (INIS)

    Choi, Sangmoo; Yang, Hyundeok; Chang, Man; Baek, Sungkweon; Hwang, Hyunsang; Jeon, Sanghun; Kim, Juhyung; Kim, Chungwoo

    2005-01-01

    Silicon nitride with silicon nanocrystals formed by low-energy silicon plasma immersion ion implantation has been investigated as a charge trapping layer of a polycrystalline silicon-oxide-nitride-oxide-silicon-type nonvolatile memory device. Compared with the control sample without silicon nanocrystals, silicon nitride with silicon nanocrystals provides excellent memory characteristics, such as larger width of capacitance-voltage hysteresis, higher program/erase speed, and lower charge loss rate at elevated temperature. These improved memory characteristics are derived by incorporation of silicon nanocrystals into the charge trapping layer as additional accessible charge traps with a deeper effective trap energy level

  5. Properties and electric characterizations of tetraethyl orthosilicate-based plasma enhanced chemical vapor deposition oxide film deposited at 400 °C for through silicon via application

    International Nuclear Information System (INIS)

    Su, Meiying; Yu, Daquan; Liu, Yijun; Wan, Lixi; Song, Chongshen; Dai, Fengwei; Xue, Kai; Jing, Xiangmeng; Guidotti, Daniel

    2014-01-01

    The dielectric via liner of through silicon vias was deposited at 400 °C using a tetraethyl orthosilicate (TEOS)-based plasma enhanced chemical vapor deposition process in a via-middle integration scheme. The morphology, conformality and chemical compositions of the liner film were characterized using field emission scanning electron microscopy and Fourier Transform Infrared spectroscopy. The thermal properties and electrical performance of blanket TEOS films were investigated by high temperature film stress and mercury probe Capacitance–Voltage measurements. The TEOS SiO 2 films show good conformality, excellent densification, low thermal stress, high breakdown voltage and low current leakage. - Highlights: • Tetraethyl orthosilicate-based oxide films were deposited for packaging application. • The oxide films deposited plasma-enhanced chemical vapor deposition (PECVD) at 400 °C. • The PECVD oxide films exhibit good step coverage. • The 400 °C PECVD oxide films exhibit low thermal stress and current leakage. • The 400 °C PECVD oxide films show high breakdown voltage and acceptable permittivity

  6. Properties and electric characterizations of tetraethyl orthosilicate-based plasma enhanced chemical vapor deposition oxide film deposited at 400 °C for through silicon via application

    Energy Technology Data Exchange (ETDEWEB)

    Su, Meiying, E-mail: sumeiying@ime.ac.cn [Institute of Microelectronics of Chinese Academy of Sciences, Beijing 100029 (China); National Center for Advanced Packaging, Wuxi 214135 (China); Yu, Daquan, E-mail: yudaquan@ime.ac.cn [Institute of Microelectronics of Chinese Academy of Sciences, Beijing 100029 (China); National Center for Advanced Packaging, Wuxi 214135 (China); Jiangsu R and D Center for Internet of Things, Wuxi 214135 (China); Liu, Yijun [Piotech Co. Ltd, Shenyang 110179 (China); Wan, Lixi [Institute of Microelectronics of Chinese Academy of Sciences, Beijing 100029 (China); Song, Chongshen; Dai, Fengwei [Institute of Microelectronics of Chinese Academy of Sciences, Beijing 100029 (China); National Center for Advanced Packaging, Wuxi 214135 (China); Xue, Kai [National Center for Advanced Packaging, Wuxi 214135 (China); Jing, Xiangmeng [Institute of Microelectronics of Chinese Academy of Sciences, Beijing 100029 (China); National Center for Advanced Packaging, Wuxi 214135 (China); Guidotti, Daniel [Institute of Microelectronics of Chinese Academy of Sciences, Beijing 100029 (China)

    2014-01-01

    The dielectric via liner of through silicon vias was deposited at 400 °C using a tetraethyl orthosilicate (TEOS)-based plasma enhanced chemical vapor deposition process in a via-middle integration scheme. The morphology, conformality and chemical compositions of the liner film were characterized using field emission scanning electron microscopy and Fourier Transform Infrared spectroscopy. The thermal properties and electrical performance of blanket TEOS films were investigated by high temperature film stress and mercury probe Capacitance–Voltage measurements. The TEOS SiO{sub 2} films show good conformality, excellent densification, low thermal stress, high breakdown voltage and low current leakage. - Highlights: • Tetraethyl orthosilicate-based oxide films were deposited for packaging application. • The oxide films deposited plasma-enhanced chemical vapor deposition (PECVD) at 400 °C. • The PECVD oxide films exhibit good step coverage. • The 400 °C PECVD oxide films exhibit low thermal stress and current leakage. • The 400 °C PECVD oxide films show high breakdown voltage and acceptable permittivity.

  7. Silicone metalization

    Energy Technology Data Exchange (ETDEWEB)

    Maghribi, Mariam N. (Livermore, CA); Krulevitch, Peter (Pleasanton, CA); Hamilton, Julie (Tracy, CA)

    2008-12-09

    A system for providing metal features on silicone comprising providing a silicone layer on a matrix and providing a metal layer on the silicone layer. An electronic apparatus can be produced by the system. The electronic apparatus comprises a silicone body and metal features on the silicone body that provide an electronic device.

  8. Functionalization of silicon oxide using supercritical fluid deposition of 3,4-epoxybutyltrimethoxysilane for the immobilization of amino-modified oligonucleotide

    Energy Technology Data Exchange (ETDEWEB)

    Rull, Jordi [Université Grenoble Alpes, Grenoble F38000 (France); CEA, LETI, MINATEC Campus, Grenoble Cedex 9 F38054 (France); CEA, iRTSV, LCBM, Grenoble 38054 (France); CNRS, UMR 5249, Grenoble (France); Nonglaton, Guillaume, E-mail: guillaume.nonglaton@cea.fr [Université Grenoble Alpes, Grenoble F38000 (France); CEA, LETI, MINATEC Campus, Grenoble Cedex 9 F38054 (France); Costa, Guillaume; Fontelaye, Caroline [Université Grenoble Alpes, Grenoble F38000 (France); CEA, LETI, MINATEC Campus, Grenoble Cedex 9 F38054 (France); Marchi-Delapierre, Caroline; Ménage, Stéphane [Université Grenoble Alpes, Grenoble F38000 (France); CEA, iRTSV, LCBM, Grenoble 38054 (France); CNRS, UMR 5249, Grenoble (France); Marchand, Gilles [Université Grenoble Alpes, Grenoble F38000 (France); CEA, LETI, MINATEC Campus, Grenoble Cedex 9 F38054 (France)

    2015-11-01

    Graphical abstract: - Highlights: • First example of grafting of 3,4-epoxybutyltrimethoxysilane (EBTMOS) onto silicon oxide by supercritical fluid deposition. • Extraordinary efficiency of the supercritical fluid deposition for the grafting of the EBTMOS compared with the conventional solution or vapor phase methodologies. • Demonstration of the efficiency of this functionalization process for the immobilization of amino-modified oligonucleotides. - Abstract: The functionalization of silicon oxide based substrates using silanes is generally performed through liquid phase methodologies. These processes involve a huge quantity of potentially toxic solvents and present some important disadvantages for the functionalization of microdevices or porous materials, for example the low diffusion. To overcome this drawback, solvent-free methodologies like molecular vapor deposition (MVD) or supercritical fluid deposition (SFD) have been developed. In this paper, the deposition process of 3,4-epoxybutyltrimethoxysilane (EBTMOS) on silicon oxide using supercritical carbon dioxide (scCO{sub 2}) as a solvent is studied for the first time. The oxirane ring of epoxy silanes readily reacts with amine group and is of particular interest for the grafting of amino-modified oligonucleotides or antibodies for diagnostic application. Then the ability of this specific EBTMOS layer to react with amine functions has been evaluated using the immobilization of amino-modified oligonucleotide probes. The presence of the probes is revealed by fluorescence using hybridization with a fluorescent target oligonucleotide. The performances of SFD of EBTMOS have been optimized and then compared with the dip coating and molecular vapor deposition methods, evidencing a better grafting efficiency and homogeneity, a lower reaction time in addition to the eco-friendly properties of the supercritical carbon dioxide. The epoxysilane layers have been characterized by surface enhanced ellipsometric

  9. What Governs Friction of Silicon Oxide in Humid Environment: Contact Area between Solids, Water Meniscus around the Contact, or Water Layer Structure?

    Science.gov (United States)

    Chen, Lei; Xiao, Chen; Yu, Bingjun; Kim, Seong H; Qian, Linmao

    2017-09-26

    In order to understand the interfacial parameters governing the friction force (F t ) between silicon oxide surfaces in humid environment, the sliding speed (v) and relative humidity (RH) dependences of F t were measured for a silica sphere (1 μm radius) sliding on a silicon oxide (SiO x ) surface, using atomic force microscopy (AFM), and analyzed with a mathematical model describing interfacial contacts under a dynamic condition. Generally, F t decreases logarithmically with increasing v to a cutoff value below which its dependence on interfacial chemistry and sliding condition is relatively weak. Above the cutoff value, the logarithmic v dependence could be divided into two regimes: (i) when RH is lower than 50%, F t is a function of both v and RH; (ii) in contrast, at RH ≥ 50%, F t is a function of v only, but not RH. These complicated v and RH dependences were hypothesized to originate from the structure of the water layer adsorbed on the surface and the water meniscus around the annulus of the contact area. This hypothesis was tested by analyzing F t as a function of the water meniscus area (A m ) and volume (V m ) estimated from a thermally activated water-bridge formation model. Surprisingly, it was found that F t varies linearly with V m and correlates poorly with A m at RH contact under ambient conditions.

  10. Studies of the dependence on oxidation thermal processes of effects on the electrical properties of silicon detectors by fast neutron radiation

    International Nuclear Information System (INIS)

    Li, Zheng; Kraner, H.W.

    1991-11-01

    High resistivity silicon detectors along with MOS capacitors made on five silicon dioxides with different thermal conditions (975 degree C to 1200 degree C) have been exposed to fast neutron irradiation up to the fluence of a few times 10 14 n/cm 2 . New measurement techniques such as capacitance-voltage (C-V) of MOS capacitors and current-voltage (I-V) of back to back diodes (p + -n - - p + if n - is not inverted to p) or resistors (p + -p-p + if inverted) have been introduced in this study in monitoring the possible type-inversion (n→p) under high neutron fluence. No type-inversion in the material underneath SiO 2 and the p + contact has been observed so far in this work for detectors made on the five oxides up to the neutron fluence of a few times 10 13 n/cm 2 . However, it has been found that detectors made on higher temperature oxides (T≤ 1100 degree C) exhibit less leakage current increase at high neutron fluence (φ ≤ 10 13 n/cm 2 )

  11. Silicon integrated circuit process

    International Nuclear Information System (INIS)

    Lee, Jong Duck

    1985-12-01

    This book introduces the process of silicon integrated circuit. It is composed of seven parts, which are oxidation process, diffusion process, ion implantation process such as ion implantation equipment, damage, annealing and influence on manufacture of integrated circuit and device, chemical vapor deposition process like silicon Epitaxy LPCVD and PECVD, photolithography process, including a sensitizer, spin, harden bake, reflection of light and problems related process, infrared light bake, wet-etch, dry etch, special etch and problems of etching, metal process like metal process like metal-silicon connection, aluminum process, credibility of aluminum and test process.

  12. Silicon integrated circuit process

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jong Duck

    1985-12-15

    This book introduces the process of silicon integrated circuit. It is composed of seven parts, which are oxidation process, diffusion process, ion implantation process such as ion implantation equipment, damage, annealing and influence on manufacture of integrated circuit and device, chemical vapor deposition process like silicon Epitaxy LPCVD and PECVD, photolithography process, including a sensitizer, spin, harden bake, reflection of light and problems related process, infrared light bake, wet-etch, dry etch, special etch and problems of etching, metal process like metal process like metal-silicon connection, aluminum process, credibility of aluminum and test process.

  13. Silicon nanowire hybrid photovoltaics

    KAUST Repository

    Garnett, Erik C.; Peters, Craig; Brongersma, Mark; Cui, Yi; McGehee, Mike

    2010-01-01

    Silicon nanowire Schottky junction solar cells have been fabricated using n-type silicon nanowire arrays and a spin-coated conductive polymer (PEDOT). The polymer Schottky junction cells show superior surface passivation and open-circuit voltages compared to standard diffused junction cells with native oxide surfaces. External quantum efficiencies up to 88% were measured for these silicon nanowire/PEDOT solar cells further demonstrating excellent surface passivation. This process avoids high temperature processes which allows for low-cost substrates to be used. © 2010 IEEE.

  14. Silicon nanowire hybrid photovoltaics

    KAUST Repository

    Garnett, Erik C.

    2010-06-01

    Silicon nanowire Schottky junction solar cells have been fabricated using n-type silicon nanowire arrays and a spin-coated conductive polymer (PEDOT). The polymer Schottky junction cells show superior surface passivation and open-circuit voltages compared to standard diffused junction cells with native oxide surfaces. External quantum efficiencies up to 88% were measured for these silicon nanowire/PEDOT solar cells further demonstrating excellent surface passivation. This process avoids high temperature processes which allows for low-cost substrates to be used. © 2010 IEEE.

  15. Oxygen transport and GeO2 stability during thermal oxidation of Ge

    Science.gov (United States)

    da Silva, S. R. M.; Rolim, G. K.; Soares, G. V.; Baumvol, I. J. R.; Krug, C.; Miotti, L.; Freire, F. L.; da Costa, M. E. H. M.; Radtke, C.

    2012-05-01

    Oxygen transport during thermal oxidation of Ge and desorption of the formed Ge oxide are investigated. Higher oxidation temperatures and lower oxygen pressures promote GeO desorption. An appreciable fraction of oxidized Ge desorbs during the growth of a GeO2 layer. The interplay between oxygen desorption and incorporation results in the exchange of O originally present in GeO2 by O from the gas phase throughout the oxide layer. This process is mediated by O vacancies generated at the GeO2/Ge interface. The formation of a substoichiometric oxide is shown to have direct relation with the GeO desorption.

  16. Metal-oxide-semiconductor devices based on epitaxial germanium-carbon layers grown directly on silicon substrates by ultra-high-vacuum chemical vapor deposition

    Science.gov (United States)

    Kelly, David Quest

    After the integrated circuit was invented in 1959, complementary metal-oxide-semiconductor (CMOS) technology soon became the mainstay of the semiconductor industry. Silicon-based CMOS has dominated logic technologies for decades. During this time, chip performance has grown at an exponential rate at the cost of higher power consumption and increased process complexity. The performance gains have been made possible through scaling down circuit dimensions by improvements in lithography capabilities. Since scaling cannot continue forever, researchers have vigorously pursued new ways of improving the performance of metal-oxide-semiconductor field-effect transistors (MOSFETs) without having to shrink gate lengths and reduce the gate insulator thickness. Strained silicon, with its ability to boost transistor current by improving the channel mobility, is one of the methods that has already found its way into production. Although not yet in production, high-kappa dielectrics have also drawn wide interest in industry since they allow for the reduction of the electrical oxide thickness of the gate stack without having to reduce the physical thickness of the dielectric. Further out on the horizon is the incorporation of high-mobility materials such as germanium (Ge), silicon-germanium (Si1-xGe x), and the III-V semiconductors. Among the high-mobility materials, Ge has drawn the most attention because it has been shown to be compatible with high-kappa dielectrics and to produce high drive currents compared to Si. Among the most difficult challenges for integrating Ge on Si is finding a suitable method for reducing the number of crystal defects. The use of strain-relaxed Si1- xGex buffers has proven successful for reducing the threading dislocation density in Ge epitaxial layers, but questions remain as to the viability of this method in terms of cost and process complexity. This dissertation presents research on thin germanium-carbon (Ge 1-yCy layers on Si for the fabrication

  17. Substoichiometric isotope dilution analysis of arsenic in biological and environmental standard reference materials by solvent extraction using toluene-3,4-dithiol in benzene

    International Nuclear Information System (INIS)

    Chutke, N.L.; Ambulkar, Ms.M.N.; Weginwar, R.G.; Garg, A.N.

    1994-01-01

    A radiochemical solvent extraction procedure has been developed for the determination of As(III) using 76 As tracer. It is based on the complexation of As(III) with toluene-3,4-dithiol (TDT) at pH 2 and subsequent extraction in benzene. The effect of various parameters such as pH, time of equilibration, nature of solvent, quantitative character and interferences have been studied. The method has been further developed into substoichiometric isotope dilution analysis for the determination of As at < 1μg level and employed for the analysis of several environmental and biological standard Reference Materials from NIST (USA), IAEA (Vienna) and NIES (Japan). (author) 39 refs.; 4 figs.; 4 tabs

  18. Comparative substoichiometric extraction and quantification of mercury in geological water samples with potassium salts of ethyl, propyl, butyl, pentyl and benzyl xanthates

    International Nuclear Information System (INIS)

    Chandrasekhar, R.P.; Rangamannar, B.

    1996-01-01

    The relative extent of extraction of mercury with potassium salts of ethyl, propyl, butyl, pentyl and benzyl xanthates has been studied employing a sensitive and rapid substoichiometric radiochemical method. The effect of pH on the extractability of mercury xanthate complexes into chloroform was investigated. Buffer solutions of pH 12, 11, 10, 9 and 5.5 were found to be suitable media for the maximum extraction of mercury as ethyl, propyl, butyl, pentyl and benzyl xanthate complexes, respectively. The procedures developed were utilized for the determination of mercury content in standard solutions and geological water samples collected in eight parts of Chittoor district of Andhra Pradesh. (author). 4 refs., 3 figs., 4 tabs

  19. Monolithic integration of a silicon nanowire field-effect transistors array on a complementary metal-oxide semiconductor chip for biochemical sensor applications.

    Science.gov (United States)

    Livi, Paolo; Kwiat, Moria; Shadmani, Amir; Pevzner, Alexander; Navarra, Giulio; Rothe, Jörg; Stettler, Alexander; Chen, Yihui; Patolsky, Fernando; Hierlemann, Andreas

    2015-10-06

    We present a monolithic complementary metal-oxide semiconductor (CMOS)-based sensor system comprising an array of silicon nanowire field-effect transistors (FETs) and the signal-conditioning circuitry on the same chip. The silicon nanowires were fabricated by chemical vapor deposition methods and then transferred to the CMOS chip, where Ti/Pd/Ti contacts had been patterned via e-beam lithography. The on-chip circuitry measures the current flowing through each nanowire FET upon applying a constant source-drain voltage. The analog signal is digitized on chip and then transmitted to a receiving unit. The system has been successfully fabricated and tested by acquiring I-V curves of the bare nanowire-based FETs. Furthermore, the sensing capabilities of the complete system have been demonstrated by recording current changes upon nanowire exposure to solutions of different pHs, as well as by detecting different concentrations of Troponin T biomarkers (cTnT) through antibody-functionalized nanowire FETs.

  20. X-ray irradiation effects of interface traps and trapped-oxide charge at the Si-SiO{sub 2} interface of segmented silicon sensors

    Energy Technology Data Exchange (ETDEWEB)

    Kopsalis, Ioannis; Fretwurst, Eckhart; Garutti, Erika; Klanner, Robert; Schwandt, Joern [Institute for Experimental Physics, Hamburg University, Luruper Chaussee 149, D-22761 Hamburg (Germany)

    2016-07-01

    The surface radiation damage of SiO{sub 2} grown on high-ohmic Si, as used for the fabrication of segmented silicon sensors, has been investigated. Circular p- and n-MOSFETs, biased in accumulation and inversion at a field in the SiO{sub 2} of about 500 kV/cm, have been irradiated by X-rays up to a dose of about 17 kGy(SiO{sub 2}) in different irradiation steps. Before and after each irradiation, the gate voltage has been cycled from inversion to accumulation conditions and back, and from the dependence of the drain-source current, on gate voltage, the threshold voltage of the MOSFET and the hole and electron mobility at the Si-SiO{sub 2} interface determined. From the threshold voltage, the effective oxide-charge density is calculated. Using the subthreshold-current technique the contribution of interface traps, in the lower and the upper part of the energy Si bandgap, and of fixed oxide-charge to the effective oxide-charge density has been estimated. Results on the dose dependence of the above quantities, the charging-up and discharging of border traps when changing the gate voltage, and the hole and electron mobilities at the Si-SiO{sub 2} interface are presented.

  1. Correlation between the transport mechanisms in conductive filaments inside Ta2O5-based resistive switching devices and in substoichiometric TaOx thin films

    Science.gov (United States)

    Rosário, Carlos M. M.; Thöner, Bo; Schönhals, Alexander; Menzel, Stephan; Wuttig, Matthias; Waser, Rainer; Sobolev, Nikolai A.; Wouters, Dirk J.

    2018-05-01

    Conductive filaments play a key role in redox-based resistive random access memory (ReRAM) devices based on the valence change mechanism, where the change of the resistance is ascribed to the modulation of the oxygen content in a local region of these conductive filaments. However, a deep understanding of the filaments' composition and structure is still a matter of debate. We approached the problem by comparing the electronic transport, at temperatures from 300 K down to 2 K, in the filaments and in TaOx films exhibiting a substoichiometric oxygen content. The filaments were created in Ta (15 nm)/Ta2O5 (5 nm)/Pt crossbar ReRAM structures. In the TaOx thin films with various oxygen contents, the in-plane transport was studied. There is a close similarity between the electrical properties of the conductive filaments in the ReRAM devices and of the TaOx films with x ˜ 1, evidencing also no dimensionality difference for the electrical transport. More specifically, for both systems there are two different conduction processes: one in the higher temperature range (from 50 K up to ˜300 K), where the conductivity follows a √{ T } dependence, and one at lower temperatures (<50 K), where the conductivity follows the exp(-1 / √{ T } ) dependence. This suggests a strong similarity between the material composition and structure of the filaments and those of the substoichiometric TaOx films. We also discuss the temperature dependence of the conductivity in the framework of possible transport mechanisms, mainly of those normally observed for granular metals.

  2. Preparation of magnetic and bioactive calcium zinc iron silicon oxide composite for hyperthermia treatment of bone cancer and repair of bone defects.

    Science.gov (United States)

    Jiang, Yumin; Ou, Jun; Zhang, Zhanhe; Qin, Qing-Hua

    2011-03-01

    In this paper, a calcium zinc iron silicon oxide composite (CZIS) was prepared using the sol-gel method. X-ray diffraction (XRD) was then employed to test the CZIS composite. The results from the test showed that the CZIS had three prominent crystalline phases: Ca(2)Fe(1.7)Zn(0.15)Si(0.15)O(5), Ca(2)SiO(4), and ZnFe(2)O(4). Calorimetric measurements were then performed using a magnetic induction furnace. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) analysis were conducted to confirm the growth of a precipitated hydroxyapatite phase after immersion in simulated body fluid (SBF). Cell culture experiments were also carried out, showing that the CZIS composite more visibly promoted osteoblast proliferation than ZnFe(2)O(4) glass ceramic and HA, and osteoblasts adhered and spread well on the surfaces of composite samples.

  3. Contribution to the study of low-energy X-ray-induced degradations on the oxide-silicon interfacial transition layer of MOS structures

    International Nuclear Information System (INIS)

    Boukabache, Ali

    1983-01-01

    The Si-SiO_2 interface is considered as a transition layer. Its thickness is typically about 10 A. It contains traps which exchange charges with silicon by a tunneling mechanism. Its influence on MOS capacitor, gate-controlled diode and MOS transistor is analyzed. Long channel MOST's (P-Substrate) are irradiated with low energy X-ray (between 0 and 240 Krads) in order to validate the model. Capacitance, recombination velocity and 1/f noise measurements indicate that the X- ray induce traps distributed in space and in energy. These traps provoke a decrease in mobility. Additionally, X-rays create a fixed oxide charge which induce a shift in the characteristics of MOS structures. Finally, under irradiation the behaviour of the gate-controlled diode and the MOS capacitor are in accordance with theoretical model of the interfacial layer. The overall noise behaviour cannot be explained by existing theoretical models. (author) [fr

  4. AFM investigation of effect of absorbed water layer structure on growth mechanism of octadecyltrichlorosilane self-assembled monolayer on oxidized silicon

    International Nuclear Information System (INIS)

    Li, Shaowei; Zheng, Yanjun; Chen, Changfeng

    2016-01-01

    The growth mechanism of an octadecyltrichlorosilane (OTS) self-assembled monolayer on a silicon oxide surface at various relative humidities has been investigated. Atomic force microscopy images show that excess water may actually hinder the nucleation and growth of OTS islands. A moderate amount of water is favorable for the nucleation and growth of OTS islands in the initial stage; however, the completion of the monolayer is very slow in the final stage. The growth of OTS islands on a low-water-content surface maintains a relatively constant speed and requires the least amount of time. The mobility of water molecules is thought to play an important role in the OTS monolayers, and a low-mobility water layer provides a steady condition for OTS monolayer growth.

  5. Formation of superhydrophobic/superhydrophilic patterns by combination of nanostructure-imprinted perfluoropolymer and nanostructured silicon oxide for biological droplet generation

    Science.gov (United States)

    Kobayashi, Taizo; Shimizu, Kazunori; Kaizuma, Yoshihiro; Konishi, Satoshi

    2011-03-01

    In this letter, we report a technology for fabricating superhydrophobic/superhydrophilic patterns using a combination of a nanostructure-imprinted perfluoropolymer and nanostructured silicon oxide. In our previous study, we used a combination of hydrophobic and superhydrophilic materials. However, it was difficult to split low-surface-tension liquids such as biological liquids into droplets solely using hydrophobic/hydrophilic patterns. In this study, the contact angle of the hydrophobic region was enhanced from 109.3° to 155.6° by performing nanostructure imprinting on a damage-reduced perfluoropolymer. The developed superhydrophobic/superhydrophilic patterns allowed the splitting of even those media that contained fetal bovine serum into droplets of a desired shape.

  6. A Facile Method for Detection of Substituted Salicylic Acids Using Pyrenesulfonamide-Terminated Self-Assembled Monolayers on Silicon Oxide Surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Han, Gyeongyeop; Choi, Jaehyuck; Lee, Jungkyu; Kumar, Ashwani; Lee, Ju-Young; Kim, Hong-Seok [Kyungpook Nation al University, Daegu (Korea, Republic of)

    2016-05-15

    We have developed a method for sensing substituted salicylic acids on silicon oxide surfaces. The receptor molecule was successfully immobilized onto the surface by self-assembly, and, as a demonstration, micropatterns of substituted salicylic acids were generated by soft lithography techniques. We believe that this approach used herein will not only widen the understanding of the specific interactions between salicylic acids and pyrenesulfonamide derivatives, but also be applicable to practical devices such as chemo/bio analytical sensors. We have successfully demonstrated the molecular recognition between salicylic acids and pyrene derivatives in solution by fluorescence measurement. Briefly, selective recognition was achieved using intermolecular interactions, including π-π interactions and multi-hydrogen bonds, and intramolecular hydrogen bonding between the phenolic O-H group and the adjacent C=O group.

  7. A Facile Method for Detection of Substituted Salicylic Acids Using Pyrenesulfonamide-Terminated Self-Assembled Monolayers on Silicon Oxide Surfaces

    International Nuclear Information System (INIS)

    Han, Gyeongyeop; Choi, Jaehyuck; Lee, Jungkyu; Kumar, Ashwani; Lee, Ju-Young; Kim, Hong-Seok

    2016-01-01

    We have developed a method for sensing substituted salicylic acids on silicon oxide surfaces. The receptor molecule was successfully immobilized onto the surface by self-assembly, and, as a demonstration, micropatterns of substituted salicylic acids were generated by soft lithography techniques. We believe that this approach used herein will not only widen the understanding of the specific interactions between salicylic acids and pyrenesulfonamide derivatives, but also be applicable to practical devices such as chemo/bio analytical sensors. We have successfully demonstrated the molecular recognition between salicylic acids and pyrene derivatives in solution by fluorescence measurement. Briefly, selective recognition was achieved using intermolecular interactions, including π-π interactions and multi-hydrogen bonds, and intramolecular hydrogen bonding between the phenolic O-H group and the adjacent C=O group

  8. Relative SHG measurements of metal thin films: Gold, silver, aluminum, cobalt, chromium, germanium, nickel, antimony, titanium, titanium nitride, tungsten, zinc, silicon and indium tin oxide

    Directory of Open Access Journals (Sweden)

    Franklin Che

    Full Text Available We have experimentally measured the surface second-harmonic generation (SHG of sputtered gold, silver, aluminum, zinc, tungsten, copper, titanium, cobalt, nickel, chromium, germanium, antimony, titanium nitride, silicon and indium tin oxide thin films. The second-harmonic response was measured in reflection using a 150 fs p-polarized laser pulse at 1561 nm. We present a clear comparison of the SHG intensity of these films relative to each other. Our measured relative intensities compare favorably with the relative intensities of metals with published data. We also report for the first time to our knowledge the surface SHG intensity of tungsten and antimony relative to that of well known metallic thin films such as gold and silver. Keywords: Surface second-harmonic generation, Nonlinear optics, Metal thin films

  9. Porous Silicon Nanowires

    Science.gov (United States)

    Qu, Yongquan; Zhou, Hailong; Duan, Xiangfeng

    2011-01-01

    In this minreview, we summarize recent progress in the synthesis, properties and applications of a new type of one-dimensional nanostructures — single crystalline porous silicon nanowires. The growth of porous silicon nanowires starting from both p- and n-type Si wafers with a variety of dopant concentrations can be achieved through either one-step or two-step reactions. The mechanistic studies indicate the dopant concentration of Si wafers, oxidizer concentration, etching time and temperature can affect the morphology of the as-etched silicon nanowires. The porous silicon nanowires are both optically and electronically active and have been explored for potential applications in diverse areas including photocatalysis, lithium ion battery, gas sensor and drug delivery. PMID:21869999

  10. Analysis of buried etch-stop layers in silicon by nitrogen-ion implantation

    International Nuclear Information System (INIS)

    Acero, M.C.; Esteve, J.; Montserrat, J.; Perez-Rodriguez, A.; Garrido, B.; Romano-Rodriguez, A.; Morante, J.R.

    1993-01-01

    The analysis of the etch-stop properties of layers obtained by substoichiometric nitrogen-ion implantation and annealing in silicon has been performed as a function of the implantation conditions. The analysis of the etching efficiency has been tested in TMAH-IPA systems. The results obtained show the need to implant at doses higher than 2 x 10 17 cm -2 to obtain etch-stop layers stable under high-temperature annealing. So, for implantation doses of 5 x 10 17 cm -2 , layers stand unetched for times longer than 2 h. The preliminary structural analysis of the samples suggests the presence of an amorphous silicon nitride layer for higher implantation doses. (author)

  11. Analysis of buried etch-stop layers in silicon by nitrogen-ion implantation

    Energy Technology Data Exchange (ETDEWEB)

    Acero, M.C.; Esteve, J.; Montserrat, J. (Centro Nacional de Microelectronica (CNM-CSIC), Bellaterra (Spain)); Perez-Rodriguez, A.; Garrido, B.; Romano-Rodriguez, A.; Morante, J.R. (Barcelona Univ. (Spain). Dept. Fisica Aplicada i Electronica)

    1993-09-01

    The analysis of the etch-stop properties of layers obtained by substoichiometric nitrogen-ion implantation and annealing in silicon has been performed as a function of the implantation conditions. The analysis of the etching efficiency has been tested in TMAH-IPA systems. The results obtained show the need to implant at doses higher than 2 x 10[sup 17] cm[sup -2] to obtain etch-stop layers stable under high-temperature annealing. So, for implantation doses of 5 x 10[sup 17] cm[sup -2], layers stand unetched for times longer than 2 h. The preliminary structural analysis of the samples suggests the presence of an amorphous silicon nitride layer for higher implantation doses. (author).

  12. Zinc tin oxide as high-temperature stable recombination layer for mesoscopic perovskite/silicon monolithic tandem solar cells

    KAUST Repository

    Werner, Jé ré mie; Walter, Arnaud; Rucavado, Esteban; Moon, Soo Jin; Sacchetto, Davide; Rienaecker, Michael; Peibst, Robby; Brendel, Rolf; Niquille, Xavier; De Wolf, Stefaan; Lö per, Philipp; Morales-Masis, Monica; Nicolay, Sylvain; Niesen, Bjoern; Ballif, Christophe

    2016-01-01

    the concept, we fabricate monolithic tandem cells with mesoscopic top cell with up to 16% efficiency. We then investigate the effect of zinc tin oxide layer thickness variation, showing a strong influence on the optical interference pattern within the tandem

  13. Oxidation resistance in air of 1-D SiC (Hi-nicalon) fibre reinforced silicon nitride ceramic matrix composite

    International Nuclear Information System (INIS)

    Dupel, P.; Veyret, J.B.

    1997-01-01

    The oxidation behaviour of a Si 3 N 4 matrix reinforced with SiC fibres (Hi-nicalon) pre-coated with a 400 nm thick pyrolytic carbon layer has been investigated in dry air in the temperature range 800-1500 C. The same study was performed for individual constituents of the composite (fibre and matrix). Two phenomena are observed in the oxidation behaviour of the composite. At low temperature (T<1200 C), the matrix oxidation is negligible, only the carbon interphase was oxidised creating an annular space between the fibres and the matrix throughout the sample. At high temperature (T≥1300 C) the rate of formation of the oxidation products of the matrix is rapid and a sealing effect is observed. While at these temperatures the interphase is protected in the bulk of the material, the time needed to seal the gap between the fibre and the matrix is too long to prevent its oxidation to a significant depth from the surface. Finally, preliminary results are presented where the consumption of the interphase is completely prevented by applying an external coating which gives oxidation protection from low to high temperature. (orig.)

  14. Characterization of Urea Versus hmta in the Preparation of Zinc Oxide NANOSTRUCTURES by Catalytic Immersion Method Grown on Gold-seeded Silicon Substrate

    International Nuclear Information System (INIS)

    Azlinda Abdul Aziz; Khusaimi, Z.; Rusop, M.

    2011-01-01

    Zinc oxide (ZnO) nano structured prepared by immersed method were successfully grown on gold-seeded silicon substrate using Zinc nitrate hexahydrate (Zn(NO 3 ) 2 .6H 2 O) as a precursor was stabilized by a non-toxic urea (CH 4 N 2 O) in a ratio of 1:2 and 1:1 ratio of hexamethylene tetraamine (HMTA). The effect of changing the stabilizer of ZnO solution on the crystal structure, morphology and photoluminescence properties of the resultant ZnO is investigated. X-ray diffraction of the synthesized ZnO shows hexagonal zincite structure. The morphology of the ZnO was characterizing using Field Emission Scanning Electron Microscope (FESEM). The growth of ZnO using urea as stabilizer shows the clusters of ZnO nano flower with serrated broad petals and sharp tips of approximately 25 nm were interestingly formed. ZnO in HMTA showed growth of nano rods. The structures has high surface area, is a potential metal oxide nano structures to be develop for optoelectronic devices and chemical sensors. The formation of ZnO nano structures is found to be significantly affected by the stabilizer. (author)

  15. Demonstration of AlGaN/GaN metal-oxide-semiconductor high-electron-mobility transistors with silicon-oxy-nitride as the gate insulator

    International Nuclear Information System (INIS)

    Balachander, K.; Arulkumaran, S.; Egawa, T.; Sano, Y.; Baskar, K.

    2005-01-01

    AlGaN/GaN metal-oxide-semiconductor high-electron-mobility transistors (MOSHEMTs) were fabricated with plasma enhanced chemical vapor deposited silicon oxy-nitride (SiON) as an insulating layer. The compositions of SiON thin films were confirmed using X-ray photoelectron spectroscopy. The fabricated MOSHEMTs exhibited a very high saturation current density of 1.1 A/mm coupled with high positive operational gate voltage up to +7 V. The MOSHEMTs also exhibited four orders of low gate leakage current and high forward-on voltage when compared with the conventional HEMTs. The drain current collapse using gate pulse measurements showed only a negligible difference in the saturation current density revealing the drastic improvement in passivation of the surface states due to the high quality of dielectric thin films deposited. Thus, based on the improved direct-current operation, SiON can be considered to be a potential gate oxide comparable with other dielectric insulators

  16. Silver nanoparticle formation in thin oxide layer on silicon by silver-negative-ion implantation for Coulomb blockade at room temperature

    International Nuclear Information System (INIS)

    Tsuji, Hiroshi; Arai, Nobutoshi; Matsumoto, Takuya; Ueno, Kazuya; Gotoh, Yasuhito; Adachi, Kouichiro; Kotaki, Hiroshi; Ishikawa, Junzo

    2004-01-01

    Formation of silver nanoparticles formed by silver negative-ion implantation in a thin SiO 2 layer and its I-V characteristics were investigated for development single electron devices. In order to obtain effective Coulomb blockade phenomenon at room temperature, the isolated metal nanoparticles should be in very small size and be formed in a thin insulator layer such as gate oxide on the silicon substrate. Therefore, conditions of a fine particles size, high particle density and narrow distribution should be controlled at their formation without any electrical breakdown of the thin insulator layer. We have used a negative-ion implantation technique with an advantage of 'charge-up free' for insulators, with which no breakdown of thin oxide layer on Si was obtained. In the I-V characteristics with Au electrode, the current steps were observed with a voltage interval of about 0.12 V. From the step voltage the corresponded capacitance was calculated to be 0.7 aF. In one nanoparticle system, this value of capacitance could be given by a nanoparticle of about 3 nm in diameter. This consideration is consistent to the measured particle size in the cross-sectional TEM observation. Therefore, the observed I-V characteristics with steps are considered to be Coulomb staircase by the Ag nanoparticles

  17. Preparation of thin hexagonal highly-ordered anodic aluminum oxide (AAO) template onto silicon substrate and growth ZnO nanorod arrays by electrodeposition

    Science.gov (United States)

    Chahrour, Khaled M.; Ahmed, Naser M.; Hashim, M. R.; Elfadill, Nezar G.; Qaeed, M. A.; Bououdina, M.

    2014-12-01

    In this study, anodic aluminum oxide (AAO) templates of Aluminum thin films onto Ti-coated silicon substrates were prepared for growth of nanostructure materials. Hexagonally highly ordered thin AAO templates were fabricated under controllable conditions by using a two-step anodization. The obtained thin AAO templates were approximately 70 nm in pore diameter and 250 nm in length with 110 nm interpore distances within an area of 3 cm2. The difference between first and second anodization was investigated in details by in situ monitoring of current-time curve. A bottom barrier layer of the AAO templates was removed during dropping the voltage in the last period of the anodization process followed by a wet etching using phosphoric acid (5 wt%) for several minutes at ambient temperature. As an application, Zn nanorod arrays embedded in anodic alumina (AAO) template were fabricated by electrodeposition. Oxygen was used to oxidize the electrodeposited Zn nanorods in the AAO template at 700 °C. The morphology, structure and photoluminescence properties of ZnO/AAO assembly were analyzed using Field-emission scanning electron microscope (FESEM), Energy dispersive X-ray spectroscopy (EDX), Atomic force microscope (AFM), X-ray diffraction (XRD) and photoluminescence (PL).

  18. Preparation and characterization of hybrid materials of epoxy resin type bisphenol a with silicon and titanium oxides by sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Carrillo C, A.; Osuna A, J. G., E-mail: acc.carrillo@gmail.com [Universidad Autonoma de Coahuila, Facultad de Ciencias Quimicas, Blvd. Venustiano Carranza y Jose Cardenas Valdes, 25000 Saltillo, Coahuila (Mexico)

    2011-07-01

    Hybrid materials were synthesized from epoxy resins as a result bisphenol type A-silicon oxide and epoxy resin bisphenol type A-titanium oxide were obtained. The synthesis was done by sol-gel process using tetraethyl orthosilicate (Teos) and titanium isopropoxide (I Ti) as inorganic precursors. The molar ratio of bisphenol A to the inorganic precursors was the studied variable. The materials were characterized by thermal analysis, infrared spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. The hybrid nature of the materials was demonstrated through thermal analysis and infrared spectroscopy. In both systems, as the amount of alkoxide increased, the bands described above were more defined. This behavior indicates the interactions between the resin and the alkoxides. Hybrids with Teos showed a smoother and homogeneous surface in its entirety, without irregularities. Hybrids with titanium isopropoxide had low roughness. Both Teos and I Ti hybrids showed a decrease on the atomic weight percentage of carbon due to a slight reduction of the organic part on the surface. (Author)

  19. Preparation and characterization of hybrid materials of epoxy resin type bisphenol a with silicon and titanium oxides by sol-gel process

    International Nuclear Information System (INIS)

    Carrillo C, A.; Osuna A, J. G.

    2011-01-01

    Hybrid materials were synthesized from epoxy resins as a result bisphenol type A-silicon oxide and epoxy resin bisphenol type A-titanium oxide were obtained. The synthesis was done by sol-gel process using tetraethyl orthosilicate (Teos) and titanium isopropoxide (I Ti) as inorganic precursors. The molar ratio of bisphenol A to the inorganic precursors was the studied variable. The materials were characterized by thermal analysis, infrared spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. The hybrid nature of the materials was demonstrated through thermal analysis and infrared spectroscopy. In both systems, as the amount of alkoxide increased, the bands described above were more defined. This behavior indicates the interactions between the resin and the alkoxides. Hybrids with Teos showed a smoother and homogeneous surface in its entirety, without irregularities. Hybrids with titanium isopropoxide had low roughness. Both Teos and I Ti hybrids showed a decrease on the atomic weight percentage of carbon due to a slight reduction of the organic part on the surface. (Author)

  20. Antireflection/Passivation Step For Silicon Cell

    Science.gov (United States)

    Crotty, Gerald T.; Kachare, Akaram H.; Daud, Taher

    1988-01-01

    New process excludes usual silicon oxide passivation. Changes in principal electrical parameters during two kinds of processing suggest antireflection treatment almost as effective as oxide treatment in passivating cells. Does so without disadvantages of SiOx passivation.

  1. Silicon detectors

    International Nuclear Information System (INIS)

    Klanner, R.

    1984-08-01

    The status and recent progress of silicon detectors for high energy physics is reviewed. Emphasis is put on detectors with high spatial resolution and the use of silicon detectors in calorimeters. (orig.)

  2. Effect of low thermal budget annealing on surface passivation of silicon by ALD based aluminum oxide films.

    Science.gov (United States)

    Vandana; Batra, Neha; Gope, Jhuma; Singh, Rajbir; Panigrahi, Jagannath; Tyagi, Sanjay; Pathi, P; Srivastava, S K; Rauthan, C M S; Singh, P K

    2014-10-21

    Thermal ALD deposited Al2O3 films on silicon show a marked difference in surface passivation quality as a function of annealing time (using a rapid thermal process). An effective and quality passivation is realized in short anneal duration (∼100 s) in nitrogen ambient which is reflected in the low surface recombination velocity (SRV passivation. Both as-deposited and low thermal budget annealed films show the presence of positive fixed charges and this is never been reported in the literature before. The role of field and chemical passivation is investigated in terms of fixed charge and interface defect densities. Further, the importance of the annealing step sequence in the MIS structure fabrication protocol is also investigated from the view point of its effect on the nature of fixed charges.

  3. Comparison of secondary ion emission induced in silicon oxide by MeV and KeV ion bombardment

    International Nuclear Information System (INIS)

    Allali, H.; Nsouli, B.; Thomas, J.P.; Szymczak, W.; Wittmaack, K.

    1993-09-01

    The surface and near-surface composition of SiO 2 layers, has been investigated by negative secondary ion emission mass spectrometry (SIMS) using MeV and KeV ion bombardment in combination with time-of-flight (TOF) mass analysis. The spectra recorded in the mass range 0-100 u are dominated by surface impurities, notably hydrocarbons and silicon polyanions incorporating H and OH entities. The characteristic (fragmentation) patterns are quite different for light and high-velocity ion impact. In high-velocity TOF-SIMS analysis of P-doped layers, prepared by chemical vapour deposition (CVD), the mass lines at 63 and 79 u are very prominent and appear to correlate with the phosphorus concentration (PO 2 and PO 3 , respectively). It is shown, however, that for unambiguous P analysis one has to use dynamic SIMS or high mass resolution. (author) 11 refs., 5 figs

  4. Arsenic implantation into polycrystalline silicon and diffusion to silicon substrate

    International Nuclear Information System (INIS)

    Tsukamoto, K.; Akasaka, Y.; Horie, K.

    1977-01-01

    Arsenic implantation into polycrystalline silicon and drive-in diffusion to silicon substrate have been investigated by MeV He + backscattering analysis and also by electrical measurements. The range distributions of arsenic implanted into polycrystalline silicon are well fitted to Gaussian distributions over the energy range 60--350 keV. The measured values of R/sub P/ and ΔR/sub P/ are about 10 and 20% larger than the theoretical predictions, respectively. The effective diffusion coefficient of arsenic implanted into polycrystalline silicon is expressed as D=0.63 exp[(-3.22 eV/kT)] and is independent of the arsenic concentration. The drive-in diffusion of arsenic from the implanted polycrystalline silicon layer into the silicon substrate is significantly affected by the diffusion atmosphere. In the N 2 atmosphere, a considerable amount of arsenic atoms diffuses outward to the ambient. The outdiffusion can be suppressed by encapsulation with Si 3 N 4 . In the oxidizing atmosphere, arsenic atoms are driven inward by growing SiO 2 due to the segregation between SiO 2 and polycrystalline silicon, and consequently the drive-in diffusion of arsenic is enhanced. At the interface between the polycrystalline silicon layer and the silicon substrate, arsenic atoms are likely to segregate at the polycrystalline silicon side

  5. Characterization of silicon oxynitride films prepared by the simultaneous implantation of oxygen and nitrogen ions into silicon

    International Nuclear Information System (INIS)

    Hezel, R.; Streb, W.

    1985-01-01

    Silicon oxynitride films about 5 nm in thickness were prepared by simultaneously implanting 5 keV oxygen and nitrogen ions into silicon at room temperature up to saturation. These films with concentrations ranging from pure silicon oxide to silicon nitride were characterized using Auger electron spectroscopy, electron energy loss spectroscopy and depth-concentration profiling. The different behaviour of the silicon oxynitride films compared with those of silicon oxide and silicon nitride with regard to thermal stability and hardness against electron and argon ion irradiation is pointed out. (Auth.)

  6. Field effect of fixed negative charges on oxidized silicon induced by AlF3 layers with fluorine deficiency

    International Nuclear Information System (INIS)

    Koenig, D.; Zahn, D.R.T.; Ebest, G.

    2004-01-01

    We recently discovered that in an AlF 3 /SiO 2 /Si structure extrinsic electrons are trapped at fluorine (F) vacancies in AlF 3 at the interface with SiO 2 , generating a high sheet density of fixed negative charges. p- and n-Type Si substrates were oxidized using rapid thermal oxidation (RTO) or furnace oxidation (th); some samples were passivated in hydrogen (H 2 ). AlF 3 was deposited onto oxidized Si wafers by a modified PVD process, leading to a F deficiency (AlF x ). Samples were characterized by mercury probe (Hg) CV and microwave photo conduction decay (μW-PCD), determining charge and trap densities and effective carrier lifetime τ eff , respectively. An effective charge density of up to |Q eff = -6.9 x 10 12 cm -2 is reached due to electrons tunneling from Si into AlF 3 , occupying F vacancies. Lifetime scans of p-type float zone (FZ) Si samples with 1.5 nm RTO and 20 nm AlF 3 show an increase in effective minority carrier lifetime by a factor of 8.4 compared to samples with 1.5 nm RTO only. The fixed negative charge density increases with exposure time to sunlight or at simulated ageing by a 24 h anneal at 200 deg. C in air

  7. Silicon microphotonic waveguides

    International Nuclear Information System (INIS)

    Ta'eed, V.; Steel, M.J.; Grillet, C.; Eggleton, B.; Du, J.; Glasscock, J.; Savvides, N.

    2004-01-01

    Full text: Silicon microphotonic devices have been drawing increasing attention in the past few years. The high index-difference between silicon and its oxide (Δn = 2) suggests a potential for high-density integration of optical functions on to a photonic chip. Additionally, it has been shown that silicon exhibits strong Raman nonlinearity, a necessary property as light interaction can occur only by means of nonlinearities in the propagation medium. The small dimensions of silicon waveguides require the design of efficient tapers to couple light to them. We have used the beam propagation method (RSoft BeamPROP) to understand the principles and design of an inverse-taper mode-converter as implemented in several recent papers. We report on progress in the design and fabrication of silicon-based waveguides. Preliminary work has been conducted by patterning silicon-on-insulator (SOI) wafers using optical lithography and reactive ion etching. Thus far, only rib waveguides have been designed, as single-mode ridge-waveguides are beyond the capabilities of conventional optical lithography. We have recently moved to electron beam lithography as the higher resolutions permitted will provide the flexibility to begin fabricating sub-micron waveguides

  8. Ion beam studied of silicon oxynitride and silicon nitroxide thin layers

    International Nuclear Information System (INIS)

    Oude Elferink, J.B.

    1989-01-01

    In this the processes occurring during high temperature treatments of silicon oxynitride and silicon oxide layers are described. Oxynitride layers with various atomic oxygen to nitrogen concentration ration (O/N) are considered. The high energy ion beam techniques Rutherford backscattering spectroscopy, elastic recoil detection and nuclear reaction analysis have been used to study the layer structures. A detailed discussion of these ion beam techniques is given. Numerical methods used to obtain quantitative data on elemental compositions and depth profiles are described. The electrical compositions and depth profiles are described. The electrical properties of silicon nitride films are known to be influenced by the behaviour of hydrogen in the film during high temperature anneling. Investigations of the behaviour of hydrogen are presented. Oxidation of silicon (oxy)nitride films in O 2 /H 2 0/HCl and nitridation of silicon dioxide films in NH 3 are considered since oxynitrides are applied as an oxidation mask in the LOCOS (Local oxidation of silicon) process. The nitridation of silicon oxide layers in an ammonia ambient is considered. The initial stage and the dependence on the oxide thickness of nitrogen and hydrogen incorporation are discussed. Finally, oxidation of silicon oxynitride layers and of silicon oxide layers are compared. (author). 76 refs.; 48 figs.; 1 tab

  9. Hole Injection at the Silicon/Aqueous Electrolyte Interface: A Possible Mechanism for Chemiluminescence from Porous Silicon

    NARCIS (Netherlands)

    Kooij, Ernst S.; Butter, K.; Kelly, J.J.

    1998-01-01

    The reduction mechanism of oxidizing agents at silicon and porous silicon electrodes has been investigated in relation to light emission from the porous semiconductor. Oxidizing agents with a positive redox potential are shown to inject holes into HF-pretreated silicon. However, as the degree of

  10. Post-growth annealing of zinc oxide thin films pulsed laser deposited under enhanced oxygen pressure on quartz and silicon substrates

    International Nuclear Information System (INIS)

    Rusop, M.; Uma, K.; Soga, T.; Jimbo, T.

    2006-01-01

    Zinc oxide (ZnO) thin films have been prepared by pulsed laser deposition (PLD) technique at room temperature on quartz and single crystal silicon (1 0 0) substrates. The oxygen ambient gas pressure was attained at 6 Torr during the deposition. The deposited films were post-growth annealed in air at various annealing temperatures for 30 min. The X-ray diffraction (XRD), optical and electrical properties have been measured to study the properties of the films as a function of annealing temperatures. XRD has shown the strength of (0 0 2) peak increases and FWHM value decreases as the annealing temperatures increases from 200 to 600 deg. C. The post-growth annealed at 600 deg. C show dominant c-axis oriented hexagonal wurtize crystal structure and exhibit high average transmittance about 85% in the visible region and very sharp absorption edge at 376 nm with energy band gap of approximately 3.46 eV. Electrical measurement indicates the resistivity decreases with the annealing temperatures up to 600 deg. C, after which it increases with higher annealing temperatures at 800 deg. C. The complex of oxygen vacancy in the ZnO films may be the source of low conductivity in undoped ZnO films

  11. Improved opto-electronic properties of silicon heterojunction solar cells with SiO x /Tungsten-doped indium oxide double anti-reflective coatings

    Science.gov (United States)

    Yu, Jian; Zhou, Jie; Bian, Jiantao; Zhang, Liping; Liu, Yucheng; Shi, Jianhua; Meng, Fanying; Liu, Jinning; Liu, Zhengxin

    2017-08-01

    Amorphous SiO x was prepared by plasma enhanced chemical vapor deposition (PECVD) to form SiO x /tungsten-doped indium oxide (IWO) double anti-reflective coatings for silicon heterojunction (SHJ) solar cell. The sheet resistance of SiO x /IWO stacks decreases due to plasma treatment during deposition process, which means thinner IWO film would be deposited for better optical response. However, the comparisons of three anti-reflective coating (ARC) structures reveal that SiO x film limits carier transport and the path of IWO-SiO x -Ag structure is non-conductive. The decrease of sheet resistance is defined as pseudo conductivity. IWO film capping with SiO x allows observably reduced reflectance and better response in 300-400 and 600-1200 nm wavelength ranges. Compared with IWO single ARC, the average reflection is reduced by 1.65% with 70 nm SiO x /80 nm IWO double anti-reflective coatings (DARCs) in 500-1200 nm wavelength range, leading to growing external quantum efficiency response, short circuit current density (J sc), and efficiency. After well optimization of SiO x /IWO stacks, an impressive efficiency of 23.08% is obtained with high J sc and without compromising open circuit voltage (V oc) and fill factor. SiO x /IWO DARCs provide better anti-reflective properties over a broad range of wavelength, showing promising application for SHJ solar cells.

  12. Effects of argon and oxygen flow rate on water vapor barrier properties of silicon oxide coatings deposited on polyethylene terephthalate by plasma enhanced chemical vapor deposition

    International Nuclear Information System (INIS)

    Kim, Sung-Ryong; Choudhury, Moinul Haque; Kim, Won-Ho; Kim, Gon-Ho

    2010-01-01

    Plasma polymer coatings were deposited from hexamethyldisiloxane on polyethylene terephthalate (PET) substrates while varying the operating conditions, such as the Ar and O 2 flow rates, at a fixed radio frequency power of 300 W. The water vapor transmission rate (WVTR) of the untreated PET was 54.56 g/m 2 /day and was decreased after depositing the silicon oxide (SiO x ) coatings. The minimum WVTR, 0.47 g/m 2 /day, was observed at Ar and O 2 flow rates of 4 and 20 sccm, respectively, with a coating thickness of 415.44 nm. The intensity of the peaks for the Si-O-Si bending at 800-820 cm -1 and Si-O-Si stretching at 1000-1150 cm -1 varied depending on the Ar and O 2 flow rates. The contact angle of the SiO x coated PET increased as the Ar flow rate was increased from 2 to 8 sccm at a fixed O 2 flow rate of 20 sccm. It decreased gradually as the oxygen flow rate increased from 12 to 28 sccm at a fixed Ar carrier gas flow rate. The examination by atomic force microscopy revealed a correlation of the SiO x morphology and the water vapor barrier performance with the Ar and O 2 flow rates. The roughness of the deposited coatings increased when either the O 2 or Ar flow rate was increased.

  13. Preparation and characterization of a calcium-phosphate-silicon coating on a Mg-Zn-Ca alloy via two-step micro-arc oxidation.

    Science.gov (United States)

    Dou, Jinhe; Chen, Yang; Chi, Yiming; Li, Huancai; Gu, Guochao; Chen, Chuanzhong

    2017-06-14

    Magnesium alloys are the most promising implant materials due to their excellent biodegradability. However, their high degradation rate limits their practical application. In this study, we produced a calcium-phosphate (Ca-P) coating and a calcium-phosphate-silicon (Ca-P-Si) coating via one-step and two-step micro-arc oxidation processes, respectively. The microstructure and chemical composition of the MAO coatings were characterized using SEM, XRD and EDS. The degradation behaviors of the MAO coatings and the substrate were investigated using electrochemical techniques and immersion tests in simulated body fluid (SBF). The results show that the silicate was successfully incorporated into the Ca-P coating in the second MAO step, and this also increased the thickness of the coating. The Ca-P-Si coatings remarkably reduced the corrosion rate of the Mg alloy and Ca-P coating during 18 days of immersion in SBF. In addition, the bone-like apatite layer on the sample surface demonstrated the good biomineralization ability of the Ca-P-Si coating. Potentiodynamic polarization results showed that the MAO coating could clearly enhance the corrosion resistance of the Mg alloy. Moreover, we propose the growth mechanism of the MAO coating in the second step.

  14. Memory Effect of Metal-Oxide-Silicon Capacitors with Self-Assembly Double-Layer Au Nanocrystals Embedded in Atomic-Layer-Deposited HfO2 Dielectric

    International Nuclear Information System (INIS)

    Yue, Huang; Hong-Yan, Gou; Qing-Qing, Sun; Shi-Jin, Ding; Wei, Zhang; Shi-Li, Zhang

    2009-01-01

    We report the chemical self-assembly growth of Au nanocrystals on atomic-layer-deposited HfO 2 films aminosilanized by (3-Aminopropyl)-trimethoxysilane aforehand for memory applications. The resulting Au nanocrystals show a density of about 4 × 10 11 cm −2 and a diameter range of 5–8nm. The metal-oxide-silicon capacitor with double-layer Au nanocrystals embedded in HfO 2 dielectric exhibits a large C – V hysteresis window of 11.9V for ±11 V gate voltage sweeps at 1 MHz, a flat-band voltage shift of 1.5 V after the electrical stress under 7 V for 1 ms, a leakage current density of 2.9 × 10 −8 A/cm −2 at 9 V and room temperature. Compared to single-layer Au nanocrystals, the double-layer Au nanocrystals increase the hysteresis window significantly, and the underlying mechanism is thus discussed

  15. Stress and phase changes in a low-thermal-expansion Al-3at.%Ge alloy film on oxidized silicon wafers

    International Nuclear Information System (INIS)

    Tu, K.N.; Rodbell, K.P.; Herd, S.R.; Mikalsen, D.J.

    1993-01-01

    The alloy of Al-3at.%Ge has been found to have a low thermal expansion and contraction in the temperature range of room temperature to 400 C. The reason for the low thermal contraction (or expansion) is the precipitation (or dissolution) of Ge in the alloy. The Ge precipitates have a diamond structure in which each Ge atom occupies a much larger atomic volume than a Ge atom dissolved substitutionally in Al. The volume difference compensates for the effect of thermal expansion and contraction with changing temperature which in turn reduces the thermal stress due to thermal mismatch. The technique of wafer bending was used to determine the stress of the alloy film on oxidized silicon wafers upon thermal cycling; indeed, it is much lower than that of pure Al on identical wafers. The morphology of precipitation and dissolution of Ge in Al has been studied by transmission and scanning electron microscopy. It is found that the precipitation follows a discontinuous mode and occurs predominantly along grain boundaries. In dissolving the Ge precipitates into Al, voids are left behind because of the volume difference. It is proposed that this may explain the enhancement of nucleation of voids in the alloy film upon thermal cycling. (orig.)

  16. Influence of average ion energy and atomic oxygen flux per Si atom on the formation of silicon oxide permeation barrier coatings on PET

    Science.gov (United States)

    Mitschker, F.; Wißing, J.; Hoppe, Ch; de los Arcos, T.; Grundmeier, G.; Awakowicz, P.

    2018-04-01

    The respective effect of average incorporated ion energy and impinging atomic oxygen flux on the deposition of silicon oxide (SiO x ) barrier coatings for polymers is studied in a microwave driven low pressure discharge with additional variable RF bias. Under consideration of plasma parameters, bias voltage, film density, chemical composition and particle fluxes, both are determined relative to the effective flux of Si atoms contributing to film growth. Subsequently, a correlation with barrier performance and chemical structure is achieved by measuring the oxygen transmission rate (OTR) and by performing x-ray photoelectron spectroscopy. It is observed that an increase in incorporated energy to 160 eV per deposited Si atom result in an enhanced cross-linking of the SiO x network and, therefore, an improved barrier performance by almost two orders of magnitude. Furthermore, independently increasing the number of oxygen atoms to 10 500 per deposited Si atom also lead to a comparable barrier improvement by an enhanced cross-linking.

  17. A Lithium-Ion Battery using a 3 D-Array Nanostructured Graphene-Sulfur Cathode and a Silicon Oxide-Based Anode.

    Science.gov (United States)

    Benítez, Almudena; Di Lecce, Daniele; Elia, Giuseppe Antonio; Caballero, Álvaro; Morales, Julián; Hassoun, Jusef

    2018-05-09

    An efficient lithium-ion battery was assembled by using an enhanced sulfur-based cathode and a silicon oxide-based anode and proposed as an innovative energy-storage system. The sulfur-carbon composite, which exploits graphene carbon with a 3 D array (3DG-S), was synthesized by a reduction step through a microwave-assisted solvothermal technique and was fully characterized in terms of structure and morphology, thereby revealing suitable features for lithium-cell application. Electrochemical tests of the 3DG-S electrode in a lithium half-cell indicated a capacity ranging from 1200 to 1000 mAh g -1 at currents of C/10 and 1 C, respectively. Remarkably, the Li-alloyed anode, namely, Li y SiO x -C prepared by the sol-gel method and lithiated by surface treatment, showed suitable performance in a lithium half-cell by using an electrolyte designed for lithium-sulfur batteries. The Li y SiO x -C/3DG-S battery was found to exhibit very promising properties with a capacity of approximately 460 mAh g S -1 delivered at an average voltage of approximately 1.5 V over 200 cycles, suggesting that the characterized materials would be suitable candidates for low-cost and high-energy-storage applications. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  18. A silicon doped hafnium oxide ferroelectric p–n–p–n SOI tunneling field–effect transistor with steep subthreshold slope and high switching state current ratio

    Directory of Open Access Journals (Sweden)

    Saeid Marjani

    2016-09-01

    Full Text Available In this paper, a silicon–on–insulator (SOI p–n–p–n tunneling field–effect transistor (TFET with a silicon doped hafnium oxide (Si:HfO2 ferroelectric gate stack is proposed and investigated via 2D device simulation with a calibrated nonlocal band–to–band tunneling model. Utilization of Si:HfO2 instead of conventional perovskite ferroelectrics such as lead zirconium titanate (PbZrTiO3 and strontium bismuth tantalate (SrBi2Ta2O9 provides compatibility to the CMOS process as well as improved device scalability. By using Si:HfO2 ferroelectric gate stack, the applied gate voltage is effectively amplified that causes increased electric field at the tunneling junction and reduced tunneling barrier width. Compared with the conventional p–n–p–n SOI TFET, the on–state current and switching state current ratio are appreciably increased; and the average subthreshold slope (SS is effectively reduced. The simulation results of Si:HfO2 ferroelectric p–n–p–n SOI TFET show significant improvement in transconductance (∼9.8X enhancement at high overdrive voltage and average subthreshold slope (∼35% enhancement over nine decades of drain current at room temperature, indicating that this device is a promising candidate to strengthen the performance of p–n–p–n and conventional TFET for a switching performance.

  19. Detection of Ammonia-Oxidizing Bacteria (AOB) Using a Porous Silicon Optical Biosensor Based on a Multilayered Double Bragg Mirror Structure.

    Science.gov (United States)

    Zhang, Hongyan; Lv, Jie; Jia, Zhenhong

    2018-01-01

    We successfully demonstrate a porous silicon (PS) double Bragg mirror by electrochemical etching at room temperature as a deoxyribonucleic acid (DNA) label-free biosensor for detecting ammonia-oxidizing bacteria (AOB). Compared to various other one-dimension photonic crystal configurations of PS, the double Bragg mirror structure is quite easy to prepare and exhibits interesting optical properties. The width of high reflectivity stop band of the PS double Bragg mirror is about 761 nm with a sharp and deep resonance peak at 1328 nm in the reflectance spectrum, which gives a high sensitivity and distinguishability for sensing performance. The detection sensitivity of such a double Bragg mirror structure is illustrated through the investigation of AOB DNA hybridization in the PS pores. The redshifts of the reflectance spectra show a good linear relationship with both complete complementary and partial complementary DNA. The lowest detection limit for complete complementary DNA is 27.1 nM and the detection limit of the biosensor for partial complementary DNA is 35.0 nM, which provides the feasibility and effectiveness for the detection of AOB in a real environment. The PS double Bragg mirror structure is attractive for widespread biosensing applications and provides great potential for the development of optical applications.

  20. Dispersion toughened silicon carbon ceramics

    Science.gov (United States)

    Wei, G.C.

    1984-01-01

    Fracture resistant silicon carbide ceramics are provided by incorporating therein a particulate dispersoid selected from the group consisting of (a) a mixture of boron, carbon and tungsten, (b) a mixture of boron, carbon and molybdenum, (c) a mixture of boron, carbon and titanium carbide, (d) a mixture of aluminum oxide and zirconium oxide, and (e) boron nitride. 4 figures.

  1. Reaction-bonded silicon nitride

    International Nuclear Information System (INIS)

    Porz, F.

    1982-10-01

    Reaction-bonded silicon nitride (RBSN) has been characterized. The oxidation behaviour in air up to 1500 0 C and 3000 h and the effects of static and cyclic oxidation on room-temperature strength have been studied. (orig./IHOE) [de

  2. Role of the tip induced local anodic oxidation in the conductive atomic force microscopy of mixed phase silicon thin films

    Czech Academy of Sciences Publication Activity Database

    Vetushka, Aliaksi; Fejfar, Antonín; Ledinský, Martin; Rezek, Bohuslav; Stuchlík, Jiří; Kočka, Jan

    2010-01-01

    Roč. 7, 3-4 (2010), s. 728-731 ISSN 1862-6351 R&D Projects: GA MŠk(CZ) LC06040; GA AV ČR KAN400100701; GA MŠk LC510; GA AV ČR(CZ) IAA100100902 Institutional research plan: CEZ:AV0Z10100521 Keywords : local anodic oxidation (LAO) * conductive atomic force microscopy (C-AFM) Subject RIV: BM - Solid Matter Physics ; Magnetism http://www3.interscience.wiley.com/journal/123289759/abstract

  3. Tin - an unlikely ally for silicon field effect transistors?

    KAUST Repository

    Hussain, Aftab M.; Fahad, Hossain M.; Singh, Nirpendra; Sevilla, Galo T.; Schwingenschlö gl, Udo; Hussain, Muhammad Mustafa

    2014-01-01

    We explore the effectiveness of tin (Sn), by alloying it with silicon, to use SiSn as a channel material to extend the performance of silicon based complementary metal oxide semiconductors. Our density functional theory based simulation shows

  4. Porous silicon carbide (SIC) semiconductor device

    Science.gov (United States)

    Shor, Joseph S. (Inventor); Kurtz, Anthony D. (Inventor)

    1996-01-01

    Porous silicon carbide is fabricated according to techniques which result in a significant portion of nanocrystallites within the material in a sub 10 nanometer regime. There is described techniques for passivating porous silicon carbide which result in the fabrication of optoelectronic devices which exhibit brighter blue luminescence and exhibit improved qualities. Based on certain of the techniques described porous silicon carbide is used as a sacrificial layer for the patterning of silicon carbide. Porous silicon carbide is then removed from the bulk substrate by oxidation and other methods. The techniques described employ a two-step process which is used to pattern bulk silicon carbide where selected areas of the wafer are then made porous and then the porous layer is subsequently removed. The process to form porous silicon carbide exhibits dopant selectivity and a two-step etching procedure is implemented for silicon carbide multilayers.

  5. Silicon containing copolymers

    CERN Document Server

    Amiri, Sahar; Amiri, Sanam

    2014-01-01

    Silicones have unique properties including thermal oxidative stability, low temperature flow, high compressibility, low surface tension, hydrophobicity and electric properties. These special properties have encouraged the exploration of alternative synthetic routes of well defined controlled microstructures of silicone copolymers, the subject of this Springer Brief. The authors explore the synthesis and characterization of notable block copolymers. Recent advances in controlled radical polymerization techniques leading to the facile synthesis of well-defined silicon based thermo reversible block copolymers?are described along with atom transfer radical polymerization (ATRP), a technique utilized to develop well-defined functional thermo reversible block copolymers. The brief also focuses on Polyrotaxanes and their great potential as stimulus-responsive materials which produce poly (dimethyl siloxane) (PDMS) based thermo reversible block copolymers.

  6. Leaf gas exchange and oxidative stress in sorghum plants supplied with silicon and infected by Colletotrichum sublineolum.

    Science.gov (United States)

    Resende, Renata Sousa; Rodrigues, Fabrício Ávila; Cavatte, Paulo Cezar; Martins, Samuel Cordeiro Vitor; Moreira, Wiler Ribas; Chaves, Agnaldo Rodrigues Melo; Damatta, Fábio Murilo

    2012-09-01

    Considering the economic importance of anthracnose, caused by Colletotrichum sublineolum, and silicon (Si) to enhance sorghum resistance against this disease, this study aimed to investigate the effect of this element on leaf gas exchange and also the antioxidative system when infected by C. sublineolum. Plants from sorghum line CMSXS142 (BR 009 [Tx623] - Texas), growing in hydroponic culture with (+Si, 2 mM) or without (-Si) Si, were inoculated with C. sublineolum. Disease severity was assessed at 2, 4, 6, 8, and 10 days after inoculation (dai) and data were used to calculate the area under anthracnose progress curve (AUAPC). Further, the net carbon assimilation rate (A), stomatal conductance to water vapor (g(s)), internal-to-ambient CO₂ concentration ratio (C(i)/C(a)), and transpiration rate (E); the activities of superoxide dismutase (SOD), catalase (CAT), ascorbate peroxidase (APX), and glutathione reductase (GR); the electrolyte leakage (EL), and the concentrations of hydrogen peroxide (H₂O₂) and malondialdehyde (MDA) were determined. The AUAPC was reduced by 86% for the +Si plants compared with the -Si plants. The values of A, g(s), and E were lower upon inoculation of -Si plants in contrast to inoculated +Si plants with decreases of 31 and 60% for A, 34 and 61% for g(s), and 27 and 57% for E, respectively, at 4 and 8 dai. For the noninoculated plants, there was no significant difference between the -Si and +Si treatments for the values of A, g(s), and E. The C(i)/C(a) ratio was similar between the -Si and +Si treatments, regardless of the pathogen inoculation. The activities of SOD, CAT, APX, and GR tended to be higher in the +Si plants compared with the -Si plants upon inoculation with C. sublineolum. The EL significantly increased for -Si plants compared with +Si plants. The MDA concentration significantly increased by 31 and 38% at 4 and 8 dai, respectively, for the -Si plants compared with the +Si plants. Based on these results, Si may have a

  7. Alterations in Gas Exchange and Oxidative Metabolism in Rice Leaves Infected by Pyricularia oryzae are Attenuated by Silicon.

    Science.gov (United States)

    Domiciano, Gisele Pereira; Cacique, Isaías Severino; Chagas Freitas, Cecília; Filippi, Marta Cristina Corsi; DaMatta, Fábio Murilo; do Vale, Francisco Xavier Ribeiro; Rodrigues, Fabrício Ávila

    2015-06-01

    Rice blast, caused by Pyricularia oryzae, is the most important disease in rice worldwide. This study investigated the effects of silicon (Si) on the photosynthetic gas exchange parameters (net CO2 assimilation rate [A], stomatal conductance to water vapor [gs], internal-to-ambient CO2 concentration ratio [Ci/Ca], and transpiration rate [E]); chlorophyll fluorescence a (Chla) parameters (maximum photochemical efficiency of photosystem II [Fv/Fm], photochemical [qP] and nonphotochemical [NPQ] quenching coefficients, and electron transport rate [ETR]); concentrations of pigments, malondialdehyde (MDA), and hydrogen peroxide (H2O2); and activities of superoxide dismutase (SOD), catalase (CAT), ascorbate peroxidase (APX), glutathione reductase (GR), and lypoxigenase (LOX) in rice leaves. Rice plants were grown in a nutrient solution containing 0 or 2 mM Si (-Si or +Si, respectively) with and without P. oryzae inoculation. Blast severity decreased with higher foliar Si concentration. The values of A, gs and E were generally higher for the +Si plants in comparison with the -Si plants upon P. oryzae infection. The Fv/Fm, qp, NPQ, and ETR were greater for the +Si plants relative to the -Si plants at 108 and 132 h after inoculation (hai). The values for qp and ETR were significantly higher for the -Si plants in comparison with the +Si plants at 36 hai, and the NPQ was significantly higher for the -Si plants in comparison with the +Si plants at 0 and 36 hai. The concentrations of Chla, Chlb, Chla+b, and carotenoids were significantly greater in the +Si plants relative to the -Si plants. For the -Si plants, the MDA and H2O2 concentrations were significantly higher than those in the +Si plants. The LOX activity was significantly higher in the +Si plants than in the -Si plants. The SOD and GR activities were significantly higher for the -Si plants than in the +Si plants. The CAT and APX activities were significantly higher in the +Si plants than in the -Si plants. The supply of

  8. Ultraviolet-visible electroluminescence from metal-oxide-semiconductor devices with CeO2 films on silicon

    International Nuclear Information System (INIS)

    Lv, Chunyan; Zhu, Chen; Wang, Canxing; Li, Dongsheng; Ma, Xiangyang; Yang, Deren

    2015-01-01

    We report on ultraviolet-visible (UV-Vis) electroluminescence (EL) from metal-oxide-semiconductor (MOS) devices with the CeO 2 films annealed at low temperatures. At the same injection current, the UV-Vis EL from the MOS device with the 550 °C-annealed CeO 2 film is much stronger than that from the counterpart with the 450 °C-annealed CeO 2 film. This is due to that the 550 °C-annealed CeO 2 film contains more Ce 3+ ions and oxygen vacancies. It is tentatively proposed that the recombination of the electrons in multiple oxygen-vacancy–related energy levels with the holes in Ce 4f 1 energy band pertaining to Ce 3+ ions leads to the UV-Vis EL

  9. Influence of reductant and germanium concentration on the growth and stress development of germanium nanocrystals in silicon oxide matrix

    International Nuclear Information System (INIS)

    Chew, H G; Zheng, F; Choi, W K; Chim, W K; Foo, Y L; Fitzgerald, E A

    2007-01-01

    Germanium (Ge) nanocrystals have been synthesized by annealing co-sputtered SiO 2 -Ge samples in N 2 or forming gas (90% N 2 +10% H 2 ) at temperatures ranging from 700 to 1000 deg. C. We concluded that the annealing ambient, temperature and Ge concentration have a significant influence on the formation and evolution of the nanocrystals. We showed that a careful selective etching of the annealed samples in hydrofluoric acid solution enabled the embedded Ge nanocrystals to be liberated from the SiO 2 matrix. From the Raman results of the as-grown and the liberated nanocrystals, we established that the nanocrystals generally experienced compressive stress in the oxide matrix and the evolution of these stress states was intimately linked to the distribution, density, size and quality of the Ge nanocrystals

  10. Spiral silicon drift detectors

    International Nuclear Information System (INIS)

    Rehak, P.; Gatti, E.; Longoni, A.; Sampietro, M.; Holl, P.; Lutz, G.; Kemmer, J.; Prechtel, U.; Ziemann, T.

    1988-01-01

    An advanced large area silicon photodiode (and x-ray detector), called Spiral Drift Detector, was designed, produced and tested. The Spiral Detector belongs to the family of silicon drift detectors and is an improvement of the well known Cylindrical Drift Detector. In both detectors, signal electrons created in silicon by fast charged particles or photons are drifting toward a practically point-like collection anode. The capacitance of the anode is therefore kept at the minimum (0.1pF). The concentric rings of the cylindrical detector are replaced by a continuous spiral in the new detector. The spiral geometry detector design leads to a decrease of the detector leakage current. In the spiral detector all electrons generated at the silicon-silicon oxide interface are collected on a guard sink rather than contributing to the detector leakage current. The decrease of the leakage current reduces the parallel noise of the detector. This decrease of the leakage current and the very small capacities of the detector anode with a capacitively matched preamplifier may improve the energy resolution of Spiral Drift Detectors operating at room temperature down to about 50 electrons rms. This resolution is in the range attainable at present only by cooled semiconductor detectors. 5 refs., 10 figs

  11. Silicone nanocomposite coatings for fabrics

    Science.gov (United States)

    Eberts, Kenneth (Inventor); Lee, Stein S. (Inventor); Singhal, Amit (Inventor); Ou, Runqing (Inventor)

    2011-01-01

    A silicone based coating for fabrics utilizing dual nanocomposite fillers providing enhanced mechanical and thermal properties to the silicone base. The first filler includes nanoclusters of polydimethylsiloxane (PDMS) and a metal oxide and a second filler of exfoliated clay nanoparticles. The coating is particularly suitable for inflatable fabrics used in several space, military, and consumer applications, including airbags, parachutes, rafts, boat sails, and inflatable shelters.

  12. Knudsen pump produced via silicon deep RIE, thermal oxidation, and anodic bonding processes for on-chip vacuum pumping

    Science.gov (United States)

    Van Toan, Nguyen; Inomata, Naoki; Trung, Nguyen Huu; Ono, Takahito

    2018-05-01

    This work describes the fabrication and evaluation of the Knudsen pump for on-chip vacuum pumping that works based on the principle of a thermal transpiration. Three AFM (atomic force microscope) cantilevers are integrated into small chambers with a size of 5 mm  ×  3 mm  ×  0.4 mm for the pump’s evaluation. Knudsen pump is fabricated using deep RIE (reactive ion etching), wet thermal oxidation and anodic bonding processes. The fabricated device is evaluated by monitoring the quality (Q) factor of the integrated cantilevers. The Q factor of the cantilever is increased from 300 -1150 in cases without and with a temperature difference approximately 25 °C between the top (the hot side at 40 °C) and bottom (the cold side at 15 °C) sides of the fabricated device, respectively. The evacuated chamber pressure of around 10 kPa is estimated from the Q factor of the integrated cantilevers.

  13. Dissolution studies of natural analogues spent fuel and U(VI)-Silicon phases of and oxidative alteration process

    International Nuclear Information System (INIS)

    Perez Morales, I.

    2000-01-01

    In order to understand the long-term behavior of the nuclear spent fuel in geological repository conditions, we have performed dissolution studies with natural analogues to UO 2 as well as with solid phases representatives of the oxidative alteration pathway of uranium dioxide, as observed in both natural environment and laboratory studies. In all cases, we have studied the influence of the bicarbonate concentration in the dissolution process, as a first approximation to the groundwater composition of a granitic environment, where carbonate is one of the most important complexing agents. As a natural analogue to the nuclear spent fuel some uraninite samples from the Oklo are deposit in Gabon, where chain fission reactions took place 2000 millions years ago, as well as a pitchblende sample from the mine Fe ore deposit, in Salamanca (spain) have been studied. The studies have been performed at 25 and 60 deg C and 60 deg C, and they have focussed on the determination of both the thermodynamic and the kinetic properties of the different samples studied, using batch and continuous experimental methodologies, respectively. (Author)

  14. Double-layer indium doped zinc oxide for silicon thin-film solar cell prepared by ultrasonic spray pyrolysis

    International Nuclear Information System (INIS)

    Jiao Bao-Chen; Zhang Xiao-Dan; Wei Chang-Chun; Sun Jian; Ni Jian; Zhao Ying

    2011-01-01

    Indium doped zinc oxide (ZnO:In) thin films were prepared by ultrasonic spray pyrolysis on corning eagle 2000 glass substrate. 1 and 2 at.% indium doped single-layer ZnO:In thin films with different amounts of acetic acid added in the initial solution were fabricated. The 1 at.% indium doped single-layers have triangle grains. The 2 at.% indium doped single-layer with 0.18 acetic acid adding has the resistivity of 6.82×10 −3 Ω·cm and particle grains. The double-layers structure is designed to fabricate the ZnO:In thin film with low resistivity (2.58×10 −3 Ω·cm) and good surface morphology. It is found that the surface morphology of the double-layer ZnO:In film strongly depends on the substrate-layer, and the second-layer plays a large part in the resistivity of the double-layer ZnO:In thin film. Both total and direct transmittances of the double-layer ZnO:In film are above 80% in the visible light region. Single junction a-Si:H solar cell based on the double-layer ZnO:In as front electrode is also investigated. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  15. Graphene Oxides Used as a New "Dual Role" Binder for Stabilizing Silicon Nanoparticles in Lithium-Ion Battery.

    Science.gov (United States)

    Shan, Changsheng; Wu, Kaifeng; Yen, Hung-Ju; Narvaez Villarrubia, Claudia; Nakotte, Tom; Bo, Xiangjie; Zhou, Ming; Wu, Gang; Wang, Hsing-Lin

    2018-05-09

    For the first time, we report that graphene oxide (GO) can be used as a new "dual-role" binder for Si nanoparticles (SiNPs)-based lithium-ion batteries (LIBs). GO not only provides a graphene-like porous 3D framework for accommodating the volume changes of SiNPs during charging/discharging cycles, but also acts as a polymer-like binder that forms strong chemical bonds with SiNPs through its Si-OH functional groups to trap and stabilize SiNPs inside the electrode. Leveraging this unique dual-role of GO binder, we fabricated GO/SiNPs electrodes with remarkably improved performances as compared to using the conventional polyvinylidene fluoride (PVDF) binder. Specifically, the GO/SiNPs electrode showed a specific capacity of 2400 mA h g -1 at the 50th cycle and 2000 mA h g -1 at the 100th cycle, whereas the SiNPs/PVDF electrode only showed 456 mAh g -1 at the 50th cycle and 100 mAh g -1 at 100th cycle. Moreover, the GO/SiNPs film maintained its structural integrity and formed a stable solid-electrolyte interphase (SEI) film after 100 cycles. These results, combined with the well-established facile synthesis of GO, indicate that GO can be an excellent binder for developing high performance Si-based LIBs.

  16. Polar and Nonpolar Gallium Nitride and Zinc Oxide based thin film heterostructures Integrated with Sapphire and Silicon

    Science.gov (United States)

    Gupta, Pranav

    This dissertation work explores the understanding of the relaxation and integration of polar and non-polar of GaN and ZnO thin films with Sapphire and silicon substrates. Strain management and epitaxial analysis has been performed on wurtzitic GaN(0001) thin films grown on c-Sapphire and wurtzitic non-polar a-plane GaN(11-20) thin films grown on r-plane Sapphire (10-12) by remote plasma atomic nitrogen source assisted UHV Pulsed Laser Deposition process. It has been established that high-quality 2-dimensional c-axis GaN(0001) nucleation layers can be grown on c-Sapphire by PLD process at growth temperatures as low as ˜650°C. Whereas the c-axis GaN on c-sapphire has biaxially negative misfit, the crystalline anisotropy of the a-plane GaN films on r-Sapphire results in compressive and tensile misfits in the two major orthogonal directions. The measured strains have been analyzed in detail by X-ray, Raman spectroscopy and TEM. Strain relaxation in GaN(0001)/Sapphire thin film heterostructure has been explained by the principle of domain matched epitaxial growth in large planar misfit system and has been demonstrated by TEM study. An attempt has been made to qualitatively understand the minimization of free energy of the system from the strain perspective. Analysis has been presented to quantify the strain components responsible for the compressive strain observed in the GaN(0001) thin films on c-axis Sapphire substrates. It was also observed that gallium rich deposition conditions in PLD process lead to smoother nucleation layers because of higher ad-atom mobility of gallium. We demonstrate near strain relaxed epitaxial (0001) GaN thin films grown on (111) Si substrates using TiN as intermediate buffer layer by remote nitrogen plasma assisted UHV pulsed laser deposition (PLD). Because of large misfits between the TiN/GaN and TiN/Si systems the TIN buffer layer growth occurs via nucleation of interfacial dislocations under domain matching epitaxy paradigm. X-ray and

  17. Ultra-low power high temperature and radiation hard complementary metal-oxide-semiconductor (CMOS) silicon-on-insulator (SOI) voltage reference.

    Science.gov (United States)

    Boufouss, El Hafed; Francis, Laurent A; Kilchytska, Valeriya; Gérard, Pierre; Simon, Pascal; Flandre, Denis

    2013-12-13

    This paper presents an ultra-low power CMOS voltage reference circuit which is robust under biomedical extreme conditions, such as high temperature and high total ionized dose (TID) radiation. To achieve such performances, the voltage reference is designed in a suitable 130 nm Silicon-on-Insulator (SOI) industrial technology and is optimized to work in the subthreshold regime of the transistors. The design simulations have been performed over the temperature range of -40-200 °C and for different process corners. Robustness to radiation was simulated using custom model parameters including TID effects, such as mobilities and threshold voltages degradation. The proposed circuit has been tested up to high total radiation dose, i.e., 1 Mrad (Si) performed at three different temperatures (room temperature, 100 °C and 200 °C). The maximum drift of the reference voltage V(REF) depends on the considered temperature and on radiation dose; however, it remains lower than 10% of the mean value of 1.5 V. The typical power dissipation at 2.5 V supply voltage is about 20 μW at room temperature and only 75 μW at a high temperature of 200 °C. To understand the effects caused by the combination of high total ionizing dose and temperature on such voltage reference, the threshold voltages of the used SOI MOSFETs were extracted under different conditions. The evolution of V(REF) and power consumption with temperature and radiation dose can then be explained in terms of the different balance between fixed oxide charge and interface states build-up. The total occupied area including pad-ring is less than 0.09 mm2.

  18. Synthesis of the cactus-like silicon nanowires/tungsten oxide nanowires composite for room-temperature NO{sub 2} gas sensor

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Weiyi, E-mail: zhangweiyi@tju.edu.cn [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Hu, Ming [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Key Laboratory for Advanced Ceramics and Machining Technology, Ministry of Education, School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China); Liu, Xing; Wei, Yulong; Li, Na [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Qin, Yuxiang, E-mail: qinyuxiang@tju.edu.cn [School of Electronic Information Engineering, Tianjin University, Tianjin, 300072 (China); Key Laboratory for Advanced Ceramics and Machining Technology, Ministry of Education, School of Materials Science and Engineering, Tianjin University, Tianjin 300072 (China)

    2016-09-15

    In the present work, the tungsten oxide (WO{sub 3}) nanowires functionalized silicon nanowires (SiNWs) with cactus-like structure has been successfully synthesized for room-temperature NO{sub 2} detection. The novel nanocomposite was fabricated by metal-assisted chemical etching (MACE) and thermal annealing of tungsten film. The WO{sub 3} nanowires were evenly distributed from the upper to the lower part of the SiNWs, indicating excellent uniformity which is conducive to adsorption and desorption of gas molecules. The gas-sensing properties have been examined by measuring the resistance change towards 0.25–5 ppm NO{sub 2} gas. At room temperature, which is the optimum working temperature, the SiNWs/WO{sub 3} nanowires composite showed two-times higher NO{sub 2} response than that of the bare SiNWs at 2 ppm NO{sub 2}. On the contrary, the responses of composite sensors to high concentrations of other reducing gases were very low, indicating excellent selectivity. Simultaneously, the composite sensors exhibited good sensing repeatability and stability. The enhancement in gas sensing properties may be attributed to the change in width of the space charge region, which is similar to the behavior of p-n junctions under forward bias, in the high-density p-n heterojunction structure formed between SiNWs and WO{sub 3} nanowires. - Highlights: • SiNWs/WO{sub 3} nanowires composite with cactus-like structure is synthesized. • The morphology of WO{sub 3} nanowires depends on the thermal annealing temperature. • The nanocomposite sensor exhibit better gas response than that of bare SiNWs. • The gas sensing mechanism is discussed using p-n heterojunction theory.

  19. A statistical approach for the optimization of indium tin oxide films used as a front contact in amorphous/crystalline silicon heterojunction solar cells

    International Nuclear Information System (INIS)

    Le, Anh Huy Tuan; Ahn, Shihyun; Kim, Sangho; Han, Sangmyeong; Kim, Sunbo; Park, Hyeongsik; Nguyen, Cam Phu Thi; Dao, Vinh Ai; Yi, Junsin

    2014-01-01

    Highlights: • The number of experiments was reduced by approximately 90% using Taguchi design. • The optimal condition of ITO films was obtained by Grey relational analysis. • Substrate temperature is dominant effect on opto-electrical properties of ITO films. • Using the optimal ITO films, the solar cell efficiency was absolutely increased by 1.750%. - Abstract: In heterojunction silicon with intrinsic thin layer (HIT) solar cells, the excellent opto-electrical properties of indium tin oxide (ITO) front contact play a critical role in attaining high efficiency. Therefore, in this study, we present and demonstrate an effective statistic approach based on combining Taguchi method and Grey relational analysis for the optimization of ITO films. A reduction in the number of experiments by approximately 90% is obtained by the Taguchi method through an orthogonal array. The reproduction of the effect of process parameters on single performance characteristic, however, is still ensured. In addition, an excellent trade-off between electrical and optical properties of ITO films was attained within the selected range of parameters by Grey relational analysis at power density of 0.685 W/cm 2 , working pressure of 0.4 Pa, substrate temperature of 200 °C, and post-annealing temperature of 200 °C in 30 min. Under optimal condition, the ITO films showed lowest electrical resistivity of 1.978 × 10 −4 Ω cm, and highest transmittance of 90.322%. The HIT solar cells using these ITO films as a front contact show highest efficiency of 16.616%, yielding a 1.750% absolute increase in efficiency compared to using ITO films with the initial condition. Furthermore, the analysis of variance (ANOVA) is determined to define the process parameters which have a dominant effect on the electrical and optical properties of ITO films. Based on ANOVA, we found that the substrate temperature was a key parameter which critically affects the opto-electrical properties of ITO films

  20. Silicon oxide barrier films deposited on PET foils in pulsed plasmas: influence of substrate bias on deposition process and film properties

    International Nuclear Information System (INIS)

    Steves, S; Bibinov, N; Awakowicz, P; Ozkaya, B; Liu, C-N; Ozcan, O; Grundmeier, G

    2013-01-01

    A widely used plastic for packaging, polyethylene terephtalate (PET) offers limited barrier properties against gas permeation. For many applications of PET (from food packaging to micro electronics) improved barrier properties are essential. A silicon oxide barrier coating of PET foils is applied by means of a pulsed microwave driven low-pressure plasma. While the adjustment of the microwave power allows for a control of the ion production during the plasma pulse, a substrate bias controls the energy of ions impinging on the substrate. Detailed analysis of deposited films applying oxygen permeation measurements, x-ray photoelectron spectroscopy and atomic force microscopy are correlated with results from plasma diagnostics describing the deposition process. The influence of a change in process parameters such as gas mixture and substrate bias on the gas temperature, electron density, mean electron energy, ion energy and the atomic oxygen density is studied. An additional substrate bias results in an increase in atomic oxygen density up to a factor of 6, although plasma parameter such as electron density of n e = 3.8 ± 0.8 × 10 17 m −3 and electron temperature of k B T e = 1.7 ± 0.1 eV are unmodified. It is shown that atomic oxygen densities measured during deposition process higher than n O = 1.8 × 10 21 m −3 yield in barrier films with a barrier improvement factor up to 150. Good barrier films are highly cross-linked and show a smooth morphology. (paper)